  1. Deposition of yttrium oxysulfide thin films by atomic layer epitaxy

    International Nuclear Information System (INIS)

    Kukli, K.; University of Tartu, Tartu,; Johansson, L-S.; Nykaenen, E.; Peussa, M.; Ninistoe, L.

    1998-01-01

    Full text: Yttrium oxysulfide is a highly interesting material for optoelectronic applications. It is industrially exploited in the form of doped powder in catholuminescent phosphors, e.g. Y 2 O 2 S: Eu 3+ for colour TV. Attempts to grow thin films of Y 2 O 2 S have not been frequent and only partially successful due to the difficulties in obtaining crystalline films at a reasonable temperature. Furthermore, sputtering easily leads to a sulphur deficiency. Evaporation of the elements from a multi-source offers a better control of the stoichiometry resulting in hexagonal (0002) oriented films at 580 deg C. In this paper we present the first successful thin film growth experiments using a chemical process with molecular precursors. Atomic layer epitaxy (ALE) allows the use of a relatively low deposition temperature and thus compatibility with other technologies. Already at 425 deg C the reaction between H 2 S and Y(thd) 3 (thd = 2,2,6,6 - tetramethyl-heptane-3,5- dione) yields a crystalline Y 2 O 2 S thin film which was characterized by XRD, XRF and XPS

  2. Unactivated yttrium tantalate phosphor

    International Nuclear Information System (INIS)

    Reddy, V.B.; Cheung, H.K.

    1992-01-01

    This patent describes an unactivated yttrium tantalate phosphor having M prime monoclinic structure and containing one or more additives of Rb and Al in an amount of between about 0.001 to 0.1 moles per mole of yttrium tantalate to improve brightness under X-radiation. This patent also describes an unactivated yttrium tantalate phosphor having M prime monoclinic structure and containing additives of Sr in an amount of between 0.001 to 0.1 moles per mole of yttrium tantalate and one or more of Rb and Al in an amount of between 0.001 to 0.1 moles per mole of yttrium tantalate the phosphor exhibiting a greater brightness under X-radiation than the phosphor absent Rb and Al

  3. Lanthanum and yttrium oxysulfides activated by europium: (Ln1-x Eux)2 O2 S - Synthesis and characterization

    International Nuclear Information System (INIS)

    Luiz, J.M.

    1989-01-01

    The synthesis of lanthanum and yttrium oxysulfides activated by europium were obtained by thermal decomposition of lanthanum and yttrium oxalates doped with europium, under an argon and sulphur atmosphere. The thermal decomposition of these compounds is studied by differential thermal analysis (DTA). The characterization of these oxysulfides were made by chemical analyses, infrared spectroscopy, X-ray diffraction, scanning electron microscopy and emission spectroscopy. (M.V.M.)

  4. Process for recovering yttrium and lanthanides from wet-process phosphoric acid

    Energy Technology Data Exchange (ETDEWEB)

    Janssen, J.A.; Weterings, C.A.

    1983-06-28

    Process for recovering yttrium and lanthanides from wet-process phosphoric acid by adding a flocculant to the phosphoric acid, separating out the resultant precipitate and then recovering yttrium and lanthanides from the precipitate. Uranium is recovered from the remaining phosphoric acid.

  5. Rare earth activated yttrium aluminate phosphors with modulated luminescence.

    Science.gov (United States)

    Muresan, L E; Popovici, E J; Perhaita, I; Indrea, E; Oro, J; Casan Pastor, N

    2016-06-01

    Yttrium aluminate (Y3 A5 O12 ) was doped with different rare earth ions (i.e. Gd(3+) , Ce(3+) , Eu(3+) and/or Tb(3+) ) in order to obtain phosphors (YAG:RE) with general formula,Y3-x-a Gdx REa Al5 O12 (x = 0; 1.485; 2.97 and a = 0.03). The synthesis of the phosphor samples was done using the simultaneous addition of reagents technique. This study reveals new aspects regarding the influence of different activator ions on the morpho-structural and luminescent characteristics of garnet type phosphor. All YAG:RE phosphors are well crystallized powders containing a cubic-Y3 Al5 O12 phase as major component along with monoclinic-Y4 Al2 O9 and orthorhombic-YAlO3 phases as the impurity. The crystallites dimensions of YAG:RE phosphors vary between 38 nm and 88 nm, while the unit cell slowly increase as the ionic radius of the activator increases. Under UV excitation, YAG:Ce exhibits yellow emission due to electron transition in Ce(3+) from the 5d level to the ground state levels ((2) F5/2 , (2) F7/2 ). The emission intensity of Ce(3+) is enhanced in the presence of the Tb(3+) ions and is decreased in the presence of Eu(3+) ions due to some radiative or non-radiative processes that take place between activator ions. By varying the rare earth ions, the emission colour can be modulated from green to white and red. Copyright © 2015 John Wiley & Sons, Ltd. Copyright © 2015 John Wiley & Sons, Ltd.

  6. Activated phosphors having matrices of yttrium-transition metal compound

    International Nuclear Information System (INIS)

    De Kalb, E.L.; Fassel, V.A.

    1975-01-01

    A method is described for preparing a phosphor composition containing a lanthanide activator element with a host matrix having a transition element as a major component. The host matrix is composed of certain rare earth phosphates or vanadates such as YPO 4 with a portion of the rare earth replaced with one or more of the transition elements. On x-ray or other electromagnetic excitation, trace lanthanide impurities or additives within the phosphor are spectrometrically determined from their characteristic luminescence

  7. Combustion synthesis and photoluminescence in novel red emitting yttrium gadolinium pyrosilicate nanocrystalline phosphor

    Energy Technology Data Exchange (ETDEWEB)

    Hedaoo, V.P., E-mail: vraikwar@rediffmail.com [Department of Physics, R. J. College, Ghatkopar, Mumbai, MS 400086 (India); Bhatkar, V.B. [Department of Physics, Shri Shivaji Science College, Amravati, MS 444602 (India); Omanwar, S.K. [Department of Physics, SGB Amravati University, Amravati, MS 444602 (India)

    2016-07-05

    Yttrium Gadolinium Pyrosilicate Y{sub 2-x}Gd{sub x}Si{sub 2}O{sub 7}:Eu{sup 3+} (x = 0.05, 0.10, 0.15) phosphor powder was prepared by facile and time efficient modified combustion method for the first time. The phosphor was characterized by powder X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), photoluminescence excitation (PLE) and emission (PL) spectroscopy and color chromaticity coordinates. XRD revealed the monoclinic crystal structure with space group P1¯. The crystallite size was calculated by Williamson-Hall (W–H) analysis. Nanoplates-like morphology was observed in FESEM analysis with size in the range 50–80 nm. TEM images confirmed the particle size and shape. Upon excitation by 254 nm UV light, the phosphor showed the characteristic red emission peaks at 589 nm and 613 nm corresponding to {sup 5}D{sub 0} → {sup 7}F{sub 1} and {sup 5}D{sub 0} → {sup 7}F{sub 2} transitions respectively. It was observed that the nanocrystalline phosphor Y{sub 2-x}Gd{sub x}Si{sub 2}O{sub 7}:Eu{sup 3+}can be tuned to emit orange to red color by adjusting the ratio Y/Gd. This phosphor thus can be a potential candidate as orange to red color emitting tunable nanocrystalline phosphor for optical devices. - Highlights: • A novel Yttrium Gadolinium Pyrosilicate doped with Eu{sup 3+} is reported. • Facile and time efficient modified combustion method is used. • The nanocrystalline structure was shown by X-ray diffraction, W–H analysis. • FESEM and TEM images confirmed the nanocrystalline structure. • The reported phosphor can be tuned from orange to red by varying Y/Gd ratio.

  8. The commercial production of compounds of the lanthanides and yttrium as CRT phosphor precursors

    International Nuclear Information System (INIS)

    Kilbourn, B.T.

    1987-01-01

    The consumer acceptance of color television at the start of the 60's was triggered by the phosphor industry's discovery and production of a satisfactory red phosphor using the element europium. This element, in the middle of the lanthanide series, had until that time been an academic curiosity, prepared only in gram quantities for research. The large-scale production by the lanthanide industry, in order to meet the demand for commercial quantities of high purity europium oxide, required the introduction of new technology. Lanthanide elements other than europium, such as cerium and terbium, are also needed as the active ions for many phosphors. In addition, the inert host lattice for those emitting ions can be provided by compounds of yttrium, the element above the lanthanides in the periodic table, with comparable properties. The lanthanide industry has developed processes to produce compounds of such elements in the required quantities and purities. For commercial separation of these elements a technology known as counter-current liquid-liquid extraction has been developed. This technique, commonly called solvent extraction, is illustrated and described. The initial ore preparation steps, together with the final high purity oxide production is also mentioned

  9. Cathodoluminescent characteristics and light technical parameters of thin-film screens based on oxides and oxysulfides of rare-earth elements

    Science.gov (United States)

    Bondar, Vyacheslav D.; Grytsiv, Myroslav; Groodzinsky, Arkady; Vasyliv, Mykhailo

    1995-11-01

    Results on creation of thin-film single-crystal high-resolution screens with energy control of luminescence color are presented. In order to create phosphor films ion-plasma technology for deposition of yttrium and lanthanum oxides and oxysulfides activated by rare earth elements has been developed. The screen consists of phosphor film on phosphor substrate with different colors of luminescence (e.g. Y2O3-Eu film with red color on Y3Al5O12- Tb, Ce substrate with green color of luminescence). Electron irradiation causes luminescence with color that depends on energy of the electron beam. The physical reason for color change is that electron beam energy defines electron penetration depth. If the energy is weak, only the film is excited. More powerful beam penetrates into the substrate and thus changes the color of luminescence.

  10. Nanopatterned yttrium aluminum garnet phosphor incorporated film for high-brightness GaN-based white light emitting diodes

    International Nuclear Information System (INIS)

    Cho, Joong-yeon; Park, Sang-Jun; Ahn, Jinho; Lee, Heon

    2014-01-01

    In this study, we fabricated high-brightness white light emitting diodes (LEDs) by developing a nanopatterned yttrium aluminum garnet (YAG) phosphor-incorporated film. White light can be obtained by mixing blue light from a GaN-based LED and yellow light of the YAG phosphor-incorporated film. If white light sources can be fabricated by exciting proper yellow phosphor using blue light, then these sources can be used instead of the conventional fluorescent lamps with a UV source, for backlighting of displays. In this work, a moth-eye structure was formed on the YAG phosphor-incorporated film by direct spin-on glass (SOG) printing. The moth-eye structures have been investigated to improve light transmittance in various optoelectronic devices, including photovoltaic solar cells, light emitting diodes, and displays, because of their anti-reflection property. Direct SOG printing, which is a simple, easy, and relatively inexpensive process, can be used to fabricate nanoscale structures. After direct SOG printing, the moth-eye structure with a diameter of 220 nm was formed uniformly on the YAG phosphor-incorporated film. As a result of moth-eye patterning on the YAG phosphor-incorporated film, the light output power of a white LED with a patterned YAG phosphor-incorporated film increased to up to 13% higher than that of a white LED with a non-patterned film. - Highlights: • GaN-based high-brightness white LED was prepared using patterned YAG phosphor-incorporated films. • Direct hydrogen silsesquioxane printing was used to form moth-eye patterns on the YAG films. • The electroluminescence intensity of the white LED was enhanced by up to 14.9%

  11. Nanopatterned yttrium aluminum garnet phosphor incorporated film for high-brightness GaN-based white light emitting diodes

    Energy Technology Data Exchange (ETDEWEB)

    Cho, Joong-yeon; Park, Sang-Jun [Department of Materials Science and Engineering, Korea University, Seoul 136-713 (Korea, Republic of); Ahn, Jinho, E-mail: jhahn@hanyang.ac.kr [Department of Material Science and Engineering, Hanyang University, Seoul 133-791 (Korea, Republic of); Lee, Heon, E-mail: heonlee@korea.ac.kr [Department of Materials Science and Engineering, Korea University, Seoul 136-713 (Korea, Republic of)

    2014-11-03

    In this study, we fabricated high-brightness white light emitting diodes (LEDs) by developing a nanopatterned yttrium aluminum garnet (YAG) phosphor-incorporated film. White light can be obtained by mixing blue light from a GaN-based LED and yellow light of the YAG phosphor-incorporated film. If white light sources can be fabricated by exciting proper yellow phosphor using blue light, then these sources can be used instead of the conventional fluorescent lamps with a UV source, for backlighting of displays. In this work, a moth-eye structure was formed on the YAG phosphor-incorporated film by direct spin-on glass (SOG) printing. The moth-eye structures have been investigated to improve light transmittance in various optoelectronic devices, including photovoltaic solar cells, light emitting diodes, and displays, because of their anti-reflection property. Direct SOG printing, which is a simple, easy, and relatively inexpensive process, can be used to fabricate nanoscale structures. After direct SOG printing, the moth-eye structure with a diameter of 220 nm was formed uniformly on the YAG phosphor-incorporated film. As a result of moth-eye patterning on the YAG phosphor-incorporated film, the light output power of a white LED with a patterned YAG phosphor-incorporated film increased to up to 13% higher than that of a white LED with a non-patterned film. - Highlights: • GaN-based high-brightness white LED was prepared using patterned YAG phosphor-incorporated films. • Direct hydrogen silsesquioxane printing was used to form moth-eye patterns on the YAG films. • The electroluminescence intensity of the white LED was enhanced by up to 14.9%.

  12. Structural and luminescence effects of Ga co-doping on Ce-doped yttrium aluminate based phosphors

    Energy Technology Data Exchange (ETDEWEB)

    Ayvacikli, M. [Celal Bayar University, Faculty of Arts and Sciences, Department of Physics, Muradiye, Manisa (Turkey); Canimoglu, A. [Nigde University, Faculty of Arts and Sciences, Physics Department, Nigde (Turkey); Muresan, L.E., E-mail: laura_muresan2003@yahoo.com [Babes Bolyai University, Raluca Ripan Institute for Research in Chemistry, Fantanele 30, 400294 Cluj-Napoca (Romania); Barbu Tudoran, L. [Babes Bolyai University, Electronic Microscopy Centre, Clinicilor 37, 400006 Cluj Napoca (Romania); Garcia Guinea, J. [Museo Nacional Ciencias Naturales, Jose Gutierrez Abascal 2, Madrid 28006 (Spain); Karabulut, Y. [Celal Bayar University, Faculty of Arts and Sciences, Department of Physics, Muradiye, Manisa (Turkey); Jorge, A. [Museo Nacional Ciencias Naturales, Jose Gutierrez Abascal 2, Madrid 28006 (Spain); Karali, T. [Ege University, Institute of Nuclear Sciences, 35100 Bornova, İzmir (Turkey); Can, N., E-mail: cannurdogan@yahoo.com [Celal Bayar University, Faculty of Arts and Sciences, Department of Physics, Muradiye, Manisa (Turkey); Jazan University, Physics Department, P.O. Box 114, 45142 Jazan (Saudi Arabia)

    2016-05-05

    Herein, we primarily focus on luminescence spectrum measurements of various types of green emitting yttrium aluminate phosphors modified with gallium (Y{sub 3}Al{sub 5-x}Ga{sub x}O{sub 12}) synthesised by solid state reaction. The luminescent emission of samples depends on sample temperature and excitation radiation such as incident X-ray, electron and laser beam. Here, we measured radioluminescence (RL), cathodoluminescence (CL), photoluminescence (PL) along with XRD in order to clarify relationship between lattice defects and the spectral luminescence emissions. The RL and CL spectra of YAG:Ce exhibit an emission band ranging from 300 to 450 nm related to Y{sub Al} antisite defects. The broad emission band of garnet phosphors is shifted from 526 nm to 498 nm with increasing of Ga{sup 3+} content, while full width at half maximum (FWHM) of the band tends to be greater than the width of unmodified YAG:Ce garnet. Deconvolution of the spectrum reveals that three emission bands centred at 139, 234 and 294 °C occur in aluminate host garnets. - Highlights: • We present preparation of YAG:Ce{sup 3+}, Ga{sup 3+} phosphors by a solid state reaction method. • The shape and size of phosphor particles were investigated. • The luminescence properties were studied by different excitation sources.

  13. Effect of ultrasound treatment on the morpho-structural and luminescent characteristics of cerium doped yttrium silicate phosphors

    Energy Technology Data Exchange (ETDEWEB)

    Muresan, L.E., E-mail: laura_muresan2003@yahoo.com [“Raluca Ripan” Institute for Research in Chemistry, Babeş Bolyai University, Fântânele 30, 400294 Cluj-Napoca (Romania); Cadis, A.I.; Perhaita, I. [“Raluca Ripan” Institute for Research in Chemistry, Babeş Bolyai University, Fântânele 30, 400294 Cluj-Napoca (Romania); Silipas, D.T. [National Institute for R& D of Isotopic and Molecular Technologies, Donath 67-103, 400293 Cluj-Napoca (Romania); Tudoran, L. Barbu [Electronic Microscopy Centre, Babeş Bolyai University, Clinicilor 37, 400006 Cluj-Napoca (Romania)

    2015-08-15

    Highlights: • Y{sub 2}SiO{sub 5}:Ce is prepared by gel combustion in ultrasound conditions (US). • Morpho-structural characteristics are revealed based on FTIR, SEM, XRD, BET. • Incorporation of Ce{sup 3+} in X1/X2 type centers depends on preparative conditions. • US treatment increases the luminescent performances up to 151%. - Abstract: Cerium activated yttrium silicate (Y{sub 2}SiO{sub 5}:Ce) phosphors were prepared by gel-combustion, using yttrium–cerium nitrate as oxidizer, aspartic acid as fuel and TEOS as source of silicon. Two modalities for samples preparation were approached namely: the classical gel-combustion and sonication gel-combustion. The ultrasound treatment during the gelling stage has a positive effect on the structural and luminescent characteristics of the final product. Therefore, a well crystallized single X2–Y{sub 2}SiO{sub 5} phase phosphor was obtained at 1200 °C. Based on FT-IR and XRD investigations, conversion of X1 to X2–Y{sub 2}SiO{sub 5} phases is observed as the firing temperature is varied (1100 °C, 1200 °C, 1300 °C 1400 °C). The ultrasound treatment leads to smaller particle size and enhances the luminescent performances up to 151% in comparison with samples prepared by classical way.

  14. Carbon footprint assessment of recycling technologies for rare earth elements: A case study of recycling yttrium and europium from phosphor.

    Science.gov (United States)

    Hu, Allen H; Kuo, Chien-Hung; Huang, Lance H; Su, Chao-Chin

    2017-02-01

    Rare earth elements are key raw materials in high-technology industries. Mining activities and manufacturing processes of such industries have caused considerable environmental impacts, such as soil erosion, vegetation destruction, and various forms of pollution. Sustaining the long-term supply of rare earth elements is difficult because of the global shortage of rare earth resources. The diminishing supply of rare earth elements has attracted considerable concern because many industrialized countries regarded such elements as important strategic resources for economic growth. This study aims to explore the carbon footprints of yttrium and europium recovery techniques from phosphor. Two extraction recovery methods, namely, acid extraction and solvent extraction, were selected for the analysis and comparison of carbon footprints. The two following functional units were used: (1) the same phosphor amounts for specific Y and Eu recovery concentrations, and (2) the same phosphor amounts for extraction. For acid extraction method, two acidic solutions (H 2 SO 4 and HCl) were used at two different temperatures (60 and 90°C). For solvent extraction method, acid leaching was performed followed by ionic liquid extraction. Carbon footprints from acid and solvent extraction methods were estimated to be 10.1 and 10.6kgCO 2 eq, respectively. Comparison of the carbon emissions of the two extraction methods shows that the solvent extraction method has significantly higher extraction efficiency, even though acid extraction method has a lower carbon footprint. These results may be used to develop strategies for life cycle management of rare earth resources to realize sustainable usage. Copyright © 2016 Elsevier Ltd. All rights reserved.

  15. Synthesis and photoluminescent properties of yttrium vanadate phosphor prepared by the non-hydrolytic sol–gel process

    International Nuclear Information System (INIS)

    Matos, Marcela G.; Faria, Emerson H. de; Rocha, Lucas A.; Calefi, Paulo S.; Ciuffi, Katia J.; Nassar, Eduardo J.; Sarmento, Victor Hugo Vitorino

    2014-01-01

    We used the non-hydrolytic sol–gel route to synthesize YVO 4 crystalline phases doped with europium III ion. We heat-treated the samples at 600, 800, and 1000 °C and characterized the materials by thermal analysis, X-ray diffraction, small-angle X-ray scattering, and photoluminescence. Larger weight loss occurred until 500 °C, ascribed to removal of residual precursor molecules. X-ray diffraction patterns evidenced YVO 4 phase formation at 600 °C. The crystallite size depended on the heat treatment temperature. SAXS showed that the nature of the system interfaces changed as a function of the thermal treatment. The excitation spectra of the samples displayed the charge transfer band. The photoluminescence data revealed the characteristic transition bands arising from the 5 D 0 → 5 F J (J=0, 1, 2, 3, and 4) manifolds under maximum excitation at the charge transfer band and the 5 L 6 level of the Eu 3+ ion. The 5 D 0 → 7 F 2 transition dominated the emission spectra, indicating that the Eu 3+ ion occupies a site without inversion center. The lifetime and quantum efficiency values were about 0.70 ms and 50%, respectively, corroborating literature results. -- Highlights: • This study described the preparation of the yttrium vanadate by non-hydrolytic sol–gel. • The SAXS curves can be interpreted from the fractal theory for a two-phase model. • The goal of the work is the preparation of the phosphors at low temperature. • The lifetimes depend on wavelength of the excitation

  16. Synthesis and photoluminescent properties of yttrium vanadate phosphor prepared by the non-hydrolytic sol–gel process

    Energy Technology Data Exchange (ETDEWEB)

    Matos, Marcela G.; Faria, Emerson H. de; Rocha, Lucas A.; Calefi, Paulo S.; Ciuffi, Katia J. [Universidade de Franca, Av. Dr. Armando Salles Oliveira, 201 Franca, SP, CEP 14404-600 (Brazil); Nassar, Eduardo J., E-mail: ejnassar@unifran.br [Universidade de Franca, Av. Dr. Armando Salles Oliveira, 201 Franca, SP, CEP 14404-600 (Brazil); Sarmento, Victor Hugo Vitorino [Universidade Federal de Sergipe, Av. Ver. Olimpio Grande s/n Itabaiana, SE, CEP 49500-000 (Brazil)

    2014-03-15

    We used the non-hydrolytic sol–gel route to synthesize YVO{sub 4} crystalline phases doped with europium III ion. We heat-treated the samples at 600, 800, and 1000 °C and characterized the materials by thermal analysis, X-ray diffraction, small-angle X-ray scattering, and photoluminescence. Larger weight loss occurred until 500 °C, ascribed to removal of residual precursor molecules. X-ray diffraction patterns evidenced YVO{sub 4} phase formation at 600 °C. The crystallite size depended on the heat treatment temperature. SAXS showed that the nature of the system interfaces changed as a function of the thermal treatment. The excitation spectra of the samples displayed the charge transfer band. The photoluminescence data revealed the characteristic transition bands arising from the {sup 5}D{sub 0}→{sup 5}F{sub J} (J=0, 1, 2, 3, and 4) manifolds under maximum excitation at the charge transfer band and the {sup 5}L{sub 6} level of the Eu{sup 3+} ion. The {sup 5}D{sub 0}→{sup 7}F{sub 2} transition dominated the emission spectra, indicating that the Eu{sup 3+} ion occupies a site without inversion center. The lifetime and quantum efficiency values were about 0.70 ms and 50%, respectively, corroborating literature results. -- Highlights: • This study described the preparation of the yttrium vanadate by non-hydrolytic sol–gel. • The SAXS curves can be interpreted from the fractal theory for a two-phase model. • The goal of the work is the preparation of the phosphors at low temperature. • The lifetimes depend on wavelength of the excitation.

  17. Phosphors

    International Nuclear Information System (INIS)

    1975-01-01

    This invention relates to phosphors that can be used in fluorescent lamps and display devices. The phosphor is comprised of a halophosphate of calcium and/or strontium of apatite crystal structure activated with trivalent cerium and trivalent terbium. The phosphor can further include manganese. Preferably, the phosphor includes up to 10% by weight of one or more of the alkali metals lithium, sodium and potassium in the form of a compound or compounds thereof. The emissions appear as a number of fairly narrow discrete bands. The temperature of preparation is 1000degC (as opposed to the usual 1450degC), therefore reducing costs (less energy is needed, more crucibles are readily obtainable and there is no need for special conditions to enable crucibles to overcome thermal shock)

  18. Study of the solubility of yttrium, praseodymium, neodymium, and gadolinium sulfates in the presence of sodium and potassium in sulfuric-phosphoric acid solutions at 20 deg C

    International Nuclear Information System (INIS)

    Lokshin, Eh.P.; Tareeva, O.A.; Kashulina, T.G.

    2007-01-01

    The solubility of yttrium, praseodymium, neodymium, and gadolinium sulfates in the presence of sodium and potassium ions and the composition of solid phases were studied at 20 deg C in relation to the concentration of acids in sulfuric acid, phosphoric acid, and sulfuric-phosphoric acid solutions containing up to 36 wt % H 2 SO 4 and 33.12 g 1 -1 H 3 PO 4 . The formation of double sulfates of praseodymium and neodymium with sodium and potassium ions, as well as of gadolinium sulfate with sodium ions of the composition 1 : 1 was revealed. In water at 20 deg C, the solubility products of PrNa(SO 4 ) 2 ·H 2 O, NdNa(SO 4 ) 2 ·H 2 O, GdNa(SO 4 ) 2 ·H 2 O, PrK(SO 4 ) 2 ·H 2 O, and NdK(SO 4 ) 2 ·H 2 O are found to be 7.28x10 -8 , 7.84x10 -8 , 3.09x10 -6 , 3.02x10 -6 , and 1.70x10 -6 , respectively [ru

  19. Rare earth phosphors and phosphor screens

    International Nuclear Information System (INIS)

    Buchanan, R.A.; Maple, T.G.; Sklensky, A.F.

    1981-01-01

    Advances in the use of stabilized rare earth phosphors and of conversion screens using these materials are examined. In particular the new phosphors discussed in this invention consist of oxybromides of yttrium, lanthanum and gadolinium with a luminescent activator ion stabilized by an oxychloride or oxyfluoride surface layer and the conversion screens include trivalent cerium as the activator ion. (U.K.)

  20. Formation of Deep Electron Trap by Yb3+ Codoping Leads into Super-Long Persistent Luminescence in Ce3+-doped Yttrium Aluminum Gallium Garnet Phosphors.

    Science.gov (United States)

    Ueda, Jumpei; Miyano, Shun; Tanabe, Setsuhisa

    2018-05-23

    The Y 3 Al 2 Ga 3 O 12 :Ce 3+ -Cr 3+ compound is one of the brightest persistent phosphors, but its persistent luminescence (PersL) duration is not so long due to the relatively shallow Cr 3+ electron trap. Comparing the vacuum referred binding energy of the electron trapping state by Cr 3+ and those by lanthanide ions, we selected Yb 3+ as a deeper electron trapping center. The Y 3 Al 2 Ga 3 O 12 :Ce 3+ -Yb 3+ phosphors show Ce 3+ :5d→4f green persistent luminescence after ceasing blue light excitation. The formation of Yb 2+ was confirmed by the increased intensity of absorption at 585 nm during the charging process. This result indicates that the Yb 3+ ions act as electron traps by capturing an electron. From the thermoluminescence glow curves, it was found the Yb 3+ trap makes much deeper electron trap with 1.01 eV depth than the Cr 3+ electron trap with 0.81 eV depth. This deeper Yb 3+ trap provides much slower detrapping rate of filled electron traps than the Cr 3+ -codoped persistent phosphor. In addition, by preparing transparent ceramics and optimizing Ce 3+ and Yb 3+ concentrations, the Y 3 Al 2 Ga 3 O 12 :Ce 3+ (0.2%)-Yb 3+ (0.1%) as-made transparent ceramic phosphor showed super long persistent luminescence for over 138.8 hours after ceasing blue light charging.

  1. Co-precipitation synthesis and luminescence behavior of Ce-doped yttrium aluminum garnet (YAG:Ce) phosphor: The effect of precipitant

    International Nuclear Information System (INIS)

    Zhang Kai; Liu Hezhou; Wu Yating; Hu Wenbin

    2008-01-01

    YAG:Ce precursors were co-precipitated using ammonia water and ammonium hydrogen carbonate as precipitants, respectively. Phase transition of the precursors during sintering was compared between the two precipitants. The precursors synthesized with ammonia water transformed to YAG at about 1000 deg. C via YAlO 3 phase. The precursors synthesized with ammonium hydrogen carbonate directly converted to pure YAG at about 900 deg. C. Comparing the powders produced with the two precipitants, the powders produced with ammonia hydrogen carbonate showed good dispersity. When sintered at 1600 deg. C, aggregation of the powders synthesized with the two precipitants both became severe. With increase the sintering temperature, the maximum wavelength of excitation and emission spectra of the phosphors synthesized with ammonium water hardly varied. While the maximum wavelength of excitation spectra of the phosphors synthesized with ammonium hydrogen carbonate unchanged, and the emission spectra showed red shift. Because of size effect and higher loss of cerium content, the emission intensity of phosphors prepared with ammonium hydrogen carbonate was lower than the phosphors prepared with ammonium water, when sintered at the same temperature

  2. Magneto-optical studies of valence instability in europium and terbium phosphors

    Czech Academy of Sciences Publication Activity Database

    Rodrigues, L.C.v.; Hölsä, J.; Brito, H.F.; Maryško, Miroslav; Matos, J.R.; Paturi, P.; Rodrigues, R.V.; Lastusaari, M.

    2016-01-01

    Roč. 170, Feb (2016), 701-706 ISSN 0022-2313 Institutional support: RVO:68378271 Keywords : valence * europium * terbium * oxysulfide and -sulfate * phosphors * paramagnetic susceptibility Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.686, year: 2016

  3. Processing and characterization of new oxysulfide glasses in the Ge-Ga-As-S-O system

    International Nuclear Information System (INIS)

    Maurel, C.; Petit, L.; Dussauze, M.; Kamitsos, E.I.; Couzi, M.; Cardinal, T.; Miller, A.C.; Jain, H.; Richardson, K.

    2008-01-01

    New oxysulfide glasses have been prepared in the Ge-Ga-As system employing a two-step melting process which involves the processing of the chalcogenide glass (ChG) and its subsequent melting with amorphous GeO 2 powder. Optical characterization of the synthesized oxysulfide glasses has shown that the cut-off wavelength decreases with increasing oxygen content, and this has been correlated to results of Raman and infrared (IR) spectroscopies which show the formation of new oxysulfide structural units. X-ray photoelectron spectroscopy (XPS) analysis to probe the bonding environment of oxygen atoms in the oxysulfide glass network, has revealed the preferred formation of Ga-O and Ge-O bonds in comparison to As-O bonds. This work has demonstrated that melting a ChG glass with GeO 2 leads to the formation of new oxysulfide glassy materials. - Graphical abstract: In this paper, we explain how new oxysulfide glasses are prepared in the Ge-Ga-As system employing a two-step process: (1) the processing of the chalcogenide glass (ChG) and (2) the re-melting of the ChG with GeO 2 powder. Raman, infrared and XPS spectroscopies show the formation of new oxysulfide structural units

  4. Bismuth Silver Oxysulfide for Photoconversion Applications: Structural and Optoelectronic Properties

    KAUST Repository

    Baqais, Amal Ali Abdulallh; Curutchet, Antton; Ziani, Ahmed; Ait Ahsaine, Hassan; Sautet, Philippe; Takanabe, Kazuhiro; Le Bahers, Tangui

    2017-01-01

    Single-phase bismuth silver oxysulfide, BiAgOS, was prepared by a hydrothermal method. Its structural, morphological and optoelectronic properties were investigated and compared with bismuth copper oxysulfide (BiCuOS). Rietveld refinement of the powder X-ray diffraction (XRD) measurements revealed that the BiAgOS and BiCuOS crystals have the same structure as ZrSiCuAs: the tetragonal space group P4/nmm. X-ray photoelectron spectroscopy (XPS) analyses confirmed that the BiAgOS has a high purity, in contrast with BiCuOS, which tends to have Cu vacancies. The Ag has a monovalent oxidation state, whereas Cu is present in the oxidation states of +1 and +2 in the BiCuOS system. Combined with experimental measurements, density functional theory calculations employing the range-separated hybrid HSE06 exchange-correlation functional with spin-orbit coupling quantitatively elucidated photophysical properties such as ab-sorption coefficients, effective masses and dielectric constants. BiCuOS and BiAgOS were found to have indirect bandgaps of 1.1 and 1.5 eV, respectively. Both possess high dielectric constants and low electron and hole effective masses. Therefore, these materials are expected to have high exciton dissociation capabilities and excellent carrier diffusion properties. This study reveals that BiAgOS is a promising candidate for photoconversion applications.

  5. Bismuth Silver Oxysulfide for Photoconversion Applications: Structural and Optoelectronic Properties

    KAUST Repository

    Baqais, Amal Ali Abdulallh

    2017-09-18

    Single-phase bismuth silver oxysulfide, BiAgOS, was prepared by a hydrothermal method. Its structural, morphological and optoelectronic properties were investigated and compared with bismuth copper oxysulfide (BiCuOS). Rietveld refinement of the powder X-ray diffraction (XRD) measurements revealed that the BiAgOS and BiCuOS crystals have the same structure as ZrSiCuAs: the tetragonal space group P4/nmm. X-ray photoelectron spectroscopy (XPS) analyses confirmed that the BiAgOS has a high purity, in contrast with BiCuOS, which tends to have Cu vacancies. The Ag has a monovalent oxidation state, whereas Cu is present in the oxidation states of +1 and +2 in the BiCuOS system. Combined with experimental measurements, density functional theory calculations employing the range-separated hybrid HSE06 exchange-correlation functional with spin-orbit coupling quantitatively elucidated photophysical properties such as ab-sorption coefficients, effective masses and dielectric constants. BiCuOS and BiAgOS were found to have indirect bandgaps of 1.1 and 1.5 eV, respectively. Both possess high dielectric constants and low electron and hole effective masses. Therefore, these materials are expected to have high exciton dissociation capabilities and excellent carrier diffusion properties. This study reveals that BiAgOS is a promising candidate for photoconversion applications.

  6. Bismuth Oxysulfide and Its Polymer Nanocomposites for Efficient Purification

    Directory of Open Access Journals (Sweden)

    Yidong Luo

    2018-03-01

    Full Text Available The danger of toxic organic pollutants in both aquatic and air environments calls for high-efficiency purification material. Herein, layered bismuth copper oxychalcogenides, BiCuSO, nanosheets of high photocatalytic activity were introduced to the PVDF (Polyvinylidene Fluoride. The fibrous membranes provide an easy, efficient, and recyclable way to purify organic pollutant. The physical and photophysical properties of the BiCuSO and its polymer composite were characterized by scanning electron microscopy (SEM, X-ray diffraction (XRD, ultraviolet-visible diffuse reflection spectroscopy (DRS, X-ray photoelectron spectroscopy (XPS, electron spin resonance (EPR. Photocatalysis of Congo Red reveals that the BiCuSO/PVDF shows a superior photocatalytic activity of a 55% degradation rate in 70 min at visible light. The high photocatalytic activity is attributed to the exposed active {101} facets and the triple vacant associates V B i ‴ V O • • V B i ‴ . By engineering the intrinsic defects on the surface of bismuth oxysulfide, high solar-driven photocatalytic activity can be approached. The successful fabrication of the bismuth oxysulfide and its polymer nanocomposites provides an easy and general approach for high-performance purification materials for various applications.

  7. Solvent extraction studies on separation of yttrium from xenotime

    International Nuclear Information System (INIS)

    Singh, D.K.; Anitha, M.; Kain, V.

    2017-01-01

    Rare earths consists a group of 15 element from La to Lu in the periodic table and it also includes Sc and Y since they tend to occur in the same ore deposits as the lanthanides and exhibit similar chemical properties. The unique physical-chemical properties of the REEs render them important in applications as varies as high strength magnets, lighting phosphors, policing compounds and ceramics. In particular, yttrium finds numerous applications in many areas including superconductors, lasers, phosphors, nuclear reactors, astronavigation, ceramics etc. Yttrium is chemically similar to heavy rare earths (HRE: terbium, dysprosium, erbium, holmium, ytterbium, thulium and lutecium). Yttrium behaves like HRE due to similarity in ionic radius and finds place between Ho and Er. The cross current profile in terms of the plot of concentration of yttrium in raffinate as a function of contact number indicated the complete recovery of rare earths from nitrate solution of xenotime wet cake

  8. Yttrium-90

    International Nuclear Information System (INIS)

    Ammerich, Marc; Frot, Patricia; Gambini, Denis-Jean; Gauron, Christine; Moureaux, Patrick; Herbelet, Gilbert; Lahaye, Thierry; Pihet, Pascal; Rannou, Alain; Vial, Eric

    2013-03-01

    This sheet belongs to a collection which relates to the use of radionuclides essentially in unsealed sources. Its goal is to gather on a single document the most relevant information as well as the best prevention practices to be implemented. These sheets are made for the persons in charge of radiation protection: users, radioprotection-skill persons, labor physicians. Each sheet treats of: 1 - the radio-physical and biological properties; 2 - the main uses; 3 - the dosimetric parameters; 4 - the measurement; 5 - the protection means; 6 - the areas delimitation and monitoring; 7 - the personnel classification, training and monitoring; 8 - the effluents and wastes; 9 - the authorization and declaration administrative procedures; 10 - the transport; and 11 - the right conduct to adopt in case of incident or accident. This sheet deals specifically with Yttrium-90

  9. Production of yttrium

    International Nuclear Information System (INIS)

    Day, J.G.

    1980-01-01

    A process is described for the production of yttrium metal, or of an alloy comprising a major proportion of yttrium, in which calcium (metal) and yttrium fluoride are reacted together by use of a submerged electric arc in a molten slag. (author)

  10. The BiCu{sub 1−x}OS oxysulfide: Copper deficiency and electronic properties

    Energy Technology Data Exchange (ETDEWEB)

    Berthebaud, D.; Guilmeau, E.; Lebedev, O.I. [Laboratoire CRISMAT, UMR 6508 CNRS/ENSICAEN/UCBN, 6 bd du Maréchal Juin, F-14050 CAEN Cedex 4 (France); Maignan, A., E-mail: antoine.maignan@ensicaen.fr [Laboratoire CRISMAT, UMR 6508 CNRS/ENSICAEN/UCBN, 6 bd du Maréchal Juin, F-14050 CAEN Cedex 4 (France); Gamon, J.; Barboux, P. [Institut de Recherche de Chimie de Paris, Ecole Nationale Supérieure de Chimie de Paris, 11 rue Pierre et Marie Curie, 75231 Paris Cedex 09 France (France)

    2016-05-15

    An oxysulfide series of nominal compositions BiCu{sub 1−x}OS with x<0.20 has been prepared and its structural properties characterized by combining powder X-ray diffraction and transmission electron microscopy techniques. It is found that this oxysulfide, crystallizing in the P4/nmm space group, tends to adopt a constant amount of copper vacancy corresponding to x=0.05 in the BiCu{sub 1−x}OS formula. The presence of Cu vacancies is confirmed by HAADF-STEM analysis showing, in the Cu atomic columns, alternating peaks of different intensities in some very localized regions. For larger Cu deficiencies (x>0.05 in the nominal composition), other types of structural nanodefects are evidenced such as bismuth oxysulfides of the “BiOS” ternary system which might explain the report of superconductivity for the BiCu{sub 1−x}OS oxysulfide. Local epitaxial growth of the BiCuOS oxysulfide on top of CuO is also observed. In marked contrast to the BiCu{sub 1−x}OSe oxyselenide, these results give an explanation to the limited impact of Cu deficiency on the Seebeck coefficient in BiCu{sub 1−x}OS compounds. - Graphical abstract: High resolution TEM image showing a Bi(Cu)OS/Bi{sub 2}O{sub 2}S interface and corresponding dislocation region. The Bi(Cu)OS structure adopts a rather constant Cu content (near 0.95); starting from BiCuOS leads to the formation of defects such as the Bi{sub 2}O{sub 2}S oxysulfide.

  11. Electron-beam-pumped phosphors

    International Nuclear Information System (INIS)

    Goldhar, J.; Krupke, W.F.

    1985-01-01

    Electron-beam excitation of solid-state scintillators, or phosphors, can result in efficient generation of visible light confined to relatively narrow regions of the spectrum. The conversion efficiency can exceed 20%, and, with proper choice of phosphors, radiation can be obtained anywhere from the near infrared (IR) to the near ultraviolet (UV). These properties qualify the phosphors as a potentially useful pump source for new solid-state lasers. New phosphors are being developed for high-brightness television tubes that are capable of higher power dissipation. Here, an epitaxial film of fluorescing material is grown on a crystalline substrate with good thermal properties. For example, researchers at North American Philips Laboratories have developed a cerium-doped yttrium aluminum garnet (YAG) grown on a YAG substrate, which has operated at 1 A/cm 2 at 20 kV without observed thermal quenching. The input power is higher by almost two orders of magnitude than that which can be tolerated by a conventional television phosphor. The authors describe tests of these new phosphors

  12. Thermoluminescent phosphor

    Science.gov (United States)

    Lasky, Jerome B.; Moran, Paul R.

    1978-01-01

    A thermoluminescent phosphor comprising LiF doped with boron and magnesium is produced by diffusion of boron into a conventional LiF phosphor doped with magnesium. Where the boron dopant is made to penetrate only the outer layer of the phosphor, it can be used to detect shallowly penetrating radiation such as tritium beta rays in the presence of a background of more penetrating radiation.

  13. Properties of precipitates formed during ammonization of extractional phosphoric acid

    International Nuclear Information System (INIS)

    Zakharova, B.S.; Komissarova, L.N.; Naumov, S.V.; Traskin, V.Yu.

    1992-01-01

    Dimensions of precipitated rare-earth phosphate particles -(0.1 μm)- are near the boundary of colloidal system sedimentation stability range at neutralization of extraction phosphoric acid. Thus, formation of multiple aggregates of colloidal particles results in immediate sedimentation of the precipitate. Processes occurring within the system may be described using second order reaction equation. Average efficient size of precipitates grows at reduction of reaction mixture pH. About 30% of rare-earth elements and yttrium in the extraction phosphoric acid is extracted from it; concentration of rare-earth elements, yttrium and scandium in precipitate is maximum 2 mass. %

  14. Nano-aggregates of cobalt nickel oxysulfide as a high-performance electrode material for supercapacitors

    Science.gov (United States)

    Liu, Lifeng

    2013-11-01

    Nano-aggregates of cobalt nickel oxysulfide (CoNi)OxSy have been synthesized by hydrothermal processing and exhibited specific and areal capacitance as high as 592 F g-1 and 1628 mF cm-2, respectively, at a current density of 0.5 A g-1/1.375 mA cm-2. They also show high capacitance retention upon extended cycling at high rates.Nano-aggregates of cobalt nickel oxysulfide (CoNi)OxSy have been synthesized by hydrothermal processing and exhibited specific and areal capacitance as high as 592 F g-1 and 1628 mF cm-2, respectively, at a current density of 0.5 A g-1/1.375 mA cm-2. They also show high capacitance retention upon extended cycling at high rates. Electronic supplementary information (ESI) available: Experimental details; supplementary tables. See DOI: 10.1039/c3nr03533f

  15. Synthesis of yttrium silicate luminescent materials by sol-gel method

    International Nuclear Information System (INIS)

    Arkhipov, D.V.; Vasina, O.Yu.; Popovich, N.V.; Galaktionov, S.S.; Soshchin, N.P.

    1996-01-01

    Several yttrium-silicate composition with Y 2 O 3 content within 44-56% have been synthesized. it is ascertained that employment of sol-gel technique permits preparation of luminescent materials on yttrium silicate basis, which compare favourably with bath-produced specimens. The influence of phase composition of sol-gel phosphors on basic performance indices: intensity and luminescence spectrum, has been analyzed

  16. Phosphors containing boron and metals of Group IIIA and IIIB

    Science.gov (United States)

    Setlur, Anant Achyut; Srivastava, Alok Mani; Comanzo, Holly Ann; Manivannan, Venkatesan

    2006-10-31

    A phosphor comprises: (a) at least a first metal selected from the group consisting of yttrium and elements of lanthanide series other than europium; (b) at least a second metal selected from the group consisting of aluminum, gallium, indium, and scandium; (c) boron; and (d) europium. The phosphor is used in light source that comprises a UV radiation source to convert UV radiation to visible light.

  17. Re-processing CRT phosphors for mercury-free applications

    International Nuclear Information System (INIS)

    Dexpert-Ghys, Jeannette; Regnier, Sophie; Canac, Sophie; Beaudette, Tristan; Guillot, Philippe; Caillier, Bruno; Mauricot, Robert; Navarro, Julien; Sekhri, Salem

    2009-01-01

    This study is part of an operation in the framework of treatment and revalorization of IEEE (Informatics, Electronics and related) wastes. It aims to recover the active phosphors in cathode ray tubes (CRTs) and to re-cycle these powders by appropriate treatments as phosphors for mercury-free applications such as plasma display panels, flat lamps, advertising and lighting. The studied waste comes from a large panel of CRTs from any supplier. Several thermo-chemical treatments have been investigated. The removal of zinc sulfide-based phosphors and the recovery of a red phosphor Y 2 O 3 :Eu 3+ has been achieved by one (basic attack) route. The photoluminescence efficiency under VUV excitation of the obtained powders is at most 30% that of a commercial phosphor. The second route (acid attack) appears less promising. It has been established that silicate-based impurities could prevent isolating the yttrium based phosphor.

  18. Re-processing CRT phosphors for mercury-free applications

    Energy Technology Data Exchange (ETDEWEB)

    Dexpert-Ghys, Jeannette, E-mail: jdexpert@cemes.f [CEMES, 29 rue Jeanne Marvig, BP 94347, 31055 Toulouse cedex 4 (France); Regnier, Sophie; Canac, Sophie [ICAM, 75 avenue de Grande Bretagne, 31300 Toulouse (France); Beaudette, Tristan; Guillot, Philippe; Caillier, Bruno [DPHE, Universite Jean Francois Champollion, place de Verdun, 81012 Albi cedex 9 (France); Mauricot, Robert; Navarro, Julien [CEMES, 29 rue Jeanne Marvig, BP 94347, 31055 Toulouse cedex 4 (France); Sekhri, Salem [ENVOI, Cheminement Glueck, 31100 Toulouse (France)

    2009-12-15

    This study is part of an operation in the framework of treatment and revalorization of IEEE (Informatics, Electronics and related) wastes. It aims to recover the active phosphors in cathode ray tubes (CRTs) and to re-cycle these powders by appropriate treatments as phosphors for mercury-free applications such as plasma display panels, flat lamps, advertising and lighting. The studied waste comes from a large panel of CRTs from any supplier. Several thermo-chemical treatments have been investigated. The removal of zinc sulfide-based phosphors and the recovery of a red phosphor Y{sub 2}O{sub 3}:Eu{sup 3+} has been achieved by one (basic attack) route. The photoluminescence efficiency under VUV excitation of the obtained powders is at most 30% that of a commercial phosphor. The second route (acid attack) appears less promising. It has been established that silicate-based impurities could prevent isolating the yttrium based phosphor.

  19. Diffusion of hydrogen in yttrium

    International Nuclear Information System (INIS)

    Vorobyov, V.V.; Ryabchikov, L.N.

    1966-01-01

    In this work the diffusion coefficients of hydrogen in yttrium were determined from the rate at which the hydrogen was released from yttrium samples under a vacuum at temperatures of 450 to 850 0 C and from the quantity of hydrogen retained by yttrium at hydrogen pressures below 5 x 10 - 4 mm Hg in the same temperature range

  20. Magnetic properties of layered oxysulfide (LnO)CuS:Ln = La, Pr, Nd

    International Nuclear Information System (INIS)

    Nakao, H.; Takano, Y.; Takase, K.; Sato, K.; Hara, S.; Ikeda, S.; Takahashi, Y.; Sekizawa, K.

    2006-01-01

    We have prepared rare earth oxysulfides (PrO)CuS and (NdO)CuS in order to introduce magnetic moments into the non-magnetic p-type semiconductor (LaO)CuS. Both compounds are semiconductors with high electrical resistivity, and show the paramagnetic behavior. The temperature dependence of the magnetic susceptibility is well explained by the trivalent rare earth ion. However, it deviates from simple Curie Wiess law below 100 K due to the crystal field effect on rare earth ions. We have succeeded to reproduce their magnetic properties by the calculation taking the crystal field effect into account using the operator equivalent method

  1. Fluorescent lighting with aluminum nitride phosphors

    Science.gov (United States)

    Cherepy, Nerine J.; Payne, Stephen A.; Seeley, Zachary M.; Srivastava, Alok M.

    2016-05-10

    A fluorescent lamp includes a glass envelope; at least two electrodes connected to the glass envelope; mercury vapor and an inert gas within the glass envelope; and a phosphor within the glass envelope, wherein the phosphor blend includes aluminum nitride. The phosphor may be a wurtzite (hexagonal) crystalline structure Al.sub.(1-x)M.sub.xN phosphor, where M may be drawn from beryllium, magnesium, calcium, strontium, barium, zinc, scandium, yttrium, lanthanum, cerium, praseodymium, europium, gadolinium, terbium, ytterbium, bismuth, manganese, silicon, germanium, tin, boron, or gallium is synthesized to include dopants to control its luminescence under ultraviolet excitation. The disclosed Al.sub.(1-x)M.sub.xN:Mn phosphor provides bright orange-red emission, comparable in efficiency and spectrum to that of the standard orange-red phosphor used in fluorescent lighting, Y.sub.2O.sub.3:Eu. Furthermore, it offers excellent lumen maintenance in a fluorescent lamp, and does not utilize "critical rare earths," minimizing sensitivity to fluctuating market prices for the rare earth elements.

  2. Structural, physical and electrochemical characteristics of a vanadium oxysulfide, a cathode material for lithium batteries

    Science.gov (United States)

    Ouvrard, G.; Tchangbédji, G.; Deniard, P.; Prouzet, E.

    A vanadium oxysulfide is obtained by a reaction between water solutions of a vanadyl salt and sodium sulfide at room temperature. After drying under mild conditions, the formulation of this phase is V 2O 3S·3H 2O. Thermogravimetric analyses show that it is not possible to remove completely water without losing sulfur. This is in agreement with proton nuclear magnetic resonance experiments which prove that water molecules are tightly bonded to vanadium. Magnetic susceptibility and X-ray absorption spectroscopy measurements allow to define the oxidation states of vanadium and sulfur, (IV) and (-II) respectively. From extended X-ray absorption fine structure spectroscopy at the vanadium K edge and infrared spectroscopy, the local structure around vanadium can be defined as a distorted octahedron, with a vanadyl bond and an opposite sulfur atom. Magnetic susceptibility and X-ray absorption spectroscopy measurements on chemically lithiated compounds show a complex charge transfer from lithium to the host structure upon lithium intercalation. If it appears that vanadium atoms are reduced, a possible role of sulfur atoms in the redox process has to be considered. Cycling tests of lithium batteries whose positive consists of oxysulfide are promising with 70 cycles under a regime of {C}/{8}, without noticeable loss in capacity of 120 Ah/kg.

  3. Cathodoluminescence properties of yttrium aluminum garnet doped with Eu2+ and Eu3+ ions

    International Nuclear Information System (INIS)

    Trofimov, A. N.; Petrova, M. A.; Zamoryanskaya, M. V.

    2007-01-01

    Yttrium aluminium garnet (YAG) doped with Eu 2+ and Eu 3+ ions is very interesting as a phosphor for conversion of light-emitting diode light for white light sources. The europium ion occupies the structural position of yttrium in yttrium aluminium garnet and has valence state Eu 3+ . Our sample was doped with Zr 4+ , which is why some of the europium ions had valence state Eu 2+ . As a rule, luminescence of Eu 3+ ions is observed in the orange and red range of spectrum. The luminescence of Eu 2+ in yttrium aluminum garnet is characterized by an intensive broad band with maximum of intensity at about 560 nm (green color). In this work, we studied the intensity and decay time dependences on europium concentration, and the influence of excitation power density on the cathodoluminescence of the sample. The most interesting result is the change of visible cathodoluminescence color in dependence on the density of the exciting power

  4. Lanthanoid and yttrium tellurates

    Energy Technology Data Exchange (ETDEWEB)

    Gonalez, C G; Guedes de Carvalho, R A [Faculdade de Engenharia, Porto (Portugal). Centro de Engenharia Quimica

    1978-05-01

    Preparation in aqueous medium of all the lanthanoid (except Ce and Pm) and yttrium tellurates is described. Chemical analyses, solubilities at 25/sup 0/C in water and thermograms of all the products prepared were determined. X-ray diffractograms and DTA and DTG curves of La, Gd and Yb tellurates were obtained and commented. Partial volatilization of lanthanoid is observed in the thermal analysis of tellurates.

  5. A new continuous two-step molecular precursor route to rare-earth oxysulfides Ln2O2S

    International Nuclear Information System (INIS)

    De Crom, N.; Devillers, M.

    2012-01-01

    A continuous two-step molecular precursor pathway is designed for the preparation of rare-earth oxysulfides Ln 2 O 2 S (Ln=Y, La, Pr, Nd, Sm–Lu). This new route involves a first oxidation step leading to the rare-earth oxysulfate Ln 2 O 2 SO 4 which is subsequently reduced to the rare-earth oxysulfide Ln 2 O 2 S by switching to a H 2 –Ar atmosphere. The whole process occurs at a temperature significantly lower than usual solid state synthesis (T≤650 °C) and avoids the use of dangerous sulfur-based gases, providing a convenient route to the synthesis of the entire series of Ln 2 O 2 S. The molecular precursors consist in heteroleptic dithiocarbamate complexes [Ln(Et 2 dtc) 3 (phen)] and [Ln(Et 2 dtc) 3 (bipy)] (Et 2 dtc=N,N-diethyldithiocarbamate; phen=1,10-phenanthroline; bipy=2,2′-bipyridine) and were synthesized by a new high yield and high purity synthesis route. The nature of the molecular precursor determines the minimum synthesis temperature and influences therefore the purity of the final Ln 2 O 2 S crystalline phase. - Graphical abstract: A continuous two-step molecular precursor pathway was designed for the preparation of rare-earth oxysulfides Ln 2 O 2 S (Ln=Y, La, Pr, Nd, Sm–Lu), starting from heteroleptic dithiocarbamate complexes. The influence of the nature of the molecular precursor on the minimum synthesis temperature and on the purity of the final Ln 2 O 2 S crystalline phase is discussed. Highlights: ► A new high yield and high purity synthesis route of rare earth dithiocarbamates is described. ► These compounds are used as precursors in a continuous process leading to rare-earth oxysulfides. ► The oxysulfides are obtained under much more moderate conditions than previously described.

  6. Oxidizer in phosphoric reactors

    International Nuclear Information System (INIS)

    Santos Benedetto, J. dos

    1985-01-01

    Oxidation during the manufacture of wet-process phosphoric acid affected the distribution of uranium and impurities between phosphoric acid and gypsum, by decreasing the uranium loss to gypsum and the impurities solubilization in phosphoric acid. (Author) [pt

  7. Yttrium-90 - ED 4310

    International Nuclear Information System (INIS)

    Ammerich, M.; Frot, P.; Gambini, D.; Gauron, C.; Moureaux, P.; Herbelet, G.; Lahaye, T.; Pihet, P.; Rannou, A.; Vidal, E.

    2013-03-01

    This sheet presents the characteristics of yttrium-90, its origin, and its radio-physical and biological properties. It briefly describes its use in nuclear medicine. It indicates its dosimetric parameters for external exposure, cutaneous contamination, and internal exposure due to acute contamination or to chronic contamination. It indicates and comments the various exposure control techniques: ambient dose rate measurement, surface contamination measurement, atmosphere contamination. It addresses the means of protection: premise design, protection against external exposure and against internal exposure. It describes how areas are delimited and controlled within the premises: regulatory areas, controls to be performed. It addresses the personnel classification, training and medical survey. It addresses the issue of solid and liquid wastes and liquid or gaseous effluents. It briefly recalls the administrative procedures related to the authorization and declaration of possession and use of sealed and unsealed sources. It indicates regulatory aspects related to the transport of yttrium-90, describes what is to be done in case of incident or accident (for the different types of contamination or exposure)

  8. Europium determination in oxide and oxysulfide luminophors and their wastes by the method of direct and derivative spectrophotometry

    International Nuclear Information System (INIS)

    Mishchenko, V.T.; Aleksandrova, N.N.

    1989-01-01

    Spectrophotometric methods for europium determination in luminophors are proposed. Application of standard and derivative spectrophotometry allows one to determine europium in oxide and oxysulfide luminophors, their wastes and raffinates produced during waste reprocessing quite accurately and reliably. When determining Eu 2 O 3 (Eu 2 O 2 S) mass shares within 4-8 % limits absolute deviation from the mean result makes up to more than ± 0.2 %, relative standard deviation does not exceed 0.02

  9. Scandium, yttrium and the lanthanides

    International Nuclear Information System (INIS)

    Hart, F.A.

    1987-01-01

    This chapter on the chemistry of the coordination complexes of scandium, yttrium and the lanthanides includes sections on the nitrogen and oxygen donor ligands and complex halides of scandium, and the phosphorus and sulfur donor ligands of yttrium and the lanthanides. Complexes with the macrocylic ligands and with halides are also discussed. Sections on the NMR and electronic spectra of the lanthanides are also included. (UK)

  10. Practical applications of phosphors

    CERN Document Server

    Yen, William M; Yamamoto, Hajime

    2006-01-01

    Drawn from the second edition of the best-selling Phosphor Handbook, Practical Applications of Phosphors outlines methods for the production of various phosphors and discusses a broad spectrum of applications. Beginning with methods for synthesis and related technologies, the book sets the stage by classifying and then explaining practical phosphors according to usage. It describes the operating principle and structure of phosphor devices and the phosphor characteristics required for a given device, then covers the manufacturing processes and characteristics of phosphors. The book discusses research and development currently under way on phosphors with potential for practical usage and touches briefly on phosphors that have played a historical role, but are no longer of practical use. It provides a comprehensive treatment of applications including lamps and cathode-ray tubes, x-ray and ionizing radiation, and for vacuum fluorescent and field emission displays and covers inorganic and organic electroluminescen...

  11. UV absorption coefficients of Y2(1-x-y)Gd2xEu2yO3 phosphors

    International Nuclear Information System (INIS)

    Ling, M.; Yocom, P.W.; Soules, T.F.

    1990-01-01

    The ability of a phosphor to absorb 254 nm excitation is important in the development of phosphors for fluorescent lamps. Recently the optical properties of phosphor coating were modeled using ray tracing Monte-Carlo techniques. These calculations provided a relationship between absorptance measured on a semi-infinite plaque at a given wavelength and the product of the absorption coefficient of the phosphor and its particle diameter. The purpose of this work is to provide experimental data for comparison with the calculated data, to demonstrate a technique for obtaining absorption coefficients and to provide UV absorption coefficients obtained in this way for important yttrium oxide europium red-emitting phosphors

  12. Yttrium and lanthanum recovery from low cerium carbonate, yttrium carbonate and yttrium concentrate

    International Nuclear Information System (INIS)

    Vasconcelos, Mari Estela de

    2006-01-01

    In this work, separation, enrichment and purification of lanthanum and yttrium were performed using as raw material a commercial low cerium rare earth concentrate named LCC (low cerium carbonate), an yttrium concentrate named 'yttrium carbonate', and a third concentrated known as 'yttrium earths oxide. The first two were industrially produced by the late NUCLEMON - NUCLEBRAS de Monazita e Associados Ltda, using Brazilian monazite. The 'yttrium earths oxide' come from a process for preparation of lanthanum during the course of the experimental work for the present thesis. The following techniques were used: fractional precipitation with urea; fractional leaching of the LCC using ammonium carbonate; precipitation of rare earth peroxycarbonates starting from the rare earth complex carbonates. Once prepared the enriched rare earth fractions the same were refined using the ion exchange chromatography with strong cationic resin without the use of retention ion and elution using the ammonium salt of ethylenediaminetetraacetic acid. With the association of the above mentioned techniques were obtained pure oxides of yttrium (>97,7%), lanthanum (99,9%), gadolinium (96,6%) and samarium (99,9%). The process here developed has technical and economic viability for the installation of a large scale unity. (author)

  13. Mechanical properties of layered oxysulfide CaZnOS from first principle calculations

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Zhi-Jun [Department of Physics, Dongguk University, Pildong-ro, Choong-gu, Seoul, 100-715 (Korea, Republic of); Feng, Ang [Key Laboratory of Transparent Opto-Functional Inorganic Materials of Chinese Academy of Sciences, Shanghai Institute of Ceramics, Shanghai, 200050 (China); Zhang, Shao-Lin; Zhang, Wei-Bin [Department of Physics, Dongguk University, Pildong-ro, Choong-gu, Seoul, 100-715 (Korea, Republic of); Yang, Woochul, E-mail: wyang@dongguk.edu [Department of Physics, Dongguk University, Pildong-ro, Choong-gu, Seoul, 100-715 (Korea, Republic of)

    2016-06-15

    Elastic and tensile properties of mixed-anion oxysulfide CaZnOS have been theoretically investigated by first principle method of density functional theory (DFT). Elastic constants were obtained by stress–strain relationships, and bulk structure parameters including bulk modulus, shear modulus, as well as Poisson's ratio were then calculated using Voigt-Reuses-Hill (VRH) approximation. The results of shear anisotropic factors, compressibility anisotropic factor and directional Young's modulus showed that CaZnOS is almost elastically isotropic in {001} planes and maintains elastic anisotropy in {100} or {010} planes. Chemical bond anisotropy shown by Mulliken atomic charges and bond overlap populations is responsible for the elastic anisotropy behavior aforementioned. Moreover, theoretical uniaxial and biaxial tensile results showed the crystal collapsed at strain more than 12%, except in the biaxial extension where CaZnOS collapsed at strain of 7%. - Highlights: • Elastic and theoretical tensile properties of CaZnOS have been investigated by first principle method. • CaZnOS is elastically isotropic in {001} planes and maintains elastic anisotropy in {100} or {010} planes. • Mulliken atomic charges and bond overlap populations are responsible for the elastic anisotropy behavior.

  14. Silicon Oxysulfide, OSiS: Rotational Spectrum, Quantum-Chemical Calculations, and Equilibrium Structure.

    Science.gov (United States)

    Thorwirth, Sven; Mück, Leonie Anna; Gauss, Jürgen; Tamassia, Filippo; Lattanzi, Valerio; McCarthy, Michael C

    2011-06-02

    Silicon oxysulfide, OSiS, and seven of its minor isotopic species have been characterized for the first time in the gas phase at high spectral resolution by means of Fourier transform microwave spectroscopy. The equilibrium structure of OSiS has been determined from the experimental data using calculated vibration-rotation interaction constants. The structural parameters (rO-Si = 1.5064 Å and rSi-S = 1.9133 Å) are in very good agreement with values from high-level quantum chemical calculations using coupled-cluster techniques together with sophisticated additivity and extrapolation schemes. The bond distances in OSiS are very short in comparison with those in SiO and SiS. This unexpected finding is explained by the partial charges calculated for OSiS via a natural population analysis. The results suggest that electrostatic effects rather than multiple bonding are the key factors in determining bonding in this triatomic molecule. The data presented provide the spectroscopic information needed for radio astronomical searches for OSiS.

  15. Fundamentals of phosphors

    CERN Document Server

    Yen, William M; Yamamoto, Hajime

    2006-01-01

    Drawing from the second edition of the best-selling Handbook of Phosphors, Fundamentals of Phosphors covers the principles and mechanisms of luminescence in detail and surveys the primary phosphor materials as well as their optical properties. The book addresses cutting-edge developments in phosphor science and technology including oxynitride phosphors and the impact of lanthanide level location on phosphor performance.Beginning with an explanation of the physics underlying luminescence mechanisms in solids, the book goes on to interpret various luminescence phenomena in inorganic and organic materials. This includes the interpretation of the luminescence of recently developed low-dimensional systems, such as quantum wells and dots. The book also discusses the excitation mechanisms by cathode-ray and ionizing radiation and by electric fields to produce electroluminescence. The book classifies phosphor materials according to the type of luminescence centers employed or the class of host materials used and inte...

  16. Synthesis and characterization of physical properties of Gd{sub 2}O{sub 2}S:Pr{sup 3+} semi-nanoflower phosphor

    Energy Technology Data Exchange (ETDEWEB)

    Bagheri, A.; Rezaee Ebrahim Saraee, Kh.; Shakur, H.R. [University of Isfahan, Department of Nuclear Engineering, Faculty of Advance Sciences and Technologies, Isfahan (Iran, Islamic Republic of); Zamani Zeinali, H. [Nuclear Science and Technology Research Institute, Agriculture, Medical and Industrial Research School, Karaj (Iran, Islamic Republic of)

    2016-05-15

    Pure gadolinium oxysulfide phosphor (Gd{sub 2}O{sub 2}S) and trivalent praseodymium-doped gadolinium oxysulfide phosphor (Gd{sub 2}O{sub 2}S:Pr{sup 3+}) scintillators with semi-nanoflower crystalline structures were successfully synthesized through a precipitation method and subsequent calcination treatment as a converter for X-ray imaging detectors. The characterization such as the crystal structures and nanostructure of Gd{sub 2}O{sub 2}S:Pr{sup 3+} scintillator measured by XRD and FeE-SEM experiment. The optical properties of Gd{sub 2}O{sub 2}S:Pr{sup 3+} scintillator were studied. Luminescence spectra of Gd{sub 2}O{sub 2}S:Pr{sup 3+} under 320 nm UV excitation show a green emission at near 511 nm corresponding to the {sup 3}P{sub 0}-{sup 3}H{sub 4} of Pr ions. After scintillation properties of synthesized Gd{sub 2}O{sub 2}S:Pr{sup 3+} scintillator investigated, Gd{sub 2}O{sub 2}S:Pr{sup 3+} scintillating film fabricated on a glass substrate by a sedimentation method. X-ray imaging of the fabricated scintillators confirmed that the Gd{sub 2}O{sub 2}S:Pr{sup 3+} scintillator could be used for radiography applications in which good spatial resolution is needed. (orig.)

  17. Monte Carlo Investigation of Phosphor Screens for X-ray Imaging

    International Nuclear Information System (INIS)

    Lim, Chang Hwy; Cheong, Min Ho; Cho, Min Kook; Shon, Choel Soon; Kim, Ho Kyung

    2006-01-01

    In order to detect X rays with pixel detectors, there are two technical methods; a direct detection using photoconductive material that permits the conversion of the incident X rays into the signal charges, and an indirect detection using scintillation material that converts the incident X rays into the optical photons. Therefore, two-dimensional (2D) photosensitive pixel array is necessary for the indirect-detection scheme. Terbium-doped gadolinium oxysulfide (Gd 2 O 2 S:Tb) phosphor screen is the most popular X-ray converter, and often employed to the digital radiographic system owing to its well-known technology and easy handling in size, thickness, and flexibility. Furthermore, the cost is effective. In cascaded imaging chains of the indirect-detection system, the phosphor screen is served as the first stage. Since the image signal-to-noise ratio (SNR) is irreversible through the cascaded system, the phosphor screen is largely responsible for the eventual image quality. For the various radiation qualities suggested by IEC (International Electrotechnical Commission, Report 1267), we have investigated important physical quantities of Gd 2 O 2 S:Tb screen with a wide range of coverages (34 . 135 mg/cm 2 ) by using Monte Carlo calculations. The results will be useful for the optimal design of digital X-ray imaging systems

  18. Phosphor scintillator structure

    International Nuclear Information System (INIS)

    Cusano, D.A.; Prener, J.S.

    1980-01-01

    A method of fabricating scintillators is described in which the phosphor is distributed within the structure in such a way as to enhance the escape of the visible wavelength radiation that would otherwise be dissipated within the scintillator body. Two embodiments of the present invention are disclosed: one in which the phosphor is distributed in a layered structure and another in which the phosphor is dispersed throughout a transparent matrix. (U.K.)

  19. Photoluminescent properties of Y2O3:Eu3+ phosphors prepared via urea precipitation in non-aqueous solution

    International Nuclear Information System (INIS)

    Sun, Y.; Qi, L.; Lee, M.; Lee, B.I.; Samuels, W.D.; Exarhos, G.J.

    2004-01-01

    Europium-doped yttrium oxide phosphors were obtained by firing precursors prepared by urea precipitation in ethanol and ethylenediamine. The precipitation in non-aqueous solution was carried out in an autoclave at 150 deg. C to allow the decomposition of urea. The photoluminescent intensities of the phosphors prepared in ethanol and ethylenediamine increased by about 30% compared to that of the phosphor prepared by the conventional urea homogeneous precipitation in aqueous solution. Amorphous carbonates and amorphous hydroxides/carbonates mixtures were identified as precursors from ethanol and ethylenediamine, respectively. The morphology and particle size were studied by SEM and dynamic laser scattering method

  20. Coprecipitation of yttrium and aluminium hydroxide for preparation of yttrium aluminium garnet

    NARCIS (Netherlands)

    Vrolijk, J.W.G.A.; Willems, J.W.M.M.; Metselaar, R.

    1990-01-01

    Coprecipitation of yttrium and aluminium hydroxide for the preparation of pure yttrium aluminium garnet (YAG) powder with small grain size is the subject of this study. Starting materials are sulphates and chlorides of yttrium and aluminium. To obtain pure YAG (Y3Al5O12), the pH during flocculation

  1. Yttrium recovery from primary and secondary sources: A review of main hydrometallurgical processes

    Energy Technology Data Exchange (ETDEWEB)

    Innocenzi, Valentina, E-mail: valentina.innocenzi1@univaq.it [Department of Industrial Engineering, of Information and Economy, University of L’Aquila, Via Giovanni Gronchi 18, Zona industriale di Pile, 67100 L’Aquila (Italy); De Michelis, Ida [Department of Industrial Engineering, of Information and Economy, University of L’Aquila, Via Giovanni Gronchi 18, Zona industriale di Pile, 67100 L’Aquila (Italy); Kopacek, Bernd [SAT, Austrian Society for Systems Engineering and Automation, Gurkasse 43/2, A-1140 Vienna (Austria); Vegliò, Francesco [Department of Industrial Engineering, of Information and Economy, University of L’Aquila, Via Giovanni Gronchi 18, Zona industriale di Pile, 67100 L’Aquila (Italy)

    2014-07-15

    Highlights: • Review of the main hydrometallurgical processes to recover yttrium. • Recovery of yttrium from primary sources. • Recovery of yttrium from e-waste and other types of waste. - Abstract: Yttrium is important rare earths (REs) used in numerous fields, mainly in the phosphor powders for low-energy lighting. The uses of these elements, especially for high-tech products are increased in recent years and combined with the scarcity of the resources and the environmental impact of the technologies to extract them from ores make the recycling waste, that contain Y and other RE, a priority. The present review summarized the main hydrometallurgical technologies to extract Y from ores, contaminated solutions, WEEE and generic wastes. Before to discuss the works about the treatment of wastes, the processes to retrieval Y from ores are discussed, since the processes are similar and derived from those already developed for the extraction from primary sources. Particular attention was given to the recovery of Y from WEEE because the recycle of them is important not only for economical point of view, considering its value, but also for environmental impact that this could be generated if not properly disposal.

  2. Diagnostic phosphors for photon beams at the ALS and APS

    International Nuclear Information System (INIS)

    Shu, Deming; Warwick, T.; Johnson, E.D.

    1991-01-01

    Some tests have been made of phosphors for photon beam diagnosis. Plasma sprayed coatings were checked for damage and decay during a period of several ampere-hours of irradiation from the NSLS Xray ring. Surface temperatures were measured and extrapolated to give an indication of the temperatures expected in more powerful photon beams. Based on our findings we have chosen plasma-sprayed coatings of Europium-doped Yttrium Oxide as the best candidate for use on masks and flags in ''white'' photon beams of the new facilities. 4 refs., 2 figs

  3. Separation of yttrium using carbon nanotube doped polymeric beads impregnated with D2EHPA

    International Nuclear Information System (INIS)

    Dasgupta, Kinshuk; Yadav, Kartikey K.; Singh, D.K.; Anitha, M.; Singh, H.

    2013-01-01

    Di-2-ethylhexyl phosphoric acid impregnated polyethersulfone based composite beads in combination with additives such as polyvinyl alcohol (PVA) and multiwalled carbon nanotube (MWCNT) has been prepared by non-solvent phase inversion method. The synthesized beads were characterized by scanning electron microscopy, thermogravimetry and infra-red spectroscopy. Effect of additives on bead morphology, solvent impregnation capacity, extractability and stability has been examined to compare their suitability for yttrium recovery from acidic medium. Microstructural investigation as well as experimental findings confirmed the role of additives in modifying the pore structures in beads, responsible for varied degree of yttrium extraction. Further the role of metal ion concentration in aqueous phase on its recovery by polymeric beads was also evaluated. Among the tested beads PES/D2EHPA/MWCNT/PVA beads were found to be superior for Y(Ill) extraction. (author)

  4. Texture and deformation mechanism of yttrium

    International Nuclear Information System (INIS)

    Adamesku, R.A.; Grebenkin, S.V.; Stepanenko, A.V.

    1992-01-01

    X-ray pole figure analysis was applied to study texture and deformation mechanism in pure and commercial polycrystalline yttrium on cold working. It was found that in cast yttrium the texture manifected itself weakly enough both for pure and commercial metal. Analysis of the data obtained made it possible to assert that cold deformation of pure yttrium in the initial stage occurred mainly by slip the role of which decreased at strains higher than 36%. The texture of heavily deformed commercial yttrium contained two components, these were an 'ideal' basic orientation and an axial one with the angle of inclination about 20 deg. Twinning mechanism was revealed to be also possible in commercial yttrium

  5. Low lag luminescent phosphors

    International Nuclear Information System (INIS)

    1976-01-01

    The addition of potassium or rubidium salts to europium-activated fluorohalide phosphors produces X-ray screens with low lag, even at very low europium concentrations. The chemical preparation and afterglow test results are described

  6. Phosphors for LED lamps

    Science.gov (United States)

    Murphy, James Edward; Manepalli, Satya Kishore; Kumar, Prasanth Nammalwar

    2013-08-13

    A phosphor, a phosphor blend including the phosphor, a phosphor prepared by a process, and a lighting apparatus including the phosphor blend are disclosed. The phosphor has the formula (Ca.sub.1-p-qCe.sub.pK.sub.q).sub.xSc.sub.y(Si.sub.1-rGa.sub.r).sub.zO.su- b.12+.delta. or derived from a process followed using disclosed amounts of reactants. In the formula, (0

  7. High temperature thermometric phosphors

    Science.gov (United States)

    Allison, Stephen W.; Cates, Michael R.; Boatner, Lynn A.; Gillies, George T.

    1999-03-23

    A high temperature phosphor consists essentially of a material having the general formula LuPO.sub.4 :Dy.sub.(x),Eu.sub.y) wherein: 0.1 wt %.ltoreq.x.ltoreq.20 wt % and 0.1 wt %.ltoreq.y.ltoreq.20 wt %. The high temperature phosphor is in contact with an article whose temperature is to be determined. The article having the phosphor in contact with it is placed in the environment for which the temperature of the article is to be determined. The phosphor is excited by a laser causing the phosphor to fluoresce. The emission from the phosphor is optically focused into a beam-splitting mirror which separates the emission into two separate emissions, the emission caused by the dysprosium dopant and the emission caused by the europium dopent. The separated emissions are optically filtered and the intensities of the emission are detected and measured. The ratio of the intensity of each emission is determined and the temperature of the article is calculated from the ratio of the intensities of the separate emissions.

  8. Intense blue upconversion emission and intrinsic optical bistability in Tm3+/Yb3+/Zn2+ tridoped YVO4 phosphors

    Science.gov (United States)

    Yadav, Manglesh; Mondal, Manisha; Mukhopadhyay, Lakshmi; Rai, Vineet Kumar

    2018-04-01

    Tm3+/Yb3+/Zn2+:yttrium metavanadate (YVO4) phosphors prepared through chemical coprecipitation and the solid state reaction method have been structurally characterized by an x-ray diffraction (XRD) study. Photoluminescence study of the developed phosphors under ultraviolet (UV) and near infrared (NIR) excitation has been performed. The excitation spectrum of the tetragonal zircon type YVO4 phosphors corresponding to the emission at ˜476 nm exhibits a broad excitation peak in the 250-350 nm region, which is due to charge distribution in the {{{{VO}}}4}3- group. Under 980 nm CW diode laser excitation, enhancements of about ˜3000 times and ˜40 times have been observed for the blue band in the tridoped Tm3+Yb3+Zn2+:YVO4 phosphors compared to those of the Tm3+:YVO4 singly and Tm3+/Yb3+:YVO4 codoped phosphors, respectively. A downconversion (DC) emission study shows an enhancement of about ˜50 times for the blue band in the tridoped phosphors compared to that of the singly doped phosphors. Optical bistability (OB) behavior of the developed phosphors has been also investigated upon 980 nm excitation. The calculated Commission Internationale de l’Éclairage (CIE) color coordinates lie in the blue region with 96.5% color purity under 980 nm excitation, having a color temperature of ˜3400 K. Our observations show that the developed phosphors may be suitably used in dual mode luminescence spectroscopy, display devices, and UV LED chips.

  9. Photoluminescent and Thermoluminescent Studies of Dy3+ and Eu3+ Doped Y2O3 Phosphors.

    Science.gov (United States)

    Verma, Tarkeshwari; Agrawal, Sadhana

    2018-01-01

    Eu 3+ doped and Dy 3+ codoped yttrium oxide (Y 2 O 3 ) phosphors have been prepared using solid-state reaction technique (SSR). The prepared phosphors were characterized by X-ray diffractometer (XRD), energy dispersive X-ray (EDX) spectroscopy, scanning electron microscopy (SEM) and Fourier transforms infrared spectroscopy (FTIR) techniques. Photoluminescence (PL) and Thermoluminescence (TL) properties were studied in detail. PL emission spectra were recorded for prepared phosphors under excitation wavelength 254 nm, which show a high intense peak at 613 nm for Y 2 O 3 :Dy 3+ , Eu 3+ (1:1.5 mol %) phosphor. The correlated color temperature (CCT) and CIE analysis have been performed for the synthesized phosphors. TL glow curves were recorded for Eu 3+ doped and Dy 3+ codoped phosphors to study the heating rate effect and dose response. The kinetic parameters were calculated using peak shape method for UV and γ exposures through computerized glow curve deconvolution (CGCD) technique. The phosphors show second order kinetics and activation energies varying from 5.823 × 10 - 1 to 18.608 × 10 - 1  eV.

  10. Reaction of yttrium polonides with carbon dioxide

    International Nuclear Information System (INIS)

    Abakumov, A.S.; Khokhlov, A.D.; Reznikova, N.F.

    1986-01-01

    It has been proved that heating of yttrium and tantalum in carbon dioxide to 500 and 800 0 C alters the gas phase composition, causing formation of carbon monoxide and reduction of oxygen content. A study of the thermal stability of yttrium polonides in carbon dioxide showed that yttrium sesqui- and monopolonides decompose at 400-430 0 C. The temperature dependence of the vapor pressure of polonium obtained upon decomposition of the referred polonides has been determined in a carbon dioxide environment radiotensometrically. The enthalpy of the process calculated from this dependence is close to the enthalpy of vaporization of elemental polonium in vacuo. The mechanism of the reactions has been suggested

  11. Europium-activated phosphors containing oxides of rare-earth and group-IIIB metals and method of making the same

    Science.gov (United States)

    Comanzo, Holly Ann; Setlur, Anant Achyut; Srivastava, Alok Mani; Manivannan, Venkatesan

    2004-07-13

    Europium-activated phosphors comprise oxides of at least a rare-earth metal selected from the group consisting of gadolinium, yttrium, lanthanum, and combinations thereof and at least a Group-IIIB metal selected from the group consisting of aluminum, gallium, indium, and combinations thereof. A method for making such phosphors comprises adding at least a halide of at least one of the selected Group-IIIB metals in a starting mixture. The method further comprises firing the starting mixture in an oxygen-containing atmosphere. The phosphors produced by such a method exhibit improved absorption in the UV wavelength range and improved quantum efficiency.

  12. Yttrium doped BSCF membranes for oxygen separation

    DEFF Research Database (Denmark)

    Haworth, P.; Smart, S.; Glasscock, Julie

    2011-01-01

    This work investigates the partial substitution of yttrium in place of iron in BSCF to form Ba0.5Sr0.5Co0.8Fe0.2−xYxO3−δ, where x varied between 0 and 0.2. X-ray diffraction patterns showed the formation of a perovskite cubic phase structure up to x = 0.15, whilst the full substitution of yttrium...

  13. Crystallization of Yttrium and Samarium Aluminosilicate Glasses

    OpenAIRE

    Lago, Diana Carolina; Prado, Miguel Oscar

    2016-01-01

    Aluminosilicate glasses containing samarium and yttrium (SmAS and YAS glasses) exhibit high glass transition temperatures, corrosion resistance, and glass stability on heating which make them useful for technological applications. Yttrium aluminosilicate glass microspheres are currently being used for internal selective radiotherapy of liver cancer. During the preparation process, crystallization needs to be totally or partially avoided depending on the final application. Thus knowing the cry...

  14. Phosphates and phosphoric acid

    Energy Technology Data Exchange (ETDEWEB)

    Becker, P [Compagnie Francaise de l' Azote, Paris (France)

    1983-01-01

    In chapter 8.5 the following aspects of uranium recovery are treated: basis of extraction process, extraction principle, solvents, strength of the acid to be treated, technology, main processes in use, impact of uranium recovery on phosphoric acid plants, and economics of uranium recovery plants.

  15. Interaction of oxygen vacancies in yttrium germanates

    KAUST Repository

    Wang, Hao

    2012-01-01

    Forming a good Ge/dielectric interface is important to improve the electron mobility of a Ge metal oxide semiconductor field-effect transistor. A thin yttrium germanate capping layer can improve the properties of the Ge/GeO 2 system. We employ electronic structure calculations to investigate the effect of oxygen vacancies in yttrium-doped GeO 2 and the yttrium germanates Y 2Ge 2O 7 and Y 2GeO 5. The calculated densities of states indicate that dangling bonds from oxygen vacancies introduce in-gap states, but the system remains insulating. However, yttrium-doped GeO 2 becomes metallic under oxygen deficiency. Y-doped GeO 2, Y 2Ge 2O 7 and Y 2GeO 5 are calculated to be oxygen substoichiometric under low Fermi energy conditions. The use of yttrium germanates is proposed as a way to effectively passivate the Ge/dielectric interface. This journal is © 2012 the Owner Societies.

  16. Kinetics of yttrium dissolution from waste ceramic dust

    OpenAIRE

    STOPIC SRECKO R.; FRIEDRIH BERND G.

    2016-01-01

    Yttrium is a silvery transition metal and has similar chemical properties to lanthanoids. Because of this similarity, yttrium belongs to rare earth elements. Ytttrium and yttrium oxide are mostly used in fluoroscent lamps, production of electrodes, in electronic filters, lasers, superconductors and as additives in various materials to improve their properties. Yttrium is mainly recovered from the minerals monazite [(Ce,La,Th,Nd,Y)PO4] and xenotime YPO4.The presence of radioactive elements suc...

  17. Improvements in phosphors

    International Nuclear Information System (INIS)

    Rabatin, J.G.

    1981-01-01

    For X-ray image converter applications, especially when used in medical radiography, it is desirable to improve the speed and brightness of response for conversion of X-rays in phosphors. The rare earth oxyhalide phosphors coactivated with a combination of rare earth activators described in this patent are capable of exhibiting low afterglow with high ultraviolet emission. They have the general formula Lnsub(1-y-w)OX:Tbsub(y)Tmsub(w) where Ln is lanthanum or gadolinium, X is chlorine and/or bromine, y is from 0.0005 to 0.010 moles per mole and w is from 0.00005 to 0.005 moles per mole of the Lnsub(1-y-w)OX host. The method of preparation and characteristics of speed, afterglow and UV emission are described. (U.K.)

  18. Features of solid solutions composition in magnesium with yttrium alloys

    International Nuclear Information System (INIS)

    Drits, M.E.; Rokhlin, L.L.; Tarytina, I.E.

    1983-01-01

    Additional data on features of yttrium solid solutions composition in magnesium in the course of their decomposition investigation in the case of aging are obtianed. The investigation has been carried out on the base of a binary magnesium-yttrium alloy the composition of which has been close to maximum solubility (at eutectic temperature) and magnesium-yttrium alloys additionally doped with zinc. It is shown that higher yttrium solubility in solid magnesium than it has been expected, issueing from the difference in atomic radii of these metals indicates electron yttrium-magnesium atoms interaction. In oversaturated magnesium-yttrium solid solutions at earlier decomposition stages Mg 3 Cd type ordering is observed. At aging temperatures up to 250 deg C and long exposures corresponding to highest strengthening in oversaturated magnesium yttrium solid solutions a rhombic crystal lattice phase with three symmetric orientations is formed

  19. Method for production of transparent yttrium oxide

    International Nuclear Information System (INIS)

    Dutta, S.K.; Gazza, G.A.

    1975-01-01

    The method comprises vacuum hot pressing the yttrium oxide (Y 2 O 3 ) powder in a graphite die at temperatures of between 1300 to 1500 0 C and uniaxial pressures of between 5000 to 7000 psi, for a period of 1 to 2 hours. (U.S.)

  20. Method for chromatographically recovering scandium and yttrium

    International Nuclear Information System (INIS)

    Snyder, T.S.; Stoltz, R.A.

    1991-01-01

    This paper describes a method for chromatographically recovering scandium and yttrium from the residue of a sand chlorinator. It comprises: providing a residue from a sand chlorinator, the residue containing scandium, yttrium, sodium, calcium and at least one radioactive metal of the group consisting of radium, thorium and uranium; digesting the residue with an acid to produce an aqueous liquid containing scandium, yttrium, sodium, calcium and at least one radioactive metal of the group consisting of radium, thorium and uranium; feeding the metal containing liquid through a cation exchanger; eluding the cation exchanger with an acid eluant to to produce: a first eluate containing at least half of the total weight of the calcium and sodium in the feed liquid; a second eluate containing at least half of the total weight of the one or more radioactive metals in the feed liquid; a third eluate containing at least half of the yttrium in the feed liquid, and a fourth eluate containing at least half of the weight of the scandium in the feed liquid

  1. New hydrotalcite-like compounds containing yttrium

    Energy Technology Data Exchange (ETDEWEB)

    Fernandez, J.M.; Barriga, C.; Ulibarri, M.A. [Universidad de Cordoba (Spain)] [and others

    1997-01-01

    The synthesis of hydrotalcite-type compounds containing yttrium was carried out by the coprecipitation of Mg(II), Al(III), and Y(III) cations at 60 degrees C with strong alkaline solutions. Thermal treatments were applied and changes studied.

  2. Recovering uranium from phosphoric acid

    International Nuclear Information System (INIS)

    Anon.

    1979-01-01

    Wet-process phosphoric acid contains a significant amount of uranium. This uranium totals more than 1,500 tons/yr in current U.S. acid output--and projections put the uranium level at 8,000 tons/yr in the year 2000. Since the phosphoric acid is a major raw material for fertilizers, uranium finds its way into those products and is effectively lost as a resource, while adding to the amount of radioactive material that can contaminate the food chain. So, resource-conservation and environmental considerations both make recovery of the uranium from phosphoric acid desirable. This paper describes the newly developed process for recovering uranium from phosphoric acid by using solvent-extraction technique. After many extractants had been tested, the researchers eventually selected the combination of di (2-ethylhexyl) phosphoric acid (DEPA) and trioctylphosphine oxide (TOPO) as the most suitable. The flowscheme of the process is included

  3. Scandium, yttrium and the lanthanide metals

    International Nuclear Information System (INIS)

    Brown, Paul L.; Ekberg, Christian

    2016-01-01

    The hydroxide and oxide phases that exist for scandium(III) include scandium hydroxide, which likely has both amorphous and crystalline forms, ScOOH(s), and scandium oxide. This chapter presents the data selected for the stability constants of the polymeric hydrolysis species of scandium at zero ionic strength. The behaviour of yttrium, and the lanthanide metals, in the environment is largely dependent on their solution equilibria. Hydrolysis and other complexation reactions of yttrium and the lanthanide metals are important in the disposal of nuclear waste. The trivalent lanthanide metals include lanthanum(III) through lutetium(III). A number of studies have reported a tetrad effect for the geochemical behaviour of the lanthanide series, including stability constants and distribution coefficients. The solubility of many of the lanthanide hydroxide phases has been studied at fixed ionic strength. In studying the hydrolysis of cerium(IV), a number of studies have utilised oxidation-reduction reactions in determining the relevant stability constants.

  4. Magnetic structure of holmium-yttrium superlattices

    DEFF Research Database (Denmark)

    Jehan, D.A.; McMorrow, D.F.; Cowley, R.A.

    1993-01-01

    We present the results of a study of the chemical and magnetic structures of a series of holmium-yttrium superlattices and a 5000 angstrom film of holmium, all grown by molecular-beam epitaxy. By combining the results of high-resolution x-ray diffraction with detailed modeling, we show...... that the superlattices have high crystallographic integrity: the structural coherence length parallel to the growth direction is typically almost-equal-to 2000 angstrom, while the interfaces between the two elements are well defined and extend over approximately four lattice planes. The magnetic structures were...... determined using neutron-scattering techniques. The moments on the Ho3+ ions in the superlattices form a basal-plane helix. From an analysis of the superlattice structure factors of the primary magnetic satellites, we are able to determine separately the contributions made by the holmium and yttrium...

  5. Treatment of acromegaly by yttrium implantation

    Energy Technology Data Exchange (ETDEWEB)

    Hibbert, J.; Shaheen, O.H.

    1977-01-01

    Yttrium implantation is one of the many ways of treating acromegaly. The advantages are the minor nature of the procedure and the fact that pituitary replacement is not as commonly required as after hypophysectomy. Thus in young female patients menstruation may be resumed following treatment and pregnancy has occurred. The procedure is not as free from complications as external irradiation but the response is more satisfactory.

  6. Yttrium and rare earths separation by ion exchange resin

    International Nuclear Information System (INIS)

    Pinatti, D.G.; Ayres, M.J.G.; Ribeiro, S.; Silva, G.L.J.P.; Silva, M.L.C.P.; Martins, A.H.

    1988-01-01

    The experimental results of yttrium and rare earths separation from Brazilian xenotime are presented. The research consist in five stage: 1) Preparation of yttrium, erbium and lutetium standard solutions, from solubilization of pure oxides 2) yttrium and rare earths separation by ion exchange chromatrography 3) Separation and recovery of EDTA 4) Precipitation and calcination and 4) Analytical control of process. (C.G.C.) [pt

  7. Yttrium addition for high temperatures stainless steel

    International Nuclear Information System (INIS)

    Furtado, Nelson Cesar Chaves Pinto

    1997-07-01

    The current work studied the effect of Yttrium on the microstructure of 2% Nb, modified - HP steel, with respect to its mechanical properties. Alloys were prepared with nominal Yttrium additions of 0,1% and 0,25%. Microstructural analyses and mechanical tests were undertaken in the as-cast condition and after ageing for 100 h at 700 deg C, 900 deg C and 1100 deg C. Structural characterization was performed by optical microscopy, scanning and transmission electron microscopy (SEM/TEM/EDS), X-ray diffractometry and X-ray photoelectron spectroscopy (XPS). Tensile testing was performed at room temperature and 871 deg C and creep testing at 925 deg C at a loading of 55 MPa. The material produced exhibited superior mechanical properties and surface oxidation resistance than traditional alloys of this class, even through gravity cast in a magnetic furnace. Agglomerates of Yttrium-rich phases were identifies in both as-cast and aged specimens, always associated with chromium carbides of characteristic morphologies. These morphologies, combined with the microstructural constituents, may have established the factors which resulted in the improved metallurgical stability of these alloys under the experimental testing conditions and temperatures which simulated real industrial service conditions and temperatures. (author)

  8. Yttrium aluminum garnet coating on glass substrate

    Energy Technology Data Exchange (ETDEWEB)

    Ferreira, Camila M.A.; Freiria, Gabriela S.; Faria, Emerson H. de; Rocha, Lucas A.; Ciuffi, Katia J.; Nassar, Eduardo J., E-mail: eduardo.nassar@unifran.edu.br

    2016-02-15

    Thin luminescent films have seen great technological advances and are applicable in the production of a variety of materials such as sensors, solar cells, photovoltaic devices, optical magnetic readers, waveguides, lasers, and recorders. Systems that contain yttrium aluminum oxide are important hosts for lanthanide ions and serve as light emission devices. This work deals with the deposition of yttrium aluminum garnet (YAG) film doped with Eu{sup 3+} onto a glass substrate obtained by the sol–gel methodology. Spray pyrolysis furnished the yttrium aluminum oxide powder. Dip-coating at a withdrawal speed of 10 mm min{sup −1} and evaporation led to deposition of different numbers of layers of the YAG:Eu{sup 3+} film onto the glass substrate from a YAG:Eu{sup 3+} powder suspension containing ethanol, water, and tetraethylorthosilicate. Photoluminescence, X-ray diffraction, scanning electron microscopy, and transparency measurements aided film characterization. The emission spectra revealed that the number of layers influenced film properties. - Highlights: • The spray pyrolysis was used to obtain luminescent YAG:Eu{sup 3+}. • The matrix was deposited as transparent films. • The YAG:Eu{sup 3+} was deposited by sol–gel process onto glass substrate.

  9. Yttrium aluminum garnet coating on glass substrate

    International Nuclear Information System (INIS)

    Ferreira, Camila M.A.; Freiria, Gabriela S.; Faria, Emerson H. de; Rocha, Lucas A.; Ciuffi, Katia J.; Nassar, Eduardo J.

    2016-01-01

    Thin luminescent films have seen great technological advances and are applicable in the production of a variety of materials such as sensors, solar cells, photovoltaic devices, optical magnetic readers, waveguides, lasers, and recorders. Systems that contain yttrium aluminum oxide are important hosts for lanthanide ions and serve as light emission devices. This work deals with the deposition of yttrium aluminum garnet (YAG) film doped with Eu 3+ onto a glass substrate obtained by the sol–gel methodology. Spray pyrolysis furnished the yttrium aluminum oxide powder. Dip-coating at a withdrawal speed of 10 mm min −1 and evaporation led to deposition of different numbers of layers of the YAG:Eu 3+ film onto the glass substrate from a YAG:Eu 3+ powder suspension containing ethanol, water, and tetraethylorthosilicate. Photoluminescence, X-ray diffraction, scanning electron microscopy, and transparency measurements aided film characterization. The emission spectra revealed that the number of layers influenced film properties. - Highlights: • The spray pyrolysis was used to obtain luminescent YAG:Eu 3+ . • The matrix was deposited as transparent films. • The YAG:Eu 3+ was deposited by sol–gel process onto glass substrate.

  10. Uranium extraction from phosphoric acid

    International Nuclear Information System (INIS)

    Lounis, A.

    1983-05-01

    A study has been carried out for the extraction of uranium from phosphoric acid produced in Algeria. First of all, the Algerian phosphoric acid produced in Algeria by SONATRACH has been characterised. This study helped us to synthesize a phosphoric acid that enabled us to pass from laboratory tests to pilot scale tests. We have then examined extraction and stripping parameters: diluent, DZEPHA/TOPO ratio and oxidising agent. The laboratory experiments enabled us to set the optimum condition for the choice of diluent, extractant concentration, ratio of the synergic mixture, oxidant concentration, redox potential. The equilibrium isotherms lead to the determination of the number of theoretical stages for the uranium extraction and stripping of uranium, then the extraction from phosphoric acid has been verified on a pilot scale (using a mixer-settler)

  11. Industrial radiography with phosphor screens

    International Nuclear Information System (INIS)

    Broadhead, P.

    1981-01-01

    An experimental system that comprises a film of low silver content and a pair of high resolution phosphor intensifying screens and a commercial industrial X-ray film of similar speed are compared for image quality. It is concluded that the use of phosphor screens offers an increase in image quality when the information is limited by the graininess or quantum mottle of a radiograph which is frequently the case in practical radiography. (author)

  12. Uranium extraction from phosphoric acid

    International Nuclear Information System (INIS)

    Araujo Figueiredo, C. de

    1984-01-01

    The recovery of uranium from phosphoric liquor by two extraction process is studied. First, uranium is reduced to tetravalent condition and is extracted by dioctypyrophosphoric acid. The re-extraction is made by concentrated phosphoric acid with an oxidizing agent. The re-extract is submitted to the second process and uranium is extracted by di-ethylhexilphosphoric acid and trioctylphosphine oxide. (M.A.C.) [pt

  13. Effect of Annealing Time of YAG:Ce3+ Phosphor on White Light Chromaticity Values

    Science.gov (United States)

    Abd, Husnen R.; Hassan, Z.; Ahmed, Naser M.; Almessiere, Munirah Abdullah; Omar, A. F.; Alsultany, Forat H.; Sabah, Fayroz A.; Osman, Ummu Shuhada

    2018-02-01

    Yttrium and aluminium nitrate phosphors doped with cerium nitrate and mixed with urea (fuel) are prepared by using microwave-induced combustion synthesis according to the formula Y(3-0.06)Al5O12:0.06Ce3+ (YAG:Ce3+) to produce white light emitting diodes by conversion from blue indium gallium nitride-light emitting diode chips. The sintering time with fixed temperature (1050°C) for phosphor powder was optimized and found to be 5 h. The crystallinity, structure, chemical composition, luminescent properties with varying currents densities and chromaticity were characterized by x-ray diffraction, field emission-scanning electron microscopy, transmission electron microscopy, energy dispersive spectroscopy, photoluminescence emission, electroluminescence and standard CIE 1931 chromaticity diagram, respectively. The energy levels of Ce3+ in YAG were discussed based on its absorption and excitation spectra. The results show that the obtained YAG:Ce3+ phosphor sintered for 5 h has good crystallinity with pure phase, low agglomerate with spherical shaped particles and strong yellow emission, offering cool-white LED with tuneable correlated color temperature and a good color rendering index compared to those prepared by sintering for 2 h and as-prepared phosphor powders.

  14. Entropy as a measure of the performance of phosphor materials used in medical imaging radiation detectors

    International Nuclear Information System (INIS)

    Cavouras, D.; Kandarakis, I.; Maris, T.; Panayiotakis, G.S.; Nomicos, C.D.

    2001-01-01

    In information theory, entropy expresses the information gain obtained after detection of a signal concerning the state of a parameter of interest. In this study, entropy has been expressed in terms of physical quantities (emitted optical fluence and MTF) related to the imaging performance of phosphor materials, which are employed in medical imaging radiation detectors. Four phosphor materials, used in the form of laboratory-prepared fluorescent layers (screens), were compared on the basis of their entropy performance. Measurements were performed using 30- and 80-kVp X-ray beams often employed in X-ray imaging. Results showed that phosphor materials with high density and effective atomic number exhibit high entropy performance, especially at the higher X-ray tube voltage of 80 kVp. Entropy values are also affected by the type of activator, which determines the intrinsic X-ray-to-light conversion efficiency, and the spectrum of emitted light. The proximity of the incident X-ray quanta energy to the energy of the K-shell threshold for photoelectric absorption is an additional important factor which increases entropy. This effect was more apparent in the performance of yttrium-based phosphors at the lower voltage of 30 kVp. (orig.)

  15. Enhancing the performance of Ce:YAG phosphor-in-silica-glass by controlling interface reaction

    International Nuclear Information System (INIS)

    Zhou, Beiying; Luo, Wei; Liu, Sheng; Gu, Shijia; Lu, Mengchen; Zhang, Yan; Fan, Yuchi; Jiang, Wan; Wang, Lianjun

    2017-01-01

    Dispersing the Ce"3"+ doped yttrium aluminum garnet (Ce:YAG) phosphor in the glass matrix has been widely investigated to replace conventional organic resin or silicone packaging. However, the reaction layer formed between commercial phosphors and glass matrix severely degrades the optical performance of Ce:YAG phosphor in silica glass (PiSG) materials. This paper demonstrates an ultra-fast method for preparing high performance PiSG materials. Instead of traditional melting process, the highly transparent PiSG samples can be rapidly fabricated from mixtures of commercial Ce:YAG phosphor and mesoporous SiO_2 (SBA-15) powders using spark plasma sintering (SPS) at relatively low temperature (1000 °C) within short time (10 min). Owing to the inhibition of the deleterious interface reactions between Ce:YAG phosphor and silica glass matrix, the phosphor has been perfectly preserved, and the internal relative quantum yield of the PiSG sample reaches as high as 93.5% when excited at 455 nm, which is the highest efficiency in current research. Furthermore, combining the PiSG sample, we successfully fabricate a light-emitting diode (LED) module exhibiting a superior performance with luminous efficacy of 127.9 lm/W, correlated color temperature of 5877 K and color rendering index of 69 at the operating current of 120 mA. This work on the high performance LED modules provides not only a new approach to fabricate the functional glass-based materials that is sensitive to the high temperature, but also a possibility to extend the lifetime and improve the optical performances of the glass based LEDs.

  16. Sol gel synthesis for preparation of yttrium aluminium garnet

    NARCIS (Netherlands)

    Vrolijk, J.W.G.A.; Willems, J.W.M.M.; Metselaar, R.; With, de G.; Terpstra, R.A.; Metselaar, R.

    1989-01-01

    Sol-gel—synthesis for preparation of pure yttrium aluminium garnet powder with small grain size is subject of this ongoing study. Starting materials were sulfates and chlorides of yttrium and aluminium. To obtain pure YAG (Y3A1SO1Z) pH during hydrolysis as well as temperature during calcination and

  17. Abscopal Effects and Yttrium-90 Radioembolization

    Energy Technology Data Exchange (ETDEWEB)

    Ghodadra, Anish; Bhatt, Sumantha [University Pittsburgh School of Medicine, Department of Radiology (United States); Camacho, Juan C. [Emory University School of Medicine, Department of Radiology and Imaging Sciences (United States); Kim, Hyun S., E-mail: kevin.kim@yale.edu [University Pittsburgh School of Medicine, Department of Radiology (United States)

    2016-07-15

    We present the case of an 80-year-old male with squamous cell carcinoma with bilobar hepatic metastases who underwent targeted Yttrium-90 radioembolization of the right hepatic lobe lesion. Subsequently, there was complete regression of the nontargeted, left hepatic lobe lesion. This may represent the first ever reported abscopal effect in radioembolization. The abscopal effect refers to the phenomenon of tumor response in nontargeted sites after targeted radiotherapy. In this article, we briefly review the immune-mediated mechanisms responsible for the abscopal effect.

  18. Nonlinear FMR spectra in yttrium iron garnet

    Directory of Open Access Journals (Sweden)

    Yu.M. Bunkov, P.M. Vetoshko, I.G. Motygullin, T.R. Safin, M.S. Tagirov, N.A. Tukmakova

    2015-12-01

    Full Text Available Results of demagnetizing effect studies in yttrium iron garnet Y3Fe5O12 thin films are reported. Experiments were performed on X-Band of electron paramagnetic resonance spectrometer at room temperature. The ferromagnetic resonance (FMR spectra were obtained for one-layer single crystal YIG films for different values of the applied microwave power. Nonlinear FMR spectra transformation by the microwave power increasing in various directions of magnetic field sweep was observed. It is explained by the influence of the demagnetization action of nonequilibrium magnons.

  19. Cerium and yttrium oxide nanoparticles are neuroprotective

    International Nuclear Information System (INIS)

    Schubert, David; Dargusch, Richard; Raitano, Joan; Chan, S.-W.

    2006-01-01

    The responses of cells exposed to nanoparticles have been studied with regard to toxicity, but very little attention has been paid to the possibility that some types of particles can protect cells from various forms of lethal stress. It is shown here that nanoparticles composed of cerium oxide or yttrium oxide protect nerve cells from oxidative stress and that the neuroprotection is independent of particle size. The ceria and yttria nanoparticles act as direct antioxidants to limit the amount of reactive oxygen species required to kill the cells. It follows that this group of nanoparticles could be used to modulate oxidative stress in biological systems

  20. Investigation of recovery and recycling of rare earth elements from waste fluorescent lamp phosphors

    Science.gov (United States)

    Eduafo, Patrick Max

    Characterization techniques and experimental measurements were used to evaluate a process for recycling rare earth elements (REEs) from spent fluorescent lamp phosphors. QEMSCAN analysis revealed that over 60% of the rare earth bearing minerals was less than 10 microm. A representative sample of the as-received feed contained 14.59 wt% total rare earth elements (TREE) and upon sieving to below 75 microm, the grade increased to 19.60 wt% REE with 98.75% recovery. Based on experimental work, a new process for extracting the chief REEs from end of life fluorescent lamps has been developed. The proposed flowsheet employs a three-stage leaching and precipitation process for selective extraction and recovery of the REEs. Hydrochloric acid was used as lixiviant in batch leach experiments on the phosphor powder. The maximum extraction obtained was 100% for both yttrium and europium under the following leaching conditions: 2.5 M HCl, 70°C, 1 hour, 180 g/L and 600 rpm. However, the solubility of cerium, lanthanum and terbium remained low at these conditions. Kinetic data of the leaching of yttrium and europium showed best fit to the logarithmic rate expression of the empirical model of leaching. Activation energy was calculated to be 77.49 kJ/mol for Y and 72.75 kJ/mol for Eu in the temperature range of 298 to 343 K. Precipitation tests demonstrate that at least 50% excess the stoichiometric amount of oxalic acid is needed to recover yttrium and europium efficiently to produce a pure (Y, Eu) mixed oxide. Total recovery of the REEs was achieved even at very low pH or without any base added. Over 99% pure mixed rare earth oxide at 99% recovery has been attained. An economic assessment of the developed process using operating and capital cost have be undertaken and based on the analysis of the three economic scenarios, two are economic and one is non-economic.

  1. Yttrium synovectomy: a meta-analysis of the literature

    International Nuclear Information System (INIS)

    Jones, G.

    1993-01-01

    Yttrium synovectomy for chronic synovitis of the knee enjoys widespread usage in Australia with approximately 400 patients receiving yttrium-90 in 1991. Despite abundant anecdotal evidence of its efficacy there is a paucity of controlled trials and those that have been done have produced conflicting results and have been of insufficient sample size. To critically and quantitatively evaluate the published English literature on comparative trials of yttrium-90 therapy for chronic synovitis of the knee, the technique of meta-analysis was utilised. The literature search was carried out using the MeSH terms of synovectomy and knee; and yttrium. This was augmented by referring to reviews, current textbooks and back-references. Outcome measures varied between trials but could be grouped as treatment success. The Peto modification of Mantel and Haenszl was used for statistical pooling of data yielding a pooled odds ratio (OR). The literature search revealed ten controlled trials of which two were excluded from further analysis. It was found that yttrium was superior to placebo (OR 2.42, 95% CI 1.02-5.73) but it is recommended that this result should be interpreted with caution due to possible publication bias. It is concluded that there is insufficient evidence from comparative trials of yttrium in the English literature to show that yttrium synovectomy is convincingly superior to triamcinolone (OR 1.89, 95% CI 0.81-10.55) or other active modalities (OR 1.04, 95% CI 0.72-1.52). 25 refs., 4 tabs

  2. 21 CFR 182.1073 - Phosphoric acid.

    Science.gov (United States)

    2010-04-01

    ... 21 Food and Drugs 3 2010-04-01 2009-04-01 true Phosphoric acid. 182.1073 Section 182.1073 Food and Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF HEALTH AND HUMAN SERVICES (CONTINUED) FOOD FOR HUMAN....1073 Phosphoric acid. (a) Product. Phosphoric acid. (b) Conditions of use. This substance is generally...

  3. 21 CFR 582.1073 - Phosphoric acid.

    Science.gov (United States)

    2010-04-01

    ... 21 Food and Drugs 6 2010-04-01 2010-04-01 false Phosphoric acid. 582.1073 Section 582.1073 Food and Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF HEALTH AND HUMAN SERVICES (CONTINUED) ANIMAL... Additives § 582.1073 Phosphoric acid. (a) Product. Phosphoric acid. (b) Conditions of use. This substance is...

  4. Recovering uranium from phosphoric acid

    International Nuclear Information System (INIS)

    Abodishish, H.A.; Ritchey, R.W.

    1982-01-01

    Precipitation of Fe 3 HN 4 H 8 (PO 4 ) 6 is prevented in the second cycle extractor, in a two cycle uranium recovery process, by washing ammonia laden organic solvent stream, from the second cycle stripper, with first cycle raffinate iron stream containing phosphoric acid, prior to passing the solvent stream into the second cycle extractor. (author)

  5. Sources and distribution of yttrium and rare earth elements in surface sediments from Tagus estuary, Portugal.

    Science.gov (United States)

    Brito, Pedro; Prego, Ricardo; Mil-Homens, Mário; Caçador, Isabel; Caetano, Miguel

    2018-04-15

    The distribution and sources of yttrium and rare-earth elements (YREE) in surface sediments were studied on 78 samples collected in the Tagus estuary (SW Portugal, SW Europe). Yttrium and total REE contents ranged from 2.4 to 32mg·kg -1 and 18 to 210mg·kg -1 , respectively, and exhibited significant correlations with sediment grain-size, Al, Fe, Mg and Mn, suggesting a preferential association to fine-grained material (e.g. aluminosilicates but also Al hydroxides and Fe oxyhydroxides). The PAAS (Post-Archean Australian Shale) normalized patterns display three distinct YREE fractionation pattern groups along the Tagus estuary: a first group, characterized by medium to coarse-grained material, a depleted and almost flat PAAS-normalized pattern, with a positive anomaly of Eu, representing one of the lithogenic components; a second group, characterized mainly by fine-grained sediment, with higher shale-normalized ratios and an enrichment of LREE relative to HREE, associated with waste water treatment plant (WWTP) outfalls, located in the northern margin; and, a third group, of fine-grained material, marked by a significant enrichment of Y, a depletion of Ce and an enrichment of HREE over LREE, located near an inactive chemical-industrial complex (e.g. pyrite roast plant, chemical and phosphorous fertilizer industries), in the southern margin. The data allow the quantification of the YREE contents and its spatial distribution in the surface sediments of the Tagus estuary, identifying the main potential sources and confirming the use of rare earth elements as tracers of anthropogenic activities in highly hydrodynamic estuaries. Copyright © 2017 Elsevier B.V. All rights reserved.

  6. Extraction of nitrates of lanthanoids (3) of the yttrium group and yttrium (3) by trialkylbenzylammonium nitrate in toluene

    International Nuclear Information System (INIS)

    Pyartman, A.K.; Kovalev, S.V.; Keskinov, V.A.; Kopyrin, A.A.

    1997-01-01

    A study was made on extraction of nitrates of lanthanoids (3) of the yttrium group (terbium-lutetium) and yttrium (3) by trialkylbensylammonium nitrate in toluene at T=298.15 K pH 2. Extraction isotherms are described with account of formation of compound of (R 4 N) 2 [Ln(NO 3 ) 5 ] composition in organic phase. Values of extraction constants decreasing in terbium (3)-lutetium (3) series, were calculated. Value of extraction constant for yttrium (3) is close to the value of extraction constant for ytterbium (3). 13 refs., 2 figs., 3 tabs

  7. Synthesis of crystalline Ce-activated garnet phosphor powders and technique to characterize their scintillation light yield

    Science.gov (United States)

    Gordienko, E.; Fedorov, A.; Radiuk, E.; Mechinsky, V.; Dosovitskiy, G.; Vashchenkova, E.; Kuznetsova, D.; Retivov, V.; Dosovitskiy, A.; Korjik, M.; Sandu, R.

    2018-04-01

    This work reports on a process of preparation of garnet phosphor powders and a technique for light yield evaluation of strongly light scattering samples. Powders of scintillation compounds could be used as individual materials or as samples for express tests of scintillation properties. However, estimation of their light yield (LY) is complicated by strong light scattering of this kind of materials. Ce3+-activated yttrium-aluminum and gallium-gadolinium-aluminum garnet phosphor powders, Y3Al5O12 (YAG:Ce) and Gd3Ga3Al2O12 (GGAG:Ce), were obtained using a modified coprecipitation technique. Ga tends to residue in mother liquor in ammonia media, but the modification allows to avoid the loss of components. We propose an approach for sample preparation and LY measurement setup with alpha particles excitation, allowing to decrease light scattering influence and to estimate a light yield of powder samples. This approach is used to evaluate the obtained powders.

  8. Radiolabeling Of Albumin Particles With Yttrium-90

    International Nuclear Information System (INIS)

    Nguyen Thi Thu; Nguyen Thi Khanh Giang; Bui Van Cuong, Vo Thi Cam Hoa

    2011-01-01

    This paper presents the process of the radiolabeling of microaggregated albumin particles with radionuclide Yttrium-90 using the directed method. The albumin microsphere kit was prepared in sodium phosphate buffer. The original solution includes 2 mg albumin particle and 0.5 mg stannous chloride dihydrate. The albumin particles size was ranged from 5 ?m to 30 ?m. The mixture was washed three times with phosphate buffer saline, pH 7.2 by centrifugation and suspended in 0.5 M sodium acetate buffer, pH 6. Yttrium - 90 in 1.0 M acetic acid was collected from 90 Sr/ 90 Y generator. The labeling of the particles with Y-90 (185 MBq) was performed at pH 5.5 in acetate buffer with agitating for 60 min at room temperature. The labeled albumin suspensions were centrifuged at 3000 rpm for 15 min. Labeling yields was calculated using centrifugation, filtration and compared with paper chromatography, which is developed in the Tris Acetic EDTA. In this system, the unbound of Y-90 migrates to an R f of 0.9-1.0 and the radiolabeled albumin particles remains at the point of origin (R f = 0). The size of 90 Y-albumin particles was compared with the albumin particles in the original solution to be sure that they did not change during the labeling treatment. The radiolabeling yields were more than 80%. The labeled compound was dialysis in phosphate buffer. The radiochemical purity was 98%. The 90 Y- albumin is an ideal radiopharmaceutical for potential use in malignant cancer treatment as brachytherapy. (author)

  9. Luminescence of yttrium niobium-tantalate doubly activated by europium and/or terbium under X-ray and electron beam excitation

    Energy Technology Data Exchange (ETDEWEB)

    Arellano, I.D., E-mail: arellano@utp.edu.co [Department of Physics, Technological University of Pereira, Vereda La Julita, Pereira (Colombia); Nazarov, M.V. [Institute of Applied Physics, Academy of Sciences of Moldova, Republic of Moldova (Moldova, Republic of); School of Materials and Mineral Resources Engineering Universiti Sains Malaysia, 14300 Nibong Tebal, Penang (Malaysia); Cortes, J.A. [Department of Physics, Technological University of Pereira, Vereda La Julita, Pereira (Colombia); Ahmad Fauzi, M.N [School of Materials and Mineral Resources Engineering Universiti Sains Malaysia, 14300 Nibong Tebal, Penang (Malaysia)

    2012-09-15

    This paper reports the luminescence emission spectra of Y(Ta,Nb)O{sub 4} activated by rare earth ions such as Eu{sup 3+} and Tb{sup 3+}. The influence of these rare earth ions on the luminescence of yttrium niobium-tantalate phosphors was investigated. The luminescent properties were studied under X-ray and electron beam excitations. Under these excitations, the emission centers of the rare earth activators (Eu{sup 3+},Tb{sup 3+}) were found to contribute efficiently to the overall luminescence. Changing the mol concentration of the incorporated activators resulted in a broad variation of visible photoluminescence. Color cathodoluminescence images showed clearly the dependence of chromaticity on the different activators. With their various luminescence chromaticities, these rare earth activated phosphors are promising materials for solid-state lighting applications as well as for X-ray intensifying screens in medical diagnosis, providing a broad variation of visible photoluminescence from blue to red. - Highlights: Black-Right-Pointing-Pointer The Y(Ta,Nb)O{sub 4} phosphors were activated by rare earth ions such as Eu{sup 3+} and Tb{sup 3+}. Black-Right-Pointing-Pointer The phosphors were studied under X-ray and electron beam excitations. Black-Right-Pointing-Pointer The emission centers contribute efficiently to the overall luminescence. Black-Right-Pointing-Pointer Changing the concentration of the activators resulted in a broad luminescence.

  10. Application of strong phosphoric acid to radiochemistry

    International Nuclear Information System (INIS)

    Terada, Kikuo

    1977-01-01

    Not only inorganic and organic compounds but also natural substrances, such as accumulations in soil, are completely decomposed and distilled by heating with strong phosphoric acid for 30 to 50 minutes. As applications of strong phosphoric acid to radiochemistry, determination of uranium and boron by use of solubilization effect of this substance, titration of uranyl ion by use of sulfuric iron (II) contained in this substance, application to tracer experiment, and determination of radioactive ruthenium in environmental samples are reviewed. Strong phosphoric acid is also applied to activation analysis, for example, determination of N in pyrographite with iodate potassium-strong phosphoric acid method, separation of Os and Ru with sulfuric cerium (IV) - strong phosphoric acid method or potassium dechromate-strong phosphoric acid method, analysis of Se, As and Sb rocks and accumulations with ammonium bromide, sodium chloride and sodium bromide-strong phosphoric acid method. (Kanao, N.)

  11. The sequential separation of strontium-90, yttrium-90, promethium-147, and cerium-144 from urine and their subsequent estimation

    International Nuclear Information System (INIS)

    Kramer, G.H.; Davies, J.M.

    1981-04-01

    A method has been developed for separating low-level activities of the beta-emitting isotopes strontium-90, yttrium-90, promethium-147 and cerium-144 from urine and aqueous solutions. They are subsequently estimated by planchet or liquid scintillation counting. The radionuclides are separated from each other and from interfering elements by solvent extraction with HDEHP (di-2-ethylhexyl phosphoric acid) in n-heptane. It is possible to separate the elements with a minimum of cross-contamination by selecting appropriate pH's and solvent concentrations. Percentage recoveries for the radionuclides are: 90 Sr, 100 +- 12; 90 Y, 65 +- 4; 147 Pm, 90 +- 8; 144 Ce, 87 +- 11. The limits of detection are: 90 Sr, 0.6 pCi; 90 Y, 0.7 pCi; 147 Pm, 1.0 pCi; 144 Ce, 0.8 pCi. (author)

  12. Thermoanalytical study of the decomposition of yttrium trifluoroacetate thin films

    International Nuclear Information System (INIS)

    Eloussifi, H.; Farjas, J.; Roura, P.; Ricart, S.; Puig, T.; Obradors, X.; Dammak, M.

    2013-01-01

    We present the use of the thermal analysis techniques to study yttrium trifluoroacetate thin films decomposition. In situ analysis was done by means of thermogravimetry, differential thermal analysis, and evolved gas analysis. Solid residues at different stages and the final product have been characterized by X-ray diffraction and scanning electron microscopy. The thermal decomposition of yttrium trifluoroacetate thin films results in the formation of yttria and presents the same succession of intermediates than powder's decomposition, however, yttria and all intermediates but YF 3 appear at significantly lower temperatures. We also observe a dependence on the water partial pressure that was not observed in the decomposition of yttrium trifluoroacetate powders. Finally, a dependence on the substrate chemical composition is discerned. - Highlights: • Thermal decomposition of yttrium trifluoroacetate films. • Very different behavior of films with respect to powders. • Decomposition is enhanced in films. • Application of thermal analysis to chemical solution deposition synthesis of films

  13. Yttrium Nitrate mediated Nitration of Phenols at room temperature in ...

    Indian Academy of Sciences (India)

    The described method is selective for phenols. ... the significant cause of post translational modification that can ... decades, significant attention was paid on nitration of phenols to .... Progress of the reaction can be noted visually. Yttrium.

  14. Attempts at treating rheumatoid arthritis with radioactive yttrium

    International Nuclear Information System (INIS)

    Scott, J.T.

    1979-01-01

    Two years' observations on 33 knee joints in 33 patients with rheumatoid arthritis did not prove a therapeutic effect of Y 90 , which was tested in a randomized study against non-radioactive yttrium. It was noticable that 9 knee joints of the isotope group but only one of the control group became unstable. Independent of the yttrium treatment, significant improvement was noticed in patients where fibrin clots had been washed out of the joints in the course of arthroscopies. (orig.) [de

  15. Treatment of rheumatoid arthritis with 90yttrium. Follow up studies

    International Nuclear Information System (INIS)

    Teuber, J.; Baenkler, H.W.; Regler, G.; Erlangen-Nuernberg Univ., Erlangen

    1978-01-01

    90 Yttrium-silicate was injected into 131 knee-joints from patients with rheumatoid arthritis with stadium II-IV according to Steinbrocker. The observation period lasted until two years. After three months about 80% and after 24 months still more than 50% of the patients treated showed complete or partial remission. Side-effects as formerly observed with 198 -goldpreparations did not occur. Therefore the treatment with 90 Yttrium-silicate offers an alternative to surgical synovectomy. (orig.) [de

  16. Thermal decomposition of yttrium(III) propionate and butyrate

    DEFF Research Database (Denmark)

    Grivel, Jean-Claude

    2013-01-01

    The thermal decompositions of yttrium(III) propionate monohydrate (Y(C2H5CO2)3·H2O) and yttrium(III) butyrate dihydrate (Y(C3H7CO2)3·2H2O) were studied in argon by means of thermogravimetry, differential thermal analysis, IR-spectroscopy, X-ray diffraction and hot-stage microscopy. These two...

  17. Radioluminescent nuclear batteries with different phosphor layers

    International Nuclear Information System (INIS)

    Hong, Liang; Tang, Xiao-Bin; Xu, Zhi-Heng; Liu, Yun-Peng; Chen, Da

    2014-01-01

    Highlights: • We present and test the electrical properties of the nuclear battery. • The best thickness range for ZnS:Cu phosphor layer is 12–14 mg cm −2 for 147 Pm radioisotope. • The best thickness range for Y 2 O 2 S:Eu phosphor layer is 17–21 mg cm −2147 Pm radioisotope. • The battery with ZnS:Cu phosphor layer can provide higher energy conversion efficiency. • The mechanism affecting the nuclear battery output performance is revealed. - Abstract: A radioluminescent nuclear battery based on the beta radioluminescence of phosphors is presented, and which consists of 147 Pm radioisotope, phosphor layers, and GaAs photovoltaic cell. ZnS:Cu and Y 2 O 2 S:Eu phosphor layers for various thickness were fabricated. To investigate the effect of phosphor layer parameters on the battery, the electrical properties were measured. Results indicate that the optimal thickness ranges for the ZnS:Cu and Y 2 O 2 S:Eu phosphor layers are 12 mg cm −2 to 14 mg cm −2 and 17 mg cm −2 to 21 mg cm −2 , respectively. ZnS:Cu phosphor layer exhibits higher fluorescence efficiency compared with the Y 2 O 2 S:Eu phosphor layer. Its spectrum properly matches the spectral response of GaAs photovoltaic cell. As a result, the battery with ZnS:Cu phosphor layer indicates higher energy conversion efficiency than that with Y 2 O 2 S:Eu phosphor layer. Additionally, the mechanism of the phosphor layer parameters that influence the output performance of the battery is discussed through the Monte Carlo method and transmissivity test

  18. Selective extraction and recovery of rare earth metals from phosphor powders in waste fluorescent lamps using an ionic liquid system.

    Science.gov (United States)

    Yang, Fan; Kubota, Fukiko; Baba, Yuzo; Kamiya, Noriho; Goto, Masahiro

    2013-06-15

    The recycling of rare earth metals from phosphor powders in waste fluorescent lamps by solvent extraction using ionic liquids was studied. Acid leaching of rare earth metals from the waste phosphor powder was examined first. Yttrium (Y) and europium (Eu) dissolved readily in the acid solution; however, the leaching of other rare earth metals required substantial energy input. Ionization of target rare earth metals from the waste phosphor powders into the leach solution was critical for their successful recovery. As a high temperature was required for the complete leaching of all rare earth metals, ionic liquids, for which vapor pressure is negligible, were used as an alternative extracting phase to the conventional organic diluent. An extractant, N, N-dioctyldiglycol amic acid (DODGAA), which was recently developed, showed a high affinity for rare earth metal ions in liquid-liquid extraction although a conventional commercial phosphonic extractant did not. An effective recovery of the rare earth metals, Y, Eu, La and Ce, from the metal impurities, Fe, Al and Zn, was achieved from the acidic leach solution of phosphor powders using an ionic liquid containing DODGAA as novel extractant system. Copyright © 2013 Elsevier B.V. All rights reserved.

  19. Y{sub 2}O{sub 3}: Dy{sup 3+}/Li{sup +} phosphors synthesized by spray

    Energy Technology Data Exchange (ETDEWEB)

    Balderas X, R.; Carmona T, S.; Falcony, C., E-mail: scarmonat81@gmail.com [IPN, Centro de Investigacion y de Estudios Avanzados, Apdo. Postal 14-740, 07000 Ciudad de Mexico (Mexico)

    2017-11-01

    Dysprosium and lithium-activated yttrium oxide phosphor was synthesized at 1100 degrees Celsius by ultrasonic spray pyrolysis (Usp) using Di water as solvent and metal chlorides as precursors. The characteristic emission peak of Dy{sup 3+} due to the transitions {sup 4}F{sub 9/2} to {sup 6}H{sub 15/2} at 483 nm, {sup 4}F{sub 9/2} to {sup 6}H{sub 13/2} at 573 nm, {sup 4}F{sub 9/2} to {sup 6}H{sub 11/2} at 667 nm and {sup 4}F{sub 9/2} to {sup 6}H{sub 9/2} at 766 nm were observed. Scanning electron microscopy and transmission electron microscopy measurements were carried out to understand surface morphological features and the particle size of the phosphor. The uniformity of phase of Dy{sup 3+} - Li{sup +} doped Y{sub 2}O{sub 3} phosphors was checked by X-ray diffraction technique. The phosphors form clusters that were found to be ∼ 1 μm in size, however, particles that form these clusters have sizes between 40 and 120 nm. (Author)

  20. Phosphorous loads evaluation from soil

    International Nuclear Information System (INIS)

    Mezzanotte, V.

    1996-01-01

    With reference to the well known difficulty of quantifying non point phosphorous loads, as well as to their growing relative importance where point source leads decrease, a literature review has been carried out concerning soil export coefficients. On such basis, the values which seem to be the most appropriate for Italy have been estimated for different land use categories. The main mechanisms determining non point phosphorous load generation and the factors affecting their importance are also described. In the end, criteria for estimating the importance of non point sources in a basin are suggested to be used for deciding whether a traditional, parametric assessment (inevitably involving a certain error) can be acceptable or experimental measures are needed

  1. Uranium extraction in phosphoric acid

    International Nuclear Information System (INIS)

    Araujo Figueiredo, C. de

    1984-01-01

    Uranium is recovered from the phosphoric liquor produced from the concentrate obtained from phosphorus-uraniferous mineral from Itataia mines (CE, Brazil). The proposed process consists of two extraction cycles. In the first one, uranium is reduced to its tetravalent state and then extracted by dioctylpyrophosphoric acid, diluted in Kerosene. Re-extraction is carried out with concentrated phosphoric acid containing an oxidising agent to convert uranium to its hexavalent state. This extract (from the first cycle) is submitted to the second cycle where uranium is extracted with DEPA-TOPO (di-2-hexylphosphoric acid/tri-n-octyl phosphine oxide) in Kerosene. The extract is then washed and uranium is backextracted and precipitated as commercial concentrate. The organic phase is recovered. Results from discontinuous tests were satisfactory, enabling to establish operational conditions for the performance of a continuous test in a micro-pilot plant. (Author) [pt

  2. Luminescence studies on phosphor screens

    International Nuclear Information System (INIS)

    Panayiotakis, G.; Nomikos, C.; Bakas, A.; Proimos, B.

    1994-01-01

    We report our results on x-ray phosphor screens prepared of some new materials focusing attention on their efficiency under fluoroscopy conditions, on optimization conditions and on comparisons among the various materials. All data are presented in absolute values. A theoretical model is presented, that takes into account the granular structure of the screens, permitting the explanation and prediction of the luminescence properties of the screens. (authors)

  3. Luminescence studies on phosphor screens

    Energy Technology Data Exchange (ETDEWEB)

    Panayiotakis, G; Nomikos, C; Bakas, A; Proimos, B [Medical Physics Department, University of Patras, 265 00 Patras, Greece (Greece)

    1994-12-31

    We report our results on x-ray phosphor screens prepared of some new materials focusing attention on their efficiency under fluoroscopy conditions, on optimization conditions and on comparisons among the various materials. All data are presented in absolute values. A theoretical model is presented, that takes into account the granular structure of the screens, permitting the explanation and prediction of the luminescence properties of the screens. (authors). 12 refs, 3 figs.

  4. Consumption of Pt anode in phosphoric acid

    Energy Technology Data Exchange (ETDEWEB)

    Kamiya, N.; Urata, K.; Motohira, N.; Ota, K. [Yokohama National University, Yokohama (Japan)

    1997-12-05

    Consumption of Pt anode was investigated in phosphoric acid of various concentration. In 30-70wt% phosphoric acid, Pt dissolved at the rate of 19{mu}gcm{sup -2}h{sup -1}. On the other hand, in 85 wt% phosphoric acid, the amount increased to 0.91 mgcm{sup -2}h{sup -1} which is ca. 180 and 1800 times as much as in 1M sulfuric acid and 1M alkaline solution, respectively. In the diluted phosphoric acid solution, the Pt surface was covered with Pt oxides during the electrolysis, which would prevent the surface from corrosion. However, in the concentrated phosphoric acid, no such oxide surface was observed. Concentrated phosphoric acid might form stable complex with Pt species, therefore the uncovered bare Pt surface is situated in the serious corrosion condition under the high overvoltage and Pt would dissolve into the solution directly instead of forming the Pt oxides. 11 refs., 9 figs., 1 tab.

  5. Method of preparing a thermoluminescent phosphor

    Science.gov (United States)

    Lasky, Jerome B.; Moran, Paul R.

    1979-01-01

    A thermoluminescent phosphor comprising LiF doped with boron and magnesium is produced by diffusion of boron into a conventional LiF phosphor doped with magnesium. Where the boron dopant is made to penetrate only the outer layer of the phosphor, it can be used to detect shallowly penetrating radiation such as tritium beta ays in the presence of a background of more penetrating radiation.

  6. Mechanical properties of lanthanum and yttrium chromites

    Energy Technology Data Exchange (ETDEWEB)

    Paulik, S.W.; Armstrong, T.R. [Pacific Northwest National Lab., Richland, WA (United States)

    1996-12-31

    In an operating high-temperature (1000{degrees}C) solid oxide fuel cell (SOFC), the interconnect separates the fuel (P(O{sub 2}){approx}10{sup -16} atm) and the oxidant (P(O2){approx}10{sup 0.2} atm), while being electrically conductive and connecting the cells in series. Such severe atmospheric and thermal demands greatly reduce the number of viable candidate materials. Only two materials, acceptor substituted lanthanum chromite and yttrium chromite, meet these severe requirements. In acceptor substituted chromites (Sr{sup 2+} or Ca{sup 2+} for La{sup 3+}), charge compensation is primarily electronic in oxidizing conditions (through the formation of Cr{sup 4+}). Under reducing conditions, ionic charge compensation becomes significant as the lattice becomes oxygen deficient. The formation of oxygen vacancies is accompanied by the reduction of Cr{sup 4+} ions to Cr{sup 3+} and a resultant lattice expansion. The lattice expansion observed in large chemical potential gradients is not desirable and has been found to result in greatly reduced mechanical strength.

  7. Tungsten - Yttrium Based Nuclear Structural Materials

    Science.gov (United States)

    Ramana, Chintalapalle; Chessa, Jack; Martinenz, Gustavo

    2013-04-01

    The challenging problem currently facing the nuclear science community in this 21st century is design and development of novel structural materials, which will have an impact on the next-generation nuclear reactors. The materials available at present include reduced activation ferritic/martensitic steels, dispersion strengthened reduced activation ferritic steels, and vanadium- or tungsten-based alloys. These materials exhibit one or more specific problems, which are either intrinsic or caused by reactors. This work is focussed towards tungsten-yttrium (W-Y) based alloys and oxide ceramics, which can be utilized in nuclear applications. The goal is to derive a fundamental scientific understanding of W-Y-based materials. In collaboration with University of Califonia -- Davis, the project is designated to demonstrate the W-Y based alloys, ceramics and composites with enhanced physical, mechanical, thermo-chemical properties and higher radiation resistance. Efforts are focussed on understanding the microstructure, manipulating materials behavior under charged-particle and neutron irradiation, and create a knowledge database of defects, elemental diffusion/segregation, and defect trapping along grain boundaries and interfaces. Preliminary results will be discussed.

  8. Neutron scattering study of yttrium iron garnet

    Science.gov (United States)

    Shamoto, Shin-ichi; Ito, Takashi U.; Onishi, Hiroaki; Yamauchi, Hiroki; Inamura, Yasuhiro; Matsuura, Masato; Akatsu, Mitsuhiro; Kodama, Katsuaki; Nakao, Akiko; Moyoshi, Taketo; Munakata, Koji; Ohhara, Takashi; Nakamura, Mitsutaka; Ohira-Kawamura, Seiko; Nemoto, Yuichi; Shibata, Kaoru

    2018-02-01

    The nuclear and magnetic structure and full magnon dispersions of yttrium iron garnet Y3Fe5O12 have been studied using neutron scattering. The refined nuclear structure is distorted to a trigonal space group of R 3 ¯ . The highest-energy dispersion extends up to 86 meV. The observed dispersions are reproduced by a simple model with three nearest-neighbor-exchange integrals between 16 a (octahedral) and 24 d (tetrahedral) sites, Ja a, Ja d, and Jd d, which are estimated to be 0.00 ±0.05 , -2.90 ±0.07 , and -0.35 ±0.08 meV, respectively. The lowest-energy dispersion below 14 meV exhibits a quadratic dispersion as expected from ferromagnetic magnons. The imaginary part of q -integrated dynamical spin susceptibility χ″(E ) exhibits a square-root energy dependence at low energies. The magnon density of state is estimated from χ″(E ) obtained on an absolute scale. The value is consistent with the single chirality mode for the magnon branch expected theoretically.

  9. Studies on yttrium-containing smart alloys

    Energy Technology Data Exchange (ETDEWEB)

    Klein, Felix; Wegener, Tobias; Litnovsky, Andrey; Rasinski, Marcin; Linsmeier, Christian [Forschungszentrum Juelich GmbH, Institut fuer Energie- und Klimaforschung - Plasmaphysik (Germany); Mayer, Joachim [Ernst Ruska-Centrum, 52425 Juelich (Germany)

    2016-07-01

    Tungsten is the main candidate as plasma-facing armour material for future fusion reactors, like DEMO. Advantages of tungsten include high melting point, high thermal conductivity, low tritium retention, and low erosion yield. A problem is oxide volatilisation under accidental conditions where the temperature of the first wall can reach 1200 K to 1450 K and air ingress occurs. Therefore smart tungsten alloys are developed. Smart alloys are supposed to preserve properties of tungsten during plasma operation coupled with suppressed tungsten oxide formation in case of an accident. Lab-scale tungsten-chromium-yttrium (W-Cr-Y) samples prepared by magnetron sputtering are used as model system. The mechanisms of oxidation and its dynamics are studied using a thermogravimetric system, focussed ion beam, and electron microscopy. A composition scan was conducted: The new material composition featuring W, ∝ 12 wt.% Cr, ∝ 0.3 wt.% Y showed strongest suppression of oxidation, no pores, and least internal oxidation. At 1273 K in argon-oxygen atmosphere an oxidation rate of 3 . 10{sup -6} mg{sup 2}cm{sup -4}s{sup -1} was measured. At 1473 K ternary W-Cr-Y alloys suppressed evaporation up to 20 min while for W-Cr evaporation was already evident after 5 min. Comparison of passivation in dry and humid atmosphere, at temperatures of 1073 K to 1473 K is performed.

  10. Yttrium-90 microsphere induced gastrointestinal tract ulceration

    Directory of Open Access Journals (Sweden)

    Rikabi Ali A

    2008-09-01

    Full Text Available Abstract Background Radiomicrosphere therapy (RT utilizing yttrium-90 (90Y microspheres has been shown to be an effective regional treatment for primary and secondary hepatic malignancies. We sought to determine a large academic institution's experience regarding the extent and frequency of gastrointestinal complications. Methods Between 2004 and 2007, 27 patients underwent RT for primary or secondary hepatic malignancies. Charts were subsequently reviewed to determine the incidence and severity of GI ulceration. Results Three patients presented with gastrointestinal bleeding and underwent upper endoscopy. Review of the pretreatment angiograms showed normal vascular anatomy in one patient, sclerosed hepatic vasculature in a patient who had undergone prior chemoembolization in a second, and an aberrant left hepatic artery in a third. None had undergone prophylactic gastroduodenal artery embolization. Endoscopic findings included erythema, mucosal erosions, and large gastric ulcers. Microspheres were visible on endoscopic biopsy. In two patients, gastric ulcers were persistent at the time of repeat endoscopy 1–4 months later despite proton pump inhibitor therapy. One elderly patient who refused surgical intervention died from recurrent hemorrhage. Conclusion Gastrointestinal ulceration is a known yet rarely reported complication of 90Y microsphere embolization with potentially life-threatening consequences. Once diagnosed, refractory ulcers should be considered for aggressive surgical management.

  11. Phosphors for X-ray intensification screens

    International Nuclear Information System (INIS)

    Rebatin, J.G.

    1980-01-01

    An improved rare earth oxyhalide phosphor for x-ray intensification screens is described. The phosphors, of formula LnOX.T where Ln = La or Gd, X = Cl or Br and T = Tm or Tb, are mixed with a small amount of a trivalent antimony compound. The addition of antimony overcomes ageing due to attack by atmospheric moisture and renders the phosphor freeflowing so that dispersions can be readily made. Preferably the phosphor is washed with an aqueous solution of the antimony compound and the compound is the fluoride, chloride or butoxide, or potassium antimony tartrate. (U.K.)

  12. Continuous production of phosphor YAG:Tb nanoparticles by hydrothermal synthesis in supercritical water

    International Nuclear Information System (INIS)

    Hakuta, Yukiya; Haganuma, Tsukasa; Sue, Kiwamu; Adschiri, Tadafumi; Arai, Kunio

    2003-01-01

    Phosphor YAG:Tb ((Y 2.7 Tb 0.3 )Al 5 O 12 ) nano particles were synthesized by a hydrothermal method at supercritical conditions (400 deg. C and 30 MPa) using a flow reactor. Hydroxide sol solutions formed by stoichiometric aluminum nitrate, yttrium nitrate, terbium nitrate and potassium hydroxide solutions. The relationship between particle size and experimental variables including pH, concentration of coexistent ions and hydroxide sol were investigated. Particles were characterized by XRD, TEM and photo-luminescence measurements. Particle size of YAG:Tb became finer as pH was increased or potassium nitrate concentration of the starting metal salt solution was increased. By removing the coexisting ions (NO 3 - , K + ) from the metal salt solution, single phase YAG:Tb particles with 20 nm particle size were obtained. The emission spectra of YAG:Tb particles of 14 nm shows a blue shift

  13. Yttrium implantation effects on extra low carbon steel and pure iron

    Energy Technology Data Exchange (ETDEWEB)

    Caudron, E.; Buscail, H. [Clermont-Ferrand-2 Univ., Le Puy en Velay (France). Lab. Vellave d`Elaboration; Jacob, Y.P.; Stroosnijder, M.F. [Institute for Advanced Materials, Joint Research Center, The European Commission, 21020, Ispra (Vatican City State, Holy See) (Italy); Josse-Courty, C. [Laboratoire de Recherche sur la Reactivite des Solides, UMR 56-13 CNRS, UFR Sciences et Techniques, 9 Avenue A. Savary, B.P. 400, 21011, Dijon Cedex (France)

    1999-05-25

    Extra low carbon steel and pure electrolytic iron samples were yttrium implanted using ion implantation technique. Compositions and structures of pure iron and steel samples were investigated before and after yttrium implantation by several analytical and structural techniques (RBS, SIMS, RHEED and XRD) to observe the yttrium implantation depth profiles in the samples. This paper shows the different effects of yttrium implantations (compositions and structures) according to the implanted sample nature. (orig.) 23 refs.

  14. Studies on yttrium oxide coatings for corrosion protection against molten uranium

    International Nuclear Information System (INIS)

    Chakravarthy, Y.; Bhandari, Subhankar; Pragatheeswaran; Thiyagarajan, T.K.; Ananthapadmanabhan, P.V.; Das, A.K.; Kumar, Jay; Kutty, T.R.G.

    2012-01-01

    Yttrium oxide is resistant to corrosion by molten uranium and its alloys. Yttrium oxide is recommended as a protective oxide layer on graphite and metal components used for melting and processing uranium and its alloys. This paper presents studies on the efficacy of plasma sprayed yttrium oxide coatings for barrier applications against molten uranium

  15. Pressure of saturated vapor of yttrium and zirconium acetylacetonates

    Energy Technology Data Exchange (ETDEWEB)

    Trembovetskij, G.V.; Berdonosov, S.S.; Murav' eva, I.A.; Martynenko, L.I. (Moskovskij Gosudarstvennyj Univ. (USSR))

    1984-08-01

    The static method and the flow method using /sup 91/Y and /sup 95/Zr radioactive indicators have been applied to determine pressure of saturated vapour of yttrium and zirconium acetylacetonates. Values of thermodynamic functions ..delta..Hsub(subl)=(98+-16)kJ/mol and ..delta..Ssub(subl.)=(155+-30)J/mol x K are calculated for sublimation of yttrium acetylacetonate. For sublimation of zirconium acetylacetonates ..delta..Hsub(subl) equals (116+-38) kJ/mol and ..delta..Ssub(subl) is equal to (198+-65) J/molxK.

  16. Determination of copper oxidizing power in superconducting yttrium ceramics

    International Nuclear Information System (INIS)

    Pontaler, R.P.; Lebed', N.B.

    1989-01-01

    A new photometric method for determining the formal copper degree of oxidation and oxygen deficiency in superconducting high-temperature oxides containing yttrium, barium and copper is developed. The method is based on oxidation of Co(2) complex with EDTA by Cu(3) ions in acetrate buffer solution with pH 4.2-4.7 and allows one to determine 1-10% of Cu(3). Relative standard deviation when determining Cu(3) makes up 0.03-0.05. Using a qualitative reaction with the application of sodium vanadate hydrochloride solution the absence of peroxide compound in superconducting yttrium ceramics is ascertained

  17. Surface modifications induced by yttrium implantation on low manganese-carbon steel

    Energy Technology Data Exchange (ETDEWEB)

    Caudron, E.; Buscail, H. [Univ. Blaise Pascal Clermont-Fd II, Le Puy en Velay (France). Lab. Vellave d' Elaboration et d' Etude des Materiaux; Haanapel, V.A.C.; Jacob, Y.P.; Stroosnijder, M.F. [Institute for Health and Consumer Protection, Joint Research Center, The European Commission, 21020, Ispra (Italy)

    1999-12-15

    Low manganese-carbon steel samples were ion implanted with yttrium. Sample compositions and structures were investigated before and after yttrium implantations to determine the yttrium distribution in the sample. Yttrium implantation effects were characterized using several analytical and structural techniques such as X-ray photoelectron spectroscopy, reflection high energy electron diffraction, X-ray diffraction, glancing angle X-ray diffraction and Rutherford backscattering spectrometry. In this paper it is shown that correlation between composition and structural analyses provides an understanding of the main compounds induced by yttrium implantation in low manganese-carbon steel. (orig.)

  18. Selective extraction and recovery of rare earth metals from phosphor powders in waste fluorescent lamps using an ionic liquid system

    International Nuclear Information System (INIS)

    Yang, Fan; Kubota, Fukiko; Baba, Yuzo; Kamiya, Noriho; Goto, Masahiro

    2013-01-01

    Highlights: • Recycling of rare earth metals from fluorescent lamps was conducted by ionic liquid-mediated extraction. • Acid leaching from a waste phosphor powder was carried out using sulfuric and nitric acids. • An ionic liquid was used as extracting solvent for the rare earth metals. • Selective extraction of rare earth metals from leach solutions was attained. •The extracting ionic liquid phase was recyclable in the recovery process. -- Abstract: The recycling of rare earth metals from phosphor powders in waste fluorescent lamps by solvent extraction using ionic liquids was studied. Acid leaching of rare earth metals from the waste phosphor powder was examined first. Yttrium (Y) and europium (Eu) dissolved readily in the acid solution; however, the leaching of other rare earth metals required substantial energy input. Ionization of target rare earth metals from the waste phosphor powders into the leach solution was critical for their successful recovery. As a high temperature was required for the complete leaching of all rare earth metals, ionic liquids, for which vapor pressure is negligible, were used as an alternative extracting phase to the conventional organic diluent. An extractant, N, N-dioctyldiglycol amic acid (DODGAA), which was recently developed, showed a high affinity for rare earth metal ions in liquid–liquid extraction although a conventional commercial phosphonic extractant did not. An effective recovery of the rare earth metals, Y, Eu, La and Ce, from the metal impurities, Fe, Al and Zn, was achieved from the acidic leach solution of phosphor powders using an ionic liquid containing DODGAA as novel extractant system

  19. Selective extraction and recovery of rare earth metals from phosphor powders in waste fluorescent lamps using an ionic liquid system

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Fan; Kubota, Fukiko; Baba, Yuzo [Department of Applied Chemistry, Graduate School of Engineering, Kyushu University, 744 Motooka, Fukuoka 819-0395 (Japan); Kamiya, Noriho [Department of Applied Chemistry, Graduate School of Engineering, Kyushu University, 744 Motooka, Fukuoka 819-0395 (Japan); Center for Future Chemistry, Kyushu University, 744 Motooka, Fukuoka 819-0395 (Japan); Goto, Masahiro, E-mail: m-goto@mail.cstm.kyushu-u.ac.jp [Department of Applied Chemistry, Graduate School of Engineering, Kyushu University, 744 Motooka, Fukuoka 819-0395 (Japan); Center for Future Chemistry, Kyushu University, 744 Motooka, Fukuoka 819-0395 (Japan)

    2013-06-15

    Highlights: • Recycling of rare earth metals from fluorescent lamps was conducted by ionic liquid-mediated extraction. • Acid leaching from a waste phosphor powder was carried out using sulfuric and nitric acids. • An ionic liquid was used as extracting solvent for the rare earth metals. • Selective extraction of rare earth metals from leach solutions was attained. •The extracting ionic liquid phase was recyclable in the recovery process. -- Abstract: The recycling of rare earth metals from phosphor powders in waste fluorescent lamps by solvent extraction using ionic liquids was studied. Acid leaching of rare earth metals from the waste phosphor powder was examined first. Yttrium (Y) and europium (Eu) dissolved readily in the acid solution; however, the leaching of other rare earth metals required substantial energy input. Ionization of target rare earth metals from the waste phosphor powders into the leach solution was critical for their successful recovery. As a high temperature was required for the complete leaching of all rare earth metals, ionic liquids, for which vapor pressure is negligible, were used as an alternative extracting phase to the conventional organic diluent. An extractant, N, N-dioctyldiglycol amic acid (DODGAA), which was recently developed, showed a high affinity for rare earth metal ions in liquid–liquid extraction although a conventional commercial phosphonic extractant did not. An effective recovery of the rare earth metals, Y, Eu, La and Ce, from the metal impurities, Fe, Al and Zn, was achieved from the acidic leach solution of phosphor powders using an ionic liquid containing DODGAA as novel extractant system.

  20. On the use of hydrogen peroxide as a masking agent for the determination of yttrium in uranium oxide - yttrium oxide mixture

    International Nuclear Information System (INIS)

    Rastogi, R.K.; Chaudhuri, N.K.; Rizvi, G.H.; Subramanian, M.S.

    1985-01-01

    The use of peroxide as a masking agent for uranium during the EDTA titration of yttrium in an yttrium-uranium mixture containing large amounts of uranium was investigated. High acetate ion concentration was necessary to keep the peroxy complex of uranium in solution during the titration. It was observed that uranium could be tolerated up to 500 mg in the determination of yttrium with 0.5 ml of 30% hydrogen peroxide in approx. 1M acetate medium. The precision and accuracy of the method based on 16 determinations of yttrium at 6-16 mg level in the presence of 300 mg uranium was found to be +-0.2%. (author)

  1. YAG:Dy – Based single white light emitting phosphor produced by solution combustion synthesis

    Energy Technology Data Exchange (ETDEWEB)

    Carreira, J.F.C., E-mail: correiacarreira@ua.pt; Sedrine, N. Ben; Monteiro, T.; Rino, L.

    2017-03-15

    Dysprosium-doped yttrium aluminum garnet (YAG:Dy) phosphor was successfully produced by a Solution Combustion Synthesis (SCS) using a mixture of two fuels (urea and glycine). The effects of Dy concentration and annealing temperature were studied by X-ray diffraction (XRD), Raman spectroscopy (RS), photoluminescence (PL) and photoluminescence excitation (PLE). X-ray diffraction results show that the phosphors are single phase YAG with crystallite size ranging from 45 to 82 nm. Raman spectroscopy corroborates these results and show that the introduction of Dy ions in the YAG lattice results in additional Raman modes. Room temperature photoluminescence results confirm the introduction of the ion in the host lattice and its optical activation for all the Dy concentrations. CIE1931 color coordinates show that the samples’ emission lays in the near white region. The highest intraionic emission intensity was achieved for a Dy concentration of 2 mol% and annealing temperature of 1400 °C. Photoluminescence excitation results show that the ions luminescence is preferential excited with 351.8 and 365.8 nm wavelength photons.

  2. Emission spectra of yttrium vanadate doped with bismuth and dysprosium

    International Nuclear Information System (INIS)

    Pawar, B.V.; Patil, R.N.

    1975-01-01

    The fluorescence spectra of YVO 4 :Bi and YVO 4 :Bi:Dy phosphors under X-rays and ultra-violet radiation have been studied. The observations on the phosphors with constant Bi 3+ and varying Dy 3+ concentration can be attributed to radiationless transfer of energy from Bi 3+ to Dy 3+ coupled with non-radiative losses due to self-quenching at higher level of Dy 3+ concentration. While the observations on the phosphors with constant Dy 3+ and varying Bi 3+ concentration indicate that there is radiationless transfer from Bi 3+ to Dy 3+ under X-ray or UV irradiation. (author)

  3. High performance yttrium-doped BSCF hollow fibre membranes

    DEFF Research Database (Denmark)

    Haworth, P.; Smart, S.; Glasscock, Julie

    2012-01-01

    measurements in air was similar for both compositions, suggesting that the higher oxygen fluxes obtained for BSCFY hollow fibres could be attributed to the higher non-stoichiometry due to yttrium addition to the BSCF crystal structure. In addition, the improvement of oxygen fluxes for small wall thickness (∼0...

  4. Microstructure and defect chemistry of yttrium aluminium garnet ceramics

    International Nuclear Information System (INIS)

    Schuh, L.H.

    1989-01-01

    This thesis describes basic aspects concerning the defect chemistry and the microstructure of yttrium aluminium garnet ceramics. The work consists of three parts: a literature study, an experimental part and a section giving computer simulation data of defects. (author). 320 refs.; 68 figs.; 72 schemes; 32 tabs

  5. A thermal neutron scattering law for yttrium hydride

    Science.gov (United States)

    Zerkle, Michael; Holmes, Jesse

    2017-09-01

    Yttrium hydride (YH2) is of interest as a high temperature moderator material because of its superior ability to retain hydrogen at elevated temperatures. Thermal neutron scattering laws for hydrogen bound in yttrium hydride (H-YH2) and yttrium bound in yttrium hydride (Y-YH2) prepared using the ab initio approach are presented. Density functional theory, incorporating the generalized gradient approximation (GGA) for the exchange-correlation energy, is used to simulate the face-centered cubic structure of YH2 and calculate the interatomic Hellmann-Feynman forces for a 2 × 2 × 2 supercell containing 96 atoms. Lattice dynamics calculations using PHONON are then used to determine the phonon dispersion relations and density of states. The calculated phonon density of states for H and Y in YH2 are used to prepare H-YH2 and Y-YH2 thermal scattering laws using the LEAPR module of NJOY2012. Analysis of the resulting integral and differential scattering cross sections demonstrates adequate resolution of the S(α,β) function. Comparison of experimental lattice constant, heat capacity, inelastic neutron scattering spectra and total scattering cross section measurements to calculated values are used to validate the thermal scattering laws.

  6. Structural and dielectric properties of yttrium substituted nickel ferrites

    International Nuclear Information System (INIS)

    Ognjanovic, Stevan M.; Tokic, Ivan; Cvejic, Zeljka; Rakic, Srdjan; Srdic, Vladimir V.

    2014-01-01

    Graphical abstract: - Highlights: • Dense NiFe 2−x Y x O 4 ceramics (with 0 ≤ x ≤ 0.3) were prepared. • Pure spinels were obtained for x ≤ 0.07 while for x ≥ 0.15 samples had secondary phases. • With addition of yttrium, ac conductivity slightly increased. • We suggest several effects that can explain the observed changes in ac conduction. • With addition of yttrium, dielectric constant increased while the tg δ decreased. - Abstract: The influence of Y 3+ ions on structural and dielectric properties of nickel ferrites (NiFe 2−x Y x O 4 , where 0 ≤ x ≤ 0.3) has been studied. The as-synthesized samples, prepared by the co-precipitation method, were analyzed by XRD and FTIR which suggested that Y 3+ ions were incorporated into the crystal lattice for all the samples. However, the XRD analysis of the sintered samples showed that secondary phases appear in the samples with x > 0.07. The samples have densities greater than 90% TD and the SEM images showed that the grain size decreases with the addition of yttrium. Dielectric properties measured from 150 to 25 °C in the frequency range of 100 Hz–1 MHz showed that the addition of yttrium slightly increases the ac conductivity and decreases the tg δ therefore making the materials better suited for the use in microwave devices

  7. Thermal decomposition of yttrium(III) hexanoate in argon

    DEFF Research Database (Denmark)

    Grivel, Jean-Claude; Suarez Guevara, Maria Josefina; Attique, Fahmida

    2015-01-01

    The thermal decomposition of yttrium(III) hexanoate (Y(C5H11CO2)3)·xH2O in argon was studied by means of thermogravimetry, differential thermal analysis, IR-spectroscopy, X-ray diffraction at a laboratory Cu-tube source and in-situ experiments at a synchrotron radiation source as well as hot...

  8. Thermal decomposition of Yttrium(III) isovalerate in argon

    DEFF Research Database (Denmark)

    Grivel, Jean-Claude; Yue, Zhao; Tang, Xiao

    2016-01-01

    The thermal behaviour of yttrium(III) isovalerate (Y(C4H9CO2)3) was studied in argon by means of thermogravimetry, differential thermal analysis, FTIR-spectroscopy, hot-stage optical microscopy and X-ray diffraction with a laboratory Cu-tube source as well as with a synchrotron radiation source...

  9. Thermal decomposition of yttrium(III) valerate in argon

    DEFF Research Database (Denmark)

    Grivel, Jean-Claude; Yue, Zhao; Tang, Xiao

    2014-01-01

    The thermal decomposition of yttrium(III) valerate (Y(C4H9CO2)3) was studied in argon by means of thermogravimetry, differential thermal analysis, IR-spectroscopy, X-ray diffraction, in-situ synchrotron diffraction and hot-stage microscopy as well as room temperature optical microscopy. Melting...

  10. Polymorphism and electrical behaviour of yttrium thin films

    International Nuclear Information System (INIS)

    Kaul, U.K.; Srivastava, O.N.

    1978-01-01

    It appears that the thickness-resistivity behaviour of yttrium embodying a thickness-dependent polymorphic phase transition can be explained in terms of surface scattering by taking into account the effect of the change in phase. It is interesting to note that, as a result of the polymorphic transition, the resistivity-thickness curve has an unusual shape. (Auth.)

  11. A new f.c.c. phase in yttrium films

    International Nuclear Information System (INIS)

    Kaul, V.K.; Srivastava, O.N.

    1976-01-01

    A new polymorphic phase characterised by a face-centered cubic structure, with lattice parameter 5.83 +- 0.02A, has been identified in thin films of yttrium. Electron diffraction evidence and electrical resistivity measurements have been carried out in order to detect the new f.c.c. phase. (Auth.)

  12. Pretreatment of industrial phosphoric acid by Algerian filter-aids

    International Nuclear Information System (INIS)

    Mellah, A.; Setti, Louisa; Chegrouche, Salah

    1993-01-01

    The present work involves the filtration of industrial phosphoric acid by different filter-aids such as kieselguhr, celite and bleaching clay. The retention of substances contained in wet phosphoric acid was determined using the three filter-aids. Thus, the phosphoric acid, obtained by filtration on kieselguhr has the same specifications as technical phosphoric acid produced by Rhone-Poulenc (France) as standard

  13. Method of purifying phosphoric acid after solvent extraction

    International Nuclear Information System (INIS)

    Kouloheris, A.P.; Lefever, J.A.

    1979-01-01

    A method of purifying phosphoric acid after solvent extraction is described. The phosphoric acid is contacted with a sorbent which sorbs or takes up the residual amount of organic carrier and the phosphoric acid separated from the organic carrier-laden sorbent. The method is especially suitable for removing residual organic carrier from phosphoric acid after solvent extraction uranium recovery. (author)

  14. 46 CFR 151.50-23 - Phosphoric acid.

    Science.gov (United States)

    2010-10-01

    ... 46 Shipping 5 2010-10-01 2010-10-01 false Phosphoric acid. 151.50-23 Section 151.50-23 Shipping... BULK LIQUID HAZARDOUS MATERIAL CARGOES Special Requirements § 151.50-23 Phosphoric acid. (a) The term phosphoric acid as used in this subpart shall include, in addition to phosphoric acid, aqueous solutions of...

  15. NIR optimized dual mode photoluminescence in Nd doped Y{sub 2}O{sub 3} ceramic phosphor

    Energy Technology Data Exchange (ETDEWEB)

    Sukul, Prasenjit Prasad; Mahata, Manoj Kumar; Kumar, Kaushal, E-mail: kumar.bhu@gmail.com

    2017-05-15

    Authors here report the dual mode photo luminescence emission in neodymium doped yttrium oxide ceramic phosphor upon 808 nm diode laser excitation. Single cubic phase Nd{sup 3+} doped Y{sub 2}O{sub 3} phosphor was synthesized using urea assisted combustion route. Nd{sup 3+} doped Y{sub 2}O{sub 3} ceramic phosphor has given photoluminescence in a wide wavelength range covering near infrared window (850–1100 nm) to the visible region i.e. green (525 nm) and red (680 nm) upon 808 nm diode laser excitation. The two most intense bands on 808 nm excitation were observed at 750 nm and 1064 nm due to the upconversion and downconversion emission processes. The sample was also tested for emission using 980 nm and intense green emission due to the trace presence of Er{sup 3+} in the raw materials was seen in the sample. The excitation power dependent upconversion measurements have shown that transitions {sup 4}F{sub 9/2}→{sup 4}I{sub 9/2} and {sup 4}S{sub 3/2}→{sup 4}I{sub 9/2} are thermally coupled and can be used to estimate the sample temperature using Boltzmann relation.

  16. Luminescence properties of Y2O3:Bi3+, Yb3+ co-doped phosphor for application in solar cells

    Science.gov (United States)

    Lee, E.; Kroon, R. E.; Terblans, J. J.; Swart, H. C.

    2018-04-01

    Bismuth (Bi3+) and ytterbium (Yb3+) co-doped yttrium oxide (Y2O3) phosphor powder was successfully synthesised using the co-precipitation technique. The X-ray diffraction (XRD) patterns confirmed that a single phase cubic structure with a Ia-3 space group was formed. The visible emission confirmed the two symmetry sites, C2 and S6, found in the Y2O3 host material and revealed that Bi3+ ions preferred the S6 site as seen the stronger emission intensity. The near-infrared (NIR) emission of Yb3+ increased significantly by the presence of the Bi3+ ions when compared to the singly doped Y2O3:Yb3+ phosphor with the same Yb3+ concentration. An increase in the NIR emission intensity was also observed by simply increasing the Yb3+ concentration in the Y2O3:Bi3+, Yb3+ phosphor material where the intensity increased up to x = 5.0 mol% of Yb3+ before decreasing due to concentration quenching.

  17. Phosphorous-Containing Polymers for Regenerative Medicine

    Science.gov (United States)

    Watson, Brendan M.; Kasper, F. Kurtis; Mikos, Antonios G.

    2014-01-01

    Disease and injury have resulted in a large, unmet need for functional tissue replacements. Polymeric scaffolds can be used to deliver cells and bioactive signals to address this need for regenerating damaged tissue. Phosphorous-containing polymers have been implemented to improve and accelerate the formation of native tissue both by mimicking the native role of phosphorous groups in the body and by attachment of other bioactive molecules. This manuscript reviews the synthesis, properties, and performance of phosphorous-containing polymers that can be useful in regenerative medicine applications. PMID:24565855

  18. Evidence of yttrium silicate inclusions in YSZ-porcelain veneers.

    Science.gov (United States)

    Stoner, Brian R; Griggs, Jason A; Neidigh, John; Piascik, Jeffrey R

    2014-04-01

    This report introduces the discovery of crystalline defects that can form in the porcelain veneering layer when in contact with yttria-stabilized zirconia (YSZ). The focus was on dental prostheses and understanding the defects that form in the YSZ/porcelain system; however the data reported herein may have broader implications toward the use and stability of YSZ-based ceramics in general. Specimens were cut from fully sintered YSZ plates and veneering porcelain was applied (X-ray (EDAX) was used for microstructural and elemental analysis. EDAX, for chemical analysis and transmission electron diffraction (TED) for structural analysis were both performed in the transmission electron microscope (TEM). Additionally, in order to spatially resolve Y-rich precipitates, micro-CT scans were conducted at varying depths within the porcelain veneer. Local EDAX (SEM) was performed in the regions of visible inclusions and showed significant increases in yttrium concentration. TEM specimens also showed apparent inclusions in the porcelain and selected area electron diffraction was performed on these regions and found the inclusions to be crystalline and identified as either yttrium-silicate (Y2 SiO5 ) or yttrium-disilicate (Y2 Si2 O7 ). Micro-CT data showed that yttrium-silicate precipitates were distributed throughout the thickness of the porcelain veneer. Future studies are needed to determine whether many of the premature failures associated with this materials system may be the result of crystalline flaws that form as a result of high temperature yttrium diffusion near the surfaces of YSZ. © 2013 Wiley Periodicals, Inc.

  19. Yttrium-90 microspheres for the treatment of hepatocellular carcinoma.

    Science.gov (United States)

    Geschwind, Jean Francois H; Salem, Riad; Carr, Brian I; Soulen, Michael C; Thurston, Kenneth G; Goin, Kathleen A; Van Buskirk, Mark; Roberts, Carol A; Goin, James E

    2004-11-01

    Unresectable hepatocellular carcinoma is extremely difficult to treat. TheraSphere consists of yttrium-90 (a pure beta emitter) microspheres, which are injected into the hepatic arteries. This article reviews the safety and survival of patients with hepatocellular carcinoma who were treated with yttrium-90 microspheres. Eighty patients were selected from a database of 108 yttrium-90 microsphere-treated patients and were staged by using Child-Pugh, Okuda, and Cancer of the Liver Italian Program scoring systems. Patients were treated with local, regional, and whole-liver approaches. Survival from first treatment was analyzed with Kaplan-Meier and Cox regression methods. Adverse events and complications of treatment were coded by using the Southwest Oncology Group toxicity scoring system. Patients received liver doses ranging from 47 to 270 Gy. Thirty-two patients (40%) received more than 1 treatment. Survival correlated with pretreatment Cancer of the Liver Italian Program scores ( P = .002), as well as with the individual Cancer of the Liver Italian Program components, Child-Pugh class, alpha-fetoprotein levels, and percentage of tumor replacement. Patients classified as Okuda stage I (n = 54) and II (n = 26) had median survival durations and 1-year survival rates of 628 days and 63%, and 384 days and 51%, respectively ( P = .02). One patient died of liver failure judged as possibly related to treatment. Thus, in selected patients with hepatocellular carcinoma, yttrium-90 microsphere treatment is safe and well tolerated. On the basis of these results, a randomized controlled trial is warranted comparing yttrium-90 microsphere treatment with transarterial chemoembolization by using the Cancer of the Liver Italian Program system for prospective stratified randomization.

  20. Magneto-optical studies of valence instability in europium and terbium phosphors

    Energy Technology Data Exchange (ETDEWEB)

    Rodrigues, Lucas C.V. [Department of Chemistry, University of Turku, FI-20014 Turku (Finland); Instituto de Química, Universidade de São Paulo, São Paulo, -SP (Brazil); Hölsä, Jorma [Department of Chemistry, University of Turku, FI-20014 Turku (Finland); Instituto de Química, Universidade de São Paulo, São Paulo, -SP (Brazil); Turku University Centre for Materials and Surfaces (MatSurf) (Finland); University of the Free State, Department of Physics, Bloemfontein (South Africa); Brito, Hermi F. [Instituto de Química, Universidade de São Paulo, São Paulo, -SP (Brazil); Maryško, Miroslav [Institute of Physics, The Academy of Sciences of the Czech Republic, Cukrovarnická 10, CZ-162 53 Praha 6 (Czech Republic); Matos, Jivaldo R. [Instituto de Química, Universidade de São Paulo, São Paulo, -SP (Brazil); Paturi, Petriina [Wihuri Physical Laboratory, Department of Physics and Astronomy, University of Turku, FI-20014 Turku (Finland); Rodrigues, Rodrigo V. [Instituto de Química, Universidade de São Paulo, São Paulo, -SP (Brazil); Lastusaari, Mika, E-mail: miklas@utu.fi [Department of Chemistry, University of Turku, FI-20014 Turku (Finland); Turku University Centre for Materials and Surfaces (MatSurf) (Finland)

    2016-02-15

    The impurities and dopants' inappropriate valences may deteriorate the performance of luminescent materials, cause waste of the precious rare earth (R) material and thus incur financial losses. The usual methods to detect the valence of rare earths; XPS, Mössbauer and XANES spectroscopies, are not sensitive enough for low concentrations and the EPR methods are not very suitable for powders. In this work, the comparison between the theoretical and experimental temperature-dependent paramagnetic susceptibilities was used to obtain quantitatively the concentrations of the impurity valence in Eu{sub 2}O{sub 2}S and Tb{sub 2}O{sub 2}SO{sub 4}, both containing nominally only R{sup 3+}. Minute (ppm level) Eu{sup 2+} impurities could be analyzed because of the huge difference in the paramagnetic susceptibility between Eu{sup 2+} and Eu{sup 3+} at low temperatures. However, temperatures below 50 K are then needed whilst the Tb{sup IV} impurity in a Tb{sup 3+} matrix can be observed already at higher temperatures. The latter method based on comparing the slopes of the Tb{sup 3+}/Tb{sup IV} paramagnetic susceptibility vs temperature curves for the Tb{sup 3+}/Tb{sup IV} couple is less sensitive than for the Eu{sup 2+}/Eu{sup 3+} one. Finally, the host independent temperature evolution of the paramagnetic susceptibility was calculated for Gd{sup 3+} (or Eu{sup 2+} or Tb{sup IV}) to yield a simple analytical expression to be used universally. - Highlights: • Wave functions for Eu{sup 3+}/Tb{sup 3+} with crystal field effect calculated for oxysulfide/sulfate. • Paramagnetic susceptibility between 4 and 300 K simulated for 4f{sup 6/7/8} configurations. • Amount of valence impurities (Eu{sup 2+} and Tb{sup IV}) evaluated from susceptibility data. • Waste of raw materials and loss of luminescence intensity of phosphors can be avoided.

  1. Improvements in x-ray image converters and phosphors

    International Nuclear Information System (INIS)

    Rabatin, J.G.

    1981-01-01

    Improvements to an X-ray image converter comprising crystals of rare earth phosphor admixtures are described. The phosphor admixtures utilize thulium-activated lanthanum and/or gadolinium oxyhalide phosphor material to increase the relative speed and resolution of an X-ray image compared with conventional rare earth phosphors. Examples of various radiographic screens containing one or more of the phosphor materials are given. (U.K.)

  2. Characteristics of the Panasonic UD-802 phosphors

    International Nuclear Information System (INIS)

    Ben-Shachar, B.; Catchen, G.L.; Hoffman, J.M.

    1989-01-01

    Several basic dosimetric characteristics of Li 2 B 4 O 7 :Cu and CaSO 4 :Tm phosphors in Panasonic UD-802 dosemeters were measured. The TL dose response linearity was determined over the useful range of personnel and environmental dosimetry (0.005 - 10 mGy), and the minimum measurable doses were calculated. The intrinsic ultraviolet (UV) radiation sensitivity of both phosphors was checked before and after γ irradiation for the purpose of re-assessing high doses. The results indicate that Li 2 B 4 O 7 :Cu is UV sensitive and, therefore, re-assessment is not applicable. Although the CaSO 4 :Tm phosphor exhibited UV sensitivity after γ irradiation, the results were not consistent with those reported earlier and more study is required. The fading of both phosphors was evaluated in Panasonic UD-801 dosemeters for periods up to 90 days. (author)

  3. Phosphate Phosphors for Solid-State Lighting

    CERN Document Server

    Shinde, Kartik N; Swart, H C; Park, Kyeongsoon

    2012-01-01

    The idea for this book arose out of the realization that, although excellent surveys and a phosphor handbook are available, there is no single source covering the area of phosphate based phosphors especially for lamp industry. Moreover, as this field gets only limited attention in most general books on luminescence, there is a clear need for a book in which attention is specifically directed toward this rapidly growing field of solid state lighting and its many applications. This book is aimed at providing a sound introduction to the synthesis and optical characterization of phosphate phosphor for undergraduate and graduate students as well as teachers and researchers. The book provides guidance through the multidisciplinary field of solid state lighting specially phosphate phosphors for beginners, scientists and engineers from universities, research organizations, and especially industry. In order to make it useful for a wide audience, both fundamentals and applications are discussed, together.

  4. Electrolyte Additives for Phosphoric Acid Fuel Cells

    DEFF Research Database (Denmark)

    Gang, Xiao; Hjuler, H.A.; Olsen, C.A.

    1993-01-01

    , as a fuel-cell performance with the modified electrolytes. Specific conductivity measurements of some of the modified phosphoric acid electrolytes are reported. At a given temperature, the conductivity of the C4F9SO3K-modified electrolyte decreases with an increasing amount of the additive; the conductivity...... of the remains at the same value as the conductivity of the pure phosphoric acid. At a given composition, the conductivity of any modified electrolyte increases with temperature. We conclude that the improved cell performance for modified electrolytes is not due to any increase in conductivity.......Electrochemical characteristics of a series of modified phosphoric acid electrolytes containing fluorinated car on compounds and silicone fluids as additives are presented. When used in phosphoric acid fuel cells, the modified electrolytes improve the performance due to the enhanced oxygen...

  5. The cation-deficient Ruddlesden-Popper oxysulfide Y2Ti2O5S2 as a layered sulfide: topotactic potassium intercalation to form KY2Ti2O5S2.

    Science.gov (United States)

    Rutt, Oliver J; Hill, Timothy L; Gál, Zoltán A; Hayward, Michael A; Clarke, Simon J

    2003-12-01

    Potassium intercalation into the cation-deficient n = 2 Ruddlesden-Popper oxysulfide Y(2)Ti(2)O(5)S(2) to form KY(2)Ti(2)O(5)S(2) has been carried out by reaction of the oxysulfide with potassium vapor in sealed metal tubes at 400 degrees C, potassium naphthalide in THF at 50 degrees C, or potassium in liquid ammonia at temperatures as low as -78 degrees C. Insertion of potassium is topotactic, and although a site 12-coordinate by oxide ions is vacant in the perovskite-type oxide slabs of the structure, potassium is too large to enter this site via the 4-coordinate window, and instead enters the rock-salt-type sulfide layers of the structure which necessitates a 30% increase in the lattice parameter c normal to the layers. In contrast with one of the sodium intercalates of Y(2)Ti(2)O(5)S(2) (beta-NaY(2)Ti(2)O(5)S(2)) in which sodium occupies a tetrahedral site in the sulfide layers, potassium favors an 8-coordinate site which necessitates a relative translation of adjacent oxide slabs. KY(2)Ti(2)O(5)S(2) is tetragonal: P4/mmm, a = 3.71563(4) A, c = 14.8682(2) A (at 298 K), Z = 1. Although the resistivity (3.4(1) x 10(3) Omega cm) is larger than would be expected for a metal, temperature independent paramagnetism dominates the magnetic susceptibility, and the material is electronically very similar to the analogous sodium intercalate beta-NaY(2)Ti(2)O(5)S(2) which features reduced-titanium-containing oxide layers of very similar geometry and electron count.

  6. Luminescence Studies on Lamp Phosphors

    Energy Technology Data Exchange (ETDEWEB)

    Nagpal, J.S.; Godbole, S.V.; Varadharajan, G.; Page, A.G

    1998-07-01

    Photoluminescence and thermoluminescence of cerium magnesium aluminate CeMgAl{sub 11}O{sub 17}(Eu,Tb) and calcium halophosphate Ca{sub 5}(PO{sub 4}){sub 3}(F,Cl):Mn,Sb, two fluorescent materials currently in use for the commercial production of lamps in India, have been studied for possible applications in radiation and ultraviolet dosimetry. Cerium magnesium aluminate is highly sensitive to the visible spectral region. It has a linear response to 254 nm UV radiation over a wide range. Its UV sensitivity is significantly higher as compared to that of other known phosphors; however, its UV response is rate-dependent and may not play a significant role in UV dosimetry. Photoluminescence of CeMg aluminate is characteristic of Eu{sup 2+} and Tb{sup 3+} dopants, whereas the thermoluminescence emission of the UV irradiated powder at room temperature is dominated by Eu{sup 2+} dopant. Calcium halophosphate is insensitive to room lights, has a linear gamma response over 0.2-10{sup 2} Gy and may be useful in the case of radiation accidents. (author)

  7. Luminescence Studies on Lamp Phosphors

    International Nuclear Information System (INIS)

    Nagpal, J.S.; Godbole, S.V.; Varadharajan, G.; Page, A.G.

    1998-01-01

    Photoluminescence and thermoluminescence of cerium magnesium aluminate CeMgAl 11 O 17 (Eu,Tb) and calcium halophosphate Ca 5 (PO 4 ) 3 (F,Cl):Mn,Sb, two fluorescent materials currently in use for the commercial production of lamps in India, have been studied for possible applications in radiation and ultraviolet dosimetry. Cerium magnesium aluminate is highly sensitive to the visible spectral region. It has a linear response to 254 nm UV radiation over a wide range. Its UV sensitivity is significantly higher as compared to that of other known phosphors; however, its UV response is rate-dependent and may not play a significant role in UV dosimetry. Photoluminescence of CeMg aluminate is characteristic of Eu 2+ and Tb 3+ dopants, whereas the thermoluminescence emission of the UV irradiated powder at room temperature is dominated by Eu 2+ dopant. Calcium halophosphate is insensitive to room lights, has a linear gamma response over 0.2-10 2 Gy and may be useful in the case of radiation accidents. (author)

  8. MULTI-PHOTON PHOSPHOR FEASIBILITY RESEARCH

    Energy Technology Data Exchange (ETDEWEB)

    R. Graham; W. Chow

    2003-05-01

    Development of multi-photon phosphor materials for discharge lamps represents a goal that would achieve up to a doubling of discharge (fluorescent) lamp efficacy. This report reviews the existing literature on multi-photon phosphors, identifies obstacles in developing such phosphors, and recommends directions for future research to address these obstacles. To critically examine issues involved in developing a multi-photon phosphor, the project brought together a team of experts from universities, national laboratories, and an industrial lamp manufacturer. Results and findings are organized into three categories: (1) Multi-Photon Systems and Processes, (2) Chemistry and Materials Issues, and (3) Concepts and Models. Multi-Photon Systems and Processes: This category focuses on how to use our current understanding of multi-photon phosphor systems to design new phosphor systems for application in fluorescent lamps. The quickest way to develop multi-photon lamp phosphors lies in finding sensitizer ions for Gd{sup 3+} and identifying activator ions to red shift the blue emission from Pr{sup 3+} due to the {sup 1}S{sub 0} {yields} {sup 1}I{sub 6} transition associated with the first cascading step. Success in either of these developments would lead to more efficient fluorescent lamps. Chemistry and Materials Issues: The most promising multi-photon phosphors are found in fluoride hosts. However, stability of fluorides in environments typically found in fluorescent lamps needs to be greatly improved. Experimental investigation of fluorides in actual lamp environments needs to be undertaken while working on oxide and oxyfluoride alternative systems for backup. Concepts and Models: Successful design of a multi-photon phosphor system based on cascading transitions of Gd{sup 3+} and Pr{sup 3+} depends critically on how the former can be sensitized and the latter can sensitize an activator ion. Methods to predict energy level diagrams and Judd-Ofelt parameters of multi

  9. Preparation of high purity yttrium single crystals by electrotransport

    International Nuclear Information System (INIS)

    Volkov, V.T.; Nikiforova, T.V.; Ionov, A.M.; Pustovit, A.N.; Sikharulidse, G.G.

    1981-01-01

    The possibility of obtaining yttrium crystals of high purity by the method of solid state electrotransport (SSE) was investigated in the present work. The behaviour of low contents of iron, aluminium, silicon, tantalum, copper, silver and vanadium as metallic impurities was studied using mass spectrometry. It is shown that all the impurities investigated, except copper, migrate to the anode. During electrotransfer a purification with respect to these impurities by a factor of 4 - 6 is obtained. It is proposed that the diffusion coefficients of the metallic impurities investigated are anomalously high and that the behaviour of the impurities during SSE in adapters necessitates further investigation. By using a three-stage process with intermediate removal of the anode end yttrium single crystals with a resistance ratio rho 293 /rhosub(4.2)=570 were produced. (Auth.)

  10. Acromegaly with sleep disturbances relieved by yttrium-90 pituitary implantation

    International Nuclear Information System (INIS)

    Rosenstock, J.; Doyle, F.H.; Joplin, G.F.; Jung, R.T.; Mashiter, K.

    1982-01-01

    A brief case history is presented of a patient, who, after yttrium-90 implantation, showed a complete clinical and hormonal remission of her acromegaly, maintaining normal pituitary function. The remarkable feature was the rapid disappearance of her attacks of somnolence within 96 hours of pituitary implantation, despite persistence of nocturnal snoring and well before any remodelling of soft tissues could have occurred. This response suggests that her daytime somnolence had a narcoleptic component. (author)

  11. Temperature dependence of sound velocity in yttrium ferrite

    International Nuclear Information System (INIS)

    L'vov, V.A.

    1979-01-01

    The effect of the phonon-magnon and phonon-phonon interoctions on the temperature dependence of the longitudinal sound velocity in yttrium ferrite is considered. It has been shown that at low temperatures four-particle phonon-magnon processes produce the basic contribution to renormalization of the sound velocity. At higher temperatures the temperature dependence of the sound velocity is mainly defined by phonon-phonon processes

  12. Acromegaly with sleep disturbances relieved by yttrium-90 pituitary implantation

    Energy Technology Data Exchange (ETDEWEB)

    Rosenstock, J.; Doyle, F.H.; Joplin, G.F.; Jung, R.T.; Mashiter, K. (Hammersmith Hospital, London (UK). Postgraduate Medical School)

    1982-03-01

    A brief case history is presented of a patient, who, after yttrium-90 implantation, showed a complete clinical and hormonal remission of her acromegaly, maintaining normal pituitary function. The remarkable feature was the rapid disappearance of her attacks of somnolence within 96 hours of pituitary implantation, despite persistence of nocturnal snoring and well before any remodelling of soft tissues could have occurred. This response suggests that her daytime somnolence had a narcoleptic component.

  13. Growth and scintillation properties of gadolinium and yttrium orthovanadate crystals

    International Nuclear Information System (INIS)

    Voloshina, O.V.; Baumer, V.N.; Bondar, V.G.; Kurtsev, D.A.; Gorbacheva, T.E.; Zenya, I.M.; Zhukov, A.V.; Sidletskiy, O.Ts.

    2012-01-01

    Aiming to explore the possibility of using the undoped rare-earth orthovanadates as scintillation materials, we developed the procedure for growth of gadolinium (GdVO 4 ) and yttrium (YVO 4 ) orthovanadate single crystals by Czochralski method, and determined the optimal conditions of their after-growth annealing. Optical, luminescent, and scintillation properties of YVO 4 and GdVO 4 were discussed versus known literature data. Scintillation characteristics of GdVO 4 were determined for the first time.

  14. Studies on Y{sub 2}SiO{sub 5}:Ce phosphors prepared by gel combustion using new fuels

    Energy Technology Data Exchange (ETDEWEB)

    Muresan, L.E., E-mail: laura_muresan2003@yahoo.com [“Raluca Ripan” Institute for Research in Chemistry, Babeş Bolyai University, Fântânele 30, 400294 Cluj-Napoca (Romania); Oprea, B.F.; Cadis, A.I.; Perhaita, I. [“Raluca Ripan” Institute for Research in Chemistry, Babeş Bolyai University, Fântânele 30, 400294 Cluj-Napoca (Romania); Ponta, O. [Faculty of Physics, Babeş Bolyai University, 400084 Cluj-Napoca (Romania)

    2014-12-05

    Highlights: • Y{sub 2}SiO{sub 5}:Ce was prepared by combustion using aspartic or glutamic acid as fuels. • Combustion process occurs differently depending on the fuels amount. • Single phase X2-Y{sub 2}SiO{sub 5} phosphors were obtained in fuel rich conditions. • PL measurements indicate that aspartic acid is a better fuel than glutamic. • Optimal preparative conditions were established for synthesis of Y{sub 2}SiO{sub 5}:Ce. - Abstract: Cerium activated yttrium silicate (Y{sub 2}SiO{sub 5}:Ce) phosphors were prepared by combustion, using yttrium–cerium nitrate as oxidizer, aspartic or glutamic acid as fuel and TEOS as source of silicon. In this study, aspartic and glutamic acid are used for the first time for the synthesis of Y{sub 2}SiO{sub 5}:Ce phosphors. The fuels molar amount was varied from 0.5 mol to 1.5 mol in order to reveal the thermal behavior of intermediary products (gels and ashes) same as the structural and luminescent characteristics of final products (phosphors). According to thermal analysis correlated with FTIR and XPS investigations, the combustion process occurs differently depending on the fuel amount; unreacted nitrate compounds have been identified in fuel lean conditions and carbonate based compounds along with organic residue in rich fuel conditions. The conversion to well crystallized silicates was revealed by changes of FTIR vibration bands and confirmed by XRD measurements. Based on luminescent spectra, aspartic acid is a better fuel than glutamic acid. A positive effect on the luminescence have been observed for samples fired in air due to complete remove of organic residue. The best luminescence was obtained for combustions with 0.75 mol aspartic acid and 1.25 mol glutamic respectively, fired at 1400 °C for 4 h in air atmosphere.

  15. Treatment of exhaust fluorescent lamps to recover yttrium: Experimental and process analyses

    International Nuclear Information System (INIS)

    De Michelis, Ida; Ferella, Francesco; Varelli, Ennio Fioravante; Veglio, Francesco

    2011-01-01

    Highlights: → Recovery of yttrium from spent fluorescent lamps by sulphuric acid leaching. → The use of sulphuric acid allows to reduce calcium dissolutions. → Main contaminant of fluorescent powder are Si, Pb, Ca and Ba. → Hydrated yttrium oxalate, recovered by selective precipitation, is quite pure (>90%). → We have studied the whole process for the treatment of dangerous waste (plant capability). - Abstract: The paper deals with recovery of yttrium from fluorescent powder coming from dismantling of spent fluorescent tubes. Metals are leached by using different acids (nitric, hydrochloric and sulphuric) and ammonia in different leaching tests. These tests show that ammonia is not suitable to recover yttrium, whereas HNO 3 produces toxic vapours. A full factorial design is carried out with HCl and H 2 SO 4 to evaluate the influence of operating factors. HCl and H 2 SO 4 leaching systems give similar results in terms of yttrium extraction yield, but the last one allows to reduce calcium extraction with subsequent advantage during recovery of yttrium compounds in the downstream. The greatest extraction of yttrium is obtained by 20% w/v S/L ratio, 4 N H 2 SO 4 concentration and 90 deg. C. Yttrium and calcium yields are nearly 85% and 5%, respectively. The analysis of variance shows that acid concentration alone and interaction between acid and pulp density have a significant positive effect on yttrium solubilization for both HCl and H 2 SO 4 medium. Two models are empirically developed to estimate yttrium and calcium concentration during leaching. Precipitation tests demonstrate that at least the stoichiometric amount of oxalic acid is necessary to recover yttrium efficiently and a pure yttrium oxalate n-hydrate can be produced (99% grade). The process is economically feasible if other components of the fluorescent lamps (glass, ferrous and non-ferrous scraps) are recovered after the equipment dismantling and valorized, besides the cost that is usually paid

  16. Phosphor blends for high-CRI fluorescent lamps

    Science.gov (United States)

    Setlur, Anant Achyut [Niskayuna, NY; Srivastava, Alok Mani [Niskayuna, NY; Comanzo, Holly Ann [Niskayuna, NY; Manivannan, Venkatesan [Clifton Park, NY; Beers, William Winder [Chesterland, OH; Toth, Katalin [Pomaz, HU; Balazs, Laszlo D [Budapest, HU

    2008-06-24

    A phosphor blend comprises at least two phosphors each selected from one of the groups of phosphors that absorb UV electromagnetic radiation and emit in a region of visible light. The phosphor blend can be applied to a discharge gas radiation source to produce light sources having high color rendering index. A phosphor blend is advantageously includes the phosphor (Tb,Y,LuLa,Gd).sub.x(Al,Ga).sub.yO.sub.12:Ce.sup.3+, wherein x is in the range from about 2.8 to and including 3 and y is in the range from about 4 to and including 5.

  17. Color stable manganese-doped phosphors

    Science.gov (United States)

    Lyons, Robert Joseph [Burnt Hills, NY; Setlur, Anant Achyut [Niskayuna, NY; Deshpande, Anirudha Rajendra [Twinsburg, OH; Grigorov, Ljudmil Slavchev [Sofia, BG

    2012-08-28

    A process for preparing color stable Mn.sup.+4 doped phosphors includes providing a phosphor of formula I; A.sub.x[MF.sub.y]:Mn.sup.+4 I and contacting the phosphor in particulate form with a saturated solution of a composition of formula II in aqueous hydrofluoric acid; A.sub.x[MF.sub.y]; II wherein A is Li, Na, K, Rb, Cs, NR.sub.4 or a combination thereof; M is Si, Ge, Sn, Ti, Zr, Al, Ga, In, Sc, Y, La, Nb, Ta, Bi, Gd, or a combination thereof; R is H, lower alkyl, or a combination thereof; x is the absolute value of the charge of the [MF.sub.y] ion; and y is 5, 6 or 7. In particular embodiments, M is Si, Ge, Sn, Ti, Zr, or a combination thereof. A lighting apparatus capable of emitting white light includes a semiconductor light source; and a phosphor composition radiationally coupled to the light source, and which includes a color stable Mn.sup.+4 doped phosphor.

  18. White light quality of phosphor converted light-emitting diodes: A phosphor materials perspective of view

    International Nuclear Information System (INIS)

    Sommer, Christian; Hartmann, Paul; Pachler, Peter; Hoschopf, Hans; Wenzl, Franz P.

    2012-01-01

    Highlights: ► We discuss the impact of the optical properties of a phosphor for colour temperature constancy in solid state lighting. ► Quantitative evaluation of permissible variations of the optical properties for batch-to-batch reproducibility. ► Quantitative evaluation of permissible variations of the optical properties upon temperature increase. ► Quantitative evaluation of permissible variations of the optical properties upon materials degradation. - Abstract: For a systematic approach to improve the white light quality of phosphor converted LEDs and to fulfil the demands for colour temperature reproducibility and constancy, it is imperative to understand how variations of the extinction coefficient and the quantum efficiency of the phosphor particles as well as variations of the excitation wavelength of the blue LED die affect the correlated colour temperature of the white LED source. Based on optical ray tracing of a phosphor converted white LED package we deduce permissible values for the variation of a given extinction coefficient and a given quantum efficiency of a phosphor material in order to maintain acceptable colour variations. These quantitative valuations of the required constancy of the optical properties of the phosphors will in particular provide some benchmarks for the synthesis of improved phosphor materials aiming at solid state lighting applications.

  19. High efficiency nitride based phosphores for white LEDs

    NARCIS (Netherlands)

    Li, Yuan Qiang; Hintzen, H.T.J.M.

    2008-01-01

    In this overview paper, novel rare-earth doped silicon nitride based phosphors for white LEDs applications have been demonstrated. The luminescence properties of orange-red-emitting phosphors (M2Si5N8:Eu2+) and green-to-yellow emitting phosphors (MSi2N2O2:Eu2+, M = Ca, Sr, Ba) are discussed in

  20. Thermoanalytical study of the formation mechanism of yttria from yttrium acetate

    International Nuclear Information System (INIS)

    Farjas, J.; Camps, J.; Roura, P.; Ricart, S.; Puig, T.; Obradors, X.

    2011-01-01

    Highlights: → Thermal decomposition of yttrium acetate: three endothermic stages. → Intermediates: yttrium hydroxide and carbonate. → Product: cubic yttria (the degree of transformation is at least 99%). → The decomposition does not depend on the oxygen partial pressure. - Abstract: The processes involved in the thermal decomposition of yttrium acetate tetrahydrate, Y(CH 3 COO) 3 .4H 2 O, in air and in an inert atmosphere have been analyzed by thermoanalytical techniques (thermogravimetry, differential thermal analysis and evolved gas analysis) and by the structural characterization (X-ray diffraction, infrared spectroscopy, elemental analysis and scanning electron microscopy) of intermediates and final products. Decomposition of yttrium acetate is an endothermic transformation that takes place in a temperature range between 350 and 900 o C. The evolution of the mass during the decomposition process is not affected by the presence of oxygen. The process is initiated by the rupture of the bond between the metallic cation and the acetate ligand. This initial step (350-450 o C) involves the formation of amorphous yttrium hydroxide and yttrium carbonate and is characterized by a fast mass loss rate. A sudden decrease of the mass loss rate indicates a change in the decomposition kinetics that continues with the decomposition of yttrium hydroxide and yttrium carbonate. The main effect of an oxygen atmosphere is an intense exothermic process due to the combustion of organic species in the gas phase.

  1. Preparation, characterization and thermal behaviour study of double selenates of lanthanides, yttrium and beryllium

    International Nuclear Information System (INIS)

    Ribeiro, C.A.

    1988-01-01

    The lanthanides (III) and yttrium (III) double selenates were studied using common analytical methods, atomic absorption, X-ray diffraction infra-red absorption, thermogravimetry and differential thermal analysis. These compounds were prepared from the mixture of lanthanides (III) and yttrium (III) selenates aqueous solution and basic beryllium selenates aqueous solution, obeying equimolar relation (1:1) to the cation

  2. Studies on effect of europium concentration on the photoemission of laser ablated Y2O3:Eu based nano-phosphors

    International Nuclear Information System (INIS)

    Nissamudeen, K.M.; Krishnan, Renju R.; Rajan, Geo; Gopchandran, K.G.

    2007-01-01

    Full text: Phosphors are essential materials in display applications. Oxide-based phosphors are likely to emerge as the potential choice for the FED red phosphor. Among those oxide-based phosphors, there has been significant research interest in the development of Y 2 O 3 :Eu thin films as one of the most promising oxide based red phosphor systems. Yttrium oxide mixed with europium exhibit strong UV and cathode-ray-excited luminescence that are useful in lamp and display applications. Dielectric Y 2 O 3 film has recently attracted much attention for its potential application as an electric insulation layer in electroluminescent devices and high-density dynamic random access memory gate dielectrics because of its high band gap (5.8 eV) and large dielectric constant (14 to 18). Another important application of Y 2 O 3 has been in luminescent displays as a host material for rare-earth ions, specifically europium, in order to get emission of red light. In the present study thin films were deposited under a vacuum of 10 -6 mbar on fused amorphous quartz substrates using a Q-switched Nd: YAG laser, 532 nm, pulse width 9 n sec, and repetition frequency of 10 Hz, with sintered Y 2 O 3 pellets having different europium concentration as target material. Attempts were made to understand the effect of europium concentration and annealing process on the photoemission properties of the films. A europium concentration of 8 wt% and an annealing temperature of 1173 K were found to be optimum conditions for maximum photoemission. The dependence of structure and morphology of the films on the photoemission intensity are described with XRD patterns and images obtained from AFM and SEM studies

  3. Phosphor investigation in the production of Syrian phosphoric acid using Nuclear Magnetic Resonance

    International Nuclear Information System (INIS)

    Al-Hassanieh, O.; Al-Hameish, M.

    2009-06-01

    Nuclear magnetic resonance spectroscopy (NMR) was applied in this work to the industrial process of extraction of uranium from phosphoric acid and to the process of the purification of the phosphoric acid for food proposes. The structural changes of used extraction materials and the organic content of the final product was studied. 13 C , 1 H and 32 P-spectra of all material during the process were recorded. The spectra of the three used extraction materials Bis(2-ethylhexyl Phosphoric Acid)) DEHPA, TriOctyl Phosphine Oxide (TOPO) (C 8 H 1 7) 3 P=O and TriButyl Phosphate (TBP) (C 4 H 9 O) 3 P=O show a partial degradation during the process. The final product ( Phosphoric acid for Food proposes) doesn't contain any organic solvents or extraction material. (author)

  4. Process for recovering a uranium containing concentrate and purified phosphoric acid from a wet process phosphoric acid containing uranium

    International Nuclear Information System (INIS)

    Weterings, C.A.M.; Janssen, J.A.

    1985-01-01

    A process is claimed for recovering from a wet process phosphoric acid which contains uranium, a uranium containing concentrate and a purified phosphoric acid. The wet process phosphoric acid is treated with a precipitant in the presence of a reducing agent and an aliphatic ketone

  5. Process for recovering a uranium containing concentrate and purified phosphoric acid from a wet process phosphoric acid containing uranium

    Energy Technology Data Exchange (ETDEWEB)

    Weterings, C.A.M.; Janssen, J.A.

    1985-04-30

    A process is claimed for recovering from a wet process phosphoric acid which contains uranium, a uranium containing concentrate and a purified phosphoric acid. The wet process phosphoric acid is treated with a precipitant in the presence of a reducing agent and an aliphatic ketone.

  6. Yttrium implantation and addition element effects on the oxidation behaviour of reference steels at 973 K

    Energy Technology Data Exchange (ETDEWEB)

    Caudron, E.; Buscail, H.; Cueff, R.; Issartel, C.; El Messki, S.; Perrier, S.; Riffard, F. [Lab. Vellave d' Elaboration et d' Etude des Materiaux, Univ. Blaise Pascal Clermont-Fd 2, Le Puy en Velay (France)

    2004-07-01

    Yttrium implantation effects on reference steels (extra low carbon and low manganese steel) were studied by rutherford backscattering spectrometry (RBS), reflection high energy electron diffraction (RHEED), X-ray diffraction (XRD) and glancing angle X-ray diffraction (GAXRD). Thermogravimetry and in situ X-ray diffraction at 700 C and P{sub O2}=0.04 Pa for 24h were used to determine the yttrium implantation and addition element effects on sample oxidation resistance at high temperatures. This study clearly shows that yttrium implantation and subsequent high temperature oxidation induced the formation of several yttrium mixed oxides which closely depend on the reference steel addition elements. Moreover, these yttrium mixed oxides seem to be responsible for the improved reference steel oxidation resistance at high temperatures. (orig.)

  7. Tattoo removal by Q-switched yttrium aluminium garnet laser

    DEFF Research Database (Denmark)

    Hutton Carlsen, K; Esmann, J; Serup, J

    2017-01-01

    BACKGROUND: Tattoo removal by Q-switched yttrium aluminium garnet (YAG) lasers is golden standard; however, clients' satisfaction with treatment is little known. OBJECTIVE: To determine clients' satisfaction with tattoo removal. METHODS: One hundred and fifty-four tattoo removal clients who had...... relative to colour of tattoo on a scale from 0 (no effect) to 10 (complete removal) scored a mean of blue 9.5, black 9.4, yellow 8.9, red 8.8 and green 6.5. Clients were dissatisfied with green pigment remnants, which could mimic bruising. One hundred and twenty-nine clients (84%) experienced moderate...

  8. Phase composition of yttrium-doped zirconia ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Hennig, Christoph; Scheinost, Andreas C. [Helmholtz-Zentrum Dresden-Rossendorf e.V., Dresden (Germany). Molecular Structures; Weiss, Stephan [Helmholtz-Zentrum Dresden-Rossendorf e.V., Dresden (Germany). Surface Processes; Ikeda-Ohno, Atsushi [Helmholtz-Zentrum Dresden-Rossendorf e.V., Dresden (Germany). Chemistry of the F-Elements; Gumeniuk, R. [Technische Univ. Bergakademie Freiberg (Germany). Inst. fuer Experimentelle Physik

    2017-06-01

    Ceramic material might be an alternative to borosilicate glass for the immobilization of nuclear waste. The crystallinity of ceramic material increases the corrosion resistance over several magnitudes in relation to amorphous glasses. The stability of such ceramics depend on several parameters, among them the crystal phase composition. A reliable quantitative phase analysis is necessary to correlate the macroscopic material properties with structure parameters. We performed a feasibility study based on yttrium-doped zirconia ceramics as analogue for trivalent actinides to ascertain that the nanosized crystal phases in zirconia ceramics can be reliably determined.

  9. Structure-terahertz property relationship in yttrium aluminum garnet ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Steere, D.W.; Clark, B.M.; Sundaram, S.K. [Alfred University, Terahertz and Millimeter Waves Laboratory (T-Lab), Kazuo Inamori School of Engineering, The New York State College of Ceramics, Alfred, NY (United States); Gaume, R. [Townes Laser Institute and the NanoScience Technology Center, CREOL, The College of Optics and Photonics, Orlando, FL (United States)

    2017-08-15

    Terahertz (THz) transmission measurements on chemically variant yttrium aluminum garnet (YAG) ceramics are described. Chemical compositions and processing parameters were varied to determine the effect of stoichiometry, density, and pore volume distribution on the optical and dielectric properties in the THz frequency regime. Density has the largest effect on properties out of the parameters that were investigated. In addition, a linear correlation between cubic root of real permittivity at 1 THz and average density of these samples is observed. Our results show promise for design and fabrication of advanced optical materials and devices with desired THz properties via controlling density and porosity of the materials. (orig.)

  10. Study on the coextraction of scandium-yttrium-lumogallion complex

    International Nuclear Information System (INIS)

    Okada, T.; Shimoishi, Y.; Miyata, H.; Toei, K.

    1977-01-01

    The coextraction of scandium-yttrium-lumogallion [LMG;4-chloro-6-(2,4-dihydroxyphenylazo)-1-hydroxybenzene-2-sulfonic acid] into diethyl ether has been studied. The acid dissociation constants of LMG, pKsub(a2) and pKsub(a3), were estimated to be 6.24 and 8.05 respectively. The composition of the complex extracted was determined by using the radioisotopes 46 Sc and 90 Y and by spectrophotometry of LMG and the ratio of the components was Sc:Y:LMG = 1:1:3. The coextraction scheme was discussed briefly. (author)

  11. Optical properties of Dy3+ doped yttrium aluminium borate

    International Nuclear Information System (INIS)

    Vazquez, R MartInez; Osellame, R; Marangoni, M; Ramponi, R; Dieguez, E; Ferrari, M; Mattarelli, M

    2004-01-01

    A Dy 3+ doped yttrium aluminium borate (Dy:YAB) crystal has been optically characterized. The refractive indices at seven different wavelengths, ranging from the visible to the near infrared (IR), have been measured and the Sellmeier curves have been calculated. The polarized optical absorption spectra have been obtained at room temperature, and the Judd-Ofelt parameters have been calculated. The lifetime of the upper laser level 4 F 9/2 has been estimated and compared with the experimental value. Evidence of high luminescence quantum efficiency of the 4 F 9/2 state in YAB is provided by measured lifetimes

  12. Kinetic properties of solid yttrium at high temperatures

    International Nuclear Information System (INIS)

    Ivliev, A.D.

    1993-01-01

    Analysis of results of experimental investigation into temperature-diffusivity, specific electroresistance and heat conductivity of yttrium is carried out. Peculiarities of variation of its kinetic characteristics under high temperatures are shown to result from two-band character of energy spectrum of collectivized electrons. In particular, growth of heat conductivity results from reduction of density of heavy electron states under heating. The suggested model describes kinetic characteristics of lutetium, as well. Usage of this model for the rest heavy rare-earth metals enables to make conclusion about reduction of magnetic scattering effcieincy in the rare-earth metals in proportion to approximation to melting temperature

  13. Knee arthroscopy after yttrium or osmic acid injection

    International Nuclear Information System (INIS)

    Guaydier-Souquieres, C.; Beguin, J.; Ollivier, D.; Loyau, G.

    1989-01-01

    This study presents the macroscopic and histologic results of 35 knee arthroscopies performed on patients with rheumatoid arthritis, some months after an yttrium or osmic acid intraarticular injection. The procedure was most often performed after a failure of the injection or a relapse of synovitis. Arthroscopy provides an understanding of the cause of synoviorthesis failure--insufficient action of the product on the synovitis or its poor diffusion, fibri-nonecrotic deposits, or cartilaginous lesions--and may be used both diagnostically and therapeutically

  14. Spectrographic determination of strontium in yttrium-90 solutions

    International Nuclear Information System (INIS)

    Roca, M.; Capdevila, C.

    1970-01-01

    The copper spark method has been used for determining strontium in the concentration range 1-100 g/ml in yttrium-90 solutions containing 0,5 % or thereabouts of ammonium citrate. The influence of the citric acid as well as the ammonium citrate with regard to 2N HCL solutions has been studied: the citric acid enhances the line intensities of strontium. The employment of either barium or lanthanum as reference element compensates for this enhancement. Because of the increase in sensitivity mentioned above, the study of influence of the citric acid has been extended and several impurities usually determined in radioisotope solutions have been considered. (Author) 4 refs

  15. Scattering of polarized protons by yttrium, iron and nickel nuclei

    International Nuclear Information System (INIS)

    Melssen, J.P.M.G.

    1978-01-01

    Results are presented of scattering experiments performed on yttrium and some iron and nickel isotopes with polarized proton beams at energies around 20 MeV. The angular distributions of the differential cross sections and analyzing powers have been measured and comparison of these with predictions from theoretical models has led to information about excited nuclear states like spin, parity and details of the wavefunctions. The DWBA has been mostly used to describe the reaction at the bombarding energies and for the target nuclei investigated. (C.F.)

  16. Childhood acromegaly successfully treated with interstitial irradiation using Yttrium-90

    International Nuclear Information System (INIS)

    Rosenstock, J.; Doyle, F.H.; Mashiter, K.; Joplin, G.F.

    1982-01-01

    A child with a growth hormone producing tumour presented at the age of 4 1/2 years. The onset of the disease was at 18 months of age. Treatment was given with three doses of interstitial irradiation using yttrium-90 implants. There were no local complications from the procedures. Now, 11 years after diagnosis, she is asymptomatic, of normal appearance, and her height and the size of the pituitary fossa are normal. Growth hormone levels are almost normal, thyroid function is intact, and she is maintained on prednisone and sex hormones. (Authors)

  17. Childhood acromegaly successfully treated with interstitial irradiation using Yttrium-90

    Energy Technology Data Exchange (ETDEWEB)

    Rosenstock, J.; Doyle, F.H.; Mashiter, K.; Joplin, G.F. (Royal Postgraduate Medical School, Hammersmith Hospital, London (UK). Dept. of Medicine and Radiology); Hall, R. (Royal Victoria Infirmary, Newcastle upon Tyne (UK))

    1982-01-01

    A child with a growth hormone producing tumour presented at the age of 4 1/2 years. The onset of the disease was at 18 months of age. Treatment was given with three doses of interstitial irradiation using Yttrium-90 implants. There were no local complications from the procedures. Now, 11 years after diagnosis, she is asymptomatic, of normal appearance, and her height and the size of the pituitary fossa are normal. Growth hormone levels are almost normal, thyroid function is intact, and she is maintained on prednisone and sex hormones.

  18. Photometric determination of yttrium in zirconium-containing materials

    International Nuclear Information System (INIS)

    Barbina, T.M.; Polezhaev, Yu.M.

    1984-01-01

    Comparative evaluation of the effect of different ways of eliminating the zirconium interfering effect on the results of yttrium photometric determination with arsenazo 2 in artificial mixtures of Y 2 O 3 and ZrO 2 , containing 5 and 10 mol.% Y 2 O 3 , has been carried out. The effect of Zr is eliminated by means of its precipitation by ammonium solution in the form of hydroxide and using camouflaging with 25% sulfosalicylic acid. Both ways do not provide a correct enough result. The use of non-reagent thermohydrolytic Zr precipitation during the analysis of zirconium-containing materials permits to obtain correct and well-reproducible results

  19. Thiocarbomide coordination compounds of yttrium subgroup rare earth chlorides

    International Nuclear Information System (INIS)

    Sakharova, Yu.G.; Perov, V.N.; Loginov, V.I.

    1978-01-01

    Thiocarbamide coordination compounds of chlorides of elements of the yttrium subgroup 4MeCl 3 x5Cs(NH 2 ) 2 x2OH 2 O (where Me stands for Tb, Dy, Ho, Er, Tm, Yb, Lu, Y) were produced for the first time. The compounds obtained are stable in air, have definite melting points, are highly soluble in methyl and ethyl alcohols, and are unstable in water. They recrystallize from ethyl alcohol without changing their chemical composition. The identity of these compounds was confirmed by X-ray analysis

  20. Pretreatment of phosphoric acid for uranium recovery by the wet phosphoric acid process

    International Nuclear Information System (INIS)

    Chern, S.L.P.; Chen, Y.C.L.; Chang, S.S.H.; Kuo, T.S.; Ting, G.C.M.

    1980-01-01

    The proposal deals with reprocessing of phosphoric acid arising from uranium separation according to the wet phosphoric acid process and being intended for recycling. In detail, the sludge will be removed by means of an inclined separating device containing corrugated plates, then the organic impurities are washed out with kerosene in suitable facilities, and the crude phase remaining in the settling tank will be separated from the kerosene in a separating centrifuge. The method has only got low cost of installation. (UWI) [de

  1. A survey of phosphors novel for thermography

    Energy Technology Data Exchange (ETDEWEB)

    Bruebach, J., E-mail: bruebach@ekt.tu-darmstadt.d [Fachgebiet Reaktive Stroemungen und Messtechnik, Center of Smart Interfaces Technische Universitaet Darmstadt, Petersenstrasse 32, 64287 Darmstadt (Germany); Kissel, T. [Fachgebiet Reaktive Stroemungen und Messtechnik, Center of Smart Interfaces Technische Universitaet Darmstadt, Petersenstrasse 32, 64287 Darmstadt (Germany); Frotscher, M. [Eduard-Zintl-Institut fuer Anorganische und Physikalische Chemie, Technische Universitaet Darmstadt, Petersenstrasse 18, 64287 Darmstadt (Germany); Euler, M. [Fachgebiet Reaktive Stroemungen und Messtechnik, Center of Smart Interfaces Technische Universitaet Darmstadt, Petersenstrasse 32, 64287 Darmstadt (Germany); Albert, B. [Eduard-Zintl-Institut fuer Anorganische und Physikalische Chemie, Technische Universitaet Darmstadt, Petersenstrasse 18, 64287 Darmstadt (Germany); Dreizler, A. [Fachgebiet Reaktive Stroemungen und Messtechnik, Center of Smart Interfaces Technische Universitaet Darmstadt, Petersenstrasse 32, 64287 Darmstadt (Germany)

    2011-04-15

    With regard to phosphor thermometry, seven luminescent ceramic materials were synthesised and characterised, namely CaMoO{sub 4}:Eu{sup 3+}, CaTiO{sub 3}:Pr{sup 3+}, LaPO{sub 4}:Eu{sup 3+}, LaVO{sub 4}:Eu{sup 3+}, LiAl{sub 5}O{sub 8}:Fe{sup 3+}, TiMg{sub 2}O{sub 4}:Mn{sup 4+} and ZnGa{sub 2}O{sub 4}:Mn{sup 2+}. In this context, emission spectra and temperature lifetime characteristics are presented. Thus, a survey of phosphors novel for thermography is given in order to encourage further studies and more detailed characterisations of the respective materials. - Research Highlights: Seven phosphor materials novel for thermometry were synthesised. These materials were characterised diffractometrically as well as concerning their emission spectra and lifetime temperature characteristics. The number of phosphor materials characterised for thermometry purposes was extended by seven materials.

  2. Phosphate phosphors for solid-state lighting

    Energy Technology Data Exchange (ETDEWEB)

    Shinde, Kartik N. [N.S. Science and Arts College, Bhadrawati (India). Dept. of Physics; Swart, H.C. [University of the Orange Free State, Bloemfontein (South Africa). Dept. of Physics; Dhoble, S.J. [R.T.M. Nagpur Univ. (India). Dept. of Physics; Park, Kyeongsoon [Sejong Univ., Seoul (Korea, Republic of). Faculty of Nanotechnology and Advanced Materials Engineering

    2012-07-01

    Essential information for students in researchers working towards new and more efficient solid-state lighting. Comprehensive survey based on the authors' long experience. Useful both for teaching and reference. The idea for this book arose out of the realization that, although excellent surveys and a phosphor handbook are available, there is no single source covering the area of phosphate based phosphors especially for lamp industry. Moreover, as this field gets only limited attention in most general books on luminescence, there is a clear need for a book in which attention is specifically directed toward this rapidly growing field of solid state lighting and its many applications. This book is aimed at providing a sound introduction to the synthesis and optical characterization of phosphate phosphor for undergraduate and graduate students as well as teachers and researchers. The book provides guidance through the multidisciplinary field of solid state lighting specially phosphate phosphors for beginners, scientists and engineers from universities, research organizations, and especially industry. In order to make it useful for a wide audience, both fundamentals and applications are discussed, together.

  3. doped LiMgPO4 phosphor

    Indian Academy of Sciences (India)

    attention because of their remarkable luminescence proper- ties and .... Figure 1. (a) X-ray diffraction patterns of LiMgPO4:Tb3+ phosphor and (b) standard data. ICDD file. .... ground signal which affects the signal to noise ratio [17]. MDD was ...

  4. Intravascular imaging with a storage phosphor detector

    Energy Technology Data Exchange (ETDEWEB)

    Shikhaliev, Polad M; Petrek, Peter; Matthews, Kenneth L II; Fritz, Shannon G [Department of Physics and Astronomy, Louisiana State University, Baton Rouge, LA (United States); Bujenovic, L Steven [PET Imaging Center, Our Lady of the Lake Medical Center, Baton Rouge, LA (United States); Xu Tong, E-mail: pshikhal@lsu.ed [Department of Physics, Carleton University, Ottawa (Canada)

    2010-05-21

    The aim of this study is to develop and test an intravascular positron imaging system based on a storage phosphor detector for imaging and detecting vulnerable plaques of human coronary arteries. The radiotracer F18-FDG accumulates in vulnerable plaques with inflammation of the overlying cap. The vulnerable plaques can, therefore, be imaged by recording positrons emitted from F18-FDG with a detector inserted into the artery. A prototype intravascular detector was constructed based on storage phosphor. The detector uses a flexible storage phosphor tube with 55 mm length, 2 mm diameter and 0.28 mm wall thickness. The intravascular detector is guided into the vessel using x-ray fluoroscopy and the accumulated x-ray signal must be erased prior to positron imaging. For this purpose, a light diffuser, 0.9 mm in diameter and 55 mm in length, was inserted into the detector tube. The light diffuser was connected to a laser source through a 2 m long optical fiber. The diffuser redirected the 0.38 W laser light to the inner surface of the phosphor detector to erase it. A heart phantom with 300 cm{sup 3} volume and three coronary arteries with 3.2 mm diameter and with several plaques was constructed. FDG solution with 0.5 {mu}Ci cm{sup -3} activity concentration was filled in the heart and coronary arteries. The detector was inserted in a coronary artery and the signal from the plaques and surrounding background activity was recorded for 2 min. Then the phosphor detector was extracted and read out using a storage phosphor reader. The light diffuser erased the signal resulting from fluoroscopic exposure to level below that encountered during positron imaging. Vulnerable plaques with area activities higher than 1.2 nCi mm{sup -2} were visualized by the detector. This activity is a factor of 10-20 lower than that expected in human vulnerable plaques. The detector was able to image the internal surface of the coronary vessels with 50 mm length and 360{sup 0} circumference. Spatial

  5. High Extraction Phosphors for Solid State Lighting

    Energy Technology Data Exchange (ETDEWEB)

    Summers, Chris [Phosphortech Corporation, Kennesaw, GA (United States); Menkara, Hisham [Phosphortech Corporation, Kennesaw, GA (United States); Wagner, Brent [Phosphortech Corporation, Kennesaw, GA (United States)

    2011-09-01

    We have developed high-index, high efficiency bulk luminescent materials and novel nano-sized phosphors for improved solid-state white LED lamps. These advances can potentially contribute to reducing the loss in luminous efficiencies due to scattering, re-absorption, and thermal quenching. The bulk and nanostructured luminescent materials investigated are index matched to GaN and have broad and size-tunable absorption bands, size and impurity tuned emission bands, size-driven elimination of scattering effects, and a separation between absorption and emission bands. These innovations were accomplished through the use of novel synthesis techniques suitable for high volume production for LED lamp applications. The program produced a full-color set of high quantum yield phosphors with high chemical stability. In the bulk phosphor study, the ZnSeS:Cu,Ag phosphor was optimized to achieve >91% efficiency using erbium (Er) and other activators as sensitizers. Detailed analysis of temperature quenching effects on a large number of ZnSeS:Cu,Ag,X and strontium- and calcium-thiogallate phosphors lead to a breakthrough in the understanding of the anti-quenching behavior and a physical bandgap model was developed of this phenomena. In a follow up to this study, optimized phosphor blends for high efficiency and color performance were developed and demonstrated a 2-component phosphor system with good white chromaticity, color temperature, and high color rendering. By extending the protocols of quantum dot synthesis, large nanocrystals, greater than 20 nm in diameter were synthesized and exhibited bulk-like behavior and blue light absorption. The optimization of ZnSe:Mn nanophosphors achieved ~85% QE The limitations of core-shell nanocrystal systems were addressed by investigating alternative deltadoped structures. To address the manufacturability of these systems, a one-pot manufacturing protocol was developed for ZnSe:Mn nanophosphors. To enhance the stability of these material

  6. Recuperation of uranium from phosphoric acid

    International Nuclear Information System (INIS)

    Cordero, G.; Jodra, L.G.; Otero, J.L.; Josa, J.M.

    1977-01-01

    The Spanish capacity for phosphoric acid production is 500.000 t P 2 O 5 /yr. This acid has an average concentration of 365 g U 3 O 8 / t P 2 O 5 . Therefore about 180 t U 3 O 8 /yr are dissolved. In 1969, the Junta de Energia Nuclear (JEN) developed, in bench scale, a solvent extraction process to recover the uranium from the phosphoric acid. The solvent used was a synergistic mixture of D2EHPA and TOPO. The results were very promising with good recovery and very high quality for the uranium concentrate. Later, the J.E.N. continued the studies in a pilot plant scale. For this purpose, was built an experimental facility in Huelva; it can treat about 7 cu. m/day of brown acid. Fosforico Espanol, S.A. (FESA) collaborated in the studies and agreed to setting up these installations in their factory. They also provided fresh phosphoric acid for the tests. In this pilot plant we studied the following stages: a) Clarification and conditioning of the phosphoric acid; b) Uranium extraction followed by stripping in a reducing medium; c) Purification by extraction and washing; d) Obtention of the concentrate by stripping with ammonia and CO 2 gas, followed by crystallization of the ammonium uranyl tricarbonate (AUT); and e) Calcination of the concentrate to decompose the AUT to uranium oxides. The results confirmed the laboratory test data. Recuperation levels were between 85 and 90%. The AUT calcined at 550 0 C. gave a product with 96-98% U 3 O 8 . In view of the pilot plant results we have prepared a black book for an industrial plant to treat about 3700 cu. m/day of phosphoric acid. At the present time the financial aspects of this installation are being studied [es

  7. Synthesis and Luminescence Characteristics of Cr3+ doped Y3Al5O12 Phosphors

    Energy Technology Data Exchange (ETDEWEB)

    Smith, Brenda A. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Dabestani, Reza T. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Lewis, Linda A. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Thompson, Cyril V. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Collins, Case T. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Aytug, Tolga [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2015-10-01

    Luminescence performance of yttrium aluminum garnet (Y3Al5O12) phosphors as a function of Cr3+ concentration has been investigated via two different wet-chemical synthesis techniques, direct- (DP) and hydrothermal-precipitation (HP). Using either of these methods, the red-emitting phosphor [Y3Al5-xCrxO12 (YAG: Cr3+)] showed similar photoluminescence (PL) intensities once the dopant concentration was optimized. Specifically, the YAG: Cr3+ PL emission intensity reached a maximum at Cr3+ concentrations of x = 0.02 (0.4 at.%) and x = 0.13 (2.6 at.%) for DP and HP processed samples, respectively. The results indicated the strong influence of the processing method on the optimized YAG: Cr3+ performance, where a more effective energy transfer rate between a pair of Cr3+ activators at low concentration levels was observed by using the DP synthesis technique. Development of a highly efficient phosphor, using a facile synthesis approach, could significantly benefit consumer and industrial applications by improving the operational efficiency of a wide range of practical devices.

  8. Effect of Al/Ga substitution on the structural and luminescence properties of Y3(Al1-xGax)5O12: Ce3+ phosphors

    Science.gov (United States)

    Fu, Sheng; Tan, Jin; Bai, Xin; Yang, Shanjie; You, Lei; Du, Zhengkang

    2018-01-01

    As candidates for display and lighting materials, a series of gallium-substituted cerium-doped yttrium aluminum garnet (Y3(GaxAl1-x)5O12: Ce3+) phosphors were synthesized by high temperature solid-state reaction. The phases, morphology, luminescence spectra and thermal stability of the phosphors were investigated. The volatilization of Ga2O3 induces the constituents out of stoichiometric ratio and different impurities in the system. The excitation and emission spectra occur red shift (339 nm - 351 nm) and blue shift (465 nm - 437 nm), and blue shift (541 nm - 517 nm), respectively. The spectra have no further blue shift and the luminescence intensity decrease with x over 0.4. Combining crystal structure with PL spectrum, the distortion of dodecahedron and crystal field splitting of 5d level of Ce3+ are influenced by Ga3+ in octahedral coordination polyhedron rather than tetrahedron. The crystalline perfection and Ga3+ occupying the tetrahedron induce less garnet phase formation, more impurities and the 5d level located in the conductive bands, thus accounting for the x = 0.4 turning points of the PL and PLE intensity. Based on the thermal quenching and CIE, the Y3(GaxAl1-x)5O12: Ce3+0.06 phosphors have great potential for use on the w-LED.

  9. Hydrogen sensor based on palladium-yttrium alloy nanosheet

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Boyi [Queensland Micro- and Nanotechnology Centre, Griffith University, Nathan, QLD 4111 (Australia); Zhu, Yong, E-mail: y.zhu@griffith.edu.au [Queensland Micro- and Nanotechnology Centre, Griffith University, Nathan, QLD 4111 (Australia); Chen, Youping; Song, Han; Huang, Pengcheng [School of Mechanical Science and Engineering, Huazhong University of Science and Technology, Wuhan, 430074 (China); Dao, Dzung Viet [Queensland Micro- and Nanotechnology Centre, Griffith University, Nathan, QLD 4111 (Australia)

    2017-06-15

    This paper presents a hydrogen sensor based on palladium-yttrium (Pd-Y) alloy nanosheet. Zigzag-shaped Pd-Y nanosheet with a thickness of 19.3 nm was deposited on a quartz substrate by using an ultrahigh-vacuum magnetron sputtering system and shadow mask. The atomic ratio of palladium to yttrium in the nanosheet was 0.92/0.08. The fabrication process was simple and low-cost, and the sensor can be mass-produced. The experimental results show the sensor has a superior sensitivity, reversibility, and reproducibility. The resistive-based hydrogen detection mechanism in this research is much simpler and more compact compared to the optical-based detection method. - Highlights: • Pd-Y sensing element was fabricated using a magnetron sputtering system and shadow mask. • The Pd-Y compound consisted of 92% Pd and 8% Y. • The fabrication process was simple, low-cost, and mass-production compatible. • The sensor showed superior sensitivity, reversibility, and reproducibility to hydrogen gas. • The device is more compact than the optical-based counterpart.

  10. Yttrium ion implantation on the surface properties of magnesium

    International Nuclear Information System (INIS)

    Wang, X.M.; Zeng, X.Q.; Wu, G.S.; Yao, S.S.

    2006-01-01

    Owing to their excellent physical and mechanical properties, magnesium and its alloys are receiving more attention. However, their application has been limited to the high reactivity and the poor corrosion resistance. The aim of the study was to investigate the beneficial effects of ion-implanted yttrium using a MEVVA ion implanter on the surface properties of pure magnesium. Isothermal oxidation tests in pure O 2 at 673 and 773 K up to 90 min indicated that the oxidation resistance of magnesium had been significantly improved. Surface morphology of the oxide scale was analyzed using scanning electron microscope (SEM). Auger electron spectroscopy (AES) and X-ray diffraction (XRD) analyses indicated that the implanted layer was mainly composed of MgO and Y 2 O 3 , and the implanted layer with a duplex structure could decrease the inward diffusion of oxygen and reduce the outward diffusion of Mg 2+ , which led to improving the oxidation resistance of magnesium. Potentiodynamic polarization curves were used to evaluate the corrosion resistance of the implanted magnesium. The results show yttrium implantation could enhance the corrosion resistance of implanted magnesium compared with that of pure magnesium

  11. Hydrogen sensor based on palladium-yttrium alloy nanosheet

    International Nuclear Information System (INIS)

    Wang, Boyi; Zhu, Yong; Chen, Youping; Song, Han; Huang, Pengcheng; Dao, Dzung Viet

    2017-01-01

    This paper presents a hydrogen sensor based on palladium-yttrium (Pd-Y) alloy nanosheet. Zigzag-shaped Pd-Y nanosheet with a thickness of 19.3 nm was deposited on a quartz substrate by using an ultrahigh-vacuum magnetron sputtering system and shadow mask. The atomic ratio of palladium to yttrium in the nanosheet was 0.92/0.08. The fabrication process was simple and low-cost, and the sensor can be mass-produced. The experimental results show the sensor has a superior sensitivity, reversibility, and reproducibility. The resistive-based hydrogen detection mechanism in this research is much simpler and more compact compared to the optical-based detection method. - Highlights: • Pd-Y sensing element was fabricated using a magnetron sputtering system and shadow mask. • The Pd-Y compound consisted of 92% Pd and 8% Y. • The fabrication process was simple, low-cost, and mass-production compatible. • The sensor showed superior sensitivity, reversibility, and reproducibility to hydrogen gas. • The device is more compact than the optical-based counterpart.

  12. Effects of hepatic arterial yttrium 90 glass microspheres in dogs.

    Science.gov (United States)

    Wollner, I; Knutsen, C; Smith, P; Prieskorn, D; Chrisp, C; Andrews, J; Juni, J; Warber, S; Klevering, J; Crudup, J

    1988-04-01

    A 22-micron glass microsphere called TheraSphere (Theragenics Corp., Atlanta, GA) has been developed in which yttrium 89 oxide is incorporated into the glass matrix and is activated by neutron bombardment to form the beta-emitting isotope yttrium 90 (Y 90) before using the spheres as radiotherapeutic vehicles. The injection of up to 12 times (on a liver weight basis) the anticipated human dose of nonradioactive TheraSphere into the hepatic arteries of dogs was well tolerated and produced clinically silent alterations within centrolobular areas. The hepatic arterial (HA) injection of radioactive TheraSphere also produced portal changes similar to those observed in humans after external beam therapy. While the extent of damage increased with the delivered dose, radiation exposures in excess of 30,000 cGy did not cause total hepatic necrosis and were compatible with survival. No microspheres distributed to the bone marrow and absolutely no myelosuppression was encountered in any animal. Proposed hepatic exposures to humans of 5000 to 10,000 cGy by means of these microspheres, therefore, would appear to be feasible and tolerable. Radiotherapeutic microsphere administration preceded by regional infusion of a radiosensitizing agent and/or immediately following the redistribution of blood flow toward intrahepatic tumor by vasoactive agents can potentially yield a synergistic, highly selective attack on tumors confined to the liver.

  13. MCrAlY bond coat with enhanced Yttrium layer

    Science.gov (United States)

    Jablonski, Paul D; Hawk, Jeffrey A

    2015-04-21

    One or more embodiments relates to an MCrAlY bond coat comprising an MCrAlY layer in contact with a Y--Al.sub.2O.sub.3 layer. The MCrAlY layer is comprised of a .gamma.-M solid solution, a .beta.-MAl intermetallic phase, and Y-type intermetallics. The Y--Al.sub.2O.sub.3 layer is comprised of Yttrium atoms coordinated with oxygen atoms comprising the Al.sub.2O.sub.3 lattice. Both the MCrAlY layer and the Y--Al.sub.2O.sub.3 layer have a substantial absence of Y--Al oxides, providing advantage in the maintainability of the Yttrium reservoir within the MCrAlY bulk. The MCrAlY bond coat may be fabricated through application of a Y.sub.2O.sub.3 paste to an MCrAlY material, followed by heating in a non-oxidizing environment.

  14. Effect of vanadium and yttrium doping on BSCCO superconductors

    International Nuclear Information System (INIS)

    Mohamed, S.B.; Halim, S.A.; Azhan, H.; Sidek, H.A.A; Tee, T.W.; Hassan, Z.A.

    1999-01-01

    The effect of vanadium and yttrium doping on the superconductivity is investigated. The doping was done on the calcium site ranging from x=0.00-0.10. The temperature dependence of electrical resistance and AC susceptibility measurements were made on these samples. The zero resistance for vanadium doped samples varied from 107 K (x = 0.00) to 68.5K (x = 0.10), whereas for yttrium doped samples it varied from 107 K (x = 0.00) to 54K (x 0.10). The volume fraction of the 2223 phase for both dopalit decreases witli increasing doping concentration. The nature of the temperature derivative of the resistance curves indicates the presence of a superconducting transition between grains coupled by weak links. The AC susceptibility data show enrichment of the volume fraction of the low Tc phase at higher compositions. The presence of low Tc phase (∼70 K) is visible in the susceptibility data. X-ray diffraction confirms the presence of mixed phases in the samples. (author)

  15. Blue- and red-emitting phosphor nanoparticles embedded in a porous matrix

    Energy Technology Data Exchange (ETDEWEB)

    Taghavinia, N. [Physics Department, Sharif University of Technology, Tehran P.O. Box 11365-9161, Tehran 14588 (Iran, Islamic Republic of) and Institute for Nanoscience and Nanotechnology, Sharif University of Technology, Tehran 14588 (Iran, Islamic Republic of)]. E-mail: taghavinia@sharif.edu; Lerondel, G. [Laboratoire de Nanotechnologie et d' Instrumentation Optique, Univ. de Technologie de Troyes, 10010 Troyes cedex (France); Makino, H. [Institute for Materials Research, Tohoku University, Sendai 980-8577 (Japan); Yao, T. [Institute for Materials Research, Tohoku University, Sendai 980-8577 (Japan)

    2006-05-01

    Eu{sup 3+}- and Ce{sup 3+}-doped yttrium silicate, as well as Eu{sup 2+}-doped zinc silicate nanoparticles, were grown in a porous SiO{sub 2} matrix using an impregnation method. For Y{sub 2}Si{sub 2}O{sub 7}:Eu{sup 3+}, particles of about 50 nm size were obtained that exhibited several photoluminescence (PL) peaks in red. Different peaks showed slightly different decay times; however, their excitation mechanism was found the same. Increasing the Eu concentration increased the PL intensity while reducing the decay time. Y{sub 2}Si{sub 2}O{sub 7}:Ce{sup 3+} nanoparticles in the porous matrix showed bright blue emission, consisting of two peaks at 358 nm and 378 nm. Re-impregnation process was found effective in changing the relative intensity of the two peaks. Zn{sub 2}SiO{sub 4}:Eu{sup 2+} nanoparticles in porous glass consisted of amorphous particles of about 20 nm size inside the porous matrix. The luminescence was a broad peak centered at 418 nm. These phosphor systems, together with our previously reported Zn{sub 2}SiO{sub 4}:Mn{sup 2+} in porous SiO{sub 2} structure, comprise a red-green-blue system that can be used in display applications.

  16. High luminous flux from single crystal phosphor-converted laser-based white lighting system

    KAUST Repository

    Cantore, Michael

    2015-12-14

    The efficiency droop of light emitting diodes (LEDs) with increasing current density limits the amount of light emitted per wafer area. Since low current densities are required for high efficiency operation, many LED die are needed for high power white light illumination systems. In contrast, the carrier density of laser diodes (LDs) clamps at threshold, so the efficiency of LDs does not droop above threshold and high efficiencies can be achieved at very high current densities. The use of a high power blue GaN-based LD coupled with a single crystal Ce-doped yttrium aluminum garnet (YAG:Ce) sample was investigated for white light illumination applications. Under CW operation, a single phosphor-converted LD (pc-LD) die produced a peak luminous efficacy of 86.7 lm/W at 1.4 A and 4.24 V and a peak luminous flux of 1100 lm at 3.0 A and 4.85 V with a luminous efficacy of 75.6 lm/W. Simulations of a pc-LD confirm that the single crystal YAG:Ce sample did not experience thermal quenching at peak LD operating efficiency. These results show that a single pc-LD die is capable of emitting enough luminous flux for use in a high power white light illumination system.

  17. The reactive element effect of yttrium and yttrium silicon on high temperature oxidation of NiCrAl coating

    Science.gov (United States)

    Ramandhany, S.; Sugiarti, E.; Desiati, R. D.; Martides, E.; Junianto, E.; Prawara, B.; Sukarto, A.; Tjahjono, A.

    2018-03-01

    The microstructure formed on the bond coat affects the oxidation resistance, particularly the formation of a protective oxide layer. The adhesion of bond coat and TGO increased significantly by addition of reactive element. In the present work, the effect of yttrium and yttrium silicon as reactive element (RE) on NiCrAl coating was investigated. The NiCrAl (without RE) and NiCrAlX (X:Y or YSi) bond coating were deposited on Hastelloy C-276 substrate by High Velocity Oxygen Fuel (HVOF) method. Isothermal oxidation was carried out at 1000 °C for 100 hours. The results showed that the addition of RE could prevent the breakaway oxidation. Therefore, the coating with reactive element were more protective against high temperature oxidation. Furthermore, the oxidation rate of NiCrAlY coating was lower than NiCrAlYSi coating with the total mass change was ±2.394 mg/cm2 after 100 hours of oxidation. The thickness of oxide scale was approximately 1.18 μm consisting of duplex oxide scale of spinel NiCr2O4 in outer scale and protective α-Al2O3 in inner scale.

  18. Recovery of yttrium from cathode ray tubes and lamps’ fluorescent powders: experimental results and economic simulation

    International Nuclear Information System (INIS)

    Innocenzi, V.; De Michelis, I.; Ferella, F.; Vegliò, F.

    2013-01-01

    Highlights: • Fluorescent powder of lamps. • Fluorescent powder of cathode ray rubes. • Recovery of yttrium from fluorescent powders. • Economic simulation for the processes to recover yttrium from WEEE. - Abstract: In this paper, yttrium recovery from fluorescent powder of lamps and cathode ray tubes (CRTs) is described. The process for treating these materials includes the following: (a) acid leaching, (b) purification of the leach liquors using sodium hydroxide and sodium sulfide, (c) precipitation of yttrium using oxalic acid, and (d) calcinations of oxalates for production of yttrium oxides. Experimental results have shown that process conditions necessary to purify the solutions and recover yttrium strongly depend on composition of the leach liquor, in other words, whether the powder comes from treatment of CRTs or lamp. In the optimal experimental conditions, the recoveries of yttrium oxide are about 95%, 55%, and 65% for CRT, lamps, and CRT/lamp mixture (called MIX) powders, respectively. The lower yields obtained during treatments of MIX and lamp powders are probably due to the co-precipitation of yttrium together with other metals contained in the lamps powder only. Yttrium loss can be reduced to minimum changing the experimental conditions with respect to the case of the CRT process. In any case, the purity of final products from CRT, lamps, and MIX is greater than 95%. Moreover, the possibility to treat simultaneously both CRT and lamp powders is very important and interesting from an industrial point of view since it could be possible to run a single plant treating fluorescent powder coming from two different electronic wastes

  19. Uranium recovery from wet process phosphoric acid

    International Nuclear Information System (INIS)

    1980-01-01

    In the field of metallurgy, specifically processes for recovering uranium from wet process phosphoric acid solution derived from the acidulation of uraniferous phosphate ores, problems of imbalance of ion exchange agents, contamination of recycled phosphoric acid with process organics and oxidizing agents, and loss and contamination of uranium product, are solved by removing organics from the raffinate after ion exchange conversion of uranium to uranous form and recovery thereof by ion exchange, and returning organics to the circuit to balance mono and disubstituted ester ion exchange agents; then oxidatively stripping uranium from the agent using hydrogen peroxide; then after ion exchange recovery of uranyl and scrubbing, stripping with sodium carbonate and acidifying the strip solution and using some of it for the scrubbing; regenerating the sodium loaded agent and recycling it to the uranous recovery step. Economic recovery of uranium as a by-product of phosphate fertilizer production is effected. (author)

  20. The Influence of Phosphor and Binder Chemistry on the Aging Characteristics of Remote Phosphor Products

    Energy Technology Data Exchange (ETDEWEB)

    Davis, Lynn; Yaga, Robert; Lamvik, Michael; Mills, Karmann; Fletcher, B.

    2017-06-30

    The influence of phosphor and binder layer chemistries on the lumen maintenance and color stability of remote phosphor disks were examined using wet high-temperature operational lifetime testing (WHTOL). As part of the experimental matrix, two different correlated color temperature (CCT) values, 2700 K and 5000 K, were studied and each had a different binder chemistry. The 2700 K samples used a urethane binder whereas the 5000 K samples used an acrylate binder. Experimental conditions were chosen to enable study of the binder and phosphor chemistries and to minimize photo-oxidation of the polycarbonate substrate. Under the more severe WHTOL conditions of 85°C and 85% relative humidity (RH), absorption in the binder layer significantly reduced luminous flux and produced a blue color shift. The milder WHTOL conditions of 75°C and 75% RH, resulted in chemical changes in the binder layer that may alter its index of refraction. As a result, lumen maintenance remained high, but a slight yellow shift was found. The aging of remote phosphor products provides insights into the impact of materials on the performance of phosphors in an LED lighting system.

  1. [Change traits of phosphorous consumption structure in China and their effects on environmental phosphorous loads].

    Science.gov (United States)

    Ma, Dun-Chao; Hu, Shan-Ying; Chen, Ding-Jiang; Li, You-Run

    2012-04-01

    Substance flow analysis was used to construct a model to analyze change traits of China's phosphorous (P) consumption structure from 1980 to 2008 and their influences on environmental phosphorous loads, then the correlation between several socioeconomic factors and phosphorous consumption pollution was investigated. It is found that phosphorous nutrient inputs of urban life and rural life on a per capita level climbed to 1.20 kg x a(-1) and 0.99 kg x a(-1) from 0.83 kg x a(-1) and 0.75 kg x a(-1) respectively, but phosphorous recycling ratios of urban life fell to 15.6% from 62.6%. P inputs of animal husbandry and planting also kept increasing, but the recycling ratio of the former decreased from 67.5% to 40.5%, meanwhile much P input of the latter was left in agricultural soil. Correlation coefficients were all above 0.90, indicating that population, urbanization level, development levels of planting and animal husbandry were important incentives for P consumption pollution in China. Environmental Kuznets curve showed that China still stayed in the early development stage, promoting economic growth at an expense of environmental quality. This study demonstrates that China's P consumption system is being transformed into a linear and open structure, and that P nutrient loss and environmental P loads increase continually.

  2. Neutron activation determination of oxygen in ceramic materials on the basis of yttrium, barium and copper

    International Nuclear Information System (INIS)

    Goldshtein, M.M.; Yudelevich, I.G.

    1991-01-01

    A procedure of determining oxygen in superconducting materials on the basis of yttrium, barium and copper oxides with the application of 14 MeV-neutron activation was developed. The method is based on determining the relation between oxygen and yttrium in the compounds investigated. In order to minimize systematic errors, expressions accounting for spectrometer dead time under conditions of varying component activity are proposed. The procedure ensures determination of the relation between oxygen and yttrium with a relative error of 0.4% with NAA using a neutron generator. (author) 4 refs.; 1 fig

  3. Study of behaviour of lanthanum- and yttrium electrodes in chloride melts

    International Nuclear Information System (INIS)

    Shkol'nikov, S.I.; Tolypin, E.S.; Yur'ev, B.P.

    1984-01-01

    A study was made on the lanthanum- and yttrium behaviour in a mixture of molten potassium- and sodium chlorides at various temperatures. It is shown that the lanthanum- and yttrium behaviour in KCl-NaCl melt is similar to the behaviour of other metals. Their corrosion rate is much higher as compared to other metals and it grows rapidly with increasing melt temperature. The temperature growth by 200 deg C results in an increase in the corrosion rate almost by an order. The potentials of lanthanum- and yttrium electrodes at the instant they are immersed in the melt have more negative values than the potentials of alkali metals under similar conditions

  4. Effect of yttrium chromite doping on its resistance to high-temperature salt and gas corrosions

    International Nuclear Information System (INIS)

    Oryshich, I.V.; Poryadchenko, N.E.; Rakitskij, A.N.; Bega, N.D.

    1996-01-01

    Effect of yttrium chromite doping with 2-4 group metal oxides on the corrosion resistance in the air at 1300 C during 5 hours and in sodium chloride and sulfate melts at 900 C during 20 hours is investigated. A notable increase of corrosion resistance is achieved under complex doping with zirconium and magnesium oxides in a quantity, close to solubility in yttrium oxide and solubility by aluminium oxide. Doping with calcium and strontium oxides in the quantities, dose to solubility in yttrium oxide does not produce any notable effect, and at higher concentrations it reduces the corrosion resistance in media indicated. Refs. 8, refs. 2, tabs. 1

  5. Ultraviolet dosimetry using thermoluminescent phosphors - an update

    International Nuclear Information System (INIS)

    Nagpal, J.S.

    1998-04-01

    Intrinsic response of various thermoluminescent (TL) materials such as CaSO 4 (Dy, Eu, Mn, Sm, Tb, or Tm), LiF (Mg, Cu, P), Mg 2 SiO 4 :Tb, CaF 2 :Dy, CaF 2 :Tb, ThO 2 :Tb and Al 2 O 3 (Si, Ti); cathodoluminescent phosphors Y 3 Al 5 O 12 :Ce, Y 3 Al 5 O 12 :Tb and Y(V,P)O 4 :Eu; and fluorescent lamp phosphors calcium halophosphate (Mn,Sb) and Ce Mg aluminate (Eu, Tb) to ultraviolet (UV) radiations has been studied. Intrinsic TL response of most of the phosphors is rate (radiant flux) dependent. For the first time, UV response of the materials is reported for a fixed total radiant energy (total UV dose), at a single radiant flux (260 μW.cm -2 ), for an appropriate comparison. A wide range of UV sensitivity is observed. Studies conducted using UV radiation from two unfiltered low pressure mercury lamps show significant differences in glow curves, as compared to those obtained with nearly monochromatic UV radiations. Photons of wavelength 365 nm induce bleaching of TL induced by 254 nm photons, in most of the materials. Sequential/tandem exposures to 254 nm and 365 nm photons have yielded new but alarming results in CaF 2 :Tb. Preferential induction and bleaching of specific TL glow peaks by 365 nm and 254 nm photons are interesting characteristics discovered in CaSO 4 :Eu. Photoluminescence studies of Tb 3+ and Eu 3+ activated phosphors have augmented the inferences drawn from the bleaching effects produced by 365 nm photons. Earlier work carried out on phototransferred thermoluminescence of CaSO 4 :Dy-teflon dosimeters, TLD-100, Mg 2 SiO 4 :Tb and Al 2 O 3 (Si,Ti) has also been reviewed. (author)

  6. Phosphor for thermoluminescent type radiation dosimeter

    International Nuclear Information System (INIS)

    Nada, N.; Yamashita, T.

    1975-01-01

    This has the accumulation effect of radiation energy and is mainly used as the element for thermoluminescent type radiation dosimeters. It has as the principal constituent a phosphor consisting of calcium sulfate as the principal constituent and other impurity elements such as dysprosium, thulium and the like. It is more sensitive by the order of 1 to 2 or more figures than the conventional ones and is excellent in the retention of absorbed radiation energy. (U.S.)

  7. Thermoluminescence of calcium-based phosphors

    International Nuclear Information System (INIS)

    Sunta, C.M.

    1985-01-01

    The paper reviews the thermoluminescence (TL) properties of calcium fluoride, calcium sulphate and calcium carbonate phosphors. In the case of the calcium fluoride mineral phosphor the main emitter of TL is the cerium impurity. Based on the TL emission spectra, two types of Ce 3+ centres can be easily distinguished; those associated with O 2- compensating ion and those which have either no local compensators or are associated with F - interstitial ions at the adjacent vacant body centre position. The spectra undergo remarkable changes at high doses. Such changes are associated with the probabilities of charge trapping at different types of traps and also with the probabilities of recombination at different types of luminescent centres. Some of the traps and recombination centres are spatially associated while others are distributed randomly. In calcium carbonate mineral, Mn 2+ is invariably the emitting impurity. Mn 2+ can be used as an efficient dopant for TL emission in all the three calcium based TL phosphors. A co-dopant like Ce 3+ intensifies the luminescence yield from Mn 2+ . Models of different types of electron and hole trapping centres are given. (author)

  8. Investigation of saturation effects in ceramic phosphors for laser lighting

    DEFF Research Database (Denmark)

    Krasnoshchoka, Anastasiia; Thorseth, Anders; Dam-Hansen, Carsten

    2017-01-01

    We report observation of saturation effects in a Ce:LuAG and Eu-doped nitride ceramic phosphor for conversion of blue laser light for white light generation. The luminous flux from the phosphors material increases linearly with the input power until saturation effects limit the conversion....... It is shown, that the temperature of the phosphor layer influences the saturation power level and the conversion efficiency. It is also shown that the correlated color temperature (CCT), phosphor conversion efficiency and color rendering index (CRI) are dependent both on incident power and spot size diameter...... of the illumination. A phosphor conversion efficiency up to 140.8 lm/W with CRI of 89.4 was achieved. The saturation in a ceramic phosphor, when illuminated by high intensity laser diodes, is estimated to play the main role in limiting the available luminance from laser based lighting systems....

  9. The spectrum of singly ionized yttrium, Y II

    International Nuclear Information System (INIS)

    Nilsson, A.E.; Johansson, S.; Kurucz, R.L.

    1991-01-01

    Hollow-cathode spectra of yttrium have been registered in the wavelength region 1000-48800 A. Resonant charge transfer reactions in the light source favour the excitation of Y II, where 174 new levels have been established by means of 1284 newly classified lines. Altogether we report 1521 lines between 235 levels in Y II. The ground complex (4d+5s) 2 is now completely known and a number of Rydberg series have been extended. The new levels belong to the 4dnl (nl=7s, 8s, 9s, 6p, 7p, 4d, 5d, 6d, 7d, 8d, 4f, 5f, 6f, 7f, 5g) and 5snl (nl=7s, 8s, 6p, 6d, 4f, 5f) configurations. Eigenvector compositions, based on paramagnetic calculations including configuration interaction, are given for all levels. The ionization limit has been determined to 98590 ± 5 cm -1 . (orig.)

  10. Calorimetric investigation of an yttrium-dysprosium spin glass

    International Nuclear Information System (INIS)

    Wenger, L.E.

    1978-01-01

    In an effort to compare the spin glass characteristics of yttrium--rare earth alloys with those of the noble-metal spin glasses, the susceptibility and heat capacity of Y/sub 0.98/Dy/sub 0.02/ have been measured in the temperature range 2.5--40 K. The low-field ac susceptibility measurement shows the characteristic cusp-like peak at 7.64 K. The magnetic specific heat of the same sample shows a peak at 7.0 K and may be qualitatively described as a semi-cusp. The magnetic entropy change from absolute zero to 7 K is approximately 0.52 of cR ln(2J+1). These results are qualitatively different than previous calorimetric results on the archetypal spin glasses, AuFe and CuMn, where rounded maxima are observed at temperatures above the spin glass transition temperatures

  11. RBS Characterization of Yttrium Iron Garnet Thin Films

    International Nuclear Information System (INIS)

    Roumie, M; Abdel samad, B.

    2008-01-01

    Magnetic materials such as yttrium iron garnet (YIG) are of great importance for its magneto-optic properties and for their potential applications in the domain of optical telecommunications. The deposition of thin films of YIG, on quartz or GGG (gadolinium gallium garnet) substrate, was performed using radio frequency non reactive magnetron sputtering, followed by high temperature annealing which is needed to enhance the crystallinity of the layers. Rutherford backscattering spectrometry RBS was used to determine the thickness and stoichiometry of the performed layers in order to investigate correlations between growth conditions and the quality of the final material. RBS measurements showed the influence of the deposition time and the temperature substrate on the film growth and its stoichiometry. (author)

  12. A divalent rare earth oxide semiconductor: Yttrium monoxide

    Energy Technology Data Exchange (ETDEWEB)

    Kaminaga, Kenichi; Sei, Ryosuke [Department of Chemistry, The University of Tokyo, Tokyo 113-0033 (Japan); Department of Chemistry, Tohoku University, Sendai 980-8578 (Japan); Hayashi, Kouichi [Department of Environmental and Materials Engineering, Nagoya Institute of Technology, Nagoya 466-8555 (Japan); Happo, Naohisa [School of Information Sciences, Hiroshima City University, Hiroshima 731-3194 (Japan); Tajiri, Hiroo [Japan Synchrotron Radiation Research Institute (JASRI)/SPring-8, Sayo 679-5198 (Japan); Oka, Daichi; Fukumura, Tomoteru, E-mail: tomoteru.fukumura.e4@tohoku.ac.jp [Department of Chemistry, Tohoku University, Sendai 980-8578 (Japan); Hasegawa, Tetsuya [Department of Chemistry, The University of Tokyo, Tokyo 113-0033 (Japan)

    2016-03-21

    Rare earth oxides are usually widegap insulators like Y{sub 2}O{sub 3} with closed shell trivalent rare earth ions. In this study, solid phase rock salt structure yttrium monoxide, YO, with unusual valence of Y{sup 2+} (4d{sup 1}) was synthesized in a form of epitaxial thin film by pulsed laser deposition method. YO has been recognized as gaseous phase in previous studies. In contrast with Y{sub 2}O{sub 3}, YO was dark-brown colored and narrow gap semiconductor. The tunable electrical conductivity ranging from 10{sup −1} to 10{sup 3} Ω{sup −1 }cm{sup −1} was attributed to the presence of oxygen vacancies serving as electron donor. Weak antilocalization behavior observed in magnetoresistance indicated significant role of spin-orbit coupling as a manifestation of 4d electron carrier.

  13. Tunable negative index metamaterial using yttrium iron garnet

    International Nuclear Information System (INIS)

    He, Yongxue; He, Peng; Dae Yoon, Soack; Parimi, P.V.; Rachford, F.J.; Harris, V.G.; Vittoria, C.

    2007-01-01

    A magnetic field tunable, broadband, low-loss, negative refractive index metamaterial is fabricated using yttrium iron garnet (YIG) and a periodic array of copper wires. The tunability is demonstrated from 18 to 23 GHz under an applied magnetic field with a figure of merit of 4.2 GHz/kOe. The tuning bandwidth is measured to be 5 GHz compared to 0.9 GHz for fixed field. We measure a minimum insertion loss of 4 dB (or 5.7 dB/cm) at 22.3 GHz. The measured negative refractive index bandwidth is 0.9 GHz compared to 0.5 GHz calculated by the transfer function matrix theory and 1 GHz calculated by finite element simulation

  14. {alpha}-particle induced reactions on yttrium and terbium

    Energy Technology Data Exchange (ETDEWEB)

    Mukherjee, S.; Kumar, B.B. [School of Studies in Physics, Vikram University, Ujjain-456010 (India); Rashid, M.H. [Variable Energy Cyclotron Center, 1/AF, Bidhan Nagar, Calcutta (India); Chintalapudi, S.N. [Inter-University Consortium for DAE Facilities, 3/LB, Bidhan Nagar, Calcutta (India)

    1997-05-01

    The stacked foil activation technique has been employed for the investigation of {alpha}-particle induced reactions on the target elements yttrium and terbium up to 50 MeV. Six excitation functions for the ({alpha},xn) type of reactions were studied using high-resolution HPGe {gamma}-ray spectroscopy. A comparison with Blann{close_quote}s geometric dependent hybrid model has been made using the initial exciton number n{sub 0}=4(4p0h) and n{sub 0}=5(5p0h). A broad general agreement is observed between the experimental results and theoretical predictions with an initial exciton number n{sub 0}=4(4p0h). {copyright} {ital 1997} {ital The American Physical Society}

  15. α-particle induced reactions on yttrium and terbium

    International Nuclear Information System (INIS)

    Mukherjee, S.; Kumar, B.B.; Rashid, M.H.; Chintalapudi, S.N.

    1997-01-01

    The stacked foil activation technique has been employed for the investigation of α-particle induced reactions on the target elements yttrium and terbium up to 50 MeV. Six excitation functions for the (α,xn) type of reactions were studied using high-resolution HPGe γ-ray spectroscopy. A comparison with Blann close-quote s geometric dependent hybrid model has been made using the initial exciton number n 0 =4(4p0h) and n 0 =5(5p0h). A broad general agreement is observed between the experimental results and theoretical predictions with an initial exciton number n 0 =4(4p0h). copyright 1997 The American Physical Society

  16. Thermal conductivity of yttrium iron garnet at low temperatures

    International Nuclear Information System (INIS)

    Joshi, Y.P.; Sing, D.P.

    1979-01-01

    An analysis of the low-temperature thermal conductivity of yttrium iron garnet is presented giving consideration to the fact that in a conventional conductivity experiment the magnon temperature gradient inside a magnetic insulator need not be necessarily equal to the phonon temperature gradient. Consequently the effective conductivity can be less than the algebraic sum of the phonon and magnon intrinsic conductivities, depending on the magnon-phonon thermal relaxation rate. This relaxation rate has been distinguished from the individual phonon and magnon relaxation rates and an expression is derived for it. Theoretical calculations of the effective conductivity are found to be in good agreement with experimental results. The contribution of magnons to the effective conductivity is observed to be small at all temperatures below the conductivity maximum. (author)

  17. Yttrium orthoferrite powder obtained by the mechanochemical synthesis

    Directory of Open Access Journals (Sweden)

    Lazarević Zorica Ž.

    2017-01-01

    Full Text Available Yttrium orthoferrite (YFeO3 powder was prepared by a mechanochemical synthesis from a mixture of Y2O3 and α-Fe2O3 powders in a planetary ball mill for 2.5 h. The obtained YFeO3 powder sample was characterized by X-ray diffraction (XRD, Raman and infrared spectroscopy. The average crystallite size calculated by the Scherrer equation was 12 nm. The Mössbauer spectroscopy at room temperature confirms the superparamagnetic character of YFeO3 orthoferrite sample. [Project of the Serbian Ministry of Education, Science and Technological Development, Grant no. III 45003, Grant no. III 45015, Grant no. III 45018

  18. Nanoscale nonlinear effects in Erbium-implanted Yttrium Orthosilicate

    Energy Technology Data Exchange (ETDEWEB)

    Kukharchyk, Nadezhda, E-mail: nadezhda.kukharchyk@physik.uni-saarland.de [Experimentalphysik, Universität des Saarlandes, D-66123 Saarbrücken (Germany); Angewandte Festkörperphysik, Ruhr-Universität Bochum, D-44780 Bochum (Germany); Shvarkov, Stepan [Optoelektronische Materialien und Bauelemente, Universität Paderborn, D-33098 Padeborn (Germany); Probst, Sebastian [Quantronics group, Service de Physique de l' Etat Condense, DSM/IRAMIS/SPEC, CNRS UMR 3680, CEA-Saclay, 91191 Gif-sur-Yvette cedex (France); Xia, Kangwei [3. Physikalisches Institut, Universität Stuttgart, D-70569 Stuttgart (Germany); Becker, Hans-Werner [RUBION, Ruhr-Universität Bochum, D-44780 Bochum (Germany); Pal, Shovon [Angewandte Festkörperphysik, Ruhr-Universität Bochum, D-44780 Bochum (Germany); AG THz Spectroscopie und Technologie, Ruhr-Universität Bochum, D-44780 Bochum (Germany); Markmann, Sergej [AG THz Spectroscopie und Technologie, Ruhr-Universität Bochum, D-44780 Bochum (Germany); Kolesov, Roman; Siyushev, Petr; Wrachtrup, Jörg [3. Physikalisches Institut, Universität Stuttgart, D-70569 Stuttgart (Germany); Ludwig, Arne [Angewandte Festkörperphysik, Ruhr-Universität Bochum, D-44780 Bochum (Germany); Ustinov, Alexey V. [Physikalisches Institut, Karlsruhe Institute of Technology, D-76128 Karlsruhe (Germany); Wieck, Andreas D. [Angewandte Festkörperphysik, Ruhr-Universität Bochum, D-44780 Bochum (Germany); and others

    2016-09-15

    Doping of substrates at desired locations is a key technology for spin-based quantum memory devices. Focused ion beam implantation is well-suited for this task due to its high spacial resolution. In this work, we investigate ion-beam implanted Erbium ensembles in Yttrium Orthosilicate crystals by means of confocal photoluminescence spectroscopy. The sample temperature and the post-implantation annealing step strongly reverberate in the properties of the implanted ions. We find that hot implantation leads to a higher activation rate of the ions. At high enough fluences, the relation between the fluence and final concentration of ions becomes non-linear. Two models are developed explaining the observed behavior.

  19. Successful treatment of Cushing's disease using yttrium-90 rods

    International Nuclear Information System (INIS)

    White, M.C.; Doyle, F.H.; Mashiter, K.; Joplin, G.F.

    1982-01-01

    Interstitial irradiation using yttrium-90 ( 90 Y) rods implanted by needle into the pituitary gland was used as primary treatment in 16 patients with pituitary dependent Cushing's disease. Clinical and biochemical remission was observed within three to six months in 13 and in the remaining three after a supplementary implant. There was no perioperative morbidity. Follow-up from the time of definitive operation ranged from six to 123 months (mean 39). No recurrence has been observed. The return of a normal diurnal cortisol rhythm has been observed in 10/12 patients studied after remission. Some form of long-term pituitary hormone replacement therapy was required in only the six patients who had received the largest irradiation dose. Implantation of 90 Y is safe and effective treatment for patients with Cushing's disease, comparing favourably with selective trans-sphenoidal pituitary surgery. (author)

  20. Photocatalysis of Yttrium Doped BaTiO3 Nanofibres Synthesized by Electrospinning

    Directory of Open Access Journals (Sweden)

    Zhenjiang Shen

    2015-01-01

    Full Text Available Yttrium doped barium titanate (BT nanofibres (NFs with significant photocatalytic effect were successfully synthesized by electrospinning. Considering the necessary factors for semiconductor photocatalysts, a well-designed procedure was carried out to produce yttrium doped BT (BYT NFs. In contrast to BYT ceramics powders and BT NFs, BYT NFs with pure perovskite phase showed much enhanced performance of photocatalysis. The surface modification in electrospinning and subsequent annealing, the surface spreading of transition metal yttrium, and the narrowed band gap energy in yttrium doping were all contributed to the final novel photocatalytic effect. This work provides a direct and efficient route to obtain doped NFs, which has a wide range of potential applications in areas based on complex compounds with specific surface and special doping effect.

  1. Polymer Derived Yttrium Silicate Ablative TPS Materials for Next-Generation Exploration Missions, Phase I

    Data.gov (United States)

    National Aeronautics and Space Administration — Through the proposed NASA SBIR program, NanoSonic will optimize its HybridSil® derived yttrium silicates to serve as next-generation reinforcement for carbon and...

  2. Synthesis of yttrium oxide nanoparticles via a facile microplasma-assisted process

    NARCIS (Netherlands)

    Lin, Liangliang; Starostin, Sergey A.; Li, Sirui; Khan, Saif A.; Hessel, Volker

    2018-01-01

    Plasma electrochemistry is an emerging technique for nanomaterial synthesis. The present study reports the preparation of yttrium oxide nanoparticles via a simple, environmentally benign, microplasma-assisted process operated in pin-to-liquid configuration under ambient atmospheric conditions using

  3. Counter current extraction of phosphoric acid: Food grade acid production

    International Nuclear Information System (INIS)

    Shlewit, H.; AlIbrahim, M.

    2009-01-01

    Extraction, scrubbing and stripping of phosphoric acid from the Syrian wet-phosphoric acid was carried out using Micro-pilot plant of mixer settler type of 8 l/h capacity. Tributyl phosphate (TBP)/di-isopropyl ether (DIPE) in kerosene was used as extractant. Extraction and stripping equilibrium curves were evaluated. The number of extraction and stripping stages to achieve the convenient and feasible yield was determined. Detailed flow sheet was suggested for the proposed continuous process. Data obtained include useful information for the design of phosphoric acid extraction plant. The produced phosphoric acid was characterized using different analytical techniques. (author)

  4. Uranium recovery from wet-process phosphoric acid

    International Nuclear Information System (INIS)

    McCullough, J.F.; Phillips, J.F. Jr.; Tate, L.R.

    1979-01-01

    A method of recovering uranium from wet-process phosphoric acid is claimed where the acid is treated with a mixture of an ammonium salt or ammonia, a reducing agent, and then a miscible solvent. Solids are separated from the phosphoric acid liquid phase. The solid consists of a mixture of metal phosphates and uranium. It is washed free of adhering phosphoric acid with fresh miscible solvent. The solid is dried and dissolved in acid whereupon uranium is recovered from the solution. Miscible solvent and water are distilled away from the phosphoric acid. The distillate is rectified and water discarded. All miscible solvent is recovered for recycle. 5 claims

  5. Method of recovering phosphoric acid type decontaminating electrolytes by electrodeposition

    International Nuclear Information System (INIS)

    Sasaki, Takashi; Wada, Koichi; Kobayashi, Toshio.

    1985-01-01

    Purpose: To recoving phosphoric acid type highly concentrated decontaminating liquid used for the electrolytic decontamination of contaminated equipments, components, etc in nuclear power plants or the like through electrodeposition by diaphragm electrolysis. Method: Before supplying phosphoric acid decontaminating liquid at high concentration used in the electrolytic decontaminating step to an electrodeposition recovering tank, phosphoric acid in the decontaminating electrolyte is extracted with solvents and decomposed liquid extracts (electrolyte reduced with the phosphoric acid component) are supplied to the cathode chamber of the electrodeposition recovering tank, where phosphoric acid is back-extracted with water from the solvents after extraction of phosphoric acid. Then, the back-extracted liquids (aqueous phosphoric acid solution scarcely containing metal ions) are sent to the anode chamber of the electrodeposition recovering tank. Metal ions in the liquid are captured by electrodeposition in the cathode chamber, as well as phosphoric acid in the liquids is concentrated to the initial concentration of the electrolyte in the anode chamber for reuse as the decontaminating electrolyte. As the phosphoric acid extracting agent used in the electrodeposition recovering step for the decontaminating electrolyte, water-insoluble and non-combustible tributyl phosphate (TBP) is most effective. (Horiuchi, T.)

  6. Point defect engineering strategies to retard phosphorous diffusion in germanium

    KAUST Repository

    Tahini, H. A.; Chroneos, Alexander I.; Grimes, Robin W.; Schwingenschlö gl, Udo; Bracht, Hartmut A.

    2013-01-01

    The diffusion of phosphorous in germanium is very fast, requiring point defect engineering strategies to retard it in support of technological application. Density functional theory corroborated with hybrid density functional calculations are used to investigate the influence of the isovalent codopants tin and hafnium in the migration of phosphorous via the vacancy-mediated diffusion process. The migration energy barriers for phosphorous are increased significantly in the presence of oversized isovalent codopants. Therefore, it is proposed that tin and in particular hafnium codoping are efficient point defect engineering strategies to retard phosphorous migration. © the Owner Societies 2013.

  7. Tm3+ activated lanthanum phosphate: a blue PDP phosphor

    International Nuclear Information System (INIS)

    Rao, R.P.

    2005-01-01

    Plasma display panels (PDPs) are gaining attention due to their high performance and scalability as a medium for large format TVs. The performance and life of a PDP strongly depends upon the nature of phosphors. Currently, Eu 2+ activated barium magnesium aluminate (BAM) is being used as a blue component. Because of its low life, efforts are being made to explore new blue emitting phosphors. One of the alternatives to BAM is Tm 3+ activated lanthanum phosphate (LPTM) phosphor. LPTM phosphor samples are prepared by a solid-state as well as sol-gel process in presence of flux. The phosphor of the present investigation, having uniform and spherical shape particles in the range of 0.1-2 μm, is appropriate for thin phosphor screens required for PDP applications. It exhibits a narrow band emission in the blue region, peaking at 452 nm and also a number of narrow bands in the UV region when excited by 147 and 173 nm radiation from a xenon gas mixture. Various possible transitions responsible for UV and visible emission from Tm 3+ ion are presented. These phosphors also exhibit good color saturation and better stability when excited with VUV radiation. To achieve higher brightness, they are blended with other UV excited blue emitting phosphors such as BAM. Results related to morphology, excitation, after glow decay, emission and degradation of these phosphors in the powder form as well as in plasma display panels are presented and discussed

  8. Recovery of yttrium from fluorescent powder of cathode ray tube, CRT: Zn removal by sulphide precipitation

    International Nuclear Information System (INIS)

    Innocenzi, Valentina; De Michelis, Ida; Ferella, Francesco; Beolchini, Francesca; Kopacek, Bernd; Vegliò, Francesco

    2013-01-01

    Highlights: • Treatment of fluorescent powder of CRT waste. • Factorial experimental designs to study acid leaching of fluorescent powder and the purification of leach liquors. • Recover of yttrium by precipitation using oxalic acid. • Suitable flowsheet to recover yttrium from fluorescent powder. - Abstract: This work is focused on the recovery of yttrium and zinc from fluorescent powder of cathode ray tube (CRT). Metals are extracted by sulphuric acid in the presence of hydrogen peroxide. Leaching tests are carried out according to a 2 2 full factorial plan and the highest extraction yields for yttrium and zinc equal to 100% are observed under the following conditions: 3 M of sulphuric acid, 10% v/v of H 2 O 2 concentrated solution at 30% v/v, 10% w/w pulp density, 70 °C and 3 h of reaction. Two series of precipitation tests for zinc are carried out: a 2 2 full factorial design and a completely randomized factorial design. In these series the factors investigated are pH of solution during the precipitation and the amount of sodium sulphide added to precipitate zinc sulphide. The data of these tests are used to describe two empirical mathematical models for zinc and yttrium precipitation yields by regression analysis. The highest precipitation yields for zinc are obtained under the following conditions: pH equal to 2–2.5% and 10–12% v/v of Na 2 S concentrated solution at 10% w/v. In these conditions the coprecipitation of yttrium is of 15–20%. Finally further yttrium precipitation experiments by oxalic acid on the residual solutions, after removing of zinc, show that yttrium could be recovered and calcined to obtain the final product as yttrium oxide. The achieved results allow to propose a CRT recycling process based on leaching of fluorescent powder from cathode ray tube and recovery of yttrium oxide after removing of zinc by precipitation. The final recovery of yttrium is 75–80%

  9. Recovery of yttrium from fluorescent powder of cathode ray tube, CRT: Zn removal by sulphide precipitation

    Energy Technology Data Exchange (ETDEWEB)

    Innocenzi, Valentina, E-mail: valentina.innocenzi1@univaq.it [Department of Industrial Engineering and Information and Economy, University of L’Aquila, Via Giovanni Gronchi n.18, Nucleo Ind.le di Pile, 67100 L’Aquila (Italy); De Michelis, Ida; Ferella, Francesco [Department of Industrial Engineering and Information and Economy, University of L’Aquila, Via Giovanni Gronchi n.18, Nucleo Ind.le di Pile, 67100 L’Aquila (Italy); Beolchini, Francesca [Department of Marine Sciences, Polytechnic Institute of Marche, Via Brecce Bianche, 60131 Ancona (Italy); Kopacek, Bernd [SAT, Austrian Society for Systems Engineering and Automation, Gurkasse 43/2, A-1140 Vienna (Austria); Vegliò, Francesco [Department of Industrial Engineering and Information and Economy, University of L’Aquila, Via Giovanni Gronchi n.18, Nucleo Ind.le di Pile, 67100 L’Aquila (Italy)

    2013-11-15

    Highlights: • Treatment of fluorescent powder of CRT waste. • Factorial experimental designs to study acid leaching of fluorescent powder and the purification of leach liquors. • Recover of yttrium by precipitation using oxalic acid. • Suitable flowsheet to recover yttrium from fluorescent powder. - Abstract: This work is focused on the recovery of yttrium and zinc from fluorescent powder of cathode ray tube (CRT). Metals are extracted by sulphuric acid in the presence of hydrogen peroxide. Leaching tests are carried out according to a 2{sup 2} full factorial plan and the highest extraction yields for yttrium and zinc equal to 100% are observed under the following conditions: 3 M of sulphuric acid, 10% v/v of H{sub 2}O{sub 2} concentrated solution at 30% v/v, 10% w/w pulp density, 70 °C and 3 h of reaction. Two series of precipitation tests for zinc are carried out: a 2{sup 2} full factorial design and a completely randomized factorial design. In these series the factors investigated are pH of solution during the precipitation and the amount of sodium sulphide added to precipitate zinc sulphide. The data of these tests are used to describe two empirical mathematical models for zinc and yttrium precipitation yields by regression analysis. The highest precipitation yields for zinc are obtained under the following conditions: pH equal to 2–2.5% and 10–12% v/v of Na{sub 2}S concentrated solution at 10% w/v. In these conditions the coprecipitation of yttrium is of 15–20%. Finally further yttrium precipitation experiments by oxalic acid on the residual solutions, after removing of zinc, show that yttrium could be recovered and calcined to obtain the final product as yttrium oxide. The achieved results allow to propose a CRT recycling process based on leaching of fluorescent powder from cathode ray tube and recovery of yttrium oxide after removing of zinc by precipitation. The final recovery of yttrium is 75–80%.

  10. Radiation protection data sheets for the use of Strontium 90-Yttrium 90 in unsealed sources

    International Nuclear Information System (INIS)

    Anon.

    1993-01-01

    This radiation protection data sheet is intended for supervisors and staff in the different medical, hospital, pharmaceutical, university and industrial laboratories and departments where Strontium 90-Yttrium 90 is handled, and also for all those involved in risk prevention in this field. It provides essential data on radiation protection measures during the use of Strontium 90-Yttrium 90 in unsealed sources: physical characteristics, risk assessment, administrative procedures, recommendations, regulations and bibliography

  11. Temperature effect on elastic properties of yttrium ferrite garnet Y3Fe5O12

    International Nuclear Information System (INIS)

    Burenkov, Yu.A.; Nikanorov, S.P.

    2002-01-01

    One studied temperature dependence of all independent elastic constants describing comprehensively elastic anisotropy of yttrium ferrite garnet within temperature wide range covering T c . One measured the Young modules for [100] and [110] crystallographic directions and the module of shift for [100] direction of specially pure single crystal of yttrium ferrite garnet within 20-600 deg C temperature range. One analyzed behavior of elastic modules and of elastic anisotropy factor near the critical temperature of magnetic phase transition [ru

  12. Quantitative description of yttrium aluminate ceramic composition by means of Er+3 microluminescence spectrum

    Science.gov (United States)

    Videla, F. A.; Tejerina, M. R.; Moreira-Osorio, L.; Conconi, M. S.; Orzi, D. J. O.; Flores, T.; Ponce, L. V.; Bilmes, G. M.; Torchia, G. A.

    2018-05-01

    The composition of erbium-doped yttrium aluminate ceramics was analyzed by means of confocal luminescence spectroscopy, EDX, and X-ray diffraction. A well-defined linear correlation was found between a proposed estimator computed from the luminescence spectrum and the proportion of ceramic phases coexisting in different samples. This result shows the feasibility of using erbium luminescence spectroscopy to perform a quantitative determination of different phases of yttrium aluminates within a micrometric region in nanograined ceramics.

  13. Shear bond strength of orthodontic brackets after acid-etched and erbium-doped yttrium aluminum garnet laser-etched

    Directory of Open Access Journals (Sweden)

    Shiva Alavi

    2014-01-01

    Full Text Available Background: Laser ablation has been suggested as an alternative method to acid etching; however, previous studies have obtained contrasting results. The purpose of this study was to compare the shear bond strength (SBS and fracture mode of orthodontic brackets that are bonded to enamel etched with acid and erbium-doped yttrium aluminum garnet (Er:YAG laser. Materials and Methods: In this experimental in vitro study, buccal surfaces of 15 non-carious human premolars were divided into mesial and distal regions. Randomly, one of the regions was etched with 37% phosphoric acid for 15 s and another region irradiated with Er:YAG laser at 100 mJ energy and 20 Hz frequency for 20 s. Stainless steel brackets were then bonded using Transbond XT, following which all the samples were stored in distilled water for 24 h and then subjected to 500 thermal cycles. SBS was tested by a chisel edge, mounted on the crosshead of universal testing machine. After debonding, the teeth were examined under Χ10 magnification and adhesive remnant index (ARI score determined. SBS and ARI scores of the two groups were then compared using t-test and Mann-Whitney U test. Significant level was set at P < 0.05. Results: The mean SBS of the laser group (16.61 ± 7.7 MPa was not significantly different from that of the acid-etched group (18.86 ± 6.09 MPa (P = 0.41. There was no significant difference in the ARI scores between two groups (P = 0.08. However, in the laser group, more adhesive remained on the brackets, which is not suitable for orthodontic purposes. Conclusion: Laser etching at 100 mJ energy produced bond strength similar to acid etching. Therefore, Er:YAG laser may be an alternative method for conventional acid-etching.

  14. Structural and magnetic properties of yttrium iron garnet (YIG) and yttrium aluminum iron garnet (YAIG) nanoferrites prepared by microemulsion method

    Energy Technology Data Exchange (ETDEWEB)

    Akhtar, Majid Niaz, E-mail: majidniazakhtar@ciitlahore.edu.pk [Department of Physics, COMSATS Institute of Information Technology, Lahore 54000 (Pakistan); Department of Mechanical and Materials Engineering, Faculty of Engineering and Built Environment, Universiti Kebangsaan Malaysia, 43600 Bangi, Selangor (Malaysia); Bakar Sulong, Abu [Department of Mechanical and Materials Engineering, Faculty of Engineering and Built Environment, Universiti Kebangsaan Malaysia, 43600 Bangi, Selangor (Malaysia); Khan, Muhammad Azhar [Department of Physics, The Islamia University of Bahawalpur, Bahawalpur 63100 (Pakistan); Ahmad, Mukhtar [Department of Physics, COMSATS Institute of Information Technology, Islamabad (Pakistan); Murtaza, Ghulam [Centre for Advanced Studies in Physics, G.C. University, Lahore, Pakistan" f Department of Mechanical Engineering, COMSATS Institute of Information Technology Sahiwal Pakistan (Pakistan); Raza, M.R. [Department of Mechanical and Materials Engineering, Faculty of Engineering and Built Environment, Universiti Kebangsaan Malaysia, 43600 Bangi, Selangor (Malaysia); Department of Mechanical Engineering, COMSATS Institute of Information Technology Sahiwal (Pakistan); Raza, R.; Saleem, M. [Department of Physics, COMSATS Institute of Information Technology, Lahore 54000 (Pakistan); Kashif, M. [Department of Physics, Govt. College University Faisalabad (Pakistan)

    2016-03-01

    Yttrium iron garnet (YIG) and yttrium aluminum iron garnet (YAIG) nanoferrite samples were synthesized by microemulsion method. The effect of sintering was examined by heating the samples at 900, 1000, and 1100 °C. The YIG and YAIG samples were then characterized using X-ray diffraction and field-emission scanning electron microscopy. Static and dynamic magnetic properties were measured by evaluating initial permeability, Q factor, and vibrating sample magnetometry properties of YIG and YAIG samples. YIG samples sintered at 1100 °C showed higher initial permeability and Q factor compared with YAIG samples. However, hysteresis loops also showed variations in the saturation magnetization, remanence, and coercivity of YIG and YAIG samples sintered at 900, 1000, and 1100 °C. The observed magnetic parameter such as saturation magnetization, coercivity and initial permeability are strongly affected by increasing temperature. The saturation magnetization and coercivity of YIG and YAIG nanoferrites were found in the range 11.56–19.92 emu/g and 7.30–87.70 Oe respectively. Furthermore, the decreasing trends in the static and magnetic properties of YAIG samples may be due to the introduction of Al ions in the YIG crystal lattice. Thus, YIG and YAIG sintered at 1100 °C can be used for wide-ranging frequency applications. - Highlights: • Static and dynamic magnetic properties of YIG and YAIG nanoferrites were determined. • Saturation magnetization, Q and initial permeability increased in YIG nanoferites. • Possible use of these nanoferrites for sensing and switching applications.

  15. N-m-nitrocinnamoylphenylhydroxyl-amine as reagent for amperometric determination of yttrium

    International Nuclear Information System (INIS)

    Oliferenko, G.L.; Gallaj, Z.A.; Sheina, N.M.; Shvedene, N.V.

    1983-01-01

    Possibility of using organic reagent of unsaturated N-arylsubstituted derivatives class of hydroxamic acids N-m-nitrocinnamoyl phenylhydroxylamire (NCPHA) for amperometric titration of yttrium using indication of e.t.p. by current of reagent oxidation on graphite electrode is investigated. Metal and the NCPHA form difficultly soluble complex with ratio of yttrium to the NCPHA, which is equal to 1:3. Buffer mixtures of 0.1MNH 3 +0.1MCH 3 COOH composis tion with pH 6.3-7.5 are optimal background solutions for amperometric titration of yttrium. The proposed method permits to determine 10-600 μkg of yttrium in the volume of 10 ml. Effect of the series of strange elements on titration of yttrium with NCPHA (Ca, Mg, Mn (2), Al, CU (2), Fe (3) REE and others) is studied. The developed method is used for yttrium determination in luminophores of Casub(n)-- Ysub(m)Fsub(z)xMn(2) (1-10%) composition

  16. The behaviour of selected yttrium containing bioactive glass microspheres in simulated body environments.

    Science.gov (United States)

    Cacaina, D; Ylänen, H; Simon, S; Hupa, M

    2008-03-01

    The study aims at the manufacture and investigation of biodegradable glass microspheres incorporated with yttrium potentially useful for radionuclide therapy of cancer. The glass microspheres in the SiO2-Na2O-P2O5-CaO-K2O-MgO system containing yttrium were prepared by conventional melting and flame spheroidization. The behaviour of the yttrium silicate glass microspheres was investigated under in vitro conditions using simulated body fluid (SBF) and Tris buffer solution (TBS), for different periods of time, according to half-life time of the Y-90. The local structure of the glasses and the effect of yttrium on the biodegradability process were evaluated by Fourier Transform Infrared (FT-IR) spectroscopy and Back Scattered Electron Imaging of Scanning Electron Microscopy (BEI-SEM) equipped with Energy Dispersive X-ray (EDX) analysis. UV-VIS spectrometry and Inductively Coupled Plasma Mass Spectrometry (ICP-MS) was used for analyzing the release behaviour of silica and yttrium in the two used solutions. The results indicate that the addition of yttrium to a bioactive glass increases its structural stability which therefore, induced a different behaviour of the glasses in simulated body environments.

  17. Size-dependent cytotoxicity of yttrium oxide nanoparticles on primary osteoblasts in vitro

    Energy Technology Data Exchange (ETDEWEB)

    Zhou, Guoqiang, E-mail: zhougq1982@163.com; Li, Yunfei; Ma, Yanyan; Liu, Zhu; Cao, Lili; Wang, Da; Liu, Sudan; Xu, Wenshi; Wang, Wenying [Hebei University, Key Laboratory of Medicinal Chemistry and Molecular Diagnosis of Ministry of Education, Key Laboratory of Chemical Biology of Hebei Province, College of Chemistry and Environmental Science (China)

    2016-05-15

    Yttrium oxide nanoparticles are an excellent host material for the rare earth metals and have high luminescence efficiency providing a potential application in photodynamic therapy and biological imaging. In this study, the effects of yttrium oxide nanoparticles with four different sizes were investigated using primary osteoblasts in vitro. The results demonstrated that the cytotoxicity generated by yttrium oxide nanoparticles depended on the particle size, and smaller particles possessed higher toxicological effects. For the purpose to elucidate the relationship between reactive oxygen species generation and cell damage, cytomembrane integrity, intracellular reactive oxygen species level, mitochondrial membrane potential, cell apoptosis rate, and activity of caspase-3 in cells were then measured. Increased reactive oxygen species level was also observed in a size-dependent way. Thus, our data demonstrated that exposure to yttrium oxide nanoparticles resulted in a size-dependent cytotoxicity in cultured primary osteoblasts, and reactive oxygen species generation should be one possible damage pathway for the toxicological effects produced by yttrium oxide particles. The results may provide useful information for more rational applications of yttrium oxide nanoparticles in the future.

  18. Studies for the yttrium determination by activation analysis, in the presence of lanthanides. Application of the substoichiometric technique

    International Nuclear Information System (INIS)

    Silva, D.I.T. da.

    1978-01-01

    Some methods using extraction chromatography for the separation of yttrium from the lanthanide elements were applied. The separation of yttrium was studied, using di-(2 ethylhexyl) orthophosphoric acid as stationary phase, Kieselguhr as support and HNO 3 of concentration between 4,5 and 5,0 N as the mobile phase. In these conditions, about 50% of pure yttrium was obtained. The substoichiometric technique was applied to the determination of yttrium. The elements was partially complexed and the Y 3 + ions were separated from the complex (EDTA-Y) - by means of a cationic resin. The sensitivity, precision and accuracy which can be expected in the analytical results were studied. The possibility of the analysis of a sample containing 1 part per million of yttrium with an error just above 8% was demonstrated. It was also shown that, admitting an error of 10%, it is possible to determine 60 parts per billion of yttrium [pt

  19. Determination of surface temperatures in combustion environments using thermographic phosphors; Wandtemperaturmessungen in Verbrennungsumgebungen mithilfe thermographischer Phosphore

    Energy Technology Data Exchange (ETDEWEB)

    Bruebach, J.; Kissel, T. [TU Darmstadt (Germany). FG Energie- und Kraftwerkstechnik; Dreizler, A. [TU Darmstadt (Germany). FG Reaktive Stroemungen und Messtechnik

    2009-07-01

    A phosphor thermometry system was characterised with regard to all sources of systematic errors. Exemplary, the point measurement of a surface temperature and the determination of wall-normal temperature gradients within an optically accessible combustion chamber are outlined. Furthermore, the temporal temperature characteristic at the quartz ring of an optically accessible engine is presented. (orig.)

  20. Uranium recovery from wet process phosphoric acid

    International Nuclear Information System (INIS)

    Carrington, O.F.; Pyrih, R.Z.; Rickard, R.S.

    1981-01-01

    Improvement in the process for recovering uranium from wetprocess phosphoric acid solution derived from the acidulation of uraniferous phosphate ores by the use of two ion exchange liquidliquid solvent extraction circuits in which in the first circuit (A) the uranium is reduced to the uranous form; (B) the uranous uranium is recovered by liquid-liquid solvent extraction using a mixture of mono- and di-(Alkyl-phenyl) esters of orthophosphoric acid as the ion exchange agent; and (C) the uranium oxidatively stripped from the agent with phosphoric acid containing an oxidizing agent to convert uranous to uranyl ions, and in the second circuit (D) recovering the uranyl uranium from the strip solution by liquid-liquid solvent extraction using di(2ethylhexyl)phosphoric acid in the presence of trioctylphosphine oxide as a synergist; (E) scrubbing the uranium loaded agent with water; (F) stripping the loaded agent with ammonium carbonate, and (G) calcining the formed ammonium uranyl carbonate to uranium oxide, the improvement comprising: (1) removing the organics from the raffinate of step (B) before recycling the raffinate to the wet-process plant, and returning the recovered organics to the circuit to substantially maintain the required balance between the mono and disubstituted esters; (2) using hydogren peroxide as the oxidizing agent in step (C); (3) using an alkali metal carbonate as the stripping agent in step (F) following by acidification of the strip solution with sulfuric acid; (4) using some of the acidified strip solution as the scrubbing agent in step (E) to remove phosphorus and other impurities; and (5) regenerating the alkali metal loaded agent from step (F) before recycling it to the second circuit

  1. Study of decomposition kinetics of volatile β-diketonates of yttrium, barium and copper in flow reactor

    International Nuclear Information System (INIS)

    Devyatykh, G.G.; Gavrishchuk, E.M.; Gibin, A.M.; Dadanov, A.Yu.; Dzyubenko, N.G.; Kaul', A.R.; Nichiporuk, R.V.; Snezhko, N.T.; Ul'yanov, A.A.

    1990-01-01

    Heterogeneous oxidative decomposition of adduct of yttrium acetylacetonate with o-phenanthroline, copper acetylacetonate and barium dipivaloylmethanate in a flow-type reactor was carried out. The basic kinetic characteristics of chemical precipitation processes of films of yttrium, copper and barium oxides, which are components of high-temperature superconductors, were obtained. The values of activation energy of precipitation process of yttrium, copper and barium oxides constituted 76±10, 108±15, 81±12 (t 600 deg C) respectively

  2. Concentration and wavelength dependent frequency downshifting photoluminescence from a Tb3+ doped yttria nano-phosphor: A photochromic phosphor

    Science.gov (United States)

    Yadav, Ram Sagar; Rai, Shyam Bahadur

    2018-03-01

    In this article, the Tb3+ doped Y2O3 nano-phosphor has been synthesized through solution combustion method. The structural measurements of the nano-phosphor have been carried out by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) techniques, which reveal nano-crystalline nature. The Fourier transform infrared (FTIR) measurements reveal the presence of different molecular species in the nano-phosphor. The UV-Vis-NIR absorption spectrum of the nano-phosphor shows large number of bands due to charge transfer band (CTB) and 4f-4f electronic transitions of Tb3+ ion. The Tb3+ doped Y2O3 nano-phosphor emits intense green downshifting photoluminescence centered at 543 nm due to 5D4 → 7F5 transition on excitation with 350 nm. The emission intensity of the nano-phosphor is optimized at 1.0 mol% concentration of Tb3+ ion. When the as-synthesized nano-phosphor is annealed at higher temperature the emission intensity of the nano-phosphor enhances upto 5 times. The enhancement in the emission intensity is due to an increase in crystallinity of the nano-phosphor, reduction in surface defects and optical quenching centers. The CIE diagram reveals that the Tb3+ doped nano-phosphor samples show the photochromic nature (color tunability) with a change in the concentration of Tb3+ ion and excitation wavelength. The lifetime measurement indicates an increase in the lifetime for the annealed sample. Thus, the Tb3+ doped Y2O3 nano-phosphor may be used in photochromic displays and photonic devices.

  3. Phosphor Scanner For Imaging X-Ray Diffraction

    Science.gov (United States)

    Carter, Daniel C.; Hecht, Diana L.; Witherow, William K.

    1992-01-01

    Improved optoelectronic scanning apparatus generates digitized image of x-ray image recorded in phosphor. Scanning fiber-optic probe supplies laser light stimulating luminescence in areas of phosphor exposed to x rays. Luminescence passes through probe and fiber to integrating sphere and photomultiplier. Sensitivity and resolution exceed previously available scanners. Intended for use in x-ray crystallography, medical radiography, and molecular biology.

  4. Analysis of phosphoric ore bacterial and eucaryal microbial diversity ...

    African Journals Online (AJOL)

    These findings provided new opportunities into phosphoric ore microbiology that could be useful in biological system removing waste gases generated from the phosphoric industry. Keywords: Microbial community, bacteria, archaea, eucarya, mining residue. African Journal of Biotechnology, Vol 13(30) 3023-3029 ...

  5. World wide IFC phosphoric acid fuel cell implementation

    Energy Technology Data Exchange (ETDEWEB)

    King, J.M. Jr

    1996-04-01

    International Fuel Cells, a subsidary of United technologies Corporation, is engaged in research and development of all types of fuel cell technologies and currently manufactures alkaline fuel cell power plants for the U.S. manned space flight program and natural gas fueled stationary power plants using phosphoric acid fuel cells. This paper describes the phosphoric acid fuel cell power plants.

  6. Separation of rare earths from solutions of phosphoric acid

    International Nuclear Information System (INIS)

    Jones, E.A.

    1977-01-01

    Rare earths are separated from 6M phosphoric acid by adsorption onto cation resin BIORAD AG50W-X8. The phosphoric acid is then washed from the column, and the rare earths are eluted with 4M hydrochloric acid

  7. Surface characterization of low-temperature grown yttrium oxide

    Science.gov (United States)

    Krawczyk, Mirosław; Lisowski, Wojciech; Pisarek, Marcin; Nikiforow, Kostiantyn; Jablonski, Aleksander

    2018-04-01

    The step-by-step growth of yttrium oxide layer was controlled in situ using X-ray photoelectron spectroscopy (XPS). The O/Y atomic concentration (AC) ratio in the surface layer of finally oxidized Y substrate was found to be equal to 1.48. The as-grown yttrium oxide layers were then analyzed ex situ using combination of Auger electron spectroscopy (AES), elastic-peak electron spectroscopy (EPES) and scanning electron microscopy (SEM) in order to characterize their surface chemical composition, electron transport phenomena and surface morphology. Prior to EPES measurements, the Y oxide surface was pre-sputtered by 3 kV argon ions, and the resulting AES-derived composition was found to be Y0.383O0.465C0.152 (O/Y AC ratio of 1.21). The SEM images revealed different surface morphology of sample before and after Ar sputtering. The oxide precipitates were observed on the top of un-sputtered Y oxide layer, whereas the oxide growth at the Ar ion-sputtered surface proceeded along defects lines normal to the layer plane. The inelastic mean free path (IMFP) characterizing electron transport was evaluated as a function of energy in the range of 0.5-2 keV from the EPES method. Two reference materials (Ni and Au) were used in these measurements. Experimental IMFPs determined for the Y0.383O0.465C0.152 and Y2O3 surface compositions, λ, were uncorrected for surface excitations and approximated by the simple function λ = kEp at electron energies E between 500 eV and 2000 eV, where k and p were fitted parameters. These values were also compared with IMFPs resulting from the TPP-2 M predictive equation for both oxide compositions. The fitted functions were found to be reasonably consistent with the measured and predicted IMFPs. In both cases, the average value of the mean percentage deviation from the fits varied between 5% and 37%. The IMFPs measured for Y0.383O0.465C0.152 surface composition were found to be similar to the IMFPs for Y2O3.

  8. Optimized conditions for chelation of yttrium-90-DOTA immunoconjugates.

    Science.gov (United States)

    Kukis, D L; DeNardo, S J; DeNardo, G L; O'Donnell, R T; Meares, C F

    1998-12-01

    Radioimmunotherapy (RIT) with 90Y-labeled immunoconjugates has shown promise in clinical trials. The macrocyclic chelating agent 1,4,7,10-tetraazacyclododecane-N,N',N",N"'-tetraacetic acid (DOTA) binds 90Y with extraordinary stability, minimizing the toxicity of 90Y-DOTA immunoconjugates arising from loss of 90Y to bone. However, reported 90Y-DOTA immunoconjugate product yields have been typically only BAD) was conjugated to the monoclonal antibody Lym-1 via 2-iminothiolane (2IT). The immunoconjugate product, 2IT-BAD-Lym-1, was labeled in excess yttrium in various buffers over a range of concentrations and pH. Kinetic studies were performed in selected buffers to estimate radiolabeling reaction times under prospective radiopharmacy labeling conditions. The effect of temperature on reaction kinetics was examined. Optimal radiolabeling conditions were identified and used in eight radiolabeling experiments with 2IT-BAD-Lym-1 and a second immunoconjugate, DOTA-peptide-chimeric L6, with 248-492 MBq (6.7-13.3 mCi) of 90Y. Ammonium acetate buffer (0.5 M) was associated with the highest uptake of yttrium. On the basis of kinetic data, the time required to chelate 94% of 90Y (four half-times) under prospective radiopharmacy labeling conditions in 0.5 M ammonium acetate was 17-148 min at pH 6.5, but it was only 1-10 min at pH 7.5. Raising the reaction temperature from 25 degrees C to 37 degrees C markedly increased the chelation rate. Optimal radiolabeling conditions were identified as: 30-min reaction time, 0.5 M ammonium acetate buffer, pH 7-7.5 and 37 degrees C. In eight labeling experiments under optimal conditions, a mean product yield (+/- s.d.) of 91%+/-8% was achieved, comparable to iodination yields. The specific activity of final products was 74-130 MBq (2.0-3.5 mCi) of 90Y per mg of monoclonal antibody. The immunoreactivity of 90Y-labeled immunoconjugates was 100%+/-11%. The optimization of 90Y-DOTA chelation conditions represents an important advance in 90Y RIT

  9. Treatment of persistent knee effusions with Yttrium 90

    International Nuclear Information System (INIS)

    Bouyoucef, S.E.; Drahmoune, R.; Mechken, F.; Amimour, A.; Hanni-Haddam, F.; Abtroun, F.; Sellah, M.; Mansouri, B.

    2002-01-01

    Yttrium 90 intra-articular injection is used in persisting active joint of the knee, where medication has failed to resolve chronic inflammation. The effective dose delivered to the synovia is linked to Y 90 activity and depends on the size of the joint space, the synovial structure and thickness and the inflammatory activity of the synovitis. The amount of the injected activity of Y90 was estimated according the volume effusion in 28 pathologic knee of 18 patients aged 18 years and more (mean age 46 years). All patients have persistent knee effusions and most of them have rheumatoid arthritis but others had ankylosing spondylitis, Behcet disease, psoriatic arthritis. According the radiological classification of Steinbrocker, 19 pathological knees were in stage 1, 5 in stage 2 and 4 in stage 3. The mean value of the monthly removed volume of the synovial liquid from the pathological knee was determined during the last month preceding the radiosynoviorthesis and four groups were identified: V0 no evidence of effusion liquid, 0 ml 100ml. The activity of Y 90 was estimated in order to obtain a total of 100 Gray in the envelope of 3 spherical phantoms with the same range of volume as defined above. The lowest activity of Y90, 111 MBq (3mCi) was determined for V0 according a mean value of standard sizes of knees. An activity of 18 MBq (0.5mCi) was added for each stage of 50 ml, so 129 MBq (3.5 mCi) for G1, 148 MBq (4 mCi) for G2 and 166 MBq (4.5 mCi) for G3. Efficacy of Y90 treatment was clinically assessed in all patients according to three parameters: pain, hydrarthrosis and range of joint movement at 1, 3, 6 and 12 months. The results were excellent in 13 knees and good in 9 and for most of them the efficacy of Y 90 was observed after 6 months. The results were less good in 3 knees but with an initial good evolution for all at 1 month. For 4 knees, the efficacy of Y 90 was bad. Although the small number of patients, these results show a high rate, 75%, of successful

  10. Photoluminescence of phosphors for PDP with VUV excitation

    International Nuclear Information System (INIS)

    Lu, H.-C.; Chen, H.-K.; Tseng, T.-Y.; Kuo, W.-L.; Alam, M.S.; Cheng, B.-M.

    2005-01-01

    In a plasma display panel (PDP) He-Xe or Ne-Xe gaseous mixtures are subjected to electric discharge between two glass panels, so to generate VUV light. Red, green and blue phosphors absorb this VUV radiation and re-radiate the energy as visible light to produce the colors that appear on the screen. The phosphor plays an important role in the working of a PDP. To improve the efficiency of phosphors, we have established a photoluminescence end station coupled to the beam line of a synchrotron to study the luminescence of PDP phosphors. This luminescence is analyzed with a 0.32 m monochromator having maximum resolution 0.04 nm, and is monitored with a photomultiplier tube operated in a photon-counting mode. Preliminary data demonstrate the powerful performance of this end-station for studying PDP phosphors

  11. Process for winning uranium from wet process phosphoric acid

    International Nuclear Information System (INIS)

    1980-01-01

    A process is described for winning uranium from wet process phosphoric acid by means of liquid-liquid extraction with organic phosphoric acid esters. The process is optimised by keeping the sulphate percentage in the phosphoric acid below 2% by weight, and preferably below 0.6% by weight, as compared to P 2 O 5 in the phosphoric acid. This is achieved by adding an excess of Ba and/or Ca carbonate or sulfide solution and filtering off the formed calcium and/or barium sulphate precipitates. Solid KClO 3 is then added to the filtrate to oxidise U 4+ to U 6+ . The normal extraction procedure using organic phosphoric esters as extraction liquid, can then be applied. (Th.P.)

  12. Thermal and Electrical Conductivity Measurements of CDA 510 Phosphor Bronze

    Science.gov (United States)

    Tuttle, James E.; Canavan, Edgar; DiPirro, Michael

    2009-01-01

    Many cryogenic systems use electrical cables containing phosphor bronze wire. While phosphor bronze's electrical and thermal conductivity values have been published, there is significant variation among different phosphor bronze formulations. The James Webb Space Telescope (JWST) will use several phosphor bronze wire harnesses containing a specific formulation (CDA 510, annealed temper). The heat conducted into the JWST instrument stage is dominated by these harnesses, and approximately half of the harness conductance is due to the phosphor bronze wires. Since the JWST radiators are expected to just keep the instruments at their operating temperature with limited cooling margin, it is important to know the thermal conductivity of the actual alloy being used. We describe an experiment which measured the electrical and thermal conductivity of this material between 4 and 295 Kelvin.

  13. Pretreatment of phosphoric acid of Annaba

    International Nuclear Information System (INIS)

    Kada, R.

    1990-03-01

    The most important step in the process of uranium recovery from phosphoric acid is the pretreatment operation. In this study, the adsorption of organic matters on activated carbon was carried out in a batch process and in a fixed bed column. First, the chemical and physical characterization of phosphoric acid, activated carbon and gypsum were performed. In addition, the organic matters were qualitatively analysed and a new and original quantitative method was experimented. Next, the various operating parameters such as agitation speed, granulometry, temperature, solid/liquid ratio, initial concentration, acid flowrate, and bed height were optimized. The experimental equilibrium isotherm was compared to the Langmuir, Freundlich, and Redlich-Peterson theoretical isotherms. It was noticed that the three models did not fit the experimental isotherm in the total concentration range. Thus, an original bilinear model was proposed. The influence of the operating conditions on the adsorption kinetics was also investigated. As a result of that, a new mathematical model was proposed to determine both the liquid and solid phases mass transfer and the solid phase diffusion coefficient. Finally, adsorption of organic matters on a fixed bed process allowed computation of the number of transfer units (NTU), the height of adsorption zone and the degree of saturation of activated carbon

  14. Enrichment of yttrium from rare earth concentrate by ammonium carbonate leaching and peroxide precipitation

    International Nuclear Information System (INIS)

    Vasconcellos, Mari E. de; Rocha, S.M.R. da; Pedreira, W.R.; Queiroz S, Carlos A. da; Abrao, Alcidio

    2006-01-01

    The rare earth elements (REE) solubility with ammonium carbonate vary progressively from element to element, the heavy rare earth elements (HRE) being more soluble than the light rare earth elements (LRE). Their solubility is function of the carbonate concentration and the kind of carbonate as sodium, potassium and ammonium. In this work, it is explored this ability of the carbonate for the dissolution of the REE and an easy separation of yttrium was achieved using the precipitation of the peroxide from complex yttrium carbonate. For this work is used a REE concentrate containing (%) Y 2 O 3 2.4, Dy 2 O 3 0.6, Gd 2 O 3 2.7, CeO 2 2.5, Nd 2 O 3 33.2, La 2 O 3 40.3, Sm 2 O 3 4.1 and Pr 6 O 11 7.5. The mentioned concentrate was produced industrially from the chemical treatment of monazite sand by NUCLEMON in Sao Paulo. The yttrium concentrate was treated with 200 g L -1 ammonium carbonate during 10 and 30 min at room temperature. The experiments indicated that a single leaching operation was sufficient to get a rich yttrium solution with about 60.3% Y 2 O 3 . In a second step, this yttrium solution was treated with an excess of hydrogen peroxide (130 volumes), cerium, praseodymium and neodymium peroxides being completely precipitated and separated from yttrium. Yttrium was recovered from the carbonate solution as the oxalate and finally as oxide. The final product is an 81% Y 2 O 3 . This separation envisages an industrial application. The work discussed the solubility of the REE using ammonium carbonate and the subsequent precipitation of the correspondent peroxides

  15. Impacts of yttrium substitution on FMR line-width and magnetic properties of nickel spinel ferrites

    Energy Technology Data Exchange (ETDEWEB)

    Ishaque, M., E-mail: ishaqdgk1@gmail.com [Department of Physics, Bahauddin Zakariya University, Multan 60800 (Pakistan); Khan, Muhammad Azhar, E-mail: azhar.khan@iub.edu.pk [Department of Physics, The Islamia University of Bahawalpur, Bahawalpur 63100 (Pakistan); Ali, Irshad; Khan, Hasan M. [Department of Physics, Bahauddin Zakariya University, Multan 60800 (Pakistan); Iqbal, M. Asif [Department of Physics, Bahauddin Zakariya University, Multan 60800 (Pakistan); College of E & ME, National University of Science and Technology, Islamabad (Pakistan); Islam, M.U. [Department of Physics, Bahauddin Zakariya University, Multan 60800 (Pakistan); Warsi, Muhammad Farooq [Department of Chemistry, The Islamia University of Bahawalpur, Bahawalpur 63100 (Pakistan)

    2015-05-15

    The influence of yttrium (Y) substitution on ferromagnetic resonance (FMR), initial permeability, and magnetic properties of NiFe{sub 2}O{sub 4} ferrites were investigated. It was observed that the FMR line-width decreases with yttrium contents for the substitution level 0≤×≤0.06. Beyond this, the FMR line-width increases with yttrium contents. The nominal composition NiY{sub 0.12}Fe{sub 1.88}O{sub 4} exhibited the smallest FMR line-width ~282 Oe. A significant change in FMR position of nickel–yttrium (Ni–Y) ferrites was observed and it found to exist between 4150 and 4600 Oe. The saturation magnetization was observed to decrease with the increase of yttrium contents and this was referred to the redistribution of cations on octahedral. The coercivity increased from 15 Oe to 59 Oe by increasing the yttrium concentration. The initial permeability decreased from 110 to 35 at 1 MHz by the incorporation of yttrium and this was attributed to the smaller grains which may obstruct the domain wall movement and impede the domain wall motion. The magnetic loss factors of substituted samples exhibit decreasing behavior in the frequency range 1 kHz to 10 MHz. The smaller FMR line-width and reduced magnetic loss factor of the investigated samples suggest the possible use of these materials in high frequency applications. - Highlights: • Influence of Y{sup 3+} substitution on the properties of nickel ferrites is investigated. • Very small FMR line-width (282 Oe) is exhibited by these substituted ferrites. • Fourfold increase in coercivity was observed for NiY{sub 0.24}Fe{sub 1.76}O{sub 4} ferrites.

  16. Modeling granular phosphor screens by Monte Carlo methods

    International Nuclear Information System (INIS)

    Liaparinos, Panagiotis F.; Kandarakis, Ioannis S.; Cavouras, Dionisis A.; Delis, Harry B.; Panayiotakis, George S.

    2006-01-01

    The intrinsic phosphor properties are of significant importance for the performance of phosphor screens used in medical imaging systems. In previous analytical-theoretical and Monte Carlo studies on granular phosphor materials, values of optical properties, and light interaction cross sections were found by fitting to experimental data. These values were then employed for the assessment of phosphor screen imaging performance. However, it was found that, depending on the experimental technique and fitting methodology, the optical parameters of a specific phosphor material varied within a wide range of values, i.e., variations of light scattering with respect to light absorption coefficients were often observed for the same phosphor material. In this study, x-ray and light transport within granular phosphor materials was studied by developing a computational model using Monte Carlo methods. The model was based on the intrinsic physical characteristics of the phosphor. Input values required to feed the model can be easily obtained from tabulated data. The complex refractive index was introduced and microscopic probabilities for light interactions were produced, using Mie scattering theory. Model validation was carried out by comparing model results on x-ray and light parameters (x-ray absorption, statistical fluctuations in the x-ray to light conversion process, number of emitted light photons, output light spatial distribution) with previous published experimental data on Gd 2 O 2 S:Tb phosphor material (Kodak Min-R screen). Results showed the dependence of the modulation transfer function (MTF) on phosphor grain size and material packing density. It was predicted that granular Gd 2 O 2 S:Tb screens of high packing density and small grain size may exhibit considerably better resolution and light emission properties than the conventional Gd 2 O 2 S:Tb screens, under similar conditions (x-ray incident energy, screen thickness)

  17. Tuning the diurnal natural daylight with phosphor converted white LED – Advent of new phosphor blend composition

    International Nuclear Information System (INIS)

    Kim, Yoon Hwa; Arunkumar, Paulraj; Park, Seung Hyok; Yoon, Ho Shin; Im, Won Bin

    2015-01-01

    Highlights: • Designed phosphor blend that mimics diurnal daylight for health benefits. • Developed new phosphor blend composition that mimics natural sunlight under near UV. • The phosphor blend also exhibits high CRI (≥90) under blue LED excitation. • Fabricated WLED exhibited ∼91% spectral resemblance with daylight at 4500 K. • While ∼39.2% spectral resemblance were observed for YAG:Ce 3+ at 4500 K. - Abstract: We demonstrate the feasibility of developing phosphor converted white LED (pc-WLED) that mimics diurnal natural daylight with the newly designed phosphor blend in the color temperature (CCT) 2700–6000 K for health benefits. Natural daylight (sunlight) spectrum possesses broad emission in the visible region and closely approximates black body radiator, with color rendition index (CRI) of 100 under wide CCT (2500–6500 K). Current white light LEDs although are efficient and durable, they are not broad enough compared to daylight. We report new phosphor blend based on Sr 3 MgSi 2 O 8 :Eu 2+ blue phosphor with broad emission and high CRI ≥ 96 under both near UV and blue excitation. The fabricated WLED has exhibited ∼91% spectral resemblance with natural daylight compared to 39.2% for YAG:Ce 3+ white LED at 4500 K. The developed phosphor blend tunes the spectrum in wider CCT and would be a prospective candidate for full spectrum daylight WLED

  18. Tuning the diurnal natural daylight with phosphor converted white LED – Advent of new phosphor blend composition

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Yoon Hwa [School of Materials Science and Engineering, Chonnam National University, 300, Yongbong-dong, Buk-gu, Gwangju 500-757 (Korea, Republic of); Research Institute, Force4 Corp., Daechon-dong, Buk-gu, Gwangju 500-470 (Korea, Republic of); Arunkumar, Paulraj [School of Materials Science and Engineering, Chonnam National University, 300, Yongbong-dong, Buk-gu, Gwangju 500-757 (Korea, Republic of); Park, Seung Hyok; Yoon, Ho Shin [Research Institute, Force4 Corp., Daechon-dong, Buk-gu, Gwangju 500-470 (Korea, Republic of); Im, Won Bin, E-mail: imwonbin@jnu.ac.kr [School of Materials Science and Engineering, Chonnam National University, 300, Yongbong-dong, Buk-gu, Gwangju 500-757 (Korea, Republic of)

    2015-03-15

    Highlights: • Designed phosphor blend that mimics diurnal daylight for health benefits. • Developed new phosphor blend composition that mimics natural sunlight under near UV. • The phosphor blend also exhibits high CRI (≥90) under blue LED excitation. • Fabricated WLED exhibited ∼91% spectral resemblance with daylight at 4500 K. • While ∼39.2% spectral resemblance were observed for YAG:Ce{sup 3+} at 4500 K. - Abstract: We demonstrate the feasibility of developing phosphor converted white LED (pc-WLED) that mimics diurnal natural daylight with the newly designed phosphor blend in the color temperature (CCT) 2700–6000 K for health benefits. Natural daylight (sunlight) spectrum possesses broad emission in the visible region and closely approximates black body radiator, with color rendition index (CRI) of 100 under wide CCT (2500–6500 K). Current white light LEDs although are efficient and durable, they are not broad enough compared to daylight. We report new phosphor blend based on Sr{sub 3}MgSi{sub 2}O{sub 8}:Eu{sup 2+} blue phosphor with broad emission and high CRI ≥ 96 under both near UV and blue excitation. The fabricated WLED has exhibited ∼91% spectral resemblance with natural daylight compared to 39.2% for YAG:Ce{sup 3+} white LED at 4500 K. The developed phosphor blend tunes the spectrum in wider CCT and would be a prospective candidate for full spectrum daylight WLED.

  19. MCrAlY bond coat with enhanced yttrium

    Science.gov (United States)

    Jablonski, Paul D.; Hawk, Jeffrey A.

    2016-08-30

    One or more embodiments relates to a method of producing an MCrAlY bond coat comprising an MCrAlY layer in contact with a Y--Al.sub.2O.sub.3 layer. The MCrAlY layer is comprised of a .gamma.-M solid solution, a .beta.-MAl intermetallic phase, and Y-type intermetallics. The Y--Al.sub.2O.sub.3 layer is comprised of Yttrium atoms coordinated with oxygen atoms comprising the Al.sub.2O.sub.3 lattice. The method comprises depositing an MCrAlY material on a substrate, applying an Y.sub.2O.sub.3 paste, and heating the substrate in a non-oxidizing atmosphere at a temperature between 400-1300.degree. C. for a time sufficient to generate the Y--Al.sub.2O.sub.3 layer. Both the MCrAlY layer and the Y--Al.sub.2O.sub.3 layer have a substantial absence of Y.sub.2O.sub.3, YAG, and YAP phases.

  20. A divalent rare earth oxide semiconductor: Yttrium monoxide

    Science.gov (United States)

    Kaminaga, Kenichi; Sei, Ryosuke; Hayashi, Kouichi; Happo, Naohisa; Tajiri, Hiroo; Oka, Daichi; Fukumura, Tomoteru; Hasegawa, Tetsuya

    Rare earth sesquioxides like Y2O3 are known as widegap insulators with the highly stable closed shell trivalent rare earth ions. On the other hand, rare earth monoxides such as YO have been recognized as gaseous phase, and only EuO and YbO were thermodynamically stable solid-phase rock salt monoxides. In this study, solid-phase rock salt yttrium monoxide, YO, was synthesized in a form of epitaxial thin film by pulsed laser deposition method. YO possesses unusual valence of Y2+ ([Kr] 4d1) . In contrast with Y2O3, YO was narrow gap semiconductor with dark-brown color. The electrical conductivity was tunable from 10-1 to 103 Ω-1 cm-1 by introducing oxygen vacancies as electron donor. Weak antilocalization behavior was observed indicating significant spin-orbit coupling owing to 4 d electron carrier. The absorption spectral shape implies the Mott-Hubbard insulator character of YO. Rare earth monoixdes will be new platform of functional oxides. This work was supported by JST-CREST, the Japan Society for the Promotion of Science (JSPS) with Grant-in-Aid for Scientific Research on Innovative Areas (Nos. 26105002 and 26105006), and Nanotechnology Platform (Project No.12024046) of MEXT, Japan.

  1. Optical properties of ytterbium-doped yttrium oxide ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Solomonov, V.I.; Maksimov, R.N. [Institute of Electrophysics UrB RAS, Amundsena 106, 620016 Ekaterinburg (Russian Federation); Ural Federal University Named After the First President of Russia B.N. Yeltsin, Mira 19, 620002 Ekaterinburg (Russian Federation); Osipov, V.V.; Shitov, V.A.; Lipchak, A.I. [Institute of Electrophysics UrB RAS, Amundsena 106, 620016 Ekaterinburg (Russian Federation)

    2017-05-15

    Ytterbium-doped yttrium oxide (Yb:Y{sub 2}O{sub 3}) transparent ceramics with different sintering additives (Lu{sub 2}O{sub 3}, Sc{sub 2}O{sub 3}, CeO{sub 2}, ZrO{sub 2}, or HfO{sub 2}) were fabricated using nanopowders produced by laser ablation. Transmission and photoluminescence spectra of the obtained ceramics were investigated at room temperature. Highest in-line transmittance was over 80% at the wavelength of 1060 nm for 2 mm thick Yb:Y{sub 2}O{sub 3} ceramics with zirconium and hafnium. Divalent Yb ions with the ground state electron configuration 4f{sup 13}6s were revealed. The absorption and emission bands caused by s <-> s transitions of these ions were observed in the IR spectral range of Yb{sup 3+} ions. The superposition of both Yb{sup 3+} and Yb{sup 2+} emission bands leads to an effective broadening of the whole luminescence band. (copyright 2016 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  2. Structural and dielectric properties of yttrium-substituted hydroxyapatites

    Energy Technology Data Exchange (ETDEWEB)

    Kaygili, Omer, E-mail: okaygili@firat.edu.tr [Department of Physics, Faculty of Science, Firat University, 23119 Elazig (Turkey); Dorozhkin, Sergey V. [Kudrinskaja sq. 1-155, 123242 Moscow (Russian Federation); Ates, Tankut [Department of Physics, Faculty of Science, Firat University, 23119 Elazig (Turkey); Canan Gursoy, N. [Department of Microbiology and Clinic Microbiology, Inonu University, 44280 Malatya (Turkey); Keser, Serhat [Department of Chemistry, Faculty of Science, Firat University, 23119 Elazig (Turkey); Yakuphanoglu, Fahrettin [Department of Physics, Faculty of Science, Firat University, 23119 Elazig (Turkey); Birkan Selçuk, A. [Technology Department, Saraykoy Nuclear Research and Training Centre, 06983 Ankara (Turkey)

    2015-02-01

    Hydroxyapatite (HAp) samples doped with 0, 2 and 4 at.% of yttrium (Y) were characterized using X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy attached with energy dispersive X-ray (EDX) spectroscopy, antimicrobial activity tests and dielectric studies. The hydroxyl groups observed in FTIR spectra confirmed the formation of HAp phase in the studied samples. The crystallite size, crystallinity degree and lattice parameters of the samples were changed with Y content. The volume of the unit cell was gradually decreased with the addition of Y. Undoped and Y-containing HAp samples were screened to determine their in vitro antimicrobial activities against the standard strains. It was found that no samples have any antimicrobial effect. The relative dielectric permittivity and dielectric loss are affected by Y content. While the alternating current conductivity increases with increasing frequency, it decreases with increasing Y content. - Highlights: • The lattice parameters and crystal size are affected by Y content. • The volume of the unit cell was gradually decreased with the addition of Y. • No samples have any antimicrobial effect. • The alternating current conductivity decreases with increasing Y content.

  3. High density Gd-substituted yttrium iron garnets by coprecipitation

    International Nuclear Information System (INIS)

    Lamastra, Francesca Romana; Bianco, Alessandra; Leonardi, Federica; Montesperelli, Giampiero; Nanni, Francesca; Gusmano, Gualtiero

    2008-01-01

    Gadolinium-substituted yttrium iron garnets are ferrite materials of primary importance in microwave engineering. Stoichiometric powders of nominal composition Y 2.6 Gd 0.4 Fe 5 O 12 (i.e. Fe/(Y + Gd) = 1.67) were prepared by reverse strike coprecipitation of metal nitrates. In order to investigate the influence of composition on phase formation, non-stoichiometric powders were also synthesised. On the basis of DTA/TGA analysis, dried coprecipitates were calcined between 600 deg. C and 1200 deg. C and then characterised by ICP, XRD and HT-XRD. Amorphous coprecipitates crystallise around 700 deg. C in cubic garnet phase along with small amounts of YFeO 3 and/or α-Fe 2 O 3 . Only iron-rich garnets, either pure or Gd-substituted, calcined at 1200 deg. C or above display a single-phase cubic garnet. According to thermal dilatometry results, calcined powders were sintered in air up to 1470 deg. C. The microstructure of sintered ceramics is made up of fine grains, the average size ranging between 3 μm and 13 μm. Density of sintered bodies ranged from 88% to 98%. Ferromagnetic resonance linewidth (ΔH -3dB ) ranged between 4352.9 A m -1 and 4392.7 A m -1 , depending on composition and microstructure

  4. Dielectronic satellites to the Ne-like yttrium resonance lines

    International Nuclear Information System (INIS)

    Osterheld, A.L.; Nilsen, J.; Khakhalin, S.Ya.; Faenov, A.Ya.; Pikuz, S.A.

    1996-01-01

    We present a detailed analysis of the spectrum of satellite transitions to the n=2-3 and n=2-4 Ne-like yttrium resonance lines. Satellite lines from the double excited 2s 2 2p 5 3l3l', 2s 2 2p 5 3l4l', 2s2p 6 3l3l' and 2s2p 6 3l4l' levels of Na-like Y as well as from 2s 2 2p 5 3l3l'3l '' and 2s2p 6 3l3l'3l '' levels of Mg-like Y were observed in spectra from a laser-produced plasma. The X-ray spectra were recorded with high spectral resolution λ/Δλ∼3500-5000 in the wavelength region of the n=2-3 Ne-like resonance lines and with λ/Δλ>1000 in the region of the n=2-4 Ne-like resonance lines. A total of more than 50 spectral features were identified, and their wavelengths were measured. A simple intensity model was developed, which agreed well with the measured spectra and assisted the line identification. The consistency of the model for different spectral regions demonstrates the potential of the Na-like and Mg-like satellite lines for diagnosing plasma conditions. (orig.)

  5. Phase Diagram for Magnon Condensate in Yttrium Iron Garnet Film

    Science.gov (United States)

    Li, Fuxiang; Saslow, Wayne M.; Pokrovsky, Valery L.

    2013-01-01

    Recently, magnons, which are quasiparticles describing the collective motion of spins, were found to undergo Bose-Einstein condensation (BEC) at room temperature in films of Yttrium Iron Garnet (YIG). Unlike other quasiparticle BEC systems, this system has a spectrum with two degenerate minima, which makes it possible for the system to have two condensates in momentum space. Recent Brillouin Light Scattering studies for a microwave-pumped YIG film of thickness d = 5 μm and field H = 1 kOe find a low-contrast interference pattern at the characteristic wavevector Q of the magnon energy minimum. In this report, we show that this modulation pattern can be quantitatively explained as due to unequal but coherent Bose-Einstein condensation of magnons into the two energy minima. Our theory predicts a transition from a high-contrast symmetric state to a low-contrast non-symmetric state on varying the d and H, and a new type of collective oscillation. PMID:23455849

  6. Few-MeV neutrons incident on yttrium

    International Nuclear Information System (INIS)

    Budtz-Jorgensen, C.; Guenther, P.; Smith, A.; Whalen, J.

    1982-09-01

    Neutron total and scattering cross sections of elemental yttrium are measured in the few-MeV region with broad resolutions. The total-cross section measurements extend from approx. = 0.5 to 4.2 MeV in steps of less than or equal to 0.1 MeV. Neutron elastic- and inelastic-scattering cross sections are measured from approx. = 1.5 to 4.0 MeV, at incident-neutron energy intervals of less than or equal to 50 keV and at ten or more scattering angles distributed between 20 and 160 deg. Inelastically-scattered neutron groups are observed corresponding to the excitation of levels at 909 +- 23, 1504 +- 20, 1747 +- 16, 2224 +- 16, 2567 +- 26, 2889 +- 12 and 3104 +- 10 keV. The experimental results are discussed in terms of the spherical optical-statistical, coupled-channels and core-coupling models and compared with corresponding quantities given in the evaluated nuclear data file ENDF/B-V

  7. Yttrium 90 microspheres for the treatment of hepatocellular carcinoma.

    Science.gov (United States)

    Memon, Khairuddin; Lewandowski, Robert J; Riaz, Ahsun; Salem, Riad

    2013-01-01

    Yttrium-90 microspheres are radioactive particles which are increasingly being employed for treating patients with unresectable hepatocellular carcinoma (HCC). The procedure is called radioembolization. It involves the injection of micron-sized embolic particles loaded with a radioisotope by use of transarterial techniques. Because of the sensitivity of liver parenchyma and relative insensitivity of tumor, external radiation has played a limited role in treating HCC. (90)Y administered via arterial route directs the highly concentrated radiation to the tumor while healthy liver parenchyma is relatively spared due to its preferential blood supply from portal venous blood. This technique has proven useful for the majority of patients with HCC as most of them present in advanced stage, beyond potentially curative options (resection/liver transplantation). (90)Y microspheres can be used in downstaging large tumors to bring within transplantable criteria, in patients with portal venous thrombosis due to tumor invasion and as palliative therapy. There are two available devices for (90)Y administration; TheraSphere® (glass based) and SIR-Spheres® (resin based). The procedure is performed on an outpatient basis. The incidence of complications is comparatively less and may include nausea, fatigue, abdominal pain, hepatic dysfunction, biliary injury, fibrosis, radiation pneumonitis, GI ulcers, and vascular injury; however, these can be avoided by meticulous pretreatment assessment, careful patient selection, and adequate dosimetry. This article explores the technical and clinical aspects of (90)Y radioembolization with keeping emphasis on patient selection, uses, and complications.

  8. Structural and dielectric properties of yttrium-substituted hydroxyapatites

    International Nuclear Information System (INIS)

    Kaygili, Omer; Dorozhkin, Sergey V.; Ates, Tankut; Canan Gursoy, N.; Keser, Serhat; Yakuphanoglu, Fahrettin; Birkan Selçuk, A.

    2015-01-01

    Hydroxyapatite (HAp) samples doped with 0, 2 and 4 at.% of yttrium (Y) were characterized using X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy attached with energy dispersive X-ray (EDX) spectroscopy, antimicrobial activity tests and dielectric studies. The hydroxyl groups observed in FTIR spectra confirmed the formation of HAp phase in the studied samples. The crystallite size, crystallinity degree and lattice parameters of the samples were changed with Y content. The volume of the unit cell was gradually decreased with the addition of Y. Undoped and Y-containing HAp samples were screened to determine their in vitro antimicrobial activities against the standard strains. It was found that no samples have any antimicrobial effect. The relative dielectric permittivity and dielectric loss are affected by Y content. While the alternating current conductivity increases with increasing frequency, it decreases with increasing Y content. - Highlights: • The lattice parameters and crystal size are affected by Y content. • The volume of the unit cell was gradually decreased with the addition of Y. • No samples have any antimicrobial effect. • The alternating current conductivity decreases with increasing Y content

  9. High Efficiency Colloidal Quantum Dot Phosphors

    Energy Technology Data Exchange (ETDEWEB)

    Kahen, Keith

    2013-12-31

    The project showed that non-Cd containing, InP-based nanocrystals (semiconductor materials with dimensions of ~6 nm) have high potential for enabling next-generation, nanocrystal-based, on chip phosphors for solid state lighting. Typical nanocrystals fall short of the requirements for on chip phosphors due to their loss of quantum efficiency under the operating conditions of LEDs, such as, high temperature (up to 150 °C) and high optical flux (up to 200 W/cm2). The InP-based nanocrystals invented during this project maintain high quantum efficiency (>80%) in polymer-based films under these operating conditions for emission wavelengths ranging from ~530 to 620 nm. These nanocrystals also show other desirable attributes, such as, lack of blinking (a common problem with nanocrystals which limits their performance) and no increase in the emission spectral width from room to 150 °C (emitters with narrower spectral widths enable higher efficiency LEDs). Prior to these nanocrystals, no nanocrystal system (regardless of nanocrystal type) showed this collection of properties; in fact, other nanocrystal systems are typically limited to showing only one desirable trait (such as high temperature stability) but being deficient in other properties (such as high flux stability). The project showed that one can reproducibly obtain these properties by generating a novel compositional structure inside of the nanomaterials; in addition, the project formulated an initial theoretical framework linking the compositional structure to the list of high performance optical properties. Over the course of the project, the synthetic methodology for producing the novel composition was evolved to enable the synthesis of these nanomaterials at a cost approximately equal to that required for forming typical conventional nanocrystals. Given the above results, the last major remaining step prior to scale up of the nanomaterials is to limit the oxidation of these materials during the tens of

  10. Hydrothermal synthesis and formation mechanism of hexagonal yttrium hydroxide fluoride nanobundles

    International Nuclear Information System (INIS)

    Tian, Li; Sun, QiLiang; Zhao, RuiNi; He, HuiLin; Xue, JianRong; Lin, Jun

    2013-01-01

    Graphical abstract: The formation of yttrium hydroxide fluorides nanobundles can be expressed as a precipitation transformation from cubic NaYF 4 to hexagonal NaYF 4 and to hexagonal Y(OH) 2.02 F 0.98 owing to ion exchange. - Highlights: • Novel Y(OH) 2.02 F 0.98 nanobundles have been successfully prepared by hydrothermal method. • The branched nanobundles composed of numerous oriented-attached nanoparticles has been studied. • The growth mechanism is proposed to be ion exchange and precipitation transformation. - Abstract: This article presents the fabrication of hexagonal yttrium hydroxide fluoride nanobundles via one-pot hydrothermal process, using yttrium nitrate, sodium hydroxide and ammonia fluoride as raw materials to react in propanetriol solvent. The X-ray diffraction pattern clearly reveals that the grown product is pure yttrium hydroxide fluoride, namely Y(OH) 2.02 F 0.98 . The morphology and microstructure of the synthesized product is testified to be nanobundles composed of numerous oriented-attached nanoparticles as observed from the field emission scanning electron microscopy (FESEM). The chemical composition was analyzed by the energy dispersive spectrum (EDS), confirming the phase transformation of the products which was clearly consistent with the result of XRD analysis. It is proposed that the growth of yttrium hydroxide fluoride nanobundles be attributed to ion exchange and precipitation transformation

  11. Development of 2024 AA-Yttrium composites by Spark Plasma Sintering

    Science.gov (United States)

    Vidyasagar, CH S.; Karunakar, D. B.

    2018-04-01

    The method of fabrication of MMNCs is quite a challenge, which includes advanced processing techniques like Spark Plasma Sintering (SPS), etc. The objective of the present work is to fabricate aluminium based MMNCs with the addition of small amounts of yttrium using Spark Plasma Sintering and to evaluate their mechanical and microstructure properties. Samples of 2024 AA with yttrium ranging from 0.1% to 0.5 wt% are fabricated by Spark Plasma Sintering (SPS). Hardness of the samples is determined using Vickers hardness testing machine. The metallurgical characterization of the samples is evaluated by Optical Microscopy (OM), Field Emission Scanning Electron Microscopy (FE-SEM). Unreinforced 2024 AA sample is also fabricated as a benchmark to compare its properties with those of the composite developed. It is found that the yttrium addition increases the above mentioned properties by altering the precipitation kinetics and intermetallic formation to some extent and then decreases gradually when yttrium wt% increases beyond 0.3 wt%. High density (˂ 99.75) is achieved in the samples and highest hardness achieved is 114 Hv, fabricated by spark plasma sintering and uniform distribution of yttrium is observed.

  12. Dependence of upconversion emission intensity on Yb3+ concentration in Er3+/Yb3+ co-doped flake shaped Y2(MoO4)3 phosphors

    International Nuclear Information System (INIS)

    Lu Weili; Cheng Lihong; Zhong Haiyang; Sun Jiashi; Wan Jing; Tian Yue; Chen Baojiu

    2010-01-01

    Yttrium molybdate phosphors with fixed Er 3+ and various Yb 3+ concentrations were synthesized via a co-precipitation method. The crystal structure and the morphology of the phosphor were characterized by means of x-ray diffraction and field-emission scanning electron microscopy. Under 980 nm excitation, red and green upconversion emissions centred at 660, 553 and 530 nm were observed. Quantitative analyses on the dependence of upconversion emission intensity on the working current of a laser diode (LD) indicated that two-photon processes are responsible for both red and green upconversion emissions in both cases of low and high Yb 3+ concentrations. The relationship between the emission intensity ratio of 2 H 11/2 → 4 I 15/2 to 4 S 3/2 → 4 I 15/2 and the working current of the LD was studied for the samples doped with low and high Yb 3+ concentrations. Finally, a set of rate equations was established based on the possible upconversion mechanism, and an empirical formula was proposed to describe the Yb 3+ concentration dependence of upconversion emission intensity; the empirical formula fits well with the experimental data.

  13. The quality study of recycled glass phosphor waste for LED

    Science.gov (United States)

    Tsai, Chun-Chin; Chen, Guan-Hao; Yue, Cheng-Feng; Chen, Cin-Fu; Cheng, Wood-Hi

    2017-02-01

    To study the feasibility and quality of recycled glass phosphor waste for LED packaging, the experiments were conducted to compare optical characteristics between fresh color conversion layer and that made of recycled waste. The fresh color conversion layer was fabricated through sintering pristine mixture of Y.A.G. powder [yellow phosphor (Y3AlO12 : Ce3+). Those recycled waste glass phosphor re-melted to form Secondary Molten Glass Phosphor (S.M.G.P.). The experiments on such low melting temperature glass results showed that transmission rates of S.M.G.P. are 9% higher than those of first-sintered glass phosphor, corresponding to 1.25% greater average bubble size and 36% more bubble coverage area in S.M.G.P. In the recent years, high power LED modules and laser projectors have been requiring higher thermal stability by using glass phosphor materials for light mixing. Nevertheless, phosphor and related materials are too expensive to expand their markets. It seems a right trend and research goal that recycling such waste of high thermal stability and quality materials could be preferably one of feasible cost-down solutions. This technical approach could bring out brighter future for solid lighting and light source module industries.

  14. Compact fluorescent lamp phosphors in accidental radiation monitoring

    International Nuclear Information System (INIS)

    Murthy, K. V. R.; Pallavi, S. P.; Ghildiyal, R.; Parmar, M. C.; Patel, Y. S.; Ravi Kumar, V.; Sai Prasad, A. S.; Natarajan, V.; Page, A. G.

    2006-01-01

    The application of lamp phosphors for accidental dosimetry is a new concept. Since the materials used in fluorescent lamps are good photo luminescent materials, if one can either use the inherent defects present in the phosphor or add suitable modifiers to induce thermoluminescence (TL) in these phosphors, then the device (fluorescent lamp) can be used as an accidental dosemeter. In continuation of our search for a suitable phosphor material, which can serve both as an efficient lamp phosphor and as a good radiation monitoring device, detailed examination has been carried out on cerium and terbium-doped lanthanum phosphate material. A 90 Sr beta source with 50 mCi strength (1.85 GBq) was used as the irradiation source for TL studies. The TL response as a function of dose received was examined for all phosphors used and it was observed that the intensity of the TL peak vs. dose received was a linear function in the dose range 0.1-200 Gy in each case. Incidentally LaPO 4 :Ce,Tb is a component of the compact fluorescent lamp marketed recently as an energy bright light source. Besides having very good luminescence efficiency, good dosimetric properties of these phosphors render them useful for their use in accidental dosimetry also. (authors)

  15. Radioactivity measurements using storage phosphor technology

    International Nuclear Information System (INIS)

    Cheng, Y.T.; Hwang, J.; Hutchinson, M.R.

    1995-01-01

    We propose to apply a recently developed charged particle radiation imaging concept in bio-medical research for fast, cost-effective characterization of radionuclides in contaminated sites and environmental samples. This concept utilizes sensors with storage photostimulable phosphor (SPP) technology as radiation detectors. They exhibit high sensitivity for all types of radiation and the response is linear over a wide dynamic range (>10 5 ), essential for quantitative analysis. These new sensors have an active area of up to 35 cm x 43 cm in size and a spatial resolution as fine as 50 μm. They offer considerable promise as large area detectors for fast characterization of radionuclides with an added ability to locate and identify hot spots

  16. Development of BaSO4:Eu thermoluminescence phosphor

    International Nuclear Information System (INIS)

    Madhusoodanan, U.; Jose, M.T.; Lakshmanan, A.R.

    1999-01-01

    A highly sensitive thermoluminescence (TL) phosphor based on BaSO 4 :Eu was developed following the coprecipitation technique and firing in argon atmosphere at 1123 K. Photoluminescence studies confirm that firing in argon atmosphere instead of air increased the incorporation of Eu ions in 2+ valence state. At low γ-ray doses, its TL sensitivity is nearly 2 to 3 times higher than that of CaSO 4 :Dy phosphor. The other salient features of this BaSO 4 :Eu TL phosphor are a constant glow curve shape and a nearly linear γ-ray dose response

  17. Development of BaSO sub 4 :Eu thermoluminescence phosphor

    CERN Document Server

    Madhusoodanan, U; Lakshmanan, A R

    1999-01-01

    A highly sensitive thermoluminescence (TL) phosphor based on BaSO sub 4 :Eu was developed following the coprecipitation technique and firing in argon atmosphere at 1123 K. Photoluminescence studies confirm that firing in argon atmosphere instead of air increased the incorporation of Eu ions in 2+ valence state. At low gamma-ray doses, its TL sensitivity is nearly 2 to 3 times higher than that of CaSO sub 4 :Dy phosphor. The other salient features of this BaSO sub 4 :Eu TL phosphor are a constant glow curve shape and a nearly linear gamma-ray dose response.

  18. Comparison between mixed and spatially separated remote phosphor fabricated via a screen-printing process

    Science.gov (United States)

    Kim, Byung-Ho; Hwang, Jonghee; Lee, Young Jin; Kim, Jin-Ho; Jeon, Dae-Woo; Lee, Mi Jai

    2016-08-01

    We developed a fabrication method for remote phosphor by a screen-printing process, using green phosphor, red phosphor, and thermally stable glass frit. The glass frit was introduced for long-term stability. The optical properties of the remote phosphor were observed via an integrating sphere; the photoluminescence spectrum dramatically changed on incorporating a minor amount of the red phosphor. These unique optical properties were elucidated using four factors: phosphor ratio, scattering induced by packing density, light intensity per unit volume, and reabsorption. The thermal stability of the remote phosphor was investigated at 500°C, demonstrating its outstanding thermal properties.

  19. Separation of Yttrium from Rare Earth Concentrates in Fractional Hydroxide Precipitation

    International Nuclear Information System (INIS)

    Tri Handini; Purwoto; Mulyono

    2007-01-01

    Yttrium has been separated from rare earth concentrates by precipitation in fractional hydroxide using urea. The purpose of this research is to increase the yttrium rate resulting from the sedimentary process through separation of yttrium from other rare earth in fractional hydroxide precipitation using urea. In this research, we study the process variable of the concentration of urea, the ratio of feed volume to condensation volume of urea, as well as the temperature. Determination analysis of the rare earth rate is conducted using an X-ray spectrometer. The best result Y=92.89 % is obtained at a concentration of urea of 50 %, a level of precipitation of 3 times, and a temperature of 80°C. (author)

  20. Fabrication of dense yttrium oxyfluoride ceramics by hot pressing and their mechanical, thermal, and electrical properties

    Science.gov (United States)

    Tahara, Ryuki; Tsunoura, Toru; Yoshida, Katsumi; Yano, Toyohiko; Kishi, Yukio

    2018-06-01

    Excellent corrosion-resistant materials have been strongly required to reduce particle contamination during the plasma process in semiconductor production. Yttrium oxyfluoride can be a candidate as highly corrosion-resistant material. In this study, three types of dense yttrium oxyfluoride ceramics with different oxygen contents, namely, YOF, Y5O4F7 and Y5O4F7 + YF3, were fabricated by hot pressing, and their mechanical, thermal, and electrical properties were evaluated. Y5O4F7 ceramics showed an excellent thermal stability up to 800 °C, a low loss factor, and volume resistivity comparable to conventional plasma-resistant oxides, such as Y2O3. From these results, yttrium oxyfluoride ceramics are strongly suggested to be used as electrostatic chucks in semiconductor production.

  1. Tribological effects of yttrium and nitrogen ion implantation on a precipitation hardening stainless steel

    International Nuclear Information System (INIS)

    Alonso, F.; Arizaga, A.; Garcia, A.; Onate, J.I.

    1994-01-01

    Yttrium, nitrogen and combined yttrium and nitrogen implantations have been carried out on an ASTM A286 precipitation hardening iron base alloy to evaluate the benefits in their tribological behaviour. Microindentation tests have shown a significant 20%-60% increment in hardness on the nitrogen implanted material, with a limited improvement in elastic recovery of the indentation. An abrasive test on the same material has also produced a 50% reduction in scratch depth. Y + and Y + +N + implantations also hardened the material but to a lesser extent. Reciprocating ball on disk friction and wear testing at 400 C resulted in very severe damage in all cases. X-ray photoelectron spectroscopy analyses combined with Ar sputtering have disclosed that nitrogen is mainly in a nitrided form, yttrium remains oxidized at the surface, below which there is an apparent increase in the metallic bond. ((orig.))

  2. Physicochemical analysis of cryocrystallization processes of aqueous solutions of yttrium, barium, copper nitrates and their mixtures

    International Nuclear Information System (INIS)

    Kulakov, A.B.; Mozhaev, A.P.; Tesker, A.M.; Churagulov, B.R.

    1992-01-01

    Products of fast hardening of aqueous solutions of different concentration of yttrium, barium copper nitrates and their mixtures including mixture of three nitrates with molar ratio equal to 1:2:3 used for synthesis of YBa 2 Cu 3 O 7-x HTSC by cryochemical technique, in liquid nitrogen, are studied using low-temperature, differential thermal and X-ray phase analyses. Aqueous solutions of barium, copper, yttrium nitrates are shown to belong to three different classes which differ in behaviour at fast cooling and subsequent slow heating. Cryogranulate at YBa 2 Cu 2 O 7-x synthesis using cryochemical technique represents mixture of X-ray amorphous Ba(NO 3 ) 2 , crystalline Cu(NO 3 ) 2 ·6H 2 O and ice, as well as, supercooled aqueous solution of yttrium and copper nitrates

  3. Fluorimetric determination of yttrium by methyl-bis(8-hydraxy--- 2-quinolyl)amine

    International Nuclear Information System (INIS)

    Golovina, A.P.; Kachin, S.V.; Runov, V.K.; Fakeeva, O.A.

    1982-01-01

    Using a method of mathematical Box-Wilson experiment planning the optimum conditions of yttrium fluorimetric determination by methyl-bis (8-hydroxy-2-quinolyl) amine (pH 7.5, csub(R)=1.4x10sup(-5) M) with the determination limit=0.05 μg/ml are found. An extraction-fluorimetric method of yttrium determination by methyl-bis (8-hydroxy-2-quinolyl) amine is developed. The extraction has been realized with aliphatic alcohols at pH > 11. The method is characteristic of the lowest determination limit (0.01 μg/ml) as compared with the known ones. The possibility is shown of yttrium determination in the presence of 5000-multiple aluminium contents, stoichiometric contents of La, Lu, Fe (3), U (6), tartrates, citrates

  4. Positive effect of yttrium on the reduction of pores in cast Al alloy

    International Nuclear Information System (INIS)

    Hua, Guomin; Ahmadi, Hojat; Nouri, Meisam; Li, Dongyang

    2015-01-01

    Mechanical and electrochemical properties of Al alloys can be improved by adding a small amount of rare-earth such as yttrium. Here we demonstrate that adding yttrium also helps suppress the porosity in cast Al alloys, thus minimizing its detrimental effect on mechanical properties of the alloys. The mechanism behind is elucidated based on the hydrogen binding energies and the diffusion activation energies of hydrogen atoms in Al and Al–Y phases, calculated using the first-principle method. - Highlights: • The porosity of commercial Al alloy can be reduced by additive yttrium. • Formed Al 3 Y phase helps reduce homogeneous nucleation of hydrogen bubbles. • Formed Al 3 Y and Al 2 Y phases could suppress the growth of hydrogen bubbles

  5. Root Cause Analysis of Gastroduodenal Ulceration After Yttrium-90 Radioembolization

    Energy Technology Data Exchange (ETDEWEB)

    Lam, Marnix G. E. H. [Stanford University School of Medicine, Division of Interventional Radiology (United States); Banerjee, Subhas [Stanford University School of Medicine, Division of Gastroenterology and Hepatology (United States); Louie, John D.; Abdelmaksoud, Mohamed H. K. [Stanford University School of Medicine, Division of Interventional Radiology (United States); Iagaru, Andrei H. [Stanford University School of Medicine, Division of Nuclear Medicine and Molecular Imaging (United States); Ennen, Rebecca E.; Sze, Daniel Y., E-mail: dansze@stanford.edu [Stanford University School of Medicine, Division of Interventional Radiology (United States)

    2013-12-15

    IntroductionA root cause analysis was performed on the occurrence of gastroduodenal ulceration after hepatic radioembolization (RE). We aimed to identify the risk factors in the treated population and to determine the specific mechanism of nontarget RE in individual cases. Methods: The records of 247 consecutive patients treated with yttrium-90 RE for primary (n = 90) or metastatic (n = 157) liver cancer using either resin (n = 181) or glass (n = 66) microspheres were reviewed. All patients who developed a biopsy-proven microsphere-induced gastroduodenal ulcer were identified. Univariate and multivariate analyses were performed on baseline parameters and procedural data to determine possible risk factors in the total population. Individual cases were analyzed to ascertain the specific cause, including identification of the culprit vessel(s) leading to extrahepatic deposition of the microspheres. Results: Eight patients (3.2 %) developed a gastroduodenal ulcer. Stasis during injection was the strongest independent risk factor (p = 0.004), followed by distal origin of the gastroduodenal artery (p = 0.004), young age (p = 0.040), and proximal injection of the microspheres (p = 0.043). Prolonged administrations, pain during administration, whole liver treatment, and use of resin microspheres also showed interrelated trends in multivariate analysis. Retrospective review of intraprocedural and postprocedural imaging showed a probable or possible culprit vessel, each a tiny complex collateral vessel, in seven patients. Conclusion: Proximal administrations and those resulting in stasis of flow presented increased risk for gastroduodenal ulceration. Patients who had undergone bevacizumab therapy were at high risk for developing stasis.

  6. Effects of yttrium 90 on experimental allergic arthritis in rabbits

    International Nuclear Information System (INIS)

    Meier-Ruge, W.; Mueller, W.; Pavelka, K.

    1976-01-01

    Fifteen weeks after allergic arthritis developed in the knee joint of 17 immunized rabbits, 8 animals were given an injection of 200 μCi yttrium 90( 90 Y) into the left joint cavity and 7 were injected with 400 μCi. The animals were sacrificed at 2, 4, 8, 12, and 16 weeks, and at 6 to 12 months after the injection. Two uninjected animals used as morphological controls were sacrificed 13 weeks after immunization, and showed allergic arthritis had progressed to severe inflammation of the knee joint marked by massive round-cell infiltration, oedema, and proliferation of synovial mesothelium in the synovial villi and joint capsule. Treatment with 90 Y was effective 2 weeks after injection and the disappearance of inflammatory odema and marked regression of round-cell infiltration. This was accompanied by degeneration of the synovial mesothelium and fibrosis of the subsynovial tissue and synovial vessels as a secondary effect of the radiation. In the animals with severe allergic arthritis, the healing effects of 90 Y were more marked than the secondary effects of the radiation which were dose-dependent. Treatment with 90 Y of arthritic knee joints with the lowest effective dose of the isotope - if necessay with repeated application - seems justified. A single large dose does not have a greater therapeutic effect and causes more radiation damage to the joint. In view of the possible secondary effects in the joint, the indication for 90 Y therapy should be restricted, particularly in young patients, to cases of chronic relapsing arthritis unresponsive to other treatment. (U.K.)

  7. Planar gamma camera imaging and quantitation of Yttrium-90 bremsstrahlung

    International Nuclear Information System (INIS)

    Shen, S.; DeNardo, G.L.; Yuan, A.

    1994-01-01

    Yttrium-90 is a promising radionuclide for radioimmunotherapy of cancer because of its energetic beta emissions. Therapeutic management requires quantitative imaging to assess the pharmacokinetics and radiation dosimetry of the 90 Y-labeled antibody. Conventional gamma photon imaging methods cannot be easily applied to imaging of 90 Y-bremsstrahlung because of its continuous energy spectrum. The sensitivity, resolution and source-to-background signal ratio (S/B) of the detector system for 90 Y-bremsstrahlung were investigated for various collimators and energy windows in order to determine optimum conditions for quantitative imaging. After these conditions were determined, the accuracy of quantitation of 90 Y activity in an Alderson abdominal phantom was examined. When the energy-window width was increased, the benefit of increased sensitivity outweighed degradation in resolution and S/B ratio until the manufacturer's energy specifications for the collimator were exceeded. Using the same energy window, the authors improved resolution and S/B for the medium-energy (ME) collimator when compared to the low-energy, all-purpose (LEAP) collimator, and there was little additional improvement using the high-energy (HE) collimator. Camera sensitivity under tissue equivalent conditions was 4.2 times greater for the LEAP and 1.7 times greater for the ME collimators when compared to the HE collimator. Thus, the best, most practical selections were found to be the ME collimator and an energy window of 55-285 keV. When they used these optimal conditions for image acquisition, the estimation of 90 Y activity in organs and tumors was within 15% of the true activities. The results for this study suggest that reasonable accuracy can be achieved in clinical radioimmunotherapy using 90 Y-bremsstrahlung quantitation. 28 refs., 5 figs., 7 tabs

  8. Hanford isotope project strategic business analysis yttrium-90 (Y-90)

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    1995-10-01

    The purpose of this analysis is to address the short-term direction for the Hanford yttrium-90 (Y-90) project. Hanford is the sole DOE producer of Y-90, and is the largest repository for its source in this country. The production of Y-90 is part of the DOE Isotope Production and Distribution (IP and D) mission. The Y-90 is ``milked`` from strontium-90 (Sr-90), a byproduct of the previous Hanford missions. The use of Sr-90 to produce Y-90 could help reduce the amount of waste material processed and the related costs incurred by the clean-up mission, while providing medical and economic benefits. The cost of producing Y-90 is being subsidized by DOE-IP and D due to its use for research, and resultant low production level. It is possible that the sales of Y-90 could produce full cost recovery within two to three years, at two curies per week. Preliminary projections place the demand at between 20,000 and 50,000 curies per year within the next ten years, assuming FDA approval of one or more of the current therapies now in clinical trials. This level of production would incentivize private firms to commercialize the operation, and allow the government to recover some of its sunk costs. There are a number of potential barriers to the success of the Y-90 project, outside the control of the Hanford Site. The key issues include: efficacy, Food and Drug Administration (FDA) approval and medical community acceptance. There are at least three other sources for Y-90 available to the US users, but they appear to have limited resources to produce the isotope. Several companies have communicated interest in entering into agreements with Hanford for the processing and distribution of Y-90, including some of the major pharmaceutical firms in this country.

  9. Hanford isotope project strategic business analysis yttrium-90 (Y-90)

    International Nuclear Information System (INIS)

    1995-10-01

    The purpose of this analysis is to address the short-term direction for the Hanford yttrium-90 (Y-90) project. Hanford is the sole DOE producer of Y-90, and is the largest repository for its source in this country. The production of Y-90 is part of the DOE Isotope Production and Distribution (IP and D) mission. The Y-90 is ''milked'' from strontium-90 (Sr-90), a byproduct of the previous Hanford missions. The use of Sr-90 to produce Y-90 could help reduce the amount of waste material processed and the related costs incurred by the clean-up mission, while providing medical and economic benefits. The cost of producing Y-90 is being subsidized by DOE-IP and D due to its use for research, and resultant low production level. It is possible that the sales of Y-90 could produce full cost recovery within two to three years, at two curies per week. Preliminary projections place the demand at between 20,000 and 50,000 curies per year within the next ten years, assuming FDA approval of one or more of the current therapies now in clinical trials. This level of production would incentivize private firms to commercialize the operation, and allow the government to recover some of its sunk costs. There are a number of potential barriers to the success of the Y-90 project, outside the control of the Hanford Site. The key issues include: efficacy, Food and Drug Administration (FDA) approval and medical community acceptance. There are at least three other sources for Y-90 available to the US users, but they appear to have limited resources to produce the isotope. Several companies have communicated interest in entering into agreements with Hanford for the processing and distribution of Y-90, including some of the major pharmaceutical firms in this country

  10. Yttrium bismuth titanate pyrochlore mixed oxides for photocatalytic hydrogen production

    Energy Technology Data Exchange (ETDEWEB)

    Merka, Oliver

    2012-10-18

    In this work, the sol-gel synthesis of new non-stoichiometric pyrochlore titanates and their application in photocatalytic hydrogen production is reported. Visible light response is achieved by introducing bismuth on the A site or by doping the B site by transition metal cations featuring partially filled d orbitals. This work clearly focusses on atomic scale structural changes induced by the systematical introduction of non-stoichiometry in pyrochlore mixed oxides and the resulting influence on the activity in photocatalytic hydrogen production. The materials were characterized in detail regarding their optical properties and their atomic structure. The pyrochlore structure tolerates tremendous stoichiometry variations. The non-stoichiometry in A{sub 2}O{sub 3} rich compositions is compensated by distortions in the cationic sub-lattice for the smaller Y{sup 3+} cation and by evolution of a secondary phase for the larger Bi{sup 3+} cation on the A site. For TiO{sub 2} rich compositions, the non-stoichiometry leads to a special vacancy formation in the A and optionally O' sites. It is shown that pyrochlore mixed oxides in the yttrium bismuth titanate system represent very active and promising materials for photocatalytic hydrogen production, if precisely and carefully tuned. Whereas Y{sub 2}Ti{sub 2}O{sub 7} yields stable hydrogen production rates over time, the bismuth richer compounds of YBiTi{sub 2}O{sub 7} and Bi{sub 2}Ti{sub 2}O{sub 7} are found to be not stable under irradiation. This drawback is overcome by applying a special co-catalyst system consisting of a precious metal core and a Cr{sub 2}O{sub 3} shell on the photocatalysts.

  11. Treatment of persistent knee synovitis with Yttrium 90

    International Nuclear Information System (INIS)

    Bouyoucef, S.E.

    2007-01-01

    Full text: Management of persistent knee synovitis includes both systemic and local articular treatment relevant to specific etiology. Local treatment may involve attempts to control inflammation and pain in knee joints by intra articular application of analgesics or glucocorticoids. However, in many patients these fail to reduce significantly the synovitis phenomenon and moreover they may lead to severe side effects. Radiosynoviorthesis with Y90 has been in use for many years in several joint pathologies. Indications of Radiosynoviorthesis include various inflammatory and degenerative diseases and its use should be envisaged when other conservative methods have failed like intra articular injections of long acting corticosteroids. Persistent knee synovitis is defined by the presence of hydrops in the joint or functional impairment with warmth, pain and local signs and symptoms requiring intra articular injection of glucocorticoids. In this study, 151 knees with persistent knee synovitis have been treated with Y 90 and have had all a minimum of one year follow up. Many parameters have been identified to measure efficiency of the RSO including pain, hydarthrosis, mobility, as well as global perception of the patients. Excellent and good responses have been appreciated through pain at rest, pain at stress, volume of effusion, and articular mobility. Results showed that percentage of excellent and good response is superior to 80% at three and six months. Success of Y 90 appears to be higher for rheumatoid arthritis as well as for oligoarthritis. Whatever the etiology, intensity of the inflammatory process appears one the major parameters which could better predict the outcomes of yttrium 90 in persistent knee synovitis. (author)

  12. Root Cause Analysis of Gastroduodenal Ulceration After Yttrium-90 Radioembolization

    International Nuclear Information System (INIS)

    Lam, Marnix G. E. H.; Banerjee, Subhas; Louie, John D.; Abdelmaksoud, Mohamed H. K.; Iagaru, Andrei H.; Ennen, Rebecca E.; Sze, Daniel Y.

    2013-01-01

    IntroductionA root cause analysis was performed on the occurrence of gastroduodenal ulceration after hepatic radioembolization (RE). We aimed to identify the risk factors in the treated population and to determine the specific mechanism of nontarget RE in individual cases. Methods: The records of 247 consecutive patients treated with yttrium-90 RE for primary (n = 90) or metastatic (n = 157) liver cancer using either resin (n = 181) or glass (n = 66) microspheres were reviewed. All patients who developed a biopsy-proven microsphere-induced gastroduodenal ulcer were identified. Univariate and multivariate analyses were performed on baseline parameters and procedural data to determine possible risk factors in the total population. Individual cases were analyzed to ascertain the specific cause, including identification of the culprit vessel(s) leading to extrahepatic deposition of the microspheres. Results: Eight patients (3.2 %) developed a gastroduodenal ulcer. Stasis during injection was the strongest independent risk factor (p = 0.004), followed by distal origin of the gastroduodenal artery (p = 0.004), young age (p = 0.040), and proximal injection of the microspheres (p = 0.043). Prolonged administrations, pain during administration, whole liver treatment, and use of resin microspheres also showed interrelated trends in multivariate analysis. Retrospective review of intraprocedural and postprocedural imaging showed a probable or possible culprit vessel, each a tiny complex collateral vessel, in seven patients. Conclusion: Proximal administrations and those resulting in stasis of flow presented increased risk for gastroduodenal ulceration. Patients who had undergone bevacizumab therapy were at high risk for developing stasis

  13. Effects of yttrium 90 on experimental allergic arthritis in rabbits

    Energy Technology Data Exchange (ETDEWEB)

    Meier-Ruge, W [Sandoz A.G., Basel (Switzerland); Mueller, W; Pavelka, K

    1976-02-01

    Fifteen weeks after allergic arthritis developed in the knee joint of 17 immunized rabbits, 8 animals were given an injection of 200 ..mu..Ci yttrium 90(/sup 90/Y) into the left joint cavity and 7 were injected with 400 ..mu..Ci. The animals were sacrificed at 2, 4, 8, 12, and 16 weeks, and at 6 to 12 months after the injection. Two uninjected animals used as morphological controls were sacrificed 13 weeks after immunization, and showed allergic arthritis had progressed to severe inflammation of the knee joint marked by massive round-cell infiltration, oedema, and proliferation of synovial mesothelium in the synovial villi and joint capsule. Treatment with /sup 90/Y was effective 2 weeks after injection and the disappearance of inflammatory odema and marked regression of round-cell infiltration. This was accompanied by degeneration of the synovial mesothelium and fibrosis of the subsynovial tissue and synovial vessels as a secondary effect of the radiation. In the animals with severe allergic arthritis, the healing effects of /sup 90/Y were more marked than the secondary effects of the radiation which were dose-dependent. Treatment with /sup 90/Y of arthritic knee joints with the lowest effective dose of the isotope - if necessay with repeated application - seems justified. A single large dose does not have a greater therapeutic effect and causes more radiation damage to the joint. In view of the possible secondary effects in the joint, the indication for /sup 90/Y therapy should be restricted, particularly in young patients, to cases of chronic relapsing arthritis unresponsive to other treatment.

  14. Dielectronic satellites to the Ne-like yttrium resonance lines

    Energy Technology Data Exchange (ETDEWEB)

    Osterheld, A.L. [Lawrence Livermore National Lab., CA (United States); Nilsen, J. [Lawrence Livermore National Lab., CA (United States); Khakhalin, S.Ya. [MISDC, VNIIFTRI, Mendeleevo (Russian Federation); Faenov, A.Ya. [MISDC, VNIIFTRI, Mendeleevo (Russian Federation); Pikuz, S.A. [Rossijskaya Akademiya Nauk, Moscow (Russian Federation). Fizicheskij Inst.

    1996-09-01

    We present a detailed analysis of the spectrum of satellite transitions to the n=2-3 and n=2-4 Ne-like yttrium resonance lines. Satellite lines from the double excited 2s{sup 2}2p{sup 5}3l3l`, 2s{sup 2}2p{sup 5}3l4l`, 2s2p{sup 6}3l3l` and 2s2p{sup 6}3l4l` levels of Na-like Y as well as from 2s{sup 2}2p{sup 5}3l3l`3l{sup ``} and 2s2p{sup 6}3l3l`3l{sup ``} levels of Mg-like Y were observed in spectra from a laser-produced plasma. The X-ray spectra were recorded with high spectral resolution {lambda}/{Delta}{lambda}{approx}3500-5000 in the wavelength region of the n=2-3 Ne-like resonance lines and with {lambda}/{Delta}{lambda}>1000 in the region of the n=2-4 Ne-like resonance lines. A total of more than 50 spectral features were identified, and their wavelengths were measured. A simple intensity model was developed, which agreed well with the measured spectra and assisted the line identification. The consistency of the model for different spectral regions demonstrates the potential of the Na-like and Mg-like satellite lines for diagnosing plasma conditions. (orig.).

  15. Spectrophotometric determination of yttrium with 2-(2-thiazolylazo)-5-dimethylaminophenol

    International Nuclear Information System (INIS)

    Tsurumi, Chikao; Furuya, Keiichi.

    1975-01-01

    Spectrophotometric determination of small amounts of yttrium with 2-(2-thiazolylazo)-5-dimethylaminophenol (TAM) in the presence of zephiramine was investigated. The recommended procedures were as follows; 2.0 ml of water, 7.0 ml of TAM-methanolic solution (2x10 -4 mol/l) and 2.0 ml of zephiramine-aqueous solution (1x10 -2 mol/l) were added to a solution containing less than 35 μg of yttrium and its pH was adjusted to 8.0 with 0.1 mol/l ammonium chloride-0.1 mol/l ammonium hydroxide solution. The solution was transferred to a 25 ml volumetric flask and diluted to the mark with water. After 20 minutes, the absorbance at 575 nm against a reagent blank was measured. The color of yttrium-TAM complex is reddish-violet in the presence of zephiramine and is stable for 90 minutes after color development. The yttrium-TAM complex shows an absorption maximum at 575 nm. The absorbance at 575 nm is constant in a pH range from 7.5 to 8.3. The molar extinction coefficient at this wavelength is 7.2x10 4 l.mol -1 .cm -1 . The band obeys Beer's law up to the concentration of 1.4 μg/ml of yttrium. The molar ratio of yttrium to TAM in the complex is 1 : 2. A number of ions interfere with the determination can be masked by the addition of various masking agents and removed in terms of trioctylamine-xylene extraction. Manganese, tantalum, tin(II), citrate and tartrate ions interfere with the determination. (auth.)

  16. Synthesis design of Y3Al5O12: Ce3+ phosphor for fabrication of ceramic converter in automotive application

    Science.gov (United States)

    Kwon, Seok Bin; Choi, Seung Hee; Yoo, Jung Hyeon; Jeong, Seong Guk; Song, Young Hyun; Yoon, Dae Ho

    2018-06-01

    A cellulose-assisted, liquid-phase precursor (LPP) was used to synthesize a YAG phosphor radiating near 530 nm with a particle size of 400 nm, which may be implemented in many applications. The mixture of the materials was homogeneous, and the cellulose-assisted LPP method involved a liquid-phase reaction at a lower temperature compared to a solid-state reaction (SSR). The reaction was performed at 1200, 1300 and 1400 °C, and the composition ratio of the samples was controlled based on yttrium (L1: 2.7, L2: 2.8, L3: 2.9, L4: 2.95, and L5: 3.1 M). ∼400 nm particles were obtained at 1200 °C and ∼1 μm at 1300 °C. At 1200 °C, the PL intensity was the highest in the Y3.1Al5O12 sample. At 1300 and 1400 °C, the strongest intensity was evident in the Y2.9Al5O12 sample. The XRD patterns for all temperatures showed a YAG phase in JCPDS.

  17. Optical bistability in erbium-doped yttrium aluminum garnet crystal combined with a laser diode.

    Science.gov (United States)

    Maeda, Y

    1994-01-10

    Optical bistability was observed in a simple structure of an injection laser diode combined with an erbium-doped yttrium aluminum garnet crystal. Since a hysteresis characteristic exists in the relationship between the wavelength and the injection current of a laser diode, an optical memory function capable of holding the output status is confirmed. In addition, an optical signal inversion was caused by the decrease of transmission of the erbium-doped yttrium aluminum garnet crystal against the red shift (principally mode hopping) of the laser diode. It is suggested that the switching time of this phenomenon is the time necessary for a mode hopping by current injection.

  18. Ultrasonic measurements and other allied parameters of yttrium soaps in mixed organic solvents

    International Nuclear Information System (INIS)

    Mehrotra, K.N.; Tandon, K.

    1990-01-01

    The ultrasonic measurements of yttrium soaps were made in a mixture of 70 % benzene and 30 % dimethylsulfoxide (ν/ν) to determine the critical micelle concentration, soap-solvent interaction and various acoustic and thermodynamic parameters. The values of the CMC decrease with increasing chainlength of fatty acid constituent of the soap molecule and are in agreement with the values obtained from other micellar properties. The various acoustic parameters (intermolecular freelength, adiabatic compressibility, apparent molar compressibility, specific acoustic impedance, apparent molar volume, molar sound velocity, solvation number, available volume and relative association) for yttrium soaps (myristate, palmitate, stearate and oleate) have been evaluated by ultrasonic velocity measurements. (Authors)

  19. Method of growing yttrium aluminate and/or lanthanide single crystals with perovskite structure

    International Nuclear Information System (INIS)

    Kvapil, Jiri; Perner, B.; Kvapil, Josef; Blazek, K.

    1989-01-01

    Single crystals of yttrium aluminate and/or lanthanide with perovskite structure are grown from melt in a vacuum at a pressure of gas residues of max. 0.01 Pa. The melt contains 1±0.05 gram-ions of aluminium per gram-ion of yttrium and/or lanthanides. The single crystals are then heated in a vacuum (0.01 Pa) at temperatures of 1,450 to 1,800 degC for 2 to 3 hours. (B.S.)

  20. Elaboration and characterisation of yttrium oxide and hafnium oxide powders by the sol-gel process

    International Nuclear Information System (INIS)

    Hours, T.

    1988-01-01

    The two classical sol-gel processes, colloidal and polymeric are studied for the preparation of yttrium oxide and hafnium oxide high performance powders. In the colloidal process, controlled and reproducible conditions for the preparation of yttrium oxide and hafnium oxide sols from salts or alkoxides are developed and the hydrothermal synthesis monodisperse hafnium oxide colloids is studied. The polymeric process is studied with hafnium ethyl-hexylate, hydrolysis kinetics for controlled preparation of sols and gels is investigated. Each step of preparation is detailed and powders obtained are characterized [fr

  1. Separation coefficients of liquid-vapor in systems formed by yttrium chloride with some impurities

    International Nuclear Information System (INIS)

    Volkov, V.T.; Nikiforova, T.V.; Nisel'son, L.A.; Telegin, G.F.

    1990-01-01

    Using equilibrium Rayleigh distillation in the 800-950 deg C temperature range, separation coefficients of liquid-vapor for systems, formed by yttrium chloride with Co, Cr, Ni, Mn, Fe, Cu, Na, K, Mg, Ca, Li impurities are determined. The impurity concentration lies within 0.02-0.4 mass. % limits of each impurity, and total impurity concentration does not exceed 1 mass. %. The tested impurities, except for calcium, are more volatile than the base, yttrium trichloride. In most systems negative deviation from the Raoult's law is observed

  2. Lack of rise in serum prolactin following yttrium-90 interstitial irradiation for acromegaly

    International Nuclear Information System (INIS)

    Clark, A.J.L.; Chahal, P.; Mashiter, K.; Joplin, G.F.

    1983-01-01

    The authors have investigated the possibility that the increase in serum PRL levels observed in patients with acromegaly treated with external irradiation could be due to damage to the hypothalamus or portal vessels, by comparing the effects of yttrium-90 interstitial irradiation, which is highly localised and does not normally extend to the hypothalamus, in a similar series of patients. These results are consistent with the hypothesis; a less likely explanation is that an overgrowth of radio-resistant PRL-secreting tumour cells is occurring after external irradiation, but not after yttrium-90 implantation. (author)

  3. Lack of rise in serum prolactin following yttrium-90 interstitial irradiation for acromegaly

    Energy Technology Data Exchange (ETDEWEB)

    Clark, A.J.L.; Chahal, P.; Mashiter, K.; Joplin, G.F. (Royal Postgraduate Medical School, London (UK))

    1983-11-01

    The authors have investigated the possibility that the increase in serum PRL levels observed in patients with acromegaly treated with external irradiation could be due to damage to the hypothalamus or portal vessels, by comparing the effects of yttrium-90 interstitial irradiation, which is highly localised and does not normally extend to the hypothalamus, in a similar series of patients. These results are consistent with the hypothesis; a less likely explanation is that an overgrowth of radio-resistant PRL-secreting tumour cells is occurring after external irradiation, but not after yttrium-90 implantation.

  4. Analysis of phosphoric ore bacterial and eucaryal microbial diversity ...

    African Journals Online (AJOL)

    SAM

    Received 30 July, 2013; Accepted 4 July, 2014. The aim ... using the single strand conformation polymorphism (SSCP) technique and ... Phosphoric industry generates a considerable quantity of ..... This phenomenon could well be the case for.

  5. The preparation of 32P labelled phosphorous acid

    International Nuclear Information System (INIS)

    Henderson, D.; Jenkinson, A.; Sorby, P.

    1986-11-01

    Phosphorous acid labelled with 32 P has been prepared, on a small scale, starting from neutron-irradiated phosphorus. The compound is intended for tracer studies in the development of novel fungicides

  6. Oxycarbonitride phosphors and light emitting devices using the same

    Science.gov (United States)

    Li, Yuanqiang; Romanelli, Michael Dennis; Tian, Yongchi

    2013-10-08

    Disclosed herein is a novel family of oxycarbidonitride phosphor compositions and light emitting devices incorporating the same. Within the sextant system of M--Al--Si--O--N--C--Ln and quintuplet system of M--Si--O--N--C--Ln (M=alkaline earth element, Ln=rare earth element), the phosphors are composed of either one single crystalline phase or two crystalline phases with high chemical and thermal stability. In certain embodiments, the disclosed phosphor of silicon oxycarbidonitrides emits green light at wavelength between 530-550 nm. In further embodiments, the disclosed phosphor compositions emit blue-green to yellow light in a wavelength range of 450-650 nm under near-UV and blue light excitation.

  7. Quantitative Characterization of Phosphor Detector for Fusion Plasmas

    International Nuclear Information System (INIS)

    Baciero, A.; Zurro, B.; McCarthy, K. J.

    2004-01-01

    Experiments made to characterize phosphor screens with application as broadband radiation detectors, are described. Several radiation sources, covering the spectral range between the ultraviolet and X ray, were used. In addition, details are given of three original phosphor-screen-based detectors that were designed for use as broadband detectors in magnetically confined fusion devices. The first measurements obtained with these detectors in plasmas created in the TJ-II stellarator device are presented together with the analysis performed. (Author)

  8. Study on stability of labeled yttrium-90 with lipiodol by chemical extraction for liver cancer

    International Nuclear Information System (INIS)

    Mu, P.Y.; Jiang, X.L.; Chen, J.; Zhu, Y.J.

    2005-01-01

    Liver cancer, particularly hepatocellular carcinoma, is one of the most common malignant diseases in many developed and developing countries. It is also one of the most common diseases endangering the people's lives and health heavily. Surgery is very effective in early-stage patients. Unfortunately, there is less than 10% of the patients with hepatocellular carcinoma fitting for surgical therapy. Instead of surgical therapy, other methods are considered for patients in whom surgery may not work well. Systemic administration of chemotherapeutic agents is not often considered in liver cancer patients, due to discouraging result and adverse side effects. Also, hepatocellular carcinoma is not keen on usual radioactive therapy. However, method of inner interventional radioactive nuclide is a potential way to cure liver tumors. Hepatocellular carcinoma would be cured with inner interventional radioactive nuclide, which is a hot topic in experimental research on hepatocellular carcinoma at home and abroad. The purpose of the study is to label Yttrium-90 with lipiodol by means of the chemical extraction method and research the stability of labeled Yttrium-90 ( 90 Y-P204-Lipiodol) in serum of a newly-born cattle and human's blood. We chose to label steady yttrium with lipiodol, because radioactive yttrium has great nuclear character for liver cancer, yttrium-90 can eradiate pure β radial, and it's half time is 64 hours. Average energy of it is 0.93 Mev, the highest energy is 2.27 Mev. Yttrium-90 can be labeled with lipiodol by means of the chemical extraction method, which is mature in chemical techniques, combined with method of radioactive nuclide labeled in. nuclear medicine. At first, yttrium-90 is extracted in certain condition(pH, temperature, whisk time, whisk frequency, etc ) after adding yttrium-90 solution. We use some distilled water to balance the labeled organic phase twice, and test the stability of labeled yttrium-90 in serum of a newly-born cattle and

  9. High temperature thermometric phosphors for use in a temperature sensor

    Science.gov (United States)

    Allison, Stephen W.; Cates, Michael R.; Boatner, Lynn A.; Gillies, George T.

    1998-01-01

    A high temperature phosphor consists essentially of a material having the general formula LuPO.sub.4 :Dy.sub.(x),Eu.sub.(y), wherein: 0.1 wt %.ltoreq.x.ltoreq.20 wt % and 0.1 wt %.ltoreq.y.ltoreq.20 wt %. The high temperature phosphor is in contact with an article whose temperature is to be determined. The article having the phosphor in contact with it is placed in the environment for which the temperature of the article is to be determined. The phosphor is excited by a laser causing the phosphor to fluoresce. The emission from the phosphor is optically focused into a beam-splitting mirror which separates the emission into two separate emissions, the emission caused by the dysprosium dopant and the emission caused by the europium dopent. The separated emissions are optically filtered and the intensities of the emission are detected and measured. The ratio of the intensity of each emission is determined and the temperature of the article is calculated from the ratio of the intensities of the separate emissions.

  10. Light Converting Inorganic Phosphors for White Light-Emitting Diodes

    Directory of Open Access Journals (Sweden)

    Chiao-Wen Yeh

    2010-03-01

    Full Text Available White light-emitting diodes (WLEDs have matched the emission efficiency of florescent lights and will rapidly spread as light source for homes and offices in the next 5 to 10 years. WLEDs provide a light element having a semiconductor light emitting layer (blue or near-ultraviolet (nUV LEDs and photoluminescence phosphors. These solid-state LED lamps, rather than organic light emitting diode (OLED or polymer light-emitting diode (PLED, have a number of advantages over conventional incandescent bulbs and halogen lamps, such as high efficiency to convert electrical energy into light, reliability and long operating lifetime. To meet with the further requirement of high color rendering index, warm light with low color temperature, high thermal stability and higher energy efficiency for WLEDs, new phosphors that can absorb excitation energy from blue or nUV LEDs and generate visible emissions efficiently are desired. The criteria of choosing the best phosphors, for blue (450-480 nm and nUV (380-400 nm LEDs, strongly depends on the absorption and emission of the phosphors. Moreover, the balance of light between the emission from blue-nUV LEDs and the emissions from phosphors (such as yellow from Y3Al5O12:Ce3+ is important to obtain white light with proper color rendering index and color temperature. Here, we will review the status of phosphors for LEDs and prospect the future development.

  11. Light Converting Inorganic Phosphors for White Light-Emitting Diodes

    Science.gov (United States)

    Chen, Lei; Lin, Chun-Che; Yeh, Chiao-Wen; Liu, Ru-Shi

    2010-01-01

    White light-emitting diodes (WLEDs) have matched the emission efficiency of florescent lights and will rapidly spread as light source for homes and offices in the next 5 to 10 years. WLEDs provide a light element having a semiconductor light emitting layer (blue or near-ultraviolet (nUV) LEDs) and photoluminescence phosphors. These solid-state LED lamps, rather than organic light emitting diode (OLED) or polymer light-emitting diode (PLED), have a number of advantages over conventional incandescent bulbs and halogen lamps, such as high efficiency to convert electrical energy into light, reliability and long operating lifetime. To meet with the further requirement of high color rendering index, warm light with low color temperature, high thermal stability and higher energy efficiency for WLEDs, new phosphors that can absorb excitation energy from blue or nUV LEDs and generate visible emissions efficiently are desired. The criteria of choosing the best phosphors, for blue (450−480 nm) and nUV (380−400 nm) LEDs, strongly depends on the absorption and emission of the phosphors. Moreover, the balance of light between the emission from blue-nUV LEDs and the emissions from phosphors (such as yellow from Y3Al5O12:Ce3+) is important to obtain white light with proper color rendering index and color temperature. Here, we will review the status of phosphors for LEDs and prospect the future development.

  12. Angle-resolved photoluminescence spectrum of a uniform phosphor layer

    Science.gov (United States)

    Fujieda, Ichiro; Ohta, Masamichi

    2017-10-01

    A photoluminescence spectrum depends on an emission angle due to self-absorption in a phosphor material. Assuming isotropic initial emission and Lambert-Beer's law, we have derived simple expressions for the angle-resolved spectra emerging from the top and bottom surfaces of a uniform phosphor layer. The transmittance of an excitation light through the phosphor layer can be regarded as a design parameter. For a strongly-absorbing phosphor layer, the forward flux is less intense and more red-shifted than the backward flux. The red-shift is enhanced as the emission direction deviates away from the plane normal. When we increase the transmittance, the backward flux decreases monotonically. The forward flux peaks at a certain transmittance value. The two fluxes become similar to each other for a weakly-absorbing phosphor layer. We have observed these behaviors in experiment. In a practical application, self-absorption decreases the efficiency of conversion and results in angle-dependent variations in chromaticity coordinates. A patterned phosphor layer with a secondary optical element such as a remote reflector alleviates these problems.

  13. Rare-earth doped phosphors: oldies or goldies?

    International Nuclear Information System (INIS)

    Moine, B.; Bizarri, G.

    2003-01-01

    The scientific research on phosphors has a long history starting more than 100 years ago. But recently the appearance of new kinds of displays and lighting devices (plasma display, fluorescent lamp without mercury, etc.) induced an increase of the research of new phosphors with better luminous efficiency than those available up to now. It has been shown that the behavior of 'classical' phosphors in a plasma display panel is quite different than in a cathode ray tube and that the vacuum ultraviolet (VUV) excitation process has to be studied with care in order to improve the phosphors efficiency. That is particularly true in PDPs. It is well established now that a good phosphor for electronic or ultraviolet excitation is not necessarily a good choice for excitation in VUV. This is probably due to the fact that the excitation process is very different in that case and also because the penetration depth of the VUV photons is extremely small inducing a large contribution of the surface of the phosphor. We will illustrate this with some examples. Methods to accelerate luminous intensity decrease under VUV excitation will be described. Low efficiency, fast aging process are both drawbacks that can be solved only in the framework of fundamental studies. Quantum cutting emission may be a solution for the first one but no satisfactory process was proposed for the moment to solve the second

  14. Technique of proton and phosphorous MR spectroscopy; Technik der Protonen- und Phosphor-MR-Spektroskopie

    Energy Technology Data Exchange (ETDEWEB)

    Backens, M. [Universitaetsklinikum des Saarlandes, Klinik fuer Diagnostische und Interventionelle Neuroradiologie, Homburg/Saar (Germany)

    2017-06-15

    Magnetic resonance spectroscopy (MRS) is an important non-invasive method that can reveal the concentration and spatial distribution of particular biochemically relevant tissue metabolites. Proton MRS is routinely applicable in the clinical setting providing good quality results even with a moderate magnetic field strength of 1.5 T. Relative values of metabolite concentrations are mostly used for the assessment of metabolic disorders. Absolute quantification of metabolites can be achieved by means of internal or external reference scans. Phosphorous MRS extends the range of detectable molecules to energy and cell membrane metabolism. The lower detection limit of metabolite concentrations is in the range of some mmol/kg. Depending on the magnetic field strength, MRS enables a spatial resolution of a few milliliters. The use of phosphorous MRS is considerably limited because higher field strengths of at least 3.0 T and additional expensive hardware for signal processing are required. (orig.) [German] Die MR-Spektroskopie (MRS) ist eine wichtige nichtinvasive Untersuchungsmethode, die Konzentration und raeumliche Verteilung einiger biochemisch relevanter Metaboliten im Gewebe ermitteln kann. Die Protonenspektroskopie ist klinisch etabliert, in der Routine einfach durchfuehrbar und liefert bereits bei einer Magnetfeldstaerke von 1,5 T qualitativ gute Ergebnisse. Fuer die Beurteilung von Stoffwechselveraenderungen werden Metabolitenkonzentrationen meist als Relativwerte angegeben. Mithilfe interner oder externer Referenzmessungen sind auch absolute Metabolitenkonzentrationen berechenbar. Die Phosphorspektroskopie erweitert den Bereich der detektierbaren Molekuele auf den Energie- und Zellmembranstoffwechsel. Die minimale nachweisbare Metabolitenkonzentration liegt bei einigen mmol/kg. Abhaengig von der Magnetfeldstaerke ist eine raeumliche Aufloesung der MRS von wenigen Millilitern erreichbar. Der Einsatz der Phosphor-MRS wird dadurch erheblich eingeschraenkt, dass sie

  15. Preparation of high purification and food grade phosphoric acid from technical grade phosphoric acid by liquid-liquid detraction method

    International Nuclear Information System (INIS)

    Alimoradi, M.; Borji, F.; Kishani, A.

    2002-01-01

    Pay attention to increasing consumption of high purification and food grade phosphoric acid in various industries and food industries and on in on hand and lack of preparation between production and distribution of this products its purification is so vital. In this article of liquid-liquid extraction method with normal hexane-mixture of ammonia and acetone-diisopropyl alcohol and normal butanol solvents and these determination of distribution coefficient each one with ph-me try titration we can evaluate effectiveness and sufficiency each one. Because of proper coefficient distribution and its local production of normal butanol solvent and low price is the best solvent. To phosphoric acid modifying coefficient distribution for extraction of phosphoric acid we can add a little value sulfuric acid to the mixture and to remove flouride impurity we add a little Na 2 O. After extraction stage extracted phosphoric acid in the normal strips by evaluating with distilled water and then by passing the carbon active bed and following passes of cationic resine column and concentrated with vacuum distillation. Conclusion of this article is produce of phosphoric acid 85% w/w and food grade from impure phosphoric acid 52% w/w with technical grade

  16. Study of phosphors determination in biological samples

    International Nuclear Information System (INIS)

    Oliveira, Rosangela Magda de.

    1994-01-01

    In this paper, phosphors determination by neutron activation analysis in milk and bone samples was studied employing both instrumental and radiochemical separation methods. The analysis with radiochemistry separation consisted of the simultaneous irradiation of the samples and standards during 30 minutes, dissolution of the samples, hold back carrier, addition precipitation of phosphorus with ammonium phosphomolibdate (A.M.P.) and phosphorus-32 by counting by using Geiger-Mueller detector. The instrumental analysis consisted of the simultaneous irradiation of the samples and standards during 30 minutes, transfer of the samples into a counting planchet and measurement of the beta radiation emitted by phosphorus-32, after a suitable decay period. After the phosphorus analysis methods were established they were applied to both commercial milk and animal bone samples, and data obtained in the instrumental and radiochemical separation methods for each sample, were compared between themselves. In this work, it became possible to obtain analysis methods for phosphorus that can be applied independently of the sample quantity available, and the phosphorus content in the samples or interference that can be present in them. (author). 51 refs., 7 figs., 4 tabs

  17. Phosphoric acid fuel cell platinum use study

    Science.gov (United States)

    Lundblad, H. L.

    1983-05-01

    The U.S. Department of Energy is promoting the private development of phosphoric acid fuel cell (PAFC) power plants for terrestrial applications. Current PAFC technology utilizes platinum as catalysts in the power electrodes. The possible repercussions that the platinum demand of PAFC power plant commercialization will have on the worldwide supply and price of platinum from the outset of commercialization to the year 2000 are investigated. The platinum demand of PAFC commercialization is estimated by developing forecasts of platinum use per unit of generating capacity and penetration of PAFC power plants into the electric generation market. The ability of the platinum supply market to meet future demands is gauged by assessing the size of platinum reserves and the capability of platinum producers to extract, refine and market sufficient quantities of these reserves. The size and timing of platinum price shifts induced by the added demand of PAFC commercialization are investigated by several analytical methods. Estimates of these price shifts are then used to calculate the subsequent effects on PAFC power plant capital costs.

  18. Separation of yttrium from strontium in the aqueous phase of the water/nitrobenzene system

    Czech Academy of Sciences Publication Activity Database

    Vaňura, P.; Makrlík, E.; Vobecký, Miloslav

    2002-01-01

    Roč. 253, č. 1 (2002), s. 171-172 ISSN 0236-5731 Institutional research plan: CEZ:AV0Z4031919 Keywords : stroncium * yttrium * separation Subject RIV: CB - Analytical Chemistry, Separation Impact factor: 0.502, year: 2002

  19. Separation of microamounts of yttrium from strontium in the two-phase water/nitrobenzene system

    Czech Academy of Sciences Publication Activity Database

    Makrlík, E.; Vaňura, P.; Vobecký, Miloslav

    2002-01-01

    Roč. 253, č. 1 (2002), s. 153-155 ISSN 0236-5731 Institutional research plan: CEZ:AV0Z4031919 Keywords : separation * stroncium * yttrium Subject RIV: CB - Analytical Chemistry, Separation Impact factor: 0.502, year: 2002

  20. Separation of yttrium from strontium in the aqueous phase of the water/nitrobenzene extraction system

    Czech Academy of Sciences Publication Activity Database

    Vaňura, P.; Makrlík, E.; Vobecký, Miloslav

    2003-01-01

    Roč. 256, č. 1 (2003), s. 171-172 ISSN 0236-5731 R&D Projects: GA MŠk LN00B084 Institutional research plan: CEZ:AV0Z4031919; CEZ:MSM 230000009 Keywords : extraction * strontium * yttrium Subject RIV: CB - Analytical Chemistry, Separation Impact factor: 0.472, year: 2003

  1. Reaction scheme of partial oxidation of methane to synthesis gas over yttrium-stabilized zirconia

    NARCIS (Netherlands)

    Zhu, J.J.; van Ommen, J.G.; Lefferts, Leonardus

    2004-01-01

    The partial oxidation of methane to synthesis gas over yttrium-stabilized zirconia (YSZ) was studied with in situ FTIR and both steady-state and transient experiments. The four major products, CO, H2, CO2, and H2O, are primary products of CPOM over YSZ. Besides these major products and traces of

  2. Adducts compounds of lanthanides (III) trifluoreacetates and yttrium and the N,N - dimenthylformamide

    International Nuclear Information System (INIS)

    Silva, M. das G. da.

    1983-01-01

    Some studies on lanthanides, f transition elements, and yttrium are presented. Adducts of lanthanides trifluoroacetates and N,N -dimethylformamide are described. The characterization of complexes from elementar analysis, conductance measurements, X-ray patterns, vibrational, electronics and fluorescence spectra are analysed. (M.J.C.) [pt

  3. Yttrium deposition on mesoporous TiO2: textural design and UV ...

    Indian Academy of Sciences (India)

    The mesoporous yttrium-doped TiO2 substrates prepared in this research work operate ... bond lengths in the nanoparticles (0.192 and 0.196 nm).18. Additionally ...... Fisicoquímica de Materiales Mesoporosos' (UAM-I CA-31. Fisicoquímica de ...

  4. Monte carlo simulations of Yttrium reaction rates in Quinta uranium target

    Directory of Open Access Journals (Sweden)

    Suchopár M.

    2017-01-01

    Full Text Available The international collaboration Energy and Transmutation of Radioactive Waste (E&T RAW performed intensive studies of several simple accelerator-driven system (ADS setups consisting of lead, uranium and graphite which were irradiated by relativistic proton and deuteron beams in the past years at the Joint Institute for Nuclear Research (JINR in Dubna, Russia. The most recent setup called Quinta, consisting of natural uranium target-blanket and lead shielding, was irradiated by deuteron beams in the energy range between 1 and 8 GeV in three accelerator runs at JINR Nuclotron in 2011 and 2012 with yttrium samples among others inserted inside the setup to measure the neutron flux in various places. Suitable activation detectors serve as one of possible tools for monitoring of proton and deuteron beams and for measurements of neutron field distribution in ADS studies. Yttrium is one of such suitable materials for monitoring of high energy neutrons. Various threshold reactions can be observed in yttrium samples. The yields of isotopes produced in the samples were determined using the activation method. Monte Carlo simulations of the reaction rates leading to production of different isotopes were performed in the MCNPX transport code and compared with the experimental results obtained from the yttrium samples.

  5. Structural differences of half-sandwich complexes of scandium and yttrium containing bulky substituents

    Czech Academy of Sciences Publication Activity Database

    Fridrichová, Adéla; Růžička, A.; Lamač, Martin; Horáček, Michal

    2017-01-01

    Roč. 76, FEB 2017 (2017), s. 62-66 ISSN 1387-7003 R&D Projects: GA ČR(CZ) GAP207/12/2368 Institutional support: RVO:61388955 Keywords : scandium * yttrium * half-sandwich Subject RIV: CF - Physical ; Theoretical Chemistry OBOR OECD: Physical chemistry Impact factor: 1.640, year: 2016

  6. Monte carlo simulations of Yttrium reaction rates in Quinta uranium target

    Science.gov (United States)

    Suchopár, M.; Wagner, V.; Svoboda, O.; Vrzalová, J.; Chudoba, P.; Tichý, P.; Kugler, A.; Adam, J.; Závorka, L.; Baldin, A.; Furman, W.; Kadykov, M.; Khushvaktov, J.; Solnyshkin, A.; Tsoupko-Sitnikov, V.; Tyutyunnikov, S.; Bielewicz, M.; Kilim, S.; Strugalska-Gola, E.; Szuta, M.

    2017-03-01

    The international collaboration Energy and Transmutation of Radioactive Waste (E&T RAW) performed intensive studies of several simple accelerator-driven system (ADS) setups consisting of lead, uranium and graphite which were irradiated by relativistic proton and deuteron beams in the past years at the Joint Institute for Nuclear Research (JINR) in Dubna, Russia. The most recent setup called Quinta, consisting of natural uranium target-blanket and lead shielding, was irradiated by deuteron beams in the energy range between 1 and 8 GeV in three accelerator runs at JINR Nuclotron in 2011 and 2012 with yttrium samples among others inserted inside the setup to measure the neutron flux in various places. Suitable activation detectors serve as one of possible tools for monitoring of proton and deuteron beams and for measurements of neutron field distribution in ADS studies. Yttrium is one of such suitable materials for monitoring of high energy neutrons. Various threshold reactions can be observed in yttrium samples. The yields of isotopes produced in the samples were determined using the activation method. Monte Carlo simulations of the reaction rates leading to production of different isotopes were performed in the MCNPX transport code and compared with the experimental results obtained from the yttrium samples.

  7. Influence of neodymium-doping on structure and properties of yttrium aluminium garnet

    DEFF Research Database (Denmark)

    Zhang, X.D.; He, W.; Yue, Yuanzheng

    2013-01-01

    We study the impact of the Nd-doping on the grain formation, the crystal structure, and the fluorescence of the Yttrium Aluminum Garnet (YAG). The results show that Nd-doping leads to the YAG lattice expansion and distortion, and hence to an increase in defect concentration. This is attributed to...

  8. Thermal decomposition of double selenates of lanthanides (III), yttrium (III) and ammonium

    International Nuclear Information System (INIS)

    Crespi, M.S.

    1989-01-01

    Double selenates of lanthanides, yttrium and ammonium were prepared by treating mixtures of simple selenates with equimolar amounts and then dried in a vacuum desiccator containing anhydrous calcium chloride, protected from light. The compounds were studied using the conventional analytical methods such as infrared absorption spectra, X-ray diffraction, differential thermal analysis (DTA), and thermogravimetry (TG). (author)

  9. Optimization of the personnel radiation protection during the treatment by antibodies labelled by yttrium 90

    International Nuclear Information System (INIS)

    Legrand, J.; Prangere, T.; Cougnenc, O.; Leleu, C.; Huglo, D.; Morschhauser, F.

    2007-01-01

    Beyond the acquired experience limiting the exposure time, measures of adequate radiation protection allow to reduce the doses of surface received to extremities by the personnel participating to the preparation of treatments by antibodies labelled by yttrium 90. (N.C.)

  10. High-pressure structural study of yttrium monochalcogenides from experiment and theory

    DEFF Research Database (Denmark)

    Vaitheeswaran, G.; Kanchana, V.; Svane, A.

    2011-01-01

    High-pressure powder x-ray diffraction experiments using synchrotron radiation are performed on the yttrium monochalcogenides YS, YSe, and YTe up to a maximum pressure of 23 GPa. The ambient NaCl structure is stable throughout the pressure range covered. The bulk moduli are determined to be 93, 82...

  11. Separation and purification of gadolinium and others rare earths, and yttrium

    International Nuclear Information System (INIS)

    Awwal, M.A.; Filgueiras, S.A.C.

    1988-01-01

    The experimental works in laboratories for developing a solvent extraction process with the purpose of gadolinium separation and purification, and secondarily samarium, europium, lanthanum and yttrium are described. Using as solvent di-2-ethylhexylphosphoric acid (DEHPA) a preliminary flow chart for separation for these elements are developed. (author)

  12. Element selective X-ray magnetic circular and linear dichroisms in ferrimagnetic yttrium iron garnet films

    Energy Technology Data Exchange (ETDEWEB)

    Rogalev, A. [European Synchrotron Radiation Facility (ESRF), B.P. 220, F-38043 Grenoble Cedex (France); Goulon, J. [European Synchrotron Radiation Facility (ESRF), B.P. 220, F-38043 Grenoble Cedex (France)], E-mail: goulon@esrf.fr; Wilhelm, F. [European Synchrotron Radiation Facility (ESRF), B.P. 220, F-38043 Grenoble Cedex (France); Brouder, Ch. [Institut de Mineralogie et de Physique des Milieux Condenses, UMR-CNRS 7590, Universite Paris VI-VII, 4 place Jussieu, F-75252 Paris Cedex 05 (France); Yaresko, A. [Max Planck Institute for Solid State Research, Heisenbergstrasse 1, 70569 Stuttgart (Germany); Ben Youssef, J.; Indenbom, M.V. [Laboratoire de Magnetisme de Bretagne, CNRS FRE 2697, UFR Sciences et Techniques, F-29328 Brest Cedex (France)

    2009-12-15

    X-ray magnetic circular dichroism (XMCD) was used to probe the existence of induced magnetic moments in yttrium iron garnet (YIG) films in which yttrium is partly substituted with lanthanum, lutetium or bismuth. Spin polarization of the 4d states of yttrium and of the 5d states of lanthanum or lutetium was clearly demonstrated. Angular momentum resolved d-DOS of yttrium and lanthanun was shown to be split by the crystal field, the two resolved substructures having opposite magnetic polarization. The existence of a weak orbital moment involving the 6p states of bismuth was definitely established with the detection of a small XMCD signal at the Bi M{sub 1}-edge. Difference spectra also enhanced the visibility of subtle changes in the Fe K-edge XMCD spectra of YIG and {l_brace}Y, Bi{r_brace}IG films. Weak natural X-ray linear dichroism signatures were systematically observed with all iron garnet films and with a bulk YIG single crystal cut parallel to the (1 1 1) plane: this proved that, at room temperature, the crystal cannot satisfy all requirements of perfect cubic symmetry (space group: Ia3-bar d), crystal distortions preserving at best trigonal symmetry (R3-bar or R3m). For the first time, a very weak X-ray magnetic linear dichroism (XMLD) was also measured in the iron K-edge pre-peak of YIG and revealed the presence of a tiny electric quadrupole moment in the ground-state charge distribution of iron atoms. Band-structure calculations carried out with fully relativistic LMTO-LSDA methods support our interpretation that ferrimagnetically coupled spins at the iron sites induce a spin polarization of the yttrium d-DOS and reproduce the observed crystal field splitting of the XMCD signal.

  13. Element selective X-ray magnetic circular and linear dichroisms in ferrimagnetic yttrium iron garnet films

    International Nuclear Information System (INIS)

    Rogalev, A.; Goulon, J.; Wilhelm, F.; Brouder, Ch.; Yaresko, A.; Ben Youssef, J.; Indenbom, M.V.

    2009-01-01

    X-ray magnetic circular dichroism (XMCD) was used to probe the existence of induced magnetic moments in yttrium iron garnet (YIG) films in which yttrium is partly substituted with lanthanum, lutetium or bismuth. Spin polarization of the 4d states of yttrium and of the 5d states of lanthanum or lutetium was clearly demonstrated. Angular momentum resolved d-DOS of yttrium and lanthanun was shown to be split by the crystal field, the two resolved substructures having opposite magnetic polarization. The existence of a weak orbital moment involving the 6p states of bismuth was definitely established with the detection of a small XMCD signal at the Bi M 1 -edge. Difference spectra also enhanced the visibility of subtle changes in the Fe K-edge XMCD spectra of YIG and {Y, Bi}IG films. Weak natural X-ray linear dichroism signatures were systematically observed with all iron garnet films and with a bulk YIG single crystal cut parallel to the (1 1 1) plane: this proved that, at room temperature, the crystal cannot satisfy all requirements of perfect cubic symmetry (space group: Ia3-bar d), crystal distortions preserving at best trigonal symmetry (R3-bar or R3m). For the first time, a very weak X-ray magnetic linear dichroism (XMLD) was also measured in the iron K-edge pre-peak of YIG and revealed the presence of a tiny electric quadrupole moment in the ground-state charge distribution of iron atoms. Band-structure calculations carried out with fully relativistic LMTO-LSDA methods support our interpretation that ferrimagnetically coupled spins at the iron sites induce a spin polarization of the yttrium d-DOS and reproduce the observed crystal field splitting of the XMCD signal.

  14. Properties of zirconium ceramics and film stabilized by yttrium

    International Nuclear Information System (INIS)

    Korobova, N.

    2004-01-01

    Full text: Unstable zirconium dioxide phase transformation can be eliminated by stabilization of the cubic phase with an addition of a selected alkaline earth or rare-earth oxide. Stabilized ZrO 2 has been widely utilized in various high-temperature refractory applications. These stabilized ZrO 2 -base solid solutions also possess rather unique electrical properties, and as a result have considerable potential as solid electrolytes in galvanic and fuel cells and, possibly, as heating elements in high-temperature furnaces. The complex study of synthesis processes, structure and properties of metal alkoxide organic sols have been developed. These have allowed to create main principles of their formation and to show the practical realization of obtained theoretical and experimental results. The correlation between hydrolysis conditions of (Zr+Y) metal alkoxide sols and synthesis of stable colloid multi-component systems has been established. Systematic research of zirconium and yttrium bi-alkoxide electrophoretic deposition was conducted for the first time. The formation mechanism of electrophoretic deposits has been offered and general scientific principles of the electrophoretic process have been formulated. The model of gel deposits structure was proposed. It has enabled to analyze the main (for example, cluster) effects, which have been exhibited in technological procedure for thin film preparation. The structure investigation of stabilized zirconium dioxide thin films and ceramics has been studied. The researches were based on the comparative analysis of the initial gel microstructure and dried gel by the various drying methods. The new approach for drying of gel electrophoretic deposits was formulated theoretically and experimentally has been proved. The modeling of the aggregate kinetics as a type of 'cluster-cluster' has been proposed like a qualitative description of the process. The data of fractal dimensions of aggregates which have been formed at the

  15. Occupational exposure following Yttrium-90 microspheres SIR therapy

    International Nuclear Information System (INIS)

    Fontaine, P.; Boirie, G.; Dieudonne, A.; Leguludec, D.; Lebtahi, R.; Ben Reguiga, M.

    2015-01-01

    Full text of publication follows. Introduction: Selective Internal Radiation Therapy (SIRT) is a promising technique for solid hepatic neoplasms treatment. SIRT consists in implanting radioactive microspheres (RMS) in targeted hepatic lesions via femoral artery. Two RMS-Therapsheres [glass-microspheres/TSR] and Sir-Spheres [resin-spheres/SSR]- are marketed in the European market, both radiolabeled with Yttrium-90. The objective of this study is to assess occupational exposure for nuclear medicine, radiology and clinical staff involved in Y 90 -RMS preparation and implantation. Materials and methods: The study was conducted on 20 patients treated for Hepato-Cellular Carcinoma: 10 treated with TSR and 10 with SSR. Dose rate (DR, mSv/h) or absorbed doses (mSv) measurements were made during all steps of TSR and SSR handling: sources receipt and unpacking, preparation, transport to radiology, implantation, and patient care. Measurements were made with portable ionization chamber(Babyline/Nardeux), spectrometer(FieldSpect/Aries), digital dosimeter (NED/Unfors) and operational dosimeter (Mk2/Siemens). Values were expressed as mean±SD. Results: patients received of 1.8 GBq to 3.1 GBq of TSR and 0.55 GBq to 2.4 GBq of SSR. TSR were delivered ready-to-use with the prescribed activity. For SSR only one activity was commercially available and shipped (3 GBq at calibration-time)requiring a preparation step to adjust needed activity. DR measured during RMS was 1723 ± 157 μSv/h SSR and 1189 ± 92 μSv/h for TSR. When preparing spheres in radiopharmacy, fingers and whole body doses were respectively 8326 ± 2360 μSv and 12.3 ± 5,2 μSv for Sir-Spheres vs. 33.5 ± 7.8 μSv and 1.1 ± 0.3 μSv for TSR. DR in contact with carrying case during RMS transfer to radiology were 299 ± 102 μSv/h for SSR and 5.3 ± 1.2 μSv/h for TSR. During RMS infusion, radiologist's finger doses were limited to 3.6 ± 1 μSv for SSR and 0.7± 0.3 μSv for TSR. Finally, following RMS

  16. Rare Earth Doped Lanthanum Calcium Borate Polycrystalline Red Phosphors

    Directory of Open Access Journals (Sweden)

    H. H. Xiong

    2014-01-01

    Full Text Available Single-phased Sm3+ doped lanthanum calcium borate (SmxLa2−xCaB10O19, SLCB, x=0.06 polycrystalline red phosphor was prepared by solid-state reaction method. The phosphor has two main excitation peaks located at 398.5 nm and 469.0 nm, which are nicely in accordance with the emitting wavelengths of commercial near-UV and blue light emitting diode chips. Under the excitation of 398.0 nm, the dominant red emission of Sm3+ in SLCB phosphor is centered at 598.0 nm corresponding to the transition of 4G5/2 → 6H7/2. The Eu3+ fluorescence in the red spectral region is applied as a spectroscopic probe to reveal the local site symmetry in the host lattice and, hence, Judd-Ofelt parameters Ωt  (t=2, 4 of Eu3+ in the phosphor matrix are derived to be 3.62×10-20 and 1.97×10-20 cm2, indicating a high asymmetrical and strong covalent environment around rare earth luminescence centers. Herein, the red phosphors are promising good candidates employed in white light emitting diodes (LEDs illumination.

  17. Laser discrimination by stimulated emission of a phosphor

    Science.gov (United States)

    Mathur, V. K.; Chakrabarti, K.

    1991-01-01

    A method for discriminating sources of UV, near infrared, and far infrared laser radiation was discovered. This technology is based on the use of a single magnesium sulfide phosphor doubly doped with rare earth ions, which is thermally/optically stimulated to generate colors correlatable to the incident laser radiation. The phosphor, after initial charging by visible light, exhibits green stimulated luminescence when exposed to a near infrared source (Nd: YAG laser). On exposure to far infrared sources (CO2 laser) the phosphor emission changes to orange color. A UV laser produces both an orange red as well as green color. A device using this phosphor is useful for detecting the laser and for discriminating between the near infrared, far infrared, and UV lasers. The technology is also capable of infrared laser diode beam profiling since the radiation source leaves an imprint on the phosphor that can be photographed. Continued development of the technology offers potential for discrimination between even smaller bandwidths within the infrared spectrum, a possible aid to communication or wavemixing devices that need to rapidly identify and process optical signals.

  18. Remarkable changes in the photoluminescent properties of Y2Ce2O7:Eu(3+) red phosphors through modification of the cerium oxidation states and oxygen vacancy ordering.

    Science.gov (United States)

    Raj, Athira K V; Prabhakar Rao, P; Sreena, T S; Sameera, S; James, Vineetha; Renju, U A

    2014-11-21

    A new series of red phosphors based on Eu(3+)-doped yttrium cerate [Y1.9Ce2O7:0.1Eu(3+), Y2Ce1.9O7:0.1Eu(3+) and Y2Ce2-xO7:xEu(3+) (x = 0.05, 0.10, 0.15, 0.20, 0.25 and 0.50)] was prepared via a conventional solid-state method. The influence of the substitution of Eu(3+) at the aliovalent site on the photoluminescent properties was determined by powder X-ray diffraction, FT Raman spectroscopy, X-ray photoelectron spectroscopy, transmission electron microscopy, scanning electron microscopy with energy-dispersive spectroscopy, UV-visible absorption spectroscopy, photoluminescence spectroscopy and lifetime measurements. The substitution of Eu(3+) at the Ce(4+) site induces a structural transition from a defect fluorite to a C-type structure, which increases the oxygen vacancy ordering and the distortion of the Eu(3+) environment, and decreases the formation of Ce(3+) states. In contrast, phosphors with isovalent substitution at the Y(3+) site exhibit the biphasic nature of defect fluorite and a C-type structure, thereby increasing the number of Ce(3+) oxidation states. These modifications resulted in remarkable changes in the photoluminescent properties of Y2Ce1.9O7:0.1Eu(3+) red phosphors, with emission intensities 3.8 times greater than those of the Ce0.9O2:0.1Eu(3+) and Y1.9Ce2O7:0.1Eu(3+). The photoluminescent properties of Y2Ce2-xO7:xEu(3+) were studied at different Eu(3+) concentrations under excitation with blue light. These phosphors emit intense red light due to the (5)D0-(7)F2 transition under excitation at 466 nm and no concentration quenching is observed with up to 50 mol% Eu(3+). They show increased lifetimes in the range 0.62-0.72 ms at Eu(3+) concentrations. The cation ordering linked to the oxygen vacancy ordering led to the uniform distribution of Eu(3+) ions in the lattice, thus allowing higher doping concentrations without quenching and consequently increasing the lifetime of the (5)D0 states. Our results demonstrate that significant improvements in

  19. Effect of yttrium on the oxide scale adherence of pre-oxidized silicon-containing heat-resistant alloy

    International Nuclear Information System (INIS)

    Yan Jingbo; Gao Yimin; Shen Yudi; Yang Fang; Yi Dawei; Ye Zhaozhong; Liang Long; Du Yingqian

    2011-01-01

    Highlights: → AE experiment shows yttrium has a beneficial effect on the pre-oxidized HP40 alloy. → Yttrium facilitates the formation of internal oxide after 10 h of oxidation. → Internal oxide changes the rupture behaviour of the oxide scale. → Twins form in the internal oxide and improve the binding strength of the scale. - Abstract: This paper investigates the effect of the rare earth element yttrium on the rupture behaviour of the oxide scale on the silicon-containing heat-resistant alloy during cooling. After 10 h of oxidation, yttrium is found to facilitate the formation of internal oxides (silica) at the scale-matrix interface. Due to the twinning observed by scanning transmission electron microscopy (STEM) in silica, the critical strain value for the scale failure can be dramatically improved, and the formation of cracks at the scale-matrix interface is inhibited.

  20. Process for recovery of uranium from wet process phosphoric acid

    International Nuclear Information System (INIS)

    Wiewiorowski, T.K.; Thornsberry, W.L. Jr.

    1978-01-01

    Process is claimed for the recovery of uranium from wet process phosphoric acid solution in which an organic extractant, containing uranium values and dissolved iron impurities and comprising a dialkylphosphoric acid and a trialkylphosphine oxide dissolved in a water immiscible organic solvent, is contacted with a substantially iron-free dilute aqueous phosphoric acid to remove said iron impurities. The removed impurities are bled from the system by feeding the resulting iron-loaded phosphoric acid to a secondary countercurrent uranium extraction operation from which they leave as part of the uranium-depleted acid raffinate. Also, process for recovering uranium in which the extractant, after it has been stripped of uranium values by aqueous ammonium carbonate, is contacted with a dilute aqueous acid selected from the group consisting of H 2 SO 4 , HCl, HNO 3 and iron-free H 3 PO 4 to improve the extraction efficiency of the organic extractant

  1. Stacking dependence of carrier transport properties in multilayered black phosphorous

    Science.gov (United States)

    Sengupta, A.; Audiffred, M.; Heine, T.; Niehaus, T. A.

    2016-02-01

    We present the effect of different stacking orders on carrier transport properties of multi-layer black phosphorous. We consider three different stacking orders AAA, ABA and ACA, with increasing number of layers (from 2 to 6 layers). We employ a hierarchical approach in density functional theory (DFT), with structural simulations performed with generalized gradient approximation (GGA) and the bandstructure, carrier effective masses and optical properties evaluated with the meta-generalized gradient approximation (MGGA). The carrier transmission in the various black phosphorous sheets was carried out with the non-equilibrium green’s function (NEGF) approach. The results show that ACA stacking has the highest electron and hole transmission probabilities. The results show tunability for a wide range of band-gaps, carrier effective masses and transmission with a great promise for lattice engineering (stacking order and layers) in black phosphorous.

  2. Persistent phosphors for painting, medical and biological applications

    International Nuclear Information System (INIS)

    Nazarov, M.

    2013-01-01

    Multiphase micro and nanoparticle persistent phosphors are synthesized and applied for different fields including painting, medical and biological investigations. A lot of examples show a broad range of applications of persistent luminescence from bulk materials to high tech products, especially in medicine. The development of high efficiency nanosized phosphor makes it possible to propose persistent materials as very good candidates for photodynamic therapy of cancer. An artificial block from slag, concrete, and sand covered with SrAl 2 O 4 :Eu 2+ , Dy 3+ based phosphor is prepared, and a new direction in biology for algae cultivation and artificial reef is discussed. For the first time, underwater luminescence is experimentally studied under real sea conditions. Bright blue-green long-lasting afterglow is registered at a depth of 5 m. The fishes are attracted by the light of the artificial reef. (author)

  3. Phosphor plate mammography: contrast studies and clinical experience

    International Nuclear Information System (INIS)

    Chang, C.H.J.; Martin, N.L.; Templeton, A.W.; Cook, L.T.; Harrison, L.A.; McFadden, M.A.; Dwyer, S.J. III; Spicer, J.; Crystal, J.M.

    1992-01-01

    Mammography and accurate microcalcification detection require very good spatial resolution. We have compared the diagnostic capabilities of reduced-exposure, third-generation, 5 cycles/mm computed radiography (CR) phosphor plates with conventional screen-film in 67 patients. No difference in diagnostic accuracy was detected. The digital characteristics of storage phosphor plates erabled us to study the relationship between contrast and spatial resolution. We developed a computer program to identify a single 100 μm pixel in a digital image and assign various gray levels to that pixel. Using this model, we determined that, for our 5 cycles/mm CR system, the imaged contrast of a 100 μm object was 62% of the original contrast. Current 5 cycles/mm phosphor plate systems cannot adequately detect microcalcifications that approximate 100 μm or smaller unless a magnification technique is used. (orig.)

  4. Ultraviolet /UV/ sensitive phosphors for silicon imaging detectors

    Science.gov (United States)

    Viehmann, W.; Cowens, M. W.; Butner, C. L.

    1981-01-01

    The fluorescence properties of UV sensitive organic phosphors and the radiometric properties of phosphor coated silicon detectors in the VUV, UV, and visible wavelengths are described. With evaporated films of coronene and liumogen, effective quantum efficiencies of up to 20% have been achieved on silicon photodiodes in the vacuum UV. With thin films of methylmethacrylate (acrylic), which are doped with organic laser dyes and deposited from solution, detector quantum efficiencies of the order of 15% for wavelengths of 120-165 nm and of 40% for wavelengths above 190 nm have been obtained. The phosphor coatings also act as antireflection coatings and thereby enhance the response of coated devices throughout the visible and near IR.

  5. Recovery of zinc in phosphor wastes via electrokinetic treatments

    International Nuclear Information System (INIS)

    Yu, M.Y.; Wang, H. Paul; Chen, C.Y.; Hsiung, T.-L.; Wei, Yu-Ling; Tai, H.-S.; Chiang, K.-C.

    2007-01-01

    Speciation of zinc in phosphor wastes during electrokinetic treatments has been studied by in situ X-ray absorption near edge structure (XANES) spectroscopy in the present work. The least-square fits of the in situ XANES spectra show that the major zinc species in the phosphor waste are ZnS (77%), ZnO (10%), and Zn(OH) 2 (13%). During the electrokinetic treatment for 90 min, 25% of ZnS and 4% of ZnO are dissolved. About 42% of zinc is enriched on the cathode under the electric field (5 V/cm). Prolonging the electrokinetic treatment time to 4 h under the electric field of 5 V/cm, at least 80% of zinc in the phosphor waste can be recovered

  6. White-electroluminescent device with horizontally patterned blue/yellow phosphor-layer structure

    International Nuclear Information System (INIS)

    Won Park, Boo; Sik Choi, Nam; Won Park, Kwang; Mo Son, So; Kim, Jong Su; Kyun Shon, Pong

    2007-01-01

    White-electroluminescent (EL) devices with stripe-patterned and square-patterned phosphor-layer structures are fabricated through a screen printing method: electrode/BaTiO 3 insulator layer/patterned blue ZnS:Cu, Cl and yellow ZnS:Cu, Mn phosphor layer/ITO PET substrate. The luminous intensities of EL devices with stripe-patterned and square-patterned phosphor-layer structures are 33% and 23% higher than a conventional device with the phosphor-layer structure without any patterns using the phosphor blend. It can be explained in terms of the absorption of the emitted blue light of blue phosphor layer by the yellow-emitting phosphor layer. The EL device of our patterned phosphor-layer structure gives the possibility to enhance the luminance

  7. An ICP AES method for determination of dysprosium and terbium in high purity yttrium oxide

    International Nuclear Information System (INIS)

    Rupawate, V.H.; Hareendran, K.N.; Roy, S.B.

    2011-01-01

    High purity yttrium finds interesting application in astronavigation, luminescence, nuclear energy and metallurgical industries. Most of these applications require yttrium oxide of highest purity. Consequently there is a need for production of high purity yttrium oxide. Separation and purification of yttrium from other rare earths is a challenging task due to their close chemical properties. Liquid-liquid extraction and ion exchange have been widely used in the production of yttrium oxide of highest purity. Determination of impurities, especially other rare earths, in ppm level is required for process development and chemical characterization of the high purity Y 2 O 3 . Many methods have been described in literature. However since the advent of ICP AES much work in this area has been carried out by this technique. This paper describes the work done for determination of dysprosium (Dy) and terbium (Tb) in yttrium oxide using a high resolution sequential ICP AES. Emission spectra of rare earth elements are very complex and due to this complexity it is important to select spectral interference free analyte lines for determination of rare earths in rare earth matrix. For the determination of Dy and Tb in Y 2 O 3 , sensitive lines of Dy and Tb are selected from the instrument wavelength table and spectral interference free emission lines for the determination is selected by scanning around the selected wavelengths using 5 g/L Y solution and 5 mg/L standard solutions of Dy and Tb prepared in 4% nitric acid. It is found 353.170 nm line of Dy and 350.917 nm line Tb is suitable for quantitative determination. The signal to background ratio increases with increase in matrix concentration, i.e. from 1 to 5 mg/L. The optimum forward power is determined and it is found to be 1100W for Dy and 1000W for Tb. The instrument is calibrated using matrix matched standards containing 5g/L of Y matrix. Samples are dissolved in nitric acid and Y concentration is maintained at 5g/L. Two

  8. Comparative study of the shear bond strength of composite resin bonded to enamel treated with acid etchant and erbium, chromium: Yttrium, scandium, gallium, garnet laser

    Directory of Open Access Journals (Sweden)

    Adel Sulaiman Alagl

    2016-01-01

    Full Text Available Aim: The purpose of this investigation is in vitro comparison of the shear bond strength (SBS of composite resin bonded to enamel pretreated with an acid etchant against enamel etched with erbium, chromium: yttrium, scandium, gallium, garnet (Er, Cr:YSGG laser. Materials and Methods: Sixty premolars were sectioned mesiodistally and these 120 specimens were separated into two groups of 60 each (Groups A and B. In Group A (buccal surfaces, enamel surface was etched using 37% phosphoric acid for 15 s. In Group B (lingual surfaces, enamel was laser-etched at 2W for 10 s by Er, Cr:YSGG laser operational at 2780 nm with pulse duration of 140 μs and a frequency of 20 Hz. After application of bonding agent on all test samples, a transparent plastic cylinder of 1.5 mm × 3 mm was loaded with composite and bonded by light curing for 20 s. All the samples were subjected to SBS analysis using Instron Universal testing machine. Failure modes were observed under light microscope and grouped as adhesive, cohesive, and mixed. Failure mode distributions were compared using the Chi-square test. Results: SBS values obtained for acid-etched enamel were in the range of 7.12–28.36 megapascals (MPa and for laser-etched enamel were in the range of 6.23–23.35 MPa. Mean SBS for acid-etched enamel was 15.77 ± 4.38 MPa, which was considerably greater (P < 0.01 than laser-etched enamel 11.24 ± 3.76 MPa. The Chi-square test revealed that the groups showed no statistically significant differences in bond failure modes. Conclusions: We concluded that the mean SBS of composite with acid etching is significantly higher as compared to Er, Cr: YSGG (operated at 2W for 10 s laser-etched enamel.

  9. Method for the recovery of uranium from a concentrate using pure phosphoric acid

    International Nuclear Information System (INIS)

    1980-01-01

    Procedure for the recovery of an uranium bearing concentrate and pure phosphoric acid from a wet process phosphoric acid from the treatment fluid with a precipitation means in conjunction with an organic diluent, the thus formed precipitate to separate and from the remaining mixture of phosphoric acid and diluent the phosphoric acid to extract, characterised in that one applies an inorganic fluorine compound. (G.C.)

  10. Reactivity of the cadmium ion in concentrated phosphoric acid solutions.

    Science.gov (United States)

    De Gyves, J; Gonzales, J; Louis, C; Bessiere, J

    1989-07-01

    The solvation transfer coefficients which characterize the changes of ion reactivity with phosphoric acid concentration have been calculated for cadmium from the constants of the successive chloride complexes, and for silver and diethyldithiophosphate from potentiometric measurements. They evidence the strong desolvation of the cadmium species in concentrated phosphoric acid media, causing a remarkable increase of its reactivity. They allow the results of liquid-liquid extraction, precipitation and flotation reactions to be correctly interpreted and their changes to be foreseen when the reagents are modified.

  11. Phosphoric acid fuel cell R and D activities at KACST

    International Nuclear Information System (INIS)

    Ghouse, M.; Aba-Oud, H.; Ba-Junaid, M.; Al-Garni, M.; Quadri, M.I.

    1993-01-01

    The PAFC (Phosphoric Acid Fuel Cell) activities are directed towards the development of components of single cell and experimental stacks at KACST. The main aim of the present task is to design and construct a 1 kW PAFC Stack and demonstrate it by integrating with an electrolyser using a DC current generated by a photovoltaic power source. This paper describes the preparation of porous teflon bonded gas diffusion carbon electrodes and their evaluation as single phosphoric acid fuel cells using hydrogen as a fuel and oxygen/air as an oxidant. 6 figs., 2 tabs., 15 refs

  12. Cadmium elemination from phosphoric acid by ionic flotation

    International Nuclear Information System (INIS)

    Brikci-Nigassa, Mounir; Hamouche, Hafida

    1995-11-01

    The ion flotation process for the recovery of cadmium from wet phosphoric acid (30%P2O5) has been studied. This technique combines a chemical recation between the collector and the cadmium to form a precipitate (sublate) which is carried to the surface of the solution by air bubbles. the resulting foam containing the cadmium may then separated from solution. The influence of parameters such as collector and cadmium concentration as well as iron content have been investigated for the case a synthetic acid (30% P2O5). The result have been applied to the industrial phosphoric acid produced from Djebel Onk's phosphates (Algeria)

  13. Transport of phosphoric acid through supported liquid membrane

    International Nuclear Information System (INIS)

    Zayzafoon, G.; Yassine, T.; Baidoun, R.

    2003-01-01

    The transport of phosphhoric acid through liquid membranes of amylalkohol, 1-octanol and 2-octanol was studied. It was found that phosphoric acid is transfered from feed side to strip side and the transport increased with the concentration of phosphoric acid up to 5M. The permeability in each membrane was determined for 5M phosphoic acid. It was found that the permeability values are 1.45 x 10 1 0 m 2 s 1 for amylakohol and ∼ 1x10 1 0 m 2 s 1 for each of 1-octanol and 2-octanol

  14. Purification of di-nonyl phenyl phosphoric acid (DNPPA) for synergistic extraction of uranium from strong phosphoric acid

    International Nuclear Information System (INIS)

    Singh, D.K.; Vijayalakshmi, R.; Singh, H.; Sharma, J.N.; Ruhela, R.

    2009-01-01

    Di-nonyl phenyl phosphoric acid (DNPPA) obtained from various synthesis methods is always associated with impurities such as mono-nonyl phenyl phosphoric acid and nonyl phenol which need to be separated for its effective use in the extraction of uranium from strong phosphoric acid. Two methods of purification namely liquid-solid separation method using neodymium salt and liquid-liquid separation method using methylene glycol have been described. In the liquid solid separation method the purity of DNPPA obtained was about 95% with less than 1.0% monoester, however it heavily suffers in the recovery aspect which is of the order of 50-60%. The methylene glycol treatment method, results in high purity and recovery of the product. Purity obtained was about 95.0% diester and less than 0.5% monoester and recovery was more than 90%. Analysis of DNPPA was done by potentiometric titration method using autotitrator. (author)

  15. Rare earths (Ce, Eu, Tb) doped Y2Si2O7 phosphors for white LED

    International Nuclear Information System (INIS)

    Sokolnicki, Jerzy

    2013-01-01

    Nanocrystalline yttrium pyrosilicate Y 2 Si 2 O 7 (YPS) singly, doubly or triply doped with Ce 3+ , Eu 3+ , Tb 3+ was obtained by the reaction of nanostructured Y 2 O 3 :Ln 3+ and colloidal SiO 2 at high temperatures. X-ray diffraction analysis confirmed the formation of a single phase of α-YPS at 1200 °C. Two series of YPS samples doped with Eu 3+ or Eu 3+ /Tb 3+ were obtained by applying the reducing atmosphere (75%N 2 +25%H 2 ) at different temperatures. The luminescence and excitation spectra are reported. The singly Eu 3+ doped YPS emit from both Eu 3+ and Eu 2+ ions, with the spectral position and width of the Eu 2+ emission different in both series. The presence of Eu 2+ in the samples was confirmed by electron paramagnetic resonance (EPR) spectra. A broadband emission of Eu 2+ (380–650 nm), combined with the red emission of Eu 3+ is perceived by the naked eye as white light. Co-doping of YPS:Eu 3+ with Tb 3+ results in enhancement of the green component of the emission, and well-balanced white luminescence. The colour of this emission is tunable, and it is possible to get Commission International de I'Eclairage (CIE) chromaticity coordinates of (0.327, 0.327), colour-rendering index (CRI) of 85, and quantum efficiency (QE) of 71%. These phosphors are efficiently excited in the wavelength range of 300–420 nm, which perfectly matches a near UV-emitting InGaN chip. It was shown that for triply (Ce 3+ , Eu 3+ and Tb 3+ ) doped samples the three emissions from the particular activators can be generated using one excitation wavelength. The white light resulting from the superposition of the blue (Ce 3+ ), green (Tb 3+ ) and red (Eu 3+ ) emissions can be obtained by varying the concentration of the active ions and the treating atmosphere, i.e. reducing or oxidising. Eu 2+ was not detected in the triply doped samples, and hence line emissions mostly exhibit CRI values equal to or below 30. - Highlights: ► Nanocrystalline Y 2 Si 2 O 7 was obtained by the

  16. Some peculiarities of thermoemission of the cathodes on the base of tanthanum and yttrium oxides

    International Nuclear Information System (INIS)

    Podgornyj, V.I.

    1982-01-01

    Thermoemission cathode characteristics on the basis of (La 2 O 3 ) lanthanum, and yttrium oxides which are used already in prctice but emission mechanism of which remains yet insufficiently elucidated, were investigated. It is shown that the heating of cathodes on the basis of Y 2 O 3 and La 2 O 3 at activation temperatures during 2-3 h with successive cooling results in the state of surface with increased thermoemission activity. It is established that the cathode heating in electric field of positive polarity results in decreasing thermoemission activity of lanthanum oxide by approximately 0.35 eV and for yttrium oxide - by approximately 0.05 eV as compared with the heating in the field of negative polarity. The effect obtained is related to the change in the metal adatom concentration on the cathode surface

  17. An XRF method for determination of common rare earth impurities in high purity yttrium oxide

    International Nuclear Information System (INIS)

    Dixit, R.M.; Deshpande, S.S.

    1975-01-01

    An XRF method for the estimation of Eu, Gd, Tb, Dy, Ho, Er and Yb in yttrium oxide has been developed. Samples are converted to yttrium oxalate and presented to the spectrometer in the form of pressed pellets. Philips PW-1220, a semi-automatic x-ray spectrometer, is used for the analysis. Line interference problems are studied for selecting analysis lines. For the elements except that of Yb, the lower estimation limit is 0.005% and for Yb, it is 0.01%. The average standard deviation is approximately 5% for various elements in the concentration range of 0.005% to 1.0%. The method has been tested for its accuracy by analysing synthesized samples with known composition at three different concentrations. (author)

  18. Characterization of photoluminescent europium doped yttrium oxide thin-films prepared by metallorganic chemical vapor deposition

    International Nuclear Information System (INIS)

    McKittrick, J.; Bacalski, C.F.; Hirata, G.A.; Hubbard, K.M.; Pattillo, S.G.; Salazar, K.V.; Trkula, M.

    1998-01-01

    Europium doped yttrium oxide, (Y 1-x Eu x ) 2 O 3 , thin-films were deposited on silicon and sapphire substrates by metallorganic chemical vapor deposition (MOCVD). The films were grown in a MOCVD chamber reacting yttrium and europium tris(2,2,6,6-tetramethyl-3,5,-heptanedionates) precursors in an oxygen atmosphere at low pressures (5 Torr) and low substrate temperatures (500--700 C). The films deposited at 500 C were flat and composed of nanocrystalline regions of cubic Y 2 O 3 , grown in a textured [100] or [110] orientation to the substrate surface. Films deposited at 600 C developed from the flat, nanocrystalline morphology into a plate-like growth morphology oriented in the [111] with increasing deposition time. Monoclinic Y 2 O 3 :Eu 3+ was observed in x-ray diffraction for deposition temperatures ≥600 C on both (111) Si and (001) sapphire substrates. This was also confirmed by the photoluminescent emission spectra

  19. Preparation of yttrium iron garnet (YIG) by modified domestic iron oxide

    International Nuclear Information System (INIS)

    Mozaffari, M.; Amighian

    2002-01-01

    Iron oxide by product of a local steel complex was modified to use for preparation of Yttrium iron garnet (YIG). The improvement was necessary to reduce impurities, especially the Si0 2 and Cl contents, which have deteriorative effects on magnetic properties and equipment used for preparation of the samples. The modified iron oxide was then mixed with Yttrium oxide of Merck Company in appropriate proportion to obtain a stoichiometric single phase YIG, using the conventional ceramic technique. XRD and SEM equipments were used to identify the resulting phases and microstructure respectively. Magnetic parameters were measured by VSM. Curie temperature of the samples was obtained by DTG (M) method. The results were compared with those obtained from samples that made by Merck iron oxide. There are small differences between the results. This was discussed according to extra pores and minute secondary phase in the samples made by domestic iron oxide. (Author)

  20. Determination of yttrium using YO band head obtained by laser enhanced ionization spectrometry

    International Nuclear Information System (INIS)

    Deshpande, S.S.; Khanna, P.P.

    1997-04-01

    The determination of yttrium (Y) in water in the concentration range of 2 μg/ml to 200 μg/ml by laser enhanced ionisation (LEI) technique is reported. The YO band head at 584.27 nm belonging to A 2 Π - X 2 Σ + system is used for LEI signal detection. It is also shown that the LEI signal is enhanced when the mixture of air - acetylene - argon (AAA) is used instead of commonly used air-acetylene (AA) mixture. In the present work an XeCl laser (308 nm) pumped rhodamine 6G dye laser, covering a range of 570-610 nm is used. The sample/standard in solution form is aspirated into the flame with pneumatic nebulizer. The working curve is a straight line showing linear dependence of LEI signal with yttrium concentration. The relative standard deviation calculated at 100 μg/ml is found to be 2.4 %. (author)

  1. Quantum design and synthesis of a boron-oxygen-yttrium phase

    International Nuclear Information System (INIS)

    Music, Denis; Chirita, Valeriu; Kreissig, Ulrich; Czigany, Zsolt; Schneider, Jochen M.; Helmersson, Ulf

    2003-01-01

    Ab initio calculations are used to design a crystalline boron-oxygen-yttrium (BOY) phase. The essential constituent is yttrium substituting for oxygen in the boron suboxide structure (BO 0.17 ) with Y/B and O/B ratios of 0.07. The calculations predict that the BOY phase is 0.36 eV/atom more stable than crystalline BO 0.17 and experiments confirm the formation of crystalline thin films. The BOY phase was synthesized with reactive rf magnetron sputtering and identified with x-ray and selected area electron diffraction. Films with Y/B ratios ranging from 0.10 to 0.32, as determined via elastic recoil detection analysis, were grown over a wide range of temperatures (300-600 deg. C) and found to withstand 1000 deg. C

  2. Yttrium-90 used to treat colon cancer: Awaiting investigational new drug approval

    International Nuclear Information System (INIS)

    Anon.

    1991-01-01

    A new radiation treatment takes just 14 to 21 days to shrink colorectal tumors in laboratory mice, is under review for clinical trials with human cancer patients. The treatment has succeeded in reducing the size of tumors by up to 95%. Colon cancer, the second leading cause of cancer deaths in the US, is extremely difficult to treat unless it is detected early enough for surgical procedures. In laboratory tests over the last 5 years, a team of researchers has developed the treatment using yttrium-90. The yttrium-90 is transported to the tumors by attaching it to monoclonal antibodies that seek out the cancer cells. Once the radioisotope has been targeted to the tumor, the radiation destroys many of the cells, dramatically reducing the size of the tumor. Since this treatment usually does not completely eliminate all the cancer cells, it cannot be called a cure, but it does seem to be an effective method of shrinking colorectal tumors

  3. Mass synthesis of yttrium oxide nano-powders using radio frequency (RF) plasma

    International Nuclear Information System (INIS)

    Ghorui, S.; Sahasrabudhe, S.N.; Chakravarthy, Y.; Nagaraj, A.; Das, A.K.; Dhamale, G.

    2014-01-01

    Mass synthesis of nano-phase Yttrium Oxide (Y 2 O 3 ) from commercially available coarse grain powder is reported. Nano-sized high purity Y 2 O 3 is an important and critical constituent of ceramics like YAG (Yttrium aluminum garnet: Y 3 Al 5 O 12 ) for laser applications. The system is characterized in terms of its thermal and electrical behavior. Boltzmann plot technique is used to measure axial variation of temperature of the generated plasma. The synthesized particles are characterized in terms of XRD, SEM, TEM and BET analyses for qualification of the developed system. Major features observed are efficient conversion into nanometer-sized highly spherical particles, narrow size distribution, highly crystallite nature and highly pure phases. The particle distribution (from TEM) peaks within 20-30 nm. Average particle sizes determined from different methods like XRD, TEM and BET are very close to each other and point toward particle sizes within 20 to 30 nm

  4. Preparation of polycrystalline lithium-yttrium fluoride for subsequent mono crystallization

    International Nuclear Information System (INIS)

    Kowalczyk, E.; Radomski, J.; Diduszko, R.; Iwanejko, J.; Kowalczyk, Z.; Grasza, K.

    1994-01-01

    High purity lithium-yttrium (YLF) doped with rare earth elements (Nd, Pr, Ho or Tm) was obtained in a two-stage synthesis consisting of (1) reaction of ammonium fluoride with a mixture of lithium carbonate, yttrium oxide, and oxides of lanthanides, and (2) heating of the obtained reaction products at a temperature of about 700 C in an inert gas atmosphere. The phase and chemical purities of the obtained materials were characterized by X-ray diffraction and mass spectrometry techniques. Single crystal growth tests were carried out by means of the Bridgman method. The results showed that the proposed method for manufacture of polycrystalline YLF doped with rare earth elements is appropriate in principle but some parameters of the preparation process are to be more strictly defined. (author). 9 refs, 4 figs, 1 tab

  5. Preparation of polycrystalline lithium-yttrium fluoride for subsequent mono crystallization

    Energy Technology Data Exchange (ETDEWEB)

    Kowalczyk, E.; Radomski, J.; Diduszko, R.; Iwanejko, J. [Institute of Vacuum Technology, Warsaw (Poland); Kowalczyk, Z. [Warsaw Univ. (Poland); Grasza, K. [Polska Akademia Nauk, Warsaw (Poland). Inst. Fizyki

    1994-12-31

    High purity lithium-yttrium (YLF) doped with rare earth elements (Nd, Pr, Ho or Tm) was obtained in a two-stage synthesis consisting of (1) reaction of ammonium fluoride with a mixture of lithium carbonate, yttrium oxide, and oxides of lanthanides, and (2) heating of the obtained reaction products at a temperature of about 700 C in an inert gas atmosphere. The phase and chemical purities of the obtained materials were characterized by X-ray diffraction and mass spectrometry techniques. Single crystal growth tests were carried out by means of the Bridgman method. The results showed that the proposed method for manufacture of polycrystalline YLF doped with rare earth elements is appropriate in principle but some parameters of the preparation process are to be more strictly defined. (author). 9 refs, 4 figs, 1 tab.

  6. Yttrium and lanthanum recovery from low cerium carbonate, yttrium carbonate and yttrium concentrate; Aproveitamento de itrio e lantanio de um carbonato de terras raras de baixo teor em cerio, de um carbonato de itrio e de um oxido de terras itricas

    Energy Technology Data Exchange (ETDEWEB)

    Vasconcelos, Mari Estela de

    2006-07-01

    In this work, separation, enrichment and purification of lanthanum and yttrium were performed using as raw material a commercial low cerium rare earth concentrate named LCC (low cerium carbonate), an yttrium concentrate named 'yttrium carbonate', and a third concentrated known as 'yttrium earths oxide. The first two were industrially produced by the late NUCLEMON - NUCLEBRAS de Monazita e Associados Ltda, using Brazilian monazite. The 'yttrium earths oxide' come from a process for preparation of lanthanum during the course of the experimental work for the present thesis. The following techniques were used: fractional precipitation with urea; fractional leaching of the LCC using ammonium carbonate; precipitation of rare earth peroxycarbonates starting from the rare earth complex carbonates. Once prepared the enriched rare earth fractions the same were refined using the ion exchange chromatography with strong cationic resin without the use of retention ion and elution using the ammonium salt of ethylenediaminetetraacetic acid. With the association of the above mentioned techniques were obtained pure oxides of yttrium (>97,7%), lanthanum (99,9%), gadolinium (96,6%) and samarium (99,9%). The process here developed has technical and economic viability for the installation of a large scale unity. (author)

  7. Hydrothermal synthesis, crystal structures and photoluminescence properties of mixed europium–yttrium organic frameworks

    International Nuclear Information System (INIS)

    Han Yinfeng; Fu Lianshe; Mafra, Luís; Shi, Fa-Nian

    2012-01-01

    Three mixed europium–yttrium organic frameworks: Eu 2−x Y x (Mel)(H 2 O) 6 (Mel=mellitic acid or benzene-1,2,3,4,5,6-hexacarboxylic acid, x=0.38 1, 0.74 2, and 0.86 3) have been synthesized and characterized. All the compounds contain a 3-D net with (4, 8)-flu topology. The study indicates that the photoluminescence properties are effectively affected by the different ratios of europium and yttrium ions, the quantum efficiency is increased and the Eu 3+ lifetime becomes longer in these MOFs than those of the Eu analog. - Graphical abstract: Three mixed europium and yttrium organic frameworks: Eu 2−x Y x (Mel)(H 2 O) 6 (Mel=mellitic acid) have been synthesized and characterized. All the compounds contain a 3-D net with (4, 8)-flu topology. The study indicates that the photoluminescence properties are effectively affected by the different ratios of europium and yttrium ions, the quantum efficiency is increased and the Eu 3+ lifetime becomes longer in these MOFs than those of the Eu analog. Highlights: ► Three (4, 8)-flu topological mixed Eu and Y MOFs were synthesized under mild conditions. ► Metal ratios were refined by the single crystal data consistent with the EDS analysis. ► Mixed Eu and Y MOFs show longer lifetime and higher quantum efficiency than the Eu analog. ► Adding inert lanthanide into luminescent MOFs enlarges the field of luminescent MOFs.

  8. Peripheral Blood Lymphocyte Depletion After Hepatic Arterial {sup 90}Yttrium Microsphere Therapy for Hepatocellular Carcinoma

    Energy Technology Data Exchange (ETDEWEB)

    Carr, Brian I., E-mail: brianicarr@hotmail.com [Department of Surgery, University of Pittsburgh Medical Center, Pittsburgh, PA and Department of Nutrition and Exptl Biology, Saverio De Bellis Medical Research Institute, Castellana Grotte, Bari (Italy); Metes, Diana M. [Department of Surgery, University of Pittsburgh Medical Center, Pittsburgh, PA and Department of Nutrition and Exptl Biology, Saverio De Bellis Medical Research Institute, Castellana Grotte, Bari (Italy)

    2012-03-01

    Purpose: The short- and long-term effects of {sup 90}Yttrium microspheres therapy for hepatocellular carcinoma (HCC) on peripheral blood lymphocytes are unknown and were therefore examined. Methods and Materials: Ninety-two HCC patients were enrolled in a {sup 90}Yttrium therapy study and routine blood counts were examined as part of standard clinical monitoring. Results: We found an early, profound, and prolonged lymphopenia. In a subsequent cohort of 25 additional HCC patients, prospective flow cytometric immune-monitoring analysis was performed to identify specific changes on distinct lymphocyte subsets (i.e., CD3, CD4, CD8 T, and CD19 B lymphocytes) and NK cells absolute numbers, in addition to the granulocytes and platelets subsets. We found that the pretreatment lymphocyte subset absolute numbers (with the exception of NK cells) had a tendency to be lower compared with healthy control values, but no significant differences were detected between groups. Posttherapy follow-up revealed that overall, all lymphocyte subsets, except for NK cells, were significantly (>50% from pretherapy values), promptly (as early as 24 h) and persistently (up to 30 months) depleted post-{sup 90}Yttrium microspheres therapy. In contrast, granulocytes increased rapidly (24 h) to compensate for lymphocyte depletion, and remained increased at 1-year after therapy. We further stratified patients into two groups, according to survival at 1 year. We found that lack of recovery of CD19, CD3, CD8, and especially CD4 T cells was linked to poor patient survival. No fungal or bacterial infections were noted during the 30-month follow-up period. Conclusions: The results show that lymphocytes (and not granulocytes, platelets, or NK cells) are sensitive to hepatic arterial {sup 90}Yttrium without associated clinical toxicity, and lack of lymphocyte recovery (possibly leading to dysregulation of adaptive cellular immunity) posttherapy indicates poor survival.

  9. The effect of yttrium substitution on the magnetic properties of magnetite nanoparticles

    International Nuclear Information System (INIS)

    Mozaffari, M.; Amighian, J.; Tavakoli, R.

    2015-01-01

    Superparamagnetic Y-substituted magnetite (Y x Fe 3–x O 4 ,with x=0.00, 0.10, 0.15, 0.20 and 0.40) nanoparticles were synthesized via hydrothermal reduction route in the presence of citric acid. The synthesized nanoparticles were characterized by X-ray diffraction (XRD) analysis, Fourier transform infrared (FTIR) spectroscopy, field emission scanning electron microscopy (FESEM), vibrating sample magnetometry (VSM) and gradient field thermomagnetic measurement. The results showed that a minimum amount of citric acid is required to obtain single phase Y-substituted magnetite nanoparticles. Citric acid acts as a modulator and reducing agent in the formation of spinel structure and controls nanoparticle size and crystallinity. Mean crystallite sizes of the single-phase powders were estimated by Williamson–Hall method. Curie temperature measurement of the samples shows that as yttrium content increases, the Curie temperature decreases. Magnetic measurements show that the saturation magnetization of the samples decreases as x increases up to 0.15 and then increases to x=0.20 and finally decreases again for x=0.40. - Highlights: • Single phase yttrium substituted magnetite nanoparticles were synthesized by hydrothermal-reduction route. • Citric acid plays a key role in reduction of Fe 3+ to Fe 2+ , which is necessary for the formation of magnetite phase. • It is possible to substitute yttrium ions for iron ones as high as x=0.4 by hydrothermal reduction route. • Pure magnetite nanoparticles prepared by this route has a high saturation magnetization. • Yttrium substituted magnetite nanoparticles are superparamagnet at room temperature

  10. Studies on the pressed yttrium oxide-tungsten matrix as a possible dispenser cathode material

    International Nuclear Information System (INIS)

    Yang, Fan; Wang, Jinshu; Liu, Wei; Liu, Xiang; Zhou, Meiling

    2015-01-01

    Yttrium oxide was chosen as the secondary emission substance based on calculation results through first principle theory method. A new kind of pressed yttrium oxide-tungsten matrix dispenser cathodes are prepared by a sol–gel method combined with high temperature sintering in dry hydrogen atmosphere. The results show that the growth of the grains is hampered by the pinning effect of Y 2 O 3 distributing uniformly between the tungsten particles, resulting in the formation of small grain size. It is found that Y 2 O 3 improves the secondary electron emission property, i.e., the secondary emission yield increases with the increase of Y 2 O 3 content in the samples. The maximum secondary emission yield δ max of the cathode with 15% amount of Y 2 O 3 can reach 2.92. Furthermore, the cathode shows a certain thermionic emission performance. The zero field emission current density J 0 of 4.18A/cm 2 has reached at 1050 °C b for this kind of cathode after being activated at 1200 °C b , which are much higher than that of rare earth oxide doped molybdenum (REO-Mo) cathode reported in the previous work. - Highlights: • Yttrium oxide was chosen as the secondary emission substance based on first principle calculation result. • A new kind of cathode has been successfully obtained. • Pressed yttrium oxide-tungsten matrix dispenser cathode exhibits good emission properties. • The improvement of the cathode emission can be well explained by the surface analysis results presented in this work

  11. Recurrent thermo-luminescence phenomenon in yttrium-aluminum garnet crystals

    International Nuclear Information System (INIS)

    Islamov, A.Kh.; Nuritdinov, I.; Esanov, Z.U.; Eshchanov, B.Kh.; Khayitov, I.A.

    2014-01-01

    Full text : The crystals of yttrium-aluminum garnet Y 2 Al 2 O 1 2 activated by cerium and praseodymium ions by their thermal and chemical durability as well as fast response are perspective scintillation materials. In this work the capture centres formed by action of the ionizing radiation on pure and doped by praseodymium and cerium crystals were investigated. The samples were grown using Chokhralsky method

  12. Trends in metallo-organic chemistry of scandium, yttrium, and the lanthanides

    International Nuclear Information System (INIS)

    Singh, A.

    1994-01-01

    Several interesting aspects of the metallo-organic chemistry of group 3 and the lanthanides have been highlighted, which include: (a) the chemistry of a few notable organolanthanide compounds, alkoxo and aryloxo derivatives derived from sterically demanding ligands, (b) new trends in the chemistry of lanthanide heterometallic alkoxides, (c) an account of zero valent organometallics of yttrium and the lanthanides, and (d) aspects of agostic interactions in the lanthanide metallo-organic compounds. (author). 49 refs

  13. Studies on the pressed yttrium oxide-tungsten matrix as a possible dispenser cathode material

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Fan; Wang, Jinshu, E-mail: wangjsh@bjut.edu.cn; Liu, Wei; Liu, Xiang; Zhou, Meiling

    2015-01-15

    Yttrium oxide was chosen as the secondary emission substance based on calculation results through first principle theory method. A new kind of pressed yttrium oxide-tungsten matrix dispenser cathodes are prepared by a sol–gel method combined with high temperature sintering in dry hydrogen atmosphere. The results show that the growth of the grains is hampered by the pinning effect of Y{sub 2}O{sub 3} distributing uniformly between the tungsten particles, resulting in the formation of small grain size. It is found that Y{sub 2}O{sub 3} improves the secondary electron emission property, i.e., the secondary emission yield increases with the increase of Y{sub 2}O{sub 3} content in the samples. The maximum secondary emission yield δ{sub max} of the cathode with 15% amount of Y{sub 2}O{sub 3} can reach 2.92. Furthermore, the cathode shows a certain thermionic emission performance. The zero field emission current density J{sub 0} of 4.18A/cm{sup 2} has reached at 1050 °C{sub b} for this kind of cathode after being activated at 1200 °C{sub b}, which are much higher than that of rare earth oxide doped molybdenum (REO-Mo) cathode reported in the previous work. - Highlights: • Yttrium oxide was chosen as the secondary emission substance based on first principle calculation result. • A new kind of cathode has been successfully obtained. • Pressed yttrium oxide-tungsten matrix dispenser cathode exhibits good emission properties. • The improvement of the cathode emission can be well explained by the surface analysis results presented in this work.

  14. Alkylation of pyridines at their 4-positions with styrenes plus yttrium reagent or benzyl Grignard reagents.

    Science.gov (United States)

    Mizumori, Tomoya; Hata, Takeshi; Urabe, Hirokazu

    2015-01-02

    A new regioselective alkylation of pyridines at their 4-position was achieved with styrenes in the presence of yttrium trichloride, BuLi, and diisobutylaluminium hydride (DIBAL-H) in THF. Alternatively, similar products were more simply prepared from pyridines and benzyl Grignard reagents. These reactions are not only a useful preparation of 4-substituted pyridines but are also complementary to other relevant reactions usually giving 2-substituted pyridines. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  15. Substitution of yttrium for boron in the structure of YBa2Cu3O7-δ

    International Nuclear Information System (INIS)

    Dwelk, H.; Herrmann, R.; Pruss, N.; Freude, D.; Pfeifer, H.

    1989-01-01

    The influence of boron on superconducting properties of Y 1-x B x Ba 2 Cu 3 O 7-δ with x = 0 to 0.4 is studied. The analysis of 11 B NMR spectra and measurements of electric conductivity as a function of temperature show that boron is not incorporated into the YBa 2 Cu 3 O 7-δ framework on yttrium positions. (author)

  16. Study of yttrium 4-nitrocinnamate to promote surface interactions with AS1020 steel

    Energy Technology Data Exchange (ETDEWEB)

    Hien, P.V. [Department of Chemical Engineering, Bach Khoa University, VNU-HCM, 268 Ly Thuong Kiet Street, District 10, Ho Chi Minh City (Viet Nam); Vu, N.S.H.; Thu, V.T.H. [Faculty of Physics and Engineering Physics, University of Science, 227 Nguyen Van Cu Street, District 5, Ho Chi Minh City (Viet Nam); Somers, A. [Institute for Frontier Materials, Deakin University, Geelong, Victoria 3220 (Australia); Nam, N.D., E-mail: namnd@pvu.edu.vn [PetroVietnam University, 762 Cach Mang Thang Tam Street, Long Toan Ward, Ba Ria City, Ba Ria—Vung Tau Province (Viet Nam)

    2017-08-01

    Highlights: • Yttrium 4-nitrocinnamate is a new corrosion inhibitor alternative to chromate technologies. • The inhibition performance is increased with increase of the inhibitor concentration. • Yttrium 4-nitrocinnamate mitigates corrosion by promoting random distribution of minor anodes. • Yttrium 4-nitrocinnamate is a good candidate for substitution of chromate inhibitors. - Abstract: Yttrium 4-nitrocinnamate (Y(4-NO{sub 2}Cin){sub 3}) was added to an aqueous chloride solution and studied as a possible corrosion inhibition system. Electrochemical techniques and surface analysis have been powerful tools to better understand the corrosion and inhibition processes of mild steel in 0.01 M NaCl solution. A combination of scanning electron microscopy (SEM), atomic force microscopy (AFM), attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR), X-ray photoelectron spectroscopy (XPS), Potentiodynamic polarization (PD), electrochemical impedance spectroscopy (EIS) and wire beam electrode (WBE) techniques was found to be useful in the characterization of this system. The result indicated that Y(4-NO{sub 2}Cin){sub 3} is able to effectively inhibit corrosion at a low concentration of 0.45 mM. Surface analysis clearly shows that the surface of steel coupons exposed to Y(4-NO{sub 2}Cin){sub 3} solution remained uniform and smooth, whereas the surface of steel coupons exposed to solution without inhibitor addition was severely corroded. The results suggest that Y(4-NO{sub 2}Cin){sub 3} behaves as a mixed inhibitor and mitigates corrosion by promoting random distribution of minor anodes. These are attributed to the formation of metal species bonding to the 4-nitrocinnamate component and hydrolysis of the Y(4-NO{sub 2}Cin){sub 3} to form oxide/hydroxides as a protective film layer.

  17. Addition compounds of lanthamide (III) and yttrium (III) hexafluorophosphates and N,N - dimethylformamide

    International Nuclear Information System (INIS)

    Braga, L.S.P.

    1983-01-01

    Addition compounds of lanthanide (III) and yttrium (III) hexafluorophosphates and N-N-Dimetylformamide are described to characterize the complexes, elemental analysis, melting ranges, molar conductance measurements, X-ray powder patters infrared and Raman spectra, TG and DTA curves, are studied. Information concerning the decomposition of the adducts through the thermogravimetric curves and the differential thermal analysis curves is obtained. (M.J.C.) [pt

  18. Preparation and characterization of Yttrium-Aluminium garnet (Y3Al5O12)

    International Nuclear Information System (INIS)

    Ruzicka, J.; Niznansky, D.; Houzvicka, J.; Nikl, M.; Cerny, R.

    2009-01-01

    This work deals with the preparation of powders and transparent yttrium aluminium garnet (Y 3 Al 5 O 12 - YAG) from nanopowders. Stoichiometric amounts of nanocrystalline Al 2 O 3 and Y 2 O 3 were mixed and chemically pretreated using different basic agents and using ultrasonic bath. Resulting mixture was dried, pressed and heated up to 1750°C. Final material was characterized by X-ray diffraction, DTA and optical and electron microscopy

  19. A study of the dynamics of hydrogen in yttrium using inelastic neutron scattering

    Energy Technology Data Exchange (ETDEWEB)

    Bennington, S M; Benham, M J; Ross, D K [Birmingham Univ. (UK). School of Physics and Space Research; Taylor, A D; Bowden, Z A [Rutherford Appleton Lab., Chilton (UK)

    1989-01-01

    The results of several high resolution inelastic scattering experiments on {alpha}-phase yttrium-hydrogen are presented including measurements of energy levels up to the fourth and a study of the splitting of certain states due to hydrogen-hydrogen interactions. An attempt is made to model the energy levels by using perturbed simple harmonic oscillator wavefunctions. This can account for most of the major features of the spectrum. (orig.).

  20. Thermodynamic Functions of Yttrium Trifluoride and Its Dimer in the Gas Phase

    Science.gov (United States)

    Osina, E. L.; Kovtun, D. M.

    2018-05-01

    New calculations of the functions for YF3 and Y2F6 in the gas phase using quantum-chemical calculations by MP2 and CCSD(T) methods are performed in connection with the ongoing work on obtaining reliable thermodynamic data of yttrium halides. The obtained values are entered in the database of the IVTANTERMO software complex. Equations approximating the temperature dependence of the reduced Gibbs energy in the T = 298.15-6000 K range of temperatures are presented.

  1. Purification in the interaction between yttria mould and Nb-silicide-based alloy during directional solidification: A novel effect of yttrium

    International Nuclear Information System (INIS)

    Ma, Limin; Tang, Xiaoxia; Wang, Bin; Jia, Lina; Yuan, Sainan; Zhang, Hu

    2012-01-01

    Nb-silicide-based alloys were directionally solidified in yttria moulds. As a result of thermal dissociation of yttria, the alloys were slightly contaminated with oxygen, which caused a competitive oxidation between yttrium and hafnium. The addition of 0.15 at.% yttrium reduced the oxygen increment by 42%, because the buoyant inclusions concentrated around the top surface. The yttrium addition caused a significant purification of the interaction between the yttria mould and the Nb-silicide-based alloys during the directional solidification.

  2. Yttrium and lanthanides in human lung fluids, probing the exposure to atmospheric fallout

    Energy Technology Data Exchange (ETDEWEB)

    Censi, P., E-mail: censi@unipa.it [Dipartimento C.F.T.A., Universita di Palermo, Via Archirafi, 36 90123 - Palermo (Italy); I.A.M.C.-CNR - UOS di Capo Granitola, Via faro, 1 - 91026 Torretta Granitola, Campobello di Mazara (TP) (Italy); En.Bio.Tech. - Via Aquileia, 35 90100 Palermo (Italy); Tamburo, E. [Dipartimento C.F.T.A., Universita di Palermo, Via Archirafi, 36 90123 - Palermo (Italy); Speziale, S. [Deutsches GeoForschungsZentrum, Telegrafenberg, Potsdam, 14473 (Germany); Zuddas, P. [Institut Genie de l' Environnement et Ecodeveloppement and Departement Sciences de la Terre, UMR 5125, Universite Claude Bernard Lyon 1, 2 rue R. Dubois, Bat GEODE 69622 Villeurbanne Cedex (France); Randazzo, L.A. [Dipartimento C.F.T.A., Universita di Palermo, Via Archirafi, 36 90123 - Palermo (Italy); I.A.M.C.-CNR - UOS di Capo Granitola, Via faro, 1 - 91026 Torretta Granitola, Campobello di Mazara (TP) (Italy); En.Bio.Tech. - Via Aquileia, 35 90100 Palermo (Italy); Institut Genie de l' Environnement et Ecodeveloppement and Departement Sciences de la Terre, UMR 5125, Universite Claude Bernard Lyon 1, 2 rue R. Dubois, Bat GEODE 69622 Villeurbanne Cedex (France); Punturo, R. [Dipartimento di Scienze Geologiche, Universita di Catania, Corso Italia, 55 - 95129 Catania (Italy); Cuttitta, A. [I.A.M.C.-CNR - UOS di Capo Granitola, Via faro, 1 - 91026 Torretta Granitola, Campobello di Mazara (TP) (Italy); Arico, P. [Dipartimento C.F.T.A., Universita di Palermo, Via Archirafi, 36 90123 - Palermo (Italy)

    2011-02-28

    Inhalation of airborne particles can produce crystallization of phosphatic microcrysts in intraaveolar areas of lungs, sometimes degenerating into pulmonary fibrosis. Results of this study indicate that these pathologies are induced by interactions between lung fluids and inhaled atmospheric dust in people exposed to volcanic dust ejected from Mount Etna in 2001. Here, the lung solid-liquid interaction is evaluated by the distribution of yttrium and lanthanides (YLn) in fluid bronchoalveolar lavages on selected individuals according the classical geochemical approaches. We found that shale-normalised patterns of yttrium and lanthanides have a 'V shaped' feature corresponding to the depletion of elements from Nd to Tb when compared to the variable enrichments of heavy lanthanides, Y, La and Ce. These features and concurrent thermodynamic simulations suggest that phosphate precipitation can occur in lungs due to interactions between volcanic particles and fluids. We propose that patterns of yttrium and lanthanides can represent a viable explanation of some pathology observed in patients after prolonged exposure to atmospheric fallout and are suitable to become a diagnostic parameter of chemical environmental stresses.

  3. The influence of implanted yttrium on the cyclic oxidation behaviour of 304 stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Riffard, F. [Laboratoire Vellave sur l' Elaboration et l' Etude des Materiaux (LVEEM), CNRS-EA 3864, Universite Blaise Pascal Clermont-Fd II, 8 rue J.B. Fabre, B. P. 219, 43006 Le Puy-en-Velay (France)]. E-mail: riffard@iut.u-clermont1.fr; Buscail, H. [Laboratoire Vellave sur l' Elaboration et l' Etude des Materiaux (LVEEM), CNRS-EA 3864, Universite Blaise Pascal Clermont-Fd II, 8 rue J.B. Fabre, B. P. 219, 43006 Le Puy-en-Velay (France); Caudron, E. [Laboratoire Vellave sur l' Elaboration et l' Etude des Materiaux (LVEEM), CNRS-EA 3864, Universite Blaise Pascal Clermont-Fd II, 8 rue J.B. Fabre, B. P. 219, 43006 Le Puy-en-Velay (France); Cueff, R. [Laboratoire Vellave sur l' Elaboration et l' Etude des Materiaux (LVEEM), CNRS-EA 3864, Universite Blaise Pascal Clermont-Fd II, 8 rue J.B. Fabre, B. P. 219, 43006 Le Puy-en-Velay (France); Issartel, C. [Laboratoire Vellave sur l' Elaboration et l' Etude des Materiaux (LVEEM), CNRS-EA 3864, Universite Blaise Pascal Clermont-Fd II, 8 rue J.B. Fabre, B. P. 219, 43006 Le Puy-en-Velay (France); Perrier, S. [Laboratoire Vellave sur l' Elaboration et l' Etude des Materiaux (LVEEM), CNRS-EA 3864, Universite Blaise Pascal Clermont-Fd II, 8 rue J.B. Fabre, B. P. 219, 43006 Le Puy-en-Velay (France)

    2006-03-15

    High-temperature alloys are frequently used in power plants, gasification systems, petrochemical industry, combustion processes and in aerospace applications. Depending on the application, materials are subjected to corrosive atmospheres and thermal cycling. In the present work, thermal cycling was carried out in order to study the influence of implanted yttrium on the oxide scale adherence on 304 steel specimens oxidised in air at 1273 K. In situ X-ray diffraction indicates that the oxides formed at 1273 K are different on blank specimens compared to implanted specimens. Glancing angle XRD allows to analyse the oxide scale composition after cooling to room temperature. Experimental results show that yttrium implantation at a nominal dose of 10{sup 17} ions cm{sup -2} does not improve significantly the cyclic oxidation behaviour of the austenitic AISI 304 steel. However, it appears that yttrium implantation remarkably enhance the oxidation resistance during isothermal oxidation. It reduces the transient oxidation stage and the parabolic oxidation rate constant by one order of magnitude.

  4. Spark plasma sintering of tungsten-yttrium oxide composites from chemically synthesized nanopowders and microstructural characterization

    International Nuclear Information System (INIS)

    Yar, M.A.; Wahlberg, Sverker; Bergqvist, Hans; Salem, H.G.; Johnsson, Mats; Muhammed, Mamoun

    2011-01-01

    Nano-crystalline W-1%Y 2 O 3 (wt.%) powder was produced by a modified solution chemical reaction of ammonium paratungstate (APT) and yttrium nitrate. The precursor powder was found to consist of particles of bimodal morphology i.e. large APT-like particles up to 20 μm and rectangular yttrium containing ultrafine plates. After thermal processing tungsten crystals were evolved from W-O-Y plate like particles. spark plasma sintering (SPS) was used to consolidate the powder at 1100 and 1200 deg. C for different holding times in order to optimize the sintering conditions to yield high density but with reduced grain growth. Dispersion of yttrium oxide enhanced the sinterability of W powder with respect to lanthanum oxide. W-1%Y 2 O 3 composites with sub-micron grain size showed improved density and mechanical properties as compared to W-La 2 O 3 composites. Sample sintered in two steps showed improved density, due to longer holding time at lower temperature (900 deg. C) and less grain growth due to shorter holding time at higher temperature i.e. 1 min at 1100 deg. C.

  5. Cold laser machining of nickel-yttrium stabilised zirconia cermets: Composition dependence

    International Nuclear Information System (INIS)

    Sola, D.; Gurauskis, J.; Pena, J.I.; Orera, V.M.

    2009-01-01

    Cold laser micromachining efficiency in nickel-yttrium stabilised zirconia cermets was studied as a function of cermet composition. Nickel oxide-yttrium stabilised zirconia ceramic plates obtained via tape casting technique were machined using 8-25 ns pulses of a Nd: YAG laser at the fixed wavelength of 1.064 μm and a frequency of 1 kHz. The morphology of the holes, etched volume, drill diameter, shape and depth were evaluated as a function of the processing parameters such as pulse irradiance and of the initial composition. The laser drilling mechanism was evaluated in terms of laser-material interaction parameters such as beam absorptivity, material spallation and the impact on the overall process discussed. By varying the nickel oxide content of the composite the optical absorption (-value is greatly modified and significantly affected the drilling efficiency of the green state ceramic substrates and the morphology of the holes. Higher depth values and improved drilled volume upto 0.2 mm 3 per pulse were obtained for substrates with higher optical transparency (lower optical absorption value). In addition, a laser beam self-focussing effect is observed for the compositions with less nickel oxide content. Holes with average diameter from 60 μm to 110 μm and upto 1 mm in depth were drilled with a high rate of 40 ms per hole while the final microstructure of the cermet obtained by reduction of the nickel oxide-yttrium stabilised zirconia composites remained unchanged.

  6. Influence of radiant heating treatments on fusion of high-temperature superconducting yttrium ceramics

    International Nuclear Information System (INIS)

    Bitenbaev, M.I.; Polyakov, A.I.

    1999-01-01

    Regardless of the fact that the materials made of HTSC-ceramics are promising, there is no any information about their successful practical application in publications. To our opinion, it is explained by the fact, first of all, that the conservative technologies of the powder metallurgy do not allow producing HTSC systems with excellent operating performance (structure homogeneity, long-term stability of Sc properties and etc.). This report presents outcomes of experiments on fusion of yttrium ceramics containing raw components irradiated by g-rays 60 Co under the temperature exceeding 500 degrees C. HTSC properties of ceramics were studied according to their differential spectra of radio-frequency (RF) field absorption. The RF absorption spectrum of yttrium ceramics samples produced according to conservative technology is sufficiently permitted triplet with the Sc transition temperatures range of 80 K, 90 K, 95 K. Irradiation under the increased temperatures and mechanical limitation allow producing samples of yttrium HTSC-ceramics with sufficient homogeneous structure and superconducting properties that are stable to air conditions for not less than one year

  7. Yttrium-90 microspheres for the treatment of hepatocellular carcinoma: A review

    International Nuclear Information System (INIS)

    Salem, Riad; Hunter, Russell D.

    2006-01-01

    To present a critical review of yttrium-90 (TheraSphere) for the treatment of hepatocellular carcinoma (HCC). Medical literature databases (Medline, Cochrane Library, and CANCERLIT) were searched for available literature concerning the treatment of HCC with TheraSphere. These publications were reviewed for scientific and clinical validity. Studies pertaining to the use of yttrium-90 for HCC date back to the 1960s. The results from the early animal safety studies established a radiation exposure range of 50-100 Gy to be used in human studies. Phase I dose escalation studies followed, which were instrumental in delineating radiation dosimetry and safety parameters in humans. These early studies emphasized the importance of differential arteriolar density between hypervascular HCC and surrounding liver parenchyma. Current trends in research have focused on advancing techniques to safely implement this technology as an alternative to traditional methods of treating unresectable HCC, such as external beam radiotherapy, conformal beam radiotherapy, ethanol ablation, trans-arterial chemoembolization, and radiofrequency ablation. Yttrium-90 (TheraSphere) is an outpatient treatment option for HCC. Current and future research should focus on implementing multicenter phase II and III trials comparing TheraSphere with other therapies for HCC

  8. Electrochemical corrosion of lanthanum chromite and yttrium chromite in coal slag

    Energy Technology Data Exchange (ETDEWEB)

    Marchant, D.D.; Bates, J.L.

    1981-01-01

    Lanthanum chromites have long been considered as electrodes for magnetohydrodynamic (MHD) generator channels. These chromites, when doped with divalent ions such as Ca, Mg or Sr, have adequate electronic and electrical conductivity (2), and melting points greater than 2500/sup 0/K. However, above approx. 1850/sup 0/K, selective vapor loss of chromium results in the formation of a La/sub 2/O/sub 3/ phase. The La/sub 2/O/sub 3/ is hydroscopic at room temperature, resulting in a large volume change and loss of mechanical integrity when exposed to H/sub 2/O. The analogous yttrium chromites have thermal and electrical properties similar to that for the lanthanum chromites. Although vapor loss of Cr results in the formation of Y/sub 2/O/sub 3/, this oxide does not hydrate. Corrosion studies of yttrium chromite compositions show that doped YCrO/sub 3/ may be a viable MHD electrode. An electrochemical corrosion study of both magnesium-doped lanthanum and yttrium chromites in synthetic coal slag electrolytes is described. Possible chemical and electrochemical degradation phenomena, as well as the relative rates of corrosion are emphasized.

  9. Yttrium-90 microspheres for the treatment of hepatocellular carcinoma: a review.

    Science.gov (United States)

    Salem, Riad; Hunter, Russell D

    2006-01-01

    To present a critical review of yttrium-90 (TheraSphere) for the treatment of hepatocellular carcinoma (HCC). Medical literature databases (Medline, Cochrane Library, and CANCERLIT) were searched for available literature concerning the treatment of HCC with TheraSphere. These publications were reviewed for scientific and clinical validity. Studies pertaining to the use of yttrium-90 for HCC date back to the 1960s. The results from the early animal safety studies established a radiation exposure range of 50-100 Gy to be used in human studies. Phase I dose escalation studies followed, which were instrumental in delineating radiation dosimetry and safety parameters in humans. These early studies emphasized the importance of differential arteriolar density between hypervascular HCC and surrounding liver parenchyma. Current trends in research have focused on advancing techniques to safely implement this technology as an alternative to traditional methods of treating unresectable HCC, such as external beam radiotherapy, conformal beam radiotherapy, ethanol ablation, trans-arterial chemoembolization, and radiofrequency ablation. Yttrium-90 (TheraSphere) is an outpatient treatment option for HCC. Current and future research should focus on implementing multicenter phase II and III trials comparing TheraSphere with other therapies for HCC.

  10. Electrochemical separation of cerium and yttrium in molten chlorides on liquid-metallic electrodes

    International Nuclear Information System (INIS)

    Yamshchikov, L.F.; Lebedev, V.A.; Nichkov, I.F.

    1978-01-01

    An estimating calculation of the coefficients of separation of cerium and yttrium in the process of electrolysis in molten salts on liquid electrodes of aluminium, gallium, indium, lead, tin, antimonium and zinc is carried out. The calculation of the separation coefficients was carried out according to the known values of activation coefficients of cerium and yttrium in fusible metals. The electrolysis was carried out at 973 K in the argon air in the cell with an eutectic mixture of NaCl and KCl as an elactrolyte. It is shown that the salten phase is concentrated by yttrium, and the melallic one- by cerium on all the electrodes. The value of the separation coefficient of Ce and Y is considerably high and continuously increases on the fusible metals in the Zn, In, Ga, Al, Pb, Sn, Sb series. The experimental values of the separation coefficients practically coincide with the theoretically calculated ones, testifying to the possibility of the effective separation of elements even in a single-staged possibility of the effective separation of elements even in a single-staged process. An electrolysis of molten salts is not inferior in its selectivity to the universally recognized methods of the fine purification of substances permitting to separate Ce and Y with the Ksub(sep) approximately equal to 10

  11. Quantum efficiency of silica-coated rare-earth doped yttrium silicate

    International Nuclear Information System (INIS)

    Cervantes-Vásquez, D.; Contreras, O.E.; Hirata, G.A.

    2013-01-01

    The photoluminescent properties of rare earth-activated white-emitting Y 2 SiO 5 :Ce,Tb nanocrystalline phosphor prepared by two different methods, pressure-assisted combustion synthesis and sol–gel, were studied. The synthesized phosphor samples were post-annealed at 1373 K and 1623 K in order to obtain the X1-Y 2 SiO 5 and X2-Y 2 SiO 5 phases, respectively, which were confirmed by X-ray diffraction measurements. Photoluminescence analysis showed the contribution of two blue-emission bands within the 380–450 nm region originating from 5d–4f transitions in Ce 3+ ions and a well-defined green emission of Tb 3+ ions located at 545 nm corresponding to 5 D 4 → 7 F 5 electronic transitions. Thereafter, Y 2 SiO 5 :Ce,Tb powders were coated with colloidal silica in order to investigate the effect of silica coatings on their luminescent properties. Absolute fluorescence quantum efficiency measurements were carefully performed, which revealed an increase of 12% of efficiency in coated compared with bare-Y 2 SiO 5 :Ce,Tb phosphor. -- Highlights: • Y 2 SiO 5 :Ce,Tb phosphor powders were successfully coated with colloidal silica. • Post-annealing treatments improved the quantum efficiency of silica-coated Y 2 SiO 5 :Ce,Tb phosphors. • Absolute fluorescence quantum efficiency measurements showed an increase of 12%

  12. Gamma ray induced thermoluminescence studies of yttrium (III oxide nanopowders doped with gadolinium

    Directory of Open Access Journals (Sweden)

    Raunak Kumar Tamrakar

    2014-10-01

    Full Text Available Y2O3:Gd3+ nanophosphor was prepared by the solid state reaction method. Systematic studies have been done to investigate the structural and optical properties of the gadolinium doped Y2O3 phosphor. The prepared phosphor was characterized by using X-ray diffractometer (XRD, scanning electron microscopy (SEM, transmission electron microscopy and UV–VIS–NIR spectrophotometer. The XRD patterns reveal that these prepared phosphors have cubic phase crystal structure. SEM and TEM images showed uniform doping of the material over the entire materials. The energy band gap for gadolinium doped Y2O3 phosphor was revealed from the optical studies and was found to 5.1 eV. The prepared phosphors were also examined by thermoluminescence technique. The kinetic parameters like trap depth, frequency factor were calculated by using the Peak shape method, which are discussed in details. The TL Glow curves were fitted in CGCD (computerized glow curve convolution deconvolution technique & trapping parameters calculated. The TL parameters such as activation energy for deconvoluted peak were found in the range of 0.82–2.24 eV. The frequency factor is of the order of between of 1.78 × 1012 and 9.84 × 1020 s−1.

  13. 46 CFR 153.558 - Special requirements for phosphoric acid.

    Science.gov (United States)

    2010-10-01

    ... CARGOES SHIPS CARRYING BULK LIQUID, LIQUEFIED GAS, OR COMPRESSED GAS HAZARDOUS MATERIALS Design and... containment system must be: (a) Lined with natural rubber or neoprene; (b) Lined with a material approved for phosphoric acid tanks by the Commandant (CG-522); or (c) Made of a stainless steel that resists corrosion by...

  14. Characterization of metallic surfaces in phosphorous-bronze ordered packings

    International Nuclear Information System (INIS)

    Sandru, Claudia; Titescu, Gh.

    1997-01-01

    Copper and its alloys, particularly the phosphorous bronze, are characterized by a high water wettability as compared with other materials. This feature led to utilization of phosphorous bronze in fabrication of contact elements, a packing type equipping the distillation columns. For heavy water separation by isotopic distillation under vacuum, ordered packings of phosphorous bronze networks were fabricated. The superior performances of these packings are determined by the material and also by the geometrical form and the state of the metallic surface. Thus, a procedure of evaluating the wettability has been developed, based on tests of the network material. The results of the tests constitute a criterion of rating the functional performances of packings, particularly of their efficiencies. Also, investigation techniques of the chemical composition and of the thickness of superficial layer on the packing were developed. It was found that the packing surface presents a layer of about 5-20 μm formed mainly by oxides of copper, tin, and, depending on the packing treatment, of oxides of other elements coming from the treatment agent. The paper presents characterization of phosphorous bronze treated with potassium permanganate, a specific treatment for improving the functional performances of the packings used in the heavy water concentration and re-concentration installations

  15. Comparison of different phosphorous adsorption models in acid ...

    African Journals Online (AJOL)

    This study was designed to compare the phosphorous fixation capacity of three soils series named Tyele, Minkonmingon and Mekoto in the south region of Cameroon and to determine the soil properties that are the main predictors of the P activity of those soils. Five adsorption equations viz. Linear, Langmuir, Van Huay, ...

  16. Fluoride removal performance of phosphoric acid treated lime ...

    African Journals Online (AJOL)

    Fluoride in drinking water above permissible levels is responsible for dental and skeletal fluorosis. In this study, removal of fluoride ions from water using phosphoric acid treated lime was investigated in continuous and point-of-use system operations. In the continuous column operations, fluoride removal performance was ...

  17. Method for recovery of uranium from phosphoric acid

    International Nuclear Information System (INIS)

    Duarte Neto, J.

    1984-01-01

    The results of a method for recuperation of uranium from phosphoric acid by humid way are presented. The extracting mixture used was di-ethylhexylphosphoric acid (D 2 EHPA) and trioctylphosphine oxide (TOPO). An installation in micro-pilot scale was made to get and visualize data for continuous process. (M.A.C.) [pt

  18. Effect of nitrogen and phosphorous on Farm Plantations in various ...

    African Journals Online (AJOL)

    use

    of different suitable species of plants. The results of the soil analysis of various Agro ecological zones and the consequent recommendation of the associated suitable species, aids the agrofarmers to pick out the best possible option. Key words: Soil analysis, agro-ecological zones, agroforestry, nitrogen and phosphorous.

  19. Corrosion of graphite composites in phosphoric acid fuel cells

    Science.gov (United States)

    Christner, L. G.; Dhar, H. P.; Farooque, M.; Kush, A. K.

    1986-01-01

    Polymers, polymer-graphite composites and different carbon materials are being considered for many of the fuel cell stack components. Exposure to concentrated phosphoric acid in the fuel cell environment and to high anodic potential results in corrosion. Relative corrosion rates of these materials, failure modes, plausible mechanisms of corrosion and methods for improvement of these materials are investigated.

  20. Natural Radiation in byproducts of the production of phosphoric acid

    International Nuclear Information System (INIS)

    Silveira, Marcilei A. Guazzelli da; Cardoso, L.L.; Medina, N.H.

    2014-01-01

    Natural radiation is the largest source of radiation exposure to which man is subject. It is formed basically by cosmic radiation and the radionuclides present in the Earth crust, as 40 K and the elements of the decay series of 232 Th and 238 U. Phosphate ores, which constitutes the raw material for the production of phosphoric acid, have a high rate of natural radiation from the decay series of 232 Th and 238 U. Phosphogypsum, which is naturally radioactivity, is a by-product of the production of phosphoric acid by the wet method. For each ton of phosphoric acid it is produced about 4.5 tons of phosphogypsum. This work presents the analysis of samples collected in all stages of the manufacturing process of phosphoric acid, which generates the phosphogypsum. Gamma-ray spectrometry was used to measure the concentration of the elements of the decay series of 232 Th and 238 U. All analyzed samples showed a high concentration of radionuclides, promoting the need for further steps in the process in order to reduce the presence of such radionuclides in the phosphogypsum. The results indicate the radionuclide 238 U has higher contribution in some samples of the intermediate stages of the process. All samples exceeded the international average range of human exposure to terrestrial gamma radiation, which is 0.3 to 1.0 mSv/year. (author)

  1. Extraction studies on rare earths using dinonyl phenyl phosphoric acid

    International Nuclear Information System (INIS)

    Anitha, M.; Singh, D.K.; Kotekar, M.K.; Vijayalakshmi, R.; Singh, H.

    2011-01-01

    Rare earths are widely used in phosphor materials, magnetic substances, alloys, catalyst, lasers, superconductors, solid oxide fuel cells and in nuclear applications. The high value of these elements depends on their effective separation into high purity compounds. The separation into individual rare earths is very difficult to achieve, due to the very low separation factors between two adjacent rare earths arising due to similar chemical properties. Taking the advantage of variation in basicity, the separation is generally accomplished by solvent extraction or ion exchange. There are several references on the separation of rare earth in different media employing various types of extractants such as 2-ethylhexyl 2-ethyhexylphosphonic acid (EHEHPA) and di-2-ethyl hexyl phosphoric acid (D2EHPA) which have been widely used for the separation and purification of rare earths. Dinonyl phenyl phosphoric acid (DNPPA) is an organo phosphorus extractant (pKa = 2.54) and is an aromatic analogue of D2EHPA, which extracts metal ion by cation exchange mechanism. DNPPA was explored to recover rare earths from phosphate media such as wet process phosphoric acid and merchant grade acid. However, there is no information available in literature on DNPPA for RE extraction from chloride medium. Therefore, an attempt has been made in the present study to investigate the feasibility of using DNPPA for extraction of La(III), Dy(III) and Y(III) from chloride medium

  2. Spectral modulation through controlling anions in nanocaged phosphors

    NARCIS (Netherlands)

    Bian, H.; Liu, Y.; Yan, D.; Zhu, H.; Liu, C.; Xu, C.S.; Liu, Y.; Zhang, H.; Wang, X.

    2013-01-01

    A new approach has been proposed and validated to modulate the emission spectra of europium-doped 12CaO center dot 7Al(2)O(3) phosphors by tuning the nonradiative and radiative transition rates, realized by controlling the sort and amount of the encaged anions. A single wavelength at 255 nm can

  3. Kinetic parameters and TL mechanism in cadmium tetra borate phosphor

    International Nuclear Information System (INIS)

    Annalakshmi, O.; Jose, M.T.; Sridevi, J.; Venkatraman, B.; Amarendra, G.; Mandal, A.B.

    2014-01-01

    Polycrystalline powder samples of cadmium tetra borate were synthesized by a simple solid state sintering technique and gamma irradiated sample showed a simple Thermoluminescence (TL) glow peak around 460 K. The TL kinetic parameters of gamma irradiated phosphor were determined by initial rise (IR), isothermal decay (ID), peak shape (PS), variable heating rate (VHR) and glow curve de-convolution method. The kinetic parameters such as activation energy (E), frequency factor (s) and order of kinetics (b) were calculated by IR, ID, PS and VHR methods are in the order of ∼1.05 eV, 10 9 –10 12 s −1 and 1.58, respectively. From the results of TL and PL emission studies carried out on the phosphor revealed that the defect centers related to TL is different from that for PL. EPR measurements were carried out to identify the defect centers formed in cadmium tetra borate phosphor on gamma irradiation. Based on EPR studies the mechanism for TL process in cadmium tetra borate is proposed in this paper -- Highlights: • Polycrystalline powder samples of undoped cadmium tetra borate synthesized. • Cadmium tetra borate phosphor exhibits a dosimetric peak at 458 K. • Kinetic parameters of the trap responsible for TL evaluated. • TL mechanism is proposed from TL to EPR correlation studies

  4. Kinetic parameters and TL mechanism in cadmium tetra borate phosphor

    Energy Technology Data Exchange (ETDEWEB)

    Annalakshmi, O. [Radiological Safety Division, Materials Physics Division, Indira Gandhi Centre for Atomic Research, Kalpakkam-603102 (India); Jose, M.T., E-mail: mtj@igcar.gov.in [Radiological Safety Division, Materials Physics Division, Indira Gandhi Centre for Atomic Research, Kalpakkam-603102 (India); Sridevi, J. [Central Leather Research Institute, Council of Scientific and Industrial Research, Chennai 600 020, Tamilnadhu (India); Venkatraman, B. [Radiological Safety Division, Materials Physics Division, Indira Gandhi Centre for Atomic Research, Kalpakkam-603102 (India); Amarendra, G. [Materials Physics Division, Indira Gandhi Centre for Atomic Research, Kalpakkam-603102 (India); Mandal, A.B. [Central Leather Research Institute, Council of Scientific and Industrial Research, Chennai 600 020, Tamilnadhu (India)

    2014-03-15

    Polycrystalline powder samples of cadmium tetra borate were synthesized by a simple solid state sintering technique and gamma irradiated sample showed a simple Thermoluminescence (TL) glow peak around 460 K. The TL kinetic parameters of gamma irradiated phosphor were determined by initial rise (IR), isothermal decay (ID), peak shape (PS), variable heating rate (VHR) and glow curve de-convolution method. The kinetic parameters such as activation energy (E), frequency factor (s) and order of kinetics (b) were calculated by IR, ID, PS and VHR methods are in the order of ∼1.05 eV, 10{sup 9}–10{sup 12} s{sup −1} and 1.58, respectively. From the results of TL and PL emission studies carried out on the phosphor revealed that the defect centers related to TL is different from that for PL. EPR measurements were carried out to identify the defect centers formed in cadmium tetra borate phosphor on gamma irradiation. Based on EPR studies the mechanism for TL process in cadmium tetra borate is proposed in this paper -- Highlights: • Polycrystalline powder samples of undoped cadmium tetra borate synthesized. • Cadmium tetra borate phosphor exhibits a dosimetric peak at 458 K. • Kinetic parameters of the trap responsible for TL evaluated. • TL mechanism is proposed from TL to EPR correlation studies.

  5. Synthesis and luminescence properties of Eu"2"+ doped CaSO_4 phosphor

    International Nuclear Information System (INIS)

    Aghalte, G.A.; Dhoble, S.J.; Pawar, N.R.

    2016-01-01

    Eu"2"+ doped CaSO_4 Phosphor were synthesized by precipitation method. PL analysis of Eu"2"+ activated CaSO_4 phosphor exhibited characteristic emission properties; CaSO_4:Eu Phosphor has received considerable attention because of its high sensitivity to X-ray and λ ray irradiation. CaSO_4:Eu phosphor powder was successfully synthesized by the wet chemical co-precipitation method. The structure morphology and luminescent properties of the phosphor were characterized by X-ray diffraction, scanning electron microscopy and photoluminescence spectroscopy

  6. On the feasibility of infrared phosphors in super-slow particle searches

    International Nuclear Information System (INIS)

    Hagstrom, R.; Rugari, A.D.

    1984-01-01

    This chapter proposes that super-slow projectiles will produce ionization signals in media with narrow bandgaps. A specific choice of narrow bandgap phosphors is recommended which would be economically suitable for use as detectors. Topics considered include the possibilities for practical detectors, a description of detectors based on narrow bandgap phosphors, the experimental determination of relevant properties of narrow bandgap phosphors, and the observation of ionizing particles using narrow bandgap phosphors. It is determined that the temperature dependence of the glow of the phosphors is strong enough that a reduction of operating temperature by about 60 C could be sufficient to produce the desired signal to background ratio

  7. Investigation of the synergic effect of some neutral organophosphoric compounds on the extraction of uranium from phosphoric acid solutions by D1-(2-Ethyl Hexyl) phosphoric acid

    International Nuclear Information System (INIS)

    Stas, J.; Khorfan, S.; Koudsi, Y.

    1998-05-01

    The extraction of uranium (VI) from pure phosphoric acid media by D2EHPA/Kerosene has been studied. The mechanism of the extraction was found as follows: The logarithm of the equilibrium constant of the extraction (LogKex) was found (3.06), (3.32), (3.24), (3.3) for the following phosphoric acid concentrations respectively (1), (2), (3), (4) Mol/1, and the enthalpy change DELTA H was found (-100.68 kj/mol). (-76 kj/mol) for (1), (2) mol/1 phosphoric acid concentrations. The synergic effect of TOPO, TBP, and TBPI with DEHPA have been studied during the extraction of uranium from pure phosphoric acid and Syrian commercial phosphoric acid. The synergic effect increases as follows: TBP< TBPI<< TOPO (In pure phosphoric acid), TBPI approx TBP<< TOPO (In Syrian commercial phosphoric acid). The difficulty of extracting uranium (VI) from Syrian commercial phosphoric acid in comparison with pure phosphoric acid is due to the presence of several impurities capable of complexing uranium, and a small amounts of solid and organic matters, all these are factors which reduce the distribution coefficient of uranium. (Author)

  8. Effect of grinding on photostimuable phosphors for x-ray screens

    International Nuclear Information System (INIS)

    Rao, R.B.

    1988-01-01

    Luminescence efficiency of a phosphor can be improved by minimizing the energy losses during excitation. The loss of excitation energy in the case of powdered samples is mainly due to scattering of incident radiation by the particles of phosphor. Thus, while considering the industrial applications of polycrystalline phosphors in lamps, screens, paints, etc., the effect of particle size on the light output has to be specially studied. It is very well established that the radiographic imaging with photostimuable (PS) phosphors has many advantages over conventional photographic film screens. In the new type of computer radiography, PS phosphors are to be used as memory materials for temporary storage of the x-ray image. Eu(2+) doped barium fluorohalide phosphors are most suitable for this purpose. The spatial resolution from the image plate can be improved to a certain extent with phosphors comprising fine particles. The fineness of the particles can be achieved by various means such as grinding, fast cooling after firing or incorporation of some flux materials during the firing processes. But the efficiency of the phosphor deteriorates with grinding. Fast cooling is a complicated process in the case of Eu(2+) doped phosphors. Incorporation of flux materials may change the characteristics of phosphor materials. In the present investigation, effect of grinding (ball milling) on particle size distribution, shape of the particles and luminescent properties of BaFCl phosphors have been studied

  9. Fabrication and electrical characterization of 15% yttrium-doped barium zirconate-nitrate freeze drying method combined with vacuum heating

    International Nuclear Information System (INIS)

    Imashuku, Susumu; Uda, Tetsuya; Nose, Yoshitaro; Awakura, Yasuhiro

    2011-01-01

    Research highlights: → Very fine 15% yttrium-doped barium zirconate powder of particle size about 30 nm was obtained by synthesizing at 500 deg. C in vacuum from powder mixed by the nitrate freeze-drying method. → Large and homogeneous grains of 15% yttrium-doped barium zirconate were easily obtained using the synthesized powder. → Grain boundary resistance was not inversely proportional to the grain size as theoretically expected. → Specific grain boundary conductivity varies with samples because impurities and/or evaporation loss of barium oxide might affect the grain-boundary resistance in 15% yttrium-doped barium zirconate. - Abstract: We applied a nitrate freeze-drying method to obtain a fine synthesized powder of 15% yttrium-doped barium zirconate. Fine 15% yttrium-doped barium zirconate powder of particle size about 30 nm was obtained by synthesizing at 500 deg. C in vacuum from a powder mixed by the nitrate freeze-drying method. However, we could not obtain such fine powder by synthesizing in air. Using the powder synthesized in vacuum, large and homogeneous grains of 15% yttrium-doped barium zirconate were easily obtained after sintering. Then, the bulk and grain boundary resistance were evaluated by AC 2-terminal measurement of sample in the form of bar and pellet and DC 4-terminal measurement of bar-shape sample. The grain boundary resistance was not inversely proportional to the grain size as theoretically expected. We concluded that specific grain boundary conductivity varies with samples. Some impurities, evaporation loss of barium oxide and/or other unexpected reasons might affect the grain boundary resistance in 15% yttrium-doped barium zirconate.

  10. Structural and luminescence properties of yellow Y3Al5012:Ce3+ thin film phosphors prepared by Pulsed Laser Deposition

    CSIR Research Space (South Africa)

    Dejene, FB

    2012-07-01

    Full Text Available of the phosphore/epoxy hybrid system is the difficulty of achieving uniform emission of white light from the LED. In order to overcome the challenges of using mixtures of phosphore powders and epoxies thin film phosphore has been used. In this study, YAG phosphore...

  11. Photoluminescence studies on holmium (III) and praseodymium (III) doped calcium borophosphate (CBP) phosphors

    Science.gov (United States)

    Reddy Prasad, V.; Damodaraiah, S.; Devara, S. N.; Ratnakaram, Y. C.

    2018-05-01

    Using solid state reaction method, Ho3+ and Pr3+ doped calcium borophosphate (CBP) phosphors were prepared. These phosphors were characterized using XRD, SEM, FT-IR, 31P solid state NMR, photoluminescence (PL) and decay profiles. Structural details were discussed from XRD and FT-IR spectra. From 31P NMR spectra of these phosphors, mono-phosphate complexes Q0-(PO43-) were observed. Photoluminescence spectra were measured for both Ho3+ and Pr3+ doped calcium borophosphate phosphors and the spectra were studied for different concentrations. Decay curves were obtained for the excited level, 5F4+5S2 of Ho3+ and 1D2 level of Pr3+ in these calcium borophosphate phosphors and lifetimes were measured. CIE color chromaticity diagrams are drawn for these two rare earth ions in calcium borophosphate phosphors. Results show that Ho3+ and Pr3+ doped CBP phosphors might be served as green and red luminescence materials.

  12. Encapsulation of strontium aluminate phosphors to enhance water resistance and luminescence

    International Nuclear Information System (INIS)

    Zhu Yong; Zeng Jianghua; Li Wenyu; Xu Li; Guan Qiu; Liu Yingliang

    2009-01-01

    Strontium aluminate SrAl 2 O 4 :Eu 2+ ,Dy 3+ phosphors are chemically unstable against water or even moisture. To enhance the water resistance of the phosphors, an encapsulation was performed by direct surface reactions with phosphoric acid (H 3 PO 4 ). The morphology, surface structure, surface element composition, water resistance, luminescence, and photoacoustic spectrum of the phosphors before and after encapsulation were discussed. Experimental results showed that phosphors were perfectly encapsulated by amorphous layers in nanoscale and crystalline layers in microscale under different conditions. The water resistance of phosphors was greatly enhanced by the two types of layer. More importantly, the amorphous layers enhanced the luminescence of phosphors markedly. The possible mechanism for the enhancements was also proposed.

  13. Preparation of red phosphor (Y, Gd)BO3:Eu by soft chemistry methods

    International Nuclear Information System (INIS)

    Cui Xiangzhong; Zhuang Weidong; Yu Zhijian; Xia Tian; Huang Xiaowei; Li Hongwei

    2008-01-01

    The three soft chemistry methods were employed to prepare the red phosphor (Y, Gd)BO 3 :Eu, such as coprecipitation-combustion method, salt assisted combustion method and emulsion method. The main factors affecting particle size, particle distribution and luminescent properties of the product were investigated in detail, and as a result, the preparation processes were optimized. The phosphors were characterized by X-ray diffraction (XRD), scanning electronic microscope (SEM), transmission electronic microscope (TEM) and vacuum ultraviolet (VUV) spectra. Results reveal that phosphors with different morphology, small particle size and high luminescence intensity could be obtained by soft chemistry methods. The difference between the luminescence properties of phosphors in this work and commercial rare earth borate phosphor is discussed. The phosphor with grain shape and high luminescence intensity could be prepared by coprecipitation-combustion method, nanophosphor could be prepared by salt assisted combustion method, and spherical phosphor with a narrow size distribution could be obtained by using emulsion method

  14. White light-emitting diodes (LEDs) using (oxy)nitride phosphors

    International Nuclear Information System (INIS)

    Xie, R-J; Hirosaki, N; Sakuma, K; Kimura, N

    2008-01-01

    (Oxy)nitride phosphors have attracted great attention recently because they are promising luminescent materials for phosphor-converted white light-emitting diodes (LEDs). This paper reports the luminescent properties of (oxy)nitride phosphors in the system of M-Si-Al-O-N (M = Li, Ca or Sr), and optical properties of white LEDs using a GaN-based blue LED and (oxy)nitride phosphors. The phosphors show high conversion efficiency of blue light, suitable emission colours and small thermal quenching. The bichromatic white LEDs exhibit high luminous efficacy (∼55 lm W -1 ) and the multi-phosphor converted white LEDs show high colour rendering index (Ra 82-95). The results indicate that (oxy)nitride phosphors demonstrate their superior suitability to use as down-conversion luminescent materials in white LEDs

  15. Nature of the bifunctional chelating agent used for radioimmunotherapy with yttrium-88 monoclonal antibodies: critical factors in determining in vivo survival and organ toxicity

    Energy Technology Data Exchange (ETDEWEB)

    Kozak, R.W.; Raubitschek, A.; Mirzadeh, S.; Brechbiel, M.W.; Junghaus, R.; Gansow, O.A.; Waldmann, T.A. (Center for Biologics Evaluation and Research, FDA, Bethesda, MD (USA))

    1989-05-15

    One factor that is critical to the potential effectiveness of radioimmunotherapy is the design of radiometal-chelated antibodies that will be stable in vivo. Stability in vivo depends on the condition that both the chelate linkage and radiolabeling procedures not alter antibody specificity and biodistribution. In addition, synthesis and selection of the chelating agent is critical for each radiometal in order to prevent inappropriate release of the radiometal in vivo. In the present study, we compare the in vivo stability of seven radioimmunoconjugates that use different polyaminocarboxylate chelating agents to complex yttrium-88 to the mouse anti-human interleukin-2 receptor monoclonal antibody, anti-Tac. Chelate linkage and radiolabeling procedures did not alter the immunospecificity of anti-Tac. In order to assess whether yttrium was inappropriately released from the chelate-coupled antibody in vivo, iodine-131-labeled and yttrium-88 chelate-coupled antibodies were simultaneously administered to the same animals to correlate the decline in yttrium and radioiodinated antibody activity. The four stable yttrium-88 chelate-coupled antibodies studied displayed similar iodine-131 and yttrium-88 activity, indicating minimal elution of yttrium-88 from the complex. In contrast, the unstable yttrium-88 chelate-coupled antibodies had serum yttrium-88 activities that declined much more rapidly than their iodine-131 activities, suggesting loss of the radiolabel yttrium-88 from the chelate. Furthermore, high rates of yttrium-88 elution correlated with deposition in bone. Four chelating agents emerged as promising immunotherapeutic reagents: isothiocyanate benzyl DTPA and its derivatives 1B3M, MX, and 1M3B.

  16. Improvement of the oxidation resistance of Tribaloy T-800 alloy by the additions of yttrium and aluminium

    International Nuclear Information System (INIS)

    Zhang, Y.-D.; Zhang, C.; Lan, H.; Hou, P.Y.; Yang, Z.-G.

    2011-01-01

    Research highlights: → The additions of yttrium (Y) reduced the oxidation rate of Tribaloy T-800 alloy. → Y promoted selective oxidation of Cr due to refinement of alloy phase size. → The oxidation rate was further reduced by Y plus Al with a protective Al 2 O 3 scale. → The positive effect of Y and Al being more pronounced at the higher temperature. - Abstract: The microstructures and oxidation behaviour of the modified Tribaloy T-800 alloys by additions of yttrium and yttrium plus aluminium have been studied. At the presence of yttrium alone, the oxidation rate decreased, and the selective oxidation of chromium was promoted, which was related to the refinement of alloy phase size. The addition of yttrium plus aluminium further reduced the oxidation rate. The selective oxidation of chromium and aluminium were both promoted significantly. The benefits were especially pronounced at 1000 o C, with the formation of protective alumina external layer and no internal oxides, which may be detrimental to the alloy mechanical property.

  17. Determination of the emission rate for the 14 MeV neutron generator with the use of radio-yttrium

    Directory of Open Access Journals (Sweden)

    Laszynska Ewa

    2015-06-01

    Full Text Available The neutron emission rate is a crucial parameter for most of the radiation sources that emit neutrons. In the case of large fusion devices the determination of this parameter is necessary for a proper assessment of the power release and the prediction for the neutron budget. The 14 MeV neutron generator will be used for calibration of neutron diagnostics at JET and ITER facilities. The stability of the neutron generator working parameters like emission and angular homogeneity affects the accuracy of calibration other neutron diagnostics. The aim of our experiment was to confirm the usefulness of yttrium activation method for monitoring of the neutron generator SODERN Model: GENIE 16. The reaction rate induced by neutrons inside the yttrium sample was indirectly measured by activation of the yttrium sample, and then by means of the γ-spectrometry method. The pre-calibrated HPGe detector was used to determine the yttrium radioactivity. The emissivity of neutron generator calculated on the basis of the measured radioactivity was compared with the value resulting from its electrical settings, and both of these values were found to be consistent. This allowed for a positive verification of the reaction cross section that was used to determine the reaction rate (6.45 × 10−21 reactions per second and the neutron emission rate (1.04 × 108 n·s−1. Our study confirms usefulness of the yttrium activation method for monitoring of the neutron generator.

  18. Phosphors for solid-state lighting: New systems, deeper understanding

    Science.gov (United States)

    Denault, Kristin Ashley

    We explore the structure-composition-property relationships in phosphor materials using a multitude of structural and optical characterization methods including high resolution synchrotron X-ray and neutron powder diffraction and total scattering, low-temperature heat capacity, temperature- and time-resolved photoluminescence, and density functional theory calculations. We describe the development of several new phosphor compositions and provide an in-depth description of the structural and optical properties. We show structural origins of improved thermal performance of photoluminescence and methods for determining structural rigidity in phosphor hosts that may lead to improved luminescent properties. New white light generation strategies are also explored. We begin by presenting the development of a green-yellow emitting oxyfluoride solid-solution phosphor Sr2Ba(AlO4F)1- x(SiO5)x:Ce3+. An examination of the host lattice, and the local structure around the Ce3+ activator ions points to how chemical substitutions play a crucial role in tuning the optical properties of the phosphor. The emission wavelength can be tuned from green to yellow by tuning the composition, x. Photoluminescent quantum yield is determined to be 70+/-5% for some of the examples in the series with excellent thermal properties. Phosphor-converted LED devices are fabricated using an InGaN LED and are shown to exhibit high color rendering white light. Next, we identify two new phosphor solid-solution systems, (Ba1- xSrx)9 Sc2Si6O24:Ce3+,Li+ and Ba9(Y1-ySc y)2Si6O24:Ce3+. The substitution of Sr for Ba in (Ba1-xSrx ) 9Sc2Si6O24:Ce 3+,Li + results in a decrease of the alkaline earth-oxygen bond distances at all three crystallographic sites, leading to changes in optical properties. The room temperature photoluminescent measurements show the structure has three excitation peaks corresponding to Ce3+ occupying the three independent alkaline earth sites. The emission of (Ba 1- xSrx) 9Sc2Si 6O24:Ce3

  19. Kinetic study of ion exchange in phosphoric acid chelating resin

    International Nuclear Information System (INIS)

    Brikci-Nigassa, Mounir; Hamouche, Hafida

    1995-11-01

    Uranium may be recovered as a by product of wet phosphoric acid using a method based on specific ion exchange resins. These resins called chelates contain amino-phosphonic functional groups. The resin studied in this work is a purolite S-940; uranium may be loaded on this resin from 30% P2O5 phosphoric acid in its reduced state. The influence of different parameters on the successive steps of the process have been studied in batch experiments: uranium reduction, loading and oxydation. Uranium may be eluted with ammonium carbonate and the resin regeneration may be done with hydrochloric acid.Ferric ions reduce the effective resin capacity considerably and inert fixation conditions are proposed to enhance uranium loading

  20. Polycrystalline Silicon Gettered by Porous Silicon and Heavy Phosphorous Diffusion

    Institute of Scientific and Technical Information of China (English)

    LIU Zuming(刘祖明); Souleymane K Traore; ZHANG Zhongwen(张忠文); LUO Yi(罗毅)

    2004-01-01

    The biggest barrier for photovoltaic (PV) utilization is its high cost, so the key for scale PV utilization is to further decrease the cost of solar cells. One way to improve the efficiency, and therefore lower the cost, is to increase the minority carrier lifetime by controlling the material defects. The main defects in grain boundaries of polycrystalline silicon gettered by porous silicon and heavy phosphorous diffusion have been studied. The porous silicon was formed on the two surfaces of wafers by chemical etching. Phosphorous was then diffused into the wafers at high temperature (900℃). After the porous silicon and diffusion layers were removed, the minority carrier lifetime was measured by photo-conductor decay. The results show that the lifetime's minority carriers are increased greatly after such treatment.

  1. X-ray image converters utilizing rare earth phosphor mixtures

    International Nuclear Information System (INIS)

    Rabatin, J.G.

    1982-01-01

    In an X-ray screen comprising a transparent support with a photographic film on each side, each film has a coating of a phosphor mixture comprising polyhedral Gd 2 O 2 S:Tb of average size 6 to 20 μ and plate-like LnOX:Tm of average size 2 to 12 μ wherein Ln=La or Gd, X=Cl or Br and Tm is present from 0.05 to 1 mole %. The mixture gives improved resolution and reduces the problem of light crossing over the transparent support. According to whether blue sensitive or green sensitive film is used, the ratio of phosphors is varied. U.V. absorbing and light reflecting layers may be incorporated in the structure. (author)

  2. Modeling Phosphorous Losses from Seasonal Manure Application Schemes

    Science.gov (United States)

    Menzies, E.; Walter, M. T.

    2015-12-01

    Excess nutrient loading, especially nitrogen and phosphorus, to surface waters is a common and significant problem throughout the United States. While pollution remediation efforts are continuously improving, the most effective treatment remains to limit the source. Appropriate timing of fertilizer application to reduce nutrient losses is currently a hotly debated topic in the Northeastern United States; winter spreading of manure is under special scrutiny. We plan to evaluate the loss of phosphorous to surface waters from agricultural systems under varying seasonal fertilization schemes in an effort to determine the impacts of fertilizers applied throughout the year. The Cayuga Lake basin, located in the Finger Lakes region of New York State, is a watershed dominated by agriculture where a wide array of land management strategies can be found. The evaluation will be conducted on the Fall Creek Watershed, a large sub basin in the Cayuga Lake Watershed. The Fall Creek Watershed covers approximately 33,000 ha in central New York State with approximately 50% of this land being used for agriculture. We plan to use the Soil and Water Assessment Tool (SWAT) to model a number of seasonal fertilization regimes such as summer only spreading and year round spreading (including winter applications), as well as others. We will use the model to quantify the phosphorous load to surface waters from these different fertilization schemes and determine the impacts of manure applied at different times throughout the year. More detailed knowledge about how seasonal fertilization schemes impact phosphorous losses will provide more information to stakeholders concerning the impacts of agriculture on surface water quality. Our results will help farmers and extensionists make more informed decisions about appropriate timing of manure application for reduced phosphorous losses and surface water degradation as well as aid law makers in improving policy surrounding manure application.

  3. Thermoluminescent phosphors for ultraviolet radiation dosimetry - a review

    International Nuclear Information System (INIS)

    Nagpal, J.S.

    2001-01-01

    Intrinsic TL response of CaSO 4 , CaF 2 , Al 2 O 3 (Si,Ti), Mg 2 SiO 4 : Tb and lamp phosphors to ultraviolet radiation is reviewed. Taking into consideration the characteristics such as afterglow at RT, rate/flux dependence, linearity of response, useful range, spectral dependence and effect of sequential/tandem UV exposures CaF 2 :Eu 2+ is an ideal TL dosemeter for UV radiation dosimetry. (author)

  4. Light Converting Inorganic Phosphors for White Light-Emitting Diodes

    OpenAIRE

    Chen, Lei; Lin, Chun-Che; Yeh, Chiao-Wen; Liu, Ru-Shi

    2010-01-01

    White light-emitting diodes (WLEDs) have matched the emission efficiency of florescent lights and will rapidly spread as light source for homes and offices in the next 5 to 10 years. WLEDs provide a light element having a semiconductor light emitting layer (blue or near-ultraviolet (nUV) LEDs) and photoluminescence phosphors. These solid-state LED lamps, rather than organic light emitting diode (OLED) or polymer light-emitting diode (PLED), have a number of advantages over conventional incand...

  5. Ultraviolet downconverting phosphor for use with silicon CCD imagers

    Science.gov (United States)

    Blouke, M. M.; Cowens, M. W.; Hall, J. E.; Westphal, J. A.; Christensen, A. B.

    1980-01-01

    The properties and application of a UV downconverting phosphor (coronene) to silicon charge coupled devices are discussed. Measurements of the absorption spectrum have been extended to below 1000 A, and preliminary results indicate the existence of useful response to at least 584 A. The average conversion efficiency of coronene was measured to be approximately 20% at 2537 A. Imagery at 3650 A using a backside illuminated 800 x 800 CCD coated with coronene is presented.

  6. Nuclear magnetic resonance of iron-57 nuclei in local fields in yttrium and iron garnets; Resonance magnetique nucleaire des noyaux du fer 57 dans les champs locaux du grenat d'yttrium et de fer

    Energy Technology Data Exchange (ETDEWEB)

    Robert, C. [Commissariat a l' Energie Atomique, Saclay (France).Centre d' Etudes Nucleaires

    1961-07-01

    We have demonstrated the nuclear resonance of {sup 57}Fe nuclei in the local field of each of the two magnetic sub-lattices of yttrium and iron garnets. The resonance frequencies and the relaxation times have been measured as a function of the temperature. (author) [French] Nous avons mis en evidence la resonance nucleaire des noyaux de {sup 57}Fe dans le champ local de chacun des deux sous-reseaux magnetiques du grenat d'yttrium et de fer. Les frequences de resonances et les temps de relaxation ont ete mesures en fonction de la temperature. (auteur)

  7. Status and prospects on development of yttrium-based high-temperature superconducting coated conductor

    International Nuclear Information System (INIS)

    Izumi, Teruo; Yanagi, Nagato

    2017-01-01

    Development of a large-sized large-current conductor using a high-temperature superconducting wire rod based on copper oxide has been started worldwide for the purpose of applying it as an option of a magnet for a nuclear fusion prototype reactor. There is yttrium-based thin film wire rod as a promising candidate. Japan is leading the development of this wire rod for many years, aiming to apply it to power equipment and the like. This paper explained the history of wire rod development, basic superconducting properties and manufacturing method, and latest achievements, and overviewed the feasibility of application to nuclear fusion reactor magnets. At present, the use of niobium-based low-temperature superconducting wire rod that is used in ITER is the basic idea. On the other hand, the development of wire rod using a copper oxide type high-temperature superconductor (HTS) has also been started. HTS wire rod is evaluated as suitable for application to nuclear fusion magnets due to its superior critical current characteristics and high mechanical rigidity up to high magnetic fields at high temperatures of yttrium. As current development progress, there are development of high-quality wire rod in the magnetic field and development of low AC loss wire rod. As future prospects, cost reduction due to mass production and improvement of yield, and investigation of low-resistance connection technology are being studied. The remaining future challenges of yttrium-based HTS are improvement of the anisotropy, influence on neutron irradiation, and problem of activation. (A.O.)

  8. Determination of vanadium in Syrian commercial and raffinate phosphoric acid

    International Nuclear Information System (INIS)

    Al-Merey, R.

    2002-04-01

    This study presents two methods for vanadium determination in Syrian commercial phosphoric acid. The vanadium (V) in the oxidized commercial phosphoric acid by ammonium persulfate solution is extracted from 5-M hydrochloride acid medium using N-benzoyl-N-phenyl hydroxyl amine (BPHA) in chloroform as an extracting solution. The first method, the extract vanadium as VOL 2 Cl is changed to V 2 O 3 L 4 complex by the addition of benzimidazole in 1-butanol to the violet organic layer. The absorbance is then measured at 440 nm (the molar absorptivity was found to be 3865 M -1 cm -1 ), where Beer law is applicable up to 36-μg ml -1 . the accuracy, precision and detection limit were found to be 3.7%, 77 ppb and 37 ppb, respectively. the second method, the organic layer is heated to evaporate chloroform, the residue is digested using 20% ammonium persulfate and 2-M sulfuric acid solutions. The vanadium concentration is measured spectrophotometrically by oxidizing gallic acid with persulfate (S 2 O 8 2- ) anion in phosphoric acid medium, where the vanadium (V) acts as a catalyst in the oxidation reaction. This method has a high sensitivity (∼10 -12 ) with accuracy and precision 5% and 0.621 ppb, respectively. Also Beer law at λ m ax=415 nm (ε=∼2 x 10 6 M -1 ) is applicable in the range 2.58-33.3 ppb. (author)

  9. Simple preparation of LiF:Mg,Ti phosphor

    International Nuclear Information System (INIS)

    Moharil, S.V.; Shahare, D.I.; Upaded, S.V.; Deshmukh, B.T.

    1993-01-01

    LiF-TLD 100 is a low-impedance (Z eff = 8.2) tissue equivalent material which is widely used in thermoluminescence (TL) dosimetry of ionizing radiations and personnel monitoring. Mg and Ti have been found to be the major impurities which impart the Tl characteristics. Recipes for the preparation of this phosphor, have not been found to be satisfactory for routine manufacture; there have always been problems associated with reproducibility and even with batch homogeneity. One of the reasons for this is that most procedures start either from readily available LiF or by melting the synthesized LiF, or both. The background impurities in the starting LiF powder can mask the intentional impurities, particularly Ti which has to be doped in rather small concentrations (10 p.p.m.). Melting LiF can again be tricky, as the LiF melt is volatile and highly corrosive. In this letter we report the preparation of LiF: Mg, Ti. The impurities were incorporated during the synthesis of LiF. The phosphor was prepared by heat treatments in ambient air without melting the compound. The characteristics of the prepared phosphors were studied and compared with those of LiF-TLD 100. (author)

  10. Instense red phosphors for UV light emitting diode devices.

    Science.gov (United States)

    Cao, Fa-Bin; Tian, Yan-Wen; Chen, Yong-Jie; Xiao, Lin-Jiu; Liu, Yun-Yi

    2010-03-01

    Ca(x)Sr1-x-1.5y-0.5zMoO4:yEu3+ zNa+ red phosphors were prepared by solid-state reaction using Na+ as charge supply for LEDs (light emitting diodes). The content of charge compensator, Ca2+ concentration, synthesis temperature, reaction time, and Eu3+ concentration were the keys to improving the properties of luminescence and crystal structure of red phosphors. The photoluminescence spectra shows the red phosphors are effectively excited at 616 nm by 311 nm, 395 nm, and 465 nm light. The wavelengths of 395 and 465 nm nicely match the widely applied emission wavelengths of ultraviolet or blue LED chips. Its chromaticity coordinates (CIE) are calculated to be x = 0.65, y = 0.32. Bright red light can be observed by the naked eye from the LED-based Ca0.60Sr0.25MoO4:0.08Eu3+ 0.06Na+.

  11. Technology of uranium recovery from wet-process phosphoric acid

    Energy Technology Data Exchange (ETDEWEB)

    Inoue, Katsutoshi [Saga Univ. (Japan). Faculty of Science and Engineering; Nakashio, Fumiyuki

    1982-12-01

    Rock phosphate contains from 0.005 to 0.02 wt.% of uranium. Though the content is a mere 5 to 10 % of that in uranium ore, the total recovery of uranium is significant since it is used for fertilizer manufacture in a large quantity. Wet-process phosphoric acid is produced by the reaction of rock phosphate with sulfuric acid. The recovery of uranium from this phosphoric acid is mostly by solvent extraction at present. According to U/sup 4 +/ or UO/sub 2//sup 2 +/ as the form of its existence, the technique of solvent extraction differs. The following matters are described: processing of rock phosphate; recovery techniques including the extraction by OPPA-octyl pyrophosphoric acid for U/sup 4 +/, and by mixed DEHPA-Di-(2)-ethylhexyl phosphoric acid and TOPO-tryoctyl phosphine oxide for UO/sub 2//sup 2 +/, and by OPAP-octylphenyl acid phosphate for U/sup 4 +/; the recent progress of the technology as seen in patents.

  12. Quantum efficiency of silica-coated rare-earth doped yttrium silicate

    Energy Technology Data Exchange (ETDEWEB)

    Cervantes-Vásquez, D., E-mail: dcervant@cnyn.unam.mx [Centro de Investigación Científica y de Educación Superior de Ensenada, Carretera Ensenada-Tijuana No. 3918, Zona Playitas, C.P. 22860 Ensenada, B.C., México (Mexico); Contreras, O.E.; Hirata, G.A. [Centro de Nanociencias y Nanotecnología, Universidad Nacional Autónoma de México, Km. 107 Carretera Tijuana-Ensenada, C.P. 22800 Ensenada, B.C., México (Mexico)

    2013-11-15

    The photoluminescent properties of rare earth-activated white-emitting Y{sub 2}SiO{sub 5}:Ce,Tb nanocrystalline phosphor prepared by two different methods, pressure-assisted combustion synthesis and sol–gel, were studied. The synthesized phosphor samples were post-annealed at 1373 K and 1623 K in order to obtain the X1-Y{sub 2}SiO{sub 5} and X2-Y{sub 2}SiO{sub 5} phases, respectively, which were confirmed by X-ray diffraction measurements. Photoluminescence analysis showed the contribution of two blue-emission bands within the 380–450 nm region originating from 5d–4f transitions in Ce{sup 3+} ions and a well-defined green emission of Tb{sup 3+} ions located at 545 nm corresponding to {sup 5}D{sub 4}→{sup 7}F{sub 5} electronic transitions. Thereafter, Y{sub 2}SiO{sub 5}:Ce,Tb powders were coated with colloidal silica in order to investigate the effect of silica coatings on their luminescent properties. Absolute fluorescence quantum efficiency measurements were carefully performed, which revealed an increase of 12% of efficiency in coated compared with bare-Y{sub 2}SiO{sub 5}:Ce,Tb phosphor. -- Highlights: • Y{sub 2}SiO{sub 5}:Ce,Tb phosphor powders were successfully coated with colloidal silica. • Post-annealing treatments improved the quantum efficiency of silica-coated Y{sub 2}SiO{sub 5}:Ce,Tb phosphors. • Absolute fluorescence quantum efficiency measurements showed an increase of 12%.

  13. Processes leading to yttrium-barium cuprates formation in synthesis using nitrates

    International Nuclear Information System (INIS)

    Kulakov, A.B.; Tesker, A.M.; Zalishchanskij, M.E.; Tret'yakov, Yu.D.; Gipius, A.A.

    1989-01-01

    An attempt to determine sequence and conditions for transformations occuring at heating both of mechanical mixture of copper, yttrium and barium nitrates and salt product of sublimated dehydration of quick frozen solution of nitrates in question of correlation which corresponds to YBa 2 Cu 3 O 7-σ final compounds is made. It is shown that unlike individual nitrates their thermolysis in the mixture occurs at lower temperatures with mechanism variation of decomposition separate stages. Specimens of superconducting ceramics with 4.3 g/cm 3 density phase composition and oxygen content which correspond to YBa 2 Cu 3 O 6.85±0.05 formula are obtaied

  14. Ultrasonic and viscometric studies of yttrium soaps in mixed organic solvents

    International Nuclear Information System (INIS)

    Mehrotra, K.N.; Tandon, K.; Rawat, M.K.

    1992-01-01

    The ultrasonic and viscosity measurements of yttrium soaps (caprylate, caprate and laurate) in a mixture of benzene and dimethyl formamide (3:2) have been carried out with a view to determine the critical micellar concentration soap-solvent interaction and other allied parameters. The various acoustic parameters (intermolecular free-length adiabatic compressibility, apparent molar compressibility, specific acoustic impedance, molar sound velocity, solvation number available volume and relative association) have been evaluated by ultrasonic velocity measurements. The results of viscosity measurement have been explained in terms of well known equations. (author). 18 refs., 2 figs., 3 tabs

  15. Erbium-doped yttrium aluminium garnet ablative laser treatment for endogenous ochronosis.

    Science.gov (United States)

    Chaptini, Cassandra; Huilgol, Shyamala C

    2015-08-01

    Ochronosis is a rare disease characterised clinically by bluish-grey skin discolouration and histologically by yellow-brown pigment deposits in the dermis. It occurs in endogenous and exogenous forms. Endogenous ochronosis, also known as alkaptonuria, is an autosomal recessive disease of tyrosine metabolism, resulting in the accumulation and deposition of homogentisic acid in connective tissue. We report a case of facial endogenous ochronosis and coexistent photodamage, which was successfully treated with erbium-doped yttrium aluminium garnet laser resurfacing and deep focal point treatment to remove areas of residual deep pigment. © 2014 The Australasian College of Dermatologists.

  16. Radio-synoviorthesis with yttrium 90 in the knee-joint in rheumatoid arthritis

    International Nuclear Information System (INIS)

    Hagena, F.W.; Muenchen Univ.

    1982-01-01

    The radio-synoviorthesis with yttrium 90 in the knee-joint in rheumatoid arthritis was performed and controlled in 106 knees of patients with rheumatoid arthritis over a span of time between 6 and 49 months. The results are similar to those of other authors. As compared to synovectomy radio-synoviorthesis seems less successful as far as long-term results are concerned. As local treatment radio-synoviorthesis seems a good supplementory element in the therapeutic plan of rheumatoid arthritis. The indication to alternative procedures has been considered carefully for each individual case and joint. (orig.) [de

  17. Nature of the magnetic susceptibility of dysprosium. Paramagnetic susceptibility of dysprosium - yttrium alloys

    International Nuclear Information System (INIS)

    Demidov, V.G.; Levitin, R.Z.; Chistyakov, O.D.

    1976-01-01

    The paramagnetic susceptibility of single crystals of dysprosium-yttirum alloys is measured in the basal plane and along the hexagonal axis. It is shown that the susceptibility of the alloys obeys the Curie-Weiss law, the effective magnetic moments allong the different directions being the same and the paramagnetic Curie temperatures being different. The difference between the paramagnetic Curie temperatures in the basal plane and along the hexagonal axis is independent of the dysprosium concentration in the alloy. As a comparison with the theoretical models of magnetic anisotropy shows, this is an indication that the magnetic anisotropy of dysprosium - yttrium alloys is of a single-ion nature

  18. Solid-phase synthesis of yttrium ferrites with structures of perovskite and garnet

    Energy Technology Data Exchange (ETDEWEB)

    Tkachenko, E V; Shapovalov, A G; Aksel' rod, N L; Pazdnikov, I P [Ural' skij Gosudarstvennyj Univ., Sverdlovsk (USSR)

    1980-09-01

    The solid phase synthesis of yttrium ferrites having a perovskite- and garnet-like structure has been investigated in the temperature range from 800 to 1500 deg C and temper times of up to 80 hours by reaction zone simulation and magnetic phase analysis. It is shown that for conversion degrees d<0.15 the reactions are diffusion-controlled. The rate constants and effective diffusion in the formation of YFeO/sub 3/ and Y/sub 3/Fe/sub 5/O/sub 12/ have been determined.

  19. PET imaging of soluble yttrium-86-labeled carbon nanotubes in mice.

    Directory of Open Access Journals (Sweden)

    Michael R McDevitt

    2007-09-01

    Full Text Available The potential medical applications of nanomaterials are shaping the landscape of the nanobiotechnology field and driving it forward. A key factor in determining the suitability of these nanomaterials must be how they interface with biological systems. Single walled carbon nanotubes (CNT are being investigated as platforms for the delivery of biological, radiological, and chemical payloads to target tissues. CNT are mechanically robust graphene cylinders comprised of sp(2-bonded carbon atoms and possessing highly regular structures with defined periodicity. CNT exhibit unique mechanochemical properties that can be exploited for the development of novel drug delivery platforms. In order to evaluate the potential usefulness of this CNT scaffold, we undertook an imaging study to determine the tissue biodistribution and pharmacokinetics of prototypical DOTA-functionalized CNT labeled with yttrium-86 and indium-111 ((86Y-CNT and (111In-CNT, respectively in a mouse model.The (86Y-CNT construct was synthesized from amine-functionalized, water-soluble CNT by covalently attaching multiple copies of DOTA chelates and then radiolabeling with the positron-emitting metal-ion, yttrium-86. A gamma-emitting (111In-CNT construct was similarly prepared and purified. The constructs were characterized spectroscopically, microscopically, and chromatographically. The whole-body distribution and clearance of yttrium-86 was characterized at 3 and 24 hours post-injection using positron emission tomography (PET. The yttrium-86 cleared the blood within 3 hours and distributed predominantly to the kidneys, liver, spleen and bone. Although the activity that accumulated in the kidney cleared with time, the whole-body clearance was slow. Differential uptake in these target tissues was observed following intravenous or intraperitoneal injection.The whole-body PET images indicated that the major sites of accumulation of activity resulting from the administration of (86Y-CNT were

  20. Optimization Recovery of Yttrium Oxide in Precipitation, Extraction, and Stripping Process

    Science.gov (United States)

    Perwira, N. I.; Basuki, K. T.; Biyantoro, D.; Effendy, N.

    2018-04-01

    Yttrium oxide can be used as a dopant control rod of nuclear reactors in YSH material and superconductors. Yttrium oxide is obtained in the Xenotime mineral derived from byproduct of tin mining PT Timah Bangka which contain rare earth elements (REE) dominant Y, Dy, and Gd whose content respectively about 29.53%, 7.76%, and 2.58%. Both usage in the field of nuclear and non-nuclear science and technology is need to pure from the impurities. The presence of impurities in the yttrium oxide may affect the characteristic of the material and the efficiency of its use. Thus it needs to be separated by precipitation and extraction-stripping and calcination in the making of the oxide. However, to obtain higher levels of Yttrium oxide, it is necessary to determine the optimum conditions for its separation. The purpose of this research was to determine the optimum pH of precipitation, determine acid media and concentration optimum in extraction and stripping process and determine the efficiency of the separation of Y from REE concentrate. This research was conducted with pH variation in the precipitation process that pHs were 4 - 8, the difference of acid media for the extraction process, i.e., HNO3, HCl and H2SO4 with each concentration of 0,5 M; 1 M; 1,5 M; and 2 M and for stripping process were HNO3, HCl, and H2SO4 with each concentration of 1 M; 2M; and 3 M. Based on the result, the optimum pH of precipitation process was 6,5, the optimumacid media was HNO3 0,5 M, and for stripping process media was HNO3 3 M. The efficiency of precipitation process at pH 6,5 was 69,53 %, extraction process was 96.39% and stripping process was 4,50%. The separation process from precipitation to extraction had increased the purity and the highest efficiency recovery of Y was in the extraction process and obtained Y2O3 purer compared to the feed with the Y2O3 content of 92.87%.

  1. Quantitative and Qualitative Assessment of Yttrium-90 PET/CT Imaging

    OpenAIRE

    Attarwala, Ali Asgar; Molina-Duran, Flavia; Büsing, Karen-Anett; Schönberg, Stefan O.; Bailey, Dale L.; Willowson, Kathy; Glatting, Gerhard

    2014-01-01

    Yttrium-90 is known to have a low positron emission decay of 32 ppm that may allow for personalized dosimetry of liver cancer therapy with (90)Y labeled microspheres. The aim of this work was to image and quantify (90)Y so that accurate predictions of the absorbed dose can be made. The measurements were performed within the QUEST study (University of Sydney, and Sirtex Medical, Australia). A NEMA IEC body phantom containing 6 fillable spheres (10-37 mm ∅) was used to measure the 90Y distribut...

  2. Phonon-impurity relaxation and acoustic wave absorption in yttrium-aluminium garnet crystals with impurities

    International Nuclear Information System (INIS)

    Ivanov, S.N.; Kotelyanskij, I.M.; Medved', V.V.

    1983-01-01

    The experimental results of investigations of the influence of substitution impurities in the yttrium-aluminium garnet lattice on absorption of high-frequency acoustic waves are presented. It is shown that the phonon-impurity relaxation processses affect at most the wave absorption and have resonance character when the acoustic wave interacts with the thermal phonon group in the vicinity of the perturbed part of the phonon spectrum caused by the impurity. The differences of time values between inelastic and elastic thermal phonons relaxations determined from the data on longitudinal and shear waves in pure and impurity garnet crystals are discussed

  3. Yttrium-90 radioembolization using TheraSphere in the management of primary and secondary liver tumors.

    Science.gov (United States)

    Riaz, A; Lewandowski, R J; Kulik, L; Salem, R

    2009-06-01

    Locoregional therapies, such as transarterial chemoembolization, radioembolization and thermal ablation (e.g., radiofrequency ablation) are establishing their roles in the management of liver malignancies. With yYttrium-90 radioembolization therapy (90Y) radionuclide labeled microspheres are injected into the tumor feeding artery. This allows the delivery of a high radioactive dose to the tumor with minimal toxicity to normal tissues. 90Y has demonstrated to be safe and effective in the management of liver tumors. Authors present a review of the literature available for the use of TheraSphere for radioembolization in the management of liver tumors.

  4. Treatment of diffuse large B-cell lymphoma of the liver with yttrium-90 microsphere embolization.

    Science.gov (United States)

    Fenske, Timothy S; Benjamin, Heather; Kroft, Steven H; Hohenwalter, Eric J; Rilling, William S

    2008-11-01

    A 41-year-old male with a 4-year history of chronic hepatitis C presented with a 1-month history of abdominal pain, fatigue, weight loss, and night sweats. Laboratory examinations, chest, abdomen, and pelvic CT scans, PET-CT scans, ultrasound-guided needle biopsies of liver lesions, bone-marrow biopsy, flow cytometry, and immunohistochemical staining for B-cell markers including CD20. Chemoresistant diffuse large B-cell lymphoma, with gradual loss of CD20 antigen expression. Embolization of hepatic tumors using yttrium-90 microspheres (Therasphere, Theragenics Corporation, Buford, GA).

  5. Yttrium-90 radioembolization of hepatocellular carcinoma and metastatic disease to the liver.

    Science.gov (United States)

    Lewandowski, Robert J; Salem, Riad

    2006-03-01

    Yttrium-90 ((90)Y) radioembolization is a catheter-based therapy that delivers internal radiation to hepatic tumors in the form of microspheres. (90)Y can be delivered to the hepatic tumor as either a constituent of a glass microsphere, TheraSphere(®), or as a biocompatible resin-based microsphere, SIR-Spheres(®). Once embedded within the tumor microcirculation, these microspheres emit β-radiation at therapeutic levels. While the technical aspects of radioembolization are quite complex, the collective clinical experience presented in the literature supports the use of (90)Y radioembolization for unresectable hepatic malignancies.

  6. Metastable phases in yttrium oxide plasma spray deposits and their effect on coating properties

    International Nuclear Information System (INIS)

    Gourlaouen, V.; Schnedecker, G.; Boncoeur, M.; Lejus, A.M.; Collongues, R.

    1993-01-01

    Yttrium oxide coatings were obtained by plasma spray. Structural investigations on these deposits show that, due to the drastic conditions of this technique, a minor monoclinic B phase is formed in the neighborhood of the major cubic C form. The authors discuss here the influence of different plasma spray parameters on the amount of the B phase formed. They describe also the main properties of Y 2 O 3 B and C phases in these deposits such as structural characteristics, thermal stability and mechanical behavior

  7. Electrical properties of single crystal Yttrium Iron Garnet ultra-thin films at high temperatures

    OpenAIRE

    Thiery, Nicolas; Naletov, Vladimir V.; Vila, Laurent; Marty, Alain; Brenac, Ariel; Jacquot, Jean-François; de Loubens, Grégoire; Viret, Michel; Anane, Abdelmadjid; Cros, Vincent; Youssef, Jamal Ben; Demidov, Vladislav E.; Demokritov, Sergej O.; Klein, Olivier

    2017-01-01

    We report a study on the electrical properties of 19 nm thick Yttrium Iron Garnet (YIG) films grown by liquid phase epitaxy. The electrical conductivity and Hall coefficient are measured in the high temperature range [300,400]~K using a Van der Pauw four-point probe technique. We find that the electrical resistivity decreases exponentially with increasing temperature following an activated behavior corresponding to a band-gap of $E_g\\approx 2$ eV, indicating that epitaxial YIG ultra-thin film...

  8. The enhanced visible light photocatalytic activity of yttrium-doped BiOBr synthesized via a reactable ionic liquid

    Energy Technology Data Exchange (ETDEWEB)

    He, Minqiang; Li, Weibing [School of Chemistry and Chemical Engineering, Jiangsu University, 301 Xuefu Road, Zhenjiang 212013 (China); Xia, Jiexiang, E-mail: xjx@ujs.edu.cn [School of Chemistry and Chemical Engineering, Jiangsu University, 301 Xuefu Road, Zhenjiang 212013 (China); Xu, Li; Di, Jun [School of Chemistry and Chemical Engineering, Jiangsu University, 301 Xuefu Road, Zhenjiang 212013 (China); Xu, Hui [School of the Environment, Jiangsu University, 301 Xuefu Road, Zhenjiang 212013 (China); Yin, Sheng [School of Chemistry and Chemical Engineering, Jiangsu University, 301 Xuefu Road, Zhenjiang 212013 (China); Li, Huaming, E-mail: lhm@ujs.edu.cn [School of Chemistry and Chemical Engineering, Jiangsu University, 301 Xuefu Road, Zhenjiang 212013 (China); Li, Mengna [School of Chemistry and Chemical Engineering, Jiangsu University, 301 Xuefu Road, Zhenjiang 212013 (China)

    2015-03-15

    Graphical abstract: Yttrium (Y)-doped BiOBr with different Y doping concentrations has been synthesized via solvothermal method in the presence of reactable ionic liquid 1-hexadecyl-3-methylimidazolium bromide ([C16mim]Br). The photocatalytic activities of the yttrium doped BiOBr samples were evaluated by the degradation of ciprofloxacin (CIP) and rhodamine B (RhB) under visible-light irradiation. The yttrium doped BiOBr exhibited enhanced photocatalytic activity for the degradation of the two types of pollutants, and the 5wt%Y-doped BiOBr showed the highest photocatalytic activity. The enhanced photocatalytic performance could be attributed to the reduced band gap and improved separation of electron–hole pairs. - Highlights: • Yttrium (Y)-doped BiOBr composites have been synthesized via solvothermal method in the presence of reactable ionic liquid [C16mim]Br. • The yttrium doped BiOBr exhibited enhanced photocatalytic activity for the degradation of ciprofloxacin (CIP) and rhodamine B (RhB). • The enhanced photocatalytic performance could be attributed to the reduced band gap and improved separation of electron–hole pairs. - Abstract: Yttrium (Y)-doped BiOBr with different Y doping concentrations has been synthesized via solvothermal method in the presence of reactable ionic liquid 1-hexadecyl-3-methylimidazolium bromide ([C{sub 16}mim]Br). Their structures, morphologies and optical properties were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS) and UV–vis diffuse reflectance spectroscopy (DRS). The photocatalytic activities of the yttrium doped BiOBr samples were evaluated by the degradation of ciprofloxacin (CIP) and rhodamine B (RhB) under visible-light irradiation. The yttrium doped BiOBr exhibited enhanced photocatalytic activity for the degradation of the two types of pollutants, and the 5wt%Y-doped BiOBr showed the highest

  9. ELECTRON MICROSCOPIC INVESTIGATION OF YTTRIUM ALUMINUM GARNET POWDERS Y3AL5O12, SYNTHESIZED BY SOL–GEL METHOD

    OpenAIRE

    A. E. Baranchikov; V. A. Maslov; S. V. Shcherbakov; V. A. Usachyov; N. E. Kononenko; P. P. Fedorov; K. V. Dukelskiy

    2015-01-01

    Subject of Study. The paper presents results of characterization for neodymium doped yttrium aluminum garnet nanopowders - YAG:Nd3+ by the method of scanning electronic microscopy. Method. Synthesis of YAG:Nd3+ was carried out by sol-gel method from nitrate or acetate - nitrate solutions with addition of some organic compounds and ammonia as well. Such substances were used as the source ones: oxides of neodymium and yttrium with the content of the basic substance equal to 99.999 %; organic co...

  10. Spectral properties of Dy3+ doped ZnAl2O4 phosphor

    Science.gov (United States)

    Prakash, Ram; Kumar, Sandeep; Mahajan, Rubby; Khajuria, Pooja; Kumar, Vinay; Choudhary, R. J.; Phase, D. M.

    2018-05-01

    Herein, Dy3+ doped ZnAl2O4 phosphor was synthesized by the solution combustion method. The synthesized phosphor was characterized by X-ray diffraction (XRD), photoluminescence (PL) spectroscopy, UV-Vis spectroscopy and X-ray photoelectron spectroscopy (XPS). The phase purity of the phosphor was confirmed by the XRD studies that showed cubic symmetry of the synthesized phosphor. Under UV excitation (388 nm) the PL emission spectrum of the phosphor shows characteristic transition from the Dy3+ ion. A band gap of 5.2 eV was estimated from the diffused reflectance spectroscopy. The surface properties of the phosphor were studied using the X-ray photoelectron spectroscopy.

  11. Neutron scintillator using Ga-doped ZnO phosphor with high detection efficiency

    International Nuclear Information System (INIS)

    Koyama, Shin; Kinoshita, Atsushi; Fujiwara, Akihiko; Kobayashi, Haruki; Takei, Yoshinori; Nanto, Hidehito; Katagiri, Masaki

    2009-01-01

    Zinc Oxide (ZnO) family phosphors as phosphor for neutron detector have prepared using Spark Plasma Sintering (SPS) method. The optical properties of ZnO phosphor prepared are investigated. The following results were obtained. Two dominant photoluminescence (PL) emission peaks at 395 nm and 495 nm were observed. The lifetime of the PL emission peak at 395 nm (UV emission band) is about 20 ns, which is suitable for neutron detection. The Ga (30 mol%)-doped ZnO phosphor exhibited an intense UV emission band without the visible emission band. The Ga-doped ZnO phosphor can be prepared at the atmospheric pressure of about 8 Pa using SPS method. It was found that the PL intensity of UV emission band is increased with improving the crystallinity of the ZnO phosphor. (author)

  12. Critical issues in enhancing brightness in thin film phosphors for flat-panel display applications

    International Nuclear Information System (INIS)

    Singh, R.K.; Chen, Z.; Kumar, D.; Cho, K.; Ollinger, M.

    2002-01-01

    Thin film phosphors have potential applications in field emission flat-panel displays. However, they are limited by the lower cathodoluminescent brightness in comparison to phosphor powders. In this paper, we have investigated the critical parameters that need to be optimized to increase the brightness of phosphor thin films. Specifically, we studied the role of surface roughness and optical properties of the substrate on the brightness of the phosphor films. Thin Y 2 O 3 :Eu phosphor films were deposited on various substrates (lanthanum aluminate, quartz, sapphire, and silicon) with thicknesses varying from 50 to 500 nm. A model that accounts for diffuse and specular or scattering effects has been developed to understand the effects of the microstructure on the emission characteristics of the cathodoluminescent films. The results from the model show that both the optical properties of the substrate and the surface roughness of the films play a critical role in controlling the brightness of laser deposited phosphor films

  13. A SrBPO5: Eu2+ phosphor for neutron imaging

    International Nuclear Information System (INIS)

    Sakasai, K.; Katagiri, M.; Toh, K.; Nakamura, T.

    2001-01-01

    A SrBPO 5 : Eu 2+ phosphor material has been investigated for neutron imaging. This phosphor showed photostimulated luminescence (PSL) by illumination of 635 nm laser light after X-ray irradiation. The spectral characteristics of the phosphor were similar to those of BaFBr: Eu 2+ , which is a commonly used phosphor of imaging plates. In addition, we found that this phosphor also showed PSL for neutron irradiation. It comes from the fact that it contains atomic boron in base matrix. Therefore, this phosphor can be used for neutron imaging without adding neutron sensitive materials such as Gd in commercially available neutron imaging plates. The PSL intensity and the neutron detection will be increased by using enriched boron instead of natural boron. (author)

  14. Calculated energy dependence of CaSO4:Dy TL phosphor and phosphor embedded Teflon for X and gamma rays

    International Nuclear Information System (INIS)

    Chang, J.-K.; Nam, Y.-M.; Kim, J.-L.; Chang, S.-Y.; Kim, B.-H.

    2001-01-01

    The energy dependence of a CaSO 4 :Dy TL phosphor for 21 monoenergetic photons of energy ranging from 0.01 to 3 MeV was calculated by using MCNP4A code. The calculation results show good agreement with those of other authors within ± 5% relative error. Calculations and experiments are also performed to determine the energy dependence of CaSO 4 : Dy phosphor with Dy concentrations from 0.01 to 1.5 mol %, and with the compositions of TL-Teflon from 10 to 90 wt %. The calculated energy responses show good agreement with the experiment results within ± 20% relative error except for a concentration lower than 0.1 mol % Dy and the low energy regions of M30 (Eave.=20 keV) and M60 (Eave.=34 keV). For the TL-Teflon mixture, the energy dependence shows an decreasing trend with the increase of Teflon concentration in MCNP calculation but shows no dependence for TL-Teflon mixture proportions in experiment. These differences are due to the non-homogeneous distribution of Dy concentration and the effect of large grain size in the phosphors. The energy dependence of the 30 wt/o CaSO 4 (0.1 mol%;Dy) and 70 wt/o Teflon that is placed behind the filters of plastic, aluminum, copper, tin and lead with a thickness from 0.1 to 2 mm were calculated, respectively

  15. Synthesis and complex forming property of phosphor acid derivatives

    International Nuclear Information System (INIS)

    Babaev, B.N.

    2004-01-01

    Full text:With the aim to get new effective and selective extra gents of noble and non-ferrous metals from acid solution and industrial sewage, research of the dependence of 'structure effectiveness' the various phosphor acid derivatives with logical changeable structure (thio phosphor acids, derivatives of dialkoxythiophosphor, O-alkyl-methylphosphon, alkylphenylphosphon, diphenylphosphine acids also 4 methyl-1,3,2 dioxaphosphorinane) which contain different functional groups, the remains of heterocyclic amines and alkaloids, new derivatives of some analytical reagents were synthesized. The structure of synthesized compounds is approved by the results of IR-, PMR-, mass-spectrum analyze. Researching mass-spectrum decay of synthesized phosphor acid derivatives we defined that differing from O-dihexyl-S-propargyl-benzylthio phosphat, mass spectrum decay of O-dialkyl-S-(piperdynobutin-2-il)thio phosphat is characterized by the appearing [M-H] + ions and during the decay ions with high intensiveness are formed. Fragmentation of M + O-alkyl-O-(aminoalkyl)phenylphosphonate proceeds in various directions and characterized with the great number of phosphor containing ions, the possession of the second phenyl radical in the molecule of diphenylphosphon acid derivatives changes the fragmentation of molecular ion of diphenylphosphon acid derivatives. The process of extraction of noble (Au, Ag, Pt, Pd, Os) metals from hydrochloric-sulphur-nitrogen acid medium was analyzed by radioactive indicator's method. It was noticed that structure, strength, conformation of compounds, the temperature, of acid medium (0,1-10 M) and the nature of acids (HCL, H 2 SO 4 , HNO 3 ) could have strong influence to the effectiveness of metal extraction. During the research of metals extraction from pure solutions we can see the followings: 1) There are such substances, which can be used as effective group reagent towards the Au, Ag and Pd. 2) Derivatives with acetylene extract ions of gold from

  16. Study of phase transformation processes in steel after phosphor ion implantation and following thermal treatment

    International Nuclear Information System (INIS)

    Zhetbaev, A.K.; Vereshchak, N.F.; Satpaev, K.K.; Dosmagambetov, T.D.; Serikbaeva, Z.T.

    1999-01-01

    In the paper process of phase transformation after phosphor ion implantation in steel-45 and annealing in vacuum at 1000 deg C and irradiation by various doses of phosphor ions with energy 100 keV an accelerator are researched by conversion electron method. The phosphor overall solubility in iron is equal 4.53 %. Implantation dose below 6·10 17 ions/cm 2 allows increase phosphor ions content in implantation region to 35 %. Therefore, iron phosphides (Fe 3 P, Fe 2 P and Fe P) forming are possible. (author)

  17. Recovering of uranium from phosphoric acid produced by the wet process

    International Nuclear Information System (INIS)

    Barreiro, A.J.; Lyon, W.L.; Holleman, R.A.; Randell, C.C.

    1977-01-01

    Process for recovering uranium as from an aqueous solution of phosphoric acid arising from a wet process, with a scrubbing agent essentially composed of a hydrocarbon whose boiling point is situated between 150 0 C and 300 0 C, which reacts with the contaminents formed in the sludge in the phosphoric acid, in an efficient enough quantity to wash the contamination products forming the phosphoric acid sludge, give a sludge phase and a purified phosphoric acid phase, after which the sludge phase is extracted [fr

  18. TL-OSL study of Li{sub 3}PO{sub 4}: Mg, Cu phosphor

    Energy Technology Data Exchange (ETDEWEB)

    Rahangdale, S. R., E-mail: sachin.rahangdale1@gmail.com; Wankhede, S. P. [Department of Physics, K.D.K.College of Engineering, Nagpur (India); Dhabekar, B. S. [RPAD, Bhabha Atomic Research Centre, Trombay, Mumbai 400085 (India); Palikundwar, U. A.; Moharil, S. V. [Department of Physics, RTM Nagpur University, Nagpur, 440010 (India)

    2015-08-28

    In the present work, we report the thermoluminescence and optically stimulated luminescence properties of Mg and Cu doped Li{sub 3}PO{sub 4} phosphor. The phosphor was synthesized by precipitation method. The thermoluminescence dosimetric peak temperature for the phosphor varies with concentrations of Mg and Cu. Li{sub 3}PO{sub 4} shows good response to 470nm optical stimulation. The OSL sensitivity of the phosphor is approximately 12 times than that of standard Lithium magnesium phosphate. This study may help to develop this material for the application in real time dosimetry using optically stimulated luminescence.

  19. New Silicate Phosphors for a White LED(Electronic Displays)

    OpenAIRE

    Toda, Kenji; Kawakami, Yoshitaka; Kousaka, Shin-ichiro; Ito, Yutaka; Komeno, Akira; Uematsu, Kazuyoshi; Sato, Mineo

    2006-01-01

    We focus on the development of new silicate phosphors for a white LED. In the europium doped silicate system, four LED phosphor candidates-Li_2SrSiO_4:Eu^, Ba_9Sc_2Si_6O_:Eu^, Ca_3Si_2O_7:Eu^ and Ba_2MgSi_2O_7:Eu^ were found. Luminescent properties under near UV and visible excitation were investigated for the new Eu^ doped LED silicate phosphors. These new phosphors have a relatively strong absorption band in a long wavelength region.

  20. Process for making a titanium diboride-chromium diboride-yttrium titanium oxide ceramic composition

    Science.gov (United States)

    Holcombe, C.E.; Dykes, N.L.

    1992-04-28

    A ceramic composition is described. The ceramic composition consists essentially of from about 84 to 96 w/o titanium diboride, from about 1 to 9 w/o chromium diboride, and from about 3 to about 15 w/o yttrium-titanium-oxide. A method of making the ceramic composition is also described. The method of making the ceramic composition comprises the following steps: Step 1--A consolidated body containing stoichiometric quantities of titanium diboride and chromium diboride is provided. Step 2--The consolidated body is enclosed in and in contact with a thermally insulated package of yttria granules having a thickness of at least 0.5 inches. Step 3--The consolidated body enclosed in the thermally insulated package of yttria granules is heated in a microwave oven with microwave energy to a temperature equal to or greater than 1,900 degrees centigrade to sinter and uniformly disperse yttria particles having a size range from about 1 to about 12 microns throughout the consolidated body forming a densified body consisting essentially of titanium diboride, chromium diboride, and yttrium-titanium-oxide. The resulting densified body has enhanced fracture toughness and hardness. No Drawings

  1. Studies on Characterization, Optical Absorption, and Photoluminescence of Yttrium Doped ZnS Nanoparticles

    Directory of Open Access Journals (Sweden)

    Ranganaik Viswanath

    2014-01-01

    Full Text Available Pure ZnS and ZnS:Y nanoparticles were synthesized by a chemical coprecipitation route using EDTA-ethylenediamine as a stabilizing agent. X-ray diffraction (XRD, high resolution transmission electron microscopy (HRTEM, field emission scanning electron microscopy (FE-SEM, Fourier transform infrared spectrometry (FTIR, thermogravimetric-differential scanning calorimetry (TG-DSC, and UV-visible and photoluminescence (PL spectroscopy were employed to characterize the as-synthesized ZnS and ZnS:Y nanoparticles, respectively. XRD and TEM studies show the formation of cubic ZnS:Y particles with an average size of ~4.5 nm. The doping did not alter the phase of the zinc sulphide, as a result the sample showed cubic zincblende structure. The UV-visible spectra of ZnS and ZnS:Y nanoparticles showed a band gap energy value, 3.85 eV and 3.73 eV, which corresponds to a semiconductor material. A luminescence characteristics such as strong and stable visible-light emissions in the orange region alone with the blue emission peaks were observed for doped ZnS nanoparticles at room temperature. The PL intensity of orange emission peak was found to be increased with an increase in yttrium ions concentration by suppressing blue emission peaks. These results strongly propose that yttrium doped zinc sulphide nanoparticles form a new class of luminescent material.

  2. Thermoelectric Properties of the Yttrium-Doped Ceramic Oxide SrTiO{sub 3}

    Energy Technology Data Exchange (ETDEWEB)

    Khan, Tamal Tahsin; Ur, Soon-Chul [Korea National University of Transportation, Chungju (Korea, Republic of)

    2017-01-15

    The doping dependence of the thermoelectric figure of merit, ZT, of the ceramic oxide SrTiO{sub 3} at high temperature has been studied. In this study, yttrium was used as the doping element. A conventional solid-state reaction method was used for the preparation of Y-doped SrTiO{sub 3}. The doping level in SrTiO{sub 3} was controlled to be in the doping range of 2 - 10 mole%. Almost all the yttrium atoms incorporated into the SrTiO{sub 3} provided charge carriers, as was observed by using X-ray diffraction pattern. The relative densities of all the samples varied from 98.53% to 99.45%. The thermoelectric properties, including the electrical conductivity σ, Seebeck coefficient S, thermal conductivity k, and the figure of merit, ZT, were investigated at medium temperatures. The ZT value showed an obvious doping level dependence, in which a value as high as 0.18 is realized at 773 K for a doping of 8 mole%.

  3. Aspects of radiation protection during the treatment of liver cancer using yttrium-90 labelled microspheres

    International Nuclear Information System (INIS)

    Klemp, P.F.B.; Perry, A.M.; Fox, R.A.; Gray, B.N.; Burton, M.A.

    1989-01-01

    Twenty eight patients have received treatment for liver cancer by the intra-hepatic arterial injection of between 1 and 4 GBq of yttrium-90 labelled microspheres. The injection was performed at laparotomy. If 11.1 MBq of yttrium-90 are distributed evenly over 1 sq cm of tissue, the tissue surface will suffer an initial beta dose rate of 16.2 Gy h -1 . Special precautions are therefore essential during the injection procedure, subsequently in nursing the patient and if further intervention becomes necessary. A specially designed apparatus is used for the injection, glass spectacles are worn and if the active liver is to be handled, lead rubber gloves are used. The theatre is prepared so that contaminated items can be easily isolated and a 'spill pack' is readily available. At completion of the operation, the bremsstrahlung dose rate at 15 cm from the liver is initially 15 μSv h -1 GBq -1 . Contamination of urine is typically 20 to 50 kBq L -1 while the contamination of other body fluids is negligible. Finger doses to the surgeons has varied from 2 to 5 mSv GBq -1 injected while personnel film badges used to monitor the dose equivalent to the surgeons and ward staff have recorded maximum doses of 1.5 mSv and 300 μSv respectively. 11 refs., 1 fig., 3 tabs

  4. Quantitation in PET using isotopes emitting prompt single gammas: application to yttrium-86

    International Nuclear Information System (INIS)

    Walrand, Stephan; Jamar, Francois; Mathieu, Isabelle; De Camps, Joelle; Lonneux, Max; Pauwels, Stanislas; Sibomana, Merence; Labar, Daniel; Michel, Christian

    2003-01-01

    Several yttrium-90 labelled somatostatin analogues are now available for cancer radiotherapy. After injection, a large amount of the compound is excreted via the urinary tract, while a variable part is trapped in the tumour(s), allowing the curative effect. Unfortunately, the compound may also be trapped in critical tissues such as kidney or bone marrow. As a consequence, a method for assessment of individual biodistribution and pharmacokinetics is required to predict the maximum dose that can be safely injected into patients. However, 90 Y, a pure β - particle emitter, cannot be used for quantitative imaging. Yttrium-86 is a positron emitter that allows imaging of tissue uptake using a PET camera. In addition to the positron, 86 Y also emits a multitude of prompt single γ-rays, leading to significant overestimation of uptake when using classical reconstruction methods. We propose a patient-dependent correction method based on sinogram tail fitting using an 86 Y point spread function library. When applied to abdominal phantom acquisition data, the proposed correction method significantly improved the accuracy of the quantification: the initial overestimation of background activity by 117% was reduced to 9%, while the initial error in respect of kidney uptake by 84% was reduced to 5%. In patient studies, the mean discrepancy between PET total body activity and the activity expected from urinary collections was reduced from 92% to 7%, showing the benefit of the proposed correction method. (orig.)

  5. High-Performance Pyrochlore-Type Yttrium Ruthenate Electrocatalyst for Oxygen Evolution Reaction in Acidic Media

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jaemin [Department; Shih, Pei-Chieh [Department; Tsao, Kai-Chieh [Department; Pan, Yung-Tin [Department; Yin, Xi [Department; Sun, Cheng-Jun [X-ray; Yang, Hong [Department

    2017-08-17

    Development of acid-stable electrocatalysts with low overpotential for oxygen evolution reaction (OER) is a major challenge for the production of hydrogen directly from water. We report in this paper a pyrochlore yttrium ruthenate (Y2Ru2O7-δ) electrocatalyst that has significantly enhanced performance towards OER in acid media over the best-known catalysts, with an onset overpotential of 190 mV and high stability in 0.1-M perchloric acid solution. X-ray absorption near-edge structure (XANES) indicates Y2Ru2O7-δ electrocatalyst had a low valence state that favors the high OER activity. Density functional theory (DFT) calculation shows this pyrochlore has lower band center energy for the overlap between Ru 4d and O 2p orbitals and therefore more stable Ru-O bond than RuO2, highlighting the effect of yttrium on the enhancement in stability. The Y2Ru2O7-δ pyrochlore is also free of expensive iridium metal, thus a cost-effective candidate for practical applications.

  6. Microstructural evolution of 316L stainless steels with yttrium addition after mechanical milling and heat treatment

    Energy Technology Data Exchange (ETDEWEB)

    Kotan, Hasan, E-mail: hasankotan@gmail.com

    2015-10-28

    Nanocrystalline 316L stainless steels with yttrium addition were prepared by mechanical milling at cryogenic temperature and subjected to annealing treatments at various temperatures up to 1200 °C. The dependence of hardness on the microstructure was utilized to study the mechanical changes in the steels occurring during annealing. The microstructural evolution of the as-milled and annealed steels was characterized by means of X-ray diffraction (XRD), focused ion beam microscopy (FIB) and transmission electron microscopy (TEM) techniques. The results have revealed that austenite in as-received powder partially transformed to martensite phase during mechanical milling whereas the annealing induced reverse transformation of martensite-to-austenite. Furthermore, while the austenite-to-martensite phase ratio increased with increasing annealing temperature, the equilibrium structure was not achieved after three hours heat treatments up to 1200 °C resulting in a dual-phased steels with around 10% martensite. The grain size of 316L steel was 19 nm after mechanical milling and remained around 116 nm at 1100 °C with yttrium addition as opposed to micron size grains of plain 316L steel at the same annealing temperature. Such microstructural features facilitate the use of these materials at elevated temperatures, as well as the development of scalable processing routes into a dense nanocrystalline compact.

  7. Microstructure and tensile properties of yttrium nitride dispersion-strengthened 14Cr–3W ferritic steels

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Liqing [State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China); School of Mechanical and Mining Engineering, University of Queensland, Brisbane 4067, QLD (Australia); Liu, Zuming, E-mail: lzm@csu.edu.cn [State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China); Chen, Shiqi; Guo, Yang [State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China)

    2015-12-15

    Highlights: • Innovative nano yttrium nitride dispersion strengthened steels were fabricated. • Higher content of additives accelerate the steel-ceramic powder milling process more. • Steel with high content (3%) of YN dispersoids can obtain good performance at 500 °C. - Abstract: 14Cr–3W ferritic steel powders were mechanically milled with microscale yttrium nitride (YN) particles to fabricate particle dispersion-strengthened ferritic steels. After hot consolidation and annealing, the steel matrix was homogeneously dispersed with nano-scale YN particles. The steel containing 0.3 wt.% YN particles exhibited a yield strength of 1445 MPa at room temperature. Its total elongation was 10.3%, and the fracture surface exhibited mixed ductile and quasi-cleavage fracture morphologies. The steel with a much higher content of YN particles (3 wt.%) in its matrix was much stronger (1652 MPa) at room temperature at the cost of ductility. In particular, it exhibited a high yield strength (1350 MPa) with applicable ductility (total elongation > 10%) at 500 °C. This study has developed a new kind of reinforcement particle to fabricate high-performance ferritic steels.

  8. Yttrium scandate thin film as alternative high-permittivity dielectric for germanium gate stack formation

    Energy Technology Data Exchange (ETDEWEB)

    Lu, Cimang, E-mail: cimang@adam.t.u-tokyo.ac.jp; Lee, Choong Hyun; Nishimura, Tomonori; Toriumi, Akira [Department of Materials Engineering, The University of Tokyo, 7-3-1 Hongo, Tokyo 113-8656 (Japan); JST, CREST, 7-3-1 Hongo, Tokyo 113-8656 (Japan)

    2015-08-17

    We investigated yttrium scandate (YScO{sub 3}) as an alternative high-permittivity (k) dielectric thin film for Ge gate stack formation. Significant enhancement of k-value is reported in YScO{sub 3} comparing to both of its binary compounds, Y{sub 2}O{sub 3} and Sc{sub 2}O{sub 3}, without any cost of interface properties. It suggests a feasible approach to a design of promising high-k dielectrics for Ge gate stack, namely, the formation of high-k ternary oxide out of two medium-k binary oxides. Aggressive scaling of equivalent oxide thickness (EOT) with promising interface properties is presented by using YScO{sub 3} as high-k dielectric and yttrium-doped GeO{sub 2} (Y-GeO{sub 2}) as interfacial layer, for a demonstration of high-k gate stack on Ge. In addition, we demonstrate Ge n-MOSFET performance showing the peak electron mobility over 1000 cm{sup 2}/V s in sub-nm EOT region by YScO{sub 3}/Y-GeO{sub 2}/Ge gate stack.

  9. Scanning-SQUID investigation of spin-orbit torque acting on yttrium iron garnet devices

    Science.gov (United States)

    Rosenberg, Aaron J.; Jermain, Colin L.; Aradhya, Sriharsha V.; Brangham, Jack T.; Nowack, Katja C.; Kirtley, John R.; Yang, Fengyuan; Ralph, Daniel C.; Moler, Kathryn A.

    Successful manipulation of electrically insulating magnets, such as yttrium iron garnet, by by current-driven spin-orbit torques could provide a highly efficient platform for spintronic memory. Compared to devices fabricated using magnetic metals, magnetic insulators have the advantage of the ultra-low magnetic damping and the elimination of shunting currents in the magnet that reduce the torque efficiency. Here, we apply current in the spin Hall metal β-Ta to manipulate the magnetic orientation of micron-sized, electrically-insulating yttrium iron garnet devices. We do not observe spin-torque switching even for applied currents well above the critical current expected in a macrospin switching model. This suggests either inefficient transfer of spin torque at our Ta/YIG interface or a breakdown of the macrospin approximation. This work is supported by FAME, one of six centers of STARnet sponsored by MARCO and DARPA. The SQUID microscope and sensors were developed with support from the NSF-sponsored Center NSF-NSEC 0830228, and from NSF IMR-MIP 0957616.

  10. Use of Yttrium-90 TheraSphere for the treatment of unresectable hepatocellular carcinoma.

    Science.gov (United States)

    Liu, Michael D; Uaje, Michelle B; Al-Ghazi, Muthana S; Fields, Denise; Herman, June; Kuo, Jeffrey V; Milne, Norah; Nguyen, Thong H; Ramsinghani, Nilam S; Tokita, Kenneth M; Tsai, Fong Y; Vajgrt, Duane J; Imagawa, David K

    2004-11-01

    This is a retrospective analysis of a new treatment modality, intra-arterial administration of Yttrium-90 TheraSphere, for unresectable hepatocellular carcinoma (HCC). Patients with HCC not amenable to surgical treatment who had satisfactory physiological function without comorbid disease or significant pulmonary shunting were eligible for treatment. Patients were categorized into complete, partial, or no response based on serum alpha-fetoprotein (AFP) levels and CT or MRI imaging. Fourteen patients were considered candidates for treatment. Three patients were excluded due to significant hepatopulmonary shunting. Eleven patients were treated with TheraSphere. One patient (9%) had a complete response, eight patients (78%) had a partial response, and two patients (18%) showed no response. Partial and complete responders with AFP-associated HCC demonstrated a median decrease in AFP levels of 79 per cent at 73 days. No patients developed liver toxicity nor died due to treatment. Five patients (45%) died of progressive disease at a median of 7 months post-treatment. Six patients (54%) were alive at a median of 11 months (range, 9 to 20 months). Okuda stage 2 and 3 patients showed a median survival of 11 months and 7 months, respectively. Yttrium-90 TheraSphere treatment for unresectable hepatocellular carcinoma is well tolerated and appears to extend survival.

  11. Experimental-statistical method for investigation of multicomponent yttrium garnet systems

    International Nuclear Information System (INIS)

    Kojouharoff, V.; Ionchey, H.

    1986-01-01

    In the present work, some problems are discussed arising in the construction and study of a mathematical model describing the synthesis of multicomponent yttrium garnets with predetermined microwave parameters. To construct the model, the following formula was used for Ca-V YIG substituted with In and Cr: Y/sub 3-2x/Ca/sub 2x/Fe/sub 5-(x+y+z)/In/sub y/Cr/sub z/V/sub x/O/sub 12/. For this purpose, ferrogarnets were synthesized differing in x, y, and z with their values chosen so as to obtain real roots of a set of equations of the type Y/sub k/ = ΣB/sub i/X/sub i/ + ΣB/sub ij/X/sub i/X/sub j/ + ΣB/sub ijk/X/sub i/X/sub j/X/sub k/, where Y/sub k/ are the ferrogarnet microwave properties. The graphical presentation of these solutions as triple diagrams is a very convenient way of obtaining ferrogarnets with predetermined microwave characteristics. The possibility is created of mathematically predicting and determining the influence of the different components on the yttrium ferrogarnet parameters as a function of their concentration

  12. Evaluation of critical distances for energy transfer between Pr{sup 3+} and Ce{sup 3+} in yttrium aluminium garnet

    Energy Technology Data Exchange (ETDEWEB)

    Zeng, Peng; Wei, Xiantao; Yin, Min; Chen, Yonghu, E-mail: yhuchen@ustc.edu.cn [Key Laboratory of Strongly-Coupled Quantum Matter Physics, Chinese Academy of Sciences, School of Physical Sciences, University of Science and Technology of China, No. 96 Jinzhai Road, Hefei, Anhui 230026 (China); Zhou, Shaoshuai [Key Laboratory of Strongly-Coupled Quantum Matter Physics, Chinese Academy of Sciences, School of Physical Sciences, University of Science and Technology of China, No. 96 Jinzhai Road, Hefei, Anhui 230026 (China); Department of Physics, Qufu Normal University, Qufu, Shandong 273165 (China)

    2016-09-07

    A series of Pr{sup 3+}/Ce{sup 3+} doped yttrium aluminium garnet (Y{sub 3}Al{sub 5}O{sub 12} or simply YAG) phosphors were synthesized to investigate the energy transfer between Pr{sup 3+} and Ce{sup 3+} for their potential application in a white light-emitting diode and quantum information storage and processing. The excitation and emission spectra of YAG:Pr{sup 3+}/Ce{sup 3+} were measured and analyzed, and it revealed that the reabsorption between Pr{sup 3+} and Ce{sup 3+} was so weak that it can be ignored, and the energy transfer from Pr{sup 3+} (5d) to Ce{sup 3+} (5d) and Ce{sup 3+} (5d) to Pr{sup 3+} ({sup 1}D{sub 2}) did occur. By analyzing the excitation and the emission spectra, the energy transfer from Pr{sup 3+} (5d) to Ce{sup 3+} (5d) and Ce{sup 3+} (5d) to Pr{sup 3+} ({sup 1}D{sub 2}) was examined in detail with an original strategy deduced from fluorescence dynamics and the Dexter energy transfer theory, and the critical distances of energy transfer were derived to be 7.9 Å and 4.0 Å for Pr{sup 3+} (5d) to Ce{sup 3+} (5d) and Ce{sup 3+} (5d) to Pr{sup 3+} ({sup 1}D{sub 2}), respectively. The energy transfer rates of the two processes of various concentrations were discussed and evaluated. Furthermore, for the purpose of sensing a single Pr{sup 3+} state with a Ce{sup 3+} ion, the optimal distance of Ce{sup 3+} from Pr{sup 3+} was evaluated as 5.60 Å, where the probability of success reaches its maximum value of 78.66%, and meanwhile the probabilities were evaluated for a series of Y{sup 3+} sites in a YAG lattice. These results will be of valuable reference for achievement of the optimal energy transfer efficiency in Pr{sup 3+}/Ce{sup 3+} doped YAG and other similar systems.

  13. Biochemical investigation of yttrium(III) complex containing 1,10-phenanthroline: DNA binding and antibacterial activity.

    Science.gov (United States)

    Khorasani-Motlagh, Mozhgan; Noroozifar, Meissam; Moodi, Asieh; Niroomand, Sona

    2013-03-05

    Characterization of the interaction between yttrium(III) complex containing 1,10-phenanthroline as ligand, [Y(phen)2Cl(OH2)3]Cl2⋅H2O, and DNA has been carried out by UV absorption, fluorescence spectra and viscosity measurements in order to investigate binding mode. The experimental results indicate that the yttrium(III) complex binds to DNA and absorption is decreasing in charge transfer band with the increase in amount of DNA. The binding constant (Kb) at different temperatures as well as thermodynamic parameters, enthalpy change (ΔH°) and entropy change (ΔS°), were calculated according to relevant fluorescent data and Vant' Hoff equation. The results of interaction mechanism studies, suggested that groove binding plays a major role in the binding of the complex and DNA. The activity of yttrium(III) complex against some bacteria was tested and antimicrobial screening tests shown growth inhibitory activity in the presence of yttrium(III) complex. Copyright © 2013 Elsevier B.V. All rights reserved.

  14. Pemisahan Unsur Samarium dan Yttrium dari Mineral Tanah Jarang dengan Teknik Membran Cair Berpendukung (Supported Liquid Membrane

    Directory of Open Access Journals (Sweden)

    Amri Amin

    2009-06-01

    Full Text Available he increasing use of rare earth elements in high technology industries needs to be supported by developmental work for the separation of elements. The research objective is fiercely attracting and challenging considering the similarity of bath physical and chemical properties among these elements. The rate separation of samarium and yttrium elements using supported liquid membrane has been studied. Polytetrafluoroethylene (PTFE with pore size of 0.45 µm has been used as the membrane and di(2-ethylhexyl phosphate (D2EHP in hexane has been used as a carrier and nitric acid solution has been used as receiving phase. Result of experiments showed that the best separation rate of samarium and yttrium elements could be obtained at feeding phase of pH 3.0, di(2-ethylhexyl phosphate (D2EHP concentration of 0.3 M, agitation rate of 700 rpm, agitation time of 2 hours, and nitric acid and its solution concentrations of 1.0 M and 0.1 M, respectively. At this condition, separation rates of samarium and yttrium were 64.4 and 67.6%, respectively.   Keywords: liquid membrane, rare earth elements, samarium, yttrium

  15. Compounds of addition between yttrium and rare-earths (III) nitrates and the N,N,N'N'-tetramethyladipamide (TMAA)

    International Nuclear Information System (INIS)

    Lima, W.N. de.

    1974-01-01

    The synthesis of addition compounds between hydrated rare-earths and yttrium nitrates with the diamine N,N,N',N'-tetramethyladipamide (TMAA) in ethanol, is described. The compounds were characterized by elemental analisys, infrared, Raman, visible and near infrared spectra, molar conductance and molecular weight measurements, conductometric titrations and X-ray powder patterns. (Author) [pt

  16. ICP-MS determination of rare earth elements, yttrium, uranium and thorium in niobium-tantalum rich samples

    International Nuclear Information System (INIS)

    Sunilkumar, Beena; Padmasubashini, V.

    2013-01-01

    ICP-MS is a powerful and extremely sensitive technique which has been applied successfully for the determination of REEs in diverse geological samples. In the present work, ICP-MS has been applied for the rapid determination of REEs, yttrium as well as uranium and thorium in niobium and tantalum rich samples, using a fluoride fusion method for sample dissolution

  17. The influence of predeformations and annealings on yield stress and modulus of elongation essentially yttrium doped copper

    International Nuclear Information System (INIS)

    Neklyudov, I.M.; Sytin, V.I.; Voevodin, V.N.

    2003-01-01

    The researches results of influence of predeformations and annealings on elastic and plastic characteristics of vacuum melting and yttrium doped copper are given. The interrelation between elastic and plastic characteristics has been shown. It is shown that the yield stress and modulus of elongation essentially depend on predeformations and annealings and they are the structurally sensitive characteristics

  18. Effect of surface composition of yttrium-stabilized zirconia on partial oxidation of methane to synthesis gas.

    NARCIS (Netherlands)

    Zhu, J.J.; van Ommen, J.G.; Knoester, A.; Lefferts, Leonardus

    2005-01-01

    Catalytic partial oxidation of methane to synthesis gas (CPOM) over yttrium-stabilized zirconia (YSZ) was studied within a wide temperature window (500¿1100 °C). The catalysts were characterized by X-ray fluorescence (XRF) and low-energy ion scattering (LEIS). The influence of calcination

  19. Effect of phase composition on the corrosion properties of alloys of the magnesium-yttrium system in neutral solutions

    International Nuclear Information System (INIS)

    Krasnoyarskii, V.V.; Petrova, L.M.; Dobatkina, T.V.; Korol'kova, I.G.

    1992-01-01

    A study is made of the effect of phase composition on the corrosive dissolution of binary alloys of the system magnesium-8.2% yttrium. It is shown that the appearance of the intermetallide Mg 24 Y 5 - being the effective cathode - intensifies self-dissolution of the alloy under conditions of anodic galvanostatic polarization

  20. A novel KMgPO{sub 4}:Tb{sup 3+}(KMPT) phosphor for radiation dosimetry

    Energy Technology Data Exchange (ETDEWEB)

    Palan, C.B., E-mail: chetanpalan27@gmail.com [Department of Physics, Sant Gadge Baba Amravati University, Amravati 44602 (India); Bajaj, N.S. [Department of Physics, Toshniwal ACS College, Sengaon, Hingoli 431542 (India); Soni, A. [Radiological Physics and Advisory Division, Bhabha Atomic Research Centre, Mumbai 400094 (India); Omanwar, S.K. [Department of Physics, Sant Gadge Baba Amravati University, Amravati 44602 (India)

    2016-08-15

    The polycrystalline sample of KMgPO{sub 4}:Tb{sup 3+}(KMPT) phosphor was successfully synthesized by using solid state method. The X-ray powder diffraction, photoluminescence (PL) emission and excitation spectra, thermoluminescence (TL) and optically stimulated luminescence (OSL) were thoroughly measured. The PL spectra of as-prepared KMPT phosphor showed characteristic blue-green emission, when excited by 226 nm under UV excitation. The optimum PL intensity was observed at 0.01 mol concentration of Tb{sup 3+}ions and this phosphor used for remaining studies. The TL glow curve of KMPT phosphor consist two characterized peaks, which were deconvoluted and the kinetic parameters i.e. trap depth or activation energy, order of kinetic and frequency factor determined by using peak shape method. TL sensitivity of KMPT phosphors was found to be 10% than that of TL sensitivity of TLD-500 phosphor. The OSL sensitivity of KMPT was 0.92 times than OSL sensitivity of α-Al{sub 2}O{sub 3}:C phosphor. The OSL decay curve KMPT phosphor consist of three component having photoionization cross sections were found to be 0.26548×10{sup −17}, 0.220×10{sup −17}, 2.92×10{sup −17} cm{sup 2}. The KMPT phosphor showed linear dose response in range 100–6000 mGy and fading of KMPT phosphor was found to be 31% in 15 days. The Minimum detectable dose (MDD) was found to be 0.39 mGy with corresponding 3σ back ground. The phosphor shows good dosimetry properties such as sensitivity, dose response, MDD, Fading.