  1. Preparation of YBCO superconducting films by spray pyrolysis method

    International Nuclear Information System (INIS)

    Mora Alonso, M.; Leyva Fabelo, A.; Rubio Frias, E.; Pupo Gonzalez, I.; Lopez Sanchez, D.

    1994-01-01

    The methodology for the preparation of YBCO superconducting films on Zr 2O (Y) substrates by spray pyrolysis method is reported. The transition temperature of these films is superior than the boiling temperature of liquid 2N . Other critical parameters are similar to those reported by other authors using the same technique

  2. Strong Flux Pinning of Nano-Sized Ysz Particles in Ybco Films Prepared by Mod Method

    Science.gov (United States)

    Ye, S.; Suo, H. L.; Liu, M.; Tang, X.; Wu, Z. P.; Zhao, Y.; Zhou, M. L.

    The YBCO films with doped YSZ nanoparticles have been prepared successfully by metal organic doepositon method using trifluoroacetates (TFA-MOD) through dissolving Zr organic salt into the YBCO precursor solution. The doped films have well in-plane and out-plane textures detected by both XRD Φ-scan and ω-scan. The YSZ nanoparticles with the size of about 5 ~ 15 nm were observed on the surface of the YBCO films using both FE-SEM and TEM. By comparing the superconducting properties, it was found that the doped YBCO films had lower Tc than that of undoped YBCO films. However, as increasing the applied magnetic field, Jc of the doped YBCO films were much better than that of undoped one. The Jc was as higher as 2.5 times than that of undoped YBCO film at 77 K and 1 T applied field.

  3. Surface resistances of 5-cm-diameter YBCO films prepared by MOD for microwave applications

    International Nuclear Information System (INIS)

    Manabe, T.; Sohma, M.; Yamaguchi, I.; Tsukada, K.; Kondo, W.; Kamiya, K.; Tsuchiya, T.; Mizuta, S.; Kumagai, T.

    2006-01-01

    Large-area high-T c superconducting films with low surface resistances R s are required for use in microwave applications such as band pass filters. In this paper, preparation of 5-cm-diameter YBCO films on LaAlO 3 (LAO) and CeO 2 -buffered sapphire (CbS) substrates by metalorganic deposition (MOD) using a fluorine-free coating solution and their superconducting properties are described. The optimum firing conditions for YBCO films greatly depend on the substrate materials; a heating rate at ramp as high as 200 deg. C /min is necessary for films on LAO whereas a lower heating rate, e.g., 20 deg. C /min, is required for films on CbS. Accordingly, the suitable furnace systems for these substrates have been varied. As a result, a YBCO film with high J c (77 K) of 2.7 MA/cm 2 and a low R s (12 GHz, 77 K) of 0.54 mΩ was prepared on LAO by using an infrared image furnace. On the other hand, a YBCO film with a higher J c (77 K) of 4.0 MA/cm 2 and the same R s (12 GHz, 77 K) of 0.54 mΩ was prepared on CbS by using a tube furnace

  4. Preparation of PZT thin films on YBCO electrodes by KrF excimer laser ablation technique

    International Nuclear Information System (INIS)

    Kurogi, H.; Yamagata, Y.; Ebihara, K.

    1998-01-01

    Pb(Zr X Ti 1-X )O 3 (PZT) films have excellent ferroelectric, optical, piezoelectric, and pyroelectric properties. We prepared PZT thin films by the excimer laser ablation technique. A pulsed KrF excimer laser (Lambda Physik LPX305icc, pulse duration of 25 ns, λ=248 nm, 850 mJ Max.) was used to ablate the bulk targets. We investigated the influence of bottom electrode materials on the characteristics of the PZT thin films prepared on Pt and YBCO underlayers. The X-ray diffraction (XRD) patterns showed that the PZT films prepared with a laser fluence of 2 Jcm -2 on YBCO/MgO(100) substrate at a wide temperature range of 550-680 C have a perovskite (001) structure. At the same laser fluence, the PZT films prepared on Pt/MgO(100) substrate have a perovskite (001) structure only at 650 C. The polarization-electric field (P-E) characteristics and fatigue properties of PZT thin films were measured by the Sawyer-Tower circuit. The remnant polarization and coercive field have been found to be P r =15 μC cm -2 , 30 μC cm -2 and E c =200 kV cm -1 , 100 kV cm -1 for Au/PZT/Pt/MgO and Au/PZT/YBCO/MgO correspondingly. The remnant polarization of Au/PZT/YBCO/MgO thin film was reduced to one-half after about 10 8 cycles of switching. (orig.)

  5. Preparation of PZT thin films on YBCO electrodes by KrF excimer laser ablation technique

    Energy Technology Data Exchange (ETDEWEB)

    Kurogi, H; Yamagata, Y; Ebihara, K [Kumamoto Univ. (Japan). Dept. of Electr. Eng. and Comput. Sci.; Inoue, N [Kyushu Electric Power Co., Inc., Suizenji, 1-6-36, Kumamoto 862 (Japan)

    1998-03-01

    Pb(Zr{sub X}Ti{sub 1-X})O{sub 3} (PZT) films have excellent ferroelectric, optical, piezoelectric, and pyroelectric properties. We prepared PZT thin films by the excimer laser ablation technique. A pulsed KrF excimer laser (Lambda Physik LPX305icc, pulse duration of 25 ns, {lambda}=248 nm, 850 mJ Max.) was used to ablate the bulk targets. We investigated the influence of bottom electrode materials on the characteristics of the PZT thin films prepared on Pt and YBCO underlayers. The X-ray diffraction (XRD) patterns showed that the PZT films prepared with a laser fluence of 2 Jcm{sup -2} on YBCO/MgO(100) substrate at a wide temperature range of 550-680 C have a perovskite (001) structure. At the same laser fluence, the PZT films prepared on Pt/MgO(100) substrate have a perovskite (001) structure only at 650 C. The polarization-electric field (P-E) characteristics and fatigue properties of PZT thin films were measured by the Sawyer-Tower circuit. The remnant polarization and coercive field have been found to be P{sub r}=15 {mu}C cm{sup -2}, 30 {mu}C cm{sup -2} and E{sub c}=200 kV cm{sup -1}, 100 kV cm{sup -1} for Au/PZT/Pt/MgO and Au/PZT/YBCO/MgO correspondingly. The remnant polarization of Au/PZT/YBCO/MgO thin film was reduced to one-half after about 10{sup 8} cycles of switching. (orig.) 7 refs.

  6. Preparation and structural properties of YBCO films grown on GaN/c-sapphire hexagonal substrate

    Energy Technology Data Exchange (ETDEWEB)

    Chromik, S., E-mail: stefan.chromik@savba.sk [Institute of Electrical Engineering, SAS, Dubravska cesta 9, 84104 Bratislava (Slovakia); Gierlowski, P. [Institute of Physics, Polish Academy of Sciences, Al. Lotnikow 32/46, 02-668 Warsaw (Poland); Spankova, M.; Dobrocka, E.; Vavra, I.; Strbik, V.; Lalinsky, T.; Sojkova, M. [Institute of Electrical Engineering, SAS, Dubravska cesta 9, 84104 Bratislava (Slovakia); Liday, J.; Vogrincic, P. [Department of Microelectronics, Slovak Technical University, Ilkovicova 3, 81219 Bratislava (Slovakia); Espinos, J.P. [Instituto de Ciencia de Materiales de Sevilla, Avda Americo Vespucio 49, 41092 Sevilla (Spain)

    2010-07-01

    Epitaxial YBCO thin films have been grown on hexagonal GaN/c-sapphire substrates using DC magnetron sputtering and pulsed laser deposition. An MgO buffer layer has been inserted between the substrate and the YBCO film as a diffusion barrier. X-ray diffraction analysis indicates a c-axis oriented growth of the YBCO films. {Phi}-scan shows surprisingly twelve maxima. Transmission electron microscopy analyses confirm an epitaxial growth of the YBCO blocks with a superposition of three a-b YBCO planes rotated by 120 deg. to each other. Auger electron spectroscopy and X-ray photoelectron spectroscopy reveal no surface contamination with Ga even if a maximum substrate temperature of 700 deg. C is applied.

  7. Preparation of SmBCO layer for the surface optimization of GdYBCO film by MOCVD process based on a simple self-heating technology

    Science.gov (United States)

    Zhao, Ruipeng; Zhang, Fei; Liu, Qing; Xia, Yudong; Lu, Yuming; Cai, Chuanbing; Tao, Bowan; Li, Yanrong

    2018-07-01

    The MOCVD process was adopted to grow the REBa2Cu3O7-δ ((REBCO), RE = rare earth elements) films on the LaMnO3 (LMO) templates. Meanwhile, the LMO-template tapes are heated by the joule effect after applying a heating current through the Hastelloy metal substrates. The surface of GdYBCO films prepared by MOCVD method is prone to form outgrowths. So the surface morphology of GdYBCO film is optimized by depositing the SmBCO layer, which is an important process method for the preparation of high-quality multilayer REBCO films. At last, the GdYBCO/SmBCO/GdYBCO multilayer films were successfully prepared on the LMO templates based on the simple self-heating method. It is demonstrated that the GdYBCO surface was well improved by the characterization analysis of scanning electron microscope. And the Δω of REBCO (005) and Δφ of REBCO (103), which were performed by an X-ray diffraction system, are respectively 1.3° and 3.3° What's more, the critical current density (Jc) has been more than 3 MA/cm2 (77 K, 0 T) and the critical current (Ic) basically shows a trend of good linear increase with the increase of the number of REBCO layers.

  8. A comparative study on the flux pinning properties of Zr-doped YBCO film with those of Sn-doped one prepared by metal-organic deposition

    International Nuclear Information System (INIS)

    Choi, S. M.; Shin, G. M.; Joo, Y.S.; Yoo, S. I.

    2013-01-01

    We investigated the flux pinning properties of both 10 mol% Zr-and Sn-doped YBa 2 Cu 3 O 7-δ (YBCO) films with the same thickness of ∽350 nm for a comparative purpose. The films were prepared on the SrTiO 3 (STO) single crystal substrate by the metal-organic deposition (MOD) process. Compared with Sn-doped YBCO film, Zr-doped one exhibited a significant enhancement in the critical current density (J c ) and pinning force density (F p ). The anisotropic J c ,min/J c ,max ratio in the field-angle dependence of J c at 77 K for 1 T was also improved from 0.23 for Sn-doped YBCO to 0.39 for Zr-doped YBCO. Thus, the highest magnetic J c values of 9.0 and 2.9 MA/cm 2 with the maximum F p (F p ,max) values of 19 and 5 GN/m 3 at 65 and 77 K for H // c, respectively, could be achieved from Zr-doped YBCO film. The stronger pinning effect in Zr-doped YBCO film is attributable to smaller BaZrO-3 (BZO) nanoparticles (the average size ≈ 28.4 nm) than YBa 2 SnO 5. 5 (YBSO) nanoparticles (the average size ≈ 45.0 nm) incorporated in Sn-doped YBCO film since smaller nanoparticles can generate more defects acting as effective flux pinning sites due to larger incoherent interfacial area for the same doping concentration.

  9. Preparation of PZT/YBCO/YAlO heterostructure thin films by KrF excimer laser ablation

    International Nuclear Information System (INIS)

    Ebihara, Kenji; Kurogi, Hiromitsu; Yamagata, Yukihiko; Ikegami, Tomoaki; Grishin, A.M.

    1998-01-01

    The perovskite oxide YBa 2 Cu 3 O 7-x (YBCO) and Pb(Zr x Ti 1-x )O 3 (PZT) thin films have been deposited for superconducting-ferroelectric devices. KrF excimer laser ablation technique was used at the deposition conditions of 200--600 mTorr O 2 , 2-3J/cm 2 and 5--10 Hz operation frequency. Heterostructures of PZT-YBCO-YAlO 3 :Nd show the zero resistivity critical temperature of 82 K and excellent ferroelectric properties of remnant polarization 32 microC/cm 2 , coercive force of 80 kV/cm and dielectric constant 800. Cycling fatigue characteristics and leakage current are also discussed

  10. Critical current density and microwave surface resistance of 5-cm-diameter YBCO films on LaAlO3 substrates prepared by MOD using an infrared image furnace

    International Nuclear Information System (INIS)

    Manabe, T.; Kondo, W.; Yamaguchi, I.; Sohma, M.; Tsuchiya, T.; Tsukada, K.; Mizuta, S.; Kumagai, T.

    2005-01-01

    Inductive critical current density (J c ) and microwave surface resistance (R s ) were investigated for 0.7-μm-thick epitaxial YBa 2 Cu 3 O 7-y (YBCO) films on 5-cm-diameter LaAlO 3 substrates prepared by a chemical solution-based metal organic deposition (MOD) process using an infrared image furnace. By varying the heating rate at ramp during the final heat treatment, we obtained various orientations of YBCO; the c- and a-axis orientation at a slower rate, i.e., 20-100 deg C/min while the pure c-axis orientation at a faster rate, 200 deg C/min. The c-axis-oriented YBCO films showed excellent superconducting properties; for example, a high inductive-J c (77 K) of 2.6 MA/cm 2 and low R s (12 GHz)'s of 0.24 and 0.52 mΩ at 50 and 77 K, respectively, by a sapphire rod resonator method. The c- and a-axis-oriented films exhibited a lower J c and a higher R s . It was found that the J c and R s values of MOD-derived YBCO films showed a strong correlation; approximately, R s is inversely proportional to J c . This correlation is in good agreement with a previous report by Ohshima et al. for sputtered-YBCO films on BaSnO 3 -buffered MgO substrates

  11. Textured YBCO films grown on wires: application to superconducting cables

    International Nuclear Information System (INIS)

    Dechoux, N; Jiménez, C; Chaudouët, P; Rapenne, L; Sarigiannidou, E; Robaut, F; Petit, S; Garaudée, S; Porcar, L; Soubeyroux, J L; Odier, P; Bruzek, C E; Decroux, M

    2012-01-01

    Efforts to fabricate superconducting wires made of YBa 2 Cu 3 O 7 (YBCO) on La 2 Zr 2 O 7 (LZO) buffered and biaxially textured Ni-5 at.%W (NiW) are described. Wires were manually shaped from LZO buffered NiW tapes. Different diameters were produced: 1.5, 2 and 3 mm. The wires were further covered with YBCO grown by metal organic chemical vapor deposition (MOCVD). We developed an original device in which the round substrate undergoes an alternated rotation of 180° around its axis in addition to a reel-to-reel translation. This new approach allows covering the whole circumference of the wire with a YBCO layer. This was confirmed by energy dispersive x-ray spectroscopy (EDX) analysis coupled to a scanning electron microscope (SEM). For all wire diameters, the YBCO layer thickness varied from 300 to 450 nm, and the cationic composition was respected. Electron backscattering diffraction (EBSD) measurements were performed directly on an as-deposited wire without surface preparation allowing the investigation of the crystalline quality of the film surface. Combining EBSD with XRD results we show that YBCO grows epitaxially on the LZO buffered NiW wires. For the first time, superconductive behaviors have been detected on round substrates in both the rolling and circular direction. J c reached 0.3 MA cm −2 as measured at 77 K by transport and third-harmonic detection. Those preliminary results confirm the effectiveness of the MOCVD for complex geometries, especially for YBCO deposition on small diameter wires. This approach opens huge perspectives for the elaboration of a new generation of YBCO-based round conductors. (paper)

  12. Vortex pinning landscape in MOD-TFA YBCO nanostroctured films

    Science.gov (United States)

    Gutierrez, J.; Puig, T.; Pomar, A.; Obradors, X.

    2008-03-01

    A methodology of general validity to study vortex pinning in YBCO based on Jc transport measurements is described. It permits to identify, separate and quantify three basic vortex pinning contributions associated to anisotropic-strong, isotropic-strong and isotropic-weak pinning centers. Thereof, the corresponding vortex pinning phase diagrams are built up. This methodology is applied to the new solution-derived YBCO nanostructured films, including controlled interfacial pinning by the growth of nanostructured templates by means of self-assembled processes [1] and YBCO-BaZrO3 nanocomposites prepared by modified solution precursors. The application of the methodology and comparison with a standard solution-derived YBCO film [2], enables us to identify the nature and the effect of the additional pinning centers induced. The nanostructured templates films show c-axis pinning strongly increased, controlling most of the pinning phase diagram. On the other hand, the nanocomposites have achieved so far, the highest pinning properties in HTc-superconductors [3], being the isotropic-strong defects contribution the origin of their unique properties. [1] M. Gibert et al, Adv. Mat. vol 19, p. 3937 (2007) [2] Puig.T et al, SuST EUCAS 2007 (to be published) [3] J. Gutierrez et al, Nat. Mat. vol. 6, p. 367 (2007) * Work supported by HIPERCHEM, NANOARTIS and MAT2005-02047

  13. Growth and BZO-doping of the nanostructured YBCO thin films on buffered metal substrates

    DEFF Research Database (Denmark)

    Huhtinen, H.; Irjala, M.; Paturi, P.

    2010-01-01

    The growth of the nanostructured YBa2Cu3O6+x (YBCO) films is investigated for the first time on biaxially textured NiW substrates used in coated conductor technology. The optimization process of superconducting layers is made in wide magnetic field and temperature range in order to understand...... the vortex pinning structure and mechanism in our films prepared from nanostructured material. Structural analysis shows that growth mechanism in YBCO films grown on NiW is completely different when compared to YBCO on STO. Films on NiW are much rougher, there is huge in-plane variation of YBCO crystals...... and moreover out-of-plane long range lattice ordering is greatly reduced. Magnetic measurements demonstrate that jc in films grown on NiW is higher in high magnetic fields and low temperatures. This effect is connected to the amount of pinning centres observed in films on metal substrates which are effective...

  14. Chemical solution deposition of YBCO thin film by different polymer additives

    International Nuclear Information System (INIS)

    Wang, W.T.; Li, G.; Pu, M.H.; Sun, R.P.; Zhou, H.M.; Zhang, Y.; Zhang, H.; Yang, Y.; Cheng, C.H.; Zhao, Y.

    2008-01-01

    A polymer-assisted chemical solution deposition approach has been proposed for the preparation of YBCO thin film. Different additives like PVB (polyvinyl butyral), PEG (polyethylene glycol) and PVP (polyvinylpyrrolidone) have been used to adjust the final viscosity of the precursor solution and thus the film formation. In this fluorine-free approach, YBCO has been deposited on single crystal substrates with metal acetates being starting materials. Biaxially textured YBCO thin films have been obtained. However, different additives lead to different microstructure. Dense, smooth and crack-free YBCO film prepared with PVB as additive yields sharp superconducting transition around T c = 90 K as well as high J c (0 T, 77 K) over 3 MA/cm 2

  15. Chemical solution deposition of YBCO thin film by different polymer additives

    Energy Technology Data Exchange (ETDEWEB)

    Wang, W.T.; Li, G.; Pu, M.H.; Sun, R.P.; Zhou, H.M.; Zhang, Y. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China, Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); Zhang, H. [Department of Physics, Peking University, Beijing 100871 (China); Yang, Y. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China, Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); Cheng, C.H. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China, Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia); Zhao, Y. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China, Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia)], E-mail: yzhao@swjtu.edu.cn

    2008-09-15

    A polymer-assisted chemical solution deposition approach has been proposed for the preparation of YBCO thin film. Different additives like PVB (polyvinyl butyral), PEG (polyethylene glycol) and PVP (polyvinylpyrrolidone) have been used to adjust the final viscosity of the precursor solution and thus the film formation. In this fluorine-free approach, YBCO has been deposited on single crystal substrates with metal acetates being starting materials. Biaxially textured YBCO thin films have been obtained. However, different additives lead to different microstructure. Dense, smooth and crack-free YBCO film prepared with PVB as additive yields sharp superconducting transition around T{sub c} = 90 K as well as high J{sub c} (0 T, 77 K) over 3 MA/cm{sup 2}.

  16. Enhancement of flux pinning of TFA-MOD YBCO thin films by embedded nanoscale Y2O3

    International Nuclear Information System (INIS)

    Cui, X M; Tao, B W; Tian, Z; Xiong, J; Zhang, X F; Li, Y R

    2006-01-01

    YBCO films with different levels of excess yttrium were prepared on single-crystal LaAlO 3 with metal-organic deposition using trifluoroacetates (TFA-MOD). X-ray diffraction and transmission electron microscope measurements revealed excess yttrium in YBCO in the form of nanoscale Y 2 O 3 with (400) preferred orientation. The field dependence of J c demonstrated that YBCO films with Y 2 O 3 doping had enhanced J c in comparison with stoichiometric YBCO films in the magnetic fields. We think the reason for this is that the Y 2 O 3 nanoparticles act as pinning centres. YBCO films with 60% yttrium excess display 43% increased J c compared to stoichiometric YBCO films at a magnetic field of 1 T

  17. Enhanced flux-pinning in fluorine-free MOD YBCO films by chemical doping

    Energy Technology Data Exchange (ETDEWEB)

    Wang, W.T.; Pu, M.H.; Yang, Y. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Zhang, H. [Department of Physics, Peking University, Beijing 100871 (China); Cheng, C.H. [Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia); Zhao, Y., E-mail: yzhao@swjtu.edu.c [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia)

    2010-11-01

    YBCO films without and with dilute cobalt and zinc doping were prepared on (0 0 l) LaAlO{sub 3} substrate by non-fluorine metal organic deposition method. Effects of dilute cobalt and zinc doping on biaxial texture, microstructure and flux-pinning properties of YBCO films were investigated. The surface density and smoothness of the doped YBCO films have been distinctly improved compared with that of the pure film. Dilute cobalt- and zinc-doped YBCO films exhibit significantly enhanced J{sub c} values in the magnetic field. The best result is achieved in the cobalt-doped YBCO film. At 77 K, J{sub c} values of cobalt-doped film are 1.7 and 5.4 times higher than that of pure film in 0.5 T and 1.5 T, respectively. These results strongly suggest that dilute cobalt and zinc doping is a promising way to increase the current carrying capability of YBCO films.

  18. High quality uniform YBCO film growth by the metalorganic deposition using trifluoroacetates

    Energy Technology Data Exchange (ETDEWEB)

    Wang, S.S., E-mail: wangssh@tsinghua.edu.cn [Key Laboratory of Micro-nano Measurement, Manipulation and Physics (Beihang University), Ministry of Education, Beijing 100191 (China); Beijing Dingchen Superconducting Technology Co., Ltd., Beijing 100084 (China); Zhang, Z.L. [Key Laboratory of Micro-nano Measurement, Manipulation and Physics (Beihang University), Ministry of Education, Beijing 100191 (China); Wang, L. [Applied superconductivity research center, Department of Physics, Tsinghua University, Beijing 100084 (China); Gao, L.K.; Liu, J. [Beijing Dingchen Superconducting Technology Co., Ltd., Beijing 100084 (China)

    2017-03-15

    Highlights: • High quality double-sided YBCO films are fabricated on LaAlO3 substrates by TFA-MOD method with diameters up to 2 in. • Large area YBCO films were very uniform in microstructure and thickness distribution, an average inductive Jc in excess of 6 MA/cm{sup 2} and low R{sub s} (10 GHz) of 0.3 mΩ at 77 K were obtained. • It will greatly promoted the research and applications of large-area YBCO films by chemical solution method. - Abstract: A need exists for the large-area superconducting YBa{sub 2}Cu{sub 3}O{sub 7-x} (YBCO) films with high critical current density for microwave communication and/or electric power applications. Trifluoroacetic metalorganic (TFA-MOD) method is a promising low cost technique for large-scale production of YBCO films, because it does not need high vacuum device and is easily applicable to substrates of various shape and size. In this paper, double-sided YBCO films with maximum 2 in diameter were prepared on LaAlO{sub 3} substrates by TFA-MOD method. Inductive critical current densitiy J{sub c}, microwave surface resistance R{sub s}, as well as the microstructure were characterized. A newly homemade furnace system was used to epitaxially grown YBCO films, which can improve the uniformity of YBCO film significantly by gas supply and temperature distribution proper design. Results showed that the large area YBCO films were very uniform in microstructure and thickness distribution, an average inductive J{sub c} in excess of 6 MA/cm{sup 2} with uniform distribution, and low R{sub s} (10 GHz) below 0.3 mΩ at 77 K were obtained. Andthe film filter may be prepared to work at temperatures lower than 74 K. These results are very close to the highest value of YBCO films made by conventional vacuum method, so we show a very promising route for large-scale production of high quality large-area YBCO superconducting films at a lower cost.

  19. Flux pinning in MOD YBCO films by chemical doping

    International Nuclear Information System (INIS)

    Zhou, Y X; Ghalsasi, S; Rusakova, I; Salama, K

    2007-01-01

    A novel nanomaterial synthesis technique has been developed to introduce 0D (particles), 1D (columnar defects) and 3D (domains) nanoscale pinning centres in MOD Y 1 Ba 2 Cu 3 O 7 (YBCO) coated conductors. We have succeeded in introducing nanoscale Y enriched particles, nanoscale 90 0 rotated Y 1/3 Sm 2/3 Ba 2 Cu 3 O 7 domains and nanoscale Zr enriched columnar defects into YBCO layers by different chemical doping. The pinning force density in Y 2 O 3 -doped YBCO film is found to be larger than that of pure YBCO film at all fields. Also it was found that YBCO films with Sm substituting for Y have yielded improved critical current density characteristics over a wide range of magnetic fields. Maximum pinning force densities exceeding 7 and 8 GN m -3 are obtained in 5% BZO-doped and Sm substituted YBCO films, respectively. Additionally, TEM studies revealed nanoscale Zr enriched columnar defects distributing in the matrix of the c-oriented YBCO film throughout the whole cross section. This indicates that chemical doping is a promising fabrication technique to create specific pinning landscapes in YBCO coated conductors

  20. Magnetron sputtering of Fe-oxides on the top of HTS YBCO films

    International Nuclear Information System (INIS)

    Nurgaliev, T.; Blagoev, B.; Buchkov, K.; Mateev, E.; Gajda, G.; Nedkov, I.; Kovacheva, D.; Slavov, L.; Starbova, I.; Starbov, N.; Nankovski, M.

    2017-01-01

    The possibilities for preparation of bilayers containing magnetic Fe-oxide (Fe-O) and high temperature superconducting (HTS) YBa 2 Cu 3 O 7−x (YBCO) thin films were investigated. For this purpose, Fe-O films were deposited using reactive magnetron sputtering at comparatively low temperatures T≤250 °C onto dielectric (for example, LaAlO 3 (LAO)) substrates, covered with a HTS YBCO film. The sputtering of the Fe-O layer at such conditions did not lead to a crucial damage of the critical temperature T C of the YBCO film, but could affect the width of the superconducting transition. A decrease of the critical temperature of the (Fe-O)/YBCO/LAO bilayer kept at ambient conditions was observed, possibly due to the negative effects of the water vapour on the sample characteristics. The double peak structure of the imaginary component of the response signal to the AC harmonic magnetic field, observed in such a (Fe-O)/YBCO/LAO sample, was ascribed from two possible views: as a consequence of morphology determined inter- and intra-granular contributions and/or as transitions from dominant irreversible processes as Bean-Livingston barrier to vortex state chains formation. - Highlights: • Iron-oxide (Fe-O) film sputtered on the top of superconducting HTS YBCO film at not very high temperatures. • No crucially damaged superconducting properties of YBCO film during Fe-O sputtering process. • A negative effect of the ambient conditions on the critical temperature of the obtained samples. • A double peak structure of the response signal to the AC harmonic magnetic field in a (Fe-O)/YBCO/LAO is observed.

  1. Magnetron sputtering of Fe-oxides on the top of HTS YBCO films

    Energy Technology Data Exchange (ETDEWEB)

    Nurgaliev, T. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Blagoev, B. [Institute of Solid State Physics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Laboratory of High Magnetic Fields and Low Temperatures, 95 Gajowicka Str., 53-421 Wroclaw (Poland); Buchkov, K. [Institute of Solid State Physics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Mateev, E. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Gajda, G. [Laboratory of High Magnetic Fields and Low Temperatures, 95 Gajowicka Str., 53-421 Wroclaw (Poland); Nedkov, I. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Kovacheva, D. [Institute of General and Inorganic Chemistry, Bulgarian Academy of Sciences, Acad. G. Bonchev Street, bl. 10, 1113 Sofia (Bulgaria); Slavov, L. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Laboratory of High Magnetic Fields and Low Temperatures, 95 Gajowicka Str., 53-421 Wroclaw (Poland); Starbova, I.; Starbov, N. [Institute of Solid State Physics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Nankovski, M. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Sofia university “St. Kliment Ohridski”, Faculty of Physics, 5 James Bourchier Blvd., 1164 Sofia (Bulgaria)

    2017-05-01

    The possibilities for preparation of bilayers containing magnetic Fe-oxide (Fe-O) and high temperature superconducting (HTS) YBa{sub 2}Cu{sub 3}O{sub 7−x} (YBCO) thin films were investigated. For this purpose, Fe-O films were deposited using reactive magnetron sputtering at comparatively low temperatures T≤250 °C onto dielectric (for example, LaAlO{sub 3} (LAO)) substrates, covered with a HTS YBCO film. The sputtering of the Fe-O layer at such conditions did not lead to a crucial damage of the critical temperature T{sub C} of the YBCO film, but could affect the width of the superconducting transition. A decrease of the critical temperature of the (Fe-O)/YBCO/LAO bilayer kept at ambient conditions was observed, possibly due to the negative effects of the water vapour on the sample characteristics. The double peak structure of the imaginary component of the response signal to the AC harmonic magnetic field, observed in such a (Fe-O)/YBCO/LAO sample, was ascribed from two possible views: as a consequence of morphology determined inter- and intra-granular contributions and/or as transitions from dominant irreversible processes as Bean-Livingston barrier to vortex state chains formation. - Highlights: • Iron-oxide (Fe-O) film sputtered on the top of superconducting HTS YBCO film at not very high temperatures. • No crucially damaged superconducting properties of YBCO film during Fe-O sputtering process. • A negative effect of the ambient conditions on the critical temperature of the obtained samples. • A double peak structure of the response signal to the AC harmonic magnetic field in a (Fe-O)/YBCO/LAO is observed.

  2. Preparation of YBCO on YSZ layers deposited on silicon and sapphire by MOCVD: influence of the intermediate layer on the quality of the superconducting film

    International Nuclear Information System (INIS)

    Garcia, G.; Casado, J.; Llibre, J.; Doudkowski, M.; Santiso, J.; Figueras, A.; Schamm, S.; Dorignac, D.; Grigis, C.; Aguilo, M.

    1995-01-01

    YSZ buffer layers were deposited on silicon and sapphire by MOCVD. The layers deposited on silicon were highly oriented along [100] direction without in-plane orientation, probably because the existence of the SiO 2 amorphous interlayer. In contrast, epitaxial YSZ was obtained on (1-102) sapphire showing an in-plane texture defined by the following relationships: (100) YSZ // (1-102) sapphire and (110) YSZ // (01-12) sapphire. Subsequently, YBCO films were deposited on YSZ by MOCVD. Structural, morphological and electrical characterization of the superconducting layers were correlated with the in-plane texture of the buffer layers. (orig.)

  3. Quality of YBCO thin films grown on LAO substrates exposed to the film deposition - film removal processes

    Energy Technology Data Exchange (ETDEWEB)

    Blagoev, B; Nurgaliev, T [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tzarigradsko Chaussee, 1784 Sofia (Bulgaria); Mozhaev, P B [Institute of Physics and Technology, Russian Academy of Sciences, 117218 Moscow (Russian Federation); Sardela, M; Donchev, T [Materials Research Laboratory, University of Illinois, 104 South Goodwin Ave., Urbana, IL 61801 (United States)], E-mail: blago_sb@yahoo.com

    2008-05-01

    The characteristics are investigated of high temperature superconducting YBa{sub 2}Cu{sub 3}O{sub 7} (YBCO) films grown on LaAlO{sub 3} (LAO) substrates being exposed a different number of times to YBCO film deposition and acid-solution-based cleaning procedures. Possible mechanisms of degradation of the substrate surface quality reflecting on the growing YBCO film parameters are discussed and analyzed.

  4. Distribution analysis of thermal effusivity for sub-micrometer YBCO thin films using thermal microscope

    International Nuclear Information System (INIS)

    Yagi, T.; Taketoshi, N.; Kato, H.

    2004-01-01

    Thermal effusivity measurements have been carried out for sub-micrometer YBCO superconducting films using thermal microscope based upon thermoreflectance technique. Two samples were prepared: c-axis aligned YBCO thin films with 800 nm in thickness synthesized on MgO and SrTiO 3 substrates. Measured thermal effusivities perpendicular to the surface, i.e. in parallel with c-axis were determined to be 1770 J/m 2 s 0.5 K on MgO substrate and 1420 J/m 2 s 0.5 K for that on SrTiO 3 substrate, respectively. The scatter of the measurements is estimated to be lower than ±5.2%. These values are consistent with reported values of YBCO single crystal in the direction of c-axis. In addition, 2D profiling image, that is, in-plane distribution of thermal effusivity was well obtained for the YBCO film on MgO substrate by operating this thermal microscope in a scanning mode. Its standard deviation of the in-plane thermal effusivity scattering due to the non-uniformity is evaluated to be ±5.7%

  5. Flux pinning characteristics of Sn-doped YBCO film by the MOD process

    International Nuclear Information System (INIS)

    Choi, S.M.; Shin, G.M.; Yoo, S.I.

    2013-01-01

    Highlights: ► The pinning effects of undoped and Sn-doped YBCO films by MOD were characterized. ► Sn-containing nanoparticles were trapped in Sn-doped YBCO films by MOD. ► Sn-containing nanoparticles were identified as the YBa 2 SnO 5.5 (YBSO) phase by TEM. ► The YBSO nanoparticles are responsible for improved flux pinning effect. ► We report the orientation relationship between YBSO nanoparticles and YBCO matrix. -- Abstract: Compared with the undoped YBa 2 Cu 3 O 7−δ (YBCO) film, 10 mol% Sn-doped YBCO film exhibited significantly enhanced critical current densities (J c ) in magnetic fields up to 5 T at 65 and 77 K for H//c, indicating that the Sn-doped YBCO film possesses more effective flux pinning centers. Both samples were grown on the SrTiO 3 (STO) (1 0 0) single crystal substrates by the metal-organic deposition (MOD) process. Larger J c (77 K, 1 T) values of Sn-doped YBCO film are observed over a wide field-orientation angle (θ) except the field-orientations close to the ab-plane of YBCO (85° c values for 85° 2 SnO 5.5 (YBSO) phase by STEM (scanning transmission electron microscopy)-EDS (energy dispersive X-ray spectroscopy) analysis. Further analyses by HR-TEM (high resolution-transmission electron microscopy) revealed that YBSO nanoparticles completely surrounded by the YBCO matrix had random orientation with YBCO while those located at the interface of YBCO/STO substrate had epitaxial relationship with YBCO

  6. Growth of YBCO superconducting thin films on CaF sub 2 buffered silicon

    CERN Document Server

    Bhagwat, S S; Patil, J M; Shirodkar, V S

    2000-01-01

    CaF sub 2 films were grown on silicon using the neutral cluster beam deposition technique. These films were highly crystalline and c-axis oriented. Superconducting YBCO thin films were grown on the Ca F sub 2 buffered silicon using the laser ablation technique. These films showed T sub c (onset) at 90 K and Tc(zero) at 86 K. X-ray diffraction analysis showed that the YBCO films were also oriented along the c-axis.

  7. Nano-engineered pinning centres in YBCO superconducting films

    Energy Technology Data Exchange (ETDEWEB)

    Crisan, A., E-mail: adrian.crisan@infim.ro [National Institute for Materials Physics Bucharest, 105 bis Atomistilor Str., 077125 Magurele (Romania); School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Dang, V.S. [School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Nano and Energy Center, VNU Hanoi University of Science, 334 Nguyen Trai, Thanh Xuan, Hanoi (Viet Nam); Mikheenko, P. [School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Department of Physics, University of Oslo, P.O. Box 1048 Blindern, N-0316 Oslo (Norway)

    2017-02-15

    Highlights: • Power applications of YBCO films/coated conductors in technological relevant magnetic fields requires nano-engineered pinning centre. • Three approaches have been proposed: substrate decoration, quasi-multilayers, and targets with secondary phase nano-inclusions. • Combination of all three approaches greatly increased critical current in YBCO films. • Bulk pinning force, pinning potential, and critical current density are estimated and discussed in relation with the type and strength of pinning centres related to the defects evidenced by Transmission Electron Microscopy. - Abstract: For practical applications of superconducting materials in applied magnetic fields, artificial pinning centres in addition to natural ones are required to oppose the Lorentz force. These pinning centres are actually various types of defects in the superconductor matrix. The pinning centres can be categorised on their dimension (volume, surface or point) and on their character (normal cores or Δκ cores). Different samples have been produced by Pulsed Laser Deposition, with various thicknesses, temperatures and nanostructured additions to the superconducting matrix. They have been characterized by SQUID Magnetic Properties Measurement System and Physical Properties Measurement System, as well as by Transmission Electron Microscopy (TEM). Correlations between pinning architecture, TEM images, and critical currents at various fields and field orientations will be shown for a large number of YBa{sub 2}Cu{sub 3}O{sub x} films with various types and architectures of artificial pinning centres.

  8. Deposition studies and coordinated characterization of MOCVD YBCO films on IBAD-MgO templates

    International Nuclear Information System (INIS)

    Aytug, T; Paranthaman, M; Heatherly, L; Zuev, Y; Zhang, Y; Kim, K; Goyal, A; Maroni, V A; Chen, Y; Selvamanickam, V

    2009-01-01

    A recently installed research-scale metal-organic chemical vapor deposition (MOCVD) system at Oak Ridge National Laboratory, provided by SuperPower, Inc., has been used to investigate processing variables for MOCVD YBCO precursors and trends in the resulting properties. Systematic studies of YBCO film growth on LaMnO 3 /IBAD-MgO templates were carried out by optimizing deposition temperature and oxygen flow rate. Microstructural and superconducting properties of the YBCO films were analyzed by x-ray diffraction, scanning electron microscopy and transport measurements. The identification of intermediate phases formed during the YBCO precursor transformation was investigated by coordinated reel-to-reel Raman microprobe analysis. With this combination of various characterization techniques, an improved understanding of the growth characteristics of MOCVD YBCO films was established. Finally, critical current densities greater than 2 MA cm -2 for film thicknesses of 0.8 μm were demonstrated.

  9. Deposition studies and coordinated characterization of MOCVD YBCO films on IBAD-MgO templates

    Energy Technology Data Exchange (ETDEWEB)

    Aytug, T; Paranthaman, M [Oak Ridge National Laboratory, Chemical Sciences Division, Oak Ridge, TN 37831 (United States); Heatherly, L; Zuev, Y; Zhang, Y; Kim, K; Goyal, A [Oak Ridge National Laboratory, Materials Science and Technology Division, Oak Ridge, TN 37831 (United States); Maroni, V A [Argonne National Laboratory, Chemical Sciences and Engineering Division, Argonne, IL 60439 (United States); Chen, Y; Selvamanickam, V [SuperPower, Incorporated, 450 Duane Avenue, Schenectady, NY 12304 (United States)], E-mail: aytugt@ornl.gov

    2009-01-15

    A recently installed research-scale metal-organic chemical vapor deposition (MOCVD) system at Oak Ridge National Laboratory, provided by SuperPower, Inc., has been used to investigate processing variables for MOCVD YBCO precursors and trends in the resulting properties. Systematic studies of YBCO film growth on LaMnO{sub 3}/IBAD-MgO templates were carried out by optimizing deposition temperature and oxygen flow rate. Microstructural and superconducting properties of the YBCO films were analyzed by x-ray diffraction, scanning electron microscopy and transport measurements. The identification of intermediate phases formed during the YBCO precursor transformation was investigated by coordinated reel-to-reel Raman microprobe analysis. With this combination of various characterization techniques, an improved understanding of the growth characteristics of MOCVD YBCO films was established. Finally, critical current densities greater than 2 MA cm{sup -2} for film thicknesses of 0.8 {mu}m were demonstrated.

  10. Structure and oxygen incorporation in low pressure sputtered YBCO films

    International Nuclear Information System (INIS)

    Chaudhary, S.; Pandya, D. K.; Kashyap, S. C.

    2002-01-01

    Thin films of YBa 2 Cu 3 O 7- δ (YBCO) have been successfully grown by reactive RF-magnetron sputtering technique at low pressure. The oxygen partial pressure of 0.95 mTorr, a total pressure (argon and oxygen) of 1.9 mTorr, and a substrate temperature of 775 grad C resulted in good quality films with T C (R=0) = 85.3 K and J Cmag (4.2 K) ≅ 2x10 7 A/cm 2 . The incorporation of oxygen in the as-grown films has been controlled by using different ambient - oxygen, air or argon during in-situ cooling. The superconducting behaviour of the films was studied using resistance-temperature and low field ac-susceptibility measurements and correlated with their structure. All the films exhibited metallic conduction in the normal state. The oxygen- and air- cooled films were superconducting, possessing the usual orthorhombic structure. The argon-cooled films were non-superconducting possessing the tetragonal structure, thus implying that the structure of the film during deposition is tetragonal which transforms to either of the oxygen rich orthorhombic-I or -II phases depending upon the oxygen/air ambient. The 'δ' values of 0.14, 0.32 and 0.70 and higher 'c'-parameters of 1.1785, 1.180 and 1.183 nm have been obtained for oxygen, air and argon cooled films respectively. (Authors)

  11. Properties of second phase (BaSnO3, Sn) added-YBCO thick films

    International Nuclear Information System (INIS)

    Ban, E.; Matsuoka, Y.

    1997-01-01

    The improvement of the critical current density J c of YBCO thick films has been attempted by adding BaSnO 3 powder and ultrafine Sn particles, whose diameter is about 2 μm and 7 x 10 -2 μm, respectively. It was found that the addition of a small amount of these particles was effective for the enhancement of J c of thick films prepared by a liquid-phase processing method. The 1 wt.% BaSnO 3 films fired at T s =1040-1060 C and the 3 wt.% Sn films (T s =1030-1060 C) showed J c values (77 K, 0 T) of about 2.1-2.4 x 10 3 Acm -2 and 3.1-3.5 x 10 3 Acm -2 , respectively, as compared to 2.0 x 10 3 Acm -2 for the undoped films. (orig.)

  12. Greatly enhanced flux pinning properties of fluorine-free metal-organic decomposition YBCO films by co-addition of halogens (Cl, Br) and metals (Zr, Sn, Hf)

    Science.gov (United States)

    Motoki, Takanori; Ikeda, Shuhei; Nakamura, Shin-ichi; Honda, Genki; Nagaishi, Tatsuoki; Doi, Toshiya; Shimoyama, Jun-ichi

    2018-04-01

    Additive-free YBCO films, as well as those with halogen (X) added, metal (M) added and (X, M) co-added, have been prepared by the fluorine-free metal-organic decomposition method on SrTiO3(100) single crystalline substrates, where X = Cl, Br and M = Zr, Sn, Hf. It was revealed that the addition of both Cl and Br to the starting solution resulted in the generation of oxyhalide, Ba2Cu3O4 X 2, in the YBCO films, and that the oxyhalide was found to promote the bi-axial orientation of the YBCO crystals. By adding a decent amount of Cl or Br, highly textured YBCO films with high J c were reproducibly obtained, even when an impurity metal, M, was co-added, while the addition of M without X did not greatly improve J c owing to the poor bi-axial orientation of the YBCO crystals. Our results suggest that the addition of Br more effectively enhances J c than the addition of Cl. The pinning force density at 40 K in 4.8 T reached ˜55 GN m-3 with the co-addition of (Br, M). This value is much larger than that of the pure YBCO film, reaching ˜17 GN m-3.

  13. BaF2 POST-DEPOSITION REACTION PROCESS FOR THICK YBCO FILMS

    International Nuclear Information System (INIS)

    SUENAGA, M.; SOLOVYOV, V.F.; WU, L.; WIESMANN, H.J.; ZHU, Y.

    2001-01-01

    The basic processes of the so-called BaF 2 process for the formation of YBa 2 Cu 3 O 7 , YBCO, films as well as its advantages over the in situ formation processes are discussed in the previous chapter. The process and the properties of YBCO films by this process were also nicely described in earlier articles by R. Feenstra, (et al.) Here, we will discuss two pertinent subjects related to fabrication of technologically viable YBCO conductors using this process. These are (1) the growth of thick (>> 1 microm) c-axis-oriented YBCO films and (2) their growth rates. Before the detail discussions of these subjects are given, we first briefly discuss what geometrical structure a YBCO-coated conductor should be. Then, we will provide examples of simple arguments for how thick the YBCO films and how fast their growth rates need to be. Then, the discussions in the following two sections are devoted to: (1) the present understanding of the nucleation and the growth process for YBCO, and why it is so difficult to grow thick c-axis-oriented films (> 3 microm), and (2) our present understanding of the YBCO growth-limiting mechanism and methods to increase the growth rates. The values of critical-current densities J c in these films are of primary importance for the applications,. and the above two subjects are intimately related to the control of J c of the films. In general, the lower the temperatures of the YBCO formation are the higher the values of J c of the films. Thus, the present discussion is limited to those films which are reacted at ∼735 C. This is the lowest temperature at which c-axis-oriented YBCO films (1-3 microm thick) are comfortably grown. It is also well known that the non-c-axis oriented YBCO platelets are extremely detrimental to the values of J c such that their effects on J c dwarf essentially all of other microstructural effects which control J c . Hence, the discussion given below is mainly focused on how to avoid the growth of these crystallites

  14. Ag induced suppression of irradiation response in YBCO/Ag composite thin films

    International Nuclear Information System (INIS)

    Behera, D.; Mohanty, T.; Mohanta, D.; Patnaik, K.; Mishra, N.C.; Senapati, L.; Kanjilal, D.; Mehta, G.K.; Pinto, R.

    1999-01-01

    Practical application of cuprate superconductors in radiation environment demands that these systems remain insensitive to the irradiation induced defects. The cuprate superconductors however are many orders of magnitude more sensitive than the conventional low T c superconductors. To suppress the irradiation sensitivity of cuprates we consider a crystal engineering approach where metal ions as Ag is made to occupy inter and intra-granular sites of YBa 2 Cu 3 O 7 thin films. We show that superconducting and normal state properties of YBCO/Ag composite thin films prepared by laser ablation remain unchanged under 140 MeV Si ion irradiation up to fluence of 8 x 10 14 ions/cm 2 . The inter- and intra-granular occupancy of Ag is shown to induce microstructural modifications and rigidity to the CuO chains respectively which in turn lead to the radiation insensitivity of the composite films. (author)

  15. Effect of processing conditions and methods on residual stress in CeO2 buffer layers and YBCO superconducting films

    International Nuclear Information System (INIS)

    Xiong Jie; Qin Wenfeng; Cui Xumei; Tao Bowan; Tang Jinlong; Li Yanrong

    2006-01-01

    CeO 2 layers have been fabricated by pulsed laser deposition (PLD) technique on (1 1 0 2) sapphire substrate. Microstructure of CeO 2 layers is characterized by X-ray diffraction as functions of substrate temperature. The effects of the substrate temperature on the residual stress have been studied. The results show that residual stress in CeO 2 film decreased with increasing substrate temperature, not the same development tendency as that of thermal stress. This means that the thermal stress is only a fraction of the residual stress. Moreover, YBCO superconducting films were prepared by direct current (DC) sputtering and pulsed laser deposition (PLD) technique. The residual stress and thermal stress of both YBCO films were measured. PLD processing apparently generated higher intrinsic compressive stresses in comparison to DC sputtering

  16. Quick screening for new flux pinning materials in YBCO films with the combinatorial-PLD method

    International Nuclear Information System (INIS)

    Yoshimura, T.; Ichino, Y.; Yoshida, Y.; Takai, Y.; Kita, R.; Suzuki, K.; Takeuchi, T.

    2011-01-01

    An effective way to improve the superconducting properties in REBa 2 Cu 3 O y (REBCO) films under a magnetic field is to dope artificial pinning centers (APC). The pinning performance depends on the content of the APC materials. Usually, the optimal APC content is explored by preparing films one at a time from the REBCO target using different APC material content, which is an extremely time-consuming process. The combinatorial-PLD (C-PLD) method allowed us to prepare films that continuously changed in composition across a single substrate. In this study, we used the C-PLD method to prepare BaSnO 3 (BSO)-doped YBCO films. The films were deposited on SrTiO 3 substrate using a fourth-harmonic Nd:YAG laser. From the results of the J c -B curves at 77 K and B//c, the film that contained 3.2 vol.% of BSO exhibited the best pinning performance in this study. We showed that the C-PLD method was efficient for quick screening of the optimal APC content with only one deposition. We also used the C-PLD method to explore new APC materials, and proved that it can quickly evaluate the new APC materials Ba 3 Cu 3 In 4 O 12 and BaTbO 3 .

  17. The effect of a thin silver layer on the critical current of epitaxial YBCO films

    International Nuclear Information System (INIS)

    Polturak, E.; Koren, G.; Cohen, D.; Cohen, D.; Snapiro, I.

    1992-01-01

    We compare measurements of the critical current density of an epitaxial YBCO film with that of an identical film overlaid by a thin silver layer. We find that the presence of the silver lowers Tc of the film by about 1.5 K, which is two orders of magnitude larger than predicted by the theory of the proximity effect for our experimental conditions. In addition, J c of the Ag/YBCO film near Tc is also significantly lower than that of the bare YBCO film. We propose two alternate interpretations of this effect, one in terms of destabilization of the flux distribution in the film and the other making use of the effect of the silver on the Bean-Livingston surface barrier for the initial penetration of flux. The latter seems the more plausible explanation of our results. (orig.)

  18. Low energy electron beam processing of YBCO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Chromik, Š., E-mail: stefan.chromik@savba.sk [Institute of Electrical Engineering, SAS, Dúbravská cesta 9, 841 04 Bratislava (Slovakia); Camerlingo, C. [CNR-SPIN, Istituto Superconduttori, Materiali Innovativi e Dispositivi, via Campi Flegrei 34, 80078 Pozzuoli (Italy); Sojková, M.; Štrbík, V.; Talacko, M. [Institute of Electrical Engineering, SAS, Dúbravská cesta 9, 841 04 Bratislava (Slovakia); Malka, I.; Bar, I.; Bareli, G. [Department of Physics, Ben Gurion University of the Negev, P.O.B. 653, 84105 Beer Sheva (Israel); Jung, G. [Department of Physics, Ben Gurion University of the Negev, P.O.B. 653, 84105 Beer Sheva (Israel); Institute of Physics, Polish Academy of Sciences, Al. Lotników 32/46, 02-668 Warsaw (Poland)

    2017-02-15

    Highlights: • Improvement of superconducting properties of irradiated bridges under certain conditions. • 30 keV irradiation influence CuO{sub 2} planes as well as oxygen chains. • Direct confirmation of changes in oxygen chains using micro-Raman spectroscopy. • Possibility of electron writing. - Abstract: Effects of low energy 30 keV electron irradiation of superconducting YBa{sub 2}Cu{sub 3}O{sub 7−δ} thin films have been investigated by means of transport and micro-Raman spectroscopy measurements. The critical temperature and the critical current of 200 nm thick films initially increase with increasing fluency of the electron irradiation, reach the maximum at fluency 3 − 4 × 10{sup 20} electrons/cm{sup 2}, and then decrease with further fluency increase. In much thinner films (75 nm), the critical temperature increases while the critical current decreases after low energy electron irradiation with fluencies below 10{sup 20} electrons/cm{sup 2}. The Raman investigations suggest that critical temperature increase in irradiated films is due to healing of broken Cu−O chains that results in increased carrier’s concentration in superconducting CuO{sub 2} planes. Changes in the critical current are controlled by changes in the density of oxygen vacancies acting as effective pinning centers for flux vortices. The effects of low energy electron irradiation of YBCO turned out to result from a subtle balance of many processes involving oxygen removal, both by thermal activation and kick-off processes, and ordering of chains environment by incident electrons.

  19. Effect of argon addition into oxygen atmosphere on YBCO thin films deposition

    International Nuclear Information System (INIS)

    Mozhaev, P. B.; Borisenko, I. V.; Ovsyannikov, G. A.; Kuehle, A.; Bindslev-Hansen, J.; Johannes, L.; Skov, J. L.

    2002-01-01

    Multicomponent nature of the YBa 2 Cu 3 O x (YBCO) high-temperature superconductor makes difficult fabrication of smooth thin films: every local deviation from stoichiometry can result in seeding of a non-superconducting oxide particle. High density of such particles on typical YBCO thin film surface, however, presumes overall non-stoichiometry of the film. Such an effect can result from (i) non-uniform material transport from target to substrate, and (ii) re-evaporation or re-sputtering from the growing film surface. The first reason is more usual for laser ablation deposition technique, the second is typical for long sputtering deposition processes. Substitution of oxygen with argon in the deposition atmosphere improves surface quality of YBCO thin films deposited both by laser ablation and DC-sputtering at high pressure techniques. In the first case, the ablated species are scattered different ways in the oxygen atmosphere. Addition of argon decreases the inelastic scattering of barium; the proper part of Ar in the deposition atmosphere makes scattering and, hence, transport of all atoms uniform. The YBCO films deposited by DC-sputtering at high pressure technique are Ba-deficient also, but the reason is re-sputtering of Ba from the growing film as a result of negative oxygen ions bombardment. Such bombardment can lead also to chemical interaction of the deposited material with the substrate, as in the case of deposition of YBCO thin film on the CeO 2 buffer layer on sapphire. Substitution of oxygen with argon not only suppresses ion bombardment of the film, but also increases discharge stability due to presence of positive Ar + ions. The limiting factor of argon substitution is sufficient oxygenation of the growing oxide film. When oxygen partial pressure is too small, the superconducting quality of the YBCO thin film decreases and such a decrease cannot be overcome by prolonged oxygenation after deposition. (Authors)

  20. In-situ deposition of YBCO high-Tc superconducting thin films by MOCVD and PE-MOCVD

    International Nuclear Information System (INIS)

    Zhao, J.; Noh, D.W.; Chern, C.; Li, Y.Q.; Norris, P.E.; Kear, B.; Gallois, B.

    1991-01-01

    Metal-Organic Chemical Vapor Deposition (MOCVD) offers the advantages of a high degree of compositional control, adaptability for large scale production, and the potential for low temperature fabrication. The capability of operating at high oxygen partial pressure is particularly suitable for in situ formation of high temperature superconducting (HTSC) films. Yttrium barium copper oxide (YBCO) thin films having a sharp zero-resistance transition with T(sub c) greater than 90 K and J(sub c) of approximately 10(exp 4) A on YSZ have been prepared, in situ, at a substrate temperature of about 800 C. Moreover, the ability to form oxide films at low temperature is very desirable for device applications of HTSC materials. Such a process would permit the deposition of high quality HTSC films with a smooth surface on a variety of substrates. Highly c-axis oriented, dense, scratch resistant, superconducting YBCO thin films with mirror-like surfaces have been prepared, in situ, at a reduced substrate temperature as low as 570 C by a remote microwave-plasma enhanced metal-organic chemical vapor deposition (PE-MOCVD) process. Nitrous oxide was used as a reactant gas to generate active oxidizing species. This process, for the first time, allows the formation of YBCO thin films with the orthorhombic superconducting phase in the as-deposited state. The as-deposited films grown by PE-MOCVD show attainment of zero resistance at 72 K with a transition width of about 5 K. MOCVD was carried out in a commercial production scale reactor with the capability of uniform deposition over 100 sq cm per growth run. Preliminary results indicate that PE-MOCVD is a very attractive thin film deposition process for superconducting device technology

  1. Intermediate Phase Study on YBCO Films Coated by Precursor Solutions With F/Ba Atomic Ratio of 2

    DEFF Research Database (Denmark)

    Wu, W.; Feng, F.; Zhao, Y.

    2016-01-01

    In the chemical solution deposition process of YBCO superconducting films, fluorine is widely regarded to be of significant importance in avoiding the formation of BaCO3, which hinders the growth of high-quality YBCO films. On the other hand, great efforts have been made to decrease the fluorine......) could be routinely obtained on lanthanum aluminate single-crystal substrates....

  2. Pulsed laser deposition of YBCO films on ISD MgO buffered metal tapes

    CERN Document Server

    Ma, B; Koritala, R E; Fisher, B L; Markowitz, A R; Erck, R A; Baurceanu, R; Dorris, S E; Miller, D J; Balachandran, U

    2003-01-01

    Biaxially textured magnesium oxide (MgO) films deposited by inclined-substrate deposition (ISD) are desirable for rapid production of high-quality template layers for YBCO-coated conductors. High-quality YBCO films were grown on ISD MgO buffered metallic substrates by pulsed laser deposition (PLD). Columnar grains with a roof-tile surface structure were observed in the ISD MgO films. X-ray pole figure analysis revealed that the (002) planes of the ISD MgO films are tilted at an angle from the substrate normal. A small full-width at half maximum (FWHM) of approx 9deg was observed in the phi-scan for ISD MgO films deposited at an inclination angle of 55deg . In-plane texture in the ISD MgO films developed in the first approx 0.5 mu m from the substrate surface, and then stabilized with further increases in film thickness. Yttria-stabilized zirconia and ceria buffer layers were deposited on the ISD MgO grown on metallic substrates prior to the deposition of YBCO by PLD. YBCO films with the c-axis parallel to the...

  3. Formation and physical properties of YBCO thick films grown by using the electrophoretic deposition method

    CERN Document Server

    Kim, U J; Kim, Y C; Han, S K; Kang, K Y

    1999-01-01

    Thick films of the YBa sub 2 Cu sub 3 O subgamma sub - subdelta (YBCO) superconductor were prepared by using the electrophoretic deposition technique and a flexible wire as the substrate. The transition temperature of the wires was 91 K, the intragranular magnetic critical current density J sub c sub g sup m sup a sup g was about 10 sup 5 A/cm sup 2 at 77 K in a weak field, and the transport J sub c sup t sup r sup a sup n sup s was about 365 A/cm sup 2 at 77 K. We calculated the intergranular magnetic critical current J sub c sub J sup m sup a sup g and the activation energy from the AC-susceptibility measurements, and their values were about 444 A/cm sup 2 at 77 K and 2.02 eV, respectively.

  4. An all-field-range description of the critical current density in superconducting YBCO films

    International Nuclear Information System (INIS)

    Golovchanskiy, I A; Pan, A V; Shcherbakova, O V; Fedoseev, S A; Dou, S X

    2011-01-01

    A new critical current density (J c ) model for high-quality YBCO (YBa 2 Cu 3 O 7 ) thin films has been proposed, combining thermally activated flux creep with a vortex pinning potential for columnar defects. The pinning for thermally activated vortices has been described as strong pinning on chains of individual edge dislocations that form low-angle domain boundaries in high-quality YBCO thin films. The model yields an adequate description of the J c behaviour over the whole applied field range, as verified by direct measurements of J c in YBCO thin films grown by pulsed-laser deposition. It also indicates that the effective pinning landscape changes under the influence of the external conditions. Remarkably, the pinning potential obtained from the model is consistent with the values obtained for columnar defects, which confirms the validity of the overall approach.

  5. Mechanical characterization of YBCO thin films using nanoindentation and finite element method

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Weixing [The Ministry of Education of China (China). Key Lab. of Mechanics on Environment and Disaster in Western China; Lanzhou Univ. (China). College of Civil Engineering and Mechanics

    2017-09-15

    The mechanical properties of YBCO thin film deposited on SrTiO{sub 3} (100) substrates by magnetron sputtering were determined using Berkovich nanoindentation and scanning electron microscopy. Hardness and elastic modulus were determined via the Oliver-Pharr method from indentation load-depth curves. The hardness values of the YBCO thin film show depth dependence, i. e., indentation size effect, which arose from the surface roughness as detected by scanning electron microscopy. Multiple pop-in events were observed on the loading curves, however, no obvious pop-out takes place during the elastic recovery. In addition, an effective analytical method accommodating the indenter imperfection was proposed and validated against experimental data in terms of elastic modulus, yield stress and friction angle using the Drucker-Prager yield criterion for the YBCO thin film.

  6. Resistive switching phenomenon and hole wind effect in YBCO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Truchly, Martin; Plecenik, Tomas [Department of Experimental Physics, Comenius University, Bratislava (Slovakia); Zhitlukhina, Elena [Donetsk Institute for Physics and Engineering, Kyiv (Ukraine)

    2016-07-01

    We present an overview of our experimental and theoretical activities aimed to clarify the mechanism of resistive memory effects in YBCO thin layers. The phenomenon was studied by scanning spreading resistance microscopy (SSRM) and scanning tunneling microscopy (STM) techniques. The most striking feature uncovered (in contrast to previous experiments on planar bilayers with YBCO films) was the opposite voltage-bias polarity of the switching effect in all SSRM and a number of STM measurements. Observed hysteresis in current-voltage characteristics is interpreted as a movement of oxygen vacancies in the vicinity of the tip-YBCO contact. Since the charge distribution in YBCO samples is expected to be strongly inhomogeneous, the balance between the direct electrostatic force on activated oxygen ions and that caused by momentum exchange with the current carriers (holes) hitting them determines direction in which the oxygen vacancies are moving. We propose a minimalist model with the only fitting parameter that accounts for the resistance hysteresis phenomenon in the YBCO films studied.

  7. Influence of interface reactions on the YBCO films grown by fluorine-free solution route

    DEFF Research Database (Denmark)

    Zhao, Yue; Wu, Wei; Tang, Xiao

    2015-01-01

    Fabrication of full-stacked coated conductors by all-chemical-solution routes exhibit a great potential in view of further reducing the cost and increasing the throughput for industrialization. Growth of YBa2Cu3O7−x (YBCO) superconducting films by fluorine-free metal organic deposition routes (FF......-MOD) which are environmental friendly has attracted more attentions recently. In this work, comparison study was performed on the YBCO-Ag superconducting thin films deposited on two types of single crystal substrates, LaAlO3 and Ce0.9La0.9O2−y/YSZ. The structural characterization and superconducting...... properties studies reveal that the interface reactions between the YBCO-Ag film and the CLO cap layer play an essential role on the nucleation and growth of YBCO-Ag films from the FF solution. Weak texture caused by serious interface reactions at high growth temperature is the main explanations for the poor...

  8. Pulsed-laser-deposited YBCO thin films using modified MTG processed targets

    CERN Document Server

    Kim, C H; Kim, I T; Hahn, T S

    1999-01-01

    YBCO thin films were deposited by pulsed laser deposition from targets fabricated using the modified melt-textured growth (MTG) method and the solid-state sintering (SSS) method. All of the films showed c-axis orientations, but the films from the MTG targets had better crystallinity than those from the SSS targets. As the substrate temperature was increased, T sub c and J sub c of the films increased. The films from the MTG targets showed better superconducting properties than those from the SSS targets. From the composition analysis of the targets, the Y-richer vapor species arriving at the substrate from the MTG targets are thought to form a thermodynamically more stable YBCO phase with less cation disorder.

  9. Bi axially textured YBCO coated tape prepared using dynamic magnetic grain alignment

    International Nuclear Information System (INIS)

    Genoud, Jean-Yves; Quinton, William

    1999-01-01

    A new magnetic grain alignment technique has been applied to produce bi axially aligned YBCO coated tapes. A bi axially aligned dispersion of orthorhombic Y 2 Ba 4 Cu 7 O 15 (Y-247) powder was settled on un textured silver substrates. The Y-247 tapes were then melt processed to achieve high critical current YBa 2 Cu 3 O 7 (Y-123) tapes with CuO as a secondary phase. The biaxial alignment is preserved after the densification process and a clear enhancement of J c relative to identically prepared un textured or uniaxially textured samples is obtained. Critical current densities of up to 5000 A cm -2 at 77 K in self-field and 1500 A cm -2 in 0.5 T magnetic field at 65 K were obtained in films from 20 to 40 μm thick. Problems were experienced in achieving fully densified thick films while retaining biaxial texture. The initial grain size distribution was found to have a major influence on the final microstructure. Provided significant improvements in J c can be obtained this method offers an alternative to coated tape processes based on epitaxial growth which has the advantage that it does not require textured substrates. The biaxial alignment technique described here intrinsically acts on the bulk material rather than at surfaces. This offers the possibility of texturing without thickness limitations. (author)

  10. Plasma-enhanced chemical vapor deposition for YBCO film fabrication of superconducting fault-current limiter

    Energy Technology Data Exchange (ETDEWEB)

    Jun, Byung Hyuk; Kim, Chan Joong

    2006-05-15

    Since the high-temperature superconductor of oxide type was founded, many researches and efforts have been performed for finding its application field. The YBCO superconducting film fabricated on economic metal substrate with uniform critical current density is considered as superconducting fault-current limiter (SFCL). There are physical and chemical processes to fabricate superconductor film, and it is understood that the chemical methods are more economic to deposit large area. Among them, chemical vapor deposition (CVD) is a promising deposition method in obtaining film uniformity. To solve the problems due to the high deposition temperature of thermal CVD, plasma-enhanced chemical vapor deposition (PECVD) is suggested. This report describes the principle and fabrication trend of SFCL, example of YBCO film deposition by PECVD method, and principle of plasma deposition.

  11. Preparing superconducting nanopowder based YBCO/Ag tapes

    DEFF Research Database (Denmark)

    Paturi, P.; Raittila, J.; Grivel, J.C.

    2002-01-01

    YBCO nanopowder consisting of 1-3 nm thick and 40 nm wide particles has been used to make silver clad superconducting tapes. After annealing in nitrogen at 945 degreesC for 10 h a critical current of 5.02 A (3300 A/cm(2)) was attained, Annealing in mixed atmosphere of oxygen and nitrogen was also...... carried out and this procedure produced tapes with a critical current of 2.83 A (2200 A/cm(2)). These tapes show very good characteristics in magnetic fields. (C) 2002 Elsevier Science B.V. All rights reserved....

  12. Evaluation on current-limiting performance of the YBCO thin-film wire considering electric coupling condition

    International Nuclear Information System (INIS)

    Du, H.-I.; Han, B.-S.; Kim, Y.-J.; Lee, D.-H.; Song, S.-S.; Han, T.-H.; Han, S.-C.

    2011-01-01

    The basic way to improve the performance of a superconducting current limiter is to apply and evaluate a superconducting device that is appropriate to the superconducting current limiter. Among the many types of superconducting devices, the YBCO thin film wire has excellent current-limiting performance that is appropriate for actual system application. For the application of the YBCO thin film wire to superconducting current limiters, its current-limiting performance as a unit device must be accurately evaluated, and measures to improve its current-limiting performance must be sought. Accordingly, to evaluate the current-limiting performance of the YBCO thin film wire, this study was conducted to evaluate its resistance-increasing trend, V max , T r , I max , I qt , and current-limiting rate as a unit device, after which the electric coupling condition that consists of a core and windings was used to evaluate the current-limiting performance of the YBCO thin film wire.

  13. Enhanced flux pinning in MOCVD-YBCO films through Zr additions : systematic feasibility studies.

    Energy Technology Data Exchange (ETDEWEB)

    Aytug, T.; Paranthaman, M.; Specht, E. D.; Zhang, Y.; Kim, K.; Zuev, Y. L.; Cantoni, C.; Goyal, A.; Christen, D. K.; Maroni, V. A.; Chen, Y.; Selvamanickam, V.; ORNL; SuperPower, Inc.

    2010-01-01

    Systematic effects of Zr additions on the structural and flux pinning properties of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) films deposited by metal-organic chemical vapor deposition (MOCVD) have been investigated. Detailed characterization, conducted by coordinated transport, x-ray diffraction, scanning and transmission electron microscopy analyses, and imaging Raman microscopy have revealed trends in the resulting property/performance correlations of these films with respect to varying mole percentages (mol%) of added Zr. For compositions {le} 7.5 mol%, Zr additions lead to improved in-field critical current density, as well as extra correlated pinning along the c-axis direction of the YBCO films via the formation of columnar, self-assembled stacks of BaZrO{sub 3} nanodots.

  14. Enhanced flux pinning in MOCVD-YBCO films through Zr additions: systematic feasibility studies

    International Nuclear Information System (INIS)

    Aytug, T; Paranthaman, M; Specht, E D; Zhang, Y; Kim, K; Zuev, Y L; Cantoni, C; Goyal, A; Christen, D K; Maroni, V A; Chen, Y; Selvamanickam, V

    2010-01-01

    Systematic effects of Zr additions on the structural and flux pinning properties of YBa 2 Cu 3 O 7-δ (YBCO) films deposited by metal-organic chemical vapor deposition (MOCVD) have been investigated. Detailed characterization, conducted by coordinated transport, x-ray diffraction, scanning and transmission electron microscopy analyses, and imaging Raman microscopy have revealed trends in the resulting property/performance correlations of these films with respect to varying mole percentages (mol%) of added Zr. For compositions ≤7.5 mol%, Zr additions lead to improved in-field critical current density, as well as extra correlated pinning along the c-axis direction of the YBCO films via the formation of columnar, self-assembled stacks of BaZrO 3 nanodots.

  15. Enhanced flux pinning in MOCVD-YBCO films through Zr additions: systematic feasibility studies

    Energy Technology Data Exchange (ETDEWEB)

    Aytug, T; Paranthaman, M; Specht, E D; Zhang, Y; Kim, K; Zuev, Y L; Cantoni, C; Goyal, A; Christen, D K [Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States); Maroni, V A [Argonne National Laboratory, Argonne, IL 60439 (United States); Chen, Y; Selvamanickam, V, E-mail: aytugt@ornl.go [SuperPower, Incorporated, 450 Duane Avenue, Schenectady, NY 12304 (United States)

    2010-01-15

    Systematic effects of Zr additions on the structural and flux pinning properties of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) films deposited by metal-organic chemical vapor deposition (MOCVD) have been investigated. Detailed characterization, conducted by coordinated transport, x-ray diffraction, scanning and transmission electron microscopy analyses, and imaging Raman microscopy have revealed trends in the resulting property/performance correlations of these films with respect to varying mole percentages (mol%) of added Zr. For compositions {<=}7.5 mol%, Zr additions lead to improved in-field critical current density, as well as extra correlated pinning along the c-axis direction of the YBCO films via the formation of columnar, self-assembled stacks of BaZrO{sub 3} nanodots.

  16. Intermediate phase evolution in YBCO thin films grown by the TFA process

    International Nuclear Information System (INIS)

    Zalamova, K; Pomar, A; Palau, A; Puig, T; Obradors, X

    2010-01-01

    The YBCO thin film growth process from TFA precursors involves a complex reaction path which includes several oxide, fluoride and oxyfluoride intermediate phases, and the final microstructure and properties of the films are strongly influenced by the morphological and chemical evolution of these intermediate phases. In this work we present a study of the evolution of the intermediate phases involved in the TFA YBCO growth process under normal pressure conditions and we show that the oxygen partial pressure during pyrolysis of the TFA precursors is an important parameter. The Cu phase after the TFA pyrolysis can be either CuO, Cu 2 O or a mixture of both as the oxygen partial pressure is modified. The kinetics evolution of the intermediate phases has been determined for films pyrolysed in oxygen and nitrogen atmospheres and it is concluded that non-equilibrium phase transformations influence the reaction path towards epitaxial YBCO films and its microstructure. The intermediate phase evolution in these two series of films is summarized in kinetic phase diagrams.

  17. Dependence of critical current density on crystalline direction in thin YBCO films

    DEFF Research Database (Denmark)

    Paturi, P.; Peurla, M.; Raittila, J.

    2005-01-01

    The dependence of critical current density (J(c)) on the angle between the current direction and the (100) direction in the ab-plane of thin YBCO films deposited on (001)-SrTiO3 from natiocrystalline and microcrystalline targets is studied using magneto-optical microscopy. In the films made from...... the nanocrystalline target it is found that J(c) does not depend on the angle whereas J(c) decreases with increasing angle in the films made from the microcrystalline target. The films were characterized by detailed X-ray diffraction measurements. The findings are explained in terms of a network of planar defects...

  18. Preparation of Superconductor YBCO-123/Ag Composite Through Urea Molten Salt

    International Nuclear Information System (INIS)

    Yustinus, P.; Indra-Gunawan; Wuryanto

    1996-01-01

    Superconductor YBCO-123/Ag composite has been prepared through Urea molten salt by mixing salt nitrate of Yttrium, Barium, Copper and Silver. The weight of Silver content varied from 0 % - 50 %. After pyrolysis process the powder was subjected to calcination at 300, 500 and 700 o C subsequently for 1 hour. The calcined powders was pelletized into a disk of 1.0 cm in diameter and thickness of 2-3 mm. Sintering of pellet samples was done at 900 o C for 16 hours. Meissner effect on all samples displayed superconductivity phenomena. Samples were examined by XRD, SEM, measurement of critical temperature by using susceptibility magnet vs temperature, and critical current density measurement by using four point probe. Based on orthorhombic structure of YBCO-123 the result of the lattice crystal calculation were is a = 3.8167 - 3.8241 A o ; b = 3.8561 - 3.8895 A o and c = 11.6518 - 11.7104 A o , this showed that silver did not influence the structure of YBCO. Superconductor YBCO-123/Ag composite was prepared. This was proved by critical current density. Jc data which showed increased with increasing of silver content and the highest result was 9.71 x 10 5 Amp/m 2

  19. Response of thick-film bridge junction of high-Tc YBCO to nuclear radiation

    International Nuclear Information System (INIS)

    Ding Honglin; Wang Jun; Zhang Wanchang

    1992-01-01

    The response of thick-film Josephson junction based on high-T c YBCO to nuclear radiation is described. The lengths of the junction are 2000 μm, 1000 μm, and 500 μm and the widths are 500 μm, 300 μm and 100 μm. When the junction is irradiated by low energy γ-ray of 59.5 KeV from 241 Am at temperature of 77 K and the transport current I b is more than I c , the authors obtained the reduction of 1.6 mA of critical current and volt-signal as high as 17 μV without amplifier. It has been noted that the signal amplitude is related to the distance between the junction and the radiation source. Finally the advantages and shortcomings of detector based on thick films of high T c YBCO are discussed in the paper

  20. The mechanism of sputter-induced orientation change in YBCO films on MgO (001)

    International Nuclear Information System (INIS)

    Huang, Y.; Vuchic, B.V.; Baldo, P.; Merkle, K.L.; Buchholz, D.B.; Mahajan, S.; Lei, J.S.; Markworth, P.R.; Chang, R.P.H.

    1996-12-01

    The mechanisms of the sputter-induced orientation change in YBa 2 Cu 3 O 7-x (YBCO) films grown on MgO (001) substrates by pulsed organometallic beam epitaxy (POMBE) are investigated by x-ray diffraction. Rutherford backscatter spectroscopy (RBS), cross-section TEM (XTEM) and microanalysis. It is found that the W atom implantation concurring with the ion sputtering plays an important role in effecting the orientation change. This implantation changes the surface structure of the substrate and induces an intermediate layer in the initial growth of the YBCO film, which in turn acts as a template that induces the orientation change. It seems that the surface morphology change caused by ion sputtering has only a minor effect on the orientation change

  1. Flux flow and flux creep in thick films of YBCO. [Y-Ba-Cu-O

    Energy Technology Data Exchange (ETDEWEB)

    Rickets, J.; Vinen, W.F.; Abell, J.S.; Shields, T.C. (Superconductivity Research Group, Univ. of Birmingham (United Kingdom))

    1991-12-01

    The results are described of new experiments designed to study flux creep and flux flow along a single flux percolation path in thick films of YBCO. The flux flow regime is studied by a four-point resistive technique using pulsed currents, and the flux creep regime by observing the rate at which flux enters a superconducting loop in parallel with the resistance that is associated with the flux percolation path. (orig.).

  2. Magnetoresistivity and Hall resistivity of a YBCO thin film in a tilted magnetic field

    International Nuclear Information System (INIS)

    Amirfeiz, M.; Cimberle, M. R.; Ferdeghini, C.; Giannini, E.; Grassano, G.; Marre', D.; Putti, M.; Siri, A. S.

    1997-01-01

    In this paper they present magnetoresistivity and Hall effect measurements performed on a YBCO epitaxial film as a function of the angle θ between the external magnetic field and the a-b planes. The resistivity and Hall effect measurements are analyzed in term of the general scaling approach proposed by Blatter and coworkers; the Hall conductivity data are examined to separate the contributions due to vortices and quasi particles

  3. Characteristics of the electrical response of YBCO films with different morphologies to optical irradiation

    International Nuclear Information System (INIS)

    Frack, E.K.; Madhavrao, L.; Patl, R.; Drake, R.E.; Radparvar, M.

    1991-01-01

    The authors have fabricated YBCO films of varying thicknesses (300 Angstrom - 3000 Angstrom) and morphologies, and measured their electrical response to optical radiation. This paper reports on these measurements, emphasizing the dependence on temperature, light chopping frequency, and cryogenic environment. The temperature dependence of the film resistance is determined in part by the film morphology. This morphology may be represented by a simple model consisting of a two-dimensional array of coupled grains. The magnitude of the bolometric response correlates as expected with the sharpness of the superconducting transition. The increased response observed at lower temperatures (non-equilibrium) correlates with the temperature dependence of the resistance above the transition

  4. Quench and recovery characteristics of Au/YBCO thin film type SFCL

    International Nuclear Information System (INIS)

    Yim, S.-W.; Kim, H.-R.; Hyun, O.-B.; Sim, J.

    2007-01-01

    Although, a superconducting fault current limiter (SFCL) guarantees the fast limiting operation, it usually needs a considerably long time to recover to superconducting state after the quench. Considering the reclosing time in the protection coordination of power systems, the time required for the recovery should be investigated clearly. In this study, the quench and recovery characteristics of Au/YBCO thin films designed as an SFCL element with a bi-spiral pattern were investigated. The quench development of the SFCL was measured by two kinds of methods. Firstly, after applying the fault current of 5.5 cycles, we measured the resistance of the YBCO by a small current flowing through the pattern of Au/YBCO thin film. The temperature variation above the critical temperature, 85 K, was investigated indirectly from the resistance variation. Secondly, in order to measure the temperature from 85 K to 77 K, a meander line shape of Au thin film was evaporated on the back side and used as a temperature detecting sensor. The temperature variations detected by both methods were compared and analyzed. For the investigation of the recovery characteristics, the required time for the recovery of the superconductivity was measured for various magnitude and duration of the applied voltages. In addition, for the purpose of examining the dependence of the line impedance on the recovery time, resistors of various resistances were inserted in the fault current testing circuit and the recovery time was measured and analyzed

  5. State of the art and prospective of large scale applications of YBCO thick films grown on metallic substrates

    International Nuclear Information System (INIS)

    Boffa, Vincenzo

    1997-09-01

    In the framework of the high temperature superconducting materials, YBa 2 Cu 3 O 7 (YBCO) shows very interesting intrinsic superconducting transport properties at temperature higher than the liquid nitrogen temperature. These properties are very important in large scale applications: transport of energy, magnets, transformers, etc. Unfortunately the potential of this material cannot be achieved today, since it is very difficult to manufacture YBCO based tapes or cables. In the last years several groups have tried to overcome the problems with new fabrication techniques. In the present report the state of the art and the prospective in the field of YBCO film fabrication on metallic substrates are presented

  6. Study of microstructure and electrical properties of bulk YBCO prepared by melt textured growth technique

    International Nuclear Information System (INIS)

    Gonal, M. R.; Krishnan, Madangopal; Tewari, R.; Tyagi, A. K.; Gyore, A.; Vajda, I.

    2015-01-01

    Bulk YBCO components were prepared using Melt Texture Growth (MTG) technique. Components were fabricated using MTG by addition of Y 2 BaCuO 5 (Y211) and Ag to YBCO, which leads to improved grain size without affecting superconducting properties. Green compacts prepared by cold isostatic pressing were pre-sintered at 930°C before subjecting melt texturing. Cooling rates lower than 1 °C.h −1 was used, in between (peritectic) temperature of about 995 and 1025°C, to obtain large grained components. Microstructure studies in details were carried out by Scanning Electron Microscope (SEM), Electron Probe Micro Analysis (EPMA), Orientation Imaging Microscope (OIM) and TEM correlated with electrical properties like Critical current density (J c )

  7. Correlating properties and microstructure of YBCO thin films by magnetic X-ray microscopy

    Energy Technology Data Exchange (ETDEWEB)

    Ruoss, Stephen; Stahl, Claudia; Weigand, Markus; Schuetz, Gisela [Max-Planck-Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Zahn, Patrick; Bayer, Jonas [Max-Planck-Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Research Institute for Innovative Surfaces, FINO, Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany); Albrecht, Joachim [Research Institute for Innovative Surfaces, FINO, Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany)

    2016-07-01

    The magnetic flux distribution in high-temperature superconductors namely YBCO has been observed using a novel high-resolution technique based on the X-ray magnetic circular dichroism (XMCD). Therefore, a CoFeB layer is deposited on the superconductor which exhibits a strong XMCD-effect. X-ray absorption measurements with circular polarized radiation allows the analysis of the magnetic flux distribution in the superconductor via the soft-magnetic sensor layer [3,4]. In the total electron yield (TEY) mode of the scanning X-ray microscope (SXM) the surface structure and the magnetic domains can be imaged at the same time. Having obtained such high resolution images, the correlation of magnetic flux penetration and defect structure of YBCO thin films can be analyzed. The measurements have been performed at the scanning X-ray microscope MAXYMUS at Bessy II, HZB Berlin.

  8. Influence of artificial pinning centers on structural and superconducting properties of thick YBCO films on ABAD-YSZ templates

    Science.gov (United States)

    Pahlke, Patrick; Sieger, Max; Ottolinger, Rick; Lao, Mayraluna; Eisterer, Michael; Meledin, Alexander; Van Tendeloo, Gustaaf; Hänisch, Jens; Holzapfel, Bernhard; Schultz, Ludwig; Nielsch, Kornelius; Hühne, Ruben

    2018-04-01

    Recent efforts in the development of YBa2Cu3O7-x (YBCO) coated conductors are devoted to the increase of the critical current I c in magnetic fields. This is typically realized by growing thicker YBCO layers as well as by the incorporation of artificial pinning centers. We studied the growth of doped YBCO layers with a thickness of up to 7 μm using pulsed laser deposition with a growth rate of about 1.2 nm s-1. Industrially fabricated ion-beam textured YSZ templates based on metal tapes were used as substrates for this study. The incorporation of BaHfO3 (BHO) or Ba2Y(Nb0.5Ta0.5)O6 (BYNTO) secondary phase additions leads to a denser microstructure compared to undoped films. A purely c-axis-oriented YBCO growth is preserved up to a thickness of about 4 μm, whereas misoriented texture components were observed in thicker films. The critical temperature is slightly reduced compared to undoped films and independent of film thickness. The critical current density J c of the BHO- and BYNTO-doped YBCO layers is lower at 77 K and self-field compared to pure YBCO layers; however, I c increases up to a thickness of 5 μm. A comparison between films with a thickness of 1.3 μm revealed that the anisotropy of the critical current density J c(θ) strongly depends on the incorporated pinning centers. Whereas BHO nanorods lead to a strong B∣∣c-axis peak, the overall anisotropy is significantly reduced by the incorporation of BYNTO forming a mixture of short c-axis-oriented nanorods and small (a-b)-oriented platelets. As a result, the J c values of the doped films outperform the undoped samples at higher fields and lower temperatures for most magnetic field directions.

  9. HTS current lead units prepared by the TFA-MOD processed YBCO coated conductors

    International Nuclear Information System (INIS)

    Shiohara, K.; Sakai, S.; Ishii, Y.; Yamada, Y.; Tachikawa, K.; Koizumi, T.; Aoki, Y.; Hasegawa, T.; Tamura, H.; Mito, T.

    2010-01-01

    Two superconducting current lead units have been prepared using ten coated conductors of the Tri-Fluoro-Acetate - Metal Organic Deposition (TFA-MOD) processed Y 1 Ba 2 Cu 3 O 7-δ (YBCO) coated conductors with critical current (I c ) of about 170 A at 77 K in self-field. The coated conductors are 5 mm in width, 190 mm in length and about 120 μm in overall thickness. The 1.5 μm thick superconducting YBCO layer was synthesized through the TFA-MOD process on Hastelloy TM C-276 substrate tape with two buffer oxide layers of Gd 2 Zr 2 O 7 and CeO 2 . The five YBCO coated conductors are attached on a 1 mm thick Glass Fiber Reinforced Plastics (GFRP) board and soldered to Cu caps at the both ends. We prepared two 500 A-class current lead units. The DC transport current of 800 A was stably applied at 77 K without any voltage generation in all coated conductors. The voltage between both Cu caps linearly increased with increasing the applied current, and was about 350 μV at 500 A in both current lead units. According to the estimated values of the heat leakage from 77 K to 4.2 K, the heat leakage for the current lead unit was 46.5 mW. We successfully attained reduction of the heat leakage because of improvement of the transport current performance (I c ), a thinner Ag layer of YBCO coated conductor and usage of the GFRP board for reinforcement instead of a stainless steel board used in the previous study. The DC transport current of 1400 A was stably applied when the two current lead units were joined in parallel. The sum of the heat leakages from 77 K to 4.2 K for the combined the current lead units was 93 mW. In comparison with the conventional Cu current leads by gas-cooling, it could be noted that the heat leakage of the current lead is about one order of magnitude smaller than that of the Cu current lead.

  10. State of the art and prospective of large scale applications of YBCO thick films grown on metallic substrates; Possibilita` applicative a larga scala dei film spessi di YBCO su substrati metallici: Stato dell`arte e prospettive

    Energy Technology Data Exchange (ETDEWEB)

    Boffa, Vincenzo [ENEA, Centro Ricerche Frascati, Rome (Italy). Dipt. Energia

    1997-09-01

    In the framework of the high temperature superconducting materials, YBa{sub 2}Cu{sub 3}O{sub 7} (YBCO) shows very interesting intrinsic superconducting transport properties at temperature higher than the liquid nitrogen temperature. These properties are very important in large scale applications: transport of energy, magnets, transformers, etc. Unfortunately the potential of this material cannot be achieved today, since it is very difficult to manufacture YBCO based tapes or cables. In the last years several groups have tried to overcome the problems with new fabrication techniques. In the present report the state of the art and the prospective in the field of YBCO film fabrication on metallic substrates are presented.

  11. Thermodynamical fluctuations and critical behavior in weakly disordered YBCO thin and ultra-thin films

    International Nuclear Information System (INIS)

    Lesueur, J.; Aprili, M.; Degoy, S.; Chambonnet, D.; Keller, D.

    1996-01-01

    The specific role of disorder in the transport properties of YBCO has been investigated, using both light-ion irradiation of thin films to finely tune the amount of atomic disorder, and ultra-thin films grown to study possible dimensional effects. For weak disorder, the samples display a resistive transition typical of the mean-field paraconductive regime of a homogeneous media, well described by the Lawrence and Doniach model for layered superconductors. As the disorder increases, two effects take place. First, the c-axis coherence length becomes shorter, leading to a more anisotropic material, as shown by the excess conductivity above T c . Second, an incipient granularity is revealed, leading to a less sharper transition, which is analyzed within the random 3D XY critical model for the paracoherence transition. Two main results are derived: an experimental test of the Ginzburg criteria for the paracoherence transition, and a new fluctuation regime in nanometric grain size superconductors

  12. Tunable pinning effects produced by non-uniform antidot arrays in YBCO thin films

    Energy Technology Data Exchange (ETDEWEB)

    George, J.; Jones, A.; Al-Qurainy, M. [Institute for Superconducting and Electronic Materials, University of Wollongong, NSW (Australia); Fedoseev, S.A. [Institute for Superconducting and Electronic Materials, University of Wollongong, NSW (Australia); Centre for Medical Radiation Physics, University of Wollongong, NSW (Australia); Rosenfeld, A. [Centre for Medical Radiation Physics, University of Wollongong, NSW (Australia); Pan, A.V. [Institute for Superconducting and Electronic Materials, University of Wollongong, NSW (Australia); National Research Nuclear University MEPhI (Moscow Engineering Physics Institute), Moscow (Russian Federation)

    2017-04-15

    Uniform, graded and spaced arrays of 3 μm triangular antidots in pulsed laser deposited YBa{sub 2}Cu{sub 3}O{sub 7} (YBCO) superconducting thin films are compared by examining the improvements in the critical current density J{sub c} they produced. The comparison is made to establish the role of their lithographically defined (non-)uniformity and the effectiveness to control and/or enhance the critical current density. It is found that almost all types of non-uniform arrays, including graded ones enhance J{sub c} over the broad applied magnetic field and temperature range due to the modified critical state. Whereas uniform arrays of antidots either reduce or produce no effect on J{sub c} compared to the original (as-deposited) thin films. (copyright 2017 by WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  13. High critical current density YBCO films and fabrication of dc-SQUIDs

    CERN Document Server

    Kuriki, S; Kawaguchi, Y; Matsuda, M; Otowa, T

    2002-01-01

    In order to improve the sensitivity of SQUID magnetometers made of high-T sub c films, we have studied the conditions of pulsed-laser deposition of YBCO films. Among the different deposition parameters examined, extensive degassing of the vacuum chamber before and precise control of the substrate temperature during the film deposition were found effective for obtaining high critical temperature T sub c and high critical current density J sub c. It was also found that the residual-resistance ratio has a clear correlation with J sub c , indicating that it can be a good, and easy to measure, index of the film quality. Films having T sub c approx 89-90 K and J sub c >= 5x10 sup 6 A cm sup - sup 2 at 77 K were used to fabricate SQUIDs without a pickup loop. Grain-boundary junctions formed on bicrystal substrates with a 30 deg. misorientation angle exhibited I sub c R sub n values of more than 100 mu V at 77 K. The well-known scaling behaviour of the relation I sub c R sub n propor to (J sup G sup B sub c) sup 1 su...

  14. Planar intrinsic Josephson junctions with in-plane aligned YBCO films

    CERN Document Server

    Zhang, L; Kobayashi, T; Goto, T; Mukaida, M

    2002-01-01

    Planar type devices were fabricated by patterning in-plane aligned YBa sub 2 Cu sub 3 O sub 7 sub - subdelta (YBCO) films. The current-voltage characteristics along the c-axis at various temperatures and oxygen contents were measured. The current voltage curves showing supercurrent and hysteresis were obtained for the samples annealed at an oxygen pressure of 1.3 x 10 sup 4 Pa, while the supercurrent and hysteresis became smaller and even disappeared as the oxygen pressure decreased. The relationships between the critical currents and temperatures are similar to those of d-wave superconducting tunnel junctions. These results indicate the formation of stacks of intrinsic Josephson junctions, which are useful for developing high-frequency electron devices.

  15. Planar intrinsic Josephson junctions with in-plane aligned YBCO films

    International Nuclear Information System (INIS)

    Zhang, L; Moriya, M; Kobayashi, T; Goto, T; Mukaida, M

    2002-01-01

    Planar type devices were fabricated by patterning in-plane aligned YBa 2 Cu 3 O 7-δ (YBCO) films. The current-voltage characteristics along the c-axis at various temperatures and oxygen contents were measured. The current voltage curves showing supercurrent and hysteresis were obtained for the samples annealed at an oxygen pressure of 1.3 x 10 4 Pa, while the supercurrent and hysteresis became smaller and even disappeared as the oxygen pressure decreased. The relationships between the critical currents and temperatures are similar to those of d-wave superconducting tunnel junctions. These results indicate the formation of stacks of intrinsic Josephson junctions, which are useful for developing high-frequency electron devices

  16. In-plane aligned YBCO film on textured YSZ buffer layer deposited on NiCr alloy tape by laser ablation with only O+ ion beam assistance

    International Nuclear Information System (INIS)

    Xin Tang Huang

    2000-01-01

    High critical current density and in-plane aligned YBa 2 Cu 3 O 7-x (YBCO) film on a textured yttria-stabilized zirconia (YSZ) buffer layer deposited on NiCr alloy (Hastelloy c-275) tape by laser ablation with only O + ion beam assistance was fabricated. The values of the x-ray phi-scan full width at half-maximum (FWHM) for YSZ(202) and YBCO(103) are 18 deg. and 11 deg., respectively. The critical current density of YBCO film is 7.9 x 105 A cm -2 at liquid nitrogen temperature and zero field, and its critical temperature is 90 K. (author)

  17. YBa2Cu3O7-x thin films prepared by chemical solution deposition

    International Nuclear Information System (INIS)

    Apetrii, Claudia

    2009-01-01

    The discovery of superconductivity in ceramic materials by Bednorz and Mueller in early 1987, immediately followed by Wu et al., who showed that YBa 2 Cu 3 O 7-x (YBCO) becomes superconducting (92 K) well above the boiling point of nitrogen (77 K) created a great excitement in superconductivity research. Potential applications of high T c -superconductors require large critical currents and high-applied magnetic fields. Effective ways to increase the critical current density at high magnetic fields in YBCO are the introduction of nanoparticles and chemical substitution of yttrium by other rare earth elements. Since low costs and environmental compatibility are essential conditions for the preparation of long length YBCO films, the cost effective chemical solution deposition (CSD) procedure was selected, given that no vacuum technology is required. To reveal the flexibility and the good optimization possibilities of the CSD approach two main processes were chosen for comparison: a fluorine-free method, namely the polymer-metal precursor technique, and a fluorine-based method, the metalorganic deposition (MOD) using the trifluoroacetates (TFA) technique. Sharp transition temperature widths ΔT c of 1.1 K for the polymer metal method, 0.8 K for TFA method and critical current densities J c of ∼3.5 MA/cm 2 shows that high quality YBCO thin films can be produced using both techniques. Especially interesting is the magnetic field dependence of the critical current density J c (B) of the Y(Dy)BCO (80 %) films showing that for the lower magnetic fields the critical current density J c (B) is higher for a standard YBCO film, but at fields higher than 4.5 T the critical current density J c (B) of Y(Dy)BCO is larger than that for the YBCO. Above 8 T, J c (B) of the Y(Dy)BCO film is more than one order of magnitude higher than in pure YBCO film. (orig.)

  18. Effect of the microscopic correlated-pinning landscape on the macroscopic critical current density in YBCO films

    Science.gov (United States)

    Ghigo, G.; Chiodoni, A.; Gerbaldo, R.; Gozzelino, L.; Laviano, F.; Mezzetti, E.; Minetti, B.; Camerlingo, C.

    This paper deals with the mechanisms controlling the critical current density vs. field behavior in YBCO films. We base our analysis on a suitable model concerning the existence of a network of intergrain Josephson junctions whose length is modulated by defects. Irradiation with 0.25 GeV Au ions provide a useful tool to check the texture of the sample, in particular to give a gauge length reference to separate “weak” links and high- J c links.

  19. In-plane aligned YBCO tape on textured YSZ buffer layer deposited on stainless steel substrate by laser ablation only with O{sup +} ion beam assistance

    Energy Technology Data Exchange (ETDEWEB)

    Huang Xintang [Huazhong Univ. of Sci. and Technol., Wuhan (China). Nat. Lab. of Laser Technol.]|[Huazhong Normal Univ., Wuhan, HB (China). Dept. of Physics; Wang Youqing; Wang Qiuliang; Chen Qingming [Huazhong Univ. of Sci. and Technol., Wuhan (China). Nat. Lab. of Laser Technol.

    1999-08-16

    In this paper we have prepared YSZ buffer layers on stainless steel substrates by laser ablation only with O{sup +} ion beam assistance and YBCO films on YSZ/steel consequently. The relevant parameters of YSZ and YBCO film deposition are indicated. (orig.) 8 refs.

  20. In-plane aligned YBCO tape on textured YSZ buffer layer deposited on stainless steel substrate by laser ablation only with O+ ion beam assistance

    International Nuclear Information System (INIS)

    Huang Xintang; Huazhong Normal Univ., Wuhan, HB; Wang Youqing; Wang Qiuliang; Chen Qingming

    1999-01-01

    In this paper we have prepared YSZ buffer layers on stainless steel substrates by laser ablation only with O + ion beam assistance and YBCO films on YSZ/steel consequently. The relevant parameters of YSZ and YBCO film deposition are indicated. (orig.)

  1. Study on optimization of YBCO thin film stack for compact NMR magnets

    International Nuclear Information System (INIS)

    Kim, S.B.; Kimoto, T.; Hahn, S.; Iwasa, Y.; Voccio, J.; Tomita, M.

    2013-01-01

    Highlights: ► Stacking methods for compact NMR magnet using YBCO thin films were tested. ► The stacking angles are 0°, 22.5° and 90° against the rolling direction. ► The best spatial field homogeneity was obtained in rotation angle of 22.5°. ► The maximum trapped magnetic fields of 0.4 T was obtained at 77.4 K. ► The maximum trapped magnetic fields of 0.95 T was obtained at 21 K. -- Abstract: A compact high temperature superconducting (HTS) magnet, which consists of a stack of 500 HTS thin film annuli, was constructed and tested. Each thin film annulus, manufactured by the AMSC using the Rolling Assisted Bi-axially Textured Substrate (RABiTS) method, has a square cross-section of 40 mm × 40 mm with a thickness of 80 m. It has a 25-mm center hole created by machining. This paper reports a study on the anisotropic J c issue due to the rolling procedure of the Ni substrate direction and its impact on field homogeneity. Also, three different stacking methods with rotation angles of 22.5°, 90°, and 0° against the rolling direction have been tested to study their impacts on strength, spatial homogeneity, and temporal stability of trapped fields. Finally, the 500-annulus magnet was tested at 21 K under a cryogen-free environment using a GM cryocooler. The spatial field homogeneity and temporal stability were measured at 21 K and compared with those obtained in a bath of liquid nitrogen at 77 K

  2. Improved interface growth and enhanced flux pinning in YBCO films deposited on an advanced IBAD-MgO based template

    Science.gov (United States)

    Khan, M. Z.; Zhao, Y.; Wu, X.; Malmivirta, M.; Huhtinen, H.; Paturi, P.

    2018-02-01

    The growth mechanism is studied from the flux pinning point of view in small-scale YBa2Cu3O6+x (YBCO) thin films deposited on a polycrystalline hastelloy with advanced IBAD-MgO based buffer layer architecture. When compared the situation with YBCO films grown on single crystal substrates, the most critical issues that affect the suitable defect formation and thus the optimal vortex pinning landscape, have been studied as a function of the growth temperature and the film thickness evolution. We can conclude that the best critical current property in a wide applied magnetic field range is observed in films grown at relatively low temperature and having intermediate thickness. These phenomena are linked to the combination of the improved interface growth, to the film thickness related crystalline relaxation and to the formation of linear array of edge dislocations that forms the low-angle grain boundaries through the entire film thickness and thus improve the vortex pinning properties. Hence, the optimized buffer layer structure proved to be particularly suitable for new coated conductor solutions.

  3. Tailoring the vortex pinning strength of YBCO thin films by systematic incorporation of hybrid artificial pinning centers

    International Nuclear Information System (INIS)

    Jha, Alok K; Matsumoto, Kaname; Horide, Tomoya; Saini, Shrikant; Mele, Paolo; Ichinose, Ataru; Yoshida, Yutaka; Awaji, Satoshi

    2015-01-01

    The effect of hybrid (columnar and spherical together) artificial pinning centers (APCs) on the vortex pinning properties of YBa 2 Cu 3 O 7−δ (YBCO) thin films is investigated in detail on the basis of variation of critical current density (J C ) with applied magnetic field and also with the orientation of the applied magnetic field at 65 K and 77 K. Premixed YBCO + BaSnO 3 composite targets are used for the deposition of the YBCO films which consist of self-assembled BaSnO 3 nanocolumns (1D APCs); on the other hand, for the deposition of the YBCO films with hybrid APCs (BaSnO 3 nanocolumns together with Y 2 O 3 nanoparticles), the surface of the premixed YBCO + BaSnO 3 composite targets are modified by putting a thin Y 2 O 3 sectored piece on the premixed YBCO + BaSnO 3 composite targets by means of silver paste. F pmax value increases systematically with incorporation of 1D and 1D and 3D APCs and it also shifts towards higher applied magnetic fields. Films with 1D APCs exhibit a strong J C peak at Θ = 0° (H//c-axis) whereas films consisting of hybrid APCs exhibit enhanced J C at all the investigated angular regimes. A possible mechanism of vortex pinning in samples with hybrid APCs is also discussed suggesting the role of 1D and 3D APCs. (paper)

  4. Transport AC losses in YBCO coated conductors

    Energy Technology Data Exchange (ETDEWEB)

    Majoros, M [Ohio State University, Columbus, OH 43210 (United States); Ye, L [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom); Velichko, A V [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom); Coombs, T A [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom); Sumption, M D [Ohio State University, Columbus, OH 43210 (United States); Collings, E W [Ohio State University, Columbus, OH 43210 (United States)

    2007-09-15

    Transport AC loss measurements have been made on YBCO-coated conductors prepared on two different substrate templates-RABiTS (rolling-assisted biaxially textured substrate) and IBAD (ion-beam-assisted deposition). RABiTS samples show higher losses compared with the theoretical values obtained from the critical state model, with constant critical current density, at currents lower than the critical current. An origin of this extra AC loss was demonstrated experimentally by comparison of the AC loss of two samples with different I-V curves. Despite a difference in I-V curves and in the critical currents, their measured losses, as well as the normalized losses, were practically the same. However, the functional dependence of the losses was affected by the ferromagnetic substrate. An influence of the presence of a ferromagnetic substrate on transport AC losses in YBCO film was calculated numerically by the finite element method. The presence of a ferromagnetic substrate increases transport AC losses in YBCO films depending on its relative magnetic permeability. The two loss contributions-transport AC loss in YBCO films and ferromagnetic loss in the substrate-cannot be considered as mutually independent.

  5. Enhancement of YBCO thin film thermal stability under 1 ATM oxygen pressure by Intermediate Cu.sub.2./sub. O nanolayer

    Czech Academy of Sciences Publication Activity Database

    Cheng, L.; Wang, X.; Yao, X.; Wan, W.; Li, F.H.; Xiong, J.; Tao, B.W.; Jirsa, Miloš

    2010-01-01

    Roč. 114, č. 22 (2010), s. 7543-7547 ISSN 1520-6106 R&D Projects: GA MŠk(CZ) ME10069 Institutional research plan: CEZ:AV0Z10100520 Keywords : YBCO thin films * thermal stability * thin film growth orientation * temperature optical microscopy Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.603, year: 2010

  6. A-axis oriented superconductive YBCO thin films. Growth mechanism on MgO substrate. [Y-Ba-Cu-O

    Energy Technology Data Exchange (ETDEWEB)

    Hamet, J F; Mercey, B; Hervieu, M; Poullain, G; Raveau, B [Centre de Materiaux Supraconducteurs, CRISMAT-ISMRa, 14 - Caen (France)

    1992-08-01

    The growth mechanism of a-axis oriented YBCO thin films has been studied by TEM. At 650degC, a disordered cubic perovskite is first formed with a[sub p]parallela[sub MgO], then a strained tetragonal a-axis oriented perovskite is observed, with c=3a[sub p], slightly misoriented with respect to MgO and showing a marquetry-like contrast. At 750degC, a [1anti 10] axis oriented perovskite is formed whose lattice exhibits a rotation with respect to MgO lattice, but also a tilting of the [CuO[sub 2

  7. Studies of proximity-effect and tunneling in YBCO/metal layered films

    Energy Technology Data Exchange (ETDEWEB)

    Greene, L.H.; Barner, J.B.; Feldmann, W.L.; Farrow, L.A.; Miceli, P.F.; Ramesh, R.; Wilkens, B.J.; Bagley, B.G.; Tarascon, J.M.; Wernick, J.H. (Bellcore, Red Bank, NJ (USA)); Giroud, M. (CRTBT-CNRS, Grenoble (France)); Rowell, J.M. (Conductus, Sunnyvale, CA (USA))

    1989-12-01

    The short coherence length of the high-Tc superconductors, coupled with their tendency to form non-superconducting surface layers, accounts for the difficulty in achieving good tunnel junctions. A proximity layer of a longer coherence length normal metal (N) is expected to ''draw out'' Cooper pairs. Our goal is to fabricate reproducible, planar tunnel junctions of SNIS layered structures for proximity tunneling spectroscopy. Such structures of YBCO/N/I/Pb and SNS structures of YBCO/N/Pb indicate that the normal metal produces a low resistance contact to the YBCO surface with a supercurrent observed in the SNS. The insulating barrier in the SNIS is reproducible, insulating and continuous: A sharp Pb gap and phonons from the counter-electrode are routinely observed. (orig.).

  8. Studies of proximity-effect and tunneling in YBCO/metal layered films

    International Nuclear Information System (INIS)

    Greene, L.H.; Barner, J.B.; Feldmann, W.L.; Farrow, L.A.; Miceli, P.F.; Ramesh, R.; Wilkens, B.J.; Bagley, B.G.; Tarascon, J.M.; Wernick, J.H.; Giroud, M.; Rowell, J.M.

    1989-01-01

    The short coherence length of the high-T c superconductors, coupled with their tendency to form non-superconducting surface layers, accounts for the difficulty in achieving good tunnel junctions. A proximity layer of a longer coherence length normal metal (N) is expected to draw out Cooper pairs. The authors' goal is to fabricate reproducible, planar tunnel junctions of SNIS layered structures for proximity tunneling spectroscopy. They discuss how such structures of YBCO/N/I/Pb and SNS structures of YBCO/N/Pb indicate that the normal metal produces a low resistance contact to the YBCO surface with a supercurrent observed in the SNS. The insulating barrier in the SNIS is reproducible, insulating and continuous: A sharp Pb gap and phonons from the counter-electrode are routinely observed

  9. Microstructures and precipitates in laser-ablated YBCO thin films on SrTiO[sub 3] (110). [Y-Ba-Cu-O

    Energy Technology Data Exchange (ETDEWEB)

    Catana, A. (IBM Research Div., Zurich Research Lab., Rueschlikon (Switzerland)); Rossel, C. (IBM Research Div., Zurich Research Lab., Rueschlikon (Switzerland)); Perrin, A. (Lab. de Chimie du Solide et Inorganique Moleculaire, Univ. de Rennes 1, 35 (France)); Guilloux-Viry, M. (Lab. de Chimie du Solide et Inorganique Moleculaire, Univ. de Rennes 1, 35 (France)); Thivet, C. (Lab. de Chimie du Solide et Inorganique Moleculaire, Univ. de Rennes 1, 35 (France))

    1993-05-10

    Thin YBCO films ([proportional to] 100 nm) have been deposited by laser ablation on SrTiO[sub 3] (110) substrates. Microstructural investigations have been performed by scanning tunneling and high-resolution electron microscopy. The results show that the surface corrugation is related to the growth of twisted YBCO domains that nucleate at the film/substrate interface. The twist is characterized by a 90 rotation of YBCO around the 100 and/or 010 axes, which results in [l brace]013[r brace] and/or [l brace]103[r brace] planes parallel to the substrate surface. Precipitates belonging to Y[sub 2]O[sub 3] are densely distributed on the film surface. No such second phases have been identified inside the YBCO films. The orientational relationship between precipitates and film is such that the lattice mismatch is minimized in the interface planes. A large number of precipitates grow from the film surface outwards. This phenomenon can be explained on the basis of lattice matching arguments and favorable growth kinetics. (orig.)

  10. Growth orientation and superconducting properties of YBa2Cu3O7-δ films prepared by the low-fluorine sol-gel process

    International Nuclear Information System (INIS)

    Lei Li; Zhao Gaoyang; Xu Hui; Zhao Juanjuan

    2010-01-01

    YBa 2 Cu 3 O 7-δ (YBCO) films were deposited on (100)-oriented LaAlO 3 (LAO) single crystal substrates by the dip-coating process using low-fluorine solution. Their microstructures were characterized with the aid of X-ray diffractometry, scanning electron microscopy and high-resolution transmission electron microscopy. Their superconducting properties were measured by the standard four-probe method. The experiment results show that the film obtained under high enough humidity conditions exhibits better c-axis texture and superconducting properties than the film under a relatively low humidity conditions. Based on the classical nucleation and chemical reaction thermodynamics theory, the underlying crystalline and growth mechanisms of YBCO films under certain humidity conditions are explained in combination with our experimental results. It is suggested that the unreacted intermediate phases such as BaF 2 and CuO aggregated in the YBCO grain boundary will cause lattice distortion in the YBCO matrix and further induce the formation of a-axis oriented YBCO grains as crystallization proceeds. Therefore, it is believed that the relative content of water vapor within the heat-treatment atmosphere plays quite an important role in the preparation of c-axis oriented YBCO film with good superconducting properties. (semiconductor materials)

  11. Factors that determine the presence of particles in YBCO films grown by PLD

    International Nuclear Information System (INIS)

    Barrales-Guadarrama, V R; Rodríguez-Rodríguez, E M; Barrales-Guadarrama, R; Reyes Ayala, N

    2017-01-01

    The method of growing thin films PLD, is widely used in applications and possesses great potential in thin YBa 2 Cu 3 O 7-δ films production with outstanding physical properties. However, it is limited in nano and micro technology due to the presence of particles on the surface of the films. This article describes some causes that create these particles. YBa 2 Cu 3 O 7-δ films have been grown on electrolytic copper used as a variable model the distance target-substrate. The effects are studied through Scanning Electronic Microscopy. It is observed particles with a large variety of shapes and distributions. The results show that ranging the target-substrate distance, the superficial morphology is modified. An evidence of it, is that the evaporation of d B-S = 7 cm, is more coherent that d B-S = 3 cm. Therefore, exist a relation between the morphology and the parameters of growing. Also affect, the structural change that exists among the substrate and the film formation, the substrate preparation and it must not be monocrystalline, these factors define a kinetic and a mechanism of growing that promotes a heterogeneous nucleation. (paper)

  12. Excess hall effect in epitaxial YBCO film under moderate magnetic fields, approached by renormalized superconducting fluctuations model

    International Nuclear Information System (INIS)

    Puica, I.; Lang, W.; Goeb, W.; Sobolewski, R.

    2002-01-01

    Full text: Measurements of the Hall effect and the resistivity on precisely-patterned YBCO thin film in moderate magnetic fields B from 0.5 to 6 T oriented parallel to the crystallographic c axis reveal a sign reversal of the Hall coefficient for B < 3 T. The data are confronted with the full quantitative expressions given by the renormalized fluctuation model for the excess Hall conductivity. The model offers a satisfactory quantitative approach to the experimental results, for moderate fields and temperatures near the critical region, provided the inhomogeneity of the critical temperature distribution is also taken into account. For lower fields and temperatures, the adequacy of the model is altered by vortex pinning. (author)

  13. Growth orientation and superconducting properties of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} films prepared by the low-fluorine sol-gel process

    Energy Technology Data Exchange (ETDEWEB)

    Lei Li; Zhao Gaoyang; Xu Hui; Zhao Juanjuan, E-mail: leili813@gmail.co [School of Materials Science and Engineering, Xi' an University of Technology, Xi' an 710048 (China)

    2010-08-15

    YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) films were deposited on (100)-oriented LaAlO{sub 3} (LAO) single crystal substrates by the dip-coating process using low-fluorine solution. Their microstructures were characterized with the aid of X-ray diffractometry, scanning electron microscopy and high-resolution transmission electron microscopy. Their superconducting properties were measured by the standard four-probe method. The experiment results show that the film obtained under high enough humidity conditions exhibits better c-axis texture and superconducting properties than the film under a relatively low humidity conditions. Based on the classical nucleation and chemical reaction thermodynamics theory, the underlying crystalline and growth mechanisms of YBCO films under certain humidity conditions are explained in combination with our experimental results. It is suggested that the unreacted intermediate phases such as BaF{sub 2} and CuO aggregated in the YBCO grain boundary will cause lattice distortion in the YBCO matrix and further induce the formation of a-axis oriented YBCO grains as crystallization proceeds. Therefore, it is believed that the relative content of water vapor within the heat-treatment atmosphere plays quite an important role in the preparation of c-axis oriented YBCO film with good superconducting properties. (semiconductor materials)

  14. Preparation of thin vyns films

    International Nuclear Information System (INIS)

    Blanc, R.; Chedin, P.; Gizon, A.

    1965-01-01

    The fabrication of thin films of VYNS resin (copolymer of chloride and vinyl acetate) of superficial density from 3 to 50 μg/cm 2 with solutions in cyclohexanone is presented. Study and discussion of some properties compared with formvar film (polyvinyl formals). It appears that both can be used as source supports but formvar films are prepared more easily and more quickly, in addition they withstand higher temperatures. The main quality of VYNS is that they can be easily separated even several days after their preparation [fr

  15. Modeling flux pinning in thin undoped and BazRo3-doped YBCO films

    DEFF Research Database (Denmark)

    Paturi, P.; Irjala, M.; Huhtinen, H.

    2009-01-01

    A simple model based on distributions of twin boundaries, dislocations, and BaZrO3 nanorods is presented to describe the Jc properties of undoped and BaZrO3 (BZO)-doped YBa2Cu3Ox thin films. The model accurately describes the shape of Jc(B,T) curves of the films, when the pinning site distributions...... are taken from distributions of twin spacings and BZO nanorods from transmission electron microscope images. Thus, assuming that the model can be used for prediction of the Jc properties, we conclude that for enhancement of undoped films more crystalline defects are needed and for doped films a dopant...

  16. Vaporization of a mixed precursors in chemical vapor deposition for YBCO films

    Science.gov (United States)

    Zhou, Gang; Meng, Guangyao; Schneider, Roger L.; Sarma, Bimal K.; Levy, Moises

    1995-01-01

    Single phase YBa2Cu3O7-delta thin films with T(c) values around 90 K are readily obtained by using a single source chemical vapor deposition technique with a normal precursor mass transport. The quality of the films is controlled by adjusting the carrier gas flow rate and the precursor feed rate.

  17. Properties of HTS YBCO thin films deposited on tilted NdGaO{sub 3} substrates

    Energy Technology Data Exchange (ETDEWEB)

    Nurgaliev, T. [Laboratory of Superconductivity and Cryoelectronics, Institute of Electronics BAS, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria)]. E-mail: timur@ie.bas.bg; Donchev, T. [Laboratory of Superconductivity and Cryoelectronics, Institute of Electronics BAS, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Mateev, E. [Laboratory of Superconductivity and Cryoelectronics, Institute of Electronics BAS, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Miteva, S. [Laboratory of Superconductivity and Cryoelectronics, Institute of Electronics BAS, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Mozhaev, P.B. [Institute of Physics and Technology RAS, Nakhimovsky Ave. 36, 117218 Moscow (Russian Federation); Mozhaeva, J.E. [Institute of Physics and Technology RAS, Nakhimovsky Ave. 36, 117218 Moscow (Russian Federation)

    2005-03-15

    Thin YBa{sub 2}Cu{sub 3}O{sub 7} films were fabricated by 2-opposed DC magnetron sputtering onto NdGaO{sub 3} substrates, tilted from standard (1 1 0) orientation by 0-26 deg , and their surface morphology and electrical characteristics were investigated. Normal state resistivity (at 295 K) and microwave surface resistance (at 77 K and {approx}8 GHz) of the films demonstrated anisotropy, introduced by the tilted substrate, and some improvement of the superconducting parameters of the films was observed at small tilt angles ({theta} {approx} 1.5-3 deg ). The increase of the microwave surface resistance at high tilt angles for the current tracks, perpendicular to the steps of the substrate, was described in the framework of a simple model, which takes into account the complex conductivity of the film and the weak links between the film terraces.

  18. Properties of HTS YBCO thin films deposited on tilted NdGaO3 substrates

    International Nuclear Information System (INIS)

    Nurgaliev, T.; Donchev, T.; Mateev, E.; Miteva, S.; Mozhaev, P.B.; Mozhaeva, J.E.

    2005-01-01

    Thin YBa 2 Cu 3 O 7 films were fabricated by 2-opposed DC magnetron sputtering onto NdGaO 3 substrates, tilted from standard (1 1 0) orientation by 0-26 deg , and their surface morphology and electrical characteristics were investigated. Normal state resistivity (at 295 K) and microwave surface resistance (at 77 K and ∼8 GHz) of the films demonstrated anisotropy, introduced by the tilted substrate, and some improvement of the superconducting parameters of the films was observed at small tilt angles (θ ∼ 1.5-3 deg ). The increase of the microwave surface resistance at high tilt angles for the current tracks, perpendicular to the steps of the substrate, was described in the framework of a simple model, which takes into account the complex conductivity of the film and the weak links between the film terraces

  19. Preparation of epitaxial YBa2Cu3O7-y films on CeO2-buffered yttria-stabilized zirconia substrates by fluorine-free metalorganic deposition

    International Nuclear Information System (INIS)

    Tsukada, Kenichi; Yamaguchi, Iwao; Sohma, Mitsugu; Kondo, Wakichi; Kamiya, Kunio; Kumagai, Toshiya; Manabe, Takaaki

    2007-01-01

    Epitaxial YBa 2 Cu 3 O 7-y (YBCO) films of 120-550 nm thickness have been prepared by fluorine-free metalorganic deposition using a metal acetylacetonate-based coating solution on yttria-stabilized zirconia (YSZ) substrates with an evaporated CeO 2 buffer layer. The YBCO films were highly (0 0 1)-oriented by X-ray diffraction θ-2θ scanning and φ scanning. The YBCO films 120-400 nm in thickness demonstrated high critical current densities (J c ) with an average in excess of 3 MA/cm 2 at 77 K using an inductive method. In particular, a 210-nm-thick film showed a J c of 4.5 MA/cm 2 . These excellent properties are attributed to the high crystallinity, small in-plane fluctuation due to high epitaxy and to the microstructure free from grain boundaries in the YBCO films. Further increase of film thickness increased the fraction of irregularities, i.e., precipitates and micropores, in the film surfaces, resulting in lower J c values

  20. High temperature superconducting YBCO microwave filters

    Science.gov (United States)

    Aghabagheri, S.; Rasti, M.; Mohammadizadeh, M. R.; Kameli, P.; Salamati, H.; Mohammadpour-Aghdam, K.; Faraji-Dana, R.

    2018-06-01

    Epitaxial thin films of YBCO high temperature superconductor are widely used in telecommunication technology such as microwave filter, antenna, coupler and etc., due to their lower surface resistance and lower microwave loss than their normal conductor counterparts. Thin films of YBCO were fabricated by PLD technique on LAO substrate. Transition temperature and width were 88 K and 3 K, respectively. A filter pattern was designed and implemented by wet photolithography method on the films. Characterization of the filter at 77 K has been compared with the simulation results and the results for a made gold filter. Both YBCO and gold filters show high microwave loss. For YBCO filter, the reason may be due to the improper contacts on the feedlines and for gold filter, low thickness of the gold film has caused the loss increased.

  1. YBa{sub 2}Cu{sub 3}O{sub 7-x} thin films prepared by chemical solution deposition

    Energy Technology Data Exchange (ETDEWEB)

    Apetrii, Claudia

    2009-11-25

    The discovery of superconductivity in ceramic materials by Bednorz and Mueller in early 1987, immediately followed by Wu et al., who showed that YBa{sub 2}Cu{sub 3}O{sub 7-x} (YBCO) becomes superconducting (92 K) well above the boiling point of nitrogen (77 K) created a great excitement in superconductivity research. Potential applications of high T{sub c}-superconductors require large critical currents and high-applied magnetic fields. Effective ways to increase the critical current density at high magnetic fields in YBCO are the introduction of nanoparticles and chemical substitution of yttrium by other rare earth elements. Since low costs and environmental compatibility are essential conditions for the preparation of long length YBCO films, the cost effective chemical solution deposition (CSD) procedure was selected, given that no vacuum technology is required. To reveal the flexibility and the good optimization possibilities of the CSD approach two main processes were chosen for comparison: a fluorine-free method, namely the polymer-metal precursor technique, and a fluorine-based method, the metalorganic deposition (MOD) using the trifluoroacetates (TFA) technique. Sharp transition temperature widths {delta}T{sub c} of 1.1 K for the polymer metal method, 0.8 K for TFA method and critical current densities J{sub c} of {approx}3.5 MA/cm{sup 2} shows that high quality YBCO thin films can be produced using both techniques. Especially interesting is the magnetic field dependence of the critical current density J{sub c}(B) of the Y(Dy)BCO (80 %) films showing that for the lower magnetic fields the critical current density J{sub c}(B) is higher for a standard YBCO film, but at fields higher than 4.5 T the critical current density J{sub c}(B) of Y(Dy)BCO is larger than that for the YBCO. Above 8 T, J{sub c}(B) of the Y(Dy)BCO film is more than one order of magnitude higher than in pure YBCO film. (orig.)

  2. Defining B-c, B* and B-phi for YBCO Thin Films

    DEFF Research Database (Denmark)

    Paturi, Petriina; Irjala, Matti; Abrahamsen, Asger Bech

    2009-01-01

    of superconducting films. Similarly, the characteristic field, B c, can be obtained from magneto-optical (MO) images from when the flux fronts meet in the middle of the film. The matching field, B phi, at which there is one vortex line per pinning site, is sometimes thought to be the same as B*, but in BaZrO3-doped...... YBa2Cu3O7 films the calculated B phi is much higher than the observed B*. B phi can be determined from angular dependent transport measurements. All of the field values correspond to some special case in the flux pinning in the film and relate to J c. In this work we have determined B c, B* and B phi...

  3. Microwave absorption in YBCO/PrBCO superlattices

    International Nuclear Information System (INIS)

    Carlos, W.E.; Kaplan, R.; Lowndes, D.H.; Norton, D.P.

    1992-01-01

    In this paper, non-resonant microwave absorption is employed to probe YBCO/PrBCO superlattices and compare the response to that of a YBCO film. Near the transition temperatures, the response of the superlattice samples and the YBCO film have similar amplitudes and orientation dependencies. At lower temperatures, the response of the superlattices is much stronger than that of the YBCO film and, while both responses are hysteretic at low temperatures, the widths of the hysteresis have opposite orientation dependencies, which the authors attribute to the role of the PrBCO layers

  4. A low-fluorine solution with a 2:1 F/Ba mole ratio for the fabrication of YBCO films

    DEFF Research Database (Denmark)

    Wu, Wei; Feng, Feng; Yue, Zhao

    2014-01-01

    must be at least 2 for full conversion of the Ba-precursor to BaF2 to avoid the formation of BaCO3, which is detrimental to the superconducting performance of YBCO films. In this study, a solution with a 2:1 F/Ba mole ratio was developed, and the fluorine content of this solution was approximately only...... 10.3% of that used in the conventional TFA-MOD method. Attenuated total reflectance-Fourier transform-infrared spectra (ATR-FT-IR) revealed that BaCO3 was remarkably suppressed in the as-pyrolyzed film—and eliminated at 700 °C. Thus, YBCO films with a critical current density (Jc) of over 5 MA cm−2...... (77 K, 0 T, 200 nm thickness) could be obtained on lanthanum aluminate single-crystal substrates. In situ FT-IR spectra showed that no obvious fluorinated gaseous by-products were detected in the pyrolysis step, which indicated that all F atoms might remain in the film as fluorides. X-ray diffraction...

  5. Nonlinear surface impedance of YBCO thin films: Measurements, modeling, and effects in devices

    International Nuclear Information System (INIS)

    Oates, D.E.; Koren, G.; Polturak, E.

    1995-01-01

    High-T c thin films continue to be of interest for passive device applications at microwave frequencies, but nonlinear effects may limit the performance. To understand these effects we have measured the nonlinear effects may limit the performance. To understand these effects we have measured the nonlinear surface impedance Z s in a number of YBa 2 Cu 3 O 7-x thin films as a function of frequency from 1 to 18 GHz, rf surface magnetic field H rf to 1500 Oe, and temperature from 4 K to T c . The results at low H rf are shown to agree quantitatively with a modified coupled-grain model and at high H rf with hysteresis-loss calculations using the Bean critical-state model applied to a thin strip. The loss mechanisms are extrinsic properties resulting from defects in the films. We also report preliminary measurements of the nonlinear impedance of Josephson junctions, and the results are related to the models of nonlinear Z s . The implications of nonlinear Z s for devices are discussed using the example of a five-pole bandpass filter

  6. High-spatial resolution resistivity mapping of large-area YBCO films by a near-field millimeter-wave microscope

    International Nuclear Information System (INIS)

    Golosovsky, M.; Galkin, A.; Davidov, D.

    1996-01-01

    The authors demonstrate a new millimeter-wave technique for the resistivity mapping of large-area conducting films, namely, a near-field resistivity microscope. The microscope is based on the idea that electromagnetic waves are transmitted through a narrow resonant slit with high efficiency. By scanning this slit at fixed height above an inhomogeneous conducting surface and measuring the intensity and phase of the reflected wave, the resistivity of this surface may be determined with a 10--100 microm spatial resolution using 80-GHz radiation. Using this technique, they map normal-sate resistivity of 1 in x 1 in YBCO films at ambient temperature. In some films they find inhomogeneities of the normal-state sheet resistance of the order of 10%--20%

  7. Investigation on orientation, epitaxial growth and microstructure of a-axis-, c-axis-, (103)/(110)- and (113)-oriented YBa2Cu3O7-δ films prepared on (001), (110) and (111) SrTiO3 single crystal substrates by spray atomizing and coprecipitating laser chemical vapor deposition

    Science.gov (United States)

    Zhao, Pei; Wang, Ying; Huang, Zhi liang; Mao, Yangwu; Xu, Yuan Lai

    2015-04-01

    a-axis-, c-axis-, (103)/(110)- and (113)-oriented YBa2Cu3O7-δ (YBCO) films were pareared by spray atomizing and coprecipitating laser chemical vapor deposition. The surface of the a-axis-oriented YBCO film consisted of rectangular needle-like grains whose in-plane epitaxial growth relationship was YBCO [100] // STO [001] (YBCO [001] // STO [100]), and that of the c-axis-oriented YBCO film consisted of dense flat surface with epitaxial growth relationship of YBCO [001] // STO [001] (YBCO [100] //STO [100]). For the (103)/(110)-oriented and (113)-oriented YBCO film, they showed wedge-shaped and triangle-shaped grains, with corresponding in-plane epitaxial growth relationship of YBCO [110] // STO [110] (YBCO [010] // STO [010]) and YBCO [100] // STO [100] (YBCO [113] // STO [111], respectively.

  8. Measurements and analysis of the noise spectral density of YBCO films

    International Nuclear Information System (INIS)

    Taoufik, A.; Bghour, M.; Labrag, A.; Bouaaddi, A.; Abaragh, A.; Ramzi, A.; Senoussi, S.; Tirbiyine, A.

    2006-01-01

    We studied the voltage noise spectral density S V (f,T,H) dependence on frequency f, temperature T and applied magnetic field H in YBa 2 Cu 3 O 7-δ films. The voltage noise spectral density S V (f) as a function of frequency exhibits 1/f behavior according to a Lorentzian shape A [(1+πf/f 0 ) B ] C , where A, f 0 , B, C constants which are determined and compared for many values of H. The influence of temperature and magnetic field is clearly observed as a function of temperature, S V (T) is found to vanish at T g , the temperature of vortex glass transition, according to a (T-T g ) x law. We interpreted those results by the formation of a large distribution of glass vortex domains. Approaching T g , these domains grow in size and lifetime, while at T g those parameters diverge. (copyright 2006 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (Abstract Copyright [2006], Wiley Periodicals, Inc.)

  9. Zone refining of sintered, microwave-derived YBCO superconductors

    International Nuclear Information System (INIS)

    Warrier, K.G.K.; Varma, H.K.; Mani, T.V.; Damodaran, A.D.; Balachandran, U.

    1993-07-01

    Post-sintering treatments such as zone melting under thermal gradient has been conducted on sintered YBCO tape cast films. YBCO precursor powder was derived through decomposition of a mixture of nitrates of cations in a microwave oven for ∼4 min. The resulting powder was characterized and made into thin sheets by tape casting and then sintered at 945 C for 5 h. The sintered tapes were subjected to repeated zone refining operations at relatively high speeds of ∼30 mm/h. A microstructure having uniformly oriented grains in the a-b plane throughout the bulk of the sample was obtained by three repeated zone refining operations. Details of precursor preparation, microwave processing and its advantages, zone refining conditions, and microstructural features are presented in this paper

  10. Fabrication and characterization of hybrid Nb-YBCO dc SQUIDs

    International Nuclear Information System (INIS)

    Frack, E.K.; Drake, R.E.; Patt, R.; Radparvar, M.

    1991-01-01

    This paper reports on the fabrication of hybrid low T c /high T c dc SQUIDs of two flavors. The first kind utilizes niobium tunnel junctions and a YBCO film strip as the most inductive portion of the SQUID loop. This configuration allows a direct measurement of the inductance of the YBCO microstrip from which the effective penetration depth can be calculated. The successful fabrication of these SQUIDs has required 1. superconducting Nb-to-YBCO contacts, 2. deposition and patterning of an SiO 2 insulation layer over YBCO, and 3. selective patterning of niobium and SiO 2 relative to YBCO. All these process steps are pertinent to the eventual use of YBCO thin films in electronic devices

  11. Weakening of thickness dependence of J{sub C} in YBa{sub 2}Cu{sub 3}O{sub 7-δ} films using a titanium-added MOD precursor solution

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, H.L., E-mail: zhanghuiliang@mail.iee.ac.cn [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); School of Science, Hebei University of Engineering, Handan 056038 (China); Ding, F.Z., E-mail: dingfazhu@mail.iee.ac.cn [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Gu, H.W., E-mail: guhw@mail.iee.ac.cn [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Dong, Z.B. [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Qu, F.; Zhang, H.; Shang, H.J. [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China)

    2017-04-15

    Highlights: • The thickness dependence of J{sub C} in YBCO film was weakened by introducing BaTiO{sub 3} nanoparticles into YBCO matrix. • The high I{sub C} value of 430 MA/cm-width was obtained in the BaTiO{sub 3}-doped YBCO film prepared by the MOD method. • The YBCO composite thick film prepared by using the precursor solution with polyethyleneglycol shows a compact and smooth surface. - Abstract: BaTiO{sub 3} (BTO)-doped YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO) films were prepared by the metal-organic deposition method using a precursor solution with titanium ion. These YBCO films were deposited on (00l)-oriented LaAlO{sub 3} single-crystal substrates using an automated dip coater. The thickness dependence of critical current density (J{sub C}) in the BTO-doped YBCO films was investigated. The J{sub C} value of the YBCO composite film was reduced from 6.3 to 4.6 MA/cm{sup 2} with increasing film thickness from 450 to 930 nm in self-filed at 77 K, which arose mainly from degradation of texture and roughening of the film. However, relative to undoped YBCO thick films, J{sub C} values of the YBCO composite thick films were greatly improved, and more importantly, the reduction in J{sub C} with increasing film thickness was hindered, especially in a high magnetic field. This result indicated that the introduction of BTO nanoparticles as pinning centers into YBCO matrix weakened the thickness dependence of J{sub C}.

  12. Oromucosal film preparations: classification and characterization methods.

    Science.gov (United States)

    Preis, Maren; Woertz, Christina; Kleinebudde, Peter; Breitkreutz, Jörg

    2013-09-01

    Recently, the regulatory authorities have enlarged the variety of 'oromucosal preparations' by buccal films and orodispersible films. Various film preparations have entered the market and pharmacopoeias. Due to the novelty of the official monographs, no standardized characterization methods and quality specifications are included. This review reports the methods of choice to characterize oromucosal film preparations with respect to biorelevant characterization and quality control. Commonly used dissolution tests for other dosage forms are not transferable for films in all cases. Alternatives and guidance on decision, which methods are favorable for film preparations are discussed. Furthermore, issues about requirements for film dosage forms are reflected. Oromucosal film preparations offer a wide spectrum of opportunities. There are a lot of suggestions in the literature on how to control the quality of these innovative products, but no standardized tests are available. Regulatory authorities need to define the standards and quality requirements more precisely.

  13. High performance GdBa{sub 2}Cu{sub 3}O{sub 7-z} film preparation by non-fluorine chemical solution deposition approach

    Energy Technology Data Exchange (ETDEWEB)

    Wang, W.T.; Pu, M.H.; Wang, W.W. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Zhang, H. [Department of Physics, Peking University, Beijing 100871 (China); Cheng, C.H. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China)] [Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia); Zhao, Y., E-mail: yzhao@swjtu.edu.cn [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China)] [Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia)

    2011-11-15

    Biaxially textured GdBa{sub 2}Cu{sub 3}O{sub 7}-z films with Tc above 93 K have been prepared on (0 0 l) by non-fluorine CSD approach. Nanoparticles with homogeneous distribution are introduced into the GdBCO films as effective pinning centers. A high Jc (77 K, 0 T) of 2.28 MA/cm{sup 2} with slow decreasing Jc-B behavior is observed in the films. Biaxially textured GdBa{sub 2}Cu{sub 3}O{sub 7-z} (GdBCO) films with T{sub c} above 93 K have been prepared on (0 0 l) LaAlO{sub 3} substrate by self-developed non-fluorine polymer-assisted chemical solution deposition (PA-CSD) approach. The GdBCO films show smooth and crack-free morphology. Many nanoscale particles with homogeneous distribution are observed in the GdBCO films, which have not been observed yet in the YBa{sub 2}Cu{sub 3}O{sub 7-z} (YBCO) films prepared by the same processing technique. Besides a high J{sub c} (77 K, 0 T) of 2.28 MA/cm{sup 2}, the optimized GdBCO films show a better J{sub c}-B behavior and an improved high-field J{sub c}, compared to the YBCO films.

  14. Spray pyrolysis process for preparing superconductive films

    International Nuclear Information System (INIS)

    Hsu, H.M.; Yee, I.Y.

    1991-01-01

    This paper describes a spray pyrolysis method for preparing thin superconductive film. It comprises: preparing a spray pyrolysis solution comprising Bi,Sr,Ca and Cu metals in a solvent; heating a substrate to a first temperature; spraying the solution onto the heated substrate to form a film thereon; heating the film and substrate to a second temperature of about 700 degrees-825 degrees C, the second temperature being higher than the first temperature; heating the film and substrate to a third temperature of about 870 degrees-890 degrees C to melt the film; once the film and substrate reach the third temperature, further heat treating the film and substrate; cooling the film and substrate to ambient temperature. This patent also describes a spray pyrolysis method for preparing thin superconductive films. It comprises: preparing a spray pyrolysis solution comprising Bi, Ca and Cu metals and fluxing agent in a solvent; heating a substrate to a first temperature; spraying the solution onto the heated substrate to form a film thereon; heating the film and substrate to a second temperature about 700 degrees-825 degrees C, the second temperature being higher than the first temperature; heating the film and substrate at a third temperature about 840 degrees-860 degrees C; and cooling the film and substrate to ambient temperature

  15. X-ray diffractometry of 10 nm thick YBa2Cu3O7-x films

    International Nuclear Information System (INIS)

    Drozdov, Yu.N.; Moldavskaya, L.D.; Parafin, A.E.

    1998-01-01

    We report on some specific features of the X-ray diffraction spectra for ultrathin c-axis-oriented YBCO films. The films were prepared by laser deposition on LaAlO 3 substrates. A DRON-4 powder diffractometer was used to analyze a structure and to measure thickness of the films. We find that this conventional technique can detect the YBCO films as thin as 5 nm. The X-ray interference fringes in the vicinity of the (005) YBCO reflections for the films from 10 to 20 nm thick were clearly visible. The oscillation period of the fringes depends on the thickness of the film and the intensity modulation yields some structural information. The I(-1)/I(+1) fringes intensity ratio was found to be sensitive to the type of atomic layer at the top and bottom of YBCO film [ru

  16. Dependences of microstructure and critical current density on the thickness of YBa2Cu3O7-x film prepared by pulsed laser deposition on buffered Ni–W tape

    International Nuclear Information System (INIS)

    Xu, Da; Wang, Ying; Liu, Linfei; Li, Yijie

    2013-01-01

    YBa 2 Cu 3 O 7−x (YBCO) films with different thicknesses were fabricated on buffered Ni–W tapes by pulsed laser deposition. The thickness dependences of microstructure and critical current density (J c ) of YBCO film were systematically investigated. The microstructure and surface morphology of YBCO film were characterized by X-ray diffraction, optical microscopy, field emission scanning electron microscopy and atomic force microscopy. And the critical current (I c ) of YBCO film was measured by the conventional four-probe method. We found that the full width at half maximum values of both omega and phi scan rocking curves, the content of a-axis oriented grain, and surface roughness of YBCO film all increased with augmenting the thickness of YBCO film. It was also found that with increasing the thickness of YBCO film from 0.3 μm to 1.5 μm, the I c of YBCO film increased from 72 A/cm to 248 A/cm and yet J c of YBCO film decreased from 2.1 × 10 6 A/cm 2 to 1.6 × 10 6 A/cm 2 . Our results indicated that the microstructure and J c of YBCO film were largely dependent on the thickness of YBCO film under the optimized deposition condition of substrate temperature. - Highlights: ► YBa 2 Cu 3 O 7−x (YBCO) films with different thicknesses were grown on metallic tapes. ► The texture and critical current were dependent on the thickness of YBCO film. ► Thickness effect was weakened by fabricating YBCO film layer by layer

  17. Towards Isotropic Vortex Pinning in YBCO Films with Double-doping BHO-Y2O3 and BZO-Y2O3 Artificial Pining Centers

    Science.gov (United States)

    Gautam, Bibek; Sebastian, Mary Ann; Chen, Shihong; Haugan, Timothy; Chen, Yanbin; Xing, Zhongwen; Prestigiacomo, Joseph; Osofsky, Mike; Wu, Judy

    2017-12-01

    Strong and isotropic vortex pinning landscape is demanded for high field applications of YaBa2Cu3O7-x (YBCO) epitaxial thin films. Double-doping (DD) of artificial pinning centers (APCs) of mixed morphologies has been identified as a viable approach for this purpose. This work presents a comparative study on the transport critical current density J c (H, θ) of 3.0 vol.%Y2O3+2.0 (or 6.0) vol.% BaZrO3 (BZO DD) and 3.0 vol.%Y2O3+ 2.0 (or 6.0) vol.% BaHfO3 (BHO DD) films. Based on the elastic strain model, BaHfO3 (BHO) nanorods have lower rigidity than their BaZrO3 (BZO) counterparts, which means their c-axis alignment is more susceptible to the local strain generated by the secondary dopant of Y2O3. Considering the increasing strain field with higher BZO (or BHO doping), the higher susceptibility may result in a large portion of the BHO APCs moving away from perfect c-axis alignment and enhancing isotropic pinning with respect to the H orientation. This is confirmed since the BHO DD films illustrate a less pronounced J c peak at H//c-axis and hence more isotropic J c(θ) than their BZO DD counterparts. At 9.0 T, the variation of the J c across the entire θ range (0-90 degree) is less than 18% for the BHO DD film, in contrast to about 100% for the 2.0 vol.% BZO DD counterpart. At the higher BHO concentration of 6.0 vol.%, this higher tunability of the Y2O3 leads to increased ab-plane aligned BHO APCs and hence enhanced J c at H//ab-plane.

  18. Formation of nanoparticles and defects in YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} prepared by the metal organic deposition process

    Energy Technology Data Exchange (ETDEWEB)

    Goswami, R. [Naval Research Laboratory, Washington, DC 20375 (United States); SAIC, Washington, DC 20003 (United States)], E-mail: goswami@anvil.nrl.navy.mil; Holtz, R.L. [Naval Research Laboratory, Washington, DC 20375 (United States); Rupich, M.W. [American Superconductors Inc., Westborough, MA 01581 (United States); Spanos, G. [Naval Research Laboratory, Washington, DC 20375 (United States)

    2007-11-15

    Nanoparticles and defects have been investigated using transmission electron microscopy in fully reacted YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO), prepared by the metal-organic deposition (MOD) process. Two types of particles, Y{sub 2}O{sub 3} and CuY{sub 2}O{sub 5}, ranging from 10 to 100 nm, have been observed in the YBCO matrix. The YBCO contains a large number of planar defects and a considerable number of (1 1 0) rotational twins. Details of the nanoparticles and defects in the MOD-processed YBCO films are presented in this paper.

  19. Sequential Ar-O2 sputtering of Y2O3, BaF2, and CuO targets for preparation of Y-Ba-Cu-O superconducting films without wet-O2 annealing

    International Nuclear Information System (INIS)

    Bhushan, M.; Strauss, A.J.; Finn, M.C.

    1989-01-01

    Superconducting Y-Ba-Cu-O (YBCO) films have been prepared by ex situ O 2 annealing of multilayer films deposited on yttria-stabilized zirconia substrates by sequential rf diode sputtering of Y 2 O 3 , BaF 2 , and CuO targets, all of which are chemically stable. If sputtering is performed in an Ar ambient, the as-deposited films contain sufficient F to require its removal by annealing in wet O 2 at about 800 degree C or above before the superconducting YBCO phase can be formed by annealing in dry O 2 . However, sputtering in an Ar-O 2 ambient greatly reduces the F content, making it possible to obtain the superconducting phase by annealing in dry O 2 only. If the ambient contains about 20% O 2 , films with T c (R=0)>85 K can be prepared without wet-O 2 annealing. The Ar-O 2 process therefore has the potential for in situ preparation of superconducting YBCO films

  20. Preparation of YBa2Cu3O7-x superconducting solutions and films from alkoxide-based precursors using sol-gel method and investigation of their chemical reaction mechanisms

    International Nuclear Information System (INIS)

    Mutlu, Ibrahim Halil; Acun, Hediye; Celik, Erdal; Turkmen, Hasan

    2007-01-01

    In the development of coated superconductors sol-gel technique has been widely used as an effective processing method, especially in making long-length wires and tapes. However, one drawback associated with the deposition of YBa 2 Cu 3 O 7-x and Gd 2 O 3 buffer layer on Ni tape is the adhesion characteristic at interfaces YBCO-Gd 2 O 3 and Gd 2 O 3 -NiO and NiO-Ni substrate. In this paper, two strategies for adhesion enhancement of multilayered ceramic oxide coatings on Ni substrate were proposed: (1) formation of chemical bonds through surface condensation reactions, and development of ceramic networks through diffusion of alkoxide precursors. The current research has focused on the fabrication and adhesion of YBCO coatings on buffered Ni substrate using nine solutions prepared from Y, Ba and Cu alkoxides, solvent and chelating agent. Only two of YBCO solutions were successfully obtained while the rest of them were unsuccessful. Among these solutions we scrutinized chemical reaction mechanisms of a successful and an unsuccessful solution for comparison. How the chemical bonds and solubility were affected by the acids, base and solvents used in the solutions was demonstrated. It was shown that pH of the solution, homogeneity of the solution and gelation, steric affect of the chemicals in sol-gel solutions are significant issues to obtain high quality superconducting YBCO thin films. In addition, X-ray diffraction (XRD) was used to analyze phase structure of YBCO and compare results of chemical reactions obtained by a chemdraw programme. Scanning electron microscope (SEM) studies was carried out to examine microstructures of YBCO films produced from alkoxide precursors, solvent, chelating agent and modifying liquid chemical materials such as triethanolamine or ammonium hydroxide. It was found to be YBCO, Gd 2 O 3 , NiO and Ni phases in YBCO/Gd 2 O 3 /Ni sample from XRD analysis. That the solution prepared by using triethanolamine provided the best film quality and

  1. YBCO coated conductors by reactive thermal co-evaporation

    Energy Technology Data Exchange (ETDEWEB)

    Schmatz, U.; Hoffmann, Ch.; Bauer, M.; Metzger, R.; Berberich, P.; Kinder, H. [Technische Univ. Muenchen, Garching (Germany). Physik-Department

    2001-12-01

    Coated tape conductors of YBCO require a deposition process allowing to obtain a high volume growth rate in order to produce long lengths of tape in a reasonable amount of time. We present our tape coating system where 15 parallel loops of travelling tape of 1 cm width can be coated simultaneously by reactive thermal co-evaporation. For high critical current densities, in-plane alignment of the YBCO film is necessary. Inclined substrate deposition (ISD) is a technique that allows to deposit in-plane oriented buffer layers suitable for YBCO growth at high deposition rates. We present results obtained for YBCO films grown on MgO-ISD buffer layers deposited by e-gun evaporation onto metallic tape substrates. (orig.)

  2. Magnetostrictive thin films prepared by RF sputtering

    International Nuclear Information System (INIS)

    Carabias, I.; Martinez, A.; Garcia, M.A.; Pina, E.; Gonzalez, J.M.; Hernando, A.; Crespo, P.

    2005-01-01

    Fe 80 B 20 thin films have been prepared by ion beam sputtering magnetron on room temperature. The films were fabricated on different substrates to compare the different magnetic and structural properties. In particular the growth of films on flexible substrates (PDMS, Kapton) has been studied to allow a simple integration of the system in miniaturized magnetostrictive devices. X-ray diffraction patterns indicate that films are mainly amorphous although the presence of some Fe nanoparticles cannot be ruled out. The coercive field of thin films ranges between 15 and 35 Oe, depending on substrate. Magnetostriction measurements indicate the strong dependence of the saturation magnetostriction with the substrate. Samples on flexible substrates exhibit a better performance than samples deposited onto glass substrates

  3. Detection of second harmonic of phase dependence of superconducting current in Nb/Au/YBCO heterojunctions

    CERN Document Server

    Komissinskij, F V; Ilichev, E V; Ivanov, Z G

    2001-01-01

    The results of the experimental study on the current phase dependence (CPD) of the heterotransitions, consisting of the niobium and the YBa sub 2 Cu sub 3 O sub x (YBCO) film with an additional interlayer from gold (Nb/Au/YBCO) are presented. The CPD measurement is carried out through the radiofrequency superconducting quantum interferometer. The CPD second harmonic is determined in the Nb/Au/YBCO heterotransitions. Possible causes of its appearance are discussed within the frames of the d +- s combined symmetry of the YBCO order parameter. One of the causes of the CPD second harmonic appearance is the twinning of the YBCO films (001). The second cause of existing the anomalously high critical current consists in the availability of the Nb/Au boundary with the transparence of approx 10 sup - sup 1 in the Nb/Au/YBCO

  4. Critical current behaviour of YBCO thin films described by vortex pinning on low-angle domain boundaries and vortex creep

    International Nuclear Information System (INIS)

    Golovchanskiy, I.A.; Pan, A.V.; Fedoseev, S.A.; Shcherbakova, O.V.; Dou, S.X.

    2012-01-01

    A pinning potential for vortices was introduced assuming plastic pinning of vortex lattice on chains of out-of-plane individual edge dislocations that form low-angle domain boundaries in high quality YBa 2 Cu 3 O 7 thin films. Using this pinning potential with the classical Kim-Anderson vortex creep approach a model for critical current dependence on field has been successfully developed. The model shows a plausible description of J c (B a ) over the entire field range. Electrical field criterion is incorporated providing the ability to compare measurements made with different criteria (including different measurement techniques). Applicability of this model has been verified by experimental data obtained by direct transport and magnetisation measurements on high quality films grown by pulsed laser deposition. Pinning potential obtained from the fitting procedure is consistent with theoretical predictions. The model showed that the effective pinning landscape changes under influence of external conditions.

  5. Critical Current Properties in Longitudinal Magnetic Field of YBCO Superconductor with APC

    Science.gov (United States)

    Kido, R.; Kiuchi, M.; Otabe, E. S.; Matsushita, T.; Jha, A. K.; Matsumoto, K.

    The critical current density (Jc) properties of the Artificial Pinning Center (APC) introduced YBa2Cu3O7 (YBCO) films in the longitudinal magnetic field were measured. Y2O3 or Y2BaCuO5 (Y211) was introduced as APCs to YBCO, and YBCO films with APC were fabricated on SrTiO3 single crystal substrate. The sizes of Y2O3 and Y211 were 5-10 nm and 10-20 nm, respectively. As a result, Jc enhancement in the longitudinal magnetic field was observed in Y2O3 introduced YBCO films. However, it was not observed in Y211 introduced YBCO films. Therefore, it was considered that Jc properties in the longitudinal magnetic field were affected by introducing of small size APC, and it was necessary that APC does not disturb the current pathway in the superconductor.

  6. RBS and ion channeling studies of Ag-doped YBa2Cu3O7-δ targets and films

    International Nuclear Information System (INIS)

    Li Yupu; Liu, J.R.; Cui, X.T.; Chu, W.K.

    1998-01-01

    The location of Ag in Ag-doped YBa 2 Cu 3 O 7-δ (YBCO) films and other high-T c materials (such as Ag-doped BiSrCaCuO films and Ag-sheathed textured BiSrCaCuO wires) is a very important issue for improving high-T c materials. In this work, laser ablated and DC magnetron sputtered YBCO films on (100) LaAlO 3 and (100) SrTiO 3 were prepared from sintered Ag-YBCO composite targets (nominally containing 5 wt% Ag) and studied by Rutherford backscattering spectrometry (RBS) and ion channeling techniques using 2.0 MeV 4 He + and 7 Li + beams. We have found that the Ag-YBCO targets contain about 3 wt% Ag and most of the retained Ag atoms form some small size Ag precipitates with a typical size smaller than a few microns. We have demonstrated that in very good single crystalline YBCO films, the percentage of retained Ag in substitutional sites can be estimated by ion channeling technique. For example, we have found that about 1.2 wt% Ag atoms remain in the laser ablated Ag-doped films prepared from the Ag-YBCO target and about two-thirds of the retained Ag atoms occupy substitutional sites. The sputtered films contain less retained Ag atoms since the deposition temperature is higher and deposition time is longer than those for laser ablated films. (orig.)

  7. Thin films prepared from tungstate glass matrix

    Energy Technology Data Exchange (ETDEWEB)

    Montanari, B.; Ribeiro, S.J.L.; Messaddeq, Y. [Departamento de Quimica Geral e Inorganica, Instituto de Quimica, Sao Paulo State University-UNESP, CP 355, CEP 14800-900, Araraquara, SP (Brazil); Li, M.S. [Instituto de Fisica, USP, CP 369, CEP 13560-970, Sao Carlos, SP (Brazil); Poirier, G. [Departamento de Ciencias Exatas, UNIFAL-MG, CEP 37130-000, Alfenas-MG (Brazil)], E-mail: gael@unifal-mg.edu.br

    2008-01-30

    Vitreous samples containing high concentrations of WO{sub 3} (above 40% M) have been used as a target to prepare thin films. Such films were deposited using the electron beam evaporation method onto soda-lime glass substrates. These films were characterized by X-ray diffraction (XRD), perfilometry, X-ray energy dispersion spectroscopy (EDS), M-Lines and UV-vis absorption spectroscopy. In this work, experimental parameters were established to obtain stable thin films showing a chemical composition close to the glass precursor composition and with a high concentration of WO{sub 3}. These amorphous thin films of about 4 {mu}m in thickness exhibit a deep blue coloration but they can be bleached by thermal treatment near the glass transition temperature. Such bleached films show several guided modes in the visible region and have a high refractive index. Controlled crystallization was realized and thus it was possible to obtain WO{sub 3} microcrystals in the amorphous phase.

  8. Preparation and mechanical properties of edible rapeseed protein films.

    Science.gov (United States)

    Jang, Sung-Ae; Lim, Geum-Ok; Song, Kyung Bin

    2011-03-01

    Edible films were manufactured from rapeseed oil extraction residues. To prepare rapeseed protein (RP) films, various concentrations of plasticizers and emulsifiers were incorporated into the preparation of a film-forming solution. The optimal conditions for the preparation of the RP film were 2% sorbitol/0.5% sucrose as plasticizer and 1.5% polysorbate 20 as an emulsifier. In addition, RP blend films were prepared. Gelidium corneum or gelatin was added to improve the physical properties of the RP film, and the highest tensile strength value of the films was 53.45 MPa for the 3% RP/4% gelatin film. Our results suggest that the RP-gelatin blend film is suitable for applications in food packaging. Edible RP films prepared in the present investigation can be applied in food packaging.

  9. Thin film preparation of semiconducting iron pyrite

    Science.gov (United States)

    Smestad, Greg P.; Ennaoui, Ahmed; Fiechter, Sebastian; Hofmann, Wolfgang; Tributsch, Helmut; Kautek, Wolfgang

    1990-08-01

    Pyrite (Fe52) has been investigated as a promising new absorber material for thin film solar cell applications because of its high optical absorption coefficient of 1OL cm1, and its bandgap of 0.9 to 1.0 eV. Thin layers have been prepared by Metal Organic Chemical Vapor Deposition, MOCVD, Chemical Spray Pyrolysis, CSP, Chemical Vapor Transport, CVT, and Sulfurization of Iron Oxide films, 510. It is postulated that for the material FeS2, if x is not zero, a high point defect concentration results from replacing 2 dipoles by single S atoms. This causes the observed photovoltages and solar conversion efficiencies to be lower than expected. Using the Fe-O-S ternary phase diagram and the related activity plots, a thermodynamic understanding is formulated for the resulting composition of each of these types of films. It is found that by operating in the oxide portion of the phase diagram, the resulting oxidation state favors pyrite formation over FeS. By proper orientation of the grains relative to the film surface, and by control of pinholes and stoichiometry, an efficient thin film photovolatic solar cell material could be achieved.

  10. The growth of large-area superconducting YBa2Cu3O7-x thin films by pulsed laser ablation

    International Nuclear Information System (INIS)

    Lai, H.C.; Chang, C.M.; Lin, R.J.; Liu, R.S.

    1996-01-01

    In-situ growth of 2-in. diameter superconducting YBa 2 Cu 3 O 7-x (YBCO) thin films using an excimer KrF pulsed laser has been studied. Films with critical transition temperature (T c,0 ) of 89±1 K and critical current density (J c,77K ) in excess of 1 x 10 6 A cm -2 have been prepared routinely. Uniformity in film thickness of below ±15% and film composition of ±5% have been measured. The effects of gas nozzle geometry and target evolution during ablation on the superconducting properties and surface morphology of YBCO thin films have also been investigated. (orig.)

  11. Out-of-substrate plane orientation control of thin YBa2Cu3O x films on NdGaO3 tilted-axes substrates

    International Nuclear Information System (INIS)

    Mozhaev, Peter B.; Mozhaeva, Julia E.; Bdikin, Igor K.; Kotelyanskii, Iosif M.; Lusanov, Valery A.; Hansen, Jorn Bindslev; Jacobsen, Claus S.; Kholkin, Andrey L.

    2006-01-01

    Epitaxial heterostructures YBa 2 Cu 3 O x (YBCO)/CeO 2 /NdGaO 3 were prepared on tilted-axes NdGaO 3 substrates using laser ablation technique. Morphology, crystal structure and electrical properties of the obtained films were characterized. The seeding mechanisms are affected by the tilt angle, resulting in superior YBCO films on NdGaO 3 substrates in an intermediate range of tilt angles of 6-14 o . The introduction of CeO 2 layer leads to change of the YBCO film orientation: at low deposition rate c-oriented films are formed, while at high deposition rates the film grows with c-axis tilted along the [1 1 0] NdGaO 3 direction. Bi-epitaxial films and structures were prepared by removal of part of the CeO 2 layer using ion-beam milling

  12. Enhancement of critical current density of YBa2Cu3O7-δ thin films by nanoscale CeO2 pretreatment of substrate surfaces

    International Nuclear Information System (INIS)

    Cui, X.M.; Liu, G.Q.; Wang, J.; Huang, Z.C.; Zhao, Y.T.; Tao, B.W.; Li, Y.R.

    2007-01-01

    YBa 2 Cu 3 O 7-δ (YBCO) films were prepared on single-crystal SrTiO 3 substrates with metal-organic deposition using trifluoroacetates (TFA-MOD). Positive results have been acquired in controlled study to investigate the effects of substrate surface modification on the growth-induced flux-pinning nanostructures in YBCO films. Nanoscale CeO 2 particles were applied to single-crystal SrTiO 3 substrate surfaces using pulsed laser deposition before YBCO precursors coating. Superconducting properties of the YBCO films grown on the controlled CeO 2 -modified substrates have shown substantial improvement in the critical current densities (J c ) at 77 K over those grown on untreated substrates in almost all the field (78% increment at 1 T, 77 K). We think the reason is that the CeO 2 nanoparticles act as pinning centers

  13. Magnetooptical garnet films: preparation, characterisation, application

    International Nuclear Information System (INIS)

    Goernert, P.; Lorenz, A.; Lindner, M.; Richert, H.

    2007-01-01

    Full text: In contemporary magnetooptics both Kerr effect and Faraday effect are applied. The Kerr effect of metals and alloys - such as Fe, Ni, Co, FePt, CoPt, MnBi, PtMnSb - with thicknesses 300 μm are established as commercial isolators in optical systems and for developments of waveguide applications. Bi-REIG is prepared mostly by conventional liquid phase epitaxy (LPE) in PbO-B 2 O 3 -Bi 2 O 3 based solvents and sometimes by laser ablation and as nanocrystalline powders. In each case high Faraday rotation and low optical absorption is necessary. Additionally, magnetooptical sensors should possess high sensitivity and a large dynamic range. All these demands can be fulfilled with (REBi) 3 (FeGaAl) 5 O 12 LPE layers. Here we discuss some new results concerning preparation, characterisation, and application of Bi-TmIG and Bi-DyIG LPE layers on high-quality gadolinium gallium garnet (GGG) or lattice matched Ca-, Mg-, Zr-substituted GGG substrates. Optimization of flux melt composition and under cooling result in sensor films with a Faraday rotation of e.g. -1.2 0 /μm at a wavelength of l=590 nm and saturation induction of Bs=70 mT. Such films are already applied for forensic investigations. However, the responsivity of the garnet films is restricted by their coercivity Hc. Surface defects are found to give rise to pinned magnetic domains correlated with typical hysteresis. Obviously, Hc and the formation of pits are due to misfit stress and substrate surface quality. Besides, it is shown that an increase of working temperature leads to smaller coercivities. (authors)

  14. Enhanced flux pinning properties in superconducting YBa{sub 2}Cu{sub 3}O{sub 7−z} films by a novel chemical doping approach

    Energy Technology Data Exchange (ETDEWEB)

    Wang, W.T., E-mail: wtwang@swjtu.edu.cn [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Mail Stop 165, Chengdu, Sichuan 610031 (China); Pu, M.H.; Lei, M.; Zhang, H.; Wang, Z. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Mail Stop 165, Chengdu, Sichuan 610031 (China); Zhang, H. [Department of Physics, Peking University, Beijing 100871 (China); Cheng, C.H. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Mail Stop 165, Chengdu, Sichuan 610031 (China); Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia); Zhao, Y., E-mail: yzhao@swjtu.edu.cn [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Mail Stop 165, Chengdu, Sichuan 610031 (China); Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia)

    2013-10-15

    Highlights: • Pure and Co-doped YBCO films were prepared by newly-developed chemical method. • The doped films have much denser and smoother surface microstructures. • Significantly enhanced fux-pinning properties have been obtained for dilute Co-doped flm. -- Abstract: Pure and cobalt-doped superconducting YBa{sub 2}Cu{sub 3}O{sub 7−z} (YBCO) films were prepared on (0 0 l) LaAlO{sub 3} substrate by a newly developed polymer-assisted metal organic deposition method. The cobalt-doped YBCO films display much denser and smoother surface microstructures and the superconducting transition temperature T{sub c} spans a small range of 1.7 K with the doping levels. Significantly enhanced flux-pinning properties have been obtained for dilute cobalt-doped film. This may be attributed to the good grain connections and the effective flux pinning centers introduced by cobalt doping.

  15. Enhanced flux pinning properties in superconducting YBa2Cu3O7−z films by a novel chemical doping approach

    International Nuclear Information System (INIS)

    Wang, W.T.; Pu, M.H.; Lei, M.; Zhang, H.; Wang, Z.; Zhang, H.; Cheng, C.H.; Zhao, Y.

    2013-01-01

    Highlights: • Pure and Co-doped YBCO films were prepared by newly-developed chemical method. • The doped films have much denser and smoother surface microstructures. • Significantly enhanced fux-pinning properties have been obtained for dilute Co-doped flm. -- Abstract: Pure and cobalt-doped superconducting YBa 2 Cu 3 O 7−z (YBCO) films were prepared on (0 0 l) LaAlO 3 substrate by a newly developed polymer-assisted metal organic deposition method. The cobalt-doped YBCO films display much denser and smoother surface microstructures and the superconducting transition temperature T c spans a small range of 1.7 K with the doping levels. Significantly enhanced flux-pinning properties have been obtained for dilute cobalt-doped film. This may be attributed to the good grain connections and the effective flux pinning centers introduced by cobalt doping

  16. YBCO/manganite layered structures on NdGaO{sub 3} substrates

    Energy Technology Data Exchange (ETDEWEB)

    Nurgaliev, T [Institute of Electronics BAS, 72 Tsarigradsko Chaussee, 1784 Sofia (Bulgaria); Blagoev, B [Institute of Electronics BAS, 72 Tsarigradsko Chaussee, 1784 Sofia (Bulgaria); Donchev, T [Institute of Electronics BAS, 72 Tsarigradsko Chaussee, 1784 Sofia (Bulgaria); Miteva, S [Institute of Electronics BAS, 72 Tsarigradsko Chaussee, 1784 Sofia (Bulgaria); Mozhaev, P B [Institute of Physics and Technology RAS, Nakhimovsky ave. 36, 117218 Moscow (Russian Federation); Mozhaeva, J E [Institute of Physics and Technology RAS, Nakhimovsky ave. 36, 117218 Moscow (Russian Federation); Ovsyannikov, G A [Institute of Radio Engineering and Electronics RAS, Mokhovaya st.11, 103907 Moscow (Russian Federation); Kotelyanskii, I M [Institute of Radio Engineering and Electronics RAS, Mokhovaya st.11, 103907 Moscow (Russian Federation); Jacobsen, C [Technical University of Denmark, Building 307-309, DK-2800, Kgs.Lyngby, Denmark (Denmark)

    2006-06-01

    Results of deposition of YBa{sub 2}Cu{sub 3}O{sub 7-x}/CeO{sub 2}/(La{sub 0.7}Ca{sub 0.3}MnO{sub 3} or La{sub 0.7}Sr{sub 0.3}MnO{sub 3}) structures on the standard oriented and tilted ( 8{sup 0}) NdGaO{sub 3} substrates and results of investigation of electrical parameters of YBa{sub 2}Cu{sub 3}O{sub 7-x} (YBCO) films in such structures are presented. The YBCO component of the structure exhibits lower value of the critical parameters in comparison with those of single YBCO films. The contribution of the magnetic layer to the microwave losses of the YBCO film in the layered structure is evaluated.

  17. YBCO/manganite layered structures on NdGaO3 substrates

    International Nuclear Information System (INIS)

    Nurgaliev, T; Blagoev, B; Donchev, T; Miteva, S; Mozhaev, P B; Mozhaeva, J E; Ovsyannikov, G A; Kotelyanskii, I M; Jacobsen, C

    2006-01-01

    Results of deposition of YBa 2 Cu 3 O 7-x /CeO 2 /(La 0.7 Ca 0.3 MnO 3 or La 0.7 Sr 0.3 MnO 3 ) structures on the standard oriented and tilted ( 8 0 ) NdGaO 3 substrates and results of investigation of electrical parameters of YBa 2 Cu 3 O 7-x (YBCO) films in such structures are presented. The YBCO component of the structure exhibits lower value of the critical parameters in comparison with those of single YBCO films. The contribution of the magnetic layer to the microwave losses of the YBCO film in the layered structure is evaluated

  18. Microstructure and transport current characterization of YBa2Cu3O7-x thick films prepared by modified solid-liquid melt growth and powder melt process routes

    International Nuclear Information System (INIS)

    Langhorn, J.; McGinn, P.J.

    1999-01-01

    From the characterization of superconducting YBa 2 Cu 3 O 7-x (YBCO) thick films processed by melt texturing on yttria-stabilized zirconia substrates from YBCO precursors it is clear that the properties are highly dependent on the precursor powder. Increased YBCO grain sizes have been induced in thick films processed from by modified solid-liquid melt growth (SLMG) and powder melt (PMP) processes with respect to those processed from pre-reacted YBCO materials. The SLMG and PMP routes utilize precursors consisting of BaCuO 2 -CuO flux material mixed with Y 2 O 3 and Y 2 BaCuO 5 respectively. Cross-sectional analysis of films textured by these routes shows a decreased Y 2 BaCuO 5 size and an increased homogeneity within the matrix with respect to films processed from YBCO powder. Such microstructural improvements lead to an improvement of both the flux pinning and current-carrying characteristics of the processed YBCO films. (author)

  19. Electrochemical and Thermal Studies of Prepared Conducting Chitosan Biopolymer Film

    International Nuclear Information System (INIS)

    Hlaing Hlaing Oo; Kyaw Naing; Kyaw Myo Naing; Tin Tin Aye; Nyunt Wynn

    2005-09-01

    In this paper, chitosan based conducting bipolymer films were prepared by casting and solvent evaporating technique. All prepared chitosan films were of pale yellow colour, transparent, and smooth. Sulphuric acid was chosen as the cross-linking agent. It enhanced conduction pathway in cross-linked chitosan films. Mechanical properties, solid-state, and thermal behavior of prepared chitosan fimls were studied by means of a material testing machine, powder X-ray diffractometry (XRD), thermogravimetric analysis (TG-DTG), and differential scanning calorimetry (DSC). By the XRD diffraction pattern, high molecular weight of chitosan product indicates the semi-crystalline nature, but the prepared chitosan film and doped chitosan film indicate significantly lower in crystallinity prove which of the amorphous characteristics. In addition, DSC thermogram of pure chitosan film exhibited exothermic peak around at 300 C, indicating polymer decomposition of chitosan molecules in chitosan films. Furthermore, these DSC thermograms clearly showed that while pure chitosan film display exothermal decomposition, the doped chitosan films mainly endothermic characteristics. The ionic conductivity of doped chitosan films were in the order of 10 to 10 S cm , which is in the range of semi-conductor. These results showed that cross-linked chitoson films may be used as polymer electrolyte film to fabricate solid state electrochemical cells

  20. Preparation of self-supporting thin metal target films

    International Nuclear Information System (INIS)

    Wang Xiuying; Ge Suxian; Yin Jianhua; Yin Xu; Jin Genming

    1989-01-01

    The preparation method and equipment for thin metal self-supporting target without oil contamination are described. The influence of target films contaminated by oil vapor on accuracy of nuclear-physics experimental data are also discussed. The analytical results on carbon content in the prepared films of three elements show that the equipment is very effective for eliminating contamination

  1. Preparation and characterization of vanadium oxide thin films

    Energy Technology Data Exchange (ETDEWEB)

    Monfort, O.; Plesch, G. [Comenius University of Bratislava, Faculty of Natural Sciences, Department of Inorganic Chemistry, 84215 Bratislava (Slovakia); Roch, T. [Comenius University of Bratislava, Faculty of Mathematics Physics and Informatics, Department of Experimental Physics, 84248 Bratislava (Slovakia)

    2013-04-16

    The thermotropic VO{sub 2} films have many applications, since they exhibit semiconductor-conductor switching properties at temperature around 70 grad C. Vanadium oxide thin films were prepared via sol-gel method. Spin coater was used to depose these films on Si/SiO{sub 2} and lime glass substrates. Thin films of V{sub 2}O{sub 5} can be reduced to metastable VO{sub 2} thin films at the temperature of 450 grad C under the pressure of 10{sup -2} Pa. These films are then converted to thermotropic VO{sub 2} at 700 grad C in argon under normal pressure. (authors)

  2. Silk fibroin/pullulan blend films: Preparation and characterization

    Energy Technology Data Exchange (ETDEWEB)

    Shivananda, C. S.; Rao, B. Lakshmeesha; Madhukumar, R.; Asha, S. [Department of Studies in Physics, Mangalore University, Mangalagangotri – 574 199 (India); Sarojini, B. K. [Department of Industrial Chemistry, Mangalore University, Mangalagangotri, Mangalore –574 199 (India); Somashekhar, R. [Department of Studies in Physics, University of Mysore, Manasagangotri, Mysore – 570 006 (India); Sangappa, Y., E-mail: syhalabhavi@yahoo.co.in [Department of Studies in Physics, Mangalore University, Mangalagangotri – 574 199 (India); School of Material Science and Engineering, Georgia Institute of Technology, Atlanta, GA 30332 (United States)

    2016-05-23

    In this work silk fibroin/pullulan blend films have been prepared by solution casting method. The blend films were examined for structural, and thermal properties using X-ray diffraction (XRD), thermogravimatric (TGA) and differential scanning calorimetry (DSC) analysis. The XRD results indicate that with the introduction of pullulan, the interaction between SF and pullulan in the blend films induced the conformation transition of SF films and amorphous phase increases with increasing pullulan ratio. The thermal properties of the blend films were improved significantly in the blend films.

  3. Overgrowth of cracks in YBa{sub 2}Cu{sub 3}O{sub 6+δ}-thin films grown on SrTiO{sub 3}- and Al{sub 2}O{sub 3}-substrates

    Energy Technology Data Exchange (ETDEWEB)

    Ackermann, Kai; Haenisch, Jens; Holzapfel, Bernhard [Institut fuer Technische Physik, Karlsruher Institut fuer Technologie, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany)

    2016-07-01

    High temperature superconducting materials like REBCO-thin films offer a wide range of applications like superconducting transformers, cables, coils or fault current limiters. Although the number of applications is increasing the REBCO-coated conductor length is still limited due to substrate and thin film fabrication defects. In order to improve the manufacturing processes of REBCO-coated conductors the growth behavior of REBCO-thin films on defective or broken substrate surfaces has to be understood. Therefore we investigated the structural and electronic properties of YBCO-thin films grown on cracked SrTiO{sub 3}- and Al{sub 2}O{sub 3}-substrates. The YBCO-films were prepared by using metalorganic (MOD) and pulsed laser deposition (PLD). Structural and electronic properties of the YBCO-films were investigated by using x-ray diffractometry, atomic force microscopy, scanning electron microscopy and temperature- and magnetic field-dependent conductivity measurements.

  4. Structure/Property Relationships for Sol-gel Derived YBa2Cu3O7-d and SrTiO3 Films

    Science.gov (United States)

    Dawley, Jeff; Clem, Paul; Siegal, Michael; Overmyer, Don

    2001-03-01

    Solution deposition of c-axis oriented YBa2Cu3O7-d (YBCO) films on buffered RABiT substrates is a potential method for rapid, low cost production of superconducting tapes for power transmission and other applications. For this work, 100-250 nm thick YBCO and SrTiO3 (STO) films have been prepared by spin-coating and dip-coating sol-gel solutions onto LaAlO3 (100) and RABiT Ni (200) substrates. Biaxially textured STO coatings have been deposited on LaAlO3 and RABiT Ni by using a "templating" technique and controlling growth temperature and pO2. YBCO films grown on STO coated LaAlO3 possess comparable superconducting properties to YBCO films grown directly on LaAlO3 ( 1 MA/cm2 at 77K), indicating that a high quality STO layer does not degrade the crystalline quality of the YBCO. The effects of processing parameters on the STO buffer layer and novel processing techniques for decreasing the processing time and simplifying the integration of sol-gel YBCO with Ni substrates will be discussed. Sandia is a multiprogram laboratory operated by Sandia Corp., a Lockheed Martin Company, for the US Dept. Of Energy under contract DE-AC04-94A185000.

  5. Pd-Ni-MWCNT nanocomposite thin films: preparation and structure

    Science.gov (United States)

    Kozłowski, Mirosław; Czerwosz, ElŻbieta; Sobczak, Kamil

    2017-08-01

    The properties of nanocomposite palladium-nickel-multi-walled (Pd-Ni-MWCNT) films deposited on aluminum oxide (Al2O3) substrate have been prepared and investigated. These films were obtained by 3 step process consisted of PVD/CVD/PVD methods. The morphology and structure of the obtained films were characterized by Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM) techniques at various stages of the film formation. EDX spectrometer was used to measurements of elements segregation in the obtained film. TEM and STEM (Scanning Transmission Electron Microscopy) observations showed MWCNTs decorated with palladium nanoparticles in the film obtained in the last step of film formation (final PVD process). The average size of the palladium nanoparticles observed both on MWCNTs and carbonaceous matrix does not exceed 5 nm. The research was conducted on the use of the obtained films as potential sensors of gases (e.g. H2, NH3, CO2) and bio-sensors or optical sensors.

  6. Preparation and properties of antimony thin film anode materials

    Institute of Scientific and Technical Information of China (English)

    SU Shufa; CAO Gaoshao; ZHAO Xinbing

    2004-01-01

    Metallic antimony thin films were deposited by magnetron sputtering and electrodeposition. Electrochemical properties of the thin film as anode materials for lithium-ion batteries were investigated and compared with those of antimony powder. It was found that both magnetron sputtering and electrodeposition are easily controllable processes to deposit antimony films with fiat charge/discharge potential plateaus. The electrochemical performances of antimony thin films, especially those prepared with magnetron sputtering, are better than those of antimony powder. The reversible capacities of the magnetron sputtered antimony thin film are above 400 mA h g-1 in the first 15 cycles.

  7. Untangling surface oxygen exchange effects in YBa2Cu3O6+x thin films by electrical conductivity relaxation.

    Science.gov (United States)

    Cayado, P; Sánchez-Valdés, C F; Stangl, A; Coll, M; Roura, P; Palau, A; Puig, T; Obradors, X

    2017-05-31

    The kinetics of oxygen incorporation (in-diffusion process) and excorporation (out-diffusion process), in YBa 2 Cu 3 O 6+x (YBCO) epitaxial thin films prepared using the chemical solution deposition (CSD) methodology by the trifluoroacetate route, was investigated by electrical conductivity relaxation measurements. We show that the oxygenation kinetics of YBCO films is limited by the surface exchange process of oxygen molecules prior to bulk diffusion into the films. The analysis of the temperature and oxygen partial pressure influence on the oxygenation kinetics has drawn a consistent picture of the oxygen surface exchange process enabling us to define the most likely rate determining step. We have also established a strategy to accelerate the oxygenation kinetics at low temperatures based on the catalytic influence of Ag coatings thus allowing us to decrease the oxygenation temperature in the YBCO thin films.

  8. Preparation of Modified Films with Protein from Grouper Fish

    Science.gov (United States)

    Tecante, A.; Granados-Navarrete, S.; Martínez-García, C.

    2016-01-01

    A protein concentrate (PC) was obtained from Grouper fish skin and it was used to prepare films with different amounts of sorbitol and glycerol as plasticizers. The best performing films regarding resistance were then modified with various concentrations of CaCl2, CaSO4 (calcium salts), and glucono-δ-lactone (GDL) with the purpose of improving their mechanical and barrier properties. These films were characterized by determining their mechanical properties and permeability to water vapor and oxygen. Formulations with 5% (w/v) protein and 75% sorbitol and 4% (w/v) protein with a mixture of 15% glycerol and 15% sorbitol produced adequate films. Calcium salts and GDL increased the tensile fracture stress but reduced the fracture strain and decreased water vapor permeability compared with control films. The films prepared represent an attractive alternative for being used as food packaging materials. PMID:27597950

  9. Preparation of Modified Films with Protein from Grouper Fish

    Directory of Open Access Journals (Sweden)

    M. A. Valdivia-López

    2016-01-01

    Full Text Available A protein concentrate (PC was obtained from Grouper fish skin and it was used to prepare films with different amounts of sorbitol and glycerol as plasticizers. The best performing films regarding resistance were then modified with various concentrations of CaCl2, CaSO4 (calcium salts, and glucono-δ-lactone (GDL with the purpose of improving their mechanical and barrier properties. These films were characterized by determining their mechanical properties and permeability to water vapor and oxygen. Formulations with 5% (w/v protein and 75% sorbitol and 4% (w/v protein with a mixture of 15% glycerol and 15% sorbitol produced adequate films. Calcium salts and GDL increased the tensile fracture stress but reduced the fracture strain and decreased water vapor permeability compared with control films. The films prepared represent an attractive alternative for being used as food packaging materials.

  10. Preparation and Characterization of High Temperature Superconductor Film Surfaces

    Science.gov (United States)

    1993-10-27

    Lanthanum Strontium Copper Oxide (LSCO) was also tested as a normal metal overlayer because of its compatibility with the high deposition temperature for...fabricate YBCO/ISCO SEB junctions using a variety of step heights (110 nm - 330 nm) on Neodymium Gallate (NGO) substrates. NGO was chosen as a...substrate because of its excellent lattice match to YBCO and its lack of crystal twinning Twinning had been a drawback of Lanthanum Aluminate (LAO)- L

  11. Preparation and Evaluation of Buccal Bioadhesive Films Containing Clotrimazole

    OpenAIRE

    Singh, S.; Jain, S.; Muthu, M. S.; Tiwari, S.; Tilak, R.

    2008-01-01

    Buccal bioadhesive films, releasing topical drugs in the oral cavity at a slow and predetermined rate, provide distinct advantages over traditional dosage forms. The aim of present study was to prepare and evaluate buccal bioadhesive films of clotrimazole for oral candidiasis. The film was designed to release the drug at a concentration above the minimum inhibitory concentration for a prolonged period of time so as to reduce the frequency of administration of the available conventional dosage...

  12. Preparation and characterization of gelatin/cerium(Ⅲ) film

    Institute of Scientific and Technical Information of China (English)

    黄崇军; 黄雅钦; 田娜; 童元建; 殷瑞贤

    2010-01-01

    A novel gelatin film with antibacterial activity was prepared by electrostatic crosslinking using cerium (Ⅲ) nitrate hexahydrate as the crosslinking agent. The structure and properties of the films were investigated by Fourier transform infrared spectra, tensile tests, thermogravimetric analysis, static drop contact angle and disc diffusion method. The results showed that cross-linking could not only improve the thermal and mechanical properties and lower the hydrophilic property of the films, but also make...

  13. Preparation of Nb thin films with bulk transition temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Peirce, L H [Florida State Univ., Tallahassee (USA). Dept. of Physics

    1984-08-01

    Thin films (1000-2000 A) of Nb were prepared with bulk transition temperatures (9.25 K) by evaporation from an electron gun. Necessary substrate temperatures, evaporation rates and H/sub 2/O pressures were determined.

  14. Development of YBCO Superconductor for Electric Systems: Cooperative Research and Development Final Report, CRADA Number CRD-04-150

    Energy Technology Data Exchange (ETDEWEB)

    Bhattacharya, R.

    2013-03-01

    The proposed project will be collaborative in exploration of high temperature superconductor oxide films between SuperPower, Inc. and the National Renewable Energy Laboratory. This CRADA will attempt to develop YBCO based high temperature oxide technology.

  15. PBCO/YBCO bilayer growth and optimization for the fabrication of buffered step-edge Josephson junctions

    CSIR Research Space (South Africa)

    Van Staden, WF

    2009-04-01

    Full Text Available Bilayers of PBCO and YBCO are grown epitaxially on MgO substrates using PLD. In this paper, researchers discuss the entire optimization process in detail, giving quantitative parameter values. Film characterization included XRD, AFM and susceptance...

  16. Nanocomposite film prepared by depositing xylan on cellulose nanowhiskers matrix

    Science.gov (United States)

    Qining Sun; Anurag Mandalika; Thomas Elder; Sandeep S. Nair; Xianzhi Meng; Fang Huang; Art J. Ragauskas

    2014-01-01

    Novel bionanocomposite films have been prepared by depositing xylan onto cellulose nanowhiskers through a pH adjustment. Analysis of strength properties, water vapour transmission, transparency, surface morphology and thermal decomposition showed the enhancement of film performance. This provides a new green route to the utilization of biomass for sustainable...

  17. Preparation and evaluation of buccal bioadhesive films containing clotrimazole.

    Science.gov (United States)

    Singh, S; Jain, S; Muthu, M S; Tiwari, S; Tilak, R

    2008-01-01

    Buccal bioadhesive films, releasing topical drugs in the oral cavity at a slow and predetermined rate, provide distinct advantages over traditional dosage forms. The aim of present study was to prepare and evaluate buccal bioadhesive films of clotrimazole for oral candidiasis. The film was designed to release the drug at a concentration above the minimum inhibitory concentration for a prolonged period of time so as to reduce the frequency of administration of the available conventional dosage forms. The different proportions of sodium carboxymethylcellulose and carbopol 974P (CP 974P) were used for the preparation of films. Carbopol was used to incorporate the desired bioadhesiveness in the films. The films were prepared by solvent casting method and evaluated for bioadhesion, in vitro drug release and effectiveness against Candida albicans. In vitro drug release from the film was determined using a modified Franz diffusion cell while bioadhesiveness was evaluated with a modified two-arm balance using rabbit intestinal mucosa as a model tissue. Films containing 5% CP 974P of the total polymer were found to be the best with moderate swelling along with favorable bioadhesion force, residence time and in vitro drug release. The microbiological studies revealed that drug released from the film could inhibit the growth of C. albicans for 6 h. The drug release mechanism was found to follow non-Fickian diffusion.

  18. Preparation and performance of Ecobras/bentonite biodegrading films

    International Nuclear Information System (INIS)

    Costa, Ana Nery M.; Melo, Nadja M.C.; Canedo, Eduardo L.; Carvalho, Laura H.; Araujo, Arthur R.A.

    2011-01-01

    Compounds based on the biodegradable polymer Ecobras and bentonite clay in its pristine, sonicated, and organically modified with a quaternary ammonium salt forms were prepared as flat films. Clays and compounds were characterized by x-ray diffraction and scanning electron microscopy. Mechanical properties of the films were determined according to pertinent ASTM standards. Reasonable properties, higher than those of the matrix, were obtained with compounds prepared with purified clays and organoclays, particularly for low clay loading. (author)

  19. Novel transparent and flexible nanocomposite film prepared from chrysotile nanofibres

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Kun, E-mail: kliu@csu.edu.cn [School of Minerals Processing and Bioengineering, Central South University, Changsha 410083 (China); Zhu, Binnan; Feng, Qiming [School of Minerals Processing and Bioengineering, Central South University, Changsha 410083 (China); Duan, Tao [Joint Laboratory for Extreme Conditions Matter Properties, Southwest University of Science and Technology and Research Center of Laser Fusion, CAEP, Mianyang 621010 (China)

    2013-10-01

    In the present study, chrysotile nanofibres, obtained from physicochemical dispersion of natural chrysotile, were used to prepare nanofibre sheets by vacuum filtration. As-prepared sheets were then impregnated by UV-curable resin and cured by ultraviolet light to fabricate the flexible and transparent nanocomposite films. Observed from SEM, the transparent films showed a smooth surface and a typical sandwich structure in cross section, viz. nanofibre sheet filled with resin was sandwiched by two layers of resin. XRD patterns indicated the amorphous nature of cured resin and characteristic crystallographic structure of chrysotile in nanocomposite films. Though the nanofibre sheets were white in colour, and nanofibre contents in nanocomposites were as much as 43.4 wt%, the nanocomposite films displayed an excellent optical transparency with about 85% light transmittance in the visible light range. Tensile tests showed that the addition of nanofibres resulted in a great improvement in mechanical strength of the nanocomposite films; with the increase of nanofibre contents, the modulus and tensile strength of nanocomposite films increased gradually. - Graphical abstract: Photos show the experimental phenomenon. The white nanofibre sheets can be written or printed like paper, and it's very interested that the handwriting is clearly visible from the front and back of the transparent films prepared from nanofibre sheets by vacuum impregnation and UV curing. This phenomenon can be attributed to the increase of transparency of film, which results from the replacement of air interstices in nanofibre sheet by resin with higher refractive index. Visible light can pass easily through the transparent film without obvious loss, but can be apparently adsorbed and scattered by ink particles that adhered to nanofibres and embedded in resin. - Highlights: • A flexible and transparent film is prepared from chrysotile nanofibres. • The nanofibre sheet is sandwiched by two

  20. Novel transparent and flexible nanocomposite film prepared from chrysotile nanofibres

    International Nuclear Information System (INIS)

    Liu, Kun; Zhu, Binnan; Feng, Qiming; Duan, Tao

    2013-01-01

    In the present study, chrysotile nanofibres, obtained from physicochemical dispersion of natural chrysotile, were used to prepare nanofibre sheets by vacuum filtration. As-prepared sheets were then impregnated by UV-curable resin and cured by ultraviolet light to fabricate the flexible and transparent nanocomposite films. Observed from SEM, the transparent films showed a smooth surface and a typical sandwich structure in cross section, viz. nanofibre sheet filled with resin was sandwiched by two layers of resin. XRD patterns indicated the amorphous nature of cured resin and characteristic crystallographic structure of chrysotile in nanocomposite films. Though the nanofibre sheets were white in colour, and nanofibre contents in nanocomposites were as much as 43.4 wt%, the nanocomposite films displayed an excellent optical transparency with about 85% light transmittance in the visible light range. Tensile tests showed that the addition of nanofibres resulted in a great improvement in mechanical strength of the nanocomposite films; with the increase of nanofibre contents, the modulus and tensile strength of nanocomposite films increased gradually. - Graphical abstract: Photos show the experimental phenomenon. The white nanofibre sheets can be written or printed like paper, and it's very interested that the handwriting is clearly visible from the front and back of the transparent films prepared from nanofibre sheets by vacuum impregnation and UV curing. This phenomenon can be attributed to the increase of transparency of film, which results from the replacement of air interstices in nanofibre sheet by resin with higher refractive index. Visible light can pass easily through the transparent film without obvious loss, but can be apparently adsorbed and scattered by ink particles that adhered to nanofibres and embedded in resin. - Highlights: • A flexible and transparent film is prepared from chrysotile nanofibres. • The nanofibre sheet is sandwiched by two

  1. Surface preparation for the heteroepitactic growth of ceramic thin films

    International Nuclear Information System (INIS)

    Norton, M.G.; Summerfelt, S.R.; Carter, C.B.

    1990-01-01

    The morphology, composition, and crystallographic orientation of the substrate influence the nucleation and growth of deposited thin films. A method for the preparation of controlled, characteristic surfaces is reported. The surfaces are suitable for the heteroepitactic growth of thin films. When used in the formation of electron-transparent thin foils, the substrates can be used to investigate the very early stages of film growth using transmission electron microscopy. The substrate preparation involves the cleaning and subsequent annealing to generate a surface consisting of a series of steps. The step terraces are formed on the energetically stable surface, and controlled nucleation and growth of films at step edges is found. The substrate materials prepared using this technique include (001) MgO, (001) SrTiO 3 , and (001) LaAlO 3

  2. Barium titanate thick films prepared by screen printing technique

    Directory of Open Access Journals (Sweden)

    Mirjana M. Vijatović

    2010-06-01

    Full Text Available The barium titanate (BaTiO3 thick films were prepared by screen printing technique using powders obtained by soft chemical route, modified Pechini process. Three different barium titanate powders were prepared: i pure, ii doped with lanthanum and iii doped with antimony. Pastes for screen printing were prepared using previously obtained powders. The thick films were deposited onto Al2O3 substrates and fired at 850°C together with electrode material (silver/palladium in the moving belt furnace in the air atmosphere. Measurements of thickness and roughness of barium titanate thick films were performed. The electrical properties of thick films such as dielectric constant, dielectric losses, Curie temperature, hysteresis loop were reported. The influence of different factors on electrical properties values was analyzed.

  3. NdFeB thick films prepared by tape casting

    International Nuclear Information System (INIS)

    Pawlowski, B.; Schwarzer, S.; Rahmig, A.; Toepfer, J.

    2003-01-01

    NdFeB films of thickness between 100 and 800 μm were prepared by tape casting of a slurry containing 84-95 wt% of commercial NdFeB powder (MQP-B, -Q and -S). After curing the flexible green tapes at 120 deg. C non-porous magnetic films are obtained. The remanence of the films is in the range of 350-450 mT and the coercivity is between 300 and 800 kA/m depending on the type of MQP powder used. The magnetic properties of the films are discussed in relation to film composition and type of magnetic material. For MEMS applications the thick films are magnetized with a multi-pole stripe pattern with 1 mm pole pitch. The induction at the surface of the films was measured with a Hall probe and compared to theoretical calculations. The results indicate that the films are completely magnetized regardless of the film thickness. Tape-casted NdFeB thick films are promising candidates for applications in micro-systems or actuators. Miniaturization of the magnet components is one of the key issues in the development of electromagnetic micro-systems, thus creating a need for replacement of small sintered magnets by magnetic thick film components. Other applications include encoders

  4. Commissioning a hobby cutting device for radiochromic film preparation.

    Science.gov (United States)

    Zolfaghari, Somayeh; Francis, Kirby E; Kairn, Tanya; Crowe, Scott B

    2017-06-01

    In addition to a high spatial resolution and well characterised dose response, one of the major advantages of radiochromic film as a dosimeter is that sheets of film can be cut into pieces suitable for use as calibration films, and for in vivo and phantom measurements. The cutting of film is typically done using scissors or a guillotine, and this process can be time-consuming, limited in precision, requires extensive handling and does not allow holes to be cut from the film without cutting from an existing edge. This study investigated the use of a Brother ScanNCut hobby cutting system for EBT3 film preparation. The optimal operating parameters (blade size, pressure, speed) that resulted in precise cuts with minimal delamination at cut edges were identified using test cutting patterns. These parameters were then used to cut a large film insert for a stereotactic head phantom for comparison against an insert cut with scissors. While the hobby cutting system caused a wider region of delamination at the film edge (1.8 mm) compared to scissors (1 mm), the hobby cutting system was found to be able to produce reproducible cuts more efficiently and more accurately than scissors. The use of the hobby cutting system is recommended for complex phantom inserts (containing sharp corners or holes for alignment rods) or in situations where large numbers of film pieces need to be prepared.

  5. Microstructure and properties of manganese dioxide films prepared by electrodeposition

    International Nuclear Information System (INIS)

    Jacob, G. Moses; Zhitomirsky, I.

    2008-01-01

    Nanostructured manganese dioxide films were obtained by galvanostatic, pulse and reverse pulse electrodeposition from 0.01 to 0.1 M KMnO 4 solutions. The deposition yield was investigated by in situ monitoring the deposit mass using a quartz crystal microbalance (QCM). Obtained films were studied by electron microscopy, X-ray diffraction analysis, energy dispersive spectroscopy, thermogravimetric and differential thermal analysis. The QCM and electron microscopy data were utilized for the investigation of deposition kinetics and film formation mechanism. It was shown that the deposition rate and film microstructure could be changed by variation of deposition conditions. The method allowed the fabrication of dense or porous films. The thickness of dense films was limited to ∼0.1 μm due to the insulating properties of manganese dioxide and film cracking, attributed to drying shrinkage. Porous and crack-free 1-2 μm films were obtained using galvanostatic or reverse pulse deposition from 0.02 M KMnO 4 solutions. It was shown that film porosity is beneficial for the charge transfer during deposition and crack prevention in thick films. Moreover, porous nanostructured films showed good capacitive behavior for applications in electrochemical supercapacitors. The porous nanostructured films prepared in the reverse pulse regime showed higher specific capacitance (SC) compared to the SC of the galvanostatic films. The highest SC of 279 F/g in a voltage window of 1 V was obtained in 0.1 M Na 2 SO 4 solutions at a scan rate of 2 mV/s

  6. AC over-current characteristics of YBCO coated conductor with copper stabilizer layer considering insulation layer

    International Nuclear Information System (INIS)

    Du, H.-I.; Kim, M.-J.; Kim, Y.-J.; Lee, D.-H.; Han, B.-S.; Song, S.-S.

    2010-01-01

    Compared with the first-generation BSCCO wire, the YBCO thin-film wire boasts low material costs and high J c and superior magnetic-field properties, among other strengths. Meanwhile, the previous BSCCO wire material for superconducting cables has been researched on considerably with regard to its post-wire quenching characteristics during the application of an alternating over-current. In this regard, the promising YBCO thin-film wire has yet to be further researched on. Moreover, still lacking is research on the YBCO thin-film wire with insulating layers, which is essential in the manufacture of superconducting cables, along with the testing of the application of an alternating over-current to the wire. In this study, YBCO thin-film wires with copper-stabilizing layers were used in testing alternating over-current application according to the presence or absence of insulating layers and to the thickness of such layers, to examine the post-quenching wire resistance increase and quenching trends. The YBCO thin-film wire with copper-stabilizing layers has a critical temperature of 90 K and a critical current of 85 A rms . Moreover, its current application cycle is 5.5 cycles, and its applied currents are 354, 517, 712, and 915 A peak . These figures enabled the YBCO thin-film wires with copper-stabilizing layers to reach 90, 180, 250, and 300 K, respectively, in this study. These temperatures serve as a relative reference to examine the post-quenching wire properties following the application of an alternating over-current.

  7. Preparation and properties of low resistivity molybdenum silicide thin films

    International Nuclear Information System (INIS)

    Beddies, G.; Hofmann, K.; Bretschneider, W.; Zscheile, H.D.; Bogdanowa, P.; Helms, H.; Wickleder, K.H.

    1983-01-01

    Using different sputtering methods and target variants Mo/Si mixed films are prepared. After the deposition these thin films are amorphous. Isothermal annealing in vacuum leads to the formation of crystalline phases. The crystallization of the hexagonal phase of MoSi 2 is connected with an increase in stress. The formation of the tetragonal phase causes a great decrease of the specific resistance

  8. Microstructure imaging of the YBCO thin film/MgO substrate interface: HRTEM and Fourier analysis of the Moire fringe pattern

    International Nuclear Information System (INIS)

    Auzary, S.; Pailloux, F.; Denanot, M.F.; Gaboriaud, R.J.

    1998-01-01

    Detailed microstructural aspects of the interface between YBaCuO thin films and MgO substrate are studied by means of a Fourier analysis of Moire fringe pattern obtained from HRTEM investigations of plan view samples. The main features of the observations are large, well oriented crystallographic domains surrounded by wide boundaries. HRTEM investigations together with the Fourier analysis show evidence of both orthorhombic and pseudo-tetragonal structure in the YBaCuO film. An accommodation mechanism is suggested from the Fourier analysis of the Moire fringe pattern. (orig.)

  9. Control of Flux Pinning in MOD YBCO Coated Conductor

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, W. [American Superconductor Corporation, Westborough, MA; Huang, Y. [American Superconductor Corporation, Westborough, MA; Li, X. [American Superconductor Corporation, Westborough, MA; Kodenkandath, Thomas [American Superconductor Corporation, Westborough, MA; Rupich, Marty [American Superconductor Corporation, Westborough, MA; Schoop, U. [American Superconductor Corporation, Westborough, MA; Verebelyi, D. T. [American Superconductor Corporation, Westborough, MA; Thieme, C. L. H. [American Superconductor Corporation, Westborough, MA; Siegal, E. E. [American Superconductor Corporation, Westborough, MA; Holesinger, T. G. [Los Alamos National Laboratory (LANL); Maiorov, B. [Los Alamos National Laboratory (LANL); Miller, D. J. [Argonne National Laboratory (ANL); Maroni, V. A. [Argonne National Laboratory (ANL); Goyal, Amit [ORNL; Specht, Eliot D [ORNL; Paranthaman, Mariappan Parans [ORNL

    2007-01-01

    Two different types of defect structures have been identified to be responsible for the enhanced pinning in metal organic deposited YBCO films. Rare earth additions result in the formation of nanodots in the YBCO matrix, which form uncorrelated pinning centers, increasing pinning in all magnetic field orientations. 124-type intergrowths, which form as laminar structures parallel to the ab-plane, are responsible for the large current enhancement when the magnetic field is oriented in the ab-plane. TEM studies showed that the intergrowths emanate from cuprous containing secondary phase particles, whose density is partially controlled by the rare earth doping level. Critical process parameters have been identified to control this phase formation, and therefore, control the f 24 intergrowth formation. This work has shown that through process control and proper conductor design, either by adjusting the composition or by multiple coatings of different functional layers, the desired angular dependence can be achieved.

  10. Control of flux pinning in MOD YBCO coated conductor.

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, W.; Huang, Y.; Li, X.; Kodenkandath, T.; Rupich, M. W.; Schoop, U.; Verebelyi, D. T.; Thieme, C. L. H.; Siegal, E.; Holesinger, T. G.; Maiorov, B.; Civale, L.; Miller, D. J.; Maroni, V. A.; Li, J.; Martin, P. M.; Specht, E. D.; Goyal, A.; Paranthaman, M. P.; American Superconductor Corp.; LANL; ORNL

    2007-06-01

    NTwo different types of defect structures have been identified to be responsible for the enhanced pinning in metal organic deposited YBCO films. Rare earth additions result in the formation of nanodots in the YBCO matrix, which form uncorrelated pinning centers, increasing pinning in all magnetic field orientations. 124-type intergrowths, which form as laminar structures parallel to the ab-plane, are responsible for the large current enhancement when the magnetic field is oriented in the ab-plane. TEM studies showed that the intergrowths emanate from cuprous containing secondary phase particles, whose density is partially controlled by the rare earth doping level. Critical process parameters have been identified to control this phase formation, and therefore, control the f 24 intergrowth formation. This work has shown that through process control and proper conductor design, either by adjusting the composition or by multiple coatings of different functional layers, the desired angular dependence can be achieved.

  11. Patterned magnetite films prepared via soft lithography and thermal decomposition

    International Nuclear Information System (INIS)

    An Lijuan; Li, Zhaoqiang; Li Wei; Nie Yaru; Chen Zhimin; Wang Yanping; Yang Bai

    2006-01-01

    A method for the fabrication of patterned magnetite (Fe 3 O 4 ) films is presented. We first prepared an ordered 2D array of Fe(acac) 3 through a selective deposition technique on patterned self-assembled monolayers. Using thermal decomposition at elevated temperature (300 o C), we transformed the patterned Fe(acac) 3 into patterned Fe 3 O 4 films in a short reaction time. These patterned films have been confirmed by using optical photographs, field emission scanning electron microscopy and atomic force microscopy

  12. Preparation and characterization of Zn Se thin films

    CERN Document Server

    Ganchev, M; Stratieva, N; Gremenok, V; Zaretskaya, E; Goncharova, O

    2003-01-01

    Chemical bath deposition technique for preparation of ZnSe thin films is presented. The influence of bath temperature and duration of deposition on film growth and quality has been studied. The effect of post-deposition annealing in different ambient is also discussed. It has been determined that heat treatment removes the oxygen-containing phase from the as-deposited films and improves crystallinity. The optical and electric properties of the deposits show their potential for an alternative buffer layer in chalcopyrite-based solar cells.

  13. Measurements and removal of substrate effects on the microwave surface impedance of YBCO films on SrTiO{sub 3}

    Energy Technology Data Exchange (ETDEWEB)

    Pompeo, N [Dipartimento di Fisica ' E Amaldi' and Unita CNISM, Universita Roma Tre, Via dellaVasca Navale 84, 00146 Rome (Italy); Muzzi, L [Dipartimento di Fisica ' E Amaldi' and Unita CNISM, Universita Roma Tre, Via dellaVasca Navale 84, 00146 Rome (Italy); Galluzzi, V [ENEA-Frascati, Via Enrico Fermi 45, 00044 Frascati, Rome (Italy); Marcon, R [Dipartimento di Fisica ' E Amaldi' and Unita CNISM, Universita Roma Tre, Via dellaVasca Navale 84, 00146 Rome (Italy); Silva, E [Dipartimento di Fisica ' E Amaldi' and Unita CNISM, Universita Roma Tre, Via dellaVasca Navale 84, 00146 Rome (Italy)

    2007-10-15

    We reconsider the problem of the measurements of the microwave complex surface impedance in thin superconducting films deposited on SrTiO{sub 3} substrates. We perform measurements of the complex surface impedance Z{sub s}' = R{sub s}'+i{delta}X{sub s}' of thin YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} films deposited by laser ablation on SrTiO{sub 3} substrates. The typical oscillations due to the strong temperature variation of the SrTiO{sub 3} permittivity are confirmed in R{sub s}' and observed in {delta}X{sub s}'. The effects of the SrTiO{sub 3} substrate are evident even well below the superconducting transition temperature of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}}. Similarly to previous works, we describe the overall response in terms of impedance transformations. We extend the known results by (i) considering the measurements of the imaginary part (ii) comparing the measurements to the absolute dc resistivity measured on the same sample, and (iii) suggesting a method for measuring the intrinsic thin film surface impedance by adjusting the substrate impedance. To demonstrate the feasibility of microwave measurements of intrinsic properties of films grown onto SrTiO{sub 3} substrates, we check the proposed method by measuring the field dependent surface impedance before and after removal of the substrate resonance.

  14. Preparation and Characterization of Chitosan—Agarose Composite Films

    Directory of Open Access Journals (Sweden)

    Zhang Hu

    2016-09-01

    Full Text Available Nowadays, there is a growing interest to develop biodegradable functional composite materials for food packaging and biomedicine applications from renewable sources. Some composite films were prepared by the casting method using chitosan (CS and agarose (AG in different mass ratios. The composite films were analyzed for physical-chemical-mechanical properties including tensile strength (TS, elongation-at-break (EB, water vapor transmission rate (WVTR, swelling ratio, Fourier-transform infrared spectroscopy, and morphology observations. The antibacterial properties of the composite films were also evaluated. The obtained results reveal that an addition of AG in varied proportions to a CS solution leads to an enhancement of the composite film’s tensile strength, elongation-at-break, and water vapor transmission rate. The composite film with an agarose mass concentration of 60% was of the highest water uptake capacity. These improvements can be explained by the chemical structures of the new composite films, which contain hydrogen bonding interactions between the chitosan and agarose as shown by Fourier-transform infrared spectroscopy (FTIR analysis and the micro-pore structures as observed with optical microscopes and scanning electron microscopy (SEM. The antibacterial results demonstrated that the films with agarose mass concentrations ranging from 0% to 60% possessed antibacterial properties. These results indicate that these composite films, especially the composite film with an agarose mass concentration of 60%, exhibit excellent potential to be used in food packaging and biomedical materials.

  15. Preparation of biaxially oriented TlCu-1234 thin films

    CERN Document Server

    Khan, N A; Tateai, F; Kojima, T; Ishida, K; Terada, N; Ihara, H

    1999-01-01

    The single phase of TlCu-1234 superconductor thin films is prepared for the first time by the amorphous phase epitaxy (APE) method, which is thallium treatment of sputtered amorphous phase at 900 degrees C for 1 h. The amorphous $9 phase is prepared by sputtering from the stoichiometric target composition CuBa/sub 2/Ca/sub 3/Cu/sub 4/O/sub 12-y/. The films on the SrTiO/sub 3/ substrate are aligned biaxially after the thallium treatment. Highly reproducible $9 TlCu-1234 films are prepared by this method. The XRD reflected a predominant single phase with the c-axis lattice constant of 18.74 AA. This lattice constant value is in between that of Cu-1234 (17.99 AA) and Tl-1234 (19.11 AA) . The $9 pole figure measurements of (103) reflection of the films showed a-axis-oriented crystals with Delta phi =0.8 degrees . The composition of the films after energy dispersive X-ray (EDX) measurements is Tl/sub 0.8/Cu/sub 0.2/Ba/sub $9 2/Ca/sub 3/Cu/sub 4/O /sub 12-y/. From the resistivity measurements, the T/sub c/ is 113 K...

  16. Electrochemical preparation of hematite nanostructured films for solar hydrogen production

    Directory of Open Access Journals (Sweden)

    Ebadzadeh T.

    2012-10-01

    Full Text Available Photoelectrochemical water splitting is a clean and promising technique for using a renewable source of energy, i.e., solar energy, to produce hydrogen. In this work electrochemical formation of iron oxyhydroxide and its conversion to hematite (α- Fe2O3 through thermal treatment have been studied. Oxyhydroxide iron compounds have been prepared onto SnO2/F covered glass substrate by potential cycling with two different potential sweep rate values; then calcined at 520 °C in air to obtain α-Fe2O3 nanostrutured films for their implementation as photoanode in a photoelectrochemical cell. X-ray diffraction analysis allowed finding that iron oxides films have nanocrystalline character. Scanning electron microscopy revealed that films have nanostructured morphology. The obtained results are discussed considering the influence of potential sweep rate employed during the preparation of iron oxyhydroxide film on optical, structural and morphological properties of hematite nanostructured films. Results show that films have acceptable characteristics as photoanode in a photoelectrochemical cell for hydrogen generation from water.

  17. Preparation of mesoporous silica films SBA-15 over different substrates

    International Nuclear Information System (INIS)

    Campos, V.O.; Sousa, E.M.B. de; Macedo, W.A.A.

    2010-01-01

    Mesoporous materials have been target of frequent interest due to its wide application possibilities, for example development of gas sensors, catalysis, molecules transportation, pharmaceuticals release, synthesis of auto-organized nanostructures, among others. The possibilities of application are enhanced when such materials are disposed in the form of thin and ultrathin films. In this work the preparation of mesoporous SBA-15 silica films is explored by means of the dipcoating technique of a sol-gel on different substrates (glass slides, stainless steel, copper), using the surfactant poly(ethylene glycol)-block-poly(propylene glycol)- block-poly(ethylene glycol), known as P123, a block copolymer. Synthesis parameters surfactant concentration, aging time and temperature were investigated. In this work we present the morphological and structural characterization of the prepared films, which were obtained using atomic force microscopy and x-ray fluorescence and diffraction. (author)

  18. Preparation of boron-nitrogen films by sputtering

    International Nuclear Information System (INIS)

    Klose, S.; Winde, B.

    1980-01-01

    Hard boron-nitrogen films adherent to various substrates can be prepared by sputtering. IR investigations suggest the existence of cubic boron nitride in certain layers. Transmission electron microscope studies have shown a quasi-amorphous structure irregularly incorporating crystallites of zinc blende structure of some nm in diameter

  19. Synthesis and characterization of zinc oxide thin films prepared by ...

    African Journals Online (AJOL)

    Zinc oxide thin films were prepared with ammonia/ammonium chloride buffer as the reaction moderating agent in the chemical bath deposition technique. An observable color change during the reaction due to variations in the reactants concentration indicated the existence of the cupric (CuO) and cuprous (Cu2O) oxides ...

  20. Preparation of DNA films for studies under vacuum conditions

    DEFF Research Database (Denmark)

    Smialek, M. A.; Balog, Richard; Jones, N. C.

    2010-01-01

    process. Using a transmission electron microscope we also examined the structure of the DNA films which are formed upon evacuation and how the proposed adducts influence the preparation process. It was found that the addition of bases cause the DNA to aggregate, noting that a base is required...

  1. Preparing polymer brushes on polytetrafluoroethylene films by free radical polymerization

    International Nuclear Information System (INIS)

    Sun Wei; Chen Yiwang; Deng Qilan; Chen Lie; Zhou Lang

    2006-01-01

    Films of polytetrafluoroethylene (PTFE) were exposed to sodium naphthalenide (Na/naphtha) etchant so as to defluorinate the surface for obtaining hydroxyl functionality. Surface-initiators were immobilized on the PTFE films by esterification of 4,4'-azobis(4-cyanopentanoic acid) (ACP) and the hydroxyl groups covalently linked to the surface. Grafting of polymer brushes on the PTFE films was carried out by the surface-initiated free radical polymerization. Homopolymers brushes of methyl methacrylate (MMA) were prepared by free radical polymerization from the azo-functionalized PTFE surface. The chemical composition and topography of the graft-functionalized PTFE surfaces were characterized by X-ray photoelectron spectroscopy (XPS), attenuated total reflectance (ATR) FT-IR spectroscopy and atomic force microscopy (AFM). Water contact angles on PTFE films were reduced by surface grafting of MMA

  2. Raman spectra, microstructure and superconducting properties of Sb(III)-YBCO composite superconductor

    Energy Technology Data Exchange (ETDEWEB)

    Elsabawy, Khaled M. [Chemistry Department, Faculty of Science, Tanta University, Tanta (Egypt)]. E-mail: ksabawy@yahoo.com

    2005-11-15

    The pure YBCO (YBa{sub 2}Cu{sub 3}O{sub 7}) and its variant antimony containing composites with general formula; Y{sub 1+x}Sb {sub x}Ba{sub 2}Cu{sub 3}O {sub z}, where x = 0.1, 0.2, 0.4 and 0.6 mol%, respectively, were prepared by the solid-state reaction route. X-ray measurements indicated that Sb{sup 3+} ions have a negligible effect on the main crystalline structure and substitutes Y-sites successfully in lattice structure of 123-YBCO at low concentrations of doping (x = 0.1 {sup {yields}} 0.2). From SE-microscopy mapping and EDX elemental analysis, Sb{sup 3+} was detected qualitatively with good approximation to the actual molar ratio but not observed at 123-YBCO grain boundaries which confirm that antimony (III) has diffused regularly into material bulk of superconducting 123-YBCO-phase at low concentrations. Additions of Sb(III) affected sharply on the main vibrating modes of YBCO regime particularly, on the apical oxygen (O{sub 4}) vibrational mode A {sub 1g}. Magnetic susceptibility measurements proved that antimony oxide additions have slight effect on the transport properties of YBCO-composites regime.

  3. AFM studies on heavy ion irradiated YBCO single crystals

    International Nuclear Information System (INIS)

    Lakhani, Archana; Marhas, M.K.; Saravanan, P.; Ganesan, V.; Srinivasan, R.; Kanjilal, D.; Mehta, G.K.; Elizabeth, Suja; Bhat, H.L.

    2000-01-01

    Atomic Force Microscopy (AFM) is extensively used to characterise the surface morphology of high energy ion irradiated single crystals of high temperature superconductor - YBCO. Our earlier systematic studies on thin films of YBCO under high energy and heavy ion irradiation shows clear evidence of ion induced sputtering or erosion, even though the effect is more on the grain boundaries. These earlier results were supported by electrical resistance measurements. In order to understand more clearly, the nature of surface modification at these high energies, AFM studies were carried out on single crystals of YBCO. Single crystals were chosen in order to see the effect on crystallites alone without interference from grain boundaries. 200 MeV gold ions were used for investigation using the facilities available at Nuclear Science Centre, New Delhi. The type of ion and the range of energies were chosen to meet the threshold for electronically mediated defect production. The results are in conformity with our earlier studies and will be described in detail in the context of electronic energy loss mediated sputtering or erosion. (author)

  4. Free-standing graphene films prepared via foam film method for great capacitive flexible supercapacitors

    Science.gov (United States)

    Zhu, Yucan; Ye, Xingke; Tang, Zhonghua; Wan, Zhongquan; Jia, Chunyang

    2017-11-01

    Recently, graphene films have always attracted attention due to their excellent characteristics in energy storage. In this work, a novel graphene oxide (GO) film with excellent mechanical properties, whose thickness was regulated simply via changing the concentration of the surfactant, was successfully prepared by foam film method. After chemical reduction, the reduced GO (rGO) films have excellent electrical conductivity of ∼172 S cm-1. Moreover, the supercapacitors based on the rGO films exhibit satisfied capacitive performance of ∼56 mF cm-2 at 0.2 mA cm-2 in 6 M KOH aqueous solution. Meanwhile, the flexible all solid state supercapacitors (FSSCs) based on the rGO films also show great volumetric capacitance of ∼2810 mF cm-3 at 12 mA cm-3 (∼1607 mF cm-3 at 613 mA cm-3) with polyvinyl alcohol-KOH gel electrolyte. Besides, after 10000 cycles and continuously bent to 180° for 300 times, the volumetric capacitance of the FSSC remains at 81.4% and 90.4% of its initial capacitance value, respectively. Therefore, the free-standing rGO films prepared via foam film method could be considered as promising electrode materials for high performance flexible supercapacitors.

  5. Preparation and Characterization of K-Carrageenan/Nanosilica Biocomposite Film

    Directory of Open Access Journals (Sweden)

    Lokesh R. Rane

    2014-01-01

    Full Text Available The purpose of this study is to improve the performance properties of K-carrageenan (K-CRG by utilizing nanosilica (NSI as the reinforcing agent. The composite films were prepared by solution casting method. NSI was added up to 1.5% in the K-CRG matrix. The prepared films were characterized for mechanical (tensile strength, tensile modulus, and elongation at break, thermal (differential scanning calorimetry, thermogravimetric analysis, barrier (water vapour transmission rate, morphological (scanning electron microscopy, contact angle, and crystallinity properties. Tensile strength, tensile modulus, and crystallinity were found to have increased by 13.8, 15, and 48% whereas water vapour transmission rate was found to have decreased by 48% for 0.5% NSI loaded K-CRG composite films. NSI was found to have formed aggregates for concentrations above 0.5% as confirmed by scanning electron microscopy. Melting temperature, enthalpy of melting, and degradation temperature of K-CRG increased with increase in concentration of NSI in K-CRG. Contact angle also increased with increase in concentration of NSI in K-CRG, indicating the decrease in hydrophilicity of the films improving its water resistance properties. This knowledge of the composite film could make beneficial contributions to the food and pharmaceutical packaging applications.

  6. Preparation and Characteristics of Biodegradable Polyurethane/Clay Nanocomposite Films

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Seong Woo [Kyonggi University, Suwon (Korea, Republic of)

    2013-06-15

    Biodegradable polyurethane (PU)/clay nanocomposite films were prepared via extrusion compounding process followed by casting film process. Organically modified montmorillonite (denoted as C30B) with a large amount of hydroxyl groups on its surface was used for the formation of strong bonding with PU resin. From both XRD analysis and TEM observations, the intercalated and exfoliated structure, and dispersion state of silicate platelets in the compounded nanocomposite films were confirmed. In addition, the rheological and tensile properties, optical transparency, oxygen permeability of the prepared nanocomposites were investigated as a function of added nanoclay content, and moreover based on these results, the correlation between the morphology and the resulting properties of the nanocomposites could be presented. The inclusion of nanoclays at appropriate content resulted in remarkable improvement in the nanocomposite performance including tensile modulus, elongation, transparency, and oxygen barrier property, however at excess amount of nanoclays, reduction or very slight increase was observed due to poor dispersion. The biodegradability of the prepared nanocomposite film was evaluated by examining the deterioration in the barrier and tensile properties during degradation period under compost.

  7. Preparation of SnSe thin films by encapsulated selenization

    International Nuclear Information System (INIS)

    Sabar D. Hutagalung; Samsudi Sakrani; Yussof Wahab

    1994-01-01

    Tin selenide thin films were prepared by encapsulated selenization. A stacked layer of evaporated Sn and Se films were annealed in a carbon block at temperatures 100 - 500 degree Celsius for 3 hours. X-ray analysis and SEM (Scanning electron) micrograph results showed that SnSe was initially formed at 150 degree Celsius with crystal size 30.0 nm and reached optimum formation at 200 daximum of 57.4 % yield of 5-decene. Other factors such as reaction temperatures, types of solvent and wt% of rhenium loadings influence the activity of the catalytic system

  8. Preparation of Track Etch Membrane Filters Using Polystyrene Film

    International Nuclear Information System (INIS)

    Kaewsaenee, Jerawut; Ratanatongchai, Wichian; Supaphol, Pitt; Visal-athaphand, Pinpan

    2007-08-01

    Full text: Polystyrene nuclear track etch membrane filters was prepared by exposed 13 .m thin film polystyrene with fission fragment. Nuclear latent track was enlarged to through hole on the film by etching with 80 o C 40% H 2 SO 4 with K 2 Cr 2 O 7 solution for 6-10 hour. The hole size was depend on concentration of etching solution and etching time with 1.3-3.4 .m hole diameter. The flow rate test of water was 0.79-1.56 mm cm-2 min-1 at 109.8-113.7 kPa pressure

  9. Preparation of Ta Te2 thin films by laser ablation

    International Nuclear Information System (INIS)

    Zidan, M.D.; Alkhwam, M.; Alkhasm, M.

    2006-03-01

    The laser ablation system consisting of a vacuum chamber and Nd-YAG laser has been built for deposition TaTe 2 on three different substrates (Silicon, glass, and Aluminium). The surface topography of the prepared thin films has been studied by atomic force microscopy (AFM). TaTe 2 powder was characterized by using x-ray diffraction. The crystallinity of the thin films was examined by x-ray diffraction (XRD). The results show no peaks corresponding TaTe 2 , but there are some indications to the Ta 3 N 5 . (author)

  10. Preparation of Ferroelectric Thin Films of Bismuth Layer Structured Compounds

    Science.gov (United States)

    Watanabe, Hitoshi; Mihara, Takashi; Yoshimori, Hiroyuki; Araujo, Carlos

    1995-09-01

    Ferroelectric thin films of bismuth layer structured compounds, SrBi2Ta2O9, SrBi2Nb2O9, SrBi4Ti4O15 and their solid solutions, were formed onto a sputtered platinum layer on a silicon substrate using spin-on technique and metal-organic decomposition (MOD) method. X-ray diffraction (XRD) analysis and some electrical measurements were performed on the prepared thin films. XRD results of SrBi2(Ta1- x, Nb x)2O9 films (0≤x≤1) showed that niobium ions substitute for tantalum ions in an arbitrary ratio without any change of the layer structure and lattice constants. Furthermore, XRD results of SrBi2 xTa2O9 films (0≤x≤1.5) indicated that the formation of the bismuth layer structure does not always require an accurate bismuth content. The layer structure was formed above 50% of the stoichiometric bismuth content in the general formula. SrBi2(Ta1- x, Nb x)2O9 films with various Ta/Nb ratios have large enough remanent polarization for nonvolatile memory application and have shown high fatigue resistance against 1011 cycles of full switching of the remanent polarization. Mixture films of the three compounds were also investigated.

  11. Indium tin oxide films prepared via wet chemical route

    International Nuclear Information System (INIS)

    Legnani, C.; Lima, S.A.M.; Oliveira, H.H.S.; Quirino, W.G.; Machado, R.; Santos, R.M.B.; Davolos, M.R.; Achete, C.A.; Cremona, M.

    2007-01-01

    In this work, indium tin oxide (ITO) films were prepared using a wet chemical route, the Pechini method. This consists of a polyesterification reaction between an α-hydroxicarboxylate complex (indium citrate and tin citrate) with a polyalcohol (ethylene glycol) followed by a post annealing at 500 deg. C. A 10 at.% of doping of Sn 4+ ions into an In 2 O 3 matrix was successfully achieved through this method. In order to characterize the structure, the morphology as well as the optical and electrical properties of the produced ITO films, they were analyzed using different experimental techniques. The obtained films are highly transparent, exhibiting transmittance of about 85% at 550 nm. They are crystalline with a preferred orientation of [222]. Microscopy discloses that the films are composed of grains of 30 nm average size and 0.63 nm RMS roughness. The films' measured resistivity, mobility and charge carrier concentration were 5.8 x 10 -3 Ω cm, 2.9 cm 2 /V s and - 3.5 x 10 20 /cm 3 , respectively. While the low mobility value can be related to the small grain size, the charge carrier concentration value can be explained in terms of the high oxygen concentration level resulting from the thermal treatment process performed in air. The experimental conditions are being refined to improve the electrical characteristics of the films while good optical, chemical, structural and morphological qualities already achieved are maintained

  12. Properties of tungsten films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Ahn, K.Y.; Ting, C.Y.; Brodsky, S.B.; Fryer, P.M.; Davari, B.; Angillelo, J.; Herd, S.R.; Licata, T.

    1986-01-01

    High-rate magnetron sputtering is a relatively simple process to produce tungsten films with good electrical and mechanical properties, and it offers good uniformity, reproducibility, process flexibility, and high throughput. The purity of the sputtered films is affected by the target purity (cold-pressed 99.95%, chemical vapor deposited 99.99% and cast 99.999%), base pressure, deposition rate, and substrate bias. Typical resistivity in films of 2000 to 3000A thickness deposited on Si, poly-Si, and SiO/sub 2/ ranges from 10 to 12 μΩ-cm, and this may be compared with 6 and 11 μΩ-cm by high-temperature evaporation and chemical vapor deposition, respectively. The presence of biaxial stress caused by substrate scanning was determined by x-ray technique. The sputtered films exhibit high compressive stress when deposited at low Ar pressure. It decreases with increasing pressure, and eventually changes sign to become tensile, and increases further with increasing pressure. Effects of processing parameters on films properties, and a comparison of film properties prepared by evaporation and chemical vapor deposition are discussed

  13. DC magnetron sputtering prepared Ag-C thin film anode for thin film lithium ion microbatteries

    International Nuclear Information System (INIS)

    Li, Y.; Tu, J.P.; Shi, D.Q.; Huang, X.H.; Wu, H.M.; Yuan, Y.F.; Zhao, X.B.

    2007-01-01

    An Ag-C thin film was prepared by DC magnetron co-sputtering, using pure silver and graphite as the targets. The microstructure and morphology of the deposited thin film were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Electrochemical performances of the Ag-C thin film anode were investigated by means of discharge/charge and cyclic voltammogram (CV) tests in model cells. The electrochemical impedance spectrum (EIS) characteristics and the chemical diffusion coefficient, D Li of the Ag-C thin film electrode at different discharging states were discussed. It was believed that the excellent cycling performance of the Ag-C electrode was ascribed to the good conductivity of silver and the volume stability of the thin film

  14. Preparation and characterization of sprayed FTO thin films

    Science.gov (United States)

    Abd-Lefdil, M.; Diaz, R.; Bihri, H.; Aouaj, M. Ait; Rueda, F.

    2007-06-01

    Fluorine doped tin oxide (FTO) thin films have been prepared by spray pyrolysis technique with no further annealing. Films with 2.5% of fluorine grown at 400 °C present a single phase and exhibit a tetragonal structure with lattice parameters a = 4.687 Å and c = 3.160 Å. Scanning electron micrographs showed homogeneous surfaces with average grain size around 190 nm. The films are transparent in the visible zone and exhibit a high reflectance in the near infrared region. The best electrical resistivity was 6.3 × 10-4 Ω cm for FTO with 2.5% of fluorine. The ratio of transmittance in the visible to the sheet resistance are in the 0.57 × 10-2 1.96 × 10-2 {Ω }-1 range.

  15. ITO thin films prepared by a microwave heating

    International Nuclear Information System (INIS)

    Okuya, Masayuki; Ito, Nobuyuki; Shiozaki, Katsuyuki

    2007-01-01

    ITO thin films were prepared by irradiating 2.45 GHz of microwave with an output power of 700 W using a commercial kitchen microwave oven. A substrate temperature went up and down rapidly between 100 and 650 deg. C in a minute by a dielectric loss of SnO 2 layer pre-deposited on a glass substrate. We found that the electrical and optical properties of films were affected by the atmosphere in a microwave irradiation, while the sintering was completed within a few minutes. Although the electrical resistivity was not reduced below 5.0 x 10 -4 Ω.cm in this study, the results lead to the possibility of a practical rapid synthesis of ITO transparent conducting oxide films

  16. Critical current in nonhomogeneous YBCO coated conductors

    International Nuclear Information System (INIS)

    Rostila, L; Mikkonen, R; Lehtonen, J

    2008-01-01

    The critical current of an YBCO tape is determined by the magnetic field inside the YBCO layer and the quality of YBCO material. In thick YBCO layers the average critical current density is reduced by the self-field and decreased material quality. In this paper the combined influence of the material nonhomogeneities and self-field on the critical current of YBCO tapes is scrutinised. First, the zero field critical current density was assumed to decrease along the YBCO thickness. Secondly, the possible defects created in the cutting of YBCO tapes were modelled as a function of lowered critical current density near the tape edges. In both cases the critical current was computed numerically with integral element method. The results suggest that the variation of zero field critical current density, J c0 , along the tape thickness does not effect on the critical current if the mean value of J c0 is kept constant. However, if J c0 is varied along the tape width the critical current can change due to the variated self-field. The computations can be used to determine when it is possible to evaluate the average zero field critical current density from a voltage-current measurement with an appropriate accuracy

  17. Preparation and thermomechanical properties of Ag-PVA nanocomposite films

    International Nuclear Information System (INIS)

    Gautam, Anurag; Ram, S.

    2010-01-01

    Metal-polymer hybrid nanocomposites have been prepared from an aqueous solution of polyvinyl alcohol (PVA) and silver nitrate (AgNO 3 ). The silver nanoparticles were generated in PVA matrix by the reduction of silver ions with PVA molecule at 60-70 deg. C over magnetic stirrer. UV-vis analysis, X-ray diffraction studies, transmission electron microscopy, scanning electron microscopy and current-voltage analysis were used to characterize the nanocomposite films prepared. The X-ray diffraction analysis reveals that silver metal is present in face centered cubic (fcc) crystal structure. Average crystallite size of silver nanocrystal is 19 nm, which increases to 22 nm on annealing the film at 150 deg. C in air. This result is in good agreement with the result obtained from TEM. The UV-vis spectrum shows a single peak at 433 nm, arising from the surface plasmon absorption of silver nanocolloids. This result clearly indicates that silver nanoparticles are embedded in PVA. An improvement of mechanical properties (storage modulus) was also noticed due to a modification of PVA up to 0.5 wt% of silver content. The current-voltage (I-V) characteristic of nanocomposite films shows increase in current drawn with increasing Ag-content in the films.

  18. High trapped fields in bulk YBCO superconductors

    Science.gov (United States)

    Fuchs, Günter; Gruss, Stefan; Krabbes, Gernot; Schätzle, Peter; Verges, Peter; Müller, Karl-Hartmut; Fink, Jörg; Schultz, Ludwig

    The trapped field properties of bulk melt-textured YBCO material were investigated at different temperatures. In the temperature range of liquid nitrogen, maximum trapped fields of 1.1 T were found at 77 K by doping of YBCO with small amounts of zinc. The improved pinning of zinc-doped YBa2Cu3O7-x (YBCO) results in a pronounced peak effect in the field dependence of the critical current density. the trapped field at lower temperatures increases due to the increasing critical current density, however, at temperatures around 50 K cracking of the material is observed which is exposed to considerably tensile stresses due to Lorentz forces. Very high trapped fields up to 14.4 T were achieved at 22.5 K for a YBCO disk pair by the addition of silver improving the tensile strength of YBCO and by using a bandage made of a steel tube. The steel tube produces a compressive stress on YBCO after cooling down from 300 K to the measuring temperature, which is due to the higher coeeficient of thermal expansion of steel compared with that of YBCO in the a,b plane. The application of superconducting permanent magnets with trapped fields of 10 T and more in superconducting bearings would allow to obtain very high levitation pressures up to 2500 N/cm2 which is two orders of magnitude higher than the levitation pressure achievable in superconducting bearings with conventional permanent magnets. The most important problem for the application of superconducting permanent magnets is the magnetizing procedure of the YBCO material. Results of magnetizing YBCO disks by using of pulsed magnetic fields will be presented.

  19. Preparation of molybdenum oxide thin films by MOCVD

    International Nuclear Information System (INIS)

    Guerrero, R. Martinez; Garcia, J.R. Vargas; Santes, V.; Gomez, E.

    2007-01-01

    In this study, molybdenum oxide films were prepared in a horizontal hot-wall MOCVD apparatus using molybdenum dioxide acetylacetonate as precursor. The molybdenum precursor was synthesized from acetylacetone and molybdenum oxide powder. Thermal gravimetric (TG) and differential thermal analyses (DTA) of the precursor suggested the formation of molybdenum oxides around 430 o C (703 K). Thus, a range of deposition temperatures varying from 350 to 630 o C (623-903 K) was explored to investigate the effects on the nature of the molybdenum oxide films. X-ray diffraction (XRD) results showed that the films consisted of α-MoO 3 phase at deposition temperatures ranging from 400 to 560 o C (673-833 K). Crystalline α-MoO 3 films can be obtained from molybdenum dioxide acetylacetonate precursor, without need of a post-annealing treatment. The best crystalline quality was found in films having needle-like crystallites grown at deposition temperature of about 560 o C (833 K), which exhibit a strong (0 1 0) preferred orientation and a transparent visual appearance

  20. Preparation of molybdenum oxide thin films by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Guerrero, R. Martinez [Depto. de Ingenieria Metalurgica, ESIQIE-IPN, Mexico 07300, D.F. (Mexico); Garcia, J.R. Vargas [Depto. de Ingenieria Metalurgica, ESIQIE-IPN, Mexico 07300, D.F. (Mexico)]. E-mail: rvargasga@ipn.mx; Santes, V. [CIIEMAD-IPN, Miguel Othon de Mendizabal 485, Mexico 07700, D.F. (Mexico); Gomez, E. [Instituto de Quimica-UNAM, Circuito Exterior-Ciudad Universitaria, Mexico 04510, D.F. (Mexico)

    2007-05-31

    In this study, molybdenum oxide films were prepared in a horizontal hot-wall MOCVD apparatus using molybdenum dioxide acetylacetonate as precursor. The molybdenum precursor was synthesized from acetylacetone and molybdenum oxide powder. Thermal gravimetric (TG) and differential thermal analyses (DTA) of the precursor suggested the formation of molybdenum oxides around 430 {sup o}C (703 K). Thus, a range of deposition temperatures varying from 350 to 630 {sup o}C (623-903 K) was explored to investigate the effects on the nature of the molybdenum oxide films. X-ray diffraction (XRD) results showed that the films consisted of {alpha}-MoO{sub 3} phase at deposition temperatures ranging from 400 to 560 {sup o}C (673-833 K). Crystalline {alpha}-MoO{sub 3} films can be obtained from molybdenum dioxide acetylacetonate precursor, without need of a post-annealing treatment. The best crystalline quality was found in films having needle-like crystallites grown at deposition temperature of about 560 {sup o}C (833 K), which exhibit a strong (0 1 0) preferred orientation and a transparent visual appearance.

  1. Preparation and Characterization of Formalated Polyvinyl Alcohol Hydrogel Film

    International Nuclear Information System (INIS)

    Than Than Aye; Nyunt Win; San Myint

    2011-12-01

    A feasible hydrogen film was prepared from polyvinyl alcohol (PVA) sample. The effect of chemical grafting on polyvinyl alcohol film was studied. Polyvinyl alcohol sample was mixed with distilled water and autoclaved at 121C for 60 minutes. An aqueous solution of polyvinyl alcohol was casted into a steel plate and dried for a certain time at room temperature. The obtained PVA film was immersed in formalation bath containing aqueous formaldehyde, sulphuric acid, anhydrous sodium sulphate with a weight ratio of (64:95:300) and 1 liter of distilled water at 60C for various hours. Effect of formalation time was studied varying 6, 12, 24, 36 and 48 hours. Degree of formalation was also evaluated. Physical properties of the hydrogel film such as gel fraction, degree of swelling and mechanical properties such as tensile strength, elongation and hardness were determined before and after formalation of the PVA film. Fourier Transform Infrared Spectroscopic (FTIR) analysis, Thermogravimetric / Differential thermal analysis (DTA / TG) were also studied for characterization. It was found that the appropriate condition for formalation was occured at 24 hours formalation time of with the calculated degree of formalation 65.35% with the determined values (9.04 Mpa) for tensile strength, (241.92%) for elongation, (45.30 Shore D) for hardness, (280.36%) for degree of swelling and (68.32%) for gel fraction.

  2. Effect of Perovskite Film Preparation on Performance of Solar Cells

    Directory of Open Access Journals (Sweden)

    Yaxian Pei

    2016-01-01

    Full Text Available For the perovskite solar cells (PSCs, the performance of the PSCs has become the focus of the research by improving the crystallization and morphology of the perovskite absorption layer. In this thesis, based on the structure of mesoporous perovskite solar cells (MPSCs, we designed the experiments to improve the photovoltaic performance of the PSCs by improved processing technique, which mainly includes the following two aspects. Before spin-coating PbI2 solution, we control the substrate temperature to modify the crystal quality and morphology of perovskite films. On the other hand, before annealing, we keep PbI2 films for the different drying time at room temperature to optimize films morphology. In our trials, it was found that the substrate temperature is more important in determining the photovoltaic performance than drying time. These results indicate that the crystallization and morphology of perovskite films affect the absorption intensity and obviously influence the short circuit current density of MPSCs. Utilizing films prepared by mentioning two methods, MPSCs with maximum power conversion efficiency of over 4% were fabricated for the active area of 0.5 × 0.5 cm2.

  3. Deposition techniques for the preparation of thin film nuclear targets

    International Nuclear Information System (INIS)

    Muggleton, A.H.F.

    1987-07-01

    This review commences with a brief description of the basic principles that regulate vacuum evaporation and the physical processes involved in thin film formation, followed by a description of the experimental methods used. The principle methods of heating the evaporant are detailed and the means of measuring and controlling the film thickness are elucidated. Types of thin film nuclear targets are considered and various film release agents are listed. Thin film nuclear target behaviour under ion-bombardment is described and the dependence of nuclear experimental results upon target thickness and uniformity is outlined. Special problems associated with preparing suitable targets for lifetime measurements are discussed. The causes of stripper-foil thickening and breaking under heavy-ion bombardment are considered. A comparison is made between foils manufactured by a glow discharge process and those produced by vacuum sublimation. Consideration is given to the methods of carbon stripper-foil manufacture and to the characteristics of stripper-foil lifetimes are considered. Techniques are described that have been developed for the fabrication of special targets, both from natural and isotopically enriched material, and also of elements that are either chemically unstable, or thermally unstable under irradiation. The reduction of metal oxides by the use of hydrogen or by utilising a metallothermic technique, and the simultaneous evaporation of reduced rare earth elements is described. A comprehensive list of the common targets is presented

  4. Investigation of DC current injection effect on the microwave characteristics of HTS YBCO microstrip resonators

    Energy Technology Data Exchange (ETDEWEB)

    Nurgaliev, T., E-mail: timur@ie.bas.bg [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Blagoev, B.; Mateev, E.; Neshkov, L. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Strbik, V. [Institute of Electrical Engineering, Slovak Academy of Sciences, Dúbravská cesta 9, 841 04 Bratislava (Slovakia); Uspenskaya, L. [Institute of Solid State Physics, Russian Academy of Sciences, 142432 Chernogolovka, Moscow (Russian Federation); Nedkov, I. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Chromik, Š. [Institute of Electrical Engineering, Slovak Academy of Sciences, Dúbravská cesta 9, 841 04 Bratislava (Slovakia)

    2014-03-15

    Highlights: • Current (spin) injection effect in LSMO/YBCO was studied by impedance measurements. • Complex impedance of YBCO increases at current injection from LSMO to YBCO at 77 K. • This increase is due to an increase of the quasiparticle conductivity of YBCO. • Injection does not significantly affect the relaxation time of the quasiparticles. - Abstract: The DC current injection effect from a ferromagnetic (FM) La{sub 0.7}Sr{sub 0.3}MnO{sub 3} (LSMO) to a high temperature superconducting (HTS) Y{sub 1}Ba{sub 2}Cu{sub 3}O{sub 7−x} (YBCO) thin film was investigated by the microwave surface impedance measurements in a FM/HTS structure, formed as a microstrip resonator for improving the sensitivity of the experiments. The quality factor and the resonance frequency of this structure were found to strongly depend on the current strength, injected from the LSMO electrode into the HTS microstrip electrode. The magnetic penetration depth and the quasiparticle conductivity of the HTS component were determined to increase under DC current injection process, which in all probability stimulated breaking of Cooper pairs and led to a decrease of the superfluid concentration and an increase of the normal fluid concentration without significantly affecting the relaxation time of the quasiparticles.

  5. Improving superconducting properties of YBCO high temperature superconductor by Graphene Oxide doping

    Energy Technology Data Exchange (ETDEWEB)

    Dadras, S., E-mail: dadras@alzahra.ac.ir; Dehghani, S.; Davoudiniya, M.; Falahati, S.

    2017-06-01

    In this research, we report the synthesis and characterization of YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO) high temperature superconductor prepared by sol-gel method and doped with Graphene Oxide (GO) in different weight percentages, 0, 0.1, 0.7 and 1 % wt. The x-ray diffraction (XRD) analysis confirms the formation of orthorhombic phase of superconductivity for all the prepared samples. We found that GO doping reduces the crystalline size of the samples. We evaluated the effects of GO doping on the normal state resistivity (ρ), superconducting transition temperature (T{sub c}) and critical current density (J{sub c}). The results show that the GO doping has a positive effect on these properties. Also, the highest J{sub c} is obtained for the 0.7 %wt GO doped YBCO compound that its critical current density is about 15 times more than the J{sub c} of pure one in 0.4 T magnetic field. The scanning electron microscope (SEM) analysis shows that there are better connections between the grains of GO doped samples. - Highlights: • Graphene Oxide doping increased the YBCO critical current density. • Graphene Oxide creates a better connection between the YBCO grains. • The normal resistivity of samples were decreased by GO doping to YBCO compounds. • Graphene Oxide doping has a positive effect on the critical transition temperature.

  6. Preparation of poly(vinylbenzyl chloride)-grafted PFA film by a simultaneous irradiation grafting method

    International Nuclear Information System (INIS)

    Fei, Geng; Shin, Jun Hwa; Nho, Young Chang; Lee, Youn Sik

    2009-01-01

    In this study, PFA-g-PVBC films were prepared by a radiation grafting of vinylbenzyl chloride (VBC) monomer onto poly(tetrafluoroethylene-co-perfluoro propyl vinyl ether) (PFA) films by simultaneous irradiation method. IR, TGA, and SEM-EDX instruments were utilized to confirm the successful preparation of the grafted film. The effects of several irradiation conditions, including the dose, VBC concentration, and film thickness on the degree of grafting of PFA-g-PVBC film were investigated

  7. Pinning Mechanisms in YBCO Tapes

    CERN Document Server

    Spera, Marcello; Ballarino, Amalia

    2015-01-01

    In this thesis work, a study on flux pinning mechanisms of commercial YBCO tapes is presented. This study has been performed via critical current characterization using transport (via direct I-V curves) and magnetization (via a Vibrating Sample Magnetometer) measurements. The latter ones turned out to be better concerning the comprehension of the pinning landscape of the provided samples, as a wider range of magnetic fields and temperatures is available for those measurements in the setup I used. The comparison of the experimental data with existing theoretical models allowed me to draw a picture of the pinning mechanisms underlying in each sample, and they turned out to be quite different one another. Moreover, for high-performance research tapes, another interesting feature has been found: the counterplay between the self-field critical current and the in-field one. Very well engineered artificial pinning structures limit the self-field critical current density due to the hi...

  8. Development of YBCO tape conductor fabrication technology

    Energy Technology Data Exchange (ETDEWEB)

    Hong, G W; Kim, C J; Lee, H G. and others

    2001-08-01

    Superconductor when fabricated into wire shape is applied for developing electric power transmission cable, transformer, generator and SMES. Such superconducting power devices are capable of maximizing the efficiency of electricity and are anticipated to contribute for solving the energy problem of humankind. Furthermore the high temperature oxide superconductor developed in late 1980s is superconducting above boiling temperature of liquid nitrogen temperature has strong potential to realize superconducting power device and a lot of researches are being done in this field. Superconducting wire is the most important core material for developing superconducting power device and thermo-mechanical powder in tube process was developed to fabricated Ag/Bi-2223 conductor in long length having high critical current carrying capacity. Several companies fabricate and sell Ag/Bi-2223 superconducting wire longer than km length and used for developed electrical power device. But because of its inherent property of sharp decrease in current carrying capacity when applying high magnetic field, the application of Bi-2223 sire is limited as low as 20 K when the power device is in operating under high magnetic field. The YBCO tape conductor has the advantages of maintaining high critical current applying high magnetic field and can be used to most of the power device without special limitation. The metal substrate having good crystallographic texture and deposition technique which can deposit the good quality superconducting thin film continuously in large area are need to fabricate coated conductor, and this technique can be applied to develop the superconducting current limiter or magnetic field shielding device. A superconducting wire for using in high magnetic field is play a critical role in developing maglev, MRI, SMES, transformer, generator and motor and the continuous film deposition technique can be applied in other industry very much.

  9. Epitaxial growth and superconducting properties of YBa23Cu3O7 thin films and YBa2Cu3O7/Dy(Pr)Ba2Cu3O7 superlattices

    International Nuclear Information System (INIS)

    Triscone, J.M.; Brunner, O.; Antognazza, L.; Kent, A.D.; Fischer, O.; Karkut, M.G.

    1990-01-01

    The authors have prepared in situ REBa 2 Cu 3 O 7 (REBCO) (RE = Y, Pr, Dy) thin films and YBCO/Dy(Pr)BCO superlattices by single target dc planar magnetron sputtering. YBCO/DyBCO superlattices have been realized with modulation wavelength as short as 24 Angstrom, i.e., a unit cell of YBCO alternates with a unit cell of DyBCO, on average. The superconducting properties of such superlattices are indistinguishable from those of single layers. T co 's (zero resistance) are between 85 and 89K, and the residual resistivity ratios are between 2.5 and 3. In contrast to these results, when YBCO is layered with PrBCO, which is insulating, a dramatic change in the superconducting properties is observed. The authors have been able to artificially vary the coupling between single 12 Angstrom unit cell of YBCO by interposing insulating planes of PrBCO. As the YBCO layer separation increases, T c is reduced and the transition broadens showing evidence of 2-D superconducting fluctuations

  10. Preparation and properties of thin films treatise on materials science and technology

    CERN Document Server

    Tu, K N

    1982-01-01

    Treatise on Materials Science and Technology, Volume 24: Preparation and Properties of Thin Films covers the progress made in the preparation of thin films and the corresponding study of their properties. The book discusses the preparation and property correlations in thin film; the variation of microstructure of thin films; and the molecular beam epitaxy of superlattices in thin film. The text also describes the epitaxial growth of silicon structures (thermal-, laser-, and electron-beam-induced); the characterization of grain boundaries in bicrystalline thin films; and the mechanical properti

  11. Passivation of Flexible YBCO Superconducting Current Lead With Amorphous SiO2 Layer

    Science.gov (United States)

    Johannes, Daniel; Webber, Robert

    2013-01-01

    across a thermal gradient with as little flow of heat as possible to make an efficient current lead. By protecting YBCO on a flexible substrate of low thermal conductivity with SiO2, a thermally efficient and flexible current lead can be fabricated. The technology is also applicable to current leads for 4 K superconducting electronics current biasing. A commercially available thin-film YBCO composite tape conductor is first stripped of its protective silver coating. It is then mounted on a jig that holds the sample flat and acts as a heat sink. Silicon dioxide is then deposited onto the YBCO to a thickness of about 1 micron using PECVD (plasma-enhanced chemical vapor deposition), without heating the YBCO to the point where degradation occurs. Since SiO2 can have good high-frequency electrical properties, it can be used to coat YBCO cable structures used to feed RF signals across temperature gradients. The prime embodiment concerns the conduction of DC current across the cryogenic temperature gradient. The coating is hard and electrically insulating, but flexible.

  12. Study on Preparation and Properties of PVC Film Modified by Rare Earth

    Institute of Scientific and Technical Information of China (English)

    2003-01-01

    The transparent PVC films were prepared by tape casting. In the process of preparation, rare earth nitrate, as a kind of modifier, was added to the solution of PVC and THF. These PVC films were tested after being crosslinked by ultraviolet light. It is found that the mechanical and physical properties of all the PVC films modified by rare earth nitrate are greatly enhanced.

  13. Magnetic response of superconducting mesoscopic-size YBCO powder

    Energy Technology Data Exchange (ETDEWEB)

    Deimling, C.V. [Grupo de Supercondutividade e Magnetismo, Departamento de Fisica, Universidade Federal de Sao Carlos, Sao Carlos, SP (Brazil)], E-mail: cesard@df.ufscar.br; Motta, M.; Lisboa-Filho, P.N. [Laboratorio de Materiais Supercondutores, Departamento de Fisica, Universidade Estadual Paulista, Bauru, SP Brazil (Brazil); Ortiz, W.A. [Grupo de Supercondutividade e Magnetismo, Departamento de Fisica, Universidade Federal de Sao Carlos, Sao Carlos, SP (Brazil)

    2008-07-15

    In this work it is reported the magnetic behavior of submicron and mesoscopic-size superconducting YBCO powders, prepared by a modified polymeric precursors method. The grain size and microstructure were analyzed using scanning electron microscopy (SEM). Measurements of magnetization and AC-susceptibility as a function of temperature were performed with a quantum design SQUID magnetometer. Our results indicated significant differences on the magnetic propreties, in connection with the calcination temperature and the pressure used to pelletize the samples. This contribution is part of an effort to study vortex dynamics and magnetic properties of submicron and mesoscopic-size superconducting samples.

  14. Epitaxial ternary nitride thin films prepared by a chemical solution method

    Energy Technology Data Exchange (ETDEWEB)

    Luo, Hongmei [Los Alamos National Laboratory; Feldmann, David M [Los Alamos National Laboratory; Wang, Haiyan [TEXAS A& M; Bi, Zhenxing [TEXAS A& M

    2008-01-01

    It is indispensable to use thin films for many technological applications. This is the first report of epitaxial growth of ternary nitride AMN2 films. Epitaxial tetragonal SrTiN2 films have been successfully prepared by a chemical solution approach, polymer-assisted deposition. The structural, electrical, and optical properties of the films are also investigated.

  15. Improvement of physical properties of IGZO thin films prepared by excimer laser annealing of sol–gel derived precursor films

    International Nuclear Information System (INIS)

    Tsay, Chien-Yie; Huang, Tzu-Teng

    2013-01-01

    Indium gallium zinc oxide (IGZO) transparent semiconductor thin films were prepared by KrF excimer laser annealing of sol–gel derived precursor films. Each as-coated film was dried at 150 °C in air and then annealed using excimer laser irradiation. The influence of laser irradiation energy density on surface conditions, optical transmittances, and electrical properties of laser annealed IGZO thin films were investigated, and the physical properties of the excimer laser annealed (ELA) and the thermally annealed (TA) thin films were compared. Experimental results showed that two kinds of surface morphology resulted from excimer laser annealing. Irradiation with a lower energy density (≤250 mJ cm −2 ) produced wavy and irregular surfaces, while irradiation with a higher energy density (≥350 mJ cm −2 ) produced flat and dense surfaces consisting of uniform nano-sized amorphous particles. The explanation for the differences in surface features and film quality is that using laser irradiation energy to form IGZO thin films improves the film density and removes organic constituents. The dried IGZO sol–gel films irradiated with a laser energy density of 350 mJ/cm 2 had the best physical properties of all the ELA IGZO thin films. The mean resistivity of the ELA 350 thin films (4.48 × 10 3 Ω cm) was lower than that of TA thin films (1.39 × 10 4 Ω cm), and the average optical transmittance in the visible range (90.2%) of the ELA 350 thin films was slightly higher than that of TA thin films (89.7%). - Highlights: • IGZO semiconductor films were prepared by laser annealing of sol–gel derived films. • Surface roughness and resistivity of ELA samples were affected by energy density. • The ELA 350 IGZO film exhibited the best properties among all of ELA IGZO films. • Transmittance and resistivity of ELA 350 films are greater than those of TA films

  16. Preparation and characterization of thick BSCCO 2223 films

    International Nuclear Information System (INIS)

    Ciancio, G; Avila, A; Malachevsky, M.T; Ovidio, C.A

    2002-01-01

    Among the most widespread applications for critical high-temperature ceramic superconductors are for silver veined tapes, with the superconductor in the middle. These tapes are prepared by the powder- in - tube method. To attain high densities of critical current, the ceramic material must have a certain texture, with the grains oriented with the c axis perpendicular to the direction in which the current circulates. In the system that was studied, the degree of orientation increases as the distance to the vein decreases, with the maximum being in the silver-ceramic inter-phase. Superconductor tapes become inconvenient when defining the ceramic, especially because of the orientation of their plates as a function of the distance to the silver. Although the silver can be dissolved by a chemical attack in order to uncover the ceramic, greater precaution is needed while manipulating the superconductor and obtaining representative data. The behavior of thick films of the compound BSCCO 2223, deposited on silver sheets, forming silver-ceramic composites, was studied. These sheets simulate the silver-ceramic inter-phase and the distribution of the grains towards the center in a thick tape. After the samples were prepared, the phases that were present were characterized by x-ray diffraction and the resulting microstructure was analyzed with a SEM (Scanning Electron Microscope). Its mechanical properties were evaluated, following the formation and propagation of cracks in real time using four point flexion microassays inside the SEM chamber, as well as generating tension-deformation curves. The method of preparation of the thick films is discussed and its influence on the results obtained with the different characterizations (cw)

  17. Preparation and characterisation of Al-doped Zn O thin films

    International Nuclear Information System (INIS)

    Saad, M.; Kassis, A.; Nounou, F.

    2010-12-01

    Al-doped Zn O thin films were prepared using RF magnetron sputtering under several preparation conditions (deposition pressure, RF power, substrate temperature). The films were optically and electrically characterized by measuring their transmission and resistance. Furthermore, x-ray diffraction spectroscopy was used in order to study the structural properties of these films. As a result of this study, the preparation conditions suitable for the highly conductive part of the window layer in solar cells were determined. (author)

  18. Surface Properties of a Novel Poly(vinyl alcohol Film Prepared by Heterogeneous Saponification of Poly(vinyl acetate Film

    Directory of Open Access Journals (Sweden)

    Seong Baek Yang

    2017-10-01

    Full Text Available Almost general poly(vinyl alcohol (PVA films were prepared by the processing of a PVA solution. For the first time, a novel poly(vinyl alcohol (PVA film was prepared by the saponification of a poly(vinyl acetate (PVAc film in a heterogenous medium. Under the same saponification conditions, the influence of saponification time on the degree of saponification (DS was studied for the preparation of the saponified PVA film, and it was found that the DS varied with time. Optical microscopy was used to confirm the characteristics and surface morphology of the saponified PVA film, revealing unusual black globules in the film structure. The contact angle of the films was measured to study the surface properties, and the results showed that the saponified PVA film had a higher contact angle than the general PVA film. To confirm the transformation of the PVAc film to the PVA film, 1H nuclear magnetic resonance spectroscopy, X-ray diffraction measurements, differential scanning calorimetry, and Fourier-transform infrared spectroscopy were employed.

  19. Texture control and growth mechanism of WSe{sub 2} film prepared by rapid selenization of W film

    Energy Technology Data Exchange (ETDEWEB)

    Li, Hongchao [State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China); Chongyi Zhangyuan Tungsten Industry Corporation Limited, Ganzhou 341300 (China); Gao, Di; Li, Kun; Pang, Mengde; Xie, Senlin [State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China); Liu, Rutie, E-mail: llrrtt@csu.edu.cn [State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China); Zou, Jianpeng [State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China)

    2017-02-01

    Highlights: • We present a highly efficient method for preparing WSe{sub 2} film by rapid selenization. • The W film phase composition has little effect on WSe{sub 2} film orientation. • W film density is a critical factor that influences the WSe{sub 2} orientation. • A growth model was proposed for two kinds of WSe{sub 2} film textures. - Abstract: The tungsten diselenide (WSe{sub 2}) films with different orientation present unique properties suitable for specific applications, such as WSe{sub 2} with a C-axis⊥substrate for optoelectronics and WSe{sub 2} with a C-axis // substrate for electrocatalysts. Orientation control of WSe{sub 2} is essential for realizing the practical applications. In this letter, a WSe{sub 2} film has been prepared via rapid selenization of a magnetron-sputtered tungsten (W) film. The influence of the magnetron-sputtered W film on WSe{sub 2} film growth was studied systematically. Scanning electron microscopy, X-ray diffractometry and high-resolution transmission electron microscopy were used to evaluate the morphology, microstructure and phase composition of the W and WSe{sub 2} films. The substrate temperature has a significant effect on the W film phase composition, but little effect on the WSe{sub 2} film orientation. The WSe{sub 2} orientation can be controlled by changing the W film microstructure. A dense W film that is deposited at low pressure is conducive to the formation of WSe{sub 2} with a C-axis⊥substrate, whereas a porous W film deposited at high pressure favors the formation of WSe{sub 2} with a C-axis // substrate. A growth model for the WSe{sub 2} film with different texture has been proposed based on the experimental results. The direction of selenium (Se) vapor diffusion differs at the top and side surfaces. This is a key factor for the preparation of anisotropic WSe{sub 2} films. Highly oriented WSe{sub 2} films with a C-axis⊥substrate grow from the dense W film deposited at low pressure because Se vapor

  20. Detection of smaller Jc region and damage in YBCO coated conductors by using permanent magnet method

    International Nuclear Information System (INIS)

    Hattori, K.; Saito, A.; Takano, Y.; Suzuki, T.; Yamada, H.; Takayama, T.; Kamitani, A.; Ohshima, S.

    2011-01-01

    We developed a non-destructive method for measuring the critical current density (J c ) in YBCO-coated conductors by using a permanent magnet (Sm 2 Co 17 ). J c could be determined from the repulsive force (F r ) generated between a permanent magnet and a coated conductor where shielding current flows. We also examined the influence of damage to the film on the J c distribution. The measured F r when the permanent magnet approached the cut part was smaller than that of the undamaged area. We developed a non-destructive method for measuring the critical current density (J c ) in YBCO-coated conductors by using a permanent magnet (Sm 2 Co 17 ). J c could be determined from the repulsive force (F r ) generated between a permanent magnet and a coated conductor where shielding current flows. We tried to detect a smaller J c region in the coated conductor by using the system. The J c distribution could be determined without influence from the thick copper film on YBCO thin film. We also examined the influence of damage to the film on the J c distribution. The surface of the coated conductors was cut by using a knife. The measured F r when the permanent magnet approached the cut part was smaller than that of the undamaged area. This J c measurement technique will be useful for detecting smaller J c regions and defects in coated conductors.

  1. Preparation and properties of Y{sub 1-x}Ho{sub x}Ba{sub 2}Cu{sub 3}O{sub 7-{delta}} thin films by TFA-MOD method

    Energy Technology Data Exchange (ETDEWEB)

    Jian Hongbin [Key Laboratory of Materials Physics, Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031 (China); Li Qi; Shi Dongqi [Institute for Superconducting and Electronic Materials, University of Wollongong, Wollongong 2522 (Australia); Zhang Li [Department of Mathematic and Physics, Anhui University of Architecture, Hefei 230022 (China); Yang Zhaorong [Key Laboratory of Materials Physics, Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031 (China); Dou Shixue [Institute for Superconducting and Electronic Materials, University of Wollongong, Wollongong 2522 (Australia); Zhu Xuebin, E-mail: xbzhu@issp.ac.cn [Key Laboratory of Materials Physics, Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031 (China); Sun Yuping [Key Laboratory of Materials Physics, Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031 (China)

    2011-12-15

    Y{sub 1-x}Ho{sub x}BCO thin films were prepared by TFA-MOD. The best performances were obtained for the Y{sub 0.6}Ho{sub 0.4}BCO thin film. The pinning mechanism was {delta}l-type for all derived thin films. Y{sub 1-x}Ho{sub x}Ba{sub 2}Cu{sub 3}O{sub 7-{delta}} (x = 0, 0.1, 0.2, 0.3, 0.4, 0.5) thin films were prepared on LaAlO{sub 3} (0 0 1) substrates by trifluoroacetate metal organic deposition (TFA-MOD) without change of the processing parameters. The highest J{sub c} was attributed to the sample of Y{sub 0.6}Ho{sub 0.4}Ba{sub 2}Cu{sub 3}O{sub 7-{delta}} thin film, whose critical current density is about 1.6 times as compared to that of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} thin film at 77 K and self field. The flux pinning type was not varied with Ho substitution and can be attributed to {delta}l pinning model, which is attributed to the close ionic radius between the Y{sup 3+} and Ho{sup 3+} ions. The improvement of J{sub c} by Ho substitution without change of the processing parameters will provide an effective route to enhance the J{sub c} of YBCO-based thin films using TFA-MOD method.

  2. Preparation and Characterization of Some Polyethylene Modified- Starch Biodegradable Films

    International Nuclear Information System (INIS)

    Badrana, A.S.; Ramadanb, A.M.; Ibrahim, N.A.; Kahild, T.; Hussienc, H.A.

    2005-01-01

    Blends of LDPE with soluble starch, wheat flour and commercial starch were prepared by mixing starch (or flour) with styrene then blending the mixture with LDPE, The starch percents vary between 5 and 50% of the total weight. Their physical and mechanical properties were recorded and compared with pure LDPE. It was observed that the increase in starch or wheat flour contents of the mixture was reversibly proportional to the tensile strength and % elongation. Samples were tested for water absorption. All of the samples were insoluble in cold and boiling water. Moisture uptake increased with immersion time and increasing starch content. The changes in the tensile strength of LDPE/starch (or wheat flour) after the course of thermal oxidation was measured. These results show negligible changes in the tensile strength of the control sample as compared to that of the samples containing the additives. Oxidation processes take advantage of the high temperatures (40-50 degree C) and the time. It was also observed that after 10 weeks of soil burial, the mechanical properties of the films decrease, mainly, due to starch removal from the films. Also, for the weight loss a drastic decrease was observed after 10 weeks of soil burial thereafter it preceded slowly. The LDPE/ starch strips showed weight loss after treating with a-amylase this due to hydrolysis and leaching of the starch. The rate of starch hydrolysis increases with the increase in starch content of the sample. The influence of addition of starch on the overall migration of these films, with different food simulant, was studied, at different temperatures (-4 degree. 25 degree and 40 degree C). All values were significantly lower than the upper limit for overall migration set by the EU (10 mg/dirf) for food grade plastics packaging materials

  3. Niobium and zirconium telluride thin films prepared by sputtering

    International Nuclear Information System (INIS)

    Kassem, M.; Pailharey, D.; Mathey, Y.

    2000-01-01

    A versatile procedure of sputter deposition, well adapted for getting a large of Te/M ratios (with M = Zr or Nb), has led to the synthesis of several highly anisotropic zirconium and niobium poly tellurides in thin film form. Upon tuning the two key parameters of the process, i.e., the Te percentage in the target and the substrate temperature during the deposition, preparation of systems ranging from ZrTe 0 .72 to ZrTe 6 .7, on the one hand, and from NbTe 1 .28 to NbTe 7 .84, on the other, has been achieved. Besides their amorphous or crystalline (with or without preferential orientations) behavior and their relationship to known structural types, the most striking feature of these films is their large departure from the stoichiometry of the bulk Mte x reference compounds. This peculiarity, together with the possible changes of composition under annealing, are described and interpreted in terms of variable of Te and M atoms trapped or intercalated within the parent structures. (author)

  4. Flux pinning characteristics of YBCO coated conductor

    International Nuclear Information System (INIS)

    Matsushita, T.; Watanabe, T.; Fukumoto, Y.; Yamauchi, K.; Kiuchi, M.; Otabe, E.S.; Kiss, T.; Watanabe, T.; Miyata, S.; Ibi, A.; Muroga, T.; Yamada, Y.; Shiohara, Y.

    2005-01-01

    Flux pinning properties of PLD-processed YBCO coated conductors deposited on IBAD substrate are investigated. The thickness of YBCO layer is changed in the range of 0.27-1.0 μm. The thickness dependence of critical current density, n-value and irreversibility field are measured in a wide range of magnetic field. The results are compared with the theoretical flux creep-flow model. It is found that these pinning properties are strongly influenced by the thickness as well as the pinning strength. Optimum condition for high field application of this superconductor is discussed

  5. Theoretical analysis of a YBCO squirrel-cage type induction motor based on an equivalent circuit

    International Nuclear Information System (INIS)

    Morita, G; Nakamura, T; Muta, I

    2006-01-01

    A HTS induction motor, with a HTS squirrel-cage rotor, is analysed using an electrical equivalent circuit. The squirrel-cage winding in the rotor consists of rotor bars and end rings, and both are considered to be made of YBCO film conductors. A wide range of electric field versus current density in YBCO film is formulated based on the Weibull function, and analysed as a non-linear resistance in the equivalent circuit. It is shown that starting and accelerating torques of the HTS induction motor are improved drastically compared to those of a conventional induction motor. Furthermore, large synchronous torque can also be realized by trapping the magnetic flux in the rotor circuit because of the persistent current mode

  6. TiCx thin films coatings prepared by reactive sputtering

    International Nuclear Information System (INIS)

    Saoula, N.; Handa, K.; Kesri, R.

    2004-01-01

    demonstrate clearly the great influence of the variation of different parameters (deposition time, RF power, total pressure, gas mixture (Ar+CH 4 ) on the film growth rates and thickness. The aim of present work is to study their influence of gas mixture, more specifically of carbon content on the structure, composition and the hardness of TiC coatings, prepared using an RF sputtering system

  7. Characterization of film-forming solutions and films incorporating free and nanoencapsulated tea polyphenol prepared by gelatins with different Bloom values

    Science.gov (United States)

    Gelatin film-forming solutions and their films incorporating tea polyphenol (TP) and chitosan nanoparticles (CSNs) were prepared from gelatins with different Bloom values (100, 150 and 225). Blank gelatin film-forming solutions and films were prepared as controls. Gelatins with higher Bloom values h...

  8. Jc enhancement by La-Al-O doping in Y-Ba-Cu-O films both in self-field and under magnetic field

    DEFF Research Database (Denmark)

    Xu, Yan; Suo, Hong-Li; Yue, Zhao

    2016-01-01

    a good epitaxial growth relationship with LAO. Compared with a pure YBCO film, the Jc value of a 5.0% LAO-doped sample is enhanced more than three times in self-field 77 K and seven times at 77 K and 1.5 T, respectively. These results indicate that LAO doping can effectively enhance the Jc of YBCO films...... toward YBCO. A series of YBCO films with different LAO doping contents was fabricated on LAO single-crystal substrates by metal organic deposition. We observed by X-ray diffractometer measurements and scanning electron microscopy observations that although a large amount of LAO is added, YBCO still keeps...

  9. Polysulfobetaine films prepared by electrografting technique for reduction of biofouling on electroconductive surfaces

    International Nuclear Information System (INIS)

    Stach, Marek; Kronekova, Zuzana; Kasak, Peter; Kollar, Jozef; Pentrak, Martin; Micusik, Matej; Chorvat, Dusan; Nunney, Tim S.; Lacik, Igor

    2011-01-01

    The sulfobetaine films were prepared on stainless steel and golden surfaces. In the first step, the poly(2-(dimethylamino)ethyl methacrylate) film was created by employing the electrografting polymerization technique. In the second step, this film was modified to polysulfobetaine, i.e. the polymer film bearing the zwitterionic groups. The presence of the electrografted film and its modification were determined by contact angle measurements, infrared spectroscopy in reflectance mode and X-ray photoelectron spectroscopy. The prepared films were homogeneous with the thickness from about 5 to 26 nm as determined by X-ray photoelectron spectroscopy. The atomic force microscopy measurements showed the increase of surface roughness upon the surface coating. In vitro tests using adherent RAT-2 fibroblast cells and fluorescently labelled bovine serum albumin proteins showed that prepared polysulfobetaine films can be used in applications requiring the resistance against cell attachment and biofouling.

  10. Titanium-silicon films prepared by spin and dip-coating

    International Nuclear Information System (INIS)

    Nassar, Eduardo J.; Ciuffi, Katia J.; Goncalves, Rogeria R.; Messaddeq, Younes; Ribeiro, Sidney J.L.

    2003-01-01

    The conditions for the preparation of luminescent materials, consisting of Eu 3+ ions entrapped in a titanium matrix, in the form of a thin film, using the sol-gel process, are described. The films were obtained from sols prepared with TEOS and TEOT, in the presence of acetylacetone as the hydrolysis-retarding agent, using the dip-coating and spin-coating techniques. The influence of these techniques on the films based on titanium and silicon are presented. The Eu 3+ was used as a luminescent probe. The films have been characterized by luminescence, reflection and transmittance. The thickness of the films could be related to the preparation procedure. Transparent thin films have been prepared by dip-coating technique. (author)

  11. Point defects in MnSi and YBCO studied by Doppler Broadening Spectroscopy using a positron beam

    Energy Technology Data Exchange (ETDEWEB)

    Reiner, Markus

    2015-10-28

    The positron beam NEPOMUC was used in order to investigate MnSi and YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO) single crystals. The Doppler broadening of the annihilation radiation of electron-positron pairs was analyzed. Thus, the concentration of Mn vacancies in MnSi crystals was determined. In thin YBCO films, the Doppler broadening is correlated with the oxygen deficiency δ. Its spatial distribution and its high-temperature behavior were studied using positrons.

  12. Preparation of transparent conducting zinc oxide films by rf reactive sputtering

    International Nuclear Information System (INIS)

    Vasanelli, L.; Valentini, A.; Losacco, A.

    1986-01-01

    Transparent conducting zinc oxide films have been prepared by reactive sputtering in a Ar/H/sub 2/ mixture. The optical and electrical properties of the films are presented and discussed. The effects of some post-deposition thermal treatment have been also investigated. ZnO/CdTe heterojunctions have been prepared by sputtering ZnO films on CdTe single crystals. The photovoltaic conversion efficiencies of the obtained solar cells was 6.8%

  13. AFM plough YBCO micro bridges: substrate effects

    CSIR Research Space (South Africa)

    Elkaseh, A

    2009-04-01

    Full Text Available AFM nanolithography was used as a novel cutting technique to define micro-size YBCO superconducting constrictions. Researchers studied the substrate effects on MgO and STO substrates and showed that the observed Shapiro steps from the bridges on STO...

  14. Measurement of noise in YBCO bi-crystal junctions

    International Nuclear Information System (INIS)

    Kuznik, J.; Hao, L.; Macfarlane, J.C.; Pegrum, C.M.; Fischer, G.M.; Mygind, J.; Pedersen, N.F.; Beck, A.; Gross, R.

    1993-01-01

    This paper describes collaborative work between three institutions as part of an ESPRIT programme to fabricate and characterise grain-boundary junctions. Bi-crystal junctions were fabricated at Tuebingen on SrTiO 3 substrates with a 24 misorientation angle and a-b tilt. 200nm of c-axis YBCO was sputter-deposited using a hollow-cathode magnetron, and the films patterned with optical lithography and Ar ion beam etching (3). For test purposes junctions with a range of sizes were made, with widths between 4 and 20μm. These have been characterised for noise properties at 0.3 - 1kHz and 60kHz at Strathclyde, and at 70GHz at Lyngby. (orig.)

  15. Preparation and adsorption properties of nano magnetite chitosan films for heavy metal ions from aqueous solution

    Energy Technology Data Exchange (ETDEWEB)

    Lasheen, M.R., E-mail: ragaei24@link.net [Water Pollution Research Department, Environmental Research Division, National Research Centre, 33-El Buhoth St., Dokki, Cairo, 12311 (Egypt); El-Sherif, Iman Y., E-mail: iman57us@yahoo.com [Water Pollution Research Department, Environmental Research Division, National Research Centre, 33-El Buhoth St., Dokki, Cairo, 12311 (Egypt); Tawfik, Magda E., E-mail: magdaemileta@yahoo.com [Polymers and Pigments Department, National Research Centre, 33-El Buhoth St., Dokki, Cairo, 12311 (Egypt); El-Wakeel, S.T., E-mail: shaimaa_tw@yahoo.com [Water Pollution Research Department, Environmental Research Division, National Research Centre, 33-El Buhoth St., Dokki, Cairo, 12311 (Egypt); El-Shahat, M.F., E-mail: elshahatmf@hotmail.com [Faculty of Science, Ain Shams University, Khalifa El-Maamon St., Abbasiya Sq., 11566, Cairo (Egypt)

    2016-08-15

    Highlights: • Nano magnetite–chitosan films were prepared by casting method. • The efficiency of the prepared films for removing heavy metals was investigated. • The adsorption mechanism was studied using different isotherm and kinetic models. • Films reuse and metals recovery were studied. - Abstract: Nano magnetite chitosan (NMag–CS) film was prepared and characterized with different analytical methods. X-ray diffraction (XRD) patterns confirmed the formation of a pure magnetite structure and NMag–CS nanocomposite. TEM image of the film, revealed the uniform dispersion of magnetite nanoparticles inside chitosan matrix. The adsorption properties of the prepared film for copper, lead, cadmium, chromium and nickel metal ions were evaluated. Different factors affecting the uptake behavior by the composite films such as time, initial pH and film dose were investigated. The adsorption equilibrium attained using 2 g/L of the film after 120 min of reaction. The equilibrium data were analyzed using Langmuir and Freundlich models. The adsorption kinetics followed the mechanism of the pseudo-second-order equation for all metals. The metals regenerated from films with an efficiency greater than 95% using 0.1 M ethylene diamine tetra acetic acid (EDTA) and films were successfully reused for adsorption.

  16. Improvement of physical properties of IGZO thin films prepared by excimer laser annealing of sol–gel derived precursor films

    Energy Technology Data Exchange (ETDEWEB)

    Tsay, Chien-Yie, E-mail: cytsay@fcu.edu.tw; Huang, Tzu-Teng

    2013-06-15

    Indium gallium zinc oxide (IGZO) transparent semiconductor thin films were prepared by KrF excimer laser annealing of sol–gel derived precursor films. Each as-coated film was dried at 150 °C in air and then annealed using excimer laser irradiation. The influence of laser irradiation energy density on surface conditions, optical transmittances, and electrical properties of laser annealed IGZO thin films were investigated, and the physical properties of the excimer laser annealed (ELA) and the thermally annealed (TA) thin films were compared. Experimental results showed that two kinds of surface morphology resulted from excimer laser annealing. Irradiation with a lower energy density (≤250 mJ cm{sup −2}) produced wavy and irregular surfaces, while irradiation with a higher energy density (≥350 mJ cm{sup −2}) produced flat and dense surfaces consisting of uniform nano-sized amorphous particles. The explanation for the differences in surface features and film quality is that using laser irradiation energy to form IGZO thin films improves the film density and removes organic constituents. The dried IGZO sol–gel films irradiated with a laser energy density of 350 mJ/cm{sup 2} had the best physical properties of all the ELA IGZO thin films. The mean resistivity of the ELA 350 thin films (4.48 × 10{sup 3} Ω cm) was lower than that of TA thin films (1.39 × 10{sup 4} Ω cm), and the average optical transmittance in the visible range (90.2%) of the ELA 350 thin films was slightly higher than that of TA thin films (89.7%). - Highlights: • IGZO semiconductor films were prepared by laser annealing of sol–gel derived films. • Surface roughness and resistivity of ELA samples were affected by energy density. • The ELA 350 IGZO film exhibited the best properties among all of ELA IGZO films. • Transmittance and resistivity of ELA 350 films are greater than those of TA films.

  17. Electrochemical preparation of poly(methylene blue)/graphene nanocomposite thin films

    International Nuclear Information System (INIS)

    Erçarıkcı, Elif; Dağcı, Kader; Topçu, Ezgi; Alanyalıoğlu, Murat

    2014-01-01

    Highlights: • Poly(MB)/graphene thin films are prepared by a simple electrochemical approach. • Graphene layers in the film show a broad band in visible region of absorbance spectra. • Morphology of composite films indicates both disordered and ordered regions. • XRD reveals that nanocomposite films include rGO layers after electropolymerization process. • Chemically prepared graphene is better than electrochemically prepared graphene for electrooxidation of nitrite. - Abstract: Poly(methylene blue)/graphene nanocomposite thin films were prepared by electropolymerization of methylene blue in the presence of graphene which have been synthesized by two different methods of a chemical oxidation process and an electrochemical approach. Synthesized nanocomposite thin films were characterized by using cyclic voltammetry, UV–vis. absorption spectroscopy, powder X-ray diffraction, and scanning tunneling microscopy techniques. Electrocatalytical properties of prepared poly(methylene blue)/graphene nanocomposite films were compared toward electrochemical oxidation of nitrite. Under optimized conditions, electrocatalytical effect of nanocomposite films of chemically prepared graphene through electrochemical oxidation of nitrite was better than that of electrochemically prepared graphene

  18. Effect of magnetic field on the growth of Be films prepared by thermal evaporation

    International Nuclear Information System (INIS)

    Li, Kai; Luo, Bing-chi; Tan, Xiu-lan; Zhang, Ji-qiang; Wu, Wei-dong; Liu, Ying

    2014-01-01

    Highlights: • The Be films were prepared on Si (1 0 0) substrates with and without a magnetic field by thermal evaporation, respectively. • The grain diameter in the Be film transited from 300 nm to 18 nm by application of the magnetic field. • The surface roughness of the Be film decreased from 61 nm to 3 nm by application of the magnetic field. • The Be film grown with the magnetic field was easily oxidized due to its refined grains and the oxidation was gradually decreased with increasing the etching depth in the film. - Abstract: Grain refinement of beryllium deposits is studied as a significant subject for beryllium capsule in the Inertial Confinement Fusion project. The Be films were prepared on the Si (1 0 0) substrates by thermal evaporation with and without a magnetic field, respectively. The two separate groups of prepared Be films were characterized. The results showed the grain diameter in the Be film transited from 300 nm to 18 nm and the surface roughness of the Be film decreased from 61 nm to 3 nm by application of the magnetic field during the deposition process of Be coating. However, the Be film grown with the magnetic field was easily oxidized in comparison with that grown without magnetic field due to the refined grains, and the oxidation was gradually decreased with the increase of etching depth in the Be film. The reason for grain refinement of Be film was also qualitatively described

  19. Preparation of Surlyn films reinforced with cellulose nanofibres and feasibility of applying the transparent composite films for organic photovoltaic encapsulation

    Science.gov (United States)

    Lertngim, Anantaya; Phiriyawirut, Manisara; Wootthikanokkhan, Jatuphorn; Yuwawech, Kitti; Sangkhun, Weradesh; Kumnorkaew, Pisist; Muangnapoh, Tanyakorn

    2017-10-01

    This research concerns the development of Surlyn film reinforced with micro-/nanofibrillated celluloses (MFC) for use as an encapsulant in organic photovoltaic (OPV) cells. The aim of this work was to investigate the effects of fibre types and the mixing methods on the structure-properties of the composite films. Three types of cellulose micro/nanofibrils were prepared: the as-received MFC, the dispersed MFC and the esterified MFC. The fibres were mixed with Surlyn via an extrusion process, using two different mixing methods. It was found that the extent of fibre disintegration and tensile modulus of the composite films prepared by the master-batching process was superior to that of the composite system prepared by the direct mixing method. Using the esterified MFC as a reinforcement, compatibility between polymer and the fibre increased, accompanied with the improvement of the percentage elongation of the Surlyn composite film. The percentage of light transmittance of the Surlyn/MFC films was above 88, regardless of the fibre types and fibre concentrations. The water vapour transmission rate of the Surlyn/esterified MFC film was 65% lower than that of the neat Surlyn film. This contributed to the longer lifetime of the OPV encapsulated with the Surlyn/esterified MFC film.

  20. Preparation and Properties of Silver Nanowire-Based Transparent Conductive Composite Films

    Science.gov (United States)

    Tian, Ji-Li; Zhang, Hua-Yu; Wang, Hai-Jun

    2016-06-01

    Silver nanowire-based transparent conductive composite films with different structures were successfully prepared using various methods, including liquid polyol, magnetron sputtering and spin coating. The experimental results revealed that the optical transmittance of all different structural composite films decreased slightly (1-3%) compared to pure films. However, the electrical conductivity of all composite films had a great improvement. Under the condition that the optical transmittance was greater than 78% over the wavelength range of 400-800 nm, the AgNW/PVA/AgNW film became a conductor, while the AZO/AgNW/AZO film and the ITO/AgNW/ITO film showed 88.9% and 94% reductions, respectively, for the sheet resistance compared with pure films. In addition, applying a suitable mechanical pressure can improve the conductivity of AgNW-based composite films.

  1. Preparation and properties of carbohydrate-based composite films incorporated with CuO nanoparticles.

    Science.gov (United States)

    Shankar, Shiv; Wang, Long-Feng; Rhim, Jong-Whan

    2017-08-01

    The present study aimed to develop the carbohydrate biopolymer based antimicrobial films for food packaging application. The nanocomposite films of various biopolymers and copper oxide nanoparticles (CuONPs) were prepared by solvent casting method. The nanocomposite films were characterized using SEM, FTIR, XRD, and UV-vis spectroscopy. The thermal stability, UV barrier, water vapor permeability, and antibacterial activity of the composite films were also evaluated. The surface morphology of the films was dependent on the types of polymers used. The XRD revealed the crystallinity of CuONPs in the composite films. The addition of CuONPs increased the thickness, tensile strength, UV barrier property, relative humidity, and water vapor barrier property. The CuONPs incorporated composite films exhibited strong antibacterial activity against Escherichia coli and Listeria monocytogenes. The developed composite films could be used as a UV-light barrier antibacterial films for active food packaging. Copyright © 2017 Elsevier Ltd. All rights reserved.

  2. Analysis of NdFeB thin films prepared by facing target sputtering

    International Nuclear Information System (INIS)

    Shivalingappa, L.; Mohan, S.; Ghantasala, M.K.; Sood, D.K.

    1999-01-01

    In this paper, we present the details of our work on the deposition and characterization of NdFeB thin films. These films were prepared using facing target sputtering technique. The silicon(100) substrates were maintained at a substrate temperature of 400 to 600 deg C during deposition. Film structure, composition and magnetic properties are analyzed using Rutherford Backscattering Spectroscopy (RBS) and X-ray Diffraction (XRD) techniques. Films deposited below 400 deg C were x-ray amorphous, while the onset of crystallinity was observed with the films deposited at 500 deg C. Typical film composition was Nd:Fe:B = 2.2:12.5:2. Film composition appear to be a function of deposition conditions. Oxygen has been found to be the main impurity in the films. Oxygen content in the film reduced as the substrate temperature is increased

  3. Hydroxyapatite coatings on titanium dioxide thin films prepared by pulsed laser deposition method

    International Nuclear Information System (INIS)

    Suda, Yoshiaki; Kawasaki, Hiroharu; Ohshima, Tamiko; Nakashima, Shouta; Kawazoe, Syuichi; Toma, Tetsuya

    2006-01-01

    Hydroxyapatite (HAp) coated on titanium dioxide (TiO 2 ) thin films has been developed to supplement the defects of both TiO 2 and HAp. Thin films have been prepared by pulsed laser deposition (PLD) method using HAp and HAp(10%) + TiO 2 targets. X-ray diffraction (XRD) shows that there are many small peaks of Ca 1 0(PO 4 ) 6 (OH) 2 crystal, and no impurity other than HAp is detected in HAp films prepared using pure HAp target. The composition ratio of the film was analyzed by X-ray photoelectron spectroscopy (XPS). HAp coatings on TiO 2 thin films have been prepared using HAp(10%) + TiO 2 targets. XRD and XPS measurements suggest that crystalline HAp + TiO 2 thin films are obtained by the PLD method using HAp(10%) + TiO 2 target

  4. Preparation, characterization and optical properties of Gadolinium doped ceria thin films by pulsed laser deposition technique

    International Nuclear Information System (INIS)

    Nagaraju, P.; Vijaya Kumar, Y.; Vishnuvardhan Reddy, C.; Ramana Reddy, M.V.; Phase, D.M; Raghavendra Reddy, V.

    2013-01-01

    The growth of Gadolinium doped ceria thin films with controlled surface structure for device quality applications presents a significant problem for experimental investigation. In the present study gadolinium doped cerium oxide thin films were prepared by pulsed laser deposition (PLD) and were studied for their surface structure evaluation in relation to the optimized operating conditions during the stage of film preparation. The deposition was made with gadolinium concentration of 10 mole% to ceria pellets. The films were deposited on quartz substrate in the presence of oxygen partial pressure of 1.5 x 10 -3 torr using KrF Excimer laser with laser energy 220 mJ at a substrate temperature 700℃. The effect of annealing temperature on 10 mole% GDC thin film was investigated. The film thickness was measured by using AMBIOS make XP-l stylus profiler. As prepared and annealed thin films were characterized for crystallinity, particle size and orientation by using G.I.XRD. The films were characterized using atomic force microscopy (AFM). The AFM results gave a consistent picture of the evolution of GDC film surface morphologies and microstructures in terms of surface roughness, grain distribution and mean grain size. The optical transmittance spectra was used to determine the optical constants such as optical band gap, refractive index, extinction coefficient of as prepared and annealed thin films. (author)

  5. Preparation and characterization of porphyrin-polythiophene stacked films as prepared by electrochemical method under stirring condition

    International Nuclear Information System (INIS)

    Sugawa, Kosuke; Akiyama, Tsuyoshi; Yamada, Sunao

    2008-01-01

    Porphyrin-polythiophene (pTh) stacked films consisting of meso-tetrathienylporphyrin (TThP) and bithiophene (BiTh) were prepared on transparent indium-tin-oxide (ITO) electrodes by sequential electrochemical scanning of applied potential between 0 and + 2 V vs Ag wire in the electrolyte solution of BiTh and TThP under stirring condition. First, the pTh films were prepared by electrochemical polymerization and then TThP was incorporated into the as-prepared pTh film by subsequent electrochemical scanning as described above in the TThP solution. The operation of solution stirring during electrochemical scanning achieved the formation of robust stacked films. UV/Vis and fluorescence spectra confirmed that the amount of TThP moiety increased with increasing the number of electrochemical scanning cycles in the TThP solution. In order to evaluate the incorporation profile of TThP, surface analyses and depth profiles of stacked films were carried out by XPS spectroscopy. The results suggested that all films formed porphyrin-polythiophene stacked structure precisely, and that TThP was exclusively incorporated around the outermost region of the pTh film

  6. Preparation of anatase TiO2 thin films by vacuum arc plasma evaporation

    International Nuclear Information System (INIS)

    Miyata, Toshihiro; Tsukada, Satoshi; Minami, Tadatsugu

    2006-01-01

    Anatase titanium dioxide (TiO 2 ) thin films with high photocatalytic activity have been prepared with deposition rates as high as 16 nm/min by a newly developed vacuum arc plasma evaporation (VAPE) method using sintered TiO 2 pellets as the source material. Highly transparent TiO 2 thin films prepared at substrate temperatures from room temperature to 400 deg. C exhibited photocatalytic activity, regardless whether oxygen (O 2 ) gas was introduced during the VAPE deposition. The highest photocatalytic activity and photo-induced hydrophilicity were obtained in anatase TiO 2 thin films prepared at 300 deg. C, which correlated to the best crystallinity of the films, as evidenced from X-ray diffraction. In addition, a transparent and conductive anatase TiO 2 thin film with a resistivity of 2.6 x 10 -1 Ω cm was prepared at a substrate temperature of 400 deg. C without the introduction of O 2 gas

  7. Preparation of BiOBr thin films with micro-nano-structure and their photocatalytic applications

    Energy Technology Data Exchange (ETDEWEB)

    Li, Rui [College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Fan, Caimei, E-mail: fancm@163.com [College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Zhang, Xiaochao, E-mail: zhang13598124761@163.com [College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Wang, Yawen; Wang, Yunfang [College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Zhang, Hui [Particle Technology Research Centre, Department of Chemical and Biochemical Engineering, The University of Western Ontario, London, Ontario N6A 5B9 (Canada)

    2014-07-01

    A series of micro-nano-structure BiOBr thin films were prepared at a low temperature by the alcoholysis-coating method using BiBr{sub 3} as precursor. The as-prepared films were characterized by X-ray powder diffraction, scanning electron microscopy, and Brunauer–Emmett–Teller surface area. The obtained results indicated that micro-nano-structure tetragonal BiOBr films with different intensity ratios of (110) to (102) characteristic peaks could be synthesized through controlling the reaction temperature and the calcination temperatures. Furthermore, the photocatalytic activities of BiOBr thin films with different preparation conditions have been evaluated by the degradation of methyl orange (MO) under UV light irradiation, suggesting that the photocatalytic activity should be closely related to the solvent, the alcoholysis reaction temperature, and the calcining temperature. The best photocatalytic degradation efficiency of MO for BiOBr thin films reaches 98.5% under 2.5 h UV irradiation. The BiOBr thin films display excellent stability and their photocatalytic activity still remains above 90% after being used five times. The main reasons for the higher photocatalytic activity of micro-nano-structure BiOBr microspheres have been investigated. In addition, the possible formation mechanism of BiOBr thin films with micro-nano-structure and excellent photocatalytic activity was proposed and discussed. - Highlights: • The BiOBr film was prepared at low temperature via alcoholysis-coating method. • The optimum process conditions of preparing BiOBr film were discussed. • As-prepared BiOBr films were composed of micro-nano flake structures. • The BiOBr films demonstrated excellent photocatalytic activity. • The formation mechanism of BiOBr films with high activity was proposed.

  8. Characteristics of tungsten oxide thin films prepared on the flexible substrates using pulsed laser deposition

    International Nuclear Information System (INIS)

    Suda, Yoshiaki; Kawasaki, Hiroharu; Ohshima, Tamiko; Yagyuu, Yoshihito

    2008-01-01

    Tungsten trioxide (WO 3 ) thin films have been prepared on the flexible indium tin oxide (ITO) substrates by pulsed laser deposition (PLD) using WO 3 targets in oxygen gas. Color of the WO 3 film on the flexible ITO substrates depends on the oxygen gas mixture. The plasma plume produced by PLD using a Nd:YAG laser and WO 3 target is investigated by temporal and spatial-resolved optical emission spectroscopy. WO 3 films prepared on the flexible ITO substrates show electrochromic properties, even when the substrates are bent. The film color changes from blue to transparent within 10-20 s after the applied DC voltage is turned off

  9. Resistivity behavior of optimized PbTiO3 thin films prepared by spin coating method

    Science.gov (United States)

    Nurbaya, Z.; Wahid, M. H.; Rozana, M. D.; Alrokayan, S. A. H.; Khan, H. A.; Rusop, M.

    2018-05-01

    Th is study presents the resistivity behavior of PbTiO3 thin films which were prepared towards metal-insulator-metal capacitor device fabrication. The PbTiO3 thin films were prepared through sol-gel spin coating method that involved various deposition parameters that is (1) different molar concentration of PbTiO3 solutions, (2) various additional PbAc-content in PbTiO3 solutions, and (3) various annealing temperature on PbTiO3 thin films. Hence, an electrical measurement of current versus voltage was done to determine the resistivity behavior of PbTiO3 thin films.

  10. A methodology for the preparation of nanoporous polyimide films with low dielectric constants

    International Nuclear Information System (INIS)

    Jiang Lizhong; Liu Jiugui; Wu Dezhen; Li Hangquan; Jin Riguang

    2006-01-01

    A method to generate nanoporous polyimide films with low dielectric constants was proposed. The preparation consisted of two steps. Firstly, a polyimide/silica hybrid film was prepared via sol-gel process. Secondly, the hybrid film was treated with hydrofluoric acid to remove the dispersed silica particles, leaving pores with diameters between 20 and 120 nm, depending on the size of silica particles. Both hybrid and porous films were subjected to a variety of characterizations including transmission electron microscopy observation, dielectric constant measurement and tensile strength measurement

  11. Plasma-polymerized SiOx deposition on polymer film surfaces for preparation of oxygen gas barrier polymeric films

    International Nuclear Information System (INIS)

    Inagaki, N.

    2003-01-01

    SiOx films were deposited on surfaces of three polymeric films, PET, PP, and Nylon; and their oxygen gas barrier properties were evaluated. To mitigate discrepancies between the deposited SiOx and polymer film, surface modification of polymer films was done, and how the surface modification could contribute to was discussed from the viewpoint of apparent activation energy for the permeation process. The SiOx deposition on the polymer film surfaces led to a large decrease in the oxygen permeation rate. Modification of polymer film surfaces by mans of the TMOS or Si-COOH coupling treatment in prior to the SiOx deposition was effective in decreasing the oxygen permeation rate. The cavity model is proposed as an oxygen permeation process through the SiOx-deposited Nylon film. From the proposed model, controlling the interface between the deposited SiOx film and the polymer film is emphasized to be a key factor to prepare SiOx-deposited polymer films with good oxygen gas barrier properties. (author)

  12. Effect of the thickness of a fluoropolymer film on the radiotically prepared fuel cell membranes

    International Nuclear Information System (INIS)

    Ko, Beom Seok; Sohn, Joon Yong; Nho, Young Chang; Shin, Jun Hwa; Kim, Jong Il

    2010-01-01

    To observe the effect of the thickness of a fluoropolymer film on the radiotically prepared fuel cell membranes, fuel cell membranes with various thickness were prepared by simultaneous radiation grafting of styrene into polyethylene-co-tetrafluoroethylene (ETFE) with various thicknesses (25, 50 and 100 μm) and subsequent sulfonation. The physico-chemical properties of the prepared membranes such as ion exchange capacity, water uptake, distribution of sulfonic acid group were evaluated in the correlation with the thickness of ETFE film. In additions, proton conductivity and methanol permeability of the prepared membranes were also evaluated. The results revealed that the proton conductivity and methanol permeability of the prepared membranes were largely affected by the thickness of ETFE film utilized as a base film

  13. Effect of the thickness of a fluoropolymer film on the radiotically prepared fuel cell membranes

    Energy Technology Data Exchange (ETDEWEB)

    Ko, Beom Seok; Sohn, Joon Yong; Nho, Young Chang; Shin, Jun Hwa [Korea Atomic Energy Research Institute, Jeongeup (Korea, Republic of); Kim, Jong Il [Chonbuk National University, Jeonju (Korea, Republic of)

    2010-06-15

    To observe the effect of the thickness of a fluoropolymer film on the radiotically prepared fuel cell membranes, fuel cell membranes with various thickness were prepared by simultaneous radiation grafting of styrene into polyethylene-co-tetrafluoroethylene (ETFE) with various thicknesses (25, 50 and 100 {mu}m) and subsequent sulfonation. The physico-chemical properties of the prepared membranes such as ion exchange capacity, water uptake, distribution of sulfonic acid group were evaluated in the correlation with the thickness of ETFE film. In additions, proton conductivity and methanol permeability of the prepared membranes were also evaluated. The results revealed that the proton conductivity and methanol permeability of the prepared membranes were largely affected by the thickness of ETFE film utilized as a base film.

  14. Preparation of mesoporous silica thin films by photocalcination method and their adsorption abilities for various proteins

    Energy Technology Data Exchange (ETDEWEB)

    Kato, Katsuya, E-mail: katsuya-kato@aist.go.jp [National Institute of Advanced Industrial Science and Technology (AIST), 2266-98 Anagahora, Shimoshidami, Moriyama-ku, Nagoya 463-8560 (Japan); Nakamura, Hitomi [National Institute of Advanced Industrial Science and Technology (AIST), 2266-98 Anagahora, Shimoshidami, Moriyama-ku, Nagoya 463-8560 (Japan); Yamauchi, Yoshihiro; Nakanishi, Kazuma; Tomita, Masahiro [Department of Chemistry for Materials, Graduate School of Engineering, Mie University, 1577 Kurimamachiya-cho, Tsu, Mie 514-8570 (Japan)

    2014-07-01

    Mesoporous silica (MPS) thin film biosensor platforms were established. MPS thin films were prepared from tetraethoxysilane (TEOS) via using sol–gel and spin-coating methods using a poly-(ethylene oxide)-block-poly-(propylene oxide)-block-poly-(ethylene oxide) triblock polymer, such as P123 ((EO){sub 20}(PO){sub 70}(EO){sub 20}) or F127 ((EO){sub 106}(PO){sub 70}(EO){sub 106}), as the structure-directing agent. The MPS thin film prepared using P123 as the mesoporous template and treated via vacuum ultraviolet (VUV) irradiation to remove the triblock copolymer had a more uniform pore array than that of the corresponding film prepared via thermal treatment. Protein adsorption and enzyme-linked immunosorbent assay (ELISA) on the synthesized MPS thin films were also investigated. VUV-irradiated MPS thin films adsorbed a smaller quantity of protein A than the thermally treated films; however, the human immunoglobulin G (IgG) binding efficiency was higher on the former. In addition, protein A–IgG specific binding on MPS thin films was achieved without using a blocking reagent; i.e., nonspecific adsorption was inhibited by the uniform pore arrays of the films. Furthermore, VUV-irradiated MPS thin films exhibited high sensitivity for ELISA testing, and cytochrome c adsorbed on the MPS thin films exhibited high catalytic activity and recyclability. These results suggest that MPS thin films are attractive platforms for the development of novel biosensors. - Highlights: • VUV-treated MPS thin films with removed polymer had uniform pore. • VUV-treated MPS thin films exhibited high sensitivity by ELISA. • Cytochrome c showed the catalytic activity and recyclability on synthesized films.

  15. Preparation of mesoporous silica thin films by photocalcination method and their adsorption abilities for various proteins

    International Nuclear Information System (INIS)

    Kato, Katsuya; Nakamura, Hitomi; Yamauchi, Yoshihiro; Nakanishi, Kazuma; Tomita, Masahiro

    2014-01-01

    Mesoporous silica (MPS) thin film biosensor platforms were established. MPS thin films were prepared from tetraethoxysilane (TEOS) via using sol–gel and spin-coating methods using a poly-(ethylene oxide)-block-poly-(propylene oxide)-block-poly-(ethylene oxide) triblock polymer, such as P123 ((EO) 20 (PO) 70 (EO) 20 ) or F127 ((EO) 106 (PO) 70 (EO) 106 ), as the structure-directing agent. The MPS thin film prepared using P123 as the mesoporous template and treated via vacuum ultraviolet (VUV) irradiation to remove the triblock copolymer had a more uniform pore array than that of the corresponding film prepared via thermal treatment. Protein adsorption and enzyme-linked immunosorbent assay (ELISA) on the synthesized MPS thin films were also investigated. VUV-irradiated MPS thin films adsorbed a smaller quantity of protein A than the thermally treated films; however, the human immunoglobulin G (IgG) binding efficiency was higher on the former. In addition, protein A–IgG specific binding on MPS thin films was achieved without using a blocking reagent; i.e., nonspecific adsorption was inhibited by the uniform pore arrays of the films. Furthermore, VUV-irradiated MPS thin films exhibited high sensitivity for ELISA testing, and cytochrome c adsorbed on the MPS thin films exhibited high catalytic activity and recyclability. These results suggest that MPS thin films are attractive platforms for the development of novel biosensors. - Highlights: • VUV-treated MPS thin films with removed polymer had uniform pore. • VUV-treated MPS thin films exhibited high sensitivity by ELISA. • Cytochrome c showed the catalytic activity and recyclability on synthesized films

  16. Out-of-substrate plane orientation control of thin YBa{sub 2}Cu{sub 3}O {sub x} films on NdGaO{sub 3} tilted-axes substrates

    Energy Technology Data Exchange (ETDEWEB)

    Mozhaev, Peter B. [Institute of Physics and Technology RAS, Moscow 117218 (Russian Federation) and Department of Physics, Technical University of Denmark, Lyngby, DK-2800 (Denmark)]. E-mail: pbmozh@nm.ru; Mozhaeva, Julia E. [Institute of Physics and Technology RAS, Moscow 117218 (Russian Federation); Department of Physics, Technical University of Denmark, Lyngby, DK-2800 (Denmark); Bdikin, Igor K. [Institute of Solid State Physics RAS, Chernogolovka, Moscow distr., 142432 (Russian Federation); CICECO, University of Aveiro, Aveiro 3810-193 (Portugal); Kotelyanskii, Iosif M. [Institute of Radio Engineering and Electronics RAS, Moscow 125009 (Russian Federation); Lusanov, Valery A. [Institute of Radio Engineering and Electronics RAS, Moscow 125009 (Russian Federation); Hansen, Jorn Bindslev [Department of Physics, Technical University of Denmark, Lyngby, DK-2800 (Denmark); Jacobsen, Claus S. [Department of Physics, Technical University of Denmark, Lyngby, DK-2800 (Denmark); Kholkin, Andrey L. [CICECO, University of Aveiro, Aveiro 3810-193 (Portugal)

    2006-02-01

    Epitaxial heterostructures YBa{sub 2}Cu{sub 3}O {sub x}(YBCO)/CeO{sub 2}/NdGaO{sub 3} were prepared on tilted-axes NdGaO{sub 3} substrates using laser ablation technique. Morphology, crystal structure and electrical properties of the obtained films were characterized. The seeding mechanisms are affected by the tilt angle, resulting in superior YBCO films on NdGaO{sub 3} substrates in an intermediate range of tilt angles of 6-14{sup o}. The introduction of CeO{sub 2} layer leads to change of the YBCO film orientation: at low deposition rate c-oriented films are formed, while at high deposition rates the film grows with c-axis tilted along the [1 1 0] NdGaO{sub 3} direction. Bi-epitaxial films and structures were prepared by removal of part of the CeO{sub 2} layer using ion-beam milling.

  17. Applying RF Magnetron sputtering to prepare ZnO thin films and their characterization

    International Nuclear Information System (INIS)

    Saad, M.; Kassis, A.

    2009-05-01

    ZnO thin films were prepared using Rf magnetron sputtering under several preparation conditions (different values of deposition pressure, Rf power, substrate temperature). The optical properties of these films were investigated by measuring their transmission in the spectral range (300-1000 nm), and the electrical properties were investigated by measuring their electrical resistance. Results have been discussed in terms of the modified Thornton model for sputtered thin metal oxide films. Preparation conditions for depositing the highly resistive transparent i-ZnO buffer layer and the highly conducting transparent n-ZnO window layer for solar cells were proposed. (author)

  18. Challenges of sample preparation for cross sectional EBSD analysis of electrodeposited nickel films

    DEFF Research Database (Denmark)

    Alimadadi, Hossein; Pantleon, Karen

    2009-01-01

    Thorough microstructure and crystallographic orientation analysis of thin films by means of electron backscatter diffraction requires cross section preparation of the film-substrate compound. During careful preparation, changes of the rather non-stable as-deposited microstructure must be avoided....... Different procedures for sample preparation including mechanical grinding and polishing, electropolishing and focused ion beam milling have been applied to a nickel film electrodeposited on top of an amorphous Ni-P layer on a Cu-substrate. Reliable EBSD analysis of the whole cross section can be obtained...

  19. Preparation and characterization of depolymerised chitosan films and crosslinked with sodium tripolyphosphate

    International Nuclear Information System (INIS)

    Salazar, Max Carlos; Valderrama Negron, Ana

    2013-01-01

    This work has studied the preparation and characterization of chitosan films (CS) crosslinked with sodium tripolyphosphate (TPP), prepared by the solvent evaporation method. Initially we studied the depolymerization of chitosan with sodium nitrite to get different polymer molecular weights in the used polymer. For example, we obtained chitosans of 554.22kDa and 133.37kDa of molecular weight. Afterward, prepared and characterized chitosans films crosslinked with TPP, evidently the hydrogen bridge interaction with the polyanion through IR, SEM, TG; also was performed swelling studies, with the objective of identified the type of kinetic model in which enable explain said phenomenon in these films. (author)

  20. The preparation and corrosion resistance of Ce and Nd modified anodic films on aluminum

    International Nuclear Information System (INIS)

    Li Qizheng; Tang Yuming; Zuo Yu

    2010-01-01

    Rare earth element Ce and Nd modified anodic films were prepared on aluminum surface by a relatively simple method: the aluminum samples were first immersed in Ni(NO 3 ) 2 solutions containing Ce or Nd salts at 90 deg. C, then were dried and anodized. The contents of Ce or Nd in the anodic films were from 0.5% to 0.9%, and about 4-5% Ni was also introduced in the films. The modified anodic films were more compact with much smaller pores and increased hardness. In neutral, acidic and basic NaCl solutions, the rare earth modified films showed obviously improved corrosion resistance. The Ce modified films showed better corrosion resistance than Nd modified films. The cracking resistance of the films under heating was also improved.

  1. Electrodeposited Fe-Co films prepared from a citric-acid-based plating bath

    OpenAIRE

    Yanai, Takeshi; Uto, H.; Shimokawa, Takaya; Nakano, Masaki; Fukunaga, Hirotoshi; Suzuki, K.

    2013-01-01

    Electrodeposited Fe-Co films are commonly prepared in a boric-acid-based bath. In this research, we applied citric acid instead of boric acid for the plating of Fe-Co films because boron in the waste bath is restricted by environmental-protection regulations in Japan. We evaluated the effect of citric acid on the magnetic and structural properties of the films. The saturation magnetization of the Fe-Co films slightly increased while the Fe content in the Fe-Co films decreased with increasing ...

  2. Preparation and characterization of milk protein films and their application for packaging of Cheddar cheese

    OpenAIRE

    Wagh, Y. R.; Pushpadass, Heartwin A.; Emerald, F. Magdaline Eljeeva; Nath, B. Surendra

    2013-01-01

    Casein and whey protein concentrate (WPC) films, plasticized with glycerol and sorbitol independently, were prepared by casting. The film thickness, water vapour and oxygen permeation and tensile and moisture sorption properties of the films were determined. The tensile strength (TS), tensile strain (TE) and elastic modulus (EM) of the films ranged from 0.71 to 4.58 MPa, 19.22 to 66.63 % and 2.05 to 6.93 MPa, respectively. The film properties were influenced by the type of biopolymer (casein ...

  3. Preparation and optical characterization of DNA-riboflavin thin films

    Science.gov (United States)

    Paulson, Bjorn; Shin, Inchul; Kong, Byungjoo; Sauer, Gregor; Dugasani, Sreekantha Reddy; Khazaeinezhad, Reza; Jung, Woohyun; Joo, Boram; Oh, Kyunghwan

    2016-09-01

    Thin films of DNA biopolymer thin film are fabricated by a drop casting process on glass and silicon substrates, as well as freestanding. The refractive index is measured by elliposmetry and in bulk DNA film the refractive index is shown to be increased in the 600 to 900 nm DNA transparency window by doping with riboflavin. Further analysis with FT-IR, Raman, and XRD are used to determine whether binding between riboflavin and DNA occurs.

  4. Introduction of Artificial Pinning Center into PLD-YBCO Coated Conductor on IBAD and Self-Epitaxial CeO2 Buffered Metal Substrate

    International Nuclear Information System (INIS)

    Kobayashi, H.; Yamada, Y.; Ishida, S.; Takahashi, K.; Konishi, M.; Ibi, A.; Miyata, S.; Kato, T.; Hirayama, T.; Shiohara, Y.

    2006-01-01

    In order to fabricate YBa2Cu3O7-x (YBCO) coated conductors with high critical current density Jc in magnetic fields, we fabricated YBCO coated conductors with artificial pinning centers by the pulsed laser deposition (PLD) method on a self epitaxial PLD-CeO2 layer and ion-beam assisted deposition (IBAD)-Gd2Zr2O7 (GZO) buffered Hastelloy tape. Artificial pinning centers were introduced by the PLD deposition using the yttria-stabilized zirconia (YSZ) oxide target (nano-dot method) and YBCO target including YSZ particles (mixed target method). In the experiments using YSZ oxide target, YSZ nano-dots were observed. They were approximately 15 nm in height and 10 nm to 70 nm in diameter. We found that the density of nano-dots was controlled by the number of laser pulses. These samples exhibited higher Jc than YBCO films in magnetic fields. Furthermore, a similar improvement of Jc was observed in the experiments using YBCO target including YSZ particles. TEM observation revealed that columnar nano-structure made of BaZrO3 was formed during YBCO deposition and it was effective for pinning. We call this new epitaxial nano-structure 'bamboo structure' from its anisotropic growth and morphology

  5. Characterization of AZO and Ag based films prepared by RF magnetron sputtering

    International Nuclear Information System (INIS)

    Miao, Dagang; Jiang, Shouxiang; Zhao, Hongmei; Shang, Songmin; Chen, Zhuoming

    2014-01-01

    Highlights: • Highly infrared reflective AZO and Ag based films were prepared. • Ag showed better crystallization on AZO film than on glass substrate. • Infrared reflection rate was inversely proportional to the film sheet resistance. • Film with infrared reflection of 97% in FIR region was acquired. - Abstract: Ag, AZO/Ag, Ag/AZO and AZO/Ag/AZO films were prepared on glass substrates by radio frequency (RF) magnetron sputtering technology. The prepared films were systematically investigated by X-ray Diffraction (XRD), Atomic Force Microscopy (AFM), UV–visible spectrophotometer, a four-point probe system and Fourier Transform Infrared Spectroscopy. The results indicated that Ag inner layer starts forming a continuous film at the thickness of 10 nm and Ag layer presents superior crystallization on AZO substrate than that on glass substrate. The continuous Ag inner layer film provided the highest average visible transmittance of 85.4% (AZO/Ag/AZO). The lowest sheet resistance of 3.21 Ω/sq and the highest infrared reflection rate of 97% in FIR region can be obtained on AZO/Ag (15 nm)/AZO film. The high infrared reflection property of the AZO/Ag/AZO coating makes it a promising candidate for solar control films

  6. Positron annihilation studies in Hf doped YBCO

    International Nuclear Information System (INIS)

    Gopalan, P.; Priya, E.R.; Premila, M.; Sundar, C.S.; Gopinathan, K.P.

    1992-01-01

    The variation of positron lifetime and oxygen stoichiometry as a function of quench temperature has been measured in undoped and 0.5at%, 0.75at%, and 1.0 at% Hf doped YBCO. In both the undoped and Hf doped samples, the lifetime decreases and the oxygen content increases as the quench temperature is lowered from 900degC to 300degC. The lifetime in the tetragonal phase (900degC) decreases with the increase in Hf content, whereas in the orthorhombic phase (450degC) it increases. The difference in lifetime between the tetragonal and orthorhombic phases decreases with the increase in the Hf content. These trends are discussed in terms of the influence of Hf doping on the oxygen content and the positron density distribution in YBCO

  7. Rapid processing method for solution deposited YBa2Cu3O7-δ thin films

    International Nuclear Information System (INIS)

    Dawley, J.T.; Clem, P.G.; Boyle, T.J.; Ottley, L.M.; Overmyer, D.L.; Siegal, M.P.

    2004-01-01

    YBa 2 Cu 3 O 7-δ (YBCO) films, deposited on buffered metal substrates, are the primary candidate for second-generation superconducting (SC) wires, with applications including expanded power grid transmission capability, compact motors, and enhanced sensitivity magnetic resonance imaging. Feasibility of manufacturing such superconducting wires is dependent on high processing speed, often a limitation of vapor and solution-based YBCO deposition processes. In this work, YBCO films were fabricated via a new diethanolamine-modified trifluoroacetic film solution deposition method. Modifying the copper chemistry of the YBCO precursor solution with diethanolamine enables a hundredfold decrease in the organic pyrolysis time required for MA/cm 2 current density (J c ) YBCO films, from multiple hours to ∼20 s in atmospheric pressure air. High quality, ∼0.2 μm thick YBCO films with J c (77 K) values ≥2 MA/cm 2 at 77 K are routinely crystallized from these rapidly pyrolyzed films deposited on LaAlO 3 . This process has also enabled J c (77 K)=1.1 MA/cm 2 YBCO films via 90 m/h dip-coating on Oak Ridge National Laboratory RABiTS textured metal tape substrates. This new YBCO solution deposition method suggests a route toward inexpensive and commercializable ∼$10/kA m solution deposited YBCO coated conductor wires

  8. Preparation and characterization of milk protein films and their application for packaging of Cheddar cheese.

    Science.gov (United States)

    Wagh, Y R; Pushpadass, Heartwin A; Emerald, F Magdaline Eljeeva; Nath, B Surendra

    2014-12-01

    Casein and whey protein concentrate (WPC) films, plasticized with glycerol and sorbitol independently, were prepared by casting. The film thickness, water vapour and oxygen permeation and tensile and moisture sorption properties of the films were determined. The tensile strength (TS), tensile strain (TE) and elastic modulus (EM) of the films ranged from 0.71 to 4.58 MPa, 19.22 to 66.63 % and 2.05 to 6.93 MPa, respectively. The film properties were influenced by the type of biopolymer (casein and whey protein concentrate), plasticizer and its concentration. Increasing the plasticizer concentration, increased the film thickness, TE and water vapour permeability (WVP), but decreased the TS and EM. As the concentration of plasticizer increased to the highest level, the film thickness increased from 0.168 to 0.305 mm for glycerol-plasticized films and from 0.251 to 0.326 mm for sorbitol-plasticized films. The film thickness increased because the amount of plasticizer in the film network increased and the amount of biopolymer remained same. Casein films showed superior tensile properties as compared to WPC films. The WVP of both casein and WPC films lied between 3.87 and 13.97 g.mm./(m(2).h.kPa). The moisture sorption isotherms of both films were typical of high-protein material, and were adequately described by the GAB model. The oxygen permeability of casein films was relatively lower than that of WPC films, regardless of the plasticizer used. The sensory data revealed that the organoleptic quality of Cheddar cheese was unaffected by milk-protein film packaging.

  9. Quasi-epitaxial barium hexaferrite thin films prepared by a topotactic reactive diffusion process

    Science.gov (United States)

    Meng, Siqin; Yue, Zhenxing; Zhang, Xiaozhi; Li, Longtu

    2014-01-01

    Quasi-epitaxial barium hexaferrite thin films (BaM) with crystallographic c-axis parallel to film normal were prepared through a topotactic reactive diffusion process using two-step solution deposition on c-plane sapphire. The two-step spin coating process involves preparing an epitaxial hematite film, coating the film with barium precursor solution and thermal annealing. The crystal orientation and magnetic anisotropy of BaM thin films were investigated by X-ray diffraction analysis, SEM observation and magnetic measurements. Hysteresis loops showed good magnetic anisotropy and high remanence ratio (RR) Mr/Ms = 0.97. The films fabricated by two-step spin coating process displayed wider rocking curve width but better magnetic anisotropy than one-step spin coating. The possible mechanism of this discrepancy is discussed in this paper.

  10. Quasi-epitaxial barium hexaferrite thin films prepared by a topotactic reactive diffusion process

    Energy Technology Data Exchange (ETDEWEB)

    Meng, Siqin; Yue, Zhenxing, E-mail: yuezhx@tsinghua.edu.cn; Zhang, Xiaozhi; Li, Longtu

    2014-01-30

    Quasi-epitaxial barium hexaferrite thin films (BaM) with crystallographic c-axis parallel to film normal were prepared through a topotactic reactive diffusion process using two-step solution deposition on c-plane sapphire. The two-step spin coating process involves preparing an epitaxial hematite film, coating the film with barium precursor solution and thermal annealing. The crystal orientation and magnetic anisotropy of BaM thin films were investigated by X-ray diffraction analysis, SEM observation and magnetic measurements. Hysteresis loops showed good magnetic anisotropy and high remanence ratio (RR) Mr/Ms = 0.97. The films fabricated by two-step spin coating process displayed wider rocking curve width but better magnetic anisotropy than one-step spin coating. The possible mechanism of this discrepancy is discussed in this paper.

  11. Characteristics of (Ti,Ta)N thin films prepared by using pulsed high energy density plasma

    Energy Technology Data Exchange (ETDEWEB)

    Feng Wenran [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100080 (China); Chen Guangliang [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100080 (China); Li Li [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100080 (China); Lv Guohua [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100080 (China); Zhang Xianhui [College of Science, Changchun University of Science and Technology, Changchun 130022, Jilin Province (China); Niu Erwu [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100080 (China); Liu Chizi [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100080 (China); Yang Size [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100080 (China)

    2007-07-21

    (Ti,Ta)N films were prepared by pulsed high energy density plasma (PHEDP) from a coaxial gun in N{sub 2} gas. The coaxial gun is composed of a tantalum inner electrode and a titanium outer one. Material characteristics of the (Ti,Ta)N film were investigated by x-ray photoelectron spectroscopy and x-ray diffraction. The microstructure of the film was observed by a scanning electron microscope. The elemental composition and the interface of the film/substrate were analysed using Auger electron spectrometry. Our results suggest that the binary metal nitride film (Ti,Ta)N, can be prepared by PHEDP. It also shows that dense nanocrystalline (Ti,Ta)N film can be achieved.

  12. A study for designing YBCO power transformer

    International Nuclear Information System (INIS)

    Hayashi, H.; Okamoto, H.; Harimoto, T.; Imayoshi, T.; Tomioka, A.; Bouno, T.; Konno, M.; Iwakuma, M.

    2007-01-01

    It is highly expected that superconducting transformers, which are characterized by incombustibility, light weight, and compactness, will be used practically for equipment in substations and office buildings sited in urban areas. In recent years, remarkable improvements in the performance of YBaCuO (YBCO) tape wire have been seen. This kind of tape wire has the property that its critical current is large in a highly magnetic field; and, its use is expected to reduce AC loss by applying slit processing on the tape wire, contributing to future cost reductions. In addition, the development of efficient, economical cryogenic units is also expected. The authors have developed a conceptual design for a 66 kV/20 MVA power transformer using YBCO tape wires, or an YBCO power transformer. As a result, we were able to identify the transformer's optimal system structure including coil winding comprised of coils and tape wires; and, we confirmed that the devised transformer can made to be both compact and highly efficient

  13. Radiolytic preparation of thin Au film directly on resin substrate using high-energy electron beam

    Energy Technology Data Exchange (ETDEWEB)

    Ohkubo, Yuji, E-mail: okubo@upst.eng.osaka-u.ac.jp [Graduate School of Engineering, Osaka University, 2-1 Yamadaoka, Suita, Osaka 565-0871 (Japan); Seino, Satoshi; Nakagawa, Takashi; Kugai, Junichiro [Graduate School of Engineering, Osaka University, 2-1 Yamadaoka, Suita, Osaka 565-0871 (Japan); Ueno, Koji [Japan Electron Beam Irradiation Service Ltd., 5-3 Ozushima, Izumiohtsu, Osaka 595-0074 (Japan); Yamamoto, Takao A. [Graduate School of Engineering, Osaka University, 2-1 Yamadaoka, Suita, Osaka 565-0871 (Japan)

    2016-04-01

    A novel method for preparing thin Au films directly on resin substrates using an electron beam was developed. The thin Au films were prepared on a resin substrate by the reduction of Au ions in an aqueous solution via irradiation with a high-energy electron beam (4.8 MeV). This reduction method required 7 s of the irradiation time of the electron beam. Furthermore, no reductant or catalyst was needed. As the concentration of Au ions in the precursor solution was increased, the amount of Au deposited on the resin substrate increased, too, and the structure of the prepared Au film changed. As a result, the film color changed as well. Cross-sectional scanning electron microscope images of the thus-prepared Au film indicated that the Au films were consisted of two layers: a particle layer and a bottom bulk layer. There was strong adhesion between the Au films and the underlying resin substrates. This was confirmed by the tape-peeling test and through ultrasonic cleaning. After both processes, Au remained on the resin substrates, while most of the particle-like moieties were removed. This indicated that the thin Au films prepared via irradiation with a high-energy electron beam adhered strongly to the resin substrates. - Highlights: • A thin gold (Au) film was formed by EBIRM for the first time. • The irradiation time of the electron beam was less than 10 s. • Thin Au films were obtained without reductant or catalyst. • Au films were consisted of two layers: a particle layer and a bottom bulk layer. • There was strong adhesion between the bottom bulk layer and the underlying resin substrates.

  14. Improvement in fatigue property for a PZT ferroelectric film device with SRO electrode film prepared by chemical solution deposition

    International Nuclear Information System (INIS)

    Miyazaki, H.; Miwa, Y.; Suzuki, H.

    2007-01-01

    PZT films with (1 0 0) and (1 1 0) orientation were prepared by spin coating using the chemical solution deposition (CSD) method on an SRO/Si or a Pt/Ti/SiO 2 /Si substrate. The remnant polarization and the saturation polarization of the PZT/SRO/Si film were 21 and 35 μC/cm 2 , and those of the PZT/Pt/Ti/SiO 2 /Si film were 20 and 31 μC/cm 2 . The remnant polarization of the PZT/SRO/Si film maintained more than 10 8 switching cycles, and the fatigue property was observed for the PZT film fabricated on the Pt/Ti/SiO 2 /Si electrode

  15. Preparation of high quality superconducting thin MgB2 films for electronics

    International Nuclear Information System (INIS)

    Surdu, Andrei; Zdravkov, Vladimir; Sidorenko, Anatolie; Rossolenko, Anna; Ryazanov, Valerii; Bdikin, Igor; Kroemer, Oliver; Nold, Eberhard; Koch, Thomas; Schimmel, Thomas

    2007-01-01

    In this work we report the growth of high-Tc MgB 2 smooth films which are prepared in a two-step process: 1) deposition of the precursor films and 2) their annealing in Mg vapor with a specially designed, reusable reactor. Our method opens perspectives for the use of MgB 2 films in microelectronics, especially for high-frequency applications. (authors)

  16. Preparation and characterization of TiO[sub 2]/Sb thin films for solar energy applications

    Energy Technology Data Exchange (ETDEWEB)

    Badawy, W.A. (Dept. of Chemistry, Cairo Univ., Giza (Egypt))

    1993-01-01

    Pure and antimony-incorporated TiO[sub 2] thin films were prepared using a spray-CVD method. The method allows for convenient incorporation of foreign atoms into the oxide matrix during film growth. The foreign atoms in the oxide film affects both the photovoltaic and photoelectrochemical properties of the n-Si/oxide heterojunction. The characteristics of the prepared oxide films were affected significantly by the presence of antimony on the oxide matrix. The increased conductivity of the Sb-containing oxide layers is reflected in the improved photovoltaic properties of the prepared n-Si/TiO[sub 2]-Sb heterojunctions, e.g. fill factor and solar conversion efficiency. The photoelectrochemical properties of the prepared devices revealed that the charge transfer step at the oxide/electrolyte interface leads to a deterioration of the cell quality. However, this drawback has been offset by the improved properties of the heterojunction. (orig.)

  17. Remarkable weakness against cleavage stress for YBCO-coated conductors and its effect on the YBCO coil performance

    International Nuclear Information System (INIS)

    Yanagisawa, Y.; Nakagome, H.; Takematsu, T.; Takao, T.; Sato, N.; Takahashi, M.; Maeda, H.

    2011-01-01

    Cleavage strength for YBCO-coated conductor is extremely low, typically 0.5 MPa. The remarkable weakness is due to cracks on the slit edge of the conductor. The cleavage stress appears on YBCO double pancake coils impregnated with epoxy. The cleavage stress should be avoided in the coil winding. Cleavage strength for an YBCO-coated conductor at 77 K was investigated with a model experiment. The nominal cleavage strength for an YBCO-coated conductor is extremely low, typically 0.5 MPa. This low nominal cleavage strength is due to stress concentration on a small part of the YBCO-coated conductor in cleavage fracture. Debonding by the cleavage stress occurs at the interface between the buffer layer and the Hastelloy substrate. The nominal cleavage strength for a slit edge of the conductor is 2.5-times lower than that for the original edge of the conductor; cracks and micro-peel existing over the slit edge reduce the cleavage strength for the slit edge. Cleavage stress and peel stress should be avoided in coil winding, as they easily delaminate the YBCO-coated conductor, resulting in substantial degradation of coil performance. These problems are especially important for epoxy impregnated YBCO-coated conductor coils. It appears that effect of cleavage stress and peel stress are mostly negligible for paraffin impregnated YBCO-coated conductor coils or dry wound YBCO-coated conductor coils.

  18. YBa2Cu3O7 films prepared by aerosol MOCVD

    International Nuclear Information System (INIS)

    Weiss, F.; Froehlich, K.; Haase, R.; Labeau, M.; Selbmann, D.; Senateur, J.P.; Thomas, O.

    1993-01-01

    In the present study we report on properties of YBa 2 Cu 3 O 7 films prepared by aerosol MOCVD. We give a short description of the process and we focus on the superconducting and related properties of the films deposited on SrTiO 3 , LaAlO 3 and NdGaO 3 single crystalline substrates. (orig.)

  19. The effect of formulation additives on the properties of films prepared ...

    African Journals Online (AJOL)

    Method: Films were prepared by solvent casting method using Terminalia, xanthan gums and hydroxylpropy lmethylcellulose (HPMC). Terminlia was also combined with xanthan, HPMC at different ratios using propylene glycol and glycerol as plaasticizers. The films were characterized using adherence, folding endurance ...

  20. Quality by design approach for optimizing the formulation and physical properties of extemporaneously prepared orodispersible films

    NARCIS (Netherlands)

    Visser, J. Caroline; Dohmen, Willem M. C.; Hinrichs, Wouter L. J.; Breitkreutz, Joerg; Frijlink, Henderik W.; Woerdenbag, Herman J.

    2015-01-01

    The quality by design (QbD) approach was applied for optimizing the formulation of extemporaneously prepared orodispersible films (ODFs) using Design-Expert Software. The starting formulation was based on earlier experiments and contained the film forming agents hypromellose and carbomer 974P and

  1. Preparation and characterization of LaNiO3 films grown by metal ...

    Indian Academy of Sciences (India)

    Administrator

    Keywords. Conductive films; LaNiO3; metal–organic deposition; texture. 1. Introduction ... films on Si (111) and quartz substrates were first prepared with the 2-ethyl hexanotes of ..... Li A, Ge C, Lü P and Ming N 1996a Appl. Phys. Lett. 68. 1347.

  2. Zirconia thin film preparation by wet chemical methods at low temperature

    NARCIS (Netherlands)

    Popovici, M.; Graaf, de J.; Verschuuren, M.A.; Graat, P.C.J.; Verheijen, M.A.

    2010-01-01

    In this study the preparation of zirconia thin films with a high refractive index at low temperature is aimed for. Two non-hydrolytic type approaches of wet chemical synthesis are presented. Both by sol–gel and colloid chemistry, highly transmissive, smooth thin films of zirconia cubic and/or

  3. Preparation and characterization of biocomposite film based on chitosan and kombucha tea as active food packaging

    DEFF Research Database (Denmark)

    Ashrafi, Azam; Jokar, Maryam

    2018-01-01

    An active film composed of chitosan and kombucha tea (KT) was successfully prepared using the solvent casting technique. The effect of incorporation of KT at the levels 1%–3% w/w on the physical and functional properties of chitosan film was investigated. The antimicrobial activity of chitosan...

  4. Structure and giant magnetoresistance of carbon-based amorphous films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Ma, L.; He, M.F.; Liu, Z.W.; Zeng, D.C.; Gu, Z.F.; Cheng, G.

    2014-01-01

    Pure amorphous carbon (a-C) and Co-doped Co x C 1−x films were prepared on n-Si(100) substrates by dc magnetron sputtering. In Co–C films, the nano-sized amorphous Co particles were homogeneously dispersed in the amorphous cross-linked carbon matrix. The structures of a-C and Co x C 1−x films were investigated by X-ray photoelectron spectroscopy and Raman spectroscopy. The results showed that the a-C films were diamond-like carbon (DLC) films. After doping cobalt into DLC film, the sp 3 -hybridized carbon content in DLC composite films almost had no change. The as-deposited Co x C 1−x granular films had larger value of magnetoresistance (MR) than the amorphous carbon film. A very high positive MR, up to 15.5% at magnetic field B = 0.8 T and x = 2.5 at.% was observed in a Co x C 1−x granular film with thickness of 80 nm at room temperature when the external magnetic field was perpendicular to the electric current and the film surface. With increase of the film thickness and Co-doped content, the MR decreased gradually. It remains a challenge to well explain the observed MR effect in the Co x C 1−x granular films. - Highlights: • The amorphous carbon films were diamond-like carbon films. • No carbide appearing, the Co–C composite films form a good metal/insulator system. • A high positive magnetoresistance, up to 15.5% at B = 0.8 T was observed in Co–C films

  5. Magnetic properties and crystal texture of Co alloy thin films prepared on double bias Cr

    Science.gov (United States)

    Deng, Y.; Lambeth, D. N.; Lee, L.-L.; Laughlin, D. E.

    1993-05-01

    A double layer Cr film structure has been prepared by sputter depositing Cr on single crystal Si substrates first without substrate bias and then with various substrate bias voltages. Without substrate bias, Cr{200} texture grows on Si at room temperature; thus the first Cr layer acts like a seed Cr layer with the {200} texture, and the second Cr layer, prepared with substrate bias, tends to replicate the {200} texture epitaxially. CoCrTa and CoNiCr films prepared on these double Cr underlayers, therefore, tend to have a {112¯0} texture with their c-axes oriented in the plane of the film. At the same time, the bias sputtering of the second Cr layer increases the coercivity of the subsequently deposited magnetic films significantly. Comparison studies of δM curves show that the use of the double Cr underlayers reduces the intergranular exchange interactions. The films prepared on the Si substrates have been compared with the films prepared on canasite and glass substrates. It has also been found that the magnetic properties are similar for films on canasite and on glass.

  6. Preparation and characterization of epitaxially grown unsupported yttria-stabilized zirconia (YSZ) thin films

    Energy Technology Data Exchange (ETDEWEB)

    Götsch, Thomas; Mayr, Lukas [Institute of Physical Chemistry, Universität Innsbruck, A-6020 Innsbruck (Austria); Stöger-Pollach, Michael [University Service Center for Transmission Electron Microscopy (USTEM), Vienna University of Technology, A-1040 Vienna (Austria); Klötzer, Bernhard [Institute of Physical Chemistry, Universität Innsbruck, A-6020 Innsbruck (Austria); Penner, Simon, E-mail: simon.penner@uibk.ac.at [Institute of Physical Chemistry, Universität Innsbruck, A-6020 Innsbruck (Austria)

    2015-03-15

    Highlights: • Preparation of unsupported yttrium-stabilized zirconia films. • Control of ordering and epitaxy by temperature of deposition template. • Adjustment of film defectivity by deposition and post-oxidation temperature. • Reproducibility of target stoichiometry in the deposited films. • Lateral and vertical chemical homogeneity. - Abstract: Epitaxially grown, chemically homogeneous yttria-stabilized zirconia thin films (“YSZ”, 8 mol% Y{sub 2}O{sub 3}) are prepared by direct-current sputtering onto a single-crystalline NaCl(0 0 1) template at substrate temperatures ≥493 K, resulting in unsupported YSZ films after floating off NaCl in water. A combined methodological approach by dedicated (surface science) analytical characterization tools (transmission electron microscopy and diffraction, atomic force microscopy, angle-resolved X-ray photoelectron spectroscopy) reveals that the film grows mainly in a [0 0 1] zone axis and no Y-enrichment in surface or bulk regions takes place. In fact, the Y-content of the sputter target is preserved in the thin films. Analysis of the plasmon region in EEL spectra indicates a defective nature of the as-deposited films, which can be suppressed by post-deposition oxidation at 1073 K. This, however, induces considerable sintering, as deduced from surface morphology measurements by AFM. In due course, the so-prepared unsupported YSZ films might act as well-defined model systems also for technological applications.

  7. Photoinducedly electrochemical preparation of Prussian blue film and electrochemical modification of the film with cetyltrimethylammonium cation

    Energy Technology Data Exchange (ETDEWEB)

    Liu Shouqing, E-mail: shouqing_liu@hotmail.co [Key Laboratory of Environmental Functional Materials of Jiangsu Province, College of Chemistry and Bioengineering, Suzhou University of Science and Technology, Suzhou 215009 (China); Li Hua; Sun Weihui; Wang Xiaomei; Chen Zhigang [Key Laboratory of Environmental Functional Materials of Jiangsu Province, College of Chemistry and Bioengineering, Suzhou University of Science and Technology, Suzhou 215009 (China); Xu Jingjuan; Ju Huangxian; Chen Hongyuan [Key Laboratory of Analytical Chemistry for Life Science, Ministry of Education, Nanjing University, Nanjing 210093 (China)

    2011-04-15

    Research highlights: {yields} Cetyltrimethylammonium cations work as counter ions in Prussian blue film was observed and confirmed by cyclic voltammetry, Fourier transform infrared spectroscopy, X-ray powder diffraction measurements, scanning electronic microscopy and transmission electron microscope for the first time. {yields} Because the cetyltrimethylammonium cations in Prussian blue film are hydrophobic, the Prussian blue film is very stable even in alkali solution, which provides a technical basis for fabrication of stable biosensors. - Abstract: This work presents a photoinducedly electrochemical preparation of Prussian blue from a single sodium nitroprusside and insertion of cetyltrimethylammonium cations into Prussian blue as counter ions. The product of photoinducedly electrochemical reactions has a couple of voltammetric peaks at E{sup o} = 0.266 V in 0.2 mol l{sup -1} KCl solution, the measurements of X-ray powder diffraction and FT-IR spectroscopy show that it is Prussian blue (PB). The formation mechanism of a pre-photochemical reaction and subsequent electrochemical reaction is suggested. The cyclic voltammetric treatment of the freshly as-prepared PB film in 1.0 mmol l{sup -1} cetyltrimethylammonium (CTA) bromide solution leads to the insertion of cetyltrimethylammonium cations into the channels of Prussian blue, which substitutes for potassium ions as counter ions in Prussian blue. The Prussian blue containing CTA counter ions shows two couples of voltammetric peaks at E{sup o} = -0.106 V and E{sup o} = 0.249 V in 0.2 mol l{sup -1} KCl solution containing 1.0 mmol l{sup -1} cetyltrimethylammonium bromide. Compared with the electrochemical behaviors of KFeFe(CN){sub 6} in 0.1 mol l{sup -1} KOH alkali solution, CTAFeFe(CN){sub 6} shows relatively durable voltammetric currents due to the hydrophobic effects of cetyltrimethylammonium. The diffusion coefficients for CTA and potassium cations were estimated to be D{sub CTA} 1.25 x 10{sup -12} cm{sup 2} s

  8. Preparation and characterization of sponge film made from feathers

    Energy Technology Data Exchange (ETDEWEB)

    Zhuang, Yuan; Wu, Xiaoqian [College of Environmental Science and Engineering, Donghua University, Shanghai 201620 (China); Cao, Zhangjun [College of Chemistry, Chemical Engineering and Biotechnology, Donghua University, Shanghai 201620 (China); Zhao, Xiaoxiang; Zhou, Meihua [College of Environmental Science and Engineering, Donghua University, Shanghai 201620 (China); Gao, Pin, E-mail: gaopin@mail.dhu.edu.cn [College of Environmental Science and Engineering, Donghua University, Shanghai 201620 (China)

    2013-12-01

    Feather wastes generated from poultry farms will pose a problem for disposal, but they are sustainable resources of keratin. Reduction is one of the commonly used methods to obtain soluble keratin from feather. However, the residues generated during feather reduction reaction were rarely investigated. In this study, the residues were transformed into a porous and flexible sponge film by freeze-drying without pretreatment or addition of cross-linking agents. Glycerol was used to alter the physical and chemical characteristics of the sponge film. The film was characterized with a fiber strong stretch instrument, a Fourier transform infrared spectrophotometer, scanning electron microscopy, an elemental analyzer, a differential scanning calorimeter and an automatic air permeability apparatus. Tensile strength and melting point of the sponge film with the optimum glycerol content were 6.2 MPa and 170 °C respectively. Due to air permeability of 368 mm/s, the film can potentially be used in medicine, biology, textile, environmental technology, and so on. It is ecologically friendly and will produce additional benefits from the renewable materials. The film was utilized as adsorbents to remove Cr(VI) from aqueous solutions and as a filtering material for air pollution. Its maximum Cr(VI) uptake capacity was about 148.8 mg/g and the removal rate of PM{sub 10} was 98.3%. - Graphical abstract: The reduction residues were made into a smooth, elastic, porous and flexible sponge film through freeze drying, no pretreatment and no cross-linking agent added. - Highlights: • The residue from feather waste reduction was turned into a sponge film. • A glycerol content of 5% produced a sponge with the optimum characteristics. • The sponge was uniform, stable up to 160 °C, and had an air permeability of 368 mm/s. • Feather-derived sponge film has potential applications in medicine and technology.

  9. Preparation and characterization of sponge film made from feathers

    International Nuclear Information System (INIS)

    Zhuang, Yuan; Wu, Xiaoqian; Cao, Zhangjun; Zhao, Xiaoxiang; Zhou, Meihua; Gao, Pin

    2013-01-01

    Feather wastes generated from poultry farms will pose a problem for disposal, but they are sustainable resources of keratin. Reduction is one of the commonly used methods to obtain soluble keratin from feather. However, the residues generated during feather reduction reaction were rarely investigated. In this study, the residues were transformed into a porous and flexible sponge film by freeze-drying without pretreatment or addition of cross-linking agents. Glycerol was used to alter the physical and chemical characteristics of the sponge film. The film was characterized with a fiber strong stretch instrument, a Fourier transform infrared spectrophotometer, scanning electron microscopy, an elemental analyzer, a differential scanning calorimeter and an automatic air permeability apparatus. Tensile strength and melting point of the sponge film with the optimum glycerol content were 6.2 MPa and 170 °C respectively. Due to air permeability of 368 mm/s, the film can potentially be used in medicine, biology, textile, environmental technology, and so on. It is ecologically friendly and will produce additional benefits from the renewable materials. The film was utilized as adsorbents to remove Cr(VI) from aqueous solutions and as a filtering material for air pollution. Its maximum Cr(VI) uptake capacity was about 148.8 mg/g and the removal rate of PM 10 was 98.3%. - Graphical abstract: The reduction residues were made into a smooth, elastic, porous and flexible sponge film through freeze drying, no pretreatment and no cross-linking agent added. - Highlights: • The residue from feather waste reduction was turned into a sponge film. • A glycerol content of 5% produced a sponge with the optimum characteristics. • The sponge was uniform, stable up to 160 °C, and had an air permeability of 368 mm/s. • Feather-derived sponge film has potential applications in medicine and technology

  10. Preparation and Characterization of FC Films Coated on PET Substrates by RF Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Huang Mei-lin

    2018-01-01

    Full Text Available Fluorocarbon (FC films were prepared on polyethylene terephthalate (PET plates and PET fabrics respectively by a radiofrequency (RF magnetron sputtering technique using polytetrafluoroethylene (PTFE as a target. Scanning electron microscope and X-ray photoelectron spectroscopy were used to investigate the morphology, structure and composition of the obtained FC films. The hydrophobicity and uvioresistant properties of the FC film coated fabric were studied. The results show that the FC films were successfully deposited on the PET substrates by a RF magnetron sputtering. The deposited films are made up of four components -CF3, -CF2-, CF- and -C-. The proportions of the four components and surface morphologies of the deposited films vary with the sputtering conditions. Compared with the original fabric samples, the hydrophobicity of the FC film coated fabrics is quite good and improved significantly.

  11. The preparation and mechanical properties of Al-containing a-C : H thin films

    International Nuclear Information System (INIS)

    Zhang Guangan; Yan Pengxun; Wang Peng; Chen Youming; Zhang Junyan

    2007-01-01

    Al-containing hydrogenated amorphous carbon (Al-C : H) films were deposited on silicon substrates using a mid frequency magnetron sputtering Al target in an argon and methane gas mixture. The composition, surface morphology, hardness and friction coefficient of the films were characterized using x-ray photoelectron spectroscopy, atomic force microscopy, nanoindentation and tribological tester. The Al-C : H films deposited at low CH 4 content show high surface roughness, low hardness and high friction coefficient, similar to metallic Al films; in contrast, the Al-C : H films prepared under high CH 4 content indicate low surface roughness, high hardness and low friction coefficient, close to that of hard a-C : H films as wear-resistance films

  12. Optical properties of flexible fluorescent films prepared by screen printing technology

    Directory of Open Access Journals (Sweden)

    Yan Chen

    2018-05-01

    Full Text Available In this work, we prepared a fluorescent film comprised phosphors and silicone on flexible polyethylene terephthalate (PET substrate using a screen printing technology. The effects of mesh number and weight ratio of phosphors to silicone on the optical properties of the flexible films were investigated. The results indicate that the emission intensity of the film increase as the mesh decreased from 400 to 200, but the film surface gradually becomes uneven. The fluorescent film with high emission intensity and smooth surface can be obtained when the weight ratio of phosphor to gel is 2:1, and mesh number is 300. The luminous efficiency of the fabricated LEDs combined the fluorescent films with 460 nm Ga(InN chip module can reach 75 lm/W. The investigation indicates that the approach can be applied in the remote fluorescent film conversion and decreases the requirements of the particle size and the dispersion state of fluorescent materials.

  13. Optical properties of flexible fluorescent films prepared by screen printing technology

    Science.gov (United States)

    Chen, Yan; Ke, Taiyan; Chen, Shuijin; He, Xin; Zhang, Mei; Li, Dong; Deng, Jinfeng; Zeng, Qingguang

    2018-05-01

    In this work, we prepared a fluorescent film comprised phosphors and silicone on flexible polyethylene terephthalate (PET) substrate using a screen printing technology. The effects of mesh number and weight ratio of phosphors to silicone on the optical properties of the flexible films were investigated. The results indicate that the emission intensity of the film increase as the mesh decreased from 400 to 200, but the film surface gradually becomes uneven. The fluorescent film with high emission intensity and smooth surface can be obtained when the weight ratio of phosphor to gel is 2:1, and mesh number is 300. The luminous efficiency of the fabricated LEDs combined the fluorescent films with 460 nm Ga(In)N chip module can reach 75 lm/W. The investigation indicates that the approach can be applied in the remote fluorescent film conversion and decreases the requirements of the particle size and the dispersion state of fluorescent materials.

  14. Preparation of PANI/PSF conductive composite films and their characteristic

    Institute of Scientific and Technical Information of China (English)

    Yang Yuying; Shang Xiuli; Kong Chao; Zhao Hongxiao; Hu Zhong'ai

    2006-01-01

    Polyaniline (PANI)/polysulfone (PSF) composite films are successfully prepared by phase separation and one-step in-situ polymerization.It is found that the head-on face (in contact with solution) of the films is green while the back face is white.The chemical component and the surface morphology of both surfaces of the films are characterized by FT-IR spectra and SEM,respectively.The effect of the polymerization temperature,time and concentration of the reactants on the electrical properties of the films are discussed in details.The thermo-oxidative degradation of the films is studied by thermogravimetric analysis (TGA).The results indicate that the thermal stability of the PANI/PSF films is higher than that of the pure PSF film.

  15. Sm-doped CeO2 single buffer layer for YBCO coated conductors by polymer assisted chemical solution deposition (PACSD) method

    International Nuclear Information System (INIS)

    Li, G.; Pu, M.H.; Sun, R.P.; Wang, W.T.; Wu, W.; Zhang, X.; Yang, Y.; Cheng, C.H.; Zhao, Y.

    2008-01-01

    An over 150 nm thick Sm 0.2 Ce 0.8 O 1.9-x (SCO) single buffer layer has been deposited on bi-axially textured NiW (2 0 0) alloy substrate. Highly in-plane and out-of-plane oriented, dense, smooth and crack free SCO single layer has been obtained via a polymer-assisted chemical solution deposition (PACSD) approach. YBCO thin film has been deposited equally via a PACSD route on the SCO-buffered NiW, the as grown YBCO yielding a sharp transition at T c0 = 87 K as well as J c (0 T, 77 K) ∼ 1 MA/cm 2 . These results indicates that RE (lanthanides other than Ce) doping may be an effective approach to improve the critical thickness of solution derived CeO 2 film, which renders it a promising candidate as single buffer layer for YBCO coated conductors

  16. Preparation and Properties of Moisture-absorbing Film Impregnated with Polyacrylic Acid Partial Sodium Salt Material

    International Nuclear Information System (INIS)

    Lee, Youn Suk; Park, Insik; Choi, Hong Yeol

    2014-01-01

    Moisture is a major factor causing the deteriorative physical change, microbial growth, and chemical reaction of the products. In this study, the moisture absorbing composite films have been prepared with moisture absorbing material of polyacrylic acid partial sodium salt (PAPSS) impregnated on LLDPE polymer for the functional packaging applications. The results showed that PAPSS impregnated film illustrated uniformly dispersed PAPSS particles in the LLDPE polymer matrix. The transparency of the PAPSS impregnated film decreased slightly at higher PAPSS concentrations. An increase in the PAPSS content for moisture-absorbing films showed a similar decrease in tensile strength, percent elongation at break, and tear strength. Their values of films impregnated with PAPSS of 0.5, 1, and 2% showed no significant difference. Meanwhile, 4% PAPSS films significantly decreased the values of mechanical properties compared to the films impregnated with different PAPSS levels. Values of the oxygen permeability and water vapor permeability for PAPSS impregnated films decreased significantly with greater PAPSS. The results indicate that 4% PAPSS impregnated in LLDPE films had high affinity of moisture absorbencies compared to the other films. The mathematical equation that best described the moisture sorption isotherm of each film sample was the GAB equation at 25 .deg. C. The crystallization and melting temperatures of PAPSS films were influenced by the addition of PAPSS material, but showed good thermal stability

  17. Preparation and Properties of Moisture-absorbing Film Impregnated with Polyacrylic Acid Partial Sodium Salt Material

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Youn Suk; Park, Insik [Yonsei University, Wonju (Korea, Republic of); Choi, Hong Yeol [CJ Cheiljedang, Seoul (Korea, Republic of)

    2014-08-15

    Moisture is a major factor causing the deteriorative physical change, microbial growth, and chemical reaction of the products. In this study, the moisture absorbing composite films have been prepared with moisture absorbing material of polyacrylic acid partial sodium salt (PAPSS) impregnated on LLDPE polymer for the functional packaging applications. The results showed that PAPSS impregnated film illustrated uniformly dispersed PAPSS particles in the LLDPE polymer matrix. The transparency of the PAPSS impregnated film decreased slightly at higher PAPSS concentrations. An increase in the PAPSS content for moisture-absorbing films showed a similar decrease in tensile strength, percent elongation at break, and tear strength. Their values of films impregnated with PAPSS of 0.5, 1, and 2% showed no significant difference. Meanwhile, 4% PAPSS films significantly decreased the values of mechanical properties compared to the films impregnated with different PAPSS levels. Values of the oxygen permeability and water vapor permeability for PAPSS impregnated films decreased significantly with greater PAPSS. The results indicate that 4% PAPSS impregnated in LLDPE films had high affinity of moisture absorbencies compared to the other films. The mathematical equation that best described the moisture sorption isotherm of each film sample was the GAB equation at 25 .deg. C. The crystallization and melting temperatures of PAPSS films were influenced by the addition of PAPSS material, but showed good thermal stability.

  18. Physical and Degradable Properties of Mulching Films Prepared from Natural Fibers and Biodegradable Polymers

    Directory of Open Access Journals (Sweden)

    Zhijian Tan

    2016-05-01

    Full Text Available The use of plastic film in agriculture has the serious drawback of producing vast quantities of waste. In this work, films were prepared from natural fibers and biodegradable polymers as potential substitutes for the conventional non-biodegradable plastic film used as mulching material in agricultural production. The physical properties (e.g., mechanical properties, heat preservation, water permeability, and photopermeability and degradation characteristics (evaluated by micro-organic culture testing and soil burial testing of the films were studied in both laboratory and field tests. The experimental results indicated that these fiber/polymer films exhibited favorable physical properties that were sufficient for use in mulching film applications. Moreover, the degradation degree of the three tested films decreased in the following order: fiber/starch (ST film > fiber/poly(vinyl alcohol (PVA film > fiber/polyacrylate (PA film. The fiber/starch and fiber/PVA films were made from completely biodegradable materials and demonstrated the potential to substitute non-biodegradable films.

  19. Effects of Preparation Conditions on the CuInS2 Films Prepared by One-Step Electrodeposition Method

    Directory of Open Access Journals (Sweden)

    Rongfeng Guan

    2015-01-01

    Full Text Available CuInS2 thin films were prepared onto indium tin oxide (ITO substrates by sulfurization of electrodeposited CuxInySz precursor films under S atmosphere. The influences of deposition potential, Cu2+/In3+ ratio, sulfurization temperature, and sulfur content on the CuInS2 thin films were investigated. Phases and structures were characterized by powder X-ray diffraction and Raman spectroscopy; surface morphology was characterized by Scanning Electron Microscopy; optical and electrical properties were characterized by UV-Vis absorption and Mott-Schottky curves, respectively. As a result, the optimal well-crystallized CuInS2 films preparation parameters were determined to be deposition potential of −0.8 V, Cu2+/In3+ ratio of 1.4, sulfur content of 1 g, and the sulfurization temperature of 550°C for 1 h; CuInS2 thin films prepared by one-step electrodeposition present the p-type semiconductor, with thickness about 4-5 μm and their optical band gaps in the range of 1.53~1.55 eV.

  20. Optimization of AZO films prepared on flexible substrates

    Indian Academy of Sciences (India)

    Administrator

    grey relational analysis, the optimization of these deposition process parameters for AZO thin films with multiple characteristics ... bias voltage, annealing temperature and plasma treatment deposition time (Pei et ... water and dried in nitrogen.

  1. High-mobility ultrathin semiconducting films prepared by spin coating.

    Science.gov (United States)

    Mitzi, David B; Kosbar, Laura L; Murray, Conal E; Copel, Matthew; Afzali, Ali

    2004-03-18

    The ability to deposit and tailor reliable semiconducting films (with a particular recent emphasis on ultrathin systems) is indispensable for contemporary solid-state electronics. The search for thin-film semiconductors that provide simultaneously high carrier mobility and convenient solution-based deposition is also an important research direction, with the resulting expectations of new technologies (such as flexible or wearable computers, large-area high-resolution displays and electronic paper) and lower-cost device fabrication. Here we demonstrate a technique for spin coating ultrathin (approximately 50 A), crystalline and continuous metal chalcogenide films, based on the low-temperature decomposition of highly soluble hydrazinium precursors. We fabricate thin-film field-effect transistors (TFTs) based on semiconducting SnS(2-x)Se(x) films, which exhibit n-type transport, large current densities (>10(5) A cm(-2)) and mobilities greater than 10 cm2 V(-1) s(-1)--an order of magnitude higher than previously reported values for spin-coated semiconductors. The spin-coating technique is expected to be applicable to a range of metal chalcogenides, particularly those based on main group metals, as well as for the fabrication of a variety of thin-film-based devices (for example, solar cells, thermoelectrics and memory devices).

  2. High-mobility ultrathin semiconducting films prepared by spin coating

    Science.gov (United States)

    Mitzi, David B.; Kosbar, Laura L.; Murray, Conal E.; Copel, Matthew; Afzali, Ali

    2004-03-01

    The ability to deposit and tailor reliable semiconducting films (with a particular recent emphasis on ultrathin systems) is indispensable for contemporary solid-state electronics. The search for thin-film semiconductors that provide simultaneously high carrier mobility and convenient solution-based deposition is also an important research direction, with the resulting expectations of new technologies (such as flexible or wearable computers, large-area high-resolution displays and electronic paper) and lower-cost device fabrication. Here we demonstrate a technique for spin coating ultrathin (~50Å), crystalline and continuous metal chalcogenide films, based on the low-temperature decomposition of highly soluble hydrazinium precursors. We fabricate thin-film field-effect transistors (TFTs) based on semiconducting SnS2-xSex films, which exhibit n-type transport, large current densities (>105Acm-2) and mobilities greater than 10cm2V-1s-1-an order of magnitude higher than previously reported values for spin-coated semiconductors. The spin-coating technique is expected to be applicable to a range of metal chalcogenides, particularly those based on main group metals, as well as for the fabrication of a variety of thin-film-based devices (for example, solar cells, thermoelectrics and memory devices).

  3. Preparation of transparent BN films with superhydrophobic surface

    International Nuclear Information System (INIS)

    Li Guoxing; Liu Yi; Wang Bo; Song Xuemei; Li Er; Yan Hui

    2008-01-01

    A novel approach was investigated to obtain the superhydrophobicity on surfaces of boron nitride films. In this method boron nitride films were deposited firstly on Si(1 0 0) and quartz substrate using a radio frequency (RF) magnetron sputtering system, and then using CF 4 plasma treatment, the topmost surface area can be modified systematically. The results have shown that the water contact angle on such surfaces can be tuned from 67 deg. to 159 deg. The films were observed to be uniform. The surfaces of films consist of micro-features, which were confirmed by Atomic Force Micrograph. The chemical bond states of the films were determined by Fourier Transform Infrared (FTIR) Spectroscopy, which indicate the dominance of B-N binding. According to the X-ray Photoelectron Spectroscopy analysis, the surface of film is mainly in BN phase. The micro-feature induced surface roughness is responsible for the observed superhydrophobic nature. The water contact angles measured on these surfaces can be modeled by the Cassie's formulation

  4. Preparation and characterization of sponge film made from feathers.

    Science.gov (United States)

    Zhuang, Yuan; Wu, Xiaoqian; Cao, Zhangjun; Zhao, Xiaoxiang; Zhou, Meihua; Gao, Pin

    2013-12-01

    Feather wastes generated from poultry farms will pose a problem for disposal, but they are sustainable resources of keratin. Reduction is one of the commonly used methods to obtain soluble keratin from feather. However, the residues generated during feather reduction reaction were rarely investigated. In this study, the residues were transformed into a porous and flexible sponge film by freeze-drying without pretreatment or addition of cross-linking agents. Glycerol was used to alter the physical and chemical characteristics of the sponge film. The film was characterized with a fiber strong stretch instrument, a Fourier transform infrared spectrophotometer, scanning electron microscopy, an elemental analyzer, a differential scanning calorimeter and an automatic air permeability apparatus. Tensile strength and melting point of the sponge film with the optimum glycerol content were 6.2 MPa and 170°C respectively. Due to air permeability of 368 mm/s, the film can potentially be used in medicine, biology, textile, environmental technology, and so on. It is ecologically friendly and will produce additional benefits from the renewable materials. The film was utilized as adsorbents to remove Cr(VI) from aqueous solutions and as a filtering material for air pollution. Its maximum Cr(VI) uptake capacity was about 148.8 mg/g and the removal rate of PM10 was 98.3%. © 2013.

  5. Development of technology for the large-scale preparation of 60Co polymer film source

    International Nuclear Information System (INIS)

    Udhayakumar, J.; Pardeshi, G.S.; Gandhi, Shymala S.; Chakravarty, Rubel; Kumar, Manoj; Dash, Ashutosh; Venkatesh, Meera

    2008-01-01

    60 Co sources (∼37 kBq) in the form of a thin film are widely used in position identification of perforation in offshore oil-well explorations. This paper describes the large-scale preparation of such sources using a radioactive polymer containing 60 Co. 60 Co was extracted into chloroform containing 8-hydroxyquinoline. The chloroform layer was mixed with polymethyl methacrylate (PMMA) polymer. A large film was prepared using the polymer solution containing the complex. The polymer film was then cut into circular sources, mounted on a source holder and supplied to various users

  6. Comparison of barium titanate thin films prepared by inkjet printing and spin coating

    Directory of Open Access Journals (Sweden)

    Jelena Vukmirović

    2015-09-01

    Full Text Available In this paper, barium titanate films were prepared by different deposition techniques (spin coating, office Epson inkjet printer and commercial Dimatix inkjet printer. As inkjet technique requires special rheological properties of inks the first part of the study deals with the preparation of inks, whereas the second part examines and compares structural characteristics of the deposited films. Inks were synthesized by sol-gel method and parameters such as viscosity, particle size and surface tension were measured. Deposited films were examined by optical and scanning electron microscopy, XRD analysis and Raman spectroscopy. The findings consider advantages and disadvantages of the particular deposition techniques.

  7. Preparation and characterization of ZnTe thin films by SILAR method

    International Nuclear Information System (INIS)

    Kale, S.S.; Mane, R.S.; Pathan, H.M.; Shaikh, A.V.; Joo, Oh-Shim; Han, Sung-Hwan

    2007-01-01

    Nanocrystalline zinc telluride (ZnTe) thin films were prepared by using successive ionic layer adsorption and reaction (SILAR) method from aqueous solutions of zinc sulfate and sodium telluride. The films were characterized by X-ray diffraction, scanning electron microscopy, energy dispersive X-ray analysis and optical absorption measurement techniques. The synthesized ZnTe thin films were nanocrystalline with densely aggregated particles in nanometer scale and were free from the voids or cracks. The optical band gap energy of the film was found to be thickness dependent. The elemental chemical compositional stoichiometric analysis revealed good Zn:Te elemental ratio of 53:47

  8. Preparation and properties of silk sericin/cellulose cross-linking films

    Directory of Open Access Journals (Sweden)

    Wang Kunyan

    2017-01-01

    Full Text Available Silk sericin/cellulose cross-linked films were successfully prepared using glutaraldehyde as cross-linkinger. FTIR was applied to characterize the chemical structure of films. Cross-linked silk sericin film was found the peak intensity of FTIR for cross-linked film decreased markedly compared to pure silk sericin, which indicating cross-linking reaction has been occurred. The increasing value of swelling ratio also indicated the cross-linking has been happened. The cross-linking reaction increased the thermal decomposition temperature.

  9. Pharmaceutical films made from the waste material from the preparation of propolis extracts: development and characterization

    Directory of Open Access Journals (Sweden)

    Lucas de Alcântara Sica de Toledo

    2015-12-01

    Full Text Available abstract This study investigated the development and characterized the physicochemical properties of films obtained from by-products (BP from the preparation of propolis extracts. Films were produced in the presence and absence of a polymeric adjuvant (gelatin or ethylcellulose and propylene glycol by a solvent casting method. Density, surface topography by scanning electron microscopy, mechanical properties (folding endurance, tensile strength and percentage elongation, water vapour permeability (WVP, moisture uptake capacity, thermogravimetry, differential scanning calorimetry and Fourier transform infrared spectroscopy (FTIR were determined. The films were a transparent, light greenish-yellow colour, with a uniform surface, and were flexible and easy to handle. The thickness and density of the preparations indicated that the compounds were homogeneously dispersed throughout the film. Mechanical properties were influenced by the film composition; films containing gelatin were more resistant to stress, while those containing ethylcellulose were more flexible. Increasing the adjuvant concentration decreased the elasticity and the rupture resistance, but increased the moisture uptake capacity and WVP of the formulations. BP was thermally stable as were the films. FTIR tests suggested interactions between BP and the adjuvants. This work could contribute to the utilization of BP to prepare films for food and pharmaceutical uses

  10. Optical properties of titanium di-oxide thin films prepared by dip coating method

    Science.gov (United States)

    Biswas, Sayari; Rahman, Kazi Hasibur; Kar, Asit Kumar

    2018-05-01

    Titanium dioxide (TiO2) thin films were prepared by sol-gel dip coating method on ITO coated glass substrate. The sol was synthesized by hydrothermal method at 90°C. The sol was then used to make TiO2 films by dip coating. After dip coating the rest of the sol was dried at 100°C to make TiO2 powder. Thin films were made by varying the number of dipping cycles and were annealed at 500°C. XRD study was carried out for powder samples that confirms the formation of anatase phase. Transmission spectra of thin films show sharp rise in the violet-ultraviolet transition region and a maximum transmittance of ˜60%. Band gap of the prepared films varies from 3.15 eV to 3.22 eV.

  11. Degradability of polylactide films by commercial microbiological preparations for household composters

    Directory of Open Access Journals (Sweden)

    Morawska Magda

    2017-09-01

    Full Text Available Environmentally friendly polymers such as polylactide are increasingly becoming available for use in packaging applications. The main advantages of polylactide packaging are evident. Polylactide is based on renewable resources and can be degraded in compost or soil. The studies on degradability of polylactide (PLA films by commercial preparation of mixture of multi-active saprophytic soil microorganisms, bacteria, actinomycetes and fungi have been done. Unmodified PLA film, metalized co-extruded PLA film and modified by silicon oxide PLA film were incubated in the liquid nutritious medium (TSB prepared to support the growth of microorganisms. The degradability of polylactide films was examined by macro and microscopic observations of surface, changes of mass and crystallinity of polymer samples before and after incubation. The obtained results indicate that the degradation of polylactide was accelerated by the presence of a biological vaccine. It was found that PLA degradation in the inoculated TSB broth was a result of both: enzymatic and chemical hydrolysis.

  12. Preparation of Pb(Zr, Ti)O3 Thin Films by Plasma-Assisted Sputtering

    Science.gov (United States)

    Hioki, Tsuyoshi; Akiyama, Masahiko; Ueda, Tomomasa; Onozuka, Yutaka; Suzuki, Kouji

    1999-09-01

    A novel plasma-assisted RF magnetron sputtering system with an immersed coil antenna between a target and a substrate was applied for preparing Pb(Zr, Ti)O3 (PZT) thin films. The antenna enabled the generation of inductively coupled plasma (ICP) independently of the target RF source. The plasma assisted by the antenna resulted in the changes of ion fluxes and these energy distributions irradiating to the substrate. The crystalline phase of the deposited PZT thin films was occupied by the perovskite phase depending on the antenna power. In addition, a high deposition rate, modified uniformity of film thickness, and a dense film structure with large columnar grains were obtained as a result of effects of the assisted plasma. The application of the plasma-assisted sputtering method may enable the preparation of PZT thin films that haveexcellent properties.

  13. The Preparation and Property of Graphene /Tin Oxide Transparent Conductive Film

    Directory of Open Access Journals (Sweden)

    SUN Tao

    2017-02-01

    Full Text Available Graphene doped tin oxide composites were prepared with SnCIZ·2HZ 0 and graphene oxide as raw materials with sol-gel method and then spincoated on the quartz glass to manufacture a new transparent conductive film. The composite film was characterized with X-ray diffraction(XRDand scanning electron microscopy(SEM analysis. XRD results show that the graphene oxide was successfully prepared with Hummers method. The graphene layers and particulate SnOZ can be clearly observed in SEM photos. The transmittance and conductivity of the thin films were tested with ultraviolet visible spectrophotometer and Hall effect measurement. The results show that the transmittivity of composite film in visible region is more than 90% and surface square resistance is 41 S2/口.The graphene/ SnOZ film exhibits a higher performance in transparence and conductivity than commercial FTO glass.

  14. Influence of the Preparation Method, DC and RF Sputtering, on theProperties of Thin Film

    International Nuclear Information System (INIS)

    Tri-Mardji-Atmono; Widdi-Usada; Agus-Purwadi; Yunanto; Edi-Suharyadi

    2000-01-01

    The research on the influence of preparation method DC- and RF Sputteringon the properties of Fe-thin films has been done. The measurement with EDAXshows. that the Fe-content of RF-sputtered film increased with the increasingof self-bias voltage in the range of 850 - 1000 V. The observation ofmicrostructure using SEM shows a more homogeneity of thin film and smallergrain size with the increasing of the self-bias voltage. On the other hand,thin films with inhomogeneity of the structure were produced by DC-Sputteringprocess, indicated by the non continuity and the spread of theglow-discharge. Based on the investigation with X-ray diffraction, thin filmprepared by RF-Sputtering was amorphous, while the film produced by theDC-Sputtering is known as crystal structure. Preparation using DC-voltageshows continual sputtering-process at the voltage of 3000 V betweenelectrode. (author)

  15. Grain size increase in pentacene thin films prepared in low-pressure gas ambient

    International Nuclear Information System (INIS)

    Yokoyama, Takamichi; Park, Chang Bum; Nagashio, Kosuke; Kita, Koji; Toriumi, Akira

    2009-01-01

    We studied a mechanism of grain size increase (that is, island density decrease) in pentacene film prepared in hydrogen (H 2 ) ambient. The island densities of pentacene films prepared in helium and deuterium were lower than those of vacuum-deposited films. This indicates that the decrease in the island density was not due to the chemical interaction between H 2 and pentacene or the substrate surface. Furthermore, the temperature dependence of the island density indicates that there is no difference in the surface diffusion energy in a vacuum and in H 2 . We also improved mobility significantly in the pentacene thin film transistor fabricated on film grown in H 2 ambient on a chemically treated substrate.

  16. Levitation force of melt-textured YBCO superconductors under non-quasi-static situation

    Science.gov (United States)

    Zhao, Z. M.; Xu, J. M.; Yuan, X. Y.; Zhang, C. P.

    2018-06-01

    The superconducting levitation force of a simple superconductor-magnet system under non-quasi-static situation is investigated experimentally. Two yttrium barium copper oxide (YBCO) samples with different performances are chosen from two small batches of samples prepared by the top-seeded melt-textured growth process. The residual carbon content of the precursor powders of the two batches is different due to different heat treatment processes. During the experimental process for measuring the levitation force, the value of the relative speed between the YBCO sample and the permanent magnet is higher than that in conventional studies. The variation characteristics of the superconducting levitation force are analyzed and a crossing phenomenon in the force-displacement hysteresis curves is observed. The results indicate that the superconducting levitation force is different due to the different residual carbon contents. As residual carbon contents reduce, the crossing phenomenon is more obvious accordingly.

  17. First steps towards cube textured nickel profile wires for YBCO-coated conductors

    International Nuclear Information System (INIS)

    Eickemeyer, J.; Gueth, A.; Freudenberger, J.; Holzapfel, B.; Schultz, L.

    2011-01-01

    The cube texture as a typical sheet texture can also be formed by cold drawing and recrystallization in profile wires. Cube textured Ni profile wires containing up to 96.2% cube oriented grains in the central region were obtained. Forthcoming investigations are promising to get a textured substrate wire for YBCO-coated conductors. Cube textured nickel alloy tapes prepared by cold rolling and annealing (RABiTS method) represent a standard metallic substrate for superconductor coatings of the YBa 2 Cu 3 O 7-δ (YBCO) type. These tapes have a width to thickness ratio of about 30-100. However, a value of close to one is optimal concerning low energetic losses under alternating current applications. First experiments on micro-alloyed nickel prove that the cube texture as a typical sheet texture can also be formed in profile wires with a rectangular cross-section after cold drawing and recrystallization treatment.

  18. Interaction of ultra soft magnetic materials with the high-T{sub c} superconductor YBCO

    Energy Technology Data Exchange (ETDEWEB)

    Stahl, Claudia; Treiber, Sebastian; Schuetz, Gisela [Max Planck Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Walker, Patrick [Max Planck Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany); Albrecht, Joachim [Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany)

    2013-07-01

    We have grown bilayers of optimally doped YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO) and ferromagnetic CoFeB on single-crystalline substrates by pulsed laser deposition and sputtering. These heterostructures are typically composed of about 100 nm YBCO and several 10 nm of CoFeB. Regarding the superconductor, the properties of the YBCO film change as a consequence of the vicinity of the ferromagnet. In detail we investigated the critical current density as a function of temperature, applied field and time as well as the transition temperature by SQUID magnetization measurements and quantitative magneto-optical measurements. The amorphous material CoFeB exhibits an in plane anisotropy and a very low coercivity. From magneto-optical images we find that the flux line lattice of the superconductor is mapped into the magnet and still visible as significant magnetic out-of-plane contrast at room temperature. We discuss this phenomenon as a new route to high-resolution mapping of the flux line distribution on a nanometer scale.

  19. Preparation of thin-film (Ba(0.5),Sr(0.5))TiO3 by the laser ablation technique and electrical properties

    Science.gov (United States)

    Yoon, Soon-Gil; Lee, Jai-Chan; Safari, A.

    1994-09-01

    The chemical composition and electrical properties were investigated for epitaxially crystallized (Ba(0.5),Sr(0.5))TiO3 (BST) films deposited on Pt/MgO and YBa2Cu3O(7-x) (YBCO)/MgO substrates by the laser ablation technique. Rutherford backscattering spectroscopy analysis shows that thin films on Pt/MgO have almost the same stoichiometric composition as the target material. Films deposited at 600 C exhibited an excellent epitaxial growth, a dielectric constant of 430, and a dissipation factor of 0.02 at 10 kHz frequency. They have a charge storage density of 40 fC/sq micron at an applied electric field of 0.15 MV/cm. Leakage current density of BST thin films on Pt/MgO was smaller than on YBCO/MgO. Their leakage current density is about 0.8 microA/sq cm at an applied electric field of 0.15 MV/cm.

  20. Effect of Au nano-particles doping on polycrystalline YBCO high temperature superconductor

    Energy Technology Data Exchange (ETDEWEB)

    Dadras, Sedigheh, E-mail: dadras@alzahra.ac.ir; Gharehgazloo, Zahra

    2016-07-01

    In this research, we prepared different Au nanoparticles (0.1–2 wt%) doped YBCO high temperature superconductor samples by sol-gel method. To characterize the samples, we used X-Ray diffraction (XRD) and scanning electron microscope (SEM) analysis. Results show the formation of orthorhombic phase of superconductivity for all prepared samples. We observed that by adding Au nanoparticles, the grains' size of the samples reduces from 76 nm to 47 nm as well. The critical current density (J{sub c}) and transition temperature (T{sub c}) were determined using current versus voltage (I–V) and resistivity versus temperature (ρ-T) measurements, respectively. We found that by increasing Au nanoparticles in the compound, in comparison to the pure YBCO sample, the transition temperature, pinning energy and critical current density will increase. Also, the highest J{sub c} is for 1 wt% Au doped YBCO compound that its critical current density is about 8 times more than the J{sub c} of pure one in 0.7 T magnetic field.

  1. The preparation of Nb3Ge thin film superconductors in a UHV evaporation and sputter device

    International Nuclear Information System (INIS)

    Krevet, B.; Schauer, W.; Wuechner, F.

    1978-10-01

    Thin film techniques like evaporation or sputtering are remarkbly suitable to vary the metallurgical and physical properties of superconductors in a wide range. In the case of the A15-compound Nb 3 Ge only these preparation techniques allow us to produce a metastable pure phase in stoichiometric composition and to study its superconducting properties. The presen report describes two UHV-plants to produce superconducting films by multisource coevaporation and cosputtering. Of special importance are the constancy, monitoring and control of the evaporation rate, and the thermalization of the sputter components on the other hand. The experimental methods used are explained in detail and discussed together with the results of Nb 3 Ge films. With the preparation parameters suitably chosen both techniques allow to prepare reproducibly Nb 3 Ge films with 21 K transition temperature (onset); under optimized conditions Tc values up to 22.3 K have been reached. (orig.) [de

  2. Preparation, Characterization, and Electrochromic Properties of Nanocellulose-Based Polyaniline Nanocomposite Films.

    Science.gov (United States)

    Zhang, Sihang; Sun, Gang; He, Yongfeng; Fu, Runfang; Gu, Yingchun; Chen, Sheng

    2017-05-17

    On the basis of nanocellulose obtained by acidic swelling and ultrasonication, rodlike nanocellulose/polyaniline nanocomposites with a core-shell structure have been prepared via in situ polymerization. Compared to pure polyaniline, the nanocomposites show superior film-forming properties, and the prepared nanocomposite films demonstrate excellent electrochemical and electrochromic properties in electrolyte solution. Nanocomposite films, especially the one prepared with 40% polyaniline coated nanocomposite, exhibited faster response time (1.5 s for bleaching and 1.0 s for coloring), higher optical contrast (62.9%), higher coloration efficiency (206.2 cm 2 /C), and more remarkable switching stability (over 500 cycles). These novel nanocellulose-based nanorod network films are promising novel electrochromic materials with excellent properties.

  3. In-situ laser processing and microstructural characteristics of YBa2Cu3O7-δ thin films on Si with TiN buffer layer

    International Nuclear Information System (INIS)

    Tiwari, P.; Zheleva, T.; Narayan, J.

    1993-01-01

    The authors have prepared high-quality superconducting YBa 2 Cu 3 O 7 -δ (YBCO) thin films on Si(100) with TiN as a buffer layer using in-situ multitarget deposition system. Both TiN and YBCO thin films were deposited sequentially by KrF excimer laser ( | = 248 nm ) at substrate temperature of 650 C . Thin films were characterized using X-ray diffraction (XRD), four-point-probe ac resistivity, scanning electron microscopy (S E M), transmission electron microscopy (TEM), and Rutherford backscattering (RBS). The TiN buffer layer was epitaxial and the epitaxial relationship was found to be cube on cube with TiN parallel Si. YBCO thin films on Si with TiN buffer layer showed the transition temperature of 90-92K with T co (zero resistance temperature) of 84K. The authors have found that the quality of the buffer layer is very important in determining the superconducting transition temperature of the thin film. The effects of processing parameters and the correlation of microstructural features with superconducting properties are discussed in detail

  4. Preparation and water absorption of cross-linked chitosan/silk fibroin blend films

    International Nuclear Information System (INIS)

    Suesat, Jantip; Rujiravanit, Ratana; Jamieson, Alexander M.; Tokura, Seiichi

    2001-01-01

    Natural polymer blend films composed of chitosan and silk fibroin were prepared by varying the ratio of chitosan to silk fibroin, with and without glutaraldehyde as a crosslinking agent. The effects of the ratio of chitosan to silk fibroin and crosslinking agent on swelling behavior of the blend films were studied. For the swelling behavior, the blend films exhibited a dramatic change in the degree of swelling when immersed in acidic solutions. The degree of swelling of the films increased as the chitosan content increased; the blend film with 80% chitosan content had the maximum degree of swelling. It appeared that crosslinking had occurred in the blend films which helped the films to retain their three dimensional structure. In addition, FTIR spectra of the films showed evidence of hydrogen bonding interaction between chitosan and silk fibroin. For the effect of salt type, the films were immersed in various types of aqueous salt solutions, viz NaCl, LiCl, CaCl 2 , AlCl 3 , and FeCl 3 . The films immersed in AlCl 3 and FeCl 3 aqueous solutions gave the maximum degree of swelling. The effects of AlCl 3 and FeCl 3 concentrations on swelling behavior were also investigated. It was found that the maximum degree of swelling of the films occurred at 1.0 x 10 -2 M of AlCl 3 and FeCl 3 aqueous solutions. (author)

  5. Nanotechnology as a way to overcome the rapid J{sub c} fall with HTS film thickness

    Energy Technology Data Exchange (ETDEWEB)

    Svetchnikov, V L; Flis, V S; Kalenyuk, A A; Kasatkin, A L; Rebikov, A I; Moskaliuk, V O; Pan, V M; Tretiatchenko, C G, E-mail: pan@imp.kiev.u [Institute for Metal Physics, 36 Vernadsky Blvd, Kiev 03142 (Ukraine)

    2010-06-01

    We have carried out a comprehensive study of a relation between the nanostructure and electromagnetic properties of the films prepared by pulse laser deposition on LaAlO{sub 3} substrates using YBCO targets with BaZrO{sub 3} additives. HREM studies revealed that depending on the deposition conditions BZO can precipitate as nanorods normal to the substrate or as BaYZr{sub x}O{sub y} nano-pancakes. BZO nanorods are formed at lower laser power and higher substrate temperature. Their lattice is rotated by 3-4{sup 0} to provide matching with matrix without dislocations. In a contrary, the nano-pancakes are surrounded with a great number of dislocations. Mechanisms of the nanostructure formation have been analyzed. Embedding of a proper kind of nanoparticles into HTS films leads not only to a certain increase of the critical current density J{sub c} but to a substantial weakening of its field and thickness dependences compared with pure YBCO films. Negative curvature of I-V-curves (in double-log scale) for YBCO (BZO) films is an evidence of strong pinning on extended defects, such as nanorods and threading dislocations, and/or collective vortex pinning.

  6. Incorporation of self-organised gold nano crystals in YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} thin films: Modification of superconducting properties

    Energy Technology Data Exchange (ETDEWEB)

    Katzer, Christian; Michalowski, Peter; Westerhausen, Markus; Koch, Stefanie; Schmidl, Frank; Seidel, Paul [Institut fuer Festkoerperphysik, Friedrich-Schiller-Universitaet Jena, Helmholtzweg 5, 07743 Jena (Germany); Treiber, Sebastian [Max-Planck-Institut fuer Intelligente Systeme, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Albrecht, Joachim [Hochschule Aalen, Beethovenstrasse 1, 73430 Aalen (Germany)

    2012-07-01

    Using pulsed laser deposition we are able to fabricate and examine Yttrium-Barium-Copper-Oxide (YBCO) thin films of high quality. A particular point of interest thereby is the influence of a pre-deposited gold layer with a well-defined film thickness. During the growth of the YBCO thin film the intermediate gold layer self assembles into crystalline nano particles, which modify the growth conditions and hence the physical properties of the growing YBCO. We report on the modification of structural and superconducting properties of our YBCO thin films (such as rocking curve widths, critical temperature T{sub c} and critical current density j{sub c}) comparing conventional to Au added YBCO. The temperature dependence of the critical current density thereby was determined using transport measurements as well as magneto-optical measurements. Furthermore investigations of the flux noise of our gold modified YBCO films are presented.

  7. Preparation and analysis of superconducting Nb-Ge films

    International Nuclear Information System (INIS)

    Testardi, L.R.; Meek, R.L.; Poate, J.M.; Royer, W.A.; Storm, A.R.; Wernick, J.H.

    1975-01-01

    The dependences of T/subc/, resistivity, resistance ratio, and structure on chemical composition and sputtering conditions for Nb-Ge films have been studied. The chemical composition, impurity content, and x-ray structure were obtained using Rutherford backscattering, nuclear techniques, and x-ray diffraction. Although T/subc/ varies with composition, it is not found to be critically dependent upon exact stoichiometry; the Nb/Ge ratios vary by approx. 13% (2.6 to 3) for films with approx. 23-K onsets and by approx. 40% (2.2 to 3.3) for films with approx. 20-K onsets. For compositions similar to the bulk, the films have comparitively much higher T/subc/'s and smaller lattice parameters. X-ray results show the films to contain predominately A-15 phase (except for Nb/Ge less-than or equal to 2.5) with lattice parameters varying from 5.15 A for Nb-rich low-T/subc/ films to 5.12 A for Ge-rich films. Several percent of oxygen and carbon occur in low-T/subc/ amorphous films deposited at 650 degreeC but this is considerably reduced in high-T/subc/ films made simultaneously at approx. 750 degreeC. No argon was found and the nitrogen content was generally less than 1%. No correlation of high T/subc/'s and impurities was found. The optimum deposition temperature and resistivity are lowest, and the resistance ratio highest for Nb/Ge ratios somewhat below 3/1. A simple correlation of T/subc/ and resistance ratio is reported which is largely independent of all sputtering conditions and composition and which suggests that slightly higher T/subc/'s may be possible. Negative bias was found to be detrimental to T/subc/ while positive bias had relatively little effect. Magnetic-field-assisted sputtering led to significant increases in the sputtering rate and the optimum deposition temperature

  8. Electrochromic Properties of Tungsten Oxide Films Prepared by Reactive Sputtering

    Science.gov (United States)

    Kim, Min Hong; Kang, Tai Young; Jung, Yu Sup; Kim, Kyung Hwan

    2013-05-01

    WO3-x thin films were deposited on induim tin oxide (ITO) glass substrates with various oxygen flow ratios from 0.55 to 0.7 by the reactive facing-target sputtering method, at a power density of 4 W/cm2 and room temperature. The structural properties of the WO3-x thin films were measured by X-ray diffractometry and Raman spectral analysis. As-deposited WO3-x thin films had an amorphous structure. In the Raman spectra, WO3-x thin films exhibited two strong peaks at 770 and 950 cm-1 attributed to the vibrations of W6+-O and W6+=O bonds, respectively. The electrochemical and optical properties of WO3-x thin films were measured by cyclic voltammetry and UV/vis spectrometry. The results showed the highest charge density at an oxygen flow ratio of 0.7 and the highest transmittance in the visible range. The maximum coloration efficiency was 30.82 cm2/C at an oxygen flow ratio of 0.7.

  9. Strong composite films with layered structures prepared by casting silk fibroin-graphene oxide hydrogels

    Science.gov (United States)

    Huang, Liang; Li, Chun; Yuan, Wenjing; Shi, Gaoquan

    2013-04-01

    Composite films of graphene oxide (GO) sheets and silk fibroin (SF) with layered structures have been prepared by facile solution casting of SF-GO hydrogels. The as-prepared composite film containing 15% (by weight, wt%) of SF shows a high tensile strength of 221 +/- 16 MPa and a failure strain of 1.8 +/- 0.4%, which partially surpass those of natural nacre. Particularly, this composite film also has a high modulus of 17.2 +/- 1.9 GPa. The high mechanical properties of this composite film can be attributed to its high content of GO (85 wt%), compact layered structure and the strong hydrogen bonding interaction between SF chains and GO sheets.Composite films of graphene oxide (GO) sheets and silk fibroin (SF) with layered structures have been prepared by facile solution casting of SF-GO hydrogels. The as-prepared composite film containing 15% (by weight, wt%) of SF shows a high tensile strength of 221 +/- 16 MPa and a failure strain of 1.8 +/- 0.4%, which partially surpass those of natural nacre. Particularly, this composite film also has a high modulus of 17.2 +/- 1.9 GPa. The high mechanical properties of this composite film can be attributed to its high content of GO (85 wt%), compact layered structure and the strong hydrogen bonding interaction between SF chains and GO sheets. Electronic supplementary information (ESI) available: XPS spectrum of the SF-GO hybrid film, SEM images of lyophilized GO dispersion and the failure surface of GO film. See DOI: 10.1039/c3nr00196b

  10. Morphology of CdSe films prepared by chemical bath deposition: The role of substrate

    International Nuclear Information System (INIS)

    Simurda, M.; Nemec, P.; Formanek, P.; Nemec, I.; Nemcova, Y.; Maly, P.

    2006-01-01

    We combine optical spectroscopy and transmission electron microscopy to study the growth and the structural morphology of CdSe films prepared by chemical bath deposition (CBD) on two considerably different substrates. The films grown on glass are compact and strongly adherent to the substrate. On the contrary, the films deposited on carbon-coated glass (with approx. 20 nm thick amorphous carbon layer) are only loosely adherent to the substrate. Using transmission electron microscopy we revealed that even though the films grown on both substrates are assembled from closely spaced nanocrystals with diameter of about 5 nm, the films morphology on the sub-micrometer scale is considerably different in the two cases. While the films deposited on glass are rather compact, the films prepared on carbon layer have high porosity and are formed by interconnected spheres which size is dependent on the duration of deposition (e.g. 155 nm for 6 h and 350 nm for 24 h). This shows that the choice of the substrate for CBD has a stronger influence on the sub-micrometer film morphology than on the properties of individual nanocrystals forming the film

  11. Preparation and characterization of micro-grid modified In_2O_3:W films

    International Nuclear Information System (INIS)

    Dong, Dongmei; Wang, Wenwen; Zhang, Fan; Fu, Qiang; Pan, Jiaojiao

    2016-01-01

    Tungsten doped indium oxide (In_2O_3:W, IWO) thin films with IWO micro-grid covered surface were prepared at room temperature using techniques of radio frequency (RF) magnetron sputtering and polystyrene (PS) microsphere template. The composition, crystallization structures, surface morphologies, and optical and electrical properties of the films were characterized by X-ray photoelectron spectroscopy, X-ray diffraction, scanning electron microscopy, spectrophotometer from visible to near infrared (NIR) range and Hall effect measurement, respectively. Periodic micro-grid modified surface was obtained to improve light trapping properties. The effects of the PS micro-spheres diameters and the sputtering time on the surface morphology, transmittance in NIR range, diffuse reflection and conductive properties of the IWO films are investigated. Experiments show that surface modification of the IWO film with micro-grid under the optimized condition can improve the conductivity of the films by 15%, and the diffuse reflectance by 150%, with less than 8% decrease of the transmittance in the visible region. The study would be beneficial to the light trapping effect of solar cells using IWO films as transparent electrodes. - Highlights: • In_2O_3:W (IWO) films were obtained by reactive frequency magnetron sputtering. • IWO micro-grids were prepared on the surface of IWO films. • Influences of micro-grid size and sputtering time on IWO films were analyzed. • Both high conductivity and transparency are acquired in near-infrared region.

  12. CdS thin films prepared by laser assisted chemical bath deposition

    International Nuclear Information System (INIS)

    Garcia, L.V.; Mendivil, M.I.; Garcia Guillen, G.; Aguilar Martinez, J.A.; Krishnan, B.; Avellaneda, D.; Castillo, G.A.; Das Roy, T.K.; Shaji, S.

    2015-01-01

    Highlights: • CdS thin films by conventional CBD and laser assisted CBD. • Characterized these films using XRD, XPS, AFM, optical and electrical measurements. • Accelerated growth was observed in the laser assisted CBD process. • Improved dark conductivity and good photocurrent response for the LACBD CdS. - Abstract: In this work, we report the preparation and characterization of CdS thin films by laser assisted chemical bath deposition (LACBD). CdS thin films were prepared from a chemical bath containing cadmium chloride, triethanolamine, ammonium hydroxide and thiourea under various deposition conditions. The thin films were deposited by in situ irradiation of the bath using a continuous laser of wavelength 532 nm, varying the power density. The thin films obtained during deposition of 10, 20 and 30 min were analyzed. The changes in morphology, structure, composition, optical and electrical properties of the CdS thin films due to in situ irradiation of the bath were analyzed by atomic force microscopy (AFM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and UV–vis spectroscopy. The thin films obtained by LACBD were nanocrystalline, photoconductive and presented interesting morphologies. The results showed that LACBD is an effective synthesis technique to obtain nanocrystalline CdS thin films having good optoelectronic properties

  13. Fluorocarbon thin film with superhydrophobic property prepared by pyrolysis of hexafluoropropylene oxide

    International Nuclear Information System (INIS)

    Wang Jun; Song Xue; Li Rui; Shen Jinpeng; Yang Guangcheng; Huang Hui

    2012-01-01

    Highlights: ► We successfully prepared nanostructured fluorocarbon thin films using CVD method without any catalysts at low pyrolysis temperature (200–300 °C) of HFPO. ► The films show disparate morphology, high content of CF 2 (>90%), which are also characteristic of bulk PTFE. ► The film deposited at 300 °C shows superhydrophobic property (water contact angle of 172.7°). - Abstract: A fluorocarbon thin film with superhydrophobic property was prepared by chemical vapor deposition (CVD) method at low temperature (200–300 °C) via pyrolysis hexafluoropropylene oxide (HFPO). The experiment results indicated the morphology and structure of fluorocarbon films were strongly dependent on the pyrolysis temperature. As shown through atomic force microscope (AFM), the surface morphology of the films ranged from rodlike grains to sheets. Fourier transform infrared (FTIR) spectroscopy revealed that all the films contained the vibrational frequencies of linear CF 2 chains, which were also characteristic of bulk poly tetrafluoroethylene (PTFE). X-ray photoelectron spectroscopy (XPS) analysis showed that CF 2 structures were predominant in the films with high order. The film deposited at 300 °C exhibited a superhydrophobic surface with contact angle up to 172.7°.

  14. CdS thin films prepared by laser assisted chemical bath deposition

    Energy Technology Data Exchange (ETDEWEB)

    Garcia, L.V.; Mendivil, M.I.; Garcia Guillen, G.; Aguilar Martinez, J.A. [Facultad de Ingenieria Mecanica y Electrica, Universidad Autonoma de Nuevo Leon, Av. Pedro de Alba s/n, Ciudad Universitaria, San Nicolas de los Garza, Nuevo Leon 66450 (Mexico); Krishnan, B. [Facultad de Ingenieria Mecanica y Electrica, Universidad Autonoma de Nuevo Leon, Av. Pedro de Alba s/n, Ciudad Universitaria, San Nicolas de los Garza, Nuevo Leon 66450 (Mexico); CIIDIT – Universidad Autonoma de Nuevo Leon, Apodaca, Nuevo Leon (Mexico); Avellaneda, D.; Castillo, G.A.; Das Roy, T.K. [Facultad de Ingenieria Mecanica y Electrica, Universidad Autonoma de Nuevo Leon, Av. Pedro de Alba s/n, Ciudad Universitaria, San Nicolas de los Garza, Nuevo Leon 66450 (Mexico); Shaji, S., E-mail: sshajis@yahoo.com [Facultad de Ingenieria Mecanica y Electrica, Universidad Autonoma de Nuevo Leon, Av. Pedro de Alba s/n, Ciudad Universitaria, San Nicolas de los Garza, Nuevo Leon 66450 (Mexico); CIIDIT – Universidad Autonoma de Nuevo Leon, Apodaca, Nuevo Leon (Mexico)

    2015-05-01

    Highlights: • CdS thin films by conventional CBD and laser assisted CBD. • Characterized these films using XRD, XPS, AFM, optical and electrical measurements. • Accelerated growth was observed in the laser assisted CBD process. • Improved dark conductivity and good photocurrent response for the LACBD CdS. - Abstract: In this work, we report the preparation and characterization of CdS thin films by laser assisted chemical bath deposition (LACBD). CdS thin films were prepared from a chemical bath containing cadmium chloride, triethanolamine, ammonium hydroxide and thiourea under various deposition conditions. The thin films were deposited by in situ irradiation of the bath using a continuous laser of wavelength 532 nm, varying the power density. The thin films obtained during deposition of 10, 20 and 30 min were analyzed. The changes in morphology, structure, composition, optical and electrical properties of the CdS thin films due to in situ irradiation of the bath were analyzed by atomic force microscopy (AFM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and UV–vis spectroscopy. The thin films obtained by LACBD were nanocrystalline, photoconductive and presented interesting morphologies. The results showed that LACBD is an effective synthesis technique to obtain nanocrystalline CdS thin films having good optoelectronic properties.

  15. Preparation of gelatin films incorporated with tea polyphenol nanoparticles for enhancing controlled-release antioxidant properties.

    Science.gov (United States)

    Liu, Fei; Antoniou, John; Li, Yue; Yi, Jiang; Yokoyama, Wallace; Ma, Jianguo; Zhong, Fang

    2015-04-22

    Gelatin films incorporated with chitosan nanoparticles in various free/encapsulated tea polyphenol (TP) ratios were prepared in order to investigate the influence of different ratios on the physicochemical and antioxidant properties of films. The TP-containing nanoparticles were prepared by cross-linking chitosan hydrochloride (CSH) with sulfobutyl ether-β-cyclodextrin sodium (SBE-β-CD) at three different encapsulation efficiencies (EE; ∼50%, ∼80%, and ∼100%) of TP. The stability of TP-loaded nanoparticles was maintained during the film drying process from the analysis of free TP content in the redissolved film solutions. Composite films showed no significant difference in visual aspects, while the light transmittance (250-550 nm) was decreased with incorporation of TP. Nanoparticles appeared to be homogeneously dispersed within the film matrix by microstructure analysis (SEM and AFM). TP-loaded films had ferric reducing and DPPH radical scavenging power that corresponded to the EEs. Sunflower oil packaged in bags made of gelatin films embedded with nanoparticles of 80% EE showed the best oxidation inhibitory effect, followed by 100% EE, 50% EE, and free TP, over 6 weeks of storage. However, when the gelatin film was placed over the headspace and was not in contact with the oil, the free TP showed the best effect. The results indicate that sustained release of TP in the contacting surface can ensure the protective effects, which vary with free/encapsulated mass ratios, thus improving antioxidant activities instead of increasing the dosage.

  16. Preparation and characterization of osmium hexacyanoferrate films and their electrocatalytic properties

    Energy Technology Data Exchange (ETDEWEB)

    Chen, S.-M. [Department of Chemical Engineering, National Taipei University of Technology, No. 1, Section 3, Chung-Hsiao East Road, Taipei, Taiwan 106 (China)]. E-mail: smchen78@ms15.hinet.net; Liao, C.-J. [Department of Chemical Engineering, National Taipei University of Technology, No. 1, Section 3, Chung-Hsiao East Road, Taipei, Taiwan 106 (China)

    2004-11-15

    Osmium hexacyanoferrate films have been prepared using repeated cyclic voltammetry, and the deposition process and the films' electrocatalytic properties in electrolytes containing various cations have been investigated. The cyclic voltammograms recorded the deposition of osmium hexacyanoferrate films directly from the mixing of Os{sup 3+} and Fe(CN){sub 6}{sup 3-} ions from solutions containing various cations. An electrochemical quartz crystal microbalance, cyclic voltammetry, and UV-visible spectroscopy were used to study the growth mechanism of the osmium hexacyanoferrate films. The osmium hexacyanoferrate films showed a single redox couple, and the redox reactions included 'electron transfer' and 'proton transfer' with a formal potential that demonstrates a proton effect in acidic solutions up to a 12 M aqueous HCl solution. The electrochemical and electrochemical quartz crystal microbalance results indicate that the redox process was confined to the immobilized osmium hexacyanoferrate film. The electrocatalytic reduction of dopamine, epinephrine, norepinephrine, S{sub 2}O{sub 3}{sup 2-}, and SO{sub 5}{sup 2-} by the osmium hexacyanoferrate films was performed. The preparation and electrochemical properties of co-deposited osmium(III) hexacyanoferrate and copper(II) hexacyanoferrate films were determined, and their two redox couples showed formal potentials that demonstrated a proton effect and an alkaline cation effect, respectively. Electrocatalytic reactions on the hybrid films were also investigated.

  17. Studies of thin films of Ti- Zr -V as non-evaporable getter films prepared by RF sputtering

    International Nuclear Information System (INIS)

    Gupta, Nidhi; Jagannath,; Sharma, R. K.; Gadkari, S. C.; Muthe, K. P.; Mukundhan, R.; Gupta, S. K.

    2013-01-01

    Non-Evaporable Getter (NEG) films of the Ti-Zr-V prepared on stainless steel substrates by Radio Frequency sputtering. To observe its getter behavior at the lowest activation temperature, the sample is heated continuously at different temperatures (100°C, 150°C, 200°C and 250°C) for 2 hours. The changes of the surface chemical composition at different temperaturesare analyzed by using XPS and SEM (Scanning Electron Microscopy) techniques. The volume elemental composition of the film has been measured by energy dispersive X-ray spectroscopy (EDX). The in-situ XPS measurements of the activated getter films show the disappearance of the superficial oxide layer through the variation in the oxygen stoichiometry during thermal activation. Results of these studies show that the deposited films of Ti-Zr-V could be used as NEG to produce extreme high vacuum.

  18. Nanoporous zinc oxide films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Ghimpu, L.; Lupan, O.; Popescu, L.; Tiginyanu, I.M.

    2011-01-01

    In this paper we demonstrate an inexpensive approach for the fabrication of nanoporous zinc oxide films by using magnetron sputtering. Study of the structural properties proves the crystallographic perfection of porous nanostructures and the possibility of its controlling by adjusting the technological parameters in the growth process. The XRD pattern of nanoporous ZnO films exhibits high intensity of the peaks relative to the background signal which is indicative of the ZnO hexagonal phase and a good crystallinity of the samples grown by magnetron sputtering.

  19. Effect of preparation conditions on the diffusion parameters of Cu/Ni thin films

    Energy Technology Data Exchange (ETDEWEB)

    Rammo, N.N.; Makadsi, M.N. [College of Science, Baghdad University, Baghdad (Iraq); Abdul-Lettif, A.M. [College of Science, Babylon University, Hilla (Iraq)

    2004-11-01

    Diffusion coefficients of vacuum-deposited Cu/Ni bilayer thin films were determined in the temperature range 200-500 C using X-ray photoelectron spectroscopy, sheet resistance measurements, and X-ray diffraction analysis. The difference between the results of the present work and those of previous relevant investigations may be attributed to the difference in the film microstructure, which is controlled by the preparation conditions. Therefore, the effects of deposition rate, substrate temperature, film thickness, and substrate structure on the diffusion parameters were separately investigated. It is shown that the diffusion activation energy (Q) decreases as deposition rate increases, whereas Q increases as substrate temperature and film thickness increase. The value of Q for films deposited on amorphous substrates is less than that for films deposited on single-crystal substrates. (copyright 2004 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  20. Preparation and characterization of ZnO films by modified SILAR method

    International Nuclear Information System (INIS)

    Zhang Ling; Liu Jie; Hou Mingdong; Sun Youmei; Duan Jinlai; Yao Huijun; Mo Dan; Chen Yanfeng

    2009-01-01

    A modified solution method, successive ionic layer adsorption and reaction(SILAR), was applied to prepare transparent zinc oxide(ZnO) film on glass substrate at (125±5) degree C in mixed ion precursor solution. The surface morphology and crystallization of films were analyzed by field emission scanning microscopy (FESEM) and X-ray diffraction(XRD), respectively. The optical properties of the films were studied by ultraviolet visible(UV-Vis)spectroscopy. The results show that the obtained samples are polycrystalline films of hexagonal wurtzite structure, with the preference of [002] orientation. The as-deposited films exhibit uniform and compact surface morphology, with the film thickness of 550 nm, and have high transmittance in the visible band(>80%). (authors)

  1. Tribological performance of ultrathin diamond-like carbon films prepared by plasma-based ion implantation

    International Nuclear Information System (INIS)

    Liao, J X; Li, E Q; Tian, Z; Pan, X F; Xu, J; Jin, L; Yang, H G

    2008-01-01

    Ultrathin diamond-like carbon (DLC) films with thicknesses of 5-60 nm have been prepared on Si by plasma-based ion implantation. Raman spectrum and x-ray photoelectron spectroscopy (XPS) show that these DLC films present high sp 3 /sp 2 ratios. XPS also displays that each DLC film firmly adheres to the Si substrate owing to a C-Si transition layer. Atomic force microscopy shows that the DLC films are smooth and compact with average roughness (R a ) of about 0.25 nm. Sliding friction experiments reveal that these DLC films show significantly improved tribological performance. With increase of DLC film thickness, the sp 3 /sp 2 ratio increases, the roughness decreases, the hardness increases, the adhesive wear lightens and thereby the tribological performance becomes enhanced. Also, the effects of the applied load and the reciprocating frequency on the tribological performance are discussed

  2. A crude protective film on historic stones and its artificial preparation through biomimetic synthesis

    Science.gov (United States)

    Liu, Qiang; Zhang, Bingjian; Shen, Zhongyue; Lu, Huanming

    2006-12-01

    A biomimetic film has been found on the surface of the historic stone buildings and monuments. The stone inscriptions under the film are preserved so well that has not been damaged for more than 1000 years. Samples of the crude film have been analyzed by XRD, FTIR, PLM, EDA, SEM and TEM. The results show that it consists mainly of calcium oxalate monohydrate. On the basis of the existence of the organism debris, it is concluded that the film should be a product of biomineralization. According to this hypothesis, a similar film has been prepared on the stone surface through biomimetic synthesis in our laboratory. The preliminary analysis shows that the artificial protective film functions well.

  3. Characteristics of W Doped Nanocrystalline Carbon Films Prepared by Unbalanced Magnetron Sputtering.

    Science.gov (United States)

    Park, Yong Seob; Park, Chul Min; Kim, Nam-Hoon; Kim, Jae-Moon

    2016-05-01

    Nanocrystalline tungsten doped carbon (WC) films were prepared by unbalanced magnetron sputtering. Tungsten was used as the doping material in carbon thin films with the aim of application as a contact strip in an electric railway. The structural, physical, and electrical properties of the fabricated WC films with various DC bias voltages were investigated. The films had a uniform and smooth surface. Hardness and frication characteristics of the films were improved, and the resistivity and sheet resistance decreased with increasing negative DC bias voltage. These results are associated with the nanocrystalline WC phase and sp(2) clusters in carbon networks increased by ion bombardment enhanced with increasing DC bias voltage. Consequently, the increase of sp(2) clusters containing WC nanocrystalline in the carbon films is attributed to the improvement in the physical and electrical properties.

  4. RBS and NRA of cobalt oxide thin films prepared by the sol-gel process

    International Nuclear Information System (INIS)

    Andrade, E.; Huerta, L.; Pineda, J.C.; Zavala, E.P.; Barrera, E.; Rocha, M. F.; Vargas, C.A.

    2001-01-01

    This work presents a study of cobalt oxide thin films produced by the sol-gel process on aluminum and glass substrates. These films have been analyzed using two ion beam analysis (IBA) techniques: a) a standard RBS 4 He 2 MeV and b) nuclear reaction analysis (NRA) using a 1 MeV deuterium beam. The 12 C(d,p 0 ) 13 C nuclear reaction provides information that carbon is incorporated into the film structure, which could be associated to the sinterization film process. Other film measurements such as optical properties, XRD, and SEM were performed in order to complement the IBA analysis. The results show that cobalt oxide film coatings prepared by this technique have good optical properties as solar absorbers and potential uses in solar energy applications

  5. SmBa2NbO6 Nanopowders, an Effective Percolation Network Medium for YBCO Superconductors

    Directory of Open Access Journals (Sweden)

    S. Vidya

    2013-01-01

    Full Text Available The percolation behavior of superconductor-insulator composite, YBa2Cu3O7–δ, and nano SmBa2NbO2 synthesized by modified combustion technique was studied. Particle size of nano SmBa2NBO6 was determined using transmission electron microscopy. The chemical nonreactivity of nano SmBa2NbO6 with YBCO is evident from the X-Ray diffraction study which makes it a suitable nanoceramic substrate material for high temperature superconducting films. A systematic increase in the sintered density, approaching the optimum value of the insulating nanophase is clearly observed, as the vol.% of YBCO in the composite decreases. SEM micrograph showed uniform distribution of nanopowder among the large clusters of YBCO. The obtained percolation threshold is ~26 vol% of YBCO in the composite. All the composites below the threshold value showed TC(0~92 K even though the room resistivity increases with increase in vol.% of nano SmBa2NbO6. The values of critical exponents obtained matches well with the theoretically expected ones for an ideal superconductor-insulator system.

  6. Shot noise in YBCO bicrystal Josephson junctions

    DEFF Research Database (Denmark)

    Constantinian, K.Y.; Ovsyannikov, G.A.; Borisenko, I.V.

    2003-01-01

    We measured spectral noise density in YBCO symmetric bicrystal Josephson junctions on sapphire substrates at bias voltages up to 100 mV and T 4.2 K. Normal state resistance of the Josephson junctions, R-N = 20-90 Omega and ICRN up to 2.2 mV have been observed in the experimental samples. Noise...... may explain the experimentally measured linewidth broadening of Josephson oscillations at mm and submm wave frequencies in high-Tc superconducting junctions. Experimental results are discussed in terms of bound states existing at surfaces of d-wave superconducting electrodes....

  7. Optical characterisation of thin film cadmium oxide prepared by a ...

    African Journals Online (AJOL)

    The optical transmission spectra of transparent conducting cadmium oxide (CdO) thin films deposited by a modified reactive evaporation process onto glass substrates have been measured. The interference fringes were used to calculate the refractive index, thickness variation, average thickness and absorption coefficient ...

  8. Preparation of A-150 tissue-equivalent plastic films

    International Nuclear Information System (INIS)

    Saion, E.B.; Shaari, A.H.; Watt, D.E.

    1992-01-01

    A-150 tissue-equivalent (TE) plastic is widely used as a wall material for tissue-equivalent proportional counters (TEPCS) used in experimental microdosimetry. The objective of this note is to give a technical account of how A-150 TE plastic film can be fabricated in the laboratory from commercially available A-150 TE plastic. (author)

  9. Transparent nanocrystalline ZnO films prepared by spin coating

    Energy Technology Data Exchange (ETDEWEB)

    Berber, M. [SusTech GmbH and Co. KG, Petersenstr. 20, 64287 Darmstadt, Hessen (Germany)]. E-mail: mete.berber@sustech.de; Bulto, V. [SusTech GmbH and Co. KG, Petersenstr. 20, 64287 Darmstadt, Hessen (Germany); Kliss, R. [SusTech GmbH and Co. KG, Petersenstr. 20, 64287 Darmstadt, Hessen (Germany); Hahn, H. [SusTech GmbH and Co. KG, Petersenstr. 20, 64287 Darmstadt, Hessen (Germany); Forschungszentrum Karlsruhe, Institute for Nanotechnology, Postfach 3640, 76021 Karlsruhe (Germany); Joint Research Laboratory Nanomaterials, TU Darmstadt, Institute of Materials Science, Petersenstr. 23, 64287 Darmstadt (Germany)

    2005-09-15

    Dispersions of zinc oxide nanoparticles synthesized by the electrochemical deposition under oxidizing conditions process with organic surfactants, were spin coated on glass substrates. After sintering, the microstructure, surface morphology, and electro-optical properties of the transparent nanocrystalline zinc oxide films have been investigated for different coating thicknesses and organic solvents.

  10. Transparent nanocrystalline ZnO films prepared by spin coating

    International Nuclear Information System (INIS)

    Berber, M.; Bulto, V.; Kliss, R.; Hahn, H.

    2005-01-01

    Dispersions of zinc oxide nanoparticles synthesized by the electrochemical deposition under oxidizing conditions process with organic surfactants, were spin coated on glass substrates. After sintering, the microstructure, surface morphology, and electro-optical properties of the transparent nanocrystalline zinc oxide films have been investigated for different coating thicknesses and organic solvents

  11. 1D - photonic crystals prepared from the amorphous chalcogenide films

    Czech Academy of Sciences Publication Activity Database

    Kohoutek, T.; Orava, J.; Wágner, T.; Hrdlička, M.; Vlček, Milan; Frumar, M.

    2009-01-01

    Roč. 20, - (2009), S346-S350 ISSN 0957-4522. [International Conference of Optical and Optoelectronic Materials and Applications. London, 29.07.2007-03.08.2007] Institutional research plan: CEZ:AV0Z40500505 Keywords : chalcogenide thin films Subject RIV: CA - Inorganic Chemistry Impact factor: 1.020, year: 2009

  12. High index of refraction films for dielectric mirrors prepared by metal-organic chemical vapor deposition

    International Nuclear Information System (INIS)

    Brusasco, R.M.

    1989-01-01

    A wide variety of metal oxides with high index of refraction can be prepared by Metal-Organic Chemical Vapor Deposition. We present some recent optical and laser damage results on oxide films prepared by MOCVD which could be used in a multilayer structure for highly reflecting (HR) dielectric mirror applications. The method of preparation affects both optical properties and laser damage threshold. 10 refs., 8 figs., 4 tabs

  13. Preparation of pectin/silver nanoparticles composite films with UV-light barrier and properties.

    Science.gov (United States)

    Shankar, Shiv; Tanomrod, Nattareya; Rawdkuen, Saroat; Rhim, Jong-Whan

    2016-11-01

    Silver nanoparticles (AgNPs) was synthesized by a green method using an aqueous extract of Caesalpinia mimosoides Lamk (CMLE) as reducing and stabilizing agents, and they were used for the preparation of pectin-based antimicrobial composite films. The AgNPs were spherical in shape with the size in the range of 20-80nm and showed the absorption peak around 500nm. The pectin/AgNPs composite film exhibited characteristic absorption peak of AgNPs at 480nm. The surface color and light transmittance of the pectin films were greatly influenced by the addition of AgNPs. The lightness of the films decreased, however, redness and yellowness of the films increased after incorporation of AgNPs. UV-light barrier property of the pectin film increased significantly with a little decrease in the transparency. Though there were no structural changes in the pectin film by the incorporation of CMLE and AgNPs as indicated by the FTIR results, the film properties such as thermal stability, mechanical strength, and water vapor barrier properties of the pectin films increased. The pectin/AgNPs nanocomposite films exhibited strong antibacterial activity against food-borne pathogenic bacteria, Escherichia coli and Listeria monocytogenes. Copyright © 2016 Elsevier B.V. All rights reserved.

  14. Preparation and characterization of collagen/hydroxypropyl methylcellulose (HPMC) blend film.

    Science.gov (United States)

    Ding, Cuicui; Zhang, Min; Li, Guoying

    2015-03-30

    This study aimed to prepare and characterize the collagen/HPMC blend film (1/1). Thermogravimetric analysis and differential scanning calorimetry were used to investigate the thermal properties of the film. Both thermal decomposition temperature and denaturation temperature of the blend film were higher than those of the collagen film due to the intermolecular hydrogen bonding interaction between collagen and HPMC, which was demonstrated by Fourier transform infrared spectroscopy. Additionally, the morphologies, mechanical properties and hydrophilicity of films were examined. The blend film exhibited a more homogeneous and compact structure compared with that of the collagen film, as observed from scanning electron microscopy and atomic force microscopy. The tensile strength, ultimate elongation and hydrophilicity of the blend film were superior to those of the pure collagen film. Furthermore, the introduction of polyethylene glycol 1500 had almost no influence on the thermal properties of the blend film but obviously improved its stretch-ability and smoothness. Copyright © 2014 Elsevier Ltd. All rights reserved.

  15. Study on the Preparation and Properties of Colored Iron Oxide Thin Films

    International Nuclear Information System (INIS)

    Zhao Xianhui; Li Changhong; Liu Qiuping; He Junjing; Wang Hai; Liang Song; Duan Yandong; Liu Su

    2013-01-01

    Colored iron oxide thin films were prepared using Sol-gel technique. The raw materials were tetraethyl orthosilicate (TEOS), etoh ehanol (EtOH), iron nitrate, and de-ionized water. Various properties were measured and analysed, including the colour of thin films, surface topography, UV-Visible spectra, corrosion resistance and hydrophobicity. To understand how these properties influenced the structural and optical properties of Fe 2 O 3 thin films, Scanning Electron Microscope (SEM), UV Spectrophotometer and other facilities were employed. Many parameters influence the performance of thin films, such as film layers, added H 2 O content, and the amount of polydimethylsiloxane (PDMS). When the volume ratio of TEOS, EtOH and H 2 O was 15: 13: 1, the quality of Fe(NO 3 ) 3 ·9H 2 O was 6g, and pH value was 3, reddish and uniform Fe 2 O 3 thin films with excellent properties were produced. Obtained thin films possessed corrosion resistance in hydrochloric acid with pH=l and the absorption edge wavelength was ∼350.2nm. Different H 2 O contents could result in different morphologies of Fe 2 O 3 nanoparticles. When 1.5 ml PDMS was added into the Sol, thin films possessed hydrophobiliry without dropping. Coating with different layers, thin films appeared different morphologies. Meanwhile, with the increment of film layers, the absorbance increased gradually.

  16. Preparation and Characterization of an Olive Flounder (Paralichthys olivaceus) Skin Gelatin and Polylactic Acid Bilayer Film.

    Science.gov (United States)

    Lee, Ka-Yeon; Song, Kyung Bin

    2017-03-01

    Olive flounder skin gelatin (OSG) was used as a film base material. A bilayer film of OSG and polylactic acid (PLA) was prepared using solvent casting method to enhance the film properties. Physical properties of the OSG-PLA film were increased compared with the nonaugmented OSG film. In particular, the PLA lamination decreased water vapor permeability from 2.17 to 0.92 × 10 -9 g·m/m 2 ·s·Pa, as well as of the water solubility from 16.62% to 9.27%, in the bilayer film relative to the OSG film. The oxygen permeability of the OSG-PLA bilayer film was held low by the OSG film, compensating for the high oxygen permeability of the PLA layer. Therefore, the OSG-PLA bilayer film with its enhanced physical properties and high water and oxygen barrier properties can be applied as a food packaging material. © 2017 Institute of Food Technologists®.

  17. Preparation and electrochemical properties of gold nanoparticles containing carbon nanotubes-polyelectrolyte multilayer thin films

    International Nuclear Information System (INIS)

    Yu Aimin; Zhang Xing; Zhang Haili; Han, Deyan; Knight, Allan R.

    2011-01-01

    Highlights: → Gold nanoparticles containing carbon nanotubes-polyelectrolyte multilayer thin films were prepared via layer-by-layer self-assembly technique. → The electron transfer behaviour of the hybrid thin films were investigated using an electrochemical probe. → The resulting thin films exhibited an electrocatalytic activity towards the oxidation of nitric oxide. - Abstract: Multi-walled carbon nanotubes (MWCNT)/polyelectrolyte (PE) hybrid thin films were fabricated by alternatively depositing negatively charged MWCNT and positively charged (diallyldimethylammonium chloride) (PDDA) via layer-by-layer (LbL) assembly technique. The stepwise growth of the multilayer films of MWCNT and PDDA was characterized by UV-vis spectroscopy. Scanning electron microscopy (SEM) images indicated that the MWCNT were uniformly embedded in the film to form a network and the coverage density of MWCNT increased with layer number. Au nanoparticles (NPs) could be further adsorbed onto the film to form PE/MWCNT/Au NPs composite films. The electron transfer behaviour of multilayer films with different compositions were studied by cyclic voltammetry using [Fe(CN) 6 ] 3-/4- as an electrochemical probe. The results indicated that the incorporation of MWCNT and Au NPs not only greatly improved the electronic conductivity of pure polyelectrolyte films, but also provided excellent electrocatalytic activity towards the oxidation of nitric oxide (NO).

  18. Preparation and characterization of nanocrystalline porous TiO2/WO3 composite thin films

    International Nuclear Information System (INIS)

    Hsu, C.-S.; Lin, C.-K.; Chan, C.-C.; Chang, C.-C.; Tsay, C.-Y.

    2006-01-01

    TiO 2 materials possessing not only photocatalytic but also electrochromic properties have attracted many research and development interests. Though WO 3 exhibits excellent electrochromic properties, the much higher cost and water-sensitivity of WO 3 as compared with the TiO 2 may restrict the practical application of WO 3 materials. In the present study, the feasibility of preparing nanocrystalline porous TiO 2 /WO 3 composite thin films was investigated. Precursors of sols TiO 2 and/or WO 3 and polystyrene microspheres were used to prepare nanocrystalline pure TiO 2 , WO 3 , and composite TiO 2 /WO 3 thin films by spin coating. The spin-coated thin films were amorphous and, after heat treating at a temperature of 500 o C, nanocrystalline TiO 2 , TiO 2 /WO 3 , and WO 3 thin films with or without pores were prepared successfully. The heat-treated thin films were colorless and coloration-bleaching phenomena can be observed during cyclic voltammetry tests. The heat-treated thin films exhibited good reversible electrochromic behavior while the porous TiO 2 /WO 3 composite film exhibited improved electrochromic properties

  19. Excimer laser processing of ZnO thin films prepared by the sol-gel process

    International Nuclear Information System (INIS)

    Winfield, R.J.; Koh, L.H.K.; O'Brien, Shane; Crean, Gabriel M.

    2007-01-01

    ZnO thin films were prepared on soda-lime glass from a single spin-coating deposition of a sol-gel prepared with anhydrous zinc acetate [Zn(C 2 H 3 O 2 ) 2 ], monoethanolamine [H 2 NC 2 H 4 OH] and isopropanol. The deposited films were dried at 50 and 300 deg. C. X-ray analysis showed that the films were amorphous. Laser annealing was performed using an excimer laser. The laser pulse repetition rate was 25 Hz with a pulse energy of 5.9 mJ, giving a fluence of 225 mJ cm -2 on the ZnO film. Typically, five laser pulses per unit area of the film were used. After laser processing, the hexagonal wurtzite phase of zinc oxide was observed from X-ray diffraction pattern analysis. The thin films had a transparency of greater than 70% in the visible region. The optical band-gap energy was 3.454 eV. Scanning electron microscopy and profilometry analysis highlighted the change in morphology that occurred as a result of laser processing. This comparative study shows that our sol-gel processing route differs significantly from ZnO sol-gel films prepared by conventional furnace annealing which requires temperatures above 450 deg. C for the formation of crystalline ZnO

  20. Polarized Raman study on the lattice structure of BiFeO3 films prepared by pulsed laser deposition

    KAUST Repository

    Yang, Yang; Yao, Yingbang; Zhang, Q.; Zhang, Xixiang

    2014-01-01

    Polarized Raman spectroscopy was used to study the lattice structure of BiFeO3 films on different substrates prepared by pulsed laser deposition. Interestingly, the Raman spectra of BiFeO3 films exhibit distinct polarization dependences

  1. Thickness dependent electrical properties of CdO thin films prepared by spray pyrolysis method

    International Nuclear Information System (INIS)

    Murthy, L.C.S.; Rao, K.S.R.K.

    1999-01-01

    A large number of thin films of cadmium oxide have been prepared on glass substrates by spray pyrolysis method. The prepared films have uniform thickness varying from 200-600 nm and good adherence to the glass substrate. A systematic study has been made on the influence of thickness on resistivity, sheet resistance, carrier concentration and mobility of the films. The resistivity, sheet resistance, carrier concentration and mobility values varied from 1.56-5.72x10 -3 Ω-cm, 128-189 Ω/□, 1.6-3.9x10 21 cm -3 and 0.3-3 cm 2 /Vs, respectively for varying film thickness. A systematic increase in mobility with grain size clearly indicates the reduction of overall scattering of charge carriers at the grain boundaries. The large concentration of charge carriers and low mobility values have been attributed to the presence of Cd as an impurity in CdO microcrystallites. Using the optical transmission data, the band gap was estimated and found to vary from 2.20-2.42 eV. These films have transmittance around 77% and average reflectance is below 2.6% in the spectral range 350-850 nm. The films are n-type and polycrystalline in nature. SEM micrographs of the CdO films were taken and the films exhibit clear grains and grain boundary formation at a substrate temperature as low as 523 K. (author)

  2. Preparation and Characterization of Silver Liquid Thin Films for Magnetic Fluid Deformable Mirror

    Directory of Open Access Journals (Sweden)

    Lianchao Zhang

    2015-01-01

    Full Text Available Silver liquid thin film, formed by silver nanoparticles stacking and spreading on the surface of the liquid, is one of the important parts of magnetic fluid deformable mirror. First, silver nanoparticles were prepared by liquid phase chemical reduction method using sodium citrate as reducing agent and stabilizer and silver nitrate as precursor. Characterization of silver nanoparticles was studied using X-ray diffractometer, UV-vis spectrophotometer, and transmission electron microscope (TEM. The results showed that silver nanoparticles are spherical and have a good monodispersity. Additionally, the effect of the reaction conditions on the particle size of silver is obvious. And then silver liquid thin films were prepared by oil-water two-phase interface technology using as-synthesized silver nanoparticles. Properties of the film were investigated using different technology. The results showed that the film has good reflectivity and the particle size has a great influence on the reflectivity of the films. SEM photos showed that the liquid film is composed of multilayer silver nanoparticles. In addition, stability of the film was studied. The results showed that after being stored for 8 days under natural conditions, the gloss and reflectivity of the film start to decrease.

  3. PLD prepared nanostructured Pt-CeO{sub 2} thin films containing ionic platinum

    Energy Technology Data Exchange (ETDEWEB)

    Vorokhta, M., E-mail: vorohtam@gmail.com [Charles University in Prague, Faculty of Mathematics and Physics, Department of Surface and Plasma Science, V Holešovičkách 2, 18000 Prague 8 (Czech Republic); Khalakhan, I.; Matolínová, I.; Nováková, J.; Haviar, S. [Charles University in Prague, Faculty of Mathematics and Physics, Department of Surface and Plasma Science, V Holešovičkách 2, 18000 Prague 8 (Czech Republic); Lančok, J.; Novotný, M. [Institute of Physics, Academy of Sciences of the Czech Republic, Na Slovance 2, 182 21 Prague, Czhech Republic (Czech Republic); Yoshikawa, H. [National Institute for Materials Science, Sengen 1-2-1, Tsukuba, Ibaraki 305-0047 (Japan); Matolín, V. [Charles University in Prague, Faculty of Mathematics and Physics, Department of Surface and Plasma Science, V Holešovičkách 2, 18000 Prague 8 (Czech Republic)

    2017-02-28

    Highlights: • Nanostructured Pt-CeO{sub 2} thin catalyst films were grown on plasma etched and non-etched carbon substrates by pulsed laser deposition. • The surface composition of the nanostructured Pt-CeO{sub 2} films was investigated by surface analysis techniques. • The effect of film roughening was separated from the effect of platinum-ceria atomic interactions. - Abstract: The composition of nanostructured Pt-CeO{sub 2} films on graphite substrates prepared by pulsed laser deposition has been investigated by means of hard X-ray photoelectron spectroscopy, scanning electron microscopy, high resolution transmission electron microscopy, and atomic force microscopy. The influence of morphology of the graphite substrates was investigated with respect to the relative concentrations of ionic and metallic Pt species in the films. It was found that the degree of Pt{sup 2+} enrichment is directly related to the surface morphology of graphite substrates. In particular, the deposition of Pt-CeO{sub 2} films on rough graphite substrate etched in oxygen plasma yielded nanostructured Pt-CeO{sub 2} catalyst films with high surface area and high Pt{sup 2+}/Pt{sup 0} ratio. The presented results demonstrate that PLD is a suitable method for the preparation of thin Pt-CeO{sub 2} catalyst films for fuel cell applications.

  4. Oromucosal film preparations: points to consider for patient centricity and manufacturing processes.

    Science.gov (United States)

    Krampe, Raphael; Visser, J Carolina; Frijlink, Henderik W; Breitkreutz, Jörg; Woerdenbag, Herman J; Preis, Maren

    2016-01-01

    According to the European Pharmacopoeia, oromucosal films comprise mucoadhesive buccal films and orodispersible films. Both oral dosage forms receive considerable interest in the recent years as commercially available pharmaceutical products and as small scale personalized extemporaneous preparations. In this review, technological issues such as viscosity of the casting liquid, mechanical properties of the film, upscaling and the stability of the casting solution and produced films will be discussed. Furthermore, patient-related problems like appearance, mucosal irritation, taste, drug load, safety and biopharmaceutics are described. Current knowledge and directions for solutions are summarized. The viscosity of the casting solution is a key factor for producing suitable films. This parameter is amongst others dependent on the polymer and active pharmaceutical ingredient, and the further excipients that are used. For optimal patient compliance, an acceptable taste and palatability are desirable. Safe and inert excipients should be used and appropriate packaging should be provided to produced films. Absorption through the oral mucosa will vary for each active compound, formulation and patient, which gives rise to pharmacokinetic questions. Finally, the European Pharmacopoeia needs to specify methods, requirement and definitions for oromucosal film preparations based on bio-relevant data.

  5. Properties and characterization of bionanocomposite films prepared with various biopolymers and ZnO nanoparticles.

    Science.gov (United States)

    Kanmani, Paulraj; Rhim, Jong-Whan

    2014-06-15

    This study was aimed to develop biopolymer based antimicrobial films for active food packaging and to reduce environmental pollution caused by accumulation of synthetic packaging. The ZnO NPs were incorporated as antimicrobials into different biopolymers such as agar, carrageenan and CMC. Solvent casting method was performed to prepare active nanocomposite films. Methods such as FE-SEM, FT-IR and XRD were used to characterize resulting films. Physical, mechanical, thermal and antimicrobial properties were also examined. Remarkable surface morphological differences were observed between control and nanocomposite films. The crystallinity of ZnO was confirmed by XRD analysis. The addition of ZnO NPs increased color, UV barrier, moisture content, hydrophobicity, elongation and thermal stability of the films, while decreased WVP, tensile strength and elastic modulus. ZnO NPs impregnated films inhibited growth of L. monocytogenes and E. coli. So these newly prepared nanocomposite films can be used as active packaging film to extend shelf-life of food. Copyright © 2014 Elsevier Ltd. All rights reserved.

  6. Synthesis and characterization of hard ternary AlMgB composite films prepared by sputter deposition

    Energy Technology Data Exchange (ETDEWEB)

    Yan Ce [Department of Physics and Materials Science and Center of Super-Diamond and Advanced Films, City University of Hong Kong (Hong Kong); Zhou, Z.F. [Department of Manufacturing Engineering and Engineering Management and Advanced Coatings Applied Research Laboratory, City University of Hong Kong (Hong Kong); Chong, Y.M.; Liu, C.P.; Liu, Z.T. [Department of Physics and Materials Science and Center of Super-Diamond and Advanced Films, City University of Hong Kong (Hong Kong); Li, K.Y., E-mail: mekyli@cityu.edu.h [Department of Manufacturing Engineering and Engineering Management and Advanced Coatings Applied Research Laboratory, City University of Hong Kong (Hong Kong); Bello, I., E-mail: apibello@cityu.edu.h [Department of Physics and Materials Science and Center of Super-Diamond and Advanced Films, City University of Hong Kong (Hong Kong); Kutsay, O.; Zapien, J.A.; Zhang, W.J. [Department of Physics and Materials Science and Center of Super-Diamond and Advanced Films, City University of Hong Kong (Hong Kong)

    2010-07-30

    Hard and superlight thin films laminated with boron carbide have been proposed as candidates for strategic use such as armor materials in military and space applications. Aluminum magnesium boride (AlMgB) films are excellent candidates for these purposes. We prepared AlMgB films by sputter deposition using multiple unbalanced planar magnetrons equipped with two boron and one AlMg targets. The film morphology changed and the film's root mean square (rms) roughness varied from 1.0 to 18 nm as the power density of the AlMg target increased from 0.2 to 1.0 W/cm{sup 2} while the power density of each boron target was maintained at 2 W/cm{sup 2}. Chemical analyses show dominating Al, Mg, B and trace elements of oxygen, carbon and argon. The film composition also varies with altering the power density supplied to the AlMg target. The film with an atomic ratio of Al:Mg:B = 1.38:0.64:1 exhibits the highest hardness ({approx} 30 GPa). This value surpasses the hardness of hydrogenated diamond-like carbon films (24-28 GPa) prepared by plasma enhanced chemical vapor deposition.

  7. Synthesis and characterization of hard ternary AlMgB composite films prepared by sputter deposition

    International Nuclear Information System (INIS)

    Yan Ce; Zhou, Z.F.; Chong, Y.M.; Liu, C.P.; Liu, Z.T.; Li, K.Y.; Bello, I.; Kutsay, O.; Zapien, J.A.; Zhang, W.J.

    2010-01-01

    Hard and superlight thin films laminated with boron carbide have been proposed as candidates for strategic use such as armor materials in military and space applications. Aluminum magnesium boride (AlMgB) films are excellent candidates for these purposes. We prepared AlMgB films by sputter deposition using multiple unbalanced planar magnetrons equipped with two boron and one AlMg targets. The film morphology changed and the film's root mean square (rms) roughness varied from 1.0 to 18 nm as the power density of the AlMg target increased from 0.2 to 1.0 W/cm 2 while the power density of each boron target was maintained at 2 W/cm 2 . Chemical analyses show dominating Al, Mg, B and trace elements of oxygen, carbon and argon. The film composition also varies with altering the power density supplied to the AlMg target. The film with an atomic ratio of Al:Mg:B = 1.38:0.64:1 exhibits the highest hardness (∼ 30 GPa). This value surpasses the hardness of hydrogenated diamond-like carbon films (24-28 GPa) prepared by plasma enhanced chemical vapor deposition.

  8. Preparing hydrophobic nanocellulose-silica film by a facile one-pot method.

    Science.gov (United States)

    Le, Duy; Kongparakul, Suwadee; Samart, Chanatip; Phanthong, Patchiya; Karnjanakom, Surachai; Abudula, Abuliti; Guan, Guoqing

    2016-11-20

    Hydrophobic nanocellulose-silica film was successfully prepared by a facile one-pot method using tetraethoxysilane (TEOS) and dodecyl triethoxylsilane (DTES). Morphological characterization of the hydrophobic nanocellulose-silica (NC-SiO2-DTES) film showed well self-assembled DTES modified silica spherical nanoparticles with the particle sizes in the range of 88-126nm over the nanocellulose film. The hydrophobicity of the NC-SiO2-DTES film was achieved owing to the improvement of roughness of the nanocellulose film by coating dodecyl- terminated silica nanoparticles. An increase in DTES loading amount and reaction time increased the hydrophobicity of the film, and the optimum condition for NC-SiO2-DTES film preparation was achieved at DTES/TEOS molar ratio of 2.0 for 8h reaction time. Besides, the NC-SiO2-DTES film performed superoleophilic property with octane and hexadecane contact angles of 0°. It also showed an excellent hydrophobic property over all pH values ranged from 1 to 14. Copyright © 2016 Elsevier Ltd. All rights reserved.

  9. Oriented Y-typehexagonal ferrite thin films prepared by chemical

    Czech Academy of Sciences Publication Activity Database

    Buršík, Josef; Kužel, R.; Knížek, Karel; Drbohlav, Ivo

    2013-01-01

    Roč. 203, JULY (2013), s. 100-105 ISSN 0022-4596 R&D Projects: GA ČR GA13-03708S Institutional support: RVO:61388980 ; RVO:68378271 Keywords : Y-type hexagonal ferrites * chemical solution deposition * thin films * epitaxial growth Subject RIV: CA - Inorganic Chemistry; BM - Solid Matter Physics ; Magnetism (FZU-D) Impact factor: 2.200, year: 2013

  10. Maximum permissible voltage of YBCO coated conductors

    Energy Technology Data Exchange (ETDEWEB)

    Wen, J.; Lin, B.; Sheng, J.; Xu, J.; Jin, Z. [Department of Electrical Engineering, Shanghai Jiao Tong University, Shanghai (China); Hong, Z., E-mail: zhiyong.hong@sjtu.edu.cn [Department of Electrical Engineering, Shanghai Jiao Tong University, Shanghai (China); Wang, D.; Zhou, H.; Shen, X.; Shen, C. [Qingpu Power Supply Company, State Grid Shanghai Municipal Electric Power Company, Shanghai (China)

    2014-06-15

    Highlights: • We examine three kinds of tapes’ maximum permissible voltage. • We examine the relationship between quenching duration and maximum permissible voltage. • Continuous I{sub c} degradations under repetitive quenching where tapes reaching maximum permissible voltage. • The relationship between maximum permissible voltage and resistance, temperature. - Abstract: Superconducting fault current limiter (SFCL) could reduce short circuit currents in electrical power system. One of the most important thing in developing SFCL is to find out the maximum permissible voltage of each limiting element. The maximum permissible voltage is defined as the maximum voltage per unit length at which the YBCO coated conductors (CC) do not suffer from critical current (I{sub c}) degradation or burnout. In this research, the time of quenching process is changed and voltage is raised until the I{sub c} degradation or burnout happens. YBCO coated conductors test in the experiment are from American superconductor (AMSC) and Shanghai Jiao Tong University (SJTU). Along with the quenching duration increasing, the maximum permissible voltage of CC decreases. When quenching duration is 100 ms, the maximum permissible of SJTU CC, 12 mm AMSC CC and 4 mm AMSC CC are 0.72 V/cm, 0.52 V/cm and 1.2 V/cm respectively. Based on the results of samples, the whole length of CCs used in the design of a SFCL can be determined.

  11. Growth techniques for monolithic YBCO solenoidal magnets

    International Nuclear Information System (INIS)

    Scruggs, S.J.; Putman, P.T.; Fang, H.; Alessandrini, M.; Salama, K.

    2006-01-01

    The possibility of growing large single domain YBCO solenoids by the use of a large seed has been investigated. There are two known methods for producing a similar solenoid. This first is a conventional top seeded melt growth process followed by a post processing machining step to create the bore. The second involves using multiple seeds spaced around the magnet bore. The appeal of the new technique lies in decreasing processing time compared to the single seed technique, while avoiding alignment problems found in the multiple seeding technique. By avoiding these problems, larger diameter monoliths can be produced. Large diameter monoliths are beneficial because the maximum magnetic field produced by a trapped field magnet is proportional to the radius of the sample. Furthermore, the availability of trapped field magnets with large diameter could enable their use in applications that traditionally have been considered to require wound electromagnets, such as beam bending magnets for particle accelerators or electric propulsion. A comparison of YBCO solenoids grown by the use of a large seed and grown by the use of two small seeds simulating multiple seeding is made. Trapped field measurements as well as microstructure evaluation were used in characterization of each solenoid. Results indicate that high quality growth occurs only in the vicinity of the seeds for the multiple seeded sample, while the sample with the large seeded exhibited high quality growth throughout the entire sample

  12. Growth techniques for monolithic YBCO solenoidal magnets

    Energy Technology Data Exchange (ETDEWEB)

    Scruggs, S.J. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States)]. E-mail: Sscruggs2@uh.edu; Putman, P.T. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States); Fang, H. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States); Alessandrini, M. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States); Salama, K. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States)

    2006-10-01

    The possibility of growing large single domain YBCO solenoids by the use of a large seed has been investigated. There are two known methods for producing a similar solenoid. This first is a conventional top seeded melt growth process followed by a post processing machining step to create the bore. The second involves using multiple seeds spaced around the magnet bore. The appeal of the new technique lies in decreasing processing time compared to the single seed technique, while avoiding alignment problems found in the multiple seeding technique. By avoiding these problems, larger diameter monoliths can be produced. Large diameter monoliths are beneficial because the maximum magnetic field produced by a trapped field magnet is proportional to the radius of the sample. Furthermore, the availability of trapped field magnets with large diameter could enable their use in applications that traditionally have been considered to require wound electromagnets, such as beam bending magnets for particle accelerators or electric propulsion. A comparison of YBCO solenoids grown by the use of a large seed and grown by the use of two small seeds simulating multiple seeding is made. Trapped field measurements as well as microstructure evaluation were used in characterization of each solenoid. Results indicate that high quality growth occurs only in the vicinity of the seeds for the multiple seeded sample, while the sample with the large seeded exhibited high quality growth throughout the entire sample.

  13. Photocatalysis of zinc oxide nanotip array/titanium oxide film heterojunction prepared by aqueous solution deposition

    Science.gov (United States)

    Lee, Ming-Kwei; Lee, Bo-Wei; Kao, Chen-Yu

    2017-05-01

    A TiO2 film was prepared on indium tin oxide (ITO)/glass by aqueous solution deposition (ASD) with precursors of ammonium hexafluoro-titanate and boric acid at 40 °C. The photocatalysis of annealed TiO2 film increases with increasing growth time and decreases with increasing growth times longer than 60 min. A ZnO nanotip array was prepared on ZnO seed layer/TiO2 film/glass by aqueous solution deposition with precursors of zinc nitrate and ammonium hydroxide at 70 °C. The photocatalysis of ASD-ZnO/ASD-TiO2 film/ITO glass can be better than that of P25.

  14. Characteristics of zinc oxide nanorod array/titanium oxide film heterojunction prepared by aqueous solution deposition

    Science.gov (United States)

    Lee, Ming-Kwei; Hong, Min-Hsuan; Li, Bo-Wei

    2016-07-01

    The characteristics of a ZnO nanorod array/TiO2 film heterojunction were investigated. A TiO2 film was prepared on glass by aqueous solution deposition with precursors of ammonium hexafluorotitanate and boric acid at 40 °C. Then, a ZnO seed layer was prepared on a TiO2 film/glass substrate by RF sputtering. A vertically oriented ZnO nanorod array was grown on a ZnO seed layer/TiO2 film/glass substrate by aqueous solution deposition with precursors of zinc nitrate and hexamethylenetetramine (HMT) at 70 °C. After thermal annealing in N2O ambient at 300 °C, this heterojunction used as an oxygen gas sensor shows much better rise time, decay time, and on/off current ratio than as-grown and annealed ZnO nanorods.

  15. Preparation of porous titanium oxide films onto indium tin oxide for application in organic photovoltaic devices

    Energy Technology Data Exchange (ETDEWEB)

    Macedo, Andreia G. [Laboratorio de Dispositivos Nanoestruturados, Departamento de Fisica, Universidade Federal do Parana, Curitiba, Parana (Brazil); Mattos, Luana L.; Spada, Edna R.; Serpa, Rafael B.; Campos, Cristiani S. [Laboratorio de Sistemas Nanoestruturados, Departamento de Fisica, Universidade Federal de Santa Catarina, Florianopolis, Santa Catarina (Brazil); Grova, Isabel R.; Ackcelrud, Leni [Laboratorio de Polimeros Paulo Scarpa, Departamento de Quimica, Universidade Federal do Parana, Curitiba, Parana (Brazil); Reis, Francoise T.; Sartorelli, Maria L. [Laboratorio de Sistemas Nanoestruturados, Departamento de Fisica, Universidade Federal de Santa Catarina, Florianopolis, Santa Catarina (Brazil); Roman, Lucimara S., E-mail: lsroman@fisica.ufpr.br [Laboratorio de Dispositivos Nanoestruturados, Departamento de Fisica, Universidade Federal do Parana, Curitiba, Parana (Brazil)

    2012-05-01

    In this work, porous ordered TiO{sub 2} films were prepared through sol gel route by using a monolayer of polystyrene spheres as template on indium-tin oxide/glass substrate. These films were characterized by SEM, AFM, Raman spectroscopy, UV-vis absorbance and XRD. The UV-vis absorbance spectrum show a pseudo band gap (PBG) with maxima at 460 nm arising from the light scattering and partial or total suppression of the photon density of states, this PBG can be controlled by the size of the pore. We also propose the use of this porous film as electron acceptor electrode in organic photovoltaic cells; we show that devices prepared with porous titania displayed higher efficiencies than devices using compact titania films as electrode. Such behaviour was observed in both bilayer and bulk heterojunction devices.

  16. Preparation of porous titanium oxide films onto indium tin oxide for application in organic photovoltaic devices

    International Nuclear Information System (INIS)

    Macedo, Andreia G.; Mattos, Luana L.; Spada, Edna R.; Serpa, Rafael B.; Campos, Cristiani S.; Grova, Isabel R.; Ackcelrud, Leni; Reis, Françoise T.; Sartorelli, Maria L.; Roman, Lucimara S.

    2012-01-01

    In this work, porous ordered TiO 2 films were prepared through sol gel route by using a monolayer of polystyrene spheres as template on indium-tin oxide/glass substrate. These films were characterized by SEM, AFM, Raman spectroscopy, UV-vis absorbance and XRD. The UV-vis absorbance spectrum show a pseudo band gap (PBG) with maxima at 460 nm arising from the light scattering and partial or total suppression of the photon density of states, this PBG can be controlled by the size of the pore. We also propose the use of this porous film as electron acceptor electrode in organic photovoltaic cells; we show that devices prepared with porous titania displayed higher efficiencies than devices using compact titania films as electrode. Such behaviour was observed in both bilayer and bulk heterojunction devices.

  17. Review of WO3 thin film preparation for photoelectrochemical water splitting

    International Nuclear Information System (INIS)

    Ehsan Eftekhari; Mohammad Kassim

    2009-01-01

    Full text: Tungsten trioxide (WO 3 ), which is one of the most essential materials in our daily life has appeared as an excellent photo electrode material for environmental purification. The nano-size of WO 3 thin film water-splitting technology has great potential for environmentally friendly solar-hydrogen production for the future hydrogen economy. There are several methods for producing tungsten oxide film. In this review, we outlined several WO 3 thin film preparation methods such as doctor Bladding, sputtering, layer-by-layer brush painting, spray pyrolysis deposition, sol-gel and other methods. Here we compare the maximum photocurrent obtained, different condition for preparation of WO 3 thin film and characterization outcome. (author)

  18. Properties of Zn O/Cr thin films prepared by Sol-Gel

    International Nuclear Information System (INIS)

    Tirado G, S.; Olvera A, R.

    2014-08-01

    Zn O films and those superficially modified with chromium were deposited on substrates of soda-lime glass, using the Sol-Gel process and the repeated immersion method. Starting from dehydrated zinc acetate was prepared a solution to 0.6 M to ambient temperature in 2-methoxyethanol and monoethanolamine (Mea) stirring magnetically. The Sol was prepared with an aging to seven days and was used to grow a films group with thickness to eight immersions. These same films were superficially modified with several depositions of a chromium nitrate Sol dissolved in ethanol to low concentration. The Zn O films were structurally characterized by X-ray diffraction, its chemical composition by energy dispersive X-ray spectroscopy and its morphology by scanning electron microscopy and atomic force microscopy, as well as their optical properties by UV-vis. Of the obtained results are proposed possible applications. (author)

  19. Preparation of Pb(Zr, Ti)O3 Thin Films on Glass Substrates

    Science.gov (United States)

    Hioki, Tsuyoshi; Akiyama, Masahiko; Ueda, Tomomasa; Onozuka, Yutaka; Hara, Yujiro; Suzuki, Kouji

    2000-09-01

    Lead-zirconate-titanate (PZT) thin films were prepared on non-alkaline glass substrates widely used in liquid crystal display (LCD) devices, by plasma-assisted magnetron RF sputtering with an immersed coil. After preparation of the PZT thin film, the glass was available for use in LCD device processing. No mutual diffusion of the elements was recognized between the glass substrate and the bottom electrode. The PZT layer had a dense film structure with rectangular and columnar grains, and only its perovskite phase was crystalline. PZT thin films on a glass substrate had leakage current densities of about 10-8 A/cm2, acceptable hysteresis loop shapes with the remanent polarization (Pr) of 45 μC/cm2 and the coercive field (Ec) of 90 kV/cm. Ferroelectric properties on a glass substrate almost conform with those on a Si-based substrate.

  20. Preparation and Hydrogen Absorption/Desorption of Nanoporous Palladium Thin Films

    Directory of Open Access Journals (Sweden)

    Wen-Chung Li

    2009-12-01

    Full Text Available Nanoporous Pd (np-Pd was prepared by co-sputtering Pd-Ni alloy films onto Si substrates, followed by chemical dealloying with sulfuric acid. X-ray diffractometry and chemical analysis were used to track the extent of dealloying. The np-Pd structure was changed from particle-like to sponge-like by diluting the sulfuric acid etchant. Using suitable precursor alloy composition and dealloying conditions, np-Pd films were prepared with uniform and open sponge-like structures, with interconnected ligaments and no cracks, yielding a large amount of surface area for reactions with hydrogen. Np-Pd films exhibited shorter response time for hydrogen absorption/desorption than dense Pd films, showing promise for hydrogen sensing.

  1. Oxygen reduction activity of N-doped carbon-based films prepared by pulsed laser deposition

    Science.gov (United States)

    Hakoda, Teruyuki; Yamamoto, Shunya; Kawaguchi, Kazuhiro; Yamaki, Tetsuya; Kobayashi, Tomohiro; Yoshikawa, Masahito

    2010-12-01

    Carbon-based films with nitrogen species on their surface were prepared on a glassy carbon (GC) substrate for application as a non-platinum cathode catalyst for polymer electrolyte fuel cells. Cobalt and carbon were deposited in the presence of N 2 gas using a pulsed laser deposition method and then the metal Co was removed by HCl-washing treatment. Oxygen reduction reaction (ORR) activity was electrochemically determined using a rotating disk electrode system in which the film samples on the GC substrate were replaceable. The ORR activity increased with the temperature of the GC substrate during deposition. A carbon-based film prepared at 600 °C in the presence of N 2 at 66.7 Pa showed the highest ORR activity among the tested samples (0.66 V vs. NHE). This film was composed of amorphous carbons doped with pyridine type nitrogen atoms on its surface.

  2. Preparation and Biodegradation of Nanocellulose Reinforced Polyvinyl Alcohol Blend Films in Bioenvironmental Media

    OpenAIRE

    Nusaiba Islam; Sharmin Jahan Proma; Ashiqur Rahman; Ashok Kumar Chakraborty

    2017-01-01

    Solution casting method was used to prepare nanocellulose reinforced polyvinyl alcohol (PVOH) from Oil palm empty fruit bunches. Different environmental test were used to investigate the biodegradability of the composite in soil and compost as well as in water and acidic solution. The morphology of the composite was investigated by scanning electron microscopy. The composite film with nanocellulose and without nanocellulose were compared, nanocellulose modified PVOH film showed more highly de...

  3. Preparation and Characterization of HPMC/PVP Blend Films Plasticized with Sorbitol

    OpenAIRE

    Somashekarappa, H.; Prakash, Y.; Hemalatha, K.; Demappa, T.; Somashekar, R.

    2013-01-01

    The aim of this present work is to investigate the effect of plasticizers like Sorbitol on microstructural and mechanical properties of hydroxypropyl methylcellulose (HPMC) and Polyvinylpyrrolidone (PVP) blend films. The pure blend and plasticized blend films were prepared by solution casting method and investigated using wide angle X-ray scattering (WAXS) method. WAXS analysis confirms that the plasticizers can enter into macromolecular blend structure and destroy the crystallinity of the f...

  4. Damp heat stability and annealing behavior of aluminum doped zinc oxide films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Tohsophon, T.; Huepkes, J.; Calnan, S.; Reetz, W.; Rech, B.; Beyer, W.; Sirikulrat, N.

    2006-01-01

    The damp heat stability and subsequent vacuum annealing behavior of aluminum doped zinc oxide (AZO) films was investigated using Hall effect measurements, X-ray diffraction (XRD) and optical spectrometry techniques. The AZO films were deposited on glass or silicon wafers using reactive and non-reactive magnetron sputtering from metallic and ceramic targets, respectively. Additionally, we characterized surface textured AZO films, which are used as light scattering transparent conductive oxide (TCO) in silicon thin film solar cells. For all films a degradation of the electrical film properties was found after the damp heat treatment. For thick compact films, with large grain size, only a small increase in the electrical resistivity was observed, whereas less compact films prepared at high deposition pressures or very thin films (< 300 nm) showed an increase in resistivity by up to a factor of three already after 300 h. The conductivity degradation during damp heat treatment could be largely reversed by annealing in vacuum. However, annealing temperatures of at least 150 deg. C were required. Possible mechanisms explaining the experimental results are discussed

  5. Preparation of mesoporous carbon nitride structure by the dealloying of Ni/a-CN nanocomposite films

    Science.gov (United States)

    Zhou, Han; Shen, Yongqing; Huang, Jie; Liao, Bin; Wu, Xianying; Zhang, Xu

    2018-05-01

    The preparation of mesoporous carbon nitride (p-CN) structure by the selective dealloying process of Ni/a-CN nanocomposite films is investigated. The composition and structure of the Ni/a-CN nanocomposite films and porous carbon nitride (p-CN) films are determined by scan electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy. Phase separated structure including nickel carbide phase and the surrounding amorphous carbon nitride (a-CN) matrix are detected for the as-deposited films. Though the bulk diffusion is introduced in the film during the annealing process, the grain sizes for the post-annealed films are around 10 nm and change little comparing with the ones of the as-deposited films, which is associated with the thermostability of the CN surrounding in the film. The p-CN skeleton with its pore size around 12.5 nm is formed by etching the post-annealed films, indicative of the stability of the phase separated structure during the annealing process.

  6. Phase Composition of Samarium Niobate and Tantalate Thin Films Prepared by Sol-Gel Method

    Science.gov (United States)

    Bruncková, H.; Medvecký, Ľ.; Múdra, E.; Kovalčiková, A.; Ďurišin, J.; Šebek, M.; Girman, V.

    2017-12-01

    Samarium niobate SmNbO4 (SNO) and tantalate SmTaO4 (STO) thin films ( 100 nm) were prepared by sol-gel/spin-coating process on alumina substrates with PZT interlayer and annealing at 1000°C. The precursors of films were synthesized using Nb or Ta tartrate complexes. The improvement of the crystallinity of monoclinic M'-SmTaO4 phase via heating was observed through the coexistence of small amounts of tetragonal T-SmTa7O19 phase in STO precursor at 1000°C. The XRD results of SNO and STO films confirmed monoclinic M-SmNbO4 and M'-SmTaO4 phases, respectively, with traces of orthorhombic O-SmNbO4 (in SNO). In STO film, the single monoclinic M'-SmTaO4 phase was revealed. The surface morphology and topography of thin films were investigated by SEM and AFM analysis. STO film was smoother with roughness 3.2 nm in comparison with SNO (6.3 nm). In the microstructure of SNO film, small spherical ( 50 nm) and larger cuboidal particles ( 100 nm) of the SmNbO4 phase were observed. In STO, compact clusters composed of fine spherical SmTaO4 particles ( 20-50 nm) were found. Effect of samarium can contribute to the formation different polymorphs of these films for the application to environmental electrolytic thin film devices.

  7. Preparation of cellulose II and IIII films by allomorphic conversion of bacterial cellulose I pellicles

    International Nuclear Information System (INIS)

    Faria-Tischer, Paula C.S.; Tischer, Cesar A.; Heux, Laurent; Le Denmat, Simon; Picart, Catherine; Sierakowski, Maria-R.

    2015-01-01

    The structural changes resulting from the conversion of native cellulose I (Cel I) into allomorphs II (Cel II) and III I (Cel III I ) have usually been studied using powder samples from plant or algal cellulose. In this work, the conversion of Cel I into Cel II and Cel III I was performed on bacterial cellulose films without any mechanical disruption. The surface texture of the films was observed by atomic force microscopy (AFM) and the morphology of the constituting cellulose ribbons, by transmission electron microscopy (TEM). The structural changes were characterized using solid-state NMR spectroscopy as well as X-ray and electron diffraction. The allomorphic change into Cel II and Cel III I resulted in films with different crystallinity, roughness and hydrophobic/hydrophilicity surface and the films remained intact during all process of allomorphic conversion. - Highlights: • Description of a method to modify the allomorphic structure of bacterial cellulose filmsPreparation of films with specific morphologies and hydrophobic/hydrophilic surface characters • First report on cellulose III films from bacterial cellulose under swelling conditions • Detailed characterization of cellulose II and III films with complementary techniques • Development of films with specific properties as potential support for cells, enzymes, and drugs

  8. Metal doped fluorocarbon polymer films prepared by plasma polymerization using an RF planar magnetron target

    International Nuclear Information System (INIS)

    Biederman, H.; Holland, L.

    1983-01-01

    Fluorocarbon films have been prepared by plasma polymerization of CF 4 using an RF planar magnetron with an aluminium target. More than one order of magnitude higher deposition rate has been achieved in comparison with an r.f. diode system operated under similar conditions of monomer pressure and flow rate and power input. A glow discharge in a CF 4 [25%]-argon[75%] mixture was used to incorporate aluminium from a target electrode into the polymer films. The foregoing mixture and another based on CF 4 [87%]-argon[13%] were used in the RF discharge with a copper target. Some experiments with a gold target and pure CF 4 as the inlet gas were also made. The film structure was examined by SEM and TEM and characteristic micrographs are presented here. The composition of the films was estimated from an EAS study. The sheet resistivity of the metal/polymer film complexes was determined. (orig.)

  9. Microstructure of thin film platinum electrodes on yttrium stabilized zirconia prepared by sputter deposition

    Energy Technology Data Exchange (ETDEWEB)

    Toghan, Arafat, E-mail: arafat.toghan@pci.uni-hannover.de [Institute of Physical Chemistry and Electrochemistry, Leibniz University of Hannover, Callinstrasse 3-3a, D-30167 Hannover (Germany); Khodari, M. [Chemistry Department, Faculty of Science, South Valley University, Qena, 83523 (Egypt); Steinbach, F.; Imbihl, R. [Institute of Physical Chemistry and Electrochemistry, Leibniz University of Hannover, Callinstrasse 3-3a, D-30167 Hannover (Germany)

    2011-09-01

    (111) oriented thin film Pt electrodes were prepared on single crystals of yttrium-stabilized zirconia (YSZ) by sputter deposition of platinum. The electrodes were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED), X-ray diffraction (XRD), energy-dispersive X-ray analysis (EDX), atomic force microscopy (AFM) and by profilometry. SEM images of the as-sputtered platinum film show a compact amorphous Pt film covering uniformly the substrate. Upon annealing at 1123 K, gaps and pores at the interface develop leading to a partial dewetting of the Pt film. Increasing the annealing temperature to 1373 K transforms the polycrystalline Pt film into single crystalline grains exhibiting a (111) orientation towards the substrate.

  10. The effect of Nb doping on ferroelectric properties of PZT thin films prepared from polymeric precursors

    International Nuclear Information System (INIS)

    Souza, E.C.F.; Simoes, A.Z.; Cilense, M.; Longo, E.; Varela, J.A.

    2004-01-01

    Pure and Nb doped PbZr 0.4 Ti 0.6 O 3 thin films was prepared by the polymeric precursor method and deposited by spin coating on Pt/Ti/SiO 2 /Si (100) substrates and annealed at 700 deg. C. The films are oriented in (1 1 0) and (1 0 0) direction. The electric properties of PZT thin films show strong dependence of the crystallographic orientation. The P-E hysteresis loops for the thin film with composition PbZr 0.39 Ti 0.6 Nb 0.1 O 3 showed good saturation, with values for coercive field (E c ) equal to 60 KV cm -1 and for remanent polarization (P r ) equal to 20 μC cm -2 . The measured dielectric constant (ε) is 1084 for this film. These results show good potential for application in FERAM

  11. Electro-physical properties of superconducting ceramic thick film prepared by partial melting method.

    Science.gov (United States)

    Lee, Sang Heon

    2013-05-01

    BiSrCaCuO superconductor thick films were prepared at several curing temperatures, and their electro-physical properties were determined to find an optimum fabrication conditions. Critical temperatures of the superconductors were decreased with increasing melting temperature, which was related to the amount of equilibrium phases of the superconducting materials with temperature. The critical temperature of BiSrCaCuO bulk and thick film superconductors were 107 K and 96 K, respectively. The variation of susceptibility of the superconductor thick film formed at 950 degrees C had multi-step-type curve for 70 G externally applied field, whereas, a superconductor thick film formed at 885 degrees C had a single step-type curve like a bulk BiSrCaCuO ceramic superconductor in the temperature-susceptibility curves. A partial melting at 865 degrees C is one of optimum conditions for making a superconductor thick film with a relatively homogeneous phase.

  12. Preparation of flexible and heat-resisting conductive transparent film by the pyrosol process

    International Nuclear Information System (INIS)

    Usami, Hisanao; Nakasa, Akihiko; Adachi, Mami; Suzuki, Eiji; Fujimatsu, Hitoshi; Ohashi, Tatsuya; Yamada, Shigeo; Tsugita, Kouhei; Taniguchi, Yoshio

    2006-01-01

    A pyrosol process was successfully applied for the preparation of a flexible, conductive, and transparent inorganic film, a tin-doped indium oxide (ITO) film lined with a thin mica layer. This flexible heat-resistant ITO-mica film exhibited high conductivity and transparency, comparable to ITO deposited on glass substrate. The minimum radius of bending for the film, without any recognizable change in the conductivity and appearance, was 8 mm. The ITO deposited on mica showed a large (222) diffraction peak with a smaller (400) peak, in contrast to ITO deposited with (400) orientation on an ordinary glass substrate. Using the ITO-mica film, a prototype model of a flexible organic light emitting diode was fabricated

  13. Preparation and characterization of ultra-thin sol-gel films

    International Nuclear Information System (INIS)

    Shapiro, Leora; Marx, Sharon; Mandler, Daniel

    2007-01-01

    The formation and characterization of nanometer thick sol-gel films are reported. The films were prepared by spin-coating of a diluted solution of a silane precursor on a number of different substrates. The effect of dilution, rotation speed and nature of substrate on the thickness and homogeneity of the films was examined. Characterization of the films was carried out by profilometry, reflectance spectroscopy, atomic force microscopy, adhesion test and electrochemistry. We find that the dilution factor has a pronounced effect on the film thickness. Moreover, the time of dilution, namely, whether dilution was carried out before or after a period of hydrolysis, has a noticeable effect on the thickness as well as on the permeability of embedded species

  14. Electrocatalytic glucose oxidation at gold and gold-carbon nanoparticulate film prepared from oppositely charged nanoparticles

    International Nuclear Information System (INIS)

    Karczmarczyk, Aleksandra; Celebanska, Anna; Nogala, Wojciech; Sashuk, Volodymyr; Chernyaeva, Olga; Opallo, Marcin

    2014-01-01

    Graphical abstract: - Highlights: • Gold nanoparticulate film electrodes were prepared by layer-by-layer method from oppositely charged nanoparticles. • Positively charged nanoparticles play dominant role in glucose oxidation in alkaline solution. • Gold and gold-carbon nanoparticulate film electrodes exhibit similar glucose oxidation current and onset potential. - Abstract: Electrocatalytic oxidation of glucose was studied at nanoparticulate gold and gold-carbon film electrodes. These electrodes were prepared by a layer-by-layer method without application of any linker molecules. Gold nanoparticles were stabilized by undecane thiols functionalized by trimethyl ammonium or carboxylate groups, whereas the carbon nanoparticles were covered by phenylsulfonate functionalities. The gold nanoparticulate electrodes were characterized by UV-vis and XPS spectroscopy, atomic force microscopy and voltammetry, before and after heat-treatment. Heat-treatment facilitates the aggregation of the nanoparticles and affects the structure of the film. The comparison of the results obtained with film electrodes prepared from gold nanoparticles with the same charge and with gold-carbon nanoparticulate electrodes, proved that positively charged nanoparticles are responsible for the high electrocatalytic activity, whereas negatively charged ones act rather as a linker of the film

  15. ZnO THIN FILMS PREPARED BY SPRAY-PYROLYSIS TECHNIQUE FROM ORGANO-METALLIC PRECURSOR

    Directory of Open Access Journals (Sweden)

    Martin Mikulics

    2012-07-01

    Full Text Available Presented experiments utilize methanolic solution of zinc acetyl-acetonate as a precursor and sapphire (001 as a substrate for deposition of thin films of ZnO. The X-ray diffraction analysis revealed polycrystalline character of prepared films with preferential growth orientation along c-axis. The roughness of prepared films was assessed by AFM microscopy and represented by roughness root mean square (RMS value in range of 1.8 - 433 nm. The surface morphology was mapped by scanning electron microscopy showing periodical structure with several local defects. The optical transmittance spectrum of ZnO films was measured in wavelength range of 200-1000 nm. Prepared films are transparent in visible range with sharp ultra-violet cut-off at approximately 370 nm. Raman spectroscopy confirmed wurtzite structure and the presence of compressive stress within its structure as well as the occurrence of oxygen vacancies. The four-point Van der Pauw method was used to study the transport prosperities. The resistivity of presented ZnO films was found 8 × 10–2 Ω cm with carrier density of 1.3 × 1018 cm–3 and electron mobility of 40 cm2 V–1 s–1.

  16. Development of polymer film dosage forms of lidocaine for buccal administration: II. Comparison of preparation methods.

    Science.gov (United States)

    Okamoto, Hirokazu; Nakamori, Takahiko; Arakawa, Yotaro; Iida, Kotaro; Danjo, Kazumi

    2002-11-01

    In previous studies, we prepared film dosage forms of lidocaine (LC) with hydroxypropylcellulose (HPC) as a film base using the solvent evaporation (SE) method. However, from the viewpoint of environmental issues, a reduction in organic solvent use in pharmaceutical and other industries is required. In this study, we prepared the LC films by direct compression of the physical mixture (DCPM method) and direct compression of the spray dried powder (DCSD method). Magnesium stearate, which was required as a lubricant for direct compression, showed no effect on the LC release rate. The LC release rate (%/h) was independent of the compression pressure, but a higher pressure was preferable to easily remove the film from the punches. An increase in the film weight decreased the LC release rate expressed in %/h, whereas no significant effect of film weight was observed on the LC release rate from unit surface area expressed in mg/h/cm(2). The LC release rate (%/h) was independent of the LC content, suggesting that the LC release rate (mg/h) can be quantitatively controlled by changing the LC content in the formulation. The LC release rate and penetration rate were affected by the preparation method; that is, DCPM method dosage form. Copyright 2002 Wiley-Liss, Inc. and the American Pharmaceutical Association J Pharm Sci 91:2424-2432, 2002

  17. Rapid processing method for solution deposited YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Dawley, J.T.; Clem, P.G.; Boyle, T.J.; Ottley, L.M.; Overmyer, D.L.; Siegal, M.P

    2004-02-01

    YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) films, deposited on buffered metal substrates, are the primary candidate for second-generation superconducting (SC) wires, with applications including expanded power grid transmission capability, compact motors, and enhanced sensitivity magnetic resonance imaging. Feasibility of manufacturing such superconducting wires is dependent on high processing speed, often a limitation of vapor and solution-based YBCO deposition processes. In this work, YBCO films were fabricated via a new diethanolamine-modified trifluoroacetic film solution deposition method. Modifying the copper chemistry of the YBCO precursor solution with diethanolamine enables a hundredfold decrease in the organic pyrolysis time required for MA/cm{sup 2} current density (J{sub c}) YBCO films, from multiple hours to {approx}20 s in atmospheric pressure air. High quality, {approx}0.2 {mu}m thick YBCO films with J{sub c} (77 K) values {>=}2 MA/cm{sup 2} at 77 K are routinely crystallized from these rapidly pyrolyzed films deposited on LaAlO{sub 3}. This process has also enabled J{sub c} (77 K)=1.1 MA/cm{sup 2} YBCO films via 90 m/h dip-coating on Oak Ridge National Laboratory RABiTS textured metal tape substrates. This new YBCO solution deposition method suggests a route toward inexpensive and commercializable {approx}$10/kA m solution deposited YBCO coated conductor wires.

  18. Preparation of membranes by radiation grafting of acrylic acid onto Teflon-FEP film

    International Nuclear Information System (INIS)

    Gupta, B.D.

    1991-01-01

    The grafting of acrylic acid on radiation-peroxidised Teflon-FEP film provides an effective technique to prepare ion-exchange membranes. It was found that the grafted membranes have very high degree of swelling in aqueous KOH. The electric resistance of the film decreases considerably by grafting. An electric resistance of 0.2Ω cm 2 was obtained for a graft level beyond 58%. The hydrophilicity of the film was evaluated in terms of contact angle which shows a decreasing trend with the increasing degree of grafting. (author). 8 refs

  19. Preparation by thermal evaporation under vacuum of thin nickel films without support

    International Nuclear Information System (INIS)

    Prugne, P.; Garin, P.; Lechauguette, G.

    1959-01-01

    This note deals with the preparation of nickel films without support by means of the technique described but using a new evaporation apparatus. In effect it was necessary, in order to obtain these nickel films, to modify the thermal evaporation conditions. An attempt to obtain a film without support after evaporation in a conventional apparatus led almost invariably to defeat. This appeared to be due to the high concentration of oxygen and of various vapors (diffusion pumps, degassing, etc.) present in the residual atmosphere of the conventional evaporation system. Reprint of a paper published in 'Le Vide, N. 74, March-April 1958, p. 82-83

  20. SERS spectra of pyridine adsorbed on nickel film prepared by magnetron sputtering

    Science.gov (United States)

    Li, Daoyong; Ouyang, Yu; Chen, Li; Cao, Weiran; Shi, Shaohua

    2011-02-01

    As a repeating well and cheaper enhancement substrate, the nickel film was fabricated with magnetron sputtering coating instrument. Surface enhanced Raman spectra (SERS) of pyridine adsorbed on this nickel film are compared with the experimental values of gaseous pyridine, the theoretical value of pyridine solution listed in other literatures and our method is better than electro-chemical etching electrode method for large scale preparation. The enhancement factor of the nickel film is calculated and the result indicates that magnetron sputtering coating technology is feasible for obtaining good SERS active surface.

  1. Development of new releasing agents for preparation of thin self-supporting target films

    Energy Technology Data Exchange (ETDEWEB)

    Sugai, I; Takaku, S; Hasegawa, T [Tokyo Univ., Tanashi (Japan). Inst. for Nuclear Study

    1978-06-01

    Several kinds of materials were examined for the usefulness as releasing agents in the preparation of various thin self-supporting target films for use in nuclear reaction experiments. NaCl, BaCl/sub 2/, KCl, CsI, Teepol, glucose, KIO/sub 3/, mica, nitrocellulose of Formvar was deposited onto glass plates as the release agent by vacuum evaporation or dipping method. The obtained target film was tested on impurities from the release agent by using nuclear reactions. The relative effectiveness of each release agent was also considered from ease in the stripping of target films.

  2. Preparation and Characterization of Nicke-iron Alloy Film as Freestanding Electrode for Oxygen Evolution Reaction

    Directory of Open Access Journals (Sweden)

    Yao Mengqi

    2018-01-01

    Full Text Available This work reports the porous nicke-iron alloy film supported on stainless steel mesh as freestanding electrode for enhanced oxygen evolution reaction (OER catalyst prepared from an one step electrodeposition method. Results indicated that the porous nickle-iron alloy film exhibits a low overpotential of 270 mV at 10 mA cm-2 and excellent electroconductibility. The superior OER properties can be attributed to its novel synthetic process, conductive substrate and porous structure. This work will provide a new strategy to fabricate alloy film for OER electrocatalyst.

  3. Development of new releasing agents for preparation of thin self-supporting target films

    International Nuclear Information System (INIS)

    Sugai, Isao; Takaku, Seisaku; Hasegawa, Takeo

    1978-01-01

    Several kinds of materials were examined for the usefulness as releasing agents in the preparation of various thin self-supporting target films for use in nuclear reaction experiments. NaCl, BaCl 2 , KCl, CsI, Teepol, glucose, KIO 3 , mica, nitrocellulose of Formvar was deposited onto glass plates as the release agent by vacuum evaporation or dipping method. The obtained target film was tested on impurities from the release agent by using nuclear reactions. The relative effectiveness of each release agent was also considered from ease in the stripping of target films. (auth.)

  4. Chalcopyrite CuInSe2 films prepared by reactive sputtering

    International Nuclear Information System (INIS)

    Lommasson, T.C.; Burnett, A.F.; Chou, L.H.; Thornton, J.A.; Kim, M.

    1987-01-01

    Polycrystalline films of CuInSe 2 have been prepared on glass substrates by reactive cosputtering from Cu and In planar magnetron targets using Ar-H 2 Se as a working gas. The film compositions were close to the Cu 2 Se-In 2 Se 3 tie-line of the ternary phase diagram with Cu/In ratios ranging from 0.75 to about 2. This paper reports on measurements of the structural, electronic and optical properties of the films. The coatings on the Cu-rich side of the stoichiometric composition were characterized by a columnar structure with an uneven surface topography

  5. Preparation and application of agar/alginate/collagen ternary blend functional food packaging films.

    Science.gov (United States)

    Wang, Long-Feng; Rhim, Jong-Whan

    2015-09-01

    Ternary blend agar/alginate/collagen (A/A/C) hydrogel films with silver nanoparticles (AgNPs) and grapefruit seed extract (GSE) were prepared. Their performance properties, transparency, tensile strength (TS), water vapor permeability (WVP), water contact angle (CA), water swelling ratio (SR), water solubility (WS), and antimicrobial activity were determined. The A/A/C film was highly transparent, and both AgNPs and GSE incorporated blend films (A/A/C(AgNPs) and A/A/C(GSE)) exhibited UV-screening effect, especially, the A/A/C(GSE) film had high UV-screening effect without sacrificing the transmittance. In addition, the A/A/C blend films formed efficient hydrogel film with the water holding capacity of 23.6 times of their weight. Both A/A/C(AgNPs) and A/A/C(GSE) composite films exhibited strong antimicrobial activity against both Gram-positive (Listeria monocytogenes) and Gram-negative (Escherichia coli) food-borne pathogenic bacteria. The test results of fresh potatoes packaging revealed that all the A/A/C ternary blend films prevented forming of condensed water on the packaged film surface, both A/A/C(AgNPs) and A/A/C(GSE) composite films prevented greening of potatoes during storage. The results indicate that the ternary blend hydrogel films incorporated with AgNPs or GSE can be used not only as antifogging packaging films for highly respiring fresh agriculture produce, but also as an active food packaging system utilizing their strong antimicrobial activity. Copyright © 2015 Elsevier B.V. All rights reserved.

  6. Preparation of anatase TiO{sub 2} thin films by vacuum arc plasma evaporation

    Energy Technology Data Exchange (ETDEWEB)

    Miyata, Toshihiro [Optoelectronic Device System R and D Center, Kanazawa Institute of Technology, 7-1 Ohgigaoka, Nonoichi, Ishikawa 921-8501 (Japan)]. E-mail: tmiyata@neptune.kanazawa-it.ac.jp; Tsukada, Satoshi [Optoelectronic Device System R and D Center, Kanazawa Institute of Technology, 7-1 Ohgigaoka, Nonoichi, Ishikawa 921-8501 (Japan); Minami, Tadatsugu [Optoelectronic Device System R and D Center, Kanazawa Institute of Technology, 7-1 Ohgigaoka, Nonoichi, Ishikawa 921-8501 (Japan)

    2006-02-01

    Anatase titanium dioxide (TiO{sub 2}) thin films with high photocatalytic activity have been prepared with deposition rates as high as 16 nm/min by a newly developed vacuum arc plasma evaporation (VAPE) method using sintered TiO{sub 2} pellets as the source material. Highly transparent TiO{sub 2} thin films prepared at substrate temperatures from room temperature to 400 deg. C exhibited photocatalytic activity, regardless whether oxygen (O{sub 2}) gas was introduced during the VAPE deposition. The highest photocatalytic activity and photo-induced hydrophilicity were obtained in anatase TiO{sub 2} thin films prepared at 300 deg. C, which correlated to the best crystallinity of the films, as evidenced from X-ray diffraction. In addition, a transparent and conductive anatase TiO{sub 2} thin film with a resistivity of 2.6 x 10{sup -1} {omega} cm was prepared at a substrate temperature of 400 deg. C without the introduction of O{sub 2} gas.

  7. Antimicrobial Activity of Thin Solid Films of Silver Doped Hydroxyapatite Prepared by Sol-Gel Method

    Science.gov (United States)

    Iconaru, Simona Liliana; Chapon, Patrick; Le Coustumer, Philippe; Predoi, Daniela

    2014-01-01

    In this work, the preparation and characterization of silver doped hydroxyapatite thin films were reported and their antimicrobial activity was characterized. Silver doped hydroxyapatite (Ag:HAp) thin films coatings substrate was prepared on commercially pure Si disks by sol-gel method. The silver doped hydroxyapatite thin films were characterized by various techniques such as Scanning electron microscopy (SEM) with energy Dispersive X-ray attachment (X-EDS), Fourier transform infrared spectroscopy (FT-IR), and glow discharge optical emission spectroscopy (GDOES). These techniques have permitted the structural and chemical characterisation of the silver doped hydroxyapatite thin films. The antimicrobial effect of the Ag:HAp thin films on Escherichia coli and Staphylococcus aureus bacteria was then investigated. This is the first study on the antimicrobial effect of Ag:HAp thin films obtained by sol-gel method. The results of this study have shown that the Ag:HAp thin films with x Ag = 0.5 are effective against E. coli and S. aureus after 24 h. PMID:24523630

  8. Regenerated cellulose/halloysite nanotube nanocomposite films prepared with an ionic liquid

    Energy Technology Data Exchange (ETDEWEB)

    Soheilmoghaddam, Mohammad [Department of Polymer Engineering, Faculty of Chemical Engineering, Universiti Teknologi Malaysia (UTM), Johor (Malaysia); Wahit, Mat Uzir, E-mail: mat.uzir@cheme.utm.my [Center for Composites, Universiti Teknologi Malaysia (UTM), 81310 Skudai, Johor (Malaysia); Mahmoudian, Shaya [Department of Textile Engineering, Kashan Branch, Islamic Azad University, Kashan (Iran, Islamic Republic of); Hanid, Nurbaiti Abdul [Department of Polymer Engineering, Faculty of Chemical Engineering, Universiti Teknologi Malaysia (UTM), Johor (Malaysia)

    2013-09-16

    Regenerated cellulose/halloysite nanotube (RC/HNT) nanocomposite films were successfully prepared in ionic liquid, 1-butyl-3-methylimidazolium chloride (BMIMCl) using solution casting method. The structural, morphological, thermal and mechanical properties of RC/HNT nanocomposites were investigated. X-ray diffraction analysis revealed a cellulose II crystalline structure and well dispersed HNT in RC/HNT nanocomposite films. At 6 wt.% HNT film, tensile strength and Young's modulus of RC films improved by 55.3% and 100%, respectively. Moisture absorption by the nanocomposites in an environment with 75% constant relative humidity was reduced by the addition of HNT to the RC. The presence of HNT enhanced the thermal stability and char yield of RC. The significant reinforcing effects of HNTs demonstrated that there is a possible interface interaction between cellulose and HNT which yielded better thermal and mechanical properties of the nanocomposite films as compared to pure RC. - Highlights: • The RC/HNT nanocomposite films were prepared via ionic liquid, BMIMCl. • XRD diffraction patterns and FESEM revealed well dispersed HNT in cellulose matrix. • The nanocomposite films exhibited excellent mechanical properties. • Moisture absorption and diffusion coefficient of RC reduced by HNT incorporation. • Addition of HNT enhanced thermal stability and activation energy of the RC.

  9. Regenerated cellulose/halloysite nanotube nanocomposite films prepared with an ionic liquid

    International Nuclear Information System (INIS)

    Soheilmoghaddam, Mohammad; Wahit, Mat Uzir; Mahmoudian, Shaya; Hanid, Nurbaiti Abdul

    2013-01-01

    Regenerated cellulose/halloysite nanotube (RC/HNT) nanocomposite films were successfully prepared in ionic liquid, 1-butyl-3-methylimidazolium chloride (BMIMCl) using solution casting method. The structural, morphological, thermal and mechanical properties of RC/HNT nanocomposites were investigated. X-ray diffraction analysis revealed a cellulose II crystalline structure and well dispersed HNT in RC/HNT nanocomposite films. At 6 wt.% HNT film, tensile strength and Young's modulus of RC films improved by 55.3% and 100%, respectively. Moisture absorption by the nanocomposites in an environment with 75% constant relative humidity was reduced by the addition of HNT to the RC. The presence of HNT enhanced the thermal stability and char yield of RC. The significant reinforcing effects of HNTs demonstrated that there is a possible interface interaction between cellulose and HNT which yielded better thermal and mechanical properties of the nanocomposite films as compared to pure RC. - Highlights: • The RC/HNT nanocomposite films were prepared via ionic liquid, BMIMCl. • XRD diffraction patterns and FESEM revealed well dispersed HNT in cellulose matrix. • The nanocomposite films exhibited excellent mechanical properties. • Moisture absorption and diffusion coefficient of RC reduced by HNT incorporation. • Addition of HNT enhanced thermal stability and activation energy of the RC

  10. Antimony sulfide thin films prepared by laser assisted chemical bath deposition

    International Nuclear Information System (INIS)

    Shaji, S.; Garcia, L.V.; Loredo, S.L.; Krishnan, B.

    2017-01-01

    Highlights: • Antimony sulfide thin films were prepared by normal CBD and laser assisted CBD. • Characterized these films using XRD, XPS, AFM, optical and electrical measurements. • Accelerated growth was observed in the laser assisted CBD process. • These films were photoconductive. - Abstract: Antimony sulfide (Sb_2S_3) thin films were prepared by laser assisted chemical bath deposition (LACBD) technique. These thin films were deposited on glass substrates from a chemical bath containing antimony chloride, acetone and sodium thiosulfate under various conditions of normal chemical bath deposition (CBD) as well as in-situ irradiation of the chemical bath using a continuous laser of 532 nm wavelength. Structure, composition, morphology, optical and electrical properties of the Sb_2S_3 thin films produced by normal CBD and LACBD were analyzed by X-Ray diffraction (XRD), Raman Spectroscopy, Atomic force microscopy (AFM), X-Ray photoelectron spectroscopy (XPS), UV–vis spectroscopy and Photoconductivity. The results showed that LACBD is an effective synthesis technique to obtain Sb_2S_3 thin films for optoelectronic applications.

  11. Antimicrobial activity of thin solid films of silver doped hydroxyapatite prepared by sol-gel method.

    Science.gov (United States)

    Iconaru, Simona Liliana; Chapon, Patrick; Le Coustumer, Philippe; Predoi, Daniela

    2014-01-01

    In this work, the preparation and characterization of silver doped hydroxyapatite thin films were reported and their antimicrobial activity was characterized. Silver doped hydroxyapatite (Ag:HAp) thin films coatings substrate was prepared on commercially pure Si disks by sol-gel method. The silver doped hydroxyapatite thin films were characterized by various techniques such as Scanning electron microscopy (SEM) with energy Dispersive X-ray attachment (X-EDS), Fourier transform infrared spectroscopy (FT-IR), and glow discharge optical emission spectroscopy (GDOES). These techniques have permitted the structural and chemical characterisation of the silver doped hydroxyapatite thin films. The antimicrobial effect of the Ag:HAp thin films on Escherichia coli and Staphylococcus aureus bacteria was then investigated. This is the first study on the antimicrobial effect of Ag:HAp thin films obtained by sol-gel method. The results of this study have shown that the Ag:HAp thin films with x(Ag) = 0.5 are effective against E. coli and S. aureus after 24 h.

  12. Antimicrobial Activity of Thin Solid Films of Silver Doped Hydroxyapatite Prepared by Sol-Gel Method

    Directory of Open Access Journals (Sweden)

    Simona Liliana Iconaru

    2014-01-01

    Full Text Available In this work, the preparation and characterization of silver doped hydroxyapatite thin films were reported and their antimicrobial activity was characterized. Silver doped hydroxyapatite (Ag:HAp thin films coatings substrate was prepared on commercially pure Si disks by sol-gel method. The silver doped hydroxyapatite thin films were characterized by various techniques such as Scanning electron microscopy (SEM with energy Dispersive X-ray attachment (X-EDS, Fourier transform infrared spectroscopy (FT-IR, and glow discharge optical emission spectroscopy (GDOES. These techniques have permitted the structural and chemical characterisation of the silver doped hydroxyapatite thin films. The antimicrobial effect of the Ag:HAp thin films on Escherichia coli and Staphylococcus aureus bacteria was then investigated. This is the first study on the antimicrobial effect of Ag:HAp thin films obtained by sol-gel method. The results of this study have shown that the Ag:HAp thin films with xAg=0.5 are effective against E. coli and S. aureus after 24 h.

  13. Antimony sulfide thin films prepared by laser assisted chemical bath deposition

    Energy Technology Data Exchange (ETDEWEB)

    Shaji, S., E-mail: sshajis@yahoo.com [Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Av. Pedro de Alba s/n, Ciudad Universitaria, San Nicolás de los Garza, Nuevo León, 66455 (Mexico); CIIDIT—Universidad Autónoma de Nuevo León, Apodaca, Nuevo León (Mexico); Garcia, L.V. [Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Av. Pedro de Alba s/n, Ciudad Universitaria, San Nicolás de los Garza, Nuevo León, 66455 (Mexico); Loredo, S.L. [Centro de Investigación en Materiales Avanzados (CIMAV), Unidad Monterrey, PIIT, Apodaca, Nuevo León (Mexico); Krishnan, B. [Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Av. Pedro de Alba s/n, Ciudad Universitaria, San Nicolás de los Garza, Nuevo León, 66455 (Mexico); CIIDIT—Universidad Autónoma de Nuevo León, Apodaca, Nuevo León (Mexico); and others

    2017-01-30

    Highlights: • Antimony sulfide thin films were prepared by normal CBD and laser assisted CBD. • Characterized these films using XRD, XPS, AFM, optical and electrical measurements. • Accelerated growth was observed in the laser assisted CBD process. • These films were photoconductive. - Abstract: Antimony sulfide (Sb{sub 2}S{sub 3}) thin films were prepared by laser assisted chemical bath deposition (LACBD) technique. These thin films were deposited on glass substrates from a chemical bath containing antimony chloride, acetone and sodium thiosulfate under various conditions of normal chemical bath deposition (CBD) as well as in-situ irradiation of the chemical bath using a continuous laser of 532 nm wavelength. Structure, composition, morphology, optical and electrical properties of the Sb{sub 2}S{sub 3} thin films produced by normal CBD and LACBD were analyzed by X-Ray diffraction (XRD), Raman Spectroscopy, Atomic force microscopy (AFM), X-Ray photoelectron spectroscopy (XPS), UV–vis spectroscopy and Photoconductivity. The results showed that LACBD is an effective synthesis technique to obtain Sb{sub 2}S{sub 3} thin films for optoelectronic applications.

  14. High quality antireflective ZnS thin films prepared by chemical bath deposition

    International Nuclear Information System (INIS)

    Tec-Yam, S.; Rojas, J.; Rejón, V.; Oliva, A.I.

    2012-01-01

    Zinc sulfide (ZnS) thin films for antireflective applications were deposited on glass substrates by chemical bath deposition (CBD). Chemical analysis of the soluble species permits to predict the optimal pH conditions to obtain high quality ZnS films. For the CBD, the ZnCl 2 , NH 4 NO 3 , and CS(NH 2 ) 2 were fixed components, whereas the KOH concentration was varied from 0.8 to 1.4 M. Groups of samples with deposition times from 60 to 120 min were prepared in a bath with magnetic agitation and heated at 90 °C. ZnS films obtained from optimal KOH concentrations of 0.9 M and 1.0 M exhibited high transparency, homogeneity, adherence, and crystalline. The ZnS films presented a band gap energy of 3.84 eV, an atomic Zn:S stoichiometry ratio of 49:51, a transmittance above 85% in the 300–800 nm wavelength range, and a reflectance below 25% in the UV–Vis range. X-ray diffraction analysis revealed a cubic structure in the (111) orientation for the films. The thickness of the films was tuned between 60 nm and 135 nm by controlling the deposition time and KOH concentration. The incorporation of the CBD-ZnS films into ITO/ZnS/CdS/CdTe and glass/Mo/ZnS heterostructures as antireflective layer confirms their high optical quality. -- Highlights: ► High quality ZnS thin films were prepared by chemical bath deposition (CBD). ► Better CBD-ZnS films were achieved by using 0.9 M-KOH concentration. ► Reduction in the reflectance was obtained for ZnS films used as buffer layers.

  15. Preparation and characterization of nanodiamond cores coated with a thin Ni-Zn-P alloy film

    International Nuclear Information System (INIS)

    Wang Rui; Ye Weichun; Ma Chuanli; Wang Chunming

    2008-01-01

    Nanodiamond cores coated with a thin Ni-Zn-P alloy film were prepared by an electroless deposition method under the conditions of tin chloride sensitization and palladium chloride activation. The prepared materials were analyzed by Fourier transform infrared (FTIR) spectrometry and X-ray diffraction (XRD). The nanostructure of the materials was then characterized by transmission electron microscopy (TEM). The alloy film composition was characterized by Energy Dispersive X-ray (EDX) analysis. The results indicated the approximate composition 49.84%Ni-37.29%Zn-12.88%P was obtained

  16. Preparation and tribological tests of thin fluoroorganic films

    International Nuclear Information System (INIS)

    Cichomski, M.; Grobelny, J.; Celichowski, G.

    2008-01-01

    Adhesion, friction and consequent wear of sliding surfaces are the basic problems that limit the performance and reliability of microelectromechanical devices. Lubrication of these nano- and microscale contacts is different from traditional lubricants. Self-assembled monolayers (SAMs) chemically bonded to the substrate are considered to be the best solution of lubrication. The majority of these monolayers are hydrophobic providing low friction, adhesion and wear. Chemical vapor deposition was used to grow a fluorosilane film on silicon Si(1 0 0) and a condensed monolayer of 3-mercaptopropyltrimethoxysilane (MPTMS) on Au(1 1 1). The films were characterized by means of a contact angle analyzer for hydrophobicity, and time-of-flight secondary ion mass spectrometry (ToF-SIMS) for identification of thin fluoroorganic monolayers deposited on silica surfaces and condensed monolayer MPTMS. Adhesion and friction measurements were performed using atomic force microscopy (AFM) and compared with measurements performed using a microtribometer operating in millinewton (mN) normal load range. Nanotribological measurements indicated that silica and MPTMS modified by fluorosilanes have the lowest friction coefficient and indicated a decrease friction coefficient with increasing fluoric alkyl chain length

  17. Preparation, characterization and evaluation of drug-delivery systems: Pectin and mefenamic acid films

    Energy Technology Data Exchange (ETDEWEB)

    Moreira, R.B. [Universidade Federal de Mato Grosso, Rodovia MT-100, Km 3,5, Barra do Garças, MT CEP 78600-000 (Brazil); Teixeira, J.A. [Universidade Federal de Mato Grosso, Cuiabá, MT CEP 78060-900 (Brazil); Furuyama-Lima, A.M. [Universidade Estadual Paulista, IBILCE, São José do Rio Preto, SP CEP 15054-000 (Brazil); Souza, N.C. de [Universidade Federal de Mato Grosso, Rodovia MT-100, Km 3,5, Barra do Garças, MT CEP 78600-000 (Brazil); Siqueira, A.B., E-mail: buzutti@cpd.ufmt.br [Universidade Federal de Mato Grosso, Rodovia MT-100, Km 3,5, Barra do Garças, MT CEP 78600-000 (Brazil)

    2014-08-20

    Highlights: • The films were prepared and characterized by FTIR, TG–DSC/FTIR and AFM microscopy. • The results provided information on the composition, dehydration, thermal stability, thermal decomposition. • DSC results of CaHCl shows two overlapping endothermic peaks. • The AFM image shows great similarity for A5 and A6 films. • A5 and A6 films functioned well as a topical delivery system. - Abstract: Mefenamic acid (H-Mef) is a nonsteroidal anti-inflammatory drug (NSAID). Various adhesive dosage forms of NSAIDs have been developed, which include adhesive tablets, gels, ointments, patches and more recently, polymeric films. The objective of this study was the development of H-Mef adhesive films to be used as a drug-delivery system with different ratios of pectin and calcium chloride dihydrate by the casting technique. The materials were characterized by TG–DSC coupled FTIR, AFM (atomic force microscopy) and spectroscopic techniques. The results provided information about the dehydration, film roughness, surface morphology, thermal decomposition, as well as identification of gaseous products evolved during thermal decomposition. The characterizations indicated the A5 and A6 films functioned well, with 99% H-Mef released within 15 min at pH 5, suggesting these degradable films could be used as a topical delivery system.

  18. Universal biomimetic preparation and immobilization of layered double hydroxide films and adsorption behavior

    Energy Technology Data Exchange (ETDEWEB)

    Zhou, Wei; Zhang, Wenpeng; Chen, Zilin

    2017-01-15

    Highlights: • An in situ method is developed for immobilization of nanoscale LDHs. • The universal method can be applied on multiple substrates. • The homogeneous LDHs film can be synthesis and immobilized in one step. • The LDHs film showed good adsorption performance towards anionic compounds. - Abstract: Preparation and immobilization of layered double hydroxides (LDHs) film onto multiple substrates is important and challenging in functional materials fields by date. In this work, a simple and universal polydopamine (PD)-based layer-by-layer assembly strategy was developed for the immobilization of LDHs film onto surfaces such as polypropylene chip, glass slides and metal coins. The surface of substrates was firstly modified by polydopamine functionalization, and then LDHs film was synthesized via urea method and directly immobilized on the PD layer by in situ growing strategy in one step. The PD layer as well as the final LDHs film was characterized by energy dispersive X-ray spectroscopy, scanning electron microscope, infrared spectroscopy, X-ray diffraction pattern and X-ray photoelectron spectra. It has been demonstrated the formation of the dense and homogeneous nanoscaled LDHs film with 400 nm thickness. Adsorption behavior of the fabricated NiAl-LDHs film toward anionic dyes and pharmaceuticals was further assessed. To demonstrate their extensive application, fast and high efficient adsorption of anionic dyes and pharmaceuticals was achieved by NiAl-LDHs-modified polypropylene centrifugal tube.

  19. Preparation and Characterization of Blended Films from Quaternized Hemicelluloses and Carboxymethyl Cellulose

    Science.gov (United States)

    Qi, Xian-Ming; Liu, Shi-Yun; Chu, Fang-Bing; Pang, Shuai; Liang, Yan-Ru; Guan, Ying; Peng, Feng; Sun, Run-Cang

    2015-01-01

    Utilization of hemicelluloses from biomass energy is an important approach to explore renewable resources. A convenient, quick, and inexpensive method for the preparation of blended films from quaternized hemicelluloses (QH) and carboxymethyl cellulose (CMC) was introduced into this study. QH and CMC solution were first mixed to form homogeneous suspension, and then were dried under vacuum to fabricate the blended films. The FT-IR and XRD results indicated that the linkage between QH and CMC was due to the hydrogen bonding and electrostatic interaction. From the results of mechanical properties and water vapor permeability (WVP), the tensile strength of the blended films increased with the QH/CMC content ratio increasing in appropriate range, and the WVP of the blended films decreased. The maximum value of tensile strength of blend film achieved was 27.4 MPa. In addition, the transmittances of the blended films increased with the decreasing of QH/CMC content ratio. When the weight ratio (QH: CMC) was 1:1.5, the blend film showed the best light transmittance (45%). All the results suggested that the blended films could be used in areas of application in the coating and packaging fields from the good tensile strength, transmittance, and low WVP. PMID:28787804

  20. Preparation and Characterization of Blended Films from Quaternized Hemicelluloses and Carboxymethyl Cellulose

    Directory of Open Access Journals (Sweden)

    Xian-Ming Qi

    2015-12-01

    Full Text Available Utilization of hemicelluloses from biomass energy is an important approach to explore renewable resources. A convenient, quick, and inexpensive method for the preparation of blended films from quaternized hemicelluloses (QH and carboxymethyl cellulose (CMC was introduced into this study. QH and CMC solution were first mixed to form homogeneous suspension, and then were dried under vacuum to fabricate the blended films. The FT-IR and XRD results indicated that the linkage between QH and CMC was due to the hydrogen bonding and electrostatic interaction. From the results of mechanical properties and water vapor permeability (WVP, the tensile strength of the blended films increased with the QH/CMC content ratio increasing in appropriate range, and the WVP of the blended films decreased. The maximum value of tensile strength of blend film achieved was 27.4 MPa. In addition, the transmittances of the blended films increased with the decreasing of QH/CMC content ratio. When the weight ratio (QH: CMC was 1:1.5, the blend film showed the best light transmittance (45%. All the results suggested that the blended films could be used in areas of application in the coating and packaging fields from the good tensile strength, transmittance, and low WVP.

  1. Preparation and characterization of sol-gel derived TiO2 films

    International Nuclear Information System (INIS)

    Hong, Y.J.; Brungs, M.P.; Chaplin, R.P.; Sizgek, E.

    2001-01-01

    Crack-free transparent titania films have been prepared through a new sol-gel process combined with hydrogen peroxide treatment. Hydrogen peroxide and HCl were used to dissolve amorphous titania powder which is obtained by drying common sol-gel titania sol. The peroxo-titania sol produced a thicker film than the common sol-gel titania sol due to a higher degree of condensation. Film thickness could be further increased by controlled drying conditions of the amorphous titania powder or 'aging' the sol. Polyethylene glycol (PEG) and chemical additives were effective in controlling condensation rate by preventing rapid condensation during curing of the film. When these two components were incorporated, it was possible to create a 0.5μm transparent film and PEG could also control the porosity of the film. The cured film was analysed by XRD and Raman spectroscopy. In order to measure the reflective index and thickness of the titania film, an ellipsometer was used. Copyright (2001) The Australian Ceramic Society

  2. Preparation and spectroscopic analysis of zinc oxide nanorod thin films of different thicknesses

    Directory of Open Access Journals (Sweden)

    Mia Nasrul Haque

    2017-10-01

    Full Text Available Zinc oxide thin films with different thicknesses were prepared on microscopic glass slides by sol-gel spin coating method, then hydrothermal process was applied to produce zinc oxide nanorod arrays. The nanorod thin films were characterized by various spectroscopic methods of analysis. From the images of field emission scanning electron microscope (FESEM, it was observed that for the film thickness up to 200 nm the formed nanorods with wurtzite hexagonal structure were uniformly distributed over the entire surface substrate. From X-ray diffraction analysis it was revealed that the thin films had good polycrystalline nature with highly preferred c-axis orientation along (0 0 2 plane. The optical characterization done by UV-Vis spectrometer showed that all the films had high transparency of 83 % to 96 % in the visible region and sharp cut off at ultraviolet region of electromagnetic spectrum. The band gap of the films decreased as their thickness increased. Energy dispersive X-ray spectroscopy (EDS showed the presence of zinc and oxygen elements in the films and Fourier transform infrared spectroscopy (FT-IR revealed the chemical composition of ZnO in the film.

  3. Preparation and water absorption of cross-linked chitosan/silk fibroin blend films

    Energy Technology Data Exchange (ETDEWEB)

    Suesat, Jantip; Rujiravanit, Ratana [Chulalongkorn University, The Petroleum and Petrochemical College, Bangkok (Thailand); Jamieson, Alexander M. [Case Western Reserve Univ., Department of Macromolecular Science, Cleveland (United States); Tokura, Seiichi [Kansai Univ., Faculty of Engineering, Osaka (Japan)

    2001-03-01

    Natural polymer blend films composed of chitosan and silk fibroin were prepared by varying the ratio of chitosan to silk fibroin, with and without glutaraldehyde as a crosslinking agent. The effects of the ratio of chitosan to silk fibroin and crosslinking agent on swelling behavior of the blend films were studied. For the swelling behavior, the blend films exhibited a dramatic change in the degree of swelling when immersed in acidic solutions. The degree of swelling of the films increased as the chitosan content increased; the blend film with 80% chitosan content had the maximum degree of swelling. It appeared that crosslinking had occurred in the blend films which helped the films to retain their three dimensional structure. In addition, FTIR spectra of the films showed evidence of hydrogen bonding interaction between chitosan and silk fibroin. For the effect of salt type, the films were immersed in various types of aqueous salt solutions, viz NaCl, LiCl, CaCl{sub 2}, AlCl{sub 3}, and FeCl{sub 3}. The films immersed in AlCl{sub 3} and FeCl{sub 3} aqueous solutions gave the maximum degree of swelling. The effects of AlCl{sub 3} and FeCl{sub 3} concentrations on swelling behavior were also investigated. It was found that the maximum degree of swelling of the films occurred at 1.0 x 10{sup -2} M of AlCl{sub 3} and FeCl{sub 3} aqueous solutions. (author)

  4. Reaction kinetics for preparation of silica film with Stoeber method

    International Nuclear Information System (INIS)

    Shang Mengying; Jiang Xiaodong; Liu Miao; Luo Xuan; Tang Yongjian; Cao Linhong

    2013-01-01

    A new formula was proposed to investigate the relationship between reaction time and tetraethylorthosilicate (TEOS) conversion rate for preparation of silica sol with Stöber method, by studying the reaction kinetics of TEOS hydrolytic process. An appropriate conversion rate was then determined and used to calculate the theoretical optimal reaction time. Meanwhile, silica sols were prepared by sol-gel process using TEOS as precursor and ammonia as catalyst. It was found that the reaction time decreases with an increasing amount of ammonia and water. The values of experimental optimal reaction time were obtained, and agree with the theoretical results (the errors are within 5%), which shows good applicability of our formula. (authors)

  5. Composition and microstructure of beryllium carbide films prepared by thermal MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    He, Yu-dan; Luo, Jiang-shan; Li, Jia; Meng, Ling-biao; Luo, Bing-chi; Zhang, Ji-qiang; Zeng, Yong; Wu, Wei-dong, E-mail: wuweidongding@163.com

    2016-02-15

    Highlights: • Non-columnar-crystal Be{sub 2}C films were firstly prepared by thermal MOCVD. • Beryllium carbide was always the dominant phase in the films. • α-Be and carbon existed in films deposited below and beyond 400 °C, respectively. • Morphology evolved with temperatures and no columnar grains were characterized. • The preferred substrate temperature for depositing high quality Be{sub 2}C films was 400 °C. - Abstract: Beryllium carbide films without columnar-crystal microstructures were prepared on the Si (1 0 0) substrate by thermal metal organic chemical vapor deposition using diethylberyllium as precursor. The influence of the substrate temperature on composition and microstructure of beryllium carbide films was systematically studied. Crystalline beryllium carbide is always the dominant phase according to XRD analysis. Meanwhile, a small amount of α-Be phase exists in films when the substrate temperature is below 400 °C, and hydrocarbon or amorphous carbon exists when the temperature is beyond 400 °C. Surfaces morphology shows transition from domes to cylinders, to humps, and to tetraquetrous crystalline needles with the increase of substrate temperature. No columnar grains are characterized throughout the thickness as revealed from the cross-section views. The average densities of these films are determined to be 2.04–2.17 g/cm{sup 3}. The findings indicate the substrate temperature has great influences on the composition and microstructure of the Be{sub 2}C films grown by thermal MOCVD.

  6. Characterization of cobalt oxide thin films prepared by a facile spray pyrolysis technique using perfume atomizer

    Energy Technology Data Exchange (ETDEWEB)

    Louardi, A.; Rmili, A.; Ouachtari, F.; Bouaoud, A. [Laboratoire des Hautes Energies, Sciences de l' Ingenierie et Reacteurs (LHESIR), Equipe Ingenierie et Materiaux (INMA), Departement de Physique, Faculte des Sciences, Kenitra (Morocco); Elidrissi, B., E-mail: e.bachir@mailcity.com [Laboratoire des Hautes Energies, Sciences de l' Ingenierie et Reacteurs (LHESIR), Equipe Ingenierie et Materiaux (INMA), Departement de Physique, Faculte des Sciences, Kenitra (Morocco); Erguig, H. [Laboratoire des Hautes Energies, Sciences de l' Ingenierie et Reacteurs (LHESIR), Equipe Ingenierie et Materiaux (INMA), Departement de Physique, Faculte des Sciences, Kenitra (Morocco)

    2011-09-15

    Highlights: > Co{sub 3}O{sub 4} thin films show a micro porous structure. > Co{sub 3}O{sub 4} thin films are formed with spherical grains less than 50 nm in diameter. > The porous structure of Co{sub 3}O{sub 4} films is expected to have promising application in electrochromism. - Abstract: Cobalt oxide (Co{sub 3}O{sub 4}) thin films were prepared by a facile spray pyrolysis technique using perfume atomizer from aqueous solution of hydrated cobalt chloride salt (CoCl{sub 2}.6H{sub 2}O) as source of cobalt. The films were deposited onto the amorphous glass substrates kept at different temperatures (300-500 deg. C). The influences of molar concentration of the starting solution and substrate temperature on the structural, morphological and optical properties of (Co{sub 3}O{sub 4}) thin films were studied. It was found from X-ray diffraction (XRD) analysis that the films prepared with molar concentration greater than 0.025 M/L were polycrystalline spinel type cubic structure. The preferred orientation of the crystallites of these films changes gradually from (6 2 2) to (1 1 1) when the substrate temperature increases. By Raman spectroscopy, five Raman active modes characteristic of Co{sub 3}O{sub 4} spinel type cubic structure were found and identified at 194, 484, 522, 620 and 691 cm{sup -1}. The scanning electron microscopy (SEM) images showed micro porous structure with very fine grains less than 50 nm in diameter. These films exhibited also a transmittance value of about 70% in the visible and infra red range.

  7. Preparation and characterization of porous carbon–titania nanocomposite films as solar selective absorbers

    International Nuclear Information System (INIS)

    Cheng, B.; Wang, K.K.; Wang, K.P.; Li, M.; Jiang, W.; Cong, B.J.; Song, C.L.; Jia, S.H.; Han, G.R.; Liu, Y.

    2015-01-01

    Highlights: • The nanocomposites porous C/TiO 2 film were fabricated via PIPS method. • The HRTEM reveals the size of carbon nanoparticles is about 1.1 nm. • The PVP advantages residual carbon content but suppresses its crystallization. • The film exhibits high α (0.928–0.959) with low ε (0.074–0.105) for single layer. - Abstract: Newly proposed selective solar absorbers of porous carbon–titania nanocomposite films with a well-defined interconnected macropores structure were prepared via a polymer-assisted photopolymerization-induced phase-separation method. The microstructure and optical properties of as-deposited nanocomposite films were characterized and discussed in detail. The results show that non-ionic water-soluble polymer polyvinylpyrrolidone works as a sol modifier advantaging the mean size of the interconnected macropores, residual carbon content, and films thickness, but suppresses the order degree of the carbon remained in the films. The high-resolution transmission electron microscopy demonstrated that a small amount of graphite particles with size of around 1.1 nm embedded in the cavity of the porous while the wall of the porous consists of amorphous carbon and titania composites. The single layer of as-prepared porous C/TiO 2 nanocomposite films exhibits high solar absorptance (α = 0.928–0.959) with low thermal emittance (ε = 0.074–0.105), yielding an optimized photothermal conversion efficiency η = α − ε of 0.864 corresponding to a film thickness of around 338 nm, indication of such film is fair enough to serve as an excellent solar absorber

  8. Atomic oxygen effect on the in situ growth of stoichiometric YBa2Cu3O7 - delta epitaxial films by facing targets 90° off-axis radiofrequency magnetron sputtering

    Science.gov (United States)

    Oya, Gin-ichiro; Diao, Chien Chen; Imai, Syozo; Uzawa, Takaaki; Sawada, Yasuji; Sugai, Tokuko; Nakajima, Kensuke; Yamashita, Tsutomu

    1995-06-01

    (110)- and (103)-oriented almost stoichiometric YBa2Cu3O7-δ (YBCO) films have been grown epitaxially on hot SrTiO3 (110) substrates using a 90° off-axis rf magnetron sputtering technique, for fabrication of vertical sandwich-type YBCO/insulator/YBCO or YBCO/normal metal/YBCO Josephson junctions utilizing the high-quality YBCO films. The YBCO epitaxial films with high transition temperatures Tc of ˜90 K have been deposited in situ only under the conditions of substrate temperatures Ts of ˜650-˜700 °C and oxygen partial pressure PO2 of ˜5×10-3-˜10×10-3 Torr, which are in close proximity to the critical stability/decomposition line for YBa2Cu3O6 in the ordinary Y-Ba-Cu-O phase diagram. Using a quadrupole mass spectrometer, a high density of atomic oxygen has directly been observed to be efficiently produced in the sputter glow discharge under the above optimum conditions of PO2. This atomic oxygen has played a key role in promoting the formation of the perovskite structure and the epitaxial growth of the YBCO films. Furthermore, Shapiro steps have successfully been observed for a Nb-YBCO point-contact junction, which is made by pressing a Nb needle on a surface-etched YBCO epitaxial film, under 525.4 GHz submillimeter-wave irradiation.

  9. Textured surface structures formed using new techniques on transparent conducting Al-doped zinc oxide films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Minami, Tadatsugu; Miyata, Toshihiro; Uozaki, Ryousuke; Sai, Hitoshi; Koida, Takashi

    2016-01-01

    Surface-textured Al-doped ZnO (AZO) films formed using two new techniques based on magnetron sputtering deposition were developed by optimizing the light scattering properties to be suitable for transparent electrode applications in thin-film silicon solar cells. Scrambled egg-like surface-textured AZO films were prepared using a new texture formation technique that post-etched pyramidal surface-textured AZO films prepared under deposition conditions suppressing c-axis orientation. In addition, double surface-textured AZO films were prepared using another new texture formation technique that completely removed, by post-etching, the pyramidal surface-textured AZO films previously prepared onto the initially deposited low resistivity AZO films; simultaneously, the surface of the low resistivity films was slightly etched. However, the obtained very high haze value in the range from the near ultraviolet to visible light in the scrambled egg-like surface-textured AZO films did not contribute significantly to the obtainable photovoltaic properties in the solar cells fabricated using the films. Significant light scattering properties as well as a low sheet resistance could be achieved in the double surface-textured AZO films. In addition, a significant improvement of external quantum efficiency in the range from the near ultraviolet to visible light was achieved in superstrate-type n-i-p μc-Si:H solar cells fabricated using a double surface-textured AZO film prepared under optimized conditions as the transparent electrode. - Highlights: • Double surface-textured AZO films prepared using a new texture formation technique • Extensive light scattering properties with low sheet resistance achieved in the double surface-textured AZO films • Improved external quantum efficiency of μc-Si:H solar cells using a double surface-textured AZO film

  10. Textured surface structures formed using new techniques on transparent conducting Al-doped zinc oxide films prepared by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Minami, Tadatsugu [Optoelectronic Device System R& D Center, Kanazawa Institute of Technology, Nonoichi, Ishikawa 921-8501 (Japan); Miyata, Toshihiro, E-mail: tmiyata@neptune.kanazawa-it.ac.jp [Optoelectronic Device System R& D Center, Kanazawa Institute of Technology, Nonoichi, Ishikawa 921-8501 (Japan); Uozaki, Ryousuke [Optoelectronic Device System R& D Center, Kanazawa Institute of Technology, Nonoichi, Ishikawa 921-8501 (Japan); Sai, Hitoshi; Koida, Takashi [Research Center for Photovoltaics, National Institute of Advanced Industrial Science and Technology (AIST), Tsukuba, Ibaraki 305-8568 (Japan)

    2016-09-01

    Surface-textured Al-doped ZnO (AZO) films formed using two new techniques based on magnetron sputtering deposition were developed by optimizing the light scattering properties to be suitable for transparent electrode applications in thin-film silicon solar cells. Scrambled egg-like surface-textured AZO films were prepared using a new texture formation technique that post-etched pyramidal surface-textured AZO films prepared under deposition conditions suppressing c-axis orientation. In addition, double surface-textured AZO films were prepared using another new texture formation technique that completely removed, by post-etching, the pyramidal surface-textured AZO films previously prepared onto the initially deposited low resistivity AZO films; simultaneously, the surface of the low resistivity films was slightly etched. However, the obtained very high haze value in the range from the near ultraviolet to visible light in the scrambled egg-like surface-textured AZO films did not contribute significantly to the obtainable photovoltaic properties in the solar cells fabricated using the films. Significant light scattering properties as well as a low sheet resistance could be achieved in the double surface-textured AZO films. In addition, a significant improvement of external quantum efficiency in the range from the near ultraviolet to visible light was achieved in superstrate-type n-i-p μc-Si:H solar cells fabricated using a double surface-textured AZO film prepared under optimized conditions as the transparent electrode. - Highlights: • Double surface-textured AZO films prepared using a new texture formation technique • Extensive light scattering properties with low sheet resistance achieved in the double surface-textured AZO films • Improved external quantum efficiency of μc-Si:H solar cells using a double surface-textured AZO film.

  11. Preparation and properties of a drug sustained-release hydrogel film

    International Nuclear Information System (INIS)

    Yue Ling; Yang Zhanshan; Yang Shuqin; Li Qinghua

    2009-01-01

    A hydrogel film of drug sustained-release was prepared to accelerate wound healing. The hydrogel films containing drug or not were prepared by the freezing and thawing process. Their properties such as the physicochemical property and the drug release behavior in vitro were studied. Effect of the freezing and thawing process on antimicrobial efficacy of the gentamicin was evaluated by diffusion method. The results indicate that swelling ratio of the hydrogel films freezed for 4h is 841.21% and their gel fraction, tensile strength and elongation at break is 96.10%, 0.222 MPa and 673.50% respectively. The antimicrobial efficacy of the gentamicin has no change. The hydrogel film contained gentamicin releases the antibiotic to peak during 6 h with the cumulative drug release rate of 59.57%. The drug releases continually up to the 5th day. The drug delivery conforms to Higuchi kinetic equation, and mechanism of the drug release is matrix diffusion. The results show that the hydrogel film prepared by the freezing and thawing process display satisfactory physicochemical properties and can be used as a drug delivery system. (authors)

  12. Microwave dynamics of YBCO bi-epitaxial Josephson structures

    DEFF Research Database (Denmark)

    Constantinian, K. Y.; Ovsyannikov, G. A.; Mashtakov, A. D.

    1996-01-01

    The processes of interaction of microwaves (frequency View the MathML source) with a single high-Tc superconducting YBa2Cu3Ox (YBCO) bi-epitaxial grain-boundary junction and with an array of two junctions connected in series, have been investigated experimentally at temperatures T = 4.2− 77 K......, as well as the subharmonic detector response at weak magnetic fields φ microwave field induced frequency synchronization of two series connected bi-epitaxial YBCO junctions....

  13. Freestanding films of crosslinked gold nanoparticles prepared via layer-by-layer spin-coating

    Science.gov (United States)

    Schlicke, Hendrik; Schröder, Jan H.; Trebbin, Martin; Petrov, Alexey; Ijeh, Michael; Weller, Horst; Vossmeyer, Tobias

    2011-07-01

    A new, extremely efficient method for the fabrication of films comprised of gold nanoparticles (GNPs) crosslinked by organic dithiols is presented in this paper. The method is based on layer-by-layer spin-coating of both components, GNPs and crosslinker, and enables the deposition of films several tens of nanometers in thickness within a few minutes. X-ray diffraction and conductance measurements reveal the proper adjustment concentration of the crosslinker solution of the critical is in order to prevent the destabilization and coalescence of particles. UV/vis spectroscopy, atomic force microscopy, and conductivity measurements indicate that films prepared via layer-by-layer spin-coating are of comparable quality to coatings prepared via laborious layer-by-layer self-assembly using immersion baths. Because spin-coated films are not bound chemically to the substrate, they can be lifted-off by alkaline underetching and transferred onto 3d-electrodes to produce electrically addressable, freely suspended films. Comparative measurements of the sheet resistances indicate that the transfer process does not compromise the film quality.

  14. Freestanding films of crosslinked gold nanoparticles prepared via layer-by-layer spin-coating

    International Nuclear Information System (INIS)

    Schlicke, Hendrik; Schroeder, Jan H; Trebbin, Martin; Petrov, Alexey; Ijeh, Michael; Weller, Horst; Vossmeyer, Tobias

    2011-01-01

    A new, extremely efficient method for the fabrication of films comprised of gold nanoparticles (GNPs) crosslinked by organic dithiols is presented in this paper. The method is based on layer-by-layer spin-coating of both components, GNPs and crosslinker, and enables the deposition of films several tens of nanometers in thickness within a few minutes. X-ray diffraction and conductance measurements reveal the proper adjustment concentration of the crosslinker solution of the critical is in order to prevent the destabilization and coalescence of particles. UV/vis spectroscopy, atomic force microscopy, and conductivity measurements indicate that films prepared via layer-by-layer spin-coating are of comparable quality to coatings prepared via laborious layer-by-layer self-assembly using immersion baths. Because spin-coated films are not bound chemically to the substrate, they can be lifted-off by alkaline underetching and transferred onto 3d-electrodes to produce electrically addressable, freely suspended films. Comparative measurements of the sheet resistances indicate that the transfer process does not compromise the film quality.

  15. Multi-Directional Growth of Aligned Carbon Nanotubes Over Catalyst Film Prepared by Atomic Layer Deposition

    Directory of Open Access Journals (Sweden)

    Zhou Kai

    2010-01-01

    Full Text Available Abstract The structure of vertically aligned carbon nanotubes (CNTs severely depends on the properties of pre-prepared catalyst films. Aiming for the preparation of precisely controlled catalyst film, atomic layer deposition (ALD was employed to deposit uniform Fe2O3 film for the growth of CNT arrays on planar substrate surfaces as well as the curved ones. Iron acetylacetonate and ozone were introduced into the reactor alternately as precursors to realize the formation of catalyst films. By varying the deposition cycles, uniform and smooth Fe2O3 catalyst films with different thicknesses were obtained on Si/SiO2 substrate, which supported the growth of highly oriented few-walled CNT arrays. Utilizing the advantage of ALD process in coating non-planar surfaces, uniform catalyst films can also be successfully deposited onto quartz fibers. Aligned few-walled CNTs can be grafted on the quartz fibers, and they self-organized into a leaf-shaped structure due to the curved surface morphology. The growth of aligned CNTs on non-planar surfaces holds promise in constructing hierarchical CNT architectures in future.

  16. Preparation and optical properties of gold-dispersed BaTiO3 thin films

    Energy Technology Data Exchange (ETDEWEB)

    Kineri, T; Mori, M [TDK Corp., Tokyo (Japan). R and D Center; Kadono, K; Sakaguchi, T; Miya, M; Wakabayashi, H [Osaka National Research Inst., Osaka (Japan); Tsuchiya, T [Science Univ. of Tokyo, Tokyo (Japan). Faculty of Industrial Science and Technology

    1993-12-01

    Recently, metal or semiconductor-doped glasses were widely studied because of their large resonant third-order nonlinearity. These glasses are utilized in an optical information field as all optical logic devices in the future. The gold-doped glass films or thin layers have a large third-order nonlinear susceptibility [chi] and are prepared by r.f. sputtering method, etc. The optical properties, particularly the refractive index or dielectric constant of the matrix, are very important for the optical nonlinearity of these materials. In this study, gold-dispersed BaTiO3 thin films and gold-dispersed SiO2 thin films are prepared using r.f. magnetron sputtering method, and the optical properties of the films are compared. The [chi] of the films are measured and the effect of the matrix of the films on [chi] is investigated. The headings in the paper are: Introduction, Experimental procedure, Results, Discussion, and Conclusion. 13 refs., 9 figs.

  17. Preparation of Nanocellulose Reinforced Chitosan Films, Cross-Linked by Adipic Acid

    Directory of Open Access Journals (Sweden)

    Pouria Falamarzpour

    2017-02-01

    Full Text Available Adipic acid, an abundant and nontoxic compound, was used to dissolve and cross-link chitosan. After the preparation of chitosan films through casting technique, the in situ amidation reaction was performed at 80–100 °C as verified by Fourier transform infrared (FT-IR. The reaction was accompanied by the release of water which was employed to investigate the reaction kinetics. Accordingly, the reaction rate followed the first-order model and Arrhenius equation, and the activation energy was calculated to be 18 kJ/mol. Furthermore, the mechanical properties of the chitosan films were comprehensively studied. First, optimal curing conditions (84 °C, 93 min were introduced through a central composite design. In order to evaluate the effects of adipic acid, the mechanical properties of physically cross-linked (uncured, chemically cross-linked (cured, and uncross-linked (prepared by acetic acid films were compared. The use of adipic acid improved the tensile strength of uncured and chemically cross-linked films more than 60% and 113%, respectively. Finally, the effect of cellulose nanofibrils (CNFs on the mechanical performance of cured films, in the presence of glycerol as a plasticizer, was investigated. The plasticized chitosan films reinforced by 5 wt % CNFs showed superior properties as a promising material for the development of chitosan-based biomaterials.

  18. Properties of pentacene-based films prepared using a heated tungsten mesh

    Energy Technology Data Exchange (ETDEWEB)

    Heya, Akira, E-mail: heya@eng.u-hyogo.ac.jp; Matsuo, Naoto

    2014-11-03

    A heated tungsten (W) mesh, set between a pentacene source and a substrate in a vacuum chamber, was used to prepare a bulk-phase pentacene film and a pentacene-based organic semiconductor film. Since the pentacene molecules come into contact with the heated W mesh before reaching the substrate, their thermal energy is increased prior to deposition. As the mesh temperature was increased from 23 to 1200 °C, the intensity ratio of bulk to thin-film phases increased from 0 to 9.7. Above 1300 °C there is a notable decomposition reaction, the products of which were identified as dihydropentacene, p-distrylbenzene, and 2,2′-dimethyl-1,1′-binaphthalene. These decomposed precursors are expected to provide a potential source of large graphene sheets and graphene nanoribbons. - Highlights: • Organic semiconductor films were prepared using pentacene, H{sub 2} gas, and heated W mesh. • The effect of mesh temperature on film deposition was observed. • Pentacene decomposition above 1300 °C provides graphene precursors. • A method is proposed for controlling the sheet resistance of organic films.

  19. Preparation of Nanocellulose Reinforced Chitosan Films, Cross-Linked by Adipic Acid.

    Science.gov (United States)

    Falamarzpour, Pouria; Behzad, Tayebeh; Zamani, Akram

    2017-02-13

    Adipic acid, an abundant and nontoxic compound, was used to dissolve and cross-link chitosan. After the preparation of chitosan films through casting technique, the in situ amidation reaction was performed at 80-100 °C as verified by Fourier transform infrared (FT-IR). The reaction was accompanied by the release of water which was employed to investigate the reaction kinetics. Accordingly, the reaction rate followed the first-order model and Arrhenius equation, and the activation energy was calculated to be 18 kJ/mol. Furthermore, the mechanical properties of the chitosan films were comprehensively studied. First, optimal curing conditions (84 °C, 93 min) were introduced through a central composite design. In order to evaluate the effects of adipic acid, the mechanical properties of physically cross-linked (uncured), chemically cross-linked (cured), and uncross-linked (prepared by acetic acid) films were compared. The use of adipic acid improved the tensile strength of uncured and chemically cross-linked films more than 60% and 113%, respectively. Finally, the effect of cellulose nanofibrils (CNFs) on the mechanical performance of cured films, in the presence of glycerol as a plasticizer, was investigated. The plasticized chitosan films reinforced by 5 wt % CNFs showed superior properties as a promising material for the development of chitosan-based biomaterials.

  20. Synthesis and Characterization of Nano Scale YBCO

    International Nuclear Information System (INIS)

    Sukirman, E.; Wisnu AA; Yustinus P; Sahidin W, D.; Rina M, Th.

    2009-01-01

    Synthesis and characterization of the nano scale YBCO superconductor have been performed. The nano scale superconductor was synthesized from YBCO system (YBa 2 Cu 3 O 7-X ). Raw materials, namely Y 2 O 3 , BaCO 3 , and Cu°, were balanced and mixed with ethanol using magnetic steering as a churn in a beaker glass. Then, the precursor was calcined at T k = 900°C for 5 hours and repeated it until three times. The resulting precursor was ground by using High Energy Milling (HEM) for t = 0, 30, 50, 70, and 90 hour and hereinafter precursors are successively referred as YKM-00, YKM-30, YKM-50, YKM-70, and YKM-90. The resulting powders phase were characterized by means of x-ray diffraction technique using the Rietveld analysis method. Precursor of YKM-90 was pressed into pellets, and then sintered at various temperatures and periods. The sample phase was then characterized by using the Rietveld analysis method based on the x-ray diffraction data. The crystallites size were calculated using Scherrer formula. Results of analysis indicate that by minimizing crystallites size, period of sinter can be shortened from 10 to 1 hour, resulting crystallite size of D = 925 Å, critical current density of J c = 4 A / cm 2 , and can be grown of about 15 weight % of 211-phase in a matrix of 123-phase. The decrease of crystallite size will generate a change in physical properties dramatically, if the crystallite size of the material, D is smaller or equal to the coherence length of 10 Å. (author)

  1. Effect of Y2O3 Nanoparticles on Critical Current Density of YBa2Cu3O7-x Thin Films

    International Nuclear Information System (INIS)

    Tran, H. D.; Reddy, Sreekantha; Wie, C. H.; Kang, B.; Oh, Sang Jun; Lee, Sung Ik

    2009-01-01

    Introduction of proper impurity into YBa 2 Cu 3 O 7-x (YBCO) thin films is an effective way to enhance its flux-pinning properties. We investigate effect of Y 2 O 3 nanoparticles on the critical current density J c of the YBCO thin films. The Y 2 O 3 nanoparticles were created perpendicular to the film surface (parallel with the c-axis) either between YBCO and substrate or on top of YBCO, YBCO/Y 2 O 3 /LAO or Y 2 O 3 /YBCO/STO, by pulsed laser deposition. The deposition temperature of the YBCO films were varied (780 degree C and 800 degree C) to modify surface morphology of the YBCO films. Surface morphology characterization revealed that the lower deposition temperature of 780 degree C created nano-sized holes on the YBCO film surface which may behave as intrinsic pinning centers, while the higher deposition temperature produced much denser and smoother surface. J-c values of the YBCO films with Y 2 O 3 particles were either remained nearly the same or decreased for the samples in which YBCO is grown at 780 degree C. On the other hand, J-c values were enhanced for the samples in which YBCO is grown at higher temperature of 800 degree C. The difference in the effect of Y 2 O 3 can be explained by the fact that the higher deposition temperature of 800 degree C reduces intrinsic pinning centers and J c is enhanced by introduction of artificial pinning centers in the form of Y 2 O 3 nanoparticles.

  2. Preparation of Ga-doped ZnO films by pulsed dc magnetron sputtering with cylindrical rotating target for thin film solar cell applications

    International Nuclear Information System (INIS)

    Shin, Beom-Ki; Lee, Tae-Il; Park, Ji-Hyeon; Park, Kang-Il; Ahn, Kyung-Jun; Park, Sung-Kee; Lee, Woong; Myoung, Jae-Min

    2011-01-01

    Applicability of Ga-doped ZnO (GZO) films for thin film solar cells (TFSCs) was investigated by preparing GZO films via pulsed dc magnetron sputtering (PDMS) with rotating target. The GZO films showed improved crystallinity and increasing degree of Ga doping with increasing thickness to a limit of 1000 nm. The films also fulfilled requirements for the transparent electrodes of TFSCs in terms of electrical and optical properties. Moreover, the films exhibited good texturing potential based on etching studies with diluted HCl, which yielded an improved light trapping capability without significant degradation in electrical propreties. It is therefore suggested that the surface-textured GZO films prepared via PDMS and etching are promising candidates for indium-free transparent electrodes for TFSCs.

  3. Preparation of Ga-doped ZnO films by pulsed dc magnetron sputtering with cylindrical rotating target for thin film solar cell applications

    Science.gov (United States)

    Shin, Beom-Ki; Lee, Tae-Il; Park, Ji-Hyeon; Park, Kang-Il; Ahn, Kyung-Jun; Park, Sung-Kee; Lee, Woong; Myoung, Jae-Min

    2011-11-01

    Applicability of Ga-doped ZnO (GZO) films for thin film solar cells (TFSCs) was investigated by preparing GZO films via pulsed dc magnetron sputtering (PDMS) with rotating target. The GZO films showed improved crystallinity and increasing degree of Ga doping with increasing thickness to a limit of 1000 nm. The films also fulfilled requirements for the transparent electrodes of TFSCs in terms of electrical and optical properties. Moreover, the films exhibited good texturing potential based on etching studies with diluted HCl, which yielded an improved light trapping capability without significant degradation in electrical propreties. It is therefore suggested that the surface-textured GZO films prepared via PDMS and etching are promising candidates for indium-free transparent electrodes for TFSCs.

  4. Preparation of SiC thin films by ion beam technology and PECVD

    International Nuclear Information System (INIS)

    Chen Changqing; Ren Congxin; Yang Lixin; Yan Jinlong; Zheng Zhihong; Zhou Zuyao; Chen Ping; Liu Xianghuai; Chen Xueliang

    1998-01-01

    The formation of β-SiC buried layers in p-type Si by ion beam methods is reported and a comparison of the results obtained under different experimental conditions is made. The preparation of amorphous SiC thin films by IBED is presented and the enhanced deposition of Xe + is found superior to that of Ar + . The work of synthesizing hydrogenated amorphous SiC films by RIBS and RIBAD is described with a discussion on the dependence of some physical parameters on the partial pressure ratio pCH 4 /pAr. Finally given is a brief introduction to a high quality α-SiC:H film which is prepared by PECVD and can exhibit green luminescence at room temperature

  5. Highly conducting p-type nanocrystalline silicon thin films preparation without additional hydrogen dilution

    Science.gov (United States)

    Patra, Chandralina; Das, Debajyoti

    2018-04-01

    Boron doped nanocrystalline silicon thin film has been successfully prepared at a low substrate temperature (250 °C) in planar inductively coupled RF (13.56 MHz) plasma CVD, without any additional hydrogen dilution. The effect of B2H6 flow rate on structural and electrical properties of the films has been studied. The p-type nc-Si:H films prepared at 5 ≤ B2H6 (sccm) ≤ 20 retains considerable amount of nanocrystallites (˜80 %) with high conductivity ˜101 S cm-1 and dominant crystallographic orientation which has been correlated with the associated increased ultra- nanocrystalline component in the network. Such properties together make the material significantly effective for utilization as p-type emitter layer in heterojunction nc-Si solar cells.

  6. Langmuir-Blodgett films prepared from pre-formed cholestanic liquid-crystalline polymers

    Energy Technology Data Exchange (ETDEWEB)

    Tundo, P.; Hodge, P.; Valli, L.; Davis, F. (Venice Univ. (Italy). Dip. di Scienze Ambientali Lecce Univ. (Italy). Dip. di Scienza dei Materiali Manchester Univ. (United Kingdom). Dep. of Chemistry)

    1992-01-01

    A series of alternating copolymers of maleic anhydride and a-olefins functionalized through different alkyl chains with cholestanic groups were synthetised and derivatives prepared by reactions of the anhydride residues with methanol, water, dimethylamine and morpholine, respectively. The same starting functionalized a-olefins were used to prepare other suitable compounds in order to correlate the features of the liquid-crystalline behaviour of the mesogenic cholestanic group with the stability of the forthcoming polymeric or not polymeric Langmuir-Blodgett (LB) films. For some copolymers surface pressure against area per molecule isotherms are reported. In some multilayer (LB) films, the spacings between the layers were determined by the detection of BRAGG peaks by X-ray diffraction. The (LB) films of these polymers are closed packed, owing to either the polymeric skeleton or liquid-crystalline interaction.

  7. Orodispersible films in individualized pharmacotherapy : The development of a formulation for pharmacy preparations

    NARCIS (Netherlands)

    Visser, Caroline; Woerdenbag, Herman J.; Crediet, Stefan; Gerrits, Edwin; Lesschen, Marjan A.; Hinrichs, Wouter L.J.; Breitkreutz, Jörg; Frijlink, Henderik W.

    2015-01-01

    Orodispersible films (ODFs) are promising drug delivery systems for customized small scale pharmacy preparations. The aim of the present study was to develop a versatile casting solution suitable for the extemporaneous production of ODFs to which active pharmaceutical ingredients (APIs) can be

  8. Energy barriers in nanometer sized magnetic islands prepared from alloyed and multilayered Co/Pt films

    NARCIS (Netherlands)

    Abelmann, Leon; de Vries, Jeroen; Bolhuis, Thijs; Kikuchi, Nobuaki

    2014-01-01

    By means of Anomalous Hall Effect measurements, we investigated the thermal switching field distribution of individual magnetic thin film circular elements with out-of-plane easy axis in a temperature range from 10K to 300K. We compared this behavior for elements prepared from either Co80Pt20

  9. Facile preparation of optically transparent and hydrophobic cellulose nanofibril composite films

    Science.gov (United States)

    Yan Qing; Zhiyong Cai; Yiqiang Wu; Chunhua Yao; Qinglin Wu; Xianjun Li

    2015-01-01

    Cellulose nanofibril (CNF) and epoxy nanocomposites with high visible light transmittance and low watersensitivity were manufactured by laminating thin layers of epoxy resin onto CNF films prepared through,pressurized filtration in combination with oven drying. Scanning Electron Microscopy (SEM) studiessuggest that the resin component bonded to the CNF substrate well....

  10. Controlling morphology, mesoporosity, crystallinity, and photocatalytic activity of ordered mesoporous TiO{sub 2} films prepared at low temperature

    Energy Technology Data Exchange (ETDEWEB)

    Elgh, Björn; Yuan, Ning; Palmqvist, Anders E. C. [Applied Surface Chemistry, Department of Chemical and Biological Engineering, Chalmers University of Technology, SE 412 96 Göteborg (Sweden); Cho, Hae Sung; Terasaki, Osamu [Graduate School of EEWS (WCU), KAIST, Daejeon 305-701 (Korea, Republic of); Magerl, David; Philipp, Martine; Müller-Buschbaum, Peter [Lehrstuhl für Funktionelle Materialien, Physik-Department, Technische Universität München, 85748 Garching (Germany); Roth, Stephan V. [DESY, Notkestrasse 85, 22603 Hamburg (Germany); Yoon, Kyung Byung [Department of Chemistry, Sogang University, Seoul 121-742 (Korea, Republic of)

    2014-11-01

    Partly ordered mesoporous titania films with anatase crystallites incorporated into the pore walls were prepared at low temperature by spin-coating a microemulsion-based reaction solution. The effect of relative humidity employed during aging of the prepared films was studied using SEM, TEM, and grazing incidence small angle X-ray scattering to evaluate the mesoscopic order, porosity, and crystallinity of the films. The study shows unambiguously that crystal growth occurs mainly during storage of the films and proceeds at room temperature largely depending on relative humidity. Porosity, pore size, mesoscopic order, crystallinity, and photocatalytic activity of the films increased with relative humidity up to an optimum around 75%.

  11. Preparation and characterization of gellan gum/glucosamine/clioquinol film as oral cancer treatment patch.

    Science.gov (United States)

    Tsai, Wanchi; Tsai, Huifang; Wong, Yinuan; Hong, Juiyen; Chang, Shwujen; Lee, Mingwei

    2018-01-01

    To administer cancer drugs with improved convenience to patients and to enhance the bioavailability of cancer drugs for oral cancer therapy, this study prepared gellan gum/glucosamine/clioquinol (GG/GS/CQ) film as the oral cancer treatment patch. GG/GS/CQ film fabricated through the EDC-mediated coupling reactions (GG/GS/CQ/EDC film). The film of the physicochemical properties and drug release kinetics were studied. The effectiveness of GG/GS/CQ/EDC film as oral cancer treatment patch were evaluated with the animal model. The results confirmed that CQ can be incorporated via EDC-mediated covalent conjugation to gellan gum/glucosamine. Mechanical testing revealed that the maximum tensile strength and elongation percentage at break were 1.91kgf/mm 2 and 5.01% for GG/GS/CQ/EDC film. After a drug release experiment lasting 45days, 86.8% of CQ was released from GG/GS/CQ/EDC film. The Huguchi model fit the GG/GS/CQ/EDC drug release data with high correlation coefficients (R 2 =0.9994, respectively). The effect of the CQ dose on oral cancer cells (OC-2) was tested, and the IC 50 of CQ alone and CQ with 10μM CuCl 2 were 9.59 and 2.22μM, respectively. The animal testing indicated that GG/GS/CQ/EDC film was decreased epidermal growth factor receptor (EGFR) expression and suppress tumor progression. These findings provide insights into a possible use for GG/GS/CQ/EDC film for oral ca in clinical practice. The GG/GS/CQ/EDC film is suitable as the dressing for use in the treatment of early-stage cancer or as wound care after surgery in late-stage of oral cancer treatment. Copyright © 2017 Elsevier B.V. All rights reserved.

  12. Pathways to prepare perfect Co_4N thin films

    International Nuclear Information System (INIS)

    Gupta, Rachana; Pandey, Nidhi; Gupta, Mukul

    2016-01-01

    Magnetic nitrides of 3d transition metals (M = Fe,Co,Ni) are interesting materials for applications in magnetic devices. Controlled nitridation of magnetic metals for small N content (∼ 10-20 at.%) is sufficient to provide them high mechanical strength and superior chemical stability as compared to pure metals. At the same time tetra metal nitrides (M_4N) are known to posses a saturation magnetization (Ms) which is even higher than the pure metal. In M_4N enhanced magnetic moment is caused by a volume expansion (compared to a hypothetical fcc metal). All M_4N share a common fcc structure, in which metal atoms are arranged in the fcc positions and N atoms occupy the body centered positions. Such incorporation of N atoms results in an expansion of the fcc lattice. Theoretical studies suggest that such volume expansion enhances the itinerary of conduction band electrons and results in spreading of bandwidth of 3d electrons thereby suppression of exchange splitting leading to a larger (than pure metal) Ms. We did polarized neutron reflectivity (PNR) to measure Ms of Co_4N thin films. We found that as LP increases, Ms also increases. Our results clearly show that the Co_4N phase is formed at much lower Ts and when deposited at high Ts, N atoms diffuse out leaving behind pure fcc Co phase which seems to have been mistaken for Co_4N phase in earlier works

  13. Water-based preparation of spider silk films as drug delivery matrices.

    Science.gov (United States)

    Agostini, Elisa; Winter, Gerhard; Engert, Julia

    2015-09-10

    The main focus of this work was to obtain a drug delivery matrix characterized by biocompatibility, water insolubility and good mechanical properties. Moreover the preparation process has to be compatible with protein encapsulation and the obtained matrix should be able to sustain release a model protein. Spider silk proteins represent exceptional natural polymers due to their mechanical properties in combination with biocompatibility. As both hydrophobic and slowly biodegrading biopolymers, recombinant spider silk proteins fulfill the required properties for a drug delivery system. In this work, we present the preparation of eADF4(C16) films as drug delivery matrices without the use of any organic solvent. Water-based spider silk films were characterized in terms of protein secondary structure, thermal stability, zeta-potential, solubility, mechanical properties, and water absorption and desorption. Additionally, this study includes an evaluation of their application as a drug delivery system for both small molecular weight drugs and high molecular weight molecules such as proteins. Our investigation focused on possible improvements in the film's mechanical properties including plasticizers in the film matrix. Furthermore, different film designs were prepared, such as: monolayer, coated monolayer, multilayer (sandwich), and coated multilayer. The release of the model protein BSA from these new systems was studied. Results indicated that spider silk films are a promising protein drug delivery matrix, capable of releasing the model protein over 90 days with a release profile close to zero order kinetic. Such films could be used for several pharmaceutical and medical purposes, especially when mechanical strength of a drug eluting matrix is of high importance. Copyright © 2015 Elsevier B.V. All rights reserved.

  14. Preparation and pharmaceutical evaluation of glibenclamide slow release mucoadhesive buccal film

    Science.gov (United States)

    Bahri-Najafi, R.; Tavakoli, N.; Senemar, M.; Peikanpour, M.

    2014-01-01

    Buccal mucoadhesive systems among novel drug delivery systems have attracted great attention in recent years due to their ability to adhere and remain on the oral mucosa and to release their drug content gradually. Buccal mucoadhesive films can improve the drug therapeutic effect by enhancement of drug absorption through oral mucosa increasing the drug bioavailability via reducing the hepatic first pass effect. The aim of the current study was to formulate the drug as buccal bioadhesive film, which releases the drug at sufficient concentration with a sustain manner reducing the frequency of the dosage form administration. One of the advantagees of this formulation is better patient compliances due to the ease of administration with no water to swallow the product. The mucoadhesive films of glibenclamide were prepared using hydroxypropyl methylcellulose (HPMC) K4M, K15M and Eudragit RL100 polymers and propylene glycol as plasticizer and co-solvent. Films were prepared using solvent casting method, and were evaluated with regard to drug content, thickness, weight variations, swelling index, tensile strength, ex vivo adhesion force and percentage of in vitro drug release. Films with high concentrations of HPMC K4M and K15M did not have favorable appearance and uniformity. The formulations prepared from Eudragit were transparent, uniform, flexible, and without bubble. The highest and the lowest percentages of swelling were observed for the films containing HPMC K15M and Eudragit RL100, respectively. Films made of HPMC K15M had adhesion force higher than those containing Eudragit RL100. Formulations with Eudragit RL100 showed the highest mean dissolution time (MDT). Drug release kinetics of all formulations followed Higuchi's model and the mechanism of diffusion was considered non-Fickian type. It was concluded that formulations containing Eudragit RL100 were more favorable than others with regard to uniformity, flexibility, rate and percentage of drug release. PMID

  15. Preparation of S-sulfo albumin film and its cell adhesive property

    International Nuclear Information System (INIS)

    Yamazoe, Hironori; Yamauchi, Kiyoshi; Tanabe, Toshizumi

    2009-01-01

    Recently, large-scale production of the pharmaceutical grade recombinant human serum albumin was achieved, and several clinical trials have proved its safety and efficacy. Albumin is thought to be a candidate for a safe biopolymer sources for application to biomaterials. In this study, we treated albumin with sodium sulfite and sodium tetrathionate to give S-sulfo albumin, which was found to loose native albumin structure by CD spectra analysis and dye-binding assay. A water-insoluble S-sulfo albumin films were prepared by drying S-sulfo albumin solution and subsequent reformation of disulfide bonds by the oxidation with iodine. Ultimate strength, ultimate elongation and Young's modulus of S-sulfo albumin film prepared at room temperature were 3.3 ± 0.4 MPa, 30.8 ± 3.2% and 40.8 ± 3.3 MPa before oxidative treatment and changed to 13.8 ± 4.2 MPa, 5.6 ± 2.8% and 401.7 ± 15.3 MPa after oxidative treatment. When the film was prepared at 60 deg. C, similar tendency was observed. Thus, the disulfide bonds formation between albumin molecules by oxidative treatment converted the film stronger and stiffer. Cell adhesion and proliferation on the films were evaluated using mouse L929 fibroblast cells. Cell adhesion largely depended on the albumin structure; that is, cells did not attach to native albumin coated surfaces, while cell adhesion and proliferation occurred on the S-sulfo albumin films which lost their native albumin structure. Eighty percent of seeded cells were adhered on S-sulfo albumin films and proliferated well in a similar manner to those on the conventional culture dish. Our results indicate that S-sulfo albumin is a favorable cell culture substrate.

  16. Pulsed laser deposition of YBCO coated conductor using Y2O3 as the seed and cap layer

    International Nuclear Information System (INIS)

    Barnes, P N; Nekkanti, R M; Haugan, T J; Campbell, T A; Yust, N A; Evans, J M

    2004-01-01

    Although a variety of buffer layers have been routinely reported, a standard architecture commonly used for the Y Ba 2 Cu 3 O 7-x (YBCO) coated conductor is Y BCO/CeO 2 /Y SZ/CeO 2 /substrate or Y BCO/CeO 2 /Y SZ/Y 2 O 3 /substrate where ceria is typically the cap layer. CeO 2 is generally used as only a seed (or cap layer) since cracking within the film occurs in thicker CeO 2 layers due to the stress of lattice mismatching. Y 2 O 3 has been proposed as a seed and as a cap layer but usually not for both in a given architecture, especially with all layers deposited in situ. Yttrium oxide films grown on nickel by electron beam evaporation processes were found to be dense and crack free with good epitaxy. In this report, pulsed laser deposition (PLD) of Y 2 O 3 is given where Y 2 O 3 serves as both the seed and cap layer in the YBCO architecture. A comparison to PLD CeO 2 is provided. Deposited layers of the YBCO coated conductor are also grown by laser ablation. Initial deposition resulted in specimens on textured Ni substrates with current densities of more than 1 MA cm -2 at 77 K, self-field

  17. Preparation and characterization of thin organosilicon films deposited on SPR chip

    Energy Technology Data Exchange (ETDEWEB)

    Szunerits, Sabine [Laboratoire d' Electrochimie et de Physicochimie des Materiaux et des Interfaces (LEPMI), CNRS-INPG-UJF, 1130 rue de la piscine, BP 75, 38402 St. Martin d' Heres Cedex (France)], E-mail: sabine.szunerits@lepmi.inpg.fr; Rich, Sami Abou [Laboratoire de Genie des Procedes d' Interaction de Fluides Reactifs-Materiaux U.S.T.L., Cite Scientifique, 59655 Villeneuve d' Ascq (France); Coffinier, Yannick [Institut de Recherche Interdisciplinaire (IRI), FRE CNRS 2963, Institut d' lectronique, de Microelectronique et de Nanotechnologie (IEMN), UMR CNRS-8520, Cite Scientifique, Avenue Poincare, BP 60069, 59652 Villeneuve d' Ascq (France); Languille, Marie-Angelique [Unite de Catalyse et de Chimie du Solide, UCCS UMR CNRS-8181, Universite des Sciences et Technologies de Lille, Bat. C3, 59655 Villeneuve d' Ascq (France); Supiot, Philippe [Laboratoire de Genie des Procedes d' Interaction de Fluides Reactifs-Materiaux U.S.T.L., Cite Scientifique, 59655 Villeneuve d' Ascq (France); Boukherroub, Rabah [Institut de Recherche Interdisciplinaire (IRI), FRE CNRS 2963, Institut d' lectronique, de Microelectronique et de Nanotechnologie (IEMN), UMR CNRS-8520, Cite Scientifique, Avenue Poincare, BP 60069, 59652 Villeneuve d' Ascq (France)], E-mail: rabah.boukherroub@iemn.univ-lille1.fr

    2008-04-20

    The paper reports on the preparation and characterization of organosilicon thin polymer films deposited on glass slides coated with 5 nm adhesion layer of titanium and 50 nm of gold. The polymer was obtained by the decomposition of 1,1,3,3-tetramethyldisiloxane precursor (TMDSO) premixed with oxygen induced in a N{sub 2} plasma afterglow using remote plasma-enhanced chemical vapor deposition (PECVD) technique. The film thickness was controlled by laser interferometry and was 9 nm. The chemical stability of the gold substrate coated with the organosilicon polymer film (p-TMDSO) was studied in different acidic and basic solutions (pH 1-14). While the gold/polymer interface showed a high stability in acidic media, the film was almost completely removed in basic solutions. The resulting surfaces were characterized using atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), water contact angle measurements, cyclic voltammetry, and surface plasmon resonance (SPR)

  18. Preparation and characterization of high-Tc superconducting thin films with high critical current densities

    International Nuclear Information System (INIS)

    Vase, P.

    1991-08-01

    The project was carried out in relation to possible cable and electronics applications of high-T c materials. Laser ablation was used as the deposition technique because of its stoichiometry conservation. Films were made in the YBa 2 Cu 3 O 7 compound due to its relatively simple stoichiometry compared to other High-T c compounds. Much attention was paid to the critical current density. A very high critical current density was reached. By using texture analysis by X-ray diffraction, it was found that films with high critical current densities were epitaxial, while films with low critical current densities contained several crystalline orientations. Four techniques for patterning the films were used - photo lithography and wet etch, laser ablation lithography, laser writing and electron beam lithography and ion milling. Sub-micron patterning has been demonstrated without degradation of the superconducting properties. The achieved patterning resolution is sufficient for preparation of many superconducting components. (AB)

  19. Preparation of polyvinyl alcohol graphene oxide phosphonate film and research of thermal stability and mechanical properties.

    Science.gov (United States)

    Li, Jihui; Song, Yunna; Ma, Zheng; Li, Ning; Niu, Shuai; Li, Yongshen

    2018-05-01

    In this article, flake graphite, nitric acid, peroxyacetic acid and phosphoric acid are used to prepare graphene oxide phosphonic and phosphinic acids (GOPAs), and GOPAs and polyvinyl alcohol (PVA) are used to synthesize polyvinyl alcohol graphene oxide phosphonate and phosphinate (PVAGOPs) in the case of faint acidity and ultrasound irradiation, and PVAGOPs are used to fabricate PVAGOPs film, and the structure and morphology of GOPAs, PVAGOPs and PVAGOPs film are characterized, and the thermal stability and mechanical properties of PVAGOPs film are investigated. Based on these, it has been proved that GOPAs consist of graphene oxide phosphonic acid and graphene oxide phosphinic acid, and there are CP covalent bonds between them, and PVAGOPs are composed of GOPAs and PVA, and there are six-member lactone rings between GOPAs and PVA, and the thermal stability and mechanical properties of PVAGOPs film are improved effectively. Copyright © 2018 Elsevier B.V. All rights reserved.

  20. Super-hydrophobic nickel films with micro-nano hierarchical structure prepared by electrodeposition

    International Nuclear Information System (INIS)

    Hang Tao; Hu Anmin; Ling Huiqin; Li Ming; Mao Dali

    2010-01-01

    Super-hydrophobic nickel films were prepared by a simple and low cost electrodepositing method. The surface morphologies of the films characterized by scanning electronic microscope exhibit hierarchical structure with micro-nanocones array, which can be responsible for their super-hydrophobic characteristic (water contact angle over 150 o ) without chemical modification. The wettability of the film can be varied from super-hydrophobic (water contact angle 154 o ) to relatively hydrophilic (water contact angle 87 o ) by controlling the size of the micro-nanocones. The mechanism of the hydrophobic characteristic of nickel films with this unique structure was illustrated by several models. Such micro-nanostructure and its special wettability are expected to be applied in the practical industry.

  1. Structural and optical characteristics of SnS thin film prepared by SILAR

    Directory of Open Access Journals (Sweden)

    Mukherjee A.

    2015-12-01

    Full Text Available SnS thin films were grown on glass substrates by a simple route named successive ion layer adsorption and reaction (SILAR method. The films were prepared using tin chloride as tin (Sn source and ammonium sulfide as sulphur (S source. The structural, optical and morphological study was done using XRD, FESEM, FT-IR and UV-Vis spectrophotometer. XRD measurement confirmed the presence of orthorhombic phase. Particle size estimated from XRD was about 45 nm which fitted well with the FESEM measurement. The value of band gap was about 1.63 eV indicating that SnS can be used as an important material for thin film solar cells. The surface morphology showed a smooth, homogenous film over the substrate. Characteristic stretching vibration mode of SnS was observed in the absorption band of FT-IR spectrum. The electrical activation energy was about 0.306 eV.

  2. Preparation and characterization of thin organosilicon films deposited on SPR chip

    International Nuclear Information System (INIS)

    Szunerits, Sabine; Rich, Sami Abou; Coffinier, Yannick; Languille, Marie-Angelique; Supiot, Philippe; Boukherroub, Rabah

    2008-01-01

    The paper reports on the preparation and characterization of organosilicon thin polymer films deposited on glass slides coated with 5 nm adhesion layer of titanium and 50 nm of gold. The polymer was obtained by the decomposition of 1,1,3,3-tetramethyldisiloxane precursor (TMDSO) premixed with oxygen induced in a N 2 plasma afterglow using remote plasma-enhanced chemical vapor deposition (PECVD) technique. The film thickness was controlled by laser interferometry and was 9 nm. The chemical stability of the gold substrate coated with the organosilicon polymer film (p-TMDSO) was studied in different acidic and basic solutions (pH 1-14). While the gold/polymer interface showed a high stability in acidic media, the film was almost completely removed in basic solutions. The resulting surfaces were characterized using atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), water contact angle measurements, cyclic voltammetry, and surface plasmon resonance (SPR)

  3. Preparation of tris(8-hydroxyquinolinato)aluminum thin films by sputtering deposition using powder and pressed powder targets

    Science.gov (United States)

    Kawasaki, Hiroharu; Ohshima, Tamiko; Yagyu, Yoshihito; Ihara, Takeshi; Tanaka, Rei; Suda, Yoshiaki

    2017-06-01

    Tris(8-hydroxyquinolinato)aluminum (Alq3) thin films, for use in organic electroluminescence displays, were prepared by a sputtering deposition method using powder and pressed powder targets. Experimental results suggest that Alq3 thin films can be prepared using powder and pressed powder targets, although the films were amorphous. The surface color of the target after deposition became dark brown, and the Fourier transform infrared spectroscopy spectrum changed when using a pressed powder target. The deposition rate of the film using a powder target was higher than that using a pressed powder target. That may be because the electron and ion densities of the plasma generated using the powder target are higher than those when using pressed powder targets under the same deposition conditions. The properties of a thin film prepared using a powder target were almost the same as those of a film prepared using a pressed powder target.

  4. Preparation and characterization of thin-film Pd–Ag supported membranes for high-temperature applications

    NARCIS (Netherlands)

    Fernandez Gesalaga, Ekain; Coenen, Kai; Helmi Siasi Farimani, Arash; Melendez, J.; Zuniga, Jon; Pacheco Tanaka, David Alfredo; van Sint Annaland, Martin; Gallucci, Fausto

    2015-01-01

    This paper reports the preparation, characterization and stability tests of thin-film Pd–Ag supported membranes for high-temperature fluidized bed membrane reactor applications. Various thin-film supported membranes have been prepared by simultaneous Pd–Ag electroless plating and have been initially

  5. Poly(vinyl alcohol) composite films with high percent elongation prepared from amylose-fatty ammonium salt inclusion complexes

    Science.gov (United States)

    Amylose inclusion complexes prepared from cationic fatty ammonium salts and jet-cooked high amylose starch were combined with poly(vinyl alcohol) (PVOH) to form glycerol-plasticized films. Their tensile properties were compared with similar films prepared previously with analogous anionic fatty acid...

  6. Electroplated Fe-Co-Ni films prepared from deep-eutectic-solvent-based plating baths

    Directory of Open Access Journals (Sweden)

    Takeshi Yanai

    2016-05-01

    Full Text Available We fabricated soft magnetic films from DES-based plating baths, and investigated magnetic properties of the plated films. The plating baths were obtained by stirring the mixture of choline chloride, ethylene glycol, FeCl2 ⋅ 4H2O, NiCl2 ⋅ 6H2O and CoCl2 ⋅ 6H2O. The composition of the electroplated film depended on the amount of the reagent in the plating bath, and we consequently obtained the films with various composition. The current efficiency of the plating process shows high values (> 88 % in the wide composition range. The soft magnetic films with low coercivity were obtained at the Fe compositions of ≈ 30 at.% and > 80 at.%, and we found that low coercivity could be realized by the control of the film composition. We also found that the Fe-rich films prepared from DES-based plating bath have some advantages as a soft magnetic phase for a nanocomposite magnet due to their high saturation magnetization and very fine crystal structure.

  7. Preparation of n-type semiconductor SnO2 thin films

    International Nuclear Information System (INIS)

    Rahal, Achour; Benramache, Said; Benhaoua, Boubaker

    2013-01-01

    We studied fluorine-doped tin oxide on a glass substrate at 350°C using an ultrasonic spray technique. Tin (II) chloride dehydrate, ammonium fluoride dehydrate, ethanol and NaOH were used as the starting material, dopant source, solvent and stabilizer, respectively. The SnO 2 : F thin films were deposited at 350°C and a pending time of 60 and 90 s. The as-grown films exhibit a hexagonal wurtzite structure and have (101) orientation. The G = 31.82 nm value of the grain size is attained from SnO 2 : F film grown at 90 s, and the transmittance is greater than 80% in the visible region. The optical gap energy is found to measure 4.05 eV for the film prepared at 90 s, and the increase in the electrical conductivity of the film with the temperature of the sample is up to a maximum value of 265.58 (Ω·cm) −1 , with the maximum activation energy value of the films being found to measure 22.85 meV, indicating that the films exhibit an n-type semiconducting nature. (semiconductor materials)

  8. Niobium Pentoxide thin films employ simple colloidal suspension at low preparation temperature

    Directory of Open Access Journals (Sweden)

    Abood M. K.

    2017-01-01

    Full Text Available In this work a nano-colloidal suspension is used to prepare Nb2O5 thin films. The effect of different substrates on structural properties of niobium pentoxide thin film deposited by spin coating technique on silicon and quartz substrates are presented. We observed that the obtained structure is monocline in both substrates. The diffraction peaks in both substrates ensured the successful formation of Nb2O5 thin films with a clear polymorphous structure. However, the structure became more crystalline with additional distinguished peaks on silicon substrate comparing to quartz substrate. The extracted structural parameters from X-Ray diffraction show that the grain size of the thin films on quartz is smaller than silicon with the values of 16.47 nm and 20.98 nm respectively. The stress measurement records the values of 0.19 and 0.00719 for the thin films deposited on silicon and quartz substrates respectively. Effects of film thickness depicted increment in the absorbance and reduction in the band gap. Energy gaps of 2.7, 2.58 and, 2.5 eV are measured as a result of increasing the film thicknesses of 325, 420 and 450 nm respectively.

  9. Zinc oxide films impurified with Ti and prepared by the Sol-gel method

    International Nuclear Information System (INIS)

    Tirado G, S.; Cazares R, J.M.; Maldonado, A.

    2006-01-01

    Titanium-doped zinc oxide thin films have been prepared on silicon substrate using the Sol-Gel technique. The structural, morphology, electrical and optical properties of such thin films were studied as a function of titanium concentration (0.5, 1 and 1.5 %) and the thin films thickness. Zinc acetate dihydrate and titanium (VI)-oxy acetylacetonate were used as precursor materials, using 2-methoxyethanol and monoethanolamine as via. The X-ray diffraction spectra show polycrystalline films in all the cases. It can see for all the thin films a preferential growth along the (002) planes where the titanium concentration and also the thin films thickness play an important rule. No structural changes are observed at all. The surface morphology studied shows as the grain size decreases when thin thickness is increases. For titanium concentration of 0.5, 1 and 1.5 % values the grains size increase also. The thin films thickness for titanium concentration of 1.5 % was 500 nm (4v), 400 nm (3v), 180 nm (2v) and 130 nm (1v), values obtained from cross-section micrographs. Highly resistive samples are obtained for substrate soda-lime even showing high transmittance. Better physical properties are required for gas sensors or semitransparent electrodes and other possible applications. (Author)

  10. Preparation and evaluation of periodontal films based on polyelectrolyte complex formation.

    Science.gov (United States)

    Kassem, Abeer Ahmed; Ismail, Fatma Ahmed; Naggar, Viviane Fahim; Aboulmagd, Elsayed

    2015-05-01

    Local intra-pocket drug delivery devices can provide an effective concentration of the antimicrobial agent at the site of action with avoidance of undesirable side effects. This study explored the application of chitosan-alginate and chitosan-pectin polyelectrolyte complex (PEC) films as drug release regulators for tetracycline HCl (Tc) to treat periodontal pockets. Periodontal films with 1:1 Tc:PEC ratio were prepared using 1:1 chitosan (Ch) to sodium alginate (A) or 1:3 Ch to pectin (P). The scanning electron microscope showed acceptable film appearance and differential scanning calorimetry analysis confirmed complex formation. The in vitro release studies for both films showed a burst drug release, followed by prolonged release for 70 h. A prolonged antibacterial activity of both films against Staphylococcus aureus ATCC 6538 was observed over a period of 21 days. Aging studies indicated that the five months storage period in freezer did not significantly influence the drug release profile or the antibacterial activity of both films. Clinical evaluation showed a significant reduction in pocket depth (p < 0.0001) to their normal values (≤3 mm). PEC films could be exploited as a prolonged drug release devices for treatment of periodontal pockets.

  11. Preparation and Analysis of Platinum Thin Films for High Temperature Sensor Applications

    Science.gov (United States)

    Wrbanek, John D.; Laster, Kimala L. H.

    2005-01-01

    A study has been made of platinum thin films for application as high temperature resistive sensors. To support NASA Glenn Research Center s high temperature thin film sensor effort, a magnetron sputtering system was installed recently in the GRC Microsystems Fabrication Clean Room Facility. Several samples of platinum films were prepared using various system parameters to establish run conditions. These films were characterized with the intended application of being used as resistive sensing elements, either for temperature or strain measurement. The resistances of several patterned sensors were monitored to document the effect of changes in parameters of deposition and annealing. The parameters were optimized for uniformity and intrinsic strain. The evaporation of platinum via oxidation during annealing over 900 C was documented, and a model for the process developed. The film adhesion was explored on films annealed to 1000 C with various bondcoats on fused quartz and alumina. From this compiled data, a list of optimal parameters and characteristics determined for patterned platinum thin films is given.

  12. Preparation and properties of Starch-g-PLA/poly(vinyl alcohol) composite film.

    Science.gov (United States)

    Hu, Yingmo; Wang, Qingling; Tang, Mingru

    2013-07-25

    Starch/lactic acid graft copolymer (Starch-g-PLA) was prepared by the in situ copolymerization of starch grafted with lactic acid catalyzed with sodium hydroxide, and then mixed with poly(vinyl alcohol) (PVA) to get composite films. The structures of the graft copolymer and composite films were characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The mechanical properties, water resistance, and thermal stability were also investigated. It was found that the compatibility of Starch-g-PLA and PVA was better than that of starch and PVA in the composite films. The tensile strength and elongation at break of the Starch-g-PLA/PVA composite film increased by 69.15% and 84.22%, respectively, while the water absorption decreased by 50.39%, which overcame the shortcomings of hydrophilicity and poor mechanical properties of Starch/PVA film. Thermogravimetric analysis (TGA) also showed that the thermal stability of Starch-g-PLA/PVA film was improved compared with Starch/PVA film. Copyright © 2013 Elsevier Ltd. All rights reserved.

  13. Preparation and antifouling property of polyurethane film modified by chondroitin sulfate

    Science.gov (United States)

    Yuan, Huihui; Xue, Jing; Qian, Bin; Chen, Huaying; Zhu, Yonggang; Lan, Minbo

    2017-02-01

    An antifouling polyurethane film modified by chondroitin sulfate (PU-CS) was prepared by chemical grafting with N-Boc-1,3-propanediamine as a spacer. The different mass fraction of N-Boc-1,3-propanediamine was investigated to obtain PU-CS films with different CS grafting density. The surface properties of PU-CS films were comprehensively characterized. Proteins adsorption and glycosaminoglycans adhesion on films were evaluated. Moreover, inorganic salt deposition on film with highest CS grafting density (3.70 μg/cm2) was briefly investigated. The results showed that the increase of CS grafting density improved not only the hydrophilicity but the antifouling performance of films. The best antifouling film reduced the adsorption of fibrinogen (BFG), human serum albumin (HSA) and lysozyme (LYS) by 81.4%, 95.0% and 76.5%, respectively, and the adhesion of chondroitin (CS), heparin (HP) and hyaluronic acid (HA) by 70.6%, 87.4% and 81.3%, respectively. In addition, the co-adsorption of proteins and glycosaminoglycans reduced up to 86.9% and 75.5%, respectively. Changes in inorganic salt deposition after co-adsorption of proteins and glycosaminoglycans on PU-CS(3) suggested that the proteins promoted the inorganic salt deposition, while glycosaminoglycans inhibited the crystal growth. The negatively charged polysaccharides might promote the generation of smaller crystals which could be conducive to provide theoretical and practical guide to develop novel urinary stents with significant anti-encrustation properties.

  14. Preparation and property of UV-curable polyurethane acrylate film filled with cationic surfactant treated graphene

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Jinghong; Cai, Xia; Shen, Fenglei, E-mail: shenfenglei@suda.edu.cn

    2016-08-30

    Highlights: • The non-covalent modification of graphene maintains the intrinsic structure of graphene compared with the covalent functionalization of graphene. • The initial degradation temperature of nanocomposite film increases by 57 °C which is much higher than that of PUA nanocomposite previously reported. • The nanocomposite film exhibits improved dielectric property and electrical conductivity. • The outstanding performance of CTAB-G/PUA films will open up enormous opportunities for applications in various regions such as high temperature or electrical field. - Abstract: The preparation of nanocomposite films composed of UV-curable polyurethane acrylate (PUA) and modified graphene were demonstrated in this paper. Cetyl trimethyl ammonium bromide modified graphene (CTAB-G) was prepared via intercalation of cationic surfactant and subsequently incorporated into PUA by UV curing technology. Fourier transform infrared spectra, wide-angle X-ray diffraction, scanning electron microscopy and transmission electron microscopy were used to characterize the structure and morphology of CTAB-G, as well as CTAB-G/PUA nanocomposite films. The results revealed that the CTAB-G sheets were layer-by-layer structure and dispersed uniformly in PUA matrix. Thermal gravimetric analysis showed that the thermal stabilities of UV-curable PUA nanocomposite films in this work were much higher than that of PUA nanocomposites previously reported. Dynamic mechanical analysis indicated that the dynamic mechanical properties of nanocomposite films were greatly enhanced in the presence of modified graphene sheets. In addition, the CTAB-G/PUA nanocomposite films exhibited improved dielectric properties and electrical conductivities compared with the pure PUA.

  15. Tuneable light-emitting carbon-dot/polymer flexible films prepared through one-pot synthesis

    Science.gov (United States)

    Bhunia, Susanta Kumar; Nandi, Sukhendu; Shikler, Rafi; Jelinek, Raz

    2016-02-01

    Development of efficient, inexpensive, and environmentally-friendly light emitters, particularly devices that produce white light, have drawn intense interest due to diverse applications in the lighting industry, photonics, solar energy, and others. We present a simple strategy for the fabrication of flexible transparent films exhibiting tuneable light emission through one-pot synthesis of polymer matrixes with embedded carbon dots assembled in situ. Importantly, different luminescence colours were produced simply by preparing C-dot/polymer films using carbon precursors that yielded C-dots exhibiting distinct fluorescence emission profiles. Furthermore, mixtures of C-dot precursors could be also employed for fabricating films exhibiting different colours. In particular, we successfully produced films emitting white light with attractive properties (i.e. ``warm'' white light with a high colour rendering index) - a highly sought after goal in optical technologies.Development of efficient, inexpensive, and environmentally-friendly light emitters, particularly devices that produce white light, have drawn intense interest due to diverse applications in the lighting industry, photonics, solar energy, and others. We present a simple strategy for the fabrication of flexible transparent films exhibiting tuneable light emission through one-pot synthesis of polymer matrixes with embedded carbon dots assembled in situ. Importantly, different luminescence colours were produced simply by preparing C-dot/polymer films using carbon precursors that yielded C-dots exhibiting distinct fluorescence emission profiles. Furthermore, mixtures of C-dot precursors could be also employed for fabricating films exhibiting different colours. In particular, we successfully produced films emitting white light with attractive properties (i.e. ``warm'' white light with a high colour rendering index) - a highly sought after goal in optical technologies. Electronic supplementary information (ESI

  16. The effects of the firing temperature of YBCO coated conductors fabricated by TFA-MOD process

    International Nuclear Information System (INIS)

    Jang, Seok Hern; Lim, Jun Hyung; Kim, Kyu Tae; Lee, Jin Sung; Yoon, Kyung Min; Kim, Ho-Jin; Joo, Jinho; Kim, Hyoungsub; Lee, Hee-Gyoun; Hong, Gye-Won

    2006-01-01

    We fabricated YBCO films on LAO substrates using the TFA-MOD method and evaluated the effects of the heat treatment temperature on the microstructure, degree of texture, and critical properties. The phase formation and microstructure were characterized by X-ray diffraction, Raman spectroscopy and scanning electron microscopy (SEM) and the degree of texture was evaluated by pole-figure analysis. The firing was performed in the temperature range of 750-800 deg. C and we found that the phase purity, grain size and orientation, degree of texture, and oxygen content varied with the firing temperature. The films fired at 775 deg. C showed the highest critical temperature (T C -onset) of 89.5 K and critical current (I C ) of 40 A/cm-width, which corresponds to a critical current density (J C ) of 1.8 MA/cm 2 . According to the results of the XRD, pole-figure, SEM and Raman analyses, these optimum critical properties can probably be attributed to the formation of a pure YBCO phase, stronger c-axis orientation and higher oxygen content

  17. Nanostructured ZnO thin films prepared by sol–gel spin-coating

    Energy Technology Data Exchange (ETDEWEB)

    Heredia, E., E-mail: heredia.edu@gmail.com [UNIDEF (CONICET-MINDEF), J.B. de La Salle 4397, 1603 Villa Martelli, Pcia. de Buenos Aires (Argentina); Bojorge, C.; Casanova, J.; Cánepa, H. [UNIDEF (CONICET-MINDEF), J.B. de La Salle 4397, 1603 Villa Martelli, Pcia. de Buenos Aires (Argentina); Craievich, A. [Instituto de Física, Universidade de São Paulo, Cidade Universitária, 66318 São Paulo, SP (Brazil); Kellermann, G. [Universidade Federal do Paraná, 19044 Paraná (Brazil)

    2014-10-30

    Highlights: • ZnO films synthesized by sol–gel were deposited by spin-coating on flat substrates. • Structural features of ZnO films with several thicknesses were characterized by means of different techniques. • The thicknesses of different ZnO thin films were determined by means of FESEM and AFM. • The nanoporous structures of ZnO thin films were characterized by GISAXS using IsGISAXS software. • The average densities of ZnO thin films were derived from (i) the critical angle in 1D XR patterns, (ii) the angle of Yoneda peak in 2D GISAXS images, (iii) minimization of chi2 using IsGISAXS best fitting procedure. - Abstract: ZnO thin films deposited on silica flat plates were prepared by spin-coating and studied by applying several techniques for structural characterization. The films were prepared by depositing different numbers of layers, each deposition being followed by a thermal treatment at 200 °C to dry and consolidate the successive layers. After depositing all layers, a final thermal treatment at 450 °C during 3 h was also applied in order to eliminate organic components and to promote the crystallization of the thin films. The total thickness of the multilayered films – ranging from 40 nm up to 150 nm – was determined by AFM and FESEM. The analysis by GIXD showed that the thin films are composed of ZnO crystallites with an average diameter of 25 nm circa. XR results demonstrated that the thin films also exhibit a large volume fraction of nanoporosity, typically 30–40 vol.% in thin films having thicknesses larger than ∼70 nm. GISAXS measurements showed that the experimental scattering intensity is well described by a structural model composed of nanopores with shape of oblate spheroids, height/diameter aspect ratio within the 0.8–0.9 range and average diameter along the sample surface plane in the 5–7 nm range.

  18. Challenges in TEM sample preparation of solvothermally grown CuInS2 films.

    Science.gov (United States)

    Frank, Anna; Changizi, Rasa; Scheu, Christina

    2018-06-01

    Transmission electron microscopy (TEM) is a widely used tool to characterize materials. The required samples need to be electron transparent which should be achieved without changing the microstructure. This work describes different TEM sample preparation techniques of nanostructured CuInS 2 thin films on fluorine-doped tin oxide substrates, synthesized solvothermally using l-cysteine as sulfur source. Focused ion beam lamellae, conventional cross section samples and scratch samples have been prepared and investigated. It was possible to prepare appropriate samples with each technique, however, each technique brings with it certain advantages and disadvantages. FIB preparation of solvothermally synthesized CuInS 2 suffers from two main drawbacks. First, the whole CuInS 2 layer displays a strongly increased Cu content caused by Cu migration and preferential removal of In. Further, electron diffraction shows the formation of an additional CuS phase after Ga + bombardment. Second, diffraction analysis is complicated by a strong contribution of crystalline Pt introduced during the FIB preparation and penetrating into the porous film surface. The conventional cross sectional CuInS 2 sample also shows a Cu signal enhancement which is caused by contribution of the brass tube material used for embedding. Additionally, Cu particles have been observed inside the CuInS 2 which have been sputtered on the film during preparation. Only the scratch samples allow an almost artefact-free and reliable elemental quantification using energy-dispersive X-ray spectroscopy. However, scratch samples suffer from the drawback that it is not possible to determine the layer thickness, which is possible for both cross sectional preparation techniques. Consequently, it is concluded that the type of sample preparation should be chosen dependent on the required information. A full characterization can only be achieved when the different techniques are combined. Copyright © 2018 Elsevier Ltd. All

  19. Experimental studies on the electronic structure of pyrite FeS2 films prepared by thermally sulfurizing iron films

    International Nuclear Information System (INIS)

    Zhang Hui; Wang Baoyi; Zhang Rengang; Zhang Zhe; Wei Long; Qian Haijie; Su Run; Kui Rexi

    2006-01-01

    Pyrite FeS 2 films have been prepared by thermally sulfurizing iron films deposited by magnetron sputtering. The electronic structures were studies by X-ray absorption near edge structure and X-ray photoemission spectrum. The results show that an S 3p valence band with relatively higher intensity compared to the calculation exists in 2-10 eV range and a high density below the Fermi level of Fe 3d states were detected. A second gap of 2.8 eV in the unoccupied density of states was found above the conduction band which was 2.4 eV by experimentally calculation. The difference between t 2g and e g which were formed in an octahedral crystal field was computed to be 2.1 eV. (authors)

  20. Humidity sensing properties of WO3 thick film resistor prepared by screen printing technique

    International Nuclear Information System (INIS)

    Garde, Arun S

    2014-01-01

    Highlights: • Polycrystalline WO 3 Thick films are fabricated by screen printing technique. • Monoclinic phases were the majority in formation of films. • The peak at 1643 cm −1 shows stretching vibrations attributed to W-OH of adsorbed H 2 O. • Absorption peaks in the range 879–650 cm −1 are attributed to the stretching W-O-W bonds. • Increase in resistance with decrease in RH when exposed to 20–100% RH. - Abstract: Thick films of tungsten oxide based were prepared using standard screen printing technique. To study the effect of temperature on the thick films were fired at different temperature for 30 min in air atmosphere. The WO 3 thick films were characterized with X-ray diffraction, scanning electron microscopy and EDAX for elemental analysis. The formation of mixed phases of the film together with majority of monoclinic phase was observed. IR spectra confirm the peak at 1643 cm −1 clearly shows stretching vibrations attributed to the W-OH bending vibration mode of the adsorbed water molecules. The absorption peaks in the range 879–650 cm −1 are attributed to the stretching W-O-W bonds (i.e. ν [W-O inter -W]). The peak located at 983 cm −1 belong to W=O terminal of cluster boundaries. A change in the resistance was observed with respect to the relative humidity when the WO 3 thick films were exposed to a wide humidity range of 20–100%. An increasing firing temperature of WO 3 film increases with the sensitivity. The parameters such as sensitivity and hysteresis of the WO 3 film sensors have been evaluated

  1. TiO2 and Cu/TiO2 Thin Films Prepared by SPT

    Directory of Open Access Journals (Sweden)

    S. S. Roy

    2015-12-01

    Full Text Available Titanium oxide (TiO2 and copper (Cu doped titanium oxide (Cu/TiO2 thin films have been prepared by spray pyrolysis technique. Titanium chloride (TiCl4 and copper acetate (Cu(CH3COO2.H2O were used as source of Ti and Cu. The doping concentration of Cu was varied from 1-10 wt. %. The X-ray diffraction studies show that TiO2 thin films are tetragonal structure and Cu/TiO2 thin films implies CuO has present with monoclinic structure. The optical properties of the TiO2 thin films have been investigated as a function of Cu-doping level. The optical transmission of the thin films was found to increase from 88 % to 94 % with the addition of Cu up to 8 % and then decreases for higher percentage of Cu doping. The optical band gap (Eg for pure TiO2 thin film is found to be 3.40 eV. Due to Cu doping, the band gap is shifted to lower energies and then increases further with increasing the concentration of Cu. The refractive index of the TiO2 thin films is found to be 2.58 and the variation of refractive index is observed due to Cu doped. The room temperature resistivity of the films decreases with increasing Cu doping and is found to be 27.50 - 23.76 W·cm. It is evident from the present study that the Cu doping promoted the thin film morphology and thereby it is aspect for various applications.

  2. Preparation of the Crosslinked Polyethersulfone Films by High Temperature Electron-Beam Irradiation

    International Nuclear Information System (INIS)

    Li, J.

    2006-01-01

    The aromatic polymers, mainly so called engineering plastics, were famed for the good stability under irradiation. However, high temperature irradiation of the aromatic polymers can result the crosslinked structure, due to the improved molecular mobility. Polyethersulfone (PES) is a wide used engineering plastic because of the high performance and high thermal stability. PES films were irradiated by electron-beam under nitrogen atmosphere above the glass transition temperature and then the covalently crosslinked PES (RX-PES) films were obtained. The irradiations were also performed at ambient temperature for comparison. The network structure formation of the RX-PES films was confirmed by the appearance of the gel, which were measured by soaking the irradiated PES films in the N,N-dimethylformamide (DMF) at room temperature. When the PES films were irradiated to 300 kGy, there was gel appeared. The gel percent increased with the increasing in the absorbed dose, and saturated when the absorbed dose exceeded 1200 kGy. However, there was no gel formed for the PES films irradiated at ambient temperature even to 2250 kGy. The G(S) and G(X) were calculated according to the Y-crosslinking mechanism. The results values are consistent in error range. G(S) of 0.10 and G(X) of 0.23 were obtained. As calculated, almost all the macromolecular radicals produced by chain scission were used for crosslinking. Also, the glass transition temperature of the RX-PES films increased with the increasing in the absorbed doses, while the glass transition temperature of the PES films irradiated at ambient temperature decreased with the increasing in the absorbed doses. The blending films of the PES with FEP or ETFE were prepared and the high temperature irradiation effects were also studies

  3. Preparation and characterization of biocomposite film based on chitosan and kombucha tea as active food packaging.

    Science.gov (United States)

    Ashrafi, Azam; Jokar, Maryam; Mohammadi Nafchi, Abdorreza

    2018-03-01

    An active film composed of chitosan and kombucha tea (KT) was successfully prepared using the solvent casting technique. The effect of incorporation of KT at the levels 1%-3% w/w on the physical and functional properties of chitosan film was investigated. The antimicrobial activity of chitosan/KT film against Escherichia coli and Staphylococcus aureus was evaluated using agar diffusion test, and its antioxidant activity was determined using DPpH assay. The results revealed that incorporation of KT into chitosan films improved the water vapor permeability (from 256.7 to 132.1gcm -2 h -1 KPa -1 mm) and enhanced the antioxidant activity of the latter up to 59% DPpH scavenging activity. Moreover, the incorporation of KT into the chitosan film increased the protective effect of the film against ultra violet (UV). Fourier transform infrared spectroscopic analysis revealed the chemical interactions between chitosan and the polyphenol groups of KT. In a minced beef model, chitosan/KT film effectively served as an active packaging and extended the shelf life of the minced beef as manifested in the retardation of lipid oxidation and microbial growth from 5.36 to 2.11logcfugr -1 in 4days storage. The present work demonstrates that the chitosan/KT film not only maintains the quality of the minced beef but also, retards microbial growth significantly, extending the shelf life of the minced beef meat up to 3days; thus, chitosan/KT film is a potential material for active food packaging. Copyright © 2017 Elsevier B.V. All rights reserved.

  4. Preparation, optimisation and characterisation of novel wound healing film dressings loaded with streptomycin and diclofenac.

    Science.gov (United States)

    Pawar, H V; Tetteh, J; Boateng, J S

    2013-02-01

    Streptomycin (STP) and diclofenac (DLF) loaded film dressings were prepared by blending Polyox(®) (POL) with four hydrophilic polymers [hydroxypropylmethylcellulose (HPMC), carrageenan (CAR), sodium alginate (SA) or chitosan (CS)] using glycerol (GLY) as plasticiser. The films were characterised by scanning electron microscopy (SEM), differential scanning calorimetry (DSC), X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy, texture analysis (tensile and swelling characteristics) and in vitro dissolution profiles using Franz diffusion cell. SEM showed homogeneous morphology for both blank (BLK) and drug loaded (DL) films. Films prepared by blending of POL with the other polymers showed a reduction in the crystallisation of POL in descending order of SA>CS>HPMC>CAR respectively. DSC and XRD showed no crystalline peaks of STP and DLF suggesting molecular dispersion of both drugs as well as possible drug interaction with negatively charged sulphate ions present in CAR. The DL films did not show any IR bands of both drugs, confirming the DSC and XRD results. POL-CAR-BLK films showed higher tensile strength (12.32±1.40 MPa) than the POL-CAR-DL films (9.52±1.12 MPa). DL films plasticised with 25%w/w GLY revealed soft and tough (tensile strength 1.02±0.28 MPa, % elongation 1031.33±16.23) formulations. The swelling capacities of POL-CAR-BLK and POL-CAR-DL films were (733.17±25.78%) and (646.39±40.39%), increasing to (1072.71±80.30%) and (1051±86.68%) for POL-CAR-BLK-25% GLY and POL-CAR-DL-25% GLY respectively. POL-CAR-DL films showed significantly (n=3, p<0.0318) lower cumulative release of STP and DLF (52.11±1.34, 55.26±2.25) compared to POL-CAR-DL-25% GLY films (60.07±1.56, 63.39±1.92) respectively. Copyright © 2012 Elsevier B.V. All rights reserved.

  5. Preparation And Properties Of Bionanocomposite Films Reinforced With Nanocellulose Isolated From Moroccan Alfa Fibres

    Directory of Open Access Journals (Sweden)

    Youssef Benyoussif

    2015-09-01

    Full Text Available Nanocellulose (NC were extracted from the Moroccan Alfa plant (Stipa tenacissima L. and characterised. These Alfa cellulosic nanoparticles were used as reinforcing phase to prepare bionanocomposite films using carboxymethyl cellulose as matrix. These films were obtained by the casting/evaporation method. The crystallinity of NC was analysed by X-ray diffraction, the dimension of NC by atomic force microscopy, molecular interactions due to incorporation of NC in carboxymethyl cellulose (CMC matrix were supported by Fourier transforms infrared (FTIR spectroscopy. The properties of the ensuing bionanocomposite films were investigated using tensile tests, water vapour permeability (WVP study and thermogravimetric analysis. With the progress of purification treatment of cellulose, the crystallinity is improved compared to the untreated fibres; this can be explained by the disappearance of the amorphous areas in cellulose chain of the plant. Consequently, the tensile modulus and tensile strength of CMC film increased by 60 and 47%, respectively, in the bionanocomposite films with 10 wt% of NC, and decrease by 8.6% for WVP with the same content of NC. The NC obtained from the Moroccan Alfa fibres can be used as a reinforcing agent for the preparation of bionanocomposites, and they have a high potential for the development of completely biodegradable food packaging materials.

  6. Electrical and optical properties of CZTS thin films prepared by SILAR method

    Directory of Open Access Journals (Sweden)

    J. Henry

    2016-03-01

    Full Text Available In the present work, Cu2ZnSnS4 (CZTS thin film was deposited onto the glass substrate by simple and economic SILAR method and its structural, morphological, optical and electrical properties were analyzed. X-ray diffraction (XRD analysis confirms the formation of CZTS with kesterite structure and the average crystallite size is found to be 142 nm. Scanning electron microscope (SEM image shows that the film has homogeneous, agglomerated surface without any cracks. The prepared CZTS film shows good optical absorption (104 cm−1 in the visible region and the optical band gap energy is found to be quite close to the optimum value of about 1.54 eV for solar cell application. The refractive index of the prepared film is found to be 2.85. The electrical resistivity of the film is found to be ∼10−2 Ω cm at room temperature.

  7. Preparation of Ta(C)N films by pulsed high energy density plasma

    Energy Technology Data Exchange (ETDEWEB)

    Feng Wenran [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, 100080 Beijing (China); Chen Guangliang [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, 100080 Beijing (China); Zhang Yan [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, 100080 Beijing (China); Gu Weichao [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, 100080 Beijing (China); Zhang Guling [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, 100080 Beijing (China); Niu Erwu [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, 100080 Beijing (China); Liu Chizi [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, 100080 Beijing (China); Yang Size [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, 100080 Beijing (China)

    2007-04-07

    The pulsed high energy density plasma (PHEDP) is generated in the working gas due to a high-voltage high-current discharge, within a coaxial gun. In PHEDP surface modification, discharge is applied for preparing the amorphous and nanostructured high-melting materials as thin films deposited on various substrates. In this investigation, Ta(C)N films were deposited using PHEDP on stainless steel. Pure tantalum and graphite were used as the inner and outer electrodes of the PHEDP coaxial gun, respectively. Nitrogen was used as the working gas and also one of the reactants. Preliminary study on the films prepared under different conditions shows that the formation of Ta(C)N is drastically voltage dependent. At lower gun voltage, no Ta(C)N was detected in the films; when the gun voltage reaches or exceeds 3.0 kV, Ta(C)N occurred. The films are composed of densely stacked nanocrystallines with diameter less than 30 nm, and some grains are within 10 nm in diameter.

  8. Preparation and physical properties of tara gum film reinforced with cellulose nanocrystals.

    Science.gov (United States)

    Ma, Qianyun; Hu, Dongying; Wang, Lijuan

    2016-05-01

    Cellulose nanocrystals (CNC) prepared from microcrystalline cellulose were blended in tara gum solution to prepare nanocomposite films. The morphology, crystallinity, and thermal properties of the CNC and films were evaluated by using transmission electron microscopy, X-ray diffractometry, and thermogravimetric analysis, respectively. The resultant CNC was rod-shaped with diameters of around 8.6 nm. The effect of CNC content on physical and thermal properties of films was studied. The composite film tensile strength increased from 27.86 to 65.73 MPa, elastic modulus increased from 160.98 MPa to 882.49 MPa and the contact angle increased from 55.8° to 98.7° with increasing CNC content from 0 to 6 wt%. However, CNC addition increased the thermal stability slightly and CNC content above 6 wt% decreased the tensile strength by CNC aggregation in the matrix. The nanocomposite film containing 6 wt% CNC possessed the highest light transmittance, mechanical properties, and lowest oxygen permeability. CNC addition is a suitable method to modify tara gum matrix polymer properties. Copyright © 2016 Elsevier B.V. All rights reserved.

  9. Carbon nanotubes length optimization for preparation of improved transparent and conducting thin film substrates

    Directory of Open Access Journals (Sweden)

    Mansoor Farbod

    2017-03-01

    Full Text Available Transparent and conductive thin films of multiwalled carbon nanotubes (MWCNTs with different lengths were prepared on glass substrates by the spin coating method. In order to reduce the MWCNTs length, they were functionalized. The initial length of MWCNTs (10–15 μm was reduced to 1200, 205 and 168 nm after 30, 60 and 120 min refluxing time, respectively. After post annealing at 285 °C for 24 h, the electrical and optical properties were greatly improved for functionalized MWCNT thin films. They strongly depend on the length of CNTs. The optical transmittance of the film prepared using 30 min reflux CNTs was 2.6% and 6.6% higher than that of the 60 min and 120 min refluxed samples respectively. The sheet resistance of this film showed reductions of 45% and 80% as well. The film also exhibited the least roughness. The percolative figure of merit, which is proportional to the transparency and disproportional to the sheet resistance, was found to be higher for the sample with 30 min refluxed MWCNTs.

  10. In situ preparation, electrical and surface analytical characterization of pentacene thin film transistors

    Science.gov (United States)

    Lassnig, R.; Striedinger, B.; Hollerer, M.; Fian, A.; Stadlober, B.; Winkler, A.

    2015-01-01

    The fabrication of organic thin film transistors with highly reproducible characteristics presents a very challenging task. We have prepared and analyzed model pentacene thin film transistors under ultra-high vacuum conditions, employing surface analytical tools and methods. Intentionally contaminating the gold contacts and SiO2 channel area with carbon through repeated adsorption, dissociation, and desorption of pentacene proved to be very advantageous in the creation of devices with stable and reproducible parameters. We mainly focused on the device properties, such as mobility and threshold voltage, as a function of film morphology and preparation temperature. At 300 K, pentacene displays Stranski-Krastanov growth, whereas at 200 K fine-grained, layer-like film growth takes place, which predominantly influences the threshold voltage. Temperature dependent mobility measurements demonstrate good agreement with the established multiple trapping and release model, which in turn indicates a predominant concentration of shallow traps in the crystal grains and at the oxide-semiconductor interface. Mobility and threshold voltage measurements as a function of coverage reveal that up to four full monolayers contribute to the overall charge transport. A significant influence on the effective mobility also stems from the access resistance at the gold contact-semiconductor interface, which is again strongly influenced by the temperature dependent, characteristic film growth mode. PMID:25814770

  11. Construction of sputtering system and preparation of high temperature superconducting thin films

    International Nuclear Information System (INIS)

    Kaynak, E.

    2000-01-01

    The preparation of high T c superconducting thin film is important both for the understanding of fundamental behaviours of these materials and for the investigations on the usefulness of technological applications. High quality thin films can be prepared by various kinds of techniques being used today. Among these, sputtering is the most preferred one. The primary aim of this work is the construction of a r. f. and c. magnetron sputtering system. For this goal, a magnetron sputtering system was designed and constructed having powers up to 500W (r.f.) and 1KW (d.c.) that enables to deposit thin films of various kinds of materials: metals, ceramics and magnetic materials. The temperature dependence of the electrical resistance of the films was investigated by using four-point probe method. The zero resistance and the transition with of the films were measured as 80-85 K, and 2-9 K, respectively. The A.C. susceptibility experiments were done by utilising the system that was designed and constructed. The applied field dependence of the real and imaginary components of the susceptibility that were measured between the 77-120 K temperature interval and at a fixed frequency was investigated

  12. Numerical analysis of the influence of buffer layer thickness on the residual stresses in YBCO/La2Zr2O7/Ni superconducting materials

    International Nuclear Information System (INIS)

    Celik, Erdal; Sayman, Onur; Karakuzu, Ramazan; Ozman, Yilmaz

    2007-01-01

    The present paper addresses a numerical investigation of the influence of buffer layer thickness on the residual stress in YBCO/La 2 Zr 2 O 7 /Ni architectured materials under cryogenic conditions by using classical lamination theory (CLT) and finite element method (FEM) for coated conductor applications. YBCO/La 2 Zr 2 O 7 multilayer films were fabricated on Ni tape substrate using reel-to-reel sol-gel and pulse laser deposition (PLD) systems. The microstructural evolution of high temperature superconducting YBCO film and buffer layers with La 2 Zr 2 O 7 configuration grown on textured Ni tape substrates was investigated by using a scanning electron microscope (SEM). Thermal stress analysis of YBCO/La 2 Zr 2 O 7 /Ni multilayer sample was performed by using CLT in the temperature range of 298-175 K in liquid helium media. The YBCO/La 2 Zr 2 O 7 /Ni sample strip was solved by using FEM for linear or nonlinear cases in the temperature range of 298-3 K in liquid helium media. SEM observations revealed that crack-free, pinhole-free, continuous superconducting film and buffer layer were obtained by sol-gel and PLD systems. In addition to microstructural observations, it was found that the largest compressive stresses and failure occur in La 2 Zr 2 O 7 buffer layer due to its smallest thermal expansion coefficient. The thickness of La 2 Zr 2 O 7 buffer layer affects the failure. The stress component of σ x is the smallest in Ni tape substrate due to its largest thickness

  13. Study on boron-film thermal neutron converter prepared by pulsed laser deposition

    International Nuclear Information System (INIS)

    Song Zifeng; Ye Shuzhen; Chen Ziyu; Song Liao; Shen Ji

    2011-01-01

    The boron film converter used in the position-sensitive thermal neutron detector is discussed and the method of preparing this converter layer via Pulsed Laser Deposition (PLD) is introduced. The morphology and the composition were studied by Scanning Electron Microscopy (SEM) and X-ray Photoelectron Spectroscopy (XPS). Both boron and boride existed on the layer surface. It was shown that the energy intensity of laser beam and the substrate temperature both had an important influence on the surface morphology of the film.

  14. Study on boron-film thermal neutron converter prepared by pulsed laser deposition

    Energy Technology Data Exchange (ETDEWEB)

    Song Zifeng; Ye Shuzhen; Chen Ziyu; Song Liao [Department of Modern Physics, University of Science and Technology of China, Anhui Hefei 230026 (China); Shen Ji, E-mail: shenji@ustc.edu.c [Department of Modern Physics, University of Science and Technology of China, Anhui Hefei 230026 (China)

    2011-02-15

    The boron film converter used in the position-sensitive thermal neutron detector is discussed and the method of preparing this converter layer via Pulsed Laser Deposition (PLD) is introduced. The morphology and the composition were studied by Scanning Electron Microscopy (SEM) and X-ray Photoelectron Spectroscopy (XPS). Both boron and boride existed on the layer surface. It was shown that the energy intensity of laser beam and the substrate temperature both had an important influence on the surface morphology of the film.

  15. The properties of B-Sb thin films prepared by molecular flow region PVD process

    International Nuclear Information System (INIS)

    Kumashiro, Y.; Nakamura, K.; Sato, K.; Ohtsuka, M.; Ohishi, Y.; Nakano, M.; Doi, Y.

    2004-01-01

    The present paper is the first description on the electrical and thermoelectric properties of amorphous PVD B 12 Sb 2 films prepared using the reaction of decaborane gas with evaporated antimony gas on Si (1900 A) / SiO x (3700 A) / Si (100) (625 μm) substrate at the temperature 350 deg. C. Ohmic metals contacts of the film were examined by making evaporated Al, followed by annealing at 200 deg. C. The comparatively high mobility of ∼100 cm 2 /V s and high thermoelectric figures-of-merit of ∼10 -4 /K were confirmed

  16. Preparation of Aluminum Nanomesh Thin Films from an Anodic Aluminum Oxide Template as Transparent Conductive Electrodes

    Science.gov (United States)

    Li, Yiwen; Chen, Yulong; Qiu, Mingxia; Yu, Hongyu; Zhang, Xinhai; Sun, Xiao Wei; Chen, Rui

    2016-02-01

    We have employed anodic aluminum oxide as a template to prepare ultrathin, transparent, and conducting Al films with a unique nanomesh structure for transparent conductive electrodes. The anodic aluminum oxide template is obtained through direct anodization of a sputtered Al layer on a glass substrate, and subsequent wet etching creates the nanomesh metallic film. The optical and conductive properties are greatly influenced by experimental conditions. By tuning the anodizing time, transparent electrodes with appropriate optical transmittance and sheet resistance have been obtained. The results demonstrate that our proposed strategy can serve as a potential method to fabricate low-cost TCEs to replace conventional indium tin oxide materials.

  17. Biodegradable Starch/Copolyesters Film Reinforced with Silica Nanoparticles: Preparation and Characterization

    Science.gov (United States)

    Lima, Roberta A.; Oliveira, Rene R.; Wataya, Célio H.; Moura, Esperidiana A. B.

    Biodegradable starch/copolyesters/silica nanocomposite films were prepared by melt extrusion, using a twin screw extruder machine and blown extrusion process. The influence of the silica nanoparticle addition on mechanical and thermal properties of nanocomposite films was investigated by tensile tests; X-rays diffraction (XRD), differential scanning calorimetry (DSC) and Scanning electron microscopy (SEM) analysis and the correlation between properties was discussed. The results showed that incorporation of 2 % (wt %) of SiO2 nanoparticle in the blend matrix of PBAT/Starch, resulted in a gain of mechanical properties of blend.

  18. Microstructure and mechanical properties of Zr-Si-N films prepared by rf-reactive sputtering

    CERN Document Server

    Nose, M; Zhou, M; Mae, T; Meshii, M

    2002-01-01

    ZrN and ZrSiN films were prepared in an rf sputtering apparatus that has a pair of targets facing each other (referred to as the facing target--type rf sputtering). Films were deposited on silicon wafers without bias application or substrate heating in order to examine only the effect of silicon addition to the transition metal nitride films. The contents of zirconium, nitrogen, and silicon of the films were determined with an electron probe microanalyzer. The transmission electron microscopy studies were carried out in addition to x-ray diffraction. For the high resolution transmission electron microscopy observation, the field emission type transmission electron microscope was used, which provides a point-to-point resolution of 0.1 nm. The samples were observed both parallel and perpendicular to the film surface, which were plane and cross sectional views, respectively. In order to investigate the relationship between the mechanical properties and microstructure of films, the hardness was measured by a nano...

  19. Characterizations of maghemite thin films prepared by a sol-gel method

    Energy Technology Data Exchange (ETDEWEB)

    Lau, L. N., E-mail: lau7798@gmail.com; Ibrahim, N. B., E-mail: baayah@ukm.edu.my [School of Applied Physics, Faculty of Science and Technology, Universiti Kebangsaan Malaysia, 43600 UKM Bangi, Selangor. Malaysia (Malaysia)

    2015-09-25

    Iron is one of the abundant elements of Mother Nature and its compound, iron oxide is an interesting material to study since its discovery in the form of magnetite. It can exist in many phases such as hematite and maghemite, this unique nature has put it as a potential candidate in various applications. The aim of this work is to study the influence of different precursor concentrations on the microstructural and magnetic properties of iron oxide thin film. All samples were prepared via the sol-gel method followed by a spin coating technique on quartz substrates. Iron oxide films were confirmed as maghemite phase from X-ray diffraction patterns. The film morphology was examined by a field emission scanning electron microscope and it showed non-systematic value of average grain size and film thickness throughout the study. Hysteresis loop further confirmed that maghemite is a magnetic material when it was characterized by a vibrating sample magnetometer. The coercivity did not show any correlation with molarity. Nevertheless, it increased as the precursor concentration of the film increased due to the domain behaviour. In conclusion, maghemite thin films were successfully synthesized by the sol-gel method with different precursor concentrations in this work.

  20. Preparation of superhydrophobic poly(methyl methacrylate)-silicon dioxide nanocomposite films

    Energy Technology Data Exchange (ETDEWEB)

    Wang Jinyan [Key Laboratory of Ministry of Education for Special Functional Materials, Henan University, Jinming Road, Kaifeng, Henan Province 475004 (China); Chen Xinhua [Key Laboratory of Ministry of Education for Special Functional Materials, Henan University, Jinming Road, Kaifeng, Henan Province 475004 (China); College of Chemistry and Chemical Engineering, Xuchang University, Xuchang 461000 (China); Kang Yingke; Yang Guangbin; Yu Laigui [Key Laboratory of Ministry of Education for Special Functional Materials, Henan University, Jinming Road, Kaifeng, Henan Province 475004 (China); Zhang Pingyu, E-mail: pingyu@henu.edu.cn [Key Laboratory of Ministry of Education for Special Functional Materials, Henan University, Jinming Road, Kaifeng, Henan Province 475004 (China)

    2010-12-15

    Superhydrophobic poly(methyl methacrylate)-SiO{sub 2} (coded as PMMA-SiO{sub 2}) nanocomposite films with micro-nanohierarchical structure were prepared via a simple approach in the absence of low surface-energy compounds. By spin-coating the suspension of hydrophobic silica (SiO{sub 2}) nanoparticles dispersed in PMMA solution, target nanocomposite films were obtained on glass slides. The wetting behavior of PMMA-SiO{sub 2} nanocomposite films was investigated in relation to the dosage of SiO{sub 2} nanoparticles dispersed in PMMA solution. It was found that hydrophilic PMMA film was transferred to superhydrophobic PMMA-SiO{sub 2} nanocomposite films when hydrophobic SiO{sub 2} nanoparticles were introduced into the PMMA solution at a high enough dosage (0.2 g and above). Resultant PMMA-SiO{sub 2} nanocomposite films had a static water contact angle of above 162{sup o}, showing promising applications in selfcleaning and waterproof for outer wall of building, outer covering for automobile, sanitary wares, and so forth.