Temperature increase beneath etched dentin discs during composite polymerization.

Science.gov (United States)

Karaarslan, Emine Sirin; Secilmis, Asli; Bulbul, Mehmet; Yildirim, Cihan; Usumez, Aslihan

2011-01-01

The purpose of this in vitro study was to measure the temperature increase during the polymerization of a composite resin beneath acid-etched or laser-etched dentin discs. The irradiation of dentin with an Er:YAG laser may have a positive effect on the thermal conductivity of dentin. This technique has not been studied extensively. Forty dentin discs (5 mm in diameter and 0.5 or 1 mm in height) were prepared from extracted permanent third molars. These dentin discs were etched with 20% orthophosphoric acid or an Er:YAG laser, and were then placed on an apparatus developed to measure temperature increases. The composite resin was polymerized with a high-intensity quartz tungsten halogen (HQTH) or light-emitting diode unit (LED). The temperature increase was measured under the dentin disc with a J-type thermocouple wire that was connected to a data logger. Five measurements were made for each dentin disc, curing unit, and etching system combination. Differences between the initial and the highest temperature readings were taken, and the five calculated temperature changes were averaged to determine the value of the temperature increase. Statistical analysis was performed with a three-way ANOVA and Tukey HSD tests at a 0.05 level of significance. Further SEM examinations were performed. The temperature increase values varied significantly, depending on etching systems (p < 0.05), dentin thicknesses (p < 0.05), and curing units (p < 0.05). Temperature increases measured beneath laser-etched discs were significantly higher than those for acid-etched dentin discs (p < 0.05). The HQTH unit induced significantly higher temperature increases than the LED unit (p < 0.05). The LED unit induced the lowest temperature change (5.2°C) in the 1-mm, acid-etched dentin group. The HQTH unit induced the highest temperature change (10.4°C) for the 0.5-mm, laser-etched dentin group. The risk of heat-induced pulpal damage should be taken into consideration

Ceramic Veneers and Direct-Composite Cases of Amelogenesis Imperfecta Rehabilitation.

Science.gov (United States)

Shibata, S; Taguchi, Cmc; Gondo, R; Stolf, S C; Baratieri, L N

2016-01-01

The aim of this article is to present two case reports for the treatment of patients affected with amelogenesis imperfecta. One case was treated with composite resin and the other case with ceramic veneers. Esthetic and functional results were achieved using both treatments, and a review of advantages and disadvantages is presented.

Combining Bioactive Multifunctional Dental Composite with PAMAM for Root Dentin Remineralization

Directory of Open Access Journals (Sweden)

Shimeng Xiao

2017-01-01

Full Text Available Objectives. The objectives of this study were to: (1 develop a bioactive multifunctional composite (BMC via nanoparticles of amorphous calcium phosphate (NACP, 2-methacryloyloxyethyl phosphorylcholine (MPC, dimethylaminohexadecyl methacrylate (DMAHDM and nanoparticles of silver (NAg; and (2 investigate the effects of combined BMC + poly (amido amine (PAMAM on remineralization of demineralized root dentin in a cyclic artificial saliva/lactic acid environment for the first time. Methods. Root dentin specimens were prepared and demineralized with 37% phosphoric acid for 15 s. Four groups were prepared: (1 root dentin control; (2 root dentin with BMC; (3 root dentin with PAMAM; (4 root dentin with BMC + PAMAM. Specimens were treated with a cyclic artificial saliva/lactic acid regimen for 21 days. Calcium (Ca and phosphate (P ion concentrations and acid neutralization were determined. The remineralized root dentin specimens were examined via hardness testing and scanning electron microscopy (SEM. Results. Mechanical properties of BMC were similar to commercial control composites (p = 0.913. BMC had excellent Ca and P ion release and acid-neutralization capability. BMC or PAMAM alone each achieved slight mineral regeneration in demineralized root dentin. The combined BMC + PAMAM induced the greatest root dentin remineralization, and increased the hardness of pre-demineralized root dentin to match that of healthy root dentin (p = 0.521. Significance. The excellent root dentin remineralization effects of BMC + PAMAM were demonstrated for the first time. BMC + PAMAM induced effective and complete root dentin remineralization in an acid challenge environment. The novel BMC + PAMAM method is promising for Class V and other restorations to remineralize and protect tooth structures.

Production of laminated veneer lumber LVL using veneer of Schizolobium amazonicum, Eucalyptus saligna and Pinus taeda

Directory of Open Access Journals (Sweden)

Setsuo Iwakiri

2010-12-01

Full Text Available This research evaluated the quality of laminated veneer lumber - LVL manufactured with veneers of Schizolobium amazonicum (paricá, Eucalyptus saligna and Pinus taeda. The LVL panels were manufactured in the laboratory conditions composed by seven veneers, 2,0 mm thickness, with different structural compositions, using phenol-formaldehyde resin. The veneers of Schizolobium amazonicum- paricá- were pre-classified by using stress wave machine. The veneers of Eucalyptus saligna and Pinus taeda were disposed in the face layer to reinforce the structural strength of LVL panels. The LVL quality was evaluated using glue line shear strength and static bending test (MOE and MOR, edge and flat. Grading of paricá veneers based on MOEd did not affected significantly the results of the glue line shear strength and MOE and MOR edge. For the MOE and MOR flat, the use of veneers of MOEd grade 1 contributed significantly to increasing the average values of these properties. In the same way, using the Eucalyptus saligna veneers on the face of LVL resulted in higher average values of MOE and MOR, edge and flat.

Fracture strengths of chair-side-generated veneers cemented with glass fibers.

Science.gov (United States)

Turkaslan, S; Bagis, B; Akan, E; Mutluay, M M; Vallittu, P K

2015-01-01

CAD/CAM (computer-aided design and computer-aided manufacturing) systems have refreshed the idea of chair-side production of restorations, but the fracture of ceramic veneers remains a problem. Cementation with glass fibers may improve the fracture strengths and affect the failure modes of CAD/CAM-generated ceramic veneers. Therefore, this study compared the fracture strengths of ceramic veneers produced at chair side and cemented with or without glass fibers with those of composite veneers. Thirty intact mandibular incisors were randomly divided into three groups ( n = 10) and treated with CAD/CAM-fabricated veneers cemented with dual-cure composite resin luting cement (CRLC; Group 1), CAD/CAM-fabricated veneers cemented with a glass fiber network (GFN) and dual-cure CRLC (Group 2), and a direct particulate filler composite veneer constructed utilizing fiber and a restorative composite resin (Group 3). The specimens were tested with a universal testing machine after thermal cycling treatment. The loads at the start of fracture were the lowest for traditionally fabricated composite veneers and higher for CAD/CAM-generated. Veneers cemented either without or with the GFN. The failure initiation loads (N) for the veneers were 798.92 for Group 1, 836.27 for Group 2, and 585.93 for Group 3. The predominant failure mode is adhesive failure between the laminates and teeth for Group 1, cohesive failure in the luting layer for Group 2, and cohesive laminate failure for Group 3, which showed chipping and small fractures. Ceramic material is a reliable alternative for veneer construction at chair side. Fibers at the cementation interface may improve the clinical longevity and provide higher fracture strength values.

Adhesive/Dentin Interface: The Weak Link in the Composite Restoration

Science.gov (United States)

Spencer, Paulette; Ye, Qiang; Park, Jonggu; Topp, Elizabeth M.; Misra, Anil; Marangos, Orestes; Wang, Yong; Bohaty, Brenda S.; Singh, Viraj; Sene, Fabio; Eslick, John; Camarda, Kyle; Katz, J. Lawrence

2010-01-01

Results from clinical studies suggest that more than half of the 166 million dental restorations that were placed in the United States in 2005 were replacements for failed restorations. This emphasis on replacement therapy is expected to grow as dentists use composite as opposed to dental amalgam to restore moderate to large posterior lesions. Composite restorations have higher failure rates, more recurrent caries, and increased frequency of replacement as compared to amalgam. Penetration of bacterial enzymes, oral fluids, and bacteria into the crevices between the tooth and composite undermines the restoration and leads to recurrent decay and premature failure. Under in vivo conditions the bond formed at the adhesive/dentin interface can be the first defense against these noxious, damaging substances. The intent of this article is to review structural aspects of the clinical substrate that impact bond formation at the adhesive/dentin interface; to examine physico-chemical factors that affect the integrity and durability of the adhesive/dentin interfacial bond; and to explore how these factors act synergistically with mechanical forces to undermine the composite restoration. The article will examine the various avenues that have been pursued to address these problems and it will explore how alterations in material chemistry could address the detrimental impact of physico-chemical stresses on the bond formed at the adhesive/dentin interface. PMID:20195761

Adhesion of resin composite core materials to dentin.

Science.gov (United States)

O'Keefe, K L; Powers, J M

2001-01-01

This study determined (1) the effect of polymerization mode of resin composite core materials and dental adhesives on the bond strength to dentin, and (2) if dental adhesives perform as well to dentin etched with phosphoric acid as to dentin etched with self-etching primer. Human third molars were sectioned 2 mm from the highest pulp horn and polished. Three core materials (Fluorocore [dual cured], Core Paste [self-cured], and Clearfil Photo Core [light cured]) and two adhesives (Prime & Bond NT Dual Cure and Clearfil SE Bond [light cured]) were bonded to dentin using two dentin etching conditions. After storage, specimens were debonded in microtension and bond strengths were calculated. Scanning electron micrographs of representative bonding interfaces were analyzed. Analysis showed differences among core materials, adhesives, and etching conditions. Among core materials, dual-cured Fluorocore had the highest bond strengths. There were incompatibilities between self-cured Core Paste and Prime & Bond NT in both etched (0 MPa) and nonetched (3.0 MPa) dentin. Among adhesives, in most cases Clearfil SE Bond had higher bond strengths than Prime & Bond NT and bond strengths were higher to self-etched than to phosphoric acid-etched dentin. Scanning electron micrographs did not show a relationship between resin tags and bond strengths. There were incompatibilities between a self-cured core material and a dual-cured adhesive. All other combinations of core materials and adhesives produced strong in vitro bond strengths both in the self-etched and phosphoric acid-etched conditions.

Grinding efficiency of abutment tooth with both dentin and core composite resin on axial plane.

Science.gov (United States)

Miho, Otoaki; Sato, Toru; Matsukubo, Takashi

2015-01-01

The purpose of this study was to evaluate grinding efficiency in abutment teeth comprising both dentin and core composite resin in the axial plane. Grinding was performed over 5 runs at two loads (0.5 or 0.25 N) and two feed rates (1 or 2 mm/sec). The grinding surface was observed with a 3-D laser microscope. Tomographic images of the grinding surfaces captured perpendicular to the feed direction were also analyzed. Using a non-ground surface as a reference, areas comprising only dentin, both dentin and core composite resin, or only core composite resin were analyzed to determine the angle of the grinding surface. Composite resins were subjected to the Vickers hardness test and scanning electron microscopy. Data were statistically analyzed using a one-way analysis of variance and multiple comparison tests. Multiple regression analysis was performed for load, feed rate, and Vickers hardness of the build-up material depending on number of runs. When grinding was performed at a constant load and feed rate, a greater grinding angle was observed in areas comprising both dentin and composite resin or only composite resin than in areas consisting of dentin alone. A correlation was found between machinability and load or feed rate in areas comprising both dentin and composite resin or composite resin alone, with a particularly high correlation being observed between machinability and load. These results suggest that great caution should be exercised in a clinical setting when the boundary between the dentin and composite resin is to be ground, as the angle of the grinding surface changes when the rotating diamond point begins grinding the composite resin.

Fracture toughness of dentin/resin-composite adhesive interfaces.

Science.gov (United States)

Tam, L E; Pilliar, R M

1993-05-01

The reliability and validity of tensile and shear bond strength determinations of dentin-bonded interfaces have been questioned. The fracture toughness value (KIC) reflects the ability of a material to resist crack initiation and unstable propagation. When applied to an adhesive interface, it should account for both interfacial bond strength and inherent defects at or near the interface, and should therefore be more appropriate for characterization of interface fracture resistance. This study introduced a fracture toughness test for the assessment of dentin/resin-composite bonded interfaces. The miniature short-rod specimen geometry was used for fracture toughness testing. Each specimen contained a tooth slice, sectioned from a bovine incisor, to form the bonded interface. The fracture toughness of an enamel-bonded interface was assessed in addition to the dentin-bonded interfaces. Tensile bond strength specimens were also prepared from the dentin surfaces of the cut bovine incisors. A minimum of ten specimens was fabricated for each group of materials tested. After the specimens were aged for 24 h in distilled water at 37 degrees C, the specimens were loaded to failure in an Instron universal testing machine. There were significant differences (p adhesives tested. Generally, both the fracture toughness and tensile bond strength measurements were highest for AllBond 2, intermediate for 3M MultiPurpose, and lowest for Scotchbond 2. Scanning electron microscopy of the fractured specimen halves confirmed that crack propagation occurred along the bond interface during the fracture toughness test. It was therefore concluded that the mini-short-rod fracture toughness test provided a valid method for characterization of the fracture resistance of the dentin-resin composite interface.

Fluorine analysis of human dentin surrounding resin composite after fluoride application by μ-PIGE/PIXE analysis

Science.gov (United States)

Okuyama, Katsushi; Komatsu, Hisanori; Yamamoto, Hiroko; Pereira, Patricia N. R.; Bedran-Russo, Ana K.; Nomachi, Masaharu; Sato, Takahiro; Sano, Hidehiko

2011-10-01

The use of fluoride for the prevention of caries is based on the transformation of hydroxylapatite to fluoroapatite in the presence of fluoride ions, thereby strengthening tooth structure. Adhesion of dentin and resin composite (tooth-colored restoration material) requires a dentin bonding system, since resin composite is not able to adhere to dentin directly. Demineralization of dentin by acid etching is an important step in the dentin bonding system, however, demineralization also introduces weaknesses in tooth structure. If the demineralized dentin could be strengthened by the application of fluoride, then the dentin-resin composite bond strength might also improve. To test this hypothesis, the present study evaluated the influence of fluoride applications on the strength of the dentin-resin composite bond by (1) tensile strength testing analyses, (2) SEM analyses of tooth structure, and (3) detection of calcium (Ca) and fluorine (F) distribution patterns by micro proton-induced X-ray emission (μ-PIXE) and micro proton-induced gamma-ray emission (μ-PIGE) analyses conducted at the Takasaki Ion Accelerators for Advanced Radiation Application (TIARA) at the Takasaki Advanced Radiation Research Institute (TARRI). In this study, the dentin in extracted human molars was exposed by grinding and the dentin was etched with 35% phosphoric acid. Fluoride was applied at two concentrations, 0.022% (100 ppm F) and 2.21% (10,000 ppm F) NaF solution, for two time periods, 30 and 60 s, prior to bonding the resin composite with the treated dentin. Controls were prepared in the same manner, but without the fluoride application. Bond strength was measured with a micro-tensile testing unit, and the fluorine and calcium distributions at the interface between dentin and resin composite were detected by μ-PIGE and μ-PIXE analysis, respectively. Results indicate that the 10,000 ppm F applications resulted in higher bond strengths than observed in either the 100 ppm F applications or

Fluorine analysis of human dentin surrounding resin composite after fluoride application by μ-PIGE/PIXE analysis

International Nuclear Information System (INIS)

Okuyama, Katsushi; Komatsu, Hisanori; Yamamoto, Hiroko; Pereira, Patricia N.R.; Bedran-Russo, Ana K.; Nomachi, Masaharu; Sato, Takahiro; Sano, Hidehiko

2011-01-01

The use of fluoride for the prevention of caries is based on the transformation of hydroxylapatite to fluoroapatite in the presence of fluoride ions, thereby strengthening tooth structure. Adhesion of dentin and resin composite (tooth-colored restoration material) requires a dentin bonding system, since resin composite is not able to adhere to dentin directly. Demineralization of dentin by acid etching is an important step in the dentin bonding system, however, demineralization also introduces weaknesses in tooth structure. If the demineralized dentin could be strengthened by the application of fluoride, then the dentin-resin composite bond strength might also improve. To test this hypothesis, the present study evaluated the influence of fluoride applications on the strength of the dentin-resin composite bond by (1) tensile strength testing analyses, (2) SEM analyses of tooth structure, and (3) detection of calcium (Ca) and fluorine (F) distribution patterns by micro proton-induced X-ray emission (μ-PIXE) and micro proton-induced gamma-ray emission (μ-PIGE) analyses conducted at the Takasaki Ion Accelerators for Advanced Radiation Application (TIARA) at the Takasaki Advanced Radiation Research Institute (TARRI). In this study, the dentin in extracted human molars was exposed by grinding and the dentin was etched with 35% phosphoric acid. Fluoride was applied at two concentrations, 0.022% (100 ppm F) and 2.21% (10,000 ppm F) NaF solution, for two time periods, 30 and 60 s, prior to bonding the resin composite with the treated dentin. Controls were prepared in the same manner, but without the fluoride application. Bond strength was measured with a micro-tensile testing unit, and the fluorine and calcium distributions at the interface between dentin and resin composite were detected by μ-PIGE and μ-PIXE analysis, respectively. Results indicate that the 10,000 ppm F applications resulted in higher bond strengths than observed in either the 100 ppm F applications or

Fluorine analysis of human dentin surrounding resin composite after fluoride application by {mu}-PIGE/PIXE analysis

Energy Technology Data Exchange (ETDEWEB)

Okuyama, Katsushi, E-mail: katsu@den.hokudai.ac.jp [Graduate School of Dental Medicine, Hokkaido University, Department of Restorative Dentistry, Kita-13, Nishi-7, Kita-ku, Hokkaido, Sapporo 060-8586 (Japan) and School of Dentistry, University of North Carolina, Department of Operative Dentistry, 302 Brauer, CB 7450, Chapel Hill, NC 27599-7450 (United States); Komatsu, Hisanori [Graduate School of Dental Medicine, Hokkaido University, Department of Restorative Dentistry, Kita-13, Nishi-7, Kita-ku, Hokkaido, Sapporo 060-8586 (Japan); Yamamoto, Hiroko [Graduate School of Dentistry, Osaka University, 1-8 Yamada-Oka, Osaka, Suita 565-0871 (Japan); Pereira, Patricia N.R. [School of Dentistry, University of North Carolina, Department of Operative Dentistry, 302 Brauer, CB 7450, Chapel Hill, NC 27599-7450 (United States); Bedran-Russo, Ana K. [University of Illinois at Chicago, College of Dentistry, Department of Restorative Dentistry, 801 S. Paulina St., Chicago, IL 60612 (United States); Nomachi, Masaharu [Graduate School of Science, Osaka University, 1-1 Machikaneyama, Osaka, Toyonaka 560-0043 (Japan); Sato, Takahiro [TARRI, JAEA, Advanced Radiation Technology, 1233 Watanuki-machi, Gunma, Takasaki 370-1292 (Japan); Sano, Hidehiko [Graduate School of Dental Medicine, Hokkaido University, Department of Restorative Dentistry, Kita-13, Nishi-7, Kita-ku, Hokkaido, Sapporo 060-8586 (Japan)

2011-10-15

The use of fluoride for the prevention of caries is based on the transformation of hydroxylapatite to fluoroapatite in the presence of fluoride ions, thereby strengthening tooth structure. Adhesion of dentin and resin composite (tooth-colored restoration material) requires a dentin bonding system, since resin composite is not able to adhere to dentin directly. Demineralization of dentin by acid etching is an important step in the dentin bonding system, however, demineralization also introduces weaknesses in tooth structure. If the demineralized dentin could be strengthened by the application of fluoride, then the dentin-resin composite bond strength might also improve. To test this hypothesis, the present study evaluated the influence of fluoride applications on the strength of the dentin-resin composite bond by (1) tensile strength testing analyses, (2) SEM analyses of tooth structure, and (3) detection of calcium (Ca) and fluorine (F) distribution patterns by micro proton-induced X-ray emission ({mu}-PIXE) and micro proton-induced gamma-ray emission ({mu}-PIGE) analyses conducted at the Takasaki Ion Accelerators for Advanced Radiation Application (TIARA) at the Takasaki Advanced Radiation Research Institute (TARRI). In this study, the dentin in extracted human molars was exposed by grinding and the dentin was etched with 35% phosphoric acid. Fluoride was applied at two concentrations, 0.022% (100 ppm F) and 2.21% (10,000 ppm F) NaF solution, for two time periods, 30 and 60 s, prior to bonding the resin composite with the treated dentin. Controls were prepared in the same manner, but without the fluoride application. Bond strength was measured with a micro-tensile testing unit, and the fluorine and calcium distributions at the interface between dentin and resin composite were detected by {mu}-PIGE and {mu}-PIXE analysis, respectively. Results indicate that the 10,000 ppm F applications resulted in higher bond strengths than observed in either the 100 ppm F

Dentin surface treatment using a non-thermal argon plasma brush for interfacial bonding improvement in composite restoration

Science.gov (United States)

Ritts, Andy Charles; Li, Hao; Yu, Qingsong; Xu, Changqi; Yao, Xiaomei; Hong, Liang; Wang, Yong

2010-01-01

The objective of this study is to investigate the treatment effects of non-thermal atmospheric gas plasmas on dentin surfaces for composite restoration. Extracted unerupted human third molars were used by removing the crowns and etching the exposed dentin surfaces with 35% phosphoric acid gel. The dentin surfaces were treated by using a non-thermal atmospheric argon plasma brush for various durations. The molecular changes of the dentin surfaces were analyzed using FTIR/ATR and an increase in carbonyl groups on dentin surfaces was detected with plasma treated dentin. Adper Single Bond Plus adhesive and Filtek Z250 dental composite were applied as directed. To evaluate the dentin/composite interfacial bonding, the teeth thus prepared were sectioned into micro-bars as the specimens for tensile test. Student Newman Keuls tests showed that the bonding strength of the composite restoration to peripheral dentin was significantly increased (by 64%) after 30 s plasma treatment. However, the bonding strength to plasma treated inner dentin did not show any improvement. It was found that plasma treatment of peripheral dentin surface up to 100 s gave an increase in interfacial bonding strength, while a prolong plasma treatment of dentin surfaces, e.g., 5 min treatments, showed a decrease in interfacial bonding strength. PMID:20831586

Aesthetic composite veneers for an adult patient with amelogenesis imperfecta: a case report.

Science.gov (United States)

Brignall, Ian; Mehta, Shamir B; Banerji, Subir; Millar, Brian J

2011-11-01

This case has been presented as part of the continual assessment requirement for the MSc in Aesthetic Dentistry, King's College Dental Institute. Amelogenesis imperfecta (AI) is a hereditary disorder of enamel formation, affecting both the permanent and deciduous dentitions. It can be classified into hypoplastic, hypomaturation and hypocalcified types and presents with different hereditary patterns. The aim of this article is to provide an overview of amelogenesis imperfecta, including a detailed case report for an aesthetically concerned adult patient presenting in general practice with a Witkop's Type IA defect managed with the placement of direct, layered resin composite veneers. Amelogenesis imperfecta patients are susceptible to the restorative cycle of replacement restorations like any other patient, but start with a distinct disadvantage.This case report demonstrates a minimally invasive, relatively simple and cost-effective option for the aesthetic correction of a case of hypoplastic amelogenesis imperfecta with layered composite veneers. Dent Update 2011; 38:594-603

Influence of light energy density on heat generation during photoactivation of dental composites with different dentin and composite thickness

Directory of Open Access Journals (Sweden)

Ricardo Danil Guiraldo

2009-08-01

Full Text Available OBJECTIVE: The aim of this study was to determine the influence of different energy densities on the heat generated during photoactivation of Filtek Z250 (3M/ESPE and Z100 (3M/ESPE composite resins with different dentin and composite thickness. MATERIAL AND METHODS: The temperature increase was registered with a type-K thermocouple connected to a digital thermometer (Iopetherm 46. A chemically polymerized acrylic resin base was prepared to serve as a guide for the thermocouple and as a support for 0.5-, 1.0-, and 1.5-mm-thick bovine dentin discs. Circular elastomer molds (1.0 mm-height x 3.0-mm diameter or 2.0-mm height x 3.0-mm diameter were adapted on the acrylic resin base to standardize the composite resin thickness. A conventional halogen light-curing unit (XL 2500, 3M/ESPE was used with light intensity of 700 mW/cm². Energy density was calculated by the light intensity applied during a certain time with values of 28 J/cm² for Z100 and 14 J/cm² for Filtek Z250. The temperature change data were subjected to three-way ANOVA and Tukey's test at 5% level. RESULTS: The higher energy density (Z100 promoted greater temperature increase (p<0.05 than the lower energy density (Filtek Z250. For both composites and all composite thicknesses, the lowest dentin thickness (0.5 mm yielded significantly higher (p<0.05 temperature increase than the other two dentin thicknesses. The 1-mm-thick composite resin layer yielded significantly higher (p<0.05 temperature changes for both composites and all dentin thicknesses. CONCLUSIONS: Temperature increase was influenced by higher energy density and dentin/composite thickness.

Randomized Clinical Trial of Indirect Resin Composite and Ceramic Veneers : Up to 3-year Follow-up

NARCIS (Netherlands)

Gresnigt, Marco M. M.; Kalk, Warner; Ozcan, Mutlu

2013-01-01

Purpose: This randomized controlled split-mouth clinical trial evaluated the short-term survival rate of indirect resin composite and ceramic laminate veneers. Materials and Methods: A total of 10 patients (mean age: 48.6 years) received 46 indirect resin composite (Estenia; n = 23) and ceramic

Damage Maps of Veneered Zirconia under Simulated Mastication

Science.gov (United States)

Kim, Jae-Won; Kim, Joo-Hyung; Janal, Malvin N.; Zhang, Yu

2016-01-01

Zirconia based restorations often fracture from chipping and/or delamination of the porcelain veneers. We hypothesize that veneer chipping/delamination is a result of the propagation of near-contact induced partial cone cracks on the occlusal surface under mastication. Masticatory loading involves the opposing tooth sliding along the cuspal inner incline surface with an applied biting force. To test this hypothesis, flat porcelain veneered zirconia plates were cemented to dental composites and cyclically loaded (contact–slide–liftoff) at an inclination angle as a simplified model of zirconia based restorations under occlusion. In the light of in-situ observation of damage evolution in a transparent glass/zirconia/polycarbonate trilayer, postmortem damage evaluation of porcelain/zirconia/composite trilayers using a sectioning technique revealed that deep penetrating occlusal surface partial cone fracture is the predominant fracture mode of porcelain veneers. Clinical relevance is discussed. PMID:19029080

Color management of porcelain veneers: influence of dentin and resin cement colors

NARCIS (Netherlands)

Dozic, A.; Tsagkari, M.; Khashayar, G.; Aboushelib, M.

2010-01-01

Objective: Porcelain veneers have become an interesting treatment option to correct the shape and color of anterior teeth. Because of their limited thickness and high translucency, achieving a good color match is influenced by several variables. The aim of this work was to investigate the influence

Shear Bond Strength of Composite to Nd-YAG Lased Dentin with and without Dye

Directory of Open Access Journals (Sweden)

H. Kermanshah

2004-06-01

Full Text Available Statement of Problem: The achievement of a good and durable dentin/composite resin bond is an important task in restorative dentistry. The application of acid conditioners and dentin bonding agents is an accepted method to enhance this bond strength. Pretreating of dentin surface by laser irradiation seems to be a supplemental way to obtain better results,since lased dentin is more roughened and has a widest surface area to interact with acidconditioner.Purpose: In this study, the effect of dentin surface pretreating by Nd-YAG laser on dentin/composite shear bond strength was examined. Moreover, the effect of Chinese ink as a surface energy absorber on this value was investigated.Methods and Materials: Thirty-nine freshly extracted human teeth without dentinal caries were collected and their occlusal dentins were exposed using a diamond disk. The collected samples were divided into three identical groups. The dentin surface of the first group was lased by an Nd-YAG pulsed laser (100 mJ, 20 Hz through a 320 mm fiber optic in a swiping movement. In the second group, 10% solution of Chinese ink was applied on the dentinal surface before lasing. The samples of the third group were not lased at all. Thedentinal surface prepared by 35% phosphoric acid and Scotchbond MP primer and adhesive. Then, composite resin was cured on dentinal surface. After incubation, in water at 37°C for 24 hours, the samples were tested by Digital Tritest ELE machine.Results: The values of bond strength were 20.83±3.96 MPa, 17.83±3.63 MPa and 19.38±4.88 MPa for the lased, unlased and dye-enhanced groups, respectively. The results were not significant by ANOVA test (a=0.05. Although in the Weiboul modulus, the lased group offered better bond strength.Conclusion: Further studies are required to determine whether chemical as well as physical alterations to the dentin surface are induced by laser etching, and whether these influence the performance of the range of dentin

Role of core support material in veneer failure of brittle layer structures.

Science.gov (United States)

Hermann, Ilja; Bhowmick, Sanjit; Lawn, Brian R

2007-07-01

A study is made of veneer failure by cracking in all-ceramic crown-like layer structures. Model trilayers consisting of a 1 mm thick external glass layer (veneer) joined to a 0.5 mm thick inner stiff and hard ceramic support layer (core) by epoxy bonding or by fusion are fabricated for testing. The resulting bilayers are then glued to a thick compliant polycarbonate slab to simulate a dentin base. The specimens are subjected to cyclic contact (occlusal) loading with spherical indenters in an aqueous environment. Video cameras are used to record the fracture evolution in the transparent glass layer in situ during testing. The dominant failure mode is cone cracking in the glass veneer by traditional outer (Hertzian) cone cracks at higher contact loads and by inner (hydraulically pumped) cone cracks at lower loads. Failure is deemed to occur when one of these cracks reaches the veneer/core interface. The advantages and disadvantages of the alumina and zirconia core materials are discussed in terms of mechanical properties-strength and toughness, as well as stiffness. Consideration is also given to the roles of interface strength and residual thermal expansion mismatch stresses in relation to the different joining methods. Copyright 2006 Wiley Periodicals, Inc.

Optical properties of composite restorations influenced by dissimilar dentin restoratives.

Science.gov (United States)

Marjanovic, Jovana; Veljovic, Djordje N; Stasic, Jovana N; Savic-Stankovic, Tatjana; Trifkovic, Branka; Miletic, Vesna

2018-05-01

To evaluate optical properties (color and translucency) of 'sandwich' restorations of resin-based composites and esthetically unfavorable dentin restoratives. Cylindrical 'dentin' specimens (8mm in diameter and 2mm thick, N=5/group) were prepared using EverX Posterior (GC), Biodentine (Septodont), experimental hydroxyapatite (HAP) or conventional composites (Gradia Direct Posterior, GC; Filtek Z250 and Filtek Z500, 3M ESPE). Capping 'enamel' layers were prepared using composites (Gradia Direct Posterior, Filtek Z250 or Z550) of A1 or A3 shade and the following thickness: 0.6, 1 or 2mm. Color (ΔE) and translucency parameter (TP) were determined using a spectrophotometer (VITA Easyshade Advance 4.0, VITA Zahnfabrik). Data were statistically analyzed using analysis of variance with Tukey's post-hoc tests (α=0.05). TP was greatly affected by layer thickness, whilst ΔE depended on shade and layer thickness of the capping composite. HAP and Biodentine showed significantly lower TP and higher ΔE (deviation from 'ideal white') than composites (p<0.05). Greater TP was seen in EverX_composite groups than in corresponding control groups of the same shade and thickness. TP of composites combined with Biodentine or HAP was below 2, lower than the corresponding control groups (p<0.05). Within-group differences of ΔE were greatest in HAP_composite groups. EverX_Gradia and EverX_FiltekZ250 combinations showed the most comparable ΔE with the control groups. A 2mm thick layer of composite covering dentin restoratives with unfavorable esthetics is recommended for a final 'sandwich' restoration that is esthetically comparable to a conventional, mono-composite control restoration. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.

Effect of Pre-heating on Microtensile Bond Strength of Composite Resin to Dentin.

Directory of Open Access Journals (Sweden)

Abdolrahim Davari

2014-10-01

Full Text Available Direct composite resin restorations are widely used and the impact of different storage temperatures on composites is not well understood. The purpose of this study was to evaluate the microtensile bond strength of composite to dentin after different pre-curing temperatures.Occlusal surfaces of 44 human molars were ground with diamond burs under water coolant and polished with 600 grit silicon carbide papers to obtain flat dentin surfaces. The dentin was etched with 37% phosphoric acid and bonded with Adper Single Bond 2 according to the manufacturer's instructions. The specimens were randomly divided into two groups (n=22 according to the composite resin applied: FiltekP60 and Filtek Z250. Each group included three subgroups of composite resin pre-curing temperatures (4°C, 23°C and 37°C. Composite resins were applied to the dentin surfaces in a plastic mold (8mm in diameter and 4mm in length incrementally and cured. Twenty-two composite-to-dentin hour-glass sticks with one mm(2 cross-sectional area per group were prepared. Microtensile bond strength measurements were made using a universal testing machine at a crosshead speed of one mm/min. For statistical analysis, t-test, one-way and two-way ANOVA were used. The level of significance was set at P<0.05.Filtek P60 pre-heated at 37ºC had significantly higher microtensile bond strength than Filtek Z250 under the same condition. The microtensile bond strengths were not significantly different at 4ºC, 23ºC and 37ºC subgroups of each composite resin group.Filtek P60 and Filtek Z250 did not have significantly different microtensile bond strengths at 4ºC and 23ºC but Filtek P60 had significantly higher microtensile bond strength at 37 ºC. Composite and temperature interactions had significant effects on the bond strength.

Effect of Provisional Cements on Shear Bond Strength of Porcelain Laminate Veneers

OpenAIRE

Altintas, Subutay Han; Tak, Onjen; Secilmis, Asli; Usumez, Aslihan

2011-01-01

Objectives: The purpose of this study was to evaluate the effect of three provisional cements and two cleaning techniques on the final bond strength of porcelain laminate veneers. Methods: The occlusal third of the crowns of forty molar teeth were sectioned and embedded in autopolymerizing acrylic resin. Dentin surfaces were polished and specimens were randomly divided into four groups (n=10). Provisional restorations were fabricated and two provisional restorations were cemented onto each to...

Calibration of a lactic-acid model for simulating biofilm-induced degradation of the dentin-composite interface.

Science.gov (United States)

Zhu, Laikuan; Li, Yuping; Carrera, Carola A; Chen, Yung-Chung; Li, Mingyu; Fok, Alex

2017-11-01

To verify and calibrate a chemical model for simulating the degradation of the dentin-composite interface induced by multi-species oral biofilms in vitro. Dentin-composite disks (5-mm dia.×2-mm thick) were made from bovine incisor roots and filled with either Z100™ (Z100) or Filtek™ LS (LS) composite. The disks, which were covered with nail varnish, but with one of the dentin-composite margins exposed, were immersed in lactic acid solution at pH 4.5 for up to 48h. Diametral compression was performed to measure the reduction in bond strength of the dentin-composite disks following acid challenge. Scanning electron microscopy (SEM) was used to examine decalcification of dentin and fracture modes of the disks. To better understand the degradation process, micro-computed tomography, in combination with a radiopaque dye (AgNO 3 ), was used to assess interfacial leakage in 3D longitudinally, while SEM was used to determine the path of leakage. One-way analysis of variance (ANOVA) was used to analyze the results, with the level of statistical significance set at pcomposite interface, instead. The degree of dentin demineralization, the reduction in debonding load and the modes of failure observed were very similar to those induced by multi-species oral biofilms found in the previous work. Leakage of AgNO 3 occurred mainly along the hybrid layer. The specimens filled with Z100 had a thicker hybrid layer (∼6.5μm), which exhibited more interfacial leakage than those filled with LS. The chemical model with lactic acid used in this study can induce degradation to the dentin-composite interface similar to those produced by multi-species biofilms. With appropriate calibration, this could provide an effective in vitro method for ageing composite restorations in assessing their potential clinical performance. Copyright © 2017 The Academy of Dental Materials. All rights reserved.

[Study on color of thermosetting resin for veneer crown].

Science.gov (United States)

Kamitomai, H

1989-02-01

Based on the viewpoint that stresses the importance of achieving natural colors and forms for veneer crown, four representative kinds of thermosetting resins were investigated colorimetrically in an attempt to clarify the relationship between the thickness and color of resins in opaque, dentin and enamel colors respectively. A spectrophotometer was used to measure the colors, the CIE colorimetric system employed to show the readings, and the CIE 1964 U*V*W* space was utilized to indicate the color differences, with the following results. 1. In the case of dentin, certain specific colors were observed for thickness of 1.3 to 1.8 mm when used alone, but when applied over opaque the range was 0.2 to 0.5 mm lower than when used alone. 2. Enamel resins were grouped into two types according to different color groups, one group similar to achromatic color with low limpidity and the other similar to the dentin color with high limpidity. The former type became more grayer with an increase in thickness when applied over dentin. The latter type showed no difference in color even when the thickness increased. This study has shown that the facing color results vary depending on the color properties of the different resins used. Therefore, it is advisable that careful consideration be given to these differencies in order to achieve the intended color facing.

Interfacial fracture of dentin adhesively bonded to quartz-fiber reinforced composite

International Nuclear Information System (INIS)

Melo, Renata M.; Rahbar, Nima; Soboyejo, Wole

2011-01-01

The paper presents the results of an experimental study of interfacial failure in a multilayered structure consisting of a dentin/resin cement/quartz-fiber reinforced composite (FRC). Slices of dentin close to the pulp chamber were sandwiched by two half-circle discs made of a quartz-fiber reinforced composite, bonded with bonding agent (All-bond 2, BISCO, Schaumburg) and resin cement (Duo-link, BISCO, Schaumburg) to make Brazil-nut sandwich specimens for interfacial toughness testing. Interfacial fracture toughness (strain energy release rate, G) was measured as a function of mode mixity by changing loading angles from 0 deg. to 15 deg. The interfacial fracture surfaces were then examined using Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDX) to determine the failure modes when loading angles changed. A computational model was also developed to calculate the driving forces, stress intensity factors and mode mixities. Interfacial toughness increased from ∼ 1.5 to 3.2 J/m 2 when the loading angle increases from ∼ 0 to 15 deg. The hybridized dentin/cement interface appeared to be tougher than the resin cement/quartz-fiber reinforced epoxy. The Brazil-nut sandwich specimen was a suitable method to investigate the mechanical integrity of dentin/cement/FRC interfaces.

Effectiveness of optical illusions 
applied on a single composite resin veneer for the diastema closure 
of maxillary central incisors.

Science.gov (United States)

Katsarou, Thomai; Antoniadou, Maria; Papazoglou, Efstratios

To assess the esthetic effectiveness of four illusion techniques applied to a composite resin veneer for diastema closure between maxillary central incisors. An acrylic model with six natural maxillary anterior teeth was fabricated with a 2-mm diastema between the central incisors. Resin veneers were constructed on the left central incisor and the following cases were derived: V0: no veneer; V1: veneer without optical illusion features; V2: veneer with centralized interproximal ridges; V3: veneer with curved incisal edges; V4: veneer with gray pigment mesially/distally; V5: veneer with gray pigment on the developmental lobes. Digital printed photos of the models (13.2 x 17.8 cm, and 6.1 x 8 cm), with low, medium, and high smile lines and without a smile line (processed by Adobe Photoshop CS6) were shown to three groups of people (faculty members, senior undergraduate students, and patients; n = 25/group) for them to assess the overall size and width of the two central incisors. The results were analyzed by Pearson's and chi-square goodness of fit tests. There was no significant influence in the estimation of the two central incisors as being the same size, according to the technique used (P = 0.869) and group of evaluators (P = 0.209). The estimated probability of assessing the tested incisor as wider was indicatively lower in V2 compared to V1 (adjusted odds ratio = 0.59; P = 0.088). The height of the smile line affected the evaluation of the veneers only in the large-sized photos. No interference is the best esthetic decision concerning a 2-mm diastema closure when restoring only one central incisor with a laminate veneer. The next best option is to deliver a veneer with centralized interproximal ridges.

Effect of Static and Cyclic Loading on Ceramic Laminate Veneers Adhered to Teeth with and Without Aged Composite Restorations

NARCIS (Netherlands)

Gresnigt, Marco M. M.; Ozcan, Mutlu; Kalk, Warner; Galhano, Graziela

2011-01-01

Purpose: Existing composite restorations on teeth are often remade prior to the cementation of fixed dental prostheses. The aim of this study was to evaluate the effect of static and cyclic loading on ceramic laminate veneers adhered to aged resin composite restorations. Materials and Methods:

Effect of dentin dehydration and composite resin polymerization mode on bond strength of two self-etch adhesives

Directory of Open Access Journals (Sweden)

Pooran Samimi

2016-01-01

Full Text Available Background: Dual-cured composite resins are similar to self-cured composite resins in some of their clinical applications due to inadequate irradiation, lack of irradiation, or delayed irradiation. Therefore, incompatibility with self-etch adhesives (SEAs should be taken into account with their use. On the other, the extent of dentin dehydration has a great role in the quality of adhesion of these resin materials to dentin. The aim of this study was to investigate the effect of dentin dehydration and composite resin polymerization mode on bond strength of two SEAs. Materials and Methods: A total of 120 dentinal specimens were prepared from extracted intact third molars. Half of the samples were dehydrated in ethanol with increasing concentrations. Then Clearfil SE Bond (CSEB and Prompt L-Pop (PLP adhesives were applied in the two groups. Cylindrical composite resin specimens were cured using three polymerization modes: (1 Immediate light-curing, (2 delayed light-curing after 20 min, and (3 self-curing. Bond strength was measured using universal testing machine at a crosshead speed of 1 mm/min. Data were analyzed with two-way ANOVA and Duncan post hoc tests. Statistical significance was defined at P 0.05. PLP showed significant differences between subgroups with the lowest bond strength in hydrated dentin with delayed light-curing and self-cured mode of polymerization. Conclusion: Within the limitations of this study, a delay in composite resin light-curing or using chemically cured composite resin had a deleterious effect on dentin bond strength of single-step SEAs used in the study.

Solvent composition of one-step self-etch adhesives and dentine wettability.

Science.gov (United States)

Grégoire, Geneviève; Dabsie, Firas; Dieng-Sarr, Farimata; Akon, Bernadette; Sharrock, Patrick

2011-01-01

Our aim was to determine the wettability of dentine by four commercial self-etch adhesives and evaluate their spreading rate on the dentine surface. Any correlation with chemical composition was sought, particularly with the amount of solvent or HEMA present in the adhesive. The adhesives used were AdheSE One, Optibond All.In.One, Adper Easy Bond and XenoV. Chemical compositions were determined by proton nuclear magnetic resonance (NMR) spectroscopy of the adhesives dissolved in dimethylsulfoxide. Apparent contact angles for sessile drops of adhesives were measured on dentine slices as a function of time for up to 180s. The water contact angles were determined for fully polymerised adhesives. All adhesives were water-based with total solvent contents ranging from 27% to 73% for HEMA-free adhesives, and averaging 45% for HEMA containing adhesives. The contents in hydrophobic groups decreased as water contents increased. No differences were found in the adhesive contact angles after 180s even though the spreading rates were different for the products tested. Water contact angles differed significantly but were not correlated with HEMA or solvent presence. Manufacturers use different approaches to stabilise acid co-monomer ingredients in self-etch adhesives. Co-solvents, HEMA, or acrylamides without co-solvents are used to simultaneously etch and infiltrate dentine. A large proportion of water is necessary for decalcification action. Copyright © 2010 Elsevier Ltd. All rights reserved.

Main Clinical Outcomes of Feldspathic Porcelain and Glass-Ceramic Laminate Veneers: A Systematic Review and Meta-Analysis of Survival and Complication Rates.

Science.gov (United States)

Morimoto, Susana; Albanesi, Rafael Borges; Sesma, Newton; Agra, Carlos Martins; Braga, Mariana Minatel

2016-01-01

The aim of this study was to perform a systematic review and meta-analysis based on clinical trials that evaluated the main outcomes of glass-ceramic and feldspathic porcelain laminate veneers. A systematic search was carried out in Cochrane and PubMed databases. From the selected studies, the survival rates for porcelain and glass-ceramic veneers were extracted, as were complication rates of clinical outcomes: debonding, fracture/chipping, secondary caries, endodontic problems, severe marginal discoloration, and influence of incisal coverage and enamel/dentin preparation. The Cochran Q test and the I(2) statistic were used to evaluate heterogeneity. Out of the 899 articles initially identified, 13 were included for analysis. Metaregression analysis showed that the types of ceramics and follow-up periods had no influence on failure rate. The estimated overall cumulative survival rate was 89% (95% CI: 84% to 94%) in a median follow-up period of 9 years. The estimated survival for glass-ceramic was 94% (95% CI: 87% to 100%), and for feldspathic porcelain veneers, 87% (95% CI: 82% to 93%). The meta-analysis showed rates for the following events: debonding: 2% (95% CI: 1% to 4%); fracture/chipping: 4% (95% CI: 3% to 6%); secondary caries: 1% (95% CI: 0% to 3%); severe marginal discoloration: 2% (95% CI: 1% to 10%); endodontic problems: 2% (95% CI: 1% to 3%); and incisal coverage odds ratio: 1.25 (95% CI: 0.33 to 4.73). It was not possible to perform meta-analysis of the influence of enamel/dentin preparation on failure rates. Glass-ceramic and porcelain laminate veneers have high survival rates. Fracture/ chipping was the most frequent complication, providing evidence that ceramic veneers are a safe treatment option that preserve tooth structure.

Microshear bond strength of preheated silorane- and methacrylate-based composite resins to dentin.

Science.gov (United States)

Demirbuga, Sezer; Ucar, Faruk Izzet; Cayabatmaz, Muhammed; Zorba, Yahya Orcun; Cantekin, Kenan; Topçuoğlu, Hüseyin Sinan; Kilinc, Halil Ibrahim

2016-01-01

The aim of this study was to investigate the effect of preheating on microshear bond strength (MSBS) of silorane and methacrylate-based composite resins to human dentin. The teeth were randomly divided into three main groups: (1) composite resins were heated upto 68 °C; (2) cooled to 4 °C; and (3) control [room temperature (RT)]. Each group was then randomly subdivided into four subgroups according to adhesive system used [Solobond M (Voco), All Bond SE (Bisco), Clearfil SE Bond (CSE) (Kuraray), Silorane adhesive system (SAS) (3M ESPE)]. Resin composite cylinders were formed (0.9 mm diameter × 0.7 mm length) and MSBS of each specimen was tested. The preheated groups exhibited the highest MSBS (p composite resins may be an alternative way to increase the MSBS of composites on dentin. © Wiley Periodicals, Inc.

Failure in a composite resin-dentin adhesive bond

Energy Technology Data Exchange (ETDEWEB)

Rezgui, B. (Dept. de Genie Mecanique, Ecole Nationale d' Ingenieurs de Monastir, Monastir (Tunisia)); Abdennagi, H. (Dept. de Genie Mecanique, Ecole Nationale d' Ingenieurs de Monastir, Monastir (Tunisia)); Sahtout, S. (Dept. de Genie Mecanique, Ecole Nationale d' Ingenieurs de Monastir, Monastir (Tunisia) Dept. d' Odontologie, Faculte de Chirurgie Dentaire de Monastir (Tunisia)); Belkhir, M.S. (Dept. de Genie Mecanique, Ecole Nationale d' Ingenieurs de Monastir, Monastir (Tunisia) Dept. d' Odontologie, Faculte de Chirurgie Dentaire de Monastir (Tunisia))

1993-11-01

Composites are drawing more and more attention as preferred materials for teeth restoration. The success of teeth restoration has been generally limited by the Composite Resin-Dentin bond strength. A testing device has been developped to allow a satisfactory testing method for evaluating bonding strength in tension and shear, which led to reproducible results. A comparaison between different bond systems has shown no significant difference in the tensile and the shear strength as well as in the fracture behavior. Moreover, results showed difference between tensile and shear strength, when considering one same bond system. Failure mode examination turned out to be, either cohesive (composite rupture), or adhesive (interface rupture) or both (mixed rupture). (orig.).

Ultrathin CAD-CAM Ceramic Occlusal Veneers and Anterior Bilaminar Veneers for the Treatment of Moderate Dental Biocorrosion: A 1.5-Year Follow-Up.

Science.gov (United States)

Resende, T H; Reis, K R; Schlichting, L H; Magne, P

2018-03-27

Dental biocorrosion can produce a devastating impact on oral health. The restorative phase of the treatment should not cause additional damage of the remaining sound tooth structure. Ultrathin occlusal veneers are a conservative alternative to traditional onlays and complete crowns for the treatment of severe biocorrosive lesions. This strategy is explained in the present case report through a full-mouth rehabilitation of a patient with moderate biocorrosion. Maxillary anterior teeth were restored using the bilaminar technique (lingual direct composite veneers with labial ceramic veneers) and posterior teeth using ultrathin CAD-CAM ceramic occlusal veneers. The technical aspects required for the implementation of this new restorative design are presented with a special emphasis on the control of tooth preparation based on diagnostic wax-up, provisionalization, and the use of CAD-CAM technology.

Tensile bond strength of indirect composites luted with three new self-adhesive resin cements to dentin

Directory of Open Access Journals (Sweden)

Cafer Türkmen

2011-08-01

Full Text Available OBJECTIVE: The aims of this study were to evaluate the tensile bond strengths between indirect composites and dentin of 3 recently developed self-adhesive resin cements and to determine mode of failure by SEM. MATERIAL AND METHODS: Exposed dentin surfaces of 70 mandibular third molars were used. Teeth were randomly divided into 7 groups: Group 1 (control group: direct composite resin restoration (Alert with etch-and-rinse adhesive system (Bond 1 primer/adhesive, Group 2: indirect composite restoration (Estenia luted with a resin cement (Cement-It combined with the same etch-and-rinse adhesive, Group 3: direct composite resin restoration with self-etch adhesive system (Nano-Bond, Group 4: indirect composite restoration luted with the resin cement combined with the same self-etch adhesive, Groups 5-7: indirect composite restoration luted with self-adhesive resin cements (RelyX Unicem, Maxcem, and Embrace WetBond, respectively onto the non-pretreated dentin surfaces. Tensile bond strengths of groups were tested with a universal testing machine at a constant speed of 1 mm/min using a 50 kgf load cell. Results were statistically analyzed by the Student's t-test. The failure modes of all groups were also evaluated. RESULTS: The indirect composite restorations luted with the self-adhesive resin cements (groups 5-7 showed better results compared to the other groups (p0.05. The surfaces of all debonded specimens showed evidence of both adhesive and cohesive failure. CONCLUSION: The new universal self-adhesive resins may be considered an alternative for luting indirect composite restorations onto non-pretreated dentin surfaces.

Amalgam stained dentin: a proper substrate for bonding resin composite?

NARCIS (Netherlands)

Scholtanus, J.D.

2016-01-01

Nowadays the use of dental amalgam is mostly abandoned and substituted by tooth colored resin composites that can be bonded to teeth tissues by adhesive techniques. The aim of this thesis was to find out whether dark stained dentin, as often observed after removal of amalgam restorations and

The effect of veneering and heat treatment on the flexural strength of Empress 2 ceramics.

Science.gov (United States)

Cattell, M J; Palumbo, R P; Knowles, J C; Clarke, R L; Samarawickrama, D Y D

2002-05-01

The aims of the study were to test and compare the biaxial flexural strength and reliability of Empress 2 ceramics after heat treatment and the addition of the veneering material and to characterise their microstructures. Forty disc specimens (2 x 14 mm) and forty disc specimens (1 x 14 mm) were produced by heat pressing in the EP 500 press furnace. Group 1 (2 x 14 mm Empress 2 core) was as heat pressed and group 2 (2 x 14 mm Empress 2 core) was subjected to the recommended firing cycles. Groups 3 and 4 (1 x 14 mm Empress 2 core) were veneered with the dentine material and heat-treated as per group 2. Groups 1, 2 and 3 were lapped to 800 grit silicon carbide paper on the compressive surface only and group 4 on both the compressive and tensile test surfaces. Twenty disc specimens per group were tested using the biaxial flexure test at a crosshead speed of 0.15 mm/min. Specimens were characterised using X-ray diffraction (XRD) and secondary electron imaging (SEM). Mean biaxial flexural strengths (MPa+/-SD) were group 1: 265.5+/-25.7; group 2: 251.3+/-30.2; group 3: 258.6+/-21.4 and group 4: 308.6+/-37.7. There was no statistical difference between groups 1, 2 and 3 (p>0.05), but differences for group 4 (pEmpress 2 core material and an amorphous glass and some evidence of a crystalline phase in the dentine material. CONCLUSIONS; Veneering or heat treatment of Empress 2 ceramics did not significantly affect the mean biaxial flexural strength (p>0.05) or reliability. Surface modification of the Empress 2 core material increased the mean biaxial flexural strength (p<0.05).

Laboratory evaluation of the effect of unfilled resin after the use of self-etch and total-etch dentin adhesives on the Shear Bond Strength of composite to dentin.

Science.gov (United States)

Nasseri, Ehsan Baradaran; Majidinia, Sara; Sharbaf, Davood Aghasizadeh

2017-05-01

Based on the frequent application of composite resins as tooth-colored fillings, this method is considered a viable alternative to dental amalgam. However, this method has the low bond strength of the composite to dentin. To solve this issue, various dental adhesive systems with different characteristics have been developed by dentistry experts. To assess the effect of an additional layer of unfilled resin in self-etch and total-etch dentin adhesives on the shear bond strength (SBS) of composite to dentin. Moreover, we assessed the effects of sample storage in artificial saliva on the SBS of composite to dentin. Methods: This experimental study was conducted on 160 freshly extracted human first or second premolar teeth, which were randomly divided into 16 groups. The teeth were prepared from Mashhad University of Medical Sciences, Mashhad, Iran (2008-2009). Scotchbond Multi-purpose (SBMP), single bond (SB), Clearfil SE Bond, and Clearfil S3 Bond were applied to dentin surface with or without the placement of hydrophobic resin (Margin Bond) in accordance with the instructions of the manufacturers. To expose the coronal dentin, the teeth were abraded with 600 grit SiC paper. Immediately after restoration, half of the samples were tested in terms of SBS, while the other samples were evaluated in terms of SBS after three months of storage in artificial saliva. SBS rates of dental composites evaluated by universal testing machine and samples were studied by optical stereomicroscopy to verify the failure type. Data analysis was performed in SPSS V.16 using Kolmogorov-Smirnov test, independent-samples t-test, ANOVA, and Duncan's logistic regression test. In this study, a significant reduction was observed in the SBS rates of SB and S3 bond adhesive systems after storage with and without hydrophobic resin (p>0.000). Without storage in normal saline, a significant increase was observed in the SBS rate of the SE bond (p=0.013). In addition, SBS rate of SBMP significantly

Comparison of silorane and methacrylate-based composites on the polymerization heat generated with different light-curing units and dentin thicknesses.

Science.gov (United States)

Guiraldo, Ricardo Danil; Consani, Simonides; Consani, Rafael Leonardo Xediek; Berger, Sandrine Bittencourt; Correr, Américo Bortolazzo; Sinhoreti, Mário Alexandre Coelho; Correr-Sobrinho, Lourenço

2013-01-01

This study evaluated the temperature variation in the pulp chamber during photoactivation of two restorative composite resins (Filtek P90 silorane-based composite and Heliomolar methacrylate-based composite) with either a quartz-tungsten-halogen (QTH) or light-emitting diodes (LED) light-curing unit (LCU) and using dentin thicknesses (0.5 and 1.0 mm). Standardized cavities (2x2x2 mm) were prepared in 80 bovine incisors, which were randomly assigned to 8 groups according to the photoactivation method and dentin thickness. Filtek P90 and Heliomolar (both in shade A3) were used with their respective adhesive systems (P90 self-etch primer / P90 adhesive bond and Excite adhesive). All experiments were carried out in a controlled environment (37°C). The temperature variations (°C) were recorded using a digital thermometer attached to a K-type thermocouple. The results were analyzed statistically by ANOVA and Tukey's test (α=0.05). For composite/dentin thickness interaction, temperature increase was significantly higher in 0.5 mm dentin thickness (40.07°C) compared with 1.0 mm dentin thickness (39.61°C) for Filtek P90. For composite/LCU interaction, the temperature increase was significantly higher for Filtek P90 (39.21°C - QTH and 40.47°C - LED) compared with Heliomolar (38.40°C - QTH and 39.30°C - LED). The silorane-based composite promoted higher temperature increase in the pulp chamber than the methacrylate-based composite.

Accelerated fatigue testing of dentin-composite bond with continuously increasing load.

Science.gov (United States)

Li, Kai; Guo, Jiawen; Li, Yuping; Heo, Young Cheul; Chen, Jihua; Xin, Haitao; Fok, Alex

2017-06-01

The aim of this study was to evaluate an accelerated fatigue test method that used a continuously increasing load for testing the dentin-composite bond strength. Dentin-composite disks (ϕ5mm×2mm) made from bovine incisor roots were subjected to cyclic diametral compression with a continuously increasingly load amplitude. Two different load profiles, linear and nonlinear with respect to the number of cycles, were considered. The data were then analyzed by using a probabilistic failure model based on the Weakest-Link Theory and the classical stress-life function, before being transformed to simulate clinical data of direct restorations. All the experimental data could be well fitted with a 2-parameter Weibull function. However, a calibration was required for the effective stress amplitude to account for the difference between static and cyclic loading. Good agreement was then obtained between theory and experiments for both load profiles. The in vitro model also successfully simulated the clinical data. The method presented will allow tooth-composite interfacial fatigue parameters to be determined more efficiently. With suitable calibration, the in vitro model can also be used to assess composite systems in a more clinically relevant manner. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Structure and composition of enamel and dentin after thermal treatment or infrared laser irradiation

International Nuclear Information System (INIS)

Bachmann, Luciano

2004-01-01

The main purpose of this work is to identify the crystallographic structure, optical properties, chemical composition and electron paramagnetic signals that laser irradiation or oven heating produces on the tissue. The thermal treatment was conducted in oven with temperature range below 1000 deg C and the laser irradiation with holmium (Ho:YLF - 2,065 μm) and erbium (Er:YAG - 2,94 μm) laser. The tissue characterization was carried out with X-ray diffraction, scanning electron microscopy, ultraviolet and visible transmission spectroscopy, light microscopy, infrared transmission/reflection spectroscopy and electron paramagnetic resonance. The holmium irradiated enamel (600-800 J/cm 2 ) shows the presence of tetracalcium phosphate that coexists with the natural phase (hydroxyapatite). The irradiated dentin shows only the sharper diffraction peaks of the natural phase. The narrows peaks, observed after irradiation, could be assigned to the dentin crystal growth and impurities elimination. Tissue discoloration is observed after thermal treatment with temperatures above 100 deg C. Heated enamel become white-opaque and the origin is assigned to the water elimination, which promotes higher light scattering by the prismatic structure. On the other hand, heated dentin, with similar temperatures becomes brown. The dentin browning changes with the temperature and shown two peaks, at 375 deg C and 700 deg C. The peak at 375 deg C is assigned to the collagen structure degradation and at 700 deg C to the cyanate formation. The dentin discoloration produced with temperatures below 200 deg C is reversible after the tissue hydration. Both enamel and dentin discoloration are also observed in erbium irradiated tissues. Thermal treatments, heating in oven or laser irradiation, change mainly the organic matrix composition and water present in the tissues. The inorganic matrix is more stable and its radicals are changed, with more predominance, only at temperatures higher than 500 deg

Synthesis of Calcium Phosphate Composite Organogels by Using Emulsion Method for Dentine Occlusion Materials

Science.gov (United States)

Nopteeranupharp, C.; Akkarachaneeyakorn, K.; Songsasaen, A.

2018-03-01

Dentinal hypersensitivity (DH) is one of the most human’s problems caused by the erosion of enamel. There are many methods and materials to solve this problem. Calcium phosphate is an excellent alternative for curing this symptom because of its osteoconductivity, and biocompatibility properties. The low-cost and low-toxicity calcium phosphate nanogel was fabricated by using emulsion method and characterized by using TEM, EDX, and DLS techniques. The results showed that P123 (poly (ethylene oxide)19-block-Poly (propylene oxide)69-block-poly (ethylene oxide)19) has played a major role as template and gel formation, SDS was used as a surfactant to form water-in-oil emulsion nanodroplets with circle-like shape. Moreover, the ability of synthesised organogel to occlude the exposed dentine tubules was tested on the model of human’s dentine slices. The results showed that calcium phosphate composite organogel can be efficiently occluded on dentine slice, characterized by SEM technique, after 1 day.

Effect of stacking sequence on mechanical properties neem wood veneer plastic composites

Science.gov (United States)

Nagamadhu, M.; Kumar, G. C. Mohan; Jeyaraj, P.

2018-04-01

This study investigates the effect of wood veneer stacking sequence on mechanical properties of neem wood polymer composite (WPC) experimentally. Wood laminated samples were fabricated by conventional hand layup technique in a mold and cured under pressure at room temperature and then post cured at elevated temperature. Initially, the tensile, flexural, and impact test were conducted to understand the effect of weight fraction of fiber on mechanical properties. The mechanical properties have increased with the weight fraction of fiber. Moreover the stacking sequence of neem wood plays an important role. As it has a significant impact on the mechanical properties. The results indicated that 0°/0° WPC shows highest mechanical properties as compared to other sequences (90°/90°, 0°/90°, 45°/90°, 45°/45°). The Fourier Transform Infrared Spectroscopy (FTIR) Analysis were carried out to identify chemical compounds both in raw neem wood and neem wood epoxy composite. The microstructure raw/neat neem wood and the interfacial bonding characteristics of neem wood composite investigated using Scanning electron microscopy images.

ESTIMATING THE SIZE OF LATE VENEER IMPACTORS FROM IMPACT-INDUCED MIXING ON MERCURY

International Nuclear Information System (INIS)

Rivera-Valentin, E. G.; Barr, A. C.

2014-01-01

Late accretion of a ''veneer'' of compositionally diverse planetesimals may introduce chemical heterogeneity in the mantles of the terrestrial planets. The size of the late veneer objects is an important control on the angular momenta, eccentricities, and inclinations of the terrestrial planets, but current estimates range from meter-scale bodies to objects with diameters of thousands of kilometers. We use a three-dimensional global Monte Carlo model of impact cratering, excavation, and ejecta blanket formation to show that evidence of mantle heterogeneity can be preserved within ejecta blankets of mantle-exhuming impacts on terrestrial planets. Compositionally distinct provinces implanted at the time of the late veneer are most likely to be preserved in bodies whose subsequent geodynamical evolution is limited. Mercury may have avoided intensive mixing by solid-state convection during much of its history. Its subsequent bombardment may have then excavated evidence of primordial mantle heterogeneity introduced by the late veneer. Simple geometric arguments can predict the amount of mantle material in the ejecta blanket of mantle-exhuming impacts, and deviations in composition relative to geometric predictions can constrain the length-scale of chemical heterogeneities in the subsurface. A marked change in the relationship between mantle and ejecta composition occurs when chemically distinct provinces are ∼250 km in diameter; thus, evidence of bombardment by thousand-kilometer-sized objects should be readily apparent from the variation in compositions of ejecta blankets in Mercury's ancient cratered terrains

Curing mode affects bond strength of adhesively luted composite CAD/CAM restorations to dentin.

Science.gov (United States)

Lührs, Anne-Katrin; Pongprueksa, Pong; De Munck, Jan; Geurtsen, Werner; Van Meerbeek, Bart

2014-03-01

To determine the effect of curing mode and restoration-surface pre-treatment on the micro-tensile bond strength (μTBS) to dentin. Sandblasted CAD/CAM composite blocks (LAVA Ultimate, 3M ESPE) were cemented to bur-cut dentin using either the etch & rinse composite cement Nexus 3 ('NX3', Kerr) with Optibond XTR ('XTR', Kerr), or the self-etch composite cement RelyX Ultimate ('RXU', 3M ESPE) with Scotchbond Universal ('SBU', 3M ESPE). All experimental groups included different 'curing modes' (light-curing of adhesive and cement ('LL'), light-curing of adhesive and auto-cure of cement ('LA'), co-cure of adhesive through light-curing of cement ('AL'), or complete auto-cure ('AA')) and different 'restoration-surface pre-treatments' of the composite block (NX3: either a silane primer (Kerr), or the XTR adhesive; RXU: either silane primer (RelyX Ceramic Primer, 3M ESPE) and SBU, or solely SBU). After water-storage (7 days, 37°C), the μTBS was measured. Additionally, the degree of conversion (DC) of both cements was measured after 10min and after 1 week, either auto-cured (21°C/37°C) or light-cured (directly/through 3-mm CAD/CAM composite). The linear mixed-effects model (α=0.05) revealed a significant influence of the factors 'curing mode' and 'composite cement', and a less significant effect of the factor 'restoration-surface pre-treatment'. Light-curing 'LL' revealed the highest μTBS, which decreased significantly for all other curing modes. For curing modes 'AA' and 'AL', the lowest μTBS and a high percentage of pre-testing failures were reported. Overall, DC increased with light-curing and incubation time. The curing mode is decisive for the bonding effectiveness of adhesively luted composite CAD/CAM restorations to dentin. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Evaluation of the retentive means, opacifiers and veneering materials for veneered crowns using 137 Cs

International Nuclear Information System (INIS)

Nour, A.M.; El-Sadeek; M.E.; Ramadan, F.A.; Eskander, M.

1991-01-01

The purpose of this investigation is to evaluate the best plastic veneering material, which affords initial sealing and adaptation to the metal backing. Cs chloride is used for this purpose. The effect of different retentive means, namely, under cuts, wire loops, stainless steel grills, and acrylic beads, as well as the effect of different opaquers were studied. The influence of time factor and changing temperature was considered as well. The results obtained showed the following: 1- A quantitative method for the evaluation of micro leakage is essential parallel to the semiquantitative one. 2- The tested opaquer exhibits a better sealing ability. 3- The leakage increases significantly by temperature cycling, and by time duration with all the veneering materials tested. Composite is the least leak-sensitive material to changes in temperature. 4- Beads offered the best means of retention, to obtain the best sealing qualities.1 tab., 2 fig

Mechanochemically synthesized kalsilite based bioactive glass-ceramic composite for dental vaneering

Science.gov (United States)

Kumar, Pattem Hemanth; Singh, Vinay Kumar; Kumar, Pradeep

2017-08-01

Kalsilite glass-ceramic composites have been prepared by a mechanochemical synthesis process for dental veneering application. The aim of the present study is to prepare bioactive kalsilite composite material for application in tissue attachment and sealing of the marginal gap between fixed prosthesis and tooth. Mechanochemical synthesis is used for the preparation of microfine kalsilite glass-ceramic. Low temperature frit and bioglass have been prepared using the traditional quench method. Thermal, microstructural and bioactive properties of the composite material have been examined. The feasibility of the kalsilite to be coated on the base commercial opaque as well as the bioactive behavior of the coated specimen has been confirmed. This study indicates that the prepared kalsilite-based composites show similar structural, morphological and bioactive behavior to that of commercial VITA VMK95 Dentin 1M2.

Influence of veneer thickness on residual stress profile in veneering ceramic: measurement by hole-drilling.

Science.gov (United States)

Mainjot, Amélie K; Schajer, Gary S; Vanheusden, Alain J; Sadoun, Michaël J

2012-02-01

The veneering process of frameworks induces residual stresses and can initiate cracks when combined with functional stresses. The stress distribution within the veneering ceramic as a function of depth is a key factor influencing failure by chipping. This is a well-known problem with Yttria-tetragonal-zirconia-polycrystal based fixed partial dentures. The objective of this study is to investigate the influence of veneer thickness on the stress profile in zirconia- and metal-based structures. The hole-drilling method, often used for engineering measurements, was adapted for use with veneering ceramic. The stress profile was measured in bilayered disc samples of 20 mm diameter, with a 1 mm thick zirconia or metal framework. Different veneering ceramic thicknesses were performed: 1 mm, 1.5 mm, 2 mm, 2.5 mm and 3 mm. All samples exhibited the same type of stress vs. depth profile, starting with compressive at the ceramic surface, decreasing with depth up to 0.5-1.0 mm from the surface, and then becoming compressive again near the framework, except for the 1.5 mm-veneered zirconia samples which exhibited interior tensile stresses. Stresses in the surface of metal samples were not influenced by veneer thickness. Variation of interior stresses at 1.2 mm from the surface in function of veneer thickness was inverted for metal and zirconia samples. Veneer thickness influences in an opposite way the residual stress profile in metal- and in zirconia-based structures. A three-step approach and the hypothesis of the crystalline transformation are discussed to explain the less favorable residual stress development in zirconia samples. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Origin and mixing timescale of Earth's late veneer

Science.gov (United States)

Prescher, C.; Allu Peddinti, D.; Bell, E. A.; Bello, L.; Cernok, A.; Ghosh, N.; Tucker, J.; Wielicki, M. M.; Zahnle, K. J.

2012-12-01

Experimental studies on the partitioning behavior of highly siderophile elements (HSE) between silicate and metallic melts imply that the Earth's mantle should have been highly depleted in these elements by core formation in an early magma ocean. However, present HSE contents of the Earth's mantle are ~3 orders of magnitude higher than that expected by experiments. The apparent over-abundance of HSE has commonly been explained by the addition of meteoritic material in the "late veneer" which describes the exogenous mass addition following the moon forming impact and concluding with the late heavy bombardment at ~3.8-3.9 Ga. The strongest evidence for this theory is that the platinum group element (PGE) contents in today's mantle are present in chondritic relative abundances, as opposed to a fractionated pattern expected with metal-silicate partitioning. Archean komatiites indicate that the PGE content of the Earth's mantle increased from about half their present abundances at 3.5 Ga to their present abundances at 2.9 Ga. This secular increase in PGE content suggests a progressive mixing of the late veneer material into the Earth's mantle. However, this time scale also implies that the whole mantle was relatively well mixed by 2.9 Ga. We use a compilation of existing isotopic and trace element data in order to constrain the origin and composition of the late veneer. We use PGE abundances, W abundances and W isotopic compositions in chondritic meteorites and the primitive upper mantle to compute the amount of mass delivered during the late veneer and find the late veneer mass to be ~0.6 % the mass of the bulk silicate Earth (consistent with earlier estimates). We also use the 187Re-187Os and 190Pt-186Os systems to constrain the composition and timing of delivery of the impacting population. We model the efficiency of mantle mixing in this time frame by using 3-dimensional numerical geodynamical simulations and geochemical constraints. Initial parameters include the

Arab Societal Awareness of Dental Veneers.

Science.gov (United States)

Alfouzan, Afnan; Al-Sanie, Aisha A; Al-Dhafiri, Reem A

2018-03-01

The aim of this study is to assess the Arab society's knowledge, awareness, and attitudes toward dental veneers. A cross-sectional study was performed by collecting data through an online questionnaire created using the Survey Monkey website and distributed among Middle Eastern societies through social media to ascertain participants' knowledge and awareness regarding dental veneers. The sample included Arab laypeople who were over 18 years old, to represent the awareness of the majority regarding dental veneers. The sample of this study included 1,332 subjects from different Middle Eastern nationalities, mainly Saudis, Kuwaitis, and Emiratis (15.6% of males and 84.4% of females). The results of this study showed that the total knowledge of dental veneers is 50.12%. The respondents with the highest level of knowledge acquired their information mainly from newspapers and magazines, followed by the Internet, then dentists, then social media, and, finally, friends and relatives. Cost was the only factor limiting 38.4% of subjects from receiving veneers, and 56% of the subjects would receive veneers if they were free of cost. In total, 72.6% of the respondents believed that veneers are currently overused. The knowledge and awareness of dental veneers were below a satisfactory level. Participants who relied on social media as a source of information had lower knowledge levels. This study emphasized the need for continual societal education regarding dental veneers.

Demineralized dentin matrix composite collagen material for bone tissue regeneration.

Science.gov (United States)

Li, Jianan; Yang, Juan; Zhong, Xiaozhong; He, Fengrong; Wu, Xiongwen; Shen, Guanxin

2013-01-01

Demineralized dentin matrix (DDM) had been successfully used in clinics as bone repair biomaterial for many years. However, particle morphology of DDM limited it further applications. In this study, DDM and collagen were prepared to DDM composite collagen material. The surface morphology of the material was studied by scanning electron microscope (SEM). MC3T3-E1 cells responses in vitro and tissue responses in vivo by implantation of DDM composite collagen material in bone defect of rabbits were also investigated. SEM analysis showed that DDM composite collagen material evenly distributed and formed a porous scaffold. Cell culture and animal models results indicated that DDM composite collagen material was biocompatible and could support cell proliferation and differentiation. Histological evaluation showed that DDM composite collagen material exhibited good biocompatibility, biodegradability and osteoconductivity with host bone in vivo. The results suggested that DDM composite collagen material might have a significant clinical advantage and potential to be applied in bone and orthopedic surgery.

Shear bond strength of composite to deep dentin after treatment with two different collagen cross-linking agents at varying time intervals.

Science.gov (United States)

Srinivasulu, S; Vidhya, S; Sujatha, M; Mahalaxmi, S

2012-01-01

This in vitro study evaluated the shear bond strength of composite resin to deep dentin using a total etch adhesive after treatment with two collagen cross-linking agents at varying time intervals. Thirty freshly extracted human maxillary central incisors were sectioned longitudinally into equal mesial and distal halves (n=60). The proximal deep dentin was exposed, maintaining a remaining dentin thickness (RDT) of approximately 1 mm. The specimens were randomly divided into three groups based on the surface treatment of dentin prior to bonding as follows: group I (n=12, control): no prior dentin surface treatment; group II (n=24): dentin surface pretreated with 10% sodium ascorbate; and group III (n=24): dentin surface pretreated with 6.5% proanthocyanidin. Groups II and III were further subdivided into two subgroups of 12 specimens each, based on the pretreatment time of five minutes (subgroup A) and 10 minutes (subgroup B). Shear bond strength of the specimens was tested with a universal testing machine, and the data were statistically analyzed. Significantly higher shear bond strength to deep dentin was observed in teeth treated with 10% sodium ascorbate (group II) and 6.5% proanthocyanidin (group III) compared to the control group (group I). Among the collagen cross-linkers used, specimens treated with proanthocyanidin showed significantly higher shear bond strength values than those treated with sodium ascorbate. No significant difference was observed between the five-minute and 10-minute pretreatment times in groups II and III. It can be concluded that dentin surface pretreatment with both 10% sodium ascorbate and 6.5% proanthocyanidin resulted in significant improvement in bond strength of resin composite to deep dentin.

A study on the compatibility between one-bottle dentin adhesives and composite resins using micro-shear bond strength.

Science.gov (United States)

Song, Minju; Shin, Yooseok; Park, Jeong-Won; Roh, Byoung-Duck

2015-02-01

This study was performed to determine whether the combined use of one-bottle self-etch adhesives and composite resins from same manufacturers have better bond strengths than combinations of adhesive and resins from different manufacturers. 25 experimental micro-shear bond test groups were made from combinations of five dentin adhesives and five composite resins with extracted human molars stored in saline for 24 hr. Testing was performed using the wire-loop method and a universal testing machine. Bond strength data was statistically analyzed using two way analysis of variance (ANOVA) and Tukey's post hoc test. Two way ANOVA revealed significant differences for the factors of dentin adhesives and composite resins, and significant interaction effect (p composite resin (p composite resin than other manufacturer's composite resin. Not all combinations of adhesive and composite resin by same manufacturers failed to show significantly higher bond strengths than mixed manufacturer combinations.

Effects of matrix metallproteinases on dentin bonding and strategies to increase durability of dentin adhesion

Directory of Open Access Journals (Sweden)

Jung-Hyun Lee

2012-02-01

Full Text Available The limited durability of resin-dentin bonds severely compromises the longevity of composite resin restorations. Resin-dentin bond degradation might occur via degradation of water-rich and resin sparse collagen matrices by host-derived matrix metalloproteinases (MMPs. This review article provides overview of current knowledge of the role of MMPs in dentin matrix degradation and four experimental strategies for extending the longevity of resin-dentin bonds. They include: (1 the use of broad-spectrum inhibitors of MMPs, (2 the use of cross-linking agents for silencing the activities of MMPs, (3 ethanol wet-bonding with hydrophobic resin, (4 biomimetic remineralization of water-filled collagen matrix. A combination of these strategies will be able to overcome the limitations in resin-dentin adhesion.

Multi-walled carbon nanotubes/graphene oxide hybrid and nanohydroxyapatite composite: A novel coating to prevent dentin erosion.

Science.gov (United States)

Nahorny, Sídnei; Zanin, Hudson; Christino, Vinie Abreu; Marciano, Fernanda Roberta; Lobo, Anderson Oliveira; Soares, Luís Eduardo Silva

2017-10-01

To date is emergent the development of novel coatings to protect erosion, especially to preventive dentistry and restorative dentistry. Here, for the first time we report the effectiveness of multi-walled carbon nanotube/graphene oxide hybrid carbon-base material (MWCNTO-GO) combined with nanohydroxyapatite (nHAp) as a protective coating for dentin erosion. Fourier transform Raman spectroscopy (FT-Raman), scanning electron (SEM), and transmission electron (TEM) microscopy were used to investigated the coatings and the effect of acidulated phosphate fluoride gel (APF) treatment on bovine teeth root dentin before and after erosion. The electrochemical corrosion performance of the coating was evaluated. Raman spectra identified that: (i) the phosphate (ν 1 PO 4 3- ) content of dentin was not significantly affected by the treatments and (ii) the carbonate (ν 1 CO 3 2- ) content in dentin increased when nHAp was used. However, the nHAp/MWCNTO-GO composite exposited lower levels of organic matrix (CH bonds) after erosion compared to other treatments. Interesting, SEM micrographs identified that the nHAp/MWCNTO-GO formed layers after erosive cycling when associate with APF treatment, indicating a possible chemical bond among them. Treatments of root dentin with nHAp, MWCNTO-GO, APF_MWCNTO-GO, and APF_nHAp/MWCNTO-GO increased the carbonate content, carbonate/phosphate ratio, and organic matrix band area after erosion. The potentiodynamic polarization curves and Nyquist plot showed that nHAp, MWCNT-GO and nHAp/MWCNT-GO composites acted as protective agents against corrosion process. Clearly, the nHAp/MWCNTO-GO composite was stable after erosive cycling and a thin and acid-resistant film was formed when associated to APF treatment. Copyright © 2017 Elsevier B.V. All rights reserved.

Porcelain veneer post-bonding crack repair by resin infiltration

NARCIS (Netherlands)

Gresnigt, Marco; Magne, Michel; Magne, Pascal

2017-01-01

Ceramic laminate veneer restorations are indicated in several clinical situations. Indirect restorations are usually chosen if the less-invasive options - bleaching, resin infiltration, or composite resin restorations - are not possible, or when it is too difficult to achieve an esthetically

Western hemlock as a veneer resource.

Science.gov (United States)

Thomas D. Fahey; Jr. Woodfin

1982-01-01

Presents recovery of veneer grade and volume from western hemlock from Oregon and Washington. Veneer grade recovery varied by grade and size of logs. Veneer volume recovered was about 45 percent of the cubic volume of the log and varied somewhat with log diameter.

Flexural properties of laminated veneer lumber manufactured from ultrasonically rated red maple veneer : a pilot study.

Science.gov (United States)

Xiping Wang; Robert J. Ross; Brian K. Brashaw; Steven A. Verhey; John W. Forsman; John R. Erickson

2003-01-01

The study described in this report was conducted to examine the flexural properties of laminated veneer lumber (LVL) manufactured from red maple veneer. Ultrasonically rated veneer, which was peeled from low value red maple saw-logs, was fabricated into 1/2-in.-(1.3-cm-) and 2-in.-(5-cm-) thick LVL billets. The flexural properties of the billets and of corresponding...

Effect of composite resin polymerization modes on temperature rise in human dentin of different thicknesses: an in vitro study

International Nuclear Information System (INIS)

Baggio Aguiar, Flavio Henrique; Kanda Peres Barros, Gisele; Alves Nunes Leite Lima, Debora; Bovi Ambrosano, Glaucia Maria; Lovadino, Jose Roberto

2006-01-01

The aim of this in vitro study was to evaluate the effect of different polymerization modes on temperature rise in human dentin of different thicknesses, and to evaluate the relation between dentin thickness and temperature rise (TR). For this purpose, 60 specimens were assigned into 20 groups (n = 3): five polymerization modes (1-conventional; 2-soft-start; 3-high intensity; 4-ramp cure: progressive and high intensity; 5-high intensity with the tip of the light-curing unit at a distance of 1.3 cm for 10 s and the tip leaning on the sample) at four dentin thicknesses (0, 1, 2, 3 mm). During composite sample polymerization (2 mm), the temperature was measured by a digital laser thermometer (CMSS2000-SL/SKF). The statistical analyses were conducted by ANOVA (p = 0.05) and post-hoc Tukey's test. There were statistical differences of TR among polymerization modes and dentin thicknesses. The temperature rise was dependent on the polymerization mode and the dentin thickness: the thicker the dentin and the lower the polymerization mode energy, the lower the temperature rise

Evaluation of a novel multiple phase veneering ceramic.

Science.gov (United States)

Sinthuprasirt, Pannapa; van Noort, Richard; Moorehead, Robert; Pollington, Sarah

2015-04-01

To produce a new veneering ceramic based on the production of a multiple phase glass-ceramic with improved performance in terms of strength and toughness. A composition of 60% leucite, 20% diopside and 20% feldspathic glass was prepared, blended and a heat treatment schedule of 930°C for 5 min was derived from differential thermal analysis (DTA) of the glasses. X-ray diffraction (XRD) and SEM analysis determined the crystalline phases and microstructure. Chemical solubility, biaxial flexural strength (BFS), fracture toughness, hardness, total transmittance and coefficient of thermal expansion (CTE) were all measured in comparison to a commercial veneering ceramic (VITA VM9). Thermal shock resistance of the leucite-diopside and VITA VM9 veneered onto a commercial high strength zirconia (Vita In-Ceram YZ) was also assessed. Statistical analysis was undertaken using Independent Samples t-test. Weibull analysis was employed to examine the reliability of the strength data. The mean chemical solubility was 6 μg/cm(2) for both ceramics (P=1.00). The mean BFS was 109 ± 8 MPa for leucite-diopside ceramic and 79 ± 11 MPa for VITA VM9 ceramic (P=0.01). Similarly, the leucite-diopside ceramic demonstrated a significantly higher fracture toughness and hardness. The average total transmittance was 46.3% for leucite-diopside ceramic and 39.8% for VITA VM9 (P=0.01). The leucite-diopside outperformed the VITA VM9 in terms of thermal shock resistance. Significance This novel veneering ceramic exhibits significant improvements in terms of mechanical properties, yet retains a high translucency and is the most appropriate choice as a veneering ceramic for a zirconia base core material. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Fracture strengths of chair‑side‑generated veneers cemented with ...

African Journals Online (AJOL)

2014-06-09

Jun 9, 2014 ... Group 1), CAD/CAM‑fabricated veneers cemented with a glass fiber ... specimens were tested with a universal testing machine after thermal cycling treatment. ... The purpose of the current in vitro study is to determine the ..... fracture resistance of fiber reinforced cups‑replacing composite restorations.

In vitro marginal adaptation of high-viscosity resin composite restorations bonded to dentin cavities.

Science.gov (United States)

Rahiotis, Christos; Tzoutzas, John; Kakaboura, Afrodite

2004-01-01

The aim of this study was to evaluate the marginal adaptation of high-viscosity resin composite restoratives bonded to dentin in a cylindrical cavity model. The buccal enamel of 64 human premolars was removed and cylindrical cavities 3 mm in diameter and 1.3 mm in depth were prepared on each dentin surface. The cavities were divided into 8 groups of 8 cavities each and restored according to the manufacturers' instructions with the following adhesive/composite systems: Bond 1/Alert, Stae/Glacier, OptiBond Solo/Prodigy Condensable, One-Step/Pyramid, Solidbond/Solitaire, Prime&Bond NT/Surefil, One Coat Bond/Synergy, and Scotchbond 1/Z250. The composite surfaces were pressed against mylar strips, covered with cover slips, and photopolymerized in a single increment for 40 s. The restorations were polished with wet SiC papers of 320 to 1000 grit size to expose dentin margins. The marginal adaptation was evaluated immediately after photopolymerization and again after 1 week of storage in water at 37 +/- 1 degrees C. Evaluation was performed under a metallographic microscope at 200X magnification by recording the frequency of gap-free restorations (GF), the percentage length of the debonded margins relative to the cavity periphery (DM), the width of the maximum marginal gap (MG), and the marginal index (MI = MG x DM / 100). The results were statistically analyzed with one-way ANOVA and the Mann-Whitney U-test at alpha = 0.05. No incidence of gaps was found in 62.5% of One Coat Bond/Synergy and 37.5% of OptiBond Solo/Prodigy Condensable restorations. All the other restorative systems exhibited restorations with gaps. One Coat Bond/Synergy, Scotchbond 1/Z250, and OptiBond Solo/Prodigy Condensable were the groups with the lowest DM values, while Stae/Glacier showed the highest DM values. One Coat Bond/Synergy and OptiBond Solo/Prodigy Condensable revealed the lowest MI values and Stae/Glacier the highest. No statistically significant differences were recorded between

Initial and long-term bond strengths of one-step self-etch adhesives with silane coupling agent to enamel-dentin-composite in combined situation.

Science.gov (United States)

Mamanee, Teerapong; Takahashi, Masahiro; Nakajima, Masatoshi; Foxton, Richard M; Tagami, Junji

2015-01-01

This study evaluated the effect of adding silane coupling agent on initial and long-term bond strengths of one-step self-etch adhesives to enamel-dentin-composite in combined situation. Cervical cavities were prepared on extracted molars and filled with Clearfil AP-X. After water-storage for one-week, the filled teeth were sectioned in halves to expose enamel, dentin and composite surfaces and then enamel-dentin-composite surface was totally applied with one of adhesive treatments (Clearfil SE One, Clearfil SE One with Clearfil Porcelain Bond Activator, Beautibond Multi, Beautibond Multi with Beautibond Multi PR Plus and Scotchbond Universal). After designed period, micro-shear bond strengths (µSBSs) to each substrate were determined. For each period of water-storage, additive silane treatments significantly increased µSBS to composite (penamel (p>0.05). Moreover, the stability of µSBS was depended on materials and substrates used.

Effect of core/veneer thickness ratio and veneer translucency on absolute and relative translucency of CAD-On restorations

Directory of Open Access Journals (Sweden)

Mennatallah Mohie el-Din Wahba, (BDS, MSc

2017-06-01

Conclusions: Only veneer translucency had significant effect over contrast ratio values, while on the other hand, absolute translucency values were significantly affected by the core/veneer thickness ratio, veneer translucency and interaction between them. It was clear that absolute translucency measurements showed higher translucency values for the restorations than contrast ratio measurements.

Influence of increment thickness on dentin bond strength and light transmission of composite base materials.

Science.gov (United States)

Omran, Tarek A; Garoushi, Sufyan; Abdulmajeed, Aous A; Lassila, Lippo V; Vallittu, Pekka K

2017-06-01

Bulk-fill resin composites (BFCs) are gaining popularity in restorative dentistry due to the reduced chair time and ease of application. This study aimed to evaluate the influence of increment thickness on dentin bond strength and light transmission of different BFCs and a new discontinuous fiber-reinforced composite. One hundred eighty extracted sound human molars were prepared for a shear bond strength (SBS) test. The teeth were divided into four groups (n = 45) according to the resin composite used: regular particulate filler resin composite: (1) G-ænial Anterior [GA] (control); bulk-fill resin composites: (2) Tetric EvoCeram Bulk Fill [TEBF] and (3) SDR; and discontinuous fiber-reinforced composite: (4) everX Posterior [EXP]. Each group was subdivided according to increment thickness (2, 4, and 6 mm). The irradiance power through the material of all groups/subgroups was quantified (MARC® Resin Calibrator; BlueLight Analytics Inc.). Data were analyzed using two-way ANOVA followed by Tukey's post hoc test. SBS and light irradiance decreased as the increment's height increased (p composite used. EXP presented the highest SBS in 2- and 4-mm-thick increments when compared to other composites, although the differences were not statistically significant (p > 0.05). Light irradiance mean values arranged in descending order were (p composites. Discontinuous fiber-reinforced composite showed the highest value of curing light transmission, which was also seen in improved bonding strength to the underlying dentin surface. Discontinuous fiber-reinforced composite can be applied safely in bulks of 4-mm increments same as other bulk-fill composites, although, in 2-mm thickness, the investigated composites showed better performance.

[Wear intensity and surface roughness of microhybrid composite and ceramic occlusal veneers on premolars after the thermocycling and cyclic mechanical loading tests].

Science.gov (United States)

Zhang, H Y; Jiang, T; Cheng, M X; Zhang, Y W

2018-02-18

To evaluate the wear intensity and surface roughness of occlusal veneers on premolars made of microhybrid composite resin or two kinds of ceramics in vitro after the thermocycling and cyclic mechanical loading tests. In the study,24 fresh extracted human premolars without root canal treatment were prepared (cusps reduction of 1.5 mm in thickness to simulate middle to severe tooth wear, the inclinations of cusps were 20°). The prepared teeth were restored with occlusal veneers made of three different materials: microhybrid composite, heat-pressed lithium disilicate ceramic and computer-aided design/computer-aided manufacturing (CAD/CAM) lithium disilicate ceramic in the thickness of 1.5 mm. The occlusal veneers were cemented with resin cement. The specimens were fatigued using the thermocycling and cyclic mechanical loading tests after being stored in water for 72 h. The wear of specimens was measured using gypsum replicas and 3D laser scanner before and after the thermocycling and cyclic mechanical loading tests and the mean lost distance (mm) was used to indicate the level of wear. The surfaces of occlusal contact area were observed and the surface roughness was recorded using 3D laser scanning confocal microscope before and after the fatigue test. Differences between the groups were compared using ONE-way ANOVA(Pcomposite group, heat-pressed lithium disilicate ceramic group, and CAD/CAM lithium disilicate ceramic group was (-0.13±0.03) mm, (-0.05±0.01) mm and (-0.05±0.01) mm, the wear of microhybrid composite was significantly higher than the two ceramic groups(Pcomposite was significantly higher than the two ceramic groups(Pcomposite(P=0.005) and CAD/CAM lithium disilicate ceramic (P=0.010). From the view of wear speed, microhybrid composite was significantly higher than the two kinds of ceramics, but it was similar to enamel when the opposing tooth was natural. The surface roughness before the themocycling and cyclic mechanical loading test of microhybrid

INFLUENCE OF SILANE HEAT TREATMENT ON THE TENSILE BOND STRENGTH BETWEEN EX-3 SYNTHETIC VENEERING PORCELAIN AND COMPOSITE RESIN USING FIVE DIFFERENT ACTIVATION TEMPERATURES

Directory of Open Access Journals (Sweden)

Spartak Yanakiev

2017-02-01

Full Text Available Purpose: The purpose of the present study is to assess the effect of five different silane activation temperatures and eight activation methods on the tensile bond strength between one veneering porcelain and one composite resin material. Material and methods: A total of 81 ceramic rods were made of EX-3 veneering ceramic (Kuraray Noritake Dental, Japan. Sintered ceramic bars were grinded with diamond disks to size 10x2x2mm ± 0,05mm. The front part of each bar was polished. After ultrasonic cleaning in distilled water, the specimens were divided into nine groups. Silane was activated with air at room temperature, 38º С, 50º С, 100º С, 120º С using a custom made blow drier. In a silicone mold, a composite resin Z250 (3М ESPE, St. Paul, USA was condensed toward the bond ceramic surface. A total of 81 specimens approximately 2,0 cm long were prepared for tensile bond testing. One way ANOVA, followed by Bonferroni and Games-Howell tests were used for statistical analysis. Results: The lowest tensile bond strength was observed in the control group (3,51MPa. Group 2 yielded the highest bond strength among all groups (19,54MPa. Silane heat treatment enhanced the bond strength for all treatment methods. Within the polished specimens, the highest bond strength was yielded with warm air at 120ºС (11,31MPa. Conclusion: The most effective method for bonding Z250 composite resin to EX-3 veneering ceramic includes HF etching, silane, and adhesive resin. The most effective heat treatment method for bonding is hot air at 120ºС.

Effect of Sandblasting on Shear Bond Strength Composite Resin Veneer

Directory of Open Access Journals (Sweden)

Octarina Octarina

2013-07-01

Full Text Available Attachment between restoration and enamel surface in indirect resin composite veneer restoration (IRCV is obtained using multi-step (MS resin cement. Recently, a one step self-adhesive dual-cured resin cement (SADRC was introduced. Objective: To determine the effect of sandblasting on shear bond strength (SBS of IRCV to enamel using MS resin cement and SADRC. Methods: Forty specimens of buccal surface of enamel human were light-cured in Solidilite chamber and were divided into two groups: IRCV without sandblasting (n=20 and with sandblasting for 10 seconds (n=20 and then bonded to enamel using MS (n=10 and SADRC (n=10, respectively. After 24h SBS of specimens were tested using a Universal Testing Machine. Data were analyzed statistically by one-way ANOVA. Results: The average SBS value of IRCV without SB and bonded with MS was 18.95+7.80MPa and MS with SB was 19.30+ SB (4.85+2.12MPa and SADRC with SB (9.57+3.45MPa(p<0.05. Conclusion: increased SBS VIRK to enamel using MS resin cement than SADRC.  

[Veneer computer aided design based on reverse engineering technology].

Science.gov (United States)

Liu, Ming-li; Chen, Xiao-dong; Wang, Yong

2012-03-01

To explore the computer aided design (CAD) method of veneer restoration, and to assess if the solution can help prosthesis meet morphology esthetics standard. A volunteer's upper right central incisor needed to be restored with veneer. Super hard stone models of patient's dentition (before and after tooth preparation) were scanned with the three-dimensional laser scanner. The veneer margin was designed as butt-to-butt type. The veneer was constructed using reverse engineering (RE) software. The technique guideline of veneers CAD was explore based on RE software, and the veneers was smooth, continuous and symmetrical, which met esthetics construction needs. It was a feasible method to reconstruct veneer restoration based on RE technology.

Femtosecond laser ablation of dentin

International Nuclear Information System (INIS)

Alves, S; Vilar, R; Oliveira, V

2012-01-01

The surface morphology, structure and composition of human dentin treated with a femtosecond infrared laser (pulse duration 500 fs, wavelength 1030 nm, fluences ranging from 1 to 3 J cm -2 ) was studied by scanning electron microscopy, x-ray diffraction, x-ray photoelectron spectroscopy and Fourier transform infrared spectroscopy. The average dentin ablation threshold under these conditions was 0.6 ± 0.2 J cm -2 and the ablation rate achieved in the range 1 to 2 µm/pulse for an average fluence of 3 J cm -2 . The ablation surfaces present an irregular and rugged appearance, with no significant traces of melting, deformation, cracking or carbonization. The smear layer was entirely removed by the laser treatment. For fluences only slightly higher than the ablation threshold the morphology of the laser-treated surfaces was very similar to the dentin fracture surfaces and the dentinal tubules remained open. For higher fluences, the surface was more porous and the dentin structure was partially concealed by ablation debris and a few resolidified droplets. Independently on the laser processing parameters and laser processing method used no sub-superficial cracking was observed. The dentin constitution and chemical composition was not significantly modified by the laser treatment in the processing parameter range used. In particular, the organic matter is not preferentially removed from the surface and no traces of high temperature phosphates, such as the β-tricalcium phosphate, were observed. The achieved results are compatible with an electrostatic ablation mechanism. In conclusion, the high beam quality and short pulse duration of the ultrafast laser used should allow the accurate preparation of cavities, with negligible damage of the underlying material. (paper)

Effect of bleaching and repolishing procedures on coffee and tea stain removal from three anterior composite veneering materials.

Science.gov (United States)

Türkün, L Sebnem; Türkün, Murat

2004-01-01

Discolored teeth can be treated with resin veneers, but their color changes when confronted with staining solutions. Polishing procedures can provide a remedy for highly stained composites, but they tend to remove some materials as well. However, bleaching procedures are an effective, nondestructive method for solving the problem. The aim of this study was to compare the color change of three veneer composites exposed to staining solutions and to evaluate the effectiveness of a 15% hydrogen peroxide bleaching agent and three polishing systems to remove the stain. Forty-five disks (12 x 2 mm) each of Clearfil ST (Kuraray Co. Ltd., Osaka, Japan), Esthet-X (Dentsply/Caulk, Milford DE, USA), and Filtek A110 (3M ESPE, St. Paul, MN, USA) were prepared. The specimens were polished with Sof-Lex (3M ESPE), Enhance (Dentsply/Caulk), or PoGo (Dentsply/Caulk). Five specimens for each material-polishing system combination were immersed in coffee (Nescafe Classic, Nestle SA, Vevey, Switzerland) or tea (Earl Grey, Lipton, Blackfriars-London, England) for 7 days. The remaining disks were stored in water. Color measurements were made with a spectrophotometer (X-Rite Seroice SP78, Loaner, Köln, Germany) at baseline; after 1, 3, 5, and 7 days; and after bleaching and repolishing. After 1 week, one side of the specimens was bleached with Illuminé-office (Dentsply De Trey GmbH, Konstanz, Germany) for 1 hour, and the other side was repolished for 30 seconds. All comparisons of color change for the polishing systems, times, and staining solutions were subjected to repeated measurements of analysis of variance. Paired t-test was used to examine whether significant color differences (deltaE*) occurred during immersion at the specified time intervals (p < or = .05). Filtek A110 was the least stained resin composite. Its color remained under a deltaE* value of 2 during the study. Clearfil ST exhibited the most color change after 1 week. All specimens polished with Enhance showed less

Short communication: pre- and co-curing effect of adhesives on shear bond strengths of composite resins to primary enamel and dentine: an in vitro study.

Science.gov (United States)

Viswanathan, R; Shashibhushan, K K; Subba Reddy, V V

2011-12-01

To evaluate and compare shear bond strengths of composite resins to primary enamel and dentine when the adhesives are pre-cured (light cured before the application of the resin) or co-cured (adhesive and the resin light cured together). Buccal surfaces of 80 caries-free primary molars were wet ground to create bonding surfaces on enamel and dentine and specimens mounted on acrylic blocks. Two bonding agents (Prime and Bond NT® and Xeno III®) were applied to either enamel or dentine as per manufacturer's instructions. In 40 specimens, the bonding agent was light cured immediately after the application (pre-cured). The other 40 specimens were not light cured until the composite resin application (co-cured). Resin composite cylinders were made incrementally using acrylic moulds over the adhesives and light cured. Specimens were stored in deionised water for 24 hours at room temperature. Shear bond strength was measured using an Instron universal testing machine (in MPa) and was analysed with Student's unpaired t test. Light curing the adhesive separately produced significantly higher bond strengths to primary dentine than co-curing (padhesive separately did not produce significantly different bond strengths to primary enamel (p>0.05). Curing sequence had no significant effect on shear bond strength of adhesives on the primary enamel. Pre-curing adhesives before curing composite resins produced greater shear bond strength to primary dentine.

Long-term dentin remineralization by poly(amido amine) and rechargeable calcium phosphate nanocomposite after fluid challenges.

Science.gov (United States)

Liang, Kunneng; Xiao, Shimeng; Wu, Junling; Li, Jiyao; Weir, Michael D; Cheng, Lei; Reynolds, Mark A; Zhou, Xuedong; Xu, Hockin H K

2018-04-01

Previous studies investigated short-term dentin remineralization; studies on long-term dentin remineralization after fluid challenges mimicking fluids in oral environment are lacking. The objective of this study was to develop a long-term remineralization method to via poly(amido amine) (PAMAM) and rechargeable composite containing nanoparticles of amorphous calcium phosphate (NACP) after fluid challenges for the first time. NACP composite was immersed at pH 4 to exhaust its calcium (Ca) and phosphate (P) ions, and then recharged with Ca and P ions, to test the remineralization of the exhausted and recharged NACP composite. Dentin was acid-etched with 37% phosphoric acid. Four groups were prepared: (1) dentin control, (2) dentin with PAMAM, (3) dentin with the recharged NACP composite, and (4) dentin with PAMAM plus recharged NACP composite. PAMAM-coated dentin was immersed in phosphate-buffered saline with shaking for 72 days, because there is fluid flow in the mouth which could potentially detach the PAMAM from dentin. Specimens were treated with a cyclic artificial saliva/lactic acid regimen for 35 days. After 72days of immersion plus shaking, the PAMAM still successfully fulfilled its mineralization nucleation. The recharged NACP composite still provided acid-neutralization and ion re-release, which did not decrease with increasing the number of recharge cycles. The immersed-PAMAM plus NACP achieved complete dentin remineralization and restored the hardness to that of healthy dentin. In conclusion, superior long-term remineralization of the PAMAM plus NACP method was demonstrated for the first time. The immersed-PAMAM plus recharged NACP completely remineralized the pre-demineralized dentin, even after prolonged fluid-challenge similar to that in oral environment. The novel PAMAM plus NACP composite method is promising to provide long-term tooth protection and caries inhibition. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Ltd. All

Influence of Thinning and Pruning on Southern Pine Veneer Quality

Science.gov (United States)

Mark D. Gibson; Terry R. Clason; Gary L. Hill; George A. Grozdits

2002-01-01

This paper presents the effects of intensive pine plantation management on veneer yields, veneer grade distribution and veneer MOE as measured by ultrasonic stress wave transmission (Metriguard). Veneer production trials were done at a commercial southern pine plywood plant to elucidate the effects of silvicultural treatments on veneer quality, yield, and modulus of...

Structural and Chemical Analysis of the Zirconia-Veneering Ceramic Interface.

Science.gov (United States)

Inokoshi, M; Yoshihara, K; Nagaoka, N; Nakanishi, M; De Munck, J; Minakuchi, S; Vanmeensel, K; Zhang, F; Yoshida, Y; Vleugels, J; Naert, I; Van Meerbeek, B

2016-01-01

The interfacial interaction of veneering ceramic with zirconia is still not fully understood. This study aimed to characterize morphologically and chemically the zirconia-veneering ceramic interface. Three zirconia-veneering conditions were investigated: 1) zirconia-veneering ceramic fired on sandblasted zirconia, 2) zirconia-veneering ceramic on as-sintered zirconia, and 3) alumina-veneering ceramic (lower coefficient of thermal expansion [CTE]) on as-sintered zirconia. Polished cross-sectioned ceramic-veneered zirconia specimens were examined using field emission gun scanning electron microscopy (Feg-SEM). In addition, argon-ion thinned zirconia-veneering ceramic interface cross sections were examined using scanning transmission electron microscopy (STEM)-energy dispersive X-ray spectrometry (EDS) at high resolution. Finally, the zirconia-veneering ceramic interface was quantitatively analyzed for tetragonal-to-monoclinic phase transformation and residual stress using micro-Raman spectroscopy (µRaman). Feg-SEM revealed tight interfaces for all 3 veneering conditions. High-resolution transmission electron microscopy (HRTEM) disclosed an approximately 1.0-µm transformed zone at sandblasted zirconia, in which distinct zirconia grains were no longer observable. Straight grain boundaries and angular grain corners were detected up to the interface of zirconia- and alumina-veneering ceramic with as-sintered zirconia. EDS mapping disclosed within the zirconia-veneering ceramic a few nanometers thick calcium/aluminum-rich layer, touching the as-sintered zirconia base, with an equally thick silicon-rich/aluminum-poor layer on top. µRaman revealed t-ZrO2-to-m-ZrO2 phase transformation and residual compressive stress at the sandblasted zirconia surface. The difference in CTE between zirconia- and the alumina-veneering ceramic resulted in residual tensile stress within the zirconia immediately adjacent to its interface with the veneering ceramic. The rather minor chemical

Effect of composite resin placement techniques on the microleakage of two self-etching dentin-bonding agents.

NARCIS (Netherlands)

Santini, A.; Plasschaert, A.J.M.; Mitchell, S.M.

2001-01-01

PURPOSE: To evaluate microleakage of Class V resin-based composites (RBC) bonded with two self-etching dentin adhesive systems. Class V cavities were restored with either one or three increments of RBC to determine whether the restorative method affected microleakage. MATERIALS AND METHODS: 60

Shear bond strength of veneering porcelain to zirconia: Effect of surface treatment by CNC-milling and composite layer deposition on zirconia.

Science.gov (United States)

Santos, R L P; Silva, F S; Nascimento, R M; Souza, J C M; Motta, F V; Carvalho, O; Henriques, B

2016-07-01

The purpose of this study was to evaluate the shear bond strength of veneering feldspathic porcelain to zirconia substrates modified by CNC-milling process or by coating zirconia with a composite interlayer. Four types of zirconia-porcelain interface configurations were tested: RZ - porcelain bonded to rough zirconia substrate (n=16); PZ - porcelain bonded to zirconia substrate with surface holes (n=16); RZI - application of a composite interlayer between the veneering porcelain and the rough zirconia substrate (n=16); PZI - application of a composite interlayer between the porcelain and the zirconia substrate treated by CNC-milling (n=16). The composite interlayer was composed of zirconia particles reinforced porcelain (30%, vol%). The mechanical properties of the ceramic composite have been determined. The shear bond strength test was performed at 0.5mm/min using a universal testing machine. The interfaces of fractured and untested specimens were examined by FEG-SEM/EDS. Data was analyzed with Shapiro-Wilk test to test the assumption of normality. The one-way ANOVA followed by Tukey HSD multiple comparison test was used to compare shear bond strength results (α=0.05). The shear bond strength of PZ (100±15MPa) and RZI (96±11MPa) specimens were higher than that recorded for RZ (control group) specimens (89±15MPa), although not significantly (p>0.05). The highest shear bond strength values were recorded for PZI specimens (138±19MPa), yielding a significant improvement of 55% relative to RZ specimens (p<0.05). This study shows that it is possible to highly enhance the zirconia-porcelain bond strength - even by ~55% - by combining surface holes in zirconia frameworks and the application of a proper ceramic composite interlayer. Copyright © 2016 Elsevier Ltd. All rights reserved.

Temperature rise produced by different light-curing units through dentin.

Science.gov (United States)

Yazici, A Rüya; Müftü, Ali; Kugel, Gerard

2007-11-01

This study investigated the temperature rise caused by different light curing units and the temperature increase in dentin of different thicknesses. Dentin discs of 1.0 and 2.0 mm thicknesses were prepared from extracted human mandibular molars. Temperatures were recorded directly at the surface of the light guide tip, under dentin discs with different thicknesses, and through a sandwich composed of 2 mm thick cured composite and dentin using a K-type thermocouple. The curing units used were two quartz-tungsten-halogen lights (Spectrum and Elipar Trilight-ET) and a light-emitting diode (LED). The highest temperature rise was observed under a Mylar strip using ET standard mode. Under 1 and 2 mm thick dentin barriers, the lowest temperature rise was measured for the LED curing light. Significant differences in temperature rise existed among all curing units except between the Spectrum and ET exponential modes under a 1 mm thick dentin barrier with cured composite. Temperature rises were insignificant between the Spectrum and ET exponential modes and between two modes of Trilight when the same experimental setup was used under a 2 mm thick dentin barrier. For all curing units, temperature elevation through 2 mm of dentin was less than for 1 mm of dentin thickness. The ET standard mode produced the highest and the LED produced the lowest temperature rise for all tested conditions. The thickness of dentin and light-curing unit might affect temperature transmission.

Tensile bond strength of hydroxyethyl methacrylate dentin bonding agent on dentin surface at various drying techniques

Directory of Open Access Journals (Sweden)

Kun Ismiyatin

2010-06-01

Full Text Available Background: There are several dentin surface drying techniques to provide a perfect resin penetration on dentin. There are two techniques which will be compared in this study. The first technique was by rubbing dentin surface gently using cotton pellet twice, this technique is called blot dry technique. The second technique is by air blowing dentin surface for one second and continued by rubbing dentin surface gently using moist cotton. Purpose: This experiment was aimed to examine the best dentin surface drying techniques after 37% phosphoric acid etching to obtain the optimum tensile bond strength between hydroxyethyl methacrylate (HEMA and dentin surface. Method: Bovine teeth was prepared flat to obtain the dentin surface and than was etched using 37% phosphoric acid for 15 seconds. After etching the dentin was cleaned using 20 cc plain water and dried with blot dry techniques (group I, or dried with air blow for one second (group II, or dried with air blow for one second, and continued with rubbing gently using moist cotton pellet (group III, and without any drying as control group (group IV. After these drying, the dentin surfaces were applied with resin dentin bonding agent and put into plunger facing the composite mould. The antagonist plunger was filled with composite resin. After 24 hours, therefore bond strength was measured using Autograph. Result: Data obtained was analyzed using One-Way ANOVA with 95% confidence level and continued with LSD test on p≤0.05. The result showed that the highest tensile bond strength was on group I, while the lowest on group IV. Group II and IV, III and IV, II and III did not show signigicant difference (p>0.05. Conclusion: Dentin surface drying techniques through gentle rubbing using cotton pellet twice (blot dry technique gave the greatest tensile bond strength.Latar belakang masalah: Tehnik pengeringan permukaan dentin agar resin dapat penetrasi dengan sempurna adalah dengan cara pengusapan secara

Bond strength of composite to dentin: effect of acid etching and laser irradiation through an uncured self-etch adhesive system

International Nuclear Information System (INIS)

Castro, F L A; Carvalho, J G; Andrade, M F; Saad, J R C; Hebling, J; Lizarelli, R F Z

2014-01-01

This study evaluated the effect on micro-tensile bond strength (µ-TBS) of laser irradiation of etched/unetched dentin through an uncured self-etching adhesive. Dentinal surfaces were treated with Clearfil SE Bond Adhesive (CSE) either according to the manufacturer’s instructions (CSE) or without applying the primer (CSE/NP). The dentin was irradiated through the uncured adhesive, using an Nd:YAG laser at 0.75 or 1 W power settings. The adhesive was cured, composite crowns were built up, and the teeth were sectioned into beams (0.49 mm 2 ) to be stressed under tension. Data were analyzed using one-way ANOVA and Tukey statistics (α = 5%). Dentin of the fractured specimens and the interfaces of untested beams were observed under scanning electron microscopy (SEM). The results showed that non-etched irradiated surfaces presented higher µ-TBS than etched and irradiated surfaces (p < 0.05). Laser irradiation alone did not lead to differences in µ-TBS (p > 0.05). SEM showed solidification globules on the surfaces of the specimens. The interfaces were similar on irradiated and non-irradiated surfaces. Laser irradiation of dentin through the uncured adhesive did not lead to higher µ-TBS when compared to the suggested manufacturer’s technique. However, this treatment brought benefits when performed on unetched dentin, since bond strengths were higher when compared to etched dentin. (paper)

Resistência adesiva de resinas compostas à dentina Adhesive strength between composite resin and dentin substract

Directory of Open Access Journals (Sweden)

Joel BIANCHI

1999-01-01

Full Text Available As pesquisas relacionadas com adesão à dentina, em virtude da ampla aplicabilidade, são de grande interesse para a Odontologia. O objetivo deste estudo foi avaliar, através de ensaios de tração, a resistência adesiva ao substrato dentinário, em função de dois sistemas adesivos (3M e Kerr, dois níveis de rugosidade do substrato dentinário (lixas 220 e 600, duas áreas de colagem (3,14 mm2 - 12,56 mm2, e duas condições de armazenagem (inicial e final. A análise dos resultados evidenciou que: 1 houve diferença estatisticamente significativa entre os dois sistemas adesivos, sendo que o da Kerr apresentou os valores mais elevados de resistência adesiva; 2 diferenças significativas não ficaram evidentes na resistência da adesão entre os dois níveis de rugosidade dentinária; 3 as colagens em áreas menores apresentaram, em nível altamente significativo, maior resistência adesiva; 4 a condição de armazenagem influiu nos resultados dependendo da área e do sistema adesivo.There is a wealthy literature on bonding strength of composites to dentine. One of the reasons for the large number of studies is the continuous introduction of new bonding agents in combination with accumulated knowledge about the dentine substrate conditions. The aim of the present study was to compare the "in vitro" tensile bond strengths of two dentine bonding systems (3M and Kerr applied to different dentine roughness (220 and 600 gritand two sizes of bonding areas (3,14 mm2 and 12,56 mm2. Different storage conditions (initial and final were also considered. One hundred and sixty human teeth were randomly allocated in 4 groups. The Kerr system groups and the smallest bonding area groups showed the highest tensile strengths. The storage condition and the substrate roughness did not display a significant influence on bond strengths.

Morphology and chemical composition of dentin in permanent first molars with the diagnose MIH.

Science.gov (United States)

Heijs, Suzanne C B; Dietz, Wolfram; Norén, Jörgen G; Blanksma, Nynke G; Jälevik, Birgitta

2007-01-01

The purpose of this investigation was to study the morphology and distribution of some inorganic elements in dentin in first permanent molars from children with Molar-Incisor Hypomineralization (MIH). Sixty four tooth sections from thirty two children were examined in polarized light. Fifteen representative sections were selected for SEM/XRMA analysis; 5 were used for SEM analysis and 10 for XRMA analysis. No morphological changes in the dentin were revealed in polarized light microscopy (PLM). However, in all but two sections interglobular dentin was found. The SEM analyzes confirmed the findings of the PLM with no structural changes to be found in the dentin. The XRMA results showed a difference in the concentration of elements between dentin below normal and dentin below carious or hypomineralized enamel. Elements related to organic matter appeared with higher values in dentin below hypomineralized and carious enamel. The morphological and chemical findings in dentin below hypomineralized enamel imply that the odontoblasts are not affected in cases of MIH, but may be affected by hypocalcemia, reflected by the presence of interglobular dentin.

Composite Replacement of Amalgam Restoration Versus Freshly Cut Dentin: An In Vitro Microleakage Comparison.

Science.gov (United States)

Redwan, H; Bardwell, D N; Ali, A; Finkelman, M; Khayat, S; Weber, H-P

2016-01-01

The aim of this study was to evaluate the microleakage of the composite restorations when bonded to tooth structure previously restored with amalgam material compared with that of freshly cut dentin. Thirty intact, extracted intact human molars were mounted in autopolymerizing acrylic resin. Class II box preparations were prepared on the occluso-proximal surfaces of each tooth (4-mm bucco-lingual width and 2-mm mesio-distal depth) with the gingival cavosurface margin 1 mm above the CEJ. Each cavity was then restored using high copper amalgam restoration (Disperalloy, Dentsply) and then thermocycled for 10,000 thermal cycles. Twenty-five of the amalgam restorations were then carefully removed and replaced with Filtek Supreme Ultra Universal (3M ESPE); the remaining five were used for scanning electron microscopy and energy dispersive x-ray spectroscopy analysis. A preparation of the same dimensions was performed on the opposite surface of the tooth and restored with composite resin and thermocycled for 5000 thermal cycles. Twenty samples were randomly selected for dye penetration testing using silver nitrate staining to detect the microleakage. The specimens were analyzed with a stereomicroscope at a magnification of 20×. All of the measurements were done in micrometers; two readings were taken for each cavity at the occlusal and proximal margins. Two measurements were taken using a 0-3 scale and the percentage measurements. Corrosion products were not detected in either group (fresh cut dentin and teeth previously restored with amalgam). No statistically significant difference was found between the microleakage of the two groups using a 0-3 scale at the occlusal margins (McNemar test, p=0.727) or proximal margins (Wilcoxon signed-rank test, p=0.174). No significance difference was found between the two groups using the percentage measurements and a Wilcoxon signed-rank test at either the occlusal (p=0.675) or proximal (p=0.513) margins. However, marginal

Effects of endodontic tri-antibiotic paste on bond strengths of dentin adhesives to coronal dentin

Directory of Open Access Journals (Sweden)

Parvin Mirzakoucheki

2015-05-01

Full Text Available Objectives The aim of this study was to evaluate the effects of tri-antibiotic paste (TAP on microtensile bond strengths (MTBS of dental adhesives to dentin. Materials and Methods Sixty extracted molars had their occlusal surfaces flattened to expose dentin. They were divided into two groups, i.e., control group with no dentin treatment and experimental group with dentin treatment with TAP. After 10 days, specimens were bonded using self-etch (Filtek P90 adhesive or etch-and-rinse (Adper Single Bond Plus adhesives and restored with composite resin. Teeth were sectioned into beams, and the specimens were subjected to MTBS test. Data were analyzed using two-way ANOVA and post hoc Tukey tests. Results There was a statistically significant interaction between dentin treatment and adhesive on MTBS to coronal dentin (p = 0.003. Despite a trend towards worse MTBS being noticed in the experimental groups, TAP application showed no significant effect on MTBS (p = 0.064. Conclusions The etch-and-rinse adhesive Adper Single Bond Plus presented higher mean bond strengths than the self-etch adhesive Filtek P90, irrespective of the group. The superior bond performance for Adper Single Bond when compared to Filtek P90 adhesive was confirmed by a fewer number of adhesive failures. The influence of TAP in bond strength is insignificant.

Defining Hardwood Veneer Log Quality Attributes

Science.gov (United States)

Jan Wiedenbeck; Michael Wiemann; Delton Alderman; John Baumgras; William Luppold

2004-01-01

This publication provides a broad spectrum of information on the hardwood veneer industry in North America. Veneer manufacturers and their customers impose guidelines in specifying wood quality attributes that are very discriminating but poorly defined (e.g., exceptional color, texture, and/or figure characteristics). To better understand and begin to define the most...

Fracture Resistance of Ceramic Laminate Veneers Bonded to Teeth with Class V Composite Fillings after Cyclic Loading

Directory of Open Access Journals (Sweden)

Leyla Sadighpour

2018-01-01

Full Text Available Purpose. Porcelain laminate veneers (PLVs are sometimes required to be used for teeth with composite fillings. This study examined the fracture strength of PLVs bonded to the teeth restored with different sizes of class V composite fillings. Materials and Methods. Thirty-six maxillary central incisors were divided into three groups (n=12: intact teeth (control and teeth with class V composite fillings of one-third or two-thirds of the crown height (small or large group, resp.. PLVs were made by using IPS e.max and bonded with a resin cement (RelyX Unicem. Fracture resistance (N was measured after cyclic loading (1 × 106 cycles, 1.2 Hz. For statistical analyses, one-way ANOVA and Tukey test were used (α=0.05. Results. There was a significant difference between the mean failure loads of the test groups (P=0.004, with the Tukey-HSD test showing lower failure loads in the large-composite group compared to the control (P=0.02 or small group (P=0.05. The control and small-composite groups achieved comparable results (P>0.05. Conclusions. Failure loads of PLVs bonded to intact teeth and to teeth with small class V composite fillings were not significantly different. However, extensive composite fillings could compromise the bonding of PLVs.

Flexural Strength of Preheated Resin Composites and Bonding Properties to Glass-Ceramic and Dentin

Directory of Open Access Journals (Sweden)

Matthias Richard Kramer

2016-01-01

Full Text Available To test the impact of preheating (25, 37, 54, or 68 °C of TetricEvoCeram (TEC, FiltekSupremeXT (FSXT, and Venus (V on flexural strength (FS, shear bond strength (SBS and interfacial tension (IFT. FS was tested with TEC and FSXT. For SBS, glass-ceramic and human dentin substrate were fabricated and luted with the preheated resin composite (RC. SBSs of 1500 thermal cycled specimens were measured. For IFT, glass slides covered with the non-polymerized RC were prepared and contact angles were measured. Data were analyzed using 2/1-way ANOVA with Scheffé-test, and t-test (p < 0.05. Preheated TEC (37–68 °C showed higher FS compared to the control-group (25 °C (p < 0.001. FSXT presented higher FS than TEC (p < 0.001. For SBS to dentin higher values for FSXT than TEC were found. The preheating temperature showed no impact on SBS to dentin. SBS to glass-ceramic revealed a positive influence of temperature for TEC 25–68 °C (p = 0.015. TEC showed higher values than V and FSXT (p < 0.001. IFT values increased with the preheating temperature. A significant difference could be observed in every RC group between 25 and 68 °C (p < 0.001.

An indirect veneer technique for simple and esthetic treatment of anterior hypoplastic teeth

Directory of Open Access Journals (Sweden)

Amit Khatri

2010-01-01

Full Text Available This study describes a technique for treating anterior hypoplastic teeth using indirect nanocomposite veneer restoration. The prime advantage of an indirect veneer technique is that it provides an esthetic and conservative result. One of the most frequent reasons that patients seek dental care is discolored anterior teeth. Although treatment options such as removal of surface stains, bleaching, microabrasion or macroabrasion, veneering, and placement of porcelain crowns are available, conservative approach such as veneer preserves the natural tooth as much as possible. Full veneers are recommended for the restoration of localized defects or areas of intrinsic discoloration, which are caused by deeper internal stains or enamel defects. Indirectly fabricated veneers are much less sensitive compared to a operator′s technique and if multiple teeth are to be veneered, indirect veneers can be usually placed much more expeditiously. Indirect veneers last much longer than the direct veneers. Therefore, indirectly fabricated veneers are more advantageous than directly fabricated veneers in many cases.

Effect of Nanofiller Addition to an Experimental Dentin Adhesive on Microtensile Bond Strength to Human Dentin

Directory of Open Access Journals (Sweden)

SH. Kasraei

2009-06-01

Full Text Available Objective: The purpose of the study was to evaluate the influence of adding nanofiller particles to a dentin bonding agent on resin-dentin bond strength.Materials and Methods: Fifty-four human intact premolar teeth were divided in to 6 groups of nine. The teeth were ground on occlusal surfaces and polished with 320 and then 600 grit silicon carbide papers. An experimental bonding system based on acetone/alcoholsolvent was provided with filler contents of 0.0, 0.5, 1.0, 2.5, 5.0, and 10.0 weight percent fumed silica nanofiller. After dentin surface etching, rinsing and blot drying, the experimentalbonding agents were applied to dentin surface. A composite resin was, then,bonded to the dentin on the bonding agent. The specimens were thermocycled for 500 cycles and sectioned in stick form. After two week of storage in distilled water, resin-dentin microtensile bond strength of the specimens was measured. Data were analyzed by one way ANOVA and DunnettT3 tests.Results: Bond strength to dentin was significantly affected by the filler level. Minimum and maximum resin-microtensile bond strength was in the experimental bonding agent with no filler (5.88 MPa and with filler level of 1.0 weight percent (15.15 MPa, respectively,and decreased with the increase of filler content down to 8.95 MPa for the filler level of 10.0 weight percent.Conclusion: Filler content seems to be one of the important factors influencing the bond strength of dental adhesives. Maximum dentin bond strength was obtained with 1% silanized nanofiller silica added to experimental adhesive system.

Six-year follow-up with Empress veneers.

Science.gov (United States)

Fradeani, M

1998-06-01

This study reports on 6 years experience with IPS Empress laminate veneers. A total of 83 anterior veneers were positioned in 21 patients from January 1991 to December 1996 in the author's private practice. Final evaluation was carried out in May and June 1997. Color match, marginal discoloration, recurrent caries, contour, and marginal integrity were evaluated using the modified U.S. Public Health Service criteria at baseline and subsequent recall appointments. On the basis of the criteria used, a large percentage of veneers were rated Alfa. Only one failure was recorded, resulting in a success rate of 98.8%. A thorough description of clinical procedures and laboratory techniques through which anterior teeth can be successfully treated with ceramic veneers is supplied. A clinical case is presented to demonstrate the satisfactory esthetic results obtained using this very conservative restorative technique.

Microtensile bond strength of bulk-fill restorative composites to dentin.

Science.gov (United States)

Mandava, Jyothi; Vegesna, Divya-Prasanna; Ravi, Ravichandra; Boddeda, Mohan-Rao; Uppalapati, Lakshman-Varma; Ghazanfaruddin, M D

2017-08-01

To facilitate the easier placement of direct resin composite in deeper cavities, bulk fill composites have been introduced. The Mechanical stability of fillings in stress bearing areas restored with bulk-fill resin composites is still open to question, since long term clinical studies are not available so far. Thus, the objective of the study was to evaluate and compare the microtensile bond strength of three bulk-fill restorative composites with a nanohybrid composite. Class I cavities were prepared on sixty extracted mandibular molars. Teeth were divided into 4 groups (n= 15 each) and in group I, the prepared cavities were restored with nanohybrid (Filtek Z250 XT) restorative composite in an incremental manner. In group II, III and IV, the bulk-fill composites (Filtek, Tetric EvoCeram, X-tra fil bulk-fill restoratives) were placed as a 4 mm single increment and light cured. The restored teeth were subjected to thermocycling and bond strength testing was done using instron testing machine. The mode of failure was assessed by scanning electron microscope (SEM). The bond strength values obtained in megapascals (MPa) were subjected to statistical analysis, using SPSS/PC version 20 software.One-way ANOVA was used for groupwise comparison of the bond strength. Tukey's Post Hoc test was used for pairwise comparisons among the groups. The highest mean bond strength was achieved with Filtek bulk-fill restorative showing statistically significant difference with Tetric EvoCeram bulk-fill ( p composites. Adhesive failures are mostly observed with X-tra fil bulk fill composites, whereas mixed failures are more common with other bulk fill composites. Bulk-fill composites exhibited adequate bond strength to dentin and can be considered as restorative material of choice in posterior stress bearing areas. Key words: Bond strength, Bulk-fill restoratives, Configuration factor, Polymerization shrinkage.

[The influence of the chemo-mechanical removal of the smear-layer and the use of a dentin adhesive on microleakage of composite resin restorations].

Science.gov (United States)

de la Macorra García, J C; Gómez Martínez, A; Gutiérrez Argumosa, B

1989-02-01

We present an "in vitro" study of microfiltration in composite resin restorations with a perimetral seal placed totally in cement. We compare the sealing capability of a dentin adhesive (ScotchBond I) used in two ways: habitual, without conditioning dentin and conditioning it by means of the Caridex system. This produced no increasing of sealing capability under the study conditions.

ON THE DURABILITY OF RESIN-DENTIN BONDS: IDENTIFYING THE WEAKEST LINKS

Science.gov (United States)

Zhang, Zihou; Beitzel, Dylan; Mutluay, Mustafa; Tay, Franklin R.; Pashley, David H.; Arola, Dwayne

2015-01-01

Fatigue of resin-dentin adhesive bonds is critical to the longevity of resin composite restorations. Objectives The objectives were to characterize the fatigue and fatigue crack growth resistance of resin-dentin bonds achieved using two different commercial adhesives and to identify apparent “weak-links”. Methods Bonded interface specimens were prepared using Adper Single Bond Plus (SB) or Adper Scotchbond Multi-Purpose (SBMP) adhesives and 3M Z100 resin composite according to the manufacturers instructions. The stress-life fatigue behavior was evaluated using the twin bonded interface approach and the fatigue crack growth resistance was examined using bonded interface Compact Tension (CT) specimens. Fatigue properties of the interfaces were compared to those of the resin-adhesive, resin composite and coronal dentin. Results The fatigue strength of the SBMP interface was significantly greater than that achieved by SB (p≤0.01). Both bonded interfaces exhibited significantly lower fatigue strength than that of the Z100 and dentin. Regarding the fatigue crack growth resistance, the stress intensity threshold (ΔKth) of the SB interface was significantly greater (p≤0.01) than that of the SBMP, whereas the ΔKth of the interfaces was more than twice that of the parent adhesives. Significance Collagen fibril reinforcement of the resin adhesive is essential to the fatigue crack growth resistance of resin-dentin bonds. Resin tags that are not well hybridized into the surrounding intertubular dentin and/or poor collagen integrity are detrimental to the bonded interface durability. PMID:26169318

Bond Strength of Resin Composite to Dentin with Different Adhesive Systems: Influence of Relative Humidity and Application Time.

Science.gov (United States)

Amsler, Fabienne; Peutzfeldt, Anne; Lussi, Adrian; Flury, Simon

2015-06-01

To investigate the influence of relative humidity and application time on bond strength to dentin of different classes of adhesive systems. A total of 360 extracted human molars were ground to mid-coronal dentin. The dentin specimens were treated with one of six adhesive systems (Syntac Classic, OptiBond FL, Clearfil SE Bond, AdheSE, Xeno Select, or Scotchbond Universal), and resin composite (Filtek Z250) was applied to the treated dentin surface under four experimental conditions (45% relative humidity/application time according to manufacturers' instructions; 45% relative humidity/reduced application time; 85% relative humidity/application time according to manufacturers' instructions; 85% relative humidity/reduced application time). After storage (37°C, 100% humidity, 24 h), shear bond strength (SBS) was measured and data analyzed with nonparametric ANOVA followed by Kruskal-Wallis tests and Mann-Whitney U-tests with Bonferroni-Holm correction for multiple testing (level of significance: α = 0.05). Increased relative humidity and reduced application time had no effect on SBS for Clearfil SE Bond and Scotchbond Universal (p = 1.00). For Syntac Classic, OptiBond FL, AdheSE, and Xeno Select there was no effect on SBS of reduced application time of the adhesive system (p ≥ 0.403). However, increased relative humidity significantly reduced SBS for Syntac Classic, OptiBond FL, and Xeno Select irrespective of application time (p ≤ 0.003), whereas for AdheSE, increased relative humidity significantly reduced SBS at recommended application time only (p = 0.002). Generally, increased relative humidity had a detrimental effect on SBS to dentin, but reduced application time had no effect.

Application of 10% Ascorbic Acid Improves Resin Shear Bond Stregth in Bleached Dentin

Directory of Open Access Journals (Sweden)

Kamizar Kamizar

2014-10-01

Full Text Available Normal 0 false false false IN X-NONE X-NONE MicrosoftInternetExplorer4 Restoration of the teeth immediately after bleaching with H2O2 35% is contraindicated due to the remnants of free radical that will stay inside dentin for 2-3 weeks which will compromise the adhesiveness of composite resin. Objective: The aim of this study was to evaluate the influence of 10% ascorbic acid on shear bond strength of composite placed on bleached dentin. Methods:Twenty seven samples were divided equally into three groups. Group 1: dentin was etched with 35% phosphoric acid; Group 2: dentin was bleached with 35% H2O2 followed by etching with 35% phosphoric acid; Group 3: dentin was bleached with 35% H2O2, followed by application of 10% ascorbic acid and etched with 35% phosphoric acid. All samples were then stored at 370C for 24 hours. The Universal Testing Machine was used to measure shear bond strength and the results were analyzed with Kruskal Wallis and Mann Whitney test. Results: After nine independent experiments, 10% ascorbic acid application on bleached dentin resulted in highest increased in bond stregth (56.04±11.06MPa compared to Group 2 (29.09±7.63MPa and Group 1 (25.55±2.22MPa and the difference was statistically significant (p<0.05. Conclusion: Application of 10% ascorbic acid to the bleached dentin improved the shear bond strength of resin composite.

Residual stress measurement in veneering ceramic by hole-drilling.

Science.gov (United States)

Mainjot, Amélie K; Schajer, Gary S; Vanheusden, Alain J; Sadoun, Michaël J

2011-05-01

Mismatch in thermal expansion properties between veneering ceramic and metallic or high-strength ceramic cores can induce residual stresses and initiate cracks when combined with functional stresses. Knowledge of the stress distribution within the veneering ceramic is a key factor for understanding and predicting chipping failures, which are well-known problems with Yttria-tetragonal-zirconia-polycrystal based fixed partial dentures. The objectives of this study are to develop a method for measuring the stress profile in veneering ceramics and to compare ceramic-fused-to-metal compounds to veneered Yttria-tetragonal-zirconia-polycrystal ceramic. The hole-drilling method, often used for engineering measurements, was adapted for use with veneering ceramic. Because of the high sensitivity needed in comparison with industrial applications, a high sensitivity electrical measurement chain was developed. All samples exhibited the same type of stress vs. depth profile, starting with compressive at the ceramic surface, decreasing with depth and becoming tensile at 0.5-1.0mm from the surface, and then becoming slightly compressive again. The zirconia samples exhibited a stress depth profile of larger magnitude. The hole drilling method was shown be a practical tool for measuring residual stresses in veneering ceramics. Copyright © 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of dentin biomodifiers on the immediate and long-term bond strengths of a simplified etch and rinse adhesive to dentin.

Science.gov (United States)

Singh, Payal; Nagpal, Rajni; Singh, Udai Pratap

2017-08-01

This in vitro study evaluated the effect of dentin biomodifiers on the immediate and long-term bond strengths of a simplified etch and rinse adhesive to dentin. Flat coronal dentin surfaces were prepared in 120 extracted human molars. Teeth were randomly divided into 5 groups ( n = 24) according to 5 different surface pre-treatments: No pre-treatment (control); 1M carbodiimide (EDC); 0.1% epigallocatechin-3-gallate (EGCG); 2% minocycline (MI); 10% sodium ascorbate (SA). After surface pre-treatment, adhesive (Adper Single Bond 2 [SB], 3M ESPE) was applied. Composite was applied into transparent plastic tubes (2.5 mm in diameter), which was placed over the bonded dentin surface. From each group, 10 samples were subjected to shear bond strength (SBS) evaluation at 24 hours (immediate) and remaining 10 samples were tested after 6 months (delayed). Additionally, 4 samples per group were subjected to scanning electron microscopic analysis for observation of resin-dentin interface. The data were statistically analysed with Shaperio‑Wilk W test, 2-way analysis of variance (ANOVA), and post hoc Tukey's test. At 24 hours, SBS of all surface pre-treatment groups were comparable with the control group, with significant differences found between EDC and SA groups only ( p = 0.009). After 6 months storage, EDC, EGCG, and MI pre-treatments preserved the resin-dentin bond strength with no significant fall. Dentin pre-treatment with all the dentin biomodifiers except SA resulted in significant preservation of resin-dentin bond over 6 months storage period, without negatively affecting the immediate bond strength of the etch and rinse adhesive tested.

The effect of air thinning on dentin adhesive bond strength.

Science.gov (United States)

Hilton, T J; Schwartz, R S

1995-01-01

The purpose of this study was to determine if air thinning three dentin adhesives would affect bond strength to dentin. Ninety human molars were mounted in acrylic and the occlusal surfaces ground to expose a flat dentin surface. Thirty teeth were randomly assigned to one of the following dentin bonding agent/composite combinations: A) Universal Bond 3/TPH (Caulk), B) All-Bond 2/Bis-Fil-P (Bisco), and C) Scotchbond Multi-Purpose/Z-100 (3m). The primers were applied following the manufacturers' instructions. The adhesives were applied by two methods. A thin layer of adhesive was applied with a brush to 15 specimens in each group and light cured. Adhesive was brushed on to the remaining 15 teeth in the group, air thinned for 3 seconds, and then polymerized. The appropriate composite was applied in 2 mm increments and light cured utilizing a 5 mm-in-diameter split Teflon mold. Following 3 months of water storage, all groups were shear tested to failure on an Instron Universal Testing Machine. Bond strength was significantly higher in all groups when the dentin bonding agent was painted on without being air thinned. Scotchbond Multi-Purpose had significantly higher bond strength than All-Bond 2, which had significantly higher bond strength than Universal Bond 3.

Efficacy of Hydrophobic Layer On Sealing Ability of Dentin Adhesive Systems in Class V Composite Resin Restorations

Directory of Open Access Journals (Sweden)

Fatemeh Maleknejad

2011-03-01

Full Text Available Background and aims. Adhesive permeability is hindered by application of an additional layer of hydrophobic resin, which increases its concentration within the hydrophilic layer, reduces its affinity to water, and enhances its physical properties. The aim of the present study was to evaluate the effect of a hydrophobic layer on the microleakage of class V composite restorations using different adhesives. Materials and methods. The adhesives including total-etch Scotchbond MP and Single Bond, and the self-etch Clearfil SE Bond and Clearfil S3 Bond were applied to 80 class V cavities in vitro on the buccal surface in CEJ and then were followed by hydrophobic resin (Margin Bond in half of the cavities in each group (n=10. After restoration with microhybrid composite, Z100 and immersion in fuchsine, the degree of microleakage was assessed. Data were analyzed using the Kruskal-Wallis, Man-Whitney, and Wilcoxon tests. Results. The hydrophobic layer significantly reduced the microleakage of Clearfil SE Bond and Clearfil S3 Bond only in dentin (p0.05. Conclusion. Within the limitation of this study, only Clearfil S3 Bond could demonstrate the identical values of microleakage in enamel and dentinal margins.

Effect of sonic application mode on the resin-dentin bond strength and dentin permeability of self-etching systems.

Science.gov (United States)

Mena-Serrano, Alexandra; Costa, Thays Regina Ferreira da; Patzlaff, Rafael Tiago; Loguercio, Alessandro Dourado; Reis, Alessandra

2014-10-01

To compare manual and sonic adhesive application modes in terms of the permeability and microtensile bond strength of a self-etching adhesive applied in the one-step or two-step protocol. Self-etching All Bond SE (Bisco) was applied as a one- or a two-step adhesive under manual or sonic vibration modes on flat occlusal dentin surfaces of 64 human molars. Half of the teeth were used to measure the hydraulic conductance of dentin at 200 cm H₂O hydrostatic pressure for 5 min immediately after the adhesive application. In the other half, composite buildups (Opallis) were constructed incrementally to create resin-dentin sticks with a cross-sectional area of 0.8 mm² to be tested in tension (0.5 mm/min) immediately after restoration placement. Data were analyzed using a two-way ANOVA and Tukey's test (α = 0.05). The fluid conductance of dentin was significantly reduced by the sonic vibration mode for both adhesives, but no effect on the bond strength values was observed for either adhesive. The sonic application mode at an oscillating frequency of 170 Hz can reduce the fluid conductance of the one- and two-step All Bond SE adhesive when applied on dentin.

Morphological and chemical changes of dentin after applying different sterilization methods

Directory of Open Access Journals (Sweden)

Cláudio Antonio Talge Carvalho

Full Text Available Aim The present study evaluated the morphological and chemical changes of dentin produced by different sterilization methods, using scanning electron microscopy (SEM and energy-dispersive X-ray spectrometry (EDS analysis. Material and method Five human teeth were sectioned into 4 samples, each divided into 3 specimens. The specimens were separated into sterilization groups, as follows: wet heat under pressure; cobalt 60 gamma radiation; and control (without sterilization. After sterilization, the 60 specimens were analyzed by SEM under 3 magnifications: 1500X, 5000X, and 10000X. The images were analyzed by 3 calibrated examiners, who assigned scores according to the changes observed in the dentinal tubules: 0 = no morphological change; 1, 2 and 3 = slight, medium and complete obliteration of the dentinal tubules. The chemical composition of dentin was assessed by EDS, with 15 kV incidence and 1 μm penetration. Result The data obtained were submitted to the statistical tests of Kruskall-Wallis and ANOVA. It was observed that both sterilization methods – with autoclave and with cobalt 60 gamma radiation – produced no significant changes to the morphology of the dentinal tubules or to the chemical composition of dentin. Conclusion Both methods may thus be used to sterilize teeth for research conducted in vitro.

Effect of dentin biomodifiers on the immediate and long-term bond strengths of a simplified etch and rinse adhesive to dentin

Directory of Open Access Journals (Sweden)

Payal Singh

2017-07-01

Full Text Available Objectives This in vitro study evaluated the effect of dentin biomodifiers on the immediate and long-term bond strengths of a simplified etch and rinse adhesive to dentin. Materials and Methods Flat coronal dentin surfaces were prepared in 120 extracted human molars. Teeth were randomly divided into 5 groups (n = 24 according to 5 different surface pre-treatments: No pre-treatment (control; 1M carbodiimide (EDC; 0.1% epigallocatechin-3-gallate (EGCG; 2% minocycline (MI; 10% sodium ascorbate (SA. After surface pre-treatment, adhesive (Adper Single Bond 2 [SB], 3M ESPE was applied. Composite was applied into transparent plastic tubes (2.5 mm in diameter, which was placed over the bonded dentin surface. From each group, 10 samples were subjected to shear bond strength (SBS evaluation at 24 hours (immediate and remaining 10 samples were tested after 6 months (delayed. Additionally, 4 samples per group were subjected to scanning electron microscopic analysis for observation of resin-dentin interface. The data were statistically analysed with Shaperio‑Wilk W test, 2-way analysis of variance (ANOVA, and post hoc Tukey's test. Results At 24 hours, SBS of all surface pre-treatment groups were comparable with the control group, with significant differences found between EDC and SA groups only (p = 0.009. After 6 months storage, EDC, EGCG, and MI pre-treatments preserved the resin-dentin bond strength with no significant fall. Conclusions Dentin pre-treatment with all the dentin biomodifiers except SA resulted in significant preservation of resin-dentin bond over 6 months storage period, without negatively affecting the immediate bond strength of the etch and rinse adhesive tested.

In vitro effect of Q-switched Nd:YAG laser exposure on morphology, hydroxyapatite composition and microhardness properties of human dentin

Directory of Open Access Journals (Sweden)

Retna Apsari

2011-12-01

Full Text Available Background: A Q-switched Nd:YAG laser was employed as a source of ablation. The fundamental wavelength of the laser is 1064 nm, with pulse duration of 8 nanosecond operates with uniphase mode of TEM00. In the following experiments, dentin samples (without caries and plaque are exposed to pulse laser with Q-switching effect at various energy dose. Purpose: The aim of this study was to investigate the effect of laser ablation on dentin samples using Q-switched Nd:YAG laser exposure. Methods: The laser was operated in repetitive mode with frequency of 10 Hz. The energy dose of the laser was ranging from 13.9 J/cm2, 21.2 J/cm2 and 41.7 J/cm2. The target material comprised of human dentin. The laser was exposed in one mode with Q-switched Nd:YAG laser. Energy delivered to the target through free beam technique. The exposed human dentin was examined by using x-ray diffraction (XRD and fluoresence scanning electron microscopy for energy dispersive (FESEM-EDAX. Microhardness of human dentin were examined by using microhardness vickers test (MVT. Results: The result obtained showed that the composition of hydroxyapatite of the dentin after exposed by Q-switched Nd:YAG laser are 75.02% to 78.21%, with microhardness of 38.7 kgf/mm2 to 86.6 kgf/mm2. This indicated that exposed pulsed Nd:YAG laser on the human dentin attributed to the phototermal effect. The power density created by the Q-switched Nd:YAG laser enables the heat to produce optical breakdown (melting and hole associated with plasma formation and shock wave propagation, from energy dose of 21.2 J/cm2. From XRD analysis showed that the exposure of Nd:YAG laser did not involve in changing the crystal structure of the dentin, but due to photoablation effect. Conclusion: In conclusion, the application of Q-switched Nd:YAG laser as contactless drills in dentistry should be regarded as an alternative to the classical mechanical technique to improve the quality of the dentin treatment.Latar belakang

Bonding stability of adhesive systems to eroded dentin

Directory of Open Access Journals (Sweden)

Janaina Barros CRUZ

2015-01-01

Full Text Available This in vitro study evaluated the immediate and 6 months microshear bond strength (µSBS of different adhesive systems to sound and eroded dentin. Sixty bovine incisors were embedded in acrylic resin and ground to obtain flat buccal dentin surfaces. Specimens were randomly allocated into two groups: sound dentin (immersion in artificial saliva and eroded dentin (erosive challenge following a pH cycling model comprising 4 ×/day Sprite Light® drink for 10 days. Then, specimens were reassigned according to the adhesive system: etch-and-rinse adhesive (Adper Single Bond, two-step self-etch system (Clearfil SE Bond, or one-step self-etch adhesive (Adper Easy One. Polyethylene tubes with an internal diameter of 0.76 mm were placed over pre-treated dentin and filled with resin composite (Z250. Half of the specimens were evaluated by the µSBS test after 24 h, and the other half 6 months later, after water storage at 37°C. Failure mode was evaluated using a stereomicroscope (400×. Data were analyzed by three-way repeated measures analysis of variance and Tukey’s post hoc tests (α = 0.05. After 6 months of water aging, marked reductions in µSBS values were observed, irrespective of the substrate. The µSBS values for eroded dentin were lower than those obtained for sound dentin. No difference in bonding effectiveness was observed among adhesive systems. For all groups, adhesive/mixed failure was observed. In conclusion, eroded dentin compromises the bonding quality of adhesive systems over time.

Penetration of amalgam constituents into dentine

NARCIS (Netherlands)

Scholtanus, Johannes D.; Ozcan, Mutlu; Huysmans, Marie-Charlotte D. N. J. M.

Objectives: Amalgam restorations are replaced by adhesively placed composite resin restorations at an increasing rate. After the removal of amalgam dentine often shows marked dark discoloration that is attributed to the penetration of corrosion products from overlying amalgams. it is questioned

Penetration of amalgam constituents into dentine.

NARCIS (Netherlands)

Scholtanus, J.D.; Ozcan, M.; Huysmans, M.C.D.N.J.M.

2009-01-01

OBJECTIVES: Amalgam restorations are replaced by adhesively placed composite resin restorations at an increasing rate. After the removal of amalgam dentine often shows marked dark discoloration that is attributed to the penetration of corrosion products from overlying amalgams. It is questioned

Micro energy-dispersive x-ray fluorescence spectrometry study of dentin coating with nanobiomaterials

Science.gov (United States)

Soares, Luís. Eduardo Silva; Nahorny, Sídnei; Marciano, Fernanda Roberta; Zanin, Hudson; Lobo, Anderson de Oliveira

2015-06-01

New biomaterials such as multi-walled carbon nanotubes oxide/graphene oxide (MWCNTO/GO), nanohydroxyapatite (nHAp) and combination of them together or not to acidulated phosphate fluoride gel (F) have been tested as protective coating before root dentin erosion. Fourteen bovine teeth were cleaned, polished, divided into two parts (n=28) and assigned to seven groups: (Control) - without previous surface treatment; F treatment; nHAp; MWCNTO/GO; F+nHAp; F+MWCNTO/GO and F+MWCNTO/GO/nHAp composites. Each sample had two sites of pre-treatments: acid etched area and an area without treatment. After the biomaterials application, the samples were submitted to six cycles (demineralization: orange juice, 10 min; remineralization: artificial saliva, 1 h). Micro energy-dispersive X-ray fluorescence spectrometry (μ-EDXRF) mapping area analyses were performed after erosive cycling on both sites (n=84). μ-EDXRF mappings showed that artificial saliva and MWCNTO/GO/nHAp/F composite treatments produced lower dentin demineralization than in the other groups. Exposed dentin tubules allowed better interaction of nanobiomaterials than in smear layer covered dentin. Association of fluoride with other biomaterials had a positive influence on acid etched dentin. MWCNTO/GO/nHAp/F composite treatment resulted in levels of demineralization similar to the control group.

Advances in dental veneers: materials, applications, and techniques.

Science.gov (United States)

Pini, Núbia Pavesi; Aguiar, Flávio Henrique Baggio; Lima, Débora Alves Nunes Leite; Lovadino, José Roberto; Terada, Raquel Sano Suga; Pascotto, Renata Corrêa

2012-01-01

Laminate veneers are a conservative treatment of unaesthetic anterior teeth. The continued development of dental ceramics offers clinicians many options for creating highly aesthetic and functional porcelain veneers. This evolution of materials, ceramics, and adhesive systems permits improvement of the aesthetic of the smile and the self-esteem of the patient. Clinicians should understand the latest ceramic materials in order to be able to recommend them and their applications and techniques, and to ensure the success of the clinical case. The current literature was reviewed to search for the most important parameters determining the long-term success, correct application, and clinical limitations of porcelain veneers.

3D-characterization of the veneer-zirconia interface using FIB nano-tomography.

Science.gov (United States)

Mainjot, Amélie K; Douillard, Thierry; Gremillard, Laurent; Sadoun, Michaël J; Chevalier, Jérôme

2013-02-01

The phenomena occurring during zirconia frameworks veneering process are not yet fully understood. In particular the study of zirconia behavior at the interface with the veneer remains a challenge. However this interface has been reported to act on residual stress in the veneering ceramic, which plays a significant role in clinical failures such as chipping. The objective of this study was thus to investigate the veneer-zirconia interface using a recent 3D-analysis tool and to confront these observations to residual stress measurements in the veneering ceramic. Two cross-sectioned bilayered disc samples (veneer on zirconia), exhibiting different residual stress profiles in the veneering ceramic, were investigated using 2D and 3D imaging (respectively Scanning Electron Microscopy (SEM) and Focused Ion Beam nanotomography (FIB-nt), associated with chemical analysis by Energy Dispersive X-ray Spectroscopy (EDS). The observations did not reveal any structural change in the bulk of zirconia layer of both samples. However the presence of structural alterations and sub-surface microcracks were highlighted in the first micrometer of zirconia surface, exclusively for the sample exhibiting interior tensile stress in the veneering ceramic. No interdiffusion phenomena were observed. FIB nanotomography was proven to be a powerful technique to study the veneer-zirconia interface. The determination of the origin and the nature of zirconia alterations need to be further studied. The results of the present study support the hypothesis that zirconia surface property changes could be involved in the development of tensile stress in the veneering ceramic, increasing the risk of chipping. Copyright © 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Fracture mechanics analyses of ceramic/veneer interface under mixed-mode loading.

Science.gov (United States)

Wang, Gaoqi; Zhang, Song; Bian, Cuirong; Kong, Hui

2014-11-01

Few studies have focused on the interface fracture performance of zirconia/veneer bilayered structure, which plays an important role in dental all-ceramic restorations. The purpose of this study was to evaluate the fracture mechanics performance of zirconia/veneer interface in a wide range of mode-mixities (at phase angles ranging from 0° to 90°), and to examine the effect of mechanical properties of the materials and the interface on the fracture initiation and crack path of an interfacial crack. A modified sandwich test configuration with an oblique interfacial crack was proposed and calibrated to choose the appropriate geometry dimensions by means of finite element analysis. The specimens with different interface inclination angles were tested to failure under three-point bending configuration. Interface fracture parameters were obtained with finite element analyses. Based on the interfacial fracture mechanics, three fracture criteria for crack kinking were used to predict crack initiation and propagation. In addition, the effects of residual stresses due to coefficient of thermal expansion mismatch between zirconia and veneer on the crack behavior were evaluated. The crack initiation and propagation were well predicted by the three fracture criteria. For specimens at phase angle of 0, the cracks propagated in the interface; whereas for all the other specimens the cracks kinked into the veneer. Compressive residual stresses in the veneer can improve the toughness of the interface structure. The results suggest that, in zirconia/veneer bilayered structure the veneer is weaker than the interface, which can be used to explain the clinical phenomenon that veneer chipping rate is larger than interface delamination rate. Consequently, a veneer material with larger fracture toughness is needed to decrease the failure rate of all-ceramic restorations. And the coefficient of thermal expansion mismatch of the substrates can be larger to produce larger compressive

Masking ability of bi- and tri- laminate all-ceramic veneers on tooth-colored ceramic discs.

Science.gov (United States)

Farhan, Daniel; Sukumar, Smitha; von Stein-Lausnitz, Axel; Aarabi, Ghazal; Alawneh, Ahmad; Reissmann, Daniel R

2014-01-01

A predictable esthetic outcome is imperative when placing ceramic veneers. Discolored teeth pose a major challenge as sufficient material thickness is required to achieve a good esthetic result. There is limited evidence in the literature that compares the masking ability of multi-laminate veneers. The aim of this in-vitro study was to compare the masking ability of bi-laminate (BL) and tri-laminate (TL) all-ceramic veneers cemented on tooth-colored ceramic discs. A total of 40 veneers (shade A1, 10-mm diameter, 0.8-mm thick) were manufactured-20 BL veneers (0.4-mm pressable ceramic coping veneered with 0.4-mm thick enamel layer) and 20 TL veneers (0.4-mm coping veneered with 0.2-mm thick opaque interlayer and 0.2-mm thick enamel layer). A bonding apparatus was utilized to adhesively cement all veneers on the ceramic discs (shade A1), simulating teeth of light and dark color. The resulting groups (N = 10 each) were the reference groups (shade A1 ceramic base) BL-1 and TL-1 veneers, and the test groups (shade A4 ceramic base) BL-4 and TL-4 veneers. The color of the cemented veneers was measured using a spectrophotometer. The data were converted to CIE L*a*b* coordinates, and ΔE* were calculated to allow for statistical analysis. The color differences between the samples with the A1 and A4 ceramic bases were significantly lower when covered with TL veneers (mean ΔE*: 3.2 units) than with BL veneers (mean ΔE*: 4.0 units: p bi-laminate veneers. Patients with discolored/darker teeth may benefit from a more predictable esthetic result when teeth restored with tri-laminate rather than bi-laminate veneers. © 2014 Wiley Periodicals, Inc.

Influence of dentinal regions on bond strengths of different adhesive systems.

Science.gov (United States)

Ozer, F; Unlü, N; Sengun, A

2003-06-01

This in vitro study assessed comparatively the shear bond strengths of three composite resins, 3M Valux Plus (3MVP), Herculite (H), Clearfil AP-X (CAP-X), a polyacid modified composite resin Dyract (D), and a resin modified glass-ionomer materials Vitremer (V), to cervical and buccal dentine regions of extracted human molar teeth. Four different bonding systems, 3M ScotchBond Multipurpose (SB), Clearfil Liner Bond 2 (LB2), Opti Bond (OB), and Prime & Bond 2.1 (PB 2.1) were used with the manufacturer's respective composite and compomer materials. One hundred freshly extracted mandibular molar teeth were selected for this study. Flat buccal dentine surfaces were created on 50 teeth and cylindrical rods of the five materials were bonded to the dentine surfaces. For assessment of cervical bond strengths, the materials were bonded to mesial and distal enamel bordered occlusal dentinal surfaces of the remaining 50 teeth. The five groups of restorative procedures were applied as follows; Group 1: SB + 3MVP, Group 2: LB2 + CAP-X, Group 3: OB + H, Group 4: PB2.1 + D, Group 5: Vitremer primer (VP) VP + V. Each restorative procedure thus had 20 specimens (10 buccal + 10 cervical). After 24 h of water storage (37 degrees C), the specimens were tested on a Universal Testing machine in shear with a cross head speed of 0.5 mm min-1. The bond strength values were calculated in MPa and the results were evaluated statistically using Kruskal-Wallis one-way/anova and Mann-Whitney U-tests. It was found that the bond strengths of SB + 3MVP, LB2 + CAP-X and VP + V to buccal dentine surfaces were significantly stronger (P 0.05). Vitremer was found the least successful adhesive material in terms of shear bond strength on both buccal and occluso-cervical dentine surfaces.

UV curing of teak veneers for decorative panel

International Nuclear Information System (INIS)

Gatot Trimulyadi Rekso; Darsono

1999-01-01

The radiation curing of surface coating of teak veneers for decorative panels has been conducted by using ultra violet (UV) as radiation source. In this experiment teak wood veneer was use as a substrate. Epoxy acrylate (import product,) and unsaturated polyester (locally product) were used as coating materials after being added with difunctional monomer TPGDA, and photo-initiator darocur 1173 or irgacure 184. Irradiation was conducted using 80 watt/cm LTV source at conveyor speed of 3,0 m/min. Parameters observed were viscosity of coating materials, hardness, adhesion, appearance, abrasion and chemical resistance of cured films. In general the results showed that viscosity of the formulations based on epoxy acrylate and unsaturated polyester resin were effected by the storage. Film cured by LTV made of epoxy acrylate and unsaturated polyester on the teak veneer wood have the same adhesion and abrasion resistant properties but the hardness and chemical resistant of epoxy acrylate are better than unsaturated polyester. From the experiment result it can be concluded the unsaturated polyester (locally product) can be used as radiation curable material for coating teak veneer panels

Characterization of Genipin-Modified Dentin Collagen

Directory of Open Access Journals (Sweden)

Hiroko Nagaoka

2014-01-01

Full Text Available Application of biomodification techniques to dentin can improve its biochemical and biomechanical properties. Several collagen cross-linking agents have been reported to strengthen the mechanical properties of dentin. However, the characteristics of collagen that has undergone agent-induced biomodification are not well understood. The objective of this study was to analyze the effects of a natural cross-linking agent, genipin (GE, on dentin discoloration, collagen stability, and changes in amino acid composition and lysyl oxidase mediated natural collagen cross-links. Dentin collagen obtained from extracted bovine teeth was treated with three different concentrations of GE (0.01%, 0.1%, and 0.5% for several treatment times (0–24 h. Changes in biochemical properties of NaB3H4-reduced collagen were characterized by amino acid and cross-link analyses. The treatment of dentin collagen with GE resulted in a concentration- and time-dependent pigmentation and stability against bacterial collagenase. The lysyl oxidase-mediated trivalent mature cross-link, pyridinoline, showed no difference among all groups while the major divalent immature cross-link, dehydro-dihydroxylysinonorleucine/its ketoamine in collagen treated with 0.5% GE for 24 h, significantly decreased compared to control (P< 0.05. The newly formed GE-induced cross-links most likely involve lysine and hydroxylysine residues of collagen in a concentration-dependent manner. Some of these cross-links appear to be reducible and stabilized with NaB3H4.

Evaluation of inactivation of intracanal antiseptics by dentin, demineralized dentin, dentin matrix and mineral component of dentin

Directory of Open Access Journals (Sweden)

Razmi H

2007-01-01

Full Text Available Background and Aim: Many studies have shown that microorganisms are the main cause of pulpal diseases and the main purpose of root canal therapy is their elimination from the root canal system. Antiseptic agents are used to reduce bacteria but their antibacterial activities differ from in vivo to in vitro studies and might be inactivated by dentin and its components in root canal space. This study was designed to investigate the effect of dentin on antibacterial activity of different antimicrobial agents. Materials and Methods: In this experimental study, two antibacterial agents (sodium hypochlorite and chlorhexidine with different concentrations were used in four experimental groups: Group 1: dentin, Group 2: demineralized dentin with EDTA, Group 3: dentin matrix and Group 4: dentin mineral component. The species used in this study was Entrococcus faecalis. Different concentration of agents were added to mixture of each experimental group and bacteria. At the baseline and after one and 24 hours, samples were collected and cultured. After incubation period, colonies were counted. Data were analyzed by Tukey test with p<0.05 as the limit of significance. Results: 2% and 0.2% chlorhexidine, and 5% sodium hypochlorite solutions at the three studied times eliminated Entrococcus faecalis completely. 1% sodium hypochlorite eliminated all bacteria in 1h and 24 hs. Statistical analysis showed significant differences between experimental and control groups (P<0.05. Sodium 1% hypochlorite at time 0, could reduce bacteria significantly (P<0.05 but didn’t eliminate them completely. Conclusion: Inactivation of intracanal antiseptics was not observed in this study. As elimination of bacteria occurred, application of these antibacterial agents are recommended in endodontic treatment. Further investigations on other antibacterial agents, other concentrations and shorter time intervals are recommended.

Effects of different peracetic acid formulations on post space radicular dentin.

Science.gov (United States)

Belizário, Lauriê Garcia; Kuga, Milton Carlos; Castro-Núñez, Gabriela Mariana; Escalante-Otárola, Wilfredo Gustavo; Só, Marcus Vinicius Reis; Pereira, Jefferson Ricardo

2018-01-05

The optimal irrigating solution with antimicrobial and dentin cleansing properties for post space preparation for fiber posts is unclear. Peracetic acid is one option but is available in various chemical formulations that require evaluation. The purpose of this in vitro study was to evaluate dentin surface cleanliness based on the presence of a smear layer and the number of open dentin tubules. It also investigates the chemical composition of residues after canal irrigation with a 1% peracetic acid solution (PA) at low or high concentration of hydrogen peroxide during the preparation of intracanal fiber posts. After filling the root canals of 40 mandibular incisors, a rotary instrument was used for intracanal preparation to place fiber posts. The teeth were divided into 4 groups (n=10) according to the post space irrigation protocol as follows: CG (control): distilled water; NA (NaOCl): 2.5% sodium hypochlorite; LH: PA with low concentration of hydrogen peroxide; and HH: PA with high concentrations of hydrogen peroxide. After irrigation, the teeth were sectioned, and the intracanal dentin surface was subjected to analysis using energy dispersive spectroscopy to evaluate chemical composition and to scanning electron microscopy (×500) to evaluate the presence of the smear layer. The number of open dentin tubules was measured by scanning electron microscopy analysis (×2000) using photo-editing software. ANOVA and the Tukey test (α=.05) were used to evaluate the data, except for the presence of a smear layer, for which the Kruskal-Wallis and Dunn tests were used (α=.05). The highest concentrations of oxygen in the dentin residues were detected in LH and HH (P.05). NA had a higher concentration of chlorine (P.05), except for HH, which also had a larger number of open dentin tubules than CG and NA (P<.05). PA 1% with a low concentration of hydrogen peroxide yielded a lower amount of smear layer and a larger number of open dentin tubules in the dentin of the post

Influences of the cold atmospheric plasma jet treatment on the properties of the demineralized dentin surfaces

Science.gov (United States)

Xiaoming, ZHU; Heng, GUO; Jianfeng, ZHOU; Xiaofei, ZHANG; Jian, CHEN; Jing, LI; Heping, LI; Jianguo, TAN

2018-04-01

Improvement of the bonding strength and durability between the dentin surface and the composite resin is a challenging job in dentistry. In this paper, a radio-frequency atmospheric-pressure glow discharge (RF-APGD) plasma jet is employed for the treatment of the acid-etched dentin surfaces used for the composite restoration. The properties of the plasma treated dentin surfaces and the resin-dentin interfaces are analyzed using the x-ray photoemission spectroscopy, contact angle goniometer, scanning electron microscope and microtensile tester. The experimental results show that, due to the abundant chemically reactive species existing in the RF-APGD plasma jet under a stable and low energy input operating mode, the contact angle of the plasma-treated dentin surfaces decreases to a stable level with the increase of the atomic percentage of oxygen in the specimens; the formation of the long resin tags in the scattered clusters and the hybrid layers at the resin-dentin interfaces significantly improve the bonding strength and durability. These results indicate that the RF-APGD plasma jet is an effective tool for modifying the chemical properties of the dentin surfaces, and for improving the immediate bonding strength and the durability of the resin-dentin bonding in dentistry.

[An in vitro study of the fracture strength of tooth preparations for Empress 2 veneers and crowns and mandibular incisors restored with Empress 2 veneers and crowns].

Science.gov (United States)

Wei, Xue; Li, Yan

2009-12-01

To compare the fracture resistance of mandibular incisors' preparations for veneers and crowns, mandibular incisors restored with Empress 2 veneers and crowns. 50 human mandibular incisors were randomly divided into five groups. Each group consisted of ten teeth and the treatment obtained as follows: A, tooth preparations for veneers; B, tooth preparations for crowns; C, teeth restored with veneers; D, teeth restored with crowns; E, untreated group. The teeth received standardized preparation and the restorations were manufactured with Empress 2 system and cemented with resin luting agent. The fracture resistances of teeth were measured by Instron universal testing machine and statistically analyzed with one-way ANOVA. The fracture resistances of A, B, C, D, E were (576.11 +/- 91.53), (204.13 +/- 85.88), (451.50 +/- 116.81), (386.16 +/- 117.75) and (566.05 +/- 121.37) N, respectively. The statistical analysis demonstrated significant differences between five groups. There were no significant differences between group A and E, group C and D. Tooth preparations for veneers did not significantly reduce the fracture resistance of mandibular incisor. The fracture resistance of teeth restored with Empress 2 veneers and crowns did not significantly differ from each other.

Ptychographic X-ray nanotomography quantifies mineral distributions in human dentine

Science.gov (United States)

Zanette, I.; Enders, B.; Dierolf, M.; Thibault, P.; Gradl, R.; Diaz, A.; Guizar-Sicairos, M.; Menzel, A.; Pfeiffer, F.; Zaslansky, P.

2015-03-01

Bones are bio-composites with biologically tunable mechanical properties, where a polymer matrix of nanofibrillar collagen is reinforced by apatite mineral crystals. Some bones, such as antler, form and change rapidly, while other bone tissues, such as human tooth dentine, develop slowly and maintain constant composition and architecture for entire lifetimes. When studying apatite mineral microarchitecture, mineral distributions or mineralization activity of bone-forming cells, representative samples of tissue are best studied at submicrometre resolution while minimizing sample-preparation damage. Here, we demonstrate the power of ptychographic X-ray tomography to map variations in the mineral content distribution in three dimensions and at the nanometre scale. Using this non-destructive method, we observe nanostructures surrounding hollow tracts that exist in human dentine forming dentinal tubules. We reveal unprecedented quantitative details of the ultrastructure clearly revealing the spatially varying mineralization density. Such information is essential for understanding a variety of natural and therapeutic effects for example in bone tissue healing and ageing.

Determination of some variables of human dentin for dosimetric purposes

International Nuclear Information System (INIS)

Peres, C.

1990-01-01

The initial objective of this work is to determine the atomic composition of human dentin, using various techniques of measurements such as X-Ray fluorescence, atomic absorption, spectrophotometry, volumetric analysis, chemistry, colorimetry and thermogravimetry. With the values of the effective atomic number Z bar dependent of the quality of the ionizing radiation, one can find the kind of material that can be used for a phantom equivalent to dentin. (author)

Regulation of Reactionary Dentine Formation.

Science.gov (United States)

Neves, V C M; Sharpe, P T

2018-04-01

During the treatment of dental caries that has not penetrated the tooth pulp, maintenance of as much unaffected dentine as possible is a major goal during the physical removal of decayed mineral. Damage to dentine leads to release of fossilized factors (transforming growth factor-β [TGF-β] and bone morphogenic protein [BMP]) in the dentine that are believed to stimulate odontoblasts to secrete new "tertiary" dentine (reactionary dentine). This is formed on the pulpal surface of existing dentine and rethickens the dentine. We have previously shown that activation of Wnt/β-catenin signaling is pivotal for tooth repair in exposed pulp injury, and the pathway can be activated by small-molecule GSK-3 antagonists, resulting in enhanced reparative dentine formation. Here, we use a nonexposed pulp injury model to investigate the mechanisms of reactionary dentine formation in vivo, using small molecules to modulate the Wnt/β-catenin, TGF-β, and BMP pathways. We found that a local increase of Wnt activation at the injury site enhances reactionary dentine secretion. In addition, inhibition of TGF-β, BMP, or Wnt pathways does not impede reactionary dentine formation, although inhibition of TGF-β and/or BMP signaling does result in more disorganized, nontubular reactionary dentine. This suggests that Wnt/β-catenin signaling plays no major role in the formation of reactionary dentine, but in common with reparative dentine formation, exogenous elevation of Wnt/β-catenin signaling can enhance tertiary dentine formation. Release of latent TGF-β or BMPs from dentine is not required for the deposition of mineral to form reactionary dentine but does play a role in its organization.

Bio-reconstruction of root canal using dentin post

Directory of Open Access Journals (Sweden)

Navin Mishra

2013-01-01

Full Text Available This case report describes the successful management of complicated crown fracture of left maxillary central incisor (#21 of 23-year-old male using dentin (biological post made from human tooth. Endodontic treatment was initiated and sectional obturation was done using ProTaper gutta-percha and AH Plus sealer. The coronal space was modified to receive a human dentin post. A two-step procedure comprising direct and indirect technique of post fabrication was done to achieve the accuracy of biological post. A maxillary cuspid from an institutional tooth bank was taken, sectioned mesiodistally using a diamond disc simulating the length and thickness of mock post. Dentin post was first verified on the plaster model and then cemented in tooth #21. Core build up was done with composite and porcelain fused to metal (PFM crown was luted. On the follow-up visits, patient was asymptomatic and radiographic evaluation revealed normal periradicular architecture. Biological posts may be good alternatives to conventional post systems as they preserve internal dentin walls, provide excellent adhesion, and resilience similar to natural tooth structure.

[A preliminary study on the color effect of IPS Empress all-ceramic veneers].

Science.gov (United States)

Li, Zhi-yong; Cheng, Xiang-rong; Wang, Yi-ning

2004-09-01

To evaluate the opaquing capacity, color compatibility and stability of IPS Empress all-ceramic veneers. A total of 86 IPS Empress all-ceramic veneers were made for 18 patients. The patients were divided into three groups: Group A was tetracycline teeth, 64 veneers for 5 patients; Group B was non-tetracycline teeth, 22 veneers for 13 patients; Group C was 22 natural vital teeth with normal color as control group. Before and after veneers were inserted, ShadeEye NCC was employed to obtain L * a * b * values of each tooth. The values of cemented veneers used as the baseline, the L * a * b * values of each veneer were measured half a year, 1 year, and 2 years after restoration respectively. All L * a * b * values at different evaluation times were analyzed by SPSS 10.0. Before and after veneers were restored, the L * a * b * values of both Group A and Group B were significantly different, the color difference being 5.01 and 4.15 respectively. The color difference between Group A and selected shade guides was 2.45. Compared with the baseline value, the L * value of Group A significantly decreased 2 years after restoration, but the DeltaE of different evaluation times was not significantly different. The color difference between Group B and Group C was 0.22 and there was no significant color difference after restoration. IPS Empress all-ceramic veneers have excellent opaquing capacity, color compatibility and stability to non-tetracycline teeth. To tetracycline teeth IPS Empress all-ceramic veneers have a certain opaquing capacity, but they cannot completely match with shade guides; the L * value is significantly different after restoration and further studies are needed to evaluate its color effect.

Numerical simulation of hot-pressed veneer products: Forming - Spring back – Distortion

DEFF Research Database (Denmark)

Ormarsson, Sigurdur; Sandberg, Dick

2007-01-01

Customers demand very high quality of veneered furniture products with regard to surface appearance, shape stability and stiffness. To meet these requirements, it is important to improve the manufacturing process by a better understanding of the thermo-hygro-mechanical behaviour of the individual...... veneers. During the manufacture of strongly curved products, the veneers are exposed to large membrane and bending deformations and to high pressure in the radial fibre direction. When hot-press forming is used, the veneers are also exposed to a high surface temperature during the pressing time (curing...... time). These severe conditions can result in plastic deformation perpendicular to the veneer surface as well as mechano-sorptive strains in the curved regions, since the heating can have a significant influence on the moisture distribution. How strong an influence these factors have on the distortion...

Peritubular dentin lacks piezoelectricity.

Science.gov (United States)

Habelitz, S; Rodriguez, B J; Marshall, S J; Marshall, G W; Kalinin, S V; Gruverman, A

2007-09-01

Dentin is a mesenchymal tissue, and, as such, is based on a collagenous matrix that is reinforced by apatite mineral. Collagen fibrils show piezoelectricity, a phenomenon that is used by piezoresponse force microscopy (PFM) to obtain high-resolution images. We applied PFM to image human dentin with 10-nm resolution, and to test the hypothesis that zones of piezoactivity, indicating the presence of collagen fibrils, can be distinguished in dentin. Piezoelectricity was observed by PFM in the dentin intertubular matrix, while the peritubular dentin remained without response. High-resolution imaging of chemically treated intertubular dentin attributed the piezoelectric effect to individual collagen fibrils that differed in the signal strength, depending on the fibril orientation. This study supports the hypothesis that peritubular dentin is a non-collagenous tissue and is thus an exception among mineralized tissues that derive from the mesenchyme.

[Preliminary study of bonding strength between diatomite-based dental ceramic and veneering porcelains].

Science.gov (United States)

Lu, Xiao-li; Gao, Mei-qin; Cheng, Yu-ye; Zhang, Fei-min

2015-04-01

In order to choose the best veneering porcelain for diatomite-based dental ceramic substrate, the bonding strength between diatomite-based dental ceramics and veneering porcelains was measured, and the microstructure and elements distribution of interface were analyzed. The coefficient of thermal expansion (CTE) of diatomite-based dental ceramics was detected by dilatometry. Three veneering porcelain materials were selected with the best CTE matching including alumina veneering porcelain (group A), titanium porcelain veneering porcelain (group B), and E-max veneering porcelain (group C). Shear bonding strength was detected. SEM and EDS were used to observe the interface microstructure and element distribution. Statistical analysis was performed using SPSS 17.0 software package. The CTE of diatomite-based dental ceramics at 25-500 degrees centigrade was 8.85×10-6K-1. The diatomite-based substrate ceramics combined best with group C. Shear bonding strength between group A and C and group B and C both showed significant differences(P<0.05). SEM and EDS showed that the interface of group C sintered tightly and elements permeated on both sides of the interface. The diatomite-based substrate ceramics combines better with E-max porcelain veneer.

Effect of Dentin Wetness on the Bond Strength of Universal Adhesives

Directory of Open Access Journals (Sweden)

An-Na Choi

2017-10-01

Full Text Available The effects of dentin wetness on the bond strength and adhesive interface morphology of universal adhesives have been investigated using micro-tensile bond strength (μTBS testing and confocal laser scanning microscopy (CLSM. Seventy-two human third molars were wet ground to expose flat dentin surfaces. They were divided into three groups according to the air-drying time of the dentin surfaces: 0 (without air drying, 5, and 10 s. The dentin surfaces were then treated with three universal adhesives: G-Premio Bond, Single Bond Universal, and All-Bond Universal in self-etch or etch-and-rinse mode. After composite build up, a μTBS test was performed. One additional tooth was prepared for each group by staining the adhesives with 0.01 wt % of Rhodamine B fluorescent dye for CLSM analysis. The data were analyzed statistically using ANOVA and Tukey’s post hoc tests (α = 0.05. Two-way ANOVA showed significant differences among the adhesive systems and dentin moisture conditions. An interaction effect was also observed (p < 0.05. One-way ANOVA showed that All-Bond Universal was the only material influenced by the wetness of the dentin surfaces. Wetness of the dentin surface is a factor influencing the micro-tensile bond strength of universal adhesives.

Veneer industry and timber use, North Central Region, 1980.

Science.gov (United States)

James E. Blyth; W. Brad Smith

1984-01-01

Shows 1980 veneer-log production and receipts by species in the Lake State (Michigan, Minnesota, and Wisconsin) and in the Central States (Illinois, Indiana, Iowa, and Missouri). Comparisons are made with similar data collected in 1976. Includes tables showing veneer-log production and receipts (for selected years) since 1946 in the Lake States and since 1956 in the...

Veneer-log production and receipts, North Central Region, 1976.

Science.gov (United States)

James E. Blyth; Jerold T. Hahn

1978-01-01

Shows 1976 veneer-log production and receipts by species in the Lake States (Michigan, Minnesota, and Wisconsin) and in the Central States (Illinois, Indiana, Iowa, and Missouri). Comparisons are made with similar data for 1974. Includes tables showing veneer-log production and receipts (for selected years) since 1946 in the Lake States and since 1956 in the Central...

Veneer-log production and receipts, North Central Region, 1974.

Science.gov (United States)

James E. Blyth; Jerold T. Hahn

1976-01-01

Shows 1974 veneer-log production and receipts by species in the Lake States (Michigan, Minnesota, and Wisconsin) and in the Central States (Illinois, Indiana, Iowa, and Missouri). Comparisons are made with similar data for 1972. Includes tables showing veneer-log production and receipts (for selected years) since 1946 in the Lake States and since 1956 in the Central...

Collagen Orientation and Crystallite Size in Human Dentin: A Small Angle X-ray Scattering Study

Energy Technology Data Exchange (ETDEWEB)

Pople, John A

2001-03-29

The mechanical properties of dentin are largely determined by the intertubular dentin matrix, which is a complex composite of type I collagen fibers and a carbonate-rich apatite mineral phase. The authors perform a small angle x-ray scattering (SAXS) study on fully mineralized human dentin to quantify this fiber/mineral composite architecture from the nanoscopic through continuum length scales. The SAXS results were consistent with nucleation and growth of the apatite phase within periodic gaps in the collagen fibers. These mineralized fibers were perpendicular to the dentinal tubules and parallel with the mineralization growth front. Within the plane of the mineralization front, the mineralized collagen fibers were isotropic near the pulp, but became mildly anisotropic in the mid-dentin. Analysis of the data also indicated that near the pulp the mineral crystallites were approximately needle-like, and progressed to a more plate-like shape near the dentino-enamel junction. The thickness of these crystallites, {approx} 5 nm, did not vary significantly with position in the tooth. These results were considered within the context of dentinogenesis and maturation.

Effect of Different Saliva Decontamination Procedures on Bond Strength to Dentin in Single Bottle Systems

Directory of Open Access Journals (Sweden)

M. Ghavam

2004-09-01

Full Text Available Statement of Problem: Following the increasing use of composites in restoring anterior and posterior teeth, problems due to its technique sensitivity have become a major concern.One of these problems is the possibility of contamination of dentin with saliva, blood and/or gingival fluid in different stages of bonding procedure, even with application of different methods of isolation. However, by introduction of Single-bottle dentin adhesives,the contamination possibility reduced to two stages. Scientific documents show that saliva contamination reduces bond strength of composites to dentin. Application of simple and efficient methods for reducing or eliminating saliva contamination enables clinicians to carry out dental treatment without any concern about deterioration of clinical longevity of restoration.Purpose: This study was designed to compare the effect of different decontamination methods on the shear bond strength of composite to dentin using a “Single-bottle” adhesive.Materials and Methods: Seventy-two extracted sound human molars and premolars were selected. Enamel of buccal surface was ground flat to expose dentin. The teeth were divided into 9 groups of 8 each. In control group (1 the adhesive “Excite” was used according tothe manufacturer, without any contamination. Conditioned and saliva contaminated dentin was (2 rinsed and blot dried, (3 rinsed, dried and re-etched. In groups 4, 5, 6 uncured adhesive was saliva contaminated and then: (4 only blot dried (5 rinsed, blot dried with adhesive reapplication and (6 resurfaced with bur, rinsed, dried and followed by repeating the whole process. In groups 7, 8, 9 cured adhesive was contaminated with saliva and then:(7 rinsed and dried (8 rinsed, blot dried with adhesive reapplication (9 same as group (6.Then “Tetric Ceram” composite cylinders were bonded to dentin surfaces. Samples were thermo cycled in 5°C and 55°C water, 30 seconds in each bath with a dowel time of 10

Fracture and Fatigue Resistance of Cemented versus Fused CAD-on Veneers over Customized Zirconia Implant Abutments.

Science.gov (United States)

Nossair, Shereen Ahmed; Aboushelib, Moustafa N; Morsi, Tarek Salah

2015-01-05

To evaluate the fracture mechanics of cemented versus fused CAD-on veneers on customized zirconia implant abutments. Forty-five identical customized CAD/CAM zirconia implant abutments (0.5 mm thick) were prepared and seated on short titanium implant abutments (Ti base). A second scan was made to fabricate 45 CAD-on veneers (IPS Empress CAD, A2). Fifteen CAD-on veneers were cemented on the zirconia abutments (Panavia F2.0). Another 15 were fused to the zirconia abutments using low-fusing glass, while manually layered veneers served as control (n = 15). The restorations were subjected to artificial aging (3.2 million cycles between 5 and 10 kg in a water bath at 37°C) before being axially loaded to failure. Fractured specimens were examined using scanning electron microscopy to detect fracture origin, location, and size of critical crack. Stress at failure was calculated using fractography principles (alpha = 0.05). Cemented CAD-on restorations demonstrated significantly higher (F = 72, p CAD-on and manually layered restorations. Fractographic analysis of fractured specimens indicated that cemented CAD-on veneers failed due to radial cracks originating from the veneer/resin interface. Branching of the critical crack was observed in the bulk of the veneer. Fused CAD-on veneers demonstrated cohesive fracture originating at the thickest part of the veneer ceramic, while manually layered veneers failed due to interfacial fracture at the zirconia/veneer interface. Within the limitations of this study, cemented CAD-on veneers on customized zirconia implant abutments demonstrated higher fracture than fused and manually layered veneers. © 2014 by the American College of Prosthodontists.

Comprehensive analyses of how tubule occlusion and advanced glycation end-products diminish strength of aged dentin

Science.gov (United States)

Shinno, Yuko; Ishimoto, Takuya; Saito, Mitsuru; Uemura, Reo; Arino, Masumi; Marumo, Keishi; Nakano, Takayoshi; Hayashi, Mikako

2016-01-01

In clinical dentistry, since fracture is a major cause of tooth loss, better understanding of mechanical properties of teeth structures is important. Dentin, the major hard tissue of teeth, has similar composition to bone. In this study, we investigated the mechanical properties of human dentin not only in terms of mineral density but also using structural and quality parameters as recently accepted in evaluating bone strength. Aged crown and root dentin (age ≥ 40) exhibited significantly lower flexural strength and toughness than young dentin (age mineral density; but showed significantly lower flexural strength than young dentin. Dentin with strong alignment of the c-axis in hydroxyapatite exhibited high fracture strength, possibly because the aligned apatite along the collagen fibrils may reinforce the intertubular dentin. Aged dentin, showing a high advanced glycation end-products (AGEs) level in its collagen, recorded low flexural strength. We first comprehensively identified significant factors, which affected the inferior mechanical properties of aged dentin. The low mechanical strength of aged dentin is caused by the high mineral density resulting from occlusion of dentinal tubules and accumulation of AGEs in dentin collagen.

Temperature changes under demineralized dentin during polymerization of three resin-based restorative materials using QTH and LED units.

Science.gov (United States)

Mousavinasab, Sayed-Mostafa; Khoroushi, Maryam; Moharreri, Mohammadreza; Atai, Mohammad

2014-08-01

Light-curing of resin-based materials (RBMs) increases the pulp chamber temperature, with detrimental effects on the vital pulp. This in vitro study compared the temperature rise under demineralized human tooth dentin during light-curing and the degrees of conversion (DCs) of three different RBMs using quartz tungsten halogen (QTH) and light-emitting diode (LED) units (LCUs). Demineralized and non-demineralized dentin disks were prepared from 120 extracted human mandibular molars. The temperature rise under the dentin disks (n = 12) during the light-curing of three RBMs, i.e. an Ormocer-based composite resin (Ceram. X, Dentsply DeTrey), a low-shrinkage silorane-based composite (Filtek P90, 3M ESPE), and a giomer (Beautifil II, Shofu GmbH), was measured with a K-type thermocouple wire. The DCs of the materials were investigated using Fourier transform infrared spectroscopy. The temperature rise under the demineralized dentin disks was higher than that under the non-demineralized dentin disks during the polymerization of all restorative materials (p 0.05). Although there were no significant differences in the DCs, the temperature rise under demineralized dentin disks for the silorane-based composite was higher than that for dimethacrylate-based restorative materials, particularly with QTH LCU.

Temperature changes under demineralized dentin during polymerization of three resin-based restorative materials using QTH and LED units

Directory of Open Access Journals (Sweden)

Sayed-Mostafa Mousavinasab

2014-08-01

Full Text Available Objectives Light-curing of resin-based materials (RBMs increases the pulp chamber temperature, with detrimental effects on the vital pulp. This in vitro study compared the temperature rise under demineralized human tooth dentin during light-curing and the degrees of conversion (DCs of three different RBMs using quartz tungsten halogen (QTH and light-emitting diode (LED units (LCUs. Materials and Methods Demineralized and non-demineralized dentin disks were prepared from 120 extracted human mandibular molars. The temperature rise under the dentin disks (n = 12 during the light-curing of three RBMs, i.e. an Ormocer-based composite resin (Ceram. X, Dentsply DeTrey, a low-shrinkage silorane-based composite (Filtek P90, 3M ESPE, and a giomer (Beautifil II, Shofu GmbH, was measured with a K-type thermocouple wire. The DCs of the materials were investigated using Fourier transform infrared spectroscopy. Results The temperature rise under the demineralized dentin disks was higher than that under the non-demineralized dentin disks during the polymerization of all restorative materials (p 0.05. Conclusions Although there were no significant differences in the DCs, the temperature rise under demineralized dentin disks for the silorane-based composite was higher than that for dimethacrylate-based restorative materials, particularly with QTH LCU.

Durable bonds at the adhesive/dentin interface: an impossible mission or simply a moving target?

Science.gov (United States)

SPENCER, Paulette; Jonggu PARK, Qiang YE; MISRA, Anil; BOHATY, Brenda S.; SINGH, Viraj; PARTHASARATHY, Ranga; SENE, Fábio; de Paiva GONÇALVES, Sérgio Eduardo; LAURENCE, Jennifer

2013-01-01

Composite restorations have higher failure rates, more recurrent caries and increased frequency of replacement as compared to dental amalgam. Penetration of bacterial enzymes, oral fluids, and bacteria into the crevices between the tooth and composite undermines the restoration and leads to recurrent decay and failure. The gingival margin of composite restora tions is particularly vulnerable to decay and at this margin, the adhesive and its seal to dentin provides the primary barrier between the prepared tooth and the environment. The intent of this article is to examine physico-chemical factors that affect the integrity and durability of the adhesive/dentin interfacial bond; and to explore how these factors act synergistically with mechanical forces to undermine the composite restoration. The article will examine the various avenues that have been pursued to address these problems and it will explore how alterations in material chemistry could address the detrimental impact of physico-chemical stresses on the bond formed at the adhesive/dentin interface. PMID:24855586

Bonding strategies for MIH-affected enamel and dentin.

Science.gov (United States)

Krämer, Norbert; Bui Khac, Ngoc-Han Nana; Lücker, Susanne; Stachniss, Vitus; Frankenberger, Roland

2018-02-01

Aim of the present study was to evaluate resin composite adhesion to dental hard tissues affected by molar incisor hypomineralisation (MIH). 94 freshly extracted human molars and incisors (53 suffering MIH) were used. 68 teeth (35 with MIH) were used for μ-TBS tests in enamel and dentin, 26 (18 with MIH) for qualitative evaluation. Specimens were bonded with Clearfil SE Bond, Scotchbond Universal, and OptiBond FL. For MIH affected enamel, additional OptiBond FL groups with NaOCl and NaOCl+Icon were investigated. Beside fractographic analysis, also qualitative evaluations were performed using SEM at different magnifications as well as histological sectioning. Highest μ-TBS values were recorded with dentin specimens (ANOVA, mod. LSD, p0.05). Pre-test failures did not occur in dentin specimens. Sound enamel specimens exhibited significantly higher μ-TBS values than MIH enamel (p0.05), however, it caused less pre-test failures (pMIH enamel is the limiting factor in adhesion to MIH teeth. MIH-affected dentin may be bonded conventionally. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Dentine microhardness after different methods for detection and removal of carious dentine tissue

Directory of Open Access Journals (Sweden)

Fernanda Brandão Mollica

2012-08-01

Full Text Available There are several methods for identifying carious dentinal tissue aiming to avoid removal of healthy dentinal tissue. OBJECTIVES: The purpose of this study was to test different methods for the detection of carious dentinal tissue regarding the amount of carious tissue removed and the remaining dentin microhardness after caries removal. MATERIAL AND METHODS: The dentin surfaces of 20 bovine teeth were exposed and half of the surface was protected with nail polish. Cariogenic challenge was performed by immersion in a demineralizing solution for 14 days. After transverse cross-section of the crown, the specimens were divided into four groups (n=10, according to the method used to identify and remove the carious tissue: "Papacárie", Caries-detector dye, DIAGNOdent and Tactile method. After caries removal, the cross-sectional surface was included in acrylic resin and polished. In a microhardness tester, the removed dentin thickness and the Vickers microhardness of the following regions were evaluated: remaining dentin after caries removal and superficial and deep healthy dentin. RESULTS: ANOVA and Tukey's test (α=0.05 were performed, except for DIAGNOdent, which did not detect the presence of caries. Results for removed dentin thickness were: "Papacárie" (424.7±105.0; a, Caries-detector dye (370.5±78.3; ab, Tactile method (322.8±51.5; bc. Results for the remaining dentin microhardness were: "Papacárie" (42.2±10.5; bc, Caries-detector dye (44.6±11.8; abc, Tactile method (24.3±9.0; d. CONCLUSIONS: DIAGNOdent did not detect the presence of carious tissue; Tactile method and "Papacárie" resulted in the least and the most dentinal thickness removal, respectively; Tactile method differed significantly from "Papacárie" and Caries-detector dye in terms of the remaining dentin microhardness, and Tactile method was the one which presented the lowest microhardness values.

Influence of curing rate of resin composite on the bond strength to dentin

DEFF Research Database (Denmark)

Benetti, Ana Raquel; Asmussen, E; Peutzfeldt, A

2007-01-01

@ 1000 mW/cm2) for all groups. A split Teflon mold was clamped to the treated dentin surface and filled with resin composite. The rate of cure was varied, using one of four LED-curing units of different power densities. The rate of cure was also varied using the continuous or pulse-delay mode....... In continuous curing mode, in order to give an energy density totaling 16 J/cm2, the power densities (1000, 720, 550, 200 mW/cm2) emitted by the various curing units were compensated for by the light curing period (16, 22, 29 or 80 seconds). In the pulse-delay curing mode, two seconds of light curing at one...... of the four power densities was followed by a one-minute interval, after which light cure was completed (14, 29, 27 or 78 seconds), likewise, giving a total energy density of 16 J/cm2. The specimens produced for each of the eight curing protocols and two resin composites (Tetric EvoCeram, Ivoclar Vivadent...

Effect of Dentin Wetness on the Bond Strength of Universal Adhesives

Science.gov (United States)

Lee, Ji-Hye; Son, Sung-Ae; Jung, Kyoung-Hwa; Kwon, Yong Hoon

2017-01-01

The effects of dentin wetness on the bond strength and adhesive interface morphology of universal adhesives have been investigated using micro-tensile bond strength (μTBS) testing and confocal laser scanning microscopy (CLSM). Seventy-two human third molars were wet ground to expose flat dentin surfaces. They were divided into three groups according to the air-drying time of the dentin surfaces: 0 (without air drying), 5, and 10 s. The dentin surfaces were then treated with three universal adhesives: G-Premio Bond, Single Bond Universal, and All-Bond Universal in self-etch or etch-and-rinse mode. After composite build up, a μTBS test was performed. One additional tooth was prepared for each group by staining the adhesives with 0.01 wt % of Rhodamine B fluorescent dye for CLSM analysis. The data were analyzed statistically using ANOVA and Tukey’s post hoc tests (α = 0.05). Two-way ANOVA showed significant differences among the adhesive systems and dentin moisture conditions. An interaction effect was also observed (p adhesives. PMID:29068404

The effect of erbium family laser on tensile bond strength of composite to dentin in comparison with conventional method.

Science.gov (United States)

Shahabi, Sima; Chiniforush, Nasim; Bahramian, Hoda; Monzavi, Abbas; Baghalian, Ali; Kharazifard, Mohammad Javad

2013-01-01

The purpose of this study was to evaluate the effect of Er:YAG and Er,Cr:YSGG laser on tensile bond strength of composite resin to dentine in comparison with bur-prepared cavities. Fifteen extracted caries-free human third molars were selected. The teeth were cut at a level below the occlusal pit and fissure plan and randomly divided into three groups. Five cavities were prepared by diamond bur, five cavities prepared by Er:YAG laser, and the other group prepared by Er,Cr:YSGG laser. Then, all the cavities were restored by composite resin. The teeth were sectioned longitudinally with Isomet and the specimens prepared in dumbbelled shape (n = 36). The samples were attached to special jigs, and the tensile bond strength of the three groups was measured by universal testing machine at a speed of 0.5 mm/min. The results of the three groups were analyzed with one-way ANOVA and Tamhane test. The means and standard deviations of tensile bond strength of bur-cut, Er:YAG laser-ablated, and Er,Cr:YSGG laser-ablated dentine were 5.04 ± 0.93, 13.37 ± 3.87, and 4.85 ± 0.93 MPa, respectively. There is little difference in tensile bond strength of composite resin in Er,Cr:YSGG lased-prepared cavities in comparison with bur-prepared cavities, but the Er:YAG laser group showed higher bond strength than the other groups.

Microtensile bond strength of etch-and-rinse and self-etching adhesives to intrapulpal dentin after endodontic irrigation and setting of root canal sealer.

Science.gov (United States)

Wattanawongpitak, Nipaporn; Nakajima, Masatoshi; Ikeda, Masaomi; Foxton, Richard M; Tagami, Junji

2009-02-01

To evaluate the effect of endodontic irrigation regimens and calcium hydroxide root canal sealer (Sealapex) on the microtensile bond strengths (muTBS) of dual-curing resin composite (Clearfil DC Core Automix) to the intrapulpal dentin. Forty standardized coronal-half root canal dentin specimens obtained from human premolars were divided into 4 groups: group A, no treatment (control); group B, Sealapex; group C, NaOCl/Sealapex; group D, EDTA/NaOCl/Sealapex. After 7 days of storage in 100% relative humidity, Sealapex was removed. Dentin surfaces were bonded with adhesives, either etch-and-rinse (Single Bond) or self-etching (Clearfil SE Bond), and built up with resin composite. The bonded specimens were trimmed into an hourglass shape with a 1-mm2 cross-sectional area for microtensile testing (n = 20). The muTBS to intrapulpal dentin was analyzed using two-way ANOVA and Dunnett's TC test. Two teeth of each group were prepared for micromorphological analysis of dentin surface. The root canal sealer with or without endodontic irrigation significantly affected the bond strengths of resin composite to intrapulpal dentin compared with the control group (p 0.05). The dentin surface was covered with a mud-like material after sealer application for 7 days. The root canal sealer reduced the muTBS of dual-curing resin composite with etch-and-rinse and self-etching adhesive systems to intrapulpal dentin. Treatment with EDTA followed by NaOCI prior to obturation caused an additional reduction in muTBS of both adhesive systems to intrapulpal dentin.

Three-unit posterior zirconia-ceramic fixed dental prostheses (FDPs) veneered with layered and milled (CAD-on) veneering ceramics: 1-year follow-up of a randomized controlled clinical trial.

Science.gov (United States)

Grohmann, Philipp; Bindl, Andreas; Hämmerle, Christoph; Mehl, Albert; Sailer, Irena

2015-01-01

The aim of this multicenter randomized controlled clinical trial was to test posterior zirconia-ceramic fixed dental prostheses (FDPs) veneered with a computer-aided design/computer- assisted manufacture (CAD/CAM) lithium disilicate veneering ceramic (CAD-on) and manually layered zirconia veneering ceramic with respect to survival of the FDPs, and technical and biologic outcomes. Sixty patients in need of one posterior three-unit FDP were included. The zirconia frameworks were produced with a CAD/CAM system (Cerec inLab 3D/Cerec inEOS inLab). Thirty FDPs were veneered with a CAD/CAM lithium disilicate veneering ceramic (Cad-on) (test) and 30 were veneered with a layered zirconia veneering ceramic (control). For the clinical evaluation at baseline, 6, and 12 months, the United States Public Health Service (USPHS) criteria were used. The biologic outcome was judged by comparing the plaque control record (PCR), bleeding on probing (BOP), and probing pocket depth (PPD). Data were statistically analyzed. Fifty-six patients were examined at a mean follow-up of 13.9 months. At the 1-year follow-up the survival rate was 100% in the test and in the control group. No significant differences of the technical outcomes occurred. Major chipping occurred in the control group (n = 3) and predominantly minor chipping in the test group (minor n = 2, major n = 1). No biologic problems or differences were found. Both types of zirconia-ceramic FDPs exhibited very good clinical outcomes without differences between groups. Chipping occurred in both types of FDPs at small amounts, yet the extension of the chippings differed. The test FDPs predominantly exhibited minor chipping, the control FDPs major chipping.

Sealing of adhesive systems in ferric sulfate-contaminated dentinal margins in class V composite resin restorations

Directory of Open Access Journals (Sweden)

Niloofar Shadman

2016-03-01

Full Text Available Background. Hemostatic agents are applied to prepare an isolated bleeding-free condition during dental treatments and can influence adhesive restorations. This study evaluated the effect of a hemostatic agent (ViscoStat on microleakage of contaminated dentinal margin of class V composite resin restorations with three adhesives. Methods. Sixty freshly extracted human molars were selected and class V cavities (3×3×1.5 mm were prepared on buccal and lingual surfaces. Gingival margins of the cavities were placed below the cementoenamel junction. The teeth were divided into six groups randomly. The adhesives were Excite, AdheSE and AdheSE One. In three groups, the gingival walls of the cavities were contaminated with ViscoStat and then rinsed. The cavities were restored with composite resin and light-cured. After storage in distilled water (37°C for 24 hours and polishing, the samples were thermocycled and sealed with nail varnish. Then they were stored in 1% basic fuchsin for 24 hours, rinsed and mounted in self-cured acryl resin, followed by sectioning buccolingually. Dye penetration was observed under a stereomicroscope and scored. Data were statistically analyzed with Kruskal-Wallis and Mann-Whitney U tests. P 0.05. In the contaminated groups, Excite had significantly less microleakage than the others (P = 0.003. AdheSE and AdheSE One did not exhibit significant difference in microleakage (P > 0.05. Conclusion. ViscoStat hemostatic agent increased dentinal microleakage in AdheSE and AdheSE One adhesives with no effect on Excite.

Bond strength and microleakage of current dentin adhesives.

Science.gov (United States)

Fortin, D; Swift, E J; Denehy, G E; Reinhardt, J W

1994-07-01

The purpose of this in vitro study was to evaluate shear bond strengths and microleakage of seven current-generation dentin adhesive systems. Standard box-type Class V cavity preparations were made at the cemento-enamel junction on the buccal surfaces of eighty extracted human molars. These preparations were restored using a microfill composite following application of either All-Bond 2 (Bisco), Clearfil Liner Bond (Kuraray), Gluma 2000 (Miles), Imperva Bond (Shofu), OptiBond (Kerr), Prisma Universal Bond 3 (Caulk), Scotchbond Multi-Purpose (3M), or Scotchbond Dual-Cure (3M) (control). Lingual dentin of these same teeth was exposed and polished to 600-grit. Adhesives were applied and composite was bonded to the dentin using a gelatin capsule technique. Specimens were thermocycled 500 times. Shear bond strengths were determined using a universal testing machine, and microleakage was evaluated using a standard silver nitrate staining technique. Clearfill Liner Bond and OptiBond, adhesive systems that include low-viscosity, low-modulus intermediate resins, had the highest shear bond strengths (13.3 +/- 2.3 MPa and 12.9 +/- 1.5 MPa, respectively). Along with Prisma Universal Bond 3, they also had the least microleakage at dentin margins of Class V restorations. No statistically significant correlation between shear bond strength and microleakage was observed in this study. Adhesive systems that include a low-viscosity intermediate resin produced the high bond strengths and low microleakage. Similarly, two materials with bond strengths in the intermediate range had significantly increased microleakage, and one material with a bond strength in the low end of the spectrum exhibited microleakage that was statistically greater. Thus, despite the lack of statistical correlation, there were observable trends.

Developing and Evaluating Composites Based on Plantation Eucalyptus Rotary-cut Veneer and High-density Polyethylene Film as Novel Building Materials

Directory of Open Access Journals (Sweden)

Wei Song

2016-02-01

Full Text Available To achieve value-added utilizations of plantation timbers, eucalyptus veneer/high-density polyethylene film composites were prepared, with process-factors (PF (hot-pressing temperature, HT; hot-pressing duration, HD; hot-pressing pressure, HP; HDPE-film content, HC and composite-properties (CP (water-resistant bonding-strength, BS; modulus of rupture, MOR; modulus of elasticity, MOE investigated. According to thermal analyses, 140 to 180 °C was appropriate for HT. Based on statistical analyses, HD was easier to affect CP, while MOE was easier to be affected by PF. Quantitative relationships between PF and CP were determined by the neural-network (ANN modeling. In ANN simulation surveys, CP displayed Gaussian distributions (R2 > 0.9 when PF changed in current ranges, with positive correlations between BS and MOR (R2 ≈ 0.5. Combining ANN and the genetic-algorithm, optimal processes (HT, 160 °C; HD, 50 s/mm; HP, 1.3 MPa; HC, 6 layers were found, and optimal results (BS, 1.30 MPa; MOR, 86.94 MPa; MOE, 8.33 GPa were comparable to various reported poplar-plywoods. Microscopic images demonstrated that composite interfaces were formed by the mechanical interlocking. The optimal BS attained Chinese standards for water-resistant plywoods, so proposed composites can serve as water-resistant and formaldehyde-free building materials for furniture and interior design.

Deformation behavior of human enamel and dentin-enamel junction under compression.

Science.gov (United States)

Zaytsev, Dmitry; Panfilov, Peter

2014-01-01

Deformation behavior under uniaxial compression of human enamel and dentin-enamel junction (DEJ) is considered in comparison with human dentin. This deformation scheme allows estimating the total response from all levels of the hierarchical composite material in contrast with the indentation, which are limited by the mesoscopic and microscopic scales. It was shown for the first time that dental enamel is the strength (up to 1850MPa) hard tissue, which is able to consider some elastic (up to 8%) and plastic (up to 5%) deformation under compression. In so doing, it is almost undeformable substance under the creep condition. Mechanical properties of human enamel depend on the geometry of sample. Human dentin exhibits the similar deformation behavior under compression, but the values of its elasticity (up to 40%) and plasticity (up to 18%) are much more, while its strength (up to 800MPa) is less in two times. Despite the difference in mechanical properties, human enamel is able to suppress the cracking alike dentin. Deformation behavior under the compression of the samples contained DEJ as the same to dentin. This feature allows a tooth to be elastic-plastic (as dentin) and wear resistible (as enamel), simultaneously. © 2013 Elsevier B.V. All rights reserved.

Micromorphological characterization of adhesive interface of sound dentin and total-etch and self-etch adhesives.

Science.gov (United States)

Drobac, Milan; Stojanac, Igor; Ramić, Bojana; Premović, Milica; Petrović, Ljubomir

2015-01-01

The ultimate goal in restorative dentistry has always been to achieve strong and permanent bond between the dental tissues and filling materials. It is not easy to achieve this task because the bonding process is different for enamel and dentin-dentin is more humid and more organic than enamel. It is moisture and organic nature of dentin that make this hard tissue very complex to achieve adhesive bond. One of the first and most widely used tools for examining the adhesive bond between hard dental tissues and composite restorative materials is scanning electron microscopy. The aim of this study was scanning electron microscopy analyzes the interfacial micro morphology of total-etch and self-etch adhesives. Micro morphological characteristics of interface between total-etch adhesive (Prime & Bond NT) in combination with the corresponding composite (Ceram X Mono) were compared with those of self-etching adhesive (AdheSE One) in, combination with the corresponding composite (Tetric EvoCeram). The specimens were observed under 1000 x magnification of scanning electron microscopy (JEOL, JSM-6460 Low Vacuum). Measurement of the thickness of the hybrid layer of the examined com posite systems was performed with the software of the device used (NIH Image Analyser). Micromorphological analysis of interface showed that the hybrid layer in sound dentin was well formed, its average thickness being 2.68 microm, with a large number of resin tags and a large amount of lateral branches for specimens with a composite system Prime & Bond NT-Ceram X Mono. However, the specimens' with composite systems Adhese One-Tetric EvoCeram did not show the presence of hybrid layer and the resin tags were poorly represented. The results of this study suggest that total-etch adhesives bond better with sound dentin than self-etch adhesive.

Three-Point Bending Tests of Zirconia Core/Veneer Ceramics for Dental Restorations

Directory of Open Access Journals (Sweden)

Massimo Marrelli

2013-01-01

Full Text Available Introduction. The mechanical strength and the surface hardness of commercially available yttrium-doped zirconia were investigated. Furthermore, a comparative study of eight different ceramic veneers, to be used for the production of two-layered all-ceramic restorative systems, was carried out. Materials and Methods. Four types of zirconia specimens were analyzed, according to a standard ISO procedure (ISO 6872. Besides, two-layered zirconia-veneer specimens were prepared for three-point bending tests. Results. A strong effect of the surface roughness on the mechanical strength of zirconia specimens was observed. Finally, a comparative study of eight commercially available veneering ceramics shows different modes of failure between the selected veneers. Conclusion. The results indicate that close attention should be paid to the preparation of zirconia-based crowns and bridges by CAD/CAM process, because surface roughness has an important effect on the mechanical strength of the material. Finally, the results of the mechanical tests on two-layered specimens represent an important support to the choice of the veneering ceramic.

Fabrication of Hydrophobic Surface on Wood Veneer via Electroless Nickel Plating Combined with Chemical Corrosion

Directory of Open Access Journals (Sweden)

Zhaojun Tang

2015-12-01

Full Text Available Birch veneers were coated with Ni-P films by a combined process of KBH4 activation and electroless plating. The plated veneers were further chemically corroded to obtain hydrophobic surfaces on wood. The effect of chemical corrosion on the contact angle of the veneers was investigated. The hydrophobic veneers were characterized by X-ray photo electron spectroscopy (XPS, scanning electron microscopy (SEM, and X-ray diffraction (XRD. The surface contact angle of birch veneer before and after it was plated with Ni-P alloy coating was 41º and 121º, respectively. The contact angle reached 136.7º when the nickel-coated veneers were corroded in CuSO4 aqueous solution for 30 min. XPS analysis showed that Cu0 cluster doped with little CuO formed on the corroded surface of Ni-P alloy film after chemical corrosion. SEM and XRD showed that rough copper clusters formed on the surface of the wood veneer and revealed the reason of the surface hydrophobicity. This study provides a new pathway for fabricating hydrophobic wood.

Microtensile bond strength of three simplified adhesive systems to caries-affected dentin.

Science.gov (United States)

Scholtanus, J D; Purwanta, Kenny; Dogan, Nilgun; Kleverlaan, Cees J; Feilzer, Albert J

2010-08-01

The purpose of the study was to determine the microtensile bond strength of three different simplified adhesive systems to caries-affected dentin. Fifteen extracted human molars with primary carious lesions were ground flat until dentin was exposed. Soft caries-infected dentin was excavated with the help of caries detector dye. On the remaining hard dentin, a standardized smear layer was created by polishing with 600-grit SiC paper. Teeth were divided into three groups and treated with one of the three tested adhesives: Adper Scotchbond 1 XT (3M ESPE), a 2-step etch-andrinse adhesive, Clearfil S3 Bond (Kuraray), a 1-step self-etching or all-in-one adhesive, and Clearfil SE Bond (Kuraray), a 2-step self-etching adhesive. Five-mm-thick composite buildups (Z-250, 3M ESPE) were built and light cured. After water storage for 24 h at 37ºC, the bonded specimens were sectioned into bars (1.0 x 1.0 mm; n = 20 to 30). Microtensile bond strength of normal dentin specimens and caries-affected dentin specimens was measured in a universal testing machine (crosshead speed = 1 mm/min). Data were analyzed using two-way ANOVA and Tukey's post-hoc test (p adhesives were found. Adper Scotchbond 1 XT and Clearfil S3 Bond showed significantly lower bond strength values to caries-affected dentin. For Clearfil SE Bond, bond strength values to normal and caries-affected dentin were not significantly different. All the tested simplified adhesives showed similar bond strength values to normal dentin. For the tested 2-step etch-and-rinse adhesive and the all-in-one adhesive, the bond strength values to caries-affected dentin were lower than to normal dentin.

Cervical and incisal marginal discrepancy in ceramic laminate veneering materials: A SEM analysis

Directory of Open Access Journals (Sweden)

Hemalatha Ranganathan

2017-01-01

Full Text Available Context: Marginal discrepancy influenced by the choice of processing material used for the ceramic laminate veneers needs to be explored further for better clinical application. Aims: This study aimed to evaluate the amount of cervical and incisal marginal discrepancy associated with different ceramic laminate veneering materials. Settings and Design: This was an experimental, single-blinded, in vitro trial. Subjects and Methods: Ten central incisors were prepared for laminate veneers with 2 mm uniform reduction and heavy chamfer finish line. Ceramic laminate veneers fabricated over the prepared teeth using four different processing materials were categorized into four groups as Group I - aluminous porcelain veneers, Group II - lithium disilicate ceramic veneers, Group III - lithium disilicate-leucite-based veneers, Group IV - zirconia-based ceramic veneers. The cervical and incisal marginal discrepancy was measured using a scanning electron microscope. Statistical Analysis Used: ANOVA and post hoc Tukey honest significant difference (HSD tests were used for statistical analysis. Results: The cervical and incisal marginal discrepancy for four groups was Group I - 114.6 ± 4.3 μm, 132.5 ± 6.5 μm, Group II - 86.1 ± 6.3 μm, 105.4 ± 5.3 μm, Group III - 71.4 ± 4.4 μm, 91.3 ± 4.7 μm, and Group IV - 123.1 ± 4.1 μm, 142.0 ± 5.4 μm. ANOVA and post hoc Tukey HSD tests observed a statistically significant difference between the four test specimens with regard to cervical marginal discrepancy. The cervical and incisal marginal discrepancy scored F = 243.408, P < 0.001 and F = 180.844, P < 0.001, respectively. Conclusion: This study concluded veneers fabricated using leucite reinforced lithium disilicate exhibited the least marginal discrepancy followed by lithium disilicate ceramic, aluminous porcelain, and zirconia-based ceramics. The marginal discrepancy was more in the incisal region than in the cervical region in all the groups.

Eroded dentin does not jeopardize the bond strength of adhesive restorative materials

Directory of Open Access Journals (Sweden)

Janaina Barros Cruz

2012-08-01

Full Text Available This in vitro study evaluated the bond strength of adhesive restorative materials to sound and eroded dentin. Thirty-six bovine incisors were embedded in acrylic resin and ground to obtain flat buccal dentin surfaces. Specimens were randomly allocated in 2 groups: sound dentin (immersion in artificial saliva and eroded dentin (pH cycling model - 3× / cola drink for 7 days. Specimens were then reassigned according to restorative material: glass ionomer cement (KetacTM Molar Easy Mix, resin-modified glass ionomer cement (VitremerTM or adhesive system with resin composite (Adper Single Bond 2 + Filtek Z250. Polyethylene tubes with an internal diameter of 0.76 mm were placed over the dentin and filled with the material. The microshear bond test was performed after 24 h of water storage at 37ºC. The failure mode was evaluated using a stereomicroscope (400×. Bond strength data were analyzed with two-way ANOVA and Tukey's post hoc tests (α = 0.05. Eroded dentin showed bond strength values similar to those for sound dentin for all materials. The adhesive system showed the highest bond strength values, regardless of the substrate (p < 0.0001. For all groups, the adhesive/mixed failure prevailed. In conclusion, adhesive materials may be used in eroded dentin without jeopardizing the bonding quality. It is preferable to use an etch-and-rinse adhesive system because it shows the highest bond strength values compared with the glass ionomer cements tested.

In situ polymerization of polyaniline in wood veneers.

Science.gov (United States)

Trey, Stacy; Jafarzadeh, Shadi; Johansson, Mats

2012-03-01

The present study describes the possibility to polymerize aniline within wood veneers to obtain a semi-conducting material with solid wood acting as the base template. It was determined that it is possible to synthesize the intrinsically conductive polymer (ICP) polyaniline in situ within the wood structure of Southern yellow pine veneers, combining the strength of the natural wood structure with the conductivity of the impregnated polymer. It was found that polyaniline is uniformly dispersed within the wood structure by light microscopy and FT-IR imaging. A weight percent gain in the range of 3-12 wt % was obtained with a preferential formation in the wood structure and cell wall, rather than in the lumen. The modified wood was found to be less hydrophilic with the addition of phosphate doped polyaniline as observed by equilibrium water swelling studies. While wood itself is insulating, the modified veneers had conductivities of 1 × 10(-4) to 1 × 10(-9) S cm(-1), demonstrating the ability to tune the conductivity and allowing for materials with a wide range of applications, from anti-static to charge-dispersing materials. Furthermore, the modified veneers had lower total and peak heat releases, as determined by cone calorimetry, because of the char properties of the ICP. This is of interest if these materials are to be used in building and furniture applications where flame retardance is of importance. © 2012 American Chemical Society

Sodium Hypochlorite Irrigation and Its Effect on Bond Strength to Dentin

Directory of Open Access Journals (Sweden)

Tariq S. Abuhaimed

2017-01-01

Full Text Available Effective shaping and cleaning of root canals are essential for the success of endodontic treatment. Due to the complex anatomy of root canal spaces, the use of various instrumentation techniques alone is not effective in producing bacteria-free root canal spaces. Irrigation, disinfectants, rinses, and intervisit medications are used in conjunction with the mechanical instrumentation to ensure the success of endodontic treatment. Sodium hypochlorite (NaOCl, a halogenated compound, is routinely used to irrigate the root canal during endodontic treatments. NaOCl has been known for its antibacterial action, proteolytic and dissolution capacity, and debridement properties. NaOCl, however, can alter the composition of dentin and hence its interaction with the adhesive resins used to bond the restorative materials to treated dentin. This review therefore covers in depth the action of NaOCl on dentin-adhesive resin bond strength including both enhancement and reduction, then mechanisms proposed for such action, and finally how the adverse action of NaOCl on dentin can be reversed.

Sodium Hypochlorite Irrigation and Its Effect on Bond Strength to Dentin.

Science.gov (United States)

Abuhaimed, Tariq S; Abou Neel, Ensanya A

2017-01-01

Effective shaping and cleaning of root canals are essential for the success of endodontic treatment. Due to the complex anatomy of root canal spaces, the use of various instrumentation techniques alone is not effective in producing bacteria-free root canal spaces. Irrigation, disinfectants, rinses, and intervisit medications are used in conjunction with the mechanical instrumentation to ensure the success of endodontic treatment. Sodium hypochlorite (NaOCl), a halogenated compound, is routinely used to irrigate the root canal during endodontic treatments. NaOCl has been known for its antibacterial action, proteolytic and dissolution capacity, and debridement properties. NaOCl, however, can alter the composition of dentin and hence its interaction with the adhesive resins used to bond the restorative materials to treated dentin. This review therefore covers in depth the action of NaOCl on dentin-adhesive resin bond strength including both enhancement and reduction, then mechanisms proposed for such action, and finally how the adverse action of NaOCl on dentin can be reversed.

In Vitro Evaluation of Dentin Hydraulic Conductance After 980 nm Diode Laser Irradiation.

Science.gov (United States)

Rizzante, Fabio A P; Maenosono, Rafael M; Duarte, Marco A H; Furuse, Adilson Y; Palma-Dibb, Regina G; Ishikiriama, Sérgio K

2016-03-01

Dentin hypersensitivity treatments are based on the physical obliteration of the dentinal tubules to reduce hydraulic conductance. The aim of the present study is to evaluate the hydraulic conductance of bovine root dentin after irradiation with a 980-nm diode laser, with or without associated fluoride varnish. Sixty bovine root dentin specimens were divided into six groups (n = 10 in each group): G1, G3, and G5 (0.5 W, 0.7 W, and 1 W diode laser, respectively); G2, G4, and G6 (fluoride varnish application + 0.5 W, 0.7 W, and 1 W diode laser, respectively). The dentin hydraulic conductance was evaluated at four time periods with a fluxmeter: 1) with smear layer, 2) after 37% phosphoric acid etching, 3) after the treatments, and 4) after 6% citric acid challenge. After the dentinal fluid flow measurements, specimens were also evaluated for mineral composition using energy dispersive X-ray spectroscopy (EDS). Analysis demonstrated a better result with increased irradiation power (P diode laser irradiation was associated with the application of fluoride varnish (P laser irradiation, the 1 W group was superior when compared with the 0.5 W and 0.7 W irradiated groups immediately after treatment (P laser treatments. Laser irradiation of exposed dentin promoted significant reduction in the dentin hydraulic conductance, mainly with higher energy densities and association with fluoride varnish.

Shear bond strength of a new one-bottle dentin adhesive.

Science.gov (United States)

Swift, E J; Bayne, S C

1997-08-01

To test the shear bond strength of a new adhesive, 3M Single Bond, to dentin surfaces containing different degrees of moisture. Two commercially available one-bottle adhesives (Prime & Bond, One-Step) and a conventional three-step system (Scotchbond Multi-Purpose Plus) were included for comparison. 120 bovine teeth were embedded in acrylic and the labial surfaces were polished to 600 grit to create standardized dentin surfaces for testing. Resin composite was bonded to dentin using a gelatin capsule technique. Four adhesive systems were evaluated with three different degrees of surface moisture (moist, wet, and overwet). Shear bond strengths of adhesives to dentin were determined using a universal testing machine and analyzed by ANOVA and Tukey's post hoc tests. Single Bond had mean shear bond strengths of 19.2, 23.2 and 20.3 MPa to moist, wet, and overwet dentin, respectively. Bond strengths of the three-component system Scotchbond Multi-Purpose Plus ranged from 23.1 to 25.3 MPa, but were not significantly higher than the values for Single Bond. Prime & Bond had bond strengths similar to those of Single Bond, but One-Step had significantly lower bond strengths (P < 0.05) in the wet and overwet conditions.

Influence of dental restorations and mastication loadings on dentine fatigue behaviour: Image-based modelling approach.

Science.gov (United States)

Vukicevic, Arso M; Zelic, Ksenija; Jovicic, Gordana; Djuric, Marija; Filipovic, Nenad

2015-05-01

The aim of this study was to use Finite Element Analysis (FEA) to estimate the influence of various mastication loads and different tooth treatments (composite restoration and endodontic treatment) on dentine fatigue. The analysis of fatigue behaviour of human dentine in intact and composite restored teeth with root-canal-treatment using FEA and fatigue theory was performed. Dentine fatigue behaviour was analysed in three virtual models: intact, composite-restored and endodontically-treated tooth. Volumetric change during the polymerization of composite was modelled by thermal expansion in a heat transfer analysis. Low and high shrinkage stresses were obtained by varying the linear shrinkage of composite. Mastication forces were applied occlusally with the load of 100, 150 and 200N. Assuming one million cycles, Fatigue Failure Index (FFI) was determined using Goodman's criterion while residual fatigue lifetime assessment was performed using Paris-power law. The analysis of the Goodman diagram gave both maximal allowed crack size and maximal number of cycles for the given stress ratio. The size of cracks was measured on virtual models. For the given conditions, fatigue-failure is not likely to happen neither in the intact tooth nor in treated teeth with low shrinkage stress. In the cases of high shrinkage stress, crack length was much larger than the maximal allowed crack and failure occurred with 150 and 200N loads. The maximal allowed crack size was slightly lower in the tooth with root canal treatment which induced somewhat higher FFI than in the case of tooth with only composite restoration. Main factors that lead to dentine fatigue are levels of occlusal load and polymerization stress. However, root canal treatment has small influence on dentine fatigue. The methodology proposed in this study provides a new insight into the fatigue behaviour of teeth after dental treatments. Furthermore, it estimates maximal allowed crack size and maximal number of cycles for a

The acid-base resistant zone in three dentin bonding systems.

Science.gov (United States)

Inoue, Go; Nikaido, Toru; Foxton, Richard M; Tagami, Junji

2009-11-01

An acid-base resistant zone has been found to exist after acid-base challenge adjacent to the hybrid layer using SEM. The aim of this study was to examine the acid-base resistant zone using three different bonding systems. Dentin disks were applied with three different bonding systems, and then a resin composite was light-cured to make dentin disk sandwiches. After acid-base challenge, the polished surfaces were observed using SEM. For both one- and two-step self-etching primer systems, an acid-base resistant zone was clearly observed adjacent to the hybrid layer - but with differing appearances. For the wet bonding system, the presence of an acid-base resistant zone was unclear. This was because the self-etching primer systems etched the dentin surface mildly, such that the remaining mineral phase of dentin and the bonding agent yielded clear acid-base resistant zones. In conclusion, the acid-base resistant zone was clearly observed when self-etching primer systems were used, but not so for the wet bonding system.

Relationship between stress wave velocities of green and dry veneer

Science.gov (United States)

Brian K. Brashaw; Xiping Wang; Robert J. Ross; Roy F. Pellerin

2004-01-01

This paper evaluates the relationship between the stress wave velocities of green and dry southern pine and Douglas-fir veneers. A commercial stress wave timer and a laboratory signal analysis system were used to measure the transit time required for an induced stress wave to travel the longitudinal length of each veneer. Stress wave transit times were measured in the...

Porcelain veneer post-bonding crack repair by resin infiltration.

Science.gov (United States)

Gresnigt, Marco; Magne, Michel; Magne, Pascal

Ceramic laminate veneer restorations are indicated in several clinical situations. Indirect restorations are usually chosen if the less-invasive options - bleaching, resin infiltration, or composite resin restorations - are not possible, or when it is too difficult to achieve an esthetically pleasing result in the long term. Bonded indirect partial restorations are highly dependent on their adhesive interface, as these thin restorations have a relatively low cohesive strength. Therefore, preservation of sound enamel, conditioning of the restorations and of the substrate, and luting procedures are of paramount importance for a successful outcome. Even when utmost care is taken during every step of the procedure, failures such as fractures, chipping, or marginal discoloration and defects sometimes occur. Only very few of these cases of failure are presented or are a subject of interest. In this case presentation, a fracture repair is performed using an infiltration technique with a resin composite material.

Influence of matrix metalloproteinase synthetic inhibitors on dentin microtensile bond strength of resin cements.

Science.gov (United States)

Stape, T H S; Menezes, M S; Barreto, B C F; Aguiar, F H B; Martins, L R; Quagliatto, P S

2012-01-01

This study evaluated the effect of dentin pretreatment with 2% chlorhexidine (CHX) or 24% ethylenediamine tetra-acetic acid gel (EDTA) on the dentin microtensile bond strength (μTBS) of resin cements. Composite blocks were luted to superficial noncarious human dentin (n=10) using two resin cements (RelyX ARC [ARC] and RelyX U100 [U100]) and three dentin pretreatments (without pretreatment-control, CHX, and EDTA). CHX was applied for 60 seconds on the acid-etched dentin in the ARC/CHX group, and for the same time on smear layer-covered dentin in the U100/CHX group. EDTA was applied for 45 seconds on smear-covered dentin in the U100/EDTA group, and it replaced phosphoric acid conditioning in the ARC/EDTA group for 60 seconds. After storage in water for 24 hours, specimens were prepared for microtensile bond strength testing. The results were submitted to two-way analysis of variance (ANOVA) followed by Tukey test. ARC produced significantly higher μTBS (pEDTA was used. For ARC, no pretreatment and CHX produced higher μTBS than EDTA. For U100, EDTA produced higher μTBS; no statistical difference occurred between CHX pretreatment and when no pretreatment was performed. While CHX did not affect immediate dentin bond strength of both cements, EDTA improved bond strength of U100, but it reduced dentin bond strength of ARC.

Evaluating the shear bond strength of enamel and dentin with or without etching: A comparative study between dimethacrylate-based and silorane-based adhesives

Science.gov (United States)

Hajizadeh, Hila; Nasseh, Atefeh; Rahmanpour, Naim

2015-01-01

Background Silorane-based composites and their specific self-etch adhesive were introduced to conquest the polymerization shrinkage of methacrylate-based composites. It has been shown that additional etching of enamel and dentin can improve the bond strength of self-etch methacrylate-based adhesives but this claim is not apparent about silorane-based adhesives. Our objective was to compare the shear bond strength (SBS) of enamel and dentin between silorane-based adhesive resin and a methacrylate-based resin with or without additional etching. Material and Methods 40 sound human premolars were prepared and divided into two groups: 1- Filtek P60 composite and Clearfil SE Bond adhesive; 2- Filtek P90 composite and Silorane adhesive. Each group divided into two subgroups: with or without additional etching. For additional etching, 37% acid phosphoric was applied before bonding procedure. A cylinder of the composite was bonded to the surface. After 24 hours storage and 500 thermo cycling between 5-55°C, shear bond strength was assessed with the cross head speed of 0.5 mm/min. Then, bonded surfaces were observed under stereomicroscope to determine the failure mode. Data were analyzed with two-way ANOVA and Fischer exact test. Results Shear bond strength of Filtek P60 composite was significantly higher than Filtek P90 composite both in enamel and dentin surfaces (Penamel or dentin for each of the composites (P>0.05). There was no interaction between composite type and additional etching (P>0.05). Failure pattern was mainly adhesive and no significant correlation was found between failure and composite type or additional etching (P>0.05). Conclusions Shear bond strength of methacrylate-based composite was significantly higher than silorane-based composite both in enamel and dentin surfaces and additional etching had no significant effect on shear bond strength in enamel or dentin for each of the composites. The mode of failure had no meaningful relation to the type of

Influence of heat treatment and veneering on the storage modulus and surface of zirconia ceramic

NARCIS (Netherlands)

Siavikis, G.; Behr, M.; van der Zel, J.M.; Feilzer, A.J.; Rosentritt, M.

2011-01-01

Objectives: Glass-ceramic veneered zirconia is used for the application as fixed partial dentures. The aim of this investigation was to evaluate whether the heat treatment during veneering, the application of glass-ceramic for veneering or long term storage has an influence on the storage modulus of

Effect of saliva and blood contamination after etching upon the shear bond strength between composite resin and enamel

Science.gov (United States)

Armadi, A. S.; Usman, M.; Suprastiwi, E.

2017-08-01

The aim of this study was to find out the surface roughness of composite resin veneer after brushing. In this study, 24 specimens of composite resin veneer are divided into three subgroups: brushed without toothpaste, brushed with non-herbal toothpaste, and brushed with herbal toothpaste. Brushing was performed for one set of 5,000 strokes and continued for a second set of 5,000 strokes. Roughness of composite resin veneer was determined using a Surface Roughness Tester. The results were statistically analyzed using Kruskal-Wallis nonparametric test and Post Hoc Mann-Whitney. The results indicate that the highest difference among the Ra values occurred within the subgroup that was brushed with the herbal toothpaste. In conclusion, the herbal toothpaste produced a rougher surface on composite resin veneer compared to non-herbal toothpaste.

In vivo effect of a self-etching primer on dentin.

Science.gov (United States)

Milia, E; Lallai, M R; García-Godoy, F

1999-08-01

To determine the ultrastructural aspects of the dentin collagen area in the cavity preparation floor produced in vivo after phosphoric acid acid-etching or after using Clearfil Liner Bond 2 self-etching primer (LB2 Primer). Twenty-four non-carious third molars scheduled for extraction from young adult patients (16-30 years old) were used. Conventional Class I cavities (+/- 2 mm deep) were prepared on the occlusal surfaces of all teeth using a cylindrical diamond bur on a high-speed handpiece with copious water spray. To avoid dehydration of the dentin, the smear layer-covered dentin was briefly air-dried for 2 seconds. Cavities were assigned at random to the following groups: Group A: Dentin etched for 15 seconds with 34% phosphoric acid, rinsed for 20 seconds and then briefly air-dried for 2 seconds with oil-free compressed air leaving the surfaces slightly moist. Group B: LB2 Primer was applied to the cavity surfaces for 30 seconds and then briefly air-dried to remove the solvent. Group C: The untreated dentin smear layer was used as a control. In all three groups, the cavities were filled incrementally with a resin-based composite (APX), light curing every increment for 40 seconds. After 30 minutes, the teeth were extracted atraumatically and the samples immediately prepared for evaluation with the transmission electron microscope. The use of a self-etching primer did not produce significant morphological changes in the moist dentin substrate. Adverse morphological conditions where observed when there was an excess water on the dentin surface. Phosphoric acid altered the collagen more severely than the self-etching primer.

Fabrication of Silicon Nitride Dental Core Ceramics with Borosilicate Veneering material

International Nuclear Information System (INIS)

Wananuruksawong, R; Jinawath, S; Wasanapiarnpong, T; Padipatvuthikul, P

2011-01-01

Silicon nitride (Si 3 N 4 ) ceramic is a great candidate for clinical applications due to its high fracture toughness, strength, hardness and bio-inertness. This study has focused on the Si 3 N 4 ceramic as a dental core material. The white Si 3 N 4 was prepared by pressureless sintering at relative low sintering temperature of 1650 deg. C in nitrogen atmosphere. The coefficient of thermal expansion (CTE) of Si 3 N 4 ceramic is lower than that of Zirconia and Alumina ceramic which are popular in this field. The borosilicate glass veneering was employed due to its compatibility in thermal expansion. The sintered Si 3 N 4 specimens represented the synthetic dental core were paintbrush coated by a veneer paste composed of borosilicate glass powder ( 2 O 3 - partial stabilized zirconia) and 30 wt% of polyvinyl alcohol (5 wt% solution). After coating the veneer on the Si 3 N 4 specimens, the firing was performed in electric tube furnace between 1000-1200 deg. C. The veneered specimens fired at 1100 deg. C for 15 mins show good bonding, smooth and glossy without defect and crazing. The veneer has thermal expansion coefficient as 3.98x10 -6 deg. C -1 , rather white and semi opaque, due to zirconia addition, the Vickers hardness as 4.0 GPa which is closely to the human teeth.

Shear bond strength of bulk-fill and nano-restorative materials to dentin.

Science.gov (United States)

Colak, Hakan; Ercan, Ertugrul; Hamidi, Mehmet Mustafa

2016-01-01

Bulk-fill composite materials are being developed for preparation depths of up to 4 mm in an effort to simplify and improve the placement of direct composite posterior restorations. The aim of our study was to compare shear-bond strength of bulk-fill and conventional posterior composite resins. In this study, 60 caries free extracted human molars were used and sectioned parallel to occlusal surface to expose midcoronal dentin. The specimens were randomly divided into four groups. Total-etch dentine bonding system (Adper Scotchbond 1XT, 3M ESPE) was applied to dentin surface in all the groups to reduce variability in results. Then, dentine surfaces covered by following materials. Group I: SonicFill Bulk-Fill, Group II: Tetric EvoCeram (TBF), Group III: Herculite XRV Ultra, and Group IV: TBF Bulk-Fill, 2 mm × 3 mm cylindrical restorations were prepared by using application apparatus. Shear bond testing was measured by using a universal testing machine. Kruskal-Wallis and Mann-Whitney U-tests were performed to evaluate the data. The highest value was observed in Group III (14.42 ± 4.34) and the lowest value was observed in Group IV (11.16 ± 2.76) and there is a statistically significant difference between these groups (P = 0.046). However, there is no statistically significant difference between the values of other groups. In this study, Group III was showed higher strength values. There is a need for future studies about long-term bond strength and clinical success of these adhesive and bulk-fill systems.

Interfacial characterization of ceramic core materials with veneering porcelain for all-ceramic bi-layered restorative systems.

Science.gov (United States)

Tagmatarchis, Alexander; Tripodakis, Aris-Petros; Filippatos, Gerasimos; Zinelis, Spiros; Eliades, George

2014-01-01

The aim of the study was to characterize the elemental distribution at the interface between all-ceramic core and veneering porcelain materials. Three groups of all-ceramic cores were selected: A) Glass-ceramics (Cergo, IPS Empress, IPS Empress 2, e-max Press, Finesse); B) Glass-infiltrated ceramics (Celay Alumina, Celay Zirconia) and C) Densely sintered ceramics (Cercon, Procera Alumina, ZirCAD, Noritake Zirconia). The cores were combined with compatible veneering porcelains and three flat square test specimens were produced for each system. The core-veneer interfaces were examined by scanning electron microscopy and energy dispersive x-ray microanalysis. The glass-ceramic systems showed interfacial zones reach in Si and O, with the presence of K, Ca, Al in core and Ca, Ce, Na, Mg or Al in veneer material, depending on the system tested. IPS Empress and IPS Empress 2 demonstrated distinct transitional phases at the core-veneer interface. In the glassinfiltrated systems, intermixing of core (Ce, La) with veneer (Na, Si) elements occurred, whereas an abrupt drop of the core-veneer elemental concentration was documented at the interfaces of all densely sintered ceramics. The results of the study provided no evidence of elemental interdiffusion at the core-veneer interfaces in densely sintered ceramics, which implies lack of primary chemical bonding. For the glass-containing systems (glassceramics and glass-infiltrated ceramics) interdiffusion of the glass-phase seems to play a critical role in establishing a primary bonding condition between ceramic core and veneering porcelain.

Improved reactive nanoparticles to treat dentin hypersensitivity.

Science.gov (United States)

Toledano-Osorio, Manuel; Osorio, Estrella; Aguilera, Fátima S; Luis Medina-Castillo, Antonio; Toledano, Manuel; Osorio, Raquel

2018-05-01

The aim of this study was to evaluate the effectiveness of different nanoparticles-based solutions for dentin permeability reduction and to determine the viscoelastic performance of cervical dentin after their application. Four experimental nanoparticle solutions based on zinc, calcium or doxycycline-loaded polymeric nanoparticles (NPs) were applied on citric acid etched dentin, to facilitate the occlusion and the reduction of the fluid flow at the dentinal tubules. After 24 h and 7 d of storage, cervical dentin was evaluated for fluid filtration. Field emission scanning electron microscopy, energy dispersive analysis, AFM and Nano-DMA analysis were also performed. Complex, storage, loss modulus and tan delta (δ) were assessed. Doxycycline-loaded NPs impaired tubule occlusion and fluid flow reduction trough dentin. Tubules were 100% occluded in dentin treated with calcium-loaded NPs or zinc-loaded NPs, analyzed at 7 d. Dentin treated with both zinc-NPs and calcium-NPs attained the highest reduction of dentinal fluid flow. Moreover, when treating dentin with zinc-NPs, complex modulus values attained at intertubular and peritubular dentin were higher than those obtained after applying calcium-NPs. Zinc-NPs are then supposed to fasten active dentin remodeling, with increased maturity and high mechanical properties. Zinc-based nanoparticles are then proposed for effective dentin remineralization and tubular occlusion. Further research to finally prove for clinical benefits in patients with dentin hypersensitivity using Zn-doped nanoparticles is encouraged. Erosion from acids provokes dentin hypersensitivity (DH) which presents with intense pain of short duration. Open dentinal tubules and demineralization favor DH. Nanogels based on Ca-nanoparticles and Zn-nanoparticles produced an efficient reduction of fluid flow. Dentinal tubules were filled by precipitation of induced calcium-phosphate deposits. When treating dentin with Zn-nanoparticles, complex modulus

Durability of feldspathic veneering ceramic on glass-infiltrated alumina ceramics after long-term thermocycling.

Science.gov (United States)

Mesquita, A M M; Ozcan, M; Souza, R O A; Kojima, A N; Nishioka, R S; Kimpara, E T; Bottino, M A

2010-01-01

This study compared the bond strength durability of a feldspathic veneering ceramic to glass-infiltrated reinforced ceramics in dry and aged conditions. Disc shaped (thickness: 4 mm, diameter: 4 mm) of glass-infiltrated alumina (In-Ceram Alumina) and glass-infiltrated alumina reinforced by zirconia (In-Ceram Zirconia) core ceramic specimens (N=48, N=12 per groups) were constructed according to the manufacturers' recommendations. Veneering ceramic (VITA VM7) was fired onto the core ceramics using a mold. The core-veneering ceramic assemblies were randomly divided into two conditions and tested either immediately after specimen preparation (Dry) or following 30000 thermocycling (5-55 ºC±1; dwell time: 30 seconds). Shear bond strength test was performed in a universal testing machine (cross-head speed: 1 mm/min). Failure modes were analyzed using optical microscope (x20). The bond strength data (MPa) were analyzed using ANOVA (α=0.05). Thermocycling did not decrease the bond strength results for both In-Ceram Alumina (30.6±8.2 MPa; P=0.2053) and In-Ceram zirconia (32.6±9 MPa; P=0.3987) core ceramic-feldspathic veneering ceramic combinations when compared to non-aged conditions (28.1±6.4 MPa, 29.7±7.3 MPa, respectively). There were also no significant differences between adhesion of the veneering ceramic to either In-Ceram Alumina or In-Ceram Zirconia ceramics (P=0.3289). Failure types were predominantly a mixture of adhesive failure between the veneering and the core ceramic together with cohesive fracture of the veneering ceramic. Long-term thermocycling aging conditions did not impair the adhesion of the veneering ceramic to the glass-infiltrated alumina core ceramics tested.

Effects of in-office bleaching on human enamel and dentin. Morphological and mineral changes.

Science.gov (United States)

Llena, Carmen; Esteve, Irene; Forner, Leopoldo

2018-05-01

The effects of HP-based products upon dental enamel and dentin are inconclusive. To evaluate changes in micromorphology and composition of calcium (Ca) and phosphate (P) in enamel and dentin after the application of 37.5% hydrogen peroxide (HP) and 35% carbamide peroxide (CP) METHODS: Crowns of 20 human teeth were divided in two halves. One half was used as control specimen and the other as experimental specimen. The control specimens were kept in artificial saliva, and the experimental specimens were divided into four groups (n=5 each): group 1 (enamel HP for 45min); group 2 (dentin HP for 45min); group 3 (enamel CP for 90min); and group 4 (dentin CP for 90min). The morphological changes were evaluated using confocal laser scanning microscopy (CLSM), while the changes in the composition of Ca and P were assessed using environmental scanning electron microscopy combined with a microanalysis system (ESEM+EDX). The results within each group and between groups were compared using the Wilcoxon test and Mann-Whitney U-test, respectively (p0.05). When bleaching products with a neutral pH are used in clinical practice, both, the concentration and the application time should be taken into account in order to avoid possible structural and mineral changes in enamel and dentin. Copyright © 2018 Elsevier GmbH. All rights reserved.

Yield and ultrasonic modulus of elasticity of red maple veneer

Science.gov (United States)

Robert J. Ross; Steven Verhey; John R. Erickson; John W. Forsman; Brian K. Brashaw; Crystal L. Pilon; Xiping Wang

2004-01-01

The purpose of the study was to assess the potential for using red maple sawlogs to manufacture laminated veneer lumber (LVL). The primary objective was to determine the yield of ultrasonically graded veneer from red maple logs. A sample of 48 logs was obtained from six Eastern and Lake States in the United States. The logs were visually graded and shipped to a plywood...

Opalescence of all-ceramic core and veneer materials.

Science.gov (United States)

Cho, Moon-Sang; Yu, Bin; Lee, Yong-Keun

2009-06-01

The enamel of natural teeth is opalescent, where there is light scattering of the shorter wavelengths of the visible spectrum, giving a tooth a bluish appearance in the reflected color and an orange/brown appearance in the transmitted color. The objective of this study was to determine the opalescence of all-ceramic core, veneer and layered specimens with a color measuring spectrophotometer. Colors of core (A2-corresponding shade), veneer (A2- and A3-corresponding shades) and layered (A2- and A3-layered) ceramics for all-ceramic restorations in clinically relevant thicknesses were measured in the reflectance and transmittance modes. The opalescence parameter (OP), which was calculated as the difference in blue-yellow coordinate (Deltab(*)) and red-green coordinate (Deltaa(*)), and the differences in blue-yellow coordinate (Deltab(*)) and in color (DeltaE(ab)(*)) between the reflected and transmitted colors were calculated. One-way ANOVA was performed for the OP values of the core, veneer and layered specimens by the kind of materials. Regression analysis was performed between the OP and Deltab(*), and the OP and DeltaE(ab)(*) values. The range of the OP value was 1.6-6.1, 2.0-7.1, 1.3-5.0 and 1.6-4.2 for the core, veneer, A2- and A3-layered specimens, respectively, all of which were significantly influenced by the kind of materials (pOpalescence varied by kind of ceramics. The OP values of ceramics were lower than those of tooth enamel. All-ceramic materials that can simulate the opalescence of natural teeth should be developed.

Effect of desensitizing toothpastes on dentin

Directory of Open Access Journals (Sweden)

Shelon Cristina Souza Pinto

2012-10-01

Full Text Available The objective of this study was to analyze the effects of toothbrushing with desensitizing toothpastes on dentin permeability and dentinal tubule occlusion. Fifty rats provided two hundred incisor teeth divided into five groups: DW, brushed with distilled water (control; FT, brushed with fluoride toothpaste; SCT, brushed with strontium chloride toothpaste; PCT, brushed with potassium citrate toothpaste; and PNT, brushed with potassium nitrate toothpaste. Cavities were prepared to expose the dentinal tubules, and the incisor teeth were brushed using the experimental agents. After each treatment, Evans blue dye solution was applied to the teeth. Dentin permeability was analyzed using scanning electron microscopy and energy-dispersive X-rays (EDX. There were significant differences (p < 0.0001, ANOVA among the groups regarding dentin permeability, number of dentinal tubules, diameter of dentinal tubules, and opened tubular area. In the SCT, PCT and PNT groups, opened and partially occluded tubules, deposits, and a few smear layers were observed. In the DW and FT groups, most of the dentinal tubules were open, with no deposits or smear layers on the dentin. EDX revealed peaks of calcium and phosphorus in all of the groups, as well as traces of strontium in the SCT group and of potassium in the PCT and PNT groups. Desensitizing toothpaste decreased dentin permeability, although it produced only partial dentin tubule occlusion.

DENTINE CARIES: ACID-TOLERANT MICROORGANISMS AND ASPECTS ON COLLAGEN DEGRADATION.

Science.gov (United States)

Lager, Anders Hedenbjörk

2014-01-01

. Key findings: Each investigated lesion harbored a unique microbiota in terms of both species composition and numbers of microorganisms. This indicates that various combinations of aciduric microorganisms can colonize, survive in and probably also propagate dentine carious lesions. We also found that solid pH-selective agars can be used successfully to select acid-tolerant microorganisms in caries lesions. This would preserve their phenotypic traits for further study. In Paper III, the relation between salivary levels of matrix metalloproteinase-8 (MMP-8), salivary levels of tissue inhibitor of MMP (TIMP-1), and the presence of manifest caries lesions in a large number of subjects was investigated. Saliva samples were collected and analyzed for concentrations of MMP-8, TIMP-1 and total protein using immunofluorometric assays, enzyme linked immunosorbent assays and Bradford assays, respectively. Key findings: Subjects with manifest caries lesions had significantly elevated levels of salivary MMP-8 compared to subjects without caries lesions. TIMP-1 was not significant in any case. In Paper IV, a new method for generating bioactive demineralized dentine matrix substrate (DDM) was developed using a dialysis system and two different demineralization approaches (acetic acid or EDTA). The generated DDM was subsequently analyzed for the presence of type 1 collagen, active MMP-8 and hydroxyproline (HYP) levels using SDS-PAGE, ELISA or immunofluorescence assay. Key findings: Both demineralization methods produced a substrate rich in collagen and with preserved MMP-8 activity. This report presents new knowledge on the composition of the acid tolerant dentine caries microbiota from three levels in dentine carious lesions and on the efficacy of operative caries removal on the numbers of viable microorganisms in the caries free cavity using two operative methods. Moreover, the basic mechanisms behind collagen degradation in the dentine caries process are studied from both a

[Effect of ceramic thickness and resin cement shades on final color of heat-pressed ceramic veneers].

Science.gov (United States)

Ren, D F; Zhan, K R; Chen, X D; Xing, W Z

2017-02-09

Objective: To analyze the effect of ceramic materials thickness and resin cement shades on the final color of ceramic veneers in the discolored teeth, and to investigate the color agreement of try-in pastes to the corresponding resin cements. Methods: Sixty artificial maxillary central incisor teeth (C2 shade) were used to simulate the natural discolored teeth and prepared according to veneer tooth preparation protocol. Veneers of different thickness in the body region (0.50 and 0.75 mm) were fabricated using ceramic materials (LT A2 shade, IPS e.max Press). The ceramic veneer specimens were bonded to the artificial teeth using the 6 shades of resin cements (Variolink Veneer: shades of LV-3, LV-2, HV+3; RelyX™ Veneer: shades of TR, A3, WO) ( n= 5). A clinical spectrophotometer was used to measure the color parameters of ceramic veneers at the cervical, body and incisal regions. Color changes of veneers before and after cementation were calculated and registered as ΔE1, and the changes between try-in paste and the corresponding resin cements were registered as ΔE2. Results: Three-way ANOVA indicated that ΔE1 and ΔE2 values were significantly affected by the ceramic thickness, resin cement shades and measuring regions ( Pceramic veneers were cemented with resin cements in shades of HV+3 and WO. The ΔE2 values of six shades ranged from 0.60-2.56. The shades of HV+3, WO and A3 resin cements were more than 1.60. Conclusions: Different thickness of ceramic materials, resin cement shades and measuring regions could affect the final color of ceramic veneers. The color differences of some resin cements and corresponding try-in pastes might be observed in clinical practice.

Influence of bruxism on survival of porcelain laminate veneers.

Science.gov (United States)

Granell-Ruíz, Maria; Agustín-Panadero, Rubén; Fons-Font, Antonio; Román-Rodríguez, Juan-Luis; Solá-Ruíz, María-Fernanda

2014-09-01

This study aims to determine whether bruxism and the use of occlusal splints affect the survival of porcelain laminate veneers in patients treated with this technique. Restorations were made in 70 patients, including 30 patients with some type of parafunctional habit. A total of 323 veneers were placed, 170 in patients with bruxism activity, and the remaining 153 in patients without it. A clinical examination determined the presence or absence of ceramic failure (cracks, fractures and debonding) of the restorations; these incidents were analyzed for association with bruxism and the use of splints. Analysis of the ceramic failures showed that of the 13 fractures and 29 debonding that were present in our study, 8 fractures and 22 debonding were related to the presence of bruxism. Porcelain laminate veneers are a predictable treatment option that provides excellent results, recognizing a higher risk of failure in patients with bruxism activity. The use of occlusal splints reduces the risk of fractures.

Stiffness and Density Analysis of Rotary Veneer Recovered from Six Species of Australian Plantation Hardwoods

Directory of Open Access Journals (Sweden)

Robert Lee McGavin

2015-08-01

Full Text Available Commercial interest in Australian hardwood plantations is increasing. The timber industry is investigating alternative supplies of forest resources, and the plantation growing industry is eager to explore alternative markets to maximize financial returns. Identifying suitable processing strategies and high-value products that suit young, plantation-grown hardwoods have proven challenging; however, recent veneer processing trials using simple veneer technology have demonstrated more acceptable recoveries of marketable products. The recovered veneers have visual qualities that are suitable for structurally-based products; however, the mechanical properties of the veneer are largely unknown. Veneers resulting from processing trials of six commercially important Australian hardwood species were used to determine key wood properties (i.e., density, dynamic modulus of elasticity (MoE, and specific MoE. The study revealed that a wide variation of properties existed between species and also within species. Simple mathematical modeling, using sigmoidal curves, was demonstrated to be an effective method to model the evolution of key wood properties across the billet radius and along the resulting veneer ribbon with benefits for tree breeders and processors.

Rehabilitation of a patient with amelogenesis imperfecta using porcelain veneers and CAD/CAM polymer restorations: A clinical report.

Science.gov (United States)

Saeidi Pour, Reza; Edelhoff, Daniel; Prandtner, Otto; Liebermann, Anja

2015-01-01

The complete dental rehabilitation of patients with a vertical dimension loss (VDL) caused by structural enamel deficits associated with amelogenesis imperfecta (AI) represents a difficult challenge for restorative teams. Accurate analysis and treatment planning that includes esthetic and functional evaluations and adequate material selection are important prerequisites for successful results. Long-term provisional restorations play an important role in exploring and elucidating the patients' esthetic demands and functional needs. Restorative treatment options can vary from requiring only oral hygiene instructions to extensive dental restorations that include composite fillings, ceramic veneers, metal-ceramic, or all-ceramic crowns. This case report describes a full-mouth rehabilitation of a patient with amelogenesis imperfecta including the case planning, bite replacement, preparation, and restoration setting steps with an experimental CAD/CAM polymer and porcelain veneers.

Shear bond strength of amalgam to dentin using different dentin adhesive systems

Directory of Open Access Journals (Sweden)

Farimah Sardari

2012-01-01

Full Text Available Background and Aims: The aim of this in vitro study was to assess the shear bond strength of amalgam to dentin using four dentin adhesive systems.Materials and Methods: One hundred human molars were selected. After enamel removal, a dentin cylinder with 3 mm thickness was prepared. Eighty specimens were resorted with amalgam and four dentin adhesive systems as follows (n=20: group 1, Scotch Bond Multi-Purpose; group 2, One Coat Bond; group 3, PQ1; and group 4, Panavia-F. In group 5, 20 specimens were resorted with amalgam and varnish as control group. The specimens were incubated at 37°C for 24 h. The shear bond strengths were then measured by using push out method. The data were analyzed by one-way ANOVA and post hoc Duncan's tests.Results: Mean values for bond strengths of test groups were as follows: group 1=21.03±8.9, group 2=23.47±9, group 3=13.16±8.8, group 4=20.07±8.9 and group 5=14.15±8.7 MPa±SD. One-way ANOVA showed the statistically significant difference between the bond strengths of five groups (P=0.001. Post hoc Duncan's test showed significant difference between groups 1and 3 (P=0.008, groups 1 and 5 (P=0.019, groups 2 and 5 (P=0.0008, groups 4 and 5 (P=0.042, and groups 3 and 4 (P=0.018.Conclusion: Results of this study showed that the bond strength of amalgam to dentin using One Coat Bond as dentin adhesive system was higher than that observed in other dentin adhesive systems.

Buffering action of human dentin in vitro.

Science.gov (United States)

Camps, J; Pashley, D H

2000-01-01

The purpose of this study was to determine the relative contributions of the mineral and organic phases of dentin to its total buffering capacity and to compare the buffering abilities of normal and caries-affected dentin for acids used in adhesive dentistry. Disks of normal and caries-affected human coronal dentin 0.6 mm thick were prepared. Fifty microL of various acids were applied to the surface of mineralized or completely demineralized dentin for varying lengths of time. They were collected from the surface and combined with water rinses to permit titration of the total amount of acid applied, the amount recovered, the total amount that was taken up by the dentin, and the amount that diffused across dentin into 1 mL of water. Equal volumes of acids were applied to mineralized or demineralized dentin powder or hydroxyapatite powder. About 88% to 90% of applied acid was recovered from the surface; only 10% to 12% of the acid was taken up by dentin. Of the H+ that was taken up, only 1% to 2% actually diffused across 0.6 mm of dentin. Increasing the application time of 37% phosphoric acid did not increase the amount of H+ that diffused across dentin. Increasing the concentration of phosphoric acid from 10% to 65% produced only slight increases in H+ diffusion across dentin. There was no difference in the buffering capacity of normal vs caries-affected dentin disks. Almost all of the buffering capacity of dentin is due to its mineral phase. The high buffering capacity of dentin and the high reactivity of H+ insure that little H+ diffuses through dentin more than 0.6 mm thick.

Dentin bond strength and nanoleakage of the adhesive interface after intracoronal bleaching.

Science.gov (United States)

Cavalli, Vanessa; Sebold, Maicon; Shinohara, Mirela Sanae; Pereira, Patrícia Nóbrega Rodrigues; Giannini, Marcelo

2018-04-01

This study evaluated dentin bond strength (BS) and nanoleakage of non- and pre-etched dentin immediately (T 0 ,), 7 days (T 7 ), and 14 days (T 14 ) after bleaching. Bovine incisors (150) were selected and half of them submitted to intrapulpal dentin etching (e). Non- and pre-etched dentin were subjected to the following (n = 15): no bleaching/control (C); 35% carbamide peroxide (CP); 35% hydrogen peroxide (35% HP); 25% hydrogen peroxide (25% HP); and sodium perborate (SP). Bleaching agents were applied to the pulp chamber four times within a 72-h interval. Afterwards, pulp chamber dentin was prepared for the BS test at different evaluation times (n = 5): T 0 , T 7 , and T 14 . Composite blocks were built on pulp chamber and sectioned in slices. Slices were reduced to an hour-glass shape with a cross-sectional area of 0.8 mm 2 and submitted to microtensile BS test. Two additional specimens for each group were prepared for nanoleakage evaluation by transmission electron microscopy (TEM). Results were analyzed by ANOVA (two-way) and Dunnett's test (p bleaching for both sound and pre-etched dentin (p bleached dentin increased for all groups, whereas the pre-etched SPe group presented BS similar to the Ce. Nanoleakage within the hybrid layer was perceptible immediately after bleaching, although a decrease in nanoleakage was observed for all groups at T 14 . Adhesive restorations should be performed 7-14 days after bleaching, according to the bleaching agent used. Intracoronal bleaching should be performed preferably with sodium perborate if previous dentin etching is applied. © 2018 Wiley Periodicals, Inc.

Fabrication of Silicon Nitride Dental Core Ceramics with Borosilicate Veneering material

Science.gov (United States)

Wananuruksawong, R.; Jinawath, S.; Padipatvuthikul, P.; Wasanapiarnpong, T.

2011-10-01

Silicon nitride (Si3N4) ceramic is a great candidate for clinical applications due to its high fracture toughness, strength, hardness and bio-inertness. This study has focused on the Si3N4 ceramic as a dental core material. The white Si3N4 was prepared by pressureless sintering at relative low sintering temperature of 1650 °C in nitrogen atmosphere. The coefficient of thermal expansion (CTE) of Si3N4 ceramic is lower than that of Zirconia and Alumina ceramic which are popular in this field. The borosilicate glass veneering was employed due to its compatibility in thermal expansion. The sintered Si3N4 specimens represented the synthetic dental core were paintbrush coated by a veneer paste composed of borosilicate glass powder (tube furnace between 1000-1200°C. The veneered specimens fired at 1100°C for 15 mins show good bonding, smooth and glossy without defect and crazing. The veneer has thermal expansion coefficient as 3.98×10-6 °C-1, rather white and semi opaque, due to zirconia addition, the Vickers hardness as 4.0 GPa which is closely to the human teeth.

Human and Bovine Dentin Composition and Its Hybridization Mechanism Assessed by FT-Raman Spectroscopy

Directory of Open Access Journals (Sweden)

L. E. S. Soares

2013-01-01

Full Text Available FT-Raman spectroscopy was used to study the human and bovine dentin and their interactions with adhesive systems. Ten human (H molars and ten bovine (B teeth were prepared exposing the dentin and then each specimen was divided into two parts. The resulted forty dentin segments were treated either with the total-etch one bottle adhesive (Prime & Bond 2.1, PB or with the single-step self-etching adhesive (Xeno III, X and divided into four groups: HPB (control, HX, BPB, and BX. Each group was analyzed by FT-Raman spectroscopy before and after the adhesive treatment. Six regions of the Raman spectrum were analyzed and the integrated areas of organic and inorganic peaks were calculated. Bovine untreated specimens showed higher peak area of PO4 3−ν2  content than in human specimens. Human untreated specimens had higher peak areas of PO4 3−ν4 and CO3 2−ν1  contents than in bovine specimens. The peak areas of amide III, CH2, and amide I contents were higher in human than in bovine specimens (before treatments. Treated dentin showed no significant statistical differences between the adhesives for both inorganic and organic contents considering the same substrate. However, the differences found between human and bovine specimens after adhesives application show a reduced accuracy of these substrates as a substitute to the human specimens.

Porcine dentin sialoprotein glycosylation and glycosaminoglycan attachments.

Science.gov (United States)

Yamakoshi, Yasuo; Nagano, Takatoshi; Hu, Jan Cc; Yamakoshi, Fumiko; Simmer, James P

2011-02-03

Dentin sialophosphoprotein (Dspp) is a multidomain, secreted protein that is critical for the formation of tooth dentin. Mutations in DSPP cause inherited dentin defects categorized as dentin dysplasia type II and dentinogenesis imperfecta type II and type III. Dentin sialoprotein (Dsp), the N-terminal domain of dentin sialophosphoprotein (Dspp), is a highly glycosylated proteoglycan, but little is known about the number, character, and attachment sites of its carbohydrate moieties. To identify its carbohydrate attachment sites we isolated Dsp from developing porcine molars and digested it with endoproteinase Glu-C or pronase, fractionated the digestion products, identified fractions containing glycosylated peptides using a phenol sulfuric acid assay, and characterized the glycopeptides by N-terminal sequencing, amino acid analyses, or LC/MSMS. To determine the average number of sialic acid attachments per N-glycosylation, we digested Dsp with glycopeptidase A, labeled the released N-glycosylations with 2-aminobenzoic acid, and quantified the moles of released glycosylations by comparison to labeled standards of known concentration. Sialic acid was released by sialidase digestion and quantified by measuring β-NADH reduction of pyruvic acid, which was generated stoichiometrically from sialic acid by aldolase. To determine its forms, sialic acid released by sialidase digestion was labeled with 1,2-diamino-4,5-methyleneoxybenzene (DMB) and compared to a DMB-labeled sialic acid reference panel by RP-HPLC. To determine the composition of Dsp glycosaminoglycan (GAG) attachments, we digested Dsp with chondroitinase ABC and compared the chromotagraphic profiles of the released disaccharides to commercial standards. N-glycosylations were identified at Asn37, Asn77, Asn136, Asn155, Asn161, and Asn176. Dsp averages one sialic acid per N-glycosylation, which is always in the form of N-acetylneuraminic acid. O-glycosylations were tentatively assigned at Thr200, Thr216 and Thr

Porcine dentin sialoprotein glycosylation and glycosaminoglycan attachments

Directory of Open Access Journals (Sweden)

Yamakoshi Fumiko

2011-02-01

Full Text Available Abstract Background Dentin sialophosphoprotein (Dspp is a multidomain, secreted protein that is critical for the formation of tooth dentin. Mutations in DSPP cause inherited dentin defects categorized as dentin dysplasia type II and dentinogenesis imperfecta type II and type III. Dentin sialoprotein (Dsp, the N-terminal domain of dentin sialophosphoprotein (Dspp, is a highly glycosylated proteoglycan, but little is known about the number, character, and attachment sites of its carbohydrate moieties. Results To identify its carbohydrate attachment sites we isolated Dsp from developing porcine molars and digested it with endoproteinase Glu-C or pronase, fractionated the digestion products, identified fractions containing glycosylated peptides using a phenol sulfuric acid assay, and characterized the glycopeptides by N-terminal sequencing, amino acid analyses, or LC/MSMS. To determine the average number of sialic acid attachments per N-glycosylation, we digested Dsp with glycopeptidase A, labeled the released N-glycosylations with 2-aminobenzoic acid, and quantified the moles of released glycosylations by comparison to labeled standards of known concentration. Sialic acid was released by sialidase digestion and quantified by measuring β-NADH reduction of pyruvic acid, which was generated stoichiometrically from sialic acid by aldolase. To determine its forms, sialic acid released by sialidase digestion was labeled with 1,2-diamino-4,5-methyleneoxybenzene (DMB and compared to a DMB-labeled sialic acid reference panel by RP-HPLC. To determine the composition of Dsp glycosaminoglycan (GAG attachments, we digested Dsp with chondroitinase ABC and compared the chromotagraphic profiles of the released disaccharides to commercial standards. N-glycosylations were identified at Asn37, Asn77, Asn136, Asn155, Asn161, and Asn176. Dsp averages one sialic acid per N-glycosylation, which is always in the form of N-acetylneuraminic acid. O-glycosylations were

Fabrication of Silicon Nitride Dental Core Ceramics with Borosilicate Veneering material

Energy Technology Data Exchange (ETDEWEB)

Wananuruksawong, R; Jinawath, S; Wasanapiarnpong, T [Research Unit of Advanced Ceramic, Department of Materials Science, Faculty of Science, Chulalongkorn University, Bangkok (Thailand); Padipatvuthikul, P, E-mail: raayaa_chula@hotmail.com [Faculty of Dentistry, Srinakharinwirot University, Bangkok (Thailand)

2011-10-29

Silicon nitride (Si{sub 3}N{sub 4}) ceramic is a great candidate for clinical applications due to its high fracture toughness, strength, hardness and bio-inertness. This study has focused on the Si{sub 3}N{sub 4} ceramic as a dental core material. The white Si{sub 3}N{sub 4} was prepared by pressureless sintering at relative low sintering temperature of 1650 deg. C in nitrogen atmosphere. The coefficient of thermal expansion (CTE) of Si{sub 3}N{sub 4} ceramic is lower than that of Zirconia and Alumina ceramic which are popular in this field. The borosilicate glass veneering was employed due to its compatibility in thermal expansion. The sintered Si{sub 3}N{sub 4} specimens represented the synthetic dental core were paintbrush coated by a veneer paste composed of borosilicate glass powder (<150 micrometer, Pyrex) with 5 wt% of zirconia powder (3 wt% Y{sub 2}O{sub 3} - partial stabilized zirconia) and 30 wt% of polyvinyl alcohol (5 wt% solution). After coating the veneer on the Si{sub 3}N{sub 4} specimens, the firing was performed in electric tube furnace between 1000-1200 deg. C. The veneered specimens fired at 1100 deg. C for 15 mins show good bonding, smooth and glossy without defect and crazing. The veneer has thermal expansion coefficient as 3.98x10{sup -6} deg. C{sup -1}, rather white and semi opaque, due to zirconia addition, the Vickers hardness as 4.0 GPa which is closely to the human teeth.

The effect of Er:YAG laser irradiation on the bond stability of self-etch adhesives at different dentin depths.

Science.gov (United States)

Karadas, Muhammet; Çağlar, İpek

2017-07-01

The aim of this study was to evaluate the effect of Er:YAG laser irradiation on the micro-shear bond strength of self-etch adhesives to the superficial dentin and the deep dentin before and after thermocycling. Superficial dentin and deep dentin surfaces were prepared by flattening of the occlusal surfaces of extracted human third molars. The deep or superficial dentin specimens were randomized into three groups according to the following surface treatments: group I (control group), group II (Er:YAG laser; 1.2 W), and group III (Er:YAG laser; 0.5 W). Clearfil SE Bond or Clearfil S 3 Bond was applied to each group's dentin surfaces. After construction of the composite blocks on the dentin surface, the micro-shear bond testing of each adhesive was performed at 24 h or after 15,000 thermal cycles. The data were analyzed using a univariate analysis of variance and Tukey's test (p  0.05). However, deep-dentin specimens irradiated with laser showed significantly higher bond strengths than did control specimens after thermocycling (p adhesives may be altered by the dentin depth. Regardless of the applied surface treatment, deep dentin showed significant bond degradation.

Study on Flexural Creep Parameters of Overlayed Particleboard by Natural and Melaminated Veneers

Directory of Open Access Journals (Sweden)

Abdollah Najafi

2012-06-01

Full Text Available In this study, effects of natural and artificial veneer on flexural creep behavior of particleboard was investigated. Particleboard panels were prepared from Pars Neopan industries with 660 kg/m3 density and then overlaid by natural and melamine veneers. Their creep behavior was compared to control particleboard. For evaluating maximum bending load in static flexural test, specimens were cut from panels according to ASTM D 1037 with dimensions of 370×50×16 mm. Then, The flexural creep tests at 20% and 40% of failure bending load was applied to test specimens. Results of flexural tests indicated that the MOR and MOE values of veneered particleboard were highest. Results of creep showed that levels of stresses are effective on all creep parameters, but showed less effect on relative creep. Also, creep parameters less effective on specimens overlaid by natural veneer.

Sealing ability of a new calcium silicate based material as a dentin substitute in class II sandwich restorations: An in vitro study

Directory of Open Access Journals (Sweden)

Raji Viola Solomon

2014-01-01

Full Text Available Background: Class ll sandwich restorations are routinely performed where conventional Glass ionomer cement (GIC or Resin-modified GIC (RMGIC is used as a base or dentin substitute and a light curing composite resin restorative material is used as an enamel substitute. Various authors have evaluated the microleakage of composite resin restorations where glass ionomer cement has been used as a base in class II sandwich restorations, but a literature survey reveals limited studies on the microleakage analysis of similar restorations with biodentine as a dentin substitute, as an alternative to glass ionomer cement. The aim of this study is: To evaluate the marginal sealing efficacy of a new calcium-silicate-based material (Biodentine as a dentin substitute, at the cervical margins, in posterior class II sandwich restorations.To compare and evaluate the microleakage at the biodentine/composite interface with the microleakage at the resin-modified GIC/composite interface, in posterior class II open sandwich restorations. To compare the efficacy between a water-based etch and rinse adhesive (Scotch bond multipurpose and an acetone-based etch and rinse adhesive (Prime and bond NT, when bonding biodentine to the composite. To evaluate the enamel, dentin, and interfacial microleakage at the composite and biodentine/RMGIC interfaces. Materials and Methods: Fifty class II cavities were prepared on the mesial and distal surfaces of 25 extracted human maxillary third molars, which were randomly divided into five groups of ten cavities each: (G1 Biodentine group, (G2 Fuji II LC GIC group, (G3 Biodentine as a base + prime and bond NT + Tetric N-Ceram composite, (G4 Biodentine + scotchbond multi-purpose + Tetric N-Ceram composite, (G5 Fuji II LC as a base + prime and bond NT+ Tetric-N Ceram composite. The samples were then subjected to thermocycling, 2500× (5°C to 55°C, followed by the dye penetration test. Scores are given from 0 to 3 based on the depth of

Influence of abutment type and esthetic veneering on preload maintenance of abutment screw of implant-supported crowns.

Science.gov (United States)

Delben, Juliana Aparecida; Barão, Valentim Adelino Ricardo; Dos Santos, Paulo Henrique; Assunção, Wirley Gonçalves

2014-02-01

The effect of veneering materials on screw joint stability remains inconclusive. Thus, this study evaluated the preload maintenance of abutment screws of single crowns fabricated with different abutments and veneering materials. Sixty crowns were divided into five groups (n = 12): UCLA abutment in gold alloy with ceramic (group GC) and resin (group GR) veneering, UCLA abutment in titanium with ceramic (group TiC) and resin (group TiR) veneering, and zirconia abutment with ceramic veneering (group ZiC). Abutment screws made of gold were used with a 35 Ncm insertion torque. Detorque measurements were obtained initially and after mechanical cycling. Data were analyzed by ANOVA and Fisher's exact test at a significance level of 5%. For the initial detorque means (in Ncm), group TiC (21.4 ± 1.78) exhibited statistically lower torque maintenance than groups GC (23.9 ± 0.91), GR (24.1 ± 1.34), and TiR (23.2 ± 1.33) (p abutment type and veneering material. More irregular surfaces in the hexagon area of the castable abutments were observed. The superiority of any veneering material concerning preload maintenance was not established. © 2013 by the American College of Prosthodontists.

Dentin bond strength and degree of conversion evaluation of experimental self-etch adhesive systems

OpenAIRE

Yazdi, Fatemeh-Maleknejad; Moosavi, Horieh; Atai, Mohammad; Zeynali, Mahsa

2015-01-01

Background The aim of this study was to investigate the effect of different concentrations of 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) monomer in one-step self-etch experimental adhesives on dentinal microshear bond strength (?SBS), their degree of conversion and bonded micro structure. Material and Methods Composite resin cylinders (Clearfil AP-X) were bonded on human sound molar dentinal surfaces by using five experimental one-step self-etching adhesives (1-SEAs) containing 0% ...

Evidence of yttrium silicate inclusions in YSZ-porcelain veneers.

Science.gov (United States)

Stoner, Brian R; Griggs, Jason A; Neidigh, John; Piascik, Jeffrey R

2014-04-01

This report introduces the discovery of crystalline defects that can form in the porcelain veneering layer when in contact with yttria-stabilized zirconia (YSZ). The focus was on dental prostheses and understanding the defects that form in the YSZ/porcelain system; however the data reported herein may have broader implications toward the use and stability of YSZ-based ceramics in general. Specimens were cut from fully sintered YSZ plates and veneering porcelain was applied (X-ray (EDAX) was used for microstructural and elemental analysis. EDAX, for chemical analysis and transmission electron diffraction (TED) for structural analysis were both performed in the transmission electron microscope (TEM). Additionally, in order to spatially resolve Y-rich precipitates, micro-CT scans were conducted at varying depths within the porcelain veneer. Local EDAX (SEM) was performed in the regions of visible inclusions and showed significant increases in yttrium concentration. TEM specimens also showed apparent inclusions in the porcelain and selected area electron diffraction was performed on these regions and found the inclusions to be crystalline and identified as either yttrium-silicate (Y2 SiO5 ) or yttrium-disilicate (Y2 Si2 O7 ). Micro-CT data showed that yttrium-silicate precipitates were distributed throughout the thickness of the porcelain veneer. Future studies are needed to determine whether many of the premature failures associated with this materials system may be the result of crystalline flaws that form as a result of high temperature yttrium diffusion near the surfaces of YSZ. © 2013 Wiley Periodicals, Inc.

Shear bond strength of one-step self-etch adhesives to dentin: Evaluation of NaOCl pretreatment.

Science.gov (United States)

Colombo, Marco; Beltrami, Riccardo; Chiesa, Marco; Poggio, Claudio; Scribante, Andrea

2018-02-01

The aim of this study was to evaluate the influence of dentin pretreatment with NaOCl on shear bond strength of four one-step self-etch adhesives with different pH values. Bovine permanent incisors were used. Four one-step self-etch adhesives were tested: Adper™ Easy Bond, Futurabond NR, G-aenial Bond, Clearfil S3 Bond. One two-step self-etch adhesive (Clearfil SE Bond) was used as control. Group 1- no pretreatment; group 2- pretratment with 5,25 % NaOCl; group 3- pretreatment with 37 % H3PO4 etching and 5,25 % NaOCl. A hybrid composite resin was inserted into the dentin surface. The specimens were tested in a universal testing machine. The examiners evaluated the fractured surfaces in optical microscope to determine failure modes, quantified with adhesive remnant index (ARI). Dentin pretreatment variably influenced bond strength values of the different adhesive systems. When no dentin pretreatment was applied, no significant differences were found ( P >.05) among four adhesives tested. No significant differences were recorded when comparing NaOCl pretreatment with H3PO4 + NaOCl pretreatment for all adhesive tested ( P >.05) except Clearfil S3 Bond that showed higher shear bond strength values when H3PO4 was applied. Frequencies of ARI scores were calculated. The influence of dentin pretreatment with NaOCl depends on the composition of each adhesive system used. There was no difference in bond strength values among self-etch adhesives with different pH values. Key words: Dentin, pretreatment, self-etch adhesives.

Hereditary dentine disorders: dentinogenesis imperfecta and dentine dysplasia

Directory of Open Access Journals (Sweden)

MacKie Iain

2008-11-01

Full Text Available Abstract The hereditary dentine disorders, dentinogenesis imperfecta (DGI and dentine dysplasia (DD, comprise a group of autosomal dominant genetic conditions characterised by abnormal dentine structure affecting either the primary or both the primary and secondary dentitions. DGI is reported to have an incidence of 1 in 6,000 to 1 in 8,000, whereas that of DD type 1 is 1 in 100,000. Clinically, the teeth are discoloured and show structural defects such as bulbous crowns and small pulp chambers radiographically. The underlying defect of mineralisation often results in shearing of the overlying enamel leaving exposed weakened dentine which is prone to wear. Currently, three sub-types of DGI and two sub-types of DD are recognised but this categorisation may change when other causative mutations are found. DGI type I is inherited with osteogenesis imperfecta and recent genetic studies have shown that mutations in the genes encoding collagen type 1, COL1A1 and COL1A2, underlie this condition. All other forms of DGI and DD, except DD-1, appear to result from mutations in the gene encoding dentine sialophosphoprotein (DSPP, suggesting that these conditions are allelic. Diagnosis is based on family history, pedigree construction and detailed clinical examination, while genetic diagnosis may become useful in the future once sufficient disease-causing mutations have been discovered. Differential diagnoses include hypocalcified forms of amelogenesis imperfecta, congenital erythropoietic porphyria, conditions leading to early tooth loss (Kostmann's disease, cyclic neutropenia, Chediak-Hegashi syndrome, histiocytosis X, Papillon-Lefevre syndrome, permanent teeth discolouration due to tetracyclines, Vitamin D-dependent and vitamin D-resistant rickets. Treatment involves removal of sources of infection or pain, improvement of aesthetics and protection of the posterior teeth from wear. Beginning in infancy, treatment usually continues into adulthood with a

Functional remineralization of carious dentin

Science.gov (United States)

Pugach, Megan Kardon

A primary goal of dental tissue engineering is the biological reconstruction of tooth substrate destroyed by caries or other diseases affecting tooth mineralization. Traditionally, dentists treat caries by using invasive techniques to remove the diseased dental tissue and restore the lesion, ideally preventing further progression of decay. Success in strategies associated with remineralization of enamel and root caries have contributed to the less invasive prospect of remineralization of dentinal carious lesions. The central hypothesis of this dissertation is that carious dentin lesions can be remineralized if the lesions contain residual mineral. Caries Detector (CD) stained zones (pink, light pink, transparent and normal) of arrested carious dentin lesions were characterized according to microstructure by atomic force microscopy (AFM) imaging, mineral content by digital transverse microradiography, and nanomechanical properties by AFM-based nanoindentation. CD-stained and unstained zones had significantly different microstructure, mineral content and nanomechanical properties. Furthermore, the most demineralized carious zone contained residual mineral. To obtain reproducible, standardized dentin caries lesions, we characterized the lesions from an artificial carious dentin lesion model using a 0.05M acetate demineralization buffer. The artificial caries-like lesions produced by the buffer had similar mineral content and nanomechanical properties in the stained and unstained zones as natural dentin lesions. Both natural and artificial lesions had significant correlations between mineral content and nanomechanical properties. Mineral crystallite size and shape was examined by small angle x-ray scattering. Both natural and artificial carious dentin had different mineral sizes than normal dentin. Collagen in natural and artificial carious dentin lesions was examined by trichrome stain, AFM high-resolution imaging, and UV resonance Raman spectroscopy, to determine if

Influence of firing time and framework thickness on veneered Y-TZP discs curvature.

Science.gov (United States)

Jakubowicz-Kohen, Boris D; Sadoun, Michaël J; Douillard, Thierry; Mainjot, Amélie K

2014-02-01

The objective of the present work was to study the curvature of very thinly, veneered Y-TZP discs of different framework thicknesses submitted to different firing times. Fifteen 20-mm-wide Y-TZP discs were produced in three different thicknesses: 0.75, 1, 1.5mm. One disc from each group was left unveneered while the others were layered with a 0.1mm veneering ceramic layer. All discs underwent five firing cycles for a total cumulative firing time of 30 min, 1, 2, 5 and 10h at 900°C. The curvature profile was measured using a profilometer after the veneering process and after each firing cycle respectively. A fitted curve was then used to estimate the, curvature radius. The coefficient of thermal expansion (CTE) measurements were taken on veneering, ceramic and Y-TZP beam samples that underwent the same firing schedule. Those data were used to calculate the curvature generated by CTE variations over firing time. All bilayered samples exhibited a curvature that increased over firing time inversely to framework thickness. However non-veneered samples did not exhibit any curvature modification. The results of the present study reveal that even a very thin veneer layer (0.1mm) can induce a significant curvature of Y-TZP discs. The dilatometric results showed that Tg and CTE, variations are not sufficient to explain this curvature. A chemical-induced zirconia volume, augmentation located at the framework sub-surface near the interface could explain the sample, curvature and its increase with firing time. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Raman Microspectrometry: An Alternative Method of Age Estimation from Dentin and Cementum

Directory of Open Access Journals (Sweden)

Karuna Kumari

2017-10-01

Full Text Available Introduction: Raman spectroscopy is simple, quick, sensitive and non destructive form of tissue examination that provides vital data about the structure, molecular composition and interactions within a sample. The human hard tissues like teeth and bone are able to resist decay for long even after other tissues are lost, thus have valuable forensic importance. Aim: To ascertain the known age of the teeth by analysing dentin and cementum using Raman microspectrometry and assess the accuracy of age estimation by comparison of dentin with cementum. Materials and Methods: The sound permanent extracted tooth specimens (40 of age ranging between 12-74 years were collected and sectioned longitudinally and different dentinal and cemental areas were analysed by Raman microspectrometry. The spectra of dentin and cementum were used as predictors of age estimation. For each sample, ratios were obtained for dentin and cementum areas, and Pearson’s correlation coefficient was calculated. Ratios, which had a correlation coefficient greater than 0.40 were used for further statistical analysis. This led to selection of ratios only for dentin areas, and it allowed us to develop a regression formula. Partial Least Square (PLS regression method was used for computing our model. Results: A significant correlation was observed between the actual chronological age and predicted age of the individual using dentinal areas of the tooth. A closest to the estimated result was achieved, with an error of three years between predicted and actual chorological age. Conclusion: Raman microspectrometry may be considered as an alternative to the conventional method of age estimation and contribute to the identification of individuals.

Paucity of Nanolayering in Resin-Dentin Interfaces of MDP-based Adhesives.

Science.gov (United States)

Tian, F; Zhou, L; Zhang, Z; Niu, L; Zhang, L; Chen, C; Zhou, J; Yang, H; Wang, X; Fu, B; Huang, C; Pashley, D H; Tay, F R

2016-04-01

Self-assembled nanolayering structures have been reported in resin-dentin interfaces created by adhesives that contain 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP). These structures have been hypothesized to contribute to bond durability. The objective of the present study was to determine the extent of nanolayering in resin-dentin interfaces after application of commercialized 10-MDP-containing self-etch and universal adhesives to human dentin. Seven commercialized adhesives were examined: Adhese Universal (Ivoclar-Vivadent), All-Bond Universal (Bisco, Inc.), Clearfil SE Bond 2, Clearfil S3 Bond Plus, Clearfil Universal Bond (all from Kuraray Noritake Dental Inc.), G-Premio Bond (GC Corp.), and Scotchbond Universal (3M ESPE). Each adhesive was applied in the self-etch mode on midcoronal dentin according to the respective manufacturer's instructions. Bonded specimens (n = 6) were covered with flowable resin composite, processed for transmission electron microscopy, and examined at 30 random sites without staining. Thin-film glancing angle X-ray diffraction (XRD) was used to detect the characteristic peaks exhibited by nanolayering (n = 4). The control consisted of 15%wt, 10%wt, and 5%wt 10-MDP (DM Healthcare Products, Inc.) dissolved in a mixed solvent (ethanol and water weight ratio 9:8, with photoinitiators). Experimental primers were applied to dentin for 20 s, covered with hydrophobic resin layer, and examined in the same manner. Profuse nanolayering with highly ordered periodicity (~3.7 nm wide) was observed adjacent to partially dissolved apatite crystallites in dentin treated with the 15% 10-MDP primer. Three peaks in the 2θ range of 2.40° (3.68 nm), 4.78° (1.85 nm), and 7.18° (1.23 nm) were identified from thin-film XRD. Reduction in the extent of nanolayering was observed in the 10% and 5% 10-MDP experimental primer-dentin interface along with lower intensity XRD peaks. Nanolayering and characteristic XRD peaks were rarely observed in

A medicated polycarboxylate cement to prevent complications in composite resin therapy

International Nuclear Information System (INIS)

Okamoto, Y.; Shintani, H.; Yamaki, M.

1990-01-01

Preparative treatment is the preferred method to protect the dentin and pulp from complications in composite resin therapy. This study investigated the in vivo effects of the polycarboxylate cement containing zinc fluoride and tannic acid in composite resin restorations. Scanning electron micrographs established that the composite resin failed to contact the axial wall. The gaps varied from 10 to 60 microns. However, this polycarboxylate cement was shown to provide excellent adaptation to dentin when used as a base and its chemical adhesion allowed it to make close contact with the unetched dentin. The newly developed electron probe x-ray microanalyzer revealed that the in vivo penetration of fluoride and zinc occurred through the dentinal tubules. When this polycarboxylate cement was used, the orifices of dentinal tubules were partially occluded, possibly with the smear layer fixed by tannic acid. In addition, by releasing the components, this polycarboxylate cement adds acid resistance to dentin and increases the resistance of dentin collagen to proteolytic enzymes. As such this polycarboxylate cement offers advantages as a base to composite resin therapy

Modification of dentin surface to enamel-like structure: A potential strategy for improving dentin bonding durability, desensitizing and self-repairing

Directory of Open Access Journals (Sweden)

Hongye Yang

2014-01-01

Full Text Available Introduction: Current theories of dentin bonding are based on the concept of "hybrid layer". However, the histological complexity of dentin, as well as the vulnerability of the hybrid layer, goes against the long-term effect of dentin bonding. At the same time, post-operative sensitivity is more likely to occur after traditional adhesive restoration. The Hypothesis: Compared to dentin bonding, enamel bonding exhibits a more optimal immediate and long-term performance, owing to its higher degree of mineralization, well-arranged enamel crystals and the porous structure after etching. Moreover, "enamel hypersensitivity" is never going to happen due to the lack of tubules existing in dentin. In light of this phenomenon, we brought up the concept and the proposal method to form an "enamel-like" dentin, simulating enamel structure to achieve satisfying durability of dentin bonding and obtain good performance for preventing post-operative sensitivity. With the application of mesoporous silicon bi-directionally binding to hydroxyapatite of dentin itself and hydroxyapatite nanorods synthetized in vitro, we may be able to form an enamel-like "functional layer" via ion-regulating self-assembly. Evaluation of Hypothesis: This paper explains how to achieve dentin enamel-like modification by chemical methods, especially, details the strategies and possible mechanisms of the hypothesis. Validation of the hypothesis is more likely to eliminate the adverse effect of dentinal fluid, improve long-term performance of dentin bonding, offer strategies for desensitizing treatment and self-repairing carious-affected dentin, and furthermore, provide the possibility to introduce new theories of dentin bonding.

Microtensile dentin bond strength of fifth with five seventh-generation dentin bonding agents after thermocycling: An in vitro study

Directory of Open Access Journals (Sweden)

Bruhvi Poptani

2012-01-01

Full Text Available Objectives: The objective of this in vitro study was to compare the microtensile dentin bond strength (μTBS of five seventh-generation dentin bonding agents (DBA with fifth-generation DBA before and after thermocycling. Materials and Methods: Ten extracted teeth were assigned to fifth generation control group (optibond solo and each of the five experimental groups namely, Group I (G-Bond ,Group II (S 3 Clearfil, Group III (One Coat 7.0, Group IV (Xeno V, and Group V (Optibond all in one. The crown portions of the teeth were horizontally sectioned below the central groove to expose the dentin. The adhesive resins from all groups were bonded to the teeth with their respective composites. Specimens of sizes 1 × 1 × 6 mm 3 were obtained. Fifty specimens that bonded to dentin from each group were selected. Twenty-five of the specimens were tested for debonding without thermocycling and the remaining were subjected to thermocycling followed by μTBS testing. The data were analyzed with one-way ANOVA and Dunnett′s-test for comparison with the reference group(Vth Generation. Results: There was no significant difference (P > 0.05 between the fifth- and seventh-generation adhesives before and after thermocycling. The results of our study showed significantly higher value (P < 0.05 of μTBS of seventh-generation Group II (Clearfil S 3 compared to the fifth-generation before and after thermocycling. Conclusion: The study demonstrated that the Clearfil S 3 bond had the highest μTBS values. In addition, of the five tested seventh-generation adhesive resins were comparable to the fifth-generation DBA.

In vitro Comparative Evaluation of Tensile Bond Strength of 6(th), 7(th) and 8(th) Generation Dentin Bonding Agents.

Science.gov (United States)

Kamble, Suresh S; Kandasamy, Baburajan; Thillaigovindan, Ranjani; Goyal, Nitin Kumar; Talukdar, Pratim; Seal, Mukut

2015-05-01

Newer dentin bonding agents were developed to improve the quality of composite restoration and to reduce time consumption in its application. The aim of the present study was to evaluate tensile bond strength of 6(th), 7(th) and 8(th) generation bonding agents by in vitro method. Selected 60 permanent teeth were assigned into 20 in each group (Group I: 6(th) generation bonding agent-Adper SE plus 3M ESPE, Group II: 7(th) generation bonding agent-G-Bond GC Corp Japan and Group III: 8(th) generation dentin adhesives-FuturaBond, DC, Voco, Germany). With high-speed diamond disc, coronal dentin was exposed, and selected dentin bonding agents were applied, followed by composite restoration. All samples were saved in saline for 24 h and tensile bond strength testing was done using a universal testing machine. The obtained data were tabulated and statistically analyzed using ANOVA test. The tensile bond strength readings for 6(th) generation bonding agent was 32.2465, for 7(th) generation was 31.6734, and for 8(th)-generation dentine bonding agent was 34.74431. The highest tensile bond strength was seen in 8(th) generation bonding agent compared to 6(th) and 7(th) generation bonding agents. From the present study it can be conclude that 8(th) generation dentine adhesive (Futura DC, Voco, Germany) resulted in highest tensile bond strength compared to 6(th) (Adper SE plus, 3M ESPE) and 7(th) generation (G-Bond) dentin bonding agents.

Comparison of shear bond strength between unfilled resin to dry enamel and dentin bonding to moist and dry enamel

Directory of Open Access Journals (Sweden)

Yasini E.

2005-05-01

Full Text Available Statement of Problem: The use of dentine bondings on enamel and dentin in total etch protocols has recently become popular. Unfilled resin is hydrophobic and dentin bonding is hydrophilic in nature. This chemical difference could be effective in enamel bonding process. Purpose: The aim of this study was to compare the shear bond strength of unfilled resin to dry enamel and dentin bonding to dry and moist enamel. Materials and Methods: In this experimental study, a total of 30 incisor teeth were used. The specimens were randomly assigned to three groups of 10. 37% phosphoric acid etchant was applied to the enamel surfaces in each group for 15 seconds, rinsed with water for 20 seconds and dried for 20 seconds with compressed air in groups one and two. After conditioning, group 1 received unfilled resin (Margin Bond, Colten and group 2 received dentin bonding (Single Bond, 3M and in group 3 after conditioning and rinsing with water, a layer of dentin bonding (Single Bond was applied on wet enamel. The enamel and dentin bonding were light cured for 20 seconds. A ring mold 3.5 mm in diameter and 2 mm height was placed over the specimens to receive the composite filling material (Z100, 3M. The composite was cured for 40 seconds. The specimens were thermocycled and shear bond strengths were determined using an Instron Universal Testing Machine. The findings were analyzed by ANOVA One-Way and Tukey HSD tests. Results: Shear bond strength of dentin bonding to dry enamel was significantly less than unfilled resin to dry enamel (P<0.05. There was no significant difference between the bond strength of dentin bonding to moist and dry enamel. In addition bond strength of dentin bonding to wet enamel was not significantly different from unfilled resin to dry enamel. Conclusion: Based on the findings of this study, it is suggested that enamel surface should remain slightly moist after etching before bonding with single bond but when using unfilled resin, the

Influence of previous acid etching on bond strength of universal adhesives to enamel and dentin.

Science.gov (United States)

Torres, Carlos Rocha Gomes; Zanatta, Rayssa Ferreira; Silva, Tatiane Josefa; Huhtala, Maria Filomena Rocha Lima; Borges, Alessandra Bühler

2017-01-01

The objective of this study was to evaluate the effect of acid pretreatment on the bond strength of composite resin bonded to enamel and dentin with 2 different universal self-etching adhesives. The null hypothesis was that the acid treatment performed prior to adhesive application would not significantly change the bond strength to enamel or dentin for either universal adhesive tested. A sample of 112 bovine incisors were selected and embedded in acrylic resin. Half were ground until a flat enamel surface was obtained, and the other half were polished until a 6 × 6-mm area of dentin was exposed, resulting into 2 groups (n = 56). The enamel and dentin groups were divided into 2 subgroups according to the adhesive system applied: Futurabond U or Scotchbond Universal. Each of these subgroups was divided into 2 additional subgroups (n = 14); 1 subgroup received phosphoric acid pretreatment, and 1 subgroup did not. The bond strength was assessed with a microtensile test. Data from enamel and dentin specimens were analyzed separately using 1-way analysis of variance. The acid pretreatment did not significantly change the bond strength of the adhesives tested, either to enamel (P = 0.4161) or to dentin (P = 0.4857). The acid etching pretreatment did not affect the bond strength to dentin and enamel when the tested universal multipurpose adhesive systems were used.

Physical, mechanical, and fire properties of oriented strandboard with fire retardant treated veneers

Science.gov (United States)

Nadir Ayrilmis; Zeki Candan; Robert White

2007-01-01

This study evaluated physical, mechanical and fire properties of oriented strand boards (OSB) covered with fire retardant treated veneers. The beech (Fagus orientalis Lipsky) veneers were treated with either monoammonium phosphate, diammonium phosphate, lime water or a borax/boric acid (1 : 1 by weight) mixture. Physical and mechanical properties of the specimens were...

Polymer Nanocarriers for Dentin Adhesion

Science.gov (United States)

Osorio, R.; Osorio, E.; Medina-Castillo, A.L.; Toledano, M.

2014-01-01

To obtain more durable adhesion to dentin, and to protect collagen fibrils of the dentin matrix from degradation, calcium- and phosphate-releasing particles have been incorporated into the dental adhesive procedure. The aim of the present study was to incorporate zinc-loaded polymeric nanocarriers into a dental adhesive system to facilitate inhibition of matrix metalloproteinases (MMPs)-mediated collagen degradation and to provide calcium ions for mineral deposition within the resin-dentin bonded interface. PolymP-nActive nanoparticles (nanoMyP) were zinc-loaded through 30-minute ZnCl2 immersion and tested for bioactivity by means of 7 days’ immersion in simulated body fluid solution (the Kokubo test). Zinc-loading and calcium phosphate depositions were examined by scanning and transmission electron microscopy, elemental analysis, and x-ray diffraction. Nanoparticles in ethanol solution infiltrated into phosphoric-acid-etched human dentin and Single Bond (3M/ESPE) were applied to determine whether the nanoparticles interfered with bonding. Debonded sticks were analyzed by scanning electron microscopy. A metalloproteinase collagen degradation assay was also performed in resin-infiltrated dentin with and without nanoparticles, measuring C-terminal telopeptide of type I collagen (ICTP) concentration in supernatants, after 4 wk of immersion in artificial saliva. Numerical data were analyzed by analysis of variance (ANOVA) and Student-Newman-Keuls multiple comparisons tests (p calcium regardless of zinc incorporation. Nanoparticles failed to infiltrate demineralized intertubular dentin and remained on top of the hybrid layer, without altering bond strength. Calcium and phosphorus were found covering nanoparticles at the hybrid layer, after 24 h. Nanoparticle application in etched dentin also reduced MMP-mediated collagen degradation. Tested nanoparticles may be incorporated into dental adhesive systems to provide the appropriate environment in which dentin MMP

The Effect of Veneer Layers on the Bending Shear Strength and Delamination of Laminated Veneer Lumber (LVL) from Oil Palm Trunk (OPT)

Science.gov (United States)

Jamaludin, M. A.; Nordin, K.; Bahari, S. A.; Ahmad, M.

2010-03-01

The aim of this study was to evaluate the effects of the number of veneer layers on the bending shear strength and delamination of Laminated Veneer Lumber (LVL) from oil palm trunk (OPT). Five (5), Six (6) and Seven (7) veneer layers of OPT LVL were manufactured. The dimension of the boards was 45 cm by 45 cm by 1.9 cm. The boards were hot pressed for 13 minutes at a pressure of 31 kgf per m2. Urea formaldehyde (UF) supplied by a local adhesive manufacturer was used as the binder for the boards. The bending shear tests consisted of the edgewise and flatwise tests, whereas the delamination test consisted of the cold and hot water boil tests. The preparation of the test specimens and tests set-up was in accordance to the Japanese Standards, JAS-1991 [1]. Six replications were used for each test. The results were analyzed by Analysis of Variance (ANOVA) using the Duncan's Multiple Range Test to test for significant differences. The results indicated that as the number of layers increased the strength also increased. All the boards passed the standard. The difference in strength between the different types of samples was significant at 95 percent confidence level. Bending shear failures were primarily in the veneers. It is possible to use the boards as light weight interior building and furniture components. Over the years, the supply of quality timber resources from the natural forest has decrease as the wood-based industry experienced rapid growth. The supply of rubberwood for the furniture industry is also decreasing as a result of increase latex price. Accordingly, OPT LVL can be an alternative or supplementary raw material for the wood-based industry.

Digital workflow for virtually designing and milling ceramic lithium disilicate veneers: a clinical report.

Science.gov (United States)

Zandinejad, A; Lin, W S; Atarodi, M; Abdel-Azim, T; Metz, M J; Morton, D

2015-01-01

Laminate veneers have been routinely used to restore and enhance the appearance of natural dentition. The traditional pathway for fabricating veneers consisted of making conventional polyvinyl siloxane impressions, producing stone casts, and fabricating final porcelain prostheses on stone dies. Pressed ceramics have successfully been used for laminate veneer fabrication for several years. Recently, digital computer-aided design/computer-aided manufacturing scanning has become commercially available to make a digital impression that is sent electronically to a dental laboratory or a chairside milling machine. However, technology has been developed to allow digital data acquisition in conjunction with electronically transmitted data that enables virtual design of restorations and milling at a remote production center. Following the aforementioned workflow will provide the opportunity to fabricate a physical cast-free restoration. This new technique has been reported recently for all-ceramic IPS e.max full-coverage pressed-ceramic restorations. However, laminate veneers are very delicate and technique-sensitive restorations when compared with all-ceramic full-coverage ones made from the same material. Complete digital design and fabrication of multiple consecutive laminate veneers seems to be very challenging. This clinical report presents the digital workflow for the virtual design and fabrication of multiple laminate veneers in a patient for enhancing the esthetics of his maxillary anterior teeth. A step-by-step process is presented with a discussion of the advantages and disadvantages of this novel technique. Additionally, the use of lithium disilicate ceramic as the material of choice and the rationale for such a decision is discussed.

The Possible Role of Dentin as a Piezoelectric Signal Generator by Determining the Elec-tromechanical Coupling Factor of Dentin

Directory of Open Access Journals (Sweden)

Atabak Shahidi

2011-08-01

Full Text Available Introduction: This article aimed at calculation of the electromechanical coupling factor of dentin which is an indicator of the effectiveness with which a piezoelectric material converts electrical en-ergy into mechanical energy, or vice versa. The hypothesis: The electro-mechanical coupling factor of dentin was determined in mode 11 and 33 by calculating the ratio of the produced electrical energy to the stored elastic energy in dentin under applied pressure. This study showed that the electromechanical coupling factor of dentin was affected by the direction of the applied force and the moisture content of dentin. Also dentin was a weak electromechanical energy converter which might be categorized as a piezoelectric pressure sensor.Evaluation of the hypothesis: Determination of the electrome-chanical coupling factor of dentin and its other piezoelectric constants is essential to investigate the biologic role of piezoelectricity in tooth.

Effect of functional monomers in all-in-one adhesive systems on formation of enamel/dentin acid-base resistant zone.

Science.gov (United States)

Nikaido, Toru; Ichikawa, Chiaki; Li, Na; Takagaki, Tomohiro; Sadr, Alireza; Yoshida, Yasuhiro; Suzuki, Kazuomi; Tagami, Junji

2011-01-01

This study aimed at evaluating the effect of functional monomers in all-in-one adhesive systems on formation of acid-base resistant zone (ABRZ) in enamel and dentin. Experimental adhesive systems containing one of three functional monomers; MDP, 3D-SR and 4-META were applied to enamel or dentin surface and light-cured. A universal resin composite was then placed. The specimens were subjected to a demineralizing solution (pH 4.5) and 5% NaClO for acid-base challenge and then observed by SEM. The ABRZ was clearly observed in both enamel and dentin interfaces. However, enamel ABRZ was thinner than dentin ABRZ in all adhesives. Morphology of the ABRZ was different between enamel and dentin, and also among the adhesives. Funnel-shaped erosion was observed only in the enamel specimen with the 4-META adhesive. The formation of enamel/dentin ABRZ was confirmed in all adhesives, but the morphology was influenced by the functional monomers.

Microshear bonding effectiveness of different dentin regions

Directory of Open Access Journals (Sweden)

Anelise F Montagner

2015-01-01

Full Text Available Aim: The aim of this in vitro study was to evaluate the influence of dentin surfaces with different tubule orientation on bond strength of a multimode adhesive system. Materials and Methods: Twenty human molars were selected and prepared in different ways in order to produce different dentin regions. The teeth were randomized (n = 5 according to the application modes of a multimode adhesive system (etch-and-rinse and self-etching and to the dentin region (occlusal and proximal - 1.5 mm depth from dentinoenamel junction. Cylindrical restorations were performed on dentin with a starch tube. The samples remained immersed in distilled water for 24 h and the microshear bond strength (μSBS test was performed. The μSBS values were expressed in MPa and analyzed with ANOVA and Tukey′s test (P < 0.05. Results: There was no significant difference in the bond strength values between the application modes of the adhesive system (P = 0.19; however, the dentin regions (P < 0.05 significantly affected the μSBS. The proximal dentin presented higher bond strength values than occlusal dentin. Conclusion: The dentin surfaces with different tubule orientation influenced the bonding effectiveness of the adhesive system tested.

No-waiting dentine self-etch concept-Merit or hype.

Science.gov (United States)

Huang, Xue-Qing; Pucci, César R; Luo, Tao; Breschi, Lorenzo; Pashley, David H; Niu, Li-Na; Tay, Franklin R

2017-07-01

A recently-launched universal adhesive, G-Premio Bond, provides clinicians with the alternative to use the self-etch technique for bonding to dentine without waiting for the adhesive to interact with the bonding substrate (no-waiting self-etch; Japanese brochure), or after leaving the adhesive undisturbed for 10s (10-s self-etch; international brochure). The present study was performed to examine in vitro performance of this new universal adhesive bonded to human coronal dentine using the two alternative self-etch modes. One hundred and ten specimens were bonded using two self-etch application modes and examined with or without thermomechanical cycling (10,000 thermal cycles and 240,000 mechanical cycles) to simulate one year of intraoral functioning. The bonded specimens were sectioned for microtensile bond testing, ultrastructural and nanoleakage examination using transmission electron microscopy. Changes in the composition of mineralised dentine after adhesive application were examined using Fourier transform infrared spectroscopy. Both reduced application time and thermomechanical cycling resulted in significantly lower bond strengths, thinner hybrid layers, and significantly more extensive nanoleakage after thermomechanical cycling. Using the conventional 10-s application time improved bonding performance when compared with the no-waiting self-etch technique. Nevertheless, nanoleakage was generally extensive under all testing parameters employed for examining the adhesive. Although sufficient bond strength to dentine may be achieved using the present universal adhesive in the no-waiting self-etch mode that does not require clinicians to wait prior to polymerisation of the adhesive, this self-etch concept requires further technological refinement before it can be recommended as a clinical technique. Although the surge for cutting application time to increase user friendliness remains the most frequently sought conduit for advancement of dentine bonding

Enamel and dentin bond strengths of a new self-etch adhesive system.

Science.gov (United States)

Walter, Ricardo; Swift, Edward J; Boushell, Lee W; Braswell, Krista

2011-12-01

statement of problem:  Self-etch adhesives typically are mildly acidic and therefore less effective than etch-and-rinse adhesives for bonding to enamel.   The purpose of this study was to evaluate the enamel and dentin shear bond strengths of a new two-step self-etch adhesive system, OptiBond XTR (Kerr Corporation, Orange, CA, USA).   The labial surfaces of 80 bovine teeth were ground to create flat, 600-grit enamel or dentin surfaces. Composite was bonded to enamel or dentin using the new two-step self-etch system or a three-step etch-and-rinse (OptiBond FL, Kerr), two-step self-etch (Clearfil SE Bond, Kuraray America, Houston, TX, USA), or one-step self-etch adhesive (Xeno IV, Dentsply Caulk, Milford, DE, USA). Following storage in water for 24 hours, shear bond strengths were determined using a universal testing machine. The enamel and dentin data sets were subjected to separate analysis of variance and Tukey's tests. Scanning electron microscopy was used to evaluate the effects of each system on enamel.   Mean shear bond strengths to enamel ranged from 18.1 MPa for Xeno IV to 41.0 MPa for OptiBond FL. On dentin, the means ranged from 33.3 MPa for OptiBond FL to 47.1 MPa for Clearfil SE Bond. OptiBond XTR performed as well as Clearfil SE Bond on dentin and as well as OptiBond FL on enamel. Field emission scanning electron microscope revealed that OptiBond XTR produced an enamel etch pattern that was less defined than that of OptiBond FL (37.5% phosphoric acid) but more defined than that of Clearfil SE Bond or Xeno IV.   The new two-step self-etch adhesive system formed excellent bonds to enamel and dentin in vitro. OptiBond XTR, a new two-step self-etch adhesive system, is a promising material for bonding to enamel as well as to dentin. © 2011 Wiley Periodicals, Inc.

Influence of Immediate Dentin Sealing on the Shear Bond Strength of Pressed Ceramic Luted to Dentin with Self-Etch Resin Cement

Directory of Open Access Journals (Sweden)

Robert Dalby

2012-01-01

Full Text Available Objectives. To examine the effect of immediate dentin sealing (IDS, with dentin bonding agents (DBAs applied to freshly cut dentin, on the shear bond strength of etched pressed ceramic luted to dentin with RelyX Unicem (RXU cement. Method. Eighty extracted noncarious third molars were ground flat to expose the occlusal dentin surfaces. The teeth were randomly allocated to five groups (A to E of sixteen teeth each. Groups A to D were allocated a dentin bonding agent (Optibond FL, One Coat Bond, Single Bond, or Go! that was applied to the dentin surface to mimic the clinical procedure of IDS. These specimen groups then had etched glass ceramic discs (Authentic luted to the sealed dentin surface using RXU. Group E (control had etched glass ceramic discs luted to the dentin surface (without a dentin bonding agent using RXU following the manufacturer’s instructions. All specimens were stored for one week in distilled water at room temperature and then shear stressed at a constant cross-head speed of 1 mm per minute until failure. Statistical analysis was performed by ANOVA followed by post hoc Tukey HSD method (0.05 in the SBS between the test groups (A–D or the control (group E. Conclusion. IDS using the dentin bonding agents tested does not statistically (>0.05 affect the shear bond strength of etched pressed ceramic luted to dentin with RXU when compared to the control.

Efficacy of Modified Bioactive Glass for Dentin Remineralization and Obstruction of Dentinal Tubules

Directory of Open Access Journals (Sweden)

Mahshid Saffarpour

2017-10-01

Full Text Available Objectives: This study assessed the efficacy of modified bioactive glass (MBG for dentin remineralization and obstruction of dentinal tubules.Materials and Methods: Thirty-six dentin discs were made from 20 third molars and were stored in 12% lactic acid solution for two weeks to induce demineralization. The samples were divided into three groups (n=12: 1- BG, 2- BG modified with 5% strontium (Sr and 3- BG modified with 10% Sr. After applying the BG, the samples were stored in artificial saliva for 7, 14 and 21 days. Attenuated Total Reflection-Fourier Transform Infrared Spectroscopy (ATR-FTIR, X-ray Diffraction (XRD analysis, Scanning Electron Microscopy (SEM, and Energy-Dispersive X-ray (EDX analysis were used to assess remineralization. Also, 6 dentin discs were divided into three groups of BG, BG modified with 5% Sr and BG modified with 10% Sr, to examine tubular occlusion. The discs were etched using 0.5M of EDTA for two minutes and were stored in artificial saliva for 7 days. Changes in dentin surface morphology were evaluated under SEM.Results: Group 3 showed high rates of remineralization at days 7 and 14, although the rate decreased at day 21. Group 2 exhibited high rates of remineralization at days 7, 14 and 21. Dentinal tubules were partially occluded by BG and BG modified with 5% Sr, while they were almost completely obstructed after the use of BG modified with 10% Sr.Conclusions: Strontium increases remineralization. Addition of 10% Sr to BG enhances apatite formation; however, the apatite dissolves over time. Addition of 5% Sr to BG stabilizes the apatite lattice and increases the remineralization.

Effect of various intermediate ceramic layers on the interfacial stability of zirconia core and veneering ceramics.

Science.gov (United States)

Yoon, Hyung-In; Yeo, In-Sung; Yi, Yang-Jin; Kim, Sung-Hun; Lee, Jai-Bong; Han, Jung-Suk

2015-01-01

The purposes of this study were to evaluate the effects of intermediate ceramics on the adhesion between the zirconia core and veneer ceramics. The polished surfaces of fully sintered Y-TZP blocks received three different treatments: (1) connector (C), (2) liner (L) or (3) wash layer (W). All the treated zirconia blocks were veneered with either (a) fluorapatite glass-ceramic (E) or (b) feldspathic porcelain (V) and divided into four groups (CE, CV, LE and WV). For the control group, the testing surfaces of metal blocks were veneered with feldspathic porcelain (VM). A half of the samples in each group (n = 21) were exposed to thermocycling, while the other half of the specimens were stored at room temperature under dry conditions. All specimens were subjected to the shear test and the failed surfaces were microscopically examined. The elemental distribution at the zirconia core/veneer interface was analyzed. The specimens in Groups CE and CV exhibited significantly greater mean bond strength values than those in Groups LE and WV, respectively (p ceramic substances into the zirconia surface. A glass-ceramic based connector is significantly more favorable to core/veneer adhesion than the other intermediate ceramics evaluated in the study. However, thermal cycling affected the bond strength at the core/veneer interface differently according to the intermediate ceramics.

Effect of provisional cements on shear bond strength of porcelain laminate veneers.

Science.gov (United States)

Altintas, Subutay Han; Tak, Onjen; Secilmis, Asli; Usumez, Aslihan

2011-08-01

The purpose of this study was to evaluate the effect of three provisional cements and two cleaning techniques on the final bond strength of porcelain laminate veneers. The occlusal third of the crowns of forty molar teeth were sectioned and embedded in autopolymerizing acrylic resin. Dentin surfaces were polished and specimens were randomly divided into four groups (n=10). Provisional restorations were fabricated and two provisional restorations were cemented onto each tooth. Restorations were fixed with one of three different provisional cements: eugenol-free provisional cement (Cavex), calcium hydroxide (Dycal), and light-cured provisional cement (Tempond Clear). Provisional restorations were removed with either a dental explorer and air-water spray, or a cleaning bur (Opticlean). In the control group, provisional restorations were not used on the surfaces of specimens. IPS Empress 2 ceramic discs were luted with a dual-cured resin cement (Panavia F). Shear bond strength was measured using a universal testing machine. Data were statistically analyzed by ANOVA, Tukey's HSD and Dunnett tests. Surfaces were examined by scanning electronic microscopy. Significant differences were found between the control group and both the light-cured provisional cement groups and the eugenol-free provisional cement-cleaning bur group (Pprovisional cement showed the lowest bond strength values. Selection of the provisional cement is an important factor in the ultimate bond strength of the final restoration. Calcium hydroxide provisional cement and cleaning with a dental explorer are advisable.

Matching the optical properties of direct esthetic dental restorative materials to those of human enamel and dentin

Science.gov (United States)

Ragain, James Carlton, Jr.

One of the goals of the restorative dentist is to restore the appearance of the natural dentition. Clinical matching of teeth and restorative materials are seldom accurate and shade selection techniques are subjective. The first specific aim of this research was to characterize the optical absorption and scattering that occurs within enamel, dentin, and composite resin and compomer restorative materials and to relate those phenomena to translucency and color. The second aim was to evaluate small color differences among composite restorative materials which would be detectable by humans. The last aim was to lay the foundation for developing an improved model of specifying layers of dental restorative materials in order to match the translucency and color to those of human enamel. The Kubelka-Munk theory was validated for enamel, dentin, and the restorative materials. These tissues and materials were then characterized in terms of their color parameters. Tooth cores were also characterized in terms of color space parameters. Human subjects were evaluated for their abilities to discriminate small color differences in the dental composite resin materials. The following conclusions were derived from this study: (1) Kubelka-Munk theory accurately predicts the diffuse reflectance spectra of enamel, dentin, and the direct esthetic dental restorative materials studied. (2) Scattering and absorption coefficients of the dental tissues and esthetic restorative materials can be directly calculated from diffuse reflectance measurements of a uniformly thick slab of tissue/material using black and white backings and the appropriate refractive index. (3) For tooth cores, there is a positive correlation between L* and b* and a negative correlation between L* and a*. (4) The range of translucency parameters for the restorative materials studied does not match those of enamel and dentin. (5) None of the shades of the dental composite resin restorative materials studied fit into the

Infra-red and Raman spectroscopic studies of infected and affected dentine

International Nuclear Information System (INIS)

Aminzadeh, A.; Aminzadeh, A.; Khosravy, K.

2002-01-01

Diagnosis of infected and affected dentine is an important factor in clinical restorative treatment of dentine. In this study, the IR and Raman spectra of the sound dentine, infected dentine and affected dentine are reported. The structure of infected dentine and affected dentine has been compared with the sound dentine and hydroxyapatite. It is shown while the infected dentine has lost its structure, the affected dentine has more or less a structure similar to the sound dentine. The molecular structure of collagen remains unchanged in both infected and affected dentine

Dentin-cement Interfacial Interaction

Science.gov (United States)

Atmeh, A.R.; Chong, E.Z.; Richard, G.; Festy, F.; Watson, T.F.

2012-01-01

The interfacial properties of a new calcium-silicate-based coronal restorative material (Biodentine™) and a glass-ionomer cement (GIC) with dentin have been studied by confocal laser scanning microscopy (CLSM), scanning electron microscopy (SEM), micro-Raman spectroscopy, and two-photon auto-fluorescence and second-harmonic-generation (SHG) imaging. Results indicate the formation of tag-like structures alongside an interfacial layer called the “mineral infiltration zone”, where the alkaline caustic effect of the calcium silicate cement’s hydration products degrades the collagenous component of the interfacial dentin. This degradation leads to the formation of a porous structure which facilitates the permeation of high concentrations of Ca2+, OH-, and CO32- ions, leading to increased mineralization in this region. Comparison of the dentin-restorative interfaces shows that there is a dentin-mineral infiltration with the Biodentine, whereas polyacrylic and tartaric acids and their salts characterize the penetration of the GIC. A new type of interfacial interaction, “the mineral infiltration zone”, is suggested for these calcium-silicate-based cements. PMID:22436906

Influence of cooling rate on residual stress profile in veneering ceramic: measurement by hole-drilling.

Science.gov (United States)

Mainjot, Amélie K; Schajer, Gary S; Vanheusden, Alain J; Sadoun, Michaël J

2011-09-01

The manufacture of dental crowns and bridges generates residual stresses within the veneering ceramic and framework during the cooling process. Residual stress is an important factor that control the mechanical behavior of restorations. Knowing the stress distribution within the veneering ceramic as a function of depth can help the understanding of failures, particularly chipping, a well-known problem with Yttria-tetragonal-zirconia-polycrystal based fixed partial dentures. The objective of this study is to investigate the cooling rate dependence of the stress profile in veneering ceramic layered on metal and zirconia frameworks. The hole-drilling method, often used for engineering measurements, was adapted for use with veneering ceramic. The stress profile was measured in bilayered disc samples 20 mm in diameter, with a 0.7 mm thick metal or Yttria-tetragonal-zirconia-polycrystal framework and a 1.5mm thick veneering ceramic. Three different cooling procedures were investigated. The magnitude of the stresses in the surface of the veneering ceramic was found to increase with cooling rate, while the interior stresses decreased. At the surface, compressive stresses were observed in all samples. In the interior, compressive stresses were observed in metal samples and tensile in zirconia samples. Cooling rate influences the magnitude of residual stresses. These can significantly influence the mechanical behavior of metal-and zirconia-based bilayered systems. The framework material influenced the nature of the interior stresses, with zirconia samples showing a less favorable stress profile than metal. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Kekuatan Rekat Restorasi Komposit Resin pada Permukaan Dentin dengan Sistem Adhesif Self-Etch dalam Berbagai Temperatur

Directory of Open Access Journals (Sweden)

Iin Sundari

2012-10-01

Full Text Available Single-step self-etch adhesive systems are the system that combine self etching primer and bonding agent into one step application. This system was developed as the effort to simplified in application prosedures and give a good bond strength of resin composites to dentin surface. The purpose of this study was to examine the bond strength of resin composites with two singlestep self-etch adhesives system (Xeno III and Clearfil Tri-S Bond to bovine dentin at temperature of adhesive 3ºC, 22ºC and 30ºC. Adhesive was applied to dentin surface (bovine insisivus mandibular dentin follow by resin composites bonded according to the manufacturer’s instructions. Tensile bond strength of 60 specimens were tested UTM (universal testing machine after 24 hours storage in aquadest at 37 ºC. The results were analyzed using ANOVA test followed by Tukey’s test (p< 0,05. The bond strength of Xeno III was significantly diffrent from that of Clearfil tri-S Bond, 0,66±0,271, 2,70±1,528, 0,23±0,104 versus 2,07±0,272, 4,77±0,689, 4,39±1,205 MPa at temperature of materials 3ºC, 22ºC and 30ºC respectively. The bond strength of two single- step adhesives system (Xeno III and Clearfil Tri-S Bond were highest at temperature 22ºC than other temperatures of materials.DOI: 10.14693/jdi.v15i3.34

Confocal Raman mapping of collagen cross-link and crystallinity of human dentin-enamel junction

Science.gov (United States)

Slimani, Amel; Nouioua, Fares; Desoutter, Alban; Levallois, Bernard; Cuisinier, Frédéric J. G.; Tassery, Hervé; Terrer, Elodie; Salehi, Hamideh

2017-08-01

The separation zone between enamel and dentin [dentin-enamel junction (DEJ)] with different properties in biomechanical composition has an important role in preventing crack propagation from enamel to dentin. The understanding of the chemical structure (inorganic and organic components), physical properties, and chemical composition of the human DEJ could benefit biomimetic materials in dentistry. Spatial distribution of calcium phosphate crystallinity and the collagen crosslinks near DEJ were studied using confocal Raman microscopy and calculated by different methods. To obtain collagen crosslinking, the ratio of two peaks 1660 cm-1 over 1690 cm-1 (amide I bands) is calculated. For crystallinity, the inverse full-width at half maximum of phosphate peak at 960 cm-1, and the ratio of two Raman peaks of phosphate at 960/950 cm-1 is provided. In conclusion, the study of chemical and physical properties of DEJ provides many benefits in the biomaterial field to improve the synthesis of dental materials in respect to the natural properties of human teeth. Confocal Raman microscopy as a powerful tool provides the molecular structure to identify the changes along DEJ and can be expanded for other mineralized tissues.

Long-term bond strength of adhesive systems applied to etched and deproteinized dentin

Directory of Open Access Journals (Sweden)

Ninoshka Uceda-Gómez

2007-12-01

Full Text Available The aim of this study was to evaluate the early and 12-month bond strength of two adhesive systems (Single Bond-SB and One Step-OS applied to demineralized dentin (WH and demineralized/NaOCl-treated dentin (H. Twenty flat dentin surfaces were exposed, etched, rinsed and slightly dried. For the H groups, a solution of 10% NaOCl was applied for 60 s, rinsed (15 s and slightly dried. The adhesives were applied according to the manufacturer's instructions and composite resin crowns were incrementally constructed. After 24 h (water-37ºC, the specimens was sectioned in order to obtain resin-dentin sticks (0.8 mm². The specimens were tested in microtensile (0.5 mm/min immediately (IM or after 12 months of water storage (12M. The data (MPa were subjected to ANOVA and Tukey's test (a=0.05. Only the main factors adhesive and time were significant (p=0.004 and p=0.003, respectively. SB (42.3±9.1 showed higher bond strengths than OS (33.6±11.6. The mean bond strength for IM-group (42.5±8.7 was statistically superior to 12M (33.3±11.8. The use of 10% NaOCl, after acid etching, did not improve the immediate and the long-term resin-dentin bond strength.

Effect of glutaraldehyde and ferric sulfate on shear bond strength of adhesives to primary dentin

Directory of Open Access Journals (Sweden)

Prabhakar A

2008-12-01

Full Text Available Aim: The present study was undertaken to evaluate the effect of alternative pulpotomy agents such as glutaraldehyde and ferric sulfate on the shear bond strength of self-etch adhesive systems to dentin of primary teeth. Materials and Methods: Eighty human primary molar teeth were sectioned in a mesiodistal direction and divided into experimental and control groups. Lingual dentin specimens in experimental groups were treated with glutaraldehyde and ferric sulfate. Buccal surfaces soaked in water served as control group. Each group was then divided into two groups based on the adhesive system used: Clearfil SE Bond and Adper Prompt L-Pop. A teflon mold was used to build the composite (Filtek Z-250 cylinders on the dentinal surface of all the specimens. Shear bond strength was tested for all the specimens with an Instron Universal Testing Machine. The failure mode analysis was performed with a Scanning Electron Microscope (SEM. Results: The results revealed that glutaraldehyde and ferric sulfate significantly reduced the shear bond strength of the tested adhesive systems to primary dentin. Clearfil SE Bond showed much higher shear bond strength than Adper Prompt L Pop to primary dentin. SEM analysis revealed a predominant cohesive failure mode for both adhesive systems. Conclusion: This study revealed that the pulpotomy medicaments glutaraldehyde and ferric sulfate adversely affected the bonding of self-etch adhesive systems to primary dentin.

Influence of thermal expansion mismatch on residual stress profile in veneering ceramic layered on zirconia: Measurement by hole-drilling.

Science.gov (United States)

Mainjot, Amélie K; Najjar, Achref; Jakubowicz-Kohen, Boris D; Sadoun, Michaël J

2015-09-01

Mismatch in thermal expansion coefficient between core and veneering ceramic (Δα=αcore-αveneer, ppm/°C) is reported as a crucial parameter influencing veneer fractures with Yttria-tetragonal-zirconia-polycrystal (Y-TZP) prostheses, which still constitutes a misunderstood problem. However, the common positive Δα concept remains empirical. The objective of this study is to investigate the Δα dependence of residual stress profiles in veneering ceramic layered on Y-TZP frameworks. The stress profile was measured with the hole-drilling method in bilayered disc samples of 20mm diameter with a 0.7mm thick Y-TZP framework and a 1.5mm thick veneer layer. 3 commercial and 4 experimental veneering ceramics (n=3 per group) were used to obtain different Δα varying from -1.3ppm/°C to +3.2ppm/°C, which were determined by dilatometric analyses. Veneer fractures were observed in samples with Δα≥+2.3 or ≤-0.3ppm/°C. Residual stress profiles measured in other groups showed compressive stresses in the surface, these stresses decreasing with depth and then becoming more compressive again near the interface. Small Δα variations were shown to induce significant changes in residual stress profiles. Compressive stress near the framework was found to decrease inversely to Δα. Veneer CTE close to Y-TZP (+0.2ppm/°C Δα) gived the most favorable stress profile. Yet, near the framework, Δα-induced residual stress varied inversely to predictions. This could be explained by the hypothesis of structural changes occurrence within the Y-TZP surface. Consequently, the optimum Δα value cannot be determined before understanding Y-TZP's particular behavior when veneered. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Elemental and chemical characterization of dolphin enamel and dentine using X-ray and Raman microanalyzes (Cetacea: Delphinoidea and Inioidea).

Science.gov (United States)

Loch, Carolina; Swain, Michael V; Fraser, Sara J; Gordon, Keith C; Kieser, Jules A; Fordyce, R Ewan

2014-01-01

Dolphins show increased tooth number and simplified tooth shape compared to most mammals, together with a simpler ultrastructural organization and less demanding biomechanical function. However, it is unknown if these factors are also reflected in the chemical composition of their teeth. Here, the bulk chemical composition and elemental distribution in enamel and dentine of extant dolphins were characterized and interpreted using X-ray and spectroscopy techniques. Teeth of 10 species of Delphinida were analyzed by WDX, EDX and Raman spectroscopy. For most of the species sampled, the mineral content was higher in enamel than in dentine, increasing from inner towards outer enamel. The transition from dentine to enamel was marked by an increase in concentration of the major components Ca and P, but also in Na and Cl. Mg decreased from dentine to enamel. Concentrations of Sr and F were often low and below detection limits, but F peaked at the outer enamel region for some species. Raman spectroscopy analyzes showed characteristics similar to carbonated hydroxyapatite, with the strongest peak for the phosphate PO4(3-) stretching mode at 960-961cm(-1). Dentine samples revealed a higher diversity of peaks representative of organic components and proteins than enamel. The similar distribution pattern and small variation in average concentration of major and minor elements in dentine and enamel of dolphins suggest that they are subject to strong physiological control. A clear trend of the elemental variations for all dolphin species sampled suggests that the general pattern of tooth chemistry is conserved among the Mammalia. Copyright © 2013 Elsevier Inc. All rights reserved.

Tensile and bending fatigue of the adhesive interface to dentin.

Science.gov (United States)

Belli, Renan; Baratieri, Luiz Narciso; Braem, Marc; Petschelt, Anselm; Lohbauer, Ulrich

2010-12-01

The aim of this study was to evaluate the fatigue limits of the dentin-composite interfaces established either with an etch-and-rinse or an one-step self-etch adhesive systems under tensile and bending configurations. Flat specimens (1.2 mm×5 mm×35 mm) were prepared using a plexiglass mold where dentin sections from human third molars were bonded to a resin composite, exhibiting the interface centrally located. Syntac Classic and G-Bond were used as adhesives and applied according to the manufacturer's instructions. The fluorochrome Rhodamine B was added to the adhesives to allow for fractographic evaluation. Tensile strength was measured in an universal testing machine and the bending strength (n=15) in a Flex machine (Flex, University of Antwerp, Belgium), respectively. Tensile (TFL) and bending fatigue limits (BFL) (n=25) were determined under wet conditions for 10(4) cycles following a staircase approach. Interface morphology and fracture mechanisms were observed using light, confocal laser scanning and scanning electron microscopy. Statistical analysis was performed using three-way ANOVA (mod LSD test, pTensile and bending characteristic strengths at 63.2% failure probability for Syntac were 23.8 MPa and 71.5 MPa, and 24.7 MPa and 72.3 MPa for G-Bond, respectively. Regarding the applied methods, no significant differences were detected between adhesives. However, fatigue limits for G-Bond (TFL=5.9 MPa; BFL=36.2 MPa) were significantly reduced when compared to Syntac (TFL=12.6 MPa; BFL=49.7 MPa). Fracture modes of Syntac were generally of adhesive nature, between the adhesive resin and dentin, while G-Bond showed fracture planes involving the adhesive-dentin interface and the adhesive resin. Cyclic loading under tensile and bending configurations led to a significant strength degradation, with a more pronounced fatigue limit decrease for G-Bond. The greater decrease in fracture strength was observed in the tensile configuration. Copyright © 2010 Academy of

Straight studs from southern pine veneer cores and cordwood

Science.gov (United States)

Peter Koch

1968-01-01

An economically feasible system has been developed for converting southern pine veneer cores into straight 8-foot studs (2). Prototype studs - two per core - were 100 percent SPIB stud grade and better.

Piecewise-Constant-Model-Based Interior Tomography Applied to Dentin Tubules

Directory of Open Access Journals (Sweden)

Peng He

2013-01-01

Full Text Available Dentin is a hierarchically structured biomineralized composite material, and dentin’s tubules are difficult to study in situ. Nano-CT provides the requisite resolution, but the field of view typically contains only a few tubules. Using a plate-like specimen allows reconstruction of a volume containing specific tubules from a number of truncated projections typically collected over an angular range of about 140°, which is practically accessible. Classical computed tomography (CT theory cannot exactly reconstruct an object only from truncated projections, needless to say a limited angular range. Recently, interior tomography was developed to reconstruct a region-of-interest (ROI from truncated data in a theoretically exact fashion via the total variation (TV minimization under the condition that the ROI is piecewise constant. In this paper, we employ a TV minimization interior tomography algorithm to reconstruct interior microstructures in dentin from truncated projections over a limited angular range. Compared to the filtered backprojection (FBP reconstruction, our reconstruction method reduces noise and suppresses artifacts. Volume rendering confirms the merits of our method in terms of preserving the interior microstructure of the dentin specimen.

Indirect veneer treatment of anterior maxillary teeth with enamel hypoplasia

Directory of Open Access Journals (Sweden)

Devi Eka Juniarti

2010-09-01

Full Text Available Background: Nowadays, aesthetic rehabilitation becomes a necessity. It is affected by patient’s background, especially career, social and economic status. The aesthetic abnormality of anterior teeth i.e discoloration, malposition and malformation can affect patient’s appearance, especially during smile. These dental abnormalities, as a result, can decrease patient’s performance. Dental malformation, for instance, can be caused by developmental tooth defect, such as enamel hypoplasia. Enamel hypoplasia is a developmental defect caused by the lack of matrix amount which leads to thin and porous enamel. Enamel hypoplasia can also be caused by matrix calcification disturbance starting from the formation and development of enamel matrix causing defect and permanent changes which can occur on one or more tooth. Purpose: The aim of the study is to improve dental discoloration and tooth surface texture on anterior maxillary teeth with enamel hypoplasia by using indirect veneer with porcelain material. Case: A 20 years-old woman with enamel hypoplasia came to the Dental Hospital, Faculty of Dentistry Airlangga University. The patient wanted to improve her anterior maxillary teeth. It is clinically known that there were some opaque white spots (chalky spotted and porous on anterior teeth’s surface. Case management: Indirect veneer with porcelain material had been chosen as a restoration treatment which has excellent aesthetics and strength, and did not cause gingival irritation. As a result, the treatment could improve the confidence of the patient, and could also make their function normal. Conclusion: Indirect veneer is an effective treatment, which can improve patient’s appearance and self confidence.Latar belakang: Saat ini perbaikan estetik menjadi suatu kebutuhan. Kebutuhan akan estetik dipengaruhi latar belakang penderita, terutama karir, status sosial dan ekonomi. Hal ini disebabkan, kelainan estetik seperti diskolorasi, malposisi

Secondary overprinting of S-Se-Te signatures in the Earth's mantle: Implications for the Late Veneer

Science.gov (United States)

Koenig, S.; Luguet, A.; Lorand, J.; Pearson, D.

2013-12-01

Sulphur, Selenium and Tellurium are both chalcophile and highly siderophile elements (HSE) with near-chondritic ratios and absolute abundances in the terrestrial mantle that exceed those predicted by core-mantle differentiation[1]. These 'excess' HSE abundances have been attributed to addition of ca. 0.5% of chondrite-like material that hit the Earth in its accretionary stage between 4 to 3.8 billion years ago after core-mantle differentiation (Late Veneer[2]). Therefore, like other HSE, S, Se and Te are considered potential tracers for the composition of the Late Veneer, provided that their bulk silicate Earth abundances are properly constrained. In contrast to ca. 250 ppm S, Se and Te are ultra-trace elements in the terrestrial mantle. Like all HSE, they are furthermore controlled by base metal sulphides (BMS) and micrometric platinum group minerals (PGMs)[3]. This strong control exerted by the host mineralogy and petrology on the S-Se-Te systematics at both the micro-scale and the whole-rock scale makes detailed mineralogical and petrological studies of BMS and PGM a pre-requisite to fully understand and accurately interpret the whole-rock signatures. Here we combine in-situ sulphide data and detailed mineralogical observations with whole-rock S-Se-Te-HSE signatures of both lherzolites and harburgites from different geodynamic settings. We demonstrate that the near-chondritic Se and Te signature of 'fertile' mantle rocks (Se/Te ≈9×5) is not a primitive signature of the Earth's mantle, but rather reflects strong enrichment in metasomatic HSE host phases, which erased previous pristine signatures. Consequently, current attempts to identify a potential Late Veneer composition are seriously flawed because, neither refertilisation/metasomatism nor true melt depletion (e.g. harzburgitic residues) have been taken into account for the Primitive Upper Mantle composition estimate[4]. Our combined whole rock and in-situ sulphide data indicate a refertilisation trend

Bonding durability of a self-etching primer system to normal and caries-affected dentin under hydrostatic pulpal pressure in vitro.

Science.gov (United States)

Nakajima, Masatoshi; Hosaka, Keiichi; Yamauti, Monica; Foxton, Richard M; Tagami, Junji

2006-06-01

To evaluate the bonding durability of a self-etching primer system to normal and caries-affected dentin under hydrostatic pulpal pressure. 18 extracted human molars with occlusal caries were used. Their occlusal dentin surfaces were ground flat to expose normal and caries-affected dentin using #600 SiC paper under running water. Clearfil SE Bond was placed on the dentin surface including the caries-affected dentin according to the manufacturer's instructions and then the crowns were built up with resin composite (Clearfil AP-X) under either a pulpal pressure of 15 cm H2O or none (control). The bonded specimens were stored in 100% humidity for 1 day (control) or for 1 week and 1 month with hydrostatic pulpal pressure. After storage, the specimens were serially sectioned into 0.7 mm-thick slabs and trimmed to an hour-glass shape with a 1 mm2 cross-section, isolated by normal or caries-affected dentin, and then subjected to the micro-tensile bond test. Data were analyzed by two-way ANOVA and Tukey's test (PHydrostatic pulpal pressure significantly reduced the bond strength to normal dentin after 1-month storage (P< 0.05), but did not affect the bond strength to caries-affected dentin.

Effect of caries-affected dentin on one-step universal and multi-step etch-and-rinse adhesives’ bond strength

Directory of Open Access Journals (Sweden)

Clecila MÜLLER

2017-10-01

Full Text Available Abstract Objective To evaluate the influence of caries-affected dentin on bond strength of a universal one-step and a multi-step etch-and-rinse adhesive system. Material and method Enamel of 60 third human molars with and without caries was removed to expose dentin. The teeth were randomly assigned to six groups: Single Bond Universal (3M ESPE, St. Paul, MN, USA in etch-and-rinse and in self-etch mode and Prime & Bond NT (Dentsply Co, Konstanz, Germany, all on sound and caries-affected dentin. Smear layer of the 30 sound dentin specimens was standardized by polishing with 600-grit SiC paper under water cooling. Residual infected dentin of the 30 caries-affected specimens was removed with a number 4 CA carbide bur until no caries smooth tissue was detectable by tactile-visual inspection. Cylinders of a light cured composite resin (Filtek Z350 XT, 3M ESPE were built up using starch tubes and microshear test was performed until failure. The data was analyzed by one-way ANOVA and Tukey’s post hoc test. Result Significant differences in microshear bond strength (μSBS were observed for the caries-affected groups, but not for sound dentin. The μSBS of Single Bond Universal were not influenced by the application protocol on sound dentin, however they were lower in the caries-affected group with both application protocols. The μSBS for Prime & Bond NT was not influenced by the dentin conditions. Conclusion Caries-affected dentin decrease in bond strength of Single Bond Universal in comparison to sound dentin. The bond strength of Prime & Bond NT was not altered by substrate conditions.

Interfacial Adhesion and Damping Characteristics of Laminated Veneer Lumber Intercalated with Rubber Sheets

Directory of Open Access Journals (Sweden)

Jingquan Han

2016-06-01

Full Text Available Laminated wood veneer lumber intercalated with rubber sheets (LLVR was fabricated using a layered adhesive system composed of polyaryl polymethylene isocyanate (PAPI for wood-rubber inter-bonding and phenol formaldehyde (PF resin to glue the wood veneers. The optimized manufacturing process (chloroprene rubber: CR; PAPI: 80 g/m2; PF: 200 g/m2; and silane: 9.0 wt.% was determined. The process as developed was then utilized to fabricate nine-ply LLVRs of five balanced constructions with two or three CR laminates used as various layers. The physico-mechanical properties of the LLVRs were evaluated, and the results showed that LLVRs had strong shear strength, sound dimensional stability, decent bending strength, and favorable toughening and buffering performances. The newly developed product is an interesting potential alternative to traditional laminated veneer lumber or plywood.

Minimally invasive restoration of a maxillary central incisor with a partial veneer.

Science.gov (United States)

Horvath, Sebastian; Schulz, Claus-Peter

2012-01-01

Minimally invasive treatment modalities allow for the preservation of sound tooth substance. However, by limiting the preparation to the extent of a defect, the transition between restoration and natural tooth may be moved to more visible areas. The materials available for the restoration of a limited defect in the anterior area are either resin composite materials or porcelain. A patient was presented who asked for the replacement of a discolored filling on the maxillary right central incisor. Tooth preparation was limited to the extent of the old filling, and a porcelain partial veneer restoration was fabricated. Despite the horizontal finish line in the middle of the clinical crown, a result could be achieved that was regarded as a success by the patient. This type of restoration proves to be a suitable alternative to direct composite restorations in the anterior area for the reconstruction of a limited defect, eg, due to a dental trauma.

[The effect of core veneer thickness ratio on the flexural strength of diatomite-based dental ceramic].

Science.gov (United States)

Jiang, Jie; Zhang, Xin; Gao, Mei-qin; Zhang, Fei-min; Lu, Xiao-li

2015-06-01

To evaluate the effect of different core veneer thickness ratios on the flexural strength and failure mode of bilayered diatomite-based dental ceramics. Diatomite-based dental ceramics blocks (16 mm×5.4 mm×1 mm) were sintered with different thickness of veneer porcelains: 0 mm (group A), 0.6 mm (group B), 0.8 mm (group C) and 1.0 mm (group D). Flexural strength was detected and scanning electron microscope was used to observe the interface microstructure. Statistical analysis was performed using SPSS 17.0 software package. With the increase of the thickness of the veneer porcelain, flexural strength of group C showed highest flexural strength up to (277.24±5.47) MPa. Different core veneer thickness ratios can significantly influence the flexural strength of bilayered diatomite-based dental ceramics. Supported by Science and Technology Projects of Nantong City (HS2013010).

Reliability and failure modes of implant-supported zirconium-oxide fixed dental prostheses related to veneering techniques

Science.gov (United States)

Baldassarri, Marta; Zhang, Yu; Thompson, Van P.; Rekow, Elizabeth D.; Stappert, Christian F. J.

2011-01-01

Summary Objectives To compare fatigue failure modes and reliability of hand-veneered and over-pressed implant-supported three-unit zirconium-oxide fixed-dental-prostheses(FDPs). Methods Sixty-four custom-made zirconium-oxide abutments (n=32/group) and thirty-two zirconium-oxide FDP-frameworks were CAD/CAM manufactured. Frameworks were veneered with hand-built up or over-pressed porcelain (n=16/group). Step-stress-accelerated-life-testing (SSALT) was performed in water applying a distributed contact load at the buccal cusp-pontic-area. Post failure examinations were carried out using optical (polarized-reflected-light) and scanning electron microscopy (SEM) to visualize crack propagation and failure modes. Reliability was compared using cumulative-damage step-stress analysis (Alta-7-Pro, Reliasoft). Results Crack propagation was observed in the veneering porcelain during fatigue. The majority of zirconium-oxide FDPs demonstrated porcelain chipping as the dominant failure mode. Nevertheless, fracture of the zirconium-oxide frameworks was also observed. Over-pressed FDPs failed earlier at a mean failure load of 696 ± 149 N relative to hand-veneered at 882 ± 61 N (profile I). Weibull-stress-number of cycles-unreliability-curves were generated. The reliability (2-sided at 90% confidence bounds) for a 400N load at 100K cycles indicated values of 0.84 (0.98-0.24) for the hand-veneered FDPs and 0.50 (0.82-0.09) for their over-pressed counterparts. Conclusions Both zirconium-oxide FDP systems were resistant under accelerated-life-time-testing. Over-pressed specimens were more susceptible to fatigue loading with earlier veneer chipping. PMID:21557985

Degradation of Multimode Adhesive System Bond Strength to Artificial Caries-Affected Dentin Due to Water Storage.

Science.gov (United States)

Follak, A C; Miotti, L L; Lenzi, T L; Rocha, R O; Soares, F Z

The purpose of this study was to evaluate the influence of water storage on bond strength of multimode adhesive systems to artificially induced caries-affected dentin. One hundred twelve sound bovine incisors were randomly assigned to 16 groups (n=7) according to the dentin condition (sound; SND, artificially induced caries-affected dentin; CAD, cariogenic challenge by pH cycling for 14 days); the adhesive system (SU, Scotchbond Universal Adhesive; AB, All-Bond Universal; PB, Prime & Bond Elect; SB, Adper Single Bond 2; and CS, Clearfil SE Bond), and the etching strategy (etch-and-rinse and self-etch). All adhesive systems were applied under manufacturer's instructions to flat dentin surfaces, and a composite block was built up on each dentin surface. After 24 hours of water storage, the specimens were sectioned into stick-shaped specimens (0.8 mm 2 ) and submitted to a microtensile test immediately (24 hours) or after six months of water storage. Bond strength data (MPa) were analyzed using three-way repeated-measures analysis of variance and post hoc Tukey test (α=5%), considering each substrate separately (SND and CAD). The etching strategy did not influence the bond strength of multimode adhesives, irrespective of the dentin condition. Water storage only reduced significantly the bond strength to CAD. The degradation of bond strength due to water storage was more pronounced in CAD, regardless of the etching strategy.

Dentin and pulp sense cold stimulus.

Science.gov (United States)

Tokuda, Masayuki; Tatsuyama, Shoko; Fujisawa, Mari; Morimoto-Yamashita, Yoko; Kawakami, Yoshiko; Shibukawa, Yoshiyuki; Torii, Mistuso

2015-05-01

Dentin hypersensitivity is a common symptom, and recent convergent evidences have reported transient receptor potential (TRP) channels in odontoblasts act as mechanical and thermal molecular sensor, which detect stimulation applied on the exposed dentin surface, to drive multiple odontoblastic cellular functions, such as sensory transduction and/or dentin formation. In the present study, we confirmed expression of TRP melastatin subfamily member-8 (TRPM8) channels in primary cultured cells derived from human dental pulp cells (HPCs) and mouse odontoblast-lineage cells (OLCs) as well as in dentin matrix protein-1 (DMP-1) and dentin sialoprotein (DSP) positive acutely isolated rat odontoblasts from dental pulp tissue slice culture by immunohistochemical analyses. In addition, we detected TRPM8 channel expression on HPCs and OLCs by RT-PCR and Western blotting analyses. These results indicated that both odontoblasts and dental pulp cells express TRPM8 channels in rat, mouse and human, and therefore we hypothesize they may contribute as cold sensor in tooth. Copyright © 2015 Elsevier Ltd. All rights reserved.

Additively Manufactured Titanium and Cobalt-Chromium Implant Frameworks: Fit and Effect of Ceramic Veneering.

Science.gov (United States)

Svanborg, Per; Eliasson, Alf; Stenport, Victoria

The purpose of this study was to evaluate the fit of additively manufactured cobalt-chromium and titanium and CNC-milled titanium frameworks before and after ceramic veneering. Ten stone casts simulating an edentulous maxilla provided with six abutment analogs were produced. For each stone cast, one additively manufactured cobalt-chromium framework (AM CoCr) and one titanium framework (AM Ti) were fabricated. The fit was analyzed with a coordinate measuring machine in three dimensions (x, y, and z axes) using best-fit virtual matching of center point coordinates, before and after ceramic veneering. CNC-milled titanium frameworks (CNC Ti) and earlier results from CNC-milled cobalt-chromium frameworks (CNC CoCr) were used for comparison. All frameworks presented minor misfit before and after veneering in the horizontal plane (x- and y-axes) between 2.9 and 13.5 μm and in the vertical plane (z-axis) between 1.6 and 5.4 μm. Ceramic veneering affected the fit of all groups of frameworks. Both AM Ti and AM CoCr presented significantly smaller distortion in the vertical plane compared with the CNC-milled frameworks. Implant-supported frameworks can be produced in either Ti or CoCr using either CNC milling or additive manufacturing with a fit well within the range of 20 μm in the horizontal plane and 10 μm in the vertical plane. The fit of frameworks of both materials and production techniques are affected by the ceramic veneering procedure to a small extent.

Adhesion of multimode adhesives to enamel and dentin after one year of water storage.

Science.gov (United States)

Vermelho, Paulo Moreira; Reis, André Figueiredo; Ambrosano, Glaucia Maria Bovi; Giannini, Marcelo

2017-06-01

This study aimed to evaluate the ultramorphological characteristics of tooth-resin interfaces and the bond strength (BS) of multimode adhesive systems to enamel and dentin. Multimode adhesives (Scotchbond Universal (SBU) and All-Bond Universal) were tested in both self-etch and etch-and-rinse modes and compared to control groups (Optibond FL and Clearfil SE Bond (CSB)). Adhesives were applied to human molars and composite blocks were incrementally built up. Teeth were sectioned to obtain specimens for microtensile BS and TEM analysis. Specimens were tested after storage for either 24 h or 1 year. SEM analyses were performed to classify the failure pattern of beam specimens after BS testing. Etching increased the enamel BS of multimode adhesives; however, BS decreased after storage for 1 year. No significant differences in dentin BS were noted between multimode and control in either evaluation period. Storage for 1 year only reduced the dentin BS for SBU in self-etch mode. TEM analysis identified hybridization and interaction zones in dentin and enamel for all adhesives. Silver impregnation was detected on dentin-resin interfaces after storage of specimens for 1 year only with the SBU and CSB. Storage for 1 year reduced enamel BS when adhesives are applied on etched surface; however, BS of multimode adhesives did not differ from those of the control group. In dentin, no significant difference was noted between the multimode and control group adhesives, regardless of etching mode. In general, multimode adhesives showed similar behavior when compared to traditional adhesive techniques. Multimode adhesives are one-step self-etching adhesives that can also be used after enamel/dentin phosphoric acid etching, but each product may work better in specific conditions.

EFFECTS OF PRESS PRESSURE ON GLUE LINE THICKNESS AND PROPERTIES OF LAMINATED VENEER LUMBER GLUED WITH MELAMINE UREA FORMALDEHYDE ADHESIVE

Directory of Open Access Journals (Sweden)

Ramazan Kurt,

2012-07-01

Full Text Available Laminated veneer lumbers (LVLs were manufactured from half-round sliced I-214 hybrid poplar clone veneers with MUF adhesives using press pressures ranging from 2.5 to 15 kg cm-2. The results showed that the press pressures affected the glue line thickness (GLT and the physical and mechanical properties of the LVLs. Higher specific gravity (SG and mechanical properties, but lower GLT were developed as a result of using higher press pressures. The optimum press pressure was found to be 10 kg cm-2 in relation to GLT, SG, and mechanical properties. Significant linear correlations were found between GLT and mechanical properties. GLT can be used to determine the quality of wood bonding and may become a valuable tool for this purpose. Reliable data on the optimum GLT and press pressures can be used to design safe wood bonding applications in all aspects of wood based composites, as well as wood constructions when appropriate techniques are adopted to measure the GLT.

Scanning electron microscopic observations of fibrous structure of cemento-dentinal junction in healthy teeth.

Science.gov (United States)

Pratebha, B; Jaikumar, N D; Sudhakar, R

2014-01-01

The cemento-dentinal junction (CDJ) is a structural and biologic link between cementum and dentin present in the roots of teeth. Conflicting reports about the origin, structure and composition of this layer are present in literature. The width of this junctional tissue is reported to be about 2-4 μm with adhesion of cementum and dentin by proteoglycans and by collagen fiber intermingling. The objective of this study is to observe and report the fibrous architecture of the CDJ of healthy tooth roots. A total of 15 healthy teeth samples were collected, sectioned into halves, demineralized in 5% ethylenediaminetetraacetic acid, processed using NaOH maceration technique and observed under a scanning electron microscope. The CDJ appeared to be a fibril poor groove with a width of 2-4 µm. Few areas of collagen fiber intermingling could be appreciated. A detailed observation of these tissues has been presented.

Dentinal tubules revealed with X-ray tensor tomography.

Science.gov (United States)

Jud, Christoph; Schaff, Florian; Zanette, Irene; Wolf, Johannes; Fehringer, Andreas; Pfeiffer, Franz

2016-09-01

Dentin is a mineralized material making up most of the tooth bulk. A system of microtubules, so called dentinal tubules, transverses it radially from the pulp chamber to the outside. This highly oriented structure leads to anisotropic mechanical properties directly connected to the tubules orientation and density: the ultimate tensile strength as well as the fracture toughness and the shear strength are largest perpendicular to dentinal tubules. Consequently, the fatigue strength depends on the direction of dentinal tubules, too. However, none of the existing techniques used to investigate teeth provide access to orientation and density of dentinal tubules for an entire specimen in a non-destructive way. In this paper, we measure a third molar human tooth both with conventional micro-CT and X-ray tensor tomography (XTT). While the achievable resolution in micro-CT is too low to directly resolve the dentinal tubules, we provide strong evidence that the direction and density of dentinal tubules can be indirectly measured by XTT, which exploits small-angle X-ray scattering to retrieve a 3D map of scattering tensors. We show that the mean directions of scattering structures correlate to the orientation of dentinal tubules and that the mean effective scattering strength provides an estimation of the relative density of dentinal tubules. Thus, this method could be applied to investigate the connection between tubule orientation and fatigue or tensile properties of teeth for a full sample without cutting one, non-representative peace of tooth out of the full sample. Copyright © 2016 The Academy of Dental Materials. All rights reserved.

Investigation on the Tribological Behavior and Wear Mechanism of Five Different Veneering Porcelains.

Directory of Open Access Journals (Sweden)

Jie Min

Full Text Available The primary aim of this research was to investigate the wear behavior and wear mechanism of five different veneering porcelains.Five kinds of veneering porcelains were selected in this research. The surface microhardness of all the samples was measured with a microhardness tester. Wear tests were performed on a ball-on-flat PLINT fretting wear machine, with lubrication of artificial saliva at 37°C. The friction coefficients were recorded by the testing system. The microstructure features, wear volume, and damage morphologies were recorded and analyzed with a confocal laser scanning microscope and a scanning electron microscope. The wear mechanism was then elucidated.The friction coefficients of the five veneering porcelains differ significantly. No significant correlation between hardness and wear volume was found for these veneering porcelains. Under lubrication of artificial saliva, the porcelain with higher leucite crystal content exhibited greater wear resistance. Additionally, leucite crystal size and distribution in glass matrix influenced wear behavior. The wear mechanisms for these porcelains were similar: abrasive wear dominates the early stage, whereas delamination was the main damage mode at the later stage. Furthermore, delamination was more prominent for porcelains with larger crystal sizes.Wear compatibility between porcelain and natural teeth is important for dental restorative materials. Investigation on crystal content, size, and distribution in glass matrix can provide insight for the selection of dental porcelains in clinical settings.

A Step-by-Step Conservative Approach for CAD-CAM Laminate Veneers

Directory of Open Access Journals (Sweden)

Gerardo Durán Ojeda

2017-01-01

Full Text Available The use of CAD/CAM technology has allowed the fabrication of ceramic restorations efficiently and with predictable results. Lithium disilicate is a type of glass ceramic material that can be used for the elaboration of laminate veneers, being monolithic restorations which require characterization through a covering ceramic in order to achieve acceptable esthetic results. The next case report shows a predictable clinical protocol for the rehabilitation of the anterior teeth through the preparation of CAD/CAM veneers (e.max CAD, Ivoclar Vivadent, Liechtenstein which have been characterized by a nanofluorapatite ceramic (e.max Ceram, Ivoclar Vivadent, Liechtenstein through the layering technique.

Evaluation of Different Dentin Bonding Agents Accompanied with Composite Coronal Barrier

Directory of Open Access Journals (Sweden)

Zahed Mohammadi

2015-06-01

Full Text Available Introduction: The purpose of this study was to evaluate the sealing ability of dentin bonding agents in root canals obturated with gutta-percha and MTA. Methods: Forty-five single rooted human premolar teeth were decoronated so that remaining root portions were 12 mm in length. The samples were divided randomly into three experimental (n=13 and two control groups (n=3. All teeth were instrumented up to #40 K-file using step-back technique. The roots were obturated with gutta-percha/AH26 and MTA for 5 and 3 mm, respectively. Excite, Clearfil SE Bond, and iBond were applied for experimental groups and then 2mm was filled with composite Filtek Z250. The roots in the controls were merely instrumented and obturated. Two coats of nail varnish were applied on the surface of the teeth in the experimental and positive groups, except 2 mm around the apical foramen and coronal surfaces. In the negative control, the surfaces were completely covered by two layers of nail varnish. After thermocycling, the roots mounted in plastic caps of tubes containing BHI medium and inoculated coronally with Enterococcus faecalis. The data were statistically analyzed using Fisher's exact and Kaplan-Meier survival Analysis. Results: There were no statistically significant differences between three experimental groups regarding the leakage rate (P=0.738. Conclusion: Within the limitations of this study, it was observed that the adhesive systems in alliance with gutta-percha and MTA obturation could not entirely

Dietary adaptions in the ultrastructure of dinosaur dentine.

Science.gov (United States)

Brink, Kirstin S; Chen, Yu-Cheng; Wu, Ya-Na; Liu, Wei-Min; Shieh, Dar-Bin; Huang, Timothy D; Sun, Chi-Kuang; Reisz, Robert R

2016-12-01

Teeth are key to understanding the feeding ecology of both extant and extinct vertebrates. Recent studies have highlighted the previously unrecognized complexity of dinosaur dentitions and how specific tooth tissues and tooth shapes differ between taxa with different diets. However, it is unknown how the ultrastructure of these tooth tissues contributes to the differences in feeding style between taxa. In this study, we use third harmonic generation microscopy and scanning electron microscopy to examine the ultrastructure of the dentine in herbivorous and carnivorous dinosaurs to understand how the structure of this tissue contributes to the overall utility of the tooth. Morphometric analyses of dentinal tubule diameter, density and branching rates reveal a strong signal for dietary preferences, with herbivorous saurischian and ornithischian dinosaurs consistently having higher dentinal tubule density than their carnivorous relatives. We hypothesize that this relates to the hardness of the dentine, where herbivorous taxa have dentine that is more resistant to breakage and wear at the dentine-enamel junction than carnivorous taxa. This study advocates the detailed study of dentine and the use of advanced microscopy techniques to understand the evolution of dentition and feeding ecology in extinct vertebrates. © 2016 The Author(s).

Effect of dentin bonding agent diffusing through dentin slices on the reactive oxygen species production and apoptosis of pulpal cells

Directory of Open Access Journals (Sweden)

Bor-Shiunn Lee

2015-04-01

Conclusion: The three DBAs after diffusion through 0.2- or 0.5-mm dentin slice still exhibit cytotoxicity to dental pulp cells. However, the 0.5-mm dentin slice is found to be a better barrier than the 0.2-mm dentin slice to protect dental pulp cells from DBA-induced cytotoxicity.

Dentin Permeability of Carious Primary Teeth

African Journals Online (AJOL)

primary dental pulp make it difficult to determine which modality offers the best ... The most common pathology of the dentine is dental caries. ... to evaluate dentine permeability is to calculate its hydraulic conductance (Lp) using fluid filtration ...

Marginal adaptation of composite resins under two adhesive techniques.

Science.gov (United States)

Dačić, Stefan; Veselinović, Aleksandar M; Mitić, Aleksandar; Nikolić, Marija; Cenić, Milica; Dačić-Simonović, Dragica

2016-11-01

In the present research, different adhesive techniques were used to set up fillings with composite resins. After the application of etch and rinse or self etch adhesive technique, marginal adaptation of composite fillings was estimated by the length of margins without gaps, and by the microretention of resin in enamel and dentin. The study material consisted of 40 extracted teeth. Twenty Class V cavities were treated with 35% phosphorous acid and restored after rinsing by Adper Single Bond 2 and Filtek Ultimate-ASB/FU 3M ESPE composite system. The remaining 20 cavities were restored by Adper Easy One-AEO/FU 3M ESPE composite system. Marginal adaptation of composite fillings was examined using a scanning electron microscope (SEM). The etch and rinse adhesive technique showed a significantly higher percentage of margin length without gaps (in enamel: 92.5%, in dentin: 57.3%), compared with the self-etch technique with lower percentage of margin length without gaps, in enamel 70.4% (p resin tugs in interprismatic spaces of enamel, while the dentin microretention was composed of adhesive and hybrid layers with resin tugs in dentin canals. In the second technique, resin tugs were rarely seen and a microgap was dominant along the border of restoration margins. The SEM analysis showed a better marginal adaptation of composite resin to enamel and dentin with better microretention when the etch and rinse adhesive procedure was applied. © 2016 Wiley Periodicals, Inc.

Microtensile bond strength of contemporary adhesives to primary enamel and dentin.

Science.gov (United States)

Marquezan, Marcela; da Silveira, Bruno Lopes; Burnett, Luiz Henrique; Rodrigues, Célia Regina Martins Delgado; Kramer, Paulo Floriani

2008-01-01

The purpose of this study was to assess bond strength of three self-etching and two total-etch adhesive systems bonded to primary tooth enamel and dentin. Forty extracted primary human molars were selected and abraded in order to create flat buccal enamel and occlusal dentin surfaces. Teeth were assigned to one of the adhesive systems: Adper Scotch Bond Multi Purpose, Adper Single Bond 2, Adper Prompt L-Pop, Clearfil SE Bond and AdheSE. Immediately to adhesive application, a composite resin (Filtek Z250) block was built up. After 3 months of water storage, each sample was sequentially sectioned in order to obtain sticks with a square cross-sectional area of about 0.72 mm2. The specimens were fixed lengthways to a microtensile device and tested using a universal testing machine with a 50-N load cell at a crosshead speed of 0.5 mm/min. Microtensile bond strength values were recorded in MPa and compared by Analysis of Variance and the post hoc Tukey test (a = 0.05). In enamel, Clearfil SE Bond presented the highest values, followed by Adper Single Bond 2, AdheSE and Adper Scotch Bond Multi Purpose, without significant difference. The highest values in dentin were obtained with Adper Scotch Bond Multi Purpose and all other adhesives did not present significant different values from that, except Adper Prompt L-Pop that achieved the lowest bond strength in both substrates. Adper Scotch Bond Multi Purpose and Adper Single Bond 2 presented significantly lower values in enamel than in dentin although all other adhesives presented similar results in both substrates. contemporary adhesive systems present similar behaviors when bonded to primary teeth, with the exception of the one-step self-etching system; and self-etching systems can achieve bond strength values as good in enamel as in dentin of primary teeth.

Machinability of some dentin simulating materials.

Science.gov (United States)

Möllersten, L

1985-01-01

Machinability in low speed drilling was investigated for pure aluminium, Frasaco teeth, ivory, plexiglass and human dentin. The investigation was performed in order to find a suitable test material for drilling experiments using paralleling instruments. A material simulating human dentin in terms of cuttability at low drilling speeds was sought. Tests were performed using a specially designed apparatus. Holes to a depth of 2 mm were drilled with a twist drill using a constant feeding force. The time required was registered. The machinability of the materials tested was determined by direct comparison of the drilling times. As regards cuttability, first aluminium and then ivory were found to resemble human dentin most closely. By comparing drilling time variances the homogeneity of the materials tested was estimated. Aluminium, Frasaco teeth and plexiglass demonstrated better homogeneity than ivory and human dentin.

Effect of a retention groove on the shear bond strength of dentin-bonded restorations

NARCIS (Netherlands)

de Kok, P.; de Jager, N.; Veerman, I.A.M.; Hafeez, N.; Kleverlaan, C.J.; Roeters, J.F.M.

2016-01-01

Statement of problem. With the increasing use of minimally invasive restorations, effective adhesion becomes more important. Applying mechanical retention to a flat dentin surface might improve the adhesion of ceramic and composite resin restorations. Purpose. The purpose of this in vitro study was

Morphology and chemical composition of dentin in permanent first molars with the diagnose MIH

NARCIS (Netherlands)

Heijs, Suzanne C. B.; Dietz, Wolfram; Noren, Jorgen G.; Blanksma, Nynke G.; Jalevik, Birgitta

2007-01-01

The purpose of this investigation was to study the morphology and distribution of some inorganic elements in dentin in first permanent molars from children with Molar-Incisor Hypomineralization (MIH). Sixty four tooth sections from thirty two children were examined in polarized light. Fifteen

Mini-interfacial Fracture Toughness of a Multimode Adhesive Bonded to Plasma-treated Dentin.

Science.gov (United States)

Ayres, Ana Paula Almeida; Pongprueksa, Pong; De Munck, Jan; Gré, Cristina Parise; Nascimento, Fábio Dupart; Giannini, Marcelo; Van Meerbeek, Bart

2017-01-01

To investigate the bonding efficacy of a multimode adhesive to plasma-treated and -untreated (control) dentin using a mini-interfacial fracture toughness (mini-iFT) test. Twenty human molars were used in a split-tooth design (n = 10). The adhesive Scotchbond Universal (SBU; 3M ESPE) was applied in etch-and-rinse (E&R) and self-etch (SE) modes. Mid-coronal dentin was exposed and covered with a standardized smear layer ground to 320 grit. One half of each dentin surface received 15 s of non-thermal atmospheric plasma (NTAP), while the other half was covered with a metallic barrier and kept untreated. Following the E&R mode, dentin was plasma treated immediately after phosphoric acid etching. SBU and a resin-based composite were applied to dentin following the manufacturer's instructions. Six mini-iFT specimens were prepared per tooth (1.5 x 2.0 x 16 to 18 mm), and a single notch was prepared at the adhesive-dentin interface using a 150-μm diamond blade under water cooling. Half of the mini-iFT specimens were immediately loaded until failure in a 4-point bending test, while the other half were first stored in distilled water for 6 months. After testing, the exact dimensions of the notch were measured with a measuring optical microscope, from which ΚIc was determined. Three-way ANOVA revealed higher mini-iFT for SBU applied in E&R than SE mode for both storage times, irrespective of NTAP treatment. Overall, mini-iFT did not decrease for any of the experimental groups upon 6-month aging, while plasma treatment did not show a direct beneficial effect on mini-iFT of SBU applied in either E&R or SE mode.

Effect of grape seed extract against biodegradation of composite resin-dentin shear bond strength

Science.gov (United States)

Generosa, D. M.; Suprastiwi, E.; Asrianti, D.

2017-08-01

This study aimed to analyze the effect of grape seed extract (GSE) on resin-dentin shear bond strength. A group of 48 dentin samples were divided into 6 groups. The six groups, each with eight specimens, included group 1 (control), group 2 (control + NaOCl 10%), group 3 (2.9% GSE application before etching), group 4 (2.9% GSE application before etching + NaOCl 10%), group 5 (2.9% GSE application after etching), and group 6 (2.9% GSE application after etching + NaOCl 10%). Shear bond strengths were measured using a universal testing machine. Statistical analysis was done with the Kruskal-Wallis test and the Mann-Whitney U test. The highest median value was in group 3, and the lowest value was in group 5. GSE can improve the shear bond strength (p = 0.002 and 0.001), but it has no effect on reducing biodegradation (p = 0.141).

BOND STRENGTH OF SELF-ETCH ADHESIVES WITH PRIMARY AND PERMANENT TEETH DENTIN – IN VITRO STUDY.

Directory of Open Access Journals (Sweden)

Natalia Gateva

2012-03-01

Full Text Available Objective: The aim of this study was to compare dentin bond strength of primary and permanent teeth with self-etching adhesive systems. Methods: On 40 intact specimens of primary and permanent teeth was created flat dentin surfaces. The patterns were divided in 4 groups. Two different self-etching adhesive systems were used – one two steps (AdheSE, VivaDent and one one step (AdheSE One, VivaDent. Resin composite build-ups were constructed by means of convetional copper ring after applying the adhesive. The specimens were stored in water for 72 h at room temperature. After that specimens were tested for macrotensile bond strength. Debonded surfaces were analyzed by SEM.Conclusions: The measured values of dentin bond strength after applying self-etching adhesives are statistically significant in group of permanent teeth in comparison with group of primary teeth, and for both adhesive generations. Two steps self-etching adhesive provide significant stronger dentin bond strength with both dentitions in comparison with one step self-etching adhesive.

Raman spectra of human dentin mineral

NARCIS (Netherlands)

Tsuda, H; Ruben, J; Arends, J

Human dentin mineral has been investigated by using micro-Raman spectroscopy. Fluorescence and thermal problems were largely avoided by preparing dentin samples by grinding and ultrasonic agitation in acetone. The Raman spectral features were consistent with those of impure hydroxyapatite containing

The effect of different surface treatments of stainless steel crown and different bonding agents on shear bond strength of direct composite resin veneer

Directory of Open Access Journals (Sweden)

Ajami B

2007-01-01

Full Text Available Background and Aim: Stainless steel crown (SSC is the most durable and reliable restoration for primary teeth with extensive caries but its metalic appearance has always been a matter of concern. With advances in restorative materials and metal bonding processes, composite veneer has enhanced esthetics of these crowns in clinic. The aim of this study was to evaluate the shear bond strength of SSC to composite resin using different surface treatments and adhesives. Materials and Methods: In this experimental study, 90 stainless steel crowns were selected. They were mounted in molds and divided into 3 groups of 30 each (S, E and F. In group S (sandblast, buccal surfaces were sandblasted for 5 seconds. In group E (etch acidic gel was applied for 5 minutes and in group F (fissure bur surface roughness was created by fissure diamond bur. Each group was divided into 3 subgroups (SB, AB, P based on different adhesives: Single Bond, All Bond2 and Panavia F. Composite was then bonded to specimens. Cases were incubated in 100% humidity at 37°C for 24 hours. Shear bond strength was measured by Zwick machine with crosshead speed of 0.5 mm/min. Data were analyzed by ANOVA test with p0.05 so the two variables were studied separately. No significant difference was observed in mean shear bond strength of composite among the three kinds of adhesives (P>0.05. Similar results were obtained regarding surface treatments (P>0.05. Conclusion: Based on the results of this study, treating the SSC surface with bur and using single bond adhesive and composite can be used successfully to obtain esthetic results in pediatric restorative treatments.

Cone calorimeter testing of foam core sandwich panels treated with intumescent paper underneath the veneer (FRV)

Science.gov (United States)

Mark A. Dietenberger; Ali Shalbafan; Johannes Welling

2017-01-01

Surfaces of novel foam core sandwich panels were adhered with intumescent fire‐retardant paper underneath the veneers (FRV) to improve their flammability properties. The panels were evaluated by means of cone calorimeter test (ASTM E 1354). Variables tested were different surface layer treatments, adhesives used for veneering, surface layer thicknesses, and processing...

Evaluation of the use potential of nine species of genus Eucalyptus for production of veneers and plywood panels

Directory of Open Access Journals (Sweden)

Setsuo Iwakiri

2013-06-01

Full Text Available The objective of thisstudywas to evaluate the use potential of nine species of Eucalyptus for production of veneer sheets and multilaminated plywood panels. Veneers were cut using a pilot laminating lathe to a nominal thickness of 2.0 mm. Analysis included finding values of overall yield and yield according to three quality classes for the nine relevant species. Plywood panels were manufactured in a laboratory, consisting of five 2.0 mm veneer sheets which were bonded together with phenol-formaldehyde resin at a weight of 360 g/m2 (double line. The panels were compressed using a specific pressure of 10 kgf/cm2, a temperature of 140ºC and a pressing time of 10 minutes. Results indicated that, with the exception of E. phaeotricha and E. pellita, all other Eucalyptus species had above 50% average veneer yield after lamination. Results of glue line shear testing and static bending parallel and perpendicular demonstrated that species Eucalyptus grandis, Eucalyptus saligna, Eucalyptus dunnii, Eucalyptus globulus, Eucalyptus viminalis, Eucalyptus robusta and Eucalyptus pellita have great potential within the parameters of this study for use in the production of veneer sheets and plywood panels intended for outdoor use.

New perspectives about molecular arrangement of primary and permanent dentin

Energy Technology Data Exchange (ETDEWEB)

Sanches Borges, Ana Flavia [Department of Dental Materials at Piracicaba Dental School, State University of Campinas, Piracicaba, SP (Brazil); Andrade Bitar, Renata [Biomedical Engineering, Valley of Paraiba University (UNIVAP) (Brazil); Kantovitz, Kamila Rosamilia [Department of Pediatric Dentistry at Piracicaba Dental School, State University of Campinas, Piracicaba, SP (Brazil); Bortollazo Correr, Americo [Department of Dental Materials at Piracicaba Dental School, State University of Campinas, Piracicaba, SP (Brazil); Martin, Airton Abrahao [Biomedical Engineering Post Graduation, Valley of Paraiba University (UNIVAP) (Brazil); Puppin-Rontani, Regina Maria [Department of Pediatric Dentistry at Piracicaba Dental School, State University of Campinas, Piracicaba, SP (Brazil)], E-mail: rmpuppin@fop.unicamp.br

2007-12-30

The dentin quality of primary and permanent teeth was inspected by Fourier transformed Raman spectroscopy (FT-Raman); scanning electron microscopy/energy-dispersive spectroscopy (SEM/EDS) and hardness test. Middle dentin of crowns were reached by carbide bur abrading providing a uniform smear layer. Phosphoric acid was applied in order to simulate the etching of total etching adhesive systems. The groups were (n = 10): G1 (primary dentin smear layer); G2 (35% phosphoric acid etched primary dentin); G3 (permanent dentin smear layer); G4 (35% phosphoric acid etched permanent dentin). FT-Raman results were subjected to cluster analysis. SEM/EDS were made in order to add the data obtained by FT-Raman. The hardness data were subjected to ANOVA and Tukey test. FT-Raman showed differences among groups, either to organic or inorganic content. For the organic content, primary and permanent dentin became similar after the etching; conversely, the inorganic content showed differences for the two substrates. Hardness test showed no significant differences between primary and permanent dentin, before or after etching, but the etching decreased these values. The mineral content arrangement of primary dentin is different from permanent dentin, independently of the etching. The substrate type did no influence the hardness, but the etching decreased it.

Evaluation of the color durability of acrylic resin veneer materials after immersion in common beverages at different time intervals: A spectrophotometric study.

Science.gov (United States)

Kohli, Shivani; Bhatia, Shekhar

2015-01-01

Proper function, esthetics, and cost are the prime factors to be considered while selecting bridge veneering materials. The purpose of the study is to evaluate color durability of acrylic veneer materials after immersion in common beverages at different time intervals. Spectrophotometer was used for taking color measurements based on the transmission of light through the specimens made of the selected materials which were Tooth moulding powder (DPI) and Acrylux (Ruthinium). Thirty specimens of standardized dimensions were prepared from each material. The specimens were divided into three groups of 10 each. One group of each material was immersed in tea (TajMahal) and another group of each material in cola (Pepsi) as the staining solutions. The remaining group of 10 from each material served as control and was stored in distilled water. Color measurements were obtained pre-immersion, and after 1, 15, and 30 days of immersion. Tooth moulding powder displayed better color durability than Acrylux over the 1 month immersion period in both staining solutions. Tea resulted in more discoloration compared to cola (Pepsi). The difference in the color durability of Acrylux and Tooth moulding powder may be attributed to the differences in the composition of tested resin veneering materials, i.e. their polar properties, which contribute to the absorption of staining solution, and the different brands and the strengths of the solutions.

Evaluation of the color durability of acrylic resin veneer materials after immersion in common beverages at different time intervals: A spectrophotometric study

Directory of Open Access Journals (Sweden)

Shivani Kohli

2015-06-01

Full Text Available Background: Proper function, esthetics, and cost are the prime factors to be considered while selecting bridge veneering materials. The purpose of the study is to evaluate color durability of acrylic veneer materials after immersion in common beverages at different time intervals. Methods: Spectrophotometer was used for taking color measurements based on the transmission of light through the specimens made of the selected materials which were Tooth moulding powder (DPI and Acrylux (Ruthinium. Thirty specimens of standardized dimensions were prepared from each material. The specimens were divided into three groups of 10 each. One group of each material was immersed in tea (TajMahal and another group of each material in cola (Pepsi as the staining solutions. The remaining group of 10 from each material served as control and was stored in distilled water. Color measurements were obtained pre-immersion, and after 1, 15, and 30 days of immersion. Results: Tooth moulding powder displayed better color durability than Acrylux over the 1 month immersion period in both staining solutions. Tea resulted in more discoloration compared to cola (Pepsi. Conclusion: The difference in the color durability of Acrylux and Tooth moulding powder may be attributed to the differences in the composition of tested resin veneering materials, i.e. their polar properties, which contribute to the absorption of staining solution, and the different brands and the strengths of the solutions.

Evaluation of veneer yields and grades from yellow-poplar, white oak, and sweetgum from the southeast

Science.gov (United States)

Robert H. McAlister

1980-01-01

Dry volume yields and standard grades of veneer are given for yellow-poplar, sweetgum, and white oak by tree diameter and location within the stem. Results show that the typical stands of mixed southern pine and hardwood timer yield enough veneer to utilize almost 90 percent of the stand volume in the production of COM-PLY lumber and panels

The influence of felling season and log-soaking temperature on the wetting and phenol formaldehyde adhesive bonding characteristics of birch veneer

Science.gov (United States)

Anti Rohumaa; Christopher G. Hunt; Charles R. Frihart; Pekka Saranpää; Martin Ohlmeyer; Mark Hughes

2014-01-01

Most adhesive studies employing wood veneer as the substrate assume that it is a relatively uniform material if wood species and veneer thickness are constant. In the present study, veneers from rotary cut birch (Betula pendula Roth) were produced from logs harvested in spring, autumn and winter, and soaked at 20°C and 70°C prior to peeling. Firstly...

Use of poly (amidoamine dendrimer for dentinal tubule occlusion: a preliminary study.

Directory of Open Access Journals (Sweden)

Tianda Wang

Full Text Available The occlusion of dentinal tubules is an effective method to alleviate the symptoms caused by dentin hypersensitivity, a significant health problem in dentistry and daily life. The in situ mineralization within dentinal tubules is a promising treatment for dentin hypersensitivity as it induces the formation of mineral on the sensitive regions and occludes the dentinal tubules. This study was carried out to evaluate the in vitro effect of a whole generation poly(amidoamine (PAMAM dendrimer (G3.0 on dentinal tubule occlusion by inducing mineralization within dentinal tubules. Dentin discs were treated with PAMAM dendrimers using two methods, followed by the in vitro characterization using Attenuated total reflection Fourier-transform infrared spectroscopy (ATR-FTIR, X-ray diffraction (XRD, Field emission scanning electron microscopy (FE-SEM and Energy-Dispersive X-ray Spectroscopy (EDS. These results showed that G3.0 PAMAM dendrimers coated on dentin surface and infiltrated in dentinal tubules could induce hydroxyapatite formation and resulted in effective dentinal tubule occlusion. Moreover, crosslinked PAMAM dendrimers could induce the remineralization of demineralized dentin and thus had the potential in dentinal tubule occlusion. In this in vitro study, dentinal tubules occlusion could be achieved by using PAMAM dendrimers. This could lead to the development of a new therapeutic technique for the treatment of dentin hypersensitivity.

The effect of core material, veneering porcelain, and fabrication technique on the biaxial flexural strength and weibull analysis of selected dental ceramics.

Science.gov (United States)

Lin, Wei-Shao; Ercoli, Carlo; Feng, Changyong; Morton, Dean

2012-07-01

The objective of this study was to compare the effect of veneering porcelain (monolithic or bilayer specimens) and core fabrication technique (heat-pressed or CAD/CAM) on the biaxial flexural strength and Weibull modulus of leucite-reinforced and lithium-disilicate glass ceramics. In addition, the effect of veneering technique (heat-pressed or powder/liquid layering) for zirconia ceramics on the biaxial flexural strength and Weibull modulus was studied. Five ceramic core materials (IPS Empress Esthetic, IPS Empress CAD, IPS e.max Press, IPS e.max CAD, IPS e.max ZirCAD) and three corresponding veneering porcelains (IPS Empress Esthetic Veneer, IPS e.max Ceram, IPS e.max ZirPress) were selected for this study. Each core material group contained three subgroups based on the core material thickness and the presence of corresponding veneering porcelain as follows: 1.5 mm core material only (subgroup 1.5C), 0.8 mm core material only (subgroup 0.8C), and 1.5 mm core/veneer group: 0.8 mm core with 0.7 mm corresponding veneering porcelain with a powder/liquid layering technique (subgroup 0.8C-0.7VL). The ZirCAD group had one additional 1.5 mm core/veneer subgroup with 0.7 mm heat-pressed veneering porcelain (subgroup 0.8C-0.7VP). The biaxial flexural strengths were compared for each subgroup (n = 10) according to ISO standard 6872:2008 with ANOVA and Tukey's post hoc multiple comparison test (p≤ 0.05). The reliability of strength was analyzed with the Weibull distribution. For all core materials, the 1.5 mm core/veneer subgroups (0.8C-0.7VL, 0.8C-0.7VP) had significantly lower mean biaxial flexural strengths (p Empress and e.max groups, regardless of core thickness and fabrication techniques. Comparing fabrication techniques, Empress Esthetic/CAD, e.max Press/CAD had similar biaxial flexural strength (p= 0.28 for Empress pair; p= 0.87 for e.max pair); however, e.max CAD/Press groups had significantly higher flexural strength (p Empress Esthetic/CAD groups. Monolithic core

Effects of Different Radiation Doses on the Bond Strengths of Two Different Adhesive Systems to Enamel and Dentin.

Science.gov (United States)

da Cunha, Sandra Ribeiro de Barros; Ramos, Pedro Augusto Minorin Mendes; Haddad, Cecília Maria Kalil; da Silva, João Luis Fernandes; Fregnani, Eduardo Rodrigues; Aranha, Ana Cecília Corrêa

2016-01-01

To evaluate the effects of three different radiation doses on the bond strengths of two different adhesive systems to enamel and dentin. Eighty human third molars were randomly divided into four groups (n = 20) according to the radiation dose (control/no radiation, 20 Gy, 40 Gy, and 70 Gy). The teeth were sagittally sectioned into three slices: one mesial and one distal section containing enamel and one middle section containing dentin. The sections were then placed in the enamel and dentin groups, which were further divided into two subgroups (n = 10) according to the adhesive used. Three restorations were performed in each tooth (one per section) using Adper Single Bond 2 (3M ESPE) or Universal Single Bond (3M ESPE) adhesive system and Filtek Z350 XT (3M ESPE) resin composite and subjected to the microshear bond test. Data were analyzed using a two-way ANOVA followed by Tukey's test. Failure modes were examined under a stereoscopic loupe. Radiotherapy did not affect the bond strengths of the adhesives to either enamel or dentin. In dentin, the Universal Single Bond adhesive system showed higher bond strength values when compared with the Adper Single Bond adhesive system. More adhesive failures were observed in the enamel for all radiation doses and adhesives. Radiotherapy did not influence the bond strength to enamel or dentin, irrespective of the adhesive or radiation dose used.

Hybridization quality and bond strength of adhesive systems according to interaction with dentin

Science.gov (United States)

Salvio, Luciana Andrea; Hipólito, Vinicius Di; Martins, Adriano Luis; de Goes, Mario Fernando

2013-01-01

Objective: To evaluate the hybridization quality and bond strength of adhesives to dentin. Materials and Methods: Ten human molars were ground to expose the dentin and then sectioned in four tooth-quarters. They were randomly divided into 5 groups according to the adhesive used: Two single-step self-etch adhesives – Adper Prompt (ADP) and Xeno III (XE), two two-step self-etching primer systems – Clearfil SE Bond (SE) and Adhe SE (ADSE), and one one-step etch-and-rinse system – Adper Single Bond (SB). Resin composite (Filtek Z250) crown buildups were made on the bonded surfaces and incrementally light-cured for 20 s. The restored tooth-quarters were stored in water at 37°C for 24 h and then sectioned into beams (0.8 mm2 in cross-section). Maximal microtensile bond strength (μ-TBS) was recorded (0.5 mm/min in crosshead speed). The results were submitted to one-way ANOVA and Tukey's test (α = 0.05). Thirty additional teeth were used to investigate the hybridization quality by SEM using silver methenamine or ammoniacal silver nitrate dyes. Results: SE reached significantly higher μ-TBS (P 0.05), and between SB and ADP (P > 0.05); ADSE and XE were significantly higher than SB and ADP (P adhesives with dentin. The hybridization quality was essential to improve the immediate μ-TBS to dentin. PMID:24926212

[Influence of different bonding agents on traction resistance of metal alloys to dentin].

Science.gov (United States)

Adabo, G L; da Silva Filho, F P; de Sá, D N; Rettondini, W C; dos Santos Cruz, C A

1990-01-01

They were casted pieces using three kinds of alloy (Ni-Cr, Ag-Sn and Cu-Al) with circular and smooth surface. They were cemented to human teeth, on occlusal surface, grounded at dentin level, through three different materials kind (zinc polycarboxylate cement, glassionomer cement and composite). After 24 hours storing, the samples were subjected to the tensile test. The results showed that the samples cemented with composite and the casts made with Ag-Sn alloy had higher bond strength.

Strontium effects on root dentin tubule occlusion and nanomechanical properties.

Science.gov (United States)

Saeki, Kuniko; Marshall, Grayson W; Gansky, Stuart A; Parkinson, Charles R; Marshall, Sally J

2016-02-01

Dentin hypersensitivity often is treated by promotion of dentin tubule occlusion. In this in vitro study we evaluated nanomechanical properties and degree of tubule occlusion conferred to sound and demineralized human root dentin following treatment with a 10% (w/w) strontium acetate solution and its relation to the treatment duration and delivery method. 24 human cervical root dentin disks (8 groups of 3) were polished through 0.25 μm. 12 disks were subjected to an acid challenge (1% citric acid, pH 3.8) for 2 min. The specimens were incubated in artificial saliva, treated by soaking or brushing with deionized (DI) water or a solution of 10% strontium acetate for 2 min twice a day for 28 days. The occlusion percent and nanomechanical properties were determined at the baseline, 5, 14 and 28 days. Cross-sectioned specimens were prepared to evaluate the depth affected by strontium acetate / dentin interaction by SEM. Statistical analysis was performed using linear mixed effects models. A 10% strontium acetate treatment over 5-28 days significantly increased tubule occlusion for normal root dentin and to a lesser extent for demineralized dentin and increased the AFM based nanomechanical properties of demineralized dentin. Brushing was more effective than soaking in recovery of properties of demineralized dentin when treated with strontium. No difference in tubuleocclusion was found between the two delivery methods. Strontium acetate itself proved to have the ability to occlude dentin tubules and result in small changes in the mechanical properties of dentin. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

In vitro evaluation of marginal microleakage in class V restorations with composite resin in bovine teeth. Laser irradiation influences and the adhesive system in the dentin pre-treatment

International Nuclear Information System (INIS)

Carvalho, Wendell Lima de

2003-01-01

Microleakage is one of the most important reasons to restorations failure, it is the responsible for marginal colors changing, new caries, hipersensibility and pulpar diseases. Several techniques and materials have been studied to eliminate or, at least, to decrease microleakage. The cavities preparation with Er:YAG laser and autoconditioning adhesive are some of these techniques and materials. This research has the objective to compare, in vitro, microleakage in class V cavities, prepared with high rotation (conventional treatment), Er:YAG laser (Enamel-400 mj/2 Hz/128,38 J/Cm 2 , Dentin 250 mJ/ 2 Hz/ 80,24 J/Cm 2 ) and the treatment made at dentin with autoconditioning adhesive (Clerafil SE Bond) using Er:YAG laser (with water or not water) or not using Er:YAG laser. It was used 48 bovines teeth with cavities prepared in vestibular face and gingival wall on cement enamel junction and oclusal wall on enamel. The materials used were autoconditioning adhesive (Clerafil SE Bond) and composite resin Z250. Teeth were divided into four groups of twelve samples each one, according to dentin treatment. Group 1 - Conventional cavity and autoconditioning adhesive. Group 2- Cavity prepared with Er: YAG laser and autoconditioning adhesive. Group 3 - Cavity prepared with Er:YAG laser and dentin conditioning with Er:YAG laser associated to water and autoconditioning adhesive. Group 4 - Cavity prepared with Er:YAG laser and dentin conditioning with Er: YAG laser without water and associated to autoconditioning adhesive. Teeth were restored and stocked at 37 deg C, thermocycled and placed into a 50% silver nitrate solution. Right after, teeth were sliced and evaluated on a stereo microscopic magnifying glass in order to see microleakage degree trying to follow a score from 0 to 3. The findings were submitted to Fisher, Anderson-Darling tests and to the not parametric Sen and Puri test. The results indicated that in gingival edge, the Group 2 showed less microleakage than others

Illuminating light-dependent color shifts in core and veneer layers of dental all-ceramics

Science.gov (United States)

Lee, Yong-Keun; Cha, Hyun-Suk; Yu, Bin

2014-09-01

The color of an object is perceived differently depending on the ambient light conditions. Since dental all-ceramic restorations are fabricated by building up several layers to reproduce the tooth shade, the optical properties of each layer should be optimized for successful shade reproduction. This study aimed to determine the separate contributions of the color shifts in each of the core and veneer layers of all-ceramics by switching the illuminating lights on the color shifts of layered ceramics. Specimens of seven kinds of core ceramics and the corresponding veneer ceramics for each core were fabricated with a layered thickness of 1.5 mm. A sintering ceramic was used as a reference core material. The Commission Internationale de l'Eclairage (CIE) color coordinates of core, veneer, and layered specimens were measured with a spectroradiometer under the CIE illuminant D65 (daylight), A (incandescent lamp), and F9 (fluorescent lamp) simulating lights. Color shifts of the layered specimens were primarily determined by the CIE a* shifts (D65 to A switch) or by the CIE b* shifts (D65 to F9 switch) of the veneer layer. The color coordinates shifts in the constituent layers differentially influenced those of the layered specimens by the kind of switched lights. Therefore, the optical properties of the constituent layers of all-ceramics should be controlled to reflect these findings.

Evaluation of bond strength of silorane and methacrylate based restorative systems to dentin using different cavity models

Directory of Open Access Journals (Sweden)

Stephano Zerlottini Isaac

2013-09-01

Full Text Available OBJECTIVE: The aim of this in vitro study was to evaluate the microtensile bond strength (µTBS to dentin of two different restorative systems: silorane-based (P90, and methacrylate-based (P60, using two cavity models. MATERIAL AND METHODS: Occlusal enamel of 40 human third molars was removed to expose flat dentin surface. Class I cavities with 4 mm mesial-distal width, 3 mm buccal-lingual width and 3 mm depth (C-factor=4.5 were prepared in 20 teeth, which were divided into two groups (n=10 restored with P60 and P90, bulk-filled after dentin treatment according to manufacturer's instructions. Flat buccal dentin surfaces were prepared in the 20 remaining teeth (C-factor=0.2 and restored with resin blocks measuring 4x3x3 mm using the two restorative systems (n=10. The teeth were sectioned into samples with area between 0.85 and 1.25 mm2 that were submitted to µTBS testing, using a universal testing machine (EMIC at speed of 0.5 mm/min. Fractured specimens were analyzed under stereomicroscope and categorized according to fracture pattern. Data were analyzed using ANOVA and Tukey Kramer tests. RESULTS: For flat surfaces, P60 obtained higher bond strength values compared with P90. However, for Class I cavities, P60 showed significant reduction in bond strength (p0.05, or between Class I Cavity and Flat Surface group, considering P90 restorative system (p>0.05. Regarding fracture pattern, there was no statistical difference among groups (p=0.0713 and 56.3% of the fractures were adhesive. CONCLUSION: It was concluded that methacrylate-based composite µTBS was influenced by cavity models, and the use of silorane-based composite led to similar bond strength values compared to the methacrylate-based composite in cavities with high C-factor.

Effect of desensitizing agents on dentin permeability.

Science.gov (United States)

Ishihata, Hiroshi; Kanehira, Masafumi; Nagai, Tomoko; Finger, Werner J; Shimauchi, Hidetoshi; Komatsu, Masashi

2009-06-01

To investigate the in vitro efficacy of two dentin desensitizing products at reducing liquid permeability through human dentin discs. The tested hypothesis was that the products, in spite of different chemical mechanisms were not different at reducing or eliminating flow through dentin discs. Dentin slices (1 mm thick) were prepared from 16 extracted human third molars and their permeability was indirectly recorded in a split chamber model, using a chemiluminescence technique, after EDTA treatment (control), after soaking with albumin, and after desensitizer application. Two products were studied: MS Coat, a self-curing resin-containing oxalate product, and Gluma Desensitizer, a glutaraldehyde/HEMA-based agent without initiator. The dentin slices were mounted between an upper chamber, filled with an aqueous solution of 1% potassium ferricyanide and 0.3% hydrogen peroxide, and a lower chamber filled with 1% sodium hydroxide solution and 0.02% luminol. The upper solution was pressurized, and upon contact with the luminol solution a photochemical signal was generated and recorded as a measure of permeability throughout two consecutive pressurizing cycles at 2.5 and 13 kPa (26 and 133 cm H2O), respectively. The permeability of the control and albumin-soaked samples was similarly high. After application of the desensitizing agents, dentin permeability was reduced to virtually zero at both pressure levels (P < 0.001).

Adhesive permeability affects coupling of resin cements that utilise self-etching primers to dentine.

Science.gov (United States)

Carvalho, R M; Pegoraro, T A; Tay, F R; Pegoraro, L F; Silva, N R F A; Pashley, D H

2004-01-01

To examine the effects of an experimental bonding technique that reduces the permeability of the adhesive layer on the coupling of resin cements to dentine. Extracted human third molars had their mid to deep dentin surface exposed flat by transversally sectioning the crowns. Resin composite overlays were constructed and cemented to the surfaces using either Panavia F (Kuraray) or Bistite II DC (Tokuyama) resin cements mediated by their respective one-step or two-step self-etch adhesives. Experimental groups were prepared in the same way, except that the additional layer of a low-viscosity bonding resin (LVBR, Scotchbond Multi-Purpose Plus, 3M ESPE) was placed on the bonded dentine surface before luting the overlays with the respective resin cements. The bonded assemblies were stored for 24 h in water at 37 degrees C and subsequently prepared for microtensile bond strength testing. Beams of approximately 0.8 mm(2) were tested in tension at 0.5 mm/min in a universal tester. Fractured surfaces were examined under scanning electron microscopy (SEM). Additional specimens were prepared and examined with TEM using a silver nitrate-staining technique. Two-way ANOVA showed significant interactions between materials and bonding protocols (p0.05). SEM observation of the fractured surfaces in Panavia F showed rosette-like features that were exclusive for specimens bonded according to manufacturer's directions. Such features corresponded well with the ultrastructure of the interfaces that showed more nanoleakage associated with the more permeable adhesive interface. The application of the additional layer of the LVBR reduced the amount of silver impregnation for both adhesives suggesting that reduced permeability of the adhesives resulted in improved coupling of the resin cements to dentin. Placement of an intermediate layer of a LVBR between the bonded dentine surface and the resin cements resulted in improved coupling of Panavia F to dentine.

Enamel and dentine demineralization by a combination of starch and sucrose in a biofilm – caries model

Directory of Open Access Journals (Sweden)

Juliana Nunes BOTELHO

2016-01-01

Full Text Available Abstract Sucrose is the most cariogenic dietary carbohydrate and starch is considered non-cariogenic for enamel and moderately cariogenic for dentine. However, the cariogenicity of the combination of starch and sucrose remains unclear. The aim of this study was to evaluate the effect of this combination on Streptococcus mutans biofilm composition and enamel and dentine demineralization. Biofilms of S. mutans UA159 were grown on saliva-coated enamel and dentine slabs in culture medium containing 10% saliva. They were exposed (8 times/day to one of the following treatments: 0.9% NaCl (negative control, 1% starch, 10% sucrose, or 1% starch and 10% sucrose (starch + sucrose. To simulate the effect of human salivary amylase on the starch metabolization, the biofilms were pretreated with saliva before each treatment and saliva was also added to the culture medium. Acidogenicity of the biofilm was estimated by evaluating (2 times/day the culture medium pH. After 4 (dentine or 5 (enamel days of growth, biofilms (n = 9 were individually collected, and the biomass, viable microorganism count, and polysaccharide content were quantified. Dentine and enamel demineralization was assessed by determining the percentage of surface hardness loss. Biofilms exposed to starch + sucrose were more acidogenic and caused higher demineralization (p < 0.0001 on either enamel or dentine than those exposed to each carbohydrate alone. The findings suggest that starch increases the cariogenic potential of sucrose.

Fracture strengths of chair‑side‑generated veneers cemented with ...

African Journals Online (AJOL)

Introduction: CAD/CAM (computer‑aided design and computer‑aided manufacturing) systems have refreshed the idea of chair‑side production of restorations, but the fracture of ceramic veneers remains a problem. Cementation with glass fibers may improve the fracture strengths and affect the failure modes of ...

Kubelka-Munk reflectance theory applied to porcelain veneer systems using a colorimeter.

Science.gov (United States)

Davis, B K; Johnston, W M; Saba, R F

1994-01-01

The purpose of this study was to demonstrate the ability of Kubelka-Munk reflectance theory to predict color parameters of veneer porcelain on various backings using colorimetric measurements. Tristimulus absorption and scattering coefficients were used to predict the respective tristimulus reflectance values of A1, D3, and translucent porcelain samples after they had been bonded to light and dark substrates using universal, opaque, and untinted shades of bonding resin. Observed and predicted reflectance values exhibited high correlation (r2 > or = 0.93 for each porcelain shade). Kubelka-Munk theory offers an accurate prediction for the resultant colorimetric reflectance parameters of veneer porcelain bonded to variously colored backings.

Evaluation of matrix metalloproteinase and cysteine cathepsin activity in dentin hybrid layer by gelatin zymography.

Science.gov (United States)

Mahalaxmi, Sekar; Madhubala, Manavalan Madhana; Jayaraman, Mahendran; Sathyakumar, Shanmugasundaram

2016-01-01

The aim of this study was to comparatively assess the gelatinolytic activity of matrix metalloproteinases(MMPs) and Cysteine Cathepsins (CCs) in the adhesive interface using etch and rinse adhesive at different time intervals using zymographic technique. Twenty freshly extracted non-carious human third molars were used in this study. Occlusal surfaces were ground flat and 1mm thick horizontal dentin slabs were obtained from each tooth using a diamond disc. The dentin surface was polished with 600-grit silicon-carbide paper. Five out of 20 samples were directly pulverized. In the remaining fifteen samples, the dentin was etched and adhesive was applied and light cured according to the manufacturer's instructions. A 1mm thick flowable composite was build up and light cured. Bonded specimens were cut vertically into 3 to 4 dentin slabs by means of diamond disc to expose the adhesive/dentin interfaces. These were then ground down to 500 µm thick resin-dentin interface using a hard tissue microtome. These sections were then pulverised into powder. Following this, every five samples were subjected to zymographic analysis after 1 day, 7 days and 21 days. Zymograms showed clear, thicker bands on all three isoforms in the etched samples compared to control samples at 1st and 7th day intervals and became inactive at 21st day for all three isoforms. MMP 9 activity was relatively higher when compared to CCs and MMP 2. Etch and rinse adhesive activated MMPs and CCs within the hybrid layer that remained active till 7th day and no gelatinolytic activity was found on 21st day and MMPs are more active compared to CCs and MMP-2.

Effect of Re-Application of Microbrush on Micro Tensile Bond Strength of an Adhesive to Dentin

Directory of Open Access Journals (Sweden)

Seied Majid Mosavi Nasab

2013-02-01

Full Text Available Background and Aims: Re-application of microbrush may affect the micro tensile bond strength of adhesives to dentin. The aim of this study was to evaluate the effect of re-application of microbrushes on the micro tensile bond strength of an adhesive to dentin.Materials and Methods: Thirty freshly extracted molars teeth were collected and enamel of occlusal surface were removed to expose superficial dentin. Then superficial dentin was etched, washed and partially air dried.According to the times of application of microbrush, teeth were divided into two test groups. In group 1, newmicrobrushs were used, but in group 2, the ones that were already used for twice were included. Ambar dentin bonding agent (FGM/Brazil was applied to the etched dentin with microbrushes according to the manufacturer’s instructions. Then the crown of teeth was built up with LLiss (FGM/Brazil composite resin. The teeth were sectioned in buccolingual direction to obtain 1mm slabs. Then 50 hourglass- shape samples were made from 30 teeth (25 Specimens per group. The microtensile bond strength of the specimens was tested using MTD500 (SD Mechatronik, Germany. The data were statistically analyzed by T-test.Results: The mean values for the microtensile bond strength were 30.49±7.18 and 23.61±9.06 MPa±SD for the first and second groups, respectively. There was significant difference between the groups (P=0.005.Conclusion: Microbrushes should not be used for more than one cavity preparation.

Bond strength of resin modified glass ionomer cement to primary dentin after cutting with different bur types and dentin conditioning

Directory of Open Access Journals (Sweden)

Rebeca Di Nicoló

2007-10-01

Full Text Available The aim of this in vitro study was to evaluate the effect of different bur types and acid etching protocols on the shear bond strength (SBS of a resin modified glass ionomer cement (RM-GIC to primary dentin. Forty-eight clinically sound human primary molars were selected and randomly assigned to four groups (n=12. In G1, the lingual surface of the teeth was cut with a carbide bur until a 2.0-mm-diameter dentin area was exposed, followed by the application of RM-GIC (Vitremer - 3M/ESPE prepared according to the manufacturer's instructions. The specimens of G2, received the same treatment of G1, however the dentin was conditioned with phosphoric acid. In groups G3 and G4 the same procedures of G1 and G2 were conducted respectively, nevertheless dentin cutting was made with a diamond bur. The specimens were stored in distilled water at 37ºC for 24h, and then tested in a universal testing machine. SBS. data were submitted to 2-way ANOVA (= 5% and indicated that SBS values of RM-GIC bonded to primary dentin cut with different burs were not statistically different, but the specimens that were conditioned with phosphoric acid presented SBS values significantly higher that those without conditioning. To observe micromorphologic characteristics of the effects of dentin surface cut by diamond or carbide rotary instruments and conditioners treatment, some specimens were examined by scanning electron microscopy. Smear layer was present in all specimens regardless of the type of rotary instrument used for dentin cutting, and specimens etched with phosphoric acid presented more effective removal of smear layer. It was concluded that SBS of a RM-GIC to primary dentin was affected by the acid conditioning but the bur type had no influence.

Adhesive sealing of dentin surfaces in vitro: A review

Science.gov (United States)

Abu-Nawareg, Manar M; Zidan, Ahmed Z; Zhou, Jianfeng; Agee, Kelli; Chiba, Ayaka; Tagami, Jungi; Pashley, David H

2016-01-01

Purpose The purpose of this review is to describe the evolution of the use of dental adhesives to form a tight seal of freshly prepared dentin to protect the pulp from bacterial products, during the time between crown preparation and final cementum of full crowns. The evolution of these “immediate dentin sealants” follows the evolution of dental adhesives, in general. That is, they began with multiple-step, etch-and-rinse adhesives, and then switched to the use of simplified adhesives. Methods Literature was reviewed for evidence that bacteria or bacterial products diffusing across dentin can irritate pulpal tissues before and after smear layer removal. Smear layers can be solubilized by plaque organisms within 7–10 days if they are directly exposed to oral fluids. It is likely that smear layers covered by temporary restorations may last more than one month. As long as smear layers remain in place, they can partially seal dentin. Thus, many in vitro studies evaluating the sealing ability of adhesive resins use smear layer-covered dentin as a reference condition. Surprisingly, many adhesives do not seal dentin as well as do smear layers. Results Both in vitro and in vivo studies show that resin-covered dentin allows dentinal fluid to cross polymerized resins. The use of simplified single bottle adhesives to seal dentin was a step backwards. Currently, most authorities use either 3-step adhesives such as Scotchbond Multi-Purposea or OptiBond FLb or two-step self-etching primer adhesives, such as Clearfil SEc, Unifil Bondd or AdheSEe, respectfully. PMID:26846037

Bond Stability of a Universal Adhesive System to Eroded/Abraded Dentin After Deproteinization.

Science.gov (United States)

Augusto, M G; Torres, Crg; Pucci, C R; Schlueter, N; Borges, A B

Erosive/abrasive challenges can potentially compromise bonding to dentin. Aiming to improve the quality and stability of bonding to this substrate, this study investigated the combined effect of erosion and toothbrush abrasion on the microtensile bond strength (μTBS) stability to dentin using a universal adhesive system in total and self-etching modes, associated or not associated with deproteinization. Bovine dentin specimens were divided into five groups according to the organic matrix condition (n=20): control (C); erosion (E); erosion + abrasion (EA); erosion + sodium hypochlorite (EH); erosion + abrasion + sodium hypochlorite (EAH). The groups were further divided (n=10) according to the mode of application (total or self-etching) of a universal adhesive. After the bonding procedure, composite blocks were built up, and the samples were cut to obtain sticks for μTBS testing. For each specimen, one-half of the sticks was immediately tested, and the other one-half was tested after artificial aging (5000 thermocycles, 5°C and 55°C). Three-way analysis of variance (α=5%) showed a significant difference for the triple interaction ( p=0.0007). Higher μTBS means were obtained for the EH and EAH groups compared with the E and EA groups. The control group showed immediate μTBS values similar to that of the E and EA groups for both bond strategies. Erosion and erosion/abrasion did not significantly influence the immediate μTBS to dentin. Artificial aging reduced μTBS values for the groups C, E, and EA using the total-etching mode. Deproteinization maintained the bond stability to artificially aged eroded and eroded/abraded dentin.

Effect of air-drying time of single-application self-etch adhesives on dentin bond strength.

Science.gov (United States)

Chiba, Yasushi; Yamaguchi, Kanako; Miyazaki, Masashi; Tsubota, Keishi; Takamizawa, Toshiki; Moore, B Keith

2006-01-01

This study examined the effect of air-drying time of adhesives on the dentin bond strength of several single-application self-etch adhesive systems. The adhesive/resin composite combinations used were: Adper Prompt L-Pop/Filtek Z250 (AP), Clearfil Tri-S Bond/Clearfil AP-X (CT), Fluoro Bond Shake One/Beautifil (FB), G-Bond/Gradia Direct (GB) and One-Up Bond F Plus/Palfique Estelite (OF). Bovine mandibular incisors were mounted in self-curing resin and wet ground with #600 SiC to expose labial dentin. Adhesives were applied according to each manufacturer's instructions followed by air-drying time for 0 (without air-drying), 5 and 10 seconds. After light irradiation of the adhesives, the resin composites were condensed into a mold (phi4x2 mm) and polymerized. Ten samples per test group were stored in 37 degrees C distilled water for 24 hours; they were then shear tested at a crosshead speed of 1.0 mm/minute. One-way ANOVA followed by Tukey's HSD tests (alpha = 0.05) were done. FE-SEM observations of the resin/dentin interface were also conducted. Dentin bond strength varied with the different air drying times and ranged from 5.8 +/- 2.4 to 13.9 +/- 2.8 MPa for AP, 4.9 +/- 1.5 to 17.1 +/- 2.3 MPa for CT, 7.9 +/- 2.8 to 13.8 +/- 2.4 MPa for FB, 3.7 +/- 1.4 to 13.4 +/- 1.2 MPa for GB and 4.6 +/- 2.1 to 13.7 +/- 2.6 MPa for OF. With longer air drying of adhesives, no significant changes in bond strengths were found for the systems used except for OF. Significantly lower bond strengths were obtained for the 10-second air-drying group for OF. From FE-SEM observations, gaps between the cured adhesive and resin composites were observed for the specimens without the air drying of adhesives except for OF. The data suggests that, with four of the single-application self-etch adhesive systems, air drying is essential to obtain adequate dentin bond strengths, but increased drying time does not significantly influence bond strength. For the other system studied, the bond strength

Deformation Behavior of Human Dentin under Uniaxial Compression

Directory of Open Access Journals (Sweden)

Dmitry Zaytsev

2012-01-01

Full Text Available Deformation behavior of a human dentin under compression including size and rate effects is studied. No difference between mechanical properties of crown and root dentin is found. It is mechanically isotropic high elastic and strong hard tissue, which demonstrates considerable plasticity and ability to suppress a crack growth. Mechanical properties of dentin depend on a shape of samples and a deformation rate.

Direct linear measurement of root dentin thickness and dentin volume changes with post space preparation: A cone-beam computed tomography study

Directory of Open Access Journals (Sweden)

Shoeb Yakub Shaikh

2018-01-01

Full Text Available Aim: The purpose of the present study was direct linear measurement of dentin thickness and dentin volume changes for post space preparation with cone-beam computed tomography (CBCT. Materials and Methods: Ten maxillary central incisors were scanned, before and after root canal and post space preparation, with Orthophos XG three-dimensional hybrid unit. Thirteen axial section scans of each tooth from orifice to apex and dentin thickness for buccal, lingual, mesial, and distal were measured using proprietary measuring tool and thereafter subjected to statistical analysis. Furthermore, dentin volume was evaluated using ITK-SNAP software. Results: There was statistically significant difference between the dentin thickness in pre- and postinstrumentation (paired t-test and also between different groups (one-way ANOVA. In the shortest post length of 4.5mm the post space preparation resulted in 2.17% loss of hard tissue volume, where as 11mm longest post length post space preparation resulted in >40% loss of hard tissue volume. Conclusion: CBCT axial section scan for direct measurements of root dentin thickness can be guideline before and after post space preparation for selection of drill length and diameter.

Dentin biomodification: strategies, renewable resources and clinical applications.

Science.gov (United States)

Bedran-Russo, Ana K; Pauli, Guido F; Chen, Shao-Nong; McAlpine, James; Castellan, Carina S; Phansalkar, Rasika S; Aguiar, Thaiane R; Vidal, Cristina M P; Napotilano, José G; Nam, Joo-Won; Leme, Ariene A

2014-01-01

The biomodification of dentin is a biomimetic approach, mediated by bioactive agents, to enhance and reinforce the dentin by locally altering the biochemistry and biomechanical properties. This review provides an overview of key dentin matrix components, targeting effects of biomodification strategies, the chemistry of renewable natural sources, and current research on their potential clinical applications. The PubMed database and collected literature were used as a resource for peer-reviewed articles to highlight the topics of dentin hierarchical structure, biomodification agents, and laboratorial investigations of their clinical applications. In addition, new data is presented on laboratorial methods for the standardization of proanthocyanidin-rich preparations as a renewable source of plant-derived biomodification agents. Biomodification agents can be categorized as physical methods and chemical agents. Synthetic and naturally occurring chemical strategies present distinctive mechanism of interaction with the tissue. Initially thought to be driven only by inter- or intra-molecular collagen induced non-enzymatic cross-linking, multiple interactions with other dentin components are fundamental for the long-term biomechanics and biostability of the tissue. Oligomeric proanthocyanidins show promising bioactivity, and their chemical complexity requires systematic evaluation of the active compounds to produce a fully standardized intervention material from renewable resource, prior to their detailed clinical evaluation. Understanding the hierarchical structure of dentin and the targeting effect of the bioactive compounds will establish their use in both dentin-biomaterials interface and caries management. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

A comparison on the flexural strength of a new dental porcelain (D.} Dentin with Vita company Dentin porcelain (VMK 68N

Directory of Open Access Journals (Sweden)

Ghahramanloo A.

2004-06-01

Full Text Available Statement of Problem: Dental porcelain is one of the best materials ever used in dentistry. Excellent tissue"ncompatibility, esthetics, very low solubility in oral fluids, high compressive strength, and the lowest bacterial"nplaque accumulation on the glazed porcelain are some of its advantages. Porcelain brittleness due to its low"ntensile strength, impact strength and the occlusal attrition of opposing teeth enamel are some of its"ndisadvantages. The most important mechanical properties of dental porcelains are their flexural strength that is"nthe ability of a porcelain to resist fracture when loaded from above. Different ways have been proposed to"neliminate porcelain brittleness and develop its flexural strength, among which baking porcelain on a metal"nframework is more commonly used."nPurpose: Considering that restoration and replacement of teeth by porcelain fused to metal restorations is still"nthe most commonly used technique, the aim of the present study was to measure the flexural strength of a"nporcelain bonded to metal powder, D4 Dentin, and to compare it with Vita Dentin powder."nMaterials and Methods: In this experimental study, a stainless steel box, 25x5x2mm was made according to"nISO 6872: 1995 (E Standard and filled with D4 Dentin powder and Vita Dentin (VMK 68N and baked in"nVita furnace. Then 10 blocks of D^ Dentin and 10 of Vita Dentin were made. Samples were placed on the"nthree point bending test machine and force was applied the middle of each block. To analyze the data, t-"nstudent test and co-variance analysis were used."nResults: Mean flexural strength of D4 Dentin was 53.40±1.35 MPa and that of Vita Dentin was 53.86+7.38"nMPa. The difference was not statistically significant."nConclusion: According to ISO 6872: 1995 (E standard, the flexural strength of all D4 Dentin samples were"ngreater than 50 Mpa.

Survival of ceramic veneers made of different materials after a minimum follow-up period of five years: a systematic review and meta-analysis.

Science.gov (United States)

Petridis, Haralampos P; Zekeridou, Alkisti; Malliari, Maria; Tortopidis, Dimitrios; Koidis, Petros

2012-01-01

The purpose of this systematic review was to compare the survival and complication rates of ceramic veneers produced with different techniques and materials after a minimum follow-up time of 5 years. A literature search was conducted, using electronic databases, relevant references, citations and journal researching, for clinical studies reporting on the survival of ceramic veneers fabricated with different techniques and materials with a mean followup time of at least 5 years. The search period spanned from January 1980 up to October 2010. Event rates were calculated for the following complications associated with ceramic veneers: fracture, debonding, marginal discoloration, marginal integrity, and caries. Summary estimates, and 5-year event rates were reported. Comparison between subgroups of different materials, as well as statistical significance, was calculated using a mixed effects model. Nine studies were selected for final analysis over an initial yield of 409 titles. No study directly compared the incidence of complications between ceramic veneers fabricated from different materials. Four of the included studies reported on the survival of ceramic veneers made out of feldspathic ceramics; four studies were on glass-ceramic veneers and one study included veneers fabricated from both materials. The mean observation time ranged between 5 and 10 years. Overall, the 5-year complication rates were low, with the exception of studies reporting on extended ceramic veneers. The most frequent complication reported was marginal discoloration (9% at 5 years), followed by marginal integrity (3.9-7.7% at 5 years). There was no statistically significant difference in the event rates between the subgroups of different materials (feldspathic vs. glass-ceramic). The results of this systematic review showed that ceramic veneers fabricated from feldspathic or glass-ceramics have an adequate clinical survival for at least 5 years of clinical service, with very low complication

Variation on Molecular Structure, Crystallinity, and Optical Properties of Dentin Due to Nd:YAG Laser and Fluoride Aimed at Tooth Erosion Prevention

Science.gov (United States)

Freitas, Anderson Z.; Bachmann, Luciano; Benetti, Carolina; Ana, Patricia A.

2018-01-01

This in vitro study evaluated the compositional, crystalline, and morphological effects promoted by Nd:YAG laser on root dentin, and verified the effects of laser and topical acidulated phosphate fluoride application (APF-gel) on dentin erosion. 180 bovine dentin slabs were randomized into 4 groups (n = 45): G1–untreated, G2–APF-gel (1.23% F−, 4 min), G3–Nd:YAG (1064 nm, 84.9 J/cm2, 10 Hz), and G4–APF-gel application followed by Nd:YAG laser irradiation. The compositional, crystalline, and morphological effects promoted by treatments were investigated on five samples of each experimental group. The other samples were submitted to a 5-day, 10-day, or 15-day erosive and abrasive demineralization and remineralization cycling in order to create erosion lesions. The area and depth of lesions, as well as the optical attenuation coefficient, were assessed, and all data were statistically analysed (p laser promoted the reduction of carbonate, the formation of tetracalcium phosphate, as well as the melting and recrystallization of the dentin surface. Laser significantly decreased the area and depth of erosion lesions and altered the optical attenuation coefficient when compared to untreated and APF-gel groups, but the association of APF-gel and laser did not promote an additional effect. Nd:YAG laser irradiation can be a promissory treatment to prevent dentin erosion and the abrasion process. PMID:29389868

The effect of propolis fluoride on caries dentine activity

Science.gov (United States)

Darwita, Risqa Rina; Soekanto, Sri Angky; Finisha, Andanali Rhukul; Wahyuni, Hardiati Nur; Andiani, Salsabila Ghina

2018-02-01

This research was conducted to analyze the effect of propolis fluoride on the occurrence of arrested caries dentine surface. The design of the study was a clinical trial experimental. The respondent were primary school students aged 6-8 years, from primary school in Kukusan, Depok, West Java, Indonesia. They were screened of dental examination and the total number of 296 children with an age range of 6-8 year old were included in the study. All students who had dentin caries were get dental treatment with propolis fluoride topical application in dentin caries surface. After one month, two months and four months all students who were got propolis fluoride topical application in dentin caries surface were controlled. All data were analyzed by Wilcoxon test. The total number of dentinal decay of 296 student was 1740 surfaces indicated to Flolis topical application. After one, two and three months of Flolis application, all arrested of dentinal decay was evaluated, the result of evaluation from the second month to the third month evaluation was found that the arrested dentinal caries surfaces were decreased significantly at 29.36% (pcaries surface from the first month to the third month was decreased significantly at 38.62% (pcaries, and their ability to arrest dental caries was significantly different. Flolis was found to be effective in arresting dentinal caries surface until three months application, and should be repeated after 3 months of Flolis application.

Chemical treatment of the intra-canal dentin surface: a new approach to modify dentin hydrophobicity

Directory of Open Access Journals (Sweden)

Cesar GAITAN-FONSECA

2013-01-01

Full Text Available Objective This study evaluated the hydrophobicity of dentin surfaces that were modified through chemical silanization with octadecyltrichlorosilane (OTS. Material and Methods An in vitro experimental study was performed using 40 human permanent incisors that were divided into the following two groups: non-silanized and silanized. The specimens were pretreated and chemically modified with OTS. After the chemical modification, the dentin hydrophobicity was examined using a water contact angle measurement (WCA. The effectiveness of the modification of hydrophobicity was verified by the fluid permeability test (FPT. Results and Conclusions Statistically significant differences were found in the values of WCA and FPT between the two groups. After silanization, the hydrophobic intraradicular dentin surface exhibited in vitro properties that limit fluid penetration into the sealed root canal. This chemical treatment is a new approach for improving the sealing of the root canal system.

Transmission electron microscopical study of teenage crown dentin on the nanometer scale

Energy Technology Data Exchange (ETDEWEB)

Panfilov, Peter, E-mail: peter.panfilov@urfu.ru [Ural Federal University, Ekaterinburg (Russian Federation); Kabanova, Anna [Ural Federal University, Ekaterinburg (Russian Federation); Guo, Jinming; Zhang, Zaoli [Erich Schmid Institute for Materials Science, Austrian Academy of Sciences, Leoben (Austria)

2017-02-01

Statement of significance: This is the first transmission electron microscopic study of teenage crown dentin on the nanometer scale. Samples for TEM were prepared by mechanical thinning and chemical polishing that allowed obtaining the electron transparent foils. It was firstly shown that human dentin possesses the layered morphology: the layers are oriented normally to the main axis of a tooth and have the thickness of ~ 50 nm. HA inorganic phase of teenage crown dentin is in the amorphous state. The cellular structure, which was formed from collagen fibers (diameter is ~ 5 nm), are observed near DEJ region in teenage dentin, whereas bioorganic phase of teenage crown dentin near the pulp camera does not contain the collagen fibers. Cracks in dentin thin foils have sharp tips, but big angles of opening (~ 30{sup °}) with plastic zone ahead crack tip. It means that young crown human dentin exhibits ductile or viscous-elastic fracture behavior on the nanometer scale. - Highlights: • Dentin has layered morphology. • Mineral component of dentin is in amorphous state. • Collagen fibers form cellular structure in dentin. • Cracks in dentin behave by elastic-plastic manner.

Transmission electron microscopical study of teenage crown dentin on the nanometer scale

International Nuclear Information System (INIS)

Panfilov, Peter; Kabanova, Anna; Guo, Jinming; Zhang, Zaoli

2017-01-01

Statement of significance: This is the first transmission electron microscopic study of teenage crown dentin on the nanometer scale. Samples for TEM were prepared by mechanical thinning and chemical polishing that allowed obtaining the electron transparent foils. It was firstly shown that human dentin possesses the layered morphology: the layers are oriented normally to the main axis of a tooth and have the thickness of ~ 50 nm. HA inorganic phase of teenage crown dentin is in the amorphous state. The cellular structure, which was formed from collagen fibers (diameter is ~ 5 nm), are observed near DEJ region in teenage dentin, whereas bioorganic phase of teenage crown dentin near the pulp camera does not contain the collagen fibers. Cracks in dentin thin foils have sharp tips, but big angles of opening (~ 30 ° ) with plastic zone ahead crack tip. It means that young crown human dentin exhibits ductile or viscous-elastic fracture behavior on the nanometer scale. - Highlights: • Dentin has layered morphology. • Mineral component of dentin is in amorphous state. • Collagen fibers form cellular structure in dentin. • Cracks in dentin behave by elastic-plastic manner.

Carbodiimide Inactivation of MMPs and Effect on Dentin Bonding

Science.gov (United States)

Mazzoni, A.; Apolonio, F.M.; Saboia, V.P.A.; Santi, S.; Angeloni, V.; Checchi, V.; Curci, R.; Di Lenarda, R.; Tay, F.R.; Pashley, D.H.; Breschi, L.

2014-01-01

The use of protein cross-linking agents during bonding procedures has been recently proposed to improve bond durability. This study aimed to use zymography and in situ zymography techniques to evaluate the ability of 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide (EDC) cross-linker to inhibit matrix metalloproteinase (MMP) activity. The hypotheses tested were that: (1) bonding procedures increase dentin gelatinolytic activity and (2) EDC pre-treatment prevents this enzymatic activity. The zymographic assay was performed on protein extracts obtained from dentin powder treated with Optibond FL or Scotchbond 1XT with or without 0.3M EDC pre-treatment. For in situ zymography, adhesive/dentin interfaces were created with the same adhesives applied to acid-etched dentin slabs pre-treated or not with EDC conditioner. Zymograms revealed increased expression of dentin endogenous MMP-2 and -9 after adhesive application, while the use of EDC as a primer inactivated dentin gelatinases. Results of in situ zymograpy showed that hybrid layers of tested adhesives exhibited intense collagenolytic activity, while almost no fluorescence signal was detected when specimens were pre-treated with EDC. The correlative analysis used in this study demonstrated that EDC could contribute to inactivate endogenous dentin MMPs within the hybrid layer created by etch-and-rinse adhesives. PMID:24334409

Composite smile designs: the key to dental artistry.

Science.gov (United States)

Portalier, L

1997-01-01

Patients seeking to improve the appearance of their smiles have driven the profession toward more challenges in esthetic dentistry to answer their needs. Better smiles are being equated with better living. Direct composite veneering has gained tremendous popularity over the past few years because the procedure can be done in one single appointment for a reasonable fee with acceptable results. Materials recently put on the market require stratification build-up techniques to allow for the best natural results. In addition, the procedure gives patients the freedom of live communication and dentists the emotive artistic recreation of a smile composition in which anterior teeth can be designed and redesigned through freehand craftmanship, until both patient and dentist are pleased with the results. This review highlights the benefits of direct composite veneering, a very unique process to investigate more about tooth and smile designs, and suggests more effective communication between patient and dentist in order to achieve predictable results.

In vivo remineralization of dentin using an agarose hydrogel biomimetic mineralization system

Science.gov (United States)

Han, Min; Li, Quan-Li; Cao, Ying; Fang, Hui; Xia, Rong; Zhang, Zhi-Hong

2017-02-01

A novel agarose hydrogel biomimetic mineralization system loaded with calcium and phosphate was used to remineralize dentin and induce the oriented densely parallel packed HA layer on defective dentin surface in vivo in a rabbit model. Firstly, the enamel of the labial surface of rabbits’ incisor was removed and the dentin was exposed to oral environment. Secondly, the hydrogel biomimetic mineralization system was applied to the exposed dentin surface by using a custom tray. Finally, the teeth were extracted and evaluated by scanning electron microscopy, X-ray diffraction, and nanoindentation test after a certain time of mineralization intervals. The regenerated tissue on the dentin surface was composed of highly organised HA crystals. Densely packed along the c axis, these newly precipitated HA crystals were perpendicular to the underlying dental surface with a tight bond. The demineralized dentin was remineralized and dentinal tubules were occluded by the grown HA crystals. The nanohardness and elastic modulus of the regenerated tissue were similar to natural dentin. The results indicated a potential clinical use for repairing dentin-exposed related diseases, such as erosion, wear, and dentin hypersensitivity.

In vivo Dentin Caries Model using Rat Molars

OpenAIRE

Takashi, HIGASHI; Junji, TAGAMI; Nobuhiro, HANADA; Cariology and Operative Dentistry, Department of Restorative Sciences, Tokyo Medical and Dental University; Cariology and Operative Dentistry, Department of Restorative Sciences, Tokyo Medical and Dental University; Department of Oral Science The National Institute of Infectious Diseases(NIID)

2000-01-01

Experimental dentinal caries was induced in rat molars which were inoculated orally with Streptococcus mutans and maintained on a carionenic diet 2000. After 30 days on the diet, the rats were sacrificed. The caries lesions were confirmed with a caries detector, then nanohardness determination of caries dentin were measured with nanoindentation. After hardness measurement, the lesion was examined by SEM and EDS. Dentin caries in sixteen fissures was induced among 20 fissures in the mandibular...

Effect of bur-cut dentin on bond strength using two all-in-one and one two-step adhesive systems.

Science.gov (United States)

Koase, Kaori; Inoue, Satoshi; Noda, Mamoru; Tanaka, Toru; Kawamoto, Chiharu; Takahashi, Akiko; Nakaoki, Yasuko; Sano, Hidehiko

2004-01-01

To compare the microtensile bond strength (MTBS) of two all-in-one adhesive systems and one experimental two-step self-etching adhesive system to two types of bur-cut dentin. Using one of the three adhesives, Xeno CF Bond (Xeno), Prompt L-Pop (PL), or the experimental two-step system ABF (ABF), resin composite was bonded to flat buccal and root dentin surfaces of eight extracted human premolars. These surfaces were produced using either regular-grit or superfine-grit diamond burs. After storage overnight in 37 degrees C water, the bonded specimens were sectioned into six or seven slices approximately 0.7 mm thick perpendicular to the bonded surface. They were then subjected to microtensile testing. The surfaces of the fractured specimens were observed microscopically to determine the failure mode. In addition, to observe the effect of conditioning, the two types of bur-cut dentin surfaces were conditioned with the adhesives, rinsed with acetone, and observed with SEM. When Xeno and PL were bonded to dentin cut with a regular-grit diamond bur, MTBS values were lower than to superfine bur-cut dentin, and failures occurred adhesively at the interface, whereas the experimental two-step adhesive showed no significant difference in microtensile bond strength between two differently cut surfaces. The all-in-one adhesives tested here improved bond strengths when bonded to superfine bur-cut dentin as a substrate, whereas the experimental two-step adhesive system showed unchanged bonding to both regular and superfine bur-cut dentin surfaces.

Effect of adhesive system and application strategy on reduction of dentin permeability

Directory of Open Access Journals (Sweden)

Adriana Oliveira Carvalho

2012-10-01

Full Text Available This study evaluated the effect of adhesive systems and application strategies on dentin hydraulic conductance (HC. The buccal enamel was removed from bovine incisors to simulate laminate cavity preparations. After removing the roots and the coronal pulp, the buccal dentin was treated with EDTA solution (0.5 M for 5 minutes, rinsed, ultrasonicated for 12 minutes and connected to a permeability device. HC of the specimens was measured at 10 psi (n = 5. Permeability was measured before and after bonding procedures using G-Bond (GB, Clearfil Tri-S Bond (CTS, Hybrid Coat (HY, Bond Force (BF, Adper Easy Bond (AEB Silorane (SI, Clearfil SE Bond (CSE and Adper Scotchbond Multi-Purpose (SMP adhesives systems, which were applied following three strategies: 1 according to the manufacturers' instructions; 2 two coats of all-in-one self-etching adhesives (GB, CTS, HY, BF, AEB or priming step plus two coats of bonding resin for the other systems (SI, CSE and SMP; and 3 a thin layer of a flowable composite applied over one coat of all-in-one self-etching adhesives or primed surface for SI, CSE and SMP adhesives. No significant difference was observed among the application modes concerning their ability to reduce HC. None of the adhesives showed complete sealing (100% of the bovine tooth dentin. SI exhibited lower HC than SMP, however, they were not significantly different from the other systems. The results suggest that all systems tested result in an HC reduction of more than 90%. The wet bonding technique seemed to be more sensitive for dentin sealing.

Hybridization quality and bond strength of adhesive systems according to interaction with dentin.

Science.gov (United States)

Salvio, Luciana Andrea; Hipólito, Vinicius Di; Martins, Adriano Luis; de Goes, Mario Fernando

2013-07-01

To evaluate the hybridization quality and bond strength of adhesives to dentin. Ten human molars were ground to expose the dentin and then sectioned in four tooth-quarters. They were randomly divided into 5 groups according to the adhesive used: Two single-step self-etch adhesives - Adper Prompt (ADP) and Xeno III (XE), two two-step self-etching primer systems - Clearfil SE Bond (SE) and Adhe SE (ADSE), and one one-step etch-and-rinse system - Adper Single Bond (SB). Resin composite (Filtek Z250) crown buildups were made on the bonded surfaces and incrementally light-cured for 20 s. The restored tooth-quarters were stored in water at 37°C for 24 h and then sectioned into beams (0.8 mm(2) in cross-section). Maximal microtensile bond strength (μ-TBS) was recorded (0.5 mm/min in crosshead speed). The results were submitted to one-way ANOVA and Tukey's test (α = 0.05). Thirty additional teeth were used to investigate the hybridization quality by SEM using silver methenamine or ammoniacal silver nitrate dyes. SE reached significantly higher μ-TBS (P 0.05), and between SB and ADP (P > 0.05); ADSE and XE were significantly higher than SB and ADP (P quality than that observed for ADP and XE. The bond strength and hybridization quality were affected by the interaction form of the adhesives with dentin. The hybridization quality was essential to improve the immediate μ-TBS to dentin.

A micromechanics model of the elastic properties of human dentine

Energy Technology Data Exchange (ETDEWEB)

Kinney, J. H. [Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States); Balooch, M. [Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States); Marshall, G. W. [Univ. of California, San Francisco, CA (United States). Dept. of Restorative Dentistry; Marshall, S. J. [Univ. of California, San Francisco, CA (United States). Dept. of Restorative Dentistry

1999-10-01

A generalized self-consistent model of cylindrical inclusions in a homogeneous and isotropic matrix phase was used to study the effects of tubule orientation on the elastic properties of dentin. Closed form expressions for the five independent elastic constants of dentin were derived in terms of tubule concentration, and the Young's moduli and Poisson ratios of peri- and intertubular dentin. An atomic force microscope (AFM) indentation technique determined the Young's moduli of the peri- and intertubular dentin as approximately 30 GPa and 15 GPa, respectively. Over the natural variation in tubule density found in dentin, there was only a slight variation in the axial and transverse shear moduli with position in the tooth, and there was no measurable effect of tubule orientation. We conclude that tubule orientation has no appreciable effect on the elastic behavior of normal dentin, and that the elastic properties of healthy dentin can be modeled as an isotropic continuum with a Young's modulus of approximately 16 GPa and a shear modulus of 6.2 GPa.

Effect of various veneering techniques on mechanical strength of computer-controlled zirconia framework designs.

Science.gov (United States)

Kanat, Burcu; Cömlekoğlu, Erhan M; Dündar-Çömlekoğlu, Mine; Hakan Sen, Bilge; Ozcan, Mutlu; Ali Güngör, Mehmet

2014-08-01

The objectives of this study were to evaluate the fracture resistance (FR), flexural strength (FS), and shear bond strength (SBS) of zirconia framework material veneered with different methods and to assess the stress distributions using finite element analysis (FEA). Zirconia frameworks fabricated in the forms of crowns for FR, bars for FS, and disks for SBS (N = 90, n = 10) were veneered with either (a) file splitting (CAD-on) (CD), (b) layering (L), or (c) overpressing (P) methods. For crown specimens, stainless steel dies (N = 30; 1 mm chamfer) were scanned using the labside contrast spray. A bilayered design was produced for CD, whereas a reduced design (1 mm) was used for L and P to support the veneer by computer-aided design and manufacturing. For bar (1.5 × 5 × 25 mm(3) ) and disk (2.5 mm diameter, 2.5 mm height) specimens, zirconia blocks were sectioned under water cooling with a low-speed diamond saw and sintered. To prepare the suprastructures in the appropriate shapes for the three mechanical tests, nano-fluorapatite ceramic was layered and fired for L, fluorapatite-ceramic was pressed for P, and the milled lithium-disilicate ceramics were fused with zirconia by a thixotropic glass ceramic for CD and then sintered for crystallization of veneering ceramic. Crowns were then cemented to the metal dies. All specimens were stored at 37°C, 100% humidity for 48 hours. Mechanical tests were performed, and data were statistically analyzed (ANOVA, Tukey's, α = 0.05). Stereomicroscopy and scanning electron microscopy (SEM) were used to evaluate the failure modes and surface structure. FEA modeling of the crowns was obtained. Mean FR values (N ± SD) of CD (4408 ± 608) and L (4323 ± 462) were higher than P (2507 ± 594) (p mechanical tests, whereas a layering technique increased the FR when an anatomical core design was employed. File splitting (CAD-on) or layering veneering ceramic on zirconia with a reduced framework design may reduce ceramic chipping

Effect of composite warming on shear bond strength.

Science.gov (United States)

McDaniel, Thomas F; Sigrist, Thomas W; Johnson, Gary M

2018-01-01

Several manufacturers produce devices designed to warm composite resins used in restorative dentistry. Previous investigators have examined the effects of heating composite restorative resins prior to placement and polymerization. Heating has been reported to reduce viscosity, improve ease of placement, enhance monomer conversion, and reduce microleakage. The aim of the present study was to compare shear bond strengths of room temperature (22°C) and prewarmed (54°C) restorative composite resin. Extracted bovine mandibular incisors were sectioned sagittally and embedded in acrylic cylinders. Enamel was selectively etched with 37% phosphoric acid, rinsed, and dried. Self-etching primer was applied to both enamel and dentin. Self-etching adhesive was then applied and photopolymerized. Composite resin capsules were then divided into prewarmed and room temperature groups. Fourteen composite specimens prewarmed in an incubator were applied to the prepared enamel and dentin and photopolymerized. Fourteen room temperature composite specimens were likewise placed. After storage in water for 24 hours, all composite specimens were subjected to shear stress testing. The resulting data were analyzed with a t test (P = 0.05). There was no statistically significant difference between the shear bond strengths of the prewarmed and room temperature composite resin specimens. Warming does not appear to affect bond strength of composite resin bonded to both dentin and enamel.

Dentin-bonded all-ceramic crowns: current status.

Science.gov (United States)

Burke, F J; Qualtrough, A J; Hale, R W

1998-04-01

Dentin-bonded all-ceramic crowns employ contemporary techniques to lute the crown to the tooth using a resin luting material and dentin-bonding system. The advantages of these crowns are that they provide good esthetics and fracture resistance and can be used in cases of substantial tooth loss. Their principal disadvantages are that the luting procedure is more time-consuming and that these crowns should not be used where margins are subgingival. Dentin-bonded all-ceramic crowns may be a useful addition to the dentist's armamentarium, but long-term clinical studies are needed to fully assess their performance.

Mineral content analysis of root canal dentin using laser-induced breakdown spectroscopy

Science.gov (United States)

2018-01-01

Objectives This study aimed to introduce the use of laser-induced breakdown spectroscopy (LIBS) for evaluation of the mineral content of root canal dentin, and to assess whether a correlation exists between LIBS and scanning electron microscopy/energy dispersive spectroscopy (SEM/EDS) methods by comparing the effects of irrigation solutions on the mineral content change of root canal dentin. Materials and Methods Forty teeth with a single root canal were decoronated and longitudinally sectioned to expose the canals. The root halves were divided into 4 groups (n = 10) according to the solution applied: group NaOCl, 5.25% sodium hypochlorite (NaOCl) for 1 hour; group EDTA, 17% ethylenediaminetetraacetic acid (EDTA) for 2 minutes; group NaOCl+EDTA, 5.25% NaOCl for 1 hour and 17% EDTA for 2 minutes; a control group. Each root half belonging to the same root was evaluated for mineral content with either LIBS or SEM/EDS methods. The data were analyzed statistically. Results In groups NaOCl and NaOCl+EDTA, the calcium (Ca)/phosphorus (P) ratio decreased while the sodium (Na) level increased compared with the other groups (p LIBS and SEM/EDS analyses (r = 0.84, p LIBS method proved to be reliable while providing data for the elemental composition of root canal dentin. PMID:29487841

[Biocompatibility of crown and bridge materials. 1. Substances in contact with dentin].

Science.gov (United States)

Klotzer, W T

1989-11-01

It is mandatory that the materials and drugs used in restorative dentistry be free from side effects resulting in potential tooth loss or irreversible damage to vital dental tissues. Up to now there have been no reliable in vitro methods available for the evaluation of pulp reactions. Since numerous different materials and drugs are successively applied to prepared dentine, pulp reactions are caused by cumulative action, and the causative factors, except for extremely toxic substances, cannot be revealed by clinical and/or posttreatment studies alone. At present, the evaluation of pulp reactions must still rely on histologic studies using human or animal teeth. Reports on pulp reactions to materials and drugs are reviewed. Few dependable figures have been reported on pulp reactions to dentinal medication, "sterilization", disinfectants and on the biologic response to and effectiveness of varnishes, liners, desensitizing agents, smear-layer removers, etc. Resins and composite materials seem to provoke acute reactions, mainly by the heat generated during setting, and chronic reactions due to the stimulation of bacterial growth. Except for glass ionomer cements, most of the publications show a high degree of agreement on the tissue reactions to luting agents. Regarding dentine bonding agents, however, it has not been possible to draw any conclusions, so far.

Association between Severity of Tooth Wear and Dentinal Hypersensitivity

Directory of Open Access Journals (Sweden)

Ashok Ayer

2016-11-01

Full Text Available Background & Objectives: Tooth wear (attrition, abrasion, erosion, and abfraction is perceived globally as ever increasing problem. Several outcome of the tooth wear are hypersensitivity, esthetic problems, functional impairment, annoyance to the patient, and fracture of the tooth. Among these, the measurable and more commonly reported outcome is hypersensitivity to stimuli. Although dentin hypersensitivity is a common clinical condition and is generally reported by the patient after experiencing a sharp, short pain caused by one of the several different external stimuli, it is often inadequately understood. None of the scientific literature available till date attempted to establish the relationship between tooth wear and dentin hypersensitivity which could be a key factor in monitoring those patients.  The aim of the study was to estimate the association between severity of teeth wear and sensitivity in the patients with reported dentinal hypersensitivity.Materials & Methods: Fifty patients with dentin hypersensitivity were investigated for tooth wear. Tooth wear measured using exact tooth wear index and level of sensitivity to stimuli was recorded using a numerical rating scale. Results: Enamel wear at cervical region of teeth showed a positive correlation (p=.010, similarly, dentin wear at cervical region of teeth showed positive correlation and significant association (p<.001 with dentinal hypersensitivity.Conclusion: The observation supports a significant association between severities of tooth surface wear and dentinal hypersensitivity.

[The durability of three self-etch adhesives bonded to dentin].

Science.gov (United States)

Tian, Fu-Cong; Wang, Xiao-Yan; Gao, Xue-Jun

2013-04-01

To investigate the durability of self-etch adhesives bonded to dentin in vitro. Forty-two extracted human molars were selected and occlusal dentin surfaces were exposed. The teeth were randomly distributed into three groups based on adhesives applied. The one-step self-etch adhesive B(Adper Prompt) and C(G-Bond) and two-step self-etch adhesive A (Clearfil SE bond) were used. After application of the adhesives to the dentin surfaces, composite crowns were built up, after 24 h water storage, the teeth were sectioned longitudinally into sticks (1.0 mm×1.0 mm bonding area) for microtensile testing or slabs (1 mm thick) for scanning electron microscopec (SEM) observation. Bonding strength (mTBS) and nano-leakage were evaluated immediately after cutting or after 6 months in water. The mTBS was analyzed using one-way ANOVA (SPSS 13.0). The nanoleakage was observed by SEM with a backscattered electron detector. Both adhesives and water storage time affected the mTBS. All adhesives showed decreased bond strength after six-month water aging [A dropped from (40.60 ± 5.76) MPa to (36.04 ± 3.15) MPa; B dropped from (19.06 ± 1.50) MPa to (11.19 ± 1.97) MPa; C dropped from (17.75 ± 1.10) MPa to (9.14 ± 1.15) MPa] (P adhesives tested were probably influenced by water aging, however, the two-step adhesive showed better durability than the one-step adhesives.

Residual stress profiles in veneering ceramic on Y-TZP, alumina and ZTA frameworks: measurement by hole-drilling.

Science.gov (United States)

Fukushima, K A; Sadoun, M J; Cesar, P F; Mainjot, A K

2014-02-01

The residual stress profile developed within the veneering ceramic during the manufacturing process is an important predicting factor in chipping failures, which constitute a well-known problem with yttria-tetragonal-zirconia polycrystal (Y-TZP) based restorations. The objectives of this study are to measure and to compare the residual stress profile in the veneering ceramic layered on three different polycrystalline ceramic framework materials: Y-TZP, alumina polycrystal (AL) and zirconia toughened alumina (ZTA). The stress profile was measured with the hole-drilling method in bilayered disk samples of 19 mm diameter with a 0.7 mm thick Y-TZP, AL or ZTA framework and a 1.5mm thick layer of the corresponding veneering ceramic. The AL samples exhibited increasing compressive stresses with depth, while compressive stresses switching into interior tensile stresses were measured in Y-TZP samples. ZTA samples exhibited compressive stress at the ceramic surface, decreasing with depth up to 0.6mm from the surface, and then becoming compressive again near the framework. Y-TZP samples exhibited a less favorable stress profile than those of AL and ZTA samples. Results support the hypothesis of the occurrence of structural changes within the Y-TZP surface in contact with the veneering ceramic to explain the presence of tensile stresses. Even if the presence of Y-TZP in the alumina matrix seems to negatively affect the residual stress profiles in ZTA samples in comparison with AL samples, the registered profiles remain positive in terms of veneer fracture resistance. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of 10% sodium bicarbonate on bond strength of enamel and dentin after bleaching with 38% hydrogen peroxide

Directory of Open Access Journals (Sweden)

Fernanda Medeiros Darzé

Full Text Available AbstractIntroductionBy-products of hydrogen peroxide degradation released during dental bleaching influence the polymerization of adhesive systems and composite resins, causing a reduction in shear bond strength to the tooth.Objectivethe aim of this article was to evaluate the effect of 10% sodium bicarbonate (SB, applied for different lengths of time, on the shear bond strength to enamel and dentin after bleaching.Material and methodEnamel and dentin blocks were divided into groups (n=10: (1 control: no bleaching; (2 immediate: bleaching immediately followed by restoration; (3 14-day: bleaching, restoration 14 days later; (4 SB for 10 minutes: bleaching, SB gel for 10 minutes, immediately followed by restoration; (5 SB for 20 minutes: bleaching, SB gel for 20 minutes, immediately followed by restoration. A 38% hydrogen peroxide gel (Opalescence Boost/Ultradent was used. After application of the adhesive system, composite resin cylinders were mounted on the surface of the substrates in order to test shear bond strength. Result: ANOVA and Tukey tests showed significantly higher mean enamel bond strength values for the 14-day follow-up group and without significant differences for control group. Mean bond strength values obtained for the other groups were intermediate. When testing dentin, the Tukey test revealed a significantly higher mean bond strength value for the 14-day follow-up group when compared with application of SB for 20 minutes.ConclusionSB gel applied was unable to reverse the low bond strength to enamel and dentin after bleaching treatment.

Shear Bond Strengths and Morphological Evaluation of Filled and Unfilled Adhesive Interfaces to Enamel and Dentine

Science.gov (United States)

Mortazavi, Vajihesadat; Fathi, Mohammadhosein; Ataei, Ebrahim; Khodaeian, Niloufar; Askari, Navid

2012-01-01

In this laboratory study shear bond strengths of three filled and one unfilled adhesive systems to enamel and dentine were compared. Forty-eight extracted intact noncarious human mandibular molars were randomly assigned to two groups of 24 one for bonding to enamel and the other for bonding to dentine. Buccal and lingual surfaces of each tooth were randomly assigned for application of each one of filled (Prime & Bond NT (PBNT), Optibond Solo Plus (OBSP), and Clearfil SE Bond (CSEB)) and unfilled (Single Bond (SB)) adhesive systems (n = 12). A universal resin composite was placed into the translucent plastic cylinders (3 mm in diameter and 2 mm in length) and seated against the enamel and dentine surfaces and polymerized for 40 seconds. Shear bond strength was determined using a universal testing machine, and the results were statistically analyzed using two-way ANOVA, one-way ANOVA, t-test, and Tukey HSD post hoc test with a 5% level of significance.There were no statistically significant differences in bond strength between the adhesive systems in enamel, but CSEB and SB exhibited significantly higher and lower bond strength to dentine, respectively, than the other tested adhesive systems while there were no statistically significant differences between PBNT and OBSP. PMID:23209471

Shear Bond Strengths and Morphological Evaluation of Filled and Unfilled Adhesive Interfaces to Enamel and Dentine

Directory of Open Access Journals (Sweden)

Vajihesadat Mortazavi

2012-01-01

Full Text Available In this laboratory study shear bond strengths of three filled and one unfilled adhesive systems to enamel and dentine were compared. Forty-eight extracted intact noncarious human mandibular molars were randomly assigned to two groups of 24 one for bonding to enamel and the other for bonding to dentine. Buccal and lingual surfaces of each tooth were randomly assigned for application of each one of filled (Prime & Bond NT (PBNT, Optibond Solo Plus (OBSP, and Clearfil SE Bond (CSEB and unfilled (Single Bond (SB adhesive systems (n=12. A universal resin composite was placed into the translucent plastic cylinders (3 mm in diameter and 2 mm in length and seated against the enamel and dentine surfaces and polymerized for 40 seconds. Shear bond strength was determined using a universal testing machine, and the results were statistically analyzed using two-way ANOVA, one-way ANOVA, t-test, and Tukey HSD post hoc test with a 5% level of significance.There were no statistically significant differences in bond strength between the adhesive systems in enamel, but CSEB and SB exhibited significantly higher and lower bond strength to dentine, respectively, than the other tested adhesive systems while there were no statistically significant differences between PBNT and OBSP.

[Mantle dentin as biomodel of materials for structural teeth restoration].

Science.gov (United States)

Starodubova, A V; Vinnichenko, Yu A; Pourovskaya, I Ya; Rusanov, F S

The article describes a structural element of natural teeth - mantle dentin. It has been shown that the presence of this element in the structure of a natural tooth largely ensures its strength under the influence of repeated loads in a functional oral environment and arrests crack growth at the enamel/dentine interface. This later effect is explained by the influence of a thin layer of mantle dentine, which has physical and mechanical characteristics different from that of the main dentin.

Bond strength of compomers to dentin using acidic primers.

Science.gov (United States)

Tate, W H; You, C; Powers, J M

1999-10-01

To determine the in vitro bond strengths of seven compomer/bonding agent restorative systems to human dentin. Seven compomer/bonding agents were bonded to human dentin, stored in water at 37 degrees C for 24 hours, and debonded in tension. Bonding conditions were with and without phosphoric acid etching, with and without the use of combined primer/bonding agents, and under moist and wet bond interfaces. Without phosphoric acid etching, F2000/F2000 Compomer Primer/Adhesive and F2000/Single Bond Dental Adhesive System were less sensitive to dentin wetness. With moist dentin, bond strengths of Dyract/Prime & Bond 2.1, Dyract AP/Prime & Bond 2.1, Hytac/OSB light-curing, one-component bonding agent, F2000/Single Bond, and Freedom/STAE single component light-cured dentin/enamel adhesive system, were improved with phosphoric acid etching. Also, with moist dentin, the bond strength of F2000/F2000 Compomer Primer/Adhesive in the 3M Clicker dispensing system was higher without phosphoric acid etching, whereas bonds of Compoglass/Syntac Single-component were not affected by phosphoric acid etching. Bonding did not occur without primer/bonding agent, regardless of surface condition or use of phosphoric acid etching.

In vivo model for microbial invasion of tooth root dentinal tubules

Directory of Open Access Journals (Sweden)

Jane L. BRITTAN

2016-04-01

Full Text Available ABSTRACT Objective Bacterial penetration of dentinal tubules via exposed dentine can lead to root caries and promote infections of the pulp and root canal system. The aim of this work was to develop a new experimental model for studying bacterial invasion of dentinal tubules within the human oral cavity. Material and Methods Sections of human root dentine were mounted into lower oral appliances that were worn by four human subjects for 15 d. Roots were then fixed, sectioned, stained and examined microscopically for evidence of bacterial invasion. Levels of invasion were expressed as Tubule Invasion Factor (TIF. DNA was extracted from root samples, subjected to polymerase chain reaction amplification of 16S rRNA genes, and invading bacteria were identified by comparison of sequences with GenBank database. Results All root dentine samples with patent tubules showed evidence of bacterial cell invasion (TIF value range from 5.7 to 9.0 to depths of 200 mm or more. A spectrum of Gram-positive and Gram-negative cell morphotypes were visualized, and molecular typing identified species of Granulicatella, Streptococcus, Klebsiella, Enterobacter, Acinetobacter, and Pseudomonas as dentinal tubule residents. Conclusion A novel in vivo model is described, which provides for human root dentine to be efficiently infected by oral microorganisms. A range of bacteria were able to initially invade dentinal tubules within exposed dentine. The model will be useful for testing the effectiveness of antiseptics, irrigants, and potential tubule occluding agents in preventing bacterial invasion of dentine.

Interfacial Chemistry of Moisture-Aged Class II Composite Restorations

Science.gov (United States)

Spencer, Paulette; Wang, Yong; Bohaty, Brenda

2007-01-01

Under in vivo conditions, the adhesive/dentin bond at the gingival margin of class II composite restorations can be the first defense against substances that may penetrate and ultimately undermine the composite restoration. Deterioration of this bond during aqueous aging is an area of intense investigation, but to date, the majority of our techniques have provided only an indirect assessment of the degrading components. The purpose of this study was to analyze the in situ molecular structure of adhesive/dentin interfaces in class II composite restorations, following aging in aqueous solutions. Class II preparations were cut from 12 unerupted human third molars, with a water-cooled, high-speed, dental handpiece. The prepared teeth were randomly selected for restoration with single bond (SB) and Z100 (3M). Teeth were restored, as per the manufacturer’s directions, under environmental conditions that simulated humidity and temperature characteristics of the oral cavity. Restored teeth were kept in sterile Delbecco’s phosphate saline for 48 h or 90 days. The samples were sectioned occlusogingivally and micro-Raman spectra were acquired at ~1.5 μm spatial resolution across the composite/adhesive/dentin interfaces at the gingival margins. Samples were wet throughout spectral acquisition. The relative intensity of bands associated with the adhesive in the interfacial region decreased dramatically after aqueous storage. This decrease in concert with the similar depth of dentin demineralization provides direct spectroscopic evidence of leaching of adhesive monomer from the interface during the 90 days of storage. SB adhesive infiltrated 4 –5 μm of 12-μm demineralized dentin at the gingival margin. After 90 days of aqueous storage, SB adhesive infiltration was reduced to ~2 μm, leaving ~10 μm of demineralized dentin collagen exposed at the gingival margin. The unprotected collagen at the gingival margin of the aged class II composite restorations was disorganized

Comparison of Marginal and Internal Adaptation of Heat-Pressed and CAD/CAM Porcelain Laminate Veneers and a 2-Year Follow-Up.

Science.gov (United States)

Yuce, Mert; Ulusoy, Mubin; Turk, Ayse Gozde

2017-12-22

To compare marginal and internal adaptations of porcelain laminate veneers fabricated with heat-pressed and CAD/CAM techniques, and to evaluate the clinical performances 2 years after cementation. Thirty heat-pressed and 31 CAD/CAM porcelain laminate veneers were fabricated for 12 patients. Silicone replicas of each veneer were obtained. Replicas were sectioned into 4 parts to measure adaptations of the veneers. A stereomicroscope was used to measure from 3 locations of replicas for marginal, and 9 locations for internal adaptations at 40x magnification. Clinical evaluations were done at baseline and 6, 12, 18, and 24 months after cementation according to the modified United States Public Health Service (USPHS) criteria. Independent samples t-test compared the adaptation values between heat-pressed and CAD/CAM groups. Paired t-test was used to evaluate marginal and internal adaptations of each group. Differences between the modified USPHS criteria ratings of heat-pressed and CAD/CAM groups were determined by the Mann-Whitney U test. Kaplan-Meier analysis was used to analyze the survival ratings of the veneers (p CAD/CAM veneers were 295 and 314.98 μm, respectively, and there was no statistically significant difference (p = 0.541). Internal adaptation values of groups were not statistically different either (201.82 μm for heat pressed; 195.47 μm for CAD/CAM p = 0.734). When marginal and internal adaptation values were compared within groups, there were significant differences both for heat-pressed (p CAD/CAM (p CAD/CAM or heat-pressed, had no effect on the marginal and internal adaptation of porcelain laminate veneers. The results showed that both fabrication techniques performed well after 2 years of clinical performance. © 2017 by the American College of Prosthodontists.

Viscoelastic finite element analysis of residual stresses in porcelain-veneered zirconia dental crowns.

Science.gov (United States)

Kim, Jeongho; Dhital, Sukirti; Zhivago, Paul; Kaizer, Marina R; Zhang, Yu

2018-06-01

The main problem of porcelain-veneered zirconia (PVZ) dental restorations is chipping and delamination of veneering porcelain owing to the development of deleterious residual stresses during the cooling phase of veneer firing. The aim of this study is to elucidate the effects of cooling rate, thermal contraction coefficient and elastic modulus on residual stresses developed in PVZ dental crowns using viscoelastic finite element methods (VFEM). A three-dimensional VFEM model has been developed to predict residual stresses in PVZ structures using ABAQUS finite element software and user subroutines. First, the newly established model was validated with experimentally measured residual stress profiles using Vickers indentation on flat PVZ specimens. An excellent agreement between the model prediction and experimental data was found. Then, the model was used to predict residual stresses in more complex anatomically-correct crown systems. Two PVZ crown systems with different thermal contraction coefficients and porcelain moduli were studied: VM9/Y-TZP and LAVA/Y-TZP. A sequential dual-step finite element analysis was performed: heat transfer analysis and viscoelastic stress analysis. Controlled and bench convection cooling rates were simulated by applying different convective heat transfer coefficients 1.7E-5 W/mm 2 °C (controlled cooling) and 0.6E-4 W/mm 2 °C (bench cooling) on the crown surfaces exposed to the air. Rigorous viscoelastic finite element analysis revealed that controlled cooling results in lower maximum stresses in both veneer and core layers for the two PVZ systems relative to bench cooling. Better compatibility of thermal contraction coefficients between porcelain and zirconia and a lower porcelain modulus reduce residual stresses in both layers. Copyright © 2018 Elsevier Ltd. All rights reserved.

Water evaporation from substrate tooth surface during dentin treatments.

Science.gov (United States)

Kusunoki, Mizuho; Itoh, Kazuo; Gokan, Yuka; Nagai, Yoshitaka; Tani, Chihiro; Hisamitsu, Hisashi

2011-01-01

The purpose of this study was to evaluate changes in the quantity of water evaporation from tooth surfaces. The amount of water evaporation was measured using Multi probe adapter MPA5 and Tewameter TM300 (Courage+Khazaka Electric GmbH, Köln, Germany) after acid etching and GM priming of enamel; and after EDTA conditioning and GM priming of dentin. The results indicated that the amount of water evaporation from the enamel surface was significantly less than that from the dentin. Acid etching did not affect the water evaporation from enamel, though GM priming significantly decreased the evaporation (83.48 ± 15.14% of that before priming). The evaporation from dentin was significantly increased by EDTA conditioning (131.38 ± 42.08% of that before conditioning) and significantly reduced by GM priming (80.26 ± 7.43% of that before priming). It was concluded that dentin priming reduced water evaporation from the dentin surface.

Optothermal transfer simulation in laser-irradiated human dentin.

Science.gov (United States)

Moriyama, Eduardo H; Zangaro, Renato A; Lobo, Paulo D C; Villaverde, Antonio Balbin; Pacheco, Marcos T; Watanabe, Ii-Sei; Vitkin, Alex

2003-04-01

Laser technology has been studied as a potential replacement to the conventional dental drill. However, to prevent pulpal cell damage, information related to the safety parameters using high-power lasers in oral mineralized tissues is needed. In this study, the heat distribution profiles at the surface and subsurface regions of human dentine samples irradiated with a Nd:YAG laser were simulated using Crank-Nicolson's finite difference method for different laser energies and pulse durations. Heat distribution throughout the dentin layer, from the external dentin surface to the pulp chamber wall, were calculated in each case, to investigate the details of pulsed laser-hard dental tissue interactions. The results showed that the final temperature at the pulp chamber wall and at the dentin surface are strongly dependent on the pulse duration, exposure time, and the energy contained in each pulse.

Effects of particles thickness and veneer reiforced layer in the properties of oriented strand boards OSB

Directory of Open Access Journals (Sweden)

Setsuo Iwakiri

2009-03-01

Full Text Available This work evaluated the effects of particle thickness and veneer reinforced layer on the physical and mechanicalproperties of OSB made of Pinus taeda L. The boards were manufactured with particle thickness of 0.4, 0.7 and 1.0 mm and phenolformaldehyderesin in the proportion of 6% of solid content. To the veneer reinforced layer was used veneer from Pinus taeda with 2.0mm of thickness. The increase in the slenderness (length/thickness ratio of thins particles, results in the higher values of MOE andMOR in the cross direction. The increase in the particles thickness contributed to higher values of the board internal bond. Thedifferent particles thickness did not clearly affected on the physical properties of OSB. The veneer reinforced layer results in the higheraverage values of MOE and MOR in the cross direction. All of the results of MOE and MOR obtained for boards with differentthickness attend tominimum values required per CSA 0437 (CSA, 1993. For the internal bond, the results were satisfactory to boardsmanufactured with particles thickness of 0.7 and 1.0 mm. According to the results the main conclusions were: (i The increase in theparticles thickness contributed to lower values of MOE and MOR, and higher values of the board internal bond; (ii the veneerreinforced layer increased MOE and MOR values in the cross direction.

Experimental etch-and-rinse adhesive systems containing MMP-inhibitors: Physicochemical characterization and resin-dentin bonding stability.

Science.gov (United States)

da Silva, Eduardo Moreira; de Sá Rodrigues, Carolina Ullmann Fernandes; de Oliveira Matos, Marcos Paulo; de Carvalho, Thais Rodrigues; dos Santos, Glauco Botelho; Amaral, Cristiane Mariote

2015-12-01

To evaluate the degree of conversion (DC%), water sorption (WS), solubility (SO) and the resin-dentin bonding stability (μTBS) of experimental (EXP) etch-and-rinse adhesive systems containing MMP-inhibitors: Galardin-GAL, Batimastat-BAT, GM1489-GM1 and chlorhexidine diacetate-CHX. DC% was measured using FT-IR spectroscopy, while WS and SO were calculated based on ISO4049. Thirty-six human molars were wet ground until the occlusal dentin was exposed. The adhesive systems were applied and resin composite buildups were incrementally constructed. After 24 h immersion in distilled water at 37 °C, the specimens were cut into resin-dentin beams with a cross-sectional area of 1 mm(2). The μTBS was evaluated after 24 h, 6 months and 12 months of water storage at 37 °C. Adper Single Bond 2 (SB2) was used as a commercial control. The data were analyzed using ANOVA and Tukey's HSD test. SB2 presented the highest DC% (p0.05). SO was found to be not significant (p>0.05). All adhesive systems maintained μTBS stability after 6 months of water storage. Only BAT, GM1 and CHX maintained μTBs stability after 12 months of water storage. The experimental adhesive systems with GM1489 and chlorhexidine diacetate presented the best physicochemical properties and preserved resin-dentin bonding stability after 12 months of water storage. GM1489 could be suitable for inclusion as an MMP-inhibitor in etch-and-rinse adhesive systems to maintain resin-dentin bonding stability over time. Copyright © 2015. Published by Elsevier Ltd.

Veneered zirconia inlay-retained fixed dental prostheses: 10-Year results from a prospective clinical study.

Science.gov (United States)

Rathmann, Friederike; Bömicke, Wolfgang; Rammelsberg, Peter; Ohlmann, Brigitte

2017-09-01

The purpose of this study was to evaluate the 10-year clinical performance of zirconia-based inlay-retained fixed dental prostheses (IRFDP). For replacement of a molar in 27 patients, 30 IRFDP were luted by use of different cements, Panavia F (Kuraray Europe GmbH) or Multilink Automix (Ivoclar Vivadent GmbH), with use of inlay/inlay, inlay/full-crown, or inlay/partial-crown retainers for anchorage. Frameworks were milled from yttria-stabilized zirconia (IPS e.maxZirCAD; Ivoclar Vivadent GmbH) and fully veneered with pressable ceramic (IPS e.max ZirPress; Ivoclar Vivadent GmbH). Before luting, the IRFDP were silica-coated (Rocatec; 3M Espe) and silanized (Monobond S; Ivoclar Vivadent GmbH). Complications (for example, chipping or delamination of the veneering ceramic, debonding, secondary caries, endodontic treatment, and abutment tooth fracture) and failure were reported, by use of standardized report forms, 2 weeks, 6 months, and 1, 2, and 10 years after cementation. Statistical analysis included Kaplan-Meier survival and success (complication-free survival) and Cox regression analysis (α=0.05 for all). During the 10-year observation period, the complications most often observed were chipping of the veneer and debonding. Twenty-five restorations failed and one participant dropped out. Cumulative 10-year survival and success were 12.1% and 0%, respectively. The design of the retainer, use of a dental dam, choice of cement, and location in the dental arch had no statistically significant effect on the occurrence of complications. Use of fully veneered zirconia-based IRFDP with this technique cannot be recommended. A large incidence of complications and poor survival were observed for fully veneered zirconia-based IRFDP, revealing an urgent need for further design improvements for this type of restoration. This, again, emphasizes the need for testing of new restoration designs in clinical trials before implementation in general dental practice. Copyright © 2017

Effectiveness of immediate bonding of etch-and-rinse adhesives to simplified ethanol-saturated dentin

Directory of Open Access Journals (Sweden)

Leandro Afonso Guimarães

2012-04-01

Full Text Available This study examined the immediate bond strength of etch-and-rinse adhesives to demineralized dentin saturated with either water or absolute ethanol. The research hypothesis was that there would be no difference in bond strength to dentin between water or ethanol wet-bonding techniques. The medium dentin of 20 third molars was exposed (n = 5. The dentin surface was then acid-etched, left moist and randomly assigned to be saturated via either water wet-bonding (WBT or absolute ethanol wet-bonding (EBT. The specimens were then treated with one of the following etch-and-rinse adhesive systems: a 3-step, water-based system (Adper Scotchbond Multipurpose, or SBMP or a 2-step, ethanol/water-based system (Adper Single Bond 2, or SB. Resin composite build-ups were then incrementally constructed. After water storage for 24 h at 37°C, the tensile strength of the specimens was tested in a universal testing machine (0.5 mm/min. Data were analyzed by two-way ANOVA and Tukey's test (a = 5%. The failure modes were verified using a stereomicroscope (40'. For both adhesives, no significant difference in bond strength was observed between WBT and EBT (p > 0.05. The highest bond strength was observed for SB, regardless of the bonding technique (p < 0.05. No significant interaction between adhesives and bonding techniques was noticed (p = 0.597. There was a predominance of adhesive failures for all tested groups. The EBT and WBT displayed similar immediate bond strength means for both adhesives. The SB adhesive exhibited higher means for all conditions tested. Further investigations are needed to evaluate long-term bonding to dentin mediated by commercial etch-and-rinse adhesives using the EBT approach.

Development of a Direct Pulp-capping Model for the Evaluation of Pulpal Wound Healing and Reparative Dentin Formation in Mice.

Science.gov (United States)

Song, Minju; Kim, Sol; Kim, Terresa; Park, Sil; Shin, Ki-Hyuk; Kang, Mo; Park, No-Hee; Kim, Reuben

2017-01-12

Dental pulp is a vital organ of a tooth fully protected by enamel and dentin. When the pulp is exposed due to cariogenic or iatrogenic injuries, it is often capped with biocompatible materials in order to expedite pulpal wound healing. The ultimate goal is to regenerate reparative dentin, a physical barrier that functions as a "biological seal" and protects the underlying pulp tissue. Although this direct pulp-capping procedure has long been used in dentistry, the underlying molecular mechanism of pulpal wound healing and reparative dentin formation is still poorly understood. To induce reparative dentin, pulp capping has been performed experimentally in large animals, but less so in mice, presumably due to their small sizes and the ensuing technical difficulties. Here, we present a detailed, step-by-step method of performing a pulp-capping procedure in mice, including the preparation of a Class-I-like cavity, the placement of pulp-capping materials, and the restoration procedure using dental composite. Our pulp-capping mouse model will be instrumental in investigating the fundamental molecular mechanisms of pulpal wound healing in the context of reparative dentin in vivo by enabling the use of transgenic or knockout mice that are widely available in the research community.

Accelerated fatigue of dentin with exposure to lactic acid.

Science.gov (United States)

Do, D; Orrego, S; Majd, H; Ryou, H; Mutluay, M M; Xu, Hockin H K; Arola, D

2013-11-01

Composite restorations accumulate more biofilm than other dental materials. This increases the likelihood for the hard tissues supporting a restoration (i.e. dentin and enamel) to be exposed to acidic conditions beyond that resulting from dietary variations. In this investigation the fatigue strength and fatigue crack growth resistance of human coronal dentin were characterized within a lactic acid solution (with pH = 5) and compared to that of controls evaluated in neutral conditions (pH = 7). A comparison of the fatigue life distributions showed that the lactic acid exposure resulted in a significant reduction in the fatigue strength (p ≤ 0.001), and nearly 30% reduction in the apparent endurance limit (from 44 MPa to 32 MPa). The reduction in pH also caused a significant decrease (p ≤ 0.05) in the threshold stress intensity range required for the initiation of cyclic crack growth, and significant increase in the incremental rate of crack extension. Exposure of tooth structure to lactic acid may cause demineralization, but it also increases the likelihood of restored tooth failures via fatigue, and after short time periods. © 2013 Elsevier Ltd. All rights reserved.

Interfacial micromorphological differences in hybrid layer formation between water- and solvent-based dentin bonding systems.

Science.gov (United States)

Gregoire, Geneviève L; Akon, Bernadette A; Millas, Arlette

2002-06-01

Many dentin bonding systems of different compositions, and in particular containing different solvents, have been introduced to the market. Their effect on the quality of the interface requires clarification by means of comparative trials. This study investigated micromorphological differences in hybrid layer formation with a variety of commercially available water- or solvent-based dentin bonding products and their recommended compomers. Five bonding systems were used on groups of 10 teeth each as follows: group I, acetone-based system used with 36% phosphoric acid; group II, a different acetone-based system containing nano-sized particles for filler loading and used with a non-rinsing conditioner containing maleic acid; group III, the acetone-based system of group II used with 36% phosphoric acid (the only difference in the treatment for groups II and III was the acid etching system); group IV, a mixed-solvent-based system (water/ethanol) used with 37% phosphoric acid; and group V, a water-based system used with 37% phosphoric acid. Each bonding system was covered with the recommended compomer. Class I occlusal preparations were made in extracted teeth and restored with one of the above systems. Five specimens of each group were studied with optical microscopy after staining. Scanning electron microscopy was used to examine the interface of the bonding system/dentin of the other 5 teeth in each group. The optical microscopy measurements were made with a 10 x 10 reticle. A micron mark with scale was used for the scanning electron microscope. All measurements were made in microm. The following criteria were used to define a good interface: absence of voids between the different parts of the interface, uniformity of the hybrid layer, good opening of the tubuli orifices, and tag adherence to the tubuli walls. Morphological differences were found at the interface depending on dentin treatment and adhesive composition. The acetone-containing systems were associated

The reduction in fatigue crack growth resistance of dentin with depth.

Science.gov (United States)

Ivancik, J; Neerchal, N K; Romberg, E; Arola, D

2011-08-01

The fatigue crack growth resistance of dentin was characterized as a function of depth from the dentino-enamel junction. Compact tension (CT) specimens were prepared from the crowns of third molars in the deep, middle, and peripheral dentin. The microstructure was quantified in terms of the average tubule dimensions and density. Fatigue cracks were grown in-plane with the tubules and characterized in terms of the initiation and growth responses. Deep dentin exhibited the lowest resistance to the initiation of fatigue crack growth, as indicated by the stress intensity threshold (ΔK(th) ≈ 0.8 MPa•m(0.5)) and the highest incremental fatigue crack growth rate (over 1000 times that in peripheral dentin). Cracks in deep dentin underwent incremental extension under cyclic stresses that were 40% lower than those required in peripheral dentin. The average fatigue crack growth rates increased significantly with tubule density, indicating the importance of microstructure on the potential for tooth fracture. Molars with deep restorations are more likely to suffer from the cracked-tooth syndrome, because of the lower fatigue crack growth resistance of deep dentin.

Deformation behavior of human dentin in liquid nitrogen: a diametral compression test.

Science.gov (United States)

Zaytsev, Dmitry; Panfilov, Peter

2014-09-01

Contribution of the collagen fibers into the plasticity of human dentin is considered. Mechanical testing of dentin at low temperature allows excluding the plastic response of its organic matrix. Therefore, deformation and fracture behavior of the dentin samples under diametral compression at room temperature and liquid nitrogen temperature are compared. At 77K dentin behaves like almost brittle material: it is deformed exclusively in the elastic regime and it fails due to growth of the sole crack. On the contrary, dentin demonstrates the ductile response at 300K. There are both elastic and plastic contributions in the deformation of dentin samples. Multiple cracking and crack tip blunting precede the failure of samples. Organic phase plays an important role in fracture of dentin: plasticity of the collagen fibers could inhibit the crack growth. Copyright © 2014 Elsevier B.V. All rights reserved.

Molecular detection of bacteria associated to caries activity in dentinal lesions.

Science.gov (United States)

Neves, Beatriz Gonçalves; Stipp, Rafael Nóbrega; da Silva Bezerra, Daniela; de Figueiredo Guedes, Sarah Florindo; Rodrigues, Lidiany Karla Azevedo

2017-07-01

This study aimed at identifying and quantifying Actinomyces naeslundii, Bifidobacterium spp., Streptococcus mitis group, Lactobacillus acidophilus, Lactobacillus casei group, Streptococcus gordonii, and Streptococcus mutans in active and inactive carious dentine lesions of children with early childhood caries by using quantitative polymerase chain reaction. Fifty-six dentin lesion samples, classified as active (n = 39) or inactive (n = 17), were collected from children aged from 2 to 5 years old. Dentinal-cavitated lesions were evaluated by Nyvad criteria for the assessment of caries lesion activity. Relative quantification revealed that Bifidobacterium spp. and the L. casei group were significantly more abundant in active dentin lesions (p oral microbiota related to dentin caries activity status is relevant, this study provides insights to better understand the differences in the microbiotas between active and arrested dentin cavities.

Esthetic Rehabilitation of Anterior Teeth with Porcelain Laminates and Sectional Veneers

NARCIS (Netherlands)

Gresnigt, Marco; Ozcan, Mutlu

2011-01-01

Full-coverage bonded porcelain restorations offer predictable treatment options in dentistry, but a certain amount of tooth material must be removed to allow space for the required thickness of the restorative material. Laminate veneers and inlays are considered minimally invasive, but they also

The Difference of Structural State and Deformation Behavior between Teenage and Mature Human Dentin

Directory of Open Access Journals (Sweden)

Peter Panfilov

2016-01-01

Full Text Available Objective. The cause of considerable elasticity and plasticity of human dentin is discussed in the relationship with its microstructure. Methods. Structural state of teenage and mature human dentin is examined by using XRD and TEM techniques, and their deformation behavior under compression is studied as well. Result. XRD study has shown that crystallographic type of calcium hydroxyapatite in human dentin (calcium hydrogen phosphate hydroxide Ca9HPO4(PO45OH; Space Group P63/m (176; a = 9,441 A; c = 6,881 A; c/a = 0,729; Crystallite (Scherrer 200 A is the same for these age groups. In both cases, dentin matrix is X-ray amorphous. According to TEM examination, there are amorphous and ultrafine grain phases in teenage and mature dentin. Mature dentin is stronger on about 20% than teenage dentin, while teenage dentin is more elastic on about 20% but is less plastic on about 15% than mature dentin. Conclusion. The amorphous phase is dominant in teenage dentin, whereas the ultrafine grain phase becomes dominant in mature dentin. Mechanical properties of human dentin under compression depend on its structural state, too.

Posterior indirect adhesive 
restorations: updated indications 
and the Morphology Driven 
Preparation Technique.

Science.gov (United States)

Veneziani, Marco

The aim of this article is to identify the indications for adhesively cemented restorations and to provide a correct step-by-step protocol for clinicians. New cavity preparation principles are based on morphological considerations in terms of geometry (maximum profile line and inclination of cusp lines), and structure (dentin concavity and enamel convexity). In this article, we discuss previous preparation concepts that were not designed purely for adhesive restorations and were therefore not conservative enough or suitable for adhesive procedures. The novel cavity shape consists of continuous inclined plane cavity margins (hollow chamfer or concave bevel) on axial walls, whenever they are coronal to the equatorial tooth line. A 1.2 mm-thick butt-joint preparation is performed in the interproximal box and on the axial walls when the margins are apical to the equatorial line. The occlusal surface is anatomically prepared, free of slots and angles. The author's suggestion is to avoid shoulder finish line preparation around cusps, occlusal slots, and pins, as they are less conservative, incompatible with adhesive procedures, and involve unnecessary dentin exposure. The clinical advantages of this new "anatomic" preparation design are 1) improving adhesion quality (optimizing the cutting of enamel prisms, and increasing the available enamel surface); 2) minimizing dentin exposure; 3) maximizing hard tissue preservation (the cavity being designed for cementation with reinforced composite resins, improvement of flow, and removal of excess material); 4) optimization of esthetic integration due to the inclined plane design, which permits a better blending at the transition area between tooth and restoration. These preparation principles may be effectively used for all adhesively cemented restorations, both according to traditional concepts (inlay, onlay, overlay) and new ones (additional overlay, occlusal-veneer, overlay-veneer, long-wrap overlay, adhesive crown). Thus, a

The effect of veneering on the marginal fit of CAD/CAM-generated, copy-milled, and cast metal copings.

Science.gov (United States)

Ates, Sabit Melih; Yesil Duymus, Zeynep; Caglar, Ipek; Hologlu, Bilal

2017-11-01

This in vitro study investigated the marginal fit of metal and zirconia copings before and after veneering on dies with shoulder/chamfer (s/c) finish lines. Using CAD/CAM, ten (n = 10) each s/c zirconia (NZ) copings and ten (n = 10) each s/c metal (MM) copings were generated. As controls, ten (n = 10) each s/c zirconia copings were copy-milled (ZZ) and ten (n = 10) each s/c metal copings were cast (CC). The vertical marginal discrepancy of the copings was measured at 20 predefined spots of the circular shoulder and chamfer finish lines in microns (μm) before and after a first and a second veneering firing using a stereomicroscope at ×40 magnification. Data were statistically analyzed, and the comparisons of CAD/CAM-milled (NZ, MM), copy-milled (ZZ), and cast (CC) copings before and after veneering were made at a significance level of p < 0.05. Gap width at s/c finish lines of ZZ was (91 ± 11/100 ± 28) and increased significantly (109 ± 21/141 ± 18) after the first firing (ZZ1). NZ showed significantly smaller gaps than ZZ (36 ± 6/46 ± 12) and (NZ1) after the first firing (61 ± 16/71 ± 29). Gap widths of CC groups (36 ± 8/25 ± 4) were not significantly different from NZ but were significantly lower after the (CC1) first veneering firing (40 ± 8/42 ± 7). MM copings showed gap values similar to NZ. Second firings did not significantly increase gaps in all groups except ZZ2 of chamfer finish line. Veneering increased the marginal gap width of copings. Within the limits of this in vitro study, aesthetic ceramic veneering of CAD/CAM-generated copings caused a statistically significant but tolerable loss of marginal fit precision.

Time-dependent fracture probability of bilayer, lithium-disilicate-based glass-ceramic molar crowns as a function of core/veneer thickness ratio and load orientation

Science.gov (United States)

Anusavice, Kenneth J.; Jadaan, Osama M.; Esquivel–Upshaw, Josephine

2013-01-01

Recent reports on bilayer ceramic crown prostheses suggest that fractures of the veneering ceramic represent the most common reason for prosthesis failure. Objective The aims of this study were to test the hypotheses that: (1) an increase in core ceramic/veneer ceramic thickness ratio for a crown thickness of 1.6 mm reduces the time-dependent fracture probability (Pf) of bilayer crowns with a lithium-disilicate-based glass-ceramic core, and (2) oblique loading, within the central fossa, increases Pf for 1.6-mm-thick crowns compared with vertical loading. Materials and methods Time-dependent fracture probabilities were calculated for 1.6-mm-thick, veneered lithium-disilicate-based glass-ceramic molar crowns as a function of core/veneer thickness ratio and load orientation in the central fossa area. Time-dependent fracture probability analyses were computed by CARES/Life software and finite element analysis, using dynamic fatigue strength data for monolithic discs of a lithium-disilicate glass-ceramic core (Empress 2), and ceramic veneer (Empress 2 Veneer Ceramic). Results Predicted fracture probabilities (Pf) for centrally-loaded 1,6-mm-thick bilayer crowns over periods of 1, 5, and 10 years are 1.2%, 2.7%, and 3.5%, respectively, for a core/veneer thickness ratio of 1.0 (0.8 mm/0.8 mm), and 2.5%, 5.1%, and 7.0%, respectively, for a core/veneer thickness ratio of 0.33 (0.4 mm/1.2 mm). Conclusion CARES/Life results support the proposed crown design and load orientation hypotheses. Significance The application of dynamic fatigue data, finite element stress analysis, and CARES/Life analysis represent an optimal approach to optimize fixed dental prosthesis designs produced from dental ceramics and to predict time-dependent fracture probabilities of ceramic-based fixed dental prostheses that can minimize the risk for clinical failures. PMID:24060349

Time-dependent fracture probability of bilayer, lithium-disilicate-based, glass-ceramic, molar crowns as a function of core/veneer thickness ratio and load orientation.

Science.gov (United States)

Anusavice, Kenneth J; Jadaan, Osama M; Esquivel-Upshaw, Josephine F

2013-11-01

Recent reports on bilayer ceramic crown prostheses suggest that fractures of the veneering ceramic represent the most common reason for prosthesis failure. The aims of this study were to test the hypotheses that: (1) an increase in core ceramic/veneer ceramic thickness ratio for a crown thickness of 1.6mm reduces the time-dependent fracture probability (Pf) of bilayer crowns with a lithium-disilicate-based glass-ceramic core, and (2) oblique loading, within the central fossa, increases Pf for 1.6-mm-thick crowns compared with vertical loading. Time-dependent fracture probabilities were calculated for 1.6-mm-thick, veneered lithium-disilicate-based glass-ceramic molar crowns as a function of core/veneer thickness ratio and load orientation in the central fossa area. Time-dependent fracture probability analyses were computed by CARES/Life software and finite element analysis, using dynamic fatigue strength data for monolithic discs of a lithium-disilicate glass-ceramic core (Empress 2), and ceramic veneer (Empress 2 Veneer Ceramic). Predicted fracture probabilities (Pf) for centrally loaded 1.6-mm-thick bilayer crowns over periods of 1, 5, and 10 years are 1.2%, 2.7%, and 3.5%, respectively, for a core/veneer thickness ratio of 1.0 (0.8mm/0.8mm), and 2.5%, 5.1%, and 7.0%, respectively, for a core/veneer thickness ratio of 0.33 (0.4mm/1.2mm). CARES/Life results support the proposed crown design and load orientation hypotheses. The application of dynamic fatigue data, finite element stress analysis, and CARES/Life analysis represent an optimal approach to optimize fixed dental prosthesis designs produced from dental ceramics and to predict time-dependent fracture probabilities of ceramic-based fixed dental prostheses that can minimize the risk for clinical failures. Copyright © 2013 Academy of Dental Materials. All rights reserved.

Molecular study of the dentin-pulp complex responses to caries progression

Directory of Open Access Journals (Sweden)

Yani Corvianindya Rahayu

2007-03-01

Full Text Available The dentin-pulp complex exhibits various responses to caries, including events of injury, defense, and repair. The overall responses dependent on pulp cell activity and the signaling processes, which regulate the behavior of these cells. The signals for tissue repair are thought to be mediated by dentin-bound growth factors released during caries progression. Growth factors are a key of molecules responsible for signaling a variety of cellular process following dental injury. The endogenous proteolytic enzymes (Matrix metalloproteinases, MMPs present in dentin matrix might also participate in releasing bioactive molecule. Several members of the MMP family are found in the soft and hard tissue compartment of dentin-pulp complex. Their presumed role in many physiological process during the development and maintenance of the dentin-pulp complex, they may also contribute to the pathogenesis of dentin caries and the responses elicited by caries.

[Influence of thermalcycling on bonding durability of self-etch adhesives with dentin].

Science.gov (United States)

Tian, Fu-cong; Wang, Xiao-yan; Gao, Xue-jun

2014-04-18

To investigate influence of thermalcycling on the bonding durability of two one-step products [Adper Prompt (AP) and G-bond (GB)] and one two-step self-etching adhesive [Clearfil SE bond (SE)] with dentin in vitro. Forty-two extracted human molars were selected. The superficial dentin was exposed by grinding off the enamel. The teeth were randomly distributed into six groups with varied bonding protocols. The adhesives were applied to the dentin surface. Composite crowns were built up, then the samples were cut longitudinally into sticks with 1.0 mm×1.0 mm bonding area [for microtensile bond strength (MTBS) testing] or 1.0 mm thick slabs (for nanoleakage observation). Bonding performance was evaluated with or without thermalcyling. For the MTBS testing, the strength values were statistically analysed using One-Way ANOVA. Four slabs in each group were observed for nanoleakage by SEM with a backscattered electron detector. Thermalcycling procedures affected MTBS. In the two one-step groups, the MTBS decreased significantly (Padhesives showed lower MTBS than two-step bonding system after aging.For AP and GB, continuous nanoleakage appearance was notable and more obvious than for SE. Thermalcycling can affect the bonding performance of self-etch adhesives including decrease of bond strength and nanoleakage pattern. one-step self-etch adhesives showed more obvious change compared with their two-step counterparts.

Remineralizing Efficacy of Fluorohydroxyapatite Gel on Artificial Dentinal Caries Lesion

Directory of Open Access Journals (Sweden)

Qianqian Wang

2015-01-01

Full Text Available The aim was to evaluate the remineralizing efficacy of fluorohydroxyapatite (FHA gel on artificial dentinal caries lesion in vitro. Artificial carious lesions were made on occlusal cavities of teeth by exposing the dentin surface to a demineralizing solution. Each cavity was capped with a 3 mm thick FHA gel for 4 weeks. After the FHA gel was removed, the surface morphology and structure of the dentin were characterized by scanning electron microscopy (SEM, energy-dispersive X-ray spectroscopy (EDX, X-ray diffraction (XRD, and Fourier transform infrared spectroscopy (FT-IR. The dentin mineral density (DMD was measured by micro-computed tomography (Micro-CT. A layer of dense and orderly hexagonal crystal structure, with average diameter of 1 μm and thickness of 4~5 μm, could be observed on dentin surface. These crystals exhibited elemental peaks for calcium, phosphorus, carbon, and oxygen and characteristic peaks of hydroxyapatite (HA and fluorapatite (FA via XRD and FT-IR. The DMD of dentin surface layer significantly increased after it was capped with FHA gel (P<0.05. In the present study, the FHA gel could rapidly construct apatite on the artificial dentin caries surface and significantly increase the mineral density, which suggests that FHA gel might be a proper IPT material with remineralizing function.

Influence of Different Types of Resin Luting Agents on Color Stability of Ceramic Laminate Veneers Subjected to Accelerated Artificial Aging.

Science.gov (United States)

Silami, Francisca Daniele Jardilino; Tonani, Rafaella; Alandia-Román, Carla Cecilia; Pires-de-Souza, Fernanda de Carvalho Panzeri

2016-01-01

The aim of this study was to evaluate the influence of accelerated aging (AAA) on the color stability of resin cements for bonding ceramic laminate veneers of different thicknesses. The occlusal surfaces of 80 healthy human molars were flattened. Ceramic laminate veneers (IPS e-max Ceram) of two thicknesses (0.5 and 1.0 mm) were bonded with three types of luting agents: light-cured, conventional dual and self-adhesive dual cement. Teeth without restorations and cement samples (0.5 mm) were used as control. After initial color evaluations, the samples were subjected to AAA for 580 h. After this, new color readouts were made, and the color stability (ΔE) and luminosity (ΔL) data were analyzed. The greatest color changes (p<0.05) occurred when 0.5 mm veneers were fixed with light-cured cement and the lowest when 1.0 mm veneers were fixed with conventional dual cement. There was no influence of the restoration thickness when the self-adhesive dual cement was used. When veneers were compared with the control groups, it was verified that the cement samples presented the greatest alterations (p<0.05) in comparison with both substrates and restored teeth. Therefore, it was concluded that the thickness of the restoration influences color and luminosity changes for conventional dual and light-cured cements. The changes in self-adhesive cement do not depend on restoration thickness.

Effect of Various Surface Treatment on Repair Strength of Composite Resin

Directory of Open Access Journals (Sweden)

Y. Alizade

2004-12-01

Full Text Available Statement of Problem: In some clinical situations, repair of composite restorations is treatment of choice. Improving the bond strength between one new and old composite usually requires increased surface roughness to promote mechanical interlocking sincechemical bonding might not be adequate. Similarly, the treatment of a laboratory fabricated resin composite restoration involves the same procedures, and there is a need to create the strongest possible bond of a resin cement to a previously polymerized composite.Purpose: The aim of this study was to evaluate the effect of various surface treatments on the shear bond strength of repaired to aged composite resin.Materials and Methods: Eighty four cylindrical specimens of a composite resin were fabricated and stored in distilled water for 100 days prior to surface treatment. Surface treatment of old composite was done in 6 groups as follow:1- Air abrasion with CoJet sand particles with micoretcher + silane + dentin bonding agent2- Air abrasion with 50μm Al2O3 particles+ phosphoric acid+ silane+ dentin bonding agent3- Air abrasion with 50μm Al2O3 particles + phosphoric acid + dentin bonding agent4- Diamond bur + phosphoric acid + silane + dentin bonding agent5- Diamond bur + phosphoric acid + dentin bonding agent6- Diamond bur + phosphoric acid + composite activator + dentin bonding agentThen fresh composite resin was bonded to treated surfaces. Twelve specimens were also fabricated as control group with the same diameter but with the height twice as much as other specimens. All of the specimens were thermocycled prior to testing for shear bondstrength. The bond strength data were analyzed statistically using one way ANOVA test, t test and Duncan's grouping test.Results: One-way ANOVA indicated no significant difference between 7 groups (P=0.059. One-way ANOVA indicated significant difference between the three diamond bur groups (P=0.036. Silane had a significant effect on the repair bond

Effect of Er,Cr:YSGG laser on the microtensile bond strength of two different adhesives to the sound and caries-affected dentin.

Science.gov (United States)

Ergücü, Z; Celik, E U; Unlü, N; Türkün, M; Ozer, F

2009-01-01

This study examined the effect of Er,Cr:YSGG laser irradiation on the microtensile bond strength (microTBS) of a three-step etch-and-rinse and a two-step self-etch adhesive to sound and caries-affected dentin. Sixteen freshly extracted human molars with occlusal dentin caries were used. The caries lesion was removed by one of the following methods: conventional treatment with burs or Er,Cr:YSGG laser (Waterlase MD, Biolase). The adhesive systems (AdheSE, Ivoclar Vivadent and Scotchbond Multi Purpose, 3M ESPE) were applied to the entire tooth surface according to the manufacturers' instructions. Resin composites were applied to the adhesive-treated dentin surfaces and light-cured. Each tooth was sectioned into multiple beams with the "non-trimming" version of the microtensile test. The specimens were subjected to microtensile forces (BISCO Microtensile Tester, BISCO). The data was analyzed by three-way ANOVA and independent t-tests (p=0.05). Er,Cr:YSGG laser irradiation exhibited similar microTBS values compared to that of conventional bur treatment, regardless of the adhesive system and type of treated dentin. The self-etch system revealed lower microTBS values, both with conventional and laser treatment techniques, compared to the etch-and-rinse adhesive in sound and caries-affected dentin (padhesive systems to sound and caries-affected dentin.

Different methods of dentin processing for application in bone tissue engineering: A systematic review.

Science.gov (United States)

Tabatabaei, Fahimeh Sadat; Tatari, Saeed; Samadi, Ramin; Moharamzadeh, Keyvan

2016-10-01

Dentin has become an interesting potential biomaterial for tissue engineering of oral hard tissues. It can be used as a scaffold or as a source of growth factors in bone tissue engineering. Different forms of dentin have been studied for their potential use as bone substitutes. Here, we systematically review different methods of dentin preparation and the efficacy of processed dentin in bone tissue engineering. An electronic search was carried out in PubMed and Scopus databases for articles published from 2000 to 2016. Studies on dentin preparation for application in bone tissue engineering were selected. The initial search yielded a total of 1045 articles, of which 37 were finally selected. Review of studies showed that demineralization was the most commonly used dentin preparation process for use in tissue engineering. Dentin extract, dentin particles (tooth ash), freeze-dried dentin, and denatured dentin are others method of dentin preparation. Based on our literature review, we can conclude that preparation procedure and the size and shape of dentin particles play an important role in its osteoinductive and osteoconductive properties. Standardization of these methods is important to draw a conclusion in this regard. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 104A: 2616-2627, 2016. © 2016 Wiley Periodicals, Inc.

Unicystic ameloblastoma with the presence of dentin

Directory of Open Access Journals (Sweden)

Sivapathasundharam B

2007-01-01

Full Text Available We present a case of unicystic ameloblastoma of the posterior mandible in a 28 year-old female, histologically showing luminal and intramural plexiform epithelial proliferation with typical dentin in the connective tissue capsule. The characteristics of hard tissue formation in ameloblastomas reported in existing literature and the possible origin of the dentin mass seen in our case are discussed.

Experimental resin cements containing bioactive fillers reduce matrix metalloproteinase-mediated dentin collagen degradation.

Science.gov (United States)

Osorio, Raquel; Yamauti, Monica; Sauro, Salvatore; Watson, Thimoty F; Toledano, Manuel

2012-09-01

Collagen dentin matrix may represent a suitable scaffold to be remineralized in the presence of bioactive materials. The purpose of this study was to determine if experimental resin cements containing bioactive fillers may modulate matrix metalloproteinase-mediated collagen degradation of etched dentin. Human dentin beams demineralized using 10% phosphoric acid or 0.5 mol/L EDTA were infiltrated with the following experimental resins: (1) unfilled resin, (2) resin with Bioglass 45S5 particles (Sylc; OSspray Ltd, London, UK), and (3) resin with β-tricalcium phosphate-modified calcium silicate cement (HCAT-β) particles. The filler/resin ratio was 40/60 wt%. The specimens were stored in artificial saliva, and the determination of C-terminal telopeptide (ICTP) was performed by radioimmunoassay after 24 hours, 1 week, and 4 weeks. Scanning electron microscopic analysis of dentin surfaces after 4 weeks of storage was also executed. Collagen degradation was prominent both in phosphoric acid and EDTA-treated dentin. Resin infiltration strongly reduced the MMP activity in demineralized dentin. Resin-containing Bioglass 45S5 particles exerted higher and more stable protection of collagen at all tested dentin states and time points. HCAT-β induced collagen protection from MMPs only in EDTA-treated specimens. Dentin remineralization was achieved when dentin was infiltrated with the resin cements containing bioactive fillers. MMP degradation of dentin collagen is strongly reduced in resin-infiltrated dentin. The inclusion of Bioglass 45S5 particles exerted an additional protection of collagen during dentin remineralization. Copyright © 2012 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

The changing veneer and plywood industry of Michigan and Wisconsin.

Science.gov (United States)

Gary R. Lindell; Lewis T. Hendricks

1972-01-01

Analyzes trends in the hardwood veneer and plywood industry of Michigan and Wisconsin between 1964 and 1969. In that period, red oak and hard maple replaced yellow birch as the major species used. Log supplies were adequate. Wall paneling was the major end market with doorskins next. Excess plywood producing capacity is a chronic problem.

SEM Evaluation of Internal Adaptation of Bases and Liners under Composite Restorations

Directory of Open Access Journals (Sweden)

Dimitrios Dionysopoulos

2014-04-01

Full Text Available The aim of this study was to evaluate the interfacial microgaps generating between different materials and between materials and dentin after polymerization of the composite restorations, using SEM. Methods: The materials investigated were a composite, an adhesive, a RMGI, and a calcium hydroxide. Thirty third molars were selected and two circular class V cavities (5 mm × 3 mm for each tooth were made. The teeth were randomly assigned into six groups and restored with a combination of the materials. The specimens were subjected to thermocycling and each tooth was sectioned mesiodistally in two halves. Each half was sectioned along the longitudinal axis through the center of the restorations to obtain a slice of 2 mm. The specimens were examined under SEM. The interfaces between the liners, the liners and dentin, and between the liners and the composite were examined for microgaps. Results: The results showed that there was not any significant difference in the mean width of microgaps in the interfaces between Dycal-dentin and Vitrebond-dentin (p>0.05. However, the width of microgaps in the interfaces between dentin-Clearfil Tri-S Bond was significantly smaller (p<0.05. The use of Clearfil Tri-S Bond reduced the possibility of microgap formation between the bonded interface and the materials tested.

Hipótesis actuales relacionadas con la sensibilidad dentinal

Directory of Open Access Journals (Sweden)

Andrés Pérez Ruiz

1999-08-01

Full Text Available Se hace una revisión sobre las hipótesis actuales concernientes a la sensibilidad dentinal, centrando el análisis en las teorías acerca de la presencia de nervios en la dentina, la transmisión del impulso nervioso mediante el odontoblasto y el movimiento de fluidos dentro de la dentina. Por ser la explicación de la sensibilidad de la dentina uno de los más complejos problemas de la fisiología y la histología del diente, se exponen los hechos morfológicos y funcionales que apoyan la validez de los mecanismos mencionados. Se concluye que aunque la teoría hidrodinámica tiene una sólida base experimental y es la de mayor aceptación en la actualidad, pudieran estar involucrados en la génesis del dolor dentinal más de una de estas explicaciones probables.A review of the present hypotheses of dentinal sensitivity was carried out. The analysis was centered on the theories of the existance of nerves in dentin, the transfer of nervous impulse through odontoblast and the fluid flow in the dentin. Since the explanation of dentin sensitivity is one of the most complex problems of dental physiology and histology; the morphological and functional aspects that support the validity of the mentioned mechanisms are stated. It is concluded that although the hydrodynamic theory has a sound experimental basis and is widely accepted at present, more than one of these likely theories could be involved in the genesis of dentinal pain.

Spectroscopic and thermal characterization of bovine enamel and dentine using the photoacoustic effect

International Nuclear Information System (INIS)

Stolf, Sandro Fernando

2003-01-01

The optical and thermal properties of dental tissues determine the nature and extent of the tissue response through the processes of absorption, transmission, reflection and scattering of the laser light and the heat produced by the absorption of that light. The spectroscopic characterization of bovine dentine and enamel, and the determination of the thermal diffusivity were the aim of this study. The photoacoustic spectra from these tissues were obtained in the Near-Infrared range 900 - 2500 nm, which is the clinical range for odontological application of most lasers. Photoacoustic spectra were taken from block, slices and powder of enamel and dentine. Also photoacoustic spectra were registered before and after 2, 5 and 10 h of topical fluoride (2.26%) application. Using the same technique spectra were taken from dentine and enamel after irradiation with Nd:YAG, Er:YAG, Ho:YLF and CO 2 . It is evident from the results that the presence of O-H in the composition of hydroxyapatite and the water present in the teeth tissue make the obtention of spectrum from components other than O-H bond a very difficult task. In this way, only bands assigned to overtones and combinations of O-H stretch were observed. The thermal diffusivity of the bovine dentine was also measured using the photoacoustic technique. The thermal diffusivity is the physical quantity which measures the rate of heat diffusion throughout the sample. For higher values of the thermal diffusivity the heat diffusion and temperature rise will be faster. As there is many studies devoted to the processes of heat transfer throughout dental tissues using bovine teeth, it is important the determination of its thermal diffusivity. The measured value was found to be a = 2.0 (±0.1).1O -3 cm 2 /s for the both direction, perpendicular and parallel to the dentinal tubules. These a lues indicate that there is no difference between the thermal diffusivities for the both directions. (author)

Sodium Thiosulfate for Recovery of Bond Strength to Dentin Treated with Sodium Hypochlorite.

Science.gov (United States)

Pimentel Corrêa, Ana Carolina; Cecchin, Doglas; de Almeida, José Flávio Affonso; Gomes, Brenda Paula Figueiredo de Almeida; Zaia, Alexandre Augusto; Ferraz, Caio Cezar Randi

2016-02-01

The aim of this study was to evaluate the efficacy of sodium thiosulfate (Na2S2O3) for restoring adhesion to pulp chamber dentin treated with sodium hypochlorite (NaOCl) and EDTA. Sixty-three crowns of bovine incisors were cut to expose the dentin pulp chamber. The specimens were polished and randomly distributed into 9 groups (n = 7) according to the following protocols used: 0.9% sodium chloride for 30 minutes (negative control), 5.25% NaOCl for 30 minutes, 17% EDTA for 3 minutes, and 5.25% NaOCl for 1 minute (positive control). The other groups, after treatments with NaOCl and EDTA, were immersed in 0.5% or 5% Na2S2O3 for 1, 5, and 10 minutes or just immersed in an inert solution for 10 minutes (0.9% sodium chloride). After drying the specimens, Scotchbond Multi-Purpose (3M ESPE, St Paul, MN) was applied to the pulp chamber dentin followed by Filtek Z250 composite (3M ESPE). Six rectangular slabs were obtained from each specimen, and the dentin/resin interface was tested by using a universal testing machine. The resulting data were submitted to 1-way analysis of variance and the Duncan test (P = .05). There was a significant decrease in bond strength regarding NaOCl and EDTA (P adhesive restorations to be immediately applied after endodontic treatment. Copyright © 2016 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

The effect of organic solvents on one-bottle adhesives' bond strength to enamel and dentin.

Science.gov (United States)

Reis, André Figueiredo; Oliveira, Marcelo Tavares; Giannini, Marcelo; De Goes, Mário Fernando; Rueggeberg, Frederick A

2003-01-01

This study evaluated the microtensile bond strength (pTBS) of ethanol/water- and acetone-based, one-bottle adhesive systems to enamel (E) and dentin (D) in the presence (P) or absence (A) of their respective solvents. Thirty-two freshly extracted third molars were flattened with 600-grit SiC paper and restored with Single Bond (SB) or Prime&Bond 2.1 (PB) according to the manufacturers' instructions and after full solvent elimination. The molars were divided into eight test groups (n = 4): G1-SB-E-P, G2-SB-E-A, G3-PBE-P, G4-PB-E-A, G5-SB-D-P, G6-SB-D-A, G7-PB-D-P and G8-PB-D-A. After applying the adhesive resins, composite crowns of approximately 8 mm were built up with TPH Spectrum composite. After 24-hour water storage, the specimens were serially sectioned bucco-lingually to obtain 0.8 mm slabs that were trimmed to an hourglass shape, approximately 0.8 mm2 at the bonded interface. The specimens were tested in tension using a universal testing machine (0.5 mm/minute). The results were statistically analyzed by ANOVA and Tukey test. The frequency of fracture mode was compared using the Kruskal-Wallis test. There were no statistically significant differences in mean bond strength among the groups restored with or without solvent for enamel. However, the results were significantly different for the dentin groups (MPa): G5-26.2 +/- 8.6a; G7-23.6 +/- 11.3ab; G6-12.8 +/- 2.1bc; G8-6.2 +/- 3.1c. SEM examination indicated that the dentin group failure modes were significantly different from the enamel groups. The results suggest that the presence of organic solvents does not influence microTBS to enamel. However, microTBS to dentin was significantly affected by the absence of solvents in the adhesive system.

Quantitative analysis of aqueous phase composition of model dentin adhesives experiencing phase separation

Science.gov (United States)

Ye, Qiang; Park, Jonggu; Parthasarathy, Ranganathan; Pamatmat, Francis; Misra, Anil; Laurence, Jennifer S.; Marangos, Orestes; Spencer, Paulette

2013-01-01

There have been reports of the sensitivity of our current dentin adhesives to excess moisture, for example, water-blisters in adhesives placed on over-wet surfaces, and phase separation with concomitant limited infiltration of the critical dimethacrylate component into the demineralized dentin matrix. To determine quantitatively the hydrophobic/hydrophilic components in the aqueous phase when exposed to over-wet environments, model adhesives were mixed with 16, 33, and 50 wt % water to yield well-separated phases. Based upon high-performance liquid chromatography coupled with photodiode array detection, it was found that the amounts of hydrophobic BisGMA and hydrophobic initiators are less than 0.1 wt % in the aqueous phase. The amount of these compounds decreased with an increase in the initial water content. The major components of the aqueous phase were hydroxyethyl methacrylate (HEMA) and water, and the HEMA content ranged from 18.3 to 14.7 wt %. Different BisGMA homologues and the relative content of these homologues in the aqueous phase have been identified; however, the amount of crosslinkable BisGMA was minimal and, thus, could not help in the formation of a crosslinked polymer network in the aqueous phase. Without the protection afforded by a strong crosslinked network, the poorly photoreactive compounds of this aqueous phase could be leached easily. These results suggest that adhesive formulations should be designed to include hydrophilic multimethacrylate monomers and water compatible initiators. PMID:22331596

Glutaraldehyde-induced remineralization improves the mechanical properties and biostability of dentin collagen

Energy Technology Data Exchange (ETDEWEB)

Chen, Chaoqun; Mao, Caiyun; Sun, Jian; Chen, Yi; Wang, Wei [Department of Stomatology, The First Affiliated Hospital, College of Medicine, Zhejiang University (China); Pan, Haihua; Tang, Ruikang [Centre for Biopathways and Biomaterials, Department of Chemistry, Zhejiang University (China); Gu, Xinhua [Department of Stomatology, The First Affiliated Hospital, College of Medicine, Zhejiang University (China)

2016-10-01

The purpose of this study was to induce a biomimetic remineralization process by using glutaraldehyde (GA) to reconstruct the mechanical properties and biostability of demineralized collagen. Demineralized dentin disks (35% phosphoric acid, 10 s) were pretreated with a 5% GA solution for 3 min and then cultivated in a calcium phosphate remineralization solution. The remineralization kinetics and superstructure of the remineralization layer were evaluated by Raman spectroscopy, transmission electron microscopy, scanning electron microscopy and nanoindentation tests. The biostability was examined by enzymatic degradation experiments. A significant difference was found in dentin remineralization process between dentin with and without GA pretreating. GA showed a specific affinity to dentin collagen resulting in the formation of a cross-linking superstructure. GA pretreating could remarkably shorten remineralization time from 7 days to 2 days. The GA-induced remineralized collagen fibrils were well encapsulated by newly formed hydroxyapatite mineral nanocrystals. With the nano-hydroxyapatite coating, both the mechanical properties (elastic modulus and hardness) and the biostability against enzymatic degradation of the collagen were significantly enhanced, matching those of natural dentin. The results indicated that GA cross-linking of dentin collagen could promote dentin biomimetic remineralization, resulting in an improved mechanical properties and biostability. It may provide a promising tissue-engineering technology for dentin repair. - Highlights: • GA cross-linking can promote the remineralization kinetics of dentin collagen. • GA-induced remineralization can reshape the demineralized dentin collagen layer. • The GA-induced remineralization enhances the degradation resistance of collagen. • GA-induced remineralization provides a new approach to improve bonding durability.

Glutaraldehyde-induced remineralization improves the mechanical properties and biostability of dentin collagen

International Nuclear Information System (INIS)

Chen, Chaoqun; Mao, Caiyun; Sun, Jian; Chen, Yi; Wang, Wei; Pan, Haihua; Tang, Ruikang; Gu, Xinhua

2016-01-01

The purpose of this study was to induce a biomimetic remineralization process by using glutaraldehyde (GA) to reconstruct the mechanical properties and biostability of demineralized collagen. Demineralized dentin disks (35% phosphoric acid, 10 s) were pretreated with a 5% GA solution for 3 min and then cultivated in a calcium phosphate remineralization solution. The remineralization kinetics and superstructure of the remineralization layer were evaluated by Raman spectroscopy, transmission electron microscopy, scanning electron microscopy and nanoindentation tests. The biostability was examined by enzymatic degradation experiments. A significant difference was found in dentin remineralization process between dentin with and without GA pretreating. GA showed a specific affinity to dentin collagen resulting in the formation of a cross-linking superstructure. GA pretreating could remarkably shorten remineralization time from 7 days to 2 days. The GA-induced remineralized collagen fibrils were well encapsulated by newly formed hydroxyapatite mineral nanocrystals. With the nano-hydroxyapatite coating, both the mechanical properties (elastic modulus and hardness) and the biostability against enzymatic degradation of the collagen were significantly enhanced, matching those of natural dentin. The results indicated that GA cross-linking of dentin collagen could promote dentin biomimetic remineralization, resulting in an improved mechanical properties and biostability. It may provide a promising tissue-engineering technology for dentin repair. - Highlights: • GA cross-linking can promote the remineralization kinetics of dentin collagen. • GA-induced remineralization can reshape the demineralized dentin collagen layer. • The GA-induced remineralization enhances the degradation resistance of collagen. • GA-induced remineralization provides a new approach to improve bonding durability.

Effects of chlorhexidine-containing adhesives on the durability of resin-dentine interfaces.

Science.gov (United States)

Stanislawczuk, Rodrigo; Pereira, Fabiane; Muñoz, Miguel Angel; Luque, Issis; Farago, Paulo Vitor; Reis, Alessandra; Loguercio, Alessandro D

2014-01-01

This study evaluated the effect of addition of diacetate CHX in different concentrations into two simplified etch-and-rinse (ER) adhesive systems (XP Bond [XP] and Ambar {AM}) on the ultimate tensile strength (UTS), degree of conversion (DC), 60-day cumulative water sorption (WS), solubility (SO) and CHX release (CR) as well as the immediate (IM) and 1-year (1Y) resin-dentine bond strength (μTBS) and nanoleakage (NL). Ten experimental adhesive systems were formulated according to the addition of CHX diacetate (0 [control], 0.01, 0.05, 0.1 and 0.2%) in the two ER. For UTS and DC, specimens were constructed and tested after 24h. For WS, SO and CR, after specimens build-up, they were stored in water and the properties measured after 60 days. The occlusal enamel of fifty molars was removed and the adhesives were applied in dentine surface after 37% phosphoric acid etching. After composite resin build-ups, specimens were longitudinally sectioned to obtain resin-dentine bonded sticks (0.8mm(2)). Specimens were tested in tension at 0.5mm/min in the IM or 1Y. For NL, 2 bonded sticks from each tooth were prepared and analyzed under SEM. The data were submitted to appropriate statistical analysis (α=0.05). The addition of CHX did not influence UTS, DC, WS and SO (padhesives with higher concentration of CHX (padhesives or it was less pronounced than the control (XP) regardless of the CHX concentration. The addition of CHX diacetate in concentrations until 0.2% in the simplified ER adhesive systems may be an alternative to increase the long-term stability of resin-dentine interfaces, without jeopardizing the adhesives' mechanical properties evaluated. Copyright © 2013. Published by Elsevier Ltd.

Fracture toughness versus micro-tensile bond strength testing of adhesive-dentin interfaces.

Science.gov (United States)

De Munck, Jan; Luehrs, Anne-Katrin; Poitevin, André; Van Ende, Annelies; Van Meerbeek, Bart

2013-06-01

To assess interfacial fracture toughness of different adhesive approaches and compare to a standard micro-tensile bond-strength (μTBS) test. Chevron-notched beam fracture toughness (CNB) was measured following a modified ISO 24370 standard. Composite bars with dimensions of 3.0×4.0×25 mm were prepared, with the adhesive-dentin interface in the middle. At the adhesive-dentin interface, a chevron notch was prepared using a 0.15 mm thin diamond blade mounted in a water-cooled diamond saw. Each specimen was loaded until failure in a 4-point bend test setup and the fracture toughness was calculated according to the ISO specifications. Similarly, adhesive-dentin micro-specimens (1.0×1.0×8-10 mm) were stressed in tensile until failure to determine the μTBS. A positive correlation (r(2)=0.64) was observed between CNB and μTBS, which however was only nearly statistically significant, mainly due to the dissimilar outcome of Scotchbond Universal (3M ESPE). While few μTBS specimens failed at the adhesive-dentin interface, almost all CNB specimens failed interfacially at the notch tip. Weibull moduli for interfacial fracture toughness were much higher than for μTBS (3.8-11.5 versus 2.7-4.8, respectively), especially relevant with regard to early failures. Although the ranking of the adhesives on their bonding effectiveness tested using CNB and μTBS corresponded well, the outcome of CNB appeared more reliable and less variable. Fracture toughness measurement is however more laborious and requires specific equipment. The μTBS nevertheless appeared to remain a valid method to assess bonding effectiveness in a versatile way. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Laboratory validation of a new gas-enhanced dentine liquid permeation evaluation system.

Science.gov (United States)

Al-Jadaa, Anas; Attin, Thomas; Peltomäki, Timo; Heumann, Christian; Schmidlin, Patrick R

2014-12-01

To validate a new automated dentine permeability testing platform based on pressure change measurements. A split chamber was designed allowing for concomitant measurement of fluid permeation and pressure difference. In a first test, system reliability was assessed by interposing a solid metal disk, embedded composite resin disks, or teeth by consecutively measuring eight times under standardized conditions. Secondly, the repeatability and applicability of the method was tested in a dentine wound model by using intact third molars: Class I (2 × 5 mm) and a full occlusal preparation as well a ceramic restoration were consecutively performed and repeatedly measured eight times each. In the last test, the system detection limit as well correlation between gas pressure difference and liquid permeation were evaluated: Again, third molars were used and occlusal preparations of increasing size (2 × 5, 3 × 5, 4 × 5, and 5 × 5 mm and full occlusal preparations, respectively) were made. Data was analyzed for the linearity of measurement, and R (2) values were calculated. The embedding procedure allowed for perfect separation of the two chambers, and no significant variation in repeated measurements of evaluated samples for the respective treatments (p = 0.05) was found. The detection was 0.002 hPa/min for the pressure slope and 0.0225 μl/min for the fluid infiltration, respectively. The saline volume was highly correlating to the gas pressure changes (R (2) = 0.996, p < 0.0001). The presented method is a reliable and exact tool to assess dentine permeability by nondestructive and repeatable measurements. This method is suitable for measurements and comparison of the effectiveness of dentine wounds sealing materials.

Inactivation of local root canal medicaments by dentine: an in vitro study.

Science.gov (United States)

Haapasalo, H K; Sirén, E K; Waltimo, T M; Ørstavik, D; Haapasalo, M P

2000-03-01

The aim of the study was to investigate the inactivation by dentine of the antibacterial activity of various commonly used local root canal medicaments. The medicaments tested were saturated calcium hydroxide solution, 1% sodium hypochlorite, 0.5% and 0.05% chlorhexidine acetate, and 2/4% and 0.2/0.4% iodine potassium iodide. Dentine was sterilized by autoclaving and crushed into powder with a particle size of 0.2-20 microns. Aliquots of dentine suspension were incubated with the medicaments in sealed test tubes at 37 degrees C for 24 h or 1 h before adding the bacteria. In some experiments bacteria were added simultaneously with dentine powder and the medicament. Enterococcus faecalis A197A was used as a test organism. Samples for bacterial culturing were taken from the suspensions at 5 min, 1 h and 24 h after adding the bacteria. Dentine powder had an inhibitory effect on all medicaments tested. The effect was dependent on the concentration of the medicament as well as on the length of the time the medicament was preincubated with dentine powder before adding the bacteria. The effect of calcium hydroxide on E. faecalis was totally abolished by the presence of dentine powder. Similarly, 0.2/0.4% iodine potassium iodide lost its effect after preincubation for 1 h with dentine before adding the bacteria. The effect of 0.05% chlorhexidine and 1% sodium hypochlorite on E. faecalis was reduced but not totally eliminated by the presence of dentine. No inhibition could be measured when full strength solutions of chlorhexidine and iodine potassium iodide were used in killing E. faecalis. The dentine powder model appears to be an efficient tool for the study of interactions between local endodontic medicaments, dentine, and microbes.

Fracture mechanism of coronal teenage dentin

Science.gov (United States)

Panfilov, P. E.; Kabanova, A. V.; Borodin, I. N.; Guo, J.; Zang, Z.

2017-10-01

The structure of coronal teenage dentin and the development of cracks in it are studied on microand nanolevels. The material is found to fail according to a ductile mechanism on a microlelvel and according to a ductile-brittle mechanism on a nanoscale. This behavior is similar to the failure of a polyethylene film and rubber, when significant elastic and irreversible deformation precedes crack growth. The viscoelastic behavior can be considered as the reaction of dentin to an applied mechanical load.

Structure and microstructure of coronary dentin in non-erupted human deciduous incisor teeth

Directory of Open Access Journals (Sweden)

Costa Luciane R.R S.

2002-01-01

Full Text Available The dentin structure of non-erupted human deciduous mandibular and maxillary central and lateral incisor teeth was studied employing light and scanning electron microscopy. For light microscopy, nitric-acid-demineralized and ground sections were used. The sections were stained by hematoxylin-eosin, picrosirius and azo-carmim methods, and ground specimens were prepared using a carborundum disk mounted in a handpiece. For SEM study, teeth were frozen in liquid nitrogen and fractured at longitudinal and transversal directions. Structurally, demineralization and ground methods revealed tubules with primary and secondary curvatures, canaliculi, giant tubules, interglobular dentin, predentin, and intertubular dentin. Scanning electron microscopy showed three-dimensional aspects of dentinal tubules, canaliculi, peritubular dentin, intertubular dentin, and predentin. This study contributes to knowledge about dentin morphology showing characteristics of teeth not yet submitted to mastication stress.

Esthetic restorations of maxillary anterior teeth with orthodontic treatment and porcelain laminate veneers: a case report.

Science.gov (United States)

Moon, Ji-Eun; Kim, Sung-Hun; Han, Jung-Suk; Yang, Jae-Ho; Lee, Jai-Bong

2010-06-01

If orthodontists and restorative dentists establish the interdisciplinary approach to esthetic dentistry, the esthetic and functional outcome of their combined efforts will be greatly enhanced. This article describes satisfying esthetic results obtained by the distribution of space for restoration by orthodontic treatment and porcelain laminate veneers in uneven space between maxillary anterior teeth. It is proposed that the use of orthodontic treatment for re-distribution of the space and the use of porcelain laminate veneers to alter crown anatomy provide maximum esthetic and functional correction for patients with irregular interdental spacing.

Effect of Silviculture on the Yield and Quality of Veneers

Science.gov (United States)

Leslie H. Groom; Ray Newbold; Jim Guldin

2002-01-01

The structural and aesthetic value of wood is typically sacrificed in an attempt to meet demand. This paper addresses the financial and quality aspects of silvicultural choices as it relates to wood veneers. Five trees each were harvested from an uneven-aged stand and from the following even- aged stands: intensive plantation, conventional plantation, and natural...

Late Veneer consequences on Venus' long term evolution

Science.gov (United States)

Gillmann, C.; Golabek, G.; Tackley, P. J.; Raymond, S. N.

2017-12-01

Modelling of Venus' evolution is able to produce scenarios consistent with present-day observation. These results are however heavily dependent on atmosphere escape and initial volatile inventory. This primordial history (the first 500 Myr) is heavily influenced by collisions. We investigate how Late Veneer impacts change the initial state of Venus and their consequences on its coupled mantle/atmosphere evolution. We focus on volatile fluxes: atmospheric escape and mantle degassing. Mantle dynamics is simulated using the StagYY code. Atmosphere escape covers both thermal and non-thermal processes. Surface conditions are calculated with a radiative-convective model. Feedback of the atmosphere on the mantle through surface temperature is included. Large impacts are capable of contributing to atmospheric escape, volatile replenishment and energy transfer. We use the SOVA hydrocode to take into account volatile loss and deposition during a collision. Large impacts are not numerous enough to substantially erode Venus' atmosphere. Single impacts don't have enough eroding power. Swarms of small bodies (history of the planet and leads to lower present-day surface temperatures. Total depletion of the mantle seems unlikely, meaning either few large impacts (1 to 4) or low energy (slow, grazing…) collisions. Combined with the lack of plate tectonics and volatile recycling in the interior of Venus, Late Veneer collisions could help explain why Venus seems dry today.

Esthetic, occlusal, and periodontal rehabilitation of anterior teeth with minimum thickness porcelain laminate veneers.

Science.gov (United States)

da Cunha, Leonardo Fernandes; Pedroche, Lorena Oliveira; Gonzaga, Carla Castiglia; Furuse, Adilson Yoshio

2014-12-01

Ceramic veneers of minimum thickness provide satisfactory esthetic outcomes while preserving the dental structure. Dental ceramics can both improve the esthetic appearance and reestablish the strength and function of teeth. In worn anterior teeth, functional surfaces, for example, anterior and lateral guidance, can be restored effectively. The characteristics of dental ceramics, such as color stability and mechanical and optical properties, make this material a good choice for indirect restorations, especially when optimum function and esthetics are required. This clinical report presents an occlusal, periodontal, and restorative solution with minimum thickness glass ceramic veneers for worn anterior teeth with multiple diastemas. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Polymerization contraction stress in dentin adhesives bonded to dentin and enamel

NARCIS (Netherlands)

Hashimoto, M.; de Gee, A.J.; Feilzer, A.J.

2008-01-01

Objective In a previous study on of polymerization contraction stress determinations of adhesives bonded to dentin a continuous decline of stress was observed after the adhesives had been light-cured. The decline was ascribed to stress relief caused by diffusion into the adhesive layer of water

PLGA nanoparticles as chlorhexidine-delivery carrier to resin-dentin adhesive interface.

Science.gov (United States)

Priyadarshini, Balasankar Meera; Mitali, Kakran; Lu, Thong Beng; Handral, Harish K; Dubey, Nileshkumar; Fawzy, Amr S

2017-07-01

To characterize and deliver fabricated CHX-loaded PLGA-nanoparticles inside micron-sized dentinal-tubules of demineralized dentin-substrates and resin-dentin interface. Nanoparticles fabricated by emulsion evaporation were assessed in-vitro by different techniques. Delivery of drug-loaded nanoparticles to demineralized dentin substrates, interaction with collagen matrix, and ex-vivo CHX-release profiles using extracted teeth connected to experimental setup simulating pulpal hydrostatic pressure were investigated. Furthermore, nanoparticles association/interaction with a commercial dentin-adhesive applied to demineralized dentin substrates were examined. The results showed that the formulated nanoparticles demonstrated attractive physicochemical properties, low cytotoxicity, potent antibacterial efficacy, and slow degradation and gradual CHX release profiles. Nanoparticles delivered efficiently inside dentinal-tubules structure to sufficient depth (>10μm) against the simulated upward pulpal hydrostatic-pressure, even after bonding-resins infiltration and were attached/retained on collagen-fibrils. These results verified the potential significance of this newly introduced drug-delivery therapeutic strategy for future clinical applications and promote for a new era of future dental research. This innovative drug-delivery strategy has proven to be a reliable method for delivering treatments that could be elaborated for other clinical applications in adhesive and restorative dentistry. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

FT-Raman spectroscopy, µ-EDXRF spectrometry, and microhardness analysis of the dentin of primary and permanent teeth.

Science.gov (United States)

Torres, Carolina Paes; Miranda Gomes-Silva, Jaciara; Menezes-Oliveira, Maria Angélica Hueb; Silva Soares, Luís Eduardo; Palma-Dibb, Regina Guenka; Borsatto, Maria Cristina

2018-05-01

The chemical compositions (organic and inorganic contents) and mechanical behaviors of the dentin of permanent and deciduous teeth were analyzed and compared using X-ray fluorescence spectrometry (µ-EDXRF) Fourier transform Raman spectroscopy (FT-Raman) and a microhardness test (HD). Healthy fresh human primary and permanent molars (n = 10) were selected, The buccal surfaces facing upwards were stabilized in an acrylic plate, flattened, polished, and submitted to the µ-EDXRF, FT-Raman, and HD analysis. The results of the analysis were subjected to ANOVAs and Mann-Whitney U/Student's t multiple comparisons tests. The data showed similar values for the dentin of the primary and permanent teeth in P content, organic content (amide I peak), inorganic content ( PO43- - 430 and 590), and microhardness, Nevertheless, Ca content and Ca/P weight ratio were higher, and the CO32- peak was lower in the dentin of the permanent teeth compared to primary teeth. It be concluded that despite permanent teeth showed more Ca element, both substrates showed similar behavior of chemical and physical properties. © 2018 Wiley Periodicals, Inc.

Treatment of dentin with stannous fluoride - SEM and electron microprobe study

International Nuclear Information System (INIS)

Ellingsen, J.E.; Roella, G.

1987-01-01

The effect of SnF 2 -treatment of dentin surfaces was investigated by means of scanning electron microscopy (SEM) and electron microprobe analysis. Human dentin was treated with aqueous SnF 2 solutions of concentrations varying from 1 to 10%. The treatment periods lasted for 1, 5, 10 or 60 min. Both tin and fluoride were identified on the surfaces. The concentration varied depending on the extensiveness of the treatment. Immersion in 1 M KOH for 15 h removed both tin and fluoride from the surfaces. This reaction was not observed after immersion in H 2 O for the same time period. Examination of the SnF 2 -treated dentin surfaces showed a dense layer of globular particles and in addition some larger particles. The dentinal tubules were totally covered even after the treatment with the lowest concentration of SnF 2 . Deposition of tin- and fluoride-containing globules on dentin surfaces may be of clinical interest. This layer may have importance both for the caries resistance of dentin and for hypersensitivity reactions. (author)

Influence of the number of cycles on shear fatigue strength of resin composite bonded to enamel and dentin using dental adhesives in self-etching mode.

Science.gov (United States)

Tsujimoto, Akimasa; Barkmeier, Wayne W; Erickson, Robert L; Takamizawa, Toshiki; Latta, Mark A; Miyazaki, Masashi

2018-01-30

The influence of the number of cycles on shear fatigue strength to enamel and dentin using dental adhesives in self-etch mode was investigated. A two-step self-etch adhesive and two universal adhesives were used to bond to enamel and dentin in self-etch mode. Initial shear bond strength and shear fatigue strength to enamel and dentin using the adhesive in self-etch mode were determined. Fatigue testing was used with 20 Hz frequency and cycling periods of 50,000, 100,000 and 1,000,000 cycles, or until failure occurred. For each of the cycling periods, there was no significant difference in shear fatigue strength across the cycling periods for the individual adhesives. Differences in shear fatigue strength were found between the adhesives within the cycling periods. Regardless of the adhesive used in self-etch mode for bonding to enamel or dentin, shear fatigue strength was not influenced by the number of cycles used for shear fatigue strength testing.

The induction of dentin bridge-like structures by constructs of subcultured dental pulp-derived cells and porous HA/TCP in porcine teeth.

Science.gov (United States)

Ando, Yusuke; Honda, Masaki J; Ohshima, Hayato; Tonomura, Akiko; Ohara, Takayuki; Itaya, Toshimitsu; Kagami, Hideaki; Ueda, Minoru

2009-02-01

The purpose of this study was to investigate dentin-bridge formation in teeth following the transplantation of dental pulp-derived cells seeded on hydroxyapatite/tricalcium phosphate (HA/TCP) scaffolds. The dental pulp tissues were removed from the extracted first molar teeth of miniature pigs and single cell populations were subcultured. Second-passage cells that had alkaline phosphatase activity were combined with scaffolds. Cell-scaffold constructs were placed in contact with the exposed pulp tissue. The dimensions of the exposed pulp site were approximately 1-2.5 mm in diameter and 2-3 mm in depth from the tooth surface. After placing the constructs, the tooth was restored with composite resin. Six weeks after transplantation, hard tissue formation was observed on the pulp tissue in histology. Dentinal tubule-like structures were observed in most of the hard tissue generated, and columnar cells, which showed positive immunoreactions with dentin sialoprotein (DSP) and heat shock protein (HSP)-25, were aligned beneath the hard tissues. When only scaffolds were placed on the pulp tissues, particles of hard tissue were formed, however dentinal tubule-like structures and odontoblasts were not observed despite the formation of hard tissue. In conclusion, the implantation of dental pulp constructs into pulp exposed stimulates the formation of calcified dentin-like structures.

Effects of a Dicalcium and Tetracalcium Phosphate-Based Desensitizer on In Vitro Dentin Permeability.

Directory of Open Access Journals (Sweden)

Jianfeng Zhou

Full Text Available The present study evaluated the effectiveness of a dicalcium and tetracalcium phosphate-based desensitizer in reducing dentin permeability in vitro. Dentin fluid flow was measured before and after treatment of dentin with patent dentinal tubules using 1 or 3 applications of the dicalcium and tetracalcium phosphate containing agent TeethmateTM (TM and comparing the results with two sodium fluoride varnishes VellaTM (VLA and VanishTM (VAN, after storage in artificial saliva for 24 h, 48 h and 7 days. Significant differences were observed among the 4 methods employed for reducing dentin permeability (p < 0.001 and the 3 post-treatment times (p < 0.001. VLA and VAN never achieved 50% permeability reductions consistently in any of the 3 time periods. Only the calcium phosphate-based desensitizer applied for 3 times consistently reduced dentin permeability by 50% after 24 h. When applied once, the permeability reduction of TM increased progressively over the 3 time periods. After 7 days, only one and three applications of the calcium phosphate-based desensitizer consistently reduced dentin permeability by more than 50%. Permeability reductions corresponded well with scanning electron microscopy examination of dentinal tubule orifice occlusion in dentin specimens treated with the agents. Overall, the dicalcium and tetracalcium phosphate-based desensitizer is effective in reducing dentin permeability via a tubule occlusion mechanism. The ability of the agent to reduce dentin permeability renders it to be potentially useful as a clinical dentin desensitizing agent, which has to be confirmed in future clinical studies. By contrast, the two sodium fluoride varnishes are not effective in dentin permeability reduction and should be considered as topical fluoride delivering agents rather than tubular orifice-blocking agents.

Biodentine-a novel dentinal substitute for single visit apexification

Directory of Open Access Journals (Sweden)

Gurudutt Nayak

2014-05-01

Full Text Available Use of an apical plug in management of cases with open apices has gained popularity in recent years. Biodentine, a new calcium silicate-based material has recently been introduced as a dentine substitute, whenever original dentine is damaged. This case report describes single visit apexification in a maxillary central incisor with necrotic pulp and open apex using Biodentine as an apical barrier, and a synthetic collagen material as an internal matrix. Following canal cleaning and shaping, calcium hydroxide was placed as an intracanal medicament for 1 mon. This was followed by placement of small piece of absorbable collagen membrane beyond the root apex to serve as matrix. An apical plug of Biodentine of 5 mm thickness was placed against the matrix using pre-fitted hand pluggers. The remainder of canal was back-filled with thermoplasticized gutta-percha and access cavity was restored with composite resin followed by all-ceramic crown. One year follow-up revealed restored aesthetics and function, absence of clinical signs and symptoms, resolution of periapical rarefaction, and a thin layer of calcific tissue formed apical to the Biodentine barrier. The positive clinical outcome in this case is encouraging for the use of Biodentine as an apical plug in single visit apexification procedures.

Influence of zirconia framework thickness on residual stress profile in veneering ceramic: measurement by hole-drilling.

Science.gov (United States)

Mainjot, Amélie K; Schajer, Gary S; Vanheusden, Alain J; Sadoun, Michaël J

2012-04-01

Framework design is reported to influence chipping in zirconia-based restorations, which is an important cause of failure of such restorations. Residual stress profile in the veneering ceramic after the manufacturing process is an important predictive factor of the mechanical behavior of the material. The objective of this study is to investigate the influence of framework thickness on the stress profile measured in zirconia-based structures. The stress profile was measured with the hole-drilling method in bilayered disc samples of 20mm diameter with a 1.5 mm thick veneering ceramic layer. Six different framework thicknesses from 0.5 mm to 3 mm were studied. Two different cooling procedures were also investigated. Compressive stresses were observed in the surface, and tensile stresses in the depth of most of the samples. The slow cooling procedure was found to promote the development of interior tensile stresses, except for the sample with a 3mm thick framework. With the tempering procedure, samples with a 1.5 mm thick framework exhibited the most favorable stress profile, while thicker and thinner frameworks exhibited respectively in surface or interior tensile stresses. The measurements performed highlight the importance of framework thickness, which determine the nature of stresses and can explain clinical failures encountered, especially with thin frameworks. The adequate ratio between veneering ceramic and zirconia is hard to define, restricting the range of indications of zirconia-based restorations until a better understanding of such a delicate veneering process is achieved. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

In Vitro Study of Dentin Hypersensitivity Treated by 980-nm Diode Laser.

Science.gov (United States)

Liu, Ying; Gao, Jie; Gao, Yan; Xu, Shuaimei; Zhan, Xueling; Wu, Buling

2013-01-01

To investigate the ultrastructural changes of dentin irradiated with 980-nm diode laser under different parameters and to observe the morphological alterations of odontoblasts and pulp tissue to determine the safety parameters of 980-nm diode laser in the treatment of dentin hypersensitivity (DH). Twenty extracted human third molars were selected to prepare dentin discs. Each dentin disc was divided into four areas and was irradiated by 980-nm diode laser under different parameters: Group A: control group, 0 J/cm(2); Group B: 2 W/CW (continuous mode), 166 J/cm(2); Group C: 3W/CW, 250 J/cm(2); and Group D: 4W/CW, 333 J/cm(2). Ten additional extracted human third molars were selected to prepare dentin discs. Each dentin disc was divided into two areas and was irradiated by 980-nm diode laser: Group E: control group, 0 J/cm(2); and Group F: 2.0 W/CW, 166 J/cm(2). The morphological alterations of the dentin surfaces and odontoblasts were examined with scanning electron microscopy (SEM), and the morphological alterations of the dental pulp tissue irradiated by laser were observed with an upright microscope. The study demonstrated that dentinal tubules can be entirely blocked after irradiation by 980-nm diode laser, regardless of the parameter setting. Diode laser with settings of 2.0 W and 980-nm sealed exposed dentin tubules effectively, and no significant morphological alterations of the pulp and odontoblasts were observed after irradiation. Irradiation with 980-nm diode laser could be effective for routine clinical treatment of DH, and 2.0W/CW (166 J/cm(2)) was a suitable energy parameter due to its rapid sealing of the exposed dentin tubules and its safety to the odontoblasts and pulp tissue.

In Vitro Study of Dentin Hypersensitivity Treated by 980-nm Diode Laser

Science.gov (United States)

Liu, Ying; Gao, Jie; Gao, Yan; XU, Shuaimei; Zhan, Xueling; Wu, Buling

2013-01-01

Introduction: To investigate the ultrastructural changes of dentin irradiated with 980-nm diode laser under different parameters and to observe the morphological alterations of odontoblasts and pulp tissue to determine the safety parameters of 980-nm diode laser in the treatment of dentin hypersensitivity (DH). Methods: Twenty extracted human third molars were selected to prepare dentin discs. Each dentin disc was divided into four areas and was irradiated by 980-nm diode laser under different parameters: Group A: control group, 0 J/cm2; Group B: 2 W/CW (continuous mode), 166 J/cm2; Group C: 3W/CW, 250 J/cm2; and Group D: 4W/CW, 333 J/cm2. Ten additional extracted human third molars were selected to prepare dentin discs. Each dentin disc was divided into two areas and was irradiated by 980-nm diode laser: Group E: control group, 0 J/cm2; and Group F: 2.0 W/CW, 166 J/cm2. The morphological alterations of the dentin surfaces and odontoblasts were examined with scanning electron microscopy (SEM), and the morphological alterations of the dental pulp tissue irradiated by laser were observed with an upright microscope. Results: The study demonstrated that dentinal tubules can be entirely blocked after irradiation by 980-nm diode laser, regardless of the parameter setting. Diode laser with settings of 2.0 W and 980-nm sealed exposed dentin tubules effectively, and no significant morphological alterations of the pulp and odontoblasts were observed after irradiation. Conclusions: Irradiation with 980-nm diode laser could be effective for routine clinical treatment of DH, and 2.0W/CW (166 J/cm2) was a suitable energy parameter due to its rapid sealing of the exposed dentin tubules and its safety to the odontoblasts and pulp tissue. PMID:25606318

Temperature changes across CO2-lased dentin during multiple exposures

Science.gov (United States)

Zakariasen, Kenneth L.; Barron, Joseph R.; Boran, Thomas L.

1990-06-01

The literature increasingly indicates that lasers will have a multitude of applications for dental hard tissue procedures, e.g. preventive therapy, caries removal, laser etching and endodontic therapy. However, it is critical that such laser therapies avoid the production of heat levels which will be damaging to the surrounding vital tissues, such as the dental pulp and periodontal tissues. Our preliminary research on temperature changes across C02 lased dentin indicated that for single preventive therapeutic exposures (1.2 W., 0. 1 sec., 1.0 mm focal spot) the mean temperature rise across 350 j.tm of dentin was 0.57 0C while across 1000 .tm of dentin the mean rise was only 0.18 °C. Further research utilizing multiple preventive therapeutic exposures (1.2 W., 0. 1 sec., 1.0 mm focal spot, 3 x 1.0 sec. intervals) showed mean temperature elevations of 1.56 0C across 350 m of dentin and 0.66 O across 1000 xm of dentin. While these temperature elevations, which would be associated with preventive therapy, are very low and would be biologically acceptable, it must be noted that exposures of higher intensities are required to fuse enamel and porcelain, or remove decay. This current research investigates temperature elevations which occuT during C02 lasing utilizing the following exposure parameters: 8.0 W., 1.0 mm focal spot, 0.1 sec. exposures, 2 or 4 exposures per site pulsed 1.0 sec. apart. Three dentin thicknesses were utilized, i.e. 1000 jim, 1500 p.tm and 2000 .tm. Four sections of each thickness were utilized with four exposure sites per specimen (2 with 2 exposures, 2 with 4 exposures). All dentin sections were prepared from non-carious third molars using a hard tissue microtome. A thermistor was placed on the dentin surface opposite each lased site and temperature changes were recorded for approximately 50 sec. following lasing. Mean temperature elevations ranged from a high of 3.07 C for the 1000 xm section utilizing four exposures to a low of 0.37 0C for the

Prevention of root caries with dentin adhesives.

Science.gov (United States)

Grogono, A L; Mayo, J A

1994-04-01

This in vitro investigation determined the feasibility of using dentin adhesives to protect root surfaces against caries. The roots of 22 recently extracted human teeth were all painted with a protective lacquer leaving two unprotected small windows. On each specimen, one window (control) was left untreated and the other window (experimental) was treated using a dentin adhesive (Scotchbond Multi-Purpose). The roots were then immersed in an in vitro acetate/calcium/phosphate demineralization model at pH 4.3. After 70 days, the samples were removed and sectioned through the windows. The undecalcified ground sections were examined under transmitted and polarized light. Lesions characteristic of natural root caries were seen in the untreated control windows. No such lesions were apparent in the experimental windows. The results of this preliminary study suggest that dentin adhesives may provide protection against root caries.

Six-month storage-time evaluation of one-bottle adhesive systems to dentin.

Science.gov (United States)

Giannini, Marcelo; Seixas, Carla Alessandra Marcelino; Reis, Andre Figueiredo; Pimenta, Luiz André Freire

2003-01-01

The goal of this study was to evaluate the 1-week, 3-month, and 6-month performance of eight commercially available one-bottle adhesive systems to dentin. Lingual and buccal surfaces from human third molars were ground wet on 600-grit SiC paper to obtain a flat dentinal surface. The specimens were randomly divided into 24 groups (n = 10), which were established to measure the shear bond strengths of Bond-1 (B1), ONE-STEP (OS), OptiBond SOLO (OP), Prime & Bond 2.1 (PB), Single Bond (SB), STAE (ST), Syntac Sprint (SS), and Tenure Quick (TQ) after 1-week, 3-month, and 6-month water storage at 37 degrees C. One-bottle adhesives were applied according to manufacturers' instructions and Z100 composite cylinders were applied on the bonded dentinal surfaces. The 3-month water-storage groups were thermocycled for 1500 cycles at 5 degrees C and 55 degrees C and 6-month groups for 3000 cycles. After storage periods, specimens were tested in shear in a universal testing machine (0.5 mm/min). were statistically analyzed by analysis of variance and Tukey test. Results: The changes in shear bond strengths were not uniform over time. Over the test period, OS, PB, SB, and SS exhibited bond strength stability, however, SS presented low bond strengths on all tested periods. A significant decrease in bond strength was observed for B1, OP, ST, and TQ after the 6-month storage period.

Role of Alcohol on the Fracture Resistance of Dentin

Energy Technology Data Exchange (ETDEWEB)

Nalla, Ravi K.; Kinney, John H.; Tomsia, Antoni P.; Ritchie,Robert O.

2006-05-01

Healthy dentin, the mineralized tissue that makes up the bulk of the tooth, is naturally hydrated in vivo; however, it is known that various chemical reagents including acetone and ethanol can induce dehydration and thereby affect its properties. Here, we seek to investigate this in light of the effect alcohol can have on the mechanical properties of dentin, specifically by measuring the stiffness, strength and toughness of dentin in simulated body fluid and scotch whisky. Results indicate that chemical dehydration induced by the whisky has a significant beneficial effect on the elastic modulus, strength and fracture toughness of dentin. Although this makes teeth more resistant to fracture, the change in properties is fully reversible upon rehydration. This effect is considered to be associated with increased cross-linking of the collagen molecules from intermolecular hydrogen-bonding where water is replaced with weaker hydrogen-bond forming solvents such as alcohol.

Effects of different desensitizing treatments on root dentin permeability

Directory of Open Access Journals (Sweden)

Raydsa Raíssa Moura ROSA

Full Text Available Abstract The objective of this study was to evaluate the effects of diode laser and a desensitizing dentifrice on dentin permeability. Fifty-two root dentin fragments were obtained (5 × 5mm and treated with 24% EDTA gel. The samples were divided into 4 groups (n = 13: G1, control (no treatment; G2, diode laser (λ = 908 nm, 1.5 W, continuous mode, 20s; G3, application of abrasive dentifrice for 1 minute (Elmex Sensitive Professional (International Gaba; and G4, application of abrasive dentifrice for 1 minute followed by irradiation with diode laser. Ten samples per group were immersed in 2% methylene blue solution for 4h. The specimens were washed, longitudinally sectioned, observed under optical microscopy, photographed and assessed based on the degree of dye leakage. The remaining samples were observed under scanning electron microscopy (SEM. The leakage data were subjected to ANOVA test, followed by Tukey’s t-test (α = 5%. Groups 2, 3 and 4 showed less dye penetration than the control group (p < 0.05, but were similar among each other. SEM images showed that dentinal tubules were open in G1, and fused and occluded in G2. Group 3 showed dentinal tubules that were occluded by the metal ions from the toothpaste. G4 presented similar characteristics to G3, and the presence of fused dentin. The diode laser and the dentifrice were effective in reducing dentinal permeability, and the combination of the two treatments did not show better results than either one used alone.

Multivariate analysis of attenuated total reflection Fourier transform infrared (ATR FT-IR) spectroscopic data to confirm phase partitioning in methacrylate-based dentin adhesive.

Science.gov (United States)

Ye, Qiang; Parthasarathy, Ranganathan; Abedin, Farhana; Laurence, Jennifer S; Misra, Anil; Spencer, Paulette

2013-12-01

Water is ubiquitous in the mouths of healthy individuals and is a major interfering factor in the development of a durable seal between the tooth and composite restoration. Water leads to the formation of a variety of defects in dentin adhesives; these defects undermine the tooth-composite bond. Our group recently analyzed phase partitioning of dentin adhesives using high-performance liquid chromatography (HPLC). The concentration measurements provided by HPLC offered a more thorough representation of current adhesive performance and elucidated directions to be taken for further improvement. The sample preparation and instrument analysis using HPLC are, however, time-consuming and labor-intensive. The objective of this work was to develop a methodology for rapid, reliable, and accurate quantitative analysis of near-equilibrium phase partitioning in adhesives exposed to conditions simulating the wet oral environment. Analysis by Fourier transform infrared (FT-IR) spectroscopy in combination with multivariate statistical methods, including partial least squares (PLS) regression and principal component regression (PCR), were used for multivariate calibration to quantify the compositions in separated phases. Excellent predictions were achieved when either the hydrophobic-rich phase or the hydrophilic-rich phase mixtures were analyzed. These results indicate that FT-IR spectroscopy has excellent potential as a rapid method of detection and quantification of dentin adhesives that experience phase separation under conditions that simulate the wet oral environment.

Ceramic (Feldspathic & IPS Empress II) vs. laboratory composite (Gradia) veneers; a comparison between their shear bond strength to enamel; an in vitro study.

Science.gov (United States)

Nikzad, S; Azari, Abbas; Dehgan, S

2010-07-01

Patient demand for aesthetic dentistry is steadily growing. Laminates and free metal restorations have evolved in an attempt to overcome the invasiveness nature of full veneer restorations. Although many different materials have been used for making these restorations, there is no single material that fits best for all purposes. Two groups of ceramic material (Feldspathic and IPS Empress II) and one group of laboratory composite (Gradia) discs (10 discs in each group; 4 mm in diameter and 2 mm in thickness) were prepared according to the manufacturer's instruction. The surface of ceramic discs were etched and silanized. In Gradia group, liquid primer was applied on composite surfaces. Thirty freshly extracted sound human molars and premolars were randomly divided into three groups. The enamel surface of each tooth was slightly flattened (0.3 mm) on the buccal or lingual side and then primed and cemented to the prepared discs with the aid of a dental surveyor. The finishing specimens were thermocycled between 5 degrees C and 55 degrees C for 2500 cycles and then prepared for shear bond strength testing. The resulting data were analyzed by one-way anova and Tukey HSD test. The fractured surfaces of each specimen were inspected by means of stereomicroscope and SEM. There is significant difference between the bond strength of materials tested. The mean bond strengths obtained with Feldspathic ceramic, IPS Empress II and Gradia were 33.10 +/- 4.31 MPa, 26.04 +/- 7.61 MPa and 14.42 +/- 5.82 MPa, respectively. The fracture pattern was mainly mixed for ceramic groups. More scientific evidence needed for standardization of bonding protocols.

Effects of solvents on the early stage stiffening rate of demineralized dentin matrix.

Science.gov (United States)

Garcia, Fernanda C P; Otsuki, Masayuki; Pashley, David H; Tay, Franklin R; Carvalho, Ricardo M

2005-05-01

To monitor the stiffening rate of demineralized dentin matrix at the early stages after exposure to different neat solvents. Dentin beams approximately 0.8x0.7x8.0 mm were obtained from human third molars. After covering their ends with resin composite, the middle exposed length of 4.0mm (gauge-length) was demineralized in 0.5 M EDTA (pH 7.0) for 7 days. The specimens were gripped by a testing machine, pre-loaded to 10 g and cyclically stressed in tension to 5% strain, for 30 repeated cycles (total 20 min) at 0.6 mm/min while immersed in water (control). Then, water was replaced by either 100% acetone, methanol, ethanol, propanol, HEMA or air and the specimens subjected to the same cyclic protocol. The maximum apparent modulus of elasticity (E(Max)) was calculated for every cycle, plotted as a function of time and subjected to regression analysis. Stiffening rate was calculated as changes in E (min). Regression analysis examined the relationship between E and time for each solvent. Data were analyzed by one-way ANOVA and Student-Newman-Keuls test at alpha=0.05. Regression analysis showed that E increased significantly with time in all water-free solvents (R2=0.8-0.99). Stiffening rate was higher for acetone (0.9 MPa/min) and ethanol (0.8 MPa/min), intermediate for air (0.7 MPa/min), methanol (0.6 MPa/min) and propanol (0.5 MPa/min), lower for HEMA (0.2 MPa/min) and practically none for water (0.07 MPa/min) with prate of demineralized dentin matrix is both time and solvent-dependent. The ability of solvents to promptly stiffen the demineralized dentin matrix may be important in maintaining the resin-infiltrated matrix expanded during the solvent evaporation stage of resin bonding.

Penetration pattern of rhodamine dyes into enamel and dentin: confocal laser microscopy observation.

Science.gov (United States)

Kwon, S R; Wertz, P W; Li, Y; Chan, D C N

2012-02-01

Enamel and dentin are susceptible to extrinsic and intrinsic stains. The purposes of this study were to determine the penetration pattern of Rhodamine B and dextran-conjugated Rhodamine B into the enamel and dentin as observed by confocal laser microscopy and to relate it to the penetration pattern of hydrogen peroxide commonly used as an active ingredient in tooth-whitening agents and high-molecular-weight staining molecules. Eighteen recently extracted human maxillary anterior teeth were used. Teeth were cleaned and painted with nail varnish except for the crown area above the cemento-enamel junction (CEJ). The painted teeth were then immersed in Rhodamine B and dextran-conjugated Rhodamine B (70 000 MW) for 4, 7, 10 and 15 days. Teeth were sliced to 3 mm thickness in transverse plane and mounted on a glass slide just prior to observation with confocal laser microscopy. Rhodamine B and dextran-conjugated Rhodamine B readily penetrated into the enamel and dentin when exposed for 4 and 7 days, respectively. Rhodamine B penetrated along the interprismatic spaces of the enamel into the dentin. The penetration was accentuated in sections with existing crack lines in the enamel. Rhodamine B was readily absorbed into the dentinal tubules at the dentino-enamel junction and continued to penetrate through the dentin via the dentinal tubules into the pre-dentin. Within the limitations of this study, it is concluded that Rhodamine B and dextran-conjugated Rhodamine B when applied to the external surface of the tooth readily penetrate into the enamel and dentin via the interprismatic spaces in the enamel and dentinal tubules in the dentin, suggesting that stain molecules and bleaching agents possibly exhibit similar penetration pathways. © 2011 The Authors. ICS © 2011 Society of Cosmetic Scientists and the Société Française de Cosmétologie.

Shear bond strength of three adhesive systems to enamel and dentin of permanent teeth

Directory of Open Access Journals (Sweden)

Niloofar Shadman

2012-01-01

Full Text Available Background and Aims: The purpose of this experimental study was to investigate the shear bond strength of three new adhesive systems to enamel and dentin of permanent human teeth using three new etch and rinse and self-etch adhesive systems.Materials and Methods: Sixty intact caries-free third molars were selected and randomly divided into 6 groups. Flat buccal and lingual enamel and dentin surfaces were prepared and mounted in the acrylic resin perpendicular to the plan of the horizon. Adhesives used in this study were Tetric N-Bond, AdheSE and AdheSE-One F (Ivoclar/Vivadent, Schaan, Liechtenstein. The adhesives were applied on the surfaces and cured with quartz tungsten halogen curing unit (600 mW/cm2 intensity for 20 s. After attaching composite to the surfaces and thermocycling (500 cycles, 5-55ºC, shear bond strength was measured using a universal testing machine at a crosshead speed of 0.5 mm/min. The failure modes were examined under a stereomicroscope. The data were statistically analyzed using T-test, one-way ANOVA, Tukey and Fisher's exact tests.Results: In enamel, Tetric N-Bond (28.57±4.58 MPa and AdheSE (21.97±7.6 MPa had significantly higher bond strength than AdheSE-One F (7.16±2.09 MPa (P0.05.Conclusion: Shear bond strength to dentin in Tetric N-Bond (etch and rinse system( was higher than self-etch adhesives (AdheSE and AdheSE-One F. The bond strength to enamel and dentin in two-step self-etch (AdheSE was higher than one-step self-etch (AdheSE-One F.

Effect of dentin pretreatment with potassium oxalate: analysis of microtensile bond strengths and morphologic aspects.

Science.gov (United States)

De Moraes Porto, Isabel Cristina Celerino; De Andrade, Ana Karina Maciel; Alves, Luiz Carlos; Braz, Rodivan

2012-02-01

An effective and stable bond is the most desirable characteristic of contemporary adhesive systems. The aim of this study was to evaluate the effect of potassium oxalate on dentin/resin bond strength. Dentin on the occlusal surface of human premolars was exposed and etched with 35% phosphoric acid, to receive 3% monohydrated potassium oxalate and the following adhesive systems: Scotchbond Multipurpose (SMO; 3M/ESPE) and Prime & Bond NT (PBO; Dentsply), followed by the application of resin composite (Z250; 3M/ESPE). The control groups (SM and PB) did not receive potassium oxalate application. The prepared teeth were kept in distilled water at 37°C for 24 h and 12 months. They were then cut longitudinally into sticks with a bond area of ∼0.8 mm(2) for submission to the microtensile bond strength test. The data were analyzed by two-factor ANOVA, Tamhane's paired comparisons, and the Student t-test (α = 0.05). The hybrid layer formed was observed by scanning electron microscopy (SEM). SEM analysis of the surfaces treated with PB revealed shorter resin tags associated with the application of potassium oxalate, whereas SM showed tags similar to those without potassium oxalate. A significant difference was shown between the two storage times for each of the protocols. There was a significant difference among SMO, SM, and PBO (24 h), as well as among SM, SMO, and PBO, and between PB and PBO (12 months). The application of potassium oxalate before conventional adhesive systems may result in alteration of the bond strength between dentin and resin composite, depending on the material. Copyright © 2011 Wiley Periodicals, Inc.

Comparative study of etched enamel and dentin for the adhesion of composite resins with the Er:YAG 2,94 μm laser and CO2 9,6 μm laser: morphological (SEM) and tensile bond strength analysis

International Nuclear Information System (INIS)

Marraccini, Tarso Mugnai

2002-01-01

The aim of this study was to evaluate and compare the tensile bond strength of a composite resin adhered to the enamel and dentin which have received superficial irradiation with an Er:YAG laser (2.94 μm) or with CO 2 laser ( 9.6 μm) and later on etched with the phosphoric acid at 35%. After the use of the adhesive system, resin cones were made on the etched surfaces by both lasers and tensile bond strength tests were performed. All samples were observed at the SEM - there was an increase of the degree of fusion and resolidification in the irradiated enamel and dentin samples with the CO 2 laser (9.6 μm), creating a vitrified layer with tiny craters. With the Er:YAG laser (2.94 μm) there were typical morphological explosive microablation with the exposition of the tubules in the dentin.The surface acquired by the association of the CO 2 laser ( 9.6 μm) plus acid etching no longer presented the aspect of fusion being this layer completely removed. There were statistical significant differences among ali three methods of etching in the treatment of the enamel and dentin surface. The tensile bond strength test showed that etching of these enamel and dentin surfaces with acid exclusively (control group) presented great values, surpassing the values of the etching acquired with the Er:YAG laser (2.94 μ) plus acid or the CO 2 laser (9.6 μm) plus acid. With the parameters used in this experiment the Er:YAG laser (2.94 μm) showed to be more effective than the CO 2 laser (9.6 μm) for the hard dental surfaces etching procedure. (author)

Composite Resin – A Versatile Restorative Tool | Koleoso | Nigerian ...

African Journals Online (AJOL)

... the use of composite resin restorations as a treatment option in several situations where conventional aesthetic restorations such as porcelain veneers, crowns and cream-metal crown could otherwise be placed. Methods and Materials: Patients who presented with restoration aesthetic challenges over a six months period ...

Pre-sintered Y-TZP sandblasting: effect on surface roughness, phase transformation, and Y-TZP/veneer bond strength