  1. WO3 nano-ribbons: their phase transformation from tungstite (WO3·H2O) to tungsten oxide (WO3)

    DEFF Research Database (Denmark)

    Ahmadi, Majid; Sahoo, Satyaprakash; Younesi, Reza

    2014-01-01

    Tungsten oxide (WO3) nano-ribbons (NRs) were obtained by annealing tungstite (WO3·H2O) NRs. The latter was synthesized below room temperature using a simple, environmentally benign, and low cost aging treatment of precursors made by adding hydrochloric acid to diluted sodium tungstate solutions (...

  2. Tungsten oxide-graphene oxide (WO3-GO) nanocomposite as an efficient photocatalyst, antibacterial and anticancer agent

    Science.gov (United States)

    Jeevitha, G.; Abhinayaa, R.; Mangalaraj, D.; Ponpandian, N.

    2018-05-01

    Functioning of ultrasonically prepared tungsten oxide-graphene oxide (WO3-GO) nanocomposite as a photocatalyst, antibacterial and anticancer system was investigated and the obtained results were compared with that of pure WO3 nanoparticles. Structural, morphological, compositional and optical properties of the prepared WO3 nanoparticles and WO3-GO nanocomposite were studied. Photocatalytic efficiency of the system on organic dyes such as methylene blue (MB, cationic) and indigo carmine (IC, anionic) was investigated. The enhanced efficiency of the WO3-GO nanocomposite system was evaluated under sunlight and compared with that of pure WO3. The degradation efficiency values for MB and IC were found to be 97.03% and 95.43% at 180 and 120 min respectively. Antibacterial activity of the WO3-GO nanocomposite under visible light was tested and improved inhibition results were observed for Escherichia coli and Bacillus subtilis after 6 h of light exposure. The photocatalytic degradation efficiency and antibacterial activity of the WO3-GO nanocomposite are attributed to the improved electron-hole pair separation rate. Investigation on anticancer activity of WO3-GO nanocomposite was tested on human lung cancer (A-549) cell line and the IC50 value was found to be 139.6 ± 4.53 μg/mL. The results obtained in this study may be used as a platform for the development of photocatalysis applications based on WO3-GO nanocomposite.

  3. Tungsten oxide (WO3) thin films for application in advanced energy systems

    International Nuclear Information System (INIS)

    Gullapalli, S. K.; Vemuri, R. S.; Manciu, F. S.; Enriquez, J. L.; Ramana, C. V.

    2010-01-01

    Inherent processes in coal gasification plants produce hazardous hydrogen sulfide (H 2 S), which must be continuously and efficiently detected and removed before the fuel is used for power generation. An attempt has been made in this work to fabricate tungsten oxide (WO 3 ) thin films by radio-frequency reactive magnetron-sputter deposition. The impetus being the use of WO 3 films for H 2 S sensors in coal gasification plants. The effect of growth temperature, which is varied in the range of 30-500 deg. C, on the growth and microstructure of WO 3 thin films is investigated. Characterizations made using scanning electron microscopy (SEM) and x-ray diffraction (XRD) indicate that the effect of temperature is significant on the microstructure of WO 3 films. XRD and SEM results indicate that the WO 3 films grown at room temperature are amorphous, whereas films grown at higher temperatures are nanocrystalline. The average grain-size increases with increasing temperature. WO 3 films exhibit smooth morphology at growth temperatures ≤300 deg. C while relatively rough at >300 deg. C. The analyses indicate that the nanocrystalline WO 3 films grown at 100-300 deg. C could be the potential candidates for H 2 S sensor development for application in coal gasification systems.

  4. Electronic structure of nanoparticles of substoichometric hexagonal tungsten oxides

    International Nuclear Information System (INIS)

    Khyzhun, O Y; Solonin, Y M

    2007-01-01

    X-ray photoelectron spectroscopy (XPS), X-ray emission spectroscopy (XES) and X-ray absorption spectroscopy (XAS) methods were used to study the electronic structure of hexagonal h-WO 3 and h-WO 2.8 nanoparticles. For comparison, nanopowder substoichiometric monoclinic tungsten oxides with close content of oxygen atoms, namely m-WO 3 and m-WO 2.77 compounds, were also investigated. For the mentioned oxides, XPS valence-band and corelevel spectra, XES O Kα bands and XAS W L III and O 1s edges were derived. The XPS valence-band spectra and O Kα emission bands in the mentioned hexagonal and monoclinic tungsten oxides were compared on a common energy scale. Both the O Kα bands and XPS valence-band spectra broaden somewhat in the sequences h-WO 3 → h-WO 2.8 and m-WO 3 → m-WO 2.77 , with the half-widths of the spectra being somewhat higher for the hexagonal oxides as compared with those for the monoclinic compounds. The effective positive charge state of tungsten atoms in h-WO 2.8 is very close to that in m-WO 2.77 , but the negative charge states of oxygen atoms are close to each other for all the tungsten oxides under consideration

  5. Cyclic Nanostructures of Tungsten Oxide (WO3)n  (n = 2–6) as NOx Gas Sensor: A Theoretical Study

    Science.gov (United States)

    Izadyar, Mohammad; Jamsaz, Azam

    2014-01-01

    Today's WO3-based gas sensors have received a lot of attention, because of important role as a sensitive layer for detection of the small quantities of  NOx. In this research, a theoretical study has been done on the sensing properties of different cyclic nanoclusters of (WO3)n  (n = 2–6) for NOx  (x = 1,2) gases. Based on the calculated adsorption energies by B3LYP and X3LYP functionals, from the different orientations of  NOx molecule on the tungsten oxide clusters, O–N⋯W was preferred. Different sizes of the mentioned clusters have been analyzed and W2O6 cluster was chosen as the best candidate for NOx detection from the energy viewpoint. Using the concepts of the chemical hardness and electronic charge transfer, some correlations between the energy of adsorption and interaction energy have been established. These analyses confirmed that the adsorption energy will be boosted with charge transfer enhancement. However, the chemical hardness relationship is reversed. Finally, obtained results from the natural bond orbital and electronic density of states analysis confirmed the electronic charge transfer from the adsorbates to WO3 clusters and Fermi level shifting after adsorption, respectively. The last parameter confirms that the cyclic clusters of tungsten oxide can be used as NOx gas sensors. PMID:25544841

  6. Cyclic Nanostructures of Tungsten Oxide WO3n  (n=2–6 as NOx Gas Sensor: A Theoretical Study

    Directory of Open Access Journals (Sweden)

    Mohammad Izadyar

    2014-01-01

    Full Text Available Today’s WO3-based gas sensors have received a lot of attention, because of important role as a sensitive layer for detection of the small quantities of  NOx. In this research, a theoretical study has been done on the sensing properties of different cyclic nanoclusters of WO3n  (n=2–6 for NOx  (x=1,2 gases. Based on the calculated adsorption energies by B3LYP and X3LYP functionals, from the different orientations of  NOx molecule on the tungsten oxide clusters, O–N⋯W was preferred. Different sizes of the mentioned clusters have been analyzed and W2O6 cluster was chosen as the best candidate for NOx detection from the energy viewpoint. Using the concepts of the chemical hardness and electronic charge transfer, some correlations between the energy of adsorption and interaction energy have been established. These analyses confirmed that the adsorption energy will be boosted with charge transfer enhancement. However, the chemical hardness relationship is reversed. Finally, obtained results from the natural bond orbital and electronic density of states analysis confirmed the electronic charge transfer from the adsorbates to WO3 clusters and Fermi level shifting after adsorption, respectively. The last parameter confirms that the cyclic clusters of tungsten oxide can be used as NOx gas sensors.

  7. Cyclic Nanostructures of Tungsten Oxide (WO3) n   (n = 2-6) as NO x Gas Sensor: A Theoretical Study.

    Science.gov (United States)

    Izadyar, Mohammad; Jamsaz, Azam

    2014-01-01

    Today's WO3-based gas sensors have received a lot of attention, because of important role as a sensitive layer for detection of the small quantities of  NO x . In this research, a theoretical study has been done on the sensing properties of different cyclic nanoclusters of (WO3) n   (n = 2-6) for NO x   (x = 1,2) gases. Based on the calculated adsorption energies by B3LYP and X3LYP functionals, from the different orientations of  NO x molecule on the tungsten oxide clusters, O-N⋯W was preferred. Different sizes of the mentioned clusters have been analyzed and W2O6 cluster was chosen as the best candidate for NO x detection from the energy viewpoint. Using the concepts of the chemical hardness and electronic charge transfer, some correlations between the energy of adsorption and interaction energy have been established. These analyses confirmed that the adsorption energy will be boosted with charge transfer enhancement. However, the chemical hardness relationship is reversed. Finally, obtained results from the natural bond orbital and electronic density of states analysis confirmed the electronic charge transfer from the adsorbates to WO3 clusters and Fermi level shifting after adsorption, respectively. The last parameter confirms that the cyclic clusters of tungsten oxide can be used as NO x gas sensors.

  8. Physical properties characterization of WO3 films grown by hot-filament metal oxide deposition

    International Nuclear Information System (INIS)

    Diaz-Reyes, J.; Delgado-Macuil, R.J.; Dorantes-Garcia, V.; Perez-Benitez, A.; Balderas-Lopez, J.A.; Ariza-Ortega, J.A.

    2010-01-01

    WO 3 is grown by hot-filament metal oxide deposition (HFMOD) technique under atmospheric pressure and an oxygen atmosphere. By X-ray diffraction obtains that WO 3 presents mainly monoclinic crystalline phase. The chemical stoichiometry is obtained by X-ray Photoelectron Spectroscopy (XPS). The IR spectrum of the as-grown WO 3 presents broad peaks in the range of 1100 to 3600 cm -1 . A broad band in the 2200 to 3600 cm -1 region and the peaks sited at 1645 and 1432 cm -1 are well resolved, which are originated from moisture and are assigned to ν(OH) and δ(OH) modes of adsorbed water and the corresponding tungsten oxide vibrations are in infrared region from 400 to 1453 cm -1 and around 3492 cm -1 , which correspond to tungsten-oxygen (W-O) stretching, bending and lattice modes. The Raman spectrum shows intense peaks at 801, 710, 262 and 61 cm -1 that are typical Raman peaks of crystalline WO 3 (m-phase) that correspond to stretching vibrations of the bridging oxygen, which are assigned to W-O stretching (ν) and W-O bending (δ) modes, respectively. By transmittance measurements obtains that the WO 3 band gap can be varied from 2.92 to 3.13 eV in the investigated annealing temperature range.

  9. Preparation of tungsten coatings on graphite by electro-deposition via Na2WO4–WO3 molten salt system

    International Nuclear Information System (INIS)

    Sun, Ning-bo; Zhang, Ying-chun; Jiang, Fan; Lang, Shao-ting; Xia, Min

    2014-01-01

    Highlights: • Tungsten coatings on graphite were firstly obtained by electro-deposition method via Na 2 WO 4 –WO 3 molten salt system. • Uniform and dense tungsten coatings could be easily prepared in each face of the sample, especially the complex components. • The obtained tungsten coatings are with high purity, ultra-low oxygen content (about 0.022 wt%). • Modulate pulse parameters can get tungsten coatings with different thickness and hardness. - Abstract: Tungsten coating on graphite substrate is one of the most promising candidate materials as the ITER plasma facing components. In this paper, tungsten coatings on graphite substrates were fabricated by electro-deposition from Na 2 WO 4 –WO 3 molten salt system at 1173 K in atmosphere. Tungsten coatings with no impurities were successfully deposited on graphite substrates under various pulsed current densities in an hour. By increasing the current density from 60 mA cm −2 to 120 mA cm −2 an increase of the average size of tungsten grains, the thickness and the hardness of tungsten coatings occurs. The average size of tungsten grains can reach 7.13 μm, the thickness of tungsten coating was in the range of 28.8–51 μm, and the hardness of coating was higher than 400 HV. No cracks or voids were observed between tungsten coating and graphite substrate. The oxygen content of tungsten coating is about 0.022 wt%

  10. Improved Charge Separation in WO3/CuWO4 Composite Photoanodes for Photoelectrochemical Water Oxidation

    Directory of Open Access Journals (Sweden)

    Danping Wang

    2016-05-01

    Full Text Available Porous tungsten oxide/copper tungstate (WO3/CuWO4 composite thin films were fabricated via a facile in situ conversion method, with a polymer templating strategy. Copper nitrate (Cu(NO32 solution with the copolymer surfactant Pluronic®F-127 (Sigma-Aldrich, St. Louis, MO, USA, generic name, poloxamer 407 was loaded onto WO3 substrates by programmed dip coating, followed by heat treatment in air at 550 °C. The Cu2+ reacted with the WO3 substrate to form the CuWO4 compound. The composite WO3/CuWO4 thin films demonstrated improved photoelectrochemical (PEC performance over WO3 and CuWO4 single phase photoanodes. The factors of light absorption and charge separation efficiency of the composite and two single phase films were investigated to understand the reasons for the PEC enhancement of WO3/CuWO4 composite thin films. The photocurrent was generated from water splitting as confirmed by hydrogen and oxygen gas evolution, and Faradic efficiency was calculated based on the amount of H2 produced. This work provides a low-cost and controllable method to prepare WO3-metal tungstate composite thin films, and also helps to deepen the understanding of charge transfer in WO3/CuWO4 heterojunction.

  11. Study of the tungsten bronze Ag0.01WO3 using positron annihilation method

    International Nuclear Information System (INIS)

    Dryzek, J.; Dryzek, E.; Placzek, A.

    1992-01-01

    The study of the positron annihilation and the Seebeck effect was performed on silver doped tungsten trioxide of composition Ag 0.01 WO 3 and the tungsten trioxide phase: WO 2.90 (W 20 O 58 ). Both methods point out that there are some clusters of Ag + ions in the first compound and oxygen vacancies in the second case. The clusters have some internal substructure. The measurements of the Seebeck effect showed that Ag 0.01 WO 3 is normal n-type semiconductor whereas WO 2.90 exhibits metal-like properties

  12. Thermal oxidation of tungsten-based sputtered coatings

    International Nuclear Information System (INIS)

    Louro, C.; Cavaleiro, A.

    1997-01-01

    The effect of the addition of nickel, titanium, and nitrogen on the air oxidation behavior of W-based sputtered coatings in the temperature range 600 to 800 C was studied. In some cases these additions significantly improved the oxidation resistance of the tungsten coatings. As reported for bulk tungsten, all the coatings studied were oxidized by layers following a parabolic law. Besides WO 3 and WO x phases detected in all the oxidized coatings, TiO 2 and NiWO 4 were also detected for W-Ti and W-Ni films, respectively. WO x was present as an inner protective compact layer covered by the porous WO 3 oxide. The best oxidation resistance was found for W-Ti and W-N-Ni coatings which also presented the highest activation energies (E a = 234 and 218 kJ/mol, respectively, as opposed to E a ∼ 188 kJ/mol for the other coatings). These lower oxidation weight gains were attributed to the greater difficulty of the inward diffusion of oxygen ions for W-Ti films, owing to the formation of fine particles of TiO 2 , and the formation of the external, more protective layer of NiWO 4 for W-N-Ni coatings

  13. Physical properties characterization of WO{sub 3} films grown by hot-filament metal oxide deposition

    Energy Technology Data Exchange (ETDEWEB)

    Diaz-Reyes, J., E-mail: jdiazr2001@yahoo.com [Centro de Investigacion en Biotecnologia Aplicada del Instituto Politecnico Nacional, Ex-Hacienda de San Juan Molino, Km. 1.5, Tepetitla, Tlaxcala, 90700 (Mexico); Delgado-Macuil, R.J. [Centro de Investigacion en Biotecnologia Aplicada del Instituto Politecnico Nacional, Ex-Hacienda de San Juan Molino, Km. 1.5, Tepetitla, Tlaxcala, 90700 (Mexico); Dorantes-Garcia, V. [Preparatoria ' Simon Bolivar' de la Benemerita Universidad Autonoma de Puebla, 4 Oriente 408, Col. Centro, Atlixco, Puebla, C. P. 74200 (Mexico); Perez-Benitez, A. [Facultad de Ciencias Quimicas de la Benemerita Universidad Autonoma Puebla, 14 Sur y Av. San Claudio, Col. San Manuel, Puebla, Puebla, C. P. 72570 (Mexico); Balderas-Lopez, J.A. [Unidad Profesional Interdisciplinaria de Biotecnologia del Instituto Politecnico Nacional, Avenida Acueducto S/N, Col. Barrio la Laguna, Ticoman, Del. Gustavo A. Madero, Mexico, D.F. 07340 (Mexico); Ariza-Ortega, J.A. [Centro de Investigacion en Biotecnologia Aplicada del Instituto Politecnico Nacional, Ex-Hacienda de San Juan Molino, Km. 1.5, Tepetitla, Tlaxcala, 90700 (Mexico)

    2010-10-25

    WO{sub 3} is grown by hot-filament metal oxide deposition (HFMOD) technique under atmospheric pressure and an oxygen atmosphere. By X-ray diffraction obtains that WO{sub 3} presents mainly monoclinic crystalline phase. The chemical stoichiometry is obtained by X-ray Photoelectron Spectroscopy (XPS). The IR spectrum of the as-grown WO{sub 3} presents broad peaks in the range of 1100 to 3600 cm{sup -1}. A broad band in the 2200 to 3600 cm{sup -1} region and the peaks sited at 1645 and 1432 cm{sup -1} are well resolved, which are originated from moisture and are assigned to {nu}(OH) and {delta}(OH) modes of adsorbed water and the corresponding tungsten oxide vibrations are in infrared region from 400 to 1453 cm{sup -1} and around 3492 cm{sup -1}, which correspond to tungsten-oxygen (W-O) stretching, bending and lattice modes. The Raman spectrum shows intense peaks at 801, 710, 262 and 61 cm{sup -1} that are typical Raman peaks of crystalline WO{sub 3} (m-phase) that correspond to stretching vibrations of the bridging oxygen, which are assigned to W-O stretching ({nu}) and W-O bending ({delta}) modes, respectively. By transmittance measurements obtains that the WO{sub 3} band gap can be varied from 2.92 to 3.13 eV in the investigated annealing temperature range.

  14. In-situ transmission electron microscopy imaging of formation and evolution of LixWO3 during lithiation of WO3 nanowires

    International Nuclear Information System (INIS)

    Qi, Kuo; Li, Xiaomin; Sun, Muhua; Huang, Qianming; Wei, Jiake; Xu, Zhi; Wang, Wenlong; Bai, Xuedong; Wang, Enge

    2016-01-01

    The phase transition from monoclinic WO 3 to cubic Li x WO 3 during lithiation of WO 3 is one of the key features for tungsten oxide as the most used electrochromic material. Conventionally, the lithium intercalation of WO 3 has been studied by building generic layered electrochromic device combining with structural characterization and electrochemistry measurement at macro scale. In-situ transmission electron microscopy (in-situ TEM) has been proposed as a method for revealing the detailed mechanism of structural, physical, and chemical properties. Here, we use in-situ TEM method to investigate the formation and evolution of Li x WO 3 in real-time during the electrochemical lithiation of WO 3 nanowires. The dynamic lithiation process is recorded by TEM imaging, diffraction, and electron energy loss spectroscopy. The WO 3 -Li x WO 3 phase boundary of reaction front has been observed at high resolution. The timeliness of crystallinity of Li x WO 3 and the intercalation channels for Li ions are also identified. Moreover, the co-existence of both polycrystalline Li-poor area and amorphous Li-rich phases of Li x WO 3 was found. Our results provide an insight into the basic lithiation process of WO 3 , which is significantly important for understanding the electrochromic mechanism of tungsten oxide.

  15. Phase modification and surface plasmon resonance of Au/WO{sub 3} system

    Energy Technology Data Exchange (ETDEWEB)

    Bose, R. Jolly; Kavitha, V.S. [Department of Optoelectronics, University of Kerala, Kariyavattom, Thiruvananthapuram 691574, Kerala (India); Sudarsanakumar, C. [School of Pure and Applied Physics, Mahatma Gandhi University, Priyadarshini Hills, Kottayam 686560, Kerala (India); Pillai, V.P. Mahadevan, E-mail: vpmpillai9@gmail.com [Department of Optoelectronics, University of Kerala, Kariyavattom, Thiruvananthapuram 691574, Kerala (India)

    2016-08-30

    Highlights: • We have investigated the role of gold as catalyst and nucleation centers, for the crystallization and phase modification of tungsten oxide, in Au/WO{sub 3} matrix. • The phase change from triclinic WO{sub 3} to monoclinic W{sub 18}O{sub 49} is found to enhance with gold incorporation. • The surface plasmon resonance is observed in gold/tungsten oxide system with the appearance of an absorption band near the wavelength 604 nm. - Abstract: We report the action of gold as catalyst for the modification of phase from triclinic WO{sub 3} to monoclinic W{sub 18}O{sub 49} and nucleation centre for the formation of W{sub 18}O{sub 49} phase, in gold incorporated tungsten oxide films prepared by RF magnetron sputtering technique. A new band is observed near 925 cm{sup −1} in the Raman spectra of gold incorporated tungsten oxide films which is not observed in the pure tungsten oxide film. The intensity of this band enhances with gold content. A localized surface plasmon resonance (LSPR) band is observed near the wavelength 604 nm in gold incorporated tungsten oxide films. The integrated intensities of LSPR band and Raman band (∼925 cm{sup −1}) can be used for sensing the quantity of gold in the Au/WO{sub 3} matrix.

  16. Preparation of tungsten coatings on graphite by electro-deposition via Na{sub 2}WO{sub 4}–WO{sub 3} molten salt system

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Ning-bo [School of Materials Science and Engineering, University of Science and Technology Beijing, 30 Xueyuan Road, Haidian District, Beijing 100083 (China); Zhang, Ying-chun, E-mail: zycustb@163.com [School of Materials Science and Engineering, University of Science and Technology Beijing, 30 Xueyuan Road, Haidian District, Beijing 100083 (China); Jiang, Fan; Lang, Shao-ting [School of Materials Science and Engineering, University of Science and Technology Beijing, 30 Xueyuan Road, Haidian District, Beijing 100083 (China); Xia, Min [School of Materials Science and Engineering, University of Science and Technology Beijing, 30 Xueyuan Road, Haidian District, Beijing 100083 (China); Institute of Powder Metallurgy and Advanced Ceramics, Southwest Jiaotong University, 111, 1st Section, Northern 2nd Ring Road, Chengdu (China)

    2014-11-15

    Highlights: • Tungsten coatings on graphite were firstly obtained by electro-deposition method via Na{sub 2}WO{sub 4}–WO{sub 3} molten salt system. • Uniform and dense tungsten coatings could be easily prepared in each face of the sample, especially the complex components. • The obtained tungsten coatings are with high purity, ultra-low oxygen content (about 0.022 wt%). • Modulate pulse parameters can get tungsten coatings with different thickness and hardness. - Abstract: Tungsten coating on graphite substrate is one of the most promising candidate materials as the ITER plasma facing components. In this paper, tungsten coatings on graphite substrates were fabricated by electro-deposition from Na{sub 2}WO{sub 4}–WO{sub 3} molten salt system at 1173 K in atmosphere. Tungsten coatings with no impurities were successfully deposited on graphite substrates under various pulsed current densities in an hour. By increasing the current density from 60 mA cm{sup −2} to 120 mA cm{sup −2} an increase of the average size of tungsten grains, the thickness and the hardness of tungsten coatings occurs. The average size of tungsten grains can reach 7.13 μm, the thickness of tungsten coating was in the range of 28.8–51 μm, and the hardness of coating was higher than 400 HV. No cracks or voids were observed between tungsten coating and graphite substrate. The oxygen content of tungsten coating is about 0.022 wt%.

  17. Field-emission properties of transparent tungsten oxide nano-urchins

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Do-Hyung [Kyungpook National University, Nano-applied Physics Laboratory, Department of Physics, Daegu (Korea, Republic of)

    2012-09-15

    The field-emission properties of transparent tungsten oxide nano-urchin (NU) films deposited on conducting glass substrates were examined. The novel crystalline tungsten oxide NUs consisted of nanowires added to a spherical shell. The WO{sub 2.72} NUs showed better field-emission properties than the WO{sub 3} NUs with a low turn-on field of approximately 5.8 V/{mu}m and a current density as high as 1.3 mA/cm{sup 2} at 7.2 V/mm. The WO{sub x} NUs films could be used in FE applications using a large-area glass substrate without the need for a catalyst and a mechanical rubbing or lift-up process. These results have implications for the enhancement of FE properties by further tuning the WO{sub x} phases. (orig.)

  18. Enhanced Water Oxidation Photoactivity of Nano-Architectured α-Fe2O3-WO3 Composite Synthesized by Single-Step Hydrothermal Method

    Science.gov (United States)

    Rahman, Gul; Joo, Oh-Shim; Chae, Sang Youn; Shah, Anwar-ul-Haq Ali; Mian, Shabeer Ahmad

    2018-04-01

    This study reports the one-step in situ synthesis of a hematite-tungsten oxide (α-Fe2O3-WO3) composite on fluorine-doped tin oxide substrate via a simple hydrothermal method. Scanning electron microscopy images indicated that the addition of tungsten (W) precursor into the reaction mixture altered the surface morphology from nanorods to nanospindles. Energy-dispersive x-ray spectroscopy analysis confirmed the presence of W content in the composite. From the ultraviolet-visible spectrum of α-Fe2O3-WO3, it was observed that absorption began at ˜ 600 nm which corresponded to the bandgap energy of ˜ 2.01 eV. The α-Fe2O3-WO3 electrode demonstrated superior performance, with water oxidation photocurrent density of 0.80 mA/cm2 (at 1.6 V vs. reversible hydrogen electrode under standard illumination conditions; AM 1.5G, 100 mW/cm2) which is 2.4 times higher than α-Fe2O3 (0.34 mA/cm2). This enhanced water oxidation performance can be attributed to the better charge separation properties in addition to the large interfacial area of small-sized particles present in the α-Fe2O3-WO3 nanocomposite film.

  19. Effect of direct current density on microstructure of tungsten coating electroplated from Na{sub 2}WO{sub 4}-WO{sub 3}-NaPO{sub 3} system

    Energy Technology Data Exchange (ETDEWEB)

    Jiang, Fan, E-mail: jiangfan1109@163.com; Zhang, Yingchun, E-mail: zycustb@163.com; Sun, Ningbo, E-mail: suningbo682@163.com; Liu, Zhi’ang, E-mail: zhiang_001@163.com

    2014-10-30

    Highlights: • Tungsten coatings were electroplated from the Na{sub 2}WO{sub 4}-WO{sub 3}-NaPO{sub 3} melt. • Tungsten coating comprised a tooth-like layer and a columnar growth layer. • The average grain size increases as increasing current density. • (2 1 1) Orientation is favored most likely for samples obtained at various durations. • The growth rate of tungsten crystal nucleus is higher than the nucleation rate. - Abstract: Pure tungsten coating with body-centered cubic (bbc) structure was successfully electrodeposited from Na{sub 2}WO{sub 4}-WO{sub 3}-NaPO{sub 3} molten salt at 1153 K in atmosphere. The coatings comprised an inner layer of tooth-like grains and an outer layer of columnar grains with a thin diffusion layer of tungsten in the Cu substrate. The effects of current density and electrodeposition duration on the morphology and microstructure of the coatings were investigated in this paper. With increasing of current density from 50 to 80 mA cm{sup −2}, the grain size of the tungsten coating increased from 7.01 μm to 12.44 μm. With the increase of the current density, the thickness of the coating changed from 25.92 μm to 34.40 μm, and then dropped to 29.72 μm. The preferred orientation of the coatings changed from (2 2 0) to (2 1 1). With the increasing of duration, the grain size and thickness of tungsten coatings increased while the (2 1 1) favored orientation dot not changed. Because of the low current efficiency at long duration of direct current electrodeposition, it should not be suitable for the electroplating of thick tungsten coating.

  20. Synergistic tungsten oxide/organic framework hybrid nanofibers for electrochromic device application

    Science.gov (United States)

    Dulgerbaki, Cigdem; Komur, Ali Ihsan; Nohut Maslakci, Neslihan; Kuralay, Filiz; Uygun Oksuz, Aysegul

    2017-08-01

    We report the first successful applications of tungsten oxide/conducting polymer hybrid nanofiber assemblies in electrochromic devices. Poly(3,4-ethylenedioxythiophene)/tungsten oxide (PEDOT/WO3) and polypyrrole/tungsten oxide (PPy/WO3) composites were prepared by an in situ chemical oxidative polymerization of monomers in different ionic liquids; 1-butyl-3-methylimidazolium tetrafluoroborate (BMIMBF4), 1-butyl-3-methylimidazolium hexafluorophosphate (BMIMPF6), 1-butyl-3-methylimidazolium bis(trifluoromethylsulfonyl) imide (BMIMTFSI) and 1-butyl-1-methylpyrrolidinium bis(trifluoromethylsulfonyl) imide (BMPTFSI). Electrospinning process was used to form hybrid nanofibers from chemically synthesized nanostructures. The electrospun hybrid samples were compared from both morphological and electrochemical perspectives. Importantly, deposition of nanofibers from chemically synthesized hybrids can be achieved homogenously, on nanoscale dimensions. The morphologies of these assemblies were evaluated by SEM, whereas their electroactivity was characterized by cyclic voltammetry. Electrochromic devices made from hybrid nanofiber electrodes exhibited highest chromatic contrast of 37.66% for PEDOT/WO3/BMIMPF6, 40.42% for PPy/WO3/BMIMBF4 and show a strong electrochromic color change from transparent to light brown. Furthermore, the nanofiber devices exhibit outstanding stability when color switching proceeds, which may ensure a versatile platform for color displays, rear-view mirrors and smart windows.

  1. Synthesis, characterization and photocatalytic activity of porous WO3/TiO2 hollow microspheres

    International Nuclear Information System (INIS)

    Yang, Liuyang; Si, Zhichun; Weng, Duan; Yao, Youwei

    2014-01-01

    Porous WO 3 /TiO 2 hollow microspheres were prepared by a spray drying method for photodegradation of methylene blue and phenol. The catalysts were characterized by X-ray diffraction, Field Emission Scanning Electron Microscope, High Resolution Transmission Electron Microscope, N 2 adsorption–desorption measurements, Raman spectrometer, UV–Vis Diffuse Reflectance Spectroscopy and Zeta-Meter measurements. The results showed that the tungsten oxides mainly existed in highly dispersed amorphous form on anatase when the loading amount of tungsten oxide was below 3 mol%. The improved photocatalytic activity under UV light irradiation of the WO 3 /TiO 2 catalyst mainly arises from the enhanced charge separation efficiency rather than the improved light absorbance by highly dispersed amorphous tungsten oxides. Highly dispersed amorphous WO x can form a shallowly trapped site due to its similar band structure with TiO 2 . The strongly electron-withdrawing of tungsten oxide in highly dispersed state facilitates the electron transition between titanium and WO x , and consequently improves the charge separation. The enhanced acidity of catalyst by WO x in reactant environment also improved the charge separation efficiency due to the timely transition of holes and electrons accumulated on TiO 2 and WO x , respectively. However, the improved photocatalytic activity under visible light irradiation of the WO 3 /TiO 2 catalyst mainly arises from light harvest. TiO 2 containing 3 mol% WO 3 displayed the highest photocatalytic activity under UV light irradiation while that containing 4 mol% WO 3 present highest activity under visible light irradiation

  2. Graphenated polyaniline-doped tungsten oxide nanocomposite sensor for real time determination of phenanthrene

    International Nuclear Information System (INIS)

    Tovide, Oluwakemi; Jaheed, Nazeem; Mohamed, Nurali; Nxusani, Ezo; Sunday, Christopher E.; Tsegaye, Abebaw; Ajayi, Rachel F.; Njomo, Njagi; Makelane, Hlamulo; Bilibana, Mawethu; Baker, Priscilla G.; Williams, Avril; Vilakazi, Sibulelo; Tshikhudo, Robert; Iwuoha, Emmanuel I.

    2014-01-01

    A graphenated polyaniline/tungsten oxide (PANI/WO 3 /GR) nanocomposite sensor was prepared by electropolymerisation of a mixture of aniline monomer and tungsten oxide on a graphene-modified glassy carbon electrode (GCE). The PANI/WO 3 /GR/GCE nanocomposite electrode was tested as a sensor for the determination of phenanthrene. The direct electro-oxidation behaviour of phenanthrene on the PANI/WO 3 /GR modified GCE was carefully investigated by cyclic voltammetry. The results indicated that the PANI/WO 3 /GR/GCE sensor was more sensitive to phenanthrene (with a dynamic linear range of 1.0 - 6.0 pM and a detection limit of 0.123 pM.) than GCE, PANI/GCE or PANI/WO 3 /GCE. The sensor exhibited excellent reproducibility and long-term stability. The sensor exhibits lower detection sensitivity than the WHO permissible level of 1.12 nM phenanthrene in wastewater

  3. Effect of pulse current parameters on microstructure of tungsten coating electroplated from Na{sub 2}WO{sub 4}–WO{sub 3}–NaPO{sub 3}

    Energy Technology Data Exchange (ETDEWEB)

    Jiang, Fan; Zhang, Yingchun, E-mail: zycustb@163.com; Sun, Ningbo; Len, Jiaxun

    2015-03-15

    Highlights: • Tungsten coatings were electroplated on cooper alloy by pulse plating. • Increasing current density resulted in an increase in grain size of tungsten coating. • With the increase in duty cycle, the grain size of tungsten coating increased. • The pulse period had an insignificant effect on the tungsten grain size. - Abstract: The tungsten coatings with low oxygen content were prepared on copper alloy substrate by pulse electroplating in Na{sub 2}WO{sub 4}–WO{sub 3}–NaPO{sub 3} molten salt. A series of tungsten coatings with compact morphologies were successfully obtained under various conditions. The influences of current density, duty cycle and period on tungsten grain size and coatings thickness were investigated. The results demonstrated that current density was the most important factor influencing tungsten grain size, which had a positive correlation with current density. The thickness of coating decreased when the current density was up to 80 mA cm{sup −2}. However, the tungsten grain size, tungsten coating thickness and current efficiency changed a little with the increase in pulse periods.

  4. Oxalic acid induced hydrothermal synthesis of single crystalline tungsten oxide nanorods

    International Nuclear Information System (INIS)

    Patil, V.B.; Adhyapak, P.V.; Suryavanshi, S.S.; Mulla, I.S.

    2014-01-01

    Highlights: • We report synthesis of 1D tungsten oxide using a hydrothermal route at 170 °C. • Oxalic acid plays an important role in the formation of 1D nanostructure. • Monoclinic transforms to hexagonal phase with increment in reaction duration. -- Abstract: One-dimensional single-crystalline tungsten oxide nanorods have been synthesized by the hydrothermal technique. The controlled morphology of tungsten oxide was obtained by using sodium tungstate and oxalic acid as an organic inducer. The reaction was carried out at 170 °C for 24, 48 and 72 h. The obtained tungsten oxides were investigated by using XRD, SEM and HRTEM techniques. In order to understand the role of organic inducer on the shape, size and phase formation of WO 3 was prepared with and without organic inducer. On heating of sodium tungstate without organic inducer for 72 h at 170 °C in the hydrothermal unit we obtain nanoparticles of monoclinic WO 3 , however, on addition of oxalic acid a single phase hexagonal WO 3 with distinct nanorods was formed. On addition of oxalic acid a systematic emergence of nanorod-like morphology was obtained with incrementing reaction times from 24 h to 48 h. The 72 h reaction generates self-assembled 20–30 nm diameter and 4–5 μm long h-WO 3 bundles of nanorods. The XRD studies show hexagonal structure of tungsten oxide, while SAED reveals its single crystalline nature. The photoluminescence (PL) emission spectrum shows a characteristic blue emission peak at 3 eV (410 nm). Raman spectra provide the evidence of hexagonal structure with stretching vibrations (830 cm −1 ) for 72 h of heating at 170 °C

  5. Oxalic acid induced hydrothermal synthesis of single crystalline tungsten oxide nanorods

    Energy Technology Data Exchange (ETDEWEB)

    Patil, V.B. [School of Physical Sciences, Solapur University, Solapur 413255 (India); Adhyapak, P.V. [Centre for Materials for Electronic Technology (C-MET), Pune 411008 (India); Suryavanshi, S.S., E-mail: sssuryavanshi@rediffmail.com [School of Physical Sciences, Solapur University, Solapur 413255 (India); Mulla, I.S., E-mail: ismulla2001@gmail.com [Emeritus Scientist (CSIR), Centre for Materials for Electronic Technology (C-MET), Pune 411008 (India)

    2014-03-25

    Highlights: • We report synthesis of 1D tungsten oxide using a hydrothermal route at 170 °C. • Oxalic acid plays an important role in the formation of 1D nanostructure. • Monoclinic transforms to hexagonal phase with increment in reaction duration. -- Abstract: One-dimensional single-crystalline tungsten oxide nanorods have been synthesized by the hydrothermal technique. The controlled morphology of tungsten oxide was obtained by using sodium tungstate and oxalic acid as an organic inducer. The reaction was carried out at 170 °C for 24, 48 and 72 h. The obtained tungsten oxides were investigated by using XRD, SEM and HRTEM techniques. In order to understand the role of organic inducer on the shape, size and phase formation of WO{sub 3} was prepared with and without organic inducer. On heating of sodium tungstate without organic inducer for 72 h at 170 °C in the hydrothermal unit we obtain nanoparticles of monoclinic WO{sub 3}, however, on addition of oxalic acid a single phase hexagonal WO{sub 3} with distinct nanorods was formed. On addition of oxalic acid a systematic emergence of nanorod-like morphology was obtained with incrementing reaction times from 24 h to 48 h. The 72 h reaction generates self-assembled 20–30 nm diameter and 4–5 μm long h-WO{sub 3} bundles of nanorods. The XRD studies show hexagonal structure of tungsten oxide, while SAED reveals its single crystalline nature. The photoluminescence (PL) emission spectrum shows a characteristic blue emission peak at 3 eV (410 nm). Raman spectra provide the evidence of hexagonal structure with stretching vibrations (830 cm{sup −1}) for 72 h of heating at 170 °C.

  6. Synthesis and optical properties of Au decorated colloidal tungsten oxide nanoparticles

    International Nuclear Information System (INIS)

    Tahmasebi, Nemat; Mahdavi, Seyed Mohammad

    2015-01-01

    Highlights: • Tungsten oxide nanoparticles were prepared by pulsed laser ablation (PLA). • A very fine metallic Au particles or coating are decorated on the surface of tungsten oxide nanoparticles. • UV–Vis spectroscopy shows an absorption peak at ∼530 nm which is due to SPR effect of gold. • After exposing to hydrogen gas, Au/WO_3 colloidal nanoparticles show excellent gasochromic coloring. - Abstract: In this study, colloidal tungsten oxide nanoparticles were fabricated by pulsed laser ablation of tungsten target using the first harmonic of a Nd:YAG laser (1064 nm) in deionized water. After ablation, a 0.33 g/lit HAuCl_4 aqueous solution was added into as-prepared colloidal nanoparticles. In this process, Au"3"+ ions were reduced to decorate gold metallic state (Au"0) onto colloidal tungsten oxide nanoparticles surface. The morphology and chemical composition of the synthesized nanoparticles were studied by AFM, XRD, TEM and XPS techniques. UV–Vis analysis reveals a distinct absorption peak at ∼530 nm. This peak can be attributed to the surface plasmon resonance (SPR) of Au and confirms formation of gold state. Moreover, X-ray photoelectron spectroscopy reveals that Au ions’ reduction happens after adding HAuCl_4 solution into as-prepared colloidal tungsten oxide nanoparticles. Transmission electron microscope shows that an Au shell has been decorated onto colloidal WO_3 nanoparticles. Noble metal decorated tungsten oxide nanostructure could be an excellent candidate for photocatalysis, gas sensing and gasochromic applications. Finally, the gasochromic behavior of the synthesized samples was investigated by H_2 and O_2 gases bubbling into the produced colloidal Au/WO_3 nanoparticles. Synthesized colloidal nanoparticles show excellent coloration contrast (∼80%) through NIR spectra.

  7. Ion sensing properties of vanadium/tungsten mixed oxides

    International Nuclear Information System (INIS)

    Guidelli, Eder Jose; Guerra, Elidia Maria; Mulato, Marcelo

    2011-01-01

    Vanadium/tungsten mixed oxide (V 2 O 5 /WO 3 ) sensing membranes were deposited on glassy carbon substrates and used as the H + sensor of the extended gate field effect transistor (EGFET) device. X-ray diffractograms indicated a decrease of the interplanar spacing of V 2 O 5 after the insertion of WO 3 revealing that the lamellar structure is under compressive stress. The crystallinity increases with increasing WO 3 molar ratio. The film is not homogeneous, with more WO 3 material sitting at the surface. This influences the response of pH sensors using the EGFET configuration. The maximum sensitivity of 68 mV pH -1 was obtained for the sample with 5% WO 3 molar ratio. For higher WO 3 molar ratios, the behavior is not linear. It can be concluded that V 2 O 5 dominates for acidic solutions while WO 3 dominates for basic solutions. Therefore, the mixed oxide with low amount of WO 3 is the main candidate for further use as biosensor.

  8. Microstructure, optical, and electrochromic properties of sol-gel nanoporous tungsten oxide films

    Science.gov (United States)

    Djaoued, Yahia; Ashrit, P. V.; Badilescu, S.; Bruning, R.

    2003-08-01

    Porous tungsten oxide films have been prepared by a nonhydrolitic sol-gel method using poly(ethylene glycol) (PEG) as a structure directing agent. The method entails the hydrolysis of an ethanolic solution of tungsten ethoxide (formed by the reaction of WCl6 with ethanol) followed by condensation and polymerization at the PEG-tungsten oxide oligometers interface. A highly porous WO3 framework was obtained after PEG was burned off by calcination at a relativley low temperature. AFM images of the films treated thermally show an ordered material rather than microscopic particulates. Both fibrilar nanostructures and striped phase can be obtained via this approach, depending on the concentration of PEG in the coating solution. XRD data from the fibrils indicate that they are crystalline with very small crystals, whereas the striped phases obtained with 20% PEG correspond to two crystalline phases, one, the stoichiometric WO3 and the other one an oxygen deficient phase, containing larger crystals (~28 nm). The results show that PEG promotes the formation of oxygen deficient phases and delays crystallization. Compared to WO3 with no PEG, the optical and electrochromic properties of the macroporous tungsten oxide films appear to be significantly improved. The formation of organized nanostructures is tentatively accounted for by the strong hydrogen bonding interactions between PEG and the tungsten oxide oligomers.

  9. Reduced graphene oxide/δ-WO{sub 3} composites for volatile organic compounds sensing

    Energy Technology Data Exchange (ETDEWEB)

    Perfecto, Tarcisio Micheli; Zito, Cecilia de Almeida; Volanti, Diogo Paschoalini, E-mail: tarcisio93@hotmail.com [Universidade Estadual Paulista Julio de Mesquita Filho (UNESP), Sao Paulo, SP (Brazil)

    2016-07-01

    Full text: Metal oxide semiconductors (MOS) is a simple and low-cost alternative to detect volatile organic compounds (VOCs) with fast response and recovery time [1]. In this context, reduced graphene oxide (RGO) is used in order to achieve a superior metal oxides gas sensing performance [2]. Thus, we report the synthesis of RGO/δ-WO{sub 3} composites by microwave-assisted hydrothermal method and its application in VOCs detection. The composites were prepared in a single-step using a graphene oxide dispersion, tungsten salt, ammonium oxalate hydrate as morphological control agent, and HCl in aqueous medium. The mixture was sealed in an autoclave and irradiated by microwave (800W) at 140 °C for 10 minutes. Then the sample was heating treatment at 400 °C for 1 hour. δ-WO{sub 3} single phase was also prepared by the same process without graphene oxide. The XRD results indicated the successful formation of triclinic phase of WO{sub 3} for both samples. FEG-SEM images showed the δ-WO{sub 3} nanoplates formation that are agglomerated and become more disperse and with irregular shape in RGO/δ-WO{sub 3} composite. TEM analysis revealed the interaction between RGO and δ-WO{sub 3} particles. The preliminary gas sensing results showed that increasing the operation temperature, more sensitive the composite RGO/δ-WO{sub 3} was toward the ethanol, methanol, acetone, toluene and benzene. So far, the highest response observed was to acetone at 300 °C. The response of RGO/δ-WO{sub 3} to 5, 10, 50, 100 and 200 ppm of acetone was 1.08, 1.12, 1.42, 1.75, and 1.99, respectively. We expect that increasing the operating temperature, more sensitive the material will become, since reports shows that WO{sub 3} sensors exhibit higher responses at higher temperatures [3]. Acknowledgments: The authors acknowledge FAPESP grants: 16/04371-1, 15/04306-2 and 14/17343-0. Refs.: [1] Jiang, D.;et al. RSC Adv. 2015, 5 (49), 39442-39448. [2] Jie, X.; et al. Sensors Actuators B Chem. 2015, 220

  10. Synthesis, characterization and photocatalytic activity of porous WO{sub 3}/TiO{sub 2} hollow microspheres

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Liuyang [Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055 (China); Si, Zhichun, E-mail: emsztsinghua@126.com [Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055 (China); Weng, Duan [Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055 (China); State Key Laboratory of New Ceramics and Fine Process, School of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Yao, Youwei [Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055 (China)

    2014-09-15

    Porous WO{sub 3}/TiO{sub 2} hollow microspheres were prepared by a spray drying method for photodegradation of methylene blue and phenol. The catalysts were characterized by X-ray diffraction, Field Emission Scanning Electron Microscope, High Resolution Transmission Electron Microscope, N{sub 2} adsorption–desorption measurements, Raman spectrometer, UV–Vis Diffuse Reflectance Spectroscopy and Zeta-Meter measurements. The results showed that the tungsten oxides mainly existed in highly dispersed amorphous form on anatase when the loading amount of tungsten oxide was below 3 mol%. The improved photocatalytic activity under UV light irradiation of the WO{sub 3}/TiO{sub 2} catalyst mainly arises from the enhanced charge separation efficiency rather than the improved light absorbance by highly dispersed amorphous tungsten oxides. Highly dispersed amorphous WO{sub x} can form a shallowly trapped site due to its similar band structure with TiO{sub 2}. The strongly electron-withdrawing of tungsten oxide in highly dispersed state facilitates the electron transition between titanium and WO{sub x}, and consequently improves the charge separation. The enhanced acidity of catalyst by WO{sub x} in reactant environment also improved the charge separation efficiency due to the timely transition of holes and electrons accumulated on TiO{sub 2} and WO{sub x}, respectively. However, the improved photocatalytic activity under visible light irradiation of the WO{sub 3}/TiO{sub 2} catalyst mainly arises from light harvest. TiO{sub 2} containing 3 mol% WO{sub 3} displayed the highest photocatalytic activity under UV light irradiation while that containing 4 mol% WO{sub 3} present highest activity under visible light irradiation.

  11. Review of WO3 thin film preparation for photoelectrochemical water splitting

    International Nuclear Information System (INIS)

    Ehsan Eftekhari; Mohammad Kassim

    2009-01-01

    Full text: Tungsten trioxide (WO 3 ), which is one of the most essential materials in our daily life has appeared as an excellent photo electrode material for environmental purification. The nano-size of WO 3 thin film water-splitting technology has great potential for environmentally friendly solar-hydrogen production for the future hydrogen economy. There are several methods for producing tungsten oxide film. In this review, we outlined several WO 3 thin film preparation methods such as doctor Bladding, sputtering, layer-by-layer brush painting, spray pyrolysis deposition, sol-gel and other methods. Here we compare the maximum photocurrent obtained, different condition for preparation of WO 3 thin film and characterization outcome. (author)

  12. Effects of process parameters on tungsten boride production from WO{sub 3} by self propagating high temperature synthesis

    Energy Technology Data Exchange (ETDEWEB)

    Yazici, Sertac [Metallurgical and Materials Engineering Department, Istanbul Technical University, Maslak, Istanbul 34469 (Turkey); Derin, Bora, E-mail: bderin@itu.edu.tr [Metallurgical and Materials Engineering Department, Istanbul Technical University, Maslak, Istanbul 34469 (Turkey)

    2013-01-01

    Highlights: Black-Right-Pointing-Pointer We produced tungsten boride compounds by SHS method. Black-Right-Pointing-Pointer Mg containing byproducts were leached out by using a hot aqueous HCl media. Black-Right-Pointing-Pointer The ratio of W{sub 2}B{sub 5}/WB was found to be {approx}2.0 containing minor phases of W{sub 2}B and W. - Abstract: In the present study, the production parameters of tungsten boride compounds by self-propagating high-temperature synthesis (SHS) method and following leaching process were investigated. In the SHS stage, the products consisting of tungsten borides, magnesium oxide, magnesium borate, and also minor compounds were obtained by using different initial molar ratios of WO{sub 3}, Mg and B{sub 2}O{sub 3} as starting materials. In the leaching step, Mg containing byproducts, i.e. MgO and Mg{sub 3}B{sub 2}O{sub 6}, existed in the selected SHS product synthesized at 1:8:2.5 initial molar ratio of WO{sub 3}:Mg:B{sub 2}O{sub 3} were leached out by using aqueous HCl solution to obtain clean tungsten boride compounds at different experimental parameters which are time, acid concentration and temperature. The acid leaching experiments of the SHS product showed that optimum leaching conditions could be achieved by using 5.8 M HCl at 1/10 S/L ratio and the temperature of 80 Degree-Sign C for 60 min.

  13. High-pressure synthesis of fully occupied tetragonal and cubic tungsten bronze oxides

    Energy Technology Data Exchange (ETDEWEB)

    Ikeuchi, Yuya; Takatsu, Hiroshi; Tassel, Cedric; Goto, Yoshihiro; Murakami, Taito; Kageyama, Hiroshi [Graduate School of Engineering, Kyoto University (Japan)

    2017-05-15

    A high-pressure reaction yielded the fully occupied tetragonal tungsten bronze K{sub 3}W{sub 5}O{sub 15} (K{sub 0.6}WO{sub 3}). The terminal phase shows an unusual transport property featuring slightly negative temperature-dependence in resistivity (dρ/dT<0) and a large Wilson ratio of R{sub W}=3.2. Such anomalous metallic behavior possibly arises from the low-dimensional electronic structure with a van Hove singularity at the Fermi level and/or from enhanced magnetic fluctuations by geometrical frustration of the tungsten sublattice. The asymmetric nature of the tetragonal tungsten bronze K{sub x}WO{sub 3}-K{sub 0.6-y}Ba{sub y}WO{sub 3} phase diagram implies that superconductivity for x≤0.45 originates from the lattice instability because of potassium deficiency. A cubic perovskite KWO{sub 3} phase was also identified as a line phase - in marked contrast to Na{sub x}WO{sub 3} and Li{sub x}WO{sub 3} with varying quantities of x (<1). This study presents a versatile method by which the solubility limit of tungsten bronze oxides can be extended. (copyright 2017 Wiley-VCH Verlag GmbH and Co. KGaA, Weinheim)

  14. Thermal oxidation of seeds for the hydrothermal growth of WO3 nanorods on ITO glass substrate

    International Nuclear Information System (INIS)

    Ng, Chai Yan; Abdul Razak, Khairunisak; Lockman, Zainovia

    2015-01-01

    This work reports a simple seed formation method for the hydrothermal growth of tungsten oxide (WO 3 ) nanorods. A WO 3 seed layer was prepared by thermal oxidation, where a W-sputtered substrate was heated and oxidized in a furnace. Oxidation temperatures and periods were varied at 400–550 °C and 5–60 min, respectively, to determine an appropriate seed layer for nanorod growth. Thermal oxidation at 500 °C for 15 min was found to produce a seed layer with sufficient crystallinity and good adhesion to the substrate. These properties prevented the seed from peeling off during the hydrothermal process, thereby allowing nanorod growth on the seed. The nanorod film showed better electrochromic behavior (higher current density of − 1.11 and + 0.65 mA cm −2 ) than compact film (lower current density of − 0.54 and + 0.28 mA cm −2 ). - Highlights: • A simple seed formation method (thermal oxidation) on sputtered W film is reported. • Crystalline seed with good adhesion to substrate is required for nanorod growth. • The appropriate temperature and period for seed formation were 500 °C and 15 min. • WO 3 nanorods exhibited higher electrochromic current density than WO 3 compact film.

  15. Synthesis and characterization of large WO{sub 3} sheets synthesized by resistive heating method

    Energy Technology Data Exchange (ETDEWEB)

    Filippo, Emanuela, E-mail: emanuela.filippo@unisalento.it [Department of Engineering for Innovation, University of Salento, Monteroni Street, Lecce I-73100 Italy (Italy); Tepore, Marco [Department of Engineering for Innovation, University of Salento, Monteroni Street, Lecce I-73100 Italy (Italy); Baldassarre, Francesca [Department of Cultural Heritage, University of Salento, Lecce I-73100 Italy (Italy); Quarta, Gianluca; Calcagnile, Lucio [Department of Engineering for Innovation, University of Salento, Monteroni Street, Lecce I-73100 Italy (Italy); Guascito, Maria Rachele [DiSTeBA, University of Salento, Lecce I-73100 Italy (Italy); Tepore, Antonio [Department of Cultural Heritage, University of Salento, Lecce I-73100 Italy (Italy)

    2015-09-01

    A simple, low-cost method is presented to grow tungsten oxide large sheets simply by resistively heating a pure tungsten filament under air/water vapor flow. The obtained structures were studied using scanning and transmission electron microscopy, selected area diffraction, X Ray diffraction, Raman and X-ray photoelectron spectroscopy, photoluminescence and zeta potential measurements. SEM observations revealed that sheets formed by broadening of the wires/belts over longer growth period. Photoluminescence measurements showed that tungsten oxide sheets had an intense visible emission band. - Highlights: • WO{sub 3} large sheets were prepared by resistively heating a W filament. • WO{sub 3} sheets were carefully characterized. • Formation mechanism of sheets was studied. • WO{sub 3} sheets had an intense visible emission band at 462 nm.

  16. Tungsten oxide nanowires grown on amorphous-like tungsten films

    International Nuclear Information System (INIS)

    Dellasega, D; Pezzoli, A; Russo, V; Passoni, M; Pietralunga, S M; Nasi, L; Conti, C; Vahid, M J; Tagliaferri, A

    2015-01-01

    Tungsten oxide nanowires have been synthesized by vacuum annealing in the range 500–710 °C from amorphous-like tungsten films, deposited on a Si(100) substrate by pulsed laser deposition (PLD) in the presence of a He background pressure. The oxygen required for the nanowires formation is already adsorbed in the W matrix before annealing, its amount depending on deposition parameters. Nanowire crystalline phase and stoichiometry depend on annealing temperature, ranging from W_1_8O_4_9-Magneli phase to monoclinic WO_3. Sufficiently long annealing induces the formation of micrometer-long nanowires, up to 3.6 μm with an aspect ratio up to 90. Oxide nanowire growth appears to be triggered by the crystallization of the underlying amorphous W film, promoting their synthesis at low temperatures. (paper)

  17. Visible light assisted nitrogen dioxide sensing using tungsten oxide - Graphene oxide nanocomposite sensors

    Energy Technology Data Exchange (ETDEWEB)

    Geng, Xin [College of Mechanical Engineering, Yangzhou University, Yangzhou 225127 (China); College of Chemistry and Chemical Engineering, Yangzhou University, Yangzhou 225002 (China); You, Jiajun; Wang, Jie [College of Mechanical Engineering, Yangzhou University, Yangzhou 225127 (China); Zhang, Chao, E-mail: zhangc@yzu.edu.cn [College of Mechanical Engineering, Yangzhou University, Yangzhou 225127 (China)

    2017-04-15

    Tungsten oxide (WO{sub 3}) coatings were deposited by solution precursor plasma spray (SPPS) on alumina substrates. In order to enhance the NO{sub 2} sensing properties of the pure WO{sub 3} coatings at room temperature, illuminating with visible light and formation of p-n heterojunction were used. The SPPS WO{sub 3} coatings were modified by immersing them into a synthesized graphene oxide (GO) suspension to obtain the WO{sub 3}-GO composites. Raman and FTIR results demonstrated that p-n heterojunctions were successfully formed in the WO{sub 3}-GO composites. The UV–Vis spectra showed that the WO{sub 3}-GO composites had a longer visible light absorption range compared with the WO{sub 3} coatings. The sensors based on the WO{sub 3}-GO coatings exhibited ultra-high responses to NO{sub 2} at room temperature performed under visible light illumination. - Highlights: • Highly porous nanostructured WO{sub 3} coatings were deposited by SPPS process. • The WO{sub 3}-GO nanocomposites with p-n heterojunctions were successfully prepared. • The WO{sub 3}-GO nanocomposites exhibited ultra-high responses to 0.9 ppm NO{sub 2}. • The enhanced performance was ascribed to the fine structure and heterojunction.

  18. Thin film deposition and characterization of pure and iron-doped electron-beam evaporated tungsten oxide for gas sensors

    Energy Technology Data Exchange (ETDEWEB)

    Tesfamichael, Tuquabo, E-mail: t.tesfamichael@qut.edu.a [Faculty of Built Environment and Engineering, School of Engineering Systems, Queensland University of Technology, 2 George Street, Brisbane, QLD 4000 (Australia); Arita, Masashi [Graduate School of Information Science and Technology, Hokkaido University, Kita-14, Nishi-9, Kita-ku, Sapporo, 060-0814 (Japan); Bostrom, Thor [Faculty of Science and Technology, School of Physical and Chemical Sciences, Queensland University of Technology, 2 George Street, Brisbane, QLD 4000 (Australia); Bell, John [Centre for Built Environment and Engineering Research, Queensland University of Technology, 2 George Street, Brisbane, QLD 4000 (Australia)

    2010-06-30

    Pure tungsten oxide (WO{sub 3}) and iron-doped (10 at.%) tungsten oxide (WO{sub 3}:Fe) nanostructured thin films were prepared using a dual crucible Electron Beam Evaporation (EBE) technique. The films were deposited at room temperature under high vacuum onto glass as well as alumina substrates and post-heat treated at 300 {sup o}C for 1 h. Using Raman spectroscopy the as-deposited WO{sub 3} and WO{sub 3}:Fe films were found to be amorphous, however their crystallinity increased after annealing. The estimated surface roughness of the films was similar (of the order of 3 nm) to that determined using Atomic Force Microscopy (AFM). As observed by AFM, the WO{sub 3}:Fe film appeared to have a more compact surface as compared to the more porous WO{sub 3} film. X-ray photoelectron spectroscopy analysis showed that the elemental stoichiometry of the tungsten oxide films was consistent with WO{sub 3}. A slight difference in optical band gap energies was found between the as-deposited WO{sub 3} (3.22 eV) and WO{sub 3}:Fe (3.12 eV) films. The differences in the band gap energies of the annealed films were significantly higher, having values of 3.12 eV and 2.61 eV for the WO{sub 3} and WO{sub 3}:Fe films respectively. The heat treated films were investigated for gas sensing applications using noise spectroscopy. It was found that doping of Fe to WO{sub 3} produced gas selectivity but a reduced gas sensitivity as compared to the WO{sub 3} sensor.

  19. Thermal oxidation of seeds for the hydrothermal growth of WO{sub 3} nanorods on ITO glass substrate

    Energy Technology Data Exchange (ETDEWEB)

    Ng, Chai Yan [School of Materials and Mineral Resources Engineering, Universiti Sains Malaysia, 14300 Nibong Tebal, Penang (Malaysia); Department of Mechanical and Material Engineering, Lee Kong Chian Faculty of Engineering and Science, Universiti Tunku Abdul Rahman, Jalan Sungai Long, Bandar Sungai Long, Cheras, 43000 Kajang, Selangor (Malaysia); Abdul Razak, Khairunisak, E-mail: khairunisak@usm.my [School of Materials and Mineral Resources Engineering, Universiti Sains Malaysia, 14300 Nibong Tebal, Penang (Malaysia); NanoBiotechnology Research and Innovation (NanoBRI), Institute for Research in Molecular Medicine (INFORMM), Universiti Sains Malaysia, 11800 USM, Penang (Malaysia); Lockman, Zainovia, E-mail: zainovia@usm.my [School of Materials and Mineral Resources Engineering, Universiti Sains Malaysia, 14300 Nibong Tebal, Penang (Malaysia)

    2015-11-30

    This work reports a simple seed formation method for the hydrothermal growth of tungsten oxide (WO{sub 3}) nanorods. A WO{sub 3} seed layer was prepared by thermal oxidation, where a W-sputtered substrate was heated and oxidized in a furnace. Oxidation temperatures and periods were varied at 400–550 °C and 5–60 min, respectively, to determine an appropriate seed layer for nanorod growth. Thermal oxidation at 500 °C for 15 min was found to produce a seed layer with sufficient crystallinity and good adhesion to the substrate. These properties prevented the seed from peeling off during the hydrothermal process, thereby allowing nanorod growth on the seed. The nanorod film showed better electrochromic behavior (higher current density of − 1.11 and + 0.65 mA cm{sup −2}) than compact film (lower current density of − 0.54 and + 0.28 mA cm{sup −2}). - Highlights: • A simple seed formation method (thermal oxidation) on sputtered W film is reported. • Crystalline seed with good adhesion to substrate is required for nanorod growth. • The appropriate temperature and period for seed formation were 500 °C and 15 min. • WO{sub 3} nanorods exhibited higher electrochromic current density than WO{sub 3} compact film.

  20. Structure of the short-range atomic order of WO3 amorphous films

    International Nuclear Information System (INIS)

    Olevskij, S.S.; Sergeev, M.S.; Tolstikhina, A.L.; Avilov, A.S.; Shkornyakov, S.M.; Semiletov, S.A.

    1984-01-01

    To study the causes of electrochromism manifestation in thin tungsten oxide films, the structure of WO 3 amorphous films has been investigated. The films were obtained by three different methods: by W(CO) 6 tungsten carbonyl pyrolysis, by high-frequency ion-plasma sputtering of a target prepared by WO 3 powder sintering, and by WO 3 powder thermal evaporation. Monocrystalline wafers of silicon and sodium chloride were used as substrates. The structure of short-range order in WO 3 amorphous films varies versus, the method of preparation in compliance with the type of polyhedral elements, (WO 6 , WO 5 ) and with the character of their packing (contacts via edges or vertices). Manifestation of electroc ro mism in WO 3 films prepared by varions methods and having different structure of short-range order is supposed to be realized through various mechanisms. One cannot exclude a potential simultaneous effect of the two coloration mechanisms

  1. Anti-tumor activity of self-charged (Eu,Ca):WO3 and Eu:CaWO4 nanoparticles

    International Nuclear Information System (INIS)

    Lin, Cao; Cong, Wang; De'An, Pan; Jiexin, Cao; Ping, Che; Volinsky, Alex A.

    2012-01-01

    Non-stoichiometric (Eu,Ca):WO 3 and Eu:CaWO 4 nanoparticles with anti-tumor activity are synthesized in a sol-gel method by adding excessive Eu 3+ and Ca 2+ ions to tungsten oxide crystal structure. Colorimetric assay shows that 10 nm (Eu,Ca):WO 3 and Eu:CaWO 4 nanoparticles can effectively inhibit growth of mammary cancer cells without any harm to normal cells. Nanoparticles are characterized by X-ray diffraction, high resolution transmission electron microscopy and fluorescence optical spectrometry. Nanomaterials, insoluble in synthesized water, have complicated self-charging surfaces that trap mammary cancer cells. Surface self-charging effect is suggested as the inhibition mechanism. (author)

  2. AC conductivity and dielectric properties of bulk tungsten trioxide (WO3)

    Science.gov (United States)

    El-Nahass, M. M.; Ali, H. A. M.; Saadeldin, M.; Zaghllol, M.

    2012-11-01

    AC conductivity and dielectric properties of tungsten trioxide (WO3) in a pellet form were studied in the frequency range from 42 Hz to 5 MHz with a variation of temperature in the range from 303 K to 463 K. AC conductivity, σac(ω) was found to be a function of ωs where ω is the angular frequency and s is the frequency exponent. The values of s were found to be less than unity and decrease with increasing temperature, which supports the correlated barrier hopping mechanism (CBH) as the dominant mechanism for the conduction in WO3. The dielectric constant (ε‧) and dielectric loss (ε″) were measured. The Cole-Cole diagram determined complex impedance for different temperatures.

  3. Electro-deposition metallic tungsten coatings in a Na{sub 2}WO{sub 4}-WO{sub 3} melt on copper based alloy substrate

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Y.H., E-mail: dreamerhong77@126.com [School of Materials Science and Engineering, University of Science and Technology Beijing, 30 Xueyuan Road, Haidian District, Beijing 100083 (China); Zhang, Y.C.; Liu, Q.Z.; Li, X.L.; Jiang, F. [School of Materials Science and Engineering, University of Science and Technology Beijing, 30 Xueyuan Road, Haidian District, Beijing 100083 (China)

    2012-11-15

    Highlights: Black-Right-Pointing-Pointer The tungsten coating (>1 mm) was obtained by electro-deposition method in molten salt. Black-Right-Pointing-Pointer Different thickness tungsten coatings were obtained by using different durations. Black-Right-Pointing-Pointer Good performance of coating was obtained when pulse parameters were modulated. - Abstract: The tungsten coating was prepared by electro-deposition technique on copper alloy substrate in a Na{sub 2}WO{sub 4}-WO{sub 3} melt. The coating's surface and cross-section morphologies as well as its impurities were investigated by XPS, SEM and line analysis. Various plating durations were investigated in order to obtain an optimal coating's thickness. The results demonstrated that the electro-deposited coating was compact, voidless, crackless and free from impurities. The tungsten coating's maximum Vickers hardness was measured to be 520 HV. The tungsten coating's minimum oxygen content was determined to be 0.018 wt%. Its maximum thickness was measured to be 1043.67 {mu}m when the duration of electrolysis was set to 100 h. The result of this study has demonstrated the feasibility of having thicker tungsten coatings on copper alloy substrates. These electrodeposited tungsten coatings can be potentially implemented as reliable armour for the medium heat flux plasma facing component (PFC).

  4. Study on the oxidation and reduction of tungsten surface for sub-50 nm patterning process

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jong Kyu; Nam, Seok Woo; Cho, Sung Il; Jhon, Myung S.; Min, Kyung Suk; Kim, Chan Kyu; Jung, Ho Bum; Yeom, Geun Young [Memory Division Semiconductor Business, Samsung Electronics, San No. 16 Banwol-Ri, Taean-Eup, Hwasung-City, Gyeonggi-Do 449-711, South Korea and Department of Advanced Materials Science and Engineering, Sungkyunkwan University, Suwon, Gyeonggi-do 440-746 (Korea, Republic of); Memory Division Semiconductor Business, Samsung Electronics, San No. 16 Banwol-Ri, Taean-Eup, Hwasung-City, Gyeonggi-Do 449-711 (Korea, Republic of); Department of Chemical Engineering and Data Storage Systems Center, Carnegie Mellon University, Pittsburgh, Pennsylvania 15213 (United States); Department of Advanced Materials Science and Engineering, Sungkyunkwan University, Suwon, Gyeonggi-do 440-746 (Korea, Republic of)

    2012-11-15

    The oxidation characteristics of tungsten line pattern during the carbon-based mask-layer removal process using oxygen plasmas have been investigated for sub-50 nm patterning processes, in addition to the reduction characteristics of the WO{sub x} layer formed on the tungsten line surface using hydrogen plasmas. The surface oxidation of tungsten lines during the mask layer removal process could be minimized by using low-temperature (300 K) plasma processing for the removal of the carbon-based material. Using this technique, the thickness of WO{sub x} on the tungsten line could be decreased to 25% compared to results from high-temperature processing. The WO{sub x} layer could also be completely removed at a low temperature of 300 K using a hydrogen plasma by supplying bias power to the tungsten substrate to provide a activation energy for the reduction. When this oxidation and reduction technique was applied to actual 40-nm-CD device processing, the complete removal of WO{sub x} formed on the sidewall of tungsten line could be observed.

  5. Magnetic susceptibility of the rare earth tungsten oxide bronzes of the defected perovskite-type structure (Rsub(x)WO/sub 3/)

    Energy Technology Data Exchange (ETDEWEB)

    Gesicki, A; Polaczek, A [Warsaw Univ. (Poland)

    1975-01-01

    Magnetic susceptibility of rare earth tungsten bronzes Rsub(x)WO/sub 3/ of cubic symmetry was measured in the 80-293 K range with the Gouy method. In disagreement with the data reported by other authors it was stated that the Curie-Weiss law with negative Weiss parameter was fulfilled in each case. Possible coupling mechanisms are briefly discussed.

  6. Pronounced effects of the nominal concentrations of WO3 and Ag: WO3 nano-plates (obtained by a co-precipitation method) on their structural, morphological and optical properties

    Science.gov (United States)

    Rajendran, V.; Deepa, B.

    2018-03-01

    Tungsten oxide and different concentration of silver (Ag)-doped tungsten oxide nano material were synthesized by co-precipitation technique. The functional vibrations, structure, and morphology of as-prepared nano material were studied by Fourier transmission infrared spectroscopy, X-ray diffraction, scanning electron microscopy (SEM) and High-resolution transmission electron microscopy (HR-TEM) techniques. The SEM and HR-TEM analysis revealed the formation of nano-plate/nano rods with an average diameter of 40-80 nm diameter and 1-1.5 mm length. Fluorescence (PL) and UV-visible absorption techniques have been used to study the optical properties of the prepared nanoparticles. The observed red shift in the visible absorption spectra confirmed the promoted electron-phonon interaction in WO3 and Ag: WO3 nanoparticles compared to bulk structures. The photoluminescence of nanocrystalline Ag2+ doped WO3 exhibited a strong violet-blue, blue-green emission. Concentration dependence of the emission intensity of Ag2+ in WO3 was studied, and the significant concentration was found to be 0.5% of Ag: WO3. The effluent dye degradation executed for the 0.5% of Ag: WO3 sample under the visible light which reveals the highest degradation efficiency in appropriate time.

  7. Moessbauer effect study of hyperfine interaction of /sup 161/Dy and /sup 151/Eu in tungsten bronzes Dysub(0. 18) WO/sub 3/ and Eusub(0. 18) WO/sub 3/

    Energy Technology Data Exchange (ETDEWEB)

    Kisynska, K

    1979-01-01

    The Moessbauer technique was used to investigate the hyperfine interaction of /sup 161/Dy and /sup 151/Eu in cubic rare earth tungsten bronzes: Dysub(0.18)WO/sub 3/ and Eusub(0.18)WO/sub 3/. Well resolved hfs spectrum was obtained at 4.2 K for Dysub(0.18)WO/sub 3/. The effective hf field approximation sufficed to interpret the spectrum. The obtained hyperfine interaction parameters were: -g/sub 0/..beta..sub(N)Hsub(eff)=(805+-19) Mc/s and e/sup 2/qQ/sub 0//4 = (506+-56) Mc/s. These results imply that ground doublet of Dy/sup +3/ ion in bronze is a Kramers doublet Vertical Bar+-15/2> with asymmetrical hyperfine tensor Asub(z) non equal to 0, Asub(x) = Asub(y) = 0 and that local crystalline field at RE metal in tungsten bronze at 4.2 K cannot be cubic. From ME absorption spectra of Eusub(0.18)WO/sub 3/ taken at 4.2 K, 78 K and 300 K the values of quadrupole interaction constants for bronze lattice and its temperature dependence were obtained. These data indicate that a phase transition from the high temperature ideal perovskite structure to a distorted one occurs in RE bronzes and that the distortion concerns the nearest tungsten-oxygen environment of RE ion.

  8. Ultrathin percolated WO{sub 3} cluster film and its resistive response to H{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Meng [Research Center for Solid State Physics and Materials, School of Mathematics and Physics, Suzhou University of Science and Technology, Suzhou 215009 (China); Department of Applied Physics and Materials Research Center, The Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong (China); Wong, Man Hon; Huang, Jian Xing [Department of Applied Physics and Materials Research Center, The Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong (China); Ong, Chung Wo, E-mail: c.w.ong@polyu.edu.hk [Department of Applied Physics and Materials Research Center, The Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong (China)

    2014-11-05

    Highlights: • Ultrathin percolated network of WO{sub 3} clusters was fabricated. • The WO{sub 3} clusters are modeled by spherical caps connected by ultrafine linkages. • The ultrathin percolated network of WO{sub 3} clusters shows fast response rate to H{sub 2}. • The fast response is attributed to the rapid electrical switching of the linkages. • Improved H{sub 2} sensing properties may be achieved if narrower linkages are used. - Abstract: Thin films composed of tungsten oxide (WO{sub 3}) nanoclusters were fabricated by oxidizing supersonic cluster beam deposited tungsten films at various temperatures. Oxidation at 700 °C resulted in aggregation of the deposits, forming a percolated network of WO{sub 3} spherical caps connected by fine links. The resistance response of the palladium-(Pd-) coated film sample to hydrogen (H{sub 2}) was investigated. The response rate was faster than those of other samples oxidized at lower temperatures. This is the result of the rapid electrical switching of the intercluster links between the highly resistive depleted state and conducting hydrogenated state. The possibility of improving the H{sub 2} sensing response rate with the use of the percolated WO{sub 3} film structure is illustrated.

  9. Refining waste hardmetals into tungsten oxide nanosheets via facile method

    Energy Technology Data Exchange (ETDEWEB)

    Li, Zhifei; Zheng, Guangwei; Wang, Jinshu, E-mail: wangjsh@bjut.edu.cn; Li, Hongyi, E-mail: lhy06@bjut.edu.cn; Wu, Junshu; Du, Yucheng [Beijing University of Technology, Key Laboratory of Advanced Functional Materials, School of Materials Science and Engineering (China)

    2016-04-15

    A new hydrothermal system has been designed to recycle waste WC–Co hardmetal with low cobalt (Co) content (3 %). In the solution system, nitric acid was designed to dissolve Co, H{sub 2}O{sub 2} served as oxidant to accelerate the oxidation of the WC–Co hardmetals, and fluorine (F{sup −}) was designed to dissolve and recrystallize generated tungsten oxides, which were found to possess a layered structure using scanning electron microscopy and transmission electron microscopy. The obtained tungsten oxides were identified as WO{sub 3}·0.33H{sub 2}O by X-ray diffraction and their specific surface area was measured as 89.2 m{sup 2} g{sup −1} via N{sub 2} adsorption–desorption techniques. The present layered structure tungsten oxides exhibited a promising capability for removing lead ion (Pb{sup 2+}) and organic species, such as methyl blue. The adsorption model was found to be in agreement with Langmuir isotherm model. Given the facile synthesis procedure and promising properties of final products, this new approach should have great potential for refining some other waste hardmetals or tungsten products.Graphical AbstractA new hydrothermal system was designed to recycle waste hardmetal with low cobalt content. Through this method, waste hardmetal was refined into WO{sub 3}·0.33H{sub 2}O nanosheets which shows excellent adsorption capacities toward methylene blue and lead ion (Pb{sup 2+}).

  10. Synthesis, formation mechanism and sensing properties of WO3 hydrate nanowire netted-spheres

    International Nuclear Information System (INIS)

    Yan, Aihua; Xie, Changsheng; Zeng, Dawen; Cai, Shuizhou; Hu, Mulin

    2010-01-01

    Tungsten oxide hydrate nanowire netted-spheres were successfully synthesized in the glycol solution using a facile solvothermal approach. The nanowires with uniform diameter of 4-6 nm are actually a kind of tungsten oxide hydrate/surfactant hybrid materials. The influence of surfactant, solvent, time and temperature on tailoring morphology was investigated in detail. The possible formation process of WO 3 hydrate nanowire netted-sphere was proposed. Sensing properties of such WO 3 hydrate sensor show that the desirable sensing characteristics towards 100 ppm ammonia gas at 320 o C were obtained, such as rapid response (18.3 s), high sensitivity, good reproducibility and stability.

  11. WO{sub 3} nanorods prepared by low-temperature seeded growth hydrothermal reaction

    Energy Technology Data Exchange (ETDEWEB)

    Ng, Chai Yan [School of Materials and Mineral Resources Engineering, Universiti Sains Malaysia, 14300 Nibong Tebal, Penang (Malaysia); Abdul Razak, Khairunisak, E-mail: khairunisak@eng.usm.my [School of Materials and Mineral Resources Engineering, Universiti Sains Malaysia, 14300 Nibong Tebal, Penang (Malaysia); NanoBiotechnology Research and Innovation (NanoBRI), Institute for Research in Molecular Medicine (INFORMM), Universiti Sains Malaysia, 11800 USM, Penang (Malaysia); Lockman, Zainovia, E-mail: zainovia@eng.usm.my [School of Materials and Mineral Resources Engineering, Universiti Sains Malaysia, 14300 Nibong Tebal, Penang (Malaysia)

    2014-03-05

    Highlights: • WO{sub 3} nanorods with 5–10 nm diameter were grown directly on seeded tungsten foil. • WO{sub 3} nanorods were successfully grown at low temperature of 80 °C. • WO{sub 3} nanorods were grown on the entire surface of the seed layer after 24 h. • Annealed nanorods showed better electrochromic properties than as-made nanorods. -- Abstract: This work describes the first tungsten oxide (WO{sub 3}) nanorods hydrothermally grown on W foil. WO{sub 3} nanorods were successfully grown at low hydrothermal temperature of 80 °C by seeded growth hydrothermal reaction. The seed layer was prepared by thermally oxidized the W foil at 400 °C for 0.5 h. This work discusses the effect of hydrothermal reaction and annealing period on the morphological, structural, and electrochromic properties of WO{sub 3} nanorods. Various hydrothermal reaction periods (8–24 h) were studied. Monoclinic WO{sub 3} nanorods with 5–10 nm diameter were obtained after hydrothermal reaction for 24 h. These 24 h WO{sub 3} nanorods were also annealed at 400 °C with varying dwelling periods (0.5–4 h). Electrochromic properties of WO{sub 3} nanorods in an acidic electrolyte were analyzed using cyclic voltammetry and UV–vis spectrophotometry. WO{sub 3} nanorods annealed at 400 °C for 1 h showed the highest charge capacity and the largest optical contrast among the 24 h WO{sub 3} films. The sample also showed good cycling stability without significant degradation. Based on the results, the reaction mechanism of WO{sub 3} nanorod formation on W foil was proposed.

  12. Fungus mediated biosynthesis of WO3 nanoparticles using Fusarium solani extract

    Science.gov (United States)

    Kavitha, N. S.; Venkatesh, K. S.; Palani, N. S.; Ilangovan, R.

    2017-05-01

    Currently nanoparticles were synthesized by emphasis bioremediation process due to less hazardous, eco-friendly and imperative applications on biogenic process. Fungus mediated biosynthesis strategy has been developed to prepare tungsten oxide nanoflakes (WO3, NFs) using the plant pathogenic fungus F.solani. The powder XRD pattern revealed the monoclinic crystal structure with improved crystalline nature of the synthesized WO3 nanoparticles. FESEM images showed the flake-like morphology of WO3, with average thickness and length around 40 nm and 300 nm respectively. The Raman spectrum of WO3 NFs showed their characteristic vibration modes that revealed the defect free nature of the WO3 NFs. Further, the elemental analysis indicated the stoichiometric composition of WO3 phase.

  13. Understanding the Potential of WO3 Based Sensors for Breath Analysis

    Science.gov (United States)

    Staerz, Anna; Weimar, Udo; Barsan, Nicolae

    2016-01-01

    Tungsten trioxide is the second most commonly used semiconducting metal oxide in gas sensors. Semiconducting metal oxide (SMOX)-based sensors are small, robust, inexpensive and sensitive, making them highly attractive for handheld portable medical diagnostic detectors. WO3 is reported to show high sensor responses to several biomarkers found in breath, e.g., acetone, ammonia, carbon monoxide, hydrogen sulfide, toluene, and nitric oxide. Modern material science allows WO3 samples to be tailored to address certain sensing needs. Utilizing recent advances in breath sampling it will be possible in the future to test WO3-based sensors in application conditions and to compare the sensing results to those obtained using more expensive analytical methods. PMID:27801881

  14. Pt supported self-assembled nest-like-porous WO3 hierarchical microspheres as electrocatalyst for methanol oxidation

    International Nuclear Information System (INIS)

    Zhang, Jun; Tu, Jiang-ping; Du, Gao-hui; Dong, Zi-min; Su, Qing-mei; Xie, Dong; Wang, Xiu-li

    2013-01-01

    Highlights: ► Nest-like-porous (NLP) WO 3 microspheres are assembled by a hydrothermal method. ► The NLP-WO 3 microspheres have a hexagonal structure and high porous surface. ► Great enhancement of electrochemical property is achieved for Pt/NLP-WO 3 microspheres. -- Abstract: Hexagonal tungsten trioxide (hex-WO 3 ) hierarchical microspheres with nest-like pores are synthesized by a facile hydrothermal method. The nest-like-porous (NLP) WO 3 hierarchical microspheres with 5–6 μm in diameters are self-assembled of single-crystal nanowires. The nanowires have lengths of several hundred nanometers and diameters of 5–30 nm; the long axis of nanowire is oriented toward 〈0 0 1〉 direction. The specific surface area of hex-WO 3 microspheres is 62 m 2 g −1 . 20 wt.% Pt nanoparticles with ∼7 nm are loaded onto the WO 3 microspheres using a conventional microwave-assisted ethylene glycol (EG) method. The electrocatalytic activity for methanol oxidation of Pt/NLP-WO 3 microspheres is investigated by cyclic voltammetry and chronoamperometry. Due to the large tunnels of hexagonal structure and high porous surface morphology, great enhancement of electrochemical performance is achieved. The Pt/NLP-WO 3 microspheres are demonstrated to be a promising anode material for direct methanol fuel cells (DMFC)

  15. Nonlinear current-voltage characteristics of WO3-x nano-/micro-rods

    Science.gov (United States)

    Shen, Zhenguang; Peng, Zhijian; Zhao, Zengying; Fu, Xiuli

    2018-04-01

    A series of crystalline tungsten oxide nano-/micro-rods with different compositions of WO3, WO2.90, W19O55 (WO2.89) and W18O49 (WO2.72) but identical morphology feature were first prepared. Then, various nanoscaled electrical devices were fabricated from them by micro-fabrication through a focused ion beam technique. Interestingly, the devices from the oxygen-deficient WO3-x display significantly nonlinear current-voltage characteristics. The calculated nonlinear coefficients of the WO2.90, WO2.83, and WO2.72 varistors are 2.52, 3.32 and 4.91, respectively. The breakdown voltage of the WO2.90, WO2.83, and WO2.72 varistors are 1.93, 1.28 and 0.93 V, respectively. Such WO3-x nano-varistors might be promising for low-voltage electrical/electronic devices.

  16. Room temperature NO2-sensing properties of porous silicon/tungsten oxide nanorods composite

    International Nuclear Information System (INIS)

    Wei, Yulong; Hu, Ming; Wang, Dengfeng; Zhang, Weiyi; Qin, Yuxiang

    2015-01-01

    Highlights: • Porous silicon/WO 3 nanorods composite is synthesized via hydrothermal method. • The morphology of WO 3 nanorods depends on the amount of oxalic acid (pH value). • The sensor can detect ppb level NO 2 at room temperature. - Abstract: One-dimensional single crystalline WO 3 nanorods have been successfully synthesized onto the porous silicon substrates by a seed-induced hydrothermal method. The controlled morphology of porous silicon/tungsten oxide nanorods composite was obtained by using oxalic acid as an organic inducer. The reaction was carried out at 180 °C for 2 h. The influence of oxalic acid (pH value) on the morphology of porous silicon/tungsten oxide nanorods composite was investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The NO 2 -sensing properties of the sensor based on porous silicon/tungsten oxide nanorods composite were investigated at different temperatures ranging from room temperature (∼25 °C) to 300 °C. At room temperature, the sensor behaved as a typical p-type semiconductor and exhibited high gas response, good repeatability and excellent selectivity characteristics toward NO 2 gas due to its high specific surface area, special structure, and large amounts of oxygen vacancies

  17. Influence of annealing conditions on anodic tungsten oxide layers and their photoelectrochemical activity

    International Nuclear Information System (INIS)

    Syrek, Karolina; Zych, Marta; Zaraska, Leszek; Sulka, Grzegorz D.

    2017-01-01

    Highlights: • Effect of annealing temperature on the morphology and crystalline structure of anodic WO 3 was investigated. • Photoelectrochemical properties of WO 3 layers annealed at different temperatures were studied. • Edges of conduction and valence bands were estimated for tungsten oxide layers annealed at different temperatures. • Influence of annealing time on crystalline structure, morphology and photoelectrochemical performance was studied. - Abstract: The nanoporous tungsten oxide films having an amorphous structure were prepared in an electrolyte containing fluoride ions via an anodization process. The as-synthesized anodic oxide layers can be easily converted to the monoclinic WO 3 phase upon annealing in air. The as-synthesized and annealed WO 3 layers were investigated by using X-ray diffraction, scanning electron microscopy, and photocurrent spectroscopy. The effect of annealing temperature and annealing time on the oxide morphology, crystal structure and electrochemical properties were studied. The samples were annealed in air at the temperatures ranging from 400 to 600 °C, and it was found that the original porous morphology of oxide is completely lost after annealing at 600 °C. The changes in the average crystallite sizes upon annealing were confirmed by XRD measurements. The photoelectrochemical performance of the annealed WO 3 layers were studied under pulsed UV illumination, and the highest photocurrents were observed at the incident light wavelength of 350 nm for the sample annealed at 500 °C for 2 h. The band gap energy and the positions of conduction and valence band edges were determined for all studied samples.

  18. Behavior of the monophosphate tungsten bronzes (PO2)4(WO3)2m (m = 7 and 8) in the course of electrochemical lithium insertion

    International Nuclear Information System (INIS)

    Martinez-de la Cruz, A.; Longoria Rodriguez, F.E.; Gonzalez, Lucy T.; Torres-Martinez, Leticia M.

    2007-01-01

    The electrochemical lithium insertion process has been studied in the family of monophosphate tungsten bronzes (PO 2 ) 4 (WO 3 ) 2m , where m = 7 and 8. Structural changes in the pristine oxides were followed as lithium insertion proceeded. Through potentiostatic intermittent technique the different processes which take place in the cathode during the discharge of the cell were analyzed. The nature of the bronzes Li x (PO 2 ) 4 (WO 3 ) 2m formed was determined by in situ X-ray diffraction experiments. These results have allowed establishing a correlation with the reversible/irreversible processes detected during the electrochemical lithium insertion

  19. The formation of tungsten doped Al_2O_3/ZnO coatings on aluminum by plasma electrolytic oxidation and their application in photocatalysis

    International Nuclear Information System (INIS)

    Stojadinović, Stevan; Vasilić, Rastko; Radić, Nenad; Tadić, Nenad; Stefanov, Plamen; Grbić, Boško

    2016-01-01

    Highlights: • Tungsten doped Al_2O_3/ZnO coatings are formed by plasma electrolytic oxidation (PEO). • Coatings are mainly composed of alpha alumina, ZnO and metallic tungsten. • Photocatalytic activity of doped Al_2O_3/ZnO coatings is higher than of undoped ones. • The increase of photoluminescence corresponds to decrease of photocatalytic activity. • Tungsten acts as a charge trap to reduce the recombination rate of electron/hole pairs. - Abstract: Tungsten doped Al_2O_3/ZnO coatings are formed by plasma electrolytic oxidation of aluminum substrate in supporting electrolyte (0.1 M boric acid + 0.05 M borax + 2 g/L ZnO) with addition of different concentrations of Na_2WO_4·2H_2O. The morphology, crystal structure, chemical composition, and light absorption characteristics of formed surface coatings are investigated. The X-ray diffraction and X-ray photoelectron spectroscopy results indicate that formed surface coatings consist of alpha and gamma phase of Al_2O_3, ZnO, metallic tungsten and WO_3. Obtained results showed that incorporated tungsten does not have any influence on the absorption spectra of Al_2O_3/ZnO coatings, which showed invariable band edge at about 385 nm. The photocatalytic activity of undoped and tungsten doped Al_2O_3/ZnO coatings is estimated by the photodegradation of methyl orange. The photocatalytic activity of tungsten doped Al_2O_3/ZnO coatings is higher thanof undoped Al_2O_3/ZnO coatings; the best photocatalytic activity is ascribed to coatings formed in supporting electrolyte with addition of 0.3 g/L Na_2WO_4·2H_2O. Tungsten in Al_2O_3/ZnO coatings acts as a charge trap, thus reducing the recombination rate of photogenerated electron-hole pairs. The results of PL measurements are in agreement with photocatalytic activity. Declining PL intensity corresponds to increasing photocatalytic activity of the coatings, indicating slower recombination of electron-hole pairs.

  20. Synthesis, Consolidation and Characterization of Sol-gel Derived Tantalum-Tungsten Oxide Thermite Composites

    Energy Technology Data Exchange (ETDEWEB)

    Cervantes, O [Univ. of California, Davis, CA (United States)

    2010-06-01

    Energetic composite powders consisting of sol-gel (SG) derived nanostructured tungsten oxide were produced with various amounts of micrometer-scale tantalum fuel metal. Such energetic composite powders were ignition-tested and results show that the powders are not sensitive to friction, spark and/or impact ignition. Initial consolidation experiments, using the High Pressure Spark Plasma Sintering (HPSPS) technique, on the SG derived nanostructured tungsten oxide produced samples with higher relative density than can be achieved with commercially available tungsten oxide. The SG derived nanostructured tungsten oxide with immobilized tantalum fuel metal (Ta - WO3) energetic composite was consolidated to a density of 9.17 g·cm-3 or 93% relative density. In addition, those samples were consolidated without significant pre-reaction of the constituents, thus retaining their stored chemical energy.

  1. Structure, electrochromic and optical properties of WO3 film prepared by dip coating-pyrolysis

    International Nuclear Information System (INIS)

    Yang Haitao; Shang Fuliang; Gao Ling; Han Haitao

    2007-01-01

    The tungsten oxide (WO 3 ) film was grown by dip coating-pyrolysis method with the PEG-400 as the structure-directing agent. Microstructure of the WO 3 film was characterized by TG-DSC, XRD and SEM techniques. It was found that the film annealed at 350 deg. C for 2 h comprised cubic WO 3 and orthorhombic WO 3 . The measurements of the cyclic voltammetry (CV) and UV-vis spectrum suggested that the WO 3 film had a good electrochromic reversibility performance. The film possessed excellent modulation to the visible light and the maximal average transmittance modulation reached 70.06%

  2. Characterization of Porous WO3 Electrochromic Device by Electrochemical Impedance Spectroscopy

    Directory of Open Access Journals (Sweden)

    Chien Chon Chen

    2013-01-01

    Full Text Available This paper concerns the microstructure of the anodic tungsten oxide (WO3 and its use in an electrochromic (EC glass device. When voltages between 100 V and 160 V were applied to tungsten film for 1 h under 0.4 wt. % NaF electrolyte, porous WO3 film was formed. The film, which had a large surface area, was used as electrochromic film for EC glass. The average transmittance in a visible region of the spectrum for a 144 cm2 EC device was above 75% in the bleached state and below 40% in the colored state, respectively. Repeatability using of the colored/bleached cycles was tested good by a cyclic voltammograms method. The internal impedance values under colored and bleached states were detected and simulated using an electrical impedance spectra (EIS technique. The EC glass impedance characteristics were simulated using resistors, capacitors, and Warburg impedance. The ITO/WO3, WO3/electrolyte, electrolyte/NiO, and NiO/ITO interfaces can be simulated using a resistance capacitance (RC parallel circuits, and bulk materials such as the indium tin oxide (ITO and conducting wire can be simulated by using a series of resisters.

  3. Electrical transport properties of nanoplates shaped tungsten oxide embedded poly(vinyl-alcohol) film

    Science.gov (United States)

    Das, Amit Kumar; Chatterjee, Piyali; Meikap, Ajit Kumar

    2018-04-01

    Tungsten oxide (WO3) nanoplates have been synthesized via hydrothermal method. The average crystallite size of the nanoplates is 28.9 ± 0.5 nm. The direct and indirect band gap of WO3 is observed. The AC conductivity of PVA-WO3 composite film has been observed and carrier transport mechanism follows correlated barrier hopping model. The maximum barrier height of the composite film is 0.1 eV. The electric modulus reflects the non-Debye type behaviour of relaxation time which is simulated by Kohlrausch-Willims-Watts (KWW) function.

  4. Characteristics of tungsten oxide thin films prepared on the flexible substrates using pulsed laser deposition

    International Nuclear Information System (INIS)

    Suda, Yoshiaki; Kawasaki, Hiroharu; Ohshima, Tamiko; Yagyuu, Yoshihito

    2008-01-01

    Tungsten trioxide (WO 3 ) thin films have been prepared on the flexible indium tin oxide (ITO) substrates by pulsed laser deposition (PLD) using WO 3 targets in oxygen gas. Color of the WO 3 film on the flexible ITO substrates depends on the oxygen gas mixture. The plasma plume produced by PLD using a Nd:YAG laser and WO 3 target is investigated by temporal and spatial-resolved optical emission spectroscopy. WO 3 films prepared on the flexible ITO substrates show electrochromic properties, even when the substrates are bent. The film color changes from blue to transparent within 10-20 s after the applied DC voltage is turned off

  5. Effect of oxygen vacancies on the electronic and optical properties of tungsten oxide from first principles calculations

    Science.gov (United States)

    Mehmood, Faisal; Pachter, Ruth; Murphy, Neil R.; Johnson, Walter E.; Ramana, Chintalapalle V.

    2016-12-01

    In this work, we investigated theoretically the role of oxygen vacancies on the electronic and optical properties of cubic, γ-monoclinic, and tetragonal phases of tungsten oxide (WO3) thin films. Following the examination of structural properties and stability of the bulk tungsten oxide polymorphs, we analyzed band structures and optical properties, applying density functional theory (DFT) and GW (Green's (G) function approximation with screened Coulomb interaction (W)) methods. Careful benchmarking of calculated band gaps demonstrated the importance of using a range-separated functional, where results for the pristine room temperature γ-monoclinic structure indicated agreement with experiment. Further, modulation of the band gap for WO3 structures with oxygen vacancies was quantified. Dielectric functions for cubic WO3, calculated at both the single-particle, essentially time-dependent DFT, as well as many-body GW-Bethe-Salpeter equation levels, indicated agreement with experimental data for pristine WO3. Interestingly, we found that introducing oxygen vacancies caused appearance of lower energy absorptions. A smaller refractive index was indicated in the defective WO3 structures. These predictions could lead to further experiments aimed at tuning the optical properties of WO3 by introducing oxygen vacancies, particularly for the lower energy spectral region.

  6. Electrochromic device based on electrospun WO{sub 3} nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Dulgerbaki, Cigdem; Maslakci, Neslihan Nohut; Komur, Ali Ihsan; Oksuz, Aysegul Uygun, E-mail: ayseguluygun@sdu.edu.tr

    2015-12-15

    Highlights: • WO{sub 3} electrochromic nanofibers were prepared by electrospinning technique. • WO{sub 3} nanofibers switched reversibly from transparent to blue color. • Electrochromic device was assembled using ionic liquid based gel electrolyte. • Significant optical modulation and excellent cycling stability were achieved for ECD. - Abstract: The tungsten oxide (WO{sub 3}) nanofibers were grown directly onto an ITO-coated glass via an electrospinning method for electrochromic applications. The electrochromic properties of WO{sub 3} nanofibers were investigated in the presence of different electrolytes including a series of ionic liquids and classic LiClO{sub 4}-PC system. A significant optical modulation of 20.82% at 760 nm, reversible coloration with efficiency of 64.58 cm{sup 2}/C and excellent cycling stability were achieved for the nanofiber electrochromic device (ECD) with ionic liquid based gel electrolyte.

  7. Annealing induced structural evolution and electrochromic properties of nanostructured tungsten oxide films

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Ching-Lin [Department of Materials Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan, ROC (China); Lin, Chung-Kwei [School of Dental Technology, Taipei Medical University, Taipei City 110, Taiwan, ROC (China); Wang, Chun-Kai [Department of Materials Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan, ROC (China); Wang, Sheng-Chang [Department of Mechanical Engineering, Southern Taiwan University, Tainan 710, Taiwan, ROC (China); Huang, Jow-Lay, E-mail: JLH888@mail.ncku.edu.tw [Department of Materials Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan, ROC (China); Department of Chemical and Materials Engineering, National University of Kaohsiung, Kaohsiung 81148, Taiwan, ROC (China); Research Center for Energy Technology and Strategy, National Cheng Kung University, Tainan 701, Taiwan, ROC (China)

    2013-12-31

    The effect of microstructure on the optical and electrochemical properties of nanostructured tungsten oxide films was evaluated as a function of annealing temperature. The films using block copolymer as the template were prepared from peroxotungstic acid (PTA) by spin-coating onto the substrate and post-annealed at 250–400 °C to form tungsten oxide films with nanostructure. The microstructure of the films was measured by X-ray diffraction and surface electron microscopy. The films annealed at temperatures below 300 °C are characterized by amorphous or nanocrystalline structures with a pore size of less than 10 nm. The evaluated annealing temperature caused a triclinic crystalline structure and microcracks. Cyclic voltammetry measurements were performed in a LiClO{sub 4}-propylene carbonate electrolyte. The results showed that the ion inserted capacity were maximized for films annealed at 300 °C and decreased with the increasing of annealing temperature. The electrochromic properties of the nanostructured tungsten oxide films were evaluated simultaneously by potentiostat and UV–vis spectroscopy. The films annealed at 300 °C exhibit high transmission modulation (∆T ∼ 40%) at λ = 633 nm and good kinetic properties. As a result, the correlation between the microstructure and kinetic properties was established, and the electrochromic properties have been demonstrated. - Highlights: • Surfactant-assisted WO{sub 3} films have been prepared by sol–gel method. • Nanostructure of porous WO{sub 3} film is retained after crystallization. • Kinetic properties of WO{sub 3} can be improved by nanostructure and crystallinity.

  8. Effect of Post-annealing on the Electrochromic Properties of Layer-by-Layer Arrangement FTO-WO3-Ag-WO3-Ag

    Science.gov (United States)

    Hoseinzadeh, S.; Ghasemiasl, R.; Bahari, A.; Ramezani, A. H.

    2018-03-01

    In the current study, composites of tungsten trioxide (W03) and silver (Ag) are deposited in a layer-by-layer electrochromic (EC) arrangement onto a fluorine-doped tin oxide coated glass substrate. Tungsten oxide nanoparticles are an n-type semiconductor that can be used as EC cathode material. Nano-sized silver is a metal that can serve as an electron trap center that facilitates charge departure. In this method, the WO3 and Ag nanoparticle powder were deposited by physical vapor deposition onto the glass substrate. The fabricated electrochromic devices (ECD) were post-annealed to examine the effect of temperature on their EC properties. The morphology of the thin film was characterized by scanning electron microscopy and atomic force microscopy. Structural analysis showed that the addition of silver dopant increased the size of the aggregation of the film. The film had an average approximate roughness of about 17.8 nm. The electro-optical properties of the thin film were investigated using cyclic voltammetry and UV-visible spectroscopy to compare the effects of different post-annealing temperatures. The ECD showed that annealing at 200°C provided better conductivity (maximum current of about 90 mA in the oxidation state) and change of transmittance (ΔT = 90% at the continuous switching step) than did the other thin films. The optical band gaps of the thin film showed that it allowed direct transition at 3.85 eV. The EC properties of these combinations of coloration efficiency and response time indicate that the WO3-Ag-WO3-Ag arrangement is a promising candidate for use in such ECDs.

  9. The correlations of electrochromism and thermochromism of tungsten oxide films studied by slow positron beam

    International Nuclear Information System (INIS)

    Ma Chuangxin; Zhou Chunlan; Zhang Zhiming; Wang Baoyi; Wei Long

    2004-01-01

    Electrochromic (EC) and thermochromic (TC) tungsten oxide (WO 3 ) films, deposited by magnetron sputtering and vacuum thermal evaporation, were studied systematically by means of slow positron measurements. The S parameters of colored amorphous WO 3 film and crystalline WO 3 film behaved quite similarly in the processes of thermochromism and electrochromism, little influenced by the different deposition methods. It indicates that the coloration processes under various external conditions are correlated with each other. It also shows that the slow positron beam technique may play a particular role in the study of chromogenic materials. (orig.)

  10. Characterization of (0.3-x)WO3-0.70Sb2O3-xAgNO3 (0.29 ≥ X ≥ 0.01) polycrystalline system

    International Nuclear Information System (INIS)

    Ramesh, S.; Das, B.B.; Nagraju, D.

    2013-01-01

    Polyoxometalates (POMs) form a characteristic class of inorganic metal-oxygen compound. Due to their structural diversity and attractive properties, POMs have been attracted during the last decades. Especially, transition metal substituted POMs have become one of the most fascinating field in the synthetic chemistry. POMs, not only due to their unique properties on size, shape, charge density, redox potential and stability, but also owing to the promising applications in catalysis, medicine and material science. It is well known that tungsten produces many complex oxides similar to molybdenum and it is known to exhibit a variety of interesting properties counting semiconductivity, photochromism and electrochromism, space-charge injection. The structural identification of tungstate would be helpful in determining the species responsible for the properties mentioned. In the tungsten trioxide systems, tungsten exhibit mixed-valence states, specifically W 5+ (5d 1 ) and W 6+ (5d 0 ). The thermal hopping of electrons between these two valence states appears to be responsible for conduction in tungsten containing complex oxides. Since a ternary system such as WO 3 -Sb 2 O 3 AgNO 3 contains different structural units with interesting paramagnetic probe, WO 3 (4d 1 ). The study of structure-property relations as well as site symmetry around the WO 5+ site of such system is indeed interesting. However, the report on EPR studies of such systems is limited

  11. The formation of tungsten doped Al{sub 2}O{sub 3}/ZnO coatings on aluminum by plasma electrolytic oxidation and their application in photocatalysis

    Energy Technology Data Exchange (ETDEWEB)

    Stojadinović, Stevan, E-mail: sstevan@ff.bg.ac.rs [University of Belgrade, Faculty of Physics, Studentski trg 12-16, 11000 Belgrade (Serbia); Vasilić, Rastko [University of Belgrade, Faculty of Physics, Studentski trg 12-16, 11000 Belgrade (Serbia); Radić, Nenad [University of Belgrade, Institute of Chemistry, Technology and Metallurgy, Department of Catalysis and Chemical Engineering, Njegoševa 12, 11000 Belgrade (Serbia); Tadić, Nenad [University of Belgrade, Faculty of Physics, Studentski trg 12-16, 11000 Belgrade (Serbia); Stefanov, Plamen [Institute of General and Inorganic Chemistry, Bulgarian Academy of Sciences, Acad. G. Bonchev Str., Block 11, 1113 Sofia (Bulgaria); Grbić, Boško [University of Belgrade, Institute of Chemistry, Technology and Metallurgy, Department of Catalysis and Chemical Engineering, Njegoševa 12, 11000 Belgrade (Serbia)

    2016-07-30

    Highlights: • Tungsten doped Al{sub 2}O{sub 3}/ZnO coatings are formed by plasma electrolytic oxidation (PEO). • Coatings are mainly composed of alpha alumina, ZnO and metallic tungsten. • Photocatalytic activity of doped Al{sub 2}O{sub 3}/ZnO coatings is higher than of undoped ones. • The increase of photoluminescence corresponds to decrease of photocatalytic activity. • Tungsten acts as a charge trap to reduce the recombination rate of electron/hole pairs. - Abstract: Tungsten doped Al{sub 2}O{sub 3}/ZnO coatings are formed by plasma electrolytic oxidation of aluminum substrate in supporting electrolyte (0.1 M boric acid + 0.05 M borax + 2 g/L ZnO) with addition of different concentrations of Na{sub 2}WO{sub 4}·2H{sub 2}O. The morphology, crystal structure, chemical composition, and light absorption characteristics of formed surface coatings are investigated. The X-ray diffraction and X-ray photoelectron spectroscopy results indicate that formed surface coatings consist of alpha and gamma phase of Al{sub 2}O{sub 3}, ZnO, metallic tungsten and WO{sub 3}. Obtained results showed that incorporated tungsten does not have any influence on the absorption spectra of Al{sub 2}O{sub 3}/ZnO coatings, which showed invariable band edge at about 385 nm. The photocatalytic activity of undoped and tungsten doped Al{sub 2}O{sub 3}/ZnO coatings is estimated by the photodegradation of methyl orange. The photocatalytic activity of tungsten doped Al{sub 2}O{sub 3}/ZnO coatings is higher thanof undoped Al{sub 2}O{sub 3}/ZnO coatings; the best photocatalytic activity is ascribed to coatings formed in supporting electrolyte with addition of 0.3 g/L Na{sub 2}WO{sub 4}·2H{sub 2}O. Tungsten in Al{sub 2}O{sub 3}/ZnO coatings acts as a charge trap, thus reducing the recombination rate of photogenerated electron-hole pairs. The results of PL measurements are in agreement with photocatalytic activity. Declining PL intensity corresponds to increasing photocatalytic activity of the

  12. Synthesis of hexagonal ultrathin tungsten oxide nanowires with diameters below 5 nm for enhanced photocatalytic performance

    Science.gov (United States)

    Lu, Huidan; Zhu, Qin; Zhang, Mengying; Yan, Yi; Liu, Yongping; Li, Ming; Yang, Zhishu; Geng, Peng

    2018-04-01

    Semiconductor with one dimension (1D) ultrathin nanostructure has been proved to be a promising nanomaterial in photocatalytic field. Great efforts were made on preparation of monoclinic ultrathin tungsten oxide nanowires. However, non-monoclinic phase tungsten oxides with 1D ultrathin structure, especially less than 5 nm width, have not been reported. Herein, we report the synthesis of hexagonal ultrathin tungsten oxide nanowires (U-WOx NW) by modified hydrothermal method. Microstructure characterization showed that U-WOx NW have the diameters of 1-3 nm below 5 nm and are hexagonal phase sub-stoichiometric WOx. U-WOx NW show absorption tail in the visible and near infrared region due to oxygen vacancies. For improving further photocatalytic performance, Ag co-catalyst was grown directly onto U-WOx NW surface by in situ redox reaction. Photocatalytic measurements revealed hexagonal U-WOx NW have better photodegradation activity, compared with commercial WO3(C-WO3) and oxidized U-WOx NW, ascribe to larger surface area, short diffusion length of photo-generated charge carriers and visible absorption of oxygen-vacancy-rich hexagonal ultrathin nanostructures. Moreover, the photocatalytic activity and stability of U-WOx NW using Ag co-catalyst were further improved.

  13. Correlations among structure, composition and electrochemical performances of WO3 anode materials for lithium ion batteries

    International Nuclear Information System (INIS)

    Li, Pu; Li, Xing; Zhao, Ziyan; Wang, Mingshan; Fox, Thomas; Zhang, Qian; Zhou, Ying

    2016-01-01

    Highlights: • The residual precursor ions affect the charge/discharge performances of WO 3 . • Lithiated monoclinic WO 3 reveals the best discharge capacity. • Lithiation can enhance the conductivity of WO 3 . - Abstract: Suitable host structure for lithium insertion and extraction is crucial for lithium-ion batteries. Tungsten trioxides (WO 3 ) are particularly interesting materials for this purpose. In this work, the influences of structure and composition of WO 3 on the charge/discharge performances of Li-ion batteries are systematically investigated. Firstly, lithiated tungsten trioxides (Li-WO 3 ) are successfully synthesized by a hydrothermal method followed by annealing at different temperatures (200–600 °C). It is found that the hexagonal framework collapses and gradually transforms to the monoclinic phase due to the release of NH 4 + and NH 3 molecules. Unexpectedly, monoclinic WO 3 reveals better performances than that of hexagonal WO 3 . Among all the investigated samples, the lithiated WO 3 annealed at 500 °C exhibits the highest discharge capacity and cycle performance (703 mAh g −1 after 10 cycles). We believe that the Li + remained in the solid structure of WO 3 can lead to a more stable structure. In addition, Li + could inhibit the oxidation of W 5+ during the heat treatment process, which increases the electron conductivity of WO 3 . Our results indicate that the electrochemical properties of WO 3 are strongly related to the residual precursor and crystal structure.

  14. Tungsten oxide proton conducting films for low-voltage transparent oxide-based thin-film transistors

    International Nuclear Information System (INIS)

    Zhang, Hongliang; Wan, Qing; Wan, Changjin; Wu, Guodong; Zhu, Liqiang

    2013-01-01

    Tungsten oxide (WO x ) electrolyte films deposited by reactive magnetron sputtering showed a high room temperature proton conductivity of 1.38 × 10 −4 S/cm with a relative humidity of 60%. Low-voltage transparent W-doped indium-zinc-oxide thin-film transistors gated by WO x -based electrolytes were self-assembled on glass substrates by one mask diffraction method. Enhancement mode operation with a large current on/off ratio of 4.7 × 10 6 , a low subthreshold swing of 108 mV/decade, and a high field-effect mobility 42.6 cm 2 /V s was realized. Our results demonstrated that WO x -based proton conducting films were promising gate dielectric candidates for portable low-voltage oxide-based devices.

  15. Synthesis, characterization and liquefied petroleum gas (LPG) sensing properties of WO3 nano-particles

    Science.gov (United States)

    Singh, Subhash; Majumder, S. B.

    2018-05-01

    Metal oxide sensors, such as ZnO, SnO2, and WO3 etc. have been utilized for several decades for low-costd etection of combustible and toxic gases. In the present work tungsten oxide (WO3) nanoparticles have been prepared by using an economic wet chemical synthesis route. To understand the phase formation behavior of the synthesized powders, X-ray diffraction analysis has been performed. The microstructure evolution of the synthesized powders was characterized by field-emission scanning electron microscopy (FESEM), and transmission electron microscopy (TEM). The calcined phase pure WO3 nanoparticles are investigated in terms of LPG gas sensing properties. The gas sensing measurements has been done in two different mode of operation (namely static and dynamic measurements). The degree of oxygen deficiency in the WO3 sensor also affected the sensor properties and the optimum oxygen content of WO3 was necessary to get high sensitivity for LPG. The WO3 sensor shows the excellent sensor properties for LPG at the operating temperature of 250°C.

  16. Enhancement of oxidative electrocatalytic properties of platinum nanoparticles by supporting onto mixed WO{sub 3}/ZrO{sub 2} matrix

    Energy Technology Data Exchange (ETDEWEB)

    Rutkowska, Iwona A., E-mail: ilinek@chem.uw.edu.pl; Wadas, Anna; Kulesza, Pawel J., E-mail: pkulesza@chem.uw.edu.pl

    2016-12-01

    Highlights: • The electrocatalytic system utilizing Pt nanoparticles dispersed on mixed metal oxide (WO{sub 3}/ZrO{sub 2}) system is proposed. • The system is characterized by high activity toward oxidations of ethanol, methanol and acetaldehyde in acid medium. • The enhancement effect is facilitated by presence of hydroxyl groups, high mobility of protons and improved distribution of electrons. • Strong interactions between Pt and the mixed oxide WO{sub 3}/ZrO{sub 2} support are postulated. - Abstract: Nanostructured mixed metal (W, Zr) oxide matrices (in a form of layered intercalated films of WO{sub 3} and ZrO{sub 2}) are considered here for supporting and activating catalytic platinum nanoparticles toward electrooxidation of ethanol. Remarkable increases of electrocatalytic (voltammetric, chronoamperometric) currents measured in 0.5 mol dm{sup −3} H{sub 2}SO{sub 4} (containing 0.5 mol dm{sup −3} ethanol) have been observed. Comparison has been made to the behavior of methanol and acetaldehyde under analogous conditions. The enhancement effects are interpreted in terms of specific interactions between platinum nanoparticles and the metal oxide species, high acidity of the mixed oxide sites, as well as high population of surface hydroxyl groups and high mobility of protons existing in close vicinity of Pt catalytic sites. The metal oxide nanostructures are expected to interact competitively (via the surface hydroxyl groups) with adsorbates of the undesirable reaction intermediates, including CO, facilitating their desorption (“third body effect”), or even oxidative removal (e.g., of CO to CO{sub 2}). The fact that the partially reduced tungsten oxide (H{sub x}WO{sub 3}) component is characterized by fast electron transfers coupled to proton displacements tends to improve the overall charge propagation at the electrocatalytic interface.

  17. Characterisation and application of WO3 films for electrochromic devices

    Science.gov (United States)

    Stapinski, Thomas; Marszalek, Konstanty; Swatowska, Barbara; Stanco, Agnieszka

    2013-07-01

    Electrochromic system is the one of the most popular devices using color memory effect under the influence of an applied voltage. The electrochromic system was produced based on the thin WO3 electrochromic films. Films were prepared by RF magnetron sputtering from tungsten targets in a reactive Ar+O2 gas atmosphere of various Ar/O2 ratios. The technological gas mixture pressure was 3 Pa and process temperature 30°C. Structural and optical properties of WO3 films were investigated for as-deposited and heat treated samples at temperature range from 350°C to 450°C in air. The material revealed the dependence of properties on preparation conditions and on post-deposition heat treatment. Main parameters of thin WO3 films: thickness d, refractive index n, extinction coefficient k and energy gap Eg were determined and optimized for application in electrochromic system. The main components of the system were glass plate with transparent conducting oxides, electrolyte, and glass plate with transparent conducting oxides and WO3 layer. The optical properties of the system were investigated when a voltage was applied across it. The electrochromic cell revealed the controllable transmittance depended on the operation voltage.

  18. Electrochromism and photocatalysis in dendrite structured Ti:WO3 thin films grown by sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Karuppasamy, A., E-mail: karuppasamy@psnacet.edu.in

    2015-12-30

    Graphical abstract: - Highlights: • Dendrite structured Ti doped WO{sub 3} (WTO) thin films are grown by co-sputtering. • Sputtering condition influences structure and surface morphology of WTO films. • Titanium doping and annealing lead to dendritic surface structures in WTO films. • Structural, optical, electrochromic and photocatalytic properties of WTO films. • Enhanced electrochromism and photocatalysis in dendrite structured WTO thin films. - Abstract: Titanium doped tungsten oxide (Ti:WO{sub 3}) thin films with dendrite surface structures were grown by co-sputtering titanium and tungsten in Ar + O{sub 2} atmosphere. Ti:WO{sub 3} thin films were deposited at oxygen flow rates corresponding to pressures in the range 1.0 × 10{sup −3}–5.0 × 10{sup −3} mbar. Argon flow rate and sputtering power densities for titanium (2 W/cm{sup 2}) and tungsten (3 W/cm{sup 2}) were kept constant. Ti:WO{sub 3} films deposited at an oxygen pressure of 5 × 10{sup −3} mbar are found to be better electrochromic and photocatalytic. They have high optical modulation (80% at λ = 550 nm), coloration efficiency (60 cm{sup 2}/C at λ = 550 nm), electron/ion storage and removal capacity (Qc: −22.01 mC/cm{sup 2}, Qa: 17.72 mC/cm{sup 2}), reversibility (80%) and methylene blue decomposition rate (−1.38 μmol/l d). The combined effects of titanium doping, dendrite surface structures and porosity leads to significant enhancement in the electrochromic and photocatalytic properties of Ti:WO{sub 3} films.

  19. Electrochromism and photocatalysis in dendrite structured Ti:WO3 thin films grown by sputtering

    International Nuclear Information System (INIS)

    Karuppasamy, A.

    2015-01-01

    Graphical abstract: - Highlights: • Dendrite structured Ti doped WO 3 (WTO) thin films are grown by co-sputtering. • Sputtering condition influences structure and surface morphology of WTO films. • Titanium doping and annealing lead to dendritic surface structures in WTO films. • Structural, optical, electrochromic and photocatalytic properties of WTO films. • Enhanced electrochromism and photocatalysis in dendrite structured WTO thin films. - Abstract: Titanium doped tungsten oxide (Ti:WO 3 ) thin films with dendrite surface structures were grown by co-sputtering titanium and tungsten in Ar + O 2 atmosphere. Ti:WO 3 thin films were deposited at oxygen flow rates corresponding to pressures in the range 1.0 × 10 −3 –5.0 × 10 −3 mbar. Argon flow rate and sputtering power densities for titanium (2 W/cm 2 ) and tungsten (3 W/cm 2 ) were kept constant. Ti:WO 3 films deposited at an oxygen pressure of 5 × 10 −3 mbar are found to be better electrochromic and photocatalytic. They have high optical modulation (80% at λ = 550 nm), coloration efficiency (60 cm 2 /C at λ = 550 nm), electron/ion storage and removal capacity (Qc: −22.01 mC/cm 2 , Qa: 17.72 mC/cm 2 ), reversibility (80%) and methylene blue decomposition rate (−1.38 μmol/l d). The combined effects of titanium doping, dendrite surface structures and porosity leads to significant enhancement in the electrochromic and photocatalytic properties of Ti:WO 3 films.

  20. Microstructure and electrical-optical properties of cesium tungsten oxides synthesized by solvothermal reaction followed by ammonia annealing

    International Nuclear Information System (INIS)

    Liu Jingxiao; Ando, Yoshihiko; Dong Xiaoli; Shi Fei; Yin Shu; Adachi, Kenji; Chonan, Takeshi; Tanaka, Akikazu; Sato, Tsugio

    2010-01-01

    Cesium tungsten oxides (Cs x WO 3 ) were synthesized by solvothermal reactions using ethanol and 57.1 vol% ethanol aqueous solution at 200 o C for 12 h, and the effects of post annealing in ammonia atmosphere on the microstructure and electrical-optical properties were investigated. Agglomerated particles consisting of disk-like nanoparticles and nanorods of Cs x WO 3 were formed in the pure ethanol and ethanol aqueous solutions, respectively. The samples retained the original morphology and crystallinity after annealing in ammonia atmosphere up to 500 o C, while a small amount of nitrogen ion were incorporated in the lattice. The as-prepared Cs x WO 3 sample showed excellent near infrared (NIR) light shielding ability as well as high transparency in the visible light region. The electrical resistivity of the pressed pellets of the powders prepared in pure ethanol and 57.1 vol% ethanol aqueous solution greatly decreased after ammonia annealing at 500 o C, i.e., from 734 to 31.5 and 231 to 3.58 Ω cm, respectively. - Graphical abstract: Cesium tungsten oxides (Cs x WO 3 ) with different morphology were synthesized by solvothermal reaction, and the effects of post-ammonia annealing on the microstructure and electrical-optical properties were investigated.

  1. Photocatalytic activity of bipolar pulsed magnetron sputter deposited TiO{sub 2}/TiWO{sub x} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Weng, Ko-Wei; Hu, Chung-Hsuan; Hua, Li-Yu; Lee, Chin-Tan [Department of Electronic Engineering, National Quemoy University, 1 Daxue Road, Jinning Township, Kinmen 89250, Taiwan, ROC (China); Zhao, Yu-Xiang [Department of Computer Science and Information Engineering, National Quemoy University, Taiwan, ROC (China); Chang, Julian; Yang, Shu-Yi [Department of Applied English, National Quemoy University, Taiwan, ROC (China); Han, Sheng, E-mail: shenghan@nutc.edu.tw [Center for General Education, National Taichung University of Science and Technology, 129 San-min Road, Section 3, Taichung 40401, Taiwan, ROC (China)

    2016-08-15

    Highlights: • TiO{sub 2}/TiWO{sub x} films were fabricated by a bipolar pulsed magnetron sputtering apparatus. • Titanium oxide being sputtered tungsten enhanced the highly oriented of TiO{sub 2} (1 0 1) plane of the specimen assemblies. • The mechanism WO{sub 3}(h{sup +}, e{sup −})/TiO{sub 2}(h{sup +}, e{sup −}) → WO{sub 3}(e{sup −})/TiO{sub 2}(h{sup +}) shows the higher hydrophilicity and lower contact angle. - Abstract: Titanium oxide films were formed by sputtering and then TiWO{sub x} films were deposited by bipolar pulsed magnetron sputtering with pure titanium and tungsten metal targets. The sputtering of titanium oxide with tungsten enhanced the orientation of the TiO{sub 2} (1 0 1) plane of the specimen assemblies. The main varying parameter was the tungsten pulse power. Titanium oxide sputtered with tungsten using a pulsing power of 50 W exhibited a superior hydrophilic property, and a contact angle of 13.1°. This fabrication conditions maximized the photocatalytic decomposition of methylene blue solution. The mechanism by which the titanium oxide was sputtered with tungsten involves the photogeneration of holes and electron traps, inhibiting the hole–electron recombination, enhancing hydrophilicity and reducing the contact angle.

  2. Study of the structural evolutions of crystalline tungsten oxide films prepared using hot-filament CVD

    International Nuclear Information System (INIS)

    Feng, P X; Wang, X P; Zhang, H X; Yang, B Q; Wang, Z B; Gonzalez-BerrIos, A; Morell, G; Weiner, B

    2007-01-01

    Structural evolutions of tungsten oxide(WO 3 ) samples on different substrates are studied using Raman spectroscopy, scanning electron microscopy, energy dispersive spectroscopy, x-ray diffraction and x-ray photoelectron spectroscopy. The WO 3 samples are prepared using hot-filament CVD techniques. The focus of the study is on the evolutions of nano structures at different stages following deposition time. The experimental measurements reveal evolutions of the surface structures from uniform film to fractal-like structures, and eventually to nano particles, and crystalline structures from mono (0 1 0) crystalline thin film to polycrystalline thick film developments. The effect of high temperature on the nanostructured WO 3 is also investigated. Well-aligned nanoscale WO 3 rod arrays are obtained at a substrate temperature of up to 1400 deg. C. Further increasing the substrate temperature yields microscale crystalline WO 3 particles

  3. Hetero- and homogeneous three-dimensional hierarchical tungsten oxide nanostructures by hot-wire chemical vapor deposition

    Energy Technology Data Exchange (ETDEWEB)

    Houweling, Z.S., E-mail: Silvester.Houweling@asml.com [Utrecht University, Debye Institute for Nanomaterials Science, Nanophotonics—Physics of Devices, Princetonlaan 4, 3584 CB Utrecht (Netherlands); Harks, P.-P.R.M.L.; Kuang, Y.; Werf, C.H.M. van der [Utrecht University, Debye Institute for Nanomaterials Science, Nanophotonics—Physics of Devices, Princetonlaan 4, 3584 CB Utrecht (Netherlands); Geus, J.W. [Utrecht University, Inorganic Chemistry and Catalysis, Padualaan 8, 3584 CH Utrecht (Netherlands); Schropp, R.E.I. [Utrecht University, Debye Institute for Nanomaterials Science, Nanophotonics—Physics of Devices, Princetonlaan 4, 3584 CB Utrecht (Netherlands)

    2015-01-30

    We present the synthesis of three-dimensional tungsten oxide (WO{sub 3−x}) nanostructures, called nanocacti, using hot-wire chemical vapor deposition. The growth of the nanocacti is controlled through a succession of oxidation, reduction and re-oxidation processes. By using only a resistively heated W filament, a flow of ambient air and hydrogen at subatmospheric pressure, and a substrate heated to about 700 °C, branched nanostructures are deposited. We report three varieties of simple synthesis approaches to obtain hierarchical homo- and heterogeneous nanocacti. Furthermore, by using catalyst nanoparticles site-selection for the growth is demonstrated. The atomic, morphological and crystallographic compositions of the nanocacti are determined using a combination of electron microscopy techniques, energy-dispersive X-ray spectroscopy and electron diffraction. - Highlights: • Continuous upscalable hot-wire CVD of 3D hierarchical nanocacti • Controllable deposition of homo- and heterogeneous WO{sub 3−x}/WO{sub 3−y} nanocacti • Introduction of three synthesis routes comprising oxidation, reduction and re-oxidation processes • Growth of periodic arrays of hetero- and homogeneous hierarchical 3D nanocacti.

  4. Effect of solution chemistry on the characteristics of hydrothermally grown WO_3 for electroactive applications

    International Nuclear Information System (INIS)

    Christou, K.; Louloudakis, D.; Vernardou, D.; Savvakis, C.; Katsarakis, N.; Koudoumas, E.; Kiriakidis, G.

    2015-01-01

    Hydrothermally grown tungsten trioxide coatings were prepared at 95 °C using different metal sulfates. Morphology of the oxides was altered from grains to flower- and urchin-like structures using potassium sulfate, sodium sulfate and lithium sulfate, respectively. The flower-like structures presented the highest deintercalated charge, 35 mC cm"−"2 with time response of 96 s. In addition, they indicated a charge transfer resistance across the tungsten trioxide–electrolyte interface of 752 Ω. These outcomes imply that they are promising candidates for electroactive applications. - Highlights: • Hydrothermally grown WO_3 coatings with controlled properties. • The choice of metal sulfate is important in determining their properties. • Flower-like hexagonal WO_3 structures for electroactive applications.

  5. Oxygen vacancy induces self-doping effect and metalloid LSPR in non-stoichiometric tungsten suboxide synergistically contributing to the enhanced photoelectrocatalytic performance of WO3-x/TiO2-x heterojunction.

    Science.gov (United States)

    Huang, Weicheng; Wang, Jinxin; Bian, Lang; Zhao, Chaoyue; Liu, Danqing; Guo, Chongshen; Yang, Bin; Cao, Wenwu

    2018-06-27

    A WO3-x/TiO2-x nanotube array (NTA) heterojunction photoanode was strategically designed to improve photoelectrocatalytic (PEC) performance by establishing a synergistic vacancy-induced self-doping effect and localized surface plasmon resonance (LSPR) effect of metalloid non-stoichiometric tungsten suboxide. The WO3-x/TiO2-x NTA heterojunction photoanode was synthesized through a successive process of anodic oxidation to form TiO2 nanotube arrays, magnetron sputtering to deposit metalloid WO3-x, and post-hydrogen reduction to engender oxygen vacancy in TiO2-x as well as crystallization. On the merits of such a synergistic effect, WO3-x/TiO2-x shows higher light-harvesting ability, stronger photocurrent response, and resultant improved photoelectrocatalytic performance than the contrast of WO3-x/TiO2, WO3/TiO2 and TiO2, confirming the importance of oxygen vacancies in improving PEC performance. Theoretical calculation based on density functional theory was applied to investigate the electronic structural features of samples and reveal how the oxygen vacancy determines the optical property. The carrier density tuning mechanism and charge transfer model were considered to be associated with the synergistic effect of self-doping and metalloid LSPR effect in the WO3-x/TiO2-x NTA.

  6. Facile Hydrogen Evolution Reaction on WO3Nanorods

    Directory of Open Access Journals (Sweden)

    Rajeswari Janarthanan

    2007-01-01

    Full Text Available AbstractTungsten trioxide nanorods have been generated by the thermal decomposition (450 °C of tetrabutylammonium decatungstate. The synthesized tungsten trioxide (WO3 nanorods have been characterized by XRD, Raman, SEM, TEM, HRTEM and cyclic voltammetry. High resolution transmission electron microscopy and X-ray diffraction analysis showed that the synthesized WO3nanorods are crystalline in nature with monoclinic structure. The electrochemical experiments showed that they constitute a better electrocatalytic system for hydrogen evolution reaction in acid medium compared to their bulk counterpart.

  7. Investigation of the optical property and structure of WO3 thin films with different sputtering depositions

    Science.gov (United States)

    Chen, Hsi-Chao; Jan, Der-Jun; Chen, Chien-Han; Huang, Kuo-Ting; Lo, Yen-Ming; Chen, Sheng-Hui

    2011-09-01

    The purpose of this research was to compare the optical properties and structure of tungsten oxide (WO3) thin films that was deposited by different sputtering depositions. WO3 thin films deposited by two different depositions of direct current (DC) magnetron sputtering and pulsed DC sputtering. A 99.95% WO3 target was used as the starting material for these depositions. These WO3 thin films were deposited on the ITO glass, PET and silicon substrate by different ratios of oxygen and argon. A shadow moiré interferometer would be introduced to measure the residual stress for PET substrate. RF magnetron sputtering had the large residual stress than the other's depositions. A Raman spectrum could exhibit the phase of oxidation of WO3 thin film by different depositions. At the ratio of oxygen and argon was about 1:1, and the WO3 thin films had the best oxidation. However, it was important at the change of the transmittance (ΔT = Tbleached - Tcolored) between the coloring and bleaching for the smart window. Therefore, we also found the WO3 thin films had the large variation of transmittance between the coloring and bleaching at the gas ratios of oxygen and argon of 1:1.

  8. Electrodeposition of metallic tungsten coating from binary oxide molten salt on low activation steel substrate

    International Nuclear Information System (INIS)

    Liu, Y.H.; Zhang, Y.C.; Jiang, F.; Fu, B.J.; Sun, N.B.

    2013-01-01

    Tungsten is considered a promising plasma facing armor material for future fusion devices. An electrodeposited metallic tungsten coating from Na 2 WO 4 –WO 3 binary oxide molten salt on low activation steel (LAS) substrate was investigated in this paper. Tungsten coatings were deposited under various pulsed currents conditions at 1173 K in atmosphere. Cathodic current density and pulsed duty cycle were investigated for pulsed current electrolysis. The crystal structure and microstructure of tungsten coatings were characterized by X-ray diffractometry, scanning electron microscopy, and energy X-ray dispersive analysis techniques. The results indicated that pulsed current density and duty cycle significantly influence tungsten nucleation and electro-crystallization phenomena. The average grain size of the coating becomes much larger with increasing cathodic current density, which demonstrates that appropriate high cathodic current density can accelerate the growth of grains on the surface of the substrate. The micro-hardness of tungsten coatings increases with the increasing thickness of coatings; the maximum micro-hardness is 482 HV. The prepared tungsten coatings have a smooth surface, a porosity of less than 1%, and an oxygen content of 0.024 wt%

  9. Electrodeposition of metallic tungsten coating from binary oxide molten salt on low activation steel substrate

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Y. H. [School of Materials Science and Engineering, University of Science and Technology BeiJing, Beijing (China); State Nuclear Power Research Institute, Xicheng District, Beijing (China); Zhang, Y.C., E-mail: zycustb@163.com [School of Materials Science and Engineering, University of Science and Technology BeiJing, Beijing (China); Jiang, F.; Fu, B. J.; Sun, N. B. [School of Materials Science and Engineering, University of Science and Technology BeiJing, Beijing (China)

    2013-11-15

    Tungsten is considered a promising plasma facing armor material for future fusion devices. An electrodeposited metallic tungsten coating from Na{sub 2}WO{sub 4}–WO{sub 3} binary oxide molten salt on low activation steel (LAS) substrate was investigated in this paper. Tungsten coatings were deposited under various pulsed currents conditions at 1173 K in atmosphere. Cathodic current density and pulsed duty cycle were investigated for pulsed current electrolysis. The crystal structure and microstructure of tungsten coatings were characterized by X-ray diffractometry, scanning electron microscopy, and energy X-ray dispersive analysis techniques. The results indicated that pulsed current density and duty cycle significantly influence tungsten nucleation and electro-crystallization phenomena. The average grain size of the coating becomes much larger with increasing cathodic current density, which demonstrates that appropriate high cathodic current density can accelerate the growth of grains on the surface of the substrate. The micro-hardness of tungsten coatings increases with the increasing thickness of coatings; the maximum micro-hardness is 482 HV. The prepared tungsten coatings have a smooth surface, a porosity of less than 1%, and an oxygen content of 0.024 wt%.

  10. Synthesis and characterization of WO3 nanostructures prepared by an aged-hydrothermal method

    International Nuclear Information System (INIS)

    Huirache-Acuna, R.; Paraguay-Delgado, F.; Albiter, M.A.; Lara-Romero, J.; Martinez-Sanchez, R.

    2009-01-01

    Nanostructures of tungsten trioxide (WO 3 ) have been successfully synthesized by using an aged route at low temperature (60 deg. C) followed by a hydrothermal method at 200 deg. C for 48 h under well controlled conditions. The material was studied by X-ray diffraction (XRD), scanning electron microscopy (SEM) and Energy Dispersive Spectroscopy (EDS), transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). Specific Surface Area (S BET ) were measured by using the BET method. The lengths of the WO 3 nanostructures obtained are between 30 and 200 nm and their diameters are from 20 to 70 nm. The growth direction of the tungsten oxide nanostructures was determined along [010] axis with an inter-planar distance of 0.38 nm.

  11. Mesoporous WN/WO3-Composite Nanosheets for the Chemiresistive Detection of NO2 at Room Temperature

    OpenAIRE

    Fengdong Qu; Bo He; Rohiverth Guarecuco; Minghui Yang

    2016-01-01

    Composite materials, which can optimally use the advantages of different materials, have been studied extensively. Herein, hybrid tungsten nitride and oxide (WN/WO3) composites were prepared through a simple aqueous solution route followed by nitriding in NH3, for application as novel sensing materials. We found that the introduction of WN can improve the electrical properties of the composites, thus improving the gas sensing properties of the composites when compared with bare WO3. The highe...

  12. Preparation of layered graphene and tungsten oxide hybrids for enhanced performance supercapacitors.

    Science.gov (United States)

    Xing, Ling-Li; Huang, Ke-Jing; Fang, Lin-Xia

    2016-11-01

    Tungsten oxide (WO 3 ), which was originally poor in capacitive performance, is made into an excellent electrode material for supercapacitors by dispersing it on graphene (Gr). The obtained Gr-WO 3 hybrids are characterized by X-ray diffraction, Raman spectroscopy, high-resolution transmission electron microscopy and scanning electron microscopy techniques, and evaluated as electrode materials for high-performance supercapacitors by cyclic voltammetry, galvanostatic charge-discharge curves and electrochemical impedance spectroscopy. A great improvement in specific capacitance is achieved with the present hybrids, from 255 F g -1 for WO 3 nanoparticles to 580 F g -1 for Gr-WO 3 hybrids (scanned at 1 A g -1 in 2 M KOH over a potential window of 0 to 0.45 V). The Gr-WO 3 hybrid exhibits an excellent high rate capability and good cycling stability with more than 92% capacitance retention over 1000 cycles at a current density of 5 A g -1 . The enhancement in supercapacitor performance of Gr-WO 3 is not only attributed to its unique nanostructure with large specific surface area, but also its excellent electro-conductivity, which facilitates efficient charge transport and promotes electrolyte diffusion. As a whole, this work indicates that Gr-WO 3 hybrids are a promising electrode material for high-performance supercapacitors.

  13. One-step inkjet printing of tungsten oxide-poly(3,4-ethylenedioxythiophene):polystyrene sulphonate hybrid film and its applications in electrochromic devices

    Energy Technology Data Exchange (ETDEWEB)

    Nguyen, Thi-Thuy-Nga, E-mail: thuysnga@gmail.com; Chan, Chih-Yu; He, Ju-Liang

    2016-03-31

    Hybrid film comprised tungsten oxide and poly (3,4-ethylenedioxythiophene):polystyrene sulphonate (WO{sub 3}–PEDOT:PSS) was developed by applying one-step inkjet printing from an office inkjet printer. The WO{sub 3} nanoparticles were synthesized from commercial crystalline WO{sub 3} powder through a wet ball-milling process, which is a simple, environmentally friendly, and cost-effective method of using water as a green solvent and low-energy milling. The WO{sub 3}–PEDOT:PSS inkjet ink was prepared by dispersing the as-milled WO{sub 3} and PEDOT:PSS in n-propanol and deionized water. The inkjet-printed WO{sub 3}–PEDOT:PSS thin films show marked improvements of cathodic electrochromism over WO{sub 3} films: the transmittance change of 20% at 550 nm (visible region) and 35% at 900 nm (infrared region) along with the response time of 5.67/0.30 s in their colored/bleached state, and the electrochromic coloration efficiency of 27.86 cm{sup 2}/C at 550 nm and 69.64 cm{sup 2}/C at 900 nm. - Highlights: • WO{sub 3} nanoparticles were synthesized by milling commercial crystalline WO{sub 3}. • Wet ball-milling was carried out by using water as a green solvent and low energy. • WO{sub 3}–PEDOT:PSS hybrid ink was simply prepared by adding n-propanol and DI water. • WO{sub 3}–PEDOT:PSS hybrid films were inkjet-printed via an office inkjet printer. • WO{sub 3}–PEDOT:PSS films show better electrochromic performances than WO{sub 3} films.

  14. Structure of tungsten electrodeposited from oxide chloride-fluoride molten salts

    International Nuclear Information System (INIS)

    Pavlovskij, V.A.; Reznichenko, V.A.

    1998-01-01

    Investigation results on the influence of electrolysis parameters and electrolyte composition on tungsten cathode deposit structure are presented. The electrolysis was performed in NaCl-NaF-WO 3 molten salts using tungsten and tungsten coated molybdenum cathodes. Morphological and metallographic studies of tungsten crystals were carrier out. Tungsten deposits were obtained in the form of crystalline conglomerates, sponge and high dispersity powder

  15. Room temperature NO2 gas sensing of Au-loaded tungsten oxide nanowires/porous silicon hybrid structure

    International Nuclear Information System (INIS)

    Wang Deng-Feng; Liang Ji-Ran; Li Chang-Qing; Yan Wen-Jun; Hu Ming

    2016-01-01

    In this work, we report an enhanced nitrogen dioxide (NO 2 ) gas sensor based on tungsten oxide (WO 3 ) nanowires/porous silicon (PS) decorated with gold (Au) nanoparticles. Au-loaded WO 3 nanowires with diameters of 10 nm–25 nm and lengths of 300 nm–500 nm are fabricated by the sputtering method on a porous silicon substrate. The high-resolution transmission electron microscopy (HRTEM) micrographs show that Au nanoparticles are uniformly distributed on the surfaces of WO 3 nanowires. The effect of the Au nanoparticles on the NO 2 -sensing performance of WO 3 nanowires/porous silicon is investigated over a low concentration range of 0.2 ppm–5 ppm of NO 2 at room temperature (25 °C). It is found that the 10-Å Au-loaded WO 3 nanowires/porous silicon-based sensor possesses the highest gas response characteristic. The underlying mechanism of the enhanced sensing properties of the Au-loaded WO 3 nanowires/porous silicon is also discussed. (paper)

  16. Tungsten oxide coatings deposited by plasma spray using powder and solution precursor for detection of nitrogen dioxide gas

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Chao, E-mail: zhangc@yzu.edu.cn [College of Mechanical Engineering, Yangzhou University, Yangzhou 225127 (China); Wang, Jie [College of Mechanical Engineering, Yangzhou University, Yangzhou 225127 (China); Geng, Xin [College of Mechanical Engineering, Yangzhou University, Yangzhou 225127 (China); College of Chemistry and Chemical Engineering, Yangzhou University, Yangzhou 225002 (China)

    2016-05-25

    Increasing attention has been paid on preparation methods for resistive-type gas sensors based on semiconductor metal oxides. In this work, tungsten oxide (WO{sub 3}) coatings were prepared on alumina substrates and used as gas sensitive layers. The coatings were deposited by atmospheric plasma spray using powder, solution precursor, or a combination of both. Tungsten oxide powder through a powder port and ammonium tungstate aqueous solution through a liquid port were injected into plasma stream respectively or together to deposit WO{sub 3} coatings. Phase structures in the coatings were characterized by X-ray diffraction analyzer. The field-emission scanning electron microscopy images confirmed that the coatings were in microstructure, nanostructure or micro-nanostructure. The sensing properties of the sensors based on the coatings exposed to 1 ppm nitrogen dioxide gas were characterized in a home-made instrument. Sensing properties of the coatings were compared and discussed. The influences of gas humidity and working temperature on the sensor responses were further studied. - Highlights: • Porous gas sensitive coatings were deposited by plasma spray using powder and solution precursor. • Crystallized WO{sub 3} were obtained through hybrid plasma spray plus a pre-conditioned step. • Plasma power had an important influence on coating microstructure. • The particle size of atmospheric plasma-sprayed microstructured coating was stable. • Solution precursor plasma-sprayed WO{sub 3} coatings had nanostructure and showed good responses to 1 ppm NO{sub 2}.

  17. The Risk Evaluation of Tungsten Oxide Nanoparticles in Cultured Rat Liver Cells for Its Safe Applications in Nanotechnology

    Directory of Open Access Journals (Sweden)

    Hasan Turkez

    2014-08-01

    Full Text Available Tungsten (VI oxide (WO3 nanoparticles (NPs are used for many industrial purposes in everyday life. However, their effects on human health have not been sufficiently evaluated. Therefore, the present study was designed to investigate the toxicity potentials of various concentrations (0 to 1000 ppm of WO3NPs (<100 nm particle size in cultured primary rat hepatocytes. The results of cell viability assay showed that the higher concentrations of dispersed WO3 NPs (300, 500 and 1000 ppm caused significant (p<0.05 decreases of cell viability. Also, dose dependent negative alterations were observed in oxidative status and antioxidant capacity levels after the application of WO3 in cultured rat primary hepatocytes. The results of genotoxicity tests revealed that these NPs did not cause significant increases of micronucleated hepatocytes (MNHEPs but increased 8-oxo-2-deoxyguanosine (8-OH-dG levels as compared to the control culture.

  18. Crystalline mesoporous tungsten oxide nanoplate monoliths synthesized by directed soft template method for highly sensitive NO2 gas sensor applications

    International Nuclear Information System (INIS)

    Hoa, Nguyen Duc; Duy, Nguyen Van; Hieu, Nguyen Van

    2013-01-01

    Graphical abstract: Display Omitted Highlights: ► Mesoporous WO 3 nanoplate monoliths were obtained by direct templating synthesis. ► Enable effective accession of the analytic molecules for the sensor applications. ► The WO 3 sensor exhibited a high performance to NO 2 gas at low temperature. -- Abstract: Controllable synthesis of nanostructured metal oxide semiconductors with nanocrystalline size, porous structure, and large specific surface area is one of the key issues for effective gas sensor applications. In this study, crystalline mesoporous tungsten oxide nanoplate-like monoliths with high specific surface areas were obtained through instant direct-templating synthesis for highly sensitive nitrogen dioxide (NO 2 ) sensor applications. The copolymer soft template was converted into a solid carbon framework by heat treatment in an inert gas prior to calcinations in air to sustain the mesoporous structure of tungsten oxide. The multidirectional mesoporous structures of tungsten oxide with small crystalline size, large specific surface area, and superior physical characteristics enabled the rapid and effective accession of analytic gas molecules. As a result, the sensor response was enhanced and the response and recovery times were reduced, in which the mesoporous tungsten oxide based gas sensor exhibited a superior response of 21,155% to 5 ppm NO 2 . In addition, the developed sensor exhibited selective detection of low NO 2 concentration in ammonia and ethanol at a low temperature of approximately 150 °C.

  19. A study of the switching mechanism and electrode material of fully CMOS compatible tungsten oxide ReRAM

    Science.gov (United States)

    Chien, W. C.; Chen, Y. C.; Lai, E. K.; Lee, F. M.; Lin, Y. Y.; Chuang, Alfred T. H.; Chang, K. P.; Yao, Y. D.; Chou, T. H.; Lin, H. M.; Lee, M. H.; Shih, Y. H.; Hsieh, K. Y.; Lu, Chih-Yuan

    2011-03-01

    Tungsten oxide (WO X ) resistive memory (ReRAM), a two-terminal CMOS compatible nonvolatile memory, has shown promise to surpass the existing flash memory in terms of scalability, switching speed, and potential for 3D stacking. The memory layer, WO X , can be easily fabricated by down-stream plasma oxidation (DSPO) or rapid thermal oxidation (RTO) of W plugs universally used in CMOS circuits. Results of conductive AFM (C-AFM) experiment suggest the switching mechanism is dominated by the REDOX (Reduction-oxidation) reaction—the creation of conducting filaments leads to a low resistance state and the rupturing of the filaments results in a high resistance state. Our experimental results show that the reactions happen at the TE/WO X interface. With this understanding in mind, we proposed two approaches to boost the memory performance: (i) using DSPO to treat the RTO WO X surface and (ii) using Pt TE, which forms a Schottky barrier with WO X . Both approaches, especially the latter, significantly reduce the forming current and enlarge the memory window.

  20. Preparation of Ba1-xSrxWO4 and Ba1-xCaxWO4 films on tungsten plate by mechanically assisted solution reaction at room temperature

    International Nuclear Information System (INIS)

    Rangappa, Dinesh; Fujiwara, Takeshi; Watanabe, Tomoaki; Yoshimura, Masahiro

    2008-01-01

    Preparation of the alkaline earth tungstate films such as Ba 1-x Sr x WO 4 and Ba 1-x Ca x WO 4 on the tungsten substrate was studied with a simple solution process assisted with the ball rotation at room temperature. The solid solution formation and limitations, the effect of oxidizing agent H 2 O 2 and alkaline earth ions concentration on the dissolution of W substrate and the growth of Ba 1-x Sr x WO 4 and Ba 1-x Ca x WO 4 films were studied in detail. The ball rotation assistance plays a very important role to enhance the dissolution of the W substrate and mass transport of the reactant species such as alkaline earth ions and WO 4 2- ions onto the solid/solution interface region, where precipitation occurs. Therefore, the rate of film formation was accelerated by the ball rotation assistance to the reaction system. Ba-rich Ba 1-x Sr x WO 4 and Ba 1-x Ca x WO 4 films were formed without high energy or high temperature treatment

  1. Tungsten oxides. I. Effects of oxygen vacancies and doping on electronic and optical properties of different phases of WO3

    Science.gov (United States)

    Migas, D. B.; Shaposhnikov, V. L.; Rodin, V. N.; Borisenko, V. E.

    2010-11-01

    In this part we present results of our ab initio calculations indicating that dispersion of the bands near the gap region for different phases of WO3 (namely, ɛ-WO3, δ-WO3, γ-WO3, β-WO3, orth-WO3, α-WO3, and hex-WO3) is rather close. The rapid increase in the absorption coefficient starts at the lower energy range for α-WO3 and hex-WO3 than for the other phases in accordance with the calculated band gaps. An oxygen vacancy has turned out to decrease the gap by 0.50 eV and to shift the absorption coefficient to the lower energy range in the room temperature γ-WO3 phase. We have also traced changes caused by molybdenum and sulfur doping of γ-WO3. Only sulfur doped γ-WO3 has been revealed to display the formation of the impurity band along with a sizable reduction in the gap and the shift in the absorption coefficient to the lower energy range.

  2. Formation of tungsten oxide nanowires by ion irradiation and vacuum annealing

    Science.gov (United States)

    Zheng, Xu-Dong; Ren, Feng; Wu, Heng-Yi; Qin, Wen-Jing; Jiang, Chang-Zhong

    2018-04-01

    Here we reported the fabrication of tungsten oxide (WO3-x ) nanowires by Ar+ ion irradiation of WO3 thin films followed by annealing in vacuum. The nanowire length increases with increasing irradiation fluence and with decreasing ion energy. We propose that the stress-driven diffusion of the irradiation-induced W interstitial atoms is responsible for the formation of the nanowires. Comparing to the pristine film, the fabricated nanowire film shows a 106-fold enhancement in electrical conductivity, resulting from the high-density irradiation-induced vacancies on the oxygen sublattice. The nanostructure exhibits largely enhanced surface-enhanced Raman scattering effect due to the oxygen vacancy. Thus, ion irradiation provides a powerful approach for fabricating and tailoring the surface nanostructures of semiconductors.

  3. A photocatalytic approach in micro arc oxidation of WO3-TiO2 nano porous semiconductors under pulse current

    International Nuclear Information System (INIS)

    Bayati, M.R.; Golestani-Fard, F.; Moshfegh, A.Z.; Molaei, R.

    2011-01-01

    Graphical abstract: WO3-TiO2 layers were fabricated via microarc oxidation process and effect of the electrical current type on their photocatalytic performance under UV and visible illuminations was investigated. Highlights: → WO3-TiO2 layers were grown by MAO under pulse current for the first time. → Effect of the frequency and duty cycle on properties of the layers was studied. → A correlation between catalytic performance and growth conditions was proposed. - Abstract: Since ultraviolet (UV) irradiation cannot be applied for a long time in practical applications, it is necessary to develop a narrow band gap photocatalyst to decompose environmental pollutants under visible irradiation. In this research, (WO 3 ) x -(TiO 2 ) 1-x nano-porous layers were fabricated by micro arc oxidation (MAO) and influence of the electrical current type on their physical and chemical properties was investigated. Morphological studies, performed by SEM technique, revealed that pore size and roughness decreased with the frequency and increased with the duty cycle. The pulse-grown layers had a finer structure when compared to those fabricated under direct current. XRD and XPS results showed that the layers consisted of anatase, rutile, and tungsten oxide phases. Applying pulse current resulted in higher anatase relative contents. Band gap energies of the MAO-grown TiO 2 and WO 3 -TiO 2 layers were respectively measured as 3.14 and 2.96 eV. The layers fabricated under pulse current exhibited higher photoactivity under ultraviolet and visible illuminations as compared to the layers grown under direct current. Methylene blue (MB) was used as a model material to examine photocatalytic performance of the layers. Maximum MB-photodegradation reaction rate constants over the pulse-synthesized WO 3 -TiO 2 layers were measured as 0.0269 and 0.0129 min -1 for ultraviolet and visible irradiations. For layers grown under direct current, the rate constants were lower, i.e. 0.0228 and 0

  4. Low-Temperature Preparation of Tungsten Oxide Anode Buffer Layer via Ultrasonic Spray Pyrolysis Method for Large-Area Organic Solar Cells

    Directory of Open Access Journals (Sweden)

    Ran Ji

    2017-07-01

    Full Text Available Tungsten oxide (WO3 is prepared by a low-temperature ultrasonic spray pyrolysis method in air atmosphere, and it is used as an anode buffer layer (ABL for organic solar cells (OSCs. The properties of the WO3 transition metal oxide material as well as the mechanism of ultrasonic spray pyrolysis processes are investigated. The results show that the ultrasonic spray pyrolysized WO3 ABL exhibits low roughness, matched energy level, and high conductivity, which results in high charge transport efficiency and suppressive recombination in OSCs. As a result, compared to the OSCs based on vacuum thermal evaporated WO3, a higher power conversion efficiency of 3.63% is reached with low-temperature ultrasonic spray pyrolysized WO3 ABL. Furthermore, the mostly spray-coated OSCs with large area was fabricated, which has a power conversion efficiency of ~1%. This work significantly enhances our understanding of the preparation and application of low temperature-processed WO3, and highlights the potential of large area, all spray coated OSCs for sustainable commercial fabrication.

  5. Dataset on electro-optically tunable smart-supercapacitors based on oxygen-excess nanograin tungsten oxide thin film

    Directory of Open Access Journals (Sweden)

    Akbar I. Inamdar

    2017-10-01

    Full Text Available The dataset presented here is related to the research article entitled “Highly Efficient Electro-optically Tunable Smart-supercapacitors Using an Oxygen-excess Nanograin Tungsten Oxide Thin Film” (Akbar et al., 2017 [9] where we have presented a nanograin WO3 film as a bifunctional electrode for smart supercapacitor devices. In this article we provide additional information concerning nanograin tungsten oxide thin films such as atomic force microscopy, Raman spectroscopy, and X-ray diffraction spectroscopy. Moreover, their electrochemical properties such as cyclic voltammetry, electrochemical supercapacitor properties, and electrochromic properties including coloration efficiency, optical modulation and electrochemical impedance spectroscopy are presented.

  6. Tungsten oxide thin films grown by thermal evaporation with high resistance to leaching

    Energy Technology Data Exchange (ETDEWEB)

    Correa, Diogo S. [Universidade Federal de Pelotas (UFPel), RS (Brazil). Centro de Ciencias Quimicas, Farmaceuticas e de Alimentos; Pazinato, Julia C.O.; Freitas, Mauricio A. de; Radtke, Claudio; Garcia, Irene T.S., E-mail: irene@iq.ufrgs.br [Universidade Federal do Rio Grande do Sul (UFRGS), Porto Alegre, RS (Brazil). Instituto de Quimica; Dorneles, Lucio S. [Universidade Federal de Santa Maria (UFSM), RS (Brazil). Centro de Ciencias Naturais e Exatas

    2014-05-15

    Tungsten oxides show different stoichiometries, crystal lattices and morphologies. These characteristics are important mainly when they are used as photocatalysts. In this work tungsten oxide thin films were obtained by thermal evaporation on (100) silicon substrates covered with gold and heated at 350 and 600 °C, with different deposition times. The stoichiometry of the films, morphology, crystal structure and resistance to leaching were characterized through X-ray photoelectron spectroscopy, micro-Raman spectroscopy, scanning and transmission electron microscopy, X-ray diffractometry, Rutherford backscattering spectrometry and O{sup 16} (α,α')O{sup 16} resonant nuclear reaction. Films obtained at higher temperatures show well-defined spherical nanometric structure; they are composed of WO{sub 3.1} and the presence of hydrated tungsten oxide was also observed. The major crystal structure observed is the hexagonal. Thin films obtained through thermal evaporation present resistance to leaching in aqueous media and excellent performance as photocatalysts, evaluated through the degradation of the methyl orange dye. (author)

  7. Investigation of water content in electrolyte solution on electrochromic properties of WO3 thin Films

    Directory of Open Access Journals (Sweden)

    Zahra Abadi

    2017-05-01

    Full Text Available Tungsten oxide thin films were prepared by a cathodic electrodeposition method at -0.450 mV in order to investigate how water content affects their electrochromic properties. FESEM images exhibit that WO3 thin films consist of 65 nm uniform grains. Thin Films were electrochemically investigated in 0.1M LiClO4 in propylene carbonate electrolyte with and without 5vol% water content by cyclic voltammetry and chronoamperometry. The results indicate that tungsten oxide thin films exhibit faster switching time between coloration and bleaching states and also higher coloration efficiency in hydrated electrolyte.  

  8. An ultraviolet photodetector fabricated from WO3 nanodiscs/reduced graphene oxide composite material

    International Nuclear Information System (INIS)

    Shao Dali; Sawyer, Shayla; Yu Mingpeng; Lian Jie

    2013-01-01

    A high sensitivity, fast ultraviolet (UV) photodetector was fabricated from WO 3 nanodiscs (NDs)/reduced graphene oxide (RGO) composite material. The WO 3 NDs/reduced GO composite material was synthesized using a facile three-step synthesis procedure. First, the Na 2 WO 4 /GO precursor was synthesized by homogeneous precipitation. Second, the Na 2 WO 4 /GO precursor was transformed into H 2 WO 4 /GO composites by acidification. Finally, the H 2 WO 4 /GO composites were reduced to WO 3 NDs/RGO via a hydrothermal reduction process. The UV photodetector showed a fast transient response and high responsivity, which are attributed to the improved carrier transport and collection efficiency through graphene. The excellent material properties of the WO 3 NDs/RGO composite demonstrated in this work may open up new possibilities for using WO 3 NDs/RGO for future optoelectronic applications. (paper)

  9. Influence of disordered morphology on electrochromic stability of WO{sub 3}/PPy

    Energy Technology Data Exchange (ETDEWEB)

    Gaikwad, Digambar K. [D. Y. Patil College of Engineering & Technology, Kasaba Bawada, Kolhapur, 416006, Maharashtra (India); Mali, Sawanta S.; Hong, Chang K. [Polymer Energy Materials Laboratory, Department of Advanced Chemical Engineering, Chonnam National University, Gwangju, 500-757 (Korea, Republic of); Kadam, Anamika V., E-mail: anamikasonavane@rediff.com [D. Y. Patil College of Engineering & Technology, Kasaba Bawada, Kolhapur, 416006, Maharashtra (India); D.Y. Patil Medical University, Kasaba Bawada, Kolhapur, 416006, Maharashtra (India)

    2016-06-05

    Tungsten oxide (WO{sub 3}) films are critical for smart windows because of their capacity of varying the throughput of visible light and solar energy. This study highlights the evolution of structural and morphological changes of electrodeposited WO{sub 3} thin films coated with polypyrrole (PPy) by using chemical bath deposition. The structural and surface properties of WO{sub 3} thin films were studied using X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy, and transmission electron microscopy. The electrochemical stability was inspected using repetitive cyclic voltammetry (CV) cycles for each sample in LiClO{sub 4}-PC electrolyte for prolonged periods. The results showed an improvement in the electrochemical stability after the CV study. - Graphical abstract: Mechanism: A schematic of the mechanism is proposed in above fig. The mechanism is based on three step process: (i) WO{sub 3} coated on ITO by electrodeposition followed by thermal treatment. It produces ordered nanoarrayed morphology. (ii) A second step involving deposition of PPy by chemical bath deposition on ITO. It possesses globular morphology. (iii) When PPy coated on WO{sub 3}, PPy applies shearing force on WO{sub 3} and produces disordered nanoarrayed morphology. - Highlights: • Nanoarrayed WO{sub 3}/PPy composite was synthesized. • Interplanar spacing enhances due to PPy coating. • PPy applies shearing force on WO{sub 3} produces disordered morphology. • Nanocomposite showed high stability in LiClO{sub 4}-PC.

  10. Crystalline mesoporous tungsten oxide nanoplate monoliths synthesized by directed soft template method for highly sensitive NO{sub 2} gas sensor applications

    Energy Technology Data Exchange (ETDEWEB)

    Hoa, Nguyen Duc, E-mail: ndhoa@itims.edu.vn [International Training Institute for Materials Science (ITIMS), Hanoi University of Science and Technology (HUST) (Viet Nam); Duy, Nguyen Van [International Training Institute for Materials Science (ITIMS), Hanoi University of Science and Technology (HUST) (Viet Nam); Hieu, Nguyen Van, E-mail: hieu@itims.edu.vn [International Training Institute for Materials Science (ITIMS), Hanoi University of Science and Technology (HUST) (Viet Nam)

    2013-02-15

    Graphical abstract: Display Omitted Highlights: ► Mesoporous WO{sub 3} nanoplate monoliths were obtained by direct templating synthesis. ► Enable effective accession of the analytic molecules for the sensor applications. ► The WO{sub 3} sensor exhibited a high performance to NO{sub 2} gas at low temperature. -- Abstract: Controllable synthesis of nanostructured metal oxide semiconductors with nanocrystalline size, porous structure, and large specific surface area is one of the key issues for effective gas sensor applications. In this study, crystalline mesoporous tungsten oxide nanoplate-like monoliths with high specific surface areas were obtained through instant direct-templating synthesis for highly sensitive nitrogen dioxide (NO{sub 2}) sensor applications. The copolymer soft template was converted into a solid carbon framework by heat treatment in an inert gas prior to calcinations in air to sustain the mesoporous structure of tungsten oxide. The multidirectional mesoporous structures of tungsten oxide with small crystalline size, large specific surface area, and superior physical characteristics enabled the rapid and effective accession of analytic gas molecules. As a result, the sensor response was enhanced and the response and recovery times were reduced, in which the mesoporous tungsten oxide based gas sensor exhibited a superior response of 21,155% to 5 ppm NO{sub 2}. In addition, the developed sensor exhibited selective detection of low NO{sub 2} concentration in ammonia and ethanol at a low temperature of approximately 150 °C.

  11. Closed-cage tungsten oxide clusters in the gas phase.

    Science.gov (United States)

    Singh, D M David Jeba; Pradeep, T; Thirumoorthy, Krishnan; Balasubramanian, Krishnan

    2010-05-06

    During the course of a study on the clustering of W-Se and W-S mixtures in the gas phase using laser desorption ionization (LDI) mass spectrometry, we observed several anionic W-O clusters. Three distinct species, W(6)O(19)(-), W(13)O(29)(-), and W(14)O(32)(-), stand out as intense peaks in the regular mass spectral pattern of tungsten oxide clusters suggesting unusual stabilities for them. Moreover, these clusters do not fragment in the postsource decay analysis. While trying to understand the precursor material, which produced these clusters, we found the presence of nanoscale forms of tungsten oxide. The structure and thermodynamic parameters of tungsten clusters have been explored using relativistic quantum chemical methods. Our computed results of atomization energy are consistent with the observed LDI mass spectra. The computational results suggest that the clusters observed have closed-cage structure. These distinct W(13) and W(14) clusters were observed for the first time in the gas phase.

  12. Morphologically different WO3 nanocrystals in photoelectrochemical water oxidation

    International Nuclear Information System (INIS)

    Biswas, Soumya Kanti; Baeg, Jin-Ook; Moon, Sang-Jin; Kong, Ki-jeong; So, Won-Wook

    2012-01-01

    Different morphologies of WO 3 nanocrystals such as nanorods and nanoplates have been obtained under hydrothermal conditions using ammonium metatungstate as the precursor in presence of different organic acids such as citric, oxalic, and tartaric acid in the reaction medium. Detailed characterization of the crystal structure, particle morphology, and optical band gap of the synthesized powders have been done by X-ray diffraction, transmission electron microscopy, scanning electron microscopy and solid-state UV–visible spectroscopy study. The as-synthesized materials are WO 3 hydrates with orthorhombic phase which transform to the hexagonal WO 3 through dehydration upon heating at 350 °C. The resultant products are crystalline with nanoscale dimensions. Finally, the photoactivity of the synthesized materials annealed at 500 °C has been compared employing in photoelectrochemical water oxidation under the illumination of AM 1.5G simulated solar light (100 mWcm −2 ). The photocurrent measurements upon irradiation of light exhibit obvious photocatalytic activity with a photocurrent of about 0.77, 0.61, and 0.65 mAcm −2 for the WO 3 film derived with the oxalic acid, tartaric, and citric acid assisting agents, respectively, at 1.8 V versus Ag/AgCl electrode.

  13. Tungsten-based nanomaterials (WO{sub 3} & Bi{sub 2}WO{sub 6}): Modifications related to charge carrier transfer mechanisms and photocatalytic applications

    Energy Technology Data Exchange (ETDEWEB)

    Girish Kumar, S., E-mail: girichem@yahoo.co.in; Koteswara Rao, K.S.R., E-mail: raoksrk@gmail.com

    2015-11-15

    Graphical abstract: - Highlights: • Photocatalytic applications of WO{sub 3} and Bi{sub 2}WO{sub 6} based nanomaterial are reviewed. • Modifications to improve their performance are highlighted. • Charge carrier generation–separation–recombination is discussed. • Challenges and future prospects in this area are addressed. - Abstract: Heterogeneous photocatalysis is an ideal green energy technology for the purification of wastewater. Although titania dominates as the reference photocatalyst, its wide band gap is a bottleneck for extended utility. Thus, search for non-TiO{sub 2} based nanomaterials has become an active area of research in recent years. In this regard, visible light absorbing polycrystalline WO{sub 3} (2.4–2.8 eV) and Bi{sub 2}WO{sub 6} (2.8 eV) with versatile structure-electronic properties has gained considerable interest to promote the photocatalytic reactions. These materials are also explored in selective functional group transformation in organic reactions, because of low reduction and oxidation potential of WO{sub 3} CB and Bi{sub 2}WO{sub 6} VB, respectively. In this focused review, various strategies such as foreign ion doping, noble metal deposition and heterostructuring with other semiconductors designed for efficient photocatalysis is discussed. These modifications not only extend the optical response to longer wavelengths, but also prolong the life-time of the charge carriers and strengthen the photocatalyst stability. The changes in the surface-bulk properties and the charge carrier transfer dynamics associated with each modification correlating to the high activity are emphasized. The presence of oxidizing agents, surface modification with Cu{sup 2+} ions and synthesis of exposed facets to promote the degradation rate is highlighted. In depth study on these nanomaterials is likely to sustain interest in wastewater remediation and envisaged to signify in various green energy applications.

  14. Influence of variable tungsten valency on optical transmittance and radiation hardness of lead tungstate (PWO) scintillation crystals

    CERN Document Server

    Burachas, S; Makov, I; Saveliev, Yu; Ippolitov, M S; Man'ko, V; Nikulin, S P; Nyanin, A; Vasilev, A; Apanasenko, A; Tamulaitis, G

    2003-01-01

    A new approach to interpret the radiation hardness of PbWO//4 (PWO) scintillators is developed by revealing importance of the inclusions of tungsten oxides WO//3//-//x with variable valency. It is demonstrated that the influence of the ionizing radiation on PWO is, in many aspects, similar to the effect of the high-temperature annealing in oxygenless ambient. In both cases, a valency change of the tungsten oxides is initiated and results in induced absorption and, consequently, in crystal coloration. In the PWO crystals doped with L//2O//3 (L = Y, La, Gd), the radiation hardness and the optical properties are mainly affected by inclusions of W//1//-//yL//yO//3//- //x (0 less than x less than 0.3) instead of inclusions of WO//3//- //x prevailing in the undoped samples. It is demonstrated that the radiation-induced bleaching and the photochromic effect of PWO are caused by phase transitions in the inclusions of tungsten oxide. Thermodynamic conditions for the phase transitions are discussed and the optimal oxid...

  15. Coating of tips for electrochemical scanning tunneling microscopy by means of silicon, magnesium, and tungsten oxides

    Science.gov (United States)

    Salerno, Marco

    2010-09-01

    Different combinations of metal tips and oxide coatings have been tested for possible operation in electrochemical scanning tunneling microscopy. Silicon and magnesium oxides have been thermally evaporated onto gold and platinum-iridium tips, respectively. Two different thickness values have been explored for both materials, namely, 40 and 120 nm for silicon oxide and 20 and 60 nm for magnesium oxide. Alternatively, tungsten oxide has been grown on tungsten tips via electrochemical anodization. In the latter case, to seek optimal results we have varied the pH of the anodizing electrolyte between one and four. The oxide coated tips have been first inspected by means of scanning electron microscopy equipped with microanalysis to determine the morphological results of the coating. Second, the coated tips have been electrically characterized ex situ for stability in time by means of cyclic voltammetry in 1 M aqueous KCl supporting electrolyte, both bare and supplemented with K3[Fe(CN)6] complex at 10 mM concentration in milliQ water as an analyte. Only the tungsten oxide coated tungsten tips have shown stable electrical behavior in the electrolyte. For these tips, the uncoated metal area has been estimated from the electrical current levels, and they have been successfully tested by imaging a gold grating in situ, which provided stable results for several hours. The successful tungsten oxide coating obtained at pH=4 has been assigned to the WO3 form.

  16. Synthesis of tungsten oxide (W{sub 18}O{sub 49}) nanosheets utilizing EDTA salt by microwave irradiation method

    Energy Technology Data Exchange (ETDEWEB)

    Hariharan, V.; Parthibavarman, M. [Centre for Nanoscience and Technology, Department of Physics, Periyar University, Salem 636 011, Tamilnadu (India); Sekar, C., E-mail: Sekar2025@gmail.com [Centre for Nanoscience and Technology, Department of Physics, Periyar University, Salem 636 011, Tamilnadu (India); Department of Bioelectronics and Biosensors, Alagappa University, Karaikudi 630 003, Tamilnadu (India)

    2011-04-07

    Research highlights: > We have synthesized tungsten oxide (WO{sub 3-{delta}}) nanoparticles by microwave irradiation method for the first time using EDTA as surface modulator. The variation in stoichiometric oxygen content of the annealed samples clearly indicates the role of EDTA in reaction medium. The variation in oxygen content also modified the transparency of the end product confirming the change in optical conductivity. - Abstract: We report the synthesis of crystalline W{sub 18}O{sub 49} with nanosheet like morphology by low cost microwave irradiation method without employing hydrothermal process for the first time. Initially, WO{sub 3}.H{sub 2}O was synthesized using ethylenediaminetetraacetic acid (EDTA) as surface modulator. The product was annealed at 600 {sup o}C for 6 h in ambient atmosphere in order to obtain anhydrous tungsten oxide W{sub 18}O{sub 49}. Powder X-ray diffraction results confirmed the as prepared WO{sub 3}.H{sub 2}O to be orthorhombic and W{sub 18}O{sub 49} to be monoclinic phase, respectively. Transmission electron micrographs (TEM) revealed that the W{sub 18}O{sub 49} nanosheets have the average dimensions of the order of 250 nm in length and around 150 nm in width. UV-visible diffusion reflectance spectroscopic (DRS) studies revealed the band gap energies to be 3.28 and 3.47 eV for WO{sub 3}.H{sub 2}O and W{sub 18}O{sub 49} samples, respectively. The growth mechanism of two dimensional W{sub 18}O{sub 49} nanosheets is discussed.

  17. Characterization and Electrical Response to Humidity of Sintered Polymeric Electrospun Fibers of Vanadium Oxide-({TiO}_{{2}} /{WO}_{{3}} )

    Science.gov (United States)

    Araújo, E. S.; Libardi, J.; Faia, P. M.; de Oliveira, H. P.

    2018-02-01

    Metal oxide composites have attracted much consideration due to their promising applications in humidity sensors in response to the physical and chemical property modifications of the resulting materials. This work focused on the preparation, microstructural characterization and analysis of humidity-dependent electrical properties of undoped and vanadium oxide (V2O5)-doped titanium oxide/tungsten oxide (TiO2/WO3) sintered ceramic films obtained by electrospinning. The electrical properties were investigated by impedance spectroscopy (400 Hz-40 MHz) as a function of relative humidity (RH). The results revealed a typical transition in the transport mechanisms controlled by the appropriated doping level of V2O5, which introduces important advantages to RH detection due to the atomic substitution of titanium by vanadium atoms in highly doped structures. These aspects are directly related to the microstructure modification and structure fabrication procedure.

  18. Effects of micro-sized and nano-sized WO_3 on mass attenauation coefficients of concrete by using MCNPX code

    International Nuclear Information System (INIS)

    Tekin, H.O.; Singh, V.P.; Manici, T.

    2017-01-01

    In the present work the effect of tungsten oxide (WO_3) nanoparticles on mass attenauation coefficients of concrete has been investigated by using MCNPX (version 2.4.0). The validation of generated MCNPX simulation geometry has been provided by comparing the results with standard XCOM data for mass attenuation coefficients of concrete. A very good agreement between XCOM and MCNPX have been obtained. The validated geometry has been used for definition of nano-WO_3 and micro-WO_3 into concrete sample. The mass attenuation coefficients of pure concrete and WO_3 added concrete with micro-sized and nano-sized have been compared. It was observed that shielding properties of concrete doped with WO_3 increased. The results of mass attenauation coefficients also showed that the concrete doped with nano-WO_3 significanlty improve shielding properties than micro-WO_3. It can be concluded that addition of nano-sized particles can be considered as another mechanism to reduce radiation dose. - Highlights: • It was found that size of the WO_3 affected the mass attenuation coefficients of concrete in all photon energies.

  19. Combustion synthesized hierarchically porous WO{sub 3} for selective acetone sensing

    Energy Technology Data Exchange (ETDEWEB)

    Dong, Chengjun; Liu, Xu; Guan, Hongtao; Chen, Gang; Xiao, Xuechun [Department of Materials Science and Engineering, Yunnan University, 650091, Kunming (China); Djerdj, Igor [Ruđer Bošković Institute, Bijenička 54, 10000, Zagreb (Croatia); Wang, Yude, E-mail: ydwang@ynu.edu.cn [Department of Materials Science and Engineering, Yunnan University, 650091, Kunming (China); Yunnan Province Key Lab of Mico-Nano Materials and Technology, Yunnan University, 650091, Kunming (China)

    2016-12-01

    An easy, inexpensive combustion route was designed to synthesize hierarchically porous WO{sub 3}. The tungsten source was fresh peroxiotungstic acid by dissolving tungsten powder into hydrogen peroxide. To promote the combustion reaction, a combined fuel of both glycine and hydrazine hydrate was used. The microstructure was well-connected pores comprised of subunit nanoparticles. Upon exposing towards acetone gas, the porous WO{sub 3} based sensor exhibits high gas response, rapid response and recovery, and good selectivity in the range of 5–1000 ppm under working temperature of 300 °C. This excellent sensing performance was plausibly attributed to the porous morphology, which hence provides more active sites for the gas molecules' reaction. - Graphical abstract: Hierarchically porous WO{sub 3} synthesized by combustion process exhibits high gas response, rapid response and recovery, and excellent selectivity for acetone, making it to be promising candidates for practical detectors for acetone. - Highlights: • Hierarchically porous WO{sub 3} synthesized by combustion process. • Hierarchically porous WO{sub 3} exhibits high gas response and excellent selectivity for acetone. • The excellent sensing property was plausibly attributed to the porous morphology.

  20. Hydrothermal deposition and photochromic performances of three kinds of hierarchical structure arrays of WO3 thin films

    International Nuclear Information System (INIS)

    Ding, Defang; Shen, Yi; Ouyang, Yali; Li, Zhen

    2012-01-01

    Three kinds of tungsten oxide (WO 3 ) thin films have been fabricated by a simple hydrothermal deposition method. Scanning electron microscopy images of the products revealed that the capping agents did impact the microstructure of WO 3 films. Films prepared without capping agents were ordered nanorod arrays, while the ones obtained with ethanol and oxalic acid revealed peeled-orange-like and cauliflower-like hierarchical structure arrays, respectively. Both of the two hierarchical structures were composed of much thinner nanorods compared with the one obtained without capping agents. All the WO 3 films exhibited good photochromic properties and the two with inducers performed even better, which could be due to the changes in the microstructure that increased the amount of photogenerated electron–hole pairs and the proton diffusion rates. - Highlights: ► Ordered WO 3 nanorod arrays were prepared by hydrothermal deposition process. ► Two hierarchical WO 3 structure arrays were obtained with ethanol and oxalic acid. ► Mechanism for the improved photochromic performances of WO 3 films is proposed.

  1. Low-cost fabrication of WO{sub 3} films using a room temperature and low-vacuum air-spray based deposition system for inorganic electrochromic device applications

    Energy Technology Data Exchange (ETDEWEB)

    Park, Sung-Ik [Department of Mechanical and Aerospace Engineering, Seoul National University, Seoul (Korea, Republic of); Kim, Sooyeun, E-mail: sooyeunk@u.washington.edu [Department of Mechanical Engineering, University of Washington, Seattle, WA (United States); Choi, Jung-Oh; Song, Ji-Hyeon [Department of Mechanical and Aerospace Engineering, Seoul National University, Seoul (Korea, Republic of); Taya, Minoru [Department of Mechanical Engineering, University of Washington, Seattle, WA (United States); Ahn, Sung-Hoon, E-mail: ahnsh@snu.ac.kr [Department of Mechanical and Aerospace Engineering, Seoul National University, Seoul (Korea, Republic of); Institute of Advanced Machines and Design, Seoul (Korea, Republic of)

    2015-08-31

    We report the deposition of tungsten oxide (WO{sub 3}) thin films on fluorine-doped tin oxide (FTO) and indium-doped tin oxide (ITO) glass substrates by using a room-temperature deposition system based on low-vacuum air-spray for the fabrication of inorganic electrochromic windows. The structure of the WO{sub 3} films was characterized using X-ray diffraction, and the surface morphology and film thickness were investigated using scanning electron microscopy and atomic force microscopy. The color of the prepared WO{sub 3} films changed from slight yellow to dark blue under applied voltages, demonstrating electrochromism. The WO{sub 3} film coated FTO glass exhibited a large electrochromic contrast of up to 50% at a wavelength of 800 nm. The electrochemical properties of the films were examined using cyclic voltammetry and chronocoulometry. - Highlights: • WO{sub 3} thin films were fabricated using an air-spray based deposition system at room temperature under low-vacuum conditions. • Dry WO{sub 3} particles were directly deposited on FTO and ITO glasses by using a low-cost deposition system. • The FTO glass based WO{sub 3} film showed the optical contrast of 50% at a wavelength of 800 nm.

  2. Hydrothermal synthesis of hierarchical WO3 nanostructures for dye-sensitized solar cells

    International Nuclear Information System (INIS)

    Rashad, M.M.; Shalan, A.E.

    2014-01-01

    Hierarchical architectures consisting of one-dimensional (1D) nanostructures are of great interest for potential use in energy and environmental applications in recent years. In this work, hierarchical tungsten oxide (WO 3 ) has been synthesized via a facile hydrothermal route from ammonium metatungstate hydrate and implemented as photoelectrode for dye-sensitized solar cells. The urchin-like WO 3 micro-patterns are constructed by self-organized nanoscale length 1D building blocks, which are single crystalline in nature, grown along (001) direction and confirm an orthorhombic crystal phase. The obtained powders were investigated by XRD, SEM, TEM and UV-Vis Spectroscopy. The photovoltaic performance of dye-sensitized solar cells based on WO 3 photoanodes was investigated. With increasing the calcination temperature of the prepared nanopowders, the light-electricity conversion efficiency (η) was increased. The results were attributed to increase the crystallinity of the particles and ease of electron movement. The DSSC based on hierarchical WO 3 showed a short-circuit current, an open-circuit voltage, a fill factor, and a conversion efficiency of 4.241 mA/cm 2 , 0.656 V, 66.74, and 1.85 %, respectively. (orig.)

  3. Structural phototransformation of WO{sub 3} thin films detected by photoacoustic analysis

    Energy Technology Data Exchange (ETDEWEB)

    Pacheco, Argelia Perez, E-mail: ekargy@hotmail.com [Universidad Nacional Autonoma de Mexico, Laboratorio de Fotofisica y Peliculas Delgadas-CCADET, Ciudad Universitaria, Coyoacan, A.P. 70-186, C.P. 04510, Mexico, D.F. (Mexico); Montes de Oca, C. Oliva; Castaneda-Guzman, R.; Garcia, A. Esparza [Universidad Nacional Autonoma de Mexico, Laboratorio de Fotofisica y Peliculas Delgadas-CCADET, Ciudad Universitaria, Coyoacan, A.P. 70-186, C.P. 04510, Mexico, D.F. (Mexico)

    2012-11-15

    Highlights: Black-Right-Pointing-Pointer The phototransformation of WO{sub 3} thin films were studied by photoacoustic technique. Black-Right-Pointing-Pointer The phase transition in WO{sub 3} thin films was induced by laser irradiation fluence. Black-Right-Pointing-Pointer The onset and end of the phototransformation in the thin films was identified. Black-Right-Pointing-Pointer The ablation threshold for each sample was identified. - Abstract: The photoacoustic technique (PA) was used to detect the phase transformation from amorphous to crystalline state of tungsten oxide (WO{sub 3}) thin films induced by UV pulsed laser radiation at low energy (<1.5 mJ). The evolution of photoacoustic signal was studied by a correlation analysis, comparing successive signals at fluences ranging from 0 to 20 mJ/cm{sup 2}. In this interval, it was possible to observe structural changes and the ablation threshold in films due to incident laser fluence effect. Thin films of WO{sub 3} were deposited by DC reactive magnetron sputtering over glass substrates at different deposition times. The results obtained by correlation analysis were compared with Raman spectroscopy data.

  4. W-containing oxide layers obtained on aluminum and titanium by PEO as catalysts in thiophene oxidation

    Science.gov (United States)

    Rudnev, V. S.; Lukiyanchuk, I. V.; Vasilyeva, M. S.; Morozova, V. P.; Zelikman, V. M.; Tarkhanova, I. G.

    2017-11-01

    W-containing oxide layers fabricated on titanium and aluminum alloys by Plasma electrolytic oxidation (PEO) have been tested in the reaction of the peroxide oxidation of thiophene. Samples with two types of coatings have been investigated. Coatings I contained tungsten oxide in the matrix and on the surface of amorphous silica-titania or silica-alumina layers, while coatings II comprised crystalline WO3 and/or Al2(WO4)3. Aluminum-supported catalyst containing a smallest amount of transition metals in the form of tungsten oxides and manganese oxides in low oxidation levels showed high activity and stability.

  5. Selective hydrodeoxygenation of cyclic vicinal diols to cyclic alcohols over tungsten oxide-palladium catalysts.

    Science.gov (United States)

    Amada, Yasushi; Ota, Nobuhiko; Tamura, Masazumi; Nakagawa, Yoshinao; Tomishige, Keiichi

    2014-08-01

    Hydrodeoxygenation of cyclic vicinal diols such as 1,4-anhydroerythritol was conducted over catalysts containing both a noble metal and a group 5-7 transition-metal oxide. The combination of Pd and WOx allowed the removal of one of the two OH groups selectively. 3-Hydroxytetrahydrofuran was obtained from 1,4-anhydroerythritol in 72 and 74% yield over WOx -Pd/C and WOx -Pd/ZrO2 , respectively. The WOx -Pd/ZrO2 catalyst was reusable without significant loss of activity if the catalyst was calcined as a method of regeneration. Characterization of WOx -Pd/C with temperature-programmed reduction, X-ray diffraction, and transmission electron microscopy/energy-dispersive X-ray spectroscopy suggested that Pd metal particles approximately 9 nm in size were formed on amorphous tungsten oxide particles. A reaction mechanism was proposed on the basis of kinetics, reaction results with tungsten oxides under an atmosphere of Ar, and density functional theory calculations. A tetravalent tungsten center (W(IV) ) was formed by reduction of WO3 with the Pd catalyst and H2 , and this center served as the reductant for partial hydrodeoxygenation. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  6. Effects of thermal treatment on the anodic growth of tungsten oxide films

    Energy Technology Data Exchange (ETDEWEB)

    Chai, Y., E-mail: yqchai85@gmail.com; Tam, C.W.; Beh, K.P.; Yam, F.K.; Hassan, Z.

    2015-08-03

    This work reports the investigation of the effects of thermal treatment on anodic growth tungsten oxide (WO{sub 3}). The increase of the thermal treatment temperature above 400 °C significantly influences WO{sub 3} film where high porosity structure reduces to more compact film. As-grown film is amorphous, which transforms to monoclinic/orthorhombic phase upon annealing at 300–600 °C. With the reducing of porous structure, preferential growth of (002) plane shifts to (020) plane at 600 °C with more than twentyfold increase of peak's intensity compared to the film annealed at 500 °C. Films annealed at low thermal treatment show better ion intercalation and reversibility during electrochemical measurements; however, it has larger optical band gap. Photoelectrochemical measurement reveals that film annealed at 400 °C exhibits the best photocatalytic performance among the films annealed at 300–600 °C. - Highlights: • Porosity of the WO{sub 3} reduces as annealing temperature increases above 400 °C. • As-grown film is amorphous which transforms to monoclinic/orthorhombic upon annealing. • As-grown film shows better ion intercalation in electrochemical process. • Optical band gap of WO{sub 3} reduces as the annealing temperature increases. • Film annealed at 400 °C exhibits best photocatalytic performance.

  7. WO3 and W Thermal Atomic Layer Etching Using "Conversion-Fluorination" and "Oxidation-Conversion-Fluorination" Mechanisms.

    Science.gov (United States)

    Johnson, Nicholas R; George, Steven M

    2017-10-04

    The thermal atomic layer etching (ALE) of WO 3 and W was demonstrated with new "conversion-fluorination" and "oxidation-conversion-fluorination" etching mechanisms. Both of these mechanisms are based on sequential, self-limiting reactions. WO 3 ALE was achieved by a "conversion-fluorination" mechanism using an AB exposure sequence with boron trichloride (BCl 3 ) and hydrogen fluoride (HF). BCl 3 converts the WO 3 surface to a B 2 O 3 layer while forming volatile WO x Cl y products. Subsequently, HF spontaneously etches the B 2 O 3 layer producing volatile BF 3 and H 2 O products. In situ spectroscopic ellipsometry (SE) studies determined that the BCl 3 and HF reactions were self-limiting versus exposure. The WO 3 ALE etch rates increased with temperature from 0.55 Å/cycle at 128 °C to 4.19 Å/cycle at 207 °C. W served as an etch stop because BCl 3 and HF could not etch the underlying W film. W ALE was performed using a three-step "oxidation-conversion-fluorination" mechanism. In this ABC exposure sequence, the W surface is first oxidized to a WO 3 layer using O 2 /O 3 . Subsequently, the WO 3 layer is etched with BCl 3 and HF. SE could simultaneously monitor the W and WO 3 thicknesses and conversion of W to WO 3 . SE measurements showed that the W film thickness decreased linearly with number of ABC reaction cycles. W ALE was shown to be self-limiting with respect to each reaction in the ABC process. The etch rate for W ALE was ∼2.5 Å/cycle at 207 °C. An oxide thickness of ∼20 Å remained after W ALE, but could be removed by sequential BCl 3 and HF exposures without affecting the W layer. These new etching mechanisms will enable the thermal ALE of a variety of additional metal materials including those that have volatile metal fluorides.

  8. Near-room temperature deposition of W and WO3 thin films by hydrogen atom assisted chemical vapor deposition

    International Nuclear Information System (INIS)

    Lee, W.W.; Reeves, R.R.

    1992-01-01

    A novel near-room temperatures CVD process has been developed using H-atoms reaction with WF 6 to produced tungsten and tungsten oxide films. The chemical, physical and electrical properties of these films were studied. Good adhesion and low resistivity of W films were measured. Conformal WO 3 films were obtained on columnar tungsten using a small amount of molecular oxygen in the gas stream. A reaction mechanism was evaluated on the basis of experimental results. The advantages of the method include deposition of adherent films in a plasma-free environment, near-room temperature, with a low level of impurity

  9. Hydrothermal deposition and photochromic performances of three kinds of hierarchical structure arrays of WO{sub 3} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Ding, Defang; Shen, Yi, E-mail: sysy7373@163.com; Ouyang, Yali; Li, Zhen

    2012-10-01

    Three kinds of tungsten oxide (WO{sub 3}) thin films have been fabricated by a simple hydrothermal deposition method. Scanning electron microscopy images of the products revealed that the capping agents did impact the microstructure of WO{sub 3} films. Films prepared without capping agents were ordered nanorod arrays, while the ones obtained with ethanol and oxalic acid revealed peeled-orange-like and cauliflower-like hierarchical structure arrays, respectively. Both of the two hierarchical structures were composed of much thinner nanorods compared with the one obtained without capping agents. All the WO{sub 3} films exhibited good photochromic properties and the two with inducers performed even better, which could be due to the changes in the microstructure that increased the amount of photogenerated electron-hole pairs and the proton diffusion rates. - Highlights: Black-Right-Pointing-Pointer Ordered WO{sub 3} nanorod arrays were prepared by hydrothermal deposition process. Black-Right-Pointing-Pointer Two hierarchical WO{sub 3} structure arrays were obtained with ethanol and oxalic acid. Black-Right-Pointing-Pointer Mechanism for the improved photochromic performances of WO{sub 3} films is proposed.

  10. Evolution of coherent collective modes through consecutive charge-density-wave transitions in the (PO2)4(WO3)12 monophosphate tungsten bronze

    Science.gov (United States)

    Stojchevska, L.; Borovšak, M.; Foury-Leylekian, P.; Pouget, J.-P.; Mertelj, T.; Mihailovic, D.

    2017-07-01

    All-optical femtosecond relaxation dynamics in a single crystal of monophosphate tungsten bronze (PO2)4(WO3)2m with alternate stacking m =6 of WO3 layers was studied through the three consequent charge-density-wave (CDW) transitions. Several transient coherent collective modes associated with the different CDW transitions were observed and analyzed in the framework of the time-dependent Ginzburg-Landau theory. Remarkably, the interference of the modes leads to an apparent rectification effect in the transient reflectivity response. A saturation of the coherent-mode amplitudes with increasing pump fluence well below the CDWs destruction threshold fluence indicates a decoupling of the electronic and lattice parts of the order parameter on the femtosecond timescale.

  11. Solid-State Electrochromic Device Consisting of Amorphous WO3 and Various Thin Oxide Layers

    Science.gov (United States)

    Shizukuishi, Makoto; Shimizu, Isamu; Inoue, Eiichi

    1980-11-01

    A mixed oxide containing Cr2O3 was introduced into an amorphous WO3 solid-state electrochromic device (ECD) in order to improve its colour memory effect. The electrochromic characteristics were greatly affected by the chemical constituents of a dielectric layer on the a-WO3 layer. Particularly, long memory effect and low power dissipation were attained in a solid-state ECD consisting of a-WO3 and Cr2O3\\cdotV2O5(50 wt.%). Some electrochromic characteristics of the a-WO3/Cr2O3\\cdotV2O5 ECD and the role of V2O5 were investigated.

  12. Tungsten Trioxide/Zinc Tungstate Bilayers: Electrochromic Behaviors, Energy Storage and Electron Transfer

    International Nuclear Information System (INIS)

    Wei, Huige; Ding, Daowei; Yan, Xingru; Guo, Jiang; Shao, Lu; Chen, Haoran; Sun, Luyi; Colorado, Henry A.; Wei, Suying; Guo, Zhanhu

    2014-01-01

    Highlights: • Tungsten oxide and zinc tungstate bilayers have been prepared via a facile sol-gel method for integrated applications of electrochromic behaviors and energy storage;. • Electron transfer behaviors between the semiconductor bilayer films have been found dependent on the bilayer assembly sequence;. • Methylene blue (MB) has been employed for the first time as an indicator to study the electron transfer phenomenon in the bilayer films. - Abstract: Pair-sequentially spin-coated tungsten trioxide (WO 3 ) and zinc tungstate (ZnWO 4 ) bilayer films onto indium tin oxide (ITO) coated glass slides have been prepared via sol-gel methods followed by annealing. The bilayers (ZnWO 4 /WO 3 denoting the bilayer film with the inner layer of ZnWO 4 and the outer layer of WO 3 on the ITO while WO 3 /ZnWO 4 standing for the bilayer film with the inner layer of WO 3 and the outer layer of ZnWO 4 on the ITO) exhibit integrated functions of electrochromic and energy storage behaviors as indicated by the in situ spectroelectrochemistry and cyclic voltammetry (CV) results. Accordingly, blue color was observed for the bilayer films at -1 V in 0.5 M H 2 SO 4 solution. An areal capacitance of 140 and 230 μF/cm 2 was obtained for the ZnWO 4 /WO 3 , and WO 3 /ZnWO 4 film, respectively, at a scan rate of 0.05 V/s in the CV measurements. The CV results also unveiled the electron transfer behavior between the semiconductor films in the oxidation process, suggesting a sequence-dependent electrochemical response in the bilayer films. Meanwhile, methylene blue (MB) was used as an indicator to study the electron transfer phenomenon during the reduction process at negative potentials of -0.4 and -0.8 V, in 0.5 M Na 2 SO 4 . The results indicated that the electrons transfer across the bilayers was enhanced at more negative potentials

  13. Hydrothermal synthesis of hierarchical WO{sub 3} nanostructures for dye-sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Rashad, M.M. [Central Metallurgical Research and Development Institute (CMRDI), Helwan, P.O. Box 87, Cairo (Egypt); Shalan, A.E. [Central Metallurgical Research and Development Institute (CMRDI), Helwan, P.O. Box 87, Cairo (Egypt); Friedrich-Alexander-University of Erlangen-Nuremberg, Institute of Materials for Electronics and Energy Technology (i-MEET), Erlangen (Germany)

    2014-08-15

    Hierarchical architectures consisting of one-dimensional (1D) nanostructures are of great interest for potential use in energy and environmental applications in recent years. In this work, hierarchical tungsten oxide (WO{sub 3}) has been synthesized via a facile hydrothermal route from ammonium metatungstate hydrate and implemented as photoelectrode for dye-sensitized solar cells. The urchin-like WO{sub 3} micro-patterns are constructed by self-organized nanoscale length 1D building blocks, which are single crystalline in nature, grown along (001) direction and confirm an orthorhombic crystal phase. The obtained powders were investigated by XRD, SEM, TEM and UV-Vis Spectroscopy. The photovoltaic performance of dye-sensitized solar cells based on WO{sub 3} photoanodes was investigated. With increasing the calcination temperature of the prepared nanopowders, the light-electricity conversion efficiency (η) was increased. The results were attributed to increase the crystallinity of the particles and ease of electron movement. The DSSC based on hierarchical WO{sub 3} showed a short-circuit current, an open-circuit voltage, a fill factor, and a conversion efficiency of 4.241 mA/cm{sup 2}, 0.656 V, 66.74, and 1.85 %, respectively. (orig.)

  14. Tungsten oxide@polypyrrole core-shell nanowire arrays as novel negative electrodes for asymmetric supercapacitors.

    Science.gov (United States)

    Wang, Fengmei; Zhan, Xueying; Cheng, Zhongzhou; Wang, Zhenxing; Wang, Qisheng; Xu, Kai; Safdar, Muhammad; He, Jun

    2015-02-11

    Among active pseudocapacitive materials, polypyrrole (PPy) is a promising electrode material in electrochemical capacitors. PPy-based materials research has thus far focused on its electrochemical performance as a positive electrode rather than as a negative electrode for asymmetric supercapacitors (ASCs). Here high-performance electrochemical supercapacitors are designed with tungsten oxide@PPy (WO3 @PPy) core-shell nanowire arrays and Co(OH)2 nanowires grown on carbon fibers. The WO3 @PPy core-shell nanowire electrode exhibits a high capacitance (253 mF/cm2) in negative potentials (-1.0-0.0 V). The ASCs packaged with CF-Co(OH)2 as a positive electrode and CF-WO3 @PPy as a negative electrode display a high volumetric capacitance up to 2.865 F/cm3 based on volume of the device, an energy density of 1.02 mWh/cm3 , and very good stability performance. These findings promote the application of PPy-based nanostructures as advanced negative electrodes for ASCs. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  15. The catalytic activity of several tungsten oxides for the oxidation of propene

    International Nuclear Information System (INIS)

    De Rossi, S.; Schiavello, M.; Rome Univ.; Iguchi, E.; Tilley, R.J.D.

    1976-01-01

    A study has been made of the catalytic oxidation of propene over the oxides WO 3 , WOsub(2,95), WOsub(2,90), WOsub(2,72) and Wo 2 , which were selected because they possess specific features of chemical and structural interest rather than for their catalytic ability. It was found that the oxides WOsub(2,95), WOsub(2,90) and WOsub(2,72) all selectively produce acrolein in small amounts. The oxides WO 3 and WO 2 were non-selective and rather inactive. The results are discussed in terms of a mechanism involving both variable valence in the crystal and the specific structural geometry of these compounds. (orig.) [de

  16. Electrosprayed heterojunction WO{sub 3}/BiVO{sub 4} films with nanotextured pillar structure for enhanced photoelectrochemical water splitting

    Energy Technology Data Exchange (ETDEWEB)

    Mali, Mukund G.; Yoon, Hyun; Yoon, Sam S., E-mail: skyoon@korea.ac.kr [School of Mechanical Engineering, Korea University, Seoul 136-713 (Korea, Republic of); Kim, Min-woo [School of Mechanical Engineering, Korea University, Seoul 136-713 (Korea, Republic of); Green School, Korea University, Seoul 136-713 (Korea, Republic of); Swihart, Mark T. [Department of Chemistry and Biological Engineering, University at Buffalo (SUNY), Buffalo, New York 14260 (United States); Al-Deyab, Salem S. [Department of Chemistry, College of Science, King Saud University, Riyadh 11451 (Saudi Arabia)

    2015-04-13

    We demonstrate that the addition of a tungsten oxide (WO{sub 3}) layer beneath a bismuth vanadate (BiVO{sub 4}) photocatalyst layer with a nanotextured pillar morphology significantly increases the photocurrent density in photoelectrochemical water splitting. The WO{sub 3}-BiVO{sub 4} bilayer films produced a photocurrent of up to 3.3 mA/cm{sup 2} under illumination at 100 mW/cm{sup 2} (AM1.5 spectrum). The bilayer film was characterized by scanning electron microscopy, X-ray diffraction, and photoelectrochemical methods, which confirmed the superiority of the bilayer film in terms of its morphology and charge separation and transport ability. Both WO{sub 3} and BiVO{sub 4} were deposited by electrostatic spraying under open-air conditions, which resulted in nanotextured pillars of BiVO{sub 4} atop a smooth WO{sub 3} film. The optimal coating conditions are also reported.

  17. Gasochromic performance of WO3-nanorod thin films fabricated with an ArF excimer laser

    International Nuclear Information System (INIS)

    Yaacob, M. H.; Ou, J. Z.; Wlodarski, W.; Kim, C. S.; Lee, J. Y.; Kim, Y. H.; Oh, C. M.; Dhakal, K. P.; Kim, J. Y.; Kang, J. H.

    2012-01-01

    Thin films with tungsten trioxide (WO 3 ) nanorods were fabricated by using an ArF pulsed laser deposition system. Because the ArF excimer laser operates at a very short wavelength of 193 nm, short enough to expect strong absorption of the photons in the semiconductor oxide targets, and because the clusters incoming to the substrates have high momentum, we could build thin films with good surface morphology. Highly homogeneous arrays of nanorods with sizes mostly in the range of 30 - 40 nm were observed. The absorbance response towards hydrogen (H 2 ) gas was investigated for a WO 3 film coated with 25-A-thick palladium (Pd). The Pd/WO 3 -nanorod thin films exhibited excellent gasochromic response when measured in the visible-NIR range (400 - 1000 nm). As low as 0.06% H 2 concentration was clearly sensed. A significant reversible absorbance change and fast recovery ( 2 at different concentrations.

  18. Synthesis of the cactus-like silicon nanowires/tungsten oxide nanowires composite for room-temperature NO{sub 2} gas sensor

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Weiyi, E-mail: zhangweiyi@tju.edu.cn [School of Electronic Information Engineering, Tianjin University, Tianjin, 300072 (China); Hu, Ming [School of Electronic Information Engineering, Tianjin University, Tianjin, 300072 (China); Key Laboratory for Advanced Ceramics and Machining Technology, Ministry of Education, School of Materials Science and Engineering, Tianjin University, Tianjin 300072 (China); Liu, Xing; Wei, Yulong; Li, Na [School of Electronic Information Engineering, Tianjin University, Tianjin, 300072 (China); Qin, Yuxiang, E-mail: qinyuxiang@tju.edu.cn [School of Electronic Information Engineering, Tianjin University, Tianjin, 300072 (China); Key Laboratory for Advanced Ceramics and Machining Technology, Ministry of Education, School of Materials Science and Engineering, Tianjin University, Tianjin 300072 (China)

    2016-09-15

    In the present work, the tungsten oxide (WO{sub 3}) nanowires functionalized silicon nanowires (SiNWs) with cactus-like structure has been successfully synthesized for room-temperature NO{sub 2} detection. The novel nanocomposite was fabricated by metal-assisted chemical etching (MACE) and thermal annealing of tungsten film. The WO{sub 3} nanowires were evenly distributed from the upper to the lower part of the SiNWs, indicating excellent uniformity which is conducive to adsorption and desorption of gas molecules. The gas-sensing properties have been examined by measuring the resistance change towards 0.25–5 ppm NO{sub 2} gas. At room temperature, which is the optimum working temperature, the SiNWs/WO{sub 3} nanowires composite showed two-times higher NO{sub 2} response than that of the bare SiNWs at 2 ppm NO{sub 2}. On the contrary, the responses of composite sensors to high concentrations of other reducing gases were very low, indicating excellent selectivity. Simultaneously, the composite sensors exhibited good sensing repeatability and stability. The enhancement in gas sensing properties may be attributed to the change in width of the space charge region, which is similar to the behavior of p-n junctions under forward bias, in the high-density p-n heterojunction structure formed between SiNWs and WO{sub 3} nanowires. - Highlights: • SiNWs/WO{sub 3} nanowires composite with cactus-like structure is synthesized. • The morphology of WO{sub 3} nanowires depends on the thermal annealing temperature. • The nanocomposite sensor exhibit better gas response than that of bare SiNWs. • The gas sensing mechanism is discussed using p-n heterojunction theory.

  19. Enhanced NO2 sensing characteristics of Au modified porous silicon/thorn-sphere-like tungsten oxide composites

    Science.gov (United States)

    Yuan, Lin; Hu, Ming; Wei, Yulong; Ma, Wenfeng

    2016-12-01

    The thorn-sphere-like tungsten oxide (WO3) made up by 1D nanorods has been successfully synthesized through hydrothermal method on the Au-modified porous silicon (PS) substrates with seed-layer induction. By using XRD, EDS, FESEM and TEM techniques, we tested and verified that the crystal structure and morphology evolution of WO3 hierarchical nanostructure on the Au-modified PS strongly depend on the Au-sputtering time and hydrothermal reaction time. In addition, by comparing the NO2-sensing properties of the prepared products, we found that the 10 s-Au decorated PS/WO3-3 h (sputtering Au for 10 s and hydrothermal reaction for 3 h) composites sensor behaving as a typical p-type semiconductor and operating at room temperature (RT) exhibits high sensitivity and response characteristics even to ppb-level NO2, which makes this kind of sensor a competitive candidate for NO2-sensing applications. Moreover, the enhanced response may not only due to the high specific surface area but the Au nanoparticles acting as promoters for the spillover effect and forming metal-semiconductor heterojunctions with the PS and WO3. The transmission of electrons and holes in the heterogeneous interface generated among PS, WO3 and Au is proposed to illustrate the p-type response mechanism.

  20. Hydrofluoric–nitric–sulphuric-acid surface treatment of tungsten for carbon fibre-reinforced composite hybrids in space applications

    Energy Technology Data Exchange (ETDEWEB)

    Kanerva, M., E-mail: Mikko.Kanerva@aalto.fi [Aalto University, School of Engineering, Department of Applied Mechanics, P.O.B. 14300, FI-00076 Aalto (Finland); Johansson, L.-S.; Campbell, J.M. [Aalto University, School of Chemical Technology, Department of Forest Products Technology, P.O.B. 16300, FI-00076 Aalto (Finland); Revitzer, H. [Aalto University, School of Chemical Technology, Department of Chemistry, P.O.B. 16300, FI-00076 Aalto (Finland); Sarlin, E. [Tampere University of Technology, Department of Materials Science, P.O.B. 589, FI-33101 Tampere (Finland); Brander, T.; Saarela, O. [Aalto University, School of Engineering, Department of Applied Mechanics, P.O.B. 14300, FI-00076 Aalto (Finland)

    2015-02-15

    Highlights: • XPS and AFM analysis of the effect of hydrofluoric–nitric–sulphuric-acid on tungsten. • Dreiling's model established 54.4% thinning of WO{sub 3} due to 67 s treatment. • Strain energy release rate increased ≈8.4 J/m{sup 2} at the interface. • Failure loci analysis expressed the oxide and carbon fibre surfaces as weak points. - Abstract: Hybrid material systems, such as combinations of tungsten foils and carbon fibre-reinforced plastic (CFRP), are replacing metal alloy concepts in spacecraft enclosures. However, a good adhesion between the tungsten oxide scale and the epoxy resin used is required. Here, the effects of a hydrofluoric–nitric–sulphuric-acid (HFNS) treatment on tungsten oxides and subsequent adhesion to CFRP are analysed using atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) and fracture testing. The work shows that HFNS treatment results in decreased oxygen content, over 50% thinner tungsten trioxide (WO{sub 3}) layer and increased nano-roughness on thin tungsten foils. Fracture testing established a 39% increase in the average critical strain for tungsten–CFRP specimens after HFNS treatment was carried out on tungsten. The effect of the oxide scale modification regarding the critical strain energy release rate was ΔG{sub c}≈ 8.4 J/m{sup 2}.

  1. Preparation of three dimensional graphene foam–WO3 nanocomposite with enhanced visible light photocatalytic activity

    International Nuclear Information System (INIS)

    Azimirad, R.; Safa, S.

    2015-01-01

    Three dimensional graphene foam (3D GF) was synthesized by chemical vapor deposition (CVD) on a nickel foam skeleton. After dissolving the nickel foam, the obtaining 3D GF was used as a highly porous conductive substrate for nucleation and growth of WO 3 particles. Scanning electron microscopy (SEM) and Raman spectroscopy was employed to ensure the quality of the prepared GFs and to judge about the 3D GF–WO 3 chemical structure. The WO 3 characteristic Raman peaks centered at 726, and 809 cm −1 are slightly broadened and displaced to lower wavelength in the 3D GF–WO 3 nanocomposite, as compared to the corresponding peaks of the bare tungsten oxide. This phenomenon confirms the formation of W–C and W–O–C bonds in composite material which is important for faster transferring the photoexcited electrons to graphene 3D network as an exceptional electron acceptor. The 3D GF−WO 3 composite material was applied in photocatalytic degradation of Rhodamine B dye. It was observed that the annealed samples show an excellent photocatalytic performance relative to the as-prepared 3D GF−WO 3 samples and bare WO 3 , which is ascribed to the lower electron/hole recombination through the formation of W–C and W–O–C bonds. - Highlights: • 3D GF synthesized by CVD on a nickel foam as a highly porous conductive substrate. • WO 3 nanoparticles coated on 3D GF by dip-coating. • 3D GF−WO 3 shows an excellent photocatalytic degradation of Rhodamine B dye. • Better photocatalytic properties assigned to the formation of W–C and W–O–C bonds

  2. Tungsten trioxide as high-{kappa} gate dielectric for highly transparent and temperature-stable zinc-oxide-based thin-film transistors

    Energy Technology Data Exchange (ETDEWEB)

    Lorenz, Michael; Wenckstern, Holger von; Grundmann, Marius [Universitaet Leipzig, Fakultaet fuer Physik und Geowissenschaften, Institut fuer Experimentelle Physik II, Linnestr. 5, 04103 Leipzig (Germany)

    2012-07-01

    We demonstrate metal-insulator-semiconductor field-effect transistors with high-{kappa}, room-temperature deposited, highly transparent tungsten trioxide (WO{sub 3}) as gate dielectric. The channel material consists of a zinc oxide (ZnO) thin-film. The transmittance and resistivity of WO{sub 3} films was tuned in order to obtain a highly transparent and insulating WO{sub 3} dielectric. The devices were processed by standard photolithography using lift-off technique. On top of the WO{sub 3} dielectric a highly transparent and conductive oxide consisting of ZnO: Al 3% wt. was deposited. The gate structure of the devices exhibits an average transmittance in the visible spectral range of 86%. The on/off-current ratio is larger than 10{sup 8} with off- and gate leakage-currents below 3 x 10{sup -8} A/cm{sup 2}. Due to the high relative permittivity of {epsilon}{sub r} {approx} 70, a gate voltage sweep of only 2 V is necessary to turn the transistor on and off with a minimum subthreshold swing of 80 mV/decade. The channel mobility of the transistors equals the Hall-effect mobility with a value of 5 cm{sup 2}/Vs. It is furthermore shown, that the devices are stable up to operating temperatures of at least 150 C.

  3. Reduction of blue tungsten oxide

    International Nuclear Information System (INIS)

    Wilken, T.; Wert, C.; Woodhouse, J.; Morcom, W.

    1975-01-01

    A significant portion of commercial tungsten is produced by hydrogen reduction of oxides. Although several modes of reduction are possible, hydrogen reduction is used where high purity tungsten is required and where the addition of other elements or compounds is desired for modification of the metal, as is done for filaments in the lamp industry. Although several investigations of the reduction of oxides have been reported (1 to 5), few principles have been developed which can aid in assessment of current commercial practice. The reduction process was examined under conditions approximating commercial practice. The specific objectives were to determine the effects of dopants, of water vapor in the reducing atmosphere, and of reduction temperature upon: (1) the rate of the reaction by which blue tungsten oxide is reduced to tungsten metal, (2) the intermediate oxides associated with reduction, and (3) the morphology of the resulting tungsten powder

  4. The optical and electrochemical properties of electrochromic films: WO3+xV2O5

    Science.gov (United States)

    Li, Zhuying; Liu, Hui; Liu, Ye; Yang, Shaohong; Liu, Yan; Wang, Chong

    2010-05-01

    Since Deb's experiment in 1973 on the electrochromic effect, transmissive electrochromic films exhibit outstanding potential as energy efficient window controls which allow dynamic control of the solar energy transmission. These films with non-volatile memory, once in the coloured state, remain in the same state even after removal of the field. The optical and electrochemical properties of electrochromic films using magnetron sputter deposition tungsten oxide thin films and vanadium oxide doped tungsten-vanadium oxide thin films on ITO coated glass were investigated. From the UV region of the transmittance spectra, the optical band gap energy from the fundamental absorption edge can be determined. And the Cyclic voltammograms of these thin films in 1 mol LiClO4 propylene carbonate electrolyte (LIPC) were measured and analysed. The anode electrochromic V2O5 doped cathode electrochromic WO3 could make films colour changing while the transmittance of films keeped invariance. These performance characteristics make tungstenvanadium oxide colour changeably thin films are suitable for electrochromic windows applications.

  5. Synthesis and Characterization of WO3/Graphene Nanocomposites for Enhanced Photocatalytic Activities by One-Step In-Situ Hydrothermal Reaction

    Directory of Open Access Journals (Sweden)

    Xiaoxiao Hu

    2018-01-01

    Full Text Available Tungsten trioxide (WO3 nanorods are synthesized on the surface of graphene (GR sheets by using a one-step in-situ hydrothermal method employing sodium tungstate (Na2WO4·2H2O and graphene oxide (GO as precursors. The resulting WO3/GR nanocomposites are characterized by X-ray diffraction, Raman spectroscopy, transmission electron microscopy, scanning electron microscopy and X-ray photoelectron spectroscopy. The results confirm that the interface between WO3 nanorod and graphene contains chemical bonds. The enhanced optical absorption properties are measured by UV-vis diffuse reflectance spectra. The photocatalytic activity of the WO3/GR nanocomposites under visible light is evaluated by the photodegradation of methylene blue, where the degradation rate of WO3/GR nanocomposites is shown to be double that of pure WO3. This is attributed to the synergistic effect of graphene and the WO3 nanorod, which greatly enhances the photocatalytic performance of the prepared sample, reduces the recombination of the photogenerated electron-hole pairs and increases the visible light absorption efficiency. Finally, the photocatalytic mechanism of the WO3/GR nanocomposites is presented. The synthesis of the prepared sample is convenient, direct and environmentally friendly. The study reports a highly efficient composite photocatalyst for the degradation of contaminants that can be applied to cleaning up the environment.

  6. Understanding the conductive channel evolution in Na:WO3-x-based planar devices

    Science.gov (United States)

    Shang, Dashan; Li, Peining; Wang, Tao; Carria, Egidio; Sun, Jirong; Shen, Baogen; Taubner, Thomas; Valov, Ilia; Waser, Rainer; Wuttig, Matthias

    2015-03-01

    An ion migration process in a solid electrolyte is important for ion-based functional devices, such as fuel cells, batteries, electrochromics, gas sensors, and resistive switching systems. In this study, a planar sandwich structure is prepared by depositing tungsten oxide (WO3-x) films on a soda-lime glass substrate, from which Na+ diffuses into the WO3-x films during the deposition. The entire process of Na+ migration driven by an alternating electric field is visualized in the Na-doped WO3-x films in the form of conductive channel by in situ optical imaging combined with infrared spectroscopy and near-field imaging techniques. A reversible change of geometry between a parabolic and a bar channel is observed with the resistance change of the devices. The peculiar channel evolution is interpreted by a thermal-stress-induced mechanical deformation of the films and an asymmetric Na+ mobility between the parabolic and the bar channels. These results exemplify a typical ion migration process driven by an alternating electric field in a solid electrolyte with a low ion mobility and are expected to be beneficial to improve the controllability of the ion migration in ion-based functional devices, such as resistive switching devices.An ion migration process in a solid electrolyte is important for ion-based functional devices, such as fuel cells, batteries, electrochromics, gas sensors, and resistive switching systems. In this study, a planar sandwich structure is prepared by depositing tungsten oxide (WO3-x) films on a soda-lime glass substrate, from which Na+ diffuses into the WO3-x films during the deposition. The entire process of Na+ migration driven by an alternating electric field is visualized in the Na-doped WO3-x films in the form of conductive channel by in situ optical imaging combined with infrared spectroscopy and near-field imaging techniques. A reversible change of geometry between a parabolic and a bar channel is observed with the resistance change of the

  7. Oxidative desulfurization of benzothiophene and thiophene with WO{sub x}/ZrO{sub 2} catalysts: Effect of calcination temperature of catalysts

    Energy Technology Data Exchange (ETDEWEB)

    Hasan, Zubair; Jeon, Jaewoo [Department of Chemistry and Green-Nano Materials Research Center, Kyungpook National University, Daegu 702-701 (Korea, Republic of); Jhung, Sung Hwa, E-mail: sung@knu.ac.kr [Department of Chemistry and Green-Nano Materials Research Center, Kyungpook National University, Daegu 702-701 (Korea, Republic of)

    2012-02-29

    Highlights: Black-Right-Pointing-Pointer Oxidative desulfurization was studied with WO{sub x}/ZrO{sub 2} calcined at different temp. Black-Right-Pointing-Pointer The importance of the phases of zirconia and tungsten oxide was suggested. Black-Right-Pointing-Pointer The catalyst was analyzed thoroughly with Raman and XRD techniques. Black-Right-Pointing-Pointer The importance of electron density on S was confirmed with the kinetics of oxidation. - Abstract: Oxidative desulfurization (ODS) of model fuel containing benzothiophene (BT) or thiophene (Th) has been carried out with WO{sub x}/ZrO{sub 2} catalyst, which was calcined at various temperatures. Based on the conversion of BT in the model fuel, it can be shown that the optimum calcination temperature of WO{sub x}/ZrO{sub 2} catalyst is around 700 Degree-Sign C. The most active catalyst is composed of tetragonal zirconia (ZrO{sub 2}) with well dispersed polyoxotungstate species and it is necessary to minimize the contents of the crystalline WO{sub 3} and monoclinic ZrO{sub 2} for a high BT conversion. The oxidation rate was interpreted with the first-order kinetics, and it demonstrated the importance of electron density since the kinetic constant for BT was higher than that for Th even though the BT is larger than Th in size. A WO{sub x}/ZrO{sub 2} catalyst, treated suitably, can be used as a reusable active catalyst in the ODS.

  8. Spectroscopic properties and thermal stability of Er3+-doped tungsten-tellurite glass for waveguide amplifier application

    International Nuclear Information System (INIS)

    Zhao Shilong; Wang Xiuli; Fang Dawei; Xu Shiqing; Hu Lili

    2006-01-01

    Tungsten-tellurite glass with molar composition of 60TeO 2 -30WO 3 -10Na 2 O has been investigated for developing planar broadband waveguide amplifier application. Spectroscopic properties and thermal stability of Er 3+ -doped tungsten-tellurite glass have been discussed. The results show that the introduction of WO 3 increases significantly the glass transition temperature and the maximum phonon energy. Er 3+ -doped tungsten-tellurite glass exhibits high glass transition temperature (377 deg. C), large emission cross-section (0.91 x 10 -20 cm 2 ) at 1532 nm and broad full width at half maximum (FWHM), which make it preferable for broadband Er 3+ -doped waveguide amplifier application

  9. Characterization of MAPLE deposited WO3 thin films for electrochromic applications

    Science.gov (United States)

    Boyadjiev, S. I.; Stefan, N.; Szilágyi, I. M.; Mihailescu, N.; Visan, A.; Mihailescu, I. N.; Stan, G. E.; Besleaga, C.; Iliev, M. T.; Gesheva, K. A.

    2017-01-01

    Tungsten trioxide (WO3) is a widely studied material for electrochromic applications. The structure, morphology and optical properties of WO3 thin films, grown by matrix assisted pulsed laser evaporation (MAPLE) from monoclinic WO3 nano-sized particles, were investigated for their possible application as electrochromic layers. A KrF* excimer (λ=248 nm, ζFWHM=25 ns) laser source was used in all experiments. The MAPLE deposited WO3 thin films were studied by atomic force microscopy (AFM), grazing incidence X-ray diffraction (GIXRD) and Fourier transform infrared spectroscopy (FTIR). Cyclic voltammetry measurements were also performed, and the coloring and bleaching were observed. The morpho-structural investigations disclosed the synthesis of single-phase monoclinic WO3 films consisting of crystalline nano-grains embedded in an amorphous matrix. All thin films showed good electrochromic properties, thus validating application of the MAPLE deposition technique for the further development of electrochromic devices.

  10. Characterization of MAPLE deposited WO3 thin films for electrochromic applications

    International Nuclear Information System (INIS)

    Boyadjiev, S I; Iliev, M T; Stefan, N; Mihailescu, N; Visan, A; Mihailescu, I N; Szilágyi, I M; Stan, G E; Besleaga, C; Gesheva, K A

    2017-01-01

    Tungsten trioxide (WO 3 ) is a widely studied material for electrochromic applications. The structure, morphology and optical properties of WO 3 thin films, grown by matrix assisted pulsed laser evaporation (MAPLE) from monoclinic WO 3 nano-sized particles, were investigated for their possible application as electrochromic layers. A KrF* excimer (λ=248 nm, ζ FWHM =25 ns) laser source was used in all experiments. The MAPLE deposited WO 3 thin films were studied by atomic force microscopy (AFM), grazing incidence X-ray diffraction (GIXRD) and Fourier transform infrared spectroscopy (FTIR). Cyclic voltammetry measurements were also performed, and the coloring and bleaching were observed. The morpho-structural investigations disclosed the synthesis of single-phase monoclinic WO 3 films consisting of crystalline nano-grains embedded in an amorphous matrix. All thin films showed good electrochromic properties, thus validating application of the MAPLE deposition technique for the further development of electrochromic devices. (paper)

  11. Investigation of Electrical, Optical and GaS Sensing properties Sol-Gel Derived WO3 Thin Films

    International Nuclear Information System (INIS)

    Dumludag, F.

    2008-01-01

    Tungsten oxide (WO 3 ) is a wide band gap n-type semiconductor. Thin films of WO 3 are considerable interest because of their potential applications in electrochromic devices, and gas sensors. In this work, WO 3 thin films were deposited on IDT (Interdigital electrodes) by a sol-gel dipping process. Precursor solution was prepared by dissolving of tungstic acid in ammonia. We investigated d.c. and a.c. (40 Hz-100 KHz) electrical properties of the films in the temperature range of 293K and 473K in vacuum ambient (10 - 2 mbar). We observed frequency dependent conductivity behavior at high frequencies. Absorption spectra of the film showed that a maximum absorption occurred at 330 nm. We also investigated the response of the films to vapors of the volatile organic compounds (acetone, chloroform, toluene, ethanol, ammonia) and water vapor. The films showed no sensitivity to the test gases at room temperature. Concentration of the vapors were controlled by mass flowmeters. All the measurement system was computerized

  12. Tungsten oxides as interfacial layers for improved performance in hybrid optoelectronic devices

    International Nuclear Information System (INIS)

    Vasilopoulou, M.; Palilis, L.C.; Georgiadou, D.G.; Argitis, P.; Kennou, S.; Kostis, I.; Papadimitropoulos, G.; Stathopoulos, N.A.; Iliadis, A.A.; Konofaos, N.; Davazoglou, D.; Sygellou, L.

    2011-01-01

    Tungsten oxide (WO 3 ) films with thicknesses ranging from 30 to 100 nm were grown by Hot Filament Vapor Deposition (HFVD). Films were studied by X-Ray Photoemission Spectroscopy (XPS) and were found to be stoichiometric. The surface morphology of the films was characterized by Atomic Force Microscopy (AFM). Samples had a granular form with grains in the order of 100 nm. The surface roughness was found to increase with film thickness. HFVD WO 3 films were used as conducting interfacial layers in advanced hybrid organic-inorganic optoelectronic devices. Hybrid-Organic Light Emitting Diodes (Hy-OLEDs) and Organic Photovoltaics (Hy-OPVs) were fabricated with these films as anode and/or as cathode interfacial conducting layers. The Hy-OLEDs showed significantly higher current density and a lower turn-on voltage when a thin WO 3 layer was inserted at the anode/polymer interface, while when inserted at the cathode/polymer interface the device performance was found to deteriorate. The improvement was attributed to a more efficient hole injection and transport from the Fermi level of the anode to the Highest Occupied Molecular Orbital (HOMO) of a yellow emitting copolymer (YEP). On the other hand, the insertion of a thin WO 3 layer at the cathode/polymer interface of Hy-OPV devices based on a polythiophene-fullerene bulk-heterojunction blend photoactive layer resulted in an increase of the produced photogenerated current, more likely due to improved electron extraction at the Al cathode.

  13. Porous three-dimensional reduced graphene oxide merged with WO3 for efficient removal of radioactive strontium

    Science.gov (United States)

    Mu, Wanjun; Yu, Qianghong; Hu, rui; Li, Xingliang; Wei, Hongyuan; Jian, Yuan

    2017-11-01

    A simple hydrothermal method was used to prepare 3D nanostructured composite adsorbents of reduced graphene oxide (RGO) and WO3 (RGO/WO3). The analysis results suggest that it possesses a mesoporous 3D structure, in which WO3 nanorods are uniformly loaded on the surface of the RGO. Combining the benefits of GO and WO3, the composites exhibit a higher adsorption capacity for removing Sr2+ from aqueous solutions over a wide pH range (4-11). Adsorption isotherms show that the data fit the Langmuir isotherms well (R > 0.99), and the maximum adsorption capacity of 149.56 mg g-1 was achieved, much higher than that for GO, WO3 and other similar adsorbents. Sr2+ adsorption on RGO/WO3 reached equilibrium within 200 min. The fast adsorption and high adsorption rate of RGO/WO3 are mostly attributable to the plentiful adsorption sites provided by the dispersed WO3 nanoparticles on the RGO surface. Furthermore, the existence of Na+ ions has no obvious effect on the removal of Sr2+ ions by RGO/WO3, and RGO/WO3 adsorbent can be repeated at least 5 times without significant loss of adsorption capacity by adsorption-desorption experiment. Thus, RGO/WO3 shows the potential ability for removal of 90Sr from radioactive wastewater.

  14. Temperature dependent selective detection of hydrogen and acetone using Pd doped WO3/reduced graphene oxide nanocomposite

    Science.gov (United States)

    Kaur, Jasmeet; Anand, Kanica; Kohli, Nipin; Kaur, Amanpreet; Singh, Ravi Chand

    2018-06-01

    Reduced graphene oxide (RGO) and Pd doped WO3 nanocomposites were fabricated by employing electrostatic interactions between poly (diallyldimethylammonium chloride) (PDDA) modified Pd doped WO3 nanostructures and graphite oxide (GO) and studied for their gas sensing application. XRD, Raman, FTIR, FESEM-EDX, TEM, TGA, XPS and Photoluminescence techniques were used for characterization of as-synthesized samples. Gas sensing studies revealed that the sensor with optimized doping of 1.5 mol% Pd and 1 wt% GO shows temperature dependent selectivity towards hydrogen and acetone. The role of WO3, Pd and RGO has been discussed in detail for enhanced sensing performance.

  15. Sliding charge density wave in the monophosphate tungsten bronze (PO2)4(WO3)2m with alternate stacking of m=4 and m=6 WO3 layers

    International Nuclear Information System (INIS)

    Foury-Leylekian, P.; Sandre, E.; Ravy, S.; Pouget, J.-P.; Elkaim, E.; Roussel, P.; Groult, D.; Labbe, Ph.

    2002-01-01

    The monophosphate tungsten bronzes (PO 2 ) 4 (WO 3 ) 2m form family of two-dimensional metals which exhibit charge density wave (CDW) instabilities. These materials are generally built by the regular stacking of (a,b) layers in which chains made of segments of m WO 6 octahedra directed along the a and a±b directions are delimited. Their electronic structure thus originates from quasi-one-dimensional (1D) bands located on these chains. As a consequence their Fermi surface (FS) exhibits large flat portions whose nesting gives rise to successive CDW instabilities. Here we present a structural study of the CDW instability of the (PO 2 ) 4 (WO 3 ) 10 member formed by the alternate stacking of layers built with segments of m=4 and m=6 WO 6 octahedra. Its ab initio electronic structure calculation shows that the FS of this member exhibits large flat portions which can be extremely well nested. Its best nesting wave vector accounts for the modulation wave vector stabilized by the CDW transition which occurs at 156 K. Because of the regular stacking of layers of different m values the FS is slightly split. The unusual thermal dependence of the x-ray satellite intensity provides evidence that the two types of layers become modulated at different temperature. This also leads to a slight thermal sliding of the CDW-nesting modulation wave vector, which can be accounted for within the framework of a Landau-Ginzburg theory. In addition, the observation of a global hysteresis in the thermal cycling of the satellite intensity, as well as the degradation of the interlayer order upon cooling, suggest the formation of a disordered lattice of dilute solitons. Such solitons allow to accommodate the charge transferred between the two types of layer. Finally the relevance of local charge transfers, at intergrowth defects, for example, to create pinned discommensurations that break the CDW coherence is emphasized in this whole family of bronzes

  16. Fractal approach to surface roughness of TiO{sub 2}/WO{sub 3} coatings formed by plasma electrolytic oxidation process

    Energy Technology Data Exchange (ETDEWEB)

    Rožić, L.J., E-mail: ljrozic@nanosys.ihtmbg.ac.rs [University of Belgrade, IChTM-Department of Catalysis and Chemical Engineering, Njegoševa 12, Belgrade (Serbia); Petrović, S.; Radić, N. [University of Belgrade, IChTM-Department of Catalysis and Chemical Engineering, Njegoševa 12, Belgrade (Serbia); Stojadinović, S. [University of Belgrade, Faculty of Physics, Studentski trg 12-16, Belgrade (Serbia); Vasilić, R. [Faculty of Environmental Governance and Corporate Responsibility, Educons University, Vojvode Putnika 87, Sremska Kamenica (Serbia); Stefanov, P. [Institute of General and Inorganic Chemistry, Bulgarian Academy of Sciences, Sofia 1113 (Bulgaria); Grbić, B. [University of Belgrade, IChTM-Department of Catalysis and Chemical Engineering, Njegoševa 12, Belgrade (Serbia)

    2013-07-31

    In this study, we have shown that atomic force microscopy is a powerful technique to study the fractal parameters of TiO{sub 2}/WO{sub 3} coatings prepared by plasma electrolytic oxidation (PEO) process. Since the surface roughness of obtained oxide coatings affects their physical properties, an accurate description of roughness parameters is highly desirable. The surface roughness, described by root mean squared and arithmetic average values, is analyzed considering the scans of a series of atomic force micrographs. The results show that the oxide coatings exhibit lower surface roughness in initial stage of PEO process. Also, the surfaces of TiO{sub 2}/WO{sub 3} coatings exhibit fractal behavior. Positive correlation between the fractal dimension and surface roughness of the surfaces of TiO{sub 2}/WO{sub 3} coatings in initial stage of PEO process was found. - Highlights: • TiO{sub 2}/WO{sub 3} coatings were obtained by plasma electrolytic oxidation. • Oxide coatings exhibit lower surface roughness in initial stage of process. • The surfaces of TiO{sub 2}/WO{sub 3} coatings exhibit fractal behavior.

  17. Synthesis of γ-WO{sub 3} thin films by hot wire-CVD and investigation of its humidity sensing properties

    Energy Technology Data Exchange (ETDEWEB)

    Jadkar, Vijaya; Waykar, Ravindra; Jadhavar, Ashok [School of Energy Studies, Savitribai Phule Pune University, Pune 411 007 (India); Pawbake, Amit [School of Energy Studies, Savitribai Phule Pune University, Pune 411 007 (India); Physical and Material Chemistry Division, National Chemical Laboratory, Pune 411 008 (India); Date, Abhijit [School of Aerospace, Mechanical and Manufacturing Engineering, RMIT University, Plenty Road, Bundoora, Melbourne VIC 3083 (Australia); Late, Dattatray [Physical and Material Chemistry Division, National Chemical Laboratory, Pune 411 008 (India); Pathan, Habib; Gosavi, Suresh; Jadkar, Sandesh [Department of Physics, Savitribai Phule Pune University, Pune 411 007 (India)

    2017-05-15

    In this study, monoclinic tungsten oxide (γ-WO{sub 3}) have been grown in a single step using HW-CVD method by resistively heating W filaments in a constant O{sub 2} pressure. The formation of γ-WO{sub 3} was confirmed using low angle-XRD and Raman spectroscopy analysis. Low angle-XRD analysis revealed that as-deposited WO{sub 3} film are highly crystalline and the crystallites have preferred orientation along the (002) direction. HRTEM analysis and SAED pattern also show the highly crystalline nature of WO{sub 3} with d spacing of ∝ 0.38 nm, having an orientation along the (002) direction. Surface topography investigated by SEM analysis shows the formation of a uniform and homogeneous cauliflower like morphology throughout the substrate surface without flaws and cracks. A humidity sensing device incorporating WO{sub 3} is also fabricated, which shows a maximum humidity sensitivity factor of ∝ 3954% along with a response time of ∝14 s and a recovery time of ∝25 s. The obtained results demonstrate that it is possible to synthesize WO{sub 3} in a single step by HW-CVD method and to fabricate a humidity sensor by using it. (copyright 2017 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  18. Dissimilar mechanism of executing hole transfer by WO{sub 3} and MoO{sub 3} nanoparticles in organic solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Park, Eung-Kyu; Kim, Jae-Hyoung; Kim, Ji-Hwan; Park, Min-Ho; Lee, Dong-Hoon; Kim, Yong-Sang, E-mail: yongsang@skku.edu

    2015-07-31

    We investigated the effect of metal oxide nanoparticles (NPs) in poly (3,4 ethylenedioxythiophence):poly (styrene-sulfonate) layer for the light harvestation in poly (3-hexylthiophene):[6,6]-pheny-C{sub 61}-butyric acid methyl ester organic solar cells. The role of tungsten trioxide nanoparticles (WO{sub 3}) and molybdenum trioxide nanoparticles (MoO{sub 3}) in enhancing the efficiency of solar cells was compared. Due to the difference in the energy band structure of the two nanoparticles, the WO{sub 3} NPs acted as a hole blocking layer, whereas MoO{sub 3} NPs helped in the hole transfer. The solar cell with WO{sub 3} NPs at 1.5 wt% concentration showed a power conversion efficiency of 4.22% under AM 1.5G illumination and the device blended with 2 wt% of MoO{sub 3} NPs showed a power conversion efficiency of 4.40%. We measured various electrical properties including, electrochemical impedance spectroscopy and recombination mechanisms using the light intensity dependent current–voltage measurement of organic solar cell. - Highlights: • An organic solar cell was fabricated with WO{sub 3} or MoO{sub 3} NPs mixed PEDOT:PSS layer. • The effects of metallic NPs in PEDOT:PSS light harvesting system was investigated. • WO{sub 3} NPs acted as a hole blocking layer and MoO{sub 3} NPs helped in hole transporting. • The MoO{sub 3} NPs gave higher performance, reduced charge recombination and low resistance.

  19. High-pressure phases in the system W-O. Pt. 2

    International Nuclear Information System (INIS)

    Barabanenkov, Yu.A.; Zakharov, N.D.; Zibrov, I.P.; Filonenko, V.P.; Werner, P.; Popov, A.I.; Valkovskii, M.D.

    1993-01-01

    A new type of tungsten oxide has been synthesized from a mixture of W and WO 3 by a solid-phase sintering method under high-pressure conditions. The crystal structure of the new oxide was investigated by HRTEM, selected-area electron diffraction and X-ray powder diffraction. The structure belongs to space group Pbam or P2 1 2 1 2 and has the following unit-cell parameters: a=21.431(9), b=17.766(7), c=3.783(2) A, V=1440 A 3 , Z=32, D x =8.33 g cm -3 . The structural model and W-cation positions were determined by HRTEM and image processing. X-ray powder analysis and the SHELX computer program were used to prove the proposed structural model: N=158, R=0.075, U iso (W)=0.019(3), U iso (O)=0.055(12) A 2 . The investigated crystal structure is, in fact, similar to WO 2.72 and is formed by W-O octahedra and pentagonal bipyramids. (orig.)

  20. Tungsten coatings electro-deposited on CFC substrates from oxide molten salt

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Ningbo; Zhang, Yingchun, E-mail: zycustb@163.com; Lang, Shaoting; Jiang, Fan; Wang, Lili

    2014-12-15

    Tungsten is considered as plasma facing material in fusion devices because of its high melting point, its good thermal conductivity, its low erosion rate and its benign neutron activation properties. On the other hand, carbon based materials like C/C fiber composites (CFC) have been used for plasma facing materials (PFMs) due to their high thermal shock resistance, light weight and high strength. Tungsten coatings on CFC substrates are used in the JET divertor in the frame of the JET ITER-like wall project, and have been prepared by plasma spray (PS) and other techniques. In this study, tungsten coatings were electro-deposited on CFC from Na{sub 2}WO{sub 4}–WO{sub 3} molten salt under various deposition parameters at 900 °C in air. In order to obtain tungsten coatings with excellent performance, the effects of pulse duration ratio and pulse current density on microstructures and crystal structures of tungsten coatings were investigated by X-ray diffraction (XRD, Rigaku Industrial Co., Ltd., D/MAX-RB) and a scanning electron microscope (SEM, JSM 6480LV). It is found that the pulsed duration ratio and pulse current density had a significant influence on tungsten nucleation and electro-crystallization phenomena. SEM observation revealed that intact, uniform and dense tungsten coatings formed on the CFC substrates. Both the average grain size and thickness of the coating increased with the pulsed current density. The XRD results showed that the coatings consisted of a single phase of tungsten with the body centered cubic (BCC) structure. The oxygen content of electro-deposited tungsten coatings was lower than 0.05%, and the micro-hardness was about 400 HV.

  1. Humidity sensing properties of WO3 thick film resistor prepared by screen printing technique

    International Nuclear Information System (INIS)

    Garde, Arun S

    2014-01-01

    Highlights: • Polycrystalline WO 3 Thick films are fabricated by screen printing technique. • Monoclinic phases were the majority in formation of films. • The peak at 1643 cm −1 shows stretching vibrations attributed to W-OH of adsorbed H 2 O. • Absorption peaks in the range 879–650 cm −1 are attributed to the stretching W-O-W bonds. • Increase in resistance with decrease in RH when exposed to 20–100% RH. - Abstract: Thick films of tungsten oxide based were prepared using standard screen printing technique. To study the effect of temperature on the thick films were fired at different temperature for 30 min in air atmosphere. The WO 3 thick films were characterized with X-ray diffraction, scanning electron microscopy and EDAX for elemental analysis. The formation of mixed phases of the film together with majority of monoclinic phase was observed. IR spectra confirm the peak at 1643 cm −1 clearly shows stretching vibrations attributed to the W-OH bending vibration mode of the adsorbed water molecules. The absorption peaks in the range 879–650 cm −1 are attributed to the stretching W-O-W bonds (i.e. ν [W-O inter -W]). The peak located at 983 cm −1 belong to W=O terminal of cluster boundaries. A change in the resistance was observed with respect to the relative humidity when the WO 3 thick films were exposed to a wide humidity range of 20–100%. An increasing firing temperature of WO 3 film increases with the sensitivity. The parameters such as sensitivity and hysteresis of the WO 3 film sensors have been evaluated

  2. S tudies on the phase transitions and properties of tungsten (VI oxide nanoparticles by X - Ray diffraction (XRD and thermal analysis

    Directory of Open Access Journals (Sweden)

    S.F. Abdullah

    2017-11-01

    Full Text Available Tungsten (VI oxide, WO3nanoparticles were synthesized by colloidal gas aphrons(CGAs technique.The resultant WO3nanoparticleswere characterized by thermogravimetric-differential thermal analysis (TG-DTA and X-Ray diffraction (XRD measurements in order to determine the phase transitions, the crystallinity and the size of theWO3nanoparticles. As a comparison, transmission electron microscope (TEM was used to investigate the size of the WO3nanoparticles. The result from XRD and DTA show that the formation of polymorphsWO3nanoparticles have the following sequence: orthorhombic (b-WO3®monoclinic (g-WO3 ®triclinic (d-WO3 ®monoclinic (e-WO3 with respect to the calcination temperature of 400, 500, 600 and 700°C. No diffraction peaks were found in the X-Ray diffraction measurements for the sample heat treated at 300°C (as-prepared, suggesting that an amorphous structure was obtained at this temperature whereas the crystallinity had been obtained by the other samples of theWO3nanoparticles at the calcination temperatures of 400, 500, 600 and 700°C. It is also found that the X-Ray diffraction measurements produced an average diameter of (30 ±5, (50 ±5, (150 ±10 and (200 ±10 nm at calcination temperatures of 400, 500, 600 and 700°C respectively by using Debye-Scherrer formula. The TG curve revealed that the WO3nanoparticles is purely anhydrous since the weight loss is insignificant (0.3 –1.4 % from 30 until 600°C for the WO3nanoparticles calcined at 400°C. Finally, the composition and the purity of the WO3nanoparticleshave been examined by X-Ray photoelectron spectroscopy (XPS. Theresults indicate no significant changes to the composition and the purity of the WO3nanoparticle produced due to the temperature variations

  3. Structural properties of WO{sub 3} dependent of the annealing temperature deposited by hot-filament metal oxide deposition

    Energy Technology Data Exchange (ETDEWEB)

    Flores M, J. E. [Benemerita Universidad Autonoma de Puebla, Facultad de Ciencias de la Electronica, Av. San Claudio y 18 Sur, Ciudad Universitaria, Col. Jardines de San Manuel, 72570 Puebla (Mexico); Diaz R, J. [IPN, Centro de Investigacion en Biotecnologia Aplicada, Ex-Hacienda de San Molino Km 1.5 Tepetitla, 90700 Tlaxcala (Mexico); Balderas L, J. A., E-mail: eflores@ece.buap.mx [IPN, Unidad Profesional Interdisciplinaria de Biotecnologia, Av. Acueducto s/n, Col. Barrio la Laguna, 07340 Mexico D. F. (Mexico)

    2012-07-01

    In this work presents a study of the effect of the annealing temperature on structural and optical properties of WO{sub 3} that has been grown by hot-filament metal oxide deposition. The chemical stoichiometry was determined by X-ray photoelectron spectroscopy. By X-ray diffraction obtained that the as-deposited WO{sub 3} films present mainly monoclinic crystalline phase. WO{sub 3} optical band gap energy can be varied from 2.92 to 3.15 eV obtained by transmittance measurements by annealing WO{sub 3} from 100 to 500 C. The Raman spectrum of the as-deposited WO{sub 3} film shows four intense peaks that are typical Raman peaks of crystalline WO{sub 3} (m-phase) that corresponds to the stretching vibrations of the bridging oxygen that are assigned to W-O stretching ({upsilon}) and W-O bending ({delta}) modes, respectively, which enhanced and increased their intensity with the annealing temperature. (Author)

  4. Degradation of malachite green on Pd/WO3 photocatalysts under simulated solar light

    International Nuclear Information System (INIS)

    Liu Yonggang; Ohko, Yoshihisa; Zhang Ruiqin; YangYingnan; Zhang Zhenya

    2010-01-01

    The photocatalytic degradation of malachite green (MG) dye molecules in aqueous solution was investigated by using palladium (Pd) modified tungsten trioxide (WO 3 ) under simulated solar light. The optimum values for Pd content vs. WO 3 and catalyst concentration in solution for MG (5.0 μmol L -1 ) degradation were 0.5 wt.% and 150 mg L -1 , respectively. The MG concentration change followed the pseudo first order kinetics of the Langmuir-Hinshelwood model. Since MG was also degraded under visible light (λ > 470 nm), which was not absorbed by WO 3 , the mechanism involved both the photocatalytic degradation and self-sensitized degradation of MG. Pd modified WO 3 would be useful as an efficient tool for the decolorization of wastewater under solar light.

  5. Gasochromic performance of WO{sub 3}-nanorod thin films fabricated with an ArF excimer laser

    Energy Technology Data Exchange (ETDEWEB)

    Yaacob, M. H. [RMIT University, Melbourne (Australia); Universiti Putra Malaysia, Selangor (Malaysia); Ou, J. Z.; Wlodarski, W. [RMIT University, Melbourne (Australia); Kim, C. S.; Lee, J. Y. [KAIST, Daejon (Korea, Republic of); Kim, Y. H. [KIST, Seoul (Korea, Republic of); Oh, C. M.; Dhakal, K. P.; Kim, J. Y.; Kang, J. H. [University of Incheon, Incheon (Korea, Republic of)

    2012-02-15

    Thin films with tungsten trioxide (WO{sub 3}) nanorods were fabricated by using an ArF pulsed laser deposition system. Because the ArF excimer laser operates at a very short wavelength of 193 nm, short enough to expect strong absorption of the photons in the semiconductor oxide targets, and because the clusters incoming to the substrates have high momentum, we could build thin films with good surface morphology. Highly homogeneous arrays of nanorods with sizes mostly in the range of 30 - 40 nm were observed. The absorbance response towards hydrogen (H{sub 2}) gas was investigated for a WO{sub 3} film coated with 25-A-thick palladium (Pd). The Pd/WO{sub 3}-nanorod thin films exhibited excellent gasochromic response when measured in the visible-NIR range (400 - 1000 nm). As low as 0.06% H{sub 2} concentration was clearly sensed. A significant reversible absorbance change and fast recovery (<2 min) were observed when the films were exposed to H{sub 2} at different concentrations.

  6. Synthesis of WO3 flower-like hierarchical architectures and their sensing properties

    International Nuclear Information System (INIS)

    Meng, Dan; Wang, Guosheng; San, Xiaoguang; Song, Yinmin; Shen, Yanbai; Zhang, Yajing; Wang, Kangjun; Meng, Fanli

    2015-01-01

    WO 3 flower-like hierarchical architectures were synthesized by hydrothermal process using sodium tungstate (Na 2 WO 4 ·2H 2 O) as tungsten source and citric acid (CA) as an assistant agent. The morphology and crystal structure were investigated using scanning electron microscope and X-ray diffractometer. It is found that CA played a significant role in governing morphologies of product during hydrothermal process. The obtained products were identified as triclinic crystal WO 3 structure. The ethanol gas sensing measurements showed that well-defined WO 3 flower-like structures synthesized at CA/W molar ratio of 1 with large specific surface area exhibited the higher responses compared with others at all operating temperatures. Moreover, the reversible and fast response to ethanol gas at various gas concentrations and good selectivity were obtained. The results indicated that the WO 3 flower-like hierarchical architectures are promising materials for gas sensors. - Highlights: • WO 3 flower-like structures were successfully synthesized by hydrothermal method. • The effect of citric acid amount on morphologies was investigated. • Good ethanol gas sensing properties of WO 3 flower-like structures were obtained

  7. Cr2O3 nanoparticle-functionalized WO3 nanorods for ethanol gas sensors

    Science.gov (United States)

    Choi, Seungbok; Bonyani, Maryam; Sun, Gun-Joo; Lee, Jae Kyung; Hyun, Soong Keun; Lee, Chongmu

    2018-02-01

    Pristine WO3 nanorods and Cr2O3-functionalized WO3 nanorods were synthesized by the thermal evaporation of WO3 powder in an oxidizing atmosphere, followed by spin-coating of the nanowires with Cr2O3 nanoparticles and thermal annealing in an oxidizing atmosphere. Scanning electron microscopy was used to examine the morphological features and X-ray diffraction was used to study the crystallinity and phase formation of the synthesized nanorods. Gas sensing tests were performed at different temperatures in the presence of test gases (ethanol, acetone, CO, benzene and toluene). The Cr2O3-functionalized WO3 nanorods sensor showed a stronger response to these gases relative to the pristine WO3 nanorod sensor. In particular, the response of the Cr2O3-functionalized WO3 nanorods sensor to 200 ppm ethanol gas was 5.58, which is approximately 4.4 times higher that of the pristine WO3 nanorods sensor. Furthermore, the Cr2O3-functionalized WO3 nanorods sensor had a shorter response and recovery time. The pristine WO3 nanorods had no selectivity toward ethanol gas, whereas the Cr2O3-functionalized WO3 nanorods sensor showed good selectivity toward ethanol. The gas sensing mechanism of the Cr2O3-functionalized WO3 nanorods sensor toward ethanol is discussed in detail.

  8. Mesoporous amorphous tungsten oxide electrochromic films: a Raman analysis of their good switching behavior

    International Nuclear Information System (INIS)

    Chatzikyriakou, Dafni; Krins, Natacha; Gilbert, Bernard; Colson, Pierre; Dewalque, Jennifer; Denayer, Jessica; Cloots, Rudi; Henrist, Catherine

    2014-01-01

    Graphical abstract: - Highlights: • Mesoporous films exhibit better electrochemical kinetics compared to the dense films. • Mesoporous films exhibit better reversibility compared to the dense films. • Li + cations disrupt WO 3 network in a reversible way in the mesoporous film. • Li + irreversibly intercalate in the voids of crystallites in the dense film. - Abstract: The intercalation and de-intercalation of lithium cations in electrochromic tungsten oxide thin films are significantly influenced by their structural and surface characteristics. In this study, we prepared two types of amorphous films via the sol-gel technique: one dense and one mesoporous in order to compare their response upon lithium intercalation and de-intercalation. According to chronoamperometric measurements, Li + intercalates/de-intercalates faster in the mesoporous film (24s/6s) than in the dense film (48s/10s). The electrochemical measurements (cyclic voltammetry and chronoamperometry) also showed worse reversibility for the dense film compared to the mesoporous film, giving rise to important Li + trapping and remaining coloration of the film. Raman analysis showed that the mesoporous film provides more accessible and various W-O surface bonds for Li + intercalation. On the contrary, in the first electrochemical insertion and de-insertion in the dense film, Li + selectively reacts with a few surface W-O bonds and preferentially intercalates into pre-existing crystallites to form stable irreversible Li x WO 3 bronze

  9. Tungsten oxide thin film exposed to low energy D and He plasma: evidence for a thermal enhancement of the erosion yield

    Science.gov (United States)

    Hijazi, Hussein; Martin, C.; Roubin, P.; Addab, Y.; Cabie, C.; Pardanaud, C.; Bannister, M.; Meyer, F.

    2017-10-01

    Nanocrystalline tungsten oxide thin films (25 nm - 250 nm thickness) produced by thermal oxidation of a tungsten substrate were exposed to low energy D and He plasma. Low energy D plasma exposure (11 eV/D+) of these films have resulted in the formation of a tungsten bronze (DxWO3) clearly observed by Raman microscopy. D plasma bombardment (4 1021 m-2) has also induced a color change of the oxide layer which is similar to the well-known electro-chromic effect and has been named ``plasma-chromic effect''. To unravel physical and chemical origins of the modifications observed under exposure, similar tungsten oxide films were also exposed to low energy helium plasma (20 eV/He+) . Due to the low fluence (4 1021 m-2) and low ion energy (20 eV), at room temperature, He exposure has induced only very few morphological and structural modifications. On the contrary, at 673 K, significant erosion is observed, which gives evidence for an unexpected thermal enhancement of the erosion yield. We present here new results concerning He beam exposures at low fluence (4 1021 m-2) varying the He+ energy from 20 eV to 320 eV to measure the tungsten oxide sputtering threshold energy. Detailed analyses before/after exposure to describe the D and He interaction with the oxide layer, its erosion and structural modification at the atomic and micrometer scale will be presented.

  10. TiO_2/WO_3 photoactive bilayers in the UV-Vis light region

    International Nuclear Information System (INIS)

    Vasilaki, E.; Vernardou, D.; Kenanakis, G.; Katsarakis, N.; Vamvakaki, M.

    2017-01-01

    In this work, photoactive bilayered films consisting of anatase TiO_2 and monoclinic WO_3 were synthesized by a sol-gel route. Titanium isopropoxide and tungsten hexachloride were used as metal precursors and deposition was achieved by spin-coating on Corning glass substrates. The samples were characterized by X-ray diffraction, photoluminescence, UV-Vis, and Raman spectroscopy, as well as field emission scanning electron microscopy. The prepared immobilized catalysts were tested for their photocatalytic performance by the decolorization of methylene blue in aqueous matrices, under UV-Vis light irradiation. The annealing process influenced the crystallinity of the bilayered films, while the concentration of the tungsten precursor solution and the position of the tungsten trioxide layer further affected their photocatalytic performance. In particular, the photocatalytic performance of the bilayered films was optimized at a concentration of 0.1 M of the WO_3 precursor solution, when deposited as an overlying layer on TiO_2 by two annealing steps (∝76% methylene blue decolorization in 300 min of irradiation versus ∝59% in the case of a bare TiO_2 film). In general, the coupled layer catalysts exhibited superior photoactivity compared to that of bare TiO_2 films with WO_3 acting as an electron trap, resulting, therefore, in a more efficient electron-hole separation and inhibiting their recombination. (orig.)

  11. Immobilized WO3 nanoparticles on graphene oxide as a photo-induced antibacterial agent against UV-resistant Bacillus pumilus

    Science.gov (United States)

    Hosseini, Farshad; Rasuli, Reza; Jafarian, Vahab

    2018-04-01

    We present the antibacterial and photo-catalytic activity of immobilized WO3 nanoparticles on graphene oxide sheets. WO3 nanoparticles were immobilized on graphene oxide using the arc discharge method in arc currents of 5, 20, 40 and 60 A. Tauc plots of the UV-visible spectra show that the band gap of the prepared samples decreases (to ~2.7 eV) with respect to the WO3 nanoparticles. Photo-catalytic activity was examined by the degradation of rhodamine B under ultra-violet irradiation and the results show that the photo-catalytic activity of WO3 nanoparticles is increased by immobilizing them on graphene oxide sheets. In addition, the photo-degradation yield of the samples prepared by the 5 A arc current is 84% in 120 min, which is more than that of the other samples. The antibacterial activity of the prepared samples was studied against Bacillus pumilus (B. pumilus) bacteria, showing high resistance to ultra-violet exposure. Our results show that the bare and immobilized WO3 nanoparticles become more active under UV irradiation and their antibacterial properties are comparable with Ag nanoparticles. Besides this, the results show that although the photo-catalytic activity of the post-annealed samples at 500 °C is less than the as-prepared samples, it is, however, more active against B. pumilus bacteria under UV irradiation.

  12. Understanding the conductive channel evolution in Na:WO(3-x)-based planar devices.

    Science.gov (United States)

    Shang, Dashan; Li, Peining; Wang, Tao; Carria, Egidio; Sun, Jirong; Shen, Baogen; Taubner, Thomas; Valov, Ilia; Waser, Rainer; Wuttig, Matthias

    2015-04-14

    An ion migration process in a solid electrolyte is important for ion-based functional devices, such as fuel cells, batteries, electrochromics, gas sensors, and resistive switching systems. In this study, a planar sandwich structure is prepared by depositing tungsten oxide (WO(3-x)) films on a soda-lime glass substrate, from which Na(+) diffuses into the WO(3-x) films during the deposition. The entire process of Na(+) migration driven by an alternating electric field is visualized in the Na-doped WO(3-x) films in the form of conductive channel by in situ optical imaging combined with infrared spectroscopy and near-field imaging techniques. A reversible change of geometry between a parabolic and a bar channel is observed with the resistance change of the devices. The peculiar channel evolution is interpreted by a thermal-stress-induced mechanical deformation of the films and an asymmetric Na(+) mobility between the parabolic and the bar channels. These results exemplify a typical ion migration process driven by an alternating electric field in a solid electrolyte with a low ion mobility and are expected to be beneficial to improve the controllability of the ion migration in ion-based functional devices, such as resistive switching devices.

  13. The effect of phosphorus on the formation of tungsten dioxide: A novel morphology

    International Nuclear Information System (INIS)

    Hegedus, E.; Neugebauer, J.

    1999-01-01

    The industrial production of tungsten is based on the hydrogen reduction of tungsten oxides, ammonium paratungstate (APT) or ammonium tungsten oxide bronze (ATOB). Hydrogen reduction is applied when high purity tungsten is required and when the addition of other elements or compounds (dopants) is desired for modification of the properties of the metal powder. The first stage of the reduction is finished when WO 2 is formed and it seems that the efficient incorporation of the additives starts mainly at this reduction step. The study reported here was undertaken to investigate the effect of phosphorus dope on the morphology of the intermediate tungsten dioxide and analyze its influence on the grain size of the final tungsten metal powder. The authors observed star shaped morphology of WO 2 , a structure which has not been describe in the literature. Contrary to the well-known cauliflower shaped tungsten dioxide, these starlets are not pseudomorphic to the initial ATOB particles; they grow separately and have a great influence on the grain size of the final metal powder

  14. Effects of deposition and annealing atmospheres on phase transition of tungsten oxide films grown by ultra-high-vacuum reactive sputtering

    International Nuclear Information System (INIS)

    Ghen, G.S.; Liao, W.L.; Chen, S.T.; Su, W.C.; Lin, C.K.

    2005-01-01

    A series of oxygen-contained tungsten films were grown on Si(100) substrates without intentional heating by ultra-high-vacuum reactive magnetron sputtering at a constant argon pressure (P Ar ) of 1.33 x 10 -1 Pa mixed with a wide range of O 2 partial pressures (P O ) from 1.33 x 10 -4 to 4 x 10 -1 Pa, equivalent to P O -to-P Ar ratios (P O/Ar ) from 1 x 10 -3 to 3. The effect of varying P O/Ar on phase evolution was evaluated by annealing the films in a controlled atmosphere (argon or oxygen) at 500 or 700 deg. C for 1 h. Grazing incident X-ray diffraction and transmission electron microscopy, together with the data of electrical resistivity and deposition rate, reveal that gradually increasing P O/Ar induces a sequence of phase transitions from nanocrystalline β-W(O) (P O/Ar ≤ 0.1), amorphous WO 2 (P O/Ar = 0.6) to amorphous WO 3 (P O/Ar ≥ 2). When annealed in argon atmosphere, the amorphous WO 2 and WO 3 exhibit a very different magnitude of crystallization temperature (T c ) and can be transformed, respectively, into monoclinic WO 2 (T c = 500 deg. C) and tetragonal WO 3 (T c = 700 deg. C). However, the oxidizing atmosphere plays a role to accelerate significantly the crystallization of the amorphous WO 2 into a completely different phase (monoclinic WO 3 ) at a significantly reduced T c of 500 deg. C

  15. Robust superhydrophobic tungsten oxide coatings with photochromism and UV durability properties

    Energy Technology Data Exchange (ETDEWEB)

    Jiang, Ting [Hubei Collaborative Innovation Centre for Advanced Organic Chemical Materials and Ministry-of-Education Key Laboratory for the Green Preparation and Application of Functional Materials, Hubei University, Wuhan, 430062 (China); State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000 (China); Guo, Zhiguang, E-mail: zguo@licp.cas.cn [Hubei Collaborative Innovation Centre for Advanced Organic Chemical Materials and Ministry-of-Education Key Laboratory for the Green Preparation and Application of Functional Materials, Hubei University, Wuhan, 430062 (China); State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000 (China)

    2016-11-30

    Highlights: • Superhydrophobic tungsten oxide (TO) coatings with a water contact angle (WCA) of 155° and rolling angle of 3.5° were developed. • The superhydrophobic coatings have excellent mechanical robustness and UV durability. • The superhydrophobic TO coatings show the reversible convert of photochromism. • The coating exhibited excellent self-cleaning behavior due to its high WCA and low rolling angle. - Abstract: Robust superhydrophobic tungsten oxide (TO) coatings with a water contact angle (WCA) of 155° were developed for photochromism via a facile and substrate-independent route. Importantly, after scatch test on both a single and two orthogonal direction, the TO coating still exhibited superhydrophobic behavior, indicating excellent mechanical robustness. It is worth mentioning that the superhydrophobic TO coatings showed the reversible convert of photochromism of WO{sub 3} induced by alternating UV and visible light irradiation. Besides that, the TO coating remained superhydrophobicity after UV irradiation for 36 h, showing excellent UV durability. In addition, the coating showed good resistance to acidic droplets. Moreover, it can also be applied on other substrates, such as copper mesh, steel, paper and fiber. The coating exhibited excellent self-cleaning behavior due to its high WCA and low rolling angle. Overall, this work is a promising approach to design and produce functional superhydrophobic coatings for various substrates.

  16. Mesoporous WN/WO3-Composite Nanosheets for the Chemiresistive Detection of NO2 at Room Temperature

    Directory of Open Access Journals (Sweden)

    Fengdong Qu

    2016-07-01

    Full Text Available Composite materials, which can optimally use the advantages of different materials, have been studied extensively. Herein, hybrid tungsten nitride and oxide (WN/WO3 composites were prepared through a simple aqueous solution route followed by nitriding in NH3, for application as novel sensing materials. We found that the introduction of WN can improve the electrical properties of the composites, thus improving the gas sensing properties of the composites when compared with bare WO3. The highest sensing response was up to 21.3 for 100 ppb NO2 with a fast response time of ~50 s at room temperature, and the low detection limit was 1.28 ppb, which is far below the level that is immediately dangerous to life or health (IDLH values (NO2: 20 ppm defined by the U.S. National Institute for Occupational Safety and Health (NIOSH. In addition, the composites successfully lower the optimum temperature of WO3 from 300 °C to room temperature, and the composites-based sensor presents good long-term stability for NO2 of 100 ppb. Furthermore, a possible sensing mechanism is proposed.

  17. Formation of self-ordered porous anodized alumina template for growing tungsten trioxide nanowires

    Science.gov (United States)

    Hussain, Tajamal; Shah, Asma Tufail; Shehzad, Khurram; Mujahid, Adnan; Farooqi, Zahoor Hussain; Raza, Muhammad Hamid; Ahmed, Mirza Nadeem; Nisa, Zaib Un

    2015-12-01

    Uniform porous anodized aluminum oxide (AAO) membrane has been synthesized by two-step anodization for fabricating tungsten trioxide (WO3) nanowires. Under assayed conditions, uniform porous structure of alumina (Al2O3) membrane with long range ordered hexagonal arrangements of nanopores was achieved. The self-assembled template possesses pores of internal diameter of 50 nm and interpore distance ( d int) of 80 nm with a thickness of about 80 µm, i.e., used for fabrication of nanostructures. WO3 nanowires have been fabricated by simple electroless deposition method inside Al2O3 nanopores. SEM images show tungsten trioxide nanowire with internal diameter of about 50 nm, similar to porous diameter of AAO template. XRD results showed that nanowires exist in cubic crystalline state with minor proportion of monoclinic phase.

  18. NH{sub 4}-doped anodic WO{sub 3} prepared through anodization and subsequent NH{sub 4}OH treatment for water splitting

    Energy Technology Data Exchange (ETDEWEB)

    Choi, Yong-Wook; Kim, Sunkyu; Seong, Mijeong; Yoo, Hyeonseok; Choi, Jinsub, E-mail: jinsub@inha.ac.kr

    2015-01-01

    Highlights: • NN{sub 4}-doped WO{sub 3} was successfully fabricated by a wet-based method using ammonium hydroxide (NH{sub 4}OH). • (NH{sub 4}){sub 10}W{sub 12}O{sub 41} phase was formed during the NH{sub 4}OH treatment. • Over-doped NH{sub 4} in WO{sub 3} led to reduced photo-electrochemical performance for OER. • The optimized surface was achieved by thermal treatment of anodic WO{sub 3} with 2 g of NH{sub 4}OH solution. - Abstract: Tungsten trioxide (WO{sub 3}) prepared by anodization of a W foil was doped with NH{sub 4} through NH{sub 4}OH treatment at 450 °C. Since aqueous NH{sub 4}OH was used during doping instead of NH{sub 3} gas, the treatment step does not require complicated annealing facilities. Moreover, the state of doped N is a form of NH{sub 3}-W instead of W{sub 2}N, which lowers the bandgap but increases photocorrosion. We found that incorporation of NH{sub 4} into WO{sub 3} leads to reduction of the bandgap from 2.9 eV to 2.2 eV, regardless of the amount of NH{sub 4}OH treatment, lowering the onset potential and increasing the current density at fixed potential for oxygen evolution reaction under illumination. Scanning electron microscopy, X-ray diffraction and X-ray photoelectron spectroscopy were employed to investigate the surface morphologies, crystallinities of tungsten oxides and existence of NH{sub 4} doping, respectively. The bandgap energy was determined by UV–Vis spectroscopy to measure the transmittance and refraction. The water splitting performance of each sample was measured by electrochemical linear sweep voltammetry in a 3-electrode configuration under illumination.

  19. Self Assembly and Properties of C:WO3 Nano-Platelets and C:VO2/V2O5 Triangular Capsules Produced by Laser Solution Photolysis

    Directory of Open Access Journals (Sweden)

    Sideras-Haddad E

    2009-01-01

    Full Text Available Abstract Laser photolysis of WCl6 in ethanol and a specific mixture of V2O5 and VCl3 in ethanol lead to carbon modified vanadium and tungsten oxides with interesting properties. The presence of graphene’s aromatic rings (from the vibrational frequency of 1,600 cm−1 together with C–C bonding of carbon (from the Raman shift of 1,124 cm−1 present unique optical, vibrational, electronic and structural properties of the intended tungsten trioxide and vanadium dioxide materials. The morphology of these samples shows nano-platelets in WO x samples and, in VO x samples, encapsulated spherical quantum dots in conjunction with fullerenes of VO x . Conductivity studies revealed that the VO2/V2O5 nanostructures are more sensitive to Cl than to the presence of ethanol, whereas the C:WO3 nano-platelets are more sensitive to ethanol than atomic C.

  20. Effects of oxygen contents on the electrochromic properties of tungsten oxide films prepared by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Lu, H.-H.

    2008-01-01

    The electrochromism have been extensively investigated due to their potential applications such as smart window of architecture and automobile glazing to save energy and modulate the transmittance of light and solar radiation. The objective of this study is to investigate the effects of sputtering conditions on the microstructure and electrochromic properties of tungsten oxide films prepared by dc reactive magnetron sputtering. Experimental results showed that the deposition rate of WO 3-y films decreased with increasing oxygen flow rate. XRD and Raman spectra analysis suggests that the WO 3-y films deposited at various oxygen flow rates are poor crystallinity or amorphous. The transmission change between colored and bleached states at a wavelength of 550 nm was 61.4% as the oxygen content was 60%. The coloration efficiency slightly increases with increasing oxygen flow rate in the low oxygen content region and reaching a maximum value of 38.94 cm 2 /C at 60% oxygen content. In addition, the films deposited at 60% oxygen content showed a good reversibility. The effects of lithium ions intercalated on the transmission of WO 3-y films were also discussed

  1. Catalytic activity of tungsten carbide-carbon (WC@C) core-shell structured for ethanol electro-oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Singla, Gourav, E-mail: gsinghla@gmail.com; Singh, K., E-mail: kusingh@thapar.edu; Pandey, O.P., E-mail: oppandey@thapar.edu

    2017-01-15

    In this study, carbon coated WC (WC@C) was synthesized through solvothermal reactions in the presence of reducing agent magnesium (Mg) by employing tungsten oxide (WO{sub 3}) as a precursor, acetone (C{sub 3}H{sub 6}O) as a carbon source. The formation of WC@C nano particles is confirmed by X-ray diffraction and Transmission electron microscopy. The thermal stability of the synthesized powder examined in air shows its stability up to 550 °C. In this method, in-situ produced outer carbon layer increase the surface area of materials which is 52.6 m{sup 2} g{sup −1} with pore volume 0.213 cm{sup 3} g{sup −1}. The Electrocatalytic activity of ethanol oxidation on a synthesized sample with and without Pt nano particles have been investigated using cyclic voltammetry (CV). The CV results show the enhancement in oxidation stability of WC@C in acidic media as well as better CO-tolerance for ethanol oxidation after the deposition of Pt nanoparticles as compared to without Pt nano particles. - Highlights: • Tungsten carbide nano powder was synthesized using acetone as carbon source. • In-situ produced outer carbon layer increase the surface area of materials. • Mesoporous WC with surface areas 52.6 m{sup 2}/g obtained. • Pt modified WC powder showed higher electrochemical stability. • Better CO-tolerance for ethanol oxidation after the deposition of Pt nanoparticles.

  2. Oxidative degradation of salicylic acid by sprayed WO{sub 3} photocatalyst

    Energy Technology Data Exchange (ETDEWEB)

    Mohite, S.V.; Rajpure, K.Y., E-mail: rajpure@yahoo.com

    2015-10-15

    Highlights: • The photoactivity of sprayed WO{sub 3} thin film. • Photoelectrocatalytic degradation of salicylic acid. • Reaction kinetics and mineralization of pollutants by COD. - Abstract: The WO{sub 3} thin films were deposited using spray pyrolysis technique. The prepared WO{sub 3} thin films were characterized using photoelectrochemical (PEC), X-ray diffraction, atomic force microscopy (AFM), and UV–vis absorbance spectroscopy techniques. PEC measurements of WO{sub 3} films deposited at different deposition temperatures were carried out to study photoresponse. The maximum photocurrent (I{sub ph} = 261 μA/cm{sup 2}) was observed for the film deposited at the 225 °C. The monoclinic crystal structure of WO{sub 3} has been confirmed from X-ray diffraction studies. AFM studies were used to calculate particle size and average roughness of the films. Optical absorbance was studied to estimate the bandgap energy of WO{sub 3} thin film which was about 2.65 eV. The photoelectrocatalytic activity of WO{sub 3} film was studied by degradation of salicylic acid with reducing concentrations as function of reaction time. The WO{sub 3} photocatalyst degraded salicylic acid to about 67.14% with significant reduction in chemical oxygen demand (COD) value.

  3. Recent progress in tungsten oxides based memristors and their neuromorphological applications

    Science.gov (United States)

    Qu, Bo; Younis, Adnan; Chu, Dewei

    2016-09-01

    The advance in conventional silicon based semiconductor industry is now becoming indeterminacy as it still along the road of Moore's Law and concomitant problems associated with it are the emergence of a number of practical issues such as short channel effect. In terms of memory applications, it is generally believed that transistors based memory devices will approach to their scaling limits up to 2018. Therefore, one of the most prominent challenges today in semiconductor industry is the need of a new memory technology which is able to combine the best characterises of current devices. The resistive switching memories which are regarded as "memristors" thus gain great attentions thanks to their specific nonlinear electrical properties. More importantly, their behaviour resembles with the transmission characteristic of synapse in biology. Therefore, the research of synapses biomimetic devices based on memristor will certainly bring a great research prospect in studying synapse emulation as well as building artificial neural networks. Tungsten oxides (WO x ) exhibits many essential characteristics as a great candidate for memristive devices including: accredited endurance (over 105 cycles), stoichiometric flexibility, complimentary metal-oxide-semiconductor (CMOS) process compatibility and configurable properties including non-volatile rectification, memorization and learning functions. Herein, recent progress on Tungsten oxide based materials and its associating memory devices had been reviewed. The possible implementation of this material as a bio-inspired artificial synapse is also highlighted. The penultimate section summaries the current research progress for tungsten oxide based biological synapses and end up with several proposals that have been suggested for possible future developments.

  4. Cathodic electrodeposition of mixed molybdenum tungsten oxides from peroxo-polymolybdotungstate solutions.

    Science.gov (United States)

    Kondrachova, Lilia; Hahn, Benjamin P; Vijayaraghavan, Ganesh; Williams, Ryan D; Stevenson, Keith J

    2006-12-05

    Mixed molybdenum tungsten trioxide films of varying stoichiometry (MoxW1 - xO3, 0 cathodic electrodeposition on indium tin oxide (ITO)-coated glass substrates from aqueous peroxo-polymolybdotungstate solutions. Electrochemical quartz crystal microbalance (EQCM), cyclic voltammetry, and chronocoulometry were used to gain insight into the electrodeposition mechanism. The compositional and structural properties were characterized for MoxW1 - xO3 films deposited at intermediate potentials (-0.35 V vs Ag/AgCl) and sintered at 250 degrees C using energy-dispersive spectroscopy, X-ray diffraction, and Raman spectroscopy. These studies reveal that films consist of homogeneously mixed MoxW1 - xO3, with an enriched Mo content ranging in composition from 0.4 < x < 0.7 depending upon the mol % Mo present in the deposition solution. Chronoamperometry and spectroelectrochemical measurements were conducted to estimate lithium ion diffusion coefficients and coloration efficiencies for the mixed metal oxide films in 1 M LiClO4/propylene carbonate. The subtle interplay between structural and compositional properties due to the uniform mixing of Mo and W oxide components shows that electrochromic and lithium ion transport properties are moderately enhanced relative to those of single-component WO3 and MoO3 and demonstrate improved structural stability over pure MoO3 polymorphs during electrochemical cycling.

  5. Electron beam induced coloration and luminescence in layered structure of WO3 thin films grown by pulsed dc magnetron sputtering

    International Nuclear Information System (INIS)

    Karuppasamy, A.; Subrahmanyam, A.

    2007-01-01

    Tungsten oxide thin films have been deposited by pulsed dc magnetron sputtering of tungsten in argon and oxygen atmosphere. The as-deposited WO 3 film is amorphous, highly transparent, and shows a layered structure along the edges. In addition, the optical properties of the as-deposited film show a steplike behavior of extinction coefficient. However, the electron beam irradiation (3.0 keV) of the as-deposited films results in crystallization, coloration (deep blue), and luminescence (intense red emission). The above changes in physical properties are attributed to the extraction of oxygen atoms from the sample and the structural modifications induced by electron bombardment. The present method of coloration and luminescence has a potential for fabricating high-density optical data storage device

  6. Incorporation of tantalum ions enhances the electrocatalytic activity of hexagonal WO3 nanowires for hydrogen evolution reaction

    International Nuclear Information System (INIS)

    Xie, Xiang; Mu, Wanjun; Li, Xingliang; Wei, Hongyuan; Jian, Yuan; Yu, Qianhong; Zhang, Rui; Lv, Kai; Tang, Hui; Luo, Shunzhong

    2014-01-01

    WO 3 has been identified as a promising candidate electrocatalyst for hydrogen evolution reaction (HER), because it can form a tungsten bronze (HxWO 3 ) which is highly electron and proton conducting. In this paper, we report that the electrocatalytic activity of WO 3 for HER can be enhanced by incorporation of tantalum ions (Ta 5+ ) into the lattice of WO 3 . The most active performance is achieved with the molar ratio of Ta/W being 0.01, which is two times more active than that of undoped WO 3 at an overpotential of -0.52 V. It is shown that incorporation of proper Ta 5+ into WO 3 can induce moderate defects and oxygen vacancies, as well as intercalate a higher amount of protons, which enhance the electron transfer and short the protons diffusion paths. These changes correlated positively with the enhanced catalytic HER activity. This study demonstrates, for the first time, that metal ions-doped WO 3 nanowires are promising electrocatalysts for HER

  7. Using reduced graphene oxide-Ca:CdSe nanocomposite to enhance photoelectrochemical activity of gold nanoparticles functionalized tungsten oxide for highly sensitive prostate specific antigen detection.

    Science.gov (United States)

    Wang, Xueping; Xu, Rui; Sun, Xu; Wang, Yaoguang; Ren, Xiang; Du, Bin; Wu, Dan; Wei, Qin

    2017-10-15

    An ultrasensitive sandwich-type photoelectrochemical (PEC) immunosensor was constructed for the detection of prostate specific antigen (PSA). In this work, Au-nanoparticle-loaded tungsten oxide (WO 3 -Au) hybrid composites was applied as PEC sensing platform, while Ca ions doped CdSe equipped on the conducting framework of reduced graphene oxide (rGO-Ca:CdSe) nanocomposites were employed as the signal amplification probe. As for WO 3 -Au, massive Au nanoparticles were formed on the surface of WO 3 without any additional reducing agent, providing a novel nanocarriers for anchoring plenty of the primary antibodies due to the large specific surface area and good biocompatibility by chemical bonding between Au nanoparticles and -NH 2 of antibodies. Besides, the incorporation of the rGO and the doping of Ca ions could improve the conductivity and hinder the recombination of electron-hole pairs of CdSe nanoparticles effectively, thereby enhancing the photocurrent conversion efficiency. Based on the sandwich immunoreaction, the primary antibody was immobilized onto WO 3 -Au substrate, after the formed rGO-Ca:CdSe labels were captured onto the electrode surface via the specific antibody-antigen interaction, the photocurrent intensity could be further enhanced due to the sensitization effect. Under the optimal conditions, the proposed PEC immunosensor shows a linear relationship between photocurrent variation and the logarithm of PSA concentration in the wide range of 5pgmL -1 to 50ngmL -1 with a low detection limit of 2.6pgmL -1 (S/N=3). Moreover, it also presented good stability and acceptable specificity, indicating the potential applications in clinical diagnostics. Copyright © 2017 Elsevier B.V. All rights reserved.

  8. TiO{sub 2}/WO{sub 3} photoactive bilayers in the UV-Vis light region

    Energy Technology Data Exchange (ETDEWEB)

    Vasilaki, E. [University of Crete, Department of Chemistry, Heraklion, Crete (Greece); Technological Educational Institute of Crete, Center of Materials Technology and Photonics, School of Engineering, Heraklion, Crete (Greece); Vernardou, D. [Technological Educational Institute of Crete, Center of Materials Technology and Photonics, School of Engineering, Heraklion, Crete (Greece); Kenanakis, G.; Katsarakis, N. [Technological Educational Institute of Crete, Center of Materials Technology and Photonics, School of Engineering, Heraklion, Crete (Greece); Foundation for Research and Technology-Hellas, Institute of Electronic Structure and Laser, Vassilika Vouton, P.O. Box 1385, Heraklion, Crete (Greece); Vamvakaki, M. [Foundation for Research and Technology-Hellas, Institute of Electronic Structure and Laser, Vassilika Vouton, P.O. Box 1385, Heraklion, Crete (Greece); University of Crete, Department of Materials Science and Technology, Heraklion, Crete (Greece)

    2017-04-15

    In this work, photoactive bilayered films consisting of anatase TiO{sub 2} and monoclinic WO{sub 3} were synthesized by a sol-gel route. Titanium isopropoxide and tungsten hexachloride were used as metal precursors and deposition was achieved by spin-coating on Corning glass substrates. The samples were characterized by X-ray diffraction, photoluminescence, UV-Vis, and Raman spectroscopy, as well as field emission scanning electron microscopy. The prepared immobilized catalysts were tested for their photocatalytic performance by the decolorization of methylene blue in aqueous matrices, under UV-Vis light irradiation. The annealing process influenced the crystallinity of the bilayered films, while the concentration of the tungsten precursor solution and the position of the tungsten trioxide layer further affected their photocatalytic performance. In particular, the photocatalytic performance of the bilayered films was optimized at a concentration of 0.1 M of the WO{sub 3} precursor solution, when deposited as an overlying layer on TiO{sub 2} by two annealing steps (∝76% methylene blue decolorization in 300 min of irradiation versus ∝59% in the case of a bare TiO{sub 2} film). In general, the coupled layer catalysts exhibited superior photoactivity compared to that of bare TiO{sub 2} films with WO{sub 3} acting as an electron trap, resulting, therefore, in a more efficient electron-hole separation and inhibiting their recombination. (orig.)

  9. Gas Sensing Properties of Pure and Cr Activated WO3 Thick Film Resistors

    Directory of Open Access Journals (Sweden)

    V. B. GAIKWAD

    2010-09-01

    Full Text Available Thick films of WO3 (Tungsten Oxide were prepared by screen-printing techniques. The surfaces of the films were modified by dipping them into an aqueous solution of Chromium Oxide (CrO3 for different intervals of time, followed by firing at 550 oC for 30 min. The gas sensing performance of the pure and Cr2O3-modified films was tested for various gases at different temperatures. The unmodified films showed response to H2S, ethanol and cigar smoke. However Cr2O3- modified films suppresses gas sensing response to all gases except H2S. The surface modification, using dipping process, altered the adsorbate-adsorbent interactions, which gave the specific selectivity and enhanced sensitivity to H2S gas. The gas response, selectivity, thermal stability and recovery time of the sensor were measured and presented. The role played by surface chromium species to improve gas sensing performance is discussed.

  10. Tungsten Oxide Nanofibers Self-assembled Mesoscopic Microspheres as High-performance Electrodes for Supercapacitor

    International Nuclear Information System (INIS)

    Xu, Juan; Ding, Taotao; Wang, Jin; Zhang, Jun; Wang, Shuai; Chen, Changqing; Fang, Yanyan; Wu, Zhihao; Huo, Kaifu; Dai, Jiangnan

    2015-01-01

    Highlights: • WO 3 mesoscopic microspheres self-assembled by nanofibers. • Inorganic solvent H 2 O 2 play an integral role in the process of self-assembly. • WO 3 mesoscopic microspheres exhibit specific capacitance value of 797.05 F g −1 at a constant density of 0.5 A g −1 in 2 M H 2 SO 4 aqueous solution. • The WO 3 //AC asymmetric supercapacitor displays a maximum energy density of 97.61 Wh kg −1 and power density of 28.01 kW kg −1 . - Abstract: Mesoscopic WO 3 microspheres composed of self-assembly nanofibers were prepared by hydrothermal reaction of tungsten acid potassium and H 2 O 2 . The mesoscopic WO 3 microspheres offer desired porous properties and large effective active areas provided by intertwining nanofibers, thereby resulting in excellent supercapacitive properties due to facile electrolyte flow and fast reaction kinetics. In three electrode configuration, mesoscopic WO 3 microspheres exhibit specific capacitance value of 797.05 F g −1 at the current density of 0.5 A g −1 and excellent cycling stability without decay after 2000 cycles in 2 M H 2 SO 4 aqueous solution. These values are superior to other reported WO 3 composites. An asymmetric supercapacitor is constructed using the as-prepared WO 3 mesoscopic microspheres as the positive electrode and the activated carbon as the negative electrode, which displays excellent electrochemical performance with a maximum energy density of 97.61 Wh kg −1 and power density of 28.01 kW kg −1 . These impressive performances suggest that the mesoscopic WO 3 microspheres are promising electrode materials for supercapacitor

  11. Preparation of WO3/g-C3N4 composites and their application in oxidative desulfurization

    International Nuclear Information System (INIS)

    Zhao, Rongxiang; Li, Xiuping; Su, Jianxun; Gao, Xiaohan

    2017-01-01

    Highlights: • The WO 3 /g-C 3 N 4 was successfully synthesized through simple calcination. • The process is simple and the cost raw materials is cheap. • The WO 3 /g-C 3 N 4 firstly applied to ODS. • The desulpurization rate of WO 3 /g-C 3 N 4 may attach to 91.2%. • Five recycles of WO 3 /g-C 3 N 4 still attach to 89.5% due to heterogeneous catalysis. - Abstract: WO 3 /graphitic carbon nitride (g-C 3 N 4 ) composites were successfully synthesized through direct calcining of a mixture of WO 3 and g-C 3 N 4 at 400 °C for 2 h. The WO 3 was prepared by calcination of phosphotungstic acid at 550 °C for 4 h, and the g-C 3 N 4 was obtained by calcination of melamine at 520 °C for 4 h. The WO 3 /g-C 3 N 4 composites were characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FT-IR), and Brunner−Emmett−Teller analysis (BET). The WO 3 /g-C 3 N 4 composites exhibited stronger XRD peaks of WO 3 and g-C 3 N 4 than the WO 3 and pure g-C 3 N 4 . In addition, two WO 3 peaks at 25.7° and 26.6° emerged for the 36% −WO 3 /g-C 3 N 4 composite. This finding indicated that WO 3 was highly dispersed on the surface of the g-C 3 N 4 nanosheets and interacted with the nanosheets, which resulted in the appearance of (012) and (022) planes of WO 3 . The WO 3 /g-C 3 N 4 composite also exhibited a larger specific surface area and higher degree of crystallization than WO 3 or pure g-C 3 N 4 , which resulted in high catalytic activity of the catalyst. Desulfurization experiments demonstrated that the desulfurization rate of dibenzothiophene (DBT) in model oil reached 91.2% under optimal conditions. Moreover, the activity of the catalyst was not significantly decreased after five recycles.

  12. Crystal structure and phase transition in (NH4)3WO2F5: from dynamic to static orientational disorder.

    Science.gov (United States)

    Udovenko, Anatoly; Laptash, Natalia

    2015-08-01

    Single crystals of tungsten double salt (NH4)3WO2F5 = (NH4)3[WO2F4]F have been synthesized by solid-state reaction or from fluoride solution and its crystal structures at 296 and 193 K were determined by X-ray diffraction. At room temperature, the crystal structure of the compound is dynamically disordered with the ligand atoms statistically distributed on two positions (6e and 24m) of the Pm3m unit cell [a = 6.0298 (1) Å], and the tungsten atom dynamically disordered on 12 orientations forming a spatial cuboctahedron [W12] that enables the real geometry of cis-WO2F4 octahedron to be determined with two short W-O distances. On cooling, the compound undergoes a first-order phase transition with the symmetry change Pm3m → Pa3 and a doubling of the unit-cell parameter [a = 11.9635 (7) Å]. The ligand F(O) atoms statistically occupy two general 24d sites and form W1X6 and W2X6 octahedra, in which the O and F atoms are not crystallographically different that means a static orientational disorder of (NH4)3WO2F5.

  13. WO3 nanoflakes decorated with CuO clusters for enhanced photoelectrochemical water splitting

    Directory of Open Access Journals (Sweden)

    Chongwu Wang

    2018-04-01

    Full Text Available The low quantum efficiency arising from poor charges transfer and insufficient light absorption is one of the critical challenges toward achieving highly efficient water splitting in photoelectrochemical cells. Three dimensions (3D structures and heterojunctions have received intensive research interests recent years due to their excellent ability to separate photo-generated charges as well as the enhanced light harvesting property. Herein, 3D CuO/WO3 structure was fabricated through a facile solvothermal method followed by chemical bath deposition. The loading of CuO clusters on WO3 nanoflake arrays results in a much improved photocurrent density compared with that of pristine WO3 nanoflake arrays, which reaches 1.8 mA/cm2 at 1.23 V vs. the reversible hydrogen electrode. The electrochemical impedance spectroscopy measurement demonstrates that the improved performance of CuO/WO3 electrode is attributed to the accelerated charge transfer kinetics as a result of the desirable band alignment in CuO/WO3 heterojunction. This work demonstrates a facile strategy to construct superior WO3 electrode, which will ultimately allow for efficient storage of solar energy into hydrogen. Keywords: Photoelectrochemistry, Water splitting, Tungsten trioxide photoanode, CuO clusters, Heterojunction

  14. Effects of different petal thickness on gas sensing properties of flower-like WO3·H2O hierarchical architectures

    International Nuclear Information System (INIS)

    Zeng, Wen; Zhang, He; Wang, Zhongchang

    2015-01-01

    Graphical abstract: In this work, we prepare four different petal thicknesses of hierarchical WO 3 ·H 2 O architectures via a simple hydrothermal process, and systematically report their formation mechanisms and gas-sensing properties. - Highlights: • Flower-like WO 3 ·H 2 O architectures with different petal thickness were reported. • The WO 3 ·H 2 O sheet-flower sensor shows a significantly enhanced gas response. • A possible growth mechanism for the flower-like architectures is proposed. - Abstract: Hierarchical architectures consisting of two-dimensional (2D) nanostructures are of great interest for potential use in recent year. Here, we report the successful synthesis of four hierarchical tungsten oxide flower-like architectures via a simple yet facile hydrothermal method. The as-prepared WO 3 ·H 2 O hierarchical architectures are in fact assembled with numerous nanosheets or nanoplates. Through a comprehensive characterization of microstructures and morphologies of the as-prepared products, we find that petal thickness is a key factor for affecting gas-sensing performances. We further propose a possible growth mechanism for the four flower-like architectures. Moreover, gas-sensing measurements showed that the well-defined sheet-flower WO 3 ·H 2 O hierarchical architectures exhibited the excellent gas-sensing properties to ethanol owing to their largest amount of thin petal structures and pores

  15. Preparation of WO3/g-C3N4 composites and their application in oxidative desulfurization

    Science.gov (United States)

    Zhao, Rongxiang; Li, Xiuping; Su, Jianxun; Gao, Xiaohan

    2017-01-01

    WO3/graphitic carbon nitride (g-C3N4) composites were successfully synthesized through direct calcining of a mixture of WO3 and g-C3N4 at 400 °C for 2 h. The WO3 was prepared by calcination of phosphotungstic acid at 550 °C for 4 h, and the g-C3N4 was obtained by calcination of melamine at 520 °C for 4 h. The WO3/g-C3N4 composites were characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FT-IR), and Brunner-Emmett-Teller analysis (BET). The WO3/g-C3N4 composites exhibited stronger XRD peaks of WO3 and g-C3N4 than the WO3 and pure g-C3N4. In addition, two WO3 peaks at 25.7° and 26.6° emerged for the 36% -WO3/g-C3N4 composite. This finding indicated that WO3 was highly dispersed on the surface of the g-C3N4 nanosheets and interacted with the nanosheets, which resulted in the appearance of (012) and (022) planes of WO3. The WO3/g-C3N4 composite also exhibited a larger specific surface area and higher degree of crystallization than WO3 or pure g-C3N4, which resulted in high catalytic activity of the catalyst. Desulfurization experiments demonstrated that the desulfurization rate of dibenzothiophene (DBT) in model oil reached 91.2% under optimal conditions. Moreover, the activity of the catalyst was not significantly decreased after five recycles.

  16. Formation of tungsten blue oxide and its phase constitution

    International Nuclear Information System (INIS)

    Zou, Z.; Wu, E.; Tan, A.; Qian, C.

    1984-01-01

    By means of X-ray diffraction structure analysis, SEM observation, chemical analysis and particle specific surface analysis etc., an investigation was made in order to determine the regularity of tungsten blue oxide formation during reductional calcine process of APT. It was found that the oxygen index (OI) decreased continuously with increasing calcine temperature. The decrease rate of OI variated as the calcine atmosphere being changed, the stronger the reductivity of the atmosphere is, the more OI decreases. The deammonia-dewater process and the phase constitution variation during calcine was studied, some idea for description of phase transformation path was suggested. It was found that the most important parameter affecting phase constitution and transformation is calcine temperature. At the temperature lower than 450 0 C, the main formed phase was ATB, while at higher temperature, the different phase like W/sub 20/O/sub 58/, WO/sub 3/ etc., could be formed by different ways depending on the atmosphere reductivity. The composition and the OI of ATB are changeable. An experiment for some blue oxides reduction at low temperature was carried out. It was found that OI and the constitution of blue oxide strongly affected the particle size of the formed W-powder

  17. Demonstration of production of tungsten metal powder and its consolidation into shapes

    International Nuclear Information System (INIS)

    Majumdar, S.; Kishor, J.; Paul, B.; Kain, V.; Dey, G.K.

    2016-01-01

    Tungsten is a strategically important metal used as plasma facing component in fusion reactors, radiation shields in cancer therapy machines, ammunition in defence applications, high speed cutting tools etc. The primary resources or minerals occurring in India contain a very low value (0.25-0.5 wt. %) of tungsten. Mineral beneficiation processes involving crushing, grinding, primary and secondary gravity separation, floatation are essential to produce the ore-concentrate suitable for further processing up to the preparation of the intermediate ammonium para-tungstate (APT). APT was further converted to tungsten tri-oxide (WO_3). Hydrogen reduction of WO_3 producing high purity W metal powder was demonstrated in large scale batches. Densification of W powder was further studied using vacuum hot pressing at 1950°C, and high density W metal plates of 5 mm thickness and 60 mm diameter were produced. The products obtained at every stage were systematically characterized using X-Ray diffraction (XRD), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) and electron backscattered diffraction (EBSD) techniques. (author)

  18. In situ synthesis of CdS/CdWO4/WO3 heterojunction films with enhanced photoelectrochemical properties

    Science.gov (United States)

    Zhan, Faqi; Li, Jie; Li, Wenzhang; Yang, Yahui; Liu, Wenhua; Li, Yaomin

    2016-09-01

    CdS/CdWO4/WO3 heterojunction films on fluorine-doped tin oxide (FTO) substrates are for the first time prepared as an efficient photoanode for photoelectrochemical (PEC) hydrogen generation by an in situ conversion process. The samples are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), ultraviolet visible spectrometry (UV-vis) and X-ray photoelectron spectroscopy (XPS). The CdS hollow spheres (∼80 nm) sensitized WO3 plate film with a CdWO4 buffer-layer exhibits increased visible light absorption and a significantly improved photoelectrochemical performance. The photocurrent density at 0 V (vs. Ag/AgCl) of the CdS/CdWO4/WO3 anode is ∼3 times higher than that of the CdWO4/WO3 anode, and ∼9 times higher than that of pure WO3 under illumination. The highest incident-photon-to-current-efficiency (IPCE) value increased from 16% to 63% when the ternary heterojunction was formed. This study demonstrates that the synthesis of ternary composite photocatalysts by the in situ conversion process may be a promising approach to achieve high photoelectric conversion efficiency.

  19. Role of indium tin oxide electrode on the microstructure of self-assembled WO3-BiVO4 hetero nanostructures

    Science.gov (United States)

    Song, Haili; Li, Chao; Van, Chien Nguyen; Dong, Wenxia; Qi, Ruijuan; Zhang, Yuanyuan; Huang, Rong; Chu, Ying-Hao; Duan, Chun-Gang

    2017-11-01

    Self-assembled WO3-BiVO4 nanostructured thin films were grown on a (001) yttrium stabilized zirconia (YSZ) substrate by the pulsed laser deposition method with and without the indium tin oxide (ITO) bottom electrode. Their microstructures including surface morphologies, crystalline phases, epitaxial relationships, interface structures, and composition distributions were investigated by scanning electron microscopy, high-resolution transmission electron microscopy, and X-ray energy dispersive spectroscopy. In both samples, WO3 formed nanopillars embedded into the monoclinic BiVO4 matrix with specific orientation relationships. In the sample with the ITO bottom electrode, an atomically sharp BiVO4/ITO interface was formed and the orthorhombic WO3 nanopillars were grown on a relaxed BiVO4 buffer layer with a mixed orthorhombic and hexagonal WO3 transition layer. In contrast, a thin amorphous layer appears at the interfaces between the thin film and the YSZ substrate in the sample without the ITO electrode. In addition, orthorhombic Bi2WO6 lamellar nanopillars were formed between WO3 and BiVO4 due to interdiffusion. Such a WO3-Bi2WO6-BiVO4 double heterojunction photoanode may promote the photo-generated charge separation and further improve the photoelectrochemical water splitting properties.

  20. Preparation of Porous F-WO3/TiO2 Films with Visible-Light Photocatalytic Activity by Microarc Oxidation

    OpenAIRE

    Yeh, Chung-Wei; Wu, Kee-Rong; Hung, Chung-Hsuang; Chang, Hao-Cheng; Hsu, Chuan-Jen

    2012-01-01

    Porous F-WO3/TiO2 (mTiO2) films are prepared on titanium sheet substrates using microarc oxidation (MAO) technique. The X-ray diffraction patterns show that visible-light (Vis) enabling mTiO2 films with a very high content of anatase TiO2 and high loading of WO3 are successfully synthesized at a low applied voltage of 300 V using electrolyte contenting NaF and Na2WO4 without subsequent heat treatment. The cross-sectional transmission electron microscopy micrograph reveals that the mTiO2 films...

  1. Dissolution kinetics of small amounts of oxygen in tantalum alloy T-111 and internal oxide displacement reactions during annealing

    Science.gov (United States)

    Stecura, S.

    1976-01-01

    Oxygen was added to T-111 (Ta-8W-2Hf, wt. %) at 820 and 990 C at an oxygen pressure of about 0.0003 torr. The technique employed permitted predetermined and reproducible doping of T-111 up to 3.0 at. % oxygen. Based on the temperature dependence of the doping reaction, it is concluded that the initial rates of oxygen pickup are probably controlled by solution of oxygen into the T-111 lattice. Although hafnium oxides are more stable than those of tantalum or tungsten, analyses of extracted residues indicate that the latter oxides predominate in the as-doped specimens, presumably because of the higher concentrations of tantalum and tungsten in the alloy. However, high-temperature annealing promotes gettering of dissolved oxygen and of other oxides to form hafnium oxides. Small amounts of tantalum and tungsten oxides were still present after high-temperature annealing. Tungsten oxide (WO3) volatilizes slightly from the surface of T-111 at 990 C. The vaporization of WO3 has no apparent affect on the doping reaction.

  2. Charge doping and large lattice expansion in oxygen-deficient heteroepitaxial WO3

    Science.gov (United States)

    Mattoni, Giordano; Filippetti, Alessio; Manca, Nicola; Zubko, Pavlo; Caviglia, Andrea D.

    2018-05-01

    Tungsten trioxide (WO3) is a versatile material with widespread applications ranging from electrochromics and optoelectronics to water splitting and catalysis of chemical reactions. For technological applications, thin films of WO3 are particularly appealing, taking advantage from a high surface-to-volume ratio and tunable physical properties. However, the growth of stoichiometric crystalline thin films is challenging because the deposition conditions are very sensitive to the formation of oxygen vacancies. In this paper, we show how background oxygen pressure during pulsed laser deposition can be used to tune the structural and electronic properties of WO3 thin films. By performing x-ray diffraction and low-temperature electrical transport measurements, we find changes in the WO3 lattice volume of up to 10% concomitantly with a resistivity drop of more than five orders of magnitude at room temperature as a function of increased oxygen deficiency. We use advanced ab initio calculations to describe in detail the properties of the oxygen vacancy defect states and their evolution in terms of excess charge concentration. Our results depict an intriguing scenario where structural, electronic, optical, and transport properties of WO3 single-crystal thin films can all be purposely tuned by controlling the oxygen vacancy formation during growth.

  3. Electrochromic Devices Based on Porous Tungsten Oxide Thin Films

    Directory of Open Access Journals (Sweden)

    Y. Djaoued

    2012-01-01

    Full Text Available Recent developments in the synthesis of transition metal oxides in the form of porous thin films have opened up opportunities in the construction of electrochromic devices with enhanced properties. In this paper, synthesis, characterization and electrochromic applications of porous WO3 thin films with different nanocrystalline phases, such as hexagonal, monoclinic, and orthorhombic, are presented. Asymmetric electrochromic devices have been constructed based on these porous WO3 thin films. XRD measurements of the intercalation/deintercalation of Li+ into/from the WO3 layer of the device as a function of applied coloration/bleaching voltages show systematic changes in the lattice parameters associated with structural phase transitions in LixWO3. Micro-Raman studies show systematic crystalline phase changes in the spectra of WO3 layers during Li+ ion intercalation and deintercalation, which agree with the XRD data. These devices exhibit interesting optical modulation (up to ~70% due to intercalation/deintercalation of Li ions into/from the WO3 layer of the devices as a function of applied coloration/bleaching voltages. The obtained optical modulation of the electrochromic devices indicates that, they are suitable for applications in electrochromic smart windows.

  4. Efficient synthesis of tungsten oxide hydrate-based nanocomposites for applications in bifunctional electrochromic-energy storage devices

    Science.gov (United States)

    Chang, Xueting; Hu, Ruirui; Sun, Shibin; Lu, Tong; Liu, Tao; Lei, Yanhua; Dong, Lihua; Yin, Yansheng; Zhu, Yanqiu

    2018-05-01

    In this work, we realized the large-scale synthesis of WO3 · H2O nanoflakes (NFs), g-C3N4/WO3 · H2O nanocomposite (NC) and graphene (G)/WO3 · H2O NC via a sonochemical process with tungsten salt as the precursor, g-C3N4 or G sheets as the supports, and distilled water as the solvent. Both the g-C3N4/WO3 · H2O NC and G/WO3 · H2O NC exhibited much better electrochromic (EC) performance (higher coloration efficiencies and faster response times) than that of the WO3 · H2O NFs. Using the WO3 · H2O-based materials as electrode materials, EC batteries that integrate the energy storage and EC functions in one device have been assembled. The energy status of the EC batteries could be visually indicated by the reversible color variations. Compared with the plain WO3 · H2O-based EC batteries, the NC-based EC batteries possessed a lower color contrast between the charged and discharged conditions but much longer discharge durations. The EC batteries could be quickly charged in a few seconds by adding H2O2, and the charged batteries exhibited significantly-enhanced discharging durations in comparison with the initial ones. The g-C3N4/WO3 · H2O NC-EC batteries charged by a small amount of H2O2 could produce a long discharging duration up to 760 min.

  5. Research and development of tungsten electrodes added with rare earth oxides

    International Nuclear Information System (INIS)

    Zuoren Nie; Ying Chen; Meiling Zhou; Tieyong Zuo

    2001-01-01

    The recent research and development of tungsten electrodes used in TIG and Plasma technologies are introduced, and the tungsten materials as well as the effects of rare earth oxides are specially discussed. in W-La 2 O 3 , W-CeO 2 , W-Y 2 O 3 and W-ThO 2 electrode materials, the W-2.2mass%La 2 O 3 electrode exhibited the best properties when the current is of little or middle volume, and when the electrodes are used in large current, the W-Y 2 O 3 electrode is the best. By a comparative study between the tungsten electrodes activated with single metal oxides, as above-mentioned, and those containing two or three rare earth oxides, namely La 2 O 3 , CeO 2 and Y 2 O 3 , it was indicated that the welding arc properties of the tungsten electrodes activated with combined rare earth oxides additions is superior than that of the electrodes containing single oxides as above mentioned. It was also shown that the operating properties of tungsten electrodes depend intensively on the rare earth oxides contained in the electrodes, and the actions of rare earth oxides during arcing are the most important factors to the electrodes' operating properties, temperature, work function as well as the arc stability. (author)

  6. Oxidation behaviour of bulk W-Cr-Ti alloys prepared by mechanical alloying and HIPing

    International Nuclear Information System (INIS)

    García-Rosales, C.; López-Ruiz, P.; Alvarez-Martín, S.; Calvo, A.; Ordás, N.; Koch, F.; Brinkmann, J.

    2014-01-01

    Self-passivating tungsten based alloys are expected to provide a major safety advantage compared to pure tungsten when used as first wall armour of future fusion reactors, due to the formation of a protective oxide scale, preventing the formation of volatile and radioactive WO 3 in case of a loss of coolant accident with simultaneous air ingress. In this work results of isothermal oxidations tests at 800 and 1000 °C on bulk alloy WCr12Ti2.5 performed by thermogravimetric analysis (TGA) and by exposure to flowing air in a furnace are presented. In both cases a thin, dense Cr 2 O 3 layer is found at the outer surface, below which a Cr 2 WO 6 scale and Ti 2 CrO 5 layers alternating with WO 3 are formed. The Cr 2 O 3 , Cr 2 WO 6 and Ti 2 CrO 5 scales act as protective barriers against fast inward O 2− diffusion. The oxidation kinetics seems to be linear for the furnace exposure tests while for the TGA tests at 800 °C the kinetics is first parabolic, transforming into linear after an initial phase. The linear oxidation rates are 2–3 orders of magnitude lower than for pure W

  7. Promotion of catalytic performance by adding W into Pt/ZrO{sub 2} catalyst for selective catalytic oxidation of ammonia

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Mengmeng [Institute of New Energy and Low-Carbon Technology, Sichuan University, Chengdu 610064, Sichuan (China); Wang, Suning; Li, Yuanshan [College of Chemical Engineering, Sichuan University, Chengdu 610064, Sichuan (China); Xu, Haidi, E-mail: xuhaidi@scu.edu.cn [Institute of New Energy and Low-Carbon Technology, Sichuan University, Chengdu 610064, Sichuan (China); Chen, Yaoqiang, E-mail: nic7501@scu.edu.cn [Institute of New Energy and Low-Carbon Technology, Sichuan University, Chengdu 610064, Sichuan (China); College of Chemical Engineering, Sichuan University, Chengdu 610064, Sichuan (China)

    2017-04-30

    Highlights: • The tungsten species weaken platinum-oxygen bond strength. • Pt{sup 0} was the active species of ammonia oxidation reaction in the low temperature. • Some PtO species could convert to Pt [111] beside WO{sub 3} species. - Abstract: Pt-WO{sub 3}/ZrO{sub 2} catalyst was prepared by co-impregnation method to improve the ammonia oxidation performance of Pt/ZrO{sub 2}. Differences in textural, structural, surface chemical states, redox properties and acid properties, together with the catalytic performance of Pt/ZrO{sub 2} and Pt-WO{sub 3}/ZrO{sub 2} catalysts were investigated systematically. The results of H{sub 2}-TPR revealed that higher reduction ability was possessed by Pt-WO{sub 3}/ZrO{sub 2} than that of Pt/ZrO{sub 2} due to the influence of tungsten on platinum. The XPS results showed that electron transfer from tungsten to platinum species made higher electron density around platinum. The TEM results revealed that the active lattice plane Pt[111] was obtained by modification of W species. Consequently, Pt-WO{sub 3}/ZrO{sub 2} exhibited obviously better ammonia oxidation performance compared with Pt/ZrO{sub 2}, the light-off temperature of NH{sub 3} shifted from 284 °C to 249 °C, the activation energy decreased from 113.4 kJ mol{sup −1} to 96.2 kJ mol{sup −1}.

  8. Tungsten oxide nanowires grown on graphene oxide sheets as high-performance electrochromic material

    International Nuclear Information System (INIS)

    Chang, Xueting; Sun, Shibin; Dong, Lihua; Hu, Xiong; Yin, Yansheng

    2014-01-01

    Graphical abstract: Electrochromic mechanism of tungsten oxide nanowires-reduced graphene oxide composite. - Highlights: • A novel inorganic-nano-carbon hybrid composite was prepared. • The hybrid composite has sandwich-like structure. • The hybrid composite exhibited high-quality electrohcromic performance. - Abstract: In this work, we report the synthesis of a novel hybrid electrochromic composite through nucleation and growth of ultrathin tungsten oxide nanowires on graphene oxide sheets using a facile solvothermal route. The competition between the growth of tungsten oxide nanowires and the reduction of graphene oxide sheets leads to the formation of sandwich-structured tungsten oxide-reduced graphene oxide composite. Due to the strongly coupled effect between the ultrathin tungsten oxide nanowires and the reduced graphene oxide nanosheets, the novel electrochromic composite exhibited high-quality electrochromic performance with fast color-switching speed, good cyclic stability, and high coloration efficiency. The present tungsten oxide-reduced graphene oxide composite represents a new approach to prepare other inorganic-reduced graphene oxide hybrid materials for electrochemical applications

  9. Synthesis and electrical characterization of tungsten oxide nanowires

    Institute of Scientific and Technical Information of China (English)

    Huang Rui; Zhu Jing; Yu Rong

    2009-01-01

    Tungsten oxide nanowires of diameters ranging from 7 to 200 nm are prepared on a tungsten rod substrate by using the chemical vapour deposition (CVD) method with vapour-solid (VS) mechanism. Tin powders are used to control oxygen concentration in the furnace, thereby assisting the growth of the tungsten oxide nanowires. The grown tungsten oxide nanowires are determined to be of crystalline W18O49. Ⅰ-Ⅴ curves are measured by an in situ transmission electron microscope (TEM) to investigate the electrical properties of the nanowires. All of the Ⅰ-Ⅴ curves observed are symmetric, which reveals that the tungsten oxide nanowires are semiconducting. Quantitative analyses of the experimental I V curves by using a metal-semiconductor-metal (MSM) model give some intrinsic parameters of the tungsten oxide nanowires, such as the carrier concentration, the carrier mobility and the conductivity.

  10. Tungsten Oxide and Polyaniline Composite Fabricated by Surfactant-Templated Electrodeposition and Its Use in Supercapacitors

    Directory of Open Access Journals (Sweden)

    Benxue Zou

    2014-01-01

    Full Text Available Composite nanostructures of tungsten oxide and polyaniline (PANI were fabricated on carbon electrode by electrocodeposition using sodium dodecylbenzene sulfonate (SDBS as the template. The morphology of the composite can be controlled by changing SDBS surfactant and aniline monomer concentrations in solution. With increasing concentration of aniline in surfactant solution, the morphological change from nanoparticles to nanofibers was observed. The nanostructured WO3/PANI composite exhibited enhanced capacitive charge storage with the specific capacitance of 201 F g−1 at 1.28 mA cm−2 in large potential window of -0.5~ 0.65 V versus SCE compared to the bulk composite film. The capacitance retained about 78% when the sweeping potential rate increased from 10 to 150 mV/s.

  11. Platelike WO3 sensitized with CdS quantum dots heterostructures for photoelectrochemical dynamic sensing of H2O2 based on enzymatic etching.

    Science.gov (United States)

    Wang, Yanhu; Gao, Chaomin; Ge, Shenguang; Yu, Jinghua; Yan, Mei

    2016-11-15

    A platelike tungsten trioxide (WO3) sensitized with CdS quantum dots (QDs) heterojunction is developed for solar-driven, real-time, and selective photoelectrochemical (PEC) sensing of H2O2 in the living cells. The structure is synthesized by hydrothermally growing platelike WO3 on fluorine doped tin oxide (FTO) and subsequently sensitized with CdS QDs. The as-prepared WO3-CdS QDs heterojunction achieve significant photocurrent enhancement, which is remarkably beneficial for light absorption and charge carrier separation. Based on the enzymatic etching of CdS QDs enables the activation of quenching the charge transfer efficiency, thus leading to sensitive PEC recording of H2O2 level in buffer and cellular environments. The results indicated that the proposed method will pave the way for the development of excellent PEC sensing platform with the quantum dot sensitization. This study could also provide a new train of thought on designing of self-operating photoanode in PEC sensing, promoting the application of semiconductor nanomaterials in photoelectrochemistry. Copyright © 2016 Elsevier B.V. All rights reserved.

  12. Preparation of ultra-thin and high-quality WO{sub 3} compact layers and comparision of WO{sub 3} and TiO{sub 2} compact layer thickness in planar perovskite solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Jincheng; Shi, Chengwu, E-mail: shicw506@foxmail.com; Chen, Junjun; Wang, Yanqing; Li, Mingqian

    2016-06-15

    In this paper, the ultra-thin and high-quality WO{sub 3} compact layers were successfully prepared by spin-coating-pyrolysis method using the tungsten isopropoxide solution in isopropanol. The influence of WO{sub 3} and TiO{sub 2} compact layer thickness on the photovoltaic performance of planar perovskite solar cells was systematically compared, and the interface charge transfer and recombination in planar perovskite solar cells with TiO{sub 2} compact layer was analyzed by electrochemical impedance spectroscopy. The results revealed that the optimum thickness of WO{sub 3} and TiO{sub 2} compact layer was 15 nm and 60 nm. The planar perovskite solar cell with 15 nm WO{sub 3} compact layer gave a 9.69% average and 10.14% maximum photoelectric conversion efficiency, whereas the planar perovskite solar cell with 60 nm TiO{sub 2} compact layer achieved a 11.79% average and 12.64% maximum photoelectric conversion efficiency. - Graphical abstract: The planar perovskite solar cell with 15 nm WO{sub 3} compact layer gave a 9.69% average and 10.14% maximum photoelectric conversion efficiency, whereas the planar perovskite solar cell with 60 nm TiO{sub 2} compact layer achieved a 11.79% average and 12.64% maximum photoelectric conversion efficiency. Display Omitted - Highlights: • Preparation of ultra-thin and high-quality WO{sub 3} compact layers. • Perovskite solar cell with 15 nm-thick WO{sub 3} compact layer achieved PCE of 10.14%. • Perovskite solar cell with 60 nm-thick TiO{sub 2} compact layer achieved PCE of 12.64%.

  13. X-ray diffraction study of WO3 at high pressure

    International Nuclear Information System (INIS)

    Bouvier, P.; Crichton, W.A.; Boulova, M.; Lucazeau, G.

    2002-01-01

    The high-pressure behaviour of microcrystalline tungsten oxide (WO 3 ) has been investigated with angle-dispersive synchrotron x-ray powder diffraction in a diamond anvil cell up to 40 GPa at room temperature. Up to 21 GPa, the pressure dependence of the volume of the monoclinic high-pressure (P2 1 /c) phase is described by a third-order Birch-Murnaghan equation of state with parameters V 0 =210.9(7)A 3 , K T =27(2)GP a and K'=9.4(5). At 24 GPa, a first-order phase transition occurs with an approximate Δ V of 7.4% to a monoclinic P2 1 /a unit cell with a=6.1669(8)A, b=4.5758(6)A, c=5.3159(6)A, β=101.440(9) deg. A second transition is observed at pressures higher than 31 GPa with an approximate Δ V of 12% to a phase described by a third monoclinic unit cell, with a=10.3633(22)A, b=3.9065(8)A, c=9.3459(18)A and β=98.539(14) deg. (author)

  14. Oxidation behaviour of bulk W-Cr-Ti alloys prepared by mechanical alloying and HIPing

    Energy Technology Data Exchange (ETDEWEB)

    García-Rosales, C., E-mail: cgrosales@ceit.es [CEIT and Tecnun (University of Navarra), E-20018 San Sebastian (Spain); López-Ruiz, P.; Alvarez-Martín, S.; Calvo, A.; Ordás, N. [CEIT and Tecnun (University of Navarra), E-20018 San Sebastian (Spain); Koch, F.; Brinkmann, J. [Max-Planck-Institut für Plasmaphysik (IPP), EURATOM Association, D-85748 Garching (Germany)

    2014-10-15

    Self-passivating tungsten based alloys are expected to provide a major safety advantage compared to pure tungsten when used as first wall armour of future fusion reactors, due to the formation of a protective oxide scale, preventing the formation of volatile and radioactive WO{sub 3} in case of a loss of coolant accident with simultaneous air ingress. In this work results of isothermal oxidations tests at 800 and 1000 °C on bulk alloy WCr12Ti2.5 performed by thermogravimetric analysis (TGA) and by exposure to flowing air in a furnace are presented. In both cases a thin, dense Cr{sub 2}O{sub 3} layer is found at the outer surface, below which a Cr{sub 2}WO{sub 6} scale and Ti{sub 2}CrO{sub 5} layers alternating with WO{sub 3} are formed. The Cr{sub 2}O{sub 3}, Cr{sub 2}WO{sub 6} and Ti{sub 2}CrO{sub 5} scales act as protective barriers against fast inward O{sup 2−} diffusion. The oxidation kinetics seems to be linear for the furnace exposure tests while for the TGA tests at 800 °C the kinetics is first parabolic, transforming into linear after an initial phase. The linear oxidation rates are 2–3 orders of magnitude lower than for pure W.

  15. Mechanistic Understanding of Tungsten Oxide In-Plane Nanostructure Growth via Sequential Infiltration Synthesis

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jae Jin; Suh, Hyo Seon; Zhou, Chun; Mane, Anil U.; Lee, Byeongdu; Kim, Soojeong; Emery, Jonathan D.; Elam, Jeffrey W.; Nealey, Paul F.; Fenter, Paul; Fister, Timothy T.

    2018-02-21

    Tungsten oxide (WO3-x) nanostructures with hexagonal in-plane arrangements were fabricated by sequential infiltration synthesis (SIS), using the selective interaction of gas phase precursors with functional groups in one domain of a block copolymer (BCP) self-assembled template. Such structures are highly desirable for various practical applications and as model systems for fundamental studies. The nanostructures were characterized by cross-sectional scanning electron microscopy, grazing-incidence small/wide-angle X-ray scattering (GISAXS/GIWAXS), and X-ray absorption near edge structure (XANES) measurements at each stage during the SIS process and subsequent thermal treatments, to provide a comprehensive picture of their evolution in morphology, crystallography and electronic structure. In particular, we discuss the critical role of SIS Al2O3 seeds toward modifying the chemical affinity and free volume in a polymer for subsequent infiltration of gas phase precursors. The insights into SIS growth obtained from this study are valuable to the design and fabrication of a wide range of targeted nanostructures.

  16. Electrochromic Properties of Tungsten Oxide Films Prepared by Reactive Sputtering

    Science.gov (United States)

    Kim, Min Hong; Kang, Tai Young; Jung, Yu Sup; Kim, Kyung Hwan

    2013-05-01

    WO3-x thin films were deposited on induim tin oxide (ITO) glass substrates with various oxygen flow ratios from 0.55 to 0.7 by the reactive facing-target sputtering method, at a power density of 4 W/cm2 and room temperature. The structural properties of the WO3-x thin films were measured by X-ray diffractometry and Raman spectral analysis. As-deposited WO3-x thin films had an amorphous structure. In the Raman spectra, WO3-x thin films exhibited two strong peaks at 770 and 950 cm-1 attributed to the vibrations of W6+-O and W6+=O bonds, respectively. The electrochemical and optical properties of WO3-x thin films were measured by cyclic voltammetry and UV/vis spectrometry. The results showed the highest charge density at an oxygen flow ratio of 0.7 and the highest transmittance in the visible range. The maximum coloration efficiency was 30.82 cm2/C at an oxygen flow ratio of 0.7.

  17. Growth of single-crystal W whiskers during humid H2/N2 reduction of Ni, Fe-Ni, and Co-Ni doped tungsten oxide

    International Nuclear Information System (INIS)

    Wang Shiliang; He Yuehui; Zou Jou; Wang Yong; Huang Han

    2009-01-01

    Numbers of W whiskers were obtained by reducing Ni, Ni-Fe, and Ni-Co doped tungsten oxide in a mixed atmosphere of humid H 2 and N 2 . The phases and morphologies of the reduction products were characterized by XRD and SEM. Intensive TEM and EDS analyses showed that the obtained whiskers were W single crystals which typical have alloyed particles (Ni-W, Fe-Ni, or Co-Ni-W) at the growth tips. The formed W whiskers were presumed to be induced by the alloyed particles. Our experimental results revealed that, during the reduction process of tungsten oxide, the pre-reduced Ni, Fe-Ni, or Co-Ni particles not only served as nucleation aids for the initial growth of W phase from W oxide but also played the roles of catalysts during the reductive decomposition of gaseous WO 2 (OH) 2 .

  18. Fabrication and characterization of WO3/Ag/WO3 multilayer transparent anode with solution-processed WO3 for polymer light-emitting diodes.

    Science.gov (United States)

    Jeon, Kangmin; Youn, Hongseok; Kim, Seongbeom; Shin, Seongbeom; Yang, Minyang

    2012-05-15

    The dielectric/metal/dielectric multilayer is suitable for a transparent electrode because of its high-optical and high-electrical properties; however, it is fabricated by an expensive and inefficient multistep vacuum process. We present a WO3/Ag/WO3 (WAW) multilayer transparent anode with solution-processed WO3 for polymer light-emitting diodes (PLEDs). This WAW multilayer not only has high transmittance and low resistance but also can be easily and rapidly fabricated. We devised a novel method to deposit a thin WO3 layer by a solution process in an air environment. A tungstic acid solution was prepared from an aqueous solution of Na2WO4 and then converted to WO3 nanoparticles (NPs) by a thermal treatment. Thin WO3 NP layers form WAW multilayer with a thermal-evaporated Ag layer, and they improve the transmittance of the WAW multilayer because of its high transmittance and refractive index. Moreover, the surface of the WO3 layer is homogeneous and flat with low roughness because of the WO3 NP generation from the tungstic acid solution without aggregation. We performed optical simulation and experiments, and the optimized WAW multilayer had a high transmittance of 85% with a sheet resistance of 4 Ω/sq. Finally, PLEDs based on the WAW multilayer anode achieved a maximum luminance of 35,550 cd/m2 at 8 V, and this result implies that the solution-processed WAW multilayer is appropriate for use as a transparent anode in PLEDs.

  19. Preparation of WO{sub 3}/g-C{sub 3}N{sub 4} composites and their application in oxidative desulfurization

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Rongxiang, E-mail: zylhzrx@126.com; Li, Xiuping, E-mail: lilili_171717@126.com; Su, Jianxun; Gao, Xiaohan

    2017-01-15

    Highlights: • The WO{sub 3}/g-C{sub 3}N{sub 4} was successfully synthesized through simple calcination. • The process is simple and the cost raw materials is cheap. • The WO{sub 3}/g-C{sub 3}N{sub 4} firstly applied to ODS. • The desulpurization rate of WO{sub 3}/g-C{sub 3}N{sub 4} may attach to 91.2%. • Five recycles of WO{sub 3}/g-C{sub 3}N{sub 4} still attach to 89.5% due to heterogeneous catalysis. - Abstract: WO{sub 3}/graphitic carbon nitride (g-C{sub 3}N{sub 4}) composites were successfully synthesized through direct calcining of a mixture of WO{sub 3} and g-C{sub 3}N{sub 4} at 400 °C for 2 h. The WO{sub 3} was prepared by calcination of phosphotungstic acid at 550 °C for 4 h, and the g-C{sub 3}N{sub 4} was obtained by calcination of melamine at 520 °C for 4 h. The WO{sub 3}/g-C{sub 3}N{sub 4} composites were characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FT-IR), and Brunner−Emmett−Teller analysis (BET). The WO{sub 3}/g-C{sub 3}N{sub 4} composites exhibited stronger XRD peaks of WO{sub 3} and g-C{sub 3}N{sub 4} than the WO{sub 3} and pure g-C{sub 3}N{sub 4}. In addition, two WO{sub 3} peaks at 25.7° and 26.6° emerged for the 36% −WO{sub 3}/g-C{sub 3}N{sub 4} composite. This finding indicated that WO{sub 3} was highly dispersed on the surface of the g-C{sub 3}N{sub 4} nanosheets and interacted with the nanosheets, which resulted in the appearance of (012) and (022) planes of WO{sub 3}. The WO{sub 3}/g-C{sub 3}N{sub 4} composite also exhibited a larger specific surface area and higher degree of crystallization than WO{sub 3} or pure g-C{sub 3}N{sub 4}, which resulted in high catalytic activity of the catalyst. Desulfurization experiments demonstrated that the desulfurization rate of dibenzothiophene (DBT) in model oil reached 91.2% under optimal conditions. Moreover, the activity of the catalyst was not significantly decreased after five recycles.

  20. Processing of tungsten csrap into powders by electroerosion dispersion

    International Nuclear Information System (INIS)

    Fominskij, L.P.; Myuller, A.S.; Levchuk, M.V.; Tarabrina, V.P.

    1985-01-01

    A powder produced by electroerosion dispersion in water from tungsten chips and rod cuttings is studied for its properties and structure. Powder particles are mainly of spherical shape, their predominant size is 2-4 μm. A fraction of -63 μm comprises a basic mass of the powder (up to 80%), an ultrafine (to 40 μm) phase of WO which is isolated by decantation comprises about 3.5% of its mass. The powder particles are low oxidized, have a fine-grain microstructure and consist of tungsten with admixture of β-W (to 30%). A fraction of total oxygen mass in the mixture of fractio s 0.74%. The powder containing less than 0.25% of oxygen is produced by decantation of the oxide phase. The product purity is determined exclusively by the purity of the raw material. Prior to producing articles it is recommended to anneal the powder either in the inert atmosphere or in the reduced medium at 750 deg C for β-W to transfer into common tungsten

  1. Partial thermodynamic functions of hydrogen in complex hydrated vanadium(5) and tungsten(6) oxides

    International Nuclear Information System (INIS)

    Volkov, V.L.; Zakharova, G.S.

    2003-01-01

    The partial thermodynamic characteristics of hydrogen in the complex hydrated vanadium(5) and tungsten(6) oxides, obtained through the sol-gel method, of the general formula H 2 V 12-y W y O 31+δ ·nH 2 O (0 ≤ x ≤ 0.33) are determined through the emf method. The changes in these values (ΔG-bar(H 2 ), ΔH-bar(H 2 ) and ΔS-bar(H 2 )) in dependence on the compound composition are discussed. It is established that ΔG-bar(H 2 ) phases, amorphous to X-rays are determined by the ΔS-bar(H 2 ) value and crystalline ones by ΔH-bar(H 2 ). The scheme of the phase relationships of the H 2 O-H-WO 3 -V 2 O 5 system, whereto the given phases are related are presented [ru

  2. Characterization and application of a new pH sensor based on magnetron sputtered porous WO3 thin films deposited at oblique angles

    International Nuclear Information System (INIS)

    Salazar, Pedro; Garcia-Garcia, Francisco J.; Yubero, Francisco; Gil-Rostra, Jorge; González-Elipe, Agustín R.

    2016-01-01

    Highlights: • A solid-state pH sensor based on WO 3 amorphous thin film electrode is reported. • Cyclic voltammetry and XRD confirmed the amorphous nature of tungsten. • Potentiometric response of the WO 3 electrode revealed a quasi-Nernstian behavior. • The interference of the most common ions (Li + , Na + , K + and NH 4 + ) was negligible. • A full solid state pH sensor is developed. - Abstract: In this communication we report about an outstanding solid-state pH sensor based on amorphous nanocolumnar porous thin film electrodes. Transparent WO 3 thin films were deposited by reactive magnetron sputtering in an oblique angle configuration to enhance their porosity onto indium tin oxide (ITO) and screen printed electrodes (SPE). The potentiometric pH response of the nanoporous WO 3 -modified ITO electrode revealed a quasi-Nernstian behaviour, i.e. a linear working range from pH 1 to 12 with a slope of about −57.7 mV/pH. pH detection with this electrode was quite reproducible, displayed excellent anti-interference properties and a high stable response that remained unaltered over at least 3 months. Finally, a pH sensor was developed using nanoporous WO 3 -modified screen printed electrode (SPE) using a polypyrrole-modified Ag/AgCl electrode as internal reference electrode. This full solid state pH sensor presented a Nernstian behaviour with a slope of about −59 mV/pH and offered important analytical and operation advantages for decentralized pH measurements in different applications.

  3. Acetone sensors based on TiO{sub 2} nanocrystals modified with tungsten oxide species

    Energy Technology Data Exchange (ETDEWEB)

    Epifani, Mauro, E-mail: mauro.epifani@le.imm.cnr.it [Consiglio Nazionale delle Ricerche – Istituto per la Microelettronica e Microsistemi (CNR-IMM), via Monteroni c/o Campus Universitario, I-73100, Lecce (Italy); Comini, Elisabetta [SENSOR Lab, Department of Information Engineering, Brescia University and CNR-INO, via Valotti, 9, 25133 Brescia (Italy); Díaz, Raül [Electrochemical Processes Unit, IMDEA Energy Institute, Avda. Ramón de la Sagra, 3 28935 Móstoles (Spain); Genç, Aziz [Metallurgy and Materials Engineering Department, Faculty of Engineering, Bartin University, 74100, Bartin (Turkey); Andreu, Teresa [Catalonia Institute for Energy Research- (IREC), Jardíns de les Dones de Negre, 1, E-08930 Sant Adrià del Besos, Barcelona, CAT (Spain); Siciliano, Pietro [Consiglio Nazionale delle Ricerche – Istituto per la Microelettronica e Microsistemi (CNR-IMM), via Monteroni c/o Campus Universitario, I-73100, Lecce (Italy); Morante, Joan R. [Catalonia Institute for Energy Research- (IREC), Jardíns de les Dones de Negre, 1, E-08930 Sant Adrià del Besos, Barcelona, CAT (Spain); Departament d' Electrònica, Universitat de Barcelona, C./ Martí i Franquès 1, E-08028 Barcelona (Spain)

    2016-04-25

    TiO{sub 2} nanocrystals were prepared by sol–gel/solvothermal processing and modified by the addition of W precursor before the solvothermal step. The W: Ti nominal atomic ratio (R{sub W}) was fixed to 0.16 and 0.64. Surface modification of TiO{sub 2} occurred for R{sub W} = 0.16 while for R{sub W} = 0.64 nanocomposites with WO{sub 3} nanocrystals were obtained after heat-treatment at 500 °C. Pure TiO{sub 2} proved to be very poorly performing in acetone sensing in all the operating conditions. Instead, the addition of both W concentrations largely enhanced the sensor response. It ranged over two orders of magnitude of conductance variation for all the tested concentrations at as low as 200 °C operating temperature. The results showed that it is possible to enhance the performance of an otherwise almost inactive oxide like TiO{sub 2} by proper combination with another more active oxide like WO{sub 3}. - Highlights: • Sensing architecture are synthesized, combining WO{sub 3} and of TiO{sub 2} nanocrystals. • Surface layers of W oxides or heterojunctions of TiO{sub 2} and WO{sub 3} are obtained. • Simple TiO{sub 2} surface modification by W oxides boosts the TiO{sub 2} acetone response. • High responses even at 200 °C show catalytic effect of WO{sub 3} addition.

  4. Effect of SiO2 Overlayer on WO3 Sensitivity to Ammonia

    Directory of Open Access Journals (Sweden)

    Vibha Srivastava

    2010-06-01

    Full Text Available Ammonia gas sensing properties of tungsten trioxide thick film sensor was investigated. The doping of noble catalysts such as Pt, Pd, Au enhanced the gas sensitivity. Platinum doping was found to result in highest sensitivity. Remarkable sensitivity enhancement was realized by coating WO3 thick film sensors with SiO2 overlayer. Sol gel process derived silica overlayer increased ammonia gas sensitivity for doped as well as undoped sensor.

  5. Two stacked tandem white organic light-emitting diodes employing WO3 as a charge generation layer

    Science.gov (United States)

    Bin, Jong-Kwan; Lee, Na Yeon; Lee, SeungJae; Seo, Bomin; Yang, JoongHwan; Kim, Jinook; Yoon, Soo Young; Kang, InByeong

    2016-09-01

    Recently, many studies have been conducted to improve the electroluminescence (EL) performance of organic lightemitting diodes (OLEDs) by using appropriate organic or inorganic materials as charge generation layer (CGL) for their application such as full color displays, backlight units, and general lighting source. In a stacked tandem white organic light-emitting diodes (WOLEDs), a few emitting units are electrically interconnected by a CGL, which plays the role of generating charge carriers, and then facilitate the injection of it into adjacent emitting units. In the present study, twostacked WOLEDs were fabricated by using tungsten oxide (WO3) as inorganic charge generation layer and 1,4,5,8,9,11- hexaazatriphenylene hexacarbonitrile (HAT-CN) as organic charge generation layer (P-CGL). Organic P-CGL materials were used due to their ease of use in OLED fabrication as compared to their inorganic counterparts. To obtain high efficiency, we demonstrate two-stacked tandem WOLEDs as follows: ITO/HIL/HTL/HTL'/B-EML/ETL/N-CGL/P-CGL (WO3 or HAT-CN)/HTL″/YG-EML/ETL/LiF/Al. The tandem devices with blue- and yellow-green emitting layers were sensitive to the thickness of an adjacent layer, hole transporting layer for the YG emitting layer. The WOLEDs containing the WO3 as charge generation layer reach a higher power efficiency of 19.1 lm/W and the current efficiency of 51.2 cd/A with the white color coordinate of (0.316, 0.318) than the power efficiency of 13.9 lm/W, and the current efficiency of 43.7 cd/A for organic CGL, HAT-CN at 10 mA/cm2, respectively. This performance with inserting WO3 as CGL exhibited the highest performance with excellent CIE color coordinates in the two-stacked tandem OLEDs.

  6. Oxidation of primary amines to oximes with molecular oxygen using 1,1-diphenyl-2-picrylhydrazyl and WO3/Al2O3 as catalysts.

    Science.gov (United States)

    Suzuki, Ken; Watanabe, Tomonari; Murahashi, Shun-Ichi

    2013-03-15

    The oxidative transformation of primary amines to their corresponding oximes proceeds with high efficiency under molecular oxygen diluted with molecular nitrogen (O2/N2 = 7/93 v/v, 5 MPa) in the presence of the catalysts 1,1-diphenyl-2-picrylhydrazyl (DPPH) and tungusten oxide/alumina (WO3/Al2O3). The method is environmentally benign, because the reaction requires only molecular oxygen as the terminal oxidant and gives water as a side product. Various alicyclic amines and aliphatic amines can be converted to their corresponding oximes in excellent yields. It is noteworthy that the oxidative transformation of primary amines proceeds chemoselectively in the presence of other functional groups. The key step of the present oxidation is a fast electron transfer from the primary amine to DPPH followed by proton transfer to give the α-aminoalkyl radical intermediate, which undergoes reaction with molecular oxygen and hydrogen abstraction to give α-aminoalkyl hydroperoxide. Subsequent reaction of the peroxide with WO3/Al2O3 gives oximes. The aerobic oxidation of secondary amines gives the corresponding nitrones. Aerobic oxidative transformation of cyclohexylamines to cyclohexanone oximes is important as a method for industrial production of ε-caprolactam, a raw material for Nylon 6.

  7. Electronic structure of indium-tungsten-oxide alloys and their energy band alignment at the heterojunction to crystalline silicon

    Science.gov (United States)

    Menzel, Dorothee; Mews, Mathias; Rech, Bernd; Korte, Lars

    2018-01-01

    The electronic structure of thermally co-evaporated indium-tungsten-oxide films is investigated. The stoichiometry is varied from pure tungsten oxide to pure indium oxide, and the band alignment at the indium-tungsten-oxide/crystalline silicon heterointerface is monitored. Using in-system photoelectron spectroscopy, optical spectroscopy, and surface photovoltage measurements, we show that the work function of indium-tungsten-oxide continuously decreases from 6.3 eV for tungsten oxide to 4.3 eV for indium oxide, with a concomitant decrease in the band bending at the hetero interface to crystalline silicon than indium oxide.

  8. Chemical behavior of lanthanides-tungsten composite materials used in thermo-emissive cathodes

    International Nuclear Information System (INIS)

    Cadoret, K.; Cachard, J. de; Martinez, L.; Millot, F.; Hennet, L.; Douy, A.; Licheron, M.

    2001-01-01

    This work presents the crystallography and chemistry of new lanthanides-tungsten composite materials developed to manufacture thermionic cathodes for power grid tubes, based on the same principle than thorium-free cathodes. By mean of x-Ray diffraction at high temperature and under vacuum with synchrotron radiation facilities, we followed in real time the different phases and phase transitions that can occur during the heating process and the carburization at 1550 o C of such tungstates deposits on thin tungsten ribbons. Melting points for composition between 9 La 2 O 3 - 1 WO 3 and 2 La 2 O 3 - 9 WO 3 were specified under the pressure of 1x10 -6 mbar. After interpretation of x-ray diffraction results, phase diagram of n La 2 O 3 - m WO 3 system under vacuum in equilibrium with metallic tungsten have been deduced. Moreover we underline by these works the fact that using a lanthanum-rich tungstate involves better stability and chemical homogeneity of the cathodes surfaces with temperature. (author)

  9. Electrochemical water splitting using nano-zeolite Y supported tungsten oxide electrocatalysts

    Science.gov (United States)

    Anis, Shaheen Fatima; Hashaikeh, Raed

    2018-02-01

    Zeolites are often used as supports for metals and metal oxides because of their well-defined microporous structure and high surface area. In this study, nano-zeolite Y (50-150 nm range) and micro-zeolite Y (500-800 nm range) were loaded with WO3, by impregnating the zeolite support with ammonium metatungstate and thermally decomposing the salt thereafter. Two different loadings of WO3 were studied, 3 wt.% and 5 wt.% with respect to the overall catalyst. The prepared catalysts were characterized for their morphology, structure, and surface areas through scanning electron microscope (SEM), XRD, and BET. They were further compared for their electrocatalytic activity for hydrogen evolution reaction (HER) in 0.5 M H2SO4. On comparing the bare micro-zeolite particles with the nano-form, the nano-zeolite Y showed higher currents with comparable overpotentials and lower Tafel slope of 62.36 mV/dec. WO3 loading brought about a change in the electrocatalytic properties of the catalyst. The overpotentials and Tafel slopes were observed to decrease with zeolite-3 wt.% WO3. The smallest overpotential of 60 mV and Tafel slope of 31.9 mV/dec was registered for nano-zeolite with 3 wt.% WO3, while the micro-zeolite gave an overpotential of 370 mV and a Tafel slope of 98.1 mV/dec. It was concluded that even with the same metal oxide loading, nano-zeolite showed superior performance, which is attributed to its size and hence easier escape of hydrogen bubbles from the catalyst.

  10. The enhanced alcohol-sensing response of ultrathin WO3 nanoplates

    International Nuclear Information System (INIS)

    Chen Deliang; Hou Xianxiang; Wen Hejing; Wang Yu; Wang Hailong; Zhang Rui; Lu Hongxia; Xu Hongliang; Guan Shaokang; Li Xinjian; Sun Jing; Gao Lian

    2010-01-01

    Chemical sensors based on semiconducting metal oxide nanocrystals are of academic and practical significance in industrial processing and environment-related applications. Novel alcohol response sensors using two-dimensional WO 3 nanoplates as active elements have been investigated in this paper. Single-crystalline WO 3 nanoplates were synthesized through a topochemical approach on the basis of intercalation chemistry (Chen et al 2008 Small 4 1813). The as-obtained WO 3 nanoplate pastes were coated on the surface of an Al 2 O 3 ceramic microtube with four Pt electrodes to measure their alcohol-sensing properties. The results show that the WO 3 nanoplate sensors are highly sensitive to alcohols (e.g., methanol, ethanol, isopropanol and butanol) at moderate operating temperatures (260-360 deg. C). For butanol, the WO 3 nanoplate sensors have a sensitivity of 31 at 2 ppm and 161 at 100 ppm, operating at 300 deg. C. For other alcohols, WO 3 nanoplate sensors also show high sensitivities: 33 for methanol at 300 ppm, 70 for ethanol at 200 ppm, and 75 for isopropanol at 200 ppm. The response and recovery times of the WO 3 nanoplate sensors are less than 15 s for all the test alcohols. A good linear relationship between the sensitivity and alcohol concentrations has been observed in the range of 2-300 ppm, whereas the WO 3 nanoparticle sensors have not shown such a linear relationship. The sensitivities of the WO 3 nanoplate sensors decrease and their response times become short when the operating temperatures increase. The enhanced alcohol-sensing performance could be attributed to the ultrathin platelike morphology, the high crystallinity and the loosely assembling structure of the WO 3 nanoplates, due to the advantages of the effective adsorption and rapid diffusion of the alcohol molecules.

  11. Nanogravimetric studies of tungsten oxide thin films obtained by the polymeric precursor method

    International Nuclear Information System (INIS)

    Fernandes, V.C.; Santos, M.C.; Bulhoes, L.O.S.

    2007-01-01

    In this work, the intercalation/de-intercalation process of Li + ions in the tungsten oxide matrix was investigated. The reaction mechanism involved was also investigated. The WO 3 films, prepared by the polymeric precursor method, were deposited on a Pt covered quartz crystal using the dip-coating technique. The electrolyte was 0.1 mol L -1 LiClO 4 in acetonitrile. The morphology and structure of the deposit was accomplished by scanning electron microscopy and X-ray diffraction, respectively. In the electrochemical quartz crystal nanobalance results, it was observed that the mass transport as well as the kinetic processes involved are facilitated in the films cycled at lower potential sweep-rates. The mass variation data as a function of the charge variations in the anodic and cathodic regions indicate the participation of solvent molecules (acetonitrile) during the Li + ion intercalation/de-intercalation process. This was confirmed by the development of a model of the species flux as a function of the potential

  12. Preparation and characterization of tungsten-loaded titanium dioxide photocatalyst for enhanced dye degradation

    International Nuclear Information System (INIS)

    Saepurahman; Abdullah, M.A.; Chong, F.K.

    2010-01-01

    Tungsten-loaded TiO 2 photocatalyst has been successfully prepared and characterized. TEM analysis showed that the photocatalysts were nanosize with the tungsten species forming layers of coverage on the surface of TiO 2 , but not in clustered form. This was confirmed by XRD and FT-Raman analyses where tungsten species were well dispersed at lower loading ( 3 at higher loadings (>12 mol%). In addition, loading with tungsten could stabilize the anatase phase from transforming into inactive rutile phase and did not shift the optical absorption to the visible region as shown by DRUV-vis analysis. PZC value of TiO 2 was found at 6.4, but the presence of tungsten at 6.5 mol% WO 3 , decreased the PZC value to 3. Tungsten-loaded TiO 2 was superior to unmodified TiO 2 with 2-fold increase in degradation rate of methylene blue, and equally effective for the degradation of different class of dyes such as methyl violet and methyl orange at 1 mol% WO 3 loading.

  13. Tuning of the acid–base properties of primary Me{sub 2}O{sub 3} (Me = Al, Ga, In) and binary (ZrO{sub 2}–Me{sub 2}O{sub 3}) (Me = B, Al, Ga, In) oxides by adding WO{sub 3}: A calorimetric study

    Energy Technology Data Exchange (ETDEWEB)

    Kourieh, Reem; Bennici, Simona; Auroux, Aline, E-mail: aline.auroux@ircelyon.univ-lyon1.fr

    2013-09-10

    Highlights: • Preparation of WO{sub 3}/Me{sub 2}O{sub 3} and WO{sub 3}/(ZrO{sub 2}–Me{sub 2}O{sub 3}) catalysts (Me{sub 2}O{sub 3} = group III oxides). • Acid–base properties were estimated by adsorption microcalorimetry of NH{sub 3} and SO{sub 2}. • The tuning of acid–base properties of amphoteric oxides was achieved by adding WO{sub 3}. • Pyridine adsorption showed that acidity is due to the presence of Lewis acid sites. - Abstract: In this work two series of samples were prepared by impregnation of Me (Me = Al, Ga, In) hydroxides and Zr–Me (Me = B, Al, Ga, In) mixed hydroxides with an ammonium metatungstate hydrate solution followed by calcination at 400 °C. The obtained WO{sub 3}/Me{sub 2}O{sub 3} and WO{sub 3}/(ZrO{sub 2}–Me{sub 2}O{sub 3}) samples have been characterized in terms of their structural, textural, and surface properties, including the acid features, by a variety of techniques (BET, XRD, TG) and microcalorimetry. The acid–base properties were estimated by the adsorption of NH{sub 3} and SO{sub 2} as probe molecules, respectively. The prepared mixed oxide samples showed very different properties in terms of surface area and X-ray diffractograms. All obtained samples showed a specific acidic–basic character influenced by the relative amounts of each oxide, the most acidic samples being WO{sub 3}/ZrO{sub 2} and WO{sub 3}/Al{sub 2}O{sub 3} and WO{sub 3}/(Al{sub 2}O{sub 3}–ZrO{sub 2})

  14. Subsolidus Phase Relations of the CaO-WO3-CuO System at 800 °C in Air

    DEFF Research Database (Denmark)

    Grivel, J. -C.

    2012-01-01

    The subsolidus phase relations of the CaO-WO3-CuO system were investigated in air. The samples were equilibrated at 800 degrees C. Under these conditions, five binary oxide phases are stable: Ca2CuO3, Cu3WO6, CuWO4, CaWO4 and Ca3WO6. The pseudo-ternary section is characterised by 6 three...

  15. Gas Sensing Properties of Metal Doped WO3 Thin Film Sensors Prepared by Pulsed Laser Deposition and DC Sputtering Process

    Science.gov (United States)

    Bhuiyan, Md. Mosharraf Hossain; Ueda, Tsuyoshi; Ikegami, Tomoaki; Ebihara, Kenji

    2006-10-01

    Tungsten trioxide (WO3) thin films gas sensors were prepared by the KrF excimer pulsed laser deposition (PLD) method. The films were prepared on the quartz glass, silicon and also on the Al2O3 sensor substrates with platinum interdigitated electrodes. The effect of doping of the platinum (Pt), palladium (Pd) or gold (Au) on the WO3 thin film was also investigated. These metals were doped to the WO3 thin film by the DC sputtering process during the PLD. The substrate temperature and the oxygen pressure were 400 °C and 100 mTorr, respectively, during the deposition. The films were characterized by atomic force microscopy (AFM) and X-ray diffraction (XRD). The sensitivity of the prepared sensors to 60 ppm NO gas was examined using the two terminal resistance method in a chamber at atmospheric pressure and operating temperatures of 25-350 °C. The sensitivity of the WO3 thin films doped with Pt, Pd, or Au was found to be higher than that of the undoped WO3 thin film.

  16. A comparative study of humidity sensing and photocatalytic applications of pure and nickel (Ni)-doped WO{sub 3} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Ramkumar, S. [Bannari Amman Institute of Technology, Department of Physics, Erode, Tamilnadu (India); Rajarajan, G. [Vidhya Mandhir Institute of Technology, Department of Physics, Erode, Tamilnadu (India)

    2017-06-15

    Nanocrystalline of pristine and nickel (Ni)-doped tungsten trioxide (WO{sub 3}) thin films was deposited by chemical bath deposition method. The concentrations of Ni ions were varied from 0 to 10 wt%. In order to improve the crystallinity of the films were annealed at 600 C for 2 h in the ambient atmosphere. X-ray diffraction results reveal that the WO{sub 3} doped with nickel crystallizes in monoclinic structure and the results are in good agreement with the standard JCPDS data (card no: 83-0951). AFM micrographs reveal that average grain size of about 27-39 nm for pure and Ni-doped WO{sub 3} thin films. In addition, the band gap of the Ni-doped WO{sub 3} nanostructures is facilely tunable by controlling the Ni contents. The humidity sensor setup was fabricated and measured for pure and Ni-doped WO{sub 3} thin film sensor with various level of RH (10-90%). The Ni-doped WO{sub 3} sensor showed fast response and high sensitivity than pure WO{sub 3}. The photocatalytic activities of the films were evaluated by degradation of methyl orange, methylene blue and phenol in an aqueous solution under visible light irradiation. The photocatalytic activity of WO{sub 3} nanostructures could be remarkably enhanced by doping the Ni impurity. (orig.)

  17. Electro-chemically-based technologies for processing of tungsten components in fusion technology

    International Nuclear Information System (INIS)

    Holstein, N.; Konys, J.; Krauss, W.; Lorenz, J.

    2010-01-01

    In fusion technology layers and bulk components fabricated from tungsten and W-alloys are used as functional materials, e.g. as coatings of blanket modules or T-permeation barriers and also as structural components in a He-cooled divertor. Their application under high heat loads and temperatures is besides manufacturing, also challenging regarding joining, caused e.g. by expansion mismatches in combination with steel or other diffusion issues. Driven by these needs, electro-chemically-based technologies were analyzed concerning their advantages in processing in the fields of soft structuring of tungsten alloys and in deposition of functional scales. The Electro-Chemistry (EC) of tungsten is characterized by its affection to build up passivation layers in aqueous media during the initial oxidation, which is the result of an unavoidable basic electrochemical reaction with water (W + 3H 2 O → WO 3 + 3H 2 ), although the element standard potential is situated between common EC material like iron and copper. (orig.)

  18. Highly efficient perovskite solar cells based on a nanostructured WO3-TiO2 core-shell electron transporting material

    KAUST Repository

    Mahmood, Khalid; Swain, Bhabani Sankar; Kirmani, Ahmad R.; Amassian, Aram

    2015-01-01

    Until recently, only mesoporous TiO2 and ZnO were successfully demonstrated as electron transport layers (ETL) alongside the reports of ZrO2 and Al2O3 as scaffold materials in organometal halide perovskite solar cells, largely owing to ease of processing and to high power conversion efficiency. In this article, we explore tungsten trioxide (WO3)-based nanostructured and porous ETL materials directly grown hydrothermally with different morphologies such as nanoparticles, nanorods and nanosheet arrays. The nanostructure morphology strongly influences the photocurrent and efficiency in organometal halide perovskite solar cells. We find that the perovskite solar cells based on WO3 nanosheet arrays yield significantly enhanced photovoltaic performance as compared to nanoparticles and nanorod arrays due to good perovskite absorber infiltration in the porous scaffold and more rapid carrier transport. We further demonstrate that treating the WO3 nanostructures with an aqueous solution of TiCl4 reduces charge recombination at the perovskite/WO3 interface, resulting in the highest power conversion efficiency of 11.24% for devices based on WO3 nanosheet arrays. The successful demonstration of alternative ETL materials and nanostructures based on WO3 will open up new opportunities in the development of highly efficient perovskite solar cells. This journal is © The Royal Society of Chemistry 2015.

  19. Microporous TiO2-WO3/TiO2 films with visible-light photocatalytic activity synthesized by micro arc oxidation and DC magnetron sputtering

    International Nuclear Information System (INIS)

    Wu, Kee-Rong; Hung, Chung-Hsuang; Yeh, Chung-Wei; Wu, Jiing-Kae

    2012-01-01

    Highlights: ► A simple MAO is used to prepare porous WO 3 /TiO 2 layer on Ti sheet as a visible-light enabled catalyst. ► The photocatalytic activity of the WO 3 /TiO 2 is enhanced by sputtering over an N,C-TiO 2 layer. ► This is ascribed to the synergetic effect of hybrid sample prepared by two-step method. - Abstract: This study reports the preparation of microporous TiO 2 -WO 3 /TiO 2 films with a high surface area using a two-step approach. A porous WO 3 /TiO 2 template was synthesized by oxidizing a titanium sheet using a micro arc oxidation (MAO) process. This sheet was subsequently overlaid with a visible light (Vis)-enabled TiO 2 (N,C-TiO 2 ) film, which was deposited by codoping nitrogen (N) and carbon (C) ions into a TiO 2 lattice using direct current magnetron sputtering. The resulting microporous TiO 2 -WO 3 /TiO 2 film with a 0.38-μm-thick N,C-TiO 2 top-layer exhibited high photocatalytic activity in methylene blue (MB) degradation among samples under ultraviolet (UV) and Vis irradiation. This is attributable to the synergetic effect of two-step preparation method, which provides a highly porous microstructure and the well-crystallized N,C-TiO 2 top-layer. This is because a higher surface area with high crystallinity favors the adsorption of more MB molecules and more photocatalytic active areas. Thus, the microporous TiO 2 -WO 3 /TiO 2 film has promising applications in the photocatalytic degradation of dye solution under UV and Vis irradiation. These results imply that the microporous WO 3 /TiO 2 can be used as a template of hybrid electrode because it enables rapid fabrication.

  20. MnWO{sub 4} nanocapsules: Synthesis, characterization and its electrochemical sensing property

    Energy Technology Data Exchange (ETDEWEB)

    Muthamizh, Selvamani; Suresh, Ranganathan; Giribabu, Krishnamoorthy; Manigandan, Ramadoss; Praveen Kumar, Sivakumar; Munusamy, Settu; Narayanan, Vengidusamy, E-mail: vnnara@yahoo.co.in

    2015-01-15

    Highlights: • Synthesis of MnWO{sub 4} nanocapsules without use of any other external reagent. • High crystalline MnWO{sub 4} was obtained with phase purity. • Electrochemical sensing platform based on MnWO{sub 4} for sensing quercetin. • Micromolar detection ability of MnWO{sub 4} modified GCE. - Abstract: Manganese tungstate (MnWO{sub 4}) was synthesized by surfactant free precipitation method. MnWO{sub 4} was characterized by using various spectroscopic techniques. The phase, crystalline nature and the morphological analysis were carried out using XRD, scanning electron microscopy (SEM), and high resolution transmission electron microscopy (HR-TEM). Further, FT-IR, Raman, and DRS-UV–Vis spectral analysis were carried out in order to ascertain the optical property and the presence of functional groups. From the analysis, the morphology of the MnWO{sub 4} was observed to be in capsules with breadth and thickness were in nm range. The oxidation state of tungsten (W), and manganese (Mn) were investigated using X-ray photo electron spectroscopy (XPS) and electron paramagnetic resonance spectroscopy (EPR). The synthesized MnWO{sub 4} nanocapsules were used to modify glassy carbon electrode (GCE) to detect quercetin.

  1. Physical Properties of Macroporous Tungsten Oxide Thin Films and Their Impact on the Photocurrent Density

    Directory of Open Access Journals (Sweden)

    I. Riech

    2013-01-01

    Full Text Available Tungsten trioxide (WO3 films were prepared using polystyrene spheres of two different diameters as a template in order to create porous layers. X-ray diffraction data and electron microscopy images show that annealed films exhibit polycrystalline structure with monoclinic phase and pore size of approximately hundred nanometers. The optical band gap energies have been determined by photoacoustic spectroscopy as 3.17 eV, and this value was not affected by sample morphology. Low temperature photoluminescence spectra exhibit broad band in the blue region. Deconvolutions of PL spectra show that there are two transitions which intensity depends on thin film pore size. We discuss the possible origin of this emissions associated with oxygen vacancies and surface states. A comparative study of the WO3 films used as photoanodes is presented and correlated with PL results.

  2. X-ray diffraction study of WO{sub 3} at high pressure

    Energy Technology Data Exchange (ETDEWEB)

    Bouvier, P. [ESRF, Grenoble (France); Laboratoire d' Electrochimie et de Physico-Chimie des Materiaux et des Interfaces UMR 5631 CNRS-INPG, St. Martin d' Heres (France); Crichton, W.A. [ESRF, Grenoble (France); Boulova, M. [Laboratoire d' Electrochimie et de Physico-Chimie des Materiaux et des Interfaces UMR 5631 CNRS-INPG, St. Martin d' Heres (France); Chemistry Department, Moscow State University, Moscow (Russian Federation); Lucazeau, G. [Laboratoire d' Electrochimie et de Physico-Chimie des Materiaux et des Interfaces UMR 5631 CNRS-INPG, St. Martin d' Heres (France)

    2002-07-08

    The high-pressure behaviour of microcrystalline tungsten oxide (WO{sub 3}) has been investigated with angle-dispersive synchrotron x-ray powder diffraction in a diamond anvil cell up to 40 GPa at room temperature. Up to 21 GPa, the pressure dependence of the volume of the monoclinic high-pressure (P2{sub 1}/c) phase is described by a third-order Birch-Murnaghan equation of state with parameters V{sub 0}=210.9(7)A{sup 3}, K{sub T}=27(2)GP a and K'=9.4(5). At 24 GPa, a first-order phase transition occurs with an approximate {delta} V of 7.4% to a monoclinic P2{sub 1}/a unit cell with a=6.1669(8)A, b=4.5758(6)A, c=5.3159(6)A, {beta}=101.440(9) deg. A second transition is observed at pressures higher than 31 GPa with an approximate {delta} V of 12% to a phase described by a third monoclinic unit cell, with a=10.3633(22)A, b=3.9065(8)A, c=9.3459(18)A and {beta}=98.539(14) deg. (author)

  3. Nanostructured tungsten trioxide thin films synthesized for photoelectrocatalytic water oxidation: a review.

    Science.gov (United States)

    Zhu, Tao; Chong, Meng Nan; Chan, Eng Seng

    2014-11-01

    The recent developments of nanostructured WO3 thin films synthesized through the electrochemical route of electrochemical anodization and cathodic electrodeposition for the application in photoelectrochemical (PEC) water splitting are reviewed. The key fundamental reaction mechanisms of electrochemical anodization and cathodic electrodeposition methods for synthesizing nanostructured WO3 thin films are explained. In addition, the effects of metal oxide precursors, electrode substrates, applied potentials and current densities, and annealing temperatures on size, composition, and thickness of the electrochemically synthesized nanostructured WO3 thin films are elucidated in detail. Finally, a summary is given for the general evaluation practices used to calculate the energy conversion efficiency of nanostructured WO3 thin films and a recommendation is provided to standardize the presentation of research results in the field to allow for easy comparison of reported PEC efficiencies in the near future. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  4. Influence of annealing temperature on microstructure and optical properties of sol-gel derived tungsten oxide films

    International Nuclear Information System (INIS)

    Sun Xilian; Cao Hongtao; Liu Zhimin; Li Jianzhong

    2009-01-01

    Tungsten oxide (WO 3 ) thin films have been extensively studied for their interesting physical properties and a variety of potential applications in electrochromic devices. In order to explore the possibility of using these in electrochromic devices, a preliminary and thorough study of the optical properties of the host materials is an important step. Based on this, the influence of annealing temperature on the structural, surface morphological, optical and electrochromic properties has been investigated in the present work. The host material, WO 3 films, has been prepared from an ethanolic acetylated peroxotungstic acid sol containing 5 wt.% oxalic acid dehydrate (OAD) by sol-gel technique. The monoclinic structure and textured nature change of the films with the temperature increasing have been investigated by X-ray diffraction analysis. The surface morphology evolution of the films has been characterized by SEM. The shift in absorption edge towards the higher wavelength region observed from optical studies may be due to the electron scattering effects and the optical band filling effect that reveals the crystallization of the film. The amorphous film shows better optical modulation (ΔT = 76.9% at λ = 610 nm), fast color-bleach kinetics (t c ∼ 4 s and t b ∼ 9 s) and good reversibility (Q b /Q c = 90%), thereby rendering it suitable for smart window applications.

  5. The gate oxide integrity of CVD tungsten polycide

    International Nuclear Information System (INIS)

    Wu, N.W.; Su, W.D.; Chang, S.W.; Tseng, M.F.

    1988-01-01

    CVD tungsten polycide has been demonstrated as a good gate material in recent very large scale integration (VLSI) technology. CVD tungsten silicide offers advantages of low resistivity, high temperature stability and good step coverage. On the other hand, the polysilicon underlayer preserves most characteristics of the polysilicon gate and acts as a stress buffer layer to absorb part of the thermal stress origin from the large thermal expansion coefficient of tungsten silicide. Nevertheless, the gate oxide of CVD tungsten polycide is less stable or reliable than that of polysilicon gate. In this paper, the gate oxide integrity of CVD tungsten polycide with various thickness combinations and different thermal processes have been analyzed by several electrical measurements including breakdown yield, breakdown fluence, room temperature TDDB, I-V characteristics, electron traps and interface state density

  6. An investigation of the insertion of the cations H{sup +}, Na{sup +}, K{sup +} on the electrochromic properties of the thermally evaporated WO{sub 3} thin films grown at different substrate temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Patel, K.J. [Applied Physics Department, Faculty of Technology and Engineering, M.S. University of Baroda, Kalabhavan, Vadodara 390001, Gujarat (India); Panchal, C.J., E-mail: cjpanchal_msu@yahoo.com [Applied Physics Department, Faculty of Technology and Engineering, M.S. University of Baroda, Kalabhavan, Vadodara 390001, Gujarat (India); Desai, M.S. [Applied Physics Department, Faculty of Technology and Engineering, M.S. University of Baroda, Kalabhavan, Vadodara 390001, Gujarat (India); Mehta, P.K. [Physics Department, Faculty of Science, M.S. University of Baroda, Vadodara 390002, Gujarat (India)

    2010-11-01

    The phenomenon of electrochromism in tungsten trioxide (WO{sub 3}) thin films has recently attained considerable interest due to their enormous applications in inorganic thin film electrochromic devices. We have investigated the compositional, optical, and electrochromic properties of the WO{sub 3} thin films grown at different substrate temperatures by the thermal evaporation of WO{sub 3} powder. The thin films were characterized using X-ray diffraction (XRD), X-ray photo-emission spectroscopy (XPS), and electrochemical techniques. The XPS analysis suggested that the oxygen to tungsten (O/W) ratio decreases, i.e., the oxygen deficiency increases, on increasing the substrate temperature up to 500 deg. C. The electrochemical analysis provided a comparative study of the coloration efficiency (CE) of the WO{sub 3} thin films intercalated with three different ions viz. H{sup +}, Na{sup +}, and K{sup +}. The effect of the variation of the substrate temperature on the CE and the switching time have also been investigated for the WO{sub 3} thin films intercalated with H{sup +} ions; the thin films deposited at RT and intercalated with H{sup +} ions are found to possess adequate electrochromic properties viz. CE and switching time from device point of view.

  7. Cold sprayed WO3 and TiO2 electrodes for photoelectrochemical water and methanol oxidation in renewable energy applications.

    Science.gov (United States)

    Haisch, Christoph; Schneider, Jenny; Fleisch, Manuel; Gutzmann, Henning; Klassen, Thomas; Bahnemann, Detlef W

    2017-10-03

    Films prepared by cold spray have potential applications as photoanodes in electrochemical water splitting and waste water purification. In the present study cold sprayed photoelectrodes produced with WO 3 (active under visible light illumination) and TiO 2 (active under UV illumination) on titanium metal substrates were investigated as photoanodes for the oxidation of water and methanol, respectively. Methanol was chosen as organic model pollutant in acidic electrolytes. Main advantages of the cold sprayed photoelectrodes are the improved metal-semiconductor junctions and the superior mechanical stability. Additionally, the cold spray method can be utilized as a large-scale electrode fabrication technique for photoelectrochemical applications. Incident photon to current efficiencies reveal that cold sprayed TiO 2 /WO 3 photoanodes exhibit the best photoelectrochemical properties with regard to the water and methanol oxidation reactions in comparison with the benchmark photocatalyst Aeroxide TiO 2 P25 due to more efficient harvesting of the total solar light irradiation related to their smaller band gap energies.

  8. Hydrogen-water deuterium exchange over metal oxide promoted nickel catalysts

    Energy Technology Data Exchange (ETDEWEB)

    Sagert, N H; Shaw-Wood, P E; Pouteau, R M.L. [Atomic Energy of Canada Ltd., Pinawa, Manitoba. Whiteshell Nuclear Research Establishment

    1975-11-01

    Specific rates have been measured for hydrogen-water deuterium isotope exchange over unsupported nickel promoted with about 20% of various metal oxides. The oxides used were Cr/sub 2/O/sub 3/, MoO/sub 2/, MnO, WO/sub 2/-WO/sub 3/, and UO/sub 2/. Nickel surface areas, which are required to measure the specific rates, were determined by hydrogen chemisorption. Specific rates were measured as a function of temperature in the range 353 to 573 K and as a function of the partial pressure of hydrogen and water over a 10-fold range of partial pressure. The molybdenum and tungsten oxides gave the highest specific rates, and manganese and uranium oxides the lowest. Chromium oxide was intermediate, although it gave the highest rate per gram of catalyst. The orders with respect to hydrogen and water over molybdenum oxide and tungsten oxide promoted nickel were consistent with a mechanism in which nickel oxide is formed from the reaction of water with the catalyst, and then is reduced by hydrogen. Over manganese and uranium oxide promoted catalysts, these orders are consistent with a mechanism in which adsorbed water exchanges with chemisorbed hydrogen atoms on the nickel surface. Chromium oxide is intermediate. It was noted that those oxides which favored the nickel oxide route had electronic work functions closest to those of metallic nickel and nickel oxide.

  9. Color in 'tungsten trioxide' thin films

    International Nuclear Information System (INIS)

    Gerard, P.; Deneuville, A.; Hollinger, G.; Duc, Tran Minh

    1977-01-01

    We show that evaporated tungsten trioxide amorphous layers commonly used in electrochromic displays actually have the composition WO_2_._7H_y (0.2< y<0.5). We emphasize that coloration of virgin transparent films can be obtained without injection of any external ion into the layer, and further that around a critical substoichiometry by sputtering, namely, WO_2_._5, one can prepare blue virgin layers without any hydrogen. The effect of substoichiometry on the valence of tungsten atoms has been followed by XPS measurements of sputtered layers.

  10. Color in ''tungsten trioxide'' thin films

    International Nuclear Information System (INIS)

    Gerard, P.; Deneuville, A.; Hollinger, G.; Tran Minh Duc

    1977-01-01

    We show that evaporated tungsten trioxide amorphous layers commonly used in electrochromic displays actually have the composition WO/sub 2.7/H/sub y/ (0.2< y<0.5). We emphasize that coloration of virgin transparent films can be obtained without injection of any external ion into the layer, and further that around a critical substoichiometry by sputtering, namely, WO/sub 2.5/, one can prepare blue virgin layers without any hydrogen. The effect of substoichiometry on the valence of tungsten atoms has been followed by XPS measurements of sputtered layers

  11. Gas sensing properties of graphene–WO3 composites prepared by hydrothermal method

    International Nuclear Information System (INIS)

    Chu, Xiangfeng; Hu, Tao; Gao, Feng; Dong, Yongping; Sun, Wenqi; Bai, Linshan

    2015-01-01

    Graphical abstract: - Highlights: • The amount of graphene had an effect on the morphology of graphene–WO 3 composites. • The optimum temperature of 0.1 wt% graphene–WO 3 sensor to acetaldehyde was 100 °C. • 0.1 wt% graphene–WO 3 sensor exhibited good selectivity to acetaldehyde at 100 °C. - Abstract: Graphene–WO 3 composites mixed with different amounts of graphene (0, 0.1, 0.5, 1 and 3 wt%) were prepared by hydrothermal method at 180 °C for 24 h. The as-prepared graphite oxide, graphene and graphene–WO 3 composites were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared spectra (FT-IR) and Raman spectroscopy, respectively. The effect of the amount of graphene in the composites on the gas-sensing responses and the gas-sensing selectivity of the materials was investigated. The experimental results revealed that the sensor based on 0.1 wt% graphene–WO 3 composite exhibited high response and good selectivity to acetaldehyde vapor at 100 °C, the optimum operating temperature of this sensor to 1000 ppm acetaldehyde vapor decreased from 180 °C to 100 °C comparing with that of pure WO 3 . The response time and the recovery time for 100 ppm acetaldehyde vapor were 250 s and 225 s, respectively

  12. CTAB-assisted ultrasonic synthesis, characterization and photocatalytic properties of WO{sub 3}

    Energy Technology Data Exchange (ETDEWEB)

    Sánchez-Martínez, D., E-mail: dansanm@gmail.com; Gomez-Solis, C.; Torres-Martinez, Leticia M.

    2015-01-15

    Highlights: • WO{sub 3} 2D nanostructures were synthesized by ultrasound method assisted with CTAB. • WO{sub 3} morphology was mainly of rectangular nanoplates with a thickness of ∼50 nm. • The highest surface area value of WO{sub 3} was obtained to lowest concentration of CTAB. • WO{sub 3} activity was attributed to morphology, surface area and the addition of CTAB. • WO{sub 3} nanoplates were able to causing almost complete mineralization of rhB and IC. - Abstract: WO{sub 3} 2D nanostructures have been prepared by ultrasound synthesis method assisted with CTAB using different molar ratios. The formation of monoclinic crystal structure of WO{sub 3} was confirmed by X-ray powder diffraction (XRD). The characterization of the WO{sub 3} samples was complemented by analysis of scanning electron microscopy (SEM), which revealed morphology mainly of rectangular nanoplates with a thickness of around 50 nm and length of 100–500 nm. Infrared spectroscopy (FT-IR) was used to confirm the elimination of the CTAB in the synthesized samples. The specific surface area was determinate by the BET method and by means of diffuse reflectance spectroscopy (DRS) it was determinate the band-gap energy (E{sub g}) of the WO{sub 3} samples. The photocatalytic activity of the WO{sub 3} oxide was evaluated in the degradation reactions of rhodamine B (rhB) and indigo carmine (IC) under Xenon lamp irradiation. The highest photocatalytic activity was observed in the samples containing low concentration of CTAB with morphology of rectangular nanoplates and with higher surface area value than commercial WO{sub 3}. Photodegradation of rhB and IC were followed by means of UV–vis absorption spectra. The mineralization degree of organic dyes by WO{sub 3} photocatalyst was determined by total organic carbon analysis (TOC) reaching percentages of mineralization of 92% for rhB and 50% for IC after 96 h of lamp irradiation.

  13. Recovery of tungsten from wolframite from the Igarape Manteiga mine (Rondonia - Brazil) via acidic leaching

    International Nuclear Information System (INIS)

    Paulino, Jessica Frontino; Afonso, Julio Carlos; Mantovano, Jose Luiz; Vianna, Claudio Augusto; Cunha, Jose Waldemar Silva Dias da

    2012-01-01

    We report results of the efficiency of tungsten extraction from wolframite concentrate (containing 61.5 wt % WO 3 ) from the Igarape Manteiga mine (state of Rondonia, Brazil) through acid leaching with strong mineral acids at 100 deg C and 400 rpm for 2-4 h. HCl yielded insoluble matter containing the highest WO 3 content (90 wt %). This solid was dissolved in concentrated NH 3(aq) at 25 deg C and the insoluble matter filtrated. The filtrate was slowly evaporated. 70 wt % of the tungsten present in the starting concentrate material was recovered as ammonium paratungstate (APT). (author)

  14. Towards Near-Infrared Photosensitization of Tungsten Trioxide Nanostructured Films by Upconverting Nanoparticles

    Science.gov (United States)

    Venne, Frederic

    Nanostructured metal oxides semiconductors are widely used in solar energy related applications, such as in dye-sensitized solar cells. Tungsten trioxide (WO3) is an electrochromic material, extensively investigated in solar energy conversion (e.g. photoelectrochemistry) and conservation (e.g. electrochromism). However, WO3, because of its wide bandgap (≈ 2.5 eV), is transparent to an important portion of the solar spectrum and can effectively absorb light only up to ca. 500 nm, which limits the power conversion efficiency of devices based thereon. Upconverting materials can absorb several low-energy photons to emit one high-energy photon. In particular, upconverting nanoparticles are widely studied in biomedical and solar energy applications, as they can transform two or several infrared photons in a visible photon. As the Sun contains important NIR and IR portion, UCNPs are interesting candidates to transform NIR or IR light into visible light to be absorbed by wide bandgap semiconductor, such as metal oxides. The work presented in this master's thesis consists in embedding NaGdF4:Er3+, Yb3+ UCNPs into a nanostructured WO3 matrix. The objective is to increase the power conversion efficiency of WO3 after solar light harvesting. The integration of two materials with nanostructured nature has the potential to lead to a good synergy between them. We include an article in this master's thesis. In this article, we report on the mixing of NaGdF4:Er3+, Yb 3+ UCNPs with WO3 in solution and on the deposition of the two-component solution on ITO-patterned electrodes. After engineering the fabrication and deposition of the thin nanocomposite films, they were systematically studied. Morphology was studied by atomic force microscopy, structure by X-ray diffraction, photoluminescence by fluorescence hyperspectral microscopy, and charge carrier transport under NIR irradiation by current-time measurements. Notably, we observed an increase in the value of the current with

  15. Enhanced photoelectrochemical and photocatalytic activity of WO3-surface modified TiO2 thin film

    Science.gov (United States)

    Qamar, Mohammad; Drmosh, Qasem; Ahmed, Muhammad I.; Qamaruddin, Muhammad; Yamani, Zain H.

    2015-02-01

    Development of nanostructured photocatalysts for harnessing solar energy in energy-efficient and environmentally benign way remains an important area of research. Pure and WO3-surface modified thin films of TiO2 were prepared by magnetron sputtering on indium tin oxide glass, and photoelectrochemical and photocatalytic activities of these films were studied. TiO2 particles were <50 nm, while deposited WO3 particles were <20 nm in size. An enhancement in the photocurrent was observed when the TiO2 surface was modified WO3 nanoparticles. Effect of potential, WO3 amount, and radiations of different wavelengths on the photoelectrochemical activity of TiO2 electrodes was investigated. Photocatalytic activity of TiO2 and WO3-modified TiO2 for the decolorization of methyl orange was tested.

  16. Preparation of Porous F-WO3/TiO2 Films with Visible-Light Photocatalytic Activity by Microarc Oxidation

    Directory of Open Access Journals (Sweden)

    Chung-Wei Yeh

    2012-01-01

    Full Text Available Porous F-WO3/TiO2 (mTiO2 films are prepared on titanium sheet substrates using microarc oxidation (MAO technique. The X-ray diffraction patterns show that visible-light (Vis enabling mTiO2 films with a very high content of anatase TiO2 and high loading of WO3 are successfully synthesized at a low applied voltage of 300 V using electrolyte contenting NaF and Na2WO4 without subsequent heat treatment. The cross-sectional transmission electron microscopy micrograph reveals that the mTiO2 films feature porous networks connected by many micron pores. The diffused reflection spectrum displays broad absorbance across the UV-Vis regions and a significant red shift in the band gap energy (∼2.23 eV for the mTiO2 film. Owing to the high specific surface area from the porous microstructure, the mTiO2 film shows a 61% and 50% rate increase in the photocatalytic dye degradation, as compared with the N,C-codoped TiO2 films under UV and Vis irradiation, respectively.

  17. Tailored temperature window of CuO{sub x}/WO{sub x}–ZrO{sub 2} for NO{sub x} reduction via adjusting the calcination temperature of WO{sub x}–ZrO{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Si, Zhichun, E-mail: si.zhichun@sz.tsinghua.edu.cn [Advanced Materials Institute, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055 (China); Wu, Xiaodong [State Key Laboratory of New Ceramics and Fine Process, Department of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Yangtze Delta Region Institute of Tsinghua University, Zhejiang 314000 (China); Weng, Duan, E-mail: duanweng@tsinghua.edu.cn [State Key Laboratory of New Ceramics and Fine Process, Department of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Ma, Ziran; Ma, Jing [State Key Laboratory of New Ceramics and Fine Process, Department of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China)

    2013-02-15

    WO{sub x}–ZrO{sub 2} support was calcined at various temperatures for obtaining controllable activity of copper catalysts for NO{sub x} reduction by ammonia. The temperature window of copper catalyst for over 80% NO{sub x} conversion shifts from 180–300 to 230–350 °C by elevating the calcination temperature of WO{sub x}–ZrO{sub 2} support from 500 to 600 °C, due to the increased Brønsted acidity and reduced structure and electronic interactions between copper oxides and tungsten oxides arising from the polymerization of WO{sub x} clusters on surface of support. Calcining WO{sub x}–ZrO{sub 2} support at 700 °C leads to the reduced redox property of copper oxides on the Cu–O–W interface and the formation of bulk-like CuO, results in a low activity of catalyst. - Graphical abstract: The temperature window of catalyst for over 80% NO{sub x} conversion shifts from 180-300 °C to 230–350 °C by elevating the calcination temperature of WO{sub x}–ZrO{sub 2} support from 500 °C to 600 °C. Highlights: ► The temperature window of catalyst is tailored by calcining the support. ► The mechanisms of tailoring the temperature window of catalyst are discussed. ► The polymerization of WO{sub x} leads to the increased Brønsted acidity of catalysts. ► The CuO{sub x}/WO{sub x} interactions are reduced by elevating calcination temperature of support.

  18. Colour centres in amorphous tungsten trioxide thin films

    International Nuclear Information System (INIS)

    Kleperis, J.J.; Cikmach, P.D.; Lusis, A.R.

    1984-01-01

    Magnetic, optical, and electrical properties of thin tungsten trioxide (a-WO 3 ) films obtained on substrates with different temperatures and annealed in air and vacuum are investigated. On the basis of these results and recent structural investigations a structure model of the a-WO 3 film is given: a spatial network of tightly bounded clusters which are built from hydrated WO 6 octahedra. These octahedra contain terminal oxygens and being axially distorted they are the sites for localization of injected electrons. The colour centres formed are paramagnetic (ESR signal from W 5+ ) and their optical absorption is satisfactorily described by the intervalence charge transfer between the localized states of W 5+ and W 6+ ions. (author)

  19. A novel composite electrode based on tungsten oxide nanoparticles and carbon nanotubes for the electrochemical determination of paracetamol

    International Nuclear Information System (INIS)

    Baytak, Aysegul Kutluay; Duzmen, Sehriban; Teker, Tugce; Aslanoglu, Mehmet

    2015-01-01

    An electrochemical sensor was prepared by the modification of a glassy carbon electrode (GCE) with a composite of nanoparticles of tungsten oxide (WO 3 ) and carbon nanotubes (CNTs) for the quantification of paracetamol (PR). Energy dispersive X-ray analysis (EDX) and scanning electron microscopy (SEM) were performed for the characterization of the nanocomposite layer. Compared with a bare GCE and a GCE modified with CNTs, the proposed electrode (WO 3 NPs/CNTs/GCE) exhibited a well-defined redox couple for PR and a marked enhancement of the current response. The experimental results also showed that ascorbic acid (AA) did not interfere with the selective determination of PR. The proposed electrode was used for the determination of PR in 0.1 M phosphate buffer solution (PBS) at pH 7.0 using square wave voltammetry (SWV). The peak current increased linearly with the concentration of PR in the range of 1.0 × 10 −9 –2.0 × 10 −7 M. The detection limit (LOD) was 5.54 × 10 −11 M (based on 3 S b /m). The proposed voltammetric sensor provided long-time stability, improved voltammetric behavior and good reproducibility for PR. The selective, accurate and precise determination of PR makes the proposed electrode of great interest for monitoring its therapeutic use. - Highlights: • A voltammetric nanosensor was prepared using nanoparticles of WO 3 and CNTs. • A selective quantification of paracetamol was carried out in the presence of AA. • A linear plot was obtained for current responses versus concentrations over the range from 1.0 × 10 −9 to 2.0 × 10 −7 M. • A detection limit of 554 pM was obtained for paracetamol using the proposed nanosensor. • An accurate quantification makes the proposed nanosensor of great interest for public health

  20. Microwave mediated synthesis of nanostructured Co -WO_3 and CoWO_4 for supercapacitor applications

    International Nuclear Information System (INIS)

    Dhilip Kumar, R.; Karuppuchamy, S.

    2016-01-01

    Co-WO_3 and CoWO_4 nanopowders have been successfully obtained from microwave mediated process. The characterization of the prepared nanopowders was carried out by X-ray diffraction (XRD), scanning electron microscopy and Energy dispersive X-ray spectroscopy techniques. The XRD pattern confirms the formation of orthorhombic and monoclinic phase of the as-synthesized and calcined samples, respectively. Scanning electron microscopic examination of the resultant powders reveals the formation of nanoporous morphology. The electrochemical performance of the Co-WO_3 and CoWO_4 coated electrodes was also investigated. The maximum specific capacitance of 45 F/g was achieved for the Co-WO_3 nanopowder. - Highlights: • Novel nano-sized Co-WO_3 and CoWO_4 materials have been prepared. • A new and simple solution growth technique was developed. • Co-WO_3 is a promising material for supercapacitor applications.

  1. Improved electrochromical properties of sol-gel WO3 thin films by doping gold nanocrystals

    International Nuclear Information System (INIS)

    Naseri, N.; Azimirad, R.; Akhavan, O.; Moshfegh, A.Z.

    2010-01-01

    In this investigation, the effect of gold nanocrystals on the electrochromical properties of sol-gel Au doped WO 3 thin films has been studied. The Au-WO 3 thin films were dip-coated on both glass and indium tin oxide coated conducting glass substrates with various gold concentrations of 0, 3.2 and 6.4 mol%. Optical properties of the samples were studied by UV-visible spectrophotometry in a range of 300-1100 nm. The optical density spectra of the films showed the formation of gold nanoparticles in the films. The optical bandgap energy of Au-WO 3 films decreased with increasing the Au concentration. Crystalline structure of the doped films was investigated by X-ray diffractometry, which indicated formation of gold nanocrystals in amorphous WO 3 thin films. X-ray photoelectron spectroscopy (XPS) was used to study the surface chemical composition of the samples. XPS analysis indicated the presence of gold in metallic state and the formation of stoichiometric WO 3 . The electrochromic properties of the Au-WO 3 samples were also characterized using lithium-based electrolyte. It was found that doping of Au nanocrystals in WO 3 thin films improved the coloration time of the layer. In addition, it was shown that variation of Au concentration led to color change in the colored state of the Au-WO 3 thin films.

  2. Matrix Assisted and/or Laser Desorption Ionization Quadrupole Ion Trap Time-of-Flight Mass Spectrometry of WO3 Clusters Formation in Gas Phase. Nanodiamonds, Fullerene, and Graphene Oxide Matrices

    Science.gov (United States)

    Ausekar, Mayuri Vilas; Mawale, Ravi Madhukar; Pazdera, Pavel; Havel, Josef

    2018-03-01

    The formation of W x O y +●/-● clusters in the gas phase was studied by laser desorption ionization (LDI) and matrix assisted laser desorption ionization (MALDI) of solid WO3. LDI produced (WO3) n + ●/- ● ( n = 1-7) clusters. In MALDI, when using nano-diamonds (NDs), graphene oxide (GO), or fullerene (C60) matrices, higher mass clusters were generated. In addition to (WO3) n -● clusters, oxygen-rich or -deficient species were found in both LDI and MALDI (with the total number of clusters exceeding one hundred ≈ 137). This is the first time that such matrices have been used for the generation of(WO3) n + ●/-● clusters in the gas phase, while new high mass clusters (WO3) n -● ( n = 12-19) were also detected. [Figure not available: see fulltext.

  3. Photoelectrochemical Properties and Behavior of α-SnWO4 Photoanodes Synthesized by Hydrothermal Conversion of WO3 Films.

    Science.gov (United States)

    Zhu, Zhehao; Sarker, Pranab; Zhao, Chenqi; Zhou, Lite; Grimm, Ronald L; Huda, Muhammad N; Rao, Pratap M

    2017-01-18

    Metal oxides with moderate band gaps are desired for efficient production of hydrogen from sunlight and water via photoelectrochemical (PEC) water splitting. Here, we report an α-SnWO 4 photoanode synthesized by hydrothermal conversion of WO 3 films that achieves photon to current conversion at wavelengths up to 700 nm (1.78 eV). This photoanode is promising for overall PEC water-splitting because the flat-band potential and voltage of photocurrent onset are more negative than the potential of hydrogen evolution. Furthermore, the photoanode utilizes a large portion of the solar spectrum. However, the photocurrent density reaches only a small fraction of that which is theoretically possible. Density functional theory based thermodynamic and electronic structure calculations were performed to elucidate the nature and impact of defects in α-SnWO 4 prepared by this synthetic route, from which hole localization at Sn-at-W antisite defects was determined to be a likely cause for the poor photocurrent. Measurements further showed that the photocurrent decreases over time due to surface oxidation, which was suppressed by improving the kinetics of hole transfer at the semiconductor/electrolyte interface. Alternative synthetic methods and the addition of protective coatings and/or oxygen evolution catalysts are suggested to improve the PEC performance and stability of this promising α-SnWO 4 material.

  4. Understanding metal–insulator transition in sodium tungsten bronze

    Indian Academy of Sciences (India)

    2015-05-20

    May 20, 2015 ... We have carried out angle-resolved photoemission spectroscopy (ARPES) and spectromicroscopy studies to understand the metal–insulator transition (MIT) observed in sodium tungsten bronzes, NaWO3. The experimentally determined band structure is compared with the theoretical calculation based ...

  5. Photodecomposition Profile of Curcumin in the Existence of Tungsten Trioxide Particles

    Science.gov (United States)

    Nandiyanto, A. B. D.; Zaen, R.; Oktiani, R.; Abdullah, A. G.

    2018-02-01

    The purpose of this study was to investigate the stability of curcumin solution in the existence of tungsten trioxide (WO3) particles under light illumination. In the experimental method, curcumin extracted from Indonesian local turmeric was added with WO3 microparticles and put into the photoreactor system. The photostability performance of curcumin was conducted for 22 hours using 100 W of Neon Lamp. The results showed that the curcumin solution was relatively stable. When curcumin without existence of WO3 was irradiated, no change in the curcumin concentration was found. However, when curcumin solution was mixed with WO3 particles, decreases in the concentration of curcumin was found. The concentration of curcumin with WO3 after light irradiation was about 73.58%. Based on the results, we concluded that the curcumin is relatively stable against light. However, its lightirradiation stability decreases with additional inorganic material.

  6. Mesoporous tungsten oxynitride as electrocatalyst for promoting redox reactions of vanadium redox couple and performance of vanadium redox flow battery

    Science.gov (United States)

    Lee, Wonmi; Jo, Changshin; Youk, Sol; Shin, Hun Yong; Lee, Jinwoo; Chung, Yongjin; Kwon, Yongchai

    2018-01-01

    For enhancing the performance of vanadium redox flow battery (VRFB), a sluggish reaction rate issue of V2+/V3+ redox couple evaluated as the rate determining reaction should be addressed. For doing that, mesoporous tungsten oxide (m-WO3) and oxyniride (m-WON) structures are proposed as the novel catalysts, while m-WON is gained by NH3 heat treatment of m-WO3. Their specific surface area, crystal structure, surface morphology and component analysis are measured using BET, XRD, TEM and XPS, while their catalytic activity for V2+/V3+ redox reaction is electrochemically examined. As a result, the m-WON shows higher peak current, smaller peak potential difference, higher electron transfer rate constant and lower charge transfer resistance than other catalysts, like the m-WO3, WO3 nanoparticle and mesoporous carbon, proving that it is superior catalyst. Regarding the charge-discharge curve tests, the VRFB single cell employing the m-WON demonstrates high voltage and energy efficiencies, high specific capacity and low capacity loss rate. The excellent results of m-WON are due to the reasons like (i) reduced energy band gap, (ii) reaction familiar surface functional groups and (ii) greater electronegativity.

  7. Preparation and characterization of WO{sub 3} nanoparticles, WO{sub 3}/TiO{sub 2} core/shell nanocomposites and PEDOT:PSS/WO{sub 3} composite thin films for photocatalytic and electrochromic applications

    Energy Technology Data Exchange (ETDEWEB)

    Boyadjiev, Stefan I., E-mail: boiajiev@gmail.com [MTA-BME Technical Analytical Chemistry Research Group, Szent Gellért tér 4, Budapest, H-1111 (Hungary); Santos, Gustavo dos Lopes; Szűcs, Júlia [Budapest University of Technology and Economics, Department of Inorganic and Analytical Chemistry, Szent Gellért tér 4, Budapest, H-1111 (Hungary); Szilágyi, Imre M., E-mail: imre.szilagyi@mail.bme.hu [MTA-BME Technical Analytical Chemistry Research Group, Szent Gellért tér 4, Budapest, H-1111 (Hungary); Budapest University of Technology and Economics, Department of Inorganic and Analytical Chemistry, Szent Gellért tér 4, Budapest, H-1111 (Hungary)

    2016-03-25

    In this study, monoclinic WO{sub 3} nanoparticles were obtained by thermal decomposition of (NH{sub 4}){sub x}WO{sub 3} in air at 600 °C. On them by atomic layer deposition (ALD) TiO{sub 2} films were deposited, and thus core/shell WO{sub 3}/TiO{sub 2} nanocomposites were prepared. We prepared composites of WO{sub 3} nanoparticles with conductive polymer as PEDOT:PSS, and deposited thin films of them on glass and ITO substrates by spin coating. The formation, morphology, composition and structure of the as-prepared pure and composite nanoparticles, as well thin films, were studied by TEM, SEM-EDX and XRD. The photocatalytic activity of both the WO{sub 3} and core/shell WO{sub 3}/TiO{sub 2} nanoparticles was studied by decomposing methyl orange in aqueous solution under UV light irradiation. Cyclic voltammetry measurements were performed on the composite PEDOT:PSS/WO{sub 3} thin films, and the coloring and bleaching states were studied.

  8. Growth study and photocatalytic properties of Co-doped tungsten oxide mesocrystals

    International Nuclear Information System (INIS)

    Sun, Shibin; Chang, Xueting; Li, Zhenjiang

    2012-01-01

    Cobalt-doped tungsten oxide mesocrystals with different morphologies have been successfully generated using a solvothermal method with tungsten hexachloride and cobalt chloride salts as precursors. The resulting mesocrystals were characterized by X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy, Brunauer–Emmet–Teller analysis of nitrogen sorptometer, and UV–vis diffuse reflectance spectroscopy. The photocatalytic properties of the cobalt-doped tungsten oxide mesocrystals were evaluated on the basis of their ability to degrade methyl orange in an aqueous solution under simulated sunlight irradiation. Results showed that the cobalt doping had obvious effect on the morphologies of the final products, and lenticular and blocky cobalt-doped tungsten oxide mesocrystals could be obtained with 1.0 wt.% and 2.0 wt.% cobalt doping, respectively. The cobalt-doped tungsten oxides exhibited superior photocatalytic activities to that of the undoped tungsten oxide. - Graphical abstract: Schematic illustrations of the growth of the bundled nanowires, lenticular mesocrystals, and blocky mesocrystals. Highlights: ► Co-doped W 18 O 49 mesocrystals were synthesized using a solvothermal method. ► The Co doping has obvious effect on the morphology of the final mesocrystals. ► The Co-doped W 18 O 49 exhibited superior photocatalytic activity to the undoped W 18 O 49 .

  9. Investigation on the photophysical properties of tungsten trioxide and tungstate based nanocomposites

    Science.gov (United States)

    Palanisamy, G.; Pazhanivel, T.

    2018-04-01

    Tungsten trioxide (WO3), Metal tungstates (SrWO4, Cr2WO6), WO3/SrWO4 and WO3/Cr2WO6 nanocomposites were successfully prepared by microwave irradiation method at relatively low temperature (500 °C). The synthesized samples were subjected to different investigation techniques, to know the materials physical and chemical properties. The structural and phase change formation of nanoparticles were investigated through XRD analysis. It shows that, the nanoparticles have highly crystalline nature. The shape and composition of the prepared nanoparticles were investigated through SEM and EDAX analysis. The optical properties of the synthesized samples were verified by Ultraviolet-diffuse reflectance spectroscopy and photoluminescence spectrometer. The emission intensity maximum of WO3 nanoparticle was red shifted when compared to composites. It may be due to the effect of delocalized electrons in the parent material. Simultaneously, the emission intensity was decreased because of trap states occurred on the surface of the composite nanoparticles. The photoluminescence spectra of the synthesized samples exhibit different emission (violet and blue) behavior. Hence, it may be useful for light emitting diode (LED) applications.

  10. Prism inside. Spectroscopic and magnetic properties of the lanthanide(III) chloride oxidotungstates(VI) Ln{sub 3}Cl{sub 3}[WO{sub 6}] (Ln = La - Nd, Sm - Tb)

    Energy Technology Data Exchange (ETDEWEB)

    Dorn, Katharina V.; Blaschkowski, Bjoern; Hartenbach, Ingo [Institute for Inorganic Chemistry, University of Stuttgart (Germany); Foerg, Katharina; Netzsch, Philip; Hoeppe, Henning A. [Institute for Physics, University of Augsburg (Germany)

    2017-11-17

    The lanthanide(III) chloride oxidotungstates(VI) with the formula Ln{sub 3}Cl{sub 3}[WO{sub 6}] for Ln = La - Nd, Sm - Tb were synthesized by solid-state reactions utilizing the respective lanthanide trichloride, lanthanide sesquioxide (where available), and tungsten trioxide together with lithium chloride as flux. The title compounds crystallize hexagonally in space group P6{sub 3}/m (no. 176, a = 941-909, c = 543-525 pm, Z = 2). The structures comprise crystallographically unique Ln{sup 3+} cations surrounded by six O{sup 2-} and four Cl{sup -} anions (C.N. = 10) forming distorted tetracapped trigonal prisms as well as rather uncommon trigonal prismatic [WO{sub 6}]{sup 6-} units, whose edges are coordinated by nine Ln{sup 3+} cations. Thus, a {sup 3}{sub ∞}{([WO_6]Ln"e_9_/_3)"3"+} framework (e = edge-sharing) is created, which contains tube-shaped channels along [001] lined with chloride anions. To elucidate the spectroscopic and magnetic properties of the obtained pure phase samples, single-crystal Raman (for Ln = La - Nd, Sm-Tb), diffuse reflectance (for Ln = La, Pr, Nd, Gd), and luminescence spectroscopy (for bulk Ln{sub 3}Cl{sub 3}[WO{sub 6}] (Ln = La, Eu, Gd, Tb) and Eu{sup 3+}- or Tb{sup 3+}-doped derivatives of La{sub 3}Cl{sub 3}[WO{sub 6}] and Gd{sub 3}Cl{sub 3}[WO{sub 6}], respectively) were performed and their temperature-dependent magnetic moments (for Ln = Pr, Nd, Gd) were determined. (copyright 2017 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  11. Crystal nucleus formation on the cathode under conditions of supersaturation of melt by lower valent forms

    International Nuclear Information System (INIS)

    Kaliev, K.A.; Aksent'ev, A.G.; Baraboshkin, A.N.

    1979-01-01

    Nucleation on the cathode of sodium-tungsten bronzes forom the Na 2 WO 4 -WO 3 melt, containing 40 mol.% WO 3 is studied. It has been found that in the initial period the cathode deposition of sodium-tungsten bronze is preceeded by the formation of tungsten soluble lower reduced forms, the concentration of which can considerably exceed the equilibrium one because of excessive overstress of oxide bronze crystal nucleation. The polarization of cathode and change of its potential at the crystal nucleation of sodium-tungsten bronze and switching-off of the electrolysis current has been studied

  12. Visible-light photocatalytic activity of graphene oxide-wrapped Bi2WO6 hierarchical microspheres

    Science.gov (United States)

    Zhai, Jiali; Yu, Hongwen; Li, Haiyan; Sun, Lei; Zhang, Kexin; Yang, Hongjun

    2015-07-01

    A facile approach of fabricating homogeneous graphene oxide (GO)-wrapped Bi2WO6 microspheres (GO/Bi2WO6) is developed. The transmission electron microscopy (TEM) results show that a heterojunction interface between GO and Bi2WO6. The UV-vis diffuse reflection spectra (DRS) reveal that the as-prepared GO/Bi2WO6 composites own more intensive absorption in the visible light range compared with pure Bi2WO6. These characteristic structural and optical properties endow GO/Bi2WO6 composites with enhanced photocatalytic activity. The enhanced photocatalytic activity of the GO/Bi2WO6 is attributed predominantly to the synergetic effect between GO and Bi2WO6, causing rapid generation and separation of photo-generated charge carriers.

  13. A supercritical carbon dioxide plasma process for preparing tungsten oxide nanowires

    International Nuclear Information System (INIS)

    Kawashima, Ayato; Nomura, Shinfuku; Toyota, Hiromichi; Takemori, Toshihiko; Mukasa, Shinobu; Maehara, Tsunehiro

    2007-01-01

    A supercritical carbon dioxide (CO 2 ) plasma process for fabricating one-dimensional tungsten oxide nanowires coated with amorphous carbon is presented. High-frequency plasma was generated in supercritical carbon dioxide at 20 MPa by using tungsten electrodes mounted in a supercritical cell, and subsequently an organic solvent was introduced with supercritical carbon dioxide into the plasma. Electron microscopy and Raman spectroscopy investigations of the deposited materials showed the production of tungsten oxide nanowires with or without an outer layer. The nanowires with an outer layer exhibited a coaxial structure with an outer concentric layer of amorphous carbon and an inner layer of tungsten oxide with a thickness and diameter of 20-30 and 10-20 nm, respectively

  14. Chemically produced nanostructured ODS-lanthanum oxide-tungsten composites sintered by spark plasma

    International Nuclear Information System (INIS)

    Yar, Mazher Ahmed; Wahlberg, Sverker; Bergqvist, Hans; Salem, Hanadi G.; Johnsson, Mats; Muhammed, Mamoun

    2011-01-01

    High purity W and W-0.9La 2 O 3 (wt.%) nanopowders were produced by a wet chemical route. The precursor was prepared by the reaction of ammonium paratungstate (APT) with lanthanum salt in aqueous solutions. High resolution electron microscopy investigations revealed that the tungstate particles were coated with oxide precipitates. The precursor powder was reduced to tungsten metal with dispersed lanthanum oxide. Powders were consolidated by spark plasma sintering (SPS) at 1300 and 1400 o C to suppress grain growth during sintering. The final grain size relates to the SPS conditions, i.e. temperature and heating rate, regardless of the starting powder particle size. Scanning electron microscopy revealed that oxide phases were mainly accumulated at grain boundaries while the tungsten matrix constituted of nanosized sub-grains. The transmission electron microscopy revealed that the tungsten grains consist of micron-scale grains and finer sub-grains. EDX analysis confirmed the presence of W in dispersed oxide phases with varying chemical composition, which evidenced the presence of complex oxide phases (W-O-La) in the sintered metals.

  15. Thermal-treatment effect on the photoluminescence and gas-sensing properties of tungsten oxide nanowires

    International Nuclear Information System (INIS)

    Sun, Shibin; Chang, Xueting; Li, Zhenjiang

    2010-01-01

    Single-crystalline non-stoichiometric tungsten oxide nanowires were initially prepared using a simple solvothermal method. High resolution transmission electron microscopy (HRTEM) investigations indicate that the tungsten oxide nanowires exhibit various crystal defects, including stacking faults, dislocations, and vacancies. A possible defect-induced mechanism was proposed to account for the temperature-dependent morphological evolution of the tungsten oxide nanowires under thermal processing. Due to the high specific surface areas and non-stoichiometric crystal structure, the original tungsten oxide nanowires were highly sensitive to ppm level ethanol at room temperature. Thermal treatment under dry air condition was found to deteriorate the selectivity of room-temperature tungsten oxide sensors, and 400 o C may be considered as the top temperature limit in sensor applications for the solvothermally-prepared nanowires. The photoluminescence (PL) characteristics of tungsten oxide nanowires were also strongly influenced by thermal treatment.

  16. Thermal-treatment effect on the photoluminescence and gas-sensing properties of tungsten oxide nanowires

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Shibin [College of Electromechanical Engineering, Qingdao University of Science and Technology, Qingdao 266061, Shandong (China); Chang, Xueting [Institute of Materials Science and Engineering, Ocean University of China, Qingdao 266100, Shandong (China); Li, Zhenjiang, E-mail: zjli126@126.com [College of Electromechanical Engineering, Qingdao University of Science and Technology, Qingdao 266061, Shandong (China)

    2010-09-15

    Single-crystalline non-stoichiometric tungsten oxide nanowires were initially prepared using a simple solvothermal method. High resolution transmission electron microscopy (HRTEM) investigations indicate that the tungsten oxide nanowires exhibit various crystal defects, including stacking faults, dislocations, and vacancies. A possible defect-induced mechanism was proposed to account for the temperature-dependent morphological evolution of the tungsten oxide nanowires under thermal processing. Due to the high specific surface areas and non-stoichiometric crystal structure, the original tungsten oxide nanowires were highly sensitive to ppm level ethanol at room temperature. Thermal treatment under dry air condition was found to deteriorate the selectivity of room-temperature tungsten oxide sensors, and 400 {sup o}C may be considered as the top temperature limit in sensor applications for the solvothermally-prepared nanowires. The photoluminescence (PL) characteristics of tungsten oxide nanowires were also strongly influenced by thermal treatment.

  17. MIS gas sensors based on porous silicon with Pd and WO{sub 3}/Pd electrodes

    Energy Technology Data Exchange (ETDEWEB)

    Solntsev, V.S. [Institute of Semiconductor Physics, National Academy of Science of Ukraine, 03028, Kiev (Ukraine); Gorbanyuk, T.I., E-mail: tatyanagor@mail.r [Institute of Semiconductor Physics, National Academy of Science of Ukraine, 03028, Kiev (Ukraine); Litovchenko, V.G.; Evtukh, A.A. [Institute of Semiconductor Physics, National Academy of Science of Ukraine, 03028, Kiev (Ukraine)

    2009-09-30

    Pd and WO{sub 3}/Pd gate metal-oxide-semiconductor (MIS) gas sensitive structures based on porous silicon layers are studied by the high frequency C(V) method. The chemical compositions of composite WO{sub 3}/Pd electrodes are characterized by secondary-ion mass spectrometry (SIMS). The atomic force microscopy (AFM) was used for morphologic studies of WO{sub 3}/Pd films. As shown in the experiments, WO{sub 3}/Pd structures are more sensitive and selective to the adsorption of hydrogen sulphide compared to Pd gate. The analyses of kinetic characteristics allow us to determine the response and characteristic times for these structures. The response time of MIS-structures with thin composite WO{sub 3}/Pd electrodes (the thickness of Pd is about 50 nm with WO{sub 3} clusters on its surface) is slower compared to the structures with Pd electrodes. Slower sensor responses of WO{sub 3}-based gas sensors may be associated with different mechanism of gas sensitivity of given structures. The enhanced sensitivity and selectivity to H{sub 2}S action of WO{sub 3}/Pd MIS-structures can also be explained by the chemical reaction that occurs at the catalytic active surface of gate electrodes. The possible mechanisms of enhanced sensitivity and selectivity to H{sub 2}S adsorption of MIS gas sensors with WO{sub 3}/Pd composite gate electrodes compared to pure Pd have been analyzed.

  18. Tungsten and molybdenum with oxide dispersion, production and properties

    International Nuclear Information System (INIS)

    Haerdtle, S.; Schmidberger, R.

    1989-01-01

    By the reaction spray process metal powders with dispersed metal oxides can be produced in one step. The systems investigated here are tungsten and molybdenum with 0,5% resp. 5% La 2 O 3 , Y 2 O 3 and ZrO 2 . The oxides with diameters below 0,5μm are finely dispersed within the metal powder particles. The sinterability of the powders depends on the oxide content. Maximum density at an oxide content of 0,5% is about 96% at a sintering temperature of 1600 0 C. The type of oxide influences the densification versus temperature but not the final density. 5 refs., 11 figs. (Author)

  19. Electronic Structure Control of Tungsten Oxide Activated by Ni for Ultrahigh-Performance Supercapacitors.

    Science.gov (United States)

    Meng, Tian; Kou, Zongkui; Amiinu, Ibrahim Saana; Hong, Xufeng; Li, Qingwei; Tang, Yongfu; Zhao, Yufeng; Liu, Shaojun; Mai, Liqiang; Mu, Shichun

    2018-04-17

    Tuning the electron structure is of vital importance for designing high active electrode materials. Here, for boosting the capacitive performance of tungsten oxide, an atomic scale engineering approach to optimize the electronic structure of tungsten oxide by Ni doping is reported. Density functional theory calculations disclose that through Ni doping, the density of state at Fermi level for tungsten oxide can be enhanced, thus promoting its electron transfer. When used as electrode of supercapacitors, the obtained Ni-doped tungsten oxide with 4.21 at% Ni exhibits an ultrahigh mass-specific capacitance of 557 F g -1 at the current density of 1 A g -1 and preferable durability in a long-term cycle test. To the best of knowledge, this is the highest supercapacitor performance reported so far in tungsten oxide and its composites. The present strategy demonstrates the validity of the electronic structure control in tungsten oxide via introducing Ni atoms for pseudocapacitors, which can be extended to other related fields as well. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  20. Growth study and photocatalytic properties of Co-doped tungsten oxide mesocrystals

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Shibin [College of Logistics Engineering, Shanghai Maritime University, Shanghai 200135 (China); College of Electromechanical Engineering, Qingdao University of Science and Technology, Qingdao 266061 (China); Chang, Xueting, E-mail: xuetingchang@yahoo.cn [College of Logistics Engineering, Shanghai Maritime University, Shanghai 200135 (China); Li, Zhenjiang [College of Electromechanical Engineering, Qingdao University of Science and Technology, Qingdao 266061 (China)

    2012-11-15

    Cobalt-doped tungsten oxide mesocrystals with different morphologies have been successfully generated using a solvothermal method with tungsten hexachloride and cobalt chloride salts as precursors. The resulting mesocrystals were characterized by X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy, Brunauer-Emmet-Teller analysis of nitrogen sorptometer, and UV-vis diffuse reflectance spectroscopy. The photocatalytic properties of the cobalt-doped tungsten oxide mesocrystals were evaluated on the basis of their ability to degrade methyl orange in an aqueous solution under simulated sunlight irradiation. Results showed that the cobalt doping had obvious effect on the morphologies of the final products, and lenticular and blocky cobalt-doped tungsten oxide mesocrystals could be obtained with 1.0 wt.% and 2.0 wt.% cobalt doping, respectively. The cobalt-doped tungsten oxides exhibited superior photocatalytic activities to that of the undoped tungsten oxide. - Graphical abstract: Schematic illustrations of the growth of the bundled nanowires, lenticular mesocrystals, and blocky mesocrystals. Highlights: Black-Right-Pointing-Pointer Co-doped W{sub 18}O{sub 49} mesocrystals were synthesized using a solvothermal method. Black-Right-Pointing-Pointer The Co doping has obvious effect on the morphology of the final mesocrystals. Black-Right-Pointing-Pointer The Co-doped W{sub 18}O{sub 49} exhibited superior photocatalytic activity to the undoped W{sub 18}O{sub 49}.

  1. Structural, morphological, gas sensing and photocatalytic characterization of MoO3 and WO3 thin films prepared by the thermal vacuum evaporation technique

    Science.gov (United States)

    Arfaoui, A.; Touihri, S.; Mhamdi, A.; Labidi, A.; Manoubi, T.

    2015-12-01

    Thin films of molybdenum trioxide and tungsten trioxide were deposited on glass substrates using a simplified thermal evaporation under vacuum method monitored by heat treatment in flowing oxygen at 500 °C for 1 h. The structural and morphological properties of the films were investigated using X-ray diffraction, Raman spectroscopy, atomic force microscopy and scanning electron microscopy. The X-ray diffraction analysis shows that the films of MoO3 and WO3 were well crystallized in orthorhombic and monoclinic phase respectively with the crystallites preferentially oriented toward (2 0 0) direction parallel a-axis for both samples. In literature, we have shown in previous papers that structural and surface morphology of metal thin films play an important role in the gas detection mechanism. In this article, we have studied the response evolution of MoO3 and WO3 thin films sensors ethanol versus time, working temperature and the concentration of the ethanol. It was found that these films had high sensitivity to ethanol, which made them as a good candidate for the ethanol sensor. Finally, the photocatalytic activity of the samples was evaluated with respect to the degradation reaction of a wastewater containing methylene blue (MB) under UV-visible light irradiation. The molybdenum trioxide exhibits a higher degradation rate than the tungsten trioxide thin films under similar experimental conditions.

  2. Oxygen-ion-migration-modulated bipolar resistive switching and complementary resistive switching in tungsten/indium tin oxide/gold memory device

    Science.gov (United States)

    Wu, Xinghui; Zhang, Qiuhui; Cui, Nana; Xu, Weiwei; Wang, Kefu; Jiang, Wei; Xu, Qixing

    2018-06-01

    In this paper, we report our investigation of room-temperature-fabricated tungsten/indium tin oxide/gold (W/ITO/Au) resistive random access memory (RRAM), which exhibits asymmetric bipolar resistive switching (BRS) behavior. The device displays good write/erase endurance and data retention properties. The device shows complementary resistive switching (CRS) characteristics after controlling the compliance current. A WO x layer electrically formed at the W/ITO in the forming process. Mobile oxygen ions within ITO migrate toward the electrode/ITO interface and produce a semiconductor-like layer that acts as a free-carrier barrier. The CRS characteristic here can be elucidated in light of the evolution of an asymmetric free-carrier blocking layer at the electrode/ITO interface.

  3. Elaboration, physical and electrochemical characterizations of CO tolerant PEMFC anode materials. Study of platinum-molybdenum and platinum-tungsten alloys and composites; Elaborations et caracterisations electrochimiques et physiques de materiaux d'anode de PEMFC peu sensibles a l'empoisonnement par CO: etude d'alliages et de composites a base de platine-molybdene et de platine-tungstene

    Energy Technology Data Exchange (ETDEWEB)

    Peyrelade, E.

    2005-06-15

    PEMFC development is hindered by the CO poisoning ability of the anode platinum catalyst. It has been previously shown that the oxidation potential of carbon monoxide adsorbed on the platinum atoms can be lowered using specific Pt based catalysts, either metallic alloys or composites. The objective is then to realize a catalyst for which the CO oxidation is compatible with the working potential of a PEMFC anode. In our approach, to enhance the CO tolerance of platinum based catalyst supported on carbon, we studied platinum-tungsten and platinum-molybdenum alloys and platinum-metal oxide materials (Pt-WO{sub x} and Pt-MoO{sub x}). The platinum based alloys demonstrate a small effect of the second metal towards the oxidation of carbon monoxide. The platinum composites show a better tolerance to carbon monoxide. Electrochemical studies on both Pt-MoO{sub x} and Pt-WO{sub x} demonstrate the ability of the metal-oxides to promote the ability of Pt to oxidize CO at low potentials. However, chrono-amperometric tests reveal a bigger influence of the tungsten oxide. Complex chemistry reactions on the molybdenum oxide surface make it more difficult to observe. (author)

  4. Photocatalytic properties of h-WO{sub 3} nanoparticles obtained by annealing and h-WO{sub 3} nanorods prepared by hydrothermal method

    Energy Technology Data Exchange (ETDEWEB)

    Boyadjiev, Stefan I., E-mail: boiajiev@gmail.com [MTA-BME Technical Analytical Chemistry Research Group, Szent Gellért tér 4, Budapest, H-1111 (Hungary); Nagy-Kovács, Teodóra [Budapest University of Technology and Economics, Department of Inorganic and Analytical Chemistry, Szent Gellért tér 4, Budapest, H-1111 (Hungary); Lukács, István [Hungarian Academy of Sciences, Research Centre for Energy, Institute of Technical Physics and Materials Science, H-1121 Budapest, Konkoly Thege M. út 29-33 (Hungary); Szilágyi, Imre M., E-mail: imre.szilagyi@mail.bme.hu [MTA-BME Technical Analytical Chemistry Research Group, Szent Gellért tér 4, Budapest, H-1111 (Hungary); Budapest University of Technology and Economics, Department of Inorganic and Analytical Chemistry, Szent Gellért tér 4, Budapest, H-1111 (Hungary)

    2016-03-25

    In the present study, two different methods for preparing hexagonal WO{sub 3} (h-WO{sub 3}) photocatalysts were used - controlled thermal decomposition and hydrothermal synthesis. WO{sub 3} nanoparticles with hexagonal structure were obtained by annealing (NH{sub 4}){sub x}WO{sub 3-y} at 500 °C in air. WO{sub 3} nanorods were prepared by a hydrothermal method using sodium tungstate Na{sub 2}WO{sub 4}, HCl, (COOH){sub 2} and NaSO{sub 4} precursors at 200 °C. The formation, morphology, structure and composition of the as-prepared nanoparticles and nanorods were studied by powder X-ray diffraction (XRD), transmission electron microscopy (TEM), and scanning electron microscopy combined with energy-dispersive X-ray spectroscopy (SEM-EDX). The photocatalytic activity of the h-WO{sub 3} nanoparticles and nanorods was studied by decomposing methyl orange in aqueous solution under UV light irradiation.

  5. Electrosprayed Metal Oxide Semiconductor Films for Sensitive and Selective Detection of Hydrogen Sulfide

    Directory of Open Access Journals (Sweden)

    Maryam Siadat

    2009-11-01

    Full Text Available Semiconductor metal oxide films of copper-doped tin oxide (Cu-SnO2, tungsten oxide (WO3 and indium oxide (In2O3 were deposited on a platinum coated alumina substrate employing the electrostatic spray deposition technique (ESD. The morphology studied with scanning electron microscopy (SEM and atomic force microscopy (AFM shows porous homogeneous films comprising uniformly distributed aggregates of nano particles. The X-ray diffraction technique (XRD proves the formation of crystalline phases with no impurities. Besides, the Raman cartographies provided information about the structural homogeneity. Some of the films are highly sensitive to low concentrations of H2S (10 ppm at low operating temperatures (100 and 200 °C and the best response in terms of Rair/Rgas is given by Cu-SnO2 films (2500 followed by WO3 (1200 and In2O3 (75. Moreover, all the films exhibit no cross-sensitivity to other reducing (SO2 or oxidizing (NO2 gases.

  6. Correlation between excited d-orbital electron lifetime in polaron dynamics and coloration of WO3 upon ultraviolet exposure

    Science.gov (United States)

    Lee, Young-Ahn; Han, Seung-Ik; Rhee, Hanju; Seo, Hyungtak

    2018-05-01

    Polarons have been suggested to explain the mechanism of the coloration of WO3 induced by UV light. However, despite the many experimental results that support small polarons as a key mechanism, direct observation of the carrier dynamics of polarons have yet to be reported. Here, we investigate the correlation between the electronic structure and the coloration of WO3 upon exposure to UV light in 5% H2/N2 gas and, more importantly, reveal photon-induced excited d-electron generation/relaxation via the W5+ oxidation state. The WO3 is fabricated by radio-frequency magnetron sputtering. X-ray diffraction patterns show that prepared WO3 is amorphous. Optical bandgap of 3.1 eV is measured by UV-vis before and after UV light. The results of Fourier transform infrared and Raman exhibit pristine WO3 is formed with surface H2O. The colored WO3 shows reduced state of W5+ state (34.3 eV) by using X-ray photoelectron spectroscopy. The valence band maximum of WO3 after UV light in H2 is shifted from mid gap to shallow donor by using ultraviolet photoelectron spectroscopy. During the exploration of the carrier dynamics, pump (700 nm)-probe (1000 nm) spectroscopy at the femtosecond scale was used. The results indicated that electron-phonon relaxation of UV-irradiated WO3, which is the origin of the polaron-induced local surface plasmonic effect, is dominant, resulting in slow decay (within a few picoseconds); in contrast, pristine WO3 shows fast decay (less than a picosecond). Accordingly, the long photoinduced carrier relaxation is ascribed to the prolonged hot-carrier lifetime in reduced oxides resulting in a greater number of free d-electrons and, therefore, more interactions with the W5+ sub-gap states.

  7. Influences of Temperature on the Conversion of Ammonium Tungstate Pentahydrate to Tungsten Oxide Particles with Controllable Sizes, Crystallinities, and Physical Properties

    Directory of Open Access Journals (Sweden)

    Asep Bayu Dani Nandiyanto

    2016-08-01

    Full Text Available The purpose of this study was to investigate influences of temperature on the conversion of ammonium tungstate pentahydrate (ATP powder to tungsten trioxide (WO3 particles with controllable sizes, crystallinities, and physicochemical properties. In this study, we used a simple thermal decomposition method. In the experimental procedure, we explored the effect of temperature on the physicochemical properties of ATP by testing various heating temperatures (from 100 to 900 °C. The heated ATP samples were then characterized by a physical observation (i.e. color and various analysis methods (i.e. a thermal gravimetric and differential thermal analysis, infrared spectroscopy, an X-ray diffraction, and a scanning electron microscope. Experimental results showed that increases in temperature had an impact to the decreases in particle size, the change in material crystallinity, and the change in physical properties (e.g. change of color from white, orange, to yellowish green. The relationships between the reaction temperatures and the physicochemical properties of the ATP were also investigated in detail along with the theoretical consideration and the proposal of the WO3 particle formation mechanism. In simplification, the phenomena can be described into three zones of temperatures. (1 Below 250 °C (release of water molecules and some ammonium ions.; (2 At 250-400 °C (release of water molecules and ammonium ions, restructurization of tungsten and oxygen elements, and formation of amorphous tungsten trioxide. (3 At higher than 400 °C (crystallization of tungsten trioxide. Since ATP possessed reactivity on temperature, its physicochemical properties changing could be observed easily, and the experimental procedure could be done easily. The present study will benefit not only for “chemistry and material science” but also potentially to be used as a model material for explaining the thermal behavior of material to undergraduate students (suitable

  8. Electrochromism in surface modified crystalline WO3 thin films grown by reactive DC magnetron sputtering

    Science.gov (United States)

    Karuppasamy, A.

    2013-10-01

    In the present work, tungsten oxide thin films were deposited at various oxygen chamber pressures (1.0-5.0 × 10-3 mbar) by maintaining the sputtering power density and argon pressure constant at 3.0 W/cm2 and 1.2 × 10-2 mbar, respectively. The role of surface morphology and porosity on the electrochromic properties of crystalline tungsten oxide thin films has been investigated. XRD and Raman studies reveal that all the samples post annealed at 450 ̊C in air for 3.0 h settle in monoclinic crystal system of tungsten oxide (W18O49). Though the phase of material is indifferent to oxygen pressure variations (PO2), morphology and film density shows a striking dependence on PO2. A systematic study on plasma (OES), morphology, optical and electrochromic properties of crystalline tungsten oxide reveal that the films deposited at PO2 of 2.0 × 10-3 mbar exhibit better coloration efficiency (58 cm2/C), electron/ion capacity (Qc: -25 mC/cm2), and reversibility (92%). This is attributed to the enhanced surface properties like high density of pores and fine particulates (100 nm) and to lesser bulk density of the film (ρ/ρo = 0.84) which facilitates the process of intercalation/de-intercalation of protons and electrons. These results show good promise toward stable and efficient crystalline tungsten oxide based electrochromic device applications.

  9. Tuning the pure monoclinic phase of WO3 and WO3-Ag nanostructures for non-enzymatic glucose sensing application with theoretical insight from electronic structure simulations

    Science.gov (United States)

    Ponnusamy, Rajeswari; Gangan, Abhijeet; Chakraborty, Brahmananda; Sekhar Rout, Chandra

    2018-01-01

    Here, we report the controlled hydrothermal synthesis and tuning of the pure monoclinic phase of WO3 and WO3-Ag nanostructures. Comparative electrochemical nonenzymatic glucose sensing properties of WO3 and WO3-Ag were investigated by cyclic voltammetry and chronoamperometric tests. We observed enhanced glucose sensing performance of WO3-Ag porous spheres as compared to bare WO3 nanoslabs. The sensitivity of the pure WO3 nanoslabs is 11.1 μA μM-1 cm-2 whereas WO3-Ag porous spheres exhibit sensitivity of 23.3 μA μM-1 cm-2. The WO3-Ag porous spheres exhibited a good linear range (5-375 μM) with excellent anti-interference property. Our experimental observations are qualitatively supported by density functional theory simulations through investigation of bonding and charge transfer mechanism of glucose on WO3 and Ag doped WO3. As the binding energy of glucose is more on the Ag doped WO3 (100) surface compared to the bare WO3 (100) surface and the Ag doped WO3 (100) surface becomes more conducting due to enhancement of density of states near the Fermi level, we can infer that Ag doped WO3 exhibits a better charge transfer media compared to bare WO3 resulting in enhanced glucose sensitivity in consistency with our experimental data.

  10. Polaron interaction energies in reduced tungsten trioxide

    International Nuclear Information System (INIS)

    Iguchi, E.; Salje, E.; Tilley, R.J.D.

    1981-01-01

    Consideration of the properties of reduced tungsten trioxide suggest that the mobile charge carriers are polarons. As it is uncertain how the presence of polarons will influence the microstructures of the crystallographic shear (CS) planes present in reduced tungsten trioxide we have calculated both the polaron-CS plane and polaron-polaron interaction energy for a variety of circumstances. Three CS plane geometries were considered, (102), (103), and (001) CS plane arrays, and the nominal compositions of the crystals ranged from WO 2 70 to WO 3 0 . The polarons were assumed to have radii from 0.6 to 1.0 nm and the polaron-CS plane electrostatic interaction was assumed to be screened. The results suggest that for the most part the total interaction energy is small and is unlikely to be of major importance in controlling the microstructures found in CS planes. However, at very high polaron densities the interaction energy could be appreciable and may have some influence on the existence range of CS phases

  11. Promotion effect of Pt on a SnO2-WO3 material for NOx sensing

    Science.gov (United States)

    Wang, Chen-Yang; Hong, Zih-Siou; Wu, Ren-Jang

    2015-05-01

    Metal-oxide nanocomposites were prepared over screen-printed gold electrodes to be used as room-temperature NOx (nitric-oxide (NO) and nitrogen dioxide (NO2)) sensors. Various weight ratios of SnO2-WO3 and Pt loadings were used for NO sensing. The sensing materials were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM) and BET surface analysis. The NO-sensing results indicated that SnO2-WO3 (1:2) was more effective than other materials were. The sensor response (S=resistance of N2/resistance of NO=RN2/RNO) for detecting 1000 ppm of NO at room temperature was 2.6. The response time (T90) and recovery time (TR90) was 40 s and 86 s, respectively. By further loading with 0.5% Pt, the sensor response increased to 3.3. The response and recovery times of 0.5% Pt/SnO2-WO3 (1:2) were 40 s and 206 s, respectively. The linearity of the sensor response for a NO concentration range of 10-1000 ppm was 0.9729. A mechanism involving Pt promotion of the SnO2-WO3 heterojunction was proposed for NO adsorption, surface reaction, and adsorbed NO2 desorption.

  12. Effects of tungsten and titanium oxide nanoparticles on the diazotrophic growth and metals acquisition by Azotobacter vinelandii under molybdenum limiting condition.

    Science.gov (United States)

    Allard, Patrick; Darnajoux, Romain; Phalyvong, Karine; Bellenger, Jean-Philippe

    2013-02-19

    The acquisition of essential metals, such as the metal cofactors (molybdenum (Mo) and iron (Fe)) of the nitrogenase, the enzyme responsible for the reduction of dinitrogen (N(2)) to ammonium, is critical to N(2) fixing bacteria in soil. The release of metal nanoparticles (MNPs) to the environment could be detrimental to N(2) fixing bacteria by introducing a new source of toxic metals and by interfering with the acquisition of essential metals such as Mo. Since Mo has been reported to limit nonsymbiotic N(2) fixation in many ecosystems from tropical to cold temperate, this question is particularly acute in the context of Mo limitation. Using a combination of microbiology and analytical chemistry techniques, we have evaluated the effect of titanium (Ti) and tungsten (W) oxide nanoparticles on the diazotrophic growth and metals acquisition in pure culture of the ubiquitous N(2) fixing bacterium Azotobacter vinelandii under Mo replete and Mo limiting conditions. We report that under our conditions (≤10 mg·L(-1)) TiO(2) NPs have no effects on the diazotrophic growth of A. vinelandii while WO(3) NPs are highly detrimental to the growth especially under Mo limiting conditions. Our results show that the toxicity of WO(3) NPs to A. vinelandii is due to an interference with the catechol-metalophores assisted uptake of Mo.

  13. Renewable energy production by photoelectrochemical oxidation of organic wastes using WO{sub 3} photoanodes

    Energy Technology Data Exchange (ETDEWEB)

    Raptis, Dimitrios [Department of Chemical Engineering, University of Patras, 26500 Patras (Greece); Dracopoulos, Vassilios [FORTH/ICE-HT, P.O. Box 1414, 26504 Patras (Greece); Lianos, Panagiotis, E-mail: lianos@upatras.gr [Department of Chemical Engineering, University of Patras, 26500 Patras (Greece)

    2017-07-05

    Highlights: • Efficient nanoparticulate WO{sub 3} photoanodes. • Photoelectrocatalytic hydrogen production by consumption of organic wastes. • Photoelectrocatalytic oxidation of ethanol, glycerol or sorbitol. • Recording of hydrogen production and calculation of efficiencies. - Abstract: The present work has studied renewable hydrogen production by photoelectrocatalytic degradation of model organic substances representing biomass derived organic wastes. Its purpose was to show that renewable energy can be produced by consuming wastes. The study has been carried out by employing nanoparticulate WO{sub 3} photoanodes in the presence of ethanol, glycerol or sorbitol, i.e. three substances which are among typical biomass products. In these substances, the molecular weight and the number of hydroxyl groups increases from ethanol to sorbitol. The photocurrent produced by the cell was the highest in the presence of ethanol, smaller in the case of glycerol and further decreased in the presence of sorbitol. The photocurrent was roughly the double of that produced in the absence of an organic additive thus demonstrating current doubling phenomena. Hydrogen was produced only under illumination and was monitored at two forward bias, 0.8 and 1.6 V vs Ag/AgCl. Hydrogen production rates followed the same order as the photocurrent thus indicating that hydrogen production by reduction of protons mainly depends on the current flowing through the external circuit connecting photoanode with cathode. The maximum solar-to-hydrogen efficiency reached by the present system was 2.35%.

  14. Subsolidus phase relations of the SrO–WO3–CuO system at 800 °C in air

    DEFF Research Database (Denmark)

    Grivel, Jean-Claude; Norby, Poul

    2012-01-01

    The subsolidus phase relations of the SrO–WO3–CuO system were investigated in air. The samples were equilibrated at 800 °C. Under these conditions, eight binary oxides are stable. The pseudo-ternary section contains two ternary oxide phases: the previously described Sr2CuWO6 phase as well as a new...

  15. A novel composite electrode based on tungsten oxide nanoparticles and carbon nanotubes for the electrochemical determination of paracetamol

    Energy Technology Data Exchange (ETDEWEB)

    Baytak, Aysegul Kutluay; Duzmen, Sehriban; Teker, Tugce; Aslanoglu, Mehmet, E-mail: maslanoglu@harran.edu.tr

    2015-12-01

    An electrochemical sensor was prepared by the modification of a glassy carbon electrode (GCE) with a composite of nanoparticles of tungsten oxide (WO{sub 3}) and carbon nanotubes (CNTs) for the quantification of paracetamol (PR). Energy dispersive X-ray analysis (EDX) and scanning electron microscopy (SEM) were performed for the characterization of the nanocomposite layer. Compared with a bare GCE and a GCE modified with CNTs, the proposed electrode (WO{sub 3}NPs/CNTs/GCE) exhibited a well-defined redox couple for PR and a marked enhancement of the current response. The experimental results also showed that ascorbic acid (AA) did not interfere with the selective determination of PR. The proposed electrode was used for the determination of PR in 0.1 M phosphate buffer solution (PBS) at pH 7.0 using square wave voltammetry (SWV). The peak current increased linearly with the concentration of PR in the range of 1.0 × 10{sup −9}–2.0 × 10{sup −7} M. The detection limit (LOD) was 5.54 × 10{sup −11} M (based on 3 S{sub b}/m). The proposed voltammetric sensor provided long-time stability, improved voltammetric behavior and good reproducibility for PR. The selective, accurate and precise determination of PR makes the proposed electrode of great interest for monitoring its therapeutic use. - Highlights: • A voltammetric nanosensor was prepared using nanoparticles of WO{sub 3} and CNTs. • A selective quantification of paracetamol was carried out in the presence of AA. • A linear plot was obtained for current responses versus concentrations over the range from 1.0 × 10{sup −9} to 2.0 × 10{sup −7} M. • A detection limit of 554 pM was obtained for paracetamol using the proposed nanosensor. • An accurate quantification makes the proposed nanosensor of great interest for public health.

  16. Vapor-transport of tungsten and its geologic application

    Energy Technology Data Exchange (ETDEWEB)

    Shibue, Y [Hyogo Univ. of Teacher Education, Hyogo (Japan)

    1988-11-10

    The volatility of tungsten in a hydrous system at elevated temperatures and pressures was examined, and a tentative model for the enrichment of tungsten in hydrothermal solutions for the deposits related to granitic activities was proposed. To produce vapor-saturated solution, 17 or 15ml of 20wt% NaCl solution was introduced into an autoclave. Ca(OH){sub 2} for tungsten and H{sub 2}WO{sub 4} for base metals were used as vapor-captures, and run products were identified by X-ray powder diffractometry. The results suggested that the ratio of tungsten to base metals was higher in a vapor phase than in a liquid phase, and more enrichment of tungsten in the vapor phase occurred at higher temperature and pressure under the coexistence of the vapor and liquid phase. The tentative model emphasizing the vapor-transport of tungsten could explain the presence of tungsten deposits without large mineralization of base metals. Geological schematic model for the generation of the hydrothermal solution enriched in tungsten compared with base metals was illustrated based on above mentioned results. 21 refs., 3 figs.

  17. Effect of negative bias on the composition and structure of the tungsten oxide thin films deposited by magnetron sputtering

    Science.gov (United States)

    Wang, Meihan; Lei, Hao; Wen, Jiaxing; Long, Haibo; Sawada, Yutaka; Hoshi, Yoichi; Uchida, Takayuki; Hou, Zhaoxia

    2015-12-01

    Tungsten oxide thin films were deposited at room temperature under different negative bias voltages (Vb, 0 to -500 V) by DC reactive magnetron sputtering, and then the as-deposited films were annealed at 500 °C in air atmosphere. The crystal structure, surface morphology, chemical composition and transmittance of the tungsten oxide thin films were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS) and UV-vis spectrophotometer. The XRD analysis reveals that the tungsten oxide films deposited at different negative bias voltages present a partly crystallized amorphous structure. All the films transfer from amorphous to crystalline (monoclinic + hexagonal) after annealing 3 h at 500 °C. Furthermore, the crystallized tungsten oxide films show different preferred orientation. The morphology of the tungsten oxide films deposited at different negative bias voltages is consisted of fine nanoscale grains. The grains grow up and conjunct with each other after annealing. The tungsten oxide films deposited at higher negative bias voltages after annealing show non-uniform special morphology. Substoichiometric tungsten oxide films were formed as evidenced by XPS spectra of W4f and O1s. As a result, semi-transparent films were obtained in the visible range for all films deposited at different negative bias voltages.

  18. Enrichment of W2B5 from WO3 and B2O3 by Double SHS Method

    Directory of Open Access Journals (Sweden)

    Bora DERIN

    2018-02-01

    Full Text Available A second self-propagating high-temperature synthesis (SHS was carried out to enrich the W2B5 content in the SHS product containing a mixture of various tungsten boride compounds. In the experiment, the process called Double-SHS (D-SHS was conducted in two steps. In the first SHS reaction, an initial molar composition ratio of WO3:B2O3:Mg mixture was selected as 1:3:8. The product was then hot-leached with hydrochloric acid to eliminate MgO and Mg3B2O6 phases. The leached product, consisting of 72.6 wt.% W2B5, 16.1 wt.% WB, 8.4 wt.% W2B, and 2.9 wt.% W, was again reacted with the Mg and B2O3 mixture by second SHS. After another acid leaching step, W2B5 content in the D-SHS product was found to be 98.2 wt.%. The study showed that D-SHS is an effective method for boron enrichment in the tungsten compounds.DOI: http://dx.doi.org/10.5755/j01.ms.24.1.17834

  19. Quantum dots as mediators in gas sensing: A case study of CdS sensitized WO{sub 3} sensing composites

    Energy Technology Data Exchange (ETDEWEB)

    Concina, Isabella, E-mail: concina@sensor.ing.unibs.it [CNR-INO SENSOR Laboratory, via Branze, 45, 25131 Brescia (Italy); SENSOR, Department of Information Engineering, Brescia University, via Valotti, 9, 25133 Brescia (Italy); Comini, Elisabetta [CNR-INO SENSOR Laboratory, via Branze, 45, 25131 Brescia (Italy); SENSOR, Department of Information Engineering, Brescia University, via Valotti, 9, 25133 Brescia (Italy); Kaciulis, Saulius [CNR-ISMN, Institute for the Study of Nanostructured Materials, Via dei Taurini, 19, 00185 Roma (Italy); Sberveglieri, Giorgio [CNR-INO SENSOR Laboratory, via Branze, 45, 25131 Brescia (Italy); SENSOR, Department of Information Engineering, Brescia University, via Valotti, 9, 25133 Brescia (Italy)

    2014-01-30

    In this study the proof of principle of the use of naked semiconductor directly generated on metal oxide surface as mediators in gas sensing is provided. Successive ionic layer absorption and reaction (SILAR) technique has been applied to sensitize a WO{sub 3} thin film with CdS quantum dots. Response to gases of bare WO{sub 3} is deeply modified: quantum dots dramatically increase the metal oxide conductance, otherwise rather poor, and modify the capability of detecting environmental pollutants, such as CO and NO{sub 2}. A modified sensing mechanism is proposed to rationalize the mediation exerted by the semiconducting active layer on the interaction between gaseous species and WO{sub 3} surface.

  20. Photoelectrocatalytic degradation of diazo dyes on nanostructured WO{sub 3} electrodes

    Energy Technology Data Exchange (ETDEWEB)

    Hepel, Maria [Department of Chemistry, State University of New York at Potsdam, Potsdam, NY 13676 (United States)]. E-mail: hepelmr@potsdam.edu; Hazelton, Sandra [Department of Chemistry, State University of New York at Potsdam, Potsdam, NY 13676 (United States)

    2005-09-05

    Photoelectrocatalytic degradation of Remazol Black B (RBB) dye in aqueous solutions was investigated. The degradation was carried out on a highly efficient n-WO{sub 3} photoelectrode, which was synthesized by electrochemical processing. Effects of various synthesis and post-treatment conditions were investigated using electrochemical techniques and AFM imaging. Photocurrent measurements have shown that Butler-Gartner equation is fulfilled for n-WO{sub 3} films, which allowed us to determine the flat-band potential (E {sub fb} = 0.35 V versus Ag/AgCl, for pH = 0). The WO{sub 3} film electrode was found to be a better photelectrocatalyst than TiO{sub 2} with similar AFM surface roughness. Kinetic measurements of photoelectrocatalytic RBB degradation have shown that a generalized Langmuir-Hinshelwood model applies to the system, leading to the overall rate constant k' = 1.1 x 10{sup -9} mol cm{sup -2} s{sup -1}, with RBB adsorption equilibrium constant K = 3.35 x 10{sup 4} mol{sup -1} L and Gibbs free energy of adsorption {delta}G deg. = -6.16 kcal/mol (-25.8 kJ/mol). In mechanistic considerations of possible lines of oxidative attack on RBB, we looked at electrolyte composition and properties of electronic structure of RBB, by utilizing quantum mechanical calculations of molecular orbitals. The ab initio SCF Hartree-Fock calculations of molecular orbitals were carried out to evaluate most vulnerable areas of RBB molecule for electrophilic and nucleophilic attacks, as well as for a direct charge transfer oxidation process. Several electronic properties were mapped onto the total electron density surface and analyzed to reveal initial reaction pathways for oxidative degradation of RBB.

  1. Granite-related Yangjiashan tungsten deposit, southern China

    Science.gov (United States)

    Xie, Guiqing; Mao, Jingwen; Li, Wei; Fu, Bin; Zhang, Zhiyuan

    2018-04-01

    The Yangjiashan scheelite-bearing deposit (38,663 metric tons of WO3 with an average ore grade of 0.70% WO3) is hosted in quartz veins in a biotite monzogranite intrusion and surrounding slate in the Xiangzhong Metallogenic Province of southern China. The monzogranite has a zircon SHRIMP U-Pb age of 406.6 ± 2.8 Ma (2σ, n = 20, MSWD = 1.4). Cassiterite coexisting with scheelite yields a weighted mean 206Pb/238U age of 409.8 ± 5.9 Ma (2σ, n = 30, MSWD = 0.20), and molybdenite intergrown with scheelite yields a weighted mean Re-Os age of 404.2 ± 3.2 Ma (2σ, n = 3, MSWD = 0.10). These results suggest that the Yangjiashan tungsten deposit is temporally related to the Devonian intrusion. The δD and calculated δ18OH2O values of quartz intergrown with scheelite range from - 87 to - 68‰, and - 1.2 to 3.4‰, respectively. Sulfides have a narrow range of δ34S values of - 2.9 to - 0.7‰ with an average value of - 1.6‰ (n = 16). The integration of geological, stable isotope, and geochronological data, combined with the quartz-muscovite greisen style of ore, supports a magmatic-hydrothermal origin for the tungsten mineralization. Compared to the more common tungsten skarn, quartz-wolframite vein, and porphyry tungsten deposits, as well as orogenic gold deposits worldwide, the Yangjiashan tungsten deposit is an unusual example of a granite-related, gold-poor, scheelite-bearing quartz vein type of deposit. The calcium needed for the formation of scheelite is derived from the sericitization of calcic plagioclase in the monzogranite and Ca-bearing psammitic country rocks, and the relatively high pH, reduced and Ca-rich mineralizing fluid may be the main reasons for the formation of scheelite rather than wolframite at Yangjiashan.

  2. Synthesis, characterization and photocatalytic activity of WO3/TiO2 for NO removal under UV and visible light irradiation

    International Nuclear Information System (INIS)

    Luévano-Hipólito, E.; Martínez-de la Cruz, A.; López-Cuellar, E.; Yu, Q.L.; Brouwers, H.J.H.

    2014-01-01

    Samples with different proportions WO 3 /TiO 2 were prepared by co-precipitation method followed by a heat treatment. The samples were characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), diffuse reflectance spectroscopy (DRS), and adsorption–desorption N 2 isotherms (BET). The photocatalytic properties of WO 3 /TiO 2 samples were evaluated in the photo-oxidation reaction of nitric oxide (NO) under UV and visible light irradiation. The highest photocatalytic activity was observed in the WO 3 /TiO 2 sample with a composition of 80% mole of TiO 2 . Among the different substrates used for supporting the photocatalyst, the best results were reached over concrete and glass when it was exposed to UV and visible light irradiation, respectively. In overall, the photocatalytic efficiency of the synthesized materials was higher under UV than visible light irradiation. - Highlights: • WO 3 /TiO 2 prepared in simple way show high photocatalytic activity for NO removal. • The concrete was the best substrate to the performance of WO 3 /TiO 2 with UV radiation. • The glass was the best substrate to the performance of WO 3 /TiO 2 with visible radiation

  3. Degradation of organic dyes using spray deposited nanocrystalline stratified WO3/TiO2 photoelectrodes under sunlight illumination

    Science.gov (United States)

    Hunge, Y. M.; Yadav, A. A.; Mahadik, M. A.; Bulakhe, R. N.; Shim, J. J.; Mathe, V. L.; Bhosale, C. H.

    2018-02-01

    The need to utilize TiO2 based metal oxide hetero nanostructures for the degradation of environmental pollutants like Rhodamine B and reactive red 152 from the wastewater using stratified WO3/TiO2 catalyst under sunlight illumination. WO3, TiO2 and stratified WO3/TiO2 catalysts were prepared by a spray pyrolysis method. It was found that the stratified WO3/TiO2 heterostructure has high crystallinity, no mixed phase formation occurs, strong optical absorption in the visible region of the solar spectrum, and large surface area. The photocatalytic activity was tested for degradation of Rhodamine B (Rh B) and reactive red 152 in an aqueous medium. TiO2 layer in stratified WO3/TiO2 catalyst helps to extend its absorption spectrum in the solar light region. Rh B and Reactive red 152is eliminated up to 98 and 94% within the 30 and 40 min respectively at optimum experimental condition by stratified WO3/TiO2. Moreover, stratified WO3/TiO2 photoelectrode has good stability and reusability than individual TiO2 and WO3 thin film in the degradation of Rh B and reactive red 152. The photoelectrocatalytic experimental results indicate that stratified WO3/TiO2 photoelectrode is a promising material for dye removal.

  4. Electrochemical catalytic activity of tungsten trioxide- modified graphite felt toward VO2+/VO2+ redox reaction

    International Nuclear Information System (INIS)

    Shen, Yang; Xu, Hongfeng; Xu, Pengcheng; Wu, Xiaoxin; Dong, Yiming; Lu, Lu

    2014-01-01

    A novel graphite felt electrode modified with tungsten trioxide (WO 3 ) was developed to improve the electrochemical performance of graphite felt toward the VO 2 + /VO 2+ redox pair. WO 3 was prepared using a hydrothermal method, and the morphology of WO 3 structures was investigated by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The electrochemical property of WO 3 -modified graphite felt toward VO 2 + /VO 2+ was carefully characterized using cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) measurements. The hydrogen-vanadium redox flow battery (H-VRFB) test indicates that single cells using 1.1 mg cm −2 WO 3 -modified graphite felt exhibited excellent performance at 70 mA cm −2 , and the corresponding coulombic, voltage, and energy efficiencies were 99.1%, 88.66% and 87.86%, respectively

  5. Structural and spectroscopic characteristics of Eu3+-doped tungsten phosphate glasses

    Science.gov (United States)

    Dousti, M. Reza; Poirier, Gael Yves; de Camargo, Andrea Simone Stucchi

    2015-07-01

    Tungsten based phosphate glasses are interesting non-crystalline materials, commonly known for photochromic and electrochromic effects, but also promising hosts for luminescent trivalent rare earth ions. Despite very few reports in the literature, association of the host´s functionalities with the efficient emissions of the dopant ions in the visible and near-infrared spectra could lead to novel applications. This work reports the preparation and characterization of glasses with the new composition 4(Sb2O3)96-x(50WO3 50NaPO3)xEu2O3 where x = 0, 0.1, 0.25, 0.5 and 1.0 mol%, obtained by the melt quenching technique. The glasses present large density (∼4.6 g cm-3), high glass transition temperature (∼480 °C) and high thermal stability against crystallization. Upon excitation at 464 nm, the characteristic emissions of Eu3+ ions in the red spectral region are observed with high intensity. The Judd-Ofelt intensity parameters Ω2 = 6.86 × 10-20, Ω4 = 3.22 × 10-20 and Ω6 = 8.2 × 10-20 cm2 were calculated from the emission spectra and found to be higher than those reported for other phosphate glass compositions. An average excited state lifetime value of 1.2 ms, was determined by fitting the luminescence decay curves with single exponential functions and it is comparable or higher than those of other oxide glasses.

  6. Defect engineering of two-dimensional WO{sub 3} nanosheets for enhanced electrochromism and photoeletrochemical performance

    Energy Technology Data Exchange (ETDEWEB)

    Zhou, Xiaofang; Zheng, Xiaoli; Yan, Bo; Xu, Tao; Xu, Qun, E-mail: qunxu@zzu.edu.cn

    2017-04-01

    Highlights: • We establish a facile strategy by solvothermal reaction and hydrogenation to synthesize 2D WO{sub 3} ultrathin nanosheets with abundant oxygen vacancies. • We find that the hydrogenated WO{sub 3} ultrathin nanosheets exhibit outstanding electrochromism properties. • Moreover, the hydrogenated WO{sub 3} nanosheets also exhibit remarkable photocatalytic performance. • The outstanding electrochromism and photoelectrochemical performances are mainly due to increased oxygen vacancies and narrowed band gap. - Abstract: The capability of introduction of oxygen vacancies in a controlled way has emerged as the heart of modern transition metal oxide semiconductor chemistry. As chemical defects, the oxygen vacancies have been proposed as electron donors, which are prone to increase carrier density and promote charge carrier separation. Herein, we have successfully prepared 2D WO{sub 3} ultrathin nanosheets with abundant surface oxygen vacancies by a combination of facile solvothermal reaction and hydrogenation method. The resultant hydrogenated WO{sub 3} ultrathin nanosheets exhibit remarkable electrochromism and photocatalytic performances compared with the non-hydrogenated samples, mainly due to their increased oxygen vacancies, narrowed band gap coupled with fast charge transfer and enhanced adsorption of visible light.

  7. Crack resistance of tungsten strengthened by dispersed refractory oxides

    International Nuclear Information System (INIS)

    Babak, A.V.; Uskov, E.I.

    1984-01-01

    Investigation results are presented for crack resistance of commercial tungsten, obtained during specimen testing at temperatures of 20 deg C to Tsub(cr) (upper boundary of temperature range of ductile-brittle transition). Comparison of s-n diagrams and temperature dependences of crack resistance are conducted for commercial tungsten and tungsten strengthened by refractory oxides. It is shown that dispersion hardening increases crack resistance in the temperature range of 20 to 2000 deg C but the upper boundary of ductile-brittle shifts to the side of higher temperatures

  8. Effect of Annealing on Tungsten Oxide Thin Films for Acetone Gas ...

    Indian Academy of Sciences (India)

    11

    Abstract: The gas sensing properties and topology of tungsten oxide thin films ..... Figure 3: Atomic force microscopy images of sensing film for (a) as-deposited (a) .... the surface, it forms compounds with the oxygen ions species present on the ...

  9. GENERATION, TRANSPORT AND DEPOSITION OF TUNGSTEN-OXIDE AEROSOLS AT 1000 C IN FLOWING AIR-STEAM MIXTURES.

    Energy Technology Data Exchange (ETDEWEB)

    GREENE,G.A.; FINFROCK,C.C.

    2001-10-01

    Experiments were conducted to measure the rates of oxidation and vaporization of pure tungsten rods in flowing air, steam and air-steam mixtures in laminar flow. Also measured were the downstream transport of tungsten-oxide condensation aerosols and their region of deposition, including plateout in the superheated flow tube, rainout in the condenser and ambient discharge which was collected on an array of sub-micron aerosol filters. The nominal conditions of the tests, with the exception of the first two tests, were tungsten temperatures of 1000 C, gas mixture temperatures of 200 C and wall temperatures of 150 C to 200 C. It was observed that the tungsten oxidation rates were greatest in all air and least in all steam, generally decreasing non-linearly with increasing steam mole fraction. The tungsten oxidation rates in all air were more than five times greater than the tungsten oxidation rates in all steam. The tungsten vaporization rate was zero in all air and increased with increasing steam mole fraction. The vaporization rate became maximum at a steam mole fraction of 0.85 and decreased thereafter as the steam mole fraction was increased to unity. The tungsten-oxide was transported downstream as condensation aerosols, initially flowing upwards from the tungsten rod through an 18-inch long, one-inch diameter quartz tube, around a 3.5-inch radius, 90{sup o} bend and laterally through a 24-inch horizontal run. The entire length of the quartz glass flow path was heated by electrical resistance clamshell heaters whose temperatures were individually controlled and measured. The tungsten-oxide plateout in the quartz tube was collected, nearly all of which was deposited at the end of the heated zone near the entrance to the condenser which was cold. The tungsten-oxide which rained out in the condenser as the steam condensed was collected with the condensate and weighed after being dried. The aerosol smoke which escaped the condenser was collected on the sub

  10. Electrical properties of tungsten trioxide films

    International Nuclear Information System (INIS)

    Xu, Z.; Vetelino, J.F.; Lec, R.; Parker, D.C.

    1990-01-01

    Selectively doped semiconducting metal oxide (SMO) films have been shown to have applications as the sensing element in gas microsensors. Critical to the design and operation of these sensors is the SMO film. In the present work, the electrical properties of both intrinsic and extrinsic (doped with gold) tungsten trioxide (WO 3 ) films, which selectively sorb hydrogen sulfide (H 2 S), are investigated. Hall effect measurements are performed as a function of film thickness, temperature, gold-doping concentration, and H 2 S gas concentration. The conductivity was found to be n type and strongly dependent on temperature, gold doping concentration, and H 2 S gas concentration and less dependent on film thickness. The mobility was relatively high while the intrinsic carrier concentration was low when compared to typical semiconductor materials. The conductivity was shown to exhibit anomalous behavior at certain temperatures and H 2 S gas concentrations

  11. Structure and properties of TeO2-WO3 system glasses

    International Nuclear Information System (INIS)

    Kolobkov, V.P.; Ovcharenko, N.V.; Morozova, I.N.; Chebotarev, S.A.; Chikovskij, A.N.; Arkatova, T.G.

    1987-01-01

    Study of TeO 2 -WO 3 system is of interest for production of high-refractive-glasses with comparatively low crystallizability. Results of investigating some properties and structural features of this system glasses are presented. Composition and properties of studied glasses are presented. The properties were studied using the following techniques: the density was measured by hydrostatic weighing in toluene; thermal expansion coefficient was measured in quartz dilatometer DKV-5A; dilatometric temperature of glass softening (T g ) was defined as an intersection point of linear and curved parts of the plot of thermal expansion coefficient; refractive index (RI) - by immersion method; dielectric properties are measured. Consideration of vibronic spectra permits to conclude that in tungsten-tellurium glasses rare earth activator ions are arranged near tellurite and tungstate groupings proportional to glass-forming component content

  12. Synthesis, Characterization, and Gas Sensing Applications of WO3 Nanobricks

    Science.gov (United States)

    Xiao, Jingkun; Song, Chengwen; Dong, Wei; Li, Chen; Yin, Yanyan; Zhang, Xiaoni; Song, Mingyan

    2015-08-01

    WO3 nanobricks are fabricated by a simple hydrothermal method. Morphology and structure of the WO3 nanobricks are characterized by scanning electron microscopy and x-ray diffraction. Gas sensing properties of the as-prepared WO3 sensor are systematically investigated by a static gas sensing system. The results show that the WO3 nanobricks with defect corners demonstrate good crystallinity, and the mean edge length and wall thickness are 1-1.5 and 400 nm, respectively. The WO3 sensor achieves its maximum sensitivity to 100 ppm ethanol at the optimal operating temperature of 300 °C. Ultra-fast response time (2-3 s) and fast recovery time (4-11 s) of the WO3 sensor toward 100 ppm ethanol are also observed at this optimal operating temperature. Moreover, the WO3 sensor exhibits high selectivity to other gases such as methanol, benzene, hexane, and dichloromethane, indicating its excellent potential application as a gas sensor for ethanol detection.

  13. A mesoporous WO3−X/graphene composite as a high-performance Li-ion battery anode

    International Nuclear Information System (INIS)

    Liu, Fei; Kim, Jong Gu; Lee, Chul Wee; Im, Ji Sun

    2014-01-01

    Graphical abstract: The highly flexible and conductive graphene layer can enhance electron transfer, protect metal oxides against disintegration and aggregation and buffer the strain induced by volume expansion during cycles. The mesoporous surface layer provides an open network for Li+ diffusion. - Highlights: • Novel cocktail effects of 2D mesoporous WO 3−X /graphene for lithium ion battery. • New approach for lithium ion battery by easy and unique synthesis method. • Mechanism study with proper data for understanding a reaction on anode surface. - Abstract: A novel mesoporous WO 3−X /graphene composite was developed. This material allowed rapid electron and Li + ion diffusion when used as a Li-ion battery (LIB) anode material. Remarkably, the graphene support protected WO 3−X from changing volume during the electrochemical cycling process; this process generally induces capacity loss. The current work describes a high-performance anode material for LIB that has highly dense WO 3−X , as well as high capacity, rate capability and stability

  14. On-chip microplasma reactors using carbon nanofibres and tungsten oxide nanowires as electrodes

    NARCIS (Netherlands)

    Agiral, A.; Groenland, A.W.; Chinthaginjala, J.K.; Kumar Chinthaginjala, J.; Seshan, Kulathuiyer; Lefferts, Leonardus; Gardeniers, Johannes G.E.

    2008-01-01

    Carbon nanofibres (CNFs) and tungsten oxide (W18O49) nanowires have been incorporated into a continuous flow type microplasma reactor to increase the reactivity and efficiency of the barrier discharge at atmospheric pressure. CNFs and tungsten oxide nanowires were characterized by high-resolution

  15. Solid-state pH ultramicrosensor based on a tungstic oxide film fabricated on a tungsten nanoelectrode and its application to the study of endothelial cells

    International Nuclear Information System (INIS)

    Yamamoto, Katsunobu; Shi Guoyue; Zhou Tianshu; Xu Fan; Zhu Min; Liu Min; Kato, Takeshi; Jin Jiye; Jin Litong

    2003-01-01

    In this paper, preparation of a novel pH ultramicrosensor and its physiological application has been discussed. A tungsten nanoelectrode was produced by an etching method in 0.1 mol/l NaOH solution at the potential of +0.4 V (versus Ag/AgCl reference electrode) for about 100 s and the diameters ranged from 500 to 800 nm. The pH ultramicrosensor was fabricated by producing WO 3 at W nanoelectrode surface by electrooxidation in 2.0 mol/l H 2 SO 4 solution between 1.0 and 2.0 V. At last, Nafion was coated on the surface of WO 3 to protect the pH ultramicrosensor. The W/WO 3 pH ultramicrosensor exhibited a good pH linear region from 2.0 to 12.0 with a super-Nernstian slope of -53.5 ± 0.5 mV/pH unit. Response times ranged from 3 s at about pH 6.0-7.0 up to 15 s at high pH. An interference of various ions to the pH measurement was also studied in this paper. We also studied the lifetime, stability and reproducibility of the W/WO 3 pH ultramicrosensor. In order to testing the performance of W/WO 3 ultramicrosensor, we applied it to measure the extracellular pH values and a pH variation was also given about the normal, damaged and recovery endothelial cells

  16. High-temperature oxidation of tungsten covered by layer of glass-enamel melt

    International Nuclear Information System (INIS)

    Vasnetsova, V.B.; Shardakov, N.T.; Kudyakov, V.Ya.; Deryabin, V.A.

    1997-01-01

    Corrosion losses of tungsten covered by the layer of glass-enamel melt were determined at 800, 850, 900, 950 deg C. It is shown that the rate of high-temperature oxidation of tungsten decreases after application of glass-enamel melt on its surface. This is probably conditioned by reduction of area of metal interaction with oxidizing atmosphere

  17. Comparison of modification strategies towards enhanced charge carrier separation and photocatalytic degradation activity of metal oxide semiconductors (TiO{sub 2}, WO{sub 3} and ZnO)

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, S. Girish [Department of Physics, Indian Institute of Science, Bengaluru, 560012 Karnataka (India); Department of Chemistry, School of Engineering and Technology, CMR University, Bengaluru, 562149, Karnataka (India); Rao, K.S.R. Koteswara, E-mail: raoksrk@gmail.com [Department of Physics, Indian Institute of Science, Bengaluru, 560012 Karnataka (India)

    2017-01-01

    Graphical abstract: Semiconductor metal oxides: Modifications, charge carrier dynamics and photocatalysis. - Highlights: • TiO{sub 2}, WO{sub 3} and ZnO based photocatalysis is reviewed. • Advances to improve the efficiency are emphasized. • Differences and similarities in the modifications are highlighted. • Charge carrier dynamics for each strategy are discussed. - Abstract: Metal oxide semiconductors (TiO{sub 2}, WO{sub 3} and ZnO) finds unparalleled opportunity in wastewater purification under UV/visible light, largely encouraged by their divergent admirable features like stability, non-toxicity, ease of preparation, suitable band edge positions and facile generation of active oxygen species in the aqueous medium. However, the perennial failings of these photocatalysts emanates from the stumbling blocks like rapid charge carrier recombination and meager visible light response. In this review, tailoring the surface-bulk electronic structure through the calibrated and veritable approaches such as impurity doping, deposition with noble metals, sensitizing with other compounds (dyes, polymers, inorganic complexes and simple chelating ligands), hydrogenation process (annealing under hydrogen atmosphere), electronic integration with other semiconductors, modifying with carbon nanostructures, designing with exposed facets and tailoring with hierarchical morphologies to overcome their critical drawbacks are summarized. Taking into account the materials intrinsic properties, the pros and cons together with similarities and striking differences for each strategy in specific to TiO{sub 2}, WO{sub 3} & ZnO are highlighted. These subtlety enunciates the primacy for improving the structure-electronic properties of metal oxides and credence to its fore in the practical applications. Future research must focus on comparing the performances of ZnO, TiO{sub 2} and WO{sub 3} in parallel to get insight into their photocatalytic behaviors. Such comparisons not only reveal

  18. Oxidative desulfurization of benzothiophene and thiophene with WOx/ZrO2 catalysts: Effect of calcination temperature of catalysts

    International Nuclear Information System (INIS)

    Hasan, Zubair; Jeon, Jaewoo; Jhung, Sung Hwa

    2012-01-01

    Highlights: ► Oxidative desulfurization was studied with WO x /ZrO 2 calcined at different temp. ► The importance of the phases of zirconia and tungsten oxide was suggested. ► The catalyst was analyzed thoroughly with Raman and XRD techniques. ► The importance of electron density on S was confirmed with the kinetics of oxidation. - Abstract: Oxidative desulfurization (ODS) of model fuel containing benzothiophene (BT) or thiophene (Th) has been carried out with WO x /ZrO 2 catalyst, which was calcined at various temperatures. Based on the conversion of BT in the model fuel, it can be shown that the optimum calcination temperature of WO x /ZrO 2 catalyst is around 700 °C. The most active catalyst is composed of tetragonal zirconia (ZrO 2 ) with well dispersed polyoxotungstate species and it is necessary to minimize the contents of the crystalline WO 3 and monoclinic ZrO 2 for a high BT conversion. The oxidation rate was interpreted with the first-order kinetics, and it demonstrated the importance of electron density since the kinetic constant for BT was higher than that for Th even though the BT is larger than Th in size. A WO x /ZrO 2 catalyst, treated suitably, can be used as a reusable active catalyst in the ODS.

  19. Studies on the pressed yttrium oxide-tungsten matrix as a possible dispenser cathode material

    International Nuclear Information System (INIS)

    Yang, Fan; Wang, Jinshu; Liu, Wei; Liu, Xiang; Zhou, Meiling

    2015-01-01

    Yttrium oxide was chosen as the secondary emission substance based on calculation results through first principle theory method. A new kind of pressed yttrium oxide-tungsten matrix dispenser cathodes are prepared by a sol–gel method combined with high temperature sintering in dry hydrogen atmosphere. The results show that the growth of the grains is hampered by the pinning effect of Y 2 O 3 distributing uniformly between the tungsten particles, resulting in the formation of small grain size. It is found that Y 2 O 3 improves the secondary electron emission property, i.e., the secondary emission yield increases with the increase of Y 2 O 3 content in the samples. The maximum secondary emission yield δ max of the cathode with 15% amount of Y 2 O 3 can reach 2.92. Furthermore, the cathode shows a certain thermionic emission performance. The zero field emission current density J 0 of 4.18A/cm 2 has reached at 1050 °C b for this kind of cathode after being activated at 1200 °C b , which are much higher than that of rare earth oxide doped molybdenum (REO-Mo) cathode reported in the previous work. - Highlights: • Yttrium oxide was chosen as the secondary emission substance based on first principle calculation result. • A new kind of cathode has been successfully obtained. • Pressed yttrium oxide-tungsten matrix dispenser cathode exhibits good emission properties. • The improvement of the cathode emission can be well explained by the surface analysis results presented in this work

  20. A study of transition from n- to p-type based on hexagonal WO3 nanorods sensor

    Science.gov (United States)

    Wu, Ya-Qiao; Hu, Ming; Wei, Xiao-Ying

    2014-04-01

    Hexagonal WO3 nanorods are fabricated by a facile hydrothermal process at 180 °C using sodium tungstate and sodium chloride as starting materials. The morphology, structure, and composition of the prepared nanorods are studied by scanning electron microscopy, X-ray diffraction spectroscopy, and energy dispersive spectroscopy. It is found that the agglomeration of the nanorods is strongly dependent on the PH value of the reaction solution. Uniform and isolated WO3 nanorods with diameters ranging from 100 nm-150 nm and lengths up to several micrometers are obtained at PH = 2.5 and the nanorods are identified as being hexagonal in phase structure. The sensing characteristics of the WO3 nanorod sensor are obtained by measuring the dynamic response to NO2 with concentrations in the range 0.5 ppm-5 ppm and at working temperatures in the range 25 °C-250 °C. The obtained WO3 nanorods sensors are found to exhibit opposite sensing behaviors, depending on the working temperature. When being exposed to oxidizing NO2 gas, the WO3 nanorod sensor behaves as an n-type semiconductor as expected when the working temperature is higher than 50 °C, whereas, it behaves as a p-type semiconductor below 50 °C. The origin of the n- to p-type transition is correlated with the formation of an inversion layer at the surface of the WO3 nanorod at room temperature. This finding is useful for making new room temperature NO2 sensors based on hexagonal WO3 nanorods.

  1. A study of transition from n- to p-type based on hexagonal WO3 nanorods sensor

    International Nuclear Information System (INIS)

    Wu Ya-Qiao; Hu Ming; Wei Xiao-Ying

    2014-01-01

    Hexagonal WO 3 nanorods are fabricated by a facile hydrothermal process at 180 °C using sodium tungstate and sodium chloride as starting materials. The morphology, structure, and composition of the prepared nanorods are studied by scanning electron microscopy, X-ray diffraction spectroscopy, and energy dispersive spectroscopy. It is found that the agglomeration of the nanorods is strongly dependent on the PH value of the reaction solution. Uniform and isolated WO 3 nanorods with diameters ranging from 100 nm–150 nm and lengths up to several micrometers are obtained at PH = 2.5 and the nanorods are identified as being hexagonal in phase structure. The sensing characteristics of the WO 3 nanorod sensor are obtained by measuring the dynamic response to NO 2 with concentrations in the range 0.5 ppm–5 ppm and at working temperatures in the range 25 °C–250 °C. The obtained WO 3 nanorods sensors are found to exhibit opposite sensing behaviors, depending on the working temperature. When being exposed to oxidizing NO 2 gas, the WO 3 nanorod sensor behaves as an n-type semiconductor as expected when the working temperature is higher than 50 °C, whereas, it behaves as a p-type semiconductor below 50 °C. The origin of the n- to p-type transition is correlated with the formation of an inversion layer at the surface of the WO 3 nanorod at room temperature. This finding is useful for making new room temperature NO 2 sensors based on hexagonal WO 3 nanorods. (general)

  2. Tungsten oxide thin films obtained by anodisation in low electrolyte concentration

    Energy Technology Data Exchange (ETDEWEB)

    Costa, Nadja B.D. da [Centro de Ciências Químicas, Farmacêuticas e de Alimentos, Universidade Federal de Pelotas, Campus Capão do Leão, s/n, Pelotas, RS (Brazil); Pazinato, Julia C.O. [Instituto de Química, Universidade Federal do Rio Grande do Sul, Av. Bento Gonçalves, 9500 Porto Alegre, RS (Brazil); Sombrio, Guilherme; Pereira, Marcelo B.; Boudinov, Henri [Instituto de Física, Universidade Federal do Rio Grande do Sul, Av. Bento Gonçalves, 9500 Porto Alegre, RS (Brazil); Gündel, André; Moreira, Eduardo C. [Universidade Federal do Pampa, Travessa 45, 1650 Bagé, RS (Brazil); Garcia, Irene T.S., E-mail: irene.garcia@ufrgs.br [Instituto de Química, Universidade Federal do Rio Grande do Sul, Av. Bento Gonçalves, 9500 Porto Alegre, RS (Brazil)

    2015-03-02

    Tungsten oxide nanostructured films were grown on tungsten substrates by anodisation under a fixed voltage and with sodium fluoride as electrolyte. The effect of the anion chloride and the influence of the modifying agent disodium hydrogen phosphate in the tungsten oxide films were also investigated. The structural characterisation of the films was performed by scanning electron microscopy, atomic force microscopy and Raman spectroscopy. The band gap was determined through diffuse reflectance spectroscopy. The thin films were photoluminescent and emitted in the range of 300 to 630 nm when irradiated at 266 nm. The synthesised films efficiently degraded of methyl orange dye in the presence of hydrogen peroxide and 250 nm radiation. The modifying agent was responsible for the improvement of the photocatalytic activity. Films with similar photocatalytic performance were obtained when the system sodium fluoride and disodium hydrogen phosphate were replaced by sodium chloride. The porous structure and low band gap values were responsible for the photocatalytic behaviour. - Highlights: • Tungsten oxide thin films were obtained by anodisation of tungsten in aqueous media. • The performance of the NaCl, NaF and NaF/Na{sub 2}HPO{sub 4} as electrolytes was investigated. • The relation between structure and optical behaviour has been discussed. • Films obtained with NaCl and NaF/Na{sub 2}HPO{sub 4} present similar photocatalytic activity.

  3. Density evaluation of remotely-supplied hydrogen radicals produced via tungsten filament method for SiCl4 reduction

    Science.gov (United States)

    Zohra Dahmani, Fatima; Okamoto, Yuji; Tsutsumi, Daiki; Ishigaki, Takamasa; Koinuma, Hideomi; Hamzaoui, Saad; Flazi, Samir; Sumiya, Masatomo

    2018-05-01

    Effect of the hydrogen radical on the reduction of a silicon tetrachloride (SiCl4) source was studied. The hydrogen radicals were generated using a tungsten (W) filament in a generation chamber, and were remotely supplied to another reaction chamber. The density of the hydrogen radical was estimated from the optical transmittance of 600-nm-wavelength light through phosphate glass doped with tungsten oxide (WO3). Lifetime of the hydrogen radical seemed sufficiently long, and its density as supplied to the reaction chamber was estimated to be on the order of 1012 cm‑3. Signal intensity of the peak corresponding to SiCl4 (m/z = 170) detected by quadrupole-mass measurement was confirmed to decrease owing to the reaction with the remotely-supplied hydrogen radical. This indicates the possibility that chemically-stable SiCl4, as one of the by-products of the Siemens process, can be reduced to produce silicon.

  4. Conduction and transport numbers in metacomposites MeWO4 · WO3 (Me = Ca, Sr, Ba)

    International Nuclear Information System (INIS)

    Nejman, A.Ya.; Pestereva, N.N.; Sharafutdinov, A.R.; Kostikov, Yu.P.

    2005-01-01

    The conductivity and transfer numbers of charge carriers for composites in the MeWO 4 -WO 3 (Me = Ca, Sr, Ba) systems are studied as a function of the temperature and the activity of oxygen in a gas phase. The transfer numbers are determined by the emf method and are estimated from dependences of conductivity on the activity of oxygen in a gas phase. The deficiencies of the given procedure as applied to investigation of properties of composite phases are analyzed. The materials under study are classified as metacomposites. The concentration intervals of the ionic, mixed, and electronic conductivities are determined. The conductivity of (100-x)MeWO 4 · xWO 3 composites is predominantly ionic at x ≤ 10 (Me = Ca), x ≤ 60 (Me = Sr), and x ≤ 45 (Me = Ba). The obtained data are explained in the framework of a model that represents a composite as a distributed matrix system where a film of surface phase MeW-s with a high mobility of oxygen ions plays the role of a connected matrix. It is presumed that the surface phase MeW-s possesses double-sided surface activity (α MeW-s ≤ α WO 3 , α MeWO 4 ) and a higher mobility with respect to MeWO 4 and WO 3 . The discovered anomalies of dependences σ O 2- (T) and partial conductivities σ O 2- , σ el (T) are explained by a change in the stoichiometry, morphology, and the degree of tie-up of surface phase MeW-s caused by a change in the temperature and composition of composites [ru

  5. Comparison of modification strategies towards enhanced charge carrier separation and photocatalytic degradation activity of metal oxide semiconductors (TiO2, WO3 and ZnO)

    Science.gov (United States)

    Kumar, S. Girish; Rao, K. S. R. Koteswara

    2017-01-01

    Metal oxide semiconductors (TiO2, WO3 and ZnO) finds unparalleled opportunity in wastewater purification under UV/visible light, largely encouraged by their divergent admirable features like stability, non-toxicity, ease of preparation, suitable band edge positions and facile generation of active oxygen species in the aqueous medium. However, the perennial failings of these photocatalysts emanates from the stumbling blocks like rapid charge carrier recombination and meager visible light response. In this review, tailoring the surface-bulk electronic structure through the calibrated and veritable approaches such as impurity doping, deposition with noble metals, sensitizing with other compounds (dyes, polymers, inorganic complexes and simple chelating ligands), hydrogenation process (annealing under hydrogen atmosphere), electronic integration with other semiconductors, modifying with carbon nanostructures, designing with exposed facets and tailoring with hierarchical morphologies to overcome their critical drawbacks are summarized. Taking into account the materials intrinsic properties, the pros and cons together with similarities and striking differences for each strategy in specific to TiO2, WO3 & ZnO are highlighted. These subtlety enunciates the primacy for improving the structure-electronic properties of metal oxides and credence to its fore in the practical applications. Future research must focus on comparing the performances of ZnO, TiO2 and WO3 in parallel to get insight into their photocatalytic behaviors. Such comparisons not only reveal the changed surface-electronic structure upon various modifications, but also shed light on charge carrier dynamics, free radical generation, structural stability and compatibility for photocatalytic reactions. It is envisioned that these cardinal tactics have profound implications and can be replicated to other semiconductor photocatalysts like CeO2, In2O3, Bi2O3, Fe2O3, BiVO4, AgX, BiOX (X = Cl, Br & I), Bi2WO6, Bi2MoO6

  6. Observation of intact desorption ionization of peptide molecules from arrays of tungsten oxide nanowires by laser irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Han, Sang Yun [Dept. of Nanochemistry, Gachon University, Seongnam (Korea, Republic of)

    2015-08-15

    Length-controlled WO{sub 3} surface nanowires with a 50 nm diameter were prepared by utilizing anodic Al{sub 2}O{sub 3} templates. Careful control of the fabrication process yielded a set of length-controlled nanowire arrays (Figure 1). The lengths of the nanowires covered a range of 60–250 nm. Typically, a 0.5-μL drop of a sample solution in 10% MeOH that contained 2 pmol of sample was pipetted directly onto the nanowire chips, which were dried under ambient conditions. We report the observation of intact LDI of thermally labile peptides from WO{sub 3} nanowire arrays, which have never been reported for any other metal oxide nanowire arrays. As metal oxides are thermally stable and useful in many applications, and fabrication of various nanostructures are well established, we suggest that the nanostructured surfaces of metal oxides are promising for LDI and thus worthy of further investigations.

  7. Facile synthesis of NiWO4/reduced graphene oxide nanocomposite with excellent capacitive performance for supercapacitors

    International Nuclear Information System (INIS)

    Xu, Xiaowei; Pei, Liyuan; Yang, Yang; Shen, Jianfeng; Ye, Mingxin

    2016-01-01

    NiWO 4 /reduced graphene oxide (NWG) nanocomposite was successfully synthesized through a facile one-pot solvothermal method for the first time. The resulting nanocomposite is composed of NiWO 4 nanoparticles that are uniformly attached on graphene sheets by in situ reducing. The as-prepared NWG composite has been systematically characterized by Powder X-ray diffraction, Fourier transform infrared spectra, Raman spectroscopy, Thermogravimetric analysis, Scanning electron microscopy, Transmission electron microscopy, X-ray photoelectron spectra, and Brunauer–Emmett–Teller analysis. The capacitive performances of the as-prepared NWG composite as electrode material are investigated. It is found that the NWG composite exhibits a high specific capacitance up to 1031.3 F g −1 at a current density of 0.5 A g −1 . The greatly enhanced capacitive performance of the NWG electrode can be attributed to the synergetic effect of NiWO 4 nanoparticles and RGO, which provides conducting channels and active sites. The cyclic stability tests demonstrated no decreases of its initial values after 5000 cycles, suggesting that such hybrid electrode possesses a great potential application in energy-storage devices. - Highlights: • NiWO 4 /RGO composite was successfully prepared through a facile solvothermal method. • The NiWO 4 /RGO composite shows a high specific capacitance of 1031.3 F g −1 . • Enhanced electrical conductivity leads to superior electrochemical performance.

  8. Faster response of NO2 sensing in graphene–WO3 nanocomposites

    International Nuclear Information System (INIS)

    Srivastava, Shubhda; Jain, Kiran; Gupta, Govind; Senguttuvan, T D; Singh, V N; Singh, Sukhvir; Vijayan, N; Dilawar, Nita

    2012-01-01

    Graphene-based nanocomposites have proven to be very promising materials for gas sensing applications. In this paper, we present a general approach for the preparation of graphene–WO 3 nanocomposites. Graphene–WO 3 nanocomposite thin-layer sensors were prepared by drop coating the dispersed solution onto the alumina substrate. These nanocomposites were used for the detection of NO 2 for the first time. TEM micrographs revealed that WO 3 nanoparticles were well distributed on graphene nanosheets. Three different compositions (0.2, 0.5 and 0.1 wt%) of graphene with WO 3 were used for the gas sensing measurements. It was observed that the sensor response to NO 2 increased nearly three times in the case of graphene–WO 3 nanocomposite layer as compared to a pure WO 3 layer at room temperature. The best response of the graphene–WO 3 nanocomposite was obtained at 250 °C. (paper)

  9. Vanadium Doped Tungsten Oxide Material - Electrical Physical and Sensing Properties

    Directory of Open Access Journals (Sweden)

    Shishkin N. Y.

    2008-05-01

    Full Text Available The electrical physical and sensing (to VOCs and inorganic gases properties of vanadium doped tungsten oxide in the regions of phase transition temperature were investigated. Vanadium oxide (II dimerization was observed in the doped material, corresponding to new phase transition. The extreme sensitivity and selectivity to chemically active gases and vapors in small concentrations: CO, NOx, NH3 acetone, ethanol near phase transitions temperature was found. Sensor elements were manufactured for the quantitative detection (close to 1 ppm of alcohol and ammonia.

  10. Exploration on anion ordering, optical properties and electronic structure in K3WO3F3 elpasolite

    International Nuclear Information System (INIS)

    Atuchin, V.V.; Isaenko, L.I.; Kesler, V.G.; Lin, Z.S.; Molokeev, M.S.; Yelisseyev, A.P.; Zhurkov, S.A.

    2012-01-01

    Room-temperature modification of potassium oxyfluorotungstate, G2-K 3 WO 3 F 3 , has been prepared by low-temperature chemical route and single crystal growth. Wide optical transparency range of 0.3–9.4 μm and forbidden band gap E g =4.32 eV have been obtained for G2-K 3 WO 3 F 3 crystal. Meanwhile, its electronic structure has been calculated with the first-principles calculations. The good agreement between the theorectical and experimental results have been achieved. Furthermore, G2-K 3 WO 3 F 3 is predicted to possess the relatively large nonlinear optical coefficients. - Graphical abstract: Using the cm-size K 3 WO 3 F 3 crystal (left upper), the transmission spectrum (right upper) and XPS valence electronic states (left lower) were measured, agreed with the ab initio results (right lower). Highlights: ► The cm-size G2-K 3 WO 3 F 3 single crystals are obtained. ► Optical absorption edge and transmission range are defined for G2-K 3 WO 3 F 3 crystal. ► Crystal structures of all known K 3 WO 3 F 3 polymorph modifications are determined. ► Experimental electronic structure is consistent with the first-principles result. ► G2-K 3 WO 3 F 3 is predicted as a crystal with large NLO coefficients.

  11. Synthesis, characterization and photocatalytic activity of WO{sub 3}/TiO{sub 2} for NO removal under UV and visible light irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Luévano-Hipólito, E. [CIIDIT, Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico); Martínez-de la Cruz, A., E-mail: azael.martinezdl@uanl.edu.mx [CIIDIT, Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico); López-Cuellar, E. [CIIDIT, Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico); Yu, Q.L.; Brouwers, H.J.H. [Department of the Built Environment, Eindhoven University of Technology, P.O. Box 513, 5600 MB Eindhoven (Netherlands)

    2014-11-14

    Samples with different proportions WO{sub 3}/TiO{sub 2} were prepared by co-precipitation method followed by a heat treatment. The samples were characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), diffuse reflectance spectroscopy (DRS), and adsorption–desorption N{sub 2} isotherms (BET). The photocatalytic properties of WO{sub 3}/TiO{sub 2} samples were evaluated in the photo-oxidation reaction of nitric oxide (NO) under UV and visible light irradiation. The highest photocatalytic activity was observed in the WO{sub 3}/TiO{sub 2} sample with a composition of 80% mole of TiO{sub 2}. Among the different substrates used for supporting the photocatalyst, the best results were reached over concrete and glass when it was exposed to UV and visible light irradiation, respectively. In overall, the photocatalytic efficiency of the synthesized materials was higher under UV than visible light irradiation. - Highlights: • WO{sub 3}/TiO{sub 2} prepared in simple way show high photocatalytic activity for NO removal. • The concrete was the best substrate to the performance of WO{sub 3}/TiO{sub 2} with UV radiation. • The glass was the best substrate to the performance of WO{sub 3}/TiO{sub 2} with visible radiation.

  12. Intrinsic Defects and H Doping in WO3

    KAUST Repository

    Zhu, Jiajie; Vasilopoulou, Maria; Davazoglou, Dimitris; Kennou, Stella; Chroneos, Alexander; Schwingenschlö gl, Udo

    2017-01-01

    WO3 is widely used as industrial catalyst. Intrinsic and/or extrinsic defects can tune the electronic properties and extend applications to gas sensors and optoelectonics. However, H doping is a challenge to WO3, the relevant mechanisms being hardly

  13. In situ growth of metal particles on 3D urchin-like WO3 nanostructures.

    Science.gov (United States)

    Xi, Guangcheng; Ye, Jinhua; Ma, Qiang; Su, Ning; Bai, Hua; Wang, Chao

    2012-04-18

    Metal/semiconductor hybrid materials of various sizes and morphologies have many applications in areas such as catalysis and sensing. Various organic agents are necessary to stabilize metal nanoparticles during synthesis, which leads to a layer of organic compounds present at the interfaces between the metal particles and the semiconductor supports. Generally, high-temperature oxidative treatment is used to remove the organics, which can extensively change the size and morphology of the particles, in turn altering their activity. Here we report a facile method for direct growth of noble-metal particles on WO(3) through an in situ redox reaction between weakly reductive WO(2.72) and oxidative metal salts in aqueous solution. This synthetic strategy has the advantages that it takes place in one step and requires no foreign reducing agents, stabilizing agents, or pretreatment of the precursors, making it a practical method for the controlled synthesis of metal/semiconductor hybrid nanomaterials. This synthetic method may open up a new way to develop metal-nanoparticle-loaded semiconductor composites. © 2012 American Chemical Society

  14. Characterization of nanosized Al2(WO4)3

    International Nuclear Information System (INIS)

    Nihtianova, D.; Velichkova, N.; Nikolova, R.; Koseva, I.; Yordanova, A.; Nikolov, V.

    2011-01-01

    Graphical abstract: TEM method allows to detect small quantities of impurities not detectable by other methods. In our case impurities of W 5 O 14 are detected in Al 2 (WO 4 ) 3 nanopowder. Highlights: → Nanosized Al 2 (WO 4 ) 3 by simple co-precipitation method. → Spherical particles with mean size of 22 nm distributed between 10 and 40 nm at 630 o C. → XRD, DTA and TEM confirm well defined products with perfect structure. → TEM locality allows detection of impurities not detectable by XRD and DTA. -- Abstract: Nanosized aluminum tungstate Al 2 (WO 4 ) 3 was prepared by co-precipitation reaction between Na 2 WO 4 and Al(NO 3 ) 3 aqueous solutions. The powder size and shape, as well as size distribution are estimated after different conditions of powder preparation. The purity of the final product was investigated by XRD and DTA analyses, using the single crystal powder as reference. Between the specimen and the reference no difference was detected. The crystal structure of Al 2 (WO 4 ) 3 nanosized powder was confirmed by TEM (SAED, HRTEM). In additional, TEM locality allows to detect some W 5 O 14 impurities, which are not visible by conventional X-ray powder diffraction and thermal analyses.

  15. Studies on the pressed yttrium oxide-tungsten matrix as a possible dispenser cathode material

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Fan; Wang, Jinshu, E-mail: wangjsh@bjut.edu.cn; Liu, Wei; Liu, Xiang; Zhou, Meiling

    2015-01-15

    Yttrium oxide was chosen as the secondary emission substance based on calculation results through first principle theory method. A new kind of pressed yttrium oxide-tungsten matrix dispenser cathodes are prepared by a sol–gel method combined with high temperature sintering in dry hydrogen atmosphere. The results show that the growth of the grains is hampered by the pinning effect of Y{sub 2}O{sub 3} distributing uniformly between the tungsten particles, resulting in the formation of small grain size. It is found that Y{sub 2}O{sub 3} improves the secondary electron emission property, i.e., the secondary emission yield increases with the increase of Y{sub 2}O{sub 3} content in the samples. The maximum secondary emission yield δ{sub max} of the cathode with 15% amount of Y{sub 2}O{sub 3} can reach 2.92. Furthermore, the cathode shows a certain thermionic emission performance. The zero field emission current density J{sub 0} of 4.18A/cm{sup 2} has reached at 1050 °C{sub b} for this kind of cathode after being activated at 1200 °C{sub b}, which are much higher than that of rare earth oxide doped molybdenum (REO-Mo) cathode reported in the previous work. - Highlights: • Yttrium oxide was chosen as the secondary emission substance based on first principle calculation result. • A new kind of cathode has been successfully obtained. • Pressed yttrium oxide-tungsten matrix dispenser cathode exhibits good emission properties. • The improvement of the cathode emission can be well explained by the surface analysis results presented in this work.

  16. Visible-light photocatalytic activity of graphene oxide-wrapped Bi{sub 2}WO{sub 6} hierarchical microspheres

    Energy Technology Data Exchange (ETDEWEB)

    Zhai, Jiali; Yu, Hongwen, E-mail: yuhw@iga.ac.cn; Li, Haiyan; Sun, Lei; Zhang, Kexin; Yang, Hongjun

    2015-07-30

    Graphical abstract: - Highlights: • GO/Bi{sub 2}WO{sub 6} are readily fabricated by facile bubbling pretreatment and freeze drying. • GO/Bi{sub 2}WO{sub 6} possess excellent photocatalytic activity under visible light irradiation. • The visible light activity of GO/Bi{sub 2}WO{sub 6} is affected by the amount of GO. • The photostablity of GO is due to the photo-generated electrons transfer to Bi{sub 2}WO{sub 6}. - Abstract: A facile approach of fabricating homogeneous graphene oxide (GO)-wrapped Bi{sub 2}WO{sub 6} microspheres (GO/Bi{sub 2}WO{sub 6}) is developed. The transmission electron microscopy (TEM) results show that a heterojunction interface between GO and Bi{sub 2}WO{sub 6}. The UV–vis diffuse reflection spectra (DRS) reveal that the as-prepared GO/Bi{sub 2}WO{sub 6} composites own more intensive absorption in the visible light range compared with pure Bi{sub 2}WO{sub 6}. These characteristic structural and optical properties endow GO/Bi{sub 2}WO{sub 6} composites with enhanced photocatalytic activity. The enhanced photocatalytic activity of the GO/Bi{sub 2}WO{sub 6} is attributed predominantly to the synergetic effect between GO and Bi{sub 2}WO{sub 6}, causing rapid generation and separation of photo-generated charge carriers.

  17. Electrochemical Behavior of TiO2 Nanoparticle Doped WO3 Thin Films

    Directory of Open Access Journals (Sweden)

    Suvarna R. Bathe

    2014-01-01

    Full Text Available Nanoparticle TiO2 doped WO3 thin films by pulsed spray pyrolysis technique have been studied on fluorine tin doped (FTO and glass substrate. XRD shows amorphous nature for undoped and anatase phase of TiO2 having (101 plane for nanoparticle TiO2 doped WO3 thin film. SEM shows microfibrous reticulated porous network for WO3 with 600 nm fiber diameter and nanocrystalline having size 40 nm for TiO2 nanoparticle doped WO3 thin film. TiO2 nanoparticle doped WO3 thin film shows ~95% reversibility due to may be attributed to nanocrystalline nature of the film, which helpful for charge insertion and deinsertion process. The diffusion coefficient for TiO2 nanoparticle doped WO3 film is less than undoped WO3.

  18. Recovery of tungsten from wolframite from the Igarape Manteiga mine (Rondonia - Brazil) via acidic leaching; Isolamento do tungstenio da volframita da mina de Igarape Manteiga (Rondonia - Brasil) por lixiviacao acida

    Energy Technology Data Exchange (ETDEWEB)

    Paulino, Jessica Frontino; Afonso, Julio Carlos [Departamento de Quimica Analitica, Instituto de Quimica, Universidade Federal do Rio de Janeiro, RJ (Brazil); Mantovano, Jose Luiz; Vianna, Claudio Augusto; Cunha, Jose Waldemar Silva Dias da [Instituto de Engenharia Nuclear (IEN/CNEN-RJ), Rio de Janeiro - RJ (Brazil)

    2012-07-01

    We report results of the efficiency of tungsten extraction from wolframite concentrate (containing 61.5 wt % WO{sub 3}) from the Igarape Manteiga mine (state of Rondonia, Brazil) through acid leaching with strong mineral acids at 100 deg C and 400 rpm for 2-4 h. HCl yielded insoluble matter containing the highest WO{sub 3} content (90 wt %). This solid was dissolved in concentrated NH{sub 3(aq)} at 25 deg C and the insoluble matter filtrated. The filtrate was slowly evaporated. 70 wt % of the tungsten present in the starting concentrate material was recovered as ammonium paratungstate (APT). (author)

  19. Study of thermoelectron emission of oxidized tungsten sponge in cesium atom flow

    International Nuclear Information System (INIS)

    Tursunmetov, K.A.; Sabirov, A.K.

    1993-01-01

    Thermoelectron emission of a tungsten sponge with 30-40% porosity is studied. The tungsten sponge is produced of fine-grain tungsten powder (diameter - 1-2 μm) according to standard technology. It is shown that tungsten sponge oxidation at T=1000 K with subsequent heating in vacuum at T=1100 K allows one to obtain the minimal stable and reproducible work function at the level of 1.03-1.05 eV in a flux of cesium atoms. Estimations show that effective emitting surface is 15-20 times as much as the polycrystal surface

  20. Hot-wire substoichiometric tungsten oxide films deposited in hydrogen environment with n-type conductivity

    International Nuclear Information System (INIS)

    Kostis, I; Vasilopoulou, M; Giannakopoulos, K; Papadimitropoulos, G; Davazoglou, D; Michalas, L; Papaioannou, G; Konofaos, N; Iliadis, A A; Kennou, S

    2012-01-01

    Substoichiometric tungsten oxide nanostructured films were synthesized by a hot-wire deposition technique in hydrogen-rich environment and characterized for their structural and electrical properties. A semiconducting behaviour was identified, allowing n-type conductivity even at room temperature which is an important result since it is well known that fully stoichiometric tungsten trioxide is nearly an insulator. Current-voltage characteristics for various temperatures were measured for tungsten oxide/Si heterostructures and analysed using proper modelling. As a result, the conduction mechanism inside the films was identified and found to be of a dual nature, with variable range hopping being dominant at near room temperatures. The saturation current was found to be thermally activated and the activation energy was calculated at 0.40 eV and the grain boundaries barrier at 150 meV. From Hall measurements it was also revealed that the dominant carriers are electrons and a carrier concentration of about 10 14 cm -3 was estimated.

  1. A mesoporous WO{sub 3−X}/graphene composite as a high-performance Li-ion battery anode

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Fei [C-Industry Incubation Center, Korea Research Institute of Chemical Technology (KRICT), Daejeon 305-600 (Korea, Republic of); Kim, Jong Gu [C-Industry Incubation Center, Korea Research Institute of Chemical Technology (KRICT), Daejeon 305-600 (Korea, Republic of); Department of Fine Chemical Engineering and Applied Chemistry, Chungnam National University, Daejeon 305-764 (Korea, Republic of); Lee, Chul Wee [C-Industry Incubation Center, Korea Research Institute of Chemical Technology (KRICT), Daejeon 305-600 (Korea, Republic of); University of Science and Technology (UST), Gajeong-ro, Yuseong-gu, Daejeon 305-333 (Korea, Republic of); Im, Ji Sun, E-mail: jsim@krict.re.kr [C-Industry Incubation Center, Korea Research Institute of Chemical Technology (KRICT), Daejeon 305-600 (Korea, Republic of); University of Science and Technology (UST), Gajeong-ro, Yuseong-gu, Daejeon 305-333 (Korea, Republic of)

    2014-10-15

    Graphical abstract: The highly flexible and conductive graphene layer can enhance electron transfer, protect metal oxides against disintegration and aggregation and buffer the strain induced by volume expansion during cycles. The mesoporous surface layer provides an open network for Li+ diffusion. - Highlights: • Novel cocktail effects of 2D mesoporous WO{sub 3−X}/graphene for lithium ion battery. • New approach for lithium ion battery by easy and unique synthesis method. • Mechanism study with proper data for understanding a reaction on anode surface. - Abstract: A novel mesoporous WO{sub 3−X}/graphene composite was developed. This material allowed rapid electron and Li{sup +} ion diffusion when used as a Li-ion battery (LIB) anode material. Remarkably, the graphene support protected WO{sub 3−X} from changing volume during the electrochemical cycling process; this process generally induces capacity loss. The current work describes a high-performance anode material for LIB that has highly dense WO{sub 3−X}, as well as high capacity, rate capability and stability.

  2. WO3 Nanowires on Graphene Sheets as Negative Electrode for Supercapacitors

    Directory of Open Access Journals (Sweden)

    Bo Liu

    2017-01-01

    Full Text Available WO3 nanowires directly grown on graphene sheets have been fabricated by using a seed-mediated hydrothermal method. The morphologies and electrochemical performance of WO3 films prepared by different process were studied. The results show that the precoated nanoseeds and graphene sheets on graphite electrode provide more reactive centers for the nucleation and formation of uniform WO3 nanowires. The WO3 nanowires electrode exhibits a high area specific capacitance of 800 mF cm−2 over negative potential range from −1.0 V to 0 V versus SCE in 1 M Li2SO4 solution. A high performance electrochemical supercapacitor assembled with WO3 nanowires as negative electrode and PANI/MnO2 as positive electrodes over voltage range of 1.6 V displays a high volumetric capacitance of 2.5 F cm−3, which indicate great potential applications of WO3 nanowires on graphene sheets as negative electrode for energy storage devices.

  3. Raman Spectroscopic Study of Tungsten(VI) Oxosulfato Complexes in WO3–K2S2O7–K2SO4 Molten Mixtures: Stoichiometry, Vibrational Properties and Molecular Structure

    DEFF Research Database (Denmark)

    Paulson, Andreas L.; Kalampounias, Angelos G.; Berg, Rolf W.

    2011-01-01

    The dissolution reaction of WO3 in pure molten K2S2O7 and in molten K2S2O7-K2SO4 mixtures is studied under static equilibrium conditions in the XWO3 0 = 0-0.33 mol fraction range at temperatures up to 860 C. High temperature Raman spectroscopy shows that the dissolution leads to formation of WVI...... configuration as a core unit within the oxosulfato complexes formed. A quantitative exploitation of the relative Raman intensities in the binary WO3-K2S2O7 system allows the determination of the stoichiometric coefficient, n, of the complex formation reaction WO3 þ nS2O7 2-fC2n-. It is found that n = 1......; therefore, the reaction WO3 þ S2O7 2- f WO2(SO4)2 2- with six-fold W coordination is proposed as fully consistent with the observed Raman features. The effects of the incremental dissolution and presence of K2SO4 inWO3-K2S2O7 melts point to aWO3 3 K2S2O7 3 K2SO4 stoichiometry and a corresponding complex...

  4. Reduced graphene oxide wrapped Bi{sub 2}WO{sub 6} hybrid with ultrafast charge separation and improved photoelectrocatalytic performance

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Huan [School of Chemical Engineering and Technology, Hebei University of Technology, Tianjin 300130, PR China (China); Liang, Yinghua, E-mail: liangyh@ncst.edu.cn [School of Chemical Engineering and Technology, Hebei University of Technology, Tianjin 300130, PR China (China); College of Chemical Engineering, North China University of Science and Technology, Tangshan 063009, PR China (China); Liu, Li; Hu, Jinshan [College of Chemical Engineering, North China University of Science and Technology, Tangshan 063009, PR China (China); Cui, Wenquan, E-mail: wkcui@163.com [College of Chemical Engineering, North China University of Science and Technology, Tangshan 063009, PR China (China)

    2017-01-15

    Highlights: • The rGO wrapped Bi{sub 2}WO{sub 6} photoelectrode was successfully synthesized. • The Bi{sub 2}WO{sub 6}@rGOhighlyincreasedthechargeseparationefficiency. • The photoelectrode exhibited enhanced photoelectrocatalytic degradation for RhB. - Abstract: A reduced graphene oxide (rGO) wrapped Bi{sub 2}WO{sub 6} (Bi{sub 2}WO{sub 6}@rGO) hybrid as photoelectrode for enhanced photoelectrocatalytic (PEC) degradation of organic pollutants is reported, which exhibited excellent charge separation and photoconversion efficiency. The core@shell structured Bi{sub 2}WO{sub 6}@rGO photoelectrode yielded a pronounced 1.56-fold and 23.8-fold photocurrent density at 1.0 V vs. saturated calomel electrode (SCE), than that of loading structured Bi{sub 2}WO{sub 6}-rGO and pure Bi{sub 2}WO{sub 6}. The Bi{sub 2}WO{sub 6}@rGO hybrid exhibited enhanced photoelectrocatalytic efficiency for degradation of Rhodamine B (RhB), which was 43.0% and 65.6% higher than that of photocatalytic (PC) and electrocatalytic (EC) processes, respectively. The enhancement in PEC degradation of RhB benefited from: (1) a strong interaction and a wide range of conjugation were formed in the core@shell system; (2) a 0.26 V of flat band potential was negatively shifted in case of Bi{sub 2}WO{sub 6}@rGO composite; (3) the photogenerated electrons and holes could be spatially separated by external electric potentials.

  5. The use of tungsten as a chronically implanted material

    Science.gov (United States)

    Shah Idil, A.; Donaldson, N.

    2018-04-01

    This review paper shows that tungsten should not generally be used as a chronically implanted material. The metal has a long implant history, from neuroscience, vascular medicine, radiography, orthopaedics, prosthodontics, and various other fields, primarily as a result of its high density, radiopacity, tensile strength, and yield point. However, a crucial material criterion for chronically implanted metals is their long-term resistance to corrosion in body fluids, either by inherently noble metallic surfaces, or by protective passivation layers of metal oxide. The latter is often assumed for elemental tungsten, with references to its ‘inertness’ and ‘stability’ common in the literature. This review argues that in the body, metallic tungsten fails this criterion, and will eventually dissolve into the soluble hexavalent form W6+, typically represented by the orthotungstate WO42- (monomeric tungstate) anion. This paper outlines the metal’s unfavourable corrosion thermodynamics in the human physiological environment, the chemical pathways to either metallic or metal oxide dissolution, the rate-limiting steps, and the corrosion-accelerating effects of reactive oxidising species that the immune system produces post-implantation. Multiple examples of implant corrosion have been reported, with failure by dissolution to varying extents up to total loss, with associated emission of tungstate ions and elevated blood serum levels measured. The possible toxicity of these corrosion products has also been explored. As the field of medical implants grows and designers explore novel solutions to medical implant problems, the authors recommend the use of alternative materials.

  6. Facile synthesis of reduced graphene oxide/CoWO4 nanocomposites with enhanced electrochemical performances for supercapacitors

    International Nuclear Information System (INIS)

    Xu, Xiaowei; Shen, Jianfeng; Li, Na; Ye, Mingxin

    2014-01-01

    Highlights: • RGO/CoWO 4 composites were successfully prepared through a facile hydrothermal method. • RGO/CoWO 4 composites show much higher specific capacitances than pure CoWO 4 . • Enhanced electrical conductivity leads to superior electrochemical performance. - Abstract: A facile one-pot hydrothermal method was provided for synthesis of the reduced graphene oxide-cobalt tungstate (RGO/CoWO 4 ) nanocomposites with the enhanced electrochemical performances for supercapacitors for the first time. The resulting nanocomposites are comprised of CoWO 4 nanospheres that are well-anchored on graphene sheets by in situ reducing. The prepared RGO/CoWO 4 nanocomposites have been thoroughly characterized by Fourier–transform infrared spectroscopy, X-ray diffraction, Raman spectroscopy, Thermogravimetric analysis, Scanning electron microscopy, Transmission electron microscopy, X-ray photoelectron spectroscopy, and N 2 adsorption–desorption. Importantly, the prepared nanocomposites exhibit superior electrochemical performance to CoWO 4 as electrodes for supercapacitors. As a result, RGO/CoWO 4 nanocomposites with 91.6 wt% CoWO 4 content achieved a specific capacitance about 159.9 F g −1 calculated from the CV curves at 5 mV s −1 , which was higher than that of CoWO 4 (60.6 F g −1 ). The good electrochemical performance can be attributed to the increased electrical conductivity and the creation of new active sites due to the synergetic effect of RGO and CoWO 4 nanospheres. The cyclic stability tests demonstrated capacitance retention of about 94.7% after 1000 cycles, suggesting the potential application of RGO/CoWO 4 nanocomposites in energy-storage devices

  7. Electrochemical fabrication of interconnected tungsten bronze nanosheets for high performance supercapacitor

    Science.gov (United States)

    Yang, Gan; Liu, Xiao-Xia

    2018-04-01

    Interconnected H0.12WO3ṡH2O nanosheets with high electrochemical performances are fabricated on partial exfoliated graphite substrate (Ex-GF) by potential-limited pulse galvanostatic method (PLPG). The dead volume problem of bulk pesudocapacitive materials is addressed by the novel interconnected nanosheets structure, enabling a large specific capacitance of 5.95 F cm-2 (495.8 F g-1) at 2 mA cm-2. Merited from the fluent electrolyte penetration channels established by the plenty voids among nanosheets, as well as fast electron transportation in the electronic conductive tungsten bronze which is directly grown from graphite substrate, the obtained WO3/Ex-GF demonstrates excellent rate capability. The material can maintain 60.0% of its capacitance when the discharge current density increases from 2 to 100 mA cm-2. Moreover, WO3/Ex-GF doesn't show capacitance decay after 5000 galvanostatic charge-discharge cycles, displaying its super stability. Furthermore, a high performance asymmetric supercapacitor assembled by using WO3/Ex-GF and electrochemical fabricated MnO2/Ex-GF as negative and positive electrodes, respectively displays a high energy density of 2.88 mWh cm-3 at the power density of 11.1 mW cm-3, demonstrating its potential application for energy storage.

  8. Thermal oxidation of reactively sputtered amorphous W80N20 films

    International Nuclear Information System (INIS)

    Vu, Q.T.; Pokela, P.J.; Garden, C.L.; Kolawa, E.; Raud, S.; Nicolet, M.

    1990-01-01

    The oxidation behavior of reactively sputtered amorphous tungsten nitride of composition W 80 N 20 was investigated in dry and wet oxidizing ambient in the temperature range of 450 degree C--575 degree C. A single WO 3 oxide phase is observed. The growth of the oxide follows a parabolic time dependence which is attributed to a process controlled by the diffusivity of the oxidant in the oxide. The oxidation process is thermally activated with an activation energy of 2.5±0.05 eV for dry ambient and 2.35±0.05 eV for wet ambient. The pre-exponential factor of the reaction constant for dry ambient is 1.1x10 21 A 2 /min; that for wet ambient is only about 10 times less and is equal to 1.3x10 20 A 2 /min

  9. Electronic-level interactions of tungsten oxide with unsupported Se/Ru electrocatalytic nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Lewera, Adam; Miecznikowski, Krzysztof [Department of Chemistry, University of Warsaw, Pasteura 1, 02-093 Warsaw (Poland); Hunger, Ralf [Institute of Materials Science, Darmstadt University of Technology, Darmstadt (Germany); Kolary-Zurowska, Aneta [Department of Chemistry, University of Warsaw, Pasteura 1, 02-093 Warsaw (Poland); Wieckowski, Andrzej [Department of Chemistry, University of Illinois at Urbana-Champaign, Urbana, IL (United States); Kulesza, Pawel J., E-mail: pkulesza@chem.uw.edu.p [Department of Chemistry, University of Warsaw, Pasteura 1, 02-093 Warsaw (Poland)

    2010-11-01

    Se/Ru nanoparticles - a potent non-platinum catalyst towards oxygen reduction reaction - were modified by hydrated WO{sub 3} and investigated using the rotating disk/ring electrode methods and by synchrotron X-ray photoelectron spectroscopy. The modification resulted in an enhanced catalytic activity towards oxygen reduction reaction (ORR). Our data indicate that the oxygen reduction current starts ca. 70 mV more positive and formation of undesirable hydrogen peroxide has significantly decreased following the modification of Se/Ru with WO{sub 3}. X-ray photoelectron spectroscopy reveals that WO{sub 3} interacts electronically with Se/Ru as the W 4f and Se 3d line-shapes change. We therefore conclude that the electronic interactions between Se/Ru and WO{sub 3} are primarily responsible for the increase in activity and selectivity of the WO{sub 3}-modified Se/Ru towards ORR.

  10. Electronic-level interactions of tungsten oxide with unsupported Se/Ru electrocatalytic nanoparticles

    International Nuclear Information System (INIS)

    Lewera, Adam; Miecznikowski, Krzysztof; Hunger, Ralf; Kolary-Zurowska, Aneta; Wieckowski, Andrzej; Kulesza, Pawel J.

    2010-01-01

    Se/Ru nanoparticles - a potent non-platinum catalyst towards oxygen reduction reaction - were modified by hydrated WO 3 and investigated using the rotating disk/ring electrode methods and by synchrotron X-ray photoelectron spectroscopy. The modification resulted in an enhanced catalytic activity towards oxygen reduction reaction (ORR). Our data indicate that the oxygen reduction current starts ca. 70 mV more positive and formation of undesirable hydrogen peroxide has significantly decreased following the modification of Se/Ru with WO 3 . X-ray photoelectron spectroscopy reveals that WO 3 interacts electronically with Se/Ru as the W 4f and Se 3d line-shapes change. We therefore conclude that the electronic interactions between Se/Ru and WO 3 are primarily responsible for the increase in activity and selectivity of the WO 3 -modified Se/Ru towards ORR.

  11. An in situ carbonization-replication method to synthesize mesostructured WO3/C composite as nonprecious-metal anode catalyst in PEMFC.

    Science.gov (United States)

    Cui, Xiangzhi; Hua, Zile; Wei, Chenyang; Shu, Zhu; Zhang, Liangxia; Chen, Hangrong; Shi, Jianlin

    2013-02-01

    A meostructured WO(3)/C composite with crystalline framework and high electric conductivity has been synthesized by a new in situ carbonization-replication route using the block copolymer (poly(ethylene glycol)-block-poly(propylene glycol)-block-poly(ethylene glycol)) present in situ in the pore channels of mesoporous silica template as carbon source. X-ray diffraction, X-ray photoelectron spectroscopy, transmission electron microscopy, thermogravimetry differential thermal analysis, and N(2) adsorption techniques were adopted for the structural characterization. Cyclic voltammetry, chronoamperometry, and single-cell test for hydrogen electrochemical oxidation were adopted to characterize the electrochemical activities of the mesoporous WO(3)/C composite. The carbon content and consequent electric conductivity of these high-surface-area (108-130 m(2) g(-1)) mesostructured WO(3)/C composite materials can be tuned by variation of the duration of heat treatment, and the composites exhibited high and stable electrochemical catalytic activity. The single-cell test results indicated that the mesostructured WO(3)/C composites showed clear electrochemical catalytic activity toward hydrogen oxidation at 25 °C, which makes them potential non-precious-metal anode catalysts in proton exchange membrane fuel cell. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  12. Tungsten Oxide Photonic Crystals as Optical Transducer for Gas Sensing.

    Science.gov (United States)

    Amrehn, Sabrina; Wu, Xia; Wagner, Thorsten

    2018-01-26

    Some metal oxide semiconductors, such as tungsten trioxide or tin dioxide, are well-known as resistive transducers for gas sensing and offer high sensitivities down to the part per billion level. Electrical signal read-out, however, limits the information obtained on the electronic properties of metal oxides to a certain frequency range and its application because of the required electrical contacts. Therefore, a novel approach for building an optical transducer for gas reactions utilizing metal oxide photonic crystals is presented here. By the rational design of the structure and composition it is possible to synthesize a functional material which allows one to obtain insight into its electronic properties in the optical frequency range with simple experimental measures. The concept is demonstrated by tungsten trioxide inverse opal structure as optical transducer material for hydrogen sensing. The sensing behavior is analyzed in a temperature range from room temperature to 500 °C and in a wide hydrogen concentration range (3000 ppm to 10%). The sensing mechanism is mainly the refractive index change resulting from hydrogen intercalation in tungsten trioxide, but the back reaction has also impact on the optical properties of this system. Detailed chemical reaction studies provide suggestions for specific sensing conditions.

  13. Photocatalytic activity of Bi_2WO_6/Bi_2S_3 heterojunctions: the facilitation of exposed facets of Bi_2WO_6 substrate

    International Nuclear Information System (INIS)

    Yan, Long; Wang, Yufei; Shen, Huidong; Zhang, Yu; Li, Jian; Wang, Danjun

    2017-01-01

    Highlights: • Bi_2S_3/Bi_2WO_6 hybrids with exposed (020) Bi_2WO_6 facets have been synthesized. • X-ray photoelectron spectroscopy reveals that a small amount of Bi_2S_3 was formed. • The enhanced photoactivity of hybrids is due to heterojunction and (020) facets. • A possible photocatalytic degradation mechanism is proposed. - Abstract: Bi_2S_3/Bi_2WO_6 hybrid architectures with exposed (020) Bi_2WO_6 facets have been synthesized via a controlled anion exchange approach. X-ray photoelectron spectroscopy (XPS) reveals that a small amount of Bi_2S_3 was formed on the surface of Bi_2WO_6 during the anion exchange process, thus leading to the transformation from the Bi_2WO_6 to Bi_2S_3/Bi_2WO_6. A rhodamine B (RhB) aqueous solution was chosen as model organic pollutants to evaluate the photocatalytic activities of the Bi_2S_3/Bi_2WO_6 catalysts. Under visible light irradiation, the Bi_2S_3/Bi_2WO_6-TAA displayed the excellent visible light photoactivities compared with pure Bi_2S_3, Bi_2WO_6 and other composite photocatalysts. The efficient photocatalytic activity of the Bi_2S_3/Bi_2WO_6-TAA composite microspheres was ascribed to the constructed heterojunctions and the inner electric field caused by the exposed (020) Bi_2WO_6 facets. Active species trapping experiments revealed that h"+ and O_2·"− are the main active species in the photocatalytic process. Furthermore, the as-obtained photocatalysts showed good photocatalytic activity after four recycles. The results presented in this study provide a new concept for the rational design and development of highly efficient photocatalysts.

  14. Microstructure and thermochromic properties of VO{sub X}-WO{sub X}-VO{sub X} ceramic thin films

    Energy Technology Data Exchange (ETDEWEB)

    Khamseh, S.; Ghahari, M. [Institute for Color Science and Technology, Department of Nanomaterial and Nanocoatings, Tehran (Iran, Islamic Republic of); Araghi, H. [Islamic Azad University, Department of Materials Engineering, Science and Research Branch, Tehran (Iran, Islamic Republic of); Faghihi Sani, M.A. [Sharif University of Technology, Department of Materials Science and Engineering, Tehran (Iran, Islamic Republic of)

    2016-03-15

    W-doped VO{sub 2} films have been synthesized via oxygen annealing of V-W-V (vanadium-tungsten-vanadium) multilayered films. The effects of middle layer's thickness of V-W-V multilayered film on structure and properties of VO{sub X}-WO{sub X}-VO{sub X} ceramic thin films were investigated. The as-deposited V-W-V multilayered film showed amorphous-like structure when mixed structure of VO{sub 2} (M) and VO{sub 2} (B) was formed in VO{sub X}-WO{sub X}-VO{sub X} ceramic thin films. Tungsten content of VO{sub X}-WO{sub X}-VO{sub X} ceramic thin films increased with increasing middle layer's thickness. With increasing middle layer's thickness, room temperature square resistance (R{sub sq}) of VO{sub X}-WO{sub X}-VO{sub X} ceramic thin films increased from 65 to 86 kΩ/sq. The VO{sub X}-WO{sub X}-VO{sub X} ceramic thin film with the thinnest middle layer showed significant SMT (semiconductor-metal transition) when SMT became negligible on increasing middle layer's thickness. (orig.)

  15. Spectroscopic manifestation of trans- effect in tungsten (6) octahedral complexes

    Energy Technology Data Exchange (ETDEWEB)

    Buslaev, Yu A; Tsivadze, A Yu; Kharitonov, Yu Ya; Kokunov, Yu V; Gustyakova, M P [AN SSSR, Moscow. Inst. Obshchej i Neorganicheskoj Khimii

    1977-10-01

    The vibration spectra are studied of the following WOF/sub 4/ acetonitrile solutions in the presence of L ligands: formamide, acetamide, propioamide, butyric acid amide, dimethyl formamide, dimethyl acetamide, oxymethyl nicotinamide, diethyl nicotinamide, benzamide, salicylic acid amide, acetal acetamide, hydrorubean acid, hexamethyl phosphorus triamide, tetramethyl urea, TBP, DMSO and diethyl amine, molar ratio of WOF/sub 4/:L = 1:1. Infrared absorption spectra (400-4000 cm/sup -1/) and combination scattering spectra (50-4000 cm/sup -1/) were recorded. A decline in the vibration frequency ..nu..(WO) was caused by a lesser strength constant in the WO bond during exchange of CH/sub 3/CN for L. A slight weakening of the WO bond depending on the nature of the trans-ligands of L on the L-W-O coordinate is representative of the trans-effect of coordinated ligands in the octahedral complexes of tungsten, WOF/sub 4/xL.

  16. Physical characterization of sputter-deposited amorphous tungsten oxynitride thin films

    Energy Technology Data Exchange (ETDEWEB)

    Nunez, O.R.; Moreno Tarango, A.J. [Department of Mechanical Engineering, University of Texas at El Paso, El Paso, TX 79968 (United States); Murphy, N.R. [Air Force Research Laboratory, Materials and Manufacturing Directorate, Wright-Patterson Air Force Base (WPAFB), Dayton, OH 45433 (United States); Phinney, L.C.; Hossain, K. [Amethyst Research Inc., 123 Case Circle, Ardmore, OK 73401 (United States); Ramana, C.V., E-mail: rvchintalapalle@utep.edu [Department of Mechanical Engineering, University of Texas at El Paso, El Paso, TX 79968 (United States)

    2015-12-01

    Tungsten oxynitride (W–O–N) thin films were deposited onto silicon (100) and quartz substrates using direct current (DC) sputtering. Composition variations in the W–O–N films were obtained by varying the nitrogen gas flow rate from 0 to 20 sccm, while keeping the total gas flow constant at 40 sccm using 20 sccm of argon with the balance comprised of oxygen. The resulting crystallinity, optical properties, and chemical composition of the DC sputtered W–O–N films were evaluated. All the W–O–N films measured were shown to be amorphous using X-ray diffraction. Spectrophotometry results indicate that the optical parameters, namely, the transmission magnitude and band gap (E{sub g}), are highly dependent on the nitrogen content in the reactive gas mixture. Within the W–O–N system, E{sub g} was able to be precisely tailored between 2.9 eV and 1.9 eV, corresponding to fully stoichiometric WO{sub 3} and highly nitrided W–O–N, respectively. Rutherford backscattering spectrometry (RBS) coupled with X-ray photoelectron spectroscopy (XPS) measurements indicate that the composition of the films varies from WO{sub 3} to W–O–N composite oxynitride films. - Highlights: • W–O–N films of ~ 100 nm thick were sputter-deposited by varying nitrogen gas flow rate. • Nitrogen incorporation into W-oxide is effective at or after 9 sccm flow rate of nitrogen. • The band gap significantly decreases from ~ 3.0 eV to ~ 2.1 eV with progressive increase in nitrogen content. • A composite oxide-semiconductor of W–O–N is proposed to explain the optical properties.

  17. Three-dimensional Ag{sub 2}O/WO{sub 3}·0.33H{sub 2}O heterostructures for improving photocatalytic activity

    Energy Technology Data Exchange (ETDEWEB)

    He, Xiaoyu [Department of Applied Physics, Chongqing University, Chongqing 400044 (China); Department of Physics and Electronic Engineering, Yangtze Normal University, Chongqing 408100 (China); Hu, Chenguo, E-mail: hucg@cqu.edu.cn [Department of Applied Physics, Chongqing University, Chongqing 400044 (China); Xi, Yi; Zhang, Kaiyou; Hua, Hao [Department of Applied Physics, Chongqing University, Chongqing 400044 (China)

    2014-02-01

    Highlights: • Ag{sub 2}O/WO{sub 3}·0.33H{sub 2}O 3D network heterostructures are prepared via a simple precipitatation method. • Ag{sub 2}O/WO{sub 3}·0.33H{sub 2}O networks exhibit much enhanced photocatalytic activity. • High photocatalytic activity is attributed to its heterostructure and 3D architectures. - Abstract: Three-dimensional Ag{sub 2}O/WO{sub 3}·0.33H{sub 2}O heterostructures were fabricated by loading Ag{sub 2}O nanoparticles on WO{sub 3}·0.33H{sub 2}O 3D networks via a simple chemical precipitation method. The Ag{sub 2}O/WO{sub 3}·0.33H{sub 2}O heterostructures exhibited much enhanced photocatalytic activity for the degradation of methylene blue (MB) under simulated solar light irradiation. The optimal molar ratio of Ag{sub 2}O and WO{sub 3}·0.33H{sub 2}O is 1:2. The outstanding photocatalytic activity of the Ag{sub 2}O/WO{sub 3}·0.33H{sub 2}O can be attributed to its large surface area of the three-dimensional networks, the enhanced sunlight absorption and the prevention of electrons–holes combination from the heterostructures. The experiment result demonstrates that wide band gap semiconductor (WO{sub 3}·0.33H{sub 2}O) modified by narrow band gap metal oxide (Ag{sub 2}O) with 3D architecture will be an effective route to enhance its photocatalytic activity.

  18. Separation of tungsten and rhenium on alumina

    Directory of Open Access Journals (Sweden)

    MILOVAN SM. STOILJKOVIC

    2004-09-01

    Full Text Available The conditions for the efficient separation of tungsten(VI and rhenium (VII on alumina were established. The distribution coefficients Kd for tungstate and perrhenate anions, as well as the separation factors a (a = KdWO42-/Kd ReO4- were determined using hydrochloric or nitric acid as the aqueous media. A solution of sodium chloride in the pH range 2–6 was also examined. Under all the tested experimental conditions, alumina is a much better adsorbent for tungsten than for rhenium. The obtained results indicated that the best separation of these two elements is achieved when 0.01– 0.1 mol dm-3 HCl or 1.0 mol dm-3 HNO3 are used as the aqueous media. If NaCl is used as the aqueous phase, the best separation is achieved with 0.20 mol dm-3 NaCl, pH 4–6. Under these experimental conditions, the breakthrough and saturation capacities of alumina for tungsten at pH 4 are 17 and 26 mg W/g Al2O3, respectively. With increasing pH, these values decrease. Thus, at pH 6 they are only 4 and 13 mg W/g Al2O3, respectively.

  19. Microscopic investigations of chemo-mechanical polishing of tungsten

    International Nuclear Information System (INIS)

    Lim, Min Soo; Heide, Paul A.W. van der; Perry, Scott S.; Galloway, Heather C.; Koeck, Deborah C.

    2004-01-01

    The influence of aqueous solutions of KNO 3 , KClO 3 , and KIO 3 on tungsten surfaces has been investigated in terms of the degree of surface oxidation, metal dissolution and interfacial friction. The surface properties of tungsten films have been measured ex-situ with X-ray photoelectron spectroscopy and in situ with atomic force microscopy. Measurements of the surface composition reveal a greater degree of oxidation for surfaces treated in solutions of KIO 3 in comparison to the other solutions. This increase in surface oxidation is correlated to a greater rate of localized film dissolution that occurs under the action of the scanning probe tip. In turn, the process of material removal is the predominant origin of the higher interfacial friction measured at tungsten surfaces immersed in KIO 3 solutions, as compared to KClO 3 and KNO 3 solutions. Collectively, these measurements portray a fundamental pathway of material removal at tungsten surfaces in the presence of oxidizing species and highlight complementary roles of chemical and mechanical action

  20. Microscopic investigations of chemo-mechanical polishing of tungsten

    Energy Technology Data Exchange (ETDEWEB)

    Lim, Min Soo; Heide, Paul A.W. van der; Perry, Scott S.; Galloway, Heather C.; Koeck, Deborah C

    2004-06-15

    The influence of aqueous solutions of KNO{sub 3}, KClO{sub 3}, and KIO{sub 3} on tungsten surfaces has been investigated in terms of the degree of surface oxidation, metal dissolution and interfacial friction. The surface properties of tungsten films have been measured ex-situ with X-ray photoelectron spectroscopy and in situ with atomic force microscopy. Measurements of the surface composition reveal a greater degree of oxidation for surfaces treated in solutions of KIO{sub 3} in comparison to the other solutions. This increase in surface oxidation is correlated to a greater rate of localized film dissolution that occurs under the action of the scanning probe tip. In turn, the process of material removal is the predominant origin of the higher interfacial friction measured at tungsten surfaces immersed in KIO{sub 3} solutions, as compared to KClO{sub 3} and KNO{sub 3} solutions. Collectively, these measurements portray a fundamental pathway of material removal at tungsten surfaces in the presence of oxidizing species and highlight complementary roles of chemical and mechanical action.

  1. Effect of cathodic current density on performance of tungsten coatings on molybdenum prepared by electrodeposition in molten salt

    Science.gov (United States)

    Jiang, Fan

    2016-02-01

    Smooth tungsten coatings were prepared at current density below 70 mA cm-2 by electrodeposition on molybdenum substrate from Na2WO4-WO3 -melt at 1173 K in air atmosphere. As the current density reached up to 90 mA cm-2, many significant nodules were observed on the surface of the coating. Surface characterization, microstructure and mechanical properties were performed on the tungsten coatings. As the increasing of current density, the preferred orientation of the coatings changed to (2 0 0). All coatings exhibited columnar-grained-crystalline. There was about a 2 μm thick diffusion layer between tungsten coating and molybdenum substrate. The bending test revealed the tungsten coating had -good bonding strength with the molybdenum substrate. There is a down trend of the grain size of the coating on molybdenum as the current density increased from 30 mA cm-2 to 50 mA cm-2. The coating obtained at 50 mA cm-2 had a minimum grain size of 4.57 μm, while the microhardness of this coating reached to a maximum value of 495 HV.

  2. Facile synthesis of hierarchical double-shell WO{sub 3} microspheres with enhanced photocatalytic activity

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Zhenfeng [College of Environment and Chemical Engineering, Tianjin Polytechnic University, Tianjin 300387 (China); State Key Laboratory of Hollow-Fiber Membrane Materials and Membrane Processes, Tianjin 300387 (China); Chu, Deqing, E-mail: dqingchu@163.com [College of Environment and Chemical Engineering, Tianjin Polytechnic University, Tianjin 300387 (China); State Key Laboratory of Hollow-Fiber Membrane Materials and Membrane Processes, Tianjin 300387 (China); Wang, Limin, E-mail: wanglimin@tjpu.edu.cn [School of Materials Science and Engineering, Tianjin Polytechnic University, Tianjin 300387 (China); State Key Laboratory of Hollow-Fiber Membrane Materials and Membrane Processes, Tianjin 300387 (China); Wang, Lipeng [School of Materials Science and Engineering, Tianjin Polytechnic University, Tianjin 300387 (China); Hu, Wenhui; Chen, Xiangyu; Yang, Huifang [College of Environment and Chemical Engineering, Tianjin Polytechnic University, Tianjin 300387 (China); Sun, Jingjing [School of Materials Science and Engineering, Tianjin Polytechnic University, Tianjin 300387 (China)

    2017-02-28

    Highlights: • HDS-WO{sub 3} were fabricated via mild process. • A possible growth mechanism for HDS-WO{sub 3} is proposed. • The excellent photocatalytic activity is attributed to the larger surface area of the HDS-WO{sub 3} nanostructures. - Abstract: Hierarchical double-shell WO{sub 3} microspheres (HDS-WO{sub 3}) have been successfully obtained through the thermal decomposition of WO{sub 3}·H{sub 2}O formed by metal salts as the templates. The products were characterized by X-ray diffraction (XRD), and the morphology was investigated by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). In addition, the HDS-WO{sub 3} microspheres were analyzed by the Thermogravimetric (TG) and Brunauer-Emmett-Teller (BET) analysis. The synthetic mechanism of the products with hierarchical structures was proposed. The obtained HDS-WO{sub 3} exhibits excellent photocatalytic efficiency (84.9%), which is much higher than other WO{sub 3} sample under visible light illumination.

  3. Optical properties of WO3 thin films using surface plasmon resonance technique

    International Nuclear Information System (INIS)

    Paliwal, Ayushi; Sharma, Anjali; Gupta, Vinay; Tomar, Monika

    2014-01-01

    Indigenously assembled surface plasmon resonance (SPR) technique has been exploited to study the thickness dependent dielectric properties of WO 3 thin films. WO 3 thin films (80 nm to 200 nm) have been deposited onto gold (Au) coated glass prism by sputtering technique. The structural, optical properties and surface morphology of the deposited WO 3 thin films were studied using X-ray diffraction, UV-visible spectrophotometer, Raman spectroscopy, and Scanning electron microscopy (SEM). XRD analysis shows that all the deposited WO 3 thin films are exhibiting preferred (020) orientation and Raman data indicates that the films possess single phase monoclinic structure. SEM images reveal the variation in grain size with increase in thickness. The SPR reflectance curves of the WO 3 /Au/prism structure were utilized to estimate the dielectric properties of WO 3 thin films at optical frequency (λ = 633 nm). As the thickness of WO 3 thin film increases from 80 nm to 200 nm, the dielectric constant is seen to be decreasing from 5.76 to 3.42, while the dielectric loss reduces from 0.098 to 0.01. The estimated value of refractive index of WO 3 film is in agreement to that obtained from UV-visible spectroscopy studies. The strong dispersion in refractive index is observed with wavelength of incident laser light

  4. Surface studies of barium and barium oxide on tungsten and its application to understanding the mechanism of operation of an impregnated tungsten cathode

    Science.gov (United States)

    Forman, R.

    1976-01-01

    Surface studies have been made of multilayer and monolayer films of barium and barium oxide on a tungsten substrate. The purpose of the investigation was to synthesize the surface conditions that exist on an activated impregnated tungsten cathode and obtain a better understanding of the mechanism of operation of such cathodes. The techniques employed in these measurements were Auger spectroscopy and work-function measurements. The results of this study show that the surface of an impregnated cathode is identical to that observed for a synthesized monolayer or partial monolayer of barium on oxidized tungsten by evaluating Auger spectra and work-function measurements. Data obtained from desorption studies of barium monolayers on a tungsten substrate in conjunction with Auger and work-function results have been interpreted to show that throughout most of its life an impreganated cathode has a partial monolayer, rather than a monolayer, of barium on its surface.

  5. Biomimetic fabrication of WO3 for water splitting under visible light with high performance

    International Nuclear Information System (INIS)

    Yin, Chao; Zhu, Shenmin; Yao, Fan; Gu, Jiajun; Zhang, Wang; Chen, Zhixin; Zhang, Di

    2013-01-01

    Inspired by the high light-harvesting properties of typical butterfly wings, ceramic WO 3 butterfly wings with hierarchical structures of bio-butterfly wings was fabricated using a template of PapilioParis butterfly wings through a sol–gel method. The effect of calcination temperatures on the structures of the ceramic butterfly wings was investigated and the results showed that the WO 3 butterfly wing replica calcined at 550 °C (WO 3 replica-550) is a single phase and has a high crystallinity and relatively fine hierarchical structure. The average grain size of WO 3 replica-550 and WO 3 powder are around 32.6 and 42.2 nm, respectively. Compared with pure WO 3 powder, WO 3 replica-550 demonstrated a higher light-harvesting capability in the region from 460 to 700 nm and more importantly the higher charge separation rate, as evidenced by electron paramagnetic resonance measurements. Photocatalytic O 2 evolutions from water were investigated on the ceramic butterfly wings and pure WO 3 powder under visible light (λ > 420 nm). The results showed that the amount of O 2 produced from WO 3 replica-550 is 50 % higher than that of the pure WO 3 powder. The improved photocatalytic performance of WO 3 replica-550 is attributed to the quasi-honeycomb structure inherited from the PapilioParis butterfly wings, providing both high light-harvesting efficiency and efficient charge transport through the WO 3

  6. Preparation and characterization of nanocrystalline porous TiO2/WO3 composite thin films

    International Nuclear Information System (INIS)

    Hsu, C.-S.; Lin, C.-K.; Chan, C.-C.; Chang, C.-C.; Tsay, C.-Y.

    2006-01-01

    TiO 2 materials possessing not only photocatalytic but also electrochromic properties have attracted many research and development interests. Though WO 3 exhibits excellent electrochromic properties, the much higher cost and water-sensitivity of WO 3 as compared with the TiO 2 may restrict the practical application of WO 3 materials. In the present study, the feasibility of preparing nanocrystalline porous TiO 2 /WO 3 composite thin films was investigated. Precursors of sols TiO 2 and/or WO 3 and polystyrene microspheres were used to prepare nanocrystalline pure TiO 2 , WO 3 , and composite TiO 2 /WO 3 thin films by spin coating. The spin-coated thin films were amorphous and, after heat treating at a temperature of 500 o C, nanocrystalline TiO 2 , TiO 2 /WO 3 , and WO 3 thin films with or without pores were prepared successfully. The heat-treated thin films were colorless and coloration-bleaching phenomena can be observed during cyclic voltammetry tests. The heat-treated thin films exhibited good reversible electrochromic behavior while the porous TiO 2 /WO 3 composite film exhibited improved electrochromic properties

  7. An investigation of tungsten by neutron activation techniques

    International Nuclear Information System (INIS)

    Svetsreni, R.

    1978-01-01

    This investigation used neutron from Plutonium-Beryllium source (5 curie) to analyse the amount of tungsten in tungsten oxide which was extracted from tungsten ores, slag and tungsten alloy of tungsten iron and carbon. The technique of neutron activation analysis with NaI(Tl) gamma detector 3'' x 3'' and 1024 multichannel analyzer. The dilution technique was used by mixing Fe 2 O 3 or pure sand into the sample before irradiation. In this study self shielding effect in the analysis of tungsten was solved and the detection limit of the tungsten in the sample was about 0.5%

  8. Mechanism of anodic oxidation of molybdenum and tungsten in nitrate-nitrite melts

    International Nuclear Information System (INIS)

    Yurkinskij, V.P.; Firsova, E.G.; Morachevskij, A.G.

    1987-01-01

    The mechanism of anode oxidation of tungsten and molybdenum in NaNO 3 -KNO 3 (50 mass %) nitrate-nitrite melts with NaNO 2 -KNO 2 (0.5-50 mass %) addition and in NaNO 2 -KNO 2 (35 mole %) nitrite melt in the 516-580 K temperature range is studied. It is supposed that the process of anode dissloving of the mentioned metals in nitrite melt and nitrate-nitrite mixtures is two-electron. Formation of oxide passivating film is possible under electrolysis on the anode surface, the film is then dissolved in nitrate-nitrite melt with formation of molybdates or tungstates

  9. Advanced nanostructured photocatalysts based on reduced graphene oxide-flower-like Bi_2WO_6 composites for an augmented simulated solar photoactivity activity

    International Nuclear Information System (INIS)

    Li, Yukun; Chen, Lin; Wang, Yue; Zhu, Liang

    2016-01-01

    Highlights: • A simple route was proposed to prepare flower-like Bi_2WO_6 and RGO/Bi_2WO_6. • Cipro HCl was degraded firstly by RGO/Bi_2WO_6 under the visible-light. • 2% RGO/Bi_2WO_6 exhibited the best removal efficiency. - Abstract: A simple hydrothermal process was proposed to prepare the flower-like Bi_2WO_6 architectures, and the as-synthesized Bi_2WO_6 photocatalysts were further processed with the prepared graphene oxide (GO) to form novel reduced graphene oxide (RGO)/Bi_2WO_6 composites. The nano-materials were characterized with the help of XRD, XPS, SEM, FTIR, UV-DRS, PL techniques to investigate their morphological, physical, optical, and photochemical properties. Photocatalytic performances of the pure flower-like Bi_2WO_6 architectures and RGO/Bi_2WO_6 composites were compared and evaluated through the degradation of ciprofloxacin hydrochloride (Cipro HCl) wastewater under the simulated visible light. It was found that the RGO/Bi_2WO_6 composites displayed enhanced visible light-driven photocatalytic activities. It might be that the RGO loading not only effectively suppressed the electron–hole recombination, but also increased the light absorption ability. The effects of operating condition involved in the photocatalytic process were further examined, and the cycle-stability experiment demonstrated that as-obtained 2% RGO/Bi_2WO_6 photocatalysts had good photocatalytic repeatability.

  10. Enhanced electrochromic coloration in Ag nanoparticle decorated WO3 thin films

    International Nuclear Information System (INIS)

    Kharade, Rohini R.; Mali, Sawanta S.; Patil, Satish P.; Patil, Kashinath R.; Gang, Myong G.; Patil, Pramod S.; Kim, Jin H.; Bhosale, Popatrao N.

    2013-01-01

    Highlights: • Electrochromic WO 3 /Ag nanocomposites prepared by hybrid physico-chemical route. • XRD and XPS results confirm formation of Ag 8 W 4 O 16 phase. • WO 3 /Ag thin films showed good optical transmittance change and coloration efficiency. • SPR enhanced coloration and bleaching mechanism is well explained for electrochromism. • Color stimuli are quantified using CIE chromaticity principles. -- Abstract: WO 3 /Ag composite thin films were prepared by microwave assisted sol–gel synthesis (MW-SGS) of WO 3 followed by vacuum evaporation of Ag nanoparticles and their enhanced electrochromic coloration was investigated. The composition and morphology of WO 3 thin films with different thickness of Ag layer obtained by vacuum evaporation were investigated. Distinct plasmon absorption bands of Ag nanoparticle thin films were obtained. The optical band gap energy of WO 3 /Ag films decreased with increasing the Ag layer thickness. The surface of these films has been examined using X-ray photoelectron spectroscopy (XPS) to gain information about the chemical states of species present at surfaces. Experimental results indicated that the conductivity of the films increased after surface modification by Ag layer. To investigate the origin of enhanced electrochromic absorption in optical properties, working electrode consisting of WO 3 /Ag thin film was used and observed the optical properties during electrochemical reaction. It was found that composite electrode shows enhancement in electrochromic properties in terms of optical modulation (ΔOD) and coloration efficiency (η)

  11. Optical materials technology for energy efficiency and solar energy conversion XI: Chromogenics for smart windows; Proceedings of the Meeting, Toulouse, France, May 19, 21, 1992

    International Nuclear Information System (INIS)

    Hugot-le Goff, A.; Granqvist, C.G.; Lampert, C.M.

    1992-01-01

    The present conference discusses electrochromic tungsten oxide and nickel oxide films, electrochromic smart window devices, and thermochromic and variable light-scattering materials. Attention is given to the structural and physical properties of WO3 films prepared by CVD, the degradation of electrochromic amorphous WO3 films after coloration, the electrochromic mechanism of RF diode-sputtered nickel oxide films, and the optical and electrochemical properties of CeO2 and CeO2-TiO2 coatings. Also discussed are new solid electrolytes for electrochromic smart windows, electrochromic glazing, a smart window using a proton-conducting polymer as an electrolyte, and the electrochromism of colloidal WO3 and IrO2

  12. Thermoemission properties of tungsten with additions of rare earth oxides

    International Nuclear Information System (INIS)

    Gural'nik, N.I.; Evstifeev, V.V.; Imangulova, N.G.

    1988-01-01

    Thermoemission properties of tungsten with addition of rare earth oxides are studied in the superhigh vacuum set with oil-free pumping system. Electronic work function eφ is determined by the method of total saturation current. Temperature dependences are obtained of the work function for three types of cathodes: W+La 2 O 3 ; W+φ 2 O 3 and W+Dy 2 O 3 . It is stated, that the first two types eφ decreases approximately from 4.2 to 3.3 eV and from 4.5 to 3.8 eV, respectively, after activation at proper temperatures. These cathodes are the most effective ones at the temperature of 1700 (W+La 2 O 3 ) and 1900-2100 K (W+ φ 4 O 3 ). The work function of cathodes with addition of dysprosium oxide did not practically vary (4.55-4.3 eV) within the whole studied temperature interval (1500-2100 K)

  13. Superconductive materials. Structural mechanisms and nano-structures of some mixed skeletons oxides. Materiaux supraconducteurs. Mecanismes structuraux et nanostructures de quelques oxydes a charpentes mixtes

    Energy Technology Data Exchange (ETDEWEB)

    Hervieu, M [Caen Univ., 14 (France)

    1993-12-01

    Two families of superconductive crystals are described: the phosphate bronze of tungsten family [A[sub x](P[sub 2]O[sub 4])[sub 2](WO[sub 3])[sub 2m] or (PO[sub 2])[sub 4](WO[sub 3])[sub 2m] or A[sub x](PO[sub 2])[sub 4](WO[sub 3])[sub 2m

  14. Polymorphism of tungsten perovskite compounds Ba/sub 2/SEsub(0. 67)WO/sub 6/

    Energy Technology Data Exchange (ETDEWEB)

    Schittenhelm, H J; Kemmler-Sack, S [Tuebingen Univ. (F.R. Germany). Inst. fuer Anorganische Chemie

    1976-09-01

    The compounds Ba/sub 2/SEsub(0.67)WO/sub 6/ with SE = Gd-Lu are polymorphic. Above 1200/sup 0/C the instable cubic modification (ordered perovskite with 4 formula units Ba/sub 2/SEsub(0.67)vacantsub(0.33)WO/sub 6/ per cell) transforms irreversibly into a hexagonal modification with completely filled cationic lattice. For Ba/sub 2/Eusub(0.67)WO/sub 6/ the transformation is incomplete. With SE = Nd and Sm only the cubic modification is formed.

  15. Isolated Pt Atoms Stabilized by Amorphous Tungstenic Acid for Metal-Support Synergistic Oxygen Activation.

    Science.gov (United States)

    Zhang, Qian; Qin, Xixi; Duanmu, Fanpeng; Ji, Huiming; Shen, Zhurui; Han, Xiaopeng; Hu, Wenbin

    2018-06-05

    Oxygen activation plays a crucial role in many important chemical reactions such as organics oxidation and oxygen reduction. For developing highly active materials for oxygen activation, herein, we report an atomically dispersed Pt on WO3 nanoplates stabilized by in-situ formed amorphous H2WO4 out-layer and the mechanism for activating molecular oxygen. Experimental and theoretical studies demonstrate that the isolated Pt atoms coordinated with oxygen atoms from [WO6] and water of H2WO4, consequently leading to optimized surface electronic configuration and strong metal support interaction (SMSI). In exemplified reactions of butanone oxidation sensing and oxygen reduction, the atomic Pt/WO3 hybrid exhibits superior activity than those of Pt nanoclusters/WO3 and bare WO3 as well as enhanced long-term durability. This work will provide insight on the origin of activity and stability for atomically dispersed materials, thus promoting the development of highly efficient and durable single atom-based catalysts. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  16. Super-Nernstian pH sensors based on WO3 nanosheets

    Science.gov (United States)

    Kuo, Chao-Yin; Wang, Shui-Jinn; Ko, Rong-Ming; Tseng, Hung-Hao

    2018-04-01

    The effects of the surface morphology of hydrothermally grown WO3 nanosheets (NSs) and sputtering WO3 film on the performance of pH sensing electrodes are presented and compared in the pH range of 2–12. Using a separated electrode of an extended-gate field-effect transistor (EGFET) configuration, the WO3 nanosheet (NS) pH sensor shows a sensitivity of 63.37 mV/pH, a good linearity of 0.9973, a low voltage hysteresis of 4.79 mV, and a low drift rate of 3.18 mV/h. In contrast, the film-type one shows a typical sensitivity of only 50.08 mV/pH and a linearity of 0.9932. The super-Nernstian response could be attributed to the significant increase in the number of surface ion adsorption sites of the NS structure and the occurrence of local electric field enhancement over the sharp edges and corners of WO3 NSs.

  17. Novel Flame-Based Synthesis of Nanowires for Multifunctional Application

    Science.gov (United States)

    2015-05-13

    pattern (SAED) of SnO2/WO2.9 heterojunction for case 7. TEM (Fig. 14(a)) reveals that the coating on the tungsten- oxide nanowires is actually a...tungsten oxide nanowire,s resulting in radial growth of Zn2SnO4 nanocube/WO2.9 nanowire heterojunction . Furthermore, the combined flame and solution...SECURITY CLASSIFICATION OF: Progress for the project has been made in various areas. Specifically, we report on: (i) flame synthesis of metal- oxide

  18. Exploration on anion ordering, optical properties and electronic structure in K{sub 3}WO{sub 3}F{sub 3} elpasolite

    Energy Technology Data Exchange (ETDEWEB)

    Atuchin, V.V. [Laboratory of Optical Materials and Structures, Institute of Semiconductor Physics, SB RAS, Novosibirsk 630090 (Russian Federation); Isaenko, L.I. [Laboratory of Crystal Growth, Institute of Geology and Mineralogy, SB RAS, Novosibirsk 630090 (Russian Federation); Kesler, V.G. [Laboratory of Physical Principles for Integrated Microelectronics, Institute of Semiconductor Physics, Novosibirsk 630090 (Russian Federation); Lin, Z.S., E-mail: zslin@mail.ipc.ac.cn [Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, P.O. Box 2711, Beijing 100190 (China); Molokeev, M.S. [Laboratory of Crystal Physics, Institute of Physics, SB RAS, Krasnoyarsk 660036 (Russian Federation); Yelisseyev, A.P.; Zhurkov, S.A. [Laboratory of Crystal Growth, Institute of Geology and Mineralogy, SB RAS, Novosibirsk 630090 (Russian Federation)

    2012-03-15

    Room-temperature modification of potassium oxyfluorotungstate, G2-K{sub 3}WO{sub 3}F{sub 3}, has been prepared by low-temperature chemical route and single crystal growth. Wide optical transparency range of 0.3-9.4 {mu}m and forbidden band gap E{sub g}=4.32 eV have been obtained for G2-K{sub 3}WO{sub 3}F{sub 3} crystal. Meanwhile, its electronic structure has been calculated with the first-principles calculations. The good agreement between the theorectical and experimental results have been achieved. Furthermore, G2-K{sub 3}WO{sub 3}F{sub 3} is predicted to possess the relatively large nonlinear optical coefficients. - Graphical abstract: Using the cm-size K{sub 3}WO{sub 3}F{sub 3} crystal (left upper), the transmission spectrum (right upper) and XPS valence electronic states (left lower) were measured, agreed with the ab initio results (right lower). Highlights: Black-Right-Pointing-Pointer The cm-size G2-K{sub 3}WO{sub 3}F{sub 3} single crystals are obtained. Black-Right-Pointing-Pointer Optical absorption edge and transmission range are defined for G2-K{sub 3}WO{sub 3}F{sub 3} crystal. Black-Right-Pointing-Pointer Crystal structures of all known K{sub 3}WO{sub 3}F{sub 3} polymorph modifications are determined. Black-Right-Pointing-Pointer Experimental electronic structure is consistent with the first-principles result. Black-Right-Pointing-Pointer G2-K{sub 3}WO{sub 3}F{sub 3} is predicted as a crystal with large NLO coefficients.

  19. Electrochromic and electrochemical capacitive properties of tungsten oxide and its polyaniline nanocomposite films obtained by chemical bath deposition method

    CSIR Research Space (South Africa)

    Nwanya, AC

    2014-05-01

    Full Text Available Polyanine and its nanocomposite WO3/PANI films were deposited on fluorine doped tin oxide (FTO) glassslides by simple chemical bath deposition method. The morphology structure of the composite film wasstudied using atomic force microscopy (AFM...

  20. Efficient room temperature oxidation of cyclohexane over highly active hetero-mixed WO3/V2O5 oxide catalyst

    CSIR Research Space (South Africa)

    Makgwane, PR

    2014-09-01

    Full Text Available catalytic activity to initiate the free-radical oxyfunctionalization of cyclohexane to afford up to 90% conversions within 6 h. The KA selectivity was found to depend on reaction time and the amount of catalyst. The WO(sub3)/V(sub2)O(sub5) catalyst...

  1. Mechanism of the electrochemical hydrogen reaction on smooth tungsten carbide and tungsten electrodes

    International Nuclear Information System (INIS)

    Wiesener, K.; Winkler, E.; Schneider, W.

    1985-01-01

    The course of the electrochemical hydrogen reaction on smooth tungsten-carbide electrodes in hydrogen saturated 2.25 M H 2 SO 4 follows a electrochemical sorption-desorption mechanism in the potential range of -0.4 to +0.1 V. At potentials greater than +0.1 V the hydrogen oxidation is controlled by a preliminary chemical sorption step. Concluding from the similar behaviour of tungsten-carbide and tungsten electrodes after cathodic pretreatment, different tungsten oxides should be involved in the course of the hydrogen reaction on tungsten carbide electrodes. (author)

  2. Optical properties of WO{sub 3} thin films using surface plasmon resonance technique

    Energy Technology Data Exchange (ETDEWEB)

    Paliwal, Ayushi; Sharma, Anjali; Gupta, Vinay, E-mail: drguptavinay@gmail.com, E-mail: vgupta@physics.du.ac.in [Department of Physics and Astrophysics, University of Delhi, Delhi 110007 (India); Tomar, Monika [Department of Physics, Miranda House, University of Delhi, Delhi 110007 (India)

    2014-01-28

    Indigenously assembled surface plasmon resonance (SPR) technique has been exploited to study the thickness dependent dielectric properties of WO{sub 3} thin films. WO{sub 3} thin films (80 nm to 200 nm) have been deposited onto gold (Au) coated glass prism by sputtering technique. The structural, optical properties and surface morphology of the deposited WO{sub 3} thin films were studied using X-ray diffraction, UV-visible spectrophotometer, Raman spectroscopy, and Scanning electron microscopy (SEM). XRD analysis shows that all the deposited WO{sub 3} thin films are exhibiting preferred (020) orientation and Raman data indicates that the films possess single phase monoclinic structure. SEM images reveal the variation in grain size with increase in thickness. The SPR reflectance curves of the WO{sub 3}/Au/prism structure were utilized to estimate the dielectric properties of WO{sub 3} thin films at optical frequency (λ = 633 nm). As the thickness of WO{sub 3} thin film increases from 80 nm to 200 nm, the dielectric constant is seen to be decreasing from 5.76 to 3.42, while the dielectric loss reduces from 0.098 to 0.01. The estimated value of refractive index of WO{sub 3} film is in agreement to that obtained from UV-visible spectroscopy studies. The strong dispersion in refractive index is observed with wavelength of incident laser light.

  3. Efficient tungsten oxide/bismuth oxyiodide core/shell photoanode for photoelectrochemical water splitting

    Science.gov (United States)

    Ma, Haipeng; Zhang, Jing; Liu, Zhifeng

    2017-11-01

    The novel WO3 nanorods (NRs)/BiOI core/shell structure composite is used as an efficient photoanode applied in photoelectrochemical (PEC) water splitting for the first time. It is synthesized via facile hydrothermal method and, successive ionic layer adsorption and reaction (SILAR) process. This facile synthesis route can achieve uniform WO3/BiOI core/shell composite nanostructures and obtain varied BiOI morphologies simultaneously. The WO3 NRs/BiOI-20 composite exhibits enhanced PEC activity compared to pristine WO3 with a photocurrent density of 0.79 mA cm-2 measured at 0.8 V vs. RHE under AM 1.5G. This excellent performance benefits from the broader absorption spectrum and suppressed electron-hole recombination. This novel core/shell composite may provide insight in developing more efficient solar driven photoelectrodes.

  4. Spin coated versus dip coated electrochromic tungsten oxide films: Structure, morphology, optical and electrochemical properties

    International Nuclear Information System (INIS)

    Deepa, M.; Saxena, T.K.; Singh, D.P.; Sood, K.N.; Agnihotry, S.A.

    2006-01-01

    A sol-gel derived acetylated peroxotungstic acid sol encompassing 4 wt.% of oxalic acid dihydrate (OAD) has been employed for the deposition of tungsten oxide (WO 3 ) films by spin coating and dip coating techniques, in view of smart window applications. The morphological and structural evolution of the as-deposited spin and dip coated films as a function of annealing temperature (250 and 500 o C) has been examined and compared by Fourier transform infrared (FT-IR) spectroscopy, scanning electron microscopy (SEM) and X-ray diffraction (XRD). A conspicuous feature of the dip coated film (annealed at 250 o C) is that its electrochromic and electrochemical properties ameliorate with cycling without degradation in contrast to the spin coated film for which these properties deteriorate under repetitive cycling. A comparative study of spin and dip coated nanostructured thin films (annealed at 250 o C) revealed a superior performance for the cycled dip coated film in terms of higher transmission modulation and coloration efficiency in solar and photopic regions, faster switching speed, higher electrochemical activity as well as charge storage capacity. While the dip coated film could endure 2500 color-bleach cycles, the spin coated film could sustain only a 1000 cycles. The better cycling stability of the dip coated film which is a repercussion of a balance between optimal water content, porosity and grain size hints at its potential for electrochromic window applications

  5. Hexagonal nanorods of tungsten trioxide: Synthesis, structure, electrochemical properties and activity as supporting material in electrocatalysis

    International Nuclear Information System (INIS)

    Salmaoui, Samiha; Sediri, Faouzi; Gharbi, Neji; Perruchot, Christian; Aeiyach, Salah; Rutkowska, Iwona A.; Kulesza, Pawel J.; Jouini, Mohamed

    2011-01-01

    Tungsten trioxide, unhydrated with hexagonal structure (h-WO 3 ), has been prepared by hydrothermal method at a temperature of 180 o C in acidified sodium tungstate solution. Thus prepared h-WO 3 has been characterized by X-ray diffraction (XRD) method and using electrochemical techniques. The morphology has been examined by scanning and transmission electron microscopies (SEM and TEM) and it is consistent with existence of nanorods of 50-70 nm diameter and up to 5 μm length. Cyclic voltammetric characterization of thin films of h-WO 3 nanorods has revealed reversible redox behaviour with charge-discharge cycling corresponding to the reversible lithium intercalation/deintercalation into the crystal lattice of the h-WO 3 nanorods. In propylene carbonate containing LiClO 4 , two successive redox processes of hexagonal WO 3 nanorods are observed at the scan rate of 50 mV/s. Such behaviour shall be attributed to the presence of at least two W atoms of different surroundings in the lattice structure of h-WO 3 nanorods. On the other hand, in aqueous LiClO 4 solution, only one redox process is observed at the scan rate of 10 mV/s. The above observations can be explained in terms of differences in the diffusion of ions inside two types of channel cavities existing in the structure of the h-WO 3 nanorods. Moreover, the material can be applied as active support for the catalytic bi-metallic Pt-Ru nanoparticles during electrooxidation of ethanol in acid medium (0.5 mol dm -3 H 2 SO 4 ).

  6. Hexagonal nanorods of tungsten trioxide: Synthesis, structure, electrochemical properties and activity as supporting material in electrocatalysis

    Science.gov (United States)

    Salmaoui, Samiha; Sediri, Faouzi; Gharbi, Néji; Perruchot, Christian; Aeiyach, Salah; Rutkowska, Iwona A.; Kulesza, Pawel J.; Jouini, Mohamed

    2011-07-01

    Tungsten trioxide, unhydrated with hexagonal structure (h-WO 3), has been prepared by hydrothermal method at a temperature of 180 °C in acidified sodium tungstate solution. Thus prepared h-WO 3 has been characterized by X-ray diffraction (XRD) method and using electrochemical techniques. The morphology has been examined by scanning and transmission electron microscopies (SEM and TEM) and it is consistent with existence of nanorods of 50-70 nm diameter and up to 5 μm length. Cyclic voltammetric characterization of thin films of h-WO 3 nanorods has revealed reversible redox behaviour with charge-discharge cycling corresponding to the reversible lithium intercalation/deintercalation into the crystal lattice of the h-WO 3 nanorods. In propylene carbonate containing LiClO 4, two successive redox processes of hexagonal WO 3 nanorods are observed at the scan rate of 50 mV/s. Such behaviour shall be attributed to the presence of at least two W atoms of different surroundings in the lattice structure of h-WO 3 nanorods. On the other hand, in aqueous LiClO 4 solution, only one redox process is observed at the scan rate of 10 mV/s. The above observations can be explained in terms of differences in the diffusion of ions inside two types of channel cavities existing in the structure of the h-WO 3 nanorods. Moreover, the material can be applied as active support for the catalytic bi-metallic Pt-Ru nanoparticles during electrooxidation of ethanol in acid medium (0.5 mol dm -3 H 2SO 4).

  7. Quasi physisorptive two dimensional tungsten oxide nanosheets with extraordinary sensitivity and selectivity to NO2.

    Science.gov (United States)

    Khan, Hareem; Zavabeti, Ali; Wang, Yichao; Harrison, Christopher J; Carey, Benjamin J; Mohiuddin, Md; Chrimes, Adam F; De Castro, Isabela Alves; Zhang, Bao Yue; Sabri, Ylias M; Bhargava, Suresh K; Ou, Jian Zhen; Daeneke, Torben; Russo, Salvy P; Li, Yongxiang; Kalantar-Zadeh, Kourosh

    2017-12-14

    Attributing to their distinct thickness and surface dependent physicochemical properties, two dimensional (2D) nanostructures have become an area of increasing interest for interfacial interactions. Effectively, properties such as high surface-to-volume ratio, modulated surface activities and increased control of oxygen vacancies make these types of materials particularly suitable for gas-sensing applications. This work reports a facile wet-chemical synthesis of 2D tungsten oxide nanosheets by sonication of tungsten particles in an acidic environment and thermal annealing thereafter. The resultant product of large nanosheets with intrinsic substoichiometric properties is shown to be highly sensitive and selective to nitrogen dioxide (NO 2 ) gas, which is a major pollutant. The strong synergy between polar NO 2 molecules and tungsten oxide surface and also abundance of active surface sites on the nanosheets for molecule interactions contribute to the exceptionally sensitive and selective response. An extraordinary response factor of ∼30 is demonstrated to ultralow 40 parts per billion (ppb) NO 2 at a relatively low operating temperature of 150 °C, within the physisorption temperature band for tungsten oxide. Selectivity to NO 2 is demonstrated and the theory behind it is discussed. The structural, morphological and compositional characteristics of the synthesised and annealed materials are extensively characterised and electronic band structures are proposed. The demonstrated 2D tungsten oxide based sensing device holds the greatest promise for producing future commercial low-cost, sensitive and selective NO 2 gas sensors.

  8. Process for recovering tungsten from alkaline leaching solution of tungsten ores

    International Nuclear Information System (INIS)

    Onozaki, S.; Nemoto, S.; Hazeyama, T.

    1976-01-01

    This invention relates to a process for recovering tungsten from an alkaline leaching solution of tungsten ores. This invention comprises adjusting the pH of an alkaline leaching solution which is obtained by lixiviating ore containing tungsten with an alkaline solution to 7--8 with acid to oxidize molybdic acid ions in the solution, adding a sulfide donor, then precipitating molybdenum sulfide compounds by adjusting the pH value of the solution to 2--3. Tungstic acid ions are recovered as calcium tungstate by the addition of a calcium ion donor after the molybdenum sulfide compounds are separated

  9. Oxidation behaviour of silicon-free tungsten alloys for use as the first wall material

    Science.gov (United States)

    Koch, F.; Brinkmann, J.; Lindig, S.; Mishra, T. P.; Linsmeier, Ch

    2011-12-01

    The use of self-passivating tungsten alloys as armour material of the first wall of a fusion power reactor may be advantageous concerning safety issues. In earlier studies good performance of the system W-Cr-Si was demonstrated. Thin films of such alloys showed a strongly reduced oxidation rate compared to pure tungsten. However, the formation of brittle tungsten silicides may be disadvantageous for the powder metallurgical production of bulk W-Cr-Si alloys if a good workability is needed. This paper shows the results of screening tests to identify suitable silicon-free alloys with distinguished self-passivation and a potentially good workability. Of all the tested systems W-Cr-Ti alloys showed the most promising results. The oxidation rate was even lower than the one of W-Cr-Si alloys, the reduction factor was about four orders of magnitude compared to pure tungsten. This performance could be conserved even if the content of alloying elements was reduced.

  10. Oxidation behaviour of silicon-free tungsten alloys for use as the first wall material

    International Nuclear Information System (INIS)

    Koch, F; Brinkmann, J; Lindig, S; Mishra, T P; Linsmeier, Ch

    2011-01-01

    The use of self-passivating tungsten alloys as armour material of the first wall of a fusion power reactor may be advantageous concerning safety issues. In earlier studies good performance of the system W-Cr-Si was demonstrated. Thin films of such alloys showed a strongly reduced oxidation rate compared to pure tungsten. However, the formation of brittle tungsten silicides may be disadvantageous for the powder metallurgical production of bulk W-Cr-Si alloys if a good workability is needed. This paper shows the results of screening tests to identify suitable silicon-free alloys with distinguished self-passivation and a potentially good workability. Of all the tested systems W-Cr-Ti alloys showed the most promising results. The oxidation rate was even lower than the one of W-Cr-Si alloys, the reduction factor was about four orders of magnitude compared to pure tungsten. This performance could be conserved even if the content of alloying elements was reduced.

  11. Biomimetic fabrication of WO{sub 3} for water splitting under visible light with high performance

    Energy Technology Data Exchange (ETDEWEB)

    Yin, Chao; Zhu, Shenmin, E-mail: smzhu@sjtu.edu.cn; Yao, Fan; Gu, Jiajun; Zhang, Wang [Shanghai Jiao Tong University, State Key Laboratory of Metal Matrix Composites (China); Chen, Zhixin [University of Wollongong, Faculty of Engineering (Australia); Zhang, Di, E-mail: zhangdi@sjtu.edu.cn [Shanghai Jiao Tong University, State Key Laboratory of Metal Matrix Composites (China)

    2013-08-15

    Inspired by the high light-harvesting properties of typical butterfly wings, ceramic WO{sub 3} butterfly wings with hierarchical structures of bio-butterfly wings was fabricated using a template of PapilioParis butterfly wings through a sol-gel method. The effect of calcination temperatures on the structures of the ceramic butterfly wings was investigated and the results showed that the WO{sub 3} butterfly wing replica calcined at 550 Degree-Sign C (WO{sub 3} replica-550) is a single phase and has a high crystallinity and relatively fine hierarchical structure. The average grain size of WO{sub 3} replica-550 and WO{sub 3} powder are around 32.6 and 42.2 nm, respectively. Compared with pure WO{sub 3} powder, WO{sub 3} replica-550 demonstrated a higher light-harvesting capability in the region from 460 to 700 nm and more importantly the higher charge separation rate, as evidenced by electron paramagnetic resonance measurements. Photocatalytic O{sub 2} evolutions from water were investigated on the ceramic butterfly wings and pure WO{sub 3} powder under visible light ({lambda} > 420 nm). The results showed that the amount of O{sub 2} produced from WO{sub 3} replica-550 is 50 % higher than that of the pure WO{sub 3} powder. The improved photocatalytic performance of WO{sub 3} replica-550 is attributed to the quasi-honeycomb structure inherited from the PapilioParis butterfly wings, providing both high light-harvesting efficiency and efficient charge transport through the WO{sub 3}.

  12. Domain structures of sodium tungsten bronzes, Na/sub x/WO/sub 3/ (0. 4 < x < 1)

    Energy Technology Data Exchange (ETDEWEB)

    Atoji, M

    1978-01-01

    Optical-microscope observations with polarized light have shown that the birefringent, twin-domain structure of sodium tungsten bronzes is exhibited by Na-deficient, epitaxial surface films and hence is not a bulk property as had been suggested elsewhere. The film is translucent, 10/sup -2/ - 10/sup -3/ mm thick or less, and often laminates to a multi-film layer. The domain boundaries are sensitive to lateral stress and, apparently, to minute changes in the substrate structure. These and related properties of the film and the substrate are presented.

  13. Advanced tungsten materials for plasma-facing components of DEMO and fusion power plants

    International Nuclear Information System (INIS)

    Neu, R.; Riesch, J.; Coenen, J.W.; Brinkmann, J.; Calvo, A.; Elgeti, S.; García-Rosales, C.; Greuner, H.; Hoeschen, T.; Holzner, G.; Klein, F.; Koch, F.

    2016-01-01

    Highlights: • Development of W-fibre enhanced W-composites incorporating extrinsic toughening mechanisms. • Production of a large sample (more than 2000 long fibres) for mechanical and thermal testing. • Even in a fully embrittled state, toughening mechanisms are still effective. • Emissions of volatile W-oxides can be suppressed by alloying W with elements forming stable oxides. • WCr10Ti2 has been successfully tested under accidental conditions and high heat fluxes. - Abstract: Tungsten is the major candidate material for the armour of plasma facing components in future fusion devices. To overcome the intrinsic brittleness of tungsten, which strongly limits its operational window, a W-fibre enhanced W-composite material (W_f/W) has been developed incorporating extrinsic toughening mechanisms. Small W_f/W samples show a large increase in toughness. Recently, a large sample (50 mm × 50 mm × 3 mm) with more than 2000 long fibres has been successfully produced allowing further mechanical and thermal testing. It could be shown that even in a fully embrittled state, toughening mechanisms as crack bridging by intact fibres, as well as the energy dissipation by fibre-matrix interface debonding and crack deflection are still effective. A potential problem with the use of pure W in a fusion reactor is the formation of radioactive and highly volatile WO_3 compounds and their potential release under accidental conditions. It has been shown that the oxidation of W can be strongly suppressed by alloying with elements forming stable oxides. WCr10Ti2 alloy has been produced on a technical scale and has been successfully tested in the high heat flux test facility GLADIS. Recently, W-Cr-Y alloys have been produced on a lab-scale. They seem to have even improved properties compared to the previously investigated W alloys.

  14. Advanced tungsten materials for plasma-facing components of DEMO and fusion power plants

    Energy Technology Data Exchange (ETDEWEB)

    Neu, R., E-mail: Rudolf.Neu@ipp.mpg.de [Max-Planck-Institut für Plasmaphysik, D-85748 Garching (Germany); Fakultät für Maschinenbau, Technische Universität München, D-85748 Garching (Germany); Riesch, J. [Max-Planck-Institut für Plasmaphysik, D-85748 Garching (Germany); Coenen, J.W. [Forschungszentrum Jülich GmbH, Institut für Energie- und Klimaforschung – Plasmaphysik, D-52425 Jülich (Germany); Brinkmann, J. [Max-Planck-Institut für Plasmaphysik, D-85748 Garching (Germany); Forschungszentrum Jülich GmbH, Institut für Energie- und Klimaforschung – Plasmaphysik, D-52425 Jülich (Germany); Calvo, A. [CEIT and Tecnun (University of Navarra), E-20018 San Sebastian (Spain); Elgeti, S. [Max-Planck-Institut für Plasmaphysik, D-85748 Garching (Germany); García-Rosales, C. [CEIT and Tecnun (University of Navarra), E-20018 San Sebastian (Spain); Greuner, H.; Hoeschen, T.; Holzner, G. [Max-Planck-Institut für Plasmaphysik, D-85748 Garching (Germany); Klein, F. [Forschungszentrum Jülich GmbH, Institut für Energie- und Klimaforschung – Plasmaphysik, D-52425 Jülich (Germany); Koch, F. [Max-Planck-Institut für Plasmaphysik, D-85748 Garching (Germany); and others

    2016-11-01

    Highlights: • Development of W-fibre enhanced W-composites incorporating extrinsic toughening mechanisms. • Production of a large sample (more than 2000 long fibres) for mechanical and thermal testing. • Even in a fully embrittled state, toughening mechanisms are still effective. • Emissions of volatile W-oxides can be suppressed by alloying W with elements forming stable oxides. • WCr10Ti2 has been successfully tested under accidental conditions and high heat fluxes. - Abstract: Tungsten is the major candidate material for the armour of plasma facing components in future fusion devices. To overcome the intrinsic brittleness of tungsten, which strongly limits its operational window, a W-fibre enhanced W-composite material (W{sub f}/W) has been developed incorporating extrinsic toughening mechanisms. Small W{sub f}/W samples show a large increase in toughness. Recently, a large sample (50 mm × 50 mm × 3 mm) with more than 2000 long fibres has been successfully produced allowing further mechanical and thermal testing. It could be shown that even in a fully embrittled state, toughening mechanisms as crack bridging by intact fibres, as well as the energy dissipation by fibre-matrix interface debonding and crack deflection are still effective. A potential problem with the use of pure W in a fusion reactor is the formation of radioactive and highly volatile WO{sub 3} compounds and their potential release under accidental conditions. It has been shown that the oxidation of W can be strongly suppressed by alloying with elements forming stable oxides. WCr10Ti2 alloy has been produced on a technical scale and has been successfully tested in the high heat flux test facility GLADIS. Recently, W-Cr-Y alloys have been produced on a lab-scale. They seem to have even improved properties compared to the previously investigated W alloys.

  15. Highly flexible sub-1 nm tungsten oxide nanobelts as efficient desulfurization catalysts.

    Science.gov (United States)

    He, Jie; Liu, Huiling; Xu, Biao; Wang, Xun

    2015-03-01

    Ultrathin tungsten oxide nanobelts are successfully synthesized via a facile solvothermal method. Sub-1 nm thickness and hydrophobic surface property endow the nanobelts with flexibility, viscosity, gelation, and good catalytic performance in oxidative desulfurization. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  16. Red photoluminescent property and modification of WO3:Eu3+ inverse opal for blue light converted LEDs

    Science.gov (United States)

    Ruan, Jiufeng; Yang, Zhengwen; Huang, Anjun; Chai, Zhuangzhuang; Qiu, Jianbei; Song, Zhiguo

    2018-01-01

    Blue light converted light-emitting diodes is of great significance as a candidate for next generation lighting. In this work, the WO3:Eu3+ inverse opal photonic crystals were prepared and their luminescence properties were studied. The results demonstrated that the main excitation peak of WO3:Eu3+ inverse opals were located at 465 nm. The red luminescence peak at the 613 nm was observed in the WO3:Eu3+ inverse opal upon 465 nm excitation, exhibiting better red color purity. The influence of photonic band gap on the photoluminescence of WO3:Eu3+ inverse opal was obtained. When the red luminescence peak is in the regions of the photonic band gap and the edge of the band-gap, the red luminescence suppression and enhancement was observed respectively. The WO3:Eu3+ inverse opals may be a promising candidate for the blue light converted LEDs.

  17. The effect of electrostatic field on the rate of metal vaporization

    International Nuclear Information System (INIS)

    Tsirlin, M.S.; Lyubimov, V.D.; Krasovskij, A.I.

    1982-01-01

    Evaporation kinetics of molybdenum and tungsten filaments 30 and 80 μm in diameter, when vacuum constitutes 1.3x10 -1 -1.3x10 -3 Pa, the temperature is 1470 K for tungsten and 1270-1670 K for Mo and intensity is E=10 7 -10 8 V/m, has been measured. In supposition of evaporation of oxide mole-- cules from metal surface the density of molecule current of (MoO 3 ) 3 and (WO 3 ) 3 over solid (MoO 3 ) 3 and (WO 3 ) 3 is determined. It is established that the rate of molecule removal from the filament under the effect of heterogeneous electric field increases with the increase of dipole momentum of (WO 3 ) 3 and (MoO 3 ) 3 , the value of field intensity and with metal temperature decrease

  18. Electrocatalytic Performance of Carbon Supported WO3-Containing Pd–W Nanoalloys for Oxygen Reduction Reaction in Alkaline Media

    Directory of Open Access Journals (Sweden)

    Nan Cui

    2018-05-01

    Full Text Available In this paper, we report that WOx containing nanoalloys exhibit stable electrocatalytic performance in alkaline media, though bulk WO3 is easy to dissolve in NaOH solution. Carbon supported oxide-rich Pd–W alloy nanoparticles (PdW/C with different Pd:W atom ratios were prepared by the reduction–oxidation method. Among the catalysts, the oxide-rich Pd0.8W0.2/C (Pd/W = 8:2, atom ratio exhibits the highest catalytic activity for the oxygen reduction reaction. The X-ray photoelectron spectroscopy data shows that ~40% of Pd atoms and ~60% of the W atoms are in their oxide form. The Pd 3d5/2 binding energy of the oxide-rich Pd–W nanoalloys is higher than that of Pd/C, indicating the electronic structure of Pd is affected by the strong interaction between Pd and W/WO3. Compare to Pd/C, the onset potential of the oxygen reduction reaction at the oxide-rich Pd0.8W0.2/C shifts to a higher potential. The current density (mA·mg Pd−1 at the oxide-rich Pd0.8W0.2/C is ~1.6 times of that at Pd/C. The oxide-rich Pd0.8W0.2/C also exhibits higher catalytic stability than Pd/C, which demonstrates that it is a prospective candidate for the cathode of fuel cells operating with alkaline electrolyte.

  19. Tungsten phosphanylarylthiolato complexes [W{PhP(2-SC6H4)2-kappa3S,S',P} 2] and [W{P(2-SC6H4)3-kappa4S,S',S",P}2]: synthesis, structures and redox chemistry.

    Science.gov (United States)

    Hildebrand, Alexandra; Lönnecke, Peter; Silaghi-Dumitrescu, Luminita; Hey-Hawkins, Evamarie

    2008-09-14

    PhP(2-SHC6H4)2 (PS2H2) reacts with WCl6 with reduction of tungsten to give the air-sensitive tungsten(IV) complex [W{PhP(2-SC6H4)2-kappa(3)S,S',P}2] (1). 1 is oxidised in air to [WO{PhPO(2-SC6H4)2-kappa(3)S,S',O}{PhP(2-SC6H4)2-kappa(3)S,S',P}] (2). The attempted synthesis of 2 by reaction of 1 with iodosobenzene as oxidising agent was unsuccessful. [W{P(2-SC6H4)3-kappa(4)S,S',S",P}2] (3) was formed in the reaction of P(2-SHC6H4)3 (PS3H3) with WCl6. The W(VI) complex 3 contains two PS3(3-) ligands, each coordinated in a tetradentate fashion resulting in a tungsten coordination number of eight. The reaction of 3 with AgBF4 yields the dinuclear tungsten complex [W2{P(2-SC6H4)3-kappa(4)S,S',S",P}3]BF4 (4). Complexes 1-4 were characterised by spectral methods and X-ray structure determination.

  20. Bi-component semiconductor oxide photoanodes for the photoelectrocatalytic oxidation of organic solutes and vapours: a short review with emphasis to TiO2-WO3 photoanodes.

    Science.gov (United States)

    Georgieva, J; Valova, E; Armyanov, S; Philippidis, N; Poulios, I; Sotiropoulos, S

    2012-04-15

    The use of binary semiconductor oxide anodes for the photoelectrocatalytic oxidation of organic species (both in solution and gas phase) is reviewed. In the first part of the review, the principle of electrically assisted photocatalysis is presented, the preparation methods for the most common semiconductor oxide catalysts are briefly mentioned, while the advantages of appropriately chosen semiconductor combinations for efficient UV and visible (vis) light utilization are highlighted. The second part of the review focuses on the discussion of TiO(2)-WO(3) photoanodes (among the most studied bi-component semiconductor oxide systems) and in particular on coatings prepared by electrodeposition/electrosynthesis or powder mixtures (the focus of the authors' research during recent years). Studies concerning the microscopic, spectroscopic and photoelectrochemical characterization of the catalysts are presented and examples of photoanode activity towards typical dissolved organic contaminants as well as organic vapours are given. Particular emphasis is paid to: (a) The dependence of photoactivity on catalyst morphology and composition and (b) the possibility of carrying out photoelectrochemistry in all-solid cells, thus opening up the opportunity for photoelectrocatalytic air treatment. Copyright © 2011 Elsevier B.V. All rights reserved.

  1. Nitridation of one-dimensional tungsten oxide nanostructures: Changes in structure and photoactivity

    KAUST Repository

    Varga, Tamás

    2017-10-12

    In the search for stable, visible light active photoelectrodes, hydrothermally synthesized tungsten oxide nanowires were modified via nitrogen incorporation into their structure. To this end, nanowires were heat-treated in ammonia/nitrogen atmosphere at different temperatures. This procedure caused transitions in their structure that were investigated along with the photoelectrochemical properties of the samples. Results were subsequently compared to the reference samples treated in inert nitrogen atmosphere. Morphological changes and structural transitions were followed by transmission and scanning electron microscopy and X-ray diffraction. Bandgap energies were determined from the UV–vis spectra of the materials, while photoelectrochemical properties were tested by linear sweep photovoltammetry and electrochemical impedance spectroscopy. Pristine tungsten oxide nanowires were first transformed into tungsten oxynitride and then tungsten nitride during high-temperature calcination in ammonia atmosphere. Electron microscopic investigation revealed that, along with phase transition, the initial fibrous morphology gradually converted into nanosheets. Simultaneously, bandgap energies significantly decreased in the calcination process, too. Photoelectrochemical measurements demonstrated that photoactivity in the treated samples was not improved by the decrease of the bandgap. This behavior might be explained with the deterioration of charge carrier transport properties of the materials due to the increased number of structural defects (acting as trap states), and current ongoing work aims to verify this notion.

  2. Investigation of the La2O3-Nb2O5-WO3 ternary phase diagram: Isolation and crystal structure determination of the original La3NbWO10 material

    KAUST Repository

    Vu, T.D.; Vu, T.D.; Barre, M.; Adil, Karim; Jouanneaux, A.; Suard, E.; Goutenoire, F.

    2015-01-01

    In the course of the exploration of the La2O3-WO3-Nb2O5 ternary phase diagram, a new compound with the formula La3NbWO10 was discovered. Its structure was determined from a combination of powder X-ray and neutron diffraction data. It crystallizes

  3. Tritium Decay Helium-3 Effects in Tungsten

    Energy Technology Data Exchange (ETDEWEB)

    Shimada, M. [Idaho National Lab. (INL), Idaho Falls, ID (United States); Merrill, B. J. [Idaho National Lab. (INL), Idaho Falls, ID (United States)

    2016-06-01

    A critical challenge for long-term operation of ITER and beyond to a Demonstration reactor (DEMO) and future fusion reactor will be the development of plasma-facing components (PFCs) that demonstrate erosion resistance to steady-state/transient heat fluxes and intense neutral/ion particle fluxes under the extreme fusion nuclear environment, while at the same time minimizing in-vessel tritium inventories and permeation fluxes into the PFC’s coolant. Tritium will diffuse in bulk tungsten at elevated temperatures, and can be trapped in radiation-induced trap site (up to 1 at. % T/W) in tungsten [1,2]. Tritium decay into helium-3 may also play a major role in microstructural evolution (e.g. helium embrittlement) in tungsten due to relatively low helium-4 production (e.g. He/dpa ratio of 0.4-0.7 appm [3]) in tungsten. Tritium-decay helium-3 effect on tungsten is hardly understood, and its database is very limited. Two tungsten samples (99.99 at. % purity from A.L.M.T. Co., Japan) were exposed to high flux (ion flux of 1.0x1022 m-2s-1 and ion fluence of 1.0x1026 m-2) 0.5%T2/D2 plasma at two different temperatures (200, and 500°C) in Tritium Plasma Experiment (TPE) at Idaho National Laboratory. Tritium implanted samples were stored at ambient temperature in air for more than 3 years to investigate tritium decay helium-3 effect in tungsten. The tritium distributions on plasma-exposed was monitored by a tritium imaging plate technique during storage period [4]. Thermal desorption spectroscopy was performed with a ramp rate of 10°C/min up to 900°C to outgas residual deuterium and tritium but keep helium-3 in tungsten. These helium-3 implanted samples were exposed to deuterium plasma in TPE to investigate helium-3 effect on deuterium behavior in tungsten. The results show that tritium surface concentration in 200°C sample decreased to 30 %, but tritium surface concentration in 500°C sample did not alter over the 3 years storage period, indicating possible tritium

  4. The ITO-capped WO3 nanowires biosensor based on field-effect transistor in label-free protein sensing

    International Nuclear Information System (INIS)

    Shariati, Mohsen

    2017-01-01

    The fabrication of ITO-capped WO 3 nanowires associated with their bio-sensing properties in field-effect transistor diagnostics basis as a biosensor has been reported. The bio-sensing property for manipulated nanowires elucidated that the grown nanostructures were very sensitive to protein. The ITO-capped WO 3 nanowires biosensor showed an intensive bio-sensing activity against reliable protein. Polylysine strongly charged bio-molecule was applied as model system to demonstrate the implementation of materialized biosensor. The employed sensing mechanism was 'label-free' and depended on bio-molecule's intrinsic charge. For nanowires synthesis, the vapor-liquid-solid mechanism was used. Nanowires were beyond a few hundred nanometers in lengths and around 15-20 nm in diameter, while the globe cap's size on the nanowires was around 15-25 nm. The indium tin oxide (ITO) played as catalyst in nanofabrication for WO 3 nanowires growth and had outstanding role in bio-sensing especially for bio-molecule adherence. In applied electric field presence, the fabricated device showed the great potential to enhance medical diagnostics. (orig.)

  5. Study on single step solid state synthesis of WC@C nanocomposite and electrochemical stability of synthesized WC@C & Pt/WC@C for alcohol oxidation (methanol/ethanol)

    Energy Technology Data Exchange (ETDEWEB)

    Singla, Gourav, E-mail: gsinghla@gmail.com; Singh, K., E-mail: kusingh@thapar.edu; Pandey, O.P., E-mail: oppandey@thapar.edu

    2016-04-25

    WC@C nano composite was prepared by a single step solid–state reaction through in situ reduction and carburization of WO{sub 3} in the presence of Mg and activated charcoal. The XRD results and thermodynamics analysis showed that the optimization of reaction temperature facilitates the reduction as well as carburization of tungsten oxide(s) at different reaction temperature. Thermogravimetric analysis of the product was done to assess the thermal stability in air. The Raman spectroscopy was used to find out the nature (amorphous/graphitic) of carbon in the obtained phase. The N{sub 2} adsorption–desorption measurement showed a narrow pore size distribution from 3 to 4 nm with BET surface area of up to 522.5 m{sup 2}/g. TEM/HRTEM images confirmed formation of the WC nano particles with spherical morphology. Electrochemical stability of pure and platinized carbide sample (Pt/WC) has been investigated using cyclic voltammetry in acidic media for alcohol (methanol and ethanol) oxidation. - Highlights: • Tungsten carbide nano powder was synthesized using charcoal as carbon source. • Formation of WC occurs through the formation of lower tungsten oxide. • CO{sub 2}/CO ratio effect the formation of WC. • Mesoporous tungsten carbide with surface areas 522.5 m{sup 2}/g obtained by using charcoal. • Pt modified WC powder showed higher electrochemical stability.

  6. Co-tolerant anode electrocatalysts for impure hydrogen oxidation in solid polymer fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Cooper, S J; Thompsett, D [Johnson Matthey Technology Centre, Sonning Common (United Kingdom); Tseung, A C.C.; Chen, K Y [Essex Univ., Colchester (United Kingdom)

    1997-09-01

    Recent work by the Chemical Energy Research Centre (CERC) at the University of Essex under the direction of Professor A.C.C. Tseung has investigated the combination of tungsten trioxide (WO{sub 3}) with carbon supported platinum (Pt) and platinum ruthenium (PtRu) catalysts for carbon monoxide (CO) tolerance for application in low temperature fuel cells. In particular, a catalyst combining Pt, Ru and WO{sub 3} gave a significantly improved tolerance to the effect of CO on H{sub 2} oxidation, at 80{sup o}C using fuel of 100 ppm CO in H{sub 2} and 0.5 M sulphuric acid (H{sub 2}SO{sub 4}) electrolyte. The aim of this project was to make a direct comparison between the catalyst technology developed at the University of Essex with the current Johnson Matthey PtRu catalyst technology as used in Proton Exchange Fuel Cells (PEMFC). (Author)

  7. Hexagonal nanorods of tungsten trioxide: Synthesis, structure, electrochemical properties and activity as supporting material in electrocatalysis

    Energy Technology Data Exchange (ETDEWEB)

    Salmaoui, Samiha; Sediri, Faouzi; Gharbi, Neji [Laboratoire de Chimie de la Matiere Condensee, Institut Preparatoire aux Etudes d' Ingenieurs, Universite de Tunis (Tunisia); Perruchot, Christian; Aeiyach, Salah [Interfaces, Traitements, Organisation et DYnamique des Systemes (ITODYS), UMR 7086, Universite Paris Diderot Paris 7, 15, rue Jean de Baif, 75205 Paris Cedex 13 (France); Rutkowska, Iwona A.; Kulesza, Pawel J. [Department of Chemistry, University of Warsaw, Pasteura 1, PL-02-093 Warsaw (Poland); Jouini, Mohamed, E-mail: jouini@univ-paris-diderot.fr [Interfaces, Traitements, Organisation et DYnamique des Systemes (ITODYS), UMR 7086, Universite Paris Diderot Paris 7, 15, rue Jean de Baif, 75205 Paris Cedex 13 (France)

    2011-07-15

    Tungsten trioxide, unhydrated with hexagonal structure (h-WO{sub 3}), has been prepared by hydrothermal method at a temperature of 180 {sup o}C in acidified sodium tungstate solution. Thus prepared h-WO{sub 3} has been characterized by X-ray diffraction (XRD) method and using electrochemical techniques. The morphology has been examined by scanning and transmission electron microscopies (SEM and TEM) and it is consistent with existence of nanorods of 50-70 nm diameter and up to 5 {mu}m length. Cyclic voltammetric characterization of thin films of h-WO{sub 3} nanorods has revealed reversible redox behaviour with charge-discharge cycling corresponding to the reversible lithium intercalation/deintercalation into the crystal lattice of the h-WO{sub 3} nanorods. In propylene carbonate containing LiClO{sub 4}, two successive redox processes of hexagonal WO{sub 3} nanorods are observed at the scan rate of 50 mV/s. Such behaviour shall be attributed to the presence of at least two W atoms of different surroundings in the lattice structure of h-WO{sub 3} nanorods. On the other hand, in aqueous LiClO{sub 4} solution, only one redox process is observed at the scan rate of 10 mV/s. The above observations can be explained in terms of differences in the diffusion of ions inside two types of channel cavities existing in the structure of the h-WO{sub 3} nanorods. Moreover, the material can be applied as active support for the catalytic bi-metallic Pt-Ru nanoparticles during electrooxidation of ethanol in acid medium (0.5 mol dm{sup -3} H{sub 2}SO{sub 4}).

  8. Luminescence and thermoluminescence properties of Sr{sub 3}WO{sub 6}:Eu{sup 3+} phosphor

    Energy Technology Data Exchange (ETDEWEB)

    Emen, F.M., E-mail: femen106@gmail.com [Department of Chemistry, Faculty of Arts and Science, Mehmet Akif Ersoy University, TR 15030, Burdur (Turkey); Altinkaya, R. [Department of Chemistry, Faculty of Arts and Science, Mersin University, TR 33343, Mersin (Turkey)

    2013-02-15

    Sr{sub 3-x}WO{sub 6}:xEu{sup 3+} (x varies from 0.01 to 0.06) phosphors have been prepared at high temperature by the solid-state method. The crystal structure of Sr{sub 2.95}WO{sub 6}:0.05Eu{sup 3+} phosphor has been determined as a triclinic P-1 space group with a=8.3608 (19) A, b=8.2903 (24) A, c=8.2145 (23) A, {alpha}=89.79 (3){sup Degree-Sign }, {beta}=89.82 (3){sup Degree-Sign }, and {gamma}=89.753 (22){sup Degree-Sign }. The excitation spectrum of Sr{sub 2.95}WO{sub 6}:0.05Eu{sup 3+} phosphor reveals five excitation bands: one is assigned to the charge-transfer (CTLM) band of Sr{sub 3}WO{sub 6} host at 307 nm, and another is assigned to intra-4f transitions between 393 nm and 600 nm. The emission spectrum of Sr{sub 2.95}WO{sub 6}:0.05Eu{sup 3+} phosphor exhibits a series of emission bands, which are attributed to the {sup 5}D{sub 0}{yields}{sup 7}F{sub j} (j=0-4) transitions of Eu{sup 3+} ions. The luminescence studies revealed that the Eu{sup 3+} ions show high luminescent efficiency in emitting red light at 616 nm. The thermoluminescence glow curve shows one dominant glow peak observed at 56 Degree-Sign C which is related to the defects at shallow trap depth. The trap parameters mainly activation energy (E{sub a}) and the order of the kinetics (b) were evaluated by using Rasheedy's three points method (TPM). - Highlights: Black-Right-Pointing-Pointer The Sr{sub 3}WO{sub 6}:Eu{sup 3+} phosphor was prepared by using conventional ceramic method. Black-Right-Pointing-Pointer The diffraction peaks of phosphor have been indexed to triclinic system. Black-Right-Pointing-Pointer The emission peak at 616 nm belongs to {sup 5}D{sub 0}{yields}{sup 7}F{sub 2} electric dipole transitions of Eu{sup 3+}. Black-Right-Pointing-Pointer The emission band of WO{sub 6} and excitation bands of Eu{sup 3+} are overlapping each other. Black-Right-Pointing-Pointer The energy transfer from WO{sub 6} groups to the Eu{sup 3+} ions occurs under the UV excitation.

  9. Fabrication and photocatalytic activity enhanced mechanism of direct Z-scheme g-C{sub 3}N{sub 4}/Ag{sub 2}WO{sub 4} photocatalyst

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, Bicheng [State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070 (China); Department of Science and Environmental Studies The Hong Kong Institute of Education, Tai Po, N.T., Hong Kong (China); Xia, Pengfei; Li, Yao [State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070 (China); Ho, Wingkei, E-mail: keithho@ied.edu.hk [Department of Science and Environmental Studies The Hong Kong Institute of Education, Tai Po, N.T., Hong Kong (China); Yu, Jiaguo, E-mail: jiaguoyu@yahoo.com [State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070 (China); Department of Physics, Faculty of Science, King Abdulaziz University, Jeddah 21589 (Saudi Arabia)

    2017-01-01

    Highlights: • g-C{sub 3}N{sub 4} acted as a support for the in situ growth of β-Ag{sub 2}WO{sub 4}. • g-C{sub 3}N{sub 4} nanosheets inhibited the phase transformation of β-Ag{sub 2}WO{sub 4} to α-Ag{sub 2}WO{sub 4}. • g-C{sub 3}N{sub 4}/Ag{sub 2}WO{sub 4} exhibited a superior photocatalytic activity. • A direct Z-scheme photocatalytic mechanism could explain activity enhancement. - Abstract: Herein, a direct Z-scheme graphitic carbon nitride (g-C{sub 3}N{sub 4})/silver tungstate (Ag{sub 2}WO{sub 4}) photocatalyst was prepared by a facile in situ precipitation method using g-C{sub 3}N{sub 4} as a support and silver nitrate as a precursor. X-ray diffraction, Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, transmission electron microscopy, and elemental mapping demonstrated that β-Ag{sub 2}WO{sub 4} nanoparticles were evenly distributed on the surface of g-C{sub 3}N{sub 4} nanosheets, which acted as a support for the nucleation and growth of β-Ag{sub 2}WO{sub 4} and inhibited the phase transformation of metastable β-Ag{sub 2}WO{sub 4} to stable α-Ag{sub 2}WO{sub 4}. Photocatalytic experiments indicated that the g-C{sub 3}N{sub 4}/Ag{sub 2}WO{sub 4} nanocomposite photocatalyst displayed a better photocatalytic activity than pure g-C{sub 3}N{sub 4} and Ag{sub 2}WO{sub 4} toward the degradation of methyl orange. The enhanced photocatalytic performance of g-C{sub 3}N{sub 4}/Ag{sub 2}WO{sub 4} could be well explained by a direct Z-scheme photocatalytic mechanism. This mechanism was related to the efficient space separation of photogenerated electron–hole pairs and the great oxidation and reduction capabilities of the g-C{sub 3}N{sub 4}/Ag{sub 2}WO{sub 4} system. This work provided new insights into the design and fabrication of g-C{sub 3}N{sub 4}-based direct Z-scheme photocatalysts.

  10. New doped tungsten cathodes. Applications to power grid tubes

    International Nuclear Information System (INIS)

    Cachard, J. de; Cadoret, K; Martinez, L.; Veillet, D.; Millot, F.

    2001-01-01

    Thermionic emission behavior of tungsten/tungsten carbide modified with rare earth (La, Ce, Y) oxides is examined on account of suitability to deliver important current densities in a thermo-emissive set up and for long lifetime. Work functions of potential cathodes have been determined from Richardson plots for La 2 O 3 doped tungsten and for tungsten covered with variable compositions rare earth tungstates. The role of platinum layers covering the cathode was also examined. Given all cathodes containing mainly lanthanum oxides were good emitters, emphasis was put on service lifetime. Comparisons of lifetime in tungsten doped with rare earth oxides and with rare earth tungstates show that microstructure of the operating cathodes may play the major role in the research of very long lifetime cathodes. Based on these results, tests still running show lifetime compatible with power grid tubes applications. (author)

  11. Nanoporous of W/WO{sub 3} thin film electrode grown by electrochemical anodization applied in the photoelectrocatalytic oxidation of the basic red 51 used in hair dye

    Energy Technology Data Exchange (ETDEWEB)

    Fraga, Luciano E.; Zanoni, Maria Valnice B., E-mail: fraga@iq.unesp.b [Universidade Estadual Paulista (IQ/UNESP), Araraquara, SP (Brazil). Inst. de Quimica. Dept. de Quimica Analitica

    2011-07-01

    Self-organized W/WO{sub 3} nanoporous electrodes can be obtained by simple electrochemical anodization of W foil in 0.15 mol L{sup -1} NaF solution as the supporting electrolyte, applying a ramp potential of 0.2 V s{sup -1} until it reached 60 V, which was maintained for 2 h. The monoclinic form is majority in the highly ordered WO{sub 3} annealed at 450 deg C, obtaining a higher photoactivity when irradiated by visible light than by UV light. The electrode promotes complete discoloration of the investigated basic red 51 dye after 60 min of photoelectrocatalytic oxidation, on current density of 1.25 mA cm{sup -2} and irradiation on wavelength of 420-630 nm. In this condition it was obtained 63% of mineralization. Lower efficiency is obtained for the system irradiated by wavelength (280- 400 nm) when only 40% of total organic carbon removal is obtained and 120 min is required for complete discoloration. (author)

  12. Advanced nanostructured photocatalysts based on reduced graphene oxide-flower-like Bi{sub 2}WO{sub 6} composites for an augmented simulated solar photoactivity activity

    Energy Technology Data Exchange (ETDEWEB)

    Li, Yukun [Key Laboratory of Integrated Regulation and Resources Development of Shallow Lakes, Ministry of Education, Hohai University, 1st Xikang Road, Nanjing 210098 (China); Chen, Lin [Key Laboratory of Integrated Regulation and Resources Development of Shallow Lakes, Ministry of Education, Hohai University, 1st Xikang Road, Nanjing 210098 (China); College of Environment, Hohai University, 1st Xikang Road, Nanjing 210098 (China); Wang, Yue [Key Laboratory of Integrated Regulation and Resources Development of Shallow Lakes, Ministry of Education, Hohai University, 1st Xikang Road, Nanjing 210098 (China); Zhu, Liang, E-mail: liangzhu_hh@163.com [Key Laboratory of Integrated Regulation and Resources Development of Shallow Lakes, Ministry of Education, Hohai University, 1st Xikang Road, Nanjing 210098 (China); College of Environment, Hohai University, 1st Xikang Road, Nanjing 210098 (China)

    2016-08-15

    Highlights: • A simple route was proposed to prepare flower-like Bi{sub 2}WO{sub 6} and RGO/Bi{sub 2}WO{sub 6}. • Cipro HCl was degraded firstly by RGO/Bi{sub 2}WO{sub 6} under the visible-light. • 2% RGO/Bi{sub 2}WO{sub 6} exhibited the best removal efficiency. - Abstract: A simple hydrothermal process was proposed to prepare the flower-like Bi{sub 2}WO{sub 6} architectures, and the as-synthesized Bi{sub 2}WO{sub 6} photocatalysts were further processed with the prepared graphene oxide (GO) to form novel reduced graphene oxide (RGO)/Bi{sub 2}WO{sub 6} composites. The nano-materials were characterized with the help of XRD, XPS, SEM, FTIR, UV-DRS, PL techniques to investigate their morphological, physical, optical, and photochemical properties. Photocatalytic performances of the pure flower-like Bi{sub 2}WO{sub 6} architectures and RGO/Bi{sub 2}WO{sub 6} composites were compared and evaluated through the degradation of ciprofloxacin hydrochloride (Cipro HCl) wastewater under the simulated visible light. It was found that the RGO/Bi{sub 2}WO{sub 6} composites displayed enhanced visible light-driven photocatalytic activities. It might be that the RGO loading not only effectively suppressed the electron–hole recombination, but also increased the light absorption ability. The effects of operating condition involved in the photocatalytic process were further examined, and the cycle-stability experiment demonstrated that as-obtained 2% RGO/Bi{sub 2}WO{sub 6} photocatalysts had good photocatalytic repeatability.

  13. Synthesis of tungsten oxide, silver, and gold nanoparticles by radio frequency plasma in water

    International Nuclear Information System (INIS)

    Hattori, Yoshiaki; Nomura, Shinfuku; Mukasa, Shinobu; Toyota, Hiromichi; Inoue, Toru; Usui, Tomoya

    2013-01-01

    Highlights: •RF plasma in water was used for nanoparticle synthesis. •Nanoparticles were produced from erosion of metallic electrode. •Rectangular and spherical tungsten oxide nanoparticles were produced. •No oxidations of the silver and gold spherical nanoparticles were produced. -- Abstract: A process for synthesis of nanoparticles using plasma in water generated by a radio frequency of 27.12 MHz is proposed. Tungsten oxide, silver, and gold nanoparticles were produced at 20 kPa through erosion of a metallic electrode exposed to plasma. Characterization of the produced nanoparticles was carried out by XRD, absorption spectrum, and TEM. The nanoparticle sizes were compared with those produced by a similar technique using plasma in liquid

  14. Reductive mineralization of cellulose with vanadium, iron and tungsten chlorides and access to MxOy metal oxides and MxOy/C metal oxide/carbon composites.

    Science.gov (United States)

    Henry, Aurélien; Hesemann, Peter; Alauzun, Johan G; Boury, Bruno

    2017-10-15

    M x O y and M x O y /C composites (M=V, Fe and W) were obtained by mineralization of cellulose with several metal chlorides. Cellulose was used both as a templating agent and as an oxygen and a carbon source. Soluble chloride molecules (VOCl 3 and WCl 6 ) and a poorly soluble ionic chloride compound (FeCl 3 ) were chosen as metal oxide precursors. In a first time, primary metal oxide/cellulose composites were obtained via a thermal treatment by reacting urea impregnated filter paper with the corresponding metal chlorides in an autoclave at 150°C after 3days. After either pyrolysis or calcination steps of these intermediate materials, interesting metal oxides with various morphologies were obtained (V 2 O 5, V 2 O 3 , Fe 3 O 4 , WO 3, H 0.23 WO 3 ), composites (V 2 O 3 /C) as well as carbides (hexagonal W 2 C and WC, Fe 3 C) This result highlight the reductive role that can play cellulose during the pyrolysis step that allows to tune the composition of M x O y /C composites. The materials were characterized by FTIR, Raman, TGA, XRD and SEM. This study highlights that cellulose can be used for a convenient preparation of a variety of highly demanded M x O y and M x O y /C composites with original shapes and morphologies. Copyright © 2017 Elsevier Ltd. All rights reserved.

  15. NO{sub 2} gas sensing of flame-made Pt-loaded WO{sub 3} thick films

    Energy Technology Data Exchange (ETDEWEB)

    Samerjai, Thanittha [Nanoscience and Nanotechnology Program, Faculty of Graduate School, Chiang Mai University, Chiang Mai 50200 (Thailand); Tamaekong, Nittaya [Program in Materials Science, Faculty of Science, Maejo University, Chiang Mai 50290 (Thailand); Liewhiran, Chaikarn [Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Wisitsoraat, Anurat [Nanoelectronics and MEMS Laboratory, National Electronics and Computer Technology Center, Klong Luang, Pathumthani 12120 (Thailand); Phanichphant, Sukon, E-mail: sphanichphant@yahoo.com [Materials Science Research Center, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand)

    2014-06-01

    Unloaded WO{sub 3} and 0.25–1.0 wt% Pt-loaded WO{sub 3} nanoparticles for NO{sub 2} gas detection were synthesized by flame spray pyrolysis (FSP) and characterized via X-ray diffraction (XRD), scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HRTEM). The BET surface area (SSA{sub BET}) of the nanoparticles was measured by nitrogen adsorption. The NO{sub 2} sensing properties of the sensors based on unloaded and Pt-loaded WO{sub 3} nanoparticles were investigated. The results showed that the gas sensing properties of the Pt-loaded WO{sub 3} sensors were excellent to those of the unloaded one. Especially, 0.25 wt% Pt-loaded WO{sub 3} sensor showed highest response to NO{sub 2} than the others at low operating temperature of 150 °C. - Graphical abstract: The response of 0.25 wt% Pt-loaded WO3 sensor was 637 towards NO{sub 2} concentration of 10 ppm at 150 °C. - Highlights: • Unloaded and Pt-loaded WO{sub 3} nanoparticles for NO{sub 2} gas detection were synthesized by flame spray pyrolysis (FSP). • Gas sensing properties of the Pt-loaded WO{sub 3} sensors were excellent to those of the unloaded one. • 0.25 wt% Pt-loaded WO{sub 3} sensor showed highest response to NO{sub 2} at low operating temperature of 150 °C.

  16. Gas sensing of ruthenium implanted tungsten oxide thin films

    Energy Technology Data Exchange (ETDEWEB)

    Tesfamichael, T., E-mail: t.tesfamichael@qut.edu.au [Institute for Future Environments, School of Chemistry, Physics and Mechanical Engineering, Queensland University of Technology, 2 George Street, Brisbane, QLD 4000 (Australia); Ahsan, M. [William A. Cook Australia, 95 Brandl Street Eight Mile Plains, Brisbane, QLD 4113 (Australia); Notarianni, M. [Institute for Future Environments, School of Chemistry, Physics and Mechanical Engineering, Queensland University of Technology, 2 George Street, Brisbane, QLD 4000 (Australia); Groß, A.; Hagen, G.; Moos, R. [University of Bayreuth, Faculty of Engineering Science, Department of Functional Materials, Universitätsstr. 30, 95440 Bayreuth (Germany); Ionescu, M. [ANSTO, Institute for Environmental Research, Locked Bag 2001, Kirrawee DC, NSW 2232 (Australia); Bell, J. [Institute for Future Environments, School of Chemistry, Physics and Mechanical Engineering, Queensland University of Technology, 2 George Street, Brisbane, QLD 4000 (Australia)

    2014-05-02

    Different amounts of Ru were implanted into thermally evaporated WO{sub 3} thin films by ion implantation. The films were subsequently annealed at 600 °C for 2 h in air to remove defects generated during the ion implantation. The Ru concentrations of four samples have been quantified by Rutherford Backscattering Spectrometry as 0.8, 5.5, 9 and 11.5 at.%. The un-implanted WO{sub 3} films were highly porous but the porosity decreased significantly after ion implantation as observed by Transmission Electron Microscopy and Scanning Electron Microscopy. The thickness of the films also decreased with increasing Ru-ion dose, which is mainly due to densification of the porous films during ion implantation. From Raman Spectroscopy two peaks at 408 and 451 cm{sup −1} (in addition to the typical vibrational peaks of the monoclinic WO{sub 3} phase) associated with Ru were observed. Their intensity increased with increasing Ru concentration. X-ray Photoelectron Spectroscopy showed a metallic state of Ru with binding energy of Ru 3d{sub 5/2} at 280.1 eV. This peak position remained almost unchanged with increasing Ru concentration. The resistances of the Ru-implanted films were found to increase in the presence of NO{sub 2} and NO with higher sensor response to NO{sub 2}. The effect of Ru concentration on the sensing performance of the films was not explicitly observed due to reduced film thickness and porosity with increasing Ru concentration. However, the results indicate that the implantation of Ru into WO{sub 3} films with sufficient film porosity and film thickness can be beneficial for NO{sub 2} sensing at temperatures in the range of 250 °C to 350 °C. - Highlights: • Densification of WO{sub 3} thin films has occurred after Ru ion implantation. • Thickness and porosity of the films decrease with increasing Ru ion dose. • The amount of oxygen vacancies and defects increases with increasing Ru ion dose. • Ru has shown a crucial role in enhancing sensor response

  17. Surface Functionalization of WO3 Thin Films with (3-Aminopropyl)triethoxysilane and Succinic Anhydride

    Science.gov (United States)

    Ta, Thi Kieu Hanh; Tran, Thi Nhu Hoa; Tran, Quang Minh Nhat; Pham, Duy Phong; Pham, Kim Ngoc; Cao, Thi Thanh; Kim, Yong Soo; Tran, Dai Lam; Ju, Heongkyu; Phan, Bach Thang

    2017-06-01

    We report effects of oxygen plasma treatment on the surface functionalization of WO3 thin films with (3-aminopropyl)triethoxysilane (APTES) and succinic anhydride (SA). X-ray diffraction and x-ray photoelectron spectroscopy results indicate the existence of the WO3 phase. Fourier transform infrared spectroscopy measurement shows clear bands at 1040 cm-1 (Si-O-Si), 1556 cm-1 (N-H), 1655 cm-1 (C=O), 2937 cm-1 (C-H) and 3298 cm-1 (N-H), confirming the surface functionalization efficiency enhanced by prior treatment of oxygen plasma. It thus follows that the prior oxygen plasma treatment activates hydroxylation with more -OH groups on the WO3 surface, which can pave a highly efficient way to the surface functionalization by APTES and SA.

  18. A Resistive Humidity Sensor Based on Nanostructured WO3-ZnO Composites

    Directory of Open Access Journals (Sweden)

    Karunesh Tiwari

    2011-11-01

    Full Text Available Paper reports morphological and humidity sensing studies of WO3 and WO3-ZnO composite pellets prepared in the weight % ratio of 10:1, 4:1 and 2:1 by solid-state reaction route. The pellets have been annealed at temperatures of 300-500 °C. XRD pattern shows peaks of ZnWO4 formed due to solid state reaction between WO3 and ZnO. SEM micrographs show that the sensing elements manifest porous structure. Granulation and tendency to agglomerate seen in the SEM micrograph are due to the presence of zinc ions in ZnWO4. Nanoparticles are having their sizes in the range 37-182 nm. The average Kelvin radius at 20˚C room temperature is 27 Ả. Humidity sensing application of the pellets has been studied in a humidity control cabinet. It is observed that as relative humidity increases, there is decrease in the resistance of pellets in the range 10-85 % RH. Sensing element of WO3-ZnO in 2:1 weight % ratio shows best results in 10-85 % relative humidity range. The average sensitivity of this sample is 1.25 MΩ/%RH. This sensing element shows good reproducibility, low hysteresis and less effect of aging.

  19. Suppression of cavitation in melted tungsten by doping with lanthanum oxide

    International Nuclear Information System (INIS)

    Yuan, Y.; Lu, G.H.; Xu, B.; Fu, B.Q.; Xu, H.Y.; Li, C.; Jia, Y.Z.; Qu, S.L.; Liu, W.; Greuner, H.; Böswirth, B.; Luo, G.-N.

    2014-01-01

    Melting and boiling behaviour of pure tungsten and 1 wt% lanthanum-oxide-doped tungsten (WL10) are investigated, focusing on the material selection with respect to material loss induced by cavitation. Melting experiments under high heat loads are carried out in the high heat flux facility GLADIS. Pulsed hydrogen neutral beams with heat flux of 10 and 23 MW m −2 are applied onto the adiabatically loaded samples for intense surface melting. Melt layer of the two tungsten grades exhibit different microstructure characteristics. Substantive voids owing to cavitation in the liquid phase are observed in pure W and lead to porous resolidified material. However, little cavitation bubbles can be found in the dense resolidified layer of WL10. In order to find out the gaseous sources, vapour collection is performed and the components are subsequently detected. Based on the observations and analyses, the microstructure evolutions corresponding to melting and vapourization behaviour of the two tungsten grades are tentatively described, and furthermore, the underlying mechanisms of cavitation in pure W and its suppression in WL10 are discussed. (paper)

  20. Role of reactive species in the photocatalytic degradation of ...

    Indian Academy of Sciences (India)

    2017-12-06

    Dec 6, 2017 ... Nitrogen doping; photocatalysis; visible light active; reactive species; ... Of a variety of semiconductors, tungsten oxide (WO3) ... sodium chloride (NaCl, Chameleon reagent), sodium nitrate ..... Ammonium. No ion .... produced.

  1. Oxygen partial pressure effects on the magnetron sputtered WO3 films

    International Nuclear Information System (INIS)

    Muğlu, G Merhan; Gür, E

    2016-01-01

    Electrochromism is changing color of a substance in response to the applied an external electric field and the phenomenon is reversible. WO 3 is very attractive material due to its electrochromic properties as well as it is also attractive for many different applications such as gas sensors, phosphorous screen, textile, glass industry. In this study, it is aimed to provide optimization of the optical and structural characteristics of WO 3 by changing the growth parameters mainly the oxygen partial pressure. The partial pressure of oxygen was changed with increments of 0.7 mTorr. For the analysis, X-ray Diffraction (XRD), absorption, Raman spectroscopy measurements were used. When O 2 gas increased, peaks belong to the WO 3 was observed in XRD patterns at the 2 theta angles of 23.0, 11.0, 23.5 and 28.5 angles corresponding to the (002), (020) and (220) planes, respectively. This shows that there is a significant effect of increasing O 2 partial pressure in the formation of WO 3 films. The bandgap energy of the WO 3 thin films are found to be around 3.0 eV. Raman measurements showed vibrational modes of W-O-W stretching and bending modes which shows small shifts depending on the partial pressures of the O 2 . Obtained results indicated that better crystal structure is obtained with higher O 2 gas partial pressure. (paper)

  2. Nanospherical composite of WO{sub 3} wrapped NaTaO{sub 3}: Improved photodegradation of tetracycline under visible light irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Qu, Lingnan; Lang, Junyu; Wang, Shuwei; Chai, Zhanli; Su, Yiguo; Wang, Xiaojing, E-mail: wang_xiao_jing@hotmail.com

    2016-12-01

    Graphical abstract: - Highlights: • A novel ternary NaTaO{sub 3}@WO{sub 3} photocatalyst was successfully fabricated. • NaTaO{sub 3}@WO{sub 3} composites exhibited spherical assemblies with fine WO{sub 3} nanosheets wrapped on the cube NaTaO{sub 3} nanoparticles. • NaTaO{sub 3}@WO{sub 3} showed the enhanced photocatalytic performance in the tetracycline hydrochloride degradation under visible light irradiation. • An adsorption−degradation photocatalytic mechanism promoted through a Z-type heterojunction was proposed. - Abstract: In this paper, WO{sub 3}-wrapped NaTaO{sub 3} nanospheres photocatalysts with different W/Ta molar ratios were successfully prepared via a facile hydrothermal method. The samples were characterized by X-ray diffraction, transmission and scan electron microscopy, X-ray photoelectron spectroscopy, FT-IR spectrum, UV−vis diffuse reflectance spectroscopy, and Barrett−Emmett−Teller technique. The photocatalytic activities for degrading tetracycline hydrochloride under visible light irradiation were examined. The results indicated that the as-prepared NaTaO{sub 3}@WO{sub 3} photocatalysts showed the obvious enhancement in the tetracycline hydrochloride degradation ratio, compared with the pure NaTaO{sub 3} and WO{sub 3} under visible light irradiation. The optimum percentage of NaTaO{sub 3}@WO{sub 3} composites with a 60.88% degradation rate was W:Ta = 0.3:1 in mole, which was mainly attributed to the effective separation of the photo-generated electron and hole as well as the expanding of the absorption edge to the visible region due to the spherical heterojunction by wrapping WO{sub 3} on the surface of NaTaO{sub 3}. The radicals trapping experiments demonstrated that there were multiple active species during the degrading process of TC. The possible mechanism of tetracycline hydrochloride degradation by NaTaO{sub 3}@WO{sub 3} composite was also proposed.

  3. Conductive surface modification of cauliflower-like WO3 and its electrochemical properties for lithium-ion batteries

    International Nuclear Information System (INIS)

    Yoon, Sukeun; Woo, Sang-Gil; Jung, Kyu-Nam; Song, Huesup

    2014-01-01

    Highlights: • Synthesis of cauliflower-like carbon-decorated WO 3 . • Superior cyclability and rate capability for cauliflower-like carbon-decorated WO 3 . • Electrochemical reaction behavior of cauliflower-like carbon-decorated WO 3 with lithium. • In-situ XRD analysis during the first discharge–charge shows a complex reaction of intercalation and conversion of WO 3 . - Abstract: Cauliflower-like WO 3 was synthesized by a hydrothermal reaction without a surfactant, followed by firing, and was investigated as an anode material for lithium-ion battery applications. The scanning electron microscope (SEM) and transmission electron microscope (TEM) characterization indicated that WO 3 nanorods had an aggregation framework and built a cauliflower morphology. With the objective of understanding the charge–discharge process within a voltage range of 0–3 V vs. Li + /Li, in situ X-ray diffraction was used and a complex reaction of intercalation and conversion of WO 3 was revealed for the first time. The cauliflower-like WO 3 after being decorated with carbon provides a high gravimetric capacity of >635 mA h/g (Li 5.5 WO 3 ) with good cycling and a high rate capability when used as an anode in lithium-ion batteries. Based on our studies, we attribute the high electrochemical performance to the nanoscopic WO 3 particles and a conductive carbon layer, which makes them a potential candidate for lithium-ion batteries

  4. A Preliminary Study on WO3‐Infiltrated W–Cu–ScYSZ Anodes for Low Temperature Solid Oxide Fuel Cells

    DEFF Research Database (Denmark)

    Abdul Jabbar, Mohammed Hussain; Reddy Sudireddy, Bhaskar; Høgh, Jens Valdemar Thorvald

    2012-01-01

    of symmetric cells were prepared by screen printing of WO3–CuO–ScYSZ ink and subsequent sintering at 1,300 °C for 1 h in 9% H2/N2. Analysis of the sintered backbone by X‐ray diffraction showed the metallic W and Cu phases. Precursor solutions of WO3 or CuO were infiltrated into porous WCS backbones to form...

  5. Formation of tungsten oxide nanostructures by laser pyrolysis: stars, fibres and spheres

    CSIR Research Space (South Africa)

    Govender, M

    2010-06-01

    Full Text Available This report focuses on the production of multi-phase WO3 and WO3-x (where x could vary between 0.2 and 0.33) nanostructures synthesized by CO2-laser pyrolysis technique at varying laser wavelengths (9.22-10.82 mm) and power densities (17-110 W/cm2...

  6. The ITO-capped WO{sub 3} nanowires biosensor based on field-effect transistor in label-free protein sensing

    Energy Technology Data Exchange (ETDEWEB)

    Shariati, Mohsen [Sharif University of Technology, Institute for Nanoscience and Nanotechnology, Tehran (Iran, Islamic Republic of)

    2017-05-15

    The fabrication of ITO-capped WO{sub 3} nanowires associated with their bio-sensing properties in field-effect transistor diagnostics basis as a biosensor has been reported. The bio-sensing property for manipulated nanowires elucidated that the grown nanostructures were very sensitive to protein. The ITO-capped WO{sub 3} nanowires biosensor showed an intensive bio-sensing activity against reliable protein. Polylysine strongly charged bio-molecule was applied as model system to demonstrate the implementation of materialized biosensor. The employed sensing mechanism was 'label-free' and depended on bio-molecule's intrinsic charge. For nanowires synthesis, the vapor-liquid-solid mechanism was used. Nanowires were beyond a few hundred nanometers in lengths and around 15-20 nm in diameter, while the globe cap's size on the nanowires was around 15-25 nm. The indium tin oxide (ITO) played as catalyst in nanofabrication for WO{sub 3} nanowires growth and had outstanding role in bio-sensing especially for bio-molecule adherence. In applied electric field presence, the fabricated device showed the great potential to enhance medical diagnostics. (orig.)

  7. Neuromorphic transistor achieved by redox reaction of WO3 thin film

    Science.gov (United States)

    Tsuchiya, Takashi; Jayabalan, Manikandan; Kawamura, Kinya; Takayanagi, Makoto; Higuchi, Tohru; Jayavel, Ramasamy; Terabe, Kazuya

    2018-04-01

    An all-solid-state neuromorphic transistor composed of a WO3 thin film and a proton-conducting electrolyte was fabricated for application to next-generation information and communication technology including artificial neural networks. The drain current exhibited a 4-order-of-magnitude increment by redox reaction of the WO3 thin film owing to proton migration. Learning and forgetting characteristics were well tuned by the gate control of WO3 redox reactions owing to the separation of the current reading path and pulse application path in the transistor structure. This technique should lead to the development of versatile and low-power-consumption neuromorphic devices.

  8. Synthesis of tungsten oxide nanoparticles using a hydrothermal method at ambient pressure

    DEFF Research Database (Denmark)

    Ahmadi, Majid; Younesi, Reza; Guinel, Maxime J-F

    2014-01-01

    ) nanoparticles were synthesized using a simple and inexpensive low temperature and low pressure hydrothermal (HT) method. The precursor solution used for the HT process was prepared by adding hydrochloric acid to diluted sodium tungstate solutions (Na2WO4 center dot 2H(2)O) at temperatures below 5 degrees C...... and then dissolved using oxalic acid. This HT process yielded tungstite (WO3 center dot H2O) nanoparticles with the orthorhombic structure. A heat treatment at temperatures at or above 300 degrees C resulted in a phase transformation to monoclinic WO3, while preserving the nanoparticles morphology. The production...

  9. Models of WO x films growth during pulsed laser deposition at elevated pressures of reactive gas

    Science.gov (United States)

    Gnedovets, A. G.; Fominski, V. Y.; Nevolin, V. N.; Romanov, R. I.; Fominski, D. V.; Soloviev, A. A.

    2017-12-01

    The films of tungsten oxides were prepared by pulsed laser ablation of W target in a reactive gas atmosphere (air of laboratory humidity). Optical analysis and ion signal measurements for the laser plume allowed to recognise a threshold gas pressure that suppresses the deposition of non-scattered atomic flux from the plume. When the pressure exceeds about 40 Pa, the films grow due to the deposition of species that could be formed in collisions of W atoms with reactive molecules (e.g., O2). Kinetic Monte Carlo method was used for modelling film growth. Comparison of the model structures with the experimentally prepared films has shown that the growth mechanism of ballistic deposition at a pressure of 40 Pa could be changed on the diffusion limited aggregation at a pressure of ~100 Pa. Thus, a cauliflower structure of the film transformed to a web-like structure. For good correlation of experimental and model structures of WO x , a dimension of structural elements in the model should coincide with W-O cluster size.

  10. Chemical purification of CaCO{sub 3} and CaWO{sub 4} powders used for CaWO{sub 4} crystal production for the CRESST experiment

    Energy Technology Data Exchange (ETDEWEB)

    Trinh Thi, H.H.; Defay, X.; Erb, A.; Hampf, R.; Lanfranchi, J.C.; Langenkaemper, A.; Morgalyuk, V.; Muenster, A.; Mondragon, E.; Oppenheimer, C.; Potzel, W.; Schoenert, S.; Steiger, H.; Ulrich, A.; Wawoczny, S.; Willers, M.; Zoeller, A. [Physik-Department and Excellence Cluster Universe, Technische Universitaet Muenchen, Garching (Germany)

    2016-07-01

    CRESST (Cryogenic Rare Event Search with Superconducting Thermometers) uses CaWO{sub 4} single crystals as targets for the direct search for dark matter particles. Since several years these CaWO{sub 4} crystals are grown at the Technische Universitaet Muenchen. Thereby, commercially available CaCO{sub 3} and WO{sub 3} powders are used for the synthesis of CaWO{sub 4} powder. For the experiment low intrinsic contaminations of the crystals play a crucial role. In order to improve the radiopurity of the crystals it is necessary to reduce potential sources for radioactive backgrounds such as U and Th. In this poster we will present our studies of the chemical purification of the CaCO{sub 3} and CaWO{sub 4} powders.

  11. Separation of Molybdenum from Acidic High-Phosphorus Tungsten Solution by Solvent Extraction

    Science.gov (United States)

    Li, Yongli; Zhao, Zhongwei

    2017-10-01

    A solvent-extraction process for deep separation of molybdenum from an acidic high-phosphate tungsten solution was developed using tributyl phosphate (TBP) as the extractant and hydrogen peroxide (H2O2) as a complexing agent. The common aqueous complexes of tungsten and molybdenum (PMoxW12-xO40 3-, x = 0-12) are depolymerized to {PO4[Mo(O)2(O-O)]4}3- and {PO4[W(O)2(O-O)]4}3- by H2O2. The former can be preferentially extracted by TBP. The extractant concentration, phase contact time, H2O2 dosage, and H2SO4 concentration were optimized. By employing 80% by volume TBP, O:A = 1:1, 1.0 mol/L H2SO4, 1.0 mol/L H3PO4, a contact time of 2 min, and a molar ratio of H2O2/(W + Mo) equal to 1.5, 60.2% molybdenum was extracted in a single stage, while limiting tungsten co-extraction to 3.2%. An extraction isotherm indicated that the raffinate could be reduced to <0.1 g/L Mo in six stages of continuous counter-current extraction.