Sol-gel synthesis of TiO2 nanoparticles and photocatalytic degradation of methyl orange in aqueous TiO2 suspensions

International Nuclear Information System (INIS)

Yang Huaming; Zhang Ke; Shi Rongrong; Li Xianwei; Dong Xiaodan; Yu Yongmei

2006-01-01

Anatase TiO 2 nanoparticles of about 16 nm in crystal size have been successfully synthesized via a sol-gel method. Thermal treatment of the precursor at 500-600 deg. C results in the formation of different TiO 2 phase compositions. The samples were characterized by means of X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM). Effects of the pH value of the solution, H 2 O 2 addition, TiO 2 phase composition and recycled TiO 2 on the photocatalytic degradation of methyl orange (MeO) in TiO 2 suspensions under ultraviolet (UV) illumination were primarily investigated. The results indicate that a low pH value, proper amount of H 2 O 2 and pure anatase TiO 2 will facilitate the photocatalytic oxidation of the MeO solution. The photodegradation degree decreases with increasing the pH value of the solution and varies with different amounts of H 2 O 2 . Pure anatase TiO 2 shows better photocatalytic activity for MeO decolorization than biphase TiO 2 . The photocatalytic mechanism of the as-synthesized TiO 2 nanoparticles was discussed

Synthesis and characterization of TiO2 nanoparticles by the method Pechini

International Nuclear Information System (INIS)

Zoccal, Joao Victor Marques; Arouca, Fabio de Oliveira; Goncalves, Jose Antonio Silveira

2009-01-01

In recent years, scientific research showed an increasing interest in the field of nanotechnology, resulting in several techniques for the production of nanoparticles, such as methods of chemical synthesis. Among the various existing methods, the Pechini method has been used to obtain nanoparticles of titanium dioxide (TiO 2 ). Thus, this work aims to synthesize and characterize nanoparticles of TiO 2 obtained by this method. The technique constitutes in the reaction between citric acid with titanium isopropoxide, resulting as the product the titanium citrate. With the addition of the ethylene glycol polymerization occurs, resulting in a polymeric resin. At the end of the process, the resin is calcined to remove organic matter, creating nanoparticles of TiO 2 . The resulting powders were characterized by thermogravimetric analysis (TGA) and thermal differential analysis (DTA), X-ray diffraction, absorption spectrophotometry in the infrared, method of adsorption nitrogen / helium (BET method) and scanning electron microscopy. The results obtained in the characterization techniques showed that the Pechini method is promising in obtaining nanosized TiO 2 . (author)

Low-Temperature Synthesis of Anatase TiO2 Nanoparticles with Tunable Surface Charges for Enhancing Photocatalytic Activity

Science.gov (United States)

Li, Ye; Qin, Zhenping; Guo, Hongxia; Yang, Hanxiao; Zhang, Guojun; Ji, Shulan; Zeng, Tingying

2014-01-01

In this work, the positively or negatively charged anatase TiO2 nanoparticles were synthesized via a low temperature precipitation-peptization process (LTPPP) in the presence of poly(ethyleneimine) (PEI) and poly(sodium4- styrenesulfonate) (PSS). X-ray diffraction (XRD) pattern and high-resolution transmission electron microscope (HRTEM) confirmed the anatase crystalline phase. The charges of the prepared TiO2, PEI-TiO2 and PSS-TiO2 nanoparticles were investigated by zeta potentials. The results showed that the zeta potentials of PEI-TiO2 nanoparticles can be tuned from +39.47 mV to +95.46 mV, and that of PSS-TiO2 nanoparticles can be adjusted from −56.63 mV to −119.32 mV. In comparison with TiO2, PSS-TiO2 exhibited dramatic adsorption and degradation of dye molecules, while the PEI modified TiO2 nanoparticles showed lower photocatalytic activity. The photocatalytic performances of these charged nanoparticles were elucidated by the results of UV-vis diffuse reflectance spectra (DRS) and the photoluminescence (PL) spectra, which indicated that the PSS-TiO2 nanoparticles showed a lower recombination rate of electron-hole pairs than TiO2 and PEI-TiO2. PMID:25506839

Complex impedance study on nano-CeO2 coating TiO2

International Nuclear Information System (INIS)

Zhang Mei; Wang Honglian; Wang Xidong; Li Wenchao

2006-01-01

Titanium dioxide (TiO 2 ) nanoparticles and cerium dioxide (CeO 2 ) nanoparticles coated titanium dioxide (TiO 2 ) nanoparticles (CeO 2 -TiO 2 nanoparticles) have been successfully synthesized by sol-gel method. The complex impedance of the materials was investigated. The grain resistance, boundary resistance and activation energy of the nanoparticles were calculated according to Arrhenius equation. According to calculating results, the active capacity of pure TiO 2 nanoparticles has been improved because of nano-CeO 2 coating. An optimal CeO 2 content of 4.9 mol% was achieved. The high resolution electron microscopy images of CeO 2 -TiO 2 nanoparticles showed that TiO 2 nanoparticles, as a core, were covered by CeO 2 nanoparticles. The average size of CeO 2 coating TiO 2 nanoparticles was about 70 nm. Scanning electron microscopy observation indicted that CeO 2 nanoparticle coating improved the separation, insulation, and stability the CeO 2 -TiO 2 nanoparticles, which was benefit to the activity of materials

Hazards of TiO2 and amorphous SiO2 nanoparticles

NARCIS (Netherlands)

Reijnders, L.; Kahn, H.A.; Arif, I.A.

2012-01-01

TiO2 and amorphous SiO2 nanoparticles have been described as ‘safe’, ‘non-toxic’ and ‘environment friendly’ in scientific literature. However, though toxicity data are far from complete, there is evidence that these nanoparticles are hazardous. TiO2 nanoparticles have been found hazardous to humans

Tailoring luminescence properties of TiO2 nanoparticles by Mn doping

International Nuclear Information System (INIS)

Choudhury, B.; Choudhury, A.

2013-01-01

TiO 2 nanoparticles are doped with three different concentrations of Mn, 2%, 4% and 6% respectively. Absorption edge of TiO 2 is shifted from UV to visible region on amplification of Mn content. Room temperature photoluminescence spectra, excited at 320 nm, exhibit band edge and visible emission peaks associated with self trapped excitons, oxygen defects, etc. Doping of Mn increases the width and decreases the intensity of the UV emission peak. Potential fluctuations of impurities increase the width and auger type non-radiative recombination decreases the intensity of the UV emission peak. The intensity ratio of the UV to defect emission band decreases on doping, indicating degradation of structural quality. Excitation of pure and doped nanoparticles at 390 nm results in Mn 2+ emission peaks at 525 nm and 585 nm respectively. Photoluminescence excitation spectra also indicate the presence of Mn 2+ in the crystalline environment of TiO 2 . The oxygen defects and Mn related impurities act as efficient trap centers and increases the lifetime of the charge carriers. -- Highlights: ► Doping of Mn increases the d-spacing of TiO 2 nanoparticles. ► Characteristic d–d electronic transition of Mn 2+ is observed in the absorption spectra. ► Doping of Mn quenches the UV and visible emission peaks of TiO 2 . ► Photoexcitation at 390 nm generates emission peaks of Mn 2+

Enhancement of the photocatalytic activity of TiO2 nanoparticles by surface-capping DBS groups

International Nuclear Information System (INIS)

Wang Baiqi; Jing Liqiang; Qu Yichun; Li Shudan; Jiang Baojiang; Yang Libin; Xin Baifu; Fu Honggang

2006-01-01

TiO 2 nanoparticles capped with sodium dodecylbenzenesulfonate (DBS) are synthesized by a sol-hydrothermal process using tetrabutyl titanate and DBS as raw materials. The effects of surface-capping DBS on the surface photovoltage spectroscopy (SPS), photoluminescence (PL) and photocatalytic performance of TiO 2 nanoparticles are principally investigated together with their relationships. The results show that the surface of TiO 2 nanoparticles can be well capped by DBS groups while the pH value and added DBS amount are controlled at 5.0 and 2% of TiO 2 mass weight, respectively, and the linkage between DBS groups and TiO 2 surfaces is mainly by means of quasi-sulphonate bond. The intensities of SPS and PL spectra of TiO 2 obviously decrease after DBS-capping, while the activity can greatly increase during the photocatalytic degradation of Rhodamine B (RhB) solution, which are mainly attributed to the electron-withdrawing character of the DBS groups. Moreover, the enhancement of photocatalytic activity of DBS-capped TiO 2 is also related to the increase in the capability for adsorbing RhB

Alpha amylase assisted synthesis of TiO2 nanoparticles: Structural characterization and application as antibacterial agents

International Nuclear Information System (INIS)

Ahmad, Razi; Mohsin, Mohd; Ahmad, Tokeer; Sardar, Meryam

2015-01-01

Graphical abstract: - Highlights: • Green synthesis of TiO 2 nanoparticles using an enzyme alpha amylase has been described. • The morphology and shape depends upon the concentration of the alpha amylase enzyme. • The biosynthesized nanoparticles show good bactericidal effect against both gram positive and gram negative bacteria. • The bactericidal effect was further confirmed by Confocal microscopy and TEM. - Abstract: The enzyme alpha amylase was used as the sole reducing and capping agent for the synthesis of TiO 2 nanoparticles. The biosynthesized nanoparticles were characterized by X-ray diffraction (XRD) and transmission electron microscopic (TEM) methods. The XRD data confirms the monophasic crystalline nature of the nanoparticles formed. TEM data shows that the morphology of nanoparticles depends upon the enzyme concentration used at the time of synthesis. The presence of alpha amylase on TiO 2 nanoparticles was confirmed by FTIR. The nanoparticles were investigated for their antibacterial effect on Staphylococcus aureus and Escherichia coli. The minimum inhibitory concentration value of the TiO 2 nanoparticles was found to be 62.50 μg/ml for both the bacterial strains. The inhibition was further confirmed using disc diffusion assay. It is evident from the zone of inhibition that TiO 2 nanoparticles possess potent bactericidal activity. Further, growth curve study shows effect of inhibitory concentration of TiO 2 nanoparticles against S. aureus and E. coli. Confocal microscopy and TEM investigation confirm that nanoparticles were disrupting the bacterial cell wall

Control of Electron Transfer from Lead-Salt Nanocrystals to TiO 2

KAUST Repository

Hyun, Byung-Ryool; Bartnik, A. C.; Sun, Liangfeng; Hanrath, Tobias; Wise, F. W.

2011-01-01

The roles of solvent reorganization energy and electronic coupling strength on the transfer of photoexcited electrons from PbS nanocrystals to TiO 2 nanoparticles are investigated. We find that the electron transfer depends only weakly

TiO2 nanoparticle thin film deposition by matrix assisted pulsed laser evaporation for sensing applications

International Nuclear Information System (INIS)

Caricato, A.P.; Capone, S.; Ciccarella, G.; Martino, M.; Rella, R.; Romano, F.; Spadavecchia, J.; Taurino, A.; Tunno, T.; Valerini, D.

2007-01-01

The MAPLE technique has been used for the deposition of nanostructured titania (TiO 2 ) nanoparticles thin films to be used for gas sensors applications. An aqueous solution of TiO 2 nanoparticles, synthesised by a novel chemical route, was frozen at liquid nitrogen temperature and irradiated with a pulsed ArF excimer laser in a vacuum chamber. A uniform distribution of TiO 2 nanoparticles with an average size of about 10 nm was deposited on Si and interdigitated Al 2 O 3 substrates as demonstrated by high resolution scanning electron microscopy-field emission gun inspection (SEM-FEG). Energy dispersive X-ray (EDX) analysis revealed the presence of only the titanium and oxygen signals and FTIR (Fourier transform infra-red) revealed the TiO 2 characteristic composition and bond. A comparison with a spin coated thin film obtained from the same solution of TiO 2 nanoparticles is reported. The sensing properties of the films deposited on interdigitated substrates were investigated, too

Ag and CdS nanoparticles co-sensitized TiO2 nanotubes for enhancing visible photoelectrochemical performance

International Nuclear Information System (INIS)

Wang Qingyao; Yang Xiuchun; Liu Dan; Chi Lina; Hou Junwei

2012-01-01

Highlights: ► Ag and CdS nanoparticles co-sensitized TiO 2 nanotubes were fabricated by the SILAR method. ► The co-sensitization expands the photoresponse range of TiO 2 NTs to 668.7 nm. ► Visible light photocurrents and photocatalytic activities of CdS–Ag/TiO 2 NTs were studied. ► The electron transfer mechanism of CdS–Ag/TiO 2 NTs was proposed. - Abstract: The Ag and CdS nanoparticles co-sensitization of TiO 2 nanotubes (CdS–Ag/TiO 2 NTs) were prepared by successive ionic layer adsorption and reaction (SILAR) technique. The phase composition, morphology and optical property were characterized by the X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and UV–vis diffusion reflection spectroscopy (DRS). The co-modification of Ag and CdS nanoparticles expanded the photoresponse range of TiO 2 NTs from ultraviolet region to 668.7 nm, and the CdS–Ag/TiO 2 NTs prepared by SILAR deposition of 5 cycles exhibited higher visible photocurrent and stability against photocorrosion. The detailed electrons transfer mechanism of CdS–Ag/TiO 2 NTs was proposed, and photocatalytic activity toward degradation of methyl orange (MO) under visible-light irradiation was also investigated.

Improvement of epoxy resin properties by incorporation of TiO2 nanoparticles surface modified with gallic acid esters

International Nuclear Information System (INIS)

Radoman, Tijana S.; Džunuzović, Jasna V.; Jeremić, Katarina B.; Grgur, Branimir N.; Miličević, Dejan S.; Popović, Ivanka G.; Džunuzović, Enis S.

2014-01-01

Highlights: • Nanocomposites of epoxy resin and TiO 2 nanoparticles surface modified with gallates. • The T g of epoxy resin was increased by incorporation of surface modified TiO 2 . • WVTR of epoxy resin decreased in the presence of surface modified TiO 2 nanoparticles. • WVTR of nanocomposites was reduced with increasing gallates hydrophobic chain length. • Modified TiO 2 nanoparticles react as oxygen scavengers, inhibiting steel corrosion. - Abstract: Epoxy resin/titanium dioxide (epoxy/TiO 2 ) nanocomposites were obtained by incorporation of TiO 2 nanoparticles surface modified with gallic acid esters in epoxy resin. TiO 2 nanoparticles were obtained by acid catalyzed hydrolysis of titanium isopropoxide and their structural characterization was performed by X-ray diffraction and transmission electron microscopy. Three gallic acid esters, having different hydrophobic part, were used for surface modification of the synthesized TiO 2 nanoparticles: propyl, hexyl and lauryl gallate. The gallate chemisorption onto surface of TiO 2 nanoparticles was confirmed by Fourier transform infrared and ultraviolet–visible spectroscopy, while the amount of surface-bonded gallates was determined using thermogravimetric analysis. The influence of the surface modified TiO 2 nanoparticles, as well as the length of hydrophobic part of the gallate used for surface modification of TiO 2 nanoparticles, on glass transition temperature, barrier, dielectric and anticorrosive properties of epoxy resin was investigated by differential scanning calorimetry, water vapor transmission test, dielectric spectroscopy, electrochemical impedance spectroscopy and polarization measurements. Incorporation of surface modified TiO 2 nanoparticles in epoxy resin caused increase of glass transition temperature and decrease of the water vapor permeability of epoxy resin. The water vapor transmission rate of epoxy/TiO 2 nanocomposites was reduced with increasing hydrophobic part chain length of

Improvement of the epoxy coating properties by incorporation of polyaniline surface treated TiO2 nanoparticles previously modified with vitamin B6

OpenAIRE

Radoman, Tijana S.; Džunuzović, Jasna V.; Grgur, Branimir; Gvozdenović, Milica M.; Jugović, Branimir; Miličević, Dejan S.; Džunuzović, Enis S.

2016-01-01

Novel TiO2-PANI core-shell nanocomposite, prepared by in situ oxidative polymerization of aniline in the presence of TiO2 nanoparticles surface modified with vitamin B6, was used to reinforce epoxy resin. The size of prepared TiO2 nanoparticles and TiO2-PANI nanocomposite were determined by a transmission electron microscopy (TEM). The surface modification of TiO2 nanoparticles was confirmed by FTIR and UV–vis spectroscopy, while the morphology of PANI and TiO2-PANI nanocomposite was investig...

Electrochemical Behavior of TiO2 Nanoparticle Doped WO3 Thin Films

Directory of Open Access Journals (Sweden)

Suvarna R. Bathe

2014-01-01

Full Text Available Nanoparticle TiO2 doped WO3 thin films by pulsed spray pyrolysis technique have been studied on fluorine tin doped (FTO and glass substrate. XRD shows amorphous nature for undoped and anatase phase of TiO2 having (101 plane for nanoparticle TiO2 doped WO3 thin film. SEM shows microfibrous reticulated porous network for WO3 with 600 nm fiber diameter and nanocrystalline having size 40 nm for TiO2 nanoparticle doped WO3 thin film. TiO2 nanoparticle doped WO3 thin film shows ~95% reversibility due to may be attributed to nanocrystalline nature of the film, which helpful for charge insertion and deinsertion process. The diffusion coefficient for TiO2 nanoparticle doped WO3 film is less than undoped WO3.

An enhanced photocatalytic response of nanometric TiO2 wrapping of Au nanoparticles for eco-friendly water applications.

Science.gov (United States)

Scuderi, Viviana; Impellizzeri, Giuliana; Romano, Lucia; Scuderi, Mario; Brundo, Maria V; Bergum, Kristin; Zimbone, Massimo; Sanz, Ruy; Buccheri, Maria A; Simone, Francesca; Nicotra, Giuseppe; Svensson, Bengt G; Grimaldi, Maria G; Privitera, Vittorio

2014-10-07

We propose a ground-breaking approach by an upside-down vision of the Au/TiO2 nano-system in order to obtain an enhanced photocatalytic response. The system was synthesized by wrapping Au nanoparticles (∼8 nm mean diameter) with a thin layer of TiO2 (∼4 nm thick). The novel idea of embedding Au nanoparticles with titanium dioxide takes advantage of the presence of metal nanoparticles, in terms of electron trapping, without losing any of the TiO2 exposed surface, so as to favor the photocatalytic performance of titanium dioxide. A complete structural characterization was made by scanning electron microscopy, transmission electron microscopy and X-ray diffraction. The remarkable photocatalytic performance together with the stability of the nano-system was demonstrated by degradation of the methylene blue dye in water. The non-toxicity of the nano-system was established by testing the effect of the material on the reproductive cycle of Mytilus galloprovincialis in an aquatic environment. The originally synthesized material was also compared to conventional TiO2 with Au nanoparticles on top. The latter system showed a dispersion of Au nanoparticles in the liquid environment, due to their instability in the aqueous solution that clearly represents an environmental contamination issue. Thus, the results show that nanometric TiO2 wrapping of Au nanoparticles has great potential in eco-friendly water/wastewater purification.

Photoluminescence studies on Eu doped TiO2 nanoparticles

International Nuclear Information System (INIS)

Ningthoujam, R.S.; Sudarsan, V.; Vatsa, R.K.; Kadam, R.M.; Jagannath; Gupta, A.

2009-01-01

Eu 3+ doped TiO 2 nanoparticles were prepared by urea hydrolysis in ethylene glycol medium at low temperature of 150 deg. C. X-ray diffraction study showed that anatase phase of tetragonal structure was formed below 500 deg. C; and above this temperature, additional peaks due to rutile phase were also observed. From luminescence study, it was found that as prepared nanoparticles showed the enhanced luminescence intensity due to energy transfer from host to europium ions. However, photoluminescence from these nanoparticles was found to disappear when the samples were heated above 900 deg. C. We established the origin of the reduction in the luminescence intensity from Eu 3+ when doped in TiO 2 and heated at 900 deg. C. Based on detailed studies at different heat-treatment temperatures using techniques such as X-ray diffraction, X-ray photoelectron spectroscopy, electron paramagnetic resonance, Raman spectroscopy, and Moessbauer spectroscopy, it has been established that formation of Eu 2 Ti 2 O 7 phase, wherein Eu 3+ ions occupy high symmetric environment (D 3d ) and also reduced distance between Eu 3+ and Eu 3+ ions is responsible for the decrease/loss in the luminescence intensity.

Photocatalytic degradation of some organic dyes under solar light irradiation using TiO2 and ZnO nanoparticles

Directory of Open Access Journals (Sweden)

Mojtaba Amini

2016-01-01

Full Text Available Nanoparticles of the ZnO and TiO2 were synthesized and the physicochemical properties of the compounds were characterized by IR, X-ray diffraction (XRD, scanning electron microscopy (SEM and transmission electron microscopy (TEM. The XRD patterns of the ZnO and TiO2 nanoparticles could be indexed to hexagonal and rutile phase, respectively. Aggregated nanoparticles of ZnO and TiO2 with spherical-like shapes were observed with particle diameter in the range of 80-100 nm. These nanoparticles were used for photocatalytic degradation of various dyes, Rhodamine B (RhB, Methylene blue (MB and Acridine orange (AO under solar light irradiation at room temperature. Effect of the amount of catalyst on the rate of photodegradation was investigated. In general, because ZnO is unstable, due to incongruous dissolution to yield Zn(OH2 on the ZnO particle surfaces and thus leading to catalyst inactivation,the catalytic activity of the system for photodegradation of dyes decreased dramatically when TiO2 was replaced by ZnO.

Laser induced photocurrent and photovoltage transient measurements of dye-sensitized solar cells based on TiO_2 nanosheets and TiO_2 nanoparticles

International Nuclear Information System (INIS)

Ghaithan, Hamid M.; Qaid, Saif M.H.; Hezam, Mahmoud; Labis, Joselito P.; Alduraibi, Mohammad; Bedja, Idriss M.; Aldwayyan, Abdullah S.

2016-01-01

Dye-sensitized solar cells (DSSCs) based on TiO_2 nanoparticles and TiO_2 nanosheets with exposed {001} facets are investigated using laser-induced photovoltage and photocurrent transient decay (LIPVCD) measurements. We adopted a simplified version of LIPVCD technique, in which a single illumination light source and a laboratory oscilloscope could be conveniently used for the measurements. Although the {001} surface of TiO_2 nanosheets allowed a noticeably slower recombination with the electrolyte, this was counterpoised by a slower electron transport probably due to its planar morphology, resulting in a shorter diffusion length in TiO_2 nanosheets. The nanosheet morphology also resulted in less surface area and therefore reduced short circuit current density in the fabricated devices. Our work highlights the fact that the morphological parameters of TiO_2 nanosheets finally resulting after electrode film deposition is of no less importance than the reported efficient dye adsorption and slow electron recombination at the surface of individual nanosheets.

1 composite mixture of TiO2 nanoparticles and nanotubes in dye

Indian Academy of Sciences (India)

Administrator

Abstract. TiO2-based nanotubes (NTs), nanoparticles (NPs) and composite structural film (50% NP + 50% ... of faster electron injection ratio compared with other .... exist in this system. .... the open circuit voltage, Im the maximum current and.

Long-term exposure of bacterial and protozoan communities to TiO2 nanoparticles in an aerobic-sequencing batch reactor

International Nuclear Information System (INIS)

Supha, Chitpisud; Boonto, Yuphada; Jindakaraked, Manee; Ananpattarachai, Jirapat; Kajitvichyanukul, Puangrat

2015-01-01

Titanium dioxide (TiO 2 ) nanopowders at different concentrations (0–50 mg L −1 ) were injected into an aerobic-sequencing batch reactor (SBR) to investigate the effects of long-term exposure to nanoparticles on bacterial and protozoan communities. The detection of nanoparticles in the bioflocs was analyzed by scanning electron microscopy, transmission electron microscopy, and energy-dispersive x-ray spectroscopy. The SBR wastewater experiments were conducted under the influence of ultraviolet light with photocatalytic TiO 2 . The intrusion of TiO 2 nanoparticles was found both on the surface and inside of the bioflocs. The change of microbial population in terms of mixed liquor-suspended solids and the sludge volume index was monitored. The TiO 2 nanoparticles tentatively exerted an adverse effect on the microbial population, causing the reduction of microorganisms (both bacteria and protozoa) in the SBR. The respiration inhibition rate of the bacteria was increased, and the viability of the microbial population was reduced at the high concentration (50 mg L −1 ) of TiO 2 . The decreasing number of protozoa in the presence of TiO 2 nanoparticles during 20 days of treatment with 0.5 and 1.0 mg L −1 TiO 2 is clearly demonstrated. The measured chemical oxygen demand (COD) in the effluent tends to increase with a long-term operation. The increase of COD in the system suggests a decrease in the efficiency of the wastewater treatment plant. However, the SBR can effectively remove the TiO 2 nanoparticles (up to 50 mg L −1 ) from the effluent. (focus issue paper)

Formation of textured microstructure by mist deposition of TiO2 nanoparticles

International Nuclear Information System (INIS)

Qin, Gang; Watanabe, Akira

2013-01-01

Unique and various textured TiO 2 films have been easily fabricated by mist deposition method on silicon and glass substrates with mild preparation conditions. Two kinds of TiO 2 nanoparticle with different shape, size, and crystal form were used as starting material, which resulted in a simple preparation process under low temperature and ordinary pressure. It was easy to control the thickness, morphology, and roughness of textured TiO 2 film by adjusting the mist deposition conditions such as deposition time, temperature, and the shape and size of nanoparticles. The optical properties of textured TiO 2 films before and after spin coating of Ag nanoparticles were investigated. The angular dependence of the reflectance was obviously reduced by textured TiO 2 surface and such effect was enhanced by Ag nanoparticles coating. A broad plasmon band of Ag grains was observed in the absorption spectrum of the textured Ag nanoparticle-coated TiO 2 film

Synthesis of dense TiO2 nanoparticle multilayers using spin coating technique

Science.gov (United States)

DeSilva, L. Ajith; Thakurdesai, Madhavi; Bandara, T. M. W. J.; Preston, Joshua; Johnson, Wyatt; Gaquere-Parker, Anne; Survase, Smita

2018-04-01

A stack of nine layers is prepared by sequential spun casting of commercially available colloidal TiO2 nanoparticles of average size of 10-15 nm. Scanning electron microscopy (SEM) is employed to investigate the surface morphology of the multilayers. SEM micrographs exhibit formation of highly uniform and dense TiO2 nanoparticle layers. The uniformity and density is found to be increasing with layer thickness. Structural characterization is carried out using X-ray diffraction (XRD) technique. XRD spectra indicate improvement in crystalline quality of all the layers with increasing layer thickness. All the layers are having mainly the anatase phase of TiO2. Optical characterization is carried out by UV-visible spectroscopy. The value of bandgap estimated on the basis of absorption coefficient is found to be 3.26 eV and approximately remains the same for the layers. The electrical characterization suggests that multilayer resistivity increases with increasing layer thickness. The good quality spin coated thin dense TiO2 layers have many applications in optoelectronics.

Efficient solar light-driven degradation of Congo red with novel Cu-loaded Fe3O4@TiO2 nanoparticles.

Science.gov (United States)

Arora, Priya; Fermah, Alisha; Rajput, Jaspreet Kaur; Singh, Harminder; Badhan, Jigyasa

2017-08-01

In this work, Cu-loaded Fe 3 O 4 @TiO 2 core shell nanoparticles were prepared in a single pot by coating of TiO 2 on Fe 3 O 4 nanoparticles followed by Cu loading. X-ray powder diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HR-TEM), thermogravimetric analysis (TGA), Brunauer-Emmett- Teller (BET), vibrating sample magnetometry (VSM), X-ray photoelectron spectroscopy (XPS), and valence band X-ray photoelectron spectroscopy (VB XPS) techniques were used for characterization of as prepared nanoparticles. Synergism between copper and titania was evaluated by studying the solar light-driven photodegradation of Congo red dye solution in the presence of Fe 3 O 4 @TiO 2 nanoparticles on one side and Cu-loaded Fe 3 O 4 @TiO 2 nanoparticles on the other side. The latter performed better than the former catalyst, indicating the enhanced activity of copper-loaded catalyst. Further photodegradation was studied by three means, i.e., under ultraviolet (UV), refluxing, and solar radiations. Cu-loaded Fe 3 O 4 @TiO 2 enhanced the degradation efficiency of Congo red dye. Thus, Cu act possibly by reducing the band gap of TiO 2 and widening the optical response of semiconductor, as a result of which solar light could be used to carry out photocatalysis. Graphical abstract Photodegradation of congo red over Cu-loaded Fe 3 O 4 @TiO 2 nanoparticles.

Enhanced visible light photocatalytic properties of Fe-doped TiO2 nanorod clusters and monodispersed nanoparticles

International Nuclear Information System (INIS)

Liu, Y.; Wei, J.H.; Xiong, R.; Pan, C.X.; Shi, J.

2011-01-01

In order to get photocatalysts with desired morphologies and enhanced visible light responses, the Fe-doped TiO 2 nanorod clusters and monodispersed nanoparticles were prepared by modified hydrothermal and solvothermal method, respectively. The microstructures and morphologies of TiO 2 crystals can be controlled by restraining the hydrolytic reaction rates. The Fe-doped photocatalysts were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), UV-vis absorption spectroscopy (UV-vis), N 2 adsorption-desorption measurement (BET), and photoluminescence spectroscopy (PL). The refinements of the microstructures and morphologies result in the enhancement of the specific surface areas. The Fe 3+ -dopants in TiO 2 lattices not only lead to the significantly extending of the optical responses from UV to visible region but also diminish the recombination rates of the electrons and holes. The photocatalytic activities were evaluated by photocatalytic decomposition of formaldehyde in air under visible light illumination. Compared with P25 (TiO 2 ) and N-doped TiO 2 nanoparticles, the Fe-doped photocatalysts show high photocatalytic activities under visible light.

Photodecomposition of volatile organic compounds using TiO2 nanoparticles.

Science.gov (United States)

Jwo, Ching-Song; Chang, Ho; Kao, Mu-Jnug; Lin, Chi-Hsiang

2007-06-01

This study examined the photodecomposition of volatile organic compounds (VOCs) using TiO2 catalyst fabricated by the Submerged Arc Nanoparticle Synthesis System (SANSS). TiO2 catalyst was employed to decompose volatile organic compounds and compare with Degussa-P25 TiO2 in terms of decomposition efficiency. In the electric discharge manufacturing process, a Ti bar, applied as the electrode, was melted and vaporized under high temperature. The vaporized Ti powders were then rapidly quenched under low-temperature and low-pressure conditions in deionized water, thus nucleating and forming nanocrystalline powders uniformly dispersed in the base solvent. The average diameter of the TiO2 nanoparticles was 20 nm. X-ray diffraction analysis confirmed that the nanoparticles in the deionized water were Anatase type TiO2. It was found that gaseous toluene exposed to UV irradiation produced intermediates that were even harder to decompose. After 60-min photocomposition, Degussa-P25 TiO2 reduced the concentration of gaseous toluene to 8.18% while the concentration after decomposition by SANSS TiO2 catalyst dropped to 0.35%. Under UV irradiation at 253.7 +/- 184.9 nm, TiO2 prepared by SANSS can produce strong chemical debonding energy, thus showing great efficiency, superior to that of Degussa-P25 TiO2, in decomposing gaseous toluene and its intermediates.

Biocorrosion studies of TiO2 nanoparticle-coated Ti-6Al-4V implant in simulated biofluids

International Nuclear Information System (INIS)

Zaveri, Nikita; McEwen, Gerald D.; Karpagavalli, Ramji; Zhou Anhong

2010-01-01

The corrosion behaviors of the TiO 2 nanoparticles coated bioimplant Ti-6Al-4V exposed to three different simulated biofluids (SBF), namely, (1) NaCl solution, (2) Hank's solution, and (3) Cigada solution, were studied by using micro-Raman spectroscopy, electrochemical techniques, and scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy (EDS). The different electrochemical impedance spectroscopy models were applied to fit the data obtained from the implants before and after the coating of TiO 2 nanoparticles (50-100 nm). It was found that the TiO 2 nanoparticle coatings increased the thickness of the pre-existing oxide layer on the Ti-6Al-4V surface, serving to improve the bioimplant corrosion resistance.

Biocorrosion studies of TiO2 nanoparticle-coated Ti-6Al-4V implant in simulated biofluids

Science.gov (United States)

Zaveri, Nikita; McEwen, Gerald D.; Karpagavalli, Ramji; Zhou, Anhong

2010-06-01

The corrosion behaviors of the TiO2 nanoparticles coated bioimplant Ti-6Al-4V exposed to three different simulated biofluids (SBF), namely, (1) NaCl solution, (2) Hank's solution, and (3) Cigada solution, were studied by using micro-Raman spectroscopy, electrochemical techniques, and scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy (EDS). The different electrochemical impedance spectroscopy models were applied to fit the data obtained from the implants before and after the coating of TiO2 nanoparticles (50-100 nm). It was found that the TiO2 nanoparticle coatings increased the thickness of the pre-existing oxide layer on the Ti-6Al-4V surface, serving to improve the bioimplant corrosion resistance.

Preparation and Tribological Properties of Dual-Coated TiO2 Nanoparticles as Water-Based Lubricant Additives

Directory of Open Access Journals (Sweden)

Yue Gu

2014-01-01

Full Text Available Titanium dioxide nanoparticles (TiO2 were synthesized and then dual-coated with silane coupling agent (KH-570 and OP-10 in sequence in order to be dispersed stably in water as lubricant additives. The tribological properties and the application performance in Q235 steel machining of the nanoparticles as water-based lubricant additives were investigated on an MSR-10D four-ball tribotester and on a bench drilling machine, respectively. Scanning electron microscope (SEM and atomic force microscope (AFM were used to analyze the worn surface. The results show that the surface-modified TiO2 nanoparticles can remarkably improve the load-carrying capacity, the friction reducing, and anti wear abilities of pure water. The wear scar diameter and the coefficient of friction of the water-based lubricating fluids with TiO2 nanoparticles decreased, and the thick deep furrows on the surface of wear scar also decreased obviously with the increase of TiO2 concentration. The power consumption in drilling process was lower and the cutting surface was smoother using the water-based lubricating fluids added TiO2 nanoparticles compared to the fluid without addition. The reason for nanoparticles improving tribological properties of water based lubricating fluid might be the formation of a dynamic deposition film during rubbing process according to analysis of the worn surface.

Exposure to TiO2 nanoparticles increases Staphylococcusaureusinfection of HeLa cells

Science.gov (United States)

Xu, Yan; Wei, Ming-Tzo; Walker, Stephen. G.; Wang, Hong Zhan; Gondon, Chris; Brink, Peter; Guterman, Shoshana; Zawacki, Emma; Applebaum, Eliana; Rafailovich, Miriam; Ou-Yang, H. Daniel; Mironava, Tatsiana

TiO2 is one of the most common nanoparticles in industry from food additives to energy generation. Even though TiO2 is also used as an anti-bacterial agent in combination with UV, we found that, in the absence of UV, exposure of HeLa cells to TiO2 nanoparticles largely increased their risk of bacterial invasion. HeLa cells cultured with low dosage rutile and anatase TiO2 nanoparticles (0.1 mg/ml) for 24 hrs prior to exposure to bacteria had 350% and 250% respectively more bacteria infected per cell. The increase was attributed to increased LDH leakage, and changes in the mechanical response of the cell membrane. On the other hand, macrophages exposed to TiO2 particles ingested 40% fewer bacteria, further increasing the risk of infection. In combination, these two factors raise serious concerns regarding the impact of exposure to TiO2 nanoparticles on the ability of organisms to resist bacterial infection.

Mixed matrix membranes prepared from high impact polystyrene with dispersed TiO2 nanoparticles for gas separation

Directory of Open Access Journals (Sweden)

P. Safaei

2016-01-01

Full Text Available The current study presents synthesis and characterization of high impact polystyrene - TiO2 nanoparticles mixed matrix membranes for separation of carbon dioxide from nitrogen. The solution-casting method was used for preparation of membranes. The nano mixed matrix membranes were characterized using scanning electron microscopy to ensure the suitable dispersion of nano particles in high impact polystyrene matrix. The effect of TiO2 nanoparticles loading on membrane performance was investigated. The separation performance of synthesized membranes was investigated in separation of CO2 from CO2/N2 mixture. Effect of feed pressure and TiO2 content on separation of CO2 was studied. The results revealed that increase of feed pressure decreases flux of gases through the mixed matrix membrane. The results also confirmed that the best separation performance can be obtained at TiO2 nanoparticles loading of 7 wt.%.

Evaluation of the content of TiO2 nanoparticles in the coatings of chewing gums.

Science.gov (United States)

Dudefoi, William; Terrisse, Hélène; Popa, Aurelian Florin; Gautron, Eric; Humbert, Bernard; Ropers, Marie-Hélène

2018-02-01

Titanium dioxide is a metal oxide used as a white pigment in many food categories, including confectionery. Due to differences in the mass fraction of nanoparticles contained in TiO 2 , the estimated intakes of TiO 2 nanoparticles differ by a factor of 10 in the literature. To resolve this problem, a better estimation of the mass of nanoparticles present in food products is needed. In this study, we focused our efforts on chewing gum, which is one of the food products contributing most to the intake of TiO 2 . The coatings of four kinds of chewing gum, where the presence of TiO 2 was confirmed by Raman spectroscopy, were extracted in aqueous phases. The extracts were analysed by transmission electron microscopy (TEM), X-ray diffraction, Fourier Transform Raman spectroscopy, and inductively coupled plasma atomic emission spectroscopy (ICP-AES) to establish their chemical composition, crystallinity and size distribution. The coatings of the four chewing gums differ chemically from each other, and more specifically the amount of TiO 2 varies from one coating to another. TiO 2 particles constitute the entire coating of some chewing gums, whereas for others, TiO 2 particles are embedded in an organic matrix and/or mixed with minerals like calcium carbonate, talc, or magnesium silicate. We found 1.1 ± 0.3 to 17.3 ± 0.9 mg TiO 2 particles per piece of chewing gum, with a mean diameter of 135 ± 42 nm. TiO 2 nanoparticles account for 19 ± 4% of all particles, which represents a mass fraction of 4.2 ± 0.1% on average. The intake of nanoparticles is thus highly dependent on the kind of chewing gum, with an estimated range extending from 0.04 ± 0.01 to 0.81 ± 0.04 mg of nano-TiO 2 per piece of chewing gum. These data should serve to refine the exposure scenario.

Surface characterization of poly(methylmethacrylate) based nanocomposite thin films containing Al2O3 and TiO2 nanoparticles

International Nuclear Information System (INIS)

Lewis, S.; Haynes, V.; Wheeler-Jones, R.; Sly, J.; Perks, R.M.; Piccirillo, L.

2010-01-01

Poly(methylmethacrylate) (PMMA) based nanocomposite electron beam resists have been demonstrated by spin coating techniques. When TiO 2 and Al 2 O 3 nanoparticles were directly dispersed into the PMMA polymer matrix, the resulting nanocomposites produced poor quality films with surface roughnesses of 322 and 402 nm respectively. To improve the surface of the resists, the oxide nanoparticles were encapsulated in toluene and methanol. Using the zeta potential parameter, it was found that the stabilities of the toluene/oxide nanoparticle suspensions were 7.7 mV and 19.4 mV respectively, meaning that the suspension was not stable. However, when the TiO 2 and Al 2 O 3 nanoparticles were encapsulated in methanol the zeta potential parameter was 31.9 mV and 39.2 mV respectively. Therefore, the nanoparticle suspension was stable. This method improved the surface roughness of PMMA based nanocomposite thin films by a factor of 6.6 and 6.4, when TiO 2 and Al 2 O 3 were suspended in methanol before being dispersed into the PMMA polymer.

Photoelectrochemical Performances and Potential Applications of TiO2 Nanotube Arrays Modified with Ag and Pt Nanoparticles

International Nuclear Information System (INIS)

Xu, Guangqing; Liu, Haipeng; Wang, Jinwen; Lv, Jun; Zheng, Zhixiang; Wu, Yucheng

2014-01-01

TiO 2 nanotube arrays (NTAs) modified with Ag (Ag/TiO 2 ) and Pt (Pt/TiO 2 ) nanoparticles were fabricated by anodic oxidation combined with photoreduction and hydrothermal methods, respectively. Structures, element components and morphologies of TiO 2 , Ag/TiO 2 and Pt/TiO 2 NTAs were measured by X-ray diffraction diffractometer, X-ray photoelectron spectroscopy, scanning electron microscope and transmission electron microscope. The photoeletrochemical performances of TiO 2 , Pt/TiO 2 and Ag/TiO 2 NTAs were characterized by cyclic voltammetry and amperometry in phosphate buffer solution in absence and presence of glucose. Modifications of Ag and Pt nanoparticles play different roles in the photoelectrochemical process and have different potential applications. Ag nanoparticles decrease the photocurrent in buffer solution but increase the photocurrent response to organic compounds, which is fit for electrochemical detection of organic compounds due to the low background photocurrent and high photocurrent response. Ag/TiO 2 NTAs achieve the best detection performance with sensitivity of 0.152 μA/μM and detection limit of 0.53 μM. On the contrary, Pt nanoparticles can enhance the photocurrent of TiO 2 NTAs in buffer solution but decrease the photocurrent response to organic compounds, which are benefit for photocatalytic water splitting but not for photoelectrochemical detection

Linear and nonlinear optical studies of bare and copper doped TiO2 nanoparticles via sol gel technique

Science.gov (United States)

Rajamannan, B.; Mugundan, S.; Viruthagiri, G.; Praveen, P.; Shanmugam, N.

2014-01-01

In general, the nanoparticles of TiO2 may exist in the phases of anatase, rutile and brookite. In the present work, we used titanium terta iso propoxide and 2-propanol as a common starting material to prepare the precursors of bare and copper doped nanosized TiO2. Then the synthesized products were calcinated at 500 °C and after calcination the pure TiO2 nanoparticles in anatase phase were harvested. The crystallite sizes of bare and copper doped TiO2 nanoparticles were calculated from X-ray diffraction analysis. The existence of functional groups of the samples was identified by Fourier transform infrared spectroscopy. The optical properties of bare and doped samples were carried out using UV-DRS and photoluminescence measurements. The surface morphology and the element constitution of the copper doped TiO2 nanoparticles were studied by scanning electron microscope fitted with energy dispersive X-ray spectrometer arrangement. The nonlinear optical properties of the products were confirmed by Kurtz second harmonic generation (SHG) test and the output power generated by the nanoparticle was compared with that of potassium di hydrogen phosphate (KDP).

Data on the effect of the dispersion of functionalized nanoparticles TiO2 with photocatalytic activity in LDPE

Directory of Open Access Journals (Sweden)

Alvarado Jahell

2018-02-01

Full Text Available This article contains the dataset referring to the article ''Study of the effect of the dispersion of functionalized nanoparticles TiO2 with photocatalytic activity in LDPE'' (Jahell et al., 2016 [1]. It includes the FT-IR data of the functionalized nanoparticles of TiO2 with Hexadecyltrimethoxysilane in different degrees of functionalization, thermogravimetric analysis, distribution and particle size in the polymer matrix by scanning electron microscopy (SEM, carbonyl index, gravimetry and scanning electron microscopy of the nanocomposite degraded by UV radiation.

Synthesis and characterization of TiO2/Ag/polymer ternary nanoparticles via surface-initiated atom transfer radical polymerization

International Nuclear Information System (INIS)

Park, Jung Tae; Koh, Joo Hwan; Seo, Jin Ah; Cho, Yong Soo; Kim, Jong Hak

2011-01-01

We report on the novel ternary hybrid materials consisting of semiconductor (TiO 2 ), metal (Ag) and polymer (poly(oxyethylene methacrylate) (POEM)). First, a hydrophilic polymer, i.e. POEM, was grafted from TiO 2 nanoparticles via the surface-initiated atom transfer radical polymerization (ATRP) technique. These TiO 2 -POEM brush nanoparticles were used to template the formation of Ag nanoparticles by introduction of a AgCF 3 SO 3 precursor and a NaBH 4 aqueous solution for reduction process. Successful grafting of polymeric chains from the surface of TiO 2 nanoparticles and the in situ formation of Ag nanoparticles within the polymeric chains were confirmed using transmission electron microscopy (TEM), UV-vis spectroscopy, X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). FT-IR spectroscopy also revealed the specific interaction of Ag nanoparticles with the C=O groups of POEM brushes. This study presents a simple route for the in situ synthesis of both metal and polymer confined within the semiconductor, producing ternary hybrid inorganic-organic nanomaterials.

Preparation of anatase TiO2 nanoparticles using low hydrothermal temperature for dye-sensitized solar cell

Science.gov (United States)

Sofyan, N.; Ridhova, A.; Yuwono, A. H.; Udhiarto, A.

2018-03-01

One device being developed as an alternative source of renewable energy by utilizing solar energy source is dye-sensitized solar cells (DSSC). This device works using simple photosynthetic-electrochemical principle in the molecular level. In this device, the inorganic oxide semiconductor of titanium dioxide (TiO2) has a great potential for the absorption of the photon energy from the solar energy source, especially in the form of TiO2 nanoparticle structure. This nanoparticle structure is expected to improve the performance of DSSC because the surface area to weight ratio of this nanostructures is very large. In this study, the synthesis of TiO2 nanoparticle from its precursors has been performed along with the fabrication of the DSSC device. Effort to improve the size of nanocrystalline anatase TiO2 was accomplished by low hydrothermal treatment at various temperatures whereas the crystallinity of the anatase phase in the structure was performed by calcination process. Characterization of the materials was performed using X-ray Diffraction (XRD) and scanning electron microscope (SEM), while the DSSC performance was examined through a high precision current versus voltage (I-V) curve analyzer. The results showed that pure anatase TiO2 nanoparticles could be obtained at low hydrothermal of 100, 125, and 150 °C followed by calcination at 450 °C. The best performance of photocurrent-voltage characteristic was given by TiO2 hydrothermally synthesized at 150 °C with power conversion efficiency (PCE) of 4.40 %, whereas the standard TiO2 nanoparticles has PCE only 4.02 %. This result is very promising in terms low temperature and thus low cost of anatase TiO2 semiconductor preparation for DSSC application.

Synthesis of Nd3+doped TiO2 nanoparticles and Its Optical Behaviour

Directory of Open Access Journals (Sweden)

Ezhil Arasi S.

2017-04-01

Full Text Available Pure and Rare earth ion doped TiO2 nanoparticles were synthesized by Sol-gel method. The synthesized TiO2 nanoparticles were characterized by X-ray diffraction, Raman spectroscopy, UV–Vis spectroscopy and photoluminescence emission spectra. From the UV-visible measurement, the absorption edge of Nd3+-TiO2 was shifted to a higher wavelength side with decreasing band gap. Photoluminescence emission studies reveal the energy transfer mechanism of Nd3+ doped TiO2 nanoparticles explain.

Mesoporous anatase TiO_2 microspheres with interconnected nanoparticles delivering enhanced dye-loading and charge transport for efficient dye-sensitized solar cells

International Nuclear Information System (INIS)

Chu, Liang; Qin, Zhengfei; Zhang, Qiaoxia; Chen, Wei; Yang, Jian; Yang, Jianping; Li, Xing’ao

2016-01-01

Graphical abstract: The photoelectrodes of DSSCs consisted of mesoporous anatase TiO_2 microspheres with interconnected nanoparticles. The interconnected nanoparticles enhance dye-loading capacity and charge transport. - Highlights: • The mesoporous anatase TiO_2 microspheres were synthesized by a template-free, one-step fast solvothermal process. • The mesoporous anatase TiO_2 microspheres with interconnected nanoparticles have the advantages of large surface area and connected-structure for electron transfer. • The mesoporous anatase TiO_2 microspheres were further utilized as efficient photoelectrodes for dye-sensitized solar cells. - Abstract: Mesoporous anatase TiO_2 microspheres with interconnected nanostructures meet both large surface area and connected-structure for electron transfer as ideal nano/micromaterials for application in solar cells, energy storage, catalysis, water splitting and gas sensing. In this work, mesoporous anatase TiO_2 microspheres consisting of interconnected nanoparticles were synthesized by template-free, one-step fast solvothermal process, where urea was used as capping agent to control phase and promote oriented growth. The morphology was assembled by nucleation-growth-assembly-mechanism. The mesoporous anatase TiO_2 microspheres with interconnected nanoparticles were further utilized as efficient photoelectrodes of dye-sensitized solar cells (DSSCs), which were beneficial to capacity of dye loading and charge transfer. The power conversion efficiency (PCE) based on the optimized thickness of TiO_2 photoelectrodes was up to 7.13% under standard AM 1.5 G illumination (100 mW/cm"2).

Synthesis, characterization and photocatalytic activity of Fe2O3-TiO2 nanoparticles and nanocomposites

Directory of Open Access Journals (Sweden)

M. Ahmadi Golsefidi

2016-01-01

Full Text Available In this pepper Fe2O3 nanoparticles were synthesized via a fast microwave method. Then Fe2O3-TiO2 nanocomposites were synthesized by a sonochemical-assisted method. The prepared products were characterized by X-ray diffraction pattern, scanning electron microscopy and Fourier transform infrared spectroscopy. The photocatalytic behaviour of Fe2O3-TiO2 nanocomposites was evaluated using the degradation of Rhodamine B under ultra violet irradiation. The results show that nanocomposites have applicable magnetic and photocatalytic performance.

Facile synthesis of Ag nanoparticles supported on TiO2 inverse opal with enhanced visible-light photocatalytic activity

International Nuclear Information System (INIS)

Zhao Yongxun; Yang Beifang; Xu Jiao; Fu Zhengping; Wu Min; Li Feng

2012-01-01

TiO 2 inverse opal films loaded with silver nanoparticles (ATIO) were synthesized on glass substrates. TiO 2 inverse opal (TIO) films were prepared via a sol–gel process using self-assembly of SiO 2 colloidal crystal template and a facile wet chemical route featuring an AgNO 3 precursor solution to fabricate silver nanoparticles on the TIO films. The inverse opal structure and Ag deposition physically and chemically modify titania, respectively. The catalysts were characterized by Raman spectroscopy, field-emission scanning electron microscopy, high-resolution transmission electron microscopy (HRTEM), UV–vis absorption spectra, X-ray photoelectron spectroscopy and photoluminescence spectroscopy. The HRTEM results show that Ag nanoparticles measuring 5–10 nm were evenly distributed on TIO. Both the UV- and visible-light photocatalytic activities of the samples were evaluated by analyzing the degradation of methylene blue (MB) in aqueous solution. The results reveal that the apparent reaction rate constant (k app ) of MB degradation of the sample ATIO under UV-light irradiation is approximately 1.5 times that of the conventional Ag-loaded TiO 2 film (ATF) without an ordered porous structure at an AgNO 3 concentration of 5 mM in the precursor solution. At an AgNO 3 concentration of 10 mM, the sample exhibits a k app value approximately 4.2 times that of ATF under visible-light irradiation. This enhanced visible-light photocatalytic performance can be attributed to the synergistic effect of optimized Ag nanoparticle deposition and an ordered macroporous TIO structure. Repeated cycling tests revealed that the samples showed stable photocatalytic activity, even after six repeated cycles. - Highlights: ►TiO 2 inverse opal films loaded with silver nanoparticles were synthesized. ►Physical and chemical modifications of TiO 2 were achieved simultaneously. ►The catalysts exhibited enhanced visible-light photocatalytic activity. ►The mechanism for enhanced

TiO2 (NanoParticles Extracted from Sugar-Coated Confectionery

Directory of Open Access Journals (Sweden)

Martina Lorenzetti

2017-01-01

Full Text Available As the debate about TiO2 food additive safety is still open, the present study focuses on the extraction and characterisation of TiO2 (nanoparticles added as a whitening agent to confectionary products, that is, chewing gum pellets. The aim was to (1 determine the colloidal properties of suspensions mutually containing TiO2 and all other chewing gum ingredients in biologically relevant media (preingestion conditions; (2 characterise the TiO2 (nanoparticles extracted from the chewing gum coating (after ingestion; and (3 verify their potential photocatalysis. The particle size distribution, in agreement with the zeta potential results, indicated that a small but significant portion of the particle population retained mean dimensions close to the nanosize range, even in conditions of moderate stability, and in presence of all other ingredients. The dispersibility was enhanced by proteins (i.e., albumin, which acted as surfactants and reduced particle size. The particle extraction methods involved conventional techniques and no harmful chemicals. The presence of TiO2 particles embedded in the sugar-based coating was confirmed, including 17–30% fraction in the nanorange (<100 nm. The decomposition of organics under UV irradiation proved the photocatalytic activity of the extracted (nanoparticles. Surprisingly, photocatalysis occurred even in presence of an amorphous SiO2 layer surrounding the TiO2 particles.

Synthesis and photocatalytic activity for TiO2 nanoparticles as air purification

Directory of Open Access Journals (Sweden)

Haider Adawiya

2018-01-01

Full Text Available In the present work, titanium dioxide (TiO2 nanoparticles (NP’s were prepared using sol-gel process from Titanium Tetrachloride (TiCl4 as a precursor with calcinations at two temperatures (500 and 900 °C. The effect of calcinations temperatures on the structural, optical, morphological and Root Mean Square (roughness properties were investigated by means of Scanning Electron Microscopy, X-ray Diffraction (XRD, and Atomic Force Microscopy (AFM. Bacterial inactivation was evaluated using TiO2-coated Petri dishes. A thin layer of photocatalytic TiO2 powder was deposited on glass substrate in order to investigate the self-cleaning effect of TiO2 nanoparticles in indoor and outdoor applications. Ultra-hydrophilicity was assessed by measuring the contact angle and it evaluated photolysis properties through the degradation of potassium permanganate (KMnO4 under direct sunlight. XRD analysis indicated that the structure of TiO2 was anatase at 500 °C and rutile at 900 °C calcination temperatures. As the calcination temperature increases, the crystallinity is improved and the crystallite size becomes larger. Coated films of TiO2 made the has permeability, low water contact angle and good optical activity. These are properties essential for the application of the surface of the self-cleaning. The final results illustrate that titanium dioxide can be used in the build materials to produce coated surfaces in order to minimize air pollutants that are placed in microbiologically sensitive circumference like hospitals and the food factory.

Rapid thermal melted TiO2 nano-particles into ZnO nano-rod and its application for dye sensitized solar cells

International Nuclear Information System (INIS)

Chao, Ching-Hsun; Chang, Chi-Lung; Chan, Chien-Hung; Lien, Shui-Yang; Weng, Ko-Wei; Yao, Kuo-Shan

2010-01-01

TiO 2 nano-particles with an anchored ZnO nano-rod structure were synthesized using the hydrothermal method to grow ZnO nano-rods and coated TiO 2 nano-particles on ZnO nano-rods using the rapid thermal annealing method on ITO conducting glass pre-coated with nano porous TiO 2 film. The XRD study showed that there was little difference in crystal composition for various types of TiO 2 nano-particles anchored to ZnO nano-rods. The as-prepared architecture was characterized using field-emission scanning electron microscopy (FE-SEM). Films with TiO 2 nano-particles anchored to ZnO nano-rods were used as electrode materials to fabricate dye sensitized solar cells (DSSCs). The best solar energy conversion efficiency of 2.397% was obtained by modified electrode material, under AM 1.5 illumination, achieved up to J sc = 15.382 mA/cm 2 , V oc = 0.479 V and fill factor = 32.8%.

Control of Electron Transfer from Lead-Salt Nanocrystals to TiO 2

KAUST Repository

Hyun, Byung-Ryool

2011-05-11

The roles of solvent reorganization energy and electronic coupling strength on the transfer of photoexcited electrons from PbS nanocrystals to TiO 2 nanoparticles are investigated. We find that the electron transfer depends only weakly on the solvent, in contrast to the strong dependence in the nanocrystal-molecule system. This is ascribed to the larger size of the acceptor in this system, and is accounted for by Marcus theory. The electronic coupling of the PbS and TiO 2 is varied by changing the length, aliphatic and aromatic structure, and anchor groups of the linker molecules. Shorter linker molecules consistently lead to faster electron transfer. Surprisingly, linker molecules of the same length but distinct chemical structures yield similar electron transfer rates. In contrast, the electron transfer rate can vary dramatically with different anchor groups. © 2011 American Chemical Society.

Development of DNA biosensor based on TiO2 nanoparticles

Science.gov (United States)

Nadzirah, Sh.; Hashim, U.; Rusop, M.

2018-05-01

A novel technique of DNA hybridization on the TiO2 nanoparticles film was developed by dropping a single droplet of target DNA onto the surface of TiO2 for the study of various concentrations of target DNA. The surface of TiO2 nanoparticle film was functionalized with APTES and covalently immobilized with 1 µM probe DNA on the silanized TiO2 nanoparticles surface. The effect of silanization, immobilization and hybridization were quantitatively measured by the output current signal obtained using a picoammeter. The 1 µM target DNA was found to be the most effective target towards the 1 µM probe DNA as the output current signal was within range; while the output current signal of the 10 µM target DNA was observed to beyond the range of the probe DNA control due to the excessive concentration as compared to the probe DNA. This approach has several advantages such as rapid, simple, low cost, and sensitive current signal during detection of different target DNA concentrations.

Plasma-induced synthesis of Pt nanoparticles supported on TiO2 nanotubes for enhanced methanol electro-oxidation

Science.gov (United States)

Su, Nan; Hu, Xiulan; Zhang, Jianbo; Huang, Huihong; Cheng, Jiexu; Yu, Jinchen; Ge, Chao

2017-03-01

A Pt/C/TiO2 nanotube composite catalyst was successfully prepared for enhanced methanol electro-oxidation. Pt nanoparticles with a particle size of 2 nm were synthesized by plasma sputtering in water, and anatase TiO2 nanotubes with an inner diameter of approximately 100 nm were prepared by a simple two-step anodization method and annealing process. Field-emission scanning electron microscopy images indicated that the different morphologies of TiO2 synthesized on the surface of Ti foils were dependent on the different anodization parameters. The electrochemical performance of Pt/C/TiO2 catalysts for methanol oxidation showed that TiO2 nanotubes were more suitable for use as Pt nanoparticle support materials than irregular TiO2 short nanorods due to their tubular morphology and better electronic conductivity. X-ray photoelectron spectroscopy characterization showed that the binding energies of the Pt 4f of the Pt/C/TiO2 nanotubes exhibited a slightly positive shift caused by the relatively strong interaction between Pt and the TiO2 nanotubes, which could mitigate the poisoning of the Pt catalyst by COads, and further enhance the electrocatalytic performance. Thus, the as-obtained Pt/C/TiO2 nanotubes composites may become a promising catalyst for methanol electro-oxidation.

Synthesis of TiO2 nanoparticles containing Fe, Si, and V using multiple diffusion flames and catalytic oxidation capability of carbon-coated nanoparticles

KAUST Repository

Ismail, Mohamed; Memon, Nasir K.; Hedhili, Mohamed N.; Anjum, Dalaver H.; Chung, Suk-Ho

2016-01-01

Titanium dioxide (TiO2) nanoparticles containing iron, silicon, and vanadium are synthesized using multiple diffusion flames. The growth of carbon-coated (C–TiO2), carbon-coated with iron oxide (Fe/C–TiO2), silica-coated (Si–TiO2), and vanadium-doped (V–TiO2) TiO2 nanoparticles is demonstrated using a single-step process. Hydrogen, oxygen, and argon are utilized to establish the flame, with titanium tetraisopropoxide (TTIP) as the precursor for TiO2. For the growth of Fe/C–TiO2 nanoparticles, TTIP is mixed with xylene and ferrocene. While for the growth of Si–TiO2 and V–TiO2, TTIP is mixed with hexamethyldisiloxane (HMDSO) and vanadium (V) oxytriisopropoxide, respectively. The synthesized nanoparticles are characterized using high-resolution transmission electron microscopy (HRTEM) with energy-filtered TEM for elemental mapping (of Si, C, O, and Ti), X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), nitrogen adsorption BET surface area analysis, and thermogravimetric analysis. Anatase is the dominant phase for the C–TiO2, Fe/C–TiO2, and Si–TiO2 nanoparticles, whereas rutile is the dominant phase for the V–TiO2 nanoparticles. For C–TiO2 and Fe/C–TiO2, the nanoparticles are coated with about 3-5-nm thickness of carbon. The iron-based TiO2 nanoparticles significantly improve the catalytic oxidation of carbon, where complete oxidation of carbon occurs at a temperature of 470 °C (with iron) compared to 610 °C (without iron). Enhanced catalytic oxidation properties are also observed for model soot particles, Printex-U, when mixed with Fe/C-TiO2. With regards to Si–TiO2 nanoparticles, a uniform coating of 3 to 8 nm of silicon dioxide is observed around the TiO2 particles. This coating mainly occurs due to variance in the chemical reaction rates of the precursors. Finally, with regards to V–TiO2, vanadium is doped within the TiO2 nanoparticles as visualized by HRTEM and XPS further confirms the formation of

Synthesis of TiO2 nanoparticles containing Fe, Si, and V using multiple diffusion flames and catalytic oxidation capability of carbon-coated nanoparticles

KAUST Repository

Ismail, Mohamed

2016-01-19

Titanium dioxide (TiO2) nanoparticles containing iron, silicon, and vanadium are synthesized using multiple diffusion flames. The growth of carbon-coated (C–TiO2), carbon-coated with iron oxide (Fe/C–TiO2), silica-coated (Si–TiO2), and vanadium-doped (V–TiO2) TiO2 nanoparticles is demonstrated using a single-step process. Hydrogen, oxygen, and argon are utilized to establish the flame, with titanium tetraisopropoxide (TTIP) as the precursor for TiO2. For the growth of Fe/C–TiO2 nanoparticles, TTIP is mixed with xylene and ferrocene. While for the growth of Si–TiO2 and V–TiO2, TTIP is mixed with hexamethyldisiloxane (HMDSO) and vanadium (V) oxytriisopropoxide, respectively. The synthesized nanoparticles are characterized using high-resolution transmission electron microscopy (HRTEM) with energy-filtered TEM for elemental mapping (of Si, C, O, and Ti), X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), nitrogen adsorption BET surface area analysis, and thermogravimetric analysis. Anatase is the dominant phase for the C–TiO2, Fe/C–TiO2, and Si–TiO2 nanoparticles, whereas rutile is the dominant phase for the V–TiO2 nanoparticles. For C–TiO2 and Fe/C–TiO2, the nanoparticles are coated with about 3-5-nm thickness of carbon. The iron-based TiO2 nanoparticles significantly improve the catalytic oxidation of carbon, where complete oxidation of carbon occurs at a temperature of 470 °C (with iron) compared to 610 °C (without iron). Enhanced catalytic oxidation properties are also observed for model soot particles, Printex-U, when mixed with Fe/C-TiO2. With regards to Si–TiO2 nanoparticles, a uniform coating of 3 to 8 nm of silicon dioxide is observed around the TiO2 particles. This coating mainly occurs due to variance in the chemical reaction rates of the precursors. Finally, with regards to V–TiO2, vanadium is doped within the TiO2 nanoparticles as visualized by HRTEM and XPS further confirms the formation of

Time-dependent translocation and potential impairment on central nervous system by intranasally instilled TiO2 nanoparticles

International Nuclear Information System (INIS)

Wang Jiangxue; Liu Ying; Jiao Fang; Lao Fang; Li Wei; Gu Yiqun; Li Yufeng; Ge Cuicui; Zhou Guoqiang; Li Bai; Zhao Yuliang; Chai Zhifang; Chen Chunying

2008-01-01

Nanoparticles can be administered via nasal, oral, intraocular, intratracheal (pulmonary toxicity), tail vein and other routes. Here, we focus on the time-dependent translocation and potential damage of TiO 2 nanoparticles on central nervous system (CNS) through intranasal instillation. Size and structural properties are important to assess biological effects of TiO 2 nanoparticles. In present study, female mice were intranasally instilled with two types of well-characterized TiO 2 nanoparticles (i.e. 80 nm, rutile and 155 nm, anatase; purity > 99%) every other day. Pure water instilled mice were served as controls. The brain tissues were collected and evaluated for accumulation and distribution of TiO 2 , histopathology, oxidative stress, and inflammatory markers at post-instillation time points of 2, 10, 20 and 30 days. The titanium contents in the sub-brain regions including olfactory bulb, cerebral cortex, hippocampus, and cerebellum were determined by inductively coupled plasma mass spectrometry (ICP-MS). Results indicated that the instilled TiO 2 directly entered the brain through olfactory bulb in the whole exposure period, especially deposited in the hippocampus region. After exposure for 30 days, the pathological changes were observed in the hippocampus and olfactory bulb using Nissl staining and transmission electron microscope. The oxidative damage expressed as lipid peroxidation increased significantly, in particular in the exposed group of anatase TiO 2 particles at 30 days postexposure. Exposure to anatase TiO 2 particles also produced higher inflammation responses, in association with the significantly increased tumor necrosis factor alpha (TNF-α) and interleukin (IL-1β) levels. We conclude that subtle differences in responses to anatase TiO 2 particles versus the rutile ones could be related to crystal structure. Thus, based on these results, rutile ultrafine-TiO 2 particles are expected to have a little lower risk potential for producing adverse

Low temperature fabrication of V-doped TiO2 nanoparticles, structure and photocatalytic studies

International Nuclear Information System (INIS)

Liu Baoshun; Wang Xuelai; Cai Guofa; Wen Liping; Song Yanbao; Zhao Xiujian

2009-01-01

V-doped TiO 2 nanoparticles were synthesized at low temperature and characterized by X-ray diffraction (XRD), Raman spectroscopy (RS), transmission electron microscopy (TEM), Brunauer-Emmet-Teller (BET), X-ray photoelectron spectroscopy (XPS), UV-vis spectroscopy, and photoluminescence (PL) spectroscopy, respectively. It is found the nanoparticle shape changed from needle, to short stick and then to cubic with the increase of doped V concentration, which was also accompanied by the improvement of crystallinity. The specific surface area (S BET ) decreased with increasing V content. It is confirmed that V ions can be doped in TiO 2 by substituting Ti 4+ ions, which suppressed the CB → VB and surface recombination of photoinduced electrons and holes, and a relation was found between the PL spectra and the UV photocatalytic activity. There was an optimum V content for the V-doped TiO 2 to present the best UV-light induced photoactivity, but they were visible-inactive. At last, the effect of the doping V as trapping centers on photocatalysis was investigated in detail, and used to explain the difference between the photocatalysis under the illumination of UV light and visible light.

Hierarchical top-porous/bottom-tubular TiO 2 nanostructures decorated with Pd nanoparticles for efficient photoelectrocatalytic decomposition of synergistic pollutants

KAUST Repository

Zhang, Zhonghai

2012-02-22

In this paper, top-porous and bottom-tubular TiO 2 nanotubes (TiO 2 NTs) loaded with palladium nanoparticles (Pd/TiO 2 NTs) were fabricated as an electrode for an enhanced photoelectrocatalytic (PEC) activity toward organic dye decomposition. TiO 2 NTs with a unique hierarchical top-porous and bottom-tubular structure were prepared by a facile two-step anodization method and Pd nanoparticles were decorated onto the TiO 2 NTs via a photoreduction process. The PEC activity of Pd/TiO 2 NTs was investigated by decomposition of methylene blue (MB) and Rhodamine B (RhB). Because of formation Schottky junctions between TiO 2 and Pd, which significantly promoted the electron transfer and reduced the recombination of photogenerated electrons and holes, the Pd/TiO 2 NT electrode showed significantly higher PEC activities than TiO 2 NTs. Interestingly, an obvious synergy between two dyes was observed and corresponding mechanism based on facilitated transfer of electrons and holes as a result of a suitable energy level alignment was suggested. The findings of this work provide a fundamental insight not only into the fabrication but also utility of Schottky junctions for enhanced environmental remediation processes. © 2012 American Chemical Society.

Electronic structure and size of TiO sub 2 nanoparticles of controlled size prepared by aerosol methods

CERN Document Server

Soriano, L; Sanchez-Agudo, M; Sanz, J M; Ahonen, P P; Kauppinen, E I; Palomares, F J; Bressler, P R

2002-01-01

A complete characterization of nanostructures has to deal both with electronic structure and dimensions. Here we present the characterization of TiO sub 2 nanoparticles of controlled size prepared by aerosol methods. The electronic structure of these nanoparticles was probed by x-ray absorption spectroscopy (XAS), the particle size by atomic force microscopy (AFM). XAS spectra show that the particles crystallize in the anatase phase upon heating at 500 sup o C, whereas further annealing at 700 sup o C give crystallites of 70 % anatase and 30 % rutile phases. Raising the temperature to 900 sup o C results in a complete transformation of the particles to rutile. AFM images reveal that the mean size of the anatase particles formed upon heating at 500 sup o C is 30 nm, whereas for the rutile particles formed upon annealing at 900 sup o C 90 nm were found. The results obtained by these techniques agree with XRD data. (author)

Enhancement of Dye-Sensitized Solar Cells Efficiency Using Mixed-Phase TiO2 Nanoparticles as Photoanode

Directory of Open Access Journals (Sweden)

Yi-Hua Fan

2017-01-01

Full Text Available Dye-sensitized solar cell (DSSC is a potential candidate to replace conventional silicon-based solar cells because of high efficiency, cheap cost, and lower energy consumption in comparison with silicon chip manufacture. In this report, mixed-phase (anatase and rutile nanoparticles TiO2 photoanode was synthesized to investigate material characteristics, carriers transport, and photovoltaic performance for future DSSC application. Field-emission scanning electron microscope (SEM, X-ray diffraction (XRD, photoluminescence (PL, and UV-visible spectroscopy were used to characterize mixed TiO2 particles. Subsequently, various mixed-phase TiO2 anodes in DSSC devices were measured by electrical impedance spectra (EIS and energy efficiency conversion. The overall energy conversion efficiency of DSSC chip was improved as a result of the increase of rutile phase of TiO2 (14% in anatase matrix. Synergistic effects including TiO2 crystallization, reduction of defect density level in energy band, longer lifetime of photoexcited electrons, and lower resistance of electron pathway all contributed to high efficiency of light energy conversion.

The Influence of TiO2 Nanoparticles on LaFeO3/TiO2 Nanocomposites for Reduction of Aqueous Organic Dyes

International Nuclear Information System (INIS)

Afifah, N.; Saleh, R.

2016-01-01

A series of Lanthanum ferrite (LaFeO3) nanoparticles over titanium dioxide (TiO2) were synthesized using sol-gel method at room temperature by varying the loading of LaFeO3 on TiO2. The magnetic properties of samples were measured using vibrating sample magnetometer and photosonocatalytic activity towards the degradation of methylene blue under light (UV or visible) and ultrasound irradiation was also evaluated. The morphology and structure of the samples were characterized by field emission scanning electron microscope, energy dispersive analysis and X-ray diffraction. Furthermore the optical properties were also characterized by UV-visible diffuse reflectance. The experimental results showed that the prepared perovskites had sphere-like shape and strong visible light absorption. LaFeO3 demonstrated ferromagnetic properties and the magnetization decreased with the incorporation of TiO2 in the samples. However, the incorporation of TiO2 increased the photosonocatalytic activity and extended the photoresponding to UV light. (paper)

The Effect of Process Parameters on the Synthesis of Ti and TiO2 Nanoparticles Producted by Electromagnetic Levitational Gas Condensation

Directory of Open Access Journals (Sweden)

Maryam Moazeni

2012-10-01

Full Text Available The nanoparticles of Ti and TiO2 have attracted extensive research interest because of their diverse applications in, for instance, catalysis, energy conversion, pigment and cosmetic manufacturing and biomedical engineering. Through this project, a one-step bulk synthesis method of electromagnetic levitational gas condensation (ELGC was utilized for the synthesis of monodispersed and crystalline Ti and TiO2 nanoparticles. Within the process, the Ti vapours ascending from the high temperature levitated droplet were condensed by an argon gas stream under atmospheric pressure. The TiO2 nanoparticles were produced by simultaneous injection of argon and oxygen into the reactor. The effects of flow rate of the condensing and oxidizing gases on the size and the size distribution of the nanoparticles were investigated. The particles were characterized by scanning electron microscopy (SEM, X-ray diffraction (XRD and image analysis. The process parameters for the synthesis of the crystalline Ti and TiO2 nanoparticles were determined.

Enhanced photocatalytic degradation of dyes under sunlight using biocompatible TiO2 nanoparticles

Science.gov (United States)

Bharati, B.; Sonkar, A. K.; Singh, N.; Dash, D.; Rath, Chandana

2017-08-01

As TiO2 is one of the most popular photocatalysts, we have studied here the photocatalytic degradation of the most common dyestuffs like rhodamine B (RhB), congo red (CR) and methylene blue (MB), which mainly come from the textile and photographic industries using nanoparticles of TiO2. Nanoparticles of TiO2 synthesized through a simple and cost effective sol-gel technique crystallizes in the anatase phase, showing a band gap less than that of bulk value. Particles consisting of coherently scattered domains of size 33 nm are found to be agglomerated and polycrystalline in nature. While the degradation rates of MB, CR and RhB after irradiating with a renewable source of energy, i.e. sunlight, show 100% degradation, TiO2 irradiated with UV light of 4.8 eV shows a much slower degradation rate. To use the waste water after photocatalysis, we examine further the biocompatibile nature of the TiO2 nanoparticles by platelet interaction activity, hemolysis effect and MTT assay. It is worth mentioning here that TiO2 nanoparticles are found to be highly hemocompatible, show no platelet aggregation, and the level of intracellular ROS in human platelets does not show significant change in ROS level. We conclude that TiO2 nanoparticles constitute an excellent photocatalyst and biocompatible material, and that after photocatalytic degradation of dye effluents obtained from textile industries, purified water can be used in agriculture and domestic sectors.

Enhanced photoelectrocatalytic degradation of 2,4-dichlorophenoxyacetic acid by CuInS2 nanoparticles deposition onto TiO2 nanotube arrays

International Nuclear Information System (INIS)

Liu Ronghua; Liu Yutang; Liu Chengbin; Luo Shenglian; Teng Yarong; Yang Lixia; Yang Renbin; Cai Qingyun

2011-01-01

Research highlights: → The photocatalytic application of CuInS 2 with a direct band gap of about 1.5 eV and a high absorption coefficient remains unknown. → We describe an impulse electrodeposition approach to deposit CuInS 2 nanoparticles in uniform size of about 20 nm onto the top surface of the highly oriented TiO 2 NT arrays while minimizing the clogging of the tube entrances. → The novel photocatalyst exhibits a highly visible-light photocatalytic degradation activity for the target organic pollutant. → Moreover, the stability of the modified TiO 2 NT is good. → Therefore, CuInS 2 nanoparticles modified TiO 2 NT photocatalysts have potential utility in practical purification of organic wastewater. - Abstract: Surface modification of TiO 2 nanotube (NT) arrays with CuInS 2 nanoparticles (NPs) for photocatalytic degradation of 2,4-dichlorophenoxyacetic acid (2,4-D) was reported. A pulse electrodeposition technique was used to prepare the CuInS 2 NPs, and the resulted CuInS 2 NPs, with a uniform size of about 20 nm, were found to deposit on the top surface of the highly oriented TiO 2 NT while without clogging the tube entrances. Compared with the unmodified TiO 2 NT, the CuInS 2 NPs modified TiO 2 NT (CuInS 2 -TiO 2 NT) showed significantly enhanced photocatalytic activity towards 2,4-D under visible light. After 160 min irradiation, the removal rate of 2,4-D is 100% by using CuInS 2 -TiO 2 NT, much higher than 65.2% by using the unmodified TiO 2 NT in photoelectrocatalytic process. The increased photodegradation efficiency mainly results from the improved photocurrent density as results of enhanced visible-light absorption and decreased hole-electron recombination due to the presence of narrow-band-gap p-type semiconductor CuInS 2 .

XRD analysis of undoped and Fe doped TiO2 nanoparticles by Williamson Hall method

International Nuclear Information System (INIS)

Bharti, Bandna; Barman, P. B.; Kumar, Rajesh

2015-01-01

Undoped and Fe doped titanium dioxide (TiO 2 ) nanoparticles were synthesized by sol-gel method at room temperature. The synthesized samples were annealed at 500°C. For structural analysis, the prepared samples were characterized by X-ray diffraction (XRD). The crystallite size of TiO 2 and Fe doped TiO 2 nanoparticles were calculated by Scherer’s formula, and was found to be 15 nm and 11 nm, respectively. Reduction in crystallite size of TiO 2 with Fe doping was observed. The anatase phase of Fe-doped TiO 2 nanoparticles was also confirmed by X-ray diffraction. By using Williamson-Hall method, lattice strain and crystallite size were also calculated. Williamson–Hall plot indicates the presence of compressive strain for TiO 2 and tensile strain for Fe-TiO 2 nanoparticles annealed at 500°C

Influences of Stacking Architectures of TiO2 Nanoparticle Layers on Characteristics of Dye-Sensitized Solar Cells

Directory of Open Access Journals (Sweden)

Chih-Hung Tsai

2013-01-01

Full Text Available We investigated the influences of stacking architectures of the TiO2 nanoparticle layers on characteristics and performances of DSSCs. TiO2 nanoparticles of different sizes and compositions were characterized for their morphological and optical/scattering properties in thin films. They were used to construct different stacking architectures of the TiO2 nanoparticle layers for use as working electrodes of DSSCs. Characteristics and performances of DSSCs were examined to establish correlation of the stacking architectures of TiO2 nanoparticle layers with characteristics of DSSCs. The results suggest that the three-layer DSSC architecture, with sandwiching a 20 nm TiO2 nanoparticle layer between a 37 nm TiO2 nanoparticle layer and a hundred nm sized TiO2 back scattering/reflection layer, is effective in enhancing DSSC efficiencies. The high-total-transmittance 37 nm TiO2 nanoparticle layer with a larger haze can serve as an effective front scattering layer to scatter a portion of the incident light into larger oblique angles and therefore increase optical paths and absorption.

Temperature effect on the nucleation and growth of TiO2 colloidal nanoparticles

Directory of Open Access Journals (Sweden)

Morteza Sasani Ghamsari

2017-01-01

Full Text Available The nucleation and growth of sol-gel derived TiO2 colloidal nanoparticles have been studied using  experiment and theory as well. In this study, the temperature effect on the formation of TiO2 nanoparticles was discussed and some effective parameters such as the supply rate of solute (Q0, the mean volumic growth rate of stable nuclei during the nucleation period (u, the diffusion coefficient of [Ti]+4 ions and the nucleus size were determined. The formation of TiO2 nanoparticles in three different temperatures (60, 70 and 80°C was studied. The obtained results showed that the process temperature has a considerable impact on the nucleation and growth of TiO2 nanoparticles. It can be concluded that  increasing the temperature leads to a decrease of the supersaturation and an increase of the nucleus size, supply rate of monomer, nanoparticles density and growth rate as evident from LaMer diagram.

A theoretical investigation of the interaction of Immucillin-A with N-doped TiO2 anatase nanoparticles: Applications to nanobiosensors and nanocarriers

Directory of Open Access Journals (Sweden)

Amirali Abbasi

2017-02-01

Full Text Available Objective(s: Adsorption of IMMUCILLIN-A (BCX4430 molecule on the pristine and N-doped TiO2 anatase nanoparticles were studied using the density functional theory (DFT calculations. The adsorption energy analysis indicated that TiO2+IMMUCILLIN-A complexes including OC-substituted TiO2 have higher adsorption energy than the complexes with OT substituted TiO2, thus providing more stable configurations. Methods: The structural properties including bond lengths, adsorption energies and bond angles were analysed. The electronic structure of the adsorption system were investigated in view of the density of states, molecular orbitals and Mulliken charge analysis.Results: The results show that, the interaction of IMMUCILLIN-A drug with N-doped TiO2 nanoparticles is more energetically favorable than the interaction with the pristine ones, suggesting that the N-doped nanoparticles can react with IMMUCILLIN-A drug more efficiently. The Mulliken charge analysis also suggests a charge transfer from IMMUCILLIN-A molecule to the TiO2 nanoparticle.Conclusions: Based on obtained results, it can be concluded that the N-doped TiO2 nanoparticle could be utilized as an efficient candidate for application as highly sensitive nanobiosensors and efficient nanocarriers for IMMUCILLIN-A drugs.

Antimicrobial Activities of TiO2 Nanoparticle Against Escherichia coli and Staphylococcus aureus

Directory of Open Access Journals (Sweden)

F Barzegary

2010-04-01

Full Text Available Introduction: Organic antibacterial materials have been used as insecticides and bactericides for many years. Unfortunately, high temperatures in manufacturing process reduce their antibacterial properties. However, inorganic materials of antibacterial agents have excellent bacterial resistance and thermal stability. Over the past few decades, inorganic nanoparticles whose structures exhibit significantly novel and improved physical, chemical and biological properties and functionality due to their nano-scale size have elicited much interest. methods:The aim of this study was to investigate the antibacterial properties of one kind of nano-specimen (TiO2 nanoparticle against Escherichia coli and Streptococcus aureus. Our study was research perusal. In the first study, the optical density of E. coli and S. aureus cultures were observed in the presence of 0.01%, 0.75% and 1.5% of TiO2. In the second study, 6.3 log CFU/ml of E. coli and S. areus were separately exposed to 1.5% TiO2 at 37 ºC in water. In third study, we studied thew growth of E.coli in solid medium with and without nanoparticles. Results: The presence of 0.01% TiO2 nanoparticles didn’t have a statistically significant effect, but in the presence of 0.75% and 1.5% nanoparticles, the bacterial colonies decreased significantly. In the control group, bacterial cells survival was nearly 13 days, while complete cell death of E. coli was seen when 1.5% TiO2 was applied for 24 hours. The same experiment for S. aureu, showed that complete cell death occured when the bacterial culture was exposed to 1.5% TiO2 for 16 hours.. It was shown that presence of 1.5% TiO2 in the solid medium suppressed the growth of E. coli 5.6 times more (p < 0.001. Discussion: Our findings showed antibacterial effects of TiO2 nanoparticles against both bacteria, but S. areus bacteria were more sensitive to nanoparticles as compared to E. coli bacteria

Influence of TiO2 Nanoparticles on Growth, Chemical Constituents and Toxicity of Fennel Plant

International Nuclear Information System (INIS)

Khater, M.S.; Osman, Y.A.H.

2015-01-01

The present work is carried out to evaluate the effect of TiO 2 nanoparticles treatments on fennel (Feoniculum Vulgare Mill) plants. The plants were sprayed with different concentrations of TiO 2 nanoparticles 2, 4 and 6 ppm. In most cases, the tallest plants, the highest number of branches , the highest fruit yield per plant and the highest values of Pigments, Carbohydrates, Sugars nitrogen , phosphorus , potassium were obtained from the treatment of 6 ppm TiO 2 nanoparticles of fennel . Results showed that sprayed fennel plant with concentrations of TiO 2 nanoparticles 0, 2, 4 and 6 ppm is safe and enhanced chlorophyll synthesis and consequently enhanced photosynthesis

Visible-light photocatalytic performances of TiO2 nanoparticles modified by trace derivatives of PVA

Directory of Open Access Journals (Sweden)

Le SHI

2016-10-01

Full Text Available In order to study the visible-light photocatalytic activity and catalysis stability of nanocomposites, a TiO2-based visible-light photocatalyst is prepared by surface-modification of TiO2 nanoparticles using trace conjugated derivatives from polyvinyl alcohol (DPVA via a facile method. The obtained DPVA/TiO2 nanocomposites are characterized by X-ray diffraction (XRD, Fourier transform infrared Spectra (FT-IR, scanning electron microscopy (SEM, UV-vis diffuse reflection spectroscopy (DRS, and X-ray photoelectron spectroscopy (XPS. With Rhodamine B (RhB as a model pollutant, the visible-light photocatalytic activity and stability of DPVA/TiO2 nanocomposites are investigated by evaluating the RhB decomposition under visible light irradiation. The results reveal that the trace conjugated polymers on the TiO2 surface doesn’t change the crystalline and crystal size of TiO2 nanoparticles, but significantly enhances their visible-light absorbance and visible-light photocatalytic activity. The nanocomposite with the PVA and TiO2 mass ratio of 1∶200 exhibits the highest visible-light photocatalytic activity. The investigated nanocomposites exhibit well visible-light photoctatalytic stability. The photogenerated holes are thought as the main active species for the RhB photodegradation in the presence of the DPVA/TiO2 nanocomposites.

Studied Localized Surface Plasmon Resonance Effects of Au Nanoparticles on TiO2 by FDTD Simulations

Directory of Open Access Journals (Sweden)

Guo-Ying Yao

2018-06-01

Full Text Available Localized surface plasmon resonance (LSPR plays a significant role in the fields of photocatalysis and solar cells. It can not only broaden the spectral response range of materials, but also improve the separation probability of photo-generated electron-hole pairs through local field enhancement or hot electron injection. In this article, the LSPR effects of Au/TiO2 composite photocatalyst, with different sizes and shapes, have been simulated by the finite difference time domain (FDTD method. The variation tendency of the resonance-absorption peaks and the intensity of enhanced local enhanced electric field were systematically compared and emphasized. When the location of Au nanosphere is gradually immersed into the TiO2 substrate, the local enhanced electric field of the boundary is gradually enhanced. When Au nanoshperes are covered by TiO2 at 100 nm depths, the local enhanced electric field intensities reach the maximum value. However, when Au nanorods are loaded on the surface of the TiO2 substrate, the intensity of the corresponding enhanced local enhanced electric field is the maximum. Au nanospheres produce two strong absorption peaks in the visible light region, which are induced by the LSPR effect and interband transitions between Au nanoparticles and the TiO2 substrate. For the LSPR resonance-absorption peaks, the corresponding position is red-shifted by about 100 nm, as the location of Au nanospheres are gradually immersed into the TiO2 substrate. On the other hand, the size change of the Au nanorods do not lead to a similar variation of the LSPR resonance-absorption peaks, except to change the length-diameter ratio. Meanwhile, the LSPR effects are obviously interfered with by the interband transitions between the Au nanorods and TiO2 substrate. At the end of this article, three photo-generated carrier separation mechanisms are proposed. Among them, the existence of direct electron transfer between Au nanoparticles and the TiO2

Uniform Gold-Nanoparticle-Decorated {001}-Faceted Anatase TiO2 Nanosheets for Enhanced Solar-Light Photocatalytic Reactions.

Science.gov (United States)

Shi, Huimin; Zhang, Shi; Zhu, Xupeng; Liu, Yu; Wang, Tao; Jiang, Tian; Zhang, Guanhua; Duan, Huigao

2017-10-25

The {001}-faceted anatase TiO 2 micro-/nanocrystals have been widely investigated for enhancing the photocatalysis and photoelectrochemical performance of TiO 2 nanostructures, but their practical applications still require improved energy conversion efficiency under solar-light and enhanced cycling stability. In this work, we demonstrate the controlled growth of ultrathin {001}-faceted anatase TiO 2 nanosheets on flexible carbon cloth for enhancing the cycling stability, and the solar-light photocatalytic performance of the synthesized TiO 2 nanosheets can be significantly improved by decorating with vapor-phase-deposited uniformly distributed plasmonic gold nanoparticles. The fabricated Au-TiO 2 hybrid system shows an 8-fold solar-light photocatalysis enhancement factor in photodegrading Rhodamine B, a high photocurrent density of 300 μA cm -2 under the illumination of AM 1.5G, and 100% recyclability under a consecutive long-term cycling measurement. Combined with electromagnetic simulations and systematic control experiments, it is believed that the tandem-type separation and transition of plasmon-induced hot electrons from Au nanoparticles to the {001} facet of anatase TiO 2 , and then to the neighboring {101} facet, is responsible for the enhanced solar-light photochemical performance of the hybrid system. The Au-TiO 2 nanosheet system addresses well the problems of the limited solar-light response of anatase TiO 2 and fast recombination of photogenerated electron-hole pairs, representing a promising high-performance recyclable solar-light-responding system for practical photocatalytic reactions.

TiO2 Nanoparticles as a Soft X-ray Molecular Probe

Energy Technology Data Exchange (ETDEWEB)

Larabell, Carolyn; Ashcroft, Jared M.; Gu, Weiwei; Zhang, Tierui; Hughes, Steven M.; Hartman, Keith B.; Hofmann, Cristina; Kanaras, Antonios G.; Kilcoyne, David A.; Le Gros, Mark; Yin, Yadong; Alivisatos, A. Paul; Larabell, Carolyn A.

2007-06-30

With the emergence of soft x-ray techniques for imaging cells, there is a pressing need to develop protein localization probes that can be unambiguously identified within the region of x-ray spectrum used for imaging. TiO2 nanocrystal colloids, which have a strong absorption cross-section within the "water-window" region of x-rays, areideally suited as soft x-ray microscopy probes. To demonstrate their efficacy, TiO2-streptavidin nanoconjugates were prepared and subsequently labeled microtubules polymerized from biotinylated tubulin. The microtubules were imaged using scanning transmission x-ray microscopy (STXM), and the TiO2 nanoparticle tags were specifically identified using x-ray absorption near edge spectroscopy (XANES). These experiments demonstrate that TiO2 nanoparticles are potential probes for protein localization analyses using soft x-ray microscopy.

Photocatalytic degradation of methylene blue on Fe3+-doped TiO2 nanoparticles under visible light irradiation

Institute of Scientific and Technical Information of China (English)

SU Bitao; WANG Ke; BAI Jie; MU Hongmei; TONG Yongchun; MIN Shixiong; SHE Shixiong; LEI Ziqiang

2007-01-01

Fe3+-doped TiO2 composite nanoparticles with different doping amounts were successfully synthesized using sol-gel method and characterized by X-ray diffraction (XRD),transmission electron microscopy (TEM) and ultraviolet-visible spectroscopy (UV-Vis) diffuse reflectance spectra (DRS). The photocatalytic degradation of methylene blue was used as a model reaction to evaluate the photocatalytic activity of Fe3+/TiO2 nanoparticles under visible light irradia-tion. The influence of doping amount of Fe3+ (ω: 0.00%-3.00%) on photocatalytic activities of TiO2 was investigated.Results show that the size of Fe3+/TiO2 particles decreases with the increase of the amount of Fe3+ and their absorptionspectra are broaden and absorption intensities are also increased. Doping Fe3+ can control the conversion of TiO2 from anatase to rutile. The doping amount of Fe3+ remarkably affects the activity of the catalyst, and the optimum efficiency occurs at about the doping amount of 0.3%. The appropriate doping of Fe3+ can markedly increase the catalytic activity of TiO2 under visible light irradiation.

Fate of pristine TiO2 nanoparticles and aged paint-containing TiO2 nanoparticles in lettuce crop after foliar exposure.

Science.gov (United States)

Larue, Camille; Castillo-Michel, Hiram; Sobanska, Sophie; Trcera, Nicolas; Sorieul, Stéphanie; Cécillon, Lauric; Ouerdane, Laurent; Legros, Samuel; Sarret, Géraldine

2014-05-30

Engineered TiO2 nanoparticles (TiO2-NPs) are present in a large variety of consumer products, and are produced in largest amount. The building industry is a major sector using TiO2-NPs, especially in paints. The fate of NPs after their release in the environment is still largely unknown, and their possible transfer in plants and subsequent impacts have not been studied in detail. The foliar transfer pathway is even less understood than the root pathway. In this study, lettuces were exposed to pristine TiO2-NPs and aged paint leachate containing TiO2-NPs and microparticles (TiO2-MPs). Internalization and in situ speciation of Ti were investigated by a combination of microscopic and spectroscopic techniques. Not only TiO2-NPs pristine and from aged paints, but also TiO2-MPs were internalized in lettuce leaves, and observed in all types of tissues. No change in speciation was noticed, but an organic coating of TiO2-NPs is likely. Phytotoxicity markers were tested for plants exposed to pristine TiO2-NPs. No acute phytotoxicity was observed; variations were only observed in glutathione and phytochelatin levels but remained low as compared to typical values. These results obtained on the foliar uptake mechanisms of nano- and microparticles are important in the perspective of risk assessment of atmospheric contaminations. Copyright © 2014 Elsevier B.V. All rights reserved.

Nuclear microscopy as a tool in TiO2 nanoparticles bioaccumulation studies in aquatic species

Science.gov (United States)

Pinheiro, Teresa; Moita, Liliana; Silva, Luís; Mendonça, Elsa; Picado, Ana

2013-07-01

Engineered Titanium nanoparticles are used for a wide range of applications from coatings, sunscreen cosmetic additives to solar cells or water treatment agents. Inevitably environmental exposure can be expected and data on the ecotoxicological evaluation of nanoparticles are still scarce. The potential effects of nanoparticles of titanium dioxide (TiO2) on two model organisms, the water flea, Daphnia magna and the duckweed Lemna minor, were examined in semichronic toxicity tests. Daphnia and Lemna were exposed to TiO2 nanoparticles (average particle size value of 28 ± 11 nm (n = 42); concentration range, 1.4-25 mg/L) by dietary route and growth in medium containing the nanoparticles of TiO2, respectively. Both morphology and microdistribution of Ti in the individuals were examined by nuclear microscopy techniques. A significant amount of TiO2 was found accumulated in Daphnia exposed to nanoparticles. Nuclear microscopy imaging revealed that Ti was localized only in the digestive tract of the Daphnia, which displayed difficulty in eliminating the nanoparticles from their body. Daphnia showed higher mortality when exposed to higher concentrations of TiO2 (>10 mg/L). The exposure to TiO2 nanoparticles above 25 mg/L caused morphological alterations in Lemna. The roots became stiff and fronds colorless. The Ti mapping of cross-sections of roots and fronds showed that Ti was mainly deposited in the epidermis of the fronds and roots, with minor internalization. In summary, exposure of aquatic organisms to TiO2 nanoparticles may alter the physiology of these organisms at individual and population levels, posing risks to aquatic ecosystems.

Nuclear microscopy as a tool in TiO2 nanoparticles bioaccumulation studies in aquatic species

International Nuclear Information System (INIS)

Pinheiro, Teresa; Moita, Liliana; Silva, Luís; Mendonça, Elsa; Picado, Ana

2013-01-01

Engineered Titanium nanoparticles are used for a wide range of applications from coatings, sunscreen cosmetic additives to solar cells or water treatment agents. Inevitably environmental exposure can be expected and data on the ecotoxicological evaluation of nanoparticles are still scarce. The potential effects of nanoparticles of titanium dioxide (TiO 2 ) on two model organisms, the water flea, Daphnia magna and the duckweed Lemna minor, were examined in semichronic toxicity tests. Daphnia and Lemna were exposed to TiO 2 nanoparticles (average particle size value of 28 ± 11 nm (n = 42); concentration range, 1.4–25 mg/L) by dietary route and growth in medium containing the nanoparticles of TiO 2 , respectively. Both morphology and microdistribution of Ti in the individuals were examined by nuclear microscopy techniques. A significant amount of TiO 2 was found accumulated in Daphnia exposed to nanoparticles. Nuclear microscopy imaging revealed that Ti was localized only in the digestive tract of the Daphnia, which displayed difficulty in eliminating the nanoparticles from their body. Daphnia showed higher mortality when exposed to higher concentrations of TiO 2 (>10 mg/L). The exposure to TiO 2 nanoparticles above 25 mg/L caused morphological alterations in Lemna. The roots became stiff and fronds colorless. The Ti mapping of cross-sections of roots and fronds showed that Ti was mainly deposited in the epidermis of the fronds and roots, with minor internalization. In summary, exposure of aquatic organisms to TiO 2 nanoparticles may alter the physiology of these organisms at individual and population levels, posing risks to aquatic ecosystems

Influence of material properties on TiO2 nanoparticle agglomeration.

Directory of Open Access Journals (Sweden)

Dongxu Zhou

Full Text Available Emerging nanomaterials are being manufactured with varying particle sizes, morphologies, and crystal structures in the pursuit of achieving outstanding functional properties. These variations in these key material properties of nanoparticles may affect their environmental fate and transport. To date, few studies have investigated this important aspect of nanoparticles' environmental behavior. In this study, the aggregation kinetics of ten different TiO2 nanoparticles (5 anatase and 5 rutile each with varying size was systematically evaluated. Our results show that, as particle size increases, the surface charge of both anatase and rutile TiO2 nanoparticles shifts toward a more negative value, and, accordingly, the point of zero charge shifts toward a lower value. The colloidal stability of anatase sphere samples agreed well with DLVO theoretical predictions, where an increase in particle size led to a higher energy barrier and therefore greater critical coagulation concentration. In contrast, the critical coagulation concentration of rutile rod samples correlated positively with the specific surface area, i.e., samples with higher specific surface area exhibited higher stability. Finally, due to the large innate negative surface charge of all the TiO2 samples at the pH value (pH = 8 tested, the addition of natural organic matter was observed to have minimal effect on TiO2 aggregation kinetics, except for the smallest rutile rods that showed decreased stability in the presence of natural organic matter.

Modification of physicochemical and thermal properties of starch films by incorporation of TiO2 nanoparticles.

Science.gov (United States)

Oleyaei, Seyed Amir; Zahedi, Younes; Ghanbarzadeh, Babak; Moayedi, Ali Akbar

2016-08-01

In this research, potato starch and TiO2 nanoparticles (0.5, 1 and 2wt%) films were developed. Influences of different concentrations of TiO2 on the functional properties of nanocomposite films (water-related properties, mechanical characteristics, and UV transmittance) were investigated. XRD, FTIR, and DSC analyses were used to characterize the morphology and thermal properties of the films. The results revealed that TiO2 nanoparticles dramatically decreased the values of water-related properties (water vapor permeability: 11-34%; water solubility: 1.88-9.26%; moisture uptake: 2.15-11.18%). Incorporation of TiO2 led to a slight increment of contact angle and tensile strength, and a decrease in elongation at break of the films. TiO2 successfully blocked more than 90% of UV light, while opacity and white index of the films were enhanced. Glass transition temperature and melting point of the films were positively affected by the addition of TiO2 nanoparticles. The result of XRD study exhibited that due to a limited agglomeration of TiO2 nanoparticles, the mean crystal size of TiO2 increased. Formation of new hydrogen bonds between the hydroxyl groups of starch and nanoparticles was confirmed by FTIR spectroscopy. In conclusion, TiO2 nanoparticles improved the functional properties of potato starch film and extended the potential for food packaging applications. Copyright © 2016 Elsevier B.V. All rights reserved.

Synthesis and Photocatalytic Activity of Mo-Doped TiO2 Nanoparticles

Directory of Open Access Journals (Sweden)

Ji-guo Huang

2015-01-01

Full Text Available The undoped and Mo-doped TiO2 nanoparticles were synthesized by sol-gel method. The as-prepared samples were characterized by X-ray diffraction (XRD, diffuse reflectance UV-visible absorption spectra (UV-vis DRS, X-ray photoelectron spectra (XPS, and transmission electron microscopy (TEM. The photocatalytic activity was evaluated by photocatalytic degradation of methylene blue under irradiation of a 500 W xenon lamp and natural solar light outdoor. Effects of calcination temperatures and Mo doping amounts on crystal phase, crystallite size, lattice distortion, and optical properties were investigated. The results showed that most of Mo6+ took the place of Ti4+ in the crystal lattice of TiO2, which inhibited the growth of crystallite size, suppressed the transformation from anatase to rutile, and led to lattice distortion of TiO2. Mo doping narrowed the band gap (from 3.05 eV of TiO2 to 2.73 eV of TiMo0.02O and efficiently increased the optical absorption in visible region. Mo doping was shown to be an efficient method for degradation of methylene blue under visible light, especially under solar light. When the calcination temperature was 550°C and the Mo doping amount was 2.0%, the Mo-doped TiO2 sample exhibited the highest photocatalytic activity.

Controlled synthesis of TiO2-B nanowires and nanoparticles for dye-sensitized solar cells

International Nuclear Information System (INIS)

Qi Lihong; Liu Yongjun; Li Chunyan

2010-01-01

Controllable synthesis of the TiO 2 -B nanowires (NWs) and nanoparticles (NPs) had been achieved via a facile hydrothermal route, respectively, only by tuning the solution volume. The dye-sensitized solar cells prototypes had been fabricated using TiO 2 -B NW and NP electrodes, respectively. The TiO 2 -B NP cells had higher photocurrent and photoelectrical conversion efficiency than the TiO 2 -B NW cells though the latter exhibited larger photovoltage compared to the former. The key factors such as the photogenerated electron injection drive force, surface defects and the interfacial charge transfer, which determined the photoelectrical properties, had been systematically researched with the surface photovoltage spectra (SPS) and the electrochemical impedance spectra (EIS). The SPS proved that there was larger photoelectron injection drive force in TiO 2 -B NP photoelectrode than that in NW photoelectrode. And the electrochemical impedance spectra (EIS) revealed that TiO 2 -B NP cells had faster interface charge transfer compared to TiO 2 -B NW cells. Both proved that NP cells had the higher photocurrents.

D-sorbitol-induced phase control of TiO2 nanoparticles and its application for dye-sensitized solar cells

Science.gov (United States)

Shaikh, Shoyebmohamad F.; Mane, Rajaram S.; Min, Byoung Koun; Hwang, Yun Jeong; Joo, Oh-Shim

2016-02-01

Using a simple hydrothermal synthesis, the crystal structure of TiO2 nanoparticles was controlled from rutile to anatase using a sugar alcohol, D-sorbitol. Adding small amounts of D-sorbitol to an aqueous TiCl4 solution resulted in changes in the crystal phase, particle size, and surface area by affecting the hydrolysis rate of TiCl4. These changes led to improvements of the solar-to-electrical power conversion efficiency (η) of dye-sensitized solar cells (DSSC) fabricated using these nanoparticles. A postulated reaction mechanism concerning the role of D-sorbitol in the formation of rutile and anatase was proposed. Fourier-transform infrared spectroscopy, 13C NMR spectroscopy, and dynamic light scattering analyses were used to better understand the interaction between the Ti precursor and D-sorbitol. The crystal phase and size of the synthesized TiO2 nanocrystallites as well as photovoltaic performance of the DSSC were examined using X-ray diffraction, Raman spectroscopy, field-emission scanning electron microscopy, high-resolution transmission electron microscopy, and photocurrent density-applied voltage spectroscopy measurement techniques. The DSSC fabricated using the anatase TiO2 nanoparticles synthesized in the presence of D-sorbitol, exhibited an enhanced η (6%, 1.5-fold improvement) compared with the device fabricated using the rutile TiO2 synthesized without D-sorbitol.

Enhanced photoelectrocatalytic performance for degradation of diclofenac and mechanism with TiO2 nano-particles decorated TiO2 nano-tubes arrays photoelectrode

International Nuclear Information System (INIS)

Cheng, Xiuwen; Liu, Huiling; Chen, Qinghua; Li, Junjing; Wang, Pu

2013-01-01

In this study, TiO 2 nano-particles decorated TiO 2 nano-tubes arrays (TiO 2 NPs/TiO 2 NTAs) photoelectrodes have been successfully prepared through anodization, combined with ultrasonic strategy, followed by annealing post-treatment. The morphology and structure of the as-prepared TiO 2 NPs/TiO 2 NTAs photoelectrodes were characterized by scanning electrons microscopy (SEM), N 2 adsorption/desorption isotherms, X-ray diffraction (XRD) and UV–visible light diffuse reflection spectroscopy (DRS). In addition, the generation of hydroxyl radicals (·OH) was detected by a photoluminescence (PL) spectra using terephthalic acid (TA) as a probe molecule. Furthermore, the photoelectrochemical (PECH) properties of TiO 2 NPs/TiO 2 NTAs photoanode were investigated through transient open circuit potential (OCP), photocurrent response (PCR) and electrochemical impedance spectroscopy (EIS). It was found that TiO 2 NPs/TiO 2 NTAs photoelectrode exhibited a distinct decrease of OCP of −0.219 mV cm −2 and PCR of 0.049 mA cm −2 , while a significantly enhanced photoelectrocatalytic (PEC) efficiency of 63.6% (0.4 V vs. SCE) for the degradation of diclofenac. Moreover, the enhanced PEC mechanism of TiO 2 NPs/TiO 2 NTAs photoanode was proposed. The high PEC performance could be attributed to the decoration of TiO 2 NPs, which could improve the mobility and separation efficiency of photoinduced charge carriers under external potential

Cluster synthesis of monodisperse rutile-TiO2 nanoparticles and dielectric TiO2-vinylidene fluoride oligomer nanocomposites

International Nuclear Information System (INIS)

Balasubramanian, Balamurugan; Kraemer, Kristin L; Valloppilly, Shah R; Ducharme, Stephen; Sellmyer, David J

2011-01-01

The embedding of oxide nanoparticles in polymer matrices produces a greatly enhanced dielectric response by combining the high dielectric strength and low loss of suitable host polymers with the high electric polarizability of nanoparticles. The fabrication of oxide-polymer nanocomposites with well-controlled distributions of nanoparticles is, however, challenging due to the thermodynamic and kinetic barriers between the polymer matrix and nanoparticle fillers. In the present study, monodisperse TiO 2 nanoparticles having an average particle size of 14.4 nm and predominant rutile phase were produced using a cluster-deposition technique without high-temperature thermal annealing and subsequently coated with uniform vinylidene fluoride oligomer (VDFO) molecules using a thermal evaporation source, prior to deposition as TiO 2 -VDFO nanocomposite films on suitable substrates. The molecular coatings on TiO 2 nanoparticles serve two purposes, namely to prevent the TiO 2 nanoparticles from contacting each other and to couple the nanoparticle polarization to the matrix. Parallel-plate capacitors made of TiO 2 -VDFO nanocomposite film as the dielectric exhibit minimum dielectric dispersion and low dielectric loss. Dielectric measurements also show an enhanced effective dielectric constant in TiO 2 -VDFO nanocomposites as compared to that of pure VDFO. This study demonstrates for the first time a unique electroactive particle coating in the form of a ferroelectric VDFO that has high-temperature stability as compared to conventionally used polymers for fabricating dielectric oxide-polymer nanocomposites.

BIOSYNTHESIS, CHARACTERIZATION AND APPLICATION OF TIO2 NANOPARTICLES IN BIOCATALYSIS AND PROTEIN FOLDING

Directory of Open Access Journals (Sweden)

Razi Ahmad,

2013-08-01

Full Text Available The nano-TiO2 was synthesized using Lactobacillus sp. and characterized by XRD and TEM. The X-ray diffraction showed that TiO2 nanoparticles were crystalline in nature. TEM images revealed that these particles are irregular in shape with an average particle size of 50–100 nm. The biosynthesized nanoparticles were used for the immobilization and refolding of thermally inactivated alpha amylase enzyme. The enzyme after adsorption on TiO2 nanoparticles retained 71% of enzyme activity. The immobilized enzyme was found to be thermally more stable as compared to the free enzyme. When the enzyme was heated to 60°C for 60 min the free enzyme loses all of its activity whereas the adsorbed enzyme retained 82% of its activity.The adsorbed/immobilized protein could be reused five times without any loss in enzyme activity. The operational stability data also shows that after immobilization the stability of alpha amylase increases. To study the nanoparticles-protein interaction, alpha amylase enzyme was inactivated by heating at 60°C for 1 hour. The thermally inactivated alpha amylase when incubated with the biosynthesized TiO2 nanoparticles regains nearly 65% activity after 2.0 hour. Thus TiO2 nanoparticles assist in refolding of the enzyme.

Effect of porphyrin on photocatalytic activity of TiO2 nanoparticles toward Rhodamine B photodegradation.

Science.gov (United States)

Ahmed, M A; Abou-Gamra, Z M; Medien, H A A; Hamza, M A

2017-11-01

As known, porphyrins have central role in photosynthesis, biological oxidation and reduction and oxygen transport beside to their intensive color which qualify them to be good photosensitizers. Herein, tetra (4-carboxyphenyl) porphyrin (TCPP) was prepared by a simple one-pot synthesis to use as a visible antenna for TiO 2 nanoparticles that were prepared via a simple template-free sol-gel method. Various loading percentages of TCPP (0.05-1%) were incorporated on the surface of TiO 2 as photosensitizer for photocatalytic degradation of Rhodamine B (Rh B) dye as a primary cationic pollutant model. Among them, 0.1% TCPP-TiO 2 was the most reactive sample. It was found that the photoactivity of 0.1% TCPP-TiO 2 sample (0.5g/L) was approximately 1.5 times greater than that of pure TiO 2 (0.5g/L) toward the degradation of Rh B (1×10 -5 M) under UV-A irradiation. Transient fluorescence decay measurements showed that the life time of TiO 2 excited state has doubled after anchoring TCPP, thus the probability of electron-hole recombination has decreased. The samples were characterized by XRD, HR-TEM, DRS and N 2 adsorption-desorption isotherms. The XRD patterns confirmed the successful preparation of TiO 2 nanoparticles with average crystalline size of 25.7nm. Also, XRD patterns suggested the presence of mixed phase TiO 2 nanoparticles of 77% anatase and 23% rutile. DRS showed that the characteristic peaks of TCPP covered the whole visible range 400-700nm. HR-TEM images showed the spheroids shape of TiO 2 nanoparticles and confirmed the presence of anatase and rutile phases as suggested from XRD data. The different parameters affecting the photodegradation of Rh B dye such as catalyst dose, dye concentration and pH were studied to obtain the optimum conditions. Almost complete degradation of Rh B was obtained which confirmed by HPLC and TOC measurements. The effect of scavengers was studied to indicate the most active species. TCPP-TiO 2 gave a good response toward the

Deposition of gold nanoparticles from colloid on TiO2 surface

Science.gov (United States)

Rehacek, Vlastimil; Hotovy, Ivan

2017-11-01

In this paper, experimental results are presented on the deposition of colloidal gold nanoparticles on the surfaces of TiO2 prepared on silicon/silicon dioxide. Important procedures, such as titanium dioxide surface hydrophilization as well as functionalization by an organosilane coupling agent (3-aminopropyl) trimethoxysilane and (3-mercaptopropyl) trimethoxysilane were investigated in order to obtain a metal oxide surface with the most convenient properties for immobilization of gold nanoparticles having a dense and uniform distribution. TiO2 nanotips prepared by reactive ion etching of oxide surface covered with self-mask gold nanoparticles are demonstrated.

Effect of TiO2 on the Gas Sensing Features of TiO2/PANi Nanocomposites

Directory of Open Access Journals (Sweden)

Duong Ngoc Huyen

2011-02-01

Full Text Available A nanocomposite of titanium dioxide (TiO2 and polyaniline (PANi was synthesized by in-situ chemical polymerization using aniline (ANi monomer and TiCl4 as precursors. SEM pictures show that the nanocomposite was created in the form of long PANi chains decorated with TiO2 nanoparticles. FTIR, Raman and UV-Vis spectra reveal that the PANi component undergoes an electronic structure modification as a result of the TiO2 and PANi interaction. The electrical resistor of the nanocomposite is highly sensitive to oxygen and NH3 gas, accounting for the physical adsorption of these gases. A nanocomposite with around 55% TiO2 shows an oxygen sensitivity of 600–700%, 20–25 times higher than that of neat PANi. The n-p contacts between TiO2 nanoparticles and PANi matrix give rise to variety of shallow donors and acceptor levels in the PANi band gap which enhance the physical adsorption of gas molecules.

Uniform TiO2 nanoparticles induce apoptosis in epithelial cell lines in a size-dependent manner.

Science.gov (United States)

Sun, Qingqing; Ishii, Takayuki; Kanehira, Koki; Sato, Takeshi; Taniguchi, Akiyoshi

2017-05-02

The size of titanium dioxide (TiO 2 ) nanoparticles is a vital parameter that determines their cytotoxicity. However, most reported studies have employed irregular shapes and sizes of TiO 2 nanoparticles, as it is difficult to produce nanoparticles of suitable sizes for research. We produced good model TiO 2 nanoparticles of uniform shape and size for use in studying their cytotoxicity. In this work, spherical, uniform polyethylene glycol-modified TiO 2 (TiO 2 -PEG) nanoparticles of differing sizes (100, 200, and 300 nm) were prepared using the sol-gel method. A size-dependent decrease in cell viability was observed with increasing nanoparticle size. Furthermore, apoptosis was found to be positively associated with nanoparticle size, as evidenced by an increase in caspase-3 activity with increasing nanoparticle size. Larger nanoparticles exhibited higher cellular uptake, suggesting that larger nanoparticles more strongly induce apoptosis. In addition, the cellular uptake of different sizes of nanoparticles was energy dependent, suggesting that there are size-dependent uptake pathways. We found that 100 and 200 nm (but not 300 nm) nanoparticles were taken up via clathrin-mediated endocytosis. These results utilizing uniform nanoparticles suggest that the size-dependent cytotoxicity of nanoparticles involves active cellular uptake, caspase-3 activation, and apoptosis in the epithelial cell line (NCI-H292). These findings will hopefully aid in the future design and safe use of nanoparticles.

TiO2 nanosheets decorated with B4C nanoparticles as photocatalysts for solar fuel production under visible light irradiation

Science.gov (United States)

Zhang, Xiaojie; Yang, Jipeng; Cai, Tiancong; Zuo, Guoqiang; Tang, Changqing

2018-06-01

Boron carbide (B4C) nanoparticles-decorated anatase titanium dioxide (TiO2) nanosheets photocatalysts were synthesized by a hydrothermal method in the presence of hydrofluoric acid and characterized by field emission scanning electron microscope, high-resolution transmission electron microscope, UV-vis diffuse reflectance spectra, photoluminescence spectra, etc. With metallic Pt nanoparticles as a co-catalyst, the as-synthesized B4C/TiO2 composites were evaluated using photocatalytic CO2 or H2O reduction to solar fuels such as methane and hydrogen. Under either simulated sunlight or visible light irradiation, coupling p-type B4C with n-type anatase TiO2 significantly improved the photocatalytic performance. Both photoluminescence and transient photocurrent measurements indicated that the interfacial coupling effect between B4C and anatase TiO2 could significantly promote photo-excited charges separations. On the basis of measurements and literatures, a possible mechanism of excited charges transfer at the B4C-anatase TiO2 heterojunction interface during irradiation was deduced.

Synthesis of TiO2 Nanoparticle and its Application to Graphite Composite Electrode for Hydroxylamine Oxidation

Directory of Open Access Journals (Sweden)

M. Mazloum-Ardakani

2013-09-01

Full Text Available In this work, sol-gel method was used tosynthesize titanium dioxide nanoparticles (TiO2. The TiO2nanoparticles was characterized by Scanning Electron Microscopy (SEM, x-ray diffraction (XRD and BET technique.The TiO2 and coumarin derivative (7-(1,3-dithiolan-2-yl-9, 10-dihydroxy-6H-benzofuro [3,2-c] chromen-6-on were incorporated in a graphite composite electrode. The resulting modified electrode displayed a good electrocatalytic activity for the oxidation of hydroxylamine, which leads to a reduction in its overpotential by more than 520 mV. Differential pulse voltammetry (DPV of hydroxylamine at the modified electrode exhibited a linear dynamic range (between 0.5 and 500.0 µM with a detection limit (3σ of 0.133 μM. The high sensitivity, ease of fabrication and low cost of this modified electrode for the detection of hydroxylamine demonstrate its potential sensing applications.

CdS Nanoparticle-Modified α-Fe2O3/TiO2 Nanorod Array Photoanode for Efficient Photoelectrochemical Water Oxidation.

Science.gov (United States)

Yin, Ruiyang; Liu, Mingyang; Tang, Rui; Yin, Longwei

2017-09-02

In this work, we demonstrate a facile successive ionic layer adsorption and reaction process accompanied by hydrothermal method to synthesize CdS nanoparticle-modified α-Fe 2 O 3 /TiO 2 nanorod array for efficient photoelectrochemical (PEC) water oxidation. By integrating CdS/α-Fe 2 O 3 /TiO 2 ternary system, light absorption ability of the photoanode can be effectively improved with an obviously broadened optical-response to visible light region, greatly facilitates the separation of photogenerated carriers, giving rise to the enhancement of PEC water oxidation performance. Importantly, for the designed abnormal type-II heterostructure between Fe 2 O 3 /TiO 2 , the conduction band position of Fe 2 O 3 is higher than that of TiO 2 , the photogenerated electrons from Fe 2 O 3 will rapidly recombine with the photogenerated holes from TiO 2 , thus leads to an efficient separation of photogenerated electrons from Fe 2 O 3 /holes from TiO 2 at the Fe 2 O 3 /TiO 2 interface, greatly improving the separation efficiency of photogenerated holes within Fe 2 O 3 and enhances the photogenerated electron injection efficiency in TiO 2 . Working as the photoanodes of PEC water oxidation, CdS/α-Fe 2 O 3 /TiO 2 heterostucture electrode exhibits improved photocurrent density of 0.62 mA cm - 2 at 1.23 V vs. reversible hydrogen electrode (RHE) in alkaline electrolyte, with an obviously negatively shifted onset potential of 80 mV. This work provides promising methods to enhance the PEC water oxidation performance of the TiO 2 -based heterostructure photoanodes.

Structural phase analysis and photoluminescence properties of Mg-doped TiO2 nanoparticles

Science.gov (United States)

Ali, T.; Ashraf, M. Anas; Ali, S. Asad; Ahmed, Ateeq; Tripathi, P.

2018-05-01

In this paper, we report the synthesis, characterization and photoluminescence properties of Mg-doped TiO2 nanoparticles (NPs). The samples were synthesized by sol-gel method and characterized using the standard analytical techniques such as X-ray diffraction (XRD), Transmission electron microscope (TEM), Energy dispersive X-ray spectroscopy (EDX), UV-visible and photoluminescence spectroscopy. The powder XRD spectra revealed that the synthesized samples are pure and crystalline in nature and showing tetragonal anatase phase of TiO2 NPs. UV-visible spectrum illustrates that an absorption edge shifts toward the visible region. This study may provide a new insight for making the nanomaterials which can be used in photocatalytic applications.

When Anatase Nanoparticles Become Bulklike: Properties of Realistic TiO2 Nanoparticles in the 1-6 nm Size Range from All Electron Relativistic Density Functional Theory Based Calculations.

Science.gov (United States)

Lamiel-Garcia, Oriol; Ko, Kyoung Chul; Lee, Jin Yong; Bromley, Stefan T; Illas, Francesc

2017-04-11

All electron relativistic density functional theory (DFT) based calculations using numerical atom-centered orbitals have been carried out to explore the relative stability, atomic, and electronic structure of a series of stoichiometric TiO 2 anatase nanoparticles explicitly containing up to 1365 atoms as a function of size and morphology. The nanoparticles under scrutiny exhibit octahedral or truncated octahedral structures and span the 1-6 nm diameter size range. Initial structures were obtained using the Wulff construction, thus exhibiting the most stable (101) and (001) anatase surfaces. Final structures were obtained from geometry optimization with full relaxation of all structural parameters using both generalized gradient approximation (GGA) and hybrid density functionals. Results show that, for nanoparticles of a similar size, octahedral and truncated octahedral morphologies have comparable energetic stabilities. The electronic structure properties exhibit a clear trend converging to the bulk values as the size of the nanoparticles increases but with a marked influence of the density functional employed. Our results suggest that electronic structure properties, and hence reactivity, for the largest anatase nanoparticles considered in this study will be similar to those exhibited by even larger mesoscale particles or by bulk systems. Finally, we present compelling evidence that anatase nanoparticles become effectively bulklike when reaching a size of ∼20 nm diameter.

Photoelectrolysis of water using heterostructural composite of TiO2 nanotubes and nanoparticles

International Nuclear Information System (INIS)

Das, Prajna P; Mohapatra, Susanta K; Misra, Mano

2008-01-01

Efficient photoelectrolysis of water to generate hydrogen (H 2 ) can be carried out by designing photocatalysts with good absorption as well as charge transport properties. One dimensional (1D), self-organized titania (TiO 2 ) nanotubes are known to have excellent charge transport properties and TiO 2 nanoparticles (NPs) are good for better photon absorption. This paper describes the synthesis of a composite photocatalyst combining the above two properties of TiO 2 nanocomposites with different morphologies. TiO 2 NPs (5-9 nm nanocrystals form 500-700 nm clusters) have been synthesized from TiCl 4 precursor on TiO 2 nanotubular arrays (∼80 nm diameter and ∼550 nm length) synthesized by the sonoelectrochemical anodization method. This TiO 2 nanotube-nanoparticle composite photoanode has enabled obtaining of enhanced photocurrent density (2.2 mA cm -2 ) as compared with NTs (0.9 mA cm -2 ) and NPs (0.65 mA cm -2 ) alone.

TiO2 Nanorods Decorated with Pd Nanoparticles for Enhanced Liquefied Petroleum Gas Sensing Performance.

Science.gov (United States)

Dhawale, Dattatray S; Gujar, Tanaji P; Lokhande, Chandrakant D

2017-08-15

Development of highly sensitive and selective semiconductor-based metal oxide sensor devices to detect toxic, explosive, flammable, and pollutant gases is still a challenging research topic. In the present work, we systematically enhanced the liquefied petroleum gas (LPG) sensing performance of chemical bath deposited TiO 2 nanorods by decorating Pd nanoparticle catalyst. Surface morphology with elemental mapping, crystal structure, composition and oxidation states, and surface area measurements of pristine TiO 2 and Pd:TiO 2 nanorods was examined by high resolution transmission electron microscopy with energy-dispersive X-ray spectroscopy, X-ray diffraction, X-ray photoelectron spectroscopy, and nitrogen adsorption-desorption characterization techniques. LPG sensing performance of pristine TiO 2 and Pd:TiO 2 nanorods was investigated in different LPG concentration and operating temperature ranges. The LPG response of 21% for pristine TiO 2 nanorods is enhanced to 49% after Pd catalyst decoration with reasonably fast response and recovery times. Further, the sensor exhibited long-term stability, which could be due to the strong metal support (Pd:TiO 2 ) interaction and catalytic properties offered by the Pd nanoparticle catalyst. The work described herein demonstrates a general and scalable approach that provides a promising route for rational design of variety of sensor devices for LPG detection.

Rapid and efficient photocatalytic reduction of hexavalent chromium by using “water dispersible” TiO2 nanoparticles

International Nuclear Information System (INIS)

Wang, Lei; Kang, Shi-Zhao; Li, Xiangqing; Qin, Lixia; Yan, Hao; Mu, Jin

2016-01-01

In the present work, “water dispersible” TiO 2 nanoparticles were prepared, and meanwhile, their photocatalytic activity was systematically tested for the reduction of aqueous Cr(VI) ions. It is found that the as-prepared “water dispersible” TiO 2 nanoparticles are a highly efficient photocatalyst for the reduction of Cr(VI) ions in water under UV irradiation, and suitable for the remediation of Cr(VI) ions wastewater with low concentration. Compared with commercial TiO 2 nanoparticles (P25), the “water dispersible” TiO 2 nanoparticles exhibit 3.8-fold higher photocatalytic activity. 100% Cr (VI) ions can be reduced into Cr(III) ions within 10 min when the Cr (VI) ions initial concentration is 10 mg L −1 . Moreover, the electrical energy consumption can be obviously decreased using the “water dispersible” TiO 2 nanoparticles. These results suggest that the “water dispersible” TiO 2 nanoparticles are a promising photocatalyst for rapid removal of Cr (VI) in environmental therapy. - Highlights: • “Water dispersible” TiO 2 nanoparticles with high photocatalytic activity. • 100% Cr (VI) (10 mg L −1 ) can be reduced within 10 min. • Obvious decrease of electrical energy consumption.

Antimicrobial Activity of TiO2 Nanoparticle-Coated Film for Potential Food Packaging Applications

Directory of Open Access Journals (Sweden)

Siti Hajar Othman

2014-01-01

Full Text Available Recent uses of titanium dioxide (TiO2 have involved various applications which include the food industry. This study aims to develop TiO2 nanoparticle-coated film for potential food packaging applications due to the photocatalytic antimicrobial property of TiO2. The TiO2 nanoparticles with varying concentrations (0–0.11 g/ 100 mL organic solvent were coated on food packaging film, particularly low density polyethylene (LDPE film. The antimicrobial activity of the films was investigated by their capability to inactivate Escherichia coli (E. coli in an actual food packaging application test under various conditions, including types of light (fluorescent and ultraviolet (UV and the length of time the film was exposed to light (one–three days. The antimicrobial activity of the TiO2 nanoparticle-coated films exposed under both types of lighting was found to increase with an increase in the TiO2 nanoparticle concentration and the light exposure time. It was also found that the antimicrobial activity of the films exposed under UV light was higher than that under fluorescent light. The developed film has the potential to be used as a food packaging film that can extend the shelf life, maintain the quality, and assure the safety of food.

TiO2 nanoparticles for enhancing the refractive index of hydrogels for ophthalmological applications

Science.gov (United States)

Hampp, Norbert; Dams, Christian; Badur, Thorben; Reinhardt, Hendrik

2017-02-01

Intraocular lenses (IOL) are currently the only treatment for cataract dependent vision impairment and blindness [1]. A polymer suitable for IOL manufacture needs to meet a plurality of properties, biocompatibility, excellent transmission in the visible range, a high flexibility for micro invasive surgery, a high refractive index as well as a good ABBE-number, just to mention the most important ones [2]. We present the use of in situ generated TiO2-nanoparticles to enhance the refractive index of poly-HEMA hydrogels - with are suitable polymers for IOL manufacture[3] - from 1.44 to 1.527 at 589.3 nm combined with an excellent ABBE-number of 54. The nanoparticles were prepared using titaniumdiisopropoxide- bis(acetylacetonate) as a precursor. First the titanium salt was diffused into the poly-HEMA matrix and then it was transformed into TiO2 in boiling water. The resulting pHEMA [TiO2] hydrogel was dried for 10 days under ambient conditions. By lathing these polymers were machined into lens precursors, the so-called Saturn-rings. After reswelling in physiological saline solutions flexible polymer lenses with high surface quality, shape memory and superior optical properties were obtained. The crystal structure of the formed TiO2 nanoparticles was identified as anatase via Xray. No release of titanium ions or TiO2 nanoparticles was observe under physiological conditions. Such hybrid materials of TiO2 nanoparticles and poly-HEMA like hydrogels are promising materials for IOL.

Photovoltaic characterization of hybrid solar cells using surface modified TiO2 nanoparticles and poly(3-hexyl)thiophene

International Nuclear Information System (INIS)

Guenes, Serap; Marjanovic, Nenad; Nedeljkovic, Jovan M; Sariciftci, Niyazi Serdar

2008-01-01

We report on the photovoltaic performance of bulk heterojunction solar cells using novel nanoparticles of 6-palmitate ascorbic acid surface modified TiO 2 as an electron acceptor embedded into the donor poly(3-hexyl)thiophene (P3HT) matrix. Devices were fabricated by using P3HT with varying amounts of red TiO 2 nanoparticles (1:1, 1:2, 1:3 w-w ratio). The devices were characterized by measuring current-voltage characteristics under simulated AM 1.5 conditions. Incident photon to current efficiency (IPCE) was spectrally resolved. The nanoscale morphology of such organic/inorganic hybrid blends was also investigated using atomic force microscopy (AFM).

Bactericidal Activity of Aqueous Acrylic Paint Dispersion for Wooden Substrates Based on TiO2 Nanoparticles Activated by Fluorescent Light

Directory of Open Access Journals (Sweden)

Diana Di Gioia

2013-08-01

Full Text Available The photocatalytic effect of TiO2 has great potential for the disinfection of surfaces. Most studies reported in the literature use UV activation of TiO2, while visible light has been used only in a few applications. In these studies, high concentrations of TiO2, which can compromise surface properties, have been used. In this work, we have developed an acrylic-water paint dispersion containing low TiO2 content (2 vol % for the inactivation of microorganisms involved in hospital-acquired infections. The nanoparticles and the coating have been characterized using spectroscopic techniques and transmission electron microscopy, showing their homogenous dispersion in the acrylic urethane coating. A common fluorescent light source was used to activate the photocatalytic activity of TiO2. The paint dispersion showed antimicrobial activity against Escherichia coli, Staphylococcus aureus and Pseudomonas aeruginosa. The coating containing the TiO2 nanoparticles maintained good UV stability, strong adhesion to the substrate and high hardness. Therefore, the approach used is feasible for paint formulation aimed at disinfection of healthcare surfaces.

TiO2 film decorated with highly dispersed polyoxometalate nanoparticles synthesized by micelle directed method for the efficiency enhancement of dye-sensitized solar cells

Science.gov (United States)

He, Lifei; Chen, Li; Zhao, Yue; Chen, Weilin; Shan, Chunhui; Su, Zhongmin; Wang, Enbo

2016-10-01

In this work, two kinds of polyoxometalate (POM) nanoparticles with controlled shapes and structures were synthesized by micelle directed method and then composited with TiO2 via calcination to remove the surfactants owing to the excellent electronic storage and transmission ability of POM, finally obtaining two kinds of TiO2 composites with highly dispersed and small-sized POM nanoparticles (∼1 nm). The TiO2 composites were then induced into the photoanodes of dye-sensitized (N719) solar cells (DSSCs). The separation of electron-holes becomes more favorable due to the nanostructure and high dispersion of POM which provide more active sites than pure POM tending to agglomeration. The TiO2 composite photoanodes finally yielded the power conversion efficiency (PCE) of 8.4% and 8.2%, respectively, which were 42% and 39% higher than the pristine TiO2 based anodes. In addition, the mechanisms of POM in DSSC are proposed.

Characterization of manufactured TiO2 nanoparticles

Science.gov (United States)

Motzkus, C.; Macé, T.; Vaslin-Reimann, S.; Ausset, P.; Maillé, M.

2013-04-01

techniques to characterize five different manufactured TiO2 nanoparticles. In this study, different measurement techniques have been implemented: Transmission Electron Microscopy (TEM), Scanning Mobility Particle Sizer (SMPS) and Aerodynamic Particle Sizer (APS). The TEM results lead to a relatively good agreement between data from the manufacturer and our characterizations of primary particle size. With regard to the dustiness, the results show a strong presence of agglomerates / aggregates of primary particles and a significant presence of emitted airborne nanoparticles with a diameter below 100 nm (composed of isolated primary particles and small aggregates / agglomerates formed from a few primary particles): the number proportion of these particles varies from 0 to 44 % in the measurement range 14-360 nm depending on the types of powders and corrections of measurements.

Characterization of manufactured TiO2 nanoparticles

International Nuclear Information System (INIS)

Motzkus, C; Macé, T; Vaslin-Reimann, S; Ausset, P; Maillé, M

2013-01-01

techniques to characterize five different manufactured TiO 2 nanoparticles. In this study, different measurement techniques have been implemented: Transmission Electron Microscopy (TEM), Scanning Mobility Particle Sizer (SMPS) and Aerodynamic Particle Sizer (APS). The TEM results lead to a relatively good agreement between data from the manufacturer and our characterizations of primary particle size. With regard to the dustiness, the results show a strong presence of agglomerates / aggregates of primary particles and a significant presence of emitted airborne nanoparticles with a diameter below 100 nm (composed of isolated primary particles and small aggregates / agglomerates formed from a few primary particles): the number proportion of these particles varies from 0 to 44 % in the measurement range 14-360 nm depending on the types of powders and corrections of measurements.

One-component solution system to prepare nanometric anatase TiO2

International Nuclear Information System (INIS)

Trung, Tran; Ha, Chang-Sik

2004-01-01

A novel one-pot synthesis route was proposed to prepare nanometric anatase TiO 2 using trichloroethylene as reaction medium, which may have great advantage over multicomponent solution systems when TiO 2 is used as a reinforcing filler for polymers dissolved in trichloroethylene. The anatase TiO 2 nanoparticles were characterized using X-ray diffraction (XRD), scanning electron microscopy and small-angle X-ray scattering (SAXS). It was found that the diameters of TiO 2 nanoparticles are in the range from 5 to 13 nm

Probing Photocatalytic Characteristics of Sb-Doped TiO2 under Visible Light Irradiation

Directory of Open Access Journals (Sweden)

Lingjing Luo

2014-01-01

Full Text Available Sb-doped TiO2 nanoparticle with varied dopant concentrations was synthesized using titanium tetrachloride (TiCl4 and antimony chloride (SbCl3 as the precursors. The properties of Sb-doped TiO2 nanoparticles were characterized by X-ray diffraction (XRD, scanning electron microscope (SEM, fluorescence spectrophotometer, and Uv-vis spectrophotometer. The absorption edge of TiO2 nanoparticles could be extended to visible region after doping with antimony, in contrast to the UV absorption of pure TiO2. The results showed that the photocatalytic activity of Sb-doped TiO2 nanoparticles was much more active than pure TiO2. The 0.1% Sb-doped TiO2 nanoparticles demonstrated the best photocatalytic activity which was better than that of the Degussa P25 under visible light irradiation using terephthalic acid as fluorescent probe. The effects of Sb dopant on the photocatalytic activity and the involved mechanism were extensively investigated in this work as well.

What atomic resolution annular dark field imaging can tell us about gold nanoparticles on TiO2 (1 1 0)

International Nuclear Information System (INIS)

Findlay, S.D.; Shibata, N.; Ikuhara, Y.

2009-01-01

Annular dark field scanning transmission electron microscopy imaging was recently applied to a catalyst consisting of gold nanoparticles on TiO 2 (1 1 0), showing directly that the gold atoms in small nanoparticles preferentially attach to specific sites on the TiO 2 (1 1 0) surface. Here, through simulation, a parameter exploration of the imaging conditions which maximise the visibility of such nanoparticles is presented. Aberration correction, finite source size and profile imaging are all considered while trying to extracting the maximum amount of information from a given sample. Comment is made on the role of the thermal vibration of the atoms in the nanoparticle, the magnitude of which is generally not known a priori but which affects the visibility of the nanoparticles in this imaging mode.

Photocatalytic activity enhancement by electron irradiation of fullerene derivative-TiO2 nanoparticles under visible light illumination

International Nuclear Information System (INIS)

Cho, Sung Oh; Yoo, Seung Hwa; Lee, Dong Hoon

2011-01-01

Photocatalytic decomposition of aqueous organic pollutant have attracted many interest due to its simple, low cost, and clean procedure. By only using the sun light and photocatalyst, especially TiO 2 nanoparticles based systems have been extensively studied and commercialized for real life application. However, TiO 2 has a critical disadvantage, which can only absorb the ultra-violet region of the solar spectrum, due to the large band-gap of 3.2 eV. Extensive studies have been preformed to expand the light absorption of TiO 2 to the visible light region of the solar spectrum, by doping metal or non-metal elements on TiO 2 or attaching small band-gap semiconductors on TiO 2 . In this study, a fullerene derivative 1-(3- carboxypropyl)-1-phenyl[6,6]C 61 (PCBA) was attached on the surface of TiO 2 nanoparticles, and its photocatalytic activity was evaluated by decomposition of methyl orange under visible light. Furthermore, enhancement in the photocatalytic activity of these nanoparticles by electron irradiation is discussed

Development of Comparative Toxicity Potentials of TiO2 Nanoparticles for Use in Life Cycle Assessment

DEFF Research Database (Denmark)

Ettrup, Kim; Kounina, Anna; Hansen, Steffen Foss

2017-01-01

for TiO2 nanoparticles (TiO2-NP) for use in LCA. We adapted the USEtox 2.0 consensus model to integrate the SimpleBox4Nano fate model, and we populated the resulting model with TiO2-NP specific data. We thus calculated CTP values for TiO2 nanoparticles for air, water, and soil emission compartments...... in earlier studies. Assumptions, which were performed in those previous studies because of lack of data and knowledge at the time they were made, primarily explain such discrepancies. For future assessment of potential toxic impacts of TiO2 nanoparticles in LCA studies, we therefore recommend the use of our......Studies have shown that releases of nanoparticles may take place through the life cycle of products embedding nanomaterials, thus resulting in potential impacts on ecosystems and human health. While several life cycle assessment (LCA) studies have assessed such products, only a few of them have...

Assessment of Environmental Performance of TiO2 Nanoparticles Coated Self-Cleaning Float Glass

Directory of Open Access Journals (Sweden)

Martina Pini

2017-01-01

Full Text Available In recent years, superhydrophilic and photocatalytic self-cleaning nanocoatings have been widely used in the easy-to-clean surfaces field. In the building sector, self-cleaning glass was one of the first nanocoating applications. These products are based on the photocatalytic property of a thin layer of titanium dioxide (TiO2 nanoparticles deposited on the surface of any kind of common glass. When exposed to UV radiation, TiO2 nanoparticles react with the oxygen and water molecules adsorbed on their surface to produce radicals leading to oxidative species. These species are able to reduce or even eliminate airborne pollutants and organic substances deposited on the material’s surface. To date, TiO2 nanoparticles’ benefits have been substantiated; however, their ecological and human health risks are still under analysis. The present work studies the ecodesign of the industrial scale-up of TiO2 nanoparticles self-cleaning coated float glass production performed by the life cycle assessment (LCA methodology and applies new human toxicity indicators to the impact assessment stage. Production, particularly the TiO2 nanoparticle application, is the life cycle phase most contributing to the total damage. According to the ecodesign approach, the production choices carried out have exacerbated environmental burdens.

Chemically synthesized TiO2 and PANI/TiO2 thin films for ethanol sensing applications

Science.gov (United States)

Gawri, Isha; Ridhi, R.; Singh, K. P.; Tripathi, S. K.

2018-02-01

Ethanol sensing properties of chemically synthesized titanium dioxide (TiO2) and polyaniline/titanium dioxide nanocomposites (PANI/TiO2) had been performed at room temperature. In-situ oxidative polymerization process had been employed with aniline as a monomer in presence of anatase titanium dioxide nanoparticles. The prepared samples were structurally and morphologically characterized by x-ray diffraction, fourier transform infrared spectra, high resolution-transmission electron microscopy and field emission-scanning electron microscopy. The crystallinity of PANI/TiO2 nanocomposite was revealed by XRD and FTIR spectra confirmed the presence of chemical bonding between the polymer chains and metal oxide nanoparticles. HR-TEM micrographs depicted that TiO2 particles were embedded in polymer matrix, which provides an advantage over pure TiO2 nanoparticles in efficient adsorption of vapours. These images also revealed that the TiO2 nanoparticles were irregular in shape with size around 17 nm. FE-SEM studies revealed that in the porous structure of PANI/TiO2 film, the intercalation of TiO2 in PANI chains provides an advantage over pure TiO2 film for uniform interaction with ethanol vapors. The sensitivity values of prepared samples were examined towards ethanol vapours at room temperature. The PANI/TiO2 nanocomposite exhibited better sensing response and faster response-recovery examined at different ethanol concentrations ranging from 5 ppm to 20 ppm in comparison to pure TiO2 nanoparticles. The increase in vapour sensing of PANI/TiO2 sensing film as compared to pure TiO2 film had been explained in detail with the help of gas sensing mechanism of TiO2 and PANI/TiO2. This provides strong evidence that gas sensing properties of TiO2 had been considerably improved and enhanced with the addition of polymer matrix.

Distinct toxic interactions of TiO2 nanoparticles with four coexisting organochlorine contaminants on algae.

Science.gov (United States)

Zhang, Shuai; Deng, Rui; Lin, Daohui; Wu, Fengchang

Engineered nanoparticles are increasingly discharged into the environment. After discharge, these nanoparticles can interact with co-existing organic contaminants, resulting in a phenomena referred to as 'joint toxicity'. This study evaluated joint toxicities of TiO 2 nanoparticles (TiO 2 NPs) with four different (atrazine, hexachlorobenzene, pentachlorobenzene, and 3,3',4,4'-tetrachlorobiphenyl) organochlorine contaminants (OCs) toward algae (Chlorella pyrenoidosa). The potential mechanisms underlying the joint toxicity were discussed, including TiO 2 NPs-OC interactions, effects of TiO 2 NPs and OCs on biophysicochemical properties of algae and effects of TiO 2 NPs and OCs on each other's bioaccumulation in algae. The results indicate that coexposure led to a synergistic effect on the joint toxicity for TiO 2 NPs-atrazine, antagonistic effect for TiO 2 NPs-hexachlorobenzene and TiO 2 NPs-3,3',4,4'-tetrachlorobiphenyl, and an additive effect for TiO 2 NPs-pentachlorobenzene. There was nearly no adsorption of OCs by TiO 2 NPs, and the physicochemical properties of TiO 2 NPs were largely unaltered by the presence of OCs. However, both OCs and NPs affected the biophysicochemical properties of algal cells and thereby influenced the cell surface binding and/or internalization. TiO 2 NPs significantly increased the bioaccumulation of each OC. However, with the exception of atrazine, the bioaccumulation of TiO 2 NPs decreased when used with each OC. The distinct joint toxicity outcomes were a result of the balance between the increased toxicities of OCs (increased bioaccumulations) and the altered toxicity of TiO 2 NPs (bioaccumulation can either increase or decrease). These results can significantly improve our understanding of the potential environmental risks associated with NPs.

Cross Linking Polymers (PVA & PEG with TiO2 Nanoparticles for Humidity Sensing

Directory of Open Access Journals (Sweden)

Monika Joshi

2009-11-01

Full Text Available Humidity Sensors of different types are being used for various applications. Resistive Humidity Sensor has advantage over others for being small, low cost, interchangeable and long term stable. This makes them suitable for industrial, commercial and residential applications. In the present investigation humidity sensing behavior of various composite films made of Polyvinyl Alcohol (PVA, Polyethylene glycol (PEG, alkalies and oxide nanoparticles has been studied. It was found that relationship of resistance v/s relative humidity (RH was linear from 40 RH to 60 RH for a composite film made of PVA + PEG+ alkalies .The film can work with reliable efficiency for more than 100 days for the above range of humidity at room temperature. In order to improve the efficiency of composite polymer film TiO2 nanoparticles were added in the film and studied for resistance vs. RH responses. It was found that humidity range expands from 30 RH to 65 RH indicating the proportional decrease in resistance with increase in humidity at both ends as a result of the presence of TiO2 nanoparticles. The composite film with TiO2 nanoparticles can thus be used for wider range of humidity with reasonable stability and consistency. The observed behavior of the film has been attributed to the transportation of charge through TiO2 nanoparticles enhancing the conduction with the cross linked polymers.

The Comparative PDT Experiment of the Inactivation of HL60 on Modified TiO2 Nanoparticles

Directory of Open Access Journals (Sweden)

Kaiqi Lu

2015-01-01

Full Text Available Four samples of modified titanium dioxide (TiO2, Fe/TiO2 (2 wt%, Fe/TiO2 (5 wt%, and 5-ALA/TiO2, were experimented in photodynamic therapy (PDT on leukemia cells HL60, performing promising photocatalytic inactivation effect. Fe/TiO2 and 5-ALA/TiO2 were synthesized in methods of precipitation and ultrasonic methods, respectively. X-ray diffraction spectra and UV-Vis spectra were studied for the samples’ crystalline phase and redshift of absorption peak. Further, FTIR spectra and Raman spectra were obtained to examine the combination of 5-aminolevulinic (5-ALA and TiO2 nanoparticles. The toxicity of these four kinds of nanoparticles was studied through darkroom experiments. And based on the concentration which caused the same toxic effect (90% on HL60, PDT experiments of TiO2, Fe/TiO2 (2%, Fe/TiO2 (5%, and ALA/TiO2 were done, resulting in the fact that the photokilling efficiency was 69.7%, 71.6%, 72%, and 80.6%, respectively. Scanning electron microscope (SEM images of the samples were also taken to study the morphology of HL60 cells before and after PDT, resulting in the fact the activation of the modified TiO2 from PDT was the main cause of cell apoptosis.

On the role of Fe ions on magnetic properties of doped TiO2 nanoparticles

Science.gov (United States)

Tolea, F.; Grecu, M. N.; Kuncser, V.; Constantinescu, S. Gr.; Ghica, D.

2015-04-01

The role of iron doping on magnetic properties of hydrothermal anatase TiO2:57Fe (0-1 at. %) nanoparticles is investigated by combining superconducting quantum interference device magnetometry with Mössbauer and electron paramagnetic resonance techniques. The results on both as-prepared and thermally treated samples in reduced air atmosphere reveal complexity of magnetic interactions, in connection to certain iron ion electron configurations and defects (oxygen vacancies, F-center, and Ti3+ ions). The distribution of iron ions is predominantly at nanoparticle surface layers. Formation of weak ferromagnetic domains up to 380 K is mainly related to defects, supporting the bound magnetic polaron model.

Investigation of TiO2 nanoparticles translocation through a Caco-2 monolayer

International Nuclear Information System (INIS)

Brun, E; Jugan, M-L; Carriere, M; Herlin-Boime, N; Jaillard, D; Fayard, B; Flank, A-M; Mabondzo, A

2011-01-01

Nanoparticles (NPs) are introduced in a growing number of commercial products, including food and beverage but their effects on gastrointestinal tract are poorly investigated. Here we focused on the translocation of TiO 2 NPs through Caco-2 monolayers exposed to anatase and rutile NPs up to 24 h. Internalization was followed by transmission electronic microscopy and μ-XRF elemental mapping, coupled to XAS analysis of Ti atoms environment. This innovative technique is among the best techniques to get insights on NP fate after internalization. The originality of this project relies on the panel of microscopy techniques implemented to investigate digestive barrier translocation, bringing together biologists, chemists and physicists in a pluridisciplinary research program.

Excess electrons in reduced rutile and anatase TiO2

Science.gov (United States)

Yin, Wen-Jin; Wen, Bo; Zhou, Chuanyao; Selloni, Annabella; Liu, Li-Min

2018-05-01

As a prototypical photocatalyst, TiO2 is a material of scientific and technological interest. In photocatalysis and other applications, TiO2 is often reduced, behaving as an n-type semiconductor with unique physico-chemical properties. In this review, we summarize recent advances in the understanding of the fundamental properties and applications of excess electrons in reduced, undoped TiO2. We discuss the characteristics of excess electrons in the bulk and at the surface of rutile and anatase TiO2 focusing on their localization, spatial distribution, energy levels, and dynamical properties. We examine specific features of the electronic states for photoexcited TiO2, for intrinsic oxygen vacancy and Ti interstitial defects, and for surface hydroxyls. We discuss similarities and differences in the behaviors of excess electrons in the rutile and anatase phases. Finally, we consider the effect of excess electrons on the reactivity, focusing on the interaction between excess electrons and adsorbates.

Cellular and molecular responses of E. fetida cœlomocytes exposed to TiO2 nanoparticles

Science.gov (United States)

Bigorgne, Emilie; Foucaud, Laurent; Caillet, Céline; Giambérini, Laure; Nahmani, Johanne; Thomas, Fabien; Rodius, François

2012-07-01

An in vitro approach using cœlomocytes of Eisenia fetida was investigated to evaluate toxicity of TiO2 nanoparticles. Cœlomocytes were exposed to well-dispersed suspension of small aggregates (130 nm) of TiO2 nanoparticles (1-25 μg/ml) during 4, 12 and 24 h. Intracellular localisation suggested that the main route of uptake was endocytosis. Cellular responses showed that TiO2 nanoparticles were not cytotoxic and had no effect on phagocytosis at any of the four concentrations for each time tested. Concerning molecular responses, an increase of fetidin and metallothionein mRNA expression was observed starting from 4 h of exposure. In contrast, expression of coelomic cytolytic factor mRNA decreased for 10 and 25 μg/ml after 4 h. Superoxide dismutase, catalase and glutathione-S-transferase expression were not modified suggesting that oxidative stress was not induced by TiO2 in our experimental conditions. This in vitro approach showed that TiO2 nanoparticles were taken up by cœlomocytes and they could modify the molecular response of immune and detoxification system.

Preparation of Transparent Bulk TiO2/PMMA Hybrids with Improved Refractive Indices via an in Situ Polymerization Process Using TiO2 Nanoparticles Bearing PMMA Chains Grown by Surface-Initiated Atom Transfer Radical Polymerization.

Science.gov (United States)

Maeda, Satoshi; Fujita, Masato; Idota, Naokazu; Matsukawa, Kimihiro; Sugahara, Yoshiyuki

2016-12-21

Transparent TiO 2 /PMMA hybrids with a thickness of 5 mm and improved refractive indices were prepared by in situ polymerization of methyl methacrylate (MMA) in the presence of TiO 2 nanoparticles bearing poly(methyl methacrylate) (PMMA) chains grown using surface-initiated atom transfer radical polymerization (SI-ATRP), and the effect of the chain length of modified PMMA on the dispersibility of modified TiO 2 nanoparticles in the bulk hybrids was investigated. The surfaces of TiO 2 nanoparticles were modified with both m-(chloromethyl)phenylmethanoyloxymethylphosphonic acid bearing a terminal ATRP initiator and isodecyl phosphate with a high affinity for common organic solvents, leading to sufficient dispersibility of the surface-modified particles in toluene. Subsequently, SI-ATRP of MMA was achieved from the modified surfaces of the TiO 2 nanoparticles without aggregation of the nanoparticles in toluene. The molecular weights of the PMMA chains cleaved from the modified TiO 2 nanoparticles increased with increases in the prolonging of the polymerization period, and these exhibited a narrow distribution, indicating chain growth controlled by SI-ATRP. The nanoparticles bearing PMMA chains were well-dispersed in MMA regardless of the polymerization period. Bulk PMMA hybrids containing modified TiO 2 nanoparticles with a thickness of 5 mm were prepared by in situ polymerization of the MMA dispersion. The transparency of the hybrids depended significantly on the chain length of the modified PMMA on the nanoparticles, because the modified PMMA of low molecular weight induced aggregation of the TiO 2 nanoparticles during the in situ polymerization process. The refractive indices of the bulk hybrids could be controlled by adjusting the TiO 2 content and could be increased up to 1.566 for 6.3 vol % TiO 2 content (1.492 for pristine PMMA).

Enhanced Optoelectronic Properties of PFO/Fluorol 7GA Hybrid Light Emitting Diodes via Additions of TiO2 Nanoparticles

Directory of Open Access Journals (Sweden)

Bandar Ali Al-Asbahi

2016-09-01

Full Text Available The effect of TiO2 nanoparticle (NP content on the improvement of poly(9,9′-di-n-octylfluorenyl-2,7-diyl (PFO/Fluorol 7GA organic light emitting diode (OLED performance is demonstrated here. The PFO/Fluorol 7GA blend with specific ratios of TiO2 NPs was prepared via a solution blending method before being spin-coated onto an indium tin oxide (ITO substrate to act as an emissive layer in OLEDs. A thin aluminum layer as top electrode was deposited onto the emissive layer using the electron beam chamber. Improvement electron injection from the cathode was achieved upon incorporation of TiO2 NPs into the PFO/Fluorol 7GA blend, thus producing devices with intense luminance and lower turn-on voltage. The ITO/(PFO/Fluorol 7GA/TiO2/Al OLED device exhibited maximum electroluminescence intensity and luminance at 25 wt % of TiO2 NPs, while maximum luminance efficiency was achieved with 15 wt % TiO2 NP content. In addition, this work proved that the performance of the devices was strongly affected by the surface morphology, which in turn depended on the TiO2 NP content.

Inverted organic solar cells with solvothermal synthesized vanadium-doped TiO2 thin films as efficient electron transport layer

Institute of Scientific and Technical Information of China (English)

Mehdi Ahmadi; Sajjad Rashidi Dafeh; Samaneh Ghazanfarpour; Mohammad Khanzadeh

2017-01-01

We investigated the effects of using different thicknesses of pure and vanadium-doped thin films of TiO2 as the electron transport layer in the inverted configuration of organic photovoltaic cells based on poly (3-hexylthiophene) P3HT:[6-6] phenyl-(6) butyric acid methyl ester (PCBM).1％ vanadium-doped TiO2 nanoparticles were synthesized via the solvothermal method.Crystalline structure,morphology,and optical properties of pure and vanadium-doped TiO2 thin films were studied by different techniques such as x-ray diffraction,scanning electron microscopy,transmittance electron microscopy,and UV-visible transmission spectrum.The doctor blade method which is compatible with roll-2-roll printing was used for deposition of pure and vanadium-doped TiO2 thin films with thicknesses of 30 nm and 60 nm.The final results revealed that the best thickness of TiO2 thin films for our fabricated cells was 30 nm.The cell with vanadium-doped TiO2 thin film showed slightly higher power conversion efficiency and great Jsc of 10.7 mA/cm2 compared with its pure counterpart.In the cells using 60 nm pure and vanadium-doped TiO2 layers,the cell using the doped layer showed much higher efficiency.It is remarkable that the extemal quantum efficiency of vanadium-doped TiO2 thin film was better in all wavelengths.

Microwave-assisted synthesis and characterization of poly(acrylic)/SiO2-TiO2 core-shell nanoparticle hybrid thin films

International Nuclear Information System (INIS)

Chien, Wen-Chen; Yu, Yang-Yen; Chen, Po-Kan; Yu, Hui-Huan

2011-01-01

In this study, poly(acrylic)/SiO 2 -TiO 2 core-shell nanoparticle hybrid thin films were successfully synthesized by microwave-assisted polymerization. The coupling agent 3-(trimethoxysilyl) propyl methacrylate (MSMA) was hydrolyzed with colloidal SiO 2 -TiO 2 core-shell nanoparticles, and then polymerized with two acrylic monomers and initiator to form a precursor solution. The results of this study showed that the spin-coated hybrid films had relatively good surface planarity, high thermal stability, a tunable refractive index (1.525 2 -TiO 2 core-shell nanoparticle hybrid thin films, for potential use in optical applications.

Synthesis of Cr3+-doped TiO2 nanoparticles: characterization and evaluation of their visible photocatalytic performance and stability.

Science.gov (United States)

Mendiola-Alvarez, Sandra Yadira; Guzmán-Mar, Jorge Luis; Turnes-Palomino, Gemma; Maya-Alejandro, Fernando; Caballero-Quintero, Adolfo; Hernández-Ramírez, Aracely; Hinojosa-Reyes, Laura

2017-09-28

Cr 3+ -doped TiO 2 nanoparticles (Ti-Cr) were synthesized by microwave-assisted sol-gel method. The Ti-Cr catalyst was characterized by X-ray diffraction, ultraviolet-visible diffuse reflectance spectroscopy, N 2 adsorption-desorption analysis, Raman spectroscopy, scanning electron microscopy, transmission electron microscopy, photoluminescence spectroscopy, X-ray photoelectron spectroscopy (XPS) and zetametry. The anatase mesoporous Ti-Cr material exhibited a specific surface area of 54.5 m 2 /g. XPS analysis confirmed the proper substitution of Ti 4+ cations by Cr 3+ cations in the TiO 2 matrix. The particle size was of average size of 17 nm for the undoped TiO 2 but only 9.5 nm for Ti-Cr. The Cr atoms promoted the formation of hydroxyl radicals and modified the surface adsorptive properties of TiO 2 due to the increase in surface acidity of the material. The photocatalytic evaluation demonstrated that the Ti-Cr catalyst completely degraded (4-chloro-2-methylphenoxy) acetic acid under visible light irradiation, while undoped TiO 2 and P25 allowed 45.7% and 31.1%, respectively. The rate of degradation remained 52% after three cycles of catalyst reuse. The higher visible light photocatalytic activity of Ti-Cr was attributed to the beneficial effect of Cr 3+ ions on the TiO 2 surface creating defects within the TiO 2 crystal lattice, which can act as charge-trapping sites, reducing the electron-hole recombination process.

Cytotoxicity of TiO2 nanoparticles towards freshwater sediment microorganisms at low exposure concentrations

International Nuclear Information System (INIS)

Kumari, Jyoti; Kumar, Deepak; Mathur, Ankita; Naseer, Arif; Kumar, Ravi Ranjan; Thanjavur Chandrasekaran, Prathna; Chaudhuri, Gouri; Pulimi, Mrudula; Raichur, Ashok M.; Babu, S.; Chandrasekaran, Natarajan; Nagarajan, R.; Mukherjee, Amitava

2014-01-01

There is a persistent need to assess the effects of TiO 2 nanoparticles on the aquatic ecosystem owing to their increasing usage in consumer products and risk of environmental release. The current study is focused on TiO 2 nanoparticle-induced acute toxicity at sub-ppm level (≤1 ppm) on the three different freshwater sediment bacterial isolates and their consortium under two different irradiation (visible light and dark) conditions. The consortium of the bacterial isolates was found to be less affected by the exposure to the nanoparticles compared to the individual cells. The oxidative stress contributed considerably towards the cytotoxicity under both light and dark conditions. A statistically significant increase in membrane permeability was noted under the dark conditions as compared to the light conditions. The optical and fluorescence microscopic images showed aggregation and chain formation of the bacterial cells, when exposed to the nanoparticles. The electron microscopic (SEM, TEM) observations suggested considerable damage of cells and bio-uptake of nanoparticles. The exopolysaccrides (EPS) production and biofilm formation were noted to increase in the presence of the nanoparticles, and expression of the key genes involved in biofilm formation was studied by RT-PCR. - Highlights: • Toxicity of NPs towards freshwater sediment bacteria at sub-ppm concentrations. • Decreased toxicity of the nanoparticles in the consortium of microorganisms. • Enhanced bacterial resistance through EPS and biofilm formation in the presence of NPs. • Considerable surface damage of cells and internalization of NPs. • Gene expression analyses related to biofilm formation in the presence of NPs

Synthesis and characterization of Fe3+ doped TiO2 nanoparticles and films and their performance for photocurrent response under UV illumination

International Nuclear Information System (INIS)

Elghniji, Kais; Atyaoui, Atef; Livraghi, Stefano; Bousselmi, Latifa; Giamello, Elio; Ksibi, Mohamed

2012-01-01

Graphical abstract: Schematic diagram illustrating the charge transfer from excited TiO 2 to the different states of Fe 3+ ions; C B and V B refer to the energy levels of the conduction and valence bands of TiO 2 , respectively. Highlights: ► In this study we examine the Iron as catalyst precursor to synthesize the Fe 3+ doped TiO 2 nanoparticles. ► The Fe 3+ doped TiO 2 catalysts show the presence of a mixed phase of anatase. ► The iron is completely absent in the XRD pattern of the doped iron TiO 2 powder. ► The analysis of EPR result further confirms that Fe 3+ ion are successfully doped in the TiO 2 lattice by substituting Ti 4+ . ► Fe 3+ doping can efficiently separate the photo-generated electrons and holes. - Abstract: Undoped TiO 2 and Fe 3+ doped (0.1, 0.3, 0.6 and 1 wt.%) TiO 2 nanoparticles have been synthesized by the acid-catalyzed sol–gel method. Iron cations are introduced in the initial solution, before gelification, what promotes their lattice localization. The Fe 3+ doped TiO 2 films have been fabricated using a dip-coating technique. The effect of iron content on the crystalline structure, phase transformation and grain growth were determined by X-ray diffraction (XRD), Raman spectroscopy, UV–visible diffused reflectance spectroscopy (DRS) and Electron paramagnetic resonance (EPR) spectroscopy. It has demonstrated that all catalysts are composed of mixed-phase crystals of anatase and brookite with anatase as dominant phase. The crystallinity of the brookite and anatase phases decreased with increasing the iron content. The analysis of EPR result further confirms that Fe 3+ ion are successfully doped in the TiO 2 lattice by substituting Ti 4+ . It was demonstrated that Fe 3+ ion in the TiO 2 films plays a role as the intermediate for the efficient separation of photogenerated hole–electron pairs and increases the photocurrent response of the film under UV light irradiation. The maximum photocurrent is obtained on the Fe 3+ doped TiO

Electron transfer dynamics of triphenylamine dyes bound to TiO2 nanoparticles from femtosecond stimulated Raman spectroscopy

KAUST Repository

Hoffman, David P.

2013-04-11

Interfacial electron transfer between sensitizers and semiconducting nanoparticles is a crucial yet poorly understood process. To address this problem, we have used transient absorption (TA) and femtosecond stimulated Raman spectroscopy (FSRS) to investigate the photoexcited dynamics of a series of triphenylamine-coumarin dye/TiO2 conjugates. The TA decay is multiexponential, spanning time scales from 100 fs to 100 ps, while the characteristic transient Raman spectrum of the radical cation decays biexponentially with a dominant ∼3 ps component. To explain these observations, we propose a model in which the decay of the TA is due to hot electrons migrating from surface trap states to the conduction band of TiO 2 while the decay of the Raman signature is due to internal conversion of the dye molecule. Furthermore, the S1 Raman spectrum of TPAC3, a dye wherein a vinyl group separates the triphenylamine and coumarin moieties, is similar to the S1 Raman spectrum of trans-stilbene; we conclude that their S1 potential energy surfaces and reactivity are also similar. This correlation suggests that dyes containing vinyl linkers undergo photoisomerization that competes with electron injection. © 2013 American Chemical Society.

Three-dimensional observation of TiO2 nanostructures by electron tomography

KAUST Repository

Suh, Young Joon

2013-03-01

Three-dimensional nanostructures of TiO2 related materials including nanotubes, electron acceptor materials in hybrid polymer solar cells, and working electrodes of dye sensitized solar cells (DSSCs) were visualized by electron tomography as well as TEM micrographs. The regions on the wall of TiO2 nanotubes where the streptavidins were attached were elucidated by electron tomogram analysis. The coverage of TiO2 nanotubes by streptavidin was also investigated. The TiO2 nanostructures in hybrid polymer solar cells made by sol-gel and atomic layer deposition (ALD) methods and the morphologies of pores between TiO2 particles in DSSCs were also observed by reconstructed three-dimensional images made by electron tomography. © 2012 Elsevier Ltd.

FD&C Yellow No. 5 (tartrazine) degradation via reactive oxygen species triggered by TiO2 and Au/TiO2 nanoparticles exposed to simulated sunlight.

Science.gov (United States)

Li, Meng; He, Weiwei; Liu, Yi; Wu, Haohao; Wamer, Wayne G; Lo, Y Martin; Yin, Jun-Jie

2014-12-10

When exposed to light, TiO2 nanoparticles (NPs) become photoactivated and create electron/hole pairs as well as reactive oxygen species (ROS). We examined the ROS production and degradation of a widely used azo dye, FD&C Yellow No. 5 (tartrazine), triggered by photoactivated TiO2 NPs. Degradation was found to follow pseudo-first order reaction kinetics where the rate constant increased with TiO2 NP concentration. Depositing Au on the surface of TiO2 largely enhanced electron transfer and ROS generation, which consequently accelerated dye degradation. Alkaline conditions promoted ROS generation and dye degradation. Results from electron spin resonance spin-trap spectroscopy suggested that at pH 7.4, both hydroxyl radical (•OH) and singlet oxygen ((1)O2) were responsible for dye discoloration, whereas at pH 5, the consumption of (1)O2 became dominant. Implications for dye degradation in foods and other consumer products that contain both TiO2 and FD&C Yellow No. 5 as ingredients are discussed.

Effects of subtoxic concentrations of TiO2 and ZnO nanoparticles on human lymphocytes, dendritic cells and exosome production

International Nuclear Information System (INIS)

Andersson-Willman, Britta; Gehrmann, Ulf; Cansu, Zekiye; Buerki-Thurnherr, Tina; Krug, Harald F.; Gabrielsson, Susanne; Scheynius, Annika

2012-01-01

Metal oxide nanoparticles are widely used in the paint and coating industry as well as in cosmetics, but the knowledge of their possible interactions with the immune system is very limited. Our aims were to investigate if commercially available TiO 2 and ZnO nanoparticles may affect different human immune cells and their production of exosomes, nano-sized vesicles that have a role in cell to cell communication. We found that the TiO 2 or ZnO nanoparticles at concentrations from 1 to 100 μg/mL did not affect the viability of primary human peripheral blood mononuclear cells (PBMC). In contrast, monocyte-derived dendritic cells (MDDC) reacted with a dose dependent increase in cell death and caspase activity to ZnO but not to TiO 2 nanoparticles. Non-toxic exposure, 10 μg/mL, to TiO 2 and ZnO nanoparticles did not significantly alter the phenotype of MDDC. Interestingly, ZnO but not TiO 2 nanoparticles induced a down regulation of FcγRIII (CD16) expression on NK-cells in the PBMC population, suggesting that subtoxic concentrations of ZnO nanoparticles might have an effect on FcγR-mediated immune responses. The phenotype and size of exosomes produced by PBMC or MDDC exposed to the nanoparticles were similar to that of exosomes harvested from control cultures. TiO 2 or ZnO nanoparticles could not be detected within or associated to exosomes as analyzed with TEM. We conclude that TiO 2 and ZnO nanoparticles differently affect immune cells and that evaluations of nanoparticles should be performed even at subtoxic concentrations on different primary human immune cells when investigating potential effects on immune functions. -- Highlights: ► ZnO nanoparticles induce cell death of MDDC but not of PBMC. ► ZnO nanoparticles induce caspase activation and DNA fragmentation in MDDC. ► TiO 2 nanoparticles are taken up by MDDC but have no effect on their phenotype. ► ZnO nanoparticles induce a significant reduction of CD16 expression on NK cells. ► ZnO and TiO 2

Al2O3 doping of TiO2 electrodes and applications in dye-sensitized solar cells

International Nuclear Information System (INIS)

Eom, Tae Sung; Kim, Kyung Hwan; Bark, Chung Wung; Choi, Hyung Wook

2014-01-01

Dye-sensitized solar cells (DSSCs) have been intensively studied since their discovery in 1991. DSSCs have been extensively researched over the past decades as cheaper alternatives to silicon solar cells due to their high energy-conversion efficiency and their low production cost. However, some problems need to be solved in order to enhance the efficiency of DSSCs. In particular, the electron recombination that occurs due to the contact between the transparent conductive oxide (TCO) and a redox electrolyte is one of the main limiting factors of efficiency. In this work, we report for the first time the improvement of the photovoltaic characteristics of DSSCs by doping TiO 2 with Al 2 O 3 . DSSCs were constructed using composite particles of Al 2 O 3 -doped TiO 2 and TiO 2 nanoparticles. The DSSCs using Al 2 O 3 showed the maximum conversion efficiency of 6.29% due to effective electron transport. DSSCs based on Al 2 O 3 -doped TiO 2 films showed better photovoltaic performance than cells fabricated with only TiO 2 nanoparticles. This result is attributed to the prevention of electron recombination between electrons in the TiO 2 conduction band with holes in the dye or the electrolyte. There mechanism is suggested based on impedance results, which indicated improved electron transport at the TiO 2 /dye/electrolyte interface.

The investigation of photo-induced chemiluminescence on Co2+-doped TiO2 nanoparticles and its analytical application.

Science.gov (United States)

Li, Guixin; Nan, Hongyan; Zheng, Xingwang

2009-07-01

A novel space- and time-resolved photo-induced chemiluminescence (PICL) analytical method was developed based on the photocatalysis of the Co2+-doped TiO2 nanoparticles. The PICL reaction procedure under the photocatalysis of Co2+-doped TiO2 nanoparticles was investigated using cyclic voltammetry and potentiometry. Meanwhile, the effect of the electrical double layer outside the Co2+-doped TiO2 nanoparticles on the PICL was investigated by contrasting with the Co2+-doped TiO2-SiO2 core-shell nanoparticles. Significantly, the CL intensity increased apparently and the time of the CL was prolonged in the presence of procaterol hydrochloride because the mechanism of the enhanced PICL reaction may be modified. The route of the PICL was changed due to the participation of the procaterol hydrochloride enriched at the surface of the Co2+-doped TiO2-SiO2 in the PICL reaction, which prolonged the time of the CL reaction and resulted in the long-term PICL. The analytical characteristics of the proposed in-situ PICL method were investigated using the procaterol hydrochloride as the model analyte. The investigation results showed that this new PICL analytical method offered higher sensitivity to the analysis of the procaterol hydrochloride and the PICL intensity was linear with the concentration of the procaterol hydrochloride in the range from ca. 2.0 x 10(-10) to 1.0 x 10(-8) g mL(-1).

The use of TiO2 nanoparticles to reduce refrigerator ir-reversibility

International Nuclear Information System (INIS)

Padmanabhan, Venkataramana Murthy V.; Palanisamy, Senthilkumar

2012-01-01

Highlights: ► COP of hydrocarbons mixture VCRSs increases less when compared to R134a. ► Compressor ir-reversibility of VCRSs decreases by 33% (R134a), 14% (R436A and R436B). ► Total ir-reversibility of selected VCRSs decreases. ► Exergy efficiency of R134a is exceptionally low at lower reference temperature. ► Exergy efficiency of selected VCRSs increases. - Abstract: The ir-reversibility at the process of a vapour-compression refrigeration system (VCRS) with nanoparticles in the working fluid was investigated experimentally. Mineral oil (MO) with 0.1 g L −1 TiO 2 nanoparticles mixture were used as the lubricant instead of Polyol-ester (POE) oil in the R134a, R436A (R290/R600a-56/44-wt.%) and R436B (R290/R600a-52/48-wt.%)VCRSs. The VCRS ir-reversibility at the process with the nanoparticles was investigated using second law of thermodynamics. The results indicate that R134a, R436A and R436B and MO with TiO 2 nanoparticles work normally and safely in the VCRS. The VCRSs total ir-reversibility (529, 588 and 570 W) at different process was better than the R134a, R436A and R436B and POE oil system (777, 697 and 683 W). The same tests with Al 2 O 3 nanoparticles showed that the different nanoparticles properties have little effect on the VCRS ir-reversibility. Thus, TiO 2 nanoparticles can be used in VCRS with reciprocating compressor to considerably reduce ir-reversibility at the process.

Adsorption and Recovery of Polyphenolic Flavonoids Using TiO_2-Functionalized Mesoporous Silica Nanoparticles

International Nuclear Information System (INIS)

Khan, M. Arif; Wallace, William T.; Islam, Syed Z.; Nagpure, Suraj; Strzalka, Joseph

2017-01-01

Exploiting specific interactions with titania (TiO_2) has been proposed for the separation and recovery of a broad range of biomolecules and natural products, including therapeutic polyphenolic flavonoids which are susceptible to degradation, such as quercetin. Functionalizing mesoporous silica with TiO_2 has many potential advantages over bulk and mesoporous TiO_2 as an adsorbent for natural products, including robust synthetic approaches leading to high surface area, stable separation platforms. Here, TiO_2 surface functionalized mesoporous silica nanoparticles (MSNPs) are synthesized and characterized as a function of TiO_2 content (up to 636 mg TiO2/g). The adsorption isotherms of two polyphenolic flavonoids, quercetin and rutin, were determined (0.05-10 mg/ml in ethanol), and a 100-fold increase in the adsorption capacity was observed relative to functionalized nonporous particles with similar TiO_2 surface coverage. An optimum extent of functionalization (approximately 440 mg TiO_2/g particles) is interpreted from characterization techniques including grazing incidence x-ray scattering (GIXS), high resolution transmission electron microscopy (HRTEM) and nitrogen adsorption, which examined the interplay between the extent of TiO_2 functionalization and the accessibility of the porous structures. The recovery of flavonoids is demonstrated using ligand displacement in ethanolic citric acid solution (20% w/v), in which greater than 90% recovery can be achieved in a multistep extraction process. The radical scavenging activity (RSA) of the recovered and particle-bound quercetin as measured by 2,2-diphenyl-1-picrylhydrazyl (DPPH) radical scavenging assay demonstrates greater than 80% retention of antioxidant activity by both particle-bound and recovered quercetin. In conclusion, these mesoporous titanosilicate materials can serve as a synthetic platform to isolate, recover, and potentially deliver degradation-sensitive natural products to biological systems.

Carrier recombination dynamics in anatase TiO 2 nanoparticles

Science.gov (United States)

Cavigli, Lucia; Bogani, Franco; Vinattieri, Anna; Cortese, Lorenzo; Colocci, Marcello; Faso, Valentina; Baldi, Giovanni

2010-11-01

We present an experimental study of the radiative recombination dynamics in size-controlled TiO 2 nanoparticles in the range 20-130 nm. Time-integrated photoluminescence spectra clearly show a dominance of self-trapped exciton (STE) emission, with main features not dependent on the nanoparticle size and on its environment. From picosecond time-resolved experiments as a function of the excitation density and the nanoparticle size we address the STE recombination dynamics as the result of two main processes related to the direct STE formation and to the indirect STE formation mediated by non-radiative surface states.

Gold nanoparticles-immobilized, hierarchically ordered, porous TiO2 nanotubes for biosensing of glutathione

Directory of Open Access Journals (Sweden)

Sheen Mers SV

2015-10-01

Full Text Available SV Sheen Mers,1,2 Elumalai Thambuswamy Deva Kumar,1 V Ganesh1,2 1Electrodics and Electrocatalysis (EEC Division, Council of Scientific and Industrial Research–Central Electrochemical Research Institute (CSIR–CECRI, Karaikudi, Tamil Nadu, India; 2Academy of Scientific and Innovative Research (AcSIR, New Delhi, India Abstract: Glutathione (GSH is vital for several functions of our human body such as neutralization of free radicals and reactive oxygen compounds, maintaining the active forms of vitamin C and E, regulation of nitric oxide cycle, iron metabolism, etc. It is also an endogenous antioxidant in most of the biological reactions. Given the importance of GSH, a simple strategy is proposed in this work to develop a biosensor for quantitative detection of GSH. This particular biosensor comprises of gold nanoparticles (Au NPs-immobilized, hierarchically ordered titanium dioxide (TiO2 porous nanotubes. Hexagonally arranged, honeycomb-like nanoporous tubular TiO2 electrodes are prepared by using a simple electrochemical anodization process by applying a constant potential of 30 V for 24 hours using ethylene glycol consisting of ammonium fluoride as an electrolytic medium. Structural morphology and crystalline nature of such TiO2 nanotubes are analyzed using field emission scanning electron microscope (FESEM and X-ray diffraction (XRD. Interestingly, nanocomposites of TiO2 with Au NPs is prepared in an effort to alter the intrinsic properties of TiO2, especially tuning of its band gap. Au NPs are prepared by a well-known Brust and Schiffrin method and are immobilized onto TiO2 electrodes which act as a perfect electrochemical sensing platform for GSH detection. Structural characterization and analysis of these modified electrodes are performed using FESEM, XRD, and UV-visible spectroscopic studies. GSH binding events on Au NPs-immobilized porous TiO2 electrodes are monitored by electrochemical techniques, namely, cyclic voltammetry (CV and

Investigation on the structural and nonlinear optical properties of Pt doped TiO2 nanoparticles

International Nuclear Information System (INIS)

Rahulan, K. Mani; Padmanathan, N.; Vinitha, G.; Kanakam, Charles Christopher

2013-01-01

Graphical abstract: The open aperture Z-scan traces of Pt doped TiO 2 nanoparticles at different Pt concentrations were carried out at an irradiation wavelength of 532 nm. It was numerically found that, two photon absorption (TPA) type process gives the best fit to the obtained open aperture Z-scan data. The nonlinear transmission was found to be of third order as it fits to a two-photon absorption. The optical limiting performances of nanoparticles were greatly enhanced with increased volume ratio of Pt. Increasing particle size reduced the limiting threshold and enhanced the optical limiting performance. - Highlights: • Pt doped TiO 2 nanoparticles with different concentrations of Pt have been synthesized by sol–gel method. • The average fluorescence lifetime decreases as the volume fraction of Pt dopant increases. • The effects of Pt content on the optical limiting property were investigated by open aperture Z-scan measurements done at 532 nm using 5 ns laser pulses. • The values of the third-order nonlinearities of nanoparticles are interesting from the application point of view which could be used as a potential candidate for the application of nonlinear optical device. - Abstract: Pt doped TiO 2 nanoparticles with different concentrations of Pt were prepared by sol–gel method. X-ray diffraction (XRD) study reveals that the samples have a homogeneous anatase phase tetragonal system and the lattice parameter analysis indicates that Pt ions substitute into the lattice of TiO 2 . The addition of dopant increases the growth of TiO 2 grains, agglomerates them and shifts the absorption band of TiO 2 from ultraviolet to visible region. The incorporation of Pt in TiO 2 is also confirmed by fluorescence quenching and the fluorescence lifetime decreases as the volume fraction of Pt dopant increases. Open aperture Z-scan measurements done at 532 nm using 7 ns laser pulses show nonlinear absorption which arises from an effective two photon absorption process

Interaction and nanotoxic effect of TiO2 nanoparticle on fibrinogen by multi-spectroscopic method

International Nuclear Information System (INIS)

Wang, Chao; Li, Ying

2012-01-01

Toxicological effects of nanoparticles (NPs) are still poorly documented while there are great demands for industrial applications and daily life. The aim of this study is to evaluate the influence of physicochemical characteristics on TiO 2 NP toxicological effects toward protein. In order to better understand the physicochemical basis of the toxic of NP in industrial applications and under conditions of environmental exposure, we performed an array of photophysical measurements to quantify the interaction of TiO 2 NP with protein. Fluorescence quenching, circular dichroism, dynamic light scattering and transmission electron microscopy measurements were performed on TiO 2 NP having a diameter range from 10 to 35 nm in the performance of protein. We find that the TiO 2 NP strongly associates with protein where the binding constant, as well as the degree of cooperativity of particle–protein binding, depends on particle size. We also find tentative evidence that the protein undergoes conformational change upon association with the NP. These results indicate that exposure to TiO 2 NP may have an unfavorable effect on human health by inactivating functional proteins. - Highlights: ► The binding constants for fibrinogen onto TiO 2 NPs depend on particle size. ► CD results showed that the structural changes of protein are quite small. ► The adsorbed protein to cause the TiO 2 NP to aggregate was indicated by DLS and TEM.

Fabrication of TiO2 nanoparticles/nanorod composite arrays via a two-step method for efficient dye-sensitized solar cells

Directory of Open Access Journals (Sweden)

Jingyang Wang

2014-12-01

Full Text Available TiO2 nanoparticles/nanorod composite arrays were prepared on the F-doped tin oxide (FTO substrate through a two-step method of hydrothermal and d.c. magnetron sputtering. The microstructure and optical properties of the samples were characterized respectively by means of X-ray diffraction (XRD, field-emission scanning electron microscopy (FESEM and UV–vis spectrometer. The results showed that the TiO2 composite nanorod arrays possess the nature of high surface area for more dye molecule absorption and the strong light scattering effects. The dye sensitized solar cells (DSSCs based on TiO2 composite nanorod arrays exhibited a 80% improvement in the overall energy conversion efficiency compared with the pure TiO2 nanorod arrays photoanode.

Visible light assisted photodecolorization of eosin-Y in aqueous solution using hesperidin modified TiO2 nanoparticles

Science.gov (United States)

Vignesh, K.; Suganthi, A.; Rajarajan, M.; Sakthivadivel, R.

2012-03-01

Hesperidin a flavanoid, modified TiO2 nanoparticles (Hes-TiO2) was synthesized to improve the visible light driven photocatalytic performance of TiO2. The synthesized nanoparticles were characterized by UV-visible diffuse reflectance spectroscopy (UV-vis-DRS), FT-IR, powder X-ray diffraction (XRD) and scanning electron microscopy (SEM). The photocatalytic activity of Hes-TiO2 was investigated based on the decolorization of eosin-Y under visible light irradiation. Hes-TiO2 showed high efficiency for the decolorization of eosin-Y. The influences of various reaction parameters like effect of pH, catalyst dosage and initial dye concentration on the photocatalytic efficiency were investigated. The adsorption of eosin-Y on Hes-TiO2 was found favorable by the Langmuir approach. The removal percentage of chemical oxygen demand (COD) was determined to evaluate the mineralization of eosin-Y during photodecolorization. Based on the intermediates obtained in the GC-MS spectroscopic technique, a probable degradation mechanism has been proposed.

Visible light assisted photodecolorization of eosin-Y in aqueous solution using hesperidin modified TiO2 nanoparticles

International Nuclear Information System (INIS)

Vignesh, K.; Suganthi, A.; Rajarajan, M.; Sakthivadivel, R.

2012-01-01

Hesperidin a flavanoid, modified TiO 2 nanoparticles (Hes-TiO 2 ) was synthesized to improve the visible light driven photocatalytic performance of TiO 2 . The synthesized nanoparticles were characterized by UV-visible diffuse reflectance spectroscopy (UV-vis-DRS), FT-IR, powder X-ray diffraction (XRD) and scanning electron microscopy (SEM). The photocatalytic activity of Hes-TiO 2 was investigated based on the decolorization of eosin-Y under visible light irradiation. Hes-TiO 2 showed high efficiency for the decolorization of eosin-Y. The influences of various reaction parameters like effect of pH, catalyst dosage and initial dye concentration on the photocatalytic efficiency were investigated. The adsorption of eosin-Y on Hes-TiO 2 was found favorable by the Langmuir approach. The removal percentage of chemical oxygen demand (COD) was determined to evaluate the mineralization of eosin-Y during photodecolorization. Based on the intermediates obtained in the GC-MS spectroscopic technique, a probable degradation mechanism has been proposed.

Multifunctional Roles of TiO 2 Nanoparticles for Architecture of Complex Core−Shells and Hollow Spheres of SiO 2 −TiO 2 −Polyaniline System

KAUST Repository

Wang, Dan Ping

2009-10-27

Nanoparticles are often used as seeds to grow one-dimensional nanomaterials or as core materials to prepare core-shell nanostructures. On the other hand, the presynthesized inorganic nanoparticles can also be used as starting building blocks to prepare inorganic-polymer nanocomposites. In this work, we explore the roles of metal-oxide nanoparticles (anatase TiO2) in the area of constructional synthesis of highly complex core-shell and hollow sphere nanostructures comprising SiO2, TiO2, and polyaniline (PAN). In particular, multifunctional roles of oleate-surfactant-protected TiO2 nanoparticles have been revealed in this study: they provide starting sites for polymerization of aniline on the surface of SiO2 mesospheres; they land on the inner surface of polyaniline shell to form a secondary material phase; they work as initial crystalline seeds for homogeneous growth of interior TiO2 shell; and they serve as primary nanobuilding blocks to form exterior TiO2 shell on the polyaniline via self-assembly. With the assistance of the TiO2 nanoparticles, a total of six complex core-shell and hollow sphere nanocomposites (SiO 2/TiO2, SiO2/TiO2/PAN, SiO 2/TiO2/PAN/TiO2, TiO2/PAN, TiO 2/PAN/TiO2, and TiO2/TiO2) have been made in this work through controlled self-assembly, templating growth, polymerization, and homogeneous seeded growth. Applicability of these nanostructures in photocatalytic applications has also been demonstrated by our preliminary investigations. The easy separation of used catalysts after reaction seems to be advantageous because of relatively large external diameters of the lightweight nanocomposites. © 2009 American Chemical Society.

A comparative study of the magnetization in transition metal ion doped CeO2, TiO2 and SnO2 nanoparticles

Science.gov (United States)

Apostolov, A. T.; Apostolova, I. N.; Wesselinowa, J. M.

2018-05-01

Using the microscopic s-d model taking into account anharmonic spin-phonon interactions we have studied the magnetic properties of Co and Cu ion doped CeO2 and TiO2 nanoparticles and compared them with those of SnO2. By Co-doping there is a maximum in the magnetization M(x) curve for all nanoparticles observed in the most transition metal doped ones. The s-d interaction plays an important role by the decrease of M at higher dopant concentration. We have discussed the magnetization in dependence of different model parameters. By small Cu-ion doping there are some differences. In CeO2M decreases with the Cu-concentration, whereas in TiO2 and SnO2M increases. For higher Cu dopant concentrations M(X) decreases in TiO2 nanoparticles. We obtain room temperature ferromagnetism also in Zn doped CeO2, TiO2 and SnO2 nanoparticles, i.e. in non-transition metal ion doped ones. The different behavior of M in Co and Cu doped nanoparticles is due to a combination effect of multivalent metal ions, oxygen vacancies, different radius of cation dopants, connection between lattice and magnetism, as well as competition between the s-d and d-d ferromagnetic or antiferromagnetic interactions.

Biocorrosion of TiO2 nanoparticle coating of Ti-6Al-4V in DMEM under specific in vitro conditions

Science.gov (United States)

Höhn, Sarah; Virtanen, Sannakaisa

2015-02-01

A TiO2 nanoparticle coating was prepared on a biomedical Ti-6Al-4V alloy using "spin-coating" technique with a colloidal suspension of TiO2 nanopowders with the aim to optimize the surface morphology (e.g., roughness) for improved biocompatibility. The influence of a TiO2 nanoparticle (NP) coating on the corrosion behavior, metal ion release, and biomimetic apatite formation was studied in DMEM, at 37.5 °C with a continuous supply of 5% CO2. Electrochemical impedance spectroscopy measurements indicate a formation of a new layer on the surface of the NP-coated sample upon 28 days immersion in DMEM. Scanning electron microscopy (SEM) and X-ray spectroscopy confirm that the surface of the NP-coated Ti-6Al-4V shows a complete coverage by a Ca-phosphate layer in contrast to the non-coated Ti-6Al-4V alloy. Hence, the TiO2-NP coating strongly enhances biomimetic apatite formation on the alloy surface. In addition, the TiO2-NP coating can efficiently reduce Al-release from the alloy, for which the bare Ti-6Al-4V alloy is significant for at least 28 days of immersion in DMEM.

Eosin-Y sensitized core-shell TiO2-ZnO nano-structured photoanodes for dye-sensitized solar cell applications.

Science.gov (United States)

Manikandan, V S; Palai, Akshaya K; Mohanty, Smita; Nayak, Sanjay K

2018-06-01

In the current investigation, TiO 2 and TiO 2 -ZnO (core-shell) spherical nanoparticles were synthesized by simple combined hydrolysis and refluxing method. A TiO 2 core nanomaterial on the shell material of ZnO was synthesized by utilizing variable ratios of ZnO. The structural characterization of TiO 2 -ZnO core/shell nanoparticles were done by XRD analysis. The spherical structured morphology of the TiO 2 -ZnO has been confirmed through field emission scanning electron microscopy (FE-SEM) and transmission electron microscopy (TEM) studies. The UV-visible spectra of TiO 2 -ZnO nanostructures were also compared with the pristine TiO 2 to investigate the shift of wavelength. The TiO 2 -ZnO core/shell nanoparticles at the interface efficiently collect the photogenarated electrons from ZnO and also ZnO act a barrier for reduced charge recombination of electrolyte and dye-nanoparticles interface. This combination improved the light absorption which induced the charge transfer ability and dye loading capacity of core-shell nanoparticles. An enhancement in the short circuit current (J sc ) from 1.67 mA/cm 2 to 2.1 mA/cm 2 has been observed for TiO 2 -ZnObased photoanode (with platinum free counter electrode), promises an improvement in the energy conversion efficiency by 57% in comparison with that of the DSSCs based on the pristine TiO 2 . Henceforth, TiO 2 -ZnO photoelectrode in ZnO will effectively act as barrier at the interface of TiO 2 -ZnO and TiO 2 , ensuring the potential for DSSC application. Copyright © 2018 Elsevier B.V. All rights reserved.

Enhancement of the irreversibility field in bulk MgB2 by TiO2 nanoparticle addition

DEFF Research Database (Denmark)

Xu, G.J.; Grivel, Jean-Claude; Abrahamsen, A.B.

2004-01-01

MgB2 samples doped with TiO2 nanoparticles were prepared and the effect of TiO2 addition on the superconducting transition temperature (T-c), irreversibility field (H-irr) and critical current density (J(c)) were investigated. It is found that the hexagonal lattice parameters a and c decrease...... with TiO2 doping. Tc decreases gradually from 38.2 to 37.8 K as the TiO2 content increases from 0 to 15 wt%. The H-irr increases at 20 K from 4.3 to 4.9 T as the TiO2 content increases from 0 to 10 wt%, and at the same temperature J(c) increases from 450 to 4250 A/cm(2) at 4.2 T. (C) 2004 Published...

Effective Electron Transfer Pathway of the Ternary TiO2/RGO/Ag Nanocomposite with Enhanced Photocatalytic Activity under Visible Light

Directory of Open Access Journals (Sweden)

Hongwei Tian

2017-05-01

Full Text Available Mesoporous TiO2/reduced graphene oxide/Ag (TiO2/RGO/Ag ternary nanocomposite with an effective electron transfer pathway is obtained by an electrostatic self-assembly method and photo-assisted treatment. Compared with bare mesoporous TiO2 (MT and mesoporous TiO2/RGO (MTG, the ternary mesoporous TiO2/RGO/Ag (MTGA nanocomposite exhibited superior photocatalytic performance for the degradation of methylene blue (MB under visible light, and the degradation rate reached 0.017 min−1, which was 3.4-times higher than that of MTG. What is more, the degradation rate of MTGA nanocomposite after three cycle times is 91.2%, and the composition is unchanged. In addition, we found that the OH•, h+ and especially O2•− contribute to the high photocatalytic activity of MTGA for MB degradation. It is proposed that Ag nanoparticles can form the local surface plasmon resonance (LSPR to absorb the visible light and distract the electrons into MT, and RGO can accept the electrons from MT to accelerate the separation efficiency of photogenerated carriers. The establishment of MTGA ternary nanocomposite makes the three components act synergistically to enhance the photocatalytic performance.

Effects of subtoxic concentrations of TiO2 and ZnO nanoparticles on human lymphocytes, dendritic cells and exosome production.

Science.gov (United States)

Andersson-Willman, Britta; Gehrmann, Ulf; Cansu, Zekiye; Buerki-Thurnherr, Tina; Krug, Harald F; Gabrielsson, Susanne; Scheynius, Annika

2012-10-01

Metal oxide nanoparticles are widely used in the paint and coating industry as well as in cosmetics, but the knowledge of their possible interactions with the immune system is very limited. Our aims were to investigate if commercially available TiO(2) and ZnO nanoparticles may affect different human immune cells and their production of exosomes, nano-sized vesicles that have a role in cell to cell communication. We found that the TiO(2) or ZnO nanoparticles at concentrations from 1 to 100μg/mL did not affect the viability of primary human peripheral blood mononuclear cells (PBMC). In contrast, monocyte-derived dendritic cells (MDDC) reacted with a dose dependent increase in cell death and caspase activity to ZnO but not to TiO(2) nanoparticles. Non-toxic exposure, 10μg/mL, to TiO(2) and ZnO nanoparticles did not significantly alter the phenotype of MDDC. Interestingly, ZnO but not TiO(2) nanoparticles induced a down regulation of FcγRIII (CD16) expression on NK-cells in the PBMC population, suggesting that subtoxic concentrations of ZnO nanoparticles might have an effect on FcγR-mediated immune responses. The phenotype and size of exosomes produced by PBMC or MDDC exposed to the nanoparticles were similar to that of exosomes harvested from control cultures. TiO(2) or ZnO nanoparticles could not be detected within or associated to exosomes as analyzed with TEM. We conclude that TiO(2) and ZnO nanoparticles differently affect immune cells and that evaluations of nanoparticles should be performed even at subtoxic concentrations on different primary human immune cells when investigating potential effects on immune functions. Copyright © 2012 Elsevier Inc. All rights reserved.

TiO2 nanoparticles prepared without harmful organics: A biosafe and economical approach

KAUST Repository

Shah, M.A.

2011-06-01

Growth of titanium oxide (TiO2) nanoparticles of varying size, ranging from 20-60 nms through a versatile and an economic route, is being reported. The approach is based on a simple reaction of titanium powder and De-Ionized (DI) water at ∼180 °C, without use of any harmful additives. Field Emission Scanning Electron Microscopy (FESEM) reveals the well defined morphology of nanoparticles, whereas X-ray Diffraction (XRD) studies reveal that the, as prepared, nanoparticles are in a mixed phase, with a dominance of a stable rutile phase. Since only water, which is regarded as a benign solvent, is used during the preparation of nanoparticles, we believe that the products so produced are biocompatible and bio-safe and can be readily used for medical applications. The biocompatibility tests are yet to be carried out and shall be reported in forthcoming publications. © 2011 Sharif University of Technology. Production and hosting by Elsevier B.V. All rights reserved.

Surface Coatings of TiO2 Nanoparticles onto the Designed Fabrics for Enhanced Self-Cleaning Properties

Directory of Open Access Journals (Sweden)

Mudassar Abbas

2018-01-01

Full Text Available Herein, the hydrophobic and self-cleaning properties of three different fabric surfaces have been evaluated after applying titanium dioxide (TiO2 nanofinishes. The nanoparticles were prepared by sol-gel techniques and were characterized by using X-ray diffraction (XRD, scanning electron microscopy (SEM and dynamic light scattering (DLS methods. The ultra-refined particles were applied over three different fabric substrates having similar weave of Z-twill (3/1. The yarns of 100% polyester, blend of viscose with mod-acrylic and high performance polyethylene containing 16 yarn count (Ne and 31.496 and 15.748 ends/cm and picks/cm, respectively, were used for required fabric preparation. The different fabric structures were applied with self-cleaning finish of TiO2 nanoparticles prepared in our laboratory and the results were compared with commercially available finish Rucoguard AFR. The static contact angles, UV-protection factor, air permeability and hydrophobic activity of nanofinished fabric helped in evaluating their breathability and self-cleaning properties.

Photocatalytic degradation of paracetamol on TiO2 nanoparticles and TiO2/cellulosic fiber under UV and sunlight irradiation

OpenAIRE

Jallouli, Nabil; Elghniji, Kais; Trabelsi, Hassen; Ksibi, Mohamed

2014-01-01

In the present study, photocatalytic degradation of acetaminophen ((N-(4-hydroxyphe-nyl)acetamide)), an analgesic drug has been investigated in a batch reactor using TiO2 P25 as a photocatalyst in slurry and under UV light. Using TiO2 P25 nanoparticles, much faster photodegradation of paracetamol and effective mineralization occurred, more than 90% of 2.65 × 10−4 M paracetamol was degraded under UV irradiation. Changes in pH values affected the adsorption and the photodegradation of paracetam...

Hydroxyl radicals (·OH) are associated with titanium dioxide (TiO2) nanoparticle-induced cytotoxicity and oxidative DNA damage in fish cells

International Nuclear Information System (INIS)

Reeves, James F.; Davies, Simon J.; Dodd, Nicholas J.F.; Jha, Awadhesh N.

2008-01-01

TiO 2 nanoparticles ( 2 nanoparticles on goldfish skin cells (GFSk-S1), either alone or in combination with UVA. Whilst neutral red retention (NRR) assay (a measure of lysosomal membrane integrity) was used to evaluate cell viability, a modified Comet assay using bacterial lesion-specific repair endonucleases (Endo-III, Fpg) was employed to specifically target oxidative DNA damage. Additionally, electron spin resonance (ESR) studies with different spin traps were carried out for qualitative analysis of free radical generation. For cell viability, TiO 2 alone (0.1-1000 μg ml -1 ) had little effect whereas co-exposure with UVA (0.5-2.0 kJ m -2 ) caused a significant dose-dependent decrease which was dependent on both the concentration of TiO 2 and the dose of UVA administered. For the Comet assay, doses of 1, 10 and 100 μg ml -1 in the absence of UVA caused elevated levels of Fpg-sensitive sites, indicating the oxidation of purine DNA bases (i.e. guanine) by TiO 2 . UVA irradiation of TiO 2 -treated cells caused further increases in DNA damage. ESR studies revealed that the observed toxic effects of nanoparticulate TiO 2 were most likely due to hydroxyl radical (·OH) formation

Development and Application of TiO2 Nanoparticles Coupled with Silver Halide

Directory of Open Access Journals (Sweden)

Xiaojia Wan

2014-01-01

Full Text Available Titanium dioxide (TiO2 is proposed to be effective photocatalyst for wastewater treatment, air purification, and self-cleaning ability, because of its strong oxidation and superhydrophilicity. In order to conquer the limits of TiO2, a variety of methods have been used. This paper presents a critical review of novel research and achievements in the modification of TiO2 nanoparticles with silver halide (AgX, X=Cl, Br, I, which aims at enhancing the visible light absorption and photosensitivity. Herein we study the synthesis, physical and chemical properties, and the mechanism of this composite photocatalyst.

Synthesis of anatase TiO2 nanoparticles with beta-cyclodextrin as a supramolecular shell.

Science.gov (United States)

Li, Landong; Sun, Xiaohong; Yang, Yali; Guan, Naijia; Zhang, Fuxiang

2006-11-20

We report a novel, green hydrothermal-synthesis route to well-dispersed anatase TiO2 nanoparticles with particle sizes of 9-16 nm in the presence of beta-CD (beta-cyclodextrin). During the synthesis process, the CD-containing synthesis mixture assembled in both longitudinal and latitudinal directions. Driven by the interaction between molecules, the beta-CDs assembled in the longitudinal direction to form long-chain compounds, whereas in the latitudinal direction, they tended to form regular aggregates through coordination with the Ti species from the hydrolysis of tetrabutyl titanate. In view of the effect of the coordination and the steric hindrance of beta-CDs as a supramolecular shell, homogeneous nuclei and slow growth of TiO2 crystals during the synthesis process was observed, which was responsible for the formation of uniform TiO2 nanoparticles. The low beta-CD dosage and the high product yield (>90%) demonstrated well the potential of this synthesis route in the large-scale industrial production of anatase nanoparticles.

Dispersion and Stabilization of Photocatalytic TiO2 Nanoparticles in Aqueous Suspension for Coatings Applications

Directory of Open Access Journals (Sweden)

Siti Hajar Othman

2012-01-01

Full Text Available To produce titanium dioxide (TiO2 nanoparticle coatings, it is desirable that the nanoparticles are dispersed into a liquid solution and remain stable for a certain period of time. Controlling the dispersion and aggregation of the nanoparticles is crucial to exploit the advantages of the nanometer-sized TiO2 particles. In this work, TiO2 nanoparticles were dispersed and stabilized in aqueous suspensions using two common dispersants which were polyacrylic acid (PAA and ammonium polymethacrylate (Darvan C. The effect of parameters such as ultrasonication amplitude and type and amount of dispersants on the dispersibility and stability of the TiO2 aqueous suspensions were examined. Rupture followed by erosion was determined to be the main break up mechanisms when ultrasonication was employed. The addition of dispersant was found to produce more dispersed and more stabilized aqueous suspension. 3 wt.% of PAA with average molecular weight (Mw of 2000 g/mol (PAA 2000 was determined to produce the best and most stable dispersion. The suspensions were then coated on quartz glass, whereby the photocatalytic activity of the coatings was studied via the degradation of formaldehyde gas under UV light. The coatings were demonstrated to be photocatalytically active.

Electrocatalytic glucose oxidation via hybrid nanomaterial catalyst of multi-wall TiO2 nanotubes supported Ni(OH)2 nanoparticles: Optimization of the loading level

International Nuclear Information System (INIS)

Gu, Yingying; Liu, Yicheng; Yang, Haihong; Li, Benqiang; An, Yarui

2015-01-01

Highlights: • Multi-wall TiO 2 nanotube supported Ni(OH) 2 nanoparticles, Ni(OH) 2 /TNTs, was prepared and investigated as anode electro-catalysts for glucose oxidation. • Ni(OH) 2 -24.2%/TNTs obtains the best catalytic activity. • Compared with Ni(OH) 2, the current density of Ni(OH) 2 -24.2%/TNTs increased 5.9 times in 0.1 M NaOH solution. - Abstract: The novel hybrid nanomaterial catalyst of multi-wall TiO 2 nanotube supported Ni(OH) 2 nanoparticles (Ni(OH) 2 /TNTs) was prepared through hydrothermal method and investigated as anode electro-catalysts for glucose oxidation. The nanostructure was characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscopy (TEM), thermogravimetry-differential thermal analysis (TGA) and nitrogen adsorption-desorption (BET-BJH). The electrochemical performance was measured by a range of electrochemical measurements. Compared with Ni(OH) 2 , the current density of Ni(OH) 2 /TNTs modified GC electrode increased 5.9 times in 0.1 M NaOH solution. The results indicated that the synthesized nanoparticles exhibited good electro-catalytic activity and stability for glucose oxidation. Meanwhile, the hybrid nanomaterial of Ni(OH) 2 /TNTs may be a potential candidate catalyst for direct glucose fuel cell

Influence of TiO2 particle size and conductivity of the CuCrO2 ...

Indian Academy of Sciences (India)

2017-11-28

Nov 28, 2017 ... Solid-state dye-sensitized solar cells; sol–gel method; TiO2 nanoparticle; CuCrO2 nanoparticles; electrical ... The purpose of this work is construction and optimization .... can be attributed to the electron transport mechanism.

Synthesis and Photocatalytic Activity of Anatase TiO2 Nanoparticles-coated Carbon Nanotubes

Directory of Open Access Journals (Sweden)

Xie Yi

2009-01-01

Full Text Available Abstract A simple and straightforward approach to prepare TiO2-coated carbon nanotubes (CNTs is presented. Anatase TiO2 nanoparticles (NPs with the average size ~8 nm were coated on CNTs from peroxo titanic acid (PTA precursor even at low temperature of 100 °C. We demonstrate the effects of CNTs/TiO2 molar ratio on the adsorption capability and photocatalytic efficiency under UV–visible irradiation. The samples showed not only good optical absorption in visible range, but also great adsorption capacity for methyl orange (MO dye molecules. These properties facilitated the great enhancement of photocatalytic activity of TiO2 NPs-coated CNTs photocatalysts. The TiO2 NPs-coated CNTs exhibited 2.45 times higher photocatalytic activity for MO degradation than that of pure TiO2.

Photoelectrocatalytic properties of Ag nanoparticles loaded TiO2 nanotube arrays prepared by pulse current deposition

International Nuclear Information System (INIS)

Xie Kunpeng; Sun Lan; Wang Chenglin; Lai Yuekun; Wang Mengye; Chen Hongbo; Lin Changjian

2010-01-01

A pulse current deposition technique was adopted to construct highly dispersed Ag nanoparticles on TiO 2 nanotube arrays which were prepared by the electrochemical anodization. The morphology, crystallinity, elemental composition, and UV-vis absorption of Ag/TiO 2 nanotube arrays were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and diffuse reflectance spectra (DRS). In particular, the photoelectrochemical properties and photoelectrocatalytic activity under UV light irradiation and the photocatalytic activity under visible light irradiation for newly synthesized Ag/TiO 2 nanotube arrays were investigated. The maximum incident photon to charge carrier efficiency (IPCE) value of Ag/TiO 2 nanotube arrays was 51%, much higher than that of pure TiO 2 nanotube arrays. Ag/TiO 2 nanotube arrays exhibited higher photocatalytic activities than the pure TiO 2 nanotube arrays under both UV and visible light irradiation. The photoelectrocatalytic activity of Ag/TiO 2 nanotube arrays under UV light irradiation was 1.6-fold enhancement compared with pure TiO 2 nanotube arrays. This approach can be used in synthesizing various metal-loaded nanotube arrays materials.

Room-temperature ferromagnetism in Co and Nb co-doped TiO2 nanoparticles

International Nuclear Information System (INIS)

Hachisu, M.; Mori, K.; Hyodo, K.; Morimoto, S.; Yamazaki, T.; Ichiyanagi, Y.

2015-01-01

Co- and Nb-doped TiO 2 nanoparticles encapsulated with amorphous SiO 2 were synthesized by our novel preparation method. An anatase TiO 2 single-phase structure was confirmed using X-ray diffraction. The particle size could be controlled to be about 5 nm. The composition of these nanoparticles was investigated by X-ray fluorescence analysis. X-ray absorption near-edge structure spectra showed that the Ti 4+ and Co 2+ states were dominant in our prepared samples. A reduction in the coordination number was also confirmed. The dependence of the electrical conductivity on the frequency was measured by an LCR meter, and the carrier concentration was determined. The magnetization curves for the nanoparticles indicated ferromagnetic behavior at room temperature. We concluded that the ferromagnetism originated in oxygen vacancies around the transition metal ions

Silicon surface passivation by PEDOT: PSS functionalized by SnO2 and TiO2 nanoparticles.

Science.gov (United States)

García-Tecedor, M; Karazhanov, S Zh; Vásquez, G C; Haug, H; Maestre, D; Cremades, A; Taeño, M; Ramírez-Castellanos, J; González-Calbet, J M; Piqueras, J; You, C C; Marstein, E S

2018-01-19

In this paper, we present a study of silicon surface passivation based on the use of spin-coated hybrid composite layers. We investigate both undoped poly(3,4-ethylenedioxythiophene)/poly-(styrenesulfonate) (PEDOT:PSS), as well as PEDOT:PSS functionalized with semiconducting oxide nanomaterials (TiO 2 and SnO 2 ). The hybrid compound was deposited at room temperature by spin coating-a potentially lower cost, lower processing time and higher throughput alternative compared with the commonly used vacuum-based techniques. Photoluminescence imaging was used to characterize the electronic properties of the Si/PEDOT:PSS interface. Good surface passivation was achieved by PEDOT:PSS functionalized by semiconducting oxides. We show that control of the concentration of semiconducting oxide nanoparticles in the polymer is crucial in determining the passivation performance. A charge carrier lifetime of about 275 μs has been achieved when using SnO 2 nanoparticles at a concentration of 0.5 wt.% as a filler in the composite film. X-ray diffraction (XRD), scanning electron microscopy, high resolution transmission electron microscopy (HRTEM), energy dispersive x-ray in an SEM, and μ-Raman spectroscopy have been used for the morphological, chemical and structural characterization. Finally, a simple model of a photovoltaic device based on PEDOT:PSS functionalized with semiconducting oxide nanoparticles has been fabricated and electrically characterized.

Photocatalytic degradation of paracetamol on TiO2 nanoparticles and TiO2/cellulosic fiber under UV and sunlight irradiation

Directory of Open Access Journals (Sweden)

Nabil Jallouli

2017-05-01

Full Text Available In the present study, photocatalytic degradation of acetaminophen ((N-(4-hydroxyphe-nylacetamide, an analgesic drug has been investigated in a batch reactor using TiO2 P25 as a photocatalyst in slurry and under UV light. Using TiO2 P25 nanoparticles, much faster photodegradation of paracetamol and effective mineralization occurred, more than 90% of 2.65 × 10−4 M paracetamol was degraded under UV irradiation. Changes in pH values affected the adsorption and the photodegradation of paracetamol. pH 9.0 is found to be the optimum for the photodegradation of paracetamol. HPLC detected hydroquinone, benzoquinone, p-nitrophenol, and 1,2,4-trihydroxybenzene during the TiO2-assisted photodegradation of paracetamol among which some pathway products are disclosed for the first time. The results showed that TiO2 suspension/UV system is more efficient than the TiO2/cellulosic fiber mode combined to solar light for the photocatalytic degradation of paracetamol. Nerveless the immobilization of TiO2 showed many advantages over slurry system because it can enhance adsorption properties while allowing easy separation of the photocatalyst from the treated solution with improved reusable performance.

Whiter, brighter, and more stable cellulose paper coated with TiO2 /SiO2 core/shell nanoparticles using a layer-by-layer approach.

Science.gov (United States)

Cheng, Fei; Lorch, Mark; Sajedin, Seyed Mani; Kelly, Stephen M; Kornherr, Andreas

2013-08-01

To inhibit the photocatalytic degradation of organic material supports induced by small titania (TiO2 ) nanoparticles, four kinds of TiO2 nanoparticles, that is, commercial P25-TiO2 , commercial rutile phase TiO2 , rutile TiO2 nanorods and rutile TiO2 spheres, prepared from TiCl4 , were coated with a thin, but dense, coating of silica (SiO2 ) using a conventional sol-gel technique to form TiO2 /SiO2 core/shell nanoparticles. These core/shell particles were deposited and fixed as a very thin coating onto the surface of cellulose paper samples by a wet-chemistry polyelectrolyte layer-by-layer approach. The TiO2 /SiO2 nanocoated paper samples exhibit higher whiteness and brightness and greater stability to UV-bleaching than comparable samples of blank paper. There are many potential applications for this green chemistry approach to protect cellulosic fibres from UV-bleaching in sunlight and to improve their whiteness and brightness. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Biocorrosion of TiO2 nanoparticle coating of Ti–6Al–4V in DMEM under specific in vitro conditions

International Nuclear Information System (INIS)

Höhn, Sarah; Virtanen, Sannakaisa

2015-01-01

Highlights: • Possibility to fabricate a TiO 2 NP-coating on Ti–6Al–4V by a simple spin-coating method. • The NP-coating enhances biomimetic apatite formation on the surface immersed in DMEM. • The TiO 2 coating can efficiently reduce Al release from the alloy during immersion in DMEM. • TiO 2 NP-coating makes the surface more bioactive. - Abstract: A TiO 2 nanoparticle coating was prepared on a biomedical Ti–6Al–4V alloy using “spin-coating” technique with a colloidal suspension of TiO 2 nanopowders with the aim to optimize the surface morphology (e.g., roughness) for improved biocompatibility. The influence of a TiO 2 nanoparticle (NP) coating on the corrosion behavior, metal ion release, and biomimetic apatite formation was studied in DMEM, at 37.5 °C with a continuous supply of 5% CO 2 . Electrochemical impedance spectroscopy measurements indicate a formation of a new layer on the surface of the NP-coated sample upon 28 days immersion in DMEM. Scanning electron microscopy (SEM) and X-ray spectroscopy confirm that the surface of the NP-coated Ti–6Al–4V shows a complete coverage by a Ca–phosphate layer in contrast to the non-coated Ti–6Al–4V alloy. Hence, the TiO 2 -NP coating strongly enhances biomimetic apatite formation on the alloy surface. In addition, the TiO 2 -NP coating can efficiently reduce Al-release from the alloy, for which the bare Ti–6Al–4V alloy is significant for at least 28 days of immersion in DMEM

Preparation of TiO sub 2 nanoparticles by pulsed laser ablation: Ambient pressure dependence of crystallization

CERN Document Server

Matsubara, M; Yamaki, T; Itoh, H; Abe, H

2003-01-01

Pulsed laser ablation (PLA) with a KrF excimer laser was used to prepare fine particles of titanium dioxide (TiO sub 2). The ablation in an atmosphere of Ar and O sub 2 (5:5) at total pressures of >= 1 Torr led to the formation of TiO sub 2 nanoparticles composed of anatase and rutile structures without any suboxides. The weight fraction of the rutile/anatase crystalline phases was dependent on the pressure of the Ar/O sub 2 gas. The TiO sub 2 nanoparticles had a spherical shape and their size, ranging from 10 and 14 nm, also appeared to be dependent on the ambient pressure. (author)

Antibacterial activity and inflammation inhibition of ZnO nanoparticles embedded TiO2 nanotubes

Science.gov (United States)

Yao, Shenglian; Feng, Xujia; Lu, Jiaju; Zheng, Yudong; Wang, Xiumei; Volinsky, Alex A.; Wang, Lu-Ning

2018-06-01

Titanium (Ti) with nanoscale structure on the surface exhibits excellent biocompatibility and bone integration. Once implanted, the surgical implantation may lead to bacterial infection and inflammatory reaction, which cause the implant failure. In this work, irregular and nanorod-shaped ZnO nanoparticles were doped into TiO2 nanotubes (TNTs) with inner diameter of about 50 nm by electro-deposition. The antibacterial properties of ZnO incorporated into TiO2 nanotubes (TNTs/ZnO) were evaluated using Staphylococcus aureus (S. aureus). Zn ions released from the nanoparticles and the morphology could work together, improving antibacterial effectiveness up to 99.3% compared with the TNTs. Macrophages were cultured on the samples to determine their respective anti-inflammatory properties. The proliferation and viability of macrophages were evaluated by the CCK-8 method and Live&Dead stain, and the morphology of the cells was observed by scanning electron microscopy. Results indicated that TNTs/ZnO has a significant inhibitory effect on the proliferation and adhesion of macrophages, which could be used to prevent chronic inflammation and control the inflammatory reaction. Besides, the release of Zn ions from the ZnO nanoparticles is a long-term process, which could be beneficial for bone integration. Results demonstrate that ZnO deposited into TNTs improved the antibacterial effectiveness and weakened the inflammatory reaction of titanium-based implants, which is a promising approach to enhance their bioactivity.

Photocatalytic properties of aqueous systems containing TiO2 nanoparticles

Czech Academy of Sciences Publication Activity Database

Paušová, Š.; Krýsa, J.; Jirkovský, Jaromír; Forano, C.; Prevot, V.; Mailhot, G.

2011-01-01

Roč. 161, č. 1 (2011), s. 140-146 ISSN 0920-5861 R&D Projects: GA MŠk 1M0577 Institutional research plan: CEZ:AV0Z40400503 Keywords : TiO2 nanoparticles * photocatalysis * aging Subject RIV: CG - Electrochemistry Impact factor: 3.407, year: 2011

High pressure synthesis of amorphous TiO2 nanotubes

Directory of Open Access Journals (Sweden)

Quanjun Li

2015-09-01

Full Text Available Amorphous TiO2 nanotubes with diameters of 8-10 nm and length of several nanometers were synthesized by high pressure treatment of anatase TiO2 nanotubes. The structural phase transitions of anatase TiO2 nanotubes were investigated by using in-situ high-pressure synchrotron X-ray diffraction (XRD method. The starting anatase structure is stable up to ∼20GPa, and transforms into a high-density amorphous (HDA form at higher pressure. Pressure-modified high- to low-density transition was observed in the amorphous form upon decompression. The pressure-induced amorphization and polyamorphism are in good agreement with the previous results in ultrafine TiO2 nanoparticles and nanoribbons. The relationship between the LDA form and α-PbO2 phase was revealed by high-resolution transmission electron microscopy (HRTEM study. In addition, the bulk modulus (B0 = 158 GPa of the anatase TiO2 nanotubes is smaller than those of the corresponding bulks and nanoparticles (180-240 GPa. We suggest that the unique open-ended nanotube morphology and nanosize play important roles in the high pressure phase transition of TiO2 nanotubes.

Disruption of Autolysis in Bacillus subtilis using TiO2 Nanoparticles.

Science.gov (United States)

McGivney, Eric; Han, Linchen; Avellan, Astrid; VanBriesen, Jeanne; Gregory, Kelvin B

2017-03-17

In contrast to many nanotoxicity studies where nanoparticles (NPs) are observed to be toxic or reduce viable cells in a population of bacteria, we observed that increasing concentration of TiO 2 NPs increased the cell survival of Bacillus subtilis in autolysis-inducing buffer by 0.5 to 5 orders of magnitude over an 8 hour exposure. Molecular investigations revealed that TiO 2 NPs prevent or delay cell autolysis, an important survival and growth-regulating process in bacterial populations. Overall, the results suggest two potential mechanisms for the disruption of autolysis by TiO 2 NPs in a concentration dependent manner: (i) directly, through TiO 2 NP deposition on the cell wall, delaying the collapse of the protonmotive-force and preventing the onset of autolysis; and (ii) indirectly, through adsorption of autolysins on TiO 2 NP, limiting the activity of released autolysins and preventing further lytic activity. Enhanced darkfield microscopy coupled to hyperspectral analysis was used to map TiO 2 deposition on B. subtilis cell walls and released enzymes, supporting both mechanisms of autolysis interference. The disruption of autolysis in B. subtilis cultures by TiO 2 NPs suggests the mechanisms and kinetics of cell death may be influenced by nano-scale metal oxide materials, which are abundant in natural systems.

Effects of TiO2 nanoparticles on the NO2− levels in cell culture media analysed by Griess colorimetric methods

International Nuclear Information System (INIS)

Popescu, Traian; Lupu, Andreea R.; Diamandescu, Lucian; Tarabasanu-Mihaila, Doina; Teodorescu, Valentin S.; Raditoiu, Valentin; Purcar, Violeta; Vlaicu, Aurel M.

2013-01-01

The Griess assay has been used to determine the possible changes in the measured NO 2 − concentrations induced by TiO 2 nanoparticles in three types of nitrite-containing samples: aqueous NaNO 2 solutions with known concentrations, and two types of cell culture media—Roswell Park Memorial Institute medium (RPMI-1640) and Dulbecco’s Modified Eagle Medium (DMEM-F12) used either as delivered or enriched in NO 2 − by NaNO 2 addition. We have used three types of titania with average particle sizes between 10 and 30 nm: Degussa P25 and two other samples (undoped and Fe 3+ -doped anatase TiO 2 ) synthesised by a hydrothermal route in our laboratory. The structural, morphological, optical and physicochemical characteristics of the used materials have been studied by X-ray diffraction, transmission electron microscopy (EDX), Mössbauer spectroscopy, Brunauer–Emmett–Teller nitrogen adsorption, UV–Vis reflectance spectroscopy, dynamic light scattering and diffuse reflectance infrared Fourier transform spectroscopy. The opacity and sedimentation behaviour of the studied TiO 2 suspensions have been investigated by photometric attenuance measurements at 540 nm. To account for the photocatalytic properties of titania in a biologically relevant context, multiple Griess tests have been performed under controlled exposure to laboratory natural daylight illumination. The results show significant variations of light attenuance (associated with NO 2 − concentrations in the Griess test) depending on the opacity, sedimentation behaviour, NO 2 − adsorption and photocatalytic properties of the tested TiO 2 nanomaterials. These findings identify material characteristics recommended to be considered when analysing the results of Griess tests performed in biological studies involving TiO 2 nanoparticles.

Synergistic effect of single-electron-trapped oxygen vacancies and carbon species on the visible light photocatalytic activity of carbon-modified TiO2

International Nuclear Information System (INIS)

Wang, Xiaodong; Xue, Xiaoxiao; Liu, Xiaogang; Xing, Xing; Li, Qiuye; Yang, Jianjun

2015-01-01

Carbon-modified TiO 2 (CT) nanoparticles were prepared via a two-step method of heat treatment without the resorcinol-formaldehyde (RF) polymer. As-prepared CT nanoparticles were characterized by means of X-ray diffraction (XRD), UV–Vis diffuse reflectance spectroscopy (UV–Vis/DRS), transmission electron microscopy (TEM), N 2 adsorption–desorption isotherms, thermal analysis (TA), electron spin resonance (ESR), and X-ray photoelectron spectroscopy (XPS). The visible light photocatalytic activities were evaluated on the basis of the degradation of methyl orange (MO). The synergistic effect of single-electron-trapped oxygen vacancies (SETOVs) and the carbon species on the visible light photocatalytic activities of the CT nanoparticles were discussed. It was found that the crystalline phase, the morphology, and particle size of the CT nanoparticles depended on the second heat-treatment temperature instead of the first heat-treatment temperature. The visible light photocatalytic activities were attributed to the synergistic effect of SETOVs and the carbon species, and also depended on the specific surface area of the photocatalysts. - Highlights: • Carbon-modified TiO 2 particles have been prepared without RF polymer. • The visible light photocatalytic activities of the particles have been evaluated. • The band gap energy structure of the carbon-modified TiO 2 has been proposed. • Synergistic effect of SETOVs and carbon species has been discussed. • The activities also depend on the specific surface area of the catalysts

Performance and electron transport properties of TiO2 nanocomposite dye-sensitized solar cells

International Nuclear Information System (INIS)

Wu, J-J; Chen, G-R; Lu, C-C; Wu, W-T; Chen, J-S

2008-01-01

TiO 2 nanowire (NW)/nanoparticle (NP) composite films have been fabricated by hybridizing various ratios of hydrothermal anatase NWs and TiO 2 NPs for use in dye-sensitized solar cells (DSSCs). Scanning electron microscopy (SEM) images reveal that uniform NW/NP composite films were formed on fluorine-doped tin oxide (FTO) substrates by the dip-coating method. The NWs are randomly but neither vertically nor horizontally oriented within the composite film. The TiO 2 NP DSSC possesses superior performance to those of the NW/NP composite and the pure NW cells, and the efficiency of the NW/NP composite DSSC increases on increasing the NP/NW ratio in the composite anode. All types of DSSC possess the same dependence of performance on the anode thickness that the efficiency increases with the anode thickness to a maximum value, then it decreases when the anode is thickened further. Electrochemical impedance spectroscopy analyses reveal that the NP DSSCs possess larger effective electron diffusion coefficients (D eff ) in the photoanodes and smaller diffusion resistances of I 3 - in electrolytes compared to those in the NW/NP and the NW DSSCs. D eff decreases when NWs are added into the photoanode. These results suggest that the vertical feature of the NWs within the anodes is crucial for achieving a high electron transport rate in the anode

Surface plasmon resonance effect of silver nanoparticles on a TiO2 electrode for dye-sensitized solar cells

Science.gov (United States)

Jung, Haeng-Yun; Yeo, In-Seon; Kim, Tae-Un; Ki, Hyun-Chul; Gu, Hal-Bon

2018-02-01

In this study, we exploit local surface plasmon resonance (LSPR) in order to improve the efficiency of dye-sensitized solar cells (DSSCs). In order to investigate the effect of LSPR, Ag nanoparticles of several sizes were formed using electro-beam equipment; sizes were varied by changing the annealing time. DSSCs were fabricated by coating Ag nanoparticles onto a TiO2 thin film. Finally, TiO2 nanoparticles were layered onto the Ag nanoparticles via a titanium tetra-isopropoxide (TTIP) treatment. This study used nanoparticle-coated TiO2 thin films as photoelectrodes, and manufactured the cell in the unit of the DSSCs. We compared the behavior of the electrical properties of DSSCs depending on the presence or absence of Ag nanoparticles, as well as on the nanoparticle size. The Ag particles did not affect dye adsorption because the content of Ag particles is very low (0.13%) compared to that in TiO2 in the photoelectrode. The DSSCs with LSPR showed increased electric current density compared to those without LSPR, and improved the solar conversion efficiency (η) by 24%. The current density of the DSSCs increased because the light absorption of the dye increased. Therefore, we determined that LSPR affects the electrical properties of DSSCs.

Toxicity of TiO2 nanoparticles to Escherichia coli: effects of particle size, crystal phase and water chemistry.

Directory of Open Access Journals (Sweden)

Xiuchun Lin

Full Text Available Controversial and inconsistent results on the eco-toxicity of TiO2 nanoparticles (NPs are commonly found in recorded studies and more experimental works are therefore warranted to elucidate the nanotoxicity and its underlying precise mechanisms. Toxicities of five types of TiO2 NPs with different particle sizes (10∼50 nm and crystal phases were investigated using Escherichia coli as a test organism. The effect of water chemistry on the nanotoxicity was also examined. The antibacterial effects of TiO2 NPs as revealed by dose-effect experiments decreased with increasing particle size and rutile content of the TiO2 NPs. More bacteria could survive at higher solution pH (5.0-10.0 and ionic strength (50-200 mg L(-1 NaCl as affected by the anatase TiO2 NPs. The TiO2 NPs with anatase crystal structure and smaller particle size produced higher content of intracellular reactive oxygen species and malondialdehyde, in line with their greater antibacterial effect. Transmission electron microscopic observations showed the concentration buildup of the anatase TiO2 NPs especially those with smaller particle sizes on the cell surfaces, leading to membrane damage and internalization. These research results will shed new light on the understanding of ecological effects of TiO2 NPs.

Toxicity of TiO2 Nanoparticles to Escherichia coli: Effects of Particle Size, Crystal Phase and Water Chemistry

Science.gov (United States)

Lin, Xiuchun; Li, Jingyi; Ma, Si; Liu, Gesheng; Yang, Kun; Tong, Meiping; Lin, Daohui

2014-01-01

Controversial and inconsistent results on the eco-toxicity of TiO2 nanoparticles (NPs) are commonly found in recorded studies and more experimental works are therefore warranted to elucidate the nanotoxicity and its underlying precise mechanisms. Toxicities of five types of TiO2 NPs with different particle sizes (10∼50 nm) and crystal phases were investigated using Escherichia coli as a test organism. The effect of water chemistry on the nanotoxicity was also examined. The antibacterial effects of TiO2 NPs as revealed by dose-effect experiments decreased with increasing particle size and rutile content of the TiO2 NPs. More bacteria could survive at higher solution pH (5.0–10.0) and ionic strength (50–200 mg L−1 NaCl) as affected by the anatase TiO2 NPs. The TiO2 NPs with anatase crystal structure and smaller particle size produced higher content of intracellular reactive oxygen species and malondialdehyde, in line with their greater antibacterial effect. Transmission electron microscopic observations showed the concentration buildup of the anatase TiO2 NPs especially those with smaller particle sizes on the cell surfaces, leading to membrane damage and internalization. These research results will shed new light on the understanding of ecological effects of TiO2 NPs. PMID:25310452

Internalization of Consumed TiO2 Nanoparticles by a Model Invertebrate Organism

Directory of Open Access Journals (Sweden)

Sara Novak

2012-01-01

Full Text Available There is little in vivo data concerning the fate of ingested TiO2 nanoparticles (nano-TiO2. We report here experiments aimed at assessing if ingested nano-TiO2 accumulates in the digestive gland epithelium or are internalized elsewhere in the body of the terrestrial isopod crustaceans. The animals (Porcellio scaber, Isopoda, Crustacea fed for 3, 7, or 14 days on food dosed with 100 or 1000 μg nano-TiO2 showed no evidence of internalization of Ti measured by microparticle-induced X-ray emission method. The effect of ingested nanoparticles was measured by conventional toxicity measures such as feeding rate, weight change, and mortality and did not indicate any toxicity. However, cell membrane of digestive glands, measured with a modified method for assessing cell membrane stability, was affected already after 3 days of exposure to 1000 μg nano-TiO2 per gram dry weight of food indicating cytotoxic potential of ingested nanoparticles. Our results confirmed hypothesis on low toxic potential and no internalization of consumed TiO2 nanoparticles by a model invertebrate organism. However, cytological marker unequivocally indicated adverse effect of ingested nano-TiO2. We conclude that the isopod model system could be used for studying the fate and effect of ingested nanoparticles.

Iron insertion and hematite segregation on Fe-doped TiO2 nanoparticles obtained from sol-gel and hydrothermal methods.

Science.gov (United States)

Santos, Reginaldo da S; Faria, Guilherme A; Giles, Carlos; Leite, Carlos A P; Barbosa, Herbert de S; Arruda, Marco A Z; Longo, Claudia

2012-10-24

Iron-doped TiO(2) (Fe:TiO(2)) nanoparticles were synthesized by the sol-gel method (with Fe/Ti molar ratio corresponding to 1, 3, and 5%), followed by hydrothermal treatment, drying, and annealing. A similar methodology was used to synthesize TiO(2) and α-Fe(2)O(3) nanoparticles. For comparison, a mixture hematite/titania, with Fe/Ti = 4% was also investigated. Characterization of the samples using Rietveld refinement of X-ray diffraction data revealed that TiO(2) consisted of 82% anatase and 18% brookite; for Fe:TiO(2), brookite increased to 30% and hematite was also identified (0.5, 1.0, and 1.2 wt % for samples prepared with 1, 3, and 5% of Fe/Ti). For hematite/titania mixture, Fe/Ti was estimated as 4.4%, indicating the Rietveld method reliability for estimation of phase composition. Because the band gap energy, estimated as 3.2 eV for TiO(2), gradually ranged from 3.0 to 2.7 eV with increasing Fe content at Fe:TiO(2), it can be assumed that a Fe fraction was also inserted as dopant in the TiO(2) lattice. Extended X-ray absorption fine structure spectra obtained for the Ti K-edge and Fe K-edge indicated that absorbing Fe occupied a Ti site in the TiO(2) lattice, but hematite features were not observed. Hematite particles also could not be identified in the images obtained by transmission electron microscopy, in spite of iron identification by elemental mapping, suggesting that hematite can be segregated at the grain boundaries of Fe:TiO(2).

Dielectric response and room temperature ferromagnetism in Cr doped anatase TiO2 nanoparticles

Science.gov (United States)

Naseem, Swaleha; Khan, Wasi; Khan, Shakeel; Husain, Shahid; Ahmad, Abid

2018-02-01

In the present work, nanocrystalline samples of Ti1-xCrxO2 (x = 0, 0.02, 0.04, 0.06 and 0.08) were synthesized in anatase phase through simple and cost effective acid modified sol gel method. The influence of Cr doping on thermal, microstructural, electrical and magnetic properties was investigated in TiO2 host matrix. The surface morphology has revealed less agglomeration and considerable reduction in particle size in case of Cr doped TiO2 as compared to undoped TiO2 nanoparticles (NPs). Energy dispersive x-ray spectroscopy (EDS), Raman and X-ray photoelectron spectroscopy (XPS) established high purity, appropriate stoichiometry and oxidation states of the compositions. The dielectric properties of the nanoparticles were altered by the doping concentration, applied frequency as well as temperature variation. The variation in dielectric constant (ε‧), dielectric loss (δ) and ac conductivity as a function of frequency and temperature at different doping concentration of Cr were interpreted in the light of Maxwell Wagner theory, space charge polarization mechanism and drift mobility of charge carriers. Both undoped and Cr doped TiO2 samples exhibit room temperature ferromagnetism (RTFM) that remarkably influenced by means of the Cr content. The significant enhancement in the magnetization was observed at 4% Cr doping. However, decrease in magnetization for higher doping signify antiferromagnetic interactions between Cr ions or superexchange mechanism. These results reveal that the oxygen vacancies play a crucial role to initiate the RTFM. Therefore, the present investigation suggests the potential applications of Cr doped TiO2 nanoparticles for spintronics application.

Uniformly distributed anatase TiO2 nanoparticles on graphene: Synthesis, characterization, and photocatalytic application

International Nuclear Information System (INIS)

Bai, Xue; Zhang, Xiaoyuan; Hua, Zulin; Ma, Wenqiang; Dai, Zhangyan; Huang, Xin; Gu, Haixin

2014-01-01

Highlights: • Uniform distributed TiO 2 nanoparticles on graphene by a modified method. • Reduced recombination rate of photogenerated electron–hole pairs. • Effective charge transfer from TiO 2 to graphene. • Better photocatalytic activity upon UV and visible irradiation. • A mechanism of bisphenol A degradation process is proposed. - Abstract: Graphene (GR)/TiO 2 nanocomposites are successfully synthesized using a simple and efficient hydrothermal method. Even-sized anatase TiO 2 nanoparticles are uniformly distributed on GR. The GR/TiO 2 nanocomposites exhibit an extended light absorption range and decreased electron–hole recombination rates. The photocatalytic activity of the as-prepared GR/TiO 2 nanocomposites for bisphenol A (BPA) degradation is investigated under UV (λ = 365 nm) and visible (λ ⩾ 400 nm) light irradiation. The results show that GR/TiO 2 nanocomposites have significantly higher photocatalytic activity than P25 (pure TiO 2 ). The large increase in photocatalytic activity is mostly attributed to effective charge transfer from TiO 2 nanoparticles to GR, which suppresses charge recombination during the photocatalytic process. After five successive cycles, the photodegradation activity of the GR/TiO 2 nanocomposites shows no significant decrease, which indicates that the nanocomposites are stable under UV and visible light. X-ray photoelectron spectroscopy (XPS) is used to investigate the chemical bonds of GR/TiO 2 nanocomposites before and after degradation to determine the degradation intermediate products of BPA under irradiation. A proposed degradation reaction pathway of BPA is also established. This study provides new insights into the fabrication and practical application of high-performance photocatalysts in wastewater treatment

Effect of tertiary amines on the synthesis and photovoltaic properties of TiO2 nanoparticles in dye sensitized solar cells

International Nuclear Information System (INIS)

Mir, Noshin; Salavati-Niasari, Masoud

2013-01-01

Highlights: • TiO 2 nanoparticles were synthesized via a two-step sol–gel method. • Two tertiary amines were selected as complexing agents. • Size control was achieved by selection of long chained amine. • The total conversion efficiency of 5.04% was reported as the best result. -- Abstract: Two different amines as complexing agents were used in a two-step sol–gel method to prepare TiO 2 nanoparticles. The effect of amines on the size of the TiO 2 nanocrystals and its influence on the performance of corresponding dye-sensitized solar cell (DSSC) were investigated. It is shown that using a tertiary long chained monoamine as a complexing agent is beneficial in two ways; one is producing the particles with smaller size and the other is slightly sticking the particles in order to have a film with higher reflectivity which both is beneficial to photovoltaic performance. The obtained products were characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared (FT-IR) spectra, and ultraviolet-visible (UV–vis) spectroscopy. The overall conversion efficiency of the long-chain-based DSSC (5.04%) appeared to be 45% higher than that obtained for the tertiary short-chain diamine

Anti-fish bacterial pathogen effect of visible light responsive Fe3O4@TiO2 nanoparticles immobilized on glass using TiO2 sol–gel

International Nuclear Information System (INIS)

Yeh, N.; Lee, Y.C.; Chang, C.Y.; Cheng, T.C.

2013-01-01

This paper demonstrates a fish pathogen reduction procedure that uses TiO 2 sol–gel coating Fe 3 O 4 @TiO 2 powder on glass substrate. Such procedure can effectively relieve two constraints that haunt TiO 2 sterilization applications: 1) the need for UV for overcoming the wide band gap of pure TiO 2 and 2) the difficulty of its recovering from water for reuse. In the process, visible light responsive Fe 3 O 4 /TiO 2 nanoparticles are synthesized and immobilized on glass using TiO 2 sol–gel as the binder for fish bacterial pathogen disinfection test. After 3 h of visible light irradiation, the immobilized Fe 3 O 4 @TiO 2 's inhibition efficiencies for fish bacterial pathogen are, respectively, 50% for Edwardsiella tarda (BCRC 10670) and 23% for Aeromonas hydrophila (BCRC 13018)

How Pt nanoparticles affect TiO2-induced gas-phase photocatalytic oxidation reactions

NARCIS (Netherlands)

Fraters, B.D.; Amrollahi Buky, Rezvaneh; Mul, Guido

2015-01-01

The effect of Pt nanoparticles on the gas-phase photocatalytic oxidation activity of TiO2 is shown to be largely dependent on the molecular functionality of the substrate. We demonstrate that Pt nanoparticles decrease rates in photocatalytic oxidation of propane, whereas a strong beneficial effect

In vivo screening to determine hazards of nanoparticles: Nanosized TiO2

International Nuclear Information System (INIS)

Drobne, Damjana; Jemec, Anita; Pipan Tkalec, Ziva

2009-01-01

A single-species laboratory test with terrestrial invertebrates was used to identify the hazard of nanosized TiO 2 . Feeding parameters, weight change, mortality, and the activities of catalase and glutathione-S-transferase were evaluated after 3 or 14 days of dietary exposure. The effects of nano-TiO 2 were dependent on exposure concentration and duration, total consumed quantity, size and pre-treatment of particles. The intensity of a response was ruled by duration of exposure and not by consumed quantity of nano-TiO 2 or exposure concentration as expected. The response to nano-TiO 2 is described as threshold-like. The exposure concentrations 10-1000 μg TiO 2 /g dry food (1.35-1025 μg of total consumed quantity of TiO 2 /g animal wet wt.) were identified as safe for tested species after tested exposure period. We conclude that the response to nanoparticles is different from that of soluble chemicals therefore these two types of data should be interpreted and processed differently. - The response of a biological system to nanoparticles is unique and depends on their physico-chemical characteristics, dose and duration of exposure

A Facile Method for Loading CeO2 Nanoparticles on Anodic TiO2 Nanotube Arrays.

Science.gov (United States)

Liao, Yulong; Yuan, Botao; Zhang, Dainan; Wang, Xiaoyi; Li, Yuanxun; Wen, Qiye; Zhang, Huaiwu; Zhong, Zhiyong

2018-04-03

In this paper, a facile method was proposed to load CeO 2 nanoparticles (NPs) on anodic TiO 2 nanotube (NT) arrays, which leads to a formation of CeO 2 /TiO 2 heterojunctions. Highly ordered anatase phase TiO 2 NT arrays were fabricated by using anodic oxidation method, then these individual TiO 2 NTs were used as tiny "nano-containers" to load a small amount of Ce(NO 3 ) 3 solutions. The loaded anodic TiO 2 NTs were baked and heated to a high temperature of 450 °C, under which the Ce(NO 3 ) 3 would be thermally decomposed inside those nano-containers. After the thermal decomposition of Ce(NO 3 ) 3 , cubic crystal CeO 2 NPs were obtained and successfully loaded into the anodic TiO 2 NT arrays. The prepared CeO 2 /TiO 2 heterojunction structures were characterized by a variety of analytical technologies, including XRD, SEM, and Raman spectra. This study provides a facile approach to prepare CeO 2 /TiO 2 films, which could be very useful for environmental and energy-related areas.

Influences of a new templating agent on the synthesis of coral-like TiO2 nanoparticles and their photocatalytic activity

Directory of Open Access Journals (Sweden)

Satwant Kaur Shahi

2017-09-01

Full Text Available We report a low cost and environmentally-friendly solvent system to synthesize TiO2 nanoparticles using an acidic deep eutectic solvent, choline chloride/p-toluene sulphonic acid as a templating and hydrolyzing agent via sol–gel method. The effect of varying concentration of the deep eutectic solvent (DES on the important physico-chemical characteristics of as-synthesized TiO2 such as phase, morphology, particle size, surface area and band gap energy was studied. A detailed characterization of the obtained nanomaterials has been performed using various techniques, including X-ray diffraction (XRD, Scanning electron microscopy (SEM, Brunauer–Emmett–Teller (BET surface area, Raman and Ultraviolet–visible absorption spectroscopy. The spherical TiO2 nanoparticles were found to be biphasic with two phases: anatase and rutile having crystallite sizes in the range of 5.6–6.8 nm. These nanoparticles assembled together to form a coral-like morphology. The effect of calcination temperature on the synthesized products was studied by heating at 750 °C. The photocatalytic activity of the prepared TiO2 materials was evaluated by the photo-discoloration of an aqueous methyl orange dye solution (20 ppm under UV light irradiation. The results indicate that the photocatalytic efficiency of an anatase–rutile mixture in the optimal sample DES-3 is higher (98% within 3 h than a commercially available Degussa P-25 (87% within 3 h.

Studies on interfacial interactions of TiO2 nanoparticles with ...

Indian Academy of Sciences (India)

Administrator

Studies on interfacial interactions of TiO2 nanoparticles with bacterial cells under light and dark conditions by Swayamprava Dalai et al (pp 371–381). Graphical abstract. Sequence of events occurring in course of cell-NP interaction: Surface adsorption, internalization and bioaccumulation of NPs which leads to stress upon ...

CdS-sensitized TiO2 nanocorals: hydrothermal synthesis, characterization, application.

Science.gov (United States)

Mali, S S; Desai, S K; Dalavi, D S; Betty, C A; Bhosale, P N; Patil, P S

2011-10-01

Cadmium sulfide (CdS) nanoparticle-sensitized titanium oxide nanocorals (TNC) were synthesized using a two-step deposition process. The TiO(2) nanocorals were grown on the conducting glass substrates (FTO) using A hydrothermal process and CdS nanoparticles were loaded on TNC using successive ionic layer adsorption and reaction (SILAR) method. The TiO(2), CdS and TiO(2)-CdS samples were characterized by optical absorption, X-ray diffraction (XRD), FT-Raman, FT-IR, scanning electron microscopy (SEM) and contact angle. Further, their photoelectrochemical (PEC) performance was tested in NaOH, Na(2)S-NaOH-S and Na(2)S electrolytes, respectively. When CdS nanoparticles are coated on TNCs, the optical absorption is found to be enhanced and band edge is red-shifted towards visible region. The TiO(2)-CdS sample exhibits improved photoelectrochemical (PEC) performance with maximum short circuit current of (J(sc)) 1.04 mA cm(-2). After applying these TiO(2)-CdS electrodes in photovoltaic cells, the photocurrent was found to be enhanced by 2.7 and 32.5 times, as compared with those of bare CdS and TiO(2) nanocorals films electrodes respectively. Also, the power conversion efficiency of TiO(2)-CdS electrodes is 0.72%, which is enhanced by about 16 and 29 times for TiO(2), CdS samples. This journal is © The Royal Society of Chemistry and Owner Societies 2011

TiO2 nanoparticles cause mitochondrial dysfunction, activate inflammatory responses, and attenuate phagocytosis in macrophages: A proteomic and metabolomic insight

Directory of Open Access Journals (Sweden)

Qun Chen

2018-05-01

Full Text Available Titanium dioxide nanoparticles (TiO2 NPs are widely used in food and cosmetics but the health impact of human exposure remains poorly defined. Emerging evidence suggests that TiO2 NPs may elicit immune responses by acting on macrophages. Our proteomic study showed that treatment of macrophages with TiO2 NPs led to significant re-organization of cell membrane and activation of inflammation. These observations were further corroborated with transmission electron microscopy (TEM experiments, which demonstrated that TiO2 NPs were trapped inside of multi-vesicular bodies (MVB through endocytotic pathways. TiO2 NP caused significant mitochondrial dysfunction by increasing levels of mitochondrial reactive oxygen species (ROS, decreasing ATP generation, and decreasing metabolic flux in tricarboxylic acid (TCA cycle from 13C-labelled glutamine using GC-MS-based metabolic flux analysis. Further lipidomic analysis showed that TiO2 NPs significantly decreased levels of cardiolipins, an important class of mitochondrial phospholipids for maintaining proper function of electron transport chains. Furthermore, TiO2 NP exposure activates inflammatory responses by increasing mRNA levels of TNF-α, iNOS, and COX-2. Consistently, our targeted metabolomic analysis showed significantly increased production of COX-2 metabolites including PGD2, PGE2, and 15d-PGJ2. In addition, TiO2 NP also caused significant attenuation of phagocytotic function of macrophages. In summary, our studies utilizing multiple powerful omic techniques suggest that human exposure of TiO2 NPs may have profound impact on macrophage function through activating inflammatory responses and causing mitochondrial dysfunction without physical presence in mitochondria.

Ce-doped nanoparticles of TiO2: Rutile-to-brookite phase transition and evolution of Ce local-structure studied with XRD and XANES

International Nuclear Information System (INIS)

Kityakarn, Sutasinee; Worayingyong, Attera; Suramitr, Anwaraporn; Smith, M.F.

2013-01-01

The crystal and electronic structural changes undergone by TiO 2 nanoparticles when Ce is introduced were studied using X-ray diffraction (XRD) and X-ray absorption near-edge spectroscopy (XANES). A small amount of Ce (less than 1% molar concentration) resulted in i/a significant reduction of the average size of the TiO 2 nanoparticles and ii/a phase transition in which brookite replaced rutile as the minority phase component (anatase was the majority phase component at all Ce concentrations studied up to 10% molar concentration). The Ce L3 edge XANES revealed changes in the local environment of Ce impurities. As Ce concentration was increased the fraction of Ce that have formal valence of +3 decreased and, for the remaining Ce with valence +4, the 4f orbitals became less-strongly hybridized with the p-orbitals of oxygen neighbors. The results have implications for photocatalytic and gas sensing properties of Ce-doped TiO 2 . - Highlights: ► Ce-doping: TiO 2 nanoparticles shrink and minority phase changes rutile-> brookite. ► XANES reveals phase change for arbitrarily small particles (while XRD fails). ► As Ce added: fraction of Ce +3 dopants falls, hybridization of Ce +4 with O weakens

Data on rhizosphere pH, phosphorus uptake and wheat growth responses upon TiO2 nanoparticles application

Directory of Open Access Journals (Sweden)

Rafia Rafique

2018-04-01

Full Text Available In this study, the data sets and analyses provided the information on the characterization of titanium dioxide nanoparticles (TiO2 NPs, and their impacts on rhizosphere pH, and soil-bound phosphorus (P availability to plants together with relevant parameters. For this purpose, wheat (Triticum aestivum L. was cultivated in the TiO2 NPs amended soil over a period of 60 days. After harvesting, the soil and plants were analyzed to examine the rhizosphere pH, P availability in rhizosphere soil, uptake in roots and shoots, biomass produced, chlorophyll content and translocation to different plant parts monitored by SEM and EDX techniques in response to different dosages of TiO2 NPs. The strong relationship can be found among TiO2 NPs application, P availability, and plant growth. Keywords: Rhizosphere pH, TiO2 NPs nanoparticles, Wheat, Phosphorus, Uptake

Toxicity of nanoparticles of CuO, ZnO and TiO2 to microalgae Pseudokirchneriella subcapitata.

Science.gov (United States)

Aruoja, Villem; Dubourguier, Henri-Charles; Kasemets, Kaja; Kahru, Anne

2009-02-01

Toxicities of ZnO, TiO2 and CuO nanoparticles to Pseudokirchneriella subcapitata were determined using OECD 201 algal growth inhibition test taking in account potential shading of light. The results showed that the shading effect by nanoparticles was negligible. ZnO nanoparticles were most toxic followed by nano CuO and nano TiO2. The toxicities of bulk and nano ZnO particles were both similar to that of ZnSO4 (72 h EC50 approximately 0.04 mg Zn/l). Thus, in this low concentration range the toxicity was attributed solely to solubilized Zn2+ ions. Bulk TiO2 (EC50=35.9 mg Ti/l) and bulk CuO (EC50=11.55 mg Cu/l) were less toxic than their nano formulations (EC50=5.83 mg Ti/l and 0.71 mg Cu/l). NOEC (no-observed-effect-concentrations) that may be used for risk assessment purposes for bulk and nano ZnO did not differ (approximately 0.02 mg Zn/l). NOEC for nano CuO was 0.42 mg Cu/l and for bulk CuO 8.03 mg Cu/l. For nano TiO2 the NOEC was 0.98 mg Ti/l and for bulk TiO2 10.1 mg Ti/l. Nano TiO2 formed characteristic aggregates entrapping algal cells that may contribute to the toxic effect of nano TiO2 to algae. At 72 h EC50 values of nano CuO and CuO, 25% of copper from nano CuO was bioavailable and only 0.18% of copper from bulk CuO. Thus, according to recombinant bacterial and yeast Cu-sensors, copper from nano CuO was 141-fold more bioavailable than from bulk CuO. Also, toxic effects of Cu oxides to algae were due to bioavailable copper ions. To our knowledge, this is one of the first systematic studies on effects of metal oxide nanoparticles on algal growth and the first describing toxic effects of nano CuO towards algae.

Enhanced Photocatalytic Properties of Ag-Loaded N-Doped Tio2 Nanotube Arrays

Directory of Open Access Journals (Sweden)

Gao Dawei

2018-03-01

Full Text Available Highly ordered TiO2 nanotube (TiO2 NT arrays were prepared by anodic oxidizing method on the surface of the Ti substrate. Nitrogen-doped TiO2 nanotube (N-TiO2 NT arrays were carried out by ammonia solution immersion, and Ag nanoparticles loaded N-doped TiO2 nanotube (Ag/N-TiO2 NT arrays were obtained by successive ionic layer adsorption and reaction (SILAR technique. The samples were characterized by the X-ray diffraction (XRD, X-ray photoelectron spectroscopy (XPS, field emission scanning electron microscopy (FESEM, high-resolution transmission electron microscopy (HRTEM, photoluminescence (PL emission spectra, ultraviolet–visible (UV–vis diffuse reflectance spectroscopy (DRS. The result indicated that the diameter and wall thickness of the TiO2 NT are 100–120 and 20–30 nm, respectively. Moreover, the morphology and structure of the highly ordered TiO2 NTs were not affected by N-doping. Furthermore, Ag nanoparticles were evenly deposited on the surface of TiO2 NTs in the form of elemental silver. Finally, the photocatalytic activity of Ag/N-TiO2 NTs was evaluated by degradation of methyl orange (MO under visible-light irradiation. The Ag/N-TiO2 NTs exhibited enhanced photocatalytic properties, which could reach 95% after 90-min irradiation.

Growth and characterization of hydroxyapatite nanorice on TiO2 nanofibers

KAUST Repository

Chetibi, Loubna

2014-04-01

Hydroxyapatite (HA) coating with nanoparticles like nanorice is fabricated on chemically pretreated titanium (Ti) surface, through an electrochemical deposition approach, for biomaterial applications. The Ti surface was chemically patterned with anatase TiO2 nanofibers. These nanofibers were prepared by in situ oxidation of Ti foils in a concentrated solution of H 2O2 and NaOH, followed by proton exchange and calcinations. Afterward, TiO2 nanofibers on Ti substrate were coated with HA nanoparticles like nanorice. The obtained samples were annealed at high temperature to produce inter diffusion between TiO2 and HA layers. The resultant layers were characterized by Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM), X-ray Photoelectron Spectroscopy (XPS), X-ray Diffraction (XRD), Infrared Spectroscopy (FTIR), corrosion tests in SBF solution, and Electron Probe Micro Analysis (EPMA). It was found that only Ti from the titanium substrate diffuses into the HA coating and a good corrosion resistance in simulated body fluid was obtained. © 2014 Elsevier B.V. All rights reserved.

The protective roles of TiO2 nanoparticles against UV-B toxicity in Daphnia magna.

Science.gov (United States)

Liu, Jie; Wang, Wen-Xiong

2017-09-01

Aquatic environments are increasingly under environmental stress due to ultraviolet (UV) radiation and potential inputs of nanoparticles with intense application of nanotechnology. In this study, we investigated the interaction between UV-B radiation and titanium nanoparticles (TiO 2 -NPs) in a model freshwater cladoceran Daphnia magna. UV-B toxicity to Daphnia magna was examined when the daphnids were exposed to a range of TiO 2 -NPs concentrations with an initial 5 or 10min of 200μW/cm 2 UV-B radiation. In addition, UV-B toxicity was also examined in the presence of TiO 2 -NPs in the body of daphnids. Our results demonstrated that the daphnid mortality under UV-B radiation decreased significantly in the presence of TiO 2 -NPs both in the water and in the body, indicating that TiO 2 -NPs had some protective effects on D. magna against UV-B. Such protective effect was mainly caused by the blockage of UV-B by TiO 2 -NPs adsorption. UV-B produced reactive oxygen species (ROS) in the water and in the daphnids, which was not sufficient to cause mortality of daphnids over short periods of radiation. Previous studies focused on the effects of TiO 2 -NPs on the toxicity of total UV radiation, and did not attempt to differentiate the potential diverse roles of UV-A and UV-B. Our study indicated that TiO 2 -NPs may conversely protect the UV-B toxicity to daphnids. Copyright © 2017 Elsevier B.V. All rights reserved.

Synthesis of TiO2 Nanoparticles from Ilmenite Through the Mechanism of Vapor-Phase Reaction Process by Thermal Plasma Technology

Science.gov (United States)

Samal, Sneha

2017-11-01

Synthesis of nanoparticles of TiO2 was carried out by non-transferred arc thermal plasma reactor using ilmenite as the precursor material. The powder ilmenite was vaporized at high temperature in plasma flame and converted to a gaseous state of ions in the metastable phase. On cooling, chamber condensation process takes place on recombination of ions for the formation of nanoparticles. The top-to-bottom approach induces the disintegration of complex ilmenite phases into simpler compounds of iron oxide and titanium dioxide phases. The vapor-phase reaction mechanism was carried out in thermal plasma zone for the synthesis of nanoparticles from ilmenite compound in a plasma reactor. The easy separation of iron particles from TiO2 was taken place in the plasma chamber with deposition of light TiO2 particles at the top of the cooling chamber and iron particles at the bottom. The dissociation and combination process of mechanism and synthesis are studied briefly in this article. The product TiO2 nanoparticle shows the purity with a major phase of rutile content. TiO2 nanoparticles produced in vapor-phase reaction process shows more photo-induced capacity.

The effect of TiO2 nanoparticles on water permeability and thermal and mechanical properties of high strength self-compacting concrete

International Nuclear Information System (INIS)

Nazari, Ali; Riahi, Shadi

2010-01-01

Research highlights: → TiO 2 nanoparticles effects on self-compacting concrete. → Strength assessments. → Water permeability. → Thermal properties. → Pore structure. → Microstructure evaluations. - Abstract: In this work, strength assessments and coefficient of water absorption of high performance self-compacting concrete containing different amounts of TiO 2 nanoparticles have been investigated. The results indicate that the strength and the resistance to water permeability of the specimens are improved by adding TiO 2 nanoparticles in the cement paste up to 4.0 wt%. TiO 2 nanoparticles, as a result of increased crystalline Ca(OH) 2 amount especially at the early age of hydration, could accelerate C-S-H gel formation and hence increase the strength of the concrete specimens. In addition, TiO 2 nanoparticles are able to act as nanofillers and recover the pore structure of the specimens by decreasing harmful pores. Several empirical relationships have been presented to predict flexural and split tensile strength of the specimens by means of the corresponding compressive strength at a certain age of curing. Accelerated peak appearance in conduction calorimetry tests, more weight loss in thermogravimetric analysis and more rapid appearance of the peaks related to hydrated products in X-ray diffraction results, all indicate that TiO 2 nanoparticles could improve mechanical and physical properties of the concrete specimens.

Manufacturing and investigation of surface morphology and optical properties of composite thin films reinforced by TiO2, Bi2O3 and SiO2 nanoparticles

Science.gov (United States)

Jarka, Paweł; Tański, Tomasz; Matysiak, Wiktor; Krzemiński, Łukasz; Hajduk, Barbara; Bilewicz, Marcin

2017-12-01

The aim of submitted paper is to present influence of manufacturing parameters on optical properties and surface morphology of composite materials with a polymer matrix reinforced by TiO2 and SiO2 and Bi2O3 nanoparticles. The novelty proposed by the authors is the use of TiO2 and SiO2 and Bi2O3 nanoparticles simultaneously in polymeric matrix. This allows using the combined effect of nanoparticles to a result composite material. The thin films of composite material were prepared by using spin-coating method with various spinning rates from solutions of different concentration of nanoparticles. In order to prepare the spinning solution polymer, Poly(methyl methacrylate) (PMMA) was used as a matrix. The reinforcing phase was the mixture of the nanoparticles of SiO2, TiO2 and B2O3. In order to identify the surface morphology of using thin films and arrangement of the reinforcing phase Atomic Force Microscope (AFM) and Scanning Electron Microscope (SEM) were used. In order to study the optical properties of the obtained thin films, the thin films of composites was subjected to an ellipsometry analysis. The measurements of absorbance of the obtained materials, from which the value of the band gap width was specified, were carried out using the UV/VIS spectroscopy. The optical properties of obtain composite thin films depend not only on the individual components used, but also on the morphology and the interfacial characteristics. Controlling the participation of three kinds of nanoparticles of different sizes and optical parameters allows to obtaining the most optimal optical properties of nanocomposites and also controlling the deposition parameters allows to obtaining the most optimal surface morphology of nanocomposites.

Experimental measurement and modelling of reactive species generation in TiO2 nanoparticle photocatalysis.

Science.gov (United States)

Turolla, Andrea; Piazzoli, Andrea; Budarz, Jeffrey Farner; Wiesner, Mark R; Antonelli, Manuela

2015-07-01

The generation of reactive species in titanium dioxide (TiO 2 ) nanoparticle photocatalysis was assessed in a laboratory scale setup, in which P25 Aeroxide TiO 2 suspensions were photoactivated by means of UV-A radiation. Photogenerated holes and hydroxyl radicals were monitored over time by observing their selective reaction with probe compounds, iodide and terephthalic acid, respectively. TiO 2 aggregate size and structure were characterized over the reaction time. Reactive species quenching was then described by a model, accounting for radiative phenomena, TiO 2 nanoparticle aggregation and kinetic reactions. The interaction between iodide and photogenerated holes was influenced by iodide adsorption on TiO 2 surface, described by a Langmuir-Hinshelwood mechanism, whose parameters were studied as a function of TiO 2 concentration and irradiation time. Iodide oxidation was effectively simulated by modelling the reaction volume as a completely stirred two-dimensional domain, in which irradiation phenomena were described by a two-flux model and the steady state for reactive species was assumed. The kinetic parameters for iodide adsorption and oxidation were estimated and successfully validated in a different experimental setup. The same model was adapted to describe the oxidation of terephthalic acid by hydroxyl radicals. The kinetic parameters for terephthalic acid oxidation were estimated and validated, while the issues in investigating the interaction mechanisms among the involved species have been discussed. The sensitivity of operating parameters on model response was assessed and the most relevant parameters were highlighted.

CoFe2O4-TiO2 Hybrid Nanomaterials: Synthesis Approaches Based on the Oil-in-Water Microemulsion Reaction Method

Directory of Open Access Journals (Sweden)

Arturo Adrián Rodríguez-Rodríguez

2017-01-01

Full Text Available CoFe2O4 nanoparticles decorated and wrapped with TiO2 nanoparticles have been prepared by mixing well-dispersed CoFe2O4 with amorphous TiO2 (impregnation approach and growing amorphous TiO2 over the magnetic core (seed approach, respectively, followed by thermal treatment to achieve TiO2 crystallinity. Synthesis strategies were based on the oil-in-water microemulsion reaction method. Thermally treated nanomaterials were characterized in terms of structure, morphology, and composition, to confirm hybrid nanoparticles formation and relate with the synthesis approaches; textural, optical, and magnetic properties were evaluated. X-ray diffraction revealed coexistence of cubic spinel-type CoFe2O4 and tetragonal anatase TiO2. Electron microscopy images depicted crystalline nanoparticles (sizes below 25 nm, with homogeneous Ti distribution for the hybrid nanoparticles synthesized by seed approach. EDX microanalysis and ICP-AES corroborated established chemical composition. XPS evidenced chemical states, as well as TiO2 predominance over CoFe2O4 surface. According to BET measurements, the hybrid nanoparticles were mesoporous. UV-Vis spectroscopy showed optical response along the UV-visible light region. Magnetic properties suggested the breaking order of magnetic domains due to modification with TiO2, especially for mediated seed approach sample. The properties of the obtained hybrid nanoparticles were different in comparison with its individual components. The results highlight the usefulness of designed microemulsion approaches for the straightforward synthesis of CoFe2O4-TiO2 nanostructured hybrids.

Interaction of TiO2 nanoparticles with the marine microalga Nitzschia closterium: Growth inhibition, oxidative stress and internalization

International Nuclear Information System (INIS)

Xia, Bin; Chen, Bijuan; Sun, Xuemei; Qu, Keming; Ma, Feifei; Du, Meirong

2015-01-01

The toxicity of TiO 2 engineered nanoparticles (NPs) to the marine microalga Nitzschia closterium was investigated by examining growth inhibition, oxidative stress and uptake. The results indicated that the toxicity of TiO 2 particles to algal cells significantly increased with decreasing nominal particle size, which was evidenced by the 96 EC 50 values of 88.78, 118.80 and 179.05 mg/L for 21 nm, 60 nm and 400 nm TiO 2 particles, respectively. The growth rate was significantly inhibited when the alga was exposed to 5 mg/L TiO 2 NPs (21 nm). Measurements of antioxidant enzyme activities showed that superoxide dismutase (SOD), catalase (CAT) and peroxidase (POD) activities were first induced and subsequently inhibited following exposure to 5 mg/L TiO 2 NPs. The depletion of antioxidant enzymes with a concomitant increase in malondialdehyde (MDA) levels and reactive oxygen species (ROS) posed a hazard to membrane integrity. A combination of flow cytometry analysis, transmission electron microscopy and Ti content measurement indicated that TiO 2 NPs were internalized in N. closterium cells. The level of extracellular ROS, which was induced by TiO 2 NPs under visible light, was negligible when compared with the intracellular ROS level (accounting for less than 6.0% of the total ROS level). These findings suggest that elevated TiO 2 nanotoxicity in marine environments is related to increased ROS levels caused by internalization of TiO 2 NPs. - Highlights: • Inhibition of marine microalgae by TiO 2 NPs and bulk particles was evaluated. • Aggregation of TiO 2 NPs and bulk particles was observed in marine algal test medium. • TiO 2 NPs induced damage to algal cell membranes as detected by flow cytometry. • Increased TiO 2 nanotoxicity to algal cells was caused by internalization of NPs

Porous TiO_2 nanofibers decorated CdS nanoparticles by SILAR method for enhanced visible-light-driven photocatalytic activity

International Nuclear Information System (INIS)

Tian, Fengyu; Hou, Dongfang; Hu, Fuchao; Xie, Kui; Qiao, Xiuqing; Li, Dongsheng

2017-01-01

Graphical abstract: A heterojunction photocatalyst with CdS Nanoparticles self-assembled via SILAR Method at surfaces of electrospun TiO2 nanofibers shows enhanced visible-light photocatalytic activities. - Highlights: • Combined electrospinning and successive ionic layer adsorption and reaction process. • Pouous TiO_2 nanofibers decorated CdS nanoparticles. • Synergetic effect of photosensitization and heterojunction. - Abstract: 1D porous CdS nanoparticles/TiO_2 nanofibers heterostructure has been fabricated via simple electrospinning and a successive ionic layer adsorption and reaction (SILAR) process. The morphology, composition, and optical properties of the resulting CdS/TiO_2 heterostructures can be rationally tailored through changing the SILAR cycles. The photocatalytic hydrogen evolution and decomposition of rhodamine B (RhB) of the as-synthesized heterostructured photocatalysts were investigated under visible light irradiation. Compared to TiO_2 nanofibers，the as-obtained CdS/TiO_2 heterostructures exhibit enhanced photocatalytic activity for hydrogen production and decomposition of RhB under visible-light irradiation. The heterojunction system performs best with H_2 generation rates of 678.61 μmol h"−"1 g"−"1 under visible light irradiation which benefits from the two effects: (a) the 1D porous nanofibrous morphology contributes to not only more active sites but also more efficient transfer of the photogenerated charges (b) the synergetic effect of heterojunction and photosensitization reducing the recombination of photogenerated electrons and holes.

Titanium dioxide (TiO2) nanoparticles filled poly(d,l lactid acid) (PDLLA) matrix composites for bone tissue engineering

NARCIS (Netherlands)

Gerhardt, L.C.; Jell, G.M.R.; Boccaccini, A.R.

2007-01-01

Titanium dioxide (TiO2) nanoparticles were investigated for bone tissue engineering applications with regard to bioactivity and particle cytotoxicity. Composite films on the basis of poly(d,l lactid acid) (PDLLA) filled with 0, 5 and 30 wt% TiO2 nanoparticles were processed by solvent casting.

Monitoring the Environmental Impact of TiO2 Nanoparticles Using a Plant-Based Sensor Network

Science.gov (United States)

Lenaghan, Scott C.; Li, Yuanyuan; Zhang, Hao; Burris, Jason N.; Stewart, C. Neal; Parker, Lynne E.; Zhang, Mingjun

2016-01-01

The increased manufacturing of nanoparticles for use in cosmetics, foods, and clothing necessitates the need for an effective system to monitor and evaluate the potential environmental impact of these nanoparticles. The goal of this research was to develop a plant-based sensor network for characterizing, monitoring, and understanding the environmental impact of TiO2 nanoparticles. The network consisted of potted Arabidopsis thaliana with a surrounding water supply, which was monitored by cameras attached to a laptop computer running a machine learning algorithm. Using the proposed plant sensor network, we were able to examine the toxicity of TiO2 nanoparticles in two systems: algae and terrestrial plants. Increased terrestrial plant growth was observed upon introduction of the nanoparticles, whereas algal growth decreased significantly. The proposed system can be further automated for high-throughput screening of nanoparticle toxicity in the environment at multiple trophic levels. The proposed plant-based sensor network could be used for more accurate characterization of the environmental impact of nanomaterials. PMID:28458617

Template-Directed Fabrication of Anatase TiO2 Hollow Nanoparticles and Their Application in Photocatalytic Degradation of Methyl Orange

Institute of Scientific and Technical Information of China (English)

Jie Chang; Wenjian Zhang; Chunyan Hong

2017-01-01

Polymerization-induced self-assembly (PISA) was used to fabricate polymeric nanoparticles via reversible addition-fragmentation chain transfer (RAFT) dispersion polymerization of benzyl methacrylate (BzMA) using diblock copolymer poly(glycerol monomethacrylate)-block-poly(2-dimethylaminoethyl methacrylate) (PGMMA-PDMAEMA-CTA) as the macro RAFT agent.The dispersion of polymeric nanoparticles with a final concentration of about 210 mg/g (solid content of 21％) was obtained via this efficient method (PISA).The resultant polymeric nanoparticles consisting of corona-shell-core three layers with weak polyelectrolyte PDMAEMA as the shell were used as sacrificial template to fabricate TiO2 hollow nanoparticles.The negatively charged titanium precursor was absorbed into the PDMAEMA shell via the electrostatic interaction,and hydrolyzed to form polymer/TiO2 hybrid nanoparticles.Anatase TiO2 hollow nanoparticles were formed after removing the polymeric templates by calcination at 550 ℃.The experiments of photocatalytic degradation of methyl orange showed that the resultant anatase TiO2 hollow nanoparticles had high photocatalytic activity and good reusability.

Structure of electron collection electrode in dye-sensitized nanocrystalline TiO2

International Nuclear Information System (INIS)

Yanagida, Masatoshi; Numata, Youhei; Yoshimatsu, Keiichi; Ochiai, Masayuki; Naito, Hiroyoshi; Han, Liyuan

2013-01-01

As part of the effort to control electron transport in the TiO 2 films of dye-sensitized solar cells (DSCs), the structure of the electron collection electrode on the films has been investigated. Here, we report the comparison between a sandwich-type dye-sensitized solar cell (SW-DSC), in which the TiO 2 film is sandwiched between a TCO glass front electron collection electrode and a sputtered Ti back charge collection electrode, and a normal DSC (N-DSC), which has no back electrode. In N-DSCs, electrons in TiO 2 that are far from the front electrode have to diffuse for a long distance (ca. 10 μm), and therefore, the photocurrent cannot rapidly respond to light with a modulation frequency >100 Hz. In SW-DSCs, the photocurrent response was enhanced at frequencies between 10 and 500 Hz because electrons in TiO 2 can be extracted by both front and back electrodes, which can be also explained by an electron diffusion model. Calculations based on the electron diffusion model suggested that a high short-circuit photocurrent could be maintained in SW-DSCs even when the electron diffusion length in the TiO 2 film was shortened.

Cisplatin Loaded Hyaluronic Acid Modified TiO2 Nanoparticles for Neoadjuvant Chemotherapy of Ovarian Cancer

Directory of Open Access Journals (Sweden)

Enling Liu

2015-01-01

Full Text Available Novel tumor-targeting titanium dioxide (TiO2 nanoparticles modified with hyaluronic acid (HA were developed to explore the feasibility of exploiting the pH-responsive drug release property of TiO2 and the tumor-targeting ability of HA to construct a tumor-targeting cisplatin (CDDP delivery system (HA-TiO2 for potential neoadjuvant chemotherapy of ovarian cancer. The experimental results indicated that CDDP release from the HA-TiO2 nanoparticles was significantly accelerated by decreasing pH from 7.4 to 5.0, which is of particular benefit to cancer therapy. CDDP-loaded HA-TiO2 nanoparticles increased the accumulation of CDDP in A2780 ovarian cancer cells via HA-mediated endocytosis and exhibited superior anticancer activity in vitro. In vivo real-time imaging assay revealed that HA-TiO2 nanoparticles possessed preferable tumor-targeting ability which might potentially minimize the toxic side effects of CDDP in clinical application.

Effect of TiO2 nanoparticles on UASB biomass activity and dewatered sludge.

Science.gov (United States)

Yadav, Tushar; Mungray, Alka A; Mungray, Arvind K

2017-02-01

The accumulation of the nanowastes in the wastewater treatment plants has raised several concerns; therefore, it is an utmost priority to study the nanoparticle (NP) toxicity in such systems. In this work, the effect of TiO 2 NPs on up-flow anaerobic sludge blanket (UASB) microflora and their photocatalytic effect on dewatered sludge were studied. We observed 99.98% removal of TiO 2 NPs by sludge biomass within 24 h, though negligible toxicity was found up to 100 mg/L TiO 2 concentration on extracellular polymeric substances (EPS), volatile fatty acid and biogas generation. The low toxicity corresponds to the agglomeration of TiO 2 NPs in UASB sludge. Alterations in dewatered sludge biochemical composition and increase in cell damage were observed upon exposure to sunlight as evidenced by FTIR and fluorescent microscopy, respectively. Results suggest the negligible toxicity of TiO 2 NPs on UASB biomass activity; however, once exposed to open environment and sunlight, they may exert detrimental effects.

TiO2/Bi2(BDC)3/BiOCl nanoparticles decorated ultrathin nanosheets with excellent photocatalytic reaction activity and selectivity

International Nuclear Information System (INIS)

Zhou, Shu-Mei; Ma, De-Kun; Cai, Ping; Chen, Wei; Huang, Shao-Ming

2014-01-01

Graphical abstract: TiO 2 /Bi 2 (BDC) 3 /BiOCl nanoparticles decorated ultrathin nanosheets showed excellent photocatalytic reaction activity and selectivity. - Highlights: • TiO 2 /Bi 2 (BDC) 3 /BiOCl nanoparticles decorated ultrathin nanosheets were synthesized through a facile hydrothermal process. • The products showed excellent photocatalytic activities for the degradation of various dyes. • The photocatalytic activities of the composite materials could be easily adjusted through tuning the content of TiO 2 . • TiO 2 /Bi 2 (BDC) 3 /BiOCl displayed obvious photocatalytic selectivity in mixed dyes systems of rhodamine B and eosin Y. - Abstract: Photocatalysts with excellent photocatalytic reaction activity and ideal selectivity are highly desirable for pollutants clearance and purification of targeted organics from a mixture. Continued efforts toward the goal, we here present a facile hydrothermal route to synthesize TiO 2 /Bi-benzenedicarboxylate/BiOCl nanoparticles decorated ultrathin nanosheets with a thickness less than 5 nm on a large scale. The as-synthesized products showed excellent photocatalytic activities for the degradation of various dyes such as rhodamine B, eosin Y and methylene blue in aqueous solution under visible light irradiation. The photocatalytic activities of TiO 2 /Bi-benzenedicarboxylate/BiOCl nanocomposites for the degradation of rhodamine B and eosin Y could be adjusted through tuning the content of TiO 2 . With increasing the amount of TiO 2 , the composites showed declining photocatalytic activities in decomposing of rhodamine B while on the contrary they displayed enhanced photocatalytic activities in decomposing of eosin Y. Interestingly, TiO 2 /Bi-benzenedicarboxylate/BiOCl composite nanosheets showed obvious photocatalytic selectivity in a mixed dyes system. The photocatalytic reaction and selectivity mechanisms of the nanocomposites for the degradation of the dyes were discussed on the basis of experimental results. The

Highly efficient enrichment of phosphopeptides from HeLa cells using hollow magnetic macro/mesoporous TiO2 nanoparticles.

Science.gov (United States)

Hong, Yayun; Zhan, Qiliang; Pu, Chenlu; Sheng, Qianying; Zhao, Hongli; Lan, Minbo

2018-09-01

In this work, hollow magnetic macro/mesoporous TiO 2 nanoparticles (denoted as Fe 3 O 4 @H-fTiO 2 ) were synthesized by a facile "hydrothermal etching assisted crystallization" route to improve the phosphopeptide enrichment efficiency. The porous nanostructure of TiO 2 shell and large hollow space endowed the Fe 3 O 4 @H-fTiO 2 with a high surface area (144.71 m 2 g -1 ) and a large pore volume (0.52 cm 3 g -1 ), which could provide more affinity sites for phosphopeptide enrichment. Besides, the large pore size of TiO 2 nanosheets and large hollow space could effectively prevent the "shadow effect", thereby facilitating the diffusion and release of phosphopeptides. Compared with the hollow magnetic mesoporous TiO 2 with small and deep pores (denoted as Fe 3 O 4 @H-mTiO 2 ) and solid magnetic macro/mesoporous TiO 2 , the Fe 3 O 4 @H-fTiO 2 nanoparticles showed a better selectivity (molar ratio of α-casein/BSA up to 1:10000) and a higher sensitivity (0.2 fmol/μL α-casein) for phosphopeptide enrichment. Furthermore, 1485 unique phosphopeptides derived from 660 phosphoproteins were identified from HeLa cell extracts after enrichment with Fe 3 O 4 @H-fTiO 2 nanoparticles, further demonstrating that the Fe 3 O 4 @H-fTiO 2 nanoparticles had a high-efficiency performance for phosphopeptide enrichment. Taken together, the Fe 3 O 4 @H-fTiO 2 nanoparticles will have unique advantages in phosphoproteomics analysis. Copyright © 2018 Elsevier B.V. All rights reserved.

TiO2 nanoparticles as exogenous contrast agent for 1 µm swept source optical coherence tomography: an in vitro study

Science.gov (United States)

Kumar, Atul; Mondal, Indranil; Roy, Poulomi; Poddar, Raju

2018-03-01

Optical coherence tomography (OCT) is a rapidly evolving, robust technology that has profoundly changed the practice of medical imaging. Swept source OCT (SSOCT) combines the standard time domain and the spatially encoded frequency domain OCT. We have employed a high-speed SSOCT system that utilizes a swept source laser with an A-scan rate of 100 kHz and a central wavelength of 1060 nm for the imaging of the tissue. SSOCT at 1060 nm allows for high penetration in the tissue. TiO2 nanoparticles (NPs) are mostly used for various experimental purposes as an exogenous imaging contrast agent. The in vitro imaging of chicken breast tissue is performed with and without the application of TiO2 NPs for exogenous contrast. Characterization of the chemically synthesized TiO2 NPs was done with dynamic light scattering and a scanning electron microscope method. The effect of TiO2 is studied at different exposure times. A significant improvement in the contrast to noise ratio has been observed through the in vitro imaging of a TiO2 treated tissue.

Conductometric sensor for ammonia and ethanol using gold nanoparticle-doped mesoporous TiO2

International Nuclear Information System (INIS)

Xiong, Wei; Liu, Huanhuan; Liu, Shantang

2015-01-01

We describe uniform and high-temperature-stable mesoporous TiO 2 beads functionalized with gold nanoparticles (AuNPs-TiO 2 ) for use in conductometric sensing of gases and organic vapors. The size of the interconnected main mesopores of the TiO 2 beads ranges from 8 to 15 nm, and the AuNPs have diameters between 8 and 10 nm. The mesoporous TiO 2 beads are formed during calcination while the structure-directing template agent is removed. Monodispersed AuNPs are formed by reduction in-situ and are placed inside the mesoporous TiO 2 framework. This prevents aggregation of the AuNPs even at 500 °C. The materials were characterized by UV–vis spectroscopy, scanning and transmission electron microscopy, nitrogen adsorption-desorption, and X-ray diffraction. Comb-type gold electrodes were then fabricated on an alumina substrate and are shown to display excellent properties in terms of sensing ammonia, ethanol, methanol or acetone. The sensitivity (defined as the ratio of resistivities under vapor and air) of a typical AuNPs(0.5 %)-TiO 2 gas sensor for ethanol reached up to 5.65 at above 600 ppm at 75 °C. Response time and recovery times (t 90  ≤ 20 s) are faster than (or comparable to) other metal-doped TiO 2 sensors, and working temperatures are much lower. An interesting observation was made in that the changes in the conductivity of the sensor change with temperature. The sensor prepared with AuNPs(0.5 %)-TiO 2 is of the p-type (in its response to ammonia gas) at 45 °C, but becomes n-type at 20 °C. Obviously, rather slight changes in temperature lead to a complete change in the direction of the conductometric signal change. This may provide a new aspect in terms of selective and highly sensitive detection of ammonia at ambient and slightly elevated temperatures. (author)

Kinetic Monte Carlo Study of Ambipolar Lithium Ion and Electron-Polaron Diffusion into Nanostructured TiO2

International Nuclear Information System (INIS)

Yu, Jianguo; Sushko, Maria L.; Kerisit, Sebastien N.; Rosso, Kevin M.; Liu, Jun

2012-01-01

Nanostructured titania (TiO2) polymorphs have proved to be promising electrode materials for next generation lithium-ion batteries. However, there is still a lack of understanding of the fundamental microscopic processes that control charge transport in these materials. Here we present microscopic simulations of the collective dynamics of lithium-ion (Li+) and charge compensating electron polarons (e-) in rutile TiO2 nanoparticles in contact with idealized conductive matrix and electrolyte. Kinetic Monte Carlo simulations are used, parameterized by molecular dynamics-based predictions of activation energy barriers for Li+ and e- diffusion. Simulations reveal the central role of electrostatic coupling between Li+ and e- on their collective drift diffusion at the nanoscale. They also demonstrate that high contact area between conductive matrix and rutile nanoparticles leads to undesirable coupling-induced surface saturation effects during Li+ insertion, which limits the overall capacity and conductivity of the material. These results help provide guidelines for design of nanostructured electrode materials with improved electrochemical performance.

Effect of TiO2 nanoparticles on the reproduction of silkworm.

Science.gov (United States)

Ni, Min; Li, Fanchi; Wang, Binbin; Xu, Kaizun; Zhang, Hua; Hu, Jingsheng; Tian, Jianghai; Shen, Weide; Li, Bing

2015-03-01

Silkworm (Bombyx mori) is an important economic insect and the model insect of Lepidoptera. Because of its high fecundity and short reproduction cycle, it has been widely used in reproduction and development research. The high concentrations of titanium dioxide nanoparticles (TiO2 NPs) show reproductive toxicity, while low concentrations of TiO2 NPs have been used as feed additive and demonstrated significant biological activities. However, whether the low concentrations of TiO2 NPs affect the reproduction of B. mori has not been reported. In this study, the growth and development of gonad of B. mori fed with a low concentration of TiO2 NPs (5 mg/L) were investigated by assessing egg production and expression of reproduction-related genes. The results showed that the low concentration of TiO2 NPs resulted in faster development of the ovaries and testes and more gamete differentiation and formation, with an average increase of 51 eggs per insect and 0.34 × 10(-4) g per egg after the feeding. The expressions of several reproduction-related genes were upregulated, such as the yolk-development-related genes Ovo-781 and vitellogenin (Vg) were increased by 5.33- and 6.77-folds, respectively. This study shows that TiO2 NPs feeding at low concentration can enhance the reproduction of B. mori, and these results are useful in developing new methods to improve fecundity in B. mori and providing new clues for its broad biological applications.

Amorphous TiO2 Shells: A Vital Elastic Buffering Layer on Silicon Nanoparticles for High-Performance and Safe Lithium Storage.

Science.gov (United States)

Yang, Jianping; Wang, Yunxiao; Li, Wei; Wang, Lianjun; Fan, Yuchi; Jiang, Wan; Luo, Wei; Wang, Yang; Kong, Biao; Selomulya, Cordelia; Liu, Hua Kun; Dou, Shi Xue; Zhao, Dongyuan

2017-12-01

Smart surface coatings of silicon (Si) nanoparticles are shown to be good examples for dramatically improving the cyclability of lithium-ion batteries. Most coating materials, however, face significant challenges, including a low initial Coulombic efficiency, tedious processing, and safety assessment. In this study, a facile sol-gel strategy is demonstrated to synthesize commercial Si nanoparticles encapsulated by amorphous titanium oxide (TiO 2 ), with core-shell structures, which show greatly superior electrochemical performance and high-safety lithium storage. The amorphous TiO 2 shell (≈3 nm) shows elastic behavior during lithium discharging and charging processes, maintaining high structural integrity. Interestingly, it is found that the amorphous TiO 2 shells offer superior buffering properties compared to crystalline TiO 2 layers for unprecedented cycling stability. Moreover, accelerating rate calorimetry testing reveals that the TiO 2 -encapsulated Si nanoparticles are safer than conventional carbon-coated Si-based anodes. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

An insight into the mechanism of charge transfer properties of hybrid organic (MEH-PPV): Inorganic (TiO2) nanocomposites

International Nuclear Information System (INIS)

Mittal, Tanu; Tiwari, Sangeeta; Mehta, Aarti; Sharma, Shailesh N.

2016-01-01

Now a days, inorganic nanoparticles are gaining importance and are potential candidate in different organic electronic device application like (LEDs, PVs) due to their novel properties and confinement in Nano-dimensions. [1, 2] In the present work, we have compared the properties of titanium di oxide (TiO 2 ) nanoparticles (NPs) synthesized by using two different chemical routes aqueous and ethanol respectively. These synthesized TiO 2 nanoparticles have been characterized by X-ray diffraction spectroscopy (XRD) for phase confirmation. It was observed that synthesized nanoparticles are in anatase phase for both preparation routes. Morphological information was collected by scanning electron microscopy (SEM) which confirms that particles are almost spherical in shape and distributed uniformly which is further ensured by transmission electron microscopy (TEM). Dynamic light scattering (DLS) technique was also used for further confirmation of size distribution of as-synthesized nanoparticles. Optical properties were also investigated by photoluminescence and UV-Vis spectroscopy and calculated bandgap was found to be in the range of 3.3-3.5eV for TiO 2 (aq/eth) nanoparticles. The increase in bandgap values with respect to bulk (3.2 eV) confirms that as- synthesized nanoparticles are confined in nanodimensions. As synthesized nanoparticles were interacted with MEHPPV polymer (donor) matrix to make their respective MEHPPV: TiO 2 nanocomposites and to confirm the charge transfer mechanism from polymer to nanoparticles. It can be observed from photoluminescence (PL) quenching experiments that continuous quenching obtained for respective nanocomposites confirms better charge transfer from polymer to inorganic TiO 2 nanoparticles respectively. Because of, better quenching and simultaneously enhanced charge transfer of respective nanocomposites, ensures that these nanocomposites are greatly applicable for photovoltaics (PVs) especially in Hybrid Solar cells (HSCs).

TiO2 nanoparticles immobilized on carbon nanotubes for enhanced visible-light photo-induced activity

Directory of Open Access Journals (Sweden)

Ali Akbar Ashkarran

2015-04-01

Full Text Available CNT–TiO2 nanocomposites were prepared through (i simple mixing of as prepared CNTs and TiO2 nanoparticles (NPs, (ii simple mixing of as prepared CNTs and TiO2 NPs followed by heat treatment and (iii simple mixing of as prepared CNTs and TiO2 NPs followed by UV illumination. The synthesis of CNTs and TiO2 NPs were performed individually by arc discharge in water and sol–gel methods, respectively and characterized by X-ray diffraction (XRD, ultra violet and visible spectroscopy (UV–vis, Fourier transform infrared spectroscopy (FT-IR, scanning electron microscopy (SEM and transmission electron microscopy (TEM. The visible-light photocatalytic performance of CNT–TiO2 nanocomposites was successfully demonstrated for the degradation of Rhodamine B (Rh. B as a model dye at room temperature. It is found that CNT–TiO2 nanocomposites extended the light absorption spectrum toward the visible region and considerably improved the photocatalytic efficiency under visible-light irradiation. The visible-light photocatalytic activities of CNT–TiO2 nanocomposites in which CNTs are produced by arc discharge in deionized (DI water at 40, 60 and 80 A arc currents and combined through three different protocols are also investigated. It was found that samples prepared at 80 A arc current and 5 s arc duration followed by UV illumination revealed best photocatalytic activity compared with the same samples prepared under simple mixing and simple mixing followed by heat treatment. The enhancement in the photocatalytic property of CNT–TiO2 nanocomposites prepared at 80 A arc current followed by UV illumination may be ascribed to the quality of CNTs produced at this current, as was reported before.

Genotoxic and cytotoxic activity of green synthesized TiO2 nanoparticles

Science.gov (United States)

Koca, Fatih Doğan; Duman, Fatih

2018-03-01

Nowadays, nanomaterials that are smaller than 100 nm in size are very attractive owing to their enhanced physicochemical properties. Although they have been used widely for industrial applications, their toxicity still remains a problem. This article is a new record of the synthesis of titanium dioxide nanoparticles (TiO2 NPs) by a Mentha aquatica leaf extract and determination of its toxicity to rat marrow mesenchymal stem cells. In this study, we aimed to determine the genotoxic and cytotoxic effects of biologically synthetized TiO2 NPs. The characteristic peak of the nanomaterial was observed at 354 nm. The mean size of the nanomaterial was measured to be 69 nm from SEM images. According to zeta analysis, the surface charge of the nanomaterial was - 37.6 mV. The crystalline structure of the nanomaterial was determined using XRD analysis. It was concluded that the obtained nanomaterial was TiO2 The results of the FT-IR analysis showed that the functional groups that were found in the plant extract could play an important role in the formation and stabilization of TiO2 NPs. The effective size of the TiO2 NPs was found to be 304 nm using DLS analysis. The TGA analysis results showed that the total mass loss was 4% at 900 °C. According to DNA cleavage analysis results, TiO2 NPs cause damage to the plasmid pBR322 DNA in a concentration-dependant matter. It has been noted that TiO2 NPs lead to decreased cell viability during increased time and concentration of applications on rat marrow mesenchymal stem cells. It has also been determined that bulk TiO2 causes a greater reduction in the stem cell viability compared to the biosynthesized NPs. The obtained results could be useful for further application and toxicity studies.

Effective Removal of Congo Red by Triarrhena Biochar Loading with TiO2 Nanoparticles

Directory of Open Access Journals (Sweden)

Peng Yu

2018-01-01

Full Text Available A composite of pyrolytic Triarrhena biochar loading with TiO2 nanoparticles has been synthesized by the sol-gel method. The composite shows a well-developed hollow mesoporous and macropore structure as characterized by XRD, BET, and SEM. When used as an absorbent to remove Congo red from aqueous solution, it was found that as-prepared composite performed better absorption capacity than single biochar or TiO2. The results suggest that biochar loading with TiO2 could be promisingly implemented as an environmentally friendly and inexpensive adsorbent for Congo red removal from wastewater.

Synthesis of mesoporous TiO2 in aqueous alcoholic medium and evaluation of its photocatalytic activity

International Nuclear Information System (INIS)

Kumaresan, L.; Prabhu, A.; Palanichamy, M.; Murugesan, V.

2011-01-01

Research highlights: → Mesoporous TiO 2 synthesized using P123 as soft template in sol-gel method. → Nanoparticle aggregates are better for photocatalytic activity than free nanoparticles. → Particle to particle transport of electrons in the conduction band of aggregates are important factor. - Abstract: Mesoporous TiO 2 was synthesized using triblock copolymer as the structure directing template in ethanol/water, isopropanol/water or 1-butanol/water medium by sol-gel method. The presence of intense peak at low angle in the XRD patterns confirmed the orderly arrangement of mesopores in the material. Among the three different alcohols, ethanol had influenced better in controlling the particle size than others. The enhanced specific surface area also revealed the formation of mesopores. Aggregates of particles were clearly seen in the TEM images and the size of the particles was approximately 10 nm. The photocatalytic activity of mesoporous TiO 2 was evaluated using aqueous alachlor as a model pollutant. The activity of mesoporous TiO 2 synthesized in ethanol/water mole ratio of 50 was higher than other mesoporous TiO 2 and commercial TiO 2 (Degussa P-25). The transport of excited electrons from one particle to its neighboring nanoparticles of mesoporous TiO 2 is suggested to be the cause for enhanced photocatalytic activity.

Uniform thin films of TiO2 nanoparticles deposited by matrix-assisted pulsed laser evaporation

International Nuclear Information System (INIS)

Caricato, A.P.; Manera, M.G.; Martino, M.; Rella, R.; Romano, F.; Spadavecchia, J.; Tunno, T.; Valerini, D.

2007-01-01

We report morphological and optical properties of a colloidal TiO 2 nanoparticle film, deposited on a quartz substrate by using the Matrix-Assisted Pulsed Laser Evaporation (MAPLE) technique. Atomic Force Microscopy demonstrated that a good uniformity of the deposition can be obtained. The presence of agglomerates with dimensions of about 1 μm in size was noticed. Form UV-vis transmission spectra, recorded in the 200-800 nm range, the optical constants and the energy gap were determined besides the film thickness. The optical constants resulted in agreement with the values reported in literature for TiO 2 nanoparticle thin films

Photocatalytic degradation of malathion using Zn2+-doped TiO2 nanoparticles: statistical analysis and optimization of operating parameters

Science.gov (United States)

Nasseri, Simin; Omidvar Borna, Mohammad; Esrafili, Ali; Rezaei Kalantary, Roshanak; Kakavandi, Babak; Sillanpää, Mika; Asadi, Anvar

2018-02-01

A Zn2+-doped TiO2 is successfully synthesized by a facile photodeposition method and used in the catalytic photo-degradation of organophosphorus pesticide, malathion. The obtained photocatalysts are characterized in detail by X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET), Field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). XRD results confirm the formation of the anatase and rutile phases for the Zn2+-doped TiO2 nanoparticles, with crystallite sizes of 12.9 nm. Zn2+-doped TiO2 that was synthesized by 3.0%wt Zn doping at 200 °C exhibited the best photocatalytic activity. 60 sets of experiments were conducted using response surface methodology (RSM) by adjusting five operating parameters, i.e. initial malathion concentration, catalyst dose, pH, reaction time at five levels and presence or absence of UV light. The analysis revealed that all considered parameters are significant in the degradation process in their linear terms. The optimum values of the variables were found to be 177.59 mg/L, 0.99 g/L, 10.99 and 81.04 min for initial malathion concentration, catalyst dose, pH and reaction time, respectively, under UV irradiation (UV ON). Under the optimized conditions, the experimental values of degradation and mineralization were 98 and 74%, respectively. Moreover, the effects of competing anions and H2O2 on photocatalyst process were also investigated.

Gd (III) chelates adsorbed on TiO2 nanoparticles - promising MRI contrast agent

International Nuclear Information System (INIS)

Rehor, Ivan; Lukes, Ivan; Peters, Joop A.; Jirak, Daniel

2009-01-01

Full text: The project deals with a new contrast agent (CA) for magnetic resonance imaging (MRI). The CA consists of two main parts - diamagnetic core (TiO 2 nanoparticle) and Gd (III) chelates grafted on its surface. The presence of the nanoparticle core is responsible for significant increase of r1 millimolar relaxivity (which corresponds to the efficiency of the CA) due to the slowing down the rotation of the complex in solution. It also affects the biodistribution characteristics of the CA - the ability to penetrate through cell membranes is well known for nanoparticles, making them useful for cell labeling. The structure of the chelate is derived from DOTA ligand, whose Gd (III) complexes are commercially used as MRI CA in human medicine. The connection of the complex to the surface is realized via penylphosphonate, which is attached to the pendant arm of the ligand. Strong interaction of the phosphonate with the TiO 2 surface results in the full surface coverage. The complexation and MRI properties of Gd chelate were studied and exhibit analogy to the complexes of DOTA, The millimolar relaxivity (r1) of the Gd (III) complex significantly increases upon adsorption on the TiO 2 nanoparticles. PVA was added to the colloidal solutions of CA to stabilize them under biological conditions and such stabilized CA was utilized for MRI visualization of rat pancreatic islets (P1). The labeled islets were detected on MR images as hyperintense area and therefore our CA seems to be promising material for cellular MRI

Three-dimensional TiO2/Au nanoparticles for plasmon enhanced photocatalysis

Science.gov (United States)

Yu, Jianyu; Zhou, Lin; Wang, Yang; Tan, Yingling; Wang, Zhenlin; Zhu, Shining; Zhu, Jia

2018-03-01

The mechanisms of plasmonic nanostructures assisted photocatalytic processes are fundamental and of great importance and interest for decades. Therefore, we adopt a unique porous structure of three-dimensional TiO2/Au nanoparticles to experimentally explore the potential mechanisms of rhodamine B (RhB) based photocatalytic degradation. The highly efficient absorbance measured across the entire ultraviolet and infrared regions shows the broadband light harvesting capability and photocatalytic activity, in which the direct bandgap transition, plasmon sensitization as well as the plasmonic photothermal effect can be beneficial for the photocatalytic reaction. The RhB photocatalytic degradation experiments were conducted systematically under solar irradiance with finely chosen optical filters. Apart from the ultraviolet-driven degradation of TiO2, the plasmon assisted photocatalytic rate of our TiO2/Au structure can be enhanced by >30% as compared to the referenced TiO2 structure (equivalent to 2-4 times promotion with respect to the same quantity of the active material TiO2). Detailed wavelength-dependent analyses have revealed that the visible-driven degradation rate can be enhanced by 10 times because of the plasmon sensitization effect; while infrared-driven degradation rate is enhanced by 4 times as well for the plasmonic photothermal effect, respectively. Our experimental results may provide a clear understanding for the wavelength-dependent plasmon enhanced photocatalytic processes.

Photocatalytic decolorization of basic dye by TiO2 nanoparticle in photoreactor

Directory of Open Access Journals (Sweden)

Jutaporn Chanathaworn1

2012-04-01

Full Text Available Photocatalytic decolorization of rhodamine B (RB and malachite green (MG basic dyes in aqueous solution wasevaluated using TiO2 powder as a semiconductor photocatalyst under UV black light irradiation. A 0.5 L batch photoreactorcontaining dyeing solution was installed in a stainless steel chamber with air cooling under irradiation. The TiO2 powder wascharacterized by XRD observation and it was shown that the nanoparticles could be identified as 73 nm anatase crystals. Theeffects of operational parameters such as light intensity (0-114 W/m2, initial dye concentration (10-30 mg/L, and TiO2 powderloading (0.5-1.5 g/L on the decolorization of dye samples were examined. The photocatalytic decolorization rate depended onthe pollutant’s structure, such that the MG dye could be removed faster than the RB dye. Decolorization efficiency (% of thephotocatalytic system increased with increasing TiO2 loading and light intensity; however, it decreased with increasing initialdye concentration. A loading of 1.5 g TiO2/L, initial dye concentration of 20 mg/L, and light intensity of 114 W/m2 were foundto yield the highest removal efficiency of dye solution based on time requirement. The kinetics are of first order and dependon the TiO2 powder loading and dye structure. The research had a perfect application foreground.

MoS2 embedded TiO2 nanoparticles for concurrent role of adsorption and photocatalysis

Science.gov (United States)

Pal, Arnab; Jana, Tushar K.; Chatterjee, Kuntal

2018-04-01

In this work, MoS2 embedded TiO2 nanoparticles, synthesized through hydrothermal process, was successfully employed to remove organic pollutant dye like methylene blue(MB) through adsorption and as well as through photocatalysis under visible light irradiation. The system was characterized by structural and morphological study. The adsorption and photocatalytic study of MB were evaluated with different concentrations of dye in aqueous solution. This work brings the MoS2-TiO2 nanostructure as excellent adsorbent as well as efficient photocatalyst materials which can be used for organic dye removal towards waste-water treatment.

Protein Corona Prevents TiO2 Phototoxicity.

Directory of Open Access Journals (Sweden)

Maja Garvas

Full Text Available TiO2 nanoparticles have generally low toxicity in the in vitro systems although some toxicity is expected to originate in the TiO2-associated photo-generated radical production, which can however be modulated by the radical trapping ability of the serum proteins. To explore the role of serum proteins in the phototoxicity of the TiO2 nanoparticles we measure viability of the exposed cells depending on the nanoparticle and serum protein concentrations.Fluorescence and spin trapping EPR spectroscopy reveal that the ratio between the nanoparticle and protein concentrations determines the amount of the nanoparticles' surface which is not covered by the serum proteins and is proportional to the amount of photo-induced radicals. Phototoxicity thus becomes substantial only at the protein concentration being too low to completely coat the nanotubes' surface.These results imply that TiO2 nanoparticles should be applied with ligands such as proteins when phototoxic effects are not desired - for example in cosmetics industry. On the other hand, the nanoparticles should be used in serum free medium or any other ligand free medium, when phototoxic effects are desired - as for efficient photodynamic cancer therapy.

Improving the Osteoblast Cell Adhesion on Electron Beam Controlled TiO2 Nanotubes

Directory of Open Access Journals (Sweden)

Sung Wook Yoon

2014-01-01

Full Text Available Here we investigate the osteogenesis and synostosis processes on the surface-modified TiO2 nanotubes via electron beam irradiation. The TiO2 nanotubes studied were synthesized by anodization process under different anodizing voltage. For the anodization voltage of 15, 20, and 25 V, TiO2 nanotubes with diameters of 59, 82, and 105 nm and length of 115, 276, and 310 nm were obtained, respectively. MC3T3-E1 osteoblast cell line was incubated on the TiO2 nanotubes to monitor the change in the cell adhesion before and after the electron beam irradiation. We observe that the electron beam irradiation affects the number of surviving osteoblast cells as well as the cultivation time. In particular, the high adhesion rate of 155% was obtained when the osteoblast cells were cultivated for 2 hours on the TiO2 nanotube, anodized under 20 V, and irradiated with 5,000 kGy of electron beam.

Fast and simple microwave synthesis of TiO2/Au nanoparticles for gas-phase photocatalytic hydrogen generation

Science.gov (United States)

May-Masnou, Anna; Soler, Lluís; Torras, Miquel; Salles, Pol; Llorca, Jordi; Roig, Anna

2018-04-01

The fabrication of small anatase titanium dioxide (TiO2) nanoparticles (NPs) attached to larger anisotropic gold (Au) morphologies by a very fast and simple two-step microwave-assisted synthesis is presented. The TiO2/Au NPs are synthesized using polyvinylpyrrolidone (PVP) as reducing, capping and stabilizing agent through a polyol approach. To optimize the contact between the titania and the gold and facilitate electron transfer, the PVP is removed by calcination at mild temperatures. The nanocatalysts activity is then evaluated in the photocatalytic production of hydrogen from water/ethanol mixtures in gas-phase at ambient temperature. A maximum value of 5.3 mmol·gcat-1·h-1 (7.4 mmol·gTiO2-1·h-1) of hydrogen is recorded for the system with larger gold particles at an optimum calcination temperature of 450 °C. Herein we demonstrate that TiO2-based photocatalysts with high Au loading and large Au particle size (≈ 50 nm) NPs have photocatalytic activity.

Photovoltaic performance enhancement of CdS quantum dot-sensitized TiO2 photoanodes with plasmonic gold nanoparticles

International Nuclear Information System (INIS)

Liu, Aiping; Ren, Qinghua; Zhao, Ming; Xu, Tao; Yuan, Ming; Zhao, Tingyu; Tang, Weihua

2014-01-01

Highlights: • CdS QD-sensitized TiO 2 porous photoanode with plasmonic gold. • A prominent light absorption enhancement of hybrid was attained by gold plasmon. • The photovoltaic response of hybrid was tunable by CdS amount. • The Au/TiO 2 /CdS hybrid had a potential application in energy conversion devices. -- Abstract: The CdS quantum dot-sensitized TiO 2 films with plasmonic gold nanoparticles were designed as photoanodes by the electrodeposition of gold combined with the “successive ionic layer adsorption and reaction” (SILAR) method for CdS deposition on porous TiO 2 films. A prominent enhancement in light absorption of Au/TiO 2 /CdS hybrid was attained by efficient light scattering of gold plasmons as sub-wavelength antennas and concentrators. The photogenerated electron formed in the near-surface region of TiO 2 and CdS were facilitated to transfer to the plasmonic gold, resulting in the enhancement of photocurrent and incident photon-to-current conversion efficiency of hybrid photoanode upon photoirradiation. Furthermore, the photovoltaic response of hybrid was highly tunable with respect to the number of SILAR cycles applied to deposit CdS. The thicker absorber layer with less porous structure and larger CdS crystals might limit the electrolyte diffusion into the hybrid electrode and impose a barrier for electron tunneling and transferring. The highly versatile and tunable properties of Au/TiO 2 /CdS photoanodes demonstrated their potential application in energy conversion devices

FTIR and Raman Characterization of TiO2 Nanoparticles Coated with Polyethylene Glycol as Carrier for 2-Methoxyestradiol

Directory of Open Access Journals (Sweden)

Andrea León

2017-01-01

Full Text Available The aim of this study was to prepare a novel targeting drug delivery system for 2-Methoxyestradiol (2ME in order to improve the clinical application of this antitumor drug. It is based in nanoparticles (NPs of titanium dioxide (TiO2 coated with polyethylene glycol (PEG and loaded with 2ME. A complete IR and Raman characterization have been made to confirm the formation of TiO2–PEG–2ME composite. Vibrational modes have been assigned for TiO2, PEG, and 2ME and functionalized TiO2–PEG and TiO2–PEG–2ME. The observed variation in peak position of FTIR and Raman of each for these composites has been elucidated in terms of intermolecular interactions between PEG–2ME and TiO2, obtaining step-by-step the modification processes that were attributed to the conjugation of PEG and 2ME to TiO2 NPs. Modifying TiO2 NPs with PEG loaded with the 2ME drug revealed that the titanium dioxide nanocarrier possesses an effective adsorption capability, and we discuss their potential application as a system of drug delivery.

Modulation of physiological responses with TiO2 nano-particle in Azolla pinnata R.Br. under 2,4-D toxicity.

Science.gov (United States)

De, Arnab Kumar; Ghosh, Arijit; Debnath, Subhas Chandra; Sarkar, Bipul; Saha, Indraneel; Adak, Malay Kumar

2018-06-05

The present work is emphasised with the herbicidal tolerance of Azolla pinnata R.Br. and its modulation with TiO 2 nano-particle. Both carbohydrate and nitrogen metabolism were effected with 2,4-D as herbicide and in few cases TiO 2 -NP had recovered few detrimental effects. From the nutrient status in Azolla it recorded the recovery of nitrogen as well as potassium by TiO 2 -NP but not in case of phosphorus. However, a conversion of nitrate to ammonium was more induced by TiO 2 -NP under herbicidal toxicity. Similar results were obtained for inter-conversion of amino acid-nitrate pool, but no changes with glutamine synthase activity with TiO 2 -NP. Initially, the effects of 2,4-D was monitored with changes of chlorophyll content but had not been recovered with nanoparticle. Photosynthetic reserves expressed as both total and reducing sugar were insensitive to TiO 2 -NP interference but activity of soluble and wall bound invertase was in reverse trend as compared to control. The 2,4-D mediated changes of redox and its oxidative stress was ameliorated in plants with over expressed ADH activity. As a whole the Azolla bio system with TiO 2 supplementation may be useful in sustenance against 2,4-D toxicity through recovery of nitrogen metabolism. Thus, Azolla-TiO 2 -NP bio system would be realised to monitor the herbicidal toxicity in soil and its possible bioremediation.

Assessment of phototoxicity, skin irritation, and sensitization potential of polystyrene and TiO2 nanoparticles

Science.gov (United States)

Park, Yoon-Hee; Jeong, Sang Hoon; Yi, Sang Min; Hyeok Choi, Byeong; Kim, Yu-Ri; Kim, In-Kyoung; Kim, Meyoung-Kon; Son, Sang Wook

2011-07-01

The human skin equivalent model (HSEM) is well known as an attractive alternative model for evaluation of dermal toxicity. However, only limited data are available on the usefulness of an HSEM for nanotoxicity testing. This study was designed to investigate cutaneous toxicity of polystyrene and TiO2 nanoparticles using cultured keratinocytes, an HSEM, and an animal model. In addition, we also evaluated the skin sensitization potential of nanoparticles using a local lymph node assay with incorporation of BrdU. Findings from the present study indicate that polystyrene and TiO2 nanoparticles do not induce phototoxicity, acute cutaneous irritation, or skin sensitization. Results from evaluation of the HSEMs correspond well with those from animal models. Our findings suggest that the HSEM might be a useful alternative model for evaluation of dermal nanotoxicity.

Assessment of phototoxicity, skin irritation, and sensitization potential of polystyrene and TiO2 nanoparticles

International Nuclear Information System (INIS)

Park, Yoon-Hee; Jeong, Sang Hoon; Yi, Sang Min; Choi, Byeong Hyeok; Son, Sang Wook; Kim, Yu-Ri; Kim, In-Kyoung; Kim, Meyoung-Kon

2011-01-01

The human skin equivalent model (HSEM) is well known as an attractive alternative model for evaluation of dermal toxicity. However, only limited data are available on the usefulness of an HSEM for nanotoxicity testing. This study was designed to investigate cutaneous toxicity of polystyrene and TiO 2 nanoparticles using cultured keratinocytes, an HSEM, and an animal model. In addition, we also evaluated the skin sensitization potential of nanoparticles using a local lymph node assay with incorporation of BrdU. Findings from the present study indicate that polystyrene and TiO 2 nanoparticles do not induce phototoxicity, acute cutaneous irritation, or skin sensitization. Results from evaluation of the HSEMs correspond well with those from animal models. Our findings suggest that the HSEM might be a useful alternative model for evaluation of dermal nanotoxicity.

Enhancing lipid productivity of Chlorella vulgaris using oxidative stress by TiO2 nanoparticles

International Nuclear Information System (INIS)

Kang, Nam Kyu; Lee, Bongsoo; Choi, Gang-Guk; Moon, Myounghoon; Park, Min S.; Yang, Ji-Won; Lim, JitKang

2014-01-01

Ability to increase the lipid production in microalgae is one of the heavily sought-after ideas to improve the economic feasibility of microalgae-derived transportation fuels for commercial applications. We used the oxidative stress by TiO 2 nanoparticles, a well-known photocatalyst, to induce lipid production in microalgae. Chlorella vulgaris UTEX 265 was cultivated under various concentrations of TiO 2 ranging from 0.1 to 5 g/L under UV-A illumination. Maximum specific growth rate was affected in responding to TiO 2 concentrations. In the presence of UV-A, chlorophyll concentration was decreased at the highest concentration of TiO 2 (5 g/L TiO 2 ) by oxidative stress. The fatty acid methyl ester (FAME) composition analysis suggested that oxidative stress causes the accumulation and decomposition of lipids. The highest FAME productivity was 18.2 g/L/d under low concentrations of TiO 2 (0.1 g/L) and a short induction time (two days). The controlled condition of TiO 2 /UV-A inducing oxidative stress (0.1 g/L TiO 2 and two days induction) could be used to increase the lipid productivity of C. vulgaris UTEX 265. Our results show the possibility of modulating the lipid induction process through oxidative stress with TiO 2 /UV-A

Au Nanoparticles Decorated TiO2 Nanotube Arrays as a Recyclable Sensor for Photoenhanced Electrochemical Detection of Bisphenol A.

Science.gov (United States)

Hu, Liangsheng; Fong, Chi-Chun; Zhang, Xuming; Chan, Leo Lai; Lam, Paul K S; Chu, Paul K; Wong, Kwok-Yin; Yang, Mengsu

2016-04-19

A photorefreshable and photoenhanced electrochemical sensing platform for bisphenol A (BPA) detection based on Au nanoparticles (NPs) decorated carbon doped TiO2 nanotube arrays (TiO2/Au NTAs) is described. The TiO2/Au NTAs were prepared by quick annealing of anodized nanotubes in argon, followed by controllable electrodeposition of Au NPs. The decoration of Au NPs not only improved photoelectrochemical behavior but also enhanced electrocatalytic activities of the resulted hybrid NTAs. Meanwhile, the high photocatalytic activity of the NTAs allowed the electrode to be readily renewed without damaging the microstructures and surface states after a short UV treatment. The electrochemical detection of BPA on TiO2/Au NTAs electrode was significantly improved under UV irradiation as the electrode could provide fresh reaction surface continuously and the further increased photocurrent resulting from the improved separation efficiency of the photogenerated electron-hole pairs derived from the consumption of holes by BPA. The results showed that the refreshable TiO2/Au NTAs electrode is a promising sensor for long-term BPA monitoring with the detection limit (S/N = 3) of 6.2 nM and the sensitivity of 2.8 μA·μM(-1)·cm(-2).

Quantitative characterization of TiO2 nanoparticle release from textiles by conventional and single particle ICP-MS

Science.gov (United States)

Mackevica, Aiga; Olsson, Mikael Emil; Hansen, Steffen Foss

2018-01-01

TiO2 is ubiquitously present in a wide range of everyday items, both as an intentionally incorporated additive and naturally occurring constituent. It can be found in a wide range of consumer products, including personal care products, food contact materials, and textiles. Normal use of these products may lead to consumer and/or environmental exposure to TiO2, possibly in form of nanoparticles. The aim of this study is to perform a leaching test and apply state-of-the-art methods to investigate nano-TiO2 and total Ti release from five types of commercially available conventional textiles: table placemats, wet wipes, microfiber cloths, and two types of baby bodysuits, with Ti contents ranging from 2.63 to 1448 μg/g. Released particle analysis was performed using conventional and single particle inductively coupled plasma mass spectrometry (ICP-MS and spICP-MS), in conjunction with transmission electron microscopy (TEM), to measure total and particulate TiO2 release by mass and particle number, as well as size distribution. Less than 1% of the initial Ti content was released over 24 h of leaching, with the highest releases reaching 3.13 μg/g. The fraction of nano-TiO2 released varied among fabric types and represented 0-80% of total TiO2 release. Particle mode sizes were 50-75 nm, and TEM imaging revealed particles in sizes of 80-200 nm. This study highlights the importance of using a multi-method approach to obtain quantitative release data that is able to provide an indication regarding particle number, size distribution, and mass concentration, all of which can help in understanding the fate and exposure of nanoparticles.

Creeping flashover characteristics improvement of nanofluid/pressboard system with TiO2 nanoparticles

Science.gov (United States)

Huang, Meng; Wang, Lei; Ge, Yang; Lv, Yu-zhen; Qi, Bo; Li, Cheng-rong

2018-03-01

Creeping flashover easily occurs at the interface between oil and pressboard in transformer and thus results in outage of power transmission system. Investigations have shown that creeping flashover characteristics at oil/pressboard interface can be improved by the addition of TiO2 nanoparticles, but the mechanism is still not thoroughly known. In this work, creeping flashover performance at nanofluid/pressboard interface modified by different sizes of nanoparticles were studied and the mechanism was presented as well. Nanofluids with the same concentration but with different sizes of TiO2 nanoparticles were prepared, and pressboards impregnated with them were prepared as well. After that, their creeping flashover characteristics were measured and compared. Nanoparticle's size affected the creeping flashover performance along oil/pressboard greatly under both AC and lightning impulse voltages. The highest creeping flashover voltage can be enhanced by as high as 12.2% and 32.0% respectively. The underlying electric field distribution and charge transportation behaviors were analyzed to demonstrate the influence of nanoparticle's size. By the addition of nanoparticles with a smaller size, the dielectric constant of nanofluid was increased closer to that of the pressboard, thus they were matched better. Moreover, charge was easier to dissipate from the oil/pressboard interface and electric field distortion at the interface was consequently reduced. Therefore, the electric field was more like a uniform field and the forward development of flashover was more difficult, leading to a better performance of creeping flashover of oil-impregnated pressboard.

A facile method to synthesize nitrogen and fluorine co-doped TiO2 nanoparticles by pyrolysis of (NH4)2TiF6

International Nuclear Information System (INIS)

Chen Daimei; Jiang Zhongyi; Geng Jiaqing; Zhu Juhong; Yang Dong

2009-01-01

The nitrogen and fluorine co-doped TiO 2 (N-F-TiO 2 ) nanoparticles of anatase crystalline structure were prepared by a facile method of (NH 4 ) 2 TiF 6 pyrolysis, and characterized by thermogravimetry-differential thermal analysis (TG-DTA), X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and ultraviolet visible (UV-Vis) spectroscopy etc. With the increase of calcination temperature, (NH 4 ) 2 TiF 6 decomposed into TiOF 2 and NH 4 TiOF 3 at first, and then formed anatase-type TiO 2 with thin sheet morphology. H 3 BO 3 as oxygen source can promote the formation of anatase TiO 2 , but decrease the F content in the N-F-TiO 2 materials due to the formation of volatile BF 3 during the precursor decomposition. The photocatalytic activity of the obtained N-F-TiO 2 samples was evaluated by the methylene blue degradation under visible light, and all the samples exhibited much higher photocatalytic activity than P25. Moreover, the merits and disadvantages of this proposed method to prepare doped TiO 2 are discussed.

TiO2 Deposition on AZ31 Magnesium Alloy Using Plasma Electrolytic Oxidation

Directory of Open Access Journals (Sweden)

Leon White

2013-01-01

Full Text Available Plasma electrolytic oxidation (PEO has been used in the past as a useful surface treatment technique to improve the anticorrosion properties of Mg alloys by forming protective layer. Coatings were prepared on AZ31 magnesium alloy in phosphate electrolyte with the addition of TiO2 nanoparticles using plasma electrolytic oxidation (PEO. This present work focuses on developing a TiO2 functional coating to create a novel electrophotocatalyst while observing the surface morphology, structure, composition, and corrosion resistance of the PEO coating. Microstructural characterization of the coating was investigated by X-ray diffraction (XRD and scanning electron microscopy (SEM followed by image analysis and energy dispersive spectroscopy (EDX. The corrosion resistance of the PEO treated samples was evaluated with electrochemical impedance spectroscopy (EIS and DC polarization tests in 3.5 wt.% NaCl. The XRD pattern shows that the components of the oxide film include Mg from the substrate as well as MgO and Mg2TiO4 due to the TiO2 nanoparticle addition. The results show that the PEO coating with TiO2 nanoparticles did improve the corrosion resistance when compared to the AZ31 substrate alloy.

TiO2 nanoparticle biosynthesis and its physiological effect on mung bean (Vigna radiata L.

Directory of Open Access Journals (Sweden)

Ramesh Raliya

2015-03-01

Full Text Available TiO2 nanoparticle (NPs biosynthesis is a low cost, ecofriendly approach developed using the fungi Aspergillus flavus TFR 7. To determine whether TiO2 NPs is suitable for nutrient, we conducted a two part study; biosynthesis of TiO2 NP and evaluates their influence on mung bean. The characterized TiO2 NPs were foliar sprayed at 10 mgL−1 concentration on the leaves of 14 days old mung bean plants. A significant improvement was observed in shoot length (17.02%, root length (49.6%, root area (43%, root nodule (67.5%, chlorophyll content (46.4% and total soluble leaf protein (94% as a result of TiO2 NPs application. In the rhizosphere microbial population increased by 21.4–48.1% and activity of acid phosphatase (67.3%, alkaline phosphatase (72%, phytase (64% and dehydrogenase (108.7% enzyme was observed over control in six weeks old plants owing to application of TiO2 NPs. A possible mechanism has also been hypothesized for TiO2 NPs biosynthesis.

Volume versus surface-mediated recombination in anatase TiO2 nanoparticles

Science.gov (United States)

Cavigli, Lucia; Bogani, Franco; Vinattieri, Anna; Faso, Valentina; Baldi, Giovanni

2009-09-01

We present an experimental study of the radiative recombination dynamics in size-controlled anatase TiO2 nanoparticles in the range 20-130 nm. From time-integrated photoluminescence spectra and picosecond time-resolved experiments as a function of the nanoparticle size, excitation density, and temperature, we show that photoluminescence comes out from a bulk and a surface radiative recombination. The spectral shift and the different time dynamics provide a clear distinction between them. Moreover, the intrinsic nature of the emission is also proven, providing a quantitative evaluation of volume and surface contributions.

Asymmetric photoelectric property of transparent TiO2 nanotube films loaded with Au nanoparticles

International Nuclear Information System (INIS)

Wang, Hui; Liang, Wei; Liu, Yiming; Zhang, Wanggang; Zhou, Diaoyu; Wen, Jing

2016-01-01

Highlights: • Highly transparent films of TiO 2 nanotube arrays were directly fabricated on FTO glasses. • Semitransparent TNT-Au composite films were obtained and exhibited excellent photoelectrocatalytic ability. • Back-side of TNT-Au composite films was firstly irradiated and tested to compare with front-side of films. - Abstract: Semitransparent composite films of Au loaded TiO 2 nanotubes (TNT-Au) were prepared by sputtering Au nanoparticles on highly transparent TiO 2 nanotubes films, which were fabricated directly on FTO glasses by anodizing the Ti film sputtered on the FTO glasses. Compared with pure TNT films, the prepared TNT-Au films possessed excellent absorption ability and high photocurrent response and improved photocatalytic activity under visible-light irradiation. It could be concluded that Au nanoparticles played important roles in improving the photoelectrochemical performance of TNT-Au films. Moreover, in this work, both sides of TNT-Au films were researched and compared owing to theirs semitransparency. It was firstly found that the photoelectric activity of TNT-Au composite films with back-side illumination was obviously superior to front-side illumination.

Toxicological effect of TiO2 nanoparticle-induced myocarditis in mice

Science.gov (United States)

Hong, Fashui; Wang, Ling; Yu, Xiaohong; Zhou, Yingjun; Hong, Jie; Sheng, Lei

2015-08-01

Currently, impacts of exposure to TiO2 nanoparticles (NPs) on the cardiovascular system are not well understood. The aim of this study was to investigate whether TiO2 NPs induce myocarditis and its underlying molecular mechanism in the cardiac inflammation in mice. Mice were exposed to TiO2 NPs for 6 months; biochemical parameters of serum and expression of Th1-related and Th2-related cytokines in the heart were investigated. The results showed that TiO2 NP exposure resulted in cardiac lesions coupling with pulmonary inflammation; increases of aspartate aminotransferase (AST), creatine kinase (CK), C-reaction protein (CRP), lactate dehydrogenase (LDH), alpha-hydroxybutyrate dehydrogenase (HBDH), adhesion molecule-1 (ICAM-1), and monocyte chemoattractant protein-1 (MCP-1) levels; and a reduction of nitric oxide (NOx) level in the serum. These were associated with increases of nuclear factor-κB (NF-κB), tumor necrosis factor-α (TNF-α), interleukin (IL)-4, IL-6, transforming growth factor-β (TGF-β), creatine kinase, CRP, adhesion molecule-1, and monocyte chemoattractant protein-1, interferon-γ (IFN-γ), signal transducers and activators of transcription (STAT)1, STAT3, or STAT6, GATA-binding domain-3, GATA-binding domain-4, endothelin-1 expression levels, and T-box expressed in T cells expression level that is the master regulator of pro-inflammatory cytokines and transcription factors in the heart. These findings imply that TiO2 NP exposure may increase the occurrence and development of cardiovascular diseases.

Effects of TiO2 and Co3O4 Nanoparticles on Circulating Angiogenic Cells