  1. Roman sophisticated surface modification methods to manufacture silver counterfeited coins

    Science.gov (United States)

    Ingo, G. M.; Riccucci, C.; Faraldi, F.; Pascucci, M.; Messina, E.; Fierro, G.; Di Carlo, G.

    2017-11-01

    By means of the combined use of X-ray photoelectron spectroscopy (XPS), optical microscopy (OM) and scanning electron microscopy (SEM) coupled with energy dispersive X-ray spectroscopy (EDS) the surface and subsurface chemical and metallurgical features of silver counterfeited Roman Republican coins are investigated to decipher some aspects of the manufacturing methods and to evaluate the technological ability of the Roman metallurgists to produce thin silver coatings. The results demonstrate that over 2000 ago important advances in the technology of thin layer deposition on metal substrates were attained by Romans. The ancient metallurgists produced counterfeited coins by combining sophisticated micro-plating methods and tailored surface chemical modification based on the mercury-silvering process. The results reveal that Romans were able systematically to chemically and metallurgically manipulate alloys at a micro scale to produce adherent precious metal layers with a uniform thickness up to few micrometers. The results converge to reveal that the production of forgeries was aimed firstly to save expensive metals as much as possible allowing profitable large-scale production at a lower cost. The driving forces could have been a lack of precious metals, an unexpected need to circulate coins for trade and/or a combinations of social, political and economic factors that requested a change in money supply. Finally, some information on corrosion products have been achieved useful to select materials and methods for the conservation of these important witnesses of technology and economy.

  2. Surface Modification of Ceramic Membranes with Thin-film Deposition Methods for Wastewater Treatment

    KAUST Repository

    Jahangir, Daniyal

    2017-12-01

    Membrane fouling, which is caused by deposition/adsorption of foulants on the surface or within membrane pores, still remains a bottleneck that hampers the widespread application of membrane bioreactor (MBR) technology for wastewater treatment. Recently membrane surface modification has proved to be a useful method in water/wastewater treatment to improve the surface hydrophilicity of membranes to obtain higher water fluxes and to reduce fouling. In this study, membrane modification was investigated by depositing a thin film of same thickness of TiO2 on the surface of an ultrafiltration alumina membrane. Various thin-film deposition (TFD) methods were employed, i.e. electron-beam evaporation, sputter and atomic layer deposition (ALD), and a comparative study of the methods was conducted to assess fouling inhibition performance in a lab-scale anaerobic MBR (AnMBR) fed with synthetic municipal wastewater. Thorough surface characterization of all modified membranes was carried out along with clean water permeability (CWP) tests and fouling behavior by bovine serum albumin (BSA) adsorption tests. The study showed better fouling inhibition performance of all modified membranes; however the effect varied due to different surface characteristics obtained by different deposition methods. As a result, ALD-modified membrane showed a superior status in terms of surface characteristics and fouling inhibition performance in AnMBR filtration tests. Hence ALD was determined to be the best TFD method for alumina membrane surface modification for this study. ALD-modified membranes were further characterized to determine an optimum thickness of TiO2-film by applying different ALD cycles. ALD treatment significantly improved the surface hydrophilicity of the unmodified membrane. Also ALD-TiO2 modification was observed to reduce the surface roughness of original alumina membrane, which in turn enhanced the anti-fouling properties of modified membranes. Finally, a same thickness of ALD

  3. Surface modification of bioceramics

    Science.gov (United States)

    Monkawa, Akira

    Hydroxyapatite [Ca10(PO4)6(OH)2, HAp] is a major inorganic component of bone and teeth tissues and has the excellent biocompatibility and high osteoconductivity. The interactions between HAp and protein or cell have been studied. The HAp related bioceramics such as bone substitute, coating substance of metal implants, inorganic-polymer composites, and cell culture. We described two methods; (1) surface modification of HAp using organosilane; (2) fabrication of HAp ultra-thin layer on gold surface for protein adsorption analyzed with QCM-D technique. The interfacial interaction between collagen and HAp in a nano-region was controlled by depositing the organosilane of n-octadecyltrimethoxysilane (ODS: -CH3) or aminopropyltriethoxysilane (APTS: -NH2) with a chemical vapor deposition method. The morphologies of collagen adsorbed on the surfaces of HAp and HAp deposited with APTS were similar, however that of the surface with ODS was apparently different, due to the hydrophobic interaction between the organic head group of -CH3 and residual groups of collagen. We present a method for coating gold quartz crystal microbalance with dissipation (QCM-D) sensor with ultra-thin layer of hydroxyapatite nanocrystals evenly covering and tightly bound to the surface. The hydroxyapatite sensor operated in liquid with high stability and sensitivity. The in-situ adsorption mechanism and conformational change of fibrinogen on gold, titanium and hydroxyapatite surfaces were investigated by QCM-D technique and Fourier-transform infrared spectroscopy. The study indicates that the hydroxyapatite sensor is applicable for qualitative and conformational analysis of protein adsorption.

  4. Development of Surface Modification Methods for Religaheart® Cardiac Support System

    Directory of Open Access Journals (Sweden)

    Major R.

    2016-09-01

    Full Text Available The work is a review of the methods of the surface modification performed by the authors dedicated for for cardiac support system. It presents the evolution of designing the surface dedicated to direct contact with blood. Initially thin and ultrathin coatings were developed. They were designed as a blood-polymer barrier. The pneumatic heart assist devices are made of a medical grade polyurethane. A major milestone was to create advanced ceramic thin films expressing the flexible effects deposited by physical techniques. Coatings have evolved. Another milestone was the surface reproducing the microenvironment to capture progenitor cells from the bloodstream. Thin coatings were prepared, using methods of ion been, controlled residual stresses were introduced. Wrinkles appeared without cracking. This enabled taking control over the process of cell differentiation. Alternatively, the tissue inspired structure resulted of the coating in the form of extracellular matrix. The outer surface was modified with synthetic materials. This enabled the effective proteins docking to induce cell growth, recreating the luminal side of the blood vessel. Coagulation processes have been slowed down. In addition, it was found pro-angiogenic effect.

  5. Multifunctional surface modification of silk fabric via graphene oxide repeatedly coating and chemical reduction method

    Science.gov (United States)

    Cao, Jiliang; Wang, Chaoxia

    2017-05-01

    Multifunctional silk fabrics with electrical conductive, anti-ultraviolet and water repellent were successfully prepared by surface modification with graphene oxide (GO). The yellow-brown GO deposited on the surface of silk fabric was converted into graphitic black reduced graphene (RGO) by sodium hydrosulfite. The surface properties of silk fabrics were changed by repeatedly RGO coating process, which have been proved by SEM and XPS. The SEM results showed that the RGO sheets were successive form a continuously thin film on the surface of silk fabrics, and the deposition of GO or RGO also can be proved by XPS. The electrical conductivity was tested by electrical surface resistance value of the silk fabric, the surface resistance decreased with increasing of RGO surface modification times, and a low surface resistance value reached to 3.24 KΩ cm-1 after 9 times of modification, indicating the silk obtained excellent conductivity. The UPF value of one time GO modification silk fabric (silk-1RGO) was enhanced significantly to 24.45 in comparison to 10.40 of original silk. The contact angle of RGO coating silk samples was all above of 120°. The durability of RGO coated silk fabrics was tested by laundering. The electrical surface resistance of silk-4RGO (65.74 KΩ cm-1), silk-6RGO (15.54 KΩ cm-1) and silk-8RGO (3.86 KΩ cm-1) fabrics was up to 86.82, 22.30 and 6.57 KΩ cm-1 after 10 times of standard washing, respectively. The UPF value, contact angle and color differences of RGO modified silk fabric slightly changed before and after 10 times of standard washing. Therefore, the washing fastness of electric conduction, anti-ultraviolet and water repellent multifunctional silk fabrics was excellent.

  6. Surface Modification of Zirconia Substrate by Calcium Phosphate Particles Using Sol-Gel Method.

    Science.gov (United States)

    Jin, So Dam; Um, Sang Cheol; Lee, Jong Kook

    2015-08-01

    Surface modification with a biphasic composition of hydroxyapatite (HA) and tricalcium phosphate (TCP) was performed on a zirconia substrate using a sol-gel method. An initial calcium phosphate sol was prepared by mixing a solution of Ca(NO3)2 · 4H20 and (C2H5O)3P(O), while both porous and dense zirconia were used as substrates. The sol-gel coating was performed using a spin coater. The coated porous zirconia substrate was re-sintered at 1350 °C 2 h, while coated dense zirconia substrate was heat-treated at 750 °C 1 h. The microstructure of the resultant HA/TCP coatings was found to be dependent on the type of zirconia substrate used. With porous zirconia as a starting substrate, numerous isolated calcium phosphate particles (TCP and HA) were uniformly dispersed on the surface, and the particle size and covered area were dependent on the viscosity of the calcium phosphate sol. Conversely, when dense zirconia was used as a starting substrate, a thick film of nano-sized HA particles was obtained after heat treatment, however, substantial agglomeration and cracking was also observed.

  7. Surface Modification for Microreactor Fabrication

    Directory of Open Access Journals (Sweden)

    Wladyslaw Torbicz

    2006-04-01

    Full Text Available In this paper, methods of surface modification of different supports, i.e. glass andpolymeric beads for enzyme immobilisation are described. The developed method ofenzyme immobilisation is based on Schiff’s base formation between the amino groups onthe enzyme surface and the aldehyde groups on the chemically modified surface of thesupports. The surface of silicon modified by APTS and GOPS with immobilised enzymewas characterised by atomic force microscopy (AFM, time-of-flight secondary ion massspectroscopy (ToF-SIMS and infrared spectroscopy (FTIR. The supports withimmobilised enzyme (urease were also tested in combination with microreactors fabricatedin silicon and Perspex, operating in a flow-through system. For microreactors filled withurease immobilised on glass beads (Sigma and on polymeric beads (PAN, a very high andstable signal (pH change was obtained. The developed method of urease immobilisationcan be stated to be very effective.

  8. Method for atmospheric pressure reactive atom plasma processing for surface modification

    Science.gov (United States)

    Carr, Jeffrey W [Livermore, CA

    2009-09-22

    Reactive atom plasma processing can be used to shape, polish, planarize and clean the surfaces of difficult materials with minimal subsurface damage. The apparatus and methods use a plasma torch, such as a conventional ICP torch. The workpiece and plasma torch are moved with respect to each other, whether by translating and/or rotating the workpiece, the plasma, or both. The plasma discharge from the torch can be used to shape, planarize, polish, and/or clean the surface of the workpiece, as well as to thin the workpiece. The processing may cause minimal or no damage to the workpiece underneath the surface, and may involve removing material from the surface of the workpiece.

  9. Chemical surface modification of calcium carbonate particles with stearic acid using different treating methods

    Energy Technology Data Exchange (ETDEWEB)

    Cao, Zhi [Materials Research Institute, Athlone Institute of Technology, Athlone (Ireland); Daly, Michael [Mergon International, Castlepollard, Westmeath (Ireland); Clémence, Lopez [Polytech Grenoble, Grenoble (France); Geever, Luke M.; Major, Ian; Higginbotham, Clement L. [Materials Research Institute, Athlone Institute of Technology, Athlone (Ireland); Devine, Declan M., E-mail: ddevine@ait.ie [Materials Research Institute, Athlone Institute of Technology, Athlone (Ireland)

    2016-08-15

    Highlights: • The effects of stearic acid treatment for CaCO{sub 3} are highly influenced by the treatment method of application. • A new stearic acid treatment method, namely, combination treatment for CaCO{sub 3} was developed. • The combination treatment was compared with two of the existing methods dry and wet method. • The negative effects of void coalescence was minimised by the utilization of the combination method. - Abstract: Calcium carbonate (CaCO{sub 3}) is often treated with stearic acid (SA) to decrease its polarity. However, the method of application of the SA treatments has a strong influence on CaCO{sub 3} thermoplastic composite’s interfacial structure and distribution. Several of papers describe the promising effects of SA surface treatment, but few compare the treatment process and its effect on the properties of the final thermoplastic composite. In the current study, we assessed a new SA treatment method, namely, complex treatment for polymer composite fabrication with HDPE. Subsequently, a comparative study was performed between the “complex” process and the other existing methods. The composites were assessed using different experiments included scanning electron microscopy (SEM), void content, density, wettability, differential scanning calorimetry (DSC), and tensile tests. It was observed that the “complex” surface treatment yielded composites with a significantly lower voids content and higher density compared to other surface treatments. This indicates that after the “complex” treatment process, the CaCO{sub 3} particles and HDPE matrix are more tightly packed than other methods. DSC and wettability results suggest that the “wet” and “complex” treated CaCO{sub 3} composites had a significantly higher heat of fusion and moisture resistance compared to the “dry” treated CaCO{sub 3} composites. Furthermore, “wet” and “complex” treated CaCO{sub 3} composites have a significantly higher tensile

  10. A new method for surface modifications of carbon steels and alloys

    Directory of Open Access Journals (Sweden)

    Valeriy Dondokovich Dugar-Zhabon

    2012-12-01

    Full Text Available A three-dimensional treatment method involving implantation of ions into solids immersed in a high voltage pulse discharge ignited on the left-hand-branch of the Paschen curve was elaborated about fifteen years ago. This method, named 3DII for short, has been used in the equipment JUPITER (Joint Universal Plasma and Ion Technologies Experimental Reactor for practical purposes. Hereafter, the need for better means to improve the metal surface protection against aggressive media prompted an elaboration of the MOSMET concept which is based on a hybrid treatment involving the processes of implantation and deposition. It is significant that the processes can be set into action simultaneously or separately. In this article, the conditions of hybrid treatment of AISI SAE 1010, 1020 y 1045 carbon steels, their subsequent electrochemical diagnostics and corrosion test results are described. The corrosion rate of the samples treated by titanium hybrid discharge is found approximately an order of magnitude smaller as compared to the non-treated samples.

  11. Microscale surface modifications for heat transfer enhancement.

    Science.gov (United States)

    Bostanci, Huseyin; Singh, Virendra; Kizito, John P; Rini, Daniel P; Seal, Sudipta; Chow, Louis C

    2013-10-09

    In this experimental study, two surface modification techniques were investigated for their effect on heat transfer enhancement. One of the methods employed the particle (grit) blasting to create microscale indentations, while the other used plasma spray coating to create microscale protrusions on Al 6061 (aluminum alloy 6061) samples. The test surfaces were characterized using scanning electron microscopy (SEM) and confocal scanning laser microscopy. Because of the surface modifications, the actual surface area was increased up to 2.8× compared to the projected base area, and the arithmetic mean roughness value (Ra) was determined to vary from 0.3 μm for the reference smooth surface to 19.5 μm for the modified surfaces. Selected samples with modified surfaces along with the reference smooth surface were then evaluated for their heat transfer performance in spray cooling tests. The cooling system had vapor-atomizing nozzles and used anhydrous ammonia as the coolant in order to achieve heat fluxes up to 500 W/cm(2) representing a thermal management setting for high power systems. Experimental results showed that the microscale surface modifications enhanced heat transfer coefficients up to 76% at 500 W/cm(2) compared to the smooth surface and demonstrated the benefits of these practical surface modification techniques to enhance two-phase heat transfer process.

  12. Ion bombardment modification of surfaces

    International Nuclear Information System (INIS)

    Auciello, O.

    1984-01-01

    An historical overview of the main advances in the understanding of bombardment-induced surface topography is presented. The implantation and sputtering mechanisms which are relevant to ion bombardment modification of surfaces and consequent structural, electronic and compositional changes are described. Descriptions of plasma and ion-beam sputtering-induced film formation, primary ion-beam deposition, dual beam techniques, cluster of molecule ion-beam deposition, and modification of thin film properties by ion bombardment during deposition are presented. A detailed account is given of the analytical and computational modelling of topography from the viewpoint of first erosion theory. Finally, an account of the possible application and/or importance of textured surfaces in technologies and/or experimental techniques not considered in previous chapters is presented. refs.; figs.; tabs

  13. Ion bombardment modification of surfaces

    International Nuclear Information System (INIS)

    Auciello, O.

    1984-01-01

    Ion bombardment-induced modification of surfaces may be considered one of the significant scientific and technological developments of the last two decades. The understanding acquired concerning the underlying mechanisms of several phenomena occurring during ion-surface interactions has led to applications within different modern technologies. These include microelectronics, surface acoustical and optical technologies, solar energy conversion, thin film technology, ion implantation metallurgy, nuclear track technology, thermonuclear fusion, vacuum technology, cold welding technology, biomedicine (implantology). It has become clear that information on many relevant advances, regarding ion bombardment modification of surfaces is dispersed among journals involving fields sometimes not clearly related. This may result, in some cases, in a loss of the type of interdisciplinary exchange of ideas, which has proved to be so fruitful for the advancement of science and technology. This book has been planned in an attempt to collect at least some of today's relevant information about the experimental and theoretical knowledge related to surface modification and its application to technology. (Auth.)

  14. Surface modification agents for lithium batteries

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Zonghai; Amine, Khalil; Belharouak, Ilias

    2017-11-21

    An active material for an electrochemical device wherein a surface of the active material is modified by a surface modification agent, wherein the surface modification agent is an organometallic compound.

  15. Modification of the surfaces of stainless steel during titanium nitride deposition by a dynamic mixing method

    Science.gov (United States)

    Yokota, Katsuhiro; Tamura, Susumu; Nakamura, Kazuhiro; Horiguchi, Motohiro; Nakaiwa, Hiroki; Sugimoto, Takashi; Akamatsu, Katsuya; Nakao, Kazuyoshi

    2000-05-01

    Surfaces of stainless steel SUS304 were coated with titanium nitride (TiN) at temperatures ranging from 400°C to 770°C using a dynamic mixing technique. The N+ ions were accelerated at energies of 0.5-2.0 keV, and were implanted into the stainless steel. The composition of the prepared TiN films was measured using Rutherford backscattering spectrometry with He ions at an energy of 2.0 MeV. Intermediate layers containing compounds such as FesNq, Cr2N, and CrFe were formed between the TiN films and substrates at substrate temperatures higher than 700°C. The thickness of the TiN films decreased significantly when the intermediate layers were formed.

  16. Effect of the Ecological Methods on the Surface Modification of the Kenaf Fibers

    Directory of Open Access Journals (Sweden)

    Süleyman İlker MISTIK

    2016-09-01

    Full Text Available Kenaf is a biodegradable and environmental friendly bast fibre. The most rapidly expanding application field for kenaf fibre is composites as reinforcing material. In this study four different chemical treatments were applied to kenaf fibre by using conventional, ultrasonic and microwave methods. Weight loss, tensile strength, elongation properties, morphological characteristics (SEM and FTIR analysis of the treated kenaf fibre were carried out. Valuable results were obtained from formic acid and acetic acid treatments of kenaf fibre by ultrasonic and microwave methods. The reasons for the ultrasonic and microwave processes to be successful are the strength achieved by sonication and microwave.DOI: http://dx.doi.org/10.5755/j01.ms.22.3.8694

  17. A new high-resolution 3-D quantitative method for identifying bone surface modifications with implications for the Early Stone Age archaeological record.

    Science.gov (United States)

    Pante, Michael C; Muttart, Matthew V; Keevil, Trevor L; Blumenschine, Robert J; Njau, Jackson K; Merritt, Stephen R

    2017-01-01

    Bone surface modifications have become important indicators of hominin behavior and ecology at prehistoric archaeological sites. However, the method by which we identify and interpret these marks remains largely unchanged despite decades of research, relying on qualitative criteria and lacking standardization between analysts. Recently, zooarchaeologists have begun using new technologies capable of capturing 3-D data from bone surface modifications to advance our knowledge of these informative traces. However, an important step in this research has been overlooked and after years of work, we lack both a universal and replicable protocol and an understanding of the precision of these techniques. Here we propose a new standard for identifying bone surface modifications using high-resolution 3-D data and offer a systematic and replicable approach for researchers to follow. Data were collected with a white-light non-contact confocal profilometer and analyzed with Digital Surf's Mountains ® software. Our data show that when methods are standardized, results between researchers are statistically indistinguishable. Multivariate analyses using the measured parameters allow discrimination between stone tool cut marks and mammalian carnivore tooth marks with 97.5% accuracy. Application of this method to fossil specimens resulted in 100% correspondence with identifications made by an experienced analyst using macroscopic observations of qualitative features of bone surface modifications. High-resolution 3-D analyses of bone surface modifications have great potential to improve the reliability and accuracy of taphonomic research, but only if our methods are replicable and precise. Copyright © 2016 Elsevier Ltd. All rights reserved.

  18. Energy conservation potential of surface modification technologies

    Energy Technology Data Exchange (ETDEWEB)

    Le, H.K.; Horne, D.M.; Silberglitt, R.S.

    1985-09-01

    This report assesses the energy conservation impact of surface modification technologies on the metalworking industries. The energy conservation impact of surface modification technologies on the metalworking industries is assessed by estimating their friction and wear tribological sinks and the subsequent reduction in these sinks when surface modified tools are used. Ion implantation, coatings, and laser and electron beam surface modifications are considered.

  19. Silica/Perfluoropolymer nanocomposites fabricated by direct melt-compounding: a novel method without surface modification on nano-silica.

    Science.gov (United States)

    Tanahashi, Mitsuru; Hirose, Masaki; Watanabe, Yusuke; Lee, Jeong-Chang; Takeda, Kunihiko

    2007-07-01

    A novel method for the fabrication of silica/perfluoropolymer nanocomposites was investigated, whereby nano-sized silica particles without surface modification were dispersed uniformly through mechanical breakdown of loosely packed agglomerates of silica nanoparticles with low fracture strength in a polymer melt during direct melt-compounding. The method consists of two stages. The first stage involves preparation of the loose silica agglomerate, and the second stage involves melt-compounding of a completely hydrophobic perfluoropolymer, poly(tetrafluoroethyleneco-perfluoropropylvinylether), with the loose silica agglomerates prepared in the first stage. In the first stage, the packing structure and the fracture strength of the silica agglomerate were controlled by destabilizing an aqueous colloidal silica solution with a mean primary diameter of 190 nm via pH control and salt addition. In the next stage, the silica/perfluoropolymer nanocomposite was fabricated by breaking down the prepared loose silica agglomerates with low fracture strength by means of a shear force inside the polymer melt during melt-compounding.

  20. Inorganic Surface Modification of Nonwoven Polymeric Substrates

    Science.gov (United States)

    Halbur, Jonathan Chandler

    In this study, atomic layer deposition (ALD), a vapor phase inorganic thin film deposition technique, is used to modify the surface of a range of industrially relevant polymers to enhance surface properties or impart additional functionalities. Several unique demonstrations of polymer surface modification are presented including uniform nanomaterial photodeposition to the surface of nonowoven fabrics and the first application of photocatalytic thin film coated nonwovens for advanced filtration of heavy metals from solution. Recent advances in polymer synthesis and processing technologies have resulted in the production of novel polymer systems with unique chemistries and sub-micron scale dimensions. As a result, advanced fiber systems have received much attention for potential use in a wide range of industrially and medically important applications such as advanced and selective filtration, catalysis, flexible electronics, and tissue engineering. However, tailoring the surface properties of the polymer is still needed in order to realize the full range of advanced applications, which can be difficult given the high complexity and non-uniformity of nonwoven polymeric structures. Uniform and controllable inorganic surface modification of nonwovens allows the introduction or modification of many crucial polymer properties with a wide range of application methods.

  1. Surface Modifications in Adhesion and Wetting

    Science.gov (United States)

    Longley, Jonathan

    Advances in surface modification are changing the world. Changing surface properties of bulk materials with nanometer scale coatings enables inventions ranging from the familiar non-stick frying pan to advanced composite aircraft. Nanometer or monolayer coatings used to modify a surface affect the macro-scale properties of a system; for example, composite adhesive joints between the fuselage and internal frame of Boeing's 787 Dreamliner play a vital role in the structural stability of the aircraft. This dissertation focuses on a collection of surface modification techniques that are used in the areas of adhesion and wetting. Adhesive joints are rapidly replacing the familiar bolt and rivet assemblies used by the aerospace and automotive industries. This transition is fueled by the incorporation of composite materials into aircraft and high performance road vehicles. Adhesive joints have several advantages over the traditional rivet, including, significant weight reduction and efficient stress transfer between bonded materials. As fuel costs continue to rise, the weight reduction is accelerating this transition. Traditional surface pretreatments designed to improve the adhesion of polymeric materials to metallic surfaces are extremely toxic. Replacement adhesive technologies must be compatible with the environment without sacrificing adhesive performance. Silane-coupling agents have emerged as ideal surface modifications for improving composite joint strength. As these coatings are generally applied as very thin layers (compression of a water drop between two gradient surfaces. This inchworm type motion is studied in detail and offers an alternative method to surface vibration for moving drops in microfluidic devices. The final surface modification considered is the application of a thin layer of rubber to a rigid surface. While this technique has many practical uses, such as easy release coatings in marine environments, it is applied herein to enable spontaneous

  2. Development of Fabrication Methods of Filler/Polymer Nanocomposites: With Focus on Simple Melt-Compounding-Based Approach without Surface Modification of Nanofillers

    Directory of Open Access Journals (Sweden)

    Mitsuru Tanahashi

    2010-03-01

    Full Text Available Many attempts have been made to fabricate various types of inorganic nanoparticle-filled polymers (filler/polymer nanocomposites by a mechanical or chemical approach. However, these approaches require modification of the nanofiller surfaces and/or complicated polymerization reactions, making them unsuitable for industrial-scale production of the nanocomposites. The author and coworkers have proposed a simple melt-compounding method for the fabrication of silica/polymer nanocomposites, wherein silica nanoparticles without surface modification were dispersed through the breakdown of loose agglomerates of colloidal nano-silica spheres in a kneaded polymer melt. This review aims to discuss experimental techniques of the proposed method and its advantages over other developed methods.

  3. Development of Fabrication Methods of Filler/Polymer Nanocomposites: With Focus on Simple Melt-Compounding-Based Approach without Surface Modification of Nanofillers

    Science.gov (United States)

    Tanahashi, Mitsuru

    2010-01-01

    Many attempts have been made to fabricate various types of inorganic nanoparticle-filled polymers (filler/polymer nanocomposites) by a mechanical or chemical approach. However, these approaches require modification of the nanofiller surfaces and/or complicated polymerization reactions, making them unsuitable for industrial-scale production of the nanocomposites. The author and coworkers have proposed a simple melt-compounding method for the fabrication of silica/polymer nanocomposites, wherein silica nanoparticles without surface modification were dispersed through the breakdown of loose agglomerates of colloidal nano-silica spheres in a kneaded polymer melt. This review aims to discuss experimental techniques of the proposed method and its advantages over other developed methods.

  4. Covalent Surface Modifications of Carbon Nanotubes.

    Energy Technology Data Exchange (ETDEWEB)

    Pavia Sanders, Adriana [Sandia National Lab. (SNL-CA), Livermore, CA (United States); O' Bryan, Greg [Sandia National Lab. (SNL-CA), Livermore, CA (United States)

    2017-07-01

    A report meant to document the chemistries investigated by the author for covalent surface modification of CNTs. Oxidation, cycloaddition, and radical reactions were explored to determine their success at covalently altering the CNT surface. Characterization through infrared spectroscopy, Raman spectroscopy, and thermo gravimetric analysis was performed in order to determine the success of the chemistries employed. This report is not exhaustive and was performed for CNT surface modification exploration as it pertains to the "Next Gen" project.

  5. Modification of surfaces and surface layers by non equilibrium processes

    International Nuclear Information System (INIS)

    Beamson, G.; Brennan, W.J.; Clark, D.T.; Howard, J.

    1988-01-01

    Plasmas are examples of non-equilibrium phenomena which are being used increasingly for the synthesis and modification of materials impossible by conventional routes. This paper introduces methods available by describing the construction and characteristics of some equipment used for the production of different types of plasmas and other non-equilibrium phenomena. This includes high energy ion beams. The special features, advantages and disadvantages of the techniques will be described. There are a multitude of potential application relevant to electronic, metallic, ceramic, and polymeric materials. However, scale-up from the laboratory to production equipment depends on establishing a better understanding of both the physics and chemistry of plasma as well as plasma-solid interactions. Examples are given of how such an understanding can be gained. The chemical analysis of polymer surfaces undergoing modification by inert gas, hydrogen or oxygen plasmas is shown to give physical information regarding the relative roles of diffusion of active species, and direct and radiative energy transfer from the plasma. Surface modification by plasma depositing a new material onto an existing substrate is discussed with particular reference to the deposition of amorphous carbon films. Applications of the unique properties of these films are outlined together with our current understanding of these properties based on chemical and physical methods of analysis of both the films and the plasmas producing them. Finally, surface modification by ion beams is briefly illustrated using examples from the electronics and metals industries where the modification has had a largely physical rather than chemical effect on the starting material. (orig.)

  6. Electroless plating of PVC plastic through new surface modification method applying a semi-IPN hydrogel film

    International Nuclear Information System (INIS)

    Wang, Ming-Qiu; Yan, Jun; Du, Shi-Guo; Li, Hong-Guang

    2013-01-01

    A novel palladium-free surface activation process for electroless nickel plating was developed. This method applied a semi-Interpenetrating Polymer Network (semi-IPN) hydrogel film to modify the poly(vinyl chloride) (PVC) surface by chemical bonds. The activation process involved the formation of semi-IPN hydrogel film on the PVC surface and the immobilization of catalyst for electroless plating linking to the pretreated substrate via N-Ni chemical bond. The hydrogel layer was used as the chemisorption sites for nickel ions, and the catalyst could initiate the subsequent electroless nickel plating onto the PVC surface. Finally, a Ni–P layer was deposited on the nickel-activated PVC substrate by electroless plating technique. The composition and morphology of nickel-plated PVC foils were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD). The results of SEM and XRD show that a compact and continuous Ni–P layer with amorphous nickel phase is formed on the PVC surface. EDS shows that the content of the nickel and the phosphorus in the deposits is 89.4 wt.% and 10.6 wt.%, respectively.

  7. Electroless plating of PVC plastic through new surface modification method applying a semi-IPN hydrogel film

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Ming-Qiu, E-mail: mqwang1514@163.com; Yan, Jun; Du, Shi-Guo; Li, Hong-Guang

    2013-07-15

    A novel palladium-free surface activation process for electroless nickel plating was developed. This method applied a semi-Interpenetrating Polymer Network (semi-IPN) hydrogel film to modify the poly(vinyl chloride) (PVC) surface by chemical bonds. The activation process involved the formation of semi-IPN hydrogel film on the PVC surface and the immobilization of catalyst for electroless plating linking to the pretreated substrate via N-Ni chemical bond. The hydrogel layer was used as the chemisorption sites for nickel ions, and the catalyst could initiate the subsequent electroless nickel plating onto the PVC surface. Finally, a Ni–P layer was deposited on the nickel-activated PVC substrate by electroless plating technique. The composition and morphology of nickel-plated PVC foils were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD). The results of SEM and XRD show that a compact and continuous Ni–P layer with amorphous nickel phase is formed on the PVC surface. EDS shows that the content of the nickel and the phosphorus in the deposits is 89.4 wt.% and 10.6 wt.%, respectively.

  8. Electroless plating of PVC plastic through new surface modification method applying a semi-IPN hydrogel film

    Science.gov (United States)

    Wang, Ming-Qiu; Yan, Jun; Du, Shi-Guo; Li, Hong-Guang

    2013-07-01

    A novel palladium-free surface activation process for electroless nickel plating was developed. This method applied a semi-Interpenetrating Polymer Network (semi-IPN) hydrogel film to modify the poly(vinyl chloride) (PVC) surface by chemical bonds. The activation process involved the formation of semi-IPN hydrogel film on the PVC surface and the immobilization of catalyst for electroless plating linking to the pretreated substrate via Nsbnd Ni chemical bond. The hydrogel layer was used as the chemisorption sites for nickel ions, and the catalyst could initiate the subsequent electroless nickel plating onto the PVC surface. Finally, a Ni-P layer was deposited on the nickel-activated PVC substrate by electroless plating technique. The composition and morphology of nickel-plated PVC foils were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD). The results of SEM and XRD show that a compact and continuous Ni-P layer with amorphous nickel phase is formed on the PVC surface. EDS shows that the content of the nickel and the phosphorus in the deposits is 89.4 wt.% and 10.6 wt.%, respectively.

  9. Competition between surface modification and abrasive polishing: a method of controlling the surface atomic structure of 4H-SiC (0001)

    Science.gov (United States)

    Deng, Hui; Endo, Katsuyoshi; Yamamura, Kazuya

    2015-03-01

    The surface atomic step-terrace structure of 4H-SiC greatly affects its performance in power device applications. On the basis of the crystal structure of 4H-SiC, we propose the generation mechanism of the a-b-a*-b* type, a-b type and a-a type step-terrace structures. We demonstrate that the step-terrace structure of SiC can be controlled by adjusting the balance between chemical modification and physical removal in CeO2 slurry polishing. When chemical modification plays the main role in the polishing of SiC, the a-b-a*-b* type step-terrace structure can be generated. When the roles of physical removal and chemical modification have similar importance, the a-b-a*-b* type step-terrace structure changes to the a-b type. When physical removal is dominant, the uniform a-a type step-terrace structure can be generated.

  10. Surface Modification of the Ti6Al4V Alloy with Silicon Carbonitride Layer Deposited by PACVD Method

    Science.gov (United States)

    Jonas, Stanisława; Konefał-Góral, Jadwiga; Małek, Anna; Kluska, Stanisława; Grzesik, Zbigniew

    2014-09-01

    Four different layers of various silicon, carbon and nitrogen contents on the Ti6Al4V alloy and (001)Si wafers have been deposited by means of Plasma Assisted Chemical Vapor Deposition (PACVD) method. The layers were obtained from reactive gas mixture containing SiH4, CH4, NH3 and Ar. After deposition the structure and chemical composition of modified surfaces have been analyzed with use of SEM/EDS technique. Based on these results and thermodynamic calculations, the diffusion coefficients, D, for nitrogen and carbon in alloy were discussed. Scratch test shown that silicon carbonitride layers have good adhesion to metal surface. In order to determine atomic structure of obtained layers, FTIR spectra for layer-(001)Si and layer-Ti6Al4V were registered.

  11. Surface modification of pharmaceutical powders

    OpenAIRE

    Zhou, Qi

    2017-01-01

    This thesis describes a body of work to investigate a mechanical dry powder coating approach aiming to modify the surface properties of fine pharmaceutical powders. Powders were coated with magnesium stearate (MgSt) in order to improve their bulk powder properties such as flowability, fluidization and aerosolization. The flow characteristics of a cohesive milled lactose monohydrate powder (Pharmatose® 450M, VMD around 20 μm) were substantially improved by processing with 1% w/w magn...

  12. Surface Modification of Catalytic Materials

    DEFF Research Database (Denmark)

    Nierhoff, Anders Ulrik Fregerslev

    aggregation techniques. With the use of two different filter mechanisms, the Quadrupole and the Lateral Time Of Flight, the nanoparticles were mass selected. This was done to correlate nanoparticle size with reactivity. Selected key findings can be summarized as: 1) CO induced surface changes of Pt based...... methanol synthesis. The importance of conducting well controlled UHV experiments and characterization in combination with experiments at higher pressures to span the pressure gap between UHV and operando conditions is definitely highlighted in this thesis....

  13. Validation of a modification to Performance-Tested Method 010403: microwell DNA hybridization assay for detection of Listeria spp. in selected foods and selected environmental surfaces.

    Science.gov (United States)

    Alles, Susan; Peng, Linda X; Mozola, Mark A

    2009-01-01

    A modification to Performance-Tested Method 010403, GeneQuence Listeria Test (DNAH method), is described. The modified method uses a new media formulation, LESS enrichment broth, in single-step enrichment protocols for both foods and environmental sponge and swab samples. Food samples are enriched for 27-30 h at 30 degrees C, and environmental samples for 24-48 h at 30 degrees C. Implementation of these abbreviated enrichment procedures allows test results to be obtained on a next-day basis. In testing of 14 food types in internal comparative studies with inoculated samples, there were statistically significant differences in method performance between the DNAH method and reference culture procedures for only 2 foods (pasteurized crab meat and lettuce) at the 27 h enrichment time point and for only a single food (pasteurized crab meat) in one trial at the 30 h enrichment time point. Independent laboratory testing with 3 foods showed statistical equivalence between the methods for all foods, and results support the findings of the internal trials. Overall, considering both internal and independent laboratory trials, sensitivity of the DNAH method relative to the reference culture procedures was 90.5%. Results of testing 5 environmental surfaces inoculated with various strains of Listeria spp. showed that the DNAH method was more productive than the reference U.S. Department of Agriculture-Food Safety and Inspection Service (USDA-FSIS) culture procedure for 3 surfaces (stainless steel, plastic, and cast iron), whereas results were statistically equivalent to the reference method for the other 2 surfaces (ceramic tile and sealed concrete). An independent laboratory trial with ceramic tile inoculated with L. monocytogenes confirmed the effectiveness of the DNAH method at the 24 h time point. Overall, sensitivity of the DNAH method at 24 h relative to that of the USDA-FSIS method was 152%. The DNAH method exhibited extremely high specificity, with only 1% false

  14. Surface modification of recording electrodes

    Directory of Open Access Journals (Sweden)

    Iaci Miranda Pereira

    2013-01-01

    Full Text Available Waterborne Polyurethanes (PUs are a family of polymers that contains urethane linkages synthesized in an aqueous environment and are thus free of organic solvents. Recently, waterborne PUs have been extensively studied for biomedical applications because of their biocompatibility. The present work investigates the following: (1 the impact on electrical performance of electrode materials (platinum and silicon modified chemically by a layer of waterborne PU, and (2 the behavior of rat cardiac fibroblasts and rat cardiomyocytes when in contact with an electrode surface. Diisocyanate and poly(caprolactone diol were the main reagents for producing PUs. The electrochemical impedance of the electrode/electrolyte interface was accessed by electrochemical impedance spectroscopy. The cellular viability, proliferation, and morphology changes were investigated using an MTT assay. Cardiomyocyte adherence was observed by scanning electron microscopy. The obtained surface was uniform, flat, and transparent. The film showed good adhesion, and no peeling was detected. The electrochemical impedance decreased over time and was influenced by the ionic permeability of the PU layer. The five samples did not show cytotoxicity when in contact with neonatal rat cells.

  15. Surface modification of materials to encourage beneficial biofilm formation

    Directory of Open Access Journals (Sweden)

    Amreeta Sarjit

    2015-10-01

    Full Text Available Biofilms are communities of sessile microorganisms that grow and produce extrapolymeric substances on an abiotic or biotic surface. Although biofilms are often associated with negative impacts, the role of beneficial biofilms is wide and include applications in bioremediation, wastewater treatment and microbial fuel cells. Microbial adhesion to a surface, which is highly dependent on the physicochemical properties of the cells and surfaces, is an essential step in biofilm formation. Surface modification therefore represents an important way to modulate microbial attachment and ultimately biofilm formation by microorganisms. In this review different surface modification processes such as organosilane surface modification, plasma treatment, and chemical modification of carbon nanotubes, electro-oxidation and covalent-immobilization with neutral red and methylene blue molecules are outlined. The effectiveness of these modifications and their industrial applications are also discussed. There is inadequate literature on surface modification as a process to enhance beneficial biofilm formation. These methods need to be safe, economically viable, scalable and environmental friendly and their potential to fulfil these criteria for many applications has yet to be determined.

  16. Excimer laser surface modification: Process and properties

    Energy Technology Data Exchange (ETDEWEB)

    Jervis, T.R.; Nastasi, M. [Los Alamos National Lab., NM (United States); Hirvonen, J.P. [Technical Research Institute, Espoo (Finland). Metallurgy Lab.

    1992-12-01

    Surface modification can improve materials for structural, tribological, and corrosion applications. Excimer laser light has been shown to provide a rapid means of modifying surfaces through heat treating, surface zone refining, and mixing. Laser pulses at modest power levels can easily melt the surfaces of many materials. Mixing within the molten layer or with the gas ambient may occur, if thermodynamically allowed, followed by rapid solidification. The high temperatures allow the system to overcome kinetic barriers found in some ion mixing experiments. Alternatively, surface zone refinement may result from repeated melting-solidification cycles. Ultraviolet laser light couples energy efficiently to the surface of metallic and ceramic materials. The nature of the modification that follows depends on the properties of the surface and substrate materials. Alloying from both gas and predeposited layer sources has been observed in metals, semiconductors, and ceramics as has surface enrichment of Cr by zone refinement of stainless steel. Rapid solidification after melting often results in the formation of nonequilibrium phases, including amorphous materials. Improved surface properties, including tribology and corrosion resistance, are observed in these materials.

  17. Steel surface modifications in magnetised sliding contact

    Energy Technology Data Exchange (ETDEWEB)

    Paulmier, D. [CNRS, 54 - Vandoeuvre les Nancy (France). Lab. de Physique et Mecanique des Materiaux; Zaidi, H. [CNRS, 54 - Vandoeuvre les Nancy (France). Lab. de Physique et Mecanique des Materiaux; Bedri, R. [CNRS, 54 - Vandoeuvre les Nancy (France). Lab. de Physique et Mecanique des Materiaux; Kadiri, E.K. [CNRS, 54 - Vandoeuvre les Nancy (France). Lab. de Physique et Mecanique des Materiaux; Pan, L. [Beijing Metall. Management Inst. (China); Jiang, Q. [Beijing Metall. Management Inst. (China)

    1995-12-01

    Modifications in the mechanical properties of a ferromagnetic steel surface in sliding contact under the influence of a d.c. magnetic field were investigated. A magnetic field was applied to the steel pin, remaining constant during each test. Experiments were conducted at ambient temperature under different applied normal loads, sliding velocities and magnetic field ensities. Experimental results show that at ambient temperature the application of a magnetic field decreases the fluctuations in the friction coefficient and wear rate and increases the microhardness of the sliding surfaces. The dislocation density increases in the thin coating of the magnetised sliding contact erface. A simple model for the agglomeration of dislocations on the sliding contact is proposed. The results were erpreted by observation and analysis of the surface. Optical microscopy shows that when a magnetic field was applied the sliding surface was covered with thin black particles. The magnetic field promoted the oxidation of the surface. (orig.)

  18. Polymer surface modification by plasmas and photons

    Science.gov (United States)

    Chan, C.-M.; Ko, T.-M.; Hiraoka, H.

    1996-05-01

    Polymers have been applied successfully in fields such as adhesion, biomaterials, protective coatings, friction and wear, composites, microelectronic devices, and thin-film technology. In general, special surface properties with regard to chemical composition, hydrophilicity, roughness, crystallinity, conductivity, lubricity, and cross-linking density are required for the success of these applications. Polymers very often do not possess the surface properties needed for these applications. However, they have excellent bulk physical and chemical properties, are inexpensive, and are easy to process. For these reasons, surface modification techniques which can transform these inexpensive materials into highly valuable finished products have become an important part of the plastics and many other industries. In recent years, many advances have been made in developing surface treatments to alter the chemical and physical properties of polymer surfaces without affecting bulk properties. Common surface modification techniques include treatments by flame, corona, plasmas, photons, electron beams, ion beams, X-rays, and γ-rays. Plasma treatment is probably the most versatile surface treatment technique. Different types of gases such as argon, oxygen, nitrogen, fluorine, carbon dioxide, and water can produce the unique surface properties required by various applications. For example, oxygen-plasma treatment can increase the surface energy of polymers, whereas fluorine-plasma treatment can decrease the surface energy and improve the chemical inertness. Cross-linking at a polymer surface can be introduced by an inert-gas plasma. Modification by plasma treatment is usually confined to the top several hundred ångströms and does not affect the bulk properties. The main disadvantage of this technique is that it requires a vacuum system, which increases the cost of operation. Thin polymer films with unique chemical and physical properties are produced by plasma polymerization

  19. Surface Modification of Nonwoven fabrics by Atmospheric Brush Plasma

    Science.gov (United States)

    Oksuz, Lutfi; Uygun, Emre; Bozduman, Ferhat; Yurdabak Karaca, Gozde; Asan, Orkun Nuri; Uygun Oksuz, Aysegul

    2017-10-01

    Polypropylene nonwoven fabrics (PPNF) are used in disposable absorbent articles, such as diapers, feminine care products, wipes. PPNF need to be wettable by water or aqueous-based liquid. Plasma surface treatment/modification has turned out to be a well-accepted method since it offers superior surface property enhancement than other chemical methods. The cold plasma brush can most efficiently use the discharge power as well as the plasma gas for material and surface treatment. The very low power consumption of such an atmospheric argon plasma brush provides many unique advantages in practical application. The purpose of this study was to reveal the effectiveness of non-thermal atmospheric plasma brush in surface wettability and modification of two different nonwoven surfaces.

  20. TEXTILE SURFACE MODIFICATION BY PYHSICAL VAPOR DEPOSITION – (REVIEW

    Directory of Open Access Journals (Sweden)

    YUCE Ismail

    2017-05-01

    Full Text Available Textile products are used in various branches of the industry from automotive to space products. Textiles produced for industrial use are generally referred to as technical textiles. Technical textiles are nowadays applied to several areas including transportation, medicine, agriculture, protection, sports, packaging, civil engineering and industry. There are rapid developments in the types of materials used in technical textiles. Therefore, modification and functionalization of textile surfaces is becoming more crucial. The improvements of the properties such as anti-bacterial properties, fire resistivity, UV radiation resistance, electrical conductivity, self cleaning, and super hydrophobic, is getting more concern with respect to developments in textile engineering. The properties of textile surfaces are closely related to the fiber structure, the differences in the polymer composition, the fiber mixture ratio, and the physical and chemical processes applied. Textile surface modifications can be examined in four groups under the name mechanical, chemical, burning and plasma. Surface modifications are made to improve the functionality of textile products. Textile surface modifications affect the properties of the products such as softness, adhesion and wettability. The purpose of this work is to reveal varieties of vapor deposition modifications to improve functionality. For this purpose, the pyhsical vapor deposition methods, their affects on textile products and their end-uses will be reviewed.

  1. Modifing the Surface Layers of Mechanical Components

    Directory of Open Access Journals (Sweden)

    K. Slanec

    2003-01-01

    Full Text Available This paper deals with the creation of thin surface layers prepared by the Plasma Assisted Chemical Vapour Deposition Method (PACVD. Polished sample surfaces made of tool steel were used. An investigation of the dependence of layer thickness on process duration was carried out. The structure of the original surface and the structure of the coated surface were evaluated and compared. The microhardness of the surface areas was also measured.

  2. Cellulose whiskers: preparation, characterization and surface modification

    International Nuclear Information System (INIS)

    Taipina, Marcia O.; Ferrarezi, Marcia M.F.; Goncalves, Maria C.

    2011-01-01

    The main objectives of this work were to produce cellulose whiskers (from cotton fibers) by acid hydrolysis and subsequently modify the surface of these whiskers with 3-iso-cyanate-propyltrietoxy-silane. Cellulose whiskers structures were characterized by X-ray diffraction and Fourier transform infrared and their morphologies were investigated by scanning and transmission electron microscopy. Due to the hydrophilic nature of native cellulose, the formation of cellulose whisker nanocomposites is limited to water-soluble polymers. The applied methodology for surface modification of the whiskers allowed to obtain nanofibers with surface features more appropriate to allow the adhesion at fiber-matrix interface, which may result in a better performance of these fibers as reinforcing agents of hydrophobic polymer matrices. (author)

  3. A facile method of hydrophobic surface modification for acrylonitrile-styrene-acrylate terpolymer based on the out-migration property of metallic soaps

    Science.gov (United States)

    Qi, Yanli; Chen, Tingting; Zhang, Jun

    2018-03-01

    Hydrophobic surface modification is conducted in this study by using additives with long alkyl chains. Several kinds of metallic soaps, such as calcium stearate (CaSt), zinc stearate (ZnSt), magnesium stearate (MgSt) and barium stearate (BaSt) were employed. Polymer matrix is acrylonitrile-styrene-acrylate (ASA) terpolymer due to its wonderful weather resistance property. The surface chemical characterization was studied by Fourier transformed infrared (FTIR) technology and X-ray photoelectron spectroscopy (XPS). Carboxylate (Osbnd Csbnd O-) indexes of composites in both transmittance and reflection modes were calculated according to FTIR results. As to the ratio of carboxylate index in reflection mode to that in transmittance mode, the sample added with 5 wt% ZnSt shows a higher value of 8.77, and a much higher value of 14.47 for the sample added with 10 wt% ZnSt. The corresponding Csbnd C/ Csbnd H /Cdbnd C peak areas of the samples added with 5 wt% or 10 wt% ZnSt are 75.4% and 77.3% respectively, much higher than other samples. This indicates ZnSt is much easier to out-migrate to material surface and therefore is more suitable for hydrophobic surface modification. In particular, the water contact angle of the ASA/ZnSt composite added with 10 wt% ZnSt significantly increased to 127o (40o increase in comparison with pure ASA), successfully converting the surface wettability from hydrophilic to hydrophobic.

  4. Lectures on Modification, Characterization and Modeling of Surfaces. Vol. I

    International Nuclear Information System (INIS)

    1997-01-01

    The field of surfaces and thin films is now so broad that has applications in protective coatings, electronic devices, displays, sensors, optical equipment, bio-compatible coatings for surgical implants, odontological and cardiovascular use, and numerous other technologies that depend on the deposition processes. Even though there exist well established methods for both, production and characterization of high-quality surfaces, the interest in finding alternative methods more reliable and less expensive is one of the challenges of present technologies. In this special issue the attention is focused on some areas concerning surface modification, characterization and modeling of surfaces. The volume contains reviews and articles on plasma processing, nitriding, nitrocarburising, diamond-like films, laser and ion-beam surface modification,texture in films and coatings, nuclear techniques in surface analysis, electron spectroscopies, ion scattering spectroscopy, secondary ion mass spectroscopy, STM and AFM applications to surface science, nano structure preparation magnetic and electric properties, surface modeling, calculation of electric and magnetic properties, statistical thermodynamics of surfaces

  5. Surface modification of cellulose by PCL grafts

    International Nuclear Information System (INIS)

    Paquet, Olivier; Krouit, Mohammed; Bras, Julien; Thielemans, Wim; Belgacem, Mohamed Naceur

    2010-01-01

    Two cellulosic substrates (microcrystalline cellulose, MCC, and bleached kraft softwood pulps, BSK) were grafted by polycaprolactone (PCL) chains with different molecular weights, following a three-step procedure using non-swelling conditions in order to limit the reaction to their surface. First, one of the two OH PCL ends was blocked by phenyl isocyanate and the reaction product (adduct 1) was subsequently reacted with 2,4-toluene diisocyanate (adduct 2) to provide it with an NCO function, capable of reacting with cellulose. The ensuing PCL-grafted cellulosic materials were characterized by weight gain, elemental analysis, contact angle measurements, attenuated total reflexion-Fourier transform infrared (ATR-FTIR), X-ray photoelectron spectroscopy (XPS) and biodegradation tests. The modification was proven to occur by the presence of nitrogen atoms in the elemental analysis tests and XPS spectra of modified and soxhlet-extracted cellulose. The contact angle measurements have also shown that the surface became as hydrophobic as PCL itself. The polar component of the surface energy of cellulosic substrates before treatment was found to be about 32 and 10 mJ m -2 , for MCC and BSK, respectively. This value vanished to practically zero after grafting with different PCLs. The strategy proposed in the present work is original since, to the best of our knowledge, this paper reports for the first time the chemical 'grafting onto' of the cellulose surface by PCL macromolecular structures, with the aim of obtaining fibre-matrix co-continuous fully sustainable and biodegradable composite materials.

  6. Surface modification of polyethylene by plasma

    International Nuclear Information System (INIS)

    Colin O, E.

    2003-01-01

    The products made of polyethylene (PE) go from construction materials, electric insulating until packing material. The films for bags and pack occupy 83.6% of the distribution of the market of PE approximately. The enormous quantity of PE that is generated by its indiscriminate use brings as consequence a deterioration to the atmosphere, due to the long life that they present as waste. This work is a study on the modification of low density polyethylene films. In this type of thin materials, the changes in the surface meet with largely on the conformation of the rest of the material. To induce changes that modify the surface of PE, plasmas were used with reactive atmospheres of air, oxygen and nitrogen. The experimentation that was carries out went to introduce the PE to a cylindrical reactor where it was generated the plasma of air, oxygen and nitrogen to different times of exposure. After having carried out the exposure to the plasma, it was found that in the polyethylene it modifies their morphology, crystallinity, hydrophobicity, composition and electric conductivity. The analytical techniques that were used to characterize later to the polyethylene of being in contact with the plasma were: X-ray diffraction, Scanning Electron Microscopy, Infrared spectroscopy, Electric conductivity, Angle of contact and finally Thermal Gravimetric Analysis. The content of this work it is presented in five chapters: In the chapter 1 there are presented some general concepts of plasma and of the one polymer in study PE. In the chapter 2 it is made a general revision on modification of surfaces, as well as the properties that were modified in polymeric materials that were exposed to plasma in previous works. In the chapter 3 the experimental part and the conditions used are described in the modification of the PE. Also in this chapter a brief description it is made of the used characterization techniques. The results and discussion are presented in the chapter 4. These results

  7. Surface Modification of Polymer Substrates for Biomedical Applications

    Directory of Open Access Journals (Sweden)

    Oldřich Neděla

    2017-09-01

    Full Text Available While polymers are widely utilized materials in the biomedical industry, they are rarely used in an unmodified state. Some kind of a surface treatment is often necessary to achieve properties suitable for specific applications. There are multiple methods of surface treatment, each with their own pros and cons, such as plasma and laser treatment, UV lamp modification, etching, grafting, metallization, ion sputtering and others. An appropriate treatment can change the physico-chemical properties of the surface of a polymer in a way that makes it attractive for a variety of biological compounds, or, on the contrary, makes the polymer exhibit antibacterial or cytotoxic properties, thus making the polymer usable in a variety of biomedical applications. This review examines four popular methods of polymer surface modification: laser treatment, ion implantation, plasma treatment and nanoparticle grafting. Surface treatment-induced changes of the physico-chemical properties, morphology, chemical composition and biocompatibility of a variety of polymer substrates are studied. Relevant biological methods are used to determine the influence of various surface treatments and grafting processes on the biocompatibility of the new surfaces—mammalian cell adhesion and proliferation is studied as well as other potential applications of the surface-treated polymer substrates in the biomedical industry.

  8. Modification of Material Surface Using Plasma-Enhanced Ion Beams

    National Research Council Canada - National Science Library

    Bystritskii, V

    1998-01-01

    ...) Technology for Materials Surface Modification. Following second year programmatic plan, formulated in the conclusion of the 1-st year report we focused our effort on study of aluminum alloys modification (Al2024, 6061, 7075...

  9. DISCUSSION METHODS: MODIFICATION AND TRANSFORMATION

    Directory of Open Access Journals (Sweden)

    Abbasova, A.A.

    2016-03-01

    Full Text Available This article is about how to the importance of selecting the optimal methods of stimulation and motivation to learn. In modern conditions it is very important that the teacher gave the students ready knowledge, and pointed the way for the acquisition of knowledge, taught to acquire knowledge. This requires the selection of effective forms of language and literature work with texts of different types and styles of speech, listening, speaking. In this regard, special attention should be given lessons of speech development. There is a special group of methods to stimulate the development of communicative competence. Among them, and the method of discussion, which is increasingly being used in the classroom in the Russian language

  10. Surface modification of YIG by magnet array

    Energy Technology Data Exchange (ETDEWEB)

    Atalay, S., E-mail: satalay@inonu.edu.tr [Inonu University, Science and Art Faculty, Physics Department, 44280 Malatya (Turkey); Kolat, V.S. [Inonu University, Science and Art Faculty, Physics Department, 44280 Malatya (Turkey); Bakır, H.G. [Inonu University, Science and Art Faculty, Astronomy Department, 44280 Malatya (Turkey); Izgi, T.; Kaya, A.O. [Inonu University, Science and Art Faculty, Physics Department, 44280 Malatya (Turkey); Kaya, O.A. [Inonu University, Education Faculty, Computer Education and Educational Technology Department, 44280 Malatya (Turkey); Gencer, H. [Inonu University, Science and Art Faculty, Physics Department, 44280 Malatya (Turkey)

    2015-11-01

    Highlights: • The surface of YIG films were magnetically modulated by magnet array. • The surface modulated YIG films formed sharp band gaps. • A very small magnetic field change leads a large change in the peak value of band gap frequency. - Abstract: In this work, magnetostatic surface spin waves (MSSW) were propagated along the single crystal YIG (Y{sub 3}Fe{sub 5}O{sub 12}) film grown on GGG substrate. In order to obtain magnonic crystals, unlike the conventional methods, the surface of YIG films were magnetically modulated by magnet array in one and two-dimensions. The surface modulated YIG films formed sharp band gaps at approximately 6.55 GHz and 6.58 GHz at 1600 Oe magnetic field for one and two-dimensional magnonic crystals, respectively. It was found that a very small magnetic field change leads a large change in the peak value of band gap frequency.

  11. Surface modification of YIG by magnet array

    International Nuclear Information System (INIS)

    Atalay, S.; Kolat, V.S.; Bakır, H.G.; Izgi, T.; Kaya, A.O.; Kaya, O.A.; Gencer, H.

    2015-01-01

    Highlights: • The surface of YIG films were magnetically modulated by magnet array. • The surface modulated YIG films formed sharp band gaps. • A very small magnetic field change leads a large change in the peak value of band gap frequency. - Abstract: In this work, magnetostatic surface spin waves (MSSW) were propagated along the single crystal YIG (Y 3 Fe 5 O 12 ) film grown on GGG substrate. In order to obtain magnonic crystals, unlike the conventional methods, the surface of YIG films were magnetically modulated by magnet array in one and two-dimensions. The surface modulated YIG films formed sharp band gaps at approximately 6.55 GHz and 6.58 GHz at 1600 Oe magnetic field for one and two-dimensional magnonic crystals, respectively. It was found that a very small magnetic field change leads a large change in the peak value of band gap frequency.

  12. Hemocompatible surface of electrospun nanofibrous scaffolds by ATRP modification

    Energy Technology Data Exchange (ETDEWEB)

    Yuan, Wenjie [School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072 (China); Feng, Yakai, E-mail: yakaifeng@hotmail.com [School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072 (China); Key Laboratory of Systems Bioengineering of Ministry of Education, Tianjin University, Tianjin 300072 (China); Tianjin University-Helmholtz-Zentrum Geesthacht, Joint Laboratory for Biomaterials and Regenerative Medicine, Weijin Road 92, 300072 Tianjin (China); Wang, Heyun [School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072 (China); School of Chemistry and Chemical Engineering, Shihezi University, Shihezi 832002 (China); Yang, Dazhi [School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072 (China); An, Bo [Department of Orthopedics, Affiliated Hospital of Logistics University of Chinese People' s Armed Police Force, Tianjin 300162 (China); Zhang, Wencheng [Department of Physiology and Pathophysiology, Logistics University of Chinese People' s Armed Police Force, Tianjin 300162 (China); Khan, Musammir [School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072 (China); Guo, Jintang [School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072 (China); Tianjin University-Helmholtz-Zentrum Geesthacht, Joint Laboratory for Biomaterials and Regenerative Medicine, Weijin Road 92, 300072 Tianjin (China)

    2013-10-15

    The electrospun scaffolds are potential application in vascular tissue engineering since they can mimic the nano-sized dimension of natural extracellular matrix (ECM). We prepared a fibrous scaffold from polycarbonateurethane (PCU) by electrospinning technology. In order to improve the hydrophilicity and hemocompatibility of the fibrous scaffold, poly(ethylene glycol) methacrylate (PEGMA) was grafted onto the fiber surface by surface-initiated atom transfer radical polymerization (SI-ATRP) method. Although SI-ATRP has been developed and used for surface modification for many years, there are only few studies about the modification of electrospun fiber by this method. The modified fibrous scaffolds were characterized by SEM, Fourier transform infrared (FTIR), and X-ray photoelectron spectroscopy (XPS). The scaffold morphology showed no significant difference when PEGMA was grafted onto the scaffold surface. Based on the water contact angle measurement, the surface hydrophilicity of the scaffold surface was improved significantly after grafting hydrophilic PEGMA (P = 0.0012). The modified surface showed effective resistance for platelet adhesion compared with the unmodified surface. Activated partial thromboplastin time (APTT) of the PCU-g-PEGMA scaffold was much longer than that of the unmodified PCU scaffold. The cyto-compatibility of electrospun nanofibrous scaffolds was tested by human umbilical vein endothelial cells (HUVECs). The images of 7-day cultured cells on the scaffold surface were observed by SEM. The modified scaffolds showed high tendency to induce cell adhesion. Moreover, the cells reached out pseudopodia along the fibrous direction and formed a continuous monolayer. Hemolysis test showed that the grafted chains of PEGMA reduced blood coagulation. These results indicated that the modified electrospun nanofibrous scaffolds were potential application as artificial blood vessels. Highlights: • Electrospun nanofibrous scaffolds were successfully

  13. Surface modification of promising cerium oxide nanoparticles for nanomedicine applications

    KAUST Repository

    Nanda, Himansu Sekhar

    2016-11-14

    Cerium oxide nanoparticles (CNPs) or nanoceria have emerged as a potential nanomedicine for the treatment of several diseases such as cancer. CNPs have a natural tendency to aggregate or agglomerate in their bare state, which leads to sedimentation in a biological environment. Since the natural biological environment is essentially aqueous, nanoparticle surface modification using suitable biocompatible hydrophilic chemical moieties is highly desirable to create effective aqueous dispersions. In this report, (6-{2-[2-(2-methoxy-ethoxy)-ethoxy]-ethoxy}-hexyl)triethoxysilane was used as a functional, biocompatible organosilane to modify the surface of CNPs to produce promising nanoparticles which open substantial therapeutic avenues. The surface modified nanoparticles were produced in situ via an ammonia-induced ethylene glycol-assisted precipitation method and were characterized using complimentary characterization techniques. The interaction between the functional moiety and the nanoparticle was studied using powerful cross polarization/magic angle sample spinning solid state nuclear magnetic resonance spectroscopy. The surface-modified nanoparticles were extremely small and demonstrated a significant improvement in aqueous dispersibility. Moreover, the existence of a strong ionic coordination between the functional moiety and the surface of the nanoparticle was realised, indicating that the surface modified nanoceria are stable and that the nanoparticles should demonstrate an enhanced circulation time in a biological environment. The surface modification approach should be promising for the production of CNPs for nanomedicine applications. © The Royal Society of Chemistry.

  14. Surface Modification and Surface - Subsurface Exchange Processes on Europa

    Science.gov (United States)

    Phillips, C. B.; Molaro, J.; Hand, K. P.

    2017-12-01

    The surface of Jupiter's moon Europa is modified by exogenic processes such as sputtering, gardening, radiolysis, sulfur ion implantation, and thermal processing, as well as endogenic processes including tidal shaking, mass wasting, and the effects of subsurface tectonic and perhaps cryovolcanic activity. New materials are created or deposited on the surface (radiolysis, micrometeorite impacts, sulfur ion implantation, cryovolcanic plume deposits), modified in place (thermal segregation, sintering), transported either vertically or horizontally (sputtering, gardening, mass wasting, tectonic and cryovolcanic activity), or lost from Europa completely (sputtering, plumes, larger impacts). Some of these processes vary spatially, as visible in Europa's leading-trailing hemisphere brightness asymmetry. Endogenic geologic processes also vary spatially, depending on terrain type. The surface can be classified into general landform categories that include tectonic features (ridges, bands, cracks); disrupted "chaos-type" terrain (chaos blocks, matrix, domes, pits, spots); and impact craters (simple, complex, multi-ring). The spatial distribution of these terrain types is relatively random, with some differences in apex-antiapex cratering rates and latitudinal variation in chaos vs. tectonic features. In this work, we extrapolate surface processes and rates from the top meter of the surface in conjunction with global estimates of transport and resurfacing rates. We combine near-surface modification with an estimate of surface-subsurface (and vice versa) transport rates for various geologic terrains based on an average of proposed formation mechanisms, and a spatial distribution of each landform type over Europa's surface area. Understanding the rates and mass balance for each of these processes, as well as their spatial and temporal variability, allows us to estimate surface - subsurface exchange rates over the average surface age ( 50myr) of Europa. Quantifying the timescale

  15. Corrosion and surface modification on biocompatible metals: A review.

    Science.gov (United States)

    Asri, R I M; Harun, W S W; Samykano, M; Lah, N A C; Ghani, S A C; Tarlochan, F; Raza, M R

    2017-08-01

    Corrosion prevention in biomaterials has become crucial particularly to overcome inflammation and allergic reactions caused by the biomaterials' implants towards the human body. When these metal implants contacted with fluidic environments such as bloodstream and tissue of the body, most of them became mutually highly antagonistic and subsequently promotes corrosion. Biocompatible implants are typically made up of metallic, ceramic, composite and polymers. The present paper specifically focuses on biocompatible metals which favorably used as implants such as 316L stainless steel, cobalt-chromium-molybdenum, pure titanium and titanium-based alloys. This article also takes a close look at the effect of corrosion towards the implant and human body and the mechanism to improve it. Due to this corrosion delinquent, several surface modification techniques have been used to improve the corrosion behavior of biocompatible metals such as deposition of the coating, development of passivation oxide layer and ion beam surface modification. Apart from that, surface texturing methods such as plasma spraying, chemical etching, blasting, electropolishing, and laser treatment which used to improve corrosion behavior are also discussed in detail. Introduction of surface modifications to biocompatible metals is considered as a "best solution" so far to enhanced corrosion resistance performance; besides achieving superior biocompatibility and promoting osseointegration of biocompatible metals and alloys. Copyright © 2017 Elsevier B.V. All rights reserved.

  16. MODIFICATION OF SURFACE KONDENSITSIONNYH AEROSOLS WELDING AND METALLURGICHESKIH PRODUCTIONS

    Directory of Open Access Journals (Sweden)

    A. A. Ennan

    2016-04-01

    Full Text Available Chemical modification of surface kondensitsionnyh aerosols (KA which formation when heat treatment metals (process of weld, foundry processes with application chlorosilanes are suggested. Adsorbtion vapor of water on modification powders KA decreases and changes in varies from modifier and conditions modification are setted.

  17. Induction of surface modification of polytetrafluoroethylene with proton ion beams

    Energy Technology Data Exchange (ETDEWEB)

    Noh, I. S.; Kim, H. R.; Choi, Y. J.; Park, H. S. [Seoul National Univ. of Technology, Seoul (Korea, Republic of)

    2007-04-15

    Cardiovascular disease is one of the leading causes of the death in the USA and developed countries. More than 570,000 artery bypass graft surgeries per USA are performed each year, though percutaneous devices have abounded in extreme cases. Based on the surgery follow-ups, large diameter expanded polytetrafluoroethylene (ePTFE) (>5 mm) are clinically employed with good results but its clinical applications in smaller vessels is still problematic due to thrombosis and neointima formation. Achievement of high patency grafts has been to some extent achieved by numerous methods of surface modification techniques, but its results are less than its initial hopes. As examples, endothelial cells coated on the luminal surface of ePTFE has demonstrated limited success after recirculation. Surface modifications of PTFE film with either argon ion beam or UV light from Xe-excimer lamp were reported to increase its interaction with vascular endothelial cell. Surface modification of poly(lactide-co-glycolide)[PLGA] is also very important in tissue engineering, in where induction of its initial high cellular adhesion and spreading is a critical step for development of tissue engineering medical products. We previously reported tissue engineering of the hybrid ePTFE scaffold by seeding smooth muscle cells and subsequently evaluation of its tissue regeneration behaviors and stabilities with circulation of pulsatile flow. To improve its tissue engineering more quickly, we here performed surface modification of ePTFE and porous PLGA scaffold and evaluated its subsequent chemical and biological properties after treating its surface with low energy ion beams. The porous ePTFE was prepared in a round shape (diameter = 1 cm) and dried after organic solvent extraction for ion beam treatment. Another porous PLGA layers (d = 1 cm, t = 1 cm with approximately 92% porosity) were fabricated and treated its surface by irradiating low energy either nitrogen or argon ion beams (1 keV, 1x1015 ions

  18. Induction of surface modification of polytetrafluoroethylene with proton ion beams

    International Nuclear Information System (INIS)

    Noh, I. S.; Kim, H. R.; Choi, Y. J.; Park, H. S.

    2007-04-01

    Cardiovascular disease is one of the leading causes of the death in the USA and developed countries. More than 570,000 artery bypass graft surgeries per USA are performed each year, though percutaneous devices have abounded in extreme cases. Based on the surgery follow-ups, large diameter expanded polytetrafluoroethylene (ePTFE) (>5 mm) are clinically employed with good results but its clinical applications in smaller vessels is still problematic due to thrombosis and neointima formation. Achievement of high patency grafts has been to some extent achieved by numerous methods of surface modification techniques, but its results are less than its initial hopes. As examples, endothelial cells coated on the luminal surface of ePTFE has demonstrated limited success after recirculation. Surface modifications of PTFE film with either argon ion beam or UV light from Xe-excimer lamp were reported to increase its interaction with vascular endothelial cell. Surface modification of poly(lactide-co-glycolide)[PLGA] is also very important in tissue engineering, in where induction of its initial high cellular adhesion and spreading is a critical step for development of tissue engineering medical products. We previously reported tissue engineering of the hybrid ePTFE scaffold by seeding smooth muscle cells and subsequently evaluation of its tissue regeneration behaviors and stabilities with circulation of pulsatile flow. To improve its tissue engineering more quickly, we here performed surface modification of ePTFE and porous PLGA scaffold and evaluated its subsequent chemical and biological properties after treating its surface with low energy ion beams. The porous ePTFE was prepared in a round shape (diameter = 1 cm) and dried after organic solvent extraction for ion beam treatment. Another porous PLGA layers (d = 1 cm, t = 1 cm with approximately 92% porosity) were fabricated and treated its surface by irradiating low energy either nitrogen or argon ion beams (1 keV, 1x1015 ions

  19. Organic light emitting diode with surface modification layer

    Science.gov (United States)

    Basil, John D.; Bhandari, Abhinav; Buhay, Harry; Arbab, Mehran; Marietti, Gary J.

    2017-09-12

    An organic light emitting diode (10) includes a substrate (12) having a first surface (14) and a second surface (16), a first electrode (32), and a second electrode (38). An emissive layer (36) is located between the first electrode (32) and the second electrode (38). The organic light emitting diode (10) further includes a surface modification layer (18). The surface modification layer (18) includes a non-planar surface (30, 52).

  20. Surface Topographical Modification of Coronary Stent: A Review

    Science.gov (United States)

    Tan, C. H.; Muhamad, N.; Abdullah, M. M. A. B.

    2017-06-01

    Driven by the urge of mediating the inflammatory response from coronary stent implant to improve patency rates of the current coronary stent, concern has been focusing on reducing the risk of in-stent restenosis and thrombosis for long-term safety. Surface modification approach has been found to carry great potential due to the surface is the vital parts that act as a buffer layer between the biomaterial and the organic material like blood and vessel tissues. Nevertheless, manipulating cell response in situ using physical patterning is very complex as the exact mechanism were yet elucidated. Thus, the aim of this review is to summarise the recent efforts on modifying the surface topography of coronary stent at the micro- and nanometer scale with the purpose of inducing rapid in situ endothelialization to regenerate a healthy endothelium layer on biomaterial surface. In particular, a discussion on the surface patterns that have been investigated on cell selective behaviour together with the methods used to generate them are presented. Furthermore, the probable future work involving the surface modification of coronary stent were indicated.

  1. MILD MODIFICATION METHOD FOR THE GENERATION OF ...

    African Journals Online (AJOL)

    B. S. Chandravanshi

    2014-05-08

    bInstituto de Catálisis y Petroleoquímica, CSIC, c/Marie Curie 2, 28049 Madrid, Spain. (Received May 8, 2014; ... All samples were characterized by X-ray diffraction (XRD), inductively coupled plasma atomic emission .... Mild modification method for generation of mesoporosity in synthetic and natural mordenite. Bull. Chem.

  2. Laser surface and subsurface modification of sapphire using femtosecond pulses

    Energy Technology Data Exchange (ETDEWEB)

    Eberle, G., E-mail: eberle@iwf.mavt.ethz.ch [Institute of Machine Tools and Manufacturing, ETH Zurich, Leonhardstrasse 21, 8092 Zurich (Switzerland); Schmidt, M. [Chair of Photonic Technologies, University of Erlangen-Nuremberg, Konrad-Zuse-Strasse 3-5, 91052 Erlangen (Germany); Pude, F. [Inspire AG, Technoparkstrasse 1, 8005 Zurich (Switzerland); Wegener, K. [Institute of Machine Tools and Manufacturing, ETH Zurich, Leonhardstrasse 21, 8092 Zurich (Switzerland); Inspire AG, Technoparkstrasse 1, 8005 Zurich (Switzerland)

    2016-08-15

    Highlights: • Single and multipulse ablation threshold of aluminium oxide is determined. • Laser ablation, and in-volume modification followed by wet etching are demonstrated. • Quality following laser processing and laser-material interactions are studied. - Abstract: Two methods to process sapphire using femtosecond laser pulses are demonstrated, namely ablation (surface), and in-volume laser modification followed by wet etching (subsurface). Firstly, the single and multipulse ablation threshold is determined and compared with previous literature results. A unique application of ablation is demonstrated by modifying the entrance aperture of water jet orifices. Laser ablation exhibits advantages in terms of geometric flexibility and resolution, however, defects in the form of edge outbreaks and poor surface quality are evident. Secondly, the role of material transformation, polarisation state and formation of multi-focus structures after in-volume laser modification is investigated in order to explain their influence during the wet etching process. Laser scanning and electron microscopy as well as electron backscatter diffraction measurements supported by ion beam polishing are used to better understand quality and laser-material interactions of the two demonstrated methods of processing.

  3. One-Step Modification of Superhydrophobic Surfaces by a Mussel-Inspired Polymer Coating

    Science.gov (United States)

    Kang, Sung Min; You, Inseong; Cho, Woo Kyung; Shon, Hyun Kyong; Lee, Tae Geol; Choi, Insung S.; Karp, Jeffery M.; Lee, Haeshin

    2010-01-01

    A bio-inspired approach for superhydrophobic surface modification was investigated. Hydrophilic conversion of the superhydrophobic surface was easily achieved through this method, and the superhydrophobic-hydrophilic alternating surface was generated by the method combined with soft-lithography. The resulting patterned surface showed high water adhesion property in addition to superhydrophobic property. PMID:21031386

  4. Surface chemical modification for exceptional wear life of MEMS materials

    Directory of Open Access Journals (Sweden)

    R. Arvind Singh

    2011-12-01

    Full Text Available Micro-Electro-Mechanical-Systems (MEMS are built at micro/nano-scales. At these scales, the interfacial forces are extremely strong. These forces adversely affect the smooth operation and cause wear resulting in the drastic reduction in wear life (useful operating lifetime of actuator-based devices. In this paper, we present a surface chemical modification method that reduces friction and significantly extends the wear life of the two most popular MEMS structural materials namely, silicon and SU-8 polymer. The method includes surface chemical treatment using ethanolamine-sodium phosphate buffer, followed by coating of perfluoropolyether (PFPE nanolubricant on (i silicon coated with SU-8 thin films (500 nm and (ii MEMS process treated SU-8 thick films (50 μm. After the surface chemical modification, it was observed that the steady-state coefficient of friction of the materials reduced by 4 to 5 times and simultaneously their wear durability increased by more than three orders of magnitude (> 1000 times. The significant reduction in the friction coefficients is due to the lubrication effect of PFPE nanolubricant, while the exceptional increase in their wear life is attributed to the bonding between the -OH functional group of ethanolamine treated SU-8 thin/thick films and the -OH functional group of PFPE. The surface chemical modification method acts as a common route to enhance the performance of both silicon and SU-8 polymer. It is time-effective (process time ≤ 11 min, cost-effective and can be readily integrated into MEMS fabrication/assembly processes. It can also work for any kind of structural material from which the miniaturized devices are/can be made.

  5. Effect of surface modification and hybridization on dynamic ...

    Indian Academy of Sciences (India)

    The paper evaluates effect of fibre surface modification and hybridization on dynamic mechanical properties of Roystonea regia/epoxy composites. Surface modification involved alkali and silane treatments. Alkali treatment proved to be more effective on dynamic mechanical properties as compared to silane treatment.

  6. Reduction of Glass Surface Reflectance by Ion Beam Surface Modification

    Energy Technology Data Exchange (ETDEWEB)

    Mark Spitzer

    2011-03-11

    This is the final report for DOE contract DE-EE0000590. The purpose of this work was to determine the feasibility of the reduction of the reflection from the front of solar photovoltaic modules. Reflection accounts for a power loss of approximately 4%. A solar module having an area of one square meter with an energy conversion efficiency of 18% generates approximately 180 watts. If reflection loss can be eliminated, the power output can be increased to 187 watts. Since conventional thin-film anti-reflection coatings do not have sufficient environmental stability, we investigated the feasibility of ion beam modification of the glass surface to obtain reduction of reflectance. Our findings are generally applicable to all solar modules that use glass encapsulation, as well as commercial float glass used in windows and other applications. Ion implantation of argon, fluorine, and xenon into commercial low-iron soda lime float glass, standard float glass, and borosilicate glass was studied by implantation, annealing, and measurement of reflectance. The three ions all affected reflectance. The most significant change was obtained by argon implantation into both low-iron and standard soda-lime glass. In this way samples were formed with reflectance lower than can be obtained with a single-layer coatings of magnesium fluoride. Integrated reflectance was reduced from 4% to 1% in low-iron soda lime glass typical of the glass used in solar modules. The reduction of reflectance of borosilicate glass was not as large; however borosilicate glass is not typically used in flat plate solar modules. Unlike conventional semiconductor ion implantation doping, glass reflectance reduction was found to be tolerant to large variations in implant dose, meaning that the process does not require high dopant uniformity. Additionally, glass implantation does not require mass analysis. Simple, high current ion implantation equipment can be developed for this process; however, before the process

  7. Surface Modification and Surface - Subsurface Exchange Processes on Europa

    Science.gov (United States)

    Phillips, Cynthia B.; Molaro, Jamie; Hand, Kevin P.

    2017-10-01

    The surface of Jupiter’s moon Europa is modified by exogenic processes such as sputtering, gardening, radiolysis, sulfur ion implantation, and thermal processing, as well as endogenic processes including tidal shaking, mass wasting, and the effects of subsurface tectonic and perhaps cryovolcanic activity. New materials are created or deposited on the surface (radiolysis, micrometeorite impacts, sulfur ion implantation, cryovolcanic plume deposits), modified in place (thermal segregation, sintering), transported either vertically or horizontally (sputtering, gardening, mass wasting, tectonic and cryovolcanic activity), or lost from Europa completely (sputtering, plumes, larger impacts). Some of these processes vary spatially, as visible in Europa’s leading-trailing hemisphere brightness asymmetry.Endogenic geologic processes also vary spatially, depending on terrain type. The surface can be classified into general landform categories that include tectonic features (ridges, bands, cracks); disrupted “chaos-type” terrain (chaos blocks, matrix, domes, pits, spots); and impact craters (simple, complex, multi-ring). The spatial distribution of these terrain types is relatively random, with some differences in apex-antiapex cratering rates and latitudinal variation in chaos vs. tectonic features.In this work, we extrapolate surface processes and rates from the top meter of the surface in conjunction with global estimates of transport and resurfacing rates. We combine near-surface modification with an estimate of surface-subsurface (and vice versa) transport rates for various geologic terrains based on an average of proposed formation mechanisms, and a spatial distribution of each landform type over Europa’s surface area.Understanding the rates and mass balance for each of these processes, as well as their spatial and temporal variability, allows us to estimate surface - subsurface exchange rates over the average surface age (~50myr) of Europa. Quantifying the

  8. Surface modification using peptide functionalized bilayers

    Science.gov (United States)

    Stroumpoulis, Dimitrios

    Engineering materials that are capable of supporting cell and tissue growth is a challenging task that involves identifying and incorporating biological signals into the material surfaces or scaffolds. One approach towards bioactivity in materials is to mimic the function of the extracellular matrix (ECM) by displaying adhesion promoting oligopeptides. Supported planar bilayers (SPB) are a good platform to study molecular interactions at interfaces, since transmembrane proteins and peptides can be incorporated in a biologically relevant environment with precise control over their concentration and presentation. SPBs can be formed on flat surfaces using the Langmuir-Blodgett (LB) technique or alternatively from vesicle solutions. The fusion of vesicles with solid substrates offers simplicity and enhanced bilayer deposition rates over the LB method, whereas it can also be used with convex and enclosed surfaces. Ellipsometry and a mass transport model were used to investigate the kinetics of SPB formation on silicon dioxide surfaces from 100 nm diameter 1,2-dimyristoyl-sn-glycero-3-phosphocholine (DMPC) vesicles. For the range of concentrations studied, 0.025 to 0.380 mg/ml, a monotonic increase in the ellipsometric signal with time was observed until saturation and the adsorption rate constant was calculated. Further, a Monte Carlo model was used to simulate the SPB formation process and the computational results were successfully fit to the experimental data. Lipid vesicles displaying RGD peptide amphiphiles were fused onto glass coverslips to control the ability of these surfaces to support cell adhesion and growth. Cell adhesion was prevented on phosphatidylcholine bilayers in the absence of RGD, whereas cells adhered and spread in the presence of accessible RGD amphiphiles. This specific interaction between cells and RGD peptides was further explored in a concentration dependent fashion by creating a surface composition array using a microfluidic device. For the

  9. Superhydrophobic surfaces fabricated by surface modification of alumina particles

    Science.gov (United States)

    Richard, Edna; Aruna, S. T.; Basu, Bharathibai J.

    2012-10-01

    The fabrication of superhydrophobic surfaces has attracted intense interest because of their widespread potential applications in various industrial fields. Recently, some attempts have been carried out to prepare superhydrophobic surfaces using metal oxide nanoparticles. In the present work, superhydrophobic surfaces were fabricated with low surface energy material on alumina particles with different sizes. It was found that particle size of alumina is an important factor in achieving stable superhydrophobic surface. It was possible to obtain alumina surface with water contact angle (WCA) of 156° and a sliding angle of Superhydrophobicity of the modified alumina is attributed to the combined effect of the micro-nanostructure and low surface energy of fatty acid on the surface. The surface morphology of the alumina powder and coatings was determined by FESEM. The stability of the coatings was assessed by conducting water immersion test. Effect of heat treatment on WCA of the coating was also studied. The transition of alumina from hydrophilic to superhydrophobic state was explained using Wenzel and Cassie models. The method is shown to have potential application for creating superhydrophobic surface on cotton fabrics.

  10. Laser surface modification of boronickelized medium carbon steel

    Science.gov (United States)

    Bartkowska, Aneta; Pertek, Aleksandra; Kulka, Michał; Klimek, Leszek

    2015-11-01

    A two-step process was applied to produce the multicomponent boride layers. Boronickelizing consisted of nickel plating and diffusion boriding. Two different methods of heat treatment of boronickelized C45 steel were used: a typical through-hardening, and a laser surface modification with remelting. Microstructure and some mechanical properties of these layers were examined. Microstructural characterization was studied using optical microscope, Scanning Electron Microscope, energy-dispersive X-ray microanalysis, Electron Back-Scatter Diffraction and X-ray diffraction. The laser modification improved wear resistance, cohesion as well as low-cycle fatigue of the boronickelized layer. Compressive stresses, occurring after laser remelting, could be the reason for the advantageous mechanical behavior of the layer.

  11. One-pot Synthesis and Surface Modification of Fe3O4 Nanoparticles Using Polyvinyl Alcohol by Coprecipitation and Ultrasonication Methods

    Science.gov (United States)

    Nugraha, Aditya D.; Wulandari, Ika O.; Hutami Rahayu, L. B.; Riva’i, Imam; Santojo, D. J. Djoko H.; Sabarudin, Akhmad

    2018-01-01

    Among the various substances developed through nanoparticles, iron oxide (Fe3O4) nanoparticle is one of the substances that have been widely used in various fields such as industry, agriculture, biotechnology and biomedicine. The synthesis of Fe3O4 nanoparticle can be carried out by two methods, consist of chemical and mechanical synthesis methods. Coprecipitation is one of the most commonly used methods for chemical synthesis. Fe3O4 compounds are easily oxidized because they are amphoteric. To avoid the continuous oxidation process, chemical modification process should be carried out with the addition of a solution of polyvinyl alcohol (PVA). In this study, PVA-coated Fe3O4 nanoparticles were synthesized by in-situ coprecipitation and ultrasonication methods through direct mixing (one-pot synthesis) of the iron (II) chloride tetrahydrate (FeCl2.4H2O), iron (III) chloride hexahydrate (FeCl3.6H2O), and PVA under alkaline condition. The effects of addition amount of NH3solution (by adjusting its flow rate using automated syringe pump) and PVA concentration were gently studied. Interaction of PVA with Fe3O4 nanoparticle was identified by infrared spectroscopy whereas lattice parameters and crystallite sizes of the synthesized Fe3O4 nanoparticles and PVA-coated Fe3O4 nanoparticles were assessed by X-ray diffraction (XRD).

  12. Silane surface modification for improved bioadhesion of esophageal stents

    Science.gov (United States)

    Karakoy, Mert; Gultepe, Evin; Pandey, Shivendra; Khashab, Mouen A.; Gracias, David H.

    2014-01-01

    Stent migration occurs in 10-40% of patients who undergo placement of esophageal stents, with higher migration rates seen in those treated for benign esophageal disorders. This remains a major drawback of esophageal stent therapy. In this paper, we propose a new surface modification method to increase the adhesion between self-expandable metallic stents (SEMS) and tissue while preserving their removability. Taking advantage of the well-known affinity between epoxide and amine terminated silane coupling agents with amine and carboxyl groups that are abundant in proteins and related molecules in the human body; we modified the surfaces of silicone coated esophageal SEMS with these adhesive self-assembled monolayers (SAMs). We utilized vapor phase silanization to modify the surfaces of different substrates including PDMS strips and SEMS, and measured the force required to slide these substrates on a tissue piece. Our results suggest that surface modification of esophageal SEMS via covalent attachment of protein-binding coupling agents improves adhesion to tissue and could offer a solution to reduce SEMS migration while preserving their removability. PMID:25663731

  13. Tribological effects of polymer surface modification through plastic ...

    Indian Academy of Sciences (India)

    The efficacy of using polymers in cylindrical applications depends closely on its surface friction and wear characteristics. In this regard, a surface modification technique through plastic deformation has been implemented. Roller burnishing is commonly used to improve the surface quality of non-ferrous surfaces, but no work ...

  14. Tribological effects of polymer surface modification through plastic ...

    Indian Academy of Sciences (India)

    Administrator

    Abstract. The efficacy of using polymers in cylindrical applications depends closely on its surface friction and wear characteristics. In this regard, a surface modification technique through plastic deformation has been implemented. Roller burnishing is commonly used to improve the surface quality of non-ferrous surfaces, but ...

  15. Directly thiolated modification onto the surface of detonation nanodiamonds.

    Science.gov (United States)

    Hsu, Ming-Hua; Chuang, Hong; Cheng, Fong-Yu; Huang, Ying-Pei; Han, Chien-Chung; Chen, Jiun-Yu; Huang, Su-Chin; Chen, Jen-Kun; Wu, Dian-Syue; Chu, Hsueh-Liang; Chang, Chia-Ching

    2014-05-28

    An efficient method for modifying the surface of detonation nanodiamonds (5 and 100 nm) with thiol groups (-SH) by using an organic chemistry strategy is presented herein. Thiolated nanodiamonds were characterized by spectroscopic techniques, and the atomic percentage of sulfur was analyzed by elemental analysis and X-ray photoelectron spectroscopy. The conjugation between thiolated nanodiamonds and gold nanoparticles was elucidated by transmission electron microscopy and UV-vis spectrometry. Moreover, the material did not show significant cytotoxicity to the human lung carcinoma cell line and may prospectively be applied in bioconjugated technology. The new method that we elucidated may significantly improve the approach to surface modification of detonation nanodiamonds and build up a new platform for the application of nanodiamonds.

  16. Surface Modification of PDMS and Plastics with Zwitterionic Polymers.

    Science.gov (United States)

    Tanaka, Mutsuo; Kurosawa, Shigeru

    2017-07-01

    Surface modification of PDMS, polycarbonate, and acrylic resin was examined using various methacryl polymers bearing sulfobetaine, phosphoryl choline, and oligoethylene glycol units. We have found that zwitterionic polymers are adsorbed on the PDMS surface treated with plasma. The surface of PDMS is stable to keep high hydrophilicity after a month of the modification. On the other hand, one of sulfobetaine polymers showed distinguished adsorption behavior in the case of polycarbonate surface treated with plasma. Suppression effect for nonspecific adsorption of BSA was evaluated using polycarbonate and acrylic resin modified with the polymers. The modified surfaces showed suppression effect for nonspecific adsorption of BSA compared with the surface only treated with plasma.

  17. Quantitative Analysis and Efficient Surface Modification of Silica Nanoparticles

    Directory of Open Access Journals (Sweden)

    Hak-Sung Jung

    2012-01-01

    Full Text Available Aminofunctional trialkoxysilanes such as aminopropyltrimethoxysilane (APTMS and (3-trimethoxysilylpropyldiethylenetriamine (DETAS were employed as a surface modification molecule for generating monolayer modification on the surface of silica (SiO2 nanoparticles. We were able to quantitatively analyze the number of amine functional groups on the modified SiO2 nanoparticles by acid-base back titration method and determine the effective number of amine functional groups for the successive chemical reaction by absorption measurements after treating with fluorescent rhodamine B isothiocyanate (RITC molecules. The numbers of amine sites measured by back titration were 2.7 and 7.7 ea/nm2 for SiO2-APTMS and SiO2-DETAS, respectively, while the numbers of effective amine sites measured by absorption calibration were about one fifth of the total amine sites, namely, 0.44 and 1.3 ea/nm2 for SiO2-APTMS(RITC and SiO2-DETAS(RITC, respectively. Furthermore, it was confirmed that the reactivity of amino groups on the surface-modified silica nanoparticles could be maintained in ethanol for more than 1.5 months without showing any significant differences in the reactivity.

  18. Study of the surface modification with oleic acid of nanosized HfO{sub 2} synthesized by the polymerized complex derived sol-gel method

    Energy Technology Data Exchange (ETDEWEB)

    Ramos-Gonzalez, R., E-mail: rramos.phd@gmail.com [Centro de Investigacion en Quimica Aplicada, Blvd. Enrique Reyna Hermosillo No. 140, Saltillo, Coahuila 25250 (Mexico); Garcia-Cerda, L.A. [Centro de Investigacion en Quimica Aplicada, Blvd. Enrique Reyna Hermosillo No. 140, Saltillo, Coahuila 25250 (Mexico); Quevedo-Lopez, M.A. [University of Texas at Dallas, 800 West Campbell Road, Richardson, TX 75080-3021 (United States)

    2012-06-01

    The synthesis of nanosized hafnium oxide by the polymerized complex derived sol-gel method is reported. The structural and morphological characterization of the HfO{sub 2} was carried out by X-ray diffraction and scanning electron microscopy. The surface of hafnium oxide nanoparticles was modified by capping with oleic acid. The nanoparticle surface area was measured by the gas adsorption technique in order to determine the minimal amount of oleic acid needed to obtain a uniform coverage of the hafnium oxide. The existence of organic layer can be confirmed by Fourier transform spectroscopy, solid state nuclear magnetic resonance spectroscopy, thermal gravimetric analysis and transmission electron microscopy. The FTIR and solid state NMR results reveal that oleic acid is chemisorbed as a carboxylate onto the HfO{sub 2} nanoparticle surface and confirm the formation of a monomolecular layer of oleic acid surrounding the HfO{sub 2}. The cover density of oleic acid on the HfO{sub 2} increases with the amount of oleic acid used to modify the nanoparticles and the surface properties of HfO{sub 2} nanoparticles modified with oleic acid change from hydrophilic to hydrophobic.

  19. Surface modification of titanium with lasers

    NARCIS (Netherlands)

    Kloosterman, Annejan Bernard

    1998-01-01

    In engineering applications the material demands often differ between bulk and surface. As a matter of fact, it is beneficial to select two different materials with the appropriate properties, for the bulk and the surface, respectively. Therefore, substantial effort has been devoted to the surface

  20. Effects of surface modification of Nd-Fe-B powders using parylene C by CVDP method on the properties of anisotropic bonded Nd–Fe–B magnets

    Energy Technology Data Exchange (ETDEWEB)

    Ma, Bin; Sun, Aizhi, E-mail: sunaizhi@126.com; Lu, Zhenwen; Cheng, Chuan; Xu, Chen

    2016-10-15

    This paper presents effects of surface modification of Nd–Fe–B powders using parylene C by means of chemical vapor deposition polymerization (CVDP) on the properties of anisotropic bonded Nd–Fe–B magnets. It can be well verified from SEM images and EDS analysis that the surface of Nd–Fe–B powder is coated with thin parylene C films. The maximum energy product ((BH)max), degree of alignment (DOA), actual density and corrosion resistance of parylene Nd–Fe–B magnets prepared at room temperature are much higher than that of non-parylene Nd–Fe–B magnets. (BH)max, DOA and actual density of parylene Nd–Fe–B magnets (70 kJ/m{sup 3}, 0.342, 5.82 g/cm{sup 3}) prepared at room temperature under 578 MPa are improved by 18.6%, 4.6%, 2.1% and 27.3%, 29.1%, 7.8% compared with non-parylene Nd‐Fe‐B magnets prepared at 140 °C (59 kJ/m{sup 3}, 0327, 5.70 g/cm{sup 3}) and room temperature (55 kJ/m{sup 3}, 0.265, 5.40 g/cm{sup 3}), respectively. Additional, the improvement of actual density and the room temperature process also solve problems such as powders’ sticking wall, non-uniform powder filling, non-uniform magnetic properties, seriously mould damage, short life cycle of mould and so on, which exists during warm compaction process. Parylene Nd–Fe–B magnets have better corrosion resistance and worse mechanical properties than that of non-parylene Nd–Fe–B magnets. The reason for the improvement of magnetic properties and actual density is the low friction cofficient of parylene C films, which results in lower frictional resistance and better lubricating property of parylene Nd–Fe–B powders. - Highlights: • Parylene Nd–Fe–B magnets prepared at room temperature show higher (BH)max and DOA. • Actual density of parylene Nd–Fe–B magnet is improved greatly. • Problems such as powders’ sticking wall, mould damage and so on are solved. • Parylene NdFeB magnets have better corrosion resistance. • Low friction cofficient of

  1. Green aqueous surface modification of polypropylene for novel polymer nanocomposites.

    Science.gov (United States)

    Thakur, Vijay Kumar; Vennerberg, Danny; Kessler, Michael R

    2014-06-25

    Polypropylene is one of the most widely used commercial commodity polymers; among many other applications, it is used for electronic and structural applications. Despite its commercial importance, the hydrophobic nature of polypropylene limits its successful application in some fields, in particular for the preparation of polymer nanocomposites. Here, a facile, plasma-assisted, biomimetic, environmentally friendly method was developed to enhance the interfacial interactions in polymer nanocomposites by modifying the surface of polypropylene. Plasma treated polypropylene was surface-modified with polydopamine (PDA) in an aqueous medium without employing other chemicals. The surface modification strategy used here was based on the easy self-polymerization and strong adhesion characteristics of dopamine (DA) under ambient laboratory conditions. The changes in surface characteristics of polypropylene were investigated using FTIR, TGA, and Raman spectroscopy. Subsequently, the surface modified polypropylene was used as the matrix to prepare SiO2-reinforced polymer nanocomposites. These nanocomposites demonstrated superior properties compared to nanocomposites prepared using pristine polypropylene. This simple, environmentally friendly, green method of modifying polypropylene indicated that polydopamine-functionalized polypropylene is a promising material for various high-performance applications.

  2. Modification of polycarbonate surface in oxidizing plasma

    Science.gov (United States)

    Ovtsyn, A. A.; Smirnov, S. A.; Shikova, T. G.; Kholodkov, I. V.

    2017-11-01

    The properties of the surface of the film polycarbonate Lexan 8010 were experimentally studied after treatment in a DC discharge plasma in oxygen and air at pressures of 50-300 Pa and a discharge current of 80 mA. The contact angles of wetting and surface energies are measured. The topography of the surface was investigated by atomic force microscopy. The chemical composition of the surface was determined from the FT-IR spectroscopy data in the variant of total internal reflection, as well as X-ray photoelectron spectroscopy. Treatment in the oxidizing plasma leads to a change in morphology (average roughness increases), an increase in the surface energy, and the concentration of oxygen-containing groups (hydroxyl groups, carbonyl groups in ketones or aldehydes and in oxyketones) on the surface of the polymer. Possible reasons for the difference in surface properties of polymer under the action of oxygen and air plasma on it are discussed.

  3. The influence of surface modification, coating agents and pH value of aqueous solutions on physical properties of magnetite nanoparticles investigated by ESR method

    Science.gov (United States)

    Dobosz, Bernadeta; Krzyminiewski, Ryszard; Kurczewska, Joanna; Schroeder, Grzegorz

    2017-05-01

    The article presents the results of electron spin resonance (ESR) studies for aqueous solutions of functionalized superparamagnetic iron(II,III) oxide nanoparticles. The samples studied differed in type of organic ligands at the magnetite surface, type of coating agent and pH value of aqueous solutions. The ESR spectra of the samples were obtained at room temperature and at 230 K. The field cooling (FC) experiment was performed for selected samples, and the effective anisotropy field (HK2) and the first order magnetocrystalline anisotropy constant (K1) was calculated. The process of the nanoparticles diffusion in different environments (human blood, human serum) forced by an inhomogeneous magnetic field was monitored and their interactions with different solvents have been discussed. It has been shown that ESR method is useful to observe the impact of organic ligands at the magnetite surface, type of coating agent and pH value of aqueous solutions on the properties of iron(II,III) oxide nanoparticles.

  4. Surface Modification on Acoustic Wave Biosensors for Enhanced Specificity

    Directory of Open Access Journals (Sweden)

    Nathan D. Gallant

    2012-09-01

    Full Text Available Changes in mass loading on the surface of acoustic biosensors result in output frequency shifts which provide precise measurements of analytes. Therefore, to detect a particular biomarker, the sensor delay path must be judiciously designed to maximize sensitivity and specificity. B-cell lymphoma 2 protein (Bcl-2 found in urine is under investigation as a biomarker for non-invasive early detection of ovarian cancer. In this study, surface chemistry and biofunctionalization approaches were evaluated for their effectiveness in presenting antibodies for Bcl-2 capture while minimizing non-specific protein adsorption. The optimal combination of sequentially adsorbing protein A/G, anti-Bcl-2 IgG and Pluronic F127 onto a hydrophobic surface provided the greatest signal-to-noise ratio and enabled the reliable detection of Bcl-2 concentrations below that previously identified for early stage ovarian cancer as characterized by a modified ELISA method. Finally, the optimal surface modification was applied to a prototype acoustic device and the frequency shift for a range of Bcl-2 concentration was quantified to demonstrate the effectiveness in surface acoustic wave (SAW-based detection applications. The surface functionalization approaches demonstrated here to specifically and sensitively detect Bcl-2 in a working ultrasonic MEMS biosensor prototype can easily be modified to detect additional biomarkers and enhance other acoustic biosensors.

  5. Surface modification and electrochemical behaviour of undoped nanodiamonds

    International Nuclear Information System (INIS)

    Zang Jianbing; Wang Yanhui; Bian Linyan; Zhang Jinhui; Meng Fanwei; Zhao Yuling; Ren Shubin; Qu Xuanhui

    2012-01-01

    Surface modifications of undoped nanodiamond (ND) particles were carried out through different annealing treatments. The methods of Fourier transform infrared spectroscopy, Raman spectroscopy, and transmission electron microscopy were used to characterize the ND surface before and after the annealing process. The electrochemical properties of the modified ND powders in aqueous solution were investigated with Fe(CN) 6 3−/4− as a redox probe. When the annealing temperature was below 850 °C, vacuum annealing removed parts of the oxygen-containing surface functionalities from the ND surface and produced more sp 2 carbon atoms in the shell. The charge transfer of the Fe(CN) 6 3−/4− redox couple decreased with increasing annealing temperature. Re-annealing in air restored the original surface conditions: few sp 2 -bonded carbon atoms and similar surface functionalities, and thus the electrochemical activity. When ND was annealed in vacuum at 900–1100 °C, more serious graphitization produced a continuous fullerenic shell wrapped around a diamond core, which had a high conductivity and electrochemical activity. This provides a novel nanoparticle with high conductivity and high stability for electrochemical applications.

  6. Surface modification and preparation techniques for textile materials

    CSIR Research Space (South Africa)

    Jacob John, Maya

    2009-01-01

    Full Text Available as it improves various properties – such as softness, dyeability, absorbance and wettability. In this chapter, the most commonly used surface modification techniques, ranging from plasma treatment to nanocoatings, for both natural and synthetic fibres have been...

  7. Preparation of poly(2-chloroaniline) membrane and plasma surface modification

    International Nuclear Information System (INIS)

    Kir, E.; Oksuz, L.; Helhel, S.

    2006-01-01

    P2ClAn membranes were obtained from chemically synthesized poly(2-chloroaniline) (P2ClAn) by casting method. These membranes were cast from dimethyl formamide (DMF) and were in the undoped state. P2ClAn membranes were characterized by Fourier infrared spectroscopy and scanning electron microscopy. Measurements of water content capacity, membrane thickness and ion-exchange capacity of the cast membranes were carried out. P2ClAn membranes were treated by electron cylotron resonance (ECR) plasma for surface modification. Plasma treatment has been successfully utilized for improving the surface properties of P2ClAn membranes such as increasing pore diameters and number of pores for better anion or molecule transportation

  8. Surface modification on PMMA: PVDF polyblend: hardening under ...

    Indian Academy of Sciences (India)

    The influence of chemical environment on polymers include the surface alteration as well as other deep modifications in surface layers. The surface hardening, as an effect of organic liquids on poly(methyl methacrylate): poly(vinylidene fluoride) (PMMA: PVDF), which is one of the few known miscible blends, has been ...

  9. Investigation of surface halide modification of nitrile butadiene rubber

    Science.gov (United States)

    Sukhareva, K. V.; Mikhailov, I. A.; Andriasyan, Yu O.; Mastalygina, E. E.; Popov, A. A.

    2017-12-01

    The investigation is devoted to the novel technology of surface halide modification of rubber samples based on nitrile butadiene rubber (NBR). 1,1,2-trifluoro-1,2,2-trichlorethane was used as halide modifier. The developed technology is characterized by production stages reduction to one by means of treating the rubber compound with a halide modifier. The surface halide modification of compounds based on nitrile butadiene rubber (NBR) was determined to result in increase of resistance to thermal oxidation and aggressive media. The conducted research revealed the influence of modification time on chemical resistance and physical-mechanical properties of rubbers under investigation.

  10. The influence of surface modification, coating agents and pH value of aqueous solutions on physical properties of magnetite nanoparticles investigated by ESR method

    Energy Technology Data Exchange (ETDEWEB)

    Dobosz, Bernadeta, E-mail: benia@amu.edu.pl [Medical Physics Division, Faculty of Physics, Adam Mickiewicz University, Umultowska 85, 61-614 Poznań (Poland); Krzyminiewski, Ryszard [Medical Physics Division, Faculty of Physics, Adam Mickiewicz University, Umultowska 85, 61-614 Poznań (Poland); Kurczewska, Joanna; Schroeder, Grzegorz [Faculty of Chemistry, Adam Mickiewicz University, Umultowska 89B, 61-614 Poznań (Poland)

    2017-05-01

    The article presents the results of electron spin resonance (ESR) studies for aqueous solutions of functionalized superparamagnetic iron(II,III) oxide nanoparticles. The samples studied differed in type of organic ligands at the magnetite surface, type of coating agent and pH value of aqueous solutions. The ESR spectra of the samples were obtained at room temperature and at 230 K. The field cooling (FC) experiment was performed for selected samples, and the effective anisotropy field (H{sub K2}) and the first order magnetocrystalline anisotropy constant (K{sub 1}) was calculated. The process of the nanoparticles diffusion in different environments (human blood, human serum) forced by an inhomogeneous magnetic field was monitored and their interactions with different solvents have been discussed. It has been shown that ESR method is useful to observe the impact of organic ligands at the magnetite surface, type of coating agent and pH value of aqueous solutions on the properties of iron(II,III) oxide nanoparticles. - Highlights: • The influence of different organic ligands, coatings and pH values of aqueous solutions on the physical properties of the magnetite nanoparticles studied by ESR method. • Nanoparticles diffusion forced by inhomogeneous magnetic field monitored by ESR and explained. • A narrow line separated in ESR spectra by CREM. • The influence of different coatings and pH values of aqueous solutions on ESR spectra of TEMPO attached to the magnetite core.

  11. Effects of aluminium surface morphology and chemical modification on wettability

    DEFF Research Database (Denmark)

    Rahimi, Maral; Fojan, Peter; Gurevich, Leonid

    2014-01-01

    of a monolayer of fluorinated silane, and a combination of those. The effect of these surface modification techniques on roughness and wettability of the aluminium surfaces was elucidated by ellipsometry, contact angle measurements and atomic force microscopy. We demonstrated that by employing different types...... of surface modifications the contact angle of water droplets on aluminium samples can be varied from 12° to more than 120°. A crossover from Cassie–Baxter to Wenzel regime upon changing the surface roughness was also observed....

  12. Surface modification of tribological components in transportation

    Energy Technology Data Exchange (ETDEWEB)

    Fenske, G.R.

    1992-11-01

    This paper reviews a number of programs funded through the Engineered Tribological Interfaces (ETI) Task area of the Tribology Program that utilize energetic beams of atoms to enhance the mechanical and microstructural properties of near-surface regions to improve the tribological performance of critical components. The processes used in these programs include techniques based on chemical vapor deposition, physical vapor deposition, and ion implantation. A common feature of these techniques is their ability to produce dense and adherent modified surfaces without need for subsequent grinding/polishing treatments. Another feature of these techniques is their ability to introduce a wide range of elements into near-surface regions.

  13. Preparation, surface modification and microwave characterization of magnetic iron fibers

    Energy Technology Data Exchange (ETDEWEB)

    Nie Yan [Department of Electronic Science and Technology, Huazhong University of Science and Technology, Wuhan 430074 (China)]. E-mail: nieyanko@yahoo.com.cn; He Huahui [Department of Electronic Science and Technology, Huazhong University of Science and Technology, Wuhan 430074 (China); Zhao Zhenshen [Department of Electronic Science and Technology, Huazhong University of Science and Technology, Wuhan 430074 (China); Gong Rongzhou [Department of Electronic Science and Technology, Huazhong University of Science and Technology, Wuhan 430074 (China); Yu Hongbin [Department of optoelectronic Engineering, Huazhong University of Science and Technology, Wuhan 430074 (China)

    2006-11-15

    In this paper, magnetic iron fibers of 3-10 {mu}m diameter and an adjustable aspect ratio were synthesized successfully by a method involving pyrolysis of carbonyl under a magnetic field. A surface modification technology was also investigated. The electromagnetic parameters of the iron-fiber-wax composites were measured using the transmission/reflection coaxial line method in the microwave frequency range of 2-18 GHz. The results show that the prepared iron-fiber-wax composites exhibit high magnetic loss that can be further improved after phosphating. On the other hand, the complex permittivity was significantly decreased after phosphating. As a result, this kind of iron fiber may be useful for thin and lightweight radar-absorbing materials.

  14. Ion-induced surface modification of alloys

    International Nuclear Information System (INIS)

    Wiedersich, H.

    1983-11-01

    In addition to the accumulation of the implanted species, a considerable number of processes can affect the composition of an alloy in the surface region during ion bombardment. Collisions of energetic ions with atoms of the alloy induce local rearrangement of atoms by displacements, replacement sequences and by spontaneous migration and recombination of defects within cascades. Point defects form clusters, voids, dislocation loops and networks. Preferential sputtering of elements changes the composition of the surface. At temperatures sufficient for thermal migration of point defects, radiation-enhanced diffusion promotes alloy component redistribution within and beyond the damage layer. Fluxes of interstitials and vacancies toward the surface and into the interior of the target induce fluxes of alloying elements leading to depth-dependent compositional changes. Moreover, Gibbsian surface segregation may affect the preferential loss of alloy components by sputtering when the kinetics of equilibration of the surface composition becomes competitive with the sputtering rate. Temperature, time, current density and ion energy can be used to influence the individual processes contributing to compositional changes and, thus, produce a rich variety of composition profiles near surfaces. 42 references

  15. Surface modifications by field induced diffusion.

    Directory of Open Access Journals (Sweden)

    Martin Olsen

    Full Text Available By applying a voltage pulse to a scanning tunneling microscope tip the surface under the tip will be modified. We have in this paper taken a closer look at the model of electric field induced surface diffusion of adatoms including the van der Waals force as a contribution in formations of a mound on a surface. The dipole moment of an adatom is the sum of the surface induced dipole moment (which is constant and the dipole moment due to electric field polarisation which depends on the strength and polarity of the electric field. The electric field is analytically modelled by a point charge over an infinite conducting flat surface. From this we calculate the force that cause adatoms to migrate. The calculated force is small for voltage used, typical 1 pN, but due to thermal vibration adatoms are hopping on the surface and even a small net force can be significant in the drift of adatoms. In this way we obtain a novel formula for a polarity dependent threshold voltage for mound formation on the surface for positive tip. Knowing the voltage of the pulse we then can calculate the radius of the formed mound. A threshold electric field for mound formation of about 2 V/nm is calculated. In addition, we found that van der Waals force is of importance for shorter distances and its contribution to the radial force on the adatoms has to be considered for distances smaller than 1.5 nm for commonly used voltages.

  16. Effects of some chemical surface modifications on resin zirconia adhesion.

    Science.gov (United States)

    Liu, Dan; Tsoi, James Kit-Hon; Matinlinna, Jukka Pekka; Wong, Hai Ming

    2015-06-01

    To evaluate the effects of various chemical surface modifications on adhesion between zirconia and resin adhesive. Pre-sintered zirconia discs were sectioned from commercial cylindrical blocks and polished with abrasive papers under running tap water. All the discs were randomly divided into five study groups according to the methods of surface treatment, including: the control group (fully sintered, without any modification), group S (fully sintered and sandblasted with silica coated alumina particles), group HN (fully sintered and etched with a blend of mineral acid solution at 100 °C for 25 min), group HF (fully sintered and etched with 48% hydrofluoric acid solution at 100 °C for 25 min), and group Si (coated with silica particles and then fully sintered). The mean value of surface roughness was evaluated before further treatment. Resin stubs (3.6mm in diameter and 3mm in height) were adhered and light cured on each zirconia disc after the application of a silane coupling agent. In each group, all the samples were further divided into three subgroups with each n=12, one for the measurement of initial adhesion strength (shear bond) value and the other two were tested after thermal cycling for 10,000 and 20,000 cycles, respectively. The results were analyzed with two-way ANOVA and Turkey HSD (pzirconia surface crystallinity. The morphological appearance of zirconia surface after surface treatment was observed with SEM. The control group showed the lowest initial shear bond strength (SBS) value (16.8 ± 2.4 MPa) and did not survive the aging treatments. All the investigated surface treatments improved resin zirconia bond strength significantly, the group S displaying the highest initial value of 25.1 ± 2.7 MPa. However, the highest resistance to the aging effects of thermal cycling was found in group Si. It was further shown in the XRD examination that only the grit-blasting caused the crystalline transformation from tetragonal phase to monoclinic phase (T

  17. Material surface modification for first wall protection

    International Nuclear Information System (INIS)

    Davis, M.J.

    1979-01-01

    The elements and strategy of a program to develop low Z surfaces for tokamak reactors is described. The development of low Z coated limiters is selected as an interim goal. Candidate materials were selected from the elements: Be, B, Al, Ti, V, C, O, N and their compounds. The effect of low energy erosion on surface morphology is shown for Be, TiC and VBe 12 . The tradeoffs in coating design are described. Stress analysis results for TiB 2 coated POCO graphite limiters for ORNL's ISX-B tokamak are given

  18. Surface Modification of Polyethylene Films using Atmospheric

    African Journals Online (AJOL)

    Dr A.B.Ahmed

    ABSTRACT. An atmospheric-pressure plasma jet (APPJ) is used to increase the wettability of polyethylene polymer films. Reduction in contact angle from 94.32 to 58.33 degrees was measured for treatment times of 1 - 5 seconds. Contact angle reductions of PE as a function of treatment time with APPJ and PE surface at ...

  19. Surface modification of polyethylene films using atmospheric ...

    African Journals Online (AJOL)

    An atmospheric-pressure plasma jet (APPJ) is used to increase the wettability of polyethylene polymer films. Reduction in contact angle from 94.32 to 58.33 degrees was measured for treatment times of 1 - 5 seconds. Contact angle reductions of PE as a function of treatment time with APPJ and PE surface at various oxygen ...

  20. Surface modification and characterization Collaborative Research Center at ORNL

    International Nuclear Information System (INIS)

    1986-01-01

    The Surface Modification and Characterization Collaborative Research Center (SMAC/CRC) is a unique facility for the alteration and characterization of the near-surface properties of materials. The SMAC/CRC facility is equipped with particle accelerators and high-powered lasers which can be used to improve the physical, electrical, and/or chemical properties of solids and to create unique new materials not possible to obtain with conventional ''equilibrium'' processing techniques. Surface modification is achieved using such techniques as ion implantation doping, ion beam mixing, laser mixing, ion deposition, and laser annealing

  1. Comparison of several innovative bridge cable surface modifications

    DEFF Research Database (Denmark)

    Kleissl, Kenneth; Georgakis, Christos T.

    Over the last two decades, several bridge cable manufacturers have introduced surface modifications on the high-density polyethylene (HDPE) sheathing that is installed for the protection of inner cable strands or wires. The modifications are based on research undertaken predominantly in Europe...... and Japan, with two different prevailing systems: HDPE tubing fitted with helical fillets and tubing with pattern-indented surfaces. In the US and Europe, helical fillets dominate, whilst pattern indented sur-faces are more common in Asia, particularly for long-span cable-stayed bridges. Research......-span bridges can now produce more than 50% of the overall horizontal load on the bridge (Gimsing and Georgakis, 2012). Recently, the authors presented a comprehensive comparative study of the aerodynamic performance of these existing cable surface modifications (Kleissl and Georgakis, 2011, 2012...

  2. Modification of inorganic surface with 1-alkenes and 1-alkynes

    NARCIS (Netherlands)

    Maat, ter J.

    2012-01-01

    Surface modification is important because it allows the tuning of surface properties, thereby enabling new applications of a material. It can change physical properties such as wettability and friction, but can also introduce chemical functionalities and binding specificity. Several techniques

  3. Short communication: Alkaline surface modification of banana stem ...

    African Journals Online (AJOL)

    One of the important issues in producing composite materials with natural fibres is the modification of the surface of the fibres to enhance adhesion and interfacial bonding with polymer matrix. In this report, the effect of alkalization on the mechanical properties, thermal stability and surface morphology of banana stem fibres ...

  4. [Research development of surface hydrophilicity and lubrication modification of interventional guide wire].

    Science.gov (United States)

    Zhao, Bing; Liu, Xiaohong; Yuan, Ting

    2015-01-01

    Surface lubricity is one of the important performance criteria for interventional guide wire. In this paper, a review of the methods of surface hydrophilicity and lubrication modification of interventional guide wire is presented, including their fundamental principles, effects and some relative applications. These methods all have their own advantages and disadvantages, therefore, limitations of experimental conditions need to be taken into account.

  5. Surface modification of steels by electrical discharge treatment in electrolyte

    International Nuclear Information System (INIS)

    Krastev, D.; Paunov, V.; Yordanov, B.; Lazarova, V.

    2013-01-01

    Full text: In this work are discussed some experimental data about the influence of applied electrical discharge treatment in electrolyte on the surface structure of steels. The electrical discharge treatment of steel surface in electrolyte gives a modified structure with specific combination of characteristics in result of nonequilibrium transformations. The modification goes by a high energy thermal process in a very small volume on the metallic surface involving melting, vaporisation, activation and alloying in electrical discharges, and after that cooling of this surface with high rate in the electrolyte. The surface layers obtain a different structure in comparison with the metal matrix and are with higher hardness, wear resistance and corrosion resistance. key words: surface modification, electrical discharge treatment in electrolyte, steels

  6. Surface modification of polypropylene membrane by polyethylene glycol graft polymerization.

    Science.gov (United States)

    Abednejad, Atiye Sadat; Amoabediny, Ghasem; Ghaee, Azadeh

    2014-09-01

    Polypropylene hollow fiber microporous membranes have been used in a wide range of applications, including blood oxygenator. The hydrophobic feature of the polypropylene surface causes membrane fouling. To minimize fouling, a modification consisting of three steps: surface activation in H2 and O2 plasma, membrane immersion in polyethylene glycol (PEG) and plasma graft polymerization was performed. The membranes were characterized by contact angle measurement, Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), tensile test, scanning electron microscopy (SEM) and atomic force microscopy (AFM). Oxygen transfer of modified membranes was also tested. The stability of grafted PEG was measured in water and in phosphate buffer saline (PBS) at 37°C. Blood compatibility of modified surfaces was evaluated by the platelet adhesion method. Water contact angel reduction from 110° to 72° demonstrates the enhanced hydrophilicity, and XPS results verify the presence of oxygenated functional groups due to the peak existence in 286 eV as a result of PEG grafting. The results clearly indicate that plasma graft-polymerization of PEG is an effective way for antifouling improvement of polypropylene membranes. Also, the results show that oxygen transfer changes in PEG grafted membranes are not significant. Copyright © 2014 Elsevier B.V. All rights reserved.

  7. Thermal performance enhancement of erythritol/carbon foam composites via surface modification of carbon foam

    Science.gov (United States)

    Li, Junfeng; Lu, Wu; Luo, Zhengping; Zeng, Yibing

    2017-03-01

    The thermal performance of the erythritol/carbon foam composites, including thermal diffusivity, thermal capacity, thermal conductivity and latent heat, were investigated via surface modification of carbon foam using hydrogen peroxide as oxider. It was found that the surface modification enhanced the wetting ability of carbon foam surface to the liquid erythritol of the carbon foam surface and promoted the increase of erythritol content in the erythritol/carbon foam composites. The dense interfaces were formed between erythritol and carbon foam, which is due to that the formation of oxygen functional groups C=O and C-OH on the carbon surface increased the surface polarity and reduced the interface resistance of carbon foam surface to the liquid erythritol. The latent heat of the erythritol/carbon foam composites increased from 202.0 to 217.2 J/g through surface modification of carbon foam. The thermal conductivity of the erythritol/carbon foam composite before and after surface modification further increased from 40.35 to 51.05 W/(m·K). The supercooling degree of erythritol also had a large decrease from 97 to 54 °C. Additionally, the simple and effective surface modification method of carbon foam provided an extendable way to enhance the thermal performances of the composites composed of carbon foams and PCMs.

  8. Nanoparticle-Based Surface Modifications for Microtribology Control and Superhydrophobicity

    Science.gov (United States)

    Hurst, Kendall Matthew

    2010-11-01

    contact" between two contacting surfaces. The studies found that AuNP thin films produced using the lowest initial concentrations of nanoparticles in solution produced estimated real contact areas of around 1%, reducing the adhesion of oxidized Si (100) surfaces from about 37 mJ/m2 down to 0.02 mJ/m 2. In addition, the reducing in real contact area effectively reduced the coefficient of static friction between silicon-based surfaces due to the extremely high dependence of stiction on friction and wear at the microscale. This work also investigated methods of permanently immobilizing AuNP-based films on the silicon surfaces of microstructures in order to create more mechanically robust coatings. The use of organic self-assembled monolayers (SAMs) functionalized with tail-groups known to bond to metallic surfaces were effective in producing much more durable coatings as opposed to non-immobilized AuNP films. Chemical vapor deposition (CVD) techniques were also used to coat rough AuNP films with very thin films of silica (SiO2) to create a robust, rough surface. This method was also very effective in creating a durable coating which is capable of reducing the adhesion energy and friction between two microscale surfaces for extended periods of time. Similar CVD techniques were also used to begin investigating the production of alumina nanoparticle-based superhydrophobic films for use in consumer electronics. Overall, the work presented in this dissertation illustrates that engineered nanoparticle-based surface modifications can be extremely effective in the reduction of the inherent interfacial phenomena that exist on microfabricated systems. This work is can potentially lead us into a new age of the miniaturization of mechanical and electronic devices.

  9. Surface modifications of polypropylene by high energy carbon ions

    International Nuclear Information System (INIS)

    Saha, A.; Chakraborty, V.; Dutta, R.K.; Chintalapudi, S.N.

    2000-01-01

    Polypropylene was irradiated with 12 C ions of 3.6 and 5.4 MeV energies using 3 MV tandem accelerator. The surface modification was investigated by Scanning Electron Microscopy (SEM). Optical changes were monitored by UV-VIS and FTIR spectroscopy. At the lowest ion fluence, only blister formation of various sizes (1-6 μm) was observed. Polymer when irradiated at a fluence of 1x10 14 ions/cm 2 exhibited a network structure. A comparative study on dose dependence of surface and bulk modification has been described. (author)

  10. Surface modification of titanium and titanium alloys by ion implantation.

    Science.gov (United States)

    Rautray, Tapash R; Narayanan, R; Kwon, Tae-Yub; Kim, Kyo-Han

    2010-05-01

    Titanium and titanium alloys are widely used in biomedical devices and components, especially as hard tissue replacements as well as in cardiac and cardiovascular applications, because of their desirable properties, such as relatively low modulus, good fatigue strength, formability, machinability, corrosion resistance, and biocompatibility. However, titanium and its alloys cannot meet all of the clinical requirements. Therefore, to improve the biological, chemical, and mechanical properties, surface modification is often performed. In view of this, the current review casts new light on surface modification of titanium and titanium alloys by ion beam implantation. (c) 2010 Wiley Periodicals, Inc.

  11. Impact of Dental Implant Surface Modifications on Osseointegration

    Directory of Open Access Journals (Sweden)

    Ralf Smeets

    2016-01-01

    Full Text Available Objective. The aim of this paper is to review different surface modifications of dental implants and their effect on osseointegration. Common marketed as well as experimental surface modifications are discussed. Discussion. The major challenge for contemporary dental implantologists is to provide oral rehabilitation to patients with healthy bone conditions asking for rapid loading protocols or to patients with quantitatively or qualitatively compromised bone. These charging conditions require advances in implant surface design. The elucidation of bone healing physiology has driven investigators to engineer implant surfaces that closely mimic natural bone characteristics. This paper provides a comprehensive overview of surface modifications that beneficially alter the topography, hydrophilicity, and outer coating of dental implants in order to enhance osseointegration in healthy as well as in compromised bone. In the first part, this paper discusses dental implants that have been successfully used for a number of years focusing on sandblasting, acid-etching, and hydrophilic surface textures. Hereafter, new techniques like Discrete Crystalline Deposition, laser ablation, and surface coatings with proteins, drugs, or growth factors are presented. Conclusion. Major advancements have been made in developing novel surfaces of dental implants. These innovations set the stage for rehabilitating patients with high success and predictable survival rates even in challenging conditions.

  12. Impact of Dental Implant Surface Modifications on Osseointegration

    Science.gov (United States)

    Smeets, Ralf; Stadlinger, Bernd; Schwarz, Frank; Beck-Broichsitter, Benedicta; Jung, Ole; Precht, Clarissa; Kloss, Frank; Gröbe, Alexander; Heiland, Max

    2016-01-01

    Objective. The aim of this paper is to review different surface modifications of dental implants and their effect on osseointegration. Common marketed as well as experimental surface modifications are discussed. Discussion. The major challenge for contemporary dental implantologists is to provide oral rehabilitation to patients with healthy bone conditions asking for rapid loading protocols or to patients with quantitatively or qualitatively compromised bone. These charging conditions require advances in implant surface design. The elucidation of bone healing physiology has driven investigators to engineer implant surfaces that closely mimic natural bone characteristics. This paper provides a comprehensive overview of surface modifications that beneficially alter the topography, hydrophilicity, and outer coating of dental implants in order to enhance osseointegration in healthy as well as in compromised bone. In the first part, this paper discusses dental implants that have been successfully used for a number of years focusing on sandblasting, acid-etching, and hydrophilic surface textures. Hereafter, new techniques like Discrete Crystalline Deposition, laser ablation, and surface coatings with proteins, drugs, or growth factors are presented. Conclusion. Major advancements have been made in developing novel surfaces of dental implants. These innovations set the stage for rehabilitating patients with high success and predictable survival rates even in challenging conditions. PMID:27478833

  13. Influence of Surface Modification on Physicochemical Properties of ZnO Thin Films and Nanostructures: a Review

    Science.gov (United States)

    Xian, Fenglin; Xu, Linhua

    The surface modification plays an important role on both physical and chemical properties of zinc oxide (ZnO) materials. In this review paper, efforts are made to summarize and analyze reported results regarding surface modification method, surface modification effect on the luminescence and superhydrophobic properties of ZnO thin films and nanostructures. Furthermore, the photocatalytic activity and gas sensor property of modified ZnO using both organic and inorganic species are also involved.

  14. Method Modification for the AtlasListeriaEnvironmental LE Detection Assay Using FoodChek ActeroListeriaEnrichment Media and Half-Fraser Media for the Detection ofListeriaspp. from Environmental Surfaces.

    Science.gov (United States)

    Maroni, Brett; Lopez, Tucker; Neal, Cambria; Verver, Sarah; Puente, Celina; Lauffer, Jannelle; Garcia, Joseph; Groschel, Bettina; Dreyling, Erin; Chaney, W Evan; Bastin, Ben; Bird, Patrick; Benzinger, M Joseph; Agin, James; Goins, David; Hariram, Upasana; Chen, Yi; Ryser, Elliot; Brodsky, Michael

    2018-03-01

    Two candidate method modifications for the Atlas Listeria Environmental LE Detection Assay were compared with the U.S. Department of Agriculture (USDA)-Food Safety and Inspection Service Microbiology Laboratory Guidebook 8.09 (MLG 8.09) method for detection of Listeria spp. on stainless steel, polyvinyl chloride (PVC), and sealed concrete surfaces. For LE candidate method 1, samples were enriched in FoodChek Actero Listeria Enrichment Media [ALEM; Performance Tested MethodSM (PTM) 111201] at 35 ± 2°C for 18 to 24 h and evaluated for a range of analytical sample volumes. For LE candidate method 2, the current Roka PTM using 90 mL of Half-Fraser broth for enrichment at 35 ± 2°C was evaluated at 24 h with a reduced sample volume. These comparisons were made in multiple studies across the three environmental surfaces. Within each method and study, a total of 5 samples were uninoculated, 20 samples were inoculated with Listeria spp. at a low level to target fractional positivity, and 5 samples were inoculated with Listeria spp. at a high level to approach a probability of detection of 1. Inclusivity and exclusivity studies were also conducted for the LE method in combination with Half-Fraser and ALEM. The Atlas Listeria Environmental LE Detection Assay detected all 50 inclusive organisms, including 25 strains of L. monocytogenes and 5 strains of each of the other five common species of Listeria (L. innocua, L. welshimeri, L. ivanovii, L. seeligeri, and L. grayi) and none of the 30 exclusive organisms across all media and with both 200 and 2000 µL sample volumes. For the LE candidate method 1 studies, no significant differences were observed within the Roka ALEM method at 18, 20, or 24 h and for both the 200 and 2000 µL sample volumes as compared with the paired culture outcome. However, the ALEM method performed significantly better as compared with the unpaired reference method for sealed concrete and stainless steel. For the LE candidate method 2 studies, no

  15. Surface Modification Effects on CNTs Adsorption of Methylene Blue and Phenol

    Directory of Open Access Journals (Sweden)

    A. H. Norzilah

    2011-01-01

    Full Text Available This study compares the adsorption capacity of modified CNTs using acid and heat treatment. The CNTs were synthesized from acetone and ethanol as carbon sources, using floating catalyst chemical vapor deposition (FC-CVD method. energy-dispersive X-ray spectroscopy (EDX and Boehm method revealed the existence of oxygen functional group on the surface of CNTs. Heat modification increases the adsorption capacity of as-synthesized CNTs for methylene blue (MB and phenol by approximately 76% and 50%, respectively. However, acid modification decreases the adsorption capacity. The equilibrium adsorption data fitted the Redlich-Peterson isotherm. For the adsorption kinetic study, the experimental data obeyed the pseudo-second-order model. Both modifications methods reduced the surface area and pore volume. The studies show that the adsorption of MB and phenol onto modified CNTs is much more influenced by their surface functional group than their surface area and pore volume.

  16. [Research on surface modification and bio-tribological properties of artificial joint].

    Science.gov (United States)

    Pan, Yusong; Wang, Jing; Ding, Guoxin

    2012-06-01

    The bio-tribological properties of an artificial joint can be obviously improved by surface modification technologies. In this paper, the benefits and disadvantages of various surface modification methods-such as surface coating, plasma treatment, surface texture and surface grafting modification-are discussed. The aim of surface coating and/or plasma treatment is to improve the surface hardness of the materials, thus enhancing the wear resistance of artificial joints. However, these technologies do not effectively alleviate stress concentration of material in the short times in which artificial joints bear physiological impact load, resulting in easy fracture. Surface texture serves mainly to improve the lubrication properties through micro-concavities on the material surface for storage lubricant. Surface texturing can realize improvements in bio-tribological properties, but it does not enhance the impact resistance of the joint. Surface grafting modification is implemented mainly by grafting hydrophilic or other specific functional groups to improve the surface hydrophilicity and wetability, thus enhancing lubricating performance and reducing the coefficient of friction.

  17. Heterogeneous polymer modification: Polyolefin maleation in supercritical carbon dioxide and amorphous fluoropolymer surface modification

    Science.gov (United States)

    Hayes, Heather J.

    1999-11-01

    Three distinct heterogeneous polymer modification reactions are explored in this work. The first is a bulk reaction commonly conducted on polyolefins---the free radical addition of maleic anhydride. This reaction was run using supercritical carbon dioxide (SC CO2) as the solvent. The second was the chemical surface modification of an amorphous fluorocopolymer of tetrafluoroethylene and a perfluorodioxole monomer (Teflon AF). Several reactions were explored to reduce the surface of the fluorocopolymer for the enhancement of wettability. The last modification was also on Teflon AF and involved the physical modification of the surface through the transport polymerization of xylylene in order to synthesize a novel bilayer membrane. The bulk maleation of poly-4-methyl-1-pentene (PMP) was the focus of the first project. SC CO2 was utilized as both solvent and swelling agent to promote this heterogeneous reaction and led to successful grafting of anhydride groups on both PMP and linear low density polyethylene. Varying the reaction conditions and reagent concentrations allowed optimization of the reaction. The grafted anhydride units were found to exist as single maleic and succinic grafts, and the PMP became crosslinked upon maleation. The surface of a fluoropolymer can be difficult to alter. An examination of three reactions was made to determine the reactivity of Teflon AF: sodium naphthalenide treatment (Na-Nap), aluminum metal modification through deposition and dissolution, and mercury/ammonia photosensitization. The fluorocopolymer with the lower perfluorodioxole percentage was found to be more reactive towards modification with the Na-Nap treatment. The other modification reactions appeared to be nearly equally reactive toward both fluorocopolymers. The functionality of the Na-Nap-treated surface was examined in detail with the use of several derivatization reactions. In the final project, an asymmetric gas separation membrane was synthesized using Teflon AF as

  18. Printing-assisted surface modifications of patterned ultrafiltration membranes

    International Nuclear Information System (INIS)

    Wardrip, Nathaniel C.; Dsouza, Melissa; Urgun-Demirtas, Meltem; Snyder, Seth W.

    2016-01-01

    Understanding and restricting microbial surface attachment will enhance wastewater treatment with membranes. We report a maskless lithographic patterning technique for the generation of patterned polymer coatings on ultrafiltration membranes. Polyethylene glycol, zwitterionic, or negatively charged hydrophilic polymer compositions in parallel- or perpendicular-striped patterns with respect to feed flow were evaluated using wastewater. Membrane fouling was dependent on the orientation and chemical composition of the coatings. Modifications reduced alpha diversity in the attached microbial community (Shannon indices decreased from 2.63 to 1.89) which nevertheless increased with filtration time. Sphingomonas species, which condition membrane surfaces and facilitate cellular adhesion, were depleted in all modified membranes. Microbial community structure was significantly different between control, different patterns, and different chemistries. Lastly, this study broadens the tools for surface modification of membranes with polymer coatings and for understanding and optimization of antifouling surfaces.

  19. Surface modification on PMMA : PVDF polyblend: hardening under ...

    Indian Academy of Sciences (India)

    Unknown

    bility of PMMA: PVDF has been reported (Nishi and. Wang 1975; Paul and Altamirano 1975). The present paper reports the study on the surface modification of. PMMA: PVDF blend system under chemical environment of some organic liquids. The tool used for detection is. Vickers microhardness technique. This technique is ...

  20. Surface modification on PMMA : PVDF polyblend: hardening under ...

    Indian Academy of Sciences (India)

    Unknown

    paper reports the study on the surface modification of. PMMA: PVDF blend system under chemical environment of some organic liquids. The tool used for detection is. Vickers microhardness technique. This technique is now being utilized widely for morphological stabilization and plasticization studies of polymers (Gonzalez ...

  1. Advancing Sustainable Catalysis with Magnetite Surface Modification and Synthetic Applications

    Science.gov (United States)

    This article surveys the recent developments in the synthesis, surface modification, and synthetic applications of magnetitenanoparticles. The emergence of iron(II,III) oxide (triiron tetraoxide or magnetite; Fe3O4, or FeO•Fe2O3) nanoparticles as a sustainable support in heteroge...

  2. Surface Modification of Poly(tetrafluoroethylene) by Magnesium Amalgam

    Czech Academy of Sciences Publication Activity Database

    Kavan, Ladislav; Janda, Pavel; Weber, Jan

    2001-01-01

    Roč. 36, - (2001), s. 879-885 ISSN 0022-2461 R&D Projects: GA ČR GA203/98/1168; GA ČR GA203/98/1181 Institutional research plan: CEZ:AV0Z4040901 Keywords : poly(tetrafluoroethylene) * surface modification * ESCA Subject RIV: CG - Electrochemistry Impact factor: 0.728, year: 2001

  3. Surface modification of polyethylene by diffuse barrier discharge plasma

    Czech Academy of Sciences Publication Activity Database

    Novák, I.; Števiar, M.; Popelka, A.; Chodák, I.; Mosnáček, J.; Špírková, Milena; Janigová, I.; Kleinová, A.; Sedliačik, J.; Šlouf, Miroslav

    2013-01-01

    Roč. 53, č. 3 (2013), s. 516-523 ISSN 0032-3888 R&D Projects: GA AV ČR(CZ) IAAX08240901 Institutional research plan: CEZ:AV0Z40500505 Keywords : low-density polyethylene * plasma discharge * surface modification Subject RIV: JI - Composite Materials Impact factor: 1.441, year: 2013

  4. Surface Modification and Heat Generation of FePt Nanoparticles

    Directory of Open Access Journals (Sweden)

    Da-Hua Wei

    2017-02-01

    Full Text Available The chemical reduction of ferric acetylacetonate (Fe(acac3 and platinum acetylacetonate (Pt(acac2 using the polyol solvent of phenyl ether as an agent as well as an effective surfactant has successfully yielded monodispersive FePt nanoparticles (NPs with a hydrophobic ligand and a size of approximately 3.8 nm. The present FePt NPs synthesized using oleic acid and oleylamine as the stabilizers under identical conditions were achieved with a simple method. The surface modification of FePt NPs by using mercaptoacetic acid (thiol as a phase transfer reagent through ligand exchange turned the NPs hydrophilic, and the FePt NPs were water-dispersible. The hydrophilic NPs indicated slight agglomeration which was observed by transmission electron microscopy images. The thiol functional group bond to the FePt atoms of the surface was confirmed by Fourier transform infrared spectroscopy (FTIR spectra. The water-dispersible FePt NPs employed as a heating agent could reach the requirement of biocompatibility and produce a sufficient heat response of 45 °C for magnetically induced hyperthermia in tumor treatment fields.

  5. Long-term stable surface modification of DLC coatings

    Directory of Open Access Journals (Sweden)

    Gotzmann Gaby

    2017-09-01

    Full Text Available The use of coatings based on diamond like carbon (DLC for medical applications was established during the last years. Main advantages of these coatings are its high hardness, good wear and friction behavior and its biocompatibility. Using low-energy electron-beam treatment, we addressed the surface modification of DLC coatings. The aim was to generate new biofunctional surface characteristics that are long-term stable.

  6. Application of xenon difluoride for surface modification of polymers

    International Nuclear Information System (INIS)

    Barsamyan, G.B.; Belokonov, K.V.; Vargasova, N.A.; Sokolov, V.B.; Chaivanov, B.B.; Zubov, V.P.

    1994-01-01

    Chemical interaction between xenon difluoride (XeF 2 ) and polymeric materials was investigated. It was shown that the reaction occurs on the surface of solid polymer layer and brings to chemical modification of the surface properties of the polymer leaving the bulk properties unchanged. The results of various analysis of the fluorinated samples (IR, FTIR-ATR, ESCA, bulk analysis etc) are presented. The mechanism of reaction is proposed. 12 refs.; 13 figs

  7. Surface modification of magnesium hydroxide using vinyltriethoxysilane by dry process

    Energy Technology Data Exchange (ETDEWEB)

    Lan, Shengjie [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008 (China); Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Chinese Academy of Sciences, Xining 810008 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Li, Lijuan, E-mail: lilj@isl.ac.cn [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008 (China); Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Chinese Academy of Sciences, Xining 810008 (China); Xu, Defang; Zhu, Donghai; Liu, Zhiqi; Nie, Feng [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008 (China); Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Chinese Academy of Sciences, Xining 810008 (China)

    2016-09-30

    Highlights: • A modification mechanism for magnesium hydroxide using silane by dry process was proposed. • Si−O−Mg bonds were formed directly by the reaction between Si-OC{sub 2}H{sub 5} and hydroxyl groups of magnesium hydroxide. • Dispersibility and compatibility of modified magnesium hydroxide improved in organic phase. - Abstract: In order to improve the compatibility between magnesium hydroxide (MH) and polymer matrix, the surface of MH was modified using vinyltriethoxysilane (VTES) by dry process and the interfacial interaction between MH and VTES was also studied. Zeta potential measurements implied that the MH particles had better dispersion and less aggregation after modification. Sedimentation tests showed that the surface of MH was transformed from hydrophilic to hydrophobic, and the dispersibility and the compatibility of MH particles significantly improved in the organic phase. Scanning electronic microscopy (SEM), Transmission electron microscopy (TEM) and X-ray powder diffraction (XRD) analyses showed that a thin layer had formed on the surface of the modified MH, but did not alter the material’s crystalline phase. Fourier transform infrared (FT-IR) spectra, X-ray photoelectron spectra (XPS) and Thermogravimetric analysis (TGA) showed that the VTES molecules bound strongly to the surface of MH after modification. Chemical bonds (Si−O−Mg) formed by the reaction between Si-OC{sub 2}H{sub 5} and hydroxyl group of MH, also there have physical adsorption effect in the interface simultaneously. A modification mechanism of VTES on the MH surface by dry process was proposed, which different from the modification mechanism by wet process.

  8. Hydrophilic Surface Modification of PDMS Microchannel for O/W and W/O/W Emulsions

    Directory of Open Access Journals (Sweden)

    Shazia Bashir

    2015-09-01

    Full Text Available A surface modification method for bonded polydimethylsiloxane (PDMS microchannels is presented herein. Polymerization of acrylic acid was performed on the surface of a microchannel using an inline atmospheric pressure dielectric barrier microplasma technique. The surface treatment changes the wettability of the microchannel from hydrophobic to hydrophilic. This is a challenging task due to the fast hydrophobic recovery of the PDMS surface after modification. This modification allows the formation of highly monodisperse oil-in-water (O/W droplets. The generation of water-in-oil-in-water (W/O/W double emulsions was successfully achieved by connecting in series a hydrophobic microchip with a modified hydrophilic microchip. An original channel blocking technique to pattern the surface wettability of a specific section of a microchip using a viscous liquid comprising a mixture of honey and glycerol, is also presented for generating W/O/W emulsions on a single chip.

  9. The effect of surface modification on initial ice formation on aluminum surfaces

    DEFF Research Database (Denmark)

    Rahimi, Maral; Afshari, Alireza; Fojan, Peter

    2015-01-01

    One of the most promising energy saving methods in cold climate areas is heat recovery in ventilation system by using air-to-air heat exchangers. However, due to a higher humidity in the exhaust air, there is a risk of ice formation on the heat exchanger fins at subzero temperatures. Since the main...... material of heat exchanger fins is aluminum, this paper focuses on the effect of aluminum wettability on the initial stages of ice formation. The ice growth was studied on bare as well as hydrophilically and hydrophobically modified surfaces of aluminum (8011A) sheets, commonly used in heat exchangers......, at different psychrometric parameters. The obtained results show that the surface modification of aluminum plays a crucial role in the ice formation. We demonstrated that flat hydrophobic surfaces exhibit slower ice growth and denser ice layers, hence making this type of treatment preferable for aluminum heat...

  10. Natural bone-like biomimetic surface modification of titanium

    Science.gov (United States)

    Yoon, Il-Kyu; Hwang, Ji-Young; Jang, Won-Cheoul; Kim, Hae-Won; Shin, Ueon Sang

    2014-05-01

    An implantable metallic surface consisting of titanium (Ti) was modified with natural bone-mimicking CNT-Gelatin-HA nanohybrids to create a new surface with similar properties to the surrounding bone tissue in terms of the chemical constitution, nanotopography, wettability, and biocompatibility. The biomimetic surface modification was achieved through the covalent immobilization of carbon nanotubes (CNTs) onto the Ti surface, the covalent tethering of gelatin molecules onto the CNT surface, and then the deposition of hydroxyl apatite (HA) crystals onto the gelatin-tethered CNTs in SBF solution. The SEM microscopic images demonstrated that the modified Ti surface continually maintained a fibrous structure of CNTs, but that the CNT fibers were hybridized with gelatin and HA in a multi-core-shell structure of similar constitution to that of the collagen fibers of natural bone. The new surface of the Ti substrates showed significantly higher mechanical properties and favorable wettability and biocompatibility.

  11. Surface modification for interaction study with bacteria and preosteoblast cells

    Science.gov (United States)

    Song, Qing

    Surface modification plays a pivotal role in bioengineering. Polymer coatings can provide biocompatibility and biofunctionalities to biomaterials through surface modification. In this dissertation, initiated chemical vapor deposition (iCVD) was utilized to coat two-dimensional (2D) and three-dimensional (3D) substrates with differently charged polyelectrolytes in order to generate antimicrobial and osteocompatible biomaterials. ICVD is a modified CVD technique that enables surface modification in an all-dry condition without substrate damage and solvent contamination. The free-radical polymerization allows the vinyl polymers to conformally coat on various micro- and nano-structured substrates and maintains the delicate structure of the functional groups. The vapor deposition of polycations provided antimicrobial activity to planar and porous substrates through destroying the negatively charged bacterial membrane and brought about high contact-killing efficiency (99.99%) against Gram-positive Bacillus subtilis and Gram-negative Escherichia coli. Additionally, the polyampholytes synthesized by iCVD exhibited excellent antifouling performance against the adhesion of Gram-positive Listeria innocua and Gram-negative E. coli in phosphate buffered saline (PBS). Their antifouling activities were attributed to the electrostatic interaction and hydration layers that served as physical and energetic barriers to prevent bacterial adhesion. The contact-killing and antifouling polymers synthesized by iCVD can be applied to surface modification of food processing equipment and medical devices with the aim of reducing foodborne diseases and medical infections. Moreover, the charged polyelectrolyte modified 2D polystyrene surfaces displayed good osteocompatibility and enhanced osteogenesis of preosteoblast cells than the un-modified polystyrene surface. In order to promote osteoinduction of hydroxyapatite (HA) scaffolds, bioinspired polymer-controlled mineralization was conducted

  12. Surface modification of polypropylene non-woven fibers with TiO2 nanoparticles via layer-by-layer self assembly method: Preparation and photocatalytic activity.

    Science.gov (United States)

    Pavasupree, Suttipan; Dubas, Stephan T; Rangkupan, Ratthapol

    2015-11-01

    Polypropylene (PP) meltblown fibers were coated with titanium dioxide (TiO2) nanoparticles using layer-by-layer (LbL) deposition technique. The fibers were first modified with 3 layers of poly(4-styrenesulfonic acid) (PSS) and poly(diallyl-dimethylammonium chloride) (PDADMAC) to improve the anchoring of the TiO2 nanoparticle clusters. PDADMAC, which is positively charged, was then used as counter polyelectrolyte in tandem with anionic TiO2 nanoparticles to construct TiO2/PDADMAC bilayer in the LbL fashion. The number of deposited TiO2/PDADMAC layers was varied from 1 to 7 bilayer, and could be used to adjust TiO2 loading. The LbL technique showed higher TiO2 loading efficiency than the impregnation approach. The modified fibers were tested for their photocatalytic activity against a model dye, Methylene Blue (MB). Results showed that the TiO2 modified fibers exhibited excellent photocatalytic activity efficiency similar to that of TiO2 powder dispersed in solution. The deposition of TiO2 3 bilayer on the PP substrate was sufficient to produce nanocomposite fibers that could bleach the MB solution in less than 4hr. TiO2-LbL constructions also preserved TiO2 adhesion on substrate surface after 1cycle of photocatalytic test. Successive photocatalytic test showed decline in MB reduction rate with loss of TiO2 particles from the substrate outer surface. However, even in the third cycle, the TiO2 modified fibers are still moderately effective as it could remove more than 95% of MB after 8hr of treatment. Copyright © 2015. Published by Elsevier B.V.

  13. Modification of surface properties of Lentinus sajor-caju mycelia by physical and chemical methods: evaluation of their Cr6+ removal efficiencies from aqueous medium.

    Science.gov (United States)

    Bayramoğlu, Gülay; Celik, Gökçe; Yalçin, Emine; Yilmaz, Meltem; Arica, M Yakup

    2005-03-17

    The hexavalent chromium biosorption onto untreated and heat-, acid- and alkali-treated Lentinus sajor-caju mycelia were studied from aqueous solutions. The particles sizes of the fungal mycelia ranged from 100 to 200 microm. The effect of pH, temperature, biosorbent dose, initial concentration of chromium ions, contact time parameters were investigated in a batch system. Biosorption equilibrium was established in about 4 h. The surface charge density of the fungal preparations varied with pH, and the maximum absorption of chromium ions on the fungal preparations were obtained at pH 2.0. The biosorption of chromium ions by the tested fungal preparations increased as the initial concentration of chromium ions increased in the medium. The maximum biosorption capacities of the untreated and heat, HCl- and NaOH-treated fungal biomass were 0.363, 0.613, 0.478 and 0.513 mmol Cr6+ per gram of dry biomass, respectively. The correlation regression coefficients and the Langmuir constant values show that the biosorption process can be well defined by Langmuir equation. The chromium adsorption data were analysed using the first- and the second-order kinetic models. The first-order equation is the most appropriate equation to predict the biosorption capacities of all the fungal preparations. In addition, the polarity and surface energy of the untreated and all the modified biomass film preparations were determined by contact angle measurement. All the tested fungal biomass preparations could be regenerated using 0.1 M NaOH solution.

  14. Beam waist position study for surface modification of polymethyl-methacrylate with femtosecond laser pulses

    Energy Technology Data Exchange (ETDEWEB)

    Caballero-Lucas, F.; Florian, C.; Fernández-Pradas, J.M., E-mail: jmfernandez@ub.edu; Morenza, J.L.; Serra, P.

    2016-06-30

    Highlights: • Surface modification of PMMA with femtosecond laser pulses. • Z-scan reflectance and transmittance study for controlling the sample surface position in the laser beam waist. • Surface modifications with dimensions in the nanometric scale with a 1027 nm wavelength laser. • Extended range of some microns for placing the sample and precise determination of the beam waist position. - Abstract: Femtosecond lasers are versatile tools to process transparent materials. This optical property poses an issue for surface modification. In this case, laser radiation would not be absorbed at the surface unless the beam is just focused there. Otherwise, absorption would take place in the bulk leaving the surface unperturbed. Therefore, strategies to position the material surface at the laser beam waist with high accuracy are essential. We investigated and compared two options to achieve this aim: the use of reflectance data and transmittance measurements across the sample, both obtained during z-scans with pulses from a 1027 nm wavelength laser and 450 fs pulse duration. As the material enters the beam waist region, a reflectance peak is detected while a transmittance drop is observed. With these observations, it is possible to control the position of the sample surface with respect to the beam waist with high resolution and attain pure surface modification. In the case of polymethyl-methacrylate (PMMA), this resolution is 0.6 μm. The results prove that these methods are feasible for submicrometric processing of the surface.

  15. Ultralow energy ion beam surface modification of low density polyethylene.

    Science.gov (United States)

    Shenton, Martyn J; Bradley, James W; van den Berg, Jaap A; Armour, David G; Stevens, Gary C

    2005-12-01

    Ultralow energy Ar+ and O+ ion beam irradiation of low density polyethylene has been carried out under controlled dose and monoenergetic conditions. XPS of Ar+-treated surfaces exposed to ambient atmosphere show that the bombardment of 50 eV Ar+ ions at a total dose of 10(16) cm(-2) gives rise to very reactive surfaces with oxygen incorporation at about 50% of the species present in the upper surface layer. Using pure O+ beam irradiation, comparatively low O incorporation is achieved without exposure to atmosphere (approximately 13% O in the upper surface). However, if the surface is activated by Ar+ pretreatment, then large oxygen contents can be achieved under subsequent O+ irradiation (up to 48% O). The results show that for very low energy (20 eV) oxygen ions there is a dose threshold of about 5 x 10(15) cm(-2) before surface oxygen incorporation is observed. It appears that, for both Ar+ and O+ ions in this regime, the degree of surface modification is only very weakly dependent on the ion energy. The results suggest that in the nonequilibrium plasma treatment of polymers, where the ion flux is typically 10(18) m(-2) s(-1), low energy ions (<50 eV) may be responsible for surface chemical modification.

  16. Plasma Processing with Fluorine Chemistry for Modification of Surfaces Wettability

    Directory of Open Access Journals (Sweden)

    Veronica Satulu

    2016-12-01

    Full Text Available Using plasma in conjunction with fluorinated compounds is widely encountered in material processing. We discuss several plasma techniques for surface fluorination: deposition of fluorocarbon thin films either by magnetron sputtering of polytetrafluoroethylene targets, or by plasma-assisted chemical vapor deposition using tetrafluoroethane as a precursor, and modification of carbon nanowalls by plasma treatment in a sulphur hexafluoride environment. We showed that conformal fluorinated thin films can be obtained and, according to the initial surface properties, superhydrophobic surfaces can be achieved.

  17. Benefits of aggregates surface modification in concrete production

    Science.gov (United States)

    Junak, J.; Sicakova, A.

    2017-10-01

    In our study, recycled concrete aggregates (RCA), which surfaces had been modified by geopolymer material based on coal fly ash, were used to produce the concrete samples. In these samples, fraction 4/8 mm was replaced by recycled concrete aggregate with a range of 100%. To modify the surface of RCA was “Solo” and “Triple stage” modification used. On these samples real density, total water absorption and compressive strength were examined after 28, 90, 180 and 365 days of hardening. The highest compressive strength 56.8 MPa, after 365 days hardening, reached sample which had improved RCA surface by “Triple stage mixing”.

  18. Effects of Ultrasonic Nanocrystal Surface Modification (UNSM) on Residual Stress State and Fatigue Strength of AISI 304

    Science.gov (United States)

    Cherif, A.; Pyoun, Y.; Scholtes, B.

    2010-03-01

    The effects of a new mechanical surface treatment method, called ultrasonic nanocrystal surface modification (UNSM), on near-surface microstructures and residual stress states as well as on the fatigue behavior of an austenitic steel AISI 304 are investigated and discussed. The results are compared with consequences of other mechanical surface treatment methods such as deep rolling or shot peening.

  19. Plasma surface modification as a new approach to protect urinary catheter against Escherichia coli biofilm formation

    OpenAIRE

    Taheran, Leila; Zarrini, Gholamreza; Khorram, Sirous; Zakerhamidi, Mohammad Sadegh

    2016-01-01

    Background and Objectives: Biomaterials are widely used in medical devices such as urinary catheters. One of the main problems associated with long term using of the urinary catheters is biofilm formation on their surfaces. Many techniques have been presented to reduce the biofilm formation. One of the most revolutionary techniques allowing such surface fictionalization is plasma surface modification. Materials and Methods: In this study, a glow discharge plasma (GDP) effect on Escherichia co...

  20. Thermal desorption and surface modification of He+ implanted into tungsten

    International Nuclear Information System (INIS)

    Fu Zhang; Yoshida, N.; Iwakiri, H.; Xu Zengyu

    2004-01-01

    Tungsten divertor plates in fusion reactors will be subject to helium bombardment. Helium retention and thermal desorption is a concerned issue in controlling helium ash. In the present study, fluence dependence of thermal desorption behavior of helium in tungsten was studied at different irradiation temperatures and ion energies. Results showed that helium desorption could start at ∼400 K with increasing fluence, while no noticeable peaks were detected at low fluence. Total helium desorption reached a saturation value at high fluence range, which was not sensitive to irradiation temperature or ion energy for the conditions evaluated. Surface modifications caused by either ion irradiation or thermal desorption were observed by SEM. The relationship of surface modifications and helium desorption behavior was discussed. Some special features of elevated irradiation temperature and lower ion energy were also indicated

  1. Modification of Ti6Al4V surface by diazonium compounds

    Science.gov (United States)

    Sandomierski, Mariusz; Buchwald, Tomasz; Strzemiecka, Beata; Voelkel, Adam

    2018-02-01

    Ti6Al4V alloy is the most commonly used in orthopedic industry as an endoprosthesis. Ti6Al4V exhibits good mechanical properties, except the abrasion resistance. Surface modification of Ti6Al4V in order to obtain organic layer, and then the attachment of the polymer, can allow for overcoming this problem. The aim of the work was the modification of Ti6Al4V surface by diazonium compounds: salt or cation generated in situ and examine the influence of the reducing agent - ascorbic acid, and the temperature of reaction on modification process. Moreover, the simulated body fluid was used for the assessment of the organic layer stability on Ti6Al4V surface. The evaluation of the modification was carried out using the following methods: Raman microspectroscopy, scanning electron microscopy and energy-dispersive X-ray spectroscopy. Higher temperature of modification by 4-hydroxymethylbenzenediazonium cation, provides the largest amount of organic layer on the Ti6Al4V alloy. In the case of the Ti6Al4V modified by Variamine Blue B salt, the amount of organic layer is not dependent on the reaction condition. Moreover, the ascorbic acid and the presence of TiO2 does not effect on the modification. The modified surface is completely coated with the organic layer which is stable in simulated body fluid.

  2. The effect of substrate modification on microbial growth on surfaces

    CERN Document Server

    Brown, A A

    1998-01-01

    The principle aim of the program was to produce a novel, non-leaching antimicrobial surface for commercial development and future use in the liquid food packaging industry. Antimicrobial surfaces which exist presently have been produced to combat the growth of prokaryotic organisms and usually function as slow release systems. A system which could inhibit eukaryotic growth without contaminating the surrounding 'environment' with the inhibitor was considered of great commercial importance. The remit of this study was concerned with creating a surface which could control the growth of eukaryotic organisms found in fruit juice with particular interest in the yeast, Saccharomyces cerevisiae. Putative antimicrobial surfaces were created by the chemical modification of the test substrate polymers; nylon and ethylvinyl alcohol (EVOH). Surfaces were chemically modified by the covalent coupling of antimicrobial agents known to be active against the yeast Saccharomyces cerevisiae as ascertained by the screening process...

  3. Surface modification and characterization of magnesium hydroxide sulfate hydrate nanowhiskers

    Energy Technology Data Exchange (ETDEWEB)

    Gao Chuanhui [Key Laboratory of Marine Chemistry Theory and Technology, Ministry of Education, Ocean University of China, Qingdao 266100 (China); Li Xianguo, E-mail: chuanhuigao@foxmail.com [Key Laboratory of Marine Chemistry Theory and Technology, Ministry of Education, Ocean University of China, Qingdao 266100 (China); Feng Lijuan; Lu Shaoyan; Liu Jinyan [Key Laboratory of Marine Chemistry Theory and Technology, Ministry of Education, Ocean University of China, Qingdao 266100 (China)

    2010-03-01

    In order to enhance the compatibility with plastic polymers, magnesium hydroxide sulfate hydrate (MHSH) nanowhiskers were modified through grafting methyl methacrylate (MMA) on the surface of the nanowhiskers by emulsion polymerization. The influences of the reaction time, MMA monomer content, adding speed of monomer and the reaction temperature on the grafting ratio were investigated. Thermogravimetry (TG), Fourier transform infrared (FT-IR) spectroscopy, X-ray powder diffraction (XRD), scanning electron microscope (SEM), energy-dispersive X-ray (EDX) spectroscopy and surface contact angle measurement were used to characterize the effect of surface modification. The results showed that the MHSH nanowhiskers were uniformly coated by polymethyl methacrylate (PMMA), and a well-defined core-shell hybrid structure of MHSH/PMMA was obtained. The surface contact angle of the hybrid whiskers increased to 87.32 deg. from 12.71 deg. and the whiskers surface was changed from hydrophilic to lipophilic.

  4. Evaluation of modifications to a physicochemical method for ...

    African Journals Online (AJOL)

    These method modifications were tested on wastewater samples from the mentioned WWTPs. The fundamentals and results of both modifications are discussed in this paper, as well as the imprecision associated with estimating influent SI from effluent CODsol in all studied methods, and its impact on SS determination ...

  5. Mild modification method for the generation of mesoporosity in ...

    African Journals Online (AJOL)

    Mild modification method for the generation of mesoporosity in synthetic and natural mordenite. ... Mild modification method for the generation of mesoporosity in synthetic and natural mordenite. W. Mamo, Y. Awoke, Y. Chebude, I. Diaz. Abstract. Zeolites are widely used as acid catalysts for the synthesis of fine chemicals in ...

  6. Preparation and Surface Modification of Silica Nanoparticles for Superhydrophopic Coating

    Directory of Open Access Journals (Sweden)

    Noor Hadi Aysa

    2017-12-01

    Full Text Available Silica  nanoparticles are well-known to be one of the multifunctional inorganic compounds which are widely used in medical applications. The aim of this study is to prepare the particles of nano silica oxide with particle size ranging from 20-25 nm. In the present study, surface modification of Silica nanoparticles was performed, and influence of modification on the structure and morphological properties was investigated. The resulting  nanoparticles were characterized by X-ray diffraction (XRD, scanning electron microscopy (SEM and atomic force microscopy (AFM.  Silica nanoparticles with the average diameter of about 20 nm were modified with oleic acid, as coupling agents, in order to modify their surface properties and make them more waterproof dispersible in the organic area. Among the results is that the  surface modification of the   Silica nano-particles leads to more dispersion in the organic medium which indicates better organic synthesis.One of the results obtained,is that modified silica-nanoparticles can be used effectively in environmental and safety applications and can be used in future medical applications as wound stick that prevent water from reaching the wound and then prevent  an inflamation.

  7. Ultrahydrophobic surface modification of polymeric fibers and inorganic substrates

    Science.gov (United States)

    Ramaratnam, Karthik

    The wettability of a solid surface is a very important property, and is governed by both the chemical composition and the geometrical microstructure of the surface. Wettability and repellency are important properties of solid surfaces from both fundamental and practical aspects. The wettability of the solid surface is a characteristic property of materials and strongly depends on both the surface energy and the surface roughness. These properties may be approached by mimicking hydrophobic structures created by nature on lotus leaf surface. The lotus effect is based on surface roughness caused by different microstructures together with the hydrophobic properties of the epicuticular wax. The present study investigates the basic principles involved in the fabrication of lotus-like materials on both fibrous and inorganic substrates utilizing the two essential requirements, surface roughness and hydrophobicity. The surface roughness was created either by a porous or a bumpy profile while the hydrophobicity was achieved by grafting a non-fluorinated hydrophobic polymer. For the porous profiles, polymer blend systems showing phase separation were utilized whereas the bumpy profiles were achieved using nanoparticles such as calcium carbonate, silver, or silica particles. In the last part of the research, functionalization of silica nanoparticles was investigated and the development of a universal modification step to obtain the ultrahydrophobic property is reported. In this approach, the adsorption of the polymer and the nanoparticles to fibers has been optimized and the self-cleaning effect of these fabrics modified with silica nanoparticles has also been demonstrated.

  8. Self-Assembled Fluorinated Organogelators for Surface Modification

    Directory of Open Access Journals (Sweden)

    Anilkumar Raghavanpillai

    2012-03-01

    Full Text Available A new class of alkyl- and perfluoroalkyl-containing urea and amide derivatives was synthesized from amino acid derivatives. Most of these compounds showed excellent gelation behavior in organic solvents at low concentrations. A few organogelators selected from the initial screening were used for surface modification of fibrous substrates to create hydrophobic and oleophobic composites. The hydrophobic and oleophobic behaviors of these composites were ascribed to a combination of increased surface roughness and the alkyl/fluorinated functionalities present in the gelator backbone.

  9. Work function modifications of graphite surface via oxygen plasma treatment

    Science.gov (United States)

    Duch, J.; Kubisiak, P.; Adolfsson, K. H.; Hakkarainen, M.; Golda-Cepa, M.; Kotarba, A.

    2017-10-01

    The surface modification of graphite by oxygen plasma was investigated experimentally (X-ray diffraction, nanoparticle tracking analysis, laser desorption ionization mass spectrometry, thermogravimetry, water contact angle) and by molecular modelling (Density Functional Theory). Generation of surface functional groups (mainly sbnd OHsurf) leads to substantial changes in electrodonor properties and wettability gauged by work function and water contact angle, respectively. The invoked modifications were analyzed in terms of Helmholtz model taking into account the theoretically determined surface dipole moment of graphite-OHsurf system (μ = 2.71 D) and experimentally measured work function increase (from 0.75 to 1.02 eV) to determine the sbnd OH surface coverage (from 0.70 to 1.03 × 1014 groups cm-2). Since the plasma treatment was confined to the surface, the high thermal stability of the graphite material was preserved as revealed by the thermogravimetric analysis. The obtained results provide a suitable quantitative background for tuning the key operating parameters of carbon electrodes: electronic properties, interaction with water and thermal stability.

  10. Improvement of β-TCP/PLLA biodegradable material by surface modification with stearic acid.

    Science.gov (United States)

    Ma, Fengcang; Chen, Sai; Liu, Ping; Geng, Fang; Li, Wei; Liu, Xinkuan; He, Daihua; Pan, Deng

    2016-05-01

    Poly-L-lactide (PLLA) is a biodegradable polymer and used widely. Incorporation of beta tricalcium phosphate (β-TCP) into PLLA can enhance its osteoinductive properties. But the interfacial layer between β-TCP particles with PLLA matrix is easy to be destroyed due to inferior interfacial compatibility of the organic/inorganic material. In this work, a method of β-TCP surface modification with stearic acid was investigated to improve the β-TCP/PLLA biomaterial. The effects of surface modification on the β-TCP were investigated by FTIR, XPS, TGA and CA. It was found that the stearic acid reacted with β-TCP and oxhydryl was formed during the surface modification. Hydrophilicity of untreated or modified β-TCP/PLLA composite was increased by the addition of 10 wt.% β-TCP, but it decreased as the addition amount increased from 10 wt.% to 20 wt.%. Two models were suggested to describe the effect of β-TCP concentration on CA of the composites. Mechanical properties of β-TCP/PLLA composites were tested by bending and tensile tests. Fractures of the composites after mechanical test were observed by SEM. It was found that surface modification with stearic acid improved bending and tensile strengths of the β-TCP/PLLA composites obviously. The SEM results indicated that surface modification decreased the probability of interface debonding between fillers and matrix under load. Copyright © 2016 Elsevier B.V. All rights reserved.

  11. Surface modification of fluorocarbon polymers by synchrotron radiation

    CERN Document Server

    Kanda, K; Matsui, S; Ideta, T; Ishigaki, H

    2003-01-01

    The surface modification of a poly (tetrafluoroethylene) sheet was carried out by synchrotron radiation in the soft X-ray region. The poly (tetrafluoroethylene) substrate was exposed to synchrotron radiation while varying the substrate temperature from room temperature to 200degC. The contact angle of the modified surfaces with a water drop decreased from 96deg to 72deg by the irradiation at room temperature, while the contact angle increased to 143deg by the irradiation at the substrate temperature of 200degC. Scanning electron microscopy suggested that this repellence was ascribable to the microstructure of the poly (tetrafluoroethylene) surface. We succeeded in controlling the wettability of the poly (tetrafluoroethylene) surface from hydrophobic to hydrophilic by irradiation of the soft X-ray light. (author)

  12. Research Progress of Optical Fabrication and Surface-Microstructure Modification of SiC

    Directory of Open Access Journals (Sweden)

    Fang Jiang

    2012-01-01

    Full Text Available SiC has become the best candidate material for space mirror and optical devices due to a series of favorable physical and chemical properties. Fine surface optical quality with the surface roughness (RMS less than 1 nm is necessary for fine optical application. However, various defects are present in SiC ceramics, and it is very difficult to polish SiC ceramic matrix with the 1 nm RMS. Surface modification of SiC ceramics must be done on the SiC substrate. Four kinds of surface-modification routes including the hot pressed glass, the C/SiC clapping, SiC clapping, and Si clapping on SiC surface have been reported and reviewed here. The methods of surface modification, the mechanism of preparation, and the disadvantages and advantages are focused on in this paper. In our view, PVD Si is the best choice for surface modification of SiC mirror.

  13. Plasma based Ar+ beam assisted poly(dimethylsiloxane) surface modification

    International Nuclear Information System (INIS)

    Vladkova, T.G.; Keranov, I.L.; Dineff, P.D.; Youroukov, S.Y.; Avramova, I.A.; Krasteva, N.; Altankov, G.P.

    2005-01-01

    Plasma based Ar + beam performed in RF (13.56 MHz) low-pressure (200 mTorr) glow discharge (at 100 W, 1200 W and 2500 W) with a serial capacitance was employed for surface modification of poly(dimethylsiloxane) (PDMS) aimed at improvement of its interactions with living cells. The presence of a serial capacitance ensures arise of an ion-flow inside the plasma volume directed toward the treated sample and the vary of the discharge power ensures varied density of the ion-flow. XPS analysis was performed to study the changes in the surface chemical composition of the modified samples and the corresponding changes in the surface energy were monitored by contact angle measurements. We found that plasma based Ar + beam transforms the initially hydrophobic PDMS surface into a hydrophilic one mainly due to a raising of the polar component of the surface tension, this effect being most probably due to an enrichment of the modified surface layer with permanent dipoles of a [SiO x ]-based network and elimination of the original methyl groups. The initial adhesion of human fibroblast cells was studied on the described above plasma based Ar + beam modified and acrylic acid (AA) grafted or not fibronectin (FN) pre-coated or bare surfaces. The cell response seems to be related with the peculiar structure and wettability of the modified PDMS surface layer after plasma based Ar + beam treatment followed or not by AA grafting

  14. Surface Modifications of Support Partitions for Stabilizing Biomimetic Membrane Arrays

    DEFF Research Database (Denmark)

    Perry, Mark; Hansen, Jesper Schmidt; Jensen, Karin Bagger Stibius

    2011-01-01

    Black lipid membrane (BLM) formation across apertures in an ethylene tetra-fluoroethylene (ETFE) partition separating two aqueous compartments is an established technique for the creation of biomimetic membranes. Recently multi-aperture BLM arrays have attracted interest and in order to increase...... with a high signal-to-noise (s/n) ratio. We demonstratesd this by reconstituting gA and α-hemolysin (α-HL) into BLM arrays. The improvement in membrane array lifetime and s/n ratio demonstrates that surface plasma polymerization of the supporting partition can be used to increase the stability of biomimetic...... modified partitions were similar and significantly lower than for arrays formed using untreated ETFE partitions. For single side n-hexene modification average membrane array lifetimes were not significantly changed compared to untreated ETFE. Double-sided n-hexene modification greatly improved average...

  15. Effective modification of particle surface properties using ultrasonic water mist

    DEFF Research Database (Denmark)

    Genina, Natalja; Räikkönen, Heikki; Heinämäki, Jyrki

    2009-01-01

    The goal of the present study was to design a new technique to modify particle surface properties and, through that, to improve flowability of poorly flowing drug thiamine hydrochloride and pharmaceutical sugar lactose monohydrate of two different grades. The powdered particles were supplied...... properties. It was found that rapid exposition of pharmaceutical materials by water mist resulted in the improvement of powder technical properties. The evident changes in flowability of coarser lactose were obviously due to smoothing of particle surface and decreasing in the level of fines with very slight...... increment in particle size. The changes in thiamine powder flow were mainly due to narrowing in particle size distribution where the tendency for better flow of finer lactose was related to surface and size modifications. The aqueous mist application did not cause any alteration of the crystal structures...

  16. Simple surface modification of poly(dimethylsiloxane) for DNA hybridization

    Science.gov (United States)

    Zhou, Jinwen; Voelcker, Nicolas H.; Ellis, Amanda V.

    2010-01-01

    Here, we present a simple chemical modification of poly(dimethylsiloxane) (PDMS) by curing a mixture of 2 wt% undecylenic acid (UDA) in PDMS prepolymer on a gold-coated glass slide. This gold slide had been previously pretreated with a self-assembled hydrophilic monolayer of 3-mercaptopropionic acid (MPA). During curing of the UDA∕PDMS prepolymer, the hydrophilic UDA carboxyl moieties diffuses toward the hydrophilic MPA carboxyl moieties on the gold surface. This diffusion of the UDA within the PDMS prepolymer to the surface is a direct result of surface energy minimization. Once completely cured, the PDMS is peeled off the gold substrate, thereby exposing the interfacial carboxyl groups. These groups are then available for subsequent attachment of 5′-amino terminated DNA oligonucleotides via amide linkages. Our results show that the covalently tethered oligonucleotides can successfully capture fluorescein-labeled complementary oligonucleotides via hybridization, which are visualized using fluorescence microscopy. PMID:21264061

  17. [Surface grafting modification and stabilization of Kevlar fiber].

    Science.gov (United States)

    Zheng, Yu-ying; Fu, Ming-lian; Wang, Can-yao; Wang, Liang-en

    2005-11-01

    Chemical disposal was used to bring the activity group onto the surface of Kevlar fiber for the purpose of surface grafting modification. The interfacial constitution of the grafting of toluene-2,4-diisocyanate (TDI) onto Kevlar fiber was determined by Fourier transform infrared spectroscopy. In the mean time, hexyl-lactam stabilization and poly-glycol (400, PEG) stabilization on the grafted product were also studied. The effects of different nTDI:nPEG ratios on the production's interfacial constitution was analysed. It is concluded that the stabilization took place on the surface. The intensity of the bands relented at about 3300 cm(-1) and was reinforced at about 1700-1720 cm(-1) when the ratio of nTDI:nPEG = 1:3, but when the ratio is 1:1 and 1:2, the bands at about 3 300 and 1700-1720 cm(-1) are almost the same.

  18. Rational surface silane modification for immobilizing glucose oxidase.

    Science.gov (United States)

    Tian, Feibao; Guo, Yi; Lin, Feifei; Zhang, Yumei; Yuan, Qipeng; Liang, Hao

    2016-06-01

    Glucose oxidase (GOx) has many significant applications in biosensor and biocatalysis. In this study, we firstly quantitatively analyzed the binding efficiency of (3-aminopropyl) trimethoxysilane (APTES) modified onto the surface of GOx. It was found that the contents of the grafted silane did not significantly influence the relative activities and tertiary structures of all surface modified GOxs. Immobilization ratio and relative activity of all instances of APTES modified GOx increased, compared with those of native enzyme. However, good stability of immobilized GOx at extreme pH and high temperature could only be obtained when modified protein with low binding silane content. At pH 2.0, the immobilized GOx with low binding content showed a more than 600% activity, compared to the free enzyme. Therefore, rational surface modification would be beneficial to improving the activity and stability of immobilized enzyme as well as increasing loading amount. Copyright © 2016 Elsevier B.V. All rights reserved.

  19. Surface Modification of Polymeric Materials by Plasma Treatment

    Directory of Open Access Journals (Sweden)

    E.F. Castro Vidaurre

    2002-03-01

    Full Text Available Low-temperature plasma treatment has been used in the last years as a useful tool to modify the surface properties of different materials, in special of polymers. In the present work low temperature plasma was used to treat the surface of asymmetric porous substrates of polysulfone (PSf membranes. The main purpose of this work was to study the influence of the exposure time and the power supplied to argon plasma on the permeability properties of the membranes. Three rf power levels, respectively 5, 10 and 15 W were used. Treatment time ranged from 1 to 50 min. Reduction of single gas permeability was observed with Ar plasma treatments at low energy bombardment (5 W and short exposure time (20 min. Higher power and/or higher plasma exposition time causes a degradation process begins. The chemical and structural characterization of the membranes before and after the surface modification was done by AFM, SEM and XPS.

  20. Laser surface modification of stainless steels for cavitation erosion resistance

    Science.gov (United States)

    Kwok, Chi Tat

    1999-12-01

    Austenitic stainless steel UNS S31603 (Fe -17.6Cr -11.2Ni -2.5Mo -1.4Mn -0.4Si -0.03C) has higher pitting corrosion resistance but lower cavitation erosion resistance than that of UNS S30400. This is because of its lower tendency for strain induced martensitic transformation and higher stacking fault energy as compared with those of UNS S30400. In order to improve its cavitation erosion resistance, surface modification of S31603 was performed by laser surface melting and laser surface alloying using a 2-kW CW Nd-YAG laser and a 3-kW CW CO2 laser. For laser surface melting, austenitic stainless steel UNS S30400, super duplex stainless steel UNS S32760 and martensitic stainless steel UNS S42000 were also investigated for comparison purpose. For laser surface alloying, alloying materials including various elements (Co, Cr, Ni, Mo, Mn, Si & C), alloys (AlSiFe & NiCrSiB), ceramics (Si3N 4, SiC, Cr3C2, TiC, CrB & Cr2O 3) and alloys-ceramics (Co-WC, Ni-WC, Ni-Al2O3, Ni-Cr2C3) were used to modify the surface of S31603. The alloyed surface was achieved first by flame spraying or pre-placing of the alloy powder on the S31603 surface and then followed by laser surface remelting. The cavitation erosion characteristics of laser surface modified specimens in 3.5% NaCl solution at 23°C were studied by means of a 20-kHz ultrasonic vibrator at a peak-to-peak amplitude of 30 mum. In addition, their pitting corrosion behaviour was evaluated by electrochemical techniques. The microstructures, compositions, phase changes and damage mechanisms under cavitation erosion were investigated by optical microscopy, SEM, EDAX and X-ray diffractometry. Mechanical properties such as microhardness profile were also examined. The cavitation erosion resistance Re (reciprocal of the mean depth of penetration rate) of laser surface melted S31603 was found to be improved by 22% and was attributed to the existence of tensile residual stress. Improvement on the Re of S42000 was found to be 8.5 times

  1. Surface modification of polymers for biocompatibility via exposure to extreme ultraviolet radiation.

    Science.gov (United States)

    Inam Ul Ahad; Bartnik, Andrzej; Fiedorowicz, Henryk; Kostecki, Jerzy; Korczyc, Barbara; Ciach, Tomasz; Brabazon, Dermot

    2014-09-01

    Polymeric biomaterials are being widely used for the treatment of various traumata, diseases and defects in human beings due to ease in their synthesis. As biomaterials have direct interaction with the extracellular environment in the biological world, biocompatibility is a topic of great significance. The introduction or enhancement of biocompatibility in certain polymers is still a challenge to overcome. Polymer biocompatibility can be controlled by surface modification. Various physical and chemical methods (e.g., chemical and plasma treatment, ion implantation, and ultraviolet irradiation etc.) are in use or being developed for the modification of polymer surfaces. However an important limitation in their employment is the alteration of bulk material. Different surface and bulk properties of biomaterials are often desirable for biomedical applications. Because extreme ultraviolet (EUV) radiation penetration is quite limited even in low density mediums, it could be possible to use it for surface modification without influencing the bulk material. This article reviews the degree of biocompatibility of different polymeric biomaterials being currently employed in various biomedical applications, the surface properties required to be modified for biocompatibility control, plasma and laser ablation based surface modification techniques, and research studies indicating possible use of EUV for enhancing biocompatibility. © 2013 Wiley Periodicals, Inc.

  2. Surface modification of silicon-containing fluorocarbon films prepared by plasma-enhanced chemical vapor deposition

    Science.gov (United States)

    Jin, Yoonyoung; Desta, Yohannes; Goettert, Jost; Lee, G. S.; Ajmera, P. K.

    2005-07-01

    Surface modification of silicon-containing fluorocarbon (SiCF) films achieved by wet chemical treatments and through x-ray irradiation is examined. The SiCF films were prepared by plasma-enhanced chemical vapor deposition, using gas precursors of tetrafluoromethane and disilane. As-deposited SiCF film composition was analyzed by x-ray photoelectron spectroscopy. Surface modification of SiCF films utilizing n-lithiodiaminoethane wet chemical treatment is discussed. Sessile water-drop contact angle changed from 95°+/-2° before treatment to 32°+/-2° after treatment, indicating a change in the film surface characteristics from hydrophobic to hydrophilic. For x-ray irradiation on the SiCF film with a dose of 27.4 kJ/cm3, the contact angle of the sessile water drop changed from 95°+/-2° before radiation to 39°+/-3° after x-ray exposure. The effect of x-ray exposure on chemical bond structure of SiCF films is studied using Fourier transform infrared measurements. Electroless Cu deposition was performed to test the applicability of the surface modified films. The x-ray irradiation method offers a unique advantage in making possible surface modification in a localized area of high-aspect-ratio microstructures. Fabrication of a Ti-membrane x-ray mask is introduced here for selective surface modification using x-ray irradiation.

  3. Application of MEVVA discharge to material surface modification

    International Nuclear Information System (INIS)

    Gao Yu; Geng Man; Huang Yuming; Gong Xiaorong; Yu Yijun; Tang Deli; Tie Jun

    1996-01-01

    The authors describes some characteristics of the MEVVA discharge, the process of generating a cathode-arc plasma and the advantages of the MEVVA discharge compared with the kind of heating-vaporizing-ionizing source. Some practical parameters and the operating process of the MEVVA ion source as well as a plasma source with MEVVA discharge used in a PSII device are presented. Various plasmas having good-quality and high-performance are obtained with MEVVA discharges and have been widely used in sight-line processing and omnibearing ion implantation for material surface modification

  4. Surface modification by EUV laser beam based on capillary discharge

    Czech Academy of Sciences Publication Activity Database

    Frolov, Oleksandr; Koláček, Karel; Schmidt, Jiří; Štraus, Jaroslav; Prukner, Václav; Shukurov, A.

    -, č. 58 (2011), s. 484-487 ISSN 2010-376X. [International Conference on Fusion and Plasma Physics. Bali, Indonésie, 26.10.2011-28.10.2011] R&D Projects: GA AV ČR KAN300100702; GA MŠk LA08024; GA MŠk(CZ) LC528 Institutional research plan: CEZ:AV0Z20430508 Keywords : soft x-ray * EUV * laser * radiation * source * capillary * discharge * plasma * ablation * surface modification Subject RIV: BL - Plasma and Gas Discharge Physics http://www.waset.org/journals/waset/v58/v58-99.pdf

  5. Boiling and quenching heat transfer advancement by nanoscale surface modification.

    Science.gov (United States)

    Hu, Hong; Xu, Cheng; Zhao, Yang; Ziegler, Kirk J; Chung, J N

    2017-07-21

    All power production, refrigeration, and advanced electronic systems depend on efficient heat transfer mechanisms for achieving high power density and best system efficiency. Breakthrough advancement in boiling and quenching phase-change heat transfer processes by nanoscale surface texturing can lead to higher energy transfer efficiencies, substantial energy savings, and global reduction in greenhouse gas emissions. This paper reports breakthrough advancements on both fronts of boiling and quenching. The critical heat flux (CHF) in boiling and the Leidenfrost point temperature (LPT) in quenching are the bottlenecks to the heat transfer advancements. As compared to a conventional aluminum surface, the current research reports a substantial enhancement of the CHF by 112% and an increase of the LPT by 40 K using an aluminum surface with anodized aluminum oxide (AAO) nanoporous texture finish. These heat transfer enhancements imply that the power density would increase by more than 100% and the quenching efficiency would be raised by 33%. A theory that links the nucleation potential of the surface to heat transfer rates has been developed and it successfully explains the current finding by revealing that the heat transfer modification and enhancement are mainly attributed to the superhydrophilic surface property and excessive nanoscale nucleation sites created by the nanoporous surface.

  6. Effect of surface modification on carbon fiber and its reinforced phenolic matrix composite

    International Nuclear Information System (INIS)

    Yuan Hua; Wang Chengguo; Zhang Shan; Lin Xue

    2012-01-01

    Highlights: ► We used very simple and effective modification method to treat PAN-based carbon fiber by liquid oxidation and coupling agent. ► Carbon fiber surface functional groups were analyzed by LRS and XPS. ► Proper treatment of carbon fiber can prove an effective way to increase composite's performance. ► Carbon fiber surface modifications by oxidation and APS could strengthen fiber activity and enlarge surface area as well as its roughness. - Abstract: In this work, polyacrylonitrile (PAN)-based carbon fiber were chemically modified with H 2 SO 4 , KClO 3 and silane coupling agent (γ-aminopropyltriethoxysilane, APS), and carbon fiber reinforced phenolic matrix composites were prepared. The structural and surface characteristics of the carbon fiber were investigated by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), laser Raman scattering (LRS) and Fourier transform infrared spectroscopy (FTIR). Single fiber mechanical properties, specific surface area, composite impact properties and interfacial shear strength (ILSS) were researched to indicate the effects of surface modification on fibers and the interaction between modified fiber surface and phenolic matrix. The results showed that carbon fiber surface modification by oxidation and APS can strengthen fiber surface chemical activity and enlarge the fiber surface area as well as its roughness. When carbon fiber (CF) is oxidized treatment, the oxygen content as well as the O/C ratio will be obviously increased. Oxygen functional groups increase with oxidation time increasing. Carbon fiber treated with APS will make C-O-R content increase and O-C=O content decrease due to surface reaction. Proper treatment of carbon fiber with acid and silane coupling agent prove an effective way to increase the interfacial adhesion and improve the mechanical and outdoor performance of the resulting fiber/resin composites.

  7. Precise surface modification of polymethyl-methacrylate with near-infrared femtosecond laser

    Energy Technology Data Exchange (ETDEWEB)

    Caballero-Lucas, F.; Florian, C.; Fernández-Pradas, J.M., E-mail: jmfernandez@ub.edu; Morenza, J.L.; Serra, P.

    2015-05-01

    Highlights: • Ablation of lines in PMMA with femtosecond laser pulses. • z-Scan transmittance study for controlling the sample surface position in the laser beam waist. • Bulk material modifications appear below lines if beam waist is inside the sample. • Extended range of few microns for placing the sample and getting similar ablation features. - Abstract: The fabrication of lines at the surface of polymethyl-methacrylate (PMMA) was studied. A femtosecond laser with pulse duration of 450 fs and wavelength of 1027 nm was used. The z-scan method was employed as a focusing procedure to control the sample position with respect to the beam waist through transmittance measurements. This allowed the production of continuous lines with a length of 2 mm on the surface of the PMMA sample. The variation of the lines profiles and dimensions was studied for different values of the sample position with reference to the beam waist. Also effects on the lines fabricated at different values of incident energy and separation on the sample surface between consecutive impinging laser pulses were investigated. A range of positions where lines with similar features and sizes were produced was obtained. Submicrometric surface modifications were achieved as surface swelling in form of successive bumps. After inspecting the sample cross section, it was observed that depending on the relative position of the beam waist regarding the sample surface, inner modifications appear under the modified material surface.

  8. Modification of TOPSIS method for solving of multicriteria tasks

    Directory of Open Access Journals (Sweden)

    Marković Zoran

    2010-01-01

    Full Text Available This paper describes the possible modifications of one of the multi-criteria analysis methods that possess certain advantages in cases of solving the real business problems. We will discuss the TOPSIS method, whereas the modification reflects in change of the determination manner of the ideal and anti-ideal points in criteria environment, in standardization of quantification and fuzzycation of the attributes in cases of criteria expressed by linguistic variables.

  9. Chemical Modification: an Effective Way of Avoiding the Collapse of SWNTs on Al Surface Revealed by Molecular Dynamics Simulations

    DEFF Research Database (Denmark)

    Xie, J.; Xue, Q. Z.; Yan, K. Y.

    2009-01-01

    The rapid collapse of intrinsic single-walled carbon nanotube (SWNT) on the aluminum surface is observed using molecular dynamics simulation. The collapsing threshold is similar to 10 angstrom, and the length has no influence on its collapse. Furthermore, we report that the structural stability...... of cylindrical SWNTs oil the aluminum surface can be improved through the surface modification method. The stability of SWNTs call be enhanced by increasing the modification coverage. When the modification coverage exceeds 3.3% and 3.8% coverage, respectively, both amidogen- and carboxyl-modified SWNTs can...... basically maintain the cylindrical structure in our described systems. The results also show that, to avoid SWNTs collapse by chemical modification, the longer and larger SWNTs are, the more modification coverage SWNTs require. and vice versa. Our method allows potentially used modified SWNTs...

  10. Carbon ion irradiation induced surface modification of polypropylene

    International Nuclear Information System (INIS)

    Saha, A.; Chakraborty, V.; Dutta, R.K.; Chintalapudi, S.N.

    2001-01-01

    Polypropylene was irradiated with 12 C ions of 3.6 and 5.4 MeV energies in the fluence range of 5x10 13 -5x10 14 ions/cm 2 using 3 MV tandem accelerator. Ion penetration was limited to a few microns and surface modifications were investigated by scanning electron microscopy. At the lowest ion fluence only blister formation of various sizes (1-6 μm) were observed, but at higher fluence (1x10 14 ions/cm 2 ) a three-dimensional network structure was found to form. A gradual degradation in the network structure was observed with further increase in the ion fluence. The dose dependence of the changes on surface morphology of polypropylene is discussed

  11. Carbon ion irradiation induced surface modification of polypropylene

    Energy Technology Data Exchange (ETDEWEB)

    Saha, A. E-mail: abhijit@alpha.iuc.res.in; Chakraborty, V.; Dutta, R.K.; Chintalapudi, S.N

    2001-12-01

    Polypropylene was irradiated with {sup 12}C ions of 3.6 and 5.4 MeV energies in the fluence range of 5x10{sup 13}-5x10{sup 14} ions/cm{sup 2} using 3 MV tandem accelerator. Ion penetration was limited to a few microns and surface modifications were investigated by scanning electron microscopy. At the lowest ion fluence only blister formation of various sizes (1-6 {mu}m) were observed, but at higher fluence (1x10{sup 14} ions/cm{sup 2}) a three-dimensional network structure was found to form. A gradual degradation in the network structure was observed with further increase in the ion fluence. The dose dependence of the changes on surface morphology of polypropylene is discussed.

  12. Surface modification of biomaterials and biomedical devices using additive manufacturing.

    Science.gov (United States)

    Bose, Susmita; Robertson, Samuel Ford; Bandyopadhyay, Amit

    2018-01-15

    The demand for synthetic biomaterials in medical devices, pharmaceutical products and, tissue replacement applications are growing steadily due to aging population worldwide. The use for patient matched devices is also increasing due to availability and integration of new technologies. Applications of additive manufacturing (AM) or 3D printing (3DP) in biomaterials have also increased significantly over the past decade towards traditional as well as innovative next generation Class I, II and III devices. In this review, we have focused our attention towards the use of AM in surface modified biomaterials to enhance their in vitro and in vivo performances. Specifically, we have discussed the use of AM to deliberately modify the surfaces of different classes of biomaterials with spatial specificity in a single manufacturing process as well as commented on the future outlook towards surface modification using AM. It is widely understood that the success of implanted medical devices depends largely on favorable material-tissue interactions. Additive manufacturing has gained traction as a viable and unique approach to engineered biomaterials, for both bulk and surface properties that improve implant outcomes. This review explores how additive manufacturing techniques have been and can be used to augment the surfaces of biomedical devices for direct clinical applications. Copyright © 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  13. Surface charging, discharging and chemical modification at a sliding contact

    International Nuclear Information System (INIS)

    Singh, S. V.; Kusano, Y.; Morgen, P.; Michelsen, P. K.

    2012-01-01

    Electrostatic charging, discharging, and consequent surface modification induced by sliding dissimilar surfaces have been studied. The surface-charge related phenomena were monitored by using a home-built capacitive, non-contact electrical probe, and the surface chemistry was studied by X-ray photoelectron spectroscopy (XPS). The experiments were performed on the disk surface of a ball-on-rotating-disk apparatus; using a glass disk and a Teflon (polytetrafluoroethylene) ball arrangement, and a polyester disks and a diamondlike carbon (DLC) coated steel ball arrangement. The capacitive probe is designed to perform highly resolved measurements, which is sensitive to relative change in charge density on the probed surface. For glass and Teflon arrangement, electrical measurements show that the ball track acquires non-uniform charging. Here not only the increase in charge density, but interestingly, increase in number of highly charged regions on the ball track was resolved. Threefold increase in the number of such highly charged regions per cycle was detected immediately before the gas breakdown-like incidences compared to that of other charge/discharge incidences at a fixed disk rotation speed. We are also able to comment on the behavior and the charge decay time in the ambient air-like condition, once the sliding contact is discontinued. XPS analysis showed a marginal deoxidation effect on the polyester disks due to the charging and discharging of the surfaces. Moreover, these XPS results clearly indicate that the wear and friction (sliding without charging) on the surface can be discarded from inducing such a deoxidation effect.

  14. Recent advances in synthesis and surface modification of superparamagnetic iron oxide nanoparticles with silica

    Energy Technology Data Exchange (ETDEWEB)

    Sodipo, Bashiru Kayode, E-mail: bashirsodipo@gmail.com [School of Physics, Universiti Sains Malaysia, 11800 Pulau Pinang (Malaysia); Nano-Biotechnology Research and Innovation (NanoBRI), Institute for Research in Molecular Medicine (INFORMM), Universiti Sains Malaysia, 11800 Pulau Pinang (Malaysia); Aziz, Azlan Abdul [School of Physics, Universiti Sains Malaysia, 11800 Pulau Pinang (Malaysia); Nano-Biotechnology Research and Innovation (NanoBRI), Institute for Research in Molecular Medicine (INFORMM), Universiti Sains Malaysia, 11800 Pulau Pinang (Malaysia)

    2016-10-15

    Research on synthesis of superparamagnetic iron oxide nanoparticles (SPION) and its surface modification for biomedical applications is of intense interest. Due to superparamagnetic property of SPION, the nanoparticles have large magnetic susceptibility, single magnetic domain and controllable magnetic behaviour. However, owing to easy agglomeration of SPION, surface modification of the magnetic particles with biocompatible materials such as silica nanoparticle has gained much attention in the last decade. In this review, we present recent advances in synthesis of SPION and various routes of producing silica coated SPION. - Highlights: • We present recent advances in synthesis of SPION and various routes of producing silica coated SPION • The synthetic routes of producing SPION can be classified into three: physical, chemical and biological methods. • The chemical method is the most cited method of producing SPION and it sub-classified into liquid and gas phase. • The techniques of producing silica coated SPION is grouped into seeded and non-seeded methods.

  15. Surface modification of polystyrene with atomic oxygen radical anions-dissolved solution

    International Nuclear Information System (INIS)

    Wang Lian; Yan Lifeng; Zhao Peitao; Torimoto, Yoshifumi; Sadakata, Masayoshi; Li Quanxin

    2008-01-01

    A novel approach to surface modification of polystyrene (PS) polymer with atomic oxygen radical anions-dissolved solution (named as O - water) has been investigated. The O - water, generated by bubbling of the O - (atomic oxygen radical anion) flux into the deionized water, was characterized by UV-absorption spectroscopy and electron paramagnetic resonance (EPR) spectroscopy. The O - water treatments caused an obvious increase of the surface hydrophilicity, surface energy, surface roughness and also caused an alteration of the surface chemical composition for PS surfaces, which were indicated by the variety of contact angle and material characterization by atomic force microscope (AFM) imaging, field emission scanning electron microscopy (FESEM), X-ray photoelectron spectroscopy (XPS), and attenuated total-reflection Fourier transform infrared (ATR-FTIR) measurements. Particularly, it was found that some hydrophilic groups such as hydroxyl (OH) and carbonyl (C=O) groups were introduced onto the polystyrene surfaces via the O - water treatment, leading to the increases of surface hydrophilicity and surface energy. The active oxygen species would react with the aromatic ring molecules on the PS surfaces and decompose the aromatic compounds to produce hydrophilic hydroxyl and carbonyl compounds. In addition, the O - water is also considered as a 'clean solution' without adding any toxic chemicals and it is easy to be handled at room temperature. Present method may suit to the surface modification of polymers and other heat-sensitive materials potentially

  16. On a modification method of Lefschetz thimbles

    Directory of Open Access Journals (Sweden)

    Tsutsui Shoichiro

    2018-01-01

    Full Text Available The QCD at finite density is not well understood yet, where standard Monte Carlo simulation suffers from the sign problem. In order to overcome the sign problem, the method of Lefschetz thimble has been explored. Basically, the original sign problem can be less severe in a complexified theory due to the constancy of the imaginary part of an action on each thimble. However, global phase factors assigned on each thimble still remain. Their interference is not negligible in a situation where a large number of thimbles contribute to the partition function, and this could also lead to a sign problem. In this study, we propose a method to resolve this problem by modifying the structure of Lefschetz thimbles such that only a single thimble is relevant to the partition function. It can be shown that observables measured in the original and modified theories are connected by a simple identity. We exemplify that our method works well in a toy model.

  17. Surface modification of lignocellulosic fibers using high-frequency ultrasound

    Science.gov (United States)

    Jayant B. Gadhe; Ram B. Gupta; Thomas Elder

    2005-01-01

    Enzymatic and chemical oxidation of fiber surfaces has been reported in the literature as a method for producing medium density fiberboards without using synthetic adhesives. This work focuses on modifying the surface properties of wood fibers by the generation of free radicals using high-frequency ultrasound. A sonochemical reactor operating at 610 kHz is used to...

  18. Microwave assisted organic modification and surface functionalization of Phyllosilicates

    CSIR Research Space (South Africa)

    Kesavan Pillai, Sreejarani

    2012-11-01

    Full Text Available Organically modified phyllosilicates (montmorillonite and palygorskite) using Arquad 2HT-75 surfactant were effectively synthesized utilizing a microwave irradiation technique. The microwave method was successfully used also for the surface...

  19. Roughened titanium surfaces with silane and further RGD peptide modification in vitro

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Wen-Cheng, E-mail: wencchen@fcu.edu.tw [Advanced Medical Devices and Composites Laboratory, Department of Fiber and Composite Materials, College of Engineering, Feng Chia University, Taichung 40724, Taiwan, ROC (China); Ko, Chia-Ling [School of Dentistry, College of Dental Medicine, Kaohsiung Medical University, Kaohsiung 807, Taiwan, ROC (China)

    2013-07-01

    The strategy to achieve osteoregeneration of dental implants during early-stage regeneration is strongly related to surface conditions for achieving highly successful effects after implantation. Surface modifications, namely, mechanical ground, silanization, bonded and sandblasted with pentasequence Gly-Arg-Gly-Asp-Ser (GRGDS) peptide, and acid-etched with Arg-Gly-Asp (RGD) peptide, were compared for their ability to support cell attachment, proliferation, and differentiation on titanium surfaces. The characteristics and comparative in vitro bio-interactions toward osteoprogenitor cells were tested in the four groups with various surface modifications. Compared with the other groups, the sandblasted and acid-etched, and silane with subsequent RGD peptide modified surfaces had the smallest wetting angle, absence of a significant cell viability difference, and largest quantity of alkaline phosphatase production during the expressions of early-stage cell differentiation. The method of synthesizing GRGDS peptides on roughened titanium surfaces has the potential to provide a combination of early bone regeneration and implant of long-term anchored capabilities. Highlights: • The osteoregeneration during early-stage is strongly related to surface conditions. • The wettability with RGD peptide treated surfaces can be enhanced. • Rougher surface binding with RGD peptide can achieve better osseogeneration. • Surfaces with RGD peptide accelerate the progenitor bone cell mineralization.

  20. Surface modification of multiwall carbon nanotubes by sulfonitric treatment

    Energy Technology Data Exchange (ETDEWEB)

    Gómez, Sofía, E-mail: sofiagomez@cetmic.unlp.edu.ar [Centro de Tecnología de Recursos Minerales y Cerámica (CETMIC), Camino Centenario y 506, C.C.49, M.B. Gonnet B1897ZCA (Argentina); Rendtorff, Nicolás M., E-mail: rendtorff@cetmic.unlp.edu.ar [Centro de Tecnología de Recursos Minerales y Cerámica (CETMIC), Camino Centenario y 506, C.C.49, M.B. Gonnet B1897ZCA (Argentina); Departamento de Química, Facultad de Ciencias Exactas—UNLP, Calle 115 y 47, La Plata 1900 (Argentina); Aglietti, Esteban F., E-mail: eaglietti@cetmic.unlp.edu.ar [Centro de Tecnología de Recursos Minerales y Cerámica (CETMIC), Camino Centenario y 506, C.C.49, M.B. Gonnet B1897ZCA (Argentina); Departamento de Química, Facultad de Ciencias Exactas—UNLP, Calle 115 y 47, La Plata 1900 (Argentina); Sakka, Yoshio, E-mail: SAKKA.Yoshio@nims.go.jp [National Institute for Materials Science, Tsukuba, Ibaraki 305-0047 (Japan); Suárez, Gustavo, E-mail: gsuarez@cetmic.unlp.edu.ar [Centro de Tecnología de Recursos Minerales y Cerámica (CETMIC), Camino Centenario y 506, C.C.49, M.B. Gonnet B1897ZCA (Argentina); Departamento de Química, Facultad de Ciencias Exactas—UNLP, Calle 115 y 47, La Plata 1900 (Argentina)

    2016-08-30

    Highlights: • After the acid treatment highly increase the amount carbonyl and carboxylic groups. • The oxidation of MWCNT generates a high negative charge of it in all the pH range. • It could achieve a good dispersion of the MWCNT in water-based suspension. • There is morphological damage on the surfaces of MWCNT after the acid treatment. • Some surface defects but no shortening were observed by TEM images. - Abstract: Carbon nanotubes are widely used for electronic, mechanical, and optical devices due to their unique structural and quantum characteristics. The species generated by oxidation on the surface of these materials permit binding new reaction chains, which improves the dispersibility, processing and compatibility with other materials. Even though different acid treatments and applications of these CNT have been reported, relatively few research studies have focused on the relationship between the acid treatment and the formation of nanodefects, specific oxidized species or CNT surface defects. In this work, multiwall carbon nanotube (MWCNT) oxidation at 90 °C was characterized in order to determine the acid treatment effect on the surface. It was found that oxidized species are already present in MWCNT without an acid treatment, but there are not enough to cause water-based dispersion. The species were identified and quantified by infrared spectroscopy and X-ray photoelectron spectroscopy. Also, transmission electron microscopy observations showed not only modifications of the oxidized species, but also morphological damage on the surfaces of MWCNT after being subjected to the acid treatment. This effect was also confirmed by Raman spectroscopy. The acid treatment generates higher oxidized species, decreasing the zeta potential in the whole pH range.

  1. Surface modification of polylactic acid films by atmospheric pressure plasma treatment

    Science.gov (United States)

    Kudryavtseva, V. L.; Zhuravlev, M. V.; Tverdokhlebov, S. I.

    2017-09-01

    A new approach for the modification of polylactic acid (PLA) materials using atmospheric pressure plasma (APP) is described. PLA films plasma exposure time was 20, 60, 120 s. The surface morphology and wettability of the obtained PLA films were investigated by atomic force microscopy (AFM) and the sitting drop method. The atmospheric pressure plasma increased the roughness and surface energy of PLA film. The wettability of PLA has been improved with the application of an atmospheric plasma surface treatment. It was shown that it is possible to obtain PLA films with various surface relief and tunable wettability. Additionally, we demonstrated that the use of cold atmospheric pressure plasma for surface activation allows for the immobilization of bioactive compounds like hyaluronic acid (HA) on the surface of obtained films. It was shown that composite PLA-HA films have an increased long-term hydrophilicity of the films surface.

  2. Laser induced surface modification of low temperature cofired ceramics (LTCC)

    Energy Technology Data Exchange (ETDEWEB)

    Duitsch, U.; Rohde, M.; Heidinger, R. [Forschungszentrum Karlsruhe GmbH, Karlsruhe (Germany). Inst. for Materials Research

    2004-07-01

    In the present study a laser induced surface modification process is used to increase the electrical conductivity of ceramic substrates locally. The laser experiments were carried out with a CO{sub 2}-Laser ({lambda}=10,6 {mu}m, cw) on LTCC-Substrates DuPont 951 by using tungsten powder as additive. The resulting microstructures within the modified lines were characterised and changes in the electrical properties have been determined. By means of the laser process and using preheating substrates to avoid thermoshock a composite of LTCC and tungsten particles was produced. The tungsten volume fraction within the modified lines was determined between 15.. 50 vol.%. The electrical conductivity in the paths reached a level of {sigma}=10{sup 5}-10{sup 6} S/m, which is only one or two orders of magnitude below the value of bulk tungsten. (orig.)

  3. Surface modification of titanium for load-bearing applications.

    Science.gov (United States)

    Bose, Susmita; Roy, Mangal; Das, Kakoli; Bandyopadhyay, Amit

    2009-12-01

    Titanium and its alloys are extensively used in load-bearing metallic devices. They are bioinert material and, therefore, get encapsulated after implantation into the living body by a fibrous tissue that isolates them from the surrounding tissues. Here we report modification of titanium surface using bioactive tricalcium phosphates (TCP) and nanoscale TiO2 to enhance cell-materials interaction. We have introduced bioactivity in Ti using laser-assisted coating of TCP and by anodization to grow surface TiO2 at room temperature using a mixed aqueous solution of sodium fluoride, citric acid and sulfuric acid as electrolyte. TCP coating showed a columnar Ti grains at the substrate side of the coating and transitioned to an equiaxed grains at the outside. Coating hardness increased from 882 +/- 67 to 1029 +/- 112 Hv as the volume fraction of TCP increased in the coating. For TiO2 nanotubes, microscopic analysis showed tubes of 50 nm in diameter with wall thickness of 15 nm and typical length between 200 nm and 1 micron based on anodization times. Effects of TCP and nanoscale TiO2 coating on bone cell-material interaction were examined by culturing osteoprecursor cells (OPC1) on coated surfaces. Antibacterial activity analysis using metallic Ag via electrodeposition showed over 99% antibacterial activity against the growth of colonies of Pseudomonas aeruginosa.

  4. EUV: induced ablation and surface modifications of solids

    Science.gov (United States)

    Bartnik, A.; Fiedorowicz, H.; Jarocki, R.; Kostecki, J.; Szczurek, M.; Szczurek, A.; Wachulak, P.

    2011-06-01

    In this work results of investigations concerning ablation and surface modification of polymers and some other solids using a laser-plasma EUV source are presented. The plasma radiation was produced using a gas puff target and was focused with a gold-plated grazing incidence ellipsoidal collector. The ablation process was investigated using a scanning electron microscope (SEM) and a quadrupole mass spectrometer (QMS). The chemical changes were investigated by X-ray photoelectron spectroscopy (XPS). Different kinds of micro- and nanostructures created in nearsurface layers of the materials were obtained. Forms of the structures depend on a particular material and the EUV exposure. In case of some polymers even a single shot was sufficient for creation of the visible changes in surface morphology. In case of inorganic solids visible changes required usually the exposure with tens or hundreds of EUV pulses. XPS investigations revealed chemical changes in near surface layers of polymers. Significant differences were revealed in the XPS spectra acquired for irradiated and not-irradiated polymers. Significant decrease of functional groups containing oxygen was indicated. Analysis of QMS spectra indicate emission of different kinds of fragments of the polymer chains including the repeating structural units. In case of some polymers only fragments of the repeating unit were detected.

  5. Materials surface damage and modification under high power plasma exposures

    Science.gov (United States)

    Garkusha, I.; Makhlaj, V.; Byrka, O.; Taran, V.; Voitsenya, V.; Malykhin, S.; Herashchenko, S.; Surovitskiy, S.; Nowakowska-Langier, K.; Sadowski, M. J.; Skladnik-Sadowska, E.; Terentyev, D.

    2018-01-01

    Influence of powerful plasma impacts on several materials used for the construction of energy systems, i.e. different grades of steels as well as tungsten coatings, has been discussed. Irradiations of these materials with hydrogen and helium plasma streams have been performed in several high-current-pulse and quasi-stationary plasma accelerators which provided the variation of a power load upon the exposed surface as well as changes of the particle flux in wide ranges: the energy flux density in the range of 1-25 MJ/m2, particle flux - up to 1026-1029 ion/m2s, the plasma stream velocity - up to about 500 km/s, and the pulse duration in the range of 1-250 μs. A response of the investigated materials to extreme plasma loads, which are relevant to transient events in fusion reactors, is briefly discussed. It is demonstrated that a broad combination of mechanisms of powerful plasma interactions with various materials includes not only a surface damage caused by different erosion mechanisms, but under certain conditions it may also result in a significant improvement of material properties in the near-surface surface layer of several tens-μm in thickness. Some improvement of the structure and substructure of such a layer may be caused by the high-speed quenching, the shock wave formation and material alloying with plasma- and coating-species. The creation of unique surface structures and a considerable improvement of physical and mechanical properties of different materials can be achieved by the pulsed plasma alloying, i.e. pre-deposited coating modifications and mixing caused by the impacting plasma streams.

  6. Surface-defect induced modifications in the optical properties of α-MnO2 nanorods

    International Nuclear Information System (INIS)

    John, Reenu Elizabeth; Chandran, Anoop; Thomas, Marykutty; Jose, Joshy; George, K.C.

    2016-01-01

    Graphical abstract: - Highlights: • Alpha-MnO 2 nanorods are prepared by chemical method. • Difference in surface defect density is achieved. • Characterized using XRD, Rietveld, XPS, EDS, HR-TEM, BET, UV–vis absorption spectroscopy and PL spectroscopy. • Explains the bandstructure modification due to Jahn–Teller distortions using crystal field theory. • Modification in the intensity of optical emissions related to defect levels validates the concept of surface defect induced tuning of optical properties. - Abstract: The science of defect engineering via surface tuning opens a new route to modify the inherent properties of nanomaterials for advanced functional and practical applications. In this work, two independent synthesis methods (hydrothermal and co-precipitation) are adopted to fabricate α-MnO 2 nanorods with different defect structures so as to understand the effect of surface modifications on their optical properties. The crystal structure and morphology of samples are investigated with the aid of X-ray diffraction (XRD) and high resolution transmission electron microscopy (HRTEM). Atomic composition calculated from energy dispersive spectroscopy (EDS) confirms non-stoichiometry of the samples. The surface properties and chemical environment are thoroughly studied using X-ray photoelectron spectroscopy (XPS) and Brunauer–Emmett–Teller (BET) analysis. Bond angle variance and bond valence sum are determined to validate distortions in the basic MnO 6 octahedron. The surface studies indicate that the concentration of Jahn–Teller manganese (III) (Mn 3+ ) ion in the samples differ from each other which results in their distinct properties. Band structure modifications due to Jahn–Teller distortion are examined with the aid of ultraviolet–visible (UV) reflectance and photoluminescence (PL) studies. The dual peaks obtained in derivative spectrum conflict the current concept on the bandgap energy of MnO 2 . These studies suggest that

  7. Surface Modification of a Nanoporous Carbon Photoanode upon Irradiation.

    Science.gov (United States)

    Gomis-Berenguer, Alicia; Velo-Gala, Inmaculada; Rodríguez-Castellón, Enrique; Ania, Conchi O

    2016-11-23

    The photocorrosion of a nanoporous carbon photoanode, with low surface functionalization and high performance towards the photoelectrochemical oxidation of water using simulated solar light, was investigated. Two different light configurations were used to isolate the effect of the irradiation wavelength (UV and visible light) on the textural and chemical features of the carbon photoanode, and its long-term photocatalytic performance for the oxygen evolution reaction. A complete characterization of the carbon showed that the photocorrosion of carbon anodes of low functionalization follows a different pathway than highly functionalized carbons. The carbon matrix gets slightly oxidized, with the formation of carboxylic and carbonyl-like moieties in the surface of the carbon anode after light exposure. The oxidation of the carbon occurred due to the photogeneration of oxygen reactive species upon the decomposition of water during the irradiation of the photoanodes. Furthermore, the photoinduced surface reactions depend on the nature of the carbon anode and its ability to photogenerate reactive species in solution, rather than on the wavelength of the irradiation source. This surface modification is responsible for the decreased efficiency of the carbon photoanode throughout long illumination periods, due to the effect of the oxidation of the carbon matrix on the charge transfer. In this work, we have corroborated that, in the case of a low functionalization carbon material, the photocorrosion also occurs although it proceeds through a different pathway. The carbon anode gets gradually slightly oxidized due to the photogeneration of O-reactive species, being the incorporation of the O-groups responsible for the decreased performance of the anode upon long-term irradiation due to the effect of the oxidation of the carbon matrix on the electron transfer.

  8. Surface modification of Ti dental implants by Nd:YVO4 laser irradiation

    International Nuclear Information System (INIS)

    Braga, Francisco J.C.; Marques, Rodrigo F.C.; Filho, Edson de A.; Guastaldi, Antonio C.

    2007-01-01

    Surface modifications have been applied in endosteal bone devices in order to improve the osseointegration through direct contact between neoformed bone and the implant without an intervening soft tissue layer. Surface characteristics of titanium implants have been modified by addictive methods, such as metallic titanium, titanium oxide and hydroxyapatite powder plasma spray, as well as by subtractive methods, such as acid etching, acid etching associated with sandblasting by either AlO 2 or TiO 2 , and recently by laser ablation. Surface modification for dental and medical implants can be obtained by using laser irradiation technique where its parameters like repetition rate, pulse energy, scanning speed and fluency must be taken into accounting to the appropriate surface topography. Surfaces of commercially pure Ti (cpTi) were modified by laser Nd:YVO 4 in nine different parameters configurations, all under normal atmosphere. The samples were characterized by SEM and XRD refined by Rietveld method. The crystalline phases αTi, βTi, Ti 6 O, Ti 3 O and TiO were formed by the melting and fast cooling processes during irradiation. The resulting phases on the irradiated surface were correlated with the laser beam parameters. The aim of the present work was to control titanium oxides formations in order to improve implants osseointegration by using a laser irradiation technique which is of great importance to biomaterial devices due to being a clean and reproducible process

  9. Surface modification of Ti dental implants by Nd:YVO 4 laser irradiation

    Science.gov (United States)

    Braga, Francisco J. C.; Marques, Rodrigo F. C.; Filho, Edson de A.; Guastaldi, Antonio C.

    2007-09-01

    Surface modifications have been applied in endosteal bone devices in order to improve the osseointegration through direct contact between neoformed bone and the implant without an intervening soft tissue layer. Surface characteristics of titanium implants have been modified by addictive methods, such as metallic titanium, titanium oxide and hydroxyapatite powder plasma spray, as well as by subtractive methods, such as acid etching, acid etching associated with sandblasting by either AlO 2 or TiO 2, and recently by laser ablation. Surface modification for dental and medical implants can be obtained by using laser irradiation technique where its parameters like repetition rate, pulse energy, scanning speed and fluency must be taken into accounting to the appropriate surface topography. Surfaces of commercially pure Ti (cpTi) were modified by laser Nd:YVO 4 in nine different parameters configurations, all under normal atmosphere. The samples were characterized by SEM and XRD refined by Rietveld method. The crystalline phases αTi, βTi, Ti 6O, Ti 3O and TiO were formed by the melting and fast cooling processes during irradiation. The resulting phases on the irradiated surface were correlated with the laser beam parameters. The aim of the present work was to control titanium oxides formations in order to improve implants osseointegration by using a laser irradiation technique which is of great importance to biomaterial devices due to being a clean and reproducible process.

  10. Surface modification of Ti dental implants by Nd:YVO{sub 4} laser irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Braga, Francisco J.C. [Materials Science and Technology Center, Institute of Energetic and Nuclear Research, Box 11049 (05422-970), Sao Paulo (Brazil); Marques, Rodrigo F.C. [Magnetic Materials and Colloid Group, Institute of Chemistry, Sao Paulo State University, Box 355, Araraquara (Brazil); Filho, Edson de A. [Biomaterials Group, Institute of Chemistry, Sao Paulo State University, Box 355, Araraquara (Brazil); Guastaldi, Antonio C. [Biomaterials Group, Institute of Chemistry, Sao Paulo State University, Box 355, Araraquara (Brazil)], E-mail: guastald@iq.unesp.br

    2007-09-30

    Surface modifications have been applied in endosteal bone devices in order to improve the osseointegration through direct contact between neoformed bone and the implant without an intervening soft tissue layer. Surface characteristics of titanium implants have been modified by addictive methods, such as metallic titanium, titanium oxide and hydroxyapatite powder plasma spray, as well as by subtractive methods, such as acid etching, acid etching associated with sandblasting by either AlO{sub 2} or TiO{sub 2}, and recently by laser ablation. Surface modification for dental and medical implants can be obtained by using laser irradiation technique where its parameters like repetition rate, pulse energy, scanning speed and fluency must be taken into accounting to the appropriate surface topography. Surfaces of commercially pure Ti (cpTi) were modified by laser Nd:YVO{sub 4} in nine different parameters configurations, all under normal atmosphere. The samples were characterized by SEM and XRD refined by Rietveld method. The crystalline phases {alpha}Ti, {beta}Ti, Ti{sub 6}O, Ti{sub 3}O and TiO were formed by the melting and fast cooling processes during irradiation. The resulting phases on the irradiated surface were correlated with the laser beam parameters. The aim of the present work was to control titanium oxides formations in order to improve implants osseointegration by using a laser irradiation technique which is of great importance to biomaterial devices due to being a clean and reproducible process.

  11. Surface modification to improve fireside corrosion resistance of Fe-Cr ferritic steels

    Science.gov (United States)

    Park, Jong-Hee; Natesan, Krishnamurti; Rink, David L.

    2010-03-16

    An article of manufacture and a method for providing an Fe--Cr ferritic steel article of manufacture having a surface layer modification for corrosion resistance. Fe--Cr ferritic steels can be modified to enhance their corrosion resistance to liquid coal ash and other chemical environments, which have chlorides or sulfates containing active species. The steel is modified to form an aluminide/silicide passivating layer to reduce such corrosion.

  12. Surface modification of biomaterials using plasma immersion ion implantation and deposition

    OpenAIRE

    Lu, Tao; Qiao, Yuqin; Liu, Xuanyong

    2012-01-01

    Although remarkable progress has been made on biomaterial research, the ideal biomaterial that satisfies all the technical requirements and biological functions is not available up to now. Surface modification seems to be a more economic and efficient way to adjust existing conventional biomaterials to meet the current and ever-evolving clinical needs. From an industrial perspective, plasma immersion ion implantation and deposition (PIII&D) is an attractive method for biomaterials owing to it...

  13. Hydrophilic Surface Modification of PDMS Using Atmospheric RF Plasma

    International Nuclear Information System (INIS)

    Hong, Sung M; Kim, Seong H; Kim, Jeong H; Hwang, Hak I

    2006-01-01

    Control of surface properties in microfluidics systems is an indispensable prerequisite for the success of bioanalytical applications. Poly(dimethylsiloxane) (PDMS) microfluidic devices are hampered from unwanted adsorption of biomolecules and the lack of methods to control electroosmotic flow(EOF). Among the various methods of hydrophilic treatment, a new cleaner technology was chosen to treat PDMS. By using atmospheric RF plasma, hydrophilic surfaces can be created. Thus, analysis was conducted with AFM, XPS, and contact angle before and after plasma treatment. Constructing hydrophilic surfaces without changing the true character of that surface has previously been costly and time consuming. But by using atmospheric plasma cost and time are both greatly reduced. There are many other benefits of hydrophilic surface treatment, including the capability to increase adhesion and capillary effects, etc. Also, with hydrophilic treatment of the micro channels on the PDMS surface, surface tension is reduced thus allowing fluids to move easily along those channels. However, the most important aim is to increase the capillary effects without any deposition or chemical treatment

  14. Performance Enhancement of Hybrid Solar Cells via Surface Modification with Diluted P3HT

    International Nuclear Information System (INIS)

    Lim, E L; Yap, C C; Yahaya, M; Salleh, M M

    2013-01-01

    Surface modification of ZnO nanorods with diluted P3HT in inverted hybrid solar cell was studied. ZnO nanorods were grown on ZnO nanoparticles-coated FTO substrate via chemical bath deposition. 0.2 mM solution of Eosin-Y was spin-coated onto ZnO nanorods at a spinning speed of 1000 rpm for 60 s. Diluted P3HT (0.5 mg/ml) was then coated on ZnO nanorods by using two different methods, namely spin coating and immersion technique. The fabrication process was followed by depositing P3HT from a 25 mg/ml solution. A device without surface modification was also made for comparison. The structure of the devices was FTO / Eosin-Y-coated ZnO nanorods/P3HT/Ag. The optical properties of the samples were investigated and the devices performance was characterized by IV measurement under 100 mW/cm 2 simulated AM 1.5G sunlight. It was found that device coated with diluted P3HT via immersion method showed the highest efficiency, followed by without surface modification and that coated with diluted P3HT using spin coating method.

  15. Surface modification of silicon carbide with silane coupling agent and hexadecyl iodiele

    Energy Technology Data Exchange (ETDEWEB)

    Shang, Xujing, E-mail: shangxujing@tju.edu.cn; Zhu, Yumei, E-mail: zymtju@163.com; Li, Zhihong, E-mail: lzhtju@163.com

    2017-02-01

    Highlights: • A novel universal method was performed to enhance hydrophobicity of SiC powder. • The modification effects of KH550 and KH590 were compared and the optimum reaction parameters were established. • Hexadecyl iodiele was successfully grafted on the surface of SiC-KH590 powder. • Surface changes on SiC powder before and after modification were analyzed via FTIR, XPS, SEM. • The related reaction mechanisms were discussed. - Abstract: In this paper, two kinds of silane coupling agents, namely 3-aminopropyl triethoxysilane (KH550) and 3-mercaptopropyl trimethoxysilane (KH590), were adopted as preliminary modifiers to improve the hydrophobic surface properties of silicon carbide (SiC) powder for the first step. The factors that influence the modification effects were investigated by measuring the contact angle. The results showed that KH590 has a better effect than KH550 for the hydrophobic modification of SiC, and the contact angle improved most after SiC powder was reacted with 0.3 g KH590 at 75 °C in aqueous/alcohol solution for 4 h. On account of further enhancement of hydrophobicity, the study was focused on utilizing nucleophilic substitution between KH590 and hexadecyl iodiele to extend the length of alkyl chain. Compared with using KH590 alone, SiC powder modified by KH590 and hexadecyl iodiele showed better water resistance with an increase of contact angle from 106.8° to 127.5°. The Fourier transform infrared spectroscopy (FT-IR) and X-ray photoelectron spectra (XPS) as well as X-ray diffraction (XRD) analysis results showed that KH550/KH590 and hexadecyl iodiele can be covalently bonded to the surface of SiC powder without altering its crystal configuration. This methodology may provide a new way of the modification of inorganic materials in further.

  16. Plasma immersion ion implantation for the efficient surface modification of medical materials

    Energy Technology Data Exchange (ETDEWEB)

    Slabodchikov, Vladimir A., E-mail: dipis1991@mail.ru; Borisov, Dmitry P., E-mail: borengin@mail.ru; Kuznetsov, Vladimir M., E-mail: kuznetsov@rec.tsu.ru [National Research Tomsk State University, Tomsk, 634050 (Russian Federation)

    2015-10-27

    The paper reports on a new method of plasma immersion ion implantation for the surface modification of medical materials using the example of nickel-titanium (NiTi) alloys much used for manufacturing medical implants. The chemical composition and surface properties of NiTi alloys doped with silicon by conventional ion implantation and by the proposed plasma immersion method are compared. It is shown that the new plasma immersion method is more efficient than conventional ion beam treatment and provides Si implantation into NiTi surface layers through a depth of a hundred nanometers at low bias voltages (400 V) and temperatures (≤150°C) of the substrate. The research results suggest that the chemical composition and surface properties of materials required for medicine, e.g., NiTi alloys, can be successfully attained through modification by the proposed method of plasma immersion ion implantation and by other methods based on the proposed vacuum equipment without using any conventional ion beam treatment.

  17. Surface modification of nanodiamond through metal free atom transfer radical polymerization

    Energy Technology Data Exchange (ETDEWEB)

    Zeng, Guangjian; Liu, Meiying; Shi, Kexin; Heng, Chunning; Mao, Liucheng; Wan, Qing; Huang, Hongye [Department of Chemistry, Nanchang University, 999 Xuefu Avenue, Nanchang 330031 (China); Deng, Fengjie, E-mail: fengjiedeng@aliyun.com [Department of Chemistry, Nanchang University, 999 Xuefu Avenue, Nanchang 330031 (China); Zhang, Xiaoyong, E-mail: xiaoyongzhang1980@gmail.com [Department of Chemistry, Nanchang University, 999 Xuefu Avenue, Nanchang 330031 (China); Wei, Yen, E-mail: weiyen@tsinghua.edu.cn [Department of Chemistry and the Tsinghua Center for Frontier Polymer Research, Tsinghua University, Beijing, 100084 (China)

    2016-12-30

    Highlights: • Surface modification of ND with water soluble and biocompatible polymers. • Functionalized ND through metal free surface initiated ATRP. • The metal free surface initiated ATRP is rather simple and effective. • The ND-poly(MPC) showed high dispersibility and desirable biocompatibility. - Abstract: Surface modification of nanodiamond (ND) with poly(2-methacryloyloxyethyl phosphorylcholine) [poly(MPC)] has been achieved by using metal free surface initiated atom transfer radical polymerization (SI-ATRP). The ATRP initiator was first immobilized on the surface of ND through direct esterification reaction between hydroxyl group of ND and 2-bromoisobutyryl bromide. The initiator could be employed to obtain ND-poly(MPC) nanocomposites through SI-ATRP using an organic catalyst. The final functional materials were characterized by {sup 1}H nuclear magnetic resonance, transmission electron microscopy, X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy and thermo gravimetric analysis in detailed. All of these characterization results demonstrated that ND-poly(MPC) have been successfully obtained via metal free photo-initiated SI-ATRP. The ND-poly(MPC) nanocomposites shown enhanced dispersibility in various solvents as well as excellent biocompatibility. As compared with traditional ATRP, the metal free ATRP is rather simple and effective. More importantly, this preparation method avoided the negative influence of metal catalysts. Therefore, the method described in this work should be a promising strategy for fabrication of polymeric nanocomposites with great potential for different applications especially in biomedical fields.

  18. Preparation and Biocompatible Surface Modification of Redox Altered Cerium Oxide Nanoparticle Promising for Nanobiology and Medicine

    Directory of Open Access Journals (Sweden)

    Himansu Sekhar Nanda

    2016-11-01

    Full Text Available The biocompatible surface modification of metal oxide nanoparticles via surface functionalization technique has been used as an important tool in nanotechnology and medicine. In this report, we have prepared aqueous dispersible, trivalent metal ion (samarium-doped cerium oxide nanoparticles (SmCNPs as model redox altered CNPs of biological relevance. SmCNP surface modified with hydrophilic biocompatible (6-{2-[2-(2-methoxy-ethoxy-ethoxy]-ethoxy}-hexyl triethoxysilane (MEEETES were prepared using ammonia-induced ethylene glycol-assisted precipitation method and were characterized using a variety of complementary characterization techniques. The chemical interaction of functional moieties with the surface of doped nanoparticle was studied using powerful 13C cross polarization magic angle sample spinning nuclear magnetic resonance spectroscopy. The results demonstrated the production of the extremely small size MEEETES surface modified doped nanoparticles with significant reduction in aggregation compared to their unmodified state. Moreover, the functional moieties had strong chemical interaction with the surface of the doped nanoparticles. The biocompatible surface modification using MEEETES should also be extended to several other transition metal ion doped and co-doped CNPs for the production of aqueous dispersible redox altered CNPs that are promising for nanobiology and medicine.

  19. Preparation and Biocompatible Surface Modification of Redox Altered Cerium Oxide Nanoparticle Promising for Nanobiology and Medicine

    KAUST Repository

    Nanda, Himansu Sekhar

    2016-11-03

    The biocompatible surface modification of metal oxide nanoparticles via surface functionalization technique has been used as an important tool in nanotechnology and medicine. In this report, we have prepared aqueous dispersible, trivalent metal ion (samarium)-doped cerium oxide nanoparticles (SmCNPs) as model redox altered CNPs of biological relevance. SmCNP surface modified with hydrophilic biocompatible (6-{2-[2-(2-methoxy-ethoxy)-ethoxy]-ethoxy}-hexyl) triethoxysilane (MEEETES) were prepared using ammonia-induced ethylene glycol-assisted precipitation method and were characterized using a variety of complementary characterization techniques. The chemical interaction of functional moieties with the surface of doped nanoparticle was studied using powerful 13C cross polarization magic angle sample spinning nuclear magnetic resonance spectroscopy. The results demonstrated the production of the extremely small size MEEETES surface modified doped nanoparticles with significant reduction in aggregation compared to their unmodified state. Moreover, the functional moieties had strong chemical interaction with the surface of the doped nanoparticles. The biocompatible surface modification using MEEETES should also be extended to several other transition metal ion doped and co-doped CNPs for the production of aqueous dispersible redox altered CNPs that are promising for nanobiology and medicine.

  20. Piezoelectric Accelerometers Modification Based on the Finite Element Method

    DEFF Research Database (Denmark)

    Liu, Bin; Kriegbaum, B.

    2000-01-01

    The paper describes the modification of piezoelectric accelerometers using a Finite Element (FE) method. Brüel & Kjær Accelerometer Type 8325 is chosen as an example to illustrate the advanced accelerometer development procedure. The deviation between the measurement and FE simulation results...

  1. A Simple Modification of Hydrostatic Method of Treatment

    African Journals Online (AJOL)

    takes place during the third stage of labor, or during the 1st h of puerperium.[1] It's a rare life-threatening complication. Incidence varies widely from 1 in 2,000 to ... we can reduce the maternal mortality and morbidity in remote areas where medical aid is scarce - by the simple technique modification of hydrostatic method for ...

  2. A modification of the restricted maximum likelihood method in ...

    African Journals Online (AJOL)

    The existing Restricted Maximum Likelihood Method of obtaining variance component estimates in generalized linear models with random effects is a complicated procedure requiring the value of the parameter it is intended to estimate. This paper addresses this problem by providing a modification to the existing Restricted ...

  3. A short review on Ferrofluids surface modification by natural and biocompatible polymers

    Directory of Open Access Journals (Sweden)

    Mahyar Ebrahimi

    2016-07-01

    Full Text Available This paper provides an overview of how the surface properties of ferromagnetic nanoparticles dispersed in fluids is modified by natural and biocompatible polymers. Among common magnetic nanoparticles, magnetite (Fe3O4 and maghemite (g-Fe203 are popular candidates because of their biocompatibility. Natural polymeric coating materials are the most commonly used biocompatible magnetic nanoparticle coatings. In this paper, recent progresses in the methods of ferrofluids surface modification by the common natural polymers consisting of dextran, chitosan, gelatin and starch are reviewed.

  4. Surface modification of microfibrous materials with nanostructured carbon

    Energy Technology Data Exchange (ETDEWEB)

    Krasnikova, Irina V., E-mail: tokareva@catalysis.ru [Boreskov Institute of Catalysis SB RAS, pr. Ac. Lavrentieva, 5, Novosibirsk 630090 (Russian Federation); National Research Tomsk Polytechnic University, Lenin av., 30, Tomsk 634050 (Russian Federation); Mishakov, Ilya V.; Vedyagin, Aleksey A. [Boreskov Institute of Catalysis SB RAS, pr. Ac. Lavrentieva, 5, Novosibirsk 630090 (Russian Federation); National Research Tomsk Polytechnic University, Lenin av., 30, Tomsk 634050 (Russian Federation); Bauman, Yury I. [Boreskov Institute of Catalysis SB RAS, pr. Ac. Lavrentieva, 5, Novosibirsk 630090 (Russian Federation); Korneev, Denis V. [State Research Center of Virology and Biotechnology VECTOR, Koltsovo, Novosibirsk Region 630559 (Russian Federation)

    2017-01-15

    The surface of fiberglass cloth, carbon and basalt microfibers was modified with carbon nanostructured coating via catalytic chemical vapor deposition (CCVD) of 1,2-dichloroethane. Incipient wetness impregnation and solution combustion synthesis (SCS) methods were used to deposit nickel catalyst on the surface of microfibrous support. Prepared NiO/support samples were characterized by X-ray diffraction analysis and temperature-programmed reduction. The samples of resulted hybrid materials were studied by means of scanning and transmission electron microscopies as well as by low-temperature nitrogen adsorption. The nature of the support was found to have considerable effect on the CCVD process peculiarities. High yield of nanostructured carbon with largest average diameter of nanofibers within the studied series was observed when carbon microfibers were used as a support. This sample characterized with moderate surface area (about 80 m{sup 2}/g after 2 h of CCVD) shows the best anchorage effect. Among the mineral supports, fiberglass tissue was found to provide highest carbon yield (up to 3.07 g/g{sub FG}) and surface area (up to 344 m{sup 2}/g) due to applicability of SCS method for Ni deposition. - Highlights: • The microfibers of different nature were coated with nanostructured carbon layer. • Features of CNF growth and characteristics of hybrid materials were studied. • Appropriate anchorage of CNF layer on microfiber’s surface was demonstrated.

  5. Controlled modification of the structure of polymer surfaces by chemically grafting inorganic species

    Directory of Open Access Journals (Sweden)

    Oréfice Rodrigo Lambert

    1999-01-01

    Full Text Available Many chemical and physical methods, such as plasma, e-beam, sputtering, CVD and others, have been used to modify the structure of polymer surfaces by depositing thin inorganic films. Most of these techniques are based upon the use of high energy sources that ultimately can damage either chemically or physically polymer surfaces. Moreover, these methods are usually not versatile enough to allow the design of structurally and chemically tailored surfaces through the control of the distribution of chemical functionalities throughout the surface. In this work, inorganic species were introduced onto polymer substrates in a controlled manner by performing a sequence of chemical reactions at the surface. Sulfonation followed by silanization reactions were used to graft alkoxysilane species at the surface of poly(aryl sulfones. The heterogeneous chemical modification of poly(aryl sulfones was monitored by FTIR-ATR (Attenuated Total Reflection - FTIR. Model compounds were used to study the chemical reactions occurring during the grafting procedure. The results showed that the developed procedure can allow a controlled introduction of inorganic species onto polymer surfaces. Furthermore, in order to prove that this procedure enables the deposition of specific chemical functionalities onto polymer surfaces that can be used to create chemically and structurally tailored surfaces, silicate films were deposited on previously silanated PAS bioactive glass composites. In vitro tests showed that the surface modified composite can enhance the rates of hydroxy-carbonate-apatite precipitation.

  6. Construction of mechanically durable superhydrophobic surfaces by thermal spray deposition and further surface modification

    Science.gov (United States)

    Chen, Xiuyong; Gong, Yongfeng; Suo, Xinkun; Huang, Jing; Liu, Yi; Li, Hua

    2015-11-01

    Here we report a simple and cost-effective technical route for constructing superhydrophobic surfaces with excellent abrasion resistance on various substrates. Rough surface structures were fabricated by thermal spray deposition of a variety of inorganic materials, and further surface modification was made by applying a thin layer of polytetrafluoroethylene. Results show that the Al, Cu, or NiCrBSi coatings with the surface roughness of up to 13.8 μm offer rough surface profile to complement the topographical morphology in micro-/nano-scaled sizes, and the hydrophobic molecules facilitate the hydrophobicity. The contact angles of water droplets of ∼155° with a sliding angle of up to 3.5° on the samples have been achieved. The newly constructed superhydrophobic coatings tolerate strong abrasion, giving clear insight into their long-term functional applications.

  7. Preparation, characterization, and surface modification of silver nanoparticles in formamide.

    Science.gov (United States)

    Sarkar, Anjana; Kapoor, Sudhir; Mukherjee, Tulsi

    2005-04-28

    The reduction of silver ions in formamide is shown to take place spontaneously at room temperature without addition of any reductant. The growth of Ag particles was found to be dependent on Ag+ ion concentration. In the absence of any stabilizer, deposition of silver film on the glass walls of the container takes place. However, in the presence of poly(N-vinyl-2-pyrrolidone) (PVP) or colloidal silica (SiO2), which are capable of stabilizing silver nanoparticles by complexing and providing support, a clear dispersion was obtained. The formation of the silver nanoparticles under different conditions was investigated through UV-visible absorption spectrophotometry, gas chromatography, and also electron and atomic force microscopic techniques. Atomic force microscopy results for silver films prepared in the absence of any stabilizer showed the formation of polygonal particles with sizes around 100 nm. Transmission electron microscopy results showed that the prepared silver particles in the presence of PVP were around 20 nm. The Ag nanoparticles get oxidized in the presence of chloroform and toluene. Surface modification of silver film was done in the presence of the tetrasodium salt of ethylenediaminetetraaceticacid (Na4EDTA). It was shown that the reactivity of the silver film increased in its presence. The Fermi potential of silver particles in the presence of Na4EDTA seems to lie between -0.33 and -0.446 V vs NHE.

  8. Surface modifications of the Sima de los Huesos fossil humans.

    Science.gov (United States)

    Andrews, P; Fernandez Jalvo, Y

    1997-01-01

    The sample of fossil human bones from the Sima de los Huesos, Atapuerca, has been analysed to trace parts of its taphonomic history. The work reported here is restricted to analysis of the skeletal elements preserved and their surface modifications. Preliminary plans of specimen distribution published 6 years ago indicate that the skeletal elements are dispersed within the cave, but more recent data are not yet available. Most of the fossils are broken, with some breakage when the bone was fresh and some when already partly mineralized, both types showing some rounding. There are few longitudinal breaks on shafts of long bones and so very few bone splinters. All skeletal elements are preserved but in unequal proportions, with elements like femora, humeri and mandibles and teeth with greater structural density being best represented. There is no evidence of weathering or of human damage such as cut marks on any of the human assemblage, but trampling damage is present on most bones. Carnivore damage is also common, with some present on more than half the sample, but it is mostly superficial, either on the surfaces of shafts and articular ends or on the edges of spiral breaks. The sizes and distribution of the carnivore pits indicate extensive canid activity, and this is interpreted as scavenging of the bones in place in the cave. Indications of tooth marks from a larger carnivore indicate the activity possibly of a large felid: the marks are too large to be produced by small canids, with the larger marks concentrated on spiral breaks on the more robust bones, and there is no evidence of bone crushing and splintering in the manner of hyaenas. The nature of the SH human assemblage is also consistent with accumulation by humans, the evidence for this being the lack of other animals, especially the lack of herbivorous animals, associated with the humans, and the high number of individuals preserved.

  9. Surface Modification of Biodegradable Polymers towards Better Biocompatibility and Lower Thrombogenicity

    Science.gov (United States)

    Rudolph, Andreas; Teske, Michael; Illner, Sabine; Kiefel, Volker; Sternberg, Katrin; Grabow, Niels; Wree, Andreas; Hovakimyan, Marina

    2015-01-01

    Purpose Drug-eluting stents (DES) based on permanent polymeric coating matrices have been introduced to overcome the in stent restenosis associated with bare metal stents (BMS). A further step was the development of DES with biodegradable polymeric coatings to address the risk of thrombosis associated with first-generation DES. In this study we evaluate the biocompatibility of biodegradable polymer materials for their potential use as coating matrices for DES or as materials for fully bioabsorbable vascular stents. Materials and Methods Five different polymers, poly(L-lactide) PLLA, poly(D,L-lactide) PDLLA, poly(L-lactide-co-glycolide) P(LLA-co-GA), poly(D,L-lactide-co-glycolide) P(DLLA-co-GA) and poly(L-lactide-co-ε-caprolactone), P(LLA-co-CL) were examined in vitro without and with surface modification. The surface modification of polymers was performed by means of wet-chemical (NaOH and ethylenediamine (EDA)) and plasma-chemical (O2 and NH3) processes. The biocompatibility studies were performed on three different cell types: immortalized mouse fibroblasts (cell line L929), human coronary artery endothelial cells (HCAEC) and human umbilical vein endothelial cells (HUVEC). The biocompatibility was examined quantitatively using in vitro cytotoxicity assay. Cells were investigated immunocytochemically for expression of specific markers, and morphology was visualized using confocal laser scanning (CLSM) and scanning electron (SEM) microscopy. Additionally, polymer surfaces were examined for their thrombogenicity using an established hemocompatibility test. Results Both endothelial cell types exhibited poor viability and adhesion on all five unmodified polymer surfaces. The biocompatibility of the polymers could be influenced positively by surface modifications. In particular, a reproducible effect was observed for NH3-plasma treatment, which enhanced the cell viability, adhesion and morphology on all five polymeric surfaces. Conclusion Surface modification of

  10. Enhancing the Properties of Carbon and Gold Substrates by Surface Modification

    Energy Technology Data Exchange (ETDEWEB)

    Harnisch, Jennifer Anne [Iowa State Univ., Ames, IA (United States)

    2001-01-01

    The properties of both carbon and gold substrates are easily affected by the judicious choice of a surface modification protocol. Several such processes for altering surface composition have been published in literature. The research presented in this thesis primarily focuses on the development of on-column methods to modify carbon stationary phases used in electrochemically modulated liquid chromatography (EMLC). To this end, both porous graphitic carbon (PGC) and glassy carbon (GC) particles have been modified on-column by the electroreduction of arenediazonium salts and the oxidation of arylacetate anions (the Kolbe reaction). Once modified, the carbon stationary phases show enhanced chromatographic performance both in conventional liquid chromatographic columns and EMLC columns. Additionally, one may also exploit the creation of aryl films to by electroreduction of arenediazonium salts in the creation of nanostructured materials. The formation of mercaptobenzene film on the surface of a GC electrode provides a linking platform for the chemisorption of gold nanoparticles. After deposition of nanoparticles, the surface chemistry of the gold can be further altered by self-assembled monolayer (SAM) formation via the chemisorption of a second thiol species. Finally, the properties of gold films can be altered such that they display carbon-like behavior through the formation of benzenehexathiol (BHT) SAMs. BHT chemisorbs to the gold surface in a previously unprecedented planar fashion. Carbon and gold substrates can be chemically altered by several methodologies resulting in new surface properties. The development of modification protocols and their application in the analytical arena is considered herein.

  11. Surface modification of polyethylene/graphene composite using corona discharge

    Science.gov (United States)

    Popelka, Anton; Noorunnisa Khanam, P.; AlMaadeed, Mariam Ali

    2018-03-01

    Polyethylene/graphene composites are suitable for electromagnetic interference shielding applications and are often fabricated as sandwich structures. However, the hydrophobic character of these composites can lead to delamination. Corona treatment was used to enhance the surface hydrophilicity of composites prepared from linear low-density polyethylene (LLDPE) and graphene nanoplatelets (GNPs) with different content (2, 4, 6, and 8 wt.%). This enhancement of wettability also led to good adhesion properties. The presence of GNPs in LLDPE had a positive effect on the surface properties after corona treatment. The surface free energy of the LLDPE/GNP composites increased by almost 64.6% for 2 wt.% of GNPs in the LLDPE/GNP composite, while the surface free energy of neat LLDPE increased by only 38.1%. The best improvement in adhesion properties after corona treatment was observed for 2 wt.% of GNPs in the LLDPE/GNP composite, while peel resistance increased by 137.9%. Various analytical techniques and methods proved that the changes in the surface morphology and chemical composition of the LLDPE/GNP composite after this treatment resulted in an improvement of adhesion.

  12. RF plasma based selective modification of hydrophilic regions on super hydrophobic surface

    International Nuclear Information System (INIS)

    Lee, Jaehyun; Hwang, Sangyeon; Cho, Dae-Hyun; Hong, Jungwoo; Shin, Jennifer H.; Byun, Doyoung

    2017-01-01

    Highlights: • Simple and amenable reforming method for a substrate with disparate patterns of hydrophilic dots on super-hydrophobic surfaces is proposed. • Wettability characteristics and modification mechanism for the surfaces are conducted and revealed through SEM, AFM, WSI, and SIMS. • Several representative materials for various applications are successfully deposited. - Abstract: Selective modification and regional alterations of the surface property have gained a great deal of attention to many engineers. In this paper, we present a simple, a cost-effective, and amendable reforming method for disparate patterns of hydrophilic regions on super-hydrophobic surfaces. Uniform super-hydrophobic layer (Contact angle; CA > 150°, root mean square (RMS) roughness ∼0.28 nm) can be formed using the atmospheric radio frequency (RF) plasma on top of the selective hydrophilic (CA ∼ 70°, RMS roughness ∼0.34 nm) patterns imprinted by electrohydrodynamic (EHD) jet printing technology with polar alcohols (butyl carbitol or ethanol). The wettability of the modified surface was investigated qualitatively utilizing scanning electron microscopy (SEM), atomic force microscopy (AFM), and wavelength scanning interferometer (WSI). Secondary ion mass spectroscopy (SIMS) analysis showed that the alcohol addiction reaction changed the types of radicals on the super-hydrophobic surface. The wettability was found to depend sensitively on chemical radicals on the surface, not on surface morphology (particle size and surface roughness). Furthermore, three different kinds of representative hydrophilic samples (polystyrene nano-particle aqueous solution, Salmonella bacteria medium, and poly(3,4-ethylenediocythiophene) ink) were tested for uniform deposition onto the desired hydrophilic regions. This simple strategy would have broad applications in various research fields that require selective deposition of target materials.

  13. RF plasma based selective modification of hydrophilic regions on super hydrophobic surface

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Jaehyun; Hwang, Sangyeon; Cho, Dae-Hyun [Department of Mechanical Engineering, Sungkyunkwan University, Suwon 16419 (Korea, Republic of); Hong, Jungwoo [Department of Mechanical Engineering, Graduate of Medical Science and Engineering, Korea Advanced Institute of Science and Technology, Daejeon 34141 (Korea, Republic of); Shin, Jennifer H., E-mail: j_shin@kaist.ac.kr [Department of Mechanical Engineering, Graduate of Medical Science and Engineering, Korea Advanced Institute of Science and Technology, Daejeon 34141 (Korea, Republic of); Byun, Doyoung, E-mail: dybyun@skku.edu [Department of Mechanical Engineering, Sungkyunkwan University, Suwon 16419 (Korea, Republic of)

    2017-02-01

    Highlights: • Simple and amenable reforming method for a substrate with disparate patterns of hydrophilic dots on super-hydrophobic surfaces is proposed. • Wettability characteristics and modification mechanism for the surfaces are conducted and revealed through SEM, AFM, WSI, and SIMS. • Several representative materials for various applications are successfully deposited. - Abstract: Selective modification and regional alterations of the surface property have gained a great deal of attention to many engineers. In this paper, we present a simple, a cost-effective, and amendable reforming method for disparate patterns of hydrophilic regions on super-hydrophobic surfaces. Uniform super-hydrophobic layer (Contact angle; CA > 150°, root mean square (RMS) roughness ∼0.28 nm) can be formed using the atmospheric radio frequency (RF) plasma on top of the selective hydrophilic (CA ∼ 70°, RMS roughness ∼0.34 nm) patterns imprinted by electrohydrodynamic (EHD) jet printing technology with polar alcohols (butyl carbitol or ethanol). The wettability of the modified surface was investigated qualitatively utilizing scanning electron microscopy (SEM), atomic force microscopy (AFM), and wavelength scanning interferometer (WSI). Secondary ion mass spectroscopy (SIMS) analysis showed that the alcohol addiction reaction changed the types of radicals on the super-hydrophobic surface. The wettability was found to depend sensitively on chemical radicals on the surface, not on surface morphology (particle size and surface roughness). Furthermore, three different kinds of representative hydrophilic samples (polystyrene nano-particle aqueous solution, Salmonella bacteria medium, and poly(3,4-ethylenediocythiophene) ink) were tested for uniform deposition onto the desired hydrophilic regions. This simple strategy would have broad applications in various research fields that require selective deposition of target materials.

  14. Fluorescent Magnetic Bioprobes by Surface Modification of Magnetite Nanoparticles

    OpenAIRE

    Pinheiro, Paula C.; Daniel-da-Silva, Ana L.; Tavares, Daniela S.; Calatayud, M. Pilar; Goya, Gerardo F.; Trindade, Tito

    2013-01-01

    Bimodal nanoprobes comprising both magnetic and optical functionalities have been prepared via a sequential two-step process. Firstly, magnetite nanoparticles (MNPs) with well-defined cubic shape and an average dimension of 80 nm were produced by hydrolysis of iron sulfate and were then surface modified with silica shells by using the sol-gel method. The Fe3O4@SiO2 particles were then functionalized with the fluorophore, fluorescein isothiocyanate (FITC), mediated by assembled shells of the c...

  15. Rare Earth Ion-Doped Upconversion Nanocrystals: Synthesis and Surface Modification

    Directory of Open Access Journals (Sweden)

    Hongjin Chang

    2014-12-01

    Full Text Available The unique luminescent properties exhibited by rare earth ion-doped upconversion nanocrystals (UCNPs, such as long lifetime, narrow emission line, high color purity, and high resistance to photobleaching, have made them widely used in many areas, including but not limited to high-resolution displays, new-generation information technology, optical communication, bioimaging, and therapy. However, the inherent upconversion luminescent properties of UCNPs are influenced by various parameters, including the size, shape, crystal structure, and chemical composition of the UCNPs, and even the chosen synthesis process and the surfactant molecules used. This review will provide a complete summary on the synthesis methods and the surface modification strategies of UCNPs reported so far. Firstly, we summarize the synthesis methodologies developed in the past decades, such as thermal decomposition, thermal coprecipitation, hydro/solvothermal, sol-gel, combustion, and microwave synthesis. In the second part, five main streams of surface modification strategies for converting hydrophobic UCNPs into hydrophilic ones are elaborated. Finally, we consider the likely directions of the future development and challenges of the synthesis and surface modification, such as the large-scale production and actual applications, stability, and so on, of the UCNPs.

  16. Altering protein surface charge with chemical modification modulates protein–gold nanoparticle aggregation

    International Nuclear Information System (INIS)

    Jamison, Jennifer A.; Bryant, Erika L.; Kadali, Shyam B.; Wong, Michael S.; Colvin, Vicki L.; Matthews, Kathleen S.; Calabretta, Michelle K.

    2011-01-01

    Gold nanoparticles (AuNP) can interact with a wide range of molecules including proteins. Whereas significant attention has focused on modifying the nanoparticle surface to regulate protein–AuNP assembly or influence the formation of the protein “corona,” modification of the protein surface as a mechanism to modulate protein–AuNP interaction has been less explored. Here, we examine this possibility utilizing three small globular proteins—lysozyme with high isoelectric point (pI) and established interactions with AuNP; α-lactalbumin with similar tertiary fold to lysozyme but low pI; and myoglobin with a different globular fold and an intermediate pI. We first chemically modified these proteins to alter their charged surface functionalities, and thereby shift protein pI, and then applied multiple methods to assess protein–AuNP assembly. At pH values lower than the anticipated pI of the modified protein, AuNP exposure elicits changes in the optical absorbance of the protein–NP solutions and other properties due to aggregate formation. Above the expected pI, however, protein–AuNP interaction is minimal, and both components remain isolated, presumably because both species are negatively charged. These data demonstrate that protein modification provides a powerful tool for modulating whether nanoparticle–protein interactions result in material aggregation. The results also underscore that naturally occurring protein modifications found in vivo may be critical in defining nanoparticle–protein corona compositions.

  17. Application of Electron Beams for Surface Modification of Nickel-base Superalloys

    Energy Technology Data Exchange (ETDEWEB)

    Sah, In Jin; Kim, Dong Hoon; Koo, Ja Hyun; Jang, Chang Heui [KAIST, Daejeon (Korea, Republic of)

    2011-05-15

    Wrought Ni-base superalloy, Alloy 617, is considered as candidate metallic materials for intermediate heat exchanger (IHX) of very high temperature gas-cooled reactors (VHTR). IHX will be exposed to the highest temperature over 900 .deg. C for the various applications including hydrogen production. Chromium is essentially added to make Cr-rich oxide layers on the surface. However, it is reported that Cr{sub 2}O{sub 3} reduction phenomena happens under helium coolant with certain amounts of impurities. Protective oxide layer is necessary for long-term stability of the components, and an excessive supply of resources to make that kind of stable oxide is required near the surface when it is destroyed at operating temperature. In this study, proper depth of Al-rich zone is developed using PVD (Physical Vapor Deposition) and EB (Electron Beam) surface alloying methods. The effects of surface modification on high temperature oxidation and self-healing capability are demonstrated

  18. Studies on polyurethane adhesives and surface modification of hydrophobic substrates

    Science.gov (United States)

    Krishnamoorthy, Jayaraman

    studies involved making functionalized, thickness-controlled, wettability-controlled multilayers on hydrophobic substrates and the adsorption of carboxylic acid-terminated poly(styrene-b-isoprene) on alumina/silica substrates. Poly(vinyl alcohol) has been shown to adsorb onto hydrophobic surfaces irreversibly due to hydrophobic interactions. This thin semicrystalline coating is chemically modified using acid chlorides, butyl isocyanate and butanal to form thicker and hydrophobic coatings. The products of the modification reactions allow adsorption of a subsequent layer of poly(vinyl alcohol) that could subsequently be hydrophobized. This 2-step (adsorption/chemical modification) allows layer-by-layer deposition to prepare coatings with thickness, chemical structure and wettability control on any hydrophobic surface. Research on adsorption characteristics of carboxylic acid-terminated poly(styrene-b-isoprene) involved syntheses of block copolymers with the functional group present at specific ends. Comparative adsorption studies for carboxylic acid-terminated and hydrogen-terminated block copolymers was carried out on alumina and silica substrates.

  19. Effects of cementation surface modifications on fracture resistance of zirconia

    Science.gov (United States)

    Srikanth, Ramanathan; Kosmac, Tomaz; Bona, Alvaro Della; Yin, Ling; Zhang, Yu

    2015-01-01

    Objectives To examine the effects of glass infiltration (GI) and alumina coating (AC) on the indentation flexural load and four-point bending strength of monolithic zirconia. Methods Plate-shaped (12 mm × 12 mm × 1.0 mm or 1.5 mm or 2.0 mm) and bar-shaped (4 mm × 3 mm × 25 mm) monolithic zirconia specimens were fabricated. In addition to monolithic zirconia (group Z), zirconia monoliths were glass-infiltrated or alumina-coated on their tensile surfaces to form groups ZGI and ZAC, respectively. They were also glass-infiltrated on their upper surfaces, and glass-infiltrated or alumina-coated on their lower (tensile) surfaces to make groups ZGI2 and ZAC2, respectively. For comparison, porcelain-veneered zirconia (group PVZ) and monolithic lithium disilicate glass-ceramic (group LiDi) specimens were also fabricated. The plate-shaped specimens were cemented onto a restorative composite base for Hertzian indentation using a tungsten carbide spherical indenter with a radius of 3.2 mm. Critical loads for indentation flexural fracture at the zirconia cementation surface were measured. Strengths of bar-shaped specimens were evaluated in four-point bending. Results Glass infiltration on zirconia tensile surfaces increased indentation flexural loads by 32% in Hertzian contact and flexural strength by 24% in four-point bending. Alumina coating showed no significant effect on resistance to flexural damage of zirconia. Monolithic zirconia outperformed porcelain-veneered zirconia and monolithic lithium disilicate glass-ceramics in terms of both indentation flexural load and flexural strength. Significance While both alumina coating and glass infiltration can be used to effectively modify the cementation surface of zirconia, glass infiltration can further increase the flexural fracture resistance of zirconia. PMID:25687628

  20. Biomolecular modification of zirconia surfaces for enhanced biocompatibility

    Energy Technology Data Exchange (ETDEWEB)

    Hsu, Shih-Kuang; Hsu, Hsueh-Chuan [Department of Dental Technology and Materials Science, Central Taiwan University of Science and Technology, Taichung 40601, Taiwan, ROC (China); Ho, Wen-Fu [Department of Chemical and Materials Engineering, National University of Kaohsiung, Taiwan, ROC (China); Yao, Chun-Hsu [Department of Biomedical Imaging and Radiological Science, China Medical University, Taichung 40402, Taiwan, ROC (China); Chang, Pai-Ling [Taoyuan General Hospital, Taoyuan 33004, Taiwan, ROC (China); Wu, Shih-Ching, E-mail: scwu@ctust.edu.tw [Department of Dental Technology and Materials Science, Central Taiwan University of Science and Technology, Taichung 40601, Taiwan, ROC (China)

    2014-12-01

    Yttria-tetragonal zirconia polycrystal (Y-TZP) is a preferred biomaterial due to its good mechanical properties. In order to improve the biocompatibility of zirconia, RGD-peptide derived from extracellular matrix proteins was employed to modify the surface of Y-TZP to promote cell adhesion in this study. The surface of Y-TZP specimens was first modified using a hydrothermal method for different lengths of time. The topographies of modified Y-TZP specimens were analyzed by contact angle, XRD, FTIR, AFM, and FE-SEM. The mechanical properties were evaluated using Vickers hardness and three point bending strength. Then, the RGD-peptide was immobilized on the surface of the Y-TZP by chemical treatment. These RGD-peptide immobilized Y-TZP specimens were characterized by FTIR and AFM, and then were cocultured with MG-63 osteoblast cells for biocompatibility assay. The cell morphology and proliferation were evaluated by SEM, WST-1, and ALP activity assay. The XRD results indicated that the phase transition, from tetragonal phase to monoclinic phase, was increased with a longer incubation time of hydrothermal treatment. However, there were no significant differences in mechanical strengths after RGD-peptide was successfully grafted onto the Y-TZP surface. The SEM images showed that the MG-63 cells appeared polygonal, spindle-shaped, and attached on the RGD-peptide immobilized Y-TZP. The proliferation and cellular activities of MG-63 cells on the RGD-peptide immobilized Y-TZP were better than that on the unmodified Y-TZP. From the above results, the RGD-peptide can be successfully grafted onto the hydrothermal modified Y-TZP surface. The RGD-peptide immobilized Y-TZP can increase cell adhesion, and thus, improve the biocompatibility of Y-TZP. - Highlights: • Covalent bonding between peptide and Y-TZP was proposed. • Stable biomimetic structures produced on the surface of zirconia. • The biocompatibility was improved.

  1. Plasma polymerization surface modification of Carbon black and its effect in elastomers

    NARCIS (Netherlands)

    Mathew, T.; Datta, Rabin; Dierkes, Wilma K.; Talma, Auke; Ooij, W.J.; Noordermeer, Jacobus W.M.

    2011-01-01

    Surface modification of carbon black by plasma polymerization was aimed to reduce its surface energy in order to compatibilize the filler with various elastomers. A fullerenic carbon black was used for the modification process. Thermogravimetric analysis, wetting behavior with liquids of known

  2. New electron-ion-plasma equipment for modification of materials and products surface

    International Nuclear Information System (INIS)

    Koval', N.N.

    2013-01-01

    Electron-ion-plasma treatment of materials and products, including surface clearing and activation, formation surface layers with changed chemical and phase structure, increased hardness and corrosion resistance; deposition of various functional coatings, has received a wide distribution in a science and industry. Widespread methods of ion-plasma modification of material and product surfaces are ion etching and activation, ion-plasma nitriding, arc or magnetron deposition of functional coatings, including nanostructured. The combination of above methods of surface modification allows essentially to improve exploitation properties of treated products and to optimize the characteristics of modified surfaces for concrete final requirements. For the purpose of a combination of various methods of ion-plasma treatment in a single work cycle at Institute of High Current Electronics of SB RAS (IHCE SB RAS) specialized technological equipment 'DUET', 'TRIO' and 'QUADRO' and 'KVINTA' have been developed. This equipment allow generating uniform low-temperature gas plasma at pressures of (0.1-1) Pa with concentration of (10 9 -10 11 ) cm -3 in volume of (0.1-1) m 3 . In the installations consistent realization of several various operations of materials and products treatment in a single work cycle is possible. The operations are preliminary heating and degassing, ion clearing, etching and activation of materials and products surface by plasma of arc discharges; chemicothermal treatment (nitriding) for formation of diffusion layer on a surface of treated sample using plasma of nonself-sustained low-pressure arc discharge; deposition of single- or multilayered superhard (≥40 GPa) nanocrystalline coatings on the basis of pure metals or their compounds (nitrides, carbides, carbonitrides) by the arc plasma-assisted method. For realization of the modes all installations are equipped by original sources of gas and metal plasma. Besides, in

  3. Inexpensive laser-induced surface modification in bismuth thin films

    Energy Technology Data Exchange (ETDEWEB)

    Contreras, A. Reyes [Facultad de Ciencias, Universidad Autónoma del Estado de México, Carretera Toluca, Ixtlahuaca Kilómetro 15.5, C.P. 50200 Edo. de México (Mexico); Hautefeuille, M., E-mail: mathieu_h@ciencias.unam.mx [Facultad de Ciencias, Universidad Nacional Autónoma de México, Avenida Universidad 3000, Circuito Exterior S/N, Coyoacán, Ciudad Universitaria, C.P. 04510 D.F. Mexico (Mexico); García, A. Esparza [Fotofísica y Películas Delgadas, Departamento de Tecnociencias, CCADET-UNAM, Circuito exterior s/n C.P. 04510 Cd. Universitaria, D.F. Mexico (Mexico); Mejia, O. Olea [Centro Conjunto de Investigación en Química Sustentable UAEM-UNAM, Carretera Toluca-Atlacomulco, Km 14.5, Unidad El Rosedal, 50200 San Cayetano, Estado de México (Mexico); López, M.A. Camacho [Facultad de Química, Universidad Autónoma del Estado de México, Tollocan s/n, esq. Paseo Colón, Toluca, Estado de México 50110 (Mexico)

    2015-05-01

    Highlights: • Laser-induced microbumps were formed on bismuth films using a simple, low-cost, laser setup. • The patterns, similar to those typically obtained with high-power lasers, were characterized. • Control of laser ablation conditions is critical in the fabrication of surface microbumps. - Abstract: In this work, we present results on texturing a 500 nm thick bismuth film, deposited by sputtering onto a glass slide using a low-cost homemade, near-infrared pulsed laser platform. A 785 nm laser diode of a CD–DVD pickup head was precisely focused on the sample mounted on a motorized two-axis translation stage to generate localized surface microbumps on the bismuth films. This simple method successfully transferred desired micropatterns on the films in a computer-numerical control fashion. Irradiated zones were characterized by atomic force microscopy and scanning electron microscopy. It was observed that final results are strongly dependent on irradiation parameters.

  4. Effect of surface modification of siliconeon Staphylococcus epidermidis adhesion and colonization.

    Science.gov (United States)

    Tang, Haiying; Cao, Ting; Wang, Anfeng; Liang, Xuemei; Salley, Steven O; McAllister, James P; Ng, K Y Simon

    2007-03-15

    Cerebrospinal fluid (CSF) shunts for the treatment of hydrocephalus are generally made of silicone rubber. The growth of bacterial colonies on the silicone surface leads to frequent CSF shunt complications. A systematic study of the effect of the surface modification of silicone on Staphylococcus epidermidis adhesion and colonization was performed for different incubation times by means of colony counting and scanning electron microscopy (SEM). Silicone was modified with different biopolymers and silanes, including heparin, hyaluronan, octadecyltrichlorosilane (OTS), and fluoroalkylsilane (FAS) to provide a stable and biocompatible surface with different surface functional groups and degrees of hydrophobicity. The modified silicone surfaces were studied by using contact angle measurements, X-ray photoelectron spectroscopy (XPS), and atomic force microscopy (AFM). After 4 and 8 h of incubation, the FAS- and OTS-coated silicone and the hyaluronan coated OTS/silicone surfaces showed significantly reduced bacterial adhesion and colonization compared to blank silicone by both quantification methods. However, the heparin coated OTS/silicone showed significantly increased bacterial adhesion. These results indicate that the nature of the surface functional group and surface roughness determine the extent of bacterial adhesion and colonization. However, the degree of hydrophobicity of the surface did not appear to play a determining role in bacterial adhesion and colonization.

  5. Ion Beam and Plasma Technology Development for Surface Modification at Los Alamos National Laboratory

    Energy Technology Data Exchange (ETDEWEB)

    Davis, H.A.; Munson, C.P.; Wood, B.P.; Bitteker, L.J.; Nastasi, M.A.; Rej, D.J.; Waganaar, W.J.; Walter, K.C. [Los Alamos National Lab., NM (United States); Coates, D.M.; Schleinitz, H.M. [DuPont Central Research and Development, Wilmington, DE (United States)

    1997-12-31

    We are developing two high-throughput technologies for materials modification. The first is a repetitive intense ion beam source for materials modification through rapid surface melt and resolidification (up to 10{sup 10} deg/sec cooling rates) and for ablative deposition of coatings. The short range of the ions (typically 0.1 to 5 micrometers) allows vaporization or melting at moderate beam energy density (typically 1-50 J/cm{sup 2}). A new repetitive intense ion beam accelerator called CHAMP is under development at Los Alamos. The design beam parameters are: E=200 keV, I=15 kA, {tau}=1 {micro}s, and 1 Hz. This accelerator will enable applications such as film deposition, alloying and mixing, cleaning and polishing, corrosion and wear resistance, polymer surface treatments, and nanophase powder synthesis. The second technology is plasma source ion implantation (PSII) using plasmas generated from both gas phase (using radio frequency excitation) and solid phase (using a cathodic arc) sources. We have used PSII to directly implant ions for surface modification or as method for generating graded interfaces to enhance the adhesion of surface coatings. Surfaces with areas of up to 16 m{sup 2} and weighing more than a thousand kilograms have been treated in the Los Alamos PSII chamber. In addition, PSII in combination with cathodic source deposition has been used to form highly adherent, thick Er{sub 2}O{sub 3} coatings on steel for reactive metal containment in casting. These coatings resist delamination under extreme mechanical and thermal stress.

  6. Hydrophobic modification of wood via surface-initiated ARGET ATRP of MMA

    Energy Technology Data Exchange (ETDEWEB)

    Fu Yanchun; Li Gang [Material Science and Engineering College, Northeast Forestry University, Harbin 150040 (China); Yu Haipeng, E-mail: yuhaipeng20000@yahoo.com.cn [Key laboratory of Bio-based Material Science and Technology of Ministry of Education, Northeast Forestry University, Harbin 150040 (China); Material Science and Engineering College, Northeast Forestry University, Harbin 150040 (China); Liu Yixing, E-mail: yxl200488@sina.com [Key laboratory of Bio-based Material Science and Technology of Ministry of Education, Northeast Forestry University, Harbin 150040 (China); Material Science and Engineering College, Northeast Forestry University, Harbin 150040 (China)

    2012-01-15

    To convert the hydrophilic surface of wood into a hydrophobic surface, the present study investigated activators regenerated by electron transfer for atom transfer radical polymerization (ARGET ATRP) as a method of grafting methyl methacrylate (MMA) onto the wood surface. The wood treated with 2-bromoisobutyryl bromide and with the subsequently attached MMA via ARGET ATRP under different polymerization times (2 h, 4 h, 6 h, 8 h) were examined using scanning electron microscopy, Fourier transform infrared spectroscopy, and thermogravimetric analysis. All the analyses confirmed that PMMA had been grafted onto the wood surface. Water contact angle measurement proved that the covering layer of PMMA on wood made the surface hydrophobic. Polymerization time had a positive influence on the contact angle value and higher contact angle can be produced with the prolongation of the polymerization time. When the reaction time was extended to 8 h, the contact angle of treated wood surface reached 130 Degree-Sign in the beginning, and remained at 116 Degree-Sign after 60 s. The ARGET ATRP method may raise an alteration on the wood surface modification.

  7. Surface modification of chitosan/PEO nanofibers by air dielectric barrier discharge plasma for acetylcholinesterase immobilization

    Energy Technology Data Exchange (ETDEWEB)

    Dorraki, Naghme, E-mail: n.dorraki@web.sbu.ac.ir [Laser and Plasma Research Institute, Shahid Beheshti University, Evin 1983963113, Tehran (Iran, Islamic Republic of); Safa, Nasrin Navab [Laser and Plasma Research Institute, Shahid Beheshti University, Evin 1983963113, Tehran (Iran, Islamic Republic of); Jahanfar, Mehdi [Protein Research Center, Shahid Beheshti University, Evin 1983963113, Tehran (Iran, Islamic Republic of); Ghomi, Hamid [Laser and Plasma Research Institute, Shahid Beheshti University, Evin 1983963113, Tehran (Iran, Islamic Republic of); Ranaei-Siadat, Seyed-Omid [Protein Research Center, Shahid Beheshti University, Evin 1983963113, Tehran (Iran, Islamic Republic of)

    2015-09-15

    Highlights: • We used an economical and effective method for surface modification. • Chitosan/PEO nanofibrous membranes were modified by air-DBD plasma. • The most NH{sub 3}{sup +} group was generated on the 6 min plasma modified membrane. • We immobilized acetylcholinesterase on the plasma modified and unmodified membranes. • More enzyme activity was detected on the modified membrane by plasma. - Abstract: There are different methods to modify polymer surfaces for biological applications. In this work we have introduced air-dielectric barrier discharge (DBD) plasma at atmospheric pressure as an economical and safe method for modifying the surface of electrospun chitosan/PEO (90/10) nanofibers for acetylcholinesterase (AChE) immobilization. According to the contact angle measurement results, the nanofibers become highly hydrophilic when they are exposed to the DBD plasma for 6 min in compared to unmodified membrane. Attenuated total reflectance-Fourier transform infrared spectroscopy (ATR-FTIR) results reveal hydroxyl, C=O and NH{sub 3}{sup +} polar groups increment after 6 min plasma treatment. Contact angle measurements and ATR-FTIR results are confirmed by X-ray photoelectron spectroscopy (XPS). AChE at pH 7.4 carries a negative charge and after immobilization on the surface of plasma-treated nanofibrous membrane attracts the NH{sub 3}{sup +} group and more enzyme activity is detected on the plasma-modified nanofibers for 6 min in compared to unmodified nanofibers. Atomic force microscopy (AFM) and scanning electron microscopy (SEM) are used for the surface topography and morphology characterization. The results have proved that air-DBD plasma is a suitable method for chitosan/PEO nanofibrous membrane modification as a biodegradable and functionalized substrate for enzyme immobilization.

  8. A study on the die steel surface modification by electron beam

    CERN Document Server

    Wu Ai Min; Zou Jian Xin; Hao Sheng Zhi; Dong Chuang; Zhang Ai Ming; Xu Tao

    2002-01-01

    A new surface modification technology-high current pulsed electron beam treatment method was applied to the surface of die steel to improve its properties. It has been shown that as a result of the HCPEB treatment, the most pronounced changes of the structure-phase state occur in the near-surface layers quenched from the liquid state, where the crystallization front velocity reaches its maximum. In these layers partial or complete dissolving of second phases and formation of over saturated solid solutions and ordered nano-sized structures may take place. This makes it possible to improve substantially the electrochemical and strength properties of the surface layer. The authors found that the thickness of remelt layer is about 10 mu m, and the sectional microhardness increased accompanied by the enhancement of the wear resistance of the material. After modification, the relative wear resistance of D2 steel have increased 5.63 times and that of H13 steel increased 11.76 times

  9. Influence of E-beam-irradiation on surface modification and micro hardness of recycled polyolefin's

    International Nuclear Information System (INIS)

    Atabaev, B.G.; Gafurov, U.

    2004-01-01

    Full text: The influence of high (E=5MeV) and low (E=0,125MeV) energy -beam irradiation on bulk and surface modification of recycled polypropylene and polyethylene has been investigated. The new techniques for measuring of polymer surface micro hardness, using decoration of indenter imprint under load lower than 100g are developed. It was shown that e-beam irradiation with high-energy lead to rise of surface micro hardness of recycled polypropylene up to two times for 50g load and 30 percent for 25g load with increasing of irradiation dose (D=100,125,150kGy). The bulk and surface modifications depend on cross-links and oxidation processes in recycled polymer under e-beam irradiation. For low energy e-beam irradiation of recycled polyethylene E=0,125MeV and doses D=50,125 kGy the like results took place. The correlation between increasing of micro hardness of irradiated polymers, E-beam radiation stimulated cross-linkage, oxidation processes by IR (FTIR) Spectroscopy method has been investigated

  10. Modification of the surface of superparamagnetic iron oxide nanoparticles to enable their safe application in humans.

    Science.gov (United States)

    Strehl, Cindy; Maurizi, Lionel; Gaber, Timo; Hoff, Paula; Broschard, Thomas; Poole, A Robin; Hofmann, Heinrich; Buttgereit, Frank

    Combined individually tailored methods for diagnosis and therapy (theragnostics) could be beneficial in destructive diseases, such as rheumatoid arthritis. Nanoparticles are promising candidates for theragnostics due to their excellent biocompatibility. Nanoparticle modifications, such as improved surface coating, are in development to meet various requirements, although safety concerns mean that modified nanoparticles require further review before their use in medical applications is permitted. We have previously demonstrated that iron oxide nanoparticles with amino-polyvinyl alcohol (a-PVA) adsorbed on their surfaces have the unwanted effect of increasing human immune cell cytokine secretion. We hypothesized that this immune response was caused by free-floating PVA. The aim of the present study was to prevent unwanted immune reactions by further surface modification of the a-PVA nanoparticles. After cross-linking of PVA to nanoparticles to produce PVA-grafted nanoparticles, and reduction of their zeta potential, the effects on cell viability and cytokine secretion were analyzed. PVA-grafted nanoparticles still stimulated elevated cytokine secretion from human immune cells; however, this was inhibited after reduction of the zeta potential. In conclusion, covalent cross-linking of PVA to nanoparticles and adjustment of the surface charge rendered them nontoxic to immune cells, nonimmunogenic, and potentially suitable for use as theragnostic agents.

  11. Modification of a recuperator construction with CFD methods

    Directory of Open Access Journals (Sweden)

    Ludwig Wojciech

    2017-12-01

    Full Text Available The purpose of the work was initial modification of the construction of a commercially produced heat exchanger – recuperator with CFD (computational fluid dynamics methods, based on designs and process parameters which were provided. Uniformity of gas distribution in the space between the tubes of the apparatus as well as the pressure drop in it were taken as modification criteria. Uniformity of the gas velocity field between the tubes of the heat exchanger should cause equalization of the local individual heat transfer coefficient values and temperature value. Changes of the apparatus construction which do not worsen work conditions of the equipment, but cause savings of constructional materials (elimination or shortening some parts of the apparatus were taken into consideration.

  12. Non-textured laser modification of silica glass surface: Wettability control and flow channel formation

    Science.gov (United States)

    Aono, Yuko; Hirata, Atsushi; Tokura, Hitoshi

    2016-05-01

    Local wettability of silica glass surface is modified by infrared laser irradiation. The silica glass surface exhibits hydrophobic property in the presence of sbnd CF3 or sbnd (CH3)2 terminal functional groups, which are decomposed by thermal treatment, and degree of the decomposition depends on the applied heat. Laser irradiation can control the number of remaining functional groups according to the irradiation conditions; the contact angle of deionized water on the laser modified surfaces range from 100° to 40°. XPS analysis confirms that the variation in wettability corresponds to the number of remaining sbnd CF3 groups. The laser irradiation achieves surface modification without causing any cracks or damages to the surface, as observed by SEM and AFM; moreover, surface transparency to visible light and surface roughness remains unaffected. The proposed method is applied to plane flow channel systems. Dropped water spreads only on the hydrophilic and invisible line modified by the laser irradiation without formation of any grooves. This indicates that the modified line can act as a surface channel. Furthermore, self-transportation of liquid is also demonstrated on a channel with gradually-varied wettability along its length. A water droplet on a hydrophobic side is self-transported to a hydrophilic side due to contact-angle hysteresis force without any actuators or external forces.

  13. Inner surface modification of a tube by magnetic glow-arc plasma source ion implantation

    International Nuclear Information System (INIS)

    Zhang Guling; Chinese Academy of Sciences, Beijing; Wang Jiuli; Feng Wenran; Chen Guangliang; Gu Weichao; Niu Erwu; Fan Songhua; Liu Chizi; Yang Size; Wu Xingfang

    2006-01-01

    A new method named the magnetic glow-arc plasma source ion implantation (MGA-PSII) is proposed for inner surface modification of tubes. In MGA-PSII, under the control of an axial magnetic field, which is generated by an electric coil around the tube sample, glow arc plasma moves spirally into the tube from its two ends. A negative voltage applied on the tube realized its inner surface implantation. Titanium nitride (TiN) films are prepared on the inner surface of a stainless steel tube in diameter 90 mm and length 600 mm. Hardness tests show that the hardness at the tube centre is up to 20 GPa. XRD, XPS and AES analyses demonstrate that good quality of TiN films can be achieved. (authors)

  14. Inner Surface Modification of a Tube by Magnetic Glow-Arc Plasma Source Ion Implantation

    Science.gov (United States)

    Zhang, Gu-Ling; Wang, Jiu-Li; Wu, Xing-Fang; Feng, Wen-Ran; Chen, Guang-Liang; Gu, Wei-Chao; Niu, Er-Wu; Fan, Song-Hua; Liu, Chi-Zi; Yang, Si-Ze

    2006-05-01

    A new method named the magnetic glow-arc plasma source ion implantation (MGA-PSII) is proposed for inner surface modification of tubes. In MGA-PSII, under the control of an axial magnetic field, which is generated by an electric coil around the tube sample, glow arc plasma moves spirally into the tube from its two ends. A negative voltage applied on the tube realized its inner surface implantation. Titanium nitride (TiN) films are prepared on the inner surface of a stainless steel tube in diameter 90 mm and length 600 mm. Hardness tests show that the hardness at the tube centre is up to 20 GPa. XRD, XPS and AES analyses demonstrate that good quality of TiN films can be achieved.

  15. Surface modification of quartz fibres for dental composites through a sol-gel process.

    Science.gov (United States)

    Wang, Yazi; Wang, Renlin; Habib, Eric; Wang, Ruili; Zhang, Qinghong; Sun, Bin; Zhu, Meifang

    2017-05-01

    In this study, quartz fibres (QFs) surface modification using a sol-gel method was proposed and dental posts reinforced with modified QFs were produced. A silica sol (SS) was prepared using tetraethoxysilane (TEOS) and 3-methacryloxypropyltrimethoxysilane (γ-MPS) as precursors. The amount of γ-MPS in the sol-gel system was varied from 0 to 24wt.% with a constant molar ratio of TEOS, ethanol, deionized water, and HCl. Thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FT-IR), and contact angle (CA) measurements were used to characterize the modified QFs, which confirmed that SS had successfully coated the surface of QFs. SEM images showed good interfacial bonding between the modified QFs and the resin matrix. The results of three-point bending tests of the fibre reinforced composite (FRC) posts showed that the QFs modified by SS with 12wt.% γ-MPS presented the best mechanical properties, demonstrating improvements of 108.3% and 89.6% for the flexural strength and flexural modulus, respectively, compared with untreated QFs. Furthermore, the sorption and solubility of the prepared dental posts were also studied by immersing the posts in artificial saliva (AS) for 4weeks, and yielded favourable results. This sol-gel surface modification method promises to resolve interfacial bonding issues of fibres with the resin matrix, and produce FRC posts with excellent properties. Copyright © 2017. Published by Elsevier B.V.

  16. Surface modification and characterization for dispersion stability of inorganic nanometer-scaled particles in liquid media

    International Nuclear Information System (INIS)

    Kamiya, Hidehiro; Iijima, Motoyuki

    2010-01-01

    Inorganic nanoparticles are indispensable for science and technology as materials, pigments and cosmetics products. Improving the dispersion stability of nanoparticles in various liquids is essential for those applications. In this review, we discuss why it is difficult to control the stability of nanoparticles in liquids. We also overview the role of surface interaction between nanoparticles in their dispersion and characterization, e.g. by colloid probe atomic force microscopy (CP-AFM). Two types of surface modification concepts, post-synthesis and in situ modification, were investigated in many previous studies. Here, we focus on post-synthesis modification using adsorption of various kinds of polymer dispersants and surfactants on the particle surface, as well as surface chemical reactions of silane coupling agents. We discuss CP-AFM as a technique to analyze the surface interaction between nanoparticles and the effect of surface modification on the nanoparticle dispersion in liquids. (topical review)

  17. Surface modification and characterization for dispersion stability of inorganic nanometer-scaled particles in liquid media

    Directory of Open Access Journals (Sweden)

    Hidehiro Kamiya and Motoyuki Iijima

    2010-01-01

    Full Text Available Inorganic nanoparticles are indispensable for science and technology as materials, pigments and cosmetics products. Improving the dispersion stability of nanoparticles in various liquids is essential for those applications. In this review, we discuss why it is difficult to control the stability of nanoparticles in liquids. We also overview the role of surface interaction between nanoparticles in their dispersion and characterization, e.g. by colloid probe atomic force microscopy (CP-AFM. Two types of surface modification concepts, post-synthesis and in situ modification, were investigated in many previous studies. Here, we focus on post-synthesis modification using adsorption of various kinds of polymer dispersants and surfactants on the particle surface, as well as surface chemical reactions of silane coupling agents. We discuss CP-AFM as a technique to analyze the surface interaction between nanoparticles and the effect of surface modification on the nanoparticle dispersion in liquids.

  18. Surface Modification Reaction of Photocatalytic Titanium Dioxide with Triethoxysilane for Improving Dispersibility

    International Nuclear Information System (INIS)

    Lee, Myung Jin; Kim, Ji Ho; Park, Young Tae

    2010-01-01

    We have carried out the surface modification of photocatalytic TiO 2 with triethoxysilane through dehydrogenation reaction and characterized the modified photocatalyst by spectroscopic methods, such as FT-IR, solid-state 29 Si MAS NMR, XPS, and XRF, etc. We also examined photocatalytic activity of the immobilized photocatalytic titanium dioxide with triethoxysilane by decolorization reaction of dyes such as cong red and methylene blue under visible light. Dispersion test showed that the photocatalytic titanium dioxide immobilized with triethoxysilane group has kept higher dispersibility than titanium dioxide itself. No appreciable precipitation takes place even after standing for 24 h in the 4:6 mixture ratio of ethanol and water

  19. STUDY OF SURFACE MODIFIED POLYMERS IN THE MODIFICATION OF NANOMATERIALS

    Directory of Open Access Journals (Sweden)

    G. V. Popov

    2014-01-01

    Full Text Available The comparative study of change of surface tension of solutions of some commercial rubbers before and after thermal ageing technique du-Nui, analyzed the features of change of surface tension of solutions of various rubbers in the presence of a mixture of fullerenes. Calculations of the Gibbs energy and the analysis of the obtained data to predict the behavior of polymer systems when changes are made to mix of fullerenes in a wide concentration range. When comparing the results of changes in Gibbs energy and the surface tension in fluids rubbers shown that mentioned above in solutions of elastomers aged, than the control. This fact confirms the initial chapeau of physic-chemical interactions of molecules fullerenes by segments of the Kuna and end groups of the polymer chains, as it is known that when thermal-oxidative degradation of rubbers, respectively the number of segments of the Kuna and branched loose ends of macromolecules that are free to react with fullerenes in solution, free from spatial constraints. A comparative analysis of the interaction of rubbers with different chemical composition with double branches has shown that it is easier to just react and has minimum energy polibutadien interaction that has to do with lack of branching and no radicals in its structure and in the backbone chain. The maximum energy of interaction with Fullerenes have SBS rubber because it has large styrene blocks in the main polymer chain that causes the spatial constraints to direct contact with fullerene molecules, you can assume that the interaction is only low-molecular fraction of Fullerenes mixture, possessing the necessary dimensions. As a result of the study shows that the application of the method of separation ring (Du-Nui allows you to predict the properties of rubber with modified nanomaterial’s with minimal labor costs.

  20. Fluorescent Magnetic Bioprobes by Surface Modification of Magnetite Nanoparticles

    Directory of Open Access Journals (Sweden)

    Tito Trindade

    2013-07-01

    Full Text Available Bimodal nanoprobes comprising both magnetic and optical functionalities have been prepared via a sequential two-step process. Firstly, magnetite nanoparticles (MNPs with well-defined cubic shape and an average dimension of 80 nm were produced by hydrolysis of iron sulfate and were then surface modified with silica shells by using the sol-gel method. The Fe3O4@SiO2 particles were then functionalized with the fluorophore, fluorescein isothiocyanate (FITC, mediated by assembled shells of the cationic polyelectrolyte, polyethyleneimine (PEI. The Fe3O4 functionalized particles were then preliminary evaluated as fluorescent and magnetic probes by performing studies in which neuroblast cells have been contacted with these nanomaterials.

  1. Surface modification by preparation of buffer zone in glow-discharge plasma

    International Nuclear Information System (INIS)

    Cho, D.L.

    1986-01-01

    Reactive species, energetic particles, and uv radiation in the plasma created by a glow discharge strongly interact with solid surfaces under the influence of the plasma. As a result of the strong interaction, various physical and chemical reactions, unique and advantageous for the surface modification of solid materials, occur on the solid surfaces. The surface modification is carried out through formation of a thin buffering layer on the solid surface. The preparation of a buffer zone on solid surfaces for surface modification is described. Two kinds of a buffer zone are prepared by plasma polymerization, or simultaneous sputter deposition of electrode material with plasma polymerization: a transitional buffer zone and a graded buffer zone. Important factors for preparation of the buffer zone (pre-conditioning of a substrate surface, thin-film deposition, post-treatment of the film, magnetron discharge, energy input, geometry of a substrate and a plasma) are discussed

  2. Enhanced surface functionality via plasma modification and plasma deposition techniques to create more biologically relevant materials

    Science.gov (United States)

    Shearer, Jeffrey C.

    Functionalizing nanoparticles and other unusually shaped substrates to create more biologically relevant materials has become central to a wide range of research programs. One of the primary challenges in this field is creating highly functionalized surfaces without modifying the underlying bulk material. Traditional wet chemistry techniques utilize thin film depositions to functionalize nanomaterials with oxygen and nitrogen containing functional groups, such as --OH and --NHx. These functional groups can serve to create surfaces that are amenable to cell adhesion or can act as reactive groups for further attachment of larger structures, such as macromolecules or antiviral agents. Additional layers, such as SiO2, are often added between the nanomaterial and the functionalized coating to act as a barrier films, adhesion layers, and to increase overall hydrophilicity. However, some wet chemistry techniques can damage the bulk material during processing. This dissertation examines the use of plasma processing as an alternative method for producing these highly functionalized surfaces on nanoparticles and polymeric scaffolds through the use of plasma modification and plasma enhanced chemical vapor deposition techniques. Specifically, this dissertation will focus on (1) plasma deposition of SiO2 barrier films on nanoparticle substrates; (2) surface functionalization of amine and alcohol groups through (a) plasma co-polymerization and (b) plasma modification; and (3) the design and construction of plasma hardware to facilitate plasma processing of nanoparticles and polymeric scaffolds. The body of work presented herein first examines the fabrication of composite nanoparticles by plasma processing. SiOxC y and hexylamine films were coated onto TiO2 nanoparticles to demonstrate enhanced water dispersion properties. Continuous wave and pulsed allyl alcohol plasmas were used to produce highly functionalized Fe2 O3 supported nanoparticles. Specifically, film composition was

  3. Porous silicon photoluminescence modification by colloidal gold nanoparticles: Plasmonic, surface and porosity roles

    International Nuclear Information System (INIS)

    Mora, M.B. de la; Bornacelli, J.; Nava, R.; Zanella, R.; Reyes-Esqueda, J.A.

    2014-01-01

    Metal nanoparticles on semiconductors are of interest because of the tunable effect of the surface plasmon resonance on the physical properties of the semiconductor. In this work, colloidal gold nanoparticles obtained by two different methods, with an average size of 6.1±2.0 nm and 5.0±2.0 nm, were added to luminescent porous silicon by drop casting. The gold nanoparticles interact with porous silicon by modifying its optical properties such as photoluminescence. That being said, plasmon effects are not the only to be taken into account; as shown in this work, surface chemical modification and porosity also play a key role in the final performance of photoluminescence of a porous silicon–gold nanoparticle hybrid system. -- Highlights: • A hybrid material consisting of porous silicon and gold nanoparticles was fabricated. • Porous silicon/gold nanoparticle hybrid material was made by drop casting. • Influence of plasmonics, surface chemical modification and porosity on the optical behavior of our material was analyzed. • Porosity is proposed as a parameter control to obtain the best effects on luminescence of the hybrid plasmonic material

  4. Surface modification of polymeric substrates by plasma-based ion implantation

    Science.gov (United States)

    Okuji, S.; Sekiya, M.; Nakabayashi, M.; Endo, H.; Sakudo, N.; Nagai, K.

    2006-01-01

    Plasma-based ion implantation (PBII) as a tool for polymer modification is studied. Polymeric films have good performances for flexible use, such as food packaging or electronic devices. Compared with inorganic rigid materials, polymers generally have large permeability for gases and moisture, which causes packaged contents and devices to degrade. In order to add a barrier function, surface of polymeric films are modified by PBII. One of the advantageous features of this method over deposition is that the modified surface does not have peeling problem. Besides, micro-cracks due to mechanical stress in the modified layer can be decreased. From the standpoint of mass production, conventional ion implantation that needs low-pressure environment of less than 10-3 Pa is not suitable for continuous large-area processing, while PBII works at rather higher pressure of several Pa. In terms of issues mentioned above, PBII is one of the most expected techniques for modification on flexible substrates. However, the mechanism how the barrier function appears by ion implantation is not well explained so far. In this study, various kinds of polymeric films, including polyethyleneterephthalate (PET), are modified by PBII and their barrier characteristics that depend on the ion dose are evaluated. In order to investigate correlations of the barrier function with implanted ions, modified surface is analyzed with X-ray photoelectron spectroscopy (XPS). It is assumed that the diffusion and sorption coefficients are changed by ion implantation, resulting in higher barrier function.

  5. High efficient and continuous surface modification of carbon fibers with improved tensile strength and interfacial adhesion

    Science.gov (United States)

    Sun, Jingfeng; Zhao, Feng; Yao, Yue; Jin, Zhen; Liu, Xu; Huang, Yudong

    2017-08-01

    Most of the surface modification technologies for carbon fibers, no matter in laboratory scale or for commercial manufacture, are accompanied by a simultaneous decrease in tensile strength. In this paper, a feasible and high efficient strategy for carbon fiber treatment which could obviously improve both tensile strength and interfacial adhesion was proposed. Continuously moving carbon fibers were treated with atmospheric helium plasma for 1 min, followed by a 5 min pyrolytic carbon deposition using ethanol as precursor at 800 °C. The effects of the new approach were characterized by SEM, AFM, nanoindentation, XPS, Raman, wettability analysis, single fiber tensile strength testing and single fiber pull-out testing. After modification, pyrolytic carbon coating was deposited on the fiber surface uniformly, and the roughness and surface energy increased significantly. The single fiber tensile testing results indicate that the resulting fiber strength increased 15.7%, rising from 3.13 to 3.62 GPa. Meanwhile, the interfacial shear strength of its epoxy composites increased from 65.3 to 83.5 MPa. The comparative studies of carbon fibers modified with commercial anodic oxidation and sizing were also carried out. The results demonstrate that the new method can be utilized in the carbon fiber manufacture process and is more efficient than the traditional approaches.

  6. Porous silicon photoluminescence modification by colloidal gold nanoparticles: Plasmonic, surface and porosity roles

    Energy Technology Data Exchange (ETDEWEB)

    Mora, M.B. de la; Bornacelli, J. [Instituto de Física, Universidad Nacional Autónoma de México, México D.F. 04510 (Mexico); Nava, R. [Centro de Investigación en Energía, Universidad Nacional Autónoma de México, Temixco, Morelos 62580 (Mexico); Zanella, R. [Centro de Ciencias Aplicadas y Desarrollo Tecnológico, Universidad Nacional Autónoma de México, México D.F. 04510 (Mexico); Reyes-Esqueda, J.A., E-mail: betarina@gmail.com [Instituto de Física, Universidad Nacional Autónoma de México, México D.F. 04510 (Mexico)

    2014-02-15

    Metal nanoparticles on semiconductors are of interest because of the tunable effect of the surface plasmon resonance on the physical properties of the semiconductor. In this work, colloidal gold nanoparticles obtained by two different methods, with an average size of 6.1±2.0 nm and 5.0±2.0 nm, were added to luminescent porous silicon by drop casting. The gold nanoparticles interact with porous silicon by modifying its optical properties such as photoluminescence. That being said, plasmon effects are not the only to be taken into account; as shown in this work, surface chemical modification and porosity also play a key role in the final performance of photoluminescence of a porous silicon–gold nanoparticle hybrid system. -- Highlights: • A hybrid material consisting of porous silicon and gold nanoparticles was fabricated. • Porous silicon/gold nanoparticle hybrid material was made by drop casting. • Influence of plasmonics, surface chemical modification and porosity on the optical behavior of our material was analyzed. • Porosity is proposed as a parameter control to obtain the best effects on luminescence of the hybrid plasmonic material.

  7. Surface Modification of Exfoliated Graphite Nano-Reinforcements, Phase II

    Data.gov (United States)

    National Aeronautics and Space Administration — Phase I results showed that two surface treatments, oxidative plasma and reactive finishes, are effective means of modifying the surface chemistry of exfoliated...

  8. Surface Modification of Cu(In,Ga)Se2 Grains

    Science.gov (United States)

    Alruqobah, Essam H.

    Nearly all of the world’s energy demand today is being met by the use of non-renewable energy sources. With the worldwide energy demand projected to increase in the coming years, it is vital to find alternative and renewable energy sources. Among the available renewable energy sources, solar energy is the most promising in meeting the worldwide energy demand. Recently, thin film solar cells have garnered attention due to their thinner architecture and relatively high optical absorption coefficients, as opposed to the conventional crytslline silicon solar cells. One of the most promising thin-film solar cell absorber materials is Cu(In,Ga)Se2 (CIGSe), achieving power conversion efficiencies approaching those of crystalline Si. The highest efficiency CIGSe devices were made via costly vacuum-based co-evaporation process. CIGSe devices made from solution-processed methods have also garnered attention due to their lower costs, and their efficiencies have increased considerably in recent years. In this thesis, CIGSe absorber layers are fabricated via the solution-processed from nanoparticle-based sulfide CIGS. The most important step in fabrication of a CIGSe solar cell absorber layer is the selenization step, which is the thermal sintering of a CIGSe precursor layer in the presence of selenium vapor to achieve large, dense selenide grains that are required for adequate PV performance. It is determined that maintaining adequate selenium vapor pressure on the substrate during the selenization and subsequent cooldown is crucial in producing high efficiency solar cell devices. Furthermore, exposing the CIGSe grains to a Se-deficient atmosphere causes Se to evaporate from the grains, and subsequently modifying the CIGSe grain surface. The modified grain surface adversely impacts the PV performance of the final solar cell device by forming defects due to the decrease in selenium concentration. These defects are manifested in increased current shunting, and decrease the

  9. A study of laser surface modification of polymers: A comparison in air and water

    DEFF Research Database (Denmark)

    Marla, Deepak; Andersen, Sebastian A.; Zhang, Yang

    2018-01-01

    Laser surface modification is a technique to modify polymer surfaces for various applications. In our earlier work [Physics Procedia, 83:211–217, 2016], we showed that when the laser surface modification process was carried out in water instead of air, the obtained surface characteristics were...... research. The observed images of laser modified surfaces suggest that a hemispherical hump is formed in the case of water at lower laser fluences that breakup with an increase in fluence. Such a behavior was not observed when the process was carried out in air. We explain this phenomenon by simulating...

  10. Surface Modifications and Their Effects on Titanium Dental Implants

    Science.gov (United States)

    Jemat, A.; Ghazali, M. J.; Razali, M.; Otsuka, Y.

    2015-01-01

    This review covers several basic methodologies of surface treatment and their effects on titanium (Ti) implants. The importance of each treatment and its effects will be discussed in detail in order to compare their effectiveness in promoting osseointegration. Published literature for the last 18 years was selected with the use of keywords like titanium dental implant, surface roughness, coating, and osseointegration. Significant surface roughness played an important role in providing effective surface for bone implant contact, cell proliferation, and removal torque, despite having good mechanical properties. Overall, published studies indicated that an acid etched surface-modified and a coating application on commercial pure titanium implant was most preferable in producing the good surface roughness. Thus, a combination of a good surface roughness and mechanical properties of titanium could lead to successful dental implants. PMID:26436097

  11. Roughness modification of surfaces treated by a pulsed dielectric barrier discharge

    CERN Document Server

    Dumitrascu, N; Apetroaei, N; Popa, G

    2002-01-01

    Local modifications of surface roughness are very important in many applications, as this surface property is able to generate new mechano-physical characteristics of a large category of materials. Roughness is one of the most important parameters used to characterize and control the surface morphology, and techniques that allow modifying and controlling the surface roughness present increasing interest. In this respect we propose the dielectric barrier discharge (DBD) as a simple and low cost method that can be used to induce controlled roughness on various surfaces in the nanoscale range. DBD is produced in helium, at atmospheric pressure, by a pulsed high voltage, 28 kV peak to peak, 13.5 kHz frequency and 40 W power. This type of discharge is a source of energy capable of modifying the physico-chemical properties of the surfaces without affecting their bulk properties. The discharge is characterized by means of electrical probes and, in order to analyse the heat transfer rate from the discharge to the tre...

  12. Surface modifications of AISI 420 stainless steel by low energy Yttrium ions

    Directory of Open Access Journals (Sweden)

    Nassisi Vincenzo

    2018-01-01

    Full Text Available In this work, we study surface modifications of AISI 420 stainless steel specimens in order to improve their surface properties. Oxidation resistance and surface micro-hardness were analyzed. Using an ion beam delivered by a Laser Ion Source (LIS coupled to an electrostatic accelerator, we performed implantation of low energy yttrium ions on the samples. The ions experienced an acceleration passing through a gap whose ends had a potential difference of 60 kV. The gap was placed immediately before the samples surface. The LIS produced high ions fluxes per laser pulse, up to 3x1011 ions/cm2, resulting in a total implanted flux of 7x1015 ions/cm2. The samples were characterized before and after ion implantation using two analytical techniques. They were also thermally treated to investigate the oxide scale. The crystal phases were identified by an X-ray diffractometer, while the micro-hardness was assayed using the scratch test and a profilometer. The first analysis was applied to blank, implanted and thermally treated sample surface, while the latter was applied only to blank and implanted sample surfaces. We found a slight increase in the hardness values and an increase to oxygen resistance. The implantation technique we used has the advantages, with respect to conventional methods, to modify the samples at low temperature avoiding stray diffusion of ions inside the substrate bulk.

  13. Surface modifications of AISI 420 stainless steel by low energy Yttrium ions

    Science.gov (United States)

    Nassisi, Vincenzo; Delle Side, Domenico; Turco, Vito; Martina, Luigi

    2018-01-01

    In this work, we study surface modifications of AISI 420 stainless steel specimens in order to improve their surface properties. Oxidation resistance and surface micro-hardness were analyzed. Using an ion beam delivered by a Laser Ion Source (LIS) coupled to an electrostatic accelerator, we performed implantation of low energy yttrium ions on the samples. The ions experienced an acceleration passing through a gap whose ends had a potential difference of 60 kV. The gap was placed immediately before the samples surface. The LIS produced high ions fluxes per laser pulse, up to 3x1011 ions/cm2, resulting in a total implanted flux of 7x1015 ions/cm2. The samples were characterized before and after ion implantation using two analytical techniques. They were also thermally treated to investigate the oxide scale. The crystal phases were identified by an X-ray diffractometer, while the micro-hardness was assayed using the scratch test and a profilometer. The first analysis was applied to blank, implanted and thermally treated sample surface, while the latter was applied only to blank and implanted sample surfaces. We found a slight increase in the hardness values and an increase to oxygen resistance. The implantation technique we used has the advantages, with respect to conventional methods, to modify the samples at low temperature avoiding stray diffusion of ions inside the substrate bulk.

  14. Biomimetic surface modification of titanium surfaces for early cell capture by advanced electrospinning

    International Nuclear Information System (INIS)

    Ravichandran, Rajeswari; Raghunath, Michael; Chan, Casey K; Ng, Clarisse CH; Liao, Susan; Pliszka, Damian; Ramakrishna, S

    2012-01-01

    The time required for osseointegration with a metal implant having a smooth surface ranges from three to six months. We hypothesized that biomimetic coating surfaces with poly(lactic-co-glycolic acid) (PLGA)/collagen fibers and nano-hydroxyapatite (n-HA) on the implant would enhance the adhesion of mesenchymal stem cells. Therefore, this surface modification of dental and bone implants might enhance the process of osseointegration. In this study, we coated PLGA or PLGA/collagen (50:50 w/w ratio) fiber on Ti disks by modified electrospinning for 5 s to 2 min; after that, we further deposited n-HA on the fibers. PLGA fibers of fiber diameter 0.957 ± 0.357 µm had a contact angle of 9.9 ± 0.3° and PLGA/collagen fibers of fiber diameter 0.378 ± 0.068 µm had a contact angle of 0°. Upon n-HA incorporation, all the fibers had a contact angle of 0° owing to the hydrophilic nature of n-HA biomolecule. The cell attachment efficiency was tested on all the scaffolds for different intervals of time (10, 20, 30 and 60 min). The alkaline phosphatase activity, cell proliferation and mineralization were analyzed on all the implant surfaces on days 7, 14 and 21. Results of the cell adhesion study indicated that the cell adhesion was maximum on the implant surface coated with PLGA/collagen fibers deposited with n-HA compared to the other scaffolds. Within a short span of 60 min, 75% of the cells adhered onto the mineralized PLGA/collagen fibers. Similarly by day 21, the rate of cell proliferation was significantly higher (p ≤ 0.05) on the mineralized PLGA/collagen fibers owing to enhanced cell adhesion on these fibers. This enhanced initial cell adhesion favored higher cell proliferation, differentiation and mineralization on the implant surface coated with mineralized PLGA/collagen fibers.

  15. One-step surface modification of poly(dimethylsiloxane) by undecylenic acid

    Science.gov (United States)

    Zhou, Jinwen; McInnes, Steven J. P.; Md Jani, Abdul Mutalib; Ellis, Amanda V.; Voelcker, Nicolas H.

    2008-12-01

    Poly(dimethylsiloxane) (PDMS) is a popular material for microfluidic devices due to its relatively low cost, ease of fabrication, oxygen permeability and optical transmission characteristics. However, its highly hydrophobic surface is still the main factor limiting its wide application, in particular as a material for biointerfaces. A simple and rapid method to form a relatively stable hydrophilised PDMS surface is reported in this paper. The PDMS surface was treated with pure undecylenic acid (UDA) for 10 min, 1 h and 1 day at 80 °C in a sealed container. The effects of the surface modification were investigated using water contact angle (WCA) measurements, Fourier transform infrared spectroscopy in attenuated total reflection mode (FTIR-ATR), and streaming zeta-potential analysis. The water contact angle of 1 day UDAmodified PDMS was found to decrease from that of native PDMS (110 °) to 75 °, demonstrating an increase in wettability of the surface. A distinctive peak at 1715 cm-1 in the FTIR-ATR spectra after UDA treatment was representative of carboxylation of the PDMS surface. The measured zeta-potential (ζ) at pH 4 changed from -27 mV for pure PDMS to -19 mV after UDA treatment. In order to confirm carboxylation of the surface visually, Lucifer Yellow CH fluorescence dye was reacted via a condensation reaction to the 1 day UDA modified PDMS surface. Fluorescent microscopy showed Lucifer Yellow CH fluorescence on the carboxylated surface, but not on the pure PDMS surface. Stability experiments were also performed showing that 1 day modified UDA samples were stable in both MilliQ water at 50 °C for 17 h, and in a desiccator at room temperature for 19.5 h.

  16. A Study on Surface Modification of Al7075-T6 Alloy against Fretting Fatigue Phenomenon

    Directory of Open Access Journals (Sweden)

    E. Mohseni

    2014-01-01

    Full Text Available Aircraft engines, fuselage, automobile parts, and energy saving strategies in general have promoted the interest and research in the field of lightweight materials, typically on alloys based on aluminum. Aluminum alloy itself does not have suitable wear resistance; therefore, it is necessary to enhance surface properties for practical applications, particularly when aluminum is in contact with other parts. Fretting fatigue phenomenon occurs when two surfaces are in contact with each other and one or both parts are subjected to cyclic load. Fretting drastically decreases the fatigue life of materials. Therefore, investigating the fretting fatigue life of materials is an important subject. Applying surface modification methods is anticipated to be a supreme solution to gradually decreasing fretting damage. In this paper, the authors would like to review methods employed so far to diminish the effect of fretting on the fatigue life of Al7075-T6 alloy. The methods include deep rolling, shot peening, laser shock peening, and thin film hard coatings. The surface coatings techniques are comprising physical vapor deposition (PVD, hard anodizing, ion-beam-enhanced deposition (IBED, and nitriding.

  17. Surface modification of polymeric materials using ultra low energy electron beam irradiation

    International Nuclear Information System (INIS)

    Oshima, Akihiro; Shiraki, Fumiya; Fujita, Hajime; Washio, Masakazu

    2011-01-01

    An ultra low energy electron beam (UL-EB) was used to irradiate various polymeric materials such as fluorinated polymers and a polyimide under an oxygen-free atmosphere. After the irradiation of the polyimide, the change in the thermal properties was measured by DSC and TGA. The surface modification of fluorinated polymers was demonstrated by use of styrene grafting by the preirradiation grafting method. By the use of UL-EB irradiation it was possible to facilitate styrene monomer grafting onto the surface of fluorinated polymers without losing their material characteristics. Moreover, in the case of the polyimide (Kapton TM ), which has excellent radiation resistance, the glass transition temperature was improved by about 20 o C by irradiation up to 40 MGy within 1 h.

  18. Surface Modification of Sputtered Ga.5In.5Sb Thin Films ISHU ...

    African Journals Online (AJOL)

    MICHAEL

    IR detectors useful for fiber optic communication. Since the efficiency of detector depends very much on the surface properties of the substrate material, improvement of substrate surfaces is a challenging task in device technology. Reports on the improved electrical properties of GaAs and InP surfaces by. Ru3+ modification ...

  19. Superhydrophobic alumina surface based on stearic acid modification

    Energy Technology Data Exchange (ETDEWEB)

    Feng Libang, E-mail: lepond@hotmail.com [School of Mechatronic Engineering, Lanzhou Jiaotong University, Lanzhou 730070 (China); Zhang Hongxia; Mao Pengzhi; Wang Yanping; Ge Yang [School of Mechatronic Engineering, Lanzhou Jiaotong University, Lanzhou 730070 (China)

    2011-02-15

    A novel superhydrophobic alumina surface is fabricated by grafting stearic acid layer onto the porous and roughened aluminum film. The chemical and phase structure, morphology, and the chemical state of the atoms at the superhydrophobic surface were investigated by techniques as FTIR, XRD, FE-SEM, and XPS, respectively. Results show that a super water-repellent surface with a contact angle of 154.2{sup o} is generated. The superhydrophobic alumina surface takes on an uneven flowerlike structure with many nanometer-scale hollows distribute in the nipple-shaped protrusions, and which is composed of boehmite crystal and {gamma}-Al{sub 2}O{sub 3}. Furthermore, the roughened and porous alumina surface is coated with a layer of hydrophobic alkyl chains which come from stearic acid molecules. Therefore, both the roughened structure and the hydrophobic layer endue the alumina surface with the superhydrophobic behavior.

  20. Modification of surface properties of copper-refractory metal alloys

    Science.gov (United States)

    Verhoeven, J.D.; Gibson, E.D.

    1993-10-12

    The surface properties of copper-refractory metal (CU-RF) alloy bodies are modified by heat treatments which cause the refractory metal to form a coating on the exterior surfaces of the alloy body. The alloys have a copper matrix with particles or dendrites of the refractory metal dispersed therein, which may be niobium, vanadium, tantalum, chromium, molybdenum, or tungsten. The surface properties of the bodies are changed from those of copper to that of the refractory metal.

  1. Modification of low-density lipoprotein by different radioiodination methods

    International Nuclear Information System (INIS)

    Sobal, G.; Resch, U.; Sinzinger, H.

    2004-01-01

    Scintigraphic imaging of radiolabeled low-density lipoproteins (LDL) is an interesting tool for the understanding of its role in pathomechanism of atherosclerosis. Metabolism of native LDL shows quite different pattern and kinetics as compared to that of modified LDL which is not mediated by classical LDL-receptor and accumulates in atherosclerotic lesions to form lipid-laden foam cells. Therefore we were interested whether radiolabelling of LDL induces structural modifications. We performed the iodine labeling of LDL for scintigraphic imaging of atherosclerosis by three different methods: chloramine-T (A), iodine monochloride (B) and iodogen (C). The highest radiolabelling yield of 125 I was obtained by the iodogen method (75.44±13.52%) and the lowest (49.01±12.74%) by iodine monochloride. Chloramine T showed a labeling yield of 62.82±6.17%. The stability of the tracer was very high with all the methods, persisting up to 6 h (98.83±1.2% - 91.38±4.7%, 15 min vs 6 h after labeling). For the first time we not only investigated the influence of radiolabelling on relative electrophoretic mobility (REM), but also various oxidation parameters such as baseline dienes (BD), thiobarbituric acid reactive substances (TBARS), endogenous peroxides (POX) and oxidation resistance in the copper-mediated oxidation system (expressed as lag-time) were measured. Furthermore, oxidation- derived fragmentation of the lipoproteins was examined with SDS-PAGE electrophoresis. Data are expressed as % change compared to native LDL before radiolabeling. BD were reduced by 32% using the method (A), but increased by 33% and 47% with the monochloride (B) and iodogen method (C), respectively. The effect on lag-time was comparable for all the three methods, ranging from 25 to 36% reduction in lag-time. TBARS were strongly increased 5-7 fold by all the methods. REM was changed by all three methods. While by methods A and C we have found a moderate increase in REM by 1.75 and 2.0 fold

  2. Improving the antimicrobial properties of titanium condenser material by surface modification using nanotechnology

    International Nuclear Information System (INIS)

    George, Rani P.; Dash, S.; Krishnan, R.; Kamruddin, M.; Kalavathi, S.; Tyagi, A.K.; Manoharan, N.; Dayal, R.K.; Vishwakarma, Vinita; Theresa, Josephine

    2008-01-01

    Biofouling is one of the major problems faced by condenser materials of power plants using seawater for cooling. Fouling control strategies in condensers include a combination of mechanical and chemical treatments like sponge ball cleaning, back washing and chlorination. In general, numerous studies have shown that no routine treatment regime can successfully keep the condenser tube clean over a period extending to years. Surface properties of the substratum influence initial adhesion and growth of bacterial cells on materials, modification of the surface for mitigating microbial attachment is the need of the hour. Metal nanoparticles are known to exhibit enhanced physical and chemical properties when compared to their bulk counter parts because of their high surface to volume ratios. Metals like copper are very toxic to microorganisms and effectively kill most of the microbes by blocking the respiratory enzyme. Copper alloys with their excellent resistance to biofouling are used extensively for marine applications. However, they are prone to localized corrosion initiation and consequently are getting replaced by extremely corrosion resistant titanium. Still, the inertness and biocompatibility of titanium makes it very susceptible to biofouling. Hence, this study attempts to use nano technology methods of surface modification of titanium using thin film of copper and also multilayers and bilayers of copper and nickel. This is aimed at improving the antimicrobial properties of this condenser pipe material. These nano structured thin films have been grown on titanium substrate using pulsed DC magnetron-sputtering and pulsed laser deposition. The thin films were characterized using Atomic Force Microscopy (AFM), Glancing Incidence X-ray Diffraction (GIXRD) and scanning electron microscopy (SEM with EDAX analysis). Antimicrobial properties were evaluated by exposure studies in seawater and bacterial cultures and by post exposure analysis using culture and

  3. Ion-beam modifications of the surface morphology and conductivity ...

    Indian Academy of Sciences (India)

    Unknown

    Abstract. Studies on the surface micromorphology and surface conductivity in thin polymer films of poly vinyl alcohol (PVA) and poly ethylene oxide (PEO) in both as-grown and ion-implanted polymer films have been carried out to reveal certain specific features of the ordered state in these materials. Optical microscopic.

  4. Reproductive tract modifications of the boar sperm surface

    NARCIS (Netherlands)

    Gadella, Bart M|info:eu-repo/dai/nl/115389873

    2017-01-01

    The sperm cell has a unique, polarized and segregated surface that is modified extensively by the changing environments in both the male and the female reproductive tracts. The sperm cannot refresh its surface, as protein translation and membrane recycling by intracellular vesicular transport have

  5. Ion-beam modifications of the surface morphology and conductivity ...

    Indian Academy of Sciences (India)

    Studies on the surface micromorphology and surface conductivity in thin polymer films of poly vinyl alcohol (PVA) and poly ethylene oxide (PEO) in both as-grown and ion-implanted polymer films have been carried out to reveal certain specific features of the ordered state in these materials. Optical microscopic ...

  6. Morphology modification of gold nanoparticles from nanoshell to C-shape: Improved surface enhanced Raman scattering

    International Nuclear Information System (INIS)

    Xing, Ting-Yang; Zhu, Jian; Li, Jian-Jun; Zhao, Jun-Wu

    2016-01-01

    Morphology modification of nanostructures is of great interest, because it can be used to fabricate nanostructures which are hard to be done using other methods. Different from traditional lithographic technique which is slow and expensive, morphology modification is easy, cheap, and reproducible. In this paper, modification of the optical and morphological properties of a hollow gold nanoshell (HGNS) is achieved by using H 2 O 2 as an oxidizer. The reshaping of these nanostructures has been demonstrated as a consequence of an oxidation process in which HGNSs are dissolved by H 2 O 2 under the acidic conditions provided by HCl. We investigate the oxidation process by a transmission electron microscope and propose a reshaping model involving four different shapes (HGNS, HGNS with hole, gold nanoring, and C-shaped gold nanoparticle) which are corresponding to the oxidation products of HGNSs at different pH values. Besides, the surface enhanced Raman scattering (SERS) activity of each oxidation product has been evaluated by using rhodamine 6G as the Raman active probe. It has been observed that the C-shaped gold nanoparticles which are corresponding to the oxidation products at the minimum pH value have the highest SERS activity and this result can also be interpreted by discrete-dipole approximation simulations. We demonstrate that the morphology modification of HGNSs becomes possible in a controlled manner using wet chemistry and can be used in preparation of gold nanoparticles such as HGNS with hole, gold nanoring, and C-shaped gold nanoparticle with large SERS activity. These nanostructures must have potential use in many plasmonic areas, including sensing, catalysis, and biomedicine.

  7. Surface modification effects of fluorine-doped tin dioxide by oxygen plasma ion implantation

    Science.gov (United States)

    Tang, Peng; Liu, Cai; Zhang, Jingquan; Wu, Lili; Li, Wei; Feng, Lianghuan; Zeng, Guanggen; Wang, Wenwu

    2018-04-01

    SnO2:F (FTO), as a kind of transparent conductive oxide (TCO), exhibits excellent transmittance and conductivity and is widely used as transparency electrodes in solar cells. It's very important to modifying the surface of FTO for it plays a critical role in CdTe solar cells. In this study, modifying effects of oxygen plasma on FTO was investigated systematically. Oxygen plasma treatment on FTO surface with ion accelerating voltage ranged from 0.4 kV to 1.6 kV has been processed. The O proportion of surface was increased after ion implantation. The Fermi level of surface measurement by XPS valance band spectra was lowered as the ion accelerating voltage increased to 1.2 kV and then raised as accelerating voltage was elevated to 1.6 kV. The work function measured by Kelvin probe force microscopy increased after ion implanting, and it was consistent with the variation of Fermi level. The change of energy band structure of FTO surface mainly originated from the surface composition variation. As FTO conduction was primarily due to oxyanion hole, the carrier was electron and its concentration was reduced while O proportion was elevated at the surface of FTO, as a result, the Fermi level lowered and the work function was enlarged. It was proved that oxygen plasma treatment is an effective method to modulate the energy band structure of the surface as well as other properties of FTO, which provides much more space for interface and surface modification and then photoelectric device performance promotion.

  8. Impact of surface modification in BSA nanoparticles for uptake in cancer cells.

    Science.gov (United States)

    Choi, Jin-Seok; Meghani, Nilesh

    2016-09-01

    Recent studies have shown that cellular uptake of nanoparticles are strongly affected by the presence and physicochemical characteristics of protein on the surface of these nanoparticles. Hence, We developed surface-modified bovine serum albumin (BSA) nanoparticles (NPs) and evaluated the effect of surface modification on cellular uptake in two types of cancer cells, MCF-7 and A549. BSA NPs were prepared by desolvation method and their surface was modified with apo-transferrin, hyaluronic acid, and Poly(allylamine hydrochloride) (PAH). Morphology of surface-modified BSA NPs was characterized by field emission scanning electron microscopy and differential scanning calorimetry. In vitro-fluorescence release study was performed in phosphate buffered saline with trypsin (100μL/mL (v/v)) for 24h. Confocal microscopy was performed to evaluate cellular uptake followed by fluorescence analysis to evaluate the quantitative uptake of nanoparticles at 0.5, 1, and 2h. Different types of BSA NPs with a mean size of ∼100nm were successfully prepared. In vitro-fluorescent release showed sustained release pattern in surface-modified BSA NPs compared to unmodified BSA NPs. Surface-modified BSA NPs showed more cellular internalization than unmodified BSA NPs. The uptake of PAH-BSA NPs was about 2 times higher than that of unmodified BSA NPs in both cell types. In conclusion, surface-modified BSA NPs showed enhanced cellular uptake, and PAH-BSA NPs are more effective compared to ligand-specific surface-modified BSA NPs (HA-BSA NPs and Tf-BSA NPs). Copyright © 2016 Elsevier B.V. All rights reserved.

  9. Influence of hardening and surface modification of endourological wires on corrosion resistance.

    Science.gov (United States)

    Walke, Witold; Przondziono, Joanna

    2012-01-01

    Guide wires with suitable functional characteristics are of crucial importance for proper urological treatment. This study presents an analysis of the effect of work hardening taking place in the process of wire cold drawing and the effect of surface modification by means of electrochemical polishing and chemical passivation on the resistance of wires made of X10CrNi18-8 steel used in urology. Corrosion resistance was evaluated on the grounds of the registered anodic polarisation curves by means of potentiodynamic method. The tests were made in solution simulating human urine. Anodic polarisation curves were presented for selected wire diameters. Mechanical properties were tested in a static uniaxial tensile test. The course of flow curve as well as mathematical form of flow stress function were determined. Curves presenting the relation of polarisation resistance as a function of strain applied in the drawing process are given. The tests carried out show that surface modification by means of electrochemical polishing and then chemical passivation of wires used in endourological treatment is fundamental.

  10. Surface Modification of Dental Titanium Implant by Layer-by-Layer Electrostatic Self-Assembly

    Directory of Open Access Journals (Sweden)

    Quan Shi

    2017-08-01

    Full Text Available In vivo implants that are composed of titanium and titanium alloys as raw materials are widely used in the fields of biology and medicine. In the field of dental medicine, titanium is considered to be an ideal dental implant material. Good osseointegration and soft tissue closure are the foundation for the success of dental implants. Therefore, the enhancement of the osseointegration and antibacterial abilities of titanium and its alloys has been the focus of much research. With its many advantages, layer-by-layer (LbL assembly is a self-assembly technique that is used to develop multilayer films based on complementary interactions between differently charged polyelectrolytes. The LbL approach provides new methods and applications for the surface modification of dental titanium implant. In this review, the application of the LbL technique to surface modification of titanium including promoting osteogenesis and osseointegration, promoting the formation and healing of soft tissues, improving the antibacterial properties of titanium implant, achieving local drug delivery and sustained release is summarized.

  11. Fabrication and surface properties of hydrophobic barium sulfate aggregates based on sodium cocoate modification

    Science.gov (United States)

    Hu, Linna; Wang, Guangxiu; Cao, Rong; Yang, Chun; Chen, Xi

    2014-10-01

    Hydrophobic barium sulfate aggregates were fabricated by the direction of cocoate anions. At 30 °C, when the weight ratio of sodium cocoate to BaSO4 particles was 2.0 wt.%, the active ratio of the product reached 99.43% and the contact angle was greater than 120°. This method could not only simplify the complex modification process, but reduce energy consumption. The surface morphology, chemical structure and composition of BaSO4 aggregates were characterized by SEM, XRD, and FTIR. The results indicated that the as-synthesized BaSO4 particles were almond-liked and were composed of many interconnected nanoballs and that their surfaces were affected by cocoate anions. The adsorption of cocoate anions reversed the charge and weakened the surface polarity of BaSO4 particles, driving the formation of aggregates. And cocoate anions induced a change of the BaSO4 particles surface from hydrophilic to hydrophobic by a self-assembly and transformation process. Due to the self-assembled structure and the surface hydrophobicity, when adding the hydrophobic BaSO4 into PVC, the mechanical properties of PVC composite materials were significantly improved.

  12. Role of PEG 2000 in the surface modification and physicochemical ...

    Indian Academy of Sciences (India)

    Gourab Karmakar

    2018-03-29

    Mar 29, 2018 ... Abstract. Hydrogenated soy phosphatidylcholine, tristearin and oleic acid were employed in preparing nanostructured lipid carriers (NLC). Surface modified NLCs (NLCPEG) were formulated by adding polyethylene glycol 2000 (PEG 2000) in the dispersion medium along with Tween 60.

  13. Ultrasound enhanced plasma surface modification at atmospheric pressure

    DEFF Research Database (Denmark)

    Kusano, Yukihiro; Singh, Shailendra Vikram; Norrman, Kion

    irradiation, the water contact angle dropped markedly, and tended to decrease furthermore at higher power. The ultrasonic irradiation during the plasma treatment consistently improved the wettability. Oxygen containing polar functional groups were introduced at the surface by the plasma treatment......Atmospheric pressure plasma treatment can be highly enhanced by simultaneous high-power ultrasonic irradiation onto the treating surface. It is because ultrasonic waves with a sound pressure level (SPL) above approximately 140 dB can reduce the thickness of a boundary gas layer between the plasma...... are separated using a polyethylene film. The gliding arc was extended by a high speed air flow into ambient air, directed the polyester surface at an angle of approximately 30o. The ultrasonic waves were introduced vertically to the surface. After the plasma treatment using each plasma source without ultrasonic...

  14. Surface modification of Chlorella vulgaris cells using magnetite particles

    Czech Academy of Sciences Publication Activity Database

    Procházková, G.; Šafařík, Ivo; Brányik, T.

    2012-01-01

    Roč. 42, č. 2012 (2012), s. 1778-1787 E-ISSN 1877-7058 Institutional support: RVO:67179843 Keywords : microalgae * physicochemical approaches * surface interactions * magnetite * XDLVO theory * harvesting Subject RIV: EI - Biotechnology ; Bionics

  15. Soft landing of polyatomic ions for selective modification of fluorinated self-assembled monolayer surfaces

    Science.gov (United States)

    Luo, Hai; Miller, Scott A.; Cooks, R. Graham; Pachuta, Steven J.

    1998-03-01

    timing have not been elucidated. The extent and nature of surface modification is controlled by choice of the total ion dose, the projectile ion and its energy. Total ion doses used in these experiments typically corresponded to ~7% of a monolayer; however, inefficiencies in deposition mean that the actual surface coverages achieved are much lower. For a series of pyridine ions, correlations are evident between successful soft landing and the steric bulk of the projectile ion. It is suggested that the bulky groups facilitate energy loss by the projectile as it moves into the SAM surface and subsequently assist in its trapping there. Ex situ TOF-SIMS analysis and in situ sputtering using projectile ions with different recombination energies provide evidence that the ions deposited into the F-SAM surface are present in the matrix as isolated charged species, a result which is further supported by thermal desorption experiments. The modified surfaces are stable in both air and vacuum for several hours, although the trapped ion signal slowly decreases with time. The present method of surface modification appears to represent a new technique for producing long-lived metastable structures by allowing trapping of unusual and chemically reactive species at interfaces.

  16. The effects of surface modification on carbon felt electrodes for use in vanadium redox flow batteries

    International Nuclear Information System (INIS)

    Kim, Ki Jae; Kim, Young-Jun; Kim, Jae-Hun; Park, Min-Sik

    2011-01-01

    Highlights: ► We observed the physical and chemical changes on the surface of carbon felts after various surface modifications. ► The surface area and chemistry of functional groups formed on the surface of carbon felt are critical to determine the kinetics of the redox reactions of vanadium ions. ► By incorporation of the surface modifications into the electrode preparation, the electrochemical activity of carbon felts could be notably enhanced. - Abstract: The surface of carbon felt electrodes has been modified for improving energy efficiency of vanadium redox flow batteries. For comparative purposes, the effects of various surface modifications such as mild oxidation, plasma treatment, and gamma-ray irradiation on the electrochemical properties of carbon felt electrodes were investigated at optimized conditions. The cell energy efficiency was improved from 68 to 75% after the mild oxidation of the carbon felt at 500 °C for 5 h. This efficiency improvement could be attributed to the increased surface area of the carbon felt electrode and the formation of functional groups on its surface as a result of the modification. On the basis of various structural and electrochemical characterizations, a relationship between the surface nature and electrochemical activity of the carbon felt electrodes is discussed.

  17. Surface modification techniques for increased corrosion tolerance of zirconium fuel cladding

    Science.gov (United States)

    Carr, James Patrick, IV

    Corrosion is a major issue in applications involving materials in normal and severe environments, especially when it involves corrosive fluids, high temperatures, and radiation. Left unaddressed, corrosion can lead to catastrophic failures, resulting in economic and environmental liabilities. In nuclear applications, where metals and alloys, such as steel and zirconium, are extensively employed inside and outside of the nuclear reactor, corrosion accelerated by high temperatures, neutron radiation, and corrosive atmospheres, corrosion becomes even more concerning. The objectives of this research are to study and develop surface modification techniques to protect zirconium cladding by the incorporation of a specific barrier coating, and to understand the issues related to the compatibility of the coatings examined in this work. The final goal of this study is to recommend a coating and process that can be scaled-up for the consideration of manufacturing and economic limits. This dissertation study builds on previous accident tolerant fuel cladding research, but is unique in that advanced corrosion methods are tested and considerations for implementation by industry are practiced and discussed. This work will introduce unique studies involving the materials and methods for accident tolerant fuel cladding research by developing, demonstrating, and considering materials and processes for modifying the surface of zircaloy fuel cladding. This innovative research suggests that improvements in the technique to modify the surface of zirconium fuel cladding are likely. Three elements selected for the investigation of their compatibility on zircaloy fuel cladding are aluminum, silicon, and chromium. These materials are also currently being investigated at other labs as alternate alloys and coatings for accident tolerant fuel cladding. This dissertation also investigates the compatibility of these three elements as surface modifiers, by comparing their microstructural and

  18. Modification of carbon fiber surfaces via grafting with Meldrum's acid

    Science.gov (United States)

    Cuiqin, Fang; Jinxian, Wu; Julin, Wang; Tao, Zhang

    2015-11-01

    The mechanism of Meldrum's acid modifying carbon fiber surfaces was investigated in this work. The existing carbonyl groups of carbon fibers were grafted with Meldrum's acid to create carboxylic functionalized surfaces. The surface functionalization effect was detected with X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM), atomic force microscopy (AFM), and thermogravimetric analysis (TGA). The XPS results showed that the relative content of carboxylic groups on carbon fiber surfaces was increased from initial 1.41% to 7.84%, however, that of carbonyl groups was decreased from 23.11% to 13.28% after grafting reaction. The SEM, AFM and TGA results indicated that the surfaces of carbon fibers neither etched nor generated coating. The tensile strength of carbon fibers was preserved after grafting reaction according to single fiber tensile strength tests. The fibers were well combined with matrix and the maximal interlaminar shear strength (ILSS) of carbon fiber/epoxy resin composites was sharply increased approximately 74% after functionalization. The effects of acetic acid and sonication on the degree of the surface functionalization were also studied.

  19. Enhancing the formation and shear resistance of nitrifying biofilms on membranes by surface modification

    DEFF Research Database (Denmark)

    Lackner, Susanne; Holmberg, Maria; Terada, Akihiko

    2009-01-01

    Polypropylene (PP) membranes and polyethylene (PE) surfaces were modified to enhance formation and shear resistance of nitrifying biofilms for wastewater treatment applications. A combination of plasma polymerization and wet chemistry was employed to ultimately introduce poly(ethyleneglycol) (PEG...... structure might be possible explanations of the superiority of the -PEG-NH2 modification. The success of the-PEG-NH2 modification was independent of the original surface and might, therefore, be used in wastewater treatment bioreactors to improve reactor performance by making biofilm formation more stable...... similar trends: biofilms on -PEG-NH2 modified surfaces were much stronger compared to the other modifications and the unmodified reference surfaces. Electrostatic interactions between the protonated amino group and negatively charged bacteria as well as PEG chain density which can affect the surface...

  20. Surface modification and its effect on attachment, spreading, and proliferation of human gingival fibroblasts.

    Science.gov (United States)

    Zhang, Feng; Huang, Ying; Li, Xiaodong; Zhao, Shifang

    2011-01-01

    The purpose of this study was to exploit potential methods of surface modification for improving the seal between the neck portion of a dental implant and the surrounding soft tissue. Titanium surfaces were modified by machining (SM-Ti group); machining and acid etching (AE-Ti group); or machining, acid etching, and depositing 4.5 collagen/hyaluronic acid (col/HA) polyelectrolyte bilayers (CHC-Ti group). These were analyzed using scanning electron microscopy, scanning force microscopy, x-ray photoelectron spectroscopy, contact angle measurement, and quartz crystal microbalance measurement. The degradation behavior of the col/HA multilayer coating was measured. Next, human gingival fibroblasts (HGFs) were cultured on the different surfaces, and cell morphology and spreading were observed using fluorescence microscopy and a shape factor measurement. Cell proliferation was examined by fluorometric quantification of the amount of cellular DNA. Matrix formation of HGFs was determined via enzyme-linked immunosorbent assay. Gene expression was analyzed via reverse transcriptase polymerase chain reaction. Similar surface topology for these three groups was observable on a microscopic scale, and morphologic differences were apparent on the nanoscale. Both acid etching and col/HA deposition improved the hydrophilicity of the titanium surface, in contrast to machining alone. Each col/HA bilayer was about 5 nm thick. The col/HA coating degraded in about a week. Attachment and spreading of HGFs was better on the CHC-Ti surface than on the SM-Ti or AE-Ti surfaces. Moreover, the proliferation and differentiation of HGFs were greatly stimulated when cultured on CHC-Ti. In contrast to two control surfaces (one machined, one machined and acid-etched), col/HA treatment of Ti improved the attachment, spreading, proliferation, and differentiation of HGFs.

  1. Innovative coatings and surface modification of titanium for sea water condenser applications

    International Nuclear Information System (INIS)

    George, R.P.; Anandkumar, B.; Vanithakumari, S.C.; Kamachi Mudali, U.

    2016-01-01

    Effectiveness of cooling water systems in various power plants to maintain highest electrical energy output per tonne of fuel is important as part of good energy management. Cooling water systems of nuclear power plants using seawater for cooling comes under constant attack from the marine and sea water environment. Many metallic components and civil structures in the cooling water systems like bridges, intake wells, intake pipes, pump house wells, water boxes, condenser pipes are subjected to severe fouling and corrosion which limits the service life and availability of power plants. The experience with a coastal water cooled power plant at Kalpakkam (MAPS), India, showed that chlorination and screening control macrofouling to a great extend by controlling protozoans, invertebrates, algae and fungi. However 90% of marine bacteria are resistant to such control measures, and they cause microfouling of condenser pipes leading to poor heat transfer and microbially influenced corrosion (MIC) failures. Titanium is used as condenser for Indian nuclear power plants employing sea water cooling, including the PFBR at Kalpakkam. Though titanium is excellent with respect to corrosion behavior under sea water conditions, its biocompatible nature results in biofouling and MIC during service. Therefore innovative antifouling coatings and surface modification techniques for titanium condenser applications in seawater and marine environments are the need of the hour. Extensive investigations were carried out by different methods including nanostructuring of surfaces for making them antibacterial. The microroughness of titanium was produced by repeated pickling and polishing which by itself reduced microbial adhesion. To utilize photocatalytic activity for antibacterial property, anodization of titanium surfaces followed by heat treatment was adopted and this also has controlled microbial fouling. Electroless plating of nanofilm of copper-nickel alloy decreased biofouling of

  2. Atomic and molecular layer deposition for surface modification

    International Nuclear Information System (INIS)

    Vähä-Nissi, Mika; Sievänen, Jenni; Salo, Erkki; Heikkilä, Pirjo; Kenttä, Eija; Johansson, Leena-Sisko; Koskinen, Jorma T.; Harlin, Ali

    2014-01-01

    Atomic and molecular layer deposition (ALD and MLD, respectively) techniques are based on repeated cycles of gas–solid surface reactions. A partial monolayer of atoms or molecules is deposited to the surface during a single deposition cycle, enabling tailored film composition in principle down to molecular resolution on ideal surfaces. Typically ALD/MLD has been used for applications where uniform and pinhole free thin film is a necessity even on 3D surfaces. However, thin – even non-uniform – atomic and molecular deposited layers can also be used to tailor the surface characteristics of different non-ideal substrates. For example, print quality of inkjet printing on polymer films and penetration of water into porous nonwovens can be adjusted with low-temperature deposited metal oxide. In addition, adhesion of extrusion coated biopolymer to inorganic oxides can be improved with a hybrid layer based on lactic acid. - Graphical abstract: Print quality of a polylactide film surface modified with atomic layer deposition prior to inkjet printing (360 dpi) with an aqueous ink. Number of printed dots illustrated as a function of 0, 5, 15 and 25 deposition cycles of trimethylaluminum and water. - Highlights: • ALD/MLD can be used to adjust surface characteristics of films and fiber materials. • Hydrophobicity after few deposition cycles of Al 2 O 3 due to e.g. complex formation. • Same effect on cellulosic fabrics observed with low temperature deposited TiO 2 . • Different film growth and oxidation potential with different precursors. • Hybrid layer on inorganic layer can be used to improve adhesion of polymer melt

  3. Atomic and molecular layer deposition for surface modification

    Energy Technology Data Exchange (ETDEWEB)

    Vähä-Nissi, Mika, E-mail: mika.vaha-nissi@vtt.fi [VTT Technical Research Centre of Finland, PO Box 1000, FI‐02044 VTT (Finland); Sievänen, Jenni; Salo, Erkki; Heikkilä, Pirjo; Kenttä, Eija [VTT Technical Research Centre of Finland, PO Box 1000, FI‐02044 VTT (Finland); Johansson, Leena-Sisko, E-mail: leena-sisko.johansson@aalto.fi [Aalto University, School of Chemical Technology, Department of Forest Products Technology, PO Box 16100, FI‐00076 AALTO (Finland); Koskinen, Jorma T.; Harlin, Ali [VTT Technical Research Centre of Finland, PO Box 1000, FI‐02044 VTT (Finland)

    2014-06-01

    Atomic and molecular layer deposition (ALD and MLD, respectively) techniques are based on repeated cycles of gas–solid surface reactions. A partial monolayer of atoms or molecules is deposited to the surface during a single deposition cycle, enabling tailored film composition in principle down to molecular resolution on ideal surfaces. Typically ALD/MLD has been used for applications where uniform and pinhole free thin film is a necessity even on 3D surfaces. However, thin – even non-uniform – atomic and molecular deposited layers can also be used to tailor the surface characteristics of different non-ideal substrates. For example, print quality of inkjet printing on polymer films and penetration of water into porous nonwovens can be adjusted with low-temperature deposited metal oxide. In addition, adhesion of extrusion coated biopolymer to inorganic oxides can be improved with a hybrid layer based on lactic acid. - Graphical abstract: Print quality of a polylactide film surface modified with atomic layer deposition prior to inkjet printing (360 dpi) with an aqueous ink. Number of printed dots illustrated as a function of 0, 5, 15 and 25 deposition cycles of trimethylaluminum and water. - Highlights: • ALD/MLD can be used to adjust surface characteristics of films and fiber materials. • Hydrophobicity after few deposition cycles of Al{sub 2}O{sub 3} due to e.g. complex formation. • Same effect on cellulosic fabrics observed with low temperature deposited TiO{sub 2}. • Different film growth and oxidation potential with different precursors. • Hybrid layer on inorganic layer can be used to improve adhesion of polymer melt.

  4. Surface charging, discharging and chemical modification at a sliding contact

    DEFF Research Database (Denmark)

    Singh, Shailendra Vikram; Kusano, Yukihiro; Morgen, Per

    2012-01-01

    -ray photoelectron spectroscopy (XPS). The experiments were performed on the disk surface of a ball-on-rotating-disk apparatus; using a glass disk and a Teflon (polytetrafluoroethylene) ball arrangement, and a polyester disks and a diamondlike carbon (DLC) coated steel ball arrangement. The capacitive probe...... is designed to perform highly resolved measurements, which is sensitive to relative change in charge density on the probed surface. For glass and Teflon arrangement, electrical measurements show that the ball track acquires non-uniform charging. Here not only the increase in charge density, but interestingly...... indicate that the wear and friction (sliding without charging) on the surface can be discarded from inducing such a deoxidation effect. © 2012 American Institute of Physics...

  5. Using a nitrilase for the surface modification of acrylic fibres.

    Science.gov (United States)

    Matamá, Teresa; Carneiro, Filipa; Caparrós, Cristina; Gübitz, Georg M; Cavaco-Paulo, Artur

    2007-03-01

    The surface of an acrylic fibre was modified with a commercial nitrilase (EC 3.5.5.1). The effect of fibre solvents and polyols on nitrilase catalysis efficiency and stability was investigated. The nitrilase action on the acrylic fabric was improved by the combined addition of 1 M sorbitol and 4% N, N-dimethylacetamide. The colour levels for samples treated with nitrilase increased 156% comparing to the control samples. When the additives were introduced in the treatment media, the colour levels increased 199%. The enzymatic conversion of nitrile groups into the corresponding carboxylic groups, on the fibre surface, was followed by the release of ammonia and polyacrylic acid. A surface erosion phenomenon took place and determined the "oscillatory" behaviour of the amount of dye uptake with time of treatment. These results showed that the outcome of the application of the nitrilase for the acrylic treatment is intimately dependent on reaction media parameters, such as time, enzyme activity and formulation.

  6. Plasma surface modification of chitosan membranes : characterization and preliminary cell response studies

    OpenAIRE

    Silva, Simone Santos; Luna, Sandra M.; Gomes, Manuela E.; Benesch, Johan; Pashkuleva, I.; Mano, J. F.; Reis, R. L.

    2008-01-01

    Surface modification of biomaterials is a way to tailor cell responses whilst retaining the bulk properties. In this work, chitosan membranes were prepared by solvent casting and treated with nitrogen or argon plasma at 20Wfor 10–40 min. AFM indicated an increase in the surface roughness as a result of the ongoing etching process. XPS and contact angle measurements showed different surface elemental compositions and higher surface free energy. The MTS test and direct contact...

  7. Effects of cementation surface modifications on fracture resistance of zirconia.

    Science.gov (United States)

    Srikanth, Ramanathan; Kosmac, Tomaz; Della Bona, Alvaro; Yin, Ling; Zhang, Yu

    2015-04-01

    To examine the effects of glass infiltration (GI) and alumina coating (AC) on the indentation flexural load and four-point bending strength of monolithic zirconia. Plate-shaped (12 mm × 12 mm × 1.0 mm or 1.5 or 2.0 mm) and bar-shaped (4 mm × 3 mm × 25 mm) monolithic zirconia specimens were fabricated. In addition to monolithic zirconia (group Z), zirconia monoliths were glass-infiltrated or alumina-coated on their tensile surfaces to form groups ZGI and ZAC, respectively. They were also glass-infiltrated on their upper surfaces, and glass-infiltrated or alumina-coated on their lower (tensile) surfaces to make groups ZGI2 and ZAC2, respectively. For comparison, porcelain-veneered zirconia (group PVZ) and monolithic lithium disilicate glass-ceramic (group LiDi) specimens were also fabricated. The plate-shaped specimens were cemented onto a restorative composite base for Hertzian indentation using a tungsten carbide spherical indenter with a radius of 3.2mm. Critical loads for indentation flexural fracture at the zirconia cementation surface were measured. Strengths of bar-shaped specimens were evaluated in four-point bending. Glass infiltration on zirconia tensile surfaces increased indentation flexural loads by 32% in Hertzian contact and flexural strength by 24% in four-point bending. Alumina coating showed no significant effect on resistance to flexural damage of zirconia. Monolithic zirconia outperformed porcelain-veneered zirconia and monolithic lithium disilicate glass-ceramics in terms of both indentation flexural load and flexural strength. While both alumina coating and glass infiltration can be used to effectively modify the cementation surface of zirconia, glass infiltration can further increase the flexural fracture resistance of zirconia. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  8. Laser surface modification of Ti implants to improve osseointegration

    International Nuclear Information System (INIS)

    Marticorena, M; Corti, G; Olmedo, D; Guglielmotti, M B; Duhalde, S

    2007-01-01

    Commercially Pure Titanium foils, were irradiated using a pulsed Nd:YAG laser under ambient air, in order to produce and characterize a well controlled surface texture (roughness and waviness) that enhances osseointegration. To study the 'peri-implant' reparative process response, the laser treated Ti foils were implanted in the tibia of 10 male Wistar rats. At 14 days post-implantation, the histological analysis showed a tendency to more bone formation compared to the untreated control implants. The formation of a layer of TiN on the surface and the obtained roughness, have been demonstrated to improve bone response

  9. Atmospheric pressure plasma surface modification of carbon fibres

    DEFF Research Database (Denmark)

    Kusano, Yukihiro; Løgstrup Andersen, Tom; Michelsen, Poul

    2008-01-01

    Carbon fibres are continuously treated with dielectric barrier discharge plasma at atmospheric pressure in various gas conditions for adhesion improvement in mind. An x-ray photoelectron spectroscopic analysis indicated that oxygen is effectively introduced onto the carbon fibre surfaces by He, He....../O2 and Ar plasma treatments, mainly attributed to an increase in the density of the C-O single bond at the carbon fibre surfaces. The O/C ratio increased to 0.182 after 1-s He plasma treatment, and remained approximately constant after longer treatment. After exposure in an ambient air at room...

  10. Biomimetic surface modification of polypropylene by surface chain transfer reaction based on mussel-inspired adhesion technology and thiol chemistry

    International Nuclear Information System (INIS)

    Niu, Zhijun; Zhao, Yang; Sun, Wei; Shi, Suqing; Gong, Yongkuan

    2016-01-01

    Highlights: • Biomimetic surface modification of PP was successfully conducted by integrating mussel-inspired technology, thiol chemistry and cell outer membranes-like structures. • The resultant biomimetic surface exhibits good interface and surface stability. • The obvious suppression of protein adsorption and platelet adhesion is also achieved. • The residue thoil groups on the surface could be further functionalized. - Abstract: Biomimetic surface modification of polypropylene (PP) is conducted by surface chain transfer reaction based on the mussel-inspired versatile adhesion technology and thiol chemistry, using 2-methacryloyloxyethylphosphorylcholine (MPC) as a hydrophilic monomer mimicking the cell outer membrane structure and 2,2-azobisisobutyronitrile (AIBN) as initiator in ethanol. A layer of polydopamine (PDA) is firstly deposited onto PP surface, which not only offers good interfacial adhesion with PP, but also supplies secondary reaction sites (-NH 2 ) to covalently anchor thiol groups onto PP surface. Then the radical chain transfer to surface-bonded thiol groups and surface re-initiated polymerization of MPC lead to the formation of a thin layer of polymer brush (PMPC) with cell outer membrane mimetic structure on PP surface. X-ray photoelectron spectrophotometer (XPS), atomic force microscopy (AFM) and water contact angle measurements are used to characterize the PP surfaces before and after modification. The protein adsorption and platelet adhesion experiments are also employed to evaluate the interactions of PP surface with biomolecules. The results show that PMPC is successfully grafted onto PP surface. In comparison with bare PP, the resultant PP-PMPC surface exhibits greatly improved protein and platelet resistance performance, which is the contribution of both increased surface hydrophilicity and zwitterionic structure. More importantly, the residue thiol groups on PP-PMPC surface create a new pathway to further functionalize such

  11. Biomimetic surface modification of polypropylene by surface chain transfer reaction based on mussel-inspired adhesion technology and thiol chemistry

    Energy Technology Data Exchange (ETDEWEB)

    Niu, Zhijun; Zhao, Yang; Sun, Wei; Shi, Suqing, E-mail: shisq@nwu.edu.cn; Gong, Yongkuan

    2016-11-15

    Highlights: • Biomimetic surface modification of PP was successfully conducted by integrating mussel-inspired technology, thiol chemistry and cell outer membranes-like structures. • The resultant biomimetic surface exhibits good interface and surface stability. • The obvious suppression of protein adsorption and platelet adhesion is also achieved. • The residue thoil groups on the surface could be further functionalized. - Abstract: Biomimetic surface modification of polypropylene (PP) is conducted by surface chain transfer reaction based on the mussel-inspired versatile adhesion technology and thiol chemistry, using 2-methacryloyloxyethylphosphorylcholine (MPC) as a hydrophilic monomer mimicking the cell outer membrane structure and 2,2-azobisisobutyronitrile (AIBN) as initiator in ethanol. A layer of polydopamine (PDA) is firstly deposited onto PP surface, which not only offers good interfacial adhesion with PP, but also supplies secondary reaction sites (-NH{sub 2}) to covalently anchor thiol groups onto PP surface. Then the radical chain transfer to surface-bonded thiol groups and surface re-initiated polymerization of MPC lead to the formation of a thin layer of polymer brush (PMPC) with cell outer membrane mimetic structure on PP surface. X-ray photoelectron spectrophotometer (XPS), atomic force microscopy (AFM) and water contact angle measurements are used to characterize the PP surfaces before and after modification. The protein adsorption and platelet adhesion experiments are also employed to evaluate the interactions of PP surface with biomolecules. The results show that PMPC is successfully grafted onto PP surface. In comparison with bare PP, the resultant PP-PMPC surface exhibits greatly improved protein and platelet resistance performance, which is the contribution of both increased surface hydrophilicity and zwitterionic structure. More importantly, the residue thiol groups on PP-PMPC surface create a new pathway to further functionalize such

  12. Crack path and fracture surface modifications in cement composites

    Directory of Open Access Journals (Sweden)

    Sajjad Ahmad

    2015-10-01

    Full Text Available There is a tremendous increase in the use of high strength and high performance self-consolidating cementitious composites due to their superior workability and mechanical strengths. Cement composites are quasi-brittle in nature and possess extremely low tensile strength as compared to their compressive strength. Due to the low tensile strength capacity, cracks develop in cementitious composites due to the drying shrinkage, plastic settlements and/or stress concentrations (due to external restrains and/or applied stresses etc. These cracks developed at the nanoscale may grow rapidly due to the applied stresses and join together to form micro and macro cracks. The growth of cracks from nanoscale to micro and macro scale is very rapid and may lead to sudden failure of the cement composites. The present paper reports the modifications in the crack growth pattern of the high performance cement composites to achieve enhanced ductility and toughness. The objective was accomplished by the incorporation of the micro sized inert particulates in the cement composite matrix. The results indicate that the incorporation of micro sized inert particles acted as the obstacles in the growth of the cracks thus improving the ductility and the energy absorption capacity of the self-consolidating cementitious composites.

  13. Design of Surface Modifications for Nanoscale Sensor Applications

    Directory of Open Access Journals (Sweden)

    Erik Reimhult

    2015-01-01

    Full Text Available Nanoscale biosensors provide the possibility to miniaturize optic, acoustic and electric sensors to the dimensions of biomolecules. This enables approaching single-molecule detection and new sensing modalities that probe molecular conformation. Nanoscale sensors are predominantly surface-based and label-free to exploit inherent advantages of physical phenomena allowing high sensitivity without distortive labeling. There are three main criteria to be optimized in the design of surface-based and label-free biosensors: (i the biomolecules of interest must bind with high affinity and selectively to the sensitive area; (ii the biomolecules must be efficiently transported from the bulk solution to the sensor; and (iii the transducer concept must be sufficiently sensitive to detect low coverage of captured biomolecules within reasonable time scales. The majority of literature on nanoscale biosensors deals with the third criterion while implicitly assuming that solutions developed for macroscale biosensors to the first two, equally important, criteria are applicable also to nanoscale sensors. We focus on providing an introduction to and perspectives on the advanced concepts for surface functionalization of biosensors with nanosized sensor elements that have been developed over the past decades (criterion (iii. We review in detail how patterning of molecular films designed to control interactions of biomolecules with nanoscale biosensor surfaces creates new possibilities as well as new challenges.

  14. Modification of polyvinyl alcohol surface properties by ion implantation

    Energy Technology Data Exchange (ETDEWEB)

    Pukhova, I.V., E-mail: ivpuhova@mail.ru [National Research Tomsk State University, 36 Lenin Ave, Tomsk 634050 (Russian Federation); Institute of High Current Electronics, 2/3 Akademichesky Ave, Tomsk 634055 (Russian Federation); Kurzina, I.A. [National Research Tomsk State University, 36 Lenin Ave, Tomsk 634050 (Russian Federation); Savkin, K.P. [Institute of High Current Electronics, 2/3 Akademichesky Ave, Tomsk 634055 (Russian Federation); Laput, O.A. [National Research Tomsk Polytechnic University, 30 Lenin Ave, Tomsk 634050 (Russian Federation); Oks, E.M. [Institute of High Current Electronics, 2/3 Akademichesky Ave, Tomsk 634055 (Russian Federation)

    2017-05-15

    We describe our investigations of the surface physicochemical properties of polyvinyl alcohol modified by silver, argon and carbon ion implantation to doses of 1 × 10{sup 14}, 1 × 10{sup 15} and 1 × 10{sup 16} ion/cm{sup 2} and energies of 20 keV (for C and Ar) and 40 keV (for Ag). Infrared spectroscopy (IRS) indicates that destructive processes accompanied by chemical bond (−C=O) generation are induced by implantation, and X-ray photoelectron spectroscopy (XPS) analysis indicates that the implanted silver is in a metallic Ag3d state without stable chemical bond formation with polymer chains. Ion implantation is found to affect the surface energy: the polar component increases while the dispersion part decreases with increasing implantation dose. Surface roughness is greater after ion implantation and the hydrophobicity increases with increasing dose, for all ion species. We find that ion implantation of Ag, Ar and C leads to a reduction in the polymer microhardness by a factor of five, while the surface electrical resistivity declines modestly.

  15. Effect of surface modification of Grewia optiva fibres on their ...

    Indian Academy of Sciences (India)

    weight to get the final weight (Wf). The percent weight loss was determined by using the following formula: % Wt loss = Wi − Wf. Wi. × 100. 3.2 Swelling behaviour. The swelling behaviour of the raw and surface modified sam- ples of Grewia optiva fibre was studied in different solvents such as water, butanol, dimethyl ...

  16. Mapping physicochemical surface modifications of flame-treated polypropylene

    Directory of Open Access Journals (Sweden)

    S. Farris

    2014-04-01

    Full Text Available The aim of this work was to investigate how the surface morphology of polypropylene (PP is influenced by the surface activation mediated by a flame obtained using a mixture of air and propane under fuel-lean (equivalence ratio φ = 0.98 conditions. Morphological changes observed on flamed samples with smooth (S, medium (M, and high (H degree of surface roughness were attributed to the combined effect of a chemical mechanism (agglomeration and ordering of partially oxidized intermediate-molecular-weight material with a physical mechanism (flattening of the original roughness by the flame’s high temperature. After two treatments, the different behavior of the samples in terms of wettability was totally reset, which made an impressive surface energy of ~43 mJ•m–2 possible, which is typical of more hydrophilic polymers (e.g., polyethylene terephthalate – PET. In particular, the polar component was increased from 1.21, 0.08, and 0.32 mJ•m–2 (untreated samples to 10.95, 11.20, and 11.17 mJ•m–2 for the flamed samples S, M, and H, respectively, an increase attributed to the insertion of polar functional groups (hydroxyl and carbonyl on the C–C backbone, as demonstrated by the X-ray photoelectron spectroscopy results.

  17. Modification of surface properties of LLDPE by water plasma discharge

    International Nuclear Information System (INIS)

    Chantara Thevy Ratnam; Hill, D.J.T.; Firas Rasoul; Whittaker, A.K.; Imelda Keen

    2007-01-01

    Linear low density polyethylene (LLDPE) surface was modified by water plasma treatment. The LLDPE surface was treated at 10 and 20 W discharge power at various exposure times. A laboratory scale Megatherm radio frequency (RF) plasma apparatus that operates at 27 MHz was used to generate the water plasmas. The changes in chemical structure of the LLDPE polymeric chain upon plasma treatment were characterized by FTIR and XPS techniques. The selectivity of trifluoroacetic anhydride (TFAA) toward hydroxyl groups is used to quantify the hydroxyl groups formed on the polymer surface upon plasma treatment. After exposition to the plasma discharge a decline in water contact angle were observed. FTIR and XPS measurements indicate an oxidation of degraded polymeric chains and creation of hydroxyl, carbonyl, ether, ester and carboxyl groups. Chemical derivatization with TFAA of water plasma treated polymer surfaces has shown that under the conditions employed, a very small (less than 5%) of the oxygen introduced by the water plasma treatment was present as hydroxyl group. (Author)

  18. Some environmental problems and their satellite monitoring. [anthropogenic modifications of earth surface

    Science.gov (United States)

    Otterman, J.

    1975-01-01

    Anthropogenic modification of the earth's surface is discussed in two problem areas: (1) land use changes and overgrazing, and how it affects albedo and land surface-atmosphere interactions, and (2) water and land surface pollution, especially oil slicks. A literature survey evidences the importance of these problems. The need for monitoring is stressed, and it is suggested that with some modifications to the sensors, ERTS (Landsat) series satellites can provide approximate monitoring information. The European Landsat receiving station in Italy will facilitate data collection for the tasks described.

  19. Biofouling behavior and performance of forward osmosis membranes with bioinspired surface modification in osmotic membrane bioreactor.

    Science.gov (United States)

    Li, Fang; Cheng, Qianxun; Tian, Qing; Yang, Bo; Chen, Qianyuan

    2016-07-01

    Forward osmosis (FO) has received considerable interest for water and energy related applications in recent years. Biofouling behavior and performance of cellulose triacetate (CTA) forward osmosis membranes with bioinspired surface modification via polydopamine (PD) coating and poly (ethylene glycol) (PEG) grafting (PD-g-PEG) in a submerged osmotic membrane bioreactor (OMBR) were investigated in this work. The modified membranes exhibited lower flux decline than the pristine one in OMBR, confirming that the bioinspired surface modification improved the antifouling ability of the CTA FO membrane. The result showed that the decline of membrane flux related to the increase of the salinity and MLSS concentration of the mixed liquid. It was concluded that the antifouling ability of modified membranes ascribed to the change of surface morphology in addition to the improvement of membrane hydrophilicity. The bioinspired surface modifications might improve the anti-adhesion for the biopolymers and biocake. Copyright © 2016 Elsevier Ltd. All rights reserved.

  20. Surface Modification of Cored, Thin Walled Castings of Nickel Superalloy IN-713C

    Directory of Open Access Journals (Sweden)

    Binczyk F.

    2015-09-01

    Full Text Available In current casting technology of cored, thin walled castings, the modifying coating is applied on the surface of wax pattern and, after the removal of the wax, is transferred to inner mould surface. This way the modification leading to grain refinement occur on the surface of the casting. In thin walled castings the modification effect can also be seen on the other (external side of the casting. Proper reproduction of details in thin walled castings require high pouring temperature which intensify the chemical reactions on the mould – molten metal interface. This may lead to degradation of the surface of the castings. The core modification process is thought to circumvent this problem. The modifying coating is applied to the surface of the core. The degradation of internal surface of the casting is less relevant. The most important factor in this technology is “trough” modification – obtaining fine grained structure on the surface opposite to the surface reproduced by the core.

  1. Research on surface modification and infrared emissivity of In2O3: W thin films

    International Nuclear Information System (INIS)

    Fu, Qiang; Wang, Wenwen; Li, Dongliang; Pan, Jiaojiao

    2014-01-01

    Tungsten-doped indium oxide films (In 2 O 3 : W, IWO) were deposited on glass substrates by DC reactive magnetron sputtering method. The as-deposited IWO films have a minimum resistivity of 6.3 × 10 −4 Ω·cm and an average infrared emissivity of 0.22 in 8–14 μm. The average transmittance is about 90% in visible region and above 81% in near-infrared region. Polystyrene microsphere template and DC magnetron sputtering were used to prepare an Ag micro-grid monolayer on the as-deposited IWO films. After surface modification, the resistivity of the films was reduced by 50% and the average infrared emissivity in 8–14 μm also reduced by 25%. The effects of sphere size and sputtering time on the surface morphology, optical and electrical properties, and infrared emissivity of the IWO thin films were investigated and the mechanism was studied. - Highlights: • High performance In 2 O 3 : W (IWO) films were obtained by DC magnetron sputtering. • Micro-grids on surface were prepared by polystyrene microsphere template method. • Influences of micro-grid size and depth on properties of IWO films were analyzed. • High conductivity and transparency in near-infrared region are obtained

  2. Corrosion Behavior and Surface Modification of Mg-Zn Implant Alloys

    Science.gov (United States)

    Ghayad, I. M.; Maamoun, M. A.; Metwally, W. A.; El-Baradie, Z. M.; Abdel-Azim, A. N.

    2016-10-01

    In this study, Mg-Zn alloys (1-4 wt.% Zn) were fabricated with high-purity raw materials using a clean melting process (fluxless method) and a protective atmosphere of CO2 + 0.4 SF6. The as-cast microstructures of the investigated alloys were characterized by optical and scanning electron microscopes, EDS and XRD. Corrosion properties of the prepared alloys were examined in simulated body fluid by electrochemical techniques and immersion test (hydrogen evolution method). Surface modification of the prepared alloys was performed using micro-arc oxidation (MAO) treatment and hydroxyapatite (HA) coating. Microstructure observation revealed that Zn was completely dissolved in the α-Mg matrix up to 2 wt.%. Higher Zn content led to a reduction in the grain size and the development of a second phase (MgZn2). Corrosion testing results revealed that Mg-1,2,3 wt.% Zn have almost the same degradation rate, whereas Mg-4Zn has the highest degradation rate. HA coating on MAO-treated magnesium alloys formed a dense and compact layer on the alloy surface, which had largely improved surface properties and enhanced corrosion resistance of the prepared alloys.

  3. Surface modification of nanodiamond through metal free atom transfer radical polymerization

    Science.gov (United States)

    Zeng, Guangjian; Liu, Meiying; Shi, Kexin; Heng, Chunning; Mao, Liucheng; Wan, Qing; Huang, Hongye; Deng, Fengjie; Zhang, Xiaoyong; Wei, Yen

    2016-12-01

    Surface modification of nanodiamond (ND) with poly(2-methacryloyloxyethyl phosphorylcholine) [poly(MPC)] has been achieved by using metal free surface initiated atom transfer radical polymerization (SI-ATRP). The ATRP initiator was first immobilized on the surface of ND through direct esterification reaction between hydroxyl group of ND and 2-bromoisobutyryl bromide. The initiator could be employed to obtain ND-poly(MPC) nanocomposites through SI-ATRP using an organic catalyst. The final functional materials were characterized by 1H nuclear magnetic resonance, transmission electron microscopy, X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy and thermo gravimetric analysis in detailed. All of these characterization results demonstrated that ND-poly(MPC) have been successfully obtained via metal free photo-initiated SI-ATRP. The ND-poly(MPC) nanocomposites shown enhanced dispersibility in various solvents as well as excellent biocompatibility. As compared with traditional ATRP, the metal free ATRP is rather simple and effective. More importantly, this preparation method avoided the negative influence of metal catalysts. Therefore, the method described in this work should be a promising strategy for fabrication of polymeric nanocomposites with great potential for different applications especially in biomedical fields.

  4. A dynamic duo: pairing click chemistry and postpolymerization modification to design complex surfaces.

    Science.gov (United States)

    Arnold, Rachelle M; Patton, Derek L; Popik, Vladimir V; Locklin, Jason

    2014-10-21

    Advances in key 21st century technologies such as biosensors, biomedical implants, and organic light-emitting diodes rely heavily on our ability to imagine, design, and understand spatially complex interfaces. Polymer-based thin films provide many advantages in this regard, but the direct synthesis of polymers with incompatible functional groups is extremely difficult. Using postpolymerization modification in conjunction with click chemistry can circumvent this limitation and result in multicomponent surfaces that are otherwise unattainable. The two methods used to form polymer thin films include physisorption and chemisorption. Physisorbed polymers suffer from instability because of the weak intermolecular forces between the film and the substrate, which can lead to dewetting, delamination, desorption, or displacement. Covalent immobilization of polymers to surfaces through either a "grafting to" or "grafting from" approach provides thin films that are more robust and less prone to degradation. The grafting to technique consists of adsorbing a polymer containing at least one reactive group along the backbone to form a covalent bond with a complementary surface functionality. Grafting from involves polymerization directly from the surface, in which the polymer chains deviate from their native conformation in solution and stretch away from the surface because of the high density of chains. Postpolymerization modification (PPM) is a strategy used by our groups over the past several years to immobilize two or more different chemical functionalities onto substrates that contain covalently grafted polymer films. PPM exploits monomers with reactive pendant groups that are stable under the polymerization conditions but are readily modified via covalent attachment of the desired functionality. "Click-like" reactions are the most common type of reactions used for PPM because they are orthogonal, high-yielding, and rapid. Some of these reactions include thiol-based additions

  5. Surface Modification of Magnetic Nanoparticles Using Gum Arabic

    International Nuclear Information System (INIS)

    Williams, Darryl N.; Gold, Katie A.; Holoman, Tracey R. Pulliam; Ehrman, Sheryl H.; Wilson, Otto C.

    2006-01-01

    Magnetite nanoparticles were synthesized and functionalized by coating the particle surfaces with gum arabic (GA) to improve particle stability in aqueous suspensions (i.e. biological media). Particle characterization was performed using transmission electron microscopy (TEM) and dynamic light scattering (DLS) to analyze the morphology and quantify the size distribution of the nanoparticles, respectively. The results from DLS indicated that the GA-treated nanoparticles formed smaller agglomerates as compared to the untreated samples over a 30-h time frame. Thermogravimetric analyses indicated an average weight loss of 23%, showing that GA has a strong affinity toward the iron oxide surface. GA most likely contributes to colloid stability via steric stabilization. It was determined that the adsorption of GA onto magnetite exhibits Langmuir behavior

  6. Surface Modification of Magnetic Nanoparticles Using Gum Arabic

    Energy Technology Data Exchange (ETDEWEB)

    Williams, Darryl N., E-mail: williamsdar@E-mail.chop.edu; Gold, Katie A.; Holoman, Tracey R. Pulliam; Ehrman, Sheryl H. [University of Maryland, Department of Chemical Engineering (United States); Wilson, Otto C. [Catholic University, Department of Biomedical Engineering (United States)

    2006-10-15

    Magnetite nanoparticles were synthesized and functionalized by coating the particle surfaces with gum arabic (GA) to improve particle stability in aqueous suspensions (i.e. biological media). Particle characterization was performed using transmission electron microscopy (TEM) and dynamic light scattering (DLS) to analyze the morphology and quantify the size distribution of the nanoparticles, respectively. The results from DLS indicated that the GA-treated nanoparticles formed smaller agglomerates as compared to the untreated samples over a 30-h time frame. Thermogravimetric analyses indicated an average weight loss of 23%, showing that GA has a strong affinity toward the iron oxide surface. GA most likely contributes to colloid stability via steric stabilization. It was determined that the adsorption of GA onto magnetite exhibits Langmuir behavior.

  7. Ultrasound enhanced plasma surface modification at atmospheric pressure

    DEFF Research Database (Denmark)

    Kusano, Yukihiro; Singh, Shailendra Vikram; Norrman, Kion

    2012-01-01

    Efficiency of atmospheric pressure plasma treatment can be highly enhanced by simultaneous high power ultrasonic irradiation onto the treating surface. It is because ultrasonic waves with a sound pressure level (SPL) above ∼140 dB can reduce the thickness of a boundary gas layer between the plasma...... arc at atmospheric pressure to study adhesion improvement. The effect of ultrasonic irradiation with the frequency diapason between 20 and 40 kHz at the SPL of ∼150 dB was investigated. After the plasma treatment without ultrasonic irradiation, the wettability was significantly improved....... The ultrasonic irradiation during the plasma treatment consistently enhanced the treatment efficiency. The principal effect of ultrasonic irradiation can be attributed to enhancing surface oxidation during plasma treatment. In addition, ultrasonic irradiation can suppress arcing, and the uniformity...

  8. Surface modification of stainless steel by carbon/nitrogen implantation

    Czech Academy of Sciences Publication Activity Database

    Jirásková, Yvonna; Schneeweiss, Oldřich; Havlíček, Stanislav; Blawert, C.; Kalvelage, H.

    2001-01-01

    Roč. 51, č. 7 (2001), s. 693-701 ISSN 0011-4626. [International Colloquium "Mössbauer Spectroscopy in Material Science". Velké Losiny, 03.09.2000-08.09.2000] R&D Projects: GA MŠk OC 516.60; GA MŠk ME 373 Institutional research plan: CEZ:AV0Z2041904 Keywords : surface * phase analysis * hardness Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.345, year: 2001

  9. Using a nitrilase for the surface modification of acrylic fibres

    OpenAIRE

    Matamá, Maria Teresa; Carneiro, Ana Filipa Gonçalves da Costa; Caparrós Vásquez, Cristina Maria; Gübitz, Georg M.; Paulo, Artur Cavaco

    2007-01-01

    The surface of an acrylic fibre was modified with a commercial nitrilase (EC 3.5.5.1). The effect of fibre solvents and polyols on nitrilase catalysis efficiency and stability was investigated. The nitrilase action on the acrylic fabric was improved by the combined addition of 1 M sorbitol and 4% N, N-dimethylacetamide. The colour levels for samples treated with nitrilase increased 156% comparing to the control samples. When the additives were introduced in the treatment media, the colour lev...

  10. Surface modification of cured cement pastes by silane coupling agents.

    Science.gov (United States)

    Stewart, Andrew; Schlosser, Brett; Douglas, Elliot P

    2013-02-01

    X-ray photoelectron spectroscopy (XPS) and static contact angle measurements were used to study the interaction between silane coupling agents and cured cement paste. Three different silane coupling agents were investigated: aminopropyltriethoxy silane (APTES), 3-glycidyloxypropyltrimethoxy silane (GPTMS), and methoxy-terminated polydimethxyl siloxane (PDMS). These silanes have different end groups, so the change in surface energy after undergoing a successful reaction between the silane and hydroxyls on the surface of the cement paste was demonstrated by a change in contact angle. Relative to untreated samples, APTES samples decreased the contact angle, PDMS samples increased the contact angle, and GPTMS did not show a significant change in contact angle. Samples with a water-to-cement ratio (w/c) of 0.5 showed a larger change in contact angle than 0.4 w/c ratio samples, because of a greater number of hydroxyl groups at the surface. Deconvolution of the O 1s and Si 2p XPS peaks were performed to determine contributions from bridging and nonbridging atoms. An increase in bridging silicon and oxygen atoms relative to untreated samples indicated successful silane condensation and that a covalent bond was formed between the cement paste and silanes.

  11. Photoresponsive cellulose fibers by surface modification with multifunctional cellulose derivatives.

    Science.gov (United States)

    Grigoray, Olga; Wondraczek, Holger; Heikkilä, Elina; Fardim, Pedro; Heinze, Thomas

    2014-10-13

    Eucalyptus bleached kraft pulp fibers were modified by adsorption of novel bio-based multifunctional cellulose derivatives in order to generate light responsive surfaces. The cellulose derivatives used were decorated with both cationic groups (degree of substitution, DS of 0.34) and photoactive groups (DS of 0.11 and 0.37). The adsorption was studied by UV-vis spectroscopy, surface plasmon resonance (SPR) and time-of-flight secondary ion mass spectroscopy (ToF-SIMS). The adsorption isotherms followed the Freundlich model and it turned out that the main driving force for the adsorption was electrostatic interaction. Moreover, strong indications for hydrophobic interactions between the fibers and the derivatives and the derivatives themselves were found. ToF-SIMS imaging revealed an even distribution of the derivatives on the fiber surfaces. The modified fibers underwent fast photocrosslinking under UV-irradiation as demonstrated by light absorbance and fluorescence measurements. Thus, our results proved that the modified fibers exhibited light-responsive properties and can potentially be used for the manufacture of smart bio-based materials. Copyright © 2014 Elsevier Ltd. All rights reserved.

  12. The surface modification of clay particles by RF plasma technique

    Science.gov (United States)

    Lee, Sang-Keol

    In this study, the surface coatings of ball clay, organoclay and exfoliated clay prepared by sol-gel process were done by RF plasma polymerization to improve the surface activity of the clay filler. Characterization of the above plasma-treated clays has been carried out by various techniques. The effects of plasma-treated clays as substitute of carbon black in styrene-butadiene rubber (SBR) and ethylene-propylene-diene monomer (EPDM) on the curing and mechanical properties were investigated. After plasma treatment, the tensile properties of organo and exfoliated clay were not unsatisfactory to that of carbon black filler system. Moreover, only 10 phr filler loading of plasma-treated organoclay in EPDM vulcanizates showed better results than 40 phr filler loading of carbon black in EPDM vulcanizates. The main objective of this study was to verify the applicability of the plasma technique for modifying clay surfaces for their use in the tire manufacturing industry. Another purpose was to reveal the advantage of the plasma technique used to obtain modified-clay and improved properties that those materials can display.

  13. The Effect of Surface Modification on Gliding Ability of Decellularized Flexor Tendon in a Canine Model In Vitro

    Science.gov (United States)

    Ozasa, Yasuhiro; Amadio, Peter C.; Thoreson, Andrew R.; An, Kai-Nan; Zhao, Chunfeng

    2013-01-01

    Purpose To investigate the gliding ability and mechanical properties of decellularized intrasynovial tendons without and with surface modification designed to reduce gliding resistance. Methods Thirty-three canine flexor digitorum profundus tendons were randomly assigned to one of 3 groups: untreated fresh tendons, to serve as a control; tendons decellularized with trypsin and Triton X-100; and tendons decellularized as in group 2 with surface modification using carbodiimide-derivatized hyaluronic acid and gelatin (cd- HA-gelatin). Tendons were subjected to cyclic friction testing for 1000 cycles with subsequent tensile stiffness testing. The surface roughness after 1000 cycles was qualitatively evaluated using scanning electron microscopy. Results The gliding resistance of the decellularized group was significantly higher than that of both the control and cd-HA-gelatin tendons (0.20N, 0.09N and 0.11N after the first cycle, 0.41N, 0.09N and 0.14N after 1000 cycles, respectively).Gliding resistance between the control and cd-HA-gelatin groups was not significantly different. The Young modulus was not significantly different between the 3 groups. The surfaces of the control and cd-HA-gelatin treated tendons appeared smooth after 1000 cycles, while those of the decellularized tendons appeared rougher under scanning electron microscopy observation. Conclusions Decellularization with trypsin and Triton X-100 did not change tendon stiffness. However, this treatment, while effective in removing cells, adversely altered the tendon surface, both in appearance and gliding resistance. Surface modification with cd- HA-gelatin improved the tendon surface smoothness and significantly decreased the gliding resistance. Clinical Relevance The combination of decellularization and surface modification may improve the function of tendon allografts when used clinically. PMID:23849733

  14. Surface modification induced enhanced CO2 sorption in cucurbit[6]uril, an organic porous material.

    Science.gov (United States)

    Mohan, Midhun; Suzuki, T; Nair, Akhil K; Pillai, Saju; Warrier, K G K; Hareesh, U S; Nair, Balagopal N; Gale, J D

    2017-09-27

    The CO 2 adsorption properties of an organic macrocycle, cucurbit[6]uril (CB[6]), have been evaluated through experimental and theoretical studies. Quantum mechanical calculations show that CB[6] is capable of adsorbing the CO 2 molecule selectively within its cavity relative to nitrogen. Adsorption experiments at 298 K and at 1 bar pressure gave a CO 2 adsorption value of 1.23 mmol g -1 for the unmodified material. Significant enhancements in the CO 2 adsorption capacity of the material were experimentally demonstrated through surface modification using physical and chemical methods. Ethanolamine (EA) modified CB[6] provided an excellent sorption selectivity value of 121.4 for CO 2 /N 2 at 323 K and is unique with respect to its discrimination potential between CO 2 and N 2 . The chemical nature of the interaction between CO 2 and amine is shown to be the primary mechanism for the enhanced CO 2 absorption performance.

  15. Albumin based versatile multifunctional nanocarriers for cancer therapy: Fabrication, surface modification, multimodal therapeutics and imaging approaches.

    Science.gov (United States)

    Kudarha, Ritu R; Sawant, Krutika K

    2017-12-01

    Albumin is a versatile protein used as a carrier system for cancer therapeutics. As a carrier it can provide tumor specificity, reduce drug related toxicity, maintain therapeutic concentration of the active moiety like drug, gene, peptide, protein etc. for long period of time and also reduce drug related toxicities. Apart from cancer therapy, it is also utilized in the imaging and multimodal therapy of cancer. This review highlights the important properties, structure and types of albumin based nanocarriers with regards to their use for cancer targeting. It also provides brief discussion on methods of preparation of these nanocarriers and their surface modification. Applications of albumin nanocarriers for cancer therapy, gene delivery, imaging, phototherapy and multimodal therapy have also been discussed. This review also provides brief discussion about albumin based marketed nano formulations and those under clinical trials. Copyright © 2017 Elsevier B.V. All rights reserved.

  16. PES Surface Modification Using Green Chemistry: New Generation of Antifouling Membranes.

    Science.gov (United States)

    Nady, Norhan

    2016-04-18

    A major limitation in using membrane-based separation processes is the loss of performance due to membrane fouling. This drawback can be addressed thanks to surface modification treatments. A new and promising surface modification using green chemistry has been recently investigated. This modification is carried out at room temperature and in aqueous medium using green catalyst (enzyme) and nontoxic modifier, which can be safely labelled "green surface modification". This modification can be considered as a nucleus of new generation of antifouling membranes and surfaces. In the current research, ferulic acid modifier and laccase bio-catalyst were used to make poly(ethersulfone) (PES) membrane less vulnerable to protein adsorption. The blank and modified PES membranes are evaluated based on e.g., their flux and protein repellence. Both the blank and the modified PES membranes (or laminated PES on silicon dioxide surface) are characterized using many techniques e.g., SEM, EDX, XPS and SPM, etc. The pure water flux of the most modified membranes was reduced by 10% on average relative to the blank membrane, and around a 94% reduction in protein adsorption was determined. In the conclusions section, a comparison between three modifiers-ferulic acid, and two other previously used modifiers (4-hydroxybenzoic acid and gallic acid)-is presented.

  17. Protein surface topology-probing by selective chemical modification and mass spectrometric peptide mapping.

    OpenAIRE

    Suckau, D; Mak, M; Przybylski, M

    1992-01-01

    Aminoacetylation of lysine residues and the modification of arginine by 1,2-cyclohexanedione to N7,N8-(dihydroxy-1,2-cyclohexylidene)arginine were used for probing the surface topology of hen-eggwhite lysozyme as a model protein. The molecular identification of lysine and arginine modification sites was provided by molecular weight determinations of modified and unmodified tryptic peptide mixtures (peptide mapping) using 252Cf plasma desorption mass spectrometry. At conditions of limited chem...

  18. Pool boiling CHF enhancement by micro/nanoscale modification of zircaloy-4 surface

    International Nuclear Information System (INIS)

    Ahn, Ho Seon; Lee, Chan; Kim, Hyungdae; Jo, HangJin; Kang, SoonHo; Kim, Joonwon; Shin, Jeongseob; Kim, Moo Hwan

    2010-01-01

    Consideration of the critical heat flux (CHF) requires difficult compromises between economy and safety in many types of thermal systems, including nuclear power plants. Much research has been directed towards enhancing the CHF, and many recent studies have revealed that the significant CHF enhancement in nanofluids is due to surface deposition of nanoparticles. The surface deposition of nanoparticles influenced various surface characteristics. This fact indicated that the surface wettability is a key parameter for CHF enhancement and so is the surface morphology. In this study, surface wettability of zircaloy-4 used as cladding material of fuel rods in nuclear power plants was modified using surface treatment technique (i.e. anodization). Pool boiling experiments of distilled water on the prepared surfaces was conducted at atmospheric and saturated conditions to examine effects of the surface modification on CHF. The experimental results showed that CHF of zircaloy-4 can be significantly enhanced by the improvement in surface wettability using the surface modification, but only the wettability effect cannot explain the CHF increase on the treated zircaloy-4 surfaces completely. It was found that below a critical value of contact angle (10 o ), micro/nanostructures created by the surface treatment increased spreadability of liquid on the surface, which could lead to further increase in CHF even beyond the prediction caused only by the wettability improvement. These micro/nanostructures with multiscale on heated surface induced more significant CHF enhancement than it based on the wettability effect, due to liquid spreadability.

  19. Ion beam modification of surfaces for biomedical applications

    International Nuclear Information System (INIS)

    Sommerfeld, Jana

    2014-01-01

    Human life expectancy increased significantly within the last century. Hence, medical care must ever be improved. Optimizing artificial replacements such as hip joints or stents etc. is of special interest. For this purpose, new materials are constantly developed or known ones modified. This work focused on the possibility to change the chemistry and topography of biomedically relevant materials such as diamond-like carbon (DLC) and titanium dioxide (TiO 2 ) by means of ion beam irradiation. Mass-separated ion beam deposition was used in order to synthesize DLC layers with a high sp 3 content (> 70%), a sufficiently smooth surface (RMS<1 nm) and a manageable film thickness (50 nm). The chemistry of the DLC layers was changed by ion beam doping with different ion species (Ag,Ti) and concentrations. Additionally, the surface topography of silicon and titanium dioxide was altered by ion beam irradiation under non-perpendicular angle of incidence. The created periodic wave structures (so-called ripples) were characterized and their dependency on the ion energy was investigated. Moreover, ripples on silicon were covered with a thin DLC layer in order to create DLC ripples. The biocompatibility of all samples was investigated by adsorption experiments. For this purpose, human plasma fibrinogen (HPF) was used due to its ambiphilic character, which allows the protein to assume different conformations on materials with different hydrophilicities. Moreover, HPF is a crucial factor in the blood coagulation process. This work comes to the conclusion that the interaction of both, the surface chemistry and topography, has a strong influence on the adsorption behavior of HPF and thus the biocompatibility of a material. Both factors can be specifically tuned by means of ion beam irradiation.

  20. Surface property modification of coatings via self-stratification

    Science.gov (United States)

    Pieper, Robert Joseph

    Biological fouling occurs everywhere in the marine environment and is a significant problem for marine vessels. Anti-fouling coatings have been used effectively to prevent fouling; however, these coatings harm non-targeted sea-life. Fouling-release coatings (FRC) appear to be an alternative way to combat fouling. FRC do not necessarily prevent the settlement of marine organisms but rather allow their easy removal with application of shear to the coatings surface. These coatings must be non-toxic, non-leaching, have low surface energy, low modulus, and durability to provide easy removal of marine organisms. Here the goal is to develop FRC based on thermosetting siloxane-polyurethane, amphiphilic polyurethane, and zwitterionic/amphiphilic polyurethane systems. A combinatorial high-throughput approach has been taken in order to explore the variables that may affect the performance of the final coatings. Libraries of acrylic polyols were synthesized using combinatorial high-throughput techniques by either batch or semi-batch processes. The design of the experiments for the batch and semi-batch processes were done combinatorially to explore a range of compositions and various reaction process variables that cannot be accomplished or are not suitable for single reaction experiments. Characterization of Rapid-GPC, high-throughput DSC, and gravimetrically calculated percent solids verified the effects of different reaction conditions on the MW, glass transition temperatures, and percent conversion of the different compositions of acrylic polyols. Coatings were characterized for their surface energy, pseudobarnacle pull-off adhesion, and were subjected to bioassays including marine bacteria, algae, and barnacles. From the performance properties results the acrylic polyol containing 20% hydroxyethyl acrylate and 80% butyl acrylate was selected for further siloxane-polyurethane formulations and were subjected to the same physical, mechanical, and performance testing

  1. Organic synthesis - applications in enzymatic studies, catalysis and surface modification

    DEFF Research Database (Denmark)

    Viart, Helene Marie-France

    as liposomes and the enzymatic activity was studied. Hydrolysis (or absence of hydrolysis) was monitored by MALDI-TOF-MS. The results observedin these experiments are compared to MD predictions and confirm them. The second chapter deals with surface functionalization of liposomes. The copper mediated [3......: a C3symmetric phosphine oxide has been synthesised, which we intend to test, after reduction to the phosphin, as a ligand in organometallic catalysed reactions. The ultimate goal is to obtain enantioselectivity, introduced by the organization of aryl substituents around phosphorous in our ligand....

  2. Interfacing biomembrane mimetic polymer surfaces with living cells - Surface modification for reliable bioartificial liver

    International Nuclear Information System (INIS)

    Iwasaki, Yasuhiko; Takami, Utae; Sawada, Shin-ichi; Akiyoshi, Kazunari

    2008-01-01

    The surface design used for reducing nonspecific biofouling is one of the most important issues for the fabrication of medical devices. We present here a newly synthesized a carbohydrate-immobilized phosphorylcholine polymer for surface modification of medical devices to control the interface with living cells. A random copolymer composed of 2-methacryloyloxyethyl phosphorylcholine (MPC), n-butyl methacrylate (BMA), and 2-lactobionamidoethyl methacrylate (LAMA) was synthesized by conventional radical polymerization. The monomer feeding ratio in the copolymer was adjusted to 24/75/1 (MPC/BMA/LAMA). The copolymer (PMBL1.0) could be coated by solvent evaporation from an ethanol solution. Cells of the human hepatocellular liver carcinoma cell line (HepG2) having asialoglycoprotein receptors (ASGPRs) were seeded on PMBL1.0 or poly(BMA) (PBMA)-coated PET plates. On PBMA, many adherent cells were observed and were well spread with monolayer adhesion. HepG2 adhesion was observed on PMBL1.0 because the cell has ASGPRs. Furthermore, some of the cells adhering to PMBL1.0 had a spheroid formation and similarly shaped spheroids were scattered on the surface. According to confocal laser microscopic observation after 96 h cultivation, it was found that albumin production preferentially occurred in the center of the spheroid. The albumin production of the cells that adhered to PBMA was sparse. The amount of albumin production per unit cell that adhered to PMBL1.0 was determined by ELISA and was significantly higher than that which adhered to PBMA. Long-term cultivation of HepG2 was also performed using hollow fiber mini-modules coated with PMBL1.0. The concentration of albumin produced from HepG2 increased continuously for one month. In the mini-module, the function of HepG2 was effectively preserved for that period. On the hollow fiber membrane, spheroid formation of HepG2 cells was also observed. In conclusion, PMBL1.0 can provide a suitable surface for the cultivation of

  3. Concatenation of electrochemical grafting with chemical or electrochemical modification for preparing electrodes with specific surface functionality

    International Nuclear Information System (INIS)

    Verma, Pallavi; Maire, Pascal; Novak, Petr

    2011-01-01

    Surface modified electrodes are used in electro-analysis, electro-catalysis, sensors, biomedical applications, etc. and could also be used in batteries. The properties of modified electrodes are determined by the surface functionality. Therefore, the steps involved in the surface modification of the electrodes to obtain specific functionality are of prime importance. We illustrate here bridging of two routes of surface modifications namely electrochemical grafting, and chemical or electrochemical reduction. First, by electrochemical grafting an organic moiety is covalently immobilized on the surface. Then, either by chemical or by electrochemical route the terminal functional group of the grafted moiety is transformed. Using the former route we prepared lithium alkyl carbonate (-O(CH 2 ) 3 OCO 2 Li) modified carbon with potential applications in batteries, and employing the latter we prepared phenyl hydroxyl amine (-C 6 H 4 NHOH) modified carbon which may find application in biosensors. Benzyl alcohol (-C 6 H 4 CH 2 OH) modified carbon was prepared by both chemical as well as electrochemical route. We report combinations of conjugating the two steps of surface modifications and show how the optimal route of terminal functional group modification depends on the chemical nature of the moiety attached to the surface in the electrochemical grafting step.

  4. Nanoscale surface modifications to control capillary flow characteristics in PMMA microfluidic devices

    Directory of Open Access Journals (Sweden)

    Mukhopadhyay Subhadeep

    2011-01-01

    Full Text Available Abstract Polymethylmethacrylate (PMMA microfluidic devices have been fabricated using a hot embossing technique to incorporate micro-pillar features on the bottom wall of the device which when combined with either a plasma treatment or the coating of a diamond-like carbon (DLC film presents a range of surface modification profiles. Experimental results presented in detail the surface modifications in the form of distinct changes in the static water contact angle across a range from 44.3 to 81.2 when compared to pristine PMMA surfaces. Additionally, capillary flow of water (dyed to aid visualization through the microfluidic devices was recorded and analyzed to provide comparison data between filling time of a microfluidic chamber and surface modification characteristics, including the effects of surface energy and surface roughness on the microfluidic flow. We have experimentally demonstrated that fluid flow and thus filling time for the microfluidic device was significantly faster for the device with surface modifications that resulted in a lower static contact angle, and also that the incorporation of micro-pillars into a fluidic device increases the filling time when compared to comparative devices.

  5. Influence of surface modification techniques on shear bond strength between different zirconia cores and veneering ceramics

    Science.gov (United States)

    Rismanchian, Mansour; Savabi, Omid; Ashtiani, Alireza Hashemi

    2011-01-01

    PURPOSE Veneering porcelain might be delaminated from underlying zirconia-based ceramics. The aim of this study was the evaluation of the effect of different surface treatments and type of zirconia (white or colored) on shear bond strength (SBS) of zirconia core and its veneering porcelain. MATERIALS AND METHODS Eighty zirconia disks (40 white and 40 colored; 10 mm in diameter and 4 mm thick) were treated with three different mechanical surface conditioning methods (Sandblasting with 110 µm Al2O3 particle, grinding, sandblasting and liner application). One group had received no treatment. These disks were veneered with 3 mm thick and 5 mm diameter Cercon Ceram Kiss porcelain and SBS test was conducted (cross-head speed = 1 mm/min). Two and one way ANOVA, Tukey's HSD Past hoc, and T-test were selected to analyzed the data (α=0.05). RESULTS In this study, the factor of different types of zirconia ceramics (P=.462) had no significant effect on SBS, but the factors of different surface modification techniques (P=.005) and interaction effect (P=.018) had a significant effect on SBS. Within colored zirconia group, there were no significant differences in mean SBS among the four surface treatment subgroups (P=0.183). Within white zirconia group, "Ground group" exhibited a significantly lower SBS value than "as milled" or control (P=0.001) and liner (P=.05) groups. CONCLUSION Type of zirconia did not have any effect on bond strength between zirconia core and veneer ceramic. Surface treatment had different effects on the SBS of the different zirconia types and grinding dramatically decreased the SBS of white zirconia-porcelain. PMID:22259706

  6. Surface modification of austenitic stainless steel by titanium ion implantation

    International Nuclear Information System (INIS)

    Evans, P.J.; Hyvarinen, J.; Samandi, M.

    1995-01-01

    The wear properties of AISI 316 austenitic stainless steel implanted with Ti were investigated for ion doses in the range (2.3-5.4)x10 16 ionscm -2 and average ion energies of 60 and 90keV. The implanted layer was examined by Rutherford backscattering, from which the retained doses were determined, and glow discharge optical emission spectroscopy. Following implantation, the surface microhardness was observed to increase with the greatest change occurring at higher ion energy. Pin-on-disc wear tests and associated friction measurements were also performed under both dry and lubricated conditions using applied loads of 2N and 10N. In the absence of lubrication, breakthrough of the implanted layer occurred after a short sliding time; only for a dose of 5.1x10 16 ionscm -2 implanted at an average energy of 90keV was the onset of breakthrough appreciably delayed. In contrast, the results of tests with lubrication showed a more gradual variation, with the extent of wear decreasing with implant dose at both 2N and 10N loads. Finally, the influence of Ti implantation on possible wear mechanisms is discussed in the light of information provided by several surface characterization techniques. ((orig.))

  7. Cellular interaction influenced by surface modification strategies of gelatin-based nanoparticles.

    Science.gov (United States)

    Tse, Wai Hei; Gyenis, Laszlo; Litchfield, David W; Zhang, Jin

    2017-02-01

    Theranostic applications of gelatin nanospheres require two major components, a method of detection and good biocompatibility. We characterized the response of UTA-6 human osteosarcoma cells to the introduction of functionalized 90 bloom-based gelatin nanospheres (158 ± 49 nm) modified with three elements in different order: (a) hybridization with cadmium-based quantum dots for optical detection, (b) bioconjugation with anti-human IgG FAB (anti-IgG) for cell targeting, with/without (c) capping with polyethylene glycol on the surface for enhanced biocompatibility. A one-pot process is developed for incorporating quantum dots and antibody with gelatin nanospheres. Path A of modifying gelatin nanospheres with quantum dots first followed by anti-IgG resulted in a significantly greater cellular viability than Path B with anti-IgG first followed by quantum dots. Capping with polyethylene glycol as the final step in modification yielded significantly opposing results with decreases in Path A and increases in Path B. Three-dimensional z-stacking fluorescent images of hybrid gelatin nanospheres with anti-IgG is observed to have an increase in cellular association. The observed results suggest the modification order for building hybrid nanospheres may have an impact on cellular response.

  8. Surface morphological modification of crosslinked hydrophilic co-polymers by nanosecond pulsed laser irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Primo, Gastón A.; Alvarez Igarzabal, Cecilia I. [IMBIV (CONICET), Departamento de Química Orgánica, Facultad de Ciencias Químicas, Universidad Nacional de Córdoba, Haya de la Torre y Medina Allende, Edificio de Ciencias II, Ciudad Universitaria, Córdoba X5000HUA (Argentina); Pino, Gustavo A.; Ferrero, Juan C. [INFIQC (CONICET), Departamento de Fisicoquímica, Facultad de Ciencias Químicas, and Centro Láser de Ciencias Moleculares, Universidad Nacional de Córdoba, Córdoba X5000IUS (Argentina); Rossa, Maximiliano, E-mail: mrossa@fcq.unc.edu.ar [INFIQC (CONICET), Departamento de Fisicoquímica, Facultad de Ciencias Químicas, and Centro Láser de Ciencias Moleculares, Universidad Nacional de Córdoba, Córdoba X5000IUS (Argentina)

    2016-04-30

    Graphical abstract: - Highlights: • Laser-induced surface modification of crosslinked hydrophilic co-polymers by ns pulses. • Formation of ablation craters observed under most of the single-pulse experimental conditions. • UV laser foaming of dried hydrogel samples resulting from single- and multiple-pulse experiments. • Threshold values of the incident laser fluence reported for the observed surface modifications. • Lower threshold fluences for acrylate-based, compared to acrylamide-based hydrogels. - Abstract: This work reports an investigation of the surface modifications induced by irradiation with nanosecond laser pulses of ultraviolet and visible wavelengths on crosslinked hydrophilic co-polymeric materials, which have been functionalized with 1-vinylimidazole as a co-monomer. A comparison is made between hydrogels differing in the base co-monomer (N,N-dimethylaminoethyl methacrylate and N-[3-(dimethylamino)propyl] methacrylamide) and in hydration state (both swollen and dried states). Formation of craters is the dominant morphological change observed by ablation in the visible at 532 nm, whereas additional, less aggressive surface modifications, chiefly microfoams and roughness, are developed in the ultraviolet at 266 nm. At both irradiation wavelengths, threshold values of the incident laser fluence for the observation of the various surface modifications are determined under single-pulse laser irradiation conditions. It is shown that multiple-pulse irradiation at 266 nm with a limited number of laser shots can be used alternatively for generating a regular microfoam layer at the surface of dried hydrogels based on N,N-dimethylaminoethyl methacrylate. The observations are rationalized on the basis of currently accepted mechanisms for laser-induced polymer surface modification, with a significant contribution of the laser foaming mechanism. Prospective applications of the laser-foamed hydrogel matrices in biomolecule immobilization are suggested.

  9. Surface modification and droplet formation of tungsten under hot plasma irradiation at the GOL-3

    Science.gov (United States)

    Arzhannikov, A. V.; Bataev, V. A.; Bataev, I. A.; Burdakov, A. V.; Ivanov, I. A.; Ivantsivsky, M. V.; Kuklin, K. N.; Mekler, K. I.; Rovenskikh, A. F.; Polosatkin, S. V.; Postupaev, V. V.; Sinitsky, S. L.; Shoshin, A. A.

    2013-07-01

    The paper presents experimental investigations of tungsten surface modification after plasma loads at the multimirror trap GOL-3. Energy loads on tungsten surface varied from 2 up to 4 MJ/m2 per shot with sets from 1 to 9 repetitive irradiations that corresponds to loads higher than tungsten melting threshold and is close to ITER giant ELM loads. Targets surface modification and transverse microsections after irradiation was studied by optical microscopy, SEM and hardness tester. Formation on tungsten surface of three different crack networks with typical cell sizes of 1000, 10 and 0.3 μm and bubbles are identified. The network of large cracks extend perpendicularly to the irradiated sample surface to a depth of 50-350 μm. Erosion depth depends on energy loads - rises from 20 to 200 μm at 2 and 4 MJ/m2 correspondingly. Cracking, development of tungsten surface morphology and droplets splashing are discussed.

  10. Surface modification and droplet formation of tungsten under hot plasma irradiation at the GOL-3

    International Nuclear Information System (INIS)

    Arzhannikov, A.V.; Bataev, V.A.; Bataev, I.A.; Burdakov, A.V.; Ivanov, I.A.; Ivantsivsky, M.V.; Kuklin, K.N.; Mekler, K.I.; Rovenskikh, A.F.; Polosatkin, S.V.; Postupaev, V.V.; Sinitsky, S.L.; Shoshin, A.A.

    2013-01-01

    The paper presents experimental investigations of tungsten surface modification after plasma loads at the multimirror trap GOL-3. Energy loads on tungsten surface varied from 2 up to 4 MJ/m 2 per shot with sets from 1 to 9 repetitive irradiations that corresponds to loads higher than tungsten melting threshold and is close to ITER giant ELM loads. Targets surface modification and transverse microsections after irradiation was studied by optical microscopy, SEM and hardness tester. Formation on tungsten surface of three different crack networks with typical cell sizes of 1000, 10 and 0.3 μm and bubbles are identified. The network of large cracks extend perpendicularly to the irradiated sample surface to a depth of 50–350 μm. Erosion depth depends on energy loads – rises from 20 to 200 μm at 2 and 4 MJ/m 2 correspondingly. Cracking, development of tungsten surface morphology and droplets splashing are discussed

  11. Surface modification of commercial tin coatings by carbon ion implantation

    Energy Technology Data Exchange (ETDEWEB)

    Liu, L.J.; Sood, D.K.; Manory, R.R. [Royal Melbourne Inst. of Tech., VIC (Australia)

    1993-12-31

    Commercial TiN coatings of about 2 {mu}m thickness on high speed steel substrates were implanted at room temperature with 95 keV carbon ions at nominal doses between 1 x 10{sup 17} - 8x10{sup 17} ions cm{sup -2}. Carbon ion implantation induced a significant improvement in ultramicrohardness, friction coefficient and wear properties. The surface microhardness increases monotonically by up to 115% until a critical dose is reached. Beyond this dose the hardness decreases, but remains higher than that of unimplanted sample. A lower friction coefficient and a longer transition period towards a steady state condition were obtained by carbon ion implantation. The changes in tribomechanical properties are discussed in terms of radiation damage and possible formation of a second phase rich in carbon. 6 refs., 3 figs.

  12. Effect of Reaction Conditions on the Surface Modification of Cellulose Nanofibrils with Aminopropyl Triethoxysilane

    Directory of Open Access Journals (Sweden)

    Eduardo Robles

    2018-04-01

    Full Text Available Nine different surface modifications of cellulose nanofibrils (CNF with 3-aminopropyl triethoxysilane (ATS by using three different solvent systems (water, ethanol, and a mixture of both were investigated. The effect of reaction conditions, such as silane to cellulose ratio and solvent type were evaluated to determine their contribution to the extent of the silane modification. Nanofibril properties were evaluated by infrared spectroscopy, powder X-ray diffraction, surface free energy, thermogravimetry, 13C and 29Si nuclear magnetic resonance, and electronic microscopy. The influence of the solvent in the solvolysis of the silane was reflected in the presence or absence of ethoxy groups in the silane. On the other hand, whereas the surface modification was increased directly proportionally to silane ratio on the reaction, the aggregation of nanofibrils was also increased, which can play a negative role in certain applications. The increment of silane modification also had substantial repercussions on the crystallinity of the nanofibrils by the addition of amorphous components to the crystalline unit; moreover, silane surface modifications enhanced the hydrophobic character of the nanofibrils.

  13. Effect of Surface Modification on Corrosion Resistance of Uncoated and DLC Coated Stainless Steel Surface

    Science.gov (United States)

    Scendo, Mieczyslaw; Staszewska-Samson, Katarzyna

    2017-08-01

    Corrosion resistance of 4H13 stainless steel (EN-X46Cr13) surface uncoated and coated with an amorphous hydrogenated carbon (a-C:H) film [diamond-like carbon (DLC)] in acidic chloride solution was investigated. The DLC films were deposited on steel surface by a plasma deposition, direct current discharge (PDCD) method. The Fourier transform infrared (FTIR) was used to determine the chemical groups existing on DLC films. The surface of the specimens was observed by a scanning electron microscope (SEM). The tribological properties of the both materials were examined using a ball-on disk tribometer. The microhardness (HV) of diamond-like carbon film increased over five times in relation to the 4H13 stainless steel without of DLC coating. Oxidation kinetic parameters were determined by gravimetric and electrochemical methods. The high value of polarization resistance indicates that the DLC film on substrate was characterized by low electrical conductivity. The corrosion rate of 4H13 stainless steel with of DLC film decreased about eight times in relation to uncoated surface of 4H13 stainless steel.

  14. Study on the mechanism of surface modification of magnesium oxysulfate whisker

    Energy Technology Data Exchange (ETDEWEB)

    Dang, Li [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Nai, Xueying; Zhu, Donghai [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008 (China); Jing, Yanwei [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Liu, Xin; Dong, Yaping [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008 (China); Li, Wu, E-mail: driverlaoli@163.com [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008 (China)

    2014-10-30

    Graphical abstract: - Highlights: • Physisorbed lauric acid was ruled out by FT-IR spectroscopy. • The inexistence of physisorbed magnesium laurate was proved by DSC analyses. • {sup 13}C NMR further verified the formation of COO–Mg< bonds on the surface of MOSw. • “Acid-base neutralization” was proved by the pH meter monitoring synchronously. • The type of surface modification of MOSw was proved to be chemical adsorption only. - Abstract: Hydrophobic-lipophilic magnesium oxysulfate whisker (MOSw) was prepared by surface modification with lauric acid and the surface morphology of MOSw was examined with field emission scanning electron microscope (FESEM). X-ray powder diffraction (XRD) was used to characterize the crystalline degree of MOSw and modified MOSw (MOSw-LA). Both FESEM and XRD suggested that modification occurred on the surface of MOSw exclusively. The inexistence of physisorbed lauric acid was proved by Fouier transform infrared (FT-IR) spectroscopy. Thermogravimetric analyses ruled out the possibility that magnesium laurate (LA-Mg) physisorbed on the surface of MOSw-LA. Solid state {sup 13}C nuclear magnetic resonance ({sup 13}C NMR) further verified the formation of COO–Mg< bonds based on the significant changes of chemical shift and decrease in intensity. Hence, we confirmed that the type of surface modification of MOSw with lauric acid was chemical adsorption taken place between lauric acid and Mg<. In order to study the dynamic state approach of this reaction, a pH meter was employed to monitor the reaction process synchronously, and then we proposed a reaction mechanism which was similar to the “acid-base neutralization”. This research provides a detailed explanation for a kind of surface modification, which may be further used in the performance of whisker/polymer matrix composites.

  15. Surface modification of magnesium hydroxide sulfate hydrate whiskers using a silane coupling agent by dry process

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, Donghai, E-mail: zhudonghai-2001@163.com [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining, 810008 (China); Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Chinese Academy of Sciences, Xining, 810008 (China); Nai, Xueying [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining, 810008 (China); Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Chinese Academy of Sciences, Xining, 810008 (China); Lan, Shengjie; Bian, Shaoju [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining, 810008 (China); Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Chinese Academy of Sciences, Xining, 810008 (China); University of Chinese Academy of Sciences, Beijing, 100049 (China); Liu, Xin [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining, 810008 (China); Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Chinese Academy of Sciences, Xining, 810008 (China); Li, Wu, E-mail: driverlaoli@163.com [Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining, 810008 (China); Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Chinese Academy of Sciences, Xining, 810008 (China)

    2016-12-30

    Highlights: • Dry process was adopted to modify the surface of MHSH whiskers using silane. • Si−O−Mg bonds were formed directly by the reaction between Si−OC{sub 2}H{sub 5} and −OH of MHSH. • Dispersibility and compatibility of modified whiskers greatly improved in organic phase. • Thermal stability of whiskers was enhanced after modified. - Abstract: In order to improve the compatibility of magnesium hydroxide sulfate hydrate (MHSH) whiskers with polymers, the surface of MHSH whiskers was modified using vinyltriethoxysilane (VTES) by dry process. The possible mechanism of the surface modification and the interfacial interactions between MHSH whiskers and VTES, as well as the effect of surface modification, were studied. Scanning electronic microscopy (SEM), transmission electron microscopy (TEM) and X-ray powder diffraction (XRD) analyses showed that the agglomerations were effectively separated and a thin layer was formed on the surface of the whiskers after modification. Fourier transform infrared (FT-IR) spectroscopy and X-ray photoelectron spectroscopy (XPS) analyses showed that the VTES molecules were bound to the surface of MHSH whiskers after modification. Chemical bonds (Si−O−Mg) were formed by the reaction between Si−OC{sub 2}H{sub 5} or Si−OH and the hydroxyl group of MHSH whiskers. The effect of surface modification was evaluated by sedimentation tests, contact angle measurements and thermogravimetric analysis (TGA). The results showed that the surface of MHSH whiskers was transformed from hydrophilic to hydrophobic, and the dispersibility and the compatibility of MHSH whiskers were significantly improved in the organic phase. Additionally, the thermal stability of the VTES-modified MHSH whiskers was improved significantly.

  16. Plasma-implantation-based surface modification of metals with single-implantation mode

    Science.gov (United States)

    Tian, X. B.; Cui, J. T.; Yang, S. Q.; Fu, Ricky K. Y.; Chu, Paul K.

    2004-12-01

    Plasma ion implantation has proven to be an effective surface modification technique. Its biggest advantage is the capability to treat the objects with irregular shapes without complex manipulation of target holder. Many metal materials such as aluminum, stainless steel, tool steel, titanium, magnesium etc, has been treated using this technique to improve their wear-resistance, corrosion-resistance, fatigue-resistance, oxidation-resistance, bio-compatiblity etc. However in order to achieve thicker modified layers, hybrid processes combining plasma ion implantation with other techniques have been frequently employed. In this paper plasma implantation based surface modification of metals using single-implantation mode is reviewed.

  17. Transglutaminase-Mediated Modifications of the Rat Sperm Surface in vitro

    Science.gov (United States)

    Paonessa, G.; Metafora, S.; Tajana, G.; Abrescia, P.; de Santis, A.; Gentile, V.; Porta, R.

    1984-11-01

    Two transglutaminase-mediated modifications of the rat epididymal spermatozoon surface were demonstrated in vitro. Transglutaminase was effective in promoting the binding of spermidine to the sperm. Moreover, the enzyme, by reacting with one of the major proteins secreted by the rat seminal vesicle epithelium, produced a modified form of the protein with a higher molecular weight and the capability of binding to the sperm cells. A specific physiological role for the enzyme, bringing about modifications of the rat sperm surface in the seminal fluid environment, is suggested.

  18. Modification of Student Snacking: Comparison of Behavioral Teaching Methods.

    Science.gov (United States)

    Hovell, Melbourne F.; And Others

    1988-01-01

    This research project tested the effects of two behavior modification programs, one emphasizing self-control and one traditional nutrition education, on the snacking habits of 91 fourth grade students. The project's methodology is discussed. (JL)

  19. Review of surface-modification programs in the DOE-OTM Tribology Program

    Energy Technology Data Exchange (ETDEWEB)

    Fenske, G.R.; Nichols, F.A.

    1991-02-01

    The use of surface-modification treatments is a widely accepted practice to reduce the wear and modify the friction behavior of surface regions while maintaining desirable bulk properties (e.g., strength, hardness, thermal conductivity, etc.) of the underlying substrate. These treatments range from conventional diffusion processes such as carburizing steels for case-hardening gears, to advanced non-equilibrium processes such as ion implantation or ion plating. The objective of this task area is to develop and investigate new or emerging surface-modification processes that show a potential for improving and controlling the tribological behavior of surfaces and thus permit engineers to design components for advanced heat engines based on desired bulk properties and near-surface tribological properties.

  20. Near-surface modifications for improved crack tolerant behavior of high strength alloys: trends and prospects

    International Nuclear Information System (INIS)

    Hettche, L.R.; Rath, B.B.

    1982-01-01

    The purpose of this chapter is to examine the potential of surface modifications in improving the crack tolerant behavior of high strength alloys. Provides a critique of two of the most promising and versatile techniques: ion implantation and laser beam surface processing. Discusses crack tolerant properties; engineering characterization; publication trends and Department of Defense interests; and emergent surface modification techniques. Finds that the efficiency with which high strength alloys can be incorporated into a structure or component is dependent on the following crack tolerant properties: fracture toughness, fatigue resistance, sustained loading cracking resistance, fretting fatigue resistance, and hydrogen embrittlement resistance. Concludes that ion implantation and laser surface processing coupled with other advanced metallurgical procedures and fracture mechanic analyses provide the means to optimize both the bulk and surface controlled crack tolerant properties

  1. The Quest for Nonthrombotic Surface Modifications to Achieve Hemocompatibility of Implantable Devices.

    Science.gov (United States)

    Tchouta, Lise Nadine; Bonde, Pramod Narayan

    2015-01-01

    The use of blood-contacting implantable devices is limited by surface-induced thrombosis, which has led to the development of thromboresistant surfaces. Multidisciplinary efforts have promoted the development of surface modifications to minimize thrombosis by targeting surface-induced coagulation. To this date, no material has been identified that remains irrevocably hemocompatible with time but many options are now available with their own limitations. Essential to this review is the understanding of some of the challenges in this field and newer opportunities for hemocompatibility research. This report will also briefly review many of the achievements in the development of hemocompatible biomaterial coating, including surface modifications against protein adsorption and platelet adhesion, biomimetism, and endothelialization.

  2. Effects of Surface Modification of MWCNT on the Mechanical and Electrical Properties of Fluoro Elastomer/MWCNT Nanocomposites

    Directory of Open Access Journals (Sweden)

    Tao Xu

    2012-01-01

    Full Text Available Surface modification is a good way to improve the surface activity and interfacial strength of multiwalled carbon nanotubes (MWCNTs when used as fillers in the polymer composites. Among the reported methods for nanotube modification, mixed acid oxidation and plasma treatment is often used by introducing polar groups to the sidewall of MWCNT successfully. The purpose of this study is to evaluate the effect of different surface modification of MWCNT on the mechanical property and electrical conductivity of Fluoro-elastomer (FE/MWCNT nanocomposites. MWCNTs were surface modified by mixed oxidation and CF4 plasma treatment and then used to reinforce the fluoro elastomer (FE, a copolymer of trifluorochloroethylene and polyvinylidene fluoride. FE/MWCNT composite films were prepared from mixture solutions of ethylacetate and butylacetate, using untreated CNTs (UCNTs, acid-modified CNTs (ACNTs, and CF4 plasma-modified CNT (FCNTs. In each case, MWCNT content was 0.01 wt%, 0.05 wt%, 0.1 wt%, and 0.2 wt% with respect to the polymer. Morphology and mechanical properties were characterized by using scanning electron microscopy (SEM, Raman spectroscopy, as well as dynamic mechanical tests. The SEM results indicated that dispersion of ACNTs and especially FCNTs in FE was better than that of UCNTs. DMA indicated mechanical properties of FCNT composites were improved over ACNT and UCNT filled FE. The resulting electrical properties of the composites ranged from dielectric behavior to bulk conductivities of 10-2 Sm-1 and were found to depend strongly on the surface modification methods of MWCNTs.

  3. Effect of Surface Modification and Macrophage Phenotype on Particle Internalization

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Daniel [Iowa State University; Phan, Ngoc [Iowa State University; Isely, Christopher [Iowa State University; Bruene, Lucas [Iowa State University; Bratlie, Kaitlin M [Ames Laboratory

    2014-11-10

    Material properties play a key role in the cellular internalization of polymeric particles. In the present study, we have investigated the effects of material characteristics such as water contact angle, zeta potential, melting temperature, and alternative activation of complement on particle internalization for pro-inflammatory, pro-angiogenic, and naïve macrophages by using biopolymers (~600 nm), functionalized with 13 different molecules. Understanding how material parameters influence particle internalization for different macrophage phenotypes is important for targeted delivery to specific cell populations. Here, we demonstrate that material parameters affect the alternative pathway of complement activation as well as particle internalization for different macrophage phenotypes. Here, we show that the quantitative structure–activity relationship method (QSAR) previously used to predict physiochemical properties of materials can be applied to targeting different macrophage phenotypes. These findings demonstrated that targeted drug delivery to macrophages could be achieved by exploiting material parameters.

  4. Modification of polymer surfaces to enhance enzyme activity and stability

    DEFF Research Database (Denmark)

    Hoffmann, Christian

    Enzyme immobilization is an important concept for the development of improved biocatalytic processes, primarily through facilitated separation procedures. However, enzyme immobilization usually comes at a price of reduced biocatalytic activity. For this reason, different immobilization methods have...... already been developed, combining the same goal to improve enzyme activity, stability and selectivity. Polymer materials have shown, due to their easy processibility and versatile properties, high potential as enzyme support. However, in order to achieve improved enzyme performance, the combination...... of different factors, such as the nature of the enzyme, the properties of the support, the type of immobilization and the interaction between enzyme and support, has to be taken into consideration. In this thesis, these factors are pursued and addressed by exploiting various types of polymers with focus...

  5. Flotation separation of polyvinyl chloride and polyethylene terephthalate plastics combined with surface modification for recycling.

    Science.gov (United States)

    Wang, Chongqing; Wang, Hui; Fu, Jiangang; Zhang, Lingling; Luo, Chengcheng; Liu, Younian

    2015-11-01

    Surface modification with potassium permanganate (KMnO4) solution was developed for separation of polyvinyl chloride (PVC) and polyethylene terephthalate (PET) waste plastics. The floatability of PVC decreases with increasing of KMnO4 concentration, treatment time, temperature and stirring rate, while that of PET is unaffected. Fourier transform infrared (FT-IR) analysis confirms that mechanism of surface modification may be due to oxidization reactions occurred on PVC surface. The optimum conditions are KMnO4 concentration 1.25 mM/L, treatment time 50 min, temperature 60°C, stirring rate 300 r/min, frother concentration 17.5 g/L and flotation time 1 min. PVC and PET with different particle sizes were separated efficiently through two-stage flotation. Additionally, after ultrasonic assisted surface modification, separation of PVC and PET with different mass ratios was obtained efficiently through one-stage flotation. The purity and the recovery of the obtained products after flotation separation are up to 99.30% and 99.73%, respectively. A flotation process was designed for flotation separation of PVC and PET plastics combined with surface modification. This study provides technical insights into physical separation of plastic wastes for recycling industry. Copyright © 2015 Elsevier Ltd. All rights reserved.

  6. PES Surface Modification Using Green Chemistry: New Generation of Antifouling Membranes

    Directory of Open Access Journals (Sweden)

    Norhan Nady

    2016-04-01

    Full Text Available A major limitation in using membrane-based separation processes is the loss of performance due to membrane fouling. This drawback can be addressed thanks to surface modification treatments. A new and promising surface modification using green chemistry has been recently investigated. This modification is carried out at room temperature and in aqueous medium using green catalyst (enzyme and nontoxic modifier, which can be safely labelled “green surface modification”. This modification can be considered as a nucleus of new generation of antifouling membranes and surfaces. In the current research, ferulic acid modifier and laccase bio-catalyst were used to make poly(ethersulfone (PES membrane less vulnerable to protein adsorption. The blank and modified PES membranes are evaluated based on e.g., their flux and protein repellence. Both the blank and the modified PES membranes (or laminated PES on silicon dioxide surface are characterized using many techniques e.g., SEM, EDX, XPS and SPM, etc. The pure water flux of the most modified membranes was reduced by 10% on average relative to the blank membrane, and around a 94% reduction in protein adsorption was determined. In the conclusions section, a comparison between three modifiers—ferulic acid, and two other previously used modifiers (4-hydroxybenzoic acid and gallic acid—is presented.

  7. Surface decontamination compositions and methods

    Science.gov (United States)

    Wright,; Karen, E [Idaho Falls, ID; Cooper, David C [Idaho Falls, ID; Peterman, Dean R [Idaho Falls, ID; Demmer, Ricky L [Idaho Falls, ID; Tripp, Julia L [Pocatello, ID; Hull, Laurence C [Idaho Falls, ID

    2011-03-29

    Clay-based compositions capable of absorbing contaminants from surfaces or objects having surface faces may be applied to a surface and later removed, the removed clay-based compositions absorbing at least a portion of the contaminant from the surface or object to which it was applied.

  8. Copper circuit patterning on polymer using selective surface modification and electroless plating

    Energy Technology Data Exchange (ETDEWEB)

    Park, Sang Jin [Department of Materials Science and Engineering, Chungnam National University, Daejeon 305-764 (Korea, Republic of); Ko, Tae-Jun [Institute for Multidisciplinary Convergence of Materials, Korea Institute of Science and Technology, Seoul 130-650 (Korea, Republic of); Department of Materials Science and Engineering, Seoul National University, Seoul 151-742 (Korea, Republic of); Yoon, Juil [Department of Mechanical Systems Engineering, Hansung University, Seoul 136-792 (Korea, Republic of); Moon, Myoung-Woon [Institute for Multidisciplinary Convergence of Materials, Korea Institute of Science and Technology, Seoul 130-650 (Korea, Republic of); Oh, Kyu Hwan [Department of Materials Science and Engineering, Seoul National University, Seoul 151-742 (Korea, Republic of); Han, Jun Hyun, E-mail: jhhan@cnu.ac.kr [Department of Materials Science and Engineering, Chungnam National University, Daejeon 305-764 (Korea, Republic of)

    2017-02-28

    Highlights: • A new simple two step method for the pattering of Cu circuits on PET substrate was proposed. • The simple patterning of the high adhesive Cu circuits was achieved by plasma treatment using a patterned mask coated with a catalyst material. • The high adhesive strength of Cu circuits was due to the nanostructure formed by oxygen plasma treatment. - Abstract: We have examined a potential new and simple method for patterning a copper circuit on PET substrate by copper electroless plating, without the pretreatment steps (i.e., sensitization and activation) for electroless plating as well as the etching processes of conventional circuit patterning. A patterned mask coated with a catalyst material, Ag, for the reduction of Cu ions, is placed on a PET substrate. Subsequent oxygen plasma treatment of the PET substrate covered with the mask promotes the selective generation of anisotropic pillar- or hair-like nanostructures coated with co-deposited nanoparticles of the catalyst material on PET. After oxygen plasma treatment, a Cu circuit is well formed just by dipping the plasma-treated PET into a Cu electroless plating solution. By increasing the oxygen gas pressure in the chamber, the height of the nanostructures increases and the Ag catalyst particles are coated on not only the top but also the side surfaces of the nanostructures. Strong mechanical interlocking between the Cu circuit and PET substrate is produced by the large surface area of the nanostructures, and enhances peel strength. Results indicate this new simple two step (plasma surface modification and pretreatment-free electroless plating) method can be used to produce a flexible Cu circuit with good adhesion.

  9. Surface modification of acetaminophen particles by atomic layer deposition.

    Science.gov (United States)

    Kääriäinen, Tommi O; Kemell, Marianna; Vehkamäki, Marko; Kääriäinen, Marja-Leena; Correia, Alexandra; Santos, Hélder A; Bimbo, Luis M; Hirvonen, Jouni; Hoppu, Pekka; George, Steven M; Cameron, David C; Ritala, Mikko; Leskelä, Markku

    2017-06-15

    Active pharmaceutical ingredients (APIs) are predominantly organic solid powders. Due to their bulk properties many APIs require processing to improve pharmaceutical formulation and manufacturing in the preparation for various drug dosage forms. Improved powder flow and protection of the APIs are often anticipated characteristics in pharmaceutical manufacturing. In this work, we have modified acetaminophen particles with atomic layer deposition (ALD) by conformal nanometer scale coatings in a one-step coating process. According to the results, ALD, utilizing common chemistries for Al 2 O 3 , TiO 2 and ZnO, is shown to be a promising coating method for solid pharmaceutical powders. Acetaminophen does not undergo degradation during the ALD coating process and maintains its stable polymorphic structure. Acetaminophen with nanometer scale ALD coatings shows slowed drug release. ALD TiO 2 coated acetaminophen particles show cytocompatibility whereas those coated with thicker ZnO coatings exhibit the most cytotoxicity among the ALD materials under study when assessed in vitro by their effect on intestinal Caco-2 cells. Copyright © 2017 Elsevier B.V. All rights reserved.

  10. Bentonite modification with pillarization method using metal stannum

    Science.gov (United States)

    Widjaya, Robert R.; Juwono, Ariadne L.; Rinaldi, Nino

    2017-11-01

    Clay minerals have received considerable attention in the last years because of their environmental compatibility, low cost, high selectivity, and operational simplicity. Although clays are very useful for many application in the field of catalysis, they have main disadvantage: their lack of pore volume and spesific surface area. Porosity and stability of these materials are improved by pillaring the clay layers with SnCl4, which leads to materials known as pillared clays (PILC). This research aims were to characterize the Bentonite and Sn-Bentonite as catalysts for cracking and oligomerization. The Sn-Bentonite was prepared by pillarization method with a variation in metal ratio of 5 mmol dan 10 mmol.gr-1 of bentonit. The catalyst characterized by X-ray Diffraction, X-ray Fluorescence, Fourier Transform Infra Red, Brunauer Emmett Teller, Thermogravimetric Analysis. The results showed that the Sn-Bentonite catalyst had large basal spacing and good porous structure, and the specific surface areas increased. XRF detected the Sn in the Bentonite and TGA results showed the ability Sn-Bentonite in receiving heat. FTIR test showed two type of acidity, broansted and lewis acid. The characterized results indicated that Sn-Bentonite with metal ratio 5 mmol.gr-1 better than Sn-Bentonite with metal ratio 10 mmol.gr-1, in which there was a significant increase the basal spacings, specific surface area, and pore volume. The TGA results for Sn-Bentonite appeared to be more thermally stable than Bentonite.

  11. Facile surface modification of silicone rubber with zwitterionic polymers for improving blood compatibility

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Pingsheng [School of Chemistry and Chemical Engineering, Nanjing University, Nanjing 210093 (China); Chen, Qiang, E-mail: chem100@nju.edu.cn [School of Chemistry and Chemical Engineering, Nanjing University, Nanjing 210093 (China); High Technology Research Institute of Nanjing University, Changzhou 213164 (China); Yuan, Bo; Chen, Mengzhou; Wu, Shishan; Lin, Sicong [School of Chemistry and Chemical Engineering, Nanjing University, Nanjing 210093 (China); Shen, Jian, E-mail: shenj1957@yahoo.com.cn [School of Chemistry and Chemical Engineering, Nanjing University, Nanjing 210093 (China)

    2013-10-15

    A facile approach to modify silicone rubber (SR) membrane for improving the blood compatibility was investigated. The hydrophobic SR surface was firstly activated by air plasma, after which an initiator was immobilized on the activated surface for atom transfer radical polymerization (ATRP). Three zwitterionic polymers were then grafted from SR membrane via surface-initiated atom transfer radical polymerization (SI-ATRP). The surface composition, wettability, and morphology of the membranes before and after modification were characterized by X-ray photoelectron spectroscopy (XPS), static water contact angle (WCA) measurement, and atomic force microscopy (AFM). Results showed that zwitterionic polymers were successfully grafted from SR surfaces, which remarkably improved the wettability of the SR surface. The blood compatibility of the membranes was evaluated by protein adsorption and platelet adhesion tests in vitro. As observed, all the zwitterionic polymer modified surfaces have improved resistance to nonspecific protein adsorption and have excellent resistance to platelet adhesion, showing significantly improved blood compatibility. This work should inspire many creative uses of SR based materials for biomedical applications such as vessel, catheter, and microfluidics. Highlights: • Facile surface modification of silicone rubber with functional brushes • Modified SR surfaces have improved resistance to nonspecific protein adsorption. • Modified SR surfaces have excellent resistance to platelet adhesion. • Zwitteironic surface significant improvement in blood compatibility • Could inspire many creative uses of SR based materials for biomedical.

  12. PTFE-nanocomposites structure and wear-resistance changing in various methods of structural modification

    Science.gov (United States)

    Mashkov, Yu K.; Ruban, A. S.; Rogachev, E. A.; Chemisenko, O. V.

    2018-01-01

    Conditions of polymer materials usage containing nanoelements as modifiers significantly affect the requirements for their physic-mechanical and tribological properties. However, the mechanisms of nanoparticles effect to the polymers tribotechnical properties have not been studied enough. The article aim is to analyze the results of studying polytetrafluoroethylene modified with cryptocrystalline graphite and silicon dioxide and to determine the effectiveness of the modification methods used and methods for further improving filled PTFE mechanical and tribotechnical properties. The effect of modifiers to PCM supramolecular structure was analyzed with SEM methods. The results of modifying the PCM samples surface by depositing a copper film with ion-vacuum deposition methods and changing the structural-phase composition and tribological characteristics are considered. The findings make possible to characterize the physicochemical processes under frictional interaction in metal polymer tribosystems.

  13. Modification of Semiconductor Surfaces through Si-N Linkages by Wet-Chemistry Approaches and Modular Functionalization of Zinc Oxide Surfaces for Chemical Protection of Material Morphology

    Science.gov (United States)

    Gao, Fei

    Semiconductor substrates are widely used in many applications. Multiple practical uses involving these materials require the ability to tune their physical and chemical properties to adjust those to a specific application. In recent years, surface and interface reactions have affected dramatically device fabrication and material design. Novel surface functionalization techniques with diverse chemical approaches make the desired physical, thermal, electrical, and mechanical properties attainable. Meanwhile, the modified surface can serve as one of the most important key steps for further assembly process in order to make novel devices and materials. In the following chapters, novel chemical approaches to the functionalization of silicon and zinc oxide substrates will be reviewed and discussed. The specific functionalities including amines, azides, and alkynes on surfaces of different materials will be applied to address subsequent attachment of large molecules and assembly processes. This research is aimed to develop new strategies for manipulating the surface properties of semiconductor materials in a controlled way. The findings of these investigations will be relevant for future applications in molecular and nanoelectronics, sensing, and solar energy conversion. The ultimate goals of the projects are: 1) Preparation of an oxygen-and carbon-free silicon surface based exclusively on Si-N linkages for further modification protocols.. This project involves designing the surface reaction of hydrazine on chlorine-terminated silicon surface, introduction of additional functional group through dehydrohalogenation condensation reaction and direct covalent attachment of C60. 2) Demonstrating alternative method to anchor carbon nanotubes to solid substrates directly through the carbon cage.. This project targets surface modification of silicon and gold substrates with amine-terminated organic monolayers and the covalent attachment of nonfunctionalized and carboxylic acid

  14. Surface modifications and Nano-composite coatings to improve the bonding strength of titanium-porcelain

    Energy Technology Data Exchange (ETDEWEB)

    Guo, Litong, E-mail: guolitong810104@163.com [China University of Mining and Technology, Xuzhou 221116 (China); ustralian Institute for Bioengineering and Nanotechnology, The University of Queensland, Brisbane, QLD 4072 (Australia); Chen, Xiaoyuan; Liu, Xuemei; Feng, Wei [China University of Mining and Technology, Xuzhou 221116 (China); Li, Baoe [School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300130 (China); Lin, Cheng; Tao, Xueyu; Qiang, Yinghuai [China University of Mining and Technology, Xuzhou 221116 (China)

    2016-04-01

    Surface modifications of Ti and nano-composite coatings were employed to simultaneously improve the surface roughness, corrosion resistance and chemical bonding between porclain-Ti. The specimens were studied by field-emission scanning electron microscopy, surface roughness, differential scanning calorimetry, Fourier transform infrared spectroscopy, corrosion resistance and bonding strength tests. The SEM results showed that hybrid structures with micro-stripes, nano-pores and nano-protuberances were prepared by surface modification of Ti, which significantly enhanced the surface roughness and corrosion resistance of Ti. Porous nano-composite coatings were synthesized on Ti anodized with pre-treatment in 40% HF acid. TiO{sub 2} nanoparticles were added into the hybrid coating to increase the solid phase content of the sols and avoid the formation of microcracks. With the TiO{sub 2} content increasing from 45 wt% to 60 wt%, the quantities of the microcracks on the coating surface gradually decreased. The optimal TiO{sub 2} content for the nanocomposite coatings is 60 wt% in this research. Compared to the uncoated group, the bonding strength of the coated groups showed a bonding strength improvement of 23.96%. The cytotoxicity of the 4# coating group was ranked as zero, which corresponds to non-cytotoxicity. - Highlights: • Surface roughness of Ti was increased by surface modification of Ti. • Corrosion resistance was enhanced by surface modification of Ti. • Porous nano-composite coatings were synthesized on Ti by sol–gel process. • TiO{sub 2} nanoparticles were added into the coating to avoid formation of cracks. • The nano-composite coatings increased the bonding strength of about 24%.

  15. Surface modification of Y3Al5O12:Ce3+ phosphor by hydrofluoric acid wet etching

    International Nuclear Information System (INIS)

    He, Zhijiang; Cheng, Weihai; Li, Zebin; Liu, Ying; Ou, Qiongrong; Liang, Rongqing

    2013-01-01

    The surface of Y 3 Al 5 O 12 :Ce 3+ phosphor prepared by solid-state reaction was modified by hydrofluoric acid wet etching. The SEM pictures show that the edge-angles-rich surface of the phosphor particles becomes smooth and the XRD spectra show that the surface crystallinity is improved after modification for more than 3 h. Consequently, the photoluminescence emission from phosphor particles with smooth surface presents a higher quantum yield (increased by 5.5%) than that without modification, and a lower backscattering light by the smoothed phosphor particles is also found, which suggests better surface characteristics of light absorption, transparency and crystallinity. -- Highlights: ► HF wet etching way is introduced to modify the YAG phosphor surface for the first time. ► The surface with riched edge angles has become smooth. ► The photoluminescence emission intensity is increased by 5.5%. ► The backscattering light intensity is obviously decreased. ► The wet etching method with HF is appropriate for mass process

  16. Adhesive bonding of resin composite to various titanium surfaces using different metal conditioners and a surface modification system

    Directory of Open Access Journals (Sweden)

    Hercules Jorge ALMILHATTI

    2013-12-01

    Full Text Available Objective: This study evaluated the effect of three metal conditioners on the shear bond strength (SBS of a prosthetic composite material to cpTi grade I having three surface treatments. Material and Methods: One hundred sixty eight rivet-shaped specimens (8.0x2.0 mm were cast and subjected to polishing (P or sandblasting with either 50 mm (50SB or 250 mm (250SB Al2O3. The metal conditioners Metal Photo Primer (MPP, Cesead II Opaque Primer (OP, Targis Link (TL, and one surface modification system Siloc (S, were applied to the specimen surfaces, which were covered with four 1-mm thick layers of resin composite. The resin layers were exposed to curing light for 90 s separately. Seven specimens from each experimental group were stored in water at 37ºC for 24 h while the other 7 specimens were subjected to 5,000 thermal cycles consisting of water baths at 4ºC and 60ºC (n=7. All specimens were subjected to SBS test (0.5 mm/min until failure occurred, and further 28 specimens were analyzed using scanning electron microscope (SEM and X-ray energy-dispersive spectroscopy (EDS. Data were analyzed by 3-way ANOVA followed by post-hoc Tukey's test (α=0.05. Results: On 50SB surfaces, OP groups showed higher SBS means than MPP (P<0.05, while no significant difference was found among OP, S, and TL groups. On 250SB surfaces, OP and TL groups exhibited higher SBS than MPP and S (P<0.05. No significant difference in SBS was found between OP and TL groups nor between MPP and S groups. The use of conditioners on 250SB surfaces resulted in higher SBS means than the use of the same products on 50SB surfaces (P<0.05. Conclusion: Sandblasting associated with the use of metal conditioners improves SBS of resin composites to cpTi.

  17. Surface Modification of Nanoclay for the Synthesis of Polycaprolactone (PCL – Clay Nanocomposite

    Directory of Open Access Journals (Sweden)

    Yusoh Kamal

    2018-01-01

    Full Text Available This paper presents a new modification method to modify the surface of nanoclay (Na-MMT to increase its d-spacing using Aminopropylisooctyl Polyhedral Oligomeric Silsesquioxane (AP-POSS and the fabrication of Polycaprolactone (PCL nanocomposite through solution intercalation technique. The structure and morphology of pure nanoclay, modified nanoclay (POSS-MMT and the PCL nanocomposite were characterized by X-ray Diffraction (XRD, Fourier Transform Infrared Spectroscopy (FTIR and Field Emission Scanning Electron Microscopy (FESEM. XRD revealed that the d-spacing of the POSS-MMT is increased by 0.64 nm as compared to pure nanoclay. FTIR and FESEM results also showed that AP-POSS were well dispersed and intercalated throughout the interlayer space of Na-MMT. An exfoliated structure was also observed for PCL/POSS-MMT nanocomposite. Thermal properties of the nanocomposite were investigated using Thermal Gravimetry Analysis (TGA which recorded highest degradation temperature for PCL/POSS-MMT 1% nanocomposite which is 394.1°C at 50% weight loss (T50% but a decrease in degradation temperature when POSS-MMT content is increased and Differential Scanning Calorimetry (DSC analysis which showed highest melting and crystallization temperature for PCL/POSS-MMT 5% nanocomposite which is 56.6°C and 32.7°C respectively whereas a decrease in degree of crystallinity for PCL/POSS-MMT nanocomposite as compared to PCL/Na-MMT nanocomposite. This study affords an efficient modification method to obtain organoclay with larger interlayer d-spacing to enhance the properties of polymer nanocomposite.

  18. Selective cell culture on UV transparent polymer by F2 laser surface modification

    International Nuclear Information System (INIS)

    Hanada, Yasutaka; Sugioka, Koji; Kawano, Hiroyuki; Tsuchimoto, Takayoshi; Miyamoto, Iwao; Miyawaki, Atsushi; Midorikawa, Katsumi

    2009-01-01

    A microchip made of UV transparent polymer (CYTOP) that can perform selective cell culture has been fabricated by F 2 laser surface modification. The refractive index of CYTOP is almost the same as that of culture medium, which is essential for three-dimensional (3D) observation of cells. The F 2 laser modification of CYTOP achieves hydrophilicity only on the laser irradiated area with little deterioration of the optical properties and surface smoothness. After the laser modification, HeLa cells were successfully cultured and strongly adhered only on the modified area of CYTOP. The cells patterned on CYTOP were applied for clear 3D observation using an optical microscope in phase contrast mode.

  19. Uniform surface modification of diatomaceous earth with amorphous manganese oxide and its adsorption characteristics for lead ions

    Science.gov (United States)

    Li, Song; Li, Duanyang; Su, Fei; Ren, Yuping; Qin, Gaowu

    2014-10-01

    A novel method to produce composite sorbent material compromising porous diatomaceous earth (DE) and surface functionalized amorphous MnO2 is reported. Via a simple in situ redox reaction over the carbonized DE powders, a uniform layer of amorphous MnO2 was anchored onto the DE surface. The hybrid adsorbent was characterized by X-ray diffraction, scanning electron microscopy, and infrared spectroscopy. The batch method has been employed to investigate the effects of surface coating on adsorption performance of DE. According to the equilibrium studies, the adsorption capacity of DE for adsorbing lead ions after MnO2 modification increased more than six times. And the adsorption of Pb2+ on the MnO2 surface is based on ion-exchange mechanism. The developed strategy presents a novel opportunity to prepare composite adsorbent materials by integrating nanocrystals with porous matrix.

  20. Microwave modification of surface hydroxyl density for g-C3N4 with enhanced photocatalytic activity

    Science.gov (United States)

    An, Na; Zhao, Yang; Mao, Zhiyong; Agrawal, Dinesh Kumar; Wang, Dajian

    2018-03-01

    Microwave modification was performed on graphitic carbon nitride (g-C3N4) photocatalysts to tail the surface hydroxyl content for enhanced photocatalytic activity in this work. The influence of microwave heating on the surface hydroxyl density was investigated by a suite of characterization methods. The microwave treated g-C3N4 (MT-g-C3N4) delivered a higher photocatalytic activity in degradation of Rhodamine B (RhB) under visible light irradiation than pristine g-C3N4 due to its improved separation efficiency of photogenerated charge carries and promoted absorption capacity of RhB reactants on surface, which resulted from the increased surface hydroxyl density induced by microwave treatment. This study provides a simple and convenient method to modify g-C3N4 materials with enhanced photocatalytic activity for the potential application in photocatalytic elimination of environmental pollutants.

  1. Modification of Teflon surface by proton microbeam and nitrogen ion beam

    Science.gov (United States)

    Kitamura (Ogawa), Akane; Satoh, Takahiro; Koka, Masashi; Kamiya, Tomihiro; Kobayashi, Tomohiro

    2013-11-01

    Teflon surfaces were modified using a combination of 3 MeV proton microbeam scanning and subsequent 250 keV N2+ ion beam irradiation. When a Teflon surface is irradiated using only an N2+ ion beam, micro-protrusions are densely formed in the irradiated area. It has been previously confirmed that these protrusions aid the attachment of biological cells, which then spread on the surface. Therefore, modification of the Teflon surface patterning is necessary in order to enhance its functionality as cell culture substrata. In this study, flat areas and depressed structures were created among the dense micro-protrusions by bubbles that were generated inside the sample using proton beam scanning. This modification will contribute to the fabrication of cell culture dishes with the advantages of micro-protrusions.

  2. Modification of surface properties of high and low density polyethylene by Ar plasma discharge

    Czech Academy of Sciences Publication Activity Database

    Švorčík, J.; Kolářová, K.; Slepička, P.; Macková, Anna; Novotná, M.; Hnatowicz, Vladimír

    2006-01-01

    Roč. 91, č. 6 (2006), s. 1219-1225 ISSN 0141-3910 R&D Projects: GA MŠk OC 527.100; GA MŠk 1P05OC014 Institutional research plan: CEZ:AV0Z10480505 Keywords : plasma polymer isation * surface modification Subject RIV: CD - Macromolecular Chemistry Impact factor: 2.174, year: 2006

  3. SURFACE MODIFICATION OF NANOPARTICLES TO OPPOSE UPTAKE BY THE MONONUCLEAR PHAGOCYTE SYSTEM

    NARCIS (Netherlands)

    STORM, G; BELLIOT, SO; DAEMEN, T; LASIC, DD

    1995-01-01

    An overview of recent advances in the surface modification of colloidal particles to oppose uptake by the mononuclear phagocyte system (MPS) is presented. First, we describe the colloidal particles and hydrophilic coating materials investigated, with particular focus on the literature concerning

  4. Low energy ion beam modification of Cu/Ni/Si(100) surface

    Indian Academy of Sciences (India)

    1569–1573. c Indian Academy of Sciences. Low energy ion beam modification of Cu/Ni/Si(100) surface. S K PARIDAa, V R R MEDICHERLAa,∗. , D K MISHRAa, S CHOUDHARYb, V SOLANKIb and. SHIKHA VARMAb. aDepartment of Physics, Institute of Technical Education & Research, Siksha 'O' Anusandhan University,.

  5. Low energy ion beam modification of Cu/Ni/Si(100) surface

    Indian Academy of Sciences (India)

    Abstract. Cu/Ni bilayer has been prepared by thermal evaporation of pure Cu and Ni metals onto Si(100) sur- face in high vacuum; it was sputtered using argon ion beam in ultra-high vacuum. The ion beam-induced surface and interface modification was investigated using X-ray photoelectron spectroscopy and atomic force ...

  6. UV Light Induced Surface Modification of HDPE Films with Bioactive Compounds

    Czech Academy of Sciences Publication Activity Database

    Daniloska, V.; Blazevska-Gilev, J.; Dimova, V.; Fajgar, Radek; Tomovska, R.

    2010-01-01

    Roč. 256, č. 7 (2010), s. 2276-2283 ISSN 0169-4332 Institutional research plan: CEZ:AV0Z40720504 Keywords : surface modification * uv irradiation * benzocaine Subject RIV: CH - Nuclear ; Quantum Chemistry Impact factor: 1.795, year: 2010

  7. Nano-scale surface modification of materials with slow, highly charged ion beams

    International Nuclear Information System (INIS)

    Sakurai, M.; Tona, M.; Takahashi, S.; Watanabe, H.; Nakamura, N.; Yoshiyasu, N.; Yamada, C.; Ohtani, S.; Sakaue, H.A.; Kawase, Y.; Mitsumori, K.; Terui, T.; Mashiko, S.

    2007-01-01

    Some results on surface modification of Si and graphite with highly charged ions (HCIs) are presented. Modified surfaces were observed using scanning tunneling microscopy. Crater-like structure with a diameter in nm region is formed on a Si(1 1 1)-(7 x 7) surface by the incidence of a single HCI. The protrusion structure is formed on a highly oriented pyrolytic graphite surface on the other hand, and the structure becomes an active site for molecular adsorption. A new, intense HCI source and an experimental apparatus are under development in order to process and observe aligned nanostructures created by the impact of collimated HCI beam

  8. Laser surface modification of polyethersulfone films: effect of laser wavelength on biocompatibility

    International Nuclear Information System (INIS)

    Pazokian, H; Jelvani, S; Mollabashi, M; Barzin, J

    2013-01-01

    In this paper laser ablation of polyethersulfone (PES) films regarding to the change in biocompatibility of the surface is investigated at 3 different wavelengths of 193nm (ArF), 248 nm (KrF) and 308 nm (XeCl). The optimum laser fluence and number of pulses for the improvement of the surface biocompatibility is found by examination of the surface behavior in contact with platelets and fibroblasts cells at 3 wavelengths. These biological modifications are explained by alteration of the surface morphology and chemistry following irradiation. The results show that the KrF laser is the best choice for treatment of PES in biological applications.

  9. Surface Modification of Photoresist SU-8 for Low Autofluorescence and Bioanalytical Applications

    DEFF Research Database (Denmark)

    Cao, Cuong; Birtwell, Sam W.; Høgberg, Jonas

    2011-01-01

    This paper reports a surface modification of epoxy-based negative photoresist SU-8 for reducing its autofluorescence while enhancing its biofunctionality. By covalently depositing a thin layer of 20 nm Au nanoparticles (AuNPs) onto the SU-8 surface, we found that the AuNPs-coated SU-8 surface...... is much less fluorescent than the untreated SU-8. Moreover, DNA probes can easily be immobilized on the Au surface and are thermally stable over a wide range of temperature. These improvements will benefit bioanalytical applications such as DNA hybridization and solid-phase PCR (SP-PCR)....

  10. Methodology of licensing for field applications of Weld Inlay and Ultrasonic Nanocrystal Surface Modification

    International Nuclear Information System (INIS)

    Cho, Hong Seok; Jung, Kwang Woon; Park, Ik Keun; Pyun, Young Sik

    2015-01-01

    There are many attempts to relieve or change high tensile residual stress to compressive residual stress for a mitigation of PWSCC. LSP(Laser Shot Peening) and WJP(Water Jet Peening) have been applied in several NPPs of Japan and technical and topical reports under Materials Reliability Program of EPRI(Electric Power Research Institute ) USA have been developed. Weld Inlay technology and UNSM(Ultrasonic Nanocrystal Surface Modification) technology using ultrasonic vibration energy as the method for a mitigation of tensile residual stress generated after Weld Inlay have been developing in Korea. So in this study, the methodology of licensing for field application of these technologies is suggested. The results of residual stress measured before and after UNSM for Weld Inlay specimens using UNSM equipment of domestic source technology holdings to obtain an equivalent effect, which has the simplification of equipment and the flexibility of field application in comparison with LSP and WJP, indicated to obtain a mitigation effect of residual stress until 0.5 mm of surface depth. In order to accomplish field application of Weld Inlay that the Code Case was already developed, the approval of a regulation agency through the preparation of TR or RR based on ASME Code Case N-766, N-803 is necessary

  11. Methodology of licensing for field applications of Weld Inlay and Ultrasonic Nanocrystal Surface Modification

    Energy Technology Data Exchange (ETDEWEB)

    Cho, Hong Seok; Jung, Kwang Woon [KEPCO KPS, Naju (Korea, Republic of); Park, Ik Keun [Seoul National Univ, Seoul (Korea, Republic of); Pyun, Young Sik [Sun Moon University, Asan (Korea, Republic of)

    2015-10-15

    There are many attempts to relieve or change high tensile residual stress to compressive residual stress for a mitigation of PWSCC. LSP(Laser Shot Peening) and WJP(Water Jet Peening) have been applied in several NPPs of Japan and technical and topical reports under Materials Reliability Program of EPRI(Electric Power Research Institute ) USA have been developed. Weld Inlay technology and UNSM(Ultrasonic Nanocrystal Surface Modification) technology using ultrasonic vibration energy as the method for a mitigation of tensile residual stress generated after Weld Inlay have been developing in Korea. So in this study, the methodology of licensing for field application of these technologies is suggested. The results of residual stress measured before and after UNSM for Weld Inlay specimens using UNSM equipment of domestic source technology holdings to obtain an equivalent effect, which has the simplification of equipment and the flexibility of field application in comparison with LSP and WJP, indicated to obtain a mitigation effect of residual stress until 0.5 mm of surface depth. In order to accomplish field application of Weld Inlay that the Code Case was already developed, the approval of a regulation agency through the preparation of TR or RR based on ASME Code Case N-766, N-803 is necessary.

  12. Tuning colloidal quantum dot band edge positions through solution-phase surface chemistry modification

    Science.gov (United States)

    Kroupa, Daniel M.; Vörös, Márton; Brawand, Nicholas P.; McNichols, Brett W.; Miller, Elisa M.; Gu, Jing; Nozik, Arthur J.; Sellinger, Alan; Galli, Giulia; Beard, Matthew C.

    2017-05-01

    Band edge positions of semiconductors determine their functionality in many optoelectronic applications such as photovoltaics, photoelectrochemical cells and light emitting diodes. Here we show that band edge positions of lead sulfide (PbS) colloidal semiconductor nanocrystals, specifically quantum dots (QDs), can be tuned over 2.0 eV through surface chemistry modification. We achieved this remarkable control through the development of simple, robust and scalable solution-phase ligand exchange methods, which completely replace native ligands with functionalized cinnamate ligands, allowing for well-defined, highly tunable chemical systems. By combining experiments and ab initio simulations, we establish clear relationships between QD surface chemistry and the band edge positions of ligand/QD hybrid systems. We find that in addition to ligand dipole, inter-QD ligand shell inter-digitization contributes to the band edge shifts. We expect that our established relationships and principles can help guide future optimization of functional organic/inorganic hybrid nanostructures for diverse optoelectronic applications.

  13. A Co-Precursor Approach Coupled with a Supercritical Modification Method for Constructing Highly Transparent and Superhydrophobic Polymethylsilsesquioxane Aerogels.

    Science.gov (United States)

    Lei, Chaoshuai; Li, Junning; Sun, Chencheng; Yang, Hailong; Xia, Tao; Hu, Zijun; Zhang, Yue

    2018-03-30

    Polymethylsilsesquioxane (PMSQ) aerogels obtained from methyltrimethoxysilane (MTMS) are well-known high-performance porous materials. Highly transparent and hydrophobic PMSQ aerogel would play an important role in transparent vacuum insulation panels. Herein, the co-precursor approach and supercritical modification method were developed to prepare the PMSQ aerogels with high transparency and superhydrophobicity. Firstly, benefiting from the introduction of tetramethoxysilane (TMOS) in the precursor, the pore structure became more uniform and the particle size was decreased. As the TMOS content increased, the light transmittance increased gradually from 54.0% to 81.2%, whereas the contact angle of water droplet decreased from 141° to 99.9°, ascribed to the increase of hydroxyl groups on the skeleton surface. Hence, the supercritical modification method utilizing hexamethyldisilazane was also introduced to enhance the hydrophobic methyl groups on the aerogel's surface. As a result, the obtained aerogels revealed superhydrophobicity with a contact angle of 155°. Meanwhile, the developed surface modification method did not lead to any significant changes in the pore structure resulting in the superhydrophobic aerogel with a high transparency of 77.2%. The proposed co-precursor approach and supercritical modification method provide a new horizon in the fabrication of highly transparent and superhydrophobic PMSQ aerogels.

  14. Chemical surface reactions by click chemistry: coumarin dye modification of 11-bromoundecyltrichlorosilane monolayers

    International Nuclear Information System (INIS)

    Haensch, Claudia; Hoeppener, Stephanie; Schubert, Ulrich S

    2008-01-01

    The functionalization of surfaces and the ability to tailor their properties with desired physico-chemical functions is an important field of research with a broad spectrum of applications. These applications range from the modification of wetting properties, over the alteration of optical properties, to the fabrication of molecular electronic devices. In each of these fields, it is of specific importance to be able to control the quality of the layers with high precision. The present study demonstrates an approach that utilizes the 1,3-dipolar cycloaddition of terminal acetylenes to prepare triazole-terminated monolayers on different substrates. The characterization of the precursor monolayers, the optimization of the chemical surface reactions as well as the clicking of a fluorescent dye molecule on such azide-terminated monolayers was carried out. A coumarin 343 derivative was utilized to discuss the aspects of the functionalization approach. Based on this approach, a number of potential surface reactions, facilitated via the acetylene-substituted functional molecules, for a broad range of applications is at hand, thus leading to numerous possibilities where surface modifications are concerned. These modifications can be applied on non-structured surfaces of silicon or glass or can be used on structured surfaces. Various possibilities are discussed

  15. Effect of Hybrid Surface Modifications on Tensile Properties of Polyacrylonitrile- and Pitch-Based Carbon Fibers

    Science.gov (United States)

    Naito, Kimiyoshi

    2016-05-01

    Recent interest has emerged in techniques that modify the surfaces of carbon fibers, such as carbon nanotube (CNT) grafting or polymer coating. Hybridization of these surface modifications has the potential to generate highly tunable, high-performance materials. In this study, the mechanical properties of surface-modified polyacrylonitrile (PAN)-based and pitch-based carbon fibers were investigated. Single-filament tensile tests were performed for fibers modified by CNT grafting, dipped polyimide coating, high-temperature vapor deposition polymerized polyimide coating, grafting-dipping hybridization, and grafting-vapor deposition hybridization. The Weibull statistical distributions of the tensile strengths of the surface-modified PAN- and pitch-based carbon fibers were examined. All surface modifications, especially hybrid modifications, improved the tensile strengths and Weibull moduli of the carbon fibers. The results exhibited a linear relationship between the Weibull modulus and average tensile strength on a log-log scale for all surface-modified PAN- and pitch-based carbon fibers.

  16. Surface modification of malachite with ethanediamine and its effect on sulfidization flotation

    Science.gov (United States)

    Feng, Qicheng; Zhao, Wenjuan; Wen, Shuming

    2018-04-01

    Ethanediamine was used to modify the mineral surface of malachite to improve its sulfidization and flotation behavior. The activation mechanism was investigated by adsorption experiments, X-ray photoelectron spectroscopy (XPS) analysis, and zeta potential measurements. Microflotation experiments showed that the flotation recovery of malachite was enhanced after the pretreatment of the mineral particles with ethanediamine prior to the addition of Na2S. Adsorption tests revealed that numerous sulfide ion species in the pulp solution were transferred onto the mineral surface through the formation of more copper sulfide species. This finding was confirmed by the results of the XPS measurements. Ethanediamine modification not only increased the contents of copper sulfide species on the malachite surface but also enhanced the reactivity of the sulfidization products. During sulfidization, Cu(II) species on the mineral surface were reduced into Cu(I) species, and the percentages of S22- and Sn2- relative to the total S increased after modification, resulting in increased surface hydrophobicity. The results of zeta potential measurements showed that the ethanediamine-modified mineral surface adsorbed with more sulfide ion species was advantageous to the attachment of xanthate species, thereby improving malachite floatability. The proposed ethanediamine modification followed by sulfidization xanthate flotation exhibits potential for industrial application.

  17. Topological surface states of Bi{sub 2}Te{sub 2}Se are robust against surface chemical modification

    Energy Technology Data Exchange (ETDEWEB)

    Thomas, Conor R.; Sahasrabudhe, Girija; Kushwaha, Satya Kumar; Cava, Robert J.; Schwartz, Jeffrey [Department of Chemistry, Princeton University, Princeton, NJ (United States); Xiong, Jun [Department of Physics, Princeton University, Princeton, NJ (United States)

    2014-12-01

    The robustness of the Dirac-like electronic states on the surfaces of topological insulators (TIs) during materials process-ing is a prerequisite for their eventual device application. Here, the (001) cleavage surfaces of crystals of the topological insulator Bi{sub 2}Te{sub 2}Se (BTS) were subjected to several surface chemical modification procedures that are common for electronic materials. Through measurement of Shubnikov-de Hass (SdH) oscillations, which are the most sensitive measure of their quality, the surface states of the treated surfaces were compared to those of pristine BTS that had been exposed to ambient conditions. In each case - surface oxidation, deposition of thin layers of Ti or Zr oxides, or chemical modification of the surface oxides - the robustness of the topological surface electronic states was demonstrated by noting only very small changes in the frequency and amplitude of the SdH oscillations. (copyright 2014 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  18. Carbon nanotubes modification with polyaniline: Revealing mechanism by mathematical modeling method

    Science.gov (United States)

    Rukhov, Artem; Dyachkova, Tatyana; Anosova, Irina; Tugolukov, Evgeniy; Burakova, Elena; Galunin, Evgeniy

    2017-11-01

    The process of carboxylated carbon nanotubes (CNT) modification with polyaniline (PANI) has been studied by molecular dynamics methods. It is shown that the formation of dimers and phenazine oligomeric products takes place on the surface of CNT, after which desorption takes place, and the growth of macromolecular PANI chains occurs in the reaction mass bulk. Carboxylate groups have an orienting effect on the arrangement of PANI molecules in the formation of the modifying layer, therefore, the properties of synthesized composites are affected not only by the presence of functional groups on the CNT surface, but also by the degree of functionalization. An approach is proposed to determine the degree of preliminary functionalization of CNT by carboxylate groups, which ensures the formation of the uniform PANI coating and the highest electrical capacity and conductivity of the composites.

  19. A Review of Additive Mixed-Electric Discharge Machining: Current Status and Future Perspectives for Surface Modification of Biomedical Implants

    Directory of Open Access Journals (Sweden)

    Abdul’Azeez Abdu Aliyu

    2017-01-01

    Full Text Available Surface treatment remained a key solution to numerous problems of synthetic hard tissues. The basic methods of implant surface modification include various physical and chemical deposition techniques. However, most of these techniques have several drawbacks such as excessive cost and surface cracks and require very high sintering temperature. Additive mixed-electric discharge machining (AM-EDM is an emerging technology which simultaneously acts as a machining and surface modification technique. Aside from the mere molds, dies, and tool fabrication, AM-EDM is materializing to finishing of automobiles and aerospace, nuclear, and biomedical components, through the concept of material migrations. The mechanism of material transfer by AM-EDM resembles electrophoretic deposition, whereby the additives in the AM-EDM dielectric fluids are melted and migrate to the machined surface, forming a mirror-like finishing characterized by extremely hard, nanostructured, and nanoporous layers. These layers promote the bone in-growth and strengthen the cell adhesion. Implant shaping and surface treatment through AM-EDM are becoming a key research focus in recent years. This paper reports and summarizes the current advancement of AM-EDM as a potential tool for orthopedic and dental implant fabrication. Towards the end of this paper, the current challenges and future research trends are highlighted.

  20. Surface Modification for Improved Design and Functionality of Nanostructured Materials and Devices

    Science.gov (United States)

    Keiper, Timothy Keiper

    through catalyst-free physical vapor deposition are implemented in the field-effect transistor structure. We have discovered that conductivity is absent in as-grown devices. However, utilizing a process for thermal treatment in vacuum and oxygen environments is found to be instrumental in fabricating field-effect transistors with significant conductivity, up to five orders of magnitude above the as-grown devices, for field-effect transistor application. Further investigation by photoluminescence coupled with the annealing parameters reveals that the likely cause of conductance comes from the reduction of surface defect states in the material. Importantly, the annealed material maintains its response to an applied gate potential showing orders of magnitude switching from the 'off' to the 'on' state. In order to show the practical relevance of our improvements on the SnO2 material, we show our results for implementing the annealed material in biomolecular sensing experiments to detect the presence of streptavidin and Hepatitis C virus. Surface modification was carried out on oxide-free gallium arsenide (in some cases doped with manganese or zinc) through self-assembly of thiol molecules. First, we investigate the ability to pattern via two complementary micro- and nanopatterning techniques, microcontact printing (muCP) and dip-pen nanolithography (DPN). DPN is a unique lithography tool that allows drawing of arbitrary patterns with a molecular ink on a complementary substrate. It is extremely useful in integration of molecular inks within a pre-defined structure. Here, DPN was used to investigate the diffusion of organic molecules from a point source for both a moving and stationary tip on oxide-free GaAs. The diffusion can be calibrated so that intricate patterns down to tens of nanometers can be arbitrarily drawn on the surface. muCP, a less complicated method for large-scale arrayed patterning, is utilized to investigate the deposition of different thiolated molecular

  1. Modified Palatoplasty Method (Busan Modification) for Incomplete Type Cleft Palate.

    Science.gov (United States)

    Bae, Yong Chan; Lee, Jae Woo; Seo, Hyoung Joon

    2015-06-01

    To achieve ultimate goals of cleft palate repair, levator muscle's appropriate reapproximation is viewed more importantly as of now, rather than simple palatal lengthening. Authors have developed modified version of 2-flap palatoplasty technique for incomplete type cleft palate and conducted follow-up study, including its early complications, speech evaluation, and facial growth measurement. Of the entire patients receiving a surgery from 2002 to 2012, the authors surveyed consecutive 100 cases of nonsyndromic incomplete cleft palate receiving our modified surgeries, and their early postoperative complication occurrence and the progress were monitored. Of them, the authors performed speech evaluation (n = 36) and facial growth measurement (n = 28) for the patients who the authors could follow-up until at least the age of 4.The medical record review has found no single, early postoperative complication requiring immediate treatment. A total of 10 cases showed delayed wound healing, but 7 of them recovered without a special problem and the other 3 showed residual fistula, recording 3% fistula formation rate. Of the 36 pronunciation evaluation cases, average score was 64.2, reaching almost to the full score of 66, but 1 case with the lowest point was found to need a corrective surgery for the clinical velopharyngeal dysfunction. Cephalometric measurement receiving 28 cases showed sella-nasion-A point angle (SNA) of 82.8° ± 3.4°, sella-nasion-B point angle (SNB) of 78.9° ± 3.9°, and a point-nasion-B point angle (ANB) of 3.9° ± 1.9°. In all range of the measurements, no significant statistical difference was found between normal population at that age and the sample group. The authors consecutively performed this modified method (Busan modification) for patients with incomplete cleft palate and consequentially found a lower rate of early postoperative complications. Moreover, relatively excellent long-term results including speech evaluation score and

  2. Surface modification of a proton exchange membrane and hydrogen storage in a metal hydride for fuel cells

    Science.gov (United States)

    Andrews, Lisa

    Interest in fuel cell technology is rising as a result of the need for more affordable and available fuel sources. Proton exchange membrane fuel cells involve the catalysis of a fuel to release protons and electrons. It requires the use of a polymer electrolyte membrane to transfer protons through the cell, while the electrons pass through an external circuit, producing electricity. The surface modification of the polymer, NafionRTM, commonly researched as a proton exchange membrane, may improve efficiency of a fuel cell. Surface modification can change the chemistry of the surface of a polymer while maintaining bulk properties. Plasma modification techniques such as microwave discharge of an argon and oxygen gas mixture as well as vacuum-ultraviolet (VUV) photolysis may cause favorable chemical and physical changes on the surface of Nafion for improved fuel cell function. A possible increase in hydrophilicity as a result of microwave discharge experiments may increase proton conductivity. Grafting of acrylic acid from the surface of modified Nafion may decrease the permeation of methanol in a direct methanol fuel cell, a process which can decrease efficiency. Modification of the surface of Nafion samples were carried out using: 1) An indirect Ar/O2 gas mixture plasma investigating the reaction of oxygen radicals with the surface, 2) A direct Ar/O2 gas mixture plasma investigating the reaction of oxygen radicals and VUV radiation with the surface and, 3) VUV photolysis investigating exclusively the interaction of VUV radiation with the surface and any possible oxidation upon exposure to air. Acrylic acid was grafted from the VUV photolysed Nafion samples. All treated surfaces were analyzed using X-ray photoelectron spectroscopy (XPS). Fourier transform infrared spectroscopy (FTIR) was used to analyze the grafted Nafion samples. Scanning electron microscopy (SEM) and contact angle measurements were used to analyze experiments 2 and 3. Using hydrogen as fuel is a

  3. Surface modification technique of structural ceramics: ion implantation-assisted multi-arc ion plating

    International Nuclear Information System (INIS)

    Peng Zhijian; Miao Hezhuo; Si Wenjie; Qi Longhao; Li Wenzhi

    2003-01-01

    Through reviewing the advantages and disadvantages of the existed surface modification techniques, a new technique, ion implantation-assisted multi-arc ion plating, was proposed. Using the proposed technique, the surfaces of silicon nitride ceramics were modified by Ti ion implantation, and then three kinds of ternary coatings, (Ti,Al)N, (Ti,Zr)N and (Ti,Cr)N, were deposited on the as-implanted ceramics. The coatings prepared by this technique are of high-hardness and well adhesive to the ceramic substrates. The maximal hardness measured by nanoindentation tests is more than 40 GPa. The maximal critical load by nanoscratch tests is more than 60 mN. The cutting tools prepared by this technique with the presented coatings are of excellent performance in industrial applications. The technique may be promising for the surface modification of structural ceramics. (orig.)

  4. Studies on surface modification of poly(tetrafluoroethylene) film by remote and direct Ar plasma

    International Nuclear Information System (INIS)

    Wang Chen; Chen Jierong; Li Ru

    2008-01-01

    Poly(tetrafluoroethylene) (PTFE) surfaces are modified with remote and direct Ar plasma, and the effects of the modification on the hydrophilicity of PTFE are investigated. The surface microstructures and compositions of the PTFE film were characterized with the goniometer, scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Results show that the remote and direct plasma treatments modify the PTFE surface in morphology and composition, and both modifications cause surface oxidation of PTFE films, in the forming of some polar functional groups enhancing polymer wettability. When the remote and direct Ar plasma treats PTFE film, the contact angles decrease from the untreated 108-58 o and 65.2 o , respectively. The effect of the remote Ar plasma is more noticeable. The role of all kinds of active species, e.g. electrons, ions and free radicals involved in plasma surface modification is further evaluated. This shows that remote Ar plasma can restrain the ion and electron etching reaction and enhance radical reaction

  5. Towards Enhanced Performance Thin-film Composite Membranes via Surface Plasma Modification.

    Science.gov (United States)

    Reis, Rackel; Dumée, Ludovic F; Tardy, Blaise L; Dagastine, Raymond; Orbell, John D; Schutz, Jürg A; Duke, Mikel C

    2016-07-01

    Advancing the design of thin-film composite membrane surfaces is one of the most promising pathways to deal with treating varying water qualities and increase their long-term stability and permeability. Although plasma technologies have been explored for surface modification of bulk micro and ultrafiltration membrane materials, the modification of thin film composite membranes is yet to be systematically investigated. Here, the performance of commercial thin-film composite desalination membranes has been significantly enhanced by rapid and facile, low pressure, argon plasma activation. Pressure driven water desalination tests showed that at low power density, flux was improved by 22% without compromising salt rejection. Various plasma durations and excitation powers have been systematically evaluated to assess the impact of plasma glow reactions on the physico-chemical properties of these materials associated with permeability. With increasing power density, plasma treatment enhanced the hydrophilicity of the surfaces, where water contact angles decreasing by 70% were strongly correlated with increased negative charge and smooth uniform surface morphology. These results highlight a versatile chemical modification technique for post-treatment of commercial membrane products that provides uniform morphology and chemically altered surface properties.

  6. Processing and surface modification of novel natural-origin architectures aimed for biomedical applications

    Science.gov (United States)

    Silva, Simone dos Santos

    In the last decades, tissue engineering has emerged as a potential therapeutical tool aimed at developing substitutes that are able to restore proper function of the damaged organs/tissues. Nature-inspired routes involving natural origin polymer-based systems represent an attractive alternative to produce novel materials by mimicking the tissue environment required for tissue regeneration. Moreover, further modifications of these systems allow the adjustment of their properties in accordance with the requirements for successful biomedical applications. The main goal of the present thesis is to develop and modify natural origin polymer-based systems using simple methodologies such as sol-gel, surface modification by means of plasma treatment and blending of chitosan with proteins (soy protein isolate and silk fibroin). A sol-gel method was used to improve the bulk properties of chitosan by the incorporation of an inorganic component at the sub-nanometric level. Chitosan/siloxane hybrid materials were synthesised, where essentially urea bridges covalently bond the chitosan to the polysiloxane network. These bifunctional materials exhibit interesting photoluminescence features and a bioactive behaviour. In most situations in the biomedical field, the surface of a biomaterial is in direct contact with living tissues. Therefore, the surface characteristics play a fundamental role on the implant biocompatibility. In this thesis, nitrogen and argon plasma treatment was applied on chitosan membranes in order to improve their surface properties. The applied modifications promoted differences on surface chemistry, wettability and roughness, which reflected in a significant improvement of fibroblast adhesion and proliferation onto chitosan membranes. Besides the surface modification, blending of chitosan with proteins such as soy protein isolate and silk fibroin was also used to modify the bulk properties of chitosan. In situ cross-linking with glutaraldehyde solutions was

  7. Surface modification and fatigue behavior of nitinol for load bearing implants

    Science.gov (United States)

    Bernard, Sheldon A.

    Musculoskeletal disorders are recognized amongst the most significant human health problems that exist today. Even though considerable research and development has gone towards understanding musculoskeletal disorders, there is still lack of bone replacement materials that are appropriate for restoring lost structures and functions, particularly for load-bearing applications. Many materials on the market today, such as titanium and stainless steel, suffer from significantly higher modulus than natural bone and low bioactivity leading to stress shielding and implant loosening over longer time use. Nitinol (NiTi) is an equiatomic intermetallic compound of nickel and titanium whose unique biomechanical and biological properties contributed to its increasing use as a biomaterial. An innovative method for creating dense and porous net shape NiTi alloy parts has been developed to improve biological properties while maintaining comparable or better mechanical properties than commercial materials that are currently in use. Laser engineered net shaping (LENS(TM)) and surface electrochemistry modification was used to create dense/porous samples and micro textured surfaces on NiTi parts, respectively. Porous implants are known to promote cell adhesion and have a low elastic modulus, a combination that can significantly increase the life of an implant. However, porosity can significantly reduce the fatigue life of an implant, and very little work has been reported on the fatigue behavior of bulk porous metals, specifically on porous nitinol alloy. High-cycle rotating bending and compression-compression fatigue behavior of porous NiTi fabricated using LENS(TM) were studied. In cyclic compression loading, plastic strain increased with increasing porosity and it was evident that maximum strain was achieved during the first 50000 cycles and remained constant throughout the remaining loading. No failures were observed due to loading up to 150% of the yield strength. When subjected

  8. Surface modification of polyacrylonitrile-based carbon fiber and its interaction with imide

    International Nuclear Information System (INIS)

    Xu Bing; Wang Xiaoshu; Lu Yun

    2006-01-01

    In this work, sized polyacrylonitrile (PAN)-based carbon fibers were chemically modified with nitric acid and maleic anhydride (MA) in order to improve the interaction between carbon fiber surface and polyimide matrix. Bismaleimide (BMI) was selected as a model compound of polyimide to react with modified carbon fiber. The surface characteristic changing after modification and surface reaction was investigated by element analysis (EA), scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) and surface enhanced Raman scattering (SERS). The results indicated that the modification of carbon fiber surface with MA might follow the Diels Alder reaction mechanism. In the surface reaction between modified fibers and BMI, among the various surface functional groups, the hydroxyl group provided from phenolic hydroxyl group and bridged structure on carbon fiber may be the most effective group reacted with imide structure. The results may shed some light on the design of the appropriate surface structure, which could react with polyimide, and the manufacture of the carbon fiber-reinforced polyimide matrix composites

  9. Characterization and application of a surface modification designed for QCM-D studies of biotinylated biomolecules.

    Science.gov (United States)

    Nilebäck, Erik; Feuz, Laurent; Uddenberg, Hans; Valiokas, Ramūnas; Svedhem, Sofia

    2011-10-15

    The rapid development of surface sensitive biosensor technologies, especially towards nanoscale devices, requires increasing control of surface chemistry to provide reliable and reproducible results, but also to take full advantage of the sensing opportunities. Here, we present a surface modification strategy to allow biotinylated biomolecules to be immobilized to gold coated sensor crystals for quartz crystal microbalance with dissipation monitoring (QCM-D) sensing. The unique feature of QCM-D is its sensitivity to nanomechanical (viscoelastic) properties at the sensing interface. The surface modification was based on mixed monolayers of oligo(ethylene glycol) (OEG) disulfides, with terminal -OH or biotin groups, on gold. Mixtures containing 1% of the biotin disulfide were concluded to be the most appropriate based on the performance when streptavidin was immobilized to biotinylated sensors and the subsequent biotinylated bovine serum albumin (BSA) interaction was studied. The OEG background kept the unspecific protein binding to a minimum, even when subjected to serum solutions with a high protein concentration. Based on characterization by contact angle goniometry, ellipsometry, and infrared spectroscopy, the monolayers were shown to be well-ordered, with the OEG chains predominantly adopting a helical conformation but also partly an amorphous structure. Storage stability was concluded to depend mainly on light exposure while almost all streptavidin binding activity was retained when storing the sensors cold and dark for 8 weeks. The surface modification was also tested for repeated antibody-antigen interactions between BSA and anti-BSA (immobilized to biotinylated protein A) in QCM-D measurements lasting for >10h with intermediate basic regeneration. This proved an excellent stability of the coating and good reproducibility was obtained for 5 interaction cycles. With this kind of generic surface modification QCM-D can be used in a variety of biosensing

  10. Nanocapillary Atmospheric Pressure Plasma Jet: A Tool for Ultrafine Maskless Surface Modification at Atmospheric Pressure.

    Science.gov (United States)

    Motrescu, Iuliana; Nagatsu, Masaaki

    2016-05-18

    With respect to microsized surface functionalization techniques we proposed the use of a maskless, versatile, simple tool, represented by a nano- or microcapillary atmospheric pressure plasma jet for producing microsized controlled etching, chemical vapor deposition, and chemical modification patterns on polymeric surfaces. In this work we show the possibility of size-controlled surface amination, and we discuss it as a function of different processing parameters. Moreover, we prove the successful connection of labeled sugar chains on the functionalized microscale patterns, indicating the possibility to use ultrafine capillary atmospheric pressure plasma jets as versatile tools for biosensing, tissue engineering, and related biomedical applications.

  11. Surface modification of an epoxy resin with polyamines and polydopamine: The effect on the initial electroless copper deposition

    Energy Technology Data Exchange (ETDEWEB)

    Schaubroeck, David, E-mail: David.Schaubroeck@elis.ugent.be [Center for Microsystems Technology (CMST), imec and Ghent University, Technologiepark 914A, B-9052 Ghent (Belgium); Mader, Lothar [Center for Microsystems Technology (CMST), imec and Ghent University, Technologiepark 914A, B-9052 Ghent (Belgium); De Geyter, Nathalie; Morent, Rino [Research Unit Plasma Technology (RUPT), Department of Applied Physics, Faculty of Engineering, Ghent University, Sint-Pietersnieuwstraat 41, B-9000 Ghent (Belgium); Dubruel, Peter [Polymer Chemistry and Biomaterials Research Group, Ghent University, Krijgslaan 281 S4 bis, B-9000 Ghent (Belgium); Vanfleteren, Jan [Center for Microsystems Technology (CMST), imec and Ghent University, Technologiepark 914A, B-9052 Ghent (Belgium)

    2014-06-01

    This paper describes the influence of polydopamine and polyamine surface modifications of an etched epoxy cresol novolak (ECN) resin on the initial electroless copper deposition. Three different strategies to introduce polyamines on a surface in aqueous environment are applied: via polyethyleneimine adsorption (PEI), via polydopamine and via polyamines grafted to polydopamine. Next, the influence of these surface modifications on the catalytic palladium activation is investigated through X-ray photoelectron spectroscopy (XPS) analysis. Finally, the initial electroless copper deposition on modified epoxy surfaces is evaluated using SEM and Energy Dispersive Spectroscopy (EDS). Grafted polyamines on polydopamine surface modifications result in a large increase of the initial deposited copper.

  12. Surface modification of polyacrylonitrile fibre by nitrile hydratase from Corynebacterium nitrilophilus.

    Science.gov (United States)

    Chen, Sheng; Gao, Huihui; Chen, Jian; Wu, Jing

    2014-11-01

    Previously, nitrile hydratase (NHase) from Corynebacterium nitrilophilus was obtained and showed potential in polyacrylonitrile (PAN) fibre modification. In the present study, the modification conditions of C. nitrilophilus NHase on PAN were investigated. In the optimal conditions, the wettability and dyeability (anionic and reactive dyes) of PAN treated by C. nitrilophilus NHase reached a similar level of those treated by alkali. In addition, the chemical composition and microscopically observable were changed in the PAN surface after NHase treatment. Meanwhile, it revealed that cutinase combined with NHase facilitates the PAN hydrolysis slightly because of the ester existed in PAN as co-monomer was hydrolyzed. All these results demonstrated that C. nitrilophilus NHase can modify PAN efficiently without textile structure damage, and this study provides a foundation for the further application of C. nitrilophilus NHase in PAN modification industry.

  13. Effects of Surface-modification of Carbon Black on the Characteristics of Polymerized Toner

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Eun Ho; Kim, Dae Su [Chungbuk National University, Cheongju (Korea, Republic of)

    2013-10-15

    Carbon black was surface-modified to prepare styrene-based suspension polymerized toner with excellent carbon black dispersibility inside toner particles. Carbon black was oxidized first to introduce hydroxyl groups on the surfaces, then esterification between the hydroxyl groups and carboxyl groups of organic acids (oleic acid, palmitic acid, acrylic acid) was followed to obtain organically surface-modified carbon black. The surface-modification of carbon black was confirmed by FTIR. Apparent carbon black dispersibility in the monomer mixture of the binder resin was tested and the particle size of dispersed carbon black was measured by particle size analyzer. Optical micrographs showed that carbon black dispersibility inside toner particles was improved considerably when the carbon black surface-modified with oleic acid was used. The polymerized toner prepared with the carbon black surface-modified with oleic acid showed ideal particle size and size distribution as a toner.

  14. Development of bio/blood compatible polypropylene through low pressure nitrogen plasma surface modification

    Energy Technology Data Exchange (ETDEWEB)

    Gomathi, N., E-mail: gomathi@iist.ac.in [Department of Chemistry, Indian Institute of Space Science and Technology, Department of Space, Trivandrum, 695547 (India); Department of Chemical Engineering, Indian Institute of Technology, Kharagpur, 721302 (India); Rajasekar, R. [Materials Science Center, Indian Institute of Technology, Kharagpur, 721302 (India); Department of BIN Fusion Technology, Chonbuk National University, Jeonju, Jeonbuk, 561-756 (Korea, Republic of); Babu, R. Rajesh [Rubber Technology Center, Indian Institute of Technology, Kharagpur, 721302 (India); Advanced Tyre Research, Apollo Tyres, Baroda, 391750 (India); Mishra, Debasish [Department of Biotechnolgy, Indian Institute of Technology, Kharagpur, 721302 (India); Neogi, S. [Department of Chemical Engineering, Indian Institute of Technology, Kharagpur, 721302 (India)

    2012-10-01

    Surface modification of polypropylene by nitrogen containing plasma was performed in this work in order to improve the wettability which resulted in enhanced biocompatibility and blood compatibility. Various nitrogen containing functional groups as well as oxygen containing functional groups were found to be incorporated to the polymer surface during plasma treatment and post plasma reaction respectively. Wettability of the polymers was evaluated by static contact angle measurement to show the improvement in hydrophilicity of plasma treated polypropylene. Cross linking and surface modification were reported to be dominating in the case of nitrogen plasma treatment compared to degradation. The effect of various process variables namely power, pressure, flow rate and treatment time on surface energy and weight loss was studied at various levels according to the central composite design of response surface methodology (RSM). Except pressure the other variables resulted in increased weight loss due to etching whereas with increasing pressure weight loss was found to increase and then decrease. The effect of process variables on surface morphology of polymers was evaluated by Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). Well spread fibroblast cells on nitrogen plasma treated polypropylene due to the presence of CO, NH{sup 2+} and NH{sup +} was observed. Reduced platelet adhesion and increased partial thromboplastin time evidenced the increased blood compatibility. - Highlights: Black-Right-Pointing-Pointer Improved biocompatibility and blood compatibility of polypropylene. Black-Right-Pointing-Pointer Nitrogen plasma surface modification. Black-Right-Pointing-Pointer Maintaining a balance between polar group incorporation and weight loss due to etching. Black-Right-Pointing-Pointer Optimization of process conditions by response surface methodology.

  15. Development of bio/blood compatible polypropylene through low pressure nitrogen plasma surface modification

    International Nuclear Information System (INIS)

    Gomathi, N.; Rajasekar, R.; Babu, R. Rajesh; Mishra, Debasish; Neogi, S.

    2012-01-01

    Surface modification of polypropylene by nitrogen containing plasma was performed in this work in order to improve the wettability which resulted in enhanced biocompatibility and blood compatibility. Various nitrogen containing functional groups as well as oxygen containing functional groups were found to be incorporated to the polymer surface during plasma treatment and post plasma reaction respectively. Wettability of the polymers was evaluated by static contact angle measurement to show the improvement in hydrophilicity of plasma treated polypropylene. Cross linking and surface modification were reported to be dominating in the case of nitrogen plasma treatment compared to degradation. The effect of various process variables namely power, pressure, flow rate and treatment time on surface energy and weight loss was studied at various levels according to the central composite design of response surface methodology (RSM). Except pressure the other variables resulted in increased weight loss due to etching whereas with increasing pressure weight loss was found to increase and then decrease. The effect of process variables on surface morphology of polymers was evaluated by Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). Well spread fibroblast cells on nitrogen plasma treated polypropylene due to the presence of CO, NH 2+ and NH + was observed. Reduced platelet adhesion and increased partial thromboplastin time evidenced the increased blood compatibility. - Highlights: ► Improved biocompatibility and blood compatibility of polypropylene. ► Nitrogen plasma surface modification. ► Maintaining a balance between polar group incorporation and weight loss due to etching. ► Optimization of process conditions by response surface methodology.

  16. Surface modification of magnesium aluminum hydroxide nanoparticles with poly(methyl methacrylate) via one-pot in situ polymerization

    Energy Technology Data Exchange (ETDEWEB)

    Guo Xiaojun, E-mail: guoxj6906@163.com [College of Chemistry and Chemical Engineering, Northwest Normal University, 967 Anning East Road, Lanzhou 730070 (China); Zhao Leihua; Zhang Li; Li Jing [College of Chemistry and Chemical Engineering, Northwest Normal University, 967 Anning East Road, Lanzhou 730070 (China)

    2012-01-15

    Hydrophobic magnesium aluminum hydroxide composite particles (PMMA-MAH) were obtained by means of grafting poly(methyl methacrylate) (PMMA) onto the surface of magnesium aluminum hydroxide(MAH) nanoparticles after a novel type of phosphate coupling agent (DN-27) modification. The introduction of functional double bonds was firstly conducted on the surface of nanoparticles by DN-27 modification, followed by one-pot in situ polymerization on the particles surface using methyl methacrylate (MMA) as monomer, azoisobutyronitrile (AIBN) as initiator and sodium dodecyl sulfate (SDS) as stabilizer to graft PMMA on the surface of DN-27-modified MAH particles. The obtained composite particles were characterized by field-emission scanning electron microscope (FESEM), Fourier transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), X-ray powder diffraction (XRD). The results show that the organic macromolecule PMMA could be successfully grafted on the surface of DN-27-modified MAH nanoparticles and the thermal stability of the PMMA-MAH composite particles had been improved. Compared with unmodified blank MAH sample, the product obtained with this method possesses better hydrophobic properties such as a higher water contact angle of 108 Degree-Sign and a well dispersion.

  17. Interaction of progenitor bone cells with different surface modifications of titanium implant

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Wen-Cheng, E-mail: wencchen@fcu.edu.tw [Advanced Medical Devices and Composites Laboratory, Department of Fiber and Composite Materials, College of Engineering, Feng Chia University, Taichung 40724, Taiwan (China); Chen, Ya-Shun [Advanced Medical Devices and Composites Laboratory, Department of Fiber and Composite Materials, College of Engineering, Feng Chia University, Taichung 40724, Taiwan (China); Ko, Chia-Ling [Advanced Medical Devices and Composites Laboratory, Department of Fiber and Composite Materials, College of Engineering, Feng Chia University, Taichung 40724, Taiwan (China); Dental Medical Devices and Materials Research Center, College of Dental Medicine, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China); Lin, Yi; Kuo, Tzu-Huang; Kuo, Hsien-Nan [Medical Device Development Division, Metal Industries Research and Development Centre, Kaohsiung 82151, Taiwan (China)

    2014-04-01

    Changes in the physical and chemical properties of Ti surfaces can be attributed to cell performance, which improves surface biocompatibility. The cell proliferation, mineralization ability, and gene expression of progenitor bone cells (D1 cell) were compared on five different Ti surfaces, namely, mechanical grinding (M), electrochemical modification through potentiostatic anodization (ECH), sandblasting and acid etching (SLA), sandblasting, hydrogen peroxide treatment, and heating (SAOH), and sandblasting, alkali heating, and etching (SMART). SAOH treatment produced the most hydrophilic surface, whereas SLA produced the most hydrophobic surface. Cell activity indicated that SLA and SMART produced significantly rougher surfaces and promoted D1 cell attachment within 1 day of culturing, whereas SAOH treatment produced moderate roughness (Ra = 1.26 μm) and accelerated the D1 cell proliferation up to 7 days after culturing. The ECH surface significantly promoted alkaline phosphatase (ALP) expression and osteocalcin (OCN) secretion in the D1 cells compared with the other surface groups. The ECH and SMART-treated Ti surfaces resulted in maximum ALP and OCN expressions during the D1 cell culture. SLA, SAOH, and SMART substrate surfaces were rougher and exhibited better cell metabolic responses during the early stage of cell attachment, proliferation, and morphologic expressions within 1 day of D1 cell culture. The D1 cells cultured on the ECH and SMART substrates exhibited higher differentiation, and higher ALP and OCN expressions after 10 days of culture. Thus, the ECH and SMART treatments promote better ability of cell mineralization in vitro, which demonstrate their great potential for clinical use. - Highlights: • Progenitor bone cells onto Ti with different modifications are characterized. • Surface roughness and hydrophilicity encourage early stage cell attachment. • Composition and surface treatments are more vital in bone cell mineralization.

  18. Graphite anode surface modification with controlled reduction of specific aryl diazonium salts for improved microbial fuel cells power output.

    Science.gov (United States)

    Picot, Matthieu; Lapinsonnière, Laure; Rothballer, Michael; Barrière, Frédéric

    2011-10-15

    Graphite electrodes were modified with reduction of aryl diazonium salts and implemented as anodes in microbial fuel cells. First, reduction of 4-aminophenyl diazonium is considered using increased coulombic charge density from 16.5 to 200 mC/cm(2). This procedure introduced aryl amine functionalities at the surface which are neutral at neutral pH. These electrodes were implemented as anodes in "H" type microbial fuel cells inoculated with waste water, acetate as the substrate and using ferricyanide reduction at the cathode and a 1000 Ω external resistance. When the microbial anode had developed, the performances of the microbial fuel cells were measured under acetate saturation conditions and compared with those of control microbial fuel cells having an unmodified graphite anode. We found that the maximum power density of microbial fuel cell first increased as a function of the extent of modification, reaching an optimum after which it decreased for higher degree of surface modification, becoming even less performing than the control microbial fuel cell. Then, the effect of the introduction of charged groups at the surface was investigated at a low degree of surface modification. It was found that negatively charged groups at the surface (carboxylate) decreased microbial fuel cell power output while the introduction of positively charged groups doubled the power output. Scanning electron microscopy revealed that the microbial anode modified with positively charged groups was covered by a dense and homogeneous biofilm. Fluorescence in situ hybridization analyses showed that this biofilm consisted to a large extent of bacteria from the known electroactive Geobacter genus. In summary, the extent of modification of the anode was found to be critical for the microbial fuel cell performance. The nature of the chemical group introduced at the electrode surface was also found to significantly affect the performance of the microbial fuel cells. The method used for

  19. Surface Modification of Biodegradable Polymers towards Better Biocompatibility and Lower Thrombogenicity.

    Science.gov (United States)

    Rudolph, Andreas; Teske, Michael; Illner, Sabine; Kiefel, Volker; Sternberg, Katrin; Grabow, Niels; Wree, Andreas; Hovakimyan, Marina

    2015-01-01

    Drug-eluting stents (DES) based on permanent polymeric coating matrices have been introduced to overcome the in stent restenosis associated with bare metal stents (BMS). A further step was the development of DES with biodegradable polymeric coatings to address the risk of thrombosis associated with first-generation DES. In this study we evaluate the biocompatibility of biodegradable polymer materials for their potential use as coating matrices for DES or as materials for fully bioabsorbable vascular stents. Five different polymers, poly(L-lactide) PLLA, poly(D,L-lactide) PDLLA, poly(L-lactide-co-glycolide) P(LLA-co-GA), poly(D,L-lactide-co-glycolide) P(DLLA-co-GA) and poly(L-lactide-co-ε-caprolactone), P(LLA-co-CL) were examined in vitro without and with surface modification. The surface modification of polymers was performed by means of wet-chemical (NaOH and ethylenediamine (EDA)) and plasma-chemical (O2 and NH3) processes. The biocompatibility studies were performed on three different cell types: immortalized mouse fibroblasts (cell line L929), human coronary artery endothelial cells (HCAEC) and human umbilical vein endothelial cells (HUVEC). The biocompatibility was examined quantitatively using in vitro cytotoxicity assay. Cells were investigated immunocytochemically for expression of specific markers, and morphology was visualized using confocal laser scanning (CLSM) and scanning electron (SEM) microscopy. Additionally, polymer surfaces were examined for their thrombogenicity using an established hemocompatibility test. Both endothelial cell types exhibited poor viability and adhesion on all five unmodified polymer surfaces. The biocompatibility of the polymers could be influenced positively by surface modifications. In particular, a reproducible effect was observed for NH3-plasma treatment, which enhanced the cell viability, adhesion and morphology on all five polymeric surfaces. Surface modification of polymers can provide a useful approach to enhance

  20. Arsonic acid as a robust anchor group for the surface modification of Fe3O4.

    Science.gov (United States)

    Ahn, Jihoon; Moon, Doo-Sik; Lee, Jin-Kyu

    2013-12-03

    In order to use iron oxide nanoparticles (Fe3O4) in various applications, a surface modification that provides colloidal stability and additional functionality to the nanoparticles is necessary. For the modification of the nanoparticle surface with ligand molecules, the ligand molecule should contain an anchor group that has a strong affinity for the surface. However, currently used anchor groups have shown some problems such as low affinity and stability as well as reactivity with the surface. In this study, arsonic acid (RAsO(OH)2) was investigated as a novel anchor group. It was possible to introduce azide groups on the surface of iron oxide nanoparticles using 4-azidophenylarsonic acid, and the desired functional molecules could be chemically attached to the surface via copper-catalyzed azide-alkyne cycloaddition (click chemistry). By quantifying and comparing the amount of attached anchors on the surface, it was found that arsonic acid displays better affinity than other currently used anchors (catechol, carboxylic acid). Furthermore, we examined the binding reversibility, long-term anchoring stability, and anchoring stability at various pH values. It was revealed that arsonic acid is a stable anchor in various conditions.

  1. Surface modification of seawater desalination reverse osmosis membranes: Characterization studies & performance evaluation

    KAUST Repository

    Matin, Asif

    2014-06-01

    In this work we report surface modification of commercial reverse osmosis membranes by depositing ultrathin copolymer coatings, which could potentially enhance the biofouling resistance of RO membranes. Hydrophilic monomer hydroxyethyl methacrylate (HEMA) and a hydrophobic monomer, perfluorodecyl acrylate (PFDA) were copolymerized directly on the active layer of commercial aromatic polyamide reverse osmosis (RO) membranes using an initiated Chemical Vapor Deposition (iCVD) technique. Attenuated total reflective Fourier transform infrared spectra (ATR-FTIR) verified the successful modification of the membrane surfaces as a new FTIR adsorption band around 1730cm-1 corresponding to carbonyl groups in the copolymer film appeared after the deposition. X-ray Photoelectron spectroscopy (XPS) analysis also confirmed the presence of the copolymer film on the membrane surface by showing strong fluorine peaks emanating from the fluorinated alkyl side chains of the PFA molecules. Contact angle measurements with deionized water showed the modified membrane surfaces to be initially very hydrophobic but quickly assumed a hydrophilic character within few minutes. Atomic Force Microscopy (AFM) revealed that the deposited films were smooth and conformal as the surface topology of the underlying membrane surface remained virtually unchanged after the deposition. FESEM images of the top surface also showed that the typical ridge-and-valley structure associated with polyamide remained intact after the deposition. Short-term permeation tests using DI water and 2000ppm NaCl water showed that the deposited copolymer coatings had negligible effect on permeate water flux and salt rejection. © 2013 Elsevier B.V.

  2. Nitrogen ion implantation on stainless steel: AFM study of surface modification

    Energy Technology Data Exchange (ETDEWEB)

    Chico, B. [Dpto. Ingenieria de Materiales, Degradacion y Durabilidad, Centro Nacional de Investigaciones Metalurgicas (CENIM), CSIC, Avda. Gregorio del Amo, 8, 28040 Madrid (Spain)]. E-mail: bchico@cenim.csic.es; Martinez, L. [Dpto. Ciencia de los Materiales e Ingenieria Metalurgica, Facultad de Ciencias Quimicas, Universidad Complutense de Madrid, Ciudad Universitaria, 28040 Madrid (Spain); Perez, F.J. [Dpto. Ciencia de los Materiales e Ingenieria Metalurgica, Facultad de Ciencias Quimicas, Universidad Complutense de Madrid, Ciudad Universitaria, 28040 Madrid (Spain)

    2005-04-30

    This work presents a study by means of atomic force microscopy (AFM) of the modification of the surface topography of AISI 304 austenitic stainless steel after N-ion implantation, irradiated by 1 x 10{sup 15} N{sub 2}{sup +}/cm{sup 2} at 80 keV. Prior to the implantation surface modification, the samples were electropolished for the optimum observation of the surface at a small scale to obtain an initial surface with the smaller roughness. The electrolytic bath was composed of a mixture of water/sulphuric acid/orthophosphoric acid in percentages 20, 20 and 60%, respectively. Once the surface was optimized, the samples were implanted and observed by AFM, a new technique whose importance relies on its resolution power, allowing the acquisition of topographic images of the surface with nanometric resolution. Thanks to the high resolution power could be observed that ion implantation increases the surface roughness and promotes the apparition of 3 {mu}m wide and 10 nm depth craters as well as the apparition of products with singular morphology.

  3. Surface modification of model hydrogel contact lenses with hyaluronic acid via thiol-ene "click" chemistry for enhancing surface characteristics.

    Science.gov (United States)

    Korogiannaki, Myrto; Zhang, Jianfeng; Sheardown, Heather

    2017-10-01

    Discontinuation of contact lens wear as a result of ocular dryness and discomfort is extremely common; as many as 26% of contact lens wearers discontinue use within the first year. While patients are generally satisfied with conventional hydrogel lenses, improving on-eye comfort continues to remain a goal. Surface modification with a biomimetic, ocular friendly hydrophilic layer of a wetting agent is hypothesized to improve the interfacial interactions of the contact lens with the ocular surface. In this work, the synthesis and characterization of poly(2-hydroxyethyl methacrylate) surfaces grafted with a hydrophilic layer of hyaluronic acid are described. The immobilization reaction involved the covalent attachment of thiolated hyaluronic acid (20 kDa) on acrylated poly(2-hydroxyethyl methacrylate) via nucleophile-initiated Michael addition thiol-ene "click" chemistry. The surface chemistry of the modified surfaces was analyzed by Fourier transform infrared spectroscopy-attenuated total reflectance and X-ray photoelectron spectroscopy. The appearance of N (1s) and S (2p) peaks on the low resolution X-ray photoelectron spectroscopy spectra confirmed successful immobilization of hyaluronic acid. Grafting hyaluronic acid to the poly(2-hydroxyethyl methacrylate) surfaces decreased the contact angle, the dehydration rate, and the amount of nonspecific sorption of lysozyme and albumin in comparison to pristine hydrogel materials, suggesting the development of more wettable surfaces with improved water-retentive and antifouling properties, while maintaining optical transparency (>92%). In vitro testing also showed excellent viability of human corneal epithelial cells with the hyaluronic acid-grafted poly(2-hydroxyethyl methacrylate) surfaces. Hence, surface modification with hyaluronic acid via thiol-ene "click" chemistry could be useful in improving contact lens surface properties, potentially alleviating symptoms of contact lens related dryness and discomfort during

  4. Tuning Tribological Performance of Layered Zirconium Phosphate Nanoplatelets in Oil by Surface and Interlayer Modifications

    Science.gov (United States)

    Han, Xiao; Yong, Huaisong; Sun, Dazhi

    2017-09-01

    Two-dimensional (2D) inorganic layered nanoplatelets exhibit superior lubricating properties in both solid states and oil dispersions. In this paper, we have systematically investigated the effects of surface and interlayer modifications on the tribological performance of layered α-zirconium phosphate (ZrP) nanoplatelets in mineral oil. The pristine layered ZrP nanoplatelets were first reacted with silanes of different alkyl chains to achieve outer surface modifications, followed by intercalation with different alkyl amines to alter the interlayer spacing. Friction and anti-wear studies on ZrP nanoplatelets with various modifications in mineral oils suggest that a longer alkyl chain on the outer surfaces along with a small increase in interlayer spacing would lead to a better tribological behavior especially under a relatively heavy load condition. Our results illustrate the ability of tuning the tribological properties of 2D layered nanoplatelets in oils by varying their surface and interlayer functionalities and would be helpful for understanding the underlying tribological mechanisms of nanolubricating oils containing 2D layered nanoplatelets. [Figure not available: see fulltext.

  5. Tuning Tribological Performance of Layered Zirconium Phosphate Nanoplatelets in Oil by Surface and Interlayer Modifications.

    Science.gov (United States)

    Han, Xiao; Yong, Huaisong; Sun, Dazhi

    2017-09-20

    Two-dimensional (2D) inorganic layered nanoplatelets exhibit superior lubricating properties in both solid states and oil dispersions. In this paper, we have systematically investigated the effects of surface and interlayer modifications on the tribological performance of layered α-zirconium phosphate (ZrP) nanoplatelets in mineral oil. The pristine layered ZrP nanoplatelets were first reacted with silanes of different alkyl chains to achieve outer surface modifications, followed by intercalation with different alkyl amines to alter the interlayer spacing. Friction and anti-wear studies on ZrP nanoplatelets with various modifications in mineral oils suggest that a longer alkyl chain on the outer surfaces along with a small increase in interlayer spacing would lead to a better tribological behavior especially under a relatively heavy load condition. Our results illustrate the ability of tuning the tribological properties of 2D layered nanoplatelets in oils by varying their surface and interlayer functionalities and would be helpful for understanding the underlying tribological mechanisms of nanolubricating oils containing 2D layered nanoplatelets. Graphical abstract ᅟ.

  6. Synthesis and property of nanoparticles in ionic liquids and their surface modification

    Science.gov (United States)

    Wang, Yong

    This thesis describes synthesis and surface modifications of inorganic nanoparticles, including noble metal, metal oxide, and semiconductors. The first part explores synthesis of nanoparticles in 1-butyl-3-methylimidazolium bis(triflylmethyl-sulfonyl)imide ionic liquid ([BMIM][Tf2N] IL). When this IL was used as solvents in the non-hydrolytic synthesis, the growing nanoparticles underwent an auto-separation process, which would drive final products out of the IL reaction mixture during reactions. Highly uniform nanoparticles of metal oxides, noble metals, and CdSe semiconductor, could be obtained through this auto-separation approach. By controlling the composition of capping agents and reaction temperature, iron oxide nanoparticles of various shapes including cube, sphere, and rod, could be readily achieved. After the synthesis, the IL kept its good chemical and thermal stabilities, and could be recycled for the synthesis of nanoparticles. Monodispersed 10-nm iron oxide nanoparticles were repeatedly produced using recycled ILs. The biphasic mixture of ionic liquid and water also facilitated the formation of nanoparticles. In this method, hydrophobic IL was mixed with aqueous solutions of precursors and reductants under vigorous stir. The reactions were thought to take place inside water droplets or around the interfacial region between IL and water. The resultant metal nanoparticles were stabilized by ionic liquid and could be subsequently transferred into other media. Ionic liquids used in this process were also recycled and used repeatedly to obtain gold nanoparticles of controlled sizes and shapes. Platinum nanoparticles stabilized by IL were used as heterogeneous catalysts for the hydrogenation reaction of cyclohexene. This system kept its catalytic activity after several rounds of reactions. The outstanding thermal stability of [BMIM][Tf2N] IL was also utilized to obtain PtCo nanoparticles of different chemical compositions. Surface properties of hydrophobic

  7. Surface Modification of Direct-Current and Radio-Frequency Oxygen Plasma Treatments Enhance Cell Biocompatibility

    Directory of Open Access Journals (Sweden)

    Wan-Ching Chou

    2017-10-01

    Full Text Available The sand-blasting and acid etching (SLA method can fabricate a rough topography for mechanical fixation and long-term stability of titanium implant, but can not achieve early bone healing. This study used two kinds of plasma treatments (Direct-Current and Radio-Frequency plasma to modify the SLA-treated surface. The modification of plasma treatments creates respective power range and different content functional OH groups. The results show that the plasma treatments do not change the micron scale topography, and plasma-treated specimens presented super hydrophilicity. The X-ray photoelectron spectroscopy (XPS-examined result showed that the functional OH content of the RF plasma-treated group was higher than the control (SLA and DC treatment groups. The biological responses (protein adsorption, cell attachment, cell proliferation, and differentiation promoted after plasma treatments, and the cell responses, have correlated to the total content of amphoteric OH groups. The experimental results indicated that plasma treatments can create functional OH groups on SLA-treated specimens, and the RF plasma-treated SLA implant thus has potential for achievement of bone healing in early stage of implantation.

  8. Surface modification of ZnS films by applying an external magnetic field in vacuum chamber

    Science.gov (United States)

    Ehsani, M. H.; Zarei Moghadam, R.; Rezagholipour Dizaji, H.; Kameli, P.

    2017-09-01

    In this paper, ZnS films were prepared using pulsed laser deposition technique in vacuum chamber in the presence and absence of an external magnetic field. The applied magnetic field effects on optical properties and film growth conditions were studied. For this reason, morphological, structural and optical properties of the grown films have been investigated by atomic force microscopy, field emission scanning electron microscopy, x-ray diffraction and UV-vis spectroscopy analysis techniques. The structural studies revealed that the ZnS films deposited at 200 °C crystallized in hexagonal structure. The results showed the improvement of the film crystallinity upon grain size increment and the surface morphology modification resulted from applying an external magnetic field. Using the UV-vis spectroscopy data, absorption coefficient (α), refractive index (n) and extinction coefficient (k) of the samples were calculated. The band gap energy (E g) and Urbach energy were also calculated by Tauc, ASF and DASF methods. The results show that by applying magnetic field, the band gap and Urbach energies reduced, due to improvement in the film crystallinity. For describing the magnetic field effect, a simulation of applied magnetic field effect on vapor flux in vacuum chamber was performed using Multi-Physics COMSOL package.

  9. Evaluation of electrode surface modification techniques for the development of chemical sensors

    International Nuclear Information System (INIS)

    Galiatsatos, C.

    1988-01-01

    This thesis covers several aspects of electrode surface modification techniques. The successful application of gamma-radiation to create polymer-coated electrodes, where the polymers can be ion exchangers and consequently of great analytical interest by themselves (such as the polymer poly(diallyl) dimethyl ammonium chloride) or where some other neutral polymers can function as convenient matrices for the introduction of biomolecules and/or other electrochemically interesting species is reported. This is demonstrated by using the neutral polymer poly(vinyl alcohol) (PVAL) as a matrix for immobilization of the enzyme glucose oxidase and the mediator methyl viologen. The effect of γ-radiation on PVAL is discussed, as well as swelling properties of the irradiated polymers and specific characteristics of the created chemical sensors. Results of an experiment where the various kinds of interactions between the ion-exchange polymer Nafion and some positively charged species are explored are reported, and a model system for competition (methyl viologen vs. ruthenium hexaamine) which increases significantly our understanding of the interaction is mentioned. The effect of γ-radiation on Nafion and its ion-exchange compabilities is discussed also. A system of conduction polymers primarily polypyrrole, used as a detector of electroinactive anions due to their doping-undergoing in the film is discussed. Preliminary results on a new method that involves chemical cross-linking of a triisocyane molecule with -OH containing polymers in the presence of enzymes are reported

  10. 3-dimensional microscope analysis of bone and tooth surface modifications: comparisons of fossil specimens and replicas.

    Science.gov (United States)

    Bello, Silvia M; Verveniotou, Efstratia; Cornish, Lorraine; Parfitt, Simon A

    2011-01-01

    Cut-marks on fossil bones and teeth are an important source of evidence in the reconstruction of ancient butchery practices. The analysis of butchery marks has allowed archaeologists to interpret aspects of past subsistence strategies and the behavior of early humans. Recent advances in optical scanning microscopy allow detailed measurements of cut-mark morphology to be undertaken. An example of this technology is the Alicona 3D InfiniteFocus imaging microscope, which has been applied recently to the study of surface modifications on bones and teeth. Three-dimensional models generated by the Alicona microscope have been used to identify cross-sectional features of experimental cut-marks that are characteristic for specific cutting actions (e.g., slicing, chopping, scraping) and different tool types (e.g., metal versus stone tools). More recently, this technology has been applied successfully to the analysis of ∼500,000 year-old cut-marked animal bones from Boxgrove (U.K.), as well as cannibalized 14,700 cal BP year-old human bones from Gough's Cave (U.K.). This article describes molding methods used to replicate fragile prehistoric bones and teeth, where image quality was adversely affected by specimen translucency and reflectivity. Alicona images generated from molds and casts are often of better quality than those of the original specimen. Copyright © 2011 Wiley Periodicals, Inc.

  11. Surface Modification of Asymmetric Polysulfone/Polyethylene Glycol Membranes by DC Ar-Glow Discharge Plasma

    Directory of Open Access Journals (Sweden)

    Chalad Yuenyao

    2016-01-01

    Full Text Available Polysulfone/polyethylene glycol (PSF/PEG membranes were prepared by dry/wet phase inversion method. Effects of direct current glow discharge plasma using argon as working gas on morphological structures and gas separation properties of membranes were studied. Alteration of membrane characteristics were analyzed by various techniques like contact angle, scanning electron microscope, Fourier transform infrared spectroscopy, and dynamic mechanical thermal analysis. Gas separation properties were measured in terms of permeation and ideal O2/N2 selectivity. Results showed that hydrophilic and gas separation properties of PSF/PEG membranes increased by plasma surface modification. It was also shown that the dosage of PEG and plasma treatment affected the morphological structures and mechanical and gas separation properties. The macro voids and transmembrane structure disappeared with a little amount of PEG dosage. Pore size and mechanical strength tend to decrease with increasing PEG dosage up to 10 wt%. Glass transition temperature (Tg receded from 201.8 to 143.7°C for pure PSF and PSF/PEG with PEG dosage of 10 wt%. O2 and N2 gases permeation through the 10-minute plasma treated membranes tend to increase. However, the permeation strongly dispersed when treatment time was more extended.

  12. Surface modification of TiO2 nanotubes by grafting with APTS coupling agents

    Science.gov (United States)

    Phan Duong, Hong; Le, Minh Duc; Dao, Hung Cuong; Chen, Chia-Yun

    2017-10-01

    Titanium dioxide nanotubes (TNTs) have been considered the promising nanostructures employed for many practical applications such as biomedical, photonic and optoelectronic devices. Nevertheless, strong aggregation of TNTs within various aqueous media significantly hindered their practical utilizations and the capability of dispersing TNTs in the desired solvents are urgent to be improved. Therefore, in this study, the methodic investigations have been performed on the grafted modification of 3-aminopropyl triethoxysilane (APTS) on the surfaces of synthesized TNTs. A preliminary study was carried out to evaluate the influences of key parameters, including the concentrations of coupling agents, temperatures and the reaction durations, on the grafting efficiency of the aminosilane using Statistical design of experiments (DoE) methodology. TNTs with approximately 10–20 nm in diameter were prepared with the controlled hydrothermal treatment of commercialized P25 particles. The obtained products were revealed by the modern physicochemical systems including x-ray diffraction (XRD), transmission electron microscopy (TEM) and Brunauer-Emmett-Teller (BET) analysis. The additions of silane agent, reaction temperature and time have been adjusted to reveal the influences of the grafting efficiency (from 2.5 to 7.8 wt %) by thermal gravimetric analysis (TGA). Analysis of Fourier transform infrared spectroscopy (FTIR) has confirmed the successful link of Ti–O–Si chemical bonds on the grafted TNTs.

  13. The third generation multi-purpose plasma immersion ion implanter for surface modification of materials

    CERN Document Server

    Tang Bao Yin; Wang Xiao Feng; Gan Kong Yin; Wang Song Yan; Chu, P K; Huang Nian Ning; Sun Hong

    2002-01-01

    The third generation multi-purpose plasma immersion ion implantation (PIII) equipment has been successfully used for research and development of surface modification of biomedical materials, metals and their alloys in the Southwest Jiaotong University. The implanter equipped with intense current, pulsed cathodic arc metal plasma sources which have both strong coating function and gas and metal ion implantation function. Its pulse high voltage power supply can provide big output current. It can acquire very good implantation dose uniformity. The equipment can both perform ion implantation and combine ion implantation with sputtering deposition and coating to form many kinds of synthetic surface modification techniques. The main design principles, features of important components and achievement of research works in recent time have been described

  14. Nanoscale surface modification for enhanced biosensing a journey toward better glucose monitoring

    CERN Document Server

    Zhang, Guigen

    2015-01-01

    This book gives a comprehensive overview of electrochemical-based biosensors and their crucial components. Practical examples are given throughout the text to illustrate how the performance of electrochemical-based biosensors can be improved by nanoscale surface modification and how an optimal design can be achieved. All essential aspects of biosensors are considered, including electrode functionalization, efficiency of the mass transport of reactive species, and long term durability and functionality of the sensor. This book also: ·       Explains how the performance of an electrochemical-based biosensor can be improved by nanoscale surface modification ·       Gives readers the tools to evaluate and improve the performance of a biosensor with a multidisciplinary approach that considers electrical, electrostatic, electrochemical, chemical, and biochemical events ·       Links the performance of a sensor to the various governing physical and chemical principles so readers can fully unders...

  15. Modification of transition's factor in the compact surface-potential-based MOSFET model

    Directory of Open Access Journals (Sweden)

    Kevkić Tijana

    2016-01-01

    Full Text Available The modification of an important transition's factor which enables continual behavior of the surface potential in entire useful range of MOSFET operation is presented. The various modifications have been made in order to obtain an accurate and computationally efficient compact MOSFET model. The best results have been achieved by introducing the generalized logistic function (GL in fitting of considered factor. The smoothness and speed of the transition of the surface potential from the depletion to the strong inversion region can be controlled in this way. The results of the explicit model with this GL functional form for transition's factor have been verified extensively with the numerical data. A great agreement was found for a wide range of substrate doping and oxide thickness. Moreover, the proposed approach can be also applied on the case where quantum mechanical effects play important role in inversion mode.

  16. Effect of surface modifications on the bond strength of zirconia ceramic with resin cement resin.

    Science.gov (United States)

    Hallmann, Lubica; Ulmer, Peter; Lehmann, Frank; Wille, Sebastian; Polonskyi, Oleksander; Johannes, Martina; Köbel, Stefan; Trottenberg, Thomas; Bornholdt, Sven; Haase, Fabian; Kersten, Holger; Kern, Matthias

    2016-05-01

    Purpose of this in vitro study was to evaluate the effect of surface modifications on the tensile bond strength between zirconia ceramic and resin. Zirconia ceramic surfaces were treated with 150-μm abrasive alumina particles, 150-μm abrasive zirconia particles, argon-ion bombardment, gas plasma, and piranha solution (H2SO4:H2O2=3:1). In addition, slip casting surfaces were examined. Untreated surfaces were used as the control group. Tensile bond strengths (TBS) were measured after water storage for 3 days or 150 days with additional 37,500 thermal cycling for artificial aging. Statistical analyses were performed with 1-way and 3-way ANOVA, followed by comparison of means with the Tukey HSD test. After storage in distilled water for three days at 37 °C, the highest mean tensile bond strengths (TBS) were observed for zirconia ceramic surfaces abraded with 150-μm abrasive alumina particles (TBS(AAP)=37.3 MPa, TBS(CAAP)=40.4 MPa), and 150-μm abrasive zirconia particles (TBS(AZP)=34.8 MPa, TBS(CAZP)=35.8 MPa). Also a high TBS was observed for specimens treated with argon-ion bombardment (TBS(BAI)=37.8 MPa). After 150 days of storage, specimens abraded with 150-μm abrasive alumina particles and 150-μm abrasive zirconia particles revealed high TBS (TBS(AAP)=37.6 MPa, TBS(CAAP)=33.0 MPa, TBS(AZP)=22.1 MPa and TBS(CAZP)=22.8 MPa). A high TBS was observed also for specimens prepared with slip casting (TBS(SC)=30.0 MPa). A decrease of TBS was observed for control specimens (TBS(UNT)=12.5 MPa, TBS(CUNT)=9.0 MPa), specimens treated with argon-ion bombardment (TBS(BAI)=10.3 MPa) and gas plasma (TBS(GP)=11.0 MPa). A decrease of TBS was observed also for specimens treated with piranha solution (TBS(PS)=3.9 MPa, TBS(CPS)=4.1 MPa). A significant difference in TBS after three days storage was observed for specimens treated with different methods (p0.05), CAAP(p>0.05) and SC(p>0.05). However, the failure patterns of debonded specimens prepared with 150-μm abrasive zirconia

  17. Surface Processing and Modification of Polymers by Water Cluster Ion Beam

    Science.gov (United States)

    Ryuto, H.; Takeuchi, M.; Ichihashi, G.; Sommani, P.; Takaoka, G. H.

    2011-01-01

    A water cluster ion beam was irradiated on a poly(methyl methacrylate) (PMMA) surface to examine the possibility of applying the water cluster ion beam technique to the surface processing and modification of polymers. The sputtering yields of PMMA substrates irradiated with water cluster ion beams increased with acceleration voltage and dose of the water cluster ion beam. The threshold acceleration voltage of sputtering was approximately 3 kV. The X-ray photoelectron spectroscopy (XPS) analysis of the PMMA surface irradiated with the water cluster ion beam suggested the degradation of the PMMA side chains. The XPS spectrum of the surface of the sputtered particle catcher at 45° backward direction showed approximately the same shape as the XPS spectrum of the PMMA surface irradiated with the water cluster ion beam.

  18. Surface modification and effects of organic ferroelectrics with blending hyperbranched polymer

    Science.gov (United States)

    Morimoto, Masahiro; Ito, Genta; Koshiba, Yasuko; Ishida, Kenji

    2018-03-01

    The surface modification of ferroelectric films is expected to improve the properties of fatigue, which is important for application in memory devices. In this study, we fabricated thin insulators at an electrode-ferroelectric interface by the phase separation of a ferroelectric polymer and an insulator. The surface and bulk characterization indicated that the insulators consisting of a hyperbranched polymer spontaneously phase-separated from the organic ferroelectric polymer by thermal annealing. It was revealed that the separated layers were composed of three layers and had a lower surface energy than the ferroelectric films. The annealing time evolution of the surface contact angle and dielectric spectra indicated the phase separation dynamics and structural behavior. The fatigue properties of the surface-modified ferroelectric films improved, but the remanent polarization and coercive electric field value resulted in a trade-off.

  19. Effect of Surface Modifications on the Retention of Cement-retained Implant Crowns under Fatigue Loads: An In vitro Study

    Science.gov (United States)

    Ajay, R.; Suma, K.; Ali, Seyed Asharaf; Kumar Sivakumar, Jambai Sampath; Rakshagan, V.; Devaki, V.; Divya, K.

    2017-01-01

    Background: Masticatory forces cause fatigue to the dental luting agents, adversely affecting the retention of these cement-retained crowns. Sandblasting (SB) and diamond abrading the abutment surface improves the bond strength of luting agents. However, the effect of acid etching (AE) on the implant abutment surface and the effect of other surface modifications under masticatory load are yet to be documented. Purpose: The aim of the study was to evaluate the effect of abutment surface modifications on the retention of cement-retained restorations subjected to cyclic fatigue loads. Materials and Methods: Forty Ni-Cr copings were made on Cp-titanium laboratory analogs. The specimens were divided into two groups as Group I: Uniaxial tensile loading (UTL) and Group II: Offaxial cyclic loading followed by uniaxial tensile loading [CTL]. Further subgrouped as, subgroup I: Control (C), subgroup II: SB, subgroup III: AE, and subgroup IV: SB + AE. The copings were luted with Zn2(PO4)3 and subjected to uniaxial tensile loading. Copings were recemented, and CTL was conducted. Two-way analysis of variance was used as the statistical test of significance. Results: In relation to the subgroups, the bond strength of Zn2(PO4)3 was higher in Group I than in Group II. The bond strength in subgroup IV was superior in both Group I and Group II (547.170 N ± 5.752 and 531.975 N ± 6.221 respectively). Conclusions: For both UTL and CTL, abutment SB + AE elicited maximum coping retention followed by AE. Off-axial cyclic loading adversely affected the retention irrespective of the surface modifications. PMID:29284956

  20. Surface modification of polytetrafluoroethylene film using the atmospheric pressure glow discharge in air

    International Nuclear Information System (INIS)

    Fang, Z; Qiu, Y; Luo, Y

    2003-01-01

    The atmospheric pressure glow discharge (APGD) is more promising in industrial applications compared with glow discharges in a gas other than air or in low-pressure air, which needs an expensive vacuum system. In this paper, the APGD and dielectric barrier discharge (DBD) are generated in atmospheric air using a power-frequency voltage source, and the transition from DBD to APGD is achieved by varying the electrode arrangement. The differences between their discharge characteristics are shown by measurement of their electrical discharge parameters and observation of light-emission phenomena. The effects of APGD and DBD on polytetrafluoroethylene (PTFE) surface modification are studied. The surface properties are characterized by contact angle measurement, x-ray photoelectron spectroscopy and scanning electron microscopy. It is found that the APGD and DBD treatments modify the PTFE surface in both morphology and composition. APGD is more effective in PTFE surface modification than DBD as it can modify the surface more uniformly, implant more oxygen atoms into the surface and make the contact angle decline to a lower level. The experimental results are discussed

  1. Surface modifications and Nano-composite coatings to improve the bonding strength of titanium-porcelain.

    Science.gov (United States)

    Guo, Litong; Chen, Xiaoyuan; Liu, Xuemei; Feng, Wei; Li, Baoe; Lin, Cheng; Tao, Xueyu; Qiang, Yinghuai

    2016-04-01

    Surface modifications of Ti and nano-composite coatings were employed to simultaneously improve the surface roughness, corrosion resistance and chemical bonding between porclain-Ti. The specimens were studied by field-emission scanning electron microscopy, surface roughness, differential scanning calorimetry, Fourier transform infrared spectroscopy, corrosion resistance and bonding strength tests. The SEM results showed that hybrid structures with micro-stripes, nano-pores and nano-protuberances were prepared by surface modification of Ti, which significantly enhanced the surface roughness and corrosion resistance of Ti. Porous nano-composite coatings were synthesized on Ti anodized with pre-treatment in 40% HF acid. TiO2 nanoparticles were added into the hybrid coating to increase the solid phase content of the sols and avoid the formation of microcracks. With the TiO2 content increasing from 45 wt% to 60 wt%, the quantities of the microcracks on the coating surface gradually decreased. The optimal TiO2 content for the nanocomposite coatings is 60 wt% in this research. Compared to the uncoated group, the bonding strength of the coated groups showed a bonding strength improvement of 23.96%. The cytotoxicity of the 4# coating group was ranked as zero, which corresponds to non-cytotoxicity. Copyright © 2015 Elsevier B.V. All rights reserved.

  2. Surface modification of coconut shell based activated carbon for the improvement of hydrophobic VOC removal.

    Science.gov (United States)

    Li, Lin; Liu, Suqin; Liu, Junxin

    2011-08-30

    In this study, coconut shell based carbons were chemically treated by ammonia, sodium hydroxide, nitric acid, sulphuric acid, and phosphoric acid to determine suitable modification for improving adsorption ability of hydrophobic volatile organic compounds (VOCs) on granular activated carbons (GAC). The saturated adsorption capacities of o-xylene, a hydrophobic volatile organic compound, were measured and adsorption effects of the original and modified activated carbons were compared. Results showed that GAC modified by alkalis had better o-xylene adsorption capacity. Uptake amount was enhanced by 26.5% and reduced by 21.6% after modification by NH(3)H(2)O and H(2)SO(4), respectively. Compared with the original, GAC modified by acid had less adsorption capacity. Both SEM/EDAX and BET were used to identify the structural characteristics of the tested GAC, while IR spectroscopy and Boehm's titration were applied to analysis the surface functional groups. Relationships between physicochemical characteristics of GAC and their adsorption performances demonstrated that o-xylene adsorption capacity was related to surface area, pore volume, and functional groups of the GAC surface. Removing surface oxygen groups, which constitute the source of surface acidity, and reducing hydrophilic carbon surface favors adsorption capacity of hydrophobic VOCs on carbons. The performances of modified GACs were also investigated in the purification of gases containing complex components (o-xylene and steam) in the stream. Copyright © 2011 Elsevier B.V. All rights reserved.

  3. Early interactions between leukocytes and three different potentially bioactive titanium surface modifications.

    Science.gov (United States)

    Arvidsson, Anna; Malmberg, Per; Kjellin, Per; Currie, Fredrik; Arvidsson, Martin; Franke Stenport, Victoria

    2011-05-01

    The aim of the present study was to compare the early interactions between leukocytes and three different surface modifications, suggested as bioactive. Blasted titanium discs were modified by alkali and heat treatment, sodium fluoride treatment, or hydroxyapatite coating. A number of these discs were also immersed in simulated body fluid (SBF) for a week, a treatment which yielded high levels of calcium and phosphate on each surface type. The specimens were exposed for human venous blood for 32 minutes and the respiratory burst response was measured in terms of reactive oxygen species with a luminometer, and coverage of viable cells with a fluorescence microscope after staining steps. The topography, morphology, and chemistry of the surfaces were evaluated with optical interferometry and scanning electron microscopy/energy dispersive X-ray analysis (SEM/EDX). A high respiratory burst response was found for HA coated titanium in comparison with the other surface groups (p burst response (p < 0.0005) and removed statistically significant differences between the surface groups. Thus, the results in the present study indicate that different titanium surface modifications influence the early inflammatory response differently, and that calcium phosphate compounds increase the inflammatory response. Copyright © 2011 Wiley Periodicals, Inc.

  4. Surface modification of RuO2 electrodes by laser irradiation and ion ...

    Indian Academy of Sciences (India)

    RuO2 thin layers were deposited on Ti supports by thermal decomposition of RuCl3 at 400°C. Some of the samples were subjected to laser irradiation between 0.5 and 1.5 J cm-2. Some others to Kr bombardment with doses between 1015 and 1016 cm-2. Modifications introduced by the surface treatments were monitored ...

  5. Surface Modification of Ferritic Stainless Steel by Active Screen Plasma Nitriding

    OpenAIRE

    NII, Hiroaki; NISHIMOTO, Akio

    2012-01-01

    Plasma nitriding is a surface modification process with a low environmental impact. Active screen plasma nitriding (ASPN) is one of the new plasma nitriding technologies, and can eliminate problems related to conventional direct current plasma nitriding (DCPN). In this study, ferritic stainless steel SUS430 samples were treated by ASPN to increase their wear resistance without decreasing their corrosion resistance. ASPN was performed in a nitrogen-hydrogen atmosphere with 25%N2 + 75%H2 for 18...

  6. Surface Modification of Nanoporous 1,2-Polybutadiene by Atom Transfer Radical Polymerization or Click Chemistry

    DEFF Research Database (Denmark)

    Guo, Fengxiao; Jankova Atanasova, Katja; Schulte, Lars

    2010-01-01

    Surface-initiated atom transfer radical polymerization (ATRP) and click chemistry were used to obtain functional nanoporous polymers based oil nanoporous 1,2-polybutadiene (PB) with gyroid morphology. The ATRP monolith initiator was prepared by immobilizing bromoester initiators onto the pore walls...... ATRP-grafting of hydrophilic polyacrylates and click of MPEG, the originally hydrophobic samples transformed into hydrophilic nanoporous materials. The successful modification was confirmed by infrared spectroscopy, contact angle measurements and measurements of spontaneous water uptake, while...

  7. Surface modification of polymers for biocompatibility via exposure to extreme ultraviolet radiation

    OpenAIRE

    Ahad, Inam Ul; Bartnik, Andrejz; Fiedorowicz, Henryk; Kostecki, Jerzy; Korkzyc, Barbara; Ciach, Tomasz; Brabazon, Dermot

    2013-01-01

    Polymeric biomaterials are being widely used for the treatment of various traumata, diseases and defects in human beings due to ease in their synthesis. As biomaterials have direct interaction with the extracellular environment in the biological world, biocompatibility is a topic of great significance. The introduction or enhancement of biocompatibility in certain polymers is still a challenge to overcome. Polymer biocompatibility can be controlled by surface modification. Various physical an...

  8. RTV silicone rubber surface modification for cell biocompatibility by negative-ion implantation

    Science.gov (United States)

    Zheng, Chenlong; Wang, Guangfu; Chu, Yingjie; Xu, Ya; Qiu, Menglin; Xu, Mi

    2016-03-01

    A negative cluster ion implantation system was built on the injector of a GIC4117 tandem accelerator. Next, the system was used to study the surface modification of room temperature vulcanization silicone rubber (RTV SR) for cell biocompatibility. The water contact angle was observed to decrease from 117.6° to 99.3° as the C1- implantation dose was increased to 1 × 1016 ions/cm2, and the effects of C1-, C2- and O1- implantation result in only small differences in the water contact angle at 3 × 1015 ions/cm2. These findings indicate that the hydrophilicity of RTV SR improves as the dose is increased and that the radiation effect has a greater influence than the doping effect on the hydrophilicity. There are two factors influence hydrophilicity of RTV: (1) based on the XPS and ATR-FTIR results, it can be inferred that ion implantation breaks the hydrophobic functional groups (Sisbnd CH3, Sisbnd Osbnd Si, Csbnd H) of RTV SR and generates hydrophilic functional groups (sbnd COOH, sbnd OH, Sisbnd (O)x (x = 3,4)). (2) SEM reveals that the implanted surface of RTV SR appears the micro roughness such as cracks and wrinkles. The hydrophilicity should be reduced due to the lotus effect (Zhou Rui et al., 2009). These two factors cancel each other out and make the C-implantation sample becomes more hydrophilic in general terms. Finally, cell culture demonstrates that negative ion-implantation is an effective method to improve the cell biocompatibility of RTV SR.

  9. Preparation and Surface Modification of Silica ‎Nanoparticles for Superhydrophopic Coating

    Directory of Open Access Journals (Sweden)

    Noor Hadi Aysa

    2017-12-01

    Full Text Available Silica  nanoparticles are well-known to be one of the multifunctional inorganic compounds which are widely used in medical applications. The aim of this study is to prepare the particles of nano silica oxide with particle size ranging from 20-25  nm. In the present study, surface modification of Silica nanoparticles was performed, and influence of modification on the structure and morphological properties was investigated. The resulting  nanoparticles were characterized by X-ray diffraction (XRD, scanning electron microscopy (SEM and atomic force microscopy (AFM.  Silica nanoparticles with the average diameter of about 20 nm were modified with oleic acid, as coupling agents, in order to modify their surface properties and make them more waterproof  dispersible in the organic area. Among the results is that the  surface modification of the   Silica nano-particles leads to more dispersion in the organic medium which indicates better organic synthesis.  One of the results obtained, is that modified silica-nanoparticles can be used effectively in environmental and safety applications and can be used in future medical applications as wound stick that prevent water from reaching the wound and then prevent  an inflamation

  10. Surface modification of cellulose isolated from Sesamun indicum underutilized seed: A means of enhancing cellulose hydrophobicity

    Directory of Open Access Journals (Sweden)

    Adewale Adewuyi

    2017-09-01

    Full Text Available Cellulose (SC isolated from sesame seed (SS was surface modified with the introduction of an ester functional group via a simple reaction to produce the modified product (SA. SS, SC and SA were characterized using Fourier transform infrared (FTIR, X-ray diffraction (XRD, thermogravimetric analysis (TG, particle size distribution (PSD, zeta potential and scanning electron microscopy (SEM. SC and SA were evaluated for their water holding capacity (WC, oil holding capacity (OC, swelling capacity (SW and their ability to adsorb heavy metals. The FTIR revealed peaks corresponding to the formation of the ester functional group at the surface of SA. The crystallinity of SC was 28.02% but after the modification, it increased to 77.03% in SA. The PSD of SC and SA was both monomodal with sizes of 10.1305 μm in SC and 10.2511 μm in SA. The adsorption capacity of SC towards Pb (II and Cu (II ions was higher than that of SA. However, SA was unable to adsorb Cu (II ions. SA exhibited the lower WC and SW values as compared to SC which suggested an improved hydrophobicity after the modification. This study has shown that hydrophobicity can be improved in cellulose via surface modification.

  11. Plasma-Assisted Synthesis and Surface Modification of Electrode Materials for Renewable Energy.

    Science.gov (United States)

    Dou, Shuo; Tao, Li; Wang, Ruilun; El Hankari, Samir; Chen, Ru; Wang, Shuangyin

    2018-02-14

    Renewable energy technology has been considered as a "MUST" option to lower the use of fossil fuels for industry and daily life. Designing critical and sophisticated materials is of great importance in order to realize high-performance energy technology. Typically, efficient synthesis and soft surface modification of nanomaterials are important for energy technology. Therefore, there are increasing demands on the rational design of efficient electrocatalysts or electrode materials, which are the key for scalable and practical electrochemical energy devices. Nevertheless, the development of versatile and cheap strategies is one of the main challenges to achieve the aforementioned goals. Accordingly, plasma technology has recently appeared as an extremely promising alternative for the synthesis and surface modification of nanomaterials for electrochemical devices. Here, the recent progress on the development of nonthermal plasma technology is highlighted for the synthesis and surface modification of advanced electrode materials for renewable energy technology including electrocatalysts for fuel cells, water splitting, metal-air batteries, and electrode materials for batteries and supercapacitors, etc. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  12. Drag reduction in reservoir rock surface: Hydrophobic modification by SiO{sub 2} nanofluids

    Energy Technology Data Exchange (ETDEWEB)

    Yan, Yong-Li, E-mail: yylhill@163.com [College of Chemistry & Chemical Engineering, Xi’an Shiyou University, Xi’an 710065 (China); Cui, Ming-Yue; Jiang, Wei-Dong; He, An-Le; Liang, Chong [Langfang Branch of Research Institute of Petroleum Exploration & Development, Langfang 065007 (China)

    2017-02-28

    Graphical abstract: The micro-nanoscale hierarchical structures at the sandstone core surface are constructed by adsorption of the modified silica nanoparticles, which leads to the effect of drag reduction to improve the low injection rate in ultra-low permeability reservoirs. - Highlights: • A micro-nanoscale hierarchical structure is formed at the reservoir rock surface. • An inversion has happened from hydrophilic into hydrophobic modified by nanofluids. • The effect of drag reduction to improve the low injection rate is realized. • The mechanism of drag reduction induced from the modified core surface was unclosed. - Abstract: Based on the adsorption behavior of modified silica nanoparticles in the sandstone core surface, the hydrophobic surface was constructed, which consists of micro-nanoscale hierarchical structure. This modified core surface presents a property of drag reduction and meets the challenge of high injection pressure and low injection rate in low or ultra-low permeability reservoir. The modification effects on the surface of silica nanoparticles and reservoir cores, mainly concerning hydrophobicity and fine structure, were determined by measurements of contact angle and scanning electron microscopy. Experimental results indicate that after successful modification, the contact angle of silica nanoparticles varies from 19.5° to 141.7°, exhibiting remarkable hydrophobic properties. These modified hydrophobic silica nanoparticles display a good adsorption behavior at the core surface to form micro-nanobinary structure. As for the wettability of these modified core surfaces, a reversal has happened from hydrophilic into hydrophobic and its contact angle increases from 59.1° to 105.9°. The core displacement experiments show that the relative permeability for water has significantly increased by an average of 40.3% via core surface modification, with the effects of reducing injection pressure and improving injection performance of water

  13. Drag reduction in reservoir rock surface: Hydrophobic modification by SiO2 nanofluids

    International Nuclear Information System (INIS)

    Yan, Yong-Li; Cui, Ming-Yue; Jiang, Wei-Dong; He, An-Le; Liang, Chong

    2017-01-01

    Graphical abstract: The micro-nanoscale hierarchical structures at the sandstone core surface are constructed by adsorption of the modified silica nanoparticles, which leads to the effect of drag reduction to improve the low injection rate in ultra-low permeability reservoirs. - Highlights: • A micro-nanoscale hierarchical structure is formed at the reservoir rock surface. • An inversion has happened from hydrophilic into hydrophobic modified by nanofluids. • The effect of drag reduction to improve the low injection rate is realized. • The mechanism of drag reduction induced from the modified core surface was unclosed. - Abstract: Based on the adsorption behavior of modified silica nanoparticles in the sandstone core surface, the hydrophobic surface was constructed, which consists of micro-nanoscale hierarchical structure. This modified core surface presents a property of drag reduction and meets the challenge of high injection pressure and low injection rate in low or ultra-low permeability reservoir. The modification effects on the surface of silica nanoparticles and reservoir cores, mainly concerning hydrophobicity and fine structure, were determined by measurements of contact angle and scanning electron microscopy. Experimental results indicate that after successful modification, the contact angle of silica nanoparticles varies from 19.5° to 141.7°, exhibiting remarkable hydrophobic properties. These modified hydrophobic silica nanoparticles display a good adsorption behavior at the core surface to form micro-nanobinary structure. As for the wettability of these modified core surfaces, a reversal has happened from hydrophilic into hydrophobic and its contact angle increases from 59.1° to 105.9°. The core displacement experiments show that the relative permeability for water has significantly increased by an average of 40.3% via core surface modification, with the effects of reducing injection pressure and improving injection performance of water

  14. A new green methodology for surface modification of diatomite filler in elastomers

    Energy Technology Data Exchange (ETDEWEB)

    Lamastra, F.R. [Italian Interuniversity Consortium on Materials Science and Technology (INSTM), Research Unit Roma Tor Vergata, Via del Politecnico 1, 00133, Rome (Italy); Mori, S.; Cherubini, V. [Italian Interuniversity Consortium on Materials Science and Technology (INSTM), Research Unit Roma Tor Vergata, Via del Politecnico 1, 00133, Rome (Italy); Department of Enterprise Engineering, University of Rome ' Tor Vergata' , Via del Politecnico 1, 00133, Rome (Italy); Scarselli, M. [Department of Physics, University of Rome ' Tor Vergata' , Via della Ricerca Scientifica 1, 00133, Rome (Italy); Nanni, F., E-mail: fnanni@ing.uniroma2.it [Italian Interuniversity Consortium on Materials Science and Technology (INSTM), Research Unit Roma Tor Vergata, Via del Politecnico 1, 00133, Rome (Italy); Department of Enterprise Engineering, University of Rome ' Tor Vergata' , Via del Politecnico 1, 00133, Rome (Italy)

    2017-06-15

    In this work a new, simple and green protocol to introduce a limited content of silanol groups on the surface of an hydrophobic diatomite, in order to be slightly hydrophilic and susceptible to be silanized by bifunctional, sulfur-containing organosilanes for rubber applications, is proposed. The chemical modification was carried out at 85 °C in a solution of H{sub 2}O:NaOH:H{sub 2}O{sub 2}. The modified diatomite was then silanized with bis(triethoxysilylpropyl) disulfide by a procedure that does not involve toxic solvent. Morphological features and elemental composition of diatomite were investigated by Field emission scanning electron microscopy coupled with Energy dispersive X-ray spectroscopy. The surface modification and silanization process were assessed by Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy. Diatomite was composed by micrometric frustules from different diatom species with pore size ranging from 25 nm to 1 μm. The spectroscopic characterizations confirmed the surface modification of diatomite with some silanols that acted as sites for silanization reaction. The silanized diatomite and the untreated one were used as filler in unvulcanized solvent-cast SBR films in order to verify that the modification does not negatively affect the polymer/filler interface and as consequence the mechanical properties. Mechanical properties of the realized samples were assessed by uniaxial tensile tests. Films filled with 10 wt% of diatomite (untreated or silanized) showed an increase of Elastic Modulus about of 50% and a decrease of the strain at break with respect to SBR samples, while the tensile strength was not significantly affected by the diatomite addition. SEM images of fracture surfaces of tested specimens showed a fine dispersion of both untreated and silanized diatomite in the polymeric matrix and the achieving of a good interfacial adhesion SBR/fillers. The silanized diatomite, as it is potentially able to bind

  15. Novel method for chemical modification and patterning of the SU-8 photoresist

    DEFF Research Database (Denmark)

    Blagoi, Gabriela; Keller, Stephan Urs; Boisen, Anja

    2007-01-01

    the wetting behaviour of SU-8. The resolution limit of the AQ photopatterning method was 20 μm when using an uncollimated light source. AQ modification followed by a reaction with amino groups of Alexa-647 cadaverine and a Biotin-amino derivative proved possible modification and patterning of polymeric...

  16. Surface modification of polyester fabric with plasma pretreatment and carbon nanotube coating for antistatic property improvement

    Energy Technology Data Exchange (ETDEWEB)

    Wang, C.X., E-mail: cxwang@mail.dhu.edu.cn [College of Textiles and Clothing, Yancheng Institute of Technology, Jiangsu 224051 (China); Collaborative Innovation Center for Ecological Building Materials and Environmental Protection Equipments, Jiangsu 224051 (China); Key Laboratory for Advanced Technology in Environmental Protection, Jiangsu 224051 (China); Lv, J.C. [College of Textiles and Clothing, Yancheng Institute of Technology, Jiangsu 224051 (China); Ren, Y. [School of Textile and Clothing, Nantong University, Jiangsu 226019 (China); Zhi, T.; Chen, J.Y.; Zhou, Q.Q. [College of Textiles and Clothing, Yancheng Institute of Technology, Jiangsu 224051 (China); Lu, Z.Q.; Gao, D.W. [College of Textiles and Clothing, Yancheng Institute of Technology, Jiangsu 224051 (China); Collaborative Innovation Center for Ecological Building Materials and Environmental Protection Equipments, Jiangsu 224051 (China); Key Laboratory for Advanced Technology in Environmental Protection, Jiangsu 224051 (China); Jin, L.M. [Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201204 (China)

    2015-12-30

    Graphical abstract: - Highlights: • PET was finished by plasma treatment and SWCNT coating to improve antistatic property. • Plasma modification had a positive effect on SWCNT coating on PET fiber surface. • O{sub 2} plasma was more effective in SWCNT coating than Ar plasma in the shorter time. • Antistatic enhanced and then declined with enhancing treatment time and output power. • Antistatic increased with increasing concentration, curing time, curing temperature. - Abstract: This study introduced a green method to prepare antistatic polyester (PET) fabrics by plasma pretreatment and single-walled carbon nanotube (SWCNT) coating. The influences of plasma conditions and SWCNT coating parameters on antistatic property of PET fabrics were investigated. PET fabrics were pretreated under various plasma conditions such as different treatment times, output powers and working gases, and then SWCNT coating on the plasma treated PET fabrics was carried out by coating-dry-cure using various coating parameters including different SWCNT concentrations, curing times and curing temperatures. PET fabrics were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and volume resistivity. SEM and XPS analysis of the plasma treated PET fabrics revealed the increase in surface roughness and oxygen/nitrogen containing groups on the PET fiber surface. SEM and XPS analysis of the plasma treated and SWCNT coated PET fabrics indicated the SWCNT coating on PET fiber surface. The plasma treated and SWCNT coated PET fabrics exhibited a good antistatic property, which increased and then decreased with the increasing plasma treatment time and output power. The antistatic property of the O{sub 2} plasma treated and SWCNT coated PET fabric was better and worse than that of N{sub 2} or Ar plasma treated and SWCNT coated PET fabric in the shorter treatment time and the longer treatment time, respectively. In addition, the antistatic property of the

  17. Surface modification of polyester fabric with plasma pretreatment and carbon nanotube coating for antistatic property improvement

    International Nuclear Information System (INIS)

    Wang, C.X.; Lv, J.C.; Ren, Y.; Zhi, T.; Chen, J.Y.; Zhou, Q.Q.; Lu, Z.Q.; Gao, D.W.; Jin, L.M.

    2015-01-01

    Graphical abstract: - Highlights: • PET was finished by plasma treatment and SWCNT coating to improve antistatic property. • Plasma modification had a positive effect on SWCNT coating on PET fiber surface. • O 2 plasma was more effective in SWCNT coating than Ar plasma in the shorter time. • Antistatic enhanced and then declined with enhancing treatment time and output power. • Antistatic increased with increasing concentration, curing time, curing temperature. - Abstract: This study introduced a green method to prepare antistatic polyester (PET) fabrics by plasma pretreatment and single-walled carbon nanotube (SWCNT) coating. The influences of plasma conditions and SWCNT coating parameters on antistatic property of PET fabrics were investigated. PET fabrics were pretreated under various plasma conditions such as different treatment times, output powers and working gases, and then SWCNT coating on the plasma treated PET fabrics was carried out by coating-dry-cure using various coating parameters including different SWCNT concentrations, curing times and curing temperatures. PET fabrics were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and volume resistivity. SEM and XPS analysis of the plasma treated PET fabrics revealed the increase in surface roughness and oxygen/nitrogen containing groups on the PET fiber surface. SEM and XPS analysis of the plasma treated and SWCNT coated PET fabrics indicated the SWCNT coating on PET fiber surface. The plasma treated and SWCNT coated PET fabrics exhibited a good antistatic property, which increased and then decreased with the increasing plasma treatment time and output power. The antistatic property of the O 2 plasma treated and SWCNT coated PET fabric was better and worse than that of N 2 or Ar plasma treated and SWCNT coated PET fabric in the shorter treatment time and the longer treatment time, respectively. In addition, the antistatic property of the plasma treated

  18. Surface modification of PDMS microfluidic devices by controlled sulfuric acid treatment and the application in chip electrophoresis.

    Science.gov (United States)

    Gitlin, Leonid; Schulze, Philipp; Ohla, Stefan; Bongard, Hans-Josef; Belder, Detlev

    2015-02-01

    Herein, we present a straightforward surface modification technique for PDMS-based microfluidic devices. The method takes advantage of the high reactivity of concentrated sulfuric acid to enhance the surface properties of PDMS bulk material. This results in alteration of the surface morphology and chemical composition that is in-depth characterized by ATR-FTIR, EDX, SEM, and XPS. In comparison to untreated PDMS, modified substrates exhibit a significantly reduced diffusive uptake of small organic molecules while retaining its low electroosmotic properties. This was demonstrated by exposing the channels of a microfluidic device to concentrated rhodamine B solution followed by fluorescence microscopy. The surface modification procedure was used to improve chip-based electrophoretic separations. Separation efficiencies of FITC-labeled amines/amino acids obtained in treated and untreated PDMS-devices as well as in glass chips were compared. We obtained higher efficiencies in H2 SO4 treated PDMS chips compared to untreated ones but lower efficiencies than those obtained in commercial microfluidic glass devices. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  19. ZnS quantum dots and their derivatives: Overview on identity, synthesis and challenge into surface modifications for restricted applications

    Directory of Open Access Journals (Sweden)

    Houcine Labiadh

    2017-10-01

    Full Text Available Among different inert materials, quantum dots have been qualified by their fashion proprieties especially those related to structure and sizes. This review talks about the structural identity and some relevant methods to synthesize quantum dots, there is a challenge in the adaptation of nanoparticles to fulfill the biological, chemical and physical applications which demonstrate the crucial role of the surface. Modifications of the surface, cross stepwise the electronic transition layers of the particles, contribute to the functionalization in order to incorporate atoms in the main structure or immobilize small molecules onto the surface which lead to a restricted application. Finally, quantum dots are revealed to be an attractive material that can be a support for large potential applications in the future.

  20. Modifications of the hydriding kinetics of a metallic surface, using ion implantation

    International Nuclear Information System (INIS)

    Crusset, D.

    1992-10-01

    Uranium reacts with hydrogen to form an hydride: this reaction leads to the total destruction of the material. To modify the reactivity of an uranium surface towards hydrogen, ion implantation was selected, among surface treatments techniques. Four elements (carbon, nitrogen, oxygen, sulfur) were implanted to different doses. The results show a modification of the hydriding mechanism and a significant increase in the reaction induction times, notably at high implantation doses. Several techniques (SIMS, X-rays phases analysis and residual stresses determination) were used to characterize the samples and understand the different mechanisms involved

  1. Surface modification of tooth root canal after application of an X-ray opaque waveguide

    Science.gov (United States)

    Dostálová, T.; Jelínková, H.; Šulc, J.; Němec, M.; Koranda, P.; Bartoňová, M.; Radina, P.; Miyagi, M.; Shi, Y.-W.; Matsuura, Y.

    The interest in endodontic use of dental laser systems has been increasing. With the development of thin and flexible delivery systems for various wavelengths, laser applications in endodontics may become even more desirable. The aim of this study is to check the X-ray opacity of a hollow waveguide and to observe the results after laser root canal treatment. The root canal systems of 10 molars were treated endodontically by laser. For the laser radiation source, an Er:YAG laser system generating a wavelength of 2940 nm and an Alexandrite laser system generating a wavelength of 375 nm were used. The hollow waveguide used was checked under X-ray . A root canal surface treated by laser radiation was analyzed by a scanning electron microscope (SEM). The special hollow glass waveguide used was visible in the root canal system under X-ray imaging. Surface modification of the root canal after laser treatment was not found. After conventional treatment the root canal was enlarged. The surface was covered with a smear layer. After application of both laser systems, the smear layer was removed. The resulting canal surface was found to be clean and smooth. Under SEM observation open dentinal tubules were visible. No cracks were present, nor were surface modifications observed.

  2. Physical and chemical modifications of PET surface using a laser-plasma EUV source

    Science.gov (United States)

    Bartnik, A.; Fiedorowicz, H.; Jarocki, R.; Kostecki, J.; Szczurek, M.; Biliński, A.; Chernyayeva, O.; Sobczak, J. W.

    2010-06-01

    Extreme ultraviolet (EUV) radiation is the electromagnetic radiation ranging from vacuum ultraviolet to soft X-rays. A single EUV photon carries enough energy to ionize any atom or molecule. The penetration depth of the radiation in any material is very short, ranging from tens to hundreds nanometers. Intense EUV pulses can remove material from the surface or modify its morphology or/and chemical structure. In this work, the radiation from a laser-plasma EUV source based on a double-stream gas-puff target was used for surface modification of polyethylene terephthalate (PET). The PET samples were irradiated with the EUV pulses emitted from krypton plasma and focused with a gold-plated ellipsoidal collector. The spectrum of the focused radiation covered the wavelength range from 9 to 70 nm. The PET samples were irradiated for 1 s-2 min at a 10-Hz repetition rate. Surface morphology of polymer samples after irradiation was investigated using a scanning electron microscope. Changes in chemical surface structure of the irradiated samples were investigated using an X-ray photoelectron spectroscopy. Different kinds of surface microstructures were obtained depending on the EUV fluence in a single pulse and the total EUV fluence. XPS measurements also revealed a modification of the chemical structure.

  3. Low energy oxygen ion beam modification of the surface morphology and chemical structure of polyurethane fibers

    International Nuclear Information System (INIS)

    Wong, K.H.; Zinke-Allmang, M.; Wan, W.K.; Zhang, J.Z.; Hu, P.

    2006-01-01

    Energetic O + ions were implanted into polyurethane (PU) fiber filaments, at 60 and 100 keV with doses of 5 x 10 14 and 1 x 10 15 ions/cm 2 , to modify the near-surface fiber morphology. The implantations were performed at room temperature and at -197 deg. C, a temperature well below the glass transition temperature for this system. At room temperature, the lower energy implantation heats the fibers primarily near their surface, causing the fiber surface to smoothen and to develop a flattened shape. At the higher energy, the ion beam deposits its energy closer to the fiber core, heating the fiber more uniformly and causing them to re-solidify slowly. This favors a cylindrical equilibrium shape with a smooth fiber surface and no crack lines. The average fiber diameter reduced during 100 keV implantation from 3.1 to 2.3 μm. At -197 deg. C, the ion implantation does not provide enough heat to cause notable physical modifications, but the fibers crack and break during subsequent warming to room temperature. The dose dependence of the crack formation along the fiber intersections is presented. The ion beams further cause near-surface chemical modifications in the fibers, particularly introducing two new chemical functional groups (C-(C=O)-C and C-N-C)

  4. Modification of titanium alloys surface properties by plasma electrolytic oxidation (PEO) and influence on biological response.

    Science.gov (United States)

    Echeverry-Rendón, Mónica; Galvis, Oscar; Aguirre, Robinson; Robledo, Sara; Castaño, Juan Guillermo; Echeverría, Félix

    2017-09-27

    Surface characteristics can mediate biological interaction improving or affecting the tissue integration after implantation of a biomaterial. Features such as topography, wettability, surface energy and chemistry can be key determinants for interactions between cells and materials. Plasma electrolytic oxidation (PEO) is a technique used to control this kind of parameters by the addition of chemical species and the production of different morphologies on the surfaces of titanium and its alloys. With the purpose to improve the biological response, surfaces of c.p titanium and Ti6Al4V were modified by using PEO. Different electrolytes, voltages, current densities and anodizing times were tested in order to obtain surfaces with different characteristics. The obtained materials were characterized by different techniques such as X-ray diffraction (XRD), scanning electron microscopy (SEM) and glow discharge optical emission spectroscopy (GDOES). Wettability of the obtained surfaces were measured and the corresponding surface energies were calculated. Superhydrophilic surfaces with contact angles of about 0 degrees were obtained without any other treatment but PEO and this condition in some cases remains stable after several weeks of anodizing; crystal phase composition (anatase-rutile) of the anodic surface appears to be critical for obtaining this property. Finally, in order to verify the biological effect of these surfaces, osteoblast were seeded on the samples. It was found that cell behavior improves as SFE (surface free energy) and coating porosity increases whereas it is affected negatively by roughness. Techniques for surface modification allow changes in the coatings such as surface energy, roughness and porosity. As a consequence of this, biological response can be altered. In this paper, surfaces of c.p Ti and Ti6Al4V were modified by using plasma electrolytic oxidation (PEO) in order to accelerate the cell adhesion process.

  5. Application of a novel atmospheric pressure plasma fluidized bed in the powder surface modification

    International Nuclear Information System (INIS)

    Chen Guangliang; Chen Shihua; Zhou Mingyan; Feng Wenran; Gu Weichao; Yang Size

    2006-01-01

    A novel atmospheric pressure plasma fluidized bed (APPFB) with one liquid electrode was designed, and its preliminary discharge characteristics were studied. The glow discharge in the APPFB was generated by applying a low power with helium (He) gas, and the plasma gas temperature was no higher than 320 K when the applied power was lower than 11 W. The plasma optical emission spectrum (OES) of the gas mixture consisting of He and hexamethyldisiloxane (HMDSO) was recorded by a UV-visible monochromator. The calcium carbonate powders were modified by APPFB using HMDSO in the He plasma. The powder surface energy was decreased greatly by coating an organosilicon polymer onto the powder surface. This surface modification process changed the wettability of the powder from super-hydrophilicity to super-hydrophobicity, and the contact angle of water on the modified powders surface was greater than 160 0

  6. Study on surface modification of polymer films by using atmospheric plasma jet source

    International Nuclear Information System (INIS)

    Takemura, Yuichiro; Hara, Tamio; Yamaguchi, Naohiro

    2008-01-01

    Reactive gas plasma treatments of poly(ethylene terephthalate) (PET) and polyimide (Kapton) have been performed using an atmospheric plasmas jet source. Characteristics of surface modification have been examined by changing the distance between the plasma jet source and the treated sample, and by changing the working gas spaces. Simultaneously, each plasma jet source has been investigated by space-resolving spectroscopy in the UV/visible region. Polymer surfaces have been analyzed by X-ray photoelectron spectroscopy (XPS). A marked improvement in the hydrophilicity of the polymer surfaces has been made by using N 2 or O 2 plasma jet source with a very short exposure time of about 0.01 s, whereas the less improvement has been obtained using on air plasma jet source because of NO x compound production. Changes in the chemical states of C of the polymer surfaces have been observed in XPS spectra after N 2 plasma jet spraying. (author)

  7. Plasma modification of polypropylene surfaces and its alloying with styrene in situ

    International Nuclear Information System (INIS)

    Ma Guiqiu; Liu Ben; Li Chen; Huang Dinghai; Sheng Jing

    2012-01-01

    The treatment of polypropylene surfaces has been studied by dielectric barrier discharges plasma of Ar. The structure and morphology of polypropylene surfaces of Ar plasma modification are characterized by X-ray photoelectron spectroscopy, Fourier transform infrared spectrometers and scanning electron microscope. The modified by plasma treatment of iPP (isotactic polypropylene) surface properties have been examined in a determination of free radicals. The modified active surfaces of polypropylene can induce grafting copolymerization of styrene onto polypropylene. The structure of grafting copolymer is characterized and the grafting percent of styrene onto polypropylene is calculated. The homopolymer of styrene can be formed under grafting copolymerization of styrene onto polypropylene, which follows that the alloying of polypropylene with styrene is achieved in situ.

  8. Plasma modification of polypropylene surfaces and its alloying with styrene in situ

    Energy Technology Data Exchange (ETDEWEB)

    Ma Guiqiu, E-mail: magq@tju.edu.cn [School of Materials Science and Engineering, Tianjin Key Laboratory of Composite and Functional Materials, Tianjin University, Tianjin, 300072 (China); Liu Ben; Li Chen; Huang Dinghai; Sheng Jing [School of Materials Science and Engineering, Tianjin Key Laboratory of Composite and Functional Materials, Tianjin University, Tianjin, 300072 (China)

    2012-01-15

    The treatment of polypropylene surfaces has been studied by dielectric barrier discharges plasma of Ar. The structure and morphology of polypropylene surfaces of Ar plasma modification are characterized by X-ray photoelectron spectroscopy, Fourier transform infrared spectrometers and scanning electron microscope. The modified by plasma treatment of iPP (isotactic polypropylene) surface properties have been examined in a determination of free radicals. The modified active surfaces of polypropylene can induce grafting copolymerization of styrene onto polypropylene. The structure of grafting copolymer is characterized and the grafting percent of styrene onto polypropylene is calculated. The homopolymer of styrene can be formed under grafting copolymerization of styrene onto polypropylene, which follows that the alloying of polypropylene with styrene is achieved in situ.

  9. Surface modification of layered zirconium phosphates: a novel pathway to multifunctional materials.

    Science.gov (United States)

    Mosby, Brian M; Díaz, Agustín; Clearfield, Abraham

    2014-07-21

    The intercalation of inorganic layered materials has resulted in a wide range of applicability. In such cases the applicability of the material is largely dependent upon the species intercalated within the layer, and the layered material acts largely as a host. Recently, the surface modification of inorganic layered materials has been investigated and it has been shown that the exterior layers can be exclusively functionalized. The advent of surface chemistry allows for the synthesis of particles with both a controlled interlayer and surface. This approach can be used to tailor nanoparticles for specific applications. Herein we review the surface chemistry of α-zirconium bis(monohydrogen orthophosphate) monohydrate (Zr(HPO4)2·H2O, α-ZrP) along with some applications of recent interest. Not only can these reactions be applied to α-ZrP, but similar chemistry can also be expanded to other layered materials and systems.

  10. Highly stable surface modification of hypercrosslinked monolithic capillary columns and their application in hydrophilic interaction chromatography.

    Science.gov (United States)

    Škeříková, Veronika; Urban, Jiří

    2013-09-01

    A two-step surface modification of poly(styrene-co-vinylbenzyl chloride-co-divinylbenzene) monolithic stationary phases, including hypercrosslinking and thermally initiated surface grafting of [2-(methacryloyloxy)ethyl]dimethyl(3-sulfopropyl)ammonium hydroxide, has been used to prepare capillary columns for the isocratic separation of small polar compounds in hydrophilic interaction chromatography (HILIC). The prepared monolithic columns provided a dual retention mechanism, combining RP and hydrophilic interaction chromatography, controlled by the composition of the mobile phase. By the optimization of the surface grafting reaction using response surface methodology, we have found that the grafting time is the main synergistic effect controlling the retention of polar compounds in HILIC. The prepared monolithic columns achieved long column lifetimes and did not lose their separation power following >10,000 injections. Finally, hypercrosslinked columns have been used in the 1- and 2D LC of phenolic compounds. © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  11. Surface modification of polysulfone membranes applied for a membrane reactor with immobilized alcohol dehydrogenase

    DEFF Research Database (Denmark)

    Hoffmann, Christian; Silau, Harald; Pinelo, Manuel

    2018-01-01

    Commercially available polysulfone (PSf) membranes with a polypropylene backing are used across a broad range of applications. However, the natural properties of the PSf surface sometimes limit their application. Here we present, how the surface of supported membranes can be heterogeneously...... activated by lithiation followed by functionalization with acid chlorides at 0 °C, permitting modification of commercial PSf membranes without compromising the mechanical integrity of the membrane. Post-functionalization polymer grafting was illustrated through both, a “grafting from” approach by surface...... initiated atom transfer radical polymerization (SI-ATRP) and by a “grafting to” approach exploiting Cu(I) catalyzed 1,3-cycloadditions of alkynes with azides (CuAAC) introducing hydrophilic polymers onto the membrane surface. Poly(1-vinyl imidazole) (pVim) grafted membranes were exploited as support...

  12. Surface Modification of C3N4through Oxygen-Plasma Treatment: A Simple Way toward Excellent Hydrophilicity.

    Science.gov (United States)

    Bu, Xiuming; Li, Jipeng; Yang, Siwei; Sun, Jing; Deng, Yuan; Yang, Yucheng; Wang, Gang; Peng, Zheng; He, Peng; Wang, Xianying; Ding, Guqiao; Yang, Junhe; Xie, Xiaoming

    2016-11-16

    We developed a universal method to prepare hydrophilic carbon nitrogen (C 3 N 4 ) nanosheets. By treating C 3 N 4 nanosheets with oxygen plasma, hydroxylamine groups (N-OH) with intense protonation could be introduced on the surface; moreover, the content of N-OH groups increased linearly with the oxygen-plasma treatment time. Thanks to the excellent hydrophilicity, uniformly dispersed C 3 N 4 solution were prepared, which was further translated into C 3 N 4 paper by simple vacuum filtration. Pure C 3 N 4 paper with good stability, excellent hydrophilicity, and biocompatibility were proved to have excellent performance in tissue repair. Further research demonstrated that the oxygen-plasma treatment method can also introduce N-OH groups into other nitrogen-containing carbon materials (NCMs) such as N-doped graphene, N-doped carbon nanotube, and C 2 N, which offers a new perspective on the surface modification and functionalization of these carbon nanomaterials.

  13. METHODS TO DEVELOP A TOROIDAL SURFACE

    Directory of Open Access Journals (Sweden)

    DANAILA Ligia

    2017-05-01

    Full Text Available The paper work presents two practical methods to draw the development of a surface unable to be developed applying classical methods of Descriptive Geometry, the toroidal surface, frequently met in technical practice. The described methods are approximate ones; the development is obtained with the help of points. The accuracy of the methods is given by the number of points used when drawing. As for any other approximate method, when practically manufactured the development may need to be adjusted on site.

  14. Enhanced osteointegration of medical titanium implant with surface modifications in micro/nanoscale structures

    Directory of Open Access Journals (Sweden)

    Liwen Lin

    2014-01-01

    Full Text Available Biomimetic design and substrate-based surface modification of medical implants will help to improve the integration of tissue to its material interfaces. Surface energy, composition, roughness, and topography all influence the biological responses of the implants, such as protein adsorption and cell adhesion, proliferation and differentiation. In the current study, different surface structures of Ti implants were constructed using facile surface techniques to create various micro-, nano-, and nano/micro composite scale topography. We have fabricated three types of hierarchical structures of TiO2 coating on Ti implants, including nanotube structure, nano sponge-like structure, and nano/micro nest-like structure. The osteointegration and biomechanical performance of the coated Ti screws were evaluated by histology and removal of torque force test in vivo. We found that the nano/micro nest-like and nanotube structured surface possessed better osteointegration ability. It indicated that the alkaline hydrothermally treated Ti substrate was the best for bone-implant integration in terms of all in vitro and in vivo testing parameters. The alkaline hydrothermally treated surface displayed a hydrophilic (contact angle value 5.92 ± 1.2, higher roughness (Ra value 911.3 ± 33.8 nm, higher specific surface area (8.26 ± 1.051 m2/g, and greater apatite inductivity. The electrochemical surface modification may become a powerful approach to enhance metal implant to bone integration in orthopaedic applications.

  15. Kinetics of ultraviolet and plasma surface modification of poly(dimethylsiloxane) probed by sum frequency vibrational spectroscopy.

    Science.gov (United States)

    Ye, Hongke; Gu, Zhiyong; Gracias, David H

    2006-02-14

    In numerous applications in microfluidics, cell growth, soft lithography, and molecular imprinting, the surface of poly(dimethylsiloxane) (PDMS) is modified from a hydrophobic methyl-terminated surface to a hydrophilic hydroxyl-terminated surface. In this study, we investigated molecular structural and orientational changes at the PDMS-air interface in response to three commonly used surface modification processes: exposure to long-wavelength ultraviolet light (UV), exposure to short-wavelength UV that generates ozone (UVO), and exposure to oxygen plasma (OP). The surfaces of two PDMS compositions (10:1 and 4:1 of base polymer/curing agent) were probed during modification, using monolayer-sensitive IR + visible sum frequency generation (SFG) vibrational spectroscopy, with two different polarization combinations. During PDMS surface modification, the peak intensities of CH3 side groups and CH2 cross-link groups decreased, while peak intensities of Si-OH groups increased. There was no significant change in the average orientation of the CH3 groups on the PDMS surface during modification. The concentration of CH3 groups on the surface decreased exponentially with time, for all three UV, UVO, and OP modification processes, with first order kinetics and time constants of approximately 160, 66, and 0.3 min, respectively. At steady state, residual CH3 groups were detected at the PDMS surface for UV and UVO treatments; however, there were negligible CH3 groups detected after OP modification.

  16. Laser surface modification of Yttria Stabilized Zirconia (YSZ) thermal barrier coating on AISI H13 tool steel substrate

    Science.gov (United States)

    Reza, M. S.; Aqida, S. N.; Ismail, I.

    2018-03-01

    This paper presents laser surface modification of plasma sprayed yttria stabilized zirconia (YSZ) coating to seal porosity defect. Laser surface modification on plasma sprayed YSZ was conducted using 300W JK300HPS Nd: YAG laser at different operating parameters. Parameters varied were laser power and pulse frequency with constant residence time. The coating thickness was measured using IM7000 inverted optical microscope and surface roughness was analysed using two-dimensional Mitutoyo Surface Roughness Tester. Surface roughness of laser surface modification of YSZ H-13 tool steel decreased significantly with increasing laser power and decreasing pulse frequency. The re-melted YSZ coating showed higher hardness properties compared to as-sprayed coating surface. These findings were significant to enhance thermal barrier coating surface integrity for dies in semi-solid processing.

  17. Surface modification of hydroxyapatite with poly(methyl methacrylate) via surface-initiated ATRP

    International Nuclear Information System (INIS)

    Wang Yan; Zhang Xi; Yan Jinliang; Xiao Yan; Lang Meidong

    2011-01-01

    This article describes the fabrication of hydroxyapatite (HAP) nanocomposites grafted with poly(methyl methacrylate) (PMMA). Surface-initiated atom transfer radical polymerization (ATRP) of methyl methacrylate (MMA) was carried out from hydroxyapatite particles derivatized with ATRP initiators. The structure and properties of the nanocomposites were investigated by thermogravimetric analysis (TGA), transmission electron microscopy (TEM), differential scanning calorimeter (DSC) measurements, and contact angle analyses. TGA was used to estimate the grafting density of ATRP initiators (0.49 initiator/nm 2 ) and the amount of grafted PMMA on the HAP surface. The contact angle analyses indicated that grafting PMMA onto the HAP surface dramatically increased the hydrophobicity of the surface. Moreover, the HAP nanocomposites showed excellent dispersibility in both aqueous solution and organic solvent.

  18. Organoselenium Surface Modification of Stainless Steel Surfaces To Prevent Biofouling in Treatment of Space Wastestreams Project

    Data.gov (United States)

    National Aeronautics and Space Administration — The objective of this work is to quantify the reduction of biofilm formation in a water distribution system resulting from an organoselenium surface coating on...

  19. Surface modification of hydroxyapatite with poly(methyl methacrylate) via surface-initiated ATRP

    Energy Technology Data Exchange (ETDEWEB)

    Wang Yan; Zhang Xi; Yan Jinliang; Xiao Yan [Shanghai Key Laboratory of Advanced Polymeric Materials, Key Laboratory for Ultrafine Materials of Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, 130 Meilong Road, Shanghai 200237 (China); Lang Meidong, E-mail: mdlang@ecust.edu.cn [Shanghai Key Laboratory of Advanced Polymeric Materials, Key Laboratory for Ultrafine Materials of Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, 130 Meilong Road, Shanghai 200237 (China)

    2011-05-01

    This article describes the fabrication of hydroxyapatite (HAP) nanocomposites grafted with poly(methyl methacrylate) (PMMA). Surface-initiated atom transfer radical polymerization (ATRP) of methyl methacrylate (MMA) was carried out from hydroxyapatite particles derivatized with ATRP initiators. The structure and properties of the nanocomposites were investigated by thermogravimetric analysis (TGA), transmission electron microscopy (TEM), differential scanning calorimeter (DSC) measurements, and contact angle analyses. TGA was used to estimate the grafting density of ATRP initiators (0.49 initiator/nm{sup 2}) and the amount of grafted PMMA on the HAP surface. The contact angle analyses indicated that grafting PMMA onto the HAP surface dramatically increased the hydrophobicity of the surface. Moreover, the HAP nanocomposites showed excellent dispersibility in both aqueous solution and organic solvent.

  20. A combination of CO2 laser and plasma surface modification of poly(etheretherketone) to enhance osteoblast response

    Science.gov (United States)

    Zheng, Yanyan; Xiong, Chengdong; Wang, Zhecun; Li, Xiaoyu; Zhang, Lifang

    2015-07-01

    Poly(etheretherketone) (PEEK) is a rigid semicrystalline polymer that combines excellent mechanical properties, broad chemical resistance and bone-like stiffness and is widely used in biomedical fields. However, the bio-inert surface of PEEK tends to hinder its biomedical applications when direct osteointegration between the implants and the host tissue is desired. In this work, we demonstrate a dual modification method, which combines the laser and plasma surface treatment to combine advantages of both chemical states and microstructures for osteoblasts responses. While the plasma treatment introduces surface carboxyl groups (sbnd COOH) onto PEEK surface, the laser treatment constructs microstructures over the PEEK surface. Our results indicated that sbnd COOH as well as microgrooves containing micropores or microcraters structure are constructed on PEEK surface and plasma treatment has no apparent effect on the morphology of microstructures produced by laser micromachining. Unexpectedly, the superior mechanical properties of PEEK were maintained irrespective of the treatment used. Compared to native PEEK and single treated PEEK, dual modified PEEK is more favorable for pre-osteoblasts (MC3T3-E1) adhesion, spreading and proliferation. Moreover, cell pseudopodia protrude into the micropores or microcraters, in favor of forming firmer bone-implant integration. Our study illustrates enhanced osteoblasts responses to dual treated PEEK surface, which gives beneficial information of its potential use in orthopedic or dental implants.

  1. RTV silicone rubber surface modification for cell biocompatibility by negative-ion implantation

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, Chenlong [Key Laboratory of Beam Technology and Material Modification Ministry of Education, College of Nuclear Science and Technology, Beijing Normal University, 100875 Beijing (China); Wang, Guangfu, E-mail: 88088@bnu.edu.cn [Key Laboratory of Beam Technology and Material Modification Ministry of Education, College of Nuclear Science and Technology, Beijing Normal University, 100875 Beijing (China); Beijing Radiation Center, 100875 Beijing (China); Chu, Yingjie; Xu, Ya; Qiu, Menglin; Xu, Mi [Key Laboratory of Beam Technology and Material Modification Ministry of Education, College of Nuclear Science and Technology, Beijing Normal University, 100875 Beijing (China)

    2016-03-01

    Highlights: • The radiation effect has a greater influence than doping effect on the hydrophilicity of RTV SR. • The implanted ions result in a new surface atomic bonding state and morphology. • Generating hydrophilic functional groups is a reason for the improved cell biocompatibility. • The micro roughness makes the hydrophilicity should be reduced due to the lotus effect. • Cell culture demonstrates that negative-ion implantation can improve biocompatibility. - Abstract: A negative cluster ion implantation system was built on the injector of a GIC4117 tandem accelerator. Next, the system was used to study the surface modification of room temperature vulcanization silicone rubber (RTV SR) for cell biocompatibility. The water contact angle was observed to decrease from 117.6° to 99.3° as the C{sub 1}{sup −} implantation dose was increased to 1 × 10{sup 16} ions/cm{sup 2}, and the effects of C{sub 1}{sup −}, C{sub 2}{sup −} and O{sub 1}{sup −} implantation result in only small differences in the water contact angle at 3 × 10{sup 15} ions/cm{sup 2}. These findings indicate that the hydrophilicity of RTV SR improves as the dose is increased and that the radiation effect has a greater influence than the doping effect on the hydrophilicity. There are two factors influence hydrophilicity of RTV: (1) based on the XPS and ATR-FTIR results, it can be inferred that ion implantation breaks the hydrophobic functional groups (Si−CH{sub 3}, Si−O−Si, C−H) of RTV SR and generates hydrophilic functional groups (−COOH, −OH, Si−(O){sub x} (x = 3,4)). (2) SEM reveals that the implanted surface of RTV SR appears the micro roughness such as cracks and wrinkles. The hydrophilicity should be reduced due to the lotus effect (Zhou Rui et al., 2009). These two factors cancel each other out and make the C-implantation sample becomes more hydrophilic in general terms. Finally, cell culture demonstrates that negative ion-implantation is an effective method

  2. Effect of Surface Modification by Oleic Acid on Physical Properties of Cellulose Nanofibers

    Directory of Open Access Journals (Sweden)

    Hadi Almasi

    2013-08-01

    Full Text Available Oleic acid was used as a hydrophobic agent to modify cellulose nanofiber (CNF and the reaction time and fatty acid content were tested in relation to the hydrophilic properties of the products as well as the physicochemical properties of CNF. It was found that the degree of substitution (DS increased by extending the reaction time though the fatty acid content had no effect on hydrophobicity of CNF. The success of the esterification reaction was confirmed by Fourier transform infrared spectroscopy. Higher degree of substitution led to increased contact angle of CNF surfaces with water, which indicated the increased surface hydrophobicity of modified CNF. The X-ray diffraction analyses showed a lowering trend in crystallinity index and crystallite size with increases in DS value. Surface modification changed the thermal stability of CNF by lowering the degradation temperature from 290.8°C for unmodified cellulose to 195.4°C for highly esterified cellulose. Scanning electron microscopy micrographs revealed that after esterification of CNF with oleic acid, its filamentous shape was preserved. As a result, although the surface modification of CNF by fatty acid increased its hydrophobicity and its ability to mix with non-polar polymers, but it changed CNF physicochemical characteristics and weakened its functional properties.

  3. Microwave-assisted surface modification of metallocene polyethylene for improving blood compatibility.

    Science.gov (United States)

    Mohandas, Hemanth; Sivakumar, Gunalan; Kasi, Palaniappan; Jaganathan, Saravana Kumar; Supriyanto, Eko

    2013-01-01

    A wide number of polymers are being used for various medical applications. In this work, microwave-assisted surface modification of metallocene polyethylene (mPE) was studied. FTIR analysis showed no significant changes in the chemical groups after treatment. Contact angle analysis revealed a decrease in contact angle of the treated samples insinuating increasing hydrophilicity and better biocompatibility. Qualitative analysis of treated samples using scanning electron microscope (SEM) depicted increasing surface roughness and holes formation further corroborating the results. Coagulation assays performed for estimating prothrombin time (PT) and activated partial thromboplastin time (APTT) showed an increase in the clotting time which further confirmed the improved blood compatibility of the microwave-treated surfaces. Further, the extent of hemolysis in the treated sample was lower than the untreated one. Hence, microwave-assisted surface modification of mPE resulted in enhanced blood compatibility. Improved blood compatibility of mPE may be exploited for fabrication of artificial vascular prostheses, implants, and various blood contacting devices.

  4. Microwave-Assisted Surface Modification of Metallocene Polyethylene for Improving Blood Compatibility

    Directory of Open Access Journals (Sweden)

    Hemanth Mohandas

    2013-01-01

    Full Text Available A wide number of polymers are being used for various medical applications. In this work, microwave-assisted surface modification of metallocene polyethylene (mPE was studied. FTIR analysis showed no significant changes in the chemical groups after treatment. Contact angle analysis revealed a decrease in contact angle of the treated samples insinuating increasing hydrophilicity and better biocompatibility. Qualitative analysis of treated samples using scanning electron microscope (SEM depicted increasing surface roughness and holes formation further corroborating the results. Coagulation assays performed for estimating prothrombin time (PT and activated partial thromboplastin time (APTT showed an increase in the clotting time which further confirmed the improved blood compatibility of the microwave-treated surfaces. Further, the extent of hemolysis in the treated sample was lower than the untreated one. Hence, microwave-assisted surface modification of mPE resulted in enhanced blood compatibility. Improved blood compatibility of mPE may be exploited for fabrication of artificial vascular prostheses, implants, and various blood contacting devices.

  5. Silane surface modification effects on the electromagnetic properties of phosphatized iron-based SMCs

    Science.gov (United States)

    Fan, Liang-Fang; Hsiang, Hsing-I.; Hung, Jia-Jing

    2018-03-01

    It is difficult to achieve homogeneous phosphatized iron powder dispersion in organic resins during the preparation of soft magnetic composites (SMCs). Inhomogeneous iron powder mixing in organic resins generally leads to the formation of micro-structural defects in SMCs and hence causes the magnetic properties to become worse. Phosphatized iron powder dispersion in organic resins can be improved by coating the phosphatized iron powder surfaces with a coupling agent. This study investigated the (3-aminopropyl) triethoxysilane (APTES) surface modification effects on the electromagnetic properties of phosphatized iron-based soft magnetic composites (SMCs). The results showed that the phosphatized iron powder surface can be modified using APTES to improve the phosphatized iron powder and epoxy resin compatibility and hence enhance phosphate iron powder epoxy mixing. The tensile strength, initial permeability, rated current under DC-bias superposition and magnetic loss in SMCs prepared using phosphatized iron powders can be effectively improved using APTES surface modification, which provides a promising candidate for power chip inductor applications.

  6. Tuning the Photocatalytic Activity of Graphitic Carbon Nitride by Plasma-Based Surface Modification.

    Science.gov (United States)

    Ji, Xueqiang; Yuan, Xiaohong; Wu, Jiajie; Yu, Lan; Guo, Huiyun; Wang, Hannian; Zhang, Haiquan; Yu, Dongli; Zhao, Yuanchun

    2017-07-26

    In this study, we demonstrate that plasma treatment can be a facile and environmentally friendly approach to perform surface modification of graphitic carbon nitride (g-CN), leading to a remarkable modulation on its photocatalytic activity. The bulk properties of g-CN, including the particle size, structure, composition, and electronic band structures, have no changes after being treated by oxygen or nitrogen plasma; however, its surface composition and specific surface area exhibit remarkable differences corresponding to an oxygen functionalization induced by the plasma post-treatment. The introduced oxygen functional groups play a key role in reducing the recombination rate of the photoexcited charge carries. As a consequence, the oxygen-plasma-treated sample shows a much superior photocatalytic activity, which is about 4.2 times higher than that of the pristine g-CN for the degradation of rhodamine B (RhB) under visible light irradiation, while the activity of nitrogen-plasma-treated sample exhibits a slight decrease. Furthermore, both of the plasma-treated samples are found to possess impressive photocatalytic stabilities. Our results suggest that plasma treatment could be a conventional strategy to perform surface modification of g-CN in forms of both powders and thin films, which holds broad interest not only for developing g-CN-based high-performance photocatalysts but also for constructing photoelectrochemical cells and photoelectronic devices with improved energy conversion efficiencies.

  7. Surface modification and stability of detonation nanodiamonds in microwave gas discharge plasma

    International Nuclear Information System (INIS)

    Stanishevsky, Andrei V.; Walock, Michael J.; Catledge, Shane A.

    2015-01-01

    Graphical abstract: - Highlights: • Single and binary gas plasma modification of nanodiamond powders studied. • Temperature-dependent effect of N 2 and N 2 /H 2 plasma reported for the first time. • Role of H 2 in H 2 /N 2 and H 2 /O 2 plasma modification of nanodiamond discussed. - Abstract: Detonation nanodiamonds (DND), with low hydrogen content, were exposed to microwave plasma generated in pure H 2 , N 2 , and O 2 gases and their mixtures, and investigated using X-ray diffraction (XRD), Fourier Transform Infrared (FTIR), Raman, and X-ray photoelectron spectroscopies. Considerable alteration of the DND surface was observed under the plasma conditions for all used gases, but the diamond structure of the DND particle core was preserved in most cases. The stabilizing effect of H 2 in H 2 /N 2 and H 2 /O 2 binary gas plasmas on the DND structure and the temperature-dependent formation of various CNH x surface groups in N 2 and H 2 /N 2 plasmas were observed and discussed for the first time. DND surface oxidation and etching were the main effects of O 2 plasma, whereas the N 2 plasma led to DND surfaces rich in amide groups below 1073 K and nitrile groups at higher temperatures. Noticeable graphitization of the DND core structure was detected only in N 2 plasma when the substrate temperature was above 1103 K.

  8. Surface modification of an experimental silicone rubber aimed at reducing initial candidal adhesion.

    Science.gov (United States)

    Price, C; Waters, M G J; Williams, D W; Lewis, M A O; Stickler, D

    2002-01-01

    Silicone rubber, which is a widely used biomaterial, is often used to make soft liners for permanent denture. Colonization of denture soft lining materials by Candida albicans can result in clinical problems. The aim of this study was to chemically modify the surface of an experimental silicone rubber in order to produce a silicone that was less susceptible to candidal colonization. Surface modification was carried out with the use of argon-plasma bombardment followed by silane treatment, which caused the incorporation of either hydrophilic or hydrophobic functional groups onto the surface. Changes in water contact angles and chemical analysis of the materials with scanning ion mass spectroscopy confirmed surface changes. In vitro assays were carried out using C. albicans to measure levels of adherence to the surface-modified silicone after 1 h. C. albicans exhibited very low adherence to all silane-treated surfaces, whether hydrophobic or hydrophilic. This led to the conclusion that incorporated long-chain functional groups were inhibiting the adherence of the yeast, possibly by the formation of a barrier between the surface of the material and the yeast. In conclusion, silane surface treatment of an experimental silicone rubber has been successful in reducing candidal adherence. Copyright 2002 Wiley Periodicals, Inc. J Biomed Mater Res (Appl Biomater) 63: 122--128, 2002; DOI 10.1002/jbm.10094

  9. Surface Modification of MXenes: A Pathway to Improve MXene Electrode Performance in Electrochemical Energy Storage Devices

    KAUST Repository

    Ahmed, Bilal

    2017-12-31

    The recent discovery of layered transition metal carbides (MXenes) is one of the most important developments in two-dimensional (2D) materials. Preliminary theoretical and experimental studies suggest a wide range of potential applications for MXenes. The MXenes are prepared by chemically etching ‘A’-layer element from layered ternary metal carbides, nitrides and carbonitrides (MAX phases) through aqueous acid treatment, which results in various surface terminations such as hydroxyl, oxygen or fluorine. It has been found that surface terminations play a critical role in defining MXene properties and affects MXene performance in different applications such as electrochemical energy storage, electromagnetic interference shielding, water purification, sensors and catalysis. Also, the electronic, thermoelectric, structural, plasmonic and optical properties of MXenes largely depend upon surface terminations. Thus, controlling the surface chemistry if MXenes can be an efficient way to improve their properties. This research mainly aims to perform surface modifications of two commonly studied MXenes; Ti2C and Ti3C2, via chemical, thermal or physical processes to enhance electrochemical energy storage properties. The as-prepared and surface modified MXenes have been studied as electrode materials in Li-ion batteries (LIBs) and supercapacitors (SCs). In pursuit of desirable MXene surface, we have developed an in-situ room temperature oxidation process, which resulted in TiO2/MXene nanocomposite and enhanced Li-ion storage. The idea of making metal oxide and MXene nanocomposites was taken to the next level by combining a high capacity anode materials – SnO2 – and MXene. By taking advantage of already existing surface functional groups (–OH), we have developed a composite of SnO2/MXene by atomic layer deposition (ALD) which showed enhanced capacity and excellent cyclic stability. Thermal annealing of MXene at elevated temperature under different atmospheres was

  10. Amino-functionalized surface modification of polyacrylonitrile hollow fiber-supported polydimethylsiloxane membranes

    Energy Technology Data Exchange (ETDEWEB)

    Hu, Leiqing; Cheng, Jun, E-mail: juncheng@zju.edu.cn; Li, Yannan; Liu, Jianzhong; Zhou, Junhu; Cen, Kefa

    2017-08-15

    Highlights: • Amino group was introduced to improve surface polarity of PDMS membrane. • The water contact angle of PDMS membrane decreased after the modification. • The concentration of N atom on surface of PDMS membrane reached up to ∼6%. • The density of PDMS membrane decreased while the swelling degree increased. • CO{sub 2} permeability increased while selectivity decreased after the modification. - Abstract: This study aimed to improve surface polarity of polydimethylsiloxane (PDMS) membranes and provide surface active sites which were easy to react with other chemicals. 3-Aminopropyltriethoxysilane (APTES) containing an amino group was introduced into a PDMS membrane by crosslinking to prepare polyacrylonitrile hollow fiber-supported PDMS membranes with an amino-functionalized surface. Fourier transform infrared and X-ray photoelectron spectroscopic analyses proved the existence of APTES and its amino group in the PDMS membrane. The concentration of N atoms on the PDMS membrane surface reached ∼6% when the mass ratio of APTES/PDMS oligomer in the PDMS coating solution was increased to 4/3. The water contact angle decreased from ∼114° to ∼87.5°, indicating the improved surface polarization of the PDMS membrane. The density and swelling degree of the PDMS membrane decreased and increased, respectively, with increasing APTES content in PDMS. This phenomenon increased CO{sub 2} permeability and decreased CO{sub 2}/H{sub 2} selectivity, CO{sub 2}/CH{sub 4} selectivity, and CO{sub 2}/N{sub 2} selectivity. When the mass ratio of APTES/PDMS oligomer was increased from 0 to 4/3, the CO{sub 2} permeation rate of the hollow fiber-supported PDMS membranes initially decreased from ∼2370 GPU to ∼860 GPU and then increased to ∼2000 GPU due to the change in coating solution viscosity.

  11. Amino-functionalized surface modification of polyacrylonitrile hollow fiber-supported polydimethylsiloxane membranes

    International Nuclear Information System (INIS)

    Hu, Leiqing; Cheng, Jun; Li, Yannan; Liu, Jianzhong; Zhou, Junhu; Cen, Kefa

    2017-01-01

    Highlights: • Amino group was introduced to improve surface polarity of PDMS membrane. • The water contact angle of PDMS membrane decreased after the modification. • The concentration of N atom on surface of PDMS membrane reached up to ∼6%. • The density of PDMS membrane decreased while the swelling degree increased. • CO 2 permeability increased while selectivity decreased after the modification. - Abstract: This study aimed to improve surface polarity of polydimethylsiloxane (PDMS) membranes and provide surface active sites which were easy to react with other chemicals. 3-Aminopropyltriethoxysilane (APTES) containing an amino group was introduced into a PDMS membrane by crosslinking to prepare polyacrylonitrile hollow fiber-supported PDMS membranes with an amino-functionalized surface. Fourier transform infrared and X-ray photoelectron spectroscopic analyses proved the existence of APTES and its amino group in the PDMS membrane. The concentration of N atoms on the PDMS membrane surface reached ∼6% when the mass ratio of APTES/PDMS oligomer in the PDMS coating solution was increased to 4/3. The water contact angle decreased from ∼114° to ∼87.5°, indicating the improved surface polarization of the PDMS membrane. The density and swelling degree of the PDMS membrane decreased and increased, respectively, with increasing APTES content in PDMS. This phenomenon increased CO 2 permeability and decreased CO 2 /H 2 selectivity, CO 2 /CH 4 selectivity, and CO 2 /N 2 selectivity. When the mass ratio of APTES/PDMS oligomer was increased from 0 to 4/3, the CO 2 permeation rate of the hollow fiber-supported PDMS membranes initially decreased from ∼2370 GPU to ∼860 GPU and then increased to ∼2000 GPU due to the change in coating solution viscosity.

  12. Design and development of anisotropic inorganic/polystyrene nanocomposites by surface modification of zinc oxide nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Han, Xiao [School of Materials Science and Engineering, Tongji University, Shanghai 200092 (China); Research Center for Translational Medicine, East Hospital, the Institute for Biomedical Engineering & Nano Science, Tongji University School of Medicine, Shanghai 200092 (China); Huang, Shiming [Department of Physics, Tongji University, Shanghai 200092 (China); Wang, Yilong, E-mail: yilongwang@tongji.edu.cn [Research Center for Translational Medicine, East Hospital, the Institute for Biomedical Engineering & Nano Science, Tongji University School of Medicine, Shanghai 200092 (China); Shi, Donglu, E-mail: shid@ucmail.uc.edu [Research Center for Translational Medicine, East Hospital, the Institute for Biomedical Engineering & Nano Science, Tongji University School of Medicine, Shanghai 200092 (China); The Materials Science and Engineering Program, College of Engineering and Applied Science, University of Cincinnati, Cincinnati, OH 45221 (United States)

    2016-07-01

    Anisotropic yolk/shell or Janus inorganic/polystyrene nanocomposites were prepared by combining miniemulsion polymerization and sol–gel reaction. The morphologies of the anisotropic composites were found to be greatly influenced by surface modification of zinc oxide (ZnO) nanoparticle seeds. Two different types of the oleic acid modified ZnO nanoparticles (OA-ZnO) were prepared by post-treatment of commercial ZnO powder and homemade OA-ZnO nanoparticles. The morphologies and properties of the nanocomposites were investigated by transmission electron microscope (TEM), thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FT-IR), dynamic light scattering (DLS), and energy dispersive X-ray spectroscopy (EDX). It was found that both post-treated OA-ZnO and in-situ prepared OA-ZnO nanoparticles resulted in the yolk–shell and Janus structure nanocomposites, but with varied size and morphology. These nanocomposites showed stable and strong fluorescence by introducing quantum dots as the co-seeds. The fluorescent anisotropic nanocomposites were decorated separately with surface carboxyl and hydroxyl groups. These composites with unique anisotropic properties will have high potential in biomedical applications, particularly in bio-detection. - Graphical abstract: Design and development of anisotropic inorganic/polystyrene nanocomposites by surface modification of zinc oxide nanoparticles. - Highlights: • Non-magnetic anisotropic yolk/shell or Janus nanocomposites are prepared and characterized. • Different surface modification of zinc oxide (ZnO) nanoparticles results in varied morphology and size of the final product. • Fluorescent anisotropic nanocomposites embodying quantum dots are an ideal candidate for bio-detection applications.

  13. Evaluation of Surface Modification as a Lunar Dust Mitigation Strategy for Thermal Control Surfaces

    Science.gov (United States)

    Gaier, James R.; Waters, Deborah L.; Misconin, Robert M.; Banks, Bruce A.; Crowder, Mark

    2011-01-01

    Three surface treatments were evaluated for their ability to lower the adhesion between lunar simulant dust and AZ93, AlFEP, and AgFEP thermal control surfaces under simulated lunar conditions. Samples were dusted in situ and exposed to a standardized puff of nitrogen gas. Thermal performance before dusting, after dusting, and after part of the dust was removed by the puff of gas, were compared to perform the assessment. None of the surface treatments was found to significantly affect the adhesion of lunar simulants to AZ93 thermal control paint. Oxygen ion beam texturing also did not lower the adhesion of lunar simulant dust to AlFEP or AgFEP. But a workfunction matching coating and a proprietary Ball Aerospace surface treatment were both found to significantly lower the adhesion of lunar simulants to AlFEP and AgFEP. Based on these results, it is recommended that all these two techniques be further explored as dust mitigation coatings for AlFEP and AgFEP thermal control surfaces.

  14. Development of a High Efficiency Dry Powder Inhaler: Effects of Capsule Chamber Design and Inhaler Surface Modifications

    Science.gov (United States)

    Behara, Srinivas R.B.; Farkas, Dale R.; Hindle, Michael; Longest, P. Worth

    2013-01-01

    Purpose The objective of this study was to explore the performance of a high efficiency dry powder inhaler (DPI) intended for excipient enhanced growth (EEG) aerosol delivery based on changes to the capsule orientation and surface modifications of the capsule and device. Methods DPIs were constructed by combining newly designed capsule chambers (CC) with a previously developed three-dimensional (3D) rod array for particle deagglomeration and a previously optimized EEG formulation. The new CCs oriented the capsule perpendicular to the incoming airflow and were analyzed for different air inlets at a constant pressure drop across the device. Modifications to the inhaler and capsule surfaces included use of metal dispersion rods and surface coatings. Aerosolization performance of the new DPIs was evaluated and compared with commercial devices. Results The proposed capsule orientation and motion pattern increased capsule vibrational frequency and reduced the aerosol MMAD compared with commercial/modified DPIs. The use of metal rods in the 3D array further improved inhaler performance. Coating the inhaler and capsule with PTFE significantly increased emitted dose (ED) from the optimized DPI. Conclusions High efficiency performance is achieved for EEG delivery with the optimized DPI device and formulation combination producing an aerosol with MMAD 90%, and ED > 80%. PMID:23949304

  15. Degradation of the electrospun silica nanofiber in a biological medium for primary hippocampal neuron – effect of surface modification

    Directory of Open Access Journals (Sweden)

    Feng ZV

    2016-02-01

    Full Text Available Z Vivian Feng,1,* Wen Shuo Chen,2,* Khomson Keratithamkul,1 Michael Stoick,1 Brittany Kapala,3 Eryn Johnson,3 An-Chi Huang,2 Ting Yu Chin,4 Yui Whei Chen-Yang,2 Mong-Lin Yang3 1Chemistry Department, Augsburg College, Minneapolis, MN, USA; 2Department of Chemistry, Center for Nanotechnology, Center for Biomedical Technology, Chung Yuan Christian University, Chung Li, Taiwan, Republic of China; 3Department of Science, Concordia University Saint Paul, Saint Paul, MN, USA; 4Department of Bioscience Technology, Chung Yuan Christian University, Chung Li, Taiwan, Republic of China *These authors contributed equally to this work Abstract: In this work, silica nanofibers (SNFs were prepared by an electrospinning method and modified with poly-D-lysine (PDL or (3-aminopropyl trimethoxysilane (APTS making biocompatible and degradable substrates for neuronal growth. The as-prepared SNF, modified SNF-PDL, and SNF-APTS were evaluated using scanning electron microscopy, nitrogen adsorption/desorption isotherms, contact angle measurements, and inductively coupled plasma atomic emission spectroscopy. Herein, the scanning electron microscopic images revealed that dissolution occurred in a corrosion-like manner by enlarging porous structures, which led to loss of structural integrity. In addition, covalently modified SNF-APTS with more hydrophobic surfaces and smaller surface areas resulted in significantly slower dissolution compared to SNF and physically modified SNF-PDL, revealing that different surface modifications can be used to tune the dissolution rate. Growth of primary hippocampal neuron on all substrates led to a slower dissolution rate. The three-dimensional SNF with larger surface area and higher surface density of the amino group promoted better cell attachment and resulted in an increased neurite density. This is the first known work addressing the degradability of SNF substrate in physiological conditions with neuron growth in vitro, suggesting a

  16. PREFACE Surface Modifications of Diamond and Related Materials (Session D, E-MRS Spring Meeting)

    Science.gov (United States)

    Nebel, Christoph E.

    2010-11-01

    This special issue contains selected papers which were presented at the E-MRS Symposium BIOMATERIALS, SENSORS & SURFACES, D: 'Surface modifications of diamond and related materials' which was held on 7-9 June 2010 in Strasbourg (France). With about 54 oral and poster presentations given from teams all over the world it was a very interesting, dense and lively meeting. The symposium focused on chemical modifications applied to graft surfaces of diamond,