  1. Sol-gel precursors and products thereof

    Science.gov (United States)

    Warren, Scott C.; DiSalvo, Jr., Francis J.; Weisner, Ulrich B.

    2017-02-14

    The present invention provides a generalizable single-source sol-gel precursor capable of introducing a wide range of functionalities to metal oxides such as silica. The sol-gel precursor facilitates a one-molecule, one-step approach to the synthesis of metal-silica hybrids with combinations of biological, catalytic, magnetic, and optical functionalities. The single-source precursor also provides a flexible route for simultaneously incorporating functional species of many different types. The ligands employed for functionalizing the metal oxides are derived from a library of amino acids, hydroxy acids, or peptides and a silicon alkoxide, allowing many biological functionalities to be built into silica hybrids. The ligands can coordinate with a wide range of metals via a carboxylic acid, thereby allowing direct incorporation of inorganic functionalities from across the periodic table. Using the single-source precursor a wide range of functionalized nanostructures such as monolith structures, mesostructures, multiple metal gradient mesostructures and Stober-type nanoparticles can be synthesized. ##STR00001##

  2. Sol-gel processing with inorganic metal salt precursors

    Science.gov (United States)

    Hu, Zhong-Cheng

    2004-10-19

    Methods for sol-gel processing that generally involve mixing together an inorganic metal salt, water, and a water miscible alcohol or other organic solvent, at room temperature with a macromolecular dispersant material, such as hydroxypropyl cellulose (HPC) added. The resulting homogenous solution is incubated at a desired temperature and time to result in a desired product. The methods enable production of high quality sols and gels at lower temperatures than standard methods. The methods enable production of nanosize sols from inorganic metal salts. The methods offer sol-gel processing from inorganic metal salts.

  3. Synthesis of Sol-Gel Precursors for Ceramics from Lunar and Martian Soil Simulars

    Science.gov (United States)

    Sibille, L.; Gavira-Gallardo, J. A.; Hourlier-Bahloul, D.

    2004-01-01

    Recent NASA mission plans for the human exploration of our Solar System has set new priorities for research and development of technologies necessary to enable a long-term human presence on the Moon and Mars. The recovery and processing of metals and oxides from mineral sources on other planets is under study to enable use of ceramics, glasses and metals by explorer outposts. We report initial results on the production of sol-gel precursors for ceramic products using mineral resources available in martian or lunar soil. The presence of SO2, TiO2, and Al2O3 in both martian (44 wt.% SiO2, 1 wt.% TiO2, 7 wt.% Al2O3) and lunar (48 wt.% SiO2, 1.5 wt.% TiO2, 16 wt.% Al2O3) soils and the recent developments in chemical processes to solubilize silicates using organic reagents and relatively little energy indicate that such an endeavor is possible. In order to eliminate the risks involved in the use of hydrofluoric acid to dissolve silicates, two distinct chemical routes are investigated to obtain soluble silicon oxide precursors from lunar and martian soil simulars. Clear solutions of sol-gel precursors have been obtained by dissolution of silica from lunar soil similar JSC-1 in basic ethylene glycol (C2H4(OH)2) solutions to form silicon glycolates. Similarly, sol-gel solutions produced from martian soil simulars reveal higher contents of iron oxides. Characterization of the precursor molecules and efforts to further concentrate and hydrolyze the products to obtain gel materials will be presented for evaluation as ceramic precursors.

  4. Synthesis of Sol-Gel Precursors for Ceramics from Lunar and Martian Soil Simulars

    Science.gov (United States)

    Sibille, L.; Gavira-Gallardo, J. A.; Hourlier-Bahloul, D.

    2003-01-01

    Recent NASA mission plans for the human exploration of our Solar System has set new priorities for research and development of technologies necessary to enable a long-term human presence on the Moon and Mars. The recovery and processing of metals and oxides from mineral sources on other planets is under study to enable use of ceramics, glasses and metals by explorer outposts. We report initial results on the production of sol-gel precursors for ceramic products using mineral resources available in martian or lunar soil. The presence of SiO2, TiO2, and Al2O3 in both martian (44 wt.% SiO2, 1 wt.% TiO2,7 wt.% Al2O3) and lunar (48 wt.% SiO2, 1.5 wt.% TiO2, 16 wt.% Al2O3) soils and the recent developments in chemical processes to solubilize silicates using organic reagents and relatively little energy indicate that such an endeavor is possible. In order to eliminate the risks involved in the use of hydrofluoric acid to dissolve silicates, two distinct chemical routes are investigated to obtain soluble silicon oxide precursors from lunar and martian soil simulars. Clear solutions of sol-gel precursors have been obtained by dissolution of silica from lunar soil simular in basic ethylene glycol (C2H4(OH)2) solutions to form silicon glycolates. Similarly, sol-gel solutions produced from martian soil simulars reveal higher contents of iron oxides. The elemental composition and structure of the precursor molecules were characterized. Further concentration and hydrolysis of the products was performed to obtain gel materials for evaluation as ceramic precursors.

  5. Preparation of YBa2Cu3O7-x superconducting solutions and films from alkoxide-based precursors using sol-gel method and investigation of their chemical reaction mechanisms

    International Nuclear Information System (INIS)

    Mutlu, Ibrahim Halil; Acun, Hediye; Celik, Erdal; Turkmen, Hasan

    2007-01-01

    In the development of coated superconductors sol-gel technique has been widely used as an effective processing method, especially in making long-length wires and tapes. However, one drawback associated with the deposition of YBa 2 Cu 3 O 7-x and Gd 2 O 3 buffer layer on Ni tape is the adhesion characteristic at interfaces YBCO-Gd 2 O 3 and Gd 2 O 3 -NiO and NiO-Ni substrate. In this paper, two strategies for adhesion enhancement of multilayered ceramic oxide coatings on Ni substrate were proposed: (1) formation of chemical bonds through surface condensation reactions, and development of ceramic networks through diffusion of alkoxide precursors. The current research has focused on the fabrication and adhesion of YBCO coatings on buffered Ni substrate using nine solutions prepared from Y, Ba and Cu alkoxides, solvent and chelating agent. Only two of YBCO solutions were successfully obtained while the rest of them were unsuccessful. Among these solutions we scrutinized chemical reaction mechanisms of a successful and an unsuccessful solution for comparison. How the chemical bonds and solubility were affected by the acids, base and solvents used in the solutions was demonstrated. It was shown that pH of the solution, homogeneity of the solution and gelation, steric affect of the chemicals in sol-gel solutions are significant issues to obtain high quality superconducting YBCO thin films. In addition, X-ray diffraction (XRD) was used to analyze phase structure of YBCO and compare results of chemical reactions obtained by a chemdraw programme. Scanning electron microscope (SEM) studies was carried out to examine microstructures of YBCO films produced from alkoxide precursors, solvent, chelating agent and modifying liquid chemical materials such as triethanolamine or ammonium hydroxide. It was found to be YBCO, Gd 2 O 3 , NiO and Ni phases in YBCO/Gd 2 O 3 /Ni sample from XRD analysis. That the solution prepared by using triethanolamine provided the best film quality and

  6. Sol-Gel Precursors for Ceramics from Minerals Simulating Soils from the Moon and Mars

    Science.gov (United States)

    Sibille, Laurent; Gavira-Gallardo, Jose-Antonio; Hourlier-Bahloul, Djamila

    2003-01-01

    Recent NASA mission plans for the human exploration of our Solar System has set new priorities for research and development of technologies necessary to enable a long-term human presence on the Moon and Mars. The recovery and processing of metals and oxides from mineral sources on other planets is under study to enable use of ceramics, glasses and metals by explorer outposts. We report some preliminary results on the production of sol-gel precursors for ceramic products using mineral resources available in Martian or Lunar soil. The presence of SiO2, TiO2, and A12O3 in both Martian (44 wt.% SiO2, 1 wt.% TiO2, 7 wt.% Al2O3) and Lunar (48 wt.% SiO2, 1.5 wt.% TiO2, 16 wt.% Al2O3) soils and the recent developments in chemical processes to solubilize silicates using organic reagents and relatively little energy indicate that such an endeavor is possible. In order to eliminate the risks involved in the use of hydrofluoric acid to dissolve silicates, two distinct chemical routes are investigated to obtain soluble silicon oxide precursors from Lunar and Martian simulant soils. Clear sol-gel precursors have been obtained by dissolution of silica from Lunar simulant soil in basic ethylene glycol (C2H4(OH)2) solutions to form silicon glycolates. Thermogravimetric Analysis and X-ray Photoelectron Spectroscopy were used to characterize the elemental composition and structure of the precursor molecules. Further concentration and hydrolysis of the products was performed to obtain gel materials for evaluation as ceramic precursors. In the second set of experiments, we used the same starting materials to synthesize silicate esters in acidified alcohol mixtures. Preliminary results indicate the presence of silicon alkoxides in the product of distillation.

  7. The influence of precursor addition order on the porosity of sol-gel bioactive glasses.

    Science.gov (United States)

    Fernando, Delihta; Colon, Pierre; Cresswell, Mark; Journet, Catherine; Pradelle-Plasse, Nelly; Jackson, Phil; Grosgogeat, Brigitte; Attik, Nina

    2018-06-16

    The superior textural properties of sol-gel derived bioactive glasses compared to conventional melt quench glasses accounts for their accelerated bioactivity in vitro. Several studies have explored ways to improve the surface properties of sol-gel glasses in order to maximise their efficiency for bone and tooth regeneration. In this study, we investigated the effect of order of network modifying precursor addition on the textural properties of sol-gel derived bioactive glasses. The effect of precursor addition order on the glass characteristics was assessed by switching the order of network modifying precursor (calcium acetate monohydrate and sodium acetate anhydrous) addition for a fixed composition of bioactive glass (75SiO 2 :5CaO:10Na 2 O:10P 2 O 5 ). The results of this study showed that the order of precursor addition does influence the porosity of these glasses. For the glasses of a fixed composition and preparation conditions we achieved a doubling of surface area, a 1.5 times increase in pore volume and a 1.2 times decrease in pore size just by the mixing the network modifying precursors and adding them together in the sol-gel preparation. This simple and straightforward route adaptation to the preparation of bioactive glasses would allow us to enhance the textural properties of existing and novel composition of bioactive glasses and thus accelerate their bioactivity. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.

  8. Spray drying of silica microparticles for sustained release application with a new sol-gel precursor.

    Science.gov (United States)

    Wang, Bifeng; Friess, Wolfgang

    2017-10-30

    A new precursor, tetrakis(2-methoxyethyl) orthosilicate (TMEOS) was used to fabricate microparticles for sustained release application, specifically for biopharmaceuticals, by spray drying. The advantages of TMEOS over the currently applied precursors are its water solubility and hydrolysis at moderate pH without the need of organic solvents or catalyzers. Thus a detrimental effect on biomolecular drug is avoided. By generating spray-dried silica particles encapsulating the high molecular weight model compound FITC-dextran 150 via the nano spray dryer Büchi-90, we demonstrated how formulation parameters affect and enable control of drug release properties. The implemented strategies to regulate release included incorporating different quantities of dextrans with varying molecular weight as well as adjusting the pH of the precursor solution to modify the internal microstructures. The addition of dextran significantly altered the released amount, while the release became faster with increasing dextran molecular weight. A sustained release over 35days could be achieved with addition of 60 kD dextran. The rate of FITC-Dextran 150 release from the dextran 60 containing particles decreased with higher precursor solution pH. In conclusion, the new precursor TMEOS presents a promising alternative sol-gel technology based carrier material for sustained release application of high molecular weight biopharmaceutical drugs. Copyright © 2017 Elsevier B.V. All rights reserved.

  9. Modification of Different Zirconium Propoxide Precursors by Diethanolamine. Is There a Shelf Stability Issue for Sol-Gel Applications?

    Science.gov (United States)

    Spijksma, Gerald I.; Blank, Dave H. A.; Bouwmeester, Henny J. M.; Kessler, Vadim G.

    2009-01-01

    Modification of different zirconium propoxide precursors with H2dea was investigated by characterization of the isolated modified species. Upon modification of zirconium n-propoxide and [Zr(OnPr)(OiPr)3(iPrOH)]2 with ½ a mol equivalent of H2dea the complexes [Zr2(OnPr)6(OCH2CH2)2NH]2 (1) and [Zr2(OnPr)2(OiPr)4(OCH2CH2)2NH]2 (2) were obtained. However, 1H-NMR studies of these tetranuclear compounds showed that these are not time-stable either in solution or solid form. The effect of this time instability on material properties is demonstrated by light scattering and TEM experiments. Modification of zirconium isopropoxide with either ½ or 1 equivalent mol of H2dea results in formation of the trinuclear complex, Zr{η3μ2-NH(C2H4O)2}3[Zr(OiPr)3]2(iPrOH)2 (3) countering a unique nona-coordinated central zirconium atom. This complex 3 is one of the first modified zirconium propoxide precursors shown to be stable in solution for long periods of time. The particle size and morphology of the products of sol-gel synthesis are strongly dependent on the time factor and eventual heat treatment of the precursor solution. Reproducible sol-gel synthesis requires the use of solution stable precursors. PMID:20087472

  10. Innovative Formulation Combining Al, Zr and Si Precursors to Obtain Anticorrosion Hybrid Sol-Gel Coating

    Directory of Open Access Journals (Sweden)

    Clément Genet

    2018-05-01

    Full Text Available The aim of our study is to improve the aluminium alloy corrosion resistance with Organic-Inorganic Hybrid (OIH sol-gel coating. Coatings are obtained from unusual formulation with precursors mixing: glycidoxypropyltrimethoxysilane (GPTMS, zirconium (IV propoxide (TPOZ and aluminium tri-sec-butoxide (ASB. This formulation was characterized and compared with sol formulations GPTMS/TPOZ and GPTMS/ASB. In each formulation, a corrosion inhibitor, cerium (III nitrate hexahydrate, is employed to improve the corrosion performance. Coatings obtained from sol based on GPTMS/TPOZ/ASB have good anti-corrosion performances with Natural Salt Spray (NSS resistance of 500 h for a thickness lower than 4 µm. Contact angle measurement showed a coating hydrophobic behaviour. To understand these performances, nuclear magnetic resonance (NMR analyses were performed, results make sol-gel coating condensation evident and are in very good agreement with previous results.

  11. Innovative Formulation Combining Al, Zr and Si Precursors to Obtain Anticorrosion Hybrid Sol-Gel Coating.

    Science.gov (United States)

    Genet, Clément; Menu, Marie-Joëlle; Gavard, Olivier; Ansart, Florence; Gressier, Marie; Montpellaz, Robin

    2018-05-10

    The aim of our study is to improve the aluminium alloy corrosion resistance with Organic-Inorganic Hybrid (OIH) sol-gel coating. Coatings are obtained from unusual formulation with precursors mixing: glycidoxypropyltrimethoxysilane (GPTMS), zirconium (IV) propoxide (TPOZ) and aluminium tri-sec-butoxide (ASB). This formulation was characterized and compared with sol formulations GPTMS/TPOZ and GPTMS/ASB. In each formulation, a corrosion inhibitor, cerium (III) nitrate hexahydrate, is employed to improve the corrosion performance. Coatings obtained from sol based on GPTMS/TPOZ/ASB have good anti-corrosion performances with Natural Salt Spray (NSS) resistance of 500 h for a thickness lower than 4 µm. Contact angle measurement showed a coating hydrophobic behaviour. To understand these performances, nuclear magnetic resonance (NMR) analyses were performed, results make sol-gel coating condensation evident and are in very good agreement with previous results.

  12. Applications of sol gel ceramic coatings

    International Nuclear Information System (INIS)

    Barrow, D.

    1996-01-01

    The sol gel method is a chemical technique in which polycrystalline ceramic films are fabricated from a solution of organometallic precursors. The technique is attractive for many industrial applications because it is a simple (films are processed in air), flexible (can be used to coat complex geometries) and cost effective (does not require expensive equipment) process. In addition, dense, high quality coatings can be achieved at much lower temperatures than is generally required for sintering bulk ceramics. In this paper the conventional sol gel method and the new datec process are reviewed and potential applications of sol gel coatings in automotive, aerospace, petrochemical, nuclear and electronic industries are discussed. (orig.)

  13. Effect of concentrations of plasticizers on the sol-gel properties developed from alkoxides precursors

    Energy Technology Data Exchange (ETDEWEB)

    Kunst, Sandra Raquel; Longhi, Marielen; Zini, Lucas Pandolphi [Universidade de Caxias do Sul (CCET/UCS), Caxias do Sul, RS (Brazil). Centro de Ciências Exatas e Tecnologia; Beltrami, Lilian Vanessa Rossa; Boniatti, Rosiana; Cardoso, Henrique Ribeiro Piaggio; Vega, Maria Rita Ortega; Malfatti, Célia de Fraga, E-mail: lvrossa@yahoo.com.br [Universidade Federal do Rio Grande do Sul (LAPEC/UFRGS), Porto Alegre, RS (Brazil). Laboratorio de Pesquisa em Corrosão

    2017-07-01

    Coatings developed through sol-gel method is presented as an interesting replacement to chromium coating. Sol-gel method present advantages as high purity and excellent distribution of the components. The objective of this work is to synthesize and characterize a film obtained by sol-gel route. The film was prepared with 3-(trimethoxysilylpropyl) methacrylate (TMSPMA), tetraethoxysilane (TEOS) and cerium nitrate, using water and ethanol as solvents. Polyethyleneglycol (PEG) plasticizer was added at four different concentrations. The sol was characterized by techniques of viscosity, thermogravimetric analysis (TGA), X-ray diffraction (XRD) nuclear magnetic resonance spectroscopy (NMR) and Fourier transform infrared spectroscopy (FT-IR). The results showed that tetrafunctional alkoxides condensation was retarded by the plasticizer, forming a compact film. The film with 20 g.L-1 of PEG showed the best electrochemical behavior. (author)

  14. Effect of concentrations of plasticizers on the sol-gel properties developed from alkoxides precursors

    Directory of Open Access Journals (Sweden)

    Sandra Raquel Kunst

    Full Text Available Abstract Coatings developed through sol-gel method is presented as an interesting replacement to chromium coating. Sol-gel method present advantages as high purity and excellent distribution of the components. The objective of this work is to synthesize and characterize a film obtained by sol-gel route. The film was prepared with 3-(trimethoxysilylpropyl methacrylate (TMSPMA, tetraethoxysilane (TEOS and cerium nitrate, using water and ethanol as solvents. Polyethyleneglycol (PEG plasticizer was added at four different concentrations. The sol was characterized by techniques of viscosity, thermogravimetric analysis (TGA, X-ray diffraction (XRD nuclear magnetic resonance spectroscopy (NMR and Fourier transform infrared spectroscopy (FT-IR. The results showed that tetrafunctional alkoxides condensation was retarded by the plasticizer, forming a compact film. The film with 20 g.L-1 of PEG showed the best electrochemical behavior.

  15. Method of making ionic liquid mediated sol-gel sorbents

    Science.gov (United States)

    Malik, Abdul; Shearrow, Anne M.

    2017-01-31

    Ionic liquid (IL)-mediated sol-gel hybrid organic-inorganic materials present enormous potential for effective use in analytical microextraction. One obstacle to materializing this prospect arises from high viscosity of ILs significantly slowing down sol-gel reactions. A method was developed which provides phosphonium-based, pyridinium-based, and imidazolium-based IL-mediated advanced sol-gel organic-inorganic hybrid materials for capillary microextraction. Scanning electron microscopy results demonstrate that ILs can serve as porogenic agents in sol-gel reactions. IL-mediated sol-gel coatings prepared with silanol-terminated polymers provided up to 28 times higher extractions compared to analogous sol-gel coatings prepared without any IL in the sol solution. This study shows that IL-generated porous morphology alone is not enough to provide effective extraction media: careful choice of the organic polymer and the precursor with close sol-gel reactivity must be made to ensure effective chemical bonding of the organic polymer to the created sol-gel material to be able to provide the desired sorbent characteristics.

  16. Colloidal probe dynamics in gelatin solution during the sol-gel transition.

    Science.gov (United States)

    Hong, Wei; Xu, Guozhi; Ou, Xiaogang; Sun, Weixiang; Wang, Tao; Tong, Zhen

    2018-05-16

    The dynamics of the colloidal probes in a gelatin solution during the time-dependent sol-gel transition was investigated by multi-particle tracking. The relationship between the relaxation of the medium at the critical gel point and the mean square displacement of the probes was elucidated. Based on this understanding, the critical gel point of gelatin and the corresponding critical exponent n were unambiguously determined by the loss angle criterion and the time-cure superposition. The shift factors of the latter are further used to estimate the time/length-scale evolution of the gelatin during the sol-gel transition. The growth of the medium length scale crossed with the two measuring length scales successively at the pre-gel regime. Coinciding with the length-scale crossovers, the probability density function (PDF) of the probe displacements displayed two transient peaks of non-Gaussianity. In the post-gel regime, the third peak of Gaussianity suggested inhomogeneity in the gel network. The non-Gaussianity results from the bifurcation of diffusivity. The present work showed that the non-Gaussian dynamics of the probes are not the direct equivalence of that of the medium, but an effect of length-scale coupling.

  17. Effect of Precursor Concentration of MgO nanostructure by using Sol-Gel Method

    Directory of Open Access Journals (Sweden)

    V.T. Srisuvetha

    2017-04-01

    Full Text Available MgO thin flims have been prepared on substrates by a novel and simple sol-gel method using magnesium nitrate and collusion as starting material.The MgO nano catalyst with good sensor crystallization were obtained after annealing at 100°C Magnesium oxide was prepared by sol-gel method. The method involves the hydrolysis of magnesium alkoxide in the presence of acid or basic catalysts followed by a Oxalic acid reaction. The synthesized solids were characterized by IR spectroscopy X-ray diffraction electron microscopy. Ultraviolet visible absorbance measurement photoluminescence and Raman scattering spectra. X-ray diffraction (XRD characterization showed the formation of smaller particles after sol gel irradiation the structure and morphology of the MgO particles were analyzed byXRD. These articles were used for FTIR spectroscopic measurement and spectra were collected. In EDS we calculated the peak intensity the SEM the images of metal oxide.UV (Ultra Violet refers to adsorption spectroscopy optical properties of assorption, band gap energy.This means if use light in the visible and adjacent ranges.

  18. Colloidal sol-gel synthesis of oxides: application to the precursors of nuclear fuels

    International Nuclear Information System (INIS)

    Gossard, Alban

    2014-01-01

    One of the main objectives for the future nuclear fuel cycle is the recycling of the minor actinides. Different options are considered: their integration into a new fuel for a prospect of a closed fuel cycle or their transmutation in order to significantly decrease the long-term radiotoxicity of ultimate wastes. In both cases, the synthesis of new advanced materials integrating the actinides jointly is required. Sol-gel processes allow the organization of the material at the colloidal scale or the insertion of controlled porosity using 'templates'. Furthermore, the possibility to work in a 'wet environment' prevents the formation of pulverulent powders which are contaminant in the case of materials incorporating radioactive elements. The main purpose of this work is to demonstrate the adaptability of this route to the nuclear field. Firstly, a methodology of synthesis from a colloidal sol-gel route was set up on a non-radioactive zirconium-based system in order to characterize and understand of the different mechanisms of this synthesis. Then, studies on shaping, including insertion of porosity, were performed. Zirconia monoliths have been obtained thanks to a coupling between a colloidal sol-gel process and the formation of an emulsion stabilized by clusters of solid particles. Finally, a transposition of this work to an uranium-based system was introduced, pointing out different promising perspectives specially concerning the possibilities of shaping of the final material. (author) [fr

  19. Thermodynamic analysis of sol-gel transition of gelatin in terms of water activity in various solutions.

    Science.gov (United States)

    Miyawaki, Osato; Omote, Chiaki; Matsuhira, Keiko

    2015-12-01

    Sol-gel transition of gelatin was analyzed as a multisite stoichiometric reaction of a gelatin molecule with water and solute molecules. The equilibrium sol-gel transition temperature, Tt , was estimated from the average of gelation and melting temperature measured by differential scanning calorimetry. From Tt and the melting enthalpy, ΔHsol , the equilibrium sol-to-gel ratio was estimated by the van't Hoff equation. The reciprocal form of the Wyman-Tanford equation, which describes the sol-to-gel ratio as a function of water activity, was successfully applied to obtain a good linear relationship. From this analysis, the role of water activity on the sol-gel transition of gelatin was clearly explained and the contributions of hydration and solute binding to gelatin molecules were separately discussed in sol-gel transition. The general solution for the free energy for gel-stabilization in various solutions was obtained as a simple function of solute concentration. © 2015 Wiley Periodicals, Inc.

  20. Mullite evolution in ceramics derived from clay, and sol-gel precursors

    International Nuclear Information System (INIS)

    Rezaie, H.R.; Naghizadeh, R.; Golestani-Fard, F.

    2002-01-01

    Mullite formation from sol-gel (behemoth and colloidal silica), and clay has been compared and the microstructural evolution examined using electron-optical techniques and XRD. The relationship between processing route and reaction sequence to form mullite is discussed. In sol-gel processing γAloof transforms to γ-Al 2 O 3 at 400-500 d eg w ithout an isothermal hold. δ-Al 2 O 3 was present after cooling directly from 1100 d eg i n air.(δ+θ)Al 2 O 3 were present above 1200 d eg . Reaction between (δ+θ)Al 2 O 3 and amorphous silica produced 3:2 mullite at∼ 1370 d eg . In kaolin, meta kaolin transforms to spinel and mullite at 980-1000 d eg w ithout an isothermal hold. Melanostatin to 3:2 mullite took place at 1200-1250 d eg . Cristobalite was observed after quenching from 1200 d eg , but could not be detected after cooling directly from 1590 d eg

  1. In situ observation of sol-gel transition of agarose aqueous solution by fluorescence measurement.

    Science.gov (United States)

    Wang, Zheng; Yang, Kun; Li, Haining; Yuan, Chaosheng; Zhu, Xiang; Huang, Haijun; Wang, Yongqiang; Su, Lei; Fang, Yapeng

    2018-06-01

    Sol-gel transition behavior of agarose aqueous solution was investigated by using rheology and fluorescence measurement. On heating, the storage modulus G' decreased gradually, then deviated abruptly at the temperature of about 65°C, and finally decreased slowly again. For fluorescence measurement, the phase transition point kept almost at the temperature of 65°C, which was consistent with that in rheology measurement. Upon compression, it was indicated that the fluorescence lifetime for the probe in the agarose aqueous solution showed a dramatic change in the vicinity of the phase transition point. T vs. P phase diagram of agarose aqueous solution was constructed, which showed that the melting point was an increasing function of pressure. Based on the phase diagram, the agarose gels were prepared by cooling under atmospheric pressure and the pressure of 300MPa, respectively. From the result of the recovered samples studied by optical rheometry, it was found that agarose gel prepared under high pressure had a higher elasticity and lower viscosity index, compared with that under atmospheric pressure. It could be speculated that such kinds of properties might be attributed to the smaller pore size during gelation under high pressure. Copyright © 2018. Published by Elsevier B.V.

  2. Preparation of (Bi,Pb)2Sr2Ca2Cu3Ox precursor powders by a modified polyethylene glycol based sol-gel process

    DEFF Research Database (Denmark)

    Grivel, Jean-Claude; Andersen, N.H.

    2002-01-01

    A modified sol-gel process based on polyethylene glycol has been developed for preparing (Bi,Pb)(2)Sr2Ca2Cu3Ox precursor powders in view of Ag-sheeted tape manufacture. A careful control of the pH and concentration temperature yields an amorphous gel, which can be converted to a fine and extremely...

  3. Study of hafnium (IV) oxide nanoparticles synthesized by polymerized complex and polymer precursor derived sol-gel methods

    KAUST Repository

    Ramos-Gonzá lez, R.; Garcí a-Cerda, L. A.; Alshareef, Husam N.; Gnade, Bruce E.; Quevedo-Ló pez, Manuel Angel Quevedo

    2010-01-01

    This work reports the preparation and characterization of hafnium (IV) oxide (HfO2) nanoparticles grown by derived sol-gel routes that involves the formation of an organic polymeric network. A comparison between polymerized complex (PC) and polymer precursor (PP) methods is presented. For the PC method, citric acid (CA) and ethylene glycol (EG) are used as the chelating and polymerizable reagents, respectively. In the case of PP method, poly(acrylic acid) (PAA) is used as the chelating reagent. In both cases, different precursor gels were prepared and the hafnium (IV) chloride (HfCl4) molar ratio was varied from 0.1 to 1.0 for the PC method and from 0.05 to 0.5 for the PP method. In order to obtain the nanoparticles, the precursors were heat treated at 500 and 800 °C. The thermal characterization of the precursor gels was carried out by thermogravimetric analysis (TGA) and the structural and morphological characterization by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The XRD patterns of the samples obtained by both methods shows the formation of HfO2 at 500 °C with monoclinic crystalline phase. The PC method exhibited also the cubic phase. Finally, the HfO2 nanoparticles size (4 to 11 nm) was determined by TEM and XRD patterns. © (2010) Trans Tech Publications.

  4. Study of hafnium (IV) oxide nanoparticles synthesized by polymerized complex and polymer precursor derived sol-gel methods

    KAUST Repository

    Ramos-González, R.

    2010-03-01

    This work reports the preparation and characterization of hafnium (IV) oxide (HfO2) nanoparticles grown by derived sol-gel routes that involves the formation of an organic polymeric network. A comparison between polymerized complex (PC) and polymer precursor (PP) methods is presented. For the PC method, citric acid (CA) and ethylene glycol (EG) are used as the chelating and polymerizable reagents, respectively. In the case of PP method, poly(acrylic acid) (PAA) is used as the chelating reagent. In both cases, different precursor gels were prepared and the hafnium (IV) chloride (HfCl4) molar ratio was varied from 0.1 to 1.0 for the PC method and from 0.05 to 0.5 for the PP method. In order to obtain the nanoparticles, the precursors were heat treated at 500 and 800 °C. The thermal characterization of the precursor gels was carried out by thermogravimetric analysis (TGA) and the structural and morphological characterization by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The XRD patterns of the samples obtained by both methods shows the formation of HfO2 at 500 °C with monoclinic crystalline phase. The PC method exhibited also the cubic phase. Finally, the HfO2 nanoparticles size (4 to 11 nm) was determined by TEM and XRD patterns. © (2010) Trans Tech Publications.

  5. Fast Processing of Sol-Gel TCO

    NARCIS (Netherlands)

    Deelen, J. van; Rem, M.; Arfsten, N.; Buskens, P.P.

    2016-01-01

    TCOs are usually deposited using sputtering or chemical vapor deposition, which have a yield of typically 50-75%. The sol gel method does not need low pressure and can be done with a high precursor yield in the range of 90 – 100%. Sol gel enables also the TCO function as a planarization or

  6. Functional coatings: the sol-gel approach

    International Nuclear Information System (INIS)

    Belleville, Ph.

    2010-01-01

    CEA's sol-gel laboratory is specialized in the development of innovative sol-gel optical coatings and has extended its application field to membrane materials and coatings for energy conversion, to electric coatings for microelectronics devices and to thin films for gas sensing. This article describes, by way of examples, the laboratory's research on sol-gel functional coatings, including nano-material synthesis, organic-inorganic hybrid-based solution preparation as well as deposition process development and prototyping. (author)

  7. Preparation and characterization of multilayer mesoporous γ-alumina membrane obtained via sol-gel using new precursors

    Directory of Open Access Journals (Sweden)

    Tafrishi R.

    2015-12-01

    Full Text Available In this paper, a mesoporous γ-alumina membrane coated on a macroporous α-alumina support via sol-gel method has been reported. A crack-free γ-alumina membrane was obtained by adding PVA to the alumina solution and optimum parameters of roughness, temperature and porosity were achieved. The support was dip-coated in different solutions using two new different solvents with different particle size distributions. Using these two solvents led to the uniform distribution of pore size in the final membrane. The alumina sols showed particle size distributions in the range of 20 to 55 nm which was measured by a DLS Zeta Sizer. X-ray diffraction technique, atomic force microscopy and scanning electron microscopy were used to characterize the membrane layer. XRD and DTA data for the γ-alumina membrane showed its thermal stability up to around 600 °C. The thickness of the mesoporous γ-alumina membrane was about 4 μm with 16 nm of surface roughness and 5 nm pore size. The resultant crack-free mesoporous membrane shows that the membrane preparation procedure was optimum. In this work, it has been investigated the performance of γ-alumina membranes for single gas permeation and separation of binary gas mixtures.

  8. Determination of hexamethylene tetramine in the process solution of sol-gel method for nuclear fuel fabrication

    International Nuclear Information System (INIS)

    Ganatra, V.R.; Sawant, R.M.; Chaudhuri, N.K.; Vaidya, V.N.

    1998-01-01

    Hexamethylene tetramine (HMTA) was determined in the presence of large quantities of urea, formaldehyde and ammonium hydroxide by potentiometric titration with perchloric acid solution using an autotitrator coupled to a personal computer. This analysis is required for the process control of the sol-gel method in the production of ceramic metal oxide (e.g., oxides and mixed oxides of Th, U and Pu) microspheres using the internal gelation route. Feed solution used for preparation of microspheres contains large quantities of urea. The washings of gel microspheres produced after the internal gelation process contain urea, formaldehyde, urea-formaldehyde complex and ammonium hydroxide. The presence of these constituents in the feed solution and washings seriously interfere in the commonly used methods for the determination of HMTA. Using this method the relative standard deviation was found to be 0.27% in eleven determinations of a typical feed solution (3.0M HMTA) when the aliquots contained 75 to 125 mg of HMTA. Time required for each titration was 5-7 minutes. Feed and effluent solutions of sol-gel process were analysed. (author)

  9. Characterization of the Sol-Gel Transition for Zirconia-Toughened Alumina Precursors

    Science.gov (United States)

    Moeti, I.; Karikari, E.; Chen, J.

    1998-01-01

    High purity ZTA ceramic powders with and without yttria were produced using metal alkoxide precursors. ZTA ceramic powders with varying volume percents of zirconia were prepared (7, 15, and 22%). Aluminum tri-sec butoxide, zirconium propoxide, and yttrium isopropoxide were the reagents used. Synthesis conditions were varied to control the hydrolysis and the aging conditions for the sol to gel transition. FTIR analysis and theological characterization were used to follow the structural evolution during the sol to gel transition. The greater extent of hydrolysis and the build-up of structure measured from viscoelastic properties were consistent. Heat treatment was conducted to produce submicron grain fully crystalline ZTA ceramic powders. In all experimental cases a-alumina and tetragonal zirconia phases were confirmed even in the absence of yttria.

  10. Preparation of macroporous zirconia monoliths from ionic precursors via an epoxide-mediated sol-gel process accompanied by phase separation

    International Nuclear Information System (INIS)

    Guo, Xingzhong; Song, Jie; Lvlin, Yixiu; Yang, Hui; Nakanishi, Kazuki; Kanamori, Kazuyoshi

    2015-01-01

    Monolithic macroporous zirconia (ZrO 2 ) derived from ionic precursors has been successfully fabricated via the epoxide-mediated sol-gel route accompanied by phase separation in the presence of propylene oxide (PO) and poly(ethylene oxide) (PEO). The addition of PO used as an acid scavenger mediates the gelation, whereas PEO enhances the polymerization-induced phase separation. The appropriate choice of the starting compositions allows the production of a macroporous zirconia monolith with a porosity of 52.9% and a Brunauer–Emmett–Teller (BET) surface area of 171.9 m 2 · g −1 . The resultant dried gel is amorphous, whereas tetragonal ZrO 2 and monoclinic ZrO 2 are precipitated at 400 and 600 °C, respectively, without spoiling the macroporous morphology. After solvothermal treatment with an ethanol solution of ammonia, tetragonal ZrO 2 monoliths with smooth skeletons and well-defined mesopores can be obtained, and the BET surface area is enhanced to 583.8 m 2 · g −1 . (paper)

  11. Influence of precursor ratios on the properties of cotton coated with a sol-gel flame retardant

    CSIR Research Space (South Africa)

    Chapple, Stephen A

    2006-11-01

    Full Text Available Cotton has many desirable properties, but is flammable. The flame retardant treatment of cotton is an important textile process. To study the effect of a sol-gel phosphate-based flame-retardant coating on fabric properties (flammability, stiffness...

  12. Sol-gel open tubular ODS columns with reversed electroosmotic flow for capillary electrochromatography.

    Science.gov (United States)

    Hayes, J D; Malik, A

    2001-03-01

    Sol-gel chemistry was successfully used for the fabrication of open tubular columns with surface-bonded octadecylsilane (ODS) stationary-phase coating for capillary electrochromatography (OT-CEC). Following column preparations, a series of experiments were performed to investigate the performance of the sol-gel coated ODS columns in OT-CEC. The incorporation of N-octadecyldimethyl[3-(trimethoxysilyl)propyl]ammonium chloride as one of the sol-gel precursors played an important role in the electrochromatographic performance of the prepared columns. This chemical reagent possesses a chromatographically favorable, bonded ODS moiety, in conjunction with three methoxy groups allowing for sol-gel reactivity. In addition, a positively charged nitrogen atom is present in the molecular structure of this reagent and provides a positively charged capillary surface responsible for the reversed electroosmotic flow (EOF) in the columns during CEC operation. Comparative studies involving the EOF within such sol-gel ODS coated and uncoated capillaries were performed using acetonitrile and methanol as the organic modifiers in the mobile phase. The use of a deactivating reagent, phenyldimethylsilane, in the sol-gel solution was evaluated. Efficiency values of over 400,000 theoretical plates per meter were achieved in CEC on a 64 cm x 25 microm i.d. sol-gel ODS open tubular column. Test mixtures of polycyclic aromatic hydrocarbons, benzene derivatives, and aromatic aldehydes and ketones were used to evaluate the CEC performances of both nondeactivated and deactivated open tubular sol-gel columns. The effects of mobile-phase organic modifier contents and pH on EOF in such columns were evaluated. The prepared sol-gel ODS columns are characterized by switchable electroosmotic flow. A pH value of approximately 8.5 was found correspond to the isoelectric point for the prepared sol-gel ODS coatings.

  13. Sol-gel derived sorbents

    Science.gov (United States)

    Sigman, Michael E.; Dindal, Amy B.

    2003-11-11

    Described is a method for producing copolymerized sol-gel derived sorbent particles for the production of copolymerized sol-gel derived sorbent material. The method for producing copolymerized sol-gel derived sorbent particles comprises adding a basic solution to an aqueous metal alkoxide mixture for a pH.ltoreq.8 to hydrolyze the metal alkoxides. Then, allowing the mixture to react at room temperature for a precalculated period of time for the mixture to undergo an increased in viscosity to obtain a desired pore size and surface area. The copolymerized mixture is then added to an immiscible, nonpolar solvent that has been heated to a sufficient temperature wherein the copolymerized mixture forms a solid upon the addition. The solid is recovered from the mixture, and is ready for use in an active sampling trap or activated for use in a passive sampling trap.

  14. Cu-Doped ZnO Thin Films Deposited by a Sol-Gel Process Using Two Copper Precursors: Gas-Sensing Performance in a Propane Atmosphere

    Directory of Open Access Journals (Sweden)

    Heberto Gómez-Pozos

    2016-01-01

    Full Text Available A study on the propane gas-sensing properties of Cu-doped ZnO thin films is presented in this work. The films were deposited on glass substrates by sol-gel and dip coating methods, using zinc acetate as a zinc precursor, copper acetate and copper chloride as precursors for doping. For higher sensitivity values, two film thickness values are controlled by the six and eight dippings, whereas for doping, three dippings were used, irrespective of the Cu precursor. The film structure was analyzed by X-ray diffractometry, and the analysis of the surface morphology and film composition was made through scanning electron microscopy (SEM and secondary ion mass spectroscopy (SIMS, respectively. The sensing properties of Cu-doped ZnO thin films were then characterized in a propane atmosphere, C3H8, at different concentration levels and different operation temperatures of 100, 200 and 300 °C. Cu-doped ZnO films doped with copper chloride presented the highest sensitivity of approximately 6 × 104, confirming a strong dependence on the dopant precursor type. The results obtained in this work show that the use of Cu as a dopant in ZnO films processed by sol-gel produces excellent catalysts for sensing C3H8 gas.

  15. Silica- and germania-based dual-ligand sol-gel organic-inorganic hybrid sorbents combining superhydrophobicity and π-π interaction. The role of inorganic substrate in sol-gel capillary microextraction.

    Science.gov (United States)

    Seyyal, Emre; Malik, Abdul

    2017-04-29

    Principles of sol-gel chemistry were utilized to create silica- and germania-based dual-ligand surface-bonded sol-gel coatings providing enhanced performance in capillary microextraction (CME) through a combination of ligand superhydrophobicity and π-π interaction. These organic-inorganic hybrid coatings were prepared using sol-gel precursors with bonded perfluorododecyl (PF-C 12 ) and phenethyl (PhE) ligands. Here, the ability of the PF-C 12 ligand to provide enhanced hydrophobic interaction was advantageously combined with π-π interaction capability of the PhE moiety to attain the desired sorbent performance in CME. The effect of the inorganic sorbent component on microextraction performance of was explored by comparing microextraction characteristics of silica- and germania-based sol-gel sorbents. The germania-based dual-ligand sol-gel sorbent demonstrated superior CME performance compared to its silica-based counterpart. Thermogravimetric analysis (TGA) of the created silica- and germania-based dual-ligand sol-gel sorbents suggested higher carbon loading on the germania-based sorbent. This might be indicative of more effective condensation of the organic ligand-bearing sol-gel-active chemical species to the germania-based sol-gel network (than to its silica-based counterpart) evolving in the sol solution. The type and concentration of the organic ligands were varied in the sol-gel sorbents to fine-tune extraction selectivity toward different classes of analytes. Specific extraction (SE) values were used for an objective comparison of the prepared sol-gel CME sorbents. The sorbents with higher content of PF-C 12 showed remarkable affinity for aliphatic hydrocarbons. Compared to their single-ligand sol-gel counterparts, the dual-ligand sol-gel coatings demonstrated significantly superior CME performance in the extraction of alkylbenzenes, providing up to ∼65.0% higher SE values. The prepared sol-gel CME coatings provided low ng L -1 limit of detections (LOD

  16. Studies of (3-mercaptopropyl)trimethoxylsilane and bis(trimethoxysilyl)ethane sol-gel coating on copper and aluminum.

    Science.gov (United States)

    Li, Ying-Sing; Lu, Weijie; Wang, Yu; Tran, Tuan

    2009-09-01

    Bis(trimethoxysilyl)ethane (BTMSE) and (3-mercaptopropyl)trimethoxysilane (MPTMS) have been used as precursors to prepare sol-gels and hybrid sol-gel under acidic condition. From the X-ray photoelectron spectroscopy data on MPTMS sol-gel coated aluminum and copper, it has been shown that the silane film is covalently bonded to Al surface through the interfacial condensation. There is no evidence of bonding interaction between the thiol group and the Cu. The recorded reflection adsorption IR (RAIR) spectrum has provided evidence that the coating BTMSE film covalently interacts with Al. Vibrational assignments have been suggested for pure BTMSE, BTMSE sol-gel, BTMSE xerogel, and BTMSE coated Al panel based on the group frequencies and the variation of frequencies with the sample treatment conditions. The progression of condensation reaction has been observed from the IR spectra of the BTMSE sol-gel and the sol-gel coated film after the treatments at different temperatures with different lengths of time. The corrosion protection of the sol-gel coated Al and Cu has been characterized in NaCl solutions by cyclic voltammetric, potentiodynamic polarization and impedance spectroscopy methods. All these electrochemical measurements indicate that the sol-gel coated metals have better corrosion protection than the corresponding uncoated metals.

  17. Electroluminescence of zinc oxide thin-films prepared via polymeric precursor and via sol-gel methods

    International Nuclear Information System (INIS)

    Lima, S.A.M.; Cremona, M.; Davolos, M.R.; Legnani, C.; Quirino, W.G.

    2007-01-01

    Zinc oxide (ZnO) is an electroluminescent (EL) material that can emit light in different regions of electromagnetic spectrum when electrically excited. Since ZnO is chemically stable, inexpensive and environmentally friendly material, its EL property can be useful to construct solid-state lamps for illumination or as UV emitter. We present here two wet chemical methods to prepare ZnO thin-films: the Pechini method and the sol-gel method, with both methods resulting in crystalline and transparent films with transmittance >85% at 550 nm. These films were used to make thin-film electroluminescent devices (TFELD) using two different insulator layers: lithium fluoride (LiF) or silica (SiO 2 ). All the devices exhibit at least two wide emission bands in the visible range centered at 420 nm and at 380 nm attributed to the electronic defects in the ZnO optical band gap. Besides these two bands, the device using SiO 2 and ZnO film obtained via sol-gel exhibits an additional band in the UV range centered at 350 nm which can be attributed to excitonic emission. These emission bands of ZnO can transfer their energy when a proper dopant is present. For the devices produced the voltage-current characteristics were measured in a specific range of applied voltage

  18. Characterisation of a new alkoxide sol-gel hydroxyapatite

    International Nuclear Information System (INIS)

    Green, D.D.; Kannangara, G.S.K.; Milev, A.; Ben-Nissan, B.

    1999-01-01

    Hydroxyapatite (HAp) coatings have been used to promote bone growth and fixation towards implant surfaces to encourage faster recovery times for the recipient. Current coating processing techniques, capable of producing thin HAp layers are pulsed-laser deposition and sputtering (high-temperature processing). Other technologies are in vitro methods, electrodeposition and sol-gel, due to the fact that these techniques utilise lower processing temperatures they avoid structural instabilities of HAp at elevated temperatures. The term sol-gel encompasses any process of producing ceramic materials (single and mixed oxides, as well as non-oxides e.g. nitrides) from solutions. The sol-gel process was first identified by Ebelman, and has been used to produce ceramic powders, coatings, and bulk materials including glasses. The implementation of a sol-gel methodology enables increased stoichiometry and homogeneity, while having the ability to coat complex shapes. Sol-gel hydroxyapatite reported by Chai et al. employed tri ethyl phosphite [ P(OEt) 3 ] as the staring phosphorus alkoxide precursor, whereby it was established that in order to obtain monophasic hydroxyapatite upon firing there must be a 24 hour ripening period. The ripening period was determined to be an equilibrium step whereby the equilibrium intermediate phase lied in favour of a diethyl phosphite arrangement (species) within the sol. Therefore, the work here under taken was to produce hydroxyapatite using diethyl phosphite [HOP(OEt) 2 ] as a starting alkoxide precursor with a final aim to reduce or eliminate the ageing period as observed by Chai et al in P(OEt) 3 solutions

  19. Sol-gel bonding of silicon wafers

    International Nuclear Information System (INIS)

    Barbe, C.J.; Cassidy, D.J.; Triani, G.; Latella, B.A.; Mitchell, D.R.G.; Finnie, K.S.; Short, K.; Bartlett, J.R.; Woolfrey, J.L.; Collins, G.A.

    2005-01-01

    Sol-gel bonds have been produced between smooth, clean silicon substrates by spin-coating solutions containing partially hydrolysed silicon alkoxides. The two coated substrates were assembled and the resulting sandwich fired at temperatures ranging from 60 to 600 deg. C. The sol-gel coatings were characterised using attenuated total reflectance Fourier transform infrared spectroscopy, ellipsometry, and atomic force microscopy, while the corresponding bonded specimens were investigated using scanning electron microscopy and cross-sectional transmission electron microscopy. Mechanical properties were characterised using both microindentation and tensile testing. Bonding of silicon wafers has been successfully achieved at temperatures as low as 60 deg. C. At 300 deg. C, the interfacial fracture energy was 1.55 J/m 2 . At 600 deg. C, sol-gel bonding provided superior interfacial fracture energy over classical hydrophilic bonding (3.4 J/m 2 vs. 1.5 J/m 2 ). The increase in the interfacial fracture energy is related to the increase in film density due to the sintering of the sol-gel interface with increasing temperature. The superior interfacial fracture energy obtained by sol-gel bonding at low temperature is due to the formation of an interfacial layer, which chemically bonds the two sol-gel coatings on each wafer. Application of a tensile stress on the resulting bond leads to fracture of the samples at the silicon/sol-gel interface

  20. Effects of precursor on the morphology and size of ZrO2 nanoparticles, synthesized by sol-gel method in non-aqueous medium

    International Nuclear Information System (INIS)

    Siddiqui, Mohammed Rafiq Hussain; Al-Wassil, Abdulaziz Ibrahim; Mahfouz, Refaat Mohamad; Al-Otaibi, Abdullah Mohmmed

    2012-01-01

    Pure zirconium oxide (ZrO 2 ) nanoparticles with diameters 10-25 nm were synthesized from ZrOCl 2 .8H 2 O and Zr(SO 4 )2.H 2 O with benzyl alcohol as non-aqueous solvent medium using sol-gel method. Sodium lauryl sulfate was added as surfactants to control the particle size. The synthesized ZrO 2 nanoparticles have a mixture of tetragonal and monoclinic structure. The XRD showed the purity of obtained ZrO 2 nanoparticles with tetragonal and monoclinic phase and the crystallite size for ZrOCl 2 .8H 2 O precursor was estimated to be 18.1 nm and that from Zr(SO 4 )2.H 2 O was 9.7 nm. The transmission electron microscopy and scanning electron microscopic studies also shows different sizes of nanoparticles and different morphology depending on the precursor used for the synthesis of ZrO 2 nanoparticles. (author)

  1. Adsorption isotherm studies of chromium (VI) from aqueous solutions using sol-gel hydrotalcite-like compounds

    Energy Technology Data Exchange (ETDEWEB)

    Ramos-Ramirez, Esthela, E-mail: ramosre@quijote.ugto.mx [Centro de Investigaciones en Quimica Inorganica de la Universidad de Guanajuato, Noria Alta s/n, Col. Noria Alta, C.P. 36050, Guanajuato, Gto. (Mexico); Gutierrez Ortega, Norma L.; Conteras Soto, Cesar A. [Centro de Investigaciones en Quimica Inorganica de la Universidad de Guanajuato, Noria Alta s/n, Col. Noria Alta, C.P. 36050, Guanajuato, Gto. (Mexico); Instituto Nacional de Investigaciones Nucleares, Carretera Mexico-Toluca s/n, km 36.5, La Marquesa, Coyoacan Mexico, C.P. 52750 (Mexico); Olguin Gutierrez, Maria T. [Instituto Nacional de Investigaciones Nucleares, Carretera Mexico-Toluca s/n, km 36.5, La Marquesa, Coyoacan Mexico, C.P. 52750 (Mexico)

    2009-12-30

    In under-developed countries, industries such as paint and pigment manufacturing, leather tanning, chrome plating and textile processing, usually discharge effluents containing Cr(VI) and Cr(III) into municipal sanitary sewers. It has been reported that Cr(VI) acts as a powerful epithelial irritant and as a human carcinogen. In the present work, hydrotalcite-like compounds with a Mg/Al ratio = 2 were synthesized by the sol-gel method. The hydrotalcite-like compounds and their corresponding thermally treated products were characterized by powder X-ray diffraction, infrared spectroscopy and N{sub 2} adsorption. The hydrotalcite-like compounds and the heated solids were used as adsorbents for Cr(VI) in aqueous solutions. Adsorption isotherm studies of Cr(VI) from aqueous solution are described. The adsorbent capacity was determined using the Langmuir, Freundlich and Dubinin-Radushkevich adsorption isotherm models. The Cr(VI) adsorption isotherm data fit best to the Langmuir isotherm model. The maximum Cr(VI) uptake by hydrotalcite and the heated solids was determined using the Langmuir equation and was found to range between 26 and 29 mg Cr(VI)/g adsorbent.

  2. Adsorption isotherm studies of chromium (VI) from aqueous solutions using sol-gel hydrotalcite-like compounds

    International Nuclear Information System (INIS)

    Ramos-Ramirez, Esthela; Gutierrez Ortega, Norma L.; Conteras Soto, Cesar A.; Olguin Gutierrez, Maria T.

    2009-01-01

    In under-developed countries, industries such as paint and pigment manufacturing, leather tanning, chrome plating and textile processing, usually discharge effluents containing Cr(VI) and Cr(III) into municipal sanitary sewers. It has been reported that Cr(VI) acts as a powerful epithelial irritant and as a human carcinogen. In the present work, hydrotalcite-like compounds with a Mg/Al ratio = 2 were synthesized by the sol-gel method. The hydrotalcite-like compounds and their corresponding thermally treated products were characterized by powder X-ray diffraction, infrared spectroscopy and N 2 adsorption. The hydrotalcite-like compounds and the heated solids were used as adsorbents for Cr(VI) in aqueous solutions. Adsorption isotherm studies of Cr(VI) from aqueous solution are described. The adsorbent capacity was determined using the Langmuir, Freundlich and Dubinin-Radushkevich adsorption isotherm models. The Cr(VI) adsorption isotherm data fit best to the Langmuir isotherm model. The maximum Cr(VI) uptake by hydrotalcite and the heated solids was determined using the Langmuir equation and was found to range between 26 and 29 mg Cr(VI)/g adsorbent.

  3. Adsorption isotherm studies of chromium (VI) from aqueous solutions using sol-gel hydrotalcite-like compounds.

    Science.gov (United States)

    Ramos-Ramírez, Esthela; Ortega, Norma L Gutiérrez; Soto, Cesar A Contreras; Gutiérrez, Maria T Olguín

    2009-12-30

    In under-developed countries, industries such as paint and pigment manufacturing, leather tanning, chrome plating and textile processing, usually discharge effluents containing Cr(VI) and Cr(III) into municipal sanitary sewers. It has been reported that Cr(VI) acts as a powerful epithelial irritant and as a human carcinogen. In the present work, hydrotalcite-like compounds with a Mg/Al ratio=2 were synthesized by the sol-gel method. The hydrotalcite-like compounds and their corresponding thermally treated products were characterized by powder X-ray diffraction, infrared spectroscopy and N(2) adsorption. The hydrotalcite-like compounds and the heated solids were used as adsorbents for Cr(VI) in aqueous solutions. Adsorption isotherm studies of Cr(VI) from aqueous solution are described. The adsorbent capacity was determined using the Langmuir, Freundlich and Dubinin-Radushkevich adsorption isotherm models. The Cr(VI) adsorption isotherm data fit best to the Langmuir isotherm model. The maximum Cr(VI) uptake by hydrotalcite and the heated solids was determined using the Langmuir equation and was found to range between 26 and 29 mg Cr(VI)/g adsorbent.

  4. Critical ageing and chemistry of nanocrystalline hydroxyapatite sol-gel solutions

    International Nuclear Information System (INIS)

    Chai, C.S.; Gross, K.A.; Kannangara, K.; Ben-Nissan, B.; Hanley, L.

    1998-01-01

    In previous work we have demonstrated that using alkoxide precursors, it is possible to produce crystalline hydroxyapatite coatings with potential uses in orthopaedic and dental applications. However, to produce monophasic hydroxyapatite coatings, sols must be aged for a minimum of 24 hours prior to deposition. 31 P NMR has been used to analyse chemical changes occurring in the sol during the ageing process and have revealed that P-O-C bonds present in the precursor material are gradually replaced by P-O-Ca bonds with an accompanying change in oxidation state from P(III) to P(V). Thermal analysis was used to examine hydrolysed gels and showed that sols aged less than 24 hours contain unreacted calcium diethoxide which produces CaO upon heating. These findings have been confirmed by x-ray diffraction. Copyright (1998) Australasian Ceramic Society

  5. Critical ageing and chemistry of nanocrystalline hydroxyapatite sol-gel solutions

    Energy Technology Data Exchange (ETDEWEB)

    Chai, C.S.; Gross, K.A.; Kannangara, K.; Ben-Nissan, B. [University of Technology, Sydney, NSW (Australia). Department of Chemistry, Materials and Forensic Sciences; Hanley, L. [University of Illinois at Chicago, (United States). Department of Chemistry

    1998-12-31

    In previous work we have demonstrated that using alkoxide precursors, it is possible to produce crystalline hydroxyapatite coatings with potential uses in orthopaedic and dental applications. However, to produce monophasic hydroxyapatite coatings, sols must be aged for a minimum of 24 hours prior to deposition. {sup 31}P NMR has been used to analyse chemical changes occurring in the sol during the ageing process and have revealed that P-O-C bonds present in the precursor material are gradually replaced by P-O-Ca bonds with an accompanying change in oxidation state from P(III) to P(V). Thermal analysis was used to examine hydrolysed gels and showed that sols aged less than 24 hours contain unreacted calcium diethoxide which produces CaO upon heating. These findings have been confirmed by x-ray diffraction. Copyright (1998) Australasian Ceramic Society 16 refs., 4 figs.

  6. Sol-gel based mid-infrared evanescent wave sensors for detection of organophosphate pesticides in aqueous solution

    Energy Technology Data Exchange (ETDEWEB)

    Janotta, Markus; Karlowatz, Manfred; Vogt, Frank; Mizaikoff, Boris

    2003-10-31

    This work demonstrates the application of organically modified sol-gels as recognition layers combined with mid-infrared evanescent wave sensors for in situ detection of nitrated organics in aqueous media. Sol-gels were prepared by acid-catalyzed copolymerization of phenyltrimethoxysilane (PTMOS) and tetramethoxysilane (TMOS) and were spin-coated onto ZnSe attenuated total reflection (ATR) waveguides. These sensors were investigated with respect to their enrichment properties of selected organophosphates, i.e. parathion, fenitrothion and paraoxon, respectively, and their capability of suppressing interfering water background absorptions. Figures of merit are derived from calibration curves determined to assess sensitivity and reproducibility of the applied sensor system. It can be concluded that sol-gel coated infrared optical sensors enable reproducible detection of organophosphates down to the sub-ppm concentration range. Furthermore, measurement of spiked river water samples demonstrates feasibility as remote field sensor system. Once the required sensitivity is achieved, sol-gel based mid-infrared evanescent wave sensors have the potential of being an alternative to commonly applied biosensors for detection of organophosphates in environmental analysis, since they provide superior mechanical and chemical stability during application relevant periods of time.

  7. Luminescent hybrid porphyrinosilica obtained by sol gel chemistry

    Directory of Open Access Journals (Sweden)

    Neri Cláudio Roberto

    2003-01-01

    Full Text Available The sol-gel process is a methodology used to obtain organic-inorganic hybrid solids, which open new possibilities in the field of material science. The sol-gel technique offers a low temperature attractive approach for introducing organic molecules into amorphous materials. In order to introduce tetrakis (2-hydroxy-5-nitrophenylporphyrin covalently bounded to a silicate matrix, the inorganic precursor 3-isocyanatopropyltriethoxysilane was added (molar ratio 2:1 to the porphyrin solution in anhydrous dimethylformamide and triethylamine. The isolated porphyrin and the hybrid porphyrinosilica have excitation maximum centred at 400 nm and 424 nm, respectively and the emission spectra for both materials has bands centred at 650 nm and 713 nm. The formation of hybrid matrix was investigated by FTIR.

  8. Current and future possibilities of sol-gel process

    International Nuclear Information System (INIS)

    Sakka, Sumio

    2004-01-01

    The sol-gel method is characterized by the low temperature processing. Since this method starts from solutions, the product is essentially nanomaterials. So far, various kinds of microstructures, including dense, porous, hybrid, amorphous and crystalline microstructures have been realized. Accordingly, sol-gel materials cover a wide range of functions, such as optical, electronic, mechanical, chemical and bio-functions. Future perspectives of the sol-gel method are described in the article. (author)

  9. Superconductive ceramics obtained with sol gel method

    International Nuclear Information System (INIS)

    Arcangeli, A.; Mosci, A.; Nardi, A.; Vatteroni, R.; Zondini, C.

    1988-01-01

    Several sol gel routes have been considered, studied and developed to produce large quantities of granulates which can be processed to obtain ceramics having good superconducting characteristics. In the considered process a mixture of commercial nitrates is atomized, at room temperature, in a solution 1:1 of Primene JMT and Benzene and a pale blue gel of the starting elements is suddently formed. The granulates obtained are free flowing, very reactive and well suited for pressing. For their intrinsic characteristics they could be very good precursors for the production of large quantities of superconductive ceramics in different forms. The precipitated gel is dried, calcinated, pressed in the form of cylindrical pellets which are sintered up to 960 degrees C. No griding or different thermal treatments are needed. The sintered material has low electric resistence, shows a clear Meissner effect and has a transition temperature of between 91 and 95 K

  10. Sol-gel synthesis of hydroxyapatite

    International Nuclear Information System (INIS)

    Zupanski, M.D.; Lucena, M.P.P.; Bergmann, C.P.

    2010-01-01

    Hydroxyapatite (HAp) has been established as the calcium phosphate based compound with most applications in the biological field. Among the numerous techniques for synthesis of HAp, the sol-gel processing route affords great control over purity and formed phases using low processing temperatures. In addition, the sol-gel approach offers an option for homogeneous HAp coating on metal substrates, as well as the ability to generate nanocrystalline powders. In this work, the sol-gel synthesis of HAp was investigated employing triethyl phosphate and calcium nitrate tetrahydrate as phosphorous and calcium precursors, respectively. The aging effect on phase composition and powder morphology of the final product was studied in terms of temperature and aging time. The powders were studied by using X-ray diffraction, Fourier transform infrared spectroscopy, particle size distribution by laser diffraction and scanning electron microscopy. (author)

  11. Effects of precursor on the morphology and size of ZrO{sub 2} nanoparticles, synthesized by sol-gel method in non-aqueous medium

    Energy Technology Data Exchange (ETDEWEB)

    Siddiqui, Mohammed Rafiq Hussain; Al-Wassil, Abdulaziz Ibrahim; Mahfouz, Refaat Mohamad [King Saud University, Riyadh (Saudi Arabia). Department of Chemistry, College of Science; Al-Otaibi, Abdullah Mohmmed [King Abdulaziz City for Science and Technology (Saudi Arabia). The NationalProgram for Advanced Materials and Building Systems

    2012-11-15

    Pure zirconium oxide (ZrO{sub 2}) nanoparticles with diameters 10-25 nm were synthesized from ZrOCl{sub 2}.8H{sub 2}O and Zr(SO{sub 4})2.H{sub 2}O with benzyl alcohol as non-aqueous solvent medium using sol-gel method. Sodium lauryl sulfate was added as surfactants to control the particle size. The synthesized ZrO{sub 2} nanoparticles have a mixture of tetragonal and monoclinic structure. The XRD showed the purity of obtained ZrO{sub 2} nanoparticles with tetragonal and monoclinic phase and the crystallite size for ZrOCl{sub 2}.8H{sub 2}O precursor was estimated to be 18.1 nm and that from Zr(SO{sub 4})2.H{sub 2}O was 9.7 nm. The transmission electron microscopy and scanning electron microscopic studies also shows different sizes of nanoparticles and different morphology depending on the precursor used for the synthesis of ZrO{sub 2} nanoparticles. (author)

  12. Effects of precursor on the morphology and size of ZrO2 nanoparticles, synthesized by sol-gel method in non-aqueous medium

    Directory of Open Access Journals (Sweden)

    Mohammed Rafiq Hussain Siddiqui

    2012-12-01

    Full Text Available Pure zirconium oxide (ZrO2 nanoparticles with diameters 10-25 nm were synthesized from ZrOCl2.8H2O and Zr(SO42.H2O with benzyl alcohol as non-aqueous solvent medium using sol-gel method. Sodium lauryl sulfate was added as surfactants to control the particle size. The synthesized ZrO2 nanoparticles have a mixture of tetragonal and monoclinic structure. The XRD showed the purity of obtained ZrO2 nanoparticles with tetragonal and monoclinic phase and the crystallite size for ZrOCl2.8H2O precursor was estimated to be 18.1 nm and that from Zr(SO42.H2O was 9.7 nm. The transmission electron microscopy and scanning electron microscopic studies also shows different sizes of nanoparticles and different morphology depending on the precursor used for the synthesis of ZrO2 nanoparticles

  13. Highly efficient solid-state neutron scintillators based on hybrid sol-gel nanocomposite materials

    International Nuclear Information System (INIS)

    Kesanli, Banu; Hong, Kunlun; Meyer, Kent; Im, Hee-Jung; Dai, Sheng

    2006-01-01

    This research highlights opportunities in the formulation of neutron scintillators that not only have high scintillation efficiencies but also can be readily cast into two-dimensional detectors. Series of transparent, crack-free monoliths were prepared from hybrid polystyrene-silica nanocomposites in the presence of arene-containing alkoxide precursor through room temperature sol-gel processing. The monoliths also contain lithium-6 salicylate as a target material for neutron-capture reactions and amphiphilic scintillator solution as a fluorescent sensitizer. Polystyrene was functionalized by trimethoxysilyl group in order to enable the covalent incorporation of aromatic functional groups into the inorganic sol-gel matrices for minimizing macroscopic phase segregation and facilitating lithium-6 doping in the sol-gel samples. Neutron and alpha responses of these hybrid polystyrene-silica monoliths were explored

  14. SYNGAS PRODUCTION FROM CO2-REFORMING OF CH4 OVER SOL-GEL SYNTHESIZED Ni-Co/Al2O3-MgO-ZrO2 NANOCATALYST: EFFECT OF ZrO2 PRECURSOR ON CATALYST PROPERTIES AND PERFORMANCE

    Directory of Open Access Journals (Sweden)

    Seyed Mehdi Sajjadi

    2015-05-01

    Full Text Available Ni-Co/Al2O3-MgO-ZrO2 nanocatalyst with utilization of two different zirconia precursors, namely, zirconyl nitrate hydrate (ZNH and zirconyl nitrate solution (ZNS, was synthesized via the sol-gel method. The physiochemical properties of nanocatalysts were characterized by XRD, FESEM, EDX, BET and FTIR analyses and employed for syngas production from CO2-reforming of CH4. XRD patterns, exhibiting proper crystalline structure and homogeneous dispersion of active phase for the nanocatalyst ZNS precursor employed (NCAMZ-ZNS. FESEM and BET results of NCAMZ-ZNS presented more uniform morphology and smaller particle size and consequently higher surface areas. In addition, average particle size of NCAMZ-ZNS was 15.7 nm, which is close to the critical size for Ni-Co catalysts to avoid carbon formation. Moreover, FESEM analysis indicated both prepared samples were nanoscale. EDX analysis confirmed the existence of various elements used and also supported the statements made in the XRD and FESEM analyses regarding dispersion. Based on the excellent physiochemical properties, NCAMZ-ZNS exhibited the best reactant conversion across all of the evaluated temperatures, e.g. CH4 and CO2 conversions were 97.2 and 99% at 850 ºC, respectively. Furthermore, NCAMZ-ZNS demonstrated a stable yield with H2/CO close to unit value during the 1440 min stability test.

  15. Thoria sol-gel processes

    International Nuclear Information System (INIS)

    Matthews, R.B.

    1978-10-01

    Alternate fuel fabrication techniques are being developed at WNRE as part of the thorium fuel cycle program. The sol-gel techniques are attractive and this report assembles and summarizes information relating to thoria sol-gel fuels. Some background information on the behaviour and advantages of sol-gel fuel forms is presented, followed by a review of relevant colloid chemistry and an explanation of the fundamental steps of sol-gel processes. Finally, several variants to the basic process are reviewed and evaluated. (author)

  16. In Vitro and In Vivo Evaluation of Sol-Gel Derived TiO2 Coatings Based on a Variety of Precursors and Synthesis Conditions

    Directory of Open Access Journals (Sweden)

    Krzysztof Marycz

    2014-01-01

    Full Text Available The effect of synthesis way of TiO2 coatings on biocompatibility of transplanted materials using an in vitro and in vivo rat model was investigated. TiO2 layers were synthesized by a nonaqueous sol-gel dip-coating method on stainless steel 316L substrates applying two different precursors and their combination. Morphology and topography of newly formed biomaterials were determined as well as chemical composition and elemental distribution of a surface samples. In vitro tests were conducted by adipose-derived mesenchymal stem cells cultured on TiO2 coatings and stainless steel without coatings to assess the bioreactivity of obtained materials. A positive biological effect of TiO2/316L/1 coatings—based on titanium(IV ethoxide—was found in both in vitro and in vivo models. The TiO2/316L/1 exhibited the highest roughness and the lowest titanium concentration in TiO2 than TiO2/316L/2—based on titanium(IV propoxide and TiO2/316L/3—based on both above-mentioned precursors. The proper fibroblast-like morphology and higher proliferation rate of cells cultured on TiO2/316L/1 were observed when compared to the other biomaterials. No inflammatory response in the bone surrounding implant covered by each of the obtained TiO2 was present. Our results showed that improvement of routinely used stainless steel 316L with TiO2/316L/1 layer can stimulate beneficial biological response.

  17. Hydroxyapatite, fluor-hydroxyapatite and fluorapatite produced via the sol-gel method. Optimisation, characterisation and rheology.

    Science.gov (United States)

    Tredwin, Christopher J; Young, Anne M; Georgiou, George; Shin, Song-Hee; Kim, Hae-Won; Knowles, Jonathan C

    2013-02-01

    Currently, most titanium implant coatings are made using hydroxyapatite and a plasma spraying technique. There are however limitations associated with plasma spraying processes including poor adherence, high porosity and cost. An alternative method utilising the sol-gel technique offers many potential advantages but is currently lacking research data for this application. It was the objective of this study to characterise and optimise the production of Hydroxyapatite (HA), fluorhydroxyapatite (FHA) and fluorapatite (FA) using a sol-gel technique and assess the rheological properties of these materials. HA, FHA and FA were synthesised by a sol-gel method. Calcium nitrate and triethylphosphite were used as precursors under an ethanol-water based solution. Different amounts of ammonium fluoride (NH4F) were incorporated for the preparation of the sol-gel derived FHA and FA. Optimisation of the chemistry and subsequent characterisation of the sol-gel derived materials was carried out using X-ray Diffraction (XRD) and Differential Thermal Analysis (DTA). Rheology of the sol-gels was investigated using a viscometer and contact angle measurement. A protocol was established that allowed synthesis of HA, FHA and FA that were at least 99% phase pure. The more fluoride incorporated into the apatite structure; the lower the crystallisation temperature, the smaller the unit cell size (changes in the a-axis), the higher the viscosity and contact angle of the sol-gel derived apatite. A technique has been developed for the production of HA, FHA and FA by the sol-gel technique. Increasing fluoride substitution in the apatite structure alters the potential coating properties. Crown Copyright © 2012. Published by Elsevier Ltd. All rights reserved.

  18. Synthesis and Characterization of Fluoro- and Chlorobimetallic Alkoxides as Precursors for Luminescent Metal Oxide Materials via Sol-Gel Technique

    Institute of Scientific and Technical Information of China (English)

    ATHAR, Taimur; SEOK, Sang II; KWON, Jeong Oh

    2007-01-01

    Heterobimetallic alkoxides are broadly recognized as versatile precursors for luminescence materials, and efforts are being made to develop novel routes by applying the concept of geometrical molecular design, for their synthesis and to design a single source precursor suited to photoluminescent materials. Novel and new series of bimetallic alkoxides has been prepared by metathesis route. They exhibit a lower sensitivity towards hydrolysis and so they are easier to handle as compared to other alkoxides. All the compounds were characterized by elemental analysis, FT-IR and multinuclear NMR spectroscopies. FT-IR revealed that the molecular structure of these metal spectroscopy provided useful information about chemical shifts for better understanding the likely structure based on interactions with their coordinate metals. The mass spectra show similar types of fragmentation pattern.SEM-EDS analyses showed consistency with the formulation. XRD patterns show an enhanced homogeneity at high temperature. TGA measurements show that thermal decomposition occured in steps that depended entirely on the chemical compositions and the synthesis routes. SEM observation reveals that the morphology and particle size strongly depend on synthesis routes for their precursors.

  19. Photodegradation of indigo carmine and methylene blue dyes in aqueous solution by SiC-TiO{sub 2} catalysts prepared by sol-gel

    Energy Technology Data Exchange (ETDEWEB)

    Gomez-Solis, Christian [Facultad de Ciencias Quimicas, Universidad Autonoma de San Luis Potosi, San Luis Potosi Av. Manuel Nava 6, San Luis Potosi, S.L.P. 78290 (Mexico); Juarez-Ramirez, Isaias, E-mail: isajua13@yahoo.com [Departamento de Ecomateriales y Energia, Facultad de Ingenieria Civil, Universidad Autonoma de Nuevo Leon, Cd. Universitaria, San Nicolas de los Garza, Nuevo Leon 66450 (Mexico); Moctezuma, Edgar [Facultad de Ciencias Quimicas, Universidad Autonoma de San Luis Potosi, San Luis Potosi Av. Manuel Nava 6, San Luis Potosi, S.L.P. 78290 (Mexico); Torres-Martinez, Leticia M. [Departamento de Ecomateriales y Energia, Facultad de Ingenieria Civil, Universidad Autonoma de Nuevo Leon, Cd. Universitaria, San Nicolas de los Garza, Nuevo Leon 66450 (Mexico)

    2012-05-30

    Highlights: Black-Right-Pointing-Pointer Photodegradation of organic dyes is possible using sol-gel SiC-TiO{sub 2} catalysts. Black-Right-Pointing-Pointer SiC-TiO{sub 2} makes a synergy effect that enhances its catalytic activity. Black-Right-Pointing-Pointer Sol-gel allows good dispersion and attachment of TiO{sub 2} particles on SiC surface. Black-Right-Pointing-Pointer SiC-TiO{sub 2} exhibits better activity than TiO{sub 2} (P25) on organic dyes degradation. Black-Right-Pointing-Pointer SiC-TiO{sub 2} catalysts are settled down and easily separated after photocatalysis. - Abstract: Indigo carmine and methylene blue dyes in aqueous solution were photodegraded using SiC-TiO{sub 2} catalysts prepared by sol-gel method. After thermal treatment at 450 Degree-Sign C, SiC-TiO{sub 2} catalysts prepared in this work showed the presence of SiC and TiO{sub 2} anatase phase. Those compounds showed specific surface area values around 22-25 m{sup 2} g{sup -1}, and energy band gap values close to 3.05 eV. In comparison with TiO{sub 2} (P25), SiC-TiO{sub 2} catalysts showed the highest activity for indigo carmine and methylene blue degradation, but this activity cannot be attributed to the properties above mentioned. Therefore, photocatalytic performance is due to the synergy effect between SiC and TiO{sub 2} particles caused by the sol-gel method used to prepare the SiC-TiO{sub 2} catalysts. TiO{sub 2} nanoparticles are well dispersed onto SiC surface allowing the transfer of electronic charges between SiC and TiO{sub 2} semiconductors, which avoid the fast recombination of the electron-hole pair during the photocatalytic process.

  20. Nanocrystal/sol-gel nanocomposites

    Science.gov (United States)

    Petruska, Melissa A [Los Alamos, NM; Klimov, Victor L [Los Alamos, NM

    2007-06-05

    The present invention is directed to solid composites including colloidal nanocrystals within a sol-gel host or matrix and to processes of forming such solid composites. The present invention is further directed to alcohol soluble colloidal nanocrystals useful in formation of sol-gel based solid composites.

  1. Sol-gel synthesis of hydroxyapatite; Sintese de hidroxiapatita via sol-gel

    Energy Technology Data Exchange (ETDEWEB)

    Zupanski, M.D.; Lucena, M.P.P.; Bergmann, C.P., E-mail: michelledunin@yahoo.com.b [Universidade Federal do Rio Grande do Sul (UFRGS), Porto Alegre, RS (Brazil)

    2010-07-01

    Hydroxyapatite (HAp) has been established as the calcium phosphate based compound with most applications in the biological field. Among the numerous techniques for synthesis of HAp, the sol-gel processing route affords great control over purity and formed phases using low processing temperatures. In addition, the sol-gel approach offers an option for homogeneous HAp coating on metal substrates, as well as the ability to generate nanocrystalline powders. In this work, the sol-gel synthesis of HAp was investigated employing triethyl phosphate and calcium nitrate tetrahydrate as phosphorous and calcium precursors, respectively. The aging effect on phase composition and powder morphology of the final product was studied in terms of temperature and aging time. The powders were studied by using X-ray diffraction, Fourier transform infrared spectroscopy, particle size distribution by laser diffraction and scanning electron microscopy. (author)

  2. BNT-BT{sub 0.08} wires derived from sol-gel precursor and their piezoelectric behavior

    Energy Technology Data Exchange (ETDEWEB)

    Cernea, M., E-mail: mcernea@infim.ro; Pintilie, L.; Trupina, L. [National Institute of Materials Physics (Romania); Vasile, B. S. [University POLITEHNICA of Bucharest (Romania); Chirila, C.; Pasuk, I. [National Institute of Materials Physics (Romania)

    2013-05-15

    Lead-free piezoelectric (Bi{sub 0.5}Na{sub 0.5}){sub 0.92}Ba{sub 0.08}TiO{sub 3}, (abbreviated as BNT-BT{sub 0.08}) wires were prepared using its corresponding precursor sol and, a polycarbonate template membrane. The polycarbonate membrane used has a thickness of 30 {mu}m and pore diameter of 300 nm. Uniform surface morphology of the wires with average diameter of 145 nm and a length of about 20 {mu}m was obtained when the concentration of the sol was 0.3 M. The ferroelectric and piezoelectric properties of an individual BNT-BT{sub 0.08} wire were investigated using the PFM technique. The hysteresis loops between the PFM phase and DC bias and, the characteristic butterfly loops of the PFM amplitude versus DC bias, indicated a ferroelectric and piezoelectric behavior of as-obtained BNT-BT{sub 0.08} wires.

  3. The structural studies of aluminosilicate gels and thin films synthesized by the sol-gel method using different Al2O3 and SiO2 precursors

    Directory of Open Access Journals (Sweden)

    Adamczyk Anna

    2015-12-01

    Full Text Available Aluminosilicate materials were obtained by sol-gel method, using different Al2O3 and SiO2 precursors in order to prepare sols based on water and organic solvents. As SiO2 precursors, Aerosil 200TM and tetraethoxysilane TEOS: Si(OC2H54 were applied, while DisperalTM and aluminium secondary butoxide ATSB: Al(OC4H93 were used for Al2O3 ones. Bulk samples were obtained by heating gels at 500 °C, 850 °C and at 1150 °C in air, while thin films were synthesized on carbon, steel and alundum (representing porous ceramics substrates by the dip coating method. Thin films were annealed in air (steel and alundum and in argon (carbon at different temperatures, depending on the substrate type. The samples were synthesized as gels and coatings of the composition corresponding the that of 3Al2O3·2SiO2 mullite because of the specific valuable properties of this material. The structure of the annealed bulk samples and coatings was studied by FT-IR spectroscopy and XRD method (in standard and GID configurations. Additionally, the electron microscopy (SEM together with EDS microanalysis were applied to describe the morphology and the chemical composition of thin films. The analysis of FT-IR spectra and X-ray diffraction patterns of bulk samples revealed the presence of γ-Al2O3 and δ-Al2O3 phases, together with the small amount of SiO2 in the particulate samples. This observation was confirmed by the bands due to vibrations of Al–O bonds occurring in γ-Al2O3 and δ-Al2O3 structures, in the range of 400 to 900 cm−1. The same phases (γ-Al2O3 and δ-Al2O were observed in the deposited coatings, but the presence of particulate ones strongly depended on the type of Al2O3 and SiO2 precursor and on the heat treatment temperature. All thin films contained considerable amounts of amorphous phase.

  4. Effect of annealing temperature on optical properties of binary zinc tin oxide nano-composite prepared by sol-gel route using simple precursors: structural and optical studies by DRS, FT-IR, XRD, FESEM investigations.

    Science.gov (United States)

    Habibi, Mohammad Hossein; Mardani, Maryam

    2015-02-25

    Binary zinc tin oxide nano-composite was synthesized by a facile sol-gel method using simple precursors from the solutions consisting of zinc acetate, tin(IV) chloride and ethanol. Effect of annealing temperature on optical and structural properties was investigated using X-ray diffraction (XRD), diffuse reflectance spectra (DRS), field emission scanning electron microscopy (FESEM) and Fourier transform infrared spectroscopy (FTIR). XRD results revealed the existence of the ZnO and SnO2 phases. FESEM results showed that binary zinc tin oxide nano-composites ranges from 56 to 60 nm in diameter at 400°C and 500°C annealing temperatures respectively. The optical band gap was increased from 2.72 eV to 3.11 eV with the increasing of the annealing temperature. FTIR results confirmed the presence of zinc oxide and tin oxide and the broad absorption peaks at 3426 and 1602 cm(-1) can be ascribed to the vibration of absorptive water, and the absorption peaks at 546, 1038 and 1410 cm(-1) are due to the vibration of Zn-O or Sn-O groups in binary zinc tin oxide. Copyright © 2014 Elsevier B.V. All rights reserved.

  5. The influence of phosphorus precursors on the synthesis and bioactivity of SiO2-CaO-P 2O 5 sol-gel glasses and glass-ceramics.

    Science.gov (United States)

    Siqueira, Renato Luiz; Zanotto, Edgar Dutra

    2013-02-01

    Bioactive glasses and glass-ceramics of the SiO(2)-CaO-P(2)O(5) system were synthesised by means of a sol-gel method using different phosphorus precursors according to their respective rates of hydrolysis-triethylphosphate (OP(OC(2)H(5))(3)), phosphoric acid (H(3)PO(4)) and a solution prepared by dissolving phosphorus oxide (P(2)O(5)) in ethanol. The resulting materials were characterised by differential scanning calorimetry and thermogravimetry, X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy coupled with energy dispersive X-ray spectroscopy and by in vitro bioactivity tests in acellular simulated body fluid. The different precursors significantly affected the main steps of the synthesis, beginning with the time required for gel formation. The most striking influence of these precursors was observed during the thermal treatments at 700-1,200 °C that were used to convert the gels into glasses and glass-ceramics. The samples exhibited very different mineralisation behaviours; especially those prepared using the phosphoric acid, which had a reduced onset temperature of crystallisation and an increased resistance to devitrification. However, all resulting materials were bioactive. The in vitro bioactivity of these materials was strongly affected by the heat treatment temperature. In general, their bioactivity decreased with increasing treatment temperature. For crystallised samples obtained above 900 °C, the bioactivity was favoured by the presence of two crystalline phases: wollastonite (CaSiO(3)) and tricalcium phosphate (α-Ca(3)(PO(4))(2)).

  6. Ternary Phase-Separation Investigation of Sol-Gel Derived Silica from Ethyl Silicate 40

    Science.gov (United States)

    Wang, Shengnan; Wang, David K.; Smart, Simon; Diniz da Costa, João C.

    2015-01-01

    A ternary phase-separation investigation of the ethyl silicate 40 (ES40) sol-gel process was conducted using ethanol and water as the solvent and hydrolysing agent, respectively. This oligomeric silica precursor underwent various degrees of phase separation behaviour in solution during the sol-gel reactions as a function of temperature and H2O/Si ratios. The solution composition within the immiscible region of the ES40 phase-separated system shows that the hydrolysis and condensation reactions decreased with decreasing reaction temperature. A mesoporous structure was obtained at low temperature due to weak drying forces from slow solvent evaporation on one hand and formation of unreacted ES40 cages in the other, which reduced network shrinkage and produced larger pores. This was attributed to the concentration of the reactive sites around the phase-separated interface, which enhanced the condensation and crosslinking. Contrary to dense silica structures obtained from sol-gel reactions in the miscible region, higher microporosity was produced via a phase-separated sol-gel system by using high H2O/Si ratios. This tailoring process facilitated further condensation reactions and crosslinking of silica chains, which coupled with stiffening of the network, made it more resistant to compression and densification. PMID:26411484

  7. Preparation of CuAlO2 Thin Films by Sol-Gel Method Using Nitrate Solution Dip-Coating

    Directory of Open Access Journals (Sweden)

    Ehara Takashi

    2016-01-01

    Full Text Available CuAlO2 thin films are prepared by sol-gel dip-coating followed by annealing in nitrogen atmosphere using copper nitrate and aluminum nitrate as metal source materials. X-ray diffraction (XRD patterns show (003, (006 and (009 oriented peaks of CuAlO2 at annealing temperature of 800 – 1000°C. This result indicates that the CuAlO2 films prepared in the present work are c-axis oriented. XRD peak intensity increase with annealing temperature and becomes maximum at 850°C. The CuAlO2 XRD peak decreased at annealing temperature of 900°C with appearance of a peak of CuO, and then increased again with annealing temperature until 1000 °C. The films have bandgap of 3.4 eV at annealing temperature of 850°C in which the transparency becomes the highest. At the annealing temperature of 850°C, scanning electron microscope (SEM observation reveals that the films are consist of amorphous fraction and microcrystalline CuAlO2 fraction.

  8. Production of continuous mullite fiber via sol-gel processing

    Science.gov (United States)

    Tucker, Dennis S.; Sparks, J. Scott; Esker, David C.

    1990-01-01

    The development of a continuous ceramic fiber which could be used in rocket engine and rocket boosters applications was investigated at the Marshall Space Flight Center. Methods of ceramic fiber production such as melt spinning, chemical vapor deposition, and precursor polymeric fiber decomposition are discussed and compared with sol-gel processing. The production of ceramics via the sol-gel method consists of two steps, hydrolysis and polycondensation, to form the preceramic, followed by consolidation into the glass or ceramic structure. The advantages of the sol-gel method include better homogeneity and purity, lower preparation temperature, and the ability to form unique compositions. The disadvantages are the high cost of raw materials, large shrinkage during drying and firing which can lead to cracks, and long processing times. Preparation procedures for aluminosilicate sol-gel and for continuous mullite fibers are described.

  9. Spatially resolved speckle-correlometry of sol-gel transition

    Science.gov (United States)

    Isaeva, A. A.; Isaeva, E. A.; Pantyukov, A. V.; Zimnyakov, D. A.

    2018-04-01

    Sol-gel transition was studied using the speckle correlometry method with a localized light source and spatial filtering of backscattered radiation. Water solutions of technical or food gelatin with added TiO2 nanoparticles were used as studied objects. Structural transformation of "sol-gel" system was studied at various temperatures from 25°C to 50°C using analysis of the correlation and structure functions of speckle intensity fluctuations. The characteristic temperatures of "sol - gel" transition were evaluated for studied systems. Obtained results can be used for various applications in biomedicine and food industry.

  10. Sol-Gel Chemistry for Carbon Dots.

    Science.gov (United States)

    Malfatti, Luca; Innocenzi, Plinio

    2018-03-14

    Carbon dots are an emerging class of carbon-based nanostructures produced by low-cost raw materials which exhibit a widely-tunable photoluminescence and a high quantum yield. The potential of these nanomaterials as a substitute of semiconductor quantum dots in optoelectronics and biomedicine is very high, however they need a customized chemistry to be integrated in host-guest systems or functionalized in core-shell structures. This review is focused on recent advances of the sol-gel chemistry applied to the C-dots technology. The surface modification, the fine tailoring of the chemical composition and the embedding into a complex nanostructured material are the main targets of combining sol-gel processing with C-dots chemistry. In addition, the synergistic effect of the sol-gel precursor combined with the C-dots contribute to modify the intrinsic chemo-physical properties of the dots, empowering the emission efficiency or enabling the tuning of the photoluminescence over a wide range of the visible spectrum. © 2018 The Chemical Society of Japan & Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  11. Sol-gel growth of vanadium dioxide

    International Nuclear Information System (INIS)

    Speck, K.R.

    1990-01-01

    This thesis examines the chemical reactivity of vanadium (IV) tetrakis(t-butoxide) as a precursor for the sol-gel synthesis of vanadium dioxide. Hydrolysis and condensation of the alkoxide was studied by FTIR spectroscopy. Chemical modification of the vanadium tetraalkoxide by alcohol interchange was studied using 51 V NMR and FTIR. Vanadium dioxide thin films and powders were made from vanadium tetrakis(t-butoxide) by standard sol-gel techniques. Post-deposition heating under nitrogen was necessary to transform amorphous gels into vanadium dioxide. Crystallization of films and powders was studied by FTIR, DSC, TGA, and XRD. Gel-derived vanadium dioxide films undergo a reversible semiconductor-to-metal phase transition near 68C, exhibiting characteristic resistive and spectral changes. The electrical resistance decreased by two to three orders of magnitude and the infrared transmission sharply dropped as the material was cycled through this thermally induced phase transition. The sol-gel method was also used to make doped vanadium dioxide films. Films were doped with tungsten and molybdenum ions to effectively lower the temperature at which the transition occurs

  12. Sol-gel derived antireflective coatings for silicon

    Energy Technology Data Exchange (ETDEWEB)

    Brinker, C J; Harrington, M S

    1981-08-01

    The preparation of TiO2-SiO2 AR coatings, containing from 30 to 95 mol % TiO2, from alkoxide precursor solutions (titanium tetraethoxide and silicon tetraethoxide) by a sol-gel process is presented. The preparation of the solutions is described, which involves the separate partial hydrolysis of one or both alkoxides prior to their mixing (Yoldas, 1980). The solutions are applied to polished, circular (1 and 2 in. diameter) silicon wafers by a spinning process. The coated wafers are successively heated in air at each of the following temperatures: 200, 300, 350, 400, and 450 C, and optical measurements are performed on them after each heat treatment. The durability of 90 and 95% TiO2 coatings is evaluated in both acidic and basic environments, and reflectivity, film thickness, and refractive index are measured as a function of exposure time. It is shown that sol-gel films applied at 400 C reveal broad regions of antireflectance compared to other titanium-based films.

  13. Sol-gel bonding of silicon wafers

    International Nuclear Information System (INIS)

    Barbe, C.J.; Cassidy, D.J.; Triani, G.; Latella, B.A.; Mitchell, D.R.G.; Finnie, K.S.; Bartlett, J.R.; Woolfrey, J.L.; Collins, G.A.

    2005-01-01

    Low temperature bonding of silicon wafers was achieved using sol-gel technology. The initial sol-gel chemistry of the coating solution was found to influence the mechanical properties of the resulting bonds. More precisely, the influence of parameters such as the alkoxide concentration, water-to-alkoxide molar ratio, pH, and solution aging on the final bond morphologies and interfacial fracture energy was studied. The thickness and density of the sol-gel coating were characterised using ellipsometry. The corresponding bonded specimens were investigated using attenuated total reflectance Fourier transformed infrared spectroscopy to monitor their chemical composition, infrared imaging to control bond integrity, and cross-sectional transmission electron microscopy to study their microstructure. Their interfacial fracture energy was measured using microindentation. An optimum water-to-alkoxide molar ratio of 10 and hydrolysis water at pH = 2 were found. Such conditions led to relatively dense films (> 90%), resulting in bonds with a fracture energy of 3.5 J/m 2 , significantly higher than those obtained using classical hydrophilic bonding (typically 1.5-2.5 J/m 2 ). Ageing of the coating solution was found to decrease the bond strength

  14. Sol-Gel Manufactured Energetic Materials

    Science.gov (United States)

    Simpson, Randall L.; Lee, Ronald S.; Tillotson, Thomas M.; Hrubesh, Lawrence W.; Swansiger, Rosalind W.; Fox, Glenn A.

    2005-05-17

    Sol-gel chemistry is used for the preparation of energetic materials (explosives, propellants and pyrotechnics) with improved homogeneity, and/or which can be cast to near-net shape, and/or made into precision molding powders. The sol-gel method is a synthetic chemical process where reactive monomers are mixed into a solution, polymerization occurs leading to a highly cross-linked three dimensional solid network resulting in a gel. The energetic materials can be incorporated during the formation of the solution or during the gel stage of the process. The composition, pore, and primary particle sizes, gel time, surface areas, and density may be tailored and controlled by the solution chemistry. The gel is then dried using supercritical extraction to produce a highly porous low density aerogel or by controlled slow evaporation to produce a xerogel. Applying stress during the extraction phase can result in high density materials. Thus, the sol-gel method can be used for precision detonator explosive manufacturing as well as producing precision explosives, propellants, and pyrotechnics, along with high power composite energetic materials.

  15. Optical Studies on Sol-Gel Derived Lead Chloride Crystals

    OpenAIRE

    Rejeena, I; Lillibai, B; Nithyaja, B; Nampoori, P.N V; Radhakrishnan, P

    2013-01-01

    Optical characterization of lead chloride crystals prepared by sol-gel method is reported. The relevant sol-gel technique is used for the preparation of PbCl2 samples with five different types. In this paper, we report the absorption and fluorescence behaviour of pure, UV& IR irradiated and electric & magnetic field applied lead chloride crystal samples in solution phase at two different concentrations. Optical bandgap and emission studies of these crystals are also done.

  16. Silica Sol-Gel Entrapment of the Enzyme Chloro peroxidase

    International Nuclear Information System (INIS)

    Le, T.; Chan, S.; Ebaid, B.; Sommerhalter, M.

    2015-01-01

    The enzyme chloro peroxidase (CPO) was immobilized in silica sol-gel beads prepared from tetramethoxysilane. The average pore diameter of the silica host structure (∼3 nm) was smaller than the globular CPO diameter (∼6 nm) and the enzyme remained entrapped after sol-gel maturation. The catalytic performance of the entrapped enzyme was assessed via the pyrogallol peroxidation reaction. Sol-gel beads loaded with 4 μg CPO per mL sol solution reached 9-12% relative activity compared to free CPO in solution. Enzyme kinetic analysis revealed a decrease in K_cat but no changes in K_M or K_I . Product release or enzyme damage might thus limit catalytic performance. Yet circular dichroism and visible absorption spectra of transparent CPO sol-gel sheets did not indicate enzyme damage. Activity decline due to methanol exposure was shown to be reversible in solution. To improve catalytic performance the sol-gel protocol was modified. The incorporation of 5, 20, or 40% methyltrimethoxysilane resulted in more brittle sol-gel beads but the catalytic performance increased to 14% relative to free CPO in solution. The use of more acidic casting buffers (ph 4.5 or 5.5 instead of 6.5) resulted in a more porous silica host reaching up to 18% relative activity

  17. Sol-gel process for thermal reactor fuel fabrication

    International Nuclear Information System (INIS)

    Mukerjee, S.K.

    2008-01-01

    Full text: Sol-gel processes have revolutionized conventional ceramic technology by providing extremely fine and uniform powders for the fabrication of ceramics. The use of this technology for nuclear fuel fabrication has also been explored in many countries. Unlike the conventional sol-gel process, sol-gel process for nuclear fuels tries to eliminate the preparation of powders in view of the toxic nature of the powders particularly those of plutonium and 233 U. The elimination of powder handling thus makes this process more readily amenable for use in glove boxes or for remote handling. In this process, the first step is the preparation of microspheres of the fuel material from a solution which is then followed by vibro-compaction of these microspheres of different sizes to obtain the required smear density of fuel inside a pin. The maximum achievable packing density of 92 % makes it suitable for fast reactors only. With a view to extend the applicability of sol-gel process for thermal reactor fuel fabrication the concept of converting the gel microspheres derived from sol-gel process, to the pellets, has been under investigation for several years. The unique feature of this process is that it combines the advantages of sol-gel process for the preparation of fuel oxide gel microspheres of reproducible quality with proven irradiation behavior of the pellet fuel. One of the important pre-requisite for the success of this process is the preparation of soft oxide gel microspheres suitable for conversion to dense pellets free from berry structure. Studies on the internal gelation process, one of the many variants of sol-gel process, for obtaining soft oxide gel microspheres suitable for gel pelletisation is now under investigation at BARC. Some of the recent findings related to Sol-Gel Microsphere Pelletisation (SGMP) in urania-plutonia and thoria-urania systems will be presented

  18. Effects of parameters of sol-gel process on the phase evolution of sol-gel-derived hydroxyapatite

    International Nuclear Information System (INIS)

    Eshtiagh-Hosseini, Hossein; Housaindokht, Mohammad Reza; Chahkandi, Mohammad

    2007-01-01

    It has been established that hydroxyapatite powders can be produced using an alkoxide-based sol-gel technique. Nanocrystalline powders of hydroxyapatite (HA) were prepared from Ca(NO 3 ) 2 .4H 2 O and PO(OC 2 H 5 ) 3 as calcium and phosphorus precursors, respectively, using a sol-gel route. For a number of samples, sol of phosphorus was first hydrolyzed for 24 h with distilled water. The sol temperature, aging time and heat treatment temperature on apatite formation were systematically studied. Increasing the aging time affected the reducing of CaO. Also, increasing the mixed sol solution temperature up to 80 deg. C had a positive effect on the disappearance of impurity phases. With the increase of the calcination temperature >600 deg. C, calcium phosphate impurity phases disappeared. Structural evolution during the synthesis of hydroxyapatite is investigated by using infrared (IR) analysis, X-ray diffraction (XRD), thermal behavior (DTA), and elemental analysis of electron microscopy examination (SEM). X-ray diffraction with the aid of Scherrer and Williamson-Hall equations has been used to characterize the distributions of crystallite size and micro-strain of HA powders .The results indicated that mean crystallite size increased and micro-strain decreased significantly with the rise in firing temperature

  19. Ionogel Electrolytes through Sol-Gel Processing

    Science.gov (United States)

    Horowitz, Ariel I.

    Electrical energy needs have intensified due to the ubiquity of personal electronics, the decarbonization of energy services through electrification, and the use of intermittent renewable energy sources. Despite developments in mechanical and thermal methods, electrochemical technologies are the most convenient and effective means of storing electrical energy. These technologies include both electrochemical cells, commonly called batteries, and electrochemical double-layer capacitors, or "supercapacitors", which store energy electrostatically. Both device types require an ion-conducting electrolyte. Current devices use solutions of complex salts in organic solvents, leading to both toxicity and flammability concerns. These drawbacks can be avoided by replacing conventional electrolytes with room-temperature molten salts, known as ionic liquids (ILs). ILs are non-volatile, non-flammable, and offer high conductivity and good electrochemical stability. Device mass can be reduced by combining ILs with a solid scaffold material to form an "ionogel," further improving performance metrics. In this work, sol-gel chemistry is explored as a means of forming ionogel electrolytes. Sol-gel chemistry is a solution-based, industrially-relevant, well-studied technique by which solids such as silica can be formed in situ. Previous works used a simple acid-catalyzed sol-gel reaction to create brittle, glassy ionogels. Here, both the range of products that can be accomplished through sol-gel processing and the understanding of interactions between ILs and the sol-gel reaction network are greatly expanded. This work introduces novel ionogel materials, including soft and compliant silica-supported ionogels and PDMS-supported ionogels. The impacts of the reactive formulation, IL identity, and casting time are detailed. It is demonstrated that variations in formulation can lead to rapid gelation and open pore structures in the silica scaffold or slow gelation and more dense silica

  20. Hydroxyapatite, fluor-hydroxyapatite and fluorapatite produced via the sol-gel method: bonding to titanium and scanning electron microscopy.

    Science.gov (United States)

    Tredwin, Christopher J; Georgiou, George; Kim, Hae-Won; Knowles, Jonathan C

    2013-05-01

    Hydroxyapatite (HA), fluor-hydroxyapatite (FHA) with varying levels of fluoride ion substitution and fluorapatite (FA) production has been characterised and optimised by the sol-gel method and the dissolution and biological properties of these materials were investigated. It was the objective of this study to investigate the potential bond strength and interaction of these materials with titanium. HA, FHA and FA were synthesised by a sol-gel method. Calcium nitrate and triethyl phosphite were used as precursors under an ethanol-water based solution. Different amounts of ammonium fluoride (NH4F) were incorporated for the preparation of the FHA and FA sol-gels. Using a spin coating technique the sol-gels were coated onto commercially pure titanium disks and crystallised at various temperatures. Using scanning electron microscopy (SEM) and elemental analysis, the surface characteristics, coating thickness and interaction of the Ti substrate and coating were investigated. The bond strengths of the coating to the Ti were investigated using an Instron Universal Load Testing Machine. Statistical analysis was performed with a two-way analysis of variance and post hoc testing with a Bonferroni correction. (1) Coating speed inversely influenced the coating thickness. (2) Increasing fluoride ion substitution and heating temperature significantly increased bond strength and (3) increasing fluoride ion substitution increased the coating thickness. FHA and FA synthesised using the sol-gel technique may offer a superior alternative to coating titanium implants with HA and plasma spraying. HA, FHA and FA materials synthesised by the sol-gel method may also have a use as bone grafting materials. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  1. New insights into uranium (VI) sol-gel processing

    International Nuclear Information System (INIS)

    King, C.M.; Thompson, M.C.; Buchanan, B.R.; King, R.B.; Garber, A.R.

    1990-01-01

    Nuclear Magnetic Resonance (NMR) investigations on the Oak Ridge National Laboratory process for sol-gel synthesis of microspherical nuclear fuel (UO 2 ), has been extremely useful in sorting out the chemical mechanism in the sol-gel steps. 13 C, 15 N, and 1 H NMR studies on the HMTA gelation agent (Hexamethylene tetramine, C 6 H 12 N 4 ) has revealed near quantitative stability of this adamantane-like compound in the sol-gel process, contrary to its historical role as an ammonia source for gelation from the worldwide technical literature. 17 O NMR of uranyl (UO 2 ++ ) hydrolysis fragments produced in colloidal sols has revealed the selective formation of a uranyl trimer, [(UO 2 ) 3 (μ 3 -O)(μ 2 -OH) 3 ] + , induced by basic hydrolysis with the HMTA gelation agent. Spectroscopic results will be presented to illustrate that trimer condensation occurs during sol-gel processing leading to layered polyanionic hydrous uranium oxides in which HMTAH + is occluded as an ''intercalation'' cation. Subsequent sol-gel processing of microspheres by ammonia washing results in in-situ exchange and formation of a layered hydrous ammonium uranate with a proposed structural formula of (NH 4 ) 2 [(UO 2 ) 8 O 4 (OH) 10 ] · 8H 2 O. This compound is the precursor to sintered UO 2 ceramic fuel. 23 refs., 10 figs

  2. Sol-gel encapsulation for controlled drug release and biosensing

    Science.gov (United States)

    Fang, Jonathan

    The main focus of this dissertation is to investigate the use of sol-gel encapsulation of biomolecules for controlled drug release and biosensing. Controlled drug release has advantages over conventional therapies in that it maintains a constant, therapeutic drug level in the body for prolonged periods of time. The anti-hypertensive drug Captopril was encapsulated in sol-gel materials of various forms, such as silica xerogels and nanoparticles. The primary objective was to show that sol-gel silica materials are promising drug carriers for controlled release by releasing Captopril at a release rate that is within a therapeutic range. We were able to demonstrate desired release for over a week from Captopril-doped silica xerogels and overall release from Captopril-doped silica nanoparticles. As an aside, the antibiotic Vancomycin was also encapsulated in these porous silica nanoparticles and desired release was obtained for several days in-vitro. The second part of the dissertation focuses on immobilizing antibodies and proteins in sol-gel to detect various analytes, such as hormones and amino acids. Sol-gel competitive immunoassays on antibody-doped silica xerogels were used for hormone detection. Calibration for insulin and C-peptide in standard solutions was obtained in the nM range. In addition, NASA-Ames is also interested in developing a reagentless biosensor using bacterial periplasmic binding proteins (bPBPs) to detect specific biomarkers, such as amino acids and phosphate. These bPBPs were doubly labeled with two different fluorophores and encapsulated in silica xerogels. Ligand-binding experiments were performed on the bPBPs in solution and in sol-gel. Ligand-binding was monitored by fluorescence resonance energy transfer (FRET) between the two fluorophores on the bPBP. Titration data show that one bPBP has retained its ligand-binding properties in sol-gel.

  3. Analyses of laser and furnace treated sol-gel coatings

    NARCIS (Netherlands)

    De Hosson, JT; De Haas, M; Sudarshan, TS; Jeandin, M; Khor, KA

    1998-01-01

    Here we explore a new method that allows thin films to be made with almost any composition and degree of porosity by means of a combination of sol-gel and laser technology. Results are presented for furnace and laser treated TEOTI-(tetraethylorthotitanate as sol precursor) coated silicon samples.

  4. Facile and green preparation of novel adsorption materials by combining sol-gel with ion imprinting technology for selective removal of Cu(II) ions from aqueous solution

    Science.gov (United States)

    Ren, Zhongqi; Zhu, Xinyan; Du, Jian; Kong, Delong; Wang, Nian; Wang, Zhuo; Wang, Qi; Liu, Wei; Li, Qunsheng; Zhou, Zhiyong

    2018-03-01

    A novel green adsorption polymer was prepared by ion imprinted technology in conjunction with sol-gel process under mild conditions for the selective removal of Cu(II) ions from aqueous solution. Effects of preparation conditions on adsorption performance of prepared polymers were studied. The ion-imprinted polymer was prepared using Cu(II) ion as template, N-[3-(2-aminoethylamino) propyl] trimethoxysilane (AAPTMS) as functional monomer and tetraethyl orthosilicate (TEOS) as cross-linker. Water was used as solvent in the whole preparation process. The imprinted and non-imprinted polymers were characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM), atomic force microscope (AFM), Brunauer, Emmett and Teller (BET) and zeta potential. Three-dimensional network structure was formed and functional monomer was successfully cross-linked into the network structure of polymers. Effects of adsorption conditions on adsorption performance of prepared polymers were studied too. The pH value is of great influence on adsorption behavior. Adsorption by ion-imprinted polymer was fast (adsorption equilibrium was reached within 60 min). The adsorption capacity of Cu(II) ion-imprinted polymer was always larger than that of non-imprinted polymer. Pseudo-second-order kinetics model and Freundlich isotherm model fitted well with adsorption data. The maximum adsorption capacity of Cu(II) ion-imprinted polymer was 39.82 mg·g-1. However, the preparation conditions used in this work are much milder than those reported in literatures. The Cu(II) ion-imprinted polymer showed high selectivity and relative selectivity coefficients for Pb(II), Ni(II), Cd(II) and Co(II). In addition, the prepared ion-imprinted polymer could be reused several times without significant loss of adsorption capacity.

  5. Sol-Gel Glasses

    Science.gov (United States)

    Mukherjee, S. P.

    1985-01-01

    Multicomponent homogeneous, ultrapure noncrystalline gels/gel derived glasses are promising batch materials for the containerless glass melting experiments in microgravity. Hence, ultrapure, homogeneous gel precursors could be used to: (1) investigate the effect of the container induced nucleation on the glass forming ability of marginally glass forming compositions; and (2) investigate the influence of gravity on the phase separation and coarsening behavior of gel derived glasses in the liquid-liquid immiscibility zone of the nonsilicate systems having a high density phase. The structure and crystallization behavior of gels in the SiO2-GeO2 as a function of gel chemistry and thermal treatment were investigated. As are the chemical principles involved in the distribution of a second network former in silica gel matrix being investigated. The procedures for synthesizing noncrystalline gels/gel-monoliths in the SiO2-GeO2, GeO2-PbO systems were developed. Preliminary investigations on the levitation and thermal treatment of germania silicate gel-monoliths in the Pressure Facility Acoustic Levitator were done.

  6. Sequential determination of urea and HMTA in the process solution of sol-gel route of advanced nuclear fuel fabrication

    International Nuclear Information System (INIS)

    Sawant, R.M.; Chaudhuri, N.K.; Ramakumar, K.L.

    2002-01-01

    Determinations of hexamethylene tetramine (HMTA) and urea in the process solutions are required to optimize their concentrations for obtaining high quality ceramic oxide microspheres, for monitoring the washing procedure and for their subsequent recovery, recycling or waste disposal. Determination of urea is the feed solution by conventional procedures is difficult as it contains HMTA. It is more so in the effluent as it contains hydrolytic products like formaldehyde, methylol derivatives of urea, ammonium nitrate and ammonium hydroxide used for washing the gel microspheres. A derivative potentiometric method using a microprocessor-based autotitrator is described. Peaks on the first derivative of the titration plot corresponded to constituents of different basicities. Urea was selectively hydrolyzed at room temperature by the catalytic action of urease enzyme leaving HMTA unaffected. Ammonium hydroxide and ammonium bicarbonate produced from urea and HMTA were sequentially titrated for the analysis of the feed solution to obtain the three corresponding peaks respectively. Two separate titrations were required for the analysis of the effluent solution, which contained free ammonia also. One aliquot was first titrated directly without adding urease (for free ammonia and HMTA) and another aliquot was titrated after treatment with urease. The end points due to the ammonia used for washing and that from urea hydrolysis merged resulting in the appearance of three peaks again. Using this sequential method the relative standard deviations were found to be 0.81% and 1.38% for urea and HMTA, respectively, in eight determinations when the aliquots contained 50 to 75 mg of urea and 75 to 125 mg of HMTA. Feed and effluent solutions of the process stream were analyzed. (author)

  7. PRODUCTION, DIELECTRIC PROPERTY AND MICROWAVE ABSORPTION PROPERTY OF SiC(Fe SOLID SOLUTION POWDER BY SOL-GEL METHOD

    Directory of Open Access Journals (Sweden)

    XIAOLEI SU

    2014-03-01

    Full Text Available SiC(Fe solid solution powders were synthesized by sol–gel method under different reaction time, using methyltriethoxysilane as the silicon and carbon source and analytic ferric chloride as the dopant, respectively. The synthesized powders have been characterized by XRD, SEM and Raman spectra. Results show that the lattice constant decreases with increasing reaction time. The electric permittivities of SiC samples were determined in the frequency range of 8.2 ~ 12.4 GHz. Results show that the permittivity of SiC decreases with increasing reaction time. The SiC(Fe solid solution powder with reaction time of 4 h with 2 mm thickness exhibit the best microwave absorption property in X-band range (8.2 - 12.4 GHz. The microwave absorption mechanism has been discussed.

  8. Sol-gel method for encapsulating molecules

    Science.gov (United States)

    Brinker, C. Jeffrey; Ashley, Carol S.; Bhatia, Rimple; Singh, Anup K.

    2002-01-01

    A method for encapsulating organic molecules, and in particular, biomolecules using sol-gel chemistry. A silica sol is prepared from an aqueous alkali metal silicate solution, such as a mixture of silicon dioxide and sodium or potassium oxide in water. The pH is adjusted to a suitably low value to stabilize the sol by minimizing the rate of siloxane condensation, thereby allowing storage stability of the sol prior to gelation. The organic molecules, generally in solution, is then added with the organic molecules being encapsulated in the sol matrix. After aging, either a thin film can be prepared or a gel can be formed with the encapsulated molecules. Depending upon the acid used, pH, and other processing conditions, the gelation time can be from one minute up to several days. In the method of the present invention, no alcohols are generated as by-products during the sol-gel and encapsulation steps. The organic molecules can be added at any desired pH value, where the pH value is generally chosen to achieve the desired reactivity of the organic molecules. The method of the present invention thereby presents a sufficiently mild encapsulation method to retain a significant portion of the activity of the biomolecules, compared with the activity of the biomolecules in free solution.

  9. Metal-silica sol-gel materials

    Science.gov (United States)

    Stiegman, Albert E. (Inventor)

    2002-01-01

    The present invention relates to a single phase metal-silica sol-gel glass formed by the co-condensation of a transition metal with silicon atoms where the metal atoms are uniformly distributed within the sol-gel glass as individual metal centers. Any transition metal may be used in the sol-gel glasses. The present invention also relates to sensor materials where the sensor material is formed using the single phase metal-silica sol-gel glasses. The sensor materials may be in the form of a thin film or may be attached to an optical fiber. The present invention also relates to a method of sensing chemicals using the chemical sensors by monitoring the chromatic change of the metal-silica sol-gel glass when the chemical binds to the sensor. The present invention also relates to oxidation catalysts where a metal-silica sol-gel glass catalyzes the reaction. The present invention also relates to a method of performing oxidation reactions using the metal-silica sol-gel glasses. The present invention also relates to organopolymer metal-silica sol-gel composites where the pores of the metal-silica sol-gel glasses are filled with an organic polymer polymerized by the sol-gel glass.

  10. The application of silicon sol-gel technology to forensic blood substitute development: Mimicking aspects of whole human blood rheology.

    Science.gov (United States)

    Stotesbury, Theresa; Illes, Mike; Wilson, Paul; Vreugdenhil, Andrew J

    2017-01-01

    Solution-gelation chemistry has promising applications in forensic synthetic blood substitute development. This research offers a silicon-based sol-gel approach to creating stable materials that share similar rheological properties to that of whole human blood samples. Room temperature, high water content, silicon sol-gels were created using the organosilane precursors 3-glycidoxypropyltrimethoxysilane and tetraethylorthosilicate along with various concentrations of filler and pigment. Shear-thinning non-Newtonian properties were observed within most formulations of the presented materials. The effects of colloidal concentration, temperature, age and filler addition on the viscosity of the sol-gels were investigated. SEM-EDS analysis was used to identify the behavior of the fillers within the film and support their inclusion for basic bloodstain pattern simulation. A final proposed candidate sol-gel was assessed using a previously reported passive drip simulation test on a hard, dry surface and passed. This works represents encouraging development in providing safe material alternatives to using whole human blood for forensic training and research. Copyright © 2016 Elsevier Ireland Ltd. All rights reserved.

  11. Low-temperature sol-gel synthesis of NaZr2P3O12

    International Nuclear Information System (INIS)

    Agrawal, D.K.; Adair, J.H.

    1990-01-01

    The NZP family of new low-expansion materials has attracted wide interest for its potential in advanced technological applications. NaZr 2 P 3 O 12 , which is the parent composition of this family, has been synthesized by the solution sol-gel method using special precursor solutions, which led to its formation (although poorly crystalline) at temperatures as low as 120 degrees C. The lowest temperature of formation of a single phase of NaZr 2 P 3 O 12 with a high degree of crystallinity was found to be 600 degrees C

  12. Silica scintillating materials prepared by sol-gel methods

    International Nuclear Information System (INIS)

    Werst, D.W.; Sauer, M.C. Jr.; Cromack, K.R.; Lin, Y.; Tartakovsky, E.A.; Trifunac, A.D.

    1993-01-01

    Silica was investigated as a rad-hard alternative to organic polymer hosts for organic scintillators. Silica sol-gels were prepared by hydrolysis of tetramethoxysilane in alcohol solutions. organic dyes were incorporated into the gels by dissolving in methanol at the sol stage of gel formation. The silica sol-gel matrix is very rad-hard. The radiation stability of silica scintillators prepared by this method is dye-limited. Transient radioluminescence was measured following excitation with 30 ps pulses of 20 MeV electrons

  13. Ceramic protective coatings applied by sol-gel or electrophoresis

    International Nuclear Information System (INIS)

    Stoch, A.

    1993-01-01

    Sol-gel and electrophoresis are the complementary techniques which may be used for obtaining the ceramic coatings. The composition of such a coatings depends on the composition of electrophoresis bath or sol solution. Thermal treatment is used for densifying the coating and promoting the adherence of coating to the substrate. In presented work silica, silica-alumina or alumina coatings are applied by sol-gel dip coating procedure on steel, aluminium or ceramic substrates. Electrophoresis is employed for obtaining zirconia, alumina or hydroxyapatite coatings on stainless steel. (author). 7 refs

  14. Fabrication of targets for transmutation of americium : synthesis of inertial matrix by sol-gel method. Procedure study on the infiltration of a radioactive solutions

    International Nuclear Information System (INIS)

    Fernandez Carretero, A.

    2002-01-01

    Transmutation and incineration are innovative options in the management and disposal of fission products and actinides. nevertheless, the fabrication of targets for transmutation and incineration of actinides and fission products require a reconsideration of conventional processes (mechanical blending) and the development of new procedures compatible with the high activity of these materials. This work presents th R and D of a new fabrication method called INRAM (Infiltration of Radioactive Materials) based on the infiltration of an actinide solution in a porous non radiotoxic material in the form of a pellet (up to 12% An), or beads (up to 40% An) produced by sol-gel. The first method have been used for the fabrication of spinel (MgAl 2 O 4 ) targets containing 11% Am, which have been irradiated in HFR-Petten (358.4 full power days). Post-test burn-up calculations showed that at the end of the irradiation the initial Am-241 concentration was reduced to 4%. The fraction of the initial americum atoms that have been fissioned is 28%. The main advantage of the INRAM method is that matrices with low or zero activity can be fabricated and formed into the required shape in an unshielded facility. This method offers other advantages over conventional ones, such as the active wastes are reduced, is easy to automate, adoptable to telemanipulation and dust free, which facilitate operator intervention and minimise radiation exposure to the personal. In addition, the infiltrant needs only be present in liquid form, i. e. it could be transferred directly from the reprocessing plant for fabrication into targets without conversion into-solid form. In order to optimise the infiltration process in depth investigations of all important process parameters, e. g. infiltration kinetics and metal (pu, Am) concentration in the feed solution, and also on extensive study or powder metallurgy parameters for the preparation of high quality fuel pellets with a high density, have been made. In

  15. Deposition of tin oxide doped with fluorine produced by sol-gel method and deposited by spray-pyrolysis

    International Nuclear Information System (INIS)

    Maia, Paulo Herbert Franca; Lima, Francisco Marcone; Sena, Aline Cosmo de; Silva, Alvaro Neuton; Almeida, Ana Fabiola Leite de; Freire, Francisco Nivaldo Aguiar

    2014-01-01

    Solar energy is one of the most important sources of renewable energy today, but its production is based on silicon cells, expensive and difficult to produce, so the research seek new materials to replace them. This work aims to deposit tin oxide doped with fluorine on the glass substrate using the sol-gel method to provide a working solution and spray pyrolysis technique to perform the deposition. F-SnO2 (FTO) were synthesized by sol-gel method, employing NH_4F and SnCl_2 precursor in an ethanol solution. Before the formation of the gel phase, the entire solution was sprayed, with the aid of a pistol aerographic substrate under heated at 600 °C divided by 50 applications and cooled in the furnace. The substrates had resistances between 10 and 30 S.cm. The energy dispersive x-ray (EDS) revealed the presence of fluorine in the SnO_2 network. (author)

  16. Variables of synthesis in obtaining nanosilicas with sol-gel

    International Nuclear Information System (INIS)

    Elia, A; Martin-Aispuro, P; Musante, L; Martin-Martinez, J.M; Vazquez, P

    2008-01-01

    Amorphous silica materials and polycrystalline are now being developed for different applications as optic components, superconductors, nano-particles used as charges in adhesives and paints, among others. Some methods of obtaining these materials involve complex techniques and high costs. Generally, the materials constituents are fused, for example, using the pyrogenic silica technique, widely used industrially. Meanwhile, the sol-gel meted is based on a mixture of liquid reagents at the molecular level, to easily obtain amorphous and polycrystalline materials, even at room temperature. Therefore, the sol-gel way is a promising option for producing new materials, due to its cost advantages compared to the traditional methods. The sol-gel technique consists of the simultaneous reaction of the hydrolysis and the condensation. In this process the precursor solution, the TEOS in our case, becomes a polymeric gel network polymer. The partial hydrolysis of the orthosilicate takes place when it is mixed with water and ethanol (EtOH), the reaction that occurs is: S i(OEt) 4 + H 2 O S i(OEt) 3 (OH) + EtOH. The condensation takes place between two OH groups or between an OH group and an ethoxy to form an oxygen bridge plus water or ethanol. S i(OEt) 4 + H 2 O + S i(OEt) 3 (OH)(EtO) 3 Si-O-Si(OEt) 3 (OH) + H 2 O S i-OH + HO-Si S i-O-Si + H 2 O. The addition of a base or of an acid catalyzes the process and changes the pH of the solution influencing the condensation process and size of the final particle. This work focuses on finding different conditions by varying the pH, using HCI, with and without agitation during the addition of the HCI, and washing the solid obtained with ethanol in order to study its effect. The nanosilicas were characterized by TEM-EDX, DTA-TGA, S BET , FT-IR, DRX, DRS, SEM and pH measurements. The morphology of the nanosilicas was characterized with SEM and TEM. Using these techniques a partial conclusion showed that the samples synthesized with HCI

  17. Sol-gel system study of Zr O2- Co3 O-4

    International Nuclear Information System (INIS)

    Cerri, J.A.; Matos, E.M.R.; Longo, E.; Varela, J.A.; Santos, C.O.P.

    1992-01-01

    Phases present in the system Zr O 2 + Co 3 O 4 were studied through X-Ray diffraction. The processing of the powder was developed through a modified sol-gel method, where the precursors Zr O (N O 3)2 and Co (N O 3)2 were in an ethanol solution. To verify the influence of CO 3 O 4 on the stabilization and phases formation, the crystallite size and the lattice parameter were determined considering as standard, the system without cobalt. (author)

  18. Sol-gel chemistry applied to the synthesis of polymetallic oxides including actinides reactivity and structure from solution to solid state

    International Nuclear Information System (INIS)

    Lemonnier, St.

    2006-02-01

    Minor actinides transmutation is studied at present in order to reduce the radiotoxicity of nuclear waste and the assessment of its technical feasibility requires specific designed materials. When considering americium, yttria stabilized zirconia (Am III YII Zriv)Or x is among the ceramic phases that one which presents the required physico-chemical properties. An innovative synthesis of this mixed oxide by sol-gel process is reported in this manuscript. The main aim of this work is to adjust the reactivity of the different metallic cations in aqueous media using complexing agent, in order to initiate a favourable interaction for a homogeneous elements repartition in the forming solid phase. The originality of the settled synthesis lies on an in-situ formation of a stable and monodisperse nano-particles dispersion in the presence of acetylacetone. The main reaction mechanisms have been identified: the sol stabilisation results from an original interaction between the three compounds (Zrly, trivalent cations and acetylacetone). The sol corresponds to a structured system at the nanometer scale for which zirconium and trivalent cations are homogeneously dispersed, preliminary to the sol-gel transition. Furthermore, preliminary studies were carried out with a view to developing materials. They have demonstrated that numerous innovative and potential applications can be developed by taking advantage of the direct and controlled formation of the sol and by adapting the sol-gel transition. The most illustrating result is the preparation of a sintered pellet with the composition Am0,13Zro,73Yo,0901,89 using this approach. (author)

  19. Sol-gel technology for biomedical engineering

    International Nuclear Information System (INIS)

    Podbielska, H.; Ulatowska-Jarza, A.

    2005-01-01

    Sol-gel derived silica possess many promising features, including low-temperature preparation procedure, porosity, chemical and physical stability. Applications exploiting porous materials to encapsulate sensor molecules, enzymes and many other compounds, are developing rapidly. In this paper some potential applications, with emphasis on biomedical and environmental ones, are reviewed. The material preparation procedure is described and practical remarks on silica-based sol-gels are included. It is reported that sol-gels with entrapped various molecules may be used in construction of implants and coatings with bioactive properties. It is shown how to exploit the sol-gel production route for construction of sol-gel coated fiberoptic applicators for laser therapy. The applications of bioactive materials are discussed, as well. It is demonstrated that it is possible to immobilize photosensitive compounds in sol-gel matrix without loosing their photoactivity. Some examples of sol-gel based biosensors are demonstrated, as well, showing their potential for detecting various gases, toxic substances, acidity, humidity, enzymes and biologically active agents. (authors)

  20. Syngas production from CO{sub 2}-reforming of CH{sub 4} over sol-gel synthesized Ni-Co/Al{sub 2}O{sub 3}-MgOZrO{sub 2} nanocatalyst: effect of ZrO{sub 2} precursor on catalyst properties and performance

    Energy Technology Data Exchange (ETDEWEB)

    Sajjadi, Seyed Mehdi; Haghighi, Mohammad; Rahmani, Farhad, E-mail: haghighi@sut.ac.ir [Reactor and Catalysis Research Center, Sahand University of Technology, Tabriz (Iran, Islamic Republic of)

    2015-05-15

    Ni-Co/Al{sub 2}O{sub 3}-MgO-ZrO{sub 2} nanocatalyst with utilization of two different zirconia precursors, namely, zirconyl nitrate hydrate (ZNH) and zirconyl nitrate solution (ZNS), was synthesized via the sol-gel method. The physiochemical properties of nanocatalysts were characterized by XRD, FESEM, EDX, BET and FTIR analyses and employed for syngas production from CO{sub 2}-reforming of CH{sub 4}. XRD patterns, exhibiting proper crystalline structure and homogeneous dispersion of active phase for the nanocatalyst ZNS precursor employed (NCAMZ-ZNS). FESEM and BET results of NCAMZ-ZNS presented more uniform morphology and smaller particle size and consequently higher surface areas. In addition, average particle size of NCAMZ-ZNS was 15.7 nm, which is close to the critical size for Ni-Co catalysts to avoid carbon formation. Moreover, FESEM analysis indicated both prepared samples were nanoscale. EDX analysis confirmed the existence of various elements used and also supported the statements made in the XRD and FESEM analyses regarding dispersion. Based on the excellent physiochemical properties, NCAMZ-ZNS exhibited the best reactant conversion across all of the evaluated temperatures, e.g. CH{sub 4} and CO{sub 2} conversions were 97.2 and 99% at 850 °C, respectively. Furthermore, NCAMZZNS demonstrated a stable yield with H{sub 2}/CO close to unit value during the 1440 min stability test. (author)

  1. Ionic liquid-silica precursors via solvent-free sol-gel process and their application in epoxy-amine network: a theoretical/experimental study

    Czech Academy of Sciences Publication Activity Database

    Perchacz, Magdalena; Donato, R. K.; Seixas, L.; Zhigunov, Alexander; Konefal, Rafal; Serkis-Rodzen, Magdalena; Beneš, Hynek

    2017-01-01

    Roč. 9, č. 19 (2017), s. 16474-16487 ISSN 1944-8244 R&D Projects: GA ČR(CZ) GA17-08273S; GA MŠk(CZ) LO1507 Institutional support: RVO:61389013 Keywords : 3D POSS structures * epoxy-silica hybrid material * IL-silica precursor Subject RIV: CD - Macromolecular Chemistry OBOR OECD: Polymer science Impact factor: 7.504, year: 2016

  2. Tough ceramic coatings: Carbon nanotube reinforced silica sol-gel

    Science.gov (United States)

    López, A. J.; Rico, A.; Rodríguez, J.; Rams, J.

    2010-08-01

    Silica coatings reinforced with carbon nanotubes were produced via sol-gel route using two mixing techniques of the sol-gel precursors, mechanical and ultrasonic mixing, and dip-coating as deposition process on magnesium alloy substrates. Effective incorporation and distribution of 0.1 wt.% of carbon nanotubes in the amorphous silica matrix of the coatings were achieved using both techniques. Fabrication procedure determines the morphological aspects of the coating. Only mechanical mixing process produced coatings dense and free of defects. Nanoindentation technique was used to examine the influence of the fabrication process in the mechanical features of the final coatings, i.e. indentation fracture toughness, Young's modulus and hardness. A maximum toughening effect of about 24% was achieved in silica coatings reinforced with carbon nanotubes produced by the mechanical mixing route. Scanning electron microscopy investigation revealed that the toughening of these reinforced coatings was mainly due to bridging effect of the reinforcement.

  3. Sol-gel antireflective coating on plastics

    Science.gov (United States)

    Ashley, Carol S.; Reed, Scott T.

    1990-01-01

    An antireflection film made from a reliquified sol-gel hydrolyzation, condensation polymeric reaction product of a silicon, alkoxides and/or metal alkoxides, or mixtures thereof. The film is particularly useful for coating plastics.

  4. Enhancement of Ce/Cr Codopant Solubility and Chemical Homogeneity in TiO2 Nanoparticles through Sol-Gel versus Pechini Syntheses.

    Science.gov (United States)

    Chen, Wen-Fan; Mofarah, Sajjad S; Hanaor, Dorian Amir Henry; Koshy, Pramod; Chen, Hsin-Kai; Jiang, Yue; Sorrell, Charles Christopher

    2018-06-18

    Ce/Cr codoped TiO 2 nanoparticles were synthesized using sol-gel and Pechini methods with heat treatment at 400 °C for 4 h. A conventional sol-gel process produced well-crystallized anatase, while Pechini synthesis yielded less-ordered mixed-phase anatase + rutile; this suggests that the latter method enhances Ce solubility and increases chemical homogeneity but destabilizes the TiO 2 lattice. Greater structural disruption from the decomposition of the Pechini precursor formed more open agglomerated morphologies, while the lower levels of structural disruption from pyrolysis of the dried sol-gel precursor resulted in denser agglomerates of lower surface areas. Codoping and associated destabilization of the lattice reduced the binding energies in both powders. Cr 4+ formation in sol-gel powders and Cr 6+ formation in Pechini powders suggest that these valence changes derive from synergistic electron exchange from intervalence and/or multivalence charge transfer. Since Ce is too large to allow either substitutional or interstitial solid solubility, the concept of integrated solubility is introduced, in which the Ti site and an adjacent interstice are occupied by the large Ce ion. The photocatalytic performance data show that codoping was detrimental owing to the effects of reduced crystallinity from lattice destabilization and surface area. Two regimes of mechanistic behavior are seen, which are attributed to the unsaturated solid solutions at lower codopant levels and supersaturated solid solutions at higher levels. The present work demonstrates that the Pechini method offers a processing technique that is superior to sol-gel because the former facilitates solid solubility and consequent chemical homogeneity.

  5. Amoeba-like self-oscillating polymeric fluids with autonomous sol-gel transition.

    Science.gov (United States)

    Onoda, Michika; Ueki, Takeshi; Tamate, Ryota; Shibayama, Mitsuhiro; Yoshida, Ryo

    2017-07-13

    In the field of polymer science, many kinds of polymeric material systems that show a sol-gel transition have been created. However, most systems are unidirectional stimuli-responsive systems that require physical signals such as a change in temperature. Here, we report on the design of a block copolymer solution that undergoes autonomous and periodic sol-gel transition under constant conditions without any on-off switching through external stimuli. The amplitude of this self-oscillation of the viscosity is about 2,000 mPa s. We also demonstrate an intermittent forward motion of a droplet of the polymer solution synchronized with the autonomous sol-gel transition. This polymer solution bears the potential to become the base for a type of slime-like soft robot that can transform its shape kaleidoscopically and move autonomously, which is associated with the living amoeba that moves forward by a repeated sol-gel transition.

  6. Sol-gel processing of bioactive glass nanoparticles: A review.

    Science.gov (United States)

    Zheng, Kai; Boccaccini, Aldo R

    2017-11-01

    Silicate-based bioactive glass nanoparticles (BGN) are gaining increasing attention in various biomedical applications due to their unique properties. Controlled synthesis of BGN is critical to their effective use in biomedical applications since BGN characteristics, such as morphology and composition, determining the properties of BGN, are highly related to the synthesis process. In the last decade, numerous investigations focusing on BGN synthesis have been reported. BGN can mainly be produced through the conventional melt-quench approach or by sol-gel methods. The latter approaches are drawing widespread attention, considering the convenience and versatility they offer to tune the properties of BGN. In this paper, we review the strategies of sol-gel processing of BGN, including those adopting different catalysts for initiating the hydrolysis and condensation of silicate precursors as well as those combining sol-gel chemistry with other techniques. The processes and mechanism of different synthesis approaches are introduced and discussed in detail. Considering the importance of the BGN morphology and composition to their biomedical applications, strategies put forward to control the size, shape, pore structure and composition of BGN are discussed. BGN are particularly interesting biomaterials for bone-related applications, however, they also have potential for other biomedical applications, e.g. in soft tissue regeneration/repair. Therefore, in the last part of this review, recently reported applications of BGN in soft tissue repair and wound healing are presented. Copyright © 2017 Elsevier B.V. All rights reserved.

  7. Sol-gel process for preparing YBa2Cu4O8 precursors from Y, Ba, and Cu acidic acetates/ammonia/ascorbic acid systems

    International Nuclear Information System (INIS)

    Deptula, A.; Lada, W.; Olczak, T.; Goretta, K.C.

    1995-08-01

    Sols were prepared by addition of ammonia to acidic acetate solutions of Y 3+ , Ba 2+ , and Cu 2+ . Ascorbic acid was added to a part of the sol. The resultant sols were gelled to a shard, a film, or microspheres by evaporation at 60 C or by extraction of water from drops of emulsion suspended in 2-ethylhexanol-1. Addition of ethanol to the sols facilitated the formation of gel films, fabricated by a dipping technique, on glass or silver substrates. At 100 C, gels that were formed in the presence of ascorbic acid were perfectly amorphous, in contrast to the crystalline acetate gels. Conversion of the amorphous ascorbate gels to final products was easier than for the acetate gels. The quality of coatings prepared from ascorbate gels was superior to that of acetate gel coatings

  8. Nanostructured sol-gel coatings doped with cerium nitrate as pre-treatments for AA2024-T3

    International Nuclear Information System (INIS)

    Zheludkevich, M.L.; Serra, R.; Montemor, M.F.; Yasakau, K.A.; Salvado, I.M. Miranda; Ferreira, M.G.S.

    2005-01-01

    Nanostructured hybrid sol-gel coatings doped with cerium ions were investigated in the present work as pre-treatments for the AA2024-T3 alloy. The sol-gel films have been synthesized from tetraethylorthosilicate (TEOS) and 3-glycidoxypropyltrimethoxysilane (GPTMS) precursors. Additionally the hybrid sol was doped with zirconia nanoparticles prepared from hydrolyzed tetra-n-propoxyzirconium (TPOZ). Cerium nitrate, as corrosion inhibitor, was added into the hybrid matrix or into the oxide nanoparticles. The chemical composition and the structure of the hybrid sol-gel films were studied by XPS (X-ray photoelectron spectroscopy) and AFM (atomic force microscopy), respectively. The evolution of the corrosion protection properties of the sol-gel films was studied by EIS (electrochemical impedance spectroscopy), which can provide quantitative information on the role of the different pre-treatments. Different equivalent circuits, for different stages of the corrosion processes, were used in order to model the coating degradation. The models were supported by SEM (scanning electron microscopy) measurements. The results show that the sol-gel films containing zirconia nanoparticles present improved barrier properties. Doping the hybrid nanostructured sol-gel coatings with cerium nitrate leads to additional improvement of the corrosion protection. The zirconia particles present in the sol-gel matrix seem to act as nanoreservoirs providing a prolonged release of cerium ions. The nanostructured sol-gel films doped with cerium nitrate can be proposed as a potential candidate for substitution of the chromate pre-treatments for AA2024-T3

  9. Electrophoretically active sol-gel processes to backfill, seal, and/or densify porous, flawed, and/or cracked coatings on electrically conductive material

    Science.gov (United States)

    Panitz, Janda K.; Reed, Scott T.; Ashley, Carol S.; Neiser, Richard A.; Moffatt, William C.

    1999-01-01

    Electrophoretically active sol-gel processes to fill, seal, and/or density porous, flawed, and/or cracked coatings on electrically conductive substrates. Such coatings may be dielectrics, ceramics, or semiconductors and, by the present invention, may have deposited onto and into them sol-gel ceramic precursor compounds which are subsequently converted to sol-gel ceramics to yield composite materials with various tailored properties.

  10. Optical and electrochromic properties of sol-gel deposited Ti- doped vanadium oxide films

    International Nuclear Information System (INIS)

    Oezer, N.; Sabuncu, S.

    1997-01-01

    Because of the yellowish color, vanadium oxide films in the as deposited state is not as favorable as transparent coatings for most elector chromic devices. an interesting possibility to alter the yellowish colours is the doping with other non-absorbing metal oxides. Ti doped vanadium oxide films with various amounts of titanium were synthesized and investigated as transparent counter electrodes for electrochromic transmissive device application. Electrochromic titanium doped vanadium pentoxide (V sub 2 O 5) coatings were prepared by the sol-gel dip coating technique. The coating solutions were synthesized from vanadium tri(isopropoxide) precursors. X-ray diffraction (XRD) studies showed that the sol-gel deposited doped films heat treated at temperatures below 350 degree centigrade, were amorphous, whereas hose heat treated at higher temperatures were slight y crystalline. The optical and electrochemical properties of the Ti doped vanadium oxide films has been investigated in 0.1 m LiClO sub 4 propylene carbonate solution color changes by dropping were noted for all investigated films exhibits good electrochemical cycling (CV) measurements also showed that Ti doped V sub 2 O sub 5 films exhibits good electrochemical cycling reversibility, 'in situ' optical measurement revealed that those films exhibits good electrochemical cycling the spectra range 300 < lambda < 800 nm and change color between yellow and light green. The change in visible transmittance was 25 % for 5% Ti doped film. (author)

  11. Encapsulation of Polymer Colloids in a Sol-Gel Matrix. Direct-Writing of Coassembling Organic-Inorganic Hybrid Photonic Crystals.

    Science.gov (United States)

    Mikosch, Annabel; Kuehne, Alexander J C

    2016-03-22

    The spontaneous self-assembly of polymer colloids into ordered arrangements provides a facile strategy for the creation of photonic crystals. However, these structures often suffer from defects and insufficient cohesion, which result in flaking and delamination from the substrate. A coassembly process has been developed for convective assembly, resulting in large-area encapsulated colloidal crystals. However, to generate patterns or discrete deposits in designated places, convective assembly is not suitable. Here we experimentally develop conditions for direct-writing of coassembling monodisperse dye-doped polystyrene particles with a sol-gel precursor to form solid encapsulated photonic crystals. In a simple procedure the colloids are formulated in a sol-gel precursor solution, drop-cast on a flat substrate, and dried. We here establish the optimal parameters to form reproducible highly ordered photonic crystals with good optical performance. The obtained photonic crystals interact with light in the visible spectrum with a narrow optical stop-gap.

  12. Effect of vanadium on the obtaining of the titanium dioxide by Sol-Gel Method

    International Nuclear Information System (INIS)

    Granado, S.R.; Silva, D.W.; Lopes, S.A.; Cavalheiro, A.A.

    2011-01-01

    The obtaining of transition metal modified titanium dioxide (TiO 2 ) can be a promising path to promote changes in crystal structure of anatase phase in order to displace the band gap toward frequencies near to visible region. The insertion of the heterovalent ions such as vanadium can be shift the titanium coordination number in the anatase matrix, leading to important changes in the photonic characteristics of the material. In Sol-Gel method, the presence of the non alkoxide precursors can affects the stability of the solution and the gelifying process, with consequences on the characteristics of the material. In this work, it was investigated the effect of 5mol% of vanadium by thermal analysis of the dried gel and XRD and adsorption isotherm in the samples obtained at different temperatures. The decomposition steps of the precursor were associated to phase formation in the material, leading to conclusion that the presence of vanadium affects the stability of anatase phase. (author)

  13. An efficient adsorption of indigo carmine dye from aqueous solution on mesoporous Mg/Fe layered double hydroxide nanoparticles prepared by controlled sol-gel route.

    Science.gov (United States)

    Ahmed, M A; Brick, A A; Mohamed, A A

    2017-05-01

    A new approach for removal of indigo carmine blue (IC) dye which is extensively used in jeans manufacture was successfully performed on novel mesoporous [LDH] nanoparticles prepared by sol-gel route using CTAB as shape and pore directing agent. The physicochemical features were monitored by X-ray diffraction (XRD), Fourier transformer infra-red (FTIR), N 2 adsorption-desorption isotherm, Field emission electron microscope (FESEM) and high resolution transmission electron microscope (HRTEM). The influence of reaction parameters affecting dye adsorption including contact time, initial dye concentration, pH and temperature were investigated. Textural analysis and HRTEM images indicate the existence of mesoporous spherical nanoparticles of size = 26 nm connected to each other's and embedded large numbers of mesopores of average pore radius = 43.5 Å. A successful adsorption of IC on LDH nanoparticles of surface area = 85.6 m 2 /g at various pH with maximum adsorption capacity = 62.8 mg/g at pH = 9.5. Langmuir model is more favorable to describe the adsorption of IC rather than Freundlich model which reflecting the preferential formation of monolayer on the surface of LDH. Both film diffusion and the intraparticle diffusion affect the dye adsorption. The values of enthalpy change (ΔH) for and (ΔS) are + 28.18 and + 0.118 kJ/mol, respectively indicating that the removal process is endothermic. The results indicated that LDH nanoparticles conserved a good activity even after five consecutive cycles of reuse. Our results suggest that mesoporous LDH nanoparticles are considered a potential novel adsorbent for remediation of wastewater containing IC. Copyright © 2017 Elsevier Ltd. All rights reserved.

  14. Preparation and characterization of conductive and transparent ruthenium dioxide sol-gel films.

    Science.gov (United States)

    Allhusen, John S; Conboy, John C

    2013-11-27

    RuO2 conductive thin films were synthesized using the sol-gel method and deposited onto transparent insulating substrates. The optical transmission, film thickness, surface morphology and composition, resistivity, and spectroelectrochemical performance have been characterized. The optical transmission values of these films ranged from 70 to 89% in the visible region and from 56 to 88% in the infrared region. Resistivity values of the RuO2 sol-gel films varied from 1.02 × 10(-3) to 1.13 Ω cm and are highly dependent on the initial solution concentration of RuO2 in the sol-gel. The RuO2 sol-gel films were used as electrodes for the electrochemical oxidation and reduction of ferrocenemethanol. The electrochemical behavior of our novel RuO2 sol-gel films was compared to that of a standard platinum disk electrode and showed no appreciable differences in the half-wave potential (E1/2). The mechanical and chemical stability of the coatings was tested by physical abrasion and exposure to highly acidic, oxidizing Piranha solution. Repeated exposure to these extreme conditions did not result in any appreciable decline in electrochemical performance. Finally, the use of the novel RuO2 sol-gel conductive and transparent films was demonstrated in a spectroelectrochemistry experiment in which the oxidation and reduction of ferrocenemethanol was monitored via UV-vis spectroscopy as the applied potential was cycled.

  15. Functionalizable Sol-Gel Silica Coatings for Corrosion Mitigation

    Science.gov (United States)

    Gąsiorek, Jolanta; Babiarczuk, Bartosz; Kaleta, Jerzy; Jones, Walis; Krzak, Justyna

    2018-01-01

    Corrosion is constantly a major problem of the world economy in the field of metal products, metal processing and other areas that utilise metals. Previously used compounds utilizing hexavalent chromium were amongst the most effective materials for corrosion protection but regulations have been recently introduced that forbid their use. Consequently, there is a huge drive by engineers, technologists and scientists from different disciplines focused on searching a new, more effective and environmentally-friendly means of corrosion protection. One novel group of materials with the potential to solve metal protection problems are sol-gel thin films, which are increasingly interesting as mitigation corrosion barriers. These environmentally-friendly and easy-to-obtain coatings have the promise to be an effective alternative to hexavalent chromium compounds using for anti-corrosion industrial coatings. In this review the authors present a range of different solutions for slow down the corrosion processes of metallic substrates by using the oxides and doped oxides obtained by the sol-gel method. Examples of techniques used to the sol-gel coating examinations, in terms of anti-corrosion protection, are also presented. PMID:29373540

  16. Functionalizable Sol-Gel Silica Coatings for Corrosion Mitigation

    Directory of Open Access Journals (Sweden)

    Jolanta Gąsiorek

    2018-01-01

    Full Text Available Corrosion is constantly a major problem of the world economy in the field of metal products, metal processing and other areas that utilise metals. Previously used compounds utilizing hexavalent chromium were amongst the most effective materials for corrosion protection but regulations have been recently introduced that forbid their use. Consequently, there is a huge drive by engineers, technologists and scientists from different disciplines focused on searching a new, more effective and environmentally-friendly means of corrosion protection. One novel group of materials with the potential to solve metal protection problems are sol-gel thin films, which are increasingly interesting as mitigation corrosion barriers. These environmentally-friendly and easy-to-obtain coatings have the promise to be an effective alternative to hexavalent chromium compounds using for anti-corrosion industrial coatings. In this review the authors present a range of different solutions for slow down the corrosion processes of metallic substrates by using the oxides and doped oxides obtained by the sol-gel method. Examples of techniques used to the sol-gel coating examinations, in terms of anti-corrosion protection, are also presented.

  17. Functionalizable Sol-Gel Silica Coatings for Corrosion Mitigation.

    Science.gov (United States)

    Gąsiorek, Jolanta; Szczurek, Anna; Babiarczuk, Bartosz; Kaleta, Jerzy; Jones, Walis; Krzak, Justyna

    2018-01-26

    Corrosion is constantly a major problem of the world economy in the field of metal products, metal processing and other areas that utilise metals. Previously used compounds utilizing hexavalent chromium were amongst the most effective materials for corrosion protection but regulations have been recently introduced that forbid their use. Consequently, there is a huge drive by engineers, technologists and scientists from different disciplines focused on searching a new, more effective and environmentally-friendly means of corrosion protection. One novel group of materials with the potential to solve metal protection problems are sol-gel thin films, which are increasingly interesting as mitigation corrosion barriers. These environmentally-friendly and easy-to-obtain coatings have the promise to be an effective alternative to hexavalent chromium compounds using for anti-corrosion industrial coatings. In this review the authors present a range of different solutions for slow down the corrosion processes of metallic substrates by using the oxides and doped oxides obtained by the sol-gel method. Examples of techniques used to the sol-gel coating examinations, in terms of anti-corrosion protection, are also presented.

  18. Sol-gel Technology and Advanced Electrochemical Energy Storage Materials

    Science.gov (United States)

    Chu, Chung-tse; Zheng, Haixing

    1996-01-01

    Advanced materials play an important role in the development of electrochemical energy devices such as batteries, fuel cells, and electrochemical capacitors. The sol-gel process is a versatile solution for use in the fabrication of ceramic materials with tailored stoichiometry, microstructure, and properties. This processing technique is particularly useful in producing porous materials with high surface area and low density, two of the most desirable characteristics for electrode materials. In addition,the porous surface of gels can be modified chemically to create tailored surface properties, and inorganic/organic micro-composites can be prepared for improved material performance device fabrication. Applications of several sol-gel derived electrode materials in different energy storage devices are illustrated in this paper. V2O5 gels are shown to be a promising cathode material for solid state lithium batteries. Carbon aerogels, amorphous RuO2 gels and sol-gel derived hafnium compounds have been studied as electrode materials for high energy density and high power density electrochemical capacitors.

  19. Sol-gel auto-combustion synthesis of hydroxyapatite nanotubes array in porous alumina template

    International Nuclear Information System (INIS)

    Yuan Yuan; Liu Changsheng; Zhang Yuan; Shan Xiaoqian

    2008-01-01

    In this paper, an array of highly ordered hydroxyapatite (HAP) nanotubes was synthesized by sol-gel auto-combustion method with porous anodic aluminum oxide (AAO) template for the first time. Based on thermogravimetry (DTA/TG), Fourier transform infrared (FTIR) and X-ray diffraction (XRD), the dried gel, derived from the sol solution with Ca(NO 3 ) 2 .4H 2 O and PO(CH 3 O) 3 as precursors and ethylene glycol as the polymeric matrix, exhibited a typical self-propagating combustion behavior at low temperature, directly resulting in hexagonal crystalline HAP materials. The resultant HAP arrays fabricated from the above sol-gel in the AAO template were uniformly distributed, highly ordered nanotubes with uniform length and diameter according to the observations of scanning electron microscopy (SEM) and transmission electron microscope (TEM). The electron diffraction (ED), XRD and X-ray photoelectron spectroscopy (XPS) survey proved the formation of HAP phase with polycrystalline structure in the AAO template. Based on these results, a potential mechanism of 'an auto-combustion from dried gel to nanoparticles and a subsequent in situ reaction from nanoparticles to nanotubes' was proposed

  20. Neutron detector using sol-gel absorber

    Science.gov (United States)

    Hiller, John M.; Wallace, Steven A.; Dai, Sheng

    1999-01-01

    An neutron detector composed of fissionable material having ions of lithium, uranium, thorium, plutonium, or neptunium, contained within a glass film fabricated using a sol-gel method combined with a particle detector is disclosed. When the glass film is bombarded with neutrons, the fissionable material emits fission particles and electrons. Prompt emitting activated elements yielding a high energy electron contained within a sol-gel glass film in combination with a particle detector is also disclosed. The emissions resulting from neutron bombardment can then be detected using standard UV and particle detection methods well known in the art, such as microchannel plates, channeltrons, and silicon avalanche photodiodes.

  1. Hybrid sol-gel optical materials

    Science.gov (United States)

    Zeigler, John M.

    1992-01-01

    Hybrid sol-gel materials comprise silicate sols cross-linked with linear polysilane, polygermane, or poly(silane-germane). The sol-gel materials are useful as optical identifiers in tagging and verification applications and, in a different aspect, as stable, visible light transparent non-linear optical materials. Methyl or phenyl silicones, polyaryl sulfides, polyaryl ethers, and rubbery polysilanes may be used in addition to the linear polysilane. The linear polymers cross-link with the sol to form a matrix having high optical transparency, resistance to thermooxidative aging, adherence to a variety of substrates, brittleness, and a resistance to cracking during thermal cycling.

  2. Recubrimientos de hidroxiapatita preparados mediante un proceso sol-gel

    Directory of Open Access Journals (Sweden)

    Peón, E.

    2005-12-01

    Full Text Available Hydroxyapatite coatings (HAp have been obtained starting from precursors of sol-gel type. The coatings previously oxidized were deposited on metal surfaces of a based on iron alloy so-called MA956. The alloys were at high temperatures, in order to improve the adhesion with the hydroxyapatite coatings. The sol-gel coating was obtained applying an aqueous route, using triethyl phosphite and aqueous calcium nitrate, as precursors of phosphorous and calcium, respectively. Different sintering thermal treatments were applied on the resulting gels in order to obtain a homogeneous, adherent and crystalline hydroxyapatite coating. The characterization techniques used for this study were optical microscopy, SEM/EDX, XDR and FTIR. Moreover, the adhesion between the hydroxylapatite coating and the substrate was assessed according to the ASTM D 3359-02 standard test method. The results of this study showed that the best thermal treatment is obtained for a sintering temperature of 550 °C during a time of 72 h.

    Se han preparado nuevos recubrimientos de hidroxiapatita (HAp obtenidos a partir de precursores de tipo sol-gel, depositados sobre sustratos metálicos de una aleación de base hierro denominada MA956, previamente oxidados a elevadas temperaturas, para mejorar la adherencia con los recubrimientos de hidroxiapatita. El recubrimiento sol-gel se obtuvo aplicando una ruta acuosa, utilizando como precursores del fósforo y del calcio trietilfosfito y nitrato cálcico tetrahidratado, respectivamente. Sobre los geles resultantes se aplicaron distintos tratamientos térmicos de sinterización, hasta la obtención de recubrimientos de hidroxiapatita homogéneos, adherentes y cristalinos. Las técnicas de caracterización utilizadas para realizar este estudio han sido microscopía óptica, MBE/EDX, DRX y FTIR. Así mismo, se ha determinado la adherencia entre el substrato y el recubrimiento de hidroxiapatita según la norma ASTM D 3359-02. Los resultados

  3. Novel hybrid sol-gel coatings for corrosion protection of AZ31B magnesium alloy

    International Nuclear Information System (INIS)

    Lamaka, S.V.; Montemor, M.F.; Galio, A.F.; Zheludkevich, M.L.; Trindade, C.; Dick, L.F.; Ferreira, M.G.S.

    2008-01-01

    This work aims to develop and study new anticorrosion films for AZ31B magnesium alloy based on the sol-gel coating approach. Hybrid organic-inorganic sols were synthesized by copolymerization of epoxy-siloxane and titanium or zirconium alkoxides. Tris(trimethylsilyl) phosphate was also used as additive to confer additional corrosion protection to magnesium-based alloy. A sol-gel coating, about 5-μm thick, shows good adhesion to the metal substrate and prevents corrosion attack in 0.005 M NaCl solution for 2 weeks. The sol-gel coating system doped with tris(trimethylsilyl)-phosphate revealed improved corrosion protection of the magnesium alloy due to formation of hydrolytically stable Mg-O-P chemical bonds. The structure and the thickness of the sol-gel film were characterized by transmission electron microscopy (TEM) and scanning electron microscopy (SEM). The corrosion behaviour of AZ31B substrates pre-treated with the sol-gel derived hybrid coatings was tested by electrochemical impedance spectroscopy (EIS). The chemical composition of the silylphosphate-containing sol-gel film at different depths was investigated by X-ray photoelectron spectroscopy (XPS) with depth profiling

  4. Fabrication of targets for transmutation of americium : synthesis of inertial matrix by sol-gel method. Procedure study on the infiltration of a radioactive solutions; Fabricacion de blancos para la transmutacion de americio: sintesis de matrices inertes por el metodo sol-gel. Estudio del procedimiento de infiltracion de disoluciones radiactivas

    Energy Technology Data Exchange (ETDEWEB)

    Fernandez Carretero, A [Universidad Complutense de Madrid (Spain)

    2002-07-01

    Transmutation and incineration are innovative options in the management and disposal of fission products and actinides. nevertheless, the fabrication of targets for transmutation and incineration of actinides and fission products require a reconsideration of conventional processes (mechanical blending) and the development of new procedures compatible with the high activity of these materials. This work presents th R and D of a new fabrication method called INRAM (Infiltration of Radioactive Materials) based on the infiltration of an actinide solution in a porous non radiotoxic material in the form of a pellet (up to 12% An), or beads (up to 40% An) produced by sol-gel. The first method have been used for the fabrication of spinel (MgAl{sub 2}O{sub 4}) targets containing 11% Am, which have been irradiated in HFR-Petten (358.4 full power days). Post-test burn-up calculations showed that at the end of the irradiation the initial Am-241 concentration was reduced to 4%. The fraction of the initial americum atoms that have been fissioned is 28%. The main advantage of the INRAM method is that matrices with low or zero activity can be fabricated and formed into the required shape in an unshielded facility. This method offers other advantages over conventional ones, such as the active wastes are reduced, is easy to automate, adoptable to telemanipulation and dust free, which facilitate operator intervention and minimise radiation exposure to the personal. In addition, the infiltrant needs only be present in liquid form, i. e. it could be transferred directly from the reprocessing plant for fabrication into targets without conversion into-solid form. In order to optimise the infiltration process in depth investigations of all important process parameters, e. g. infiltration kinetics and metal (pu, Am) concentration in the feed solution, and also on extensive study or powder metallurgy parameters for the preparation of high quality fuel pellets with a high density, have been

  5. Synthesis of phthalocyanine doped sol-gel materials

    Science.gov (United States)

    Dunn, Bruce

    1993-01-01

    The synthesis of sol-gel silica materials doped with three different types of metallophthalocyanines has been studied. Homogeneous materials of good optical quality were prepared and the first optical limiting measurements of dyes in sol-gel hosts were carried out. The properties of these solid state limiters are similar to limiters based on phthalocyanine (Pc) in solution. Sol-gel silica materials containing copper, tin and germanium phthalocyanines were investigated. The initial step in all cases was to prepare silica sols by the sonogel method using tetramethoxy silane (TMOS), HCl and distilled water. Thereafter, the synthesis depended upon the specific Pc and its solubility characteristics. Copper phthalocyanine tetrasulfonic acid tetra sodium salt (CuPc4S) is soluble in water and various doping levels (1 x 10 (exp -4) M to 1 x 10 (exp -5) M) were added to the sol. The group IV Pc's, SnPc(OSi(n-hexyl)3)2 and GePc(OSi(n-hexyl)3)2, are insoluble in water and the process was changed accordingly. In these cases, the compounds were dissolved in THF and then added to the sol. The Pc concentration in the sol was 2 x 10(exp -5)M. The samples were then aged and dried in the standard method of making xerogel monoliths. Comparative nanosecond optical limiting experiments were performed on silica xerogels that were doped with the different metallophthalocyanines. The ratio of the net excited state absorption cross section (sigma(sub e)) to the ground state cross section (sigma(sub g)) is an important figure of merit that is used to characterize these materials. By this standard the SnPc sample exhibits the best limiting for the Pc doped sol-gel materials. Its cross section ratio of 19 compares favorably with the value of 22 that was measured in toluene. The GePc materials appear to not be as useful as those containing SnPc. The GePc doped solids exhibit a higher onset energy (2.5 mj and lower cross section ratio, 7. The CuPc4S sol-gel material has a still lower cross

  6. Encapsulation of nanoclusters in dried gel materials via an inverse micelle/sol gel synthesis

    Science.gov (United States)

    Martino, Anthony; Yamanaka, Stacey A.; Kawola, Jeffrey S.; Showalter, Steven K.; Loy, Douglas A.

    1998-01-01

    A dried gel material sterically entrapping nanoclusters of a catalytically active material and a process to make the material via an inverse micelle/sol-gel synthesis. A surfactant is mixed with an apolar solvent to form an inverse micelle solution. A salt of a catalytically active material, such as gold chloride, is added along with a silica gel precursor to the solution to form a mixture. To the mixture are then added a reducing agent for the purpose of reducing the gold in the gold chloride to atomic gold to form the nanoclusters and a condensing agent to form the gel which sterically entraps the nanoclusters. The nanoclusters are normally in the average size range of from 5-10 nm in diameter with a monodisperse size distribution.

  7. Sol-Gel Synthesis Of Aluminoborosilicate Powders

    Science.gov (United States)

    Bull, Jeffrey; Leiser, Daniel; Selvaduray, Guna

    1992-01-01

    Application of sol-gel process to synthesis of aluminoborosilicate powders shows potential for control of microstructures of materials. Development of materials having enhanced processing characteristics prove advantageous in extending high-temperature endurance of fibrous refractory composite insulation made from ceramic fibers.

  8. Sol-Gel Derived Hafnia Coatings

    Science.gov (United States)

    Feldman, Jay D.; Stackpoole, Mairead; Blum, Yigal; Sacks, Michael; Ellerby, Don; Johnson, Sylvia M.; Venkatapathy, Ethiras (Technical Monitor)

    2002-01-01

    Sol-gel derived hafnia coatings are being developed to provide an oxidation protection layer on ultra-high temperature ceramics for potential use in turbine engines (ultra-efficient engine technology being developed by NASA). Coatings using hafnia sol hafnia filler particles will be discussed along with sol synthesis and characterization.

  9. Fluorescence metrology of silica sol-gels

    Indian Academy of Sciences (India)

    We have developed a new method for measuring in-situ the growth of the nanometre-size silica particles which lead to the formation of sol-gel glasses. This technique is based on the decay of fluorescence polarisation anisotropy due to Brownian rotation of dye molecules bound to the particles. Results to date give near ...

  10. Electrochemical corrosion behavior of composite MAO/sol-gel coatings on magnesium alloy AZ91D using combined micro-arc oxidation and sol-gel technique

    International Nuclear Information System (INIS)

    Shang Wei; Chen Baizhen; Shi Xichang; Chen Ya; Xiao Xiang

    2009-01-01

    Protective composite coatings were obtained on a magnesium alloy by micro-arc oxidation (MAO) and sol-gel technique. The coatings consisted of a MAO layer and a sol-gel layer. The microstructure and composition of the MAO coating and the composite coatings were analyzed by scanning electron microscopy (SEM) and energy dispersive X-rays (EDX). Potentiodynamic polarization, electrochemical impedance spectroscopy (EIS) and total immersion tests were used to evaluate the corrosion behavior of these coatings in a 3.5 wt.% NaCl solution. The results show that the sol-gel layer provides corrosion protection by physically sealing the pores in the MAO coating and acting as a barrier. The composite coatings can suppress the corrosion process by preventing the corrosive ions from transferring or diffusing to the magnesium alloy substrate. This enhances the corrosion resistance of the magnesium alloy AZ91D significantly

  11. Sol-gel applications for ceramic membrane preparation

    Science.gov (United States)

    Erdem, I.

    2017-02-01

    Ceramic membranes possessing superior properties compared to polymeric membranes are more durable under severe working conditions and therefore their service life is longer. The ceramic membranes are composed of some layers. The support is the layer composed of coarser ceramic structure and responsible for mechanical durability under filtration pressure and it is prepared by consolidation of ceramic powders. The top layer is composed of a finer ceramic micro-structure mainly responsible for the separation of components present in the fluid to be filtered and sol-gel method is a versatile tool to prepare such a tailor-made ceramic filtration structure with finer pores. Depending on the type of filtration (e.g. micro-filtration, ultra-filtration, nano-filtration) aiming separation of components with different sizes, sols with different particulate sizes should be prepared and consolidated with varying precursors and preparation conditions. The coating of sol on the support layer and heat treatment application to have a stable ceramic micro-structure are also important steps determining the final properties of the top layer. Sol-gel method with various controllable parameters (e.g. precursor type, sol formation kinetics, heat treatment conditions) is a practical tool for the preparation of top layers of ceramic composite membranes with desired physicochemical properties.

  12. Effect of calcium source on structure and properties of sol-gel derived bioactive glasses.

    Science.gov (United States)

    Yu, Bobo; Turdean-Ionescu, Claudia A; Martin, Richard A; Newport, Robert J; Hanna, John V; Smith, Mark E; Jones, Julian R

    2012-12-18

    The aim was to determine the most effective calcium precursor for synthesis of sol-gel hybrids and for improving homogeneity of sol-gel bioactive glasses. Sol-gel derived bioactive calcium silicate glasses are one of the most promising materials for bone regeneration. Inorganic/organic hybrid materials, which are synthesized by incorporating a polymer into the sol-gel process, have also recently been produced to improve toughness. Calcium nitrate is conventionally used as the calcium source, but it has several disadvantages. Calcium nitrate causes inhomogeneity by forming calcium-rich regions, and it requires high temperature treatment (>400 °C) for calcium to be incorporated into the silicate network. Nitrates are also toxic and need to be burnt off. Calcium nitrate therefore cannot be used in the synthesis of hybrids as the highest temperature used in the process is typically 40-60 °C. Therefore, a different precursor is needed that can incorporate calcium into the silica network and enhance the homogeneity of the glasses at low (room) temperature. In this work, calcium methoxyethoxide (CME) was used to synthesize sol-gel bioactive glasses with a range of final processing temperatures from 60 to 800 °C. Comparison is made between the use of CME and calcium chloride and calcium nitrate. Using advanced probe techniques, the temperature at which Ca is incorporated into the network was identified for 70S30C (70 mol % SiO(2), 30 mol % CaO) for each of the calcium precursors. When CaCl(2) was used, the Ca did not seem to enter the network at any of the temperatures used. In contrast, Ca from CME entered the silica network at room temperature, as confirmed by X-ray diffraction, (29)Si magic angle spinning nuclear magnetic resonance spectroscopy, and dissolution studies. CME should be used in preference to calcium salts for hybrid synthesis and may improve homogeneity of sol-gel glasses.

  13. Efficacy of a new tan doped sol-gel sorbent for uptake of zinc

    International Nuclear Information System (INIS)

    Khan, A.; Ahmed, S.; Riaz, M.; Mahmood, F.; Younas Khokhar, M.

    2003-01-01

    A TAN (1-(2-Thiazolylazo)-2-naphthol) doped sol gel silica sorbent (reddish colour, porous, stable, hard, non-swelling) were prepared and investigated for the removal of Zn (II) from aqueous solutions. The kinetics, adsorption isotherm, equilibration time and pH effect on the removal were studied from non competitive aqueous solution to optimize the conditions to be utilized on a large scale. Fast equilibration was observed and adsorption equilibria were reached within 30 minutes. Adsorption of zinc ions on the blank (un-doped) sol gel was found negligible. The maximum adsorption of Zn (II) ions onto the TAN doped sol-gel from single solutions were 2.33 mg/g (0.035 mmol/g). TAN doped sol gel can be regenerated through washing with a solution of 0.1 M HCl solution. The maximum regeneration value was as high as 99.0%. The TAN-doped sol gel silica is suitable at least for four adsorption-desorption cycles without experiencing considerable loss of adsorption capacity. The uptake route and the nature of the Zn-TAN complex have been discussed. (orig.)

  14. Fluorescence yield in rare-earth-doped sol-gel silicate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Silversmith, A.J., E-mail: asilvers@hamilton.ed [Physics Department, Hamilton College, 198 College Hill Road, Clinton, NY 13323 (United States); Nguyen, Nguyen T.T.; Campbell, D.L. [Physics Department, Hamilton College, 198 College Hill Road, Clinton, NY 13323 (United States); Boye, D.M.; Ortiz, C.P. [Davidson College, Davidson, NC 28035 (United States); Hoffman, K.R. [Whitman College, Walla Walla, WA 99362 (United States)

    2009-12-15

    We have used trivalent terbium to investigate the mechanism behind fluorescence enhancement by Al{sup 3+} co-doping. Our results indicate that rare-earth (RE) ions cluster together in aluminum-rich regions of the glass, and behave as if they were dispersed uniformly throughout these regions when the ratio of Al to RE is {approx}10 or greater. We also studied the effects of adding chemical drying agents to the precursor solution for the synthesis of sol-gel-derived silicate glasses. Such glasses can be treated at significantly higher annealing temperatures without degradation of optical quality, and have the density of melt glass. Fluorescence yield from doped RE ions improves markedly with the addition of the drying agents, and the denser glasses are not subject to rehydration.

  15. Preparation and characterization of ultra-thin sol-gel films

    International Nuclear Information System (INIS)

    Shapiro, Leora; Marx, Sharon; Mandler, Daniel

    2007-01-01

    The formation and characterization of nanometer thick sol-gel films are reported. The films were prepared by spin-coating of a diluted solution of a silane precursor on a number of different substrates. The effect of dilution, rotation speed and nature of substrate on the thickness and homogeneity of the films was examined. Characterization of the films was carried out by profilometry, reflectance spectroscopy, atomic force microscopy, adhesion test and electrochemistry. We find that the dilution factor has a pronounced effect on the film thickness. Moreover, the time of dilution, namely, whether dilution was carried out before or after a period of hydrolysis, has a noticeable effect on the thickness as well as on the permeability of embedded species

  16. Magnetic resonance as a structural probe of a uranium (VI) sol-gel process

    International Nuclear Information System (INIS)

    King, C.M.; Thompson, M.C.; Buchanan, B.R.; King, R.B.; Garber, A.R.

    1989-01-01

    NMR investigations on the ORNL process for sol-gel synthesis of microspherical nuclear fuel (UO 2 ), has been useful in sorting out the chemical mechanism in the sol-gel steps. 13 C, 15 N, and 1 H NMR studies on the HMTA gelation agent (Hexamethylene tetramine, C 6 H l2 N 4 ) has revealed near quantitative stability of this adamantane-like compound in the sol-Gel process, contrary to its historical role as an ammonia source for gelation from the worldwide technical literature. 17 0 NMR of uranyl (UO 2 ++ ) hydrolysis fragments produced in colloidal sols has revealed the selective formation of a uranyl trimer, [(UO 2 ) 3 (μ 3 -O)(μ 2 -OH) 3 ] + , induced by basic hydrolysis with the HMTA gelation agent. Spectroscopic results show that trimer condensation occurs during sol-gel processing leading to layered polyanionic hydrous uranium oxides in which HMTAH + is occluded as an ''intercalation'' cation. Subsequent sol-gel processing of microspheres by ammonia washing results in in-situ ion exchange and formation of a layered hydrous ammonium uranate with a proposed structural formula of (NH 4 ) 2 [(UO 2 ) 8 O 4 (OH) 10 ] · 8H 2 0. This compound is the precursor to sintered U0 2 ceramic fuel

  17. Screen-printable sol-gel enzyme-containing carbon inks.

    Science.gov (United States)

    Wang, J; Pamidi, P V; Park, D S

    1996-08-01

    Enzymes usually cannot withstand the high-temperature curing associated with the thick-film fabrication process and require a separate immobilization step in connection with the production of single-use biosensors. We report on the development of sol-gel-derived enzyme-containing carbon inks that display compatibility with the screen-printing process. Such coupling of sol-gel and thick-film technologies offers a one-step fabrication of disposable enzyme electrodes, as it obviates the need for thermal curing. The enzyme-containing sol-gel carbon ink, prepared by dispersing the biocatalyst, along with the graphite powder and a binder, within the sol-gel precursors, is cured very rapidly (10 min) at low temperature (4 °C). The influence of the ink preparation conditions is explored, and the sensor performance is evaluated in connection with the incorporation of glucose oxidase or horseradish peroxidase. The resulting strips are stable for at least 3 months. Such sol-gel-derived carbon inks should serve as hosts for other heat-sensitive biomaterials in connection with the microfabrication of various thick-film biosensors.

  18. SOL-Gel microspheres and nanospheres for controlled release applications

    International Nuclear Information System (INIS)

    Barbe, C.; Beyer, R.; Kong, L.; Blackford, M.; Trautman, R.; Bartlett, J.

    2002-01-01

    We present a novel approach to the synthesis of inorganic sol-gel microspheres for encapsulating organic and bioactive molecules, and controlling their subsequent release kinetics. The bioactive species are incorporated, at ambient temperature, into the inorganic particles using an emulsion gelation process. Independent control of the release rate (by adapting the nanostructure of the internal pore network to the physico-chemical properties of the bioactive molecules) and particle size (by tailoring the emulsion chemistry) is demonstrated. Sol-gel chemistry has been shown to be a flexible technique for producing inorganic silica matrices with tailored microstructures, which can be used for the encapsulation and controlled release of organic and bioactive molecules. The present paper extends this concept by combining sol-gel chemistry with an emulsion approach for producing inorganic particles with controlled dimensions, and demonstrates how the particle size and microstructure can be independently controlled. Sol-Gel Chemistry and Encapsulation of Model Compounds. A stock solution of 4-(2-hydroxy-l-naphthylazo) benzene sulfonic acid (Orange II) was produced by dissolving Orange II in water (0.1 wt%), and adjusting the pH to the required value. Sol-gel solutions were subsequently prepared by mixing the aqueous solution with tetramethylorthosilicate (TMOS) and methanol (MeOH), to achieve H 2 O:TMOS (W] and MeOH:TMOS mole ratios (D) of four. The resulting solution was stirred and left to age at ambient temperature for one day. A transparent emulsion was prepared by mixing selected surfactants and organic solvents. The surfactants used included sorbitan monooleate, sorbitan monolaurate and bis-2-ethylhexylsulfo-succinate (AOT), while the organic phase was typically chosen from the group consisting of kerosene, hexane, heptane, octane, decane, dodecane and cyclohexane. The sol-gel solution was added to the emulsion, and the resulting mixture was stirred at 500 rpm for

  19. Salt-assisted and salt-suppressed sol-gel transitions of methylcellulose in water.

    Science.gov (United States)

    Xu, Y; Wang, C; Tam, K C; Li, L

    2004-02-03

    The effects of various salts on the sol-gel transition of aqueous methylcellulose (MC) solutions have been studied systematically by means of a micro differential scanning calorimeter. It was found that the heating process was endothermic while the cooling process was exothermic for both MC solutions with and without salts. The addition of salts did not change the patterns of gelation and degelation of MC. However, the salts could shift the sol-gel transition and the gel-sol transition to lower or higher temperatures from a pure MC solution, depending on the salt type. These opposite effects were termed the salt-assisted and salt-suppressed sol-gel transitions. Either the salt-assisted transition or the salt-suppressed sol-gel transition was a function of salt concentration. In addition, each salt was found to have its own concentration limit for producing a stable aqueous solution of MC at a given concentration of MC, which was related to the anionic charge density of the salt. Cations were proved to have weaker effects than anions. The "salt-out strength", defined as the salt effect per mole of anion, was obtained for each anion studied. The thermodynamic mechanisms involved in the salt-assisted and salt-suppressed sol-gel transitions are discussed.

  20. Optical sensing of HCl with phenol red doped sol-gels

    International Nuclear Information System (INIS)

    Wang Enju; Chow, Kwok-Fan; Wang Wenqun; Wong, Crystal; Yee, Cynthia; Persad, Alvin; Mann, Jonathan; Bocarsly, Andrew

    2005-01-01

    A dye doped sol-gel for the sensing of hydrochloric acid in solution and/or gaseous phase is described. The sol-gel is obtained by acidic hydrolysis of tetraethoxysilane (TEOS) and phenyltriethoxysilane (Ph-TriEOS) in the presence of phenol red (PR) and further spin-coating onto glass slides. The sensitive response is based on an increase of the absorption band at 510 nm of phenol red entrapped in the sol-gel casting when exposed to HCl solution or gas, due to protonation of the dye. The detection limit of the sol-gel response to moisturized gaseous HCl is below 12 ppm, and its response to HCl in solution falls in the range of 0.01-6 M. The sol-gel coating has a response time of less than 40 s in steady-state, and life-time of more than a year. Weak acids such as acetic acid, benzoic acid, salicylate acid, citrate acid, and carbonic acid do not interfere the response. The responses in acid solutions are completely reversible. In the gaseous phase, response of HCl appears to be moisture sensitive

  1. Optical sensing of HCl with phenol red doped sol-gels

    Energy Technology Data Exchange (ETDEWEB)

    Wang Enju [Department of Chemistry, St. John' s University, 8000 Utopia Parkway, Jamaica, NY 11439 (United States)]. E-mail: wange@stjohns.edu; Chow, Kwok-Fan [Department of Chemistry, St. John' s University, 8000 Utopia Parkway, Jamaica, NY 11439 (United States); Wang Wenqun [Department of Chemistry, St. John' s University, 8000 Utopia Parkway, Jamaica, NY 11439 (United States); Wong, Crystal [Department of Chemistry, St. John' s University, 8000 Utopia Parkway, Jamaica, NY 11439 (United States); Yee, Cynthia [Department of Chemistry, St. John' s University, 8000 Utopia Parkway, Jamaica, NY 11439 (United States); Persad, Alvin [Department of Chemistry, St. John' s University, 8000 Utopia Parkway, Jamaica, NY 11439 (United States); Mann, Jonathan [Department of Chemistry, Princeton University, Princeton, NJ 08540 (United States); Bocarsly, Andrew [Department of Chemistry, Princeton University, Princeton, NJ 08540 (United States)

    2005-04-08

    A dye doped sol-gel for the sensing of hydrochloric acid in solution and/or gaseous phase is described. The sol-gel is obtained by acidic hydrolysis of tetraethoxysilane (TEOS) and phenyltriethoxysilane (Ph-TriEOS) in the presence of phenol red (PR) and further spin-coating onto glass slides. The sensitive response is based on an increase of the absorption band at 510 nm of phenol red entrapped in the sol-gel casting when exposed to HCl solution or gas, due to protonation of the dye. The detection limit of the sol-gel response to moisturized gaseous HCl is below 12 ppm, and its response to HCl in solution falls in the range of 0.01-6 M. The sol-gel coating has a response time of less than 40 s in steady-state, and life-time of more than a year. Weak acids such as acetic acid, benzoic acid, salicylate acid, citrate acid, and carbonic acid do not interfere the response. The responses in acid solutions are completely reversible. In the gaseous phase, response of HCl appears to be moisture sensitive.

  2. Sol-gel process for the manufacture of high power switches

    Science.gov (United States)

    Landingham, Richard L.; Satcher, Jr, Joe; Reibold, Robert

    2016-09-27

    According to one embodiment, a photoconductive semiconductor switch includes a structure of nanopowder of a high band gap material, where the nanopowder is optically transparent, and where the nanopowder has a physical characteristic of formation from a sol-gel process. According to another embodiment, a method includes mixing a sol-gel precursor compound, a hydroxy benzene and an aldehyde in a solvent thereby creating a mixture, causing the mixture to gel thereby forming a wet gel, drying the wet gel to form a nanopowder, and applying a thermal treatment to form a SiC nanopowder.

  3. Sol-gel additive for systems with inorganic binders

    International Nuclear Information System (INIS)

    Akstinat, M.; Antenen, D.; Suter, W.

    1996-01-01

    A sol-gel additive for inorganic binder systems and sol-gel process for producing air-placed concrete and mortar by using such sol-gel additives are disclosed. Sol-gel additives for gel-derived inorganic binder systems (for example plaster, cement, lime, special slags, etc.) marked improve the consistency of such binder systems during processing or allow their consistency to be regulated. In addition, these sol-gel additives regulate setting times and substantially improve durability (chemical resistance, reduced permeability) and the mechanical properties of the set binder system. (author)

  4. Synthesis and characterization of TiC nanopowders via sol-gel and subsequent carbothermal reduction process

    Science.gov (United States)

    Chen, Xu; Fan, Jinglian; Lu, Qiong

    2018-06-01

    TiC nanocrystalline powders were synthesized by in-situ carbothermic reduction of Ti-O-C precursor under vacuum atmosphere. And the Ti-O-C precursor was formed by sol-gel method from titanium butyrate (TBOT) and sucrose. To obtain stable sol, TBOT was directly added into mixed solution which contains water, sucrose, acetic acid (AcOH) and acetylacetone (ACAC). This procedure is more convenient and economical because it avoids the use of alcohol which is used as solvent in most reports of alkoxide hydrolysis sol-gel method. TG-DSC, XRD, FTIR and SEM/TEM were employed to analyze and characterize the product during the entire process. The phase composition and crystalline structure parameters of powders with different C/Ti molar ratio were investigated by Rietveld refinement method, and elemental quantitative analysis of the samples were performed. Furthermore, the optimal parameters of carbothermal reduction were obtained and the grain growth mechanism was demonstrated. The results show that TiC nanocrystalline powders (C/Ti molar ratio is 3.5 in the precursor) were synthesized at 1300 °C for 2 h, which have near standard lattice parameter, well crystallinity and fine average grain size ( 37.4 nm).

  5. Analysis of coupled mass transfer and sol-gel reaction in a two-phase system

    NARCIS (Netherlands)

    Castelijns, H.J.; Huinink, H.P.; Pel, L.; Zitha, P.L.J.

    2006-01-01

    The coupled mass transfer and chemical reactions of a gel-forming compound in a two-phase system were studied in detail. Tetra-methyl-ortho-silicate (TMOS) is often used as a precursor in sol-gel chemistry to produce silica gels in aqueous systems. TMOS can also be mixed with many hydrocarbons

  6. Entrapment of subtilisin in ceramic sol-gel coating for antifouling applications.

    Science.gov (United States)

    Regina, Viduthalai Rasheedkhan; Søhoel, Helmer; Lokanathan, Arcot Raghupathi; Bischoff, Claus; Kingshott, Peter; Revsbech, Niels Peter; Meyer, Rikke Louise

    2012-11-01

    Enzymes with antifouling properties are of great interest in developing nontoxic antifouling coatings. A bottleneck in developing enzyme-based antifouling coatings is to immobilize the enzyme in a suitable coating matrix without compromising its activity and stability. Entrapment of enzymes in ceramics using the sol-gel method is known to have several advantages over other immobilization methods. The sol-gel method can be used to make robust coatings, and the aim of this study was to explore if sol-gel technology can be used to develop robust coatings harboring active enzymes for antifouling applications. We successfully entrapped a protease, subtilisin (Savinase, Novozymes), in a ceramic coating using a sol-gel method. The sol-gel formulation, when coated on a stainless steel surface, adhered strongly and cured at room temperature in less than 8 h. The resultant coating was smoother and less hydrophobic than stainless steel. Changes in the coating's surface structure, thickness and chemistry indicate that the coating undergoes gradual erosion in aqueous medium, which results in release of subtilisin. Subtilisin activity in the coating increased initially, and then gradually decreased. After 9 months, 13% of the initial enzyme activity remained. Compared to stainless steel, the sol-gel-coated surfaces with active subtilisin were able to reduce bacterial attachment of both Gram positive and Gram negative bacteria by 2 orders of magnitude. Together, our results demonstrate that the sol-gel method is a promising coating technology for entrapping active enzymes, presenting an interesting avenue for enzyme-based antifouling solutions.

  7. Ring-Resonator/Sol-Gel Interferometric Immunosensor

    Science.gov (United States)

    Bearman, Gregory; Cohen, David

    2007-01-01

    A proposed biosensing system would be based on a combination of (1) a sensing volume containing antibodies immobilized in a sol-gel matrix and (2) an optical interferometer having a ring resonator configuration. The antibodies would be specific to an antigen species that one seeks to detect. In the ring resonator of the proposed system, light would make multiple passes through the sensing volume, affording greater interaction length and, hence, greater antibody- detection sensitivity.

  8. Transparent Hydrophobic Coating by Sol Gel Method

    International Nuclear Information System (INIS)

    Mohd Hamzah Harun; Nik Ghazali Nik Salleh; Mahathir Mohamed; Mohd Sofian Alias

    2016-01-01

    Transparent hydrophobic coating of inorganic based tetra orthosilicate (TEOS) was prepared by sol gel method by varying fluoroalkylsilane (FAS) content which works as hydrophobic agent. Surface contact angle, transmittance degree and surface morphology were characterized for each sample. All samples show good transparency which was confirmed by UV visible spectroscopy. The hydrophobicity obtained increases with FAS content indicates that FAS is best candidate to induce hydrophobicity for inorganic coating. (author)

  9. Synthesis of ZNO nanoparticles by Sol-Gel processing

    International Nuclear Information System (INIS)

    Savi, B.M.; Rodrigues, L.; Uggioni, E.; Bernardin, A.M.

    2011-01-01

    The aim of this study was to obtain and characterize ZnO nanoparticles by Sol-Gel technique. ZnCl 2 , Zn(NO 3 ) 2 , NaOH were used as precursors for the synthesis. NaOH was dissolved in distilled water at a concentration of 1.0 M with agitation to the desired reaction temperature (50°C and 90°C). 0.5 M ZnCl 2 and 0.5 M Zn(NO3)2 were added by dripping (60 and 30 min). The powder was characterized by XRD (Cu Kα), UV-Vis, and HR-TEM. Nano ZnO particles were obtained with crystallite size between 20 and 40 nm (HR-TEM and XRD). The results of UV-Vis spectrometry show that the band gap energy, given by the absorbance at 300 nm depends on the precursor used. (author)

  10. Brilliant molecular nanocrystals emerging from sol-gel thin films: towards a new generation of fluorescent biochips

    International Nuclear Information System (INIS)

    Dubuisson, E; Monnier, V; Sanz-Menez, N; Ibanez, A; Boury, B; Usson, Y; Pansu, R B

    2009-01-01

    To develop highly sensitive biosensors, we made directly available to biological aqueous solutions organic nanocrystals previously grown in the pores of sol-gel films. Through the controlled dissolution of the sol-gel surface, we obtained emerging nanocrystals that remained strongly anchored to the sol-gel coating for good mechanical stability of the final sensing device. We demonstrated that in the presence of a solution of DNA functionalized with a molecular probe, the nanocrystal fluorescence is strongly quenched by Foerster resonance energy transfer thus opening the way towards very sensitive fluorescent biosensors through biomolecules grafted onto fluorescent nanocrystals. Finally, this controlled dissolution, involving weak concentrated NaOH solution, is a generic process that can be used for the thinning of any kind of sol-gel layer.

  11. rhEGF-containing thermosensitive and mucoadhesive polymeric sol-gel for endoscopic treatment of gastric ulcer and bleeding.

    Science.gov (United States)

    Maeng, Jin Hee; So, Jung Won; Kim, Jungju; Kim, In Ae; Jung, Ji Hoon; Min, Kyunghyun; Lee, Don Haeng; Yang, Su-Geun

    2014-03-01

    Gastrointestinal endoscopy is a standard diagnostic tool for gastrointestinal ulcers and cancer. In this study, we have developed recombinant human epidermal growth factor-containing ulcer-coating polymeric sol-gel for endoscopic application. Chitosan and pluronic F127 were employed for their thermoresponsive and bioadhesive properties. At temperatures below 21, polymeric sol-gel remains liquid during endoscopic application and transforms to gel at body temperature after application on ulcers. In an in vitro cellular wounding assay, recombinant human epidermal growth factor sol-gel significantly enhanced the cell migration and decreased the wounding area (68%) compared to nontreated, recombinant human epidermal growth factor solution, and sol-gel without recombinant human epidermal growth factor (42, 49, and 32 % decreased at day 1). The in vivo ulcer-healing study was performed in an acetic acid-induced gastric ulcer rat model and proved that our recombinant human epidermal growth factor endoscopic sol-gel facilitated the ulcer-healing process more efficiently than the other treatments. Ulcer sizes in the recombinant human epidermal growth factor sol-gel group were decreased 2.9- and 2.1-fold compared with those in the nontreated group on days 1 and 3 after ulceration, respectively. The mucosal thickness in the recombinant human epidermal growth factor sol-gel group was significantly increased compared to that in the nontreated group (3.2- and 6.9-fold on days 1 and 3 after ulceration, respectively). In a gastric retention study, recombinant human epidermal growth factor sol-gel stayed on the gastric mucosa more than 2 h after application. The present study suggests that recombinant human epidermal growth factor sol-gel is a prospective candidate for treating gastric ulcers via endoscopic application.

  12. Spectroscopic and electrochemical characterization of cytochrome c encapsulated in a bio sol-gel matrix.

    Science.gov (United States)

    Deriu, Daniela; Pagnotta, Sara Emanuela; Santucci, Roberto; Rosato, Nicola

    2008-08-01

    Sol-gel technique represents a remarkably versatile method for protein encapsulation. To enhance sol-gel biocompatibility, systems envisaging the presence of calcium and phosphates in the sol-gel composition were recently prepared and investigated. Unfortunately, the low pH at which solutions were prepared (pH proteins, because the acidic environment induces protein denaturation. In this paper we apply a new protocol based on the introduction of calcium nitrate to the inorganic phase, with formation of a binary bioactive system. In this case protein encapsulation results versatile and secure, being achieved at a pH close to neutrality (pH 6.0); also, the presence of calcium is expected to enhance system biocompatibility. To determine the properties of the salt-doped sol-gel and the influence exerted on entrapped biosystems, the structural and functional properties of embedded cytochrome c have been investigated. Data obtained indicate that the salt-doped sol-gel induces no significant change in the structure and the redox properties of the embedded protein; also, the matrix increases protein stability. Interestingly, the presence of calcium nitrate appears determinant for refolding of the acid-denatured protein. This is of interest in the perspective of future applications in biosensoristic area.

  13. Sol-gel synthesis of lanthanum-gallate-based ceramic coatings

    International Nuclear Information System (INIS)

    Golubko, N.V.; Kaleva, G.M.; Roginskaya, Yu.E.; Politova, E.D.

    2007-01-01

    Phase-pure (La 0.9 Sr 0.1 )(Ga 0.7 Fe 0.3 )O 3-y and (Sr 1.8 La 0.2 )(GaFe)O 5.1 solid solutions with the perovskite and brownmillerite structures have been prepared from salt solutions by sol-gel processing at temperatures from 570 to 870 K. Ceramic coatings up to 100 μm in thickness have been produced by applying suspensions of the sol-gel powders to various substrates. The structure and microstructure of the ceramic coatings have been studied by X-ray diffraction and scanning electron microscopy [ru

  14. Positron annihilation lifetime studies of sol-gel transition of carrageenan gels

    International Nuclear Information System (INIS)

    Wakabayashi, Y.; Ito, K.; Li, H.L.; Ujihara, Y.

    1996-01-01

    Positron annihilation lifetime measurement was applied to study the sol-gel transition of anionic polysaccharide aqueous solutions in terms of free-volume parameters the size, intensity, and size distribution of free volumes of the gelation of K-form κ-carrageenan solutions as a function of temperature. Slight variations of free volume size and intensity against temperature were observed near 295 K. The correlation of free-volume data with other physical properties vibrational spectra (IR and Raman), conductivity, SAXS, elastic measurement, differential scanning calorimetry were investigated to understand the mechanism of sol-gel transition of carrageenan. (author)

  15. Sol-gel processing to form doped sol-gel monoliths inside hollow core optical fiber and sol-gel core fiber devices made thereby

    Science.gov (United States)

    Shaw, Harry C. (Inventor); Ott, Melanie N. (Inventor); Manuel, Michele V. (Inventor)

    2002-01-01

    A process of fabricating a fiber device includes providing a hollow core fiber, and forming a sol-gel material inside the hollow core fiber. The hollow core fiber is preferably an optical fiber, and the sol-gel material is doped with a dopant. Devices made in this manner includes a wide variety of sensors.

  16. Processing and Characterization of Sol-Gel Cerium Oxide Microspheres

    Energy Technology Data Exchange (ETDEWEB)

    McClure, Zachary D. [Pacific Northwest National Lab. (PNNL), Richland, WA (United States); Padilla Cintron, Cristina [Pacific Northwest National Lab. (PNNL), Richland, WA (United States)

    2016-09-27

    Of interest to space exploration and power generation, Radioisotope Thermoelectric Generators (RTGs) can provide long-term power to remote electronic systems without the need for refueling or replacement. Plutonium-238 (Pu-238) remains one of the more promising materials for thermoelectric power generation due to its high power density, long half-life, and low gamma emissions. Traditional methods for processing Pu-238 include ball milling irregular precipitated powders before pressing and sintering into a dense pellet. The resulting submicron particulates of Pu-238 quickly accumulate and contaminate glove boxes. An alternative and dust-free method for Pu-238 processing is internal gelation via sol-gel techniques. Sol-gel methodology creates monodisperse and uniform microspheres that can be packed and pressed into a pellet. For this study cerium oxide microspheres were produced as a surrogate to Pu-238. The similar electronic orbitals between cerium and plutonium make cerium an ideal choice for non-radioactive work. Before the microspheres can be sintered and pressed they must be washed to remove the processing oil and any unreacted substituents. An investigation was performed on the washing step to find an appropriate wash solution that reduced waste and flammable risk. Cerium oxide microspheres were processed, washed, and characterized to determine the effectiveness of the new wash solution.

  17. Sol-gel derived C-SiC composites and protective coatings for sustained durability in the space environment

    Science.gov (United States)

    Haruvy, Yair; Liedtke, Volker

    2003-09-01

    Composites and coatings were produced via the fast sol-gel process of a mixture of alkoxysilane precursors. The composites were comprised of carbon fibers, fabrics, or their precursors as reinforcement, and sol-gel-derived silicon carbide as matrix, aiming at high-temperature stable ceramics that can be utilized for re-entry structures. The protective coatings were comprised of fluorine-rich sol-gel derived resins, which exhibit high flexibility and coherence to provide sustained ATOX protection necessary for LEO space-exposed elements. For producing the composites, the sol-gel-derived resin is cast onto the reinforcement fibers/fabrics mat (carbon or its precursors) to produce a 'green' composite that is being cured. The 'green' composite is converted into a C-SiC composite via a gradual heat-pressure process under inert atmosphere, during which the organic substituents on the silicon atoms undergo internal oxidative pyrolysis via the schematic reaction: (SiRO3/2)n -> SiC + CO2 + H2O. The composition of the resultant silicon-oxi-carbide is tailorable via modifying the composition of the sol-gel reactants. The reinforcement, when made of carbon precursors, is converted into carbon during the heat-and-pressure processing as well. The C-SiC composites thus derived exhibit superior thermal stability and comparable thermal conductivity, combined with good mechanical strength features and failure resistance, which render them greatly applicable for re-entry shielding, heat-exchange pipes, and the like. Fluorine rich sol-gel derived coatings were developed as well, via the use of HF rich sol-gel process. These coatings provide oxidation-protection via the silica formation process, together with flexibility that allows 18,000 repetitive folding of the coating without cracking.

  18. Bioactive materials for biomedical applications using sol-gel technology

    International Nuclear Information System (INIS)

    Gupta, Radha; Kumar, Ashok

    2008-01-01

    This review paper focuses on the sol-gel technology that has been applied in many of the potential research areas and highlights the importance of sol-gel technology for preparing bioactive materials for biomedical applications. The versatility of sol-gel chemistry enables us to manipulate the characteristics of material required for particular applications. Sol-gel derived materials have proved to be good biomaterials for coating films and for the construction of super-paramagnetic nanoparticles, bioactive glasses and fiberoptic applicators for various biomedical applications. The introduction of the sol-gel route in a conventional method of preparing implants improves the mechanical strength, biocompatibility and bioactivity of scaffolds and prevents corrosion of metallic implants. The use of organically modified silanes (ORMOSILS) yields flexible and bioactive materials for soft and hard tissue replacement. A novel approach of nitric-oxide-releasing sol-gels as antibacterial coatings for reducing the infection around orthopedic implants has also been discussed

  19. Sol-Gel Entrapped Levonorgestrel Antibodies: Activity and Structural Changes as a Function of Different Polymer Formats

    Science.gov (United States)

    Shalev, Moran; Miriam, Altstein

    2011-01-01

    The paper describes development of a sol-gel based immunoaffinity method for the steroid hormone levonorgestrel (LNG) and the effects of changes in the sol-gel matrix format on the activity of the entrapped antibodies (Abs) and on matrix structure. The best sol-gel format for Ab entrapment was found to be a tetramethoxysilane (TMOS) based matrix at a TMOS:water ratio of 1:8, containing 10% polyethylene glycol (PEG) of MW 0.4 kDa. Addition of higher percentages of PEG or a higher MW PEG did not improve activity. No activity was obtained with a TMOS:water ratio of 1:12, most likely because of the very dense polymer that resulted from these polymerization conditions. Only minor differences in the non-specific binding were obtained with the various formats. TMOS was found to be more effective than tetrakis (2-hydroxyethyl)orthosilicate (THEOS) for entrapment of anti-levonorgestrel (LNG) Abs. However, aging the THEOS-based sol-gel for a few weeks at 4 °C stabilized the entrapped Abs and increased its binding capacity. Confocal fluorescent microscopy with fluorescein isothiocyanate (FITC) labeled immunoglobulines (IgGs) entrapped in the sol-gel matrix showed that the entrapped Abs were distributed homogenously within the gel. Scanning electron microscopy (SEM) images have shown the diverse structures of the various sol-gel formats and precursors. PMID:28880001

  20. Matrix molecularly imprinted mesoporous sol-gel sorbent for efficient solid-phase extraction of chloramphenicol from milk.

    Science.gov (United States)

    Samanidou, Victoria; Kehagia, Maria; Kabir, Abuzar; Furton, Kenneth G

    2016-03-31

    Highly selective and efficient chloramphenicol imprinted sol-gel silica based inorganic polymeric sorbent (sol-gel MIP) was synthesized via matrix imprinting approach for the extraction of chloramphenicol in milk. Chloramphenicol was used as the template molecule, 3-aminopropyltriethoxysilane (3-APTES) and triethoxyphenylsilane (TEPS) as the functional precursors, tetramethyl orthosilicate (TMOS) as the cross-linker, isopropanol as the solvent/porogen, and HCl as the sol-gel catalyst. Non-imprinted sol-gel polymer (sol-gel NIP) was synthesized under identical conditions in absence of template molecules for comparison purpose. Both synthesized materials were characterized by Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectroscopy (FT-IR) and nitrogen adsorption porosimetry, which unambiguously confirmed their significant structural and morphological differences. The synthesized MIP and NIP materials were evaluated as sorbents for molecularly imprinted solid phase extraction (MISPE) of chloramphenicol in milk. The effect of critical extraction parameters (flow rate, elution solvent, sample and eluent volume, selectivity coefficient, retention capacity) was studied in terms of retention and desorption of chloramphenicol. Competition and cross reactivity tests have proved that sol-gel MIP sorbent possesses significantly higher specific retention and enrichment capacity for chloramphenicol compared to its non-imprinted analogue. The maximum imprinting factor (IF) was found as 9.7, whereas the highest adsorption capacity of chloramphenicol by sol-gel MIP was 23 mg/g. The sol-gel MIP was found to be adequately selective towards chloramphenicol to provide the necessary minimum required performance limit (MRPL) of 0.3 μg/kg set forth by European Commission after analysis by LC-MS even without requiring time consuming solvent evaporation and sample reconstitution step, often considered as an integral part in solid phase extraction work-flow. Intra and

  1. Sol-gel chemistry applied to the synthesis of polymetallic oxides including actinides reactivity and structure from solution to solid state; Synthese par voie douce d'oxydes polymetalliques incluant des actinides: reactivite et structure de la solution au solide

    Energy Technology Data Exchange (ETDEWEB)

    Lemonnier, St

    2006-02-15

    Minor actinides transmutation is studied at present in order to reduce the radiotoxicity of nuclear waste and the assessment of its technical feasibility requires specific designed materials. When considering americium, yttria stabilized zirconia (Am{sup III} YII Zriv)Or{sub x} is among the ceramic phases that one which presents the required physico-chemical properties. An innovative synthesis of this mixed oxide by sol-gel process is reported in this manuscript. The main aim of this work is to adjust the reactivity of the different metallic cations in aqueous media using complexing agent, in order to initiate a favourable interaction for a homogeneous elements repartition in the forming solid phase. The originality of the settled synthesis lies on an in-situ formation of a stable and monodisperse nano-particles dispersion in the presence of acetylacetone. The main reaction mechanisms have been identified: the sol stabilisation results from an original interaction between the three compounds (Zrly, trivalent cations and acetylacetone). The sol corresponds to a structured system at the nanometer scale for which zirconium and trivalent cations are homogeneously dispersed, preliminary to the sol-gel transition. Furthermore, preliminary studies were carried out with a view to developing materials. They have demonstrated that numerous innovative and potential applications can be developed by taking advantage of the direct and controlled formation of the sol and by adapting the sol-gel transition. The most illustrating result is the preparation of a sintered pellet with the composition Am0,13Zro,73Yo,0901,89 using this approach. (author)

  2. The increase in pH during aging of porous sol-gel silica spheres

    NARCIS (Netherlands)

    Titulaer, M.K.; Kegel, W.K.; Jansen, J.B.H.; Geus, John W.

    1994-01-01

    The increase in pH in the hydrothermal fluid is studied after hydrothermal aging of porous silica gel spheres of 1–3 mm diameter. The porous silica spheres are formed by the sol-gel process from a supersaturated silica solution. The increase of the pH of the hydrothermal solution affects the silica

  3. Sol-gel coatings on large area glass sheets for electrochromic devices

    NARCIS (Netherlands)

    Vroon, Z.A.E.P.; Spee, C.I.M.A.

    1997-01-01

    The preparation of vanadium and tungsten oxide coatings is described using vanadium oxide tri-2-propoxide/2-propanol and tungsten penta-ethoxide/2-propanol solutions. These solutions are dip coated onto K-glass substrates and cured. For vanadium oxide coatings it is shown that sol-gel/dip coat

  4. Abstracts of International Conference on Sol-Gel Materials' 04

    International Nuclear Information System (INIS)

    2004-01-01

    International Conference on Sol-Gel Materials '04 was an important forum for discussion on problems related to sol-gel processes applied for preparation materials with special physical properties and assignment. The application of sol-gel materials as phosphors, surface coatings, sensors, waveguides, medical implants, joints etc. has been presented. Preparation conditions, methods of physical characterization as well as optimal chemical composition of such materials have been also discussed in detail

  5. Bioorganically doped sol-gel materials containing amyloglucosidase activity

    Directory of Open Access Journals (Sweden)

    Vlad-Oros Beatrice

    2006-01-01

    Full Text Available Amyloglucosidase (AMG from Aspergillus niger was encapsulated in various matrices derived from tetraethoxysilane, methyltriethoxysilane, phenyltriethoxysilane and vinyltriacetoxysilane by different methods of immobilization. The immobilized enzyme was prepared by entrapment in two steps, in one-step and entrapment/deposition, respectively. The activities of the immobilized AMG were assayed and compared with that of the native enzyme. The effects of the organosilaneprecursors and their molar ratios, the immobilization method, the inorganic support (white ceramic, red ceramic, purolite, alumina, TiO2, celite, zeolite and enzyme loading upon the immobilized enzyme activity were tested. The efficiency of the sol-gel biocomposites can be improved through combination of the fundamental immobilization techniques and selection of the precursors.

  6. Industrial applications of sol-gel technology

    International Nuclear Information System (INIS)

    Tuloch, S.M.; Tulloch, G.E.

    1995-01-01

    The purpose of this paper has been to provide a broad, rather than comprehensive view. We have presented a range of applications and only a selection of involved companies and researchers and have relied to a large extent on published information. Nevertheless, we are sure that our view of the importance of Sol-gel technology as an emerging technology, with enormous impact across a wide range of manufacturing, is demonstrated. Applications which are either in production or have been foreshadowed include four broad categories: coatings, fibres, powders and monoliths

  7. Effect of vanadium on the obtaining of the titanium dioxide by Sol-Gel Method; Efeito do vanadio na obtencao de dioxido de titanio pelo Metodo Sol-Gel

    Energy Technology Data Exchange (ETDEWEB)

    Granado, S.R.; Silva, D.W.; Lopes, S.A.; Cavalheiro, A.A., E-mail: sandrogranado02@gmail.com [Universidade Estadual de Mato Grosso do Sul (CPTREN/UEMS), Navirai, MS (Brazil). Centro de Pesquisas Tecnologicas em Recursos Naturais

    2011-07-01

    The obtaining of transition metal modified titanium dioxide (TiO{sub 2}) can be a promising path to promote changes in crystal structure of anatase phase in order to displace the band gap toward frequencies near to visible region. The insertion of the heterovalent ions such as vanadium can be shift the titanium coordination number in the anatase matrix, leading to important changes in the photonic characteristics of the material. In Sol-Gel method, the presence of the non alkoxide precursors can affects the stability of the solution and the gelifying process, with consequences on the characteristics of the material. In this work, it was investigated the effect of 5mol% of vanadium by thermal analysis of the dried gel and XRD and adsorption isotherm in the samples obtained at different temperatures. The decomposition steps of the precursor were associated to phase formation in the material, leading to conclusion that the presence of vanadium affects the stability of anatase phase. (author)

  8. Study of silica sol-gel materials for sensor development

    Science.gov (United States)

    Lei, Qiong

    Silica sol-gel is a transparent, highly porous silicon oxide glass made at room temperature by sol-gel process. The name of silica sol-gel comes from the observable physical phase transition from liquid sol to solid gel during its preparation. Silica sol-gel is chemically inert, thermally stable, and photostable, it can be fabricated into different desired shapes during or after gelation, and its porous structure allows encapsulation of guest molecules either before or after gelation while still retaining their functions and sensitivities to surrounding environments. All those distinctive features make silica sol-gel ideal for sensor development. Study of guest-host interactions in silica sol-gel is important for silica-based sensor development, because it helps to tailor local environments inside sol-gel matrix so that higher guest loading, longer shelf-life, higher sensitivity and faster response of silica gel based sensors could be achieved. We focused on pore surface modification of two different types of silica sol-gel by post-grafting method, and construction of stable silica hydrogel-like thin films for sensor development. By monitoring the mobility and photostability of rhodamine 6G (R6G) molecules in silica alcogel thin films through single molecule spectroscopy (SMS), the guest-host interactions altered by post-synthesis grafting were examined. While physical confinement remains the major factor that controls mobility in modified alcogels, both R6G mobility and photostability register discernable changes after surface charges are respectively reversed and neutralized by aminopropyltriethoxysilane (APTS) and methyltriethoxysilane (MTES) grafting. The change in R6G photostability was found to be more sensitive to surface grafting than that of mobility. In addition, silica film modification by 0.4% APTS is as efficient as that by pure MTES in lowering R6G photostability, which suggests that surface charge reversal is more effective than charge neutralization

  9. Sol-gel reaction stability studied: Influence in the formation temperature and properties of ferroelectric thin films

    International Nuclear Information System (INIS)

    Perez, J.; Vilarinho, P.M.; Kholkin, A.L.; Almeida, A.

    2009-01-01

    Lead zirconium titanate (PZT) sol-gel solutions were prepared based on distilled lead acetate precursor solutions. A detailed analysis of the distillation effect on the lead precursor and the final PZT solution were carried out by Infrared and Raman techniques. It was found that the increase in the number of distillation steps experienced by the lead precursor solutions removes the constitutional water and increases the lead acetate-2-methoxyethanol interconnectivity; thus improving stability and avoiding the aging effect of the resulting PZT solutions. The thermal decomposition process of the PZT solutions was analyzed based on the thermogravimetric (TG) and differential thermogravimetric analysis (DTA) measurements. It was found that as the number of distillation steps in the lead precursor solutions increases, the decomposition rate increases and the formation temperature of pure perovskite PZT films decreases. X-ray diffraction (XRD) technique was used to study the film phase formation. A pure perovskite phase at 500 deg. C was found by the XRD analysis after the second distillation step. Scanning electron microscope technique was used to carry out the microstructural analysis. Dense microstructure was found in all analyzed films and an incipient columnar grain growth was revealed in PZT films prepared based on lead precursor solution with more than three distillation steps. The dependence of the dielectric, ferroelectric and piezoelectric properties on the number of distillation steps was revealed and a correlation between the distillation process, film microstructure properties and electrical performance was established

  10. Development of novel biocompatible hybrid nanocomposites based on polyurethane-silica prepared by sol gel process

    Energy Technology Data Exchange (ETDEWEB)

    Rashti, Ali [Department of Medical Nanotechnology, School of Advanced Technologies in Medicine, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Yahyaei, Hossein [Department of Polymer Engineering and Color Technology, Amirkabir University of Technology, Tehran (Iran, Islamic Republic of); Firoozi, Saman [Department of Tissue Engineering & Regenerative Medicine, Faculty of Advanced Technologies in Medicine, Iran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Ramezani, Sara [Department of Neuroscience, School of Advanced Technologies in Medicine, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Rahiminejad, Ali [Department of Medical Nanotechnology, School of Advanced Technologies in Medicine, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Karimi, Roya [Department of Tissue Engineering and Applied Cell Science, School of Advanced Technologies in Medicine, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Farzaneh, Khadijeh [Tehran Heart Center, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Mohseni, Mohsen [Department of Polymer Engineering and Color Technology, Amirkabir University of Technology, Tehran (Iran, Islamic Republic of); Ghanbari, Hossein, E-mail: hghanbari@tums.ac.ir [Department of Medical Nanotechnology, School of Advanced Technologies in Medicine, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Tehran Heart Center, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Medical Biomaterials Research Center, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of)

    2016-12-01

    Due to high biocompatibility, polyurethane has found many applications, particularly in development of biomedical devices. A new nanocomposite based on thermoset polyurethane and silica nanoparticles was synthesized using sol-gel method. Sol-gel process was fulfilled in two acidic and basic conditions by using tetraethylorthosilicate (TEOS) and trimethoxyisocyanatesilane as precursors. The hybrid films characterized for mechanical and surface properties using tensile strength, contact angle, ATR-FTIR and scanning electron microscopy. Biocompatibility and cytotoxicity of the hybrids were assessed using standard MTT, LDH and TUNEL assays. The results revealed that incorporation of silica nanoparticles was significantly improved tensile strength and mechanical properties of the hybrids. Based on the contact angle results, silica nanoparticles increased hydrophilicity of the hybrids. Biocompatibility by using human lung epithelial cell line (MRC-5) demonstrated that the hybrids were significantly less cytotoxic compared to pristine polymer as tested by MTT and LDH assays. TUNEL assay revealed no signs of apoptosis in all tested samples. The results of this study demonstrated that incorporation of silica nanoparticles into polyurethane lead to the enhancement of biocompatibility, indicating that these hybrids could potentially be used in biomedical field in particular as a new coating for medical implants. - Highlights: • Nanocomposites based on polyurethane and nanosilica prepared by sol-gel method fabricated • Addition of inorganic phase improved mechanical properties. • Nanosilica prepared by sol-gel method increased hydrophilicity. • By adding nanosilica to polyurethane biocompatibility increased significantly.

  11. Sol-gel synthesis of YBa2Cu3O7-x superconductor by mixed organic-inorganic polymerization

    International Nuclear Information System (INIS)

    Valente, I.; Sanchez, C.; Henry, M.; Livage, J.

    1989-01-01

    Sol-gel processes are quite attractive methods to produce films or fibers of high Tc superconducting materials. The gel step allows a good chemical homogeneity and generally provides a rather low processing temperature. Blue sols or monolithic gels can be easily produced using mixed organic-inorganic polymerisation of molecular precursors. An aqueous solution of copper, barium acetates and yttrium nitrate is mixed with an acrylic acid solution where a radical organic polymerisation process has been initiated. After pH adjustments, the viscosity of the resulting solution can be adjusted by heating. After drying at 150 0 C and calcination above 700 0 C, the YBaCuO network is formed and superconducting properties appears above 850 0 C. Fine particles (0.1-1 μm) are obtained which can be sintered to produce a ceramic material with a particularly narrow resistive transition [fr

  12. Computational investigation and synthesis of a sol-gel imprinted material for sensing application of some biologically active molecules

    Energy Technology Data Exchange (ETDEWEB)

    Atta, Nada F., E-mail: Nada_fah1@yahoo.com [Department of Chemistry, Faculty of Science, University of Cairo, Post Code 12613, Giza (Egypt); Hamed, Maher M.; Abdel-Mageed, Ali M. [Department of Chemistry, Faculty of Science, University of Cairo, Post Code 12613, Giza (Egypt)

    2010-05-14

    A hybrid sol-gel material was molecularly imprinted with a group of neurotransmitters. Imprinted material is a sol-gel thin film that is spin coated on the surface of a glassy carbon electrode. Imprinted films were characterized electrochemically using cyclic voltammetry (CV) and the encapsulated molecules were extracted from the films and complementary molecular cavities are formed that enable their rebind. The films were tested in their corresponding template solutions for rebinding using square wave voltammetry (SWV). Computational approach for exploring the primary intermolecular forces between templates and hydrolyzed form of the precursor monomer, tetraethylorthosilicate (TEOS), were carried out using Hartree-Fock method (HF). Interaction energy values were computed for each adduct formed between a monomer and a template. Analysis of the optimized conformations of various adducts could explain the mode of interaction between the templates and the monomer units. We found that interaction via the amino group is the common mode among the studied compounds and the results are in good agreement with the electrochemical measurements.

  13. Structural and optical properties of sol-gel deposited proton conducting Ta{sub 2}O{sub 5} films

    Energy Technology Data Exchange (ETDEWEB)

    Ozer, N.; Lampert, C.M.

    1995-08-01

    Proton conducting tantalum oxide films were deposited by spin coating using a sol-gel process. The coating solutions were prepared using Ta(OC{sub 2}H{sub 5}){sub 5} as a precursor. X-ray diffraction studies determined that the sol-gel films, heat treated at temperatures below 400 C, were amorphous. Films heat treated at higher temperatures were crystalline Ta{sub 2}O{sub 5}. The solar transmission values (T{sub s}) of tantala films on glass generally range from 0.8--0.9 depending on thickness. The refractive index and the extinction coefficient were evaluated from transmittance characteristics in the UV-VIS-NIR regions. The refractive index values calculated at 550 nm increased from 1.78 to 1.97 with increasing heat treatment from 150 to 450 C. The films heat treated at different temperatures showed low absorption with extinction coefficients of less than k=1x10{sup -3} in the visible range. Spectrophotometric and impedance spectroscopic investigations performed on Ta{sub 2}O{sub 5} films revealed that these films have protonic conductivity of 3.2x10{sup -6} S/cm. The films are suitable for proton conducting layers in electrochromic (EC) devices.

  14. Catalytic activity of acid and base with different concentration on sol-gel kinetics of silica by ultrasonic method.

    Science.gov (United States)

    Das, R K; Das, M

    2015-09-01

    The effects of both acid (acetic acid) and base (ammonia) catalysts in varying on the sol-gel synthesis of SiO2 nanoparticles using tetra ethyl ortho silicate (TEOS) as a precursor was determined by ultrasonic method. The ultrasonic velocity was received by pulsar receiver. The ultrasonic velocity in the sol and the parameter ΔT (time difference between the original pulse and first back wall echo of the sol) was varied with time of gelation. The graphs of ln[ln1/ΔT] vs ln(t), indicate two region - nonlinear region and a linear region. The time corresponds to the point at which the non-linear region change to linear region is considered as gel time for the respective solutions. Gelation time is found to be dependent on the concentration and types of catalyst and is found from the graphs based on Avrami equation. The rate of condensation is found to be faster for base catalyst. The gelation process was also characterized by viscosity measurement. Normal sol-gel process was also carried out along with the ultrasonic one to compare the effectiveness of ultrasonic. The silica gel was calcined and the powdered sample was characterized with scanning electron microscopy, energy dispersive spectra, X-ray diffractogram, and FTIR spectroscopy. Copyright © 2014 Elsevier B.V. All rights reserved.

  15. Fabrication and study of sol-gel ZnO films for use in Si-based heterojunction photovoltaic devices

    Directory of Open Access Journals (Sweden)

    Daniya Mukhamedshina

    2017-12-01

    Full Text Available This paper considers the use of zinc oxide thin films prepared via the sol-gel route as an n-type layer in heterojunction ZnO/Si solar cells. The ZnO films were prepared via a simple spin-coating technique using zinc acetate dihydrate as a zinc precursor, isopropanol as a solvent and monoethanolamine as a stabilizing agent. Optical, structural and morphological properties of ZnO were investigated for thin films grown from sol-gel solutions with different concentrations both on glass and silicon substrates. As such, a distribution of crystallite sizes and surface topology parameters corresponding to various zinc acetate dihydrate concentrations were obtained to elucidate optimal film deposition conditions. Correlation between thin film morphology and structural characteristics of ZnO thin films was made based on atomic-force microscopy studies. Finally, our results on fabrication, characterization and simulation of ZnO/Si heterojunctions for use as photovoltaic devices are presented. Although noticeable rectifying and photovoltaic properties were observed for Al/Si/ZnO/Ti/Au devices, there appears to exist a considerable room for device improvement with simulation studies suggesting that efficiencies of the order of 24% may be obtained for devices with optimal silicon wafer passivation, i.e. with lifetimes of the order of 1000 μs.

  16. Preparation and characterization of quercetin-loaded silica microspheres stabilized by combined multiple emulsion and sol-gel processes

    Directory of Open Access Journals (Sweden)

    Kim Young Ho

    2015-01-01

    Full Text Available Despite exhibiting a wide spectrum of cosmeceutical properties, flavonoids and related compounds have some limitations related to their stability and solubility in distilledwater. In this project, we prepared silica microspheres using a novel method that uses polyol-in-oil-in-water (P/O/W emulsion and sol-gel methods as techniques for stabilizing quercetin. A stable microsphere suspension was successfully preparedusing a mixed solvent system comprising a polyol-phase medium for performing the sol-gel processing of tetraethyl orthosilicate (TEOS as an inorganic precursor with outer water phase. The morphology of the microsphere was evaluated using a scanning electron microscope (SEM, which showed a characteristic spherical particle shape with a smooth surface. Furthermore, SEM/EDSanalysis of a representative microsphere demonstrated that the inner structure of the silica microspheres was filled with quercetin. The mean diameter of the microsphere was in the range 20.6-35.0 μm, and the encapsulation efficiency ranged from 17.8% to 27.5%. The free and encapsulated quercetin samples were incubated in separateaqueous solutions at 25 and 42°C for 28 days. The residualcontent of the quercetin encapsulated by silica microspheres was 82% at 42°C. In contrast, that of the free quercetin stored at 42°C decreased to ~24%.

  17. Uranium Dioxide Powder Flow ability Improvement Using Sol-Gel

    International Nuclear Information System (INIS)

    Juanda, D.; Sambodo Daru, G.

    1998-01-01

    The improvement of flow ability characteristics of uranium dioxide powder has been done using sol-gel process. To anticipate a pellet mass production with uniform pellet dimension, the uranium dioxide powder must be have a spherical form. Uranium dioxide spherical powder has been diluted in acid transformed into sol colloidal solution. To obtain uranium dioxide spherical form, the uranium sol-colloidal solution has been dropped in a hot paraffin ( at the temperature of 90 0 C) to form gelatinous colloid and then dried at 800 0 C, and sintered at the temperature of 1700 0 C. The flow ability of spherical uranium dioxide powder has been examined by using Flowmeter Hall (ASTM. B. 213-46T). The measurement result reveals that the spherical uranium dioxide powder has a flow ability twice than that of unprocessed uranium dioxide powder

  18. Sol-Gel processing of silica nanoparticles and their applications.

    Science.gov (United States)

    Singh, Lok P; Bhattacharyya, Sriman K; Kumar, Rahul; Mishra, Geetika; Sharma, Usha; Singh, Garima; Ahalawat, Saurabh

    2014-11-06

    Recently, silica nanoparticles (SNPs) have drawn widespread attention due to their applications in many emerging areas because of their tailorable morphology. During the last decade, remarkable efforts have been made on the investigations for novel processing methodologies to prepare SNPs, resulting in better control of the size, shape, porosity and significant improvements in the physio-chemical properties. A number of techniques available for preparing SNPs namely, flame spray pyrolysis, chemical vapour deposition, micro-emulsion, ball milling, sol-gel etc. have resulted, a number of publications. Among these, preparation by sol-gel has been the focus of research as the synthesis is straightforward, scalable and controllable. Therefore, this review focuses on the recent progress in the field of synthesis of SNPs exhibiting ordered mesoporous structure, their distribution pattern, morphological attributes and applications. The mesoporous silica nanoparticles (MSNPs) with good dispersion, varying morphology, narrow size distribution and homogeneous porous structure have been successfully prepared using organic and inorganic templates. The soft template assisted synthesis using surfactants for obtaining desirable shapes, pores, morphology and mechanisms proposed has been reviewed. Apart from single template, double and mixed surfactants, electrolytes, polymers etc. as templates have also been intensively discussed. The influence of reaction conditions such as temperature, pH, concentration of reagents, drying techniques, solvents, precursor, aging time etc. have also been deliberated. These MSNPs are suitable for a variety of applications viz., in the drug delivery systems, high performance liquid chromatography (HPLC), biosensors, cosmetics as well as construction materials. The applications of these SNPs have also been briefly summarized. Copyright © 2014 Elsevier B.V. All rights reserved.

  19. Biocatalysis with Sol-Gel Encapsulated Acid Phosphatase

    Science.gov (United States)

    Kulkarni, Suhasini; Tran, Vu; Ho, Maggie K.-M.; Phan, Chieu; Chin, Elizabeth; Wemmer, Zeke; Sommerhalter, Monika

    2010-01-01

    This experiment was performed in an upper-level undergraduate biochemistry laboratory course. Students learned how to immobilize an enzyme in a sol-gel matrix and how to perform and evaluate enzyme-activity measurements. The enzyme acid phosphatase (APase) from wheat germ was encapsulated in sol-gel beads that were prepared from the precursor…

  20. Reversible sol-gel-sol medium for enzymatic optical biosensors

    NARCIS (Netherlands)

    Safaryan, S.; Yakovlev, A.; Pidko, E.A.; Vinogradov, A.; Vinogradov, V.

    2017-01-01

    In this paper we for the first time report a reversible sol-gel-sol approach to obtain optical enzymatic biosensors with improved enzyme stability and good sensitivity by using desktop inkjet printing. The developed technique is based on the bio-inorganic inks allowing for a sol-gel-sol transition

  1. Self-Healing Corrosion Protective Sol-Gel Coatings

    NARCIS (Netherlands)

    Abdolah Zadeh, M.

    2016-01-01

    Inspired by the state of the art and the recent advances in the field of self-healing corrosion protective coatings, the thesis entitled “Self-healing corrosion protective sol-gel coatings” addresses novel routes to self-healing corrosion protective sol-gel coatings via extrinsic and intrinsic

  2. Structure and properties of carbon nanotubes/sol-gel nanocomposites

    International Nuclear Information System (INIS)

    Pokrass, Mariana

    2013-08-01

    Carbon Nanotubes (CNTs) are promising filler materials owing to their exceptional mechanical, electrical, thermal and optical properties. Since their discovery in 1991, a major effort has been made in developing CNT-polymer nanocomposites, whereas CNT/ceramic based nanocomposites, in particularly, CNT/silica nanocomposites, have been very little studied. This thesis focuses on preparation and characterization of novel CNT/silica nanocomposite glasses synthesized by the Sol-Gel technology. A comprehensive analysis of their morphological, optical, and electrical properties was conducted, and analyzed according to existing theoretical models. The nanocomposites hosting matrix is a hybrid organic/inorganic glass prepared by the Fast-Sol-Gel (FSG) route. Using specific conditions in the FSG procedure, the resultant glasses are nonporous, exhibiting no contraction upon drying. Their analogous Classical-Sol-Gel (CSG) glasses, however, are porous, and do exhibit contraction upon drying. The FSG glasses are relatively new materials, and their physical and optical properties were only meagerly studied. In our present work we have conducted a comprehensive experimental research on some previously ignored characteristics such as: UV-vis-IR optical absorption and transmission, and the organic content effect on the refraction index n, density ρ, thermal expansion coefficient β, and thermo-optic coefficient dn/dT. We found that organic residues within the glass decrease the refractive index, density, and thermo-optic coefficient. The thermal expansion coefficient, however, increases with the organic content. A negative linear dependence of the thermo-optic coefficient on the thermal expansion coefficient was obtained. CNT/FSG nanocomposites were prepared by using a solution mixing method, while CNT/CSG nanocomposites were prepared by means of an in situ polymerization technique. Nanocomposites based on FSG hybrid glasses were characterized for their nonlinear optical and

  3. Processing of non-oxide ceramics from sol-gel methods

    Science.gov (United States)

    Landingham, Richard; Reibold, Robert A.; Satcher, Joe

    2014-12-12

    A general procedure applied to a variety of sol-gel precursors and solvent systems for preparing and controlling homogeneous dispersions of very small particles within each other. Fine homogenous dispersions processed at elevated temperatures and controlled atmospheres make a ceramic powder to be consolidated into a component by standard commercial means: sinter, hot press, hot isostatic pressing (HIP), hot/cold extrusion, spark plasma sinter (SPS), etc.

  4. Solution precursor plasma deposition of nanostructured ZnO coatings

    International Nuclear Information System (INIS)

    Tummala, Raghavender; Guduru, Ramesh K.; Mohanty, Pravansu S.

    2011-01-01

    Highlights: → The solution precursor route employed is an inexpensive process with capability to produce large scale coatings at fast rates on mass scale production. → It is highly capable of developing tailorable nanostructures. → This technique can be employed to spray the coatings on any kind of substrates including polymers. → The ZnO coatings developed via solution precursor plasma spray process have good electrical conductivity and reflectivity properties in spite of possessing large amount of particulate boundaries, porosity and nanostructured grains. -- Abstract: Zinc oxide (ZnO) is a wide band gap semiconducting material that has various applications including optical, electronic, biomedical and corrosion protection. It is usually synthesized via processing routes, such as vapor deposition techniques, sol-gel, spray pyrolysis and thermal spray of pre-synthesized ZnO powders. Cheaper and faster synthesis techniques are of technological importance due to increased demand in alternative energy applications. Here, we report synthesis of nanostructured ZnO coatings directly from a solution precursor in a single step using plasma spray technique. Nanostructured ZnO coatings were deposited from the solution precursor prepared using zinc acetate and water/isopropanol. An axial liquid atomizer was employed in a DC plasma spray torch to create fine droplets of precursor for faster thermal treatment in the plasma plume to form ZnO. Microstructures of coatings revealed ultrafine particulate agglomerates. X-ray diffraction confirmed polycrystalline nature and hexagonal Wurtzite crystal structure of the coatings. Transmission electron microscopy studies showed fine grains in the range of 10-40 nm. Observed optical transmittance (∼65-80%) and reflectivity (∼65-70%) in the visible spectrum, and electrical resistivity (48.5-50.1 mΩ cm) of ZnO coatings are attributed to ultrafine particulate morphology of the coatings.

  5. Solution precursor plasma deposition of nanostructured ZnO coatings

    Energy Technology Data Exchange (ETDEWEB)

    Tummala, Raghavender [Department of Mechanical Engineering, University of Michigan - Dearborn, MI 48128 (United States); Guduru, Ramesh K., E-mail: rkguduru@umich.edu [Department of Mechanical Engineering, University of Michigan - Dearborn, MI 48128 (United States); Mohanty, Pravansu S. [Department of Mechanical Engineering, University of Michigan - Dearborn, MI 48128 (United States)

    2011-08-15

    Highlights: {yields} The solution precursor route employed is an inexpensive process with capability to produce large scale coatings at fast rates on mass scale production. {yields} It is highly capable of developing tailorable nanostructures. {yields} This technique can be employed to spray the coatings on any kind of substrates including polymers. {yields} The ZnO coatings developed via solution precursor plasma spray process have good electrical conductivity and reflectivity properties in spite of possessing large amount of particulate boundaries, porosity and nanostructured grains. -- Abstract: Zinc oxide (ZnO) is a wide band gap semiconducting material that has various applications including optical, electronic, biomedical and corrosion protection. It is usually synthesized via processing routes, such as vapor deposition techniques, sol-gel, spray pyrolysis and thermal spray of pre-synthesized ZnO powders. Cheaper and faster synthesis techniques are of technological importance due to increased demand in alternative energy applications. Here, we report synthesis of nanostructured ZnO coatings directly from a solution precursor in a single step using plasma spray technique. Nanostructured ZnO coatings were deposited from the solution precursor prepared using zinc acetate and water/isopropanol. An axial liquid atomizer was employed in a DC plasma spray torch to create fine droplets of precursor for faster thermal treatment in the plasma plume to form ZnO. Microstructures of coatings revealed ultrafine particulate agglomerates. X-ray diffraction confirmed polycrystalline nature and hexagonal Wurtzite crystal structure of the coatings. Transmission electron microscopy studies showed fine grains in the range of 10-40 nm. Observed optical transmittance ({approx}65-80%) and reflectivity ({approx}65-70%) in the visible spectrum, and electrical resistivity (48.5-50.1 m{Omega} cm) of ZnO coatings are attributed to ultrafine particulate morphology of the coatings.

  6. Fast and efficient proteolysis by reusable pepsin-encapsulated magnetic sol-gel material for mass spectrometry-based proteomics applications.

    Science.gov (United States)

    Kayili, H Mehmet; Salih, Bekir

    2016-08-01

    Hydrophobic silicon-based material having magnetic properties was fairly synthesized by a classical sol-gel approach. Pepsin enzyme was encapsulated in the sol-gel material and the enzyme activity was evaluated in consequence of the digestion of some common proteins such as α- and β-casein, cytochrome c, myoglobin, and bovine serum albumin (BSA) both in a single protein batch and in the protein mixture. The optimum digestion time of the studied proteins using pepsin-encapsulated magnetic sol-gel material was found to be 20min. To produce the magnetic sol-gel material for convenient and easy proteomics applications, Fe3O4 was doped inside sol-gel material during the gelation step. It was observed that the activity of encapsulated pepsin was not affected by the amount of Fe3O4. Poly(ethylene glycol) was also inserted in sol-gel bulk to obtain suitable roughness and increase the hydrophilicity of the material surface to let protein molecules reach to the sol-gel material easily. The digestion of the protein mixture and non-fat bovine milk was performed with the pepsin-encapsulated magnetic sol-gel material and the digested solutions were analyzed using SDS-PAGE, MALDI-TOF-MS and LC-MS/MS for the protein identification. Reusability of the pepsin-encapsulated sol-gel material was examined and it was determined that they could be used at least 20 times. Finally, IgG digestions with a fast incubation time period were carried out using pepsin-encapsulated sol-gel material for generation of (Fab)2 product to evaluate the kinetic performance of the material. Copyright © 2016 Elsevier B.V. All rights reserved.

  7. Hydrogen permeation through sol-gel-coated iron during galvanostatic charging

    International Nuclear Information System (INIS)

    Zakorchemna, I.; Carmona, N.; Zakroczymski, T.

    2008-01-01

    One-layer sol-gel silica-zirconia and two-layer silica-zirconia and zirconia coatings were deposited on one side of iron membranes by spin-coating, densified in air and annealed up to 800 deg. C in vacuum. Hydrogen permeation through the membranes, coated and uncoated, polarised cathodically under galvanostatic control in 0.1 M NaOH solution was studied using the electrochemical permeation technique. During the initial period, the effect of the sol-gel coatings was insignificant. However, the coatings quite efficiently prevented the iron surface become more active to hydrogen entry during a long-lasting cathodic polarisation. In addition, the electrochemical-corrosion behaviour of the coated iron and the effect of the sol-gel coatings on the effective diffusivity of hydrogen in the coated membranes were studied. On the basis of the polarisation curves and the hydrogen permeation data it was proved that the sol-gel coatings blocked the iron surface for the hydrogen evolution reaction and, consequently, for the hydrogen entry into iron. The effective coating coverage was determined by comparison of the hydrogen fluxes permeating the coated and uncoated membranes. Finally the real concentration of hydrogen beneath the uncoated iron sites and the amount of hydrogen stored in a membrane were evaluated

  8. A sol-gel-modified poly(methyl methacrylate) electrophoresis microchip with a hydrophilic channel wall.

    Science.gov (United States)

    Chen, Gang; Xu, Xuejiao; Lin, Yuehe; Wang, Joseph

    2007-01-01

    A sol-gel method was employed to fabricate a poly(methyl methacrylate) (PMMA) electrophoresis microchip that contains a hydrophilic channel wall. To fabricate such a device, tetraethoxysilane (TEOS) was injected into the PMMA channel and was allowed to diffuse into the surface layer for 24 h. After removing the excess TEOS, the channel was filled with an acidic solution for 3 h. Subsequently, the channel was flushed with water and was pretreated in an oven to obtain a sol-gel-modified PMMA microchip. The water contact angle for the sol-gel-modified PMMA was approximately 27.4 degrees compared with approximately 66.3 degrees for the pure PMMA. In addition, the electro-osmotic flow increased from 2.13x10(-4) cm2 V(-1) s(-1) for the native-PMMA channel to 4.86x10(-4) cm2 V(-1) s(-1) for the modified one. The analytical performance of the sol-gel-modified PMMA microchip was demonstrated for the electrophoretic separation of several purines, coupled with amperometric detection. The separation efficiency of uric acid increased to 74,882.3 m(-1) compared with 14,730.5 m(-1) for native-PMMA microchips. The result of this simple modification is a significant improvement in the performance of PMMA for microchip electrophoresis and microfluidic applications.

  9. A new sol-gel synthesis of 45S5 bioactive glass using an organic acid as catalyst.

    Science.gov (United States)

    Faure, J; Drevet, R; Lemelle, A; Ben Jaber, N; Tara, A; El Btaouri, H; Benhayoune, H

    2015-02-01

    In this paper a new sol-gel approach was explored for the synthesis of the 45S5 bioactive glass. We demonstrate that citric acid can be used instead of the usual nitric acid to catalyze the sol-gel reactions. The substitution of nitric acid by citric acid allows to reduce strongly the concentration of the acid solution necessary to catalyze the hydrolysis of silicon and phosphorus alkoxides. Two sol-gel powders with chemical compositions very close to that of the 45S5 were obtained by using either a 2M nitric acid solution or either a 5mM citric acid solution. These powders were characterized and compared to the commercial Bioglass®. The surface properties of the two bioglass powders were assessed by scanning electron microscopy (SEM) and by Brunauer-Emmett-Teller method (BET). The Fourier transformed infrared spectroscopy (FTIR) and the X-ray diffraction (XRD) revealed a partial crystallization associated to the formation of crystalline phases on the two sol-gel powders. The in vitro bioactivity was then studied at the key times during the first hours of immersion into acellular Simulated Body Fluid (SBF). After 4h immersion into SBF we clearly demonstrate that the bioactivity level of the two sol-gel powders is similar and much higher than that of the commercial Bioglass®. This bioactivity improvement is associated to the increase of the porosity and the specific surface area of the powders synthesized by the sol-gel process. Moreover, the nitric acid is efficiently substituted by the citric acid to catalyze the sol-gel reactions without alteration of the bioactivity of the 45S5 bioactive glass. Copyright © 2014 Elsevier B.V. All rights reserved.

  10. Molecularly imprinted sol-gel nanofibers based solid phase microextraction coupled on-line with high performance liquid chromatography for selective determination of acesulfame.

    Science.gov (United States)

    Moein, Mohammad Mahdi; Javanbakht, Mehran; Karimi, Mohammad; Akbari-Adergani, Behrouz

    2015-03-01

    Sol-gel based molecularly imprinted polymer (MIP) nanofiber was successfully fabricated by electrospinning technique on the surface of a stainless steel bar. The manufactured tool was applied for on-line selective solid phase microextraction (SPME) and determination of acesulfame (ACF) as an artificial sweetener with high performance liquid chromatography (HPLC). The selective ability of method for the extraction of ACF was investigated in the presence of some selected sweeteners such as saccharine (SCH), aspartame (ASP) and caffeine (CAF). Electrospinning of MIP sol-gel solution on the stainless steel bar provided an unbreakable sorbent with high thermal, mechanical, and chemical stability. Moreover, application of the MIP-SPME tool revealed a unique approach for the selective microextraction of the analyte in beverage samples. In this work, 3-(triethoxysilyl)-propylamine (TMSPA) was chosen as a precursor due to its ability to imprint the analyte by hydrogen bonding, Van der Walls, and dipole-dipole interactions. Nylon 6 was also added as a backbone and support for the precursor in which sol could greatly growth during the sol-gel process and makes the solution electrospinable. Various effective parameters in the extraction efficiency of the MIP-SPME tool such as loading time, flow rate, desorption time, selectivity, and the sample volume were evaluated. The linearity for the ACF in beverage sample was in the range of 0.78-100.5 ng mL(-1). Limit of detection (LOD) and quantification (LOQ) were 0.23 and 0.78 ng mL(-1) respectively. The RSD values (n=5) were all below 3.5%at the 20 ng mL(-1) level. Copyright © 2014 Elsevier B.V. All rights reserved.

  11. AZO Thin Films by Sol-Gel Process for Integrated Optics

    Directory of Open Access Journals (Sweden)

    Azzedine Boudrioua

    2013-07-01

    Full Text Available Undoped and aluminum-doped zinc oxide (AZO thin films are prepared by the sol-gel process. Zinc acetate dihydrate, ethanol, and monoethanolamine are used as precursor, solvent, and stabilizer, respectively. In the case of AZO, aluminum nitrate nonahydrate is added to the precursor solution with an atomic percentage equal to 1 and 2 at.% Al. The multi thin layers are deposited by spin-coating onto glass substrates, and are transformed into ZnO upon annealing at 550 °C. Films display a strong preferential orientation, with high values for the Texture Coefficients (TC of the (002 direction (TC(002 ≈ 3. The structural, morphological, and optical properties of the thin films as a function of aluminum content have been investigated using X-Ray Diffraction (XRD, Atomic Force Microscopy (AFM, and Scanning Electronic Microscopy (SEM. Waveguiding properties of the thin films have been also studied using m-lines spectroscopy. The results indicate that the films are monomodes at 632.8 nm with optical propagation optical losses estimated around 1.6 decibel per cm (dB/cm.

  12. Sol-Gel Process for Making Pt-Ru Fuel-Cell Catalysts

    Science.gov (United States)

    Narayanan, Sekharipuram; Valdez, Thomas; Kumta, Prashant; Kim, Y.

    2005-01-01

    A sol-gel process has been developed as a superior alternative to a prior process for making platinum-ruthenium alloy catalysts for electro-oxidation of methanol in fuel cells. The starting materials in the prior process are chloride salts of platinum and ruthenium. The process involves multiple steps, is time-consuming, and yields a Pt-Ru product that has relatively low specific surface area and contains some chloride residue. Low specific surface area translates to incomplete utilization of the catalytic activity that might otherwise be available, while chloride residue further reduces catalytic activity ("poisons" the catalyst). In contrast, the sol-gel process involves fewer steps and less time, does not leave chloride residue, and yields a product of greater specific area and, hence, greater catalytic activity. In this sol-gel process (see figure), the starting materials are platinum(II) acetylacetonate [Pt(C5H7O2)2, also denoted Pt-acac] and ruthenium(III) acetylacetonate [Ru(C5H7O2)3, also denoted Ru-acac]. First, Pt-acac and Ru-acac are dissolved in acetone at the desired concentrations (typically, 0.00338 moles of each salt per 100 mL of acetone) at a temperature of 50 C. A solution of 25 percent tetramethylammonium hydroxide [(CH3)4NOH, also denoted TMAH] in methanol is added to the Pt-acac/Ruacac/ acetone solution to act as a high-molecular-weight hydrolyzing agent. The addition of the TMAH counteracts the undesired tendency of Pt-acac and Ru-acac to precipitate as separate phases during the subsequent evaporation of the solvent, thereby helping to yield a desired homogeneous amorphous gel. The solution is stirred for 10 minutes, then the solvent is evaporated until the solution becomes viscous, eventually transforming into a gel. The viscous gel is dried in air at a temperature of 170 C for about 10 hours. The dried gel is crushed to make a powder that is the immediate precursor of the final catalytic product. The precursor powder is converted to the

  13. Development of novel Sol-Gel Indicators (SGI's) for in-situ environmental measurements: Part 1, Program and a new pH Sol-Gel Indicator

    International Nuclear Information System (INIS)

    Livingston, R.R.; Baylor, L.; Wicks, G.G.

    1992-01-01

    The feasibility of incorporating analytical indicators into a sol-gel glassy matrix and then coating substrates with this composite material has bee demonstrated. Substrates coated include paper, wood, glass, and the lens of an analytical probe. The first SRTC sol-gel indicator, comprising bromophenol blue dispersed in a silica matrix, was fabricated and successfully used to measure solution pH in the range of pH 3.0 to 7.5. material exhibited a quick response time, as measured by color changes both qualitatively and quantitatively, and the measuring device was reversible or reusable. Additional indicators with responses over other ranges as well as indicators sensitive to the presence of elements of interest, are also under development. The new SGI composites possess promising properties and an excellent potential for performing a variety important in-situ environmental measurements and area discussed in this report

  14. Analysis on the factors affecting the preparation of TIO2-ADUN composite sol by sol-gel method

    International Nuclear Information System (INIS)

    Wang Hui; Yin Rongcai; Liu Jinhong

    2010-01-01

    With C 2 H 2 O 5 and water as solvent and TBT as precursor and HNO 3 as the activator and valorize, the process for preparing TiO 2 -ADUN composite Sol method was studied. The influence of different reaction conditions on Sol-Gel time was analyzed in this study. The optimal reaction condition are: reaction temperature 20-25 degree C; pH value of reaction mixture 2-5; HNO 3 value of reaction mixture 0.3-0.5 ml; molar rations of alcohol to TBT 10, of water to TBT 2-3, respectively. A concentrated ADUN solution with Ti Sol , urea, water as additive is dispersed into uniform which are prepared by external mlii. (authors)

  15. Dependence of electrical and optical properties of sol-gel prepared undoped cadmium oxide thin films on annealing temperature

    International Nuclear Information System (INIS)

    Santos-Cruz, J.; Torres-Delgado, G.; Castanedo-Perez, R.; Jimenez-Sandoval, S.; Jimenez-Sandoval, O.; Zuniga-Romero, C.I.; Marquez Marin, J.; Zelaya-Angel, O.

    2005-01-01

    The effect of the annealing temperature (T a ) on the optical, electrical and structural properties of the undoped cadmium oxide (CdO) thin films obtained by the sol-gel method, using a simple precursor solution, was studied. All the CdO films annealed in the range from 200 to 450 deg. C are polycrystalline with (111) preferential orientation and present high optical transmission > 85% for wavelengths above 500 nm. The resistivity decreases as T a increases until it reaches a value of 6 x 10 -4 Ω cm for T a 350 deg. C. For higher temperatures the resistivity experiences a slight increase. Images obtained by atomic force microscopy show an evident incremental change of the aggregate size (clusters of grains) as T a increases. The grain size also increases when T a increases as observed in data calculated from X-ray measurements

  16. A copper ion-selective electrode with high selectivity prepared by sol-gel and coated wire techniques.

    Science.gov (United States)

    Mazloum Ardakani, M; Salavati-Niasari, M; Khayat Kashani, M; Ghoreishi, S M

    2004-03-01

    A sol-gel electrode and a coated wire ion-selective poly(vinyl chloride) membrane, based on thiosemicarbazone as a neutral carrier, were successfully developed for the detection of Cu (II) in aqueous solutions. The sol-gel electrode and coated electrode exhibited linear response with Nernstian slopes of 29.2 and 28.1 mV per decade respectively, within the copper ion concentration ranges 1.0 x 10(-5) - 1.0 x 10(-1) M and 6.0 x 10(-6) - 1.0 x 10(-1) M for coated and sol-gel sensors. The coated and sol-gel electrodes show detection limits of 3.0 x 10(-6) and 6.0 x 10(-6) M respectively. The electrodes exhibited good selectivities for a number of alkali, alkaline earth, transition and heavy metal ions. The proposed electrodes have response times ranging from 10-50 s to achieve a 95% steady potential for Cu2+ concentration. The electrodes are suitable for use in aqueous solutions over a wide pH range (4-7.5). Applications of these electrodes for the determination of copper in real samples, and as an indicator electrode for potentiometric titration of Cu2+ ion using EDTA, are reported. The lifetimes of the electrodes were tested over a period of six months to investigate their stability. No significant change in the performance of the sol-gel electrode was observed over this period, but after two months the coated wire copper-selective electrode exhibited a gradual decrease in the slope. The selectivity of the sol-gel electrode was found to be better than that of the coated wire copper-selective electrode. Based on these results, a novel sol-gel copper-selective electrode is proposed for the determination of copper, and applied to real sample assays.

  17. Sol-gel preparation of uranium oxide spheres

    International Nuclear Information System (INIS)

    Dolezal, J.; Urbanek, V.

    1978-01-01

    Information is presented on problems of preparing nuclear fuel by the sol-gel method. Basic data on different process types are given. A more detailed description of the method of preparation of spherical particles of uranium oxide gel developed and used at the Nuclear Research Institute at Rez is given. Advantages and disadvantages of sol-gel materials are discussed in comparison with fuel materials prepared by classical precipitation methods. The feasibility of the sol-gel methods for preparing other materials is shortly mentioned and their application outlined. (author)

  18. Iron specificity of a biosensor based on fluorescent pyoverdin immobilized in sol-gel glass

    Science.gov (United States)

    2011-01-01

    Two current technologies used in biosensor development are very promising: 1. The sol-gel process of making microporous glass at room temperature, and 2. Using a fluorescent compound that undergoes fluorescence quenching in response to a specific analyte. These technologies have been combined to produce an iron biosensor. To optimize the iron (II or III) specificity of an iron biosensor, pyoverdin (a fluorescent siderophore produced by Pseudomonas spp.) was immobilized in 3 formulations of porous sol-gel glass. The formulations, A, B, and C, varied in the amount of water added, resulting in respective R values (molar ratio of water:silicon) of 5.6, 8.2, and 10.8. Pyoverdin-doped sol-gel pellets were placed in a flow cell in a fluorometer and the fluorescence quenching was measured as pellets were exposed to 0.28 - 0.56 mM iron (II or III). After 10 minutes of exposure to iron, ferrous ion caused a small fluorescence quenching (89 - 97% of the initial fluorescence, over the range of iron tested) while ferric ion caused much greater quenching (65 - 88%). The most specific and linear response was observed for pyoverdin immobilized in sol-gel C. In contrast, a solution of pyoverdin (3.0 μM) exposed to iron (II or III) for 10 minutes showed an increase in fluorescence (101 - 114%) at low ferrous concentrations (0.45 - 2.18 μM) while exposure to all ferric ion concentrations (0.45 - 3.03 μM) caused quenching. In summary, the iron specificity of pyoverdin was improved by immobilizing it in sol-gel glass C. PMID:21554740

  19. Porphyrinosilica and metalloporphyrinosilica: hybrid organic-inorganic materials prepared by sol-gel processing

    Science.gov (United States)

    Iamamoto; Sacco; Biazzotto; Ciuffi; Serra

    2000-01-01

    New materials porphyrinosilica and metalloporphyrinosilica template have been obtained by a sol-gel processing where functionalyzed porphyrins and metalloporphyrins "building blocks" were assembled into a three-dimensional silicate network. The optimized conditions for preparation of these materials are revised. The monomer precursors porphyrinopropylsilyl and metalloporphyrinopropylsilyl preparation reactions and subsequent one pot sol-gel processing with tetraethoxysilane are discussed. In the case of metalloporphyrins the nitrogen base coordinates to the central metal and acts as a template in the molecular imprinting technique. UV-visible absorption spectroscopy, thermogravimetric analysis, electron paramagnetic resonance, nuclear magnetic spectra, infrared spectra, luminescence spectra, surface area and electron spectroscopy imaging of the materials are used to characterize the prepared materials. The catalytic activities of these metalloporphyrinosilica-template are compared.

  20. Porphyrinosilica and metalloporphyrinosilica: hybrid organic-inorganic materials prepared by sol-gel processing

    Directory of Open Access Journals (Sweden)

    YASSUKO IAMAMOTO

    2000-03-01

    Full Text Available New materials porphyrinosilica and metalloporphyrinosilica template have been obtained by a sol-gel processing where functionalyzed porphyrins and metalloporphyrins "building blocks" were assembled into a three-dimensional silicate network. The optimized conditions for preparation of these materials are revised. The monomer precursors porphyrinopropylsilyl and metalloporphyrinopropylsilyl preparation reactions and subsequent one pot sol-gel processing with tetraethoxysilane are discussed. In the case of metalloporphyrins the nitrogen base coordinates to the central metal and acts as a template in the molecular imprinting technique. UV-visible absorption spectroscopy, thermogravimetric analysis, electron paramagnetic resonance, nuclear magnetic spectra, infrared spectra, luminescence spectra, surface area and electron spectroscopy imaging of the materials are used to characterize the prepared materials. The catalytic activities of these metalloporphyrinosilica- template are compared.

  1. Effect of reaction solvent on hydroxyapatite synthesis in sol-gel process

    Science.gov (United States)

    Nazeer, Muhammad Anwaar; Yilgor, Emel; Yagci, Mustafa Baris; Unal, Ugur; Yilgor, Iskender

    2017-12-01

    Synthesis of hydroxyapatite (HA) through sol-gel process in different solvent systems is reported. Calcium nitrate tetrahydrate (CNTH) and diammonium hydrogen phosphate (DAHP) were used as calcium and phosphorus precursors, respectively. Three different synthesis reactions were carried out by changing the solvent media, while keeping all other process parameters constant. A measure of 0.5 M aqueous DAHP solution was used in all reactions while CNTH was dissolved in distilled water, tetrahydrofuran (THF) and N,N-dimethylformamide (DMF) at a concentration of 0.5 M. Ammonia solution (28-30%) was used to maintain the pH of the reaction mixtures in the 10-12 range. All reactions were carried out at 40 ± 2°C for 4 h. Upon completion of the reactions, products were filtered, washed and calcined at 500°C for 2 h. It was clearly demonstrated through various techniques that the dielectric constant and polarity of the solvent mixture strongly influence the chemical structure and morphological properties of calcium phosphate synthesized. Water-based reaction medium, with highest dielectric constant, mainly produced β-calcium pyrophosphate (β-CPF) with a minor amount of HA. DMF/water system yielded HA as the major phase with a very minor amount of β-CPF. THF/water solvent system with the lowest dielectric constant resulted in the formation of pure HA.

  2. Dip coating of sol-gels

    Science.gov (United States)

    Schunk, P. R.; Hurd, A. J.; Brinker, C. J.

    Dip coating is the primary means of depositing sol-gel films for precision optical coatings. Sols are typically multicomponent systems consisting of an inorganic phase dispersed in a solvent mixture, with each component differing in volatility and surface tension. This, together with slow coating speeds (less than 1cm/s), makes analysis of the coating process complicated; unlike most high-speed coating methods, solvent evaporation, evolving rheology, and surface tension gradients alter significantly the fluid mechanics of the deposition stage. These phenomena were studied with computer-aided predictions of the flow and species transport fields. The underlying theory involves mass, momentum, and species transport on a domain of unknown shape, with models and constitutive equations for vapor-liquid equilibria and surface tension. Due accounting is made for the unknown position of the free surface, which locates according to the capillary hydrodynamic forces and solvent loss by evaporation. Predictions of the effects of mass transfer, hydrodynamics, and surface tension gradients on final film thickness are compared with ellipsometry measurements of film thickness on a laboratory pilot coater. Although quantitative agreement is still lacking, both experiment and theory reveal that the film profile near the drying line takes on a parabolic shape.

  3. Electrophoretic Porosimetry of Sol-Gels

    Science.gov (United States)

    Snow, L. A.; Smith, D. D.; Sibille, L.; Hunt, A. J.; Ng, J.; Rose, M. Franklin (Technical Monitor)

    2000-01-01

    It has been hypothesized that gravity has an effect on the formation and resulting microstructure of sol-gels. In order to more clearly resolve the effect of gravity, pores may be non-destructively analyzed in the wet gel, circumventing the shrinkage and coarsening associated with the drying procedure. We discuss the development of an electrophoretic technique, analogous to affinity chromatography, for the determination of pore size distribution and its application to silica gels. Specifically a monodisperse charged dye is monitored by an optical densitometer as it moves through the wet gel under the influence of an electric field. The transmittance data (output) represents the convolution of the dye concentration profile at the beginning of the run (input) with the pore size distribution (transfer function), i.e. linear systems theory applies. Because of the practical difficulty in producing a delta function input dye profile we prefer instead to use a step function. Average pore size is then related to the velocity of this dye front, while the pore size distribution is related to the spreading of the front. Preliminary results of this electrophoretic porosimetry and its application to ground and space-grown samples will be discussed.

  4. Sol-gel optical coatings for lasers: Part 1

    International Nuclear Information System (INIS)

    Floch, H.G.; Belleville, P.F.; Priotton, J.J.

    1995-01-01

    Many manufacturers and users claim that optical coatings are best prepared by physical vapor deposition technology. Others believe that sol-gel technology is an effective and competitive alternative. This article, the first of three, emphasizes sol-gel thin-film history and relates it to high-power laser technology, chemistry of the sol-gel process, production of optical coatings and deposition techniques. The second and third articles describe the preparation and performance of antireflective and highly reflective sol-gel optical coatings, respectively, that have been developed for the 1.8-MJ/500-TW (351-nm) pulsed neodymium-glass laser. This powerful laser is to be used in France's Inertial Confinement Fusion (ICF) program. It will demonstrate, at the laboratory scale, ignition of deuterium-tritium fusion fuel

  5. Safe and Environmentally Acceptable Sol-Gel-Derived Pyrophoric Pyrotechnics

    National Research Council Canada - National Science Library

    Simpson, Randall L; Hubble, William; Stevenson, Bradley; Gash, Alexander; Satcher, Joe; Metcalf, Patricia

    2004-01-01

    ...% H2 in Ar, N2, CO2, or CO) at intermediate temperatures (350 C to 700 C). All of the resulting sol-gel-derived metallic iron powders were ignitable by thermal methods, however none were pyrophoric...

  6. Safe and Environmentally Acceptable Sol-Gel-Derived Pyrophoric Pyrotechnics

    National Research Council Canada - National Science Library

    Simpson, Randall L; Hubble, William; Stevenson, Bradley; Gash, Alexander; Satcher, Joe; Metcalf, Patricia

    2004-01-01

    It was demonstrated that highly porous sol-gel derived iron (III) oxide materials could be reduced to sub-micron-sized metallic iron by heating the materials to intermediate temperatures in a hydrogen atmosphere...

  7. Sol-Gel Derived, Nanostructured Oxide Lubricant Coatings

    National Research Council Canada - National Science Library

    Taylor, Douglas

    2000-01-01

    In this program, we deposited oxide coatings of titanium and nickel by wet-chemical deposition methods, also referred to as sol-gel, which showed excellent tribological properties in previous investigations...

  8. Sol-gel materials for optofluidics - process and applications

    DEFF Research Database (Denmark)

    Mikkelsen, Morten Bo Lindholm

    2011-01-01

    This Ph.D. thesis is concerned with the use of sol-gel materials in optofluidic applications and the physics of DNA molecules in nanoconfinement. The bottom-up formation of solid material, which is provided by the sol-gel process, enables control of the chemical composition and porosity...... of the material. At early stages of gelation, thin gel coatings can be structured by nanoimprint lithography, and purely inorganic silica materials can be obtained by subsequent thermal annealing. The sol-gel process thus constitutes a unique method for nanofabrication of silica materials of special properties....... In this work, sol-gel silica is introduced as a new material class for the fabrication of lab-on-a-chip devices for DNA analysis. An imprint process with a rigid, non-permeable stamp was developed, which enabled fabrication of micro- and nanofluidic silica channels in a single process step without use of any...

  9. Controlled Sol-Gel Transitions of a Thermoresponsive Polymer in a Photoswitchable Azobenzene Ionic Liquid as a Molecular Trigger.

    Science.gov (United States)

    Wang, Caihong; Hashimoto, Kei; Tamate, Ryota; Kokubo, Hisashi; Watanabe, Masayoshi

    2018-01-02

    Producing ionic liquids (ILs) that function as molecular trigger for macroscopic change is a challenging issue. Photoisomerization of an azobenzene IL at the molecular level evokes a macroscopic response (light-controlled mechanical sol-gel transitions) for ABA triblock copolymer solutions. The A endblocks, poly(2-phenylethyl methacrylate), show a lower critical solution temperature in the IL mixture containing azobenzene, while the B midblock, poly(methyl methacrylate), is compatible with the mixture. In a concentrated polymer solution, different gelation temperatures were observed in it under dark and UV conditions. Light-controlled sol-gel transitions were achieved by a photoresponsive solubility change of the A endblocks upon photoisomerization of the azobenzene IL. Therefore, an azobenzene IL as a molecular switch can tune the self-assembly of a thermoresponsive polymer, leading to macroscopic light-controlled sol-gel transitions. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  10. Microcontroller based instrumentation for the fuel pin preparation facility by sol-gel method

    International Nuclear Information System (INIS)

    Suhasini, B.; Prabhakar Rao, J.; Srinivas, K.C.

    2009-01-01

    The fuel pin preparation facility by Sol-Gel route has been set up at Chemistry Group at Indira Gandhi Centre for Atomic Research, Kalpakkam. Sol-Gel, a solution-gelation process involves conversion of solutions of nitrates of uranium-plutonium (at 0 deg C) into gel microspheres. To measure the exact quantities of the above solutions and to ensure their temperatures, a variety of sensors have been used at various stages in the plant. To monitor and acquire the data of process parameters used in the production and for an automated operation of the plant, a PC (master)-microcontroller (slave) based instrumentation has been developed along with acquisition software and a GU interface developed in Visual Basic. (author)

  11. Sol-gel-based biosensing applied to medicinal science.

    Science.gov (United States)

    Moreira, Felismina T C; Moreira-Tavares, Ana P; Sales, M Goreti F

    2015-01-01

    Biosensors have opened new horizons in biomedical analysis, by ensuring increased assay speed and flexibility, and allowing point-of-care applications, multi-target analyses, automation and reduced costs of testing. This has been a result of many studies merging nanotechnology with biochemistry over the years, thereby enabling the creation of more suitable environments to biological receptors and their substitution by synthetic analogue materials. Sol-gel chemistry, among other materials, is deeply involved in this process. Sol-gel processing allows the immobilization of organic molecules, biomacromolecules and cells maintaining their properties and activities, permitting their integration into different transduction devices, of electrochemical or optical nature, for single or multiple analyses. Sol-gel also allows to the production of synthetic materials mimicking the activity of natural receptors, while bringing advantages, mostly in terms of cost and stability. Moreover, the biocompatibility of sol-gel materials structures of biological nature allowed the use of these materials in emerging in vivo applications. In this chapter, biosensors for biomedical applications based on sol-gel derived composites are presented, compared and described, along with current emerging applications in vivo, concerning drug delivery or biomaterials. Sol-gel materials are shown as a promising tool for current, emerging and future medical applications.

  12. Preparation of silica by sol-gel method using formamide

    Directory of Open Access Journals (Sweden)

    R.F.S. Lenza

    2001-07-01

    Full Text Available In this work we obtained microporous and mesoporous silica gels by sol-gel processing. Tetraethylortosilicate (TEOS was used as precursor. Nitric acid and hydrofluoric acid were used as catalysts. In order to study the affect of formamide as drying additive, we used a molar ratio alkoxide/formamide of 1/1. The performance of formamide in obtaining crack-free gels was evaluated through monolithicity measurements. The structural evolution occurring in the interconnected network of the gels during thermal treatment was monitored by Fourier transform infrared spectroscopy (FTIR, shrinkage and density measurements and nitrogen gas sorption. We noted that in the presence of formamide, the Si-O-Si bonds are stronger and belong to a more cross-linked structure. The samples obtained in the presence of formamide have larger pore volume and its pore structure is in the range of mesoporosity. The samples obtained without additive are microporous. Formamide allowed the preparation of crack-free silica gels stabilized at high temperatures.

  13. Mullite fibres preparation by aqueous sol-gel process and activation energy of mullitization

    International Nuclear Information System (INIS)

    Tan Hongbin; Ding Yaping; Yang Jianfeng

    2010-01-01

    Mullite fibres were prepared by sol-gel process using aluminum carboxylates (ACs) and silica sol. ACs was synthesized from dissolving aluminum powder in a mixture of formic acid and oxalic acid using aluminum chloride hexahydrate as catalyst. A molar ratio of 1:2:1 for aluminum, formic acid and oxalic acid was optimized to obtain clear solution and viscous ACs sol for fibres synthesis. Thermogravimetry-differential scanning calorimetry (TG-DSC), Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD), and scanning electron microscopy (SEM) analysis were used to characterize the properties of the gel and ceramic fibres. The gel fibres completely transformed to mullite at 1200 o C, with a smooth surface and uniform diameter. The activation energy for mullite formation in precursor gel fibres was determined by means of differential thermal analysis. The value obtained, E a = 741.4 kJ/mol, was lower than most data reported in the literatures, which was attributed to the silica-alumina micro-phase separation when organic acids decomposed during gel fibres heating.

  14. Phase study of titanium dioxide nanoparticle prepared via sol-gel process

    Science.gov (United States)

    Oladeji Araoyinbo, Alaba; Bakri Abdullah, Mohd Mustafa Al; Salleh, Mohd Arif Anuar Mohd; Aziz, Nurul Nadia Abdul; Iskandar Azmi, Azwan

    2018-03-01

    In this study, titanium dioxide nanoparticles have been prepared via sol-gel process using titanium tetraisopropoxide as a precursor with hydrochloric acid as a catalyst, and ethanol with deionized water as solvents. The value of pH used is set to 3, 7 and 8. The sols obtained were dried at 100 °C for 1 hr and calcined at 350, 550, and 750 °C for 3 hrs to observe the phase transformation of titanium dioxide nanoparticle. The samples were characterized by x-ray diffraction and field emission scanning electron microscope. The morphology analysis is obtained from field emission scanning electron microscope. The phase transformation was investigated by x-ray diffraction. It was found that the pH of the solution affect the agglomeration of titanium dioxide particle. The x-ray diffraction pattern of titanium dioxide shows the anatase phase most abundant at temperature of 350 °C. At temperature of 550 °C the anatase and rutile phase were present. At temperature of 750 °C the rutile phase was the most abundant for pH 3, 7 and 8. It was confirmed that at higher temperature the rutile phase which is the stable phase are mostly present.

  15. Structural development and kinetic analysis of PbTiO3 powders processed at low-temperature via new sol-gel approach

    Science.gov (United States)

    Bel-Hadj-Tahar, Radhouane; Abboud, Mohamed

    2018-04-01

    The synthesis of crystalline lead titanate powder by a generic low-temperature sol-gel approach is developed. Acetoin was added as ligand, instead of the commonly used alkanolamines, to ensure total dissolution of the precursor compounds. The feasibility of the acetoin-Ti isopropoxide complex as a new precursor of PbTiO3 perovskite particles via sol-gel method has been demonstrated. No excess lead has been introduced. Nanometric PbTiO3 crystallites have been formed at 400 °C under atmospheric pressure from titanium isopropoxide and lead acetate in alcoholic solution by remarkably low activation energy of crystallization process of 90 kJ mol-1. The powders show tetragonal lattice and dendritic morphology. In addition to the effect of heat-treatment temperature, time, and atmosphere, the sol chemistry particularly influenced the phase composition, particle size, and particle morphology. The use of different ligands significantly modified powder morphology. The extent of the crystallization was quantitatively evaluated by differential thermal analysis and analyzed by Johnson-Mehl-Avrami approach. The crystallization followed two rate regimes depending on the interval of the crystallized fraction.

  16. Photocatalytic Graphene-TiO2 Thin Films Fabricated by Low-Temperature Ultrasonic Vibration-Assisted Spin and Spray Coating in a Sol-Gel Process

    Directory of Open Access Journals (Sweden)

    Fatemeh Zabihi

    2017-05-01

    Full Text Available In this work, we communicate a facile and low temperature synthesis process for the fabrication of graphene-TiO2 photocatalytic composite thin films. A sol-gel chemical route is used to synthesize TiO2 from the precursor solutions and spin and spray coating are used to deposit the films. Excitation of the wet films during the casting process by ultrasonic vibration favorably influences both the sol-gel route and the deposition process, through the following mechanisms. The ultrasound energy imparted to the wet film breaks down the physical bonds of the gel phase. As a result, only a low-temperature post annealing process is required to eliminate the residues to complete the conversion of precursors to TiO2. In addition, ultrasonic vibration creates a nanoscale agitating motion or microstreaming in the liquid film that facilitates mixing of TiO2 and graphene nanosheets. The films made based on the above-mentioned ultrasonic vibration-assisted method and annealed at 150 °C contain both rutile and anatase phases of TiO2, which is the most favorable configuration for photocatalytic applications. The photoinduced and photocatalytic experiments demonstrate effective photocurrent generation and elimination of pollutants by graphene-TiO2 composite thin films fabricated via scalable spray coating and mild temperature processing, the results of which are comparable with those made using lab-scale and energy-intensive processes.

  17. Sol - gel inorganic ion exchangers for conditioning of medium level radioactive waste

    International Nuclear Information System (INIS)

    Arcangeli, G.; Traverso, D.M.; Gerontopoulos, P.; Fava, R.

    1988-01-01

    Decontamination of high-level liquid wastes and medium activity wastes streams by inorganic ion exchange combined with the conversion of the spent inorganic ion exchange material to waste ceramics presents a considerable potential for utilisation in waste conditioning. Ceramic waste forms are found superior to other candidate waste immobilisation forms but practical implementation is hampered because of the complexity of the related fabrication technology. This report shows the possibility of improving this situation by resorting to sol gel techniques earlier developed for preparation of nuclear fuel ceramics. The principal findings are: - superior quality ion exchange xerogel titanates in the form of mechanically resistant, size controlled microspheres can be prepared using a simple sol-gel technique; - the titanate particles can be also used as precursors in Evaporative Deposition on Xerogel Particles (EDXP) a new waste solidification process based on physical impregnation of the xerogel material with the waste liquid followed by evaporation; - waste loaded ion exchange microspheres can be converted to leach resistant ceramics by firing and/or cold pressing and sintering at 900 0 -1100 0 C; - sol-gel inorganic ion exchange and EDXP may find useful application in conditioning MAW streams. 44 figs., 43 refs

  18. Surface modification of quartz fibres for dental composites through a sol-gel process.

    Science.gov (United States)

    Wang, Yazi; Wang, Renlin; Habib, Eric; Wang, Ruili; Zhang, Qinghong; Sun, Bin; Zhu, Meifang

    2017-05-01

    In this study, quartz fibres (QFs) surface modification using a sol-gel method was proposed and dental posts reinforced with modified QFs were produced. A silica sol (SS) was prepared using tetraethoxysilane (TEOS) and 3-methacryloxypropyltrimethoxysilane (γ-MPS) as precursors. The amount of γ-MPS in the sol-gel system was varied from 0 to 24wt.% with a constant molar ratio of TEOS, ethanol, deionized water, and HCl. Thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FT-IR), and contact angle (CA) measurements were used to characterize the modified QFs, which confirmed that SS had successfully coated the surface of QFs. SEM images showed good interfacial bonding between the modified QFs and the resin matrix. The results of three-point bending tests of the fibre reinforced composite (FRC) posts showed that the QFs modified by SS with 12wt.% γ-MPS presented the best mechanical properties, demonstrating improvements of 108.3% and 89.6% for the flexural strength and flexural modulus, respectively, compared with untreated QFs. Furthermore, the sorption and solubility of the prepared dental posts were also studied by immersing the posts in artificial saliva (AS) for 4weeks, and yielded favourable results. This sol-gel surface modification method promises to resolve interfacial bonding issues of fibres with the resin matrix, and produce FRC posts with excellent properties. Copyright © 2017. Published by Elsevier B.V.

  19. Biological influence of Ca/P ratio on calcium phosphate coatings by sol-gel processing.

    Science.gov (United States)

    Catauro, M; Papale, F; Sapio, L; Naviglio, S

    2016-08-01

    The objective of this work has been to develop low temperature sol-gel glass coatings to modify the substrate surface and to evaluate their bioactivity and biocompatibility. Glasses, based on SiO2·CaO·P2O5, were synthesized by the sol-gel technique using tetraethyl orthosilicate, calcium nitrate tetrahydrate and triethyl phosphate as precursors of SiO2, CaO and P2O5, respectively. Those materials, still in the sol phase, have been used to coat substrates by means of the dip-coating technique. Attenuated total reflectance Fourier transform infrared (ATR-FTIR) has been used for characterize coatings and a microstructural analysis has been obtained using scanning electron microscopy (SEM). The potential applications of the coatings in the biomedical field were evaluated by bioactivity and biocompatibility tests. The coated substrate was immersed in simulated body fluid (SBF) for 21days and the hydroxyapatite deposition on its surface was subsequently evaluated via SEM-EDXS analysis, as an index of bone-bonding capability. In order to study the cell behavior and response to our silica based materials, prepared via the sol-gel method, with various Ca/P ratio and coating substrate, we have used the human osteoblast-like U2OS cell line. Copyright © 2016 Elsevier B.V. All rights reserved.

  20. Determination of Insulator-to-Semiconductor Transition in Sol-Gel Oxide Semiconductors Using Derivative Spectroscopy.

    Science.gov (United States)

    Lee, Woobin; Choi, Seungbeom; Kim, Kyung Tae; Kang, Jingu; Park, Sung Kyu; Kim, Yong-Hoon

    2015-12-23

    We report a derivative spectroscopic method for determining insulator-to-semiconductor transition during sol-gel metal-oxide semiconductor formation. When an as-spun sol-gel precursor film is photochemically activated and changes to semiconducting state, the light absorption characteristics of the metal-oxide film is considerable changed particularly in the ultraviolet region. As a result, a peak is generated in the first-order derivatives of light absorption ( A' ) vs. wavelength (λ) plots, and by tracing the peak center shift and peak intensity, transition from insulating-to-semiconducting state of the film can be monitored. The peak generation and peak center shift are described based on photon-energy-dependent absorption coefficient of metal-oxide films. We discuss detailed analysis method for metal-oxide semiconductor films and its application in thin-film transistor fabrication. We believe this derivative spectroscopy based determination can be beneficial for a non-destructive and a rapid monitoring of the insulator-to-semiconductor transition in sol-gel oxide semiconductor formation.

  1. Hybrid titanium dioxide/PS-b-PEO block copolymer nanocomposites based on sol-gel synthesis

    International Nuclear Information System (INIS)

    Gutierrez, J; Tercjak, A; Garcia, I; Peponi, L; Mondragon, I

    2008-01-01

    The poly(styrene)-b-poly(ethylene oxide) (SEO) amphiphilic block copolymer, with two different molecular weights, has been used as a structure directing agent for generating nanocomposites of TiO 2 /SEO via the sol-gel process. SEO amphiphilic block copolymers are designed with a hydrophilic PEO-block which can interact with inorganic molecules, as well as a hydrophobic PS-block which builds the matrix. The addition of different amounts of sol-gel provokes strong variations in the self-assembled morphology of TiO 2 /SEO nanocomposites with respect to the neat block copolymer. As confirmed by atomic force microscopy (AFM), TiO 2 /PEO-block micelles get closer, forming well-ordered spherical domains, in which TiO 2 nanoparticles constitute the core surrounded by a corona of PEO-blocks. Moreover, for 20 vol% sol-gel the generated morphology changes to a hexagonally ordered structure for both block copolymers. The cylindrical structure of these nanocomposites has been confirmed by the two-dimensional Fourier transform power spectrum of the corresponding AFM height images. Affinity between titanium dioxide precursor and PEO-block of SEO allows us to generate hybrid inorganic/organic nanocomposites, which retain the optical properties of TiO 2 , as evaluated by UV-vis spectroscopy

  2. Biological influence of Ca/P ratio on calcium phosphate coatings by sol-gel processing

    Energy Technology Data Exchange (ETDEWEB)

    Catauro, M., E-mail: michelina.catauro@unina2.it [Department of Industrial and Information Engineering, Second University of Naples, Via Roma 29 (Italy); Papale, F. [Department of Industrial and Information Engineering, Second University of Naples, Via Roma 29 (Italy); Sapio, L.; Naviglio, S. [Department of Biochemistry, Biophysics and General Pathology, Second University of Naples, Via L. De Crecchio 7, 80138 Naples (Italy)

    2016-08-01

    The objective of this work has been to develop low temperature sol-gel glass coatings to modify the substrate surface and to evaluate their bioactivity and biocompatibility. Glasses, based on SiO{sub 2}·CaO·P{sub 2}O{sub 5}, were synthesized by the sol-gel technique using tetraethyl orthosilicate, calcium nitrate tetrahydrate and triethyl phosphate as precursors of SiO{sub 2}, CaO and P{sub 2}O{sub 5}, respectively. Those materials, still in the sol phase, have been used to coat substrates by means of the dip-coating technique. Attenuated total reflectance Fourier transform infrared (ATR-FTIR) has been used for characterize coatings and a microstructural analysis has been obtained using scanning electron microscopy (SEM). The potential applications of the coatings in the biomedical field were evaluated by bioactivity and biocompatibility tests. The coated substrate was immersed in simulated body fluid (SBF) for 21 days and the hydroxyapatite deposition on its surface was subsequently evaluated via SEM-EDXS analysis, as an index of bone-bonding capability. In order to study the cell behavior and response to our silica based materials, prepared via the sol-gel method, with various Ca/P ratio and coating substrate, we have used the human osteoblast-like U2OS cell line. - Highlights: • Coatings consisting of SiO{sub 2}·CaO·P{sub 2}O{sub 5} glasses were prepared via sol-gel dip coating. • Ca/P molar ratio affects the film morphology and biocompatibility. • Higher cell proliferation was found in response to higher Ca/P ratios coatings. • A growth cell proliferation inhibition was observed in response to lower Ca/P ratio.

  3. Mesoscopic objects, porous layers and nanocomposites-Possibilities of sol-gel chemistry

    International Nuclear Information System (INIS)

    Piwonski, Ireneusz

    2009-01-01

    The goal of this study was to prepare mesoscopic objects, thin porous films and nanocomposite coatings with the use of sol-gel technique. Silica nanotubes, titania nanoparticles, porous titania and zirconia coatings as well as titania nanocomposites were successfully synthesized by changing the type of sol-gel precursor, sol composition and applying dip-coating deposition procedure in order to obtain thin films or coatings. All materials were visualized and characterized by the Atomic Force Microcscopy (AFM) technique. Moreover, characterization of titania nanocomposites was extended to the tribological tests performed by means of microtribometer operating in normal loads range of 30-100 mN. The AFM analysis of mesoscopic objects and nanoparticles showed that the diameter of synthesized silica nanotubes was 60-70 nm and the size of titania nanoparticles was 43 nm. In case of porous layers the pore size in titania and zirconia coatings oscillated between 100 and 240 nm, however their shape and distribution were irregular. Microtribological studies of nanocomposites revealed the moderate decrease of the coefficient of friction for samples containing 5, 15 and 5 wt.% of zirconia nanoparticles in titania coatings annealed at 100, 500 and 1000 deg. C respectively. An enhancement of antiwear properties was already observed for 1 wt.% of nanophase content, except the sample annealed at 500 deg. C. It was also found that the annealing at high temperatures is a primary factor which affects the reduction of friction and wear of titania coatings while the presence of nanoparticles has secondary effect. Investigations in this study carried out with the use of the AFM technique highlighted the potential and flexibility of sol-gel approach in designing of various types of advanced materials in a form of mesoscopic objects, porous coatings and composite layers. Results collected in this study clearly demonstrated that sol-gel technique can be applied effectively in preparation of

  4. Effect of sintering time at low temperature on the properties of IGZO TFTs fabricated by using the sol-gel process

    International Nuclear Information System (INIS)

    Choi, Jun Hyuk; Shim, Jong Hyun; Hwang, Soo Min

    2010-01-01

    We explored the application of the sol-gel process technique to the fabrication of InGaZnO (IGZO) thin film transistors (TFTs). We fabricated IGZO TFTs by using the sol-gel method and evaluated the effect of the sintering time on the electrical properties of the IGZO system with an atomic ratio of In:Ga:Zn = 2:1:1. In the process, IGZO precursor solutions were prepared by mixing In nitrate, Ga nitrate, and Zn acetate and were then deposited on a p-type Si-wafer covered with a thermally grown SiO 2 layer by spin-coating. The sintering process was performed for 3 h, 6 h or 12 h at 300 .deg. C in the ambient atmosphere. The source/drain electrodes of the TFT devices were fabricated using Al thermal evaporation. For all of the samples, a low off current (∼10 -1 1 A) and on-to-off current ratio (∼ 5 x 10 4 ) were obtained in their transfer curves. The saturation mobility increased with increasing sintering time: for the samples sintered for 3 h, 6 h and 12 h, the saturation mobilities were calculated to be 0.825 cm 2 /Vs, 1.65 cm 2 /Vs, and 2.06 cm 2 /Vs, respectively. Based on the XPS and TEM analyses, the enhancement of the mobility was attributed to the increase in the number of oxygen vacancies and the nanocrystalline structure in the amorphous matrix with increasing sintering time. These results demonstrate for the potential application of sol-gel processed IGZO devices on flexible polymer substrates.

  5. Preparation of nanospinels NiMn{sub x}Fe{sub 2-x}O{sub 4} using sol-gel method and their applications on removal of azo dye from aqueous solutions

    Energy Technology Data Exchange (ETDEWEB)

    Khosravi, Iman [Department of Chemistry, Faculty of Sciences, Ferdowsi University of Mashhad, Mashhad 917791436 (Iran, Islamic Republic of); Yazdanbakhsh, Mohammad, E-mail: myazdan@um.ac.ir [Department of Chemistry, Faculty of Sciences, Ferdowsi University of Mashhad, Mashhad 917791436 (Iran, Islamic Republic of); Goharshadi, Elaheh K. [Department of Chemistry, Faculty of Sciences, Ferdowsi University of Mashhad, Mashhad 917791436 (Iran, Islamic Republic of); Center of Nano Research, Ferdowsi University of Mashhad, Mashhad 91799 (Iran, Islamic Republic of); Youssefi, Abbas [Par -e- Tavous Research Institute, Mashhad 91000 (Iran, Islamic Republic of)

    2011-11-01

    Highlights: {yields} The nanospinels, NiMn{sub x}Fe{sub 2-x}O{sub 4} (x = 0.05, 0.1, 0.3, 0.5, 0.7, and 1), prepared by Sol-gel method. {yields} The nanospinels prepared, have been used for removal of approximately 90% of reactive blue 5 within 1 min. {yields} The degradation of RB5 dye, follows merely an adsorption process. - Abstract: In this paper, nanospinels NiMn{sub x}Fe{sub 2-x}O{sub 4} (x = 0.05, 0.1, 0.3, 0.5, 0.7, and 1) were prepared by sol-gel method in the presence of nitrate-metal-ethylene glycol (EG) polymerized complex. The nanospinels were characterized using thermogravimetry analysis (TGA), X-ray powder diffraction (XRD), Fourier infrared spectroscopy (FTIR), and transmission electron microscope (TEM). The adsorption of an azo dye, reactive blue 5 (RB5), from water was determined using the prepared nanospinels. The effect of operational parameters such as the initial dye concentration, the concentration of nanospinels, temperature, and pH on the degradation of dye was investigated. The adsorption process follows second-order kinetics and Arrhenius behavior. Two common models, the Langmuir and Freundlich isotherms were used to investigate the interaction of dye and nanospinels. The isotherm evaluations revealed that the Freundlich model provides better fit to the experimental data than that of the Langmuir model. The photocatalytic degradation of RB5 at pH 1 under UV irradiation was examined. The results showed that the degradation of RB5 dye follows merely an adsorption process.

  6. Slow Release of Plant Volatiles Using Sol-Gel Dispensers.

    Science.gov (United States)

    Bian, L; Sun, X L; Cai, X M; Chen, Z M

    2014-12-01

    The black citrus aphid, also known as the tea aphid, (Toxoptera aurantii Boyer) attacks economically important crops, including tea (Camellia sinensis (L.) O. Kuntze). In the current study, silica sol-gel formulations were screened to find one that could carry and release C. sinensis plant volatiles to lure black citrus aphids in a greenhouse. The common plant volatile trans-2-hexen-1-al was used as a model molecule to screen for suitable sol-gel formulations. A zNose (Electronic Sensor Technology, Newbury Park, CA) transportable gas chromatograph was used to continuously monitor the volatile emissions. A sol-gel formulation containing tetramethyl orthosilicate and methyltrimethoxysilane in an 8:2 (vol:vol) ratio was selected to develop a slow-release dispenser. The half-life of trans-2-hexen-1-al in the sol-gel dispenser increased slightly with the volume of this compound in the dispenser. Ten different volatiles were tested in the sol-gel dispenser. Alcohols of 6-10 carbons had the longest half-lives (3.01-3.77 d), while esters of 6-12 carbons had the shortest (1.53-2.28 d). Release of these volatiles from the dispensers could not be detected by the zNose after 16 d (cis-3-hexenyl acetate) to 26 d (3,7-dimethylocta-1,6-dien-3-ol). In greenhouse experiments, trans-2-hexen-1-al and cis-3-hexen-1-ol released from the sol-gel dispensers attracted aphids for ≍17 d, and release of these volatiles could not be detected by the zNose after ≍24 d. The sol-gel dispensers performed adequately for the slow release of plant volatiles to trap aphids in the greenhouse. © 2014 Entomological Society of America.

  7. Microstructure investigation on micropore formation in microporous silica materials prepared via a catalytic sol-gel process by small angle X-ray scattering.

    Science.gov (United States)

    Shimizu, Wataru; Hokka, Junsuke; Sato, Takaaki; Usami, Hisanao; Murakami, Yasushi

    2011-08-04

    The so-called sol-gel technique has been shown to be a template-free, efficient way to create functional porous silica materials having uniform micropores. This appears to be closely linked with a postulation that the formation of weakly branched polymer-like aggregates in a precursor solution is a key to the uniform micropore generation. However, how such a polymer-like structure can precisely be controlled, and further, how the generated low-fractal dimension solution structure is imprinted on the solid silica materials still remain elusive. Here we present fabrication of microporous silica from tetramethyl orthosilicate (TMOS) using a recently developed catalytic sol-gel process based on a nonionic hydroxyacetone (HA) catalyst. Small angle X-ray scattering (SAXS), nitrogen adsorption porosimetry, and transmission electron microscope (TEM) allowed us to observe the whole structural evolution, ranging from polymer-like aggregates in the precursor solution to agglomeration with heat treatment and microporous morphology of silica powders after drying and hydrolysis. Using the HA catalyst with short chain monohydric alcohols (methanol or ethanol) in the precursor solution, polymer-like aggregates having microscopic correlation length (or mesh-size) micropores with diameters 2 nm) in the solid product due to apertures between the particle-like aggregates. The data demonstrate that the extremely fine porous silica architecture comes essentially from a gaussian polymer-like nature of the silica aggregates in the precursor having the microscopic mesh-size and their successful imprint on the solid product. The result offers a general but significantly efficient route to creating precisely designed fine porous silica materials under mild condition that serve as low refractive index and efficient thermal insulation materials in their practical applications.

  8. Optical ph sensing material prepared from doped sol-gel film for use in acid-base titration

    Directory of Open Access Journals (Sweden)

    Musa Ahmad

    2017-11-01

    Full Text Available An optical pH sensing material has been prepared in this study by using sol-gel technique. Bromothymol blue, bromophenol blue and thymol blue were chosen in this study as acidbase indicators for strong acid-strong base, strong acid-weak base and weak acid-strong base titration, respectively. The results show that these indicators could be successfully entrapped inside the sol-gel film and still maintain its chemical behaviour as in solution. The entrapped acid-base indicators respond well to any pH changes and could be used to determine the end-point of the acid-base titration.

  9. Optical ph sensing material prepared from doped sol-gel film for use in acid-base titration

    OpenAIRE

    Musa Ahmad; T.W. Tan

    2017-01-01

    An optical pH sensing material has been prepared in this study by using sol-gel technique. Bromothymol blue, bromophenol blue and thymol blue were chosen in this study as acidbase indicators for strong acid-strong base, strong acid-weak base and weak acid-strong base titration, respectively. The results show that these indicators could be successfully entrapped inside the sol-gel film and still maintain its chemical behaviour as in solution. The entrapped acid-base indicators respond well to ...

  10. A Review of Photocatalysts Prepared by Sol-Gel Method for VOCs Removal

    Directory of Open Access Journals (Sweden)

    Ting Ke Tseng

    2010-05-01

    Full Text Available The sol-gel process is a wet-chemical technique (chemical solution deposition, which has been widely used in the fields of materials science, ceramic engineering, and especially in the preparation of photocatalysts. Volatile organic compounds (VOCs are prevalent components of indoor air pollution. Among the approaches to remove VOCs from indoor air, photocatalytic oxidation (PCO is regarded as a promising method. This paper is a review of the status of research on the sol-gel method for photocatalyst preparation and for the PCO purification of VOCs. The review and discussion will focus on the preparation and coating of various photocatalysts, operational parameters, and will provide an overview of general PCO models described in the literature.

  11. A sol-gel method to synthesize indium tin oxide nanoparticles

    Institute of Scientific and Technical Information of China (English)

    Xiuhua Li; Xiujuan xu; Xin Yin; Chunzhong Li; Jianrong Zhang

    2011-01-01

    Transparent conductive indium tin oxide (ITO) nanoparticles were synthesized by a novel sol-gel method.Granulated indium and tin were dissolved in HNO3 and partially complexed with citric acid.A sol-gel process was induced when tertiary butyl alcohol was added dropwise to the above solution.ITO nanoparticles with an average crystallite size of 18.5 nm and surface area of 32.6 m2/g were obtained after the gel was heat-treated at 700 C.The ITO nanoparticles showed good sinterability,the starting sintering temperature decreased sharply to 900 C,and the 1400 C sintered pellet had a density of 98.1 % of theoretical density (TD).

  12. Dissolution testing of intermediary products in uranium dioxide production by the sol-gel method

    International Nuclear Information System (INIS)

    Melichar, F.; Landspersky, H.; Urbanek, V.

    1979-01-01

    A method was developed of dissolving polyuranates and uranium dioxides in sulphuric acid and in carbonate solutions for testing intermediate products in the sol-gel process preparation of uranium dioxide. A detailed granulometric analysis of spherical particle dispersion was included as part of the tests. Two different production methods were used for the two types of studied materials. The test results show that the test method is suitable for determining temperature sensitivity of the materials to dissolution reaction. The geometrical distribution of impurities in the spherical particles can be determined from the dissolution kinetics. The method allows the determination of the effect of carbon from impurities on the process of uranium dioxide leaching and is thus applicable for testing materials prepared by the sol-gel method. (Z.M.)

  13. Osteoconducting bioglass synthesis via sol-gel process; Biovidro osteocondutor sintetizado pelo processo sol-gel

    Energy Technology Data Exchange (ETDEWEB)

    Pereira, R.V.; Aragones, A.; Barra, G.O.M.; Salmoria, G.V.; Fredel, M.C., E-mail: rafaelavpereira@gmail.com [Universidade Federal de Santa Catarina (UFSC), Florianopolis, SC (Brazil)

    2012-07-01

    The presence of bioglasses in scaffolds has been studied as they promote the osteoconduction in bones. The scaffolds are developed in order to induce the repair and regeneration in bone tissue. An absorbable bioglass from SiO2-CaO-P2O5 system was synthesized by sol-gel process with the intent of producing these scaffolds. Bioglass 58S was define for these work once it presents ions (Ca and P) which assist at the carbonated apatite layer formation when released. The apatite layer presents an important role at the bone regeneration and metabolism, being involved at grow and mineralization of bones. FTIR was realized to characterize the synthesized bioglass on its chemical composition, XRD to analyze the crystalline structure, solubility test to observe the weight variance and SEM to observe the particles morphology. The obtained results confirmed the production of a bioglass with the desired composition to produce osteoconducting scaffolds. (author)

  14. Structural Evolution and Stability of Sol-Gel Biocatalysts

    International Nuclear Information System (INIS)

    Rodgers, L.E.; Foster, L.J.R.; Holden, P.J.; Knott, R.B.; Bartlett, J.B.

    2005-01-01

    Full text: Immobilisation strategies for catalytic enzymes are important as they allow reuse of the biocatalysts. Sol-gel materials have been used to immobilise Candida antarctica lipase B (CALB), a commonly used industrial enzyme with a known crystal structure. The sol-gel bioencapsulate is produced through the condensation of suitable metal alkoxides in the presence of CALB, yielding materials with controlled pore sizes, volume and surface chemistry. Sol-gel matrices have been shown to prolong the catalytic life and enhance the activity of CALB, although the molecular basis for this effect has yet to be elucidated due to the limitations of analysis techniques applied to date. Small angle neutron scattering (SANS) allows such multicomponent systems to be characterised through contrast matching. In the sol-gel bioencapsulate system, at the contrast match point for silica, residual scattering intensity is due to the CALB and density fluctuations in the matrix. A SANS contrast variation series found the match point for the silica matrix, both with and without enzyme present, to be around 35 percent. The model presented here proposes a mechanism for the interaction between CALB and the surrounding sol-gel matrix, and the observed improvement in enzyme activity and matrix strength. The SANS protocol developed here may be applied more generally to bioencapsulates. (authors)

  15. The chemistry of plutonium in sol-gel processes

    International Nuclear Information System (INIS)

    Lloyd, M.H.; Haire, R.G.

    1978-01-01

    Studies of plutonium chemical behavior conducted in conjunction with plutonia sol-gel process development at ORNL are described. The colloidal solutions produced consist of 'Pu(IV) polymer,' and this is therefore the study of polymeric plutonium behavior. Spectrophotometric, electron diffraction, and electron microscopy studies, in addition to specific studies that were concerned with the colloidal behavior of Pu(IV) polymer, indicate several characteristics of polymer that are not generally recognized. The particle nature of Pu(IV) polymer indicated by electron microscopy, the amorphous-crystalline characteristics of primary polymer particles demonstrated by electron diffraction, and the reversible and irreversible aggregation of the primary particles shown by spectrophotometric techniques present a useful view of the nature of Pu(IV) polymer that has been helpful in solving or understanding various types of processing problems involving plutonium hydrolytic behavior. The colloidal characteristics of Pu(IV) polymer and crystallite growth of primary polymer particles by thermal denitration are also described. (orig.) [de

  16. Exploring encapsulation mechanism of DNA and mononucleotides in sol-gel derived silica.

    Science.gov (United States)

    Kapusuz, Derya; Durucan, Caner

    2017-07-01

    The encapsulation mechanism of DNA in sol-gel derived silica has been explored in order to elucidate the effect of DNA conformation on encapsulation and to identify the nature of chemical/physical interaction of DNA with silica during and after sol-gel transition. In this respect, double stranded DNA and dAMP (2'-deoxyadenosine 5'-monophosphate) were encapsulated in silica using an alkoxide-based sol-gel route. Biomolecule-encapsulating gels have been characterized using UV-Vis, 29 Si NMR, FTIR spectroscopy and gas adsorption (BET) to investigate chemical interactions of biomolecules with the porous silica network and to examine the extent of sol-gel reactions upon encapsulation. Ethidium bromide intercalation and leach out tests showed that helix conformation of DNA was preserved after encapsulation. For both biomolecules, high water-to-alkoxide ratio promoted water-producing condensation and prevented alcoholic denaturation. NMR and FTIR analyses confirmed high hydraulic reactivity (water adsorption) for more silanol groups-containing DNA and dAMP encapsulated gels than plain silica gel. No chemical binding/interaction occurred between biomolecules and silica network. DNA and dAMP encapsulated silica gelled faster than plain silica due to basic nature of DNA or dAMP containing buffer solutions. DNA was not released from silica gels to aqueous environment up to 9 days. The chemical association between DNA/dAMP and silica host was through phosphate groups and molecular water attached to silanols, acting as a barrier around biomolecules. The helix morphology was found not to be essential for such interaction. BET analyses showed that interconnected, inkbottle-shaped mesoporous silica network was condensed around DNA and dAMP molecules.

  17. Fabrication and application of mesoporous TiO{sub 2} film coated on Al wire by sol-gel method with EISA

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Linkang; Lu, Jianjun, E-mail: lujianjunktz@tyut.edu.cn

    2017-04-30

    Highlights: • Successfully fabricated mesoporous TiO{sub 2} thin film on Al wire by sol-gel method with EISA. • Ni supported on this film and exhibits good methanation performance. • Investigate the decomposition temperature of template agent F127 in TiO{sub 2} precursor system. - Abstract: Mesoporous TiO{sub 2} film on Al wire was fabricated by sol-gel method with evaporation induced self assembly (EISA) process using F127 as templating agent in the mixed solution of ethanol and Tetra-n-butyl Titanate. The Ni/TiO{sub 2} film catalyst supported on Al wire was prepared by impregnation and the catalytic performance on methanation was carried out in a titanium alloy micro-reactor tube. It was shown that anatase mesoporous TiO{sub 2} film was prepared in this conditions (1 g F127,calcined at 400 °C and aged for 24 h), which has specific surface area of 127 m{sup 2} g{sup −1} and narrow pore size distribution of 5.3 nm. Low calcined temperature (300 °C) cannot transfer film to anatase and decompose F127 completely. Ni/TiO{sub 2} film on Al wire catalyst was proved to be active in CO methanation reaction. And the CO conversion reaches 99% and CH{sub 4} selectivity close is to 80% when the reaction temperature is higher 360 °C.

  18. In-situ sol-gel synthesis and thin film deposition of Cu(In,Ga)(S,Se)2 solar cells

    International Nuclear Information System (INIS)

    Oliveira, L.; Lyubenova, T.; Marti, R.; Fraga, D.; Rey, A.; Carda, J.; Kozhukharov, V.

    2013-01-01

    Full text: Nowadays chalcogenide-based solar cells, like Cu(In,Ga)Se 2 , are competitive in the photovoltaic market, due to its improved performances like higher efficiency (20,3%), long-time stability and excellent durability. In addition, CIGS stand out with an exceptionally high absorption coefficient (more than; 105/cm for 1.5eV) and higher energy photons. These properties make it an excellent candidate as an absorber material for large scale production of photovoltaic modules for building-integrated applications. Traditional methods of manufacture involve vacuum processes including co-evaporation and sputtering that increase production costs. With the aim to lower the expenses by using non-vacuum solution processes we propose an ‘in-situ’ sol-gel synthesis route and direct thin film deposition in the same production step. As a result, we achieved better stoichiometric control, simplicity in the procedure and cost reduction. In this work we describe a procedure to obtain CIGS absorber layer by soft chemistry technique and further deposition onto different substrates. Preparation parameters like precursors, chemical composition, solvents, thermal treatment factors (temperature, time, and atmosphere) were detailed studied. Finally, the resulting materials were characterized by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM) coupled with Energy dispersive X-ray analysis (EDAX), UV-VIS Spectroscopy among others.; key words: sol-gel synthesis, thin film deposition, photovoltaic modules, solar cells

  19. Optical Sensors for Biomolecules Using Nanoporous Sol-Gel Materials

    Science.gov (United States)

    Fang, Jonathan; Zhou, Jing C.; Lan, Esther H.; Dunn, Bruce; Gillman, Patricia L.; Smith, Scott M.

    2004-01-01

    An important consideration for space missions to Mars is the ability to detect biosignatures. Solid-state sensing elements for optical detection of biological entities are possible using sol-gel based biologically active materials. We have used these materials as optical sensing elements in a variety of bioassays, including immunoassays and enzyme assays. By immobilizing an appropriate biomolecule in the sol-gel sensing element, we have successfully detected analytes such as amino acids and hormones. In the case of the amino acid glutamate, the enzyme glutamate dehydrogenase was the immobilized molecule, whereas in the case of the hormone cortisol, an anti-cortisol antibody was immobilized in the sensing element. In this previous work with immobilized enzymes and antibodies, excellent sensitivity and specificity were demonstrated in a variety of formats including bulk materials, thin films and fibers. We believe that the sol-gel approach is an attractive platform for bioastronautics sensing applications because of the ability to detect a wide range of entities such as amino acids, fatty acids, hopanes, porphyrins, etc. The sol-gel approach produces an optically transparent 3D silica matrix that forms around the biomolecule of interest, thus stabilizing its structure and functionality while allowing for optical detection. This encapsulation process protects the biomolecule and leads to a more "rugged" sensor. The nanoporous structure of the sol-gel matrix allows diffusion of small target molecules but keeps larger, biomolecules immobilized in the pores. We are currently developing these biologically active sol-gel materials into small portable devices for on-orbit cortisol detection

  20. Sol-gel-state of hydrated zirconium dioxide

    International Nuclear Information System (INIS)

    Karakchiev, L.G.; Lyakhov, N.Z.

    1995-01-01

    The change in viscosity and density of a system in the course of sol-gel-xerogel has been traced. The size and molecular mass of particles in sol have been determined. Initial sol is practically a monodisperse system. Gel is a spatial net of similar particles. Reversible character of sol-gel transition with a change in water content in the system suggests instability of the bond between the particles in the structure of the solid state body formed. 11 refs.; 4 figs

  1. Functionalization of sol-gel zirconia composites with europium complexes

    International Nuclear Information System (INIS)

    Danchova, Nina; Gutzov, Stoyan

    2014-01-01

    Different sol-gel strategies based on functionalization of ZrO 2 :Eu microparticles with 1,10-phenanthroline (phen) and incorporation of colloidal Eu(phen) 2 (NO 3 ) 3 into zirconia have been used to obtain hybrid sol-gel composites with controlled optical properties. The process leads to materials with quantum yields of about 48 % monitoring the 615 nm emission line at 350 nm excitation. Excitation/luminescence spectroscopy, diffuse reflectance spectroscopy and X-ray diffraction have been used to characterize the hybrid zirconia composites. (orig.)

  2. ENEA contribution to the development of the sol-gel technologies

    International Nuclear Information System (INIS)

    Vatteroni, R.; Arcangeli, G.; Borrello, A.; Majani, C.; Picconi, C.

    1994-11-01

    Compared with conventional ceramic processes, the Sool-Gel technology, invented at the end of sixties for the preparation of ceramic nuclear fuel, seems suitable for obtaining pure and homogeneous fine grade precursors with a deeper control of chemical purity and crystallinity. In the frame of some agreements with other italianrResearch institutes, ENEA (Italian Agency for New Technologies, Energy and Environment) has applied the Sol-Gel technologies to the development of a few advanced ceramic materials; some of these particular applications are described in this report

  3. Synthesis of hybrid sol-gel coatings for corrosion protection of we54-ae magnesium alloy

    International Nuclear Information System (INIS)

    Hernández-Barrios, C A; Peña, D Y; Coy, A E; Duarte, N Z; Hernández, L M; Viejo, F

    2013-01-01

    The present work shows some preliminary results related to the synthesis, characterization and corrosion evaluation of different hybrid sol-gel coatings applied on the WE54-AE magnesium alloy attending to the two experimental variables, i.e. the precursors ratio and the aging time, which may affect the quality and the electrochemical properties of the coatings resultant. The experimental results confirmed that, under some specific experimental conditions, it was possible to obtain homogeneous and uniform, porous coatings with good corrosion resistance that also permit to accommodate corrosion inhibitors

  4. Synthesis of Copper-Based Transparent Conductive Oxides with Delafossite Structure via Sol-Gel Processing

    OpenAIRE

    Götzendörfer, Stefan

    2011-01-01

    Starting off with solubility experiments of possible precursors, the present study reveals the whole development of a sol gel processing route for transparent p type semiconductive thin films with delafossite structure right to the fabrication of functional p-n junctions. The versatile sol formulation could successfully be modified for several oxide compositions, enabling the synthesis of CuAlO2, CuCrO2, CuMnO2, CuFeO2 and more. Although several differences in the sintering behaviour of powde...

  5. Characterizations of maghemite thin films prepared by a sol-gel method

    Energy Technology Data Exchange (ETDEWEB)

    Lau, L. N., E-mail: lau7798@gmail.com; Ibrahim, N. B., E-mail: baayah@ukm.edu.my [School of Applied Physics, Faculty of Science and Technology, Universiti Kebangsaan Malaysia, 43600 UKM Bangi, Selangor. Malaysia (Malaysia)

    2015-09-25

    Iron is one of the abundant elements of Mother Nature and its compound, iron oxide is an interesting material to study since its discovery in the form of magnetite. It can exist in many phases such as hematite and maghemite, this unique nature has put it as a potential candidate in various applications. The aim of this work is to study the influence of different precursor concentrations on the microstructural and magnetic properties of iron oxide thin film. All samples were prepared via the sol-gel method followed by a spin coating technique on quartz substrates. Iron oxide films were confirmed as maghemite phase from X-ray diffraction patterns. The film morphology was examined by a field emission scanning electron microscope and it showed non-systematic value of average grain size and film thickness throughout the study. Hysteresis loop further confirmed that maghemite is a magnetic material when it was characterized by a vibrating sample magnetometer. The coercivity did not show any correlation with molarity. Nevertheless, it increased as the precursor concentration of the film increased due to the domain behaviour. In conclusion, maghemite thin films were successfully synthesized by the sol-gel method with different precursor concentrations in this work.

  6. Effect of Chelating Agents on the Stability of Nano-TiO2 Sol Particles for Sol-Gel Coating.

    Science.gov (United States)

    Maeng, Wan Young; Yoo, Mi

    2015-11-01

    Agglomeration of sol particles in a titanium alkoxide (tetrabutyl orthotitanate (TBOT), > 97%) solution during the hydrolysis and condensation steps makes the sol solution difficult to use for synthesizing homogeneous sol-gel coating. Here, we have investigated the effect of stabilizing agents (acetic acid and ethyl acetoacetate (EAcAc)) on the agglomeration of Ti alkoxide particles during hydrolysis and condensation in order to determine the optimized conditions for controlling the precipitation of TiO2 particles. The study was conducted at R(AC) ([acetic acid]/[TBOT]) = 0.1-5 and R(EAcAc)([EAcAc]/[TBOT]) = 0.05-0.65. We also studied the effects of a basic catalyst ethanolamine (ETA), water, and HCl on sol stability. The chelating ligands in the precursor sol were analyzed with FT-IR. The coating properties were examined by focused ion beam. The stabilizing agents (acetic acid and EAcAc) significantly influenced the agglomeration and precipitation of TBOT precursor particles during hydrolysis. As R(AC) and R(EAcAc) increased, the agglomeration remarkably decreased. The stability of the sol with acetic acid and EAcAc arises from the coordination of the chelating ligand to TBOT that hinders hydrolysis and condensation. A uniform fine coating (thickness: 30 nm) on stainless steel was obtained by using an optimized sol with R(AC) = 0.5 and R(EAcAc) = 0.65.

  7. Sol-gel based optical sensor for determination of Fe (II): a novel probe for iron speciation.

    Science.gov (United States)

    Samadi-Maybodi, Abdolraouf; Rezaei, Vida; Rastegarzadeh, Saadat

    2015-02-05

    A highly selective optical sensor for Fe (II) ions was developed based on entrapment of a sensitive reagent, 2,4,6-tri(2-pyridyl)-s-triazine (TPTZ), in a silica sol-gel thin film coated on a glass substrate. The thin films fabricated based on tetraethoxysilane (TEOS) as precursor, sol-gel pH∼3, water:alkoxyde ratio of 4:1 and TPTZ concentration of 0.112 mol L(-1). The influence of sol-gel parameters on sensing behavior of the fabricated sensor was also investigated. The fabricated sensor can be used for determination of Fe (II) ion with an outstanding high selectivity over a dynamic range of 5-115 ng mL(-1) and a detection limit of 1.68 ng mL(-1). It also showed reproducible results with relative standard deviation of 3.5% and 1.27% for 10 and 90 ng mL(-1) of Fe (II), respectively, along with a fast response time of ∼120 s. Total iron also was determined after reduction of Fe (III) to Fe (II) using ascorbic acid as reducing agent. Then, the concentration of Fe (III) was calculated by subtracting the concentration of Fe (II) from the total iron concentration. Interference studies showed a good selectivity for Fe (II) with trapping TPTZ into sol-gel matrix and appropriately adjusting the structure of doped sol-gel. The sensor was compared with other sensors and was applied to determine iron in different water samples with good results. Copyright © 2014 Elsevier B.V. All rights reserved.

  8. Synthesis and studies of Y-Ba-Cu-O high temperature superconductor prepared by sol-gel method

    International Nuclear Information System (INIS)

    Grigoryan, S.G.; Manukyan, A.L.; Hayrapetyan, A.G.; Arzumanyan, A.M.; Rashidyan, L.H.; Mkrtichyan, N.Y.; Mkrtchyan, A.A.; Kurginyan, K.A.; Trozyan, A.H.; Vardanyan, R.S.

    2004-01-01

    The method of preparation of Y-Ba-Cu-O high temperature superconducting materials by sol-gel processing technique both for powders and thin films are described. All these methods are based on using yttrium alkoxides as precursors, which are not ready available reagents, besides the majority of these methods use copper alkoxides, which show low solubility in organic solvents, moreover they are very sensitive to hydrolysis in air. The new method of preparation of Y-Ba-Cu-O ceramic materials by sol-gel processing technique based on new and convenient precursors stable in air, having high compatibility with each other is offered. Basic scientific and technological issues related to the synthesis of bulk materials, their structure and electrical conductivity are discussed

  9. Sol-gel coatings on carbon/carbon composites

    International Nuclear Information System (INIS)

    Sim, S.M.; Krabill, R.M.; Dalzell, W.J. Jr.; Chu, P.Y.; Clark, D.E.

    1986-01-01

    The need for structural materials that can withstand severe environments up to 4000 0 F has promulgated the investigation of sol-gel derived ceramic and composite coatings on carbon/carbon composite materials. Alumina and zirconia sols have been deposited via thermophoresis on carbon/carbon substrates

  10. Process of forming a sol-gel/metal hydride composite

    Science.gov (United States)

    Congdon, James W [Aiken, SC

    2009-03-17

    An external gelation process is described which produces granules of metal hydride particles contained within a sol-gel matrix. The resulting granules are dimensionally stable and are useful for applications such as hydrogen separation and hydrogen purification. An additional coating technique for strengthening the granules is also provided.

  11. ARSENIC REMOVAL USING SOL-GEL SYNTHESIZED TITANIUM DIOXIDE NANOPARTICLES

    Science.gov (United States)

    In this study, the effectiveness of TiO2 nanoparticles in arsenic adsorption was examined. TiO2 particles (LS) were synthesized via sol-gel techniques and characterized for their crystallinity, surface area and pore volume. Batch adsorption studies were perf...

  12. Stoichiometric hydroxyapatite obtained by precipitation and sol gel processes

    Energy Technology Data Exchange (ETDEWEB)

    Guzman V, C.; Pina B, C.; Munguia, N. [IIM-UNAM, A.P. 70-360, 04510 Mexico D.F. (Mexico)]. e-mail: caroguz@servidor.unam.mx

    2005-07-01

    Three methods for obtaining hydroxyapatite (HA) are described. HA is a very interesting ceramic because of its many medical applications. The first two precipitation methods start from calcium and phosphorous compounds, whereas the third method is a sol-gel process that uses alkoxides. The products were characterized and compared. The observed differences are important for practical applications. (Author)

  13. Neutron detector based on lithiated sol-gel glass

    CERN Document Server

    Wallace, S; Miller, L F; Dai, S

    2002-01-01

    A neutron detector technology is demonstrated based on sup 6 Li/ sup 1 sup 0 B doped sol-gel glass. The detector is a sol-gel glass film coated silicon surface barrier detector (SBD). The ionized charged particles from (n, alpha) reactions in the sol-gel film enter the SBD and are counted. Data showing that gamma-ray pulse amplitudes interfere with identifying charged particles that exit the film layer with energies below the gamma-ray energy is presented. Experiments were performed showing the effect of sup 1 sup 3 sup 7 Cs and sup 6 sup 0 Co gamma rays on the SBD detector. The reaction product energies of the triton and alpha particles from sup 6 Li are significantly greater than the energies of the Compton electrons from high-energy gamma rays, allowing the measurement of neutrons in a high gamma background. The sol-gel radiation detection technology may be applicable to the characterization of transuranic waste, spent nuclear fuel and to the monitoring of stored plutonium.

  14. Sol-gel matrices for direct colorimetric detection of analytes

    Science.gov (United States)

    Charych, Deborah H.; Sasaki, Darryl; Yamanaka, Stacey

    2000-01-01

    The present invention relates to methods and compositions for the direct detection of analytes using color changes that occur in immobilized biopolymeric material in response to selective binding of analytes to their surface. In particular, the present invention provides methods and compositions related to the encapsulation of biopolymeric material into metal oxide glass using the sol-gel method.

  15. Sol-gel synthesis and characterization of fine-grained ceramics in the alumina-titania system

    Energy Technology Data Exchange (ETDEWEB)

    Otterstein, E. [Institute of Physics, University of Rostock, August-Bebel-Strasse 55, 18055 Rostock (Germany)], E-mail: otterstein@physik1.uni-rostock.de; Karapetyan, G. [Institute of Chemistry, University of Rostock, Albert-Einstein-Strasse 3a, 18059 Rostock (Germany); Nicula, R. [Institute of Physics, University of Rostock, August-Bebel-Strasse 55, 18055 Rostock (Germany); Stir, M. [Institute of Physics, University of Rostock, August-Bebel-Strasse 55, 18055 Rostock (Germany); National Institute for Materials Physics, 105b Atomistilor Strasse, P.O.B. MG7, 077125 Bucharest-Magurele (Romania); Schick, C. [Institute of Physics, University of Rostock, Universitaetsplatz 3, 18051 Rostock (Germany); Burkel, E. [Institute of Physics, University of Rostock, August-Bebel-Strasse 55, 18055 Rostock (Germany)

    2008-02-05

    Fine-grained ceramics of the Al{sub 2}O{sub 3}-TiO{sub 2} system were synthesised by reactive sintering of sol-gel precursors (Al- and Ti-alkoxides). The thermal behaviour of the as-prepared xerogels was examined by thermal analysis and X-ray powder diffraction. Preliminary results concerning powder consolidation into bulk ceramic parts using spark plasma sintering (SPS) are discussed.

  16. SOL-GEL SILICA-BASED Ag–Ca–P COATINGS WITH AGRESSIVE PRETREATMENT OF TITANIUM SUBSTRATE

    Directory of Open Access Journals (Sweden)

    ELENA BORSHCHEVA

    2011-12-01

    Full Text Available The aim of the experiment was the obtaining of thin silica coatings on titanium by sol-gel method, using mechanical (SiC - paper No.180 and chemical (leaching in HF pretreatments of the titanium substrates. The solutions were based on TEOS. For the sol-gel dipping process 4 different solutions were prepared: silica, silica with AgNO3 and silica + AgNO3 with brushite (CaHPO4·2H2O or monetite (CaHPO4 powders. The solutions were aged for 7 and 14 days at laboratory temperature. After sol-gel dip-coating process the samples were dried and fired. The adhesion of fired coatings was measured by tape test according to ASTM procedure and the bioactivity of the coatings was tested using in vitro test. The surfaces of the samples after firing, tape test and in vitro test were observed with the optical and electron microscopes. The firing results showed that silica-silver coatings did not change, brushite sol-gel coatings have cracked and the monetite sol-gel coatings have cracked also, but less than brushite ones. In spite of coating´s crackings, the square’s frames made on the surfaces were without any breakdowns after tape tests and the adhesion of all coatings was very good, classified by the highest grade 5. The results of in vitro tests showed that all coatings interacted with simulated body fluid (SBF. After exposition in SBF the new layer formed on substrates. In case of 7 days aged coatings containing brushite the new layer was uniform and compact. In case of 7 days aged coatings containing monetite the new layer was formed by crystals aggregated tightly together. The monetite and brushite coatings prepared from 14 days aged sol were the same as previous ones, but they were thicker. X-ray analyses after in vitro test confirmed dellaite, titanate and hydroxyapatite phases.

  17. COMPARISON OF SOL-GEL SILICATE COATINGS ON Ti SUBSTRATE

    Directory of Open Access Journals (Sweden)

    DIANA HORKAVCOVÁ

    2012-12-01

    Full Text Available The objective of the submitted work was to prepare and to characterize two types of silicate coatings prepared by the sol-gel method using the dip-coating technique on a titanium substrate. Efforts have been made to use mechanical properties of bio-inert titanium and bioactive properties of a silicate layer enriched with an admixture of compounds identified below. The first group consisted of silicate coatings containing silver, brushite and monetite. The other group of silicate coatings contained calcium nitrate and triethyl phosphate. Mechanically and chemically treated titanium substrates were dipped into sols and dried and fired. Silicate coatings from the first group were also chemically treated in 10 mol.l-1 solution of sodium hydroxide. All coatings were measured to determine their adhesive and bioactive properties and furthermore the antibacterial properties were tested in the case of first group. Surfaces of the coated substrates were investigated after the firing and after the individual tests with optical and electron microscopy and X-ray microdiffraction. A tape test demonstrated excellent adhesive property of all coatings to the substrate, classified with degree 5. A static in vitro test demonstrated bioactivity of nearly all the coatings. The basic silicate coating from the first group and one type of coating from the second group were identified as inert. Antibacterial properties of silicate coatings containing silver showed to be different when tested against Escherichia coli bacteria. A complete inhibition of the growth of bacteria under our experimental conditions was observed for the coating containing silver and monetite and a partial inhibition of the growth of bacteria for coatings containing silver and silver in combination with brushite.

  18. Blade-coated sol-gel indium-gallium-zinc-oxide for inverted polymer solar cell

    Directory of Open Access Journals (Sweden)

    Yan-Huei Lee

    2016-11-01

    Full Text Available The inverted organic solar cell was fabricated by using sol-gel indium-gallium-zinc-oxide (IGZO as the electron-transport layer. The IGZO precursor solution was deposited by blade coating with simultaneous substrate heating at 120 °C from the bottom and hot wind from above. Uniform IGZO film of around 30 nm was formed after annealing at 400 °C. Using the blend of low band-gap polymer poly[(4,8-bis-(2-ethylhexyloxy-benzo(1,2-b:4,5-b’dithiophene-2,6-diyl-alt- (4-(2-ethylhexanoyl-thieno [3,4-b]thiophene--2-6-diyl] (PBDTTT-C-T and [6,6]-Phenyl C71 butyric acid methyl ester ([70]PCBM as the active layer for the inverted organic solar cell, an efficiency of 6.2% was achieved with a blade speed of 180 mm/s for the IGZO. The efficiency of the inverted organic solar cells was found to depend on the coating speed of the IGZO films, which was attributed to the change in the concentration of surface OH groups. Compared to organic solar cells of conventional structure using PBDTTT-C-T: [70]PCBM as active layer, the inverted organic solar cells showed significant improvement in thermal stability. In addition, the chemical composition, as well as the work function of the IGZO film at the surface and inside can be tuned by the blade speed, which may find applications in other areas like thin-film transistors.

  19. Influence of annealing temperature on optical properties of Al doped ZnO nanoparticles via sol-gel methods

    Science.gov (United States)

    Rashid, Affa Rozana Abd; Hazwani, Tuan Nur; Mukhtar, Wan Maisarah; Taib, Nur Athirah Mohd

    2018-06-01

    Zinc oxide (ZnO) thin films have become technologically important materials due to their wide range of electrical and optical properties. The characteristics can be further adjusted by adequate doping processes. The effect of dopant concentration of Al, heating treatment and annealing in reducing atmosphere on the optical properties of the thin films is discussed. Undoped and aluminum-doped zinc oxide (AZO) thin films are prepared by the sol-gel method. Zinc acetate dihydrate, 2-methoxyethanol and monoethanolamine are used as precursor, solvent and stabilizer. In the case of AZO, aluminum nitrate nanohydrate is added to the precursor solution with an atomic percentage equal to 0 %, 1 %, 2 % and 3 % of Al. The multi thin layers are transformed into ZnO upon annealing at 450 °C and 500 °C. The optical properties such as transmittance, absorbance, band gap and refractive index of the thin films have been investigated by using UV-Visible Spectroscopy (UV-Vis). The results show that the effect of aluminium dopant concentration on the optical properties is depend on the post-heat treatment of the films. By doping with Al, the transmittance spectra in visible range increased and widen the band gap of ZnO which might due to Burstein-moss effects.

  20. Silica doped with lanthanum sol-gel thin films for corrosion protection

    Energy Technology Data Exchange (ETDEWEB)

    Abuin, M. [Department of Materials Physics, Complutense University at Madrid, Avda. Complutense sn, 28004 Madrid (Spain); Serrano, A. [Glass and Ceramic Institute, CSIC, C. Kelsen 5, 28049 Madrid (Spain); Llopis, J. [Department of Materials Physics, Complutense University at Madrid, Avda. Complutense sn, 28004 Madrid (Spain); Garcia, M.A. [Glass and Ceramic Institute, CSIC, C. Kelsen 5, 28049 Madrid (Spain); IMDEA Nanoscience, Fco. Tomas y Valiente 7, 28049 Madrid (Spain); Carmona, N., E-mail: n.carmona@fis.ucm.es [Department of Materials Physics, Complutense University at Madrid, Avda. Complutense sn, 28004 Madrid (Spain)

    2012-06-01

    We present here anticorrosive silica coatings doped with lanthanum ions for the protection of metallic surfaces as an alternative to chromate (VI)-based conversion coatings. The coatings were synthesized by the sol-gel method starting from silicon alkoxides and two different lanthanum precursors: La (III) acetate hydrate and La (III) isopropoxide. Artificial corrosion tests in acid and alkaline media showed their effectiveness for the corrosion protection of AA2024 aluminum alloy sheets for coating prepared with both precursors. The X-ray absorption Near Edge Structure and X-ray Absorption Fine Structure analysis of the coatings confirmed the key role of lanthanum in the structural properties of the coating determining its anticorrosive properties. - Highlights: Black-Right-Pointing-Pointer Silica sol-gel films doped with lanthanum ions were synthesized. Black-Right-Pointing-Pointer Films from lanthanum-acetate and La-alkoxide were prepared for comparison purposes. Black-Right-Pointing-Pointer La-acetate is an affordable chemical reactive preferred for the industry. Black-Right-Pointing-Pointer Films properties were explored by scanning electron microscopy and X-Ray absorption spectroscopy. Black-Right-Pointing-Pointer An alternative to anticorrosive pre-treatments for metallic surfaces is suggested.

  1. Production of Monodisperse Cerium Oxide Microspheres with Diameters near 100 µm by Internal Gelation Sol-Gel Methods

    Energy Technology Data Exchange (ETDEWEB)

    Katalenich, Jeffrey A.; Kitchen, Brian B.; Pierson, Bruce

    2018-05-01

    Internal gelation sol-gel methods have used a variety of sphere forming methods in the past to produce metal oxide microspheres, but typically with poor control over the size uniformity at diameters near 100 µm. This work describes efforts to make and measure internal gelation, sol-gel microspheres with very uniform diameters in the 100 – 200 µm size range using a two-fluid nozzle. A custom apparatus was used to form aqueous droplets of sol-gel feed solutions in silicone oil and heat them to cause gelation of the spheres. Gelled spheres were washed, dried, and sintered prior to mounting on glass slides for optical imaging and analysis. Microsphere diameters and shape factors were determined as a function of silicone oil flow rate in a two-fluid nozzle and the size of a needle dispensing the aqueous sol-gel solution. Nine batches of microspheres were analyzed and had diameters ranging from 65.5 ± 2.4 µm for the smallest needle and fastest silicone oil flow rate to 211 ± 4.7 µm for the largest needle and slowest silicone oil flow rate. Standard deviations for measured diameters were less than 8% for all samples and most were less than 4%. Microspheres had excellent circularity with measured shape factors of 0.9 – 1. However, processing of optical images was complicated by shadow effects in the photoresist layer on glass slides and by overlapping microspheres. Based on calculated flow parameters, microspheres were produced in a simple dripping mode in the two-fluid nozzle. Using flow rates consistent with a simple dripping mode in a two-fluid nozzle configuration allows for very uniform oxide microspheres to be produced using the internal-gelation sol-gel method.

  2. Transparent Glass-Ceramics Produced by Sol-Gel: A Suitable Alternative for Photonic Materials.

    Science.gov (United States)

    Gorni, Giulio; Velázquez, Jose J; Mosa, Jadra; Balda, Rolindes; Fernández, Joaquin; Durán, Alicia; Castro, Yolanda

    2018-01-30

    Transparent glass-ceramics have shown interesting optical properties for several photonic applications. In particular, compositions based on oxide glass matrices with fluoride crystals embedded inside, known as oxyfluoride glass-ceramics, have gained increasing interest in the last few decades. Melt-quenching is still the most used method to prepare these materials but sol-gel has been indicated as a suitable alternative. Many papers have been published since the end of the 1990s, when these materials were prepared by sol-gel for the first time, thus a review of the achievements obtained so far is necessary. In the first part of this paper, a review of transparent sol-gel glass-ceramics is made focusing mainly on oxyfluoride compositions. Many interesting optical results have been obtained but very little innovation of synthesis and processing is found with respect to pioneering papers published 20 years ago. In the second part we describe the improvements in synthesis and processing obtained by the authors during the last five years. The main achievements are the preparation of oxyfluoride glass-ceramics with a much higher fluoride crystal fraction, at least double that reported up to now, and the first synthesis of NaGdF₄ glass-ceramics. Moreover, a new SiO₂ precursor was introduced in the synthesis, allowing for a reduction in the treatment temperature and favoring hydroxyl group removal. Interesting optical properties demonstrated the incorporation of dopant ions in the fluoride crystals, thus obtaining crystal-like spectra along with higher efficiencies with respect to xerogels, and hence demonstrating that these materials are a suitable alternative for photonic applications.

  3. Transparent Glass-Ceramics Produced by Sol-Gel: A Suitable Alternative for Photonic Materials

    Directory of Open Access Journals (Sweden)

    Giulio Gorni

    2018-01-01

    Full Text Available Transparent glass-ceramics have shown interesting optical properties for several photonic applications. In particular, compositions based on oxide glass matrices with fluoride crystals embedded inside, known as oxyfluoride glass-ceramics, have gained increasing interest in the last few decades. Melt-quenching is still the most used method to prepare these materials but sol-gel has been indicated as a suitable alternative. Many papers have been published since the end of the 1990s, when these materials were prepared by sol-gel for the first time, thus a review of the achievements obtained so far is necessary. In the first part of this paper, a review of transparent sol-gel glass-ceramics is made focusing mainly on oxyfluoride compositions. Many interesting optical results have been obtained but very little innovation of synthesis and processing is found with respect to pioneering papers published 20 years ago. In the second part we describe the improvements in synthesis and processing obtained by the authors during the last five years. The main achievements are the preparation of oxyfluoride glass-ceramics with a much higher fluoride crystal fraction, at least double that reported up to now, and the first synthesis of NaGdF4 glass-ceramics. Moreover, a new SiO2 precursor was introduced in the synthesis, allowing for a reduction in the treatment temperature and favoring hydroxyl group removal. Interesting optical properties demonstrated the incorporation of dopant ions in the fluoride crystals, thus obtaining crystal-like spectra along with higher efficiencies with respect to xerogels, and hence demonstrating that these materials are a suitable alternative for photonic applications.

  4. Transparent Glass-Ceramics Produced by Sol-Gel: A Suitable Alternative for Photonic Materials

    Science.gov (United States)

    Gorni, Giulio; Mosa, Jadra; Balda, Rolindes; Fernández, Joaquin; Durán, Alicia; Castro, Yolanda

    2018-01-01

    Transparent glass-ceramics have shown interesting optical properties for several photonic applications. In particular, compositions based on oxide glass matrices with fluoride crystals embedded inside, known as oxyfluoride glass-ceramics, have gained increasing interest in the last few decades. Melt-quenching is still the most used method to prepare these materials but sol-gel has been indicated as a suitable alternative. Many papers have been published since the end of the 1990s, when these materials were prepared by sol-gel for the first time, thus a review of the achievements obtained so far is necessary. In the first part of this paper, a review of transparent sol-gel glass-ceramics is made focusing mainly on oxyfluoride compositions. Many interesting optical results have been obtained but very little innovation of synthesis and processing is found with respect to pioneering papers published 20 years ago. In the second part we describe the improvements in synthesis and processing obtained by the authors during the last five years. The main achievements are the preparation of oxyfluoride glass-ceramics with a much higher fluoride crystal fraction, at least double that reported up to now, and the first synthesis of NaGdF4 glass-ceramics. Moreover, a new SiO2 precursor was introduced in the synthesis, allowing for a reduction in the treatment temperature and favoring hydroxyl group removal. Interesting optical properties demonstrated the incorporation of dopant ions in the fluoride crystals, thus obtaining crystal-like spectra along with higher efficiencies with respect to xerogels, and hence demonstrating that these materials are a suitable alternative for photonic applications. PMID:29385706

  5. Fabrication of gelatin-siloxane fibrous mats via sol-gel and electrospinning procedure and its application for bone tissue engineering

    International Nuclear Information System (INIS)

    Ren Lei; Wang Jun; Yang Fangyu; Wang Lin; Wang Dong; Wang Tianxiao; Tian Miaomiao

    2010-01-01

    Our strategy is to design and fabricate biomimetic and bioactive scaffolds that resemble the native extracellular matrix as closely as possible so as to create conducive living milieu that will induce cell to function naturally. In the present study, gelatin/siloxane (GS) hybrids were prepared by a sol-gel processing, and electrospinning technique was used to fabricate GS fibrous mats to support the growth of bone marrow-derived mesenchymal stem cells (BMSCs) for tissue engineering of bone. The results indicate that the porous structure and fiber size of the GS fibrous mats can be fine tuned by varying the viscosity of GS precursor solution. Additionally, the Ca 2+ -containing GS fibrous mats biomimetically deposited apatite in a simulated body fluid (SBF), as well as stimulating its BMSCs proliferation and differentiation in vitro, thereby dignifying its in vitro bioactivity.

  6. Hybrid Silicon-Based Organic/Inorganic Block Copolymers with Sol-Gel Active Moieties: Synthetic Advances, Self-Assembly and Applications in Biomedicine and Materials Science.

    Science.gov (United States)

    Czarnecki, Sebastian; Bertin, Annabelle

    2018-03-07

    Hybrid silicon-based organic/inorganic (multi)block copolymers are promising polymeric precursors to create robust nano-objects and nanomaterials due to their sol-gel active moieties via self-assembly in solution or in bulk. Such nano-objects and nanomaterials have great potential in biomedicine as nanocarriers or scaffolds for bone regeneration as well as in materials science as Pickering emulsifiers, photonic crystals or coatings/films with antibiofouling, antibacterial or water- and oil-repellent properties. Thus, this Review outlines recent synthetic efforts in the preparation of these hybrid inorganic/organic block copolymers, gives an overview of their self-assembled structures and finally presents recent examples of their use in the biomedical field and material science. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  7. Red shifts of the Eg(1) Raman mode of nanocrystalline TiO2:Er monoliths grown by sol-gel process

    Science.gov (United States)

    Palomino-Merino, R.; Trejo-Garcia, P.; Portillo-Moreno, O.; Jiménez-Sandoval, S.; Tomás, S. A.; Zelaya-Angel, O.; Lozada-Morales, R.; Castaño, V. M.

    2015-08-01

    Nanocrystalline monoliths of Er doped TiO2 were prepared by the sol-gel technique, by controlling the Er-doping levels into the TiO2 precursor solution. As-prepared and annealed in air samples showed the anatase TiO2 phase. The average diameter of the nanoparticles ranged from 19 to 2.6 nm as the nominal concentration of Er varies from 0% to 7%, as revealed by EDS analysis in an electron microscope. Photo Acoustic Spectroscopy (PAS) allowed calculate the forbidden band gap, evidencing an absorption edge at around 300 nm, attributed to TiO2 and evidence of electronic transitions or Er3+. The Raman spectra, corresponding to the anatase phase, show the main phonon mode Eg(1) band position at 144 cm-1 with a red shift for the annealing samples.

  8. Sol-gel derived polymer composites for energy storage and conversion

    Science.gov (United States)

    Han, Kuo

    Sol-gel process is a simple chemistry to convert the small precursor molecules into an inorganic polymer, which could be applied to synthesize inorganic materials, modify the interface of materials, bridge the organic and inorganic materials, etc. In this dissertation, novel sol-gel derived composites have been developed for high dielectric breakdown capacitors, low high frequency loss capacitors and flexible piezoelectrics. Numerous efforts have been made in the past decades to improve the energy storage capability of composite materials by incorporating nanometer scale ceramic addictives with high dielectric permittivity into dielectric polymers with high breakdown strength. However, most composites suffer from the low breakdown strength and make the potential gain in energy density small. Here, a new chemical strategy is proposed that, through sol-gel reactions between ceramic precursors and functional groups at the end of the functionalized Poly(vinylidene fluoride -co-chlorotrifluoroethylene) chains, amorphous low permittivity ceramics was in-situ generated in the polymer matrix and cross-linked the polymer chains simultaneously. By carefully tuning precursors, the polymer/precursors feeding ratios, a series of nanocomposites were systematically designed. All the samples are comprehensively characterized and the structure-property correlations are well investigated. The optimal samples exhibit higher breakdown strength than the pristine polymer. The enhanced breakdown strength ascribed to low contrast in permittivity, great dispersion and improved electrical and mechanical properties. This newly developed approach has shown great promise for new composite capacitors. The percolative polymer composites have recently exhibited great potential in energy storage due to their high dielectric permittivities at the neighborhood of the percolation threshold. Yet high energy dissipation and poor voltage endurance of the percolative composites resulted from electrical

  9. Epitaxial growth of Er, Ti doped LiNbO3 films prepared by sol-gel method

    International Nuclear Information System (INIS)

    Takahashi, Makoto; Yoshiga, Tsuyoshi; Kajitani, Naofumi; Takeda, Yuki; Sato, Shoji; Wakita, Koichi; Ohnishi, Naoyuki; Hotta, Kazutoshi; Kurachi, Masato

    2006-01-01

    Erbium (Er 3+ ) doped lithium niobate (LiNbO 3 ) thick films were deposited on z-cut congruent LiNbO 3 (LN) substrate by the sol-gel method from the 0.20 mol/dm 3 precursor solution containing various Er 3+ concentration and 0.10 mol/dm 3 poly(vinyl alcohol) (PVA), and their crystal characteristics were evaluated. The Er 3+ concentration in the LN film was controlled by the Er 3+ concentration in the starting solution. The orientation relationships between Er doped LN films and substrates were determined by X-ray diffraction, Raman spectroscopy, and transmission electron microscopy, and (006) oriented Er doped LN epitaxial layers with parallel epitaxial relationships could be grown on the z-cut LN wafer. Moreover, it was made clear from the electron beam diffraction measurements that the film came to be polycrystalline, when the Er concentration was over 3 mol%. The refractive index of Er-doped LN films decreased with increasing Er concentration. 1.5 mol% Ti: 1.0 mol% Er LN films, which acted as a waveguide, were prepared by our so-gel method. It showed the 1530 nm emission by 980 nm excitation, which was considered to be due to the Er 3+ corresponding to the 4 I 13/2 → 4 I 15/2 transition. (author)

  10. Electrochemically assisted deposition of sol-gel bio-composite with co-immobilized dehydrogenase and diaphorase

    Energy Technology Data Exchange (ETDEWEB)

    Wang Zhijie [LCPME, UMR 7564, CNRS-Nancy University, 405, rue de Vandoeuvre, 54600 Villers-les-Nancy (France); Etienne, Mathieu, E-mail: mathieu.etienne@lcpme.cnrs-nancy.fr [LCPME, UMR 7564, CNRS-Nancy University, 405, rue de Vandoeuvre, 54600 Villers-les-Nancy (France); Kohring, Gert-Wieland [Mikrobiologie, Universitaet des Saarlandes, Campus, Geb. A1.5, D-66123 Saarbruecken (Germany); Bon-Saint-Come, Yemima; Kuhn, Alexander [Universite Bordeaux, ISM, ENSCPB, 16 avenue Pey Berland, 33607 Pessac (France); Walcarius, Alain [LCPME, UMR 7564, CNRS-Nancy University, 405, rue de Vandoeuvre, 54600 Villers-les-Nancy (France)

    2011-10-30

    We report here that the electrochemically assisted deposition (EAD) of silica thin films can be a good strategy to co-encapsulate D-sorbitol dehydrogenase (DSDH) and diaphorase in an active form. This is achieved via the electrolysis of a hydrolyzed sol containing the biomolecules to initiate the poly-condensation of silica precursors upon electrochemically induced pH increase at the electrode/solution interface. DSDH was found to be very sensitive to the silica gel environment and the addition of a positively-charged polyelectrolyte was necessary to ensure effective operational behavior of the biomolecules. The composition of the sol and the conditions for electrolysis have been optimized with respect to the intensity of the electrochemical response to D-sorbitol oxidation. The K{sub m} of DSDH in the electrodeposited film was in the range of 3 mM, slightly better than the value determined biochemically in solution (6.5 mM). The co-immobilization of DSDH and diaphorase in this way led on the one hand to the possible reduction of NAD{sup +} to NADH (simultaneously to D-sorbitol oxidation) and on the other hand to the safe re-oxidation of the co-factor using a mediator (ferrocenedimethanol) as electron relay. The bioelectrocatalytic response looks promising for electro-enzymatic applications. To support this idea, the EAD of sol-gel bio-composite has been extended to macroporous electrodes displaying a much bigger electroactive surface area.

  11. Tunable Optical Properties of Metal Nanoparticle Sol-Gel Composites

    Science.gov (United States)

    Smith, David D.; Snow, Lanee A.; Sibille, Laurent; Ignont, Erica

    2001-01-01

    We demonstrate that the linear and non-linear optical properties of sol-gels containing metal nanoparticles are highly tunable with porosity. Moreover, we extend the technique of immersion spectroscopy to inhomogeneous hosts, such as aerogels, and determine rigorous bounds for the average fractional composition of each component, i.e., the porosity of the aerogel, or equivalently, for these materials, the catalytic dispersion. Sol-gels containing noble metal nanoparticles were fabricated and a significant blue-shift in the surface plasmon resonance (SPR) was observed upon formation of an aerogel, as a result of the decrease in the dielectric constant of the matrix upon supercritical extraction of the solvent. However, as a result of chemical interface damping and aggregation this blue-shift does not strictly obey standard effective medium theories. Mitigation of these complications is achieved by avoiding the use of alcohol and by annealing the samples in a reducing atmosphere.

  12. Electrophoretic deposition of sol-gel-derived ceramic coatings

    International Nuclear Information System (INIS)

    Zhang, Y.; Crooks, R.M.

    1992-01-01

    In this paper the physical, optical, and chemical characteristics of electrophoretically and dip-coated sol-gel ceramic films are compared. The results indicate that electrophoresis may allow a higher level of control over the chemistry and structure of ceramic coatings than dip-coating techniques. For example, controlled-thickness sol-gel coatings can be prepared by adjusting the deposition time or voltage. Additionally, electrophoretic coatings can be prepared in a four-component alumino-borosilicate sol display interesting optical characteristics. For example, the ellipsometrically-measured refractive indices of electrophoretic coatings are higher than the refractive indices of dip-coated films cast from identical sols, and they are also higher than any of the individual sol components. This result suggests that there are physical and/or chemical differences between films prepared by dip-coating and electrophoresis

  13. Epoxy-silica hybrids by nonaqueous sol-gel process

    Czech Academy of Sciences Publication Activity Database

    Ponyrko, Sergii; Kobera, Libor; Brus, Jiří; Matějka, Libor

    2013-01-01

    Roč. 54, č. 23 (2013), s. 6271-6282 ISSN 0032-3861 R&D Projects: GA ČR GAP108/12/1459 Grant - others:AV ČR(CZ) M200500903 Institutional support: RVO:61389013 Keywords : epoxy-silica hybrid * nonaqueous sol-gel process * gelation Subject RIV: CD - Macromolecular Chemistry Impact factor: 3.766, year: 2013

  14. Sol-Gel Thin Films for Plasmonic Gas Sensors

    Science.gov (United States)

    Della Gaspera, Enrico; Martucci, Alessandro

    2015-01-01

    Plasmonic gas sensors are optical sensors that use localized surface plasmons or extended surface plasmons as transducing platform. Surface plasmons are very sensitive to dielectric variations of the environment or to electron exchange, and these effects have been exploited for the realization of sensitive gas sensors. In this paper, we review our research work of the last few years on the synthesis and the gas sensing properties of sol-gel based nanomaterials for plasmonic sensors. PMID:26184216

  15. Analyses of desorbed H2O with temperature programmed desorption technique in sol-gel derived HfO2 thin films

    International Nuclear Information System (INIS)

    Shimizu, H.; Nemoto, D.; Ikeda, M.; Nishide, T.

    2009-01-01

    Hafnium oxide (HfO 2 ) is a promising material for the gate insulator in highly miniaturized silicon (Si) ultra-large-scale-integration (ULSI) devices (32 nm and beyond). In the field chemistry, a sol-gel processing has been used to fabricate HfO 2 thin film with the advantages of low cost, relative simplicity, and easy control of the composition of the layers formed. Temperature-programmed desorption (TPD) has been used not only for analyzing adsorbed gases on the surfaces of bulk sol-gel-derived HfO 2 of sol-gel-derived HfO 2 thin film fired at 350, 450, 550 and 700 deg C in sol-gel derived HfO 2 films in air is investigated using TPD, and also the material characterization of HfO 2 thin films is evaluated by X-ray diffraction (XRD) method. The dielectric constant of the films was also estimated using the capacitance-voltage (C-V) method. TPD is essentially a method of analyzing desorped gases from samples heated by infra-red light as a function of temperature under vacuum conditions using a detector of quadruple mass spectroscopy (QMS). Sol-gel-derived HfO 2 films were fabricated on 76-mm-diameter Si(100) wafers as follows. Hafnia sol solutions were prepared by dissolving HfCl 4 in NH 4 OH solution, followed by the of HCOOH. (author)

  16. Sol-gel derived zinc oxide films alloyed with cobalt and aluminium

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, Mamta [Department of Electronic Science, University of Delhi South Campus, Benito Juarez Road, New Delhi 110 021 (India); Mehra, R.M., E-mail: rammehra2003@yahoo.co [Department of Electronic Science, University of Delhi South Campus, Benito Juarez Road, New Delhi 110 021 (India)

    2010-05-03

    ZnO films codoped with 5 at.% Co and 1 at.% Al were prepared by sol-gel technique on corning glass and silicon substrates with precursor sols of different pH values. The pH was varied from 5.4 to 11 by adding varying amounts of monoethanolamine to the sol. Since pH plays an important role in controlling the properties of films, we discuss in detail the effect of pH value on the structural, morphological and optical properties of the grown films. X-ray diffraction and atomic force microscopy images reveal that the size of crystallites increases with pH of the sol. The variation of pH in the reaction system influences the density of homogeneous nucleation and the crystal growth along the c-axis. High quality Co and Al codoped ZnO films annealed at 600 {sup o}C have been obtained using a sol with pH = 9. These sol-gel derived films find their suitability to be used as dilute magnetic semiconductors.

  17. Sol-gel derived zinc oxide films alloyed with cobalt and aluminium

    International Nuclear Information System (INIS)

    Sharma, Mamta; Mehra, R.M.

    2010-01-01

    ZnO films codoped with 5 at.% Co and 1 at.% Al were prepared by sol-gel technique on corning glass and silicon substrates with precursor sols of different pH values. The pH was varied from 5.4 to 11 by adding varying amounts of monoethanolamine to the sol. Since pH plays an important role in controlling the properties of films, we discuss in detail the effect of pH value on the structural, morphological and optical properties of the grown films. X-ray diffraction and atomic force microscopy images reveal that the size of crystallites increases with pH of the sol. The variation of pH in the reaction system influences the density of homogeneous nucleation and the crystal growth along the c-axis. High quality Co and Al codoped ZnO films annealed at 600 o C have been obtained using a sol with pH = 9. These sol-gel derived films find their suitability to be used as dilute magnetic semiconductors.

  18. Synthesis and characterization of NiO nanopowder by sol-gel process

    Energy Technology Data Exchange (ETDEWEB)

    Ningsih, Sherly Kasuma Warda [Department of Chemistry, Faculty of Mathematics and Natural Sciences Padang State University, Kampus Air Tawar, Jl. Prof. Dr. Hamka, West Sumatera, 25161, Indonesia Email: sherly-kasuma@yahoo.com (Indonesia)

    2015-09-30

    Preparation of nickel oxide (NiO) nanopowder by sol-gel process has been studied. NiO nanopowders were obtained by sol-gel method by using nickel nitrate hexahydrate and sodium hydroxide and aquadest were used as precursor, agent precipitator and solvent, respectively. The powders were formed by drying at 110°C and followed by heating in the furnace at 400°C for 1.5 hours. The product was obtained black powder. The product was characterized by Energy Dispesive X-ray Fluorescence (ED-XRF), X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM). The ED-XRF pattern shows the composition of NiO produced was 97.1%. The XRD pattern showed NiO forms were produced generally in monoclinic stucture. The crystalline size of NiO was obtained in the range 40-85 nm. SEM micrograph clearly showed that powder had a spherical with uniform distribution size is 0.1-1.0 µm approximately.

  19. Phospholipid Fatty Acids as Physiological Indicators of Paracoccus denitrificans Encapsulated in Silica Sol-Gel Hydrogels

    Directory of Open Access Journals (Sweden)

    Josef Trögl

    2015-02-01

    Full Text Available The phospholipid fatty acid (PLFA content was determined in samples of Paracoccus denitrificans encapsulated in silica hydrogel films prepared from prepolymerized tetramethoxysilane (TMOS. Immediately after encapsulation the total PLFA concentration was linearly proportional to the optical density (600 nm of the input microbial suspension (R2 = 0.99. After 7 days this relationship remained linear, but with significantly decreased slope, indicating a higher extinction of bacteria in suspensions of input concentration 108 cells/mL and higher. trans-Fatty acids, indicators of cytoplasmatic membrane disturbances, were below the detection limit. The cy/pre ratio (i.e., ratio of cyclopropylated fatty acids (cy17:0 + cy19:0 to their metabolic precursors (16:1ω7 + 18:1ω7, an indicator of the transition of the culture to a stationary growth-phase, decreased depending on co-immobilization of nutrients in the order phosphate buffer > mineral medium > Luria Broth rich medium. The ratio, too, was logarithmically proportional to cell concentration. These results confirm the applicability of total PLFA as an indicator for the determination of living biomass and cy/pre ratio for determination of nutrient limitation of microorganisms encapsulated in sol-gel matrices. This may be of interest for monitoring of sol-gel encapsulated bacteria proposed as optical recognition elements in biosensor construction, as well as other biotechnological applications.

  20. Improvement of Adhesion Properties and Corrosion Resistance of Sol-Gel Coating on Zinc.

    Science.gov (United States)

    Savignac, Pauline; Menu, Marie-Joëlle; Gressier, Marie; Denat, Bastien; Khadir, Yacine El; Manov, Stephan; Ansart, Florence

    2018-05-03

    Corrosion is a major problem for durability of many metals and alloys. Among the efficient classical surface treatments, chromate-based treatments must be banished from industrial use due to their toxicity. At the same time, sol-gel routes have demonstrated high potential to develop an efficient barrier effect against aggressive environments. By this process, the anti-corrosion property can be also associated to others in the case of the development of multi-functional hybrid coatings. In this paper, the main goal is precisely to improve both the corrosion resistance and the adhesion properties of phosphated zinc substrates by the deposition of a hybrid (organic-inorganic) sol-gel layer. To reach this double objective, a choice between two formulations 3-glycidoxypropyltrimethoxysilane (GPTMS)/aluminum-tri-sec-butoxide (ASB) and 3-(trimethoxysilyl)propylmethacrylate (MAP)/tetraethylorthosilicate (TEOS) was firstly made based on the results obtained by microstructural characterizations using SEM, optical analysis, and mechanical characterization such as shock and/or scratch tests (coupled to climatic chamber and salt spray exposure). Several investigations were performed in this study, and the best formulation and performances of the system were obtained by adding a new precursor (1-[3-(trimethoxysilyl)propyl]ureido-UPS) under controlled conditions, as detailed in this paper.

  1. Preparation of mesoporous silica microparticles by sol-gel/emulsion route for protein release.

    Science.gov (United States)

    Vlasenkova, Mariya I; Dolinina, Ekaterina S; Parfenyuk, Elena V

    2018-04-06

    Encapsulation of therapeutic proteins into particles from appropriate material can improve both stability and delivery of the drugs, and the obtained particles can serve as a platform for development of their new oral formulations. The main goal of this work was development of sol-gel/emulsion method for preparation of silica microcapsules capable of controlled release of encapsulated protein without loss of its native structure. For this purpose, the reported in literature direct sol-gel/W/O/W emulsion method of protein encapsulation was used with some modifications, because the original method did not allow to prepare silica microcapsules capable for protein release. The particles were synthesized using sodium silicate and tetraethoxysilane as silica precursors and different compositions of oil phase. In vitro kinetics of bovine serum albumin (BSA) release in buffer (pH 7.4) was studied by Fourier transform infrared (FTIR) and fluorescence spectrometry, respectively. Structural state of encapsulated BSA and after release was evaluated. It was found that the synthesis conditions influenced substantially the porous structure of the unloaded silica particles, release properties of the BSA-loaded silica particles and structural state of the encapsulated and released protein. The modified synthesis conditions made it possible to obtain the silica particles capable of controlled release of the protein during a week without loss of the protein native structure.

  2. Reinforcement of LENRA film by in-situ generated silica produced by sol gel process

    International Nuclear Information System (INIS)

    Mahathir Mohamed; Eda Yuhana Ariffin; Dahlan Mohd; Ibrahim Abdullah

    2008-08-01

    Liquid epoxidised natural rubber acrylate (LENRA) film was reinforced with silica-siloxane structures formed in-situ via sol gel process. Combination of these two components produces organic-inorganic composites. Tetraethylorthosilicate (TEOS) was used as precursor material for silica generation. Sol gel reaction was carried out at different concentrations of TEOS i.e. between 10 and 50 phr. Instrumental analysis was carried out by dynamic mechanical analysis (DMA), thermogravimetry analysis (TGA) and FTIR. It was found that miscibility between organic and inorganic components improved with the presence of silanol groups (Si-OH) and polar solvent i.e. THF, via hydrogen bonding formation between siloxane and LENRA. In this work, the effects of TEOS composition on mechanical properties and interaction that occurs between fillers and matrix have also been studied. It was observed that increasing the concentration of TEOS improved the scratch and stress properties of the film. Morphology study by the scanning electron microscopy (SEM) showed in-situ generated silica particles were homogenous and well dispersed at low concentrations of TEOS. (Author)

  3. The Influence of Microgravity on Silica Sol-Gel Formation

    Science.gov (United States)

    Sibille, L.; Smith, D. D.; Cronise, R.; Hunt, A. J.; Wolfe, D. B.; Snow, L. A.; Oldenberg, S.; Halas, N.; Rose, M. Franklin (Technical Monitor)

    2000-01-01

    We discuss space-flight experiments involving the growth of silica particles and gels. The effect of microgravity on the growth of silica particles via the sol-gel route is profound. In four different recipes spanning a large range of the parameter space that typically produces silica nanoparticles in unit-gravity, low-density gel structures were instead formed in microgravity. The particles that did form were generally smaller and more polydisperse than those grown on the ground. These observations suggest that microgravity reduces the particle growth rate, allowing unincorporated species to form aggregates and ultimately gel. Hence microgravity favors the formation of more rarefied structures, providing a bias towards diffusion-limited cluster-cluster aggregation. These results further suggest that in unit gravity, fluid flows and sedimentation can significantly perturb sol-gel substructures prior to gelation and these deleterious perturbations may be "frozen" into the resulting microstructure. Hence, sol-gel pores may be expected to be smaller, more uniform, and less rough when formed in microgravity.

  4. Synthesis of cadmium tungstate films via sol-gel processing

    Energy Technology Data Exchange (ETDEWEB)

    Lennstrom, Kirk; Limmer, Steven J.; Cao Guozhong

    2003-06-23

    Cadmium tungstate is a scintillator material with excellent intrinsic photoluminescent properties. It is highly resistant to gamma radiation, has an almost non-existent afterglow and is highly efficient. Cadmium tungstate is also non-hydroscopic, unlike the more prevalent thallium-doped alkali halide scintillators. In order to create thin films of cadmium tungstate with precise stoichiometric control, a sol-gel processing technique has been applied to produce this material for the first time. In addition to lower processing temperatures, sol-gel-derived cadmium tungstate is cheaper and easier than other technologies, particularly for thin films. Furthermore, it has the potential to produce nanostructured materials with good optical quality. X-Ray diffraction results of sol-gel-derived materials fired at various temperatures imply crystallization of cadmium tungstate without the intermediate formation of either tungsten oxide or cadmium oxide. Scanning electron microscopy analysis shows the formation of nano-sized particles prior to heat treatment, which form meso-sized particles after the heat treatment. Photoluminesce analysis indicates emission of derived films at 480 nm, which agrees with other published data. Finally, the efficiency of derived films was approximately 6%{+-}1.8%.

  5. Development of highly-ordered, ferroelectric inverse opal films using sol gel infiltration

    Science.gov (United States)

    Matsuura, N.; Yang, S.; Sun, P.; Ruda, H. E.

    2005-07-01

    Highly-ordered, ferroelectric, Pb-doped Ba0.7Sr0.3TiO3, inverse opal films were fabricated by spin-coating a sol gel precursor into a polystyrene artificial opal template followed by heat treatment. Thin films of the ferroelectric were independently studied and were shown to exhibit good dielectric properties and high refractive indices. The excellent quality of the final inverse opal film using this spin-coating infiltration method was confirmed by scanning electron microscopy images and the good correspondence between optical reflection data and theoretical simulations. Using this method, the structural and material parameters of the final ferroelectric inverse opal film were easily adjusted by template heating and through repeated infiltrations, without changes in the initial template or precursor. Also, crack-free inverse opal thin films were fabricated over areas comparable to that of the initial crack-free polystyrene template (˜100 by 100 μm2).

  6. Evaluation of hybrid sol-gel incorporated with nanoparticles as nano paint

    International Nuclear Information System (INIS)

    Jameel, Zainab N.; Haider, Adawiya J.; Taha, Samar Y.; Gangopadhyay, Shubhra; Bok, Sangho

    2016-01-01

    A coating with self-cleaning characteristics has been developed using a TiO_2/SiO_2 hybrid sol-gel, TiO_2 nanoparticles and organosilicate nanoparticles (OSNP). A patented technology of the hybrid sol-gel and OSNP was combined with TiO_2 nanoparticles to create the surface chemistry for self-cleaning. Two synthesis methods have been developed to prepare TiO_2 nanoparticles (NPs), resulting in the enhancement of local paint by the addition of anatase and rutile TiO_2 phases. The NPs size as determined by Dynamic Light Scattering (DLS) ranges within of (3-4) and (20-42) nm, which was also confirmed by Scanning Electron Microscopy (SEM). The nanoparticles showed surface charge (zeta-potential, ζ) of +35 and +25.62 mV for the methods, respectively, and ζ values of +41.31 and 34.02 mV for anatase and rutile phases, respectively. The NPs were mixed with the coating solution (i.e., hybrid sol-gel and OSNP) in different concentrations and thin films were prepared by spin coating. Self-cleaning tests were performed using Rhodamine B (RhB) as a pollution indicator. The effect of UV-irradiation on the films was also studied. Anatase and rutile incorporated as a mixture with different ratios in local paint and washability as well as a contrast ratio tests were performed. It was found that the addition of TiO_2 NPs in combination with irradiation show a great enhancement of RhB degradation (1%) wt. with a decrease in contact angle and improved washability.

  7. Evaluation of hybrid sol-gel incorporated with nanoparticles as nano paint

    Energy Technology Data Exchange (ETDEWEB)

    Jameel, Zainab N., E-mail: zeinb76-alrekbe@yahoo.com; Haider, Adawiya J., E-mail: adawiyahaider@yahoo.com [Nanotechnology and Advanced Materials Research Center, The University of Technology, Baghdad (Iraq); Taha, Samar Y., E-mail: samarjam2002@yahoo.com [College of Science for Women, University of Baghdad, Baghdad (Iraq); Gangopadhyay, Shubhra, E-mail: gangopadhyays@missouri.edu; Bok, Sangho, E-mail: BokSa@missouri.edu [Department of Electrical and Computer, University of Missouri, Engineering, Building West, Columbia, Missouri 65211 (United States)

    2016-07-25

    A coating with self-cleaning characteristics has been developed using a TiO{sub 2}/SiO{sub 2} hybrid sol-gel, TiO{sub 2} nanoparticles and organosilicate nanoparticles (OSNP). A patented technology of the hybrid sol-gel and OSNP was combined with TiO{sub 2} nanoparticles to create the surface chemistry for self-cleaning. Two synthesis methods have been developed to prepare TiO{sub 2} nanoparticles (NPs), resulting in the enhancement of local paint by the addition of anatase and rutile TiO{sub 2} phases. The NPs size as determined by Dynamic Light Scattering (DLS) ranges within of (3-4) and (20-42) nm, which was also confirmed by Scanning Electron Microscopy (SEM). The nanoparticles showed surface charge (zeta-potential, ζ) of +35 and +25.62 mV for the methods, respectively, and ζ values of +41.31 and 34.02 mV for anatase and rutile phases, respectively. The NPs were mixed with the coating solution (i.e., hybrid sol-gel and OSNP) in different concentrations and thin films were prepared by spin coating. Self-cleaning tests were performed using Rhodamine B (RhB) as a pollution indicator. The effect of UV-irradiation on the films was also studied. Anatase and rutile incorporated as a mixture with different ratios in local paint and washability as well as a contrast ratio tests were performed. It was found that the addition of TiO{sub 2} NPs in combination with irradiation show a great enhancement of RhB degradation (1%) wt. with a decrease in contact angle and improved washability.

  8. Influence of Experimental Parameters Using the Dip-Coating Method on the Barrier Performance of Hybrid Sol-Gel Coatings in Strong Alkaline Environments

    Directory of Open Access Journals (Sweden)

    Rita B. Figueira

    2015-04-01

    Full Text Available Previous studies have shown that the barrier effect and the performance of organic-inorganic hybrid (OIH sol-gel coatings are highly dependent on the coating deposition method as well as on the processing conditions. However, studies on how the coating deposition method influences the barrier properties in alkaline environments are scarce. The aim of this experimental research was to study the influence of experimental parameters using the dip-coating method on the barrier performance of an OIH sol-gel coating in contact with simulated concrete pore solutions (SCPS. The influence of residence time (Rt, a curing step between each dip step and the number of layers of sol-gel OIH films deposited on hot-dip galvanized steel to prevent corrosion in highly alkaline environments was studied. The barrier performance of these OIH sol-gel coatings, named U(400, was assessed in the first instants of contact with SCPS, using electrochemical impedance spectroscopy and potentiodynamic methods. The durability and stability of the OIH coatings in SCPS was monitored during eight days by macrocell current density. The morphological characterization of the surface was performed by Scanning Electronic Microscopy before and after exposure to SCPS. Glow Discharge Optical Emission Spectroscopy was used to investigate the thickness of the U(400 sol-gel coatings as a function of the number of layers deposited with and without Rt in the coatings thickness.

  9. Sol-gel processes. January 1970-September 1989 (Citations from the NTIS data base). Report for January 1970-September 1989

    International Nuclear Information System (INIS)

    1989-09-01

    This bibliography contains citations concerning the development and utilization of sol-gel processes and techniques. Topics include antireflective coatings, studies of sol-gel transitions, sol-gel synthesis and polymerization, sol-gel derived thin films and glasses, and sol-gel production of microspheres. Applications in nuclear waste management, nuclear-fuel manufacturing, glass optical waveguide development, and solar-energy collection are presented. (This updated bibliography contains 179 citations, 39 of which are new entries to the previous edition.)

  10. Investigation of Electrical, Optical and GaS Sensing properties Sol-Gel Derived WO3 Thin Films

    International Nuclear Information System (INIS)

    Dumludag, F.

    2008-01-01

    Tungsten oxide (WO 3 ) is a wide band gap n-type semiconductor. Thin films of WO 3 are considerable interest because of their potential applications in electrochromic devices, and gas sensors. In this work, WO 3 thin films were deposited on IDT (Interdigital electrodes) by a sol-gel dipping process. Precursor solution was prepared by dissolving of tungstic acid in ammonia. We investigated d.c. and a.c. (40 Hz-100 KHz) electrical properties of the films in the temperature range of 293K and 473K in vacuum ambient (10 - 2 mbar). We observed frequency dependent conductivity behavior at high frequencies. Absorption spectra of the film showed that a maximum absorption occurred at 330 nm. We also investigated the response of the films to vapors of the volatile organic compounds (acetone, chloroform, toluene, ethanol, ammonia) and water vapor. The films showed no sensitivity to the test gases at room temperature. Concentration of the vapors were controlled by mass flowmeters. All the measurement system was computerized

  11. The influence of the matrix structure on the oxidation of aniline in a silica sol-gel composite

    International Nuclear Information System (INIS)

    Widera, J.; Kijak, A.M.; Ca, D.V.; Pacey, G.E.; Taylor, R.T.; Perfect, H.; Cox, J.A.

    2005-01-01

    Mesoporous and microporous silica matrices were formed on indium tin oxide electrodes for liquid-phase voltammetry and as monoliths for solid-state voltammetry of aniline. The pore structure, which was verified by scanning probe microscopy and by surface area measurement, was directed by either control of pH during sol-gel processing or by inclusion of a templating agent. Whether aniline was included as a dopant in the sol-gel or as a component of the contacting liquid, the pore size influenced the coupling of the product of its electrochemical oxidation. With microporous silica, the dominant products were dimers and related short-chain products whereas with mesoporous silica, polymerization was suggested. As a step toward the formation of polyaniline (PANI) that is covalently anchored to the sol-gel, the electrochemistry of aniline was investigated using composites prepared from sols comprising tetraethyl orthosilicate (TEOS), 3-aminophenyl-[3-triethoxylsilyl)-propyl] urea (ormosil), and aniline in various ratios. Combinatorial chemistry identified that the optimum combination of silica precursors in terms of obtaining PANI was a 1:12 mole ratio of ormosil:TEOS

  12. Fluorescent silica hybrid materials containing benzimidazole dyes obtained by sol-gel method and high pressure processing

    International Nuclear Information System (INIS)

    Hoffmann, Helena Sofia; Stefani, Valter; Benvenutti, Edilson Valmir; Costa, Tania Maria Haas; Gallas, Marcia Russman

    2011-01-01

    Research highlights: → Sol-gel technique was used to obtain silica based hybrid materials containing benzimidazole dyes. → The sol-gel catalysts, HF and NaF, produce xerogels with different optical and textural characteristics. → High pressure technique (6.0 GPa) was used to produce fluorescent and transparent silica compacts with the dyes entrapped in closed pores, maintaining their optical properties. → The excited state intramolecular proton transfer (ESIPT) mechanism of benzimidazole dyes was studied by steady-state fluorescence spectroscopy for the monoliths, powders, and compacts. - Abstract: New silica hybrid materials were obtained by incorporation of two benzimidazole dyes in the silica network by sol-gel technique, using tetraethylorthosilicate (TEOS) as inorganic precursor. Several syntheses were performed with two catalysts (HF and NaF) producing powders and monoliths with different characteristics. The dye 2-(2'-hydroxy-5'-aminophenyl)benzimidazole was dispersed and physically adsorbed in the matrix, and the dye 2'(5'-N-(3-triethoxysilyl)propylurea-2'-hydroxyphenyl)benzimidazole was silylated, becoming chemically bonded to the silica network. High pressure technique was used to produce fluorescent and transparent silica compacts with the silylated and incorporated dye, at 6.0 GPa and room temperature. The excited state intramolecular proton transfer (ESIPT) mechanism of benzimidazole dyes was studied by steady-state fluorescence spectroscopy for the monoliths, powders, and compacts. The influence of the syntheses conditions was investigated by textural analysis using nitrogen adsorption isotherms.

  13. Nitrate ions as cathodic alkalization promoters for the electro-assisted deposition of sol-gel thin films

    Energy Technology Data Exchange (ETDEWEB)

    Ding Shangzhi; Liu Liang [Department of Chemistry, Yuquan Campus, Zhejiang University, Hangzhou, Zhejiang 310027 (China); Hu Jiming [Department of Chemistry, Yuquan Campus, Zhejiang University, Hangzhou, Zhejiang 310027 (China)], E-mail: kejmhu@zju.edu.cn; Zhang Jianqing; Cao Chunan [Department of Chemistry, Yuquan Campus, Zhejiang University, Hangzhou, Zhejiang 310027 (China); State Key Laboratory for Corrosion and Protection, Shenyang 110016 (China)

    2008-08-15

    Nitrate was used as a promoter to prepare dodecyltrimethoxysilane thin films on aluminum substrates. With the addition of nitrate into silane sol-gel precursors, the electro-assisted formation of silane films was facilitated, as indicated by electrochemical impedance spectroscopy, scanning electron microscopy and secondary-ion mass spectroscopy, due to the promotion in cathodic alkalization. However, an extra-high concentration of nitrate would be harmful because of the salting-out effect in precursors and the soluble nitrate remaining in silane films.

  14. Properties of Zn O/Cr thin films prepared by Sol-Gel; Propiedades de peliculas delgadas ZnO/Cr preparadas por Sol-Gel

    Energy Technology Data Exchange (ETDEWEB)

    Tirado G, S.; Olvera A, R., E-mail: tirado@esfm.ipn.mx [IPN, Escuela Superior de Fisica y Matematicas, Edificio 9, Unidad Profesional A. L. M., San Pedro Zacatenco, 07788 Mexico D. F. (Mexico)

    2014-08-15

    Zn O films and those superficially modified with chromium were deposited on substrates of soda-lime glass, using the Sol-Gel process and the repeated immersion method. Starting from dehydrated zinc acetate was prepared a solution to 0.6 M to ambient temperature in 2-methoxyethanol and monoethanolamine (Mea) stirring magnetically. The Sol was prepared with an aging to seven days and was used to grow a films group with thickness to eight immersions. These same films were superficially modified with several depositions of a chromium nitrate Sol dissolved in ethanol to low concentration. The Zn O films were structurally characterized by X-ray diffraction, its chemical composition by energy dispersive X-ray spectroscopy and its morphology by scanning electron microscopy and atomic force microscopy, as well as their optical properties by UV-vis. Of the obtained results are proposed possible applications. (author)

  15. Highly stable and imperceptible electronics utilizing photoactivated heterogeneous sol-gel metal-oxide dielectrics and semiconductors.

    Science.gov (United States)

    Jo, Jeong-Wan; Kim, Jaekyun; Kim, Kyung-Tae; Kang, Jin-Gu; Kim, Myung-Gil; Kim, Kwang-Ho; Ko, Hyungduk; Kim, Jiwan; Kim, Yong-Hoon; Park, Sung Kyu

    2015-02-18

    Incorporation of Zr into an AlOx matrix generates an intrinsically activated ZAO surface enabling the formation of a stable semiconducting IGZO film and good interfacial properties. Photochemically annealed metal-oxide devices and circuits with the optimized sol-gel ZAO dielectric and IGZO semiconductor layers demonstrate the high performance and electrically/mechanically stable operation of flexible electronics fabricated via a low-temperature solution process. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  16. Fabrication of YBa2Cu3O7-δ superconducting fibers by the sol-gel method

    International Nuclear Information System (INIS)

    Umeda, Tetsu; Kozuka, Hiromitsu; Sakka, Sumio

    1988-01-01

    High-T c superconducting oxide fibers were fabricated by the sol-gel method. An aqueous solution of metal acetates was concentrated to form a viscous sol, from which gel fibers were spun. The gel fibers, 5 to 1,000 μm in diameter, were converted to ceramic fibers by heating to 900 degree C. The fired fibers (T c (onset) of 94 K and T c (end) of 62.2 K) were rough and had porous microstructures

  17. La0.6Sr0.4Co0.2Fe0.8O3-δ nanofiber cathode for intermediate-temperature solid oxide fuel cells by water-based sol-gel electrospinning: Synthesis and electrochemical behaviour

    DEFF Research Database (Denmark)

    Enrico, Anna; Zhang, Wenjing (Angela); Traulsen, Marie Lund

    2018-01-01

    Water-based sol-gel electrospinning is employed to manufacture perovskite oxide La0.6Sr0.4Co0.2Fe0.8O3-δ (LSCF) nanofiber cathodes for intermediate-temperature solid oxide fuel cells. LSCF fibrous scaffolds are synthesized through electrospinning of a sol-gel solution employing water as the only...

  18. New Functionalized Sol-Gel Hybrid Sorbent Coating for Stir Bar Sorptive Extraction of Selected Non-Steroidal Anti Inflammatory Drugs in Human Urine Samples

    International Nuclear Information System (INIS)

    Mashkurah Abd Rahim; Wan Aini Wan Ibrahim; Zainab Ramli; Mohd Marsin Sanagi

    2015-01-01

    A new sol-gel hybrid material, methyltrimethoxysilane-cyanopropyltriethoxysilane (MTMOS-CNPrTEOS) was successfully synthesized and used as a coating material in stir bar sorptive extraction (SBSE) of selected non-steroidal anti-inflammatory drugs (NSAIDs) in urine samples. The MTMOS-CNPrTEOS hybrid was synthesized by hydrolysis and condensation of MTMOS and CNPrTEOS in the presence of trifluoroacetic acid as catalyst via sol-gel method. Several factors influencing the synthesized sol-gel hybrid MTMOS-CNPrTEOS process such as mole ratio of MTMOS-CNPrTEOS, NaOH concentrations as etching solution, etching time, coating time and water content were investigated and optimized in this study. The optimum synthesis conditions obtained were 1:1 mol ratio of MTMOS-CNPrTEOS, 1 M NaOH as etching solution, 60 min etching time, 2 h coating time and 6 mmol water. The sol-gel hybrid MTMOS-CNPrTEOS synthesized under the optimum conditions was used to determine selected NSAIDs in human urine samples using normal stacking mode capillary electrophoresis with ultraviolet detection. MTMOS-CNPrTEOS SBSE method demonstrated good linearity (60 to 20,000 μg L -1 ) with excellent coefficient of determination (r 2 > 0.9990). The sol-gel hybrid MTMOS-CNPrTEOS SBSE method showed low limit of detection (35 - 41 μg L -1 ) with good precision (RSD < 6 %, n = 3) and excellent extraction recoveries (83.5 - 98.9 %) for the selected NSAIDs. The sol-gel hybrid MTMOS-CNPrTEOS SBSE method demonstrated good potential as an alternative sorbent in SBSE method for NSAIDs. (author)

  19. Coating of the orthopaedic titanium alloys with sol-gel derived hydroxyapatite

    International Nuclear Information System (INIS)

    Milev, A.; Green, D.; Chai, C.S.; Ben-Nissan, B.

    1999-01-01

    Hydroxyapatite (HAp) is known to be both biocompatible and bioactive material, however, due to its poor mechanical properties and design limitations is not suitable for applying as a load bearing implant. This could be overcome by using appropriate metallic substrates covered with HAp, derived via different techniques. These coatings allow improved adhesion strength of the load bearing substrate to the bone, resulting in shorter healing periods as well as predictable behaviour of the implant for longer periods of time. There are different techniques of producing HAp appropriate for coating purposes. Due to the small particle size of the grains derived, sol-gel route is preferable where lower sintering temperatures are of primary importance. For better adhesion between substrate and hydroxyapatite coating, the surface of titanium substrate, in this study, was converted to titanium nitride and/or oxynitride. Sintering temperatures of 900 deg C have been used for producing crystalline HAp coatings. The control of sol-gel solutions and the analysis of the coatings were carried out using XRD, SEM and DTA techniques. Results obtained indicate high quality HAp coatings can be produced on titanium substrates especially with complex shapes that benefits over the other coating methods

  20. Fabrication of hydrophobic compressed oil palm trunk surface by sol-gel process

    Science.gov (United States)

    Muzakir, Syafiqah; Salim, Nurjannah; Huda Abu Bakar, Nurul; Roslan, Rasidi; Sin, Lim Wan; Hashim, Rokiah

    2018-04-01

    Improvement of the robustness of hydrophobic surfaces is crucial to achieving commercial applications of these surfaces in such various areas as self-cleaning, water repellency and corrosion resistance. Compressed oil palm trunk (OPT) panel is one of potential product which can be used as panelling and indoor furniture application. By adding hydrophobic properties to compressed oil palm trunk panel might increase the application of compressed oil palm trunk especially for outdoor application. In this study, fabrication is using the sol-gel technique. Sol-gel was prepared by adding ethanol with Hexadecyl Trimethyl Ammonium Bromide (CTAB) solution with Tetraethyl Orthosilicate (TEOS) with surface modification of chlorotrimethylsilane (CTMS). The surface with hydrophobic coating was undergone surface analysis with contact angle machine with the aid of software SCA 20 and the determined of the morphology of surface with scanning electron microscope (SEM). The produced compressed oil palm trunk surfaces exhibited promising hydrophobic properties with a contact angle of 104° and the relatively better mechanical robustness.

  1. Persistent superhydrophilicity of sol-gel derived nanoporous silica thin films

    International Nuclear Information System (INIS)

    Ganjoo, S; Azimirad, R; Akhavan, O; Moshfegh, A Z

    2009-01-01

    In this investigation, sol-gel synthesized nanoporous silica thin films, annealed at different temperatures, with long time superhydrophilic property have been studied. Two kinds of sol-gel silica thin films were fabricated by dip-coating of glass substrates in two different solutions; with low and high water. The transparent coated films were dried at 100 deg. C and then annealed in a temperature range of 200-500 deg. C. The average water contact angle of the silica films prepared with low water content and annealed at 300 deg. C measured about 5 deg. for a long time (6 months) without any UV irradiation. Instead, adding water into the sol resulted in silica films with an average water contact angle greater than 60 deg. Atomic force microscopic analysis revealed that the silica films prepared with low water had a rough surface (∼30 nm), while the films prepared with high water had a smoother surface (∼2 nm). Using x-ray photoelectron spectroscopy, we have shown that with a decrease in the surface water on the film, its hydrophilicity increases logarithmically.

  2. Sol-gel prepared active ternary oxide coating on titanium in cathodic protection

    Directory of Open Access Journals (Sweden)

    VLADIMIR V. PANIC

    2007-12-01

    Full Text Available The characteristics of a ternary oxide coating, on titanium, which consisted of TiO2, RuO2 and IrO2 in the molar ratio 0.6:0.3:0.1, calculated on the metal atom, were investigated for potential application for cathodic protection in a seawater environment. The oxide coatings on titanium were prepared by the sol gel procedure from a mixture of inorganic oxide sols, which were obtained by forced hydrolysis of metal chlorides. The morphology of the coating was examined by scanning electron microscopy. The electrochemical properties of activated titanium anodes were investigated by cyclic voltammetry and polarization measurements in a H2SO4- and NaCl-containing electrolyte, as well as in seawater sampled on the Adriatic coast in Tivat, Montenegro. The anode stability during operation in seawater was investigated by the galvanostatic accelerated corrosion stability test. The morphology and electrochemical characteristics of the ternary coating are compared to that of a sol-gel-prepared binary Ti0.6Ru0.4O2 coating. The activity of the ternary coating was similar to that of the binary Ti0.6Ru0.4O2 coating in the investigated solutions. However, the corrosion stability in seawater is found to be considerably greater for the ternary coating.

  3. Preparation of Natural Rubber (NR) Based Nano-Sized Materials Using Sol-Gel Technique

    International Nuclear Information System (INIS)

    Dahlan Mohd; Mahathir Mohamed

    2011-01-01

    The objectives of this project are to prepare nano-sized natural rubber-based hybrid coating material by sol-gel technique; to explore the possibility of producing ENR-Si (epoxidized natural rubber-silica) cramer with toughening effects; and to use it in radiation curing of surface coating. Since early 1960s Malaysia has introduced various forms of value-added natural rubber such as Standard Malaysian Rubber (SMR), methylmethacrylate-grafted natural rubber (MG rubber), followed by liquid natural rubber and epoxidized natural rubber (ENR). Products such as liquid epoxidized natural rubber acrylate (LENRA) and thermoplastic natural rubber (TPNR) are still on-going research projects in Nuclear Malaysia. The former has strong possibility to be used as radiation-sensitive comparabilities in TPNR blends, besides its original purpose for example in radiation curing of surface coating. But earlier findings indicated that, to make it (as for surface coating) more effective, reinforcement system is needed to be introduced. Strong candidate is silica by sol-gel technique, since common reinforcement filler for example carbon black has drawbacks in this particular case. This technique was introduced in late 1960s to produce metal oxides such as silica and titanium oxides in solution. (author)

  4. Enhanced Red Emission in Ultrasound-Assisted Sol-Gel Derived ZnO/PMMA Nanocomposite

    Directory of Open Access Journals (Sweden)

    Van-Tuan Mai

    2018-01-01

    Full Text Available Cost-effective methods for preparing ZnO nanostructures are of importance for the deployment of ZnO in many applications including n-type conduits, catalysts, nanophosphor, and optoelectronics. Herein, we present a room-temperature sol-gel method with the aid of ultrasonication to prepare white-emitting ZnO nanoparticles (NPs. X-ray diffraction and electron microscopic analyses revealed that the size and shape of ZnO NPs can be controlled simply by changing the concentration of the Zn precursor. The ZnO NPs had a broad photoluminescence emission, ranging from 450 nm to 800 nm, while their composite in PMMA matrix showed an enhancement in the red region induced by ZnO-PMMA interfacial band-bending effects. The results demonstrated herein promise a simple tool for control over size, shape, and emission of ZnO materials for diverse applications.

  5. Impact of temperature on zinc oxide particle size by using sol-gel process

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Keanchuan, E-mail: lee.kc@petronas.com.my; Ching, Dennis Ling Chuan, E-mail: dennis.ling@petronas.com.my [Fundamental and Applied Sciences Department, Universiti Teknologi PETRONAS, 31750 Tronoh, Perak (Malaysia); Saipolbahri, Zulhilmi Akmal bin, E-mail: zulhilmiakmal@gmail.com [Geoscience and Petroleum Engineering Department, Universiti Teknologi PETRONAS, 31750 Tronoh, Perak (Malaysia); Guan, Beh Hoe, E-mail: beh.hoeguan@petronas.com.my, E-mail: hassan.soleimani@petronas.com.my; Soleimani, Hassan, E-mail: beh.hoeguan@petronas.com.my, E-mail: hassan.soleimani@petronas.com.my

    2014-10-24

    Zinc oxide (ZnO) nanoparticles were prepared and synthesized via sol-gel method, by using citric acid as a precursor. The impact of annealing on the particle size was investigated. Based on the results from the Thermogravimetric Analysis (TGA), three different annealing temperature which is 500, 600 and 700 °C were chosen followed by the characterization of the ZnO nanoparticle by using Powder X-Ray Diffraction (PXRD), Transmission Electron Microscopy (TEM) and Field Emission Scanning Electron Microscopy (FESEM). Results showed that the crystallite size estimated from PXRD increased with the annealing temperature which was hexagonal structure for ZnO. TEM further revealed the same tendency which the Zn NPs size also increased with the annealing temperature.

  6. Impact of temperature on zinc oxide particle size by using sol-gel process

    International Nuclear Information System (INIS)

    Lee, Keanchuan; Ching, Dennis Ling Chuan; Saipolbahri, Zulhilmi Akmal bin; Guan, Beh Hoe; Soleimani, Hassan

    2014-01-01

    Zinc oxide (ZnO) nanoparticles were prepared and synthesized via sol-gel method, by using citric acid as a precursor. The impact of annealing on the particle size was investigated. Based on the results from the Thermogravimetric Analysis (TGA), three different annealing temperature which is 500, 600 and 700 °C were chosen followed by the characterization of the ZnO nanoparticle by using Powder X-Ray Diffraction (PXRD), Transmission Electron Microscopy (TEM) and Field Emission Scanning Electron Microscopy (FESEM). Results showed that the crystallite size estimated from PXRD increased with the annealing temperature which was hexagonal structure for ZnO. TEM further revealed the same tendency which the Zn NPs size also increased with the annealing temperature

  7. Structural transformation of nanocrystalline titania by sol-gel and the growth kinetics of crystallites

    International Nuclear Information System (INIS)

    Hu Linhua; Dai Songyuan; Wang Kongjia

    2002-05-01

    Structural transformation of nanocrystalline titania prepared by sol-gel with hydrolysis precursor titanium isopropoxide was investigated. At the same time, the growth kinetics of titania powders was also studied here. It was found that the grain size of the powders increased slowly with autoclave heating temperature up to 230 degree C, when hydrolysis pH was 0.9, but grew rapidly when heating temperature was higher that 230 degree C. The activation energies for growth of anatase crystallites in two temperature regions were calculated to be 18.5 kJ/mol and 59.7 kJ/mol respectively. The X-ray diffraction results show that the transformation from anatase phase to rutile phase starts at 230 degree C and structural transformation finished when temperature raises to 270 degree C, which is a temperature much more lower than that of the transformation by conventional literature reports

  8. Sol-Gel Synthesis and Characterization of Selected Transition Metal Nano-Ferrites

    Directory of Open Access Journals (Sweden)

    Aurelija GATELYTĖ

    2011-09-01

    Full Text Available In the present work, the sinterability and formation of nanosized yttrium iron garnet (Y3Fe5O12, yttrium perovskite ferrite (YFeO3, cobalt, nickel and zinc iron spinel (CoFe2O4, NiFe2O4 and ZnFe2O4, respectively powders by an aqueous sol-gel processes are investigated. The metal ions, generated by dissolving starting materials of transition metals in the diluted acetic acid were complexed by 1,2-ethanediol to obtain the precursors for the transition metal ferrite ceramics. The phase purity of synthesized nano-compounds was characterized by infrared spectroscopy (IR and powder X-ray diffraction analysis (XRD. The microstructural evolution and morphological features of obtained transition metal ferrites were studied by scanning electron microscopy (SEM.http://dx.doi.org/10.5755/j01.ms.17.3.598

  9. Sol-gel synthesis and densification of aluminoborosilicate powders. Part 1: Synthesis

    Science.gov (United States)

    Bull, Jeffrey; Selvaduray, Guna; Leiser, Daniel

    1992-01-01

    Aluminoborosilicate powders high in alumina content were synthesized by the sol-gel process utilizing various methods of preparation. Properties and microstructural effects related to these syntheses were examined. After heating to 600 C for 2 h in flowing air, the powders were amorphous with the metal oxides comprising 87 percent of the weight and uncombusted organics the remainder. DTA of dried powders revealed a T(sub g) at approximately 835 C and an exotherm near 900 C due to crystallization. Powders derived from aluminum secbutoxide consisted of particles with a mean diameter 5 microns less than those from aluminum isopropoxide. Powders synthesized with aluminum isopropoxide produced agglomerates comprised of rod shaped particulates while powders made with the secbutoxide precursor produced irregular glassy shards. Compacts formed from these powders required different loadings for equivalent densities according to the method of synthesis.

  10. Structural properties and gas sensing behavior of sol-gel grown nanostructured zinc oxide

    Energy Technology Data Exchange (ETDEWEB)

    Rajyaguru, Bhargav; Gadani, Keval; Kansara, S. B.; Pandya, D. D.; Shah, N. A.; Solanki, P. S., E-mail: piyush.physics@gmail.com [Department of Physics, Saurashtra University, Rajkot – 360 005 (India); Rathod, K. N.; Solanki, Sapana [Department of Physics, Saurashtra University, Rajkot – 360 005 (India); V.V.P. Engineering College, Gujarat Technological University, Rajkot – 360 005 (India)

    2016-05-06

    In this communication, we report the results of the studies on structural properties and gas sensing behavior of nanostructured ZnO grown using acetone precursor based modified sol-gel technique. Final product of ZnO was sintered at different temperatures to vary the crystallite size while their structural properties have been studied using X-ray diffraction (XRD) measurement performed at room temperature. XRD results suggest the single phasic nature of all the samples and crystallite size increases from 11.53 to 20.96 nm with increase in sintering temperature. Gas sensing behavior has been studied for acetone gas which indicates that lower sintered samples are more capable to sense the acetone gas and related mechanism has been discussed in the light of crystallite size, crystal boundary density, defect mechanism and possible chemical reaction between gas traces and various oxygen species.

  11. SiO2 sol-gel films after ammonia and heat two-step treatments

    International Nuclear Information System (INIS)

    Zhang Chunlai; Wang Biyi; Tian Dongbin; Yin Wei; Jiang Xiaodong; Yuan Xiaodong; Yan Lianghong; Zhang Hongliang; Zhao Songnan; Lv Haibing

    2008-01-01

    SiO 2 thin films were deposited using tetraethoxylsilane as precursor, ammonia as catalyst on K9 glass by sol-gel method. These films were post-treated by ammonia and heat. The properties of the coatings were characterized by ellipsometer, UV-vis spectrophotometry, FTIR-spectroscopy, scanning probe microscope and contact angle measurement apparatus. The resuits indicate that the thickness of the films with ammonia and heat treatment tend to decrease. Both the refractive index and water contact angle increase after ammonia treatment. However, they both decrease after heat treatment. The former increases by 0.236 for the first step, then decreases by 0.202 for the second. The latter increases to 58.92 degree, then decreases to 38.07 degree. The transmittance of the coatings turn to be better and continuously shift to short wave by UV-vis spectrophotometry. The surface becomes smoother by AFM after the two-step treatment. (authors)

  12. Characterization of selenium doped silica glasses synthesized by sol-gel method

    International Nuclear Information System (INIS)

    Kobayashi, R.A.; Toffoli, S.M.

    2012-01-01

    Selenium is a rare element in nature. It is used in the food, pharmaceutical, and glass industries. In commercial glasses, selenium is the element responsible for most of the pink or light red color, but its effect is primarily dependent on the oxidation state of the element in the glassy matrix. Besides, selenium is highly volatile, and as high as 80 wt% may be lost in the furnace during the industrial glass elaboration. The sol– gel method yields synthesized materials of high purity and homogeneity, and uses low processing temperatures. Samples of silica glass were obtained by sol-gel method, incorporating precursors of selenium, with the main objective of reducing selenium losses during its heating. The results of optical absorption, XRD and thermal analysis (TGA, DSC) of the glasses are presented and discussed. (author)

  13. Iron porphyrins doped sol-gel glasses: a chemometric study

    International Nuclear Information System (INIS)

    Sacco, Herica C.; Vidoto, Ednalva A.; Nascimento, Otaciro R.

    2000-01-01

    This paper describes the optimized conditions for preparation of iron porphyrin-template doped silica Fe PDS-template) obtained by the sol-gel process. The following porphyrins (Fe P) were used: Fe TFPP Cl, Fe TDCSPP(Na) 4 Cl and Fe TCPP(Na) 4 Cl. Pyridine or 4-phenylimidazole was used as template. The variables that present significant influence on iron porphyrin loading on xerogel were identified and the values that maximize the iron porphyrin loading on xerogel were established . The variables (Solvent volume, fractional factorial design in two levels, 2 5-1 type, generating 16 total experiments for each Fe P studied. (author)

  14. Iron porphyrins doped sol-gel glasses: a chemometric study

    Energy Technology Data Exchange (ETDEWEB)

    Sacco, Herica C.; Vidoto, Ednalva A.; Nascimento, Otaciro R. [Soap Paulo Univ (USP), Sao Carlos (Brazil). Inst. de Fisica; Biazzotto, Juliana C.; Serra, Osvaldo A.; Iamamoto, Yassuko [Sao Paulo Univ. (USP), Ribeirao Preto, SP (Brazil). Faculdade de Filosofia, Ciencias e Letras; Ciuffi, Katia J.; Mello, Cesar A.; Oliveira, Daniela C. de [Universidade de Franca , SP (Brazil)

    2000-07-01

    This paper describes the optimized conditions for preparation of iron porphyrin-template doped silica Fe (PDS-template) obtained by the sol-gel process. The following porphyrins (Fe P) were used: Fe TFPP Cl, Fe TDCSPP(Na){sub 4}Cl and Fe TCPP(Na){sub 4} Cl. Pyridine or 4-phenylimidazole was used as template. The variables that present significant influence on iron porphyrin loading on xerogel were identified and the values that maximize the iron porphyrin loading on xerogel were established. The variables Solvent volume, fractional factorial design in two levels, 2{sup 5-1} type, generating 16 total experiments for each Fe P studied. (author)

  15. Electrochemical redox reactions in solvated silica sol-gel glass

    International Nuclear Information System (INIS)

    Opallo, M.

    2002-01-01

    The studies of electrochemical redox reactions in solvated silica sol-gel glass were reviewed. The methodology of the experiments with emphasis on the direct preparation of the solid electrolyte and the application ultra microelectrodes was described. Generally, the level of the electrochemical signal is not much below that observed in liquid electrolyte. The current depends on time elapsed after gelation, namely the longer time, the smaller current. The differences between electrochemical behaviour of the redox couples in monoliths and thin layers were described. (author)

  16. Synthesis of lithium doped zinc oxide by sol gel

    International Nuclear Information System (INIS)

    Meziane, K; Elhichou, A; Elhamidi, A; Almaggoussi, A; CHHIBA, M

    2016-01-01

    Li-doped ZnO thin films were prepared by sol-gel method and deposed on glass substrate using spin coating technique. The effects of Li on structural and optical properties were investigated. The X-ray diffraction (XRD) analysis reveals that Li incorporation leads to the great improvement of the crystalline quality of ZnO thin films. Scanning electron microscopy (SEM) images showed that nanowires are aligned nearly perpendicular to the substrate plane and are affected significantly by Li incorporation. The optical transmission of the films was higher than 80% in the visible region. It is found that the optical gap and the refractive index remain practically constant. (paper)

  17. Characterization of a sol-gel-entrapped artificial receptor

    Science.gov (United States)

    Dunbar, Richard A.; Narang, Upvan; Prasad, Paras N.; Bright, Frank V.

    1993-04-01

    We report on the development, characterization, and photophysics of a new fiber-optic-based sensor which uses a sol-gel entrapped recognition element. The recognition element is modified (beta) -cyclodextrin to which we have added a short tether (glycine) and a fluorophore (dansyl). This recognition element forms an intramolecular complex, and the dansyl group can include within the cyclodextrin cavity. Non-fluorescent analytes, that bind to the cyclodextrin cavity, can effectively displace the included dansyl group and result in a measurable change in signal. We report on the detection limits, dynamic range, and photophysics (i.e., transduction mechanism) of this new sensor.

  18. Sol-gel synthesis and characterization of lithiummolybdosilicate glass

    International Nuclear Information System (INIS)

    Prakash, I.; Nallamuthu, N.; Muralidharan, P.; Satyanarayana, N.; Venkateswarlu, M.; Balasubramanyam, S.

    2008-01-01

    10 % Li 2 O + 0.9 % MoO 3 + 89.1 %SiO 2 (LMS) glassy sample was prepared using Sol-gel process and was characterized by powder X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Differential scanning calorimetry (DSC) techniques. The ion conducting mechanism was studied through impedance technique at various temperatures. The conductivity of the sample was found to be 4.1257 x 10 -8 Scm -1 at 613 K. The activation energy was calculated from the log (sT) vs. 1000/T plot and it was found to be (0.1466 ± 0.012) eV. (author)

  19. Moment scaling at the sol-gel transition

    International Nuclear Information System (INIS)

    Botet, R.

    1998-01-01

    Two standard models of sol-gel transition are revisited here from the point of view of their fluctuations in various moments of both the mass-distribution and the gel-mass. Bond-percolation model is an at-equilibrium system and undergoes a static second-order phase transition, while Monte-Carlo Smoluchowski model is an off-equilibrium one and shows a dynamical critical phenomenon. It is shown that the macroscopic quantities can be splitted into the three classes with different scaling properties of their fluctuations, depending on whether they correspond to: (i) non-critical quantities, (ii) critical quantities or to (iii) an order parameter. (author)

  20. Equipment for production of hydrogel by sol-gel method

    International Nuclear Information System (INIS)

    Urbanek, V.

    1975-01-01

    The method of uranyl gel preparation is described by the sol-gel process of the internal gelation type. A laboratory-scale equipment with an output of 1.5 kg of gel per hour was built at the Nuclear Research Institute, Rez; the diameter of the microspheres produced may vary between 0.5 and 4.0 mm. The reliability of the equipment was verified by producing several tens of kilograms of uranyl gels and of gels based on other non-nuclear materials. (author)

  1. Modified sol-gel coatings for biotechnological applications

    Energy Technology Data Exchange (ETDEWEB)

    Beganskiene, A [Department of General and Inorganic Chemistry, Vilnius University, Vilnius LT-03225 (Lithuania); Raudonis, R [Department of General and Inorganic Chemistry, Vilnius University, Vilnius LT-03225 (Lithuania); Jokhadar, S Zemljic [Faculty of Medicine, Institute of Biophysics, Lipiceva 2, Ljubljana SI-1000 (Slovenia); Batista, U [Faculty of Medicine, Institute of Biophysics, Lipiceva 2, Ljubljana SI-1000 (Slovenia); Kareiva, A [Department of General and Inorganic Chemistry, Vilnius University, Vilnius LT-03225 (Lithuania)

    2007-12-15

    The modified sol-gel derived silica coatings were prepared and characterized. The amino and methyl groups were introduced onto the colloidal silica. The silica coatings with different wettability properties: coloidal silica (water contact angle 17 deg.), polysiloxane (61 deg.), methyl-modified (158 deg. and 46 deg.) coatings samples were tested for CaCo-2 cells proliferation. Methyl-modified coating (46 deg.) proved to be the best substrate for cell proliferation. CaCo-2 cell proliferation two days post seeding was significantly faster on almost laminine, fibronectin and collagen-1 coated samples compared to corresponding controls.

  2. Integrating nanohybrid membranes of reduced graphene oxide: chitosan: silica sol gel with fiber optic SPR for caffeine detection

    Science.gov (United States)

    Kant, Ravi; Tabassum, Rana; Gupta, Banshi D.

    2017-05-01

    Caffeine is the most popular psychoactive drug consumed in the world for improving alertness and enhancing wakefulness. However, caffeine consumption beyond limits can result in lot of physiological complications in human beings. In this work, we report a novel detection scheme for caffeine integrating nanohybrid membranes of reduced graphene oxide (rGO) in chitosan modified silica sol gel (rGO: chitosan: silica sol gel) with fiber optic surface plasmon resonance. The chemically synthesized nanohybrid membrane forming the sensing route has been dip coated over silver coated unclad central portion of an optical fiber. The sensor works on the mechanism of modification of dielectric function of sensing layer on exposure to analyte solution which is manifested in terms of red shift in resonance wavelength. The concentration of rGO in polymer network of chitosan and silica sol gel and dipping time of the silver coated probe in the solution of nanohybrid membrane have been optimized to extricate the supreme performance of the sensor. The optimized sensing probe possesses a reasonably good sensitivity and follows an exponentially declining trend within the entire investigating range of caffeine concentration. The sensor boasts of an unparalleled limit of detection value of 1.994 nM and works well in concentration range of 0-500 nM with a response time of 16 s. The impeccable sensor methodology adopted in this work combining fiber optic SPR with nanotechnology furnishes a novel perspective for caffeine determination in commercial foodstuffs and biological fluids.

  3. Influence of initial sulfur content in precursor solution for the growth of molybdenum disulfide

    Science.gov (United States)

    Tan, A. L.; Ng, S. S.; Abu Hassan, H.

    2018-04-01

    This work investigated the influence of initial sulfur content in the precursor solution for the growth of molybdenum disulfide (MoS2) films by thermal vapour sulfurization (TVS) with sol-gel spin coating as pre-deposition technique. The early introduction of sulfur shows the presence of grains are uniformly distributed and homogeneous on the surface of the film. MoS2 (002) planes are detected for both films with and without initial sulfur conditions, however, the presence of initial sulfur contents gives slightly higher intensity of diffraction peak. Two phonon modes for MoS2, namely the E2g 1 (in-plane) and the A1g (out-of plane), are well detected from which the frequency difference of Raman peaks between E2g 1 and A1g suggest the grown MoS2 consisted of multi-layers. There is a slight shift of E2g 1 which is caused by the carbon impurities but no shift for A1g. Besides, MoS2 film with the presence of initial sulfur content shows better crystal as indicated by its narrower Raman peaks linewidth. Two broad absorption peaks of MoS2 are detected at 614nm and 665nm. Hence, the early introduction of sulfur content in prepared precursor solution is one way of optimizing the growth of MoS2 films.

  4. Sol-gel based sensor for selective formaldehyde determination

    Energy Technology Data Exchange (ETDEWEB)

    Bunkoed, Opas [Trace Analysis and Biosensor Research Center, Prince of Songkla University, Hat Yai, Songkhla 90112 (Thailand); Department of Chemistry and Center for Innovation in Chemistry, Faculty of Science, Prince of Songkla University, Hat Yai, Songkhla 90112 (Thailand); Davis, Frank [Cranfield Health, Cranfield University, Bedford MK43 0AL (United Kingdom); Kanatharana, Proespichaya, E-mail: proespichaya.K@psu.ac.th [Trace Analysis and Biosensor Research Center, Prince of Songkla University, Hat Yai, Songkhla 90112 (Thailand); Department of Chemistry and Center for Innovation in Chemistry, Faculty of Science, Prince of Songkla University, Hat Yai, Songkhla 90112 (Thailand); Thavarungkul, Panote [Trace Analysis and Biosensor Research Center, Prince of Songkla University, Hat Yai, Songkhla 90112 (Thailand); Department of Physics, Faculty of Science, Prince of Songkla University, Hat Yai, Songkhla 90112 (Thailand); Higson, Seamus P.J., E-mail: s.p.j.higson@cranfield.ac.uk [Cranfield Health, Cranfield University, Bedford MK43 0AL (United Kingdom)

    2010-02-05

    We report the development of transparent sol-gels with entrapped sensitive and selective reagents for the detection of formaldehyde. The sampling method is based on the adsorption of formaldehyde from the air and reaction with {beta}-diketones (for example acetylacetone) in a sol-gel matrix to produce a yellow product, lutidine, which was detected directly. The proposed method does not require preparation of samples prior to analysis and allows both screening by visual detection and quantitative measurement by simple spectrophotometry. The detection limit of 0.03 ppmv formaldehyde is reported which is lower than the maximum exposure concentrations recommended by both the World Health Organisation (WHO) and the Occupational Safety and Health Administration (OSHA). This sampling method was found to give good reproducibility, the relative standard deviation at 0.2 and 1 ppmv being 6.3% and 4.6%, respectively. Other carbonyl compounds i.e. acetaldehyde, benzaldehyde, acetone and butanone do not interfere with this analytical approach. Results are provided for the determination of formaldehyde in indoor air.

  5. Sol-gel based sensor for selective formaldehyde determination

    International Nuclear Information System (INIS)

    Bunkoed, Opas; Davis, Frank; Kanatharana, Proespichaya; Thavarungkul, Panote; Higson, Seamus P.J.

    2010-01-01

    We report the development of transparent sol-gels with entrapped sensitive and selective reagents for the detection of formaldehyde. The sampling method is based on the adsorption of formaldehyde from the air and reaction with β-diketones (for example acetylacetone) in a sol-gel matrix to produce a yellow product, lutidine, which was detected directly. The proposed method does not require preparation of samples prior to analysis and allows both screening by visual detection and quantitative measurement by simple spectrophotometry. The detection limit of 0.03 ppmv formaldehyde is reported which is lower than the maximum exposure concentrations recommended by both the World Health Organisation (WHO) and the Occupational Safety and Health Administration (OSHA). This sampling method was found to give good reproducibility, the relative standard deviation at 0.2 and 1 ppmv being 6.3% and 4.6%, respectively. Other carbonyl compounds i.e. acetaldehyde, benzaldehyde, acetone and butanone do not interfere with this analytical approach. Results are provided for the determination of formaldehyde in indoor air.

  6. Nanostructured energetic materials derived from sol-gel chemistry

    International Nuclear Information System (INIS)

    Simpson, R L; Tillotson, T M; Hrubesh, L W; Gash, A E

    2000-01-01

    Initiation and detonation properties are dramatically affected by an energetic material's microstructural properties. Sol-gel chemistry allows intimacy of mixing to be controlled and dramatically improved over existing methodologies. One material goal is to create very high power energetic materials which also have high energy densities. Using sol-gel chemistry we have made a nanostructured composite energetic material. Here a solid skeleton of fuel, based on resorcinol-formaldehyde, has nanocrystalline ammonium perchlorate, the oxidizer, trapped within its pores. At optimum stoichiometry it has approximately the energy density of HMX. Transmission electron microscopy indicated no ammonium perchlorate crystallites larger than 20 nm while near-edge soft x-ray absorption microscopy showed that nitrogen was uniformly distributed, at least on the scale of less than 80 nm. Small-angle neutron scattering studies were conducted on the material. Those results were consistent with historical ones for this class of nanostructured materials. The average skeletal primary particle size was on the order of 2.7 nm, while the nanocomposite showed the growth of small 1 nm size crystals of ammonium perchlorate with some clustering to form particles greater than 10 nm

  7. Dielectric Properties of Sol-Gel Derived Barium Strontium Titanate and Microwave Sintering of Ceramics

    Science.gov (United States)

    Selmi, Fathi A.

    This thesis consists of two areas of research: (1) sol-gel processing of Ba_{rm 1-x}Sr_{rm x} TiO_3 ceramics and their dielectric properties measurement; and (2) microwave versus conventional sintering of ceramics such as Al_2 O_3, Ba_{ rm 1-x}Sr_{rm x}TiO_3, Sb-doped SnO _2 and YBa_2Cu _3O_7. Sol-gel powders of BaTiO_3, SrTiO_3, and their solid solutions were synthesized by the hydrolysis of titanium isopropoxide and Ba and Sr methoxyethoxides. The loss tangent and dielectric constant of both sol-gel and conventionally prepared and sintered Ba_{rm 1-x}Sr _{rm x}TiO _3 ceramics were investigated at high frequencies. The sol-gel prepared ceramics showed higher dielectric constant and lower loss compared to those prepared conventionally. Ba _{rm 1-x}Sr _{rm x}TiO_3 ceramics were tunable with applied bias, indicating the potential use of this material for phase shifter applications. Porous Ba_{0.65}Sr _{0.35}TiO_3 was also investigated to lower the dielectric constant. Microwave sintering of alpha -Al_2O_3 and SrTiO_3 was investigated using an ordinary kitchen microwave oven (2.45 GHz; 600 Watts). The use of microwaves with good insulation of alpha -Al_2O_3 and SrTiO_3 samples resulted in their rapid sintering with good final densities of 96 and 98% of the theoretical density, respectively. A comparison of grain size for conventionally and microwave sintered SrTiO_3 samples did not show a noticeable difference. However, the grain size of microwave sintered alpha-Al_2O _3 was found to be larger than that of conventionally sintered sample. These results show that rapid sintering of ceramics can be achieved by using microwave radiation. The sintering behavior of coprecipitated Sb-doped SnO_2 was investigated using microwave power absorption. With microwave power, samples were sintered at 1450^circC for 20 minutes and showed a density as high as 99.9% of theoretical. However, samples fired in a conventional electric furnace at the same temperature for 4 hours showed only

  8. Preparation of Flame Retardant Polyacrylonitrile Fabric Based on Sol-Gel and Layer-by-Layer Assembly.

    Science.gov (United States)

    Ren, Yuanlin; Huo, Tongguo; Qin, Yiwen; Liu, Xiaohui

    2018-03-23

    This paper aims to develop a novel method, i.e., sol-gel combined with layer-by-layer assembly technology, to impart flame retardancy on polyacrylonitrile (PAN) fabrics. Silica-sol was synthesized via the sol-gel process and acted as cationic solution, and phytic acid (PA) was used as the anionic medium. Flame-retardant-treated PAN fabric (FR-PAN) could achieve excellent flame retardancy with 10 bilayer (10BL) coating through layer-by-layer assembly. The structure of the fabrics was characterized by X-ray photoelectron spectroscopy (XPS) and Fourier transform infrared spectroscopy (FTIR). The thermal stability and flame retardancy were evaluated by thermogravimetric (TG) analysis, cone calorimetry (CC) and limiting oxygen index (LOI). The LOI value of the coated fabric was up to 33.2 vol % and the char residue at 800 °C also increased to 57 wt %. Cone calorimetry tests revealed that, compared to the control fabric, the peak of heat release rate (PHRR) and total heat release (THR) of FR-PAN decreased by 66% and 73%, respectively. These results indicated that sol-gel combined with layer-by-layer assembly technique could impart PAN fabric with satisfactory flame-retardant properties, showing an efficient flame retardant strategy for PAN fabric.

  9. High Refractive Organic–Inorganic Hybrid Films Prepared by Low Water Sol-Gel and UV-Irradiation Processes

    Directory of Open Access Journals (Sweden)

    Hsiao-Yuan Ma

    2016-03-01

    Full Text Available Organic-inorganic hybrid sols (Ti–O–Si precursor were first synthesized by the sol-gel method at low addition of water, and were then employed to prepare a highly refractive hybrid optical film. This film was obtained by blending the Ti–O–Si precursor with 2-phenylphenoxyethyl acrylate (OPPEA to perform photo-polymerization by ultraviolet (UV irradiation. Results show that the film transparency of poly(Ti–O–Si precursor-co-OPPEA film is higher than that of a pure poly(Ti–O–Si precursor film, and that this poly(Ti–O–Si precursor-co-OPPEA hybrid film exhibits a high transparency of ~93.7% coupled with a high refractive index (n of 1.83 corresponding to a thickness of 2.59 μm.

  10. Thermal stability of a modified sol-gel derived hydroxyapatite nanopowders

    Science.gov (United States)

    Herradi, S.; El Bali, B.; Khaldi, M.; Lachkar, M.

    2017-03-01

    Hydroxyapatite Ca10(PO4)6(OH)2 (HA) powder was successfully synthesized by a modified sol-gel method using a solution of calcium nitrate in ethanol, along with a solution of diammonium hydrogen phosphate in water and NH4OH as starting materials. The Ca/P molar ratio was maintained at 1.67. The powder was subjected to furnace and microwave heating to compare the decomposition of HA and study the crystallite sizes. It was found that microwave heated powders were pure HAP up to 230°C with absence of secondary phases. However, XRD patterns show that furnace heated powders convert completely to β-TCP when treated at 750°C and 1000°C. This result was confirmed by the absence of hydroxyl bands in the FT-IR spectra for these temperatures.

  11. Production of TiO_2 particles by sol-gel ultrasound assisted for photocatalytic applications

    International Nuclear Information System (INIS)

    Martinez Rojas, Vanessa; Solis Veliz, Jose; Gomez Leon, Monica; Matejova, Lenka; Lopez, Alcides; Cruz, Gerardo J.

    2015-01-01

    Synthesis of TiO_2 particles was made by sol-gel technique assisted of ultrasonic radiation from an alcoholic solution of titanium isopropoxide. Then was subjected to a heat treatment in air at 350 °C for 1 h. X-ray diffraction and transmission electron microscopy confirmed that the size of the crystalline domains is between 10 and 37 nm. Infrared spectroscopy study confirms the presence of -OH groups on the surface of TiO_2. Modification of the morphology and surface area, due to the influence of exposure time to the ultrasonic radiation, is evidenced by studies of SEM and BET respectively. Properties of TiO_2 obtained were studied by monitoring the degradation of solutions of methyl orange in the presence of UV-A radiation. It was observed that larger the ultrasonic radiation exposure during the TiO_2 synthesis larger the constant velocity for the photocatalytic reaction for the methyl orange. (author)

  12. Obtención de Cordierita por Sol-Gel a partir de fuentes nacionales cubanas

    Directory of Open Access Journals (Sweden)

    Pacheco, P.

    2003-10-01

    Full Text Available For cordierite synthesis through the Sol-Gel method, the sodium silicate obtained from the dissolution of a solid residue coming from the aluminum sulfate production based on kaolin, was used. The sources of magnesium and aluminum were obtained using the technologies previously developed by CIPIMM. The elements were mixed in a determined order and quantity to obtain a Gel with cordierite stechiometry. The gel was washed and dried and briquettes were made to treat them at different temperatures, obtaining cordierite in a major phase at 1200ºC. This was checked through the X-Ray diffraction analysis of the products coming from the thermical treatment. The method used when compared to the traditional ones, permitted to reduce crystallization temperature, obtaining more dense products and clean technology.

    Para la síntesis de la Cordierita por el método de Sol-Gel se utilizó, el silicato de sodio, obtenido de la disolución de un residuo sólido proveniente de la producción de sulfato de aluminio a partir de caolín. Los precursores de magnesio y aluminio fueron obtenidos utilizando las tecnologías previamente desarrolladas por el CIPIMM. Los materiales fueron mezclados en un orden y cantidad determinada hasta obtener el Gel con estequiometría de cordierita. El gel fue lavado, secado, briqueteado y tratado térmicamente a diferentes temperaturas, lográndose cordierita en fase mayoritaria a los 1200 ºC, lo cual fue corroborado mediante el análisis por difracción de rayos X de los productos del tratamiento térmico. El método utilizado comparado con los tradicionales permitió reducir la temperatura de cristalización, obtener productos más densificados y tecnología limpia.

  13. Synthesis and characterization of uniform silica nanoparticles on nickel substrate by spin coating and sol-gel method

    Science.gov (United States)

    Ngoc Thi Le, Hien; Jeong, Hae Kyung

    2014-01-01

    Spin coating and sol-gel methods are proposed for the preparation of silica nanoparticles on a nickel substrate using silicon tetrachloride, 2-methoxyethanol, and four different types of alkaline solutions. The effects of the type of alkaline solution, concentration of silica solution, and speed of spin coating on the properties of silica nanoparticles are investigated systematically. Uniform spherical shape of silica nanoparticles on Ni with the smallest size are obtained with sodium carbonate among the alkaline solutions after stirring at 70 °C for 6 h and spin-coating at 7000 rpm. Physical and electrochemical properties of the silica particles are investigated.

  14. Sol-gel based oxidation catalyst and coating system using same

    Science.gov (United States)

    Watkins, Anthony N. (Inventor); Leighty, Bradley D. (Inventor); Oglesby, Donald M. (Inventor); Patry, JoAnne L. (Inventor); Schryer, Jacqueline L. (Inventor)

    2010-01-01

    An oxidation catalyst system is formed by particles of an oxidation catalyst dispersed in a porous sol-gel binder. The oxidation catalyst system can be applied by brush or spray painting while the sol-gel binder is in its sol state.

  15. Bactericidal micron-thin sol-gel films prevent pin tract and periprosthetic infection.

    Science.gov (United States)

    Qu, Haibo; Knabe, Christine; Burke, Megan; Radin, Shula; Garino, Jonathan; Schaer, Thomas; Ducheyne, Paul

    2014-08-01

    Orthopedic injuries constitute the majority of wounds sustained by U.S. soldiers in recent conflicts. The risk of infection is considerable with fracture fixation devices. In this pilot study, we examined the use of unique bactericidal micron-thin sol-gel films on fracture fixation devices and their ability to prevent and eradicate infections. External fixation was studied with micron-thin sol-gel coated percutaneous pins releasing triclosan and inserted medially into rabbit tibiae. A total of 11 rabbits received percutaneous pins that were either uncoated or sol-gel/triclosan coated. Internal fracture fixation was also studied using sol-gel coated intramedullary (IM) nails releasing vancomycin in the intramedullary tibiae. Six sheep received IM nails that were coated with a sol-gel film that either contained vancomycin or did not contain vancomycin. All animals were challenged with Staphylococcus aureus around the implant. Animals were euthanized at 1 month postoperative. Rabbits receiving triclosan/sol-gel coated percutaneous pins did not show signs of infection. Uncoated percutaneous pins had a significantly higher infection rate. In the sheep study, there were no radiographic signs of osteomyelitis with vancomycin/sol-gel coated IM nails, in contrast to the observations in the control cohort. Hence, the nanostructured sol-gel controlled release technology offers the promise of a reliable and continuous delivery system of bactericidals from orthopedic devices to prevent and treat infection. Reprint & Copyright © 2014 Association of Military Surgeons of the U.S.

  16. Radiation hardening in sol-gel derived Er3+-doped silica glasses

    International Nuclear Information System (INIS)

    Hari Babu, B.; León Pichel, Mónica; Ollier, Nadège; El Hamzaoui, Hicham; Bigot, Laurent; Savelii, Inna; Bouazaoui, Mohamed; Poumellec, Bertrand; Lancry, Matthieu; Ibarra, Angel

    2015-01-01

    The aim of the present paper is to report the effect of radiation on the Er 3+ -doped sol-gel silica glasses. A possible application of these sol-gel glasses could be their use in harsh radiation environments. The sol-gel glasses are fabricated by densification of erbium salt-soaked nanoporous silica xerogels through polymeric sol-gel technique. The radiation-induced attenuation of Er 3+ -doped sol-gel silica is found to increase with erbium content. Electron paramagnetic resonance studies reveal the presence of E′ δ point defects. This happens in the sol-gel aluminum-silica glass after an exposure to γ-rays (kGy) and in sol-gel silica glass after an exposure to electrons (MGy). The concentration levels of these point defects are much lower in γ-ray irradiated sol-gel silica glasses. When the samples are co-doped with Al, the exposure to γ-ray radiation causes a possible reduction of the erbium valence from Er 3+ to Er 2+ ions. This process occurs in association with the formation of aluminum oxygen hole centers and different intrinsic point defects

  17. Anion embedded sol-gel films on Al for corrosion protection

    International Nuclear Information System (INIS)

    Sheffer, Mari; Groysman, Alec; Starosvetsky, David; Savchenko, Natali; Mandler, Daniel

    2004-01-01

    We report here on the successful incorporation of organic anions into a sol-gel film on Al as a means of enhancing the protection against corrosion. Following our previous study where we showed that hydrophobic sol-gel films provided pronounced corrosion inhibition, we studied the corrosion inhibition that phenylphosphonic acid (PPA) has when embedded inside a thin sol-gel coating on Al. The anion of this organic anion tends to stay inside a phenyltrimethoxysilane (PTMOS) based sol-gel film due to π-interactions. Our findings, which are derived primarily from potentiodynamic polarization measurements, electrochemical noise, scanning electron microscopy measurements and Auger electron spectroscopy (AES), clearly show that the organic phosphonate adds to the protection efficiency of the sol-gel film

  18. Synthesis of nanoparticles of magnetite by sol-gel and precipitation methods: study of chemical composition and structure

    International Nuclear Information System (INIS)

    Picasso, Gino; Vega, Jaime; Uzuriaga, Rosario; Ruiz, Gean Pieer

    2012-01-01

    In this work, nanoparticles based on magnetite have been prepared by sol-gel and precipitation methods. In the first case two variants have been applied: by growing of sol starting from nitrate precursor and ethylene glycol as solvent and to control the reduction process and force hydrolysis and steric control prepared from ferrum sulfate precursor and sodium citrate. In the second case the starting material was sulfate precursor, ammonium hydroxide as precipitaing agent and ethylene glycol as surfactant. The samples have been characterized by X-ray diffraction technique (XRD), adsorption-desorption of N 2 (BET equation model) and Moessbauer spectroscopy. XRD patterns of all samples showed typical peaks of magnetite which were detected in the following positions: 30,06 o , 35,42 o , 62,55 o . Average specific surface quantified by BET method was ranging from 40 to 50 m 2 /g with isotherm type IV corresponding to mesoporous surface. Moessbauer spectra of sample prepared from sol-gel (gel growing) carried out at home temperature detected the presence of 2 sextets consisting in 2 type of sites: first one due to octahedral positions (Fe 2+ , Fe 3+ ) and the second one due to tetrahedral positions (Fe 3+ ). Grain size of magnetite samples, evaluated by Scherrer equation and specific surface area, was ranging from 2 to 20 nm. (author).

  19. Polymer sol-gel composite inverse opal structures.

    Science.gov (United States)

    Zhang, Xiaoran; Blanchard, G J

    2015-03-25

    We report on the formation of composite inverse opal structures where the matrix used to form the inverse opal contains both silica, formed using sol-gel chemistry, and poly(ethylene glycol), PEG. We find that the morphology of the inverse opal structure depends on both the amount of PEG incorporated into the matrix and its molecular weight. The extent of organization in the inverse opal structure, which is characterized by scanning electron microscopy and optical reflectance data, is mediated by the chemical bonding interactions between the silica and PEG constituents in the hybrid matrix. Both polymer chain terminus Si-O-C bonding and hydrogen bonding between the polymer backbone oxygens and silanol functionalities can contribute, with the polymer mediating the extent to which Si-O-Si bonds can form within the silica regions of the matrix due to hydrogen-bonding interactions.

  20. Manufacture of Regularly Shaped Sol-Gel Pellets

    Science.gov (United States)

    Leventis, Nicholas; Johnston, James C.; Kinder, James D.

    2006-01-01

    An extrusion batch process for manufacturing regularly shaped sol-gel pellets has been devised as an improved alternative to a spray process that yields irregularly shaped pellets. The aspect ratio of regularly shaped pellets can be controlled more easily, while regularly shaped pellets pack more efficiently. In the extrusion process, a wet gel is pushed out of a mold and chopped repetitively into short, cylindrical pieces as it emerges from the mold. The pieces are collected and can be either (1) dried at ambient pressure to xerogel, (2) solvent exchanged and dried under ambient pressure to ambigels, or (3) supercritically dried to aerogel. Advantageously, the extruded pellets can be dropped directly in a cross-linking bath, where they develop a conformal polymer coating around the skeletal framework of the wet gel via reaction with the cross linker. These pellets can be dried to mechanically robust X-Aerogel.

  1. Protic ionic liquid as additive on lipase immobilization using silica sol-gel.

    Science.gov (United States)

    de Souza, Ranyere Lucena; de Faria, Emanuelle Lima Pache; Figueiredo, Renan Tavares; Freitas, Lisiane dos Santos; Iglesias, Miguel; Mattedi, Silvana; Zanin, Gisella Maria; dos Santos, Onélia Aparecida Andreo; Coutinho, João A P; Lima, Álvaro Silva; Soares, Cleide Mara Faria

    2013-03-05

    Ionic liquids (ILs) have evolved as a new type of non-aqueous solvents for biocatalysis, mainly due to their unique and tunable physical properties. A number of recent review papers have described a variety of enzymatic reactions conducted in IL solutions, on the other hand, to improve the enzyme's activity and stability in ILs; major methods being explored include the enzyme immobilization (on solid support, sol-gel, etc.), protic ionic liquids used as an additive process. The immobilization of the lipase from Burkholderia cepacia by the sol-gel technique using protic ionic liquids (PIL) as additives to protect against inactivation of the lipase due to release of alcohol and shrinkage of the gel during the sol-gel process was investigated in this study. The influence of various factors such as the length of the alkyl chain of protic ionic liquids (monoethanolamine-based) and a concentration range between 0.5 and 3.0% (w/v) were evaluated. The resulting hydrophobic matrices and immobilized lipases were characterised with regard to specific surface area, adsorption-desorption isotherms, pore volume (V(p)) and size (d(p)) according to nitrogen adsorption and scanning electron microscopy (SEM), physico-chemical properties (thermogravimetric - TG, differential scanning calorimetry - DSC and Fourier transform infrared spectroscopy - FTIR) and the potential for ethyl ester and emulsifier production. The total activity yields (Y(a)) for matrices of immobilized lipase employing protic ionic liquids as additives always resulted in higher values compared with the sample absent the protic ionic liquids, which represents 35-fold increase in recovery of enzymatic activity using the more hydrophobic protic ionic liquids. Compared with arrays of the immobilized biocatalyst without additive, in general, the immobilized biocatalyst in the presence of protic ionic liquids showed increased values of surface area (143-245 m(2) g(-1)) and pore size (19-38 Å). Immobilization with

  2. Transparent conducting sol-gel ATO coatings for display applications by an improved dip coating technique

    International Nuclear Information System (INIS)

    Guzman, G.; Dahmani, B.; Puetz, J.; Aegerter, M.A.

    2006-01-01

    Transparent conducting coatings of sol-gel ATO (antimony-doped tin oxide) were used to improve surface smoothness of commercial sputter-deposited ITO (indium tin oxide) coatings for application as display electrodes. In order to overcome the deteriorating evaporation-cooling during dip coating, the coating solution was heated moderately to 25 deg. C thus providing the substrate with the required heat. This way, the surface roughness of the ITO could be reduced with an only 45 nm thick ATO coating to R pv = 3.8 nm (R a = 0.4 nm) compared to 31 nm (3.8 nm) for the ITO substrate. Another benefit of such additional coating is the possibility to tailor surface properties of the electrodes in wide ranges. This was used to increase the work function of the ITO substrate from initially 4.3-4.6 eV to about 4.8-5.2 eV by the ATO coating

  3. Incorporation of sol-gel SnO2:Sb into nanoporous SiO2

    International Nuclear Information System (INIS)

    Canut, B.; Blanchin, M.G.; Ramos-Canut, S.; Teodorescu, V.; Toulemonde, M.

    2006-01-01

    Silicon oxide films thermally grown on Si(1 0 0) wafers were irradiated with 200 MeV 197 Au ions in the 10 9 -10 1 cm -2 fluence range. The targets were then etched at room temperature in aqueous HF solution (1 vol.%) for various durations. Atomic force microscopy (AFM) in the tapping mode was used to probe the processed surfaces. Conical holes with a low size dispersion were evidenced. Their surface diameter varies between 20 and 70 nm, depending on the etching time. Sol-gel dip coating technique, associated with a further annealing treatment performed at 500 o C for 15 min, was used to fill the nanopores created in SiO 2 with a transparent conductive oxide (SnO 2 doped with antimony). Transmission electron microscopy (TEM) performed on cross-sectional specimen showed that SnO 2 :Sb crystallites of ∼5 nm mean size are trapped in the holes without degrading their geometry

  4. Characterization of composites prepared by sol-gel process through positrons lifetime spectroscopy

    International Nuclear Information System (INIS)

    Sousa, Edesia M.B. de; Magalhaes, Welligton F. de; Mohallem, Nelcy D.S.

    1996-01-01

    Si O 2 matrix were prepared by sol-gel method using TEOS, ethanol and H 2 O in a 1/3/10 mol ratio, with HCl and HF as catalysts. This silica gels were doped with copper and titanium adding Cu Cl and titanium tetra-iso-prop oxide in the starting solution, during agitation. The samples were prepared in monolithic shape, were dried at 110 deg C for 24 hours and thermally treated for 2 hours at 500, 900 and 1100 deg C. The structural evolution was studied y x-ray diffraction, mercury porosimetry and pycnometry. In this work, it was also used the Position Annihilation Lifetime Spectroscopy which have been used, nowadays, as a microscopic probe in order to investigate the free volume in zeolites, polymers and metallic alloy. All the samples have shown a stable pore structure until 900 deg C and a strong densification process at 1100 deg C. (author)

  5. Formation and characterization of vitreous materials prepared by the sol-gel technique

    International Nuclear Information System (INIS)

    Martinez, J.R.; Ruiz, J.F.; Cruz M, J.A. de la; Villasenor G, P.

    1999-01-01

    A full process of preparation and characterization of silica gel, which can be implemented in a experimental course for undergraduate laboratories is presented. Samples of silica gel and sol-gel derived SiO 2 films on glass substrates were fabricated and characterized using atomic force microscopy, Raman and Infrared absorption techniques. Raman and Infrared spectroscopy were used to analyze the local structure. The microstructure characteristics of the films, fabricated by dip-coating, were monitored using atomic force microscopy. The samples were prepared from alcoholic solutions of tetraethylortosilicate (TEOS) keeping the H 2 O/TEOS and Et-OH/TEOS molar ratios constant and equal to 11.66 and 4 respectively. (Author)

  6. Repair of glass by sol-gel coating using either conventional or microwave heating

    International Nuclear Information System (INIS)

    Boonyapiwat, A.; Fathi, Z.; Folz, D.C.; Clark, D.E.

    1993-01-01

    A method of repairing glass is discussed. Microindentation was used to deliberately weaken the glass. Some samples were dip coated with silica sol. Effects of dipping the glass in copper nitrate solution also were studied. Heat treatments were conducted in either a conventional furnace or a microwave oven. Four-point bend testing was used to evaluate the merit of each process. Microwave hybrid heating had the same effect on the repair of uncoated glass as conventional heating. Coating the glass with sol resulted in higher strength of glass than heat treatment alone. Treating the glass with copper nitrate without heat treating had no effect on strength. Microwave hybrid heating appears to yield higher reliability in sol-gel coated samples than conventional processing. 21 refs., 8 figs., 2 tabs

  7. Properties of Zn O/Cr thin films prepared by Sol-Gel

    International Nuclear Information System (INIS)

    Tirado G, S.; Olvera A, R.

    2014-08-01

    Zn O films and those superficially modified with chromium were deposited on substrates of soda-lime glass, using the Sol-Gel process and the repeated immersion method. Starting from dehydrated zinc acetate was prepared a solution to 0.6 M to ambient temperature in 2-methoxyethanol and monoethanolamine (Mea) stirring magnetically. The Sol was prepared with an aging to seven days and was used to grow a films group with thickness to eight immersions. These same films were superficially modified with several depositions of a chromium nitrate Sol dissolved in ethanol to low concentration. The Zn O films were structurally characterized by X-ray diffraction, its chemical composition by energy dispersive X-ray spectroscopy and its morphology by scanning electron microscopy and atomic force microscopy, as well as their optical properties by UV-vis. Of the obtained results are proposed possible applications. (author)

  8. Organic carbon aerogels from the sol-gel polymerization of phenolic-furfural mixtures

    Science.gov (United States)

    Pekala, R.W.

    1998-04-28

    The sol-gel polymerization of a phenolic-furfural mixture in dilute solution leads to a highly cross-linked network that can be supercritically dried to form a high surface area foam. These porous materials have cell/pore sizes {<=}1000 {angstrom}, and although they are dark brown in color, they can be classified as a new type of aerogel. The phenolic-furfural aerogel can be pyrolyzed in an inert atmosphere at 1050 C to produce carbon aerogels. This new aerogel may be used for thermal insulation, chromatographic packing, water filtration, ion-exchange, and carbon electrodes for energy storage devices, such as batteries and double-layer capacitors. 8 figs.

  9. Organic aerogels from the sol-gel polymerization of phenolic-furfural mixtures

    Science.gov (United States)

    Pekala, R.W.

    1995-12-19

    The sol-gel polymerization of a phenolic-furfural mixture in dilute solution leads to a highly cross-linked network that can be supercritically dried to form a high surface area foam. These porous materials have cell/pore sizes{<=}1000{angstrom}, and although they are dark brown in color, they can be classified as a new type of aerogel. The phenolic-furfural aerogel can be pyrolyzed in an inert atmosphere at 1050 C to produce carbon aerogels. This new aerogel may be used for thermal insulation, chromatographic packing, water filtration, ion-exchange, and carbon electrodes for energy storage devices, such as batteries and double-layer capacitors. 8 figs.

  10. Ozonation and sol-gel method to obtain Cu/Cu O nanoparticles from cyanidation wastewater

    Energy Technology Data Exchange (ETDEWEB)

    Soria A, M. J.; Puente S, D. M.; Carrillo P, F. R. [Universidad Autonoma de Coahuila, Facultad de Metalurgia, Carretera 57 Km 4.5, 25710 Monclova, Coahuila (Mexico); Garcia C, L. A. [Centro de Investigacion en Quimica Aplicada, Blvd. Enrique Reyna No. 140, Col. Los Pinos, 25253 Saltillo, Coahuila (Mexico); Velazquez S, J., E-mail: frrcarrillo@yahoo.com.mx [University of Texas at San Antonio, Department of Physics and Astronomy, San Antonio TX 78249 (United States)

    2015-07-01

    The extraction process of gold and silver by cyanidation generates large amounts of effluent which also contain contaminants such as cyanide and significant metal values such as copper. This paper presents the results of the removal and recovery of copper from ozonation treatment of a residual aqueous cyanide. The residual solution was treated by ozonation-precipitation to obtain a precipitate of copper. From this, copper nano composites obtained by Pechini modified sol-gel method were obtained. The compounds obtained were characterized by X-ray diffraction, showing a dependence of the type of compounds formed over time of ozonation and heat treatment of the gel. The particle size was measured by scanning electron microscopy and calculated by the Scherrer equation, being between 50 and 120 nm. (Author)

  11. Sol-gel chemistry applied to the synthesis of polymetallic oxides including actinides reactivity and structure from solution to solid state; Synthese par voie douce d'oxydes polymetalliques incluant des actinides: reactivite et structure de la solution au solide

    Energy Technology Data Exchange (ETDEWEB)

    Lemonnier, St

    2006-02-15

    Minor actinides transmutation is studied at present in order to reduce the radiotoxicity of nuclear waste and the assessment of its technical feasibility requires specific designed materials. When considering americium, yttria stabilized zirconia (Am{sup III} YII Zriv)Or{sub x} is among the ceramic phases that one which presents the required physico-chemical properties. An innovative synthesis of this mixed oxide by sol-gel process is reported in this manuscript. The main aim of this work is to adjust the reactivity of the different metallic cations in aqueous media using complexing agent, in order to initiate a favourable interaction for a homogeneous elements repartition in the forming solid phase. The originality of the settled synthesis lies on an in-situ formation of a stable and monodisperse nano-particles dispersion in the presence of acetylacetone. The main reaction mechanisms have been identified: the sol stabilisation results from an original interaction between the three compounds (Zrly, trivalent cations and acetylacetone). The sol corresponds to a structured system at the nanometer scale for which zirconium and trivalent cations are homogeneously dispersed, preliminary to the sol-gel transition. Furthermore, preliminary studies were carried out with a view to developing materials. They have demonstrated that numerous innovative and potential applications can be developed by taking advantage of the direct and controlled formation of the sol and by adapting the sol-gel transition. The most illustrating result is the preparation of a sintered pellet with the composition Am0,13Zro,73Yo,0901,89 using this approach. (author)

  12. Sol-Gel Glass Holographic Light-Shaping Diffusers

    Science.gov (United States)

    Yu, Kevin; Lee, Kang; Savant, Gajendra; Yin, Khin Swe (Lillian)

    2005-01-01

    Holographic glass light-shaping diffusers (GLSDs) are optical components for use in special-purpose illumination systems (see figure). When properly positioned with respect to lamps and areas to be illuminated, holographic GLSDs efficiently channel light from the lamps onto specified areas with specified distributions of illumination for example, uniform or nearly uniform irradiance can be concentrated with intensity confined to a peak a few degrees wide about normal incidence, over a circular or elliptical area. Holographic light diffusers were developed during the 1990s. The development of the present holographic GLSDs extends the prior development to incorporate sol-gel optical glass. To fabricate a holographic GLSD, one records a hologram on a sol-gel silica film formulated specially for this purpose. The hologram is a quasi-random, micro-sculpted pattern of smoothly varying changes in the index of refraction of the glass. The structures in this pattern act as an array of numerous miniature lenses that refract light passing through the GLSD, such that the transmitted light beam exhibits a precisely tailored energy distribution. In comparison with other light diffusers, holographic GLSDs function with remarkably high efficiency: they typically transmit 90 percent or more of the incident lamp light onto the designated areas. In addition, they can withstand temperatures in excess of 1,000 C. These characteristics make holographic GLSDs attractive for use in diverse lighting applications that involve high temperatures and/or requirements for high transmission efficiency for ultraviolet, visible, and near-infrared light. Examples include projectors, automobile headlights, aircraft landing lights, high-power laser illuminators, and industrial and scientific illuminators.

  13. Fabrication of carbon microcapsules containing silicon nanoparticles-carbon nanotubes nanocomposite by sol-gel method for anode in lithium ion battery

    International Nuclear Information System (INIS)

    Bae, Joonwon

    2011-01-01

    Carbon microcapsules containing silicon nanoparticles (Si NPs)-carbon nanotubes (CNTs) nanocomposite (Si-CNT-C) have been fabricated by a surfactant mediated sol-gel method followed by a carbonization process. Silicon nanoparticles-carbon nanotubes (Si-CNT) nanohybrids were produced by a wet-type beadsmill method. To obtain Si-CNT nanocomposites with spherical morphologies, a silica precursor (tetraethylorthosilicate, TEOS) and polymer (PMMA) mixture was employed as a structure-directing medium. Thus the Si-CNT/Silica-Polymer microspheres were prepared by an acid catalyzed sol-gel method. Then a carbon precursor such as polypyrrole (PPy) was incorporated onto the surfaces of pre-existing Si-CNT/silica-polymer to generate Si-CNT/Silica-Polymer-PPy microspheres. Subsequent thermal treatment of the precursor followed by wet etching of silica produced Si-CNT-C microcapsules. The intermediate silica/polymer must disappear during the carbonization and etching process resulting in the formation of an internal free space. The carbon precursor polymer should transform to carbon shell to encapsulate remaining Si-CNT nanocomposites. Therefore, hollow carbon microcapsules containing Si-CNT nanocomposites could be obtained (Si-CNT-C). The successful fabrication was confirmed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). These final materials were employed for anode performance improvement in lithium ion battery. The cyclic performances of these Si-CNT-C microcapsules were measured with a lithium battery half cell tests. - Graphical Abstract: Carbon microcapsules containing silicon nanoparticles (Si NPs)-carbon nanotubes (CNTs) nanocomposite (Si-CNT-C) have been fabricated by a surfactant mediated sol-gel method. Highlights: → Polymeric microcapsules containing Si-CNT transformed to carbon microcapsules. → Accommodate volume changes of Si NPs during Li ion charge/discharge. → Sizes of microcapsules were controlled by experimental parameters.

  14. Alumina support prodn. with active component by sol-gel method - and use esp. for regenerative absorption of sulphur dioxide, oxygen or hydrogen sulphide

    NARCIS (Netherlands)

    Frens, G.

    1991-01-01

    Prodn. of a support contg. Al2O3 with an active component and/or precursor for this is carried out by the sol/gel technique by (a) producing a sol from AlCl3 or material forming Al2O3, (b) supplying the sol to the top of a column filled with a water-immiscible solvent (I) in the upper pt. and an

  15. Sol-Gel Synthesis and Characterization of Cubic Bismuth Zinc Niobium Oxide Nanopowders

    Directory of Open Access Journals (Sweden)

    Ganchimeg Perenlei

    2014-01-01

    Full Text Available Bismuth zinc niobium oxide (BZN was successfully synthesized by a diol-based sol-gel reaction utilizing metal acetate and alkoxide precursors. Thermal analysis of a liquid suspension of precursors suggests that the majority of organic precursors decompose at temperatures up to 150°C, and organic free powders form above 350°C. The experimental results indicate that a homogeneous gel is obtained at about 200°C and then converts to a mixture of intermediate oxides at 350–400°C. Finally, single-phased BZN powders are obtained between 500 and 900°C. The degree of chemical homogeneity as determined by X-ray diffraction and EDS mapping is consistent throughout the samples. Elemental analysis indicates that the atomic ratio of metals closely matches a Bi1.5ZnNb1.5O7 composition. Crystallite sizes of the BZN powders calculated from the Scherrer equation are about 33–98 nm for the samples prepared at 500–700°C, respectively. The particle and crystallite sizes increase with increased sintering temperature. The estimated band gap of the BZN nanopowders from optical analysis is about 2.60–2.75 eV at 500-600°C. The observed phase formations and measured results in this study were compared with those of previous reports.

  16. Preparación y densificación de monolitos cerámicos nanoestructurados de Y-TZP por Sol-gel

    Directory of Open Access Journals (Sweden)

    Tartaj, J.

    1999-12-01

    Full Text Available Y-TZP seeded gel monoliths have been prepared by a sol-gel method based on the coprecipitation of Zr4+ and Y3+ precursors as hydroxides and the stabilisation of the suspension in pure ethanol with a disc turbine. The addition of solid Y-TZP nanometer- size seed particles into the Y-TZP precursor solution play a crucial role during cristallisation and densification of monoliths. Basically, induced a preferential nucleation, which enhance the crystallisation kinetics and the activation energy is reasonably lowered. As a result of the increased nucleation frequency for the crystallisation process a well-developed homogeneous porous microstructure is obtained facilitating the sintering and so the densification at lower temperatures. In this way, Y-TZP highly densificated ceramics monoliths have been obtained at 1050ºC, with a grain size within the nanometer range.

    Monolitos de geles de Y-TZP semillados han sido preparados por un método de sol-gel basado en la coprecipitación de precursores de Zr4+ y Y3+ en forma de hidróxidos y la estabilización de la suspensión en etanol puro con una turbina de disco. La adición de partículas nanométricas de Y-TZP cristalizadas a la solución precursora juega un papel fundamental durante la cristalización y densificación de los monolitos. Básicamente, se induce una nucleación preferente, que mejora la cinética de cristalización y reduce razonablemente la energía de activación. Como resultado del incremento de la frecuencia de nucleación para el proceso de cristalización, se obtiene una microestructura porosa, homogénea y bien desarrollada que facilita la sinterización y por tanto la densificación del material a temperaturas más bajas. De esta forma, monolitos cerámicos de Y-TZP altamente densificados han sido obtenidos a 1050ºC, con un tamaño de grano dentro de un rango nanométrico.

  17. Chitosan-doped-hybrid/TiO2 nanocomposite based sol-gel coating for the corrosion resistance of aluminum metal in 3.5% NaCl medium.

    Science.gov (United States)

    J, Balaji; M G, Sethuraman

    2017-11-01

    The study outlines the role of chitosan, a biopolymer on corrosion behavior of Hy/nano-TiO 2 based sol-gel coating over aluminum metal. In this study organic-inorganic hybrid sols were synthesized through hydrolysis and condensation of 3-glycidoxypropyltrimethoxy silane (GPTMS), tetraethoxysilane (TEOS) and titanium (IV) isopropoxide (TIP) in acidic solution. Chitosan was doped into sol-gel matrix and self-assembled over aluminum substrate. The resultant chitosan-doped-Hy/nano-TiO 2 sol-gel coating was characterized by Fourier Transform Infrared (FT-IR) spectra, Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM) and Energy-Dispersive X-ray Spectroscopy (EDX) analyses. The as-tailored aluminum substrate was evaluated for corrosion resistance in neutral medium. The protection ability of these coatings was evaluated by electrochemical impedance studies (EIS) and potentiodynamic polarization (PP) measurements in 3.5% NaCl medium. The EIS and PP results showed that chitosan-doped- Hy/nano-TiO 2 sol-gel coating exhibited better protection from corrosion than the undoped Hy/TiO 2 nanocomposite coating. Copyright © 2017 Elsevier B.V. All rights reserved.

  18. Template-directed formation of functional complex metal-oxide nanostructures by combination of sol-gel processing and spin coating

    International Nuclear Information System (INIS)

    Choi, Y.C.; Kim, J.; Bu, S.D.

    2006-01-01

    We report the template-based formation of functional complex metal-oxide nanostructures by a combination of sol-gel processing and spin coating. This method employs the spin-coating of a sol-gel solution into an anodic aluminum oxide membrane (SSAM). Various metal-oxide nanowires and nanotubes with a high aspect-ratio were prepared. The aspect-ratios of the PbO 2 nanowires and Pb(Zr 0.52 Ti 0.48 )O 3 nanowires were about 300 and 400, respectively, and their diameters were about 50 nm. The fabricated PbTiO 3 nanotubes have a relatively constant wall thickness of about 20 nm with an outer diameter of about 60 nm. The deposition time for all of the fabricated metal-oxide nanowires and nanotubes is less than 120 s, which is far shorter than those required in both the sol-gel dipping and sol-gel electrophoretic methods. These results indicate that the SSAM method can be a versatile pathway to prepare functional complex metal-oxide nanowires and nanotubes with a high aspect-ratio. The possible formation process for the one-dimensional nanostructures by SSAM is discussed

  19. Modified Au nanoparticles-imprinted sol-gel, multiwall carbon nanotubes pencil graphite electrode used as a sensor for ranitidine determination.

    Science.gov (United States)

    Rezaei, B; Lotfi-Forushani, H; Ensafi, A A

    2014-04-01

    A new, simple, and disposable molecularly imprinted electrochemical sensor for the determination of ranitidine was developed on pencil graphite electrode (PGE) via cyclic voltammetry (CV). The PGEs were coated with MWCNTs containing the carboxylic functional group (f-MWCNTs), imprinted with sol-gel and Au nanoparticle (AuNPs) layers (AuNP/MIP-sol-gel/f-MWCNT/PGE), respectively, to enhance the electrode's electrical transmission and sensitivity. The thin film of molecularly imprinted sol-gel polymers with specific binding sites for ranitidine was cast on modified PGE by electrochemical deposition. The AuNP/MIP-sol-gel/f-MWCNT/PGE thus developed was characterized by electrochemical impedance spectroscopy (EIS) and CV. The interaction between the imprinted sensor and the target molecule was also observed on the electrode by measuring the current response of 5.0mMK3[Fe(CN)6] solution as an electrochemical probe. The pick currents of ranitidine increased linearly with concentration in the ranges of 0.05 to 2.0μM, with a detection limit of (S/N=3) 0.02μM. Finally, the modified electrode was successfully employed to determine ranitidine in human urine samples. Copyright © 2014 Elsevier B.V. All rights reserved.

  20. Tertiary-amine-containing thermo- and pH-sensitive hydrophilic ABA triblock copolymers: effect of different tertiary amines on thermally induced sol-gel transitions.

    Science.gov (United States)

    Henn, Daniel M; Wright, Roger A E; Woodcock, Jeremiah W; Hu, Bin; Zhao, Bin

    2014-03-11

    This Article reports on the synthesis of a series of well-defined, tertiary-amine-containing ABA triblock copolymers, composed of a poly(ethylene oxide) (PEO) central block and thermo- and pH-sensitive outer blocks, and the study of the effect of different tertiary amines on thermally induced sol-gel transition temperatures (T(sol-gel)) of their 10 wt % aqueous solutions. The doubly responsive ABA triblock copolymers were prepared from a difunctional PEO macroinitiator by atom transfer radical polymerization of methoxydi(ethylene glycol) methacrylate and ethoxydi(ethylene glycol) methacrylate at a feed molar ratio of 30:70 with ∼5 mol % of either N,N-diethylaminoethyl methacrylate (DEAEMA), N,N-diisopropylaminoethyl methacrylate, or N,N-di(n-butyl)aminoethyl methacrylate. The chain lengths of thermosensitive outer blocks and the molar contents of tertiary amines were very similar for all copolymers. Using rheological measurements, we determined the pH dependences of T(sol-gel) of 10 wt % aqueous solutions of these copolymers in a phosphate buffer. The T(sol-gel) versus pH curves of all polymers exhibited a sigmoidal shape. The T(sol-gel) increased with decreasing pH; the changes were small on both high and low pH sides. At a specific pH, the T(sol-gel) decreased with increasing the hydrophobicity of the tertiary amine, and upon decreasing pH the onset pH value for the T(sol-gel) to begin to increase noticeably was lower for the more hydrophobic tertiary amine-containing copolymer. In addition, we studied the effect of different tertiary amines on the release behavior of FITC-dextran from 10 wt % micellar gels in an acidic medium at 37 and 27 °C. The release profiles for three studied hydrogels at 37 °C were essentially the same, suggesting that the release was dominated by the diffusion of FITC-dextran. At 27 °C, the release was significantly faster for the DEAEMA-containing copolymer, indicating that both diffusion and gel dissolution contributed to the

  1. Some features associated with organosilane groups grafted by the sol-gel process onto synthetic talc-like phyllosilicate.

    Science.gov (United States)

    Sales, José A A; Petrucelli, Giovanni C; Oliveira, Fernando J V E; Airoldi, Claudio

    2006-05-01

    Two new lamellar inorganic-organic magnesium silicates have been successfully synthesized by using sol-gel based processes under mild temperature conditions. The talc-organosilicates derived using two silylating agents as the silicon source, (i) 3-chloropropyltrimethoxysilane, and (ii) from the attachment of 5-amino-1,3,4-thiadiazole-2-thiol molecule to this precursor agent, yielded PhMg-Cl and PhMg-Tz phyllosilicates. These organoclays were characterized through elemental analyses, infrared spectroscopy, X-ray diffractometry, surface area, thermogravimetry, and carbon and silicon solid state nuclear magnetic resonance spectroscopy. The results confirmed the presence of organic moieties covalently bonded to the inorganic silicon sheet network of the 2:1 class of phyllosilicates, with a density of organic molecules of 6.6+/-0.1 and 2.7+/-0.2 mmol g(-1) anchored on the inorganic layer and with interlayer distances of 1158 and 1628 pm, respectively. The nuclear magnetic resonances results in the solid state are in agreement with the sequence of carbons distributed in the pendant chains of the original silylating agents and the silicon bonded to oxygen atoms or carbon atoms of the inorganic sheets, as expected for the organically functionalized phyllosilicates. The enhanced potential of the new compound PhMg-Tz as a multi property material was explored in adsorbing cations from aqueous solution. The basic sulfur and nitrogen centers attached to the pendant chains inside the lamellar cavity can coordinate mercury, by presenting an isotherm saturated at 0.19 mmol g(-1) of this heavy metal. The functionality of this organoclay-like material expresses its potential for heavy cation removal from an ecosystem.

  2. Synthesis of LiFePO4/C composites based on natural iron stone using a sol gel method

    Science.gov (United States)

    Angela, Riyan; Islam, Humaatul; Sari, Vamellia; Latif, Chaironi; Zainuri, Mochamad; Pratapa, Suminar

    2017-01-01

    Synthesis of LiFePO4/C composites has been carried out using a sol gel method. The Fe precursor was made from a natural iron stone of Tanah Laut, South Kalimantan, while the other raw materials were commercial Li2CO3 powder and NH4H2PO4 powder with HCl and water as solvents. Citric acid was used as the carbon source in the synthesis. This study used a molar ratio of 1:1:2 for Li:Fe:P with variation of added citric acid of 1.5 and 2.5 g. The solutions were dried in air at 100°C. The dried powders were characterized using DSC-TGA and then calcined at 600 and 700°C under argon environment for 10 hours. The calcined powders were characterized by X-ray diffractometry (XRD), scanning electron microscopy-energy dispersive x-ray (SEM-EDX), and LCR meter. It was found that the samples contained LiFePO4 as the dominant phase and LiFeP2O7 and Fe2O3 as secondary phases. The analysis showed that the addition of citric acid influenced the electronic conductivity of the composites. A Rietveld relative weight fraction of up to 94.7% was achieved in the synthesis at temperature 600°C. The LFP/C sample exhibited electronic conductivity of 4.56×10-3 Scm-1 which was six times of that of the pure LFP.

  3. A utilização de materiais obtidos pelo processo de sol-gel na construção de biossensores The utilization of materials obtained by the sol-gel process in biosensors construction

    Directory of Open Access Journals (Sweden)

    Antonio A. S. Alfaya

    2002-09-01

    Full Text Available The use of sol-gel materials to develop new biosensors has received great attention due to its characteristics and versatility of sol-gel process. An overview is presented of the state-of-the-art of electrochemical biosensors employing sol-gel materials. Low-temperature, porous sol-gel ceramics represent a new class for the immobilization of biomolecules. The rational design of sol-gel sensing materials, based on the judicious choice of the starting alkoxide, encapsulated reagents, and preparation conditions, allows tailoring of material properties in a wide range, and offers great potential for the development of electrochemical biosensors.

  4. Formulation and evaluation of antimicrobial activity of Morus alba sol-gel against periodontal pathogens

    Directory of Open Access Journals (Sweden)

    Shilpa Gunjal

    2015-01-01

    Full Text Available Background: Periodontitis has a multifactorial etiology, with primary etiologic agents being pathogenic bacteria that reside in the subgingival area. Recent advances in the field of alternative medicine introduced various herbal products for the treatment of periodontitis. Aim: To assess and compare the antimicrobial activity of Morus alba sol-gel with chlorhexidine sol-gel against ATCC standard strains of Aggregatibacter actinomycetemcomitans, Porphyromonas gingivalis, and Tannerella forsythia. Materials and Methods: Crude extract of Morus alba leaves was prepared by Soxhlet method by using ethanol as a solvent. Phytochemical screening of the crude extract of M. alba was performed to check the various chemical constituents. M. alba sol-gel and chlorhexidine sol-gel were formulated using Pluronic f127 and Pluronic f108 and compared for their antimicrobial activity. The minimum inhibitory concentration of both the gels was performed using agar well diffusion technique. Results: The minimum inhibitory concentration of M. alba sol-gel and chlorhexidine sol-gel against A. actinomycetemcomitans is 19 and 17 mm, T. forsythia is 12 and 21 mm, and P. gingivalis is 16 and 18 mm, respectively. Conclusion: Both M. alba and chlorhexidine sol-gel exhibited potent antimicrobial activity against periodontal pathogens.

  5. Sol-Gel Deposition of Iridium Oxide for Biomedical Micro-Devices

    Directory of Open Access Journals (Sweden)

    Cuong M. Nguyen

    2015-02-01

    Full Text Available Flexible iridium oxide (IrOx-based micro-electrodes were fabricated on flexible polyimide substrates using a sol-gel deposition process for utilization as integrated pseudo-reference electrodes for bio-electrochemical sensing applications. The fabrication method yields reliable miniature on-probe IrOx electrodes with long lifetime, high stability and repeatability. Such sensors can be used for long-term measurements. Various dimensions of sol-gel iridium oxide electrodes including 1 mm × 1 mm, 500 µm × 500 µm, and 100 µm × 100 µm were fabricated. Sensor longevity and pH dependence were investigated by immersing the electrodes in hydrochloric acid, fetal bovine serum (FBS, and sodium hydroxide solutions for 30 days. Less pH dependent responses, compared to IrOx electrodes fabricated by electrochemical deposition processes, were measured at 58.8 ± 0.4 mV/pH, 53.8 ± 1.3 mV/pH and 48 ± 0.6 mV/pH, respectively. The on-probe IrOx pseudo-reference electrodes were utilized for dopamine sensing. The baseline responses of the sensors were higher than the one using an external Ag/AgCl reference electrode. Using IrOx reference electrodes integrated on the same probe with working electrodes eliminated the use of cytotoxic Ag/AgCl reference electrode without loss in sensitivity. This enables employing such sensors in long-term recording of concentrations of neurotransmitters in central nervous systems of animals and humans.

  6. Sol-Gel Deposition of Iridium Oxide for Biomedical Micro-Devices

    Science.gov (United States)

    Nguyen, Cuong M.; Rao, Smitha; Yang, Xuesong; Dubey, Souvik; Mays, Jeffrey; Cao, Hung; Chiao, Jung-Chih

    2015-01-01

    Flexible iridium oxide (IrOx)-based micro-electrodes were fabricated on flexible polyimide substrates using a sol-gel deposition process for utilization as integrated pseudo-reference electrodes for bio-electrochemical sensing applications. The fabrication method yields reliable miniature on-probe IrOx electrodes with long lifetime, high stability and repeatability. Such sensors can be used for long-term measurements. Various dimensions of sol-gel iridium oxide electrodes including 1 mm × 1 mm, 500 μm × 500 μm, and 100 μm × 100 μm were fabricated. Sensor longevity and pH dependence were investigated by immersing the electrodes in hydrochloric acid, fetal bovine serum (FBS), and sodium hydroxide solutions for 30 days. Less pH dependent responses, compared to IrOx electrodes fabricated by electrochemical deposition processes, were measured at 58.8 ± 0.4 mV/pH, 53.8 ± 1.3 mV/pH and 48 ± 0.6 mV/pH, respectively. The on-probe IrOx pseudo-reference electrodes were utilized for dopamine sensing. The baseline responses of the sensors were higher than the one using an external Ag/AgCl reference electrode. Using IrOx reference electrodes integrated on the same probe with working electrodes eliminated the use of cytotoxic Ag/AgCl reference electrode without loss in sensitivity. This enables employing such sensors in long-term recording of concentrations of neurotransmitters in central nervous systems of animals and humans. PMID:25686309

  7. Sol-gel synthesis of TiO2 nanoparticles and photocatalytic degradation of methyl orange in aqueous TiO2 suspensions

    International Nuclear Information System (INIS)

    Yang Huaming; Zhang Ke; Shi Rongrong; Li Xianwei; Dong Xiaodan; Yu Yongmei

    2006-01-01

    Anatase TiO 2 nanoparticles of about 16 nm in crystal size have been successfully synthesized via a sol-gel method. Thermal treatment of the precursor at 500-600 deg. C results in the formation of different TiO 2 phase compositions. The samples were characterized by means of X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM). Effects of the pH value of the solution, H 2 O 2 addition, TiO 2 phase composition and recycled TiO 2 on the photocatalytic degradation of methyl orange (MeO) in TiO 2 suspensions under ultraviolet (UV) illumination were primarily investigated. The results indicate that a low pH value, proper amount of H 2 O 2 and pure anatase TiO 2 will facilitate the photocatalytic oxidation of the MeO solution. The photodegradation degree decreases with increasing the pH value of the solution and varies with different amounts of H 2 O 2 . Pure anatase TiO 2 shows better photocatalytic activity for MeO decolorization than biphase TiO 2 . The photocatalytic mechanism of the as-synthesized TiO 2 nanoparticles was discussed

  8. Minimally Adhesive, Advanced Non-toxic Coatings of Dendrimeric Catalysts in Sol-Gel Matrices

    Science.gov (United States)

    2015-10-19

    Catalysts in Sol -Gel Matrices 5a. CONTRACT NUMBER 5b. GRANT NUMBER N00014-09-1-0217 5c. PROGRAM ELEMENT NUMBER 6. AUTHOR(S) Detty, Michael R. 5d...Technical Report for ONR N00014-09-1-0217 Minimally Adhesive, Advanced Non-toxic Coatings of Dendrimeric Catalysts in Sol -Gel Matrices Michael R. Detty, PI...Environmentally benign sol -gel antifouling and foul-releasing coatings. Ace. Chem. Res. 2014, 47, 678-687. 11) Alberto, E. E.; Müller, L. M

  9. Ultrasound-assisted sol-gel synthesis of ZrO2.

    Science.gov (United States)

    Guel, Marlene Lariza Andrade; Jiménez, Lourdes Díaz; Hernández, Dora Alicia Cortés

    2017-03-01

    Synthesis of tetragonal ZrO 2 by both conventional sol-gel and ultrasound-assisted sol-gel methods and using a non-ionic surfactant Tween-20, was performed. A porous microstructure composed of nanometric particles was observed. Tetragonal ZrO 2 was obtained using a low heat treatment temperature of powders, 500°C by both methods. A higher crystallinity and a shorter reaction time were observed when ultrasound was used in the sol-gel method due to the cavitation phenomenon. Copyright © 2016 Elsevier B.V. All rights reserved.

  10. Synthesis and characterization of CdO nano particles by the sol-gel method

    Science.gov (United States)

    Vadgama, V. S.; Vyas, R. P.; Jogiya, B. V.; Joshi, M. J.

    2017-05-01

    Cadmium Oxide (CdO) is an inorganic compound and one of the main precursors to other cadmium compounds. It finds applications in cadmium plating, storage batteries, in transparent conducting film, etc. Here, an attempt is made to synthesize CdO nano particles by sol-gel technique. The gel was prepared using cadmium nitrate tetra hydrate (Cd(NO3)2.4H2O) and aqueous ammonium hydroxide (NH4OH) as a precursor. The synthesized powder is further characterized by techniques like Powder X-ray diffraction (XRD), Transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FT-IR) and Thermal gravimetric analysis (TGA). Powder XRD analysis suggested the nano-crystalline nature of the sample with the cubic crystal system. Nano scaled particles of spherical morphology with the size ranging from 50-100 nm are observed from TEM images. While, FT-IR study is used to confirm the presence of different functional groups. Thermo-gravimetric analysis suggests the highly thermally stable nature of the samples. The results are discussed.

  11. Partial Oxidation of n-Butane over a Sol-Gel Prepared Vanadium Phosphorous Oxide

    Directory of Open Access Journals (Sweden)

    Juan M. Salazar

    2013-01-01

    Full Text Available Vanadium phosphorous oxide (VPO is traditionally manufactured from solid vanadium oxides by synthesizing VOHPO4∙0.5H2O (the precursor followed by in situ activation to produce (VO2P2O7 (the active phase. This paper discusses an alternative synthesis method based on sol-gel techniques. Vanadium (V triisopropoxide oxide was reacted with ortho-phosphoric acid in an aprotic solvent. The products were dried at high pressure in an autoclave with a controlled excess of solvent. This procedure produced a gel of VOPO4 with interlayer entrapped molecules. The surface area of the obtained materials was between 50 and 120 m2/g. Alcohol produced by the alkoxide hydrolysis reduced the vanadium during the drying step, thus VOPO4 was converted to the precursor. This procedure yielded non-agglomerated platelets, which were dehydrated and evaluated in a butane-air mixture. Catalysts were significantly more selective than the traditionally prepared materials with similar intrinsic activity. It is suggested that the small crystallite size obtained increased their selectivity towards maleic anhydride.

  12. Phase Composition of Samarium Niobate and Tantalate Thin Films Prepared by Sol-Gel Method

    Science.gov (United States)

    Bruncková, H.; Medvecký, Ľ.; Múdra, E.; Kovalčiková, A.; Ďurišin, J.; Šebek, M.; Girman, V.

    2017-12-01

    Samarium niobate SmNbO4 (SNO) and tantalate SmTaO4 (STO) thin films ( 100 nm) were prepared by sol-gel/spin-coating process on alumina substrates with PZT interlayer and annealing at 1000°C. The precursors of films were synthesized using Nb or Ta tartrate complexes. The improvement of the crystallinity of monoclinic M'-SmTaO4 phase via heating was observed through the coexistence of small amounts of tetragonal T-SmTa7O19 phase in STO precursor at 1000°C. The XRD results of SNO and STO films confirmed monoclinic M-SmNbO4 and M'-SmTaO4 phases, respectively, with traces of orthorhombic O-SmNbO4 (in SNO). In STO film, the single monoclinic M'-SmTaO4 phase was revealed. The surface morphology and topography of thin films were investigated by SEM and AFM analysis. STO film was smoother with roughness 3.2 nm in comparison with SNO (6.3 nm). In the microstructure of SNO film, small spherical ( 50 nm) and larger cuboidal particles ( 100 nm) of the SmNbO4 phase were observed. In STO, compact clusters composed of fine spherical SmTaO4 particles ( 20-50 nm) were found. Effect of samarium can contribute to the formation different polymorphs of these films for the application to environmental electrolytic thin film devices.

  13. Structural and electrochemical behavior of sol-gel ZrO2 ceramic film on chemically pre-treated AZ91D magnesium alloy

    International Nuclear Information System (INIS)

    Li Qing; Chen Bo; Xu Shuqiang; Gao Hui; Zhang Liang; Liu Chao

    2009-01-01

    In the present investigation sol-gel-based ZrO 2 ceramic film was obtained using zirconium acetate as the precursor material. The film was deposited on AZ91D magnesium alloy by a dip-coating technique. An uniform stannate conversion coating as chemical pretreatment was employed as an intermediate layer prior to deposition of the ZrO 2 film in order to provide advantage for the formation of sol-gel-based ZrO 2 layer. The corrosion properties, structure, composition and morphology of these coatings on AZ91D magnesium alloy were studied by potentiodynamic polarization tests, EIS, XRD, SEM, respectively. According to the electrochemical tests, the corrosion resistance of AZ91D magnesium alloy was found to be greatly improved by means of this new environment-friendly surface treatment.

  14. Laser ablation inductively coupled plasma mass spectrometry analysis of agricultural soils using the sol-gel technique of pellet preparation

    International Nuclear Information System (INIS)

    Hubova, I.; Hola, M.; Vaculovic, T.; Pinkas, J.; Prokes, L.; Stefan, I.; Kanicky, V.

    2009-01-01

    Full text: Monitoring of metals in agricultural soils is gaining importance as they are accumulated by plants. A LAICPQMS method with Nd:YAG 213 nm laser has been developed for determination of Cr, Ni, Cu, Zn and Pb in soil pellets prepared by the sol-gel technique. LA-ICPMS analysis of archive samples was verified by XRF of wax-soil pellets and ICPMS with nebulization of solutions obtained by total soil decomposition and by analysis of reference materials. Sequention extraction was used for fractionation analysis. (author)

  15. Ultralow-density SiO2 aerogels prepared by a two-step sol-gel process

    International Nuclear Information System (INIS)

    Wang Jue; Li Qing; Shen Jun; Zhou Bin; Chen Lingyan; Jiang; Weiyang

    1996-01-01

    Low density SiO 2 gels are prepared by a two-step sol-gel process from TEOS. The influence of various solution ratios on the gelation process is investigated. The comparative characterization of gels using different solvent, such as ethanol, acetone and methyl cyanide, is also given. The ultralow-density SiO 2 aerogels with density less than 10 kg/m 3 are prepared by CO 2 supercritical drying technique. The structure difference between SiO 2 aerogels prepared by conventional single-step process and the two-step process is also presented

  16. Synthesis of uranium and thorium dioxides by Complex Sol-Gel Processes (CSGP). Synthesis of uranium oxides by Complex Sol-Gel Processes (CSGP)

    International Nuclear Information System (INIS)

    Deptula, A.; Brykala, M.; Lada, W.; Olczak, T.; Wawszczak, D.; Chmielewski, A.G.; Modolo, G.; Daniels, H.

    2010-01-01

    In the Institute of Nuclear Chemistry and Technology (INCT), a new method of synthesis of uranium and thorium dioxides by original variant of sol-gel method - Complex Sol-Gel Process (CSGP), has been elaborated. The main modification step is the formation of nitrate-ascorbate sols from components alkalized by aqueous ammonia. Those sols were gelled into: - irregularly agglomerates by evaporation of water; - medium sized microspheres (diameter <150) by IChTJ variant of sol-gel processes by water extraction from drops of emulsion sols in 2-ethylhexanol-1 by this solvent. Uranium dioxide was obtained by a reduction of gels with hydrogen at temperatures >700 deg. C, while thorium dioxide by a simple calcination in the air atmosphere. (authors)

  17. Effect of annealing temperature on structural, morphological and electrical properties of nanoparticles TiO{sub 2} thin films by sol-gel method

    Energy Technology Data Exchange (ETDEWEB)

    Muaz, A. K. M.; Hashim, U., E-mail: uda@unimap.edu.my; Arshad, M. K. Md.; Ruslinda, A. R.; Ayub, R. M.; Gopinath, Subash C. B.; Voon, C. H.; Liu, Wei-Wen; Foo, K. L. [Institute of Nano Electronic Engineering, Univerisiti Malaysia Perlis, 01000 Kangar, Perlis (Malaysia)

    2016-07-06

    In this paper, the sol-gel method is used to prepare nanoparticles titanium dioxide (TiO{sub 2}) thin films at different annealing temperature. The prepared sol was deposited on the p-SiO{sub 2} substrates by spin coating technique under room temperature. The nanoparticles TiO{sub 2} solution was synthesized using Ti{OCH(CH_3)_2}{sub 4} as a precursor with an methanol solution at a molar ratio 1:10. The prepared TiO{sub 2} sols will further validate through structural, morphological and electrical properties. From the X-ray diffraction (XRD) analysis, as-deposited films was found to be amorphous in nature and tend to transform into tetragonal anatase and rutile phase as the films annealed at 573 and 773 K, respectively. The diversification of the surface roughness was characterized by atomic force microscopy (AFM) indicated the roughness and thickness very dependent on the annealing temperature. The two-point probe electrical resistance and conductance of nanoparticles TiO{sub 2} thin films were determined by the DC current-voltage (IV) analysis. From the I-V measurement, the electrical conductance increased as the films annealed at higher temperature.

  18. Preparation and optical properties of mesoporous TiO2 thin films by a two-step sol-gel technique

    International Nuclear Information System (INIS)

    Kartini, I.; Lu, G.Q.; Meredith, P.; Zhao, X.S.

    2002-01-01

    This paper concerns the preparation of mesoporous titania nanopowders and thin films for use in next generation photoelectrochemical solar cells. We have recently developed a novel method for preparing mesoporous TiO 2 powders using a Two-Step Sol-gel method (TSS). These materials have crystalline domains characteristic of anatase. The first step of the process involves the hydrolysis of titanium isopropoxide in a basic aqueous solution mediated by neutral surfactant. The solid product resulting from Step-1 is then treated in acidified ethanol solution containing a titanium precursor to yield anatase TiO 2 . The resultant powder exhibits a high surface area and large pore volume with uniform mesopores. Slurries made from the resultant powder of Steps 1 and 2 have been used to produce thin titania films on glass slides. The optical and structural properties of these films have been compared to the films made of a commercial titania (Degussa P25, BASF). We will discuss these properties with respect to the possible use of such mesoporous titania films as the wide band gap semiconductor in dye-sensitized nanocrystalline TiO 2 solar cells

  19. Crystal structures of sol-gel deposited zirconia thin films

    International Nuclear Information System (INIS)

    Bell, J.M.; Cheary, R.W.; Rice, M.; Ben-Nissan, B.; Cocking, J.L.; Johnstone, G.R.

    1992-01-01

    The authors reports on the crystal structure of zirconia thin films by high temperature x-ray diffraction. The films were deposited by sol-gel processing onto polished stainless steel substrates, and dried at 200 deg C. X-ray diffraction at temperatures between 400 deg C and 800 deg C was carried out using an APEX diffractometer with a position sensitive detector. Previous results indicated that there was a transformation between the tetragonal phase and the monoclinic phase at approximately 770 deg C. Two experiments have been carried out: temperature runs, where the structure evolution is studied as a function of temperature; and time evolution of the structure at fixed temperatures. The results for both experiments, including structural analysis of the different phases found in the thin zirconia films and an analysis of the kinetics of the phase transformation(s) from the time evolution work are presented. This will include a comparison with theories of nucleation and crystallisation in single element films. Impurity phases introduced by interaction of the zirconia with the substrate have been observed, and the effect of increasing annealing time on the substrate-film interaction will also be discussed. 17 refs., 1 tab., 3 figs

  20. Sol-gel derived electrode materials for supercapacitor applications

    Science.gov (United States)

    Lin, Chuan

    1998-12-01

    Electrochemical capacitors have been receiving increasing interest in recent years for use in energy storage systems because of their high energy and power density and long cycle lifes. Possible applications of electrochemical capacitors include high power pulsed lasers, hybrid power system for electric vehicles, etc. In this dissertation, the preparation of electrode materials for use as electrochemical capacitors has been studied using the sol-gel process. The high surface area electrode materials explored in this work include a synthetic carbon xerogel for use in a double-layer capacitor, a cobalt oxide xerogel for use in a pseudocapacitor, and a carbon-ruthenium xerogel composite, which utilizes both double-layer and faradaic capacitances. The preparation conditions of these materials were investigated in detail to maximize the surface area and optimize the pore size so that more energy could be stored while minimizing mass transfer limitations. The microstructures of the materials were also correlated with their performance as electrochemical capacitors to improve their energy and power densities. Finally, an idealistic mathematical model, including both double-layer and faradaic processes, was developed and solved numerically. This model can be used to perform the parametric studies of an electrochemical capacitor so as to gain a better understanding of how the capacitor works and also how to improve cell operations and electrode materials design.

  1. Control size of silver nanoparticles in sol-gel glasses

    Science.gov (United States)

    Renteria, Victor M.; Celis, Antonio C.; Garcia-Macedo, Jorge A.

    2000-10-01

    By the sol-gel processing, silver ions in presence of stabilizing function (3-thiocyanatopropyl)triethoxysilane are reduced by heating gels at 180 C for several times in air atmosphere. The spectroscopic Uv-Vis observations, confirm silver nanoparticles presence with peak maximum around 350 nm. The optical properties of the metallic particles are observed at room temperature as function of time, and the absorption spectra practically do not change, which indicated they are trapped and stabilized within the fine porous silica cage. Mie theory calculations, considering the mean free path effect of the conduction electrons, are compatible with experimental spectra, indicating homogeneity in size and form of the metallic nanoparticles. Smithard correlation curve, between half width height (W1/2) of the optical absorption and the particle diameter 2r, predict silver particles size between 4 and 10 nm, during composite heating. Activation energy was measured and compared with previous data on similar systems and the probable reduction process are discussed.

  2. Synthesis of Titania-Silica Materials by Sol-Gel

    Directory of Open Access Journals (Sweden)

    Rubia F. S. Lenza

    2002-10-01

    Full Text Available In this work TiO2-SiO2 glasses containing as much as 20 mol % of TiO2 were prepared via sol-gel process using titanium and silicon alkoxides, in the presence of chlorine, in the form of titanium tetrachloride or HCl. The gels were heat-treated until 800 °C. X-ray diffraction and Fourier transform infrared spectroscopy were used to understand the structural properties of TiO2-SiO2 oxides calcined at different temperatures and to evaluate the homogeneity of these materials. The degree of the compactness of the silica network is inferred from the frequency of the asymmetric stretching vibrations of Si-O-Si bonds. Formation of Si-O-Ti bridges, as monitored by the intensity of characteristic 945 cm-1 ¾ 960 cm-1 vibration, is particularly prominent if the method of basic two-step prehydrolysis of silicon alkoxide, addition of titanium alkoxide and completion of hydrolysis was used.

  3. Porous olivine composites synthesized by sol-gel technique

    Energy Technology Data Exchange (ETDEWEB)

    Dominko, R.; Bele, M.; Gaberscek, M.; Jamnik, J. [National Institute of Chemistry, P.O. Box 660, SI-1001 Ljubljana (Slovenia); Remskar, M.; Hanzel, D. [Jozef Stefan Institute, Jamova 39, SI-1000 Ljubljana (Slovenia); Goupil, J.M. [ENSICAEN, UMR CNRS 6506, Catalyse and Spectrochimie Lab, F-14050 Caen (France); Pejovnik, S. [Faculty of Chemistry and Chemical Technology, University of Ljubljana, Askerceva 5, SI-1000 Ljubljana (Slovenia)

    2006-02-28

    Porous LiMPO{sub 4}/C composites (where M stands for Fe and/or Mn) with micro-sized particles were synthesised by sol-gel technique. Particles porosity is discussed in terms of qualitative results obtained from SEM micrographs and in terms of quantitative results obtained from N{sub 2} adsorption isotherms. Porous particles could be described as an inverse picture of nanoparticulate arrangement, where the pores serve as channels for lithium supply and the distance between the pores determines the materials kinetics. Tests show that the electrochemical behaviour of porous LiMPO{sub 4}/C composite is comparable with the results from the literature. The best electrochemical results were obtained with a LiFePO{sub 4}/C composite (over 140mAhg{sup -1} at C/2 rate during continuous cycling). The capacity obtained with LiMnPO{sub 4}/C composite is much lower (40mAhg{sup -1} at C/20 rate), although the textural properties are similar to those observed in the LiFePO{sub 4}/C composite. (author)

  4. Sol-gel-cum-hydrothermal synthesis of mesoporous Co-Fe@Al2O3 ...

    Indian Academy of Sciences (India)

    Oxides; sol-gel; adsorption; surface properties; composite materials. 1. Introduction. Industrial dyes ... acid green 25, Congo red, N719), phenolic compounds. (bromophenol blue .... microscopy (TEM) images were obtained using Philips CM.

  5. The role of crosslinkers in epoxy-amine crosslinked silicon sol-gel barrier protection coatings

    International Nuclear Information System (INIS)

    Vreugdenhil, A.J.; Gelling, V.J.; Woods, M.E.; Schmelz, J.R.; Enderson, B.P.

    2008-01-01

    The search for chromate replacements in corrosion prevention materials has identified the use of hybrid sol-gel coatings as one, very promising approach. Appropriately functionalized hybrid sol-gel materials can be crosslinked to enhance their chemical durability and mechanical strength. In this work, we evaluate three crosslinkers used in a tetramethoxysilane-glycidoxypropyltrimethoxysilane binary sol-gel system in order to identify the role of the crosslinkers in corrosion protection. The crosslinkers examined were ethylenediamine, N-aminethylepiperazine, and diethylenetriamine. The sol-gel coatings were examined by contact angle, atomic force microscopy, and electrochemical impedance spectroscopy (EIS). Circuit modeling of the EIS results yielded valuable insights into the significant differences between the durabilities of the variously crosslinked coatings. Crosslinker hydrophobicity was identified as not playing a significant role whereas the number of reactive sites per crosslinker and the resulting morphology of the material may be an important parameter

  6. Waveguide fabrication in UV-photocurable sol-gel materials: Influence of the photoinitiating system

    International Nuclear Information System (INIS)

    Versace, D.L.; Oubaha, M.; Copperwhite, R.; Croutxe-Barghorn, C.; MacCraith, B.D.

    2008-01-01

    In this paper we identify and explain the different chemical interactions involved between a sol-gel matrix and photoinitiators used in the fabrication of optical waveguides. A well-established sol-gel matrix composed of 3-methacryloxypropyltrimethoxysilane, zirconium n-propoxide and methacrylic acid was developed, and two different photoinitiators (Irgacure (registered) 819 and 1800) were added to the host matrix. Optical microscopy was used to characterise the structure of the waveguides as a function of the photoinitiator nature and concentration, and aging of the hybrid sol-gel material. It is clearly demonstrated that the width of the waveguides is strongly influenced by the sol aging. Furthermore, it is shown that degradation of photoinitiators occurs during the sol-gel process. Oxidation of the phosphonyl groups by the zirconium complex accounts for this results

  7. Synthesis of Hollow Sphere and 1D Structural Materials by Sol-Gel Process.

    Science.gov (United States)

    Li, Fa-Liang; Zhang, Hai-Jun

    2017-08-25

    The sol-gel method is a simple and facile wet chemical process for fabricating advanced materials with high homogeneity, high purity, and excellent chemical reactivity at a relatively low temperature. By adjusting the processing parameters, the sol-gel technique can be used to prepare hollow sphere and 1D structural materials that exhibit a wide application in the fields of catalyst, drug or gene carriers, photoactive, sensors and Li-ion batteries. This feature article reviewed the development of the preparation of hollow sphere and 1D structural materials using the sol-gel method. The effects of calcination temperature, soaking time, pH value, surfactant, etc., on the preparation of hollow sphere and 1D structural materials were summarized, and their formation mechanisms were generalized. Finally, possible future research directions of the sol-gel technique were outlined.

  8. Porous alumina scaffold produced by sol-gel combined polymeric sponge method

    Science.gov (United States)

    Hasmaliza, M.; Fazliah, M. N.; Shafinaz, R. J.

    2012-09-01

    Sol gel is a novel method used to produce high purity alumina with nanometric scale. In this study, three-dimensional porous alumina scaffold was produced using sol-gel polymeric sponge method. Briefly, sol gel alumina was prepared by evaporation and polymeric sponge cut to designated sizes were immersed in the sol gel followed by sintering at 1250 and 1550°C. In order to study the cell interaction, the porous alumina scaffold was sterilized using autoclave prior to Human Mesenchymal Stem Cells (HMSCs) seeding on the scaffold and the cell proliferation was assessed by alamarBlue® assay. SEM results showed that during the 21 day period, HMSCs were able to attach on the scaffold surface and the interconnecting pores while maintaining its proliferation. These findings suggested the potential use of the porous alumina produced as a scaffold for implantation procedure.

  9. Preparation of oxide glasses from metal alkoxides by sol-gel method

    Science.gov (United States)

    Kamiya, K.; Yoko, T.; Sakka, S.

    1987-01-01

    An investigation is carried out on the types of siloxane polymers produced in the course of the hydrolysis of silicon tetraethoxide, as well as the preparation of oxide glasses from metal alkoxides by the sol-gel method.

  10. Environmentally Benign Sol-Gel Surface Treatment for Aluminum Bonding Applications

    National Research Council Canada - National Science Library

    Osborne, Joseph

    1996-01-01

    A surface treatment process for aluminum using sol-gel chemistry has been developed that produces strong adhesive bonds without the rinse water requirements of traditional anodizing or etching processes...

  11. Extraction of Silica from Cassava Periderm using Modified Sol-Gel ...

    African Journals Online (AJOL)

    Akorede

    6School of Chemical and Metallurgical Engineering, Faculty of Engineering and the Built ... glycol as capping agent in modified sol-gel method for ..... Effect of Organic Acid Treatment on the Properties of ... Journal of Analytical and Applied.

  12. Nanostructured Mesoporous Titanium Dioxide Thin Film Prepared by Sol-Gel Method for Dye-Sensitized Solar Cell

    Directory of Open Access Journals (Sweden)

    Yu-Chang Liu

    2011-01-01

    Full Text Available Titanium dioxide (TiO2 paste was prepared by sol-gel and hydrothermal method with various precursors. Nanostructured mesoporous TiO2 thin-film back electrode was fabricated from the nanoparticle colloidal paste, and its performance was compared with that made of commercial P25 TiO2. The best performance was demonstrated by the DSSC having a 16 μm-thick TTIP-TiO2 back electrode, which gave a solar energy conversion efficiency of 6.03%. The ability of stong adhesion on ITO conducting glass substrate and the high surface area are considered important characteristics of TiO2 thin film. The results show that a thin film with good adhesion can be made from the prepared colloidal paste as a result of alleviating the possibility of electron transfer loss. One can control the colloidal particle size from sol-gel method. Therefore, by optimizing the preparation conditions, TiO2 paste with nanoparticle and narrow diameter distribution was obtained.

  13. Evaluation of the photocatalytic ability of a sol-gel-derived MgO-ZrO2 oxide material

    Directory of Open Access Journals (Sweden)

    Ciesielczyk Filip

    2017-02-01

    Full Text Available This paper deals with the synthesis and characterization of a novel group of potential photocatalysts, based on sol-gel-derived MgO-ZrO2 oxide material. The material was synthesized in a typical sol-gel system using organic precursors of magnesia and zirconia, ammonia as a promoter of hydrolysis and methanol as a solvent. All materials were thoroughly analyzed, including morphology and particle sizes, chemical composition, identification of characteristic functional groups, porous structure parameters and crystalline structure. The proposed methodology of synthesis resulted in obtaining pure MgO-ZrO2 oxide material with micrometric-sized particles and a relatively high surface area. The samples underwent an additional calcination process which led to the crystalline phase of zirconia being formed. The key element of the study was the evaluation of the effectiveness of decomposition of C.I. Basic Blue 9 dye. It was shown that the calcined materials exhibit both satisfactory adsorption and photocatalytic activity with respect to the decomposition of a selected model organic impurity. Total dye removal varied in the range of 50-70%, and was strongly dependent on process parameters such as quantity of photocatalyst, time of irradiation, and the addition of promoters.

  14. Sol-gel immobilization as a suitable technique for enhancement of α-amylase activity of Aspergillus oryzae PP.

    Science.gov (United States)

    Evstatieva, Yana; Yordanova, Mariya; Chernev, Georgi; Ruseva, Yanislava; Nikolova, Dilyana

    2014-07-04

    Bioencapsulation of microbial cells in silica-based matrices has proved to be a good strategy to enhance the biosynthetic capabilities and viability of bioproducers. In the present study, mycelium and pellet cultures of strain Aspergillus oryzae PP were successfully immobilized in sol-gel hybrid matrices composed of tetraethylorthosilicate as an inorganic precursor, 5% (w/v) starch and 10 or 15% (w/v) polyethylene oxide, or 10% (w/v) calcium alginate as organic compounds. Biosynthetic activity of immobilized cultures was investigated by batch and fed-batch cultivation and the obtained results of 3042.04 IU cm -3 were comparable with the enzyme activity of the free cell culture. Immobilized cultures retained their viability and biosynthetic capabilities up to the 744th h during fed-batch fermentation processes. Consequently, sol-gel encapsulation in hybrid matrices could be considered as a promising technique for immobilization of Aspergillus oryzae PP in order to increase the α-amylase production.

  15. Synthesis of yttrium silicate luminescent materials by sol-gel method

    International Nuclear Information System (INIS)

    Arkhipov, D.V.; Vasina, O.Yu.; Popovich, N.V.; Galaktionov, S.S.; Soshchin, N.P.

    1996-01-01

    Several yttrium-silicate composition with Y 2 O 3 content within 44-56% have been synthesized. it is ascertained that employment of sol-gel technique permits preparation of luminescent materials on yttrium silicate basis, which compare favourably with bath-produced specimens. The influence of phase composition of sol-gel phosphors on basic performance indices: intensity and luminescence spectrum, has been analyzed

  16. Strength of interactions between immobilized dye molecules and sol-gel matrices.

    Science.gov (United States)

    Ismail, Fanya; Schoenleber, Monika; Mansour, Rolan; Bastani, Behnam; Fielden, Peter; Goddard, Nicholas J

    2011-02-21

    In this paper we present a new theory to re-examine the immobilization technique of dye doped sol-gel films, define the strength and types of possible bonds between the immobilized molecule and sol-gel glass, and show that the immobilized molecule is not free inside the pores as was previously thought. Immobilizing three different pH sensitive dyes with different size and functional groups inside the same sol-gel films revealed important information about the nature of the interaction between the doped molecule and the sol-gel matrix. The samples were characterized by means of ultraviolet-visible spectrophotometer (UV-VIS), thermal gravimetric analysis (TGA), mercury porosimetry (MP), nuclear magnetic resonance spectroscopy ((29)Si NMR) and field-emission environmental scanning electron microscopy (ESEM-FEG). It was found that the doped molecule itself has a great effect on the strength and types of the bonds. A number of factors were identified, such as number and types of the functional groups, overall charge, size, pK(a) and number of the silanol groups which surround the immobilized molecule. These results were confirmed by the successful immobilization of bromocresol green (BCG) after a completely polymerized sol-gel was made. The sol-gel consisted of 50% tetraethoxysilane (TEOS) and 50% methyltriethoxysilane (MTEOS) (w/w). Moreover, the effect of the immobilized molecule on the structure of the sol-gel was studied by means of a leaky waveguide (LW) mode for doped films made before and after polymerization of the sol-gel.

  17. Making MgO/SiO2 Glasses By The Sol-Gel Process

    Science.gov (United States)

    Bansal, Narottam P.

    1989-01-01

    Silicon dioxide glasses containing 15 mole percent magnesium oxide prepared by sol-gel process. Not made by conventional melting because ingredients immiscible liquids. Synthesis of MgO/SiO2 glass starts with mixing of magnesium nitrate hexahydrate with silicon tetraethoxide, both in alcohol. Water added, and transparent gel forms. Subsequent processing converts gel into glass. Besides producing glasses of new composition at lower processing temperatures, sol-gel method leads to improved homogeneity and higher purity.

  18. Morphology, structure and optical properties of sol-gel ITO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Stoica, T.F.; Teodorescu, V.S.; Blanchin, M.G.; Stoica, T.A.; Gartner, M.; Losurdo, M.; Zaharescu, M

    2003-08-15

    The alkoxidic route and the spinning deposition were used to prepare monolayer sol-gel indium tin oxide (ITO) films. The morphology and crystalline structure were investigated by cross-section transmission electron microscopy (XTEM) and atomic force microscopy (AFM). The ITO sol-gel mono-layer contains three regions of different porosities. The basic crystalline structure is that of the In{sub 2}O{sub 3} lattice. The optical properties have been studied by optical transmission and spectroscopic ellipsometry.

  19. Sol-Gel Synthesis and Luminescence of Green Light Emitting Phosphors Zn2SiO4/Mn2+

    Institute of Scientific and Technical Information of China (English)

    2006-01-01

    Mn2+ doped Zn2SiO4 phosphors were synthesized by sol-gel method, and the influence of zinc source, Mn2+ dopant concentration and annealing temperature were investigated. Results show that zinc nitrate based precursor with strong green emission intensities is better than zinc acetate based precursor. The intensity of green light emission reaches a peak at 254 nm when the Mn2+ dopant concentration is about 5%( molar percentage). Structural details of the phosphors were examined through X-ray diffractometry, thermogravimetric and differential thermal analysis. The result indicates that they are both rhombohedral structures, which remain amorphous below 700 ℃and crystallize completely around 1 000℃. The luminescent properties of Zn2SiO4/Mn2+ phosphors were characterized by excitation and emission spectra.

  20. Synthesis and characterization of the Pt/SiO2 nanocomposite by the sol-gel method

    Directory of Open Access Journals (Sweden)

    A. Salabat

    2011-01-01

    Full Text Available The silica supported platinum nanoparticles was synthesized by using the sol-gel method. The possibility of using diamminedinitro platinum (II as Pt precursor and effect of metal precursor concentration on the final Pt nanoparticle size was investigated. A stable silica sol was prepared via hydrolysis of tetraethyl orthosilicate (TEOS as a metal alcoxide and condensation reaction. Subsequently, diamminedinitro platinum (II was added to sol to form the Pt/silica sol. After drying and calcination of the sol, the Pt/SiO2 nanocpmposite has been obtained. Crystallographic information and crystalline size of the synthesized Pt/SiO2 were determined by X-ray diffraction (XRD method. Morphology of the nanoparticles and hydrogen-bonding interaction between silanol groups and amine ligands were characterized by SEM and Fourier transform infrared (FTIR spectra, respectively. Transmission Electron Microscopy (TEM was employed in evaluating the distribution and size of the platinum nanoparticles in the silica.

  1. α Fe2O3 films grown by the spin-on sol-gel deposition method

    International Nuclear Information System (INIS)

    Avila G, A.; Carbajal F, G.; Tiburcio S, A.; Barrera C, E.; Andrade I, E.

    2003-01-01

    α-Fe 2 O 3 polycrystalline films with grains larger than 31 nm were grown by the spin-on sol-gel deposition method. The particular sol used was prepared starting from two distinct precursor reagents. Both precursors leaded to similar films. Order within the films was altered by adding tin to the samples. Transmittance measurements confirmed that the hematite phase is obtained by annealing the samples above 400 C and yielded an optical gap of about 2.2 eV, but additional transitions at 2.7 eV were also observed. From RBS measurements it was found that tin inclusion decreases iron content as expected, but also increases oxygen concentration within the films. This last observation was associated to the disorder rise when introducing tin atoms. (Author)

  2. Preparation and characterization of the titanium dioxide thin films used for pH electrode and procaine drug sensor by sol-gel method

    International Nuclear Information System (INIS)

    Liao Yihung; Chou, J.-C.

    2009-01-01

    We used titanium dioxide (TiO 2 ) as the sensing layer of an ion selective pH sensor electrode, and as the substrate for a procaine drug sensitive membrane sensor. The TiO 2 thin films were prepared using sol-gel spin coating technology. We adopted the Ti(OC 4 H 9 ) 4 as the precursor, and added an ethanol solute to obtain the TiO 2 sol. The sol-gel was spun coated onto the indium tin oxide (ITO) substrate. The drug sensitive membrane was coated on the TiO 2 film. We then measured the I DS -V G curves of the TiO 2 ion selective electrode (ISE) pH sensor in pH buffer solutions that had different pH concentrations using a Keithley 236 Semiconductor Parameter Analyzer instrument. The procaine concentration was measured from 10 -2 M to 10 -6 M with the drug sensitive membrane using a HP 34401A Digital Multimeter. We prepared the TiO 2 ISE pH sensor and obtained a high pH sensitivity of 58.73 mV/pH. Uniform TiO 2 films surface structures, with an average roughness (Ra) of 10.211 nm and root mean square roughness (Rms) of 13.01 nm were obtained. The drift effect of the titanium dioxide ion selective pH sensor electrode is 1.97 mV h -1 . The sensitivity of the procaine drug sensor is 55.03 mV pC -1 between 1.0 x 10 -2 mol L -1 and 1.0 x 10 -6 mol L -1 procaine concentrations. The detection limit is 5.0 x 10 -6 mol L -1 . The response time to reach 90% output voltage is 16 s. Forty seconds are required to reach 95% output voltage. The procaine drug sensor 1 x 10 -3 mol L -1 drift test is 3.64 mV h -1 and the variation in output voltage of the repeated measurement is less than 7.4 mV

  3. One-step sol-gel imprint lithography for guided-mode resonance structures.

    Science.gov (United States)

    Huang, Yin; Liu, Longju; Johnson, Michael; C Hillier, Andrew; Lu, Meng

    2016-03-04

    Guided-mode resonance (GMR) structures consisting of sub-wavelength periodic gratings are capable of producing narrow-linewidth optical resonances. This paper describes a sol-gel-based imprint lithography method for the fabrication of submicron 1D and 2D GMR structures. This method utilizes a patterned polydimethylsiloxane (PDMS) mold to fabricate the grating coupler and waveguide for a GMR device using a sol-gel thin film in a single step. An organic-inorganic hybrid sol-gel film was selected as the imprint material because of its relatively high refractive index. The optical responses of several sol-gel GMR devices were characterized, and the experimental results were in good agreement with the results of electromagnetic simulations. The influence of processing parameters was investigated in order to determine how finely the spectral response and resonant wavelength of the GMR devices could be tuned. As an example potential application, refractometric sensing experiments were performed using a 1D sol-gel device. The results demonstrated a refractive index sensitivity of 50 nm/refractive index unit. This one-step fabrication process offers a simple, rapid, and low-cost means of fabricating GMR structures. We anticipate that this method can be valuable in the development of various GMR-based devices as it can readily enable the fabrication of complex shapes and allow the doping of optically active materials into sol-gel thin film.

  4. Controlled release of vancomycin from thin sol-gel films on implant surfaces successfully controls osteomyelitis.

    Science.gov (United States)

    Adams, Christopher S; Antoci, Valentin; Harrison, Gerald; Patal, Payal; Freeman, Terry A; Shapiro, Irving M; Parvizi, Javad; Hickok, Noreen J; Radin, Shula; Ducheyne, Paul

    2009-06-01

    Peri-prosthetic infection remains a serious complication of joint replacement surgery. Herein, we demonstrate that a vancomycin-containing sol-gel film on Ti alloy rods can successfully treat bacterial infections in an animal model. The vancomycin-containing sol-gel films exhibited predictable release kinetics, while significantly inhibiting S. aureus adhesion. When evaluated in a rat osteomyelitis model, microbiological analysis indicated that the vancomycin-containing sol-gel film caused a profound decrease in S. aureus number. Radiologically, while the control side showed extensive bone degradation, including abscesses and an extensive periosteal reaction, rods coated with the vancomycin-containing sol-gel film resulted in minimal signs of infection. MicroCT analysis confirmed the radiological results, while demonstrating that the vancomycin-containing sol-gel film significantly protected dense bone from resorption and minimized remodeling. These results clearly demonstrate that this novel thin sol-gel technology can be used for the targeted delivery of antibiotics for the treatment of periprosthetic as well as other bone infections. Copyright 2008 Orthopaedic Research Society

  5. Highly sensitive determination of hydroxylamine using fused gold nanoparticles immobilized on sol-gel film modified gold electrode

    Energy Technology Data Exchange (ETDEWEB)

    Kannan, P. [Department of Chemistry, Gandhigram Rural University, Gandhigram 624302, Dindigul, Tamilnadu (India); John, S. Abraham, E-mail: abrajohn@yahoo.co.in [Department of Chemistry, Gandhigram Rural University, Gandhigram 624302, Dindigul, Tamilnadu (India)

    2010-03-24

    We are reporting the highly sensitive determination of hydroxylamine (HA) using 2-mercapto-4-methyl-5-thiazoleacetic acid (TAA) capped fused spherical gold nanoparticles (AuNPs) modified Au electrode. The fused TAA-AuNPs were immobilized on (3-mercaptopropyl)-trimethoxysilane (MPTS) sol-gel film, which was pre-assembled on Au electrode. The immobilization of fused TAA-AuNPs on MPTS sol-gel film was confirmed by UV-vis absorption spectroscopy and atomic force microscopy (AFM). The AFM image showed that the AuNPs retained the fused spherical morphology after immobilized on sol-gel film. The fused TAA-AuNPs on MPTS modified Au electrode were used for the determination of HA in phosphate buffer (PB) solution (pH = 7.2). When compared to bare Au electrode, the fused AuNPs modified electrode not only shifted the oxidation potential of HA towards less positive potential but also enhanced its oxidation peak current. Further, the oxidation of HA was highly stable at fused AuNPs modified electrode. Using amperometric method, determination of 17.5 nM HA was achieved for the first time. Further, the current response of HA increases linearly while increasing its concentration from 17.5 nM to 22 mM and a detection limit was found to be 0.39 nM (S/N = 3). The present modified electrode was also successfully used for the determination of 17.5 nM HA in the presence of 200-fold excess of common interferents such as urea, NO{sub 2}{sup -}, NH{sub 4}{sup +}, oxalate, Mn{sup 2+}, Na{sup +}, K{sup +}, Mg{sup 2+}, Ca{sup 2+}, Ba{sup 2+} and Cu{sup 2+}. The practical application of the present modified electrode was demonstrated by measuring the concentration of HA in ground water samples.

  6. Resultados preliminares sobre un proceso Sol-Gel para la síntesis de disoluciones precursoras de láminas delgadas ferroeléctricas con estructura de Perovskita laminar

    Directory of Open Access Journals (Sweden)

    Calzada, M. L.

    1999-10-01

    Full Text Available SrBi2Ta2O9 precursor solutions have been prepared by sol-gel using, as reactives, tantalum ethoxide and strontium and bismuth 2-ethyl-hexanoates. These compounds were disolved in 1,3-propanediol as majoritary solvent. The resulting solutions had low hydrolysis and condensation, thus making possible their manipulation and storage in atmospheres with moisture. Films deposited from these solutions were crystallised at 750ºC, developing, as majoritary phase, the SrBi2Ta2O9 layered perovskite. Electric poling of these films indicates a moderate ferroelectric response with values of remanent polarisation of Pr~1μC/cm2.

    Se han preparado por sol-gel soluciones precursoras de SrBi2Ta2O9, utilizando como reactivos el etóxido de tántalo y los 2-etilhexanoatos de estroncio y de bismuto. Como disolvente mayoritario se empleó el 1,3-propanodiol. Las soluciones resultantes presentaron una baja velocidad de hidrólisis y condensación, haciendo posible su almacenaje y manipulación en atmósferas no exentas de humedad. Las láminas derivadas de estas soluciones y cristalizadas a 750ºC presentaron como fase mayoritaria la perovskita laminar de SrBi2Ta2O9. La polarización eléctrica de estas láminas puso de manifiesto una moderada actividad ferroeléctrica, con valores de polarización remanente de Pr~1μC/cm2.

  7. Study of alumosilicate porcelains: Sol-gel preparation, characterization and erosion evaluated by gravimetric method

    International Nuclear Information System (INIS)

    Bogdanoviciene, Irma; Jankeviciute, Audrone; Pinkas, Jiri; Beganskiene, Aldona; Kareiva, Aivaras

    2008-01-01

    In this paper, the sol-gel synthesis and characteristic properties of kalsilite-type alumosilicates (KAlSiO 4 and K 0.5 Na 0.5 AlSiO 4 ) are reported. The polycrystalline powders were characterized by thermal analysis (TG/DTA), powder X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM). Single-phase kalsilite oxides have been obtained after annealing precursor gels for 5 h in the temperature range of 750-850 deg. C. It was demonstrated that crystallinity of the samples slightly depends on the temperature of annealing. From the results obtained, it could be concluded that the KAlSiO 4 solids are composed of the volumetric plate-like grains with no regular size (from 5 μm to 30 μm at 750 deg. C and around 5-50 μm at 850 deg. C). Larger crystallites for mixed potassium-sodium kalsilite have formed (from 10 μm to 80 μm at 750 deg. C and >100 μm at 850 deg. C) in comparison with potassium kalsilite samples). The erosion of obtained dental porcelain samples stored in saliva, beer and Coca-Cola was compared

  8. Sol-gel synthesis of lithium metatitanate as tritium breeding material under different sintering conditions

    Science.gov (United States)

    Lu, Wei; Wang, Jing; Pu, Wenjing; Li, Kaiping; Ma, Shubing; Wang, Weihua

    2018-04-01

    Lithium metatitanate (Li2TiO3) is a promising tritium breeding material candidate for solid blanket of D-T fusion reactors, due to its high mechanical strength, chemical stability, and tritium release rate. In this paper, Li2TiO3 powder with homogeneous crystal structure is synthesized by sol-gel method. The chemical reactions in gel thermal cracking and sintering process are studied by thermo gravimetric/differential scanning calorimetry (TG-DSC). The relationship between the sintering condition and the particle/grain size is characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Results show that below 673 K the gel precursor is completely decomposed and Li2TiO3 phase initially forms. The LiTiO2 by-product formed under the reductive atmosphere in muffle furnace, could be oxidized continually to Li2TiO3 at higher sintering temperature (≥1273 K) for longer sintering time (≥10 h). Both grain and particle sizes rely on a linear growth with the increase of sintering time at 1273 K. Over 1473 K, significant agglomerations exist among particles. The optimal sintering condition is selected as 1273 K for 10 h, for the purer Li2TiO3 phase (>99%), smaller grain and particle size.

  9. Natamycin based sol-gel antimicrobial coatings on polylactic acid films for food packaging.

    Science.gov (United States)

    Lantano, Claudia; Alfieri, Ilaria; Cavazza, Antonella; Corradini, Claudio; Lorenzi, Andrea; Zucchetto, Nicola; Montenero, Angelo

    2014-12-15

    In this work a comprehensive study on a new active packaging obtained by a hybrid organic-inorganic coating with antimicrobial properties was carried out. The packaging system based on polylactic acid was realised by sol-gel processing, employing tetraethoxysilane as a precursor of the inorganic phase and polyvinyl alcohol as the organic component, and incorporating natamycin as the active agent. Films with different organic-inorganic ratios (in a range between 1:19 and 1:4) were prepared, and the amount of antimycotic entrapped was found to be modulated by the sol composition, and was between 0.18 and 0.25mg/dm(2). FTIR microspectroscopic measurements were used to characterise the prepared coatings. The antifungal properties of the films were investigated against mould growth on the surface of commercial semi-soft cheese. The release of natamycin from the films to ethanol 50% (v/v) was studied by means of HPLC UV-DAD. The maximal level released was about 0.105 mg/dm(2), which is far below the value allowed by legislation. Copyright © 2014 Elsevier Ltd. All rights reserved.

  10. Preparation, microstructure and properties of yttrium aluminum garnet fibers prepared by sol-gel method

    Energy Technology Data Exchange (ETDEWEB)

    Li Chengshun [Key Laboratory for Liquid Structure and Heredity of Materials of Ministry of Education, Shandong University, Jinan 250061 (China); Zhang Yujun [Key Laboratory for Liquid Structure and Heredity of Materials of Ministry of Education, Shandong University, Jinan 250061 (China)], E-mail: yujunzhangcn@sdu.edu.cn; Gong Hongyu; Zhang Jingde; Nie Lifang [Key Laboratory for Liquid Structure and Heredity of Materials of Ministry of Education, Shandong University, Jinan 250061 (China)

    2009-01-15

    Yttrium aluminum garnet (YAG) fiber was prepared by sol-gel method using water as the solvent. The spinnable YAG sol was synthesized using Al powder, Y(CH{sub 3}COOH){sub 3}.4H{sub 2}O and HCl as precursors, polyethylene oxide as viscosity adjusting agent. Gel fibers with diameter of 5-10 {mu}m were prepared from the YAG sol by using centrifugal spinning technique. YAG crystalline fibers were obtained by drying gel fibers and heat-treating at selected temperature. TG/DTA analysis showed an exotherm at 906 deg. C attributed to formation of YAG phase and weight loss of 45% at 1000 deg. C. XRD and FT-IR analysis showed that phase-pure YAG can be formed at 900 deg. C, and no other intermediate was observed. The grain size of YAG fibers increased from 25 to 220 nm and tensile strength decreased rapidly from 970 to 380 MPa when the sintering temperature increased from 900 to 1550 deg. C.

  11. Synthesis and Characterization of ZNO/MN Nanocomposite by using Sol-Gel Method

    Science.gov (United States)

    Ningsih, S. K. W.; Bahrizal, B.; Nasra, E.; Nizar, U. K.; Farisya, R.

    2018-04-01

    Zink oxide doped Mn nanocomposites were synthesized by simple sol-gel method at low temperature by using combination of aquadest with methanol as the solvent and ethylene glycol as the additive. Zink acetate dehydrate and manganese chloride tetrahydrate were used as the precursors. Composition dopants were 1,3,5,and 7%. The crystals were formed by drying at 110°C for 1 hour, after which they were heated at ± 500°C for 2 hours. The as-prepared ZnO/Mn nanocomposites were characterized by X-ray diffraction (XRD) and UV Diffuse Reflectance Spectrometer (UVDRS). The XRD patterns of the ZnO nanocrystals showed that they are mostly hexagonal wurtzite with specific peaks at 2θ = 31, 34, 36, 47, 56, 63, 66 dan 69. The sizes of the ZnO doped Mn particles produced with 1%, 3%, 5% and 7% were18-95; 17-87; 18-96 19-98 nm, respectively. UVDRS analysis showed that the band gap of the ZnO were 2,60; 2,90; 2,99 dan 3,01 eV for 1%, 3%, 5% and 7% Mn respectively.

  12. Water-based sol-gel synthesis of hydroxyapatite: process development.

    Science.gov (United States)

    Liu, D M; Troczynski, T; Tseng, W J

    2001-07-01

    Hydroxyapatite (HA) ceramics were synthesized using a sol-gel route with triethyl phosphite and calcium nitrate as phosphorus and calcium precursors, respectively. Two solvents, water and anhydrous ethanol, were used as diluting media for HA sol preparation. The sols were stable and no gelling occurred in ambient environment for over 5 days. The sols became a white gel only after removal of the solvents at 60 degrees C. X-ray diffraction showed that apatitic structure first appeared at a temperature as low as 350 degrees C. The crystal size and the HA content in both gels increase with increasing calcination temperature. The type of initial diluting media (i.e., water vs. anhydrous ethanol) did not affect the microstructural evolution and crystallinity of the resulting HA ceramic. The ethanol-based sol dip-coated onto a Ti substrate, followed by calcination at 450 degrees C, was found to be porous with pore size ranging from 0.3 to 1 microm. This morphology is beneficial to the circulation of physiological fluid when the coating is used for biomedical applications. The satisfactory adhesion between the coating and substrate suggests its suitability for load-bearing uses.

  13. High dose thermoluminescence dosimetry performance of Sol-gel synthesized TiO{sub 2} phosphors

    Energy Technology Data Exchange (ETDEWEB)

    Salas J, Ch. J.; Cruz V, C. [Universidad de Sonora, Departamento de Investigacion en Polimeros y Materiales, Apdo. Postal 130, 83000 Hermosillo, Sonora (Mexico); Castillo U, D. M.; Flores M, K. [Universidad de Sonora, Departamento de Ciencias Quimico Biologicas, Apdo. Postal 130, 83000 Hermosillo, Sonora (Mexico); Bernal, R. [Universidad de Sonora, Departamento de Investigacion en Fisica, Apdo. Postal 5-088, 83190 Hermosillo, Sonora (Mexico); Castano, V. M., E-mail: castillouzeta@gmail.com [UNAM, Instituto de Fisica, Centro de Fisica Aplicada y Tecnologia Avanzada, Apdo. Postal 1-1010, Queretaro, Qro. (Mexico)

    2015-10-15

    Full text: TiO{sub 2} is a ceramic material with many applications due to their different crystalline phases (rutile, anatase and brookite). It has attracted attention in several fields because their high mechanical strength, chemical stability and ion-conducting properties. Moreover, in recent years, some research groups gained interest in the thermoluminescence features of TiO{sub 2} concerning their potential use as thermoluminescence dosimeter. In this work, we present experimental results obtained in the first stage of a long-term research project focused in the synthesis of TiO{sub 2} phosphors for dosimetric applications. The thermoluminescent characterization of samples was carried out after being exposed to beta particle irradiation. TiO{sub 2} was prepared by alkoxide sol-gel route using titanium tetrabutoxide as precursor, ethanol, water and ammonia as catalyst. Pellet-shaped samples were annealed at 700 degrees C for 6 h in air atmosphere followed by slow cooling, and then were exposed to radiation doses from 25 to 400 Gy. The glow curves display maxima located at 103 and 238 degrees C when a 5 C/s heating rate is used. From the experimental results here presented, we conclude that TiO{sub 2} is a promising material to develop high dose Tl dosimeters. (Author)

  14. Zinc oxide films impurified with Ti and prepared by the Sol-gel method

    International Nuclear Information System (INIS)

    Tirado G, S.; Cazares R, J.M.; Maldonado, A.

    2006-01-01

    Titanium-doped zinc oxide thin films have been prepared on silicon substrate using the Sol-Gel technique. The structural, morphology, electrical and optical properties of such thin films were studied as a function of titanium concentration (0.5, 1 and 1.5 %) and the thin films thickness. Zinc acetate dihydrate and titanium (VI)-oxy acetylacetonate were used as precursor materials, using 2-methoxyethanol and monoethanolamine as via. The X-ray diffraction spectra show polycrystalline films in all the cases. It can see for all the thin films a preferential growth along the (002) planes where the titanium concentration and also the thin films thickness play an important rule. No structural changes are observed at all. The surface morphology studied shows as the grain size decreases when thin thickness is increases. For titanium concentration of 0.5, 1 and 1.5 % values the grains size increase also. The thin films thickness for titanium concentration of 1.5 % was 500 nm (4v), 400 nm (3v), 180 nm (2v) and 130 nm (1v), values obtained from cross-section micrographs. Highly resistive samples are obtained for substrate soda-lime even showing high transmittance. Better physical properties are required for gas sensors or semitransparent electrodes and other possible applications. (Author)

  15. Thickness controlled sol-gel silica films for plasmonic bio-sensing devices

    Energy Technology Data Exchange (ETDEWEB)

    Figus, Cristiana, E-mail: cristiana.figus@dsf.unica.it; Quochi, Francesco, E-mail: cristiana.figus@dsf.unica.it; Artizzu, Flavia, E-mail: cristiana.figus@dsf.unica.it; Saba, Michele, E-mail: cristiana.figus@dsf.unica.it; Marongiu, Daniela, E-mail: cristiana.figus@dsf.unica.it; Mura, Andrea; Bongiovanni, Giovanni [Dipartimento di Fisica - University of Cagliari, S.P. Km 0.7, I-09042 Monserrato (Canada) (Italy); Floris, Francesco; Marabelli, Franco; Patrini, Maddalena; Fornasari, Lucia [Dipartimento di Fisica - University of Pavia, Via Agostino Bassi 6, I-27100 Pavia (PV) (Italy); Pellacani, Paola; Valsesia, Andrea [Plasmore S.r.l. -Via Grazia Deledda 4, I-21020 Ranco (Vatican City State, Holy See) (Italy)

    2014-10-21

    Plasmonics has recently received considerable interest due to its potentiality in many fields as well as in nanobio-technology applications. In this regard, various strategies are required for modifying the surfaces of plasmonic nanostructures and to control their optical properties in view of interesting application such as bio-sensing, We report a simple method for depositing silica layers of controlled thickness on planar plasmonic structures. Tetraethoxysilane (TEOS) was used as silica precursor. The control of the silica layer thickness was obtained by optimizing the sol-gel method and dip-coating technique, in particular by properly tuning different parameters such as pH, solvent concentration, and withdrawal speed. The resulting films were characterized via atomic force microscopy (AFM), Fourier-transform (FT) spectroscopy, and spectroscopic ellipsometry (SE). Furthermore, by performing the analysis of surface plasmon resonances before and after the coating of the nanostructures, it was observed that the position of the resonance structures could be properly shifted by finely controlling the silica layer thickness. The effect of silica coating was assessed also in view of sensing applications, due to important advantages, such as surface protection of the plasmonic structure.

  16. Sol-gel processing of glasses and glass-ceramics for microelectronic packaging

    International Nuclear Information System (INIS)

    Sriram, M.A.; Kumta, P.N.

    1992-01-01

    In recent years considerable progress has been made in electronic packaging substrate technology. The future need of miniaturization of devices to increase the signal processing speeds calls for an increase in the device density requiring the substrates to be designed for better thermal, mechanical and electrical efficiency. Fast signal propagation with minimum delay requires the substrate to possess very low dielectric constant. Several glasses and glass-ceramic materials have been identified over the years which show good promise as candidate substrate materials. among these borophosphate and borophosphosilicate glass-ceramics have been recently identified to have the lowest dielectric constant. This paper reports that sol-gel processing has been used to synthesize borosilicate, borophosphosilicate and borophosphate glasses and glass-ceramics using inexpensive boron oxide and phosphorus pentoxide precursors. Preliminary results of the processing of these gels and the effect of volatility of boron alkoxide and its modification on the gel structure are described. X-ray diffraction, Differential thermal analyses and FTIR have been used to characterize the as-prepared and heat treated gels

  17. EXAFS Study on LiFePO4 Powders Produced From Two Sol-Gel Routes

    Science.gov (United States)

    Negara, V. S. I.; Latif, C.; Wongtepa, W.; Pratapa, S.

    2018-04-01

    The local structure of LiFePO4 powders has been investigated using Fe K-edge Extended X-Ray Absorption Fine Structure (EXAFS) Spectroscopy data. The synthesis of LFP powders was carried out using two different sol-gel methods. The raw materials for Fe source were ironstone and commercial precursor of FeCl2·4H2O. Synthesis using natural materials produced two phases, namely LiFePO4 olivine and Li3Fe2(PO4)3 nasicon, whereas that using a commercial product produced a single phase of LiFePO4 olivine. The EXAFS data for both samples were collected at Synchrotron Light Research Institute (SLRI), Thailand. Fitting of the model on the experimental curve provided parameters that can be interpreted as the distance between Fe as the absorber and the nearest atoms on the LFP materials. The EXAFS data analysis has shown that synthesis of LFPs using different Fe sources gives slightly different nearest-neighbor distances, namely Fe-O of 0.21% -0.23%, Fe-P of 0.14% - 0.16%, Fe-Fe of 0.12% for both samples, respectively.

  18. Sol-gel processes and materials. January 1970-August 1988 (Citations from the US Patent data base). Report for January 1970-August 1988

    International Nuclear Information System (INIS)

    1988-08-01

    This bibliography contains citations of selected patents concerning Sol-Gel processes and Sol-Gel derived materials and products. Selected patents include Sol-Gel compositions, ceramic and refractory materials, fabrication of silica glass, cataylsts and catalyst supports, nuclear fuels preparation, abrasives for grinding wheels, Sol-Gel production of microspheres, Sol-Gel thin films and coatings, photographic materials, and dental materials. (Contains 71 citations fully indexed and including a title list.)

  19. Application of sol gel spin coated yttria-stabilized zirconia layers for the improvement of solid oxide fuel cell electrolytes produced by atmospheric plasma spraying

    Energy Technology Data Exchange (ETDEWEB)

    Rose, Lars [University of British Columbia, Department of Materials Engineering, 309-6350 Stores Road, Vancouver, British Columbia, V6T 1Z4 (Canada); National Research Council, Institute for Fuel Cell Innovation, 4250 Wesbrook Mall, Vancouver, British Columbia, V6T 1W5 (Canada); Kesler, Olivera [National Research Council, Institute for Fuel Cell Innovation, 4250 Wesbrook Mall, Vancouver, British Columbia, V6T 1W5 (Canada); University of British Columbia, Department of Mechanical Engineering, 2054-6250 Applied Science Lane, Vancouver, British Columbia, V6T 1Z4 (Canada); Tang, Zhaolin; Burgess, Alan [Northwest Mettech Corp., 467 Mountain Hwy, North Vancouver, British Columbia, V7J 2L3 (Canada)

    2007-05-15

    Due to its high thermal stability and purely oxide ionic conductivity, yttria-stabilized zirconia (YSZ) is the most commonly used electrolyte material for solid oxide fuel cells (SOFCs). Standard electrolyte fabrication techniques for planar SOFCs involve wet ceramic techniques such as tape-casting or screen printing, requiring sintering steps at temperatures above 1300 C. Plasma spraying (PS) may provide a more rapid and cost efficient method to produce SOFCs without sintering. High-temperature sintering requires long processing times and can lead to oxidation of metal alloys used as mechanical supports, or to detrimental interreactions between the electrolyte and adjacent electrode layers. This study investigates the use of spin coated sol gel derived YSZ precursor solutions to fill the pores present in plasma sprayed YSZ layers, and to enhance the surface area for reaction at the electrolyte-cathode interface, without the use of high-temperature firing steps. The effects of different plasma conditions and sol concentrations and solid loadings on the gas permeability and fuel cell performance have been investigated. (author)

  20. Structural and Luminescence Properties of Lu2O3:Eu3+ F127 Tri-Block Copolymer Modified Thin Films Prepared by Sol-Gel Method

    Science.gov (United States)

    de Jesus Morales Ramírez, Angel; Hernández, Margarita García; Murillo, Antonieta García; de Jesús Carrillo Romo, Felipe; Palmerin, Joel Moreno; Velazquez, Dulce Yolotzin Medina; Jota, María Luz Carrera

    2013-01-01

    Lu2O3:Eu3+ transparent, high density, and optical quality thin films were prepared using the sol-gel dip-coating technique, starting with lutetium and europium nitrates as precursors and followed by hydrolysis in an ethanol-ethylene glycol solution. Acetic acid and acetylacetonate were incorporated in order to adjust pH and as a sol stabilizer. In order to increment the thickness of the films and orient the structure, F127 Pluronic acid was incorporated during the sol formation. Structural, morphological, and optical properties of the films were investigated for different F127/Lu molar ratios (0–5) in order to obtain high optical quality films with enhanced thickness compared with the traditional method. X-ray diffraction (XRD) shows that the films present a highly oriented cubic structure beyond 1073 K for a 3-layer film, on silica glass substrates. The thickness, density, porosity, and refractive index evolution of the films were investigated by means of m-lines microscopy along with the morphology by scanning electron microscope (SEM) and luminescent properties. PMID:28809336

  1. Lithium ceramics: sol-gel preparation and tritium release

    International Nuclear Information System (INIS)

    Renoult, O.

    1994-04-01

    Ceramics based on lithium aluminate (LiA1O 2 ), lithium zirconate (Li 2 ZrO 3 ) and lithium titanate (Li 2 TiO 3 ) are candidates as tritium breeder blanket materials for forthcoming nuclear fusion reactors. Lithium silico-aluminate Li 4+x A1 4-3x Si 2x O 8 (0 ≤ x ≤ 0,25) powders were synthetized from alkoxyde-hydroxyde sol-gel route. By direct sintering at 850-1100 deg C (without prior calcination), ceramics with controlled stoichiometry and homogenous microstructure were obtained. We have also prepared, using a comparable method, Li 2 Zr 1-x Ti x O 3 (x = 0, x = 0,1 et x = 1) materials. All these ceramics, with different microstructures and compositions, have been tested in out-of-reactor experiments. Concerning lithium aluminate microporous ceramics, the silicon substitution leads to a significant improvement of the tritrium release. Classical models taking into account independent surface mechanisms are not able to describe correctly the observed tritium release kinetics. We show, using a simple model, that the release kinetics is in fact limited by an intergranular diffusion followed by a desorption. The delay in tritium release, which occurs when the ceramic compacity increases, is explained in terms of an enhancement of the ionic T + diffusion path length. The energy required for desorption includes a leading term independent of hydrogen contained in the sweep gas. This term is attributed to the limiting recombination step of T + in molecular species HTO. For similar microstructures, the facility of tritium release for the different studied materials is explained by three properties: the crystal structure of the ceramic, the acidity of oxides and finally the presence of electronic non-stoichiometric defects. (author). 89 refs., 50 figs., 2 tabs., 1 annexe

  2. Bulk and thick films of the superconducting phase YBa2Cu3O7/sub -//sub y/ made by controlled precipitation and sol-gel processes

    International Nuclear Information System (INIS)

    Barboux, P.; Tarascon, J.M.; Greene, L.H.; Hull, G.W.; Bagley, B.G.

    1988-01-01

    The synthesis of high-temperature superconducting oxides using solution chemistry has been investigated and physical properties are compared to ceramics obtained by conventional solid-state reactions. We report on controlled precipitation and sol-gel processes, both of which produce materials with particle sizes smaller than 5 μm. We find that the superconducting properties of the high T/sub c/ ceramics are affected by their manner of preparation, such that the transitions are slightly lower in temperature, but sharper, for samples made by solution rather than solid-state chemistry. The ability to prepare stable viscous gels provides an opportunity for obtaining large areas of superconducting coatings. For thick films on alumina or silicon substrates, contamination from the substrate is shown to be a problem. Finally, we observe that the sol-gel process lowers the synthesis temperature by 100 0 C.ing,

  3. Structural and optical studies of nano-structure silica gel doped with different rare earth elements, prepared by two different sol -gel techniques

    International Nuclear Information System (INIS)

    Battisha, I.K.; El Beyally, A.; Seliman, S.I.; El Nahrawi, A.S.

    2005-01-01

    Structural and optical characteristics of pure silica gel (silica-xerogel, SiO 2 ) and doped with different concentrations ranging from 1 up to 6% of some rare earth (REEs) ions such as, praseodymium Pr +3 ,and Europium Eu +3 , Erbium Er +3 and Holmium Ho +3 , ions, in the form of thin film and monolith materials were prepared by sol - gel technique, Using tetra-ethoxysilane as precursor materials, which are of particular interest for sol-gel integrated optics applications. Some structural and optical features of sol-gel derived monolith and thin films are analyzed and compared, namely the structure of nano-particle monolith and thin film silica-gel samples, based on X-ray diffraction (XRD). The types of structural information obtainable are compared in detail. It is show that the XRD spectra of a-cristobalite are obtained for the two type materials and even by doping with the four REEs ions. Optical measurements of monolith and thin films were also studied and compared, the normal transmission and specular reflection were measured. The refractive index were calculated and discussed

  4. In vitro toxicity assessment of extracts derived from sol-gel coatings on polycarbonate intended to be used in food contact applications.

    Science.gov (United States)

    Séverin, Isabelle; Lionti, Krystelle; Dahbi, Laurence; Loriot, Catherine; Toury, Bérangère; Chagnon, Marie-Christine

    2016-07-01

    Polycarbonate is a widely used polymer in food contact applications all around the world. However, due to the potential release of Bisphenol A (BPA) during repeated washing cycles, its use becomes compromised as BPA is known for being an endocrine disruptor for rodents. In order to tackle this issue, sol-gel coatings based on organoalkoxysiloxane were developed on PC, to act as a physical barrier. To this end, two sol-gel systems based on tetraethylorthosilicate (TEOS), methyltriethoxysilane (MTES) and 3-glycidyloxypropyltriethoxysilane (GPTES), three common sol-gel precursors, were prepared. The coatings derived from the latter two systems were then studied with regards to their potential toxicity in vitro. Migration tests were performed in food simulants, and the maximal migration was obtained in ethanol 10% (v/v) for one system and in isooctane for the other one. In vitro genotoxicity was assessed with the Ames test (OECD 471) and the micronucleus assay (OECD 487), and no genotoxic effect was observed. Moreover, the estrogenic activity of the extracts was studied with a transcriptional activation assay using transient transfection in human cells; none of the extracts was found estrogenic. These negative in vitro results are highly promising for the future use of these new barrier coating formulations onto food contact materials. Copyright © 2016 Elsevier Ltd. All rights reserved.

  5. Infrared and Raman spectroscopic studies of tris-[3-(trimethoxysilyl)propyl] isocyanurate, its sol-gel process, and coating on aluminum and copper.

    Science.gov (United States)

    Li, Ying-Sing; Church, Jeffrey S; Woodhead, Andrea L; Vecchio, Nicolas E; Yang, Johnny

    2014-11-11

    Tris-[3-(trimethoxysilyl)propyl] isocyanurate (TTPI) has been used as a precursor to prepare a sol using ethanol as the solvent under acidic conditions. The sol-gel was applied for the surface treatment of aluminum and copper. Infrared and Raman spectra have been recorded for pure TTPI and the TTPI sol, xerogel and TTPI sol-gel coated metals. From the vibrational spectra, TTPI is likely to have the C1 point group. Vibrational assignments are suggested based on group frequencies, the expected reactions in the sol-gel process and the vibrational studies of some related molecules. From the experimental infrared spectra of xerogels annealed at different temperatures and from the thermal-gravimetric analysis, it is found that the TTPI xerogel decomposes at around 450°C with silica being the major decomposition product. A cyclic voltammetric study of the metal electrodes coated with different concentrations of TTPI ranging from 5% to 42% (v/v) has shown that the films with high concentrations of sol would provide better corrosion protection for aluminum and copper. Copyright © 2014 Elsevier B.V. All rights reserved.

  6. Structural and physicochemical properties of nickel manganite NiMn{sub 2}O{sub 4-δ}synthesized by sol-gel and ultra sound assisted methods

    Energy Technology Data Exchange (ETDEWEB)

    Alburquenque, D. [Materials Chemistry Department, USACH, Ave L.B.O' Higgins 3363, Santiago 9170022 (Chile); Metallurgy Department, USACH, Ave Ecuador 3469, Santiago 9170124 (Chile); Troncoso, L.; Denardin, J.C. [Physics Department, USACH, Ave. Ecuador 3493, Santiago 9170124 (Chile); Butera, A. [Atomic Center, CNEA, Ito. Balseiro, Bariloche Rio Negro 84000 (Argentina); Padmasree, K.D. [Cinvestav, U.Saltillo, Monterrey Km 13.5, Saltillo CP 25900 (Mexico); Ortiz, J.; Herrera, F. [Materials Chemistry Department, USACH, Ave L.B.O' Higgins 3363, Santiago 9170022 (Chile); Marco, J.F. [Institute of Physical Chemistry “Rocasolano”, CSIC, Serrano 119, Madrid 28006 (Spain); Gautier, J.L., E-mail: juan.gautier@usach.cl [Materials Chemistry Department, USACH, Ave L.B.O' Higgins 3363, Santiago 9170022 (Chile)

    2016-07-05

    In this work we present the structural, magnetic and surface characterization of the ceramic nickel manganite oxide NiMn{sub 2}O{sub 4-δ} synthesized by two methods: sol-gel and ultrasound-assisted sol-gel using nitrate salts as precursors. We have characterized the non-stoichiometric samples NiMn{sub 2}O{sub 4-δ} using different physicochemical analyses. X-ray diffraction and Rietveld refinement of the X-ray data indicated that the samples crystallize in the Fd3m space group characteristic of cubic spinel-related oxides. The specific surface area of the oxides was 1.3 m{sup 2}/g (SG) and 16.3 m{sup 2}/g (UASG). SEM results showed particle agglomerates of 1.05 μm (SG) and 0.85 μm (UASG). Temperature dependence magnetization measurements were performed and a ferrimagnetic transition was identified at 103 K and 105 K depending on the preparation method (SG and UASG, respectively). The observed Curie constant was found to vary from 7.4 to 7.7 cm{sup 3} K mol{sup −1} and hysteretic magnetization vs. applied field curves at different temperatures were obtained. XPS studies of these oxides reveal the presence of Ni{sup 2+}, Mn{sup 2+}, Mn{sup 3+} and Mn{sup 4+} ions at the surface. A probable ionic distribution as a function of the synthesis method is proposed. - Highlights: • Nickel manganite was synthesized by sol gel synthesis and a novel ultrasound-assisted sol gel method. . • Bulk and surface cation distributions are proposed. • Physicochemical properties, including magnetic and surface area measurements, were studied for both types of samples.

  7. Sol-gel preparation of ion-conducting ceramics for use in thin films

    International Nuclear Information System (INIS)

    Steinhauser, M.I.

    1992-12-01

    A metal alkoxide sol-gel solution suitable for depositing a thin film of La 0.6 Sr 0.4 CoO 3 on a porous substrate has been developed; such films should be useful in fuel cell electrode and oxygen separation membrane manufacture. Crack-free films have been deposited on both dense and porous substrates by dip-coating and spin-coating techniques followed by a heat treatment in air. Fourier transform infrared spectroscopy was used to determine the chemical structure of metal alkoxide solution system. X-ray diffraction was used to determine crystalline phases formed at various temperatures, while scanning electron microscopy was used to determine physical characteristics of the films. Surface coatings have been successfully applied to porous substrates through the control of the substrate pore size, deposition parameters, and firing parameters. Conditions have been defined for which films can be deposited, and for which the physical and chemical characteristics of the film can be improved. A theoretical discussion of the chemical reactions taking place before and after hydrolysis in the mixed alkoxide solutions is presented, and the conditions necessary for successful synthesis are defined. Applicability of these films as ionic and electronic conductors is discussed

  8. Morphology evolution of ZrB2 nanoparticles synthesized by sol-gel method

    International Nuclear Information System (INIS)

    Zhang Yun; Li Ruixing; Jiang Yanshan; Zhao Bin; Duan Huiping; Li Junping; Feng Zhihai

    2011-01-01

    Zirconium diboride (ZrB 2 ) nanoparticles were synthesized by sol-gel method using zirconium n-propoxide (Zr(OPr) 4 ), boric acid (H 3 BO 3 ), sucrose (C 12 H 22 O 11 ), and acetic acid (AcOH). Clearly, it was a non-aqueous solution system at the very beginning of the reactions. Here, AcOH was used as both chemical modifier and solvent to control Zr(OPr) 4 hydrolysis. Actually, AcOH could dominate the hydrolysis by self-produced water of the chemical propulsion, rather than the help of outer water. C 12 H 22 O 11 was selected, since it can be completely decomposed to carbon. Thus, carbon might be accounted precisely for the carbothermal reduction reaction. Furthermore, we investigated the influence of the gelation temperature on the morphology of ZrB 2 particles. Increasing the gelation temperature, the particle shapes changed from sphere-like particles at 65 deg. C to a particle chain at 75 deg. C, and then form rod-like particles at 85 deg. C. An in-depth HRTEM observation revealed that the nanoparticles of ZrB 2 were gradually fused together to evolve into a particle chain, finally into a rod-like shape. These crystalline nature of ZrB 2 related to the gelation temperature obeyed the 'oriented attachment mechanism' of crystallography. - Graphical Abstract: Increasing the gelation temperature, the particle shapes changed from sphere-like particles at 65 deg. C to a particle chain at 75 deg. C, and then form rod-like particles at 85 deg. C. Highlights: → ZrB 2 nanoparticles were synthesized by sol-gel method in an non-aqueous solution system. → AcOH was used as both chemical modifier and solvent to control Zr(OPr) 4 hydrolysis. → C 12 H 22 O 11 was selected since it can be completely decomposed to carbon. → Increasing the gelation temperature, the particles changed from sphere-like to rod-like ones. → Crystalline nature of ZrB 2 obeyed the 'oriented attachment mechanism' of crystallography.

  9. Lithium ceramics: sol-gel preparation and tritium release; Ceramiques lithiees: elaboration sol-gel et relachement du tritium

    Energy Technology Data Exchange (ETDEWEB)

    Renoult, O

    1994-04-01

    Ceramics based on lithium aluminate (LiA1O{sub 2}), lithium zirconate (Li{sub 2}ZrO{sub 3}) and lithium titanate (Li{sub 2}TiO{sub 3}) are candidates as tritium breeder blanket materials for forthcoming nuclear fusion reactors. Lithium silico-aluminate Li{sub 4+x}A1{sub 4-3x}Si{sub 2x}O{sub 8} (0 {<=} x {<=} 0,25) powders were synthetized from alkoxyde-hydroxyde sol-gel route. By direct sintering at 850-1100 deg C (without prior calcination), ceramics with controlled stoichiometry and homogenous microstructure were obtained. We have also prepared, using a comparable method, Li{sub 2}Zr{sub 1-x}Ti{sub x}O{sub 3} (x = 0, x = 0,1 et x = 1) materials. All these ceramics, with different microstructures and compositions, have been tested in out-of-reactor experiments. Concerning lithium aluminate microporous ceramics, the silicon substitution leads to a significant improvement of the tritrium release. Classical models taking into account independent surface mechanisms are not able to describe correctly the observed tritium release kinetics. We show, using a simple model, that the release kinetics is in fact limited by an intergranular diffusion followed by a desorption. The delay in tritium release, which occurs when the ceramic compacity increases, is explained in terms of an enhancement of the ionic T{sup +} diffusion path length. The energy required for desorption includes a leading term independent of hydrogen contained in the sweep gas. This term is attributed to the limiting recombination step of T{sup +} in molecular species HTO. For similar microstructures, the facility of tritium release for the different studied materials is explained by three properties: the crystal structure of the ceramic, the acidity of oxides and finally the presence of electronic non-stoichiometric defects. (author). 89 refs., 50 figs., 2 tabs., 1 annexe.

  10. Size control of nanocrystals in InGaZnO4 thin films fabricated by using the sol-gel method

    International Nuclear Information System (INIS)

    Seo, S. J.; Cho, J. H.; Jang, Y. H.; Kim, C. H.

    2012-01-01

    We report the structural properties of InGaZnO 4 (IGZO) thin films prepared by using the sol-gel method. The structural properties of IGZO thin films were controlled by using the film thickness and thermal annealing temperature. In this study, the crystallization temperature of amorphous IGZO thin films was observed to be about 700 .deg. C. Also, we observed that the crystal size of IGZO thin films increased as the thickness and the annealing temperature were increased. In addition, we could observe that the atomic ratio of In, Ga and Zn of the IGZO thin film was slightly different from the molar ratio of a previous IGZO sol-gel solution (In:Ga:Zn = 1:1:1) post-annealed at 900 .deg. C because In and Zn are more volatile than Ga. The study of the crystallization of amorphous IGZO thin films provides an understanding of the growth mechanisms and thermal annealing effects for IGZO nanocrystals.

  11. Low temperature synthesis of hydroxyapatite nano-rods by a modified sol-gel technique

    International Nuclear Information System (INIS)

    Jadalannagari, Sushma; More, Sandeep; Kowshik, Meenal; Ramanan, Sutapa Roy

    2011-01-01

    Hydroxyapatite (HAp) nano-rods were successfully synthesized by a modified sol-gel method using a solution of CaCl 2 .2H 2 O in water, along with a solution of H 3 PO 4 in triethylamine and NH 4 OH as starting materials. The Ca/P molar ratio was maintained at 1.67. The sol obtained was dried in an oven for 2 days at 100 deg. C after being dialyzed for 12 h. Pellets were made from the crystalline powders and immersed in simulated body fluid (SBF) to check its biocompatibility after 15, 45 and 180 days of immersion. The HAp powders and pellets were characterized by X-Ray Diffraction crystallography (XRD), Fourier transform Infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and Transmission electron microscopy (TEM). The HAp nano-rods had an average diameter of 25 nm and length 110-120 nm. Immersion of the HAp pellets in SBF led to the formation of a highly porous interconnecting HAp layer on the surface. The porosity increased with increase in immersion time. Highlights: → Low temperature synthesis of hydroxyapatite nanorods using Ca and P sources and triethylamine. → The synthesis time was only 0.5 hours. → Crystalline material was obtained after drying at 100oC only in air. → SBF studies showed the HAP bodies to be biocompatible.

  12. Microstructure, optical, and electrochromic properties of sol-gel nanoporous tungsten oxide films

    Science.gov (United States)

    Djaoued, Yahia; Ashrit, P. V.; Badilescu, S.; Bruning, R.

    2003-08-01

    Porous tungsten oxide films have been prepared by a nonhydrolitic sol-gel method using poly(ethylene glycol) (PEG) as a structure directing agent. The method entails the hydrolysis of an ethanolic solution of tungsten ethoxide (formed by the reaction of WCl6 with ethanol) followed by condensation and polymerization at the PEG-tungsten oxide oligometers interface. A highly porous WO3 framework was obtained after PEG was burned off by calcination at a relativley low temperature. AFM images of the films treated thermally show an ordered material rather than microscopic particulates. Both fibrilar nanostructures and striped phase can be obtained via this approach, depending on the concentration of PEG in the coating solution. XRD data from the fibrils indicate that they are crystalline with very small crystals, whereas the striped phases obtained with 20% PEG correspond to two crystalline phases, one, the stoichiometric WO3 and the other one an oxygen deficient phase, containing larger crystals (~28 nm). The results show that PEG promotes the formation of oxygen deficient phases and delays crystallization. Compared to WO3 with no PEG, the optical and electrochromic properties of the macroporous tungsten oxide films appear to be significantly improved. The formation of organized nanostructures is tentatively accounted for by the strong hydrogen bonding interactions between PEG and the tungsten oxide oligomers.

  13. Composite coating prepared by micro-arc oxidation followed by sol-gel process and in vitro degradation properties

    International Nuclear Information System (INIS)

    Zhang Yi; Bai Kuifeng; Fu Zhenya; Zhang Caili; Zhou Huan; Wang Liguo; Zhu Shijie; Guan Shaokang; Li Dongsheng; Hu Junhua

    2012-01-01

    A Mg phosphate coating was prepared on home-developed Mg-Zn-Ca alloy to improve its anticorrosion performance in simulated body fluid (SBF, Kokubo solution). The coating was prepared by micro-arc oxidation (MAO) method at the working voltage of 120-140 V. Evident improvement of anticorrosion was obtained even through the surface was porous. To further diminish the contact with SBF, a TiO 2 layer was coated on the porous MAO layer by sol-gel dip coating followed by an annealing treatment. The coatings were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM) and energy dispersion spectroscopy (EDS). The electrochemical performance of the MAO and TiO 2 /MAO coated alloys was evaluated by anodic polarization measurements. The pores on Mg phosphate layer provided accommodation sites for the subsequent TiO 2 sol-gel coating which sealed the pores and hence significantly enhanced the anticorrosion while single MAO coating only improve anticorrosion within a limited range. The present result indicates that fabrication of composite coatings is a significant strategy to improve the corrosion resistance of Mg-Zn-Ca alloy and other alloys, thus enhancing the potential of using Mg alloys as bio-implants.

  14. Double-Layer Surface Modification of Polyamide Denture Base Material by Functionalized Sol-Gel Based Silica for Adhesion Improvement.

    Science.gov (United States)

    Hafezeqoran, Ali; Koodaryan, Roodabeh

    2017-09-21

    Limited surface treatments have been proposed to improve the bond strength between autopolymerizing resin and polyamide denture base materials. Still, the bond strength of autopolymerizing resins to nylon polymer is not strong enough to repair the fractured denture effectively. This study aimed to introduce a novel method to improve the adhesion of autopolymerizing resin to polyamide polymer by a double layer deposition of sol-gel silica and N-2-(aminoethyl)-3-aminopropyltrimethoxysilane (AE-APTMS). The silica sol was synthesized by acid-catalyzed hydrolysis of tetraethylorthosilicate (TEOS) as silica precursors. Polyamide specimens were dipped in TEOS-derived sol (TS group, n = 28), and exposed to ultraviolet (UV) light under O 2 flow for 30 minutes. UV-treated specimens were immersed in AE-APTMS solution and left for 24 hours at room temperature. The other specimens were either immersed in AE-APTMS solution (AP group, n = 28) or left untreated (NT group, n = 28). Surface characterization was investigated by fourier transform infrared spectroscopy (FTIR) and atomic force microscopy (AFM). Two autopolymerizing resins (subgroups G and T, n = 14) were bonded to the specimens, thermocycled, and then tested for shear bond strength with a universal testing machine. Data were analyzed with one-way ANOVA followed by Tukey's HSD (α = 0.05). FTIR spectra of treated surfaces confirmed the chemical modification and appearance of functional groups on the polymer. One-way ANOVA revealed significant differences in shear bond strength among the study groups. Tukey's HSD showed that TS T and TS G groups had significantly higher shear bond strength than control groups (p = 0.001 and p < 0.001, respectively). Moreover, bond strength values of AP T were statistically significant compared to controls (p = 0.017). Amino functionalized TEOS-derived silica coating is a simple and cost-effective method for improving the bond strength between the autopolymerizing resin and polyamide

  15. Proteic sol-gel synthesis of copper doped misfit Ca-cobaltites with potential SOFC application

    Energy Technology Data Exchange (ETDEWEB)

    Lima, Chrystian G.M. [Materials Science and Engineering Postgraduate Program, UFPB, 58051-900, João Pessoa (Brazil); Silva, Rinaldo M. [Department of Chemical Engineering, UFPB, 58051-900, João Pessoa (Brazil); Aquino, Flávia de M. [Alternative and Renewable Energy Center, UFPB, 58051-900, João Pessoa (Brazil); Raveau, Bernard; Caignaert, Vincent [Laboratoire CRISMAT ENSICAEN UMR CNRS 6508, 6 Boulevard du Maréchal Juin, 14050, Caen Cedex 04 (France); Cesário, Moisés R., E-mail: moises.cesario@ensicaen.fr [Laboratoire CRISMAT ENSICAEN UMR CNRS 6508, 6 Boulevard du Maréchal Juin, 14050, Caen Cedex 04 (France); Macedo, Daniel A., E-mail: damaced@gmail.com [Materials Science and Engineering Postgraduate Program, UFPB, 58051-900, João Pessoa (Brazil)

    2017-02-01

    The present work reports the synthesis, structure and electrochemical assessment of Cu-doped calcium cobaltites as cathode materials for solid oxide fuel cells (SOFCs). Powders of composition Ca{sub 3−x}Cu{sub x}Co{sub 4}O{sub 9−δ} (0 ≤ x ≤ 0.2) were obtained by a proteic sol-gel method which uses gelatin as polymerizing agent. As-prepared materials were calcined at 900 °C for 1 h and characterized by X-ray diffraction, with Rietveld refinement of the diffraction data, and scanning electron microscopy. Screen-printed porous electrodes fired (at 950 °C for 2 h) on both faces of ceria based electrolytes were electrochemically characterized by impedance spectroscopy between 600 and 800 °C in air atmosphere. The results indicated the attainment of Ca{sub 3−x}Cu{sub x}Co{sub 4}O{sub 9−δ} solid solutions with monoclinic misfit layered structure and around 2 vol% Co{sub 3}O{sub 4} as a secondary phase. Micro-plates like powders had irregular shape and average diameter near 2 μm. The area specific resistance (ASR) is in line with literature data for cathodes of similar compositions prepared by other synthetic routes. ASR was optimized for the composition Ca{sub 2.99}Cu{sub 0.01}Co{sub 4}O{sub 9−δ}, achieving 0.84 Ω cm{sup 2} at 800 °C in air. - Highlights: • Proteic sol-gel synthesis of Ca{sub 3−x}Cu{sub x}Co{sub 4}O{sub 9−δ} (0 ≤ x ≤ 0.2). • Cu{sup 2+} doping enhances electrode densification. • Area specific resistance (ASR = 0.84 Ω cm{sup 2} at 800 °C) optimized for Ca{sub 2.99}Cu{sub 0.01}Co{sub 4}O{sub 9−δ}.

  16. Thermal Annealing Effect on Optical Properties of Binary TiO2-SiO2 Sol-Gel Coatings

    Directory of Open Access Journals (Sweden)

    Xiaodong Wang

    2012-12-01

    Full Text Available TiO2-SiO2 binary coatings were deposited by a sol-gel dip-coating method using tetrabutyl titanate and tetraethyl orthosilicate as precursors. The structure and chemical composition of the coatings annealed at different temperatures were analyzed by Raman spectroscopy and Fourier Transform Infrared (FTIR spectroscopy. The refractive indices of the coatings were calculated from the measured transmittance and reflectance spectra. An increase in refractive index with the high temperature thermal annealing process was observed. The Raman and FTIR results indicate that the refractive index variation is due to changes in the removal of the organic component, phase separation and the crystal structure of the binary coatings.

  17. Variation in Structural and Optical Properties of Al Doped ZnO Nanoparticles Synthesized by Sol-gel Process

    Directory of Open Access Journals (Sweden)

    Vanaja Aravapalli

    2017-04-01

    Full Text Available This article focuses on analyzing structural and optical properties of Al doped ZnO (AZO synthesized with two different precursors aluminum chloride and aluminum nitrate. The nanoparticles were successfully fabricated and characterized at room temperature by sol-gel process. The objective of improving properties of ZnO nanoparticles by introducing dopants was successful with formation of nanoparticles having different crystalline sizes, optical absorption and luminescence properties. The two different sources influenced properties of ZnO. The particles with less crystalline size obtained from aluminum nitrate. Change in morphology from spherical to bar like morphology proved from SEM spectra. Presence of functional groups predicted from FTIR spectra. PL spectra proved UV emission and visible emission for AZO nanoparticles synthesized using dopant sources aluminum chloride and aluminum nitrate respectively. The obtained properties prove successful utilization of AZO nanoparticles as building materials in fabrication of optoelectronic devices.

  18. Synthesis by Sol-gel and characterization of catalysts Ag/Al2O3-CeO2

    International Nuclear Information System (INIS)

    Zayas, M.L.; Perez H, R.; Rubio, E.; Velasco, A.

    2004-01-01

    Aluminia, cerium and mixed oxides Al 2 O 3 -CeO 2 with different relationship Al/Ce (0.75, 0.50 and 0.25) were prepared by sol-gel and used as support for the Ag. The samples were characterized by XRD, DRIFT, TPR and adsorption of N 2 to temperature of liquid nitrogen. The surface area BET showed that the materials that contain aluminia present near values among them. XRD allowed to identify to the cerianite in the oxides that whose support contains cerium and to the α-aluminia. A mixture of phases was observed in the aluminia. Vibration bands attributed to the bond Al-O and Ce-O were observed by DRIFT in the catalytic materials. TPR showed differences in the reducibility of the Ag precursor in the indicative catalysts of a different interaction with the support. (Author)

  19. Trimetallic oxide nanocomposites of transition metals titanium and vanadium by sol-gel technique: synthesis, characterization and electronic properties

    Science.gov (United States)

    Kumar, Amit; Mishra, Neeraj Kumar; Sachan, Komal; Ali, Md Asif; Soaham Gupta, Sachchidanand; Singh, Rajeev

    2018-04-01

    Novel titanium and vanadium based trimetallic oxide nanocomposites (TMONCs) have been synthesized using metal salts of titanium-vanadium along with three others metals viz. tin, aluminium and zinc as precursors by the sol-gel method. Aqueous ammonia and hydrazine hydrate were used as the reducing agents. The preparations of nanocomposites were monitored by observing the visual changes during each step of synthesis. The synthesized TMONCs were characterized using UV–vis, SEM, EDX, TEM and DLS. Band gap of the synthesized TMONCs ranges from 3–4.5 eV determined using tauc plot. FTIR study revealed the molecular stretching and bending peaks of corresponding M–O/M–O–M bonds thus confirming their formation. Molecular composition and particle size were determined using EDX and DLS respectively. Molecular shape, size and surface morphology have been examined by SEM and TEM.

  20. Fabrication of ceramic oxide-coated SWNT composites by sol-gel process with a polymer glue

    Science.gov (United States)

    Zhang, Cheng; Gao, Lei; Chen, Yongming

    2011-09-01

    The functional copolymer bearing alkoxysilyl and pyrene groups, poly[3-(triethoxysilyl)propyl methacrylate]- co-[(1-pyrene-methyl) methacrylate] (TEPM13- co-PyMMA3), was synthesized via atom transfer radical polymerization. Attributing the π-π interaction of pyrene units with the walls of single-walled carbon nanotubes (SWNTs), this polymer could disperse and exfoliate SWNTs in different solvents through physical interaction as demonstrated by TEM, UV/Vis absorption, and FT-IR analysis. The alkoxysilyl groups functionalized SWNTs were reacted with different inorganic precursors via sol-gel reaction, and, as a results, silica, titania, and alumina were coated onto the surface of SWNTs, respectively via copolymers as a molecular glue. The nanocomposites of ceramic oxides/SWNTs were characterized by SEM analysis. Dependent upon the feed, the thickness of inorganic coating can be tuned easily. This study supplies a facile and general way to coat SWNTs with ceramic oxides without deteriorating the properties of pristine SWNTs.

  1. Mechanical compatibility of sol-gel annealing with titanium for orthopaedic prostheses.

    Science.gov (United States)

    Greer, Andrew I M; Lim, Teoh S; Brydone, Alistair S; Gadegaard, Nikolaj

    2016-01-01

    Sol-gel processing is an attractive method for large-scale surface coating due to its facile and inexpensive preparation, even with the inclusion of precision nanotopographies. These are desirable traits for metal orthopaedic prostheses where ceramic coatings are known to be osteoinductive and the effects may be amplified through nanotexturing. However there are a few concerns associated with the application of sol-gel technology to orthopaedics. Primarily, the annealing stage required to transform the sol-gel into a ceramic may compromise the physical integrity of the underlying metal. Secondly, loose particles on medical implants can be carcinogenic and cause inflammation so the coating needs to be strongly bonded to the implant. These concerns are addressed in this paper. Titanium, the dominant material for orthopaedics at present, is examined before and after sol-gel processing for changes in hardness and flexural modulus. Wear resistance, bending and pull tests are also performed to evaluate the ceramic coating. The findings suggest that sol-gel coatings will be compatible with titanium implants for an optimum temperature of 500 °C.

  2. Radiation hardening of sol gel-derived silica fiber preforms through fictive temperature reduction.

    Science.gov (United States)

    Hari Babu, B; Lancry, Matthieu; Ollier, Nadege; El Hamzaoui, Hicham; Bouazaoui, Mohamed; Poumellec, Bertrand

    2016-09-20

    The impact of fictive temperature (Tf) on the evolution of point defects and optical attenuation in non-doped and Er3+-doped sol-gel silica glasses was studied and compared to Suprasil F300 and Infrasil 301 glasses before and after γ-irradiation. To this aim, sol-gel optical fiber preforms have been fabricated by the densification of erbium salt-soaked nanoporous silica xerogels through the polymeric sol-gel technique. These γ-irradiated fiber preforms have been characterized by FTIR, UV-vis-NIR absorption spectroscopy, electron paramagnetic resonance, and photoluminescence measurements. We showed that a decrease in the glass fictive temperature leads to a decrease in the glass disorder and strained bonds. This mainly results in a lower defect generation rate and thus less radiation-induced attenuation in the UV-vis range. Furthermore, it was found that γ-radiation "hardness" is higher in Er3+-doped sol-gel silica compared to un-doped sol-gel silica and standard synthetic silica glasses. The present work demonstrates an effective strategy to improve the radiation resistance of optical fiber preforms and glasses through glass fictive temperature reduction.

  3. Molecularly Imprinted Sol-Gel-Based QCM Sensor Arrays for the Detection and Recognition of Volatile Aldehydes

    Directory of Open Access Journals (Sweden)

    Chuanjun Liu

    2017-02-01

    Full Text Available The detection and recognition of metabolically derived aldehydes, which have been identified as important products of oxidative stress and biomarkers of cancers; are considered as an effective approach for early cancer detection as well as health status monitoring. Quartz crystal microbalance (QCM sensor arrays based on molecularly imprinted sol-gel (MISG materials were developed in this work for highly sensitive detection and highly selective recognition of typical aldehyde vapors including hexanal (HAL; nonanal (NAL and bezaldehyde (BAL. The MISGs were prepared by a sol-gel procedure using two matrix precursors: tetraethyl orthosilicate (TEOS and tetrabutoxytitanium (TBOT. Aminopropyltriethoxysilane (APT; diethylaminopropyltrimethoxysilane (EAP and trimethoxy-phenylsilane (TMP were added as functional monomers to adjust the imprinting effect of the matrix. Hexanoic acid (HA; nonanoic acid (NA and benzoic acid (BA were used as psuedotemplates in view of their analogous structure to the target molecules as well as the strong hydrogen-bonding interaction with the matrix. Totally 13 types of MISGs with different components were prepared and coated on QCM electrodes by spin coating. Their sensing characters towards the three aldehyde vapors with different concentrations were investigated qualitatively. The results demonstrated that the response of individual sensors to each target strongly depended on the matrix precursors; functional monomers and template molecules. An optimization of the 13 MISG materials was carried out based on statistical analysis such as principle component analysis (PCA; multivariate analysis of covariance (MANCOVA and hierarchical cluster analysis (HCA. The optimized sensor array consisting of five channels showed a high discrimination ability on the aldehyde vapors; which was confirmed by quantitative comparison with a randomly selected array. It was suggested that both the molecularly imprinting (MIP effect and the matrix

  4. Sol-Gel TiO2 thin films sensitized with the mulberry pigment cyanidin

    Directory of Open Access Journals (Sweden)

    Emerson Henrique de Faria

    2007-12-01

    Full Text Available TiO2 films have various applications, among them solar cells and photodegradation of pollutants. In this study, we investigated TiO2 films functionalized with the organic dye cyanidin extracted from black mulberry (Morus nigra. The TiO2 was functionalized by the sol-gel method and the film was deposited on glass substrates by dip-coating. Our aim was to investigate the interaction between the semiconductor and the dye, as well as the influence of the velocity and number of deposits on the characteristics of the film. Using ultraviolet-visible spectroscopy, we observed a shift from the maximum absorption band at 545 nm for the dye’s ethanol solution to 595 nm for the film, indicating interaction of the cyanidin with the TiO2. The absorption spectra in the infrared region of the functionalized TiO2 particles showed bands characteristic of the oxide and indicated their interaction with the dye. Using profilometry and m-line techniques, we found that the films presented thicknesses in the order of 100 nm. A SEM analysis confirmed the high density of the films.

  5. Porous MnO2 prepared by sol-gel method for electrochemical supercapacitor

    Science.gov (United States)

    Bazzi, K.; Kumar, A.; Jayakumar, O. D.; Nazri, G. A.; Naik, V. M.; Naik, R.

    2015-03-01

    MnO2 has attracted great attention as material for electrochemical pseudocapacitor due to its high theoretical specific faradic capacitance (~ 1370 F .g-1) , environmental friendliness and wide potential window in both aqueous and nonaqueous electrolytes. However, the MnO2 has a low surface area which depresses its electrochemical performance. The amorphous α-MnO2 composite was synthesized by sol gel method in the presence of the tri-block copolymer P123. Our aim is to investigate the role of P123 on the electrochemical performance of MnO2. The samples with and without P123 were prepared and characterized by x-ray diffraction (XRD), SEM, TEM and Brunauer-Emmett-Teller (BET) method. The electrochemical performances of the amorphous MnO2 composites as the electrode materials for supercapacitors were evaluated by cyclic voltammetry and AC impedance measurements in a 1M Na2SO4 solution. The results show that the sample prepared without P123 exhibited a relatively low specific capacitance of 28F .g-1, whereas the porous MnO2 prepared with P123 exhibited 117 F .g-1at 5 mV/s. The results of crystalline MnO2 composites will also be presented. The authors acknowledge the support from the Richard J. Barber Foundation for Interdisciplinary Research.

  6. Composites characterization by sol-gel process using positron lifetime spectroscopy

    International Nuclear Information System (INIS)

    Sousa, Edesia M.B. de; Minas Gerais Univ., Belo Horizonte, MG; Magalhaes, Wellington F. de; Mohallem, Nelci D.S.

    1997-01-01

    Si O 2 matrix were prepared by sol-gel method using TEOS, ethanol and H 2 O in a 1/3/10 mole ratio, with H Cl and HF as catalysts. These silica gels were doped with copper and titanium adding Cu Cl and titanium tetra-iso-propoxide in the starting solution during agitation. The samples were prepared in monolithic shape, dried at 110 0 C for 24 hours and thermally treated for 2 hours at 500, 900 and 110 0 C for 24 hours The structural evolution was studied by X-Ray diffraction, mercury porosimetry and picnometry. In this work it was also used the Positron Annihilation Lifetime Spectroscopy which have been used , now a days, as a microscopic probe in order to investigate the free volume in zeolites, polymers and metallic alloy. All the samples have shown a stable pore structure until 900 0 C and a strong densification process at 1100 0 C. (author). 10 refs., 4 figs., 2 tabs

  7. Effects of PEG4000 template on sol-gel synthesis of porous cerium titanate photocatalyst

    Science.gov (United States)

    Zhang, Wenjie; Tao, Yingjie; Li, Chuanguo

    2018-04-01

    Porous cerium titanate was synthesized by sol-gel method, using polyethylene glycol (PEG4000) as template agent. Brannerite structured CeTi2O6 in monoclinic system is the major substance formed in the materials. Formation of CeO2 and rutile TiO2 depends on the amount of PEG4000. The addition of PEG4000 leads to production of fine particles in the samples, but it does not apparently affect the band gap energy. Pore volume of the cerium titanate sample continuously increases with rising PEG4000 amount. The sample obtained using 3.5 g PEG4000 has BET surface area of 16.2 m2/g and pore volume of 0.0232 cm3/g. The addition of PEG4000 can obviously promote photocatalytic activity of cerium titanate, which can be proven by both enhanced production of hydroxyl radical and ofloxacin degradation efficiency. As much as 95.2% of the initial ofloxacin molecules are removed from the solution after 50 min of photocatalytic degradation on the cerium titanate obtained using 3.5 g PEG4000, while only 48.4% ofloxacin is removed on cerium titanate obtained without PEG4000.

  8. Zirconia sol-gel coatings deposited on 304 stainless steel for chemical protection in acid media

    International Nuclear Information System (INIS)

    Luna, F. Perdomo; Atik, M.; Avaca, Luis A.; Aegerter, M.A.

    1995-01-01

    Zr O 2 thin films were prepared by sol-gel method and using dip-coating technique for deposition on 304 austenitic stainless steel, from sonocatalyzed sols of zirconia alkoxide, isopropanol (Zr(O C 3 H 7 )4/C 3 H 7 OH = 0.5), glacial acetic acid and water (C H 3 CO OH/H 2 O = 0.5). The films were dried at 40 deg C/15 min and thermally treated in the air with a linear variation of 5 deg C/min and two isothermal holdings at 400 deg C during 1 h and afterwards at 800 deg C during several periods of time (up to 20 h). The film thickness ranges between 0.6 and 0.8 μm. Structure and morphology were studied by x-ray diffraction and scanning electron microscopy. The corrosion potential, the corrosion current density, the polarization resistance and the corrosion rate (mpy) in 1,0 N aqueous solution of H 2 SO 4 at room temperature were determined using potentiometric polarization curves with a scanning velocity of 1 mV/s. These films act as a blocking physical layer in the corrosion media and increase the substrate life time in a factor of 7

  9. Ultra-small dye-doped silica nanoparticles via modified sol-gel technique

    Science.gov (United States)

    Riccò, R.; Nizzero, S.; Penna, E.; Meneghello, A.; Cretaio, E.; Enrichi, F.

    2018-05-01

    In modern biosensing and imaging, fluorescence-based methods constitute the most diffused approach to achieve optimal detection of analytes, both in solution and on the single-particle level. Despite the huge progresses made in recent decades in the development of plasmonic biosensors and label-free sensing techniques, fluorescent molecules remain the most commonly used contrast agents to date for commercial imaging and detection methods. However, they exhibit low stability, can be difficult to functionalise, and often result in a low signal-to-noise ratio. Thus, embedding fluorescent probes into robust and bio-compatible materials, such as silica nanoparticles, can substantially enhance the detection limit and dramatically increase the sensitivity. In this work, ultra-small fluorescent silica nanoparticles (NPs) for optical biosensing applications were doped with a fluorescent dye, using simple water-based sol-gel approaches based on the classical Stöber procedure. By systematically modulating reaction parameters, controllable size tuning of particle diameters as low as 10 nm was achieved. Particles morphology and optical response were evaluated showing a possible single-molecule behaviour, without employing microemulsion methods to achieve similar results. [Figure not available: see fulltext.

  10. Zirconia sol-gel coatings deposited on 304 stainless steel for chemical protection in acid media

    Energy Technology Data Exchange (ETDEWEB)

    Luna, F Perdomo; Atik, M; Avaca, Luis A; Aegerter, M A [Sao Paulo Univ., Sao Carlos, SP (Brazil). Inst. de Fisica

    1996-12-31

    Zr O{sub 2} thin films were prepared by sol-gel method and using dip-coating technique for deposition on 304 austenitic stainless steel, from sonocatalyzed sols of zirconia alkoxide, isopropanol (Zr(O C{sub 3} H{sub 7})4/C{sub 3} H{sub 7} OH = 0.5), glacial acetic acid and water (C H{sub 3} CO OH/H{sub 2} O = 0.5). The films were dried at 40 deg C/15 min and thermally treated in the air with a linear variation of 5 deg C/min and two isothermal holdings at 400 deg C during 1 h and afterwards at 800 deg C during several periods of time (up to 20 h). The film thickness ranges between 0.6 and 0.8 {mu}m. Structure and morphology were studied by x-ray diffraction and scanning electron microscopy. The corrosion potential, the corrosion current density, the polarization resistance and the corrosion rate (mpy) in 1,0 N aqueous solution of H{sub 2} SO{sub 4} at room temperature were determined using potentiometric polarization curves with a scanning velocity of 1 mV/s. These films act as a blocking physical layer in the corrosion media and increase the substrate life time in a factor of 7 16 refs., 3 figs., 1 tab.

  11. Urea functionalized surface-bonded sol-gel coating for on-line hyphenation of capillary microextraction with high-performance liquid chromatography.

    Science.gov (United States)

    Jillani, Shehzada Muhammad Sajid; Alhooshani, Khalid

    2018-03-30

    Sol-gel urea functionalized-[bis(hydroxyethyl)amine] terminated polydimethylsiloxane coating was developed for capillary microextraction-high performance liquid chromatographic analysis from aqueous samples. A fused silica capillary is coated from the inside with surface bonded coating material and is created through in-situ sol-gel reaction. The urea-functionalized coating was immobilized to the inner surface of the capillary by the condensation reaction of silanol groups of capillary and sol-solution. The characterization of the coating material was successfully done by using X-ray photoelectron spectroscopy, thermogravimetric analysis, field emission scanning electron microscope, and energy dispersive X-ray spectrometer. To make a setup of online capillary microextraction-high performance liquid chromatography, the urea functionalized capillary was installed in the HPLC manual injection port. The analytes of interest were pre-concentrated in the coated sampling loop, desorbed by the mobile phase, chromatographically separated on C-18 column, and analyzed by UV detector. Sol-gel coated capillaries were used for online extraction and high-performance liquid chromatographic analysis of phenols, ketones, aldehydes, and polyaromatic hydrocarbons. This newly developed coating showed excellent extraction for a variety of analytes ranging from highly polar to non-polar in nature. The analysis using sol-gel coating showed excellent overall sensitivity in terms of lower detection limits (S/N = 3) for the analytes (0.10 ng mL -1 -14.29 ng mL -1 ) with acceptable reproducibility that is less than 12.0%RSD (n = 3). Moreover, the capillary to capillary reproducibility of the analysis was also tested by changing the capillary of the same size. This provided excellent%RSD of less than 10.0% (n = 3). Copyright © 2018 Elsevier B.V. All rights reserved.

  12. Correlation of the oxidation state of cerium in sol-gel glasses as a function of thermal treatment via optical spectroscopy and XANES studies.

    Science.gov (United States)

    Assefa, Zerihun; Haire, R G; Caulder, D L; Shuh, D K

    2004-07-01

    Sol-gel glass matrices containing lanthanides have numerous technological applications and their formation involves several chemical facets. In the case of cerium, its ability to exist in two different oxidation states or in mixed valence state provides additional complexities for the sol-gel process. The oxidation state of cerium present during different facets of preparation of sol-gel glasses, and also as a function of the starting oxidation state of cerium added, were studied both by optical spectroscopy and X-ray absorption near-edge structures (XANES). The findings acquired by each approach were compared. The primary focus was on the redox chemistries associated with sample preparation, gelation, and thermal treatment. When Ce3+ is introduced into the starting sols, the trivalent state normally prevails in the wet and room temperature-dried gels. Heating in air at >100 degrees C can generate a light yellow coloration with partial oxidation to the tetravalent state. Above 200 degrees C and up to approximately 1000 degrees C, cerium is oxidized to its tetravalent state. In contrast, when tetravalent cerium is introduced into the sol, both the wet and room temperature-dried gels lose the yellow-brown color of the initial ceric ammonium nitrate solution. When the sol-gel is heated to 110 degrees C it turns yellowish as the cerium tends to be re-oxidized. The yellow color is believed to represent the effect of oxidation and oligomerization of the cerium-silanol units in the matrix. The luminescence properties are also affected by these changes, the details of which are reported herein.

  13. Preparation and characterization of bismuth ruthenate pyrochlore via solid state reaction and sol-gel methods

    Directory of Open Access Journals (Sweden)

    Mayuree Sansernnivet

    2010-01-01

    Full Text Available Bismuth ruthenate pyrochlores, potential cathode materials for intermediate temperature solid oxide fuel cells(ITSOFCs, were prepared via solid-state and sol-gel method. Effects of the preparation routes and conditions on the phase and microstructures of the materials were investigated in this study using XRD and SEM. The study showed that the preparation method and the adding sequence of the starting meterials have a significant effect on the crystal phase and the particle size obtained. Sol-gel synthesis could yield a material with only pyrochlore structure, i.e. Bi2Ru2O7, while the solid state method yielded powder with a small amount of the secondary RuO2 phase. The sol-gel synthesis resulted in materialswith a finer particle size (~0.3-1.0 μm compared to powder synthesized via the solid state reaction method.

  14. Thermal stability of octadecylsilane hybrid silicas prepared by grafting and sol-gel methods

    International Nuclear Information System (INIS)

    Brambilla, Rodrigo; Santos, Joao H.Z. dos; Miranda, Marcia S.L.; Frost, Ray L.

    2008-01-01

    Hybrid silicas bearing octadecylsilane groups were prepared by grafting and sol-gel (SG) methods. The effect of the preparative route on the thermal stability was evaluated by means of thermal gravimetric analysis (TGA), infrared emission spectroscopy (IRES) and, complementary, by 13 C solid-state nuclear magnetic resonance ( 13 C NMR) and matrix assisted laser deionization time of flight mass spectroscopy (MALDI-TOF-MS). Silicas prepared by the grafting route seem to be slightly more stable than those produced by the sol-gel method. This behavior seems to be associated to the preparative route, since grafting affords a liquid-like conformation, while in the case of sol-gel a highly organized crystalline chain conformation was observed

  15. Sol-gel transition accelerated by the co-assembly of two components in supramolecular hydrogels.

    Science.gov (United States)

    Matsumoto, Keigo; Shundo, Atsuomi; Ohno, Masashi; Saruhashi, Kowichiro; Miyachi, Nobuhide; Tsuruzoe, Nobutomo; Tanaka, Keiji

    2015-10-28

    N-Palmitoyl-Gly-His (PalGH) and glycerol 1-monopalmitate (GMP) in water co-assembled into fibrils with twisted ribbon structures and formed a homogeneous network, resulting in gel formation. Shaking the gel easily broke the fibril network leading to a sol in which high and low fibril density regions exist. After a period at room temperature, the higher density regions became interconnected. The spontaneous sol-gel transition did not take place for a gel made from only PalGH. Also, during the transition, the aggregation state of the co-assembly remained unchanged at a molecular level, unlike the fibril network. Thus, it can be claimed that the sol-gel transition is not associated with the assembled molecular configuration, but with the change in the fibril network. This knowledge might be useful for understanding and controlling sol-gel transition, thereby leading to the design and functionalization of hydrogels.

  16. Relationship between sol-gel conditions and enzyme stability: a case study with β-galactosidase/silica biocatalyst for whey hydrolysis.

    Science.gov (United States)

    Escobar, Sindy; Bernal, Claudia; Mesa, Monica

    2015-01-01

    The sol-gel process has been very useful for preparing active and stable biocatalysts, with the possibility of being reused. Especially those based on silica are well known. However, the study of the enzyme behavior during this process is not well understood until now and more, if the surfactant is involved in the synthesis mixture. This work is devoted to the encapsulation of β-galactosidase from Bacillus circulans in silica by sol-gel process, assisted by non-ionic Triton X-100 surfactant. The correlation between enzyme activity results for the β-galactosidase in three different environments (soluble in buffered aqueous reference solution, in the silica sol, and entrapment on the silica matrix) explains the enzyme behavior under stress conditions offered by the silica sol composition and gelation conditions. A stable β-galactosidase/silica biocatalyst is obtained using sodium silicate, which is a cheap source of silica, in the presence of non-ionic Triton X-100, which avoids the enzyme deactivation, even at 40 °C. The obtained biocatalyst is used in the whey hydrolysis for obtaining high value products from this waste. The preservation of the enzyme stability, which is one of the most important challenges on the enzyme immobilization through the silica sol-gel, is achieved in this study.

  17. Fabrication of carbon microcapsules containing silicon nanoparticles-carbon nanotubes nanocomposite by sol-gel method for anode in lithium ion battery

    Science.gov (United States)

    Bae, Joonwon

    2011-07-01

    Carbon microcapsules containing silicon nanoparticles (Si NPs)-carbon nanotubes (CNTs) nanocomposite (Si-CNT@C) have been fabricated by a surfactant mediated sol-gel method followed by a carbonization process. Silicon nanoparticles-carbon nanotubes (Si-CNT) nanohybrids were produced by a wet-type beadsmill method. To obtain Si-CNT nanocomposites with spherical morphologies, a silica precursor (tetraethylorthosilicate, TEOS) and polymer (PMMA) mixture was employed as a structure-directing medium. Thus the Si-CNT/Silica-Polymer microspheres were prepared by an acid catalyzed sol-gel method. Then a carbon precursor such as polypyrrole (PPy) was incorporated onto the surfaces of pre-existing Si-CNT/silica-polymer to generate Si-CNT/Silica-Polymer@PPy microspheres. Subsequent thermal treatment of the precursor followed by wet etching of silica produced Si-CNT@C microcapsules. The intermediate silica/polymer must disappear during the carbonization and etching process resulting in the formation of an internal free space. The carbon precursor polymer should transform to carbon shell to encapsulate remaining Si-CNT nanocomposites. Therefore, hollow carbon microcapsules containing Si-CNT nanocomposites could be obtained (Si-CNT@C). The successful fabrication was confirmed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). These final materials were employed for anode performance improvement in lithium ion battery. The cyclic performances of these Si-CNT@C microcapsules were measured with a lithium battery half cell tests.

  18. Simple Preparation of ZnO Nano-layer by Sol-Gel Method as Active Electrode in P3HT/ZnO Heterojunction Solar Cell

    Science.gov (United States)

    Aprilia, Annisa; Herman, Hidayat, Rahmat

    2010-10-01

    Highly transparent undoped ZnO thin films have been prepared on glass and indium tin oxide substrates with simple process by sol-gel route and dip-coating deposition. Gel precursor of ZnO was prepared from zinc acetat dehydrate solution in methanol with the addition of trietylamine as stabilizing agent. Thin layer of gel precursor was prepared by dip coating and then followed by calcination at 400° C for 5 minute in air atmosphere. The thickness of the resulted ZnO thin film produced by ten times coating is about 150 nm. The films shows high transmittance larger than 98% in the visible region (400-800 nm). Absorption is observed in the UV region with absorption onset at about 390 nm indicating varying band gap between 3.18 eV until 3.23 eV depending on the number of coating layer. The AFM image shows that the films seems to be constructed from random stacking of nano-sized ZnO particle in the order of 50 nm. Among the prepared samples, the lowest resistivity is about 1.8×107 Ωm observed in the five-layer coating film. In order to fabricate solar cell structure, P3HT was deposited onto the ZnO thin film layer by spin casting technique and then followed by metal (Au) layer deposition by thermal evaporation. The formed solar cell has the inverted type solar cell with ITO/ZnO/P3HT/Au configuration. By the insertion ZnO layer, the photocurrent was improved by more than ten orders of magnitude in comparison to that of without ZnO layer. The measured photocurrent decreases at large number of coating layer which is supposed to be related with the current limitation by the effective carrier path length in ZnO layer.

  19. Preparation of high-purity ZrSiO4 powder using sol-gel processing and mechanical properties of the sintered body

    International Nuclear Information System (INIS)

    Mori, T.; Yamamura, H.; Kobayashi, H.; Mitamura, T.

    1992-01-01

    This paper reports that effects of the concentration of ZrOCl 2 , calcination temperature, heating rate, and the size of secondary particles after hydrolysis on the preparation of high-purity ZrSiO 4 fine powders from ZrOCl 2 :8H 2 O (0.2M to 1.7M) and equimolar colloidal SiO 2 using Sol--gel processing have been studied. Mechanical properties of the sintered ZrSiO 4 from the high-purity ZrSiO 4 powders have been also investigated. Single-phase ZrSiO 4 fine powders were synthesized at 1300 degrees C by forming ZrSiO 4 precursors having a Zr---O---Si bond, which was found in all the hydrolysis solutions, and by controlling a secondary particle size after hydrolysis. The conversion rate of ZrSiO 4 precursor gels to ZrSiO 4 powders from concentrations other than 0.4M ZrOCl 2 ·8H 2 O increased when the heating rate was high, whereupon the crystallization of unreacted ZrO 2 and SiO 2 was depressed and the propagation and increase of ZrSiO 4 nuclei in the gels were accelerated. The density of the ZrSiO 4 sintered bodies, manufactured by firing the ZrSiO 4 compacts at 1600 degrees to 1700 degrees C, was more than 95% of the theoretical density, and the grain size ranged around 2 to 4 μm. The mechanical strength was 320 MPa (room temperature to 1400 degrees C), and the thermal shock resistance was superior to that of mullite and alumina, with fairly high stability at higher temperatures

  20. Laser sintering of doped strontium aluminate via modified sol-gel for use as a ceramic pigment; Sinterizacao a laser do aluminato de estroncio dopado via sol-gel modificado para aplicacao como pigmento ceramico

    Energy Technology Data Exchange (ETDEWEB)

    Soares, F.M. dos S.; Valerio, M.E.G. [Universidade Federal de Sergipe (UFS), Sao Cristovao, SE (Brazil)

    2017-01-15

    Powder of Dy{sup 3+} co-doped SrAl{sub 2}O{sub 4} :Eu{sup 3+} was produced via proteic sol-gel method, a modified sol-gel route which allows the formation of oxides at lower temperatures than other methods. CO{sub 2} laser sintering was used as a method for heat treatment, effective in reducing trivalent europium ions in doped samples. Thermal analysis of the precursors, performed by TG and DTA, revealed that the crystallization of SrAl{sub 2}O{sub 4} phase occurred at approximately 1060 °C. X-ray diffraction showed that the samples, before and after sintering, had monoclinic and hexagonal phases formation. DLS technique revealed the presence of nanosized and micrometric particles, and particle agglomerates, confirmed by SEM images. Micrographs of the fracture surface of a sintered pellet revealed a high degree of densification caused by heat treatment. Photoluminescence measurements showed that the samples after synthesis and before heat treatment with laser had reddish emission, composed of characteristic narrow emission lines from Eu{sup 3+} and more intense emission when the samples were excited at 265 nm. The laser treatment promoted the reduction of Eu{sup 3+} to Eu{sup 2+} and this effect was confirmed by the presence of a wide emission band in the green region of the spectrum with a maximum emission obtained after excitation at 350 nm. The luminescent decay time of the thermally treated sample was approximately 100 min. Via XRF measurements of acquired frit and DTA and TG of the frit, pigment and mixtures of both, it was noticed good compatibility in terms of thermal processes, that indicated that the pigment has a potential to be used in ceramic tiles. (author)

  1. Sol-Gel Production; Proceedings of the First International Conference on Application and Commercialization of Sol-Gel Processing Held in Saarbruecken, Germany on 24-25 May 1993

    National Research Council Canada - National Science Library

    Schmidt, Helmut

    1998-01-01

    ...; Sol-Gel Coatings on Large Glass Substrates for Multilayer Interference Systems; A SiO2-ZrO2 Gel Film doped with Organic Pigments Made by the Sol-Gel Method for Contrast Enhancement of Color Picture Tubes...

  2. Fundamental electrochemiluminescence characteristics of fluorine-doped tin oxides synthesized by sol-gel combustion.

    Science.gov (United States)

    Moon, B H; Chaoumead, A; Sung, Y M

    2013-10-01

    Fluorine-doped tin oxide (FTO) materials synthesized by sol-gel combustion method were investigated for electrochemical luminescence (ECL) application. Effects of sol-gel combustion conditions on the structures and morphology of the porous FTO (p-FTO) materials were studied. ECL efficiency of p-FTO-based cell was about 251 cd/m2 at 4 V bias, which is higher than the sell using only FTO electrodes (102.8 cd/m2). The highest intensity of the emitting light was obtained at the wavelength of about 610 nm. The porous FTO layer was effective for increasing ECL intensities.

  3. Application of sol-gel process on the elaboration of SnO2 based ceramics

    International Nuclear Information System (INIS)

    Prescatan, R.T.; Silva, D.V. da; Hiratsuka, R.S.; Santilli, C.V.; Pulcinelli, S.H.

    1990-01-01

    The electrical, optical and chemical peculiar properties of SnO 2 confers it-self some potential application. The densification difficulty during sintering of SnO 2 compromises its elaboration by ceramic conventional process. In this work the preparation of SnO 2 ceramics by sol-gel process was investigated. Some parameters envolved on the colloidal stability, sol-gel transition and drying process were analysed. The obtained materials were characterized by rheological, X-ray diffraction, infra-red spectroscopy and pores size distribution measurements. The results show that a considerable densification during sintering at 400 and 600 0 C was obtained. (author) [pt

  4. Micro- and nanostructured sol-gel-based materials for optical chemical sensing (2005–2015)

    International Nuclear Information System (INIS)

    Barczak, Mariusz; McDonagh, Colette; Wencel, Dorota

    2016-01-01

    This review (with 172 references) highlights the progress made in the past 10 years in silica sol-gel-based materials for use in optical chemical sensing. Following an introduction, the processes leading to the sol-gel-based and ormosil materials, their printability and methods for characterisation are discussed. Then various classes of optical sensors, with a focus on sensors for pH values, oxygen, carbon dioxide, ammonia (also in dissolved form), and heavy metal ions are described. A further section covers nanoparticle-based optical sensors mainly for use in intracellular sensing of the above species. Recent developments in this area are also emphasised and future trends discussed. (author)

  5. Deposition of sol-gel sensor spots by nanoimprint lithography and hemi-wicking

    DEFF Research Database (Denmark)

    Mikkelsen, Morten Bo Lindholm; Marie, Rodolphe; Hansen, Jan H.

    2011-01-01

    We present a method for homogeneous deposition of sol-gel sensor materials, which enable fabrication of sensor spots for optical pH and oxygen measurements inside plastic containers. A periodic pattern of posts is imprinted into a polycarbonate substrate and, using the principle of hemi-wicking, ......We present a method for homogeneous deposition of sol-gel sensor materials, which enable fabrication of sensor spots for optical pH and oxygen measurements inside plastic containers. A periodic pattern of posts is imprinted into a polycarbonate substrate and, using the principle of hemi...

  6. Porous Silica Sol-Gel Glasses Containing Reactive V2O5 Groups

    Science.gov (United States)

    Stiegman, Albert E.

    1995-01-01

    Porous silica sol-gel glasses into which reactive vanadium oxide functional groups incorporated exhibit number of unique characteristics. Because they bind molecules of some species both reversibly and selectively, useful as chemical sensors or indicators or as scrubbers to remove toxic or hazardous contaminants. Materials also oxidize methane gas photochemically: suggests they're useful as catalysts for conversion of methane to alcohol and for oxidation of hydrocarbons in general. By incorporating various amounts of other metals into silica sol-gel glasses, possible to synthesize new materials with broad range of new characteristics.

  7. Site selective generation of sol-gel deposits in layered bimetallic macroporous electrode architectures.

    Science.gov (United States)

    Lalo, Hélène; Bon-Saint-Côme, Yémima; Plano, Bernard; Etienne, Mathieu; Walcarius, Alain; Kuhn, Alexander

    2012-02-07

    The elaboration of an original composite bimetallic macroporous electrode containing a site-selective sol-gel deposit is reported. Regular colloidal crystals, obtained by a modified Langmuir-Blodgett approach, are used as templates for the electrogeneration of the desired metals in the form of a well-defined layered bimetallic porous electrode. This porous matrix shows a spatially modulated electroactivity which is subsequently used as a strategy for targeted electrogeneration of a sol-gel deposit, exclusively in one predefined part of the porous electrode.

  8. Fabrication of superhydrophobic sol-gel composite films using hydrophobically modified colloidal zinc hydroxide.

    Science.gov (United States)

    Lakshmi, R V; Basu, Bharathibai J

    2009-11-15

    A superhydrophobic sol-gel composite film was fabricated by incorporating hydrophobically modified colloidal zinc hydroxide (CZH) in sol-gel matrix. CZH was prepared by controlled precipitation and modified by treatment with stearic acid. The concentration of stearic acid and stirring time were optimized to obtain modified CZH with very high water contact angle (WCA) of 165 degrees and sliding angle (SA)superhydrophobic surfaces. FTIR spectrum also confirmed the presence of zinc stearate in the composite film. The method is simple and cost-effective and does not involve any expensive chemicals or equipments.

  9. Influence of crosslinker structure on performance of functionalised organic-inorganic hybrid sol-gel coating

    Science.gov (United States)

    Vasiljević, J.; Zorko, M.; Štular, D.; Tomšič, B.; Jerman, I.; Orel, B.; Medved, J.; Simončič, B.

    2017-10-01

    This research aimed to investigate the influence of the co-condensation of the three different organofunctional trialkoxysilane precursors with two different crosslinkers, i.e. tetraethoxysilane or organocyclotetrasiloxane on the performance and the washing fastness of this multicomponent multifunctional sol-gel coating on cellulose fibres. To this aim, a three-component equimolar sol mixture (MC), which included 1H,1H,2H,2H-perfluorooctyltriethoxysilane (SiF), 3-(trimethoxysilyl)-propyldimethyloctadecyl ammonium chloride (SiQ) and P,P-diphenyl-N-(3-(trimethoxysilyl)propyl) phosphinic amide (SiP) in combination with two different concentrations of TEOS (T and 3T) or organocyclotetrasiloxane 2,4,6,8-tetrakis(2-(diethoxy(methyl)silyl)ethyl)-2,4,6,8-tetramethyl-cyclotetrasiloxane (T4) as crosslinkers, was applied to the cotton fibres by a pad-dry-cure process. The functional properties of the coated samples before and after repeated washing were investigated by the water θ (W) and n-hexadecane θ (C16) static contact angle as well as water sliding (roll-off) (α) angle measurements. The inclusion of both TEOS and T4 into the MC sol increased the hydrophobic affect and simultaneously decreased the oleophobic effect of the MC coating. These phenomena were more pronounced for higher concentration of TEOS and T4 crosslinker. The inclusion of T4 into the MC sol improved the coating washing fastness to a significantly higher extent than the inclusion of TEOS, with respect to the applied concentrations.

  10. Novel cobalt releasing sol-gel derived bioactive glass for bone tissue engineering

    International Nuclear Information System (INIS)

    Oliveira, Ana Celeste Ximenes; Barrioni, Breno Rocha; Leite, Maria de Fatima; Pereira, Marivalda Magalhaes

    2016-01-01

    Full text: Bone defects are caused by traumas, congenital disorders or infections, and bone grafts are the usual treatment. However, limitations of this therapy have lead to the advance of tissue engineering approaches. Bioactive glasses (BG) are an attractive bioactive ceramic for bone repair [1], due to its osteogenic properties and capability of releasing different ions, inducing specific biological responses. Tissue repair depends also on blood vessels formation. Among angiogenic agents, cobalt ion has been regarded as strategic component to incorporate into ion releasing materials. In this study, 5% (molar) cobalt releasing BG was synthesized by sol-gel method. To characterize the material, powder samples were evaluated by FTIR and DRX. To access the cytotoxic effects, MTT and LIVE/DEAD tests were performed on osteoblasts exposed to the ionic product of the material (100 μg/mL) for 72h. FTIR analysis reveals typical absorption bands of present groups in BG. X-ray diffractogram of DRX confirmed the amorphous character of BG, without the occurrence of recrystallization of cobalt precursor, suggesting that cobalt incorporation was well succeeded. MTT test showed that cells exposed to ionic product presented high levels of metabolic activity. LIVE/DEAD assay evidenced that cell membrane integrity and intracellular esterases activity were preserved. Both cytotoxic tests proved that cobalt-BG material generated a cell friendly environment. This work shows that BG with cobalt agent presented proper structural features and a non-cytotoxic behaviour. Reference: [1] Hench LL, J Mater Sci Mater Med 17(11), 967-78 (2006). (author)

  11. Visible emission from Er-doped SnO2 thin films deposited by sol-gel Emissão no visível de filmes finos, depositados via sol-gel, de SnO2 dopados com Er

    Directory of Open Access Journals (Sweden)

    L. P. Ravaro

    2007-06-01

    Full Text Available Emission from Er-doped SnO2 thin film deposited via sol-gel by the dip coating technique is obtained in the range 500-700 nm with peak at 530 nm (green. Electron-hole generation in the tin dioxide matrix is used to promote the rare-earth ion excitation. Evaluation of crystallite dimensions through X-ray diffraction results leads to nanoscopic size, what could play a relevant role in the emission spectra. The electron-hole mechanism is also responsible for the excitation of the transition in the 1540 nm range in powders obtained from the same precursor solution of films. The thin film matrix presents a very useful shape for technological application, since it allows integration in optical devices and the application of electric fields to operate electroluminescent devices.Foi obtida emissão de filmes finos de SnO2 dopados com Er no intervalo 500-700 nm, com pico em 530 nm (verde. Esses filmes foram depositados pela técnica de molhamento via sol-gel. A geração de pares elétron-buraco na matriz de SnO2 é usada para promover a excitação do íon terra-rara. A avaliação do tamanho dos cristalitos por meio de resultados de difração de raios X indica dimensões nanoscópicas, o que pode ser relevante para a interpretação do espectro de emissão. O mecanismo de excitação elétron-buraco é também responsável pela excitação da transição no intervalo que inclui 1540 nm em pós obtidos da mesma solução precursora dos filmes. Filmes finos constituem um formato muito útil para aplicações tecnológicas, desde que permite integração em dispositivos ópticos e a aplicação de campos elétricos para operar dispositivos eletroluminescentes.

  12. Sol-gel preparation of lead magnesium niobate (PMN) powders and thin films

    Science.gov (United States)

    Boyle, T.J.

    1999-01-12

    A method of preparing a lead magnesium niobium oxide (PMN), Pb(Mg{sub 1/3}Nb{sub 2/3})O{sub 3}, precursor solution by a solvent method wherein a liquid solution of a lead-complex PMN precursor is combined with a liquid solution of a niobium-complex PMN precursor, the combined lead- and niobium-complex liquid solutions are reacted with a magnesium-alkyl solution, forming a PMN precursor solution and a lead-based precipitate, and the precipitate is separated from the reacted liquid PMN precursor solution to form a precipitate-free PMN precursor solution. This precursor solution can be processed to form both ferroelectric powders and thin films. 3 figs.

  13. Laser sintering of doped strontium aluminate via modified sol-gel for use as a ceramic pigment

    International Nuclear Information System (INIS)

    Soares, F.M. dos S.; Valerio, M.E.G.

    2017-01-01

    Powder of Dy"3"+ co-doped SrAl_2O_4 :Eu"3"+ was produced via proteic sol-gel method, a modified sol-gel route which allows the formation of oxides at lower temperatures than other methods. CO_2 laser sintering was used as a method for heat treatment, effective in reducing trivalent europium ions in doped samples. Thermal analysis of the precursors, performed by TG and DTA, revealed that the crystallization of SrAl_2O_4 phase occurred at approximately 1060 °C. X-ray diffraction showed that the samples, before and after sintering, had monoclinic and hexagonal phases formation. DLS technique revealed the presence of nanosized and micrometric particles, and particle agglomerates, confirmed by SEM images. Micrographs of the fracture surface of a sintered pellet revealed a high degree of densification caused by heat treatment. Photoluminescence measurements showed that the samples after synthesis and before heat treatment with laser had reddish emission, composed of characteristic narrow emission lines from Eu"3"+ and more intense emission when the samples were excited at 265 nm. The laser treatment promoted the reduction of Eu"3"+ to Eu"2"+ and this effect was confirmed by the presence of a wide emission band in the green region of the spectrum with a maximum emission obtained after excitation at 350 nm. The luminescent decay time of the thermally treated sample was approximately 100 min. Via XRF measurements of acquired frit and DTA and TG of the frit, pigment and mixtures of both, it was noticed good compatibility in terms of thermal processes, that indicated that the pigment has a potential to be used in ceramic tiles. (author)

  14. Sol-gel synthesis and characterization of single-phase Ni ferrite nanoparticles dispersed in SiO2 matrix

    International Nuclear Information System (INIS)

    Nadeem, K.; Traussnig, T.; Letofsky-Papst, I.; Krenn, H.; Brossmann, U.; Wuerschum, R.

    2010-01-01

    Nanoparticles of NiFe 2 O 4 dispersed in SiO 2 (25 wt%) matrix were synthesized by sol-gel method using tetraethyl orthosilicate (TEOS), as a precursor for SiO 2 . The sol-gel method for nanocomposites normally provides multi-phase nanoparticles. We investigated by a synopsis of different analysis methods, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and SQUID-magnetometry, how the various chemical phases are transformed to a single-phase spinel structure during the various stages of annealing from 300 to 900 o C. We have developed a full phase diagram of chemical phases as a function of annealing temperature. The average particle size lies in the range 16-27 nm. The chemical phases formed below 900 o C are NiFe, NiO, γ-Fe 2 O 3 , α-Fe 2 O 3 , and NiFe 2 O 4 , respectively. The role of the TEOS prepared SiO 2 matrix is to restrict the particle size in a small range in order to rule out particle size effects. In the mid-infrared, a shift of the vibrational Fe-O bond is observed from 568 to 586 cm -1 for annealing between 500 and 700 o C which indicates an increasing NiFe 2 O 4 phase formation. A systematic study of coercivity field (ranging from 32 to 200 Oe) and saturation magnetic moment (ranging from 12.2 to 32.1 emu/g) for differently annealed samples supports our findings about the evolution of single-phase NiFe 2 O 4 at 900 o C. The opposite trend of saturation magnetic moment and coercivity with respect to annealing temperature clearly separates the different phases of metallic, antiferromagnetic, and finally single-phase spinel NiFe 2 O 4 .

  15. Improving the scratch resistance of sol-gel metal oxide coatings cured at 250 C through use of thermogenerated amines

    NARCIS (Netherlands)

    Langanke, J.; Arfsten, N.; Buskens, P.; Habets, R.; Klankermayer, J.; Leitner, W.

    2013-01-01

    Scratch resistant sol-gel metal oxide coatings typically require a thermal post-treatment step (curing process) at temperatures between 400 and 700 C. In this report, we demonstrate that the in situ generation of amines within sol-gel films facilitates the preparation of scratch resistant metal

  16. On the healing mechanism of sol-gel derived hybrid materials containing dynamic di-sulfide bonds

    NARCIS (Netherlands)

    AbdolahZadeh, M.; Esteves, A.C.C.; Van der Zwaag, S.; Garcia Espallargas, S.J.

    2013-01-01

    Sol-gel technology is increasingly being used in coatings for corrosion protection and adhesion improvement. So far, the self-healing concept in sol-gel coatings has only been approached from extrinsic healing perspective (i.e. use of nano and micro carriers of corrosion inhibitors) [1]. Despite the

  17. THERMALLY STABLE NANOCRYSTALLINE TIO2 PHOTOCATALYSTS SYNTHESIZED VIA SOL-GEL METHODS MODIFIED WITH IONIC LIQUID AND SURFACTANT MOLECULES

    Science.gov (United States)

    Recently, sol-gel methods employing ionic liquids (ILs) have shown significant implications for the synthesis of well-defined nanostructured inorganic materials. Herein, we synthesized nanocrystalline TiO2 particles via an alkoxide sol-gel method employing a water-immi...

  18. Environmentally benign sol-gel antifouling and foul-releasing coatings.

    Science.gov (United States)

    Detty, Michael R; Ciriminna, Rosaria; Bright, Frank V; Pagliaro, Mario

    2014-02-18

    Biofouling on ships and boats, characterized by aquatic bacteria and small organisms attaching to the hull, is an important global issue, since over 80000 tons of antifouling paint is used annually. This biofilm, which can form in as little as 48 hours depending on water temperature, increases drag on watercraft, which greatly reduces their fuel efficiency. In addition, biofouling can lead to microbially induced corrosion (MIC) due to H2S formed by the bacteria, especially sulfate-reducing bacteria. When the International Maritime Organization (IMO) international convention banned the use of effective but environmentally damaging coatings containing tributyl tin in 2008, the development of clean and effective antifouling systems became more important than ever. New nonbiocidal coatings are now in high demand. Scientists have developed new polymers, materials, and biocides, including new elastomeric coatings that they have obtained by improving the original silicone (polydimethylsiloxane) formulation patented in 1975. However, the high cost of silicones, especially of fluoropolymer-modified silicones, has generally prevented their large-scale diffusion. In 2009, traditional antifouling coatings using cuprous oxide formulated in copolymer paints still represented 95% of the global market volume of anti-fouling paints. The sol-gel nanochemistry approach to functional materials has emerged as an attractive candidate for creating low fouling surfaces due to the unique structure and properties of silica-based coatings and of hybrid inorganic-organic silicas in particular. Sol-gel formulations easily bind to all types of surfaces, such as steel, fiberglass, aluminum, and wood. In addition, they can cure at room temperature and form thin glassy coatings that are markedly different from thick silicone elastomeric foul-releasing coatings. Good to excellent performance against biofouling, low cure temperatures, enhanced and prolonged chemical and physical stability, ease of

  19. Effectiveness of silica based sol-gel microencapsulation method for odorants and flavors leading to sustainable environment.

    Science.gov (United States)

    Ashraf, Muhammad Aqeel; Khan, Aysha Masood; Ahmad, Mushtaq; Sarfraz, Maliha

    2015-01-01

    Microencapsulation has become a hot topic in chemical research. Technology mainly used for control release and protection purposes. The sol-gel micro encapsulation approach for fragrance and aroma in porous silica-based materials leads to sustainable odorant and flavored materials with novel and unique beneficial properties. Sol-gel encapsulation of silica based micro particles considered economically cheap as capital investment in manufacturing is very low and environmentally friendly. Amorphous sol-gel SiO2 is non-toxic and safe, whereas the sol-gel entrapment of delicate chemicals in its inner pores results in pronounced chemical and physical stabilization of the entrapped active agents, thereby broadening the practical utilization of chemically unstable essential oils (EOs). Reviewing progress in the fabrication of diverse odorant and flavored sol-gels, shows us how different synthetic strategies are appropriate for practical application with important health and environmental benefits.

  20. Effectiveness of silica based sol-gel microencapsulation method for odorants and flavors leading to sustainable environment

    Science.gov (United States)

    Ashraf, Muhammad Aqeel; Khan, Aysha Masood; Ahmad, Mushtaq; Sarfraz, Maliha

    2015-01-01

    Microencapsulation has become a hot topic in chemical research. Technology mainly used for control release and protection purposes. The sol-gel micro encapsulation approach for fragrance and aroma in porous silica-based materials leads to sustainable odorant and flavored materials with novel and unique beneficial properties. Sol-gel encapsulation of silica based micro particles considered economically cheap as capital investment in manufacturing is very low and environmentally friendly. Amorphous sol-gel SiO2 is non-toxic and safe, whereas the sol-gel entrapment of delicate chemicals in its inner pores results in pronounced chemical and physical stabilization of the entrapped active agents, thereby broadening the practical utilization of chemically unstable essential oils (EOs). Reviewing progress in the fabrication of diverse odorant and flavored sol-gels, shows us how different synthetic strategies are appropriate for practical application with important health and environmental benefits. PMID:26322304

  1. Organization in sol-gel polymerization of methacrylate co-oligomers containing trimethoxysilylpropyl methacrylate

    Czech Academy of Sciences Publication Activity Database

    Vraštil, J.; Matějka, Libor; Špaček, V.; Večeřa, M.; Prokůpek, L.

    2005-01-01

    Roč. 46, č. 25 (2005), s. 11232-11240 ISSN 0032-3861 Institutional research plan: CEZ:AV0Z40500505 Keywords : organic-inorganic hybrid * sol-gel process * oligomers Subject RIV: CD - Macromolecular Chemistry Impact factor: 2.849, year: 2005

  2. Analysis and theory of gas transport in microporous sol-gel derived ceramic membranes

    NARCIS (Netherlands)

    de Lange, R.S.A.; de Lange, Rob; Keizer, Klaas; Burggraaf, Anthonie; Burggraaf, A.J.

    1995-01-01

    Sol-gel modification of mesoporous alumina membranes is a very successful technique to improve gas separation performance. Due to the formed microporous top layer, the membranes show activated transport and molecular sieve-like separation factors. This paper concentrates on the mechanism of

  3. Study of positron lifetime spectrum for Zn O varistor ceramics fabricated by Sol-gel route

    International Nuclear Information System (INIS)

    Li Xigui; Wei Shutao; Zhang Ruiying; Cheng Guosheng; Dai Xianqi; Zhang Jincang; Xing Huaimin

    2000-01-01

    An investigation of positron lifetime spectrum for ZnO varistor ceramics fabricated by Sol-gel route was carried out. The relationship between lifetime parameters and the densification and nonlinear coefficient α was given. The dependence of electrical properties on sintering temperature and duration was discussed

  4. Amperometric biosensor for hydrogen peroxide based on hemoglobin entrapped in titania sol-gel film

    International Nuclear Information System (INIS)

    Yu Jiuhong; Ju Huangxian

    2003-01-01

    Hemoglobin (Hb) was entrapped in a titania sol-gel matrix and used as a mimetic peroxidase to construct a novel amperometric biosensor for hydrogen peroxide. The Hb entrapped titania sol-gel film was obtained with a vapor deposition method, which simplified the traditional sol-gel process for protein immobilization. The morphologies of both titania sol-gel and the Hb films were characterized using scanning electron microscopy (SEM) and proved to be chemically clean, porous, homogeneous. This matrix provided a biocompatible microenvironment for retaining the native structure and activity of the entrapped Hb and a very low mass transport barrier to the substrates. H 2 O 2 could be reduced by the catalysis of the entrapped hemoglobin at -300 mV without any mediator. The reagentless H 2 O 2 sensor exhibited a fast response (less than 5 s) and sensitivity as high as 1.29 mA mM -1 cm -2 . The linear range for H 2 O 2 determination was from 5.0x10 -7 to 5.4x10 -5 M with a detection limit of 1.2x10 -7 M. The apparent Michaelis-Menten constant of the encapsulated hemoglobin was calculated to be 0.18±0.02 mM. The stability of the biosensor was also evaluated

  5. Sol-gel technology applied to alternative high-level waste forms development

    International Nuclear Information System (INIS)

    Angelini, P.; Stinton, D.P.; Vavruska, J.S.; Caputo, A.J.; Lackey, W.J.

    1981-01-01

    Sol-gel technology appears applicable to waste solidification. It is attractive for remote operation, and a variety of waste compositions and forms can be produced. Spheres and pellets of gel-derived Synroc waste forms were produced. Spheres of the Synroc-B type were coated with pyrolytic carbon and silicon carbide. Partitioning of actinides in Synroc-B was experimentally determined

  6. Silica-Based Sol-Gel Coating on Magnesium Alloy with Green Inhibitors

    Directory of Open Access Journals (Sweden)

    Vinod Upadhyay

    2017-06-01

    Full Text Available In this work, the performances of several natural organic inhibitors were investigated in a sol-gel system (applied on the magnesium alloy Mg AZ31B substrate. The inhibitors were quinaldic acid (QDA, betaine (BET, dopamine hydrochloride (DOP, and diazolidinyl urea (DZU. Thin, uniform, and defect-free sol-gel coatings were prepared with and without organic inhibitors, and applied on the Mg AZ31B substrate. SEM and EDX were performed to analyze the coating surface properties, the adhesion to the substrate, and the thickness. Electrochemical measurements, including electrochemical impedance spectroscopy (EIS and anodic potentiodynamic polarization scan (PDS, were performed on the coated samples to characterize the coatings’ protective properties. Also, hydrogen evolution measurement—an easy method to measure magnesium corrosion—was performed in order to characterize the efficiency of coating protection on the magnesium substrate. Moreover, scanning vibrating electrode technique (SVET measurements were performed to examine the efficiency of the coatings loaded with inhibitors in preventing and containing corrosion events in defect areas. From the testing results it was observed that the formulated sol-gel coatings provided a good barrier to the substrate, affording some protection even without the presence of inhibitors. Finally, when the inhibitors’ performances were compared, the QDA-doped sol-gel was able to contain the corrosion event at the defect.

  7. Tin dioxide sol-gel derived films doped with platinum and antimony deposited on porous silicon

    NARCIS (Netherlands)

    Savaniu, C.; Arnautu, A.; Cobianu, C.; Craciun, G.; Flueraru, C.; Zaharescu, M.; Parlog, C.; Paszti, F.; van den Berg, Albert

    1999-01-01

    SnO2 sol-gel derived thin films doped simultaneously with Pt and Sb are obtained and reported for the first time. The Sn sources were tin(IV) ethoxide or tin(II) ethylhexanoate, while hexachloroplatinic acid (H2PtCl6) and antimony chloride (SbCl3) were used as platinum and antimony sources,

  8. Sol-Gel Synthesis of Phosphate-Based Glasses for Hydrophilic Enamel Applications

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Dae-Sung; Ryu, Bong-ki [Pusan National University, Busan (Korea, Republic of)

    2017-04-15

    In this study, quaternary phosphate-based sol-gel derived glasses were synthesized from a P{sub 2}O{sub 5}-CaO-Na{sub 2}O-TiO{sub 2} system with a high TiO{sub 2} content of up to 50 mol%. The sol-gel method was chosen because incorporating a high percentage of titanium into a phosphate network via traditional melt-quench methods is non-trivial. The structure and thermal properties of the obtained stabilized sol-gel glasses were characterized using X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, and differential scanning calorimetry (DSC). The XRD results confirmed the amorphous nature of all of the stabilized sol–gel derived glasses. The FTIR results revealed that added TiO{sub 2} enters the network as (TiO{sub 6}), which likely acts as a modifier oxide. Consequently, the number of terminal oxygen atoms increases, leading to an increase in the number of P-OH bonds. In addition, DSC results confirmed a decrease in glass transition and crystallization temperatures with increasing TiO{sub 2} content. This is the first report of a sol-gel synthesis strategy combined with enameling to prepare glass at low processing temperatures and the first use of such a system for both hydrophilic and chemical resistance purposes.

  9. Sol-gel/hydrothermal synthesis of mixed metal oxide of Titanium and ...

    African Journals Online (AJOL)

    Mixed metal oxides of titanium and zinc nanocomposites were prepared through sol-gel method under hydrothermal condition using titanium oxy-(1, 2 - pentadione) and zinc acetate without hazardous additives. The resulting composites were characterized by X-Ray Diffractometer (XRD), Scanning Electron Microscope ...

  10. Influence of p H on optical properties of nano structure sol-gel-derived silica films

    International Nuclear Information System (INIS)

    Heshmatpuor, F.; Adelkhani, H.; Nahavandi, M.; Noorbakhsh Shourabadi, M.

    2006-01-01

    Sol-gel derived silica films were fabricated by dip-coating onto glass microscope substrates. Film properties such as transmission and surface morphology were monitored as function of dip speed and sol p H. Film transmission was increased with increasing of p H in visible range. The surface morphology of films were investigated with scanning electron microscopy.

  11. Patterned transparent zinc oxide films produced by sol-gel embossing

    Energy Technology Data Exchange (ETDEWEB)

    Rao, J.; Koh, L.H.K.; Crean, G.M. [Tyndall National Institute, Lee Maltings, Prospect Row, Cork (Ireland); Department of Microelectronic Engineering, University College Cork, Cork (Ireland); O' Brien, S. [Tyndall National Institute, Lee Maltings, Prospect Row, Cork (Ireland); Winfield, R.J.

    2008-08-15

    A low cost zinc oxide embossing technique is reported as a method of fabricating structures relevant to a variety of applications. A zinc based sol-gel material was prepared from zinc acetate[Zn(C{sub 2}H{sub 3}O{sub 2}){sub 2}], monoethanolamine[H{sub 2}NC{sub 2}H{sub 4}OH] and isopropanol. The sol-gel was cast into a polydimethylsiloxane (PDMS) mould a track design, placed in contact with the substrate and dried under vacuum at 70 C for 3 hours. The formed track pattern was further densified to provide a stable conductor film that retained the embossed shape. An optimum Zn sol-gel content of 0.6 M was identified. The embossed films had a transparency of greater than 83% in the visible region. The optical bandgap energy was evaluated to be 3.306 eV. The influence of ZnO sol-gel film synthesis and embossing parameters on the microstructure, morphology and optical transparency of fabricated structures is described. (copyright 2008 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  12. Sol-Gel Synthesis of Phosphate-Based Glasses for Hydrophilic Enamel Applications

    International Nuclear Information System (INIS)

    Kim, Dae-Sung; Ryu, Bong-ki

    2017-01-01

    In this study, quaternary phosphate-based sol-gel derived glasses were synthesized from a P 2 O 5 -CaO-Na 2 O-TiO 2 system with a high TiO 2 content of up to 50 mol%. The sol-gel method was chosen because incorporating a high percentage of titanium into a phosphate network via traditional melt-quench methods is non-trivial. The structure and thermal properties of the obtained stabilized sol-gel glasses were characterized using X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, and differential scanning calorimetry (DSC). The XRD results confirmed the amorphous nature of all of the stabilized sol–gel derived glasses. The FTIR results revealed that added TiO 2 enters the network as (TiO 6 ), which likely acts as a modifier oxide. Consequently, the number of terminal oxygen atoms increases, leading to an increase in the number of P-OH bonds. In addition, DSC results confirmed a decrease in glass transition and crystallization temperatures with increasing TiO 2 content. This is the first report of a sol-gel synthesis strategy combined with enameling to prepare glass at low processing temperatures and the first use of such a system for both hydrophilic and chemical resistance purposes.

  13. Nanocrystalline Ni-Zn ferrites prepared by sol-gel method

    Czech Academy of Sciences Publication Activity Database

    Popovici, M.; Savii, C.; Nižňanský, Daniel; Šubrt, Jan; Boháček, Jaroslav; Becherescu, D.; Caizer, C.; Enache, C.; Ionescu, C.

    2003-01-01

    Roč. 5, č. 1 (2003), s. 251-256 ISSN 1454-4164 R&D Projects: GA MŠk LN00A028 Institutional research plan: CEZ:AV0Z4032918 Keywords : nanostructures * sol-gel processing * XRD Subject RIV: CA - Inorganic Chemistry Impact factor: 0.996, year: 2003

  14. Foldable and Cytocompatible Sol-gel TiO2 Photonics.

    Science.gov (United States)

    Li, Lan; Zhang, Ping; Wang, Wei-Ming; Lin, Hongtao; Zerdoum, Aidan B; Geiger, Sarah J; Liu, Yangchen; Xiao, Nicholas; Zou, Yi; Ogbuu, Okechukwu; Du, Qingyang; Jia, Xinqiao; Li, Jingjing; Hu, Juejun

    2015-09-07

    Integrated photonics provides a miniaturized and potentially implantable platform to manipulate and enhance the interactions between light and biological molecules or tissues in in-vitro and in-vivo settings, and is thus being increasingly adopted in a wide cross-section of biomedical applications ranging from disease diagnosis to optogenetic neuromodulation. However, the mechanical rigidity of substrates traditionally used for photonic integration is fundamentally incompatible with soft biological tissues. Cytotoxicity of materials and chemicals used in photonic device processing imposes another constraint towards these biophotonic applications. Here we present thin film TiO2 as a viable material for biocompatible and flexible integrated photonics. Amorphous TiO2 films were deposited using a low temperature (<250 °C) sol-gel process fully compatible with monolithic integration on plastic substrates. High-index-contrast flexible optical waveguides and resonators were fabricated using the sol-gel TiO2 material, and resonator quality factors up to 20,000 were measured. Following a multi-neutral-axis mechanical design, these devices exhibit remarkable mechanical flexibility, and can sustain repeated folding without compromising their optical performance. Finally, we validated the low cytotoxicity of the sol-gel TiO2 devices through in-vitro cell culture tests. These results demonstrate the potential of sol-gel TiO2 as a promising material platform for novel biophotonic devices.

  15. Sol-gel immobilization of serine proteases for application in organic solvents

    NARCIS (Netherlands)

    van Unen, D.J.; Engbersen, Johannes F.J.; Reinhoudt, David

    2001-01-01

    The serine proteases α-chymotrypsin, trypsin, and subtilisin Carlsberg were immobilized in a sol-gel matrix and the effects on the enzyme activity in organic media are evaluated. The percentage of immobilized enzyme is 90% in the case of α-chymotrypsin and the resulting specific enzyme activity in

  16. Sol-gel coatings of ceramic fibres for composites with ceramic matrix

    International Nuclear Information System (INIS)

    Maier, B.; Grathwohl, G.; Spallek, M.; Pannhorst, W.

    1992-01-01

    The aim of this work was to show the feasibility in principle of sol-gel coating of ceramic reinforcement components for composites from technical aspects as well. The complexity of the coating task rises with the transition from individual fibres to bundles of fibres of different thickness to weaves, and finally to composites. (orig.) [de

  17. Sol-gel deposition of buffer layers on biaxially textured metal substances

    Science.gov (United States)

    Shoup, Shara S.; Paranthamam, Mariappan; Beach, David B.; Kroeger, Donald M.; Goyal, Amit

    2000-01-01

    A method is disclosed for forming a biaxially textured buffer layer on a biaxially oriented metal substrate by using a sol-gel coating technique followed by pyrolyzing/annealing in a reducing atmosphere. This method is advantageous for providing substrates for depositing electronically active materials thereon.

  18. Hybrid Thin Film Organosilica Sol-Gel Coatings To Support Neuronal Growth and Limit Astrocyte Growth.

    Science.gov (United States)

    Capeletti, Larissa Brentano; Cardoso, Mateus Borba; Dos Santos, João Henrique Zimnoch; He, Wei

    2016-10-07

    Thin films of silica prepared by a sol-gel process are becoming a feasible coating option for surface modification of implantable neural sensors without imposing adverse effects on the devices' electrical properties. In order to advance the application of such silica-based coatings in the context of neural interfacing, the characteristics of silica sol-gel are further tailored to gain active control of interactions between cells and the coating materials. By incorporating various readily available organotrialkoxysilanes carrying distinct organic functional groups during the sol-gel process, a library of hybrid organosilica coatings is developed and investigated. In vitro neural cultures using PC12 cells and primary cortical neurons both reveal that, among these different types of hybrid organosilica, the introduction of aminopropyl groups drastically transforms the silica into robust neural permissive substrate, supporting neuron adhesion and neurite outgrowth. Moreover, when this organosilica is cultured with astrocytes, a key type of glial cells responsible for glial scar response toward neural implants, such cell growth promoting effect is not observed. These findings highlight the potential of organo-group-bearing silica sol-gel to function as advanced coating materials to selectively modulate cell response and promote neural integration with implantable sensing devices.

  19. Improving the temperature performance of low-density ceramic heatshields through sol-gel processing

    Science.gov (United States)

    Bull, Jeffrey; Leiser, Daniel; Sommers, Jeneen; Esfahani, Lili

    1991-01-01

    The performance of rigid insulations for use as thermal protection materials on reentry vehicles can be characterized by their resistance to dimensional and morphological change when exposed to an isothermal environment equivalent to that generated in entry. Improvements in these material characteristics for alumina-enhanced thermal barrier insulation by compositional modification through sol-gel processing are reported.

  20. Gel stabilization in chelate sol-gel preparation of Bi-2223 superconductors

    Czech Academy of Sciences Publication Activity Database

    Rubešová, K.; Jakeš, V.; Hlásek, T.; Vašek, Petr; Matějka, P.

    2012-01-01

    Roč. 73, č. 3 (2012), s. 448-453 ISSN 0022-3697 Institutional research plan: CEZ:AV0Z10100521 Keywords : superconductors * sol-gel growth * infrared spectroscopy * thermogravimetric analysis (TGA) * X-ray diffraction Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.527, year: 2012