Crystal size effect on the electrochemical oxidation of formate on carbon-supported palladium nanoparticles

International Nuclear Information System (INIS)

Santos, Rayana Marcela Izidoro da Silva; Nakazato, Roberto Zenhei; Ciapina, Eduardo Goncalves

2016-01-01

Full text: The electrochemical oxidation of formate in alkaline electrolytes has emerged an a promising anodic reaction in the Direct Formate Fuel Cells[1]. Although palladium is considered to be one of the best electro catalyst for the oxidation of formate, important structure-activity relationships are still not understood. In the present work, we investigated the effect of the size of the palladium crystals in the electrochemical oxidation of formate in 0.1 mol L -1 KOH. Carbon-supported palladium nanoparticles (Pd/C) were prepared by chemical reduction of palladium (II) chloride in aqueous media by sodium borohydride in the presence of varying quantities of sodium citrate in the reaction media to obtain metallic crystals with distinct sizes. Analysis of the X-ray diffraction profile revealed the presence of palladium crystals in the range of 6 to 19 nm. Potentiostatic oxidation of formate on the distinct Pd/C samples revealed a volcano-like dependence of the specific activity with the size of the palladium crystals, presenting the highest activity for crystals around 7.5 nm. Reference: [1] A.M. Bartrom, J.L. Haan, The direct formate fuel cell with an alkaline anion exchange membrane, J. Power Sources. 214 (2012) 68-74. (author)

Fuel clean-up: poisoning of palladium-silver membranes by gaseous impurities

International Nuclear Information System (INIS)

Chabot, J.; Lecomte, J.; Grumet, C.; Sannier, J.

1988-01-01

The feasibility of a permeation process using a palladium-silver alloy membrane, to separate deuterium and tritium from fusion reactor gaseous wastes needs demonstration owing to poisoning effects of impurities. A parametric investigation of the poisoning by the most important expected gaseous impurities (C0, C0 2 and CH 4 ) is carried out with the loop PALLAS, in function of membrane temperature (100 to 450 0 C), H 2 pressure (0.3 to 14 kPa) and impurity concentration (0.2 to 9.5 vol. %). The poisoning effect of C0 is a concern for the process while C0 2 and CH 4 appear to have no practical effect on the permeation rate. Depending on C0 concentration optimal operating temperatures of the membrane should lie between 250 and 375 0 C limits

Organometallic approach to polymer-protected antibacterial silver nanoparticles: optimal nanoparticle size-selection for bacteria interaction

Energy Technology Data Exchange (ETDEWEB)

Crespo, Julian; Garcia-Barrasa, Jorge; Lopez-de-Luzuriaga, Jose M.; Monge, Miguel, E-mail: miguel.monge@unirioja.es; Olmos, M. Elena [Universidad de La Rioja, Centro de Investigacion en Sintesis Quimica (CISQ), Departamento de Quimica (Spain); Saenz, Yolanda; Torres, Carmen [Centro de Investigacion Biomedica de La Rioja, Area de Microbiologia Molecular (Spain)

2012-12-15

The optimal size-specific affinity of silver nanoparticles (Ag NPs) towards E. coli bacteria has been studied. For this purpose, Ag NPs coated with polyvinylpyrrolidone (PVP) and cellulose acetate (CA) have been prepared using an organometallic approach. The complex NBu{sub 4}[Ag(C{sub 6}F{sub 5}){sub 2}] has been treated with AgClO{sub 4} in a 1:1 molar ratio giving rise to the nanoparticle precursor [Ag(C{sub 6}F{sub 5})] in solution. Addition of an excess of PVP (1) or CA (2) and 5 h of reflux in tetrahydrofuran (THF) at 66 Degree-Sign C leads to Ag NPs of small size (4.8 {+-} 3.0 nm for PVP-Ag NPs and 3.0 {+-} 1.2 nm for CA-Ag NPs) that coexist in both cases with larger nanoparticles between 7 and 25 nm. Both nanomaterials display a high antibacterial effectiveness against E. coli. The TEM analysis of the nanoparticle-bacterial cell membrane interaction shows an optimal size-specific affinity for PVP-Ag NPs of 5.4 {+-} 0.7 nm in the presence of larger size silver nanoparticles.Graphical AbstractAn organometallic approach permits the synthesis of small size silver nanoparticles (ca 5 nm) as a main population in the presence of larger size nanoparticles. Optimal silver nanoparticle size-selection (5.4 nm) for the interaction with the bacterial membrane is achieved.

Size control and supporting of palladium nanoparticles made by laser ablation in saline solution as a facile route to heterogeneous catalysts

International Nuclear Information System (INIS)

Marzun, Galina; Nakamura, Junji; Zhang, Xiaorui; Barcikowski, Stephan; Wagener, Philipp

2015-01-01

Graphical abstract: - Highlights: • We studied laser-generated, size-controlled palladium nanoparticles in saline solution. • Palladium nanoparticles were electrostatically stabilized by anions. • Photo- and electrocatalyst are prepared by supporting Pd nanoparticles to TiO 2 and graphene. • Particle size does not change during supporting process, while 18 wt% load has been achieved. • Palladium nanoparticles and graphene undergo a redox-reaction during adsorption. - Abstract: In the literature many investigations on colloidal stability and size control of gold nanoparticles are shown but less for ligand-free palladium nanoparticles, which can be promising materials in various applications. Palladium nanoparticles are perspective materials for a manifold of energy application like photo- and electrocatalysis or hydrogen storage. For this purpose, size-controlled nanoparticles with clean surfaces and facile immobilization on catalyst supports are wanted. Laser ablation in saline solution yields ligand-free, charged colloidal palladium nanoparticles that are supported by titania and graphene nanosheets as model systems for photo- and electrocatalysis, respectively. By adjusting the ionic strength during laser ablation in liquid, it is possible to control stability and particle size without compromising subsequent nanoparticle adsorption of supporting materials. A quantitative deposition of nearly 100% yield with up to 18 wt% nanoparticle load was achieved. The average size of the laser-generated nanoparticles remains the same after immobilization on a support material, in contrast to other preparation methods of catalysts. The characterization by X-ray photoelectron spectroscopy reveals a redox reaction between the immobilized nanoparticles and the graphene support

Adsorption of volatile polonium species on metals in various gas atmospheres. Pt. II. Adsorption of volatile polonium on platinum, silver and palladium

Energy Technology Data Exchange (ETDEWEB)

Maugeri, Emilio Andrea; Joerg Neuhausen; Dressler, Rugard; Piguet, David; Voegele, Alexander; Schumann, Dorothea [Paul Scherrer Institut (PSI), Villigen (Switzerland). Lab. for Radiochemistry; Misiak, Ryszard [The Henryk Niewodniczanski Institute of Nuclear Physics, Krakow (Poland); Eichler, Robert [Paul Scherrer Institut (PSI), Villigen (Switzerland). Lab. for Radiochemistry; Bern Univ. (Switzerland). Dept. for Chemistry and Biochemistry

2016-07-01

This work presents the results obtained from studying the interaction between polonium compounds formed in different atmospheres and platinum, palladium and silver surfaces obtained by thermochromatography. These results are of crucial importance for the design of cover gas filter systems for lead-bismuth eutectic (LBE)-based nuclear facilities such as accelerator driven systems (ADS). The results obtained from studying the interaction of polonium and platinum under inert atmosphere and reducing atmospheres with and without addition of moisture show that polonium is deposited at temperatures between 993 and 1221 K, with adsorption enthalpies ranging from -235 to -291 kJ mol{sup -1}, indicating a very strong adsorption of the polonium species present on platinum surfaces. The interaction between polonium and silver was investigated using purified inert, reducing and oxidizing carrier gases. Results show a deposition temperature between 867 and 990 K, with adsorption enthalpies ranging from -205 to -234 kJ mol{sup -1}. The interaction of polonium and palladium was studied in purified helium and purified hydrogen. For both conditions a deposition temperature of 1221 K was observed corresponding to an adsorption enthalpy of -340 kJ mol{sup -1}. No highly volatile polonium species was formed at any of the applied experimental conditions.

Selective extraction of copper, mercury, silver and palladium ionsfrom water using hydrophobic ionic liquids.

Energy Technology Data Exchange (ETDEWEB)

Papaiconomou, Nicolas; Lee, Jong-Min; Salminen, Justin; VonStosch, Moritz; Prausnitz, John M.

2007-06-25

Extraction of dilute metal ions from water was performed near room temperature with a variety of ionic liquids. Distribution coefficients are reported for fourteen metal ions extracted with ionic liquids containing cations 1-octyl-4-methylpyridinium [4MOPYR]{sup +}, 1-methyl-1-octylpyrrolidinium [MOPYRRO]{sup +} or 1-methyl-1-octylpiperidinium [MOPIP]{sup +}, and anions tetrafluoroborate [BF{sub 4}]{sup +}, trifluoromethyl sulfonate [TfO]{sup +} or nonafluorobutyl sulfonate [NfO]{sup +}. Ionic liquids containing octylpyridinium cations are very good for extracting mercury ions. However, other metal ions were not significantly extracted by any of these ionic liquids. Extractions were also performed with four new task-specific ionic liquids. Such liquids containing a disulfide functional group are efficient and selective for mercury and copper, whereas those containing a nitrile functional group are efficient and selective for silver and palladium.

Glass frits coated with silver nanoparticles for silicon solar cells

International Nuclear Information System (INIS)

Li, Yingfen; Gan, Weiping; Zhou, Jian; Li, Biyuan

2015-01-01

Graphical abstract: - Highlights: • Silver-coated glass frits for solar cells were prepared by electroless plating. • Gum Arabic was used as the activating agent of glass frits. • Silver-coated glass frits can improve the photovoltaic performances of solar cells. - Abstract: Glass frits coated with silver nanoparticles were prepared by electroless plating. Gum Arabic (GA) was used as the activating agent of glass frits without the assistance of stannous chloride or palladium chloride. The silver-coated glass frits prepared with different GA dosages were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and thermogravimetric analysis (TGA). The characterization results indicated that silver-coated glass frits had the structures of both glass and silver. Spherical silver nanoparticles were distributed on the glass frits evenly. The density and particle size of silver nanoparticles on the glass frits can be controlled by adjusting the GA dosage. The silver-coated glass frits were applied to silver pastes to act as both the densification promoter and silver crystallite formation aid in the silver electrodes. The prepared silver-coated glass frits can improve the photovoltaic performances of solar cells

Glass frits coated with silver nanoparticles for silicon solar cells

Energy Technology Data Exchange (ETDEWEB)

Li, Yingfen, E-mail: lyf350857423@163.com; Gan, Weiping; Zhou, Jian; Li, Biyuan

2015-06-30

Graphical abstract: - Highlights: • Silver-coated glass frits for solar cells were prepared by electroless plating. • Gum Arabic was used as the activating agent of glass frits. • Silver-coated glass frits can improve the photovoltaic performances of solar cells. - Abstract: Glass frits coated with silver nanoparticles were prepared by electroless plating. Gum Arabic (GA) was used as the activating agent of glass frits without the assistance of stannous chloride or palladium chloride. The silver-coated glass frits prepared with different GA dosages were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and thermogravimetric analysis (TGA). The characterization results indicated that silver-coated glass frits had the structures of both glass and silver. Spherical silver nanoparticles were distributed on the glass frits evenly. The density and particle size of silver nanoparticles on the glass frits can be controlled by adjusting the GA dosage. The silver-coated glass frits were applied to silver pastes to act as both the densification promoter and silver crystallite formation aid in the silver electrodes. The prepared silver-coated glass frits can improve the photovoltaic performances of solar cells.

Determination of the Debye-Waller Factor of hydrogen in Palladium and Palladium Silver alloy

International Nuclear Information System (INIS)

Khodabakhsh, R.

1986-01-01

The mean square amplitude of the vibrating hydrogen in metals can be determined by using coherent elastic neutron scattering experiments, inelastic one-phonon scattering measurements. To determine the D.W.F. Debye-Waller Factor from the coherent elastic scattering measurements, information about the positions of atoms within the unit is required, and vice versa. The main difficulty concerning the determination of the D.W.F. from the inelastic experiment is in elimination of multi-phonon contribution from the measured spectrum. However, the D.W.F. of hydrogen in palladium has been usually determined by the intensity of the quasi-elastic line. An integration of the measured scattering law S(Q,W) at constant Q, over a certain energy window ΔE, results in the quasi-elastic intensity. To obtain an accurate result, this window has to be chosen large enough to comprise most of the quasi-elastic line, but sufficiently small so that the phonon contributions are small. The MARX spectrometer is ideally constructed for this type of measurement where the window is about +-1 Mev for incident neutron wavelength, =4.115 A. Thus, the quasi-elastic scattering method was considered the best method of determining the D.W.F. of hydrogen in palladium using the MARX spectrometer. However, if the acoustic part overlaps with the quasi-elastic part, one has to obtain the D.W.F. by fitting the data to a quasi-elastic model. The work to be reported here is the investigation of variations of the D.W.F. of hydrogen in Pd and PdAgsub(0.085) with temperature and extension of the available data to as high a temperature as possible. Therefore the integrated intensity of incoherent quasi-elastic neutron scattering by proton in polycrystallin Pd/H and PdAgsub(0.085)/H was investigated as a function of the scattering vector Q. A quasi-harmonic D.W.F. behaviour was observed at elevated temperatures. The observed Debye-Waller Factor depends strongly on the form of the amplitude weighted frequency

Size-dependent surface plasmon resonance in silver silica nanocomposites

International Nuclear Information System (INIS)

Thomas, Senoy; Nair, Saritha K; Jamal, E Muhammad Abdul; Anantharaman, M R; Al-Harthi, S H; Varma, Manoj Raama

2008-01-01

Silver silica nanocomposites were obtained by the sol-gel technique using tetraethyl orthosilicate (TEOS) and silver nitrate (AgNO 3 ) as precursors. The silver nitrate concentration was varied for obtaining composites with different nanoparticle sizes. The structural and microstructural properties were determined by x-ray diffractometry (XRD), Fourier transform infrared spectroscopy (FTIR) and transmission electron microscopy (TEM). X-ray photoelectron spectroscopic (XPS) studies were done for determining the chemical states of silver in the silica matrix. For the lowest AgNO 3 concentration, monodispersed and spherical Ag crystallites, with an average diameter of 5 nm, were obtained. Grain growth and an increase in size distribution was observed for higher concentrations. The occurrence of surface plasmon resonance (SPR) bands and their evolution in the size range 5-10 nm is studied. For decreasing nanoparticle size, a redshift and broadening of the plasmon-related absorption peak was observed. The observed redshift and broadening of the SPR band was explained using modified Mie scattering theory

Size dependence of the optical spectrum in nanocrystalline silver

International Nuclear Information System (INIS)

Taneja, Praveen; Ayyub, Pushan; Chandra, Ramesh

2002-01-01

We report a detailed study of the optical reflectance in sputter-deposited, nanocrystalline silver thin films in order to understand the marked changes in color that occur with decreasing particle size. In particular, samples with an average particle size in the 20 to 35 nm range are golden yellow, while those with a size smaller than 15 nm are black. We simulate the size dependence of the observed reflection spectra by incorporating Mie's theory of scattering and absorption of light in small particles, into the bulk dielectric constant formalism given by Ehrenreich and Philipp [Phys. Rev. 128, 1622 (1962)]. This provides a general method for understanding the reflected color of a dense collection of nanoparticles, such as in a nanocrystalline thin film. A deviation from Mie's theory is observed due to strong interparticle interactions

Size-Controlled Dissolution of Organic-Coated Silver Nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Ma, Rui; Levard, Clément; Marinakos, Stella M.; Cheng, Yingwen; Liu, Jie; Michel, F. Marc; Brown, Jr., Gordon E.; Lowry, Gregory V. (Duke)

2012-04-02

The solubility of Ag NPs can affect their toxicity and persistence in the environment. We measured the solubility of organic-coated silver nanoparticles (Ag NPs) having particle diameters ranging from 5 to 80 nm that were synthesized using various methods, and with different organic polymer coatings including poly(vinylpyrrolidone) and gum arabic. The size and morphology of Ag NPs were characterized by transmission electron microscopy (TEM). X-ray absorption fine structure (XAFS) spectroscopy and synchrotron-based total X-ray scattering and pair distribution function (PDF) analysis were used to determine the local structure around Ag and evaluate changes in crystal lattice parameters and structure as a function of NP size. Ag NP solubility dispersed in 1 mM NaHCO{sub 3} at pH 8 was found to be well correlated with particle size based on the distribution of measured TEM sizes as predicted by the modified Kelvin equation. Solubility of Ag NPs was not affected by the synthesis method and coating as much as by their size. Based on the modified Kelvin equation, the surface tension of Ag NPs was found to be {approx}1 J/m{sup 2}, which is expected for bulk fcc (face centered cubic) silver. Analysis of XAFS, X-ray scattering, and PDFs confirm that the lattice parameter, {alpha}, of the fcc crystal structure of Ag NPs did not change with particle size for Ag NPs as small as 6 nm, indicating the absence of lattice strain. These results are consistent with the finding that Ag NP solubility can be estimated based on TEM-derived particle size using the modified Kelvin equation for particles in the size range of 5-40 nm in diameter.

Preparation of palladium impregnated alumina adsorbents: Thermal and neutron activation analysis

Energy Technology Data Exchange (ETDEWEB)

Mukherjee, Sumanta; Gupta, N.K.; Roy, S.P.; Dash, S.; Kumar, A.; Bamankar, Y.R.; Rao, T.V. Vittal [Product Development Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Kumar, N. [Fuel Chemistry Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Naik, Y., E-mail: ynaik@barc.gov.in [Product Development Division, Bhabha Atomic Research Centre, Mumbai 400085 (India)

2016-02-10

Highlights: • Pd/Al{sub 2}O{sub 3} composite microspheres particles with high surface area were prepared sol–gel process. • Scanning electron microscopy (SEM) studies on silver coated particle. • Content of the palladium was determined using Neutron Activation Analysis (NAA). • Decomposition study has been done by quadrupole mass analyser. - Abstract: Pd/Al{sub 2}O{sub 3} composite microspheres particles with high surface area were prepared sol–gel process. The decomposition of dried gel-particles was studied by TGA/DTA and FT-IR technique. TGA studies indicated that formation of palladium is marked by a broad exothermic peak with a loss of water and oxidation of trapped HMTA/Urea nitrate mixture. The main decomposition reaction took place in the temperature range of 660–1250 K in helium and relatively lower temperature of 400 K to 1250 K in oxygen. Optical microscopy indicated that the distribution of palladium is uniform. SEM studies on silver coated particle indicated that there was surface erosion of some gel spheres while in few of them micro cracks were seen at high resolution. Content of the palladium was determined using Neutron Activation Analysis (NAA). Decomposition at various temperatures was studied using Residual gas analyser and decomposition species were identified using quadrupole mass analyser.

Silver nanoparticles: synthesis and size control by electron irradiation

Energy Technology Data Exchange (ETDEWEB)

Bogle, K A; Dhole, S D; Bhoraskar, V N [Microtron Accelerator Laboratory, Department of Physics, University of Pune, Pune-411007 (India)

2006-07-14

Silver nanoparticles were synthesized by irradiating solutions, prepared by mixing AgNO{sub 3} and poly-vinyl alcohol (PVA), with 6 MeV electrons. The electron-irradiated solutions and the thin coatings cast from them were characterized using the ultraviolet-visible (UV-vis), x-ray diffraction (XRD), transmission electron microscopy (TEM) and scanning electron microscopy (SEM) techniques. During electron irradiation, the process of formation of the silver nanoparticles appeared to be initiated at an electron fluence of {approx}2 x 10{sup 13} e cm{sup -2}. This was evidenced from the solution, which turned yellow and exhibited the characteristic plasmon absorption peak around 455 nm. Silver nanoparticles of different sizes in the range 60-10 nm, with a narrow size distribution, could be synthesized by varying the electron fluence from 2 x 10{sup 13} to 3 x 10{sup 15} e cm{sup -2}. Silver nanoparticles of sizes in the range 100-200 nm were also synthesized by irradiating an aqueous AgNO{sub 3} solution with 6 MeV electrons.

Co-deposition of palladium with hydrogen isotopes

International Nuclear Information System (INIS)

Dash, J.; Ambadkar, A.

2006-01-01

Palladium was co-deposited with hydrogen isotopes on a Pd cathode. This resulted in enhanced production of excess thermal power. After electrolysis the Pd Lβ/ Lα ratio was found to be increased in characteristic X-ray spectra from localized, microscopic areas on the surface of the Pd cathode. This suggests the possibility that appreciable amounts of silver are present in these areas. (authors)

Size distribution of silver nanoclusters induced by ion, electron, laser beams and thermal treatments of an organometallic precursor

International Nuclear Information System (INIS)

D'Urso, L.; Nicolosi, V.; Compagnini, G.; Puglisi, O.

2004-01-01

Recently, a huge variety of physical and chemical synthetic processes have been reported to prepare nanostructured materials made of very small (diameter<50 nm) metallic clusters. Depending on the nature of clusters, this new kind of materials posses interesting properties (electronic, optical, magnetic, catalytic) that can be tailored as a function of the particles size and shape. Silver nanoparticles have been obtained by direct thermal treatment or by beam-enhanced decomposition (ion, electron and laser) of a silver organometallic compound (precursor) spinned onto suitable substrates. In this paper, we present the results of a study on the size distribution of such nanoparticles as a function of the different synthesis methods. It was found that the methods employed strongly affect the silver nanoparticles formation. Smaller silver nanoclusters were obtained after reduction by ion beam irradiation and thermal treatment, as observed by using different techniques (AFM, XRD and UV-Vis)

Influence of size-corrected bound-electron contribution on nanometric silver dielectric function. Sizing through optical extinction spectroscopy

International Nuclear Information System (INIS)

Santillán, J M J; Videla, F A; Scaffardi, L B; Schinca, D C; Fernández van Raap, M B; Muraca, D

2013-01-01

The study of metal nanoparticles (NPs) is of great interest due to their ability to enhance optical fields on the nanometric scale, which makes them interesting for various applications in several fields of science and technology. In particular, their optical properties depend on the dielectric function of the metal, its size, shape and surrounding environment. This work analyses the contributions of free and bound electrons to the complex dielectric function of spherical silver NPs and their influence on the optical extinction spectra. The contribution of free electrons is usually corrected for particle size under 10 nm, introducing a modification of the damping constant to account for the extra collisions with the particle's boundary. For the contribution of bound electrons, we considered the interband transitions from the d-band to the conduction band including the size dependence of the electronic density states for radii below 2 nm. Bearing in mind these specific modifications, it was possible to determine optical and band energy parameters by fitting the bulk complex dielectric function. The results obtained from the optimum fit are: K bulk = 2 × 10 24 (coefficient for bound-electron contribution), E g = 1.91 eV (gap energy), E F = 4.12 eV (Fermi energy), and γ b = 1.5 × 10 14 Hz (damping constant for bound electrons). Based on this size-dependent dielectric function, extinction spectra of silver particles in the nanometric–subnanometric radius range can be calculated using Mie's theory, and its size behaviour analysed. These studies are applied to fit experimental extinction spectrum of very small spherical particles fabricated by fs laser ablation of a solid target in water. From the fitting, the structure and size distribution of core radius and shell thickness of the colloidal suspension could be determined. The spectroscopic results suggest that the colloidal suspension is composed by two types of structures: bare core and core–shell. The former

Size effects in electronic and catalytic properties of unsupported palladium nanoparticles in electrooxidation of formic acid.

Science.gov (United States)

Zhou, Wei Ping; Lewera, Adam; Larsen, Robert; Masel, Rich I; Bagus, Paul S; Wieckowski, Andrzej

2006-07-13

We report a combined X-ray photoelectron spectroscopy (XPS), cyclic voltammetry (CV), and chronoamperometry (CA) study of formic acid electrooxidation on unsupported palladium nanoparticle catalysts in the particle size range from 9 to 40 nm. The CV and CA measurements show that the most active catalyst is made of the smallest (9 and 11 nm) Pd nanoparticles. Besides the high reactivity, XPS data show that such nanoparticles display the highest core-level binding energy (BE) shift and the highest valence band (VB) center downshift with respect to the Fermi level. We believe therefore that we found a correlation between formic acid oxidation current and BE and VB center shifts, which, in turn, can directly be related to the electronic structure of palladium nanoparticles of different particle sizes. Clearly, such a trend using unsupported catalysts has never been reported. According to the density functional theory of heterogeneous catalysis, and mechanistic considerations, the observed shifts are caused by a weakening of the bond strength of the COOH intermediate adsorption on the catalyst surface. This, in turn, results in the increase in the formic acid oxidation rate to CO2 (and in the associated oxidation current). Overall, our measurements demonstrate the particle size effect on the electronic properties of palladium that yields different catalytic activity in the HCOOH oxidation reaction. Our work highlights the significance of the core-level binding energy and center of the d-band shifts in electrocatalysis and underlines the value of the theory that connects the center of the d-band shifts to catalytic reactivity.

Green synthesis of silver nanoparticles using Beta vulgaris: Role of process conditions on size distribution and surface structure

Energy Technology Data Exchange (ETDEWEB)

Parameshwaran, R., E-mail: parameshviews@gmail.com [Department of Mechanical Engineering, Anna University, Chennai 600 025 (India); Centre for Nanoscience and Technology, Anna University, Chennai 600 025 (India); Kalaiselvam, S., E-mail: kalai@annauniv.edu [Centre for Nanoscience and Technology, Anna University, Chennai 600 025 (India); Department of Applied Science and Technology, Anna University, Chennai 600 025 (India); Jayavel, R., E-mail: rjvel@annauniv.edu [Centre for Nanoscience and Technology, Anna University, Chennai 600 025 (India)

2013-06-15

The present work reports the green synthesis of silver nanoparticles, using Beta vulgaris peel extract with a subsequent investigation on the size distribution and surface structure of nanoparticles formed under various process conditions. The green-chemical reduction mechanism of silver ions to nanoparticles by the active organic functional groups present in the extract was characterized, using the respective spectroscopic techniques. The effects of various process parameters, including induced intraparticle ripening, were attributed to the controlled formation of anisotropic silver nanoparticles within the supporting matrix of the extract. The plasmon absorption and resonance scattering properties were expected to be favourable for small and larger size nanoparticles (below 25 nm and above 75 nm) respectively, which was considered to be an indicative aspect for synthesizing nanoparticles of narrow size distribution. The zeta potential and dynamic light scattering (DLS) results suggest the good stability and mono-dispersed size distribution of the silver nanoparticles. The transmission electron microscope, selective area electron diffraction (SAED) and X-ray diffraction studies infer that the nanoparticles formed were spherical/quasi-spherical in shape, which primarily exhibited a face centred cubic crystal (FCC) structure. The green-chemical reduction of organic phases in the extract (especially amine (NH{sub 2}) groups) as reflected through shifts observed in the Fourier-transform infra red (FTIR) peaks, reveal the possible interaction of the organic molecules with the silver ions in the effective formation, surface modification and stabilization of the silver nanoparticles. - Highlights: • Functionally stable and crystalline silver nanoparticles were green synthesized. • Beta vulgaris peel extract was used as potential reducing and stabilizing agent. • Amine groups in extract were expected to reduce Ag{sup +} and stabilize nanoparticles. • Induced

Green synthesis of silver nanoparticles using Beta vulgaris: Role of process conditions on size distribution and surface structure

International Nuclear Information System (INIS)

Parameshwaran, R.; Kalaiselvam, S.; Jayavel, R.

2013-01-01

The present work reports the green synthesis of silver nanoparticles, using Beta vulgaris peel extract with a subsequent investigation on the size distribution and surface structure of nanoparticles formed under various process conditions. The green-chemical reduction mechanism of silver ions to nanoparticles by the active organic functional groups present in the extract was characterized, using the respective spectroscopic techniques. The effects of various process parameters, including induced intraparticle ripening, were attributed to the controlled formation of anisotropic silver nanoparticles within the supporting matrix of the extract. The plasmon absorption and resonance scattering properties were expected to be favourable for small and larger size nanoparticles (below 25 nm and above 75 nm) respectively, which was considered to be an indicative aspect for synthesizing nanoparticles of narrow size distribution. The zeta potential and dynamic light scattering (DLS) results suggest the good stability and mono-dispersed size distribution of the silver nanoparticles. The transmission electron microscope, selective area electron diffraction (SAED) and X-ray diffraction studies infer that the nanoparticles formed were spherical/quasi-spherical in shape, which primarily exhibited a face centred cubic crystal (FCC) structure. The green-chemical reduction of organic phases in the extract (especially amine (NH 2 ) groups) as reflected through shifts observed in the Fourier-transform infra red (FTIR) peaks, reveal the possible interaction of the organic molecules with the silver ions in the effective formation, surface modification and stabilization of the silver nanoparticles. - Highlights: • Functionally stable and crystalline silver nanoparticles were green synthesized. • Beta vulgaris peel extract was used as potential reducing and stabilizing agent. • Amine groups in extract were expected to reduce Ag + and stabilize nanoparticles. • Induced intraparticle

Simple and environmentally friendly preparation and size control of silver nanoparticles using an inhomogeneous system with silver-containing glass powder

International Nuclear Information System (INIS)

Mori, Yasutaka; Tagawa, Toshio; Fujita, Masanori; Kuno, Toyohiko; Suzuki, Satoshi; Matsui, Takemi; Ishihara, Masayuki

2011-01-01

A simple, environmentally friendly method for preparing highly size-controlled spherical silver nanoparticles was developed that involved heating a mixture of silver-containing glass powder and an aqueous solution of glucose. The stabilizing agent for silver nanoparticles was found to be caramel, which was generated from glucose when preparing the nanoparticles. The particle size was independent of the reaction time, but it increased proportionally with the square root of the glucose concentration in the range 0.25–8.0 wt% (corresponding to particle sizes of 3.48 ± 1.83 to 20.0 ± 2.76 nm). Difference of the generation mechanism of silver nanoparticles between this inhomogeneous system and a system in which Ag + was homogeneously dispersed was discussed.

Surface plasmon resonance-based fiber-optic hydrogen gas sensor utilizing palladium supported zinc oxide multilayers and their nanocomposite.

Science.gov (United States)

Tabassum, Rana; Gupta, Banshi D

2015-02-10

We analyze surface plasmon resonance-based fiber-optic sensor for sensing of small concentrations of hydrogen gas in the visible region of the electromagnetic spectrum. One of the two probes considered has multilayers of zinc oxide (ZnO) and palladium (Pd) while the other has layer of their composite over a silver coated unclad core of the fiber. The analysis is carried out for different volume fractions of palladium nanoparticles dispersed in zinc oxide host material in the nanocomposite layer. For the analysis, a Maxwell-Garnett model is adopted for calculating the dielectric function of a ZnO:Pd nanocomposite having nanoparticles of dimensions smaller than the wavelength of radiation used. The effects of the volume fraction of the nanoparticles in the nanocomposite and the thickness of the nanocomposite layer on the figure of merit of the sensor have been studied. The film thickness of the layer and the volume fraction of nanoparticles in the ZnO:Pd nanocomposite layer have been optimized to achieve the maximum value of the figure of merit of the sensor. It has been found that the figure of merit of the sensing probe coated with ZnO:Pd nanocomposite is more than twofold of the sensing probe coated with multilayers of Pd and ZnO over a silver coated unclad core of the fiber; hence, the sensor with a nanocomposite layer works better than that with multilayers of zinc oxide and palladium. The sensor can be used for online monitoring and remote sensing of hydrogen gas.

Size-dependent structure of silver nanoparticles under high pressure

Energy Technology Data Exchange (ETDEWEB)

Koski, Kristie Jo [Univ. of California, Berkeley, CA (United States)

2008-12-31

Silver noble metal nanoparticles that are<10 nm often possess multiply twinned grains allowing them to adopt shapes and atomic structures not observed in bulk materials. The properties exhibited by particles with multiply twinned polycrystalline structures are often far different from those of single-crystalline particles and from the bulk. I will present experimental evidence that silver nanoparticles<10 nm undergo a reversible structural transformation under hydrostatic pressures up to 10 GPa. Results for nanoparticles in the intermediate size range of 5 to 10 nm suggest a reversible linear pressure-dependent rhombohedral distortion which has not been previously observed in bulk silver. I propose a mechanism for this transitiion that considers the bond-length distribution in idealized multiply twinned icosahedral particles. Results for nanoparticles of 3.9 nm suggest a reversible linear pressure-dependent orthorhombic distortion. This distortion is interpreted in the context of idealized decahedral particles. In addition, given these size-dependent measurements of silver nanoparticle compression with pressure, we have constructed a pressure calibration curve. Encapsulating these silver nanoparticles in hollow metal oxide nanospheres then allows us to measure the pressure inside a nanoshell using x-ray diffraction. We demonstrate the measurement of pressure gradients across nanoshells and show that these nanoshells have maximum resolved shear strengths on the order of 500 MPa to IGPa.

Control size of silver nanoparticles in sol-gel glasses

Science.gov (United States)

Renteria, Victor M.; Celis, Antonio C.; Garcia-Macedo, Jorge A.

2000-10-01

By the sol-gel processing, silver ions in presence of stabilizing function (3-thiocyanatopropyl)triethoxysilane are reduced by heating gels at 180 C for several times in air atmosphere. The spectroscopic Uv-Vis observations, confirm silver nanoparticles presence with peak maximum around 350 nm. The optical properties of the metallic particles are observed at room temperature as function of time, and the absorption spectra practically do not change, which indicated they are trapped and stabilized within the fine porous silica cage. Mie theory calculations, considering the mean free path effect of the conduction electrons, are compatible with experimental spectra, indicating homogeneity in size and form of the metallic nanoparticles. Smithard correlation curve, between half width height (W1/2) of the optical absorption and the particle diameter 2r, predict silver particles size between 4 and 10 nm, during composite heating. Activation energy was measured and compared with previous data on similar systems and the probable reduction process are discussed.

Bacterial inhibiting surfaces caused by the effects of silver release and/or electrical field

DEFF Research Database (Denmark)

Chiang, Wen-Chi; Hilbert, Lisbeth Rischel; Schroll, Casper

2008-01-01

In this study, silver-palladium surfaces and silver-bearing stainless steels were designed and investigated focusing on electrochemical principles to form inhibiting effects on planktonic and/or biofilm bacteria in water systems. Silver-resistant Escherichia coli and silver-sensitive E. coli were...... silver ions release can occur from their Surfaces. For silver-bearing stainless steels, the inhibiting effect can only be explained by high local silver ions release. and can be limited or deactivated dependent on the specific environment. (c) 2008 Elsevier Ltd. All rights reserved....

Phenomenological in-situ TEM gas exposure studies of palladium particles on MgO at room temperature

Science.gov (United States)

Heinemann, K.; Poppa, H.; Osaka, T.

1983-01-01

It has been found that very small vapor-deposited catalytically active metal particles in the 1-2 nm size range on metal oxide substrates can undergo significant changes when they are exposed to gases such as oxygen or air, or even when allowed to 'anneal' at room temperature (RT) under vacuum conditions. The present investigation is concerned with continued in-situ gas exposures of as-deposited, 1 to 2 nm size palladium particles on MgO to air, oxygen, nitrogen, hydrogen, CO, and water vapor at RT. It is found that the low-pressure exposure to various gases at RT can significantly affect small palladium particles supported on MgO surfaces. Exposure to oxygen for 3 min at 0.0002 m bar produces a considerable amount of coalescence, flattening of the particles, and some distinct crystallographic particle shapes.

Preparation of Size-Controlled Silver Nanoparticles and Chitin-Based Composites and Their Antimicrobial Activities

Directory of Open Access Journals (Sweden)

Vinh Quang Nguyen

2013-01-01

Full Text Available A simple method for the preparation of size-controlled spherical silver nanoparticles (Ag NPs was reported for their generation by autoclaving a mixture of silver-containing glass powder and glucose. The particle size is regulated by the glucose concentration, with concentrations of 0.25, 1.0, and 4.0 wt% glucose providing small (3.48±1.83 nm in diameter, medium (6.53±1.78 nm, and large (12.9±2.5 nm particles, respectively. In this study, Ag NP/chitin composites were synthesized by mixing each of these three Ag NP suspensions with a <5% deacetylated (DAc chitin powder (pH 7.0 at room temperature. The Ag NPs were homogenously dispersed and stably adsorbed onto the chitin. The Ag NP/chitin composites were obtained as yellow or brown powders. Approximately 5, 15, and 20 μg of the small, medium, and large Ag NPs, respectively, were estimated to maximally adsorb onto 1 mg of chitin. The bactericidal and antifungal activities of the Ag NP/chitin composites increased as the amount of Ag NPs in the chitin increased. Furthermore, smaller Ag NPs (per weight in the chitin composites provided higher bactericidal and anti-fungal activities.

Laser induced morphology change of silver colloids: formation of nano-size wires

International Nuclear Information System (INIS)

Tsuji, Takeshi; Watanabe, Norihisa; Tsuji, Masaharu

2003-01-01

We have performed laser irradiation at 355 nm onto spherical silver colloids in pure water, which were prepared by laser ablation of silver plate in pure water. In addition to size-reduced particles due to fragmentation, we have found that nano-size wire structures were formed in solution for the first time. The width of the wires was in the 10-100 nm range, and the length of long wires was more than 1 μm. Electron diffraction patterns revealed that these wires were composed of pure silver. It was suggested that the wires were formed via fusion of particles photo-thermally melted by laser irradiation

Palladium nanoparticles on InP for hydrogen detection

Directory of Open Access Journals (Sweden)

Zdansky Karel

2011-01-01

Full Text Available Abstract Layers of palladium (Pd nanoparticles on indium phosphide (InP were prepared by electrophoretic deposition from the colloid solution of Pd nanoparticles. Layers prepared by an opposite polarity of deposition showed different physical and morphological properties. Particles in solution are separated and, after deposition onto the InP surface, they form small aggregates. The size of the aggregates is dependent on the time of deposition. If the aggregates are small, the layer has no lateral conductance. Forward and reverse I-V characteristics showed a high rectification ratio with a high Schottky barrier height. The response of the structure on the presence of hydrogen was monitored.

Facile Synthesis of Micron-Sized Hollow Silver Spheres as Substrates for Surface-Enhanced Raman Scattering

Directory of Open Access Journals (Sweden)

Lixin Xia

2014-01-01

Full Text Available A well-designed type of micron-sized hollow silver sphere was successfully synthesized by a simple hard-template method to be used as substrates for surface-enhanced Raman scattering. 4 Å molecular sieves were employed as a removable solid template. [Ag(NH32]+ was absorbed as the precursor on the surface of the molecular sieve. Formaldehyde was selected as a reducing agent to reduce [Ag(NH32]+, resulting in the formation of a micron-sized silver shell on the surface of the 4 Å molecular sieves. The micron-sized hollow silver spheres were obtained by removing the molecular sieve template. SEM and XRD were used to characterize the structure of the micron-sized hollow silver spheres. The as-prepared micro-silver spheres exhibited robust SERS activity in the presence of adsorbed 4-mercaptobenzoic acid (4-MBA with excitation at 632.8 nm, and the enhancement factor reached ~1.5 × 106. This synthetic process represents a promising method for preparing various hollow metal nanoparticles.

Environment friendly approach for size controllable synthesis of biocompatible Silver nanoparticles using diastase.

Science.gov (United States)

Maddinedi, Sireesh Babu; Mandal, Badal Kumar; Anna, Kiran Kumar

2017-01-01

A green, facile method for the size selective synthesis of silver nanoparticles (AgNPs) using diastase as green reducing and stabilizing agent is reported. The thiol groups present in the diastase are mainly responsible for the rapid reaction rate of silver nanoparticles synthesis. The variation in the size and morphology of AgNPs were studied by changing the pH of diastase. The prepared silver nanoparticles were characterized by using UV-vis, XRD, FTIR, TEM and SAED. The FTIR analysis revealed the stabilization of diastase molecules on the surface of AgNPs. Additionally, in-vitro cytotoxicity experiments concluded that the cytotoxicity of the as-synthesized AgNPs towards mouse fibroblast (3T3) cell lines is dose and size dependent. Furthermore, the present method is an alternative to the traditional chemical methods of size controlled AgNPs synthesis. Copyright © 2016 Elsevier B.V. All rights reserved.

[Antimicrobial activity of stable silver nanoparticles of a certain size].

Science.gov (United States)

Mukha, Iu P; Eremenko, A M; Smirnova, N P; Mikhienkova, A I; Korchak, G I; Gorchev, V F; Chunikhin, A Iu

2013-01-01

Conditions for obtaining stable silver nanoparticles smaller than 10 nm were developed using a binary stabilizer polyvinylpyrrolidone/sodium dodecylsulphate in optimal ratio. Optical spectra, morphology and dependence of size of the nanoparticles on the amount of reducing agent were studied. Colloidal solutions of nanosilver showed a high bactericidal activity against strains of Staphylococcus aureus, Escherichia coli and Pseudomonas aeruginosa, and fungicidal activity against Candida albicans. The mechanism of action of nanosized silver on microbial cell was examined by laser scanning confocal microscope using fluorescent label. First step of antimicrobial effect on microorganisms was membrane damage and penetration of silver nanoparticles into the cell. Prolonged stability of nanoparticles and their antimicrobial activity over the past two years were showed.

Potentiodynamic polarization study of the corrosion behavior of palladium-silver dental alloys.

Science.gov (United States)

Sun, Desheng; Brantley, William A; Frankel, Gerald S; Heshmati, Reza H; Johnston, William M

2018-04-01

Although palladium-silver alloys have been marketed for over 3 decades for metal-ceramic restorations, understanding of the corrosion behavior of current alloys is incomplete; this understanding is critical for evaluating biocompatibility and clinical performance. The purpose of this in vitro study was to characterize the corrosion behavior of 3 representative Pd-Ag alloys in simulated body fluid and oral environments and to compare them with a high-noble Au-Pd alloy. The study obtained values of important electrochemical corrosion parameters, with clinical relevance, for the rational selection of casting alloys. The room temperature in vitro corrosion characteristics of the 3 Pd-Ag alloys and the high-noble Au-Pd alloy were evaluated in 0.9% NaCl, 0.09% NaCl, and Fusayama solutions. After simulated porcelain firing heat treatment, 5 specimens of each alloy were immersed in the electrolytes for 24 hours. For each specimen, the open-circuit potential (OCP) was first recorded, and linear polarization was then performed from -20 mV to +20 mV (versus OCP) at a rate of 0.125 mV/s. Cyclic polarization was subsequently performed on 3 specimens of each alloy from -300 mV to +1000 mV and back to -300 mV (versus OCP) at a scanning rate of 1 mV/s. The differences in OCP and corrosion resistance parameters (zero-current potential and polarization resistance) among alloys and electrolyte combinations were compared with the 2-factor ANOVA (maximum-likelihood method) with post hoc Tukey adjustments (α=.05). The 24-hour OCPs and polarization resistance values of the 3 Pd-Ag alloys and the Au-Pd alloy were not significantly different (P=.233 and P=.211, respectively) for the same electrolyte, but significant differences were found for corrosion test results in different electrolytes (Palloy and electrolyte (P=.249 and P=.713, respectively). The 3 Pd-Ag silver alloys appeared to be resistant to chloride ion corrosion, and passivation and de-alloying were identified for these

Size- and coating-dependent cytotoxicity and genotoxicity of silver nanoparticles evaluated using in vitro standard assays.

Science.gov (United States)

Guo, Xiaoqing; Li, Yan; Yan, Jian; Ingle, Taylor; Jones, Margie Yvonne; Mei, Nan; Boudreau, Mary D; Cunningham, Candice K; Abbas, Mazhar; Paredes, Angel M; Zhou, Tong; Moore, Martha M; Howard, Paul C; Chen, Tao

2016-11-01

The physicochemical characteristics of silver nanoparticles (AgNPs) may greatly alter their toxicological potential. To explore the effects of size and coating on the cytotoxicity and genotoxicity of AgNPs, six different types of AgNPs, having three different sizes and two different coatings, were investigated using the Ames test, mouse lymphoma assay (MLA) and in vitro micronucleus assay. The genotoxicities of silver acetate and silver nitrate were evaluated to compare the genotoxicity of nanosilver to that of ionic silver. The Ames test produced inconclusive results for all types of the silver materials due to the high toxicity of silver to the test bacteria and the lack of entry of the nanoparticles into the cells. Treatment of L5718Y cells with AgNPs and ionic silver resulted in concentration-dependent cytotoxicity, mutagenicity in the Tk gene and the induction of micronuclei from exposure to nearly every type of the silver materials. Treatment of TK6 cells with these silver materials also resulted in concentration-dependent cytotoxicity and significantly increased micronucleus frequency. With both the MLA and micronucleus assays, the smaller the AgNPs, the greater the cytotoxicity and genotoxicity. The coatings had less effect on the relative genotoxicity of AgNPs than the particle size. Loss of heterozygosity analysis of the induced Tk mutants indicated that the types of mutations induced by AgNPs were different from those of ionic silver. These results suggest that AgNPs induce cytotoxicity and genotoxicity in a size- and coating-dependent manner. Furthermore, while the MLA and in vitro micronucleus assay (in both types of cells) are useful to quantitatively measure the genotoxic potencies of AgNPs, the Ames test cannot.

Optical properties of palladium nanoparticles under exposure of hydrogen and inert gas prepared by dewetting synthesis of thin-sputtered layers

Energy Technology Data Exchange (ETDEWEB)

Kracker, Michael, E-mail: Michael.Kracker@uni-jena.de; Worsch, Christian; Ruessel, Christian [Otto-Schott-Institut, Jena University (Germany)

2013-04-15

Thin layers of palladium with a thickness of 5 nm were sputtered on fused silica substrates. Subsequently, the coated glasses were annealed at a temperature of 900 Degree-Sign C for 1 h. This resulted in the formation of small and well-separated palladium nanoparticles with diameters in the range from 20 to 200 nm on the glass surface. The existence of a palladium oxide layer can be detected using optical absorption spectroscopy. Purging with hydrogen leads to an irreversible change in the optical spectra due to the reduction of PdO to metallic palladium. Changing the gas atmosphere from hydrogen to argon leads to significant reversible changes in the optical properties of the particle layer. Based on Mie theory and the respective dielectric functions, the spectra were calculated using the real particle size distribution, weighted dispersions relation to adapt the geometrical conditions and complex dielectric functions of palladium and palladium hydride. A good agreement with measured spectra was found and the dependency of the surrounding media can be explained.Graphical Abstract.

The effect of silver nanoparticle size on Jc of YBa2Cu3O7-x superconductor

International Nuclear Information System (INIS)

Farbod, M.; Batvandi, M.; Shoushtari, M. Z.

2007-01-01

Full text: Critical current density Jc is one of the most important superconducting parameters which is crucial in superconductor's applications. Introducing silver into the superconductors as intergrain filler has been a routine way to increase the Jc. In this work, YBa 2 Cu 3 O 7-x (YBCO), was doped by silver nanoparticles and their effect was studied on Jc as the flux pinning centers. Silver nanoparticles with sizes ranging from 30 to 1000 nm have been prepared using the reduction of silver in ethanol. The stoichiometric amounts of initial material of YBCO superconductor were added to the solution. After evaporation of ethanol, the obtained powder was used to fabricate YBCO samples. The total weight ratio of silver nanoparticles to superconductor was 1:100. The samples were characterized using SEM, EDX and XRD measurements. Jc was measured by a standard four probe technique. The results show by increasing silver nanoparticle size up to 700 nm, Jc increases then decreases by further increase in silver particle size. (authors)

Size-tunable silver nanoparticles synthesized by using aminopolycarboxylic acids at ambient-temperature

International Nuclear Information System (INIS)

Malkar, Vishwabharati V.; Chadha, R.; Biswas, N.; Mukherjee, T.; Kapoor, S.

2009-01-01

Full text: Stable aqueous sols of silver nanoparticles are prepared by using various aminopolycarboxylic acids as stabilizing agents at ambient temperature. The precursor silver perchlorate is reduced using γ radiations. Interestingly, it was observed that size of silver nanoparticles obtained could be tuned using various aminopolycarboxylic acids of varying carboxylic acid groups The silver sols synthesized by this method were stable for months and particles obtained were monodisperse in almost all cases. Particle formation was observed at equimolar concentration of silver and aminopolycarboxylic acids. The stabilization of particles even in the absence of any polymer indicates that the adsorption of aminopolycarboxylic acids on silver particle is a spontaneous process. The adsorbed aminopolycarboxylic acids can saturate the residual valence force of the silver atom on the particle surface by coordinating with unoccupied orbital. Adsorption of aminopolycarboxylic acids does not lead to any change in surface plasmon band of silver nanoparticles; this indicates that anions in the double layer on the colloidal particle have different chemical properties from the free anions. Synthesized silver nanoparticles were characterized by UV-visible spectrophotometer, X-ray Diffraction, Dynamic Light Scattering and Transmission Electron Microscope

Adhesion enhancement between electroless nickel and polyester fabric by a palladium-free process

Energy Technology Data Exchange (ETDEWEB)

Lu Yinxiang, E-mail: yxlu@fudan.edu.cn [Department of Materials Science, Fudan University, 220 Handan Road, Shanghai 200433 (China); Xue Longlong; Li Feng [Department of Materials Science, Fudan University, 220 Handan Road, Shanghai 200433 (China)

2011-01-15

A new, efficient, palladium- and etchant-free process for the electroless nickel plating of poly(ethylene terephthalate) (PET) fabric has been developed. PET electroless plating can be prepared in three steps, namely: (i) the grafting of thiol group onto PET, (ii) the silver Ag{sup 0} seeding of the PET surface, and (iii) the nickel metallization using electroless plating bath. Scanning electron microscopy (SEM), energy dispersive X-ray (EDX) analysis, X-ray photoelectron spectroscopy (XPS), Raman spectrometer, X-ray diffraction (XRD), and thermogravimetric analysis (TG) were used to characterize the samples in the process, and the nickel loading was quantified by weighing. This process successfully compares with the traditional one based on KMnO{sub 4}/H{sub 2}SO{sub 4} etching and palladium-based seed layer. The nickel coating obtained in this palladium-free process can pass through ultrasonic washing challenge, and shows excellent adhesion with the PET substrate. However, the sample with Pd catalyst via traditional process was damaged during the testing experiment.

Size-controlled in situ synthesis and photo-responsive properties of silver/poly(methyl methacrylate) nanocomposite films with high silver content

Energy Technology Data Exchange (ETDEWEB)

Chen Cheng; Li Junguo [State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070 (China); Luo Guoqiang, E-mail: qhy2013@163.com [State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070 (China); Xiong Yuanlu; Zhang Qiang; Shen Lianmeng [State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070 (China)

2012-10-01

Highlights: Black-Right-Pointing-Pointer Ag/PMMA nanocomposite films with high silver content are prepared by in situ synthesis. Black-Right-Pointing-Pointer The size of Ag nanoparticles can be controlled by reaction time. Black-Right-Pointing-Pointer The electrical properties of Ag/PMMA nanocomposites films shows enhancement compared with the pure PMMA. Black-Right-Pointing-Pointer The recycle photo-responsive properties of Ag/PMMA nanocomposite films are proposed. - Abstract: Ag/PMMA nanocomposites have attracted much attention due to its superior mechanical, optical and electrical properties. In this article, Ag/PMMA nanocomposite films with high silver content (20 wt%) have been successfully in situ synthesized. UV-vis analysis, transmission electron microscopy (TEM), current-voltage (I-V) analysis, hall effect measurement system and electrochemical workstation are used to characterize the nanocomposite films. The results reveal that silver nanoparticles (NPs) homogeneously distribute in PMMA films and the particles size of silver NPs which has been controlled from 1.68 to 6.98 nm. Ag/PMMA nanocomposite films show electrical properties due to the conduction paths created by Ag nanoparticles. With the increasing diameter of silver NPs, the current density decreases and resistivity increases, respectively. Photo-responsive properties of Ag/PMMA nanocomposite films indicate that conduction paths could be destroyed by illumination and rebuilt in dark condition.

Size-controlled in situ synthesis and photo-responsive properties of silver/poly(methyl methacrylate) nanocomposite films with high silver content

International Nuclear Information System (INIS)

Chen Cheng; Li Junguo; Luo Guoqiang; Xiong Yuanlu; Zhang Qiang; Shen Lianmeng

2012-01-01

Highlights: ► Ag/PMMA nanocomposite films with high silver content are prepared by in situ synthesis. ► The size of Ag nanoparticles can be controlled by reaction time. ► The electrical properties of Ag/PMMA nanocomposites films shows enhancement compared with the pure PMMA. ► The recycle photo-responsive properties of Ag/PMMA nanocomposite films are proposed. - Abstract: Ag/PMMA nanocomposites have attracted much attention due to its superior mechanical, optical and electrical properties. In this article, Ag/PMMA nanocomposite films with high silver content (20 wt%) have been successfully in situ synthesized. UV–vis analysis, transmission electron microscopy (TEM), current–voltage (I–V) analysis, hall effect measurement system and electrochemical workstation are used to characterize the nanocomposite films. The results reveal that silver nanoparticles (NPs) homogeneously distribute in PMMA films and the particles size of silver NPs which has been controlled from 1.68 to 6.98 nm. Ag/PMMA nanocomposite films show electrical properties due to the conduction paths created by Ag nanoparticles. With the increasing diameter of silver NPs, the current density decreases and resistivity increases, respectively. Photo-responsive properties of Ag/PMMA nanocomposite films indicate that conduction paths could be destroyed by illumination and rebuilt in dark condition.

Effect of the size of silver nanoparticles on SERS signal enhancement

Science.gov (United States)

He, Rui Xiu; Liang, Robert; Peng, Peng; Norman Zhou, Y.

2017-08-01

The localized surface plasmon resonance arising from plasmonic materials is beneficial in solution-based and thin-film sensing applications, which increase the sensitivity of the analyte being tested. Silver nanoparticles from 35 to 65 nm in diameter were synthesized using a low-temperature method and deposited in a monolayer on a (3-aminopropyl)triethoxysilane (APTES)-functionalized glass slide. The effect of particle size on monolayer structure, optical behavior, and surface-enhanced Raman scattering (SERS) is studied. While increasing particle size decreases particle coverage, it also changes the localized surface plasmon resonance and thus the SERS activity of individual nanoparticles. Using a laser excitation wavelength of 633 nm, the stronger localized surface plasmon resonance coupling to this excitation wavelength at larger particle sizes trumps the loss in surface coverage, and greater SERS signals are observed. The SERS signal enhancement accounts for the higher SERS signal, which was verified using a finite element model of a silver nanoparticle dimer with various nanoparticle sizes and separation distances.

The solubility of palladium(II) bis-dimethylglyoximate

International Nuclear Information System (INIS)

Maghzian, R.

1978-01-01

The solubility of palladium(II) bis-dimethylglyoximate in different solutions has been determined. Values obtained for the solubility of the palladium complex are tabulated. The solubility is the lowest in water, ammonium acetate and a 25% acetone-water mixture. It is highest in dilute HCl and acetone but precipitation from aqueous acetone should be satisfactory for most purposes if the acetone content of the solvent is roughly less than 50% by volume. The solubility in dilute HCl reflects the concern by previous workers for losses in precipitation from mineral acid. In general, however, the losses are unlikely to be significant unless the quantity of palladium to be precipitated and weighed is small. (T.G.)

Reversible Size Control of Silver Nanoclusters via Ligand-exchange

KAUST Repository

Bootharaju, Megalamane Siddaramappa

2015-05-21

The properties of atomically monodisperse noble metal nanoclusters (NCs) are intricately intertwined with their precise molecular formula. The vast majority of size-specific NC syntheses start from the reduction of the metal salt and thiol ligand mixture. Only in gold was it recently shown that ligand-exchange could induce the growth of NCs from one atomically precise species to another; a process of yet unknown reversibility. Here, we present a process for the ligand-exchange-induced growth of atomically precise silver NCs, in a biphasic liquid-liquid system, which is particularly of interest because of its complete reversibility and ability to occur at room temperature. We explore this phenomenon in-depth using Ag35(SG)18 [SG= glutathionate] and Ag44(4-FTP)30 [4-FTP= 4-fluorothiophenol] as model systems. We show that the ligand-exchange conversion of Ag35(SG)18 into Ag44(4-FTP)30 is rapid (< 5 min) and direct, while the reverse process proceeds slowly through intermediate cluster sizes. We adapt a recently developed theory of reverse Ostwald ripening to model the NCs’ interconvertibility. The model’s predictions are in good agreement with the experimental observations, and they highlight the importance of small changes in the ligand-metal binding energy in determining the final equilibrium NC size. Based on the insight provided by this model, we demonstrated experimentally that by varying the choice of ligands, ligand-exchange can be used to obtain different sized NCs. The findings in this work establish ligand-exchange as a versatile tool for tuning cluster sizes.

Reversible Size Control of Silver Nanoclusters via Ligand-exchange

KAUST Repository

Bootharaju, Megalamane Siddaramappa; Burlakov, Victor M.; Besong, Tabot M.D.; Joshi, Chakra Prasad; AbdulHalim, L; Black, David; Whetten, Robert; Goriely, Alain; Bakr, Osman

2015-01-01

The properties of atomically monodisperse noble metal nanoclusters (NCs) are intricately intertwined with their precise molecular formula. The vast majority of size-specific NC syntheses start from the reduction of the metal salt and thiol ligand mixture. Only in gold was it recently shown that ligand-exchange could induce the growth of NCs from one atomically precise species to another; a process of yet unknown reversibility. Here, we present a process for the ligand-exchange-induced growth of atomically precise silver NCs, in a biphasic liquid-liquid system, which is particularly of interest because of its complete reversibility and ability to occur at room temperature. We explore this phenomenon in-depth using Ag35(SG)18 [SG= glutathionate] and Ag44(4-FTP)30 [4-FTP= 4-fluorothiophenol] as model systems. We show that the ligand-exchange conversion of Ag35(SG)18 into Ag44(4-FTP)30 is rapid (< 5 min) and direct, while the reverse process proceeds slowly through intermediate cluster sizes. We adapt a recently developed theory of reverse Ostwald ripening to model the NCs’ interconvertibility. The model’s predictions are in good agreement with the experimental observations, and they highlight the importance of small changes in the ligand-metal binding energy in determining the final equilibrium NC size. Based on the insight provided by this model, we demonstrated experimentally that by varying the choice of ligands, ligand-exchange can be used to obtain different sized NCs. The findings in this work establish ligand-exchange as a versatile tool for tuning cluster sizes.

Nano structural Features of Silver Nanoparticles Powder Synthesized through Concurrent Formation of the Nano sized Particles of Both Starch and Silver

International Nuclear Information System (INIS)

Hebeish, A.; El-Rafie, M.H.; El-Sheikh, M.A.; El-Naggar, M.E.

2013-01-01

Green innovative strategy was developed to accomplish silver nanoparticles formation of starch-silver nanoparticles (St-AgNPs) in the powder form. Thus, St-AgNPs were synthesized through concurrent formation of the nano sized particles of both starch and silver. The alkali dissolved starch acts as reducing agent for silver ions and as stabilizing agent for the formed AgNPs. The chemical reduction process occurred in water bath under high-speed homogenizer. After completion of the reaction, the colloidal solution of AgNPs coated with alkali dissolved starch was cooled and precipitated using ethanol. The powder precipitate was collected by centrifugation, then washed, and dried; St-AgNPs powder was characterized using state-of-the-art facilities including UV-vis spectroscopy, Transmission Electron Microscopy (TEM), particle size analyzer (PS), Polydispersity index (PdI), Zeta potential (ZP), XRD, FT-IR, EDX, and TGA. TEM and XRD indicate that the average size of pure AgNPs does not exceed 20 nm with spherical shape and high concentration of AgNPs (30000 ppm). The results obtained from TGA indicates that the higher thermal stability of starch coated AgNPS than that of starch nanoparticles alone. In addition to the data obtained from EDX which reveals the presence of AgNPs and the data obtained from particle size analyzer and zeta potential determination indicate that the good uniformity and the highly stability of St-AgNPs).

Atomistic simulation of helium bubble nucleation in palladium

Energy Technology Data Exchange (ETDEWEB)

Wang Liang [Department of Applied Physics, Hunan University, Changsha 410082 (China); Hu, Wangyu [Department of Applied Physics, Hunan University, Changsha 410082 (China)], E-mail: wangyuhu2001cn@yahoo.com.cn; Xiao Shifang [Department of Applied Physics, Hunan University, Changsha 410082 (China)], E-mail: sfxiao@yahoo.com.cn; Yang Jianyu [Department of Maths and Physics, Hunan Institute of Engineering, Xiangtan 411104 (China); Deng Huiqiu [Department of Applied Physics, Hunan University, Changsha 410082 (China)

2009-09-15

A palladium crystal has been constructed with 11808 atoms. 55 helium atoms occupied the octahedral position of palladium crystal are introduced and retained in a spherical region. Molecular dynamic simulations are performed in a constant temperature and constant volume ensemble (NVT) with temperature controlled by Nose-Hoover thermostat. The interactions between palladium atoms are described with modified analytic embedded atom method (MAEAM), the interactions between palladium atom and helium atom are in the form of Morse potential, and the interactions between helium atoms are in the form of L-J potential function. With the analysis of the radial distribution function (RDF) and microstructure, it reveals that some of helium atoms form a series of clusters with different size, and the nucleation core is random at low temperature, and which is the embryo of helium bubble. Increasing temperature can accelerate the process of bubble nucleation, and the clusters will aggregate and coalesce into a bigger one in which there are no palladium atoms, and it is considered as a helium bubble.

Microwave-assisted synthesis of palladium nanocubes and nanobars

International Nuclear Information System (INIS)

Yu, Yanchun; Zhao, Yanxi; Huang, Tao; Liu, Hanfan

2010-01-01

Microwave was employed in the shape-controlled synthesis of palladium nanoparticles. Palladium nanocubes and nanobars with a mean size of about 23.8 nm were readily synthesized with H 2 PdCl 4 as a precursor, tetraethylene glycol (TEG) as both a solvent and a reducing agent in the presence of PVP and CTAB in 80 s under microwave irradiation. The structures of the as-prepared palladium nanoparticles were characterized by transmission electron microscopy (TEM), X-ray powder diffraction (XRD) and ultraviolet-visible (UV-vis) absorption spectroscopy. The formation of PdBr 4 2- due to the coordination replacement of the ligand Cl - ions in PdCl 4 2- ions by Br - ions in the presence of bromide was responsible for the synthesis of Pd nanocubes and nanobars. In addition, a milder reducing power, a higher viscosity and a stronger affinity of TEG were beneficial to the larger sizes of Pd nanocubes and nanobars.

Structural, electronic and magnetic properties of small bimetallic zirconium–palladium clusters: Ab initio study

International Nuclear Information System (INIS)

Bezi Javan, Masoud

2015-01-01

Highlights: • Electronic and magnetic properties of small Zr n Pd m (n + m ⩽ 5) have been investigated. • Binding energies of the Zr n clusters are significantly higher than Pd n clusters. • Binding energy of the Pd n clusters increase with substituting one or more Zr atom. • HOMO–LUMO gap of the Zr n Pd m clusters increase in comparison with pure states. - Abstract: Structural, electronic and magnetic properties of small bimetallic zirconium–palladium clusters, Zr n Pd m (n + m ⩽ 5), have been investigated using density functional theory with considering generalized gradient approximation and PBE functional. We have determined the ground state conformations of the bimetallic zirconium–palladium clusters by substitution of Zr and Pd atoms in the optimized lowest energy structures of pure zirconium and palladium clusters. Results reveal that binding energies of the pure Zr n clusters are significantly higher than Pd n clusters with the same number of atoms. Also it is found that binding energy of the Zr n and Pd n clusters increase with growth of the number of consisting atoms in the clusters. Results indicate that, for both Zr n and Pd n clusters the binding energy of planar forms is lower than three-dimensional structures. We have also found that the binding energy of the Pd n clusters increase with substituting one or more Zr atoms in these clusters. We have also studied the HOMO–LUMO energy gap and magnetic moment of the pure and combined Zr and Pd clusters. The energy gap analysis of the pure and combined Pd and Zr clusters show that in generally the HOMO–LUMO gap of the bimetallic Zr n Pd m clusters increase in comparison with their corresponding pure clusters with the same number of atoms. According to the spin polarization DFT calculations all of the Zr n Pd m (n + m ⩽ 5) have net magnetic moments as instance the Zr 2 , Pd 2 and ZrPd clusters show a total magnetic moment value of 2 μ B . Some more discussions around charge population

Silver enhancement of nanogold and undecagold

Energy Technology Data Exchange (ETDEWEB)

Hainfield, J.F.; Furuya, F.R.

1995-07-01

A recent advance in immunogold technology has been the use of molecular gold instead of colloidal gold. A number of advantages are realized by this approach, such as stable covalent, site-specific attachment, small probe size and absence of aggregates for improved penetration. Silver enhancement has led to improved and unique results for electron and light microscopy, as well as their use with blots and gels. Most previous work with immunogold silver staining has been done with colloidal gold particles. More recently, large gold compounds (``clusters``) having a definite number of gold atoms and defined organic shell, have been used, frequently with improved results. These gold dusters, large compared to simple compounds, are, however, at the small end of the colloidal gold scale in size; undecagold is 0.8 nm and Nanogold is 1.4 nm. They may be used in practically all applications where colloidal gold is used (Light and electron microscopy, dot blots, etc.) and in some unique applications, where at least the larger colloidal golds don`t work, such as running gold labeled proteins on gels (which are later detected by silver enhancement). The main differences between gold clusters and colloidal golds are the small size of the dusters and their covalent attachment to antibodies or other molecules.

Controlled synthesis of colloidal silver nanoparticles in capillary micro-flow reactor

International Nuclear Information System (INIS)

He Shengtai; Liu Yulan; Maeda, Hideaki

2008-01-01

In this study, using a polytetrafluoroethylene (PTFE) capillary tube as a micro-flow reactor, well-dispersed colloidal silver nanoparticles were controllably synthesized with different flow rates of precursory solution. Scanning transmission electron microscopy images and UV-visible absorbance spectra showed that silver nanoparticles with large size can be prepared with slow flow rate in the PTFE capillary reactor. The effects of tube diameters on the growth of colloidal silver nanoparticles were investigated. Experiment results demonstrated that using tube with small diameter was more propitious for the controllable synthesis of silver nanoparticles with different sizes.

Characterization of Electrochemically Generated Silver

Science.gov (United States)

Adam, Niklas; Martinez, James; Carrier, Chris

2014-01-01

Silver biocide offers a potential advantage over iodine, the current state of the art in US spacecraft disinfection technology, in that silver can be safely consumed by the crew. Low concentrations of silver (Silver does not require hardware to remove it from a water system, and therefore can provide a simpler means for disinfecting water. The Russian segment of the International Space Station has utilized an electrochemically generated silver solution, which is colloidal in nature. To be able to reliably provide a silver biocide to drinking water by electrochemical means would reduce mass required for removing another biocide such as iodine from the water. This would also aid in crew time required to replace iodine removal cartridges. Future long term missions would benefit from electrochemically produced silver as the biocide could be produced on demand and requires only a small concentration to be effective. Since it can also be consumed safely, there is less mass in removal hardware and little consumables required for production. The goal of this project initially is to understand the nature of the electrochemically produced silver, the particle sizes produced by the electrochemical cell and the effect that voltage adjustment has on the particle size. In literature, it has been documented that dissolved oxygen and pH have an effect on the ionization of the electrochemical silver so those parameters would be measured and possibly adjusted to understand their effect on the silver.

Thickness- and Particle-Size-Dependent Electrochemical Reduction of Carbon Dioxide on Thin-Layer Porous Silver Electrodes.

Science.gov (United States)

Zhang, Lin; Wang, Zhiyong; Mehio, Nada; Jin, Xianbo; Dai, Sheng

2016-03-08

The electrochemical reduction of CO2 can not only convert it back into fuels, but is also an efficient manner to store forms of renewable energy. Catalysis with silver is a possible technology for CO2 reduction. We report that in the case of monolithic porous silver, the film thickness and primary particle size of the silver particles, which can be controlled by electrochemical growth/reduction of AgCl film on silver substrate, have a strong influence on the electrocatalytic activity towards CO2 reduction. A 6 μm thick silver film with particle sizes of 30-50 nm delivers a CO formation current of 10.5 mA cm(-2) and a mass activity of 4.38 A gAg (-1) at an overpotential of 0.39 V, comparable to levels achieved with state-of-the-art gold catalysts. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Estimation of silver nanoparticles size in SiO2 sol-gel layers by use of UV-VIS spectroscopy

Directory of Open Access Journals (Sweden)

Marek Novotný

2011-12-01

Full Text Available Silica glass layers containing silver nanoparticles were prepared by the sol-gel method. The layers were deposited on a glass substrate by the dip-coating method, dried and heat treated at various temperatures. The average silver particle size was determined from absorption spectra according to Mie’s theory. A good correlation was found between the calculated values and analysis of HRTEM images. A very narrow size distribution was obtained by this procedure. The average particle size of silver particles fell between 1 and 2 nm for dried samples; in case of glasses treated at 500 and 550°C the size ranged between 2 and 4 nm.

A DFT study of arsine adsorption on palladium doped graphene: Effects of palladium cluster size

International Nuclear Information System (INIS)

Kunaseth, Manaschai; Mudchimo, Tanabat; Namuangruk, Supawadee; Kungwan, Nawee; Promarak, Vinich; Jungsuttiwong, Siriporn

2016-01-01

Graphical abstract: The relationship between charge difference and adsorption strength demonstrates that charge migration from Pd_n-SDG to AsH_x significantly enhanced adsorption strength, the Pd_6 clusters doped SDG with a steep slope is recommended as a superior adsorbent material for AsH_3 removal from gas stream. - Highlights: • Pd atom and Pd clusters bind strongly onto the defective graphene surface. • Larger size of Pd cluster adsorbs arsine and its hydrogenated products stronger. • Order of adsorption strength on Pd_n doped graphene: As > AsH > AsH_2 > > AsH_3. • Charge migration characterizes the strong adsorption of AsH_2, AsH, and As. • Pd cluster doped graphene is thermodynamically preferable for arsine removal. - Abstract: In this study, we have investigated the size effects of palladium (Pd) doped single-vacancy defective graphene (SDG) surface to the adsorption of AsH_3 and its dehydrogenated products on Pd using density functional theory calculations. Here, Pd cluster binding study revealed that Pd_6 nanocluster bound strongest to the SDG surface, while adsorption of AsH_x (x = 0–3) on the most stable Pd_n doped SDG showed that dehydrogenated arsine compounds adsorbed onto the surface stronger than the pristine AsH_3 molecule. Charge analysis revealed that considerable amount of charge migration from Pd to dehydrogenated arsine molecules after adsorption may constitute strong adsorption for dehydrogenated arsine. In addition, study of thermodynamic pathways of AsH_3 dehydrogenation on Pd_n doped SDG adsorbents indicated that Pd cluster doping on SDG adsorbent tends to be thermodynamically favorable for AsH_3 decomposition than the single-Pd atom doped SDG. Hence, our study has indicated that Pd_6 clusters doped SDG is more advantageous as adsorbent material for AsH_3 removal.

Polymer producing palladium complexes of unidentate phosphines in the methoxycarbonylation of ethene.

Science.gov (United States)

Smith, Graeme; Vautravers, Nicolas R; Cole-Hamilton, David J

2009-02-07

A wide range of unidentate phosphines have been studied as ligands for the palladium-catalysed methoxycarbonylation of ethene in the presence of methanesulfonic acid using methanol as the solvent. At high phosphine to Pd ratios, methyl propanoate is formed at a low rate. However, at P-Pd ratios of 4 : 1, some unidentate phosphines promote the formation of polyketone with moderate rates. Analysis of all the phosphines shows that good electron donating power, combined with small size, favours polyketone formation.

Determination of palladium content in palladium-alumina/palladium-silica/palladium-tin oxide catalyst for nuclear reactor applications

International Nuclear Information System (INIS)

Sharma, P.K.; Bassan, M.K.T.; Avhad, D.K.; Singhal, R.K.

2012-01-01

Alumina and silica act as support for finely divided palladium metal powder in synthesis of catalyst. These catalyst (Pd-Al 2 O 3 , Pd-SiO 2 and Pd-SnO 2 ) used in nuclear power reactor (moderator cover gas system) for the conversion of hydrogen. In Indian nuclear power programme these catalyst are regularly used in Kaiga 1 and 2 and Rajasthan atomic power plant 3 and 4. The performance of the catalyst, solely depends on the concentration of palladium, which is the active component in this catalyst composition. Therefore it is highly desirable to have rouged analytical methodology for the accurate estimation of palladium. Leaching of Pd from the bulk matrix is tedious due to the less reactive nature of Pd therefore complete solubilization of the matrix is carried out by fusion method

Surface-Enhanced Raman Spectroscopy of Dye and Thiol Molecules Adsorbed on Triangular Silver Nano structures: A Study of Near-Field Enhancement, Localization of Hot-Spots, and Passivation of Adsorbed Carbonaceous Species

International Nuclear Information System (INIS)

Goncalves, M.R.; Marti, O.; Fabian Enderle, F.

2012-01-01

Surface-enhanced Raman spectroscopy (SERS) of thiols and dye molecules adsorbed on triangular silver nanostructures was investigated. The SERS hot-spots are localized at the edges and corners of the silver triangular particles. AFM and SEM measurements permit to observe many small clusters formed at the edges of triangular particles fabricated by nanosphere lithography. Finite-element calculations show that near-field enhancements can reach values of more than 200 at visible wavelengths, in the gaps between small spherical particles and large triangular particles, although for the later no plasmon resonance was found at the wavelengths investigated. The regions near the particles showing strong near-field enhancement are well correlated with spatial localization of SERS hot-spots done by confocal microscopy. Silver nanostructures fabricated by thermal evaporation present strong and fast fluctuating SERS activity, due to amorphous carbon contamination. Thiols and dye molecules seem to be able to passivate the undesired SERS activity on fresh evaporated silver. excitation: by far-field illumination of metal nanostructures or rough metal Raman scattering cross-section of gold-palladium target Temporal Fluctuation in SERS Temporal and spectral fluctuations.

Effect of laser energy on the SPR and size of silver nanoparticles synthesized by pulsed laser ablation in distilled water

Science.gov (United States)

Baruah, Prahlad K.; Sharma, Ashwini K.; Khare, Alika

2018-04-01

The effect of incident laser energy on the surface plasmon resonance (SPR) and size of silver nanoparticles synthesized via pulsed laser ablation of silver immersed in distilled water is reported in this paper. The broadening in the plasmonic bandwidth of the synthesized nanoparticles with the increase in the laser energy incident onto the silver target indicates the reduction in size of the nanoparticles. This is confirmed by the transmission electron microscope (TEM) images which show a decrease in the average particle size of the nanoparticles from approximately 15 to 10 nm with the increase in incident laser energy from 30 to 70 mJ, respectively. The structural features as revealed by the selected area electron diffraction and ultra-high resolution TEM studies confirmed the formation of both silver as well as silver oxide nanoparticles.

Synthesis and characterization of silver nanoparticles: effect on phytopathogen Colletotrichum gloesporioides

Energy Technology Data Exchange (ETDEWEB)

Aguilar-Mendez, Miguel A., E-mail: maguilarme@ipn.mx; San Martin-Martinez, Eduardo; Ortega-Arroyo, Lesli [Instituto Politecnico Nacional, Centro de Investigacion en Ciencia Aplicada y Tecnologia Avanzada (Mexico); Cobian-Portillo, Georgina [Instituto Politecnico Nacional, Centro Interdisciplinario de Investigacion para el Desarrollo Integral Regional (Mexico); Sanchez-Espindola, Esther [Instituto Politecnico Nacional, Escuela Nacional de Ciencias Biologicas, Prolongacion Manuel M. Carpio s/n, esq. Plan de Ayala (Mexico)

2011-06-15

Colloidal silver nanoparticles were synthesized by reducing silver nitrate solutions with glucose, in the presence of gelatin as capping agent. The obtained nanoparticles were characterized by means of UV-Vis spectroscopy, transmission electron microscopy (TEM), and Fourier transform infrared (FTIR) spectroscopy. The response surface methodology (RSM) was also used to determine the influence of the variables on the size of the nanoparticles. The antifungal activity of the silver nanoparticles was evaluated on the phytopathogen Colletotrichum gloesporioides, which causes anthracnose in a wide range of fruits. The UV-Vis spectra indicated the formation of silver nanoparticles preferably spherical and of relatively small size (<20 nm). The above-mentioned was confirmed by TEM, observing a size distribution of 5-24 nm. According to RSM the synthesis variables influenced on the size of the silver nanoparticles. By means of FTIR spectroscopy it was determined that gelatin, through their amide and hydroxyl groups, interacts with nanoparticles preventing their agglomeration. The growth of C. gloesporioides in the presence of silver nanoparticles was significantly delayed in a dose dependent manner.

Synthesis and characterization of silver nanoparticles: effect on phytopathogen Colletotrichum gloesporioides

International Nuclear Information System (INIS)

Aguilar-Méndez, Miguel A.; San Martín-Martínez, Eduardo; Ortega-Arroyo, Lesli; Cobián-Portillo, Georgina; Sánchez-Espíndola, Esther

2011-01-01

Colloidal silver nanoparticles were synthesized by reducing silver nitrate solutions with glucose, in the presence of gelatin as capping agent. The obtained nanoparticles were characterized by means of UV–Vis spectroscopy, transmission electron microscopy (TEM), and Fourier transform infrared (FTIR) spectroscopy. The response surface methodology (RSM) was also used to determine the influence of the variables on the size of the nanoparticles. The antifungal activity of the silver nanoparticles was evaluated on the phytopathogen Colletotrichum gloesporioides, which causes anthracnose in a wide range of fruits. The UV–Vis spectra indicated the formation of silver nanoparticles preferably spherical and of relatively small size (<20 nm). The above-mentioned was confirmed by TEM, observing a size distribution of 5–24 nm. According to RSM the synthesis variables influenced on the size of the silver nanoparticles. By means of FTIR spectroscopy it was determined that gelatin, through their amide and hydroxyl groups, interacts with nanoparticles preventing their agglomeration. The growth of C. gloesporioides in the presence of silver nanoparticles was significantly delayed in a dose dependent manner.

Impurities determination in precious metals like rhodium, palladium and platinum by neutron activation without separation

International Nuclear Information System (INIS)

May, S.; Piccot, D.; Pinte, G.

1978-01-01

The possibilities of the method explored using an installation of gamma or X ray spectrometry of good performance. The irradiations were realized in the reactors EL.3 (flux approximately 6.10 12 n.cm -2 .s -1 ) and Osiris (flux > 10 14 n.cm -2 .s -1 ) of the CEN Saclay. In rhodium the presence of iridium limits the analysis possibilities. However gold, silver and platinum are easily determined, just as the other elements (As, Br, Cl, Co, Mn, Na, Sb). In platinum it is possible to determine the elements of long period, especially antimony, silver, cobalt, iridium, tantalum and zinc. As for palladium the principal impurities are gold, silver and ruthenium for what is of precious metals and particularly zinc among the other metals. For the three matrices considered the detection limits of a certain number of elements are indicated [fr

Low-cost method for fabricating palladium and palladium-alloy thin films on porous supports

Science.gov (United States)

Lee, Tae H; Park, Chan Young; Lu, Yunxiang; Dorris, Stephen E; Balachandran, Uthamalingham

2013-11-19

A process for forming a palladium or palladium alloy membrane on a ceramic surface by forming a pre-colloid mixture comprising a powder palladium source, carrier fluid, dispersant and a pore former and a binder. Ultrasonically agitating the precolloid mixture and applying to a substrate with an ultrasonic nozzle and heat curing the coating form a palladium-based membrane.

Green synthesis of monodisperse silver nanoparticles using hydroxy propyl methyl cellulose

Energy Technology Data Exchange (ETDEWEB)

Dong, Chunfa; Zhang, Xianglin, E-mail: hust_zxl@mail.hust.edu.cn; Cai, Hao

2014-01-15

Graphical abstract: -- Highlights: • Synthesis of silver nanoparticles using hydroxy propyl methyl cellulose is reported. • HPMC and glucose are used as capping agent and reducing agent respectively. • It is the first time to use HPMC for synthesis of silver nanoparticles. • The small, spherical and well-dispersed particle is observed in the range of 3–17 nm. • The green method can be extended to other noble metals. -- Abstract: A simple and environmentally friendly method for the synthesis of highly stable and small sized silver nanoparticles with narrow distribution from 3 nm to 17 nm is reported. Silver nitrate, hydroxy propyl methyl cellulose (HPMC) and glucose, were used as silver precursor, capping agents and reducing agents respectively. The formation of silver nanoparticles was observed by change of color from colorless to wine red. The silver nanoparticles were characterized by transmission electron microscopy (TEM), UV–visible spectroscopy (UV–vis), X-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FT-IR). The results demonstrated that the obtained metallic nanoparticles were single crystalline silver nanoparticles capped with HPMC. The effects of the reaction time, reaction temperature and the concentration of silver ion and reducing agents on the particle size were investigated. A possible formation mechanism was proposed. The method may be extended to other noble metal for other technological applications such as additional medicinal, industrial applications.

Green synthesis of monodisperse silver nanoparticles using hydroxy propyl methyl cellulose

International Nuclear Information System (INIS)

Dong, Chunfa; Zhang, Xianglin; Cai, Hao

2014-01-01

Graphical abstract: -- Highlights: • Synthesis of silver nanoparticles using hydroxy propyl methyl cellulose is reported. • HPMC and glucose are used as capping agent and reducing agent respectively. • It is the first time to use HPMC for synthesis of silver nanoparticles. • The small, spherical and well-dispersed particle is observed in the range of 3–17 nm. • The green method can be extended to other noble metals. -- Abstract: A simple and environmentally friendly method for the synthesis of highly stable and small sized silver nanoparticles with narrow distribution from 3 nm to 17 nm is reported. Silver nitrate, hydroxy propyl methyl cellulose (HPMC) and glucose, were used as silver precursor, capping agents and reducing agents respectively. The formation of silver nanoparticles was observed by change of color from colorless to wine red. The silver nanoparticles were characterized by transmission electron microscopy (TEM), UV–visible spectroscopy (UV–vis), X-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FT-IR). The results demonstrated that the obtained metallic nanoparticles were single crystalline silver nanoparticles capped with HPMC. The effects of the reaction time, reaction temperature and the concentration of silver ion and reducing agents on the particle size were investigated. A possible formation mechanism was proposed. The method may be extended to other noble metal for other technological applications such as additional medicinal, industrial applications

The size control of silver nanocrystals with different polyols and its application to low-reflection coating materials

Energy Technology Data Exchange (ETDEWEB)

Park, Keum Hwan; Park, O Ok [Department of Chemical and Biomolecular Engineering, Korea Advanced Institute of Science and Technology (KAIST), 291 Daehak-ro, Yuseong-gu, Daejeon 305-701 (Korea, Republic of); Im, Sang Hyuk, E-mail: imromy@krict.re.kr, E-mail: ookpark@kaist.ac.kr [Korea Research Institute of Chemical Technology (KRICT), 19 Singsungno, Yuseong-gu, Daejeon 305-600 (Korea, Republic of)

2011-01-28

The size of silver nanocrystals in polyol synthesis can be simply controlled by tuning the viscosity of the reaction medium such as ethylene glycol, 1,2-propanediol, 1,4-butanediol and 1,5-pentanediol. We found that a higher viscose medium (1,5-pentanediol) led to monodispersed smaller particles thanks to the slow addition of silver atoms into the nuclei. Size-controlled silver nanocrystals of 30 nm were obtained in a viscosity controlled medium of 1,5-pentanediol to synthesize a low refractive index filler by coating with silica and subsequent etching of the silver core. The coated low-reflection layer from the hollow silica nanoparticles on polyethylene terephthalate (PET) film can greatly reduce the reflection of the PET film from 10% to 2% over the entire visible region.

Facile fabrication of silver nanoparticles with temperature-responsive sizes as highly active SERS substrates

Science.gov (United States)

Wu, Jing; Fang, Jinghuai; Cheng, Mingfei; Gong, Xiao

2016-12-01

In our work, large-scale silver NPs (nanoparticles) are successfully synthesized on zinc foils with controllable size by regulating the temperature of the displacement reaction. Our results show that when the temperature is 70 °C, the average size of silver NPs is approximately 88 nm in diameter, and they exhibit the strongest SERS activity. The gap between nanoparticles is simultaneously regulated as near as possible, which produces abundant "hot spots" and nanogaps. Crystal violet (CV) was used as probe molecules, and the SERS signals show that the values of relative standard deviation in the intensity of the main vibration modes are less than 10%, demonstrating excellent reproducibility of the silver NPs. Furthermore, the high surface-average enhancement factor of 3.86 × 107 is achieved even when the concentration of CV is 10-7 M, which is sufficient for single-molecule detection. We believe that this low cost and rapid route would get wide applications in chemical synthesis.

Sol-gel synthesized of nanocomposite palladium-alumina ceramic membrane for H{sub 2} permeability: Preparation and characterization

Energy Technology Data Exchange (ETDEWEB)

Ahmad, A.L.; Mustafa, N.N.N. [School of Chemical Engineering, Engineering Campus, Universiti Sains Malaysia, Seri Ampangan, 14300 Nibong Tebal, Penang (Malaysia)

2007-08-15

Palladium-alumina membrane with mesopore and narrow pore size distribution was prepared by the sol-gel method. Effect of the finely dispersed metal on the microstructure and the characteristic properties of the palladium-alumina membrane were investigated. Observations were made on membrane weight loss, morphology, pore structure, pore size, surface area, pore surface fractal and membrane's crystal structure. Autosorb analysis, X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and Fourier Transform Infrared (FTIR) analysis were employed in the membrane characterization. Autosorb analysis found that, BET surface area decreased and pore size of the membrane increased with the increasing of calcinations temperature (500-1100{sup o}C) and with the increasing of palladium amount in the membrane. FTIR and TG/DTA analysis show that the suitable temperature for calcinations of palladium-alumina membrane is at 700{sup o}C. Palladium metals are highly dispersed at calcinations temperature of 700{sup o}C as observed by TEM analysis. The fine crystallinity of the palladium and {gamma}-alumina phase was obtained after calcined at 700{sup o}C. The SEM morphology shows a smooth and free crack layer of palladium-alumina membrane after repeating the process of dipping, drying and calcinations at temperature of 700{sup o}C. The membrane also successfully coated with a good adhesion on support. The thickness of the final membrane layer was estimated as 9{mu} m. (author)

A DFT study of arsine adsorption on palladium doped graphene: Effects of palladium cluster size

Energy Technology Data Exchange (ETDEWEB)

Kunaseth, Manaschai, E-mail: manaschai@nanotec.or.th [National Nanotechnology Center (NANOTEC), National Science and Technology Development Agency (NSTDA) , Pathum Thani 12120 (Thailand); Mudchimo, Tanabat [Department of Chemistry and Center of Excellence for Innovation in Chemistry, Faculty of Science, Ubon Ratchathani University, Ubon Ratchathani 34190 (Thailand); Namuangruk, Supawadee [National Nanotechnology Center (NANOTEC), National Science and Technology Development Agency (NSTDA) , Pathum Thani 12120 (Thailand); Kungwan, Nawee [Department of Chemistry, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Promarak, Vinich [Department of Material Science and Engineering, School of Molecular Science and Engineering, Vidyasirimedhi Institute of Science and Technology, Rayong 21201 (Thailand); Jungsuttiwong, Siriporn, E-mail: siriporn.j@ubu.ac.th [Department of Chemistry and Center of Excellence for Innovation in Chemistry, Faculty of Science, Ubon Ratchathani University, Ubon Ratchathani 34190 (Thailand)

2016-03-30

Graphical abstract: The relationship between charge difference and adsorption strength demonstrates that charge migration from Pd{sub n}-SDG to AsH{sub x} significantly enhanced adsorption strength, the Pd{sub 6} clusters doped SDG with a steep slope is recommended as a superior adsorbent material for AsH{sub 3} removal from gas stream. - Highlights: • Pd atom and Pd clusters bind strongly onto the defective graphene surface. • Larger size of Pd cluster adsorbs arsine and its hydrogenated products stronger. • Order of adsorption strength on Pd{sub n} doped graphene: As > AsH > AsH{sub 2} > > AsH{sub 3}. • Charge migration characterizes the strong adsorption of AsH{sub 2}, AsH, and As. • Pd cluster doped graphene is thermodynamically preferable for arsine removal. - Abstract: In this study, we have investigated the size effects of palladium (Pd) doped single-vacancy defective graphene (SDG) surface to the adsorption of AsH{sub 3} and its dehydrogenated products on Pd using density functional theory calculations. Here, Pd cluster binding study revealed that Pd{sub 6} nanocluster bound strongest to the SDG surface, while adsorption of AsH{sub x} (x = 0–3) on the most stable Pd{sub n} doped SDG showed that dehydrogenated arsine compounds adsorbed onto the surface stronger than the pristine AsH{sub 3} molecule. Charge analysis revealed that considerable amount of charge migration from Pd to dehydrogenated arsine molecules after adsorption may constitute strong adsorption for dehydrogenated arsine. In addition, study of thermodynamic pathways of AsH{sub 3} dehydrogenation on Pd{sub n} doped SDG adsorbents indicated that Pd cluster doping on SDG adsorbent tends to be thermodynamically favorable for AsH{sub 3} decomposition than the single-Pd atom doped SDG. Hence, our study has indicated that Pd{sub 6} clusters doped SDG is more advantageous as adsorbent material for AsH{sub 3} removal.

Changes in silver nanoparticles exposed to human synthetic stomach fluid: Effects of particle size and surface chemistry

International Nuclear Information System (INIS)

Mwilu, Samuel K.; El Badawy, Amro M.; Bradham, Karen; Nelson, Clay; Thomas, David; Scheckel, Kirk G.; Tolaymat, Thabet; Ma, Longzhou; Rogers, Kim R.

2013-01-01

The significant rise in consumer products and applications utilizing the antibacterial properties of silver nanoparticles (AgNPs) has increased the possibility of human exposure. The mobility and bioavailability of AgNPs through the ingestion pathway will depend, in part, on properties such as particle size and the surface chemistries that will influence their physical and chemical reactivities during transit through the gastrointestinal tract. This study investigates the interactions between synthetic stomach fluid and AgNPs of different sizes and with different capping agents. Changes in morphology, size and chemical composition were determined during a 30 min exposure to synthetic human stomach fluid (SSF) using Absorbance Spectroscopy, High Resolution Transmission Electron and Scanning Electron Microscopy (TEM/SEM), Dynamic Light Scattering (DLS), and Nanoparticle Tracking Analysis (NTA). AgNPs exposed to SSF were found to aggregate significantly and also released ionic silver which physically associated with the particle aggregates as silver chloride. Generally, the smaller sized AgNPs (< 10 nm) showed higher rates of aggregation and physical transformation than larger particles (75 nm). Polyvinylpyrrolidone (pvp)-stabilized AgNPs prepared in house behaved differently in SSF than particles obtained from a commercial source despite having similar surface coating and size distribution characteristics. - Highlights: ► Interactions between synthetic stomach fluid (SSF) and silver nanoparticles (AgNPs) are described. ► AgNPs exposed to SSF aggregate and silver chloride are associated with the particle aggregates. ► Smaller AgNPs (< 10 nm) showed higher rates of aggregation and transformation than larger particles (75 nm). ► Polyvinylpyrrolidone-stabilized AgNPs obtained from different sources aggregated at different rates when exposed to SSF

Influence of dose on particle size of colloidal silver nanoparticles synthesized by gamma radiation

International Nuclear Information System (INIS)

Naghavi, Kazem; Saion, Elias; Rezaee, Khadijeh; Yunus, Wan Mahmood Mat

2010-01-01

Colloidal silver nanoparticles were synthesized by γ-irradiation-induced reduction method of an aqueous solution containing silver nitrate as a precursor in various concentrations between 7.40x10 -4 and 1.84x10 -3 M, polyvinyl pyrrolidone for capping colloidal nanoparticles, isopropanol as radical scavenger of hydroxyl radicals and deionised water as a solvent. The irradiations were carried out in a 60 Co γ source chamber at doses up to 70 kGy. The optical absorption spectra were measured using UV-vis spectrophotometer and used to study the particle distribution and electronic structure of silver nanoparticles. As the radiation dose increases from 10 to 70 kGy, the absorption intensity increases with increasing dose. The absorption peak λ max blue shifted from 410 to 403 nm correspond to the increase of absorption conduction electron energy from 3.02 to 3.08 eV, indicating the particle size decreases with increasing dose. The particle size was determined by photon cross correlation spectroscopy and the results showed that the particle diameter decreases exponentially with the increase of dose. The transmission electron microscopy images were taken at doses of 20 and 60 kGy and the results confirmed that as the dose increases the diameter of colloidal silver nanoparticle decreases and the particle distribution increases.

Silver, gold, and alloyed silver-gold nanoparticles: characterization and comparative cell-biologic action

Science.gov (United States)

Mahl, Dirk; Diendorf, Jörg; Ristig, Simon; Greulich, Christina; Li, Zi-An; Farle, Michael; Köller, Manfred; Epple, Matthias

2012-10-01

Silver, gold, and silver-gold-alloy nanoparticles were prepared by citrate reduction modified by the addition of tannin during the synthesis, leading to a reduction in particle size by a factor of three. Nanoparticles can be prepared by this easy water-based synthesis and subsequently functionalized by the addition of either tris(3-sulfonatophenyl)phosphine or poly( N-vinylpyrrolidone). The resulting nanoparticles of silver (diameter 15-25 nm), gold (5-6 nm), and silver-gold (50:50; 10-12 nm) were easily dispersable in water and also in cell culture media (RPMI + 10 % fetal calf serum), as shown by nanoparticle tracking analysis and differential centrifugal sedimentation. High-resolution transmission electron microscopy showed a polycrystalline nature of all nanoparticles. EDX on single silver-gold nanoparticles indicated that the concentration of gold is higher inside a nanoparticle. The biologic action of the nanoparticles toward human mesenchymal stem cells (hMSC) was different: Silver nanoparticles showed a significant concentration-dependent influence on the viability of hMSC. Gold nanoparticles showed only a small effect on the viability of hMSC after 7 days. Surprisingly, silver-gold nanoparticles had no significant influence on the viability of hMSC despite the silver content. Silver nanoparticles and silver-gold nanoparticles in the concentration range of 5-20 μg mL-1 induced the activation of hMSC as indicated by the release of IL-8. In contrast, gold nanoparticles led to a reduction of the release of IL-6 and IL-8.

Synthesis and characterization of silver nanoparticles: effect on phytopathogen Colletotrichum gloesporioides

Science.gov (United States)

Aguilar-Méndez, Miguel A.; San Martín-Martínez, Eduardo; Ortega-Arroyo, Lesli; Cobián-Portillo, Georgina; Sánchez-Espíndola, Esther

2011-06-01

Colloidal silver nanoparticles were synthesized by reducing silver nitrate solutions with glucose, in the presence of gelatin as capping agent. The obtained nanoparticles were characterized by means of UV-Vis spectroscopy, transmission electron microscopy (TEM), and Fourier transform infrared (FTIR) spectroscopy. The response surface methodology (RSM) was also used to determine the influence of the variables on the size of the nanoparticles. The antifungal activity of the silver nanoparticles was evaluated on the phytopathogen Colletotrichum gloesporioides, which causes anthracnose in a wide range of fruits. The UV-Vis spectra indicated the formation of silver nanoparticles preferably spherical and of relatively small size (silver nanoparticles. By means of FTIR spectroscopy it was determined that gelatin, through their amide and hydroxyl groups, interacts with nanoparticles preventing their agglomeration. The growth of C. gloesporioides in the presence of silver nanoparticles was significantly delayed in a dose dependent manner.

Laccases as palladium oxidases.

Science.gov (United States)

Mekmouche, Yasmina; Schneider, Ludovic; Rousselot-Pailley, Pierre; Faure, Bruno; Simaan, A Jalila; Bochot, Constance; Réglier, Marius; Tron, Thierry

2015-02-01

The first example of a coupled catalytic system involving an enzyme and a palladium(ii) catalyst competent for the aerobic oxidation of alcohol in mild conditions is described. In the absence of dioxygen, the fungal laccase LAC3 is reduced by a palladium(0) species as evidenced by the UV/VIS and ESR spectra of the enzyme. During the oxidation of veratryl alcohol performed in water, at room temperature and atmospheric pressure, LAC3 regenerates the palladium catalyst, is reduced and catalyzes the four-electron reduction of dioxygen into water with no loss of enzyme activity. The association of a laccase with a water-soluble palladium complex results in a 7-fold increase in the catalytic efficiency of the complex. This is the first step in the design of a family of renewable palladium catalysts for aerobic oxidation.

Nanostructured silver sulfide: synthesis of various forms and their application

Science.gov (United States)

Sadovnikov, S. I.; Rempel, A. A.; Gusev, A. I.

2018-04-01

The results of experimental studies on nanostructured silver sulfide are analyzed and generalized. The influence of small particle size on nonstoichiometry of silver sulfide is discussed. Methods for the synthesis of various forms of nanostructured Ag2S including nanopowders, stable colloidal solutions, quantum dots, core–shell nanoparticles and heteronanostructures are described. The advantages and drawbacks of different synthetic procedures are analyzed. Main fields of application of nanostructured silver sulfide are considered. The bibliography includes 184 references.

Detection of colloidal silver chloride near solubility limit

Science.gov (United States)

Putri, K. Y.; Adawiah, R.

2018-03-01

Detection of nanoparticles in solution has been made possible by several means; one of them is laser-induced breakdown detection (LIBD). LIBD is able to distinguish colloids of various sizes and concentrations. This technique has been used in several solubility studies. In this study, the formation of colloids in a mixed system of silver nitrate and sodium chloride was observed by acoustic LIBD. Silver chloride has low solubility limit, therefore LIBD measurement is appropriate. Silver and chloride solutions with equal concentrations, set at below and above the solubility of silver chloride as the expected solid product, were mixed and the resulting colloids were observed. The result of LIBD measurement showed that larger particles were present as more silver and chloride introduced. However, once the concentrations exceeded the solubility limit of silver chloride, the detected particle size seemed to be decreasing, hence suggested the occurrence of coprecipitation process. This phenomenon indicated that the ability of LIBD to detect even small changes in colloid amounts might be a useful tool in study on formation and stability of colloids, i.e. to confirm whether nanoparticles synthesis has been successfully performed and whether the system is stable or not.

Morphology of one-time coated palladium-alumina composite membrane prepared by sol-gel process and electroless plating technique

Science.gov (United States)

Sari, R.; Dewi, R.; Pardi; Hakim, L.; Diana, S.

2018-03-01

Palladium coated porous alumina ceramic membrane tube was obtained using a combination of sol-gel process and electroless plating technique. The thickness, structure and composition of palladium-alumina composite membrane were analyzed by transmission electron microscopy (TEM), scanning electron microscopy (SEM), energy-dispersive X-ray (EDX), and atomic force microscopy (AFM). Palladium particle size was 6.18 to 7.64 nm. Palladium membrane with thickness of approximately 301.5 to 815.1 nm was formed at the outer surface of the alumina layer. EDX data confirmed the formation of palladium-alumina membrane containing 45% of palladium. From this research it shows the combination of sol-gel process and electroless plating technique with one-time coating can produce a homogeneous and smoother palladium nano layer film on alumina substrate.

Influence of dose on particle size of colloidal silver nanoparticles synthesized by gamma radiation

Energy Technology Data Exchange (ETDEWEB)

Naghavi, Kazem, E-mail: Kazem.naghavi@gmail.co [Universiti Putra Malaysia, Physics Department, 43400 UPM SERDANG, Selangor (Malaysia); Saion, Elias [Universiti Putra Malaysia, Physics Department, 43400 UPM SERDANG, Selangor (Malaysia); Rezaee, Khadijeh [Department of Nuclear Engineering, Faculty of Modern Sciences and Technologies, University of Isfahan, Isfahan 81746-73441 (Iran, Islamic Republic of); Yunus, Wan Mahmood Mat [Universiti Putra Malaysia, Physics Department, 43400 UPM SERDANG, Selangor (Malaysia)

2010-12-15

Colloidal silver nanoparticles were synthesized by {gamma}-irradiation-induced reduction method of an aqueous solution containing silver nitrate as a precursor in various concentrations between 7.40x10{sup -4} and 1.84x10{sup -3} M, polyvinyl pyrrolidone for capping colloidal nanoparticles, isopropanol as radical scavenger of hydroxyl radicals and deionised water as a solvent. The irradiations were carried out in a {sup 60}Co {gamma} source chamber at doses up to 70 kGy. The optical absorption spectra were measured using UV-vis spectrophotometer and used to study the particle distribution and electronic structure of silver nanoparticles. As the radiation dose increases from 10 to 70 kGy, the absorption intensity increases with increasing dose. The absorption peak {lambda}{sub max} blue shifted from 410 to 403 nm correspond to the increase of absorption conduction electron energy from 3.02 to 3.08 eV, indicating the particle size decreases with increasing dose. The particle size was determined by photon cross correlation spectroscopy and the results showed that the particle diameter decreases exponentially with the increase of dose. The transmission electron microscopy images were taken at doses of 20 and 60 kGy and the results confirmed that as the dose increases the diameter of colloidal silver nanoparticle decreases and the particle distribution increases.

Electrical properties of polyimides containing a near-surface deposit of silver

Science.gov (United States)

Rancourt, J. D.; Porta, G. M.; Taylor, L. T.

1987-01-01

Films containing a surface or near-surface deposit of palladium, gold or copper metal as well as tin, cobalt, copper, or lithium oxides have been prepared by dissolving appropriate metal salts into poly(amide-acid)/N,N-dimethylacetamide solutions and curing the solvent cast films to temperatures up to 300 C. This preparation technique has been extended to evaluate the thermal, spectroscopic, and electrical characteristics of condensation polyimide films modified with silver nitrate. A near-surface deposit of metallic silver results but the reflective surface has high electrical resistivity (sheet resistivity) due to a polymer coating or overlayer above the metal. Details pertaining to the silver nitrate modified condensation polyimides are presented. Also, the applicability of the structural model and electrical model previously proposed for the cobalt oxide system are assessed.

Polarographic determination of selenium and tellurium in silver-gold alloys

International Nuclear Information System (INIS)

Gornostaeva, T.D.; Shmargun, S.V.

1986-01-01

The determination of selenium and tellurium is of importance in monitoring the composition of silver-gold alloys (SGA) since these elements are harmful impurities in the pure metals. Tellurium is determined in silver alloys by atomic absorption and atomic emmission methods; selenium determination is made by atomic absorption methods. This paper examines the polarographic determination of silver and tellurium in SGA containing platinum metals and copper. Copper and the bulk of the platinum and palladium were removed by precipitating selenium and tellurium with potassium hypophosphite in the elementary state from 6 M HC1. The results of an analysis of samples of SGA according to the proposed method were compared with the results obtained by the atomic absorption method. the relative deviation in the determination of 0.02-1.0% by weight selenium and tellurium does not exceed 0.12 (n = 5)

Silver, gold, and alloyed silver-gold nanoparticles: characterization and comparative cell-biologic action

Energy Technology Data Exchange (ETDEWEB)

Mahl, Dirk; Diendorf, Joerg; Ristig, Simon [University of Duisburg-Essen, Department of Inorganic Chemistry, Center for Nanointegration Duisburg-Essen (CeNIDE) (Germany); Greulich, Christina [Ruhr-University of Bochum, Bergmannsheil University Hospital/Surgical Research (Germany); Li Zian; Farle, Michael [University of Duisburg-Essen, Faculty of Physics, Center for Nanointegration Duisburg-Essen (CeNIDE) (Germany); Koeller, Manfred [Ruhr-University of Bochum, Bergmannsheil University Hospital/Surgical Research (Germany); Epple, Matthias, E-mail: matthias.epple@uni-due.de [University of Duisburg-Essen, Department of Inorganic Chemistry, Center for Nanointegration Duisburg-Essen (CeNIDE) (Germany)

2012-10-15

Silver, gold, and silver-gold-alloy nanoparticles were prepared by citrate reduction modified by the addition of tannin during the synthesis, leading to a reduction in particle size by a factor of three. Nanoparticles can be prepared by this easy water-based synthesis and subsequently functionalized by the addition of either tris(3-sulfonatophenyl)phosphine or poly(N-vinylpyrrolidone). The resulting nanoparticles of silver (diameter 15-25 nm), gold (5-6 nm), and silver-gold (50:50; 10-12 nm) were easily dispersable in water and also in cell culture media (RPMI + 10 % fetal calf serum), as shown by nanoparticle tracking analysis and differential centrifugal sedimentation. High-resolution transmission electron microscopy showed a polycrystalline nature of all nanoparticles. EDX on single silver-gold nanoparticles indicated that the concentration of gold is higher inside a nanoparticle. The biologic action of the nanoparticles toward human mesenchymal stem cells (hMSC) was different: Silver nanoparticles showed a significant concentration-dependent influence on the viability of hMSC. Gold nanoparticles showed only a small effect on the viability of hMSC after 7 days. Surprisingly, silver-gold nanoparticles had no significant influence on the viability of hMSC despite the silver content. Silver nanoparticles and silver-gold nanoparticles in the concentration range of 5-20 {mu}g mL{sup -1} induced the activation of hMSC as indicated by the release of IL-8. In contrast, gold nanoparticles led to a reduction of the release of IL-6 and IL-8.

Green synthesis of palladium nanoparticles with carboxymethyl cellulose for degradation of azo-dyes

Energy Technology Data Exchange (ETDEWEB)

Li, Gang; Li, Yun; Wang, Zhengdong; Liu, Huihong, E-mail: huihongliu@126.com

2017-02-01

Palladium nanoparticles (PdNPs) were synthesized through friendly environmental method using PdCl{sub 2} and carboxymethyl cellulose (CMC) in an aqueous solution (pH 6) at controlled water bath (80 °C) for 30 min. CMC functioned as both reducing and stabilizing agent. The characterization through high resolution-transmission electron microscopic (HRTEM) and X-ray Fluorescence Spectrometry (XRF) inferred that the as-synthesized PdNPs were spherical in shape with a face cubic crystal (FCC) structure. The results from dynamic light scattering (DLS) suggested the PdNPs had the narrow size distribution with an average size of 2.5 nm. The negative zeta potential (−52.6 mV) kept the as-synthesized PdNPs stable more than one year. The PdNPs showed the excellent catalytic activity by reducing degradation of azo-dyes, such as p-Aminoazobenzene, acid red 66, acid orange 7, scarlet 3G and reactive yellow 179, in the present of sodium borohydride. - Highlights: • Green synthesis of palladium nanoparticles using carboxymethyl cellulose. • The synthesis of palladium nanoparticles were performed easily. • Carboxymethyl cellulose acts as both reducing and stabilization agents. • The as-synthesized palladium nanoparticles show excellent catalytic activity.

Synthesis and characterization of silver nanoparticles in AOT microemulsion system

International Nuclear Information System (INIS)

Zhang Wanzhong; Qiao Xueliang; Chen Jianguo

2006-01-01

Colloidal silver nanoparticles have been synthesized in water-in-oil microemulsion using silver nitrate solubilized in the water core of one microemulsion as source of silver ions, hydrazine hydrate solubilized in the water core of another microemulsion as reducing agent, dodecane as the oil phase, sodium bis(2-ethylhexyl) sulfosuccinate (AOT) as the surfactant. The UV-vis absorption spectra and transmission electron microscopy (TEM) have been used to trace the growth process and elucidate the structure of the silver nanoparticles. UV-vis spectra show that the Ag 4 + intermediates formed at early stages of the reaction and then the clusters grow or aggregate to larger nanoparticles. TEM micrographs confirm that the silver nanoparticles are all spherical. The resulting particles have a very narrow size distribution. Meanwhile, the diameter size of the particles is so small that the smallest mean diameter is only 1.6nm. IR results show that the surfactant molecules are strongly adsorbed on the surface of silver particles through a coordination bond between the silver atom and the sulfonic group of AOT molecules, which endows the particles with a good stability in oil solvents. As dodecane is used as oil solvent to prepare silver nanoparticles, the formed nano-silver sol is almost nontoxic. As a result, the silver nanoparticles need not be separated from the reaction solution and the silver sol may be directly used in antibacterial fields

Synthesis and characterization of silver nanoparticles from (bis)alkylamine silver carboxylate precursors

Energy Technology Data Exchange (ETDEWEB)

Uznanski, Pawel, E-mail: puznansk@cbmm.lodz.pl; Zakrzewska, Joanna [Centre of Molecular and Macromolecular Studies, PAS (Poland); Favier, Frederic, E-mail: fredf@univ-montp2.fr [Université Montpellier II, ICGM - UMR5253- Equipe AIME (France); Kazmierski, Slawomir; Bryszewska, Ewa [Centre of Molecular and Macromolecular Studies, PAS (Poland)

2017-03-15

A comparative study of amine and silver carboxylate adducts [R{sub 1}COOAg-2(R{sub 2}NH{sub 2})] (R{sub 1} = 1, 7, 11; R{sub 2} = 8, 12) as a key intermediate in NPs synthesis is carried out via differential scanning calorimetry, solid-state FT-infrared spectroscopy, {sup 13}C CP MAS NMR, powder X-ray diffraction and X-ray photoelectron spectroscopy, and various solution NMR spectroscopies ({sup 1}H and {sup 13}C NMR, pulsed field gradient spin-echo NMR, and ROESY). It is proposed that carboxyl moieties in the presence of amine ligands are bound to silver ions via chelating bidentate type of coordination as opposed to bridging bidentate coordination of pure silver carboxylates resulting from the formation of dimeric units. All complexes are packed as lamellar bilayer structures. Silver carboxylate/amine complexes show one first-order melting transition. The evidence presented in this study shows that phase behavior of monovalent metal carboxylates are controlled, mainly, by head group bonding. In solution, insoluble silver salt is stabilized by amine molecules which exist in dynamic equilibrium. Using (bis)amine-silver carboxylate complex as precursor, silver nanoparticles were fabricated. During high-temperature thermolysis, the (bis)amine-carboxylate adduct decomposes to produce silver nanoparticles of small size. NPs are stabilized by strongly interacting carboxylate and trace amounts of amine derived from the silver precursor interacting with carboxylic acid. A corresponding aliphatic amide obtained from silver precursor at high-temperature reaction conditions is not taking part in the stabilization. Combining NMR techniques with FTIR, it was possible to follow an original stabilization mechanism.

Size- and Shape-Dependent Antibacterial Studies of Silver Nanoparticles Synthesized by Wet Chemical Routes

Directory of Open Access Journals (Sweden)

Muhammad Akram Raza

2016-04-01

Full Text Available Silver nanoparticles (AgNPs of different shapes and sizes were prepared by solution-based chemical reduction routes. Silver nitrate was used as a precursor, tri-sodium citrate (TSC and sodium borohydride as reducing agents, while polyvinylpyrrolidone (PVP was used as a stabilizing agent. The morphology, size, and structural properties of obtained nanoparticles were characterized by scanning electron microscopy (SEM, UV-visible spectroscopy (UV-VIS, and X-ray diffraction (XRD techniques. Spherical AgNPs, as depicted by SEM, were found to have diameters in the range of 15 to 90 nm while lengths of the edges of the triangular particles were about 150 nm. The characteristic surface plasmon resonance (SPR peaks of different spherical silver colloids occurring in the wavelength range of 397 to 504 nm, whereas triangular particles showed two peaks, first at 392 nm and second at 789 nm as measured by UV-VIS. The XRD spectra of the prepared samples indicated the face-centered cubic crystalline structure of metallic AgNPs. The in vitro antibacterial properties of all synthesized AgNPs against two types of Gram-negative bacteria, Pseudomonas aeruginosa and Escherichia coli were examined by Kirby–Bauer disk diffusion susceptibility method. It was noticed that the smallest-sized spherical AgNPs demonstrated a better antibacterial activity against both bacterial strains as compared to the triangular and larger spherical shaped AgNPs.

Micellized sequestered silver atoms and small silver clusters

International Nuclear Information System (INIS)

Borgarello, E.; Lawless, D.; Serpone, N.; Pelizzetti, E.; Meisel, D.

1990-01-01

Pulse radiolysis was used to examine the nature of the silver species obtained when an aqueous solution containing sequestered Ag + ions was reduced by hydrated electrons in the presence of a surfactant macrocyclic crown ether, labeled L, and/or a maltoside surfactant. The initially formed product is the Ag 0 (L) species which rapidly loses its ligand (half-life ≤5 μs) and reacts with another Ag + (L) ion to form Ag 2 + (L). The latter species decays by a bimolecular process to form the Ag 4 2+ (L) n species at a faster rate than its ligand free analogue. Ultimately, colloidal metallic silver, (Ag) n , forms which is stabilized by the surfactant moieties. No long-term stability to the reduced monomolecular species could be obtained

Nanostructured palladium tailored via carbonyl chemical route towards oxygen reduction reaction

International Nuclear Information System (INIS)

Luo, Y.; Mora-Hernández, J.M.; Estudillo-Wong, L.A.; Arce-Estrada, E.M.; Alonso-Vante, N.

2015-01-01

Graphical Abstract: Mass-depending morphologies of nanostructured Palladium obtained via the carbonyl chemical route. Display Omitted -- Highlights: •Mass-depending morphology was observed in nanostructured palladium supported on carbon prepared by the carbonyl chemical route. •The Morphological effect of carbon supported Pd was investigated towards ORR. -- Abstract: Carbon supported palladium nanostructures were synthesized via the carbonyl chemical route. Compared with nanostructured platinum, prepared via carbonyl chemical route, Pd nanomaterials showed mass-loading morphology, whereas particle size and morphology of Pt nanostructures was constant. The oxygen reduction reaction (ORR) on nanostructured Pd, with different morphology in both acid and alkaline medium was investigated. A relationship, based on X-ray diffraction structural analysis pattern, transmission electron microscope, with the Pd morphological effect on ORR activity was identified

Shaping surface of palladium nanospheres through the control of reaction parameters

International Nuclear Information System (INIS)

Wang Lianmeng; Tan Enzhong; Guo Lin; Wang Lihua; Han Xiaodong

2011-01-01

Solid, cracked, and flower-shaped surfaces of palladium nanospheres with high yields and good uniformity were successfully prepared by a wet chemical method. On the basis of the experimental data, the same size of palladium nanosphere with different surface morphologies can be regulated only by changing the amount of ammonium hydroxide and reductant in one experimental system. The as-prepared products were studied by transmission electron microscopy (TEM), scanning electron microscopy (SEM) and x-ray diffraction (XRD). In addition, surface-enhanced Raman scattering (SERS) spectra on the as-prepared different surface of palladium nanospheres exhibit high activity towards p-aminothiophenol (PATP) detection, and the result further reveals that the predominance of the a1 vibration mode in the SERS spectra via an electromagnetic (EM) mechanism is significant.

Gravimetric and volumetric determination of the purity of electrolytically refined silver and the produced silver nitrate

Directory of Open Access Journals (Sweden)

Ačanski Marijana M.

2007-01-01

Full Text Available Silver is, along with gold and the platinum-group metals, one of the so called precious metals. Because of its comparative scarcity, brilliant white color, malleability and resistance to atmospheric oxidation, silver has been used in the manufacture of coins and jewelry for a long time. Silver has the highest known electrical and thermal conductivity of all metals and is used in fabricating printed electrical circuits, and also as a coating for electronic conductors. It is also alloyed with other elements such as nickel or palladium for use in electrical contacts. The most useful silver salt is silver nitrate, a caustic chemical reagent, significant as an antiseptic and as a reagent in analytical chemistry. Pure silver nitrate is an intermediate in the industrial preparation of other silver salts, including the colloidal silver compounds used in medicine and the silver halides incorporated into photographic emulsions. Silver halides become increasingly insoluble in the series: AgCl, AgBr, AgI. All silver salts are sensitive to light and are used in photographic coatings on film and paper. The ZORKA-PHARMA company (Sabac, Serbia specializes in the production of pharmaceutical remedies and lab chemicals. One of its products is chemical silver nitrate (argentum-nitricum (l. Silver nitrate is generally produced by dissolving pure electrolytically refined silver in hot 48% nitric acid. Since the purity of silver nitrate, produced in 2002, was not in compliance with the p.a. level of purity, there was doubt that the electrolytically refined silver was pure. The aim of this research was the gravimetric and volumetric determination of the purity of electrolytically refined silver and silver nitrate, produced industrially and in a laboratory. The purity determination was carried out gravimetrically, by the sedimentation of silver(I ions in the form of insoluble silver salts: AgCl, AgBr and Agi, and volumetrically, according to Mohr and Volhardt. The

Cloud point extraction and flame atomic absorption spectrometric determination of cadmium(II), lead(II), palladium(II) and silver(I) in environmental samples

International Nuclear Information System (INIS)

Ghaedi, Mehrorang; Shokrollahi, Ardeshir; Niknam, Khodabakhsh; Niknam, Ebrahim; Najibi, Asma; Soylak, Mustafa

2009-01-01

The phase-separation phenomenon of non-ionic surfactants occurring in aqueous solution was used for the extraction of cadmium(II), lead(II), palladium(II) and silver(I). The analytical procedure involved the formation of understudy metals complex with bis((1H-benzo [d] imidazol-2yl)ethyl) sulfane (BIES), and quantitatively extracted to the phase rich in octylphenoxypolyethoxyethanol (Triton X-114) after centrifugation. Methanol acidified with 1 mol L -1 HNO 3 was added to the surfactant-rich phase prior to its analysis by flame atomic absorption spectrometry (FAAS). The concentration of BIES, pH and amount of surfactant (Triton X-114) was optimized. At optimum conditions, the detection limits of (3 sdb/m) of 1.4, 2.8, 1.6 and 1.4 ng mL -1 for Cd 2+ , Pb 2+ , Pd 2+ and Ag + along with preconcentration factors of 30 and enrichment factors of 48, 39, 32 and 42 for Cd 2+ , Pb 2+ , Pd 2+ and Ag + , respectively, were obtained. The proposed cloud point extraction has been successfully applied for the determination of metal ions in real samples with complicated matrix such as radiology waste, vegetable, blood and urine samples.

Synthesis of honeycomb-like palladium nanostructures by using cucurbit[7]uril and their catalytic activities for reduction of 4-nitrophenol

Energy Technology Data Exchange (ETDEWEB)

Premkumar, Thathan [Department of Materials Science and Engineering, Gwangju Institute of Science and Technology (GIST), 1 Oryong-dong, Buk-gu, Gwangju 500-712 (Korea, Republic of); The University College/Department of Chemistry, Sungkyunkwan University, Suwon 440-746 (Korea, Republic of); Geckeler, Kurt E., E-mail: keg@gist.ac.kr [Department of Materials Science and Engineering, Gwangju Institute of Science and Technology (GIST), 1 Oryong-dong, Buk-gu, Gwangju 500-712 (Korea, Republic of); Department of Nanobio Materials and Electronics (WCU), Gwangju Institute of Science and Technology (GIST), 1 Oryong-dong, Buk-gu, Gwangju 500-712 (Korea, Republic of)

2014-12-15

An eco-friendly one-pot method to synthesize self-assembled palladium nanoclusters using a macrocycle, namely cucurbit[7]uril, in the alkaline medium without employing any special reducing or capping agents and/or external energy at room temperature is described. This greener approach, which utilizes water as a benign solvent and biocompatible cucurbit[7]uril as both reducing and protecting agents, can be applied to synthesize other noble metal nanoparticles such as gold, silver, and platinum. Owing to unique structural arrangement of cucurbit[7]uril, it was possible to prepare palladium nanoclusters of honeycomb-like structure irrespective of the reaction conditions. The honeycomb-like palladium nanoclusters were characterized using transmission electron microscopy (TEM), higher-resolution TEM (HR-TEM), X-ray diffraction (XRD), thermogravimetric analysis (TGA), UV–vis, and FT-IR spectroscopy. Significantly, the synthesized palladium nanoclusters exhibited catalytic activity for the reduction reaction of 4-nitrophenol at room temperature. The approach launched here is easy, green, and user-friendly in contrast to the conventional techniques using polymers or surfactants and harsh reductants. - Highlights: • A simple and one-pot method to synthesis palladium nanostructures with honey-comb like structure. • The strategy established here does not require any harsh and toxic reducing agents. • It has a potential to be a general method for the synthesis of metal nanoparticles in water medium. • Palladium nanoclusters can be used as catalyst for the reduction reaction of 4-nitrophenol. • This system makes a novel platform for industrial and biomedical applications.

Pore surface fractal analysis of palladium-alumina ceramic membrane using Frenkel-Halsey-Hill (FHH) model.

Science.gov (United States)

Ahmad, A L; Mustafa, N N N

2006-09-15

The alumina ceramic membrane has been modified by the addition of palladium in order to improve the H(2) permeability and selectivity. Palladium-alumina ceramic membrane was prepared via a sol-gel method and subjected to thermal treatment in the temperature range 500-1100 degrees C. Fractal analysis from nitrogen adsorption isotherm is used to study the pore surface roughness of palladium-alumina ceramic membrane with different chemical composition (nitric acid, PVA and palladium) and calcinations process in terms of surface fractal dimension, D. Frenkel-Halsey-Hill (FHH) model was used to determine the D value of palladium-alumina membrane. Following FHH model, the D value of palladium-alumina membrane increased as the calcinations temperature increased from 500 to 700 degrees C but decreased after calcined at 900 and 1100 degrees C. With increasing palladium concentration from 0.5 g Pd/100 ml H(2)O to 2 g Pd/100 ml H(2)O, D value of membrane decreased, indicating to the smoother surface. Addition of higher amount of PVA and palladium reduced the surface fractal of the membrane due to the heterogeneous distribution of pores. However, the D value increased when nitric acid concentration was increased from 1 to 15 M. The effect of calcinations temperature, PVA ratio, palladium and acid concentration on membrane surface area, pore size and pore distribution also studied.

Formic acid-assisted synthesis of palladium nanocrystals and their electrocatalytic properties.

Science.gov (United States)

Wang, Qinchao; Wang, Yiqian; Guo, Peizhi; Li, Qun; Ding, Ruixue; Wang, Baoyan; Li, Hongliang; Liu, Jingquan; Zhao, X S

2014-01-14

Palladium (Pd) nanocrystals have been synthesized by using formic acid as the reducing agent at room temperature. When the concentration of formic acid was increased continuously, the size of Pd nanocrystals first decreased to a minimum and then increased slightly again. The products have been investigated by a series of techniques, including X-ray diffraction, high-resolution transmission electron microscopy (HRTEM), UV-vis absorption, and electrochemical measurements. The formation of Pd nanocrystals is proposed to be closely related to the dynamical imbalance of the growth and dissolution rate of Pd nanocrystals associated with the adsorption of formate ions onto the surface of the intermediates. It is found that small Pd nanocrystals showed blue-shifted adsorption peaks compared with large ones. Pd nanocrystals with the smallest size display the highest electrocatalytic activity for the electrooxidation of formic acid and ethanol on the basis of cyclic voltammetry and chronoamperometric data. It is suggested that both the electrochemical active surface area and the small size effect are the key roles in determining the electrocatalytic performances of Pd nanocrystals. A "dissolution-deposition-aggregation" process is proposed to explain the variation of the electrocatalytic activity during the electrocatalysis according to the HRTEM characterization.

Poly(methyl methacrylate) Composites with Size-selected Silver Nanoparticles Fabricated Using Cluster Beam Technique

DEFF Research Database (Denmark)

Muhammad, Hanif; Juluri, Raghavendra R.; Chirumamilla, Manohar

2016-01-01

based on cluster beam technique allowing the formation of monocrystalline size-selected silver nanoparticles with a ±5–7% precision of diameter and controllable embedment into poly (methyl methacrylate). It is shown that the soft-landed silver clusters preserve almost spherical shape with a slight...... tendency to flattening upon impact. By controlling the polymer hardness (from viscous to soft state) prior the cluster deposition and annealing conditions after the deposition the degree of immersion of the nanoparticles into polymer can be tuned, thus, making it possible to create composites with either...

Dislocation/hydrogen interaction mechanisms in hydrided nanocrystalline palladium films

International Nuclear Information System (INIS)

Amin-Ahmadi, Behnam; Connétable, Damien; Fivel, Marc; Tanguy, Döme; Delmelle, Renaud; Turner, Stuart; Malet, Loic; Godet, Stephane; Pardoen, Thomas; Proost, Joris; Schryvers, Dominique

2016-01-01

The nanoscale plasticity mechanisms activated during hydriding cycles in sputtered nanocrystalline Pd films have been investigated ex-situ using advanced transmission electron microscopy techniques. The internal stress developing within the films during hydriding has been monitored in-situ. Results showed that in Pd films hydrided to β-phase, local plasticity was mainly controlled by dislocation activity in spite of the small grain size. Changes of the grain size distribution and the crystallographic texture have not been observed. In contrast, significant microstructural changes were not observed in Pd films hydrided to α-phase. Moreover, the effect of hydrogen loading on the nature and density of dislocations has been investigated using aberration-corrected TEM. Surprisingly, a high density of shear type stacking faults has been observed after dehydriding, indicating a significant effect of hydrogen on the nucleation energy barriers of Shockley partial dislocations. Ab-initio calculations of the effect of hydrogen on the intrinsic stable and unstable stacking fault energies of palladium confirm the experimental observations.

Silver-doped manganese dioxide and trioxide nanoparticles inhibit both gram positive and gram negative pathogenic bacteria.

Science.gov (United States)

Kunkalekar, R K; Prabhu, M S; Naik, M M; Salker, A V

2014-01-01

Palladium, ruthenium and silver-doped MnO2 and silver doped Mn2O3 nanoparticles were synthesized by simple co-precipitation technique. SEM-TEM analysis revealed the nano-size of these synthesized samples. XPS data illustrates that Mn is present in 4+ and 3+ oxidation states in MnO2 and Mn2O3 respectively. Thermal analysis gave significant evidence for the phase changes with increasing temperature. Antibacterial activity of these synthesized nanoparticles on three Gram positive bacterial cultures (Staphylococcus aureus ATCC 6538, Streptococcus epidermis ATCC 12228, Bacillus subtilis ATCC 6633) and three Gram negative cultures (Escherichia coli ATCC 8739, Salmonella abony NCTC 6017 and Klebsiella pneumoniae ATCC 1003) was investigated using a disc diffusion method and live/dead assay. Only Ag-doped MnO2 and Ag-doped Mn2O3 nanoparticles showed antibacterial property against all six-test bacteria but Ag-doped MnO2 was found to be more effective than Ag-doped Mn2O3. Copyright © 2013 Elsevier B.V. All rights reserved.

Recent palladium membrane reactor development at the tritium systems test assembly

International Nuclear Information System (INIS)

Willms, R.S.; Birdsell, S.A.; Wilhelm, R.C.

1995-01-01

The palladium membrane reactor (PMR) is proving to be a simple and effective means for recovering hydrogen isotopes from fusion fuel impurities such as methane and water. This device directly combines two techniques which have long been utilized for hydrogen processing, namely catalytic shift reactions and palladium/silver permeators. A proof-of-principle (PMR) has been constructed and tested at the Tritium Systems Test Assembly of Los Alamos National Laboratory. The first tests with this device showed that is was effective for the proposed purpose. Initial work concluded that a nickel catalyst was an appropriate choice for use in a PMR. More detailed testing of the PMR with such a catalyst was performed and reported in other works. It was shown that a nickel catalyst-packed PMR did, indeed, recover hydrogen from water and methane with efficiencies approaching 100% in a single processing pass. These experiments were conducted over an extended period of time and no failure or need for regeneration was encountered. These positive results have prompted further PMR development. Topics addressed include alternate PMR geometries and initial testing of the PMR with tritium. These are the subjects of this paper

Optical properties of DNA-hosted silver clusters

NARCIS (Netherlands)

Markešević, Nemanja

2015-01-01

DNA-hosted silver clusters (Ag:DNAs) have attracted a lot of attention due to their small size (~20 atoms), wide range of applications in chemistry and biology, and sequence-dependent optical tunability. Most of the previous studies are focused on the ensemble of emitters in solution. However,

Plasmonic characterization of photo-induced silver nanoparticles extracted from silver halide based TEM film

Energy Technology Data Exchange (ETDEWEB)

Sudheer,, E-mail: sudheer@rrcat.gov.in; Tiwari, P.; Rai, V. N.; Srivastava, A. K. [Indus Synchrotrons Utilization Division, Raja Ramanna Centre for Advanced Technology Indore, Madhya Pradesh 452013 (India); Varshney, G. K. [Laser Bio-medical Applications & Instrumentation Division, Raja Ramanna Centre for Advanced Technology Indore, Madhya Pradesh 452013 (India)

2016-05-23

The plasmonic responses of silver nanoparticles extracted from silver halide based electron microscope film are investigated. Photo-reduction process is carried out to convert the silver halide grains into the metallic silver. The centrifuge technique is used for separating the silver nanoparticles from the residual solution. Morphological study performed by field emission scanning electron microscope (FESEM) shows that all the nanoparticles have an average diameter of ~120 nm with a high degree of mono dispersion in size. The localized surface plasmon resonance (LSPR) absorption peak at ~537 nm confirms the presence of large size silver nanoparticles.

Impact electrochemistry on screen-printed electrodes for the detection of monodispersed silver nanoparticles of sizes 10-107 nm.

Science.gov (United States)

Nasir, Muhammad Zafir Mohamad; Pumera, Martin

2016-10-12

Impact electrochemistry provides a useful alternative technique for the detection of silver nanoparticles in solutions. The combined use of impact electrochemistry on screen-printed electrodes (SPEs) for the successful detection of silver nanoparticles provides an avenue for future on-site, point-of-care detection devices to be made for environmental, medicinal and biological uses. Here we discuss the use of screen-printed electrodes for the detection of well-defined monodispersed silver nanoparticles of sizes 10, 20, 40, 80, and 107 nm.

Preparation and characterization of uniform-sized chitosan/silver microspheres with antibacterial activities.

Science.gov (United States)

An, Jing; Ji, Zhenxing; Wang, Desong; Luo, Qingzhi; Li, Xueyan

2014-03-01

The chitosan/silver microspheres (CAgMs), which possess effective inhibitory on microorganisms, were prepared by an inverse-emulsification cross-linking method using CS/Ag sol as dispersed phase, whiteruss as continuous phase, and glutaraldehyde as crosslinking agent. The size and shape of CAgMs, greatly affecting their antibacterial activities, were controlled by varying the concentrations of cross-linking agent, emulsifier and CS/Ag colloid. The preparation conditions for obtaining uniform-sized microspheres were optimized. The morphology of CAgMs was characterized by scanning electron microscopy (SEM) and laser particle size analysis. The spherical CAgMs with smooth surface in the mean size of ca. 5 μm exhibited a narrow particle size distribution. Energy Dispersive X-ray spectroscopy (EDX) revealed the elemental composition of the microspheres. Transmission electron micrographs (TEM) and Fourier transform infrared spectroscopy (FTIR) of the microspheres confirmed the formation of silver nanoparticles (AgNPs). The X-ray diffraction (XRD) patterns and UV-Visible diffuse reflectance spectroscopy (UV-vis DRS) of the sample showed that AgNPs with the diameter no more than 20 nm were face-centered cubic crystallites. X-ray photoelectron spectroscopy (XPS) proved that AgO bond existed in the microspheres. Thermogravimetric analysis (TGA) showed that the starting decomposition temperature of CAgMs (ca. 260°C) was much higher than that of CS (ca. 160°C), suggesting that the as-prepared CAgMs possessed better thermal stability than original CS did. Antimicrobial assays were performed using typical Gram bacteria and fungi. The inhibitory effect indicated that the as-prepared microspheres exerted a stronger antibacterial activity as the concentration of the AgNPs is increasing, and the microspheres in smaller size had much better antibacterial activity than those in the larger size. The antimicrobial mechanism of CAgMs was discussed. Copyright © 2013 Elsevier B.V. All

Synthesis of silver nanoparticles using DL-alanine for ESR dosimetry applications

International Nuclear Information System (INIS)

Guidelli, Eder José; Ramos, Ana Paula; Zaniquelli, Maria Elisabete D.; Nicolucci, Patricia; Baffa, Oswaldo

2012-01-01

The potential use of alanine for the production of nanoparticles is presented here for the first time. Silver nanoparticles were synthesized using a simple green method, namely the thermal treatment of silver nitrate aqueous solutions with DL-alanine. The latter compound was employed both as a reducing and a capping agent. Particles with average size equal to 7.5 nm, face-centered cubic crystalline structure, narrow size distribution, and spherical shape were obtained. Interaction between the silver ions present on the surface of the nanoparticles and the amine group of the DL-alanine molecule seems to be responsible for reduction of the silver ions and for the stability of the colloid. The bio-hybrid nano-composite was used as an ESR dosimeter. The amount of silver nanoparticles in the nanocomposite was not sufficient to cause considerable loss of tissue equivalency. Moreover, the samples containing nanoparticles presented increased sensitivity and reduced energetic dependence as compared with pure DL-alanine, contributing to the construction of small-sized dosimeters. - Highlights: ► The synthesis is environmentally benign, easy to perform, and of low-cost. ► DL-Alanine was employed both as reducing and capping agent. ► Mean size of 7.5 nm, narrow size distribution, and spherical shape of particles. ► Increased sensitivity and reduced energetic dependence compared with pure alanine. ► The nanocomposite has potential application for ESR dosimetry.

Biological synthesis of very small silver nanoparticles by culture supernatant of Klebsiella pneumonia: The effects of visible-light irradiation and the liquid mixing process

International Nuclear Information System (INIS)

Mokhtari, Narges; Daneshpajouh, Shahram; Seyedbagheri, Seyedali; Atashdehghan, Reza; Abdi, Khosro; Sarkar, Saeed; Minaian, Sara; Shahverdi, Hamid Reza; Shahverdi, Ahmad Reza

2009-01-01

This study has investigated different visible-light irradiation's effect on the formation of silver nanoparticles from silver nitrate using the culture supernatant of Klebsiella pneumonia. Our study shows that visible-light emission can significantly prompt the synthesis of silver nanoparticles. Also, the study experimentally investigated the liquid mixing process effect on silver nanoparticle synthesis by visible-light irradiation. This study successfully synthesized uniformly dispersed silver nanoparticles with a uniform size and shape in the range of 1-6 nm with an average size of 3 nm. Furthermore, the study investigated the mechanism of the reduction of silver ions by culture supernatant of K. pneumonia, and used X-ray diffraction to characterize silver chloride as an intermediate compound. Silver chloride was prepared synthetically and used as a substrate for the synthesis of silver nanoparticles by culture supernatant of K. pneumonia. The silver nanoparticles have been prepared from silver chloride during this investigation for the first time.

Biological synthesis of very small silver nanoparticles by culture supernatant of Klebsiella pneumonia: The effects of visible-light irradiation and the liquid mixing process

Energy Technology Data Exchange (ETDEWEB)

Mokhtari, Narges [Department of Pharmaceutical Biotechnology and Biotechnology Research Center, Faculty of Pharmacy, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Daneshpajouh, Shahram; Seyedbagheri, Seyedali; Atashdehghan, Reza [Hydrometallurgy Research Unit, Research and Development Center, National Iranian Copper Industries Company, Sarcheshmeh, Rafsanjan (Iran, Islamic Republic of); Abdi, Khosro [Department of Pharmaceutical Biotechnology and Biotechnology Research Center, Faculty of Pharmacy, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Sarkar, Saeed [Research Center for Science and Technology in Medicine, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Minaian, Sara [Department of Pharmaceutical Biotechnology and Biotechnology Research Center, Faculty of Pharmacy, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Shahverdi, Hamid Reza [Department of Material Science, Faculty of Engineering, Tarbiat Modares University, Tehran (Iran, Islamic Republic of); Shahverdi, Ahmad Reza, E-mail: shahverd@sina.tums.ac.ir [Department of Pharmaceutical Biotechnology and Biotechnology Research Center, Faculty of Pharmacy, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of)

2009-06-03

This study has investigated different visible-light irradiation's effect on the formation of silver nanoparticles from silver nitrate using the culture supernatant of Klebsiella pneumonia. Our study shows that visible-light emission can significantly prompt the synthesis of silver nanoparticles. Also, the study experimentally investigated the liquid mixing process effect on silver nanoparticle synthesis by visible-light irradiation. This study successfully synthesized uniformly dispersed silver nanoparticles with a uniform size and shape in the range of 1-6 nm with an average size of 3 nm. Furthermore, the study investigated the mechanism of the reduction of silver ions by culture supernatant of K. pneumonia, and used X-ray diffraction to characterize silver chloride as an intermediate compound. Silver chloride was prepared synthetically and used as a substrate for the synthesis of silver nanoparticles by culture supernatant of K. pneumonia. The silver nanoparticles have been prepared from silver chloride during this investigation for the first time.

Green synthesis of silver nanoparticles and silver colloidal solutions

International Nuclear Information System (INIS)

Nguyen Thi Phuong Phong; Ngo Hoang Minh; Ngo Vo Ke Thanh; Dang Mau Chien

2009-01-01

In this paper, silver colloidal solutions have been synthesized rapidly in green conditions by using microwave irradiation and non-toxic chemistry substances (acid oxalic, silver nitrate, polyvinyl pyrolidone (PVP; Mw = 55 000)). The particle size and morphology of these solutions can be controlled by altering several factors like the time, the power of microwave exposure, and the ratio of silver oxalate and PVP etc. The silver nanoparticles were fabricated by thermal decomposition of silver oxalate. The synthesized silver colloidal solutions and silver nanoparticles were characterized by several analytical techniques like UV- VIS, XRD, TEM, FESEM/EDS and ICP-AAS studies. Finally, we used the synthesized silver colloidal solutions for antibacterial purpose. The obtained results showed that the synthesized silver colloidal solutions, even at very low concentrations, have highly efficient anti-bacterial property.

Leaching of Silver from Silver-Impregnated Food Storage Containers

Science.gov (United States)

Hauri, James F.; Niece, Brian K.

2011-01-01

The use of silver in commercial products has proliferated in recent years owing to its antibacterial properties. Food containers impregnated with micro-sized silver promise long food life, but there is some concern because silver can leach out of the plastic and into the stored food. This laboratory experiment gives students the opportunity to…

Grazing incidence small angle X-ray scattering study of silver nanoparticles in ion-exchanged glasses

Energy Technology Data Exchange (ETDEWEB)

Cheng, Weidong, E-mail: 57399942@qq.com [College of Materials Science and Engineering, Qiqihar University, Qiqihar 161006 (China); Wu, Zhaojun [Department of Practice Teaching and Equipment Management, Qiqihar University, Qiqihar 161006 (China); Gu, Xiaohua [College of Materials Science and Engineering, Qiqihar University, Qiqihar 161006 (China); Xing, Xueqing; Mo, Guang [Institute of High Energy Physics, Chinese Academy of Sciences, Beijing 100049 (China); Wu, Zhonghua, E-mail: wuzh@ihep.ac.cn [Institute of High Energy Physics, Chinese Academy of Sciences, Beijing 100049 (China)

2015-05-15

The size and distribution of silver nanoparticles in ion-exchanged silicate glass induced by thermal treatments in air at different temperatures were investigated by means of grazing incidence small angle X-ray scattering technique, X-ray diffraction and optical absorption spectra. Silver–sodium ion exchange of soda-lime silicate glasses was done at 350 °C for 240 min, then the samples were treated by thermal annealing in air at different temperatures 400, 500 and 550 °C, respectively, for 1 h. After the annealing treatment above 400 °C for 1 h, smaller Ag nanoparticles occurred, together with bigger ones. Both dissolution of smaller Ag nanoparticles and diffusion of larger ones are discussed in these stages of annealing in this contribution.

Sensitization to palladium in Europe

DEFF Research Database (Denmark)

Muris, Joris; Goossens, An; Gonçalo, Margarida

2015-01-01

BACKGROUND: Recently, sodium tetrachloropalladate (Na2 PdCl4 ) was found to be a more sensitive palladium patch test allergen than palladium dichloride (PdCl2 ). OBJECTIVES: To determine the optimal test concentration of Na2 PdCl4 , to evaluate the prevalence of palladium sensitization with Na2 P...... patch test concentration. Sensitization to palladium is almost as prevalent as sensitization to nickel. The sex distribution is different between nickel-sensitized and palladium-sensitized patients, suggesting different sources of exposure.......Cl4 and PdCl2 , and to compare the results with nickel sensitization in a European multicentre study. MATERIALS AND METHODS: In addition to the European or national baseline series including NiSO4 ·6H2 0 5% pet., consecutive patients were tested with PdCl2 and Na2 PdCl4 2%, 3% and 4% pet. in eight...... European dermatology clinics. The age and sex distributions were also evaluated in patients sensitized to nickel and palladium. RESULTS: In total, 1651 patients were tested. Relative to 3% Na2 PdCl4 , 4% Na2 PdCl4 did not add any information. Two per cent Na2 PdCl4 resulted in more doubtful reactions...

Cloud point extraction and flame atomic absorption spectrometric determination of cadmium(II), lead(II), palladium(II) and silver(I) in environmental samples

Energy Technology Data Exchange (ETDEWEB)

Ghaedi, Mehrorang, E-mail: m_ghaedi@mail.yu.ac.ir [Chemistry Department, Yasouj University, Yasouj 75914-353 (Iran, Islamic Republic of); Shokrollahi, Ardeshir [Chemistry Department, Yasouj University, Yasouj 75914-353 (Iran, Islamic Republic of); Niknam, Khodabakhsh [Chemistry Department, Persian Gulf University, Bushehr (Iran, Islamic Republic of); Niknam, Ebrahim; Najibi, Asma [Chemistry Department, Yasouj University, Yasouj 75914-353 (Iran, Islamic Republic of); Soylak, Mustafa [Chemistry Department, University of Erciyes, 38039 Kayseri (Turkey)

2009-09-15

The phase-separation phenomenon of non-ionic surfactants occurring in aqueous solution was used for the extraction of cadmium(II), lead(II), palladium(II) and silver(I). The analytical procedure involved the formation of understudy metals complex with bis((1H-benzo [d] imidazol-2yl)ethyl) sulfane (BIES), and quantitatively extracted to the phase rich in octylphenoxypolyethoxyethanol (Triton X-114) after centrifugation. Methanol acidified with 1 mol L{sup -1} HNO{sub 3} was added to the surfactant-rich phase prior to its analysis by flame atomic absorption spectrometry (FAAS). The concentration of BIES, pH and amount of surfactant (Triton X-114) was optimized. At optimum conditions, the detection limits of (3 sdb/m) of 1.4, 2.8, 1.6 and 1.4 ng mL{sup -1} for Cd{sup 2+}, Pb{sup 2+}, Pd{sup 2+} and Ag{sup +} along with preconcentration factors of 30 and enrichment factors of 48, 39, 32 and 42 for Cd{sup 2+}, Pb{sup 2+}, Pd{sup 2+} and Ag{sup +}, respectively, were obtained. The proposed cloud point extraction has been successfully applied for the determination of metal ions in real samples with complicated matrix such as radiology waste, vegetable, blood and urine samples.

Complex conductivity response to silver nanoparticles in ...

Science.gov (United States)

The increase in the use of nanoscale materials in consumer products has resulted in a growing concern of their potential hazard to ecosystems and public health from their accidental or intentional introduction to the environment. Key environmental, health, and safety research needs include knowledge and methods for their detection, characterization, fate, and transport. Specifically, techniques available for the direct detection and quantification of their fate and transport in the environment are limited. Their small size, high surface area to volume ratio, interfacial, and electrical properties make metallic nanoparticles, such as silver nanoparticles, good targets for detection using electrical geophysical techniques. Here we measured the complex conductivity response to silver nanoparticles in sand columns under varying moisture conditions (0–30%), nanoparticle concentrations (0–10 mg/g), lithology (presence of clay), pore water salinity (0.0275 and 0.1000 S/m), and particle size (35, 90–210 and 1500–2500 nm). Based on the Cole-Cole relaxation models we obtained the chargeability and the time constant. We demonstrate that complex conductivity can detect silver nanoparticles in porous media with the response enhanced by higher concentrations of silver nanoparticles, moisture content, ionic strength, clay content and particle diameter. Quantification of the volumetric silver nanoparticles content in the porous media can also be obtained from complex co

Toxicological evaluation of nano-sized colloidal silver in experiments on mice. behavioral reactions, morphology of internals

Directory of Open Access Journals (Sweden)

N.V. Zaitseva

2015-06-01

Full Text Available The results of toxicity studies of nano-sized colloidal silver (NCC, the most widely used in medicine, food and life, are given. When evaluating safe doses of silver NP (using commercially available NCC solution stabilized with polyvinylpyrrolidone (PVP, with the size of silver NP at the range of 5-80 nm when orally administered to male mice, BALB/c mice at doses of 0.1; 1.0 and 10 mg/kg of body weight per silver different effects from the motor and orienting-exploratory activity were revealed, for the part of them the dependence on the dose of the NCC was typical. The following peculiarities were found: reduction in motor activity to reduce the frequency of activities requiring physical effort, reduction of the execution time of these actions; increasing anxiety in terms of frequency and duration of attacks of orienting-investigative activity and animals washing. Morphological examination revealed a series of tissue changes of internal organs (especially liver and spleen, to a lesser extent – kidney, heart and colon with increase of the spectrum and severity of structural changes with increasing doses of the NCC. From the combination of the data the conclusion was made that maximal ineffective dose (NOAEL of this nanomaterial at subacute oral administration is no more than 0.1 mg/kg body weight.

Photochemical Synthesis of Silver Nanodecahedrons and Related Nanostructures for Plasmonic Field Enhancement Applications

Science.gov (United States)

Lu, Haifei

Noble-metal nanocrystals have received considerable attention in recent years for their size and shape dependent localized surface Plasmon resonances (LSPR). Various applications based on colloidal nanoparticles, such as surface enhanced Raman scattering (SERS), surface enhanced fluorescence (SEF), plasmonic sensing, photothermal therapy etc., have been broadly explored in the field of biomedicine, because of their extremely large optical scattering and absorption cross sections, as well as giant electric field enhancement on their surface. However, despite its high chemical stability, gold exhibits quite large losses and electric field enhancement is comparatively weaker than silver. Silver nanoparticles synthesized by the traditional technique only cover an LSPR ranged from 420~500 nm. On the other hand, the range of 500~660 nm, which is covered by several easily available commercial laser lines, very limited colloidal silver nanostructures with controllable size and shape have been reported, and realization of tuning the resonance to longer wavelengths is very important for the practical applications. In this thesis, a systematic study on photochemical synthesis of silver nanodecahedrons (NDs) and related nanostructures, and their plasmonic field enhancements are presented. First, the roles of chemicals and the light source during the formation of silver nanoparticles have been studied. We have also developed a preparation route for the production size-controlled silver nanodecahedrons (LSPR range 420 ~ 660 nm) in high purity. Indeed our experiments indicate that both the chemicals and the light sources can affect the shape and purity of final products. Adjusting the molar ratio between sodium citrate and silver nitrate can help to control the crystal structure following rapid reduction from sodium borohydride. Light from a blue LED (465 nm) can efficiently transform the polyvinylpyrrolidone stabilized small silver nanoparticles into silver NDs through photo

Superlattices of platinum and palladium nanoparticles

Energy Technology Data Exchange (ETDEWEB)

MARTIN,JAMES E.; WILCOXON,JESS P.; ODINEK,JUDY G.; PROVENCIO,PAULA P.

2000-04-06

The authors have used a nonionic inverse micelle synthesis technique to form nanoclusters of platinum and palladium. These nanoclusters can be rendered hydrophobic or hydrophilic by the appropriate choice of capping ligand. Unlike Au nanoclusters, Pt nanoclusters show great stability with thiol ligands in aqueous media. Alkane thiols, with alkane chains ranging from C{sub 6} to C{sub 18} were used as hydrophobic ligands, and with some of these they were able to form 2-D and/or 3-D superlattices of Pt nanoclusters as small as 2.7 nm in diameter. Image processing techniques were developed to reliably extract from transmission electron micrographs (TEMs) the particle size distribution, and information about the superlattice domains and their boundaries. The latter permits one to compute the intradomain vector pair correlation function of the particle centers, from which they can accurately determine the lattice spacing and the coherent domain size. From these data the gap between the particles in the coherent domains can be determined as a function of the thiol chain length. It is found that as the thiol chain length increases, the gaps between particles within superlattice domains increases, but more slowly than one might expect, possibly indicating thiol chain interdigitation.

Silver-enhanced block copolymer membranes with biocidal activity

KAUST Repository

Madhavan, Poornima

2014-11-12

Silver nanoparticles were deposited on the surface and pore walls of block copolymer membranes with highly ordered pore structure. Pyridine blocks constitute the pore surfaces, complexing silver ions and promoting a homogeneous distribution. Nanoparticles were then formed by reduction with sodium borohydride. The morphology varied with the preparation conditions (pH and silver ion concentration), as confirmed by field emission scanning and transmission electron microscopy. Silver has a strong biocide activity, which for membranes can bring the advantage of minimizing the growth of bacteria and formation of biofilm. The membranes with nanoparticles prepared under different pH values and ion concentrations were incubated with Pseudomonas aeruginosa and compared with the control. The strongest biocidal activity was achieved with membranes containing membranes prepared under pH 9. Under these conditions, the best distribution with small particle size was observed by microscopy.

Silver-enhanced block copolymer membranes with biocidal activity

KAUST Repository

Madhavan, Poornima; Hong, Pei-Ying; Sougrat, Rachid; Nunes, Suzana Pereira

2014-01-01

Silver nanoparticles were deposited on the surface and pore walls of block copolymer membranes with highly ordered pore structure. Pyridine blocks constitute the pore surfaces, complexing silver ions and promoting a homogeneous distribution. Nanoparticles were then formed by reduction with sodium borohydride. The morphology varied with the preparation conditions (pH and silver ion concentration), as confirmed by field emission scanning and transmission electron microscopy. Silver has a strong biocide activity, which for membranes can bring the advantage of minimizing the growth of bacteria and formation of biofilm. The membranes with nanoparticles prepared under different pH values and ion concentrations were incubated with Pseudomonas aeruginosa and compared with the control. The strongest biocidal activity was achieved with membranes containing membranes prepared under pH 9. Under these conditions, the best distribution with small particle size was observed by microscopy.

Size control and catalytic activity of bio-supported palladium nanoparticles.

Science.gov (United States)

Søbjerg, Lina Sveidal; Lindhardt, Anders T; Skrydstrup, Troels; Finster, Kai; Meyer, Rikke Louise

2011-07-01

The development of nanoparticles has greatly improved the catalytic properties of metals due to the higher surface to volume ratio of smaller particles. The production of nanoparticles is most commonly based on abiotic processes, but in the search for alternative protocols, bacterial cells have been identified as excellent scaffolds of nanoparticle nucleation, and bacteria have been successfully employed to recover and regenerate platinum group metals from industrial waste. We report on the formation of bio-supported palladium (Pd) nanoparticles on the surface of two bacterial species with distinctly different surfaces: the gram positive Staphylococcus sciuri and the gram negative Cupriavidus necator. We investigated how the type of bacterium and the amount of biomass affected the size and catalytic properties of the nanoparticles formed. By increasing the biomass:Pd ratio, we could produce bio-supported Pd nanoparticles smaller than 10nm in diameter, whereas lower biomass:Pd ratios resulted in particles ranging from few to hundreds of nm. The bio-supported Pd nanoparticle catalytic properties were investigated towards the Suzuki-Miyaura cross coupling reaction and hydrogenation reactions. Surprisingly, the smallest nanoparticles obtained at the highest biomass:Pd ratio showed no reactivity towards the test reactions. The lack of reactivity appears to be caused by thiol groups, which poison the catalyst by binding strongly to Pd. Different treatments intended to liberate particles from the biomass, such as burning or rinsing in acetone, did not re-establish their catalytic activity. Sulphur-free biomaterials should therefore be explored as more suitable scaffolds for Pd(0) nanoparticle formation. Copyright © 2011 Elsevier B.V. All rights reserved.

Small head size after atomic irradiation

International Nuclear Information System (INIS)

Miller, R.W.; Mulvihill, J.J.

1975-01-01

A study of children exposed to nuclear explosions in Hiroshima and Nagasaki showed small head size and mental retardation when exposure occurred less than 18 weeks of gestational age. Increased frequency of small head size occurred when maternal exposure was 10 to 19 rad. Tables and graphs are presented to show relationships between dose, gestational age, and frequency of small head size

Ballistic-type field penetration into metals illustrated by high- and low-frequency size-effect measurements in silver

DEFF Research Database (Denmark)

Gantmakher, V. F.; Lebech, Jens; Bak, Christen Kjeldahl

1979-01-01

Radio-frequency size-effect experiments were performed on silver plane-parallel plates at high, 45 GHz, and low, 3 MHz, frequencies. By investigation of size-effect structures we show the influence of frequency on the field distribution inside the metal. When the frequency increases, the splash...

Synthesis and characterization of silver nanoparticles by sol-gel route from silver nitrate

International Nuclear Information System (INIS)

Morales, Jorge; Moran, Jose; Quintana, Maria; Estrada, Walter

2009-01-01

Silver nanoparticles colloids have been synthesized by sol-gel method. This synthesis consists in silver nitrate reduction by ethylene glycol in a process called polyol. The growth of the nanoparticles have been controlled by the steric stabilization of the colloid with polyvinylpyrrolidone (PVP, M w = 40 000). The silver nanoparticle size and structure was depending on the control of parameters such as: molar concentrations ratio of silver nitrate and PVP, temperature of reaction and the reflux time. Colloids have been characterized by UV-vis spectroscopy in the range from 300 to 1000 nm. The results show that the typical peak of surface plasmon resonance is formed at 400-450 nm indicating the formation of silver nanoparticles. The presences of silver nanoparticles of spherical shape with size among 20-40 nm were observed by transmission electronic microscopy (TEM). Electron diffraction patterns confirmed that synthesized colloids contain metallic silver with a crystal structure face centered cubic FCC. (author)

In vitro percutaneous penetration and characterization of silver from silver-containing textiles

Directory of Open Access Journals (Sweden)

Bianco C

2015-03-01

Full Text Available Carlotta Bianco,1 Sanja Kezic,2 Matteo Crosera,1 Vesna Svetličić,3 Suzana Šegota,3 Giovanni Maina,4 Canzio Romano,5 Francesca Larese,6,7 Gianpiero Adami11Department of Chemical and Pharmaceutical Sciences, University of Trieste, Trieste, Italy; 2Academic Medical Center, Coronel Institute, University of Amsterdam, Amsterdam, the Netherlands; 3Laboratory for Bioelectrochemistry and Surface Imaging, Division for Marine and Environmental Research, Ruder Boškovic Institute, Zagreb, Croatia; 4Department of Clinical and Biological Sciences, University of Turin, Turin, Italy; 5Department of Public and Pediatric Health Sciences, University of Turin, Turin, Italy; 6Unit of Occupational Medicine, University of Trieste, Trieste, Italy; 7Department of Medical Sciences, University of Trieste, Trieste, ItalyAbstract: The objective of this study was to determine the in vitro percutaneous penetration of silver and characterize the silver species released from textiles in different layers of full thickness human skin. For this purpose, two different wound dressings and a garment soaked in artificial sweat were placed in the donor compartments of Franz cells for 24 hours. The concentration of silver in the donor phase and in the skin was determined by an electrothermal atomic absorption spectrometer (ET-AAS and by inductively coupled plasma mass spectrometer (ICP-MS. The characterization of silver species in the textiles and in the skin layers was made by scanning electron microscopy with integrated energy dispersive X-ray spectroscopy (SEM-EDX. Additionally, the size distribution of silver nanoparticles in the textiles was performed by atomic force microscopy (AFM. On the surface of all investigated materials, silver nanoparticles of different size and morphology were found. Released silver concentrations in the soaking solutions (ie, exposure concentration ranged from 0.7 to 4.7 µg/mL (0.6–4.0 µg/cm2, fitting the bactericidal range. Silver and silver

Confined palladium colloids in mesoporous frameworks for carbon nanotube growth

NARCIS (Netherlands)

Berenguer-Murcia, A.; Rebrov, E.V.; Cabaj, M.; Wheatley, A.E.H.; Johnson, B.F.G.; Robertson, J.; Schouten, J.C.

2009-01-01

Palladium colloidal nanoparticles with an average size of approximately 2.4 nm have been incorporated into mesoporous inorganic thin films following a multistep approach. This involves the deposition of mesoporous titania thin films with a thickness of 200 nm by spin-coating on titanium plates with

Some remarks on the neutron elastic- and enelastic-scattering cross sections of palladium

International Nuclear Information System (INIS)

Chiba, S.; Guenther, P.T.; Smith, A.B.

1989-05-01

The cross sections for the elastic-scattering of 5.9, 7.1 and 8.0 MeV neutrons from elemental palladium were measured at forty scattering angles distributed between ∼15/degree/ and 160/degree/. The inelastic-scattering cross sections for the excitation of palladium levels at energies of 260 keV to 560 keV were measured with high resolution at the same energies, and at a scattering angle of 80/degree/. The experimental results were combined with lower-energy values previously obtained by this group to provide a comprehensive data base extending from near the inelastic-scattering threshold to 8 MeV. That data base was interpreted in terms of a coupled-channel model, including the inelastic excitation of one- and two-phonon vibrational levels of the even isotopes of palladium. It was concluded that the palladium inelastic-scattering cross section, at the low energies of interest in assessment of fast-fission-reactor performance, are large (∼50% greater than given in widely used evaluated fission-product data files). They primarily involve compound-nucleus processes, with only a small direct-reaction component attributable to the excitation of the one-phonon, 2 + , vibrational levels of the even isotopes of palladium. 24 refs., 6 figs

Palladium-cobalt particles as oxygen-reduction electrocatalysts

Science.gov (United States)

Adzic, Radoslav [East Setauket, NY; Huang, Tao [Manorville, NY

2009-12-15

The present invention relates to palladium-cobalt particles useful as oxygen-reducing electrocatalysts. The invention also relates to oxygen-reducing cathodes and fuel cells containing these palladium-cobalt particles. The invention additionally relates to methods for the production of electrical energy by using the palladium-cobalt particles of the invention.

Enantioselective silver nanoclusters: Preparation, characterization and photoluminescence spectroscopy

Energy Technology Data Exchange (ETDEWEB)

Farrag, Mostafa, E-mail: mostafafarrag@aun.edu.eg

2016-09-01

Herein, we report a new wet-synthesis method to separate some water-soluble chiral silver nanoclusters with high yield. The cluster material was obtained by the reduction of silver nitrate with NaBH{sub 4} in the presence of three ligands L-penicillamine (L-pen), D-penicillamine (D-pen) and racemic mixture of penicillamine (rac-pen), functioning as capping ligand. For characterizing all silver cluster samples, the particle size was assessed by transmission electron microscopy (TEM) and powder X-ray diffraction (XRD) and their average chemical formula was determined from thermogravimetric analysis (TGA) and elemental analysis (EA). The particles sizes of all three clusters are 2.1 ± 0.2 nm. The optical properties of the samples were studied by four different methods: UV-vis spectroscopy, Fourier transform infrared spectroscopy (FTIR), photoluminescence spectroscopy (PL) and circular dichroism (CD) spectroscopy. The spectra are dominated by the typical and intense plasmon peak at 486 nm accompanied by a small shoulder at 540 nm. Infrared spectroscopy was measured for the free ligand and protected silver nanoclusters, where the disappearance of the S-H vibrational band (2535–2570 cm{sup −1}) in the silver nanoclusters confirmed anchoring of ligand to the cluster surface through the sulfur atom. PL studies yielded the fluorescent properties of the samples. The main focus of this work, however, lies in the chirality of the particles. For all silver clusters CD spectra were recorded. While for clusters capped with one of the two enantiomers (D- or L-form) typical CD spectra were observed, no significant signals were detected for a racemic ligand mixture. Furthermore, silver clusters show quite large asymmetry factors (up to 3 × 10{sup −4}) in comparison to most other ligand protected clusters. These large factors and bands in the visible range of the spectrum suggest a strong chiral induction from the ligand to the metal core. Textural features of the

Size measurement of gold and silver nanostructures based on their extinction spectrum: limitations and extensions

Directory of Open Access Journals (Sweden)

A A Ashkarran

2013-09-01

Full Text Available  This paper reports on physical principles and the relations between extinction cross section and geometrical properties of silver and gold nanostructures. We introduce some simple relations for determining geometrical properties of silver and gold nanospheres based on the situation of their plasmonic peak. We also applied, investigated and compared the accuracy of these relations using other published works in order to make clear the effects of shape, size distribution and refractive index of particles’ embedding medium. Finally, we extended the equations to non-spherical particles and investigated their accuracy. We found that modified forms of the equations may lead to more exact results for non-spherical metal particles, but for better results, modified equations should depend on shape and size distribution of particles. It seems that these equations are not applicable to particles with corners sharper than cubes' corners i.e. nanostructures with spatial angles less than π/2 sr.

Low Temperature Steam Methane Reforming Over Ni Based Catalytic Membrane Prepared by Electroless Palladium Plating.

Science.gov (United States)

Lee, Sang Moon; Hong, Sung Chang; Kim, Sung Su

2018-09-01

A Pd/Ni-YSZ porous membrane with different palladium loadings and hydrazine as a reducing reagent was prepared by electroless plating and evaluated for the steam methane reforming activity. The steam-reforming activity of a Ni-YSZ porous membrane was greatly increased by the deposition of 4 g/L palladium in the low-temperature range (600 °C). With an increasing amount of reducing reagent, the Pd clusters were well dispersed on the Ni-YSZ surface and were uniform in size (∼500 nm). The Pd/Ni-YSZ catalytic porous membrane prepared by 1 of Pd/hydrazine ratio possessed an abundant amount of metallic Pd. The optimal palladium loadings and Pd/hydrazine ratio increased the catalytic activity in both the steam-reforming reaction and the Pd dispersion.

Rod-shaped silica particles derivatized with elongated silver nanoparticles immobilized within mesopores

Energy Technology Data Exchange (ETDEWEB)

Mnasri, Najib [Institut Charles Gerhardt de Montpellier, CNRS UMR 5253, Université Montpellier, Place Eugène Bataillon, 34095 Montpellier Cedex 5 (France); Materials, Environment and Energy Laboratory (UR14ES26), Faculty of Science, University of Gafsa, 2112 Gafsa (Tunisia); Charnay, Clarence; Ménorval, Louis-Charles de [Institut Charles Gerhardt de Montpellier, CNRS UMR 5253, Université Montpellier, Place Eugène Bataillon, 34095 Montpellier Cedex 5 (France); Elaloui, Elimame [Materials, Environment and Energy Laboratory (UR14ES26), Faculty of Science, University of Gafsa, 2112 Gafsa (Tunisia); Zajac, Jerzy, E-mail: jerzy.zajac@umontpellier.fr [Institut Charles Gerhardt de Montpellier, CNRS UMR 5253, Université Montpellier, Place Eugène Bataillon, 34095 Montpellier Cedex 5 (France)

2016-11-15

Silver-derivatized silica particles possessing a non-spherical morphology and surface plasmon resonance properties have been achieved. Nanometer-sized silica rods with uniformly sized mesopore channels were prepared first making use of alkyltrimethyl ammonium surfactants as porogens and the 1:0.10 tetraethyl orthosilicate (TEOS) : 3-aminopropyltriethoxysilane (APTES) mixture as a silicon source. Silica rods were subsequently functionalized by introducing elongated silver nanoparticles within the intra-particle mesopores thanks to the AgNO{sub 3} reduction procedure based on the action of hemiaminal groups previously located on the mesopore walls. The textural and structural features of the samples were inferred from the combined characterization studies including SEM and TEM microscopy, nitrogen adsorption-desorption at 77 K, powder XRD in the small- and wide-angle region, as well as UV–visible spectroscopy. {sup 129}Xe NMR spectroscopy appeared particularly useful to obtain a correct information about the porous structure of rod-shaped silica particles and the silver incorporation within their intra-particle mesopores. - Highlights: • Mesoporous monodisperse submicron-sized silica rods were achieved. • Silver nanoparticles were located lengthwise within the intra-particle mesopores. • Textural and plasmonic properties of particles studied by {sup 129}Xe NMR and UV–Vis.

Preparation and characterization of uniform-sized chitosan/silver microspheres with antibacterial activities

Energy Technology Data Exchange (ETDEWEB)

An, Jing; Ji, Zhenxing; Wang, Desong, E-mail: dswang06@126.com; Luo, Qingzhi; Li, Xueyan

2014-03-01

The chitosan/silver microspheres (CAgMs), which possess effective inhibitory on microorganisms, were prepared by an inverse-emulsification cross-linking method using CS/Ag sol as dispersed phase, whiteruss as continuous phase, and glutaraldehyde as crosslinking agent. The size and shape of CAgMs, greatly affecting their antibacterial activities, were controlled by varying the concentrations of cross-linking agent, emulsifier and CS/Ag colloid. The preparation conditions for obtaining uniform-sized microspheres were optimized. The morphology of CAgMs was characterized by scanning electron microscopy (SEM) and laser particle size analysis. The spherical CAgMs with smooth surface in the mean size of ca. 5 μm exhibited a narrow particle size distribution. Energy Dispersive X-ray spectroscopy (EDX) revealed the elemental composition of the microspheres. Transmission electron micrographs (TEM) and Fourier transform infrared spectroscopy (FTIR) of the microspheres confirmed the formation of silver nanoparticles (AgNPs). The X-ray diffraction (XRD) patterns and UV–Visible diffuse reflectance spectroscopy (UV–vis DRS) of the sample showed that AgNPs with the diameter no more than 20 nm were face-centered cubic crystallites. X-ray photoelectron spectroscopy (XPS) proved that Ag-O bond existed in the microspheres. Thermogravimetric analysis (TGA) showed that the starting decomposition temperature of CAgMs (ca. 260 °C) was much higher than that of CS (ca. 160 °C), suggesting that the as-prepared CAgMs possessed better thermal stability than original CS did. Antimicrobial assays were performed using typical Gram bacteria and fungi. The inhibitory effect indicated that the as-prepared microspheres exerted a stronger antibacterial activity as the concentration of the AgNPs is increasing, and the microspheres in smaller size had much better antibacterial activity than those in the larger size. The antimicrobial mechanism of CAgMs was discussed. - Highlights: • CAgM was

Palladium transport in SiC

International Nuclear Information System (INIS)

Olivier, E.J.; Neethling, J.H.

2012-01-01

Highlights: ► We investigate the reaction of Pd with SiC at typical HTGR operating temperatures. ► The high temperature mobility of palladium silicides within polycrystalline SiC was studied. ► Corrosion of SiC by Pd was seen in all cases. ► The preferential corrosion and penetration of Pd along grain boundaries in SiC was found. ► The penetration and transport of palladium silicides in SiC along grain boundaries was found. - Abstract: This paper reports on a transmission electron microscopy (TEM) and scanning electron microscopy (SEM) study of Pd corroded SiC. The reaction of Pd with different types of SiC at typical HTGR operating temperatures was examined. In addition the high temperature mobility of palladium silicides within polycrystalline SiC was investigated. The results indicated corrosion of the SiC by Pd in all cases studied. The corrosion leads to the formation of palladium silicides within the SiC, with the predominant phase found being Pd 2 Si. Evidence for the preferential corrosion and penetration of Pd along grain boundaries in polycrystalline SiC was found. The penetration and transport, without significant corrosion, of palladium silicides into polycrystalline SiC along grain boundaries was also observed. Implications of the findings with reference to the use of Tri Isotropic particles in HTGRs will be discussed.

Preparation of 103Pd seed-molecular plating of 103Pd onto silver rod

International Nuclear Information System (INIS)

Zhang Chunfu; Wang Yongxian; Tian Haibin; Yin Duanzhi

2002-01-01

A method for 103 Pd 'molecular plating' onto the surface of a silver rod is reported. The optimal composition of the plating bath is as follows: palladium chloride 0.1 mol/l, formaldehyde 2 mol/l, nitric acid 1 mol/l, and formic acid 0.4 mol/l. The 103 Pd molecular plating procedure will last 25 min at 30 deg. C. This article provides a valuable experience for the preparation of 103 Pd brachytherapy seed

Silver Flakes and Silver Dendrites for Hybrid Electrically Conductive Adhesives with Enhanced Conductivity

Science.gov (United States)

Ma, Hongru; Li, Zhuo; Tian, Xun; Yan, Shaocun; Li, Zhe; Guo, Xuhong; Ma, Yanqing; Ma, Lei

2018-03-01

Silver dendrites were prepared by a facile replacement reaction between silver nitrate and zinc microparticles of 20 μm in size. The influence of reactant molar ratio, reaction solution volume, silver nitrate concentration, and reaction time on the morphology of dendrites was investigated systematically. It was found that uniform tree-like silver structures are synthesized under the optimal conditions. Their structure can be described as a trunk, symmetrical branches, and leaves, which length scales of 5-10, 1-2 μm, and 100-300 nm, respectively. All features were systematically characterized by scanning electron microscopy, transmission electron microscopy (TEM), high-resolution TEM, and x-ray powder diffraction. A hybrid fillers system using silver flakes and dendrites as electrically conductive adhesives (ECAs) exhibited excellent overall performance. This good conductivity can be attributed mainly to the synergy between the silver microflakes (5-20 μm sized irregular sheet structures) and dendrites, allowing more conductive pathways to be formed between the fillers. In order to further optimize the overall electrical conductivity, various mixtures of silver microflakes and silver dendrites were tested in ECAs, with results indicating that the highest conductivity was shown when the amounts of silver microflakes, silver dendrites and the polymer matrix were 69.4 wt.% (20.82 vol.%), 0.6 wt.% (0.18 vol.%), and 30.0 wt.% (79.00 vol.%), respectively. The corresponding mass ratio of silver flakes to silver dendrites was 347:3. The resistivity of ECAs reached as low as 1.7 × 10-4 Ω cm.

77 FR 30227 - Small Business Size Regulations, Small Business Innovation Research (SBIR) Program and Small...

Science.gov (United States)

2012-05-22

... Business Size Regulations, Small Business Innovation Research (SBIR) Program and Small Business Technology... public Webinar and Roundtable Meetings regarding its proposal to amend its regulations governing size and eligibility for the Small Business Innovation Research (SBIR) and Small Business Technology Transfer (STTR...

Hyaluronan/Tween 80-assisted synthesis of silver nanoparticles for biological application

Science.gov (United States)

Li, Hui-Jun; Zhang, An-Qi; Sui, Li; Qian, Dong-Jin; Chen, Meng

2015-02-01

Water-soluble and well-stabilized silver nanoparticles (NPs) of small size have been synthesized using hyaluronan (HA) and Tween 80 as reducing and stabilizing agents. The effect of reaction conditions on the formation process of silver NPs was studied, and an aggregative growth mechanism of the silver NPs dominated in HA/Tween 80 system at pH 12 has been proposed. The obtained Ag NPs were characterized by UV-Vis spectroscopy, transmission electron microscopy, X-ray powder diffraction, and X-ray photoelectron spectroscopy. Moreover, the stability of the HA-Tween 80-silver NPs in normal saline was also studied, and a flexible blend membrane containing chitosan, gelatin, and the HA-Tween 80-silver NPs was prepared for further biological applications. Due to the high specific surface area and improved stability of silver NPs, the chitosan-gelatin-silver membrane has shown high antibacterial activity for strains of Escherichia coli. The cell viability tests indicate that the polymer membrane is non-cytotoxic to HepG2 cells, which might be attributed to its good biocompatibility.

Hyaluronan/Tween 80-assisted synthesis of silver nanoparticles for biological application

International Nuclear Information System (INIS)

Li, Hui-Jun; Zhang, An-Qi; Sui, Li; Qian, Dong-Jin; Chen, Meng

2015-01-01

Water-soluble and well-stabilized silver nanoparticles (NPs) of small size have been synthesized using hyaluronan (HA) and Tween 80 as reducing and stabilizing agents. The effect of reaction conditions on the formation process of silver NPs was studied, and an aggregative growth mechanism of the silver NPs dominated in HA/Tween 80 system at pH 12 has been proposed. The obtained Ag NPs were characterized by UV–Vis spectroscopy, transmission electron microscopy, X-ray powder diffraction, and X-ray photoelectron spectroscopy. Moreover, the stability of the HA–Tween 80-silver NPs in normal saline was also studied, and a flexible blend membrane containing chitosan, gelatin, and the HA–Tween 80-silver NPs was prepared for further biological applications. Due to the high specific surface area and improved stability of silver NPs, the chitosan–gelatin-silver membrane has shown high antibacterial activity for strains of Escherichia coli. The cell viability tests indicate that the polymer membrane is non-cytotoxic to HepG2 cells, which might be attributed to its good biocompatibility

Effect of non-stationary current regimes on the morphology of silver electrodeposits

OpenAIRE

Dimitrov, Aleksandar; Paunovic, Perica; Popovski, Orce

2009-01-01

Abstract: This work is concerned with the use of reverse current regimes in order to form small-grained and compact silver deposits during the electrorefining process. Several parameters were varied, i.e., i) anodic overpotential,ii) cathodic vs. anodic time ratio and iii) duration of the anodic pulse. After optimization of these parameters, phosphate ions were added and the electrolyte was stirred. The effects of a rise of the anodic overpotential on the grain sizes of the silver depos...

76 FR 63216 - Small Business Size Standards: Information

Science.gov (United States)

2011-10-12

... Federal small business assistance, SBA establishes small business definitions (referred to as size... business definition or size standard established by the SBA Administrator. The SBA considers as part of its... SMALL BUSINESS ADMINISTRATION 13 CFR Part 121 RIN 3245-AG26 Small Business Size Standards...

Extracellular Palladium Nanoparticle Production using Geobacter sulfurreducens

KAUST Repository

Yates, Matthew D.

2013-09-03

Sustainable methods are needed to recycle precious metals and synthesize catalytic nanoparticles. Palladium nanoparticles can be produced via microbial reduction of soluble Pd(II) to Pd(0), but in previous tests using dissimilatory metal reducing bacteria (DMRB), the nanoparticles were closely associated with the cells, occupying potential reductive sites and eliminating the potential for cell reuse. The DMRB Geobacter sulfurreducens was shown here to reduce soluble Pd(II) to Pd(0) nanoparticles primarily outside the cell, reducing the toxicity of metal ions, and allowing nanoparticle recovery without cell destruction that has previously been observed using other microorganisms. Cultures reduced 50 ± 3 mg/L Pd(II) with 1% hydrogen gas (v/v headspace) in 6 h incubation tests [100 mg/L Pd(II) initially], compared to 8 ± 3 mg/L (10 mM acetate) without H2. Acetate was ineffective as an electron donor for palladium removal in the presence or absence of fumarate as an electron acceptor. TEM imaging verified that Pd(0) nanoparticles were predominantly in the EPS surrounding cells in H2-fed cultures, with only a small number of particles visible inside the cell. Separation of the cells and EPS by centrifugation allowed reuse of the cell suspensions and effective nanoparticle recovery. These results demonstrate effective palladium recovery and nanoparticle production using G. sulfurreducens cell suspensions and renewable substrates such as H2 gas. © 2013 American Chemical Society.

Quantitative optical extinction-based parametric method for sizing a single core-shell Ag-Ag2O nanoparticle

International Nuclear Information System (INIS)

Santillan, J M J; Scaffardi, L B; Schinca, D C

2011-01-01

This paper develops a parametric method for determining the core radius and shell thickness in small silver-silver-oxide core-shell nanoparticles (Nps) based on single particle optical extinction spectroscopy. The method is based on the study of the relationship between plasmon peak wavelength, full width at half maximum (FWHM) and contrast of the extinction spectra as a function of core radius and shell thickness. This study reveals that plasmon peak wavelength is strongly dependent on shell thickness, whereas FWHM and contrast depend on both variables. These characteristics may be used for establishing an easy and fast stepwise procedure to size core-shell NPs from single particle absorption spectrum. The importance of the method lies in the possibility of monitoring the growth of the silver-oxide layer around small spherical silver Nps in real time. Using the electrostatic approximation of Mie theory, core-shell single particle extinction spectra were calculated for a silver particle's core size smaller than about 20 nm and different thicknesses of silver oxide around it. Analysis of the obtained curves shows a very particular characteristic of the plasmon peak of small silver-silver-oxide Nps, expressed in the fact that its position is strongly dependent on oxide thickness and weakly dependent on the core radius. Even a very thin oxide layer shifts the plasmon peak noticeably, enabling plasmon tuning with appropriate shell thickness. This characteristic, together with the behaviour of FWHM and contrast of the extinction spectra can be combined into a parametric method for sizing both core and shell of single silver Nps in a medium using only optical information. In turn, shell thickness can be related to oxygen content in the Np's surrounding media. The method proposed is applied to size silver Nps from single particle extinction spectrum. The results are compared with full optical spectrum fitting using the electrostatic approximation in Mie theory. The method

DNA-Protected Silver Clusters for Nanophotonics

Directory of Open Access Journals (Sweden)

Elisabeth Gwinn

2015-02-01

Full Text Available DNA-protected silver clusters (AgN-DNA possess unique fluorescence properties that depend on the specific DNA template that stabilizes the cluster. They exhibit peak emission wavelengths that range across the visible and near-IR spectrum. This wide color palette, combined with low toxicity, high fluorescence quantum yields of some clusters, low synthesis costs, small cluster sizes and compatibility with DNA are enabling many applications that employ AgN-DNA. Here we review what is known about the underlying composition and structure of AgN-DNA, and how these relate to the optical properties of these fascinating, hybrid biomolecule-metal cluster nanomaterials. We place AgN-DNA in the general context of ligand-stabilized metal clusters and compare their properties to those of other noble metal clusters stabilized by small molecule ligands. The methods used to isolate pure AgN-DNA for analysis of composition and for studies of solution and single-emitter optical properties are discussed. We give a brief overview of structurally sensitive chiroptical studies, both theoretical and experimental, and review experiments on bringing silver clusters of distinct size and color into nanoscale DNA assemblies. Progress towards using DNA scaffolds to assemble multi-cluster arrays is also reviewed.

Selective liquid-phase oxidation of alcohols catalyzed by a silver-based catalyst promoted by the presence of ceria

DEFF Research Database (Denmark)

Beier, Matthias Josef; Hansen, Thomas Willum; Grunwaldt, Jan-Dierk

2009-01-01

simultaneously. When a high catalytic conversion (>30% over 2 h) was found the number of catalyst components was reduced in the following tests. Thereby, a collaborative effect between a physical mixture of ceria nanoparticles and silver-impregnated silica (10 wt.% Ag–SiO2) was found. The catalytic activity...... by in situ XAS experiments. Oxygen species incorporated in the silver lattice appear to be important for the catalytic oxidation of the alcohol for which a preliminary mechanism is presented. The application of the catalyst was extended to the oxidation of a wide range of primary and secondary alcohols....... Compared to palladium and gold catalysts, the new silver catalyst performed similarly or even superior in the presence of CeO2. In addition, the presence of ceria increased the catalytic activity of all investigated catalysts....

Palladium transport in SiC

Energy Technology Data Exchange (ETDEWEB)

Olivier, E.J., E-mail: jolivier@nmmu.ac.za [Centre for High Resolution Transmission Electron Microscopy, Nelson Mandela Metropolitan University, Port Elizabeth (South Africa); Neethling, J.H. [Centre for High Resolution Transmission Electron Microscopy, Nelson Mandela Metropolitan University, Port Elizabeth (South Africa)

2012-03-15

Highlights: Black-Right-Pointing-Pointer We investigate the reaction of Pd with SiC at typical HTGR operating temperatures. Black-Right-Pointing-Pointer The high temperature mobility of palladium silicides within polycrystalline SiC was studied. Black-Right-Pointing-Pointer Corrosion of SiC by Pd was seen in all cases. Black-Right-Pointing-Pointer The preferential corrosion and penetration of Pd along grain boundaries in SiC was found. Black-Right-Pointing-Pointer The penetration and transport of palladium silicides in SiC along grain boundaries was found. - Abstract: This paper reports on a transmission electron microscopy (TEM) and scanning electron microscopy (SEM) study of Pd corroded SiC. The reaction of Pd with different types of SiC at typical HTGR operating temperatures was examined. In addition the high temperature mobility of palladium silicides within polycrystalline SiC was investigated. The results indicated corrosion of the SiC by Pd in all cases studied. The corrosion leads to the formation of palladium silicides within the SiC, with the predominant phase found being Pd{sub 2}Si. Evidence for the preferential corrosion and penetration of Pd along grain boundaries in polycrystalline SiC was found. The penetration and transport, without significant corrosion, of palladium silicides into polycrystalline SiC along grain boundaries was also observed. Implications of the findings with reference to the use of Tri Isotropic particles in HTGRs will be discussed.

Oxygen kinetics and mechanism at electrocatalysts on the base of palladium-iron system

International Nuclear Information System (INIS)

Tarasevich, M.R.; Zhutaeva, G.V.; Bogdanovskaya, V.A.; Radina, M.V.; Ehrenburg, M.R.; Chalykh, A.E.

2007-01-01

Binary nanodispersed carbon XC72 supported PdFe catalysts with different atomic palladium-to-iron ratios are synthesized and studied in oxygen reduction reaction in acid solution at 60 o C. The Pd:Fe ratio was well controlled by the initial concentrations of Pd and Fe in the precursor solutions. The nanoparticles were characterized by transmission electron microscopy, X-ray diffractometry and X-ray photoelectron spectroscopy. The optimum Pd:Fe ratio for this reaction was determined to be 3:1. The comparison of activities of the catalysts with component ratios equaled 3:1 and 10:1 is shown that the activities are differed from each other by 10-15 times in advantage of catalyst with lesser content of palladium. This phenomenon can be related to the different particle size of both catalysts and different distribution of particles by size discovered by TEM method. The achievement of maximum activity near the ratio of Pd:Fe = 3:1 is due to as effect of alloy-forming and the influence of binary system component ratio and synthesis conditions on dispersity degree of metallic phase nanoparticles. Under optimal conditions of precursor mixture high-temperature pyrolysis, iron produces the stabilizing effect palladium. It gives rise to obtaining the uniform and finely divided (7-8 nm) metallic particles

Towards conducting inks: Polypyrrole–silver colloids

International Nuclear Information System (INIS)

Omastová, Mária; Bober, Patrycja; Morávková, Zuzana; Peřinka, Nikola; Kaplanová, Marie; Syrový, Tomáš; Hromádková, Jiřina; Trchová, Miroslava; Stejskal, Jaroslav

2014-01-01

Graphical abstract: - Highlights: • Composite colloidal particles combining conducting polymer and metal have been prepared. • Conducting colloids are suitable for printing applications. • Polypyrrole/silver colloids are prepared in a single reaction step. • The conductivity control is discussed and still needs improvement. - Abstract: The oxidation of pyrrole with silver nitrate in the presence of suitable water-soluble polymers yields composite polypyrrole–silver colloids. The polypyrrole–silver nanoparticles stabilized with poly(N-vinylpyrrolidone) have a typical size around 350 nm and polydispersity index 0.20, i.e. a moderate polydispersity in size. Similar results have been obtained with poly(vinyl alcohol) as stabilizer. The effect of stabilizer concentration on the particle size is marginal. In the present study, several types of stabilizers have been tested in addition to currently used poly(N-vinylpyrrolidone). Transmission electron microscopy and optical microscopy revealed the gemini morphology of polypyrrole and silver colloidal nanoparticles and confirmed their size and size-distribution determined by dynamic light scattering. The use of colloidal dispersions provides an efficient tool for the UV–vis and FT Raman spectroscopic characterization of polypyrrole, including the transition between polypyrrole salt and corresponding polypyrrole base. The dispersions were used for the preparation of coatings on polyethylene terephthalate foils, and the properties for polypyrrole–silver composites have been compared with those produced from polypyrrole colloids alone

Polypyrrole-palladium nanocomposite coating of micrometer-sized polymer particles toward a recyclable catalyst.

Science.gov (United States)

Fujii, Syuji; Matsuzawa, Soichiro; Hamasaki, Hiroyuki; Nakamura, Yoshinobu; Bouleghlimat, Azzedine; Buurma, Niklaas J

2012-02-07

A range of near-monodisperse, multimicrometer-sized polymer particles has been coated with ultrathin overlayers of polypyrrole-palladium (PPy-Pd) nanocomposite by chemical oxidative polymerization of pyrrole using PdCl(2) as an oxidant in aqueous media. Good control over the targeted PPy-Pd nanocomposite loading is achieved for 5.2 μm diameter polystyrene (PS) particles, and PS particles of up to 84 μm diameter can also be efficiently coated with the PPy-Pd nanocomposite. The seed polymer particles and resulting composite particles were extensively characterized with respect to particle size and size distribution, morphology, surface/bulk chemical compositions, and conductivity. Laser diffraction studies of dilute aqueous suspensions indicate that the polymer particles disperse stably before and after nanocoating with the PPy-Pd nanocomposite. The Fourier transform infrared (FT-IR) spectrum of the PS particles coated with the PPy-Pd nanocomposite overlayer is dominated by the underlying particle, since this is the major component (>96% by mass). Thermogravimetric and elemental analysis indicated that PPy-Pd nanocomposite loadings were below 6 wt %. The conductivity of pressed pellets prepared with the nanocomposite-coated particles increased with a decrease of particle diameter because of higher PPy-Pd nanocomposite loading. "Flattened ball" morphologies were observed by scanning/transmission electron microscopy after extraction of the PS component from the composite particles, which confirmed a PS core and a PPy-Pd nanocomposite shell morphology. X-ray diffraction confirmed the production of elemental Pd and X-ray photoelectron spectroscopy studies indicated the existence of elemental Pd on the surface of the composite particles. Transmission electron microscopy confirmed that nanometer-sized Pd particles were distributed in the shell. Near-monodisperse poly(methyl methacrylate) particles with diameters ranging between 10 and 19 μm have been also successfully

Unexpectedly high uptake of palladium by bituminous coals

Energy Technology Data Exchange (ETDEWEB)

Lakatos, J. [Research Lab. for Mining Chemistry, Hungarian Academy of Sciences, Miskolc-Egyetemvaros (Hungary); Brown, S.D.; Snape, C.E. [Univ. of Strathclyde, Dept. of Pure and Applied Chemistry, Glasgow (United Kingdom)

1997-12-31

The uptake of palladium as a conversion catalyst onto coals of different rank was investigated. Palladium fixation occurs by a different mode to that for alkaline earth and first row transition metals. Therefore, the dispersion of relatively high concentration of palladium by an ion sorption process is even possible for bituminous coals. (orig.)

Effect of non-stationary current regimes on the morphology of silver electrodeposits

OpenAIRE

ALEKSANDAR T. DIMITROV; PERICA PAUNOVIĆ; ORCE POPOVSKI; DRAGAN SLAVKOV; ŽELJKO KAMBEROVIĆ; SVETOMIR HADŽI JORDANOV

2009-01-01

This work is concerned with the use of reverse current regimes in order to form small-grained and compact silver deposits during the electro-refining process. Several parameters were varied, i.e., i) anodic overpotential, ii) cathodic vs. anodic time ratio and iii) duration of the anodic pulse. After optimization of these parameters, phosphate ions were added and the electrolyte was stirred. The effects of a rise of the anodic overpotential on the grain sizes of the silver deposit and compact...

Quantitative optical extinction-based parametric method for sizing a single core-shell Ag-Ag{sub 2}O nanoparticle

Energy Technology Data Exchange (ETDEWEB)

Santillan, J M J; Scaffardi, L B; Schinca, D C, E-mail: lucias@ciop.unlp.edu.ar [Centro de Investigaciones Opticas (CIOp), (CONICET La Plata-CIC) (Argentina)

2011-03-16

This paper develops a parametric method for determining the core radius and shell thickness in small silver-silver-oxide core-shell nanoparticles (Nps) based on single particle optical extinction spectroscopy. The method is based on the study of the relationship between plasmon peak wavelength, full width at half maximum (FWHM) and contrast of the extinction spectra as a function of core radius and shell thickness. This study reveals that plasmon peak wavelength is strongly dependent on shell thickness, whereas FWHM and contrast depend on both variables. These characteristics may be used for establishing an easy and fast stepwise procedure to size core-shell NPs from single particle absorption spectrum. The importance of the method lies in the possibility of monitoring the growth of the silver-oxide layer around small spherical silver Nps in real time. Using the electrostatic approximation of Mie theory, core-shell single particle extinction spectra were calculated for a silver particle's core size smaller than about 20 nm and different thicknesses of silver oxide around it. Analysis of the obtained curves shows a very particular characteristic of the plasmon peak of small silver-silver-oxide Nps, expressed in the fact that its position is strongly dependent on oxide thickness and weakly dependent on the core radius. Even a very thin oxide layer shifts the plasmon peak noticeably, enabling plasmon tuning with appropriate shell thickness. This characteristic, together with the behaviour of FWHM and contrast of the extinction spectra can be combined into a parametric method for sizing both core and shell of single silver Nps in a medium using only optical information. In turn, shell thickness can be related to oxygen content in the Np's surrounding media. The method proposed is applied to size silver Nps from single particle extinction spectrum. The results are compared with full optical spectrum fitting using the electrostatic approximation in Mie theory

Characterization of intracellular palladium nanoparticles synthesized by Desulfovibrio desulfuricans and Bacillus benzeovorans

Energy Technology Data Exchange (ETDEWEB)

Omajali, Jacob B., E-mail: JBO037@bham.ac.uk, E-mail: jbomajali@gmail.com; Mikheenko, Iryna P. [University of Birmingham, Unit of Functional Bionanomaterials, School of Biosciences, Institute of Microbiology and Infection (United Kingdom); Merroun, Mohamed L. [University of Granada, Department of Microbiology, Faculty of Sciences (Spain); Wood, Joseph [University of Birmingham, School of Chemical Engineering (United Kingdom); Macaskie, Lynne E. [University of Birmingham, Unit of Functional Bionanomaterials, School of Biosciences, Institute of Microbiology and Infection (United Kingdom)

2015-06-15

Early studies have focused on the synthesis of palladium nanoparticles within the periplasmic layer or on the outer membrane of Desulfovibrio desulfuricans and on the S-layer protein of Bacillus sphaericus. However, it has remained unclear whether the synthesis of palladium nanoparticles also takes place in the bacterial cell cytoplasm. This study reports the use of high-resolution scanning transmission electron microscopy with a high-angle annular dark field detector and energy dispersive X-ray spectrometry attachment to investigate the intracellular synthesis of palladium nanoparticles (Pd NPs). We show the intracellular synthesis of Pd NPs within cells of two anaerobic strains of D. desulfuricans and an aerobic strain of B. benzeovorans using hydrogen and formate as electron donors. The Pd nanoparticles were small and largely monodispersed, between 0.2 and 8 nm, occasionally from 9 to 12 nm with occasional larger nanoparticles. With D. desulfuricans NCIMB 8307 (but not D. desulfuricans NCIMB 8326) and with B. benzeovorans NCIMB 12555, the NPs were larger when made at the expense of formate, co-localizing with phosphate in the latter, and were crystalline, but were amorphous when made with H{sub 2,} with no phosphorus association. The intracellular Pd nanoparticles were mainly icosahedrons with surfaces comprising {111} facets and about 5 % distortion when compared with that of bulk palladium. The particles were more concentrated in the cell cytoplasm than the cell wall, outer membrane, or periplasm. We provide new evidence for synthesis of palladium nanoparticles within the cytoplasm of bacteria, which were confirmed to maintain cellular integrity during this synthesis.

Tritium evolution from various morphologies of palladium

International Nuclear Information System (INIS)

Tuggle, D.G.; Claytor, T.N.; Taylor, S.F.

1994-01-01

The authors have been able to extend the tritium production techniques to various novel morphologies of palladium. These include small solid wires of various diameters and a type of pressed powder wire and a plasma cell. In most successful experiments, the amount of palladium required, for an equivalent tritium output, has been reduced by a factor of 100 over the older powder methods. In addition, they have observed rates of tritium production (>5 nCi/h) that far exceed most of the previous results. Unfortunately, the methods that they currently use to obtain the tritium are poorly understood and consequently there are numerous variables that need to be investigated before the new methods are as reliable and repeatable as the previous techniques. For instance, it seems that surface and/or bulk impurities play a major role in the successful generation of any tritium. In those samples with total impurity concentrations of >400 ppM essentially no tritium has been generated by the gas loading and electrical simulation methods

Radiochemical neutron activation analysis of high pure palladium and platinum by ion exchange chromatography

International Nuclear Information System (INIS)

Sadikov, I.I.; Zinov'ev, V.G.; Sadikova, Z.O.; Salimov, M.I.

2006-01-01

Full text: The palladium and platinum are widely used for jewel manufacture because of their beautiful white color. However the most part of these metals are widely adopted in the world as catalysts. Many works on analytical chemistry of platinum group elements published during last years are devoted to determination of platinum and palladium in other materials. There are no articles on analysis technique of the palladium and platinum purity published during last 20 years. Available publications are very old and are published till 70th of the last century, and implement chemical and spectral methods. At the same time, the palladium and platinum are very suitable for NAA. Therefore the purpose of our research was development of high-sensitivity and multielement techniques of radiochemical neutron activation analysis of a high pure palladium and platinum. Research of nuclear characteristics of palladium and platinum has shown that radioactive nuclides with different yields are formed under the reactor neutrons. 109 , 111 , 111m Pd, 109m , 111 Ag, 191 , 197 , 199 Pt, 199 Au are the most important among them. 109Pd separation factor is equal to 1*10 5 at palladium analysis, whereas 197 Pt and 199 Au separation factor is equal to 1*10 4 at the platinum analysis every other day after irradiation. Palladium and platinum can be separated by precipitation, extraction and ion exchange methods. For separation of radioactive nuclide of the matrix elements from the impurity elements we used ion exchange chromatography system Dowex-1x8 - 1 M HNO 3 for palladium and Dowex-1x8 - 0.1 M HNO 3 for platinum. At the HNO 3 acid concentrations variation from 0,1 M to 1 M more then 25 elements have distribution factors less than 1 and 10 elements have distribution factors 5 while matrix elements have distribution factors higher than 100. It allows an effective separation of these elements from palladium and platinum. Optimum sizes of the chromatographic column and the column effluent

: Recyclable, ligand free palladium(II) catalyst for Heck reaction

Indian Academy of Sciences (India)

well as heterogeneous palladium catalysts, generated from either palladium(0) compounds or palladium(II) acetate or chloride salts.6 Several ligands such as phosphines, phoshites, carbenes, thioethers have been successfully employed for this reaction.7 However, homogeneous catalysis results in problems of recovery.

77 FR 72702 - Small Business Size Standards: Information

Science.gov (United States)

2012-12-06

... SMALL BUSINESS ADMINISTRATION 13 CFR Part 121 RIN 3245-AG26 Small Business Size Standards: Information AGENCY: U.S. Small Business Administration. ACTION: Final rule. SUMMARY: The United States Small Business Administration (SBA) is increasing the receipts based small business size standards for 15...

Palladium allergy in relation to dentistry

NARCIS (Netherlands)

Muris, J.

2015-01-01

Palladium is a metal that is used as alloying metal for dental crowns and bridges. This thesis focusses on the possible impact of oral exposure to this metal on the immune system, and allergy in particular. An alternative skin test allergen for diagnosing palladium allergy is introduced: (di)sodium

Use of a silver ion selective electrode to assess mechanisms responsible for biological effects of silver nanoparticles

International Nuclear Information System (INIS)

Koch, Marcus; Kiefer, Silke; Cavelius, Christian; Kraegeloh, Annette

2012-01-01

For a detailed analysis of the biological effects of silver nanoparticles, discrimination between effects related to the nano-scale size of the particles and effects of released silver ions is required. Silver ions are either present in the initial particle dispersion or released by the nanoparticles over time. The aim of this study is to monitor the free silver ion activity {Ag + } in the presence of silver nanoparticles using a silver ion selective electrode. Therefore, silver in the form of silver nanoparticles, 4.2 ± 1.4 nm and 2–30 nm in size, or silver nitrate was added to cell culture media in the absence or presence of A549 cells as a model for human type II alveolar epithelial cells. The free silver ion activity measured after the addition of silver nanoparticles was determined by the initial ionic silver content. The p {Ag + } values indicated that the cell culture media decrease the free silver ion activity due to binding of silver ions by constituents of the media. In the presence of A549 cells, the free silver ion activity was further reduced. The morphology of A549 cells, cultivated in DME medium containing 9.1% (v/v) FBS, was affected by adding AgNO 3 at concentrations of ≥30 μM after 24 h. In comparison, silver nanoparticles up to a concentration of 200 μM Ag did not affect cellular morphology. Our experiments indicate that the effect of silver nanoparticles is mainly mediated by silver ions. An effect of silver on cellular morphology was observed at p {Ag + } ≤ 9.2.

Distribution of silver in rats following 28 days of repeated oral exposure to silver nanoparticles or silver acetate

DEFF Research Database (Denmark)

Löschner, Katrin; Hadrup, Niels; Qvortrup, Klaus

2011-01-01

Background: The study investigated the distribution of silver after 28 days repeated oral administration of silver nanoparticles (AgNPs) and silver acetate (AgAc) to rats. Oral administration is a relevant route of exposure because of the use of silver nanoparticles in products related to food...... and food contact materials. Results: AgNPs were synthesized with a size distribution of 14 ± 4 nm in diameter (90% of the nanoparticle volume) and stabilized in aqueous suspension by the polymer polyvinylpyrrolidone (PVP). The AgNPs remained stable throughout the duration of the 28-day oral toxicity study...... in rats. The organ distribution pattern of silver following administration of AgNPs and AgAc was similar. However the absolute silver concentrations in tissues were lower following oral exposure to AgNPs. This was in agreement with an indication of a higher fecal excretion following administration of Ag...

Electron microscopy and EXAFS studies on oxide-supported gold-silver nanoparticles prepared by flame spray pyrolysis

Energy Technology Data Exchange (ETDEWEB)

Hannemann, Stefan [Institute of Chemical and Bioengineering, Swiss Federal Institute of Technology, ETH Hoenggerberg, CH-8093 Zurich (Switzerland); Grunwaldt, Jan-Dierk [Institute of Chemical and Bioengineering, Swiss Federal Institute of Technology, ETH Hoenggerberg, CH-8093 Zurich (Switzerland)]. E-mail: grunwaldt@chem.ethz.ch; Krumeich, Frank [Laboratory of Inorganic Chemistry, Swiss Federal Institute of Technology, ETH Hoenggerberg, CH-8093 Zurich (Switzerland); Kappen, Peter [Department of Physics, La Trobe University, Victoria 3086 (Australia); Baiker, Alfons [Institute of Chemical and Bioengineering, Swiss Federal Institute of Technology, ETH Hoenggerberg, CH-8093 Zurich (Switzerland)

2006-09-15

Gold and gold-silver nanoparticles prepared by flame spray pyrolysis (FSP) were characterized by electron microscopy, in situ X-ray absorption spectroscopy (XANES and EXAFS), X-ray diffraction (XRD) and their catalytic activity in CO oxidation. Within this one-step flame-synthesis procedure, precursor solutions of dimethyl gold(III) acetylacetonate and silver(I) benzoate together with the corresponding precursor of the silica, iron oxide or titania support, were sprayed and combusted. In order to prepare small metal particles, a low noble metal loading was required. A loading of 0.1-1 wt.% of Au and Ag resulted in 1-6 nm particles. The size of the noble metal particles increased with higher loadings of gold and particularly silver. Both scanning transmission electron microscopy (STEM) combined with energy dispersive X-ray spectroscopy (EDXS) and X-ray absorption spectroscopy (XAS) studies proved the formation of mixed Au-Ag particles. In case of 1% Au-1% Ag/SiO{sub 2}, TEM combined with electron spectroscopic imaging (ESI) using an imaging filter could be used in addition to prove the presence of silver and gold in the same noble metal particle. CO oxidation in the presence of hydrogen was chosen as a test reaction sensitive to small gold particles. Both the influence of the particle size and the alloying of gold and silver were reflected in the CO oxidation activity.

Electron microscopy and EXAFS studies on oxide-supported gold-silver nanoparticles prepared by flame spray pyrolysis

International Nuclear Information System (INIS)

Hannemann, Stefan; Grunwaldt, Jan-Dierk; Krumeich, Frank; Kappen, Peter; Baiker, Alfons

2006-01-01

Gold and gold-silver nanoparticles prepared by flame spray pyrolysis (FSP) were characterized by electron microscopy, in situ X-ray absorption spectroscopy (XANES and EXAFS), X-ray diffraction (XRD) and their catalytic activity in CO oxidation. Within this one-step flame-synthesis procedure, precursor solutions of dimethyl gold(III) acetylacetonate and silver(I) benzoate together with the corresponding precursor of the silica, iron oxide or titania support, were sprayed and combusted. In order to prepare small metal particles, a low noble metal loading was required. A loading of 0.1-1 wt.% of Au and Ag resulted in 1-6 nm particles. The size of the noble metal particles increased with higher loadings of gold and particularly silver. Both scanning transmission electron microscopy (STEM) combined with energy dispersive X-ray spectroscopy (EDXS) and X-ray absorption spectroscopy (XAS) studies proved the formation of mixed Au-Ag particles. In case of 1% Au-1% Ag/SiO 2 , TEM combined with electron spectroscopic imaging (ESI) using an imaging filter could be used in addition to prove the presence of silver and gold in the same noble metal particle. CO oxidation in the presence of hydrogen was chosen as a test reaction sensitive to small gold particles. Both the influence of the particle size and the alloying of gold and silver were reflected in the CO oxidation activity

Effets of Silver Salt Concentrations on Green Synthesis of Silver Nanoparticles Using the Plant Nigella Saliva

Directory of Open Access Journals (Sweden)

M.R. Saeri

2016-03-01

Full Text Available Bio-inspired silver nanoparticles were synthesized with the aid of a novel method, using leaves of the plant Nigella sativa. After drying the leaves in air, they were first sweltered in boiling distilled water and the liquid was filtered subsequently. The result was the brothused to reduce solutions including various concentrations of silver nitrate in a proper amount of pH. The displayed UV–visible spectra identified formation of silver nanoparticles whenever the colorless initial acclimated mixture turned brown. The centrifuged powder samples were examined using X-ray diffraction (XRD, Fourier transform infrared spectroscopy (FTIR, scanning electron microscopy (FESEM and energy dispersive X-ray diffraction analysis (EDX methods. The results clearly revealed that the final particles of precipitated powder are high purity agglomerates of silver nanoparticles. Besides, the effects of various amounts of the silver salt on particle size of nano silver were studied, using a particle size analyzer. FTIR results also indicated the role of different functional groups in the synthetic process.

MONTANA PALLADIUM RESEARCH INITIATIVE

Energy Technology Data Exchange (ETDEWEB)

Peters, John; McCloskey, Jay; Douglas, Trevor; Young, Mark; Snyder, Stuart; Gurney, Brian

2012-05-09

Project Objective: The overarching objective of the Montana Palladium Research Initiative is to perform scientific research on the properties and uses of palladium in the context of the U.S. Department of Energy's Hydrogen, Fuel Cells and Infrastructure Technologies Program. The purpose of the research will be to explore possible palladium as an alternative to platinum in hydrogen-economy applications. To achieve this objective, the Initiatives activities will focus on several cutting-edge research approaches across a range of disciplines, including metallurgy, biomimetics, instrumentation development, and systems analysis. Background: Platinum-group elements (PGEs) play significant roles in processing hydrogen, an element that shows high potential to address this need in the U.S. and the world for inexpensive, reliable, clean energy. Platinum, however, is a very expensive component of current and planned systems, so less-expensive alternatives that have similar physical properties are being sought. To this end, several tasks have been defined under the rubric of the Montana Palladium Research Iniative. This broad swath of activities will allow progress on several fronts. The membrane-related activities of Task 1 employs state-of-the-art and leading-edge technologies to develop new, ceramic-substrate metallic membranes for the production of high-purity hydrogen, and develop techniques for the production of thin, defect-free platinum group element catalytic membranes for energy production and pollution control. The biomimetic work in Task 2 explores the use of substrate-attached hydrogen-producing enzymes and the encapsulation of palladium in virion-based protein coats to determine their utility for distributed hydrogen production. Task 3 work involves developing laser-induced breakdown spectroscopy (LIBS) as a real-time, in situ diagnostic technique to characterize PGEs nanoparticles for process monitoring and control. The systems engineering work in task 4

In Vivo Toxicity of Silver Nanoparticles and Silver Ions in Zebrafish (Danio rerio

Directory of Open Access Journals (Sweden)

Katrine Bilberg

2012-01-01

Full Text Available The influence of water chemistry on characterised polyvinyl pyrrolidone- (PVP- coated silver nanoparticles (81 nm was investigated. NaCl solution series of 100–800 mg L−1 lead to initial and temporal increase in nanoparticles size, but agglomeration was limited. pH variation (5–8 had only minor influence on the hydrodynamic particle size. Acute toxicity of nanosivler to zebrafish (Danio rerio was investigated in a 48-hour static renewal study and compared with the toxicity of silver ions (AgNO3. The nanosilver and silver ion 48-hour median lethal concentration (LC50 values were 84 μg L−1 and 25 μg L−1, respectively. To investigate exposure-related stress, the fish behaviour was observed visually after 0, 3, 6, 12, 24, 27, 30, and 48 hours of both nanosilver and ionic silver treatments. These observations revealed increased rate of operculum movement and surface respiration after nanosilver exposure, suggesting respiratory toxicity. The present study demonstrates that silver nanoparticles are lethal to zebrafish.

Size Control Technology of Silver Nanoparticles Using Electron Beam Irradiation

International Nuclear Information System (INIS)

Kang, Hyun Suk; Kim, Byungnam; Kim, Hye Won; Koo, Yong Hwan; Lee, Byung Cheol; Park, Ji Hyun; Bae, Hyung Bin; Park, Changmoon

2013-01-01

The manufacturing of silver nanoparticles using an electron beam is easy, fast, and highly productive, and it is possible at room temperature with no chemical residuals. Its various advantages therefore make this an important method for manufacturing nanoparticles such as silver, copper, and platinum. In particular, despite the use of electron beam irradiation, the results show that this method makes it possible to produce silver nanoparticles at low cost since low beam energy and low doses are used. This means that middle and high-energy electron beam accelerators are very expensive, but a low-energy electron beam accelerator has a relatively low cost of around 4-5 times, and mass production for a flow reaction without the need for extra radiation shielding is possible. Silver nanoparticles are of great interest to many researchers owing to their ability to be used in many applications such as catalysis, nanoelectronics, optical filters, electromagnetic interference shielding, surface Raman scattering, medical supplies, fabrics, cosmetics, hygiene and kitchen supplies, and electric home appliances

Size Control Technology of Silver Nanoparticles Using Electron Beam Irradiation

Energy Technology Data Exchange (ETDEWEB)

Kang, Hyun Suk; Kim, Byungnam; Kim, Hye Won; Koo, Yong Hwan; Lee, Byung Cheol [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Park, Ji Hyun [Univ. of Science and Technology, Daejeon (Korea, Republic of); Bae, Hyung Bin [Korea Advanced Institute of Science and Technology, Daejeon (Korea, Republic of); Park, Changmoon [Chungnam National Univ., Daejeon (Korea, Republic of)

2013-12-15

The manufacturing of silver nanoparticles using an electron beam is easy, fast, and highly productive, and it is possible at room temperature with no chemical residuals. Its various advantages therefore make this an important method for manufacturing nanoparticles such as silver, copper, and platinum. In particular, despite the use of electron beam irradiation, the results show that this method makes it possible to produce silver nanoparticles at low cost since low beam energy and low doses are used. This means that middle and high-energy electron beam accelerators are very expensive, but a low-energy electron beam accelerator has a relatively low cost of around 4-5 times, and mass production for a flow reaction without the need for extra radiation shielding is possible. Silver nanoparticles are of great interest to many researchers owing to their ability to be used in many applications such as catalysis, nanoelectronics, optical filters, electromagnetic interference shielding, surface Raman scattering, medical supplies, fabrics, cosmetics, hygiene and kitchen supplies, and electric home appliances.

Investigation of radiation-chemical behaviour of divalent palladium in perchloric acid solutions

International Nuclear Information System (INIS)

Vladimirova, M.V.; Kalinina, S.V.

1988-01-01

Gamma-radiolysis of divalent palladium in perchloric acid solutions is studied. Absorption spectra of intermediate palladium compounds formed in the irradiated solution are taken. The analysis of literature data as well as comparative analysis of the absorption spectra obtained under irradiation of palladium (2) perchloric acid solutions with absorption spectra of palladium chlorocomplexes allows to suppose that the mentioned compounds are chlorocomplexes of palladium (2) of different composition depending on HClO 4 concentration in the initial solution and absorbed radiation dose. Radiation-chemical reduction of palladium (2) up to metal is stated to take place in the whole studied range of initial concentrations of components of the system and dose rates. Kinetic dependences of metallic palladium formation are obtained. Values of radiation-chemical yields of metallic palladium formation depending on the initial concentrations of palladium (2) and perchloric acid are given. A mechanism of radiolytic reduction of palladium (2) in the investigated system is suggested based on the experimental data, and a theoretical value of the radiation-chemical yield of palladium (2) reduction being in a good agreement with experimentally found values is calculated

Synthesis of different-sized silver nanoparticles by simply varying reaction conditions with leaf extracts of Bauhinia variegata L.

Science.gov (United States)

Kumar, V; Yadav, S K

2012-03-01

Green synthesis of nanoparticles is one of the crucial requirements in today's climate change scenario all over the world. In view of this, leaf extract (LE) of Bauhinia variegata L. possessing strong antidiabetic and antibacterial properties has been used to synthesise silver nanoparticles (SNP) in a controlled manner. Various-sized SNP (20-120 nm) were synthesised by varying incubation temperature, silver nitrate and LE concentrations. The rate of SNP synthesis and their size increased with increase in AgNO(3) concentration up to 4 mM. With increase in LE concentration, size and aggregation of SNP was increased. The size and aggregation of SNP were also increased at temperatures above and below 40°C. This has suggested that size and dispersion of SNP can be controlled by varying reaction components and conditions. Polarity-based fractionation of B. variegata LE has suggested that only water-soluble fraction is responsible for SNP synthesis. Fourier transform infrared spectroscopy analysis revealed the attachment of polyphenolic and carbohydrate moieties to SNP. The synthesised SNPs were found stable in double distilled water, BSA and phosphate buffer (pH 7.4). On the contrary, incubation of SNP with NaCl induced aggregation. This suggests the safe use of SNP for various in vivo applications.

Photochemical Study of Silver Nanoparticles Formed from the Reduction of Silver Ions by Humic Acid

Science.gov (United States)

Leslie, Renee M.

This study focuses on the ability of silver ions and humic acid to form silver nanoparticles in the presence of UV and visible light. Silver nanoparticles have a number of industrial applications due primarily to their antimicrobial properties, but these properties pose an environmental threat. Silver nanoparticles can directly disrupt sensitive ecosystems by harming bacteria. Consumption of silver nanoparticles results in silver ions and silver nanoparticles entering waterways; the presence of silver ions raises the question of whether nanoparticles can reform in environmental waters. As our data show, silver nanoparticles can form from the reduction of silver ions by humic acid after irradiation with UV and visible light. In order to better understand the mechanism of these naturally synthesized silver nanoparticles, we investigated the effects of reactant concentration, experimental conditions and presence of ions/reactive species. We monitored silver nanoparticle growth with UV-visible spectroscopy. The evolution in time of nanoparticle size was monitored by dynamic light scattering (DLS).

Synthesis of monodisperse palladium nanocubes and their catalytic activity for methanol electrooxidation

Science.gov (United States)

Ding, Hao; Shi, Xue-Zhao; Shen, Cheng-Min; Hui, Chao; Xu, Zhi-Chuan; Li, Chen; Tian, Yuan; Wang, Deng-Ke; Gao, Hong-Jun

2010-10-01

The single crystalline palladium nanocubes with an average size of 7 nm were prepared in the presence of poly (vinyl pyrrolidone) (PVP) and KBr using the polyol method. The as-prepared Pd nanocubes were highly uniform in both size and shape. The ordered packing structures including monolayer and multilayer can be fabricated via the rate-controlled evaporation of solution solvent. The electrochemical catalytic activity of these Pd nanocubes towards methanol oxidation was found to be higher than that of spherical Pd nanoparticles of similar size.

Complex conductivity response to silver nanoparticles in partially saturated sand columns

Science.gov (United States)

Abdel Aal, Gamal; Atekwana, Estella A.; Werkema, D. Dale

2017-02-01

The increase in the use of nanoscale materials in consumer products has resulted in a growing concern of their potential hazard to ecosystems and public health from their accidental or intentional introduction to the environment. Key environmental, health, and safety research needs include knowledge and methods for their detection, characterization, fate, and transport. Specifically, techniques available for the direct detection and quantification of their fate and transport in the environment are limited. Their small size, high surface area to volume ratio, interfacial, and electrical properties make metallic nanoparticles, such as silver nanoparticles, good targets for detection using electrical geophysical techniques. Here we measured the complex conductivity response to silver nanoparticles in sand columns under varying moisture conditions (0-30%), nanoparticle concentrations (0-10 mg/g), lithology (presence of clay), pore water salinity (0.0275 and 0.1000 S/m), and particle size (35, 90-210 and 1500-2500 nm). Based on the Cole-Cole relaxation models we obtained the chargeability and the time constant. We demonstrate that complex conductivity can detect silver nanoparticles in porous media with the response enhanced by higher concentrations of silver nanoparticles, moisture content, ionic strength, clay content and particle diameter. Quantification of the volumetric silver nanoparticles content in the porous media can also be obtained from complex conductivity parameters based on the strong power law relationships.

Converting a Natural Protein Compartment into a Nanofactory for the Size-Constrained Synthesis of Antimicrobial Silver Nanoparticles.

Science.gov (United States)

Giessen, Tobias W; Silver, Pamela A

2016-12-16

Engineered biological systems are used extensively for the production of high value and commodity organics. On the other hand, most inorganic nanomaterials are still synthesized via chemical routes. By engineering cellular compartments, functional nanoarchitectures can be produced under environmentally sustainable conditions. Encapsulins are a new class of microbial nanocompartments with promising applications in nanobiotechnology. Here, we engineer the Thermotoga maritima encapsulin EncTm to yield a designed compartment for the size-constrained synthesis of silver nanoparticles (Ag NPs). These Ag NPs exhibit uniform shape and size distributions as well as long-term stability. Ambient aqueous conditions can be used for Ag NP synthesis, while no reducing agents or solvents need to be added. The antimicrobial activity of the synthesized protein-coated or shell-free Ag NPs is superior to that of silver nitrate and citrate-capped Ag NPs. This study establishes encapsulins as an engineerable platform for the synthesis of biogenic functional nanomaterials.

76 FR 70667 - Small Business Size Standards: Educational Services

Science.gov (United States)

2011-11-15

... business assistance, SBA establishes small business size definitions (referred to as size standards) for... SMALL BUSINESS ADMINISTRATION 13 CFR Part 121 RIN 3245-AG29 Small Business Size Standards: Educational Services AGENCY: U.S. Small Business Administration. ACTION: Proposed rule. SUMMARY: The U.S...

Improved electroless plating method through ultrasonic spray atomization for depositing silver nanoparticles on multi-walled carbon nanotubes

Energy Technology Data Exchange (ETDEWEB)

Zhao, Qi [School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093 (China); Xie, Ming [Kunming Institute of Precious Metals, Kunming 650106 (China); Liu, Yichun, E-mail: liuyichun@kmust.edu.cn [School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093 (China); Yi, Jianhong [School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093 (China)

2017-07-01

Highlights: • Electroless plating method assisted by ultrasonic spray atomization was developed. • This method leads to much more uniform silver coatings on MWCNTs. • The plating parameters affect the layer morphologies a lot. - Abstract: A novel method was developed to deposit nanosized silver particles on multi-walled carbon nanotubes (MWCNTs). The electroless plating of silver on MWCNTs accomplished in small solution drops generated by ultrasonic spray atomization, which inhibited excessive growth of silver particles and led to much more uniform nanometer grain-sized coatings. The results showed that pretreatment was essential for silver particles to deposit on the MWCNTs, and the electrolyte concentration and reaction temperature were important parameters which had a great influence on the morphology and structure of the silver coatings. Possible mechanisms of this method are also discussed in the paper.

Improved electroless plating method through ultrasonic spray atomization for depositing silver nanoparticles on multi-walled carbon nanotubes

International Nuclear Information System (INIS)

Zhao, Qi; Xie, Ming; Liu, Yichun; Yi, Jianhong

2017-01-01

Highlights: • Electroless plating method assisted by ultrasonic spray atomization was developed. • This method leads to much more uniform silver coatings on MWCNTs. • The plating parameters affect the layer morphologies a lot. - Abstract: A novel method was developed to deposit nanosized silver particles on multi-walled carbon nanotubes (MWCNTs). The electroless plating of silver on MWCNTs accomplished in small solution drops generated by ultrasonic spray atomization, which inhibited excessive growth of silver particles and led to much more uniform nanometer grain-sized coatings. The results showed that pretreatment was essential for silver particles to deposit on the MWCNTs, and the electrolyte concentration and reaction temperature were important parameters which had a great influence on the morphology and structure of the silver coatings. Possible mechanisms of this method are also discussed in the paper.

Exposure to silver nanoparticles induces size- and dose-dependent oxidative stress and cytotoxicity in human colon carcinoma cells

DEFF Research Database (Denmark)

Miethling-Graff, Rona; Rumpker, Rita; Richter, Madeleine

2014-01-01

The antimicrobial properties of silver nanoparticles (AgNPs) have made these particles one of the most frequently utilized nanomaterials in consumer products; therefore, a comprehensive understanding of their toxicity is necessary. In particular, information about the cellular uptake and size...

[Morphological changes of the intestine in experimental acute intestinal infection in the treatment of colloidal silver].

Science.gov (United States)

Polov'ian, E S; Chemich, N D; Moskalenko, R A; Romaniuk, A N

2012-06-01

At the present stage of infectionist practice in the treatment of acute intestinal infections caused by opportunistic microorganisms, colloidal silver is used with a particle size of 25 nm as an alternative to conventional causal therapy. In 32 rats, distributed in 4 groups of 8 animals each (intact; healthy, got colloidal silver; with a modeled acute intestinal infection in the basic treatment and with the addition of colloidal silver), histological examination was performed of small and large intestine of rats. Oral administration of colloidal silver at a dose of 0.02 mg/day to intact rats did not lead to changes in morphometric parameters compared to the norm, and during early convalescence in rats with acute intestinal infections were observed destructive and compensatory changes in the intestine, which depended on the treatment regimen. With the introduction of colloidal silver decreased activity of the inflammatory process and the severity of morphological changes in tissues of small and large intestine, indicating that the positive effect of study drug compared with baseline therapy.

Franklin D. Roosevelt, Silver, and China.

OpenAIRE

Friedman, Milton

1992-01-01

The silver purchase program, initiated by Franklin Roosevelt in late 1933 in response to the economically small but politically potent silver bloc, gave a large short-run subsidy to silver producers at the cost of destroying any long-run monetary role for silver. More important, it imposed severe deflation on China, the only major country still on a silver standard, and forced it off the silver standard and on to a fiat standard, which brought forward in time and increased in severity the sub...

A simple approach to uniform PdAg alloy membranes: Comparative study of conventional and silver concentration-controlled co-plating

KAUST Repository

Zeng, Gaofeng

2014-03-01

An Ag-controlled co-plating method was developed for the preparation of palladium/silver alloy membranes on porous tubular alumina supports. By controlling the feed rate of Ag to the Pd bath, the concentration of the silver in the plating bath was restricted during the course of plating. As a result, preferential deposition of silver at the beginning was suppressed and uniform dispersion of silver inside the membrane with silver composition in the desired range was achieved. Ultrathin (∼2.5 μm) PdAg alloy membranes with uniform silver composition of ∼25% were successfully obtained. The membrane showed a hydrogen permeance of 0.88 mol m-2 s-1 and pure-gas H2/N2 selectivity of 2140 at 823 K with ΔP = 100 kPa. Only one hydride phase existed in the studied temperature range from 373 to 823 K with ΔPH=100kPa. Direct comparisons with the conventional simply-mixed co-plating method showed that membranes made by the novel Ag-controlled co-plating method had much more uniform silver distribution, smoother surface, denser membrane structure, higher utilization rate of metal sources, and shorter alloying time. © 2013, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.

A simple approach to uniform PdAg alloy membranes: Comparative study of conventional and silver concentration-controlled co-plating

KAUST Repository

Zeng, Gaofeng; Shi, Lei; Liu, Yunyang; Zhang, Yanfeng; Sun, Yuhan

2014-01-01

An Ag-controlled co-plating method was developed for the preparation of palladium/silver alloy membranes on porous tubular alumina supports. By controlling the feed rate of Ag to the Pd bath, the concentration of the silver in the plating bath was restricted during the course of plating. As a result, preferential deposition of silver at the beginning was suppressed and uniform dispersion of silver inside the membrane with silver composition in the desired range was achieved. Ultrathin (∼2.5 μm) PdAg alloy membranes with uniform silver composition of ∼25% were successfully obtained. The membrane showed a hydrogen permeance of 0.88 mol m-2 s-1 and pure-gas H2/N2 selectivity of 2140 at 823 K with ΔP = 100 kPa. Only one hydride phase existed in the studied temperature range from 373 to 823 K with ΔPH=100kPa. Direct comparisons with the conventional simply-mixed co-plating method showed that membranes made by the novel Ag-controlled co-plating method had much more uniform silver distribution, smoother surface, denser membrane structure, higher utilization rate of metal sources, and shorter alloying time. © 2013, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.

Palladium Nanoparticle Hydrogen Sensor

Directory of Open Access Journals (Sweden)

I. Pavlovsky

2006-12-01

Full Text Available An innovative hydrogen sensor based on palladium (Pd nanoparticle networks is described in the article. Made by Applied Nanotech Inc. sensor has a fast response time, in the range of seconds, which is increased at 80 °C due to higher hydrogen diffusion rates into the palladium lattice. The low detection limit of the sensor is 10 ppm of H2, and the high limit is 40,000 ppm. This is 100% of a lowest flammability level of hydrogen. This range of sensitivities complies with the requirements that one would expect for a reliable hydrogen sensor.

Silver-zinc: status of technology and applications

Energy Technology Data Exchange (ETDEWEB)

Karpinski, A.P.; Makovetski, B.; Russell, S.J.; Serenyi, J.R.; Williams, D.C. [Yardney Technical Products, Pawcatuck, CT (United States)

1999-07-01

available in small cylindrical cells) and lack of an established data base. In spite of the advantages noted for the popular secondary systems, the silver-zinc couple still is the system of choice where high specific energy/energy density, coupled with high specific power/power density are important for high-rate, weight or size-sensitive applications. In the 1950s, Yardney developed the first practical rechargeable silver-zinc cell for an underwater application. The U.S. Navy, recognizing the potential of this system for torpedo propulsion, soon adopted it to power the majority of its electric torpedoes - increasing their speed and range, and allowing more room for increasing the performance capability of the torpedo. One of the first programmes which adopted the silver-zinc technology was the MK58 or `Brush` torpedo which consisted of 44 A h cells. At that time, silver-zinc batteries became the preferred system for many other applications. Some of the unique systems include the largest silver-zinc battery ever made, a 256-ton battery for the Albacore G-5 submarine. This battery consisted of a two-section, two-hundred-and-eighty-cell battery, with each cell rated at 20,000 A h. Each cell was essentially the size of a standard four-drawer filing cabinet. Since that time, many of the silver-zinc applications have considerably scaled down their power requirements. Underwater applications are consistently using the larger sized batteries while the smallest are typically found in missile applications. This paper will describe some of the current activities in addressing the major components of the cell and a summary of the current applications of the silver-zinc system. (orig.)

The biosynthesis of palladium nanoparticles by antioxidants in Gardenia jasminoides Ellis: long lifetime nanocatalysts for p-nitrotoluene hydrogenation

Energy Technology Data Exchange (ETDEWEB)

Jia Lishan; Zhang Qian; Li Qingbiao; Song Hao, E-mail: jials@xmu.edu.c [Department of Chemical and Biochemical Engineering, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005 (China); Key Laboratory for Chemistry and Biochemical Engineering, Department of Chemical and Biochemical Engineering, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005 (China); Key Laboratory for Chemical Biology of Fujian Province, Xiamen University, Xiamen 361005 (China)

2009-09-23

Gardenia jasminoides Ellis' water crude extract was used for the bioreduction of palladium chloride in this paper. The UV-vis spectrum, x-ray diffraction spectrum measurement, the Fourier transform infrared spectroscopy and TEM technique confirmed the formation of palladium nanoparticles and identified antioxidants including geniposide, chlorogenic acid, crocins and crocetin were reducing and stabilizing agents for synthesizing palladium nanoparticles in water crude extract. The particle size and dispersity were temperature-dependent. The particle sizes ranged from 3 to 5 nm and revealed the best dispersity at 70 {sup 0}C. Catalytic performance of the biosynthetic Pd nanoparticles with good dispersity was investigated by hydrogenation of p-nitrotoluene. The catalysts showed a conversion of 100% under conditions of 5 MPa, 150 {sup 0}C for 2 h. The selectivity of p-methyl-cyclohexylamine achieved 26.3%. The catalyst was recycled five times with no agglomeration and maintained activity, which was attributed to the appropriate protection of the antioxidants. On the basis of the study, it appears to be a new promising biosynthetic nanocatalyst for the development of an industrial process.

The biosynthesis of palladium nanoparticles by antioxidants in Gardenia jasminoides Ellis: long lifetime nanocatalysts for p-nitrotoluene hydrogenation

Science.gov (United States)

Jia, Lishan; Zhang, Qian; Li, Qingbiao; Song, Hao

2009-09-01

Gardenia jasminoides Ellis' water crude extract was used for the bioreduction of palladium chloride in this paper. The UV-vis spectrum, x-ray diffraction spectrum measurement, the Fourier transform infrared spectroscopy and TEM technique confirmed the formation of palladium nanoparticles and identified antioxidants including geniposide, chlorogenic acid, crocins and crocetin were reducing and stabilizing agents for synthesizing palladium nanoparticles in water crude extract. The particle size and dispersity were temperature-dependent. The particle sizes ranged from 3 to 5 nm and revealed the best dispersity at 70 °C. Catalytic performance of the biosynthetic Pd nanoparticles with good dispersity was investigated by hydrogenation of p-nitrotoluene. The catalysts showed a conversion of 100% under conditions of 5 MPa, 150 °C for 2 h. The selectivity of p-methyl-cyclohexylamine achieved 26.3%. The catalyst was recycled five times with no agglomeration and maintained activity, which was attributed to the appropriate protection of the antioxidants. On the basis of the study, it appears to be a new promising biosynthetic nanocatalyst for the development of an industrial process.

Processing Tritiated Water at the Savannah River Site: A Production-Scale Demonstration of a palladium membrane reactor

International Nuclear Information System (INIS)

Sessions, K

2004-01-01

The Palladium Membrane Reactor (PMR) process was installed in the Tritium Facilities at the Savannah River Site to perform a production-scale demonstration for the recovery of tritium from tritiated water adsorbed on molecular sieve (zeolite). Unlike the current recovery process that utilizes magnesium, the PMR offers a means to process tritiated water in a more cost effective and environmentally friendly manner. The design and installation of the large-scale PMR process was part of a collaborative effort between the Savannah River Site and Los Alamos National Laboratory. The PMR process operated at the Savannah River Site between May 2001 and April 2003. During the initial phase of operation the PMR processed thirty-four kilograms of tritiated water from the Princeton Plasma Physics Laboratory. The water was processed in fifteen separate batches to yield approximately 34,400 liters (STP) of hydrogen isotopes. Each batch consisted of round-the-clock operations for approximately nine days. In April 2003 the reactor's palladium-silver membrane ruptured resulting in the shutdown of the PMR process. Reactor performance, process performance and operating experiences have been evaluated and documented. A performance comparison between PMR and current magnesium process is also documented

Synthesis of monodisperse palladium nanocubes and their catalytic activity for methanol electrooxidation

International Nuclear Information System (INIS)

Hao, Ding; Xue-Zhao, Shi; Cheng-Min, Shen; Chao, Hui; Zhi-Chuan, Xu; Chen, Li; Yuan, Tian; Deng-Ke, Wang; Hong-Jun, Gao

2010-01-01

The single crystalline palladium nanocubes with an average size of 7 nm were prepared in the presence of poly (vinyl pyrrolidone) (PVP) and KBr using the polyol method. The as-prepared Pd nanocubes were highly uniform in both size and shape. The ordered packing structures including monolayer and multilayer can be fabricated via the rate-controlled evaporation of solution solvent. The electrochemical catalytic activity of these Pd nanocubes towards methanol oxidation was found to be higher than that of spherical Pd nanoparticles of similar size. (condensed matter: structure, thermal and mechanical properties)

Hydrothermal-induced assembly of colloidal silver spheres into various nanoparticles on the basis of HTAB-modified silver mirror reaction.

Science.gov (United States)

Yu, Dabin; Yam, Vivian Wing-Wah

2005-03-31

Small colloidal silver spheres (diameter synthesis process. Adjustment of the synthesis parameters, in particular the concentrations of HTAB and [Ag(NH3)2]+, led to an obvious shape evolution of silver nanoparticles, thus resulting in the shape-selective formation of the silver nanoparticles. The monodisperse nanocubes with a well-defined crystallographical structure (a single crystal bounded by six {200} facets) have a strong tendency to assemble into two-dimensional arrays on substrates. The nanowires with uniform diameter usually existed in the form of two-dimensional alignments. The findings suggested that hydrothermal-induced assembly of small silver colloidal particles should be a convenient and effective approach to the preparation of various silver nanoparticles.

A high sensitivity SQUID-method for the measurement of magnetic susceptibility of small samples in the temperature range 1.5 K-40 K and application on small palladium particles

International Nuclear Information System (INIS)

Tu Nguyen Quang.

1979-01-01

In this paper a method is developed for magnetic susceptibility measurements which is superior to the common methods. The method is based on the SQUID-principle (Superconducting Quantum Interference Device) using the tunnel effect of a superconducting point contact and magnetic flux quantization for measuring electric and magnetic quantities. Due to this refined method susceptibility changes of very small palladium particles could be detected in the temperature range 1.5 K-40 K with respect to the bulk. In addition susceptibility differences of particle distributions with different means diameters (81 Angstroem and 65 Angstroem) have been measured for the first time. A quantitative comparison of the measurements with theoretical results shows satisfactory agreement. (orig./WBU) [de

Moderating effect of ammonia on particle growth and stability of quasi-monodisperse silver nanoparticles synthesized by the Turkevich method.

Science.gov (United States)

Gorup, Luiz F; Longo, Elson; Leite, Edson R; Camargo, Emerson R

2011-08-15

A new method to stabilize silver nanoparticles by the addition of ammonia is proposed. Colloidal dispersions of silver nanoparticles were synthesized by the Turkevich method using sodium citrate to reduce silver nitrate at high pH and at 90 °C. After approximately 12 min, a diluted ammonia solution was added to the reaction flask to form soluble diamine silver (I) complexes that played an important growth moderating role, making it possible to stabilize metallic silver nanoparticles with sizes as small as 1.6 nm after 17 min of reaction. Colloidal dispersions were characterized by UV-visible absorption spectroscopy, X-ray diffraction, and transmission electronic microscopy. Copyright © 2011 Elsevier Inc. All rights reserved.

77 FR 28520 - Small Business Size Regulations, Small Business Innovation Research (SBIR) Program and Small...

Science.gov (United States)

2012-05-15

... SMALL BUSINESS ADMINISTRATION 13 CFR Part 121 RIN 3245-AG46 Small Business Size Regulations, Small Business Innovation Research (SBIR) Program and Small Business Technology Transfer (STTR) Program AGENCY: Small Business Administration. ACTION: Proposed rule. SUMMARY: The U.S. Small Business Administration...

Synthesis and Bactericidal Properties of Hyaluronic Acid Doped with Metal Nanoparticles

Directory of Open Access Journals (Sweden)

Galo Cárdenas-Triviño

2017-01-01

Full Text Available A study on the nanoparticles size and the antibacterial properties of hyaluronic acid (HA doped with nanoparticles is reported. Nanoparticles from gold, silver, copper, and silver palladium with HA support were performed. The solvated metal atom dispersion (SMAD method with 2-propanol and HA was used. High-resolution transmission electron microscopy (HRTEM, infrared spectroscopy (FT-IR, and thermogravimetric analysis (TGA were conducted. The average sizes of nanoclusters were as follows: HA-Au = 17.88 nm; HA-Ag = 50.41 nm; HA-Cu = 13.33 nm; and HA-AgPd = 33.22 nm. The antibacterial activity of solutions and films containing nanoparticles against American Type Culture Collection (ATCC bacterial strains Escherichia coli (EC, Staphylococcus aureus (SA, Staphylococcus epidermidis (SE, and Pseudomonas aeruginosa (PA was determined. Inhibition was observed for HA-Ag, HA-Cu, and HA-AgPd. Toxicological tests were performed in rats that were injected intraperitoneally with two concentrations of gold, copper, silver, and silver-palladium nanoparticles. No alterations in hepatic parameters, including ALT (alanine aminotransferase, GGT (gamma-glutamyl transpeptidase bilirubin, and albumin, were observed after 14 days. These films could be used as promoters of skin recovery and Grades I and II cutaneous burns and as scaffolds.

Silver powder effectiveness and mechanism of silver paste on silicon solar cells

International Nuclear Information System (INIS)

Tsai, Jung-Ting; Lin, Shun-Tian

2013-01-01

Highlights: ► Optimizing the silver paste in 80–85 wt.%. ► Optimizing its particle size in 1–1.5 μm spherical powder. ► The sheet resistance is 4 mΩ/sq during the 860 °C sintering process. ► Redox reaction cause Ag crystallites to grow on the interface. ► A thin layer of silicon oxide (75–150 nm) was formed. - Abstract: Since the silver paste plays a major role in the mass production of silicon solar cells, this work has succeeded in optimizing the silver paste in 80–85 wt.% and optimizing its particle size in 1–1.5 μm spherical powder. As the firing temperature is increased, the growth trend of silver grain is improved. The result of this work has showed that the lowest sheet resistance is 4 mΩ/sq during the 860 °C sintering process. The scanning electron microscope (SEM) observation has showed that the formation of silver oxide is formed during the melting process of glass and triggered redox reaction of Ag crystallites to grow on the interface. It has proven by transmission electron microscope (TEM) that a thin layer of silicon oxide (75–150 nm) was formed, respectively.

Antimicrobial effects of silver zeolite, silver zirconium phosphate silicate and silver zirconium phosphate against oral microorganisms

Institute of Scientific and Technical Information of China (English)

Sirikamon Saengmee-anupharb; Toemsak Srikhirin; Boonyanit Thaweboon; Sroisiri Thaweboon; Taweechai Amornsakchai; Surachai Dechkunakorn; Theeralaksna Suddhasthira

2013-01-01

Objective: To evaluate the antimicrobial activities of silver inorganic materials, including silver zeolite (AgZ), silver zirconium phosphate silicate (AgZrPSi) and silver zirconium phosphate (AgZrP), against oral microorganisms. In line with this objective, the morphology and structure of each type of silver based powders were also investigated. Methods: The antimicrobial activities of AgZ, AgZrPSi and AgZrP were tested against Streptococcus mutans, Lactobacillus casei, Candidaalbicans and Staphylococcus aureus using disk diffusion assay as a screening test. The minimum inhibitory concentration (MIC) and minimum lethal concentration (MLC) were determined using the modified membrane method. Scanning electron microscope and X-ray diffraction were used to investigate the morphology and structure of these silver materials. Results: All forms of silver inorganic materials could inhibit the growth of all test microorganisms. The MIC of AgZ, AgZrPSi and AgZrP was 10.0 g/L whereas MLC ranged between 10.0-60.0 g/L. In terms of morphology and structure, AgZrPSi and AgZrP had smaller sized particles (1.5-3.0 µm) and more uniformly shaped than AgZ. Conclusions: Silver inorganic materials in the form of AgZ, AgZrPSi and AgZrP had antimicrobial effects against all test oral microorganisms and those activities may be influenced by the crystal structure of carriers. These results suggest that these silver materials may be useful metals applied to oral hygiene products to provide antimicrobial activity against oral infection.

Antimicrobial effects of silver zeolite,silver zirconium phosphate silicate and silver zirconium phosphate against oral microorganisms

Institute of Scientific and Technical Information of China (English)

Sirikamon; Saengmee-anupharb; Toemsak; Srikhirin; Boonyanit; Thaweboon; Sroisiri; Thaweboon; Taweechai; Amornsakchai; Surachai; Dechkunakorn; Theeralaksna; Suddhasthira

2013-01-01

Objective:To evaluate the antimicrobial activities of silver inorganic materials,including silver zeolite(AgZ),silver zirconium phosphate silicate(AgZrPSi)and silver zirconium phosphate(AgZrp),against oral microorganisms.In line with this objective,the morphology and structure of each type of silver based powders were also investigated.Methods:The antimicrobial activities of AgZ,AgZrPSi and AgZrP were tested against Streptococcus mutans,Lactobacillus casei,Candida albicans and Staphylococcus aureus using disk diffusion assay as a screening test.The minimum inhibitory concentration(MIC)and minimum lethal concentration(MLC)were determined using the modified membrane method.Scanning electron microscope and X-ray diffraction were used to investigate the morphology and structure of these silver materials.Results:All forms of silver inorganic materials could inhibit the growth of all test microorganisms.The MIC of AgZ,AgZrPSi and AgZrP was 10.0 g/L whereas MLC ranged between 10.0-60.0 g/L.In terms of morphology and structure.AgZrPSi and AgZrP had smaller sized particles(1.5-3.0μm)and more uniformly shaped than AgZ.Conclusions:Silver inorganic materials in the form of AgZ,AgZrPSi and AgZrP had antimicrobial effects against all test oral microorganisms and those activities may be influenced by the crystal structure of carriers.These results suggest that these silver materials may be useful metals applied to oral hygiene products to provide antimicrobial activity against oral infection.

Synthesis and antimicrobial effects of silver nanoparticles

Directory of Open Access Journals (Sweden)

S kheybari

2010-09-01

Full Text Available "n  "n "nBackground and the purpose of the study:The most prominent nanoparticles for medical uses are nanosilver particles which are famous for their high anti-microbial activity. Silver ion has been known as a metal ion that exhibit anti-mold, anti-microbial and anti-algal properties for a long time. In particular, it is widely used as silver nitrate aqueous solution which has disinfecting and sterilizing actions. The purpose of this study was to evaluate the antimicrobial activity as well as physical properties of the silver nanoparticles prepared by chemical reduction method. "nMethods:Silver nanoparticles (NPs were prepared by reduction of silver nitrate in the presence of a reducing agent and also poly [N-vinylpyrolidone] (PVP as a stabilizer. Two kinds of NPs were synthesized by ethylene glycol (EG and glucose as reducing agent. The nanostructure and particle size of silver NPs were confirmed by scanning electron microscopy (SEM and laser particle analyzer (LPA. The formations of the silver NPs were monitored using ultraviolet-visible spectroscopy. The anti-bacterial activity of silver NPs were assessed by determination of their minimum inhibitory concentrations (MIC against the Gram positive (Staphylococcus aureus and Staphylococcus epidermidis as well as Gram-negative (Escherichia coli and Pseudomonas aeruginosa bacteria. "nResults and Conclusion:The silver nanoparticles were spherical with particle size between 10 to 250 nm. Analysis of the theoretical (Mie light scattering theory and experimental results showed that the silver NPs in colloidal solution had a diameter of approximately 50 nm. "nBoth colloidal silver NPs showed high anti-bacterial activity against Gram positive and Gram negative bacteria. Glucose nanosilver colloids showed a shorter killing time against most of the tested bacteria which could be due to their nanostructures and uniform size distribution patterns.

Hydrogen Production via Steam Reforming of Ethyl Alcohol over Palladium/Indium Oxide Catalyst

Directory of Open Access Journals (Sweden)

Tetsuo Umegaki

2009-01-01

Full Text Available We report the synergetic effect between palladium and indium oxide on hydrogen production in the steam reforming reaction of ethyl alcohol. The palladium/indium oxide catalyst shows higher hydrogen production rate than indium oxide and palladium. Palladium/indium oxide affords ketonization of ethyl alcohol with negligible by-product carbon monoxide, while indium oxide mainly affords dehydration of ethyl alcohol, and palladium affords decomposition of ethyl alcohol with large amount of by-product carbon monoxide. The catalytic feature of palladium/indium oxide can be ascribed to the formation of palladium-indium intermetallic component during the reaction as confirmed by X-ray diffraction and X-ray photoelectron spectroscopic measurements.

The potent antimicrobial properties of cell penetrating peptide-conjugated silver nanoparticles with excellent selectivity for gram-positive bacteria over erythrocytes.

Science.gov (United States)

Liu, Lihong; Yang, Jun; Xie, Jianping; Luo, Zhentao; Jiang, Jiang; Yang, Yi Yan; Liu, Shaomin

2013-05-07

Silver nanoparticles are of great interest for use as antimicrobial agents. Studies aimed at producing potent nano-silver biocides have focused on manipulation of particle size, shape, composition and surface charge. Here, we report the cell penetrating peptide catalyzed formation of antimicrobial silver nanoparticles in N,N-dimethylformamide. The novel nano-composite demonstrated a distinctly enhanced biocidal effect toward bacteria (gram-positive Bacillus subtilis, gram-negative Escherichia coli) and pathogenic yeast (Candida albicans), as compared to triangular and extremely small silver nanoparticles. In addition, a satisfactory biocompatibility was verified by a haemolysis test. Our results provide a paradigm in developing strategies that can maximize the silver nanoparticle application potentials while minimizing the toxic effects.

The Effect of Silver Nanoparticles Size, Produced Using Plant Extract from Arbutus unedo, on Their Antibacterial Efficacy

Directory of Open Access Journals (Sweden)

Nicholas Skandalis

2017-07-01

Full Text Available Silver nanoparticles (AgNPs have been demonstrated to restrain bacterial growth, while maintaining minimal risk in development of bacterial resistance and human cell toxicity that conventional silver compounds exhibit. Several physical and chemical methods have been reported to synthesize AgNPs. However, these methods are expensive and involve heavy chemical reduction agents. An alternative approach to produce AgNPs in a cost-effective and environmentally friendly way employs a biological pathway using various plant extracts to reduce metal ions. The size control issue, and the stability of nanoparticles, remain some of the latest challenges in such methods. In this study, we used two different concentrations of fresh leaf extract of the plant Arbutus unedo (LEA as a reducing and stabilizing agent to produce two size variations of AgNPs. UV-Vis spectroscopy, Dynamic Light Scattering, Transmission Electron Microscopy, and zeta potential were applied for the characterization of AgNPs. Both AgNP variations were evaluated for their antibacterial efficacy against the gram-negative species Escherichia coli and Pseudomonas aeruginosa, as well as the gram-positive species Bacillus subtilis and Staphylococcus epidermidis. Although significant differences have been achieved in the nanoparticles’ size by varying the plant extract concentration during synthesis, the antibacterial effect was almost the same.

The Effect of Silver Nanoparticles Size, Produced Using Plant Extract from Arbutus unedo, on Their Antibacterial Efficacy.

Science.gov (United States)

Skandalis, Nicholas; Dimopoulou, Anastasia; Georgopoulou, Anthie; Gallios, Nikolaos; Papadopoulos, Dimitrios; Tsipas, Dimitrios; Theologidis, Ioannis; Michailidis, Nikolaos; Chatzinikolaidou, Maria

2017-07-10

Silver nanoparticles (AgNPs) have been demonstrated to restrain bacterial growth, while maintaining minimal risk in development of bacterial resistance and human cell toxicity that conventional silver compounds exhibit. Several physical and chemical methods have been reported to synthesize AgNPs. However, these methods are expensive and involve heavy chemical reduction agents. An alternative approach to produce AgNPs in a cost-effective and environmentally friendly way employs a biological pathway using various plant extracts to reduce metal ions. The size control issue, and the stability of nanoparticles, remain some of the latest challenges in such methods. In this study, we used two different concentrations of fresh leaf extract of the plant Arbutus unedo (LEA) as a reducing and stabilizing agent to produce two size variations of AgNPs. UV-Vis spectroscopy, Dynamic Light Scattering, Transmission Electron Microscopy, and zeta potential were applied for the characterization of AgNPs. Both AgNP variations were evaluated for their antibacterial efficacy against the gram-negative species Escherichia coli and Pseudomonas aeruginosa , as well as the gram-positive species Bacillus subtilis and Staphylococcus epidermidis . Although significant differences have been achieved in the nanoparticles' size by varying the plant extract concentration during synthesis, the antibacterial effect was almost the same.

Combined biocidal action of silver nanoparticles and ions against Chlorococcales (Scenedesmus quadricauda, Chlorella vulgaris) and filamentous algae (Klebsormidium sp.).

Science.gov (United States)

Zouzelka, Radek; Cihakova, Pavlina; Rihova Ambrozova, Jana; Rathousky, Jiri

2016-05-01

Despite the extensive research, the mechanism of the antimicrobial and biocidal performance of silver nanoparticles has not been unequivocally elucidated yet. Our study was aimed at the investigation of the ability of silver nanoparticles to suppress the growth of three types of algae colonizing the wetted surfaces or submerged objects and the mechanism of their action. Silver nanoparticles exhibited a substantial toxicity towards Chlorococcales Scenedesmus quadricauda, Chlorella vulgaris, and filamentous algae Klebsormidium sp., which correlated with their particle size. The particles had very good stability against agglomeration even in the presence of multivalent cations. The concentration of silver ions in equilibrium with nanoparticles markedly depended on the particle size, achieving about 6 % and as low as about 0.1 % or even less for the particles 5 nm in size and for larger ones (40-70 nm), respectively. Even very limited proportion of small particles together with larger ones could substantially increase concentration of Ag ions in solution. The highest toxicity was found for the 5-nm-sized particles, being the smallest ones in this study. Their toxicity was even higher than that of silver ions at the same silver concentration. When compared as a function of the Ag(+) concentration in equilibrium with 5-nm particles, the toxicity of ions was at least 17 times higher than that obtained by dissolving silver nitrite (if not taking into account the effect of nanoparticles themselves). The mechanism of the toxicity of silver nanoparticles was found complex with an important role played by the adsorption of silver nanoparticles and the ions released from the particles on the cell surface. This mechanism could be described as some sort of synergy between nanoparticles and ions. While our study clearly showed the presence of this synergy, its detailed explanation is experimentally highly demanding, requiring a close cooperation between materials scientists

77 FR 39385 - Receipts-Based, Small Business Size Standard

Science.gov (United States)

2012-07-03

.... The NRC is increasing its receipts-based, small business size standard from $6.5 million to $7 million...-based, small business size standard increasing from $6.5 million to $7.0 million. This adjustment is to... regulatory programs. The NRC is increasing its receipts-based, small business size standard from $6.5 million...

76 FR 69154 - Small Business Size and Status Integrity

Science.gov (United States)

2011-11-08

... SMALL BUSINESS ADMINISTRATION 13 CFR Parts 121, 124, 125, 126, and 127 RIN 3245-AG23 Small Business Size and Status Integrity AGENCY: U.S. Small Business Administration (SBA). ACTION: Proposed rule... implement provisions of the Small Business Jobs Act of 2010 (Jobs Act) pertaining to small business size and...

Fabrication of palladium-based microelectronic devices by microcontact printing

International Nuclear Information System (INIS)

Wolfe, Daniel B.; Love, J. Christopher; Paul, Kateri E.; Chabinyc, Michael L.; Whitesides, George M.

2002-01-01

This letter demonstrates the patterning of thin films of metallic palladium by microcontact printing (μCP) of octadecanethiol, and the use of the patterned films in the fabrication of a functional sensor. This technique was also used to prepare templates of palladium for the electroless deposition of copper. The resistivity of the palladium and copper microstructures was 13.8 and 2.8 μΩ cm, respectively; these values are approximately 40% larger than the values for the pure bulk metals. Palladium patterned into serpentine wires using μCP functioned as a hydrogen sensor with sensitivity of 0.03 vol % H 2 in N 2 , and a response time of ∼10 s (at room temperature)

Phytotoxicity of silver nanoparticles to Lemna minor L

Energy Technology Data Exchange (ETDEWEB)

Gubbins, Eva J. [Department of Geography and Environmental Science, University of Birmingham, Edgbaston, Birmingham, B15 2TT (United Kingdom); Batty, Lesley C., E-mail: l.c.batty@bham.ac.uk [Department of Geography and Environmental Science, University of Birmingham, Edgbaston, Birmingham, B15 2TT (United Kingdom); Lead, Jamie R. [Department of Geography and Environmental Science, University of Birmingham, Edgbaston, Birmingham, B15 2TT (United Kingdom)

2011-06-15

The use of silver nanoparticles (AgNPs) in commercial products has increased significantly in recent years. Although there has been some attempt to determine the toxic effects of AgNPs, there is little information on aquatic plants which have a vital role in ecosystems. This study reports the use of Lemna minor L. clone St to investigate the phytotoxicity of AgNPs under modified OECD test conditions. AgNPs were synthesised, characterised and subsequently presented to the L. minor. Results showed that inhibition of plant growth was evident after exposure to small ({approx}20 nm) and larger ({approx}100 nm) AgNPs at low concentrations (5 {mu}g L{sup -1}) and this effect became more acute with a longer exposure time. There was a linear dose-response relationship after 14 d exposure. Using predicted environmental concentrations for wastewaters it was found that AgNPs may pose a significant potential risk to the environment. - Highlights: > Silver nanoparticles are toxic to Lemna minor at concentrations of 5 {mu}g L{sup -1}. > The effect of silver nanoparticles varies with size and concentration. > Standard toxicity tests are not appropriate for application to NPs. > Silver nanoparticles pose a potential environmental risk based on modelled environmental concentrations. - Silver nanoparticles are toxic to Lemna minor at low concentrations and constitute a significant environmental risk.

Phytotoxicity of silver nanoparticles to Lemna minor L

International Nuclear Information System (INIS)

Gubbins, Eva J.; Batty, Lesley C.; Lead, Jamie R.

2011-01-01

The use of silver nanoparticles (AgNPs) in commercial products has increased significantly in recent years. Although there has been some attempt to determine the toxic effects of AgNPs, there is little information on aquatic plants which have a vital role in ecosystems. This study reports the use of Lemna minor L. clone St to investigate the phytotoxicity of AgNPs under modified OECD test conditions. AgNPs were synthesised, characterised and subsequently presented to the L. minor. Results showed that inhibition of plant growth was evident after exposure to small (∼20 nm) and larger (∼100 nm) AgNPs at low concentrations (5 μg L -1 ) and this effect became more acute with a longer exposure time. There was a linear dose-response relationship after 14 d exposure. Using predicted environmental concentrations for wastewaters it was found that AgNPs may pose a significant potential risk to the environment. - Highlights: → Silver nanoparticles are toxic to Lemna minor at concentrations of 5 μg L -1 . → The effect of silver nanoparticles varies with size and concentration. → Standard toxicity tests are not appropriate for application to NPs. → Silver nanoparticles pose a potential environmental risk based on modelled environmental concentrations. - Silver nanoparticles are toxic to Lemna minor at low concentrations and constitute a significant environmental risk.

The determination, by atomic-absorption spectrophotometry using electrothermal atomization, of platinum, palladium, rhodium, ruthenium, and iridium

International Nuclear Information System (INIS)

Haines, J.; Robert, R.V.D.

1982-01-01

A method that involves measurement by atomic-absorption spectrophotometry using electrothermal atomization has been developed for the determination of trace quantities of platinum, palladium, rhodium, ruthenium, and iridium in mineralogical samples. The elements are separated and concentrated by fusion, nickel sulphide being used as the collector, and the analyte elements are measured in the resulting acid solution. An organic extraction procedure was found to offer no advantages over the proposed method. Mutual interferences between the five platinum-group metals examined, as well as interferences from gold, silver, and nickel were determined. The accuracy of the measurement was established by the analysis of a platinum-ore reference material. The lower limits of determination of each of the analyte elements in a sample material are as follows: platinum 1,6μg/l, palladium 0,2μg/1, rhodium 0,5μg/l, ruthenium 3μg/l, and iridium 2,5μg/l. The relative standard deviations range from 0,05 for rhodium to 0.08 for iridium. The method, which is described in detail in the Appendix, is applicable to the determination of these elements in ores, tailings, and geological materials in which the total concentration of the noble metals is less than 1g/t

Silver nanoparticles: Synthesis methods, bio-applications and properties.

Science.gov (United States)

Abbasi, Elham; Milani, Morteza; Fekri Aval, Sedigheh; Kouhi, Mohammad; Akbarzadeh, Abolfazl; Tayefi Nasrabadi, Hamid; Nikasa, Parisa; Joo, San Woo; Hanifehpour, Younes; Nejati-Koshki, Kazem; Samiei, Mohammad

2016-01-01

Silver nanoparticles size makes wide range of new applications in various fields of industry. Synthesis of noble metal nanoparticles for applications such as catalysis, electronics, optics, environmental and biotechnology is an area of constant interest. Two main methods for Silver nanoparticles are the physical and chemical methods. The problem with these methods is absorption of toxic substances onto them. Green synthesis approaches overcome this limitation. Silver nanoparticles size makes wide range of new applications in various fields of industry. This article summarizes exclusively scalable techniques and focuses on strengths, respectively, limitations with respect to the biomedical applicability and regulatory requirements concerning silver nanoparticles.

Small-size low-temperature scanning tunnel microscope

International Nuclear Information System (INIS)

Al'tfeder, I.B.; Khajkin, M.S.

1989-01-01

A small-size scanning tunnel microscope, designed for operation in transport helium-filled Dewar flasks is described. The microscope design contains a device moving the pin to the tested sample surface and a piezoelectric fine positioning device. High vibration protection of the microscope is provided by its suspension using silk threads. The small-size scanning tunnel microscope provides for atomic resolution

Surface Modification, Characterization and Photocatalytic Performance of Nano-Sized Titania Modified with Silver and Bentonite Clay

Directory of Open Access Journals (Sweden)

Neetu Divya

2009-12-01

Full Text Available In many textile industries dyes are used as coloring agents. Advanced oxidation processes are used for degrading or removing color from dye baths. Catalysts play a key role in these industries for the treatment of water. Solid catalysts are usually composed of metals that form supports onto the surface and create metal particles with high surface areas. TiO2 composites containing transition metal ions (silver and/or bentonite clay were prepared. Photocatalytic efficiencies have been investigated for the degradation of Orange G an azo dye. Various analytical techniques were used to characterize the surface properties of nano-sized titania modified using silver and/or bentonite clay. Scanning electron microscopy (SEM, Transmission electron microscopy (TEM, X-ray diffraction (XRD and FTIR analyses showed that TiO2 (10 ± 2 nm and Ag (2 to 3 nm particles were supported on the surface of the bentonite clay and the size was in the range of 100 ± 2 nm. The modified catalysts P-25 TiO2/Bentonite/Ag and P-25 TiO2/Ag were found to be very active for the photocatalytic decomposition of Orange G. The percent decolorization in 60 min was 98% with both P-25 TiO2/Ag and P-25 TiO2/Bentonite/Ag modified catalysts. Whereas mineralization achieved in 9 hr were 68% and 71% with P-25 TiO2/Bentonite/Ag and P-25 TiO2/Ag catalyst respectively. © 2009 BCREC UNDIP. All rights reserved[Received: 30 October 2009, Revised: 20 November 2009, Accepted: 21 November 2009][How to Cite: N. Divya, A. Bansal, A. K. Jana. (2009. Surface Modification, Characterization and Photocatalytic Performance of Nano-Sized Titania Modified with Silver and Bentonite Clay. Bulletin of Chemical Reaction Engineering and Catalysis, 4(2: 43-53.  doi:10.9767/bcrec.4.2.1249.43-53][How to Link/ DOI: http://dx.doi.org/10.9767/bcrec.4.2.1249.43-53 || or local: http://ejournal.undip.ac.id/index.php/bcrec/article/view/1249

Palladium alloy membrane process for the treatment of hydrogen isotopes

Energy Technology Data Exchange (ETDEWEB)

Chung, Hongsuk; Paek, Seungwoo; Lee, Minsoo; Kim, Kwangrag; Yim, Sungpaal; Ahn, Dohee [KAERI, Daejeon (Korea, Republic of); Shim, Myunghwa [Univ. of Science and Technology, Daejeon (Korea, Republic of)

2005-11-15

Tritium is a radioactive isotope of hydrogen and it has a half-life of 12.3 years; it decays to He-3 by emitting a low energy beta radiation with an average energy of 5.7 keV and a maximum energy of 18.6 keV. Transfer of environmentally tritiated water to humans takes place via an inhalation, diffusion through the skin and ingestion. Radioactive waste containing tritium is continuously generated by the nuclear industry in, for example, nuclear reactor operations and a radioisotope production, as well as in medical research. Methods for removing tritium from liquid waste provide an alternative to the control of tritium emissions and a personnel exposure. A combined electrolysis and catalytic exchange process is a very effective method to remove small quantities of tritium from light or heavy waste water streams. The process consists of three main steps: (a) A front end step that exchanges the tritium to a less toxic hydrogen phase. This can be performed either through a chemical exchange in the presence of a platinum supported catalyst or through the decomposition of water. (b) A back end process that purifies the tritiated hydrogen gas which evolved from the electrolysis. This can be performed through a palladium alloy membrane separator. (c) A means of storing the concentrated gas safely. Uranium is used if the storage is temporary; titanium is usually employed for long term storage. To gain a better understanding of the tritiated hydrogen gas purification process, a mathematical model of the palladium alloy membrane has been used. This model is described herein, and the representative results of the model calculations are presented. The authors selected the palladium alloy membrane for the hydrogen purification process by considering the membrane properties, such as a chemical resistance, mechanical stability, thermal stability, high permeability, and a stable operation. The solution-diffusion model can be a useful tool for designing a membrane permeator. The

Palladium alloy membrane process for the treatment of hydrogen isotopes

International Nuclear Information System (INIS)

Chung, Hongsuk; Paek, Seungwoo; Lee, Minsoo; Kim, Kwangrag; Yim, Sungpaal; Ahn, Dohee; Shim, Myunghwa

2005-01-01

Tritium is a radioactive isotope of hydrogen and it has a half-life of 12.3 years; it decays to He-3 by emitting a low energy beta radiation with an average energy of 5.7 keV and a maximum energy of 18.6 keV. Transfer of environmentally tritiated water to humans takes place via an inhalation, diffusion through the skin and ingestion. Radioactive waste containing tritium is continuously generated by the nuclear industry in, for example, nuclear reactor operations and a radioisotope production, as well as in medical research. Methods for removing tritium from liquid waste provide an alternative to the control of tritium emissions and a personnel exposure. A combined electrolysis and catalytic exchange process is a very effective method to remove small quantities of tritium from light or heavy waste water streams. The process consists of three main steps: (a) A front end step that exchanges the tritium to a less toxic hydrogen phase. This can be performed either through a chemical exchange in the presence of a platinum supported catalyst or through the decomposition of water. (b) A back end process that purifies the tritiated hydrogen gas which evolved from the electrolysis. This can be performed through a palladium alloy membrane separator. (c) A means of storing the concentrated gas safely. Uranium is used if the storage is temporary; titanium is usually employed for long term storage. To gain a better understanding of the tritiated hydrogen gas purification process, a mathematical model of the palladium alloy membrane has been used. This model is described herein, and the representative results of the model calculations are presented. The authors selected the palladium alloy membrane for the hydrogen purification process by considering the membrane properties, such as a chemical resistance, mechanical stability, thermal stability, high permeability, and a stable operation. The solution-diffusion model can be a useful tool for designing a membrane permeator. The

Determination of palladium by flame photometry

International Nuclear Information System (INIS)

Parellada Bellod, R.

1964-01-01

A study on the determination of palladium by lame photometry, fixing the most convent experimental conditions and using solvents to increase the emission of this elements is carried out. Among the organic solvents, acetone has been found the most efficient. The interferences produced by anions and cations have also been studied and an analytical method is related, in which lines of calibration of 0 to 100 ppm palladium re used. (Author) 7 refs

Structural characterization and gas reactions of small metal particles by high-resolution TEM and TED

Science.gov (United States)

Heinemann, K.

1985-01-01

The interaction of 100 and 200 keV electron beams with amorphous alumina, titania, and aluminum nitride substrates and nanometer-size palladium particulate deposits was investigated for the two extreme cases of (1) large-area electron-beam flash-heating and (2) small-area high-intensity electron-beam irradiation. The former simulates a short-term heating effect with minimum electron irradiation exposure, the latter simulates high-dosage irradiation with minimum heating effect. All alumina and titania samples responded to the flash-heating treatment with significant recrystallization. However, the size, crystal structure, shape, and orientation of the grains depended on the type and thickness of the films and the thickness of the Pd deposit. High-dosage electron irradiation also readily crystallized the alumina substrate films but did not affect the titania films. The alumina recrystallization products were usually either all in the alpha phase, or they were a mixture of small grains in a number of low-temperature phases including gamma, delta, kappa, beta, theta-alumina. Palladium deposits reacted heavily with the alumina substrates during either treatment, but they were very little effected when supported on titania. Both treatments had the same, less prominent localized crystallization effect on aluminum nitride films.

Adsorption of palladium ions by modified carbons from rice husks

International Nuclear Information System (INIS)

Mostafa, M.R.

1994-01-01

Steam activated carbon of high surface area does not show palladium ions adsorption. Treatment of this carbon with HF acid increases to a great extent the gas adsorption capacity expressed as nitrogen surface area as well as the adsorption capacity of palladium ions from aqueous solution. HHB was loaded in different amounts on to these carbons. The acid sites represent the active fraction of the surface on which the adsorption palladium ions proceed. The uptake of palladium ions by HHB treated carbons is related to the total number of HHB molecules loaded on the carbon surface. (author)

Development of Separation Materials Containing Palladium for Hydrogen Isotopes Separation

International Nuclear Information System (INIS)

Deng Xiaojun; Luo Deli; Qian Xiaojing

2010-01-01

Displacement chromatography (DC) is a ascendant technique for hydrogen isotopes separation. The performance of separation materials is a key factor to determine the separation effect of DC. At present,kinds of materials are researched, including palladium materials and non-palladium materials. It is hardly replaceable because of its excellent separation performance, although palladium is expensive. The theory of hydrogen isotopes separation using DC was introduced at a brief manner, while several palladium separation materials were expatiated in detail(Pd/K, Pd-Al 2 O 3 , Pd-Pt alloy). Development direction of separation materials for DC was forecasted elementarily. (authors)

Synthesis, characterization and SERS activity of biosynthesized silver nanoparticles

Science.gov (United States)

Bindhu, M. R.; Sathe, V.; Umadevi, M.

2013-11-01

Silver nanoparticles were rapidly synthesized using Moringa oleifera flower extract as the reducing agent shows surface plasmon resonance peak at 439 nm. The size and shape of the nanoparticles controlled by varying the concentration of M. oleifera flower extract in the reaction medium. The synthesized silver nanoparticles were well-dispersed spherical nanoparticles with the average size of 14 nm. The retinoic acid present in M. oleifera flower extract used as reducing agent and proteins was responsible for capping of the bioreduced silver nanoparticles. The obtained nanoparticle shows size-dependent SERS activity. The SERS spectrum indicates that the pyridine adsorbed on the silver surface in a stand-on orientation via its nitrogen lone pair electrons.

INITIAL PLANETESIMAL SIZES AND THE SIZE DISTRIBUTION OF SMALL KUIPER BELT OBJECTS

International Nuclear Information System (INIS)

Schlichting, Hilke E.; Fuentes, Cesar I.; Trilling, David E.

2013-01-01

The Kuiper Belt is a remnant from the early solar system and its size distribution contains many important constraints that can be used to test models of planet formation and collisional evolution. We show, by comparing observations with theoretical models, that the observed Kuiper Belt size distribution is well matched by coagulation models, which start with an initial planetesimal population with radii of about 1 km, and subsequent collisional evolution. We find that the observed size distribution above R ∼ 30 km is primordial, i.e., it has not been modified by collisional evolution over the age of the solar system, and that the size distribution below R ∼ 30 km has been modified by collisions and that its slope is well matched by collisional evolution models that use published strength laws. We investigate in detail the resulting size distribution of bodies ranging from 0.01 km to 30 km and find that its slope changes several times as a function of radius before approaching the expected value for an equilibrium collisional cascade of material strength dominated bodies for R ∼< 0.1 km. Compared to a single power-law size distribution that would span the whole range from 0.01 km to 30 km, we find in general a strong deficit of bodies around R ∼ 10 km and a strong excess of bodies around 2 km in radius. This deficit and excess of bodies are caused by the planetesimal size distribution left over from the runaway growth phase, which left most of the initial mass in small planetesimals while only a small fraction of the total mass is converted into large protoplanets. This excess mass in small planetesimals leaves a permanent signature in the size distribution of small bodies that is not erased after 4.5 Gyr of collisional evolution. Observations of the small Kuiper Belt Object (KBO) size distribution can therefore test if large KBOs grew as a result of runaway growth and constrained the initial planetesimal sizes. We find that results from recent KBO

PVP-Stabilized Palladium Nanoparticles in Silica as Effective Catalysts for Hydrogenation Reactions

Directory of Open Access Journals (Sweden)

Caroline Pires Ruas

2013-01-01

Full Text Available Palladium nanoparticles stabilized by poly (N-vinyl-2-pyrrolidone (PVP can be synthesized by corresponding Pd(acac2 (acac = acetylacetonate as precursor in methanol at 80°C for 2 h followed by reduction with NaBH4 and immobilized onto SiO2 prepared by sol-gel process under acidic conditions (HF or HCl. The PVP/Pd molar ratio is set to 6. The effect of the sol-gel catalyst on the silica morphology and texture and on Pd(0 content was investigated. The catalysts prepared (ca. 2% Pd(0/SiO2/HF and ca. 0,3% Pd(0/SiO2/HCl were characterized by TEM, FAAS, and SEM-EDS. Palladium nanoparticles supported in silica with a size 6.6 ± 1.4 nm were obtained. The catalytic activity was tested in hydrogenation of alkenes.

Heterogeneous precipitation of silver nanoparticles on kaolinite plates

International Nuclear Information System (INIS)

Cabal, B; Moya, J S; Torrecillas, R; Malpartida, F

2010-01-01

Two different methods to obtain silver nanoparticles supported on kaolin crystals have been performed: the first one followed a thermal reduction and the second one a chemical reduction. In both cases, the silver nanoparticles with two different average particles size (ca.12 and 30 nm) were perfectly isolated and attached to the surface of the kaolin plates. The silver nanoparticles were localized mainly at the edge of the single crystal plates, the hydroxyl groups being the main centres of adsorption. The samples were fully characterized by XRD, UV-vis spectroscopy and TEM. The antimicrobial benefits of the composites were evaluated as antibacterial against common Gram-positive and Gram-negative bacteria, and antifungal activity against yeast. The results indicated a high antimicrobial activity for Escherichia coli JM 110 and Micrococcus luteus, while being inactive against yeast under our experimental conditions. The chemical analysis of Ag in the fermentation broths show that only a small portion of metal (<9 ppm) is released from the kaolin/metakaolin particles. Therefore, the risk of toxicity due to a high concentration of metal in the medium is minimized.

Heterogeneous precipitation of silver nanoparticles on kaolinite plates.

Science.gov (United States)

Cabal, B; Torrecillas, R; Malpartida, F; Moya, J S

2010-11-26

Two different methods to obtain silver nanoparticles supported on kaolin crystals have been performed: the first one followed a thermal reduction and the second one a chemical reduction. In both cases, the silver nanoparticles with two different average particles size (ca.12 and 30 nm) were perfectly isolated and attached to the surface of the kaolin plates. The silver nanoparticles were localized mainly at the edge of the single crystal plates, the hydroxyl groups being the main centres of adsorption. The samples were fully characterized by XRD, UV-vis spectroscopy and TEM. The antimicrobial benefits of the composites were evaluated as antibacterial against common Gram-positive and Gram-negative bacteria, and antifungal activity against yeast. The results indicated a high antimicrobial activity for Escherichia coli JM 110 and Micrococcus luteus, while being inactive against yeast under our experimental conditions. The chemical analysis of Ag in the fermentation broths show that only a small portion of metal (<9 ppm) is released from the kaolin/metakaolin particles. Therefore, the risk of toxicity due to a high concentration of metal in the medium is minimized.

Heterogeneous precipitation of silver nanoparticles on kaolinite plates

Energy Technology Data Exchange (ETDEWEB)

Cabal, B; Moya, J S [Instituto de Ciencia de Materiales de Madrid (ICMM-CSIC), 28049, Cantoblanco, Madrid (Spain); Torrecillas, R [Centro de Investigacion en Nanomateriales y NanotecnologIa (CINN), Consejo Superior de Investigaciones CientIficas (CSIC)-Universidad de Oviedo-UO-Principado de Asturias, Parque Tecnologico de Asturias, 33428, Llanera (Spain); Malpartida, F, E-mail: bcabal@icmm.csic.es [Centro Nacional de BiotecnologIa (CNB-CSIC), 28049, Cantoblanco, Madrid (Spain)

2010-11-26

Two different methods to obtain silver nanoparticles supported on kaolin crystals have been performed: the first one followed a thermal reduction and the second one a chemical reduction. In both cases, the silver nanoparticles with two different average particles size (ca.12 and 30 nm) were perfectly isolated and attached to the surface of the kaolin plates. The silver nanoparticles were localized mainly at the edge of the single crystal plates, the hydroxyl groups being the main centres of adsorption. The samples were fully characterized by XRD, UV-vis spectroscopy and TEM. The antimicrobial benefits of the composites were evaluated as antibacterial against common Gram-positive and Gram-negative bacteria, and antifungal activity against yeast. The results indicated a high antimicrobial activity for Escherichia coli JM 110 and Micrococcus luteus, while being inactive against yeast under our experimental conditions. The chemical analysis of Ag in the fermentation broths show that only a small portion of metal (<9 ppm) is released from the kaolin/metakaolin particles. Therefore, the risk of toxicity due to a high concentration of metal in the medium is minimized.

Testing of elastomer seals using small-size rigs

International Nuclear Information System (INIS)

Leeks, C.W.E.; Dunford, B.; Barnfield, J.H.; Gray, I.L.S.

1997-01-01

This paper looks at the use of small size seal leakage test rigs to demonstrate the compliance of full size container seals against the IAEA Transport Regulation's limits for activity release for normal transport and accident conditions. The detailed requirements of the regulations are discussed and it is concluded that an appropriate test programme to meet these requirements using only small size test rigs, can normally be set up and carried out on a relatively short time scale. It is important that any small test rigs should be designed to represent the relevant features of the seal arrangement and the overall test programme should cover all of the conditions, specified by the regulations, for the type, classification and contents of the container under consideration. The parameters of elastomer O-rings, which affect their sealing ability, are considered and those which are amenable to small scale testing or have to be modelled at full size are identified. Generally, the seals used in leakage tests have to be modelled with a full size cross-section but can have a reduced peripheral length. (Author)

Efficiency of Al2O3 supported palladium sorbents in the process of hydrogen isotope exchange

International Nuclear Information System (INIS)

Andreev, B.M.; Perevezentsev, A.N.; Yasenkov, V.I.

1981-01-01

It is found that in the hydrogen-palladium system while applying the metal to aluminium oxide a considerable increase of the heterogeneous hydrogen isotopic exchange rate is observed due to the increase of its specific surface at 167-298 K temperatures and 350-500 Torr hydrogen pressures. It is shown that in the process of thermal treatment of the supported palladium sorbent resulting in reconstruction of the carrier porous structure, as well as in increasing the metal crystal size, the change of the stage, limiting the isotopic exchange process, occurs. The values of the rate and energy of activation of the hydrogen isotopic exchange are presented [ru

Separation of bismuth from gram amounts of thallium and silver by cation-exchange chromatography in nitric acid.

Science.gov (United States)

Meintjies, E; Strelow, F W; Victor, A H

1987-04-01

Traces and small amounts of bismuth can be separated from gram amounts of thallium and silver by successively eluting these elements with 0.3M and 0.6M nitric acid from a column containing 13 ml (3 g) of AG50W-X4, a cation-exchanger (100-200 mesh particle size) with low cross-linking. Bismuth is retained and can be eluted with 0.2M hydrobromic acid containing 20% v/v acetone, leaving many other trace elements absorbed. Elution of thallium is quite sharp, but silver shows a small amount of tailing (less than 1 gmg/ml silver in the eluate) when gram amounts are present, between 20 and 80 mug of silver appearing in the bismuth fraction. Relevant elution curves and results for the analysis of synthetic mixtures containing between 50 mug and 10 mg of bismuth and up to more than 1 g of thallium and silver are presented, as well as results for bismuth in a sample of thallium metal and in Merck thallium(I) carbonate. As little as 0.01 ppm of bismuth can be determined when the separation is combined with electrothermal atomic-absorption spectrometry.

Chemical vapour generation of silver: reduced palladium as permanent reaction modifier for enhanced performance

Czech Academy of Sciences Publication Activity Database

Matoušek, Tomáš; Sturgeon, R. E.

2004-01-01

Roč. 19, č. 8 (2004), s. 1014-1017 ISSN 0267-9477 R&D Projects: GA ČR GA203/01/0453 Institutional research plan: CEZ:AV0Z4031919 Keywords : chemical vapour generation * chemical modification * silver Subject RIV: CB - Analytical Chemistry, Separation Impact factor: 3.926, year: 2004

Interaction of silver nanoparticles with biological objects: antimicrobial properties and toxicity for the other living organisms

Energy Technology Data Exchange (ETDEWEB)

Egorova, E M, E-mail: emenano@mail.ru [Laboratory of Nanopathology, Institute of General Pathology and Patophysiology of RAMS, Baltijskaya st., 8, 125315 Moscow (Russian Federation); Science-technology Company ' Nanomet' , Moscow (Russian Federation)

2011-04-01

This paper presents several examples of the biological effects of small-sized silver nanoparticles (10.5{+-}3.5nm) observed in experiments on bacteria, slim mold, unicellular alga and plant seeds. The nanoparticles were prepared by the biochemical synthesis, based on the reduction of metal ions in reverse vicelles by biological reductants - natural plant pigments (flavonoids). It is found that, except for the plant seeds, silver nanoparticles (SNP) act as a strong toxic agent, both in water solution and as part of liquid-phase material. It is shown also that the biological action of silver nanoparticles can not be reduced to the toxic action of silver ions in equivalent concentrations or to that of the surfactant (the SNP stabilizer) present in the SNP water solution. Possible SNP applications are suggested.

Interaction of silver nanoparticles with biological objects: antimicrobial properties and toxicity for the other living organisms

International Nuclear Information System (INIS)

Egorova, E M

2011-01-01

This paper presents several examples of the biological effects of small-sized silver nanoparticles (10.5±3.5nm) observed in experiments on bacteria, slim mold, unicellular alga and plant seeds. The nanoparticles were prepared by the biochemical synthesis, based on the reduction of metal ions in reverse vicelles by biological reductants - natural plant pigments (flavonoids). It is found that, except for the plant seeds, silver nanoparticles (SNP) act as a strong toxic agent, both in water solution and as part of liquid-phase material. It is shown also that the biological action of silver nanoparticles can not be reduced to the toxic action of silver ions in equivalent concentrations or to that of the surfactant (the SNP stabilizer) present in the SNP water solution. Possible SNP applications are suggested.

Optimization of silver nanoparticles production by laser ablation in water using a 150-ps laser

International Nuclear Information System (INIS)

Stašić, J.; Živković, Lj.; Trtica, M.

2016-01-01

Silver nanoparticles were synthesized by laser ablation in liquid (water) using a 150-ps Nd:YAG laser. Due to their extraordinary characteristics, especially when obtained by this method providing high purity and high stability of colloids, silver NPs are nowadays highly important in various applications. The objective of this study was to optimize the process parameters in order to achieve the highest possible yield while retaining small particle size. Yield/mass concentration of the obtained particles was measured depending on different parameters: time of irradiation, pulse energy, position regarding the focus, and number of irradiation locations. The conditions providing relatively high yield, small particle size, highest production rate, and highest efficiency are 7 mJ, 15-min irradiation time (9000 pulses), and target position ∼4 mm in front of the lens focus. The results are compared with the results obtained by the longer nanosecond as well as the ultrashort pulsed lasers. A possible physical explanation is given.

Optimization of silver nanoparticles production by laser ablation in water using a 150-ps laser

Energy Technology Data Exchange (ETDEWEB)

Stašić, J.; Živković, Lj.; Trtica, M., E-mail: etrtica@vinca.rs [University of Belgrade, Institute of Nuclear Sciences “Vinča” (Serbia)

2016-12-15

Silver nanoparticles were synthesized by laser ablation in liquid (water) using a 150-ps Nd:YAG laser. Due to their extraordinary characteristics, especially when obtained by this method providing high purity and high stability of colloids, silver NPs are nowadays highly important in various applications. The objective of this study was to optimize the process parameters in order to achieve the highest possible yield while retaining small particle size. Yield/mass concentration of the obtained particles was measured depending on different parameters: time of irradiation, pulse energy, position regarding the focus, and number of irradiation locations. The conditions providing relatively high yield, small particle size, highest production rate, and highest efficiency are 7 mJ, 15-min irradiation time (9000 pulses), and target position ∼4 mm in front of the lens focus. The results are compared with the results obtained by the longer nanosecond as well as the ultrashort pulsed lasers. A possible physical explanation is given.

Large-size, high-uniformity, random silver nanowire networks as transparent electrodes for crystalline silicon wafer solar cells.

Science.gov (United States)

Xie, Shouyi; Ouyang, Zi; Jia, Baohua; Gu, Min

2013-05-06

Metal nanowire networks are emerging as next generation transparent electrodes for photovoltaic devices. We demonstrate the application of random silver nanowire networks as the top electrode on crystalline silicon wafer solar cells. The dependence of transmittance and sheet resistance on the surface coverage is measured. Superior optical and electrical properties are observed due to the large-size, highly-uniform nature of these networks. When applying the nanowire networks on the solar cells with an optimized two-step annealing process, we achieved as large as 19% enhancement on the energy conversion efficiency. The detailed analysis reveals that the enhancement is mainly caused by the improved electrical properties of the solar cells due to the silver nanowire networks. Our result reveals that this technology is a promising alternative transparent electrode technology for crystalline silicon wafer solar cells.

Dendritic surface morphology of palladium hydride produced by electrolytic deposition

International Nuclear Information System (INIS)

Julin, Peng; Bursill, L.A.

1990-01-01

Conventional and high-resolution electron microscopic studies of electrolytically-deposited palladium hydride reveal a fascinating variety of surface profile morphologies. The observations provide direct information concerning the surface structure of palladium electrodes and the mechanism of electrolytic deposition of palladium black. Both classical electrochemical mechanisms and recent 'modified diffusion-limited-aggregation' computer simulations are discussed in comparison with the experimental results. 13 refs., 9 figs

Monodisperse Silver Nanoparticles Synthesized by a Microwave-Assisted Method

International Nuclear Information System (INIS)

Shao-Peng, Zhu; Shao-Chun, Tang; Xiang-Kang, Meng

2009-01-01

Silver nanoparticles with an average size of about 20 nm are synthesized in a colloidal solution with the aid of microwave irradiation. Neither additional reductant nor stabilizer is required in this microwave-assisted method. The color of the colloidal solution is found to be dark green, different from the characteristic yellow of silver colloidal solutions. The silver nanoparticles in the colloidal solution have a narrow size distribution and large yield quantity. UV-visible absorption spectroscopy analysis reveals that the as-synthesized monodisperse silver nanoparticles have exceptional optical properties. Raman spectroscopy measurements demonstrate that these silver nanoparticles exhibit a notable surface-enhanced Raman scattering ability. (cross-disciplinary physics and related areas of science and technology)

Radiation synthesis of silver nanostructures in cotton matrix

International Nuclear Information System (INIS)

Chmielewska, Dagmara; Sartowska, Bożena

2012-01-01

Cotton is one of the most popular natural fibres, composed mainly of cellulose, which finds a wide range of applications in paper, textile and health care products industry. Researchers have focused their interest on the synthesis of cotton nanocomposites, which enhances its mechanical, thermal and antimicrobial properties by the incorporation of various nanoparticles into the cotton matrix. Silver is one of the most popular antimicrobial agents with a wide spectrum of antibacterial and antifungal activity that results from a complex mechanism of its interactions with the cells of harmful microorganism. In this work, electron beam radiation was applied to synthesise silver nanostructures in cotton fibres. Investigations of the influence of the initial silver salt concentration on the size and distribution of the obtained silver nanostructures were carried out. A detailed characterisation of these nanocomposites with SEM-BSE and EDS methods was performed. TGA and DSC analyses were performed to assess the influence of different size silver nanoparticles and the effect of electron beam irradiation on the thermal properties of cotton fibres. A microbiological investigation to determine the antibacterial activity of Ag-cotton nanocomposites was carried out. - Highlights: ► Ag NPs embedded in cotton matrix were synthesised by electron beam irradiation. ► Concentration of silver salt solution influences on size of silver nanoparticles. ► Silver content as well as irradiation affect thermal properties of cotton fabrics. ► Ag-cotton nanocomposites exhibit antibacterial activity against bacteria and fungi.

Silver nanoparticle formation in thin oxide layer on silicon by silver-negative-ion implantation for Coulomb blockade at room temperature

International Nuclear Information System (INIS)

Tsuji, Hiroshi; Arai, Nobutoshi; Matsumoto, Takuya; Ueno, Kazuya; Gotoh, Yasuhito; Adachi, Kouichiro; Kotaki, Hiroshi; Ishikawa, Junzo

2004-01-01

Formation of silver nanoparticles formed by silver negative-ion implantation in a thin SiO 2 layer and its I-V characteristics were investigated for development single electron devices. In order to obtain effective Coulomb blockade phenomenon at room temperature, the isolated metal nanoparticles should be in very small size and be formed in a thin insulator layer such as gate oxide on the silicon substrate. Therefore, conditions of a fine particles size, high particle density and narrow distribution should be controlled at their formation without any electrical breakdown of the thin insulator layer. We have used a negative-ion implantation technique with an advantage of 'charge-up free' for insulators, with which no breakdown of thin oxide layer on Si was obtained. In the I-V characteristics with Au electrode, the current steps were observed with a voltage interval of about 0.12 V. From the step voltage the corresponded capacitance was calculated to be 0.7 aF. In one nanoparticle system, this value of capacitance could be given by a nanoparticle of about 3 nm in diameter. This consideration is consistent to the measured particle size in the cross-sectional TEM observation. Therefore, the observed I-V characteristics with steps are considered to be Coulomb staircase by the Ag nanoparticles

Silver Eco-Solvent Ink for Reactive Printing of Polychromatic SERS and SPR Substrates.

Science.gov (United States)

Dustov, Mavlavi; Golovina, Diana I; Polyakov, Alexander Yu; Goldt, Anastasia E; Eliseev, Andrei A; Kolesnikov, Efim A; Sukhorukova, Irina V; Shtansky, Dmitry V; Grünert, Wolfgang; Grigorieva, Anastasia V

2018-02-09

A new reactive ink based on a silver citrate complex is proposed for a photochemical route to surface-enhanced Raman spectroscopy active substrates with controllable extinction spectra. The drop-cast test of the ink reveals homogeneous nucleation of silver and colloid particle growth originating directly from photochemical in situ reduction in droplets, while the following evaporation of the deposited ink produces small nano- and micron-size particles. The prepared nanostructures and substrates were accurately characterized by electron microscopy methods and optical extinction spectroscopy. Varying the duration of UV irradiation allows tuning the morphology of individual silver nanoparticles forming hierarchical ring structures with numerous "hot spots" for most efficient Raman enhancement. Raman measurements of probe molecules of rhodamine 6G and methylene blue reached the largest signal enhancement of 10⁶ by the resonance effects.

High-yield water-based synthesis of truncated silver nanocubes

International Nuclear Information System (INIS)

Chang, Yun-Min; Lu, I-Te; Chen, Chih-Yuan; Hsieh, Yu-Chi; Wu, Pu-Wei

2014-01-01

Highlights: • Development of a water-based formula to fabricate truncated Ag nanocubes. • The sample exhibits (1 0 0), (1 1 0), and (1 1 1) on the facets, edges, and corners. • The sample shows three characteristic absorption peaks due to plasma resonance. -- Abstract: A high-yield water-based hydrothermal synthesis was developed using silver nitrate, ammonia, glucose, and cetyltrimethylammonium bromide (CTAB) as precursors to synthesize truncated silver nanocubes with uniform sizes and in large quantities. With a fixed CTAB concentration, truncated silver nanocubes with sizes of 49.3 ± 4.1 nm were produced when the molar ratio of glucose/silver cation was maintained at 0.1. The sample exhibited (1 0 0), (1 1 0), and (1 1 1) planes on the facets, edges, and corners, respectively. In contrast, with a slightly larger glucose/silver cation ratio of 0.35, well-defined nanocubes with sizes of 70.9 ± 3.8 nm sizes were observed with the (1 0 0) plane on six facets. When the ratio was further increased to 1.5, excess reduction of silver cations facilitated the simultaneous formation of nanoparticles with cubic, spherical, and irregular shapes. Consistent results were obtained from transmission electron microscopy, scanning electron microscopy, X-ray diffraction, and UV–visible absorption measurements

High-yield water-based synthesis of truncated silver nanocubes

Energy Technology Data Exchange (ETDEWEB)

Chang, Yun-Min; Lu, I-Te; Chen, Chih-Yuan; Hsieh, Yu-Chi; Wu, Pu-Wei, E-mail: ppwu@mail.nctu.edu.tw

2014-02-15

Highlights: • Development of a water-based formula to fabricate truncated Ag nanocubes. • The sample exhibits (1 0 0), (1 1 0), and (1 1 1) on the facets, edges, and corners. • The sample shows three characteristic absorption peaks due to plasma resonance. -- Abstract: A high-yield water-based hydrothermal synthesis was developed using silver nitrate, ammonia, glucose, and cetyltrimethylammonium bromide (CTAB) as precursors to synthesize truncated silver nanocubes with uniform sizes and in large quantities. With a fixed CTAB concentration, truncated silver nanocubes with sizes of 49.3 ± 4.1 nm were produced when the molar ratio of glucose/silver cation was maintained at 0.1. The sample exhibited (1 0 0), (1 1 0), and (1 1 1) planes on the facets, edges, and corners, respectively. In contrast, with a slightly larger glucose/silver cation ratio of 0.35, well-defined nanocubes with sizes of 70.9 ± 3.8 nm sizes were observed with the (1 0 0) plane on six facets. When the ratio was further increased to 1.5, excess reduction of silver cations facilitated the simultaneous formation of nanoparticles with cubic, spherical, and irregular shapes. Consistent results were obtained from transmission electron microscopy, scanning electron microscopy, X-ray diffraction, and UV–visible absorption measurements.

Influence of surfactant on the preparation of silver nanoparticles by polyol method

International Nuclear Information System (INIS)

Dung Dang, Thi My; Tuyet Le, Thi Thu; Dang, Mau Chien; Fribourg-Blanc, Eric

2012-01-01

In this study, silver nanoparticles were synthesized from silver nitrate via a polyol method in ambient atmosphere. In our synthesis route, polyvinylpyrrolidone (PVP) is used as both size controller and capping agent, ethylene glycol acts both as solvent and reducing agent. The obtained silver nanoparticles were characterized by ultraviolet-visible spectrophotometry which indicated the formation of nanoparticles. Investigation of Fourier transform infrared spectroscopy clearly demonstrated the coordination between silver nanoparticles and PVP. Transmission electron microscopy (TEM) contributed to the particle size analysis. The surface plasmon resonance peak in absorption spectra of silver colloidal solution showed absorption from 406 to 409 nm. The average size of the resulting silver nanoparticles was below 10 nm with a dependency on the PVP concentration. (paper)

In Vivo Quantitative Study of Sized-Dependent Transport and Toxicity of Single Silver Nanoparticles Using Zebrafish Embryos

Science.gov (United States)

Lee, Kerry J.; Browning, Lauren M.; Nallathamby, Prakash D.; Desai, Tanvi; Cherukui, Pavan K.; Xu, Xiao-Hong Nancy

2012-01-01

Nanomaterials possess distinctive physicochemical properties (e.g., small sizes, high surface area-to-volume ratios) and promise a wide variety of applications, ranging from design of high quality consumer products to effective disease diagnosis and therapy. These properties can lead to toxic effects, potentially hindering advance in nanotechnology. In this study, we have synthesized and characterized purified and stable (non-aggregation) silver nanoparticles (Ag NPs, 41.6±9.1 nm in average diameters), and utilized early-developing (cleavage-stage) zebrafish embryos (critical aquatic and eco- species) as in vivo model organisms to probe diffusion and toxicity of Ag NPs. We found that single Ag NPs (30–72 nm diameters) passively diffused into the embryos through chorionic pores via random Brownian motion and stayed inside the embryos throughout their entire development (120 hours-post-fertilization, hpf). Dose and size dependent toxic effects of the NPs on embryonic development were observed, showing the possibility of tuning biocompatibility and toxicity of the NPs. At lower concentrations of the NPs (≤ 0.02 nM), 75–91% of embryos developed to normal zebrafish. At the higher concentrations of NPs (≥ 0.20 nM), 100% of embryos became dead. At the concentrations in between (0.02–0.2 nM), embryos developed to various deformed zebrafish. Number and sizes of individual Ag NPs embedded in tissues of normal and deformed zebrafish at 120 hpf were quantitatively analyzed, showing deformed zebrafish with higher number of larger NPs than normal zebrafish, and size-dependent nanotoxicity. By comparing with our previous studies of smaller Ag NPs (11.6±3.5 nm), the results further demonstrate striking size-dependent nanotoxicity that, at the same molar concentration, the larger Ag NPs (41.6±9.1 nm) are more toxic than the smaller Ag NPs (11.6±3.5 nm). PMID:22486336

Fexofenadine Suppresses Delayed-Type Hypersensitivity in the Murine Model of Palladium Allergy

Directory of Open Access Journals (Sweden)

Ryota Matsubara

2017-06-01

Full Text Available Palladium is frequently used in dental materials, and sometimes causes metal allergy. It has been suggested that the immune response by palladium-specific T cells may be responsible for the pathogenesis of delayed-type hypersensitivity in study of palladium allergic model mice. In the clinical setting, glucocorticoids and antihistamine drugs are commonly used for treatment of contact dermatitis. However, the precise mechanism of immune suppression in palladium allergy remains unknown. We investigated inhibition of the immune response in palladium allergic mice by administration of prednisolone as a glucocorticoid and fexofenadine hydrochloride as an antihistamine. Compared with glucocorticoids, fexofenadine hydrochloride significantly suppressed the number of T cells by interfering with the development of antigen-presenting cells from the sensitization phase. Our results suggest that antihistamine has a beneficial effect on the treatment of palladium allergy compared to glucocorticoids.

Palladium assisted silver transport in polycrystalline SiC

Energy Technology Data Exchange (ETDEWEB)

Neethling, J.H., E-mail: Jan.Neethling@nmmu.ac.za [Physics Department, Nelson Mandela Metropolitan University, PO Box 77000, Port Elizabeth 6031 (South Africa); O' Connell, J.H.; Olivier, E.J. [Physics Department, Nelson Mandela Metropolitan University, PO Box 77000, Port Elizabeth 6031 (South Africa)

2012-10-15

The transport of silver in polycrystalline 3C-SiC and hexagonal 6H-SiC has been investigated by annealing the SiC samples in contact with a Pd-Ag compound at temperatures of 800 and 1000 Degree-Sign C and times of 24 and 67 h. The Pd was added in an attempt to improve the low wetting of SiC by Ag and further because Pd is produced in measurable concentrations in coated particles during reactor operation. Pd is also known to coalesce at the IPyC-SiC interface and to chemically attack the SiC layer. SEM, TEM and EDS were used to show that the Ag penetrates polycrystalline SiC along grain boundaries together with Pd. It is suggested that Ag transport in SiC takes place along grain boundaries in the form of moving nodules consisting of a Ag-Pd mixture. It is assumed that the nodules move along grain boundaries by dissolving the SiC at the leading edge followed by the reprecipitation of SiC at the trailing edge. Since the solubility of Cs in Ag and Pd is extremely low, it is unlikely that Cs will penetrate the SiC together with the Ag-Pd compound if present at the IPyC-SiC interface. If it is assumed that the dominant transport mechanism of Ag in intact polycrystalline SiC is indeed the Pd assisted mechanism, then the stabilization of Pd (and other metallic fission products) in the kernel could be a way of mitigating Ag release from TRISO-coated particles.

Palladium assisted silver transport in polycrystalline SiC

International Nuclear Information System (INIS)

Neethling, J.H.; O’Connell, J.H.; Olivier, E.J.

2012-01-01

The transport of silver in polycrystalline 3C-SiC and hexagonal 6H-SiC has been investigated by annealing the SiC samples in contact with a Pd–Ag compound at temperatures of 800 and 1000 °C and times of 24 and 67 h. The Pd was added in an attempt to improve the low wetting of SiC by Ag and further because Pd is produced in measurable concentrations in coated particles during reactor operation. Pd is also known to coalesce at the IPyC–SiC interface and to chemically attack the SiC layer. SEM, TEM and EDS were used to show that the Ag penetrates polycrystalline SiC along grain boundaries together with Pd. It is suggested that Ag transport in SiC takes place along grain boundaries in the form of moving nodules consisting of a Ag–Pd mixture. It is assumed that the nodules move along grain boundaries by dissolving the SiC at the leading edge followed by the reprecipitation of SiC at the trailing edge. Since the solubility of Cs in Ag and Pd is extremely low, it is unlikely that Cs will penetrate the SiC together with the Ag–Pd compound if present at the IPyC–SiC interface. If it is assumed that the dominant transport mechanism of Ag in intact polycrystalline SiC is indeed the Pd assisted mechanism, then the stabilization of Pd (and other metallic fission products) in the kernel could be a way of mitigating Ag release from TRISO-coated particles.

Use of electrothermal atomic absorption spectrometry for size profiling of gold and silver nanoparticles.

Science.gov (United States)

Panyabut, Teerawat; Sirirat, Natnicha; Siripinyanond, Atitaya

2018-02-13

Electrothermal atomic absorption spectrometry (ETAAS) was applied to investigate the atomization behaviors of gold nanoparticles (AuNPs) and silver nanoparticles (AgNPs) in order to relate with particle size information. At various atomization temperatures from 1400 °C to 2200 °C, the time-dependent atomic absorption peak profiles of AuNPs and AgNPs with varying sizes from 5 nm to 100 nm were examined. With increasing particle size, the maximum absorbance was observed at the longer time. The time at maximum absorbance was found to linearly increase with increasing particle size, suggesting that ETAAS can be applied to provide the size information of nanoparticles. With the atomization temperature of 1600 °C, the mixtures of nanoparticles containing two particle sizes, i.e., 5 nm tannic stabilized AuNPs with 60, 80, 100 nm citrate stabilized AuNPs, were investigated and bimodal peaks were observed. The particle size dependent atomization behaviors of nanoparticles show potential application of ETAAS for providing size information of nanoparticles. The calibration plot between the time at maximum absorbance and the particle size was applied to estimate the particle size of in-house synthesized AuNPs and AgNPs and the results obtained were in good agreement with those from flow field-flow fractionation (FlFFF) and transmission electron microscopy (TEM) techniques. Furthermore, the linear relationship between the activation energy and the particle size was observed. Copyright © 2017 Elsevier B.V. All rights reserved.

Studying the morphological features of plasma treated silver and PEGylated silver nanoparticles: antibacterial activity

Science.gov (United States)

Waseem, M.; Awan, T.; Yasin, H. M.; Rehman, N. U.

2018-03-01

A strategy to treat the silver and PEGylated silver nanoparticles with plasma was being purposed. Oil in water (o/w) microemulsion method was used for the synthesis of Ag nanoparticles (AgNPs). Polyethylene glycol (PEG) having molecular weight 600 was used to coat the surface of AgNPs. Optical emission spectroscopy (OES) was used to characterize the plasma and it is noted that plasma treatment is useful to modify the structural characteristic of silver nanoparticles. The nanoparticles were treated with helium-oxygen mixture plasma, generated in plasma needle at atmospheric pressure. Both AgNPs and PEGylated AgNPs before and after plasma treatment were characterized by x-rays diffraction (XRD), scanning electron microscopy (SEM) and Fourier transform infrared (FTIR) spectroscopy. The crystallite size of silver nanoparticles after the treatment of plasma decreases from 71 nm to 27 nm. The SEM micrographs show that the size of Ag nanoparticles was nearly 118 nm whereas the thickness of the silver needle was around 135 nm. All the characteristics IR bands associated to the silver nanoparticles were detected. The FTIR spectrum also support the accumulation of OH radicals in the plasma treated samples. The samples before and after plasma treatment were screened against Gram positive (Bacillus Subtilis and Staphylococcus Aureus) and Gram negative (Escherichia Coli and Pseudomonas Aeruginosa) bacteria. The promising response was detected when plasma treated PEGylated AgNPs was tested against bacterial strains.

Palladium-Catalyzed Cross-Coupling Reactions of Perfluoro Organic Compounds

Directory of Open Access Journals (Sweden)

Masato Ohashi

2014-09-01

Full Text Available In this review, we summarize our recent development of palladium(0-catalyzed cross-coupling reactions of perfluoro organic compounds with organometallic reagents. The oxidative addition of a C–F bond of tetrafluoroethylene (TFE to palladium(0 was promoted by the addition of lithium iodide, affording a trifluorovinyl palladium(II iodide. Based on this finding, the first palladium-catalyzed cross-coupling reaction of TFE with diarylzinc was developed in the presence of lithium iodide, affording α,β,β-trifluorostyrene derivatives in excellent yield. This coupling reaction was expanded to the novel Pd(0/PR3-catalyzed cross-coupling reaction of TFE with arylboronates. In this reaction, the trifluorovinyl palladium(II fluoride was a key reaction intermediate that required neither an extraneous base to enhance the reactivity of organoboronates nor a Lewis acid additive to promote the oxidative addition of a C–F bond. In addition, our strategy utilizing the synergetic effect of Pd(0 and lithium iodide could be applied to the C–F bond cleavage of unreactive hexafluorobenzene (C6F6, leading to the first Pd(0-catalyzed cross-coupling reaction of C6F6 with diarylzinc compounds.

Sputtering induced surface composition changes in copper-palladium alloys

International Nuclear Information System (INIS)

Sundararaman, M.; Sharma, S.K.; Kumar, L.; Krishnan, R.

1981-01-01

It has been observed that, in general, surface composition is different from bulk composition in multicomponent materials as a result of ion beam sputtering. This compositional difference arises from factors like preferential sputtering, radiation induced concentration gradients and the knock-in effect. In the present work, changes in the surface composition of copper-palladium alloys, brought about by argon ion sputtering, have been studied using Auger electron spectroscopy. Argon ion energy has been varied from 500 eV to 5 keV. Enrichment of palladium has been observed in the sputter-altered layer. The palladium enrichment at the surface has been found to be higher for 500 eV argon ion sputtering compared with argon ion sputtering at higher energies. Above 500 eV, the surface composition has been observed to remain the same irrespective of the sputter ion energy for each alloy composition. The bulk composition ratio of palladium to copper has been found to be linearly related to the sputter altered surface composition ratio of palladium to copper. These results are discussed on the basis of recent theories of alloy sputtering. (orig.)

Synthesis and electrical properties of silver nanoplates for electronic applications

Directory of Open Access Journals (Sweden)

Xiong Nana

2015-06-01

Full Text Available In this paper, silver nanoplates of 100 to 500 nm size were synthesized by reduction of silver nitrate with N,Ndimethylformamide, using poly(vinylpyrolidone as a surfactant and ferric chloride as a controlling agent, at 120 to 160 °C for 5 to 24 hours. The influence of the concentration of ferric chloride, the reaction temperature and reaction time on the morphology of the product has been investigated by transmission electron microscopy, scanning electron microscopy and UV-Vis spectroscopy. The results indicated that the products obtained at the low reaction temperature and short reaction time in the presence of FeCl3 in the reaction solution were in the form of silver nanoplates, whose morphology was mainly triangular and hexagonal. In addition, the size and thickness of the nanoplates increased with increasing of the FeCl3 concentration. At a high reaction temperature and long reaction time, the truncated triangle and hexagonal nanoplates were mainly produced. Furthermore, the sintering behavior of nanoplates was studied and the results showed that sintering of the silver nanoplates started at 180 °C, and a typical sintering behavior was observed at higher temperatures. The incorporation of the silver nanoplates into the polymer matrix with micro-sized silver flakes led to an increase in the matrix resistivity in almost all cases, especially at high fractions and low curing temperatures. The curing temperature had an influence on the resistivity of the conductive adhesives filled with micro-sized silver flakes and silver nanoplates due to sintering of the silver nanoplates.

In situ green synthesis of antimicrobial carboxymethyl chitosan-nanosilver hybrids with controlled silver release.

Science.gov (United States)

Huang, Siqi; Yu, Zhiming; Zhang, Yang; Qi, Chusheng; Zhang, Shifeng

2017-01-01

In order to fabricate antimicrobial carboxymethyl chitosan-nanosilver (CMC-Ag) hybrids with controlled silver release, this study demonstrated comparable formation via three synthetic protocols: 1) carboxymethyl chitosan (CMC) and glucose (adding glucose after AgNO 3 ), 2) CMC and glucose (adding glucose before AgNO 3 ), and 3) CMC only. Under principles of green chemistry, the synthesis was conducted in an aqueous medium exposed to microwave irradiation for 10 minutes with nontoxic chemicals. The structure and formation mechanisms of the three CMC-Ag hybrids were explored using X-ray diffraction, ultraviolet-visible spectroscopy, transmission electron microscopy, and Fourier-transform infrared analyses. Additionally, antimicrobial activity and in vitro silver release of the three synthesized hybrids were investigated in detail. The results revealed that a large number of stable, uniform, and small silver nanoparticles (AgNPs) were synthesized in situ on CMC chains via protocol 1. AgNPs were well dispersed with narrow size distribution in the range of 6-20 nm, with mean diameter only 12.22±2.57 nm. The addition of glucose resulted in greater AgNP synthesis. The order of addition of glucose and AgNO 3 significantly affected particle size and size distribution of AgNPs. Compared to CMC alone and commercially available AgNPs, the antimicrobial activities of three hybrids were significantly improved. Of the three hybrids, CMC-Ag1 synthesized via protocol 1 exhibited better antimicrobial activity than CMC-Ag2 and CMC-Ag3, and showed more effective inhibition of Staphylococcus aureus than Escherichia coli . Due to strong coordination and electrostatic interactions between CMC and silver and good steric protection provided by CMC, CMC-Ag1 displayed stable and continuous silver release and better performance in retaining silver for prolonged periods than CMC-Ag2 and CMC-Ag3.

In situ green synthesis of antimicrobial carboxymethyl chitosan–nanosilver hybrids with controlled silver release

Science.gov (United States)

Huang, Siqi; Yu, Zhiming; Zhang, Yang; Qi, Chusheng; Zhang, Shifeng

2017-01-01

In order to fabricate antimicrobial carboxymethyl chitosan–nanosilver (CMC-Ag) hybrids with controlled silver release, this study demonstrated comparable formation via three synthetic protocols: 1) carboxymethyl chitosan (CMC) and glucose (adding glucose after AgNO3), 2) CMC and glucose (adding glucose before AgNO3), and 3) CMC only. Under principles of green chemistry, the synthesis was conducted in an aqueous medium exposed to microwave irradiation for 10 minutes with nontoxic chemicals. The structure and formation mechanisms of the three CMC-Ag hybrids were explored using X-ray diffraction, ultraviolet-visible spectroscopy, transmission electron microscopy, and Fourier-transform infrared analyses. Additionally, antimicrobial activity and in vitro silver release of the three synthesized hybrids were investigated in detail. The results revealed that a large number of stable, uniform, and small silver nanoparticles (AgNPs) were synthesized in situ on CMC chains via protocol 1. AgNPs were well dispersed with narrow size distribution in the range of 6–20 nm, with mean diameter only 12.22±2.57 nm. The addition of glucose resulted in greater AgNP synthesis. The order of addition of glucose and AgNO3 significantly affected particle size and size distribution of AgNPs. Compared to CMC alone and commercially available AgNPs, the antimicrobial activities of three hybrids were significantly improved. Of the three hybrids, CMC-Ag1 synthesized via protocol 1 exhibited better antimicrobial activity than CMC-Ag2 and CMC-Ag3, and showed more effective inhibition of Staphylococcus aureus than Escherichia coli. Due to strong coordination and electrostatic interactions between CMC and silver and good steric protection provided by CMC, CMC-Ag1 displayed stable and continuous silver release and better performance in retaining silver for prolonged periods than CMC-Ag2 and CMC-Ag3. PMID:28458539

The Synthesis of Silver Nanoparticles Produced by Chemical Reduction of Silver Salt Solution

International Nuclear Information System (INIS)

Sri Budi Harmani; Dewi Sondari; Agus Haryono

2008-01-01

Described in this research are the synthesis of silver nanoparticle produced by chemical reduction of silver salt (silver nitrate AgNO 3 ) solution. As a reducer, sodium citrate (C 6 H 5 O 7 Na 3 ) was used. Preparation of silver colloid is done by using chemical reduction method. In typical experiment 150 ml of 1.10 -3 M AgNO 3 solution was heated with temperature variation such as 90, 100, 110 degree of Celsius. To this solution 15 ml of 1 % trisodium citrate was added into solution drop by drop during heating. During the process, solution was mixed vigorously. Solution was heated until colour's change is evident (pale yellow solution is formed). Then it was removed from the heating element and stirred until cooled to room temperature. Experimental result showed that diameter of silver nanoparticles in colloid solution is about 28.3 nm (Ag colloid, 90 o C); 19.9 nm (Ag colloid, 100 o C)and 26.4 nm (Ag colloid, 110 o C). Characterization of the silver nanoparticle colloid conducted by using UV-Vis Spectroscopy, Particles Size Analyzer (PSA) and Scanning Electron Microscope (SEM) indicate the produced structures of silver nanoparticles. (author)

Synthesis of self-assembly plasmonic silver nanoparticles with tunable luminescence color

International Nuclear Information System (INIS)

Al-Ghamdi, Haifa S.; Mahmoud, Waleed E.

2014-01-01

Assembly is an elegant and effective bottom-up approach to prepare arrays of nanoparticles from nobel metals. Noble metal nanoparticles are perfect building blocks because they can be prepared with an adequate functionalization to allow their assembly and with controlled sizes. Herein, we report a novel recipe for the synthesis of self-assembled silver nanoparticles with tunable optical properties and sizes. The synthetic route followed here based on the covalent binding among silver nanoparticles by means of poly vinyl alcohol for the first time. The size of silver nanoparticle is governed by varying the amount of sodium borohydride. The as-synthesized nanoparticles were characterized by transmission electron microscopy, x-ray diffraction, energy dispersive x-ray spectroscopy, selected area electron diffraction and UV–vis spectroscopy. Results depicted that self-assembly of mono-dispersed silver nanoparticles with different sizes have been achieved. The silver nanostructure has a single crystalline faced centered cubic structure with growth orientation along (1 1 1) facet. These nanoparticles exhibited localized surface plasmon resonance at 403 nm. The luminescence peaks were red-sifted from violet to green due to the increase of the particle sizes. -- Highlights: • Self-assembled silver nanoparticles based PVA were synthesized. • NaBH 4 amount was found particle size dependent. • Silver nanoparticles strongly affected the surface plasmon resonance. • Highly symmetric luminescence emission band narrow width is obtained. • Dark field image showed a tunable color change from violet to green

The effect of the deposition parameters on size, distribution and antimicrobial properties of photoinduced silver nanoparticles on titania coatings

Energy Technology Data Exchange (ETDEWEB)

Piwonski, Ireneusz, E-mail: irek@uni.lodz.pl [University of Lodz, Department of Technology and Chemistry of Materials, Pomorska 163, 90-236 Lodz (Poland); Kadziola, Kinga; Kisielewska, Aneta; Soliwoda, Katarzyna [University of Lodz, Department of Technology and Chemistry of Materials, Pomorska 163, 90-236 Lodz (Poland); Wolszczak, Marian [Technical University of Lodz, Institute of Applied Radiation Chemistry, Wroblewskiego 15, 93-590 Lodz (Poland); Lisowska, Katarzyna; Wronska, Natalia; Felczak, Aleksandra [University of Lodz, Department of Industrial Microbiology and Biotechnology, Pilarskiego 14/16, 90-231 Lodz (Poland)

2011-06-01

Controlled photodeposition of silver nanoparticles (AgNP) on titania coatings using two different sources of UV light is described. Titania (anatase) thin films were prepared by the sol-gel dip-coating method on silicon wafers. AgNPs were grown on the titania surface as a result of UV illumination of titania films immersed in aqueous solutions of silver nitrate. UV xenon lamp or excimer laser, both operating at the wavelength 351 {+-} 5 nm, was used as illumination sources. The AFM topography of AgNP/TiO{sub 2} nanocomposites revealed that silver nanoparticles could be synthesized by both sources of illumination, however the photocatalysis carried out by UV light from xenon lamp illumination leads to larger AgNP than those synthesized using the laser beam. It was found that the increasing concentration of silver ions in the initial solution increases the number of Ag nanoparticles on the titania surface, while longer time of irradiation results the growth of larger size nanoparticles. Antibacterial tests performed on TiO{sub 2} covered by Ag nanoparticles revealed that increasing density of nanoparticles enhances the inhibition of bacterial growth. It was also found that antibacterial activity drops by only 10-15% after 6 cycles compared to the initial use.

The effect of the deposition parameters on size, distribution and antimicrobial properties of photoinduced silver nanoparticles on titania coatings

International Nuclear Information System (INIS)

Piwonski, Ireneusz; Kadziola, Kinga; Kisielewska, Aneta; Soliwoda, Katarzyna; Wolszczak, Marian; Lisowska, Katarzyna; Wronska, Natalia; Felczak, Aleksandra

2011-01-01

Controlled photodeposition of silver nanoparticles (AgNP) on titania coatings using two different sources of UV light is described. Titania (anatase) thin films were prepared by the sol-gel dip-coating method on silicon wafers. AgNPs were grown on the titania surface as a result of UV illumination of titania films immersed in aqueous solutions of silver nitrate. UV xenon lamp or excimer laser, both operating at the wavelength 351 ± 5 nm, was used as illumination sources. The AFM topography of AgNP/TiO 2 nanocomposites revealed that silver nanoparticles could be synthesized by both sources of illumination, however the photocatalysis carried out by UV light from xenon lamp illumination leads to larger AgNP than those synthesized using the laser beam. It was found that the increasing concentration of silver ions in the initial solution increases the number of Ag nanoparticles on the titania surface, while longer time of irradiation results the growth of larger size nanoparticles. Antibacterial tests performed on TiO 2 covered by Ag nanoparticles revealed that increasing density of nanoparticles enhances the inhibition of bacterial growth. It was also found that antibacterial activity drops by only 10-15% after 6 cycles compared to the initial use.

Rapid and Efficient Synthesis of Silver Nanofluid Using Electrical Discharge Machining

Directory of Open Access Journals (Sweden)

Kuo-Hsiung Tseng

2013-01-01

Full Text Available The electrical discharge machining (EDM system has been proven feasible as a rapid and efficient method for silver nanofluid preparation. This study prepared the silver nano-fluid via EDM and investigated the relationship between its process parameters and product characteristics. The prior study had found that the silver nano-fluid prepared by EDM contained both silver nanoparticles and silver ions. Silver ions had revealed the cause of the high suspension of the silver nanoparticles. To examine the relationship between the stability of silver nanofluid and the process parameters, this study quantified the relationship of process parameters to the material removal rate (MRR of silver electrode and silver ion output rate (IOR in the fluid, in order to achieve the most effective process parameter condition. Furthermore, the stability of silver nano-fluid was analyzed by various devices, including UV-Vis spectroscopy, size-distribution, and Zeta-potential analyzer. The effects of MRR, IOR, particle size, Zeta-potential, and optical properties of silver nanofluid under different process parameters are also discussed.

77 FR 39442 - Receipts-Based, Small Business Size Standard

Science.gov (United States)

2012-07-03

... RIN 3150-AJ14 [NRC-2012-0062] Receipts-Based, Small Business Size Standard AGENCY: Nuclear Regulatory... Regulatory Flexibility Act of 1980, as amended. The NRC is proposing to increase its receipts-based, small business size standard from $6.5 million to $7 million to conform to the standard set by the Small Business...

78 FR 77334 - Small Business Size Standards: Construction

Science.gov (United States)

2013-12-23

... enrollment in the System of Award Management's (SAM) Dynamic Small Business Search database, and more firms... SMALL BUSINESS ADMINISTRATION 13 CFR Part 121 RIN 3245-AG37 Small Business Size Standards: Construction AGENCY: U.S. Small Business Administration. ACTION: Final rule. SUMMARY: The United States Small...

Biosynthesis of silver nanoparticles by marine bacterium, Idiomarina

Indian Academy of Sciences (India)

UV-visible absorption scan of a 48 h culture exposed to 5mM silver nitrate revealed a broad peak at 450nm indicative of the surface plasmon resonance of SNPs. XRD analysis confirmed the presence of elemental silver and the crystallite size was calculated to be 25nm using Scherrer formula. The average particle size as ...

Investigation of small and modular-sized fast reactor

International Nuclear Information System (INIS)

Kubota, Kenichi; Kawasaki, Nobuchika; Umetsu, Yoichiro; Akatsu, Minoru; Kasai, Shigeo; Konomura, Mamoru; Ichimiya, Masakazu

2000-06-01

In this paper, feasibility of the multipurpose small fast reactor, which could be used for requirements concerned with various utilization of electricity and energy and flexibility of power supply site, is discussed on the basis of examination of literatures of various small reactors. And also, a possibility of economic improvement by learning effect of fabrication cost is discussed for the modular-sized reactor which is expected to be a base load power supply system with lower initial investment. (1) Multipurpose small reactor (a) The small reactor with 10MWe-150MWe has a potential as a power source for large co-generation, a large island, a middle city, desalination and marine use. (b) Highly passive mechanism, long fuel exchange interval, and minimized maintenance activities are required for the multipurpose small reactor design. The reactor has a high potential for the long fuel exchange interval, since it is relatively easy for FR to obtain a long life core. (c) Current designs of small FRs in Japan and USA (NERI Project) are reviewed to obtain design requirements for the multipurpose small reactor. (2) Modular-sized reactor (a) In order that modular-sized reactor could be competitive to 3200MWe twin plant (two large monolithic reactor) with 200kyenWe, the target capital cost of FOAK is estimated to be 260kyen/yenWe for 800MWe modular, 280kyen/yenWe for 400MWe modular and 290kyen/yenWe for 200MWe by taking account of the leaning effect. (b) As the result of the review on the current designs of modular-sized FRs in Japan and USA (S-PRISM) from the viewpoint of economic improvement, since it only be necessary to make further effort for the target capital cost of FOAK, since the modular-sized FRs requires a large amount of material for shielding, vessels and heat exchangers essentially. (author)

76 FR 27935 - Small Business Size Standards: Transportation and Warehousing

Science.gov (United States)

2011-05-13

... assistance, SBA establishes small business definitions (referred to as size standards) for private sector... SMALL BUSINESS ADMINISTRATION 13 CFR Part 121 RIN 3245-AG08 Small Business Size Standards: Transportation and Warehousing AGENCY: U.S. Small Business Administration. ACTION: Proposed rule. SUMMARY: The U...

Efficient silver modification of TiO2 nanotubes with enhanced photocatalytic activity

Science.gov (United States)

Huang, Jing; Ding, Lei; Xi, Yaoning; Shi, Liang; Su, Ge; Gao, Rongjie; Wang, Wei; Dong, Bohua; Cao, Lixin

2018-06-01

In this paper, Ag(CH3NH2)2+, Ag(NH3)2+ and Ag+ with different radii have been used as silver sources to find out the distribution of Ag ions on the H-TNT surface, which is critical to the final performance. The influence of this distribution on visible photocatalytic activity is further studied. The results indicate that, when Ag+ used as silver source with low concentration, these small sized silver ions mainly distribute on interlayer spacing of H-TNT. After heat-treatment and photo-reduction, the generated silver nanoparticles uniformly embed in the anatase TiO2 nanotube walls, and bring large interfacial area between Ag particles and TiO2 nanotubes. The separation effect of photogenerated electron-hole pair in TiO2 is enhanced by Ag particles, and achieves the best at 0.15 g/L, much higher than P25, TiO2/0, Ag-N@TiO2 and Ag-C-N@TiO2. This paper provides new ideas for the modification of TiO2 nanotubes.

Chironomid midges (Diptera, chironomidae) show extremely small genome sizes.

Science.gov (United States)

Cornette, Richard; Gusev, Oleg; Nakahara, Yuichi; Shimura, Sachiko; Kikawada, Takahiro; Okuda, Takashi

2015-06-01

Chironomid midges (Diptera; Chironomidae) are found in various environments from the high Arctic to the Antarctic, including temperate and tropical regions. In many freshwater habitats, members of this family are among the most abundant invertebrates. In the present study, the genome sizes of 25 chironomid species were determined by flow cytometry and the resulting C-values ranged from 0.07 to 0.20 pg DNA (i.e. from about 68 to 195 Mbp). These genome sizes were uniformly very small and included, to our knowledge, the smallest genome sizes recorded to date among insects. Small proportion of transposable elements and short intron sizes were suggested to contribute to the reduction of genome sizes in chironomids. We discuss about the possible developmental and physiological advantages of having a small genome size and about putative implications for the ecological success of the family Chironomidae.

The causal effect of board size in the performance of small and medium-sized firms

DEFF Research Database (Denmark)

Bennedsen, Morten; Kongsted, Hans Christian; Meisner Nielsen, Kasper

2008-01-01

correlation between family size and board size and show this correlation to be driven by firms where the CEO's relatives serve on the board. Second, we find empirical evidence of a small adverse board size effect driven by the minority of small and medium-sized firms that are characterized by having......Empirical studies of large publicly traded firms have shown a robust negative relationship between board size and firm performance. The evidence on small and medium-sized firms is less clear; we show that existing work has been incomplete in analyzing the causal relationship due to weak...... identification strategies. Using a rich data set of almost 7000 closely held corporations we provide a causal analysis of board size effects on firm performance: We use a novel instrument given by the number of children of the chief executive officer (CEO) of the firms. First, we find a strong positive...

Catalytic wet oxidation of ammonia solution: Activity of the nanoscale platinum-palladium-rhodium composite oxide catalyst

International Nuclear Information System (INIS)

Hung, C.-M.

2009-01-01

Aqueous solutions of 400-1000 mg/L of ammonia were oxidized in a trickle-bed reactor (TBR) in this study of nanoscale platinum-palladium-rhodium composite oxide catalysts, which were prepared by the co-precipitation of H 2 PtCl 6 , Pd(NO 3 ) 3 and Rh(NO 3 ) 3 . Hardly any of the dissolved ammonia was removed by wet oxidation in the absence of any catalyst, whereas about 99% of the ammonia was reduced during wet oxidation over nanoscale platinum-palladium-rhodium composite oxide catalysts at 503 K in an oxygen partial pressure of 2.0 MPa. A synergistic effect exists in the nanoscale platinum-palladium-rhodium composite structure, which is the material with the highest ammonia reduction activity. The nanometer-sized particles were characterized by TEM, XRD and FTIR. The effect of the initial concentration and reaction temperature on the removal of ammonia from the effluent streams was also studied at a liquid hourly space velocity of under 9 h -1 in the wet catalytic processes

Catalytic wet oxidation of ammonia solution: Activity of the nanoscale platinum-palladium-rhodium composite oxide catalyst

Energy Technology Data Exchange (ETDEWEB)

Hung, C.-M. [Department of Industry Engineering and Management, Yung-Ta Institute of Technology and Commerce, 316 Chung-shan Road, Linlo, Pingtung 909, Taiwan (China)], E-mail: hungcm1031@gmail.com

2009-04-15

Aqueous solutions of 400-1000 mg/L of ammonia were oxidized in a trickle-bed reactor (TBR) in this study of nanoscale platinum-palladium-rhodium composite oxide catalysts, which were prepared by the co-precipitation of H{sub 2}PtCl{sub 6}, Pd(NO{sub 3}){sub 3} and Rh(NO{sub 3}){sub 3}. Hardly any of the dissolved ammonia was removed by wet oxidation in the absence of any catalyst, whereas about 99% of the ammonia was reduced during wet oxidation over nanoscale platinum-palladium-rhodium composite oxide catalysts at 503 K in an oxygen partial pressure of 2.0 MPa. A synergistic effect exists in the nanoscale platinum-palladium-rhodium composite structure, which is the material with the highest ammonia reduction activity. The nanometer-sized particles were characterized by TEM, XRD and FTIR. The effect of the initial concentration and reaction temperature on the removal of ammonia from the effluent streams was also studied at a liquid hourly space velocity of under 9 h{sup -1} in the wet catalytic processes.

Catalytic wet oxidation of ammonia solution: activity of the nanoscale platinum-palladium-rhodium composite oxide catalyst.

Science.gov (United States)

Hung, Chang-Mao

2009-04-15

Aqueous solutions of 400-1000 mg/L of ammonia were oxidized in a trickle-bed reactor (TBR) in this study of nanoscale platinum-palladium-rhodium composite oxide catalysts, which were prepared by the co-precipitation of H(2)PtCl(6), Pd(NO(3))(3) and Rh(NO(3))(3). Hardly any of the dissolved ammonia was removed by wet oxidation in the absence of any catalyst, whereas about 99% of the ammonia was reduced during wet oxidation over nanoscale platinum-palladium-rhodium composite oxide catalysts at 503 K in an oxygen partial pressure of 2.0 MPa. A synergistic effect exists in the nanoscale platinum-palladium-rhodium composite structure, which is the material with the highest ammonia reduction activity. The nanometer-sized particles were characterized by TEM, XRD and FTIR. The effect of the initial concentration and reaction temperature on the removal of ammonia from the effluent streams was also studied at a liquid hourly space velocity of under 9 h(-1) in the wet catalytic processes.

Enhancing the performance of single-chambered microbial fuel cell using manganese/palladium and zirconium/palladium composite cathode catalysts.

Science.gov (United States)

Jadhav, Dipak A; Deshpande, Parag A; Ghangrekar, Makarand M

2017-08-01

Application of ZrO 2 , MnO 2 , palladium, palladium-substituted-zirconium oxide (Zr 0.98 Pd 0.02 O 2 ) and palladium-substituted-manganese oxide (Mn 0.98 Pd 0.02 O 2 ) cathode catalysts in a single-chambered microbial fuel cell (MFC) was explored. The highest power generation (1.28W/m 3 ) was achieved in MFC with Mn 0.98 Pd 0.02 O 2 catalyst, which was higher than that with MnO 2 (0.58W/m 3 ) alone; whereas, MFC having Zr 0.98 Pd 0.02 O 2 catalyzed cathode and non-catalyzed cathode produced powers of 1.02 and 0.23W/m 3 , respectively. Also, low-cost zirconium-palladium-composite showed better catalytic activity and capacitance over ZrO 2 with 20A/m 3 current production and demonstrated its suitability for MFC applications. Cyclic voltammetry analyses showed higher well-defined redox peaks in composite catalysts (Mn/Zr-Pd-C) over other catalyzed MFCs containing MnO 2 or ZrO 2 . Electrochemical behaviour of composite catalysts on cathode showed higher availability of adsorption sites for oxygen reduction and, hence, enhanced the rate of cathodic reactions. Thus, Mn/Zr-Pd-C-based composite catalysts exhibited superior cathodic performance and could be proposed as alternatives to costly Pd-catalyst for field applications. Copyright © 2017 Elsevier Ltd. All rights reserved.

Facile synthesis of bacitracin-templated palladium nanoparticles with superior electrocatalytic activity

Science.gov (United States)

Li, Yanji; Wang, Zi; Li, Xiaoling; Yin, Tian; Bian, Kexin; Gao, Faming; Gao, Dawei

2017-02-01

Palladium nanomaterials have attracted great attention on the development of electrocatalysts for fuel cells. Herein, we depicted a novel strategy in the synthesis of palladium nanoparticles with superior electrocatalytic activity. The new approach, based on the self-assembly of bacitracin biotemplate and palladium salt for the preparation of bacitracin-palladium nanoparticles (Bac-PdNPs), was simple, low-cost, and green. The complex, composed by a series of spherical Bac-PdNPs with a diameter of 70 nm, exhibited a chain-liked morphology in TEM and a face-centered cubic crystal structure in X-Ray diffraction and selected area electron diffraction. The palladium nanoparticles were mono-dispersed and stable in aqueous solution as shown in TEM and zeta potential. Most importantly, compared to the commercial palladium on carbon (Pd/C) catalyst (8.02 m2 g-1), the Bac-PdNPs showed a larger electrochemically active surface area (47.57 m2 g-1), which endowed the products an excellent electrocatalytic activity for ethanol oxidation in alkaline medium. The strategy in synthesis of Bac-PdNPs via biotemplate approach might light up new ideas in anode catalysts for direct ethanol fuel cells.

System design study of a membrane reforming hydrogen production plant using a small sized sodium cooled reactor

International Nuclear Information System (INIS)

Chikazawa, Y.; Konomura, M.; Hori, T.; Sato, H.; Uchida, S.

2004-01-01

In this study, a membrane reforming hydrogen production plant using a small sized sodium cooled reactor was designed as one of promising concepts. In the membrane reformer, methane and steam are reformed into carbon dioxide and hydrogen with sodium heat at a temperature 500 deg-C. In the equilibrium condition, steam reforming proceeds with catalyst at a temperature more than 800 deg-C. Using membrane reformers, the steam reforming temperature can be decreased from 800 to 500 deg-C because the hydrogen separation membrane removes hydrogen selectively from catalyst area and the partial pressure of hydrogen is kept much lower than equilibrium condition. In this study, a hydrogen and electric co-production plant has been designed. The reactor thermal output is 375 MW and 25% of the thermal output is used for hydrogen production (70000 Nm 3 /h). The hydrogen production cost is estimated to 21 yen/Nm 3 but it is still higher than the economical goal (17 yen/Nm 3 ). The major reason of the high cost comes from the large size of hydrogen separation reformers because of the limit of hydrogen separation efficiency of palladium membrane. A new highly efficient hydrogen separation membrane is needed to reduce the cost of hydrogen production using membrane reformers. There is possibility of multi-tube failure in the membrane reformers. In future study, a design of measures against tube failure and elemental experiments of reaction between sodium and reforming gas will be needed. (authors)

Synthesis of Conjugated Small Molecules and Polymers by a Palladium Catalyzed Cyclopentannulation Strategy: Towards New Organic Semiconductors

Science.gov (United States)

Bheemireddy, Sambasiva Reddy

The utility of conjugated small molecules and polymers as organic semiconductors have seen a tremendous growth in research and development in academia as well as industry because of their processability and flexibility advantages in comparison to inorganic semiconductors. The extensive research over the years has produced a large number of p-type (hole conducting) and n-type (electron conducting) semiconductors that can be used to construct organic electronic devices. Of these materials, p-type semiconductors are more established and extensively studied because of the ease of preparation as well as their better general stability in comparison to n-type materials. Despite recent research into the development of n-type materials, fullerene (C60 and C 70) and its derivatives are still the predominant materials used as electron acceptors for OPV applications. By taking advantage of the electron accepting behavior of cyclopenta[hi]aceanthrylene fragment of C70, we have designed and synthesized new materials based on cyclopenta-fused polycyclic aromatic hydrocarbons (CP-PAHs). By using a newly developed palladium catalyzed cyclopentannulation methodology, 1,2,6,7- tetraarylcyclopenta[hi]aceanthrylenes were prepared by treating diarylethynylenes with 9,10-dibromoanthracene. Scholl cyclodehydrogenation was used to close the externally fused aryl groups to provide access to contorted 2,7,13,18- tetraalkoxytetrabenzo[f,h,r,t]rubicenes. The contortion provides access to more soluble materials than their planar counterparts but still ii allows significant pi-pi stacking between molecules. Using a modified palladium catalyzed cyclopentannulation polymerization followed by a cyclodehydrogenation reaction, a nonconventional synthesis of CP-PAH embedded ladder polymers was also achieved. These ladder polymers possess broad UV-Vis absorptions and narrow optical gaps of 1.17-1.29 eV. The synthesis of new donor-acceptor copolymers incorporating electron accepting 1,2,6,7- tetra(4

Factors influencing the preparation of silver-coated glass frit with polyvinyl-pyrrolidone

Science.gov (United States)

Xiang, Feng; Gan, Weiping

2018-01-01

In this work, a new electroless silver plating method for the synthesis of silver-coated glass frit composite powders with good morphology has been proposed and the polyvinyl-pyrrolidone (PVP) was used the activating agent. It was found that the weight ratio of PVP to glass frit affected the distribution and number of silver nanoparticles. Moreover, the loading capacity of the glass frit, the pH value and reaction temperature could influence the size of the silver nanoparticles and morphology of silver on the surface of glass frit. The as-prepared silver-coated glass frit was used to prepare a silver paste using an optimized process to form silver nanoparticles with uniform size and high density. The silver paste with silver-coated glass frit increased the photovoltaic conversion efficiency of silicon solar cells by 0.271% compared with the silver paste prepared with pure glass frit. The silver nanoparticles can promoted the precipitation of Ag crystallites on the silicon wafer. Therefore, the silver-coated glass frit can further optimize and enhance the electrical performance of solar cells.

A new metal electrocatalysts supported matrix: Palladium nanoparticles supported silicon carbide nanoparticles and its application for alcohol electrooxidation

International Nuclear Information System (INIS)

Dai Hong; Chen Yanling; Lin Yanyu; Xu Guifang; Yang Caiping; Tong Yuejin; Guo Longhua; Chen Guonan

2012-01-01

In this paper, we propose a facile approach for palladium nanoparticles load using silicon carbide nanoparticles as the new supported matrix and a familiar NaBH 4 as reducer. Detailed X-ray photoelectron spectrum (XPS) and transmission electron microscopy (TEM) analysis of the resultant products indicated that palladium nanoparticles are successfully immobilized onto the surface of the silicon carbide nanoparticles with uniform size distribution between 5 and 7 nm. The relative electrochemical characterization clearly demonstrated excellent electrocatalytic activity of this material toward alcohol in alkaline electrolytes. Investigation on the characteristics of the electrocatalytic activity of this material further indicated that the palladium nanoparticles supporting on SiC are very promising for direct alcohol fuel cells (DMFCs), biosensor and electronic devices. Moreover, it was proved that silicon carbide nanoparticles with outstanding properties as support for catalysis are of strong practical interest. And the silicon carbide could perform attractive role in adsorbents, electrodes, biomedical applications, etc.

Gold and palladium adsorption from leached electronic scrap using ordered mesoporous carbon nanoscaffolds

Energy Technology Data Exchange (ETDEWEB)

McDowell, Rocklan; Dutech, Guy

2014-09-01

Ordered mesoporous carbon (OMC) nanoscaffolds are engineered agglomerates of carbon nanotubes held together by small carbon nanofibers with uniform pore sizes, high pore volume, and high channel permeability. These materials exhibit very high affinity for the adsorption of gold from aqueous acidic mixtures. The efficiency of gold recovery is comparable to those typically accomplished using biopolymer-based adsorbents. The adsorption efficiency for other precious metals such as palladium and platinum is lower. Studies on the precious metal (Au, Pd) adsorption on OMC materials from actual liquors of leached electronics will be presented. Adsorption properties will be compared for several different sorbents used for the recovery of precious metals. The leach liquor compositions for three different types of electronic scrap materials (personal computer board, cell phone and tv input/output board) will be presented. The sorption efficiencies for Au, Pd, together with a spectrum of competing and non-competing metals, from such leach mixtures will be compared.

Gold and palladium adsorption from leached electronic scrap using ordered mesoporous carbon nanoscaffolds

International Nuclear Information System (INIS)

McDowell, Rocklan; Dutech, Guy

2014-01-01

Ordered mesoporous carbon (OMC) nanoscaffolds are engineered agglomerates of carbon nanotubes held together by small carbon nanofibers with uniform pore sizes, high pore volume, and high channel permeability. These materials exhibit very high affinity for the adsorption of gold from aqueous acidic mixtures. The efficiency of gold recovery is comparable to those typically accomplished using biopolymer-based adsorbents. The adsorption efficiency for other precious metals such as palladium and platinum is lower. Studies on the precious metal (Au, Pd) adsorption on OMC materials from actual liquors of leached electronics will be presented. Adsorption properties will be compared for several different sorbents used for the recovery of precious metals. The leach liquor compositions for three different types of electronic scrap materials (personal computer board, cell phone and tv input/output board) will be presented. The sorption efficiencies for Au, Pd, together with a spectrum of competing and non-competing metals, from such leach mixtures will be compared.

Porous palladium coated conducting polymer nanoparticles for ultrasensitive hydrogen sensors

Science.gov (United States)

Lee, Jun Seop; Kim, Sung Gun; Cho, Sunghun; Jang, Jyongsik

2015-12-01

Hydrogen, a clean-burning fuel, is of key importance to various industrial applications, including fuel cells and in the aerospace and automotive industries. However, hydrogen gas is odorless, colorless, and highly flammable; thus appropriate safety protocol implementation and monitoring are essential. Highly sensitive hydrogen leak detection and surveillance sensor systems are needed; additionally, the ability to maintain uniformity through repetitive hydrogen sensing is becoming increasingly important. In this report, we detail the fabrication of porous palladium coated conducting polymer (3-carboxylate polypyrrole) nanoparticles (Pd@CPPys) to detect hydrogen gas. The Pd@CPPys are produced by means of facile alkyl functionalization and chemical reduction of a pristine 3-carboxylate polypyrrole nanoparticle-contained palladium precursor (PdCl2) solution. The resulting Pd@CPPy-based sensor electrode exhibits ultrahigh sensitivity (0.1 ppm) and stability toward hydrogen gas at room temperature due to the palladium sensing layer.Hydrogen, a clean-burning fuel, is of key importance to various industrial applications, including fuel cells and in the aerospace and automotive industries. However, hydrogen gas is odorless, colorless, and highly flammable; thus appropriate safety protocol implementation and monitoring are essential. Highly sensitive hydrogen leak detection and surveillance sensor systems are needed; additionally, the ability to maintain uniformity through repetitive hydrogen sensing is becoming increasingly important. In this report, we detail the fabrication of porous palladium coated conducting polymer (3-carboxylate polypyrrole) nanoparticles (Pd@CPPys) to detect hydrogen gas. The Pd@CPPys are produced by means of facile alkyl functionalization and chemical reduction of a pristine 3-carboxylate polypyrrole nanoparticle-contained palladium precursor (PdCl2) solution. The resulting Pd@CPPy-based sensor electrode exhibits ultrahigh sensitivity (0.1 ppm

Effects of different operating parameters on the particle size of silver chloride nanoparticles prepared in a spinning disk reactor

Science.gov (United States)

Dabir, Hossein; Davarpanah, Morteza; Ahmadpour, Ali

2015-07-01

The aim of this research was to present an experimental method for large-scale production of silver chloride nanoparticles using spinning disk reactor. Silver nitrate and sodium chloride were used as the reactants, and the protecting agent was gelatin. The experiments were carried out in a continuous mode by injecting the reactants onto the surface of the spinning disk, where a chemical precipitation reaction took place to form AgCl particles. The effects of various operating variables, including supersaturation, disk rotational speed, reactants flow rate, disk diameter, and excess ions, on the particle size of products were investigated. In addition, the AgCl nanoparticles were characterized by scanning electron microscopy, energy-dispersive X-ray spectroscopy, and X-ray diffraction. According to the results, smaller AgCl particles are obtained under higher supersaturations and also higher disk rotation speeds. Moreover, in the range of our investigation, the use of lower reactants flow rates and larger disk diameter can reduce the particle size of products. The non-stoichiometric condition of reactants has a significant influence on the reduction in particle aggregation. It was also found that by optimizing the operating conditions, uniform AgCl nanoparticles with the mean size of around 37 nm can be produced.

Investigation of antibacterial activity of cotton fabric incorporating nano silver colloid

International Nuclear Information System (INIS)

Ngo Vo Ke Thanh; Nguyen Thi Phuong Phong

2009-01-01

In this work, silver nanoparticles were prepared by polyol process with microwave heating and incorporated on cotton fabric surfaces. The antibacterial performance of the antibacterial cotton fabric was tested for different concentration of nano-sized silver colloid, contact time germs, and washing times. It was found that antibacterial activity increased with the increasing concentration of nano-sized silver colloid. The antibacterial fabric with 758 mg/kg of silver nanoparticles on surface cotton was highly effective in killing test bacteria and had excellent water resisting property.

Highly bacterial resistant silver nanoparticles: synthesis and antibacterial activities

International Nuclear Information System (INIS)

Chudasama, Bhupendra; Vala, Anjana K.; Andhariya, Nidhi; Mehta, R. V.; Upadhyay, R. V.

2010-01-01

In this article, we describe a simple one-pot rapid synthesis route to produce uniform silver nanoparticles by thermal reduction of AgNO 3 using oleylamine as reducing and capping agent. To enhance the dispersal ability of as-synthesized hydrophobic silver nanoparticles in water, while maintaining their unique properties, a facile phase transfer mechanism has been developed using biocompatible block co-polymer pluronic F-127. Formation of silver nanoparticles is confirmed by X-ray diffraction (XRD), transmission electron microscopy (TEM) and UV-vis spectroscopy. Hydrodynamic size and its distribution are obtained from dynamic light scattering (DLS). Hydrodynamic size and size distribution of as-synthesized and phase transferred silver nanoparticles are 8.2 ± 1.5 nm (σ = 18.3%) and 31.1 ± 4.5 nm (σ = 14.5%), respectively. Antimicrobial activities of hydrophilic silver nanoparticles is tested against two Gram positive (Bacillus megaterium and Staphylococcus aureus), and three Gram negative (Escherichiacoli, Proteusvulgaris and Shigellasonnei) bacteria. Minimum inhibitory concentration (MIC) values obtained in the present study for the tested microorganisms are found much better than those reported for commercially available antibacterial agents.

Highly bacterial resistant silver nanoparticles: synthesis and antibacterial activities

Energy Technology Data Exchange (ETDEWEB)

Chudasama, Bhupendra, E-mail: bnchudasama@gmail.co [Thapar University, School of Physics and Materials Science (India); Vala, Anjana K.; Andhariya, Nidhi; Mehta, R. V. [Bhavnagar University, Department of Physics (India); Upadhyay, R. V. [Charotar University of Science and Technology, P.D. Patel Institute of Applied Sciences (India)

2010-06-15

In this article, we describe a simple one-pot rapid synthesis route to produce uniform silver nanoparticles by thermal reduction of AgNO{sub 3} using oleylamine as reducing and capping agent. To enhance the dispersal ability of as-synthesized hydrophobic silver nanoparticles in water, while maintaining their unique properties, a facile phase transfer mechanism has been developed using biocompatible block co-polymer pluronic F-127. Formation of silver nanoparticles is confirmed by X-ray diffraction (XRD), transmission electron microscopy (TEM) and UV-vis spectroscopy. Hydrodynamic size and its distribution are obtained from dynamic light scattering (DLS). Hydrodynamic size and size distribution of as-synthesized and phase transferred silver nanoparticles are 8.2 {+-} 1.5 nm ({sigma} = 18.3%) and 31.1 {+-} 4.5 nm ({sigma} = 14.5%), respectively. Antimicrobial activities of hydrophilic silver nanoparticles is tested against two Gram positive (Bacillus megaterium and Staphylococcus aureus), and three Gram negative (Escherichiacoli, Proteusvulgaris and Shigellasonnei) bacteria. Minimum inhibitory concentration (MIC) values obtained in the present study for the tested microorganisms are found much better than those reported for commercially available antibacterial agents.

Thermal decomposition process of silver behenate

International Nuclear Information System (INIS)

Liu Xianhao; Lu Shuxia; Zhang Jingchang; Cao Weiliang

2006-01-01

The thermal decomposition processes of silver behenate have been studied by infrared spectroscopy (IR), X-ray diffraction (XRD), combined thermogravimetry-differential thermal analysis-mass spectrometry (TG-DTA-MS), transmission electron microscopy (TEM) and UV-vis spectroscopy. The TG-DTA and the higher temperature IR and XRD measurements indicated that complicated structural changes took place while heating silver behenate, but there were two distinct thermal transitions. During the first transition at 138 deg. C, the alkyl chains of silver behenate were transformed from an ordered into a disordered state. During the second transition at about 231 deg. C, a structural change took place for silver behenate, which was the decomposition of silver behenate. The major products of the thermal decomposition of silver behenate were metallic silver and behenic acid. Upon heating up to 500 deg. C, the final product of the thermal decomposition was metallic silver. The combined TG-MS analysis showed that the gas products of the thermal decomposition of silver behenate were carbon dioxide, water, hydrogen, acetylene and some small molecule alkenes. TEM and UV-vis spectroscopy were used to investigate the process of the formation and growth of metallic silver nanoparticles

Involvement of small and medium-sized enterprises (SMEs in elaborating and implementing public policies: Study case-Romanian small and medium-sized enterprises

Directory of Open Access Journals (Sweden)

Popescu Ruxandra

2017-07-01

Full Text Available Involvement and development of the private sector in boosting the economy nationwide is a main objective of the current program of the government, which means that a good cooperation between small and medium companies, private companies and multinationals and public environment including both public institutions and policies implemented and developed by them, becomes more than necessary. The paper summarizes the findings of a quantitative research based on a self-applied questionnaire which was aimed at Romanian small and medium-sized enterprises and also of a qualitative research that gives an overview of the process of elaborating and implementing a public policy. The involvement of small and medium-sized enterprises in the process of designing and implementing a public policy can become indispensable but it is well know that there is, in fact, a lack of initiative at this level, from both parties. One of the main research questions of this paper is to find out how much do representatives of small and medium-sized enterprises get involved in the process of elaborating a public policy and how much do these actions and measures impact the organizational policies of the companies themselves. A good cooperation between the business environment and the public institutions and a strong correlation of their joint efforts, should become a common practice between both parties, being crucial that this form of cooperation to be initiated from the very beginning. The contribution of this paper is a practical one, given the fact that the paper itself entails the direct responses of small and medium-sized enterprises on the current and future public policies that directly targets them, providing as well an analysis on the effects of public policies on small and medium-sized enterprises. Thus being said, the paper can also be a guide for both small and medium-sized enterprises in providing examples and measures of involvement and favorable public policies

Shape- and Size-Controlled Synthesis of Silver Nanoparticles Using Aloe vera Plant Extract and Their Antimicrobial Activity

Science.gov (United States)

Logaranjan, Kaliyaperumal; Raiza, Anasdass Jaculin; Gopinath, Subash C. B.; Chen, Yeng; Pandian, Kannaiyan

2016-11-01

Biogenic synthesis of silver nanoparticles (AgNP) was performed at room temperature using Aloe vera plant extract in the presence of ammoniacal silver nitrate as a metal salt precursor. The formation of AgNP was monitored by UV-visible spectroscopy at different time intervals. The shape and size of the synthesized particle were visualized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM) observations. These results were confirmed by X-ray powder diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) analyses and further supported by surface-enhanced Raman spectroscopy/Raman scattering (SERS) study. UV-visible spectrum has shown a sharp peak at 420 nm and further evidenced by FTIR peak profile (at 1587.6, 1386.4, and 1076 cm-1 with corresponding compounds). The main band position with SERS was noticed at 1594 cm-1 (C-C stretching vibration). When samples were heated under microwave radiation, AgNP with octahedron shapes with 5-50 nm were found and this method can be one of the easier ways to synthesis anisotropic AgNP, in which the plant extract plays a vital role to regulate the size and shape of the nanoparticles. Enhanced antibacterial effects (two- to fourfold) were observed in the case of Aloe vera plant protected AgNP than the routinely synthesized antibiotic drugs.

Thermosonic wire bonding of IC devices using palladium wire

International Nuclear Information System (INIS)

Shze, J.H.; Poh, M.T.; Tan, R.M.

1996-01-01

The feasibility of replacing gold wire by palladium wire in thermosonic wire bonding of CMOS and bipolar devices are studied in terms of the manufacturability, physical, electrical and assembly performance. The results that palladium wire is a viable option for bonding the bipolar devices but not the CMOS devices

Preparation of silver nanoparticles at low temperature

Energy Technology Data Exchange (ETDEWEB)

Mishra, Mini, E-mail: mishramini5@gmail.com [Centre of Environmental Science, Department of Botany, University of Allahabad, Allahabad, U.P. (India); Chauhan, Pratima, E-mail: mangu167@yahoo.co.in [Department of Physics, University of Allahabad, Allahabad U.P. (India)

2016-04-13

Silver from ancient time is used as antimicrobial agent in the bulk form but now with the advancement in nanotechnology silver in the form of nanoparticles shown potential effect against microbes which make us easy to fight with many diseases plants and animals. In this work silver nanoparticles were synthesized by chemical routes using sodium borohydride as reducing agent at low temperature. The particles were characterized through UV-Visible spectroscopy as well as X-Ray Diffraction. The UV-visible spectra of silver nanoparticles exhibited absorption at 425 cm; the crystallite size of the particles is between 19nm to 39nm. EDAX graph shows two peaks of silver and oxygen. Water absorbed by silver nanoparticles was removed by the calcinations.

Preparation of silver nanoparticles at low temperature

International Nuclear Information System (INIS)

Mishra, Mini; Chauhan, Pratima

2016-01-01

Silver from ancient time is used as antimicrobial agent in the bulk form but now with the advancement in nanotechnology silver in the form of nanoparticles shown potential effect against microbes which make us easy to fight with many diseases plants and animals. In this work silver nanoparticles were synthesized by chemical routes using sodium borohydride as reducing agent at low temperature. The particles were characterized through UV-Visible spectroscopy as well as X-Ray Diffraction. The UV-visible spectra of silver nanoparticles exhibited absorption at 425 cm; the crystallite size of the particles is between 19nm to 39nm. EDAX graph shows two peaks of silver and oxygen. Water absorbed by silver nanoparticles was removed by the calcinations.

Cluster size matters: Size-driven performance of subnanometer clusters in catalysis, electrocatalysis and Li-air batteries

Science.gov (United States)

Vajda, Stefan

2015-03-01

This paper discusses the strongly size-dependent performance of subnanometer cluster based catalysts in 1) heterogeneous catalysis, 2) electrocatalysis and 3) Li-air batteries. The experimental studies are based on I. fabrication of ultrasmall clusters with atomic precision control of particle size and their deposition on oxide and carbon based supports; II. test of performance, III. in situand ex situ X-ray characterization of cluster size, shape and oxidation state; and IV.electron microscopies. Heterogeneous catalysis. The pronounced effect of cluster size and support on the performance of the catalyst (catalyst activity and the yield of Cn products) will be illustrated on the example of nickel and cobalt clusters in Fischer-Tropsch reaction. Electrocatalysis. The study of the oxygen evolution reaction (OER) on size-selected palladium clusters supported on ultrananocrystalline diamond show pronounced size effects. While Pd4 clusters show no reaction, Pd6 and Pd17 clusters are among the most active catalysts known (in in terms of turnover rate per Pd atom). The system (soft-landed Pd4, Pd6, or Pd17 clusters on an UNCD Si coated electrode) shows stable electrochemical potentials over several cycles, and the characterization of the electrodes show no evidence for evolution or dissolution of either the support Theoretical calculations suggest that this striking difference may be a demonstration that bridging Pd-Pd sites, which are only present in three-dimensional clusters, are active for the oxygen evolution reaction in Pd6O6. Li-air batteries. The studies show that sub-nm silver clusters have dramatic size-dependent effect on the lowering of the overpotential, charge capacity, morphology of the discharge products, as well as on the morphology of the nm size building blocks of the discharge products. The results suggest that by precise control of the active surface sites on the cathode, the performance of Li-air cells can be significantly improved

Absorption of hydrogen by vanadium-palladium alloys

International Nuclear Information System (INIS)

Artman, D.; Lynch, J.F.; Flanagan, T.B.

1976-01-01

Pressure composition isotherms (273-373 K) have been determined for the absorption of hydrogen by a series of six palladium alloys (f.c.c) in the composition range from 1 to 8 at.% vanadium. At a given hydrogen content, the equilibrium hydrogen pressure progressively increases with vanadium content. Thermodynamic parameters for the absorption of hydrogen are reported at infinite dilution of hydrogen and for the formation of the nonstoichiometric hydride from the hydrogen-saturated alloy. The relative, partial molar enthalpy of solution of hydrogen at infinite dilution increases slightly with vanadium content. The presence of vanadium, which absorbs hydrogen itself in its normal b.c.c. structure, greatly inhibits the ability of palladium to absorb hydrogen. For example, the isobaric solubility of hydrogen (1 atm, 298K) decreases from H/Pd=0.7 (palladium) to 0.024 (V(6%)-Pd). The lattice expansion due to the presence of interstitial hydrogen has been determined by X-ray diffraction. From these data it can be concluded that the formation of two non-stoichiometric hydride phases does not occur at vanadium contents greater that 5 at.% (298 K). Electrical resistance has been measured as a function of the hydrogen content of the alloys. The electrical resistance increases more markedly with hydrogen content for these alloys than for any of the palladium alloys previously examined. (Auth.)

Growth of nanoparticles in hydrogen-implanted palladium subsurfaces

International Nuclear Information System (INIS)

Okuyama, F.

2010-01-01

Solid particles with nanometric dimensions are shown to grow in the opened subsurface of a polycrystalline palladium (Pd) hydrogen-implanted at around 500 C. The particles are Pd in main composition and densely grown on sloping walls of fissured grain boundaries or cracks. The average grain size increases from deeper to shallow regions, suggesting that a negative temperature gradient toward the surface existed along the crack walls. The nanoparticles are certain to arise from the condensation of Pd vapors on the walls, forcing us to assume that hydrogen atoms implanted in an overpopulation heated their implantation zone so strongly as to vaporize Pd. (orig.)

Growth of nanoparticles in hydrogen-implanted palladium subsurfaces

Energy Technology Data Exchange (ETDEWEB)

Okuyama, F. [Nagoya Institute of Technology, Graduate School of Engineering, Nagoya (Japan)

2010-07-15

Solid particles with nanometric dimensions are shown to grow in the opened subsurface of a polycrystalline palladium (Pd) hydrogen-implanted at around 500 C. The particles are Pd in main composition and densely grown on sloping walls of fissured grain boundaries or cracks. The average grain size increases from deeper to shallow regions, suggesting that a negative temperature gradient toward the surface existed along the crack walls. The nanoparticles are certain to arise from the condensation of Pd vapors on the walls, forcing us to assume that hydrogen atoms implanted in an overpopulation heated their implantation zone so strongly as to vaporize Pd. (orig.)

Superparamagnetic bimetallic iron-palladium nanoalloy: synthesis and characterization

Energy Technology Data Exchange (ETDEWEB)

Nazir, Rabia; Mazhar, Muhammad [Department of Chemistry, Quaid-i-Azam University, Islamabad 45320 (Pakistan); Akhtar, M Javed; Nadeem, M; Siddique, Muhammad [Physics Division, PINSTECH, PO Nilore, Islamabad 44000 (Pakistan); Shah, M Raza [HEJ Research Institute of Chemistry, University of Karachi, Karachi 75270 (Pakistan); Khan, Nawazish A [Material Science Laboratory, Department of Physics, Quaid-i-Azam University, Islamabad 45320 (Pakistan); Mehmood, Mazhar [National Centre for Nanotechnology, PIEAS, Islamabad 45650 (Pakistan); Butt, N M [Pakistan Science Foundation, Islamabad 44000 (Pakistan)], E-mail: mazhar42pk@yahoo.com

2008-05-07

Iron-palladium nanoalloy in the particle size range of 15-30 nm is synthesized by the relatively low temperature thermal decomposition of coprecipitated [Fe(Bipy){sub 3}]Cl{sub 2} and [Pd(Bipy){sub 3}]Cl{sub 2} in an inert ambient of dry argon gas. The silvery black Fe-Pd alloy nanoparticles are air-stable and have been characterized by EDX-RF, XRD, AFM, TEM, magnetometry, {sup 57}Fe Moessbauer and impedance spectroscopy. This Fe-Pd nanoalloy is in single phase and contains iron sites having up to 11 nearest-neighboring atoms. It is superparamagnetic in nature with high magnetic susceptibility, low coercivity and hyperfine field.

76 FR 14323 - Small Business Size Standards: Professional, Scientific and Technical Services

Science.gov (United States)

2011-03-16

... government small business assistance programs, SBA establishes small business size definitions (referred to... its field of operation and (3) within a specific small business definition or size standard... SMALL BUSINESS ADMINISTRATION 13 CFR Part 121 RIN 3245-AG07 Small Business Size Standards...

Sponge-like silver obtained by decomposition of silver nitrate hexamethylenetetramine complex

International Nuclear Information System (INIS)

Afanasiev, Pavel

2016-01-01

Silver nitrate hexamethylenetetramine [Ag(NO 3 )·N 4 (CH 2 ) 6 ] coordination compound has been prepared via aqueous route and characterized by chemical analysis, XRD and electron microscopy. Decomposition of [Ag(NO 3 )·N 4 (CH 2 ) 6 ] under hydrogen and under inert has been studied by thermal analysis and mass spectrometry. Thermal decomposition of [Ag(NO 3 )·N 4 (CH 2 ) 6 ] proceeds in the range 200–250 °C as a self-propagating rapid redox process accompanied with the release of multiple gases. The decomposition leads to formation of sponge-like silver having hierarchical open pore system with pore size spanning from 10 µm to 10 nm. The as-obtained silver sponges exhibited favorable activity toward H 2 O 2 electrochemical reduction, making them potentially interesting as non-enzyme hydrogen peroxide sensors. - Graphical abstract: Thermal decomposition of silver nitrate hexamethylenetetramine coordination compound [Ag(NO 3 )·N 4 (CH 2 ) 6 ] leads to sponge like silver that possesses open porous structure and demonstrates interesting properties as an electrochemical hydrogen peroxide sensor. Display Omitted - Highlights: • [Ag(NO 3 )·N 4 (CH 2 ) 6 ] orthorhombic phase prepared and characterized. • Decomposition of [Ag(NO 3 )·N 4 (CH 2 ) 6 ] leads to metallic silver sponge with opened porosity. • Ag sponge showed promising properties as a material for hydrogen peroxide sensors.

Nano-palladium is a cellular catalyst for in vivo chemistry

Science.gov (United States)

Miller, Miles A.; Askevold, Bjorn; Mikula, Hannes; Kohler, Rainer H.; Pirovich, David; Weissleder, Ralph

2017-07-01

Palladium catalysts have been widely adopted for organic synthesis and diverse industrial applications given their efficacy and safety, yet their biological in vivo use has been limited to date. Here we show that nanoencapsulated palladium is an effective means to target and treat disease through in vivo catalysis. Palladium nanoparticles (Pd-NPs) were created by screening different Pd compounds and then encapsulating bis[tri(2-furyl)phosphine]palladium(II) dichloride in a biocompatible poly(lactic-co-glycolic acid)-b-polyethyleneglycol platform. Using mouse models of cancer, the NPs efficiently accumulated in tumours, where the Pd-NP activated different model prodrugs. Longitudinal studies confirmed that prodrug activation by Pd-NP inhibits tumour growth, extends survival in tumour-bearing mice and mitigates toxicity compared to standard doxorubicin formulations. Thus, here we demonstrate safe and efficacious in vivo catalytic activity of a Pd compound in mammals.

Green synthesis of silver nanoparticles: The reasons for and against Aspergillus parasiticus

Directory of Open Access Journals (Sweden)

Maryam Moazeni

2014-09-01

Full Text Available Abstract Objective(s: The enzymatic activity of fungi has recently inspired the scientists with re-explore the fungi as potential biofactories rather than the causing agents of humans and plants infections. In very recent years, fungi are considered as worthy, applicable and available candidates for synthesis of smaller gold, silver and other nano-sized particles. Materials and Methods: A standard strain of Aspergillus parasiticus was grown on a liquid medium containing mineral salt. The cell-free filtrate of the culture was then obtained and subjected to synthesize SNPs while expose with 1mM of AgNO 3. Further characterization of synthesized SNPs was performed afterward. In addition, antifungal activity of synthesized SNPs was evaluated against a standard strain of Candida albicans. The reduction of Ag+ ions to metal nanoparticles was investigated virtually by tracing the color of the solution which turned into reddish-brown after 72h. Results: The UV-vis spectra demonstrated a broad peak centering at 400nm which corresponds to the particle size much less than 70nm. The results of TEM demonstrated that the particles were formed fairly uniform, spherical, and small in size with almost 90% in 5-30nm range. The zeta potential of silver nanoparticles was negative and equal to -15.0 which meets the quality and suggested that there was not much aggression. Silver nanoparticles synthesized by A. parasiticus showed antifungal activity against yeast strain tested an d exhibited MIC value of 4 μg/mL. Conclusion: The filamentous fungus, A. parasiticus has successfully demonstrated potential for extra cellular synthesis of fairly monodispersed, tiny silver nanoparticles.

Size and Aging Effects on Antimicrobial Efficiency of Silver Nanoparticles Coated on Polyamide Fabrics Activated by Atmospheric DBD Plasma.

Science.gov (United States)

Zille, Andrea; Fernandes, Margarida M; Francesko, Antonio; Tzanov, Tzanko; Fernandes, Marta; Oliveira, Fernando R; Almeida, Luís; Amorim, Teresa; Carneiro, Noémia; Esteves, Maria F; Souto, António P

2015-07-01

This work studies the surface characteristics, antimicrobial activity, and aging effect of plasma-pretreated polyamide 6,6 (PA66) fabrics coated with silver nanoparticles (AgNPs), aiming to identify the optimum size of nanosilver exhibiting antibacterial properties suitable for the manufacture of hospital textiles. The release of bactericidal Ag(+) ions from a 10, 20, 40, 60, and 100 nm AgNPs-coated PA66 surface was a function of the particles' size, number, and aging. Plasma pretreatment promoted both ionic and covalent interactions between AgNPs and the formed oxygen species on the fibers, favoring the deposition of smaller-diameter AgNPs that consequently showed better immediate and durable antimicrobial effects against Gram-negative Escherichia coli and Gram-positive Staphylococcus aureus bacteria. Surprisingly, after 30 days of aging, a comparable bacterial growth inhibition was achieved for all of the fibers treated with AgNPs silver. Overall, the results suggest that instead of reducing the size of the AgNPs, which is associated with higher toxicity, similar long-term effects can be achieved with larger NPs (40-60 nm), even in lower concentrations. Because the antimicrobial efficiency of AgNPs larger than 30 nm is mainly ruled by the release of Ag(+) over time and not by the size and number of the AgNPs, this parameter is crucial for the development of efficient antimicrobial coatings on plasma-treated surfaces and contributes to the safety and durability of clothing used in clinical settings.

Biogenic synthesis of silver nanoparticles by leaf extract of Cassia angustifolia

Science.gov (United States)

Amaladhas, T. Peter; Sivagami, S.; Akkini Devi, T.; Ananthi, N.; Priya Velammal, S.

2012-12-01

In this study Cassia angustifolia (senna) is used for the environmentally friendly synthesis of silver nanoparticles. Stable silver nanoparticles having symmetric surface plasmon resonance (SPR) band centred at 420 nm were obtained within 10 min at room temperature by treating aqueous solutions of silver nitrate with C. angustifolia leaf extract. The water soluble components from the leaves, probably the sennosides, served as both reducing and capping agents in the synthesis of silver nanoparticles. The nanoparticles were characterized using UV-Vis, Fourier transform infrared (FTIR) spectroscopic techniques and transmission electron microscopy (TEM). The nanoparticles were poly-dispersed, spherical in shape with particle size in the range 9-31 nm, the average size was found to be 21.6 nm at pH 11. The zeta potential was -36.4 mV and the particles were stable for 6 months. The crystalline phase of the nanoparticles was confirmed from the selected area diffraction pattern (SAED). The rate of formation and size of silver nanoparticles were pH dependent. Functional groups responsible for capping of silver nanoparticles were identified from the FTIR spectrum. The synthesized silver nanoparticles exhibited good antibacterial potential against Escherichia coli and Staphylococcus aureus.

Biogenic synthesis of silver nanoparticles by leaf extract of Cassia angustifolia

International Nuclear Information System (INIS)

Peter Amaladhas, T; Akkini Devi, T; Ananthi, N; Priya Velammal, S; Sivagami, S

2012-01-01

In this study Cassia angustifolia (senna) is used for the environmentally friendly synthesis of silver nanoparticles. Stable silver nanoparticles having symmetric surface plasmon resonance (SPR) band centred at 420 nm were obtained within 10 min at room temperature by treating aqueous solutions of silver nitrate with C. angustifolia leaf extract. The water soluble components from the leaves, probably the sennosides, served as both reducing and capping agents in the synthesis of silver nanoparticles. The nanoparticles were characterized using UV–Vis, Fourier transform infrared (FTIR) spectroscopic techniques and transmission electron microscopy (TEM). The nanoparticles were poly-dispersed, spherical in shape with particle size in the range 9–31 nm, the average size was found to be 21.6 nm at pH 11. The zeta potential was –36.4 mV and the particles were stable for 6 months. The crystalline phase of the nanoparticles was confirmed from the selected area diffraction pattern (SAED). The rate of formation and size of silver nanoparticles were pH dependent. Functional groups responsible for capping of silver nanoparticles were identified from the FTIR spectrum. The synthesized silver nanoparticles exhibited good antibacterial potential against Escherichia coli and Staphylococcus aureus. (paper)

Nanotoxicity of silver nanoparticles to red blood cells: size dependent adsorption, uptake, and hemolytic activity.

Science.gov (United States)

Chen, Li Qiang; Fang, Li; Ling, Jian; Ding, Cheng Zhi; Kang, Bin; Huang, Cheng Zhi

2015-03-16

Silver nanoparticles (AgNPs) are increasingly being used as antimicrobial agents and drug carriers in biomedical fields. However, toxicological information on their effects on red blood cells (RBCs) and the mechanisms involved remain sparse. In this article, we examined the size dependent nanotoxicity of AgNPs using three different characteristic sizes of 15 nm (AgNPs15), 50 nm (AgNPs50), and 100 nm (AgNPs100) against fish RBCs. Optical microscopy and transmission electron microscopy observations showed that AgNPs exhibited a size effect on their adsorption and uptake by RBCs. The middle sized AgNPs50, compared with the smaller or bigger ones, showed the highest level of adsorption and uptake by the RBCs, suggesting an optimal size of ∼50 nm for passive uptake by RBCs. The toxic effects determined based on the hemolysis, membrane injury, lipid peroxidation, and antioxidant enzyme production were fairly size and dose dependent. In particular, the smallest sized AgNPs15 displayed a greater ability to induce hemolysis and membrane damage than AgNPs50 and AgNPs100. Such cytotoxicity induced by AgNPs should be attributed to the direct interaction of the nanoparticle with the RBCs, resulting in the production of oxidative stress, membrane injury, and subsequently hemolysis. Overall, the results suggest that particle size is a critical factor influencing the interaction between AgNPs and the RBCs.

Chromatographic enrichment of isotopes in hydrogen and water samples on palladium

International Nuclear Information System (INIS)

Andreev, B.M.; Polevoi, A.S.; Perevezentsev, A.N.

1987-01-01

Data on the isotopic enrichment of hydrogen and water samples by chromatography on palladium have been analyzed. Experimental data on the effect of temperature, hydrogen flow, volume of the enriched fraction, and length of the chromatographic column on the degree of separation attainable in the column have been obtained. It has been shown that the maximum separation achievable (regardless of the type of the isotope mixture) at 273 K falls with increase of hydrogen flow and volume of the enriched gas fraction recoverable from the column. A separation degree of ∼ 1040 has been achieved for a mixture of protium and deuterium in a 10-mm wide and 0.6-m long chromatographic column packed with palladium black with a grain size of 0.2-0.5 mm at 273 K and a specific hydrogen flow of 1.22 mole/m 2 x sec. For a protium-tritium mixture a separation degree of ∼ 90 has been reached in a similar column at 273 K and a specific hydrogen flow of 0.4 mole/m 2 x sec

Selective recovery of silver from waste low-temperature co-fired ceramic and valorization through silver nanoparticle synthesis.

Science.gov (United States)

Swain, Basudev; Shin, Dongyoon; Joo, So Yeong; Ahn, Nak Kyoon; Lee, Chan Gi; Yoon, Jin-Ho

2017-11-01

Considering the value of silver metal and silver nanoparticles, the waste generated during manufacturing of low temperature co-fired ceramic (LTCC) were recycled through the simple yet cost effective process by chemical-metallurgy. Followed by leaching optimization, silver was selectively recovered through precipitation. The precipitated silver chloride was valorized though silver nanoparticle synthesis by a simple one-pot greener synthesis route. Through leaching-precipitation optimization, quantitative selective recovery of silver chloride was achieved, followed by homogeneous pure silver nanoparticle about 100nm size were synthesized. The reported recycling process is a simple process, versatile, easy to implement, requires minimum facilities and no specialty chemicals, through which semiconductor manufacturing industry can treat the waste generated during manufacturing of LTCC and reutilize the valorized silver nanoparticles in manufacturing in a close loop process. Our reported process can address issues like; (i) waste disposal, as well as value-added silver recovery, (ii) brings back the material to production stream and address the circular economy, and (iii) can be part of lower the futuristic carbon economy and cradle-to-cradle technology management, simultaneously. Copyright © 2017 Elsevier Ltd. All rights reserved.

A simple method of growing silver chloride nanocubes on silver nanowires

Science.gov (United States)

Hosseinzadeh Khaligh, Hadi; Goldthorpe, Irene A.

2015-09-01

The growth of AgCl nanocubes directly on the sidewalls of Ag nanowires is demonstrated. The nanocubes can be simply obtained through extended low temperature annealing of polyol-synthesized silver nanowires in a vacuum. The length of time and temperature of the anneal and the diameter of the nanowire affect the size and density of the nanocubes obtained. It is hypothesized that the AgCl material is supplied from reactants leftover from the silver nanowire synthesis. This novel hybrid nanostructure may have applications in areas such as photovoltaics, surface enhanced Raman spectroscopy, and photocatalysis.

Development of small-size baking oven

Energy Technology Data Exchange (ETDEWEB)

Tabata, Akihisa; Kuwabara, Shigeru; Yamazawa, Yoshitaka; Shigeta, Eiji

1987-03-01

In the bakery business, oven fresh bakeries selling fresh bread by installing their own baking ovens at their shops have become popular recently. This article reports the development of a small-size gas baking oven for oven fresh bakaries. The gas convection oven developed recently is based on the structure of the conventional electric convection oven, and uses low pressure gas. The gas oven has an advantage that the combustion gas contains moisture. The convection oven bakes bread normally at the baking density approximately 2.5 times as much as that of the radiation oven, thereby the size of the oven may become smaller. This oven can bake many kinds of bread ranging from croissants to bean-jam buns by gas combnstion heat as well as radiation heat from the radiation plates installed at the top of each compartment in the oven. An ultra small air heat type burner was developed to provide stable short flames in order to make the size of the combustion chamber smaller. (20 figs, 2 tabs)

Electron-transfer reactions of extremely small AgI colloids

International Nuclear Information System (INIS)

Vucemilovic, M.I.; Micic, O.I.

1988-01-01

Small colloidal AgI particles (particle diameter 20-50 A) have been prepared in water and acetonitrile, and optical effects due to size quantization have been observed. Electron transfer reactions involving electron donors and electron acceptors with AgI have been studied by pulse radiolysis techniques. Both reduction and oxidation of the colloids led to transient bleaching of semiconductor absorption. The recovery of the bleaching has been attributed to corrosion processes. Electrons injected into AgI colloids produce metallic silver and hydrogen. Hydrogen evolution is catalyzed by metallic silver formation. (author)

The value chain of small-sized energy wood

Energy Technology Data Exchange (ETDEWEB)

Karttunen, K.; Foehr, J.; Ranta, T. (Lappeenranta Univ. of Technology, Mikkeli (Finland), LUT Energy), Email: kalle.karttunen@lut.fi, Email: jarno.fohr@lut.fi, Email: tapio.ranta@lut.fi; Ahtikoski, A. (The Finnish Forest Research Institute, Rovaniemi (Finland)), Email: anssi.ahtikoski@metla.fi; Valsta, L. (Helsinki Univ. (Finland), Dept. of Forest Economics), Email: lauri.valsta@helsinki.fi

2009-07-01

Finland has agreed to increase the share of renewable energy to the level of 38% by the end of 2020. Most of the increase is to be based on bioenergy. According to the National Climate and Energy Strategy, the need for forest biomass will come to more than 20 TWh, or some 10 million cubic meters per year. Energy wood from young stand thinnings are the biomass resource with the most potential at the moment. The purpose of this study was to compare cost differences between forest management incorporating energy wood thinning and forest management based on traditional roundwood thinning. In addition, alternative supply chain costs for small-sized wood were studied. The results of the study show that it is worth considering the following points if the demand and average price for forest chips remain high. 1. Forest-owners: Forest management including energy wood thinning is financially feasible. 2. Supply chain: A terminal chipping chain enables large-scale procurement of small-sized energy wood. 3. Power plants: Currently, subsidies, emission trading, and decreasing pulpwood prices together enable large-scale use of small-sized wood for energy purposes. The value chain of small-sized energy wood in large-scale power plants could be mobilised. (orig.)

Palladium configuration dependence of hydrogen detection sensitivity based on graphene FET for breath analysis

Science.gov (United States)

Sakamoto, Yuri; Uemura, Kohei; Ikuta, Takashi; Maehashi, Kenzo

2018-04-01

We have succeeded in fabricating a hydrogen gas sensor based on palladium-modified graphene field-effect transistors (FETs). The negative-voltage shift in the transfer characteristics was observed with exposure to hydrogen gas, which was explained by the change in work function. The hydrogen concentration dependence of the voltage shift was investigated using graphene FETs with palladium deposited by three different evaporation processes. The results indicate that the hydrogen detection sensitivity of the palladium-modified graphene FETs is strongly dependent on the palladium configuration. Therefore, the palladium-modified graphene FET is a candidate for breath analysis.

A review of the antibacterial effects of silver nanomaterials and potential implications for human health and the environment

Science.gov (United States)

Marambio-Jones, Catalina; Hoek, Eric M. V.

2010-06-01

Here, we present a review of the antibacterial effects of silver nanomaterials, including proposed antibacterial mechanisms and possible toxicity to higher organisms. For purpose of this review, silver nanomaterials include silver nanoparticles, stabilized silver salts, silver-dendrimer, polymer and metal oxide composites, and silver-impregnated zeolite and activated carbon materials. While there is some evidence that silver nanoparticles can directly damage bacteria cell membranes, silver nanomaterials appear to exert bacteriocidal activity predominantly through release of silver ions followed (individually or in combination) by increased membrane permeability, loss of the proton motive force, inducing de-energization of the cells and efflux of phosphate, leakage of cellular content, and disruption DNA replication. Eukaryotic cells could be similarly impacted by most of these mechanisms and, indeed, a small but growing body of literature supports this concern. Most antimicrobial studies are performed in simple aquatic media or cell culture media without proper characterization of silver nanomaterial stability (aggregation, dissolution, and re-precipitation). Silver nanoparticle stability is governed by particle size, shape, and capping agents as well as solution pH, ionic strength, specific ions and ligands, and organic macromolecules—all of which influence silver nanoparticle stability and bioavailability. Although none of the studies reviewed definitively proved any immediate impacts to human health or the environment by a silver nanomaterial containing product, the entirety of the science reviewed suggests some caution and further research are warranted given the already widespread and rapidly growing use of silver nanomaterials.

A review of the antibacterial effects of silver nanomaterials and potential implications for human health and the environment

Energy Technology Data Exchange (ETDEWEB)

Marambio-Jones, Catalina; Hoek, Eric M. V., E-mail: emvhoek@ucla.ed [University of California, Los Angeles, Department of Civil and Environmental Engineering, California NanoSystems Institute (United States)

2010-06-15

Here, we present a review of the antibacterial effects of silver nanomaterials, including proposed antibacterial mechanisms and possible toxicity to higher organisms. For purpose of this review, silver nanomaterials include silver nanoparticles, stabilized silver salts, silver-dendrimer, polymer and metal oxide composites, and silver-impregnated zeolite and activated carbon materials. While there is some evidence that silver nanoparticles can directly damage bacteria cell membranes, silver nanomaterials appear to exert bacteriocidal activity predominantly through release of silver ions followed (individually or in combination) by increased membrane permeability, loss of the proton motive force, inducing de-energization of the cells and efflux of phosphate, leakage of cellular content, and disruption DNA replication. Eukaryotic cells could be similarly impacted by most of these mechanisms and, indeed, a small but growing body of literature supports this concern. Most antimicrobial studies are performed in simple aquatic media or cell culture media without proper characterization of silver nanomaterial stability (aggregation, dissolution, and re-precipitation). Silver nanoparticle stability is governed by particle size, shape, and capping agents as well as solution pH, ionic strength, specific ions and ligands, and organic macromolecules-all of which influence silver nanoparticle stability and bioavailability. Although none of the studies reviewed definitively proved any immediate impacts to human health or the environment by a silver nanomaterial containing product, the entirety of the science reviewed suggests some caution and further research are warranted given the already widespread and rapidly growing use of silver nanomaterials.

A review of the antibacterial effects of silver nanomaterials and potential implications for human health and the environment

International Nuclear Information System (INIS)

Marambio-Jones, Catalina; Hoek, Eric M. V.

2010-01-01

Here, we present a review of the antibacterial effects of silver nanomaterials, including proposed antibacterial mechanisms and possible toxicity to higher organisms. For purpose of this review, silver nanomaterials include silver nanoparticles, stabilized silver salts, silver-dendrimer, polymer and metal oxide composites, and silver-impregnated zeolite and activated carbon materials. While there is some evidence that silver nanoparticles can directly damage bacteria cell membranes, silver nanomaterials appear to exert bacteriocidal activity predominantly through release of silver ions followed (individually or in combination) by increased membrane permeability, loss of the proton motive force, inducing de-energization of the cells and efflux of phosphate, leakage of cellular content, and disruption DNA replication. Eukaryotic cells could be similarly impacted by most of these mechanisms and, indeed, a small but growing body of literature supports this concern. Most antimicrobial studies are performed in simple aquatic media or cell culture media without proper characterization of silver nanomaterial stability (aggregation, dissolution, and re-precipitation). Silver nanoparticle stability is governed by particle size, shape, and capping agents as well as solution pH, ionic strength, specific ions and ligands, and organic macromolecules-all of which influence silver nanoparticle stability and bioavailability. Although none of the studies reviewed definitively proved any immediate impacts to human health or the environment by a silver nanomaterial containing product, the entirety of the science reviewed suggests some caution and further research are warranted given the already widespread and rapidly growing use of silver nanomaterials.

Activity enhancement of Ag/mordenite catalysts by addition of palladium for the removal of nitrogen oxides from diesel engine exhaust gas

Energy Technology Data Exchange (ETDEWEB)

Masuda, K.; Tsujimura, K. [New A.C.E. Institute Co., Ltd., Ibaraki (Japan); Shinoda, K.; Kato, T. [Mitsui Mining and Smelting Co., Ltd., Saitama (Japan)

1998-01-15

Various Ag-Pd/mordenite catalysts were prepared on washcoated honeycombs and tested in terms of NO{sub x} removal from diesel exhaust gas with (CH{sub 3}){sub 2}O as a reducing agent at a practical high level of space velocity. The activity was dependent upon the palladium loading. In terms of NO{sub x} removal, the order of catalytic activity was Ag(3)/Pd(0.01)/mordenite Ag(3)/Pd(0.1)/mordenite Ag(3)/mordenite catalyst Ag(3)/Pd(1.0)/mordenite. It was found that a relatively small loading of palladium on Ag/mordenite catalysts led to a significant improvement in catalytic activity over a wide range of temperatures. The properties of these catalysts were also investigated by the NH{sub 3} temperature programed desorption (TPD) and BET method. It was found that Ag(3)/Pd(0.01)/mordenite had a larger amount of acid sites. It was concluded that Ag/mordenite catalyst with a small amount of palladium can effectively remove NO{sub x} over a wide range of temperatures using (CH{sub 3}){sub 2}O as a reducing agent

Synthesis and optical properties of silver nanoparticles

Science.gov (United States)

Singh, Jaiveer; Kaurav, Netram; Choudhary, K. K.; Okram, Gunadhor S.

2015-07-01

The preparation of stable, uniform silver nanoparticles by reduction of silver acetate by ethylene glycol (EG) is reported in the present paper. It is a simple process of recent interest for obtaining silver nanoparticles. The samples were characterized by X-Ray diffraction (XRD), which reveals an average particle size (D) of 38 nm. The UV/Vis spectra show that an absorption peak, occurring due to surface plasmon resonance (SPR), exists at 319 nm.

Improving the Vase life of Cut Carnation ‘Tempo’ (Dianthus carryophyllusL. Flower by Silver Thiosulphate and Silver Nano-Particles

Directory of Open Access Journals (Sweden)

D. Hashemabadi

2014-08-01

Full Text Available Nanometer-sized silver particle can be act as an anti-microbial compound. Thus, in this research, the efficacy of silver thiosulphate and silver nano-particles as antimicrobial agents in extending the vase-life of cut carnation flowers was evaluated. A factorial experiment carried out based on randomized completely blocks design with two factors: silver thiosulphate (0, 0.1, 0.2 and 0.3 mM and silver nano-particles (0, 5, 10 and 15 mg/L. Mean comparison of the data showed that the combined treatments of 0.3 mM silver thiosulphate + 15 mg/L silver nano-particles had the highest vase life, water uptake and super oxide dismutase enzyme. Thus, the mentioned above treatment was proposed to increase prolong vase life and improvement of water relations and control of stem end blockage. Based to results of this study, silver thiosulphate and silver nano-particles can be used for increasing postharvest longevity of cut carnation "Tempo".

Controlled synthesis and characterization of hollow flower-like silver nanostructures

Directory of Open Access Journals (Sweden)

Eid KAM

2012-03-01

Full Text Available Kamel AM Eid, Hassan ME AzzazyNovel Diagnostics and Therapeutics Group, Yousef Jameel Science and Technology Research Center, School of Sciences and Engineering, The American University in Cairo, New Cairo, EgyptBackground: The synthesis of anisotropic silver nanoparticles is a time-consuming process and involves the use of expensive toxic chemicals and specialized laboratory equipment. The presence of toxic chemicals in the prepared anisotropic silver nanostructures hindered their medical application. The authors have developed a fast and inexpensive method for the synthesis of three-dimensional hollow flower-like silver nanostructures without the use of toxic chemicals.Methods: In this method, silver nitrate was reduced using dextrose in presence of trisodium citrate as a capping agent. Sodium hydroxide was added to enhance reduction efficacy of dextrose and reduce time of synthesis. The effects of all four agents on the shape and size of silver nanostructures were investigated.Results: Robust hollow flower-like silver nanostructures were successfully synthesized and ranged in size from 0.2 µm to 5.0 µm with surface area between 25–240 m2/g. Changing the concentration of silver nitrate, dextrose, sodium hydroxide, and trisodium citrate affected the size and shape of the synthesized structures, while changing temperature had no effect.Conclusion: The proposed method is simple, safe, and allows controlled synthesis of anisotropic silver nanostructures, which may represent promising tools as effective antimicrobial agents and for in vitro diagnostics. The synthesized hollow nanostructures may be used for enhanced drug encapsulation and sustained release.Keywords: silver nanoparticles, 3D hollow, flower-like, green synthesis

Information Security in Small and Medium-Sized Companies

OpenAIRE

David Kral

2011-01-01

Information security doesn’t involve only large organizations. Small and medium-sized companies must closely examine this issue too, because they are increasingly threatened by cyber attacks. Many of them mistakenly believe, that security of their valuable data is sufficient, or that the attackers are not interested in them. Existing standards and methodologies for implementation and management of information security are often hard to transfer to the environment of small and medium-sized bus...

Synthesis of silver nano-materials from Grevillea robusta A Cunn (Silver-oak tree) leaves extract and shape directing role of cetyltrimethylammonium bromide

International Nuclear Information System (INIS)

Ahmad, Rabia; Faisal, Qamer; Hussain, Sajjad

2016-01-01

Grevillea robusta (Silver-oak tree) tree is a medicinal tree. Conventional UV-visible spectrophotometric and transmission electron microscopic technique were used to determine the morphology of silver nanoplates (AgNP) using Grevillea robusta (Silver-oak tree) aqueous leaves extract for the first time. The visible spectra showed the presence of three well defined surface plasmon absorption (SPR) bands at 500, 550 and 675 nm which was attributed to the anisotropic growth of Ag-nanoplates. Transmission electron microscopic (TEM) analysis of AgNP showed formation of truncated triangular, polyhedral with some irregular shapes nanoplates in the size range 8-20 nm. Cetyltrimethylammonium bromide (CTAB) has no significant effect on the shape of the spectra, position of SPR bands, size and size distribution of AgNP.

Synthesis of silver nano-materials from Grevillea robusta A Cunn (Silver-oak tree) leaves extract and shape directing role of cetyltrimethylammonium bromide

Energy Technology Data Exchange (ETDEWEB)

Ahmad, Rabia; Faisal, Qamer; Hussain, Sajjad [Department of Chemistry, Jamia Millia Islamia (Central University), New Delhi-110025 (India)

2016-05-23

Grevillea robusta (Silver-oak tree) tree is a medicinal tree. Conventional UV-visible spectrophotometric and transmission electron microscopic technique were used to determine the morphology of silver nanoplates (AgNP) using Grevillea robusta (Silver-oak tree) aqueous leaves extract for the first time. The visible spectra showed the presence of three well defined surface plasmon absorption (SPR) bands at 500, 550 and 675 nm which was attributed to the anisotropic growth of Ag-nanoplates. Transmission electron microscopic (TEM) analysis of AgNP showed formation of truncated triangular, polyhedral with some irregular shapes nanoplates in the size range 8-20 nm. Cetyltrimethylammonium bromide (CTAB) has no significant effect on the shape of the spectra, position of SPR bands, size and size distribution of AgNP.

Surface topography of a palladium cathode after electrolysis in heavy water

International Nuclear Information System (INIS)

Silver, D.S.; Dash, J.; Keefe, P.S.

1993-01-01

Electrolysis was performed with a palladium cathode and an electrolyte containing both hydrogen and deuterium ions. The cathode bends toward the anode during this process. Examination of both the concave and the convex surfaces with the scanning electron microscope, scanning tunneling microscope, and atomic force microscope shows unusual surface characteristics. Rimmed craters with faceted crystals inside and multitextural surfaces were observed on an electrolyzed palladium cathode but not on palladium that has not been electrolyzed. 9 refs., 9 figs

Toward Efficient Palladium-Catalyzed Allylic C-H Alkylation

DEFF Research Database (Denmark)

Jensen, Thomas; Fristrup, Peter

2009-01-01

Recent breakthroughs have proved that direct palladium (II)-catalyzed allylic C-H alkylation can be achieved. This new procedure shows that the inherent requirement for a leaving group in the Tsuji-Trost palladium-catalyzed allylic alkylation can be lifted. These initial reports hold great promise...... for the development of allylic C-H alkylation into a widely applicable methodology, thus providing a means to enhance synthetic efficiency in these reactions....

78 FR 37404 - Small Business Size Standards: Support Activities for Mining

Science.gov (United States)

2013-06-20

... assistance programs, SBA establishes small business size definitions (referred to as size standards) for... million should be the limit of a small business definition and anything larger than that, such as that SBA... Business Act (15 U.S.C. 632(a)) (Act) requires that small business size definitions vary to reflect...

Palladium-Catalysed Coupling Reactions

NARCIS (Netherlands)

de Vries, Johannes G.; Beller, M; Blaser, HU

2012-01-01

Palladium-catalysed coupling reactions have gained importance as a tool for the production of pharmaceutical intermediates and to a lesser extent also for the production of agrochemicals, flavours and fragrances, and monomers for polymers. In this review only these cases are discussed where it seems

77 FR 72766 - Small Business Size Standards: Support Activities for Mining

Science.gov (United States)

2012-12-06

... eligibility for Federal small business assistance, SBA establishes small business size definitions (referred... operation; and (3) within a specific small business definition or size standard established by SBA... to SBA's Administrator the responsibility for establishing small business definitions. The Act also...

Toxicity of nano- and micro-sized silver particles in human hepatocyte cell line L02

International Nuclear Information System (INIS)

Liu Pengpeng; Guan Rongfa; Jiang Jiaxin; Liu Mingqi; Huang Guangrong; Chen Xiaoting; Ye Xingqian

2011-01-01

Silver nanoparticles (Ag NPs) previously classified as antimicrobial agents have been widely used in consumers and industrial products, especially food storage material. Ag NPs used as antimicrobial agents may be found in liver. Thus, examination of the ability of Ag NPs to penetrate the liver is warranted. The aim of the study was to determine the optimal viability assay for using with Ag NPs in order to assess their toxicity to liver cells. For toxicity evaluations, cellular morphology, mitochondrial function (3-(4, 5-dimethylazol-2-yl)-2, 5-diphenyl-tetrazolium bromide, MTT assay), membrane leakage of lactate dehydrogenase (lactate dehydrogenase, LDH release assay), Oxidative stress markers (malonaldehyde (MDA), glutathione (GSH) and superoxide dismutase (SOD)), DNA damage (single cell gel eletrophoresis, SCGE assay), and protein damage were assessed under control and exposed conditions (24 h of exposure). The results showed that mitochondrial function decreased significantly in cells exposed to Ag NPs at 25 μg·mL -1 . LDH leakage significantly increased in cells exposed to Ag NPs (≥ 25 μg mL -1 ) while micro-sized silver particles tested displayed LDH leakage only at higher doses (100 μg·mL -1 ). The microscopic studies demonstrated that nanoparticle-exposed cells at higher doses became abnormal in size, displaying cellular shrinkage, and an acquisition of an irregular shape. Due to toxicity of silver, further study conducted with reference to its oxidative stress. The results exhibited significant depletion of GSH level, increase in SOD levels and lead to lipid peroxidation, which suggested that cytotoxicity of Ag NPs in liver cells might be mediated through oxidative stress. The results demonstrates that Ag NPs lead to cellular morphological modifications, LDH leakage, mitochondrial dysfunction, and cause increased generation of ROS, depletion of GSH, lipid peroxidation, oxidative DNA damage and protein damage. Though the exact mechanism behind Ag NPs

Toxicity of nano- and micro-sized silver particles in human hepatocyte cell line L02

Science.gov (United States)

Liu, Pengpeng; Guan, Rongfa; Ye, Xingqian; Jiang, Jiaxin; Liu, Mingqi; Huang, Guangrong; Chen, Xiaoting

2011-07-01

Silver nanoparticles (Ag NPs) previously classified as antimicrobial agents have been widely used in consumers and industrial products, especially food storage material. Ag NPs used as antimicrobial agents may be found in liver. Thus, examination of the ability of Ag NPs to penetrate the liver is warranted. The aim of the study was to determine the optimal viability assay for using with Ag NPs in order to assess their toxicity to liver cells. For toxicity evaluations, cellular morphology, mitochondrial function (3-(4, 5-dimethylazol-2-yl)-2, 5-diphenyl-tetrazolium bromide, MTT assay), membrane leakage of lactate dehydrogenase (lactate dehydrogenase, LDH release assay), Oxidative stress markers (malonaldehyde (MDA), glutathione (GSH) and superoxide dismutase (SOD)), DNA damage (single cell gel eletrophoresis, SCGE assay), and protein damage were assessed under control and exposed conditions (24 h of exposure). The results showed that mitochondrial function decreased significantly in cells exposed to Ag NPs at 25 μg·mL-1. LDH leakage significantly increased in cells exposed to Ag NPs (>= 25 μg mL-1) while micro-sized silver particles tested displayed LDH leakage only at higher doses (100 μg·mL-1). The microscopic studies demonstrated that nanoparticle-exposed cells at higher doses became abnormal in size, displaying cellular shrinkage, and an acquisition of an irregular shape. Due to toxicity of silver, further study conducted with reference to its oxidative stress. The results exhibited significant depletion of GSH level, increase in SOD levels and lead to lipid peroxidation, which suggested that cytotoxicity of Ag NPs in liver cells might be mediated through oxidative stress. The results demonstrates that Ag NPs lead to cellular morphological modifications, LDH leakage, mitochondrial dysfunction, and cause increased generation of ROS, depletion of GSH, lipid peroxidation, oxidative DNA damage and protein damage. Though the exact mechanism behind Ag NPs

Toxicity of nano- and micro-sized silver particles in human hepatocyte cell line L02

Energy Technology Data Exchange (ETDEWEB)

Liu Pengpeng; Guan Rongfa; Jiang Jiaxin; Liu Mingqi; Huang Guangrong; Chen Xiaoting [Zhejiang Provincial Key Laboratory of Biometrology and Inspection and Quarantine, College of Life Sciences, China Jiliang University, Hangzhou 310018 (China); Ye Xingqian, E-mail: rfguan@163.com [Department of Food Science and Nutrition, School of Biosystems Engineering and Food Science, Zhejiang University, Hangzhou 310029 (China)

2011-07-06

Silver nanoparticles (Ag NPs) previously classified as antimicrobial agents have been widely used in consumers and industrial products, especially food storage material. Ag NPs used as antimicrobial agents may be found in liver. Thus, examination of the ability of Ag NPs to penetrate the liver is warranted. The aim of the study was to determine the optimal viability assay for using with Ag NPs in order to assess their toxicity to liver cells. For toxicity evaluations, cellular morphology, mitochondrial function (3-(4, 5-dimethylazol-2-yl)-2, 5-diphenyl-tetrazolium bromide, MTT assay), membrane leakage of lactate dehydrogenase (lactate dehydrogenase, LDH release assay), Oxidative stress markers (malonaldehyde (MDA), glutathione (GSH) and superoxide dismutase (SOD)), DNA damage (single cell gel eletrophoresis, SCGE assay), and protein damage were assessed under control and exposed conditions (24 h of exposure). The results showed that mitochondrial function decreased significantly in cells exposed to Ag NPs at 25 {mu}g{center_dot}mL{sup -1}. LDH leakage significantly increased in cells exposed to Ag NPs ({>=} 25 {mu}g mL{sup -1}) while micro-sized silver particles tested displayed LDH leakage only at higher doses (100 {mu}g{center_dot}mL{sup -1}). The microscopic studies demonstrated that nanoparticle-exposed cells at higher doses became abnormal in size, displaying cellular shrinkage, and an acquisition of an irregular shape. Due to toxicity of silver, further study conducted with reference to its oxidative stress. The results exhibited significant depletion of GSH level, increase in SOD levels and lead to lipid peroxidation, which suggested that cytotoxicity of Ag NPs in liver cells might be mediated through oxidative stress. The results demonstrates that Ag NPs lead to cellular morphological modifications, LDH leakage, mitochondrial dysfunction, and cause increased generation of ROS, depletion of GSH, lipid peroxidation, oxidative DNA damage and protein damage

Antioxidant properties of biohybrids based on liposomes and sage silver nanoparticles.

Science.gov (United States)

Barbinta-Patrascu, Marcela Elisabeta; Bunghez, Ioana-Raluca; Iordache, Stefan Marian; Badea, Nicoleta; Fierascu, Radu-Claudiu; Ion, Rodica Mariana

2013-03-01

This paper is aimed to describe a simple and rapid eco-friendly bottom-up approach for the preparation of antioxidant silver bionanostructures using a leaf extract from sage (Salvia officinalis L.). The bioreduction property of sage in the synthesis of silver nanoparticles was investigated by UV-VIS and Attenuated Total Reflectance Fourier Transform Infrared spectroscopy. During their preparation, the particle size analysis was performed by using Dynamic Light Scattering technique. Ultrasonic irradiation was used to obtain sage silver nanoparticles. The morphology (size and shape) of the herbal silver nanoparticles was evaluated by Scanning Electron Microscopy that revealed the formation of spherical phytonanoparticles with size less than 80 nm. In order to increase their stability and their biocompatibility, the sage silver nanoparticles were introduced in two types of liposomes: soybean lecithin- and Chla-DPPC-lipid vesicles which were prepared by thin film hydration method. X-Ray Fluorescence analysis confirmed the silver presence in liposomes/sage-AgNPs biohybrids. The stability of liposomes/herbal AgNPs bioconstructs was checked by zeta potential measurements. The most stable biohybrids: Chla-DPPC/sage-AgNPs with zeta potential value of -34.2 mV, were characterized by Atomic Force Microscopy revealing the spherical and quasi-spherical shaped profiles of these nanobiohybrids with size less than 96 nm. The antioxidant activity of the silver bionanostructures was evaluated using chemiluminescence assay. The developed eco-friendly silver phytonanostructures based on lipid membranes, nanosilver and sage extract, manifest strong antioxidant properties (between 86.5% and 98.6%).

Development of high temperature reference electrodes for in-pile application: Part I. Feasibility study of the external pressure balanced Ag/AgCl reference electrode (EPBRE) and the cathodically charged Palladium hydrogen electrode

International Nuclear Information System (INIS)

Bosch, R.W.; Van Nieuwenhove, R.

1998-10-01

The main problems connected with corrosion potential measurements at elevated temperatures and pressures are related to the stability and lifetime of the reference electrode and the correct estimation of the potential related to the Standard Hydrogen Scale (SHE). Under Pressurised Water Reactor (PWR) conditions of 300 degrees Celsius and 150 bar, the choice of materials is also a limiting factor due to the influence of radiation. Investigations on two reference electrodes that can be used under PWR conditions are reported: the cathodically charged palladium hydrogen electrode, and the external pressure balanced silver/silver chloride electrode. Preliminary investigations with the Pd-electrode were focused on the calculation of the required charging time and the influence of dissolved oxygen. High temperature applications are discussed on the basis of results reported in the literature. Investigations with the silver/silver chloride reference electrode mainly dealt with the salt bridge which is necessary to connect the reference electrode with the testing solution. It is shown that the thermal junction potential is independent of the length of the salt bridge. In addition, the high temperature contributes to an increase of the conductivity of the solution, which is beneficial for the salt bridge connection

Biosynthesis of Silver and Gold Crystals Using Grapefruit Extract

OpenAIRE

Chen Long; Wang Jianli; Wang Hongfeng; Qi Zhaopeng; Zheng Yuchuan; Wang Junbo; Pan Le; Chang Guanru; Yang Yongmei

2016-01-01

In this paper, biological synthesis of silver and gold crystals using grapefruit extract is reported. On treatment of aqueous solutions of silver nitrate and chloroauric acid with grapefruit extract, the formation of stable silver and gold particles at high concentrations is observed to occur. The silver particles formed are quasi-spherical or irregular with sizes ranging from several hundred nanometers to several microns. The gold quasi-spheres with holes on surfaces and with diameters rangi...

Characterization of silver nanoparticles prepared by wet chemical ...

African Journals Online (AJOL)

Results: The silver nanoparticles formed were spherical in shape with mean size of 10.3 nm. The ... antibacterial activity against various strains of bacteria. Keywords: Wet ..... Fang J, Zhong C, Mu R. The study of deposited silver particulate ...

Prognosis method to predict small-sized breast cancer affected by fibrocystic disease

Directory of Open Access Journals (Sweden)

S. A. Velichko

2017-01-01

Full Text Available The purpose of the study is to develop an effective radiological symptom-complex of small-sized breast cancer affected by fibrocystic breast disease by using multivariate statistical methods.Materials and methods. Radiological findings of small-sized breast cancer affected by fibrocystic mastopathy were analyzed in 100 patients with histologically verified diagnosis.Results. It was revealed that the conventional approach to the analysis of mammograms based on the detection of the primary, secondary and indirect mammographic signs of small-sized breast cancer is not effective enough - the sensitivity of mammography is only 62%. Fibrocystic disease and moderate-to-severe sclerosing adenosis make small-sized breast cancer hard to visualize by mammography. The detailed analysis of mammograms allowed us to identify the additional manifestations of small-sized breast cancer affected by mastopathy. The computer program allowing us to evaluate the risk of small-size breast cancer and the diagnostic algorithm for detecting small size breast cancer with sensitivity of 92% were developed. 

Development of silver coating process and facilities for ITER thermal shield

Energy Technology Data Exchange (ETDEWEB)

Kang, D.K. [ITER Korea, National Fusion Research Institute, Daejeon 305-333 (Korea, Republic of); Kim, R.G. [COTEC Corp., Changwon 641-846 (Korea, Republic of); Nam, K., E-mail: kwnam@nfri.re.kr [ITER Korea, National Fusion Research Institute, Daejeon 305-333 (Korea, Republic of); Noh, C.H.; Chung, W. [ITER Korea, National Fusion Research Institute, Daejeon 305-333 (Korea, Republic of); Yoon, D.C. [COTEC Corp., Changwon 641-846 (Korea, Republic of); Lim, K.; Baek, J.P. [SFA Engineering Corp., Asan 336-873 (Korea, Republic of)

2016-11-01

This paper describes both the test results of the bath type silver coating and the design of the bath to construct the silver coating plant for ITER thermal shield. The tests of small specimens made of SS304L and SS304LN were carried out to investigate the effect of the nitrogen content in SS304LN on the silver coating quality. The effect of different degreasing agents was also investigated to improve silver coating process. Small mock-up was tested to find a proper dipping direction during the electroplating process. Finally, noble bath design was conceived and structurally validated. Overall layout of silver coating plant is also shown in this paper.

Small-size biofuel cell on paper.

Science.gov (United States)

Zhang, Lingling; Zhou, Ming; Wen, Dan; Bai, Lu; Lou, Baohua; Dong, Shaojun

2012-05-15

In this work, we demonstrated a novel paper-based mediator-less and compartment-less biofuel cell (BFC) with small size (1.5 cm × 1.5 cm). Ionic liquid functionalized carbon nanotubes (CNTs-IL) nanocomposite was used as support for both stably confining the anodic biocatalyst (i.e., NAD(+)-dependent glucose dehydrogenase, GDH) for glucose electrooxidation and for facilitating direct electrochemistry of the cathodic biocatalyst (i.e., bilirubin oxidase, BOD) for O(2) electroreduction. Such BFC provided a simple approach to fabricate low-cost and portable power devices on small-size paper, which can harvest energy from a wide range of commercial beverages containing glucose (e.g., Nescafe instant coffee, Maidong vitamin water, Watermelon fresh juice, and Minute Maid grape juice). These made the low-cost paper-based biodevice potential for broad energy applications. Copyright © 2012 Elsevier B.V. All rights reserved.

Palladium-Catalyzed Atom-Transfer Radical Cyclization at Remote Unactivated C(sp3 )-H Sites: Hydrogen-Atom Transfer of Hybrid Vinyl Palladium Radical Intermediates.

Science.gov (United States)

Ratushnyy, Maxim; Parasram, Marvin; Wang, Yang; Gevorgyan, Vladimir

2018-03-01

A novel mild, visible-light-induced palladium-catalyzed hydrogen atom translocation/atom-transfer radical cyclization (HAT/ATRC) cascade has been developed. This protocol involves a 1,5-HAT process of previously unknown hybrid vinyl palladium radical intermediates, thus leading to iodomethyl carbo- and heterocyclic structures. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Controllable synthesis and sintering of silver nanoparticles for inkjet-printed flexible electronics

International Nuclear Information System (INIS)

Zhang, Zhiliang; Zhu, Weiyue

2015-01-01

An effective and facile strategy was developed to successfully synthesize nearly uniform silver nanoparticles (AgNPs) with particle size of <10 nm, and demonstrated to achieve the sintering of AgNPs at room temperature for inkjet-printed flexible electronics. In such system, a series of different chain-length alkylamines were exploited as capped molecules to controllable synthesis of uniform AgNPs with the mean nanoparticle size in rang of 8.6 ± 0.9, 8.9 ± 1.2 and 9.2 ± 1.6 nm, and these ultra-small nanoparticles were very favorable to attain an excellent printing fluency. Based on the as-synthesized AgNPs, a sequence of flexible electrocircuits was successfully fabricated by ink-jet printing technique. After the dipped treatment, the printed AgNPs were achieved to spontaneous coalescence and aggregation at room temperature induced by preferential dissolution of capped molecules on AgNPs surfaces into methanol solution. These aggregated AgNPs demonstrated superior controllability, excellent stability and low resistivity in the range of 31.6–26.5 μΩ cm, and would have enormous potential in the application to be tailored for assembly of optoelectronics devices. - Highlights: • Silver nanoparticles with particle size of <10 nm was controllably synthesized. • The sintering of silver nanoparticles was conducted at room temperature. • The resistivity was reached as low as 26.5 μΩ cm for flexible electronics

Examination on small-sized cogeneration HTGR for developing countries

International Nuclear Information System (INIS)

Sakaba, Nariaki; Tachibana, Yukio; Shimakawa, Satoshi; Ohashi, Hirofumi; Sato, Hiroyuki; Yan, Xing; Murakami, Tomoyuki; Ohashi, Kazutaka; Nakagawa, Shigeaki; Goto, Minoru; Ueta, Shohei; Mozumi, Yasuhiro; Imai, Yoshiyuki; Tanaka, Nobuyuki; Okuda, Hiroyuki; Iwatsuki, Jin; Kubo, Shinji; Takada, Shoji; Nishihara, Tetsuo; Kunitomi, Kazuhiko

2008-03-01

The small-sized and safe cogeneration High Temperature Gas-cooled Reactor (HTGR) that can be used not only for electric power generation but also for hydrogen production and district heating is considered one of the most promising nuclear reactors for developing countries where sufficient infrastructure such as power grids is not provided. Thus, the small-sized cogeneration HTGR, named High Temperature Reactor 50-Cogeneration (HTR50C), was studied assuming that it should be constructed in developing countries. Specification, equipment configuration, etc. of the HTR50C were determined, and economical evaluation was made. As a result, it was shown that the HTR50C is economically competitive with small-sized light water reactors. (author)

75 FR 61597 - Small Business Size Standards: Retail Trade

Science.gov (United States)

2010-10-06

... eligibility for Federal small business assistance programs, SBA establishes small business size definitions... authorizes the SBA Administrator to establish only one definition of small business for an industry. [[Page... SBA's Administrator the responsibility for establishing small business definitions. The Act also...

Green Synthesis of Silver Nanoparticles by using Eucalyptus Globulus Leaf Extract

Science.gov (United States)

Balamurugan, Madheswaran; Saravanan, Shanmugam

2017-12-01

A single step eco-friendly, energy efficient and economically scalable green method was employed to synthesize silver nanoparticles. In this work, the synthesis of silver nanoparticles using Eucalyptus globulus leaf extract as reducing and capping agent along with water as solvent at normal room temperature is described. Silver nanoparticles were prepared from aqueous silver nitrate solution by adding the leaf extract. The prepared nanoparticles were characterized by using UV-visible Spectrophotometer, X-ray diffractometer, High Resolution Transmission Electron Microscope (HR-TEM) and Fourier Transform Infrared Spectroscope (FTIS). X-ray diffraction studies brought to light the crystalline nature and the face centered cubic structure of the silver nanoparticles. Using HR-TEM. the nano sizes and morphology of the particles were studied. The mean sizes of the prepared silver nanoparticles ranged from 30 to 36 nm. The density of the particles was tuned by varying the molar ratio of silver nitrate. FTIS studies showed the functional group of organic molecules which were located on the surface of the silver nanoparticles. Originating from the leaf extracts, these organic molecules reduced and capped the particles.

Thermodynamics of the hybrid interaction of hydrogen with palladium nanoparticles

NARCIS (Netherlands)

Griessen, R.P.; Strohfeldt, N.; Giessen, H.

2015-01-01

Palladium-hydrogen is a prototypical metal-hydrogen system. It is therefore not at all surprising that a lot of attention has been devoted to the absorption and desorption of hydrogen in nanosized palladium particles. Several seminal articles on the interaction of H with Pd nanocubes and

Antimicrobial active silver nanoparticles and silver/polystyrene core-shell nanoparticles prepared in room-temperature ionic liquid

International Nuclear Information System (INIS)

An Jing; Wang Desong; Luo Qingzhi; Yuan Xiaoyan

2009-01-01

Uniform silver nanoparticles and silver/polystyrene core-shell nanoparticles were successfully synthesized in a room temperature ionic liquid, 1-n-butyl-3-methylimidazolium tetrafluoroborate ([BMIM].BF 4 ). [BMIM].BF 4 plays a protective role to prevent the nanoparticles from aggregation during the preparation process. Transmission electron micrographs confirm that both silver nanoparticles and core-shell nanoparticles are regular spheres with the sizes in the range of 5-15 nm and 15-25 nm, respectively. The X-ray diffraction analysis reveals the face-centered cubic geometry of silver nanoparticles. The as-prepared nanoparticles were also characterized by Fourier transform infrared spectroscopy, Raman spectroscopy, UV-vis diffuse reflectance spectroscopy and X-ray photoelectron spectroscopy. In addition, antimicrobial activities against E. coli and S. aureus were studied and the results show that both silver nanoparticles and core-shell nanoparticles possess excellent antimicrobial activities. The antimicrobial mechanism of the as-prepared nanoparticles was discussed.

77 FR 42211 - Small Business Size Standards: Arts, Entertainment, and Recreation

Science.gov (United States)

2012-07-18

..., SBA establishes small business definitions (referred to as size standards) for private sector... operated; (2) not dominant in its field of operation; and (3) within a specific small business definition... SMALL BUSINESS ADMINISTRATION 13 CFR Part 121 RIN 3245-AG36 Small Business Size Standards: Arts...

Sunlight-assisted synthesis of colloidal silver nanoparticles using chitosan as reducing agent

Science.gov (United States)

Susilowati, E.; Maryani; Ashadi

2018-04-01

The present study we explore an environmentally friendly colloidal silver nanoparticles preparation using chitosan as reducing agent and stabilizer. It develops a new strategy on preparation of silver nanoparticles through the gel phase using sodium hydroxide (NaOH) as accelerator reagent. Sunlight irradiation was employed to assisted reducing process of silver ions to silver nanoparticles. Localized surface plasmon resonance (LSPR) phenomenon of silver nanoparticles was investigated using UV-Vis spectrophotometer. The shape and size of silver particles were analyzed using TEM. The formation of silver nanoparticles was confirmed by the appearance of LSPR absorption peak at 396.0–412.0 nm. The absorption peak of LSPR were affected by NaOH amount, time of sulight irradiation and concentration of AgNO3. The produced silver nanoparticles were spherical with dominant size range of 5 to 8 nm as shown by TEM images. All colloidals were stable without any aggregation for 30 days after preparation.

Assessing bio-available silver released from silver nanoparticles embedded in silica layers using the green algae Chlamydomonas reinhardtii as bio-sensors

Energy Technology Data Exchange (ETDEWEB)

Pugliara, Alessandro [nMat group-CEMES (Centre d' Elaboration de Matériaux et d' Etudes Structurales)-CNRS, Université de Toulouse, 29 rue Jeanne Marvig, BP 94347, F-31055 Toulouse Cedex 4 (France); LAPLACE (LAboratoire PLAsma et Conversion d' Energie), Université de Toulouse, CNRS, UPS, INPT, 118 route de Narbonne, F-31062 Toulouse (France); Makasheva, Kremena; Despax, Bernard [LAPLACE (LAboratoire PLAsma et Conversion d' Energie), Université de Toulouse, CNRS, UPS, INPT, 118 route de Narbonne, F-31062 Toulouse (France); Bayle, Maxime; Carles, Robert; Benzo, Patrizio; BenAssayag, Gérard; Pécassou, Béatrice [nMat group-CEMES (Centre d' Elaboration de Matériaux et d' Etudes Structurales)-CNRS, Université de Toulouse, 29 rue Jeanne Marvig, BP 94347, F-31055 Toulouse Cedex 4 (France); Sancho, Maria Carmen; Navarro, Enrique [IPE (Instituto Pirenaico de Ecología)-CSIC, Avda. Montañana 1005, Zaragoza 50059 (Spain); Echegoyen, Yolanda [I3A, Department of Analytical Chemistry, University of Zaragoza, C/ María de Luna 3, 50018, Zaragoza (Spain); Bonafos, Caroline, E-mail: bonafos@cemes.fr [nMat group-CEMES (Centre d' Elaboration de Matériaux et d' Etudes Structurales)-CNRS, Université de Toulouse, 29 rue Jeanne Marvig, BP 94347, F-31055 Toulouse Cedex 4 (France)

2016-09-15

Silver nanoparticles (AgNPs) because of their strong antibacterial activity are widely used in health-care sector and industrial applications. Their huge surface-volume ratio enhances the silver release compared to the bulk material, leading to an increased toxicity for microorganisms sensitive to this element. This work presents an assessment of the toxic effect on algal photosynthesis due to small (size < 20 nm) AgNPs embedded in silica layers. Two physical approaches were originally used to elaborate the nanocomposite structures: (i) low energy ion beam synthesis and (ii) combined silver sputtering and plasma polymerization. These techniques allow elaboration of a single layer of AgNPs embedded in silica films at defined nanometer distances (from 0 to 7 nm) beneath the free surface. The structural and optical properties of the nanostructures were studied by transmission electron microscopy and optical reflectance. The silver release from the nanostructures after 20 h of immersion in buffered water was measured by inductively coupled plasma mass spectrometry and ranges between 0.02 and 0.49 μM. The short-term toxicity of Ag to photosynthesis of Chlamydomonas reinhardtii was assessed by fluorometry. The obtained results show that embedding AgNPs reduces the interactions with the buffered water free media, protecting the AgNPs from fast oxidation. The release of bio-available silver (impacting on the algal photosynthesis) is controlled by the depth at which AgNPs are located for a given host matrix. This provides a procedure to tailor the toxicity of nanocomposites containing AgNPs. - Highlights: • Controlled synthesis of 2D arrays of silver nanoparticles embedded in silica. • Assessing bio-available silver release using the green algae as bio-sensors. • The Ag release can be controlled by the distance nanoparticles/dielectric surface. • All the Ag released in solution is in the form of Ag{sup +} ions. • Toxicity comparable to similar concentrations of

Controlled size and one-dimensional growth

Indian Academy of Sciences (India)

875–881. c Indian Academy of Sciences. Synthesis of azamacrocycle stabilized palladium nanoparticles: Controlled size and one-dimensional growth. JEYARAMAN ATHILAKSHMI and DILLIP KUMAR CHAND. ∗. Department of Chemistry, Indian Institute of Technology Madras, Chennai 600036, India e-mail: dillip@iitm.ac.

Low-temperature solution processing of palladium/palladium oxide films and their pH sensing performance.

Science.gov (United States)

Qin, Yiheng; Alam, Arif U; Pan, Si; Howlader, Matiar M R; Ghosh, Raja; Selvaganapathy, P Ravi; Wu, Yiliang; Deen, M Jamal

2016-01-01

Highly sensitive, easy-to-fabricate, and low-cost pH sensors with small dimensions are required to monitor human bodily fluids, drinking water quality and chemical/biological processes. In this study, a low-temperature, solution-based process is developed to prepare palladium/palladium oxide (Pd/PdO) thin films for pH sensing. A precursor solution for Pd is spin coated onto pre-cleaned glass substrates and annealed at low temperature to generate Pd and PdO. The percentages of PdO at the surface and in the bulk of the electrodes are correlated to their sensing performance, which was studied by using the X-ray photoelectron spectroscope. Large amounts of PdO introduced by prolonged annealing improve the electrode's sensitivity and long-term stability. Atomic force microscopy study showed that the low-temperature annealing results in a smooth electrode surface, which contributes to a fast response. Nano-voids at the electrode surfaces were observed by scanning electron microscope, indicating a reason for the long-term degradation of the pH sensitivity. Using the optimized annealing parameters of 200°C for 48 h, a linear pH response with sensitivity of 64.71±0.56 mV/pH is obtained for pH between 2 and 12. These electrodes show a response time shorter than 18 s, hysteresis less than 8 mV and stability over 60 days. High reproducibility in the sensing performance is achieved. This low-temperature solution-processed sensing electrode shows the potential for the development of pH sensing systems on flexible substrates over a large area at low cost without using vacuum equipment. Copyright © 2015 Elsevier B.V. All rights reserved.

Synthesis of Silver nanoparticles (AgNPs) with Antibacterial Activity

Science.gov (United States)

Campillo Gloria, E.; Ederley, Vélez; Gladis, Morales; César, Hincapié; Jaime, Osorio; Oscar, Arnache; Uribe José, Ignacio; Franklin, Jaramillo

2017-06-01

The synthesis of nanomaterials is currently one of the most active in nanoscience branches; especially those help improve the human quality life. Silver nanoparticles (AgNPs) are an example of this as it is known to have inhibitory and bactericidal effects. In this work, we report the synthesis of silver nanoparticles by chemical reduction method of silver nitrate (AgNO3) from aqueous solution, using a mix of polivinyl pyrrolidone (PVP) - Aloe Vera as reducing agent and for stabilization and control of particle size. Silver nanoparticles obtained were characterized by Scanning Electron Microscopy (SEM), UV-visible spectroscopy and measurements using Zetasizer Nano ZS were applied to size estimation. The existence of surface plasmon resonance peak at λmax ~ 420 nm is evidence of silver nanoparticles formation. It was possible to standardize an appropriate protocol for the evaluation of bactericidal activity of the nanoparticles, for mesophilic microorganisms. Bactericidal activity above 90% against these kinds of bacteria was demonstrated.

Synthesis of Silver nanoparticles (AgNPs) with Antibacterial Activity

International Nuclear Information System (INIS)

Gloria, E. Campillo; Ederley, Vélez; César, Hincapié; Gladis, Morales; Jaime, Osorio; Oscar, Arnache; José, Ignacio Uribe; Franklin, Jaramillo

2017-01-01

The synthesis of nanomaterials is currently one of the most active in nanoscience branches; especially those help improve the human quality life. Silver nanoparticles (AgNPs) are an example of this as it is known to have inhibitory and bactericidal effects. In this work, we report the synthesis of silver nanoparticles by chemical reduction method of silver nitrate (AgNO 3 ) from aqueous solution, using a mix of polivinyl pyrrolidone (PVP) – Aloe Vera as reducing agent and for stabilization and control of particle size. Silver nanoparticles obtained were characterized by Scanning Electron Microscopy (SEM), UV–visible spectroscopy and measurements using Zetasizer Nano ZS were applied to size estimation. The existence of surface plasmon resonance peak at λ max ∼ 420 nm is evidence of silver nanoparticles formation. It was possible to standardize an appropriate protocol for the evaluation of bactericidal activity of the nanoparticles, for mesophilic microorganisms. Bactericidal activity above 90% against these kinds of bacteria was demonstrated. (paper)

Structural characterization of silver nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Garcia, Paulo Ricardo; Sousa, Edi Carlos Pereira de; Pontuschka, Walter Maigon; Oliveira, Cristiano Luis Pinto de, E-mail: pauloricardoafg@yahoo.com.br [Universidade de Sao Paulo (USP), Sao Paulo, SP (Brazil). Instituto de Fisica

2016-07-01

Full text: Due to magnetic, optical and electrical properties metallic nanoparticles have been extensively studied to potential applications in biosensor production, separation of biological molecules, image techniques, drug delivery among several others. For such applications, it is crucial to have crystals with morphology and well defined structure. In this work we presented a detailed structured characterization of silver nanoparticles using small angle x-rays and light scattering methods. The comparison and correlation of these results with electron microscopy images permitted the determination of interesting structural parameters for the studied systems. The oscillations of the intensity curve of SAXS data reveal that this sample has particles with reasonable stability and well defined sizes. The mean radius obtained from the size distribution curve is in good agreement with the ones obtained by TEM images. As will be shown, the combination of several techniques and the correct analysis for the obtained experimental data provides unique information on the structure of the studied systems. (author)

Electroless Deposition of Palladium on Macroscopic 3D-Printed Polymers with Dense Microlattice Architectures for Development of Multifunctional Composite Materials

International Nuclear Information System (INIS)

Jones, Christopher G.; Mills, Bernice E.; Nishimoto, Ryan K.; Robinson, David B.

2017-01-01

A simple procedure has been developed to create palladium (Pd) films on the surface of several common polymers used in commercial fused deposition modeling (FDM) and stereolithography (SLA) based three-dimensional (3D) printing by an electroless deposition process. The procedure can be performed at room temperature, with equipment less expensive than many 3D printers, and occurs rapidly enough to achieve full coverage of the film within a few minutes. 3D substrates composed of dense logpile or cubic lattices with part sizes in the mm to cm range, and feature sizes as small as 150 μm were designed and printed using commercially available 3D printers. The deposition procedure was successfully adapted to show full coverage in the lattice substrates. As a result, the ability to design, print, and metallize highly ordered three-dimensional microscale structures could accelerate development of a range of optimized chemical and mechanical engineering systems.

Structural characterization and antimicrobial properties of silver nanoparticles prepared by inverse microemulsion method.

Science.gov (United States)

Wani, Irshad A; Khatoon, Sarvari; Ganguly, Aparna; Ahmed, Jahangeer; Ahmad, Tokeer; Manzoor, Nikhat

2013-01-01

Silver nanoparticles have been synthesized in the inverse microemulsions formed using three different surfactants viz., cetyl-trimethyl ammonium bromide (CTAB), Tergitol and Triton X-100. We have done a systematic study of the effect of the surfactants on the particle size and properties of the silver nanoparticles. Microscopic studies show the formation of spheres, cubes and discs shaped silver nanostructures with the size in the range from 8 to 40 nm. Surface plasmon resonance (SPR) peak was observed around 400 nm and 500 nm. In addition to SPR some extra peaks have also been observed due to the formation of silver metal clusters. The surface area increases from 3.45 to 15.06 m(2)/g with decreasing the size of silver nanoparticles (40-8 nm). To investigate the antimicrobial activity of silver nanoparticles, the nanoparticles were tested against the yeast, Candida albicans and the bacterium, E. coli. The results suggest very good antimicrobial activity of the silver nanoparticles against the test microbes. The mode of action of the antimicrobial activity was also proposed. Copyright © 2012 Elsevier B.V. All rights reserved.

A simple method of growing silver chloride nanocubes on silver nanowires

International Nuclear Information System (INIS)

Khaligh, Hadi Hosseinzadeh; Goldthorpe, Irene A

2015-01-01

The growth of AgCl nanocubes directly on the sidewalls of Ag nanowires is demonstrated. The nanocubes can be simply obtained through extended low temperature annealing of polyol-synthesized silver nanowires in a vacuum. The length of time and temperature of the anneal and the diameter of the nanowire affect the size and density of the nanocubes obtained. It is hypothesized that the AgCl material is supplied from reactants leftover from the silver nanowire synthesis. This novel hybrid nanostructure may have applications in areas such as photovoltaics, surface enhanced Raman spectroscopy, and photocatalysis. (fast track communication)

Testing of a 7-tube palladium membrane reactor for potential use in TEP

International Nuclear Information System (INIS)

Carlson, Bryan J.; Trujillo, Stephen; Willms, R. Scott

2010-01-01

A Palladium Membrane Reactor (PMR) consists of a palladium/silver membrane permeator filled with catalyst (catalyst may be inside or outside the membrane tubes). The PMR is designed to recover tritium from the methane, water, and other impurities present in fusion reactor effluent. A key feature of a PMR is that the total hydrogen isotope content of a stream is significantly reduced as (1) methane-steam reforming and/or water-gas shift reactions proceed on the catalyst bed and (2) hydrogen isotopes are removed via permeation through the membrane. With a PMR design matched to processing requirements, nearly complete hydrogen isotope removals can be achieved. A 3-tube PMR study was recently completed. From the results presented in this study, it was possible to conclude that a PMR is appropriate for TEP, perforated metal tube protectors function well, platinum on aluminum (PtA) catalyst performs the best, conditioning with air is probably required to properly condition the Pd/Ag tubes, and that CO/CO 2 ratios maybe an indicator of coking. The 3-tube PMR had a permeator membrane area of 0.0247 m 2 and a catalyst volume to membrane area ratio of 4.63 cc/cm 2 (with the catalyst on the outside of the membrane tubes and the catalyst only covering the membrane tube length). A PMR for TEP will require a larger membrane area (perhaps 0.35 m 2 ). With this in mind, an intermediate sized PMR was constructed. This PMR has 7 permeator tubes and a total membrane area of 0.0851 m 2 . The catalyst volume to membrane area ratio for the 7-tube PMR was 5.18 cc/cm 2 . The total membrane area of the 7-tube PMR (0.0851 m 2 ) is 3.45 times larger than total membrane area of the 3-tube PMR (0.0247 m 2 ). The following objectives were identified for the 7-tube PMR tests: (1) Refine test measurements, especially humidity and flow; (2) Refine maintenance procedures for Pd/Ag tube conditioning; (3) Evaluate baseline PMR operating conditions; (4) Determine PMR scaling method; (5) Evaluate PMR

SAXS Combined with UV-vis Spectroscopy and QELS: Accurate Characterization of Silver Sols Synthesized in Polymer Matrices.

Science.gov (United States)

Bulavin, Leonid; Kutsevol, Nataliya; Chumachenko, Vasyl; Soloviov, Dmytro; Kuklin, Alexander; Marynin, Andrii

2016-12-01

The present work demonstrates a validation of small-angle X-ray scattering (SAXS) combining with ultra violet and visible (UV-vis) spectroscopy and quasi-elastic light scattering (QELS) analysis for characterization of silver sols synthesized in polymer matrices. Polymer matrix internal structure and polymer chemical nature actually controlled the sol size characteristics. It was shown that for precise analysis of nanoparticle size distribution these techniques should be used simultaneously. All applied methods were in good agreement for the characterization of size distribution of small particles (less than 60 nm) in the sols. Some deviations of the theoretical curves from the experimental ones were observed. The most probable cause is that nanoparticles were not entirely spherical in form.

Restoration: Implant with Devastated Platform through Metal Post

Directory of Open Access Journals (Sweden)

Luna Salinas Tatiana

2017-01-01

Full Text Available Case Presentation. Implant prostheses are a successful treatment for replacing missing teeth. However, this treatment modality can have biological and mechanical complications causing serious problems for the dentist, as demonstrated in this clinical case. The patient presented with a fractured screw and a severely damaged implant hex connection that corresponded to the second premolar, upper left, stating that she unsuccessfully tried to remove the prosthetic screw, which was most likely to have been loose. After clinical and radiographic review, it was decided to remove small fragments of the fractured prosthetic screw inside the implant head. Removal by conventional methods was unsuccessful but was eventually achieved through use of a bur. Then it was possible to make a cast post (gold-palladium and develop a fixed prosthesis (silver-palladium, which were attached with luting cement. A cast post (gold-palladium was made and a fixed prosthesis was developed (silver-palladium, which were attached with luting cement, the same ones that can present mechanical complications such as fractures between the third and fourth thread of the implant, loosening of the abutment, and/or the prosthetic screw in individual crowns, most frequently in partially edentulous patients, mainly in the premolar and molar regions of the maxilla. Conclusion. Therefore the present technique used in this case is very simple, noninvasive, and useful to readers.

Iodine, krypton and xenon retention efficiencies of silver impregnated silica gel media with different silver loadings and under different test conditions

International Nuclear Information System (INIS)

Motes, B.G.; Fernandez, S.J.; Tkachyk, J.W.

1983-02-01

The purpose of an independent study conducted by Exxon Nuclear Idaho, Co. (ENICO) was to evaluate a silver impregnated silica gel adsorption medium associated with a radioiodine air sampler developed at Brookhaven National Laboratory (BNL). Specifically, ENICO's responsibility was to evaluate the iodine and noble gas retention efficiencies of the adsorption medium. The evaluation was comprised of a four-phase program: 1) test assemblies capable of challenging the silver silica gel filled adsorber canister with radioiodine species or noble gases at flow rates up to 10 scfm and relative humidities up to 83% were constructed; 2) more than 45 kgs of the 4 and 8% silver impregnated silica gel were prepared and characterized for particle size distribution, bulk silver content, bulk density, and silver content by particle size; 3) iodine species retention efficiencies of the silver silica gel were determined; and 4 krypton and xenon retention efficiencies were measured. The iodine species retention efficiencies were greater than 90% under most conditions. A combination of flow rates >5 scfm and 4% silver loaded silica gel reduced the methyl iodide retention efficiency to less than 90%. The retention efficiencies for both krypton and xenon were on the order of 8 x 10 -2 % and were not affected greatly by any test variable except test duration. A reduced retention efficiency with increased test durations indicates adsorption equilibrium may be established within five minutes. (author)

75 FR 1296 - Small Business Size Regulations; 8(a) Business Development/Small Disadvantaged Business Status...

Science.gov (United States)

2010-01-11

... SMALL BUSINESS ADMINISTRATION 13 CFR Parts 121 and 124 Small Business Size Regulations; 8(a) Business Development/Small Disadvantaged Business Status Determinations AGENCY: U.S. Small Business Administration. ACTION: Notice of public meetings; request for comments. SUMMARY: The U.S. Small Business...

Optical Materials with a Genome: Nanophotonics with DNA-Stabilized Silver Clusters

Science.gov (United States)

Copp, Stacy M.

Fluorescent silver clusters with unique rod-like geometries are stabilized by DNA. The sizes and colors of these clusters, or AgN-DNA, are selected by DNA base sequence, which can tune peak emission from blue-green into the near-infrared. Combined with DNA nanostructures, AgN-DNA promise exciting applications in nanophotonics and sensing. Until recently, however, a lack of understanding of the mechanisms controlling AgN-DNA fluorescence has challenged such applications. This dissertation discusses progress toward understanding the role of DNA as a "genome" for silver clusters and toward using DNA to achieve atomic-scale precision of silver cluster size and nanometer-scale precision of silver cluster position on a DNA breadboard. We also investigate sensitivity of AgN-DNA to local solvent environment, with an eye toward applications in chemical and biochemical sensing. Using robotic techniques to generate large data sets, we show that fluorescent silver clusters are templated by certain DNA base motifs that select "magic-sized" cluster cores of enhanced stabilities. The linear arrangement of bases on the phosphate backbone imposes a unique rod-like geometry on the clusters. Harnessing machine learning and bioinformatics techniques, we also demonstrate that sequences of DNA templates can be selected to stabilize silver clusters with desired optical properties, including high fluorescence intensity and specific fluorescence wavelengths, with much higher rates of success as compared to current strategies. The discovered base motifs can be also used to design modular DNA host strands that enable individual silver clusters with atomically precise sizes to bind at specific programmed locations on a DNA nanostructure. We show that DNA-mediated nanoscale arrangement enables near-field coupling of distinct clusters, demonstrated by dual-color cluster assemblies exhibiting resonant energy transfer. These results demonstrate a new degree of control over the optical properties

78 FR 38811 - Small Business Size and Status Integrity

Science.gov (United States)

2013-06-28

.... Firms will not be able submit offers for small business contracts based on their online representations... SMALL BUSINESS ADMINISTRATION 13 CFR Parts 121, 124, 125, 126, and 127 RIN 3245-AG23 Small Business Size and Status Integrity AGENCY: Small Business Administration. ACTION: Final rule. SUMMARY: This...

Facile synthesis of palladium nanoparticle doped polyaniline nanowires in soft templates for catalytic applications

Science.gov (United States)

Kshirasagar, Krushna J.; Markad, Uddhav S.; Saha, Abhijit; Sharma, Kiran Kumar K.; Sharma, Geeta K.

2017-02-01

Palladium nanoparticles doped polyaniline (Pd-PANI) nanocomposite (NCs) is synthesized in surfactant based liquid crystalline mesophase by chemical oxidation followed by radiolysis. The confinement of the liquid crystalline mesophase facilitates polymerization of aniline monomers and their 1D growth into polyaniline (PANI) nanowires by using ammonium persulfate. The PANI nanowires have an average diameter of 30-40 nm. The in situ radiolytic reduction of palladium ions ensures uniform size distribution of the palladium (Pd) nanoparticles on the surface of the PANI nanowires. The synthesized Pd-PANI nanocomposites show wire like structures of PANI (diameter ~30-40 nm) on which Pd nanoparticles of the size 10 nm are decorated. The identical average diameter of the PANI nanowires before and post gamma irradiation suggest high stability of the PANI nanowires in liquid crystalline mesophase. Surface characterization of the NCs were carried out using BET and XPS. The catalytic activity of Pd-PANI NCs are investigated in the reduction of methylene blue (MB) and 4-nitro phenol (4-NP) by sodium borohydride (NaBH4). The kinetics of the Pd-PANI NCs catalysed reactions are analysed using the Langmuir-Hinshelwood model. The apparent rate constant (k app) for the MB and 4-NP reduction reactions is 29  ×  10-3 s-1 and 20  ×  10-3 s-1 respectively with an actual Pd catalyst loading of 2.665  ×  10-4 ppm. Further, the recyclability of the Pd-PANI NCs catalyst in both the reduction reactions shows the stability of the catalyst up to four reaction cycles tested in this investigation and the multifunctional nature of the catalyst. The study provides a new approach for the directional synthesis of conducting polymer-metal nanocomposites and their possible application as a nanocatalyst in environmental remediation.

Ageing of palladium tritide: mechanical characterization, helium state and modelling

International Nuclear Information System (INIS)

Segard, M.

2010-01-01

Palladium is commonly used for the storage of tritium (the hydrogen radioactive isotope), since it forms a low-equilibrium-pressure and reversible tritide. Tritium decay into helium-3 is responsible for the ageing of the tritide, leading to the apparition of helium-3 bubbles for instance. Both experimental and theoretical aspects of this phenomenon are studied here.Previous works on ageing modelling led to two main models, dealing with:- Helium-3 bubbles nucleation (using a cellular automaton), - Bubbles growth (using continuum mechanics).These models were quite efficient, but their use was limited by the lack of input data and fitting experimental parameters.To get through these limitations, this work has consisted in studying the most relevant experimental data to improve the modelling of the palladium tritide ageing.The first part of this work was focused on the assessment of the mechanical properties of the palladium tritide (yield strength, ultimate strength, mechanical behaviour). They were deduced from the in situ tensile tests performed on palladium hydride and deuteride. In the second part, ageing characterization was undertaken, mainly focusing on: - Bubbles observations in palladium tritide using transmission electron microscopy, - Internal bubble pressure measurements using nuclear magnetic resonance, - Macroscopic swelling measurements using pycno-metry.The present work has led to significant progress in ageing understanding and has brought very valuable improvements to the modelling of such a phenomenon. (author) [fr

Ab initio calculations of non-stoichiometric copper nitride, pure and with palladium

International Nuclear Information System (INIS)

Moreno-Armenta, Maria G.; Soto, Gerardo; Takeuchi, Noboru

2011-01-01

Research highlights: → The most stable arrangement corresponds to the Cu 3 N-anti ReO 3 structure. → Formation energy of Cu 32 Vac 0 N 8 and Cu 24 Pd 8 Vac 0 N 8 are very similar. → The biggest volume in the compound is Cu 31 Pd 1 Vac 0 N 8/ . → Small amount introduction of extra metal atoms in copper nitride is possible. - Abstract: We present first principles calculations of copper nitride by using periodic density functional theory within a plane-wave ultrasoft pseudopotential scheme. The insertions of extra Cu and/or Pd atoms in the empty sites, vacancy reorganization, and substitution of Cu by Pd atoms were studied. We have used an equivalent reduced-symmetry 2 x 2 x 2 Cu 3 N-like cubic super-cell. Small Cu and/or Pd concentrations and vacancy rearrangements in the copper sub-lattice were conveniently calculated in these low-symmetry cells. We cover probable situations like: the occupation of the initially empty copper sites by (1) copper atoms, and by (2) palladium; (3) the relocation of vacancies in the copper sub-lattice; and (4) the substitution of small quantities of copper by palladium atoms in the copper sub-lattice. The equilibrium volumes and energies after relaxing the atomic positions are compared to those of intrinsic copper nitride. We found that the most stable arrangement corresponds to the ideal stoichiometric Cu 3 N. We also found that any deviation from this ideal configuration shift the semiconductor state to a metallic or semi-metallic one.

Preparation of silver nanocrystals in microemulsion by the γ-radiation method

International Nuclear Information System (INIS)

Hongkai Wu; Xiangling Xu; Xuewu Ge; Zhicheng Zhang

1997-01-01

Silver colloids of well-defined shape, size were synthesized by γ-ray irradiating silver salt in reversed microemulsions, and then pure silver dry powders were obtained. The sols were studied by absorption spectroscopy, and the silver powders were characterized by Transmission Electron Micrographs (TEM) and X-ray Diffraction (XRD). The effect of radiation dose and aging time was discussed. (Author)

Palladium nanoparticle anchored polyphosphazene nanotubes ...

Indian Academy of Sciences (India)

607–610. c Indian Academy of Sciences. Palladium ... 2Department of Chemistry, APA College of Arts and Culture, Palani, Tamil Nadu 624 601, India. 3Department of .... K Dinakaran acknowledges the financial support from. Department of ...

Small and medium-sized nuclear power plants

International Nuclear Information System (INIS)

Schmidt, R.

1986-01-01

Small and medium-sized nuclear power plants have long been under discussion as possible applications of nuclear power in countries with small transmission grid systems, in threshold countries and developing countries, and under special local supply conditions. IAEA has condensed and promoted this interest and tried to establish the demand, and possibilities of meeting it, in special events and campaigns. In recent years, considerable interest was registered even in industrialized countries, but here specially for heating and process heat generation applications and for special purposes and, in medium-sized units, also for combined supplies of electricity and heat. This corresponds to special reactor and plant concepts, some of which have already been developed to a stage at which construction work could begin. The analysis presented deals with necessary preconditions on the sides of the users and the vendors, with problems of economy, infrastructure and financing and with the market prospects of small nuclear power plants. (orig./HP) [de

Monocrystalline solar cells performance coated by silver nanoparticles: Effect of NPs sizes from point of view Mie theory

Science.gov (United States)

Elnoby, Rasha M.; Mourad, M. Hussein; Elnaby, Salah L. Hassab; Abou Kana, Maram T. H.

2018-05-01

Solar based cells coated by nanoparticles (NPs) acknowledge potential utilizing as a part of photovoltaic innovation. The acquired silicon solar cells (Si-SCs) coated with different sizes of silver nanoparticles (Ag NPs) as well as uncoated were fabricated in our lab. The sizes and optical properties of prepared NPs were characterized by spectroscopic techniques and Mie theory respectively. The reflectivity of Si-SCs showed reduction of this property as the size of NPs increased. Electrical properties as open circuit current, fill factor and output power density were assessed and discussed depending on point of view of Mie theory for the optical properties of NPs. Also, photostabilities of SCs were assessed using diode laser of wavelength 450 nm and power 300 mW. Coated SCs with the largest Ag NPs size showed the highest Photostability due to its highest scattering efficiency according to Mie theory concept.

Mineral commodity profiles: Silver

Science.gov (United States)

Butterman, W.C.; Hilliard, Henry E.

2005-01-01

Overview -- Silver is one of the eight precious, or noble, metals; the others are gold and the six platinum-group metals (PGM). World mine production in 2001 was 18,700 metric tons (t) and came from mines in 60 countries; the 10 leading producing countries accounted for 86 percent of the total. The largest producer was Mexico, followed by Peru, Australia, and the United States. About 25 percent of the silver mined in the world in 2001 came from silver ores; 15 percent, from gold ores and the remaining 60 percent, from copper, lead, and zinc ores. In the United States, 14 percent of the silver mined in 2001 came from silver ores; 39 percent, from gold ores; 10 percent, from copper and copper-molybdenum ores; and 37 percent, from lead, zinc, and lead-zinc ores. The precious metal ores (gold and silver) came from 30 lode mines and 10 placer mines; the base-metal ores (copper, lead, molybdenum, and zinc) came from 24 lode mines. Placer mines yielded less than 1 percent of the national silver production. Silver was mined in 12 States, of which Nevada was by far the largest producer; it accounted for nearly one-third of the national total. The production of silver at domestic mines generated employment for about 1,100 mine and mill workers. The value of mined domestic silver was estimated to be $290 million. Of the nearly 27,000 t of world silver that was fabricated in 2001, about one-third went into jewelry and silverware, one-fourth into the light-sensitive compounds used in photography, and nearly all the remainder went for industrial uses, of which there were 7 substantial uses and many other small-volume uses. By comparison, 85 percent of the silver used in the United States went to photography and industrial uses, 8 percent to jewelry and silverware, and 7 percent to coins and medals. The United States was the largest consumer of silver followed by India, Japan, and Italy; the 13 largest consuming countries accounted for nearly 90 percent of the world total. In the

TMV Disk Scaffolds for Making sub-30 nm Silver Nanorings.

Science.gov (United States)

Bayram, Serene; Zahr, Omar; Del Re, Julia; Blum, Amy Szuchmacher

2018-01-01

Nanosized bioscaffolds can be utilized to tackle the challenge of size reduction of metallic rings owing to their miniature features as well as their well-known biomineralization capacity. The tobacco mosaic virus coat protein is used as a command surface to grow and assemble silver nanoparticles into sub-30 nm rings. The versatility of TMV allows the formation of both solid silver rings and rings consisting of discrete silver nanoparticles. The pH-dependent coulombic surface map along with the annular geometry of the protein aggregate allow the generation of rings with or without a central nanoparticle. Our silver rings are believed to be the smallest to date, and they can offer a test material for existing theories on metallic nanorings of this heretofore unreached size scale.

Highly Stable Monocrystalline Silver Clusters for Plasmonic Applications

DEFF Research Database (Denmark)

Novikov, Sergey M.; Popok, Vladimir N.; Evlyukhin, Andrey B.

2017-01-01

Plasmonic sensor configurations utilizing localized plasmon resonances in silver nanostructures typically suffer from the rapid degradation of silver under ambient atmospheric conditions. In this work, we report on the fabrication and detailed characterization of ensembles of monocrystalline silver......-beam technique and characterized by linear spectroscopy, two-photon-excited photoluminescence, surface-enhanced Raman scattering microscopy, and transmission electron, helium ion, and atomic force microscopies. It is found that the fabricated ensembles of monocrystalline silver NPs preserve their plasmonic...... properties (monitored with optical spectroscopy) and strong field enhancements (revealed by surface-enhanced Raman spectroscopy) at least 5 times longer as compared to chemically synthesized silver NPs with similar sizes. The obtained results are of high practical relevance for the further development...

Spatially controlled synthesis of silver nanoparticles and nanowires by photosensitized reduction

Energy Technology Data Exchange (ETDEWEB)

Jradi, S; Zeng, X H; Plain, J; Royer, P; Bachelot, R; Akil, S [Laboratoire de Nanotechnologie et d' Instrumentation Optique, ICD CNRS FRE 2848, Universite de Technologie de Troyes, 12 rue Marie Curie, BP 2060, 10010 Troyes (France); Balan, L; Lougnot, D J; Soppera, O; Vidal, L, E-mail: lavinia.balan@uha.fr [Institut de Science des Materiaux de Mulhouse CNRS LRC 7228, 15 rue Jean Starcky, 68057 Mulhouse (France)

2010-03-05

The present paper reports on the spatially controlled synthesis of silver nanoparticles (NPs) and silver nanowires by photosensitized reduction. In a first approach, direct photogeneration of silver NPs at the end of an optical fiber was carried out. Control of both size and density of silver NPs was possible by changing the photonic conditions. In a further development, a photochemically assisted procedure allowing silver to be deposited at the surface of a polymer microtip was implemented. Finally, polymer tips terminated by silver nanowires were fabricated by simultaneous photopolymerization and silver photoreduction. The silver NPs were characterized by UV-visible spectroscopy and scanning electron microscopy.

Antimicrobial Bacterial Cellulose-Silver Nanoparticles Composite Membranes

Directory of Open Access Journals (Sweden)

Hernane S. Barud

2011-01-01

Full Text Available Antimicrobial bacterial cellulose-silver nanoparticles composite membranes have been obtained by “in situ” preparation of Ag nanoparticles from hydrolytic decomposition of silver nitrate solution using triethanolamine as reducing and complexing agent. The formation of silver nanoparticles was evidenced by the X-ray diffraction, scanning electron microscopy (SEM, transmission electron microscopy (TEM, and absorption in the UV-Visible (350 nm to 600 nm. Thermal and mechanical properties together with swelling behavior for water were considered. TEA concentration was observed to be important in order to obtain only Ag particles and not a mixture of silver oxides. It was also observed to control particle size and amount of silver contents in bacterial cellulose. The composite membranes exhibited strong antimicrobial activity against Gram-negative and Gram-positive bacteria.

Removal of silver from wastewater using cross flow microfiltration

Directory of Open Access Journals (Sweden)

Zanain M.

2013-04-01

Full Text Available Removal of silver from wastewater was investigated using continuous cross flow microfiltration (MF technique hollow fiber membranes with a pore size 0.2μm, with sorbent coated material Al2O3/SDSH2Dz particle size (8 μm. The coating investigated was dithizone (Diphenylthiocarbazone in 0.005M ammonia solution. In the filtration of silver ion solutions, the effects of the permeate flow rate and cross flow velocity on the absorption of silver ion solutions, and since the pore size of membrane (=0.2 μm is smaller then that of the (Al2O3, no need to consider the variation of (Al2O3.rejection as it can be considered to be 100%. The amount of silver absorbed into sorbent material Al2O3/SDSH2Dz was (25.35, 39.68 ppm for the cross flown velocity of 5, 2.5 L/hr respectively, and were the results as function of permeate flow was (25.35, 39.68 ppm for the velocity of 5, 2.5 L/hr respectively.

Assessment of the fate of silver nanoparticles in the A(2)O-MBR system.

Science.gov (United States)

Yuan, Zhi-Hua; Yang, Xiaoyong; Hu, Anyi; Zheng, Yu-Ming; Yu, Chang-Ping

2016-02-15

In this study, we employed a bench scale A(2)O-MBR (anaerobic-anoxic-oxic membrane bioreactor) system to systematically investigate the behavior and distribution of silver nanoparticles (AgNPs) in the activated sludge. The results showed that AgNPs would aggregate and form Ag-sulfur complexes in the activated sludge, and the dissolved silver only reached 13.6 μg/L when AgNPs of 5mg/L was spiked into the A(2)O-MBR. The long-term mass balance analysis showed that most of the silver contents were accumulated in the bioreactor and wasted excess sludge. Only a small fraction (less than 0.5%) of silver could get across the hollow fiber membranes with 0.1 μm nominal pore size in the effluent. In addition, the comparison between total AgNP concentration in aerobic sludge supernatant and effluent suggested that the membrane modules played a role in controlling the discharge of AgNPs into the effluent, especially under a higher influent concentration of AgNPs. Our results also showed that the adsorbed AgNPs or silver complexes in activated sludge still could release dissolved silver at the ambient pH. Thus, since activated sludge could be a sink for AgNPs, the risks of AgNPs in wasted excess sludge during utilization and disposal should be further studied. Copyright © 2015 Elsevier B.V. All rights reserved.

Mechanism of the palladium-catalyzed hydrothiolation of alkynes to thioethers: a DFT study.

Science.gov (United States)

Zhang, Xing-hui; Geng, Zhi-yuan; Wang, Ke-tai; Li, Shan-shan

2014-09-01

The mechanisms of the palladium-catalyzed hydrothiolation of alkynes with thiols were investigated using density functional theory at the B3LYP/6-31G(d, p) (SDD for Pd) level. Solvent effects on these reactions were explored using the polarizable continuum model (PCM) for the solvent tetrahydrofuran (THF). Markovnikov-type vinyl sulfides or cis-configured anti-Markovnikov-type products were formed by three possible pathways. Our calculation results suggested the following: (1) the first step of the cycle is a proton-transfer process from thiols onto the palladium atom to form a palladium-thiolate intermediate. The palladium-thiolate species is attacked on alkynes to obtain an elimination product, liberating the catalyst. (2) The higher activation energies for the alkyne into the palladium-thiolate bond indicate that this step is the rate-determining step. The Markovnikov-type vinyl sulfide product is favored. However, for the aromatic alkyne, the cis-configured anti-Markovnikov-type product is favored. (3) The activation energy would reduce when thiols are substituted with an aromatic group. Our calculated results are consistent with the experimental observations of Frech and colleagues for the palladium-catalyzed hydrothiolation of alkynes to thiols.

Bank Size and Small- and Medium-sized Enterprise (SME) Lending: Evidence from China

Science.gov (United States)

SHEN, YAN; SHEN, MINGGAO; XU, ZHONG; BAI, YING

2014-01-01

Summary Using panel data collected in 2005, we evaluate how bank size, discretion over credit, incentive schemes, competition, and the institutional environment affect lending to small- and medium-sized enterprises in China. We deal with the endogeneity problem using instrumental variables, and a reduced-form approach is also applied to allow for weak instruments in estimation. We find that total bank asset is an insignificant factor for banks’ decision on small- and medium-enterprise (SME) lending, but more local lending authority, more competition, carefully designed incentive schemes, and stronger law enforcement encourage commercial banks to lend to SMEs. PMID:26052179

Bank Size and Small- and Medium-sized Enterprise (SME) Lending: Evidence from China.

Science.gov (United States)

Shen, Yan; Shen, Minggao; Xu, Zhong; Bai, Ying

2009-04-01

Using panel data collected in 2005, we evaluate how bank size, discretion over credit, incentive schemes, competition, and the institutional environment affect lending to small- and medium-sized enterprises in China. We deal with the endogeneity problem using instrumental variables, and a reduced-form approach is also applied to allow for weak instruments in estimation. We find that total bank asset is an insignificant factor for banks' decision on small- and medium-enterprise (SME) lending, but more local lending authority, more competition, carefully designed incentive schemes, and stronger law enforcement encourage commercial banks to lend to SMEs.

Sponge-like silver obtained by decomposition of silver nitrate hexamethylenetetramine complex

Energy Technology Data Exchange (ETDEWEB)

Afanasiev, Pavel, E-mail: pavel.afanasiev@ircelyon.univ-lyon.fr

2016-07-15

Silver nitrate hexamethylenetetramine [Ag(NO{sub 3})·N{sub 4}(CH{sub 2}){sub 6}] coordination compound has been prepared via aqueous route and characterized by chemical analysis, XRD and electron microscopy. Decomposition of [Ag(NO{sub 3})·N{sub 4}(CH{sub 2}){sub 6}] under hydrogen and under inert has been studied by thermal analysis and mass spectrometry. Thermal decomposition of [Ag(NO{sub 3})·N{sub 4}(CH{sub 2}){sub 6}] proceeds in the range 200–250 °C as a self-propagating rapid redox process accompanied with the release of multiple gases. The decomposition leads to formation of sponge-like silver having hierarchical open pore system with pore size spanning from 10 µm to 10 nm. The as-obtained silver sponges exhibited favorable activity toward H{sub 2}O{sub 2} electrochemical reduction, making them potentially interesting as non-enzyme hydrogen peroxide sensors. - Graphical abstract: Thermal decomposition of silver nitrate hexamethylenetetramine coordination compound [Ag(NO{sub 3})·N{sub 4}(CH{sub 2}){sub 6}] leads to sponge like silver that possesses open porous structure and demonstrates interesting properties as an electrochemical hydrogen peroxide sensor. Display Omitted - Highlights: • [Ag(NO{sub 3})·N{sub 4}(CH{sub 2}){sub 6}] orthorhombic phase prepared and characterized. • Decomposition of [Ag(NO{sub 3})·N{sub 4}(CH{sub 2}){sub 6}] leads to metallic silver sponge with opened porosity. • Ag sponge showed promising properties as a material for hydrogen peroxide sensors.

Carbon nanotubes decorated with palladium nanoparticles : Synthesis, characterization, and catalytic activity

NARCIS (Netherlands)

Karousis, Nikolaos; Tsotsou, Georgia-Eleni; Evangelista, Fabrizio; Rudolf, Petra; Ragoussis, Nikitas; Tagmatarchis, Nikos

2008-01-01

In this article, the in situ preparation of palladium nanoparticles, as mediated by the self-regulated reduction of palladium acetate with the aid of sodium dodecyl sulfate (SDS), followed by subsequent deposition onto single-walled carbon nanotubes and multimalled carbon nanotubes (MWCNTs), is

Synthesis of pure colloidal silver nanoparticles with high electroconductivity for printed electronic circuits: the effect of amines on their formation in aqueous media.

Science.gov (United States)

Natsuki, Jun; Abe, Takao

2011-07-01

This paper describes a practical and convenient method to prepare stable colloidal silver nanoparticles for use in printed electronic circuits. The method uses a dispersant and two kinds of reducing agents including 2-(dimethylamino) ethanol (DMAE), which play important roles in the reduction of silver ions in an aqueous medium. The effect of DMAE and dispersant, as well as the factors affecting particle size and morphology are investigated. In the formation of the silver nanoparticles, reduction occurs rapidly at room temperature and the silver particles can be separated easily from the mixture in a short time. In addition, organic solvents are not used. Pure, small and relatively uniform particles with a diameter less than 10 nm can be obtained that exhibit high electroconductivity. The silver nanoparticles are stable, and can be isolated as a dried powder that can be fully redispersed in deionized water. This method of producing colloidal silver nanoparticles will find practical use in electronics applications. Copyright © 2011 Elsevier Inc. All rights reserved.

Internationalization of small and medium-sized enterprises

Directory of Open Access Journals (Sweden)

Zoran Paunović

2010-06-01

Full Text Available Highly developed countries, which are similar to Croatia by size and population, highlight the importance of small and medium-sized enterprises (SMEs as holders of export activities and key factors in raising the competitiveness of the entire economy. In this paper authors research the concept of internationalization of SMEs. Analyzing the influence of decision makers on the process of internationalization and showing its advantages and disadvantages for the respective company and country, this research introduces the most common models on the basis of which this process is implemented in practice. A case study of a small export company from Croatia illustrates the process of internationalization to the U.S. market and provides useful information to the companies which are planning to enter new markets.

Small-sized reverberation chamber for the measurement of sound absorption

International Nuclear Information System (INIS)

Rey, R. del; Alba, J.; Bertó, L.; Gregori, A.

2017-01-01

This paper presents the design, construction, calibration and automation of a reverberation chamber for small samples. A balance has been sought between reducing sample size, to reduce the manufacturing costs of materials, and finding the appropriate volume of the chamber, to obtain reliable values at high and mid frequencies. The small-sized reverberation chamber, that was built, has a volume of 1.12 m3 and allows for the testing of samples of 0.3 m2. By using diffusers, to improve the diffusion degree, and automating measurements, we were able to improve the reliability of the results, thus reducing test errors. Several comparison studies of the measurements of the small-sized reverberation chamber and the standardised reverberation chamber are shown, and a good degree of adjustment can be seen between them, within the range of valid frequencies. This paper presents a small laboratory for comparing samples and making decisions before the manufacturing of larger sizes. [es

A sunlight-induced method for rapid biosynthesis of silver nanoparticles using an Andrachnea chordifolia ethanol extract

Energy Technology Data Exchange (ETDEWEB)

Karimi Zarchi, A.A.; Faridi Majidi, R. [Tehran University of Medical Sciences, Department of Nanomedicine, School of Advanced Medical Technologies, Tehran (Iran, Islamic Republic of); Mokhtari, N.; Shahverdi, A.R. [Tehran University of Medical Sciences, Department of Pharmaceutical Biotechnology and Medicinal Plants Research Center, Faculty of Pharmacy, Tehran (Iran, Islamic Republic of); Arfan, M.; Rehman, T.; Ali, M. [University of Peshawar, Institute of Chemical Sciences, Peshawar, Khyber Pakhtoonkhwa (Pakistan); Amini, M. [Tehran University of Medical Sciences, Department of Medicinal Chemistry, Faculty of Pharmacy, Tehran (Iran, Islamic Republic of)

2011-05-15

In this study a sunlight-induced method for rapid synthesis of silver nanoparticles using an ethanol extract of Andrachnea chordifolia is described. The silver nitrate solutions (1 mM) containing the ethanol extract of Andrachnea chordifolia were irradiated by both sunlight radiation and by sunlight radiation passed through different colored filters (red, yellow or green). The smallest size of silver nanoparticles was obtained when a silver ion solution was irradiated for 5 minutes by direct sunlight radiation. Further examination of the shape and size and of the surface chemistry of these biogenic silver nanoparticles, which were prepared under sunlight radiation, was carried out using transmission electron microscopy and infrared spectroscopy, respectively. Transmission electron microscopy images show spherical particles with an average size of 3.4 nm. Hydroxyl residues were also detected on the surface of these biogenic silver nanoparticles fabricated using plant extract of Andrachnea chordifolia under sunlight radiation. Our study on the reduction of silver ions by this plant extract in darkness shows that the synthesis process can take place under dark conditions at much longer incubations (48 hours). Larger silver polydispersed nanoparticles ranging in size from 3 to 30 nm were obtained when the silver ions were treated with the ethanol extract of Andrachnea chordifolia under dark conditions for 48 hours. (orig.)

Decision Support on Small size Passive Samples

Directory of Open Access Journals (Sweden)

Vladimir Popukaylo

2018-05-01

Full Text Available A construction technique of adequate mathematical models for small size passive samples, in conditions when classical probabilistic-statis\\-tical methods do not allow obtaining valid conclusions was developed.

Oxygen Activated, Palladium Nanoparticle Catalyzed, Ultrafast Cross-Coupling of Organolithium Reagents

NARCIS (Netherlands)

Heijnen, Dorus; Tosi, Filippo; Vila, Carlos; Stuart, Marc C. A.; Elsinga, Philip H.; Szymanski, Wiktor; Feringa, Ben L.

2017-01-01

The discovery of an ultrafast cross-coupling of alkyland aryllithium reagents with a range of aryl bromides is presented. The essential role of molecular oxygen to form the active palladium catalyst was established; palladium nanoparticles that are highly active in cross-coupling reactions with

Palladium sulphide (PdS) films as a new thermoelectric sulphide compound

Energy Technology Data Exchange (ETDEWEB)

Ares, J.R.; Diaz-Chao, P.; Clamagirand, J.; Macia, M.D.; Ferrer, I.J.; Sanchez, C. [Universidad Autonoma de Madrid (Spain). Lab. de Materiales de Interes en Energias Renovables

2010-07-01

Palladium sulphide (PdS) films have been prepared by direct sulphuration of 20 nm thick palladium films at different temperatures (200 C < T < 450 C). Sulphurated films exhibit an unique crystalline phase: PdS. Seebeck coefficient and electrical resistivity of these films are between -110 and -150 {mu}V/K and {proportional_to} 0.08 to 0.8 {omega}cm depending on the sulphuration temperature. Negative sign of Seebeck coefficient indicates an n type conduction in all films. Discussion is focused on the influence of atomic ratio between sulphur and palladium as well as impurities arising from the substrate on transport properties. (orig.)

Green synthesis of silver nanoparticles using tannins

Science.gov (United States)

Raja, Pandian Bothi; Rahim, Afidah Abdul; Qureshi, Ahmad Kaleem; Awang, Khalijah

2014-09-01

Colloidal silver nanoparticles were prepared by rapid green synthesis using different tannin sources as reducing agent viz. chestnut (CN), mangrove (MG) and quebracho (QB). The aqueous silver ions when exposed to CN, MG and QB tannins were reduced which resulted in formation of silver nanoparticles. The resultant silver nanoparticles were characterized using UV-Visible, X-ray diffraction (XRD), scanning electron microscopy (SEM/EDX), and transmission electron microscopy (TEM) techniques. Furthermore, the possible mechanism of nanoparticles synthesis was also derived using FT-IR analysis. Spectroscopy analysis revealed that the synthesized nanoparticles were within 30 to 75 nm in size, while XRD results showed that nanoparticles formed were crystalline with face centered cubic geometry.

Extracellular Production of Silver Nanoparticles by Using Three Common Species of Dermatophytes: Trichophyton rubrum, Trichophyton mentagrophytes and Microsporum canis

International Nuclear Information System (INIS)

Moazeni, M.; Rashidi, N.; Shahverdi, Ahmad R.; Noorbakhsh, F.; Rezaie, S.

2012-01-01

To develop a new green approach for biosynthesis of silver nanoparticles, myconanotechnology has been represented as a novel field of study in nano technology. In this study, we have reported the extracellular synthesis of highly stable silver nanoparticles using three species of dermatophytes: Trichophyton rubrum, Trichophyton mentagrophytes and Microsporum canis. Methods: Clinical strains of these species were grown in a liquid medium containing mineral salt and incubated at 25 d egree C for 5-7 days. The cell-free filtrate of each culture was obtained and subjected to synthesize silver nanoparticles in the presence of 1 m M AgNO 3 . Results: The reduction of Ag + ions in metal nanoparticles was investigated virtually by tracing the solution color which was switched into reddish-light brown after 72 h. For T. mentagrophytes, a UV-visible spectra demonstrating a strong, quite narrow peak located between 422 and 425 nm was obtained. For M. canis, a fairly wide peak centering at 441 nm and for T. rubrum, a weak spectrum to decipher were observed. According to transmission electron microscopy results, fairly uniform, spherical, and small in size with almost less than 50 nm particles were forms in case of T. mentagrophytes. For the other two species, transmission electron microscopy images showed existence of small spherical nano silvers but not as small as nanoparticles synthesized by T. mentagrophytes. Conclusion: We observed that species belong to a single genus of the fungi have variable ability to synthesize silver nanoparticles extracellulary with different efficiency. Furthermore, the extracellular synthesis may make the process simpler and easier for following processes.

Iodine, krypton and xenon retention efficiencies of silver impregnated silica gel media with different silver loadings and under different test conditions

Energy Technology Data Exchange (ETDEWEB)

Motes, B G; Fernandez, S J; Tkachyk, J W

1983-02-01

The purpose of an independent study conducted by Exxon Nuclear Idaho, Co. (ENICO) was to evaluate a silver impregnated silica gel adsorption medium associated with a radioiodine air sampler developed at Brookhaven National Laboratory (BNL). Specifically, ENICO's responsibility was to evaluate the iodine and noble gas retention efficiencies of the adsorption medium. The evaluation was comprised of a four-phase program: 1) test assemblies capable of challenging the silver silica gel filled adsorber canister with radioiodine species or noble gases at flow rates up to 10 scfm and relative humidities up to 83% were constructed; 2) more than 45 kgs of the 4 and 8% silver impregnated silica gel were prepared and characterized for particle size distribution, bulk silver content, bulk density, and silver content by particle size; 3) iodine species retention efficiencies of the silver silica gel were determined; and 4 krypton and xenon retention efficiencies were measured. The iodine species retention efficiencies were greater than 90% under most conditions. A combination of flow rates >5 scfm and 4% silver loaded silica gel reduced the methyl iodide retention efficiency to less than 90%. The retention efficiencies for both krypton and xenon were on the order of 8 x 10{sup -2}% and were not affected greatly by any test variable except test duration. A reduced retention efficiency with increased test durations indicates adsorption equilibrium may be established within five minutes. (author)

Kinetic formation of silver-copper nanoparticles and its characterization

Science.gov (United States)

Zulkafi, Nurul Hikmah; Idrus, Nor Faeqah; Jai, Junaidah; Hadi, Abdul

2017-12-01

A study of the kinetic formation of silver-copper nanoparticles in aqueous medium on the basis of size distribution and its characterization has been carried out and reported in this paper. The Ag-Cu nanoparticles were synthesized through polyol method that using Ethylene Glycol (H2C6O12) as a reduction agent and solvent and Polyoxyethylene-(80)-Sorbitan Monooleate (Tween 80) as a stabilizer. The kinetic formation of Ag-Cu nanoparticles was observed using Dynamic Light Scattering (DLS) and characterized by using X-ray Diffraction (XRD), Field Emission Scanning Electron Microscope (FESEM) and Transmission Electron Microscope (TEM). The XRD analysis results confirmed that size distribution was strongly dependent on molarity of precursors of silver (AgNO3) and copper (Cu(NO3)2.3H2O). The FESEM and TEM analysis indicated the existence of Ag and Cu nanoparticles in the core-shell shape. The silver-copper nanoparticles were spherical and uniform particles size with the average size of about 28 nm and 38 nm for silver and copper, respectively. DLS observation showed the growth of nanoparticles at the temperature of 140°C as the effect of reaction time at 1, 2, 3, 4 and 5 hours.

Method for recovering palladium and technetium values from nuclear fuel reprocessing waste solutions

Science.gov (United States)

Horwitz, E. Philip; Delphin, Walter H.

1979-07-24

A method for recovering palladium and technetium values from nuclear fuel reprocessing waste solutions containing these and other values by contacting the waste solution with an extractant of tricaprylmethylammonium nitrate in an inert hydrocarbon diluent which extracts the palladium and technetium values from the waste solution. The palladium and technetium values are recovered from the extractant and from any other coextracted values with a strong nitric acid strip solution.

76 FR 70680 - Small Business Size Standards: Real Estate and Rental and Leasing

Science.gov (United States)

2011-11-15

... eligibility for Federal small business assistance, SBA establishes small business size definitions (referred... business definition or size standard established by the SBA Administrator. SBA considers as part of its... SMALL BUSINESS ADMINISTRATION 13 CFR Part 121 RIN 3245-AG28 Small Business Size Standards: Real...

Development of anodic stripping voltametry for the determination of palladium in high level nuclear waste

Energy Technology Data Exchange (ETDEWEB)

Bhardwaj, T. K. [North Carolina State University, Raleigh (United States); Sharma, H. S.; Affarwal, S. K. [Bhabha Atomic Research Centre, Mumbai (India); Jain, P. C. [Meerut College, Meerut (India)

2012-12-15

Deposition potential, deposition time, square wave frequency, rotation speed of the rotating disc electrode, and palladium concentration were studied on a Glassy Carbon Electrode (GCE) in 0.01M HCl for the determination of palladium in High Level Nuclear Waste (HLNW) by anodic stripping voltammetry. Experimental conditions were optimized for the determination of palladium at two different, 10-8 and 10-7 M, levels. Error and standard deviation of this method were under 1% for all palladium standard solutions. The developed technique was successfully applied as a subsidiary method for the determination of palladium in simulated high level nuclear waste with very good precision and high accuracy (under 1 % error and standard deviation).

77 FR 76215 - Small Business Size Regulations, Small Business Innovation Research (SBIR) Program and Small...

Science.gov (United States)

2012-12-27

... overall goal of simplification and maximization of benefits for small businesses, SBA proposed amendments... franchisee. F. Section 121.704--When SBA Determines Size and Eligibility SBA's proposed regulations for the...

76 FR 8221 - Small Business Size Regulations; 8(a) Business Development/Small Disadvantaged Business Status...

Science.gov (United States)

2011-02-11

... Vol. 76 Friday, No. 29 February 11, 2011 Part VII Small Business Administration 13 CFR Parts 121 and 124 Small Business Size Regulations; 8(a) Business Development/Small Disadvantaged Business Status... Regulations#0;#0; [[Page 8222

Irradiation of silver and agar/silver nanoparticles with argon, oxygen glow discharge plasma, and mercury lamp.

Science.gov (United States)

Ahmad, Mahmoud M; Abdel-Wahab, Essam A; El-Maaref, A A; Rawway, Mohammed; Shaaban, Essam R

2014-01-01

The irradiation effect of argon, oxygen glow discharge plasma, and mercury lamp on silver and agar/silver nanoparticle samples is studied. The irradiation time dependence of the synthesized silver and agar/silver nanoparticle absorption spectra and their antibacterial effect are studied and compared. In the agar/silver nanoparticle sample, as the irradiation time of argon glow discharge plasma or mercury lamp increases, the peak intensity and the full width at half maximum, FWHM, of the surface plasmon resonance absorption band is increased, however a decrease of the peak intensity with oxygen glow plasma has been observed. In the silver nanoparticle sample, as the irradiation time of argon, oxygen glow discharge plasma or mercury lamp increases, the peak intensity of the surface plasmon resonance absorption band is increased, however, there is no significant change in the FWHM of the surface plasmon resonance absorption band. The SEM results for both samples showed nanoparticle formation with mean size about 50 nm and 40 nm respectively. Throughout the irradiation time with the argon, oxygen glow discharge plasma or mercury lamp, the antibacterial activity of several kinds of Gram-positive and Gram-negative bacteria has been examined.

Toxicity of silver nanoparticles in monocytes and keratinocytes

DEFF Research Database (Denmark)

Orłowski, Piotr; Krzyzowska, Malgorzata; Winnicka, Anna

2012-01-01

Silver nanoparticles are of interest to be used as antimicrobial agents in wound dressings and coatings in medical devices, but potential adverse effects have been reported in the literature. The possible local inflammatory response to silver nanoparticles and the role of cell death in determining...... these effects are largely unknown. Effects of the mixture of silver nanoparticles of different sizes were compared in in vitro assays for cytotoxicity, caspase-1 and caspase-9 activity and bax expression. In all tested concentrations, silver nanoparticles were more toxic for RAW 264.7 monocytes than for 291.03C...... keratinocytes and induced significant caspase-1 activity and necrotic cell death. In keratinocytes, more significantly than in macrophages, silver nanoparticles led to increase of caspase-9 activity and apoptosis. These results indicate that effects of silver nanoparticles depend on the type of exposed cells...

Palladium silicide - a new contact for semiconductor radiation detectors

International Nuclear Information System (INIS)

Totterdell, D.H.J.

1981-11-01

Silicide layers can be used as low resistance contacts in semiconductor devices. The formation of a metal rich palladium silicide Pd 2 Si is discussed. A palladium film 100A thick is deposited at 300 0 C and the resulting silicide layer used as an ohmic contact in an n + p silicon detector. This rugged contact has electrical characteristics comparable with existing evaporated gold contacts and enables the use of more reproducible bonding techniques. (author)

Preparation and Characterization of Silver Liquid Thin Films for Magnetic Fluid Deformable Mirror

Directory of Open Access Journals (Sweden)

Lianchao Zhang

2015-01-01

Full Text Available Silver liquid thin film, formed by silver nanoparticles stacking and spreading on the surface of the liquid, is one of the important parts of magnetic fluid deformable mirror. First, silver nanoparticles were prepared by liquid phase chemical reduction method using sodium citrate as reducing agent and stabilizer and silver nitrate as precursor. Characterization of silver nanoparticles was studied using X-ray diffractometer, UV-vis spectrophotometer, and transmission electron microscope (TEM. The results showed that silver nanoparticles are spherical and have a good monodispersity. Additionally, the effect of the reaction conditions on the particle size of silver is obvious. And then silver liquid thin films were prepared by oil-water two-phase interface technology using as-synthesized silver nanoparticles. Properties of the film were investigated using different technology. The results showed that the film has good reflectivity and the particle size has a great influence on the reflectivity of the films. SEM photos showed that the liquid film is composed of multilayer silver nanoparticles. In addition, stability of the film was studied. The results showed that after being stored for 8 days under natural conditions, the gloss and reflectivity of the film start to decrease.

Comparison on Bactericidal and Cytotoxic Effect of Silver Nanoparticles Synthesized by Different Methods

Science.gov (United States)

Mala, R.; Celsia, A. S. Ruby; Malathi Devi, S.; Geerthika, S.

2017-08-01

Biologically synthesized silver nanoparticle are biocompatible for medical applications. The present work is aimed to synthesize silver nanoparticle using the fruit pulp of Tamarindusindica and to evaluate its antibacterial and anticancer activity against lung cancercell lines. Antibacterial activity was assessed by well diffusion method. Cytotoxicity was evaluated using MTT assay. GC-MS of fruit pulp extract showed the presence of levoglucosenone, n-hexadecanoic acid, 9,12-octadecadienoic acid etc. Antioxidant activity of the fruit pulp was determined by DPPH assay, hydrogen peroxide scavenging assay and lipid peroxidation. The size of biologically synthesized silver nanoparticle varied from 50 nm to 76 nm. It was 59 nm to 98 nm for chemically synthesized silver nanoparticle. Biologically synthesized silver nanoparticle showed 26 mm inhibition zone against E. coli and chemically synthesized silver nanoparticle showed 20 mm. Antioxidant activity of fruit extract by DPPH showed 84 % reduction. The IC 50 of biologically synthesized silver nanoparticle against lung cancer cell lines was 48 µg/ml. It was 95 µg/ml for chemically synthesized silver nanoparticle. The increased activity of biologically synthesized silver nanoparticle was due to its smaller size, stability and the bioactive compounds capping the silver nanoparticle extracted from the fruit extract.

77 FR 11001 - Small Business Size Standards: Health Care and Social Assistance

Science.gov (United States)

2012-02-24

..., and (3) within a specific small business definition or size standard established by the SBA... SMALL BUSINESS ADMINISTRATION 13 CFR Part 121 RIN 3245-AG30 Small Business Size Standards: Health Care and Social Assistance AGENCY: U.S. Small Business Administration. ACTION: Proposed rule. SUMMARY...

77 FR 55755 - Small Business Size Standards: Agriculture, Forestry, Fishing, and Hunting

Science.gov (United States)

2012-09-11

... operation; and (3) within a specific small business definition or size standard established by SBA... SMALL BUSINESS ADMINISTRATION 13 CFR Part 121 RIN 3245-AG43 Small Business Size Standards: Agriculture, Forestry, Fishing, and Hunting AGENCY: U.S. Small Business Administration. ACTION: Proposed rule...

76 FR 27952 - Small Business Size Standards: Professional, Scientific and Technical Services.

Science.gov (United States)

2011-05-13

... Administration (SBA or Agency) proposed to increase small business size standards for 35 industries and one sub... SMALL BUSINESS ADMINISTRATION 13 CFR Part 121 RIN 3245-AG07 Small Business Size Standards: Professional, Scientific and Technical Services. AGENCY: U.S. Small Business Administration. ACTION: Proposed...

Ultrasonic electrodeposition of silver nanoparticles on dielectric silica spheres

International Nuclear Information System (INIS)

Tang Shaochun; Tang Yuefeng; Gao Feng; Liu Zhiguo; Meng Xiangkang

2007-01-01

In the present study, a facile and one-step ultrasonic electrodeposition method is first applied to controllably coat colloidal silica spheres with silver nanoparticles. This method is additive-free and very direct, because processes necessary in many other approaches, such as pretreatment of the silica sphere surface and pre-preparation of silver nanoparticles, are not involved in it. Furthermore, it makes possible the coating of dielectric substrates with metal through an electrodeposition route. Under appropriate conditions, silver nanoparticles with sizes of 8-10 nm in diameter can be relatively homogeneously deposited onto the surface of preformed colloidal silica spheres. Silver particles with different sizes and dispersive uniformity on silica sphere surfaces can also be obtained by adjusting the current density (I), the concentration of electrolyte (C) and the electrolysis time (t). The possible ultrasonic electrodeposition mechanism is also suggested according to the experimental results

Palladium alloys for hydrogen diffusion

International Nuclear Information System (INIS)

1977-01-01

A palladium-base alloy with tin and/or a silicon addition and its use in the production of hydrogen from water via a cycle of chemical reactions, of which the decomposition of HI into H 2 and I 2 is the most important, is described

Synthesis and characterization of nano silver ferrite composite

International Nuclear Information System (INIS)

Murthy, Y.L.N.; Kondala Rao, T.; Kasi viswanath, I.V.; Singh, Rajendra

2010-01-01

We report the synthesis of nano sized silver ferrite composite having the empirical formula AgFeO 2 by a co-precipitation method. The resulting powders are thin platelets, transparent and a rich ruby red in color in transmission. The X-ray diffraction (XRD) powder data consisted of only nine reflections, and the analysis showed the unit cell to be rhombohedral. The powders showed extensive XRD line broadening and the sizes of the crystals are calculated to be in the range 4-36.5 nm. The morphology of the silver ferrite composite studied using scanning electron microscope showed nano sized particles. The particle size is found to increase with increase in annealing temperature. The magnetic behavior, measured using a vibrating sample magnetometer, indicated a change from paramagnetic to ferromagnetic with increase in particle size.

78 FR 45051 - Small Business Size Standards; Support Activities for Mining; Correction

Science.gov (United States)

2013-07-26

... Regulations by increasing small business size standards for three of the four industries in North American... SMALL BUSINESS ADMINISTRATION 13 CFR Part 121 RIN 3245-AG44 Small Business Size Standards; Support Activities for Mining; Correction AGENCY: U.S. Small Business Administration. ACTION: Final rule; correction...

Small renal size in newborns with spina bifida: possible causes.

Science.gov (United States)

Montaldo, Paolo; Montaldo, Luisa; Iossa, Azzurra Concetta; Cennamo, Marina; Caredda, Elisabetta; Del Gado, Roberto

2014-02-01

Previous studies reported that children with neural tube defects, but without any history of intrinsic renal diseases, have small kidneys when compared with age-matched standard renal growth. The aim of this study was to investigate the possible causes of small renal size in children with spina bifida by comparing growth hormone deficiency, physical limitations and hyperhomocysteinemia. The sample included 187 newborns with spina bifida. Renal sizes in the patients were assessed by using maximum measurement of renal length and the measurements were compared by using the Sutherland monogram. According to the results, the sample was divided into two groups--a group of 120 patients with small kidneys (under the third percentile) and a control group of 67 newborns with normal kidney size. Plasma total homocysteine was investigated in mothers and in their children. Serum insulin-like growth factor-1 (IGF-1) levels were measured. Serum IGF-1 levels were normal in both groups. Children and mothers with homocysteine levels >10 μmol/l were more than twice as likely to have small kidneys and to give to birth children with small kidneys, respectively, compared with newborns and mothers with homocysteine levels <10 μmol/l. An inverse correlation was also found between the homocysteine levels of mothers and kidney sizes of children (r = - 0.6109 P ≤ 0.01). It is highly important for mothers with hyperhomocysteinemia to be educated about benefits of folate supplementation in order to reduce the risk of small renal size and lower renal function in children.

Metal allergen of the 21st century--a review on exposure, epidemiology and clinical manifestations of palladium allergy

DEFF Research Database (Denmark)

Faurschou, Annesofie; Menné, Torkil; Johansen, Jeanne D

2011-01-01

Consumers are mainly exposed to palladium from jewellery and dental restorations. Palladium contact allergy is nearly always seen together with nickel allergy, as palladium and nickel tend to cross-react. We aimed to analyse the available palladium patch test data and case reports to determine...

From mineral industry to industrial waste recycling: the Valme Company in Falaise

Energy Technology Data Exchange (ETDEWEB)

Delubac, G

1993-07-01

Computers reach their final destination in the Calvados town of Falaise. There, the Valme Company recovers the gold, silver and palladium contained in computer parts. On average, Valme thus recovers between 500 and 600 kg of gold, 4.5 tons of silver, and 100 to 150 kg of palladium per year. The Falaise plant also handles refining of the Rouez-en-Champagne gold mining products. (Author). 4 figs.

Thin film platinum–palladium thermocouples for gas turbine engine applications

Energy Technology Data Exchange (ETDEWEB)

Tougas, Ian M.; Gregory, Otto J., E-mail: gregory@egr.uri.edu

2013-07-31

Thin film platinum:palladium thermocouples were fabricated on alumina and mullite surfaces using radio frequency sputtering and characterized after high temperature exposure to oxidizing environments. The thermoelectric output, hysteresis, and drift of these sensors were measured at temperatures up to 1100 °C. Auger electron spectroscopy was used to follow the extent of oxidation in each thermocouple leg and interdiffusion at the metallurgical junction. Minimal oxidation of the platinum and palladium thermoelements was observed after high temperature exposure, but considerable dewetting and faceting of the films were observed in scanning electron microscopy. An Arrhenius temperature dependence on the drift rate was observed and later attributed to microstructural changes during thermal cycling. The thin film thermocouples, however, did exhibit excellent stability at 1000 °C with drift rates comparable to commercial type-K wire thermocouples. Based on these results, platinum:palladium thin film thermocouples have considerable potential for use in the hot sections of gas turbine engines. - Highlights: • Stable thin film platinum:palladium thermocouples for gas turbine engines • Little oxidation but significant microstructural changes from thermal cycling • Minimal hysteresis during repeated thermal cycling • Drift comparable to commercial wire thermocouples.