  1. Plasma Treated Multi-Walled Carbon Nanotubes (MWCNTs for Epoxy Nanocomposites

    Directory of Open Access Journals (Sweden)

    Jie Lian

    2011-12-01

    Full Text Available Plasma nanocoating of allylamine were deposited on the surfaces of multi-walled carbon nanotubes (MWCNTs to provide desirable functionalities and thus to tailor the surface characteristics of MWCNTs for improved dispersion and interfacial adhesion in epoxy matrices. Plasma nanocoated MWCNTs were characterized using scanning electron microscopy (SEM, high-resolution transmission electron microscopy (HR-TEM, surface contact angle, and pH change measurements. Mechanical testing results showed that epoxy reinforced with 1.0 wt % plasma coated MWCNTs increased the tensile strength by 54% as compared with the pure epoxy control, while epoxy reinforced with untreated MWCNTs have lower tensile strength than the pure epoxy control. Optical and electron microscopic images show enhanced dispersion of plasma coated MWCNTs in epoxy compared to untreated MWCNTs. Plasma nanocoatings from allylamine on MWCNTs could significantly enhance their dispersion and interfacial adhesion in epoxy matrices. Simulation results based on the shear-lag model derived from micromechanics also confirmed that plasma nanocoating on MWCNTs significantly improved the epoxy/fillers interface bonding and as a result the increased composite strength.

  2. Growth of carbon nanotubes in arc plasma treated graphite disc: microstructural characterization and electrical conductivity study

    Science.gov (United States)

    Nayak, B. B.; Sahu, R. K.; Dash, T.; Pradhan, S.

    2018-03-01

    Circular graphite discs were treated in arc plasma by varying arcing time. Analysis of the plasma treated discs by field emission scanning electron microscope revealed globular grain morphologies on the surfaces, but when the same were observed at higher magnification and higher resolution under transmission electron microscope, growth of multiwall carbon nanotubes of around 2 nm diameter was clearly seen. In situ growth of carbon nanotube bundles/bunches consisting of around 0.7 nm tube diameter was marked in the case of 6 min treated disc surface. Both the untreated and the plasma treated graphite discs were characterized by X-ray diffraction, energy dispersive spectra of X-ray, X-ray photoelectron spectroscopy, transmission electron microscopy, micro Raman spectroscopy and BET surface area measurement. From Raman spectra, BET surface area and microstructure observed in transmission electron microscope, growth of several layers of graphene was identified. Four-point probe measurements for electrical resistivity/conductivity of the graphite discs treated under different plasma conditions showed significant increase in conductivity values over that of untreated graphite conductivity value and the best result, i.e., around eightfold increase in conductivity, was observed in the case of 6 min plasma treated sample exhibiting carbon nanotube bundles/bunches grown on disc surface. By comparing the microstructures of the untreated and plasma treated graphite discs, the electrical conductivity increase in graphite disc is attributed to carbon nanotubes (including bundles/bunches) growth on disc surface by plasma treatment.

  3. Interactions between plasma-treated carbon nanotubes and electrically neutral materials

    Science.gov (United States)

    Ogawa, Daisuke; Nakamura, Keiji

    2014-10-01

    A plasma treatment can create dangling bonds on the surface of carbon nanotubes (CNTs). The dangling bonds are so reactive that the bonds possibly interact with other neutral species even out of the plasma if the lifetime of the bonds is effectively long. In order to have good understandings with the interactions, we placed multi-wall CNTs (MWCNTs) in atmospheric dielectric barrier discharge that was created in a closed environment with the voltage at 5 kV. We set 50 W for the operating power and 15 minutes for the process time for this plasma treatment. Our preliminary results showed that the reaction between dangling bonds and neutrals likely occurred in the situation when CNTs were treated with argon plasma, and then exposed in a nitrogen-rich dry box. We did Fourier transform infrared (FTIR) spectroscopy after the treatments. The measurement showed that the spectrum with plasma-treated CNTs was different from pristine CNTs. This is an indication that the plasma-treated CNTs have reactive cites on the surface even after the discharge (~ minutes), and then the CNTs likely reacted with the neutral species that causes the different spectrum. In this poster, we will show more details from our results and further progresses from this research.

  4. Plasma Treated Active Carbon for Capacitive Deionization of Saline Water

    Directory of Open Access Journals (Sweden)

    Aiping Zeng

    2017-01-01

    Full Text Available The plasma treatment on commercial active carbon (AC was carried out in a capacitively coupled plasma system using Ar + 10% O2 at pressure of 4.0 Torr. The RF plasma power ranged from 50 W to 100 W and the processing time was 10 min. The carbon film electrode was fabricated by electrophoretic deposition. Micro-Raman spectroscopy revealed the highly increased disorder of sp2 C lattice for the AC treated at 75 W. An electrosorption capacity of 6.15 mg/g was recorded for the carbon treated at 75 W in a 0.1 mM NaCl solution when 1.5 V was applied for 5 hours, while the capacity of the untreated AC was 1.01 mg/g. The plasma treatment led to 5.09 times increase in the absorption capacity. The jump of electrosorption capacity by plasma treatment was consistent with the Raman spectra and electrochemical double layer capacitance. This work demonstrated that plasma treatment was a potentially efficient approach to activating biochar to serve as electrode material for capacitive deionization (CDI.

  5. Interaction of multiwalled carbon nanotube produces structural ...

    African Journals Online (AJOL)

    Abstract. Multiwalled carbon nanotube (MWCNT) has been found to produce structural changes in Calf Thymus-DNA (CT-DNA). The interaction or binding of the multi-walled carbon nanotubes (MWCNT) was investigated in order to discover if it brings about any significant changes of the DNA double helix using CD spectra ...

  6. Multiwall carbon nanotube microcavity arrays

    Energy Technology Data Exchange (ETDEWEB)

    Ahmed, Rajib; Butt, Haider, E-mail: h.butt@bham.ac.uk [Nanotechnology Laboratory, School of Mechanical Engineering, University of Birmingham, Birmingham B15 2TT (United Kingdom); Rifat, Ahmmed A. [Integrated Lightwave Research Group, Department of Electrical Engineering, Faculty of Engineering, University of Malaya, Kuala Lumpur 50603 (Malaysia); Yetisen, Ali K.; Yun, Seok Hyun [Harvard Medical School and Wellman Center for Photomedicine, Massachusetts General Hospital, 65 Landsdowne Street, Cambridge, Massachusetts 02139 (United States); Harvard-MIT Division of Health Sciences and Technology, Massachusetts Institute of Technology, Cambridge, Massachusetts 02139 (United States); Dai, Qing [National Center for Nanoscience and Technology, Beijing 100190 (China)

    2016-03-21

    Periodic highly dense multi-wall carbon nanotube (MWCNT) arrays can act as photonic materials exhibiting band gaps in the visible regime and beyond terahertz range. MWCNT arrays in square arrangement for nanoscale lattice constants can be configured as a microcavity with predictable resonance frequencies. Here, computational analyses of compact square microcavities (≈0.8 × 0.8 μm{sup 2}) in MWCNT arrays were demonstrated to obtain enhanced quality factors (≈170–180) and narrow-band resonance peaks. Cavity resonances were rationally designed and optimized (nanotube geometry and cavity size) with finite element method. Series (1 × 2 and 1 × 3) and parallel (2 × 1 and 3 × 1) combinations of microcavities were modeled and resonance modes were analyzed. Higher order MWCNT microcavities showed enhanced resonance modes, which were red shifted with increasing Q-factors. Parallel microcavity geometries were also optimized to obtain narrow-band tunable filtering in low-loss communication windows (810, 1336, and 1558 nm). Compact series and parallel MWCNT microcavity arrays may have applications in optical filters and miniaturized optical communication devices.

  7. Degradation of multiwall carbon nanotubes by bacteria

    International Nuclear Information System (INIS)

    Zhang, Liwen; Petersen, Elijah J.; Habteselassie, Mussie Y.; Mao, Liang; Huang, Qingguo

    2013-01-01

    Understanding the environmental transformation of multiwall carbon nanotubes (MWCNTs) is important to their life cycle assessment and potential environmental impacts. We report that a bacterial community is capable of degrading 14 C-labeled MWCNTs into 14 CO 2 in the presence of an external carbon source via co-metabolism. Multiple intermediate products were detected, and genotypic characterization revealed three possible microbial degraders: Burkholderia kururiensis, Delftia acidovorans, and Stenotrophomonas maltophilia. This result suggests that microbe/MWCNTs interaction may impact the long-term fate of MWCNTs. Highlights: •Mineralization of MWCNTs by a bacterial community was observed. •The mineralization required an external carbon source. •Multiple intermediate products were identified in the MWCNT degrading culture. •Three bacterial species were found likely responsible for MWCNT degradation. -- The 14 C-labeled multiwall carbon nanotubes can be degraded to 14 CO 2 and other byproducts by a bacteria community under natural conditions

  8. Efficient electrochemical degradation of multiwall carbon nanotubes.

    Science.gov (United States)

    Reipa, Vytas; Hanna, Shannon K; Urbas, Aaron; Sander, Lane; Elliott, John; Conny, Joseph; Petersen, Elijah J

    2018-07-15

    As the production mass of multiwall carbon nanotubes (MWCNT) increases, the potential for human and environmental exposure to MWCNTs may also increase. We have shown that exposing an aqueous suspension of pristine MWCNTs to an intense oxidative treatment in an electrochemical reactor, equipped with an efficient hydroxyl radical generating Boron Doped Diamond (BDD) anode, leads to their almost complete mineralization. Thermal optical transmittance analysis showed a total carbon mass loss of over two orders of magnitude due to the electrochemical treatment, a result consistent with measurements of the degraded MWCNT suspensions using UV-vis absorbance. Liquid chromatography data excludes substantial accumulation of the low molecular weight reaction products. Therefore, up to 99% of the initially suspended MWCNT mass is completely mineralized into gaseous products such as CO 2 and volatile organic carbon. Scanning electron microscopy (SEM) images show sporadic opaque carbon clusters suggesting the remaining nanotubes are transformed into structure-less carbon during their electrochemical mineralization. Environmental toxicity of pristine and degraded MWCNTs was assessed using Caenorhabditis elegans nematodes and revealed a major reduction in the MWCNT toxicity after treatment in the electrochemical flow-by reactor. Published by Elsevier B.V.

  9. Multiwalled Carbon Nanotube Deposition on Model Environmental Surfaces

    Science.gov (United States)

    Deposition of multiwalled carbon nanotubes (MWNTs) on model environmental surfaces was investigated using a quartz crystal microbalance with dissipation monitoring (QCM-D). Deposition behaviors of MWNTs on positively and negatively charged surfaces were in good agreement with Der...

  10. Application of multi-walled carbon nanotubes to enhance anodic ...

    African Journals Online (AJOL)

    STORAGESEVER

    2009-12-15

    Dec 15, 2009 ... Key words: Multi-walled carbon nanotubes, microbial fuel cell, Enterobacter cloacae, ... Aldrich) was prepared in absolute ethanol (Hu et al., 2006; Tkac .... incorporated Eu3+ by voltammetry and electrochemical impedance.

  11. Overview on the Surface Functionalization Mechanism and Determination of Surface Functional Groups of Plasma Treated Carbon Nanotubes.

    Science.gov (United States)

    Saka, Cafer

    2018-01-02

    The use of carbon materials for many applications is due to the unique diversity of structures and properties ranging from chemical bonds between the carbon atoms of the materials to nanostructures, crystallite alignment, and microstructures. Carbon nanotubes and other nanoscale carbonaceous materials draw much attention due to their physical and chemical properties, such as high strength, high resistance to corrosion, electrical and thermal conductivity, stability and a qualified adsorbent. Carbon-based nanomaterials, which have a relatively large specific area and layered structure, can be used as an adsorbent for efficient removal of organic and inorganic contaminants. However, one of the biggest obstacles to the development of carbon-based nanomaterials adsorbents is insolubility and the lack of functional groups on the surface. There are several approaches to introduce functional groups on carbon nanotubes. One of these approaches, plasma applications, now has an important place in the creation of surface functional groups as a flexible, fast, and environmentally friendly method. This review focuses on recent information concerning the surface functionalization and modification of plasma treated carbon nanotube. This review considers the surface properties, advantages, and disadvantages of plasma-applied carbon nanotubes. It also examines the reaction mechanisms involved in the functional groups on the surface.

  12. A thermodynamic model for growth mechanisms of multiwall carbon nanotubes.

    Energy Technology Data Exchange (ETDEWEB)

    Kaatz, Forrest H.; Overmyer, Donald L.; Siegal, Michael P.

    2006-02-01

    Multiwall carbon nanotubes are grown via thermal chemical vapor deposition between temperatures of 630 and 830 C using acetylene in nitrogen as the carbon source. This process is modeled using classical thermodynamics to explain the total carbon deposition as a function of time and temperature. An activation energy of 1.60 eV is inferred for nanotube growth after considering the carbon solubility term. Scanning electron microscopy shows growth with diameters increasing linearly with time. Transmission electron microscopy and Raman spectroscopy show multiwall nanotubes surrounded by a glassy-carbon sheath, which grows with increasing wall thickness as growth temperatures and times rise.

  13. Thermodynamic model for growth mechanisms of multiwall carbon nanotubes

    Science.gov (United States)

    Kaatz, F. H.; Siegal, M. P.; Overmyer, D. L.; Provencio, P. P.; Tallant, D. R.

    2006-12-01

    Multiwall carbon nanotubes are grown via thermal chemical vapor deposition between temperatures of 630 and 830°C using acetylene in nitrogen as the carbon source. This process is modeled using classical thermodynamics to explain the total carbon deposition as a function of time and temperature. An activation energy of 1.60eV is inferred for nanotube growth after considering the carbon solubility term. Scanning electron microscopy shows growth with diameters increasing linearly with time. Transmission electron microscopy and Raman spectroscopy show multiwall nanotubes surrounded by a glassy-carbon sheath, which grows with increasing wall thickness as growth temperatures and times rise.

  14. The Synthesis of Nitrogen-Doped Multiwalled Carbon Nanotubes ...

    African Journals Online (AJOL)

    ACVDmethod was used to prepare high-quality nitrogen-doped multiwalled carbon nanotubes (N-MWCNTs) using acetonitrile as the nitrogen and carbon source and acetylene as a carbon source over an Fe-Co/CaCO3 catalyst in the temperature range 700–850 °C. This represents a continuation of earlier work in which ...

  15. Raman spectroscopic characterization of multiwall carbon nanotubes and of composites

    Directory of Open Access Journals (Sweden)

    L. Bokobza

    2012-07-01

    Full Text Available In this work Raman spectroscopy was used for extensive characterization of multiwall carbon nanotube (MWNTs and of MWCNTs/rubber composites. We have measured the Raman spectra of bundled and dispersed multiwall carbon nanotubes. All the Raman bands of the carbon nanotubes are seen to shift to higher wavenumbers upon debundling on account of less intertube interactions. Effects of laser irradiation were also investigated. Strong effects are observed by changing the wavelength of the laser excitation. On the other hand, at a given excitation wavelength, changes on the Raman bands are observed by changing the laser power density due to sample heating during the measurement procedure.

  16. Application of multi-walled carbon nanotubes to enhance anodic ...

    African Journals Online (AJOL)

    The effect of multi-walled carbon nanotube (MWCNT) modification of anodes and the optimisation of relevant parameters thereof for application in an Enterobacter cloacae microbial fuel cell were examined. The H – type microbial fuel cells were used for the fundamental studies, with a carbon sheet as a control anode and ...

  17. Ag-catalysed cutting of multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    La Torre, A; Rance, G A; Miners, S A; Lucas, C Herreros; Smith, E F; Giménez-López, M C; Khlobystov, A N; Fay, M W; Brown, P D; Zoberbier, T; Kaiser, U

    2016-01-01

    In this work, the cutting of carbon nanotubes is investigated using silver nanoparticles deposited on arc discharge multi-walled carbon nanotubes. The composite is subsequently heated in air to fabricate shortened multi-walled nanotubes. Complementary transmission electron microscopy and spectroscopy techniques shed light on the cutting mechanism. The nanotube cutting is catalysed by the fundamental mechanism based on the coordination of the silver atoms to the π-bonds of carbon nanotubes. As a result of the metal coordination, the strength of the carbon–carbon bond is reduced, promoting the oxidation of carbon at lower temperature when heated in air, or lowering the activation energy required for the removal of carbon atoms by electron beam irradiation, assuring in both cases the cutting of the nanotubes. (paper)

  18. Novel fabrication of silica nanotubes using multi-walled carbon ...

    Indian Academy of Sciences (India)

    Administrator

    Abstract. Silica nanotubes were synthesized using multi-walled carbon nanotubes (MWCNTs) as template. The as-obtained samples were characterized by infrared spectroscopy (FTIR), X-ray diffraction (XRD), transmission electron microscopy (TEM), field emission scanning electron microscope (FE–SEM) and photo-.

  19. Role of iron oxide impurities in electrocatalysis by multiwall carbon

    Indian Academy of Sciences (India)

    The role of iron oxide impurities in the electrocatalytic properties of multiwall carbon nanotubes (MWCNTs) prepared by catalytic chemical vapour decomposition method (CCVD) is studied in detail. A novel magnetically modified electrodes have been developed by which MWCNTs were immobilized on indium-tin oxide ...

  20. Decoration of Multi-walled Carbon Nanotubes by Metal ...

    African Journals Online (AJOL)

    The powder patterns of the as-prepared and acid treated MWCNTs are shown by the XRD spectra. The TEM results show the microstructure of the multi-walled carbon nanotubes well decorated with metal nanoparticles (Cu, Fe, Ni) and metal oxides (CuO, Fe2O3, NiO), while the SEM show the surface morphology.

  1. Preparation of supported electrocatalyst comprising multiwalled carbon nanotubes

    Science.gov (United States)

    Wu, Gang; Zelenay, Piotr

    2013-08-27

    A process for preparing a durable non-precious metal oxygen reduction electrocatalyst involves heat treatment of a ball-milled mixture of polyaniline and multiwalled carbon nanotubes in the presence of a Fe species. The catalyst is more durable than catalysts that use carbon black supports. Performance degradation was minimal or absent after 500 hours of operation at constant cell voltage of 0.40 V.

  2. Thermal Analysis of Copper-Titanium-Multiwall Carbon Nanotube Composites.

    Science.gov (United States)

    Hamamda, Smail; Jari, Ahmed; Revo, S; Ivanenko, K; Jari, Youcef; Avramenko, T

    2017-12-01

    The aim of this research is the thermostructural study of Cu-Ti, Cu-Ti 1 vol% multiwall carbon nanotubes (MWCNTs) and Cu-Ti 3 vol% MWCNTs. Several investigation techniques were used to achieve this objective. Dilatometric data show that the coefficient of thermal expansion of the nanocomposite containing less multiwall carbon nanotubes is linear and small. The same nanocomposite exhibits regular heat transfer and weak mass exchange with the environment. Raman spectroscopy shows that the nanocomposite with more MWCNTs contains more defects. This implies that the carbon nanotubes have better dispersion in Cu-Ti 1 vol% MWCNTs. Infrared spectroscopy reveals that Cu-Ti 1 vol% MWCNTs has better crystallinity than Cu-Ti 3 vol% MWCNTs.

  3. Explosive compaction of aluminum oxide modified by multiwall carbon nanotubes

    Science.gov (United States)

    Buzyurkin, A. E.; Kraus, E. I.; Lukyanov, Ya L.

    2018-04-01

    This paper presents experiments and numerical research on explosive compaction of aluminum oxide powder modified by multiwall carbon nanotubes (MWCNT) and modeling of the stress state behind the shock front at shock loading. The aim of this study was to obtain a durable low-porosity compact sample. The explosive compaction technology is used in this problem because the aluminum oxide is an extremely hard and refractory material. Therefore, its compaction by traditional methods requires special equipment and considerable expenses.

  4. Vertically aligned multiwalled carbon nanotubes as electronic interconnects

    Science.gov (United States)

    Gopee, Vimal Chandra

    The drive for miniaturisation of electronic circuits provides new materials challenges for the electronics industry. Indeed, the continued downscaling of transistor dimensions, described by Moore’s Law, has led to a race to find suitable replacements for current interconnect materials to replace copper. Carbon nanotubes have been studied as a suitable replacement for copper due to its superior electrical, thermal and mechanical properties. One of the advantages of using carbon nanotubes is their high current carrying capacity which has been demonstrated to be three orders of magnitude greater than that of copper. Most approaches in the implementation of carbon nanotubes have so far focused on the growth in vias which limits their application. In this work, a process is described for the transfer of carbon nanotubes to substrates allowing their use for more varied applications. Arrays of vertically aligned multiwalled carbon nanotubes were synthesised by photo-thermal chemical vapour deposition with high growth rates. Raman spectroscopy was used to show that the synthesised carbon nanotubes were of high quality. The carbon nanotubes were exposed to an oxygen plasma and the nature of the functional groups present was determined using X-ray photoelectron spectroscopy. Functional groups, such as carboxyl, carbonyl and hydroxyl groups, were found to be present on the surface of the multiwalled carbon nanotubes after the functionalisation process. The multiwalled carbon nanotubes were metallised after the functionalisation process using magnetron sputtering. Two materials, solder and sintered silver, were chosen to bind carbon nanotubes to substrates so as to enable their transfer and also to make electrical contact. The wettability of solder to carbon nanotubes was investigated and it was demonstrated that both functionalisation and metallisation were required in order for solder to bond with the carbon nanotubes. Similarly, functionalisation followed by metallisation

  5. Multi-walled carbon nanotubes integrated in microcantilevers for application of tensile strain

    DEFF Research Database (Denmark)

    Dohn, Søren; Kjelstrup-Hansen, Jakob; Madsen, D.N.

    2005-01-01

    variations in the response. Using a simple resistor model we estimate the expected conductance-strain response for a multi-walled carbon nanotube, and compare to our results on multi-walled carbon nanotubes as well as measurements by others on single-walled carbon nanotubes. Integration of nanotubes...

  6. Reactor scale modeling of multi-walled carbon nanotube growth

    International Nuclear Information System (INIS)

    Lombardo, Jeffrey J.; Chiu, Wilson K.S.

    2011-01-01

    As the mechanisms of carbon nanotube (CNT) growth becomes known, it becomes important to understand how to implement this knowledge into reactor scale models to optimize CNT growth. In past work, we have reported fundamental mechanisms and competing deposition regimes that dictate single wall carbon nanotube growth. In this study, we will further explore the growth of carbon nanotubes with multiple walls. A tube flow chemical vapor deposition reactor is simulated using the commercial software package COMSOL, and considered the growth of single- and multi-walled carbon nanotubes. It was found that the limiting reaction processes for multi-walled carbon nanotubes change at different temperatures than the single walled carbon nanotubes and it was shown that the reactions directly governing CNT growth are a limiting process over certain parameters. This work shows that the optimum conditions for CNT growth are dependent on temperature, chemical concentration, and the number of nanotube walls. Optimal reactor conditions have been identified as defined by (1) a critical inlet methane concentration that results in hydrogen abstraction limited versus hydrocarbon adsorption limited reaction kinetic regime, and (2) activation energy of reaction for a given reactor temperature and inlet methane concentration. Successful optimization of a CNT growth processes requires taking all of those variables into account.

  7. Heat Dissipation for Microprocessor Using Multiwalled Carbon Nanotubes Based Liquid

    OpenAIRE

    Hung Thang, Bui; Trinh, Pham Van; Chuc, Nguyen Van; Khoi, Phan Hong; Minh, Phan Ngoc

    2013-01-01

    Carbon nanotubes (CNTs) are one of the most valuable materials with high thermal conductivity (2000 W/m · K compared with thermal conductivity of Ag 419 W/m · K). This suggested an approach in applying the CNTs in thermal dissipation system for high power electronic devices, such as computer processor and high brightness light emitting diode (HB-LED). In this work, multiwalled carbon nanotubes (MWCNTs) based liquid was made by COOH functionalized MWCNTs dispersed in distilled water with conce...

  8. Electrical conductivity of compacts of graphene, multi-wall carbon nanotubes, carbon black, and graphite powder

    NARCIS (Netherlands)

    Marinho, B.; Gomes Ghislandi, M.; Tkalya, E.; Koning, C.E.; With, de G.

    2012-01-01

    The electrical conductivity of different carbon materials (multi-walled carbon nanotubes, graphene, carbon black and graphite), widely used as fillers in polymeric matrices, was studied using compacts produced by a paper preparation process and by powder compression. Powder pressing assays show that

  9. The effect of different order of purification treatments on the purity of multiwalled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Ling, Xinlong [College of Materials Science and Engineering, State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, Donghua University, 2999 North People Road, Shanghai 201620 (China); Department of Biological and Chemical Engineering, Guangxi University of Technology, 268 Donghuan Road, Liuzhou 545006 (China); Wei, Yizhe [College of Materials Science and Engineering, State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, Donghua University, 2999 North People Road, Shanghai 201620 (China); Zou, Liming, E-mail: lmzou@dhu.edu.cn [College of Materials Science and Engineering, State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, Donghua University, 2999 North People Road, Shanghai 201620 (China); Xu, Su [College of Materials Science and Engineering, State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, Donghua University, 2999 North People Road, Shanghai 201620 (China)

    2013-07-01

    The multiwalled carbon nanotubes were purified with different order treatments of gas phase and liquid phase. Amorphous carbon and iron catalysts were removed and some oxygen-containing groups were attached to the surface of multiwalled carbon nanotubes after purification. The multiwalled carbon nanotubes were determined and characterized by thermogravimetric analysis, Fourier transform infrared spectroscopy, Raman spectroscopy, X-ray photoelectron spectroscopy, Boehm's neutralizing titration method and weighing method. The morphology of multiwalled carbon nanotubes was verified using scanning electron microscopy and transmission electron microscopy. The results indicated amorphous carbon and iron catalysts were removed completely while the structure of multiwalled carbon nanotubes was slightly destructed by two treatment methods. Three principal oxygen-containing groups on the surface of multiwalled carbon nanotubes were carboxyl, lactone and phenolic hydroxyl in descending order of their concentrations. The method I including gas phase treatment firstly and then liquid phase treatment, is more effective to purify multiwalled carbon nanotubes and to protect the structure of multiwalled carbon nanotubes than method II including liquid phase treatment firstly and then gas phase treatment.

  10. Nanoscratch technique for aligning multiwalled carbon nanotubes ...

    Indian Academy of Sciences (India)

    Carbon nanotube; arc discharge; characterization; alignment; nanoscratch. 1. Introduction ... During arc discharge, when the gap between the electrodes is ∼ 1 mm, ..... increase in the D band intensity in the aligned region may not be possibly ...

  11. Electronic structure of multi-walled carbon fullerenes

    International Nuclear Information System (INIS)

    Doore, Keith; Cook, Matthew; Clausen, Eric; Lukashev, Pavel V; Kidd, Tim E; Stollenwerk, Andrew J

    2017-01-01

    Despite an enormous amount of research on carbon based nanostructures, relatively little is known about the electronic structure of multi-walled carbon fullerenes, also known as carbon onions. In part, this is due to the very high computational expense involved in estimating electronic structure of large molecules. At the same time, experimentally, the exact crystal structure of the carbon onion is usually unknown, and therefore one relies on qualitative arguments only. In this work we present the results of a computational study on a series of multi-walled fullerenes and compare their electronic structures to experimental data. Experimentally, the carbon onions were fabricated using ultrasonic agitation of isopropanol alcohol and deposited onto the surface of highly ordered pyrolytic graphite using a drop cast method. Scanning tunneling microscopy images indicate that the carbon onions produced using this technique are ellipsoidal with dimensions on the order of 10 nm. The majority of differential tunneling spectra acquired on individual carbon onions are similar to that of graphite with the addition of molecular-like peaks, indicating that these particles span the transition between molecules and bulk crystals. A smaller, yet sizable number exhibited a semiconducting gap between the highest occupied molecular orbital (HOMO) and the lowest unoccupied molecular orbital (LUMO) levels. These results are compared with the electronic structure of different carbon onion configurations calculated using first-principles. Similar to the experimental results, the majority of these configurations are metallic with a minority behaving as semiconductors. Analysis of the configurations investigated here reveals that each carbon onion exhibiting an energy band gap consisted only of non-metallic fullerene layers, indicating that the interlayer interaction is not significant enough to affect the total density of states in these structures. (paper)

  12. Respiratory toxicity of multi-wall carbon nanotubes

    International Nuclear Information System (INIS)

    Muller, Julie; Huaux, Francois; Moreau, Nicolas; Misson, Pierre; Heilier, Jean-Francois; Delos, Monique; Arras, Mohammed; Fonseca, Antonio; Nagy, Janos B.; Lison, Dominique

    2005-01-01

    Carbon nanotubes focus the attention of many scientists because of their huge potential of industrial applications, but there is a paucity of information on the toxicological properties of this material. The aim of this experimental study was to characterize the biological reactivity of purified multi-wall carbon nanotubes in the rat lung and in vitro. Multi-wall carbon nanotubes (CNT) or ground CNT were administered intratracheally (0.5, 2 or 5 mg) to Sprague-Dawley rats and we estimated lung persistence, inflammation and fibrosis biochemically and histologically. CNT and ground CNT were still present in the lung after 60 days (80% and 40% of the lowest dose) and both induced inflammatory and fibrotic reactions. At 2 months, pulmonary lesions induced by CNT were characterized by the formation of collagen-rich granulomas protruding in the bronchial lumen, in association with alveolitis in the surrounding tissues. These lesions were caused by the accumulation of large CNT agglomerates in the airways. Ground CNT were better dispersed in the lung parenchyma and also induced inflammatory and fibrotic responses. Both CNT and ground CNT stimulated the production of TNF-α in the lung of treated animals. In vitro, ground CNT induced the overproduction of TNF-α by macrophages. These results suggest that carbon nanotubes are potentially toxic to humans and that strict industrial hygiene measures should to be taken to limit exposure during their manipulation

  13. Activity and stability studies of platinized multi-walled carbon nanotubes as fuel cell electrocatalysts

    DEFF Research Database (Denmark)

    Stamatin, Serban Nicolae; Borghei, Maryam; Dhiman, Rajnish

    2015-01-01

    A non-covalent functionalization for multi-walled carbon nanotubes has been used as an alternative to the damaging acid treatment. Platinum nanoparticles with similar particle size distribution have been deposited on the surface modified multi-walled carbon nanotubes. The interaction between...

  14. Toxicological effects of multi-wall carbon nanotubes in rats

    International Nuclear Information System (INIS)

    Liu Aihong; Sun Kangning; Yang, Jiafeng; Zhao Dongmei

    2008-01-01

    The aim of this study was to evaluate the lung toxicity of multi-wall carbon nanotubes (MWCNTs). The present work exposed MWCNTs into the rats in intratracheal instillation administration modes. We systematically studied the distribution of nanoparticles in vivo, target organs and time-effects of nanotoxicity, dose-effects of nanotoxicity, etc. These results indicate that under the conditions of this test, pulmonary exposures to MWCNTs in rats by intratracheal instillation produced a series of multiple lesions in a dose-dependent and time-dependent manner, evidence of a foreign tissue body reaction.

  15. Toxicological effects of multi-wall carbon nanotubes in rats

    Energy Technology Data Exchange (ETDEWEB)

    Liu Aihong; Sun Kangning, E-mail: Sunkangning@sdu.edu.cn; Yang, Jiafeng [Engineering Ceramics Key Laboratory of Shandong Province, Material Science and Engineering Institute, Shandong University, Key Laboratory of Liquid Structure and Heredity of Materials ministry of Education (China); Zhao Dongmei [The Second Hospital of Shandong University (China)

    2008-12-15

    The aim of this study was to evaluate the lung toxicity of multi-wall carbon nanotubes (MWCNTs). The present work exposed MWCNTs into the rats in intratracheal instillation administration modes. We systematically studied the distribution of nanoparticles in vivo, target organs and time-effects of nanotoxicity, dose-effects of nanotoxicity, etc. These results indicate that under the conditions of this test, pulmonary exposures to MWCNTs in rats by intratracheal instillation produced a series of multiple lesions in a dose-dependent and time-dependent manner, evidence of a foreign tissue body reaction.

  16. Multiwalled Carbon Nanotubes Decorated with Cobalt Oxide Nanoparticles

    Directory of Open Access Journals (Sweden)

    D. G. Larrude

    2012-01-01

    Full Text Available Multiwalled carbon nanotubes (MWCNTs synthesized by spray pyrolysis were decorated with cobalt oxide nanoparticles using a simple synthesis route. This wet chemistry method yielded nanoparticles randomly anchored to the surface of the nanotubes by decomposition of cobalt nitrate hexahydrate diluted in acetone. Electron microscopy analysis indicated that dispersed particles were formed on the MWCNTs walls. The average size increased with the increasing concentration of cobalt nitrate in acetone in the precursor mixture. TEM images indicated that nanoparticles were strongly attached to the tube walls. The Raman spectroscopy results suggested that the MWCNT structure was slightly damaged after the nanoparticle growth.

  17. Nano-QSAR: Genotoxicity of Multi-Walled Carbon Nanotubes

    International Nuclear Information System (INIS)

    Toropova, A. P.; Toropov, A. A.; Rallo, R.; Leszczynska, D.; Leszczynski, J.

    2016-01-01

    The study was carried out to develop an efficient approach for prediction the genotoxicity of carbon nano tubes. The experimental data on the bacterial reverse mutation test (TA100) on multi-walled carbon nano tubes was collected from the literature and examined as an endpoint. By means of the optimal descriptors calculated with the Monte Carlo method a mathematical model of the endpoint was built up. The model is represented by a function of: (i) dose (μg/plate); (ii) metabolic activation (i.e. with S9 mix or without S9 mix); and (iii) two types of multi-walled carbon nano tubes. The above listed conditions were represented by so-called quasi-SMILES. Simplified molecular input-line entry system (SMILES) is a tool for representation of molecular structure. The quasi-SMILES is a tool to represent physicochemical and / or biochemical conditions for building up a predictive model. Thus, instead of well-known paradigm of predictive modeling “endpoint is a mathematical function of molecular structure” a fresh paradigm “endpoint is a mathematical function of available eclectic data (conditions) is suggested.

  18. Hot wire production of single-wall and multi-wall carbon nanotubes

    Science.gov (United States)

    Dillon, Anne C.; Mahan, Archie H.; Alleman, Jeffrey L.

    2010-10-26

    Apparatus (210) for producing a multi-wall carbon nanotube (213) may comprise a process chamber (216), a furnace (217) operatively associated with the process chamber (216), and at least one filament (218) positioned within the process chamber (216). At least one power supply (220) operatively associated with the at least one filament (218) heats the at least one filament (218) to a process temperature. A gaseous carbon precursor material (214) operatively associated with the process chamber (216) provides carbon for forming the multi-wall carbon nanotube (213). A metal catalyst material (224) operatively associated with the process (216) catalyzes the formation of the multi-wall carbon nanotube (213).

  19. Improvements of electrocatalytic activity of PtRu nanoparticles on multi-walled carbon nanotubes by a H2 plasma treatment in methanol and formic acid oxidation

    International Nuclear Information System (INIS)

    Jiang Zhongqing; Jiang Zhongjie

    2011-01-01

    Graphical abstract: A H 2 plasma, that aims at reducing the fraction of the oxidized species at the outermost perimeter of metal particles, has been used to treat the PtRu nanoparticles supported on the plasma functionalized multi-walled carbon nanotubes (PtRu/PS-MWCNTs). The plasma treated PtRu/PS-MWCNTs exhibit increased electrochemically active surface area, reduced charge transfer resistance, improved electrocatalytic activity and long term stability toward methanol and formic acid oxidation, and enhanced tolerance to carbonaceous species relative to the sample untreated with the H 2 plasma. Highlights: → A H 2 plasma technique is used to treat the PtRu nanoparticles. → The H 2 plasma treated PtRu/PS-MWCNTs exhibit improved electrocatalytic activity. → The H 2 plasma treated PtRu/PS-MWCNTs have significantly reduced charge transfer resistance. → The H 2 plasma treated PtRu/PS-MWCNTs show the increased stability. → The Pt:Ru atomic ratio of PtRu nanoparticles has a significant effect on the electrochemical activity. - Abstract: A H 2 plasma has been used to treat the PtRu nanoparticles supported on the plasma functionalized multi-walled carbon nanotubes (PtRu/PS-MWCNTs). The plasma treatment does not change the size and crystalline structure of PtRu nanoparticles, but reduces the fraction of the oxidized species at the outermost perimeter of particles. The electrochemical results show that these plasma treated PtRu/PS-MWCNTs exhibit increased electrochemically active surface area, improved electrocatalytic activity and long term stability toward methanol and formic acid oxidation, and enhanced tolerance to carbonaceous species relative to the sample untreated with the H 2 plasma. The electrocatalytic activities of the plasma treated PtRu/PS-MWCNTs are found to be dependent upon the Pt:Ru atomic ratios of PtRu nanoparticles. The catalysts with a Pt:Ru atomic ratio close to 1:1 show superior properties in the electrooxidation of methanol and formic acid

  20. (PC12) cell lines to oxidized multi-walled carbon nanotubes

    African Journals Online (AJOL)

    EB

    Methods: The pristine multi-walled carbon nanotubes (p-MWCNTs) were ... characterize the MWCNTs. ..... South Africa and NRF Focus Area, Nanotechnology ... of carbon nanotubes in drug delivery. Current. Opinion in Chemical Biology, 2005 ...

  1. Lithium storage properties of multiwall carbon nanotubes prepared by CVD

    International Nuclear Information System (INIS)

    Ahn, J.-O.; Andong National University,; Wang, G.X.; Liu, H.K.; Dou, S.X.

    2003-01-01

    Full text: Multiwall carbon nanotubes (MWCNTs) were synthesised by chemical vapour deposition (CVD) method using acetylene gas. The XRD pattern of as prepared carbon nanotubes showed that the d 002 value is 3.44 Angstroms. The morphology and microstructure of carbon nanotubes were characterized by HRTEM. Most of carbon nanotubes are entangled together to form bundles or ropes. The diameter of the carbon nanotubes is in the range of 10 ∼ 20 nm. There is a small amount of amorphous carbon particles presented in the sample. However, the yield of carbon nanotubes is more than 95%. Electrochemical properties of carbon nanotubes were characterised via a variety of electrochemical testing techniques. The result of CV test showed that the Li insertion potential is quite low, which is very close to O V versus Li + /Li reference electrode, whereas the potential for Li de-intercalation is in the range of 0.2-0.4 V. There exists a slight voltage hysteresis between Li intercalation and Li de-intercalation, which is similar to the other carbonaceous materials. The intensity of redox peaks of carbon nanotubes decrease with scanning cycle, indicating that the reversible Li insertion capacity gradually decreases. The carbon nanotubes electrode demonstrated a reversible lithium storage capacity of 340 mAh/g with good cyclability at moderate current density. Further improvement of Li storage capacity is possible by opening the end of carbon nanotubes to allow lithium insertion into inner graphene sheet of carbon nanotubes. The kinetic properties of lithium insertion in carbon nanotube electrodes were characterised by a.c. impedance measurements. It was found that the lithium diffusion coefficient d Li decreases with an increase of Li ion concentration in carbon nanotube host

  2. Drilling Fluids Using Multiwall Carbon Nanotube (MWCNT

    Directory of Open Access Journals (Sweden)

    Mostafa Sedaghatzadeh

    2012-11-01

    Full Text Available Designing drilling fluids for drilling in deep gas reservoirs and geothermal wells is a major challenge. Cooling drilling fluids and preparing stable mud with high thermal conductivity are of great concern. Drilling nanofluids, i.e. a low fraction of carbon nanotube (CNT well dispersed in mud, may enhance the mixture thermal conductivity compared to the base fluids. Thus, they are potentially useful for advanced designing high temperature and high pressure (HTHP drilling fluids. In the present study, the impacts of CNT volume fraction, ball milling time, functionalization, temperature, and dispersion quality (by means of scanning electron microscopy, SEM on the thermal and rheological properties of water-based mud are experimentally investigated. The thermal conductivities of the nano-based drilling fluid are measured with a transient hot wire method. The experimental results show that the thermal conductivity of the water-based drilling fluid is enhanced by 23.2% in the presence of 1 vol% functionalized CNT at room temperature; it increases by 31.8% by raising the mud temperature to 50 °C. Furthermore, significant improvements are seen in the rheological properties—such as yield point, filtration properties, and annular viscosity—of the CNTmodified drilling fluid compared to the base mud, which pushes forward their future development.

  3. Intershell resistance in multiwall carbon nanotubes: A Coulomb drag study

    DEFF Research Database (Denmark)

    Lunde, Anders Mathias; Flensborg, Karsten; Jauho, Antti-Pekka

    2005-01-01

    We calculate the intershell resistance R-21 in a multiwall carbon nanotube as a function of temperature T and Fermi level epsilon(F) (e.g., a gate voltage), varying the chirality of the inner and outer tubes. This is done in a so-called Coulomb drag setup, where a current I-1 in one shell induces...... a voltage drop V-2 in another shell by the screened Coulomb interaction between the shells neglecting the intershell tunneling. We provide benchmark results for R-21 = V2/I-1 within the Fermi liquid theory using Boltzmann equations. The band structure gives rise to strongly chirality-dependent suppression...... effects for the Coulomb drag between different tubes due to selection rules combined with mismatching of wave vector and crystal angular momentum conservation near the Fermi level. This gives rise to orders of magnitude changes in R-21 and even the sign of R-21 can change depending on the chirality...

  4. Control of growth mode of multiwalled carbon nanotubes

    International Nuclear Information System (INIS)

    Nguyen Hong Quang; Kim, Do-Hyung

    2009-01-01

    We have conducted an experimental study to investigate the synthesis of multi-walled carbon nanotubes (CNTs) by a dc plasma-enhanced chemical vapour deposition (PECVD) technique. The synthesis of base and tip-type of CNTs was selectively controlled by changing the catalyst size, catalyst film thickness correlated with altering the NH 3 pretreatment plasma current. These types of CNT showed distinctive properties in nanotube structure, growth rate and vertical alignment, which were confirmed by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and in situ optical interference measurement. The vertically aligned behaviour of CNT was systematically studied by using a fine-patterned catalyst layer with diverse critical dimensions. Freestanding single CNT was successfully realized by optimum tip-type CNT growth, conventional photolithography and wet-etch process.

  5. Electric current distribution of a multiwall carbon nanotube

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Li-Ying; Chang, Chia-Seng, E-mail: jasonc@phys.sinica.edu.tw [Department of Physics, National Taiwan University, Taipei 10617, Taiwan (China); Institute of Physics, Academia Sinica, Taipei 11529, Taiwan (China); Nano Science and Technology Program, Taiwan International Graduate Program, Academia Sinica and National Taiwan University, Taiwan (China); Chen, Yu-Jyun [Institute of Physics, Academia Sinica, Taipei 11529, Taiwan (China)

    2016-07-15

    The electric current distribution in a multiwall carbon nanotube (MWCNT) was studied by in situ measuring the electric potential along an individual MWCNT in the ultra-high vacuum transmission electron microscope (TEM). The current induced voltage drop along each section of a side-bonded MWCNT was measured by a potentiometric probe in TEM. We have quantitatively derived that the current on the outermost shell depends on the applied current and the shell diameter. More proportion of the total electronic carriers hop into the inner shells when the applied current is increased. The larger a MWCNT’s diameter is, the easier the electronic carriers can hop into the inner shells. We observed that, for an 8 nm MWCNT with 10 μA current applied, 99% of the total current was distributed on the outer two shells.

  6. Preparation and characterization of polycarbonate/multiwalled carbon nanotube nanocomposites

    Directory of Open Access Journals (Sweden)

    Claudio Larosa

    2017-09-01

    Full Text Available A polymer nanocomposite was produced by ultrasonic-assisted dispersion of multiwalled carbon nanotubes (MWCNTs in a polycarbonate matrix using p-xylene and dichloromethane as the solvents. The filler loading was varied from 1 to 3 wt % in order to examine the effect of MWCNTs on the structure and properties of the composites. The nanocomposites were characterized by DSC, DTA, TGA, UV–vis, FTIR and Raman spectroscopy to evaluate the changes induced by the filler in the polymer matrix. UV–vis, FTIR and Raman spectroscopy measurements confirmed the presence of the dispersed phase in the composite films, while TGA and DSC analysis of the nanocomposites revealed enhanced thermal stability and decreased crystallinity, respectively, as compared to the neat polymer. The proposed composites can find application in a number of everyday products where polycarbonate is the base polymer.

  7. Preparation polystyrene/multiwalled carbon nanotubes nanocomposites by copolymerization of styrene and styryl-functionalized multiwalled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Hua, Jing, E-mail: huajing72@qust.edu.cn [Key Laboratory of Rubber-Plastics Ministry of Education, Qingdao University of Science and Technology, Qingdao (China); Wang, Zhongguang; Xu, Ling; Wang, Xin; Zhao, Jian; Li, Feifei [Key Laboratory of Rubber-Plastics Ministry of Education, Qingdao University of Science and Technology, Qingdao (China)

    2013-01-15

    Styryl-functionalized multiwalled carbon nanotubes (p-MWNTs) were prepared by esterification based on the carboxylate salt of carbon nanotubes and p-chloromethylstyrene in toluene. Then in situ radical copolymerization of p-MWNTs and styrene initiated by 2,2 Prime -azobis(isobutyronitrile) (AIBN) was applied to synthesize composites of styryl-functionalized multiwalled carbon nanotubes and polystyrene (PS) (p-MWNTs/PS). Characterizations carried out by FT-IR, {sup 1}H NMR, UV-vis show that styryl group covalently bond to the surface of MWNTs. The results of UV showed that the solutions of p-MWNTs/PS in chloroform have the hyperchromic effect. Transmission electron microscopy (TEM) images of p-MWNTs/PS composites and scanning electron microscopy (SEM) images of fracture surface of p-MWNTs/PS composites showed the functionalized nanotubes had a better dispersion than that of the unfunctionalized MWNTs in the matrix. The results of thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) suggested that the thermal stability of p-MWNTs/PS composites improved in the presence of MWNTs. -- Highlights: Black-Right-Pointing-Pointer A facile and simple way to successfully prepare the polystyrene/MWNTs nanocomposites. Black-Right-Pointing-Pointer Characterizations show that styryl group covalently bond to the surface of MWNTs. Black-Right-Pointing-Pointer The solutions of p-MWNTs/PS in chloroform have the hyperchromic effect. Black-Right-Pointing-Pointer Thermal stability of p-tpas composites improved in the presence of MWNTs. Black-Right-Pointing-Pointer The performance of polymer prepared by this method have great potential for exploitation.

  8. Evaluation of multiwalled carbon nanotubes toxicity in two fish species.

    Science.gov (United States)

    Cimbaluk, Giovani Valentin; Ramsdorf, Wanessa Algarte; Perussolo, Maiara Carolina; Santos, Hayanna Karla Felipe; Da Silva De Assis, Helena Cristina; Schnitzler, Mariane Cristina; Schnitzler, Danielle Caroline; Carneiro, Pedro Gontijo; Cestari, Marta Margarete

    2018-04-15

    Carbon Nanotubes are among the most promising materials for the technology industry. Their unique physical and chemical proprieties may reduce the production costs and improve the efficiency of a large range of products. However, the same characteristics that have made nanomaterials interesting for industry may be responsible for inducing toxic effects on the aquatic organisms. Since the carbon nanotubes toxicity is still a controversial issue, we performed tests of acute and subchronic exposure to a commercial sample of multiwalled carbon nanotubes in two fish species, an exotic model (Danio rerio) and a native one (Astyanax altiparanae). Using the alkaline version of the comet assay on erythrocytes and the piscine micronucleous, also performed on erythrocytes, it was verified that the tested carbon nanotubes sample did not generate apparent genotoxicity by means of single/double DNA strand break or clastogenic/aneugenic effects over any of the species, independently of the exposure period. Although, our findings indicate the possibility of the occurrence of CNTs-DNA crosslinks. Apparently, the sample tested induces oxidative stress after subchronic exposure as shown by activity of superoxide dismutase and catalase. The data obtained by the activity levels of acetylcholinesterase suggests acute neurotoxicity in Astyanax altiparanae and subchronic neurotoxicity in Danio rerio. Copyright © 2017 Elsevier Inc. All rights reserved.

  9. Synthesis of multiwalled carbon nanotube from different grades of carbon black using arc discharge method

    Energy Technology Data Exchange (ETDEWEB)

    Arora, Neha, E-mail: n4neha31@gmail.com [Department of Mechanical Engineering, Birla Institute of Technology and Science, Pilani (India); Sharma, N. N. [Department of Mechanical Engineering, Birla Institute of Technology and Science, Pilani (India); Director, School of Automobile, Mechanical & Mechatronics, Manipal University,Jaipur,India (India)

    2016-04-13

    This paper describes the synthesis of nanotube from different grades (Tread * A(non-ASTM), N134,N121,N660 and N330)of carbon black using DC arc discharge method at 40A current for 60sec. Carbon black samples of different grades were procured from industry (Aditya Birla Science and Technology Limited, India). Scanning Electron Micrographs (SEM) of the deposited carbon nanostructures suggests that MWCNTs are formed at 40A and for a minimal exposure time of 60sec.The result formed indicates the N330 grade of carbon black gets converted to MWCNTs (Multiwall Carbon nanotube) as compared to other grades.

  10. Multi-wall carbon nanotubes with nitrogen-containing carbon coating

    Czech Academy of Sciences Publication Activity Database

    Tomšík, Elena; Morávková, Zuzana; Stejskal, Jaroslav; Trchová, Miroslava; Šálek, Petr; Kovářová, Jana; Zemek, Josef; Cieslar, M.; Prokeš, J.

    2013-01-01

    Roč. 67, č. 8 (2013), s. 1054-1065 ISSN 0366-6352 R&D Projects: GA ČR GPP108/11/P763; GA ČR GAP205/12/0911; GA ČR GA202/09/0428 Institutional support: RVO:61389013 ; RVO:68378271 Keywords : polyaniline coating * carbon ization * multi-wall carbon nanotubes Subject RIV: CD - Macromolecular Chemistry; BM - Solid Matter Physics ; Magnetism (FZU-D) Impact factor: 1.193, year: 2013

  11. Exchange of Surfactant by Natural Organic Matter on the Surfaces of Multi-Walled Carbon Nanotubes

    Science.gov (United States)

    The increasing production and applications of multi-walled carbon nanotubes (MWCNTs) have elicited concerns regarding their release and potential adverse effects in the environment. To form stable aqueous MWCNTs suspensions, surfactants are often employed to facilitate dispersion...

  12. Optical Study of Liquid Crystal Doped with Multiwalled Carbon Nanotube

    Science.gov (United States)

    Gharde, Rita A.; Thakare, Sangeeta Y.

    2014-11-01

    Liquid crystalline materials have been useful for display devices i.e watches, calculators, automobile dashboards, televisions, multi media projectors etc. as well as in electro tunable lasers, optical fibers and lenses. Carbon nanotube is chosen as the main experimental factor in this study as it has been observed that Carbon Nano Tube influence the existing properties of liquid crystal host and with the doping of CNT can enhance1 the properties of LC. The combination of carbon nanotube (CNT) and liquid crystal (LC) materials show considerable interest in the scientific community due to unique physical properties of CNT in liquid crystal. Dispersion of CNTs in LCs can provide us a cheap, simple, versatile and effective means of controlling nanotube orientation on macroscopic scale with no restrictions on nanotube type. LCs have the long range orientational order rendering them to be anisotropic phases. If CNTs can be well dispersed in LC matrix, they will align with their long axes along the LC director to minimize distortions of the LC director field and the free energy. In this paper, we doped liquid crystal (Cholesteryl Nonanoate) by a small amount of multiwall carbon nanotube 0.05% and 0.1% wt. We found that by adding carbon nanotube to liquid crystals the melting point of the mixture is decreased but TNI is increased. It has been also observed that with incereas in concentration of carbon nanotube into liquid crystal shows conciderable effect on LC. The prepared samples were characterized using various techniques to study structural, thermal and optical properties i.e PMS, FPSS, UV-Vis spectroscopy, FT-IR measurements, and DTA.

  13. Photothermal therapy of melanoma tumor using multiwalled carbon nanotubes.

    Science.gov (United States)

    Sobhani, Zahra; Behnam, Mohammad Ali; Emami, Farzin; Dehghanian, Amirreza; Jamhiri, Iman

    2017-01-01

    Photothermal therapy (PTT) is a therapeutic method in which photon energy is transformed into heat rapidly via different operations to extirpate cancer. Nanoparticles, such as carbon nanotubes (CNTs) have exceptional optical absorbance in visible and near infrared spectra. Therefore, they could be a good converter to induce hyperthermia in PTT technique. In our study, for improving the dispersibility of multiwalled CNTs in water, the CNTs were oxidized (O-CNTs) and then polyethylene glycol (PEG) was used for wrapping the surface of nanotubes. The formation of a thin layer of PEG around the nanotubes was confirmed through Fourier transform infrared, thermogravimetric analysis, and field emission scanning electron microscopy techniques. Results of thermogravimetric analysis showed that the amount of PEG component in the O-CNT-PEG was approximately 80% (w/w). Cell cytotoxicity study showed that O-CNT was less cytotoxic than pristine multiwalled nanotubes, and O-CNT-PEG had the lowest toxicity against HeLa and HepG2 cell lines. The effect of O-CNT-PEG in reduction of melanoma tumor size after PTT was evaluated. Cancerous mice were exposed to a continuous-wave near infrared laser diode (λ=808 nm, P =2 W and I =8 W/cm 2 ) for 10 minutes once in the period of the treatment. The average size of tumor in mice receiving O-CNT-PEG decreased sharply in comparison with those that received laser therapy alone. Results of animal studies indicate that O-CNT-PEG is a powerful candidate for eradicating solid tumors in PTT technique.

  14. Turning refuse plastic into multi-walled carbon nanotube forest

    Science.gov (United States)

    Oh, Eugene; Lee, Jaegeun; Jung, Seung-Ho; Cho, Seungho; Kim, Hye-Jin; Lee, Sung-Hyun; Lee, Kun-Hong; Song, Kyong-Hwa; Choi, Chi-Hoon; Han, Do Suck

    2012-01-01

    A novel and effective method was devised for synthesizing a vertically aligned carbon nanotube (CNT) forest on a substrate using waste plastic obtained from commercially available water bottles. The advantages of the proposed method are the speed of processing and the use of waste as a raw material. A mechanism for the CNT growth was also proposed. The growth rate of the CNT forest was ∼2.5 μm min−1. Transmission electron microscopy images indicated that the outer diameters of the CNTs were 20–30 nm on average. The intensity ratio of the G and D Raman bands was 1.27 for the vertically aligned CNT forest. The Raman spectrum showed that the wall graphitization of the CNTs, synthesized via the proposed method was slightly higher than that of commercially available multi-walled carbon nanotubes (MWCNTs). We expect that the proposed method can be easily adapted to the disposal of other refuse materials and applied to MWCNT production industries. PMID:27877482

  15. Turning refuse plastic into multi-walled carbon nanotube forest

    Directory of Open Access Journals (Sweden)

    Eugene Oh, Jaegeun Lee, Seung-Ho Jung, Seungho Cho, Hye-Jin Kim, Sung-Hyun Lee, Kun-Hong Lee, Kyong-Hwa Song, Chi-Hoon Choi and Do Suck Han

    2012-01-01

    Full Text Available A novel and effective method was devised for synthesizing a vertically aligned carbon nanotube (CNT forest on a substrate using waste plastic obtained from commercially available water bottles. The advantages of the proposed method are the speed of processing and the use of waste as a raw material. A mechanism for the CNT growth was also proposed. The growth rate of the CNT forest was ~2.5 μm min−1. Transmission electron microscopy images indicated that the outer diameters of the CNTs were 20–30 nm on average. The intensity ratio of the G and D Raman bands was 1.27 for the vertically aligned CNT forest. The Raman spectrum showed that the wall graphitization of the CNTs, synthesized via the proposed method was slightly higher than that of commercially available multi-walled carbon nanotubes (MWCNTs. We expect that the proposed method can be easily adapted to the disposal of other refuse materials and applied to MWCNT production industries.

  16. Effect of multiwalled carbon nanotubes on UASB microbial consortium.

    Science.gov (United States)

    Yadav, Tushar; Mungray, Alka A; Mungray, Arvind K

    2016-03-01

    The continuous rise in production and applications of carbon nanotubes (CNTs) has grown a concern about their fate and toxicity in the environment. After use, these nanomaterials pass through sewage and accumulate in wastewater treatment plants. Since, such plants rely on biological degradation of wastes; their activity may decrease due to the presence of CNTs. This study investigated the effect of multiwalled carbon nanotubes (MWCNTs) on upflow anaerobic sludge blanket (UASB) microbial activity. The toxic effect on microbial viability, extracellular polymeric substances (EPS), volatile fatty acids (VFA), and biogas generation was determined. The reduction in a colony-forming unit (CFU) was 29 and 58 % in 1 and 100 mg/L test samples, respectively, as compared to control. The volatile fatty acids and biogas production was also found reduced. The scanning electron microscopy (SEM) and fluorescent microscopy images confirmed that the MWCNT mediated microbial cell damage. This damage caused the increase in EPS carbohydrate, protein, and DNA concentration. Fourier transform infrared (FTIR) spectroscopy results supported the alterations in sludge EPS due to MWCNT. Our observations offer a new insight to understand the nanotoxic effect of MWCNTs on UASB microflora in a complex environment system.

  17. Heat Dissipation for Microprocessor Using Multiwalled Carbon Nanotubes Based Liquid

    Science.gov (United States)

    Trinh, Pham Van; Chuc, Nguyen Van; Khoi, Phan Hong; Minh, Phan Ngoc

    2013-01-01

    Carbon nanotubes (CNTs) are one of the most valuable materials with high thermal conductivity (2000 W/m · K compared with thermal conductivity of Ag 419 W/m · K). This suggested an approach in applying the CNTs in thermal dissipation system for high power electronic devices, such as computer processor and high brightness light emitting diode (HB-LED). In this work, multiwalled carbon nanotubes (MWCNTs) based liquid was made by COOH functionalized MWCNTs dispersed in distilled water with concentration in the range between 0.2 and 1.2 gram/liter. MWCNT based liquid was used in liquid cooling system to enhance thermal dissipation for computer processor. By using distilled water in liquid cooling system, CPU's temperature decreases by about 10°C compared with using fan cooling system. By using MWCNT liquid with concentration of 1 gram/liter MWCNTs, the CPU's temperature decreases by 7°C compared with using distilled water in cooling system. Theoretically, we also showed that the presence of MWCNTs reduced thermal resistance and increased the thermal conductivity of liquid cooling system. The results have confirmed the advantages of the MWCNTs for thermal dissipation systems for the μ-processor and other high power electronic devices. PMID:24453829

  18. Sorption of Heterocyclic Organic Compounds to Multiwalled Carbon Nanotubes.

    Science.gov (United States)

    Metzelder, Florian; Funck, Matin; Schmidt, Torsten C

    2018-01-16

    Sorption is an important natural and technical process. Sorption coefficients are typically determined in batch experiments, but this may be challenging for weakly sorbing compounds. An alternative method enabling analysis of those compounds is column chromatography. A column packed with the sorbent is used and sorption data are determined by relating sorbate retention to that of a nonretarded tracer. In this study, column chromatography was applied for the first time to study sorption of previously hardly investigated heterocyclic organic compounds to multiwalled carbon nanotubes (MWCNTs). Sorption data for these compounds are very limited in literature, and weak sorption is expected from predictions. Deuterium oxide was used as nonretarded tracer. Sorption isotherms were well described by the Freundlich model and data showed reasonable agreement with predicted values. Sorption was exothermic and physisorption was observed. H-bonding may contribute to overall sorption, which is supported by reduced sorption with increasing ionic strength due to blocking of functional groups. Lowering pH reduced sorption of ionizable compounds, due to electrostatic repulsion at pH 3 where sorbent as well as sorbates were positively charged. Overall, column chromatography was successfully used to study sorption of heterocyclic compounds to MWCNTs and could be applied for other carbon-based sorbents.

  19. Dispersion of multi-walled carbon nanotubes in biocompatible dispersants

    International Nuclear Information System (INIS)

    Piret, J.-P.; Detriche, S.; Vigneron, R.; Vankoningsloo, S.; Rolin, S.; Mejia Mendoza, J. H.; Masereel, B.; Lucas, S.; Delhalle, J.; Luizi, F.; Saout, C.; Toussaint, O.

    2010-01-01

    Owing to their phenomenal electrical and mechanical properties, carbon nanotubes (CNT) have been an area of intense research since their discovery in 1991. Different applications for these nanoparticles have been proposed, among others, in electronics and optics but also in the medical field. In parallel, emerging studies have suggested potential toxic effects of CNT while others did not, generating some conflicting outcomes. These discrepancies could be, in part, due to different suspension approaches used and to the agglomeration state of CNT in solution. In this study, we described a standardized protocol to obtain stable CNT suspensions, using two biocompatible dispersants (Pluronic F108 and hydroxypropylcellulose) and to estimate the concentration of CNT in solution. CNT appear to be greatly individualized in these two dispersants with no detection of remaining bundles or agglomerates after sonication and centrifugation. Moreover, CNT remained perfectly dispersed when added to culture medium used for in vitro cell experiments. We also showed that Pluronic F108 is a better dispersant than hydroxypropylcellulose. In conclusion, we have developed a standardized protocol using biocompatible surfactants to obtain reproducible and stable multi-walled carbon nanotubes suspensions which can be used for in vitro or in vivo toxicological studies.

  20. Atomic layer deposition of ruthenium on plasma-treated vertically aligned carbon nanotubes for high-performance ultracapacitors.

    Science.gov (United States)

    Kim, Jun Woo; Kim, Byungwoo; Park, Suk Won; Kim, Woong; Shim, Joon Hyung

    2014-10-31

    It is challenging to realize a conformal metal coating by atomic layer deposition (ALD) because of the high surface energy of metals. In this study, ALD of ruthenium (Ru) on vertically aligned carbon nanotubes (CNTs) was carried out. To activate the surface of CNTs that lack surface functional groups essential for ALD, oxygen plasma was applied ex situ before ALD. X-ray photoelectron spectroscopy and Raman spectroscopy confirmed surface activation of CNTs by the plasma pretreatment. Transmission electron microscopy analysis with energy-dispersive x-ray spectroscopy composition mapping showed that ALD Ru grew conformally along CNTs walls. ALD Ru/CNTs were electrochemically oxidized to ruthenium oxide (RuOx) that can be a potentially useful candidate for use in the electrodes of ultracapacitors. Electrode performance of RuOx/CNTs was evaluated using cyclic voltammetry and galvanostatic charge-discharge measurements.

  1. Prospects for using multi-walled carbon nanotubes formed from renewable feedstock in hydrogen energy

    International Nuclear Information System (INIS)

    Onishchenko, D. V.

    2013-01-01

    Mechanoactivation of amorphous carbon synthesized from renewable feedstock promotes formation of multi-walled carbon nanotubes, and the best results were obtained using the feedstock of sphagnum moss. It is shown that the carbon nanotubes formed from different plant feedstock have a high sorption capacity with respect to hydrogen. (author)

  2. Multiwall carbon nanotube Josephson junctions with niobium contacts

    International Nuclear Information System (INIS)

    Pallecchi, Emiliano

    2009-01-01

    The main goal of this thesis is the investigation of dissipationless supercurrent in multiwall carbon nanotubes embedded in a controlled environment. The experimental observation of a dissipationless supercurrent in gated carbon nanotubes remains challenging because of its extreme sensitivity to the environment and to noise fluctuations. We address these issues by choosing niobium as a superconductor and by designing an optimized on chip electromagnetic environment. The environment is meant to reduce the suppression of the supercurrent and allows to disentangle the effects of thermal fluctuations from the intrinsic behavior of the junction. This is crucial for the extraction of the value critical current from the measured data. When the transparency of the contacts is high enough we observed a fully developed supercurrent and we found that it depends on the gate voltage in a resonant manner. In average the critical current increases when the gate is tuned more negative, reflecting the increase of the transparency of the contacts, while the resonant behavior is due to quantum interference effects. We measured the temperature dependence of the switching current and we analyzed the data with an extended RCSJ model that allow to extract the critical current from the experimental data. The measured critical currents are very high with respect to previous reports on gated devices. At positive gate voltage the contacts transparency is lowered and Coulomb blockade is observed. This allows to use Coulomb blockade measurements to further characterize the nanotube and to study the physics of a quantum dot coupled to superconducting leads. The last part of this thesis is dedicated to the measurements of a carbon nanotube Josephson junction in the Coulomb blockade regime. (orig.)

  3. Multiwall carbon nanotubes modulate paraquat toxicity in Arabidopsis thaliana.

    Science.gov (United States)

    Fan, Xiaoji; Xu, Jiahui; Lavoie, Michel; Peijnenburg, W J G M; Zhu, Youchao; Lu, Tao; Fu, Zhengwei; Zhu, Tingheng; Qian, Haifeng

    2018-02-01

    Carbon nanotubes can be either toxic or beneficial to plant growth and can also modulate toxicity of organic contaminants through surface sorption. The complex interacting toxic effects of carbon nanotubes and organic contaminants in plants have received little attention in the literature to date. In this study, the toxicity of multiwall carbon nanotubes (MWCNT, 50 mg/L) and paraquat (MV, 0.82 mg/L), separately or in combination, were evaluated at the physiological and the proteomic level in Arabidopsis thaliana for 7-14 days. The results revealed that the exposure to MWCNT had no inhibitory effect on the growth of shoots and leaves. Rather, MWCNT stimulated the relative electron transport rate and the effective photochemical quantum yield of PSII value as compared to the control by around 12% and lateral root production up to nearly 4-fold as compared to the control. The protective effect of MWCNT on MV toxicity on the root surface area could be quantitatively explained by the extent of MV adsorption on MWCNT and was related to stimulation of photosynthesis, antioxidant protection and number and area of lateral roots which in turn helped nutrient assimilation. The influence of MWCNT and MV on photosynthesis and oxidative stress at the physiological level was consistent with the proteomics analysis, with various over-expressed photosynthesis-related proteins (by more than 2 folds) and various under-expressed oxidative stress related proteins (by about 2-3 folds). This study brings new insights into the interactive effects of two xenobiotics (MWCNT and MV) on the physiology of a model plant. Copyright © 2017 Elsevier Ltd. All rights reserved.

  4. Multiwall carbon nanotube Josephson junctions with niobium contacts

    Energy Technology Data Exchange (ETDEWEB)

    Pallecchi, Emiliano

    2009-02-17

    The main goal of this thesis is the investigation of dissipationless supercurrent in multiwall carbon nanotubes embedded in a controlled environment. The experimental observation of a dissipationless supercurrent in gated carbon nanotubes remains challenging because of its extreme sensitivity to the environment and to noise fluctuations. We address these issues by choosing niobium as a superconductor and by designing an optimized on chip electromagnetic environment. The environment is meant to reduce the suppression of the supercurrent and allows to disentangle the effects of thermal fluctuations from the intrinsic behavior of the junction. This is crucial for the extraction of the value critical current from the measured data. When the transparency of the contacts is high enough we observed a fully developed supercurrent and we found that it depends on the gate voltage in a resonant manner. In average the critical current increases when the gate is tuned more negative, reflecting the increase of the transparency of the contacts, while the resonant behavior is due to quantum interference effects. We measured the temperature dependence of the switching current and we analyzed the data with an extended RCSJ model that allow to extract the critical current from the experimental data. The measured critical currents are very high with respect to previous reports on gated devices. At positive gate voltage the contacts transparency is lowered and Coulomb blockade is observed. This allows to use Coulomb blockade measurements to further characterize the nanotube and to study the physics of a quantum dot coupled to superconducting leads. The last part of this thesis is dedicated to the measurements of a carbon nanotube Josephson junction in the Coulomb blockade regime. (orig.)

  5. Interface interactions in benzophenone doped by multiwalled carbon nanotubes

    Science.gov (United States)

    Lebovka, N. I.; Goncharuk, A.; Melnyk, V. I.; Puchkovska, G. A.

    2009-08-01

    The interface interactions were studied by methods of conductometry, low-temperature phosphorescence and differential scanning calorimetry (DSC) in multiwalled carbon nanotubes (MWCNT) and benzophenone (BP) composite. The concentration of MWCNTs was varied within 0-1 wt%. A percolative threshold was found at MWCNT concentrations exceeding 0.1 wt%. The integration of MWCNTs caused melting temperature increase (≈3 K for 1 wt% of MWCNTs). The effect of positive thermal resistively coefficient, as well as substantial hysteretic behaviour of electrical conductivity σ in a heating-cooling cycle, was observed near the melting point of BP ( T m=321.5 K). The activation-type temperature behaviour of electrical conductivity was observed in the temperature range of supercooled BP. The activation energy was decreasing with increase of MWCNT concentration. The observed nonlinear dependencies of electrical conductivity σ vs. applied voltage U reflect the transport mechanism of the charge carriers through amorphous interface films formed near the surface of the MWCNTs. The thermal shifts of phosphorescence spectra measured within the temperature range 5-200 K evidence existence of such interface films of amorphous BP with width of the order of 0.1 μm.

  6. Magnetoresistance in cobalt-contacted multi-wall carbon nanotubes

    International Nuclear Information System (INIS)

    Vinzelberg, H.; Zhao, B.; Moench, I.; Schumann, J.; Schneider, C.M.

    2005-01-01

    We present results for magnetotransport measurements on multiwall-carbon nanotubes (MWCNT) contacted by cobalt electrodes. By measuring the V(I) characteristics at constant magnetic fields and different orientation of the magnetization directions in the Co electrodes, we were able to determine both current and voltage dependences of the magnetoresistance (MR) effects. These tunneling MR values are compared with the directly measured MR at constant current with sweeping magnetic field. The V(I) curves show an ohmic behavior at 295 K and a non-linear tunneling behavior at 4.2 K. With decreasing bias current the MR increased up to 60% at 4.2 K, and with decreasing bias voltages even up to 175%. The MR disappears at high bias current (voltages) and temperatures higher than 40 K. For most of the samples the current dependences of the MR were found to be nearly symmetric upon reversing the current direction. However, in some cases we also observed a sign change of the MR as function of the applied current, which suggests an inversion of the spin polarization in one of the Co interfaces

  7. Spectroscopic investigations on oxidized multi-walled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Anandhi, C. M. S.; Premkumar, S.; Asath, R. Mohamed; Mathavan, T.; Benial, A. Milton Franklin, E-mail: miltonfranklin@yahoo.com [Department of Physics, N.M.S.S.V.N. College, Madurai-625 019, Tamil Nadu (India)

    2016-05-06

    The pristine multi-walled carbon nanotubes (MWCNTs) were oxidized by the ultrasonication process. The oxidized MWCNTs were characterized by the X-ray diffraction (XRD), ultraviolet–visible (UV-Vis) and Fourier transform -Raman (FT-Raman) spectroscopic techniques. The XRD analysis confirms that the oxidized MWCNTs exist in a hexagonal structure and the sharp XRD peak corresponds to the (002) Bragg’s reflection plane, which indicates that the MWCNTs have higher crystalline nature. The UV-Vis analysis confirms that the MWCNTs functionalized with the carboxylic acid. The red shift was observed corresponds to the D band in the Raman spectrum, which reveals that the reduced disordered graphitic structure of oxidized MWCNTs. The strong Raman peak was observed at 2563 cm{sup -1} corresponds to the overtone of the D band, which is the characteristic vibrational mode of oxidized MWCNTs. The carboxylic acid functionalization of MWCNTs enhances the dispersibility, which paves the way for potential applications in the field of biosensors and targeted drug delivery.

  8. Preparation and desalination performance of multiwall carbon nanotubes

    International Nuclear Information System (INIS)

    Zhang Dengsong; Shi Liyi; Fang Jianhui; Dai Kai; Li Xuanke

    2006-01-01

    Multiwall carbon nanotubes (MWCNTs) were prepared by catalytic decomposition of methane at 680-700 deg. C, using nickel oxide-silica binary aerogels as the catalyst. The morphological structure of MWCNTs was investigated by transmission electron microscopy (TEM), X-ray diffraction (XRD) and Raman spectroscopy. The results revealed that MWCNTs had a diameter of 40-60 nm, with high quality and high length/diameter ratio, and some metal catalyst particles were encapsulated at the tip of nanotubes. Using MWCNTs as the electrodes of flow-through capacitor (FTC), desalination performance was investigated. The results showed that modification methods had great effect on desalination performance of MWCNTs. The removal amount of NaCl was generally dependent on the surface area and pore volume of MWCNTs. After modification in diluted HNO 3 solution with ultrasonic and then ball milling, the metal catalyst particles at the tip of nanotubes disappeared, the nanotube length became short, the cap at the tip of nanotubes was opened, the internal surface area could be effectively used, leading to increasing the specific surface area and pore volume for MWCNTs, and thus, the desalination performance thereof was the best of all

  9. Microwave conductance properties of aligned multiwall carbon nanotube textile sheets

    Energy Technology Data Exchange (ETDEWEB)

    Brown, Brian L. [Univ. of Texas, Dallas, TX (United States); Martinez, Patricia [Univ. of Texas, Dallas, TX (United States); Zakhidov, Anvar A. [Univ. of Texas, Dallas, TX (United States); Shaner, Eric A. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Lee, Mark [Univ. of Texas, Dallas, TX (United States)

    2015-07-06

    Understanding the conductance properties of multi-walled carbon nanotube (MWNT) textile sheets in the microwave regime is essential for their potential use in high-speed and high-frequency applications. To expand current knowledge, complex high-frequency conductance measurements from 0.01 to 50 GHz and across temperatures from 4.2 K to 300 K and magnetic fields up to 2 T were made on textile sheets of highly aligned MWNTs with strand alignment oriented both parallel and perpendicular to the microwave electric field polarization. Sheets were drawn from 329 and 520 μm high MWNT forests that resulted in different DC resistance anisotropy. For all samples, the microwave conductance can be modeled approximately by a shunt capacitance in parallel with a frequency-independent conductance, but with no inductive contribution. Finally, this is consistent with diffusive Drude conduction as the primary transport mechanism up to 50 GHz. Further, it is found that the microwave conductance is essentially independent of both temperature and magnetic field.

  10. Common Wet Chemical Agents for Purifying Multiwalled Carbon Nanotubes

    Directory of Open Access Journals (Sweden)

    Rasel Das

    2014-01-01

    Full Text Available Purification and functionalization of multiwalled carbon nanotubes (MWCNTs are challenging but vital for their effective applications in various fields including water purification technologies, optoelectronics, biosensors, fuel cells, and electrode arrays. The currently available purification techniques, often complicated and time consuming, yielded shortened and curled MWCNTs that are not suitable for applications in certain fields such as membrane technologies, hybrid catalysis, optoelectronics, and sensor developments. Here we described the H2O2 synergy on the actions of HCl and KOH in purifying and functionalizing pristine MWCNTs. The method (HCl/H2O2 showed 100% purification yield as compared to HCl and KOH/H2O2 with purification yields 93.46 and 3.92%, respectively. We probed the findings using transmission electron microscope, energy dispersive X-ray spectroscope, attenuated total reflectance infrared spectroscope, Raman spectroscope, thermal gravimetric analysis, and X-ray powder diffraction. The study is a new avenue for simple, rapid, low cost, and scalable purification of pristine MWCNTs for application in versatile fields.

  11. Direct Vapor-Phase Bromination of Multiwall Carbon Nanotubes

    Directory of Open Access Journals (Sweden)

    Ilya Mazov

    2012-01-01

    Full Text Available We present the simple procedure of the vapor-phase bromination of multiwall carbon nanotubes (MWNTs at moderate temperatures. MWNTs with average diameter 9±3 nm were treated with Br2 vapors at 250°C to produce Br-functionalized product. Transmission electron microscopy analysis was used to prove low damage of MWNT walls during bromination. X-ray photoelectron spectroscopy (XPS and differential thermal analysis (DTA were used to investigate chemical composition of the surface of initial and brominated nanotubes. The experimental results show that the structure of MWNTs is not affected by the bromination process and the total amount of Br-containing surface functions reaches 2.5 wt. %. Electrophysical properties of initial and brominated MWNTs were investigated showing decrease of conductivity for functionalized sample. Possible mechanism of the vapor-phase bromination via surface defects and oxygen-containing functional groups was proposed according to data obtained. Additional experiments with bromination of annealed low-defected MWNTs were performed giving Br content a low as 0.75 wt. % proving this hypothesis.

  12. Photothermal therapy of melanoma tumor using multiwalled carbon nanotubes

    Directory of Open Access Journals (Sweden)

    Sobhani Z

    2017-06-01

    Full Text Available Zahra Sobhani,1,2 Mohammad Ali Behnam,3 Farzin Emami,3 Amirreza Dehghanian,4 Iman Jamhiri5 1Quality Control Department, Faculty of Pharmacy, 2Center for Nanotechnology in Drug Delivery, Faculty of Pharmacy, Shiraz University of Medical Sciences, 3Opto-Electronic Research Center, Electrical and Electronics Engineering Department, Shiraz University of Technology, 4Pathology Department, 5Stem Cell Technology Research Center, Shiraz University of Medical Sciences, Shiraz, Iran Abstract: Photothermal therapy (PTT is a therapeutic method in which photon energy is transformed into heat rapidly via different operations to extirpate cancer. Nanoparticles, such as carbon nanotubes (CNTs have exceptional optical absorbance in visible and near infrared spectra. Therefore, they could be a good converter to induce hyperthermia in PTT technique. In our study, for improving the dispersibility of multiwalled CNTs in water, the CNTs were oxidized (O-CNTs and then polyethylene glycol (PEG was used for wrapping the surface of nanotubes. The formation of a thin layer of PEG around the nanotubes was confirmed through Fourier transform infrared, thermogravimetric analysis, and field emission scanning electron microscopy techniques. Results of thermogravimetric analysis showed that the amount of PEG component in the O-CNT-PEG was approximately 80% (w/w. Cell cytotoxicity study showed that O-CNT was less cytotoxic than pristine multiwalled nanotubes, and O-CNT-PEG had the lowest toxicity against HeLa and HepG2 cell lines. The effect of O-CNT-PEG in reduction of melanoma tumor size after PTT was evaluated. Cancerous mice were exposed to a continuous-wave near infrared laser diode (λ=808 nm, P=2 W and I=8 W/cm2 for 10 minutes once in the period of the treatment. The average size of tumor in mice receiving O-CNT-PEG decreased sharply in comparison with those that received laser therapy alone. Results of animal studies indicate that O-CNT-PEG is a powerful candidate for

  13. Carbon paste electrode incorporating multi-walled carbon nanotube ...

    Indian Academy of Sciences (India)

    The preparation and electrochemical performance of the carbon nanotube paste electrode modified with ferrocene (FCMCNPE) was investigated for electrocatalytic behaviour toward oxidation of -acetyl--cysteine (NAC) in the presence of tryptophan (Trp) using cyclic voltammetry (CV) and differential pulse voltammetry ...

  14. Multiwalled carbon nanotube hybrids as MRI contrast agents

    Directory of Open Access Journals (Sweden)

    Nikodem Kuźnik

    2016-07-01

    Full Text Available Magnetic resonance imaging (MRI is one of the most commonly used tomography techniques in medical diagnosis due to the non-invasive character, the high spatial resolution and the possibility of soft tissue imaging. Contrast agents, such as gadolinium complexes and superparamagnetic iron oxides, are administered to spotlight certain organs and their pathologies. Many new models have been proposed that reduce side effects and required doses of these already clinically approved contrast agents. These new candidates often possess additional functionalities, e.g., the possibility of bioactivation upon action of particular stimuli, thus serving as smart molecular probes, or the coupling with therapeutic agents and therefore combining both a diagnostic and therapeutic role. Nanomaterials have been found to be an excellent scaffold for contrast agents, among which carbon nanotubes offer vast possibilities. The morphology of multiwalled carbon nanotubes (MWCNTs, their magnetic and electronic properties, the possibility of different functionalization and the potential to penetrate cell membranes result in a unique and very attractive candidate for a new MRI contrast agent. In this review we describe the different issues connected with MWCNT hybrids designed for MRI contrast agents, i.e., their synthesis and magnetic and dispersion properties, as well as both in vitro and in vivo behavior, which is important for diagnostic purposes. An introduction to MRI contrast agent theory is elaborated here in order to point to the specific expectations regarding nanomaterials. Finally, we propose a promising, general model of MWCNTs as MRI contrast agent candidates based on the studies presented here and supported by appropriate theories.

  15. Temperature dependent evolution of the local electronic structure of atmospheric plasma treated carbon nanotubes: Near edge x-ray absorption fine structure study

    International Nuclear Information System (INIS)

    Roy, S. S.; Papakonstantinou, P.; Okpalugo, T. I. T.; Murphy, H.

    2006-01-01

    Near edge x-ray absorption fine structure (NEXAFS) spectroscopy has been employed to obtain the temperature dependent evolution of the electronic structure of acid treated carbon nanotubes, which were further modified by dielectric barrier discharge plasma processing in an ammonia atmosphere. The NEXAFS studies were performed from room temperature up to 900 deg. C. The presence of oxygen and nitrogen containing functional groups was observed in C K edge, N K edge, and O K edge NEXAFS spectra of the multiwalled carbon nanotubes. The N K edge spectra revealed three types of π* features, the source of which was decisively identified by their temperature dependent evolution. It was established that these features are attributed to pyridinelike, NO, and graphitelike structures, respectively. The O K edge indicated that both carbonyl (C=O), π*(CO), and ether C-O-C, σ*(CO), functionalities were present. Upon heating in a vacuum to 900 deg. C the π*(CO) resonances disappeared while the σ*(CO) resonances were still present confirming their higher thermal stability. Heating did not produce a significant change in the π* feature of the C K edge spectrum indicating that the tabular structure of the nanotubes is essentially preserved following the thermal decomposition of the functional groups on the nanotube surface

  16. Effect of doping of multi-walled carbon nanotubes on phenolic based carbon fiber reinforced nanocomposites

    International Nuclear Information System (INIS)

    Saeed, Sadaf; Hakeem, Saira; Faheem, Muhammad; Alvi, Rashid Ahmed; Farooq, Khawar; Hussain, Syed Tajammul; Ahmad, Shahid Nisar

    2013-01-01

    We report on the effect of multi-walled carbon nanotubes (MWCNTs) on different properties of phenolic resin. A low content of MWCNTs (∼ 0.05 wt%) was mixed in phenolic resin and a stable dispersion was achieved by ultrasonication, followed by melt mixing. After curing the characterization of these composites was done by using scanning electron microscopy (SEM), thermogravimetric analysis (TGA), and Fourier transform infra-red spectroscopy (FTIR). The thermal and ablative properties of carbon fiber reinforced MWCNTs-phenolic nanocomposites were also studied. The addition of MWCNTs showed improvement in thermal stability and ablation properties.

  17. The hepatotoxicity of multi-walled carbon nanotubes in mice

    Science.gov (United States)

    Ji, Zongfei; Zhang, Danying; Li, Ling; Shen, Xizhong; Deng, Xiaoyong; Dong, Ling; Wu, Minhong; Liu, Yuanfang

    2009-11-01

    The hepatotoxicity of two types of multi-walled carbon nanotubes (MWCNTs), acid-oxidized MWCNTs (O-MWCNTs) and Tween-80-dispersed MWCNTs (T-MWCNTs), were investigated with Kunming mice exposed to 10 and 60 mg kg-1 by intravenous injection for 15 and 60 d. Compared with the PBS group, the body-weight gain of the mice decreased and the level of total bilirubin and aspartate aminotransferase increased in the MWCNT-exposed group with a significant dose-effect relationship, while tumor necrosis factor alpha level did not show significant statistical change within 60 d. Spotty necrosis, inflammatory cell infiltration in portal region, hepatocyte mitochondria swelling and lysis were observed with a significant dose-effect relationship in the MWCNT groups. Liver damage of the T-MWCNT group was more severe than that of the O-MWCNT group according to the Roenigk classification system. Furthermore, T-MWCNTs induce slight liver oxidative damage in mice at 15 d, which was recovered at 60 d. Part of the gene expressions of mouse liver in the MWCNT groups changed compared to the PBS group, including GPCRs (G protein-coupled receptors), cholesterol biosynthesis, metabolism by cytochrome P450, natural-killer-cell-mediated cytotoxicity, TNF- α, NF-κB signaling pathway, etc. In the P450 pathway, the gene expressions of Gsta2 (down-regulated), Cyp2B19 (up-regulated) and Cyp2C50 (down-regulated) had significant changes in the MWCNT groups. These results show that a high dose of T-MWCNTs can induce hepatic toxicity in mice while O-MWCNTs seem to have less toxicity.

  18. Vibration electrospinning of Polyamide-66/Multiwall Carbon Nanotube Nanocomposite: introducing electrically conductive, ultraviolet blocking and antibacterial properties

    Directory of Open Access Journals (Sweden)

    Zohoori Salar

    2017-09-01

    Full Text Available Fabrication of electro-conductive fiber is a novel process. Nanocomposites of multiwall carbon nanotube/polyamide66 were produced by electrospinning with different amounts of multiwall carbon nanotube. Field emission scanning electron microscope and Fourier transform infrared spectroscopy of samples proved the existence of multiwall carbon nanotube distribution in polyamide 66 nanofibers. Results showed that electro conductivity of electrospun multiwall carbon nanotube/polyamide 66 nano fiber has increased in comparison with electrospun polyamide 66. Moreover, UV blocking of samples was investigated which has shown that using multiwall carbon nanotube in polyamide 66 increases UV blocking of fibers. Furthermore, anti-bacterial activity of nanocomposite showed that these nanocomposites have antibacterial property against both Staphylococcus Aureus and Escherichia Coli bacteria according to AATCC test method.

  19. Quantum oscillations and ferromagnetic hysteresis observed in iron filled multiwall carbon nanotubes.

    Science.gov (United States)

    Barzola-Quiquia, J; Klingner, N; Krüger, J; Molle, A; Esquinazi, P; Leonhardt, A; Martínez, M T

    2012-01-13

    We report on the electrical transport properties of single multiwall carbon nanotubes with and without an iron filling as a function of temperature and magnetic field. For the iron filled nanotubes the magnetoresistance shows a magnetic behavior induced by iron, which can be explained by taking into account a contribution of s-d hybridization. In particular, ferromagnetic-like hysteresis loops were observed up to 50 K for the iron filled multiwall carbon nanotubes. The magnetoresistance shows quantum interference phenomena such as universal conductance fluctuations and weak localization effects.

  20. Structural and electrical properties of functionalized multiwalled carbon nanotube/epoxy composite

    International Nuclear Information System (INIS)

    Gantayat, S.; Rout, D.; Swain, S. K.

    2016-01-01

    The effect of the functionalization of multiwalled carbon nanotube on the structure and electrical properties of composites was investigated. Samples based on epoxy resin with different weight percentage of MWCNTs were prepared and characterized. The interaction between MWCNT & epoxy resin was noticed by Fourier transform infrared spectroscopy (FTIR). The structure of functionalized multiwalled carbon nanotube (f-MWCNT) reinforced epoxy composite was studied by field emission scanning electron microscope (FESEM). The dispersion of f-MWCNT in epoxy resin was evidenced by high resolution transmission electron microscope (HRTEM). Electrical properties of epoxy/f-MWCNT nanocomposites were measured & the result indicated that the conductivity increased with increasing concentration of f-MWCNTs.

  1. Determination of multi-walled carbon nanotube bioaccumulation in earthworms measured by a microwave-based detection technique

    Science.gov (United States)

    Reliable quantification techniques for carbon nanotubes (CNTs) are limited. In this study, a new procedure was developed for quantifying multi-walled carbon nanotubes (MWNTs) in earthworms (Eisenia fetida) based on freeze drying and microwave-induced heating. Specifically, earthw...

  2. On Young's modulus of multi-walled carbon nanotubes

    Indian Academy of Sciences (India)

    WINTEC

    load transfer in nanocomposites. In the present work, CNT/Al ... calculations. The theoretical modulus of the graphene sheet is supposed to be 1060 GPa (Harris 2004). The reason why multi-walled nanotubes have a modulus > 1060 GPa (that of graphene sheet) is currently not understood. However, in the present paper, ...

  3. Effect of amino acid-functionalized multi-walled carbon nanotubes ...

    Indian Academy of Sciences (India)

    In a single-step, rapid microwave-assisted process, multi-walled carbon nanotubes were functionalized by -valine amino acid. Formation of amino acid on nanotube surface was confirmed by Fourier transform-infrared spectroscopy, thermogravimetric analysis, X-ray diffraction, field emission scanning and transmission ...

  4. Effect of Multiwalled Carbon Nanotubes on the Properties of EPDM/NBR Dissimilar Elastomer Blends

    NARCIS (Netherlands)

    Hoikkanen, M.; Poikelispää, M.; Das, A.; Honkanen, M.; Dierkes, Wilma K.; Vuorinen, J.

    2015-01-01

    In the presence of multiwalled carbon nanotubes (MWCNT), polar nitrile-butadiene rubber (NBR) and nonpolar ethylene propylene diene rubber (EPDM) blends were prepared following a melt mixing method. For the preparation of MWCNT filled EPDM/NBR blends, two mixing methods were used: direct mixing and

  5. Comparative Study of Single- and Multi-Wall Carbon Nanotubes with Application in Cerebral Aneurysm

    Directory of Open Access Journals (Sweden)

    Rodica-Mariana Ion

    2011-01-01

    Full Text Available Helping improve humanity is one of the promises of nanotech-
    nology and nanomedicine. This paper will highlight some of the research findings in the nanomedicine area by testing some single- and multi-walls carbon nanotubues in rats cerebral aneurisms.

  6. Electrochemical capacitive behaviour of multiwalled carbon nanotubes modified with electropolymeric films of nickel tetraaminophthalocyanine

    CSIR Research Space (South Africa)

    Chidembo, AT

    2010-11-01

    Full Text Available Electrochemical capacitive behaviour of the electropolymeric nickel tetra-aminophthalocyanine (poly-NiTAPc) supported on multiwalled carbon nanotube (MWCNT) platform is described. From the data in 1 M H2SO4, the MWCNT-poly-NiTAPc exhibited superior...

  7. Field emission from individual multiwalled carbon nanotubes prepared in an electron microscope

    NARCIS (Netherlands)

    de Jonge, N.; van Druten, N.J.

    2003-01-01

    Individual multiwalled carbon nanotube field emitters were prepared in a scanning electron microscope. The angular current density, energy spectra, and the emission stability of the field-emitted electrons were measured. An estimate of the electron source brightness was extracted from the

  8. Crystallization and melting behavior of multi-walled carbon nanotube-reinforced nylon-6 composites

    NARCIS (Netherlands)

    Phang, In Yee; Ma, Jianhua; Shen, Lu; Liu, Tianxi; Zhang, Wei-De

    2006-01-01

    The crystallization and melting behavior of neat nylon-6 (PA6) and multi-walled carbon nanotubes (MWNTs)/PA6 composites prepared by simple melt-compounding was comparatively studied. Differential scanning calorimetry (DSC) results show two crystallization exotherms (TCC, 1 and TCC, 2) for PA6/MWNTs

  9. Water-Dispersible Multi-Walled Carbon Nanotubes and Novel Hybrid Nanostructures

    NARCIS (Netherlands)

    Pham, Tuan Anh; Son, Se Mo; Jeong, Yeon Tae

    2010-01-01

    Water-dispersible multi-walled carbon nanotubes (MWNTs) were successfully prepared by the chemical grafting of acylated MWNTs with adenosine. The MWNTs were first purified and oxidized in order to obtain carboxylic acid funcionalized MWNTs, which was further acylated with thionyl chloride to give

  10. Vascular effects of multiwalled carbon nanotubes in dyslipidemic ApoE-/- mice and cultured endothelial cells

    DEFF Research Database (Denmark)

    Cao, Yi; Jacobsen, Nicklas Raun; Danielsen, Pernille Høgh

    2014-01-01

    Accumulating evidences indicate that pulmonary exposure to carbon nanotubes (CNTs) is associated with increased risk of lung diseases, whereas the effect on the vascular system is less studied. We investigated vascular effects of 2 types of multiwalled CNTs (MWCNTs) in apolipoprotein E(-/-) mice,...

  11. A Multi-Walled Carbon Nanotube-based Biosensor for Monitoring Microcystin-LR in Sources of Drinking Water Supplies

    Science.gov (United States)

    A multi-walled carbon nanotube-based electrochemical biosensor is developed for monitoring microcystin-LR (MC-LR), a toxic cyanobacterial toxin, in sources of drinking water supplies. The biosensor electrodes are fabricated using dense, mm-long multi-walled CNT (MWCNT) arrays gro...

  12. Biosensor based on a glassy carbon electrode modified with tyrosinase immobilized on multiwalled carbon nanotubes

    International Nuclear Information System (INIS)

    Ren, J.; Kang, T.F.; Xue, R.; Ge, C.N.; Cheng, S.Y.

    2011-01-01

    We describe a biosensor for phenolic compounds that is based on a glassy carbon electrode modified with tyrosinase immobilized on multiwalled carbon nanotubes (MWNTs). The MWNTs possess excellent inherent electrical conductivity which enhances the electron transfer rate and results in good electrochemical catalytic activity towards the reduction of benzoquinone produced by enzymatic reaction. The biosensor was characterized by cyclic voltammetry, and the experimental conditions were optimized. The cathodic current is linearly related to the concentration of the phenols between 0.4 μM and 10 μM, and the detection limit is 0.2 μM. The method was applied to the determination of phenol in water samples (author)

  13. Electrochemical parameters of ethamsylate at multi-walled carbon nanotube modified glassy carbon electrodes.

    Science.gov (United States)

    Wang, Sheng-Fu; Xu, Qiao

    2007-05-01

    In this paper, some electrochemical parameters of ethamsylate at a multi-walled carbon nanotube modified glassy carbon electrode, such as the charge number, exchange current density, standard heterogeneous rate constant and diffusion coefficient, were measured by cyclic voltammetry, chronoamperometry and chronocoulometry. The modified electrode exhibits good promotion of the electrochemical reaction of ethamsylate and increases the standard heterogeneous rate constant of ethamsylate greatly. The differential pulse voltammetry responses of ethamsylate were linearly dependent on its concentrations in a range from 2.0 x 10(-6) to 6.0 x 10(-5) mol L(-1), with a detection limit of 4.0 x 10(-7) mol L(-1).

  14. High-efficiency supercapacitor electrodes of CVD-grown graphenes hybridized with multiwalled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Kalam, Amir Abul; Bae, Joon Ho [Dept. of Nano-physics, Gachon University, Seongnam (Korea, Republic of); Park, Soo Bin; Seo, Yong Ho [Nanotechnology and Advanced Material Engineering, HMC, and GRI, Sejong University, Seoul (Korea, Republic of)

    2015-08-15

    We demonstrate, for the first time, high-efficiency supercapacitors by utilizing chemical vapor deposition (CVD)-grown graphenes hybridized with multiwalled carbon nanotubes (CNTs). A single-layer graphene was grown by simple CVD growth method, and transferred to polyethylene terephthalate substrates. The bare graphenes were further hybridized with multiwalled CNTs by drop-coating CNTs on graphenes. The supercapacitors using bare graphenes and graphenes with CNTs revealed that graphenes with CNTs resulted in enhanced supercapacitor performances of 2.2- (the mass-specific capacitance) and 4.4-fold (the area-specific capacitance) of those of bare graphenes. Our strategy to improve electrochemical performance of CVD-grown graphenes is advantageous for large-scale graphene electrodes due to high electrical conductivity of CVD-grown graphenes and cost-effectiveness of using multiwalled CNTs as compared to conventional employment of single-walled CNTs.

  15. High-efficiency supercapacitor electrodes of CVD-grown graphenes hybridized with multiwalled carbon nanotubes

    International Nuclear Information System (INIS)

    Kalam, Amir Abul; Bae, Joon Ho; Park, Soo Bin; Seo, Yong Ho

    2015-01-01

    We demonstrate, for the first time, high-efficiency supercapacitors by utilizing chemical vapor deposition (CVD)-grown graphenes hybridized with multiwalled carbon nanotubes (CNTs). A single-layer graphene was grown by simple CVD growth method, and transferred to polyethylene terephthalate substrates. The bare graphenes were further hybridized with multiwalled CNTs by drop-coating CNTs on graphenes. The supercapacitors using bare graphenes and graphenes with CNTs revealed that graphenes with CNTs resulted in enhanced supercapacitor performances of 2.2- (the mass-specific capacitance) and 4.4-fold (the area-specific capacitance) of those of bare graphenes. Our strategy to improve electrochemical performance of CVD-grown graphenes is advantageous for large-scale graphene electrodes due to high electrical conductivity of CVD-grown graphenes and cost-effectiveness of using multiwalled CNTs as compared to conventional employment of single-walled CNTs

  16. Reduction of short wavelength reflectance of multi-wall carbon nanotubes through ultraviolet laser irradiation

    Science.gov (United States)

    Stephens, Michelle S.; Simonds, Brian J.; Yung, Christopher S.; Conklin, Davis; Livigni, David J.; Oliva, Alberto Remesal; Lehman, John H.

    2018-05-01

    Multi-wall carbon nanotube coatings are used as broadband, low-reflectance absorbers for bolometric applications and for stray light control. They are also used as high emittance blackbody radiators. Irradiation of single wall carbon nanotubes with ultraviolet (UV) laser light has been shown to remove amorphous carbon debris, but there have been few investigations of the interaction of UV light with the more complex physics of multi-wall carbon nanotubes. We present measurements of reflectance and surface morphology before and after exposure of multi-wall carbon nanotube coatings to 248 nm UV laser light. We show that UV exposure reduces the reflectivity at wavelengths below 600 nm and present modeling of the thermal cycling the UV exposure causes at the surface of the carbon nanotubes. This effect can be used to flatten the spectral shape of the reflectivity curve of carbon nanotube absorber coatings used for broadband applications. Finally, we find that the effect of UV exposure depends on the nanotube growth process.

  17. Noncovalent Attachment of PbS Quantum Dots to Single- and Multiwalled Carbon Nanotubes

    Directory of Open Access Journals (Sweden)

    Anirban Das

    2014-01-01

    Full Text Available Attachment of PbS quantum dots (QD to single-walled carbon nanotubes (SWNT and multiwalled carbon nanotubes (MWCNT is described; wherein commercially obtained PbS-QD of size 2.7 nm, stabilized by oleic acid, are added to a suspension of single- or multiwalled carbon nanotubes (CNT prefunctionalized noncovalently with 1,2-benzenedimethanethiol (1,2-BDMT in ethanol. The aromatic part of 1,2-BDMT attaches to the CNT by π-π stacking interactions, noncovalently functionalizing the CNT. The thiol part of the 1,2-BDMT on the functionalized CNT replaces oleic acid on the surface of the QD facilitating the noncovalent attachment of the QD to the CNT. The composites were characterized by TEM and FTIR spectroscopy. Quenching of NIR fluorescence of the PbS-QD on attachment to the carbon nanotubes (CNT was observed, indicating FRET from the QD to the CNT.

  18. Multiwalled carbon nanotubes effect on the bioavailability of artemisinin and its cytotoxity to cancerous cells

    Science.gov (United States)

    Rezaei, Behzad; Majidi, Najmeh; Noori, Shokoofe; Hassan, Zuhair M.

    2011-12-01

    Artemisinin regarded as one of the most promising anticancer drugs can bind to DNA with a binding constant of 1.04 × 104 M-1. The electrochemical experiments indicated that for longer incubation time periods, the reduction peak current of artemisinin on carbon nanotube modified electrode increases. Therefore, the uptake of drug molecules from a solution into CNTs will be achieved automatically by adsorption of 88.7% of artemisinin onto carbon nanotubes surface without alteration in drug properties. Hence, capability of carbon nanotubes to have synergistic effect on the bioavailability of artemisinin was investigated. Experimental tests on K562 cancer cell lines growth by MTT assay proved that multi-walled carbon nanotubes can enhance the cytotoxity of artemisinin to the targeted cancer cells with unprecedented accuracy and efficiency. The IC50 values were 65 and 35 μM for artemisinin and artemisinin loaded on multi-walled carbon nanotubes, respectively; demonstrating that artemisinin loaded on multi-walled carbon nanotubes is more effective in inhibition of cancer cell lines growth.

  19. Multiwalled carbon nanotubes effect on the bioavailability of artemisinin and its cytotoxity to cancerous cells

    International Nuclear Information System (INIS)

    Rezaei, Behzad; Majidi, Najmeh; Noori, Shokoofe; Hassan, Zuhair M.

    2011-01-01

    Artemisinin regarded as one of the most promising anticancer drugs can bind to DNA with a binding constant of 1.04 × 10 4 M −1 . The electrochemical experiments indicated that for longer incubation time periods, the reduction peak current of artemisinin on carbon nanotube modified electrode increases. Therefore, the uptake of drug molecules from a solution into CNTs will be achieved automatically by adsorption of 88.7% of artemisinin onto carbon nanotubes surface without alteration in drug properties. Hence, capability of carbon nanotubes to have synergistic effect on the bioavailability of artemisinin was investigated. Experimental tests on K562 cancer cell lines growth by MTT assay proved that multi-walled carbon nanotubes can enhance the cytotoxity of artemisinin to the targeted cancer cells with unprecedented accuracy and efficiency. The IC 50 values were 65 and 35 μM for artemisinin and artemisinin loaded on multi-walled carbon nanotubes, respectively; demonstrating that artemisinin loaded on multi-walled carbon nanotubes is more effective in inhibition of cancer cell lines growth.

  20. Comparative study of reflectance properties of nanodiamonds, onion-like carbon and multiwalled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Kuznetsov, V.L. [Novosibirsk State University, Pirogova St. 2, 630090 Novosibirsk (Russian Federation); Moseenkov, S.I. [Boreskov Institute of Catalysis, SB RAS, Lavrentiev Ave. 5, 630090 Novosibirsk (Russian Federation); Nikolaev Institute of Inorganic Chemistry, SB RAS, Lavrentiev Ave. 3, 630090 Novosibirsk (Russian Federation); Elumeeva, K.V. [Novosibirsk State University, Pirogova St. 2, 630090 Novosibirsk (Russian Federation); Boreskov Institute of Catalysis, SB RAS, Lavrentiev Ave. 5, 630090 Novosibirsk (Russian Federation); Larina, T.V.; Anufrienko, V.F. [Boreskov Institute of Catalysis, SB RAS, Lavrentiev Ave. 5, 630090 Novosibirsk (Russian Federation); Romanenko, A.I.; Anikeeva, O.B.; Tkachev, E.N. [Novosibirsk State University, Pirogova St. 2, 630090 Novosibirsk (Russian Federation); Nikolaev Institute of Inorganic Chemistry, SB RAS, Lavrentiev Ave. 3, 630090 Novosibirsk (Russian Federation)

    2011-11-15

    Carbon nanomaterials are the promising candidates for potential broadband limiting applications and extremely low reflectance coatings, particularly in the infrared, visible and UV spectral regions. In this paper we have performed the comparative study of diffuse reflectance of nanodiamond (ND), sp{sup 2}/sp{sup 3} composites, onion-like carbon (OLC) and multiwalled carbon nanotubes (MWNTs) in visible and UV regions. ND, sp{sup 2}/sp{sup 3} composites and OLC produced via high temperature annealing of the same set of NDs allow us to vary sp{sup 2}/sp{sup 3} carbon ratio, size of primary particle agglomerates and concentration of defects while MWNT set provides possibility to vary NT diameters and length, order/disorder degree (via high temperature MWNTS annealing). The diffuse reflectance of carbon nanomaterials depends mainly on the electronic configuration, defect concentration, size of graphene-like ordered fragments and agglomerates of nanoparticles along with their morphology. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  1. ELECTROPHORETIC DEPOSITION OF TIO2-MULTI-WALLED CARBON NANOTUBE COMPOSITE COATINGS: MORPHOLOGICAL STUDY

    Directory of Open Access Journals (Sweden)

    M. S. MAHMOUDI JOZEE

    2016-09-01

    Full Text Available A homogenous TiO2 / multi-walled carbon nanotubes(MWCNTs composite film were prepared by electrophoretic co-deposition from organic suspension on a stainless steel substrate.  In this study, MWCNTs was incorporated to the coating because of their long structure and their capability to be functionalized by different inorganic groups on the surface. FTIR spectroscopy showed the existence of carboxylic groups on the modified carbon nanotubes surface. The effect of applied electrical fields, deposition time and concentration of nanoparticulates on coatings morphology were investigated by scanning electron microscopy. It was found that combination of MWCNTs within TiO2 matrix eliminating micro cracks presented on TiO2 coating. Also, by increasing the deposition voltages, micro cracks were increased. SEM observation of the coatings revealed that TiO2/multi-walled carbon nanotubes coatings produced from optimized electric field was uniform and had good adhesive to the substrate.

  2. Multiwalled Carbon Nanotube Forest Grown via Chemical Vapor Deposition from Iron Catalyst Nanoparticles, by XPS

    Energy Technology Data Exchange (ETDEWEB)

    Jensen, David S.; Kanyal, Supriya S.; Madaan, Nitesh; Vail, Michael A.; Dadson, Andrew; Engelhard, Mark H.; Linford, Matthew R.

    2013-09-25

    Carbon nanotubes (CNTs) have unique chemical and physical properties. Herein, we report an XPS analysis of a forest of multiwalled CNTs using monochromatic Al Kα radiation. Survey scans show only one element: carbon. The carbon 1s peak is centered 284.5 eV. The C 1s envelope also shows the expected π → π* shake-up peak at ca. 291 eV. The valence band and carbon KVV Auger signals are presented. When patterned, the CNT forests can be used as a template for subsequent deposition of metal oxides to make thin layer chromatography plates.1-3

  3. Electrochemical biosensing of galactose based on carbon materials: graphene versus multi-walled carbon nanotubes.

    Science.gov (United States)

    Dalkıran, Berna; Erden, Pınar Esra; Kılıç, Esma

    2016-06-01

    In this study, two enzyme electrodes based on graphene (GR), Co3O4 nanoparticles and chitosan (CS) or multi-walled carbon nanotubes (MWCNTs), Co3O4 nanoparticles, and CS, were fabricated as novel biosensing platforms for galactose determination, and their performances were compared. Galactose oxidase (GaOx) was immobilized onto the electrode surfaces by crosslinking with glutaraldehyde. Optimum working conditions of the biosensors were investigated and the analytical performance of the biosensors was compared with respect to detection limit, linearity, repeatability, and stability. The MWCNTs-based galactose biosensor provided about 1.6-fold higher sensitivity than its graphene counterpart. Moreover, the linear working range and detection limit of the MWCNTs-based galactose biosensor was superior to the graphene-modified biosensor. The successful application of the purposed biosensors for galactose biosensing in human serum samples was also investigated.

  4. The surface modifications of multi-walled carbon nanotubes for multi-walled carbon nanotube/poly(ether ether ketone) composites

    International Nuclear Information System (INIS)

    Cao, Zongshuang; Qiu, Li; Yang, Yongzhen; Chen, Yongkang; Liu, Xuguang

    2015-01-01

    Graphical abstract: Multi-walled carbon nanotube/poly(ether ether ketone) (MWCNT/PEEK) composites incorporating surface modified multi-walled carbon nanotubes (MWCNTs) as fillers were fabricated in a solution blending method in order to explore the dynamic mechanical and tribological properties of MWCNT/PEEK composites systematically. It is evident that surface modifications of MWCNTs have a significant impact on dispersibility of MWCNTs in PEEK, dynamic mechanical and tribological properties of MWCNT/PEEK composites. Typically, a clear effect of surface modifications of MWCNTs on tribological properties of MWCNT/PEEK composites was observed. A significant reduction in frictional coefficient of MWCNT/PEEK composites with the MWCNTs modified with ethanolamine has been achieved and the self-lubricating film on their worn surfaces was also observed. - Highlights: • The dispersibility of surface modified MWCNTs in PEEK has been studied. • MWCNTs modified with ethanolamine have showed a good dispersion in PEEK. • Surface modifications of MWCNTs have a significant impact on both dynamic mechanical and tribological properties of MWCNT/PEEK composites. - Abstract: The effects of surface modifications of multi-walled carbon nanotubes (MWCNTs) on the morphology, dynamic mechanical and tribological properties of multi-walled carbon nanotube/poly(ether ether ketone) (MWCNT/PEEK) composites have been investigated. MWCNTs were treated with mixed acids to obtain acid-functionalized MWCNTs. Then the acid-functionalized MWCNTs were modified with ethanolamine (named e-MWCNTs). The MWCNT/PEEK composites were prepared by a solution-blending method. A more homogeneous distribution of e-MWCNTs within the composites was found with scanning electron microscopy. Dynamic mechanical analysis demonstrated a clear increase in the storage modulus of e-MWCNT/PEEK composites because of the improved interfacial adhesion strength between e-MWCNTs and PEEK. Furthermore, the presence of e

  5. The surface modifications of multi-walled carbon nanotubes for multi-walled carbon nanotube/poly(ether ether ketone) composites

    Energy Technology Data Exchange (ETDEWEB)

    Cao, Zongshuang [Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education, Taiyuan University of Technology, Taiyuan 030024 (China); Research Center of Advanced Material Science and Technology, Taiyuan University of Technology, Taiyuan 030024 (China); Qiu, Li [Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education, Taiyuan University of Technology, Taiyuan 030024 (China); College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Yang, Yongzhen, E-mail: yyztyut@126.com [Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education, Taiyuan University of Technology, Taiyuan 030024 (China); Research Center of Advanced Material Science and Technology, Taiyuan University of Technology, Taiyuan 030024 (China); Chen, Yongkang, E-mail: y.k.chen@herts.ac.uk [Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education, Taiyuan University of Technology, Taiyuan 030024 (China); University of Hertfordshire, School of Engineering and Technology, Hatfield, Hertfordshire AL10 9AB (United Kingdom); Liu, Xuguang [Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education, Taiyuan University of Technology, Taiyuan 030024 (China); College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China)

    2015-10-30

    Graphical abstract: Multi-walled carbon nanotube/poly(ether ether ketone) (MWCNT/PEEK) composites incorporating surface modified multi-walled carbon nanotubes (MWCNTs) as fillers were fabricated in a solution blending method in order to explore the dynamic mechanical and tribological properties of MWCNT/PEEK composites systematically. It is evident that surface modifications of MWCNTs have a significant impact on dispersibility of MWCNTs in PEEK, dynamic mechanical and tribological properties of MWCNT/PEEK composites. Typically, a clear effect of surface modifications of MWCNTs on tribological properties of MWCNT/PEEK composites was observed. A significant reduction in frictional coefficient of MWCNT/PEEK composites with the MWCNTs modified with ethanolamine has been achieved and the self-lubricating film on their worn surfaces was also observed. - Highlights: • The dispersibility of surface modified MWCNTs in PEEK has been studied. • MWCNTs modified with ethanolamine have showed a good dispersion in PEEK. • Surface modifications of MWCNTs have a significant impact on both dynamic mechanical and tribological properties of MWCNT/PEEK composites. - Abstract: The effects of surface modifications of multi-walled carbon nanotubes (MWCNTs) on the morphology, dynamic mechanical and tribological properties of multi-walled carbon nanotube/poly(ether ether ketone) (MWCNT/PEEK) composites have been investigated. MWCNTs were treated with mixed acids to obtain acid-functionalized MWCNTs. Then the acid-functionalized MWCNTs were modified with ethanolamine (named e-MWCNTs). The MWCNT/PEEK composites were prepared by a solution-blending method. A more homogeneous distribution of e-MWCNTs within the composites was found with scanning electron microscopy. Dynamic mechanical analysis demonstrated a clear increase in the storage modulus of e-MWCNT/PEEK composites because of the improved interfacial adhesion strength between e-MWCNTs and PEEK. Furthermore, the presence of e

  6. Freestanding bucky paper with high strength from multi-wall carbon nanotubes

    International Nuclear Information System (INIS)

    Li, Zhonglai; Xu, Ju; O'Byrne, Justin P.; Chen, Lan; Wang, Kaixue; Morris, Michael A.; Holmes, Justin D.

    2012-01-01

    Bucky papers have been investigated by some research groups, however, due to different qualities of carbon nanotubes used, various results of strength and electronic properties were reported in the literatures. In this article, the effects of carbon nanotubes synthesized over different catalysts on the qualities of bucky papers were systemically investigated. Multi-wall carbon nanotubes were synthesized over a series of MgO supported catalysts with different weight ratios of Mo and Co. As the ratios of Mo/Co in the catalysts were increased from 0 to 3, the yields of carbon nanotubes were enhanced from 7 wt% to 400 wt%. However, the yield enhancement of carbon nanotubes was achieved at the expense of higher proportion of structural defects within carbon nanotubes, which has been proved by Raman spectroscopy and thermogravimetry analysis. It was demonstrated that the tensile strength of bucky paper composed of numerous MCNTs bundles strongly depends on the structure of carbon nanotubes used. By optimizing reaction conditions, a bucky paper with high strain up to 15.36 MPa and electrical conductivity of 61.17 S cm −1 was obtained by Supercritical Fluid (SCF) drying technique. -- Highlights: ► Multi-wall carbon nanotube bucky paper. ► Structural defects of carbon nanotubes. ► CoMo catalyst. ► Tensile strength of bucky paper.

  7. Immobilization of Bovine Serum Albumin Upon Multiwall Carbon Nanotube for High Speed Humidity Sensing Application.

    Science.gov (United States)

    Bhattacharya, Sankhya; Sasmal, Milan

    2016-01-01

    We present a high-speed humidity sensor based on immobilization of bovine serum albumin upon multiwall carbon nanotube (IBC). A simple and versatile drop casting technique was employed to make the humidity sensor using novel material IBC at room temperature. IBC was synthesized using easy solution process technique. The working principle of the IBC humidity sensor depends upon the variation of output current or conductance with the exposure of different humidity level. Humidity sensing properties of our device is explained on the basis of charge transfer from water molecules to IBC and bovine serum albumin to multiwall carbon nanotube (MWCNT). Our sensor exhibits faster response time around 1.2 s and recovery time 1.5 s respectively.

  8. The effect of functionalization on structure and electrical conductivity of multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    Lau, Cher Hon; Cervini, Raoul; Clarke, Stephen R.; Markovic, Milena Ginic; Matisons, Janis G.; Hawkins, Stephen C.; Huynh, Chi P.; Simon, George P.

    2008-01-01

    Carbon nanotubes (CNTs) are of interest in many areas of nanotechnology and used in a number of novel applications. However effective dispersion remains a problem and one solution is to functionalize the nanotubes. Any functionalization that is undertaken must preferably not influence other key properties such as strength and electrical conductivity. In this work, multi-walled CNTs are functionalized for comparison, using a range of oxidative techniques, including thermal treatment, acid reflux, and dry UV-ozonolysis. The effects of these treatments on the multi-walled carbon nanotubes (MWCNTs) and their electrical properties were characterized using a range of surface and compositional techniques. The electrical conductivity of MWCNTs was found to increase with functionalization in all cases, and dry UV-ozonolysis was shown to be the treatment technique which best increased conductivity, whilst at the same time maintaining the structural integrity of the nanotubes, even though the level of modification was less than by the other treatment methods.

  9. Patterned forests of vertically-aligned multiwalled carbon nanotubes using metal salt catalyst solutions.

    Science.gov (United States)

    Garrett, David J; Flavel, Benjamin S; Baronian, Keith H R; Downard, Alison J

    2013-01-01

    A simple method for producing patterned forests of multiwalled carbon nanotubes (MWCNTs) is described. An aqueous metal salt solution is spin-coated onto a substrate patterned with photoresist by standard methods. The photoresist is removed by acetone washing leaving the acetone-insoluble catalyst pattern on the substrate. Dense forests of vertically aligned (VA) MWCNTs are grown on the patterned catalyst layers by chemical vapour deposition. The procedures have been demonstrated by growing MWCNT forests on two substrates: silicon and conducting graphitic carbon films. The forests adhere strongly to the substrates and when grown directly on carbon film, offer a simple method of preparing MWCNT electrodes.

  10. Multi-walled carbon nanotubes (MWCNTs) functionalized with amino groups by reacting with supercritical ammonia fluids

    International Nuclear Information System (INIS)

    Shao Lu; Bai Yongping; Huang Xu; Gao Zhangfei; Meng Linghui; Huang Yudong; Ma Jun

    2009-01-01

    For the first time, supercritical ammonia fluid was utilized to simply functionalize multi-walled carbon nanotube (MWCNT) with amino groups. The successful amino functionalization of MWCNTs was proven and the physicochemical properties of MWCNTs before and after supercritical ammonia fluids modifications were characterized using X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM), atomic force microscope (AFM) and Raman spectroscopy. The results also indicated that the supercritical ammonia fluids had the visible effects on the nanostructure of carbon nanotubes. Our novel modification approach provides an easy way to modify MWCNTs with amino groups, which is very useful for realizing 'carbon nanotube economy' in the near future.

  11. Control of neuronal network organization by chemical surface functionalization of multi-walled carbon nanotube arrays

    International Nuclear Information System (INIS)

    Liu Jie; Bibari, Olivier; Marchand, Gilles; Benabid, Alim-Louis; Sauter-Starace, Fabien; Appaix, Florence; De Waard, Michel

    2011-01-01

    Carbon nanotube substrates are promising candidates for biological applications and devices. Interfacing of these carbon nanotubes with neurons can be controlled by chemical modifications. In this study, we investigated how chemical surface functionalization of multi-walled carbon nanotube arrays (MWNT-A) influences neuronal adhesion and network organization. Functionalization of MWNT-A dramatically modifies the length of neurite fascicles, cluster inter-connection success rate, and the percentage of neurites that escape from the clusters. We propose that chemical functionalization represents a method of choice for developing applications in which neuronal patterning on MWNT-A substrates is required.

  12. Control of neuronal network organization by chemical surface functionalization of multi-walled carbon nanotube arrays

    Energy Technology Data Exchange (ETDEWEB)

    Liu Jie; Bibari, Olivier; Marchand, Gilles; Benabid, Alim-Louis; Sauter-Starace, Fabien [CEA, LETI-Minatec, 17 Rue des Martyrs, 38054 Grenoble Cedex 9 (France); Appaix, Florence; De Waard, Michel, E-mail: fabien.sauter@cea.fr, E-mail: michel.dewaard@ujf-grenoble.fr [Inserm U836, Grenoble Institute of Neuroscience, Site Sante la Tronche, Batiment Edmond J Safra, Chemin Fortune Ferrini, BP170, 38042 Grenoble Cedex 09 (France)

    2011-05-13

    Carbon nanotube substrates are promising candidates for biological applications and devices. Interfacing of these carbon nanotubes with neurons can be controlled by chemical modifications. In this study, we investigated how chemical surface functionalization of multi-walled carbon nanotube arrays (MWNT-A) influences neuronal adhesion and network organization. Functionalization of MWNT-A dramatically modifies the length of neurite fascicles, cluster inter-connection success rate, and the percentage of neurites that escape from the clusters. We propose that chemical functionalization represents a method of choice for developing applications in which neuronal patterning on MWNT-A substrates is required.

  13. Ferromagnetic behaviour of polyaniline-coated multi-wall carbon nanotubes containing nickel nanoparticles

    Czech Academy of Sciences Publication Activity Database

    Konyushenko, Elena; Kazantseva, N. E.; Stejskal, Jaroslav; Trchová, Miroslava; Kovářová, Jana; Sapurina, I.; Tomishko, M. M.

    2008-01-01

    Roč. 320, 3-4 (2008), s. 231-240 ISSN 0304-8853 R&D Projects: GA AV ČR IAA4050313; GA AV ČR IAA400500504; GA MŠk ME 847; GA ČR GA202/06/0419 Institutional research plan: CEZ:AV0Z40500505 Keywords : multi-wall carbon nanotube * conducting polymer * polyaniline coating Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.283, year: 2008

  14. Positron annihilation characteristics in multi-wall carbon nanotubes with different average diameters

    International Nuclear Information System (INIS)

    Tuyen, L A; Khiem, D D; Phuc, P T; Kajcsos, Zs; Lázár, K; Tap, T D

    2013-01-01

    Positron lifetime spectroscopy was used to study multi-wall carbon nanotubes. The measurements were performed in vacuum on the samples having different average diameters. The positron lifetime values depend on the nanotube diameter. The results also show an influence of the nanotube diameter on the positron annihilation intensity on the nanotube surface. The change in the annihilation probability is described and interpreted by the modified diffusion model introducing the positron escape rate from the nanotubes to their external surface.

  15. Equilibrium and Thermodynamic Studies of Methane Adsorption on Multi-Walled Carbon Nanotube

    OpenAIRE

    Sanaz. Monemtabary; Mojtaba Shariati Niasar; Mohsen Jahanshahi; Ali Asghar Ghoreyshi

    2013-01-01

    In this work, The adsorption of methane onto multi-walled carbon nanotubes (MWCNTs) was studied, in which the influences of temperatureand pressure were investigated. The physical properties of the MWCNT were systematically characterised by Scanning Electron Microscopy (SEM) and Brunauere-Emmette-Teller (BET) surface area measurements. The equilibrium adsorption data were analyzed using threecommon adsorption models: Langmuir, Freundlich and Sips. All of the models fit the experimental result...

  16. Multi-walled carbon nanotube physicochemical properties predict pulmonary inflammation and genotoxicity

    DEFF Research Database (Denmark)

    Poulsen, Sarah S.; Jackson, Petra; Kling, Kirsten

    2016-01-01

    Lung deposition of multi-walled carbon nanotubes (MWCNT) induces pulmonary toxicity. Commercial MWCNT vary greatly in physicochemical properties and consequently in biological effects. To identify determinants of MWCNT-induced toxicity, we analyzed the effects of pulmonary exposure to 10 commerci...... diameter was associated with increased genotoxicity. This study provides information on possible toxicity-driving physicochemical properties of MWCNT. The results may contribute to safe-by-design manufacturing of MWCNT, thereby minimizing adverse effects....

  17. Chlorophenols Sorption on Multi-Walled Carbon Nanotubes: DFT Modeling and Structure-Property Relationship Analysis

    OpenAIRE

    Watkins, Marquita; Sizochenko, Natalia; Moore, Quentarius; Golebiowski, Marek; Leszczynska, Danuta; Leszczynski, Jerzy

    2017-01-01

    Presence of chlorophenols in drinking water could be hazardous to human health. Optimization and computational modeling of experimental conditions of adsorption lead to understanding the mechanisms of this process and to creating the efficient experimental equipment. In the current study, we investigated multi-walled carbon nanotubes by means of density functional theory (DFT) approach. This is applied to study selected types of interactions between six solvents, five types of nanotubes, and ...

  18. Selfassembly of gold nanoparticles onto the surface of multiwall carbon nanotubes functionalized with mercaptobenzene moieties

    International Nuclear Information System (INIS)

    Shi Jin; Wang Zhe; Li Hulin

    2006-01-01

    We have developed a new and effective method to robustly self-assemble gold nanoparticles onto the surface of multiwall carbon nanotubes (MWNTs) functionalized with mercaptobenzene moieties. Fourier transform infrared and electron diffraction spectroscopy were used to verify whether or not the mercaptobenzene moieties have been attached to the π-conjugated body of MWNTs. Transmission electron microscope images give direct evidences for the success of selfassembly of gold nanoparticles onto the functionalized MWNTs

  19. Supramolecular modification of multi-walled carbon nanotubes with β-cyclodextrin for better dispersibility

    International Nuclear Information System (INIS)

    He, Yi; Xu, Zhonghao; Yang, Qiangbin; Wu, Feng; Liang, Lv

    2015-01-01

    A novel hybrid material based on multi-walled carbon nanotubes was synthesized using organic synthesis, and the structures of multi-walled carbon nanotube derivatives were characterized by Fourier transform infrared spectroscopy, X-ray diffraction, thermogravimetric analysis, 1 H NMR spectroscopy, transmission electron microscopy, and scanning electron microscope. The analytical results indicated that β-cyclodextrin (β-CD) was anchored to the surface of Multi-walled carbon nanotubes (MWCNTs, OD: 10–20 nm, length: 10–30 μm) and dispersion experiments exhibited that the introduction of β-CD onto the MWCNTs would dramatically enhance the dispersion of MWCNTs in both ethanol and water media; the suspensions were found to be very stable for 2 months, and the results of this technique confirmed the experimental results. This novel technique would provide a new, simple, and facile route to prepare the modified nanomaterials based on silane-coupling agent and β-CD, and the obtained modified nanomaterials have great potential practical significance and theoretical value to develop the novel organic–inorganic hybrid material, which was very useful for water treatment and biological medicine

  20. Reinforcement of Multiwalled Carbon Nanotube in Nitrile Rubber: In Comparison with Carbon Black, Conductive Carbon Black, and Precipitated Silica

    Directory of Open Access Journals (Sweden)

    Atip Boonbumrung

    2016-01-01

    Full Text Available The properties of nitrile rubber (NBR reinforced by multiwalled carbon nanotube (MWCNT, conductive carbon black (CCB, carbon black (CB, and precipitated silica (PSi were investigated via viscoelastic behavior, bound rubber content, electrical properties, cross-link density, and mechanical properties. The filler content was varied from 0 to 15 phr. MWCNT shows the greatest magnitude of reinforcement considered in terms of tensile strength, modulus, hardness, and abrasion resistance followed by CCB, CB, and PSi. The MWCNT filled system also exhibits extremely high levels of filler network and trapped rubber even at relatively low loading (5 phr leading to high electrical properties and poor dynamic mechanical properties. Although CCB possesses the highest specific surface area, it gives lower level of filler network than MWCNT and also gives the highest elongation at break among all fillers. Both CB and PSi show comparable degree of reinforcement which is considerably lower than CCB and MWCNT.

  1. Preparation of Hydroxypropyl-β-cyclodextrin Cross-linked Multi-walled Carbon Nanotubes and Their Application in Enantioseparation of Clenbuterol

    Institute of Scientific and Technical Information of China (English)

    Yu Jingang; Huang Dushu; Huang Kelong; Hong Yong

    2011-01-01

    A method of cross-linking multi-walled carbon nanotubes by a nucleophilic substitution of brominated multi-walled carbon nanotubes using hydroxypropyl-β-cyclodextrin anions was studied. The modified multi-walled carbon nanotube samples were characterized using thermogravimetric analysis, energy-dispersive X-ray spectros-copy, transmission electron microscopy, scanning electron microscopy, Raman spectroscopy and Fourier transform infrared spectroscopy. The hydroxypropyi-β-cyclodextrin modified multi-walled carbon nanotubes were used as a chiral stationary phase additive for thin-layer chromatography to separate clenbuterol enantiomers, and the chiral separation factor was increased.

  2. Load transfer issues in the tensile and compressive behavior of multiwall carbon nanotubes

    International Nuclear Information System (INIS)

    Shen, G.A.; Namilae, S.; Chandra, N.

    2006-01-01

    Carbon nanotubes (CNT) are considered to be ultra strong and stiff reinforcements for structural composite applications. The load transfer between the inner and outer nanotubes in multiwall carbon nanotubes (MWCNT) has to be clearly understood to realize their potential in not only composites, but also other applications such as nano-springs and nano-bearings. In this paper, we study the load transfer between the walls of multiwall nanotubes both in tension and compression using molecular dynamics simulations. It is found that very minimal load is transferred to the inner nanotube during tension. The load transfer in compression of capped nanotubes is much greater than that in tension. In the case of uncapped nanotubes, the inner nanotube is deformed in bending, only after the outer nanotube is extensively deformed by buckling. It is found that the presence of a few interstitial atoms between the walls of multiwall nanotube can improve the stiffness and enhance the load transfer to the inner nanotubes both in tension and compression

  3. Unraveling the growth of vertically aligned multi-walled carbon nanotubes by chemical vapor deposition

    International Nuclear Information System (INIS)

    Ramirez, A; Royo, C; Latorre, N; Mallada, R; Monzón, A; Tiggelaar, R M

    2014-01-01

    The interaction between the main operational variables during the growth of vertically aligned multiwalled carbon nanotubes (VA-MWCNTs) by catalytic chemical vapor deposition is studied. In this contribution, we report the influence of the carbon source (i.e. acetylene, ethylene and propylene), the reaction/activation temperature, the rate of heating, the reaction time, the metal loading, and the metallic nanoparticle size and distribution on the growth and alignment of carbon nanotubes. Fe/Al thin films deposited onto silicon samples by electron-beam evaporation are used as catalyst. A phenomenological growth mechanism is proposed to explain the interaction between these multiple factors. Three different outcomes of the synthesis process are found: i) formation of forests of non-aligned, randomly oriented multi-walled carbon nanotubes, ii) growth of vertically aligned tubes with a thin and homogeneous carbonaceous layer on the top, and iii) formation of vertically aligned carbon nanotubes. This carbonaceous layer (ii) has not been reported before. The main requirements to promote vertically aligned carbon nanotube growth are determined. (paper)

  4. Binding energy and mechanical stability of single- and multi-walled carbon nanotube serpentines

    International Nuclear Information System (INIS)

    Zhao, Junhua; Lu, Lixin; Rabczuk, Timon

    2014-01-01

    Recently, Geblinger et al. [Nat. Nanotechnol. 3, 195 (2008)] and Machado et al. [Phys. Rev. Lett. 110, 105502 (2013)] reported the experimental and molecular dynamics realization of S-like shaped single-walled carbon nanotubes (CNTs), the so-called CNT serpentines. We reported here results from continuum modeling of the binding energy γ between different single- and multi-walled CNT serpentines and substrates as well as the mechanical stability of the CNT serpentine formation. The critical length for the mechanical stability and adhesion of different CNT serpentines are determined in dependence of E i I i , d, and γ, where E i I i and d are the CNT bending stiffness and distance of the CNT translation period. Our continuum model is validated by comparing its solution to full-atom molecular dynamics calculations. The derived analytical solutions are of great importance for understanding the interaction mechanism between different single- and multi-walled CNT serpentines and substrates

  5. The enhanced alcohol sensing response of multiwalled carbon nanotube networks induced by alkyl diamine treatment

    Czech Academy of Sciences Publication Activity Database

    Benlikaya, R.; Slobodian, P.; Říha, Pavel; Olejník, R.

    2014-01-01

    Roč. 201, October (2014), s. 122-130 ISSN 0925-4005 R&D Projects: GA MŠk(CZ) CZ.1.07/2.3.00/20.0104 Grant - others:UTB Zlín(CZ) IGA/FT/2013/018; GA MŠk(CZ) ED2.1.00/03.0111 Institutional research plan: CEZ:AV0Z20600510 Institutional support: RVO:67985874 Keywords : carbon nanotubes * multiwalled carbon nanotube networks * vapor sensing * linear alcohols * alkyl diamine treatment Subject RIV: BK - Fluid Dynamics Impact factor: 4.097, year: 2014

  6. Precise control of multiwall carbon nanotube diameters using thermal chemical vapor deposition

    Science.gov (United States)

    Siegal, M. P.; Overmyer, D. L.; Provencio, P. P.

    2002-03-01

    We grow multiwall carbon nanotube (CNT) films using thermal chemical vapor deposition at atmospheric pressure using a mixture of acetylene and nitrogen from a 4-nm-thick Ni film catalyst. CNTs are characterized using electron microscopy and Rutherford backscattering spectrometry. CNTs grown with this method are extremely uniform in diameter, both throughout the sample and within the lengths of individual tubes. Nanotube outer diameters, ranging from 5-350 nm, and the total deposition of carbon material, increase exponentially with growth temperature from 630 °C-790 °C.

  7. The enhanced alcohol sensing response of multiwalled carbon nanotube networks induced by alkyl diamine treatment

    Czech Academy of Sciences Publication Activity Database

    Benlikaya, R.; Slobodian, P.; Říha, Pavel; Olejník, R.

    2014-01-01

    Roč. 201, October (2014), s. 122-130 ISSN 0925-4005 R&D Projects: GA MŠk(CZ) CZ.1.07/2.3.00/20.0104 Grant - others:UTB Zlín(CZ) IGA/FT/2013/018; GA MŠk(CZ) ED2.1.00/03.0111 Institutional research plan: CEZ:AV0Z20600510 Institutional support: RVO:67985874 Keywords : carbon nanotubes * multiwalled carbon nanotube networks * vapor sensing * linear alcohol s * alkyl diamine treatment Subject RIV: BK - Fluid Dynamics Impact factor: 4.097, year: 2014

  8. The effects of liquid-phase oxidation of multiwall carbon nanotubes on their surface characteristics

    Science.gov (United States)

    Burmistrov, I. N.; Muratov, D. S.; Ilinykh, I. A.; Kolesnikov, E. A.; Godymchuk, A. Yu; Kuznetsov, D. V.

    2016-01-01

    The development of new sorbents based on nanostructured carbon materials recently became a perspective field of research. Main topic of current study is to investigate the effect of different regimes of multiwall carbon nanotubes (MWCNT) surface modification process on their structural characteristics. MWCNT samples were treated with nitric acid at high temperature. Structural properties were studied using low temperature nitrogen adsorption and acid-base back titration methods. The study showed that diluted nitric acid does not affect MWCNT structure. Concentrated nitric acid treatment leads to formation of 2.8 carboxylic groups per 1 nm2 of the sample surface.

  9. Optical and electrical characterizations of nanocomposite film of titania adsorbed onto oxidized multiwalled carbon nanotubes

    International Nuclear Information System (INIS)

    Feng Wei; Feng Yiyu; Wu Zigang; Fujii, Akihiko; Ozaki, Masanori; Yoshino, Katsumi

    2005-01-01

    Composite film containing titania electrostatically linked to oxidized multiwalled carbon nanotubes (TiO 2 -s-MWNTs) was prepared from a suspension of TiO 2 nanoparticles in soluble carbon nanotubes. The structure of the film was analysed principally by Fourier transform infrared spectroscopy, scanning electron micrography and x-ray diffraction. The optical and electrical characterizations of the film were investigated by UV-vis spectrum, photoluminescence and photoconductivity. The enhancement of photocurrent in the TiO 2 -s-MWNT film is discussed by taking the photoinduced charge transfer between the MWNT and TiO 2 into consideration

  10. Fabrication and mechanical properties of multi-walled carbon nanotubes/epoxy nanocomposites

    International Nuclear Information System (INIS)

    Yeh, M.-K.; Hsieh, T.-H.; Tai, N.-H.

    2008-01-01

    Carbon nanotubes have better physical and mechanical behavior than the traditional materials. In this study, the multi-walled carbon nanotubes (MWNTs) were added to the epoxy resin as a reinforcement to fabricate MWNTs/epoxy nanocomposites. The pressure and temperature were applied to cure the MWNTs/epoxy compound by hot press method. Mechanical properties such as tensile strength, Young's modulus, and Poisson's ratio were measured. The effect of weight percentages of the MWNTs was investigated. Morphologies of the fracture surface of MWNTs/epoxy nanocomposites were observed by scanning electron microscope

  11. Quantum oscillations and ferromagnetic hysteresis observed in iron filled multiwall carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Barzola-Quiquia, Jose; Klingner, Niko; Molle, Axel [Division of Superconductivity and Magnetism, University of Leipzig, D-04103 Leipzig (Germany); Leonhardt, Albrecht [Leibniz Institute for Solid State and Materials Research (IFW) Dresden, Helmholtzstrasse 20, 01069 Dresden (Germany)

    2011-07-01

    Carbon-based materials as multiwall carbon nanotubes (MWCNT) are attractive for spintronics because spin is only weakly coupled to the lattice, leading to large spin-flip scattering length and long spin relaxation times. In this contribution we have investigated the electrical transport properties of iron filled MWCNT (outer diameter 150 nm, inner diameter 25 nm and length 2000 nm) as a function of temperature and magnetic field. We observed quantum interference effects, i.e. universal conductance fluctuations, and weak localization effects. The in-plane magnetoresistance shows typical butterfly structure revealing the ferromagnetic properties of the Fe-filled MWCNT. The ferromagnetic hysteresis was observed up to 40K.

  12. Removal of oxidative fragments from chemically functionalized multi-walled carbon nanotubes (MWCNTs)

    International Nuclear Information System (INIS)

    Mohd Hamzah Harun; Whitby, Raymond; Khairul Zaman Dahlan; Nik Ghazali Nik Salleh; Mohd Sofian Alias; Mahathir Mohamed; Mohd Yusof Hamzah; Mohd Faizal Abdul Rahman

    2010-01-01

    Acid oxidized multi-walled carbon nano tubes (MWCNTs) were prepared by refluxing MWCNTs with nitric acid (70 %). To remove the oxidative fragment/ debris, in which partially attached onto the carbon nano tubes lattice, the functionalized MWCNTs (f-MWCNTs) then were refluxed with NaOH (1M) and followed with HCl (1M) wash. The presence of carboxylic group that covalently attached onto the MWCNTs lattice are confirmed with acid-base titration. The TEM image shows the comparison of pure MWCNTs, f-MWCNTs and base-acid wash of f-MWCNTs. (author)

  13. Parameterizing A Surface Water Model for Multiwalled Carbon Nanotubes

    Science.gov (United States)

    The unique electronic, mechanical, and structural properties of carbon nanotubes (CNTs) has lead to increasing production of these versatile materials; currently, the use of carbon-based nanomaterials in consumer products is second only to that of nano-scale silver. Although ther...

  14. Effects of nitrogen-doped multi-walled carbon nanotubes compared to pristine multi-walled carbon nanotubes on human small airway epithelial cells.

    Science.gov (United States)

    Mihalchik, Amy L; Ding, Weiqiang; Porter, Dale W; McLoughlin, Colleen; Schwegler-Berry, Diane; Sisler, Jennifer D; Stefaniak, Aleksandr B; Snyder-Talkington, Brandi N; Cruz-Silva, Rodolfo; Terrones, Mauricio; Tsuruoka, Shuji; Endo, Morinobu; Castranova, Vincent; Qian, Yong

    2015-07-03

    Nitrogen-doped multi-walled carbon nanotubes (ND-MWCNTs) are modified multi-walled carbon nanotubes (MWCNTs) with enhanced electrical properties that are used in a variety of applications, including fuel cells and sensors; however, the mode of toxic action of ND-MWCNT has yet to be fully elucidated. In the present study, we compared the interaction of ND-MWCNT or pristine MWCNT-7 with human small airway epithelial cells (SAEC) and evaluated their subsequent bioactive effects. Transmission electron microscopy, X-ray photoelectron spectroscopy, Raman spectroscopy, and X-ray diffraction suggested the presence of N-containing defects in the lattice of the nanotube. The ND-MWCNTs were determined to be 93.3% carbon, 3.8% oxygen, and 2.9% nitrogen. A dose-response cell proliferation assay showed that low doses of ND-MWCNT (1.2μg/ml) or MWCNT-7 (0.12μg/ml) increased cellular proliferation, while the highest dose of 120μg/ml of either material decreased proliferation. ND-MWCNT and MWCNT-7 appeared to interact with SAEC at 6h and were internalized by 24h. ROS were elevated at 6 and 24h in ND-MWCNT exposed cells, but only at 6h in MWCNT-7 exposed cells. Significant alterations to the cell cycle were observed in SAEC exposed to either 1.2μg/ml of ND-MWCNT or MWCNT-7 in a time and material-dependent manner, possibly suggesting potential damage or alterations to cell cycle machinery. Our results indicate that ND-MWCNT induce effects in SAEC over a time and dose-related manner which differ from MWCNT-7. Therefore, the physicochemical characteristics of the materials appear to alter their biological effects. Published by Elsevier Ireland Ltd.

  15. Fabrication And Properties Of Silver Based Multiwall Carbon Nanotube Composite Prepared By Spark Plasma Sintering Method

    Directory of Open Access Journals (Sweden)

    Lis M.

    2015-06-01

    Full Text Available The paper presents results of investigations of the obtained nanocomposite materials based on silver with addition of multiwall carbon nanotubes. The powder of carbon nanotubes content from 0.1 to 3 wt. % was produced by application of powder metallurgy methods, through mixing and high-energetic milling, and also chemical methods. Modification of carbon nanotubes included electroless deposition of silver particles on the carbon nanotube active surfaces and chemical reduction with strong reducing agent – sodium borohydride (NaBH4. The obtained powder mixtures were consolidated by SPS – Spark Plasma Sintering method. The formed composites were subjected to tests of relative density, electrical conductivity and electro-erosion properties. Detailed examinations of the structure with application of X-ray microanalysis, with consideration of carbon nanotubes distribution, were also carried out. The effect of manufacturing methods on properties of the obtained composites was observed.

  16. Cement Pastes and Mortars Containing Nitrogen-Doped and Oxygen-Functionalized Multiwalled Carbon Nanotubes

    Directory of Open Access Journals (Sweden)

    Mauricio Martínez-Alanis

    2016-01-01

    Full Text Available Cement pastes and mortars based on ordinary Portland cement containing nitrogen-doped multiwalled carbon nanotubes (MWCNT-Nx or oxygen-functionalized multiwalled carbon nanotubes (MWCNT-Ox are investigated. To incorporate MWCNTs into the cementitious matrix, the as-produced carpets are dispersed over periods of 1 and 2 hours in distilled water at pH levels of 1 and 7. The cement pastes are prepared by adding 0.1 wt% of MWCNTs to cement powder, followed by characterization with SEM and X-ray diffraction (XRD at an early age (first hours of hydration. The mortars are mechanically characterized during the hydration process for a period of 28 days. SEM characterization of cement pastes revealed that the carbon nanotubes are well incorporated in the cementitious matrix, with the hydrated cement grains interconnected by long carbon nanotubes. XRD characterizations demonstrated that, during the hydration of cement pastes, different peaks emerged that were associated with ettringite, hydrated calcium silicate, and calcium hydroxide, among other structures. Results of the compressive strength measurements for mortars simultaneously mixed with MWCNT-Nx and MWCNT-Ox reached an increment of approximately 30% in compressive strength. In addition, density functional theory calculations were performed in nitrogen-doped and oxygen-functionalized carbon nanotubes interacting with a cement grain.

  17. Multi-walled Carbon Nanotubes/Graphite Nanosheets Modified Glassy Carbon Electrode for the Simultaneous Determination of Acetaminophen and Dopamine.

    Science.gov (United States)

    Zhang, Susu; He, Ping; Zhang, Guangli; Lei, Wen; He, Huichao

    2015-01-01

    Graphite nanosheets prepared by thermal expansion and successive sonication were utilized for the construction of a multi-walled carbon nanotubes/graphite nanosheets based amperometric sensing platform to simultaneously determine acetaminophen and dopamine in the presence of ascorbic acid in physiological conditions. The synergistic effect of multi-walled carbon nanotubes and graphite nanosheets catalyzed the electrooxidation of acetaminophen and dopamine, leading to a remarkable potential difference up to 200 mV. The as-prepared modified electrode exhibited linear responses to acetaminophen and dopamine in the concentration ranges of 2.0 × 10(-6) - 2.4 × 10(-4) M (R = 0.999) and 2.0 × 10(-6) - 2.0 × 10(-4) M (R = 0.998), respectively. The detection limits were down to 2.3 × 10(-7) M for acetaminophen and 3.5 × 10(-7) M for dopamine (S/N = 3). Based on the simple preparation and prominent electrochemical properties, the obtained multi-walled carbon nanotubes/graphite nanosheets modified electrode would be a good candidate for the determination of acetaminophen and dopamine without the interference of ascorbic acid.

  18. Radical scavenging reaction kinetics with multiwalled carbon nanotubes

    NARCIS (Netherlands)

    Tsuruoka, Shuji; Matsumoto, Hidetoshi; Koyama, Kenichi; Akiba, Eiji; Yanagisawa, Takashi; Cassee, Flemming R.; Saito, Naoto; Usui, Yuki; Kobayashi, Shinsuke; Porter, Dale W.; Castranova, Vincent; Endo, Morinobu

    2015-01-01

    Progress in the development of carbon nanotubes (CNTs) has stimulated great interest among industries providing new applications. Meanwhile, toxicological evaluations on nanomaterials are advancing leading to a predictive exposure limit for CNTs, which implies the possibility of designing safer

  19. Decoration of Multi-walled Carbon Nanotubes by Metal ...

    African Journals Online (AJOL)

    NICO

    tures inside the nanotubes to increase the available surface for catalysis6 or in ... most common method to decorate CNTs by metal nanoparticles and metal oxides due .... 2.6 Characterization of Carbon Nanotubes, Metal Nano- particles and ...

  20. Eradicating group A streptococcus bacteria and biofilms using functionalised multi-wall carbon nanotubes.

    Science.gov (United States)

    Levi-Polyachenko, Nicole; Young, Christie; MacNeill, Christopher; Braden, Amy; Argenta, Louis; Reid, Sean

    2014-11-01

    The aim of this study was to demonstrate that multi-wall carbon nanotubes can be functionalised with antibodies to group A streptoccocus (GAS) for targeted photothermal ablation of planktonic and biofilm residing bacteria. Antibodies for GAS were covalently attached to carboxylated multi-wall carbon nanotubes and incubated with either planktonic or biofilm GAS. Bacterium was then exposed to 1.3 W/cm(2) of 800 nm light for 10-120 s, and then serially diluted onto agar plates from which the number of colony forming units was determined. Photothermal ablation of GAS on the surface of full thickness ex vivo porcine skin and histological sectioning were done to examine damage in adjacent tissue. Approximately 14% of the GAS antibody-functionalised nanotubes attached to the bacterium, and this amount was found to be capable of inducing photothermal ablation of GAS upon exposure to 1.3 W/cm(2) of 800 nm light. Cell viability was not decreased upon exposure to nanotubes or infrared light alone. Compared to carboxylated multi-wall carbon nanotubes, antibody-labelled nanotubes enhanced killing in both planktonic and biofilm GAS in conjunction with infrared light. Analysis of GAS photothermally ablated in direct contact with ex vivo porcine skin shows that heat sufficient for killing GAS remains localised and does not cause collateral damage in tissue adjacent to the treated area. The results of this study support the premise that carbon nanotubes may be effectively utilised as highly localised photothermal agents with the potential for translation into the clinical treatment of bacterial infections of soft tissue.

  1. Inelastic x-ray study of plasmons in oriented single and multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    Casa, D.M.; Upton, M.H.; Gog, T.; Misewich, J.; Hill, J.P.; Lowndes, D.; Eres, G.

    2006-01-01

    Carbon nanotubes (CNT) have a wide variety of interesting properties and a large number of potential aplications in electronic and optical devices. In this study we concentrate on one important aspect of their electronic stucture: the plasmon dispersions in both single- and multi-wall CNTs and their relation to those in graphite. For the first time inelastic X-ray scattering is used to study these collective electronic excitations in oriented CNT samples. The experiments were performed on the IXS instrument at beamline 9ID CMC-XOR, APS, ANL. The incident energy was defined by a Si(333) monochromator, a spherically bent Ge(733) diced analyzer at the end of a 1-m arm focused the incident radiation onto a solid-state detector. The overall resolution was ∼300 meV FWHM. The incident photons were linearly polarized perpendicular to the scattering plane. Energy loss scans were taken by varying the incident energy while keeping the exit energy fixed at 8.9805 keV. The momentum transfer was kept along the nanotubes axis. Spectra were taken at room temperature. The samples were oriented CNTs (both single- and multi-wall) grown on a Si substrate. The samples referred to as 'single-wall' were in fact a few walls at most (1-5) while the multi-walled ones had ∼12 walls. Fig. 1. shows the inelastic spectra for the single-, multi-wall, and highly oriented pyrolithic graphite (HOPG) from top to bottom. Momentum transfer was Q = 0.79 (angstrom) -1 in all cases, its direction was along the tubes for the first two samples or parallel to the sheets for graphite. The peaks at ∼10 and ∼30 eV are known as the π and σ + π plasmons respectively. Fig. 2. shows the complete dispersion curves for both plasmon modes as a function of momentum transfer for all three samples.

  2. Hematoxylin multi-wall carbon nanotubes modified glassy carbon electrode for electrocatalytic oxidation of hydrazine

    International Nuclear Information System (INIS)

    Zare, Hamid R.; Nasirizadeh, Navid

    2007-01-01

    A new hydrazine sensor has been fabricated by immobilizing hematoxylin at the surface of a glassy carbon electrode (GCE) modified with multi-wall carbon nanotube (MWCNT). The adsorbed thin films of hematoxylin on the MWCNT modified GCE show one pair of peaks with surface confined characteristics. The hematoxylin MWCNT (HMWCNT) modified GCE shows highly catalytic activity toward hydrazine electro-oxidation. The results show that the peak potential of hydrazine at HMWCNT modified GCE surface shifted by about 167 and 255 mV toward negative values compared with that at an MWCNT and activated modified GCE surface, respectively. In addition, at HMWCNT modified electrode surface remarkably improvement the sensitivity of determination of hydrazine. The kinetic parameters, such as the electron transfer coefficient, α, and the standard heterogeneous rate constant, k 0 , for oxidation of hydrazine at the HMWCNT modified GCE were determined and also is shown that the heterogeneous rate constant, k', is strongly potential dependent. The overall number of electron involved in the catalytic oxidation of hydrazine and the number of electrons involved in the rate-determining steps are 2 and 1, respectively. The amperometric detection of hydrazine is carried out at 220 mV in 0.1 M phosphate buffer solution (pH 7) with linear response range 2.0-122.8 μM hydrazine, detection limit of 0.68 μM and sensitivity of 0.0208 μA μM -1 . Finally the amperometric response for hydrazine determination is reproducible, fast and extremely stable, with no loss in sensitivity over a continual 400 s operation

  3. Effect of Novel Quercetin Titanium Dioxide-Decorated Multi-Walled Carbon Nanotubes Nanocomposite on Bacillus subtilis Biofilm Development

    DEFF Research Database (Denmark)

    Raie, Diana S; Mhatre, Eisha; El-Desouki, Doaa S

    2018-01-01

    The present work was targeted to design a surface against cell seeding and adhering of bacteria, Bacillus subtilis. A multi-walled carbon nanotube/titanium dioxide nano-power was produced via simple mixing of carbon nanotube and titanium dioxide nanoparticles during the sol-gel process followed...

  4. Properties of Retinal Precursor Cells Grown on Vertically Aligned Multiwalled Carbon Nanotubes Generated for the Modification of Retinal Implant-Embedded Microelectrode Arrays.

    Science.gov (United States)

    Johnen, Sandra; Meißner, Frank; Krug, Mario; Baltz, Thomas; Endler, Ingolf; Mokwa, Wilfried; Walter, Peter

    2016-01-01

    Background. To analyze the biocompatibility of vertically aligned multiwalled carbon nanotubes (MWCNT), used as nanomodification to optimize the properties of prostheses-embedded microelectrodes that induce electrical stimulation of surviving retinal cells. Methods. MWCNT were synthesized on silicon wafers. Their growth was achieved by iron particles (Fe) or mixtures of iron-platinum (Fe-Pt) and iron-titanium (Fe-Ti) acting as catalysts. Viability, growth, adhesion, and gene expression of L-929 and retinal precursor (R28) cells were analyzed after nondirect and direct contact. Results. Nondirect contact had almost no influence on cell growth, as measured in comparison to reference materials with defined levels of cytotoxicity. Both cell types exhibited good proliferation properties on each MWCNT-coated wafer. Viability ranged from 95.9 to 99.8%, in which better survival was observed for nonfunctionalized MWCNT generated with the Fe-Pt and Fe-Ti catalyst mixtures. R28 cells grown on the MWCNT-coated wafers showed a decreased gene expression associated with neural and glial properties. Expression of the cell cycle-related genes CCNC, MYC, and TP53 was slightly downregulated. Cultivation on plasma-treated MWCNT did not lead to additional changes. Conclusions. All tested MWCNT-covered slices showed good biocompatibility profiles, confirming that this nanotechnology is a promising tool to improve prostheses bearing electrodes which connect with retinal tissue.

  5. Properties of Retinal Precursor Cells Grown on Vertically Aligned Multiwalled Carbon Nanotubes Generated for the Modification of Retinal Implant-Embedded Microelectrode Arrays

    Directory of Open Access Journals (Sweden)

    Sandra Johnen

    2016-01-01

    Full Text Available Background. To analyze the biocompatibility of vertically aligned multiwalled carbon nanotubes (MWCNT, used as nanomodification to optimize the properties of prostheses-embedded microelectrodes that induce electrical stimulation of surviving retinal cells. Methods. MWCNT were synthesized on silicon wafers. Their growth was achieved by iron particles (Fe or mixtures of iron-platinum (Fe-Pt and iron-titanium (Fe-Ti acting as catalysts. Viability, growth, adhesion, and gene expression of L-929 and retinal precursor (R28 cells were analyzed after nondirect and direct contact. Results. Nondirect contact had almost no influence on cell growth, as measured in comparison to reference materials with defined levels of cytotoxicity. Both cell types exhibited good proliferation properties on each MWCNT-coated wafer. Viability ranged from 95.9 to 99.8%, in which better survival was observed for nonfunctionalized MWCNT generated with the Fe-Pt and Fe-Ti catalyst mixtures. R28 cells grown on the MWCNT-coated wafers showed a decreased gene expression associated with neural and glial properties. Expression of the cell cycle-related genes CCNC, MYC, and TP53 was slightly downregulated. Cultivation on plasma-treated MWCNT did not lead to additional changes. Conclusions. All tested MWCNT-covered slices showed good biocompatibility profiles, confirming that this nanotechnology is a promising tool to improve prostheses bearing electrodes which connect with retinal tissue.

  6. Facile synthesis of highly aligned multiwalled carbon nanotubes from polymer precursors.

    Energy Technology Data Exchange (ETDEWEB)

    Han, C. Y.; Xiao, Z.-L.; Wang, H. H.; Lin, X.-M.; Trasobares, S.; Cook, R. E.; Richard J. Daley Coll.; Northern Illinois Univ.; Univ. de Cadiz

    2009-01-01

    We report a facile one-step approach which involves no flammable gas, no catalyst, and no in situ polymerization for the preparation of well-aligned carbon nanotube array. A polymer precursor is placed on top of an anodized aluminum oxide (AAO) membrane containing regular nanopore arrays, and slow heating under Ar flow allows the molten polymer to wet the template through adhesive force. The polymer spread into the nanopores of the template to form polymer nanotubes. Upon carbonization the resulting multi-walled carbon nanotubes duplicate the nanopores morphology precisely. The process is demonstrated for 230, 50, and 20 nm pore membranes. The synthesized carbon nanotubes are characterized with scanning/transmission electron microscopies, Raman spectroscopy, and resistive measurements. Convenient functionalization of the nanotubes with this method is demonstrated through premixing CoPt nanoparticles in the polymer precursors.

  7. Field emission response from multi-walled carbon nanotubes grown on electrochemically engineered copper foil

    Energy Technology Data Exchange (ETDEWEB)

    Tripathi, Amit Kumar; Jain, Vaibhav [Nanomaterials and Applications Lab., Department of Metallurgical and Materials Engineering, Indian Institute of Technology Roorkee, Roorkee, 247667, Uttarakhand (India); Saini, Krishna [Nanomaterials and Applications Lab., Department of Metallurgical and Materials Engineering, Indian Institute of Technology Roorkee, Roorkee, 247667, Uttarakhand (India); Centre of Excellence: Nanotechnology, Indian Institute of Technology Roorkee, Roorkee, 247667, Uttarakhand (India); Lahiri, Indranil, E-mail: indrafmt@iitr.ac.in [Nanomaterials and Applications Lab., Department of Metallurgical and Materials Engineering, Indian Institute of Technology Roorkee, Roorkee, 247667, Uttarakhand (India); Centre of Excellence: Nanotechnology, Indian Institute of Technology Roorkee, Roorkee, 247667, Uttarakhand (India)

    2017-02-01

    Exciting properties of carbon nanotube has proven it to be a promising candidate for field emission applications, if its processing cost can be reduced effectively. In this research, a new electrochemical technique is proposed for growing carbon nanotubes in selective areas by thermal chemical vapour deposition. In this process, electrochemical processing is used to create localized pits and deposition of catalysts, which act as roots to support growth and alignment of the CNTs on copper substrate. CNTs grown thus were characterized and studied using scanning electron microscope, transmission electron microscope and Raman spectroscopy, elucidating presence of multiwall carbon nanotubes (MWCNT). These CNT emitters have comparatively lower turn-on field and higher field enhancement factor. - Highlights: • Electrochemical pitting for localized carbon nanotube growth is proposed. • Electrochemical pitting method shows patterning effect on the substrate. • Size and density of pits depend on voltage, pH and temperature. • CNTs thus grown shows good field emission response.

  8. Facile Synthesis of Highly Aligned Multiwalled Carbon Nanotubes from Polymer Precursors

    Directory of Open Access Journals (Sweden)

    Catherine Y. Han

    2009-01-01

    Full Text Available We report a facile one-step approach which involves no flammable gas, no catalyst, and no in situ polymerization for the preparation of well-aligned carbon nanotube array. A polymer precursor is placed on top of an anodized aluminum oxide (AAO membrane containing regular nanopore arrays, and slow heating under Ar flow allows the molten polymer to wet the template through adhesive force. The polymer spread into the nanopores of the template to form polymer nanotubes. Upon carbonization the resulting multi-walled carbon nanotubes duplicate the nanopores morphology precisely. The process is demonstrated for 230, 50, and 20 nm pore membranes. The synthesized carbon nanotubes are characterized with scanning/transmission electron microscopies, Raman spectroscopy, and resistive measurements. Convenient functionalization of the nanotubes with this method is demonstrated through premixing CoPt nanoparticles in the polymer precursors.

  9. Radiation damage to multi-walled carbon nanotubes and their ...

    Indian Academy of Sciences (India)

    Since their discovery in 1991 by Iijima, carbon nanotubes (CNTs) have been of great interest, both from a fundamental point of view and for future applications. As recent experimental and theoretical studies demonstrate, irradiation of CNTs with energetic particles can successfully be used for nano-engineering, e.g., ...

  10. Improved covalent functionalization of multi-walled carbon ...

    Indian Academy of Sciences (India)

    Carbon nanotubes (CNTs) play a fundamental role in the rapidly developing .... using field emission scanning electron microscopy (FE-. SEM). The images ..... The limiting oxygen index (LOI) is the minimum concen- tration of oxygen that .... Chem. Lett. 22 185. [19] Mallakpour S and Zadehnazari A 2014 J. Solid State Chem.

  11. Improved field emission properties of thiolated multi-wall carbon nanotubes on a flexible carbon cloth substrate

    International Nuclear Information System (INIS)

    Chuang, F T; Chen, P Y; Cheng, T C; Chien, C H; Li, B J

    2007-01-01

    In this paper we report the observation of enhanced field emission properties from thiolated multi-wall carbon nanotubes (MWCNTs) produced by a simple and effective two-step chemical surface modification technique. This technique implements carboxylation and thiolation on the MWCNTs synthesized by microwave plasma chemical vapor deposition (MPCVD) on the flexible carbon cloth substrate. The resulting thiolated MWCNTs were found to have a very low threshold field value of 1.25 V μm -1 and a rather high field enhancement factor of 1.93 x 10 4 , which are crucial for applications in versatile vacuum microelectronics

  12. Time-resolved laser-induced incandescence from multiwalled carbon nanotubes in air

    Energy Technology Data Exchange (ETDEWEB)

    Mitrani, J. M. [Princeton Plasma Physics Laboratory, Princeton, New Jersey 08540, USA; Shneider, M. N. [Department of Mechanical Engineering, Princeton University, Princeton, New Jersey 08544, USA

    2015-01-26

    We observed temporal laser-induced incandescence (LII) signals from multiwalled carbon nanotubes(MWCNTs) suspended in ambient air. Unlike previous LII experiments with soot particles, which showed that primary particles with larger diameters cool at slower timescales relative to smaller particles, we observed that thicker MWCNTs with larger outer diameters (ODs) cool at faster timescales relative to thinner MWCNTs with smaller ODs. We suggested a simple explanation of this effect, based on the solution of one-dimensional nonstationary heat conduction equation for the initial non-uniform heating of MWCNTs with ODs greater than the skin depth.

  13. Mild hydrothermal treatment to prepare highly dispersed multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    Zhang Li; Hashimoto, Yoshio; Taishi, Toshinori; Ni Qingqing

    2011-01-01

    Multi-walled carbon nanotubes (MWCNTs) with improved dispersion property have been prepared by a mild and fast hydrothermal treatment. The hydrothermal process avoids using harsh oxidants and organic solvents, which is environmental friendly and greatly decreases the damage to intrinsic structure of MWCNTs. The modified MWCNTs were highly soluble in polar solvents such as water, ethanol and dimethylformamide. Morphological observation by TEM indicated that the diameter and inherent structure were well reserved in modified MWCNTs. X-ray photoelectron spectroscopy and Raman spectroscopy were used to quantify functional groups created on the MWCNT surface, and to determine rational parameters of hydrothermal process.

  14. Breakdown voltage reduction by field emission in multi-walled carbon nanotubes based ionization gas sensor

    Energy Technology Data Exchange (ETDEWEB)

    Saheed, M. Shuaib M.; Muti Mohamed, Norani; Arif Burhanudin, Zainal, E-mail: zainabh@petronas.com.my [Centre of Innovative Nanostructures and Nanodevices, Universiti Teknologi PETRONAS, Bandar Seri Iskandar, 31750 Tronoh, Perak (Malaysia)

    2014-03-24

    Ionization gas sensors using vertically aligned multi-wall carbon nanotubes (MWCNT) are demonstrated. The sharp tips of the nanotubes generate large non-uniform electric fields at relatively low applied voltage. The enhancement of the electric field results in field emission of electrons that dominates the breakdown mechanism in gas sensor with gap spacing below 14 μm. More than 90% reduction in breakdown voltage is observed for sensors with MWCNT and 7 μm gap spacing. Transition of breakdown mechanism, dominated by avalanche electrons to field emission electrons, as decreasing gap spacing is also observed and discussed.

  15. Growth of apatite on chitosan-multiwall carbon nanotube composite membranes

    Energy Technology Data Exchange (ETDEWEB)

    Yang Jun; Yao Zhiwen [State Key Laboratory of Oral Diseases, West China College of Stomatology, Sichuan University, No 14, 3rd Section South People' s Road, Chengdu 610041 (China); Tang Changyu [Department of Polymer Science and Materials, Sichuan University (China); Darvell, B.W. [Dental Materials Science, Faculty of Dentistry, University of Hong Kong (Hong Kong); Zhang Hualin; Pan Lingzhan; Liu Jingsong [State Key Laboratory of Oral Diseases, West China College of Stomatology, Sichuan University, No 14, 3rd Section South People' s Road, Chengdu 610041 (China); Chen Zhiqing, E-mail: yangj0710@gmail.com [State Key Laboratory of Oral Diseases, West China College of Stomatology, Sichuan University, No 14, 3rd Section South People' s Road, Chengdu 610041 (China)

    2009-07-30

    Bioactive membranes for guided tissue regeneration would be of value for periodontal therapy. Chitosan-multiwall carbon nanotube (CS-MWNT) composites were treated to deposit nanoscopic apatite for MWNT proportions of 0-4 mass%. Fourier-transform infrared spectroscopy, scanning electron microscopy, energy-dispersive X-ray analysis, and X-ray diffraction were used for characterization. Apatite was formed on the CS-MWNT composites at low MWNT concentrations, but the dispersion of the MWNT affects the crystallite size and the Ca/P molar ratio of the composite. The smallest crystallite size was 9 nm at 1 mass% MWNT.

  16. Controlling the site density of multiwall carbon nanotubes via growth conditions

    Science.gov (United States)

    Siegal, M. P.; Overmyer, D. L.; Kaatz, F. H.

    2004-06-01

    We present two complementary methods for controlling the site density of multiwall carbon nanotubes (CNTs) directly as a function of growth conditions from 1011to107CNTs/cm2. Several potential applications require significant spacing between individual CNTs. The first method shows that the site density varies with the heat of formation of the hydrocarbon gas used during CNT growth by thermal chemical vapor deposition. The second method demonstrates that the site density decreases with increasing residual stress of the metal catalyst/diffusion barrier layers. These methods are combined for wide-range control of CNT site density.

  17. Defect evolution in multiwalled carbon nanotube films irradiated by Ar ions

    International Nuclear Information System (INIS)

    Honda, Shin-ichi; Nanba, Shuhei; Hasegawa, Yoichi

    2012-01-01

    Controlling defect structure in multiwalled carbon nanotube (MWCNT) is essential to realization of MWCNT devices. Here, we show that the diagram of the Raman intensity ratio of the G to D peaks and the G peak width can reveal two damaging stages of MWCNT films. In a transition period, additional peaks appeared in the X-ray absorption spectra, thereby indicating some significant change in the electronic structure. Also, a remarkable increase occurred in the diameter of the MWCNTs in the latter stage, suggesting the formation of dislocation dipoles which may relate to the change in the properties of field-emission devices. (author)

  18. Multiwalled carbon nanotubes sensor for organic liquid detection at room temperature

    Science.gov (United States)

    Chaudhary, Deepti; Khare, Neeraj; Vankar, V. D.

    2016-04-01

    We have explored the possibility of using multiwalled carbon nanotubes (MWCNTs) as room temperature chemical sensor for the detection of organic liquids such as ethanol, propanol, methanol and toluene. MWCNTs were synthesized by thermal chemical vapor deposition (TCVD) technique. The interdigitated electrodes were fabricated by conventional photolithography technique. The sensor was fabricated by drop depositing MWCNT suspension onto the interdigitated electrodes. The sensing properties of MWCNTs sensor was studied for organic liquids detection. The resistance of sensor was found to increase upon exposure to these liquids. Sensor shows good reversibility and fast response at room temperature. Charge transfer between the organic liquid and sensing element is the dominant sensing mechanism.

  19. Immobilization of cross-linked tannase enzyme on multiwalled carbon nanotubes and its catalytic behavior.

    Science.gov (United States)

    Ong, Chong-Boon; Annuar, Mohamad S M

    2018-02-07

    Immobilization of cross-linked tannase on pristine multiwalled carbon nanotubes (MWCNT) was successfully performed. Cross-linking of tannase molecules was made through glutaraldehyde. The immobilized tannase exhibited significantly improved pH, thermal, and recycling stability. The optimal pH for both free and immobilized tannase was observed at pH 5.0 with optimal operating temperature at 30°C. Moreover, immobilized enzyme retained greater biocatalytic activities upon 10 repeated uses compared to free enzyme in solution. Immobilization of tannase was accomplished by strong hydrophobic interaction most likely between hydrophobic amino acid moieties of the glutaraldehyde-cross-linked tannase to the MWCNT.

  20. High performance dye-sensitized solar cell based on hydrothermally deposited multiwall carbon nanotube counter electrode

    Science.gov (United States)

    Siriroj, Sumeth; Pimanpang, Samuk; Towannang, Madsakorn; Maiaugree, Wasan; Phumying, Santi; Jarernboon, Wirat; Amornkitbamrung, Vittaya

    2012-06-01

    Conductive glass was coated with multiwall carbon nanotubes (MWCNTs) by a hydrothermal method. MWCNTs films were subsequently used as dye-sensitized solar cell (DSSC) counter electrodes. The performance of hydrothermal MWCNT DSSC was ˜2.37%. After film annealing in an Ar atmosphere, annealed-hydrothermal MWCNT (AHT-CNT) DSSC efficiency was significantly increased to ˜7.66%, in comparison to ˜8.01% for sputtered-Pt DSSC. Improvement of AHT-CNT DSSC performance is attributed to a decrease in charge-transfer resistance from 1500 Ω to 30 Ω as observed by electrochemical impedance spectroscopy.

  1. p-doped multiwall carbon nanotube/perylene diimide derivative photoelectrochemical cells for photocurrent generation

    Energy Technology Data Exchange (ETDEWEB)

    Troeger, Anna; Ledendecker, Marc; Margraf, Johannes T.; Sgobba, Vito; Guldi, Dirk M. [Department of Chemistry and Pharmacy and Interdisciplinary Center for Molecular Materials, Friedrich Alexander University Erlangen-Nuremberg, Erlangen (Germany); Vieweg, Benito F.; Spiecker, Erdmann [Center for Nanoanalysis and Electron Microscopy (CENEM) and Department Werkstoffwissenschaften/VII, Friedrich Alexander University Erlangen-Nuremberg, Erlangen (Germany); Suraru, Sabin-Lucian; Wuerthner, Frank [Institut fuer Organische Chemie and Roentgen Research Center for Complex Material Systems, Universitaet Wuerzburg, Wuerzburg (Germany)

    2012-05-15

    A perylene diimide (PDI) derivative bearing four chlorine substituents in the bay area is deposited together with pristine multiwall carbon nanotubes (MWNTs) and/or Nafion p-doped MWNTs (p-MWNTs) onto indium tin oxide (ITO) solid substrates by means of air-brushing. The resulting photoanodes are studied in photoelectrochemical cells and reveal highest photocurrent efficiencies when PDI and p-MWNT are combined as photoactive materials, indicating the beneficial effect of Nafion. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  2. Dielectric behaviour of the composite system: multiwall carbon nanotubes dispersed in ferroelectric liquid crystalline material

    Czech Academy of Sciences Publication Activity Database

    Shukla, R.K.; Raina, K.K.; Hamplová, Věra; Kašpar, Miroslav; Bubnov, Alexej

    2011-01-01

    Roč. 84, 9-10 (2011), 850-857 ISSN 0141-1594 R&D Projects: GA AV ČR IAA100100911; GA AV ČR(CZ) GA202/09/0047; GA ČR(CZ) GAP204/11/0723 Grant - others:RFASI(RU) 02.740.11.5166 Institutional research plan: CEZ:AV0Z10100520 Keywords : ferroelectric liquid crystal * multiwall carbon nanotube * composite * mesomorphic property * dielectric spectroscopy Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.006, year: 2011

  3. Metal octacarboxyphthalocyanine / multi-walled carbon nanotube hybrid for the development of dye solar cells

    CSIR Research Space (South Africa)

    Mphahlele, N

    2013-09-01

    Full Text Available overall efficiencies even though it was lower than unexpected. Nevertheless, the TiO2/ZnOCPc/MWCNT performed better with the efficiency of about 0.1% than TiO2/SiOCPc/MWCNT and TiO2/GaOCPc/MWCNT. These findings open up avenues for improving... Conditions 50 3.3 FUNCTIONALISATION OF MULTI-WALLED CARBON NANOTUBES 51 3.4 PURIFICATION AND OXIDATION OF MWCNT 51 3.4.1 Amine-Functionalised MWCNT 52 3.5 SYTHESIS OF METAL 2,3,9,10,16,17,23,24 OCTACARBOXYPHTHALOCYANINES 52 3.5.1 Synthesis...

  4. Feasibility of multi-walled carbon nanotube probes in AFM anodization lithography

    International Nuclear Information System (INIS)

    Choi, Ji Sun; Bae, Sukjong; Ahn, Sang Jung; Kim, Dal Hyun; Jung, Ki Young; Han, Cheolsu; Chung, Chung Choo; Lee, Haiwon

    2007-01-01

    Multi-walled carbon nanotube (CNT) tips were used in atomic force microscope (AFM) anodization lithography to investigate their advantages over conventional tips. The CNT tip required a larger threshold voltage than the mother silicon tip due to the Schottky barrier at the CNT-Si interface. Current-to-voltage curves distinguished the junction property between CNTs and mother tips. The CNT-platinum tip, which is more conductive than the CNT-silicon tip, showed promising results for AFM anodization lithography. Finally, the nanostructures with high aspect ratio were fabricated using a pulsed bias voltage technique as well as the CNT tip

  5. Biofunctionalization of multiwalled carbon nanotubes by electropolymerized poly(pyrrole-concanavalin A) films.

    Science.gov (United States)

    Papper, Vladislav; Elouarzaki, Kamal; Gorgy, Karine; Sukharaharja, Ayrine; Cosnier, Serge; Marks, Robert S

    2014-10-13

    The synthesis and electropolymerization of a pyrrolic concanavalin A derivative (pyrrole-Con A) onto a multiwalled carbon nanotube (MWCNT) deposit is reported. Glucose oxidase was then immobilized onto the MWCNT-poly(pyrrole-Con A) coating by affinity carbohydrate interactions with the polymerized Con A protein. The resulting enzyme electrode was applied to the amperometric detection of glucose exhibiting a high sensitivity of 36 mA cm(-2) mol(-1) L and a maximum current density of 350 μA cm(-2) . © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  6. Effects of phonon dimensionality in the specific heat of multiwall carbon nanotubes at low temperatures

    International Nuclear Information System (INIS)

    Jorge, Guillermo A; Bekeris, V; Acha, C; Escobar, M M; Goyanes, S; Zilli, D; Cukierman, A L; Candal, R J

    2009-01-01

    We have measured the specific heat at constant pressure, C p , of three different samples of multiwall carbon nanotubes (MWNT). For all samples, C p departs from a graphitic behavior at T p measurements show a temperature threshold from a linear regime for intermediate temperature to a higher-order power law for low temperatures. Moreover, it was found that this crossover only depends on the internal structure of the individual MWNT and not on the spatial order of the MWNT within a bundle.

  7. Synthesis of multi-walled carbon nanotubes and their application in resin based nanocomposites

    International Nuclear Information System (INIS)

    Ahmad, Shahid Nisar; Hakeem, Saira; Alvi, Rashid Ahmed; Farooq, Khawar; Farooq, Naveed; Yasmin, Farida; Saeed, Sadaf

    2013-01-01

    Multi-walled carbon nanotubes (MWCNTs) were synthesized by catalytic decomposition of hydrocarbon gas using chemical vapor deposition method. Synthesis was done at different growth temperatures and catalyst ratios. These MWCNTs were dispersed in epoxy resin (E-51) and their effect on mechanical strength of epoxy nanocomposites was studied. Increase in the mechanical strength of epoxy was observed with the addition of CNTs. The surface characterization was done by using optical microscope and scanning electron microscope (SEM). Mechanical properties were determined by the general tensile strength testing method.

  8. Plasma treatment of multiwall carbon nanotubes for dispersion improvement in water

    International Nuclear Information System (INIS)

    Chen Changlun; Ogino, Akihisa; Nagatsu, Masaaki; Wang Xiangke

    2010-01-01

    Microwave excited Ar/H 2 O surface-wave plasma was used to treat multiwall carbon nanotubes (MWCNTs) to modify their surface characteristics and thus improve their dispersion capability in water. Changes in the atom composition and structure properties of MWCNTs were analyzed using x-ray photoelectron spectroscopy and Raman spectroscopy, and the surface morphology of MWCNTs was observed by field emission scanning electron microscopy and scanning transmission electron microscopy. The results indicated that Ar/H 2 O plasma treatment greatly enhanced the content of oxygen, and modified surface microstructure properties. The integrity of nanotube patterns, however, was not damaged.

  9. Long-term hepatotoxicity of polyethylene-glycol functionalized multi-walled carbon nanotubes in mice

    Science.gov (United States)

    Zhang, Danying; Deng, Xiaoyong; Ji, Zongfei; Shen, Xizhong; Dong, Ling; Wu, Minghong; Gu, Taoying; Liu, Yuanfang

    2010-04-01

    The toxicity of polyethylene-glycol functionalized (PEGylated) multi-walled carbon nanotubes (MWCNTs) and non-PEGylated MWCNTs in vivo was evaluated and compared. Mice were exposed to MWCNTs by intravenous injection. The activity level of glutathione, superoxide dismutase and gene expression in liver, as well as some biochemical parameters and the tumor necrosis factor alpha level in blood were measured over 2 months. The pathological and electron micrographic observations of liver evidently indicate that the damage caused by non-PEGylated MWCNTs is slightly more severe than that of PEGylated MWCNTs, which means that PEGylation can partly, but not substantially, improve the in vivo biocompatibility of MWCNTs.

  10. Effects of phonon dimensionality in the specific heat of multiwall carbon nanotubes at low temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Jorge, Guillermo A; Bekeris, V; Acha, C [Laboratorio de Bajas Temperaturas, Departamento de Fisica, FCEyN-UBA, Pab. 1, Ciudad Universitaria (1428), Buenos Aires (Argentina); Escobar, M M; Goyanes, S [Laboratorio de Polimeros y Materiales Compuestos, Departamento de Fisica, FCEyN-UBA, Pab. 1, Ciudad Universitaria (1428), Buenos Aires (Argentina); Zilli, D; Cukierman, A L [PINMATE, Departamento de Industrias, FCEyN-UBA, Pab. Industrias, Ciudad Universitaria (1428), Buenos Aires (Argentina); Candal, R J, E-mail: gjorge@df.uba.a [Instituto de Fisicoquimica de Materiales, Ambiente y EnergIa, CONICET-UBA, Ciudad Universitaria (1428) Buenos Aires (Argentina)

    2009-05-01

    We have measured the specific heat at constant pressure, C{sub p}, of three different samples of multiwall carbon nanotubes (MWNT). For all samples, C{sub p} departs from a graphitic behavior at T < 120 K. C{sub p} measurements show a temperature threshold from a linear regime for intermediate temperature to a higher-order power law for low temperatures. Moreover, it was found that this crossover only depends on the internal structure of the individual MWNT and not on the spatial order of the MWNT within a bundle.

  11. Viscoelastic behavior of multiwalled carbon nanotubes into phenolic resin

    Energy Technology Data Exchange (ETDEWEB)

    Botelho, Edson Cocchieri; Costa, Michelle Leali; Braga, Carlos Isidoro, E-mail: ebotelho@feg.unesp.br [Universidade Estadual Paulista Julio de Mesquita Filho (UNESP), Guaratingueta, SP (Brazil). Dept. de Materiais e Tecnologia; Burkhart, Thomas [Institut fuer Verbundwerkstoffe GmbH, Kaiserslautern, (Germany); Lauke, Bernd [Leibniz-Institut fuer Polymerforschung, Dresden (Germany)

    2013-11-01

    Nanostructured polymer composites have opened up new perspectives for multi-functional materials. In particular, carbon nanotubes (CNTs) have the potential applications in order to improve mechanical and electrical performance in composites with aerospace application. This study focuses on the viscoelastic evaluation of phenolic resin reinforced carbon nanotubes, processed by using two techniques: aqueous-surfactant solution and three roll calender (TRC) process. According to our results a relative small amount of CNTs in a phenolic resin matrix is capable of enhancing the viscoelastic properties significantly and to modify the thermal stability. Also has been observed that when is used TRC process, the incorporation and distribution of CNT into phenolic resin is more effective when compared with aqueous solution dispersion process. (author)

  12. Interlaminar Fracture Toughness of CFRP Laminates Incorporating Multi-Walled Carbon Nanotubes

    Directory of Open Access Journals (Sweden)

    Elisa Borowski

    2015-06-01

    Full Text Available Carbon fiber reinforced polymer (CFRP laminates exhibit limited fracture toughness due to characteristic interlaminar fiber-matrix cracking and delamination. In this article, we demonstrate that the fracture toughness of CFRP laminates can be improved by the addition of multi-walled carbon nanotubes (MWCNTs. Experimental investigations and numerical modeling were performed to determine the effects of using MWCNTs in CFRP laminates. The CFRP specimens were produced using an epoxy nanocomposite matrix reinforced with carboxyl functionalized multi-walled carbon nanotubes (COOH–MWCNTs. Four MWCNTs contents of 0.0%, 0.5%, 1.0%, and 1.5% per weight of the epoxy resin/hardener mixture were examined. Double cantilever beam (DCB tests were performed to determine the mode I interlaminar fracture toughness of the unidirectional CFRP composites. This composite material property was quantified using the critical energy release rate, GIC. The experimental results show a 25%, 20%, and 17% increase in the maximum interlaminar fracture toughness of the CFRP composites with the addition of 0.5, 1.0, and 1.5 wt% MWCNTs, respectively. Microstructural investigations using Fourier transform infrared (FTIR spectroscopy and X-ray photoelectron spectroscopy (XPS verify that chemical reactions took place between the COOH–MWCNTs and the epoxy resin, supporting the improvements experimentally observed in the interlaminar fracture toughness of the CFRP specimens containing MWCNTs. Finite element (FE simulations show good agreement with the experimental results and confirm the significant effect of MWCNTs on the interlaminar fracture toughness of CFRP.

  13. Removal of heavy metal ions from wastewaters using dendrimer-functionalized multi-walled carbon nanotubes.

    Science.gov (United States)

    Iannazzo, Daniela; Pistone, Alessandro; Ziccarelli, Ida; Espro, Claudia; Galvagno, Signorino; Giofré, Salvatore V; Romeo, Roberto; Cicero, Nicola; Bua, Giuseppe D; Lanza, Giuseppe; Legnani, Laura; Chiacchio, Maria A

    2017-06-01

    Dendrimer-functionalized multi-walled carbon nanotubes (MWCNT) for heavy metal ion removal from wastewaters were developed. Triazole dendrimers (TD) were built directly onto the carbon nanotube surface by successive click chemistry reactions affording the zero- and first-generation dendrimer-functionalized MWCNT (MWCNT-TD1 and MWCNT-TD2). The Moedritzer-Irani reaction carried out on the amino groups present on the MWCNT-TD2 sample gave the corresponding α-aminophosphonate nanosystem MWCNT-TD2P. Both MWCNT-TD2 and MWCNT-TD2P nanosystems have been characterized by physical, chemical, and morphological analyses. Their chelating abilities towards the toxic metal ions Pb 2+ , Hg 2+ , and Ni 2+ and the harmless Ca 2+ ion have been experimentally evaluated in the two different sets of experiments and at the salt concentrations of 1 mg/mL or 1 μg/mL by inductively coupled plasma mass spectrometry (ICP-MS). The results of these studies pointed out the interesting chelating behavior for the phosphonated nanosystem towards the Hg 2+ ion. The complexation mode of the best chelating system MWCNT-TD2P with mercury was investigated through density functional theory (DFT) calculations, suggesting a chelation mechanism involving the two oxygen atoms of the phosphate group. The synthesized dendrimers, supported on the multi-walled carbon nanotubes, have shown the potential to be used for the selective toxic metal ion removal and recovery.

  14. Transport comparison of multiwall carbon nanotubes by contacting outer shell and all shells.

    Science.gov (United States)

    Luo, Qiang; Cui, A-Juan; Zhang, Yi-Guang; Lu, Chao; Jin, Ai-Zi; Yang, Hai-Fang; Gu, Chang-Zhi

    2010-11-01

    Carbon nanotubes, particularly multiwall carbon nanotubes (MWCNTs) can serve as interconnects in nanoelectronic devices and integrated circuits because of their extremely large current-carrying capacity. Many experimental results about the transport properties of individual MWCNTs by contacting outer shell or all shells have been reported. In this work, a compatible method with integrated circuit manufacturing process was presented to compare the transport property of an individual multiwall carbon nanotube (MWCNT) by contacting outer shell only and all shells successively. First of the Ti/Au electrodes contacting outer shell only were fabricated onto the nanotube through the sequence of electron beam lithography (EBL) patterning, metal deposition and lift-off process. After the characterization of its transport property, focused ion beam (FIB) was used to drill holes through the same nanotube at the as-deposited electrodes. Then new contact to the holes and electrodes were made by ion-induced deposition of tungsten from W(CO)6 precursor gas. The transport results indicated that the new contact to all shells can clear up the intershell resistance and the electrical conductance of the tube can be improved about 8 times compared to that of by contacting outer shell only.

  15. Mechanical properties of multi-walled carbon nanotube/epoxy polysulfide nanocomposite

    International Nuclear Information System (INIS)

    Shirkavand Hadavand, Behzad; Mahdavi Javid, Kimya; Gharagozlou, Mehrnaz

    2013-01-01

    Highlights: ► Preparation of epoxy polysulfide nanocomposite. ► Multi-walled carbon nanotubes have been modified and dispersed in epoxy polysulfide matrix. ► Mechanical properties of MWNT/epoxy polysulfide have been studied. - Abstract: In this research, multi-walled carbon nanotubes (MWCNTs) were modified by acid functionalization (H 2 SO 4 :HNO 3 = 1:3 by volume) and then mechanical properties of reinforced epoxy polysulfide resin by the both pure and treated MWNTs have been evaluated. For achieving this goal, different weight percentages of pure and treated MWCNT (0.1–0.3 wt%) were dispersed in the epoxy polysulfide resin separately and then mixed with curing agent. Experimental results have shown significant difference between acid treated and untreated MWCNTs in mechanical properties of epoxy polysulfide nanocomposites. In nanocomposite with 0.1–0.3% acid treated MWCNTs we observed increase of Young’s modulus from 458 to 723 MPa, tensile strength from 5.29 to 8.83 MPa and fracture strain from 0.16% to 0.25%. For understanding the structure and morphology of nanocomposite, the dispersion states were studied using scanning electron microscopy (SEM) and field emission electron microscopy (FESEM). The results showed better dispersion of modified carbon nanotube than unmodified in polymeric matrix

  16. Single- and Multiwalled Carbon Nanotubes with Phosphorus Based Flame Retardants for Textiles

    Directory of Open Access Journals (Sweden)

    D. Wesolek

    2014-01-01

    Full Text Available Due to growing popularity of composites, modification methods to obtain the best properties are searched for. The aim of the study is to reduce the flammability of textile materials using nanocomposite polymer back-coating. Different types of carbon nanotubes (single- and multiwalled and different phosphorus flame retardants (ammonium polyphosphates and melamine polyphosphate were introduced into the resin and then the fabrics were covered by the obtained composites. Homogeneous dispersion of multiwalled carbon nanotubes in the polyurethane resin was obtained by sonification, which was confirmed by scanning electron microscopy. Flammability tests of fabrics coated by modified polyurethane resin were carried out using pyrolysis combustion flow calorimeter (PCFC and thermal stability of textiles was evaluated. Also, organoleptic estimation of coatings was conducted (flexibility and fragility. The use of polymer nanocomposites with phophorus flame retardants as a back-coating for textiles effectively reduces flammability and improves thermal stability of the fabric. Furthermore, the synergistic effect beetwen carbon nanotubes and phosphorous compound occurs. The resulting coatings are flexible and do not crack or change the feel of fabrics.

  17. Comparative inhalation toxicity of multi-wall carbon nanotubes, graphene, graphite nanoplatelets and low surface carbon black.

    Science.gov (United States)

    Ma-Hock, Lan; Strauss, Volker; Treumann, Silke; Küttler, Karin; Wohlleben, Wendel; Hofmann, Thomas; Gröters, Sibylle; Wiench, Karin; van Ravenzwaay, Bennard; Landsiedel, Robert

    2013-06-17

    Carbon nanotubes, graphene, graphite nanoplatelets and carbon black are seemingly chemically identical carbon-based nano-materials with broad technological applications. Carbon nanotubes and carbon black possess different inhalation toxicities, whereas little is known about graphene and graphite nanoplatelets. In order to compare the inhalation toxicity of the mentioned carbon-based nanomaterials, male Wistar rats were exposed head-nose to atmospheres of the respective materials for 6 hours per day on 5 consecutive days. Target concentrations were 0.1, 0.5, or 2.5 mg/m3 for multi-wall carbon nanotubes and 0.5, 2.5, or 10 mg/m3 for graphene, graphite nanoplatelets and low-surface carbon black. Toxicity was determined after end of exposure and after three-week recovery using broncho-alveolar lavage fluid and microscopic examinations of the entire respiratory tract. No adverse effects were observed after inhalation exposure to 10 mg/m3 graphite nanoplatelets or relatively low specific surface area carbon black. Increases of lavage markers indicative for inflammatory processes started at exposure concentration of 0.5 mg/m3 for multi-wall carbon nanotubes and 10 mg/m3 for graphene. Consistent with the changes in lavage fluid, microgranulomas were observed at 2.5 mg/m3 multi-wall carbon nanotubes and 10 mg/m3 graphene. In order to evaluate volumetric loading of the lung as the key parameter driving the toxicity, deposited particle volume was calculated, taking into account different methods to determine the agglomerate density. However, the calculated volumetric load did not correlate to the toxicity, nor did the particle surface burden of the lung. The inhalation toxicity of the investigated carbon-based materials is likely to be a complex interaction of several parameters. Until the properties which govern the toxicity are identified, testing by short-term inhalation is the best option to identify hazardous properties in order to avoid unsafe applications or select

  18. Comparative inhalation toxicity of multi-wall carbon nanotubes, graphene, graphite nanoplatelets and low surface carbon black

    Science.gov (United States)

    2013-01-01

    Background Carbon nanotubes, graphene, graphite nanoplatelets and carbon black are seemingly chemically identical carbon-based nano-materials with broad technological applications. Carbon nanotubes and carbon black possess different inhalation toxicities, whereas little is known about graphene and graphite nanoplatelets. Methods In order to compare the inhalation toxicity of the mentioned carbon-based nanomaterials, male Wistar rats were exposed head-nose to atmospheres of the respective materials for 6 hours per day on 5 consecutive days. Target concentrations were 0.1, 0.5, or 2.5 mg/m3 for multi-wall carbon nanotubes and 0.5, 2.5, or 10 mg/m3 for graphene, graphite nanoplatelets and low-surface carbon black. Toxicity was determined after end of exposure and after three-week recovery using broncho-alveolar lavage fluid and microscopic examinations of the entire respiratory tract. Results No adverse effects were observed after inhalation exposure to 10 mg/m3 graphite nanoplatelets or relatively low specific surface area carbon black. Increases of lavage markers indicative for inflammatory processes started at exposure concentration of 0.5 mg/m3 for multi-wall carbon nanotubes and 10 mg/m3 for graphene. Consistent with the changes in lavage fluid, microgranulomas were observed at 2.5 mg/m3 multi-wall carbon nanotubes and 10 mg/m3 graphene. In order to evaluate volumetric loading of the lung as the key parameter driving the toxicity, deposited particle volume was calculated, taking into account different methods to determine the agglomerate density. However, the calculated volumetric load did not correlate to the toxicity, nor did the particle surface burden of the lung. Conclusions The inhalation toxicity of the investigated carbon-based materials is likely to be a complex interaction of several parameters. Until the properties which govern the toxicity are identified, testing by short-term inhalation is the best option to identify hazardous properties in

  19. The Synthesis of Peculiar Structure of Springlike Multiwall Carbon Nanofibers/Nanotubes via Mechanothermal Method

    Directory of Open Access Journals (Sweden)

    Sahebali Manafi

    2012-01-01

    Full Text Available Mechanothermal (MT method is one of the methods used for large-scale production of carbon nanotubes/nanofibers. The different peculiar morphologies of carbon allotropes are introduced with an extraordinary structure for the first time by MT method. In this paper, the influence of milling time and annealing temperature on the crystallinity and morphology of the synthesized nanopowders was investigated. Surprisingly, in this investigation, we report the synthesis of springlike multiwalled carbon nanofibers (S-MWCNFs by a two-step annealing of milled graphite in an Ar atmosphere. On the other hand, the MT method could be used for the preparation of suitable structures with applications in nanocomposite materials, which is an important task in the era of nanotechnology.

  20. Visible and near-infrared radiative properties of vertically aligned multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    Wang, X J; Zhang, Z M; Flicker, J D; Ready, W J; Lee, B J

    2009-01-01

    This work investigates the reflection and scattering from vertically aligned carbon nanotubes, fabricated on silicon substrate using thermally enhanced chemical vapor deposition with both tip-growth and base-growth mechanisms. The directional-hemispherical reflectance in the visible and near-infrared wavelengths was measured with an integrating sphere. The polarization-dependent bidirectional reflectance distribution function was characterized with a laser scatterometer at the wavelength of 635 nm. The effective medium theory was used to elucidate the mechanism of high absorptance (greater than 0.97 in the spectral region from 400 to 1800 nm) of the multi-walled carbon nanotube samples. It is observed that scattering by impurities on the top of the nanotubes, by the nanotube tips, and by defects and misalignment can significantly increase the reflectance and introduce retroreflection. This study may facilitate application of carbon nanotubes in pyroelectric detectors as well as thermophotovoltaic emitters and absorbers.

  1. Electrochemical selective detection of dopamine on microbial carbohydrate-doped multiwall carbon nanotube-modified electrodes.

    Science.gov (United States)

    Jin, Joon-Hyung; Cho, Eunae; Jung, Seunho

    2010-03-01

    Microbial carbohydrate-doped multiwall carbon nanotube (MWNT)-modified electrodes were prepared for the purpose of determining if 4-(2-aminoethyl)benzene-1,2-diol (3,4-dihydroxyphenylalanine; dopamine) exists in the presence of 0.5 mM ascorbic acid, a representative interfering agent in neurotransmitter detection. The microbial carbohydrate dopants were alpha-cyclosophorohexadecaose (alpha-C16) from Xanthomonas oryzae and cyclic-(1 --> 2)-beta-d-glucan (Cys) from Rhizobium meliloti. The cyclic voltammetric responses showed that the highest sensitivity (5.8 x 10(-3) mA cm(-2) microM(-1)) is attained with the Cys-doped MWNT-modified ultra-trace carbon electrode, and that the alpha-C16-doped MWNT-modified glassy carbon electrode displays the best selectivity to dopamine (the approximate peak potential separation is 310 mV).

  2. Effect of Acid Oxidation on the Dispersion Property of Multiwalled Carbon Nanotubes

    Science.gov (United States)

    Goh, P. S.; Ismail, A. F.; Aziz, M.

    2009-06-01

    A means of dispersion of multiwalled carbon nanotube (MWCNT) via mixed acid (HNO3 and H2SO4) oxidation with different treatment durations was investigated through the solubility study of the treated carbon nanotubes in some common solvents. Fourier transformed infrared (FTIR) characterization of the reaction products revealed that the surface of MWCNTs was successfully functionalized with surface acidic groups. The acid-base titration demonstrated that the amount of surface acidic groups increased in parallel with the refluxing duration. The acid modified MWCNTs were found to be well dispersed in polar solvents, such as ethanol and water due to the presence of the hydrophilic acid functional groups on the surface of raw MWCNTs. Such chemical modification of carbon nanotube properties will pave the way towards the realistic applications in the nanotechnology world.

  3. Fabrication of antibacterial PVA nanocomposite films containing dendritic polymer functionalized multi-walled carbon nanotubes

    Science.gov (United States)

    Sapalidis, Andreas; Sideratou, Zili; Panagiotaki, Katerina N.; Sakellis, Elias; Kouvelos, Evangelos P.; Papageorgiou, Sergios; Katsaros, Fotios

    2018-03-01

    A series of Poly(vinyl alcohol) (PVA) nanocomposite films containing quaternized hyperbranched polyethyleneimine (PEI) functionalized multi-walled carbon nanotubes (ox-CNTs@QPEI) are prepared by solvent casting technique. The modified carbon based material exhibits high aqueous solubility, due to the hydrophilic character of the functionalized hyperbranched dendritic polymer. The quaternized PEI successfully wraps around nanotube walls, as polycations provide electrostatic repulsion. Various contents of ox-CNTs@QPEI ranging from 0.05 to 1.0 % w/w were employed to prepare functionalized PVA nanocomposites. The developed films exhibit adequate optical transparency, improved mechanical properties and extremely high antibacterial behavior due to the excellent dispersion of the functionalized carbon nanotubes into the PVA matrix.

  4. Evaluation of Cardiopulmonary Toxicity Following Oral Administration of Multi-walled Carbon Nanotubes in Wistar Rats

    Directory of Open Access Journals (Sweden)

    Ehsan Zayerzadeh

    2016-07-01

    Full Text Available Objective(s: Carbon nanotubes have unique mechanical, electrical, and thermal properties, with potential different applications in nanomedicine, electronics, and other industries. These new applications of carbon nanotubes in different industries lead to the increased exposure risk of nanomaterials to human. Up to now, all aspects of carbon nanotubes toxicity are not completely clear following human and animal exposures with these novel compounds. The aim of this study was to assess cardiopulmonary toxicity of multi-walled carbon nanotubes following oral administration in rats with respect to the histopathological and biochemical evaluation. Methods: In the present investigation, we studied cardiorespiratory toxicity of multi-wall carbon nanotubes (MWCNT with regard to histopathological changes and some biomarkers including TnT, CK-MB and LDH in experimental rats following oral administration. One dose per 24 h of MWCNT suspension was administered orally (gavage technique to animals at the doses of 500, 1000 and 2000 mg/kg/day BW for 5 days. Results: The results of these study showed oral administration of MWCNT induces histopathological complications such as severe alveolar edema and hemorrhage in lungs and myocytolysis in heart of all experimental groups of animals. In all of the groups, troponin T level showed no changes when compared to baseline. Lactate dehydrogenase and CK-MB activity showed significant increment in all of animal groups following oral administration of carbon nanotubes. Conclusions: It can be concluded that oral exposure of MWCNT may be toxic for cardiovascular and respiratory systems, because MWCNT induced biochemical alterations and histopathological abnormalities in these vital systems.

  5. The Influence of Multiwalled Carbon Nanotubes on Polycyclic Aromatic Hydrocarbon (PAH) Bioavailability and Toxicity to Soil Microbial Communities in Alfalfa Rhizosphere

    Science.gov (United States)

    Carbon nanotubes (CNTs) may affect bioavailability and toxicity of organic contaminants due to their adsorption properties. Recent studies have observed the influence of multiwalled carbon nanotubes (MWNTs) on the fate of polycyclic aromatic hydrocarbons (PAHs) and other organic contaminants. Greenh...

  6. Novel star-like surfactant as dispersant for multi-walled carbon nanotubes in aqueous suspensions at high concentration

    Science.gov (United States)

    Qiao, Min; Ran, Qianping; Wu, Shishan

    2018-03-01

    A kind of novel surfactant with star-like molecular structure and terminated sulfonate was synthesized, and it was used as the dispersant for multi-walled carbon nanotubes (CNTs) in aqueous suspensions compared with a traditional single-chained surfactant. The star-like surfactant showed good dispersing ability for multi-walled CNTs in aqueous suspensions. Surface tension analysis, total organic carbon analysis, X-ray photoelectron spectroscopy, zeta potential, dynamic light scattering and transmission electron microscopy were performed to research the effect of star-like surfactant on the dispersion of multi-walled CNTs in aqueous suspensions. With the assistance of star-like surfactant, the CNTs could disperse well in aqueous suspension at high concentration of 50 g/L for more than 30 days, while the CNTs precipitated completely in aqueous suspension after 1 day without any dispersant or after 10 days with sodium 4-dodecylbenzenesulfonic acid as dispersant.

  7. Limited transport of functionalized multi-walled carbon nanotubes in two natural soils

    International Nuclear Information System (INIS)

    Kasel, Daniela; Bradford, Scott A.; Šimůnek, Jiří; Pütz, Thomas; Vereecken, Harry; Klumpp, Erwin

    2013-01-01

    Column experiments were conducted in undisturbed and in repacked soil columns at water contents close to saturation (85–96%) to investigate the transport and retention of functionalized 14 C-labeled multi-walled carbon nanotubes (MWCNT) in two natural soils. Additionally, a field lysimeter experiment was performed to provide long-term information at a larger scale. In all experiments, no breakthrough of MWCNTs was detectable and more than 85% of the applied radioactivity was recovered in the soil profiles. The retention profiles exhibited a hyper-exponential shape with greater retention near the column or lysimeter inlet and were successfully simulated using a numerical model that accounted for depth-dependent retention. In conclusion, results indicated that the soils acted as a strong sink for MWCNTs. Little transport of MWCNTs is therefore likely to occur in the vadose zone, and this implies limited potential for groundwater contamination in the investigated soils. -- Highlights: •Investigation of undisturbed soil columns and lysimeter. •Transport experiments under water-unsaturated conditions. •Retention profiles were measured and numerically modeled. •Complete retention of MWCNT in undisturbed and repacked soil columns. -- In undisturbed columns and a lysimeter study, complete retention of functionalized multi-walled carbon nanotubes was found in two soils at environmentally relevant conditions

  8. Latex stage blending of multiwalled carbon nanotube in carboxylated acrylonitrile butadiene rubber: Mechanical and electrical properties

    International Nuclear Information System (INIS)

    Preetha Nair, K.; Thomas, Paulbert; Joseph, Rani

    2012-01-01

    Highlights: ► MWCNT can act as a reinforcing filler in XNBR at very low concentration. ► SEM and XRD analysis confirm uniform distribution of nanotube in the matrix. ► Mechanical properties showed considerable improvement. ► Thermal stability of the composite is marginally improved. -- Abstract: Multiwalled carbon nanotube (MWCNT) was dispersed in sodium dodecyl benzene sulphonate (SDBS) by sonication. The dispersed MWCNT (0.05–0.3 gm) was incorporated in carboxylated acrylonitrile butadiene rubber (XNBR) latex. Mechanical, electrical and thermal properties of these composites were studied. Mechanical properties of the composites increased up to an optimum concentration and then decreased. Dielectric properties of the composites were studied in the S band (frequency range 2–4 GHz) by Cavity Perturbation method. Direct current (DC) electrical conductivity shows a percolation behaviour and conductivity increased by about 10 orders of magnitude. Thermal studies were conducted using Differential Scanning Calorimetry (DSC) and Thermo Gravimetric Analysis (TGA). As expected with the very small concentration of multiwalled carbon nanotube, glass transition temperature (T g ) and thermal stability of the composite showed a marginal increase. Composites were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and Scanning electron microscope (SEM) analysis.

  9. Electrochemical performance of Si-multiwall carbon nanotube nanocomposite anode synthesized by thermal plasma

    Energy Technology Data Exchange (ETDEWEB)

    Na, Ye-Seul; Yoo, Hyeonseok; Kim, Tae-Hee; Choi, Jinsub; Lee, Wan In; Choi, Sooseok, E-mail: sooseok@jejunu.ac.kr; Park, Dong-Wha, E-mail: dwpark@inha.ac.kr

    2015-07-31

    Lithium-ion (Li-ion) batteries are widely used in electric devices and vehicles. Silicon is a promising material for the anode of Li-ion battery due to high theoretical specific capacity. However, it shows large volume changes during charge–discharge cycles leading to the pulverization of electrode. In order to improve such disadvantage, a multiwall carbon nanotube (MWCNT) has been used with silicon as composite material. In this work, Si-MWCNT nanocomposite was prepared in thermal plasma by attaching silicon nanoparticles to MWCNT column. Electrochemical tests for raw materials and synthesized nanocomposites were carried out. The discharge capacities of silicon, MWCNT, synthesized nanocomposites collected from a reaction tube, and a chamber were 4000, 310, 200, and 1447 mAh/g, respectively. - Highlights: • Si-Multiwall carbon nanotube nanocomposite was synthesized by thermal plasma. • The effect on the collection position of product after experiment was examined. • Cycle performance of electrodes was measured. • Product collected from chamber showed good electrochemical performance.

  10. Surfactive stabilization of multi-walled carbon nanotube dispersions with dissolved humic substances

    Energy Technology Data Exchange (ETDEWEB)

    Chappell, Mark A. [Environmental Laboratory, Engineering Research and Development Center, US Army Corps of Engineers, 3909 Halls Ferry Road, Vicksburg, MS 39180 (United States)], E-mail: mark.a.chappell@usace.army.mil; George, Aaron J.; Dontsova, Katerina M.; Porter, Beth E. [SpecPro, Inc., 4815 Bradford Drive, Suite 201, Huntsville, AL 35805 (United States); Price, Cynthia L. [Environmental Laboratory, Engineering Research and Development Center, US Army Corps of Engineers, 3909 Halls Ferry Road, Vicksburg, MS 39180 (United States); Zhou Pingheng; Morikawa, Eizi [J. Bennett Johnston Sr. Center for Advanced Microstructures and Devices, Louisiana State University, 6980 Jefferson Highway, Baton Rouge, LA 70806 (United States); Kennedy, Alan J.; Steevens, Jeffery A. [Environmental Laboratory, Engineering Research and Development Center, US Army Corps of Engineers, 3909 Halls Ferry Road, Vicksburg, MS 39180 (United States)

    2009-04-15

    Soil humic substances (HS) stabilize carbon nanotube (CNT) dispersions, a mechanism we hypothesized arose from the surfactive nature of HS. Experiments dispersing multi-walled CNT in solutions of dissolved Aldrich humic acid (HA) or water-extractable Catlin soil HS demonstrated enhanced stability at 150 and 300 mg L{sup -1} added Aldrich HA and Catlin HS, respectively, corresponding with decreased CNT mean particle diameter (MPD) and polydispersivity (PD) of 250 nm and 0.3 for Aldrich HA and 450 nm and 0.35 for Catlin HS. Analogous trends in MPD and PD were observed with addition of the surfactants Brij 35, Triton X-405, and SDS, corresponding to surfactant sorption maximum. NEXAFS characterization showed that Aldrich HA contained highly surfactive domains while Catlin soil possessed a mostly carbohydrate-based structure. This work demonstrates that the chemical structure of humic materials in natural waters is directly linked to their surfactive ability to disperse CNT released into the environment. - Suspensions of multi-walled carbon nanotubes are stabilized by relatively low concentrations of dissolved humic substances in solution through surfactive mechanisms.

  11. Nickel and cobalt filled multiwalled carbon nantubes : structural transformation under heavy ion irradiation and high pressure

    International Nuclear Information System (INIS)

    Misra, D.S.; Misra, A.; Tyagi, Pawan K.; Karamakar, S.; Sharma, Surinder M.

    2006-01-01

    Full text: The nickel and cobalt nano wires of diameters ranging from 5-15 nm are formed inside the multiwalled carbon nantubes using microwave plasma chemical vapor deposition in our laboratory. The nano wires inside the tubes are found to have a perfect crystalline structure and the crystalline planes of (111) orientations are aligned for FCC nickel and cobalt in a particular fashion. We find that the cobalt can exist either in FCC or HCP phase in confinement depending upon the diameter of the tubes. The irradiation of these nanowires with high energy Au + ions alter the orientation of the crystalline planes and generate various types of domains and defects in the nanowires. The complete amorphization of the walls of the nano tubes is observed at the fluence of 5x10 13 /cm 2 and results in amorphization of nickel nano wires as well. The cobalt nano wires have FCC structure in ambient conditions and transform to HCP cobalt irreversibly when subjected to high pressure of ∼9 GPa. Multi-walled carbon nano tubes that encapsulate the cobalt nano wires do not undergo any other structural transformation with pressure except partial reversible amorphization beyond 9 GPa

  12. Photoexcitations in fully organic nanocomposites of poly(3-hexylthiophene) and multiwalled carbon nanotubes

    International Nuclear Information System (INIS)

    Bakour, Anass; Geschier, Fredéric; Baitoul, Mimouna; Wéry, Jany; Massuyeau, Florian; Faulques, Eric

    2016-01-01

    Insertion effects of multiwalled carbon nanotubes (MWNTs) at different loads in the regioregular poly(3-hexylthiophene) (RR-P3HT) electroactive polymer are investigated with transmission electron microscopy (TEM), X-ray diffraction, infrared and optical absorption, photoluminescence (PL) and photoconductivity techniques. MWNTs in composites quench the deep red emission of P3HT. They also act as inhibitors of polymer aggregates favoring shorter conjugated segments during composite synthesis and the formation of a charge-transfer complex at the P3HT/MWNT interface through delocalization of π electrons along the conjugated segments. Under photoexcitation, a significant fraction of excitons dissociates non radiatively with charge hopping towards the MWNTs network and triggers an augmentation of photoconductivity. - Highlights: • Composites of multiwalled carbon nanotubes (MWNTs) and poly(3- hexylthiophene) (P3HT). • Thin nanocomposite films with various MWNTs concentrations x. • Full study with synthesis, structural, optical and vibrational experiments. • Drastic and ultrafast photoluminescence quenching with increasing x. • Augmentation of photoconductivity in composite.

  13. Surfactive stabilization of multi-walled carbon nanotube dispersions with dissolved humic substances

    International Nuclear Information System (INIS)

    Chappell, Mark A.; George, Aaron J.; Dontsova, Katerina M.; Porter, Beth E.; Price, Cynthia L.; Zhou Pingheng; Morikawa, Eizi; Kennedy, Alan J.; Steevens, Jeffery A.

    2009-01-01

    Soil humic substances (HS) stabilize carbon nanotube (CNT) dispersions, a mechanism we hypothesized arose from the surfactive nature of HS. Experiments dispersing multi-walled CNT in solutions of dissolved Aldrich humic acid (HA) or water-extractable Catlin soil HS demonstrated enhanced stability at 150 and 300 mg L -1 added Aldrich HA and Catlin HS, respectively, corresponding with decreased CNT mean particle diameter (MPD) and polydispersivity (PD) of 250 nm and 0.3 for Aldrich HA and 450 nm and 0.35 for Catlin HS. Analogous trends in MPD and PD were observed with addition of the surfactants Brij 35, Triton X-405, and SDS, corresponding to surfactant sorption maximum. NEXAFS characterization showed that Aldrich HA contained highly surfactive domains while Catlin soil possessed a mostly carbohydrate-based structure. This work demonstrates that the chemical structure of humic materials in natural waters is directly linked to their surfactive ability to disperse CNT released into the environment. - Suspensions of multi-walled carbon nanotubes are stabilized by relatively low concentrations of dissolved humic substances in solution through surfactive mechanisms

  14. Photoexcitations in fully organic nanocomposites of poly(3-hexylthiophene) and multiwalled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Bakour, Anass [Laboratory of Solid State Physics, Research Group Polymers and Nanomaterials, University Sidi Mohammed Ben Abdellah, Faculty of Sciences Dhar El Mahraz, P.O. Box 1796 Atlas, 30000 Fes (Morocco); Geschier, Fredéric [Institut des Matériaux Jean Rouxel, Université de Nantes, CNRS, UMR 6502, 2 Rue de la Houssinière, 44322 Nantes (France); Baitoul, Mimouna [Laboratory of Solid State Physics, Research Group Polymers and Nanomaterials, University Sidi Mohammed Ben Abdellah, Faculty of Sciences Dhar El Mahraz, P.O. Box 1796 Atlas, 30000 Fes (Morocco); Wéry, Jany; Massuyeau, Florian [Institut des Matériaux Jean Rouxel, Université de Nantes, CNRS, UMR 6502, 2 Rue de la Houssinière, 44322 Nantes (France); Faulques, Eric, E-mail: eric.faulques@cnrs-imn.fr [Institut des Matériaux Jean Rouxel, Université de Nantes, CNRS, UMR 6502, 2 Rue de la Houssinière, 44322 Nantes (France)

    2016-03-01

    Insertion effects of multiwalled carbon nanotubes (MWNTs) at different loads in the regioregular poly(3-hexylthiophene) (RR-P3HT) electroactive polymer are investigated with transmission electron microscopy (TEM), X-ray diffraction, infrared and optical absorption, photoluminescence (PL) and photoconductivity techniques. MWNTs in composites quench the deep red emission of P3HT. They also act as inhibitors of polymer aggregates favoring shorter conjugated segments during composite synthesis and the formation of a charge-transfer complex at the P3HT/MWNT interface through delocalization of π electrons along the conjugated segments. Under photoexcitation, a significant fraction of excitons dissociates non radiatively with charge hopping towards the MWNTs network and triggers an augmentation of photoconductivity. - Highlights: • Composites of multiwalled carbon nanotubes (MWNTs) and poly(3- hexylthiophene) (P3HT). • Thin nanocomposite films with various MWNTs concentrations x. • Full study with synthesis, structural, optical and vibrational experiments. • Drastic and ultrafast photoluminescence quenching with increasing x. • Augmentation of photoconductivity in composite.

  15. The effect of calcination on multi-walled carbon nanotubes produced by dc-arc discharge.

    Science.gov (United States)

    Pillai, Sreejarani K; Augustyn, Willem G; Rossouw, Margaretha H; McCrindle, Robert I

    2008-07-01

    Multi-walled carbon nanotubes were synthesized by dc-arc discharge in helium atmosphere and the effect of calcination at different temperatures ranging from 300-600 degrees C was studied in detail. The degree of degradation to the structural integrity of the multi-walled carbon nanotubes during the thermal process was studied by Raman spectroscopy, Scanning electron microscopy and High resolution transmission electron microscopy. The thermal behaviour of the as prepared and calcined samples was investigated by thermogravimetric analysis. Calcination in air at 400 degrees C for 2 hours was found to be an efficient and simple method to eliminate carbonaceous impurities from the nanotube bundles with minimal damage to the tube walls and length. The impurities were oxidized at a faster rate when compared to the nanotubes and gave good yield of about 50%. The nanotubes were observed to be damaged at temperature higher than 450 degrees C. The results show that this method is less destructive when compared liquid phase oxidation with 5 M HNO3.

  16. Chemical attachment of functionalized multiwalled carbon nanotubes on glassy carbon electrode for electrocatalytic application

    International Nuclear Information System (INIS)

    Rajalakshmi, K.; Abraham John, S.

    2015-01-01

    Highlights: • FMWCNTs were covalently attached on GC surface with the aid of alkyldiamine. • The attached FMWCNTs were stable for a wide potential window due to the robust C−N bond. • The composite electrode was prepared by electropolymerizing thiadiazole on FMWCNTs. • The detection limit of 0.27 μM (S/N = 3) of GMP was achieved using composite modified electrode. - Abstract: The covalent attachment of acid functionalized multiwalled carbon nanotubes (FMWCNTs) on glassy carbon (GC) electrode using 1,8-octanediamine (OD) as a linker via carbodiimide chemistry was described. The attachment of FMWCNTs on GC electrode were confirmed by attenuated total reflectance Fourier transform infra-red (ATR-FT-IR) spectroscopy, Raman, scanning electron microscopy (SEM) and electrochemical impedance studies. Raman spectrum of FMWCNTs modified surface shows the characteristic G and D bands at 1563 cm −1 and 1340 cm −1 , respectively. This confirmed the successful attachment of FMWCNTs on the OD modified GC surface. Further, the attachment of FMWCNTs on OD modified surface via amide linkage was confirmed from the observed characteristic peak at 1681 cm −1 in the ATR-FT-IR spectrum. The SEM images showed that the covalently attached FMWCNTs retained their morphology similar to powder and the average diameter of them was found to be 58 nm. Unlike modification of FMWCNTs on gold substrates with the aid of conventional thiol linkers (Au−S bond), modification of them by the present method was stable for a wide positive potential window due to the robust C−N bond. To demonstrate the electrochemical stability of the MWCNTs modified electrode at more positive potential, guanosine 5′-monophosphate (GMP) was selected as a representative probe because its oxidation occurs at more than 1 V. It was found that the FMWCNTs modified electrode not only showed a stable signal for GMP but also enhanced its oxidation current when compared to bare GC electrode. Further, the

  17. Multiple functionalization of multi-walled carbon nanotubes with carboxyl and amino groups

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Zhiyuan [College of Chemistry and Chemical Engineering, Central South University, Changsha 410083 (China); Yang, Zhanhong, E-mail: zhongnan320@gmail.com [College of Chemistry and Chemical Engineering, Central South University, Changsha 410083 (China); Key Laboratory of Resource Chemistry of Nonferrous Metals, Ministry of Education, Central South University, Changsha 410083 (China); Hu, Youwang; Li, Jianping [College of Mechanical and Electrical Engineering, Central South University, Changsha 410083 (China); Fan, Xinming [College of Chemistry and Chemical Engineering, Central South University, Changsha 410083 (China)

    2013-07-01

    In this paper, carboxyl and amino groups have been introduced onto the surface of the multi-walled carbon nanotubes (MWCNTs) by the mixed acid treatment and the diazonium reaction, respectively. The presence of multifunctionality groups on the MWCNTs has been characterized by Fourier transform infrared (FT-IR) spectroscopy, thermogravimetric (TGA) analysis, Raman spectra, scanning electron microscopy (SEM) and energy dispersive X-ray spectrum (EDS). The multifunctionalized carbon nanotubes were further utilized to react with acetyl chloride and ethylenediamine (EDA). The formation of the amide bond in the grafting reaction has been confirmed by FT-IR spectroscopy. The result indicates that the further grafting is successful. The multifunctionalized MWCNTs can be a new versatile platform for many interesting applications.

  18. Environmental Conditions Influencing Sorption of Inorganic Anions to Multiwalled Carbon Nanotubes Studied by Column Chromatography.

    Science.gov (United States)

    Metzelder, Florian; Schmidt, Torsten C

    2017-05-02

    Sorption to carbon-based nanomaterials is typically studied in batch experiments. An alternative method offering advantages to study sorption is column chromatography. Sorbent packed columns are used and sorption data are determined by relating sorbate retention to that of a nonretarded tracer. We have now for the first time applied this technique to study the influence of environmental conditions on sorption of inorganic anions (bromide, nitrite, nitrate, and iodide) to multiwalled carbon nanotubes. Deuterium oxide was used as nonretarded tracer. Sorption isotherms were best described by the Freundlich model. Sorption increased in the order bromide 4.5 the surface charge was negative, but sorption was still detectable at pH 6 and 9. Consequently, other forces than electrostatic attraction contributed to sorption. These forces may include H-bonding as indicated by sorption enthalpy determined by variation of column temperature. Overall, column chromatography represents a promising alternative in sorption studies to reveal sorbent properties.

  19. Chemical splitting of multiwalled carbon nanotubes to enhance electrochemical capacitance for supercapacitors

    Science.gov (United States)

    Li, Xinlu; Li, Tongtao; Zhang, Xinlin; Zhong, Qineng; Li, Hongyi; Huang, Jiamu

    2014-06-01

    Multiwalled carbon nanotubes (MWCNTs) were chemically split and self-assembled to a flexible porous paper made of graphene oxide nanoribbons (GONRs). The morphology and microstructure of the pristine MWCNTs and GONRs were analyzed by transmission electron microscopy, scanning electron microscopy, X-ray diffraction, Raman spectroscopy and Fourier transform infrared spectroscopy. And the specific surface area and porosity structure were measured by N2 adsorption-desorption. The longitudinally split MWCNTs show an enhancement in specific capacitance from 21 F g-1 to 156 F g-1 compared with the pristine counterpart at 0.1 A g-1 in a 6 M KOH aqueous electrolytes. The electrochemical experiments prove that the chemical splitting of MWCNTs will make inner carbon layers opened and exposed to electrochemical double layers, which can effectively improve the electrochemical capacitance for supercapacitors.

  20. Effect of porosity variation on the electrochemical behavior of vertically aligned multi-walled carbon nanotubes.

    Science.gov (United States)

    Raut, Akshay S; Parker, Charles B; Stoner, Brian R; Glass, Jeffrey T

    2012-06-01

    Electrochemical charge storage characteristics of vertically aligned multi-walled carbon nanotubes (MWCNTs) as a function of varying diameter and spacing are reported. It was observed that the specific capacitance of the MWCNTs increased as both diameter and inter-tube spacing decreased. The MWCNT films with 229 nm inter-MWCNT spacing exhibited specific capacitance of 228 F/g versus 70 F/g for 506 nm spacing, when tested in a non-aqueous electrolyte. Further, a trend in specific capacitance versus pore size is proposed. Coupled with previously reported trends observed in the sub-10 nm pore size regime, this is expected to offer better understanding of electrochemical behavior of porous carbon materials over a wide range of pore sizes.

  1. Third sound measurements of superfluid 4He films on multiwall carbon nanotubes below 1 K

    International Nuclear Information System (INIS)

    Menachekanian, Emin; Abraham, John B S; Chen, Bob; Iaia, Vito; Li, Andrew; Williams, Gary A

    2014-01-01

    Third sound is studied for superfluid films of 4He adsorbed on multiwall carbon nanotubes packed into an annular resonator. The third sound is generated with mechanical oscillation of the cell, and detected with carbon bolometers. A filling curve at temperatures near 250 mK shows oscillations in the third sound velocity, with maxima at the completion of the 4th and 5th atomic layers. Sharp changes in the Q factor of the third sound are found at partial layer fillings. Temperature sweeps at a number of fill points show strong broadening effects on the Kosterlitz-Thouless (KT) transition, and rapidly increasing dissipation, in qualitative agreement with the predictions of Machta and Guyer. At the 4th layer completion there is a sudden reduction of the transition temperature T KT , and then a recovery back to linear variation with temperature, although the slope is considerably smaller than the KT prediction

  2. H_{2} adsorption on multiwalled carbon nanotubes at low temperatures and low pressures

    Directory of Open Access Journals (Sweden)

    F. Xu

    2008-11-01

    Full Text Available We present an experimental study on H_{2} adsorption on multiwalled carbon nanotubes (MWCNTs at low temperatures (12–30 K and low pressures (2×10^{-5}  Torr using the temperature programmed desorption technique. Our results show that the molecular hydrogen uptake increases nearly exponentially from 6×10^{-9}  wt. % at 24.5 K to 2×10^{-7}  wt. % at 12.5 K and that the desorption kinetics is of the first order. Comparative measurements indicate that MWCNTs have an adsorption capacity about two orders higher than that of activated carbon (charcoal making them a possible candidate as hydrogen cryosorber for eventual applications in accelerators and synchrotrons.

  3. Bonding titanium on multi-walled carbon nanotubes for hydrogen storage: An electrochemical approach

    Energy Technology Data Exchange (ETDEWEB)

    Brieno-Enriquez, K.M.; Ledesma-Garcia, J. [Centro de Investigacion y Desarrollo Tecnologico en Electroquimica, S.C., Parque Tecnologico Queretaro-Sanfandila, Pedro Escobedo, Qro, C.P. 76703 (Mexico); Perez-Bueno, J.J., E-mail: jperez@cideteq.mx [Centro de Investigacion y Desarrollo Tecnologico en Electroquimica, S.C., Parque Tecnologico Queretaro-Sanfandila, Pedro Escobedo, Qro, C.P. 76703 (Mexico); Godinez, Luis A. [Centro de Investigacion y Desarrollo Tecnologico en Electroquimica, S.C., Parque Tecnologico Queretaro-Sanfandila, Pedro Escobedo, Qro, C.P. 76703 (Mexico); Terrones, H. [Instituto Potosino de Investigacion Cientifica y Tecnologica, Division de Materiales Avanzados, Camino a la Presa San Jose 2055, Col. Lomas 4o Seccion C.P. 78216, San Luis Potosi (Mexico); Angeles-Chavez, C. [Instituto Mexicano del Petroleo, Programa de Ingenieria Molecular, Eje Central Lazaro Cardenas 152, A.P. 14-805, 07730 Mexico D.F. (Mexico)

    2009-06-15

    This work explores the use of some procedures, involving electrochemistry, in order to bond atomic Ti on the outer surface of multi-walled carbon nanotubes (MWNTs). It is assumed that each titanium atom has the potential of host up to four hydrogen molecules and relinquish them by heated. As a way to spread and stick nanotubes on an electrode, a tested route was drying a solution with nanotubes on a glassy carbon flat electrode. The MWNTs were treated by anodic polarization in organic media. Dichloromethane was selected as the medium and titanium tetrachloride as the precursor for attaching atomic Ti onto the nanotubes. The hydrogen adsorption, estimated from voltamperometry was five times higher on Ti-MWNTs that on bare nanotubes. The use of anodic polarization during the preparation of Ti-MWNTs may represent great significance in procedure, which was manifest during the voltamperometric evaluation of samples.

  4. Electro-optical memory of a nematic liquid crystal doped by multi-walled carbon nanotubes

    Directory of Open Access Journals (Sweden)

    L. Dolgov

    2012-10-01

    Full Text Available A pronounced irreversible electro-optical response (memory effect has been recently observed for nematic liquid crystal (LC EBBA doped by multi-walled carbon nanotubes (MWCNTs near the percolation threshold of the MWCNTs (0.02÷0.05 wt. %. It is caused by irreversible homeotropic-to-planar reorientation of LC in an electric field. This feature is explained by electro-hydrodynamically stimulated dispergation of MWCNTs in LC and by the formation of a percolation MWCNT network which acts as a spatially distributed surface stabilizing the planar state of the LC. This mechanism is confirmed by the absence of memory in the EBBA/MWCNT composites, whose original structure is fixed by a polymer. The observed effect suggests new operation modes for the memory type and bistable LC devices, as well as a method for in situ dispergation of carbon nanotubes in LC cells.

  5. Humidity Sensor Based on Multi-Walled Carbon Nanotube Thin Films

    International Nuclear Information System (INIS)

    Cao, C.L.; Hu, C.G.; Fang, L.; Wang, S.X.; Cao, C.L.; Tian, Y.S.; Pan, C.Y.

    2009-01-01

    The properties of the humidity sensors made of chemically treated and untreated multi-walled carbon nano tube (MWCNT) thin films are investigated systematically. It shows that both the chemically treated and untreated MWCNT thin films demonstrate humidity sensitive properties, but the former have stronger sensitivity than the latter. In the range of 11%-98% relative humidity (RH), the resistances of the chemically treated and untreated MWCNT humidity sensors increase 120% and 28%, respectively. Moreover, the treated humidity sensors showed higher sensitivity and better stability. In addition, the response and recover properties, and stabilization of the humidity sensors are measured, and the humidity sensitive mechanisms of the sensors are analyzed. The humidity sensitivity of carbon nano tube thin films indicates it promise as a kind of humidity sensitive material

  6. The Role of Multi-wall Carbon Nanotubes on Fracture Mechanism of Epoxy Nanocomposite

    Directory of Open Access Journals (Sweden)

    M. Hooshiar Sadegian

    2008-12-01

    Full Text Available In order to investigate the role of multi-wall carbon nanotubes (MWCNTs on fracture mechanism of epoxy nanocomposites, a series of tensile standard specimens reinforced with different carbon nanotube contents (0, 0.3, 0.6 and 1 wt% were produced. The fracture surfaces of the produced nanocomposites were evaluated using scanning electron microscope (SEM. The results show that the surface fracture of epoxy nanocomposites comprised of three regions, i.e. mirror, transition and final propagation zones. The extension of all zones depends strongly on curing agent as well asMWCNTs content. The mirror zone is disappeared as curing agent and MWCNTs content increases, while the transition zone depends on the nucleation rate of secondary microcrack. The pattern of final propagation zone becomes coarser as MWCNTs are added to epoxy system.

  7. Effect of Novel Quercetin Titanium Dioxide-Decorated Multi-Walled Carbon Nanotubes Nanocomposite on Bacillus subtilis Biofilm Development

    Directory of Open Access Journals (Sweden)

    Diana S. Raie

    2018-01-01

    Full Text Available The present work was targeted to design a surface against cell seeding and adhering of bacteria, Bacillus subtilis. A multi-walled carbon nanotube/titanium dioxide nano-power was produced via simple mixing of carbon nanotube and titanium dioxide nanoparticles during the sol-gel process followed by heat treatment. Successfully, quercetin was immobilized on the nanocomposite via physical adsorption to form a quercetin/multi-walled carbon nanotube/titanium dioxide nanocomposite. The adhesion of bacteria on the coated-slides was verified after 24 h using confocal laser-scanning microscopy. Results indicated that the quercetin/multi-walled carbon nanotube/titanium dioxide nanocomposite had more negativity and higher recovery by glass surfaces than its counterpart. Moreover, coating surfaces with the quercetin-modified nanocomposite lowered both hydrophilicity and surface-attached bacteria compared to surfaces coated with the multi-walled carbon nanotubes/titanium dioxide nanocomposite.

  8. Airway exposure to multi-walled carbon nanotubes disrupts the female reproductive cycle without affecting pregnancy outcomes in mice

    DEFF Research Database (Denmark)

    Johansson, Hanna Katarina Lilith; Hansen, J. S.; Elfving, B.

    2017-01-01

    Background: The use of multiwalled carbon nanotubes (MWCNT) is increasing due to a growing use in a variety of products across several industries. Thus, occupational exposure is also of increasing concern, particularly since airway exposure to MWCNTs can induce sustained pulmonary acute phase res...

  9. A new approach combining analytical methods for workplace exposure assessment of inhalable multi-walled carbon nanotubes

    NARCIS (Netherlands)

    Tromp, P.C.; Kuijpers, E.; Bekker, C.; Godderis, L.; Lan, Q.; Jedynska, A.D.; Vermeulen, R.; Pronk, A.

    2017-01-01

    To date there is no consensus about the most appropriate analytical method for measuring carbon nanotubes (CNTs), hampering the assessment and limiting the comparison of data. The goal of this study is to develop an approach for the assessment of the level and nature of inhalable multi-wall CNTs

  10. Co-transport of chlordecone and sulfadiazine in the presence of functionalized multi-walled carbon nanotubes in soils

    Science.gov (United States)

    Batch and saturated soil column experiments were conducted to investigate sorption and mobility of two 14C-labeled contaminants, the hydrophobic chlordecone (CLD) and the readily water-soluble sulfadiazine (SDZ), in the absence or presence of functionalized multi-walled carbon nanotubes (MWCNTs). Th...

  11. Do goethite surfaces really control the transport and retention of multi-walled carbon nanotubes in chemically heterogeneous porous media?

    Science.gov (United States)

    Transport and retention behavior of multiwalled carbon nanotubes (MWCNTs) was studied in mixtures of negatively charged quartz sand (QS) and positively charged goethite-coated sand (GQS) to assess the role of chemical heterogeneity. The linear equilibrium sorption model provided a good description o...

  12. Electrophoretic deposition (EPD) of multi-walled carbon nano tubes (MWCNT) onto indium-tin-oxide (ITO) glass substrates

    International Nuclear Information System (INIS)

    Mohd Roslie Ali; Shahrul Nizam Mohd Salleh

    2009-01-01

    Full text: Multi-Walled Carbon Nano tubes (MWCNT) were deposited onto Indium-Tin-Oxide (ITO)-coated glass substrates by introducing the use of Electrophoretic Deposition (EPD) as the method. The Multi-Walled Carbon Nano tubes (MWCNT) were dispersed ultrasonically in ethanol and sodium hydroxide (NaOH) to form stable suspension. The addition of Sodium Hydroxide in ethanol can stabilize the suspension, which was very important step before the deposition take place. Two substrates of Indium-Tin-Oxide(ITO)-coated glass placed in parallel facing each other (conductive side) into the suspension. The deposition occurs at room temperature, which the distance fixed at 1 cm between both electrodes and the voltage level applied was fixed at 400 V, respectively. The deposition time also was fixed at 30 minutes. The deposited ITO-Glass with Multi-Walled Carbon Nano tubes (MWCNT) will be characterized using Scanning Electron Microscope (SEM), Atomic Force Microscope (AFM), and Raman Microscope. The images of SEM shows that the Multi -Walled Carbon Nano tubes (MWCNT) were distributed uniformly onto the surface of ITO-Glass. The deposited ITO-Glass with Multi-Walled Carbon Nano tubes (MWCNT) could be the potential material in various practical applications such as field emission devices, fuel cells, and super capacitors. Electrophoretic deposition (EPD) technique was found to be an efficient technique in forming well distribution of Multi-Walled Carbon Nano tubes (MWCNT) onto ITO-Glass substrates, as proved in characterization methods, in which the optimum conditions will play the major role. (author)

  13. Nanocomposites of nitrile (NBR) rubber with multi-walled carbon nanotubes

    Science.gov (United States)

    Warasitthinon, Nuthathai

    Nanotechnology offers the promise of creating new materials with enhanced performance. There are different kinds of fillers used in rubber nanocomposites, such as carbon black, silica, carbon fibers, and organoclays. Carbon nanotube reinforced elastomers have potential for improved rubber properties in aggressive environments. The first chapter is an introduction to the literature. The second chapter investigated the incorporation of multi-walled carbon nanotubes (MWCNTs) into rubber matrix for potential use in high temperature applications. The vulcanization kinetics of acrylonitrile butadiene rubber (NBR) reinforced with multi-walled carbon nanotubes was investigated. The vulcanized NBR rubber with different loading percentages of MWCNTs was also compared to NBR reinforced with carbon black N330. The optimum curing time at 170°C (T90) was found to decrease with increasing content of MWCNTs. Increased filler loading of both carbon black and MWCNTs gave higher modulus and strength. The MWCNTs filled materials gave better retention of modulus and tensile strength at high temperatures, but lower strength as compared to the carbon black filled samples. In the third chapter, carbon black (CB, 50phr) content in nitrile rubber (NBR) nanocomposites was partially replaced by multi-walled carbon nanotubes (MWCNTs). NBR/CB/CNTs nanocomposites with varying ratio of CB/CNTs (50/0 phr to 40/10 phr) were formulated via the melt-mixing method using an internal mixer. The reinforcing effect of single filler (CB) and mixture of fillers (CB and CNTs) on the properties of NBR nanocomposites was investigated. The cure kinetics and bound rubber content were analyzed using rheometry and solvent swelling method. In addition, mechanical behavior at both room temperature and high temperature (350°F/ 121°C) were examined. The scorch time and curing time values showed that there was no significant effect on the curing behavior of NBR nanocomposites after the partial replacement of CB with

  14. Mass production of multi-wall carbon nanotubes by metal dusting process with high yield

    Energy Technology Data Exchange (ETDEWEB)

    Ghorbani, H. [School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Narmak, Tehran (Iran, Islamic Republic of); Rashidi, A.M., E-mail: Rashidiam@ripi.ir [Nanotechnology Research Center, Research Institute of Petroleum Industry (RIPI), West Blvd. Azadi Sport Complex, P.O. Box 14665-1998, Tehran (Iran, Islamic Republic of); Rastegari, S.; Mirdamadi, S. [School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Narmak, Tehran (Iran, Islamic Republic of); Alaei, M. [Nanotechnology Research Center, Research Institute of Petroleum Industry (RIPI), West Blvd. Azadi Sport Complex, P.O. Box 14665-1998, Tehran (Iran, Islamic Republic of)

    2011-05-15

    Research highlights: {yields} Synthesis of carbon nanotubes over Fe-Ni nanoparticles supported alloy 304L. {yields} Production of carbon nanotubes with high yield (700-1000%) and low cost catalyst. {yields} Optimum growth condition is CO/H{sub 2} = 1/1, 100 cm{sup 3}/min, at 620 {sup o}C under long term repetitive thermal cycling. {yields} Possibility of the mass production by metal dusting process with low cost. -- Abstract: Carbon nanotube materials were synthesized over Fe-Ni nanoparticles generated during disintegration of the surface of alloy 304L under metal dusting environment. The metal dusting condition was simulated and optimized through exposing stainless steel samples during long term repetitive thermal cycling in CO/H{sub 2} = 1/1, total gas flow rate 100 cm{sup 3}/min, at 620 {sup o}C for 300 h. After reaction, surface morphology of the samples and also carbonaceous deposition which had grown on sample surfaces were examined by stereoscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Results revealed that multi-wall carbon nanotubes could be formed over nanocatalyst generated on the alloy surface by exploiting metal dusting process. By optimization of reaction parameters the yields of carbon nanotube materials obtained were 700-1000%. Also it has been shown herein that the amount of carbon nanotube materials remarkably increases when the reaction time is extended up to 300 h, indicating a possibility of the mass production by this easy method.

  15. Mass production of multi-wall carbon nanotubes by metal dusting process with high yield

    International Nuclear Information System (INIS)

    Ghorbani, H.; Rashidi, A.M.; Rastegari, S.; Mirdamadi, S.; Alaei, M.

    2011-01-01

    Research highlights: → Synthesis of carbon nanotubes over Fe-Ni nanoparticles supported alloy 304L. → Production of carbon nanotubes with high yield (700-1000%) and low cost catalyst. → Optimum growth condition is CO/H 2 = 1/1, 100 cm 3 /min, at 620 o C under long term repetitive thermal cycling. → Possibility of the mass production by metal dusting process with low cost. -- Abstract: Carbon nanotube materials were synthesized over Fe-Ni nanoparticles generated during disintegration of the surface of alloy 304L under metal dusting environment. The metal dusting condition was simulated and optimized through exposing stainless steel samples during long term repetitive thermal cycling in CO/H 2 = 1/1, total gas flow rate 100 cm 3 /min, at 620 o C for 300 h. After reaction, surface morphology of the samples and also carbonaceous deposition which had grown on sample surfaces were examined by stereoscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Results revealed that multi-wall carbon nanotubes could be formed over nanocatalyst generated on the alloy surface by exploiting metal dusting process. By optimization of reaction parameters the yields of carbon nanotube materials obtained were 700-1000%. Also it has been shown herein that the amount of carbon nanotube materials remarkably increases when the reaction time is extended up to 300 h, indicating a possibility of the mass production by this easy method.

  16. Comparison of cellular toxicity between multi-walled carbon nanotubes and onion-like shell-shaped carbon nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Kang, Seunghyon [Seoul National University, School of Mechanical and Aerospace Engineering (Korea, Republic of); Kim, Ji-Eun [Korea Research Institute of Standard and Science, Center for NanoSafety Metrology, Division of Convergence Technology (Korea, Republic of); Kim, Daegyu [LG Electronics (Korea, Republic of); Woo, Chang Gyu [Korea Institute of Machinery and Materials, Environmental and Energy Systems Research Division (Korea, Republic of); Pikhitsa, Peter V. [Seoul National University, School of Mechanical and Aerospace Engineering (Korea, Republic of); Cho, Myung-Haing, E-mail: mchotox@snu.ac.kr [Seoul National University, Laboratory of Toxicology, College of Veterinary Medicine (Korea, Republic of); Choi, Mansoo, E-mail: mchoi@snu.ac.kr [Seoul National University, School of Mechanical and Aerospace Engineering (Korea, Republic of)

    2015-09-15

    The cellular toxicity of multi-walled carbon nanotubes (MWCNTs) and onion-like shell-shaped carbon nanoparticles (SCNPs) was investigated by analyzing the comparative cell viability. For the reasonable comparison, physicochemical characteristics were controlled thoroughly such as crystallinity, carbon bonding characteristic, hydrodynamic diameter, and metal contents of the particles. To understand relation between cellular toxicity of the particles and generation of reactive oxygen species (ROS), we measured unpaired singlet electrons of the particles and intracellular ROS, and analyzed cellular toxicity with/without the antioxidant N-acetylcysteine (NAC). Regardless of the presence of NAC, the cellular toxicity of SCNPs was found to be lower than that of MWCNTs. Since both particles show similar crystallinity, hydrodynamic size, and Raman signal with negligible contribution of remnant metal particles, the difference in cell viability would be ascribed to the difference in morphology, i.e., spherical shape (aspect ratio of one) for SCNP and elongated shape (high aspect ratio) for MWCNT.

  17. Comparison of cellular toxicity between multi-walled carbon nanotubes and onion-like shell-shaped carbon nanoparticles

    International Nuclear Information System (INIS)

    Kang, Seunghyon; Kim, Ji-Eun; Kim, Daegyu; Woo, Chang Gyu; Pikhitsa, Peter V.; Cho, Myung-Haing; Choi, Mansoo

    2015-01-01

    The cellular toxicity of multi-walled carbon nanotubes (MWCNTs) and onion-like shell-shaped carbon nanoparticles (SCNPs) was investigated by analyzing the comparative cell viability. For the reasonable comparison, physicochemical characteristics were controlled thoroughly such as crystallinity, carbon bonding characteristic, hydrodynamic diameter, and metal contents of the particles. To understand relation between cellular toxicity of the particles and generation of reactive oxygen species (ROS), we measured unpaired singlet electrons of the particles and intracellular ROS, and analyzed cellular toxicity with/without the antioxidant N-acetylcysteine (NAC). Regardless of the presence of NAC, the cellular toxicity of SCNPs was found to be lower than that of MWCNTs. Since both particles show similar crystallinity, hydrodynamic size, and Raman signal with negligible contribution of remnant metal particles, the difference in cell viability would be ascribed to the difference in morphology, i.e., spherical shape (aspect ratio of one) for SCNP and elongated shape (high aspect ratio) for MWCNT

  18. Electrocatalysis of oxygen reduction on nitrogen-containing multi-walled carbon nanotube modified glassy carbon electrodes

    International Nuclear Information System (INIS)

    Vikkisk, Merilin; Kruusenberg, Ivar; Joost, Urmas; Shulga, Eugene; Tammeveski, Kaido

    2013-01-01

    Highlights: ► Pyrolysis in the presence of urea was used for nitrogen doping of carbon nanotubes. ► N-doped carbon nanotubes were used as catalysts for the oxygen reduction reaction. ► N-doped carbon material showed a high catalytic activity for ORR in alkaline media. ► N-containing CNT material is an attractive cathode catalyst for alkaline membrane fuel cells. - Abstract: The electrochemical reduction of oxygen was studied on nitrogen-doped multi-walled carbon nanotube (NCNT) modified glassy carbon (GC) electrodes employing the rotating disk electrode (RDE) method. Nitrogen doping was achieved by simple pyrolysis of the carbon nanotube material in the presence of urea. The surface morphology and composition of the NCNT samples were investigated by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The SEM images revealed a rather uniform distribution of NCNTs on the GC electrode substrate. The XPS analysis showed a successful doping of carbon nanotubes with nitrogen species. The RDE results revealed that in alkaline solution the N-doped nanotube materials showed a remarkable electrocatalytic activity towards oxygen reduction. At low overpotentials the reduction of oxygen followed a two-electron pathway on undoped carbon nanotube modified GC electrodes, whereas on NCNT/GC electrodes a four-electron pathway of O 2 reduction predominated. The results obtained are significant for the development of nitrogen-doped carbon-based cathodes for alkaline membrane fuel cells.

  19. Enhancement of heat transfer for thermal energy storage application using stearic acid nanocomposite with multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    Li, TingXian; Lee, Ju-Hyuk; Wang, RuZhu; Kang, Yong Tae

    2013-01-01

    A latent heat storage nanocomposite made of stearic acid (SA) and multi-walled carbon nanotube (MWCNT) is prepared for thermal energy storage application. The thermal properties of the SA/MWCNT nanocomposite are characterized by SEM (scanning electron microscopy) and DSC (differential scanning calorimeter) analysis techniques, and the effects of different volume fractions of MWCNT on the heat transfer enhancement and thermal performance of stearic acid are investigated during the charging and discharging phases. The SEM analysis shows that the additive of MWCNT is uniformly distributed in the phase change material of stearic acid, and the DSC analysis reveals that the melting point of SA/MWCNT nanocomposite shifts to a lower temperature during the charging phase and the freezing point shifts to a higher temperature during the discharging phase when compared with the pure stearic acid. The experimental results show that the addition of MWCNT can improve the thermal conductivity of stearic acid effectively, but it also weakens the natural convection of stearic acid in liquid state. In comparison with the pure stearic acid, the charging rate can be decreased by about 50% while the discharging rate can be improved by about 91% respectively by using the SA/5.0% MWCNT nanocomposite. It appears that the MWCNT is a promising candidate for enhancing the heat transfer performance of latent heat thermal energy storage system. - Highlights: • A nanocomposite made of stearic acid and multi-walled carbon nanotube is prepared for thermal energy storage application. • Effects of multi-walled carbon nanotube on the thermal performance of the nanocomposite are investigated. • Multi-walled carbon nanotube enhances the thermal conductivity but weakens the natural convection of stearic acid. • Discharging/charging rates of stearic acid are increased/decreased by using multi-walled carbon nanotube

  20. Evaluating the biological risk of functionalized multiwalled carbon nanotubes and functionalized oxygen-doped multiwalled carbon nanotubes as possible toxic, carcinogenic, and embryotoxic agents

    Directory of Open Access Journals (Sweden)

    Lara-Martínez LA

    2017-10-01

    Full Text Available Luis A Lara-Martínez,1 Felipe Massó,2 Eduardo Palacios González,3 Isabel García-Peláez,4 Alejandra Contreras–Ramos,5 Mahara Valverde,6 Emilio Rojas,6 Felipe Cervantes-Sodi,7 Salomón Hernández-Gutiérrez1 1Department of Molecular Biology, School of Medicine, Universidad Panamericana, Mexico City, Mexico; 2Department of Physiology, National Institute of Cardiology Ignacio Chavez, Mexico City, Mexico; 3Department of Microscopy, Ultra High Resolution Electron Microscopy Laboratory, Instituto Mexicano del Petróleo, Mexico City, Mexico; 4Department of Embryology, Medicine Faculty, Universidad Nacional Autonoma de Mexico, Mexico City, Mexico; 5Department of Developmental Biology Research and Experimental Teratogenicity, Children’s Hospital of Mexico, Federico Gomez, Mexico City, Mexico; 6Department of Genomic Medicine, Institute of Biomedical Research, Universidad Nacional Autonoma de Mexico, Mexico City, Mexico; 7Department of Physics and Mathematics, Nanoscience and Nanotechnology Laboratory, Universidad Iberoamericana, Mexico City, Mexico Abstract: Carbon nanotubes (CNTs have been a focus of attention due to their possible applications in medicine, by serving as scaffolds for cell growth and proliferation and improving mesenchymal cell transplantation and engraftment. The emphasis on the benefits of CNTs has been offset by the ample debate on the safety of nanotechnologies. In this study, we determine whether functionalized multiwalled CNTs (fMWCNTs and functionalized oxygen-doped multiwalled CNTs (fCOxs have toxic effects on rat mesenchymal stem cells (MSCs in vitro by analyzing morphology and cell proliferation and, using in vivo models, whether they are able to transform MSCs in cancer cells or induce embryotoxicity. Our results demonstrate that there are statistically significant differences in cell proliferation and the cell cycle of MSCs in culture. We identified dramatic changes in cells that were treated with fMWCNTs. Our

  1. Cellular cytotoxic response induced by highly purified multi-wall carbon nanotube in human lung cells.

    Science.gov (United States)

    Tsukahara, Tamotsu; Haniu, Hisao

    2011-06-01

    Carbon nanotubes, a promising nanomaterial with unique characteristics, have applications in a variety of fields. The cytotoxic effects of carbon nanotubes are partially due to the induction of oxidative stress; however, the detailed mechanisms of nanotube cytotoxicity and their interaction with cells remain unclear. In this study, the authors focus on the acute toxicity of vapor-grown carbon fiber, HTT2800, which is one of the most highly purified multi-wall carbon nanotubes (MWCNT) by high-temperature thermal treatment. The authors exposed human bronchial epithelial cells (BEAS-2B) to HTT2800 and measured the cellular uptake, mitochondrial function, cellular LDH release, apoptotic signaling, reactive oxygen species (ROS) generation and pro-inflammatory cytokine release. The HTT2800-exposed cells showed cellular uptake of the carbon nanotube, increased cell death, enhanced DNA damage, and induced cytokine release. However, the exposed cells showed no obvious intracellular ROS generation. These cellular and molecular findings suggest that HTT2800 could cause a potentially adverse inflammatory response in BEAS-2B cells.

  2. Silica-coated multi-walled carbon nanotubes impregnated with polyethyleneimine for carbon dioxide capture under the flue gas condition

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Min-Sang; Park, Soo-Jin, E-mail: sjpark@inha.ac.kr

    2015-03-15

    In this study, silica-coated multi-walled carbon nanotubes impregnated with polyethyleneimine (PEI) were prepared via a two-step process: (i) hydrolysis of tetraethylorthosilicate onto multi-walled carbon nanotubes, and (ii) impregnation of PEI. The adsorption properties of CO{sub 2} were investigated using CO{sub 2} adsorption–desorption isotherms at 298 K and thermogravimetric analysis under the flue gas condition (15% CO{sub 2}/85% N{sub 2}). The results obtained in this study indicate that CO{sub 2} adsorption increases after impregnation of PEI. The increase in CO{sub 2} capture was attributed to the affinity between CO{sub 2} and the amine groups. CO{sub 2} adsorption–desorption experiments, which were repeated five times, also showed that the prepared adsorbents have excellent regeneration properties. - Graphical abstract: Fabrication and CO{sub 2} adsorption process of the S-MWCNTs impregnated with PEI. - Highlights: • Silica coated-MWCNT impregnated with PEI was synthesized. • Amine groups of PEI gave CO{sub 2} affinity sites on MWCNT surfaces. • The S-MWCNT/PEI(50) exhibited the highest CO{sub 2} adsorption capacity.

  3. Highly enhanced vapor sensing of multi-walled carbon nanotube network sensors by n-butylamine functionalization

    Czech Academy of Sciences Publication Activity Database

    Slobodian, P.; Říha, Pavel; Cavallo, P.; Barbero, C.A.; Cvelbar, U.; Benlikaya, R.; Petras, D.; Sáha, P.

    2014-01-01

    Roč. 2014, August (2014), Article ID 589627 ISSN 1687-4110 Grant - others:UTB Zlín(CZ) IGA/FT/2014/013; GA MŠk(CZ) ED2.1.00/03.0111; GA MŠk(CZ) 7AMB13AR019 Institutional support: RVO:67985874 Keywords : carbon nanotube (CNT) * multiwall carbon nanotube (MWCNT) * nanotube networks * volatile organic compounds (VOC) Subject RIV: BK - Fluid Dynamics Impact factor: 1.644, year: 2014

  4. Blood compatibility of gas plasma-treated diamond-like carbon surface-Effect of physicochemical properties of DLC surface on blood compatibility

    International Nuclear Information System (INIS)

    Mochizuki, Akira; Ogawa, Tatsuhisa; Okamoto, Keishi; Nakatani, Tatsuyuki; Nitta, Yuki

    2011-01-01

    From the knowledge that zwitterion-type polymers show good blood compatibility, the introduction of both cationic and anionic functional groups onto diamond-like carbon (DLC) surface is expected to improve blood compatibility. Thus, DLC films were treated with oxygen and ammonia gas plasmas. The surfaces were characterized in terms of chemical composition by XPS, contact angle, and zeta potential. XPS analysis showed the introductions of a carboxyl group by oxygen plasma treatment and nitrogen atoms by ammonia plasma treatment. The evaluation of blood compatibility for the DLC surfaces was carried out in terms of platelets and the coagulation system. Excellent improvement of platelet compatibility was observed by the treatment with the gas plasmas, regardless of the plasma species. As for the compatibility with the coagulation system, DLC surfaces with a high concentration of carboxyl groups (COOH) markedly activated the system via the intrinsic pathway. However, the surfaces treated with ammonia plasma did not activate the system even though they had high COOH concentration. Measurement of the zeta potential revealed that the ammonia plasma treatment raised the potential from a negative value to a positive one. Though the introduction of amino groups to the surface was not detected directly, the treatment of ammonia plasma changed the electrical state of the DLC surface having COOH group, causing a difference in blood compatibility among the DLCs obtained by various plasma conditions.

  5. Immobilization of Aspergillus niger cellulase on multiwall carbon nanotubes for cellulose hydrolysis.

    Science.gov (United States)

    Ahmad, Razi; Khare, Sunil Kumar

    2018-03-01

    In present study, Aspergillus niger cellulase was immobilized onto functionalized multiwalled carbon nanotubes (MWCNTs) via carbodiimide coupling. MWCNTs offer unique advantages including enhanced electronics properties, a large edge to basal plane ratio, rapid electrode kinetics and it's possess higher tensile strength properties due to their structural arrangements. The immobilization was confirmed by FTIR (Fourier transform infrared spectroscopy) and SEM (scanning electron microscope). The bionanoconjugates prepared under optimized condition retained 85% activity with improved pH and thermal stability. The t 1/2 of immobilized cellulase at 70 °C was four fold higher than free enzyme. The Km value indicates that affinity of bionanoconjugates towards substrate has increased by two times. The preparation could be reused ten times without much loss in enzyme activity. The enhanced catalytic efficiency, stability and reusability makes it useful for efficient cellulose hydrolysis. Copyright © 2017 Elsevier Ltd. All rights reserved.

  6. In situ coating multiwalled carbon nanotubes with CdS nanoparticles

    International Nuclear Information System (INIS)

    Liu Yangqiao; Gao Lian

    2005-01-01

    CdS nanoparticles were homogeneously coated on multiwalled carbon nanotubes by an in situ method through introducing thiol groups onto the tube wall using a novel method. A cationic polyelectrolyte containing reactive imine groups, polyethyleneimine (PEI), was firstly adsorbed on the surface of nanotubes. 3-Mercaptopropionic acid (MPA) was then anchored by an amidation reaction between its carboxyl group and the imine group of the polyelectrolyte under the activation of carbodiimide reagents. These -SH terminated MWCNTs were coated with CdS nanoparticles by an in situ method. The phase composition, microstructure, and the UV-vis properties of the CdS coated MWCNTs were characterized. The addition of the carbodiimide reagents played an important role in linking the MPA with PEI covalently and subsequently coating the MWCNTs with CdS homogeneously. A blue shift in the absorption edge was observed for the MWCNTs-CdS hybrid material due to the quantum size effect

  7. Angle-dependent light emission from aligned multiwalled carbon nanotubes under CO2 laser irradiation

    International Nuclear Information System (INIS)

    Zhang, Y; Gong, T; Liu, W J; Wei, J Q; Zhang, X F; Wang, K L; Zhong, M L; Wu, D H

    2007-01-01

    This paper reports the light emission from aligned multiwalled carbon nanotubes (MWNTs) under continuous wave CO 2 laser (λ = 10.6 μm) irradiation. Results indicate that the light emission is dependent on the angle θ between the laser incident direction and the nanotube axis. The relative intensity of the light emission at certain wavelengths shows a Lorentzian feature when θ varies from 0 0 to 90 0 . The Lorentzian fitting curve displays a distinct tendency between shorter (λ 700 nm). A minimum intensity was observed at θ m close to 67 0 under shorter wavelength, whereas a maximum intensity was shown at θ m of about 60 0 at longer wavelength. These results show the anisotropic property of aligned MWNTs

  8. Superior Performance Nanocomposites from Uniformly Dispersed Octadecylamine Functionalized Multi-Walled Carbon Nanotubes

    KAUST Repository

    Chen, Ye

    2015-12-08

    Polyetherimide (PEI) is a widely applied as engineering plastic in the electronics, aerospace, and automotive industries but the disadvantages of extremely low conductivity, atmospheric moisture absorption, and poor fluidity at high temperature limits its application. Herein, commercial multi-walled carbon nanotubes (MWCNTs) were modified with a long alkyl chain molecule, octadecylamine (ODA), to produce a uniform dispersion in commercial PEI matrices. Both covalent and noncovalent modification of MWCNTs with ODA, were prepared and compared. Modified MWCNTs were incorporated in PEI matrices to fabricate nanocomposite membranes by a simple casting method. Investigating mechanical properties, thermal stability, and conductivity of the polyetherimide (PEI)/MWCNT composites showed a unique combination of properties, such as high electrical conductivity, high mechanical properties, and high thermal stability at a low content of 1.0 wt % loading of ODA modified MWCNTs. Moreover, electrical resistivity decreased around 10 orders of magnitude with only 0.5 wt % of modified MWCNTs.

  9. Hydrogen storage in microwave-treated multi-walled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Geng, Hong-Zhang [BK21 Physics Division, Department of Energy Science, Center for Nanotubes and Nanostructured Composites, Sungkyunkwan Advanced Institute of Nanotechnology, Sungkyunkwan University, Suwon 440-746 (Korea); School of Materials Science and Engineering, Tianjin Polytechnic University, Tianjin 300160 (China); Kim, Tae Hyung; Lim, Seong Chu; Jeong, Hae-Kyung; Jin, Mei Hua; Jo, Young Woo; Lee, Young Hee [BK21 Physics Division, Department of Energy Science, Center for Nanotubes and Nanostructured Composites, Sungkyunkwan Advanced Institute of Nanotechnology, Sungkyunkwan University, Suwon 440-746 (Korea)

    2010-03-15

    Multiwalled carbon nanotubes (MWCNTs) treated by microwave and heat treatment were used for hydrogen storage. Their storage capacity was measured using a quadruple quartz crystal microbalance in a moisture-free chamber at room temperature and at relatively low pressure (0.5 MPa). Deuterium was also used to monitor the presence of moisture. The hydrogen storage capacity of the microwave-treated MWCNTs was increased to nearly 0.35 wt% over 0.1 wt% for the pristine sample and increased further to 0.4 wt%, with improved stability after subsequent heat-treatment. The increase in the storage capacity by the microwave treatment was mostly attributed to the introduction of micropore surfaces, while the stability improvement after the subsequent heat treatment was related to the removal of functional groups. We also propose a measurement method that eliminates the moisture effect by measuring the storage capacity with hydrogen and deuterium gas. (author)

  10. Effects of interfaces on nano-friction of vertically aligned multi-walled carbon nanotube arrays

    International Nuclear Information System (INIS)

    Lou, J.; Kim, K.-S.

    2008-01-01

    Sliding friction properties of vertically aligned multi-walled carbon nanotube (VAMWNT) arrays have been investigated in current study in a quantitative manner. The VAMWNT arrays have been fabricated on an anodic aluminum oxide template by chemical vapor deposition at 650 deg. C. Friction force was measured in air by a modified atomic force microscopy (AFM) cantilever-bead assembly with 15 μm diameter borosilicate sphere attached to the end of the regular AFM cantilever. Quantitative measurements were achieved by using a novel in situ calibration methods recently developed based on diamagnetic levitation [Q. Li, K.-S. Kim, A. Rydberg, Rev. Sci. Instrum. 77 (2006) 065105-1-13]. The effects of different interfaces were studied using both cantilever-bead assembly coated with and without Al thin layer coatings. A reverse stick-slip behavior was observed in the current system as compared to the normal stick-slip behavior found in the literature

  11. Strong adhesion of Saos-2 cells to multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    Matsuoka, Makoto; Akasaka, Tsukasa; Totsuka, Yasunori; Watari, Fumio

    2010-01-01

    In recent years, carbon nanotubes (CNTs) have been considered potential biomedical materials because of their unique character. The aim of this study was to investigate the response of a human osteoblast-like cell line - Saos-2 - on single-walled CNTs (SWCNTs) and multi-walled CNTs (MWCNTs). The surface of a culture dish was coated with CNTs, and Saos-2 cells were cultured for three days. Cell morphology, viability, alkaline phosphatase (ALP) activity, adhesion, and vinculin expression were evaluated. The result showed high cell viability and strong adhesion to MWCNTs. Saos-2 cultured on MWCNTs exhibited vinculin expression throughout the cell body, while the cells attached to SWCNTs and glass were mostly limited to their periphery. Our results suggest that CNT coatings promote cell activity and adhesiveness. These findings indicate that MWCNTs could be used as surface coating materials to promote cell adhesion.

  12. Poly(lauryl acrylate) and poly(stearyl acrylate) grafted multiwalled carbon nanotubes for polypropylene composites

    DEFF Research Database (Denmark)

    Daugaard, Anders Egede; Jankova Atanasova, Katja; Hvilsted, Søren

    2014-01-01

    Two new polymer grafts on an industrial grade multiwalled carbon nanotube (MWCNT) were prepared through a non-oxidative pathway employing controlled free radical polymerization for surface initiated polymer grafting. After photochemical introduction of an ATRP initiator onto the MWCNT......, polymerizations of lauryl or stearyl acrylate were performed, resulting in two novel polymer modifications on the MWCNT (poly(lauryl acrylate) or poly(stearyl acrylate)). The method was found to give time dependent loading of polymers as a function of time (up to 38 wt% for both acrylates), and showed a plateau...... in loading after 12 h of polymerization. The modified nanomaterials were melt mixed into polypropylene composites with very low filler loading (0.3 wt%), whereafter both the thermal and electrical properties were investigated by DSC and dielectric resonance spectroscopy. The electrical properties were found...

  13. Effects of gas composition on the growth of multi-walled carbon nanotube

    International Nuclear Information System (INIS)

    Fang, T.-H.; Chang, W.-J.; Lu, D.-M.; Lien, W.-C.

    2007-01-01

    This paper studies the effects of different gas compositions on the growth of multi-walled carbon nanotube (MWCNT) films by using an electron cyclotron resonance chemical vapor deposition (ECR-CVD) method. The Raman spectrum was employed to explore the composition of the MWCNT films grown under different mixtures of C 3 H 8 and H 2 . The results showed that the optimum relative intensity ratio of the D band to G band (i.e., I D /I G ) is 2 for the cases considered in this study. In addition, the morphology and microstructure of the MWCNTs were examined by field emission scanning electron microscopy (FE-SEM) and field emission gun transmission electron microscopy (FEG-TEM). Furthermore, atomic force microscopy (AFM) and scanning thermal microscopy (SThM) were used to study the surface topography and thermal properties of the MWCNTs

  14. Electrophoretically deposited multiwalled carbon nanotube based amperometric genosensor for E.coli detection

    International Nuclear Information System (INIS)

    Bhardwaj, Hema; Solanki, Shipra; Sumana, Gajjala

    2016-01-01

    This work reports on a sensitive and selective genosensor fabrication method for Escherichia coli ( E.coli) detection. The functionalized multiwalled carbon nanotubes (MWCNT) synthesized via chemical vapour deposition have been deposited electrophoretically onto indium tin oxide coated glass surface and have been utilized as matrices for the covalent immobilization of E.coli specific probe oligonucleotide that was identified from the 16s rRNA coding region of the E.coli genome. This fabricated functionalized MWCNT based platform sought to provide improved fundamental characteristics to electrode interface in terms of electro-active surface area and diffusion coefficient. Electrochemical cyclic voltammetry revealed that this genosensor exhibits a linear response to complementary DNA in the concentration range of 10 -7 to 10 -12 M with a detection limit of 1×10 -12 M. (paper)

  15. Superior Performance Nanocomposites from Uniformly Dispersed Octadecylamine Functionalized Multi-Walled Carbon Nanotubes

    KAUST Repository

    Chen, Ye; Tao, Jing; Ezzeddine, Alaa; Mahfouz, Remi; Al-Shahrani, Abdullah; Alabedi, Gasan; Khashab, Niveen M.

    2015-01-01

    Polyetherimide (PEI) is a widely applied as engineering plastic in the electronics, aerospace, and automotive industries but the disadvantages of extremely low conductivity, atmospheric moisture absorption, and poor fluidity at high temperature limits its application. Herein, commercial multi-walled carbon nanotubes (MWCNTs) were modified with a long alkyl chain molecule, octadecylamine (ODA), to produce a uniform dispersion in commercial PEI matrices. Both covalent and noncovalent modification of MWCNTs with ODA, were prepared and compared. Modified MWCNTs were incorporated in PEI matrices to fabricate nanocomposite membranes by a simple casting method. Investigating mechanical properties, thermal stability, and conductivity of the polyetherimide (PEI)/MWCNT composites showed a unique combination of properties, such as high electrical conductivity, high mechanical properties, and high thermal stability at a low content of 1.0 wt % loading of ODA modified MWCNTs. Moreover, electrical resistivity decreased around 10 orders of magnitude with only 0.5 wt % of modified MWCNTs.

  16. Ultraviolet pulsed laser irradiation of multi-walled carbon nanotubes in nitrogen atmosphere

    Energy Technology Data Exchange (ETDEWEB)

    Pérez del Pino, Ángel, E-mail: aperez@icmab.es; Cabana, Laura; Tobias, Gerard [Instituto de Ciencia de Materiales de Barcelona, Consejo Superior de Investigaciones Científicas (ICMAB-CSIC), Campus UAB, 08193 Bellaterra (Spain); György, Enikö [Instituto de Ciencia de Materiales de Barcelona, Consejo Superior de Investigaciones Científicas (ICMAB-CSIC), Campus UAB, 08193 Bellaterra (Spain); National Institute for Lasers, Plasma and Radiation Physics, P. O. Box MG 36, 76900 Bucharest V (Romania); Ballesteros, Belén [ICN2—Institut Catala de Nanociencia i Nanotecnologia, Campus UAB, 08193 Bellaterra, Barcelona (Spain)

    2014-03-07

    Laser irradiation of randomly oriented multi-walled carbon nanotube (MWCNT) networks has been carried out using a pulsed Nd:YAG UV laser in nitrogen gas environment. The evolution of the MWCNT morphology and structure as a function of laser fluence and number of accumulated laser pulses has been studied using electron microscopies and Raman spectroscopy. The observed changes are discussed and correlated with thermal simulations. The obtained results indicate that laser irradiation induces very fast, high temperature thermal cycles in MWCNTs which produce the formation of different nanocarbon forms, such as nanodiamonds. Premelting processes have been observed in localized sites by irradiation at low number of laser pulses and low fluence values. The accumulation of laser pulses and the increase in the fluence cause the full melting and amorphization of MWCNTs. The observed structural changes differ from that of conventional high temperature annealing treatments of MWCNTs.

  17. Vertically aligned multiwalled carbon nanotubes for pressure, tactile and vibration sensing.

    Science.gov (United States)

    Yilmazoglu, O; Popp, A; Pavlidis, D; Schneider, J J; Garth, D; Schüttler, F; Battenberg, G

    2012-03-02

    We report a simple method for the micro-nano integration of flexible, vertically aligned multiwalled CNT arrays sandwiched between a top and bottom carbon layer via a porous alumina (Al(2)O(3)) template approach. The electromechanical properties of the flexible CNT arrays have been investigated under mechanical stress conditions. First experiments show highly sensitive piezoresistive sensors with a resistance decrease of up to ∼35% and a spatial resolution of <1 mm. The results indicate that these CNT structures can be utilized for tactile sensing components. They also confirm the feasibility of accessing and utilizing nanoscopic CNT bundles via lithographic processing. The method involves room-temperature processing steps and standard microfabrication techniques.

  18. In situ Raman spectroscopy for growth monitoring of vertically aligned multiwall carbon nanotubes in plasma reactor

    Energy Technology Data Exchange (ETDEWEB)

    Labbaye, T.; Gaillard, M.; Lecas, T.; Kovacevic, E.; Boulmer-Leborgne, Ch.; Guimbretière, G. [GREMI, Université-CNRS, BP6744, 45067 Orléans Cedex 2 (France); Canizarès, A.; Raimboux, N.; Simon, P.; Ammar, M. R., E-mail: mohamed-ramzi.ammar@cnrs-orleans.fr [CNRS, CEMHTI UPR3079, Univ. Orléans, F-45071 Orléans Cedex 2 (France); Strunskus, T. [Institute of Material Science, Chritian-Albrechts-University of Kiel, D-24143 Kiel (Germany)

    2014-11-24

    Portable and highly sensitive Raman setup was associated with a plasma-enhanced chemical vapor deposition reactor enabling in situ growth monitoring of multi-wall carbon nanotubes despite the combination of huge working distance, high growth speed and process temperature and reactive plasma condition. Near Edge X-ray absorption fine structure spectroscopy was used for ex situ sample analysis as a complementary method to in situ Raman spectroscopy. The results confirmed the fact that the “alternating” method developed here can accurately be used for in situ Raman monitoring under reactive plasma condition. The original analytic tool can be of great importance to monitor the characteristics of these nanostructured materials and readily define the ultimate conditions for targeted results.

  19. Proposed model for biomineralization of novel nanohydroxyapatite/vertically aligned multiwalled carbon nanotube scaffolds

    Directory of Open Access Journals (Sweden)

    Tayra Rodrigues Brazil

    2013-06-01

    Full Text Available For the first time, the growth mechanism of biominerals formed on plate-like nanohydroxyapatite (nHAp electrodeposited on superhydrophilic vertically aligned multi-walled carbon nanotubes (VAMWCNT-O2 is presented and a model for the specific growth preference is discussed. VAMWCNT-O2 films were obtained by microwave-assisted chemical vapor deposition method and funcionalized by oxygen plasma. nHAp/VAMWCNT-O2 nanocomposites were fabricated with a direct electrodeposition of the thin nHAp films onto the VAMWCNT-O2 films. The biomineralized "scaffolds" were obtained by soaking nHAp/VAMWCNT-O2 in simulated body fluid for 7, 14 and 21 days. Results show that the carboxyl functional groups directly attached onto VAMWCNT tips after oxygen plasma treatment were essential for the acceleration of the OH- formation and the deposition of plate-like nHAp crystals.

  20. Calcification in vitro of biomineralizated nanohydroxyapatite/superydrophilic vertically aligned multiwalled carbon nanotube scaffolds

    Directory of Open Access Journals (Sweden)

    Marcele Florencio Neves

    2013-06-01

    Full Text Available Nanocomposites based on superhydrophilic vertically aligned multi-walled carbon nanotubes (VAMWCNT-O2 and nanohydroxyapatite (nHAp are of great interest in bone regenerative medicine. The biomineralization using simulated body fluid (SBF has been extensively studied to evaluate the bioactivity of biomaterials. Thus, the combination of nHAp and VAMWCNT-O2 is attractive and promising. The aim of this study was to evaluate the in vitro calcification of nHAp/VAMWCNT-O2 nanocomposites before and after the period of biomineralization in SBF. In vitro calcification of the extracellular matrix (ECM of HOB cells in culture after 24 hours was investigated through the assay of alkaline phosphatase. These promising in vitro results validate biomineralized nHAp/VAMWCNT-O2 as possible scaffolds for bone tissue regeneration.

  1. Simple quantification of surface carboxylic acids on chemically oxidized multi-walled carbon nanotubes

    Science.gov (United States)

    Gong, Hyejin; Kim, Seong-Taek; Lee, Jong Doo; Yim, Sanggyu

    2013-02-01

    The surface of multi-walled carbon nanotube (MWCNT) was chemically oxidized using nitric acid and sulfuric-nitric acid mixtures. Thermogravimetric analysis, transmission electron microscopy and infrared spectroscopy revealed that the use of acid mixtures led to higher degree of oxidation. More quantitative identification of surface carboxylic acids was carried out using X-ray photoelectron spectroscopy (XPS) and acid-base titration. However, these techniques are costly and require very long analysis times to promptly respond to the extent of the reaction. We propose a much simpler method using pH measurements and pre-determined pKa value in order to estimate the concentration of carboxylic acids on the oxidized MWCNT surfaces. The results from this technique were consistent with those obtained from XPS and titration, and it is expected that this simple quantification method can provide a cheap and fast way to monitor and control the oxidation reaction of MWCNT.

  2. Effect of chemical treatments on hydrogen storage behaviors of multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    Lee, Seul-Yi; Park, Soo-Jin

    2010-01-01

    In this work, the hydrogen storage behaviors of chemically treated multi-walled carbon nanotubes (MWNTs) were investigated. The surface properties of the functionalized MWNTs were confirmed by Fourier transfer infrared spectroscopy, X-ray diffraction, the Boehm titration method, and zeta-potential measurements. The hydrogen storage capacity of the MWNTs was evaluated at 298 K and 100 bar. In the experimental results, it was found that the chemical treatments introduced functional groups onto the MWNT surfaces. The amount of hydrogen storage was enhanced, by acidic surface treatment, to 0.42 wt.% in the acidic-treated MWNTs compared with 0.26 wt.% in the as-received MWNTs. Meanwhile, the basic surface treatment actually reduced the hydrogen storage capacity, to 0.24 wt.% in the basic-treated MWNTs sample. Consequently, it could be concluded that hydrogen storage is greatly influenced by the acidic characteristics of MWNT surfaces, resulting in enhanced electron acceptor-donor interaction at interfaces.

  3. Highly conductive, transparent flexible films based on open rings of multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    Ko, Wen-Yin; Su, Jun-Wei; Guo, Chian-Hua; Fu, Shu-Juan; Hsu, Chuen-Yuan; Lin, Kuan-Jiuh

    2011-01-01

    Open rings of multi-walled carbon nanotubes were stacked to form porous networks on a poly(ethylene terephthalate) substrate to form a flexible conducting film (MWCNT-PET) with good electrical conductivity and transparency by a combination of ultrasonic atomization and spin-coating technique. To enhance the electric flexibility, we spin-coated a cast film of poly(vinyl alcohol) onto the MWCNT-PET substrate, which then underwent a thermo-compression process. Field-emission scanning electron microscopy of the cross-sectional morphology illustrates that the film has a robust network with a thickness of ∼ 175 nm, and it remarkably exhibits a sheet resistance of approximately 370 Ω/sq with ∼ 77% transmittance at 550 nm even after 500 bending cycles. This electrical conductivity is much superior to that of other MWCNT-based transparent flexible films.

  4. MnO2/multiwall carbon nanotube/Ni-foam hybrid electrode for electrochemical capacitor

    Science.gov (United States)

    Chen, L. H.; Li, L.; Qian, W. J.; Dong, C. K.

    2018-01-01

    The ternary composites of manganese dioxide/multiwall carbon nanotube/Ni-foam (MnO2/MWNT/Ni-foam) for supercapacitors were fabricated via a hydrothermal method after direct growth of MWNTs on the Ni-foam. The structural properties of the electrodes were characterized by SEM and TEM. The electrode exhibited excellent electrochemical properties from the investigation based on the three-electrode setup. Low contact resistance Rs of about 0.291 Ω between MnO2/MWNT and Ni-foam was reached benefited from the direct growth structure. High capacitance of 355.1 F/g at the current density of 2 A/g was achieved, with good capacitive response at high current density. The MnO2/MWNT/Ni-foam electrode exhibits good stability performance after 2000 cycles at a current of 40 mA.

  5. Dry-Transfer of Aligned Multiwalled Carbon Nanotubes for Flexible Transparent Thin Films

    Directory of Open Access Journals (Sweden)

    Matthew Cole

    2012-01-01

    Full Text Available Herein we present an inexpensive facile wet-chemistry-free approach to the transfer of chemical vapour-deposited multiwalled carbon nanotubes to flexible transparent polymer substrates in a single-step process. By controlling the nanotube length, we demonstrate accurate control over the electrical conductivity and optical transparency of the transferred thin films. Uniaxial strains of up to 140% induced only minor reductions in sample conductivity, opening up a number of applications in stretchable electronics. Nanotube alignment offers enhanced functionality for applications such as polarisation selective electrodes and flexible supercapacitor substrates. A capacitance of 17 F/g was determined for supercapacitors fabricated from the reported dry-transferred MWCNTs with the corresponding cyclic voltagrams showing a clear dependence on nanotube length.

  6. The functionalization and characterization of multi-walled carbon nanotubes (MWCNTs)

    Energy Technology Data Exchange (ETDEWEB)

    Abdullah, Mohd Pauzi [School of Chemical Sciences and Food Technology, Faculty Science and Technology, Universiti Kebangsaan Malaysia, 43600, Bangi, Selangor (Malaysia); Center of Water Analysis and Research (ALIR), Universiti Kebangsaan Malaysia, 43600, Bangi, Selangor (Malaysia); Zulkepli, Siti Aminah [School of Chemical Sciences and Food Technology, Faculty Science and Technology, Universiti Kebangsaan Malaysia, 43600, Bangi, Selangor (Malaysia)

    2015-09-25

    Functionalization is the process of introducing chemical functional groups on the surface of the material. In this study, a multi-walled carbon nanotube (MWCNTs) was functionalized by oxidation treatment using concentrated nitric acid. The functionalized and pristine MWCNTs were analyzed by using Fourier Transform Infrared Spectroscopy (FT-IR) and X-Ray Diffraction (XRD). The XRD patterns exhibit the graphitic properties for all samples. Besides, the XRD results also demonstrate that the percent of crystallinity of MWCNTs increases as the duration of acid treatment increases. The percent of crystallinity increases from 66% to 80% when the pristine MWCNT treated for 12 hours with additional 12 hours reflux process with nitric acid. The IR spectrum for the 12 hours-treated MWCNTs shows the formation of carboxyl functional group. Additional 12 hours reflux process with nitric acid on the 12 hours-treated MWCNTs have shown the loss of existing carboxyl group and only hydroxyl group formed.

  7. Removal of copper ions from water using chemical modified multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    Zhang, Y.J.; Yang, J.

    2014-01-01

    Multi-walled carbon nanotubes (CNTs) were modified by oxidation with sodium hypochlorite (NaClO) solutions and were employed as adsorbents to study the adsorption characteristics of copper ions from water. The results show that adsorption capacity of CNTs treated by NaClO solution can be greatly enhanced. The adsorption capacity of Cu2+ on as received and modified CNTs increased with the increase of pH and CNTs mass, but it decreased with the temperature. Experimental data also indicated that the adsorption process could achieve equilibrium within 40 min. Both Langmuir and Freundlich isotherm models fitted the experimental data very well. According to the Langmuir model the maximum copper ions adsorption uptake onto modified CNTs was determined as 40.00 mg/g. Our results suggest that CNTs have profound potential application in environmental protection. (author)

  8. The origin of polarized blackbody radiation from resistively heated multiwalled carbon nanotubes

    International Nuclear Information System (INIS)

    Aliev, Ali E.; Kuznetsov, Alexander A.

    2008-01-01

    We observed very pronounced polarization of light emitted by highly aligned free-standing multiwall carbon nanotube (MWNT) sheet in axial direction which is turned to the perpendicular polarization when a number of layers are increased. The radiation spectrum of resistively heated MWNT sheet closely follows to the Plank's blackbody radiation distribution. The obtained polarization features can be described by a classical dielectric cylindrical shell model, taking into consideration the contribution of delocalized π-electrons (π surface plasmons). In absorption (emission) the optical transverse polarizability, which is much smaller than longitudinal one, is substantially suppressed by depolarization effect due to screening by induced charges. This phenomenon suggests very simple and precise method to estimate the alignment of nanotubes in bundles or large assemblies

  9. Growth of small diameter multi-walled carbon nanotubes by arc discharge process

    International Nuclear Information System (INIS)

    Chaudhary, K. T.; Ali, J.; Yupapin, P. P.

    2014-01-01

    Multi-walled carbon nanotubes (MWCNTs) are grown by arc discharge method in a controlled methane environment. The arc discharge is produced between two graphite electrodes at the ambient pressures of 100 torr, 300 torr, and 500 torr. Arc plasma parameters such as temperature and density are estimated to investigate the influences of the ambient pressure and the contributions of the ambient pressure to the growth and the structure of the nanotubes. The plasma temperature and density are observed to increase with the increase in the methane ambient pressure. The samples of MWCNT synthesized at different ambient pressures are analyzed using transmission electron microscopy, scanning electron microscopy, Raman spectroscopy, Fourier transform infrared spectroscopy, and X-ray diffraction. An increase in the growth of MWCNT and a decrease in the inner tube diameter are observed with the increase in the methane ambient pressure

  10. Collapse and stability of single- and multi-wall carbon nanotubes

    International Nuclear Information System (INIS)

    Xiao, J; Liu, B; Huang, Y; Zuo, J; Hwang, K-C; Yu, M-F

    2007-01-01

    The collapse and stability of carbon nanotubes (CNTs) have important implications for their synthesis and applications. While nanotube collapse has been observed experimentally, the conditions for the collapse, especially its dependence on tube structures, are not clear. We have studied the energetics of the collapse of single- and multi-wall CNTs via atomistic simulations. The collapse is governed by the number of walls and the radius of the inner-most wall. The collapsed structure is energetically favored about a certain diameter, which is 4.12, 4.96 and 5.76 nm for single-, double- and triple-wall CNTs, respectively. The CNT chirality also has a strong influence on the collapsed structure, leading to flat, warped and twisted CNTs, depending on the chiral angle

  11. Proposed model for biomineralization of novel nanohydroxyapatite/vertically aligned multiwalled carbon nanotube scaffolds

    Energy Technology Data Exchange (ETDEWEB)

    Brazil, Tayra Rodrigues; Neves, Marcele Florencio das; Marciano, Fernanda Roberta; Lobo, Anderson Oliveira, E-mail: aolobo@univap.br [Universidade do Vale do Paraiba (UniVap), Sao Jose dos Campos, SP (Brazil). Lab. de Nanotecnologia Biomedica; Regiani, Inacio [Instituto Tecnologico de Aeronautica (ITA), Sao Jose dos Campos, SP (Brazil)

    2013-11-01

    For the first time, the growth mechanism of biominerals formed on plate-like nanohydroxyapatite (nHAp) electrodeposited on superhydrophilic vertically aligned multi-walled carbon nanotubes (VAMWCNT-O{sub 2} ) is presented and a model for the specific growth preference is discussed. VAMWCNT-O{sub 2} films were obtained by microwave-assisted chemical vapor deposition method and functionalized by oxygen plasma. nHAp/VAMWCNT-O{sub 2} nanocomposites were fabricated with a direct electrodeposition of the thin nHAp films onto the VAMWCNT-O{sub 2} films. The biomineralized 'scaffolds' were obtained by soaking nHAp/VAMWCNT-O{sub 2} in simulated body fluid for 7, 14 and 21 days. Results show that the carboxyl functional groups directly attached onto VAMWCNT tips after oxygen plasma treatment were essential for the acceleration of the OH- formation and the deposition of plate-like nHAp crystals (author)

  12. Multiwalled carbon nanotube destruction in the radiation damages to electron irradiation

    Directory of Open Access Journals (Sweden)

    T. M. Pinchuk-Rugal’

    2015-10-01

    Full Text Available Behavior of the X-ray diffraction and vibrational Raman spectra of multiwalled carbon nanotubes (MWCNT under high-energy electron irradiation (Ee = 1.8 MeV with large doses of absorption to 10 MGy were studied. With increasing dose uptake to 10.0 MGy, the interlayer correlation in the distribution of the individual graphene nanotubes nets not only is maintained, but is even improved. Defective bands D, D' and G band with increasing dose absorption have significant transformation, which show radiation damages of MWCNT. The destruction of nanotubes under electron irradiation is accompanied by increased regulation in the arrangement of individual nanotubes by interlayer cross-links involving interstitial atoms. The severity of degradation and cross-linking of MWCNT depends on the electron absorption dose.

  13. Secondary doping in polyaniline layers coated on multi-walled carbon nanotubes

    Directory of Open Access Journals (Sweden)

    Zhou Yi

    2015-01-01

    Full Text Available HC1 doped coaxial polyaniline/multiwalled carbon nanotubes (MWCNTs nanocomposites were first prepared by in–situ chemical polymerization of aniline monomers in the presence of MWCNTs with less structural defects. P-toluene sulfonic acid (TSA and 5-sulfosalicylic acid dihydrate (SSA redoped PANI/MWCNT nanocomposites were achieved after the as-prepared nanocomposites were treated by ammonia respectively. The redoped nanocomposites were characterized by field emission scanning electron microscopy, transmission electron microscopy, fourier transform infrared spectroscopy, Raman, X–ray diffraction, thermogravimetric analysis and cyclic voltammetry, respectively. The results indicated that the thermal stability and electrochemical behaviour of TSA doped PANI/MWCNT nanocomposites were better than that of SSA doped PANI/MWCNT nanocomposites.

  14. Skin effect mitigation in laser processed multi-walled carbon nanotube/copper conductors

    Science.gov (United States)

    Keramatnejad, K.; Zhou, Y. S.; Gao, Y.; Rabiee Golgir, H.; Wang, M.; Jiang, L.; Silvain, J.-F.; Lu, Y. F.

    2015-10-01

    In this study, laser-processed multi-walled carbon nanotube (MWCNT)/Cu conductors are introduced as potential passive components to mitigate the skin effect of Cu at high frequencies (0-10 MHz). Suppressed skin effect is observed in the MWCNT/Cu conductors compared to primitive Cu. At an AC frequency of 10 MHz, a maximum AC resistance reduction of 94% was observed in a MWCNT/Cu conductor after being irradiated at a laser power density of 189 W/cm2. The reduced skin effect in the MWCNT/Cu conductors is ascribed to the presence of MWCNT channels which are insensitive to AC frequencies. The laser irradiation process is observed to play a crucial role in reducing contact resistance at the MWCNT-Cu interfaces, removing impurities in MWCNTs, and densifying MWCNT films.

  15. Skin effect mitigation in laser processed multi-walled carbon nanotube/copper conductors

    Energy Technology Data Exchange (ETDEWEB)

    Keramatnejad, K.; Zhou, Y. S.; Gao, Y.; Rabiee Golgir, H.; Wang, M.; Lu, Y. F., E-mail: ylu2@unl.edu [Department of Electrical and Computer Engineering, University of Nebraska-Lincoln, Lincoln, Nebraska 68588-0511 (United States); Jiang, L. [School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081 (China); Silvain, J.-F. [Institut de Chimie de la Matière Condensée de Bordeaux (ICMCB-CNRS) 87, Avenue du Docteur Albert Schweitzer F-33608 Pessac Cedex (France)

    2015-10-21

    In this study, laser-processed multi-walled carbon nanotube (MWCNT)/Cu conductors are introduced as potential passive components to mitigate the skin effect of Cu at high frequencies (0–10 MHz). Suppressed skin effect is observed in the MWCNT/Cu conductors compared to primitive Cu. At an AC frequency of 10 MHz, a maximum AC resistance reduction of 94% was observed in a MWCNT/Cu conductor after being irradiated at a laser power density of 189 W/cm{sup 2}. The reduced skin effect in the MWCNT/Cu conductors is ascribed to the presence of MWCNT channels which are insensitive to AC frequencies. The laser irradiation process is observed to play a crucial role in reducing contact resistance at the MWCNT-Cu interfaces, removing impurities in MWCNTs, and densifying MWCNT films.

  16. Skin effect mitigation in laser processed multi-walled carbon nanotube/copper conductors

    International Nuclear Information System (INIS)

    Keramatnejad, K.; Zhou, Y. S.; Gao, Y.; Rabiee Golgir, H.; Wang, M.; Lu, Y. F.; Jiang, L.; Silvain, J.-F.

    2015-01-01

    In this study, laser-processed multi-walled carbon nanotube (MWCNT)/Cu conductors are introduced as potential passive components to mitigate the skin effect of Cu at high frequencies (0–10 MHz). Suppressed skin effect is observed in the MWCNT/Cu conductors compared to primitive Cu. At an AC frequency of 10 MHz, a maximum AC resistance reduction of 94% was observed in a MWCNT/Cu conductor after being irradiated at a laser power density of 189 W/cm 2 . The reduced skin effect in the MWCNT/Cu conductors is ascribed to the presence of MWCNT channels which are insensitive to AC frequencies. The laser irradiation process is observed to play a crucial role in reducing contact resistance at the MWCNT-Cu interfaces, removing impurities in MWCNTs, and densifying MWCNT films

  17. Biofunctionalization of multiwalled carbon nanotubes by irradiation of electropolymerized poly(pyrrole-diazirine) films.

    Science.gov (United States)

    Papper, Vladislav; Gorgy, Karine; Elouarzaki, Kamal; Sukharaharja, Ayrine; Cosnier, Serge; Marks, Robert S

    2013-07-15

    A photoactivatable poly(pyrrole-diazirine) film was synthesized and electropolymerized as a versatile tool for covalent binding of laccase and glucose oxidase on multiwalled carbon nanotube coatings and Pt, respectively. Irradiation of the functionalized nanotubes allowed photochemical grafting of laccase and its subsequent direct electrical wiring, as illustrated by the electrocatalytic reduction of oxygen. Moreover, covalent binding of glucose oxidase as model enzyme, achieved by UV activation of electropolymerized pyrrole-diazirine, allowed a glucose biosensor to be realized. This original method to graft biomolecules combines electrochemical and photochemical techniques. The simplicity of this new method allows it to be extended easily to other biological systems. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  18. Using of Multiwall Carbon Nanotube Based Nanofluid in the Heat Pipe to Get Better Thermal Performance

    Directory of Open Access Journals (Sweden)

    Y. Bakhshan

    2014-09-01

    Full Text Available Thermal performance of a cylindrical heat pipe is investigated numerically. Three different types of water based nanofluids, namely, Al2O3 + Water, Diamond + Water, and Multi-Wall Carbon Nano tube (MWCNT + Water, have been used. The influence of using the simple nanofluids and MWCNT nanofluid on the heat pipe characteristics such as liquid velocity, pressure profile, temperature profile, thermal resistance, and heat transfer coefficient of heat pipe has been studied. A new correlation developed by Bakhshan and Saljooghi (2014 for viscosity of nanofluids has been implemented. The results show, a good agreement with the available analytical and experimental data. Also the results show, that the MWCNT based nanofluid has lower thermal resistance, higher heat transfer coefficient, and lower temperature difference between evaporator and condenser sections, so it has good thermal specifications as a working fluid for use in heat pipes. The prepared code has capability for parametric studies also.

  19. Dynamic Behavior of Nanocomposites Reinforced with Multi-Walled Carbon Nanotubes (MWCNTs

    Directory of Open Access Journals (Sweden)

    Chun-Yu Lai

    2013-06-01

    Full Text Available The influence of multi-walled carbon nanotubes (MWCNT on the structural dynamic behavior of MWCNT/epoxy nanocomposites was investigated. Two different types of MWCNTs, pristine MWCNT and functionalized MWCNT, were used in this study. Carboxylic acid-functionalized MWCNTs (MWCNT-COOH were obtained by oxidation pristine MWCNTs via sonication in sulfuric-nitric acid and characterized by Fourier transform infrared spectroscopy (FTIR. Dynamic behaviors of the MWCNT reinforced nanocomposite including the natural frequency and damping ratio were determined using free vibration test. Experimental results showed that the damping ratio of the nanocomposite decreases with the increase of the MWCNT addition, while the natural frequency is increasing with the increase of the MWCNT addition. Functionalized MWCNTs improved the interfacial bonding between the nanotubes and epoxy resin resulting in the reduction of the interfacial energy dissipation ability and enhancement of the stiffness.

  20. Nanocomposites with Liquid-Like Multiwalled Carbon Nanotubes Dispersed in Epoxy Resin without Solvent Process

    Directory of Open Access Journals (Sweden)

    Xi Zhang

    2014-01-01

    Full Text Available Liquid-like multiwall carbon nanotubes (MWNTs were prepared with as-received carboxylic MWNTs-COOH and poly(ethylene oxide-block-poly(propylene oxide-block-poly(ethylene oxide (PEO-b-PPO-b-PEO through hydrogen bonding. The sample has liquid-like behavior above 58°C. The MWNTs content is 26.6 wt%. The liquid-like MWNTs nanofluids were incorporated into epoxy matrix with solvent-free process and dispersed well. When the liquid-like MWNTs nanofluids content is up to 1 wt%, the impact toughness of the nanocomposite is 153% higher than the pure epoxy matrix.

  1. Micro/Nanomechanical characterization of multi-walled carbon nanotubes reinforced epoxy composite.

    Science.gov (United States)

    Cui, Peng; Wang, Xinnan; Tangpong, X W

    2012-11-01

    In this paper, the mechanical properties of 1 wt.% multi-walled carbon nanotubes (MWCNTs) reinforced epoxy nanocomposites were characterized using a self-designed micro/nano three point bending tester that was on an atomic force microscope (AFM) to in situ observe MWCNTs movement on the sample surface under loading. The migration of an individual MWCNT at the surface of the nanocomposite was tracked to address the nanomechanical reinforcing mechanism of the nanocomposites. Through morphology analysis of the nanocomposite via scanning electron microscopy, AFM, and digital image correlation technique, it was found that the MWCNTs agglomerate and the bundles were the main factors for limiting the bending strength of the composites. The agglomeration/bundle effect was included in the Halpin-Tsai model to account for the elastic modulus of the nanocomposites.

  2. Soft purification of N-doped and undoped multi-wall carbon nanotubes

    International Nuclear Information System (INIS)

    Alvizo-Paez, Edgar Rogelio; Ruiz-Garcia, Jaime; Hernandez-Lopez, Jose Luis; Romo-Herrera, Jose Manuel; Terrones, Humberto; Terrones, Mauricio

    2008-01-01

    A soft method for purifying multi-wall carbon nanotubes (N-doped and undoped) is presented. The technique includes a hydrothermal/ultrasonic treatment of the material in conjunction with other subsequent treatments, including the extraction of polyaromatic compounds, dissolution of metal particles, bundle exfoliation, and uniform dispersion. This method avoids harsh oxidation protocols that burn (via thermal treatments) or functionalize (by introducing chemical groups) the nanotubes. We show a careful analysis of each purification step and demonstrate that the technique is extremely efficient when characterizing the materials using scanning electron microscopy (SEM), energy dispersive x-ray analysis (EDAX), scanning tuneling electron microscopy (STEM), x-ray powder diffraction (XRD), diffuse reflectance Fourier transform infrared (DRFTIR) spectroscopy and thermogravimetric analysis (TGA)

  3. Rheology, Morphology and Temperature Dependency of Nanotube Networks in Polycarbonate/Multiwalled Carbon Nanotube Composites

    International Nuclear Information System (INIS)

    Abbasi, Samaneh; Carreau, Pierre J.; Derdouri, Abdessalem

    2008-01-01

    We present several issues related to the state of dispersion and rheological behavior of polycarbonate/multiwalled carbon nanotube (MWCNT) composites. The composites were prepared by diluting a commercial masterbatch containing 15 wt% nanotubes using optimized melt-mixing conditions. The state of dispersion was then analyzed by scanning and transmission electron microscopy (SEM, TEM). Rheological characterization was also used to assess the final morphology. Further, it was found that the rheological percolation threshold decreased significantly with increasing temperature and finally reached a constant value. This is described in terms of the Brownian motion, which increases with temperature. However, by increasing the nanotube content, the temperature effects on the complex viscosity at low frequency decreased significantly. Finally, the percolation thresholds were found to be approximately equal to 0.3 and 2 wt% for rheological and electrical conductivity measurements, respectively

  4. Comparison of quasistatic to impact mechanical properties of multiwall carbon nanotube/polycarbonate composites

    Energy Technology Data Exchange (ETDEWEB)

    Brühwiler, Paul A.; Barbezat, Michel; Necola, Adly; Kohls, Doug J.; Bunk, Oliver; Schaefer, Dale W.; Pötschke, Petra (PSI); (EMMPA); (UCIN); (Leibniz)

    2010-10-22

    We report the quasistatic tensile and impact penetration properties (falling dart test) of injection-molded polycarbonate samples, as a function of multiwall carbon nanotube (MWNT) concentration (0.0-2.5%). The MWNT were incorporated by dilution of a commercial MWNT/polycarbonate masterbatch. The stiffness and quasistatic yield strength of the composites increased approximately linearly with MWNT concentration in all measurements. The energy absorbed in fracture was, however, a negative function of the MWNT concentration, and exhibited different dependencies in quasistatic and impact tests. Small-angle x-ray scattering (SAXS) showed that the dispersion of the MWNT was similar at all concentrations. The negative effects on energy absorption are attributed to agglomerates remaining in the samples, which were observed in optical microscopy and SAXS. Overall, there was a good correspondence between static and dynamic energy absorption.

  5. Multiwalled carbon nanotubes and fluoroelastomer antistatic nanocomposite for automotive fuel system components

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Seok; Park, Seong Hwan; Ha, Kiryong [Keimyung University, Daegu (Korea, Republic of); Lee, Jong Cheol [Jin-Yang Oil Seal Co., Ltd., Daegu (Korea, Republic of)

    2016-03-15

    Fluoroelastomer (FKM) composites, reinforced with multiwalled carbon nanotubes (MWNTs), were prepared by conventional method to determine the possibility of using MWNTs to develop an antistatic composite in automotive fuel systems. The results obtained from the composite containing 0-9 phr of MWNTs were compared. A 5 points increase in hardness was achieved with the addition of only 1 phr of MWNTs and 9 phr added FKM composite was increased 6.4MPa in tensile strength compared to the MWNTs unfilled FKM composite. In addition, electrical conductivity increased from 0 to 1.039 Scm{sup -1} with increase in the MWNTs concentration, and the dynamic damping property was increased in the rubbery state region accordingly. These phenomena can be explained by the MWNTs networks formed in FKM matrix. This research will therefore be useful in the development of an antistatic rubber composite for fuel system components, which are deformed or vibrated while in operation.

  6. Poly(vinyl chloride-grafted multi-walled carbon nanotubes via Friedel-Crafts alkylation

    Directory of Open Access Journals (Sweden)

    2010-11-01

    Full Text Available A novel approach was developed for the surface modification of the multi-walled carbon nanotubes (MWCNTs with high percentage of grafting (PG% by the grafting of polymer via the Friedel-Crafts alkylation. The graft reaction conditions, such as the amount of catalyst added, the reaction temperature, and the reaction time were optimized for the Friedel-Crafts alkylation of the MWCNTs with poly(vinyl chloride (PVC with anhydrous aluminum chloride (AlCl3 as catalyst in chloroform (CHCl3. The Fourier Transform Infrared (FT-IR, Raman, and thermogravimetric (TGA analysis showed that PVC had been successfully grafted onto MWCNTs both at the ends and on the sidewalls by the proposed Friedel-Crafts alkylation. The PVC grafted MWCNTs (PVC-MWCNTs could be dispersed well in organic solvent and the dispersion was more stable.

  7. Multi-Walled Carbon Nanotube-Assisted Electrodeposition of Silver Dendrite Coating as a Catalytic Film

    Directory of Open Access Journals (Sweden)

    Li Fu

    2017-12-01

    Full Text Available A multi-walled carbon nanotube (MWCNT-coated indium tin oxide (ITO slide was used as a platform for the growth of a silver dendrite (Ag-D film using cyclic voltammetry. The particular dendritic nanostructures were formed by the diffusion-limited-aggregation model due to the potential difference between the MWCNTs and the ITO surface. The Ag-D-coated ITO film was then used for the catalytic degradation of methyl orange (MO and methylene blue (MB under static aqueous conditions. The network structure of the Ag-D allows the efficient diffusion of MO and MB, and consequently enhances the catalytic performance. Since the thin film is much easier to use for the post-treatment of powder catalysts, the proposed method shows great potential in many catalytic applications.

  8. Multiwalled carbon nanotubes and fluoroelastomer antistatic nanocomposite for automotive fuel system components

    International Nuclear Information System (INIS)

    Lee, Seok; Park, Seong Hwan; Ha, Kiryong; Lee, Jong Cheol

    2016-01-01

    Fluoroelastomer (FKM) composites, reinforced with multiwalled carbon nanotubes (MWNTs), were prepared by conventional method to determine the possibility of using MWNTs to develop an antistatic composite in automotive fuel systems. The results obtained from the composite containing 0-9 phr of MWNTs were compared. A 5 points increase in hardness was achieved with the addition of only 1 phr of MWNTs and 9 phr added FKM composite was increased 6.4MPa in tensile strength compared to the MWNTs unfilled FKM composite. In addition, electrical conductivity increased from 0 to 1.039 Scm -1 with increase in the MWNTs concentration, and the dynamic damping property was increased in the rubbery state region accordingly. These phenomena can be explained by the MWNTs networks formed in FKM matrix. This research will therefore be useful in the development of an antistatic rubber composite for fuel system components, which are deformed or vibrated while in operation.

  9. Calcification in vitro of Biomineralized nanohydroxyapatite / superhydrophilic vertically aligned multiwalled carbon nanotube scaffolds

    Energy Technology Data Exchange (ETDEWEB)

    Neves, Marcele Florencio; Silva, Gislene Rodrigues; Brazil, Tayra Rodrigues; Marciano, Fernanda Roberta; Lobo, Anderson Oliveira, E-mail: loboao@yahoo.com, E-mail: aolobo@univap.br [Universidade do Vale do Paraiba (UniVap), Sao Jose dos Campos, SP (Brazil). Lab. de Nanotecnologia Biomedica; Pacheco-Soares, Cristina [Universidade do Vale do Paraiba (UniVap), Sao Jose dos Campos, SP (Brazil). Lab. de Dinamica de Compartimentos Celulares

    2013-11-01

    Nanocomposites based on superhydrophilic vertically aligned multi-walled carbon nanotubes (VAMWCNT-O{sub 2}) and nanohydroxyapatite (nHAp) are of great interest in bone regenerative medicine. The biomineralization using simulated body fluid (SBF) has been extensively studied to evaluate the bioactivity of biomaterials. Thus, the combination of nHAp and VAMWCNT-O{sub 2} is attractive and promising. The aim of this study was to evaluate the in vitro calcification of nHAp/VAMWCNT-O{sub 2} nanocomposites before and after the period of biomineralization in SBF. In vitro calcification of the extracellular matrix (ECM) of HOB cells in culture after 24 hours was investigated through the assay of alkaline phosphatase. These promising in vitro results validate biomineralized nHAp/VAMWCNT-O{sub 2} as possible scaffolds for bone tissue regeneration. (author)

  10. Proposed model for biomineralization of novel nanohydroxyapatite/vertically aligned multiwalled carbon nanotube scaffolds

    Energy Technology Data Exchange (ETDEWEB)

    Brazil, Tayra Rodrigues; Neves, Marcele Florencio das; Marciano, Fernanda Roberta; Lobo, Anderson Oliveira, E-mail: aolobo@univap.br [Universidade do Vale do Paraiba (UniVap), Sao Jose dos Campos, SP (Brazil). Lab. de Nanotecnologia Biomedica; Regiani, Inacio [Instituto Tecnologico de Aeronautica (ITA), Sao Jose dos Campos, SP (Brazil)

    2013-11-01

    For the first time, the growth mechanism of biominerals formed on plate-like nanohydroxyapatite (nHAp) electrodeposited on superhydrophilic vertically aligned multi-walled carbon nanotubes (VAMWCNT-O{sub 2} ) is presented and a model for the specific growth preference is discussed. VAMWCNT-O{sub 2} films were obtained by microwave-assisted chemical vapor deposition method and functionalized by oxygen plasma. nHAp/VAMWCNT-O{sub 2} nanocomposites were fabricated with a direct electrodeposition of the thin nHAp films onto the VAMWCNT-O{sub 2} films. The biomineralized 'scaffolds' were obtained by soaking nHAp/VAMWCNT-O{sub 2} in simulated body fluid for 7, 14 and 21 days. Results show that the carboxyl functional groups directly attached onto VAMWCNT tips after oxygen plasma treatment were essential for the acceleration of the OH- formation and the deposition of plate-like nHAp crystals (author)

  11. Alternative mannosylation method for nanomaterials: application to oxidized debris-free multiwalled carbon nanotubes

    International Nuclear Information System (INIS)

    Sousa, Marcelo de; Martinez, Diego Stéfani Teodoro; Alves, Oswaldo Luiz

    2016-01-01

    Mannosylation is a method commonly used to deliver nanomaterials to specific organs and tissues via cellular macrophage uptake. In this work, for the first time, we proposed a method that involves the binding of d-mannose to ethylenediamine to form mannosylated ethylenediamine, which is then coupled to oxidized and purified multiwalled carbon nanotubes. The advantage of this approach is that mannosylated ethylenediamine precipitates in methanol, which greatly facilitates the separation of this product in the synthesis process. Carbon nanotubes were oxidized using concentrated H_2SO_4 and HNO_3 by conventional reflux method. However, during this oxidation process, carbon nanotubes generated carboxylated carbonaceous fragments (oxidation debris). These by-products were removed from the oxidized carbon nanotubes to ensure that the functionalization would occur only on the carbon nanotube surface. The coupling of mannosylated ethylenediamine to debris-free carbon nanotubes was accomplished using n-(3-dimethylaminopropyl)-n-ethylcarbodiimide and n-hydroxysuccinimide. Deconvoluted N1s spectra obtained from X-ray photoelectron spectroscopy gave binding energies of 399.8 and 401.7 eV, which we attributed to the amide and amine groups, respectively, of carbon nanotubes functionalized with mannosylated ethylenediamine. Deconvoluted O1s spectra showed a binding energy of 532.4 eV, which we suggest is caused by an overlap in the binding energies of the aliphatic CO groups of d-mannose and the O=C group of the amide bond. The functionalization degree was approximately 3.4 %, according to the thermogravimetric analysis. Scanning electron microscopy demonstrated that an extended carbon nanotube morphology was preserved following the oxidation, purification, and functionalization steps.

  12. Alternative mannosylation method for nanomaterials: application to oxidized debris-free multiwalled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Sousa, Marcelo de, E-mail: marcelosousap2@yahoo.com.br [University of Campinas (Unicamp), Solid State Chemistry Laboratory (LQES) and NanoBioss Laboratory, Institute of Chemistry (Brazil); Martinez, Diego Stéfani Teodoro, E-mail: diego.martinez@lnnano.cnpem.br [Brazilian Center for Research in Energy and Materials (CNPEM), Brazilian Nanotechnology National Laboratory (LNNano) (Brazil); Alves, Oswaldo Luiz, E-mail: oalves@iqm.unicamp.br [University of Campinas (Unicamp), Solid State Chemistry Laboratory (LQES) and NanoBioss Laboratory, Institute of Chemistry (Brazil)

    2016-06-15

    Mannosylation is a method commonly used to deliver nanomaterials to specific organs and tissues via cellular macrophage uptake. In this work, for the first time, we proposed a method that involves the binding of d-mannose to ethylenediamine to form mannosylated ethylenediamine, which is then coupled to oxidized and purified multiwalled carbon nanotubes. The advantage of this approach is that mannosylated ethylenediamine precipitates in methanol, which greatly facilitates the separation of this product in the synthesis process. Carbon nanotubes were oxidized using concentrated H{sub 2}SO{sub 4} and HNO{sub 3} by conventional reflux method. However, during this oxidation process, carbon nanotubes generated carboxylated carbonaceous fragments (oxidation debris). These by-products were removed from the oxidized carbon nanotubes to ensure that the functionalization would occur only on the carbon nanotube surface. The coupling of mannosylated ethylenediamine to debris-free carbon nanotubes was accomplished using n-(3-dimethylaminopropyl)-n-ethylcarbodiimide and n-hydroxysuccinimide. Deconvoluted N1s spectra obtained from X-ray photoelectron spectroscopy gave binding energies of 399.8 and 401.7 eV, which we attributed to the amide and amine groups, respectively, of carbon nanotubes functionalized with mannosylated ethylenediamine. Deconvoluted O1s spectra showed a binding energy of 532.4 eV, which we suggest is caused by an overlap in the binding energies of the aliphatic CO groups of d-mannose and the O=C group of the amide bond. The functionalization degree was approximately 3.4 %, according to the thermogravimetric analysis. Scanning electron microscopy demonstrated that an extended carbon nanotube morphology was preserved following the oxidation, purification, and functionalization steps.

  13. Implication of multi-walled carbon nanotubes on polymer/graphene composites

    International Nuclear Information System (INIS)

    Araby, Sherif; Saber, Nasser; Ma, Xing; Kawashima, Nobuyuki; Kang, Hailan; Shen, Heng; Zhang, Liqun; Xu, Jian; Majewski, Peter; Ma, Jun

    2015-01-01

    Highlights: • Influence of adding carbon nanotubes (CNTs) into elastomer/graphene composites. • Multi-walled CNTs work supplementally to GnPs by forming conductive networks. • The findings illuminate marked synergistic effect between MWCNTs and graphene sheets. - Abstract: Graphene sheets stack in polymer matrices while multi-walled carbon nanotubes (MWCNTs) entangle themselves, forming two daunting challenges in the design and fabrication of polymer composites. Both challenges have been simultaneously addressed in this study by hybridizing the two nanomaterials through melt compounding to develop elastomer/graphene platelet/MWCNT (3-phase) composites, where MWCNTs were fixed at 2.8 vol% (5 wt%) for all fractions. We investigated the composites’ structure and properties, and compared the 3-phase composites with elastomer/graphene platelet (2-phase) composites. MWCNTs may bridge graphene platelets (GnPs) and promote their dispersion in the matrix, which would provide more interface area between the matrix and the fillers. MWCNTs worked supplementally to GnPs by forming conductive networks, where MWCNTs acted as long nanocables to transport electrons and stress while GnPs served as interconnection sites between the tubes forming local conductive paths. This produced a percolation threshold of electrical conductivity at 2.3 vol% for 3-phase composites, 88% lower than that of 2-phase composites. At 26.7 vol% of total filler content (MWCNTs + GnPs), tensile strength, Young’s modulus and tear strength showed respectively 303%, 115%, 155% further improvements over those of 2-phase composites. These improvements are originated from the synergistic effect between GnPs and MWCNTs. The conducting elastomeric composites developed would potentially open the door for applications in automotive and aerospace industries

  14. A flexible graphene/multiwalled carbon nanotube film as a high performance electrode material for supercapacitors

    Energy Technology Data Exchange (ETDEWEB)

    Xiangjun, Lu [College of Material Science and Engineering, Nanjing University of Aeronautics and Astronautics, Yudao Street 29, Nanjing 210016, Jiangsu (China); Dou Hui, E-mail: dh_msc@nuaa.edu.cn [College of Material Science and Engineering, Nanjing University of Aeronautics and Astronautics, Yudao Street 29, Nanjing 210016, Jiangsu (China); Bo, Gao [College of Material Science and Engineering, Nanjing University of Aeronautics and Astronautics, Yudao Street 29, Nanjing 210016, Jiangsu (China); Changzhou, Yuan [School of Materials Science and Engineering, Anhui University of Technology, Maanshan 243002 (China); Yang, Sudong; Liang, Hao; Laifa, Shen [College of Material Science and Engineering, Nanjing University of Aeronautics and Astronautics, Yudao Street 29, Nanjing 210016, Jiangsu (China); Zhang Xiaogang, E-mail: azhangxg@nuaa.edu.cn [College of Material Science and Engineering, Nanjing University of Aeronautics and Astronautics, Yudao Street 29, Nanjing 210016, Jiangsu (China)

    2011-05-30

    Highlights: > A flexible graphene/multiwalled carbon nanotube (GN/MWCNT) film fabricated by flow-directed assembly and hydrazine to reduce. > The MWCNTs in the obtained composite film not only efficiently increase the basal spacing but also bridge the defects for electron transfer between GN sheets. > The freestanding GN/MWCNT film has a potential application in flexible energy storage devices. - Abstract: A flexible graphene/multiwalled carbon nanotube (GN/MWCNT) film has been fabricated by flow-directed assembly from a complex dispersion of graphite oxide (GO) and pristine MWCNTs followed by the use of gas-based hydrazine to reduce the GO into GN sheets. The GN/MWCNT (16 wt.% MWCNTs) film characterized by Fourier transformation infrared spectra, X-ray diffraction and scanning electron microscope has a layered structure with MWCNTs uniformly sandwiched between the GN sheets. The MWCNTs in the obtained composite film not only efficiently increase the basal spacing but also bridge the defects for electron transfer between GN sheets, increasing electrolyte/electrode contact area and facilitating transportation of electrolyte ion and electron into the inner region of electrode. Electrochemical data demonstrate that the GN/MWCNT film possesses a specific capacitance of 265 F g{sup -1} at 0.1 A g{sup -1} and a good rate capability (49% capacity retention at 50 A g{sup -1}), and displays an excellent specific capacitance retention of 97% after 2000 continuous charge/discharge cycles. The results of electrochemical measurements indicate that the freestanding GN/MWCNT film has a potential application in flexible energy storage devices.

  15. A flexible graphene/multiwalled carbon nanotube film as a high performance electrode material for supercapacitors

    International Nuclear Information System (INIS)

    Lu Xiangjun; Dou Hui; Gao Bo; Yuan Changzhou; Yang, Sudong; Hao Liang; Shen Laifa; Zhang Xiaogang

    2011-01-01

    Highlights: → A flexible graphene/multiwalled carbon nanotube (GN/MWCNT) film fabricated by flow-directed assembly and hydrazine to reduce. → The MWCNTs in the obtained composite film not only efficiently increase the basal spacing but also bridge the defects for electron transfer between GN sheets. → The freestanding GN/MWCNT film has a potential application in flexible energy storage devices. - Abstract: A flexible graphene/multiwalled carbon nanotube (GN/MWCNT) film has been fabricated by flow-directed assembly from a complex dispersion of graphite oxide (GO) and pristine MWCNTs followed by the use of gas-based hydrazine to reduce the GO into GN sheets. The GN/MWCNT (16 wt.% MWCNTs) film characterized by Fourier transformation infrared spectra, X-ray diffraction and scanning electron microscope has a layered structure with MWCNTs uniformly sandwiched between the GN sheets. The MWCNTs in the obtained composite film not only efficiently increase the basal spacing but also bridge the defects for electron transfer between GN sheets, increasing electrolyte/electrode contact area and facilitating transportation of electrolyte ion and electron into the inner region of electrode. Electrochemical data demonstrate that the GN/MWCNT film possesses a specific capacitance of 265 F g -1 at 0.1 A g -1 and a good rate capability (49% capacity retention at 50 A g -1 ), and displays an excellent specific capacitance retention of 97% after 2000 continuous charge/discharge cycles. The results of electrochemical measurements indicate that the freestanding GN/MWCNT film has a potential application in flexible energy storage devices.

  16. Laser-induced selective metallization of polypropylene doped with multiwall carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Ratautas, Karolis, E-mail: karolis.ratautas@ftmc.lt [Center for Physical Sciences and Technology, Savanoriu Ave. 231, Vilnius LT-02300 (Lithuania); Gedvilas, Mindaugas; Stankevičiene, Ina; Jagminienė, Aldona; Norkus, Eugenijus [Center for Physical Sciences and Technology, Savanoriu Ave. 231, Vilnius LT-02300 (Lithuania); Pira, Nello Li [Centro Ricerche Fiat, Strada Torino 50, Orbassano 10043 (Italy); Sinopoli, Stefano [BioAge Srl, Via Dei Glicini 25, Lamezia Terme 88046 (Italy); Račiukaitis, Gediminas [Center for Physical Sciences and Technology, Savanoriu Ave. 231, Vilnius LT-02300 (Lithuania)

    2017-08-01

    Highlights: • PP doped with multiwall CNT can be activated with ns laser for electroless plating. • Developed material is cheap decision for MID applications. • Activation mechanism was preliminary proposed. • Demo for automotive application has been manufactured. - Abstract: Moulded interconnect devices (MID) offer the material, weight and cost saving by integration electronic circuits directly into polymeric components used in automotive and other consumer products. Lasers are used to write circuits directly by modifying the surface of polymers followed by an electroless metal plating. A new composite material – the polypropylene doped with multiwall carbon nanotubes was developed for the laser-induced selective metallization. Mechanism of surface activation by laser irradiation was investigated in details utilising pico- and nanoseconds lasers. Deposition of copper was performed in the autocatalytic electroless plating bath. The laser-activated polymer surfaces have been studied using the Raman spectroscopy and scanning electron microscope (SEM). Microscopic images revealed that surface becomes active only after its melting by a laser. Alterations in the Raman spectra of the D and G bands indicated the clustering of carbon additives in the composite material. Optimal laser parameters for the surface activation were found by measuring a sheet resistance of the finally metal-plated samples. A spatially selective copper plating was achieved with the smallest conductor line width of 22 μm at the laser scanning speed of 3 m/s and the pulse repetition rate of 100 kHz. Finally, the technique was validated by making functional electronic circuits by this MID approach.

  17. Laser-induced selective metallization of polypropylene doped with multiwall carbon nanotubes

    International Nuclear Information System (INIS)

    Ratautas, Karolis; Gedvilas, Mindaugas; Stankevičiene, Ina; Jagminienė, Aldona; Norkus, Eugenijus; Pira, Nello Li; Sinopoli, Stefano; Račiukaitis, Gediminas

    2017-01-01

    Highlights: • PP doped with multiwall CNT can be activated with ns laser for electroless plating. • Developed material is cheap decision for MID applications. • Activation mechanism was preliminary proposed. • Demo for automotive application has been manufactured. - Abstract: Moulded interconnect devices (MID) offer the material, weight and cost saving by integration electronic circuits directly into polymeric components used in automotive and other consumer products. Lasers are used to write circuits directly by modifying the surface of polymers followed by an electroless metal plating. A new composite material – the polypropylene doped with multiwall carbon nanotubes was developed for the laser-induced selective metallization. Mechanism of surface activation by laser irradiation was investigated in details utilising pico- and nanoseconds lasers. Deposition of copper was performed in the autocatalytic electroless plating bath. The laser-activated polymer surfaces have been studied using the Raman spectroscopy and scanning electron microscope (SEM). Microscopic images revealed that surface becomes active only after its melting by a laser. Alterations in the Raman spectra of the D and G bands indicated the clustering of carbon additives in the composite material. Optimal laser parameters for the surface activation were found by measuring a sheet resistance of the finally metal-plated samples. A spatially selective copper plating was achieved with the smallest conductor line width of 22 μm at the laser scanning speed of 3 m/s and the pulse repetition rate of 100 kHz. Finally, the technique was validated by making functional electronic circuits by this MID approach.

  18. Synthesis of MnO{sub 2}/short multi-walled carbon nanotube nanocomposite for supercapacitors

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Jinhui; Wang, Yanhui; Zang, Jianbing, E-mail: diamondzjb@163.com; Xin, Guoxiang; Ji, Huiying; Yuan, Yungang

    2014-01-15

    Multi-walled carbon nanotubes (MWNTs) were selectively etched in molten nitrate to produce short MWNTs (s-MWNTs). MnO{sub 2}/s-MWNT nanocomposite was synthesized by a reduction of potassium permanganate under microwave irradiation. For comparative purpose, MnO{sub 2}/MWNT nanocomposite was also synthesized and investigated for its physical and electrochemical performance. Uniform and conformal MnO{sub 2} coatings were more easily formed on the surfaces of individual s-MWNTs. MnO{sub 2}/s-MWNT nanocomposite estimated by cyclic voltammetry (CV) in 0.5 M Na{sub 2}SO{sub 4} aqueous solution had the specific capacitance as high as 392.1 F g{sup −1} at 2 mV s{sup −1}. This value was more than 48.9% larger than MnO{sub 2}/s-MWNT nanocomposite. In addition, MnO{sub 2}/s-MWNT nanocomposite was also examined by repeating the CV test at a scan rate of 50 mV s{sup −1}, exhibiting an excellent cycling stability along with 99.2% specific capacitance retained after 1000 cycles. Therefore, MnO{sub 2}/s-MWNT nanocomposite is a promising electrode material in the supercapacitors. - Highlights: • Multi-walled carbon nanotubes are etched in molten nitrate to produce short MWNTs. • S-MWNTs can form more stable suspensions than did the pristine MWNTs. • Nano-scaled MnO{sub 2} is more effectively dispersed on the surface of the s-MWNTs. • This microstructure promotes the electrical conductivity of the electrode. • The electrode exhibits high specific capacitance and a cycle stability.

  19. Coexistence of positive and negative photoconductivity in nickel oxide decorated multiwall carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Jiménez-Marín, E. [Departamento de Ingeniería en Metalurgia y Materiales, Escuela Superior de Ingeniería Química e Industrias Extractivas, Instituto Politécnico Nacional, Ciudad de México 07300 (Mexico); Villalpando, I. [Centro de Investigación para los Recursos Naturales, Salaices, Chihuahua 33941 (Mexico); Trejo-Valdez, M. [Escuela Superior de Ingeniería Química e Industrias Extractivas, Instituto Politécnico Nacional, México, Ciudad de México 07738 (Mexico); Cervantes-Sodi, F. [Departamento de Física y Matemáticas, Universidad Iberoamericana, Prolongación Paseo de la Reforma 880, Lomas de Santa Fe, Ciudad de México 01219 (Mexico); Vargas-García, J.R. [Centro de Nanociencias y Micro y Nanotecnologías del Instituto Politécnico Nacional, Ciudad de México 07738 (Mexico); Torres-Torres, C., E-mail: ctorrest@ipn.mx [Sección de Estudios de Posgrado e Investigación, Escuela Superior de Ingeniería Mecánica y Eléctrica Unidad Zacatenco, Instituto Politécnico Nacional, Ciudad de México 07738 (Mexico)

    2017-06-15

    Highlights: • Nickel oxide decorated carbon nanotubes were prepared by chemical vapor deposition. • Contrast in photoconductivity phenomena in the nanohybrid was analyzed. • Electrical and nonlinear optical properties were evaluated. • A Wheatstone bridge sensor based metal/carbon nanostructures was proposed. - Abstract: Within this work was explored the influence of nickel oxide decoration on the photoconductive effects exhibited by multiwall carbon nanotubes. Samples in thin film form were prepared by a chemical vapor deposition method. Experiments for evaluating the photo-response of the nanomaterials at 532 nanometers wavelength were undertaken. A contrasting behavior in the photoelectrical characteristics of the decorated nanostructures was analyzed. The decoration technique allowed us to control a decrease in photoconduction of the sample from approximately 100 μmhos/cm to −600 μmhos/cm. Two-wave mixing experiments confirmed an enhancement in nanosecond nonlinearities derived by nickel oxide contributions. It was considered that metallic nanoparticles present a strong responsibility for the evolution of the optoelectronic phenomena in metal/carbon nanohybrids. Impedance spectroscopy explorations indicated that a capacitive behavior correspond to the samples. A potential development of high-sensitive Wheatstone bridge sensors based on the optoelectrical performance of the studied samples was proposed.

  20. Multi-walled carbon nanotubes/polymer composites in absence and presence of acrylic elastomer (ACM).

    Science.gov (United States)

    Kumar, S; Rath, T; Mahaling, R N; Mukherjee, M; Khatua, B B; Das, C K

    2009-05-01

    Polyetherimide/Multiwall carbon nanotube (MWNTs) nanocomposites containing as-received and modified (COOH-MWNT) carbon nanotubes were prepared through melt process in extruder and then compression molded. Thermal properties of the composites were characterized by thermo-gravimetric analysis (TGA). Field emission scanning electron microscopy (FESEM) images showed that the MWNTs were well dispersed and formed an intimate contact with the polymer matrix without any agglomeration. However the incorporation of modified carbon nanotubes formed fascinating, highly crosslinked, and compact network structure throughout the polymer matrix. This showed the increased adhesion of PEI with modified MWNTs. Scanning electron microscopy (SEM) also showed high degree of dispersion of modified MWNTs along with broken ends. Dynamic mechanical analysis (DMA) results showed a marginal increase in storage modulus (E') and glass transition temperature (T(g)) with the addition of MWNTs. Increase in tensile strength and impact strength of composites confirmed the use the MWNTs as possible reinforcement agent. Both thermal and electrical conductivity of composites increased, but effect is more pronounced on modification due to formation of network of carbon nanotubes. Addition of acrylic elastomer to developed PEI/MWNTs (modified) nanocomposites resulted in the further increase in thermal and electrical properties due to the formation of additional bond between MWNTs and acrylic elastomers at the interface. All the results presented are well corroborated by SEM and FESEM studies.

  1. Studies on the heterogeneous electron transport and oxygen reduction reaction at metal (Co, Fe) octabutylsulphonylphthalocyanines supported on multi-walled carbon nanotube modified graphite electrode

    CSIR Research Space (South Africa)

    Mamuru, SA

    2010-09-01

    Full Text Available Heterogeneous electron transfer dynamics and oxygen reduction reaction (ORR) activities using octabutylsulphonylphthalocyanine complexes of iron (FeOBSPc) and cobalt (CoOBSPc) supported on multi-walled carbon nanotube (MWCNT) platforms have been...

  2. Iron (II) tetrakis(diaquaplatinum) octacarboxyphthalocyanine supported on multi-walled carbon nanotubes as effective electrocatalyst for oxygen reduction reaction in alkaline medium

    CSIR Research Space (South Africa)

    Mamuru, SA

    2010-11-01

    Full Text Available Oxygen reduction reaction (ORR) in alkaline medium at iron (II) tetrakis (diaquaplatinum) octacarboxyphthalocyanine (PtFeOCPc) catalyst supported on multi-walled carbon nanotubes (MWCNTs) has been described. The ORR followed the direct 4-electron...

  3. Comprehensive Environmental Assessment Applied to Multiwalled Carbon Nanotube Flame-Retardant Coatings in Upholstery Textiles: A Case Study Presenting Priority Research Gaps for Future Risk Assessments (Final Report)

    Science.gov (United States)

    In September 2013, EPA announced the availability of the final report, Comprehensive Environmental Assessment Applied to Multiwalled Carbon Nanotube Flame-Retardant Coatings in Upholstery Textiles: A Case Study Presenting Priority Research Gaps for Future Risk Assessments...

  4. Effectively Improved Field Emission Properties of Multiwalled Carbon Nanotubes/Graphenes Composite Field Emitter by Covering on the Si Pyramidal Structure

    DEFF Research Database (Denmark)

    Chen, Leifeng; Yu, Hua; Zhong, Jiasong

    2015-01-01

    The composite nanostructure emitter of multiwalled carbon nanotubes and graphenes was deposited on pyramidal silicon substrate by the simple larger scale electrophoretic deposition process. The field emission (FE) properties of the composite/pyramidal Si device were greatly improved compared...

  5. Heat dissipation for the Intel Core i5 processor using multiwalled carbon-nanotube-based ethylene glycol

    International Nuclear Information System (INIS)

    Thang, Bui Hung; Trinh, Pham Van; Quang, Le Dinh; Khoi, Phan Hong; Minh, Phan Ngoc; Huong, Nguyen Thi

    2014-01-01

    Carbon nanotubes (CNTs) are some of the most valuable materials with high thermal conductivity. The thermal conductivity of individual multiwalled carbon nanotubes (MWCNTs) grown by using chemical vapor deposition is 600 ± 100 Wm -1 K -1 compared with the thermal conductivity 419 Wm -1 K -1 of Ag. Carbon-nanotube-based liquids - a new class of nanomaterials, have shown many interesting properties and distinctive features offering potential in heat dissipation applications for electronic devices, such as computer microprocessor, high power LED, etc. In this work, a multiwalled carbon-nanotube-based liquid was made of well-dispersed hydroxyl-functional multiwalled carbon nanotubes (MWCNT-OH) in ethylene glycol (EG)/distilled water (DW) solutions by using Tween-80 surfactant and an ultrasonication method. The concentration of MWCNT-OH in EG/DW solutions ranged from 0.1 to 1.2 gram/liter. The dispersion of the MWCNT-OH-based EG/DW solutions was evaluated by using a Zeta-Sizer analyzer. The MWCNT-OH-based EG/DW solutions were used as coolants in the liquid cooling system for the Intel Core i5 processor. The thermal dissipation efficiency and the thermal response of the system were evaluated by directly measuring the temperature of the micro-processor using the Core Temp software and the temperature sensors built inside the micro-processor. The results confirmed the advantages of CNTs in thermal dissipation systems for computer processors and other high-power electronic devices.

  6. Nitrogen doped carbon derived from polyimide/multiwall carbon nanotube composites for high performance flexible all-solid-state supercapacitors

    Science.gov (United States)

    Kim, Dae Kyom; Kim, Nam Dong; Park, Seung-Keun; Seong, Kwang-dong; Hwang, Minsik; You, Nam-Ho; Piao, Yuanzhe

    2018-03-01

    Flexible all-solid-state supercapacitors are desirable as potential energy storage systems for wearable technologies. Herein, we synthesize aminophenyl multiwall carbon nanotube (AP-MWCNT) grafted polyimide precursor by in situ polymerization method as a nitrogen-doped carbon precursor. Flexible supercapacitor electrodes are fabricated via a coating of carbon precursor on carbon cloth surface and carbonization at high temperature directly. The as-obtained electrodes, which can be directly used without any binders or additives, can deliver a high specific capacitance of 333.4 F g-1 at 1 A g-1 (based on active material mass) and excellent cycle stability with 103% capacitance retention after 10,000 cycles in a three-electrode system. The flexible all-solid-state supercapacitor device exhibits a high volumetric capacitance of 3.88 F cm-3 at a current density of 0.02 mA cm-3. And also the device can deliver a maximum volumetric energy density of 0.50 mWh cm-3 and presents good cycling stability with 85.3% capacitance retention after 10,000 cycles. This device cell can not only show extraordinary mechanical flexibilities allowing folding, twisting, and rolling but also demonstrate remarkable stable electrochemical performances under their forms. This work provides a novel approach to obtain carbon textile-based flexible supercapacitors with high electrochemical performance and mechanical flexibility.

  7. The Effect of Plasma Treated PLGA/MWCNTs-COOH Composite Nanofibers on Nerve Cell Behavior

    Directory of Open Access Journals (Sweden)

    Jing Wang

    2017-12-01

    Full Text Available Electrospun nanofibrous scaffolds which can mimic the architecture of the natural extracellular matrix (ECM are potential candidates for peripheral nerve repair application. Multi-walled carbon nanotubes (MWCNTs are used in peripheral nerve repair due to their ability to promote neurite extension and support neural network formation. In this study, surface-modified nanofibrous scaffolds composed of poly(lactic-co-glycolic acid (PLGA and various ratios of carboxyl-modified MWCNTs (MWCNTs-COOH (PC0, PC2, PC4 and PC8 were fabricated by electrospinning. The effects of MWCNTs-COOH on the fibers’ morphology, diameter distribution, mechanical properties and surface hydrophilicity were characterized by Scanning Electron Microscopy (SEM, ImageJ software, tensile testing and water contact angle. Furthermore, air plasma treatment was applied to improve the surface hydrophilicity of the scaffolds, and the optimal treatment condition was determined in terms of surface morphology, water contact angle and PC12 cell adhesion. Plasma treated nanofibers (p-PC0, p-PC2, p-PC4 and p-PC8 under optimal treatment conditions were used for further study. PC12 cell proliferation and differentiation were both improved by the addition of MWCNTs-COOH in scaffolds. Additionally, the proliferation and maturation of Schwann cells were enhanced on scaffolds containing MWCNTs-COOH. The neurite outgrowth of rat dorsal root ganglia (DRG neurons was promoted on MWCNTs-COOH-containing scaffolds, and those cultured on p-PC8 scaffolds showed elongated neurites with a length up to 78.27 μm after 3 days culture. Our results suggested that plasma treated nanofibers under appropriate conditions were able to improve cell attachment. They also demonstrated that plasma treated scaffolds containing MWCNTs-COOH, especially the p-PC8 nanofibrous scaffold could support the proliferation, differentiation, maturation and neurite extension of PC12 cells, Schwann cells and DRG neurons. Therefore

  8. Aligned multi-walled carbon nanotube-reinforced composites: processing and mechanical characterization

    International Nuclear Information System (INIS)

    Thostenson, Erik T.; Chou, Tsuwei

    2002-01-01

    Carbon nanotubes have been the subject of considerable attention because of their exceptional physical and mechanical properties. These properties observed at the nanoscale have motivated researchers to utilize carbon nanotubes as reinforcement in composite materials. In this research, a micro-scale twin-screw extruder was used to achieve dispersion of multi-walled carbon nanotubes in a polystyrene matrix. Highly aligned nanocomposite films were produced by extruding the polymer melt through a rectangular die and drawing the film prior to cooling. Randomly oriented nanocomposites were produced by achieving dispersion first with the twin-screw extruder followed by pressing a film using a hydraulic press. The tensile behaviour of the aligned and random nanocomposite films with 5 wt.{%} loading of nanotubes were characterized. Addition of nanotubes increased the tensile modulus, yield strength and ultimate strengths of the polymer films, and the improvement in elastic modulus with the aligned nanotube composite is five times greater than the improvement for the randomly oriented composite. (author)

  9. Solid-contact pH-selective electrode using multi-walled carbon nanotubes.

    Science.gov (United States)

    Crespo, Gastón A; Gugsa, Derese; Macho, Santiago; Rius, F Xavier

    2009-12-01

    Multi-walled carbon nanotubes (MWCNT) are shown to be efficient transducers of the ionic-to-electronic current. This enables the development of a new solid-contact pH-selective electrode that is based on the deposition of a 35-microm thick layer of MWCNT between the acrylic ion-selective membrane and the glassy carbon rod used as the electrical conductor. The ion-selective membrane was prepared by incorporating tridodecylamine as the ionophore, potassium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate as the lipophilic additive in a polymerized methylmethacrylate and an n-butyl acrylate matrix. The potentiometric response shows Nernstian behaviour and a linear dynamic range between 2.89 and 9.90 pH values. The response time for this electrode was less than 10 s throughout the whole working range. The electrode shows a high selectivity towards interfering ions. Electrochemical impedance spectroscopy and chronopotentiometry techniques were used to characterise the electrochemical behaviour and the stability of the carbon-nanotube-based ion-selective electrodes.

  10. Bromate Removal from Water Using Doped Iron Nanoparticles on Multiwalled Carbon Nanotubes (CNTS

    Directory of Open Access Journals (Sweden)

    Aasem Zeino

    2014-01-01

    Full Text Available The raw carbon nanotubes (CNTs were prepared by the floating catalyst chemical vapor deposition method. The raw carbon nanotubes were functionalized, impregnated with iron nanoparticles, and characterized using high resolution transmission electron microscopy (HRTEM, scanning electron microscopy with energy dispersive spectroscopy (SEM-EDS, Fourier transform infrared spectroscopy (FTIR, Differential Scanning Calorimetry (DSC, and thermogravimetric analysis (TGA. The three types of these multiwalled carbon nanotubes were applied as adsorbents for the removal of bromate from drinking water. The effects of the pH, the concentration of BrO3- anion, the adsorbent dose, the contact time, and the coanions on the adsorption process have been investigated. The results concluded that the highest adsorption capacities were 0.3460 and 0.3220 mg/g through using CNTs-Fe and raw CNTs, respectively, at the same conditions. The results showed that the CNTs-Fe gives higher adsorption capacity compared with the raw CNTs and the functionalized CNTs. The presence of nitrate (NO3- in the solution decreases the adsorption capacity of all CNTs compared with chloride (Cl- associated with pH adjustment caused by nitric acid or hydrochloric acid, respectively. However, the adsorption of all MWNCTs types increases as the pH of solution decreases.

  11. Multi-walled carbon nanotubes: A cytotoxicity study in relation to functionalization, dose and dispersion.

    Science.gov (United States)

    Zhou, Lulu; Forman, Henry Jay; Ge, Yi; Lunec, Joseph

    2017-08-01

    Chemical functionalization broadens carbon nanotube (CNT) applications, conferring new functions, but at the same time potentially altering toxicity. Although considerable experimental data related to CNT toxicity, at the molecular and cellular levels, have been reported, there is very limited information available for the corresponding mechanism involved (e.g. cell apoptosis and genotoxicity). The threshold dose for safe medical application in relation to both pristine and functionalized carbon nanotubes remains ambiguous. In this study, we evaluated the in vitro cytotoxicity of pristine and functionalized (OH, COOH) multi-walled carbon nanotubes (MWCNTs) for cell viability, oxidant detection, apoptosis and DNA mutations, to determine the non-toxic dose and influence of functional group in a human lung-cancer cell line exposed to 1-1000μg/ml MWCNTs for 24, 48 and 72h. The findings suggest that pristine MWCNTs induced more cell death than functionalized MWCNTs while functionalized MWCNTs are more genotoxic compared to their pristine form. The level of both dose and dispersion in the matrix used should be taken into consideration before applying further clinical applications of MWCNTs. Copyright © 2017 Elsevier Ltd. All rights reserved.

  12. Preparation of chitosan/amino multiwalled carbon nanotubes nanocomposite beads for bilirubin adsorption in hemoperfusion.

    Science.gov (United States)

    Zong, Wenhui; Chen, Jian; Han, Wenyan; Chen, Jie; Wang, Yue; Wang, Weichao; Cheng, Guanghui; Ou, Lailiang; Yu, Yaoting

    2018-01-01

    Chitosan-carbon nanotube composite beads combines the advantages of chitosan in forming a stable biocompatible framework and carbon nanotube that provide nanometer effects (high strength and high specific surface area etc.). In this study, chitosan/amino multiwalled carbon nanotubes (CS/AMWCNT) composite beads was prepared by phase-inversion method, in which CS and AMWCNT was crosslinked by ethylene glycol diglycidyl ether (EGDE). The CS/AMWCNT nanocomposite beads produced has been characterized by BET, SEM, TGA, and Raman spectroscopy which exhibited enhanced thermal stability due to the incorporation of AMWCNT. Mechanical test results showed that mechanical strength of the CS/AMWCNT composite beads was significantly enhanced when comparing to unmodified chitosan beads, the breakage percentage decreased from 34.1% to 0.67%. The adsorption capacity for bilirubin was measured in PBS and BSA solutions, and the CS/AMWCNT composite beads with 5 wt% AMWCNT showed much higher adsorption capacity (12.7 mg/g in PBS and 7.6 mg/g in BSA) to bilirubin than chitosan beads (8.5 mg/g in PBS and 4.2 mg/g in BSA). Our nanocomposite beads with excellent hemocompatibility has a high potential application in blood purification as an efficient adsorbent for bilirubin. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 96-103, 2018. © 2016 Wiley Periodicals, Inc.

  13. Synthesis of multiwall carbon nanotube wrapped Co(OH)_2 flakes: A high-performance supercapacitor

    International Nuclear Information System (INIS)

    Mondal, Chanchal; Ghosh, Debasis; Ganguly, Mainak; Sasmal, Anup Kumar; Roy, Anindita; Pal, Tarasankar

    2015-01-01

    Graphical abstract: - Highlights: • Multiwalled carbon nanotube wrapped Co(OH)_2 nanoflakes has been fabricated. • It showed high supercapcitive performance with specific capacitance of 603 F/g. • The as-prepared composite material exhibited remarkable cycling stability. • It may be applied for the development of supercapacitor electrode material. - Abstract: The problem of poor electron conductivity is always associated with pseudocapacitive electrode material that deters full utilization of the active material. To have a viable solution to this problem, we report fabrication of a composite material bringing highly conductive carbon nanotube (CNT) wrapped pseudocapacitive with Co(OH)_2 nanoflakes. An in situ growth route evolves the supercapacitor via our laboratory developed modified hydrothermal reaction condition (MHT). An electrochemical investigation substantiates that the composite material electrode is highly active, which delivers a maximum specific capacitance of 603 F g"−"1 (at 1 mV s"−"1 scan rate), outstanding long-term cyclic stability with 96% retention at a constant current density of 1.5 A g"−"1 after 1000 cycles of operation. Thus it offers almost an effortless approach to fabricate high-power and high-energy density supercapacitors. By virtue of having high-capacity of pseudocapacitive hydroxides and desirable conductivity of carbon-based materials, the as-synthesized material could be a promising candidate for the development of supercapacitor electrode material.

  14. Carbon capture from natural gas using multi-walled CNTs based mixed matrix membranes.

    Science.gov (United States)

    Hussain, Abid; Farrukh, Sarah; Hussain, Arshad; Ayoub, Muhammad

    2017-12-05

    Most of the polymers and their blends, utilized in carbon capture membranes, are costly, but cellulose acetate (CA) being inexpensive is a lucrative choice. In this research, pure and mixed matrix membranes (MMMs) have been fabricated to capture carbon from natural gas. Polyethylene glycol (PEG) has been utilized in the fabrication of membranes to modify the chain flexibility of polymers. Multi-walled carbon nanotubes (MWCNTs) provide mechanical strength, thermal stability, an extra free path for CO 2 molecules and augment CO 2 /CH 4 selectivity. Membranes of pure CA, CA/PEG blend of different PEG concentrations (5%, 10%, 15%) and CA/PEG/MWCNTs blend of 10% PEG with different MWCNTs concentrations (5%, 10%, 15%) were prepared in acetone using solution casting techniques. Fabricated membranes were characterized using SEM, TGA and tensile testing. Permeation results revealed remarkable improvement in CO 2 /CH 4 selectivity. In single gas experiments, CO 2 /CH 4 selectivity is enhanced 8 times for pure membranes containing 10% PEG and 14 times for MMMs containing 10% MWCNTs. In mix gas experiments, the CO 2 /CH 4 selectivity is increased 13 times for 10% PEG and 18 times for MMMs with 10% MWCNTs. Fabricated MMMs have a tensile strength of 13 MPa and are more thermally stable than CA membranes.

  15. Diffusion of multiwall carbon nanotubes (MWCNTs) through a high density polyethylene (HDPE) geomembrane.

    Science.gov (United States)

    Saheli, P T; Rowe, R K; Petersen, E J; O'Carroll, D M

    2017-05-01

    The new applications for carbon nanotubes (CNTs) in various fields and consequently their greater production volume have increased their potential release to the environment. Landfills are one of the major locations where carbon nanotubes are expected to be disposed and it is important to ensure that they can limit the release of CNTs. Diffusion of multiwall carbon nanotubes (MWCNTs) dispersed in an aqueous media through a high-density polyethylene (HDPE) geomembrane (as a part of the landfill barrier system) was examined. Based on the laboratory tests, the permeation coefficient was estimated to be less than 5.1×10 -15 m 2 /s. The potential performance of a HDPE geomembrane and geosynthetic clay liner (GCL) as parts of a composite liner in containing MWCNTs was modelled for six different scenarios. The results suggest that the low value of permeation coefficient of an HDPE geomembrane makes it an effective diffusive barrier for MWCNTs and by keeping the geomembrane defects to minimum during the construction (e.g., number of holes and length of wrinkles) a composite liner commonly used in municipal solid waste landfills will effectively contain MWCNTs.

  16. Influence of multi-walled carbon nanotubes on the cognitive abilities of Wistar rats

    Science.gov (United States)

    Sayapina, Nina V.; Sergievich, Alexander A.; Kuznetsov, Vladimir L.; Chaika, Vladimir V.; Lisitskaya, Irina G.; Khoroshikh, Pavel P.; Batalova, Tatyana A.; Tsarouhas, Kostas; Spandidos, Demetrios; Tsatsakis, Aristidis M.; Fenga, Concettina; Golokhvast, Kirill S.

    2016-01-01

    Studies of the neurobehavioral effects of carbon nanomaterials, particularly those of multi-walled carbon nanotubes (MWCNTs), have concentrated on cognitive effects, but data are scarce. The aim of this study was to assess the influence of MWCNTs on a number of higher nervous system functions of Wistar rats. For a period of 10 days, two experimental groups were fed with MWCNTs of different diameters (MWCNT-1 group, 8–10 nm; MWCNT-2 group, 18–20 nm) once a day at a dosage of 500 mg/kg. In the open-field test, reductions of integral indications of researching activity were observed for the two MWCNT-treated groups, with a parallel significant (Ptest, integral indices of researching activity in the MWCNT-1 and MWCNT-2 groups reduced by day 10 by 51 and 62%, respectively, while rat stress levels remained relatively unchanged. In the universal problem solving box test, reductions in motivation and energy indices of researching activity were observed in the two experimental groups. Searching activity in the MWCNT-1 group by day 3 was reduced by 50% (Ptests demonstrated that MWCNT-treated rats experienced a significant reduction of some of their cognitive abilities, a disturbing and worrying finding, taking into consideration the continuing and accelerating use of carbon nanotubes in medicine and science. PMID:27588053

  17. Plasma-activated multi-walled carbon nanotube-polystyrene composite substrates for biosensing

    International Nuclear Information System (INIS)

    Fernandez-Sanchez, Cesar; Orozco, Jahir; Jimenez-Jorquera, Cecilia; Pellicer, Eva; Lechuga, Laura M; Mendoza, Ernest

    2009-01-01

    Carbon nanotube-polymer composites have shown to be suitable materials for the fabrication of electrochemical transducers. The exposed surface of these materials is commonly passivated by a very thin layer of the polymer component that buries the conductive carbon particles. Working with multi-walled carbon nanotube-polystyrene (MWCNT-PS) composite structures, it was previously described how a simple low power oxygen plasma process produced an effective etching of the composite surface, thereby exposing the conductive surface of CNTs. This work shows how this plasma process not only gave rise to a suitable composite conductive surface for electrochemical sensing but simultaneously exposed and created a high density of oxygen-containing functional groups at both the CNT and the PS components, without affecting the material's mechanical stability. These chemical groups could be effectively modified for the stable immobilization of biological receptors. A detailed chemical characterization of the plasma-activated composite surface was possible using x-ray photoelectron spectroscopy. The material reactivity towards the tethering of a protein was studied and protein-protein interactions were then evaluated on the modified composite transducers by scanning electron microscopy. Finally, an amperometric immunosensor approach for the detection of rabbit Immunoglobulin G target analyte was described and a minimum concentration of 3 ng ml -1 was easily measured.

  18. Plasma-activated multi-walled carbon nanotube-polystyrene composite substrates for biosensing

    Energy Technology Data Exchange (ETDEWEB)

    Fernandez-Sanchez, Cesar; Orozco, Jahir; Jimenez-Jorquera, Cecilia [Instituto de Microelectronica de Barcelona, IMB-CNM (CSIC), Campus UAB, E-08193 Bellaterra, Barcelona (Spain); Pellicer, Eva; Lechuga, Laura M; Mendoza, Ernest, E-mail: cesar.fernandez@imb-cnm.csic.e [Nanobiosensors and Molecular Nanobiophysics Group, Research Center on Nanoscience and Nanotechnology (CIN2) CSIC-ICN, ETSE, Campus UAB-Edificio Q, E-08193 Bellaterra, Barcelona (Spain)

    2009-08-19

    Carbon nanotube-polymer composites have shown to be suitable materials for the fabrication of electrochemical transducers. The exposed surface of these materials is commonly passivated by a very thin layer of the polymer component that buries the conductive carbon particles. Working with multi-walled carbon nanotube-polystyrene (MWCNT-PS) composite structures, it was previously described how a simple low power oxygen plasma process produced an effective etching of the composite surface, thereby exposing the conductive surface of CNTs. This work shows how this plasma process not only gave rise to a suitable composite conductive surface for electrochemical sensing but simultaneously exposed and created a high density of oxygen-containing functional groups at both the CNT and the PS components, without affecting the material's mechanical stability. These chemical groups could be effectively modified for the stable immobilization of biological receptors. A detailed chemical characterization of the plasma-activated composite surface was possible using x-ray photoelectron spectroscopy. The material reactivity towards the tethering of a protein was studied and protein-protein interactions were then evaluated on the modified composite transducers by scanning electron microscopy. Finally, an amperometric immunosensor approach for the detection of rabbit Immunoglobulin G target analyte was described and a minimum concentration of 3 ng ml{sup -1} was easily measured.

  19. Morphology optimization of CCVD-synthesized multiwall carbon nanotubes, using statistical design of experiments

    International Nuclear Information System (INIS)

    Nourbakhsh, Amirhasan; Ganjipour, Bahram; Zahedifar, Mostafa; Arzi, Ezatollah

    2007-01-01

    The possibility of optimization of morphological features of multiwall carbon nanotubes (MWCNTs) using the statistical design of experiments (DoE) is investigated. In this study, MWCNTs were synthesized using a catalytic chemical vapour deposition (CCVD) method in a horizontal reactor using acetylene as the carbon source. The effects of six synthesis parameters (synthesis time, synthesis temperature, catalyst mass, reduction time, acetylene flow rate and hydrogen flow rate) on the average diameter and mean rectilinear length (MRL) of carbon nanotubes were examined using fractional-factorial design (FFD) coupled with response surface methodology (RSM). Using a 2 III 6-3 FFD, the main effects of reaction temperature, hydrogen flow rate and chemical reduction time were concluded to be the key factors influencing the diameter and MRL of MWCNTs; then Box-Behnken design (BBD) was exploited to create a response surface from the main factors. The total number of required runs is 26: 8 runs are for FFD parameter screening, 17 runs are for the response surface obtained by the BBD, and the final run is used to confirm the predicted results

  20. Preparation of Multiwalled Carbon Nanotube-Poly (4-Styrenesulfonic Acid Aqueous Dispersion for Dopamine Sensing

    Directory of Open Access Journals (Sweden)

    Aihua LIU

    2006-12-01

    Full Text Available A simple and facile method for the non-covalent functionalization of multi-walled carbon nanotubes (MWNTs using poly(4-styrenesulfonic acid (PSS is proposed. The resulting PSS-MWNTs dispersion is readily soluble in water and can be left to stand for 2 weeks at room temperature, no phase separation with aggregation of nanotubes at the bottom of the vials was observed. The as-prepared PSS-MWNTs dispersions could facilitate the processing of the nanotubes into composites with high nanotube loading. The PSS-MWNTs complex shows high electrocatalytic activity to the oxidation of neutrontransmitter of dopamine, suggesting that the coating of PSS onto carbon nanotubes surface without destroying the electronic structures of the pristine carbon nanotubes; therefore, the unique properties including the catalytic property of the nanotubes retained. It is envisioned that the PSS-MWNTs aqueous dispersions may find possible applications in the development of biosensors, bioelectronics, separation and environment protection as well as other biological events where water-based environment is required.

  1. Dispersion of multi-wall carbon nanotubes in polyhistidine: Characterization and analytical applications

    International Nuclear Information System (INIS)

    Dalmasso, Pablo R.; Pedano, María L.; Rivas, Gustavo A.

    2012-01-01

    Highlights: ► Polyhistidine (Polyhis) is an efficient dispersing agent of MWCNT. ► MWCNT/Polyhis ratio and sonication time are critical variables when dispersing MWCNT. ► MWCNT–Polyhis deposited at GCE largely catalyzes the oxidation of ascorbic acid. ► GCE/MWCNT–Polyhis allows the selective and sensitive quantification of UA and Do. - Abstract: We report for the first time the use of polyhistidine (Polyhis) to efficiently disperse multiwall carbon nanotubes (MWCNTs). The optimum dispersion MWCNT–Polyhis was obtained by sonicating for 30 min 1.0 mg mL −1 MWCNTs in 0.25 mg mL −1 Polyhis solution prepared in 75:25 (v/v) ethanol/0.200 M acetate buffer solution pH 5.00. The dispersion was characterized by scanning electron microscopy, and by cyclic voltammetry and amperometry using ascorbic acid as redox marker. The modification of glassy carbon electrodes with MWCNT–Polyhis produces a drastic decrease in the overvoltage for the oxidation of ascorbic acid (580 mV) at variance with the response observed at glassy carbon electrodes modified just with Polyhis, where the charge transfer is more difficult due to the blocking effect of the polymer. The reproducibility for the sensitivities obtained after 10 successive calibration plots using the same surface was 6.3%. The MWCNT-modified glassy carbon electrode demonstrated to be highly stable since after 45 days storage at room temperature the response was 94.0% of the original. The glassy carbon electrode modified with MWCNT–Polyhis dispersion was successfully used to quantify dopamine or uric acid at nanomolar levels, even in the presence of large excess of ascorbic acid. Determinations of uric acid in human blood serum samples demonstrated a very good correlation with the value reported by Wienner laboratory.

  2. Dispersion of multi-wall carbon nanotubes in polyhistidine: Characterization and analytical applications

    Energy Technology Data Exchange (ETDEWEB)

    Dalmasso, Pablo R. [INFIQC, Departamento de Fisicoquimica, Facultad de Ciencias Quimicas, Universidad Nacional de Cordoba, Ciudad Universitaria, 5000 Cordoba (Argentina); Pedano, Maria L., E-mail: mlpedano@fcq.unc.edu.ar [INFIQC, Departamento de Fisicoquimica, Facultad de Ciencias Quimicas, Universidad Nacional de Cordoba, Ciudad Universitaria, 5000 Cordoba (Argentina); Rivas, Gustavo A., E-mail: grivas@mail.fcq.unc.edu.ar [INFIQC, Departamento de Fisicoquimica, Facultad de Ciencias Quimicas, Universidad Nacional de Cordoba, Ciudad Universitaria, 5000 Cordoba (Argentina)

    2012-01-13

    Highlights: Black-Right-Pointing-Pointer Polyhistidine (Polyhis) is an efficient dispersing agent of MWCNT. Black-Right-Pointing-Pointer MWCNT/Polyhis ratio and sonication time are critical variables when dispersing MWCNT. Black-Right-Pointing-Pointer MWCNT-Polyhis deposited at GCE largely catalyzes the oxidation of ascorbic acid. Black-Right-Pointing-Pointer GCE/MWCNT-Polyhis allows the selective and sensitive quantification of UA and Do. - Abstract: We report for the first time the use of polyhistidine (Polyhis) to efficiently disperse multiwall carbon nanotubes (MWCNTs). The optimum dispersion MWCNT-Polyhis was obtained by sonicating for 30 min 1.0 mg mL{sup -1} MWCNTs in 0.25 mg mL{sup -1} Polyhis solution prepared in 75:25 (v/v) ethanol/0.200 M acetate buffer solution pH 5.00. The dispersion was characterized by scanning electron microscopy, and by cyclic voltammetry and amperometry using ascorbic acid as redox marker. The modification of glassy carbon electrodes with MWCNT-Polyhis produces a drastic decrease in the overvoltage for the oxidation of ascorbic acid (580 mV) at variance with the response observed at glassy carbon electrodes modified just with Polyhis, where the charge transfer is more difficult due to the blocking effect of the polymer. The reproducibility for the sensitivities obtained after 10 successive calibration plots using the same surface was 6.3%. The MWCNT-modified glassy carbon electrode demonstrated to be highly stable since after 45 days storage at room temperature the response was 94.0% of the original. The glassy carbon electrode modified with MWCNT-Polyhis dispersion was successfully used to quantify dopamine or uric acid at nanomolar levels, even in the presence of large excess of ascorbic acid. Determinations of uric acid in human blood serum samples demonstrated a very good correlation with the value reported by Wienner laboratory.

  3. In situ growth rate measurements during plasma-enhanced chemical vapour deposition of vertically aligned multiwall carbon nanotube films

    International Nuclear Information System (INIS)

    Joensson, M; Nerushev, O A; Campbell, E E B

    2007-01-01

    In situ laser reflectivity measurements are used to monitor the growth of multiwalled carbon nanotube (MWCNT) films grown by DC plasma-enhanced chemical vapour deposition (PECVD) from an iron catalyst film deposited on a silicon wafer. In contrast to thermal CVD growth, there is no initial increase in the growth rate; instead, the initial growth rate is high (as much as 10 μm min -1 ) and then drops off rapidly to reach a steady level (2 μm min -1 ) for times beyond 1 min. We show that a limiting factor for growing thick films of multiwalled nanotubes (MWNTs) using PECVD can be the formation of an amorphous carbon layer at the top of the growing nanotubes. In situ reflectivity measurements provide a convenient technique for detecting the onset of the growth of this layer

  4. Multiwalled carbon nanotubes@octavinyl polyhedral oligomeric silsesquioxanes nanocomposite preparation via cross-linking reaction in acidic media

    Energy Technology Data Exchange (ETDEWEB)

    Somasekharan, Lakshmipriya; Thomas, Sabu [Mahatma Gandhi University, International and Interuniversity Centre for Nanoscience and Nanotechnology (India); Comoy, Corinne [Université de Lorraine, SRSMC, UMR 7565 (France); Sivasankarapillai, Anilkumar [NSS Hindu College (India); Kalarikkal, Nandakumar [Mahatma Gandhi University, International and Interuniversity Centre for Nanoscience and Nanotechnology (India); Lamouroux, Emmanuel, E-mail: Emmanuel.Lamouroux@univ-lorraine.fr [Université de Lorraine, SRSMC, UMR 7565 (France)

    2016-11-15

    Multiwalled carbon nanotubes have unique properties allowing their use in a wide range of applications—from microelectronics to biomedical and polymer fields. Nevertheless, a crucial aspect for their use resides in the ease of handling them during the process. Here, we report a facile route to prepare multiwalled carbon nanotubes@octavinyl polyhedral oligomeric silsesquioxanes (MWCNT@POSS) nanocomposite. The method involves the formation of a covalent bond between carboxylated MWCNTs and OV-POSS using acid-catalyzed electrophilic addition reaction. The resulting nanocomposite have been characterized by Fourier transform infrared spectroscopy (FTIR), powder X-Ray diffraction (PXRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and thermogravimetric analysis (TGA). The results confirmed that the formation of MWCNT@POSS nanocomposite did not deteriorate MWCNT structure or morphology. Here, we used a 1:1 ratio of carboxylated MWCNTs and OV-POSS and the POSS content in the nanocomposite was 39.5 wt%.

  5. Thermogravimetric analysis of atomized ferromagnetic composites with multiwalled carbon nanotubes: an unusual behavior of nickel in nanospace.

    Science.gov (United States)

    Chen, Xu; Gupta, S; Santhanam, K S V

    2014-03-01

    A spin polarization of atomized ferromagnetic atoms like cobalt or nickel in nano space results in the modification of the electron configuration in the ferromagnetic atom that changes its oxidative property. We have prepared cobalt and nickel composites with multiwalled carbon nanotubes using atomized cobalt and nickel particles, for investigating their thermal oxidative behavior by thermogravimetric analysis (TGA). The composites showed the absence of a thermal oxidation in the temperature range of ambient to the break down temperature of multiwalled carbon nanotubes at 800 degrees C. At this temperature while Co composite forms cobalt oxide, the Ni composite becomes volatile that results in the divergent behavior of the two ferromagnetic compounds with a weight gain observed in TGA for Co and a loss for Ni. The mechanisms operating in the two cases are discussed in this work.

  6. Molecular Dynamics Simulation of a Multi-Walled Carbon Nanotube Based Gear

    Science.gov (United States)

    Han, Jie; Globus, Al; Srivastava, Deepak; Chancellor, Marisa K. (Technical Monitor)

    1997-01-01

    We used molecular dynamics to investigate the properties of a multi-walled carbon nanotube based gear. Previous work computationally suggested that molecular gears fashioned from (14,0) single-walled carbon nanotubes operate well at 50-100 gigahertz. The gears were formed from nanotubes with teeth added via a benzyne reaction known to occur with C60. A modified, parallelized version of Brenner's potential was used to model interatomic forces within each molecule. A Leonard-Jones 6-12 potential was used for forces between molecules. The gear in this study was based on the smallest multi-walled nanotube supported by some experimental evidence. Each gear was a (52,0) nanotube surrounding a (37,10) nanotube with approximate 20.4 and 16,8 A radii respectively. These sizes were chosen to be consistent with inter-tube spacing observed by and were slightly larger than graphite inter-layer spacings. The benzyne teeth were attached via 2+4 cycloaddition to exterior of the (52,0) tube. 2+4 bonds were used rather than the 2+2 bonds observed by Hoke since 2+4 bonds are preferred by naphthalene and quantum calculations by Jaffe suggest that 2+4 bonds are preferred on carbon nanotubes of sufficient diameter. One gear was 'powered' by forcing the atoms near the end of the outside buckytube to rotate to simulate a motor. A second gear was allowed to rotate by keeping the atoms near the end of its outside buckytube on a cylinder. The ends of both gears were constrained to stay in an approximately constant position relative to each other, simulating a casing, to insure that the gear teeth meshed. The stiff meshing aromatic gear teeth transferred angular momentum from the powered gear to the driven gear. The simulation was performed in a vacuum and with a software thermostat. Preliminary results suggest that the powered gear had trouble turning the driven gear without slip. The larger radius and greater mass of these gears relative to the (14,0) gears previously studied requires a

  7. Efficient and facile one pot carboxylation of multiwalled carbon nanotubes by using oxidation with ozone under mild conditions

    International Nuclear Information System (INIS)

    Naeimi, Hossein; Mohajeri, Ali; Moradi, Leila; Rashidi, Ali Morad

    2009-01-01

    Graphical abstract: In this work, oxidation of carbon nanotubes with ozone in the presence of hydrogen peroxide was studied. The reactions were performed under clean and mild conditions and oxidized products with high concentration of oxygenated groups were yielded. The reaction products were characterized with attenuated total reflectance (ATR), Raman spectroscopy, scanning electron microscopy (SEM), X-ray diffractometry (XRD), back titration, X-ray photoelectron spectroscopy (XPS) and the dispersion behavior of the oxidized multiwalled carbon nanotubes (MWCNTs) was also studied. The results confirmed the presence of high concentrations of oxidative groups on the carbon nanotubes (CNTs) treated by the method of the present work.

  8. Polyvinyl alcohol (PVA)-cellulose nanofibril (CNF)-multiwalled carbon nanotube (MWCNT) hybrid organic aerogels with superior mechanical properties

    Science.gov (United States)

    Qifeng Zheng; Alireza Javadi; Ronald Sabo; Zhiyong Cai; Shaoqin Gong

    2013-01-01

    Polyvinyl alcohol (PVA)–cellulose nanofibril (CNF)–multiwalled carbon nanotube (MWCNT) hybrid organic aerogels were prepared using an environmentally friendly freeze-drying process with renewable materials. The material properties of these “green” hybrid aerogels were characterized extensively using various techniques. It was found that adding a small amount of CNFs...

  9. Extraction of ochratoxin A in red wine with dopamine-coated magnetic multi-walled carbon nanotubes.

    Science.gov (United States)

    Wan, Hong; Zhang, Bo; Bai, Xiao-Lin; Zhao, Yan; Xiao, Meng-Wei; Liao, Xun

    2017-10-01

    A new, rapid, green, and cost-effective magnetic solid-phase extraction of ochratoxin A from red wine samples was developed using polydopamine-coated magnetic multi-walled carbon nanotubes as the absorbent. The polydopamine-coated magnetic multi-walled carbon nanotubes were fabricated with magnetic multi-walled carbon nanotubes and dopamine by an in situ oxidative self-polymerization approach. Transmission electron microscopy, dynamic light scattering, X-ray photoelectron spectroscopy and vibrating sample magnetometry were used to characterize the absorbents. Ochratoxin A was quantified with high-performance liquid chromatography coupled with fluorescence detection, with excitation and emission wavelengths of 338 and 455 nm, respectively. The conditions affecting the magnetic solid-phase extraction procedure, such as pH, extraction solution, extraction time, absorbent amount, desorption solution and desorption time were investigated to obtain the optimal extraction conditions. Under the optimized conditions, the extraction recovery was 91.8-104.5% for ochratoxin A. A linear calibration curve was obtained in the range of 0.1-2.0 ng/mL. The limit of detection was 0.07 ng/mL, and the limit of quantitation was 0.21 ng/mL. The recoveries of ochratoxin A for spiked red wine sample ranged from 95.65 to 100.65% with relative standard deviation less than 8%. The polydopamine-coated magnetic multi-walled carbon nanotubes showed a high affinity toward ochratoxin A, allowing selective extraction and quantification of ochratoxin A from complex sample matrixes. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  10. Facile graft polystyrene onto multi-walled carbon nanotubes via in situ thermo-induced radical polymerization

    International Nuclear Information System (INIS)

    Liu Peng

    2009-01-01

    A facile procedure was developed for the grafting of polystyrene onto the surfaces of multi-walled carbon nanotubes (MWNTs) via the in situ thermo-induced bulk radical polymerization of styrene at the different polymerizing temperatures, in the presence of MWNTs without any initiator added. The grafting products were validated by the dispersibility, TEM, TGA, FT-IR, and Raman analysis. The TGA results also showed the lower polymerizing temperature was propitious to the free radical addition reactions.

  11. Preparation, characterization and properties of acid functionalized multi-walled carbon nanotube reinforced thermoplastic polyurethane nanocomposites

    International Nuclear Information System (INIS)

    Kumar Barick, Aruna; Kumar Tripathy, Deba

    2011-01-01

    Graphical abstract: Highlights: → Preparation and characterization of TPU nanocomposite for tailor made applications. → The structural analyses were carried out by FTIR, WAXD, FESEM and HRTEM. → The thermal and dynamic mechanical properties were evaluated by TGA, DSC and DMA. → The dynamic rheological behavior was investigated by RPA in frequency sweep. → The frequency dependence of electrical properties was studied by LCR meter. - Abstract: The multi-walled carbon nanotube (MWNT) reinforced thermoplastic polyurethane (TPU) nanocomposites were prepared through melt compounding method followed by compression molding. The spectroscopic study indicated that a strong interfacial interaction was developed between carbon nanotube (CNT) and the TPU matrix in the nanocomposites. The microscopic observation showed that the CNTs were homogeneously dispersed throughout the TPU matrix well apart from a few clusters. The results from thermal analysis indicated that the glass transition temperature (T g ) and storage modulus (E') of the nanocomposites were increased with increase in CNTs content and their thermal stability were also improved in comparison with pure TPU matrix. The rheological analysis showed the low frequency plateau of shear modulus and the shear thinning behavior of the nanocomposites. The electrical behaviors of the nanocomposites are increased with increase in weight percent (wt%) of CNT loading. The mechanical properties of nanocomposites were substantially improved by the incorporation of CNTs into the TPU matrix.

  12. Characterization of functionalized multiwalled carbon nanotubes for use in an enzymatic sensor.

    Science.gov (United States)

    Guadarrama-Fernández, Leonor; Chanona-Pérez, Jorge; Manzo-Robledo, Arturo; Calderón-Domínguez, Georgina; Martínez-Rivas, Adrián; Ortiz-López, Jaime; Vargas-García, Jorge Roberto

    2014-10-01

    Carbon nanotubes (CNT) have proven to be materials with great potential for the construction of biosensors. Development of fast, simple, and low cost biosensors to follow reactions in bioprocesses, or to detect food contaminants such as toxins, chemical compounds, and microorganisms, is presently an important research topic. This report includes microscopy and spectroscopy to characterize raw and chemically modified multiwall carbon nanotubes (MWCNTs) synthesized by chemical vapor deposition with the intention of using them as the active transducer in bioprocessing sensors. MWCNT were simultaneously purified and functionalized by an acid mixture involving HNO3-H2SO4 and amyloglucosidase attached onto the chemically modified MWCNT surface. A 49.0% decrease in its enzymatic activity was observed. Raw, purified, and enzyme-modified MWCNTs were analyzed by scanning and transmission electron microscopy and Raman and X-ray photoelectron spectroscopy. These studies confirmed purification and functionalization of the CNTs. Finally, cyclic voltammetry electrochemistry was used for electrical characterization of CNTs, which showed promising results that can be useful for construction of electrochemical biosensors applied to biological areas.

  13. Electrical and dielectric properties of foam injection-molded polypropylene/multiwalled carbon nanotube composites

    Energy Technology Data Exchange (ETDEWEB)

    Ameli, A.; Nofar, M.; Saniei, M.; Hossieny, N.; Park, C. B. [Microcellular Plastics Manufacturing Laboratory, Department of Mechanical and Industrial Engineering, University of Toronto, 5 King’s College Road, Toronto, Ontario, Canada M5S 3G8 (Canada); Pötschke, P. [Leibniz-Institut für Polymerforschung Dresden e.V. (IPF), Hohe Strasse 6, D-01069 Dresden (Germany)

    2015-05-22

    A combination of high dielectric permittivity (ε′) and low dielectric loss (tan δ) is required for charge storage applications. In percolative systems such as conductive polymer composites, however, obtaining high ε′ and low tan δ is very challenging due to the sharp insulation-conduction transition near the threshold region. Due to the particular arrangement of conductive fillers induced by both foaming and injection molding processes, they may address this issue. Therefore, this work evaluates the application of foam injection molding process in fabricating polymer nanocomposites for energy storage. Polypropylene-multiwalled carbon nanotubes (PP-MWCNT) composites were prepared by melt mixing and foamed in an injection molding process. Electrical conductivity (σ), ε′ and tan δ were then characterized. Also, scanning and transmission electron microscopy (SEM and TEM) was used to investigate the carbon nanotube’s arrangement as well as cellular morphology. The results showed that foam injection-molded composites exhibited highly superior dielectric properties to those of solid counterparts. For instance, foamed samples had ε′=68.3 and tan δ =0.05 (at 1.25 vol.% MWCNT), as opposed to ε′=17.8 and tan δ=0.04 in solid samples (at 2.56 vol.% MWCNT). The results of this work reveal that high performance dielectric nanocomposites can be developed using foam injection molding technologies for charge storage applications.

  14. Electrical resistivity and thermal properties of compatibilized multi-walled carbon nanotube/polypropylene composites

    Directory of Open Access Journals (Sweden)

    A. Szentes

    2012-06-01

    Full Text Available The electrical resistivity and thermal properties of multi-walled carbon nanotube/polypropylene (MWCNT/PP composites have been investigated in the presence of coupling agents applied for improving the compatibility between the nanotubes and the polymer. A novel olefin-maleic-anhydride copolymer and an olefin-maleic-anhydride copolymer based derivative have been used as compatibilizers to achieve better dispersion of MWCNTs in the polymer matrix. The composites have been produced by extrusion followed by injection moulding. They contained different amounts of MWCNTs (0.5, 2, 3 and 5 wt% and coupling agent to enhance the interactions between the carbon nanotubes and the polymer. The electrical resistivity of the composites has been investigated by impedance spectroscopy, whereas their thermal properties have been determined using a thermal analyzer operating on the basis of the periodic thermal perturbation method. Rheological properties, BET-area and adsorption-desorption isotherms have been determined. Dispersion of MWCNTs in the polymer has been studied by scanning electron microscopy (SEM.

  15. Structural, electronic and photovoltaic characterization of multiwalled carbon nanotubes grown directly on stainless steel

    Directory of Open Access Journals (Sweden)

    Luca Camilli

    2012-05-01

    Full Text Available We have taken advantage of the native surface roughness and the iron content of AISI-316 stainless steel to grow multiwalled carbon nanotubes (MWCNTs by chemical vapour deposition without the addition of an external catalyst. The structural and electronic properties of the synthesized carbon nanostructures have been investigated by a range of electron microscopy and spectroscopy techniques. The results show the good quality and the high graphitization degree of the synthesized MWCNTs. Through energy-loss spectroscopy we found that the electronic properties of these nanostructures are markedly different from those of highly oriented pyrolytic graphite (HOPG. Notably, a broadening of the π-plasmon peak in the case of MWCNTs is evident. In addition, a photocurrent was measured when MWCNTs were airbrushed onto a silicon substrate. External quantum efficiency (EQE and photocurrent values were reported both in planar and in top-down geometry of the device. Marked differences in the line shapes and intensities were found for the two configurations, suggesting that two different mechanisms of photocurrent generation and charge collection are in operation. From this comparison, we are able to conclude that the silicon substrate plays an important role in the production of electron–hole pairs.

  16. Heat transfer nanofluid based on curly ultra-long multi-wall carbon nanotubes

    Science.gov (United States)

    Boncel, Sławomir; Zniszczoł, Aurelia; Pawlyta, Mirosława; Labisz, Krzysztof; Dzido, Grzegorz

    2018-02-01

    The main challenge in the use of multi-wall carbon nanotube (MWCNT) as key components of nanofluids is to transfer excellent thermal properties from individual nanotubes into the bulk systems. We present studies on the performance of heat transfer nanofluids based on ultra-long ( 2 mm), curly MWCNTs - in the background of various other nanoC-sp2, i.e. oxidized MWCNTs, commercially available Nanocyl™ MWCNTs and spherical carbon nanoparticles (SCNs). The nanofluids prepared via ultrasonication from water and propylene glycol were studied in terms of heat conductivity and heat transfer in a scaled up thermal circuit containing a copper helical heat exchanger. Ultra-long curly MWCNT (1 wt.%) nanofluids (stabilized with Gum Arabic in water) emerged as the most thermally conducting ones with a 23-30%- and 39%-enhancement as compared to the base-fluids for water and propylene glycol, respectively. For turbulent flows ( Re = 8000-11,000), the increase of heat transfer coefficient for the over-months stable 1 wt.% ultra-long MWCNT nanofluid was found as high as >100%. The findings allow to confirm that longer MWCNTs are promising solid components in nanofluids and hence to predict their broader application in heat transfer media.

  17. Nanocomposites of Graphene Nanosheets/Multiwalled Carbon Nanotubes as Electrodes for In-plane Supercapacitors

    International Nuclear Information System (INIS)

    Trigueiro, João Paulo C.; Lavall, Rodrigo L.; Silva, Glaura G.

    2016-01-01

    Flexible supercapacitors with large power and energy densities, long life cycles and good operational safety are necessary devices for various applications. In this work, we demonstrate the integration of a composite based on graphene nanosheets/multiwalled carbon nanotubes in an in-plane supercapacitor configuration by using a straightforward preparation involving the filtration of nanomaterials to produce an electrode film. Reduced graphene oxide (RGO) received 15 wt % carbon nanotubes to act as a conducting additive, which led to a flexible and transferable thin film (RGO/MW) with an average conductivity of 20.0 S cm −1 . Three ionic liquids were tested as electrolytes for the supercapacitor, among which 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide (EMITFSI) was observed to exhibit the best performance. The specific capacitance of the supercapacitor based on RGO/MW-EMITFSI reached 153.7 F g −1 at a current density of 0.2 A g −1 and exhibited a capacitance retention of 88% after 2000 cycles. The maximum energy and power densities were calculated to be 41.3 Wh kg −1 and 3.5 kW kg −1 , respectively, for the RGO/MW-EMITFSI supercapacitor.

  18. 3D printing nano conductive multi-walled carbon nanotube scaffolds for nerve regeneration

    Science.gov (United States)

    Lee, Se-Jun; Zhu, Wei; Nowicki, Margaret; Lee, Grace; Nyoung Heo, Dong; Kim, Junghoon; Zuo, Yi Y.; Zhang, Lijie Grace

    2018-02-01

    Objective. Nanomaterials, such as carbon nanotubes (CNTs), have been introduced to modify the surface properties of scaffolds, thus enhancing the interaction between the neural cells and biomaterials. In addition to superior electrical conductivity, CNTs can provide nanoscale structures similar to those present in the natural neural environment. The primary objective of this study is to investigate the proliferative capability and differential potential of neural stem cells (NSCs) seeded on a CNT incorporated scaffold. Approach. Amine functionalized multi-walled carbon nanotubes (MWCNTs) were incorporated with a PEGDA polymer to provide enhanced electrical properties as well as nanofeatures on the surface of the scaffold. A stereolithography 3D printer was employed to fabricate a well-dispersed MWCNT-hydrogel composite neural scaffold with a tunable porous structure. 3D printing allows easy fabrication of complex 3D scaffolds with extremely intricate microarchitectures and controlled porosity. Main results. Our results showed that MWCNT-incorporated scaffolds promoted neural stem cell proliferation and early neuronal differentiation when compared to those scaffolds without the MWCNTs. Furthermore, biphasic pulse stimulation with 500 µA current promoted neuronal maturity quantified through protein expression analysis by quantitative polymerase chain reaction. Significance. Results of this study demonstrated that an electroconductive MWCNT scaffold, coupled with electrical stimulation, may have a synergistic effect on promoting neurite outgrowth for therapeutic application in nerve regeneration.

  19. Investigation of Mechanical Properties and Morphology of Multi-Walled Carbon Nanotubes Reinforced Cellulose Acetate Fibers

    Directory of Open Access Journals (Sweden)

    Quazi Nahida Sultana

    2017-11-01

    Full Text Available Cellulose acetate (CA fibers were reinforced with multi-walled carbon nanotubes (MWCNTs at 0.5%, 1.0%, 1.5% and 2.0%. Yield strength, ultimate tensile strength, fracture strain and toughness of the nanocomposite fiber increased up to 1.5 wt. % of the carbon nanotube (CNT loading, however, further inclusion (2.0% of MWCNTs in CA decreased the mechanical properties. Experimental properties were also compared with analytical predictions using a Shear lag model for strength and the rule of mixture for modulus. A solution spinning process, coupled with sonication, mixing, and extrusion, was used to process the CNT-reinforced composite fiber. Scanning electron microscopy (SEM images of the cross sections of neat CA and CA-MWCNT fibers showed the formation of voids and irregular features. The enhanced interconnected fibrillation in the CNT-reinforced CA samples resulted in improved mechanical properties, which were observed by tensile testing. Fourier transform infrared spectroscopy (FTIR spectra showed the area under the curve for C–H bonding after the inclusion of CNT. There was no significant shift of wavenumber for the inclusion of MWCNT in the CA matrix, which indicates that the sonication process of the CNT-loaded solution did not degrade the CA bonding structure.

  20. Measurements of near-ultimate strength for multiwalled carbon nanotubes and irradiation-induced crosslinking improvements.

    Science.gov (United States)

    Peng, Bei; Locascio, Mark; Zapol, Peter; Li, Shuyou; Mielke, Steven L; Schatz, George C; Espinosa, Horacio D

    2008-10-01

    The excellent mechanical properties of carbon nanotubes are being exploited in a growing number of applications from ballistic armour to nanoelectronics. However, measurements of these properties have not achieved the values predicted by theory due to a combination of artifacts introduced during sample preparation and inadequate measurements. Here we report multiwalled carbon nanotubes with a mean fracture strength >100 GPa, which exceeds earlier observations by a factor of approximately three. These results are in excellent agreement with quantum-mechanical estimates for nanotubes containing only an occasional vacancy defect, and are approximately 80% of the values expected for defect-free tubes. This performance is made possible by omitting chemical treatments from the sample preparation process, thus avoiding the formation of defects. High-resolution imaging was used to directly determine the number of fractured shells and the chirality of the outer shell. Electron irradiation at 200 keV for 10, 100 and 1,800 s led to improvements in the maximum sustainable loads by factors of 2.4, 7.9 and 11.6 compared with non-irradiated samples of similar diameter. This effect is attributed to crosslinking between the shells. Computer simulations also illustrate the effects of various irradiation-induced crosslinking defects on load sharing between the shells.

  1. Application of multiwall carbon nanotubes for thermal dissipation in a micro-processor

    Energy Technology Data Exchange (ETDEWEB)

    Bui Hung Thang; Phan Ngoc Hong; Phan Hong Khoi; Phan Ngoc Minh [Institute of Materials Science, Vietnam Academy of Science and Technology, 18 Hoang Quoc Viet Road, Cau Giay District, Hanoi (Viet Nam)], E-mail: minhpn@ims.vast.ac.vn

    2009-09-01

    One of the most valuable properties of the carbon nanotubes materials is its high thermal conductivity with 2000 W/m.K (compared to thermal conductivity of Ag 419 W/m.K). It suggested an approach in applying the CNTs in thermal dissipation media to improve the performance of computer processors and other high power electronic devices. In this research, the multiwall carbon nanotubes (MWCNTs) made by thermal chemical vapour deposition (CVD) at our laboratory was employed as the heat dissipation media in a microprocessor a Personal Computer with configuration: Intel Pentium IV 3.066 GHz, 512Mb of RAM and Windows XP Service Pack 2 Operating System. We directly measured the temperature of the microprocessor during the operation of the computer in two modes: 100% usage CPU mode and over-clocking mode. The measured results showed that when using our thermal dissipation media (a mixture of the mentioned commercial thermal compound and 2 wt.%. MWCNTs), the temperature of the microprocessor decreased 5 deg. C, and the time for increasing the temperature of the microprocessor was three times longer than that when using commercial thermal compound. In over-clocking mode, the processor speed reached 3.8 GHz with 165 MHz of system bus clock speed; it was 1.24 times higher than that in non over-clocking mode. The results confirmed a promising way of using MWCNTs as the thermal dissipation media for microprocessor and high power electronic devices.

  2. Tuning vertical alignment and field emission properties of multi-walled carbon nanotube bundles

    Science.gov (United States)

    Sreekanth, M.; Ghosh, S.; Srivastava, P.

    2018-01-01

    We report the growth of vertically aligned carbon nanotube bundles on Si substrate by thermal chemical vapor deposition technique. Vertical alignment was achieved without any carrier gas or lithography-assisted deposition. Growth has been carried out at 850 °C for different quantities of solution of xylene and ferrocene ranging from 2.25 to 3.00 ml in steps of 0.25 ml at a fixed concentration of 0.02 gm (ferrocene) per ml. To understand the growth mechanism, deposition was carried out for different concentrations of the solution by changing only the ferrocene quantity, ranging from 0.01 to 0.03 gm/ml. A tunable vertical alignment of multi-walled carbon nanotubes (CNTs) has been achieved by this process and examined by scanning and transmission electron microscopic techniques. Micro-crystalline structural analysis has been done using Raman spectroscopy. A systematic variation in field emission (FE) current density has been observed. The highest FE current density is seen for the film grown with 0.02 gm/ml concentration, which is attributed to the better alignment of CNTs, less structural disorder and less entanglement of CNTs on the surface. The alignment of CNTs has been qualitatively understood on the basis of self-assembled catalytic particles.

  3. Electrical and Raman spectroscopic studies of vertically aligned multi-walled carbon nanotubes.

    Science.gov (United States)

    Mathur, Ashish; Tweedie, Mark; Roy, Susanta Sinha; Maguire, P D; McLaughlin, James A

    2009-07-01

    Microwave plasma enhanced chemical vapour deposition (MPECVD) was used for the production of carbon nanotubes. Vertically aligned multi-walled carbon nanotubes (MWCNTs) were grown on silicon substrates coated with cobalt thin films of thickness ranging from 0.5 nm to 3 nm. Prior to the nanotube growth the catalyst were treated with N2 plasma for 5-10 minutes that break the films into small nanoparticles which favour the growth of nanotubes. The CNTs were grown at a substrate temperature of 700 degrees C for 5, 10 and 15 minutes. The height of the CNT films ranging from 10 microm-30 microm indicating that the initial growth rate of the CNTs are very high at a rate of approximately 100 nm/sec. Electrical resistivity of the above samples was evaluated from I-V measurements. The activation energy (E(a)) was also calculated from the temperature dependent studies and it was found that the E(a) lies in the range of 15-35 meV. Raman spectroscopy was used to identify the quality of the nanotubes.

  4. Development of Prototype Laboratory Setup for Selective Detection of Ethylene Based on Multiwalled Carbon Nanotubes

    Directory of Open Access Journals (Sweden)

    J. Kathirvelan

    2014-01-01

    Full Text Available We report here a prototype laboratory setup for detecting ethylene (C2H4 in ppm level employing a sensor made of multiwalled carbon nanotubes of 40 nm average tube diameter. The proposed reversible chemoresistive ethylene sensor is fabricated using Kapton as the substrate onto which carbon nanotubes are coated using thick film technology. IDT silver electrodes are printed using piezo head based ink-jet printing technology. The increases in electrical resistance of the sensor element are measured on exposure to ethylene for different ethylene concentrations using a potentiostat and data acquisition system. The increase in resistance of the calibrated sensor element on exposure to ethylene (analyte is about 18.4% at room temperature for 50 ppm ethylene concentration. This change is reversible. Our sensor element exhibits a better performance than those reported earlier (1.8% and it has got the rise and fall time of 10 s and 60 s, respectively. It could be used for testing the ripening of fruits.

  5. Measurements of near-ultimate strength for multiwalled carbon nanotubes and irradiation-induced crosslinking improvements.

    Energy Technology Data Exchange (ETDEWEB)

    Peng, B.; Locascio, M.; Zapol, P.; Li, S.; Mielke, S. L.; Schatz, G. C.; Espinosa, H. D.; Northwestern Univ.

    2008-01-01

    The excellent mechanical properties of carbon nanotubes are being exploited in a growing number of applications from ballistic armour to nanoelectronics. However, measurements of these properties have not achieved the values predicted by theory due to a combination of artifacts introduced during sample preparation and inadequate measurements. Here we report multiwalled carbon nanotubes with a mean fracture strength >100 GPa, which exceeds earlier observations by a factor of approximately three. These results are in excellent agreement with quantum-mechanical estimates for nanotubes containing only an occasional vacancy defect, and are {approx}80% of the values expected for defect-free tubes. This performance is made possible by omitting chemical treatments from the sample preparation process, thus avoiding the formation of defects. High-resolution imaging was used to directly determine the number of fractured shells and the chirality of the outer shell. Electron irradiation at 200 keV for 10, 100 and 1,800 s led to improvements in the maximum sustainable loads by factors of 2.4, 7.9 and 11.6 compared with non-irradiated samples of similar diameter. This effect is attributed to crosslinking between the shells. Computer simulations also illustrate the effects of various irradiation-induced crosslinking defects on load sharing between the shells.

  6. Measurements of near-ultimate strength for multiwalled carbon nanotubes and irradiation-induced crosslinking improvements

    International Nuclear Information System (INIS)

    Peng, B.; Locascio, M.; Zapol, P.; Li, S.; Mielke, S.L.; Schatz, G.C.; Espinosa, H.D.

    2008-01-01

    The excellent mechanical properties of carbon nanotubes are being exploited in a growing number of applications from ballistic armour to nanoelectronics. However, measurements of these properties have not achieved the values predicted by theory due to a combination of artifacts introduced during sample preparation and inadequate measurements. Here we report multiwalled carbon nanotubes with a mean fracture strength >100 GPa, which exceeds earlier observations by a factor of approximately three. These results are in excellent agreement with quantum-mechanical estimates for nanotubes containing only an occasional vacancy defect, and are ∼80% of the values expected for defect-free tubes. This performance is made possible by omitting chemical treatments from the sample preparation process, thus avoiding the formation of defects. High-resolution imaging was used to directly determine the number of fractured shells and the chirality of the outer shell. Electron irradiation at 200 keV for 10, 100 and 1,800 s led to improvements in the maximum sustainable loads by factors of 2.4, 7.9 and 11.6 compared with non-irradiated samples of similar diameter. This effect is attributed to crosslinking between the shells. Computer simulations also illustrate the effects of various irradiation-induced crosslinking defects on load sharing between the shells.

  7. Amperometric Acetylcholinesterase Biosensor Based on Multilayer Multiwall Carbon Nanotubes-chitosan Composite

    Directory of Open Access Journals (Sweden)

    Xia SUN

    2011-11-01

    Full Text Available A simple method for immobilization of acetylcholinesterase (AChE onto the glassy carbon electrode (GCE modified with five layers of multiwall carbon nanotubes (MWNTs-chitosan (CHIT composite was proposed, and thus a fast, sensitive and stable amperometric sensor for quantitative determination of pesticides was developed. Five layers of MWNTs-CHIT promoted electron transfer reactions at a lower potential and catalyzed the electro-oxidation of thiocholine, thus, it improved the detection sensitivity of biosensor. Based on the inhibition of pesticides to the enzymatic activity of AChE, using carbofuran as a model compound, under optimal conditions, the inhibition of carbofuran was proportional to its concentration in two ranges, from 5×10-4 to 7.5 μg/mL and 7.5 to 20 μg/mL with a detection limit of 1×10-4 μg/mL. The constructed biosensor showed prominent characteristics and performances such as good precision, acceptable stability, fast response and low detection limit, which provided a new promising tool for pesticide analysis.

  8. Plasma-modified graphene nanoplatelets and multiwalled carbon nanotubes as fillers for advanced rubber composites

    International Nuclear Information System (INIS)

    Sicinski, M; Gozdek, T; Bielinski, D M; Kleczewska, J; Szymanowski, H; Piatkowska, A

    2015-01-01

    In modern rubber industry, there still is a room for new fillers, which can improve the mechanical properties of the composites, or introduce a new function to the material. Modern fillers like carbon nanotubes or graphene nanoplatelets (GnP), are increasingly applied in advanced polymer composites technology. However, it might be hard to obtain a well dispersed system for such systems. The polymer matrix often exhibits higher surface free energy (SFE) level with the filler, which can cause problems with polymer-filler interphase adhesion. Filler particles are not wet properly by the polymer, and thus are easier to agglomerate. As a consequence, improvement in the mechanical properties is lower than expected. In this work, multi-walled carbon nanotubes (MWCNT) and GnP surface were modified with low-temperature plasma. Attempts were made to graft some functionalizing species on plasma-activated filler surface. The analysis of virgin and modified fillers’ SFE was carried out. MWCNT and GnP rubber composites were produced, and ultimately, their morphology and mechanical properties were studied. (paper)

  9. Dependence of the cytotoxicity of multi-walled carbon nanotubes on the culture medium

    International Nuclear Information System (INIS)

    Zhu Ying; Ran Tiecheng; Li Yuguo; Guo Jinxue; Li Wenxin

    2006-01-01

    This study examined the influence of multi-walled carbon nanotubes (MWNTs) on the growth of the unicellular protozoan Tetrahymena pyriformis. Contrary to the findings from most other investigations, our experiment indicated that MWNTs stimulated growth of the cells cultured in proteose peptone yeast extract medium (PPY). Atomic force microscopy images and thermogravimetric analysis showed the spontaneous formation of peptone-MWNT conjugates in the medium by noncovalent binding. Uptake of large amounts of the conjugates by Tetrahymena pyriformis was responsible for growth stimulation, evidenced by images with fluorescently labelled peptone. After the PPY medium was replaced by a filtrated pond water medium (FPW), however, inhibition of the growth of cells exposed to MWNTs occurred. Measurements of the level of malondialdehyde and superoxide dismutase activity demonstrated further that MWNTs might be either toxic or nontoxic, depending on the medium used to cultivate Tetrahymena pyriformis. The biological effects of the interaction of MWNTs with some composites in culture media would be helpful for understanding the mechanisms of the toxicity of carbon nanotubes to living systems

  10. Magnetic MoS2 on multiwalled carbon nanotubes for sulfide sensing.

    Science.gov (United States)

    Li, Chunxiang; Zhang, Dan; Wang, Jiankang; Hu, Pingan; Jiang, Zhaohua

    2017-07-04

    A novel hybrid metallic cobalt insided in multiwalled carbon nanotubles/molybdenum disulfide (Co@CNT/MoS 2 ) modified glass carbon electrode (GCE) was fabricated with a adhesive of Nafion suspension and used as chemical sensors for sulfide detection. Single-layered MoS 2 was coated on CNTs through magnetic traction force between paramagnetic monolayer MoS 2 and Co particles in CNTs. Co particles faciliated the collection of paramagnetic monolayer MoS 2 exfoliated from bulk MoS 2 in solution. Amperometric analysis, cycle voltammetry, cathodic stripping analysis and linear sweep voltammetry results showed the Co@CNT/MoS 2 modified GCE exhibited excellent electrochemical activity to sulfide in buffer solutions, but amperometric analysis was found to be more sensitive than the other methods. The amperometric response result indicated the Co@CNT/MoS 2 -modified GCE electrode was an excellent electrochemical sensor for detecting S 2- with a detection limit of 7.6 nM and sensitivity of 0.23 mA/μM. The proposed electrode was used for the determination of sulfide levels in hydrogen sulfide-pretreated fruits, and the method was also verified with recovery studies. Copyright © 2017 Elsevier B.V. All rights reserved.

  11. Graphene versus Multi-Walled Carbon Nanotubes for Electrochemical Glucose Biosensing

    Directory of Open Access Journals (Sweden)

    Edmond Lam

    2013-03-01

    Full Text Available : A simple procedure was developed for the fabrication of electrochemical glucose biosensors using glucose oxidase (GOx, with graphene or multi-walled carbon nanotubes (MWCNTs. Graphene and MWCNTs were dispersed in 0.25% 3-aminopropyltriethoxysilane (APTES and drop cast on 1% KOH-pre-treated glassy carbon electrodes (GCEs. The EDC (1-ethyl-(3-dimethylaminopropyl carbodiimide-activated GOx was then bound covalently on the graphene- or MWCNT-modified GCE. Both the graphene- and MWCNT-based biosensors detected the entire pathophysiological range of blood glucose in humans, 1.4–27.9 mM. However, the direct electron transfer (DET between GOx and the modified GCE’s surface was only observed for the MWCNT-based biosensor. The MWCNT-based glucose biosensor also provided over a four-fold higher current signal than its graphene counterpart. Several interfering substances, including drug metabolites, provoked negligible interference at pathological levels for both the MWCNT- and graphene-based biosensors. However, the former was more prone to interfering substances and drug metabolites at extremely pathological concentrations than its graphene counterpart.

  12. Graphene versus Multi-Walled Carbon Nanotubes for Electrochemical Glucose Biosensing.

    Science.gov (United States)

    Zheng, Dan; Vashist, Sandeep Kumar; Dykas, Michal Marcin; Saha, Surajit; Al-Rubeaan, Khalid; Lam, Edmond; Luong, John H T; Sheu, Fwu-Shan

    2013-03-14

    : A simple procedure was developed for the fabrication of electrochemical glucose biosensors using glucose oxidase (GOx), with graphene or multi-walled carbon nanotubes (MWCNTs). Graphene and MWCNTs were dispersed in 0.25% 3-aminopropyltriethoxysilane (APTES) and drop cast on 1% KOH-pre-treated glassy carbon electrodes (GCEs). The EDC (1-ethyl-(3-dimethylaminopropyl) carbodiimide)-activated GOx was then bound covalently on the graphene- or MWCNT-modified GCE. Both the graphene- and MWCNT-based biosensors detected the entire pathophysiological range of blood glucose in humans, 1.4-27.9 mM. However, the direct electron transfer (DET) between GOx and the modified GCE's surface was only observed for the MWCNT-based biosensor. The MWCNT-based glucose biosensor also provided over a four-fold higher current signal than its graphene counterpart. Several interfering substances, including drug metabolites, provoked negligible interference at pathological levels for both the MWCNT- and graphene-based biosensors. However, the former was more prone to interfering substances and drug metabolites at extremely pathological concentrations than its graphene counterpart.

  13. Laser-induced selective metallization of polypropylene doped with multiwall carbon nanotubes

    Science.gov (United States)

    Ratautas, Karolis; Gedvilas, Mindaugas; Stankevičiene, Ina; Jagminienė, Aldona; Norkus, Eugenijus; Pira, Nello Li; Sinopoli, Stefano; Račiukaitis, Gediminas

    2017-08-01

    Moulded interconnect devices (MID) offer the material, weight and cost saving by integration electronic circuits directly into polymeric components used in automotive and other consumer products. Lasers are used to write circuits directly by modifying the surface of polymers followed by an electroless metal plating. A new composite material - the polypropylene doped with multiwall carbon nanotubes was developed for the laser-induced selective metallization. Mechanism of surface activation by laser irradiation was investigated in details utilising pico- and nanoseconds lasers. Deposition of copper was performed in the autocatalytic electroless plating bath. The laser-activated polymer surfaces have been studied using the Raman spectroscopy and scanning electron microscope (SEM). Microscopic images revealed that surface becomes active only after its melting by a laser. Alterations in the Raman spectra of the D and G bands indicated the clustering of carbon additives in the composite material. Optimal laser parameters for the surface activation were found by measuring a sheet resistance of the finally metal-plated samples. A spatially selective copper plating was achieved with the smallest conductor line width of 22 μm at the laser scanning speed of 3 m/s and the pulse repetition rate of 100 kHz. Finally, the technique was validated by making functional electronic circuits by this MID approach.

  14. Application of multiwall carbon nanotubes for thermal dissipation in a micro-processor

    Science.gov (United States)

    Thang, Bui Hung; Hong, Phan Ngoc; Khoi, Phan Hong; Minh, Phan Ngoc

    2009-09-01

    One of the most valuable properties of the carbon nanotubes materials is its high thermal conductivity with 2000 W/m.K (compared to thermal conductivity of Ag 419 W/m.K). It suggested an approach in applying the CNTs in thermal dissipation media to improve the performance of computer processors and other high power electronic devices. In this research, the multiwall carbon nanotubes (MWCNTs) made by thermal chemical vapour deposition (CVD) at our laboratory was employed as the heat dissipation media in a microprocessor a Personal Computer with configuration: Intel Pentium IV 3.066 GHz, 512Mb of RAM and Windows XP Service Pack 2 Operating System. We directly measured the temperature of the microprocessor during the operation of the computer in two modes: 100% usage CPU mode and over-clocking mode. The measured results showed that when using our thermal dissipation media (a mixture of the mentioned commercial thermal compound and 2 wt.%. MWCNTs), the temperature of the microprocessor decreased 5°C, and the time for increasing the temperature of the microprocessor was three times longer than that when using commercial thermal compound. In over-clocking mode, the processor speed reached 3.8 GHz with 165 MHz of system bus clock speed; it was 1.24 times higher than that in non over-clocking mode. The results confirmed a promising way of using MWCNTs as the thermal dissipation media for microprocessor and high power electronic devices.

  15. Application of multiwall carbon nanotubes for thermal dissipation in a micro-processor

    International Nuclear Information System (INIS)

    Bui Hung Thang; Phan Ngoc Hong; Phan Hong Khoi; Phan Ngoc Minh

    2009-01-01

    One of the most valuable properties of the carbon nanotubes materials is its high thermal conductivity with 2000 W/m.K (compared to thermal conductivity of Ag 419 W/m.K). It suggested an approach in applying the CNTs in thermal dissipation media to improve the performance of computer processors and other high power electronic devices. In this research, the multiwall carbon nanotubes (MWCNTs) made by thermal chemical vapour deposition (CVD) at our laboratory was employed as the heat dissipation media in a microprocessor a Personal Computer with configuration: Intel Pentium IV 3.066 GHz, 512Mb of RAM and Windows XP Service Pack 2 Operating System. We directly measured the temperature of the microprocessor during the operation of the computer in two modes: 100% usage CPU mode and over-clocking mode. The measured results showed that when using our thermal dissipation media (a mixture of the mentioned commercial thermal compound and 2 wt.%. MWCNTs), the temperature of the microprocessor decreased 5 deg. C, and the time for increasing the temperature of the microprocessor was three times longer than that when using commercial thermal compound. In over-clocking mode, the processor speed reached 3.8 GHz with 165 MHz of system bus clock speed; it was 1.24 times higher than that in non over-clocking mode. The results confirmed a promising way of using MWCNTs as the thermal dissipation media for microprocessor and high power electronic devices.

  16. Multiwalled Carbon Nanotube Synthesis Using Arc Discharge with Hydrocarbon as Feedstock

    Directory of Open Access Journals (Sweden)

    K. T. Chaudhary

    2013-01-01

    Full Text Available Synthesis of multiwalled carbon nanotube (MWCNT by arc discharge process is investigated with methane (CH4 as background and feedstock gas. The arc discharge is carried out between two graphite electrodes for ambient pressures 100, 300, and 500 torr and arc currents 50, 70, and 90 A. Plasma kinetics such as the density and temperature for arc discharge carbon plasma is determined to find out the contribution of physical parameters as arc current and ambient pressure on the plasma dynamics and growth of MWCNT. With increase in applied arc current and ambient pressure, an increase in plasma temperature and density is observed. The synthesized samples of MWCNT at different experimental conditions are characterized by transmission electron microscopy, scanning electron microscopy, Raman spectroscopy, Fourier transform infrared spectroscopy, and X-ray diffraction. A decrease in the diameter and improvement in structure quality and growth of MWCNT are observed with increase in CH4 ambient pressure and arc current. For CH4 ambient pressure 500 torr and arc current 90 A, the well-aligned and straight MWCNT along with graphene stakes are detected.

  17. On the possibility of electrochemical unzipping of multiwalled carbon nanotubes to produce graphene nanoribbons

    Energy Technology Data Exchange (ETDEWEB)

    Zehtab Yazdi, Alireza; Roberts, Edward P.L.; Sundararaj, Uttandaraman, E-mail: u.sundararaj@ucalgary.ca

    2016-08-15

    Highlights: • MWCNTs synthesized and electrochemically oxidized to study the formation of GNR • HRTEM, Raman and XPS confirmed no successful unzipping occurred after oxidation • Electrochemical oxidation very unlikely facilitate formation of intercalated MWCNTs - Abstract: Multiwalled carbon nanotubes (MWCNTs) with different geometrical characteristics and chemical doping have been synthesized and electrochemically oxidized to study the possibility of unzipping, and creating graphene nanoribbon (GNR) nanostructures. Modified glassy carbon electrodes of the MWCNTs have been tested in an aqueous electrolyte via anodic scans in a wide range of potentials, followed by keeping at the maximum potential for different times. The microstructural features, structural defects, and functional groups and their elements have been then studied using high resolution transmission electron microscopy (HRTEM), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS), respectively. All results have confirmed that no successful unzipping occurs in the MWCNTs after electrochemical oxidation, even for the nitrogen-doped MWCNTs (CN{sub x}-MWCNTs) with reactive nitrogen groups and defective bamboo structures. In contrast to the report by Shinde et al. (J. Am. Chem. Soc. 2011, 133, 4168–4171), it has been concluded that the electrochemical oxidation in aqueous electrolytes is very unlikely to facilitate sufficient incorporation of the intercalated molecules among the walls of the MWCNTs. These molecules are, however, responsible for unzipping of MWCNTs.

  18. Long-Term Effects of Multiwalled Carbon Nanotubes and Graphene on Microbial Communities in Dry Soil.

    Science.gov (United States)

    Ge, Yuan; Priester, John H; Mortimer, Monika; Chang, Chong Hyun; Ji, Zhaoxia; Schimel, Joshua P; Holden, Patricia A

    2016-04-05

    Little is known about the long-term effects of engineered carbonaceous nanomaterials (ECNMs) on soil microbial communities, especially when compared to possible effects of natural or industrial carbonaceous materials. To address these issues, we exposed dry grassland soil for 1 year to 1 mg g(-1) of either natural nanostructured material (biochar), industrial carbon black, three types of multiwalled carbon nanotubes (MWCNTs), or graphene. Soil microbial biomass was assessed by substrate induced respiration and by extractable DNA. Bacterial and fungal communities were examined by terminal restriction fragment length polymorphism (T-RFLP). Microbial activity was assessed by soil basal respiration. At day 0, there was no treatment effect on soil DNA or T-RFLP profiles, indicating negligible interference between the amended materials and the methods for DNA extraction, quantification, and community analysis. After a 1-year exposure, compared to the no amendment control, some treatments reduced soil DNA (e.g., biochar, all three MWCNT types, and graphene; P graphene); however, there were no significant differences across the amended treatments. These findings suggest that ECNMs may moderately affect dry soil microbial communities but that the effects are similar to those from natural and industrial carbonaceous materials, even after 1-year exposure.

  19. Electrochemical Oxidation of Sulfamethazine on Multi-Walled Nanotube Film Coated Glassy Carbon Electrode

    Directory of Open Access Journals (Sweden)

    L. Fotouhi

    2014-04-01

    Full Text Available The electrochemical oxidation of sulfamethazine (SMZ has been studied at a multi-walled carbon nanotubes modified glassy carbon electrode (MWCNT-GCE by cyclic voltammetry. This modified electrode (MWCNT-GCE exhibited excellent electrocatalytic behavior toward the oxidation of SMZ as evidenced by the enhancement of the oxidation peak current and the shift in the anodic potential to less positive values (170 mV in comparison with the bare GCE. The formal potential, E0', of SMZ is pH dependent with a slope of 54 mV per unit of pH, close to the anticipated Nerstian value of 59 mV for a 2-electron and 2-proton oxidation process. A detailed analysis of cyclic voltammograms gave fundamental electrochemical parameters including the electroactive surface coverage (Г, the transfer coefficient (a, the heterogeneous rate constant (ks. Under the selected conditions, the peak current shows two dynamic linear ranges of 10-200 mM and 300-3000 mM with the detection limit of 6.1 mM. The method was successfully applied to analyze SMZ in serum sample

  20. Study on the Highly Sensitive AChE Electrode Based on Multiwalled Carbon Nanotubes

    Directory of Open Access Journals (Sweden)

    Shuping Zhang

    2014-01-01

    Full Text Available Using chitosan (CS as carrier, the method named layer-by-layer (LBL self-assembly modification to modify the glassy carbon electrode (GCE with multiwalled carbon nanotubes (MWNTs and acetylcholine esterase (AChE was proposed to prepare the acetylcholine esterase electrode with high sensitivity and stability. The modified electrode was used to detect pesticide of aldicarb, and the enzyme inhibition rate of the electrode showed good linearity with pesticide concentrations in the range of 10−10 g·L−1 to 10−3 g·L−1. The detection limit was 10−11 g·L−1. The modified electrode was also used to detect the actual sample, and the recovery rate range was from 97.72% to 107.15%, which could meet the rapid testing need of the aldicarb residue. After being stored in the phosphate buffer solution (PBS in 4°C for 30 days, the modified electrode showed good stability with the response current that was 80% of the original current.

  1. Selective ex-vivo photothermal ablation of human pancreatic cancer with albumin functionalized multiwalled carbon nanotubes.

    Science.gov (United States)

    Mocan, Lucian; Tabaran, Flaviu A; Mocan, Teodora; Bele, Constantin; Orza, Anamaria Ioana; Lucan, Ciprian; Stiufiuc, Rares; Manaila, Ioana; Iulia, Ferencz; Dana, Iancu; Zaharie, Florin; Osian, Gelu; Vlad, Liviu; Iancu, Cornel

    2011-01-01

    The process of laser-mediated ablation of cancer cells marked with biofunctionalized carbon nanotubes is frequently called "nanophotothermolysis". We herein present a method of selective nanophotothermolisys of pancreatic cancer (PC) using multiwalled carbon nanotubes (MWCNTs) functionalized with human serum albumin (HSA). With the purpose of testing the therapeutic value of these nanobioconjugates, we have developed an ex-vivo experimental platform. Surgically resected specimens from patients with PC were preserved in a cold medium and kept alive via intra-arterial perfusion. Additionally, the HSA-MWCNTs have been intra-arterially administered in the greater pancreatic artery under ultrasound guidance. Confocal and transmission electron microscopy combined with immunohistochemical staining have confirmed the selective accumulation of HSA-MWCNTs inside the human PC tissue. The external laser irradiation of the specimen has significantly produced extensive necrosis of the malign tissue after the intra-arterial administration of HSA-MWCNTs, without any harmful effects on the surrounding healthy parenchyma. We have obtained a selective photothermal ablation of the malign tissue based on the selective internalization of MWCNTs with HSA cargo inside the pancreatic adenocarcinoma after the ex-vivo intra-arterial perfusion.

  2. Field-Effect-Transistor Behavior of a Multiwall Carbon Nano Fiber Directly Grown on Nickel Electrodes

    Directory of Open Access Journals (Sweden)

    L. W. Chang

    2009-01-01

    Full Text Available Multiwall carbon nanofibers (MWCNFs were directly grown across the catalyst electrodes fabricated through photolithography by a microwave plasma-enhanced chemical vapor deposition (MPECVD method. The conductivities were measured repeatedly at various ranges of the drain-source voltage VDS at low temperatures which shows clearly the nonlinear behavior in electrical conductance. The electric-charging energy increases as the length and diameter of the floated carbon nanowire increases in accord with the theoretical estimation for capacitive charging as further verified from the experimentally nonlinear I-V characterization. The oscillation of the I-V curves is tacitly assumed to be embodied in the irregular variation of conductance rewarding the tremendous applications of single-electron devices for MWCNFs. The directly lateral growth of MWCNFs across electrodes allows a high contact current in spite of the existence of tunneling barriers between the wire and electrodes. The high absorption capacity of environment gases of this device is expecting it to have a pragmatic use in gas sensing.

  3. High-yield Synthesis of Multiwalled Carbon Nanotube by Mechanothermal Method

    Directory of Open Access Journals (Sweden)

    Manafi SA

    2009-01-01

    Full Text Available Abstract This study reports on the mechanothermal synthesis of multiwalled carbon nanotube (MWCNTs from elemental graphite powder. Initially, high ultra-active graphite powder can be obtained by mechanical milling under argon atmosphere. Finally, the mechanical activation product is heat-treated at 1350°C for 2–4 h under argon gas flow. After heat-treatment, active graphite powders were successfully changed into MWCNTs with high purity. The XRD analyses showed that in the duration 150 h of milling, all the raw materials were changed to the desired materials. From the broadening of the diffraction lines in the XRD patterns, it was concluded that the graphite crystallites were nanosized, and raising the milling duration resulted in the fineness of the particles and the increase of the strain. The structure and morphology of MWCNTs were investigated using scanning electron microscopy (SEM and high-resolution transmission electron microscopy (HRTEM. The yield of MWCNTs was estimated through SEM and TEM observations of the as-prepared samples was to be about 90%. Indeed, mechanothermal method is of interest for fundamental understanding and improvement of commercial synthesis of carbon nanotubes (CNTs. As a matter of fact, the method of mechanothermal guarantees the production of MWCNTs suitable for different applications.

  4. Enhancement of thermal stability of multiwalled carbon nanotubes via different silanization routes

    International Nuclear Information System (INIS)

    Scheibe, B.; Borowiak-Palen, E.; Kalenczuk, R.J.

    2010-01-01

    This work presents an effect of two different silanization procedures on thermal and structural properties of oxidized and oxidized followed by sodium borohydrate (NaBH 4 ) reduction of multiwalled carbon nanotubes (MWCNTs). Purified sample was oxidized in a mixture of nitric and sulfuric acids in a reflux. An oxidized material was divided into two batches. The first batch underwent a silanization procedure directly, while the second batch was reduced by NaBH 4 treatment prior to the silanization. The silanization experiments were performed: (A) with γ-aminopropyltriethoxysilane (APTES) at room temperature in acetone (pH ∼7) and (B) with condensated γ-aminopropyltriethoxysilane at 40 o C in water (pH 4). The extent of the functionalization of the samples after each procedure was examined by Raman spectroscopy. The vibrational properties of the materials were studied via Fourier transform infrared spectroscopy. Boehms titration technique was applied to quantify the amount of the functional groups on MWCNTs. The morphology of the pristine and functionalized carbon nanotubes was exposed to high-resolution transmission electron microscopy analysis. The energy dispersive X-ray (EDX) analysis was used to characterize the elemental composition of each sample. The effect of the silanization process on the thermal properties of MWCNTs was investigated by thermogravimetry analysis. Interestingly, the significant increase of the thermal stability of silanized MWCNTs samples in respect to the pristine MWCNTs was observed.

  5. Electrochemistry of metoclopramide at multi-walled carbon nanotube modified electrode and its voltammetric detection.

    Science.gov (United States)

    Guo, Wei; Geng, Mingjiang; Zhou, Lingyun

    2012-01-01

    A simple, sensitive and inexpensive electrochemical method was developed for the determination of metoclopramide (MCP) with a multi-wall carbon nanotube (MWNT) modified glassy carbon electrode (GCE). MWNT was dispersed into polyacrylic acid (PAA); the aqueous suspension was then cast on GCE electrodes, forming MWNT-PAA films after evaporation of the solvent. The electrochemical behavior of MCP at the MWNT-modified electrode was investigated in detail. Compared with the bare GCE, the MWNT-modified electrode exhibits electrocatalytic activity to the oxidation of MCP because of the significant oxidation peak-current enhancement. Furthermore, various experimental parameters, such as the solution pH value, the amount of MWNT-PAA suspension and accumulation conditions were optimized for the determination of MCP. Based on the electrocatalytic effect of the MWNT-modified electrode, linear sweep voltammetry (LSV) was developed for the determination of MCP with the linear response in the range from 1.0 × 10(-7) to 1.0 × 10(-5) mol L(-1) and a detection limit of 5.0 × 10(-8) mol L(-1). The method has been successfully applied to the determination of MCP in commercial MCP tablets.

  6. Chronocoulometry of wine on multi-walled carbon nanotube modified electrode: Antioxidant capacity assay.

    Science.gov (United States)

    Ziyatdinova, Guzel; Kozlova, Ekaterina; Budnikov, Herman

    2016-04-01

    Phenolic antioxidants of wine were electrochemically oxidized on multi-walled carbon nanotubes modified glassy carbon electrode (MWNT/GCE) in phosphate buffer solution. Three oxidation peaks were observed at 0.39, 0.61 and 0.83V for red dry wine and 0.39, 0.80 and 1.18 V for white dry wine, respectively, using differential pulse voltammetry at pH 4.0. The oxidation potentials for individual phenolic antioxidants confirmed the integral nature of the analytical signals for the wines examined. A one-step chronocoulometric method at 0.83 and 1.18 V for red and white wines, respectively, has been developed for the evaluation of wine antioxidant capacity (AOC). The AOC is expressed in gallic acid equivalents per 1L of wine. The AOC of white wine was significantly less than red wine (386 ± 112 vs. 1224 ± 184, pwine and total antioxidant capacity, based on coulometric titration with electrogenerated bromine (r=0.8957 at n=5 and r=0.8986 at n=4 for red and white wines, respectively). Copyright © 2015 Elsevier Ltd. All rights reserved.

  7. Highly Stable and Flexible Pressure Sensors with Modified Multi-Walled Carbon Nanotube/Polymer Composites for Human Monitoring.

    Science.gov (United States)

    He, Yin; Ming, Yue; Li, Wei; Li, Yafang; Wu, Maoqi; Song, Jinzhong; Li, Xiaojiu; Liu, Hao

    2018-04-26

    A facile method for preparing an easy processing, repeatable and flexible pressure sensor was presented via the synthesis of modified multi-walled carbon nanotubes (m-MWNTs) and polyurethane (PU) films. The surface modification of multi-walled carbon nanotubes (MWNTs) simultaneously used a silane coupling agent (KH550) and sodium dodecyl benzene sulfonate (SDBS) to improve the dispersibility and compatibility of the MWNTs in a polymer matrix. The electrical property and piezoresistive behavior of the m-MWNT/PU composites were compared with raw multi-walled carbon nanotube (raw MWNT)/PU composites. Under linear uniaxial pressure, the m-MWNT/PU composite exhibited 4.282%kPa −1 sensitivity within the pressure of 1 kPa. The nonlinear error, hysteresis error and repeatability error of the piezoresistivity of m-MWNT/PU decreased 9%, 16.72% and 54.95% relative to raw MWNT/PU respectively. Therefore, the piezoresistive response of m-MWNT/PU had better stability than that of raw MWNT/PU composites. The m-MWNT/PU sensors could be utilized in wearable devices for body movement detection, monitoring of respiration and pressure detection in garments.

  8. Effect of Different Catalyst Deposition Technique on Aligned Multiwalled Carbon Nanotubes Grown by Thermal Chemical Vapor Deposition

    Directory of Open Access Journals (Sweden)

    Mohamed Shuaib Mohamed Saheed

    2014-01-01

    Full Text Available The paper reported the investigation of the substrate preparation technique involving deposition of iron catalyst by electron beam evaporation and ferrocene vaporization in order to produce vertically aligned multiwalled carbon nanotubes array needed for fabrication of tailored devices. Prior to the growth at 700°C in ethylene, silicon dioxide coated silicon substrate was prepared by depositing alumina followed by iron using two different methods as described earlier. Characterization analysis revealed that aligned multiwalled carbon nanotubes array of 107.9 µm thickness grown by thermal chemical vapor deposition technique can only be achieved for the sample with iron deposited using ferrocene vaporization. The thick layer of partially oxidized iron film can prevent the deactivation of catalyst and thus is able to sustain the growth. It also increases the rate of permeation of the hydrocarbon gas into the catalyst particles and prevents agglomeration at the growth temperature. Combination of alumina-iron layer provides an efficient growth of high density multiwalled carbon nanotubes array with the steady growth rate of 3.6 µm per minute for the first 12 minutes and dropped by half after 40 minutes. Thicker and uniform iron catalyst film obtained from ferrocene vaporization is attributed to the multidirectional deposition of particles in the gaseous form.

  9. Effect of wrinkles on electrochemical performance of multiwalled carbon nanotubes as anode material for Li ion battery

    International Nuclear Information System (INIS)

    Sahoo, Madhumita; Ramaprabhu, S.

    2015-01-01

    Highlights: • Wrinkly surfaced gC is employed as anode material for Li ion battery. • Temperature controlled protrusions were uniformly distributed over the nanotubes. • gC shows superior performance of 373 mAh g −1 at 100 mA g −1 after 150 cycle. • Synergistic effect of defects and conductivity gives higher Li storage over MWNTs. - Abstract: A 1-D monohybrid of multiwalled carbon nanotubes and graphene sheets, graphene wrapped multiwalled carbon nanotubes (gC) structure, synthesized in a template-free simple chemical vapor deposition technique without any chemical functionalization, was employed as efficient anode material for Li ion battery. Graphene nanosheets affixed to the multiwalled carbon nanotubes (MWNTs) surface by van der Waal's attraction gives a wrinkled surface to the final 1-D gC configuration. The protrusions on the surface of the tube enhances the porosity of the system and also acts as defects, enhancing lithium adsorption sites while the inner MWNT core gives high electrical conductivity, resulting enhanced electrochemical performance of 373 mAh g −1 at 100 mA g −1 current density after 150 cycles.

  10. Glassy carbon electrode modified with multi-walled carbon nanotubes sensor for the quantification of antihistamine drug pheniramine in solubilized systems

    Directory of Open Access Journals (Sweden)

    Rajeev Jain

    2012-02-01

    Full Text Available A sensitive electroanalytical method for quantification of pheniramine in pharmaceutical formulation has been investigated on the basis of the enhanced electrochemical response at glassy carbon electrode modified with multi-walled carbon nanotubes in the presence of sodium lauryl sulfate. The experimental results suggest that the pheniramine in anionic surfactant solution exhibits electrocatalytic effect resulting in a marked enhancement of the peak current response. Peak current response is linearly dependent on the concentration of pheniramine in the range 200–1500 μg/mL with correlation coefficient 0.9987. The limit of detection is 58.31 μg/mL. The modified electrode shows good sensitivity and repeatability. Keywords: Pheniramine, Sodium lauryl sulfate (SLS, Glassy carbon electrode modified with multi-walled carbon nanotubes (GCE-MWCNTs, Solubilized systems, Voltammetric quantification

  11. Parametric study on vapor-solid-solid growth mechanism of multiwalled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Shukrullah, S., E-mail: zshukrullah@gmail.com [Center of Innovative Nanostructures and Nanodevices, Universiti Teknologi PETRONAS, 32610, Bandar Seri Iskandar, Perak (Malaysia); Mohamed, N.M. [Center of Innovative Nanostructures and Nanodevices, Universiti Teknologi PETRONAS, 32610, Bandar Seri Iskandar, Perak (Malaysia); Shaharun, M.S. [Department of Fundamental and Applied Sciences, Universiti Teknologi PETRONAS, 32610, Bandar Seri Iskandar, Perak (Malaysia); Naz, M.Y. [Department of Mechanical Engineering, Universiti Teknologi PETRONAS, 32610, Bandar Seri Iskandar, Perak (Malaysia)

    2016-06-15

    This study aimed at investigating the effect of the fluidized bed chemical vapor deposition (FBCVD) process parameters on growth mechanism, morphology and purity of the multiwalled carbon nanotubes (MWCNTs). Nanotubes were produced in a vertical FBCVD reactor by catalytic decomposition of ethylene over Al{sub 2}O{sub 3} supported nano-iron catalyst buds at different flow rates. FESEM, TEM, Raman spectroscopy and TGA thermograms were used to elaborate the growth parameters of the as grown MWCNTs. As the growth process was driven by the process temperatures well below the iron-carbon eutectic temperature (1147 °C), the appearance of graphite platelets from the crystallographic faces of the catalyst particles suggested a solid form of the catalyst during CNT nucleation. A vapor-solid-solid (VSS) growth mechanism was predicted for nucleation of MWCNTs with very low activation energy. The nanotubes grown at optimized temperature and ethylene flow rate posed high graphitic symmetry, purity, narrow diameter distribution and shorter inter-layer spacing. In Raman and TGA analyses, small I{sub D}/I{sub G} ratio and residual mass revealed negligible ratios of structural defects and amorphous carbon in the product. However, several structural defects and impurity elements were spotted in the nanotubes grown under unoptimized process parameters. - Graphical abstract: Arrhenius plot of relatively pure MWCNTs grown over Al2O3 supported nano-iron buds. - Highlights: • Vapor–solid–solid growth mechanism of MWCNTs was studied in a vertical FBCVD reactor. • MWCNTs were grown over Al2O3 supported nano-iron buds at very low activation energy. • FBCVD reactor was operated at temperatures well below the iron-carbon eutectic point. • Ideally graphitized structures were obtained at a process temperature of 800 °C. • Tube diameter revealed a narrow distribution of 20–25 nm at the optimum temperature.

  12. Parametric study on vapor-solid-solid growth mechanism of multiwalled carbon nanotubes

    International Nuclear Information System (INIS)

    Shukrullah, S.; Mohamed, N.M.; Shaharun, M.S.; Naz, M.Y.

    2016-01-01

    This study aimed at investigating the effect of the fluidized bed chemical vapor deposition (FBCVD) process parameters on growth mechanism, morphology and purity of the multiwalled carbon nanotubes (MWCNTs). Nanotubes were produced in a vertical FBCVD reactor by catalytic decomposition of ethylene over Al_2O_3 supported nano-iron catalyst buds at different flow rates. FESEM, TEM, Raman spectroscopy and TGA thermograms were used to elaborate the growth parameters of the as grown MWCNTs. As the growth process was driven by the process temperatures well below the iron-carbon eutectic temperature (1147 °C), the appearance of graphite platelets from the crystallographic faces of the catalyst particles suggested a solid form of the catalyst during CNT nucleation. A vapor-solid-solid (VSS) growth mechanism was predicted for nucleation of MWCNTs with very low activation energy. The nanotubes grown at optimized temperature and ethylene flow rate posed high graphitic symmetry, purity, narrow diameter distribution and shorter inter-layer spacing. In Raman and TGA analyses, small I_D/I_G ratio and residual mass revealed negligible ratios of structural defects and amorphous carbon in the product. However, several structural defects and impurity elements were spotted in the nanotubes grown under unoptimized process parameters. - Graphical abstract: Arrhenius plot of relatively pure MWCNTs grown over Al2O3 supported nano-iron buds. - Highlights: • Vapor–solid–solid growth mechanism of MWCNTs was studied in a vertical FBCVD reactor. • MWCNTs were grown over Al2O3 supported nano-iron buds at very low activation energy. • FBCVD reactor was operated at temperatures well below the iron-carbon eutectic point. • Ideally graphitized structures were obtained at a process temperature of 800 °C. • Tube diameter revealed a narrow distribution of 20–25 nm at the optimum temperature.

  13. Compressed multiwall carbon nanotube composite electrodes provide enhanced electroanalytical performance for determination of serotonin

    International Nuclear Information System (INIS)

    Fagan-Murphy, Aidan; Patel, Bhavik Anil

    2014-01-01

    Serotonin (5-HT) is an important neurochemical that is present in high concentrations within the intestinal tract. Carbon fibre and boron-doped diamond based electrodes have been widely used to date for monitoring 5-HT, however these electrodes are prone to fouling and are difficult to fabricate in certain sizes and geometries. Carbon nanotubes have shown potential as a suitable material for electroanalytical monitoring of 5-HT but can be difficult to manipulate into a suitable form. The fabrication of composite electrodes is an approach that can shape conductive materials into practical electrode geometries suitable for biological environments. This work investigated how compression of multiwall carbon nanotubes (MWCNTs) epoxy composite electrodes can influence their electroanalytical performance. Highly compressed composite electrodes displayed significant improvements in their electrochemical properties along with decreased internal and charge transfer resistance, reproducible behaviour and improved batch to batch variability when compared to non-compressed composite electrodes. Compression of MWCNT epoxy composite electrodes resulted in an increased current response for potassium ferricyanide, ruthenium hexaammine and dopamine, by preferentially removing the epoxy during compression and increasing the electrochemical active surface of the final electrode. For the detection of serotonin, compressed electrodes have a lower limit of detection and improved sensitivity compared to non-compressed electrodes. Fouling studies were carried out in 10 μM serotonin where the MWCNT compressed electrodes were shown to be less prone to fouling than non-compressed electrodes. This work indicates that the compression of MWCNT carbon-epoxy can result in a highly conductive material that can be moulded to various geometries, thus providing scope for electroanalytical measurements and the production of a wide range of analytical devices for a variety of systems

  14. A novel flexible nanogenerator made of ZnO nanoparticles and multiwall carbon nanotube

    Science.gov (United States)

    Sun, Hui; Tian, He; Yang, Yi; Xie, Dan; Zhang, Yu-Chi; Liu, Xuan; Ma, Shuo; Zhao, Hai-Ming; Ren, Tian-Ling

    2013-06-01

    In this paper, a novel flexible nanogenerator (FNG) made of zinc-oxide (ZnO) nanoparticles (NPs) and multiwall-carbon nanotubes (MW-CNTs) is presented. In this structure, ZnO NPs and MW-CNTs are mixed with polydimethylsiloxane (PDMS) uniformly to form an entire flexible nanogenerator. Serial tests illustrate that the output voltage and power density are as high as 7.5 V and 18.75 μW per cycle, respectively. Furthermore, by foot stamp on the FNG, a peak voltage as high as 30 V can be generated. Comparing to the control samples, it is also proved that adding MW-CNTs into the matrix could significantly enhance the output voltage from 0.8 to 7.5 V. In summary, our work indicates that the realization of flexible nanogenerators made of ZnO NPs and MW-CNTs is technologically feasible, which may bring out some important and interesting applications in energy harvesting.In this paper, a novel flexible nanogenerator (FNG) made of zinc-oxide (ZnO) nanoparticles (NPs) and multiwall-carbon nanotubes (MW-CNTs) is presented. In this structure, ZnO NPs and MW-CNTs are mixed with polydimethylsiloxane (PDMS) uniformly to form an entire flexible nanogenerator. Serial tests illustrate that the output voltage and power density are as high as 7.5 V and 18.75 μW per cycle, respectively. Furthermore, by foot stamp on the FNG, a peak voltage as high as 30 V can be generated. Comparing to the control samples, it is also proved that adding MW-CNTs into the matrix could significantly enhance the output voltage from 0.8 to 7.5 V. In summary, our work indicates that the realization of flexible nanogenerators made of ZnO NPs and MW-CNTs is technologically feasible, which may bring out some important and interesting applications in energy harvesting. Electronic supplementary information (ESI) available. See DOI: 10.1039/c3nr00866e

  15. Electrooxidation of Indomethacin at Multiwalled Carbon Nanotubes-Modified GCE and Its Determination in Pharmaceutical Dosage Form and Human Biological Fluids

    OpenAIRE

    Sataraddi, Sanjeevaraddi R.; Patil, Shreekant M.; Bagoji, Atmanand M.; Pattar, Vijay P.; Nandibewoor, Sharanappa T.

    2014-01-01

    A simple, rapid, selective, and sensitive electrochemical method for the direct determination of indomethacin was developed. The electrochemical behavior of indomethacin was carried at multiwalled carbon nanotube- (MWCNTs-) modified glassy carbon electrode (GCE). The cyclic voltammetric results indicated that MWCNT-modified glassy carbon electrode remarkably enhanced electrocatalytic activity towards the oxidation of indomethacin in slightly acidic solutions. It led to a considerable improvem...

  16. Hydrogen peroxide sensor based on modified vitreous carbon with multiwall carbon nanotubes and composites of Pt nanoparticles-dopamine

    Energy Technology Data Exchange (ETDEWEB)

    Guzman, C.; Orozco, G. [Electrochemistry Department, Centro de Investigacion y Desarrollo Tecnologico en Electroquimica S.C., P.O. Box 064, C.P. 76700, Pedro Escobedo, Queretaro (Mexico); Verde, Y. [Instituto Tecnologico de Cancun, Av. Kabah Km. 3, C.P. 77500, Cancun, Quintana Roo (Mexico); Jimenez, S. [Unidad Queretaro Centro de Investigacion y de Estudios Avanzados del I.P.N., Juriquilla, Santiago de Queretaro (Mexico); Godinez, Luis A. [Electrochemistry Department, Centro de Investigacion y Desarrollo Tecnologico en Electroquimica S.C., P.O. Box 064, C.P. 76700, Pedro Escobedo, Queretaro (Mexico); Juaristi, E. [Chemistry Department, Centro de Investigacion y de Estudios Avanzados del I.P.N., P.O. Box 14-740, C.P. 07360 Mexico, D.F. (Mexico); Bustos, E. [Electrochemistry Department, Centro de Investigacion y Desarrollo Tecnologico en Electroquimica S.C., P.O. Box 064, C.P. 76700, Pedro Escobedo, Queretaro (Mexico); Chemistry Department, Centro de Investigacion y de Estudios Avanzados del I.P.N., P.O. Box 14-740, C.P. 07360 Mexico, D.F. (Mexico)], E-mail: ebustos@cideteq.mx

    2009-02-15

    Sensors using nanostructured materials have been under development in the last decade due to their selectivity for the detection and quantification of different compounds. The physical and chemical characteristics of carbon nanotubes provide significant advantages when used as electrodes for electronic devices, fuel cells and electrochemical sensors. This paper presents preliminary results on the modification of vitreous carbon electrodes with Multiwall Carbon Nanotubes (MWCNTs) and composites of Pt nanoparticles-dopamine (DA) as electro-catalytic materials for the hydrogen peroxide (H{sub 2}O{sub 2}) reaction. Chemical pre-treatment and consequent functionalization of MWCNTs with carboxylic groups was necessary to increase the distribution of the composites. In addition, the presence of DA was important to protect the active sites and eliminate the pasivation of the surface after the electro-oxidation of H{sub 2}O{sub 2} takes place. The proposed H{sub 2}O{sub 2} sensor exhibited a linear response in the 0-5 mM range, with detection and quantification limits of 0.3441 mM and 1.1472 mM, respectively.

  17. Hydrogen peroxide sensor based on modified vitreous carbon with multiwall carbon nanotubes and composites of Pt nanoparticles-dopamine

    International Nuclear Information System (INIS)

    Guzman, C.; Orozco, G.; Verde, Y.; Jimenez, S.; Godinez, Luis A.; Juaristi, E.; Bustos, E.

    2009-01-01

    Sensors using nanostructured materials have been under development in the last decade due to their selectivity for the detection and quantification of different compounds. The physical and chemical characteristics of carbon nanotubes provide significant advantages when used as electrodes for electronic devices, fuel cells and electrochemical sensors. This paper presents preliminary results on the modification of vitreous carbon electrodes with Multiwall Carbon Nanotubes (MWCNTs) and composites of Pt nanoparticles-dopamine (DA) as electro-catalytic materials for the hydrogen peroxide (H 2 O 2 ) reaction. Chemical pre-treatment and consequent functionalization of MWCNTs with carboxylic groups was necessary to increase the distribution of the composites. In addition, the presence of DA was important to protect the active sites and eliminate the pasivation of the surface after the electro-oxidation of H 2 O 2 takes place. The proposed H 2 O 2 sensor exhibited a linear response in the 0-5 mM range, with detection and quantification limits of 0.3441 mM and 1.1472 mM, respectively

  18. Nanofluids with plasma treated diamond nanoparticles

    International Nuclear Information System (INIS)

    Yu Qingsong; Kim, Young Jo; Ma Hongbin

    2008-01-01

    In this study, diamond nanoparticles were plasma treated by glow discharges of methane and oxygen with an aim of improving their dispersion characteristics in a base fluid of water and enhancing the thermal conductivity of the resulting nanofluids. It was found that, after plasma treatment, stable nanofluids with improved thermal conductivity were obtained without using any stabilizing agents. With <0.15 vol % addition of plasma treated nanoparticles into water, a 20% increase in thermal conductivity was achieved and a 5%-10% increase in both fluid density and viscosity was observed

  19. Aspect ratio has no effect on genotoxicity of multi-wall carbon nanotubes.

    Science.gov (United States)

    Kim, Jin Sik; Lee, Kyu; Lee, Young Hee; Cho, Hyun Sun; Kim, Ki Heon; Choi, Kyung Hee; Lee, Sang Hee; Song, Kyung Seuk; Kang, Chang Soo; Yu, Il Je

    2011-07-01

    Carbon nanotubes (CNTs) have specific physico-chemical and electrical properties that are useful for telecommunications, medicine, materials, manufacturing processes and the environmental and energy sectors. Yet, despite their many advantages, it is also important to determine whether CNTs may represent a hazard to the environment and human health. Like asbestos, the aspect ratio (length:diameter) and metal components of CNTs are known to have an effect on the toxicity of carbon nanotubes. Thus, to evaluate the toxic potential of CNTs in relation to their aspect ratio and metal contamination, in vivo and in vitro genotoxicity tests were conducted using high-aspect-ratio (diameter: 10-15 nm, length: ~10 μm) and low-aspect-ratio multi-wall carbon nanotubes (MWCNTs, diameter: 10-15 nm, length: ~150 nm) according to OECD test guidelines 471 (bacterial reverse mutation test), 473 (in vitro chromosome aberration test), and 474 (in vivo micronuclei test) with a good laboratory practice system. To determine the treatment concentration for all the tests, a solubility and dispersive test was performed, and a 1,2-dipalmitoyl-sn-glycero-3-phosphocholine (DPPC) solution found to be more suitable than distilled water. Neither the high- nor the low-aspect-ratio MWCNTs induced any genotoxicity in a bacterial reverse mutation test (~1,000 μg/plate), in vitro chromosome aberration test (without S9: ~6.25 μg/ml, with S9: ~50 μg/ml), or in vivo micronuclei test (~50 mg/kg). However, the high-aspect-ratio MWCNTs were found to be more toxic than the low-aspect-ratio MWCNTs. Thus, while high-aspect-ratio MWCNTs do not induce direct genotoxicity or metabolic activation-mediated genotoxicity, genotoxicity could still be induced indirectly through oxidative stress or inflammation.

  20. A comparative study of enzyme immobilization strategies for multi-walled carbon nanotube glucose biosensors

    Energy Technology Data Exchange (ETDEWEB)

    Shi, Jin; Jaroch, David; Rickus, Jenna L; Marshall Porterfield, D [Weldon School of Biomedical Engineering, Purdue University (United States); Claussen, Jonathan C; Ul Haque, Aeraj; Diggs, Alfred R [Physiological Sensing Facility, Bindley Bioscience Center and Birck Nanotechnology Center, Purdue University (United States); McLamore, Eric S [Department of Agricultural and Biological Engineering, University of Florida (United States); Calvo-Marzal, Percy, E-mail: porterf@purdue.edu [Department of Chemistry, Purdue University (United States)

    2011-09-02

    This work addresses the comparison of different strategies for improving biosensor performance using nanomaterials. Glucose biosensors based on commonly applied enzyme immobilization approaches, including sol-gel encapsulation approaches and glutaraldehyde cross-linking strategies, were studied in the presence and absence of multi-walled carbon nanotubes (MWNTs). Although direct comparison of design parameters such as linear range and sensitivity is intuitive, this comparison alone is not an accurate indicator of biosensor efficacy, due to the wide range of electrodes and nanomaterials available for use in current biosensor designs. We proposed a comparative protocol which considers both the active area available for transduction following nanomaterial deposition and the sensitivity. Based on the protocol, when no nanomaterials were involved, TEOS/GOx biosensors exhibited the highest efficacy, followed by BSA/GA/GOx and TMOS/GOx biosensors. A novel biosensor containing carboxylated MWNTs modified with glucose oxidase and an overlying TMOS layer demonstrated optimum efficacy in terms of enhanced current density (18.3 {+-} 0.5 {mu}A mM{sup -1} cm{sup -2}), linear range (0.0037-12 mM), detection limit (3.7 {mu}M), coefficient of variation (2%), response time (less than 8 s), and stability/selectivity/reproducibility. H{sub 2}O{sub 2} response tests demonstrated that the most possible reason for the performance enhancement was an increased enzyme loading. This design is an excellent platform for versatile biosensing applications.

  1. Biosynthesis of Bacterial Cellulose/Carboxylic Multi-Walled Carbon Nanotubes for Enzymatic Biofuel Cell Application

    Directory of Open Access Journals (Sweden)

    Pengfei Lv

    2016-03-01

    Full Text Available Novel nanocomposites comprised of bacterial cellulose (BC with carboxylic multi-walled carbon nanotubes (c-MWCNTs incorporated into the BC matrix were prepared through a simple method of biosynthesis. The biocathode and bioanode for the enzyme biological fuel cell (EBFC were prepared using BC/c-MWCNTs composite injected by laccase (Lac and glucose oxidase (GOD with the aid of glutaraldehyde (GA crosslinking. Biosynthesis of BC/c-MWCNTs composite was characterized by digital photos, scanning electron microscope (SEM, and Fourier Transform Infrared (FTIR. The experimental results indicated the successful incorporation of c-MWCNTs into the BC. The electrochemical and biofuel performance were evaluated by cyclic voltammetry (CV and linear sweep voltammetry (LSV. The power density and current density of EBFCs were recorded at 32.98 µW/cm3 and 0.29 mA/cm3, respectively. Additionally, the EBFCs also showed acceptable stability. Preliminary tests on double cells indicated that renewable BC have great potential in the application field of EBFCs.

  2. Hydrogen storage behaviors of platinum-supported multi-walled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Park, Soo-Jin; Lee, Seul-Yi [Department of Chemistry, Inha University, 253 Nam-gu, Incheon 402-751 (Korea, Republic of)

    2010-12-15

    In this work, the hydrogen storage behaviors of multi-walled carbon nanotubes (MWNTs) loaded by crystalline platinum (Pt) particles were studied. The microstructure of the Pt/MWNTs was characterized by X-ray diffraction and transmission electron microscopy. The pore structure and total pore volumes of the Pt/MWNTs were analyzed by N{sub 2}/77 K adsorption isotherms. The hydrogen storage capacity of the Pt/MWNTs was evaluated at 298 K and 100 bar. From the experimental results, it was found that Pt particles were homogeneously distributed on the MWNT surfaces. The amount of hydrogen storage capacity increased in proportion to the Pt content, with Pt-5/MWNTs exhibiting the largest hydrogen storage capacity. The superior amount of hydrogen storage was linked to an increase in the number of active sites and the optimum-controlled micropore volume for hydrogen adsorption due to the well-dispersed Pt particles. Therefore, it can be concluded that Pt particles play an important role in hydrogen storage characteristics due to the hydrogen spillover effect. (author)

  3. 3D printing of highly elastic strain sensors using polyurethane/multiwall carbon nanotube composites

    Science.gov (United States)

    Christ, Josef F.; Hohimer, Cameron J.; Aliheidari, Nahal; Ameli, Amir; Mo, Changki; Pötschke, Petra

    2017-04-01

    As the desire for wearable electronics increases and the soft robotics industry advances, the need for novel sensing materials has also increased. Recently, there have been many attempts at producing novel materials, which exhibit piezoresistive behavior. However, one of the major shortcomings in strain sensing technologies is in the fabrication of such sensors. While there is significant research and literature covering the various methods for developing piezoresistive materials, fabricating complex sensor platforms is still a manufacturing challenge. Here, we report a facile method to fabricate multidirectional embedded strain sensors using additive manufacturing technology. Pure thermoplastic polyurethane (TPU) and TPU/multiwall carbon nanotubes (MWCNT) nanocomposites were 3D printed in tandem using a low-cost multi-material FDM printer to fabricate uniaxial and biaxial strain sensors with conductive paths embedded within the insulative TPU platform. The sensors were then subjected to a series of cyclic strain loads. The results revealed excellent piezoresistive responses of the sensors with cyclic repeatability in both the axial and transverse directions and in response to strains as high as 50%. Further, while strain-softening did occur in the embedded printed strain sensors, it was predictable and similar to the results found in the literature for bulk polymer nanocomposites. This works demonstrates the possibility of manufacturing embedded and multidirectional flexible strain sensors using an inexpensive and versatile method, with potential applications in soft robotics and flexible electronics and health monitoring.

  4. Electrodeposition in the Ni-plating bath containing multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    An Baigang; Li Lixiang; Li Hongxi

    2008-01-01

    An electrodeposition procedure is performed in the Ni-plating bath containing multi-walled carbon nanotubes (MWNTs). The effects of MWNTs on the electrodeposits and process of Ni deposition are investigated by scanning electron microscopy, X-ray diffraction and electrochemical methods. The results show that there is an optimum concentration of MWNTs, at which the surface of the cathode can be uniformly and completely covered by MWNTs and thus Ni can be uniformly deposited on the MWNTs to form the MWNTs coated with a uniform Ni layer. The introduction of MWNTs in the Ni-plating bath increases the cathodic polarization of Ni deposition due to the two aspects as follows: The addition of MWNTs enhances the charge transfer for the reduction of Ni and also supplies a large active surface area for a great deal of nucleation of Ni, consequently results in an increase of concentration polarization. The deposition of Ni on the MWNTs requires the higher activation energy than that on the Cu. The MWNTs adsorbed on the cathode also induce Ni to deposit as smaller grains due to a large increase of nucleation sites of Ni. Therefore, more uniform and compact coating in appearance than Ni coating formed in the plating bath without MWNTs can be obtained

  5. Strain-dependent electrical resistance of multi-walled carbon nanotube/polymer composite films

    International Nuclear Information System (INIS)

    Park, Myounggu; Kim, Hyonny; Youngblood, Jeffrey P

    2008-01-01

    The strain-dependent electrical resistance characteristics of multi-walled carbon nanotube (MWCNT)/polymer composite films were investigated. In this research, polyethylene oxide (PEO) is used as the polymer matrix. Two representative volume fractions of MWCNT/PEO composite films were selected: 0.56 vol% (near the percolation threshold) and 1.44 vol% (away from the percolation threshold) of MWCNT. An experimental setup which can measure electrical resistance and strain simultaneously and continuously has been developed. Unique and repeatable relationships in resistance versus strain were obtained for multiple specimens with different volume fractions of MWCNT. The overall pattern of electrical resistance change versus strain for the specimens tested consists of linear and nonlinear regions. A resistance change model to describe the combination of linear and nonlinear modes of electrical resistance change as a function of strain is suggested. The unique characteristics in electrical resistance change for different volume fractions imply that MWCNT/PEO composite films can be used as tunable strain sensors and for application into embedded sensor systems in structures

  6. Incorporation of multiwalled carbon nanotubes to acrylic based bone cements: effects on mechanical and thermal properties.

    Science.gov (United States)

    Ormsby, Ross; McNally, Tony; Mitchell, Christina; Dunne, Nicholas

    2010-02-01

    Polymethyl methacrylate (PMMA) bone cement-multiwalled carbon nanotube (MWCNT) nanocomposites with a weight loading of 0.1% were prepared using 3 different methods of MWCNT incorporation. The mechanical and thermal properties of the resultant nanocomposite cements were characterised in accordance with the international standard for acrylic resin cements. The mechanical properties of the resultant nanocomposite cements were influenced by the type of MWCNT and method of incorporation used. The exothermic polymerisation reaction for the PMMA bone cement was significantly reduced when thermally conductive functionalised MWCNTs were added. This reduction in exotherm translated in a decrease in thermal necrosis index value of the respective nanocomposite cements, which potentially could reduce the hyperthermia experienced in vivo. The morphology and degree of dispersion of the MWCNTs in the PMMA matrix at different scales were analysed using scanning electron microscopy. Improvements in mechanical properties were attributed to the MWCNTs arresting/retarding crack propagation through the cement by providing a bridging effect into the wake of the crack, normal to the direction of crack growth. MWCNT agglomerations were evident within the cement microstructure, the degree of these agglomerations was dependent on the method used to incorporate the MWCNTs into the cement. Copyright 2009. Published by Elsevier Ltd.

  7. Poly(3-hexylthiophene)/multiwalled carbon hybrid coaxial nanotubes: nanoscale rectification and photovoltaic characteristics.

    Science.gov (United States)

    Kim, Kihyun; Shin, Ji Won; Lee, Yong Baek; Cho, Mi Yeon; Lee, Suk Ho; Park, Dong Hyuk; Jang, Dong Kyu; Lee, Cheol Jin; Joo, Jinsoo

    2010-07-27

    We fabricate hybrid coaxial nanotubes (NTs) of multiwalled carbon nanotubes (MWCNTs) coated with light-emitting poly(3-hexylthiophene) (P3HT). The p-type P3HT material with a thickness of approximately 20 nm is electrochemically deposited onto the surface of the MWCNT. The formation of hybrid coaxial NTs of the P3HT/MWCNT is confirmed by a transmission electron microscope, FT-IR, and Raman spectra. The optical and structural properties of the hybrid NTs are characterized using ultraviolet and visible absorption, Raman, and photoluminescence (PL) spectra where, it is shown that the PL intensity of the P3HT materials decreases after the hybridization with the MWCNTs. The current-voltage (I-V) characteristics of the outer P3HT single NT show the semiconducting behavior, while ohmic behavior is observed for the inner single MWCNT. The I-V characteristics of the hybrid junction between the outer P3HT NT and the inner MWCNT, for the hybrid single NT, exhibit the characteristics of a diode (i.e., rectification), whose efficiency is clearly enhanced with light irradiation. The rectification effect of the hybrid single NT has been analyzed in terms of charge tunneling models. The quasi-photovoltaic effect is also observed at low bias for the P3HT/MWCNT hybrid single NT.

  8. Synthesis of ZnO coated multi-walled carbon nanotubes and their antibacterial activities

    Energy Technology Data Exchange (ETDEWEB)

    Sui, Minghao, E-mail: suiminghao.sui@gmail.com; Zhang, Lingdian, E-mail: 970864427@qq.com; Sheng, Li, E-mail: shengli1971@gmail.com; Huang, Shuhang, E-mail: hsh880813@qq.com; She, Lei, E-mail: selery1989@163.com

    2013-05-01

    ZnO coated multi-walled carbon nanotubes (ZnO/MWCNTs) were prepared and evaluated for their application potentials as an antimicrobial material for simultaneous concentrating and inactivating pathogenic bacteria. X-ray energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), and X-ray photoelectron spectra (XPS) were used to characterize the ZnO/MWCNTs. Escherichia coli (E. coli) was employed as the target bacterium. Comparing with the raw and the purified MWCNTs (r-MWCNTs and p-MWCNTs), which have been reported to possess antibacterial activity towards E. coli, ZnO/MWCNTs exhibited stronger antibacterial ability. The deposited ZnO was suggested to play an important role in the bactericidal action of ZnO/MWCNTs, while, the r-MWCNTs and p-MWCNTs served as more like adsorbing materials for E. coli. - Highlights: ► ZnO/MWCNTs were prepared and characterized. ► ZnO/MWCNTs were evaluated for the application potential as disinfection material. ► ZnO/MWCNTs exhibited strong antibacterial ability towards E. coli. ► ZnO seems to play an important role in the bactericidal action of ZnO/MWCNTs. ► MWCNTs served as more like adsorbing materials for E. coli.

  9. Flexible and Transparent Strain Sensors with Embedded Multiwalled Carbon Nanotubes Meshes.

    Science.gov (United States)

    Nie, Bangbang; Li, Xiangming; Shao, Jinyou; Li, Xin; Tian, Hongmiao; Wang, Duorui; Zhang, Qiang; Lu, Bingheng

    2017-11-22

    Strain sensors combining high sensitivity with good transparency and flexibility would be of great usefulness in smart wearable/flexible electronics. However, the fabrication of such strain sensors is still challenging. In this study, new strain sensors with embedded multiwalled carbon nanotubes (MWCNTs) meshes in polydimethylsiloxane (PDMS) films were designed and tested. The strain sensors showed elevated optical transparency of up to 87% and high sensitivity with a gauge factor of 1140 at a small strain of 8.75%. The gauge factors of the sensors were also found relatively stable since they did not obviously change after 2000 stretching/releasing cycles. The sensors were tested to detect motion in the human body, such as wrist bending, eye blinking, mouth phonation, and pulse, and the results were shown to be satisfactory. Furthermore, the fabrication of the strain sensor consisting of mechanically blading MWCNTs aqueous dispersions into microtrenches of prestructured PDMS films was straightforward, was low cost, and resulted in high yield. All these features testify to the great potential of these sensors in future real applications.

  10. Adsorption of diuron and dichlobenil on multiwalled carbon nanotubes as affected by lead.

    Science.gov (United States)

    Chen, Guang-Cai; Shan, Xiao-Quan; Pei, Zhi-Guo; Wang, Huanhua; Zheng, Li-Rong; Zhang, Jing; Xie, Ya-Ning

    2011-04-15

    The effect of lead on the adsorption of diuron and dichlobenil on multiwalled carbon nanotubes (MWCNTs) was investigated to explore the possible application of MWCNTs for removal of both herbicides from contaminated water. The adsorption of diuron and dichlobenil on MWCNTs at pH 6 was nonlinear and fit the Polanyi-Manes model well. The adsorption of diuron and dichlobenil was closely correlated with specific surface areas and micropore volumes of MWCNTs. An increase in oxygen content of MWCNTs with same diameters and similar surface areas decreased the adsorption of diuron and dichlobenil, while increased the adsorption of lead. Micro-Fourier transform infrared spectroscopic study indicated that hydrogen bonding is a main mechanism responsible for the adsorption of diuron or dichlobenil onto MWCNTs-O. Oxygen containing groups, mainly carboxylic groups, significantly increased the adsorption of lead through the formations of outer-sphere and inner-sphere complexes, which are verified by X-ray absorption spectroscopic measurements. Oxygen containing groups and the presence of lead diminished the adsorption of diuron and dichlobenil. The suppression mechanisms of lead were ascribed to hydration and complexation of lead with carboxylic groups, which may occupy part of surface of MWCNTs-O. The large hydration shell of lead cations may intrude or shield hydrophobic and hydrophilic sites, resulting in a decreased adsorption of diuron and dichlobenil at the lead-complexed moieties. Copyright © 2011 Elsevier B.V. All rights reserved.

  11. The pulmonary inflammatory response to multiwalled carbon nanotubes is influenced by gender and glutathione synthesis

    Directory of Open Access Journals (Sweden)

    Megan M. Cartwright

    2016-10-01

    Full Text Available Inhalation of multiwalled carbon nanotubes (MWCNTs during their manufacture or incorporation into various commercial products may cause lung inflammation, fibrosis, and oxidative stress in exposed workers. Some workers may be more susceptible to these effects because of differences in their ability to synthesize the major antioxidant and immune system modulator glutathione (GSH. Accordingly, in this study we examined the influence of GSH synthesis and gender on MWCNT-induced lung inflammation in C57BL/6 mice. GSH synthesis was impaired through genetic manipulation of Gclm, the modifier subunit of glutamate cysteine ligase, the rate-limiting enzyme in GSH synthesis. Twenty-four hours after aspirating 25 µg of MWCNTs, all male mice developed neutrophilia in their lungs, regardless of Gclm genotype. However, female mice with moderate (Gclm heterozygous and severe (Gclm null GSH deficiencies developed significantly less neutrophilia. We found no indications of MWCNT-induced oxidative stress as reflected in the GSH content of lung tissue and epithelial lining fluid, 3-nitrotyrosine formation, or altered mRNA or protein expression of several redox-responsive enzymes. Our results indicate that GSH-deficient female mice are rendered uniquely susceptible to an attenuated neutrophil response. If the same effects occur in humans, GSH-deficient women manufacturing MWCNTs may be at greater risk for impaired neutrophil-dependent clearance of MWCNTs from the lung. In contrast, men may have effective neutrophil-dependent clearance, but may be at risk for lung neutrophilia regardless of their GSH levels.

  12. The Effect of Clay/Multiwall Carbon Nanotube Hybrid Fillers on the Properties of Elastomer Nanocomposites

    Directory of Open Access Journals (Sweden)

    Sung Ho Song

    2018-01-01

    Full Text Available The hybrid fillers of 1D multiwalled carbon nanotubes (MWNT and 2D montmorillonite (MMT have led to excellent physical and chemical properties in high performance elastomer nanocomposites. In this study, the hybridization of PDDA (polydiallyldimethylammonium chloride functionalized MWNT (P-MWNT and hydroxyl-functionalized MMT (H-MMT was prepared by the electrostatic interaction between the positive charge on the MWNT and the negative charge on the MMT using a simple solution mixing process. Also, a styrene-butadiene rubber (SBR nanocomposite containing the hybrid nanofillers was prepared to improve the dispersion of nanofillers with SBR latex. The SBR nanocomposites with the hybrid nanofillers exhibited outstanding mechanical properties including modulus, tensile strength, and elongation at break, due to the enhanced interfacial bonding with the elastomer matrix. Furthermore, the hybrid nanofillers in the SBR matrix showed superior thermal and electrical properties and gas barrier performance at low loadings. The synergistic effects of the SBR produced by the hybridized nanofillers will open up new opportunities for elastomer composites with high performance.

  13. KOH-activated multi-walled carbon nanotubes as platinum supports for oxygen reduction reaction

    Science.gov (United States)

    He, Chaoxiong; Song, Shuqin; Liu, Jinchao; Maragou, Vasiliki; Tsiakaras, Panagiotis

    In the present investigation, multi-walled carbon nanotubes (MWCNTs) thermally treated by KOH were adopted as the platinum supporting material for the oxygen reduction reaction electrocatalysts. FTIR and Raman spectra were used to investigate the surface state of MWCNTs treated by KOH at different temperatures (700, 800, and 900 °C) and showed MWCNTs can be successfully functionalized. The structural properties of KOH-activated MWCNTs supported Pt were determined by X-ray diffraction (XRD) and transmission electron microscopy (TEM), and their electrochemical performance was evaluated by the aid of cyclic voltammetry (CV) and rotating disk electrode (RDE) voltammetry. According to the experimental findings of the present work, the surrface of MWCNTs can be successfully functionalized with oxygen-containing groups after activation by KOH, favoring the good dispersion of Pt nanoparticles with narrow size distribution. The as-prepared Pt catalysts supported on KOH treated MWCNTs at higher temperature, possess higher electrochemical surface area and exhibit desirable activity towards oxygen reduction reaction (ORR). More precisely, it has been found that the electrochemical active area of Pt/MWCNTs-900 is approximately two times higher than that of Pt/MWCNTs. It can be concluded that KOH activation is an effective way to decorate MWCNTs' surface with oxygen-containing groups and bigger surface area, which makes them more suitable as electrocatalyst support materials.

  14. Hydroxyapatite growth on multiwall carbon nanotubes grown on titanium fibers from a titanium sheet

    KAUST Repository

    Chetibi, Loubna

    2013-09-27

    Nano-hydroxyapatite (HA) was grown on functionalized multiwalled carbon nanotubes (MWCNTs) deposited on TiO2 nanofibers (NFs) that were hydrothermally grown on Ti metal sheets. The HA was electrochemically grown on the MWCNTs/TiO2 porous layer. It was found that the HA grows on the MWCNTs/TiO2 NFs in the form of dense coating with nanorice grain-shaped. The incorporation of MWCNTs between HA and TiO2 NFs has led to higher adhesion strength as measured by micro-scratching test indicating the benefit of MWCNTs on the improving the bonding strength of HA layer. The obtained coatings exhibit excellent corrosion resistance in simulated body fluid. It is expected that this simple route for preparing the new HA/MWCNTs/TiO2/Ti-layered structure might be used not only in the biomedical field, but also in catalysis and biological sensing among others. © 2013 Springer Science+Business Media New York.

  15. Graphene oxide-multiwalled carbon nanotubes composite as an anode for lithium ion batteries

    Directory of Open Access Journals (Sweden)

    Majchrzycki Łukasz

    2016-09-01

    Full Text Available Nowadays reduced graphene oxide (rGO is regarded as a highly interesting material which is appropriate for possible applications in electrochemistry, especially in lithium-ion batteries (LIBs. Several methods were proposed for the preparation of rGO-based electrodes, resulting in high-capacity LIBs anodes. However, the mechanism of lithium storage in rGO and related materials is still not well understood. In this work we focused on the proposed mechanism of favorable bonding sites induced by additional functionalities attached to the graphene planes. This mechanism might increase the capacity of electrodes. In order to verify this hypothesis the composite of non-reduced graphene oxide (GO with multiwalled carbon nanotubes electrodes was fabricated. Electrochemical properties of GO composite anodes were studied in comparison with similarly prepared electrodes based on rGO. This allowed us to estimate the impact of functional groups on the reversible capacity changes. As a result, it was shown that oxygen containing functional groups of GO do not create, in noticeable way, additional active sites for the electrochemical reactions of lithium storage, contrary to what has been postulated previously.

  16. Carcinogenicity of multi-walled carbon nanotubes: challenging issue on hazard assessment.

    Science.gov (United States)

    Fukushima, Shoji; Kasai, Tatsuya; Umeda, Yumi; Ohnishi, Makoto; Sasaki, Toshiaki; Matsumoto, Michiharu

    2018-01-25

    This report reviews the carcinogenicity of multi-walled carbon nanotubes (MWCNTs) in experimental animals, concentrating on MWNT-7, a straight fibrous MWCNT. MWCNTs were administered to mice and rats by intraperitoneal injection, intrascrotal injection, subcutaneous injection, intratracheal instillation and inhalation. Intraperitoneal injection of MWNT-7 induced peritoneal mesothelioma in mice and rats. Intrascrotal injection induced peritoneal mesothelioma in rats. Intratracheal instillation of MWCNT-N (another straight fibrous MWCNT) induced both lung carcinoma and pleural mesothelioma in rats. In the whole body inhalation studies, in mice MWNT-7 promoted methylcholanthrene-initiated lung carcinogenesis. In rats, inhalation of MWNT-7 induced lung carcinoma and lung burdens of MWNT-7 increased with increasing concentration of airborne MWNT-7 and increasing duration of exposure. Straight, fibrous MWCNTs exerted carcinogenicity in experimental animals. Phagocytosis of MWCNT fibers by macrophages was very likely to be a principle factor in MWCNT lung carcinogenesis. Using no-observed-adverse-effect level-based approach, we calculated that the occupational exposure limit (OEL) of MWNT-7 for cancer protection is 0.15 μg/m 3 for a human worker. Further studies on the effects of the shape and size of MWCNT fibers and mode of action on the carcinogenicity are required.

  17. Improvement of interaction between pre-dispersed multi-walled carbon nanotubes and unsaturated polyester resin

    Energy Technology Data Exchange (ETDEWEB)

    Beg, M. D. H., E-mail: dhbeg@yahoo.com; Moshiul Alam, A. K. M., E-mail: akmmalam@gmail.com; Yunus, R. M. [Universiti Malaysia Pahang, Faculty of Chemical and Natural Resources Engineering (Malaysia); Mina, M. F. [Bangladesh University of Engineering and Technology, Department of Physics (Bangladesh)

    2015-01-15

    Efforts are being given to the development of well-dispersed nanoparticle-reinforced polymer nanocomposites in order to tailor the material properties. In this perspective, well dispersion of multi-walled carbon nanotubes (MWCNTs) in unsaturated polyester resin (UPR) was prepared using pre-dispersed MWCNTs in tetrahydrofuran solvent with ultrasonication method. Then the well-dispersed MWCNTs reinforced UPR nanocomposites were fabricated through solvent evaporation. Fourier-transform infrared spectroscopy indicates a good interaction between matrix and MWCNTs. This along with homogeneous dispersion of nanotubes in matrix has been confirmed by the field emission scanning electron microscopy. At low shear rate, the value of viscosity of UPR is 8,593 mPa s and that of pre-dispersed MWCNT–UPR suspension is 43,491 mPa s, showing implicitly a good dispersion of nanotubes. A notable improvement in the crystallinity of UPR from 14 to 21 % after MWCNTs inclusion was observed by X-ray diffractometry. The mechanical properties, such as tensile strength, tensile modulus, impact strength, and elongation-at-break, of nanocomposite were found to be increased to 22, 20, 28, and 87 %, respectively. The estimated melting enthalpy per gram for composites as analyzed by differential scanning calorimetry is higher than that of UPR. The onset temperature of thermal decomposition in the nanocomposites as monitored by thermogravimetric analysis is found higher than that of UPR. Correlations among MWCNTs dispersion, nucleation, fracture morphology, and various properties were measured and reported.

  18. Alkaline electrochemical advanced oxidation process for chromium oxidation at graphitized multi-walled carbon nanotubes.

    Science.gov (United States)

    Xue, Yudong; Zheng, Shili; Sun, Zhi; Zhang, Yi; Jin, Wei

    2017-09-01

    Alkaline electrochemical advanced oxidation processes for chromium oxidation and Cr-contaminated waste disposal were reported in this study. The highly graphitized multi-walled carbon nanotubes g-MWCNTs modified electrode was prepared for the in-situ electrochemical generation of HO 2 - . RRDE test results illustrated that g-MWCNTs exhibited much higher two-electron oxygen reduction activity than other nanocarbon materials with peak current density of 1.24 mA cm -2 , %HO 2 - of 77.0% and onset potential of -0.15 V (vs. Hg/HgO). It was originated from the highly graphitized structure and good electrical conductivity as illustrated from the Raman, XRD and EIS characterizations, respectively. Large amount of reactive oxygen species (HO 2 - and ·OH) were in-situ electro-generated from the two-electron oxygen reduction and chromium-induced alkaline electro-Fenton-like reaction. The oxidation of Cr(III) was efficiently achieved within 90 min and the conversion ratio maintained more than 95% of the original value after stability test, offering an efficient and green approach for the utilization of Cr-containing wastes. Copyright © 2017 Elsevier Ltd. All rights reserved.

  19. Improved field emission from indium decorated multi-walled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Sreekanth, M.; Ghosh, S., E-mail: santanu1@physics.iitd.ernet.in; Biswas, P.; Kumar, S.; Srivastava, P.

    2016-10-15

    Graphical abstract: Improved field emission properties have been achieved for Indium (In) decorated MWCNTs and are shown using the schematic of field emission set up with In/CNT cathode, and a plot of J-E characteristics for pristine and In decorated CNTs. - Highlights: • Field emission (FE) properties have been studied for the first time from Indium (In) decorated MWCNT films. • Observed increased density of states near the Fermi level for In decorated films. • Superior field emission properties have been achieved for In decorated CNT films. - Abstract: Multi-walled carbon nanotube (MWCNT) films were grown using thermal chemical vapor deposition (T-CVD) process and were decorated with indium metal particles by thermal evaporation technique. The In metal particles are found to get oxidized. The In decorated films show 250% enhancement in the FE current density, lower turn-on and threshold fields, and better temporal stability as compared to their undecorated counterpart. This improvement in field emission properties is primarily attributed to increased density of states near the Fermi level. The presence of O 2p states along with a small contribution from In 5s states results in the enhancement of density of states in the vicinity of the Fermi level.

  20. Effect of alignment on adsorption characteristics of self-oriented multi-walled carbon nanotube arrays

    International Nuclear Information System (INIS)

    Zilli, D; Bonelli, P R; Cukierman, A L

    2006-01-01

    The adsorption characteristics of self-oriented multi-walled carbon nanotube (MWCNT) arrays are examined from N 2 (-196 deg. C) adsorption measurements. The arrays were synthesized in a laboratory by in situ chemical vapour deposition of iron or cobalt phthalocyanines at 880 and 950 deg. C, under otherwise constant conditions, in an attempt to obtain different morphological structures. For both precursors, increasing the temperature leads to MWCNT arrays with lower Brunauer-Emmett-Teller (BET) surface area and total pore volume, though the effect is more pronounced for those arising from the iron-based compound. Despite this, precursor yields of individual nanotubes of larger diameter, higher BET area and total pore volume characterize the resulting arrays compared to those arising from cobalt phthalocyanine for the same temperatures. As evidenced by SEM and TEM images, the arrays synthesized from iron phthalocyanine at 880 deg. C show better vertical alignment and denser structures than those obtained from this compound at 950 deg. C, and also from cobalt phthalocyanine at both temperatures. Further ultrasonication of the arrays produced from the iron compound brings about a significant reduction in their adsorption capacity, attributable to the pronounced disarrangement of the resulting structures. The present results demonstrate that the alignment of MWCNT arrays plays a crucial role in their N 2 adsorption characteristics

  1. A comparative study of enzyme immobilization strategies for multi-walled carbon nanotube glucose biosensors

    International Nuclear Information System (INIS)

    Shi, Jin; Jaroch, David; Rickus, Jenna L; Marshall Porterfield, D; Claussen, Jonathan C; Ul Haque, Aeraj; Diggs, Alfred R; McLamore, Eric S; Calvo-Marzal, Percy

    2011-01-01

    This work addresses the comparison of different strategies for improving biosensor performance using nanomaterials. Glucose biosensors based on commonly applied enzyme immobilization approaches, including sol-gel encapsulation approaches and glutaraldehyde cross-linking strategies, were studied in the presence and absence of multi-walled carbon nanotubes (MWNTs). Although direct comparison of design parameters such as linear range and sensitivity is intuitive, this comparison alone is not an accurate indicator of biosensor efficacy, due to the wide range of electrodes and nanomaterials available for use in current biosensor designs. We proposed a comparative protocol which considers both the active area available for transduction following nanomaterial deposition and the sensitivity. Based on the protocol, when no nanomaterials were involved, TEOS/GOx biosensors exhibited the highest efficacy, followed by BSA/GA/GOx and TMOS/GOx biosensors. A novel biosensor containing carboxylated MWNTs modified with glucose oxidase and an overlying TMOS layer demonstrated optimum efficacy in terms of enhanced current density (18.3 ± 0.5 μA mM -1 cm -2 ), linear range (0.0037-12 mM), detection limit (3.7 μM), coefficient of variation (2%), response time (less than 8 s), and stability/selectivity/reproducibility. H 2 O 2 response tests demonstrated that the most possible reason for the performance enhancement was an increased enzyme loading. This design is an excellent platform for versatile biosensing applications.

  2. Potentiometric urea biosensor based on multi-walled carbon nanotubes (MWCNTs)/silica composite material

    International Nuclear Information System (INIS)

    Ahuja, Tarushee; Kumar, D.; Singh, Nahar; Biradar, A.M.; Rajesh

    2011-01-01

    A novel potentiometric urea biosensor has been fabricated with urease (Urs) immobilized multi-walled carbon nanotubes (MWCNTs) embedded in silica matrix deposited on the surface of indium tin oxide (ITO) coated glass plate. The enzyme Urs was covalently linked with the exposed free -COOH groups of functionalized MWCNTs (F-MWCNTs), which are subsequently incorporated within the silica matrix by sol-gel method. The Urs/MWCNTs/SiO 2 /ITO composite modified electrode was characterized by Fourier transform infrared (FTIR) spectroscopy, thermal gravimetric analysis (TGA) and UV-visible spectroscopy. The morphologies and electrochemical performance of the modified Urs/MWCNTs/SiO 2 /ITO electrode have been investigated by scanning electron microscopy (SEM) and potentiometric method, respectively. The synergistic effect of silica matrix, F-MWCNTs and biocompatibility of Urs/MWCNTs/SiO 2 made the biosensor to have the excellent electro catalytic activity and high stability. The resulting biosensor exhibits a good response performance to urea detection with a wide linear range from 2.18 x 10 -5 to 1.07 x 10 -3 M urea. The biosensor shows a short response time of 10-25 s and a high sensitivity of 23 mV/decade/cm 2 .

  3. Electronic excitation induced modifications in elongated iron nanoparticle encapsulated multiwalled carbon nanotubes under ion irradiation

    Science.gov (United States)

    Saikiran, V.; Bazylewski, P.; Sameera, I.; Bhatia, Ravi; Pathak, A. P.; Prasad, V.; Chang, G. S.

    2018-05-01

    Multi-wall carbon nanotubes (MWCNT) filled with Fe nanorods were shown to have contracted and deformed under heavy ion irradiation. In this study, 120 MeV Ag and 80 MeV Ni ion irradiation was performed to study the deformation and defects induced in iron filled MWCNT under heavy ion irradiation. The structural modifications induced due to electronic excitation by ion irradiation were investigated employing high-resolution transmission electron microscopy, micro-Raman scattering experiments, and synchrotron-based X-ray absorption and emission spectroscopy. We understand that the ion irradiation causes modifications in the Fe nanorods which result in compressions and expansions of the nanotubes, and in turn leads to the buckling of MWCNT. The G band of the Raman spectra shifts slightly towards higher wavenumber and the shoulder G‧ band enhances with the increase of ion irradiation fluence, where the buckling wavelength depends on the radius 'r' of the nanotubes as exp[(r)0.5]. The intensity ratio of the D to G Raman modes initially decreases at the lowest fluence, and then it increases with the increase in ion fluence. The electron diffraction pattern and the high resolution images clearly show the presence of ion induced defects on the walls of the tube and encapsulated iron nanorods.

  4. The role of the iron catalyst in the toxicity of multi-walled carbon nanotubes (MWCNTs).

    Science.gov (United States)

    Visalli, Giuseppa; Facciolà, Alessio; Iannazzo, Daniela; Piperno, Anna; Pistone, Alessandro; Di Pietro, Angela

    2017-09-01

    This study aimed to investigate the role of iron, used as a catalyst, in the biological response to pristine and functionalized multi-walled carbon nanotubes (p/fMWCNTs) with an iron content of 2.5-2.8%. Preliminarily, we assessed the pro-oxidant activity of MWCNTs-associated iron by an abiotic test. To evaluate iron bioavailability, we measured intracellular redox-active iron in A549 cells exposed to both MWCNT suspensions and to the cell medium preconditioned by MWCNTs, in order to assess the iron dissolution rate under physiological conditions. Moreover, in exposed cells, we detected ROS levels, 8-oxo-dG and mitochondrial function. The results clearly highlighted that MWCNTs- associated iron was not redox-active and that iron leakage did not occur under physiological conditions, including the oxidative burst of specialized cells. Despite this, in MWCNTs exposed cells, higher level of intracellular redox-active iron was measured in comparison to control and a significant time-dependent ROS increase was observed (P<0.01). Higher levels of 8-oxo-dG, a marker of oxidative DNA damage, and decreased mitochondrial function, confirmed the oxidative stress induced by MWCNTs. Based on the results we believe that oxidative damage could be attributable to the release of endogenous redox-active iron. This was due to the damage of acidic vacuolar compartment caused by endocytosis-mediated MWCNT internalization. Copyright © 2017 Elsevier GmbH. All rights reserved.

  5. Real time radiation dosimeters based on vertically aligned multiwall carbon nanotubes and graphene.

    Science.gov (United States)

    Funaro, Maria; Sarno, Maria; Ciambelli, Paolo; Altavilla, Claudia; Proto, Antonio

    2013-02-22

    Measurements of the absorbed dose and quality assurance programs play an important role in radiotherapy. Ionization chambers (CIs) are considered the most important dosimeters for their high accuracy, practicality and reliability, allowing absolute dose measurements. However, they have a relative large physical size, which limits their spatial resolution, and require a high bias voltage to achieve an acceptable collection of charges, excluding their use for in vivo dosimetry. In this paper, we propose new real time radiation detectors with electrodes based on graphene or vertically aligned multiwall carbon nanotubes (MWCNTs). We have investigated their charge collection efficiency and compared their performance with electrodes made of a conventional material. Moreover, in order to highlight the effect of nanocarbons, reference radiation detectors were also tested. The proposed dosimeters display an excellent linear response to dose and collect more charge than reference ones at a standard bias voltage, permitting the construction of miniaturized CIs. Moreover, an MWCNT based CI gives the best charge collection efficiency and it enables working also to lower bias voltages and zero volts, allowing in vivo applications. Graphene based CIs show better performance with respect to reference dosimeters at a standard bias voltage. However, at decreasing bias voltage the charge collection efficiency becomes worse if compared to a reference detector, likely due to graphene's semiconducting behavior.

  6. Contacts, non-linear transport effects and failure in multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    Berger, C; Yi, Y; Gezo, J; Poncharal, P; Heer, W A de

    2003-01-01

    Pristine arc-produced multi-walled carbon nanotubes are contacted to liquid mercury in situ in a transmission electron microscope. The conductance G(V) for all tubes increases with increasing bias voltage V. This is related to the electronic density of the nanotubes. Similar G(V) behaviour is observed for HOPG-graphite contacted in air with Hg, with dG(V)/dV∼0.3G 0 . Variations observed in the conductance are related to nanotube-Hg contact effects. For tubes barely touching the Hg surface, the conductance is low (typically G(V=0)∼0.1-0.5G 0 ); G(V) may maximize around V=1.5-2 V or continue to increase linearly depending on the MWNT-Hg contact. For good contacts the maximum low-bias conductance is 1G 0 . Non-conducting tubes are observed having a low-bias conductance smaller than 10 -3 G 0 . High-voltage tube failure usually occurs at the contact with Hg for clean tubes, or at tube defects. An important phenomenon is the formation of a Hg bubble near the contact nanotube-Hg surface when the nanotube is negatively biased, under high bias current conditions, indicating the heating effect of hot electrons injected into the mercury

  7. Structural, thermal and electrical characterizations of multiwalled carbon nanotubes and polyaniline composite

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Kamal, E-mail: singhkamal204@gmail.com; Garg, Leena; Singh, Jaspal [Department of Applied Sciences, Chandigarh University, Gharuan, Mohali (India); Kumar, Sanjeev [Applied Sciences Department, PEC University of Technology, Chandigarh (India); Sharma, Amit L. [Central Scientific Instrumentation Organization, Sector 30, Chandigarh (India)

    2016-05-06

    The undoped and doped composite of MWNTs (Multiwalled Carbon Nanotubes) with PANI (/Polyaniline) was prepared by chemical oxidative polymerization. The MWNTs/PANI composites have been characterized by using various techniques like Thermogravometric Analysis (TGA), Fourier transform infrared (FT-IR) spectrometer and Field emission scanning electron microscope (FE-SEM) and conductivity measurement by using two probe method. TGA results has shown that thermal stability followed the pattern undoped MWNTs/PANI composite < doped MWNTs/PANI composite. FE-SEM micrographs demonstrated the morphological changes on the surface of MWNTs as a result of composite formation. Fourier transformed infrared (FT-IR) spectra ascertained the formation of the composite. Study of electrical characteristics demonstrated that the doped MWNTs/PANI composite (1.2 × 10{sup 1} Scm{sup −1}) have better conductivity than the undoped MWNTs/PANI composite (10{sup −4} Scm{sup −1}). These CNTs based polymeric composites are of great importance in developing new nano-scale devices for future chemical, mechanical and electronic applications.

  8. Oxidized multiwalled carbon nanotubes decorated with silver nanoparticles for fluorometric detection of dimethoate.

    Science.gov (United States)

    Hsu, Chun-Wei; Lin, Zhong-Yi; Chan, Tzu-Yi; Chiu, Tai-Chia; Hu, Cho-Chun

    2017-06-01

    A novel method for the detection of dimethoate based on the peroxidase-like activity of silver-nanoparticles-modified oxidized multiwalled carbon nanotubes (AgNPs/oxMWCNTs) has been developed. The synthesized AgNPs/oxMWCNTs showed excellent peroxidease-like catalytic activity in hydrogen peroxide-Amplex red (AR) system (AR is oxidized to resorufinat, with the resorufin fluorescence at 584nm being used to monitor the catalytic activity). After dimethoate was added to AgNPs/oxMWCNTs, the interaction between dimethoate and the AgNPs inhibited the catalytic activity of AgNPs/oxMWCNTs. The decrease in fluorescence was used for the detection of dimethoate in the range of 0.01-0.35μgmL -1 (R 2 =0.998) with a detection limit of 0.003μgmL -1 (signal/noise=3). This method exhibited good selectivity for the detection of dimethoate even in the presence of high concentration of other pesticides. Consequently, the method was applied to measure the concentration of dimethoate residue in lake water and fruit, thus obtaining satisfactory results. Copyright © 2016 Elsevier Ltd. All rights reserved.

  9. Multi-walled carbon nanotubes can enhance root elongation of wheat (Triticum aestivum) plants

    Energy Technology Data Exchange (ETDEWEB)

    Wang Xiuping; Han Heyou, E-mail: hyhan@mail.hzau.edu.cn; Liu Xueqin; Gu Xiaoxu; Chen Kun; Lu Donglian [Huazhong Agricultural University, College of Science, State Key Laboratory of Agricultural Microbiology, Institute of Chemical Biology (China)

    2012-06-15

    The potential effects of oxidized multi-walled carbon nanotubes (o-MWCNTs) with a length ranging from 50 to 630 nm on the development and physiology of wheat plants were evaluated by examining their effects on seed germination, root elongation, stem length, and vegetative biomass at a concentration ranging from 10 to 160 {mu}g/mL in the plant. Results indicated that after 7 days of exposure to the o-MWCNTs medium, faster root growth and higher vegetative biomass were observed, but seed germination and stem length did not show any difference as compared with controls. Moreover, a physiological study was conducted at cellular level using a traditional physiological approach to evidence the possible alterations in morphology, the cell length of root zone, and the dehydrogenase activity of seedlings. Transmission electron microscopy images revealed that o-MWCNTs could penetrate the cell wall and enter the cytoplasm after being taken up by roots. The cell length of root zone for the seedlings germinated and grown in the o-MWCNTs (80 {mu}g/mL) medium increased by 1.4-fold and a significant concentration-dependent increase in the dehydrogenase activity for the o-MWCNT-treated wheat seedlings was detected. These findings suggest that o-MWCNTs can significantly promote cell elongation in the root system and increase the dehydrogenase activity, resulting in faster root growth and higher biomass production.

  10. Multi-wall carbon nanotubes investigated by positron annihilation techniques and microscopies for further production handling

    Energy Technology Data Exchange (ETDEWEB)

    Luu, A.T.; Thanh, N.D.; Dung, T.Q.; Son, L.T.; Phuc, P.T. [Center for Nuclear Techniques, Vietnam Atomic Energy Commission, Ho Chi Minh City (Viet Nam); Kajcsos, Zs. [KFKI Research Institute for Particle and Nuclear Physics, Budapest (Hungary); Nhon, M.V.; Tap, T.D. [Department of Nuclear Physics, Faculty of Physics, University of Natural Sciences, Ho Chi Minh City (Viet Nam); Lazar, K. [Institute of Isotopes HAS, Budapest (Hungary); Havancsak, K.; Huhn, G. [Department of Materials Physics, Budapest Univ. (Hungary); Horvath, Z.E. [Research Institute for Technical Physics and Materials Sciences, Budapest (Hungary)

    2009-11-15

    Multi-wall carbon nanotube samples with various tube diameters produced by Thermal Chemical Vapor Deposition technique using various catalysts were studied by various microscopic methods and positron annihilation spectroscopy (PAS) with the aim of assessing the applicability of these methods for structural studies in these novel materials. Specifically, positron lifetime (LT) and Doppler broadening (DB) techniques, transmission electron microscopy (TEM) and atomic force microscopy (AFM) were employed, on iron-containing samples Moessbauer spectroscopy was also utilized. The PAS measurements were carried out on densely packed powder samples and on samples pressed into pills in atmospheric pressure and in vacuum as well. The lifetime values could be interpreted by assuming trapping of positrons, the low contribution from longer-living trapped positronium can be probably related to defects on walls of the tubes. Possibility of correlation of LT and DB data with the nanotube sizes and sample composition was also considered. (copyright 2009 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  11. Oxidation behavior of multiwall carbon nanotubes with different diameters and morphology

    Energy Technology Data Exchange (ETDEWEB)

    Mazov, Ilya, E-mail: ilya.mazov@gmail.com [Boreskov Institute of Catalysis, Lavrentieva ave. 5, Novosibirsk, 630090 (Russian Federation); Kuznetsov, Vladimir L. [Boreskov Institute of Catalysis, Lavrentieva ave. 5, Novosibirsk, 630090 (Russian Federation); Novosibirsk State University, Pirogova st. 2, Novosibirsk, 630090 (Russian Federation); Simonova, Irina A. [Boreskov Institute of Catalysis, Lavrentieva ave. 5, Novosibirsk, 630090 (Russian Federation); Stadnichenko, Andrey I. [Boreskov Institute of Catalysis, Lavrentieva ave. 5, Novosibirsk, 630090 (Russian Federation); Novosibirsk State University, Pirogova st. 2, Novosibirsk, 630090 (Russian Federation); Ishchenko, Arkady V. [Boreskov Institute of Catalysis, Lavrentieva ave. 5, Novosibirsk, 630090 (Russian Federation); Romanenko, Anatoly I.; Tkachev, Evgeniy N.; Anikeeva, Olga B. [Nikolaev Institute of Inorganic Chemistry, Lavrentieva ave. 3, Novosibirsk, 630090 (Russian Federation); Novosibirsk State University, Pirogova st. 2, Novosibirsk, 630090 (Russian Federation)

    2012-06-15

    Multiwall carbon nanotubes (MWNT) with three medium diameters (20-22, 9-13, and 6-8 nm) and different morphology were chemically oxidized using concentrated nitric acid, mixture of nitric and sulfuric acids ('melange' solution) and mixture of sulfuric acid and hydrogen peroxide ('piranha' solution). Influence of MWNT type and structure as well as type of oxidizer on the surface composition and structure of nanotubes after oxidation was investigated. Acid-base titration, X-ray photoelectron spectroscopy and thermal gravimetric analysis were used for quantitative and qualitative investigation of surface group composition of initial and oxidized nanotubes. Amount of oxygen-containing groups on the surface of oxidized MWNT depends on the type of initial MWNT. It was found that ratio of different oxygen containing groups is less dependent on the type of oxidizer. Electrophysical properties of initial and oxidized nanotubes were investigated in temperature range 4-293 K and main types of electrical conductivity were determined. It was shown that oxidation results in decrease in electrical conductivity of all samples with simultaneous change in the conductivity mechanism. Dispersive behavior of initial and oxidized nanotubes in different commonly used solvents was investigated. It was shown that oxidation leads to the improvement of sedimentation stability of MWNT in polar solvents.

  12. Oxidation behavior of multiwall carbon nanotubes with different diameters and morphology

    Science.gov (United States)

    Mazov, Ilya; Kuznetsov, Vladimir L.; Simonova, Irina A.; Stadnichenko, Andrey I.; Ishchenko, Arkady V.; Romanenko, Anatoly I.; Tkachev, Evgeniy N.; Anikeeva, Olga B.

    2012-06-01

    Multiwall carbon nanotubes (MWNT) with three medium diameters (20-22, 9-13, and 6-8 nm) and different morphology were chemically oxidized using concentrated nitric acid, mixture of nitric and sulfuric acids ("mélange" solution) and mixture of sulfuric acid and hydrogen peroxide ("piranha" solution). Influence of MWNT type and structure as well as type of oxidizer on the surface composition and structure of nanotubes after oxidation was investigated. Acid-base titration, X-ray photoelectron spectroscopy and thermal gravimetric analysis were used for quantitative and qualitative investigation of surface group composition of initial and oxidized nanotubes. Amount of oxygen-containing groups on the surface of oxidized MWNT depends on the type of initial MWNT. It was found that ratio of different oxygen containing groups is less dependent on the type of oxidizer. Electrophysical properties of initial and oxidized nanotubes were investigated in temperature range 4-293 K and main types of electrical conductivity were determined. It was shown that oxidation results in decrease in electrical conductivity of all samples with simultaneous change in the conductivity mechanism. Dispersive behavior of initial and oxidized nanotubes in different commonly used solvents was investigated. It was shown that oxidation leads to the improvement of sedimentation stability of MWNT in polar solvents.

  13. Removal of virus and toxin using heatable multi-walled carbon nanotube web filters

    Directory of Open Access Journals (Sweden)

    Hoon-Sik Jang

    2016-02-01

    Full Text Available Many studies have used a carbon nanotube (CNT filter for pathogen removal and/or inactivation by means of electrochemical or electrochlorination. The large surface area, fine pore size and high electrical and thermal conductivity of CNTs make them suitable and distinct to use for the filtering and removal of pathogens. Here, we grew spin-capable multi-walled CNTs (MWCNTs and manufactured a web filter using the spun MWCNTs. Botulinum toxin type E light chain (BoT/E-LC and vaccinia virus (VV were filtered using the MWCNT web filters and were evaporated and removed by applying direct current (DC voltage to both sides of the MWCNT webs, excluding electrochemical or electrochlorination. The filtering and removal of BoT/E-LC and VV were performed after seven layers of the MWCNT sheets were coated onto a silicon oxide porous plate. The electrical resistance of the webs in the seven layer sheet was 293 Ω. The temperature of MWCNTs webs was linearly increased to ∼300 °C at 210 V of DC voltage. This temperature was enough to remove BoT/E-LC and VV. From the SEM and XPS results, we confirmed that BoT/E-LC and VV on the MWCNT webs were almost removed by applying a DC voltage and that some element (N, Na, Cl, etc. as residues on the MWCNT webs remained.

  14. Effect of p-type multi-walled carbon nanotubes for improving hydrogen storage behaviors

    International Nuclear Information System (INIS)

    Lee, Seul-Yi; Yop Rhee, Kyong; Nahm, Seung-Hoon; Park, Soo-Jin

    2014-01-01

    In this study, the hydrogen storage behaviors of p-type multi-walled carbon nanotubes (MWNTs) were investigated through the surface modification of MWNTs by immersing them in sulfuric acid (H 2 SO 4 ) and hydrogen peroxide (H 2 O 2 ) at various ratios. The presence of acceptor-functional groups on the p-type MWNT surfaces was confirmed by X-ray photoelectron spectroscopy. Measurement of the zeta-potential determined the surface charge transfer and dispersion of the p-type MWMTs, and the hydrogen storage capacity was evaluated at 77 K and 1 bar. From the results obtained, it was found that acceptor-functional groups were introduced onto the MWNT surfaces, and the dispersion of MWNTs could be improved depending on the acid-mixed treatment conditions. The hydrogen storage was increased by acid-mixed treatments of up to 0.36 wt% in the p-type MWNTs, compared with 0.18 wt% in the As-received MWNTs. Consequently, the hydrogen storage capacities were greatly influenced by the acceptor-functional groups of p-type MWNT surfaces, resulting in increased electron acceptor–donor interaction at the interfaces. - Graphical abstract: Hydrogen storage behaviors of the p-type MWNTs with the acid-mixed treatments are described. Display Omitted Display Omitted

  15. Effects of multi-walled carbon nanotubes (MWCNT under Neisseria meningitidis transformation process

    Directory of Open Access Journals (Sweden)

    Mattos Ives B

    2011-11-01

    Full Text Available Abstract Background This study aimed at verifying the action of multi-walled carbon nanotubes (MWCNT under the naturally transformable Neisseria meningitidis against two different DNA obtained from isogenic mutants of this microorganism, an important pathogen implicated in the genetic horizontal transfer of DNA, causing the escape of the principal vaccination measured worldwide by the capsular switching process. Materials and methods The bacterium receptor strain C2135 was cultivated and had its mutant DNA donor M2 and M6, which received a receptor strain and MWCNT at three different concentrations. The inhibition effect of DNAse on the DNA in contact with nanoparticles was evaluated. Results The results indicated an in increase in the transformation capacity of N. meninigtidis in different concentrations of MWCNT when compared with negative control without nanotubes. A final analysis of the interaction between DNA and MWCNT was carried out using Raman Spectroscopy. Conclusion These increases in the transformation capacity mediated by MWCNT, in meningococci, indicate the interaction of these particles with the virulence acquisition of these bacteria, as well as with the increase in the vaccination escape process.

  16. Synthesis of multi-walled carbon nanotubes/{beta}-FeOOH nanocomposites with high adsorption capacity

    Energy Technology Data Exchange (ETDEWEB)

    Song Haojie, E-mail: shj6922@163.com [School of Materials Science and Engineering, Jiangsu University (China); Liu Lei [Pharmaceutic College of Henan University (China); Jia Xiaohua; Min Chunying [School of Materials Science and Engineering, Jiangsu University (China)

    2012-12-15

    A hybrid nanostructure of multi-walled carbon nanotubes (CNTs) and {beta}-ferric oxyhydroxide ({beta}-FeOOH) nanoparticles is synthesized by ultrasonic-assisted in situ hydrolysis of the precursor ferric chloride and CNTs. Characterization by X-ray diffraction, scanning electron microscopy , and transmission electron microscopy establishes the nanohybrid structure of the synthesized sample. The results revealed that the surface of CNTs was uniformly assembled by numerous {beta}-FeOOH nanoparticles and had an average diameter of 3 nm. The formation route of anchoring {beta}-FeOOH nanoparticles onto CNTs was proposed as the intercalation and adsorption of iron ions onto the wall of CNTs, followed by the nucleation and growth of {beta}-FeOOH nanoparticles. The values of remanent magnetization (M{sub r}) and coercivity (H{sub c}) of the as-synthesized CNTs/{beta}-FeOOH nanocomposites were 0.1131 emu g, and 490.824 Oe, respectively. Furthermore, CNTs/{beta}-FeOOH nanocomposites showed a very high adsorption capacity of Congo red and thus these nanocomposites can be used as good adsorbents and can be used for the removal of the dye of Congo red from the waste water system.

  17. Gas sensors for ammonia detection based on polyaniline-coated multi-wall carbon nanotubes

    International Nuclear Information System (INIS)

    He Lifang; Jia Yong; Meng Fanli; Li Minqiang; Liu Jinhuai

    2009-01-01

    Polyaniline-coated multi-wall carbon nanotubes (PANI-coated MWNTs) were prepared by in situ polymerization method. Field emission scanning electron microscopy, transmission electron microscopy, Raman spectroscopy, and thermogravimetric analysis were used to characterize the as-prepared PANI-coated MWNTs. Obtained results indicated that PANI was uniformly coated on MWNTs, and the thickness of the coatings can be controlled by changing the weight ratios of aniline monomer and MWNTs in the polymerization process. Sensors were fabricated by spin-coating onto pre-patterned electrodes, and ammonia gas sensing properties of the as-prepared PANI-coated MWNTs were studied. The results showed a good response and reproducibility towards ammonia at room temperature. In addition, PANI-coated MWNTs exhibited a linear response to ammonia in the range of 0.2-15 ppm. The effects of the thickness of PANI coatings on the gas sensing properties were also investigated in detail. The results suggest a potential application of PANI-coated MWNTs in gas sensor for detecting ammonia.

  18. Multiwalled Carbon Nanotube-TiO2 Nanocomposite for Visible-Light-Induced Photocatalytic Hydrogen Evolution

    Directory of Open Access Journals (Sweden)

    Ke Dai

    2014-01-01

    Full Text Available Multiwalled carbon nanotube- (MWCNT- TiO2 nanocomposite was synthesized via hydrothermal process and characterized by X-ray diffraction, UV-vis diffuse reflectance spectroscopy, field emission scanning electron microscope, thermogravimetry analysis, and N2 adsorption-desorption isotherms. Appropriate pretreatment on MWCNTs could generate oxygen-containing groups, which is beneficial for forming intimate contact between MWCNTs and TiO2 and leads to a higher thermal stability of MWCNT-TiO2 nanocomposite. Modification with MWCNTs can extend the visible-light absorption of TiO2. 5 wt% MWCNT-TiO2 derived from hydrothermal treatment at 140°C exhibiting the highest hydrogen generation rate of 15.1 μmol·h−1 under visible-light irradiation and a wide photoresponse range from 350 to 475 nm with moderate quantum efficiency (4.4% at 420 nm and 3.7% at 475 nm. The above experimental results indicate that the MWCNT-TiO2 nanocomposite is a promising photocatalyst with good stability and visible-light-induced photoactivity.

  19. Hyaluronate tethered, "smart" multiwalled carbon nanotubes for tumor-targeted delivery of doxorubicin.

    Science.gov (United States)

    Datir, Satyajit R; Das, Manasmita; Singh, Raman Preet; Jain, Sanyog

    2012-11-21

    The present study reports the optimized synthesis, physicochemical characterization, and biological evaluation of a novel, multiwalled carbon nanotube-hyaluronic acid (MWCNT-HA) conjugate, complexed with an anticancer agent, Doxorubicin (DOX) via π-π stacking interaction. The therapeutic conjugate was concomitantly labeled with a near-infrared fluorescent dye, Alexa-Flour-647 (AF-647), and radiotracer Technetium-99m ((99m)Tc) to track its whereabouts both in vitro and in vivo via optical and scintigraphic imaging techniques. Covalent functionalization of MWCNTs with HA facilitated their internalization into human lung adenocarcinoma, A549 cells via hyaluronan receptors (HR) mediated endocytosis. Internalized nanotubes showed lysosomal trafficking, followed by low pH-triggered DOX release under endolysosomal conditions. Consequently, DOX-loaded HA-MWCNTs exhibited 3.2 times higher cytotoxicity and increased apoptotic activity than free DOX in equivalent concentrations. Organ distribution studies in Ehlrich ascites tumor (EAT) bearing mice model indicated that tumor specific localization of (99m)Tc-MWCNT-HA-DOX is significantly higher than both free drug and nontargeted MWCNTs. Pharmacodynamic studies in chemically breast-cancer-induced rats showed that the tumor-growth inhibitory effect of HA-MWCNT-DOX was 5 times higher than free DOX in equivalent concentration. DOX delivered through HA-MWCNTs was devoid of any detectable cardiotoxity, hepatotoxicity, or nephrotoxicity. All these promising attributes make HA-MWCNTs a "smart" platform for tumor-targeted delivery of anticancer agents.

  20. Oriented Polyaniline Nanowire Arrays Grown on Dendrimer (PAMAM) Functionalized Multiwalled Carbon Nanotubes as Supercapacitor Electrode Materials.

    Science.gov (United States)

    Jin, Lin; Jiang, Yu; Zhang, Mengjie; Li, Honglong; Xiao, Linghan; Li, Ming; Ao, Yuhui

    2018-04-19

    At present, PANI/MWNT composites have been paid more attention as promising electrode materials in supercapacitors. Yet some shortcomings still limit the widely application of PANI/MWNT electrolytes. In this work, in order to improve capacitance ability and long-term stability of electrode, a multi-amino dendrimer (PAMAM) had been covalently linked onto multi-walled carbon nanotubes (MWNT) as a bridge to facilitating covalent graft of polyaniline (PANI), affording P-MWNT/PANI electrode composites for supercapacitor. Surprisingly, ordered arrays of PANI nanowires on MWNT (setaria-like morphology) had been observed by scanning electron microscopy (SEM). Electrochemical properties of P-MWNT/PANI electrode had been characterized by cyclic voltammetry (CV) and galvanostatic charge-discharge technique. The specific capacitance and long cycle life of P-MWNT-PANI electrode material were both much higher than MWNT/PANI. These interesting results indicate that multi-amino dendrimer, PAMAM, covalently linked on MWNT provides more reaction sites for in-situ polymerization of ordered PANI, which could efficiently shorten the ion diffusion length in electrolytes and lead to making fully use of conducting materials.

  1. Polyaniline/partially exfoliated multi-walled carbon nanotubes based nanocomposites for supercapacitors

    International Nuclear Information System (INIS)

    Potphode, Darshna D.; Sivaraman, P.; Mishra, Sarada P.; Patri, Manoranjan

    2015-01-01

    In the present study, polyaniline (PANI)/partially exfoliated multi-walled carbon nanotubes (Px-MWCNT) nanocomposites were investigated for supercapacitor application. Nanocomposites with varying weight/weight ratio of PANI and Px-MWCNT were prepared by in-situ polymerization of aniline over Px-MWCNT. Transmission and scanning electron microscopic analysis showed that the MWCNT was partial unzipped along the length of tubes. The morphology of PANI/Px-MWCNT nanocomposites exhibited wrapping of PANI over Px-MWCNT. Symmetric supercapacitors containing PANI/Px-MWCNT nanocomposites as the electrode material were fabricated. The electrochemical characterization of the nanocomposites was carried by two electrode method (unit cell configuration). Cyclic voltammetric analysis showed a synergistic increase in specific capacitance of the nanocomposites. Charge-discharge cycle study indicated that nanocomposites have greater charge-discharge rate capability than pure PANI. The observed result is attributed to the shorter diffusion length of ions in the nanocomposites as compared to that of pure PANI. The electrochemical impedance spectra of supercapacitors were resolved into real and losscapacitances. The loss capacitance indicated that the time constant of the nanocomposites decreases with increase in the Px-MWCNT content. The supercapacitors showed enhanced stability during continuous charge-discharge cycling as the PX-MWCNT content in the nanocomposites increased. PANI-50 and PANI-25 nanocomposites based supercapacitors exhibited 91% and 93% capacitive retention after 2000 charge-discharge cycle while pure PANI showed only 67% capacitance retention for the same number of cycles

  2. Highly Conductive Aromatic Functionalized Multi-Walled Carbon Nanotube for Inkjet Printable High Performance Supercapacitor Electrodes.

    Directory of Open Access Journals (Sweden)

    Sanjeev K Ujjain

    Full Text Available We report the functionalization of multiwalled carbon nanotubes (MWCNT via the 1,3-dipolar [3+2] cycloaddition of aromatic azides, which resulted in a detangled CNT as shown by transmission electron microscopy (TEM. Carboxylic moieties (-COOH on aromatic azide result in highly stable aqueous dispersion (max. conc. ~ 10 mg/mL H2O, making the suitable for inkjet printing. Printed patterns on polyethylene terephthalate (PET flexible substrate exhibit low sheet resistivity ~65 Ω. cm, which is attributed to enhanced conductivity. Fabricated Supercapacitors (SC assembled using these printed substrates exhibit good electrochemical performance in organic as well as aqueous electrolytes. High energy and power density (57.8 Wh/kg and 0.85 kW/kg in 1M H2SO4 aqueous electrolyte demonstrate the excellent performance of the proposed supercapacitor. Capacitive retention varies from ~85-94% with columbic efficiency ~95% after 1000 charge/discharge cycles in different electrolytes, demonstrating the excellent potential of the device for futuristic power applications.

  3. Hydroxyapatite growth on multiwall carbon nanotubes grown on titanium fibers from a titanium sheet

    KAUST Repository

    Chetibi, Loubna; Achour, Amine; Peszke, Jerzy; Hamana, Djamel; Achour, Slimane

    2013-01-01

    Nano-hydroxyapatite (HA) was grown on functionalized multiwalled carbon nanotubes (MWCNTs) deposited on TiO2 nanofibers (NFs) that were hydrothermally grown on Ti metal sheets. The HA was electrochemically grown on the MWCNTs/TiO2 porous layer. It was found that the HA grows on the MWCNTs/TiO2 NFs in the form of dense coating with nanorice grain-shaped. The incorporation of MWCNTs between HA and TiO2 NFs has led to higher adhesion strength as measured by micro-scratching test indicating the benefit of MWCNTs on the improving the bonding strength of HA layer. The obtained coatings exhibit excellent corrosion resistance in simulated body fluid. It is expected that this simple route for preparing the new HA/MWCNTs/TiO2/Ti-layered structure might be used not only in the biomedical field, but also in catalysis and biological sensing among others. © 2013 Springer Science+Business Media New York.

  4. Electrical conductivity and piezoresistive response of 3D printed thermoplastic polyurethane/multiwalled carbon nanotube composites

    Science.gov (United States)

    Hohimer, Cameron J.; Petrossian, Gayaneh; Ameli, Amir; Mo, Changki; Pötschke, Petra

    2018-03-01

    Additive manufacturing (AM) is an emerging field experiencing rapid growth. This paper presents a feasibility study of using fused-deposition modeling (FDM) techniques with smart materials to fabricate objects with sensing and actuating capabilities. The fabrication of objects with sensing typically requires the integration and assembly of multiple components. Incorporating sensing elements into a single FDM process has the potential to significantly simplify manufacturing. The integration of multiple materials, especially smart materials and those with multi-functional properties, into the FDM process is challenging and still requires further development. Previous works by the authors have demonstrated a good printability of thermoplastic polyurethane/multiwall carbon nanotubes (TPU/MWCNT) while maintaining conductivity and piezoresistive response. This research explores the effects of layer height, nozzle temperature, and bed temperature on the electrical conductivity and piezoresistive response of printed TPU/MWCNT nanocomposites. An impedance analyzer was used to determine the conductivity of printed samples under different printing conditions from 5Hz-13MHz. The samples were then tested under compression loads to measure the piezoresistive response. Results show the conductivity and piezoresistive response are only slightly affected by the print parameters and they can be largely considered independent of the print conditions within the examined ranges of print parameters. This behavior simplifies the printing process design for TPU/MWCNT complex structures. This work demonstrates the possibility of manufacturing embedded and multidirectional flexible strain sensors using an inexpensive and versatile method, with potential applications in soft robotics, flexible electronics, and health monitoring.

  5. Adsorption and desorption of radionuclide europium(III) on multiwalled carbon nanotubes studied by batch techniques

    International Nuclear Information System (INIS)

    Songsheng Lu; Junzheng Xu; Caicai Zhang; Zhiwei Niu

    2011-01-01

    The adsorption of Eu(III) on multiwalled carbon nanotubes (MWCNTs) as a function of pH, ionic strength and solid contents are studied by batch technique. The results indicate that the adsorption of Eu(III) on MWCNTs is strongly dependent on pH values, dependent on ionic strength at low pH values and independent of ionic strength at high pH values. Strong surface complexation and ion exchange contribute to the adsorption of Eu(III) on MWCNTs at low pH values, whereas surface complexation and surface precipitation are the main adsorption mechanism of Eu(III) on MWCNTs. The desorption of adsorbed Eu(III) from MWCNTs by adding HCl is also studied and the recycling use of MWCNTs in the removal of Eu(III) is investigated after the desorption of Eu(III) at low pH values. The results indicate that adsorbed Eu(III) can be easily desorbed from MWCNTs at low pH values, and MWCNTs can be repeatedly used to remove Eu(III) from aqueous solutions. MWCNTs are suitable material in the preconcentration and solidification of radionuclides from large volumes of aqueous solutions in nuclear waste management. (author)

  6. Miniemulsion copolymerization of (methacrylates in the presence of functionalized multiwalled carbon nanotubes for reinforced coating applications

    Directory of Open Access Journals (Sweden)

    Bertha T. Pérez-Martínez

    2017-06-01

    Full Text Available Film forming, stable hybrid latexes made of methyl metacrylate (MMA, butyl acrylate (BA and 2-hydroxyethyl methacrylate (HEMA copolymer reinforced with modified multiwalled carbon nanotubes (MWCNTs were synthesized by in situ miniemulsion polymerization. The MWCNTs were pretreated by an air sonication process and stabilized by polyvinylpyrrolidone. The presence of the MWCNTs had no significant effect on the polymerization kinetics, but strongly affected the polymer characteristics (Tg and insoluble polymer fraction. The performance of the in situ composites was compared with that of the neat polymer dispersion as well as with those of the polymer/MWCNT physical blends. The in situ composites showed the presence of an additional phase likely due to the strong interaction between the polymer and MWNCTs (including grafting that reduced the mobility of the polymer chains. As a result, a substantial increase of both the storage and the loss moduli was achieved. At 60 °C, which is above the main transition region of the polymer, the in situ composites maintained the reinforcement, whereas the blends behaved as a liquid-like material. This suggests the formation of a 3D network, in good agreement with the high content of insoluble polymer in the in situ composites.

  7. Optimized network of multi-walled carbon nanotubes for chemical sensing

    International Nuclear Information System (INIS)

    Gohier, A; Chancolon, J; Porterat, D; Mayne-L'Hermite, M; Reynaud, C; Chenevier, P

    2011-01-01

    This work reports the design of a resistive gas sensor based on 2D mats of multi-walled carbon nanotubes (MWCNTs) grown by aerosol-assisted chemical vapour deposition. The sensor sensitivity was optimized using chlorine as analyte by tuning both CNT network morphology and CNT electronic properties. Optimized devices, operating at room temperature, have been calibrated over a large range of concentration and are shown to be sensitive down to 27 ppb of chlorine. The as-grown MWCNT response is compared with responses of 2000 deg. C annealed CNTs, as well as of nitrogen-doped CNTs and CNTs functionalized with polyethyleneimine (PEI). Under chlorine exposure, the resistance decrease of as-grown and annealed CNTs is attributed to charge transfer from chlorine to CNTs and demonstrates their p-type semiconductor behaviour. XPS analysis of CNTs exposed to chlorine shows the presence of chloride species that confirms electron charge transfer from chlorine to CNTs. By contrast, the resistance of nitrogen-doped and PEI functionalized CNTs exposed to chlorine increases, in agreement with their n-type semiconductor nature. The best response is obtained using annealed CNTs and is attributed to their higher degree of crystallinity.

  8. Development of multi-walled carbon nanotubes reinforced monetite bionanocomposite cements for orthopedic applications

    International Nuclear Information System (INIS)

    Boroujeni, Nariman Mansoori; Zhou, Huan; Luchini, Timothy J.F.; Bhaduri, Sarit B.

    2013-01-01

    In this study, we present results of our research on biodegradable monetite (DCPA, CaHPO 4 ) cement with surface-modified multi-walled carbon nanotubes (mMWCNTs) as potential bone defect repair material. The cement pastes showed desirable handling properties and possessed a suitable setting time for use in surgical setting. The incorporation of mMWCNTs shortened the setting time of DCPA and increased the compressive strength of DCPA cement from 11.09 ± 1.85 MPa to 21.56 ± 2.47 MPa. The cytocompatibility of the materials was investigated in vitro using the preosteoblast cell line MC3T3-E1. An increase of cell numbers was observed on both DCPA and DCPA-mMWCNTs. Scanning electron microscopy (SEM) results also revealed an obvious cell growth on the surface of the cements. Based on these results, DCPA-mMWCNTs composite cements can be considered as potential bone defect repair materials. - Highlights: • A monetite bone cement for orthopedic applications is reported. • Incorporation of MWCNTs into monetite bone cement is discussed. • Surface functionalized MWCNTs can improve the mechanical strength of monetite cement. • MWCNTs have no impacts on the cytocompatibility of monetite cements

  9. Development of multi-walled carbon nanotubes reinforced monetite bionanocomposite cements for orthopedic applications

    Energy Technology Data Exchange (ETDEWEB)

    Boroujeni, Nariman Mansoori [Department of Mechanical, Industrial and Manufacturing Engineering, The University of Toledo, Toledo, OH (United States); Zhou, Huan, E-mail: Huan.Zhou@Rockets.utoledo.edu [Department of Mechanical, Industrial and Manufacturing Engineering, The University of Toledo, Toledo, OH (United States); Luchini, Timothy J.F. [Department of Mechanical, Industrial and Manufacturing Engineering, The University of Toledo, Toledo, OH (United States); Bhaduri, Sarit B. [Department of Mechanical, Industrial and Manufacturing Engineering, The University of Toledo, Toledo, OH (United States); Division of Dentistry, The University of Toledo, Toledo, OH (United States)

    2013-10-15

    In this study, we present results of our research on biodegradable monetite (DCPA, CaHPO{sub 4}) cement with surface-modified multi-walled carbon nanotubes (mMWCNTs) as potential bone defect repair material. The cement pastes showed desirable handling properties and possessed a suitable setting time for use in surgical setting. The incorporation of mMWCNTs shortened the setting time of DCPA and increased the compressive strength of DCPA cement from 11.09 ± 1.85 MPa to 21.56 ± 2.47 MPa. The cytocompatibility of the materials was investigated in vitro using the preosteoblast cell line MC3T3-E1. An increase of cell numbers was observed on both DCPA and DCPA-mMWCNTs. Scanning electron microscopy (SEM) results also revealed an obvious cell growth on the surface of the cements. Based on these results, DCPA-mMWCNTs composite cements can be considered as potential bone defect repair materials. - Highlights: • A monetite bone cement for orthopedic applications is reported. • Incorporation of MWCNTs into monetite bone cement is discussed. • Surface functionalized MWCNTs can improve the mechanical strength of monetite cement. • MWCNTs have no impacts on the cytocompatibility of monetite cements.

  10. Bilirubin oxidase bound to multi-walled carbon nanotube-modified gold

    International Nuclear Information System (INIS)

    Schubert, Kirsten; Goebel, Gero; Lisdat, Fred

    2009-01-01

    We report on direct electron transfer (DET) reactions of bilirubin oxidase at multi-walled carbon nanotube-(MWCNT) modified gold electrodes. MWCNTs are very suitable for protein immobilisation and provide surface groups that can be used for the stable fixation on electrodes. They can also effectively replace the natural substrate of BOD - bilirubin, the electron donor for oxygen reduction. The bioelectrocatalytic oxygen reduction was recorded using linear sweep voltammetry (LSV) with BOD covalently linked to the nanotubes. The start potential of the bioelectrocatalytic oxygen reduction at pH 7 and a scan rate of 10 mV/s was determined to be 485 ± 10 mV vs. Ag/AgCl, 1 M KCl (720 mV vs. SHE). Current densities up to 500 μA/cm 2 were detected in an air-saturated buffer at room temperature (25 ± 5 deg. C). Experiments with a rotating disk electrode (RDE) indicate a diffusion controlled electrode reaction. A k s value in the range of 80-100 s -1 could be estimated. The DET could also be observed directly by the redox conversion of a copper centre of BOD under anaerobic conditions. A peak pair with a formal potential of 680 ± 10 mV vs. SHE was found. The T1 site is probably addressed by the electrode as indicated by several experimental studies

  11. Adsorption of ionizable organic contaminants on multi-walled carbon nanotubes with different oxygen contents

    International Nuclear Information System (INIS)

    Li Xiaona; Zhao Huimin; Quan Xie; Chen Shuo; Zhang Yaobin; Yu Hongtao

    2011-01-01

    Multi-walled carbon nanotubes (MWNTs), which are considered to be promising candidates for the adsorption of toxic organics, are released into aqueous environment with their increasing production and application. In this study, the adsorption behaviors of five structurally related ionizable organic contaminants namely perfluorooctane sulfonate (PFOS), perfluorooctanoic acid (PFOA), perfluorooctanesulfonamide (PFOSA), 2,4-dichlorophenoxyacetic acid (2,4-D) and 4-n-nonylphenol (4-NP) onto MWNTs with different oxygen contents (3.84-22.85%) were investigated. The adsorption kinetics was investigated and simulated with pseudo-second-order model. The adsorption isotherms were found to be fitted with Freundlich model and influenced by both the properties of organic chemicals and the oxygen contents of MWNTs. As adsorption capacity decreases dramatically with the increasing of oxygen contents, the MWNTs with the lowest oxygen contents possess the highest adsorption capacity among four MWNTs. For the MWNTs with the oxygen contents of 3.84%, the adsorption affinity related with hydrophobic interaction and π-electron polarizability decreased in the order of 4-NP > PFOSA > PFOS > 2,4-D > PFOA. Furthermore, the adsorption characters of five contaminants were affected by solution pH and solute pK a considering electrostatic repulse force and hydrogen bonding, which showed the adsorption of MWNTs with lower oxygen content is much sensitive to solution chemistry.

  12. Polyindole/ carboxylated-multiwall carbon nanotube composites produced by in-situ and interfacial polymerization

    International Nuclear Information System (INIS)

    Joshi, Leela; Singh, Arun Kumar; Prakash, Rajiv

    2012-01-01

    Composites of polyindole (PIn), a conducting polymer, with carboxylated-multiwalled carbon nanotubes (c-MWCNT/PIn) were synthesized; the synthesis was done using (i) two miscible solvents (in-situ method) and (ii) two immiscible solvents (interfacial method). A tubular composite, with a uniform coating of the polymer over c-MWCNTs, was observed in the case of interfacial synthesis. However, the in-situ synthesis of c-MWCNT/PIn composites exhibited a densely packed spherical morphology, with c-MWCNT incorporated within the polymer spheres. The spherical morphology was probably obtained due to fast polymerization kinetics and the formation of micelles in case of in-situ polymerization, whereas tubular morphology was obtained in case of interfacial polymerization due to the sufficient time provided for the growth of polymer chains over the c-MWCNT surfaces. Nanoscale electrical properties of composites, in a metal/(c-MWCNT/PIn) configuration, were studied using current sensing atomic force microscopy. Interfacial c-MWCNT/PIn composite, on Al metal substrate, exhibited a typical rectifying diode behavior. This composite had manifested enormous potential for electronic applications and fabrication of nanoscale organic devices. Highlights: ► Polyindole/c-MWNT nanocomposites produced by in-situ and interfacial polymerization. ► Densely packed spherical morphology was observed in in-situ polymerization route. ► Tubular core-shell morphology was observed in interfacial polymerization route. ► Interfacial nanocomposite manifested a nano-schottky junction with Al metal.

  13. Optical properties of ordered vertical arrays of multi-walled carbon nanotubes from FDTD simulations.

    Science.gov (United States)

    Bao, Hua; Ruan, Xiulin; Fisher, Timothy S

    2010-03-15

    A finite-difference time-domain (FDTD) method is used to model thermal radiative properties of vertical arrays of multi-walled carbon nanotubes (MWCNT). Individual CNTs are treated as solid circular cylinders with an effective dielectric tensor. Consistent with experiments, the results confirm that CNT arrays are highly absorptive. Compared with the commonly used Maxwell-Garnett theory, the FDTD calculations generally predict larger reflectance and absorbance, and smaller transmittance, which are attributed to the diffraction and scattering within the cylinder array structure. The effects of volume fraction, tube length, tube distance, and incident angle on radiative properties are investigated systematically. Low volume fraction and long tubes are more favorable to achieve low reflectance and high absorbance. For a fixed volume fraction and finite tube length, larger periodicity results in larger reflectance and absorbance. The angular dependence studies reveal an optimum incident angle at which the reflectance can be minimized. The results also suggest that an even darker material could be achieved by using CNTs with good alignment on the top surface.

  14. Size response of an SMPS-APS system to commercial multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    Lee, Seung-Bok; Lee, Jun-Hyun; Bae, Gwi-Nam

    2010-01-01

    Carbon nanotubes (CNTs) are representative-engineered nanomaterials with unique properties. The safe production of CNTs urgently requires reliable tools to assess inhalation exposure. In this study, on-line aerosol instruments were employed to detect the release of multi-walled CNTs (MWCNTs) in workplace environments. The size responses of aerosol instruments consisting of both a scanning mobility particle sizer (SMPS) and an aerodynamic particle sizer (APS) were examined using five types of commercial MWCNTs. A MWCNT solution and powder were aerosolized using atomizing and shaking methods, respectively. Regardless of the phase and purity, the aerosolized MWCNTs showed consistent size distributions with both SMPS and APS. The SMPS and APS measurements revealed a dominant broad peak at approximately 200-400 nm and a distinct narrow peak at approximately 2 μm, respectively. Comparing with field application of the two aerosol instruments, the APS response could be a fingerprint of the MWCNTs in a real workplace environment. A modification of the atomizing method is recommended for the long-term inhalation toxicity studies.

  15. Comparison of Electronic Structure and Magnetic Properties of Few Layer Graphene and Multiwall Carbon Nanotubes

    Directory of Open Access Journals (Sweden)

    Sekhar Chandra Ray

    2016-01-01

    Full Text Available A comparative study has been made for the non-catalyst based few layer graphene (FLG and Fe-catalyst based multiwall carbon nanotubes (MWCNTs. Magnetic and electronic properties of FLG and MWCNTs were studied using magnetic M-H hysteresis loops and synchrotron radiation based X-ray absorption fine structure spectroscopy measurements. Structural defects and electronic and bonding properties of FLG/MWCNTs have been studied using Raman spectroscopy, X-ray photoelectron spectroscopy (XPS, and ultraviolet photoelectron spectroscopy (UPS. The work functions of FLG and MWCNTs are 4.01 eV and 3.79 eV, respectively, obtained from UPS (He-I spectra. UPS (He-II results suggest that the density of states (DOS of MWCNTs is higher than FLG and is consistent with Raman spectroscopy result that shows the defect of MWCNTs is higher than FLG. The magnetic coercivity (Hc of the MWCNTs (~750 Oe is higher than FLG (~85 Oe which could be used for various technological magnetic applications.

  16. Toxicity of multi-walled carbon nanotubes, graphene oxide, and reduced graphene oxide to zebrafish embryos.

    Science.gov (United States)

    Liu, Xiao Tong; Mu, Xi Yan; Wu, Xiao Li; Meng, Li Xuan; Guan, Wen Bi; Ma, Yong Qiang; Sun, Hua; Wang, Cheng Ju; Li, Xue Feng

    2014-09-01

    This study was aimed to investigate the toxic effects of 3 nanomaterials, i.e. multi-walled carbon nanotubes (MWCNTs), graphene oxide (GO), and reduced graphene oxide (RGO), on zebrafish embryos. The 2-h post-fertilization (hpf) zebrafish embryos were exposed to MWCNTs, GO, and RGO at different concentrations (1, 5, 10, 50, 100 mg/L) for 96 h. Afterwards, the effects of the 3 nanomateria on spontaneous movement, heart rate, hatching rate, length of larvae, mortality, and malformations ls were evaluated. Statistical analysis indicated that RGO significantly inhibited the hatching of zebrafish embryos. Furthermore, RGO and MWCNTs decreased the length of the hatched larvae at 96 hpf. No obvious morphological malformation or mortality was observed in the zebrafish embryos after exposure to the three nanomaterials. MWCNTs, GO, and RGO were all toxic to zebrafish embryos to influence embryos hatching and larvae length. Although no obvious morphological malformation and mortality were observed in exposed zebrafish embryos, further studies on the toxicity of the three nanomaterials are still needed. Copyright © 2014 The Editorial Board of Biomedical and Environmental Sciences. Published by China CDC. All rights reserved.

  17. Investigating Linear and Nonlinear Viscoelastic behaviour and microstructures of Gelatine-Multiwalled carbon nanotubes composites

    KAUST Repository

    Yang, Zhi

    2015-12-01

    We have investigated the linear and nonlinear rheology of various gelatine-multiwalled carbon nanotube (gel-MWNT) composites, namely physically-crosslinked-gelatine gel-MWNT composites, chemically-crosslinked-gelatine gel-MWNT composites, and chemically-physically-crosslinked-gelatine gel-MWNT composites. Further, the internal structures of these gel-MWNT composites were characterized by ultra-small angle neutron scattering and scanning electron microscopy. The adsorption of gelatine onto the surface of MWNT is also investigated to understand gelatine-assisted dispersion of MWNT during ultrasonication. For all gelatine gels, addition of MWNT increases their complex modulus. The dependence of storage modulus with frequency for gelatine-MWNT composites is similar to that of the corresponding neat gelatine matrix. However, by incorporating MWNT, the dependence of the loss modulus on frequency is reduced. The linear viscoelastic region is decreased approximately linearly with the increase of MWNT concentration. The pre-stress results demonstrate that the addition of MWNT does not change the strain-hardening behaviour of physically-crosslinked gelatine gel. However, the addition of MWNT can increase the strain-hardening behaviour of chemically-crosslinked gelatine gel, and chemically-physically crosslinked gelatine gel. Results from light microscopy, cryo-SEM, and USANS demonstrate the hierarchical structures of MWNT, including that tens-of-micron scale MWNT agglomerates are present. Furthermore, the adsorption curve of gelatine onto the surface of MWNT follows two-stage pseudo-saturation behaviour.

  18. Preparation and characterization of bagasse/HDPE composites using multi-walled carbon nanotubes.

    Science.gov (United States)

    Ashori, Alireza; Sheshmani, Shabnam; Farhani, Foad

    2013-01-30

    This article presents the preparation and characterization of bagasse/high density polyethylene (HDPE) composites. The effects of multi-walled carbon nanotubes (MWCNTs), as reinforcing agent, on the mechanical and physical properties were also investigated. In order to increase the interphase adhesion, maleic anhydride grafted polyethylene (MAPE) was added as a coupling agent to all the composites studied. In the sample preparation, MWCNTs and MAPE contents were used as variable factors. The morphology of the specimens was characterized using scanning electron microscopy (SEM) technique. The results of strength measurement indicated that when 1.5 wt% MWCNTs were added, tensile and flexural properties reached their maximum values. At high level of MWCNTs loading (3 or 4 wt%), increased population of MWCNTs lead to agglomeration and stress transfer gets blocked. The addition of MWCNTs filler slightly decreased the impact strength of composites. Both mechanical and physical properties were improved when 4 wt% MAPE was applied. SEM micrographs also showed that the surface roughness improved with increasing MAPE loading from 0 to 4 wt%. The improvement of physicomechanical properties of composites confirmed that MWCNTs have good reinforcement and the optimum synergistic effect of MWCNTs and MAPE was achieved at the combination of 1.5 and 4 wt%, respectively. Copyright © 2012 Elsevier Ltd. All rights reserved.

  19. Mass-produced multi-walled carbon nanotubes as catalyst supports for direct methanol fuel cells.

    Science.gov (United States)

    Jang, In Young; Park, Ki Chul; Jung, Yong Chae; Lee, Sun Hyung; Song, Sung Moo; Muramatsu, Hiroyuki; Kim, Yong Jung; Endo, Morinobu

    2011-01-01

    Commercially mass-produced multi-walled carbon nanotubes, i.e., VGNF (Showa Denko Co.), were applied to support materials for platinum-ruthenium (PtRu) nanoparticles as anode catalysts for direct methanol fuel cells. The original VGNFs are composed of high-crystalline graphitic shells, which hinder the favorable surface deposition of the PtRu nanoparticles that are formed via borohydride reduction. The chemical treatment of VGNFs with potassium hydroxide (KOH), however, enables highly dispersed and dense deposition of PtRu nanoparticles on the VGNF surface. This capability becomes more remarkable depending on the KOH amount. The electrochemical evaluation of the PtRu-deposited VGNF catalysts showed enhanced active surface areas and methanol oxidation, due to the high dispersion and dense deposition of the PtRu nanoparticles. The improvement of the surface deposition states of the PtRu nanoparticles was significantly due to the high surface area and mesorporous surface structure of the KOH-activated VGNFs.

  20. Multi-walled carbon nanotubes can enhance root elongation of wheat (Triticum aestivum) plants

    International Nuclear Information System (INIS)

    Wang Xiuping; Han Heyou; Liu Xueqin; Gu Xiaoxu; Chen Kun; Lu Donglian

    2012-01-01

    The potential effects of oxidized multi-walled carbon nanotubes (o-MWCNTs) with a length ranging from 50 to 630 nm on the development and physiology of wheat plants were evaluated by examining their effects on seed germination, root elongation, stem length, and vegetative biomass at a concentration ranging from 10 to 160 μg/mL in the plant. Results indicated that after 7 days of exposure to the o-MWCNTs medium, faster root growth and higher vegetative biomass were observed, but seed germination and stem length did not show any difference as compared with controls. Moreover, a physiological study was conducted at cellular level using a traditional physiological approach to evidence the possible alterations in morphology, the cell length of root zone, and the dehydrogenase activity of seedlings. Transmission electron microscopy images revealed that o-MWCNTs could penetrate the cell wall and enter the cytoplasm after being taken up by roots. The cell length of root zone for the seedlings germinated and grown in the o-MWCNTs (80 μg/mL) medium increased by 1.4-fold and a significant concentration-dependent increase in the dehydrogenase activity for the o-MWCNT-treated wheat seedlings was detected. These findings suggest that o-MWCNTs can significantly promote cell elongation in the root system and increase the dehydrogenase activity, resulting in faster root growth and higher biomass production.

  1. Synthesis and properties of platinum on multiwall carbon nanotube modified by chitosan

    Science.gov (United States)

    Fikriyyah, A. K.; Chaldun, E. R.; Indriyati

    2018-03-01

    Platinum nanoparticles on multiwall carbon nanotubes (Pt/MWCNT) play an important role in fuel cell to convert the chemical energy from a fuel into electricity. In this study, Pt/MWCNT electrocatalysts were prepared by chemical reduction of the metal salts in chitosan as the support. Firstly, commercial MWCNTs were functionalized by oxidative process using a mixture of nitric acid and sulfuric acid. Then, functionalized MWCNTs were mixed with chitosan-acetic acid solution to conduct grafting reaction with NH2 groups in chitosan by solution polymerization method. Platinum nanoparticles were loaded onto the surface of the MWCNTs after hexachloroplatinic acid was reduced by sodium hydroxide solution. The result showed that Pt was attached on MWCNT based on analysis from EDS, XRD, and UV Vis Spectroscopy. UV Vis analysis indicates the plasmon absorbance band of Pt nanoparticles in Pt/MWCNT, while XRD analysis confirmed the size of Pt particle in nanometer. This elucidates the potential procedure to synthesize Pt/MWCNT using chitosan.

  2. Structure and Properties of Multiwall Carbon Nanotubes/Polystyrene Composites Prepared via Coagulation Precipitation Technique

    Directory of Open Access Journals (Sweden)

    I. N. Mazov

    2011-01-01

    Full Text Available Coagulation technique was applied for preparation of multiwall carbon nanotube- (MWNT-containing polystyrene (PSt composite materials with different MWNT loading (0.5–10 wt.%. Scanning and transmission electron microscopies were used for investigation of the morphology and structure of produced composites. It was shown that synthesis of MWNT/PSt composites using coagulation technique allows one to obtain high dispersion degree of MWNT in the polymer matrix. According to microscopy data, composite powder consists of the polystyrene matrix forming spherical particles with diameter ca. 100–200 nm, and the surface of MWNT is strongly wetted by the polymer forming thin layer with 5–10 nm thickness. Electrical conductivity of MWNT/PSt composites was investigated using a four-probe technique. Observed electrical percolation threshold of composite materials is near to 10 wt.%, mainly due to the insulating polymer layer deposited on the surface of nanotubes. Electromagnetic response of prepared materials was investigated in broadband region (0.01–4 and 26–36 GHz. It was found that MWNT/PSt composites are almost radiotransparent for low frequency region and possess high absorbance of EM radiation at higher frequencies.

  3. Adsorption of triazine herbicides from aqueous solution by functionalized multiwall carbon nanotubes grown on silicon substrate

    Science.gov (United States)

    D'Archivio, Angelo Antonio; Maggi, Maria Anna; Odoardi, Antonella; Santucci, Sandro; Passacantando, Maurizio

    2018-02-01

    Multi-walled carbon nanotubes (MWCNTs), because of their small size and large available surface area, are potentially efficient sorbents for the extraction of water solutes. Dispersion of MWCNTs in aqueous medium is suitable to adsorb organic contaminants from small sample volumes, but, the recovery of the suspended sorbent for successive re-use represents a critical step, which makes this method inapplicable in large-scale water-treatment technologies. To overcome this problem, we proposed here MWCNTs grown on silicon supports and investigated on a small-volume scale their adsorption properties towards triazine herbicides dissolved in water. The adsorption efficiency of the supported MWCNTs has been tested on seven triazine herbicides, which are emerging water contaminants in Europe and USA, because of their massive use, persistence in soils and potential risks for the aquatic organisms and human health. The investigated compounds, in spite of their common molecular skeleton, cover a relatively large property range in terms of both solubility in water and hydrophilicity/hydrophobicity. The functionalisation of MWCNTs carried out by acidic oxidation, apart from increasing wettability of the material, results in a better adsorption performance. Increasing of functionalisation time between 17 and 60 h progressively increases the extraction of all seven pesticides and produces a moderate increment of selectivity.

  4. Comprehensive spectroscopic studies on the interaction of biomolecules with surfactant detached multi-walled carbon nanotubes.

    Science.gov (United States)

    Sekar, Gajalakshmi; Mukherjee, Amitava; Chandrasekaran, Natarajan

    2015-04-01

    This paper investigates the interaction of ten diverse biomolecules with surfactant detached Multi-Walled Carbon Nanotubes (MWCNTs) using multiple spectroscopic methods. Declining fluorescence intensity of biomolecules in combination with the hyperchromic effect in UV-Visible spectra confirmed the existence of the ground state complex formation. Quenching mechanism remains static and non-fluorescent. 3D spectral data of biomolecules suggested the possibilities of disturbances to the aromatic microenvironment of tryptophan and tyrosine residues arising out of CNTs interaction. Amide band Shifts corresponding to the secondary structure of biomolecules were observed in the of FTIR and FT-Raman spectra. In addition, there exists an increased Raman intensity of tryptophan residues of biomolecules upon interaction with CNTs. Hence, the binding of the aromatic structures of CNTs with the aromatic amino acid residues, in a particular, tryptophan was evidenced. Far UV Circular spectra have showed the loss of alpha-helical contents in biomolecules upon interaction with CNTs. Near UV CD spectra confirmed the alterations in the tryptophan positions of the peptide backbone. Hence, our results have demonstrated that the interaction of biomolecules with OH-MWCNTs would involve binding cum structural changes and alteration to their aromatic micro-environment. Copyright © 2015 Elsevier B.V. All rights reserved.

  5. Fluorescence spectrometry of the interaction of multi-walled carbon nanotubes with catalase

    International Nuclear Information System (INIS)

    Fan, Y.; Cai, H.; Miao, J.; Yang, Q.; Li, Y.; Li, J.; Fu, D.

    2014-01-01

    The interaction of multi-walled carbon nanotubes (MWCNTs) with catalase is investigated using fluorescence and circular dichroism spectroscopic techniques. The results of the fluorescence experiments suggest that MWCNTs quench the intrinsic fluorescence of catalase via a static quenching mechanism. The circular dichroism spectral results reveal the unfolding of catalase with a significant decrease in the α-helix content in the presence of MWCNTs, which indicates that the conformation of catalase is changed in the binding process, thereby remarkably decreasing its activity. The binding constants and the number of binding sites of the MWCNT to the catalase are calculated at different temperatures. The thermodynamic parameters, such as the changes in free energy (ΔG), enthalpy (ΔH), and entropy (ΔS), are calculated using thermodynamic equations. The fact that all negative values of ΔG, ΔH, and ΔS are obtained suggests that the interaction of the MWCNTs with catalase is spontaneous, and that hydrogen bonding and van der Waals interactions play an important role in the binding process. (authors)

  6. Temperature effects on the nitric acid oxidation of industrial grade multiwalled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Andrade, Nadia F., E-mail: nadia@fisica.ufc.br [Universidade Federal do Ceara, Departamento de Fisica (Brazil); Martinez, Diego Stefani T., E-mail: diegostefani.br@gmail.com; Paula, Amauri J., E-mail: amaurijp@gmail.com [Universidade Estadual de Campinas (UNICAMP), Laboratorio de Quimica do Estado Solido (LQES), Instituto de Quimica (Brazil); Silveira, Jose V. [Universidade Federal do Ceara, Departamento de Fisica (Brazil); Alves, Oswaldo L., E-mail: oalves@iqm.unicamp.br [Universidade Estadual de Campinas (UNICAMP), Laboratorio de Quimica do Estado Solido (LQES), Instituto de Quimica (Brazil); Souza Filho, Antonio G., E-mail: agsf@fisica.ufc.br [Universidade Federal do Ceara, Departamento de Fisica (Brazil)

    2013-07-15

    In this study, we report an oxidative treatment of multiwalled carbon nanotubes (MWCNTs) by using nitric acid at different temperatures (25-175 Degree-Sign C). The analyzed materials have diameters varying from 10 to 40 nm and majority lengths between 3 and 6 {mu}m. The characterization results obtained by different techniques (e.g., field emission scanning electron microscopy, thermogravimetric analysis, energy-filtered transmission electron microscopy, Braunauer, Emmet and Teller method, {zeta}-potential and confocal Raman spectroscopy) allowed us to access the effects of temperature treatment on the relevant physico-chemical properties of the MWCNTs samples studied in view of an integrated perspective to use these samples in a bio-toxicological context. Analytical microbalance measurements were used to access the purity of samples (metallic residue) after thermogravimetric analysis. Confocal Raman spectroscopy measurements were used to evaluate the density of structural defects created on the surface of the tubes due to the oxidation process by using 2D Raman image. Finally, we have demonstrated that temperature is an important parameter in the generation of oxidation debris (a byproduct which has not been properly taken into account in the literature) in the industrial grade MWCNTs studied after nitric acid purification and functionalization.

  7. Unusual electrochemical response of ZnO nanowires-decorated multiwalled carbon nanotubes

    International Nuclear Information System (INIS)

    Mo Guangquan; Ye Jianshan; Zhang Weide

    2009-01-01

    A novel type of ZnO nanowires-modified multiwalled carbon nanotubes (MWCNTs) nanocomposite (ZnO-NWs/MWCNTs) has been prepared by a hydrothermal process. The ZnO-NWs/MWCNTs nanocomposite has a uniform surface distribution and large coverage of ZnO nanowires onto MWCNTs with 3D configuration, which was characterized by scanning electron microscopy. Cyclic voltammetry and electrochemical impedance spectroscopy methods were applied to investigate the electrochemical properties of ZnO-NWs/MWCNTs nanocomposite. Surprisingly, unlike the conventional n-type semiconducting ZnO nanowires grown on Ta substrate, the ZnO-NWs/MWCNTs nanocomposite exhibits excellent electron transfer capability and gives a pair of well-defined symmetric redox peaks towards ferricyanide probe. What's more, the ZnO-NWs/MWCNTs nanocomposite shows remarkable electrocatalytic activity (current response increased 4 folds at 0.3 V) towards H 2 O 2 by comparing with bare MWCNTs. The ZnO-NWs/MWCNTs nanocomposite could find applications in novel biosensors and other electronic devices.

  8. Mechanical Properties and Durability of Ultra High Strength Concrete Incorporating Multi-Walled Carbon Nanotubes.

    Science.gov (United States)

    Lu, Liulei; Ouyang, Dong; Xu, Weiting

    2016-05-27

    In this work, the effect of the addition of multi-walled carbon nanotubes (MWCNTs) on the mechanical properties and durability of ultra high strength concrete (UHSC) is reported. First, the MWCNTs were dispersed by a nano sand-mill in the presence of a surfactant in water. The UHSC specimens were prepared with various amounts of MWCNTs, ranging from 0% to 0.15% by weight of cement (bwoc). Results indicated that use of an optimal percentage of MWCNTs (0.05% bwoc) caused a 4.63% increase in compressive strength and a 24.0% decrease in chloride diffusion coefficient of UHSC at 28 days curing. Moreover, the addition of MWCNTs also improved the flexural strength and deformation ability. Furthermore, a field-emission scanning electron microscopy (FE-SEM) was used to observe the dispersion of MWCNTs in the cement matrix and morphology of the hardened cement paste containing MWCNTs. FE-SEM observation revealed that MWCNTs were well dispersed in the matrix and no agglomerate was found and the reinforcing effect of MWCNTs on UHSC was thought to be pulling out and microcrack bridging of MWCNTs, which transferred the load in tension.

  9. Electromechanical Behavior of Chemically Reduced Graphene Oxide and Multi-walled Carbon Nanotube Hybrid Material

    Science.gov (United States)

    Benchirouf, Abderrahmane; Müller, Christian; Kanoun, Olfa

    2016-01-01

    In this paper, we propose strain-sensitive thin films based on chemically reduced graphene oxide (GO) and multi-walled carbon nanotubes (MWCNTs) without adding any further surfactants. In spite of the insulating properties of the thin-film-based GO due to the presence functional groups such as hydroxyl, epoxy, and carbonyl groups in its atomic structure, a significant enhancement of the film conductivity was reached by chemical reduction with hydro-iodic acid. By optimizing the MWCNT content, a significant improvement of electrical and mechanical thin film sensitivity is realized. The optical properties and the morphology of the prepared thin films were studied using ultraviolet-visible spectroscopy (UV-Vis) and scanning electron microscope (SEM). The UV-Vis spectra showed the ability to tune the band gap of the GO by changing the MWCNT content, whereas the SEM indicated that the MWCNTs were well dissolved and coated by the GO. Investigations of the piezoresistive properties of the hybrid nanocomposite material under mechanical load show a linear trend between the electrical resistance and the applied strain. A relatively high gauge factor of 8.5 is reached compared to the commercial metallic strain gauges. The self-assembled hybrid films exhibit outstanding properties in electric conductivity, mechanical strength, and strain sensitivity, which provide a high potential for use in strain-sensing applications.

  10. Structure and composition of single Pt–Ru electrocatalyst nanoparticles supported on multiwall carbon nanotubes

    International Nuclear Information System (INIS)

    Paraguay-Delgado, Francisco; Malac, Marek; Alonso-Nuñez, Gabriel

    2014-01-01

    Individual Pt-Ru nanoparticles (NPs) supported on multiwall carbon nanotubes (MWCNTs) synthesized by microemulsion method were characterized by nano beam diffraction (NBD) and high resolution imaging in transmission electron microscopy (TEM). Comparing the TEM images and NBD to simulations provided insight into particle composition, structure and morphology in three dimensions. In particular, the NBD allowed us to detect various components of the individual NPs that would be difficult to observe otherwise. We find that the NPs contain four different components: Pt–RuO 2 , Pt–Ru, RuO 2 and metallic Pt. Often an individual NP is composed of more than one component. The most frequently encountered external morphology is close to a spherical shape and ∼3.7 nm in diameter. The collective properties of NPs’ assemblies were studied by thermogravimetry, differential thermal analysis and x-ray diffraction. The results allowed us to gain some insight into the relation of the NPs’ structure and composition with their catalytic performance, and revealed the presence of components not detectable by bulk methods. The electrocatalytic properties were evaluated by CO stripping, methanol oxidation and oxygen reduction. Bulk characterization methods miss many properties and structures present in the sample due to low volume fraction and due to overlap of reflections. Single NPs should be analyzed to obtain reliable indication of sample composition. (paper)

  11. Rheological and mechanical properties of polypropylene prepared with multi-walled carbon nanotube masterbatch.

    Science.gov (United States)

    Shim, Young-Sun; Park, Soo-Jin

    2012-07-01

    In this study, the effects of polypropylene-grafted maleic-anhydride-treated multi-walled carbon nanotubes (PP-MWNTs) on the viscoelastic behaviors and mechanical properties of a polypropylene-(PP)-based composite system were examined. The PP-MWNT/PP composites were prepared via melt mixing with a 3:1 ratio of PP-g-MA and acid-treated MWNTs at 220 degrees C. The surface characteristics of the PP-MWNTs were confirmed via Fourier transform infrared (FTIR) spectroscopy and transmission electron microscopy (TEM). The viscoelastic behavior and mechanical properties of the PP-MWNT/PP composites were confirmed using a rheometer and an ultimate testing machine (UTM). The storage and loss moduli increased with increasing PP-MWNT content. The critical intensity stress factor (K(IC)) of the PP-MWNT/PP composites at high filler loading was also higher than that of the MWNT/PP composites. In conclusion, the viscoelastic behavior and mechanical properties of MWNT/PP can be improved by grafting MWNTs to PP-g-MA.

  12. A comparative study of enzyme immobilization strategies for multi-walled carbon nanotube glucose biosensors

    Science.gov (United States)

    Shi, Jin; Claussen, Jonathan C.; McLamore, Eric S.; Haque, Aeraj ul; Jaroch, David; Diggs, Alfred R.; Calvo-Marzal, Percy; Rickus, Jenna L.; Porterfield, D. Marshall

    2011-09-01

    This work addresses the comparison of different strategies for improving biosensor performance using nanomaterials. Glucose biosensors based on commonly applied enzyme immobilization approaches, including sol-gel encapsulation approaches and glutaraldehyde cross-linking strategies, were studied in the presence and absence of multi-walled carbon nanotubes (MWNTs). Although direct comparison of design parameters such as linear range and sensitivity is intuitive, this comparison alone is not an accurate indicator of biosensor efficacy, due to the wide range of electrodes and nanomaterials available for use in current biosensor designs. We proposed a comparative protocol which considers both the active area available for transduction following nanomaterial deposition and the sensitivity. Based on the protocol, when no nanomaterials were involved, TEOS/GOx biosensors exhibited the highest efficacy, followed by BSA/GA/GOx and TMOS/GOx biosensors. A novel biosensor containing carboxylated MWNTs modified with glucose oxidase and an overlying TMOS layer demonstrated optimum efficacy in terms of enhanced current density (18.3 ± 0.5 µA mM - 1 cm - 2), linear range (0.0037-12 mM), detection limit (3.7 µM), coefficient of variation (2%), response time (less than 8 s), and stability/selectivity/reproducibility. H2O2 response tests demonstrated that the most possible reason for the performance enhancement was an increased enzyme loading. This design is an excellent platform for versatile biosensing applications.

  13. Sorption of humic acid to functionalized multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    Wang, Fei; Yao, Jun; Chen, Huilun; Yi, Zhengji; Xing, Baoshan

    2013-01-01

    The environmental behavior of carbon nanotubes (CNTs) and humic acid (HA) is a prominent concern, but effect of functionalities on their sorption is not clear yet. Functionalized multi-walled CNTs (MCNT15) and HA were used to study their sorption behavior. Sorption rate of HA to MCNTs was dominantly controlled by its diffusion from liquid-MCNT boundary to MCNT surfaces. The sorption is in the sequence of MCNT15 > MCNT15-NH 2 > MCNT15-OH > MCNT15-COOH > MCNT15-Ni, which was dependent on their surface area and meso- and macro-pore volume. The functionalities of MCNTs regulated the sorption by affecting their interaction mechanisms (i.e., H-bonding, π–π, and hydrophobic interaction). Additionally, the amount of these functionalities on the MCNT surface reduced indirectly the sorption sites due to the steric hindrance. Electrostatic repulsion deceased the sorption of HA by MCNTs with increasing pH. This study demonstrated the importance of functionalities on the MCNTs for the sorption of HA. -- Highlights: •HA sorption kinetics was well fitted using Lagergren pseudo second-order model. •Sorption rate of HA was controlled by diffusion from liquid-MCNT boundary to MCNT surfaces. •Sorption was dependent on their surface area and meso- and macro-pore volume. •Functionalities of MCNTs regulated the sorption by affecting interaction mechanisms. -- The functionalities of MCNTs regulated the sorption behavior between MCNTs and HA

  14. Milling and dispersion of multi-walled carbon nanotubes in texanol

    Science.gov (United States)

    Darsono, Nono; Yoon, Dang-Hyok; Kim, Jaemyung

    2008-03-01

    Rheological results were used to determine the optimum type of dispersant and its concentration for six commercial dispersants for the dispersion of multi-walled carbon nanotube (MWCNT) agglomerates in texanol. An unsaturated polycarboxylic acid copolymer (BYK P-104) exhibited the optimum performance with the lowest MWCNT slurry viscosity in texanol. The cutting and dispersion efficiencies of MWCNTs with 20 wt.% of BYK P-104 dispersant were compared using conventional ball milling and high energy milling, whereby the latter was found to be more effective. High energy milling for 2 h produced a large portion of MWCNT agglomerates smaller than 150 nm, showing a drastic increase in slurry viscosity due to the dispersion into individual CNTs. On the other hand, 120 h ball milling was required to achieve the agglomerate size of 300 nm with less viscosity increase upon milling. Decrease in the degree of MWCNT crystallinity was observed by both milling, even though 2 h high energy milling showed slightly less damage than 120 h ball milling based on XRD and Raman spectroscopy results.

  15. Multi-walled carbon nanotube supported CdS-DETA nanocomposite for efficient visible light photocatalysis

    Energy Technology Data Exchange (ETDEWEB)

    Lv, Jiali; Li, Dongpei [College of Physics and Electronic Information, Anhui Key Laboratory of Energetic Materials, Huaibei Normal University, Huaibei, 235000 (China); Dai, Kai, E-mail: daikai940@chnu.edu.cn [College of Physics and Electronic Information, Anhui Key Laboratory of Energetic Materials, Huaibei Normal University, Huaibei, 235000 (China); Liang, Changhao, E-mail: chliang@issp.ac.cn [College of Physics and Electronic Information, Anhui Key Laboratory of Energetic Materials, Huaibei Normal University, Huaibei, 235000 (China); Key Laboratory of Materials Physics and Anhui Key Laboratory of Nanomaterials and Nanotechnology, Institute of Solid State Physics, Chinese Academy of Sciences, Hefei, 230031 (China); Jiang, Dequan [College of Physics and Electronic Information, Anhui Key Laboratory of Energetic Materials, Huaibei Normal University, Huaibei, 235000 (China); Lu, Luhua [Faculty of Material Science and Chemical Engineering, China University of Geosciences, Wuhan, 430074 (China); Zhu, Guangping [College of Physics and Electronic Information, Anhui Key Laboratory of Energetic Materials, Huaibei Normal University, Huaibei, 235000 (China)

    2017-01-15

    Designing high performance functional nanomaterials by tuning their dimension at nanoscale and constructing novel interface has been a hot topic in recent years. In this work, multi-walled carbon nanotube (MWCNT)/CdS-diethylenetriamine (DETA) composite photocatalyst was synthesized via hydrothermal method. The structure, morphology, optical property and core level analysis of MWCNT/CdS-DETA nanocomposite were characterized by X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), energy-dispersive X-ray spectroscopy spectra (EDS), UV–Vis diffuse reflectance spectroscopy (DRS) and X-ray photoelectron spectrum (XPS). CdS-DETA can be uniformly dispersed on the surface of MWCNT. Photocatalytic properties of as-prepared photocatalysts were investigated under 410 nm LED light irradiation for photodegradation of methylene bule (MB). The k{sub app} of MWCNT/CdS-DETA is 0.034 min{sup −1}, which is about 6 times more than pure CdS-DETA. Photostability test indicated that MWCNT/CdS-DETA hybrid can be reused for degradation of organic pollution, suggesting the possible application of MWCNT/CdS-DETA hybrid is the most promising strategy for advanced photocatalyst material design. - Highlights: • Novel MWCNT/CdS-DETA photocatalyst was prepared. • MWCNT/CdS-DETA showed high photocatalytic activity. • MWCNT/CdS-DETA showed long reusable life.

  16. Magneto-resistance of multiwall carbon nanotube Fermat yarn and coil yarn

    Science.gov (United States)

    Truong, Kieu; Kang, Haeyong; Lee, Yourack; Kim, Joong-Gyu; Lee, Young Hee; Suh, Dongseok; IBS CenterIntegrated Nanostructure Physics, InstituteBasic Science (IBS), SKKU, Korea Collaboration; Department of Energy Science, Sungkyunkwan University, Suwon 440-746, Korea Collaboration; Department of Physics, Sungkyunkwan University, Suwon 440-746, Korea Collaboration

    2015-03-01

    Multiwall carbon nanotube (MWCNT) based yarn has attracted a great attention for the development of multifunctional super-fiber due to its light weight, high flexibility, high conductivity, and strong mechanical properties (Lima et al. 2011, Science). Recently the importance of coiled yarn structure was demonstrated for practical applications (Haines et al. 2014, Science). In this study, we measured the electrical resistance of neat yarns and coiled yarns at different temperatures and magnetic fields. The coiled yarn was formed by twist-insertion into the neat yarn, and the transverse and longitudinal magnetoresistance (MR) measurements were carried out. The logarithmic temperature dependence of normalized resistance and the negative MR can be explained by the combined contribution of weak-localization effect and the tunneling transport at different temperature ranges. The magnitude difference of MR between two configurations and the survival of such difference even at room temperature indicate that one-dimensional transport features are quite significant in this system. Developing Route for sub-micrometer-scale coil is discussed. This work was supported by Project code (IBS - R011-D1).

  17. Electrical conductivity and electromagnetic interference shielding characteristics of multiwalled carbon nanotube filled polyacrylate composite films

    International Nuclear Information System (INIS)

    Li Yong; Chen Changxin; Zhang Song; Ni Yuwei; Huang Jie

    2008-01-01

    Multiwalled carbon nanotubes (MWCNTs) were homogeneously dispersed in pure acrylic emulsion by ultrasonication to prepare MWCNT/polyacrylate composites applied on building interior wall for electromagnetic interference (EMI) shielding applications. The structure and surface morphology of the MWCNTs and MWCNT/polyacrylate composites were studied by field emission scanning microscopy (FESEM) and transmission electron microscopy (TEM). The electrical conductivity at room temperature and EMI shielding effectiveness (SE) of the composite films on concrete substrate with different MWCNT loadings were investigated and the measurement of EMI SE was carried out in two different frequency ranges of 100-1000 MHz (radio frequency range) and 8.2-12.4 GHz (X-band). The experimental results show that a low mass concentration of MWCNTs could achieve a high conductivity and the EMI SE of the MWCNT/polyacrylate composite films has a strong dependence on MWCNTs content in both two frequency ranges. The SE is higher in X-band than that in radio frequency range. For the composite films with 10 wt.% MWCNTs, the EMI SE of experiment agrees well with that of theoretical prediction in far field

  18. Response of methane production via propionate oxidation to carboxylated multiwalled carbon nanotubes in paddy soil enrichments

    Directory of Open Access Journals (Sweden)

    Jianchao Zhang

    2018-01-01

    Full Text Available Carboxylated multiwalled carbon nanotubes (MWCNTs-COOH have become a growing concern in terms of their fate and toxicity in aqueous environments. Methane (CH4 is a major product of organic matter degradation in waterlogged environments. In this study, we determined the effect of MWCNTs-COOH on the production of CH4 from propionate oxidation in paddy soil enrichments. The results showed that the methanogenesis from propionate degradation was accelerated in the presence of MWCNTs-COOH. In addition, the rates of CH4 production and propionate degradation increased with increasing concentrations of MWCNTs-COOH. Scanning electron microscopy (SEM observations showed that the cells were intact and maintained their structure in the presence of MWCNTs-COOH. In addition, SEM and fluorescence in situ hybridization (FISH images revealed that the cells were in direct contact with the MWCNTs and formed cell-MWCNTs aggregates that contained both bacteria and archaea. On the other hand, nontoxic magnetite nanoparticles (Fe3O4 had similar effects on the CH4 production and cell integrity as the MWCNTs-COOH. Compared with no nanomaterial addition, the relative abundances of Geobacter and Methanosarcina species increased in the presence of MWCNTs-COOH. This study suggests that MWCNTs-COOH exerted positive rather than cytotoxic effects on the syntrophic oxidation of propionate in paddy soil enrichments and affected the bacterial and archaeal community structure at the test concentrations. These findings provide novel insight into the consequences of nanomaterial release into anoxic natural environments.

  19. Industrial compatible re-growth of vertically aligned multiwall carbon nanotubes by ultrafast pure oxygen purification process

    DEFF Research Database (Denmark)

    Bu, Ian Y.Y.; Hou, Kai; Engstrøm, Daniel Southcott

    2011-01-01

    amorphous carbon and reactivate nickel catalyst. Controlling of the purification temperature is important for high yield CNTs, as excessive high annealing temperature results in deformation of the CNTs. Unlike hazardous wet purification treatments, purified CNTs remained vertically aligned and offer......Reproducible high-yield purification process of multiwalled carbon nanotubes (CNTs) was developed by thermal annealing in ultrapure oxygen. The optimized condition involves thermal annealing via a PID controlled heater in high purity oxygen at temperature of 450°C for 180s, which burns out...

  20. Copper-Multiwall Carbon Nanotubes and Copper-Diamond Composites for Advanced Rocket Engines

    Science.gov (United States)

    Bhat, Biliyar N.; Ellis, Dave L.; Smelyanskiy, Vadim; Foygel, Michael; Rape, Aaron; Singh, Jogender; Vohra, Yogesh K.; Thomas, Vinoy; Otte, Kyle G.; Li, Deyu

    2013-01-01

    This paper reports on the research effort to improve the thermal conductivity of the copper-based alloy NARloy-Z (Cu-3 wt.%Ag-0.5 wt.% Zr), the state-of-the-art alloy used to make combustion chamber liners in regeneratively-cooled liquid rocket engines, using nanotechnology. The approach was to embed high thermal conductivity multiwall carbon nanotubes (MWCNTs) and diamond (D) particles in the NARloy-Z matrix using powder metallurgy techniques. The thermal conductivity of MWCNTs and D have been reported to be 5 to 10 times that of NARloy-Z. Hence, 10 to 20 vol. % MWCNT finely dispersed in NARloy-Z matrix could nearly double the thermal conductivity, provided there is a good thermal bond between MWCNTs and copper matrix. Quantum mechanics-based modeling showed that zirconium (Zr) in NARloy-Z should form ZrC at the MWCNT-Cu interface and provide a good thermal bond. In this study, NARloy-Z powder was blended with MWCNTs in a ball mill, and the resulting mixture was consolidated under high pressure and temperature using Field Assisted Sintering Technology (FAST). Microstructural analysis showed that the MWCNTs, which were provided as tangles of MWCNTs by the manufacturer, did not detangle well during blending and formed clumps at the prior particle boundaries. The composites made form these powders showed lower thermal conductivity than the base NARloy-Z. To eliminate the observed physical agglomeration, tangled multiwall MWCNTs were separated by acid treatment and electroless plated with a thin layer of chromium to keep them separated during further processing. Separately, the thermal conductivities of MWCNTs used in this work were measured, and the results showed very low values, a major factor in the low thermal conductivity of the composite. On the other hand, D particles embedded in NARloy-Z matrix showed much improved thermal conductivity. Elemental analysis showed migration of Zr to the NARloy-Z-D interface to form ZrC, which appeared to provide a low contact

  1. Copper Multiwall Carbon Nanotubes and Copper-Diamond Composites for Advanced Rocket Engines

    Science.gov (United States)

    Bhat, Biliyar N.; Ellis, Dave L.; Smelyanskiy, Vadim; Foygel, Michael; Singh, Jogender; Rape, Aaron; Vohra, Yogesh; Thomas, Vinoy; Li, Deyu; Otte, Kyle

    2013-01-01

    This paper reports on the research effort to improve the thermal conductivity of the copper-based alloy NARloy-Z (Cu-3 wt.%Ag-0.5 wt.% Zr), the state-of-the-art alloy used to make combustion chamber liners in regeneratively-cooled liquid rocket engines, using nanotechnology. The approach was to embed high thermal conductivity multiwall carbon nanotubes (MWCNTs) and diamond (D) particles in the NARloy-Z matrix using powder metallurgy techniques. The thermal conductivity of MWCNTs and D have been reported to be 5 to 10 times that of NARloy-Z. Hence, 10 to 20 vol. % MWCNT finely dispersed in NARloy-Z matrix could nearly double the thermal conductivity, provided there is a good thermal bond between MWCNTs and copper matrix. Quantum mechanics-based modeling showed that zirconium (Zr) in NARloy-Z should form ZrC at the MWCNT-Cu interface and provide a good thermal bond. In this study, NARloy-Z powder was blended with MWCNTs in a ball mill, and the resulting mixture was consolidated under high pressure and temperature using Field Assisted Sintering Technology (FAST). Microstructural analysis showed that the MWCNTs, which were provided as tangles of MWCNTs by the manufacturer, did not detangle well during blending and formed clumps at the prior particle boundaries. The composites made form these powders showed lower thermal conductivity than the base NARloy-Z. To eliminate the observed physical agglomeration, tangled multiwall MWCNTs were separated by acid treatment and electroless plated with a thin layer of chromium to keep them separated during further processing. Separately, the thermal conductivities of MWCNTs used in this work were measured, and the results showed very low values, a major factor in the low thermal conductivity of the composite. On the other hand, D particles embedded in NARloy-Z matrix showed much improved thermal conductivity. Elemental analysis showed migration of Zr to the NARloy-Z-D interface to form ZrC, which appeared to provide a low contact

  2. Heat dissipation for the Intel Core i5 processor using multiwalled carbon-nanotube-based ethylene glycol

    Energy Technology Data Exchange (ETDEWEB)

    Thang, Bui Hung; Trinh, Pham Van; Quang, Le Dinh; Khoi, Phan Hong; Minh, Phan Ngoc [Vietnam Academy of Science and Technology, Ho Chi Minh CIty (Viet Nam); Huong, Nguyen Thi [Hanoi University of Science, Hanoi (Viet Nam); Vietnam National University, Hanoi (Viet Nam)

    2014-08-15

    Carbon nanotubes (CNTs) are some of the most valuable materials with high thermal conductivity. The thermal conductivity of individual multiwalled carbon nanotubes (MWCNTs) grown by using chemical vapor deposition is 600 ± 100 Wm{sup -1}K{sup -1} compared with the thermal conductivity 419 Wm{sup -1}K{sup -1} of Ag. Carbon-nanotube-based liquids - a new class of nanomaterials, have shown many interesting properties and distinctive features offering potential in heat dissipation applications for electronic devices, such as computer microprocessor, high power LED, etc. In this work, a multiwalled carbon-nanotube-based liquid was made of well-dispersed hydroxyl-functional multiwalled carbon nanotubes (MWCNT-OH) in ethylene glycol (EG)/distilled water (DW) solutions by using Tween-80 surfactant and an ultrasonication method. The concentration of MWCNT-OH in EG/DW solutions ranged from 0.1 to 1.2 gram/liter. The dispersion of the MWCNT-OH-based EG/DW solutions was evaluated by using a Zeta-Sizer analyzer. The MWCNT-OH-based EG/DW solutions were used as coolants in the liquid cooling system for the Intel Core i5 processor. The thermal dissipation efficiency and the thermal response of the system were evaluated by directly measuring the temperature of the micro-processor using the Core Temp software and the temperature sensors built inside the micro-processor. The results confirmed the advantages of CNTs in thermal dissipation systems for computer processors and other high-power electronic devices.

  3. Amperometric sensing of anti-HIV drug zidovudine on Ag nanofilm-multiwalled carbon nanotubes modified glassy carbon electrode

    Energy Technology Data Exchange (ETDEWEB)

    Rafati, Amir Abbas, E-mail: aa_rafati@basu.ac.ir; Afraz, Ahmadreza

    2014-06-01

    The zidovudine (ZDV) is the first drug approved for the treatment of HIV virus infection. The detection and determination of this drug are very importance in human serum because of its undesirable effects. A new ZDV sensor was fabricated on the basis of nanocomposite of silver nanofilm (Ag-NF) and multiwalled carbon nanotubes (MWCNTs) immobilized on glassy carbon electrode (GCE). The modified electrodes were characterized by scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), cyclic voltammetry (CV), and linear sweep voltammetry (LSV) techniques. Results showed that the electrodeposited silver has a nanofilm structure and further electrochemical studies showed that the prepared nanocomposite has high electrocatalytic activity and is appropriate for using in sensors. The amperometric technique under optimal conditions is used for the determination of ZDV ranging from 0.1 to 400 ppm (0.37 μM–1.5 mM) with a low detection limit of 0.04 ppm (0.15 μM) (S/N = 3) and good sensitivity. The prepared sensor possessed accurate and rapid response to ZDV and shows an average recovery of 98.6% in real samples. - Highlights: • New anti-HIV drug sensor was fabricated on the basis of nanomaterials composite. • The GCE modified by prepared hydrophilic MWCNT silver nanoparticles. • Silver nanofilm electrodeposited on MWCNT/GCE and characterized by SEM, EDX, CV and LSV • Response of electrode to ZDV was thoroughly investigated by electrochemical techniques.

  4. Ubiquinol-cytochrome c reductase (Complex III) electrochemistry at multi-walled carbon nanotubes/Nafion modified glassy carbon electrodes

    International Nuclear Information System (INIS)

    Pelster, Lindsey N.; Minteer, Shelley D.

    2012-01-01

    Highlights: ► The electron transport chain is important to the understanding of metabolism in the living cell. ► Ubiquinol-cytochrome c reductase is a membrane bound complex of the electron transport chain (Complex III). ► The paper details the first bioelectrochemical characterization of ubiquinol-cytochrome c reductase at an electrode. - Abstract: Electron transport chain complexes are critical to metabolism in living cells. Ubiquinol-cytochrome c reductase (Complex III) is responsible for carrying electrons from ubiquinol to cytochrome c, but the complex has not been evaluated electrochemically. This work details the bioelectrochemistry of ubiquinol-cytochrome c reductase of the electron transport chain of tuber mitochondria. The characterization of the electrochemistry of this enzyme is investigated in carboxylated multi-walled carbon nanotube/tetrabutyl ammonium bromide-modified Nafion ® modified glassy carbon electrodes by cyclic voltammetry. Increasing concentrations of cytochrome c result in a catalytic response from the active enzyme in the nanotube sandwich. The experiments show that the enzyme followed Michaelis–Menten kinetics with a K m for the immobilized enzyme of 2.97 (±0.11) × 10 −6 M and a V max of 6.31 (±0.82) × 10 −3 μmol min −1 at the electrode, but the K m and V max values decreased compared to the free enzyme in solution, which is expected for immobilized redox proteins. This is the first evidence of ubiquinol-cytochrome c reductase bioelectrocatalysis.

  5. Sorption of carbamazepine by commercial graphene oxides: a comparative study with granular activated carbon and multiwalled carbon nanotubes.

    Science.gov (United States)

    Cai, Nan; Larese-Casanova, Philip

    2014-07-15

    Graphene nanosheet materials represent a potentially new high surface area sorbent for the treatment of endocrine disrupting compounds (EDCs) in water. However, sorption behavior has been reported only for laboratory graphene prepared by a laborious and hazardous graphite exfoliation process. A careful examination of commercially available, clean, high-volume produced graphene materials should reveal whether they are appropriate for sorbent technologies and which physicochemical properties most influence sorption performance. In this study, three commercially available graphene oxide powders of various particle sizes, specific surface areas, and surface chemistries were evaluated for their sorption performance using carbamazepine and nine other EDCs and were compared to that of conventional granular activated carbon (GAC) and multi-walled carbon nanotubes (MWCNTs). Sorption kinetics of carbamazepine on graphene oxide powders was rapid and reversible with alcohol washing, consistent with π-π interactions. The various sorption extents as described by Freundlich isotherms were best explained by available surface area, and only the highest surface area graphene oxide (771 m(2)/g) out-performed GAC and MWCNTs. Increasing pH caused more negative surface charge, a twofold decrease in sorption of anionic ibuprofen, a onefold increase in sorption of cationic atenolol, and no change for neutral carbamazepine, highlighting the role of electrostatic interactions. Copyright © 2014 Elsevier Inc. All rights reserved.

  6. Adsorption of Reactive Red M-2BE dye from water solutions by multi-walled carbon nanotubes and activated carbon.

    Science.gov (United States)

    Machado, Fernando M; Bergmann, Carlos P; Fernandes, Thais H M; Lima, Eder C; Royer, Betina; Calvete, Tatiana; Fagan, Solange B

    2011-09-15

    Multi-walled carbon nanotubes and powdered activated carbon were used as adsorbents for the successful removal of Reactive Red M-2BE textile dye from aqueous solutions. The adsorbents were characterised by infrared spectroscopy, N(2) adsorption/desorption isotherms and scanning electron microscopy. The effects of pH, shaking time and temperature on adsorption capacity were studied. In the acidic pH region (pH 2.0), the adsorption of the dye was favourable using both adsorbents. The contact time to obtain equilibrium at 298K was fixed at 1h for both adsorbents. The activation energy of the adsorption process was evaluated from 298 to 323K for both adsorbents. The Avrami fractional-order kinetic model provided the best fit to the experimental data compared with pseudo-first-order or pseudo-second-order kinetic adsorption models. For Reactive Red M-2BE dye, the equilibrium data were best fitted to the Liu isotherm model. Simulated dyehouse effluents were used to check the applicability of the proposed adsorbents for effluent treatment. Copyright © 2011 Elsevier B.V. All rights reserved.

  7. Modifications of Graphite and Multiwall Carbon Nanotubes in the Presence of Urea

    Science.gov (United States)

    Duraia, El-Shazly M.; Fahami, Abbas; Beall, Gary W.

    2018-02-01

    The effect of high-energy ball milling on two carbon allotropes, graphite and multiwall carbon nanotubes (MWCNT) in the presence of urea has been studied. Samples were investigated using Raman spectroscopy, x-ray diffraction, scanning electron microscope (SEM) and x-ray photoelectron spectroscopy (XPS). Nitrogen-doped graphene has been successfully synthesized via a simple scalable mechanochemistry method using urea and graphite powder precursors. XPS results revealed the existence of the different nitrogen atoms configurations including pyridine, pyrrodic and graphitic N. SEM observations showed that the graphene nanosheets morphology become more wrinkles folded and crumbled as the milling time increased. The ID/IG ratio also increased as the milling time rose. The presence of both D' and G + D bands at 1621 cm-1 and 2940 cm-1, respectively, demonstrated the nitrogen incorporation in the graphene lattice Two factors contribute to the used urea: first it helps to exfoliate graphite into graphene, and second it preserves the graphitic structure from damage during the milling process as well as acting as a solid-state nitrogen source. Based on the phase analysis, the d-spacing of MWCNT samples in the presence of urea decreased due to the mechanical force in the milling process as the milling time increased. On the other hand, in the graphite case, due to its open flat surface, the graphite (002) peak shifts toward lower two theta as the milling time increase. Such findings are important and could be used for large-scale production of N-doped graphene, diminishing the use of either dangerous chemicals or sophisticated equipment.

  8. Quantitative evaluation of multi-walled carbon nanotube uptake in wheat and rapeseed

    Energy Technology Data Exchange (ETDEWEB)

    Larue, Camille, E-mail: Camille.larue@cea.fr [UMR3299 CEA-CNRS, Service Interdisciplinaire des Systemes Moleculaires et Materiaux, Laboratoire Structure et Dynamique par Resonance Magnetique (LSDRM), CEA Saclay, 91191 Gif sur Yvette (France); Pinault, Mathieu, E-mail: Mathieu.pinault@cea.fr [CEA, IRAMIS, SPAM, Laboratoire Francis Perrin (CNRS URA 2453), 91191 Gif sur Yvette (France); Czarny, Bertrand, E-mail: Bertrand.czarny@cea.fr [CEA, iBiTecS SIMOPRO, CEA Saclay, 91191 Gif sur Yvette (France); Georgin, Dominique, E-mail: Dominique.georgin@cea.fr [CEA, IBiTecS, SCBM, CEA Saclay, 91191 Gif sur Yvette (France); Jaillard, Danielle, E-mail: danielle.jaillard@u-psud.fr [UMR8195 CNRS-Universite Paris-Sud, Centre Commun de Microscopie Electronique, F-91405 Orsay (France); Bendiab, Nedjma, E-mail: Nedjma.bendiab@grenoble.cnrs.fr [Institut Neel, CNRS-Universite Joseph Fourier, 25 rue des Martyrs, 38049 Grenoble Cedex 9 (France); Mayne-L' Hermite, Martine, E-mail: martine.mayne@cea.fr [CEA, IRAMIS, SPAM, Laboratoire Francis Perrin (CNRS URA 2453), 91191 Gif sur Yvette (France); Taran, Frederic, E-mail: frederic.taran@cea.fr [CEA, IBiTecS, SCBM, CEA Saclay, 91191 Gif sur Yvette (France); Dive, Vincent, E-mail: vincent.dive@cea.fr [CEA, iBiTecS SIMOPRO, CEA Saclay, 91191 Gif sur Yvette (France); and others

    2012-08-15

    Highlights: Black-Right-Pointing-Pointer Wheat and rapeseed accumulate MWCNT through root exposure, and translocate them to their leaves. Black-Right-Pointing-Pointer Transfer factor of MWCNT from hydroponic solution to leaves never exceeds 0.005 Per-Mille-Sign . Black-Right-Pointing-Pointer MWCNT majorly accumulate in the most peripheral areas and in newly developed leaves. Black-Right-Pointing-Pointer Accumulation of less than 200 ng MWCNT per g of leaf does not impact plant development and physiology. - Abstract: Environmental contamination with carbon nanotubes would lead to plant exposure and particularly exposure of agricultural crops. The only quantitative exposure data available to date which can be used for risk assessment comes from computer modeling. The aim of this study was to provide quantitative data relative to multi-walled carbon nanotube (MWCNT) uptake and distribution in agricultural crops, and to correlate accumulation data with impact on plant development and physiology. Roots of wheat and rapeseed were exposed in hydroponics to uniformly {sup 14}C-radiolabeled MWCNTs. Radioimaging, transmission electron microscopy and raman spectroscopy were used to identify CNT distribution. Radioactivity counting made it possible absolute quantification of CNT accumulation in plant leaves. Impact of CNTs on seed germination, root elongation, plant biomass, evapotranspiration, chlorophyll, thiobarbituric acid reactive species and H{sub 2}O{sub 2} contents was evaluated. We demonstrate that less than 0.005 Per-Mille-Sign of the applied MWCNT dose is taken up by plant roots and translocated to the leaves. This accumulation does not impact plant development and physiology. In addition, it does not induce any modifications in photosynthetic activity nor cause oxidative stress in plant leaves. Our results suggest that if environmental contamination occurs and MWCNTs are in the same physico-chemical state than the ones used in the present article, MWCNT transfer to

  9. Polymer-derived ceramic composite fibers with aligned pristine multiwalled carbon nanotubes.

    Science.gov (United States)

    Sarkar, Sourangsu; Zou, Jianhua; Liu, Jianhua; Xu, Chengying; An, Linan; Zhai, Lei

    2010-04-01

    Polymer-derived ceramic fibers with aligned multiwalled carbon nanotubes (MWCNTs) are fabricated through the electrospinning of polyaluminasilazane solutions with well-dispersed MWCNTs followed by pyrolysis. Poly(3-hexylthiophene)-b-poly (poly (ethylene glycol) methyl ether acrylate) (P3HT-b-PPEGA), a conjugated block copolymer compatible with polyaluminasilazane, is used to functionalize MWCNT surfaces with PPEGA, providing a noninvasive approach to disperse carbon nanotubes in polyaluminasilazane chloroform solutions. The electrospinning of the MWCNT/polyaluminasilazane solutions generates polymer fibers with aligned MWCNTs where MWCNTs are oriented along the electrospun jet by a sink flow. The subsequent pyrolysis of the obtained composite fibers produces ceramic fibers with aligned MWCNTs. The study of the effect of polymer and CNT concentration on the fiber structures shows that the fiber size increases with the increment of polymer concentration, whereas higher CNT content in the polymer solutions leads to thinner fibers attributable to the increased conductivity. Both the SEM and TEM characterization of the polymer and ceramic fibers demonstrates the uniform orientation of CNTs along the fibers, suggesting excellent dispersion of CNTs and efficient CNT alignment via the electrospinning. The electrical conductivity of a ceramic fibers with 1.2% aligned MWCNTs is measured to be 1.58 x 10(-6) S/cm, which is more than 500 times higher than that of bulk ceramic (3.43 x 10(-9) S/cm). Such an approach provides a versatile method to disperse CNTs in preceramic polymer solutions and offers a new approach to integrate aligned CNTs in ceramics.

  10. Reverse capillary flow of condensed water through aligned multiwalled carbon nanotubes

    International Nuclear Information System (INIS)

    Yun, Jongju; Jeon, Wonjae; Alam Khan, Fakhre; Lee, Jinkee; Baik, Seunghyun

    2015-01-01

    Molecular transport through nanopores has recently received considerable attention as a result of advances in nanofabrication and nanomaterial synthesis technologies. Surprisingly, water transport investigations through carbon nanochannels resulted in two contradicting observations: extremely fast transport or rejection of water molecules. In this paper, we elucidate the mechanism of impeded water vapor transport through the interstitial space of aligned multiwalled carbon nanotubes (aligned-MWCNTs)—capillary condensation, agglomeration, reverse capillary flow, and removal by superhydrophobicity at the tip of the nanotubes. The origin of separation comes from the water’s phase change from gas to liquid, followed by reverse capillary flow. First, the saturation water vapor pressure is decreased in a confined space, which is favorable for the phase change of incoming water vapor into liquid drops. Once continuous water meniscus is formed between the nanotubes by the adsoprtion and agglomeration of water molecules, a high reverse Laplace pressure is induced in the mushroom-shaped liquid meniscus at the entry region of the aligned-MWCNTs. The reverse Laplace pressure can be significantly enhanced by decreasing the pore size. Finally, the droplets pushed backward by the reverse Laplace pressure can be removed by superhydrophobicity at the tip of the aligned-MWCNTs. The analytical analysis was also supported by experiments carried out using 4 mm-long aligned-MWCNTs with different intertube distances. The water rejection rate and the separation factor increased as the intertube distance decreased, resulting in 90% and 10, respectively, at an intertube distance of 4 nm. This mechanism and nanotube membrane may be useful for energy-efficient water vapor separation and dehumidification. (paper)

  11. Functionalized Multiwalled Carbon Nanotube Electrochemical Sensor for Determination of Anticancer Drug Flutamide

    Science.gov (United States)

    Farias, Julianna Santos; Zanin, Hudson; Caldas, Adriana Silva; dos Santos, Clenilton Costa; Damos, Flavio Santos; de Cássia Silva Luz, Rita

    2017-10-01

    An electrochemical sensor based on functionalized multiwalled carbon nanotubes (MWCNTf) has been developed and applied for determination of anticancer drug flutamide in pharmaceutical and artificial urine samples. The electrode was prepared by modifying a glassy carbon electrode with MWCNTf, denoted herein as MWCNTf/GCE. The MWCNTf/GCE electrode exhibited high catalytic activity, high sensitivity, and high stability and was applicable over a wide concentration range for flutamide. The effects of the scan rate, pH, and nature of the electrolyte on the electrochemical behavior of flutamide on the MWCNTf/GCE were investigated. The results showed that this electrode presented the best square-wave voltammetric response to flutamide in Britton-Robinson buffer solution at pH 5.0 at frequency of 50 Hz and amplitude of 0.06 V. The proposed sensor presents a wide linear response range from concentration of 0.1 μmol L-1 up to 1000 μmol L-1 (or 27.6 μg L-1 up to 0.27 g L-1), with limit of detection, limit of quantification, and sensitivity of 0.03 μmol L-1, 0.1 μmol L-1, and 0.30 μA μmol-1 L, respectively. The MWCNTf/GCE electrode was successfully applied for determination of flutamide in pharmaceutical formulations and artificial urine samples, giving results in agreement with those obtained by a comparative method described in literature. A paired Student's t-test revealed no statistical difference between the reference and proposed method at 95% confidence level. The average recovery for fortified samples was 101 ± 1%.

  12. Multi-walled carbon nanotube structural instability with/without metal nanoparticles under electron beam irradiation

    Science.gov (United States)

    Khan, Imran; Huang, Shengli; Wu, Chenxu

    2017-12-01

    The structural transformation of multi-walled carbon nanotubes (MWCNT) under electron beam (e-beam) irradiation at room temperature is studied, with respect to a novel passivation effect due to gold nanoparticles (Au NPs). MWCNT structural evolution induced by energetic e-beam irradiation leads to faster shrinkage, as revealed via in situ transmission electron microscopy, while MWCNT surface modification with Au NPs (Au-MWCNT) slows down the shrinkage by impeding the structural evolution process for a prolonged time under the same irradiation conditions. The new relationship between MWCNT and Au-MWCNT shrinking radii and irradiation time illustrates that the MWCNT shrinkage rate is faster than either theoretical predictions or the same process in Au-MWCNTs. As compared with the outer surface energy (positive curvature), the inner surface energy (negative curvature) of the MWCNT contributes more to the athermal evaporation of tube wall atoms, leading to structural instability and shrinkage under e-beam irradiation. Conversely, Au NPs possess only outer surface energy (positive curvature) compared with the MWCNT. Their presence on MWCNT surfaces retards the dynamics of MWCNT structural evolution by slowing down the evaporation process of carbon atoms, thus restricting Au-MWCNT shrinkage. Au NP interaction and growth evolves athermally on MWCNT surfaces, exhibits increase in their size, and indicates the association of this mechanism with the coalescence induced by e-beam activated electronic excitations. Despite their growth, Au NPs show extreme structural stability, and remain crystalline under prolonged irradiation. It is proposed that the surface energy of MWCNTs and Au NPs, together with e-beam activated soft modes or lattice instability effects, predominantly govern all the above varieties of structural evolution.

  13. Quantitative evaluation of multi-walled carbon nanotube uptake in wheat and rapeseed

    International Nuclear Information System (INIS)

    Larue, Camille; Pinault, Mathieu; Czarny, Bertrand; Georgin, Dominique; Jaillard, Danielle; Bendiab, Nedjma; Mayne-L’Hermite, Martine; Taran, Frédéric; Dive, Vincent

    2012-01-01

    Highlights: ► Wheat and rapeseed accumulate MWCNT through root exposure, and translocate them to their leaves. ► Transfer factor of MWCNT from hydroponic solution to leaves never exceeds 0.005‰. ► MWCNT majorly accumulate in the most peripheral areas and in newly developed leaves. ► Accumulation of less than 200 ng MWCNT per g of leaf does not impact plant development and physiology. - Abstract: Environmental contamination with carbon nanotubes would lead to plant exposure and particularly exposure of agricultural crops. The only quantitative exposure data available to date which can be used for risk assessment comes from computer modeling. The aim of this study was to provide quantitative data relative to multi-walled carbon nanotube (MWCNT) uptake and distribution in agricultural crops, and to correlate accumulation data with impact on plant development and physiology. Roots of wheat and rapeseed were exposed in hydroponics to uniformly 14 C-radiolabeled MWCNTs. Radioimaging, transmission electron microscopy and raman spectroscopy were used to identify CNT distribution. Radioactivity counting made it possible absolute quantification of CNT accumulation in plant leaves. Impact of CNTs on seed germination, root elongation, plant biomass, evapotranspiration, chlorophyll, thiobarbituric acid reactive species and H 2 O 2 contents was evaluated. We demonstrate that less than 0.005‰ of the applied MWCNT dose is taken up by plant roots and translocated to the leaves. This accumulation does not impact plant development and physiology. In addition, it does not induce any modifications in photosynthetic activity nor cause oxidative stress in plant leaves. Our results suggest that if environmental contamination occurs and MWCNTs are in the same physico-chemical state than the ones used in the present article, MWCNT transfer to the food chain via food crops would be very low.

  14. Selective ex-vivo photothermal ablation of human pancreatic cancer with albumin functionalized multiwalled carbon nanotubes

    Directory of Open Access Journals (Sweden)

    Mocan L

    2011-04-01

    Full Text Available Lucian Mocan1, Flaviu A Tabaran2, Teodora Mocan1, Constantin Bele3, Anamaria Ioana Orza1, Ciprian Lucan4, Rares Stiufiuc1, Ioana Manaila1, Ferencz Iulia1, Iancu Dana1, Florin Zaharie1, Gelu Osian1, Liviu Vlad1, Cornel Iancu11Department of Nanomedicine, “Iuliu Hatieganu” University of Medicine and Pharmacy, Cluj-Napoca, Romania; 2Department of Pathology, University of Agricultural Sciences and Veterinary Medicine, Cluj-Napoca, Romania; 3Department of Biochemistry, University of Agricultural Sciences and Veterinary Medicine, Cluj-Napoca, Romania; 4Clinical Institute of Urology and Renal Transplantation, Cluj-Napoca, RomaniaAbstract: The process of laser-mediated ablation of cancer cells marked with biofunctionalized carbon nanotubes is frequently called “nanophotothermolysis”. We herein present a method of selective nanophotothermolisys of pancreatic cancer (PC using multiwalled carbon nanotubes (MWCNTs functionalized with human serum albumin (HSA. With the purpose of testing the therapeutic value of these nanobioconjugates, we have developed an ex-vivo experimental platform. Surgically resected specimens from patients with PC were preserved in a cold medium and kept alive via intra-arterial perfusion. Additionally, the HSA-MWCNTs have been intra-arterially administered in the greater pancreatic artery under ultrasound guidance. Confocal and transmission electron microscopy combined with immunohistochemical staining have confirmed the selective accumulation of HSA-MWCNTs inside the human PC tissue. The external laser irradiation of the specimen has significantly produced extensive necrosis of the malign tissue after the intra-arterial administration of HSA-MWCNTs, without any harmful effects on the surrounding healthy parenchyma. We have obtained a selective photothermal ablation of the malign tissue based on the selective internalization of MWCNTs with HSA cargo inside the pancreatic adenocarcinoma after the ex-vivo intra

  15. Magnetic multiwalled carbon nanotubes as nanocarrier tags for sensitive determination of fetuin in saliva.

    Science.gov (United States)

    Sánchez-Tirado, Esther; González-Cortés, Araceli; Yáñez-Sedeño, Paloma; Pingarrón, José M

    2018-08-15

    This paper reports the development and performance of an electrochemical immunosensor using magnetic multiwalled carbon nanotubes (m-MWCNTs) as nanocarrier tags for the determination of human fetuin A (HFA), a relevant biomarker of obesity, insulin resistance, and type-2 diabetes as well as for pancreatic and liver cancers and inflammatory processes. Screen-printed carbon electrodes were grafted with p-aminobezoic acid and streptavidin was covalently immobilized on the electrode surface. A biotinylated capture antibody was immobilized through streptavidin-biotin interaction and a sandwich assay configuration was implemented using m-MWCNTs conjugated with HRP and anti-HFA antibodies as the detection label. The determination of HFA was accomplished by measuring the current produced by the electrochemical reduction of benzoquinone at -200 mV upon addition of H 2 O 2 as HRP substrate. The prepared m-MWCNTs were characterized by SEM, TEM, XRD and EDS. All the steps involved in the immunosensor preparation were monitored by electrochemical impedance spectroscopy and cyclic voltammetry. A linear calibration plot for HFA was found between 20 and 2000 pg/mL with a LOD value of 16 pg/mL. This performance is notably better than that reported for an ELISA kit and a chronoimpedimetric immunosensor. The favorable contribution of m-MWCNTs in comparison with MWCNTs without incorporated magnetic particles to this excellent analytical performance is also highlighted. The immunosensor selectivity against other proteins and potentially interfering compounds was excellent. In addition, the usefulness of the immunosensor was demonstrated by the analysis of HFA in saliva with minimal sample treatment. Copyright © 2018 Elsevier B.V. All rights reserved.

  16. Glassy carbon electrodes modified with multiwalled carbon nanotubes for the determination of ascorbic acid by square-wave voltammetry

    Directory of Open Access Journals (Sweden)

    Sushil Kumar

    2012-05-01

    Full Text Available Multiwalled carbon nanotubes were used to modify the surface of a glassy carbon electrode to enhance its electroactivity. Nafion served to immobilise the carbon nanotubes on the electrode surface. The modified electrode was used to develop an analytical method for the analysis of ascorbic acid (AA by square-wave voltammetry (SWV. The oxidation of ascorbic acid at the modified glassy carbon electrode showed a peak potential at 315 mV, about 80 mV lower than that observed at the bare (unmodified electrode. The peak current was about threefold higher than the response at the bare electrode. Replicate measurements of peak currents showed good precision (3% rsd. Peak currents increased with increasing ascorbic acid concentration (dynamic range = 0.0047–5.0 mmol/L and displayed good linearity (R2 = 0.994. The limit of detection was 1.4 μmol/L AA, while the limit of quantitation was 4.7 μmol/L AA. The modified electrode was applied to the determination of the amount of ascorbic acid in four brands of commercial orange-juice products. The measured content agreed well (96–104% with the product label claim for all brands tested. Recovery tests on spiked samples of orange juice showed good recovery (99–104%. The reliability of the SWV method was validated by conducting parallel experiments based on high-performance liquid chromatography (HPLC with absorbance detection. The observed mean AA contents of the commercial orange juice samples obtained by the two methods were compared statistically and were found to have no significant difference (P = 0.05.

  17. Removal of Malachite Green Dye from Aqueous Solution Using Multi-Walled Carbon Nano tubes: An Application of Experimental Design

    International Nuclear Information System (INIS)

    Siti Aminah Zulkepli; Md Pauzi Abdullah; Md Pauzi Abdullah; Wan Mohd Afiq Wan Mohd Khalik

    2016-01-01

    An experimental design methodology was performed in the optimization of removal of malachite green dye by multi-walled carbon nano tubes. A Central Composite Design (25) was chosen to develop a mathematical model and determine the optimum condition for adsorption of malachite green by carbon nano tubes. Five experimental factors, namely initial dye concentration, mass of adsorbent, pH, contact time and agitation speed were studied. Maximum adsorption of malachite green was achieved at the suggested optimum conditions: initial dye concentration (20 ppm), weight of adsorbent (0.03 g), pH solution (7) contact time (17 min) and agitation speed (150 strokes per min). The experimental value of adsorption by multi-walled carbon nano tubes were found to be in good agreement with the predicted value (R"2 = 0.922).The experimental equilibrium data were best fitted to isotherm model (Langmuir) and kinetic model (pseudo second-order) respectively. Maximum adsorption by carbon nano tubes at monolayer for malachite green was obtained at 112.36 mg/ g while kinetic rate constant was calculated to be 0.0017 g mg"-"1 min"-"1. (author)

  18. SYNTHESIS AND STUDY OF CORROSION PERFORMANCE OF EPOXY COATING CONTAINING MULTI-WALLED CARBON NANOTUBE/ POLY ORTHO AMINOPHENOL NANOCOMPOSITE

    Directory of Open Access Journals (Sweden)

    N. Bahrami Panah

    2016-03-01

    Full Text Available The epoxy coatings containing multi-walled carbon nanotube/ poly ortho aminophenol nanocomposite were prepared and used as anticorrosive coatings. The nanocomposites with different contents of carbon nanotube were synthesized in a solution of sodium dodecyl sulfate and ammonium peroxy disulfate as a surfactant and an oxidant, respectively. The morphology and structural properties were confirmed by Fourier transform infrared spectroscopy and scanning electron microscopy methods. The mean size of nanocomposite particles was 20-35 nm determined by scanning electron microscopy. The epoxy coatings containing the nanocomposites were applied over mild steel panels and their corrosion performance was investigated using electrochemical impedance spectroscopy and potentiodynamic polarization measurements in a 3.5 % sodium chloride solution. The results showed that epoxy coatings consisting of nanocomposite with 1 wt.% multi-walled carbon nanotube exhibited higher anticorrosive properties than other prepared coatings of different carbon nanotube contents, which could be due to the strong interaction between the mild steel surface and the conjugated nanocomposite.

  19. Quasi-QSAR for mutagenic potential of multi-walled carbon-nanotubes.

    Science.gov (United States)

    Toropov, Andrey A; Toropova, Alla P

    2015-04-01

    Available on the Internet, the CORAL software (http://www.insilico.eu/coral) has been used to build up quasi-quantitative structure-activity relationships (quasi-QSAR) for prediction of mutagenic potential of multi-walled carbon-nanotubes (MWCNTs). In contrast with the previous models built up by CORAL which were based on representation of the molecular structure by simplified molecular input-line entry system (SMILES) the quasi-QSARs based on the representation of conditions (not on the molecular structure) such as concentration, presence (absence) S9 mix, the using (or without the using) of preincubation were encoded by so-called quasi-SMILES. The statistical characteristics of these models (quasi-QSARs) for three random splits into the visible training set and test set and invisible validation set are the following: (i) split 1: n=13, r(2)=0.8037, q(2)=0.7260, s=0.033, F=45 (training set); n=5, r(2)=0.9102, s=0.071 (test set); n=6, r(2)=0.7627, s=0.044 (validation set); (ii) split 2: n=13, r(2)=0.6446, q(2)=0.4733, s=0.045, F=20 (training set); n=5, r(2)=0.6785, s=0.054 (test set); n=6, r(2)=0.9593, s=0.032 (validation set); and (iii) n=14, r(2)=0.8087, q(2)=0.6975, s=0.026, F=51 (training set); n=5, r(2)=0.9453, s=0.074 (test set); n=5, r(2)=0.8951, s=0.052 (validation set). Copyright © 2014 Elsevier Ltd. All rights reserved.

  20. Wet spinning of PVA composite fibers with a large fraction of multi-walled carbon nanotubes

    Directory of Open Access Journals (Sweden)

    Dengpan Lai

    2015-10-01

    Full Text Available PVA composites fibers with a large fraction of multi-walled carbon nanotubes modified by both covalent and non-covalent functionalization were produced by a wet-spinning process. Model XQ-1 tensile tester, thermogravimetric analysis, scanning electron microscopy, differential scanning calorimetry, and wide-angle X-ray diffraction were used to characterize the properties of PVA/MWNT composite fibers. The TGA results suggested that MWNTs content in composite fibers were ranged from 5.3 wt% to 27.6 wt%. The mechanical properties of PVA/MWNT composite fibers were obviously superior to pure PVA fiber. The Young׳s modulus of composite fibers enhanced with increasing the content of MWNTs, and it rised gradually from 6.7 GPa for the pure PVA fiber to 12.8 GPa for the composite fibers with 27.6 wt% MWNTs. Meanwhile, the tensile strength increased gradually from 0.39 GPa for the pure PVA fiber to 0.74 GPa for the composite fibers with 14.4 wt% MWNTs. Nevertheless, the tensile strength of the composite fibers decreased as the MWNTs content up to 27.6 wt%. SEM results indicated that the MWNTs homogeneously dispersed in the composite fibers, however some agglomerates also existed when the content of MWNTs reached 27.6 wt%. DSC results proved strong interfacial interaction between MWNTs and PVA chain, which benefited composite fibers in the efficient stress-transfer. WXAD characterization showed that the orientation of PVA molecules declined from 94.1% to 90.9% with the increasing of MWNTs content. The good dispersibility of MWNTs throughout PVA matrix and efficient stress-transfer between MWNTs and PVA matrix may contributed to significant enhancement in the mechanical properties.

  1. Synthesis and characterization of poly lactic acid and multiwall carbon nano-tubes mixtures

    Science.gov (United States)

    Kumar LG, Santhosh; del A. Cardona, Rocío; Berríos-Soto, Melvin; Santiago-Avilés, Jorge J.

    2011-10-01

    The motivation for this study is to reproduce processing conditions which lead to the formation of photo or photoinduced thermal actuation, combined with inexpensive, environmentally friendly (easily degradable) materials. Commercially available polymer, poly lactic acid (PLA), was used in our studies. PLA is a well know biodegradable polymer naturally obtained from corn. PLA was received as a solid resin in pellet form and dissolved in 1:3 acetone/chloroform solutions, to achieve the proper electrospinning kinematic viscosity. Once in the liquid phase, the material was mixed with commercially available multi-walled carbon nanotubes (MWCNTs) at varying concentrations and dispersed by severe sonication. The mixtures was electrospun at room temperature using a home built electrospinning apparatus capable of depositing randomly oriented fiber mats or oriented fibers onto different substrates, ranging from oxidized silicon wafers, alumina squares or glass microscope slides. The fibers diameters and lengths are statistically distributed following a log-normal distribution and the mean and dispersion are controlled by spinning parameters. Once the fibers were electrospun, they were compositionally, morphologically and structurally characterized by thermal and gravimetric analysis (TGA/DTA), rheology, imaging using a focused Ion Beam Scanning Electron Microscope (IBSEM), and IR /Raman methodologies. These studies can be used to explore PLA-MWCNTs mixtures suitability in applications such as super-capacitor technology, which would enable us to pursue further research in this field, while focusing on improving the electro spinning conditions so as to be able to better anticipate fiber morphology to generate a consistent regime of fibers.

  2. Application of modified multiwall carbon nanotubes as a sorbent for zirconium (IV) adsorption from aqueous solution

    International Nuclear Information System (INIS)

    Yavari, R.; Davarkhah, R.

    2013-01-01

    Modified multiwall carbon nanotubes (MWCNTs) by nitric acid solution were used to investigate the adsorption behavior of zirconium from aqueous solution. Pristine and oxidized MWCNTs were characterized using nitrogen adsorption/desorption isotherm, Boehm's titration method, thermogravimetry analysis, transmission electron microscopy and Fourier transform infrared spectroscopy. The results showed that the surface properties of MWCNTs such as specific surface area, total pore volume, functional groups and the total number of acidic and basic sites were improved after oxidation. These improvements are responsible for their hydrophobic properties and consequently an easy dispersion in water and suitable active sites for more adsorption of zirconium. The adsorption of Zr(IV) as a function of initial concentration of zirconium, contact time, MWCNTs dosage, HCl and HNO 3 concentration and also ionic strength was investigated using a batch technique under ambient conditions. The experimental results indicated that sorption of Zr(IV) was strongly influenced by zirconium concentrations, oxidized MWCNTs content and acid pH values. The calculated correlation coefficient of the linear regressions values showed that Langmuir model fits the adsorption equilibrium data better than the Freundlich model. Kinetic data of sorption indicated that equilibrium was achieved within 60 min and the adsorption process can be described by the pseudo second-order reaction rate model. Based on the experimental results, surface complexation is the major mechanism for adsorption of Zr(IV) onto MWCNTs. Also, Study on the desorption process of zirconium showed that the complete recovery can be obtained using nitric or hydrochloric acids of 4 M. (author)

  3. Photothermal effects of multi-walled carbon nanotubes on the viability of BT-474 cancer cells

    International Nuclear Information System (INIS)

    Chou, Hung-Tao; Wang, Tsung-Pao; Lee, Chi-Young; Tai, Nyan-Hwa; Chang, Hwan-You

    2013-01-01

    Functionalized multi-walled carbon nanotubes (f-MWCNTs) were conjugated to an antibody of BT-474 cancer cells (f-MWCNTs-ab), and the photothermal effect of the f-MWCNTs-ab for BT-474 cancer cell destruction was demonstrated. After near-infrared irradiation, the f-MWCNTs-ab were more capable of killing cancer cells and possessed higher cell specificity than f-MWCNTs. Quantitative results showed that the viability of the cancer cells was affected by the concentration of the f-MWCNTs-ab solution, irradiation time, and settling time after irradiation. The membrane impermeable fluorescence dye ethidium bromide was used to detect cell viability after near-infrared irradiation, and the results agreed with those obtained from the Alamar Blue cell viability assay. The EtBr fluorescence results suggest that the cell membrane, attached to f-MWCNTs-ab, was damaged after irradiation, which led to cell death and necrosis. Using confocal microscopy, a few f-MWCNTs-ab were detected in the cell, indicating the endocytosis effect. The results not only explain the improved efficiency of thermotherapy but also indicate that necrosis may result from protein denaturation attributing to the heated f-MWCNTs-ab in the cell. Highlights: ► f-MWCNTs conjugated with anti-HER2 antibody by chemical method. ► Kill breast cancer cells by using low dose f-MWCNTs-ab due to photothermal effect. ► Use EtBr fluorescent to prove that the cell membrane was broken by heated f-MWCNTs. ► Few f-MWCNTs-ab were detected in the cell indicating the endocytosis effect. ► Necrosis may result from protein denaturation due to contact with the heated CNTs.

  4. Multiwalled carbon nanotubes enhance electrochemical properties of titanium to determine in situ bone formation

    Energy Technology Data Exchange (ETDEWEB)

    Sirivisoot, Sirinrath; Webster, Thomas J [Division of Engineering, Brown University, Providence, RI 02912 (United States)], E-mail: Thomas_Webster@Brown.edu

    2008-07-23

    Multiwalled carbon nanotubes (MWCNTs) enhance osteoblast (bone-forming cell) calcium deposition compared to currently implanted materials (such as titanium). In this study, MWCNTs were grown out of nanopores anodized on titanium (MWCNT-Ti). The electrochemical responses of MWCNT-Ti were investigated in an attempt to ascertain if MWCNT-Ti can serve as novel in situ sensors of bone formation. For this purpose, MWCNT-Ti was subjected to a ferri/ferrocyanide redox couple and its electrochemical behavior measured. Cyclic voltammograms (CVs) showed an enhanced redox potential for the MWCNT-Ti. These redox signals were superior to that obtained with bare unmodified Ti, which did not sense either oxidation or reduction peaks in the CVs. A further objective of this study was to investigate the redox reactions of MWCNT-Ti in a solution of extracellular components secreted by osteoblasts in vitro. It was found that MWCNT-Ti exhibited well-defined and persistent CVs, similar to the ferri/ferrocyanide redox reaction. The higher electrodic performance and electrocatalytic activity of the MWCNT-Ti compared to the bare titanium observed in this study were likely due to the fact that MWCNTs enhanced direct electron transfer and facilitated double-layer effects, leading to a strong redox signal. Thus these results encourage the further study and modification of MWCNT-Ti to sense new bone growth in situ next to orthopedic implants and perhaps monitor other events (such as infection and/or harmful scar tissue formation) to improve the current clinical diagnosis of orthopedic implants.

  5. Engineering Multi-Walled Carbon Nanotube Therapeutic Bionanofluids to Selectively Target Papillary Thyroid Cancer Cells.

    Directory of Open Access Journals (Sweden)

    Idit Dotan

    Full Text Available The incidence of papillary thyroid carcinoma (PTC has risen steadily over the past few decades as well as the recurrence rates. It has been proposed that targeted ablative physical therapy could be a therapeutic modality in thyroid cancer. Targeted bio-affinity functionalized multi-walled carbon nanotubes (BioNanofluid act locally, to efficiently convert external light energy to heat thereby specifically killing cancer cells. This may represent a promising new cancer therapeutic modality, advancing beyond conventional laser ablation and other nanoparticle approaches.Thyroid Stimulating Hormone Receptor (TSHR was selected as a target for PTC cells, due to its wide expression. Either TSHR antibodies or Thyrogen or purified TSH (Thyrotropin were chemically conjugated to our functionalized Bionanofluid. A diode laser system (532 nm was used to illuminate a PTC cell line for set exposure times. Cell death was assessed using Trypan Blue staining.TSHR-targeted BioNanofluids were capable of selectively ablating BCPAP, a TSHR-positive PTC cell line, while not TSHR-null NSC-34 cells. We determined that a 2:1 BCPAP cell:α-TSHR-BioNanofluid conjugate ratio and a 30 second laser exposure killed approximately 60% of the BCPAP cells, while 65% and >70% of cells were ablated using Thyrotropin- and Thyrogen-BioNanofluid conjugates, respectively. Furthermore, minimal non-targeted killing was observed using selective controls.A BioNanofluid platform offering a potential therapeutic path for papillary thyroid cancer has been investigated, with our in vitro results suggesting the development of a potent and rapid method of selective cancer cell killing. Therefore, BioNanofluid treatment emphasizes the need for new technology to treat patients with local recurrence and metastatic disease who are currently undergoing either re-operative neck explorations, repeated administration of radioactive iodine and as a last resort external beam radiation or chemotherapy, with

  6. Effects of transferrin conjugated multi-walled carbon nanotubes in lung cancer delivery

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Rahul Pratap [Department of Pharmacology, Institute of Medical Sciences, Banaras Hindu University, Varanasi 221005 (India); Sharma, Gunjan [Genotoxicology and Cancer Biology Lab, Department of Zoology, Institute of Science, Banaras Hindu University, Varanasi 221005 (India); Sonali [Department of Pharmacology, Institute of Medical Sciences, Banaras Hindu University, Varanasi 221005 (India); Singh, Sanjay [Department of Pharmaceutics, Indian Institute of Technology (BHU), Varanasi 221005 (India); Patne, Shashikant C.U. [Department of Pathology, Institute of Medical Sciences, Banaras Hindu University, Varanasi 221005 (India); Pandey, Bajarangprasad L. [Department of Pharmacology, Institute of Medical Sciences, Banaras Hindu University, Varanasi 221005 (India); Koch, Biplob, E-mail: kochbiplob@gmail.com [Genotoxicology and Cancer Biology Lab, Department of Zoology, Institute of Science, Banaras Hindu University, Varanasi 221005 (India); Muthu, Madaswamy S., E-mail: muthubits@rediffmail.com [Department of Pharmaceutics, Indian Institute of Technology (BHU), Varanasi 221005 (India); Department of Pharmacology, Institute of Medical Sciences, Banaras Hindu University, Varanasi 221005 (India)

    2016-10-01

    The aim of this study was to develop multi-walled carbon nanotubes (MWCNT) which were covalently conjugated with transferrin by carbodiimide chemistry and loaded with docetaxel as a model drug for effective treatment of lung cancer in comparison with the commercial docetaxel injection (Docel™). D-Alpha-tocopheryl polyethylene glycol 1000 succinate (TPGS) was used as amphiphilic surfactant to improve the aqueous dispersity and biocompatibility of MWCNT. Human lung cancer cells (A549 cells) were employed as an in-vitro model to access cellular uptake, cytotoxicity, cellular apoptosis, cell cycle analysis, and reactive oxygen species (ROS) of the docetaxel/coumarin-6 loaded MWCNT. The cellular uptake results of transferrin conjugated MWCNT showed higher efficiency in comparison with free C6. The IC{sub 50} values demonstrated that the transferrin conjugated MWCNT could be 136-fold more efficient than Docel™ after 24 h treatment with the A549 cells. Flow cytometry analysis confirmed that cancerous cells appeared significantly (P < 0.05) in the sub-G1 phase for transferrin conjugated MWCNT in comparison with Docel™. Results of transferrin conjugated MWCNT have showed better efficacy with safety than Docel™. - Highlights: • It shows the development of transferrin conjugated MWCNT formulation of DTX for the effective treatment of lung cancer. • Evaluated the cellular uptake, cytotoxicity, cellular apoptosis, cell cycle, and ROS level of the DTX/C6 loaded MWCNT. • The IC{sub 50} values demonstrated that the transferrin conjugated MWCNT could be 136-fold more effective than Docel™. • Safety of the DTX formulations were studied by the measurements of ALP, LDH and total protein count levels in BAL fluid. • Results of transferrin conjugated MWCNT have showed better efficacy with safety than Docel™ in lung cancer delivery.

  7. Synthesis and investigation of PMMA films with homogeneously dispersed multiwalled carbon nanotubes

    International Nuclear Information System (INIS)

    Pantoja-Castro, M.A.; Pérez-Robles, J.F.; González-Rodríguez, H.; Vorobiev-Vasilievitch, Y.; Martínez-Tejada, H.V.; Velasco-Santos, C.

    2013-01-01

    Multiwalled carbon nanotubes (MWNT) modified by 2.2′-azoiso-butyronitrile (AIBN) were incorporated into methyl methacrylate (MMA) by sonochemistry method, resulting in homogenous dispersion of MWNT, which makes possible to obtain flexible conductive polymer-matrix nanocomposites films of PMMA, with MWNT concentrations ranging from 0 to 0.5 wt%. Modified MWNT (AIBN-MWNT) were studied by Fourier transform infrared (FT-IR), Raman spectroscopy, X-ray Photoelectron Spectroscopy (XPS) and through visual observations in order to compare the dispersion in 2-propanone and toluene with that of pristine MWNT. Synthesized PMMA-AIBN-MWNT films were studied by FT-IR and Raman spectroscopy. Using FT-IR for the AIBN-MWNT it was not possible to identify any group or groups attached to the nanotubes. Raman spectroscopy shows a small modification in the Lorentzian peaks ratio I D/G of AIBN-MWNT, meanwhile XPS showed that atomic compositions does not change for AIBN-MWNT compared to the pristine nanotubes. Also by impedance it was analyzed the conductivity of PMMA-MWNT films and the results showed a threshold percolation at 0.5 wt%. FT-IR and Raman analyses for PMMA-AIBN-MWNT composite indicate a covalent bonding between PMMA and MWNT due to the opening of π-bonds of the nanotubes, which is related with a possible proposed reaction scheme. - Graphical abstract: Display Omitted - Highlights: • We used sonochemistry-in situ polymerization to disperse MWNT very soon in PMMA. • A high and homogenous dispersion of MWNT in PMMA was achieved. • The modification of MWNT by AIBN was analyzed using Raman. • A covalent bonding between PMMA and MWNT was analyzed by FT-IR and Raman. • According to the results of PMMA-MWNT it was proposed a scheme reaction

  8. Cytotoxicity effects of water dispersible oxidized multiwalled carbon nanotubes on marine alga, Dunaliella tertiolecta

    International Nuclear Information System (INIS)

    Wei Liping; Thakkar, Megha; Chen Yuhong; Ntim, Susana Addo; Mitra, Somenath; Zhang Xueyan

    2010-01-01

    The multiwalled carbon nanotubes (MWNTs) are novel materials with many potential applications. The ecotoxicity of these materials is not well studied, but it is essential for environmental impact assessments. In this study a commercially available MWNT material was carboxylated by microwave assisted acid oxidation. This functionalized MWNT (f-MWNT) material was examined for toxicity effects using unicellular marine green alga Dunaliella tertiolecta. D. tertiolecta was exposed to f-MWNT which had been pre-equilibrated with culture media for 24 h. Substantial growth lag phase was observed at 5 and 10 mg L -1 f-MWNT, and the resulting 50% effective concentration (EC50) on 96-h growth was 0.82 ± 0.08 mg L -1 . During mid-exponential growth phase cytotoxicity was evidenced at 10 mg L -1 f-MWNT in 36% reduction in exponential growth rate, 88 mV more positive glutathione redox potential (indicative of oxidative stress), 5% and 22% reduction in photosystem II (PSII) quantum yield and functional cross section respectively, all relative to the control cultures. However, when the large f-MWNT aggregates in the media with 10 mg L -1 f-MWNT were removed by 0.2 μm filtration, D. tertiolecta did not show significant cytotoxicity effects in any of the above parameters. This suggests that the cytotoxicity effects originated predominately from the large f-MWNT aggregates. Analysis of the f-MWNT aggregation dynamics suggests active interaction between f-MWNT and algal cells or cell metabolites that promoted f-MWNT aggregation formation. The f-MWNT particles were also found absorbed on algal cell surface. The direct contact between f-MWNT and cell surface was likely responsible for reduced PSII functional cross section and oxidative stress during exponential growth.

  9. Thermophysical properties of multi-wall carbon nanotube bundles at elevated temperatures up to 830 K

    International Nuclear Information System (INIS)

    Wang, Xinwei; Wang, Jianmei; Huang, Xiaopeng; Eres, Gyula

    2011-01-01

    In this paper we discuss the results of thermal transport measurements in multi-wall carbon nanotube (MWCNT) bundles at elevated temperatures. A novel generalized electrothermal technique (GET) was developed for measuring the thermal diffusivity ( ) and conductivity (k) of MWCNT bundles. The results show that the feeding current has a negligible effect on the thermal properties. The measured k is larger than the reported values for unaligned bundles, and is comparable to that of typical aligned arrays. Compared with experimental and theoretical data for individual CNTs, k of the MWCNT bundles is two to three orders of magnitude lower, suggesting that the thermal transport in CNT bundles is dominated by the thermal contact resistance of tube-to-tube junctions. The effective density for the two MWCNT bundles, which is difficult to measure using other techniques, was determined to be 116 kg/m3 and 234 kg/m3, respectively. The temperature dependences of and k at temperatures up to 830 K was obtained. slightly decreases with temperature while k exhibits a small increase with temperature up to 500 K and then decreases. For the first time, the behavior of specific heat cp(T) for CNTs above room temperature was determined. The specific heat is close to graphite at 300-400 K but is lower than that for graphite above 400 K, indicating that the behavior of phonons in MWCNT bundles is dominated by boundary scattering rather than by the three-phonon Umklapp process. The length of the mean curvature between two adjacent tube contact points in these bundles is estimated to be on the order of micrometer to millimeter. The analysis of the radiation heat loss suggests that it needs to be considered when measuring the thermophysical properties of micro/nano wires of high aspect ratios at elevated temperatures, especially for individual CNTs due to their extremely small diameter.

  10. Adsorption behavior of multi-walled carbon nanotubes for the removal of olaquindox from aqueous solutions

    International Nuclear Information System (INIS)

    Zhang, Lei; Xu, Tianci; Liu, Xueyan; Zhang, Yunyu; Jin, Hongjing

    2011-01-01

    Highlights: ► Removal of olaquindox—a hazardous pollutant using MWCNT was investigated. ► A comparative analysis showed MWCNT was highly efficient for the removal of olaquindox. ► Adsorption equilibrium was reached in 2.0 min following pseudo-second-order model. ► Physisorption and inner diffusion are the characteristics of the adsorption system. ► Langmuir adsorption isotherms are adequate for modeling the adsorption process. - Abstract: Multi-walled carbon nanotubes (MWCNT) were employed for the sorption of olaquindox (OLA) from aqueous solution. A detailed study of the adsorption process was performed by varying pH, ionic strength, sorbent amount, sorption time and temperature. The adsorption mechanism is probably the non-electrostatic π–π dispersion interaction and hydrophobic interaction between OLA and MWCNT. The adsorption efficiency could reach 99.7%, suggesting that MWCNT is excellent adsorbents for effective OLA removal from water. OLA adsorption kinetics were found to be very fast and equilibrium was reached within 2.0 min following the pseudo-second-order model with observed rate constants (k) of 0.169–1.048 g mg −1 min −1 (at varied temperatures). The overall rate process appeared to be influenced by both external mass transfer and intraparticle diffusion, but mainly governed by intraparticle diffusion. A rapid initial adsorption behavior occurred within a short period of time in this adsorption system. The sorption data could be well interpreted by the Langmuir model with the maximum adsorption capacity of 133.156 mg g −1 (293 K) of OLA on MWCNT. The mean energy of adsorption was calculated to be 0.124 kJ mol −1 (293 K) from the Dubinin–Radushkevich adsorption isotherm. Moreover, the thermodynamic parameters showed the spontaneous, exothermic and physical nature of the adsorption process.

  11. Efficient removal of cadmium using magnetic multiwalled carbon nanotube nanoadsorbents: equilibrium, kinetic, and thermodynamic study

    Energy Technology Data Exchange (ETDEWEB)

    Pashai Gatabi, Maliheh; Milani Moghaddam, Hossain, E-mail: Milani@umz.ac.ir [University of Mazandaran, Soid State Physics Department (Iran, Islamic Republic of); Ghorbani, Mohsen [Babol Noshirvani University of Technology, Chemical Engineering Department (Iran, Islamic Republic of)

    2016-07-15

    Adsorptive potential of maghemite decorated multiwalled carbon nanotubes (MWCNTs) for the removal of cadmium ions from aqueous solution was investigated. The magnetic nanoadsorbent was synthesized using a versatile and cost effective chemical route. Structural, magnetic and surface charge properties of the adsorbent were characterized using FTIR, XRD, TEM, VSM analysis and pH{sub PZC} determination. Batch adsorption experiments were performed under varied system parameters such as pH, contact time, initial cadmium concentration and temperature. Highest cadmium adsorption was obtained at pH 8.0 and contact time of 30 min. Adsorption behavior was kinetically studied using pseudo first-order, pseudo second-order, and Weber–Morris intra particle diffusion models among which data were mostly correlated to pseudo second-order model. Adsorbate-adsorbent interactions as a function of temperature was assessed by Langmuir, Freundlich, Dubinin–Radushkevich (D-R) and Temkin isotherm models from which Freundlich model had the highest consistency with the data. The adsorption capacity increased with increasing temperature and maximum Langmuir’s adsorption capacity was found to be 78.81 mg g{sup −1} at 298 K. Thermodynamic parameters and activation energy value suggest that the process of cadmium removal was spontaneous and physical in nature, which lead to fast kinetics and high regeneration capability of the nanoadsorbent. Results of this work are of great significance for environmental applications of magnetic MWCNTs as promising adsorbent for heavy metals removal from aqueous solutions.Graphical Abstract.

  12. Polyetheretherketone Hybrid Composites with Bioactive Nanohydroxyapatite and Multiwalled Carbon Nanotube Fillers

    Directory of Open Access Journals (Sweden)

    Chen Liu

    2016-12-01

    Full Text Available Polyetheretherketone (PEEK hybrid composites reinforced with inorganic nanohydroxyapatite (nHA and multiwalled carbon nanotube (MWNT were prepared by melt-compounding and injection molding processes. The additions of nHA and MWNT to PEEK were aimed to increase its elastic modulus, tensile strength, and biocompatibility, rendering the hybrids suitable for load-bearing implant applications. The structural behavior, mechanical property, wettability, osteoblastic cell adhesion, proliferation, differentiation, and mineralization of the PEEK/nHA-MWNT hybrids were studied. X-ray diffraction and SEM observation showed that both nHA and MWNT fillers are incorporated into the polymer matrix of PEEK-based hybrids. Tensile tests indicated that the elastic modulus of PEEK can be increased from 3.87 to 7.13 GPa by adding 15 vol % nHA and 1.88 vol % MWNT fillers. The tensile strength and elongation at break of the PEEK/(15% nHA-(1.88% MWNT hybrid were 64.48 MPa and 1.74%, respectively. Thus the tensile properties of this hybrid were superior to those of human cortical bones. Water contact angle measurements revealed that the PEEK/(15% nHA-(1.88% MWNT hybrid is hydrophilic due to the presence of nHA. Accordingly, hydrophilic PEEK/(15% nHA-(1.88% MWNT hybrid promoted the adhesion, proliferation, differentiation, and mineralization of murine MC3T3-E1 osteoblasts on its surface effectively on the basis of cell culture, fluorescence microscopy, MTT assay, WST-1 assay, alkaline phosphatase activity, and Alizarin red staining tests. Thus the PEEK/(15% nHA-(1.88% MWNT hybrid has the potential to be used for fabricating load-bearing bone implants.

  13. Synthesis and investigation of PMMA films with homogeneously dispersed multiwalled carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Pantoja-Castro, M.A., E-mail: m_pantojaq@yahoo.com.mx [Facultad de Ingeniería Química, Universidad Michoacana de San Nicolás de Hidalgo, Av. J. Múgica S/N Col., Villa Universidad, CP 58040 Morelia, Michoacán (Mexico); Pérez-Robles, J.F. [Centro de Investigación y de Estudios Avanzados del IPN, Unidad Querétaro, Libramiento Norponiente #2000, Fracc. Real de Juriquilla, CP 76230 Querétaro (Mexico); González-Rodríguez, H. [Facultad de Ingeniería Química, Universidad Michoacana de San Nicolás de Hidalgo, Av. J. Múgica S/N Col., Villa Universidad, CP 58040 Morelia, Michoacán (Mexico); Vorobiev-Vasilievitch, Y. [Centro de Investigación y de Estudios Avanzados del IPN, Unidad Querétaro, Libramiento Norponiente #2000, Fracc. Real de Juriquilla, CP 76230 Querétaro (Mexico); Martínez-Tejada, H.V. [Instituto de Energía, Materiales y Medio Ambiente, Universidad Pontificia Bolivariana, Circular 1 No. 70-01, Bloque 22, Medellín (Colombia); Velasco-Santos, C. [Centro de Física Aplicada y Tecnología Avanzada, Universidad Autónoma de México, Av. Boulevard Juriquilla, No. 3001 Juriquilla, CP 76230 Querétaro (Mexico)

    2013-07-15

    Multiwalled carbon nanotubes (MWNT) modified by 2.2′-azoiso-butyronitrile (AIBN) were incorporated into methyl methacrylate (MMA) by sonochemistry method, resulting in homogenous dispersion of MWNT, which makes possible to obtain flexible conductive polymer-matrix nanocomposites films of PMMA, with MWNT concentrations ranging from 0 to 0.5 wt%. Modified MWNT (AIBN-MWNT) were studied by Fourier transform infrared (FT-IR), Raman spectroscopy, X-ray Photoelectron Spectroscopy (XPS) and through visual observations in order to compare the dispersion in 2-propanone and toluene with that of pristine MWNT. Synthesized PMMA-AIBN-MWNT films were studied by FT-IR and Raman spectroscopy. Using FT-IR for the AIBN-MWNT it was not possible to identify any group or groups attached to the nanotubes. Raman spectroscopy shows a small modification in the Lorentzian peaks ratio I{sub D/G} of AIBN-MWNT, meanwhile XPS showed that atomic compositions does not change for AIBN-MWNT compared to the pristine nanotubes. Also by impedance it was analyzed the conductivity of PMMA-MWNT films and the results showed a threshold percolation at 0.5 wt%. FT-IR and Raman analyses for PMMA-AIBN-MWNT composite indicate a covalent bonding between PMMA and MWNT due to the opening of π-bonds of the nanotubes, which is related with a possible proposed reaction scheme. - Graphical abstract: Display Omitted - Highlights: • We used sonochemistry-in situ polymerization to disperse MWNT very soon in PMMA. • A high and homogenous dispersion of MWNT in PMMA was achieved. • The modification of MWNT by AIBN was analyzed using Raman. • A covalent bonding between PMMA and MWNT was analyzed by FT-IR and Raman. • According to the results of PMMA-MWNT it was proposed a scheme reaction.

  14. Multiwalled carbon nanotubes enhance electrochemical properties of titanium to determine in situ bone formation

    International Nuclear Information System (INIS)

    Sirivisoot, Sirinrath; Webster, Thomas J

    2008-01-01

    Multiwalled carbon nanotubes (MWCNTs) enhance osteoblast (bone-forming cell) calcium deposition compared to currently implanted materials (such as titanium). In this study, MWCNTs were grown out of nanopores anodized on titanium (MWCNT-Ti). The electrochemical responses of MWCNT-Ti were investigated in an attempt to ascertain if MWCNT-Ti can serve as novel in situ sensors of bone formation. For this purpose, MWCNT-Ti was subjected to a ferri/ferrocyanide redox couple and its electrochemical behavior measured. Cyclic voltammograms (CVs) showed an enhanced redox potential for the MWCNT-Ti. These redox signals were superior to that obtained with bare unmodified Ti, which did not sense either oxidation or reduction peaks in the CVs. A further objective of this study was to investigate the redox reactions of MWCNT-Ti in a solution of extracellular components secreted by osteoblasts in vitro. It was found that MWCNT-Ti exhibited well-defined and persistent CVs, similar to the ferri/ferrocyanide redox reaction. The higher electrodic performance and electrocatalytic activity of the MWCNT-Ti compared to the bare titanium observed in this study were likely due to the fact that MWCNTs enhanced direct electron transfer and facilitated double-layer effects, leading to a strong redox signal. Thus these results encourage the further study and modification of MWCNT-Ti to sense new bone growth in situ next to orthopedic implants and perhaps monitor other events (such as infection and/or harmful scar tissue formation) to improve the current clinical diagnosis of orthopedic implants

  15. The pulmonary inflammatory response to multiwalled carbon nanotubes is influenced by gender and glutathione synthesis.

    Science.gov (United States)

    Cartwright, Megan M; Schmuck, Stefanie C; Corredor, Charlie; Wang, Bingbing; Scoville, David K; Chisholm, Claire R; Wilkerson, Hui-Wen; Afsharinejad, Zahra; Bammler, Theodor K; Posner, Jonathan D; Shutthanandan, Vaithiyalingam; Baer, Donald R; Mitra, Somenath; Altemeier, William A; Kavanagh, Terrance J

    2016-10-01

    Inhalation of multiwalled carbon nanotubes (MWCNTs) during their manufacture or incorporation into various commercial products may cause lung inflammation, fibrosis, and oxidative stress in exposed workers. Some workers may be more susceptible to these effects because of differences in their ability to synthesize the major antioxidant and immune system modulator glutathione (GSH). Accordingly, in this study we examined the influence of GSH synthesis and gender on MWCNT-induced lung inflammation in C57BL/6 mice. GSH synthesis was impaired through genetic manipulation of Gclm, the modifier subunit of glutamate cysteine ligase, the rate-limiting enzyme in GSH synthesis. Twenty-four hours after aspirating 25µg of MWCNTs, all male mice developed neutrophilia in their lungs, regardless of Gclm genotype. However, female mice with moderate (Gclm heterozygous) and severe (Gclm null) GSH deficiencies developed significantly less neutrophilia. We found no indications of MWCNT-induced oxidative stress as reflected in the GSH content of lung tissue and epithelial lining fluid, 3-nitrotyrosine formation, or altered mRNA or protein expression of several redox-responsive enzymes. Our results indicate that GSH-deficient female mice are rendered uniquely susceptible to an attenuated neutrophil response. If the same effects occur in humans, GSH-deficient women manufacturing MWCNTs may be at greater risk for impaired neutrophil-dependent clearance of MWCNTs from the lung. In contrast, men may have effective neutrophil-dependent clearance, but may be at risk for lung neutrophilia regardless of their GSH levels. Copyright © 2016. Published by Elsevier B.V.

  16. Multiwall carbon nanotube-filled natural rubber: Electrical and mechanical properties

    Directory of Open Access Journals (Sweden)

    L. Bokobza

    2012-03-01

    Full Text Available The influence of multiwall carbon nanotube (MWNTs contents on electrical and mechanical properties of MWNTs-reinforced natural rubber (NR composites is studied. The volume resistivity of the composites decreases with increasing the MWNTs content and the electrical percolation threshold is reached at less than 1 phr of MWNTs (phr = parts of filler by weight per hundred parts of rubber. This is caused by the formation of conductive chains in the composites. Electrical measurements under uniaxial deformation of a composite carried out at a filler loading above the percolation threshold, indicate a gradual disconnection of the conducting network with the bulk deformation. The drop in the storage modulus G' with the shear strain amplitude (Payne effect is also attributed to a breakdown of the filler network. Considerable improvement in the stiffness is obtained upon incorporation of MWNTs in the polymer matrix but the main factor for reinforcement of NR by MWNTs appears to be their high aspect ratio rather than strong interfacial interaction with rubber. The tensile strength and the elongation at break of the composites are reduced with regard to the unfilled sample. This is probably due to the presence of some agglomerates that increase with the nanotube content. This hypothesis is confirmed by a cyclic loading of the composites where it is seen that the deformation at break occurs at a much higher level of strain in the second stretch than in the first one. The overall significant property improvements are the result of a better nanotube dispersion attributed to the combined use of tip sonication and cyclohexane as dispersion aids during composite processing.

  17. Removal of heavy metals from water using multistage functionalized multiwall carbon nanotubes

    Directory of Open Access Journals (Sweden)

    Budimirović Dragoslav

    2017-01-01

    Full Text Available The multistage synthesis of the multi-wall carbon nanotubes (MWCNT modified with polyamidoamine dendrimers, A1/ and A2/MWCNT, capable of cation removal, is presented in this work, as well as novel adsorbents based on these precursor materials and modified with goethite nano-deposit, α-FeOOH, A1/ and A2/MWCNT–α-FeO(OH adsorbents used for As(V removal. In a batch test, the influence of pH, contact time, initial ion concentration and temperature on adsorption efficiency were studied. Adsorption data modelling by the Langmuir isotherm, revealed good adsorption capacities (in mg g-1 of 18.8 for As(V and 60.1 and 44.2 for Pb2+ and Cd2+ on A2/MWCNT, respectively. Also, 27.6 and 29.8 mg g-1 of As(V on A1/ and A2/MWCNT–α-FeO(OH, respectively, were removed. Thermodynamic parameters showed that the adsorption is spontaneous and endothermic processes. Results of the study of influences of competitive ions: bicarbonate, sulfate, phosphate, silicate, chromate, fluoride and natural organic matter (NOM, i.e., humic acid (HA, showed the highest effect of phosphate on the decrease of arsenate adsorption. Time-dependent adsorption was best described by pseudo-second-order kinetic model and Weber–Morris model which predicted intra-particle diffusion as a rate-controlling step. Also, activation energy (Ea / kJ mol-1: 8.85 for Cd2+, 9.25 for Pb2+ and 7.98 for As(V, were obtained from kinetic data. [Project of the Serbian Ministry of Education, Science and Technological Development, Grant no. III45019 and Grant no. OI 172057

  18. Optimization and evaluation of chelerythrine nanoparticles composed of magnetic multiwalled carbon nanotubes by response surface methodology

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Yong [School of Life and Environmental Sciences, Guilin University of Electronic Technology, Guilin, Guangxi 541014 (China); Yuan, Yulin [Department of Clinical Laboratory, the People' s Hospital of Guangxi Zhuang Autonomous Region, Nanning, Guangxi 530021 (China); Zhou, Zhide; Liang, Jintao; Chen, Zhencheng [School of Life and Environmental Sciences, Guilin University of Electronic Technology, Guilin, Guangxi 541014 (China); Li, Guiyin, E-mail: liguiyin01@163.com [School of Life and Environmental Sciences, Guilin University of Electronic Technology, Guilin, Guangxi 541014 (China)

    2014-02-15

    In this study, a new chelerythrine nanomaterial targeted drug delivery system (Fe{sub 3}O{sub 4}/MWNTs-CHE) was designed with chelerythrine (CHE) as model of antitumor drug and magnetic multiwalled carbon nanotubes (Fe{sub 3}O{sub 4}/MWNTs) nanocomposites as drug carrier. The process and formulation variables of Fe{sub 3}O{sub 4}/MWNTs-CHE were optimized using response surface methodology (RSM) with a three-level, three-factor Box–Behnken design (BBD). Mathematical equations and response surface plots were used to relate the dependent and independent variables. The experimental results were fitted into second-order response surface model. When Fe{sub 3}O{sub 4}/MWNTs:CHE ratio was 20.6:1, CHE concentration was 172.0 μg/mL, temperature was 34.5 °C, the drug loading content and entrapment efficiency were 3.04 ± 0.17% and 63.68 ± 2.36%, respectively. The optimized Fe{sub 3}O{sub 4}/MWNTs-CHE nanoparticles were characterized by scanning electron microscopy (SEM), Zeta potential, in vitro drug release and MTT assays. The in vitro CHE drug release behavior from Fe{sub 3}O{sub 4}/MWNTs-CHE displayed a biphasic drug release pattern and followed Korsmeyer–Peppas model with Fickian diffusion mechanism for drug release. The results from MTT assays suggested that the Fe{sub 3}O{sub 4}/MWNTs-CHE could effectively inhibit the proliferation of human hepatoma cells (HepG2), which displayed time or concentration-dependent manner. All these preliminary studies were expected to provide a theoretical basis and offer new methods for preparation efficient magnetic targeted drug delivery systems.

  19. Effects of transferrin conjugated multi-walled carbon nanotubes in lung cancer delivery

    International Nuclear Information System (INIS)

    Singh, Rahul Pratap; Sharma, Gunjan; Sonali; Singh, Sanjay; Patne, Shashikant C.U.; Pandey, Bajarangprasad L.; Koch, Biplob; Muthu, Madaswamy S.

    2016-01-01

    The aim of this study was to develop multi-walled carbon nanotubes (MWCNT) which were covalently conjugated with transferrin by carbodiimide chemistry and loaded with docetaxel as a model drug for effective treatment of lung cancer in comparison with the commercial docetaxel injection (Docel™). D-Alpha-tocopheryl polyethylene glycol 1000 succinate (TPGS) was used as amphiphilic surfactant to improve the aqueous dispersity and biocompatibility of MWCNT. Human lung cancer cells (A549 cells) were employed as an in-vitro model to access cellular uptake, cytotoxicity, cellular apoptosis, cell cycle analysis, and reactive oxygen species (ROS) of the docetaxel/coumarin-6 loaded MWCNT. The cellular uptake results of transferrin conjugated MWCNT showed higher efficiency in comparison with free C6. The IC_5_0 values demonstrated that the transferrin conjugated MWCNT could be 136-fold more efficient than Docel™ after 24 h treatment with the A549 cells. Flow cytometry analysis confirmed that cancerous cells appeared significantly (P < 0.05) in the sub-G1 phase for transferrin conjugated MWCNT in comparison with Docel™. Results of transferrin conjugated MWCNT have showed better efficacy with safety than Docel™. - Highlights: • It shows the development of transferrin conjugated MWCNT formulation of DTX for the effective treatment of lung cancer. • Evaluated the cellular uptake, cytotoxicity, cellular apoptosis, cell cycle, and ROS level of the DTX/C6 loaded MWCNT. • The IC_5_0 values demonstrated that the transferrin conjugated MWCNT could be 136-fold more effective than Docel™. • Safety of the DTX formulations were studied by the measurements of ALP, LDH and total protein count levels in BAL fluid. • Results of transferrin conjugated MWCNT have showed better efficacy with safety than Docel™ in lung cancer delivery.

  20. Uptake and cytotoxic effects of multi-walled carbon nanotubes in human bronchial epithelial cells

    International Nuclear Information System (INIS)

    Hirano, Seishiro; Fujitani, Yuji; Furuyama, Akiko; Kanno, Sanae

    2010-01-01

    Carbon nanotubes (CNT) are cytotoxic to several cell types. However, the mechanism of CNT toxicity has not been fully studied, and dosimetric analyses of CNT in the cell culture system are lacking. Here, we describe a novel, high throughput method to measure cellular uptake of CNT using turbimetry. BEAS-2B, a human bronchial epithelial cell line, was used to investigate cellular uptake, cytotoxicity, and inflammatory effects of multi-walled CNT (MWCNT). The cytotoxicity of MWCNT was higher than that of crocidolite asbestos in BEAS-2B cells. The IC 50 of MWCNT was 12 μg/ml, whereas that of asbestos (crocidolite) was 678 μg/ml. Over the course of 5 to 8 h, BEAS-2B cells took up 17-18% of the MWCNT when they were added to the culture medium at a concentration of 10 μg/ml. BEAS-2B cells were exposed to 2, 5, or 10 μg/ml of MWCNT, and total RNA was extracted for cytokine cDNA primer array assays. The culture supernatant was collected for cytokine antibody array assays. Cytokines IL-6 and IL-8 increased in a dose dependent manner at both the mRNA and protein levels. Migration inhibitory factor (MIF) also increased in the culture supernatant in response to MWCNT. A phosphokinase array study using lysates from BEAS-2B cells exposed to MWCNT indicated that phosphorylation of p38, ERK1, and HSP27 increased significantly in response to MWCNT. Results from a reporter gene assays using the NF-κB or AP-1 promoter linked to the luciferase gene in transiently transfected CHO-KI cells revealed that NF-κB was activated following MWCNT exposure, while AP-1 was not changed. Collectively, MWCNT activated NF-κB, enhanced phosphorylation of MAP kinase pathway components, and increased production of proinflammatory cytokines in human bronchial epithelial cells.

  1. BisGMA-polyvinylpyrrolidone blend based nanocomposites reinforced with chitosan grafted f-multiwalled carbon nanotubes

    Directory of Open Access Journals (Sweden)

    A. Praharaj

    2015-01-01

    Full Text Available In this work, initially a non-destroyable surface grafting of acid functionalized multiwalled carbon nanotubes (f-MWCNTs with biopolymer chitosan (CS was carried out using glutaraldehyde as a cross-linking agent via the controlled covalent deposition method which was characterized by Fourier transform infrared spectroscopy (FTIR and scanning electron microscopy (SEM. Then, BisGMA (bisphenol-A glycidyldimethacrylate-polyvinylpyrrolidone (PVP blend was prepared (50:50 wt% by a simple sonication method. The CS grafted f-MWCNTs (CS/f-MWCNTs were finally dispersed in BisGMA-PVP blend (BGP50 system in different compositions i.e. 0, 2, 5 and 7 wt% and pressed into molds for the fabrication of reinforced nanocomposites which were characterized by SEM. Nanocomposites reinforced with 2 wt% raw MWCNTs and acid f-MWCNTs were also fabricated and their properties were studied in detail. The results of comparative study report lower values of the investigated properties in nanocomposites with 2 wt% raw and f-MWCNTs than the one with 2 wt% CS/f-MWCNTs proving it to be a better reinforcing nanofiller. Further, the mechanical behavior of the nanocomposites with various CS/f-MWCNTs content showed a dramatic increase in Young’s Modulus, tensile strength, impact strength and hardness along with improved dynamic mechanical, thermal and electrical properties at 5 wt% content of CS/f-MWCNTs. The addition of CS/f-MWCNTs also resulted in reduced corrosion and swelling properties. Thus, the fabricated nanocomposites with optimum nanofiller content could serve as low cost and light weight structural, thermal and electrical materials compatible in various corrosive and solvent based environments.

  2. Ni-coated multi-walled carbon nanotubes enhanced the magnetorheological performance of magnetorheological gel

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Pingan; Yu, Miao, E-mail: yumiao@cqu.edu.cn; Fu, Jie [Chongqing University, Key Lab for Optoelectronic Technology and Systems, Ministry of Education, College of Optoelectronic Engineering (China)

    2016-03-15

    As a kind of new Magnetorheological (MR) material, MR Gel (MRG) can be regarded as the analog of MR fluid (MRF), which can overcome the iron particles sedimentation and unstable application of MRF. Normally, the storage modulus of conventional MRG is relatively small, although it has a very high relative MR effect. Therefore, practical engineering application of conventional MRG has been restricted more or less. In this work, an MRG with high magneto-induced shear storage modulus and excellent relative MR effect has been fabricated by incorporating Ni-coated multi-walled carbon nanotubes (Ni-coated MWCNTs). And several polyurethane-based MRG composites with the addition of Ni-coated MWCNTs were prepared. The dynamic mechanical property of those MRG composites with applying magnetic field is researched through an advanced commercial rheometer. The experimental results indicated that the initial storage modulus and magneto-induced modulus in sample 4 (containing 6 wt% of the Ni-coated MWCNTs) were approximately 4.45 and 2.27 times than that in the sample 1 (without Ni-coated MWCNTs). Moreover, the relative MR effect of sample 4 can reach 3427 %. The high modulus of sample 4 can be mainly attributed to the following points. One is the Ni-coated MWCNTs can be aligned along the direction of the magnetic field within the matrix which provided a better reinforcing efficiency. The other is Ni-coated MWCNTs can be made to form a better bonding between the iron particles and the matrix. It is concluded that this study provides a meaningful way to improve the mechanical properties of MRG and expected to promote the application of MRG in practice.

  3. Photothermal effects of multi-walled carbon nanotubes on the viability of BT-474 cancer cells

    Energy Technology Data Exchange (ETDEWEB)

    Chou, Hung-Tao [Department of Materials Science and Engineering, National Tsing Hua University, No. 101, Sec. 2 Kuang-Fu Rd., Hsin-chu 30013, Taiwan (China); Wang, Tsung-Pao [Department of Medical Science, National Tsing Hua University, No. 101, Sec. 2 Kuang-Fu Rd., Hsin-chu 30013, Taiwan (China); Lee, Chi-Young [Department of Materials Science and Engineering, National Tsing Hua University, No. 101, Sec. 2 Kuang-Fu Rd., Hsin-chu 30013, Taiwan (China); Tai, Nyan-Hwa, E-mail: nhtai@mx.nthu.edu.tw [Department of Materials Science and Engineering, National Tsing Hua University, No. 101, Sec. 2 Kuang-Fu Rd., Hsin-chu 30013, Taiwan (China); Chang, Hwan-You, E-mail: hychang@mx.nthu.edu.tw [Department of Medical Science, National Tsing Hua University, No. 101, Sec. 2 Kuang-Fu Rd., Hsin-chu 30013, Taiwan (China)

    2013-03-01

    Functionalized multi-walled carbon nanotubes (f-MWCNTs) were conjugated to an antibody of BT-474 cancer cells (f-MWCNTs-ab), and the photothermal effect of the f-MWCNTs-ab for BT-474 cancer cell destruction was demonstrated. After near-infrared irradiation, the f-MWCNTs-ab were more capable of killing cancer cells and possessed higher cell specificity than f-MWCNTs. Quantitative results showed that the viability of the cancer cells was affected by the concentration of the f-MWCNTs-ab solution, irradiation time, and settling time after irradiation. The membrane impermeable fluorescence dye ethidium bromide was used to detect cell viability after near-infrared irradiation, and the results agreed with those obtained from the Alamar Blue cell viability assay. The EtBr fluorescence results suggest that the cell membrane, attached to f-MWCNTs-ab, was damaged after irradiation, which led to cell death and necrosis. Using confocal microscopy, a few f-MWCNTs-ab were detected in the cell, indicating the endocytosis effect. The results not only explain the improved efficiency of thermotherapy but also indicate that necrosis may result from protein denaturation attributing to the heated f-MWCNTs-ab in the cell. Highlights: Black-Right-Pointing-Pointer f-MWCNTs conjugated with anti-HER2 antibody by chemical method. Black-Right-Pointing-Pointer Kill breast cancer cells by using low dose f-MWCNTs-ab due to photothermal effect. Black-Right-Pointing-Pointer Use EtBr fluorescent to prove that the cell membrane was broken by heated f-MWCNTs. Black-Right-Pointing-Pointer Few f-MWCNTs-ab were detected in the cell indicating the endocytosis effect. Black-Right-Pointing-Pointer Necrosis may result from protein denaturation due to contact with the heated CNTs.

  4. High Performance Flexible Pseudocapacitor based on Nano-architectured Spinel Nickel Cobaltite Anchored Multiwall Carbon Nanotubes

    International Nuclear Information System (INIS)

    Shakir, Imran

    2014-01-01

    Highlights: • Two-step fabrication method for nano-architectured spinel nickel cobaltite (NiCo 2 O 4 ) anchored MWCNTs composite. • High performance flexible energy-storage devices. • The NiCo 2 O 4 anchored MWCNTs Exhibits 2032 Fg −1 capacitance which is 1.62 times greater than pristine NiCo 2 O 4 at 1 Ag −1 . - Abstract: We demonstrate a facile two-step fabrication method for nano-architectured spinel nickel cobaltite (NiCo 2 O 4 ) anchored multiwall carbon nanotubes (MWCNTs) based electrodes for high performance flexible energy-storage devices. As electrode materials for flexible supercapacitors, the NiCo 2 O 4 anchored MWCNTs exhibits a high specific capacitance of 2032 Fg −1 , which is nearly 1.62 times greater than pristine NiCo 2 O 4 nanoflakes at 1 Ag −1 . The synthesized NiCo 2 O 4 anchored MWCNTs composite shows excellent rate performance (83.96% capacity retention at 30 Ag −1 ) and stability with coulombic efficiency over 96% after 5,000 cycles when being fully charged/discharged at 1 Ag −1 . Furthermore, NiCo 2 O 4 anchored MWCNTs achieve a maximum energy density of 48.32 Whkg −1 at a power density of 480 Wkg −1 which is 60% higher than pristine NiCo 2 O 4 electrode and significantly outperformed electrode materials based on NiCo 2 O 4 which are currently used in the state-of-the-art supercapacitors throughout the literature. This superior rate performance and high-capacity value offered by NiCo 2 O 4 anchored MWCNTs is mainly due to enhanced electronic and ionic conductivity, which provides a short diffusion path for ions and an easy access of electrolyte flow to nickel cobaltite redox centers besides the high conductivity of MWCNTs

  5. Functional characteristics, wettability properties and cytotoxic effect of starch film incorporated with multi-walled and hydroxylated multi-walled carbon nanotubes.

    Science.gov (United States)

    Shahbazi, Mahdiyar; Rajabzadeh, Ghadir; Sotoodeh, Shahnaz

    2017-11-01

    Two types of multi-walled carbon nanotubes (CNT and CNT-OH) at different levels (0.1-0.9wt%) were introduced into starch matrix in order to modify its functional properties. The optimum concentration of each nanotube was selected based on the results of water solubility, water permeability and mechanical experiments. The physico-mechanical data showed that CNT up to 0.7wt% led to a notable increase in water resistance, water barrier property and tensile strength, whilst regarding CNT-OH, these improvements found at 0.9wt%. Therefore, effects of optimized level of each nanotube on the starch film were evaluated by XRD, surface hydrophobicity, wettability and surface energy tests. XRD revealed that the position of starch characteristic peak shifted to higher degree after nanotubes introducing. The hydrophobic character of the film was greatly increased with incorporation of nanoparticles, as evidenced by increased contact angle with greatest value regarding CNT-OH. Moreover, CNT-OH notably decreased the surface free energy of the starch film. Finally, the conformity of both nanocomposites with actual food regulations on biodegradable materials was tested by cytotoxicity assay to evaluate the possibility of application in food packaging sector. Both nanocomposite films had potential of cytotoxic effects, since they could increase cytoplasmic lactate dehydrogenase release from L-929 fibroblast cells in contact with their surface. Copyright © 2017 Elsevier B.V. All rights reserved.

  6. SnS2 nanoflakes decorated multiwalled carbon nanotubes as high performance anode materials for lithium-ion batteries

    International Nuclear Information System (INIS)

    Sun, Hongyu; Ahmad, Mashkoor; Luo, Jun; Shi, Yingying; Shen, Wanci; Zhu, Jing

    2014-01-01

    Graphical abstract: The synthesized SnS 2 nanoflakes decorated multiwalled carbon nanotubes hybrid structures exhibit large reversible capacity, superior cycling performance, and good rate capability as compared to pure SnS 2 nanoflakes. - Highlights: • Synthesis of SnS 2 nanoflakes decorated multiwalled carbon nanotubes hybrid structures. • Simple solution-phase approach. • Morphology feature of SnS 2 . • Enhanced performance as Li-ion batteries. - Abstract: SnS 2 nanoflakes decorated multiwalled carbon nanotubes (MWCNTs) hybrid structures are directly synthesized via a simple solution-phase approach. The as-prepared SnS 2 /MWCNTs structures are investigated as anode materials for Li-ion batteries as compared with SnS 2 nanoflakes. It has been found that the composite structure exhibit excellent lithium storage performance with a large reversible capacity, superior cycling performance, and good rate capability as compared to pure SnS 2 nanoflakes. The first discharge and charge capacities have been found to be 1416 and 518 mA h g −1 for SnS 2 /MWCNTs composite electrodes at a current density of 100 mA g −1 between 5 mV and 1.15 V versus Li/Li + . A stable reversible capacity of ∼510 mA h g −1 is obtained for 50 cycles. The improved electrochemical performance may be attributed to the flake-morphology feature of SnS 2 and the addition of MWCNTs that can hinder the agglomeration of the active materials and improve the conductivity of the composite electrode simultaneously

  7. SnS{sub 2} nanoflakes decorated multiwalled carbon nanotubes as high performance anode materials for lithium-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Hongyu [Beijing National Center for Electron Microscopy, The State Key Laboratory of New Ceramics and Fine Processing, Department of Material Science and Engineering, Tsinghua University, Beijing 100084 (China); Ahmad, Mashkoor, E-mail: mashkoorahmad2003@yahoo.com [Nanomaterials Research Group (NRG), Physics Division, PINSTECH, P.O. Nilore, Islamabad (Pakistan); Luo, Jun [Beijing National Center for Electron Microscopy, The State Key Laboratory of New Ceramics and Fine Processing, Department of Material Science and Engineering, Tsinghua University, Beijing 100084 (China); Shi, Yingying; Shen, Wanci [Laboratory of Advanced Materials, Department of Material Science and Engineering, Tsinghua University, Beijing 100084 (China); Zhu, Jing, E-mail: jzhu@mail.tsinghua.edu.cn [Beijing National Center for Electron Microscopy, The State Key Laboratory of New Ceramics and Fine Processing, Department of Material Science and Engineering, Tsinghua University, Beijing 100084 (China)

    2014-01-01

    Graphical abstract: The synthesized SnS{sub 2} nanoflakes decorated multiwalled carbon nanotubes hybrid structures exhibit large reversible capacity, superior cycling performance, and good rate capability as compared to pure SnS{sub 2} nanoflakes. - Highlights: • Synthesis of SnS{sub 2} nanoflakes decorated multiwalled carbon nanotubes hybrid structures. • Simple solution-phase approach. • Morphology feature of SnS{sub 2}. • Enhanced performance as Li-ion batteries. - Abstract: SnS{sub 2} nanoflakes decorated multiwalled carbon nanotubes (MWCNTs) hybrid structures are directly synthesized via a simple solution-phase approach. The as-prepared SnS{sub 2}/MWCNTs structures are investigated as anode materials for Li-ion batteries as compared with SnS{sub 2} nanoflakes. It has been found that the composite structure exhibit excellent lithium storage performance with a large reversible capacity, superior cycling performance, and good rate capability as compared to pure SnS{sub 2} nanoflakes. The first discharge and charge capacities have been found to be 1416 and 518 mA h g{sup −1} for SnS{sub 2}/MWCNTs composite electrodes at a current density of 100 mA g{sup −1} between 5 mV and 1.15 V versus Li/Li{sup +}. A stable reversible capacity of ∼510 mA h g{sup −1} is obtained for 50 cycles. The improved electrochemical performance may be attributed to the flake-morphology feature of SnS{sub 2} and the addition of MWCNTs that can hinder the agglomeration of the active materials and improve the conductivity of the composite electrode simultaneously.

  8. The impact of different multi-walled carbon nanotubes on the X-band microwave absorption of their epoxy nanocomposites.

    Science.gov (United States)

    Che, Bien Dong; Nguyen, Bao Quoc; Nguyen, Le-Thu T; Nguyen, Ha Tran; Nguyen, Viet Quoc; Van Le, Thang; Nguyen, Nieu Huu

    2015-01-01

    Carbon nanotube (CNT) characteristics, besides the processing conditions, can change significantly the microwave absorption behavior of CNT/polymer composites. In this study, we investigated the influence of three commercial multi-walled CNT materials with various diameters and length-to-diameter aspect ratios on the X-band microwave absorption of epoxy nanocomposites with CNT contents from 0.125 to 2 wt%, prepared by two dispersion methods, i.e. in solution with surfactant-aiding and via ball-milling. The laser diffraction particle size and TEM analysis showed that both methods produced good dispersions at the microscopic level of CNTs. Both a high aspect ratio resulting in nanotube alignment trend and good infiltration of the matrix in the individual nanotubes, which was indicated by high Brookfield viscosities at low CNT contents of CNT/epoxy dispersions, are important factors to achieve composites with high microwave absorption characteristics. The multi-walled carbon nanotube (MWCNT) with the largest aspect ratio resulted in composites with the best X-band microwave absorption performance, which is considerably better than that of reported pristine CNT/polymer composites with similar or lower thicknesses and CNT loadings below 4 wt%. A high aspect ratio of CNTs resulting in microscopic alignment trend of nanotubes as well as a good level of micro-scale CNT dispersion resulting from good CNT-matrix interactions are crucial to obtain effective microwave absorption performance. This study demonstrated that effective radar absorbing MWCNT/epoxy nanocomposites having small matching thicknesses of 2-3 mm and very low filler contents of 0.25-0.5 wt%, with microwave energy absorption in the X-band region above 90% and maximum absorption peak values above 97%, could be obtained via simple processing methods, which is promising for mass production in industrial applications. Graphical AbstractComparison of the X-band microwave reflection loss of epoxy composites of

  9. Thermal characteristics of carbon fiber reinforced epoxy containing multi-walled carbon nanotubes

    Directory of Open Access Journals (Sweden)

    Jin-woo Lee

    2018-06-01

    Full Text Available The material with irregular atomic structures such as polymer material exhibits low thermal conductivity because of the complex structural properties. Even materials with same atomic configurations, thermal conductivity may be different based on their structural properties. It is expected that nanoparticles with conductivity will change non-conductive polymer base materials to electrical conductors, and improve the thermal conductivity even with extremely small filling amount. Nano-composite materials contain nanoparticles with a higher surface ratio which makes the higher interface percentage to the total surface of nanoparticles. Therefore, thermal resistance of the interface becomes a dominating factor determines the effective thermal conductivity in nano-composite materials. Carbon fiber has characteristic of resistance or magnetic induction and Also, Carbon nanotube (CNT has electronic and thermal property. It can be applied for heating system. These characteristic are used as heating composite. In this research, the exothermic characteristics of Carbon fiber reinforced composite added CNT were evaluated depend on CNT length and particle size. It was found that the CNT dispersed in the resin reduces the resistance between the interfaces due to the decrease in the total resistance of the heating element due to the addition of CNTs. It is expected to improve the life and performance of the carbon fiber composite material as a result of the heating element resulting from this paper. Keywords: Carbon Nanotube (CNT, Carbon Fiber Reinforcement Plastic (CFRP, Heater, Exothermic characteristics

  10. Electromechanical properties of multi-walled carbon nano-tubes; Proprietes electromecaniques des nanotubes de carbone multiparois

    Energy Technology Data Exchange (ETDEWEB)

    Lefevre, R

    2005-12-15

    In this PhD thesis, we tackled theoretically and experimentally the problem of designing nano-electromechanical systems (NEMS) based on multi-walled carbon nano-tubes (MWCNTs). Furthermore, we applied our know-how to perform components like switches. We developed a theoretical model to describe the deflection of a suspended MWCNT stressed by an attractive electrostatic force. Our model highlights a scaling law linking up the electrostatic deflection, geometrical, electrical and physical parameters of MWCNTs based NEMS. This result constitutes a practical designing tool because it predicts their electromechanical behaviour on a 'large' range of operational parameters. At the same time, we developed several processes to fabricate nano-structures incorporating a suspended MWCNT electrostatically actuated. Among these different structures, the simplest was used to develop a method for probing electromechanical properties of MWCNTs. Our method is based on atomic force microscopy measurements on a doubly clamped suspended MWCNT electrostatically deflected by a drive voltage. These measurements show clearly for different MWCNTs (different diameter and length) the existence of such scaling law in agreement with the continuum model prediction. From these results, we extracted the Young's modulus of MWCNTs. For diameters smaller than 30 nm it is constant and its average value equals 400 GPa. Above, we observed a strong decrease that could be explained by the entry in a non-linear regime of deformation. Finally, we show the realization of an electromechanical switch based on a suspended MWCNT which presents good switching behaviour. (author)

  11. Simultaneous electrochemical determination of dopamine and paracetamol on multiwalled carbon nanotubes/graphene oxide nanocomposite-modified glassy carbon electrode.

    Science.gov (United States)

    Cheemalapati, Srikanth; Palanisamy, Selvakumar; Mani, Veerappan; Chen, Shen-Ming

    2013-12-15

    In the present study, multiwalled carbon nanotubes (MWCNT)/graphene oxide (GO) nanocomposite was prepared by homogenous dispersion of MWCNT and GO and used for the simultaneous voltammetric determination of dopamine (DA) and paracetamol (PA). The TEM results confirmed that MWCNT walls were wrapped well with GO sheets. The MWCNT/GO nanocomposite showed superior electrocatalytic activity towards the oxidation of DA and PA, when compared with either pristine MWCNT or GO. The major reason for the efficient simultaneous detection of DA and PA at nanocomposite was the synergistic effect between MWCNT and GO. The electrochemical oxidation of DA and PA was investigated by cyclic voltammetry, differential pulse voltammetry and amperometry. The nanocomposite modified electrode showed electrocatalytic oxidation of DA and PA in the linear response range from 0.2 to 400 µmol L(-1) and 0.5 to 400 µmol L(-1) with the detection limit of 22 nmol L(-1) and 47 nmol L(-1) respectively. The proposed sensor displayed good selectivity, sensitivity, stability with appreciable consistency and precision. © 2013 Elsevier B.V. All rights reserved.

  12. Determination of cyanide in wastewaters using modified glassy carbon electrode with immobilized silver hexacyanoferrate nanoparticles on multiwall carbon nanotube

    International Nuclear Information System (INIS)

    Noroozifar, Meissam; Khorasani-Motlagh, Mozhgan; Taheri, Aboozar

    2011-01-01

    Research highlights: → GC electrode modified with silver hexacyanoferrate nanoparticles (SHFNPs) immobilized on MWCNT. → Modified electrode use for determination of Cyanide in waste water. → The detection limit of the sensor is 8.3 nM. → The linear range is from 40.0 nM to 150.0 μM. - Abstract: The sensitive determination of cyanide in wastewaters using modified GC electrode with silver hexacyanoferrate nanoparticles (SHFNPs) immobilized on multiwall carbon nanotube (MWCNT) was reported. The immobilization of SHFNPs on MWCNT was confirmed by transmission electron microscopy (TEM). The TEM image showed that the SHFNPs retained the spherical morphology after immobilized on MWCNT. The size of SHFNPs was examined around 27 nm. The GC/MWCNT-SHFNPs was used for the determination of cyanide in borax buffer (BB) solution (pH 8.0). Using square wave voltammetry, the current response of cyanide increases linearly while increasing its concentration from 40.0 nM to 150.0 μM and a detection limit was found to be 8.3 nM (S/N = 3). The present modified electrode was also successfully used for the determination of 5.0 μM cyanide in the presence of common contaminants at levels presenting in industrial wastewaters. The practical application of the present modified electrode was demonstrated by measuring the concentration of cyanide in industrial wastewater samples. Moreover, the studied sensor exhibited high sensitivity, good reproducibility and long-term stability.

  13. Electromechanical properties of multi-walled carbon nano-tubes; Proprietes electromecaniques des nanotubes de carbone multiparois

    Energy Technology Data Exchange (ETDEWEB)

    Lefevre, R.

    2005-12-15

    In this PhD thesis, we tackled theoretically and experimentally the problem of designing nano-electromechanical systems (NEMS) based on multi-walled carbon nano-tubes (MWCNTs). Furthermore, we applied our know-how to perform components like switches. We developed a theoretical model to describe the deflection of a suspended MWCNT stressed by an attractive electrostatic force. Our model highlights a scaling law linking up the electrostatic deflection, geometrical, electrical and physical parameters of MWCNTs based NEMS. This result constitutes a practical designing tool because it predicts their electromechanical behaviour on a 'large' range of operational parameters. At the same time, we developed several processes to fabricate nano-structures incorporating a suspended MWCNT electrostatically actuated. Among these different structures, the simplest was used to develop a method for probing electromechanical properties of MWCNTs. Our method is based on atomic force microscopy measurements on a doubly clamped suspended MWCNT electrostatically deflected by a drive voltage. These measurements show clearly for different MWCNTs (different diameter and length) the existence of such scaling law in agreement with the continuum model prediction. From these results, we extracted the Young's modulus of MWCNTs. For diameters smaller than 30 nm it is constant and its average value equals 400 GPa. Above, we observed a strong decrease that could be explained by the entry in a non-linear regime of deformation. Finally, we show the realization of an electromechanical switch based on a suspended MWCNT which presents good switching behaviour. (author)

  14. Fabrication and characterization of ZnO-coated multi-walled carbon nanotubes with enhanced photocatalytic activity

    International Nuclear Information System (INIS)

    Jiang Linqin; Gao Lian

    2005-01-01

    Through noncovalent modification of multi-walled carbon nanotubes (MWNTs) with the dispersant of sodium dodecyl sulfate (SDS), ZnO nanocrystals-coated MWNTs composite was fabricated. The electrostatic interaction mechanism is used to illustrate the formation of ZnO/MWNTs nanocomposite. The ZnO-coated MWNTs composite shows a small blue-shift absorption compared with pure ZnO nanomaterial and preserves the electronic energy states of MWNTs. The photocatalytic experiments exhibit that this composite has a higher photocatalytic activity than ZnO bulk material or the mechanical mixture of MWNTs and ZnO

  15. Different cellular response mechanisms contribute to the length-dependent cytotoxicity of multi-walled carbon nanotubes

    OpenAIRE

    Liu, Dun; Wang, Lijun; Wang, Zhigang; Cuschieri, Alfred

    2012-01-01

    To date, there has not been an agreement on the best methods for the characterisation of multi-walled carbon nanotube (MWCNT) toxicity. The length of MWCNTs has been identified as a factor in in vitro and in vivo studies, in addition to their purity and biocompatible coating. Another unresolved issue relates to the variable toxicity of MWCNTs on different cell types. The present study addressed the effects of MWCNTs' length on mammalian immune and epithelial cancer cells RAW264.7 and MCF-7, r...

  16. Cytocompatibility studies of vertically-aligned multi-walled carbon nanotubes: Raw material and functionalized by oxygen plasma

    Energy Technology Data Exchange (ETDEWEB)

    Lobo, A.O., E-mail: loboao@yahoo.com [Laboratorio Associado de Sensores e Materiais, INPE, Sao Jose dos Campos/SP (Brazil); Instituto Tecnologico de Aeronautica, ITA, Sao Jose dos Campos/SP (Brazil); Laboratorio de Nanotecnologia Biomedica, Universidade do Vale do Paraiba, Sao Jose dos Campos/SP (Brazil); Corat, M.A.F. [Centro Multidisciplinar para Investigacao Biologica na Area da Ciencia em Animais de Laboratorio, CEMIB, UNICAMP,