Large-scale synthesis and microwave absorption enhancement of actinomorphic tubular ZnO/CoFe2O4 nanocomposites.

Science.gov (United States)

Cao, Jing; Fu, Wuyou; Yang, Haibin; Yu, Qingjiang; Zhang, Yanyan; Liu, Shikai; Sun, Peng; Zhou, Xiaoming; Leng, Yan; Wang, Shuangming; Liu, Bingbing; Zou, Guangtian

2009-04-09

Actinomorphic tubular ZnO/CoFe(2)O(4) nanocomposites were fabricated in large scale via a simple solution method at low temperature. The phase structures, morphologies, particle size, shell thickness, chemical compositions of the composites have been characterized by X-ray diffraction (XRD), field emission scanning electron microscope (FESEM), energy dispersive X-ray spectroscopy (EDS), and transmission electron microscopy (TEM). The as-synthesized nanocomposites were uniformly dispersed into the phenolic resin then the mixture was pasted on metal plate with the area of 200 mm x 200 mm as the microwave absorption test plate. The test of microwave absorption was carried out by the radar-absorbing materials (RAM) reflectivity far field radar cross-section (RCS) method. The range of microwave absorption is from 2 to 18 Hz and the best microwave absorption reach to 28.2 dB at 8.5 Hz. The results indicate that the composites are of excellence with respect to microwave absorption.

Emission analysis of Tb3+ -and Sm3+ -ion-doped (Li2 O/Na2 O/K2 O) and (Li2 O + Na2 O/Li2 O + K2 O/K2 O + Na2 O)-modified borosilicate glasses.

Science.gov (United States)

Naveen Kumar Reddy, B; Sailaja, S; Thyagarajan, K; Jho, Young Dahl; Sudhakar Reddy, B

2018-05-01

Four series of borosilicate glasses modified by alkali oxides and doped with Tb 3+ and Sm 3+ ions were prepared using the conventional melt quenching technique, with the chemical composition 74.5B 2 O 3 + 10SiO 2 + 5MgO + R + 0.5(Tb 2 O 3 /Sm 2 O 3 ) [where R = 10(Li 2 O /Na 2 O/K 2 O) for series A and C, and R = 5(Li 2 O + Na 2 O/Li 2 O + K 2 O/K 2 O + Na 2 O) for series B and D]. The X-ray diffraction (XRD) patterns of all the prepared glasses indicate their amorphous nature. The spectroscopic properties of the prepared glasses were studied by optical absorption analysis, photoluminescence excitation (PLE) and photoluminescence (PL) analysis. A green emission corresponding to the 5 D 4 → 7 F 5 (543 nm) transition of the Tb 3+ ions was registered under excitation at 379 nm for series A and B glasses. The emission spectra of the Sm 3+ ions with the series C and D glasses showed strong reddish-orange emission at 600 nm ( 4 G 5/2 → 6 H 7/2 ) with an excitation wavelength λ exci = 404 nm ( 6 H 5/2 → 4 F 7/2 ). Furthermore, the change in the luminescence intensity with the addition of an alkali oxide and combinations of these alkali oxides to borosilicate glasses doped with Tb 3+ and Sm 3+ ions was studied to optimize the potential alkali-oxide-modified borosilicate glass. Copyright © 2017 John Wiley & Sons, Ltd.

Physical and optical studies of BaO-TeO2-TiO2-B2O3 glasses containing Cu2+ transition metal ion

Science.gov (United States)

Srinivas, B.; Kumar, R. Vijaya; Hameed, Abdul; Sagar, D. Karuna; Chary, M. Narasimha; Shareefuddin, Md.

2018-05-01

Glasses with the composition xBaO-(30-x) TeO2-10TiO2-59B2O3-1CuO (where x = 10, 15, 20 and 25 mole %) were prepared by melt quenching technique. The XRD studies were made on these glass samples at room temperature. The amorphous nature of the glass samples was confirmed from the XRD patterns. The physical parameters such as density (ρ), molar volume (Vm), average boron-boron separation (dB-B) and oxygen packing density (OPD) were calculated. The change in density and molar volume has been investigated in terms of the variation of BaO in the glass composition. The optical absorption spectra have been recorded at room temperature. The values of optical band gap have been estimated from the ASF and Tauc's methods. Both Tauc's and ASF methods have been showing progressively increasing indirect optical band gap values with the increase of BaO concentrations.

Luminescence and energy transfer of Tb3+-doped BaO-Gd2O3-Al2O3-B2O3-SiO2 glasses.

Science.gov (United States)

Zuo, Chenggang; Huang, Jinze; Liu, Shaoyou; Xiao, Anguo; Shen, Youming; Zhang, Xiangyang; Zhou, Zhihua; Zhu, Ligang

2017-12-05

Transparent Tb 3+ -doped BaO-Gd 2 O 3 -Al 2 O 3 -B 2 O 3 -SiO 2 glasses with the greater than 4g/cm 3 were prepared by high temperature melting method and its luminescent properties have been investigated by measured UV-vis transmission, excitation, emission and luminescence decay spectra. The transmission spectrum shows there are three weak absorption bands locate at about 312, 378 and 484nm in the glasses and it has good transmittance in the visible spectrum region. Intense green emission can be observed under UV excitation. The effective energy transfer from Gd 3+ ion to Tb 3+ ion could occur and sensitize the luminescence of Tb 3+ ion. The green emission intensity of Tb 3+ ion could change with the increasing SiO 2 /B 2 O 3 ratio in the borosilicate glass matrix. With the increasing concentration of Tb 3+ ion, 5 D 4 → 7 F J transitions could be enhanced through the cross relaxation between the two nearby Tb 3+ ions. Luminescence decay time of 2.12ms from 546nm emission is obtained. The results indicate that Tb 3+ -doped BaO-Gd 2 O 3 -Al 2 O 3 -B 2 O 3 -SiO 2 glasses would be potential scintillating material for applications in X-ray imaging. Copyright © 2017 Elsevier B.V. All rights reserved.

Optical absorption and spectroscopic properties of thulium doped (TeO{sub 2})(Nb{sub 2}O{sub 5})(TiO{sub 2}) glasses

Energy Technology Data Exchange (ETDEWEB)

Kabalci, Idris [Department of Physics Education, Education Faculty, Harran University, Sanliurfa (Turkey); Tay, Turgay [Department of Chemistry, Science Faculty, Anadolu University, Eskisehir (Turkey); Oezen, Goenuel [Department of Physics, Science and Arts Faculty, Istanbul Technical University, Istanbul (Turkey)

2011-09-15

A type of thulium doped tellurite based optical glasses was prepared through conventional melt quenching technique. In the experiments, the effect of different Tm{sup 3+} ion concentration and glass composition on optical properties of (TeO{sub 2}){sub (1-x-y)}(Nb{sub 2}O{sub 5}){sub (x)}(TiO{sub 2}){sub (y)} (x=0.05, 0.10, 0.15, and 0.20 mol) glasses have been investigated by using UV-VIS-NIR optical spectrophotometry measurements in a wavelength range 400-2000 nm. Considering absorption measurements for the 1.0mol% Tm{sup 3+} doped of (TeO{sub 2}){sub 0.9}(Nb{sub 2}O{sub 5}){sub 0.05}(TiO{sub 2}){sub 0.05} glass, {sup 1}G{sub 4}, {sup 3}F{sub 2}, {sup 3}F{sub 3}, {sup 3}F{sub 4}, {sup 3}H{sub 5}, and {sup 3}H{sub 4} absorption bands were observed from the {sup 3}H{sub 6} ground level, at 463, 660, 687, 793, 1211 and 1700 nm wavelengths, respectively. Furthermore, spontaneous emission probabilities, and the radiative lifetimes for the 4f-4f transitions of the Tm{sup 3+} ions were calculated. The spectral intensities were determined in terms of Judd-Ofelt parameters ({omega}{sub 2}, {omega}{sub 4}, {omega}{sub 6}). Luminescence analysis was realized for the different Tm{sup 3+} ion concentration (0.002, 0.005 and 0.01mol) at room temperature. The luminescence band intensity of the {sup 3}F{sub 4}{yields}{sup 3}H{sub 4} transition was measured as a function of Tm{sup 3+} ion concentration (0.002, 0.005 and 0.01mol). Furthermore, luminescence data of the thulium doped glass samples were used to determine the compositional dependence of the emission cross sections at 1470 nm (copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Ionization yield and absorption spectra reveal superexcited Rydberg state relaxation processes in H{sub 2}O and D{sub 2}O

Energy Technology Data Exchange (ETDEWEB)

Fillion, J-H [LERMA, CNRS-UMR 8112, Observatoire de Paris-Meudon, 5 place J Janssen, F-92195, Meudon (France); Dulieu, F [LERMA, CNRS-UMR 8112, Observatoire de Paris-Meudon, 5 place J Janssen, F-92195, Meudon (France); Baouche, S [LERMA, CNRS-UMR 8112, Observatoire de Paris-Meudon, 5 place J Janssen, F-92195, Meudon (France); Lemaire, J-L [LERMA, CNRS-UMR 8112, Observatoire de Paris-Meudon, 5 place J Janssen, F-92195, Meudon (France); Jochims, H W [Institut fuer Physikalische und Theoretische Chemie der Freien Universitaet Berlin, Takustrasse 3, D-14195 Berlin 33 (Germany); Leach, S [LERMA, CNRS-UMR 8112, Observatoire de Paris-Meudon, 5 place J Janssen, F-92195, Meudon (France)

2003-07-14

The absorption cross section and the ionization quantum yield of H{sub 2}O have been measured using a synchrotron radiation source between 9 and 22 eV. Comparison between the two curves highlights competition between relaxation processes for Rydberg states converging to the first A-tilde {sup 2}A{sub 1} and to the second B-tilde {sup 2}B{sub 2} excited states of H{sub 2}O{sup +}. Comparison with D{sub 2}O absorption and ionization yields, derived from Katayama et al (1973 J. Chem. Phys. 59 4309), reveals specific energy-dependent deuteration effects on competitive predissociation and autoionization relaxation channels. Direct ionization was found to be only slightly affected by deuteration.

Crystallization behavior of Li2O-SiO2, Na2O-SiO2 and Na2O-CaO-SiO2 glasses; Li2O-SiO2, Na2O-SiO2, Na2O-CaO-SiO2 kei glass no kessho sekishutsu kyodo

Energy Technology Data Exchange (ETDEWEB)

Tsutsumi, K.; Otake, J.; Nagasaka, T.; Hino, M. [Tohoku University, Sendai (Japan)

1998-06-01

It has been known that crystallization of mold powder is effective on the disturbance of heat transfer between mold and solidified shell in production of middle carbon steel slabs in continuous casting process. But it has not yet been made clear which composition of mold powder is the most suitable for crystallization. The crystallization behavior of Li2O-SiO2, Na2O-SiO2 and Na2O-CaO-SiO2 glasses was observed by differential thermal analysis (DTA) and hot-thermocouple methods with DTA in the present work. As a result, addition of alkaline metal and alkaline earth metal oxides to SiO2 increased the critical cooling rate for glass formation in binary system of Li2O-SiO2 and Na2O-SiO2 and Li2O-SiO2 system crystallized easier than Na2O-SiO2 system. In ternary system of Na2O-CaO-SiO2, addition of Na2O hurried the critical cooling rate at CaO/SiO2=0.93 mass ratio, but the rate was almost constant in the composition range of more than 15 mass% Na2O. The slag of CaO/SiO2=0.93 made the rate faster than the slag of CaO/SiO2=0.47 at constant content of 10mass% Na2O. 17 refs., 10 figs., 3 tabs.

Synthesis of Bi2O3 architectures in DMF–H2O solution by precipitation method and their photocatalytic activity

International Nuclear Information System (INIS)

Yang, Li-Li; Han, Qiao-Feng; Zhao, Jin; Zhu, Jun-Wu; Wang, Xin; Ma, Wei-Hua

2014-01-01

Graphical abstract: Flowerlike α-Bi 2 O 3 architectures assembled by nanobrick-based petals with pineapple surface were firstly synthesized by precipitation method at room temperature in DMF–H 2 O solution. - Highlights: • Nanobrick-based flowerlike Bi 2 O 3 crystals with pineapple surface were synthesized by precipitation method. • Good solubility of Bi(NO 3 ) 3 in DMF played a crucial role in the growth of flowerlike Bi 2 O 3 . • The growth mechanism of Bi 2 O 3 microcrystallites has been explained in detail. - Abstract: Well-crystalline flowerlike α-Bi 2 O 3 hierarchical architectures with pineapple-shaped petals have been synthesized by precipitation method at a volume ratio of DMF/H 2 O of 5, where DMF and H 2 O were used to dissolve Bi(NO 3 ) 3 and KOH, respectively. If the DMF/H 2 O ratio was decreased to 2:1, 1:1 and 0:30, flower-, bundle- and dendrite-shaped α-Bi 2 O 3 microcrystallites aggregated by nanorods were formed, respectively. The simple synthetic route and thus obtained Bi 2 O 3 architectures of various morphologies provide a basis insight for their formation mechanism. The photocatalytic activity of the as-prepared Bi 2 O 3 particles for degradation of Rhodamine B (RhB) under visible-light irradiation was obviously influenced by their morphologies. Bi 2 O 3 of nanorod-based microstructures exhibited higher photodegradation activity than nanobrick-based ones, owing to higher light absorption and carrier separation efficiency in one-dimensional (1D) nanostructured materials

Development and characterization of nickel catalysts supported in CeO{sub 2}-ZrO{sub 2}-Al{sub 2}O{sub 3}, CeO{sub 2}-La{sub 2}O{sub 3}-Al{sub 2}O{sub 3} e ZrO{sub 2}-La{sub 2}O{sub 3}-Al{sub 2}O{sub 3} matrixes evaluated for methane reforming reactions; Desenvolvimento e caracterização de catalisadores de níquel suportados em matrizes CeO{sub 2}-ZrO{sub 2}-Al{sub 2}O{sub 3}, CeO{sub 2}-La{sub 2}O{sub 3}-Al{sub 2}O{sub 3} e ZrO{sub 2}-La{sub 2}O{sub 3}-Al{sub 2}O{sub 3} avaliados para as reações de reforma do metano

Energy Technology Data Exchange (ETDEWEB)

Abreu, Amanda Jordão de

2012-07-01

Nowadays, the methane reforming is large interest industrial for the take advantage of these gas in production the hydrogen and synthesis gas (syngas). Among in the reactions of methane stand of the reactions steam reforming and carbon dioxide reforming of methane. The main catalysts uses in the methane reforming is Ni/Al{sub 2}O{sub 3}. However, the supported-nickel catalyst is susceptible to the deactivation or the destruction by coke deposition. The carbon dissolves in the nickel crystallite and its diffuses through the nickel, leading for formation of the carbon whiskers, which results in fragmentation of the catalyst. Modification of such catalysts, like incorporation of suitable promoters, is desirable to achieve reduction of the methane hydrogenolysis and/or promotion of the carbon gasification. Catalysts 5%Ni/Al{sub 2}O{sub 3} supported on solid solutions formed by ZrO{sub 2}-CeO{sub 2}, La{sub 2}O{sub 3} and CeO{sub 2}-ZrO{sub 2}-La{sub 2}O{sub 3} were prepared, characterized and evaluated in reactions steam and carbon dioxide reforming and partial oxidation of methane with objective the value effect loading solution solid in support. The supports were prepared by co-precipitation method and catalysts were prepared by impregnation method and calcined at 500 deg C. The supports and catalysts were characterized by Nitrogen Adsorption, method -rays diffraction (XRD), X-rays dispersive spectroscopy (XDS), spectroscopy in the region of the ultraviolet and the visible (UV-vis NIR) to and temperature programmed reduction (TPR), Raman Spectroscopy, X-ray absorption spectroscopy and Thermogravimetric Analysis. After all the catalytic reactions check which the addition of solid solution is beneficial for Ni/Al{sub 2}O{sub 3} catalysts and the best catalysts are Ni/CeO{sub 2}-La{sub 2}O{sub 3}-Al{sub 2}O{sub 3}. (author)

Photolysis of H2O-H2O2 Mixtures: The Destruction of H2O2

Science.gov (United States)

Loeffler, M. J.; Fama, M.; Baragiola, R. A.; Carlson, R. W.

2013-01-01

We present laboratory results on the loss of H2O2 in solid H2O + H2O2 mixtures at temperatures between 21 and 145 K initiated by UV photolysis (193 nm). Using infrared spectroscopy and microbalance gravimetry, we measured the decrease of the 3.5 micrometer infrared absorption band during UV irradiation and obtained a photodestruction cross section that varies with temperature, being lowest at 70 K. We use our results, along with our previously measured H2O2 production rates via ionizing radiation and ion energy fluxes from the spacecraft to compare H2O2 creation and destruction at icy satellites by ions from their planetary magnetosphere and from solar UV photons. We conclude that, in many cases, H2O2 is not observed on icy satellite surfaces because the H2O2 photodestruction rate is much higher than the production rate via energetic particles, effectively keeping the H2O2 infrared signature at or below the noise level.

Spectroscopic study on the intermolecular interaction of SO{sub 2} absorption in poly-ethylene glycol+H{sub 2}O systems

Energy Technology Data Exchange (ETDEWEB)

He, Zhiqiang; Liu, Jinrong; Zhang, Jianbin; Zhang, Na [Inner Mongolia University of Technology, Huhhot (China)

2014-03-15

Poly-Ethylene Glycol (PEG) 300+H{sub 2}O solutions (PEGWs) has been used as a promising medium for the absorption of SO{sub 2}. We investigated the UV, FTIR, {sup 1}H-NMR, and fluorescence spectra in the absorption processes of SO{sub 2} in PEGWs to present an important absorption mechanism. Based on the spectral results, the possibility of intermolecular hydrogen bond formation by hydroxyl oxygen atom in the PEG molecule with hydrogen atom in H{sub 2}O and S…O interaction formation by the oxygen atoms in PEG with the sulfur atom in SO{sub 2} are discussed. This shows that the spectral changes may be due to the formation of -CH{sub 2}CH{sub 2}O(H)…HOH… and -CH{sub 2}-CH{sub 2}-O(CH{sub 2}-CH{sub 2}-)…HOH… in PEGWs and the formation of -CH{sub 2}CH{sub 2}OH…OSO…, and intermolecular S…O interaction between PEG and SO{sub 2} as the formation of -CH{sub 2}CH{sub 2}OCH{sub 2}CH{sub 2}O(H)…(O)S(O)… and -CH{sub 2}-CH{sub 2}-O(CH{sub 2}-CH{sub 2}-) …(O)S(O)…. The existence of these bonds benefits the absorption and desorption processes of SO{sub 2} in PEGWs.

Study of CO2 cyclic absorption stability of CaO-based sorbents derived from lime mud purified by sucrose method.

Science.gov (United States)

Ma, AiHua; Jia, QingMing; Su, HongYing; Zhi, YunFei; Tian, Na; Wu, Jing; Shan, ShaoYun

2016-02-01

Using lime mud (LM) purified by sucrose method, derived from paper-making industry, as calcium precursor, and using mineral rejects-bauxite-tailings (BTs) from aluminum production as dopant, the CaO-based sorbents for high-temperature CO2 capture were prepared. Effects of BTs content, precalcining time, and temperature on CO2 cyclic absorption stability were illustrated. The cyclic carbonation behavior was investigated in a thermogravimetric analyzer (TGA). Phase composition and morphologies were analyzed by XRD and SEM. The results reflected that the as-synthesized CaO-based sorbent doped with 10 wt% BTs showed a superior CO2 cyclic absorption-desorption conversion during multiple cycles, with conversion being >38 % after 50 cycles. Occurrence of Ca12Al14O33 phase during precalcination was probably responsible for the excellent CO2 cyclic stability.

Thermal, structural and optical properties of new TeO2sbnd Sb2O3sbnd GeO2 ternary glasses

Science.gov (United States)

Pereira, C.; Barbosa, J.; Cassanjes, F. C.; Gonçalves, R. R.; Ribeiro, S. J. L.; Poirier, G.

2016-12-01

In this work the novel glass system TeO2sbnd Sb2O3sbnd GeO2 was investigated and promising glass compositions were selected for further specific studies. Glass samples in the (80-0.8x)TeO2-(20-0.2x)Sb2O3-xGeO2 molar composition were prepared by the melt-quenching method with a glass-forming domain from x = 10 to x = 90. Samples were investigated by XRD, DSC, FTIR, Raman spectroscopy and UV-visible absorption. The XRD and DSC results bring informations about the non-crystalline state and thermal properties of these materials. It has been observed that higher GeO2 contents lead to higher glass transition temperatures and thermal stabilities against crystallization. FTIR and Raman spectroscopies suggest a progressive incorporation of GeO2 in the covalent network of TeO2 with conversion of structural units TeO4 to TeO3. Absorption spectra revealed the high visible transparency of these samples and an increase of the optical band gap with GeO2 addition, in agreement with a decreasing polarizability of the glass network. Er3+ doped and Er3+/Yb3+ codoped samples were also studied with respect to their infrared emission properties and higher GeO2 contents lead to an increase in IR emission intensity at 1,5 μm as well as longer radiative lifetimes. Finally, upconversion emission in the visible were also recorded and were shown to be strongly dependent of the composition.

Compositional dependence of absorption coefficient and band-gap for Nb2O5-SiO2 mixture thin films

International Nuclear Information System (INIS)

Sancho-Parramon, Jordi; Janicki, Vesna; Zorc, Hrvoje

2008-01-01

The absorption coefficient of composite films consisting of niobia (Nb 2 O 5 ) and silica (SiO 2 ) mixtures is studied for photon energies around the band gap. The films were deposited by co-evaporation and their composition was varied by changing the ratio of deposition rates of the two materials. Both, as-deposited and thermally annealed films were characterized by different techniques: the absorption coefficient was determined by spectrophotometric measurements and the structural properties were investigated using infrared spectroscopy, transmission electron microscopy and X-ray diffraction. The correlation between the variations of absorption properties and film composition and structure is established. The absorption coefficients determined experimentally are compared with the results derived from effective medium theories in order to evaluate the suitability of these theories for the studied composites

Electromagnetic and microwave absorption properties of single-walled carbon nanotubes and CoFe{sub 2}O{sub 4} nanocomposites

Energy Technology Data Exchange (ETDEWEB)

Li, Guo; Sheng, Leimei, E-mail: slmss@shu.edu.cn; Yu, Liming; An, Kang; Ren, Wei; Zhao, Xinluo, E-mail: xlzhao@shu.edu.cn

2015-03-15

Highlights: • LPA-SWCNTs have been abundantly fabricated by a facile, time-saving, economical and non-hazardous method using DC arc discharge technique in low-pressure air. • The electromagnetic and microwave absorption properties of LPA-SWCNTs, CoFe{sub 2}O{sub 4} nanocrystals and LPA-SWCNT/CoFe{sub 2}O{sub 4} nanocomposites were investigated and the LPA-SWCNT/CoFe{sub 2}O{sub 4} nanocomposites exhibited excellent microwave absorption properties. • The Debye theory and impedance matching were used to analyze the electromagnetic parameters and microwave absorption properties. - Abstract: Single-walled carbon nanotubes were facilely and abundantly synthesized by low-pressure air arc discharge method (LPA-SWCNTs), and CoFe{sub 2}O{sub 4} nanocrystals were synthesized by a nitrate citric acid sol–gel auto-ignition method. The electromagnetic and microwave absorption properties of LPA-SWCNTs, CoFe{sub 2}O{sub 4} nanocrystals and their nanocomposites were investigated. The LPA-SWCNT/CoFe{sub 2}O{sub 4} nanocomposites showed excellent microwave absorption properties. The minimum efficient reflection loss is −30.7 dB at 12.9 GHz for 10 wt% of LPA-SWCNTs in the nanocomposites, and an effective absorption bandwidth with a reflection loss below −10 dB is 7.2 GHz. The Debye equation and impedance matching were introduced to explain the microwave absorption properties. Compared with the single-component materials, the LPA-SWCNT/CoFe{sub 2}O{sub 4} nanocomposites are an excellent candidate for microwave absorbers.

Electronic structure of Ti/sub 2/O/sub 3/, V/sub 2/O/sub 3/, and Cr/sub 2/O/sub 3/

Energy Technology Data Exchange (ETDEWEB)

Bondarenko, T N; Zhurakovskii, E A; Dzeganovskii, V P [AN Ukrainskoj SSR, Kiev. Inst. Problem Materialovedeniya

1975-11-01

Electronic structure of oxides Ti/sub 2/O/sub 3/, V/sub 2/O/sub 3/, Cr/sub 2/O/sub 3/ was elucidated by means of X-ray and ESCA methods and the results were compared with the data obtained by other methods and with the available models of electronic structures. Energy diagram of V/sub 2/O/sub 3/ and common energy scale of X-ray spectra of Ti and Cr in Ti/sub 2/O/sub 3/ and Cr/sub 2/O/sub 3/ are presented. X-ray spectra show that these oxides possess the states which are related genetically to the M4p-states i.e. the X-ray data complement essentially to the result of optical and electrophysical measurements. MO and M/sub 2/O/sub 3/ compounds in the region of Fermi level have overlapping emission and absorption spectra which is specific to the matters with the metallic type of bonding. Actually TiO, VO, Ti/sub 2/O/sub 3/ and V/sub 2/O/sub 3/ have metallic type of bonding. However such overlap was observed in Cr/sub 2/O/sub 3/ as well whose forbidden zone according to photoconductivity measurments is about 3 eV. Absence of energy gap between emission and absorption spectra in Cr/sub 2/O/sub 3/ may be explained by traces of impurities which convert dielectrics conductors - impurities act as agents caus:ng filling or generation of vacancies rather than independent allowing additives. On the other hand this may be due to the defects in Cr/sub 2/O/sub 3/ lattice which may cause appearance of excited states in forbidden zone. These investigations enable to draw energy diagram of V/sub 2/O/sub 3/ and to combine the spectra of M in Ti/sub 2/O/sub 3/ into common energy scheme. Analysis of the diagram and combined spectra revealed great similarity in the electronic structures of M/sub 2/O/sub 3/ oxides (M - Ti, V, Cr) .

Spectroscopic and optical properties of the VO2+ ion doped TeO2-TiO2-ZnO-Nb2O5 glass system

Science.gov (United States)

Swapna; Upender, G.; Sreenivasulu, V.; Prasad, M.

2016-04-01

Studies such as optical absorption, Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy, Electron paramagnetic resonance (EPR) spectroscopy and Differential scanning calorimetry (DSC) were carried out on VO2+ ion doped TeO2-TiO2-ZnO-Nb2O5 glass system. Raman and FTIR spectra of the glasses revealed the presence of [TeO3], [TeO4] and [NbO6] structural units in the glass network. The Urbach energy (Δ E), cut-off wavelength (λ c ), optical band gap ( E opt ), optical basicity (Λ) and electron polarizability ( α) of the glasses were determined from optical absorption studies. The density ( ρ), molar volume ( V m ), oxygen molar volume ( V o ) and refractive index ( n) were also measured. Spin-Hamiltonian parameters were calculated from the EPR studies. When Nb2O5 was increased at the expense of ZnO, the density, optical band gap and Urbach energy of the glasses increased, and the electronic polarizability and optical basicity decreased. The EPR spectra clearly showed that vanadium was in the glass as VO2+ and occupied octahedral sites with tetrahedral compression. Spin-Hamiltonian parameters g‖ and g⊥ decreased as Nb2O5 content increased in the glass. The glass transition temperature ( T g ) also increased with increasing Nb2O5 content in the glass.

Microwave electromagnetic and absorption properties of SiO2/C core/shell composites plated with metal cobalt

Science.gov (United States)

Shen, Guozhu; Fang, Xumin; Wu, Hongyan; Wei, Hongyu; Li, Jingfa; Li, Kaipeng; Mei, Buqing; Xu, Yewen

2017-04-01

A facile method has been developed to fabricate magnetic core/shell SiO2/C/Co sub-microspheres via the pyrolysis of SiO2/PANI (polyaniline) and electroless plating method. The electromagnetic parameters of these SiO2/C and SiO2/C/Co composites were measured and the microwave reflection loss properties were evaluated in the frequency range of 2-18 GHz. The results show that the dielectric loss of SiO2/C composite increases with the increase of carbonization temperature and the magnetic loss enhances due to the deposition of cobalt on the SiO2/C sub-microspheres. The reflection loss results exhibit that the microwave absorption properties of the SiO2/C/Co composites are more excellent than those of SiO2/C composites for each thickness. The maximum effective absorption bandwidth (reflection loss ≤ -10 dB) arrives at 5.0 GHz (13.0-18 GHz) for SiO2/C/Co composite with 1.5 mm of thickness and the minimum reflection loss value is -24.0 dB at 5.0 GHz with 4.0 mm of thickness. The microwave loss mechanism of the SiO2/C/Co composites was also discussed in this paper.

Easily Dispersible NiFe2O4/RGO Composite for Microwave Absorption Properties in the X-Band

Science.gov (United States)

Bateer, Buhe; Zhang, Jianjao; Zhang, Hongchen; Zhang, Xiaochen; Wang, Chunyan; Qi, Haiqun

2018-01-01

Composites with good dispersion and excellent microwave absorption properties have important applications. Therefore, an easily dispersible NiFe2O4/reduced graphene oxide (RGO) composite has been prepared conveniently through a simple hydrothermal method. Highly crystalline, small size (about 7 nm) monodispersed NiFe2O4 nanoparticles (NPs) are evenly distributed on the surface of RGO. The microwave absorbability revealed that the NiFe2O4/RGO composite exhibits excellent microwave absorption properties in the X-band (8-12 GHz), and the minimum reflection loss of the NiFe2O4/RGO composite is -27.7 dB at 9.2 GHz. The NiFe2O4/RGO composite has good dispersibility in nonpolar solvent, which facilitates the preparation of stable commercial microwave absorbing coatings. It can be a promising candidate for lightweight microwave absorption materials in many application fields.

Absorption spectra of trapped holes in anatase TiO2

DEFF Research Database (Denmark)

Zawadzki, Pawel

2013-01-01

absorption spectroscopy (TAS), but the understanding of the optical absorption due to trapped carriers in TiO2 is incomplete. On the basis of the generalized Δ self-consistent field density functional theory (Δ-SCF DFT) calculations, we attribute the experimentally observed absorption band at 430-550 nm...

In-situ X-ray absorption spectroscopy analysis of capacity fade in nanoscale-LiCoO2

International Nuclear Information System (INIS)

Patridge, Christopher J.; Love, Corey T.; Swider-Lyons, Karen E.; Twigg, Mark E.; Ramaker, David E.

2013-01-01

The local structure of nanoscale (∼10–40 nm) LiCoO 2 is monitored during electrochemical cycling utilizing in-situ X-ray absorption spectroscopy (XAS). The high surface area of the LiCoO 2 nanoparticles not only enhances capacity fade, but also provides a large signal from the particle surface relative to the bulk. Changes in the nanoscale LiCoO 2 metal-oxide bond lengths, structural disorder, and chemical state are tracked during cycling by adapting the delta mu (Δμ) technique in complement with comprehensive extended X-ray absorption fine structure (EXAFS) modeling. For the first time, we use a Δμ EXAFS method, and by comparison of the difference EXAFS spectra, extrapolate significant coordination changes and reduction of cobalt species with cycling. This combined approach suggests Li–Co site exchange at the surface of the nanoscale LiCoO 2 as a likely factor in the capacity fade and irreversible losses in practical, microscale LiCoO 2 . - Graphical abstract: Electrochemical cycling of Li-ion batteries has strong impact on the structure and integrity of the cathode active material particularly near the surface/electrolyte interface. In developing a new method, we have used in-situ X-ray absorption spectroscopy during electrochemical cycling of nanoscale LiCoO 2 to track changes during charge and discharge and between subsequent cycles. Using difference spectra, several small changes in Co-O bond length, Co-O and Co-Co coordination, and site exchange between Co and Li sites can be tracked. These methods show promise as a new technique to better understand processes which lead to capacity fade and loss in Li-ion batteries. - Highlights: • A new method is developed to understand capacity fade in Li-ion battery cathodes. • Structural changes are tracked during Li intercalation/deintercalation of LiCoO 2 . • Surface structural changes are emphasized using nanoscale-LiCoO 2 and difference spectra. • Full multiple scattering calculations are used to

Raman, FTIR, thermal and optical properties of TeO2-Nb2O5-B2O3-V2O5 quaternary glass system

Directory of Open Access Journals (Sweden)

Swapna

2017-07-01

Full Text Available A series of quaternary glass systems with the composition 79TeO2-(20−xNb2O5-xB2O3-1V2O5 was prepared using the melt quench technique. Such studies as optical absorption, Raman, FTIR spectroscopy, EPR and DSC were carried out on the glass system. The physical properties, such as density (ρ and molar volume (VM, were determined. The Urbach energy (ΔE, optical band gap (Eopt, optical basicity (Λ, refractive index (n and electron polarizability (α of the glasses were determined from optical absorption data. Spin-Hamiltonian parameters of VO2+ ions were calculated from the EPR data. With the gradual substitution of B2O3 at the expense of Nb2O5, the density and optical band gap of the glasses decreased, and the electronic polarizability increased. EPR spectra revealed that VO2+ occupies an octahedral site with tetrahedral compression. Spin-Hamiltonian parameters g|| and g⊥ increased as B2O3 content increased in the glass. The glass transition temperature (Tg also decreased as the B2O3 content in the glass increased.

Optical properties of ternary TeO2-B2O3-ZnO Glass system

International Nuclear Information System (INIS)

Nurfarhana Ayuni Joha; Halimah, M.K.; Talib, Z.A.; Sidek, H.A.A.; Daud, W.M.; Zaidan, A.W.; Khamirul, A.M.

2009-01-01

Full text: A series of ternary tellurite based glasses [ (TeO 2 ) 70 (B 2 0 3 ) 30 ] 100-x [ZnO] x glasses with different compositions of ZnO (x= 5 to 30 wt.% in steps of 5 wt.%) have been synthesized by melt quenching method. The role of ZnO to the glasses structure was studied by IR spectroscopy. FTIR spectra revealed broad, weak and strong absorption bands in the investigated range of wavenumber from 280 - 4000 cm -1 which associated with their corresponding bond modes of vibration and the glass structure. The indirect optical band gap and the direct optical band gap are in the range 2.08-3.12 and 1.54-2.36 eV, respectively. An increase in the values of energy band gap E g may come down to the reason that the non-bridging oxygen ion content decreases with increasing ZnO content and shifting the band edge to higher energies. The optical band gap and Urbach energies were calculated from the absorption spectra measured between 190 and 900 nm at room temperature. The refractive index, n of the glasses change from 1.84 - 2.00 while the molar refractivities decrease from 13.06 to 12.00 with the increase of ZnO in mol %. (author)

Exergetic and energetic comparison of LiCl-H_2O and LiBr-H_2O working pairs in a solar absorption cooling system

International Nuclear Information System (INIS)

Bellos, Evangelos; Tzivanidis, Christos; Antonopoulos, Kimon A.

2016-01-01

Highlights: • Two working pairs (LiCl-H_2O and LiBr-H_2O) are examined in a solar absorption chiller. • The examined single effect absorption chiller is driven by flat plate collectors. • The system is analyzed energetically and energetically for 3 ambient temperatures. • LiCl-H_2O performs better than LiBr-H_2O in all the examined cases. • The optimum operating temperature is lower for the case of pair LiCl-H_2O. - Abstract: The objective of this study is to investigate the use of an alternative working pair in a solar absorption cooling system. LiCl-H_2O is the new examined pair and it is compared energetically and exegetically with the conventional pair LiBr-H_2O, which is the most usual in air-conditioning applications. The simplest solar cooling system is analyzed in order to focus in the comparison between these working fluids. Specifically, flat plate collectors, coupled with a storage tank, feed the single effect absorption chiller which produces 250 kW cooling at 10 °C. The two pairs are examined parametrically for various heat source temperature levels and for three ambient temperature levels (25 °C, 30 °C and 35 °C). The minimization of the collecting area, which means maximum exergetic efficiency, is the optimization goal in every case. The final results show that LiCl-H_2O pair performs better in all cases by giving greater exergetic efficiency. More specifically, about 8% lower collecting area is required to cover the demanded cooling load with this working pair. Another interesting result is that the optimum heat source temperature for the LiCl-H_2O is roughly lower than the respective for the LiBr-H_2O. The system is analyzed in steady state with the commercial software Engineering Equator Solver (EES).

Detection of transient infrared absorption of SO3 and 1,3,2-dioxathietane-2,2-dioxide [cyc-(CH2)O(SO2)O] in the reaction CH2OO+SO2

Science.gov (United States)

Wang, Yi-Ying; Dash, Manas Ranjan; Chung, Chao-Yu; Lee, Yuan-Pern

2018-02-01

We recorded time-resolved infrared absorption spectra of transient species produced on irradiation at 308 nm of a flowing mixture of CH2I2/O2/N2/SO2 at 298 K. Bands of CH2OO were observed initially upon irradiation; their decrease in intensity was accompanied by the appearance of an intense band at 1391.5 cm-1 that is associated with the degenerate SO-stretching mode of SO3, two major bands of HCHO at 1502 and 1745 cm-1, and five new bands near >1340, 1225, 1100, 940, and 880 cm-1. The band near 1340 cm-1 was interfered by absorption of SO2 and SO3, so its band maximum might be greater than 1340 cm-1. SO3 in its internally excited states was produced initially and became thermalized at a later period. The rotational contour of the band of thermalized SO3 agrees satisfactorily with the reported spectrum of SO3. These five new bands are tentatively assigned to an intermediate 1,3,2-dioxathietane-2,2-dioxide [cyc-(CH2)O(SO2)O] according to comparison with anharmonic vibrational wavenumbers and relative IR intensities predicted for this intermediate. Observation of a small amount of cyc-(CH2)O(SO2)O is consistent with the expected reaction according to the potential energy scheme predicted previously. SO3+HCHO are the major products of the title reaction. The other predicted product channel HCOOH+SO2 was unobserved and its branching ratio was estimated to be <5%.

Photocatalytic Removal of Phenol under Natural Sunlight over N-TiO2-SiO2 Catalyst: The Effect of Nitrogen Composition in TiO2-SiO2

Directory of Open Access Journals (Sweden)

Viet-Cuong Nguyen

2009-01-01

Full Text Available In this present work, high specific surface area and strong visible light absorption nitrogen doped TiO2-SiO2 photocatalyst was synthesized by using sol-gel coupled with hydrothermal treatment method. Nitrogen was found to improve the specific surface area while it also distorted the crystal phase of the resulting N-TiO2-SiO2 catalyst. As the N/ (TiO2-SiO2 molar ratio was more than 10%, the derived catalyst presented the superior specific surface area up to 260 m2/g. Nevertheless, its photoactivity towards phenol removal was observed to significantly decrease, which could results from the too low crystallinity. The nitrogen content in N-TiO2-SiO2 catalyst was therefore necessary to be optimized in terms of phenol removal efficiency and found at ca. 5%. Under UVA light and natural sunlight irradiation of 80 min, N(5%-TiO2-SiO2 catalyst presented the phenol decomposition efficiencies of 68 and 100%, respectively. It was also interestingly found in this study that the reaction rate was successfully expressed using a Langmuir-Hinshelwood (L-H model, indicating the L-H nature of photocatalytic phenol decomposition reaction on the N-TiO2-SiO2 catalyst.

Structure and crystallization of B{sub 2}O{sub 3}-Al{sub 2}O{sub 3}-SiO{sub 2} glasses

Energy Technology Data Exchange (ETDEWEB)

Cheng Yin, E-mail: zjbcy@126.co [College of Physics and Electronic Science, Changsha University of Science and Technology, Changsha 410114 (China); Xiao Hanning [College of Physics and Electronic Science, Changsha University of Science and Technology, Changsha 410114 (China); College of Materials Science and Engineering, Hunan University, Changsha 410082 (China); Shuguang Chen; Tang Bingzhong [College of Physics and Electronic Science, Changsha University of Science and Technology, Changsha 410114 (China)

2009-05-01

B{sub 2}O{sub 3}-Al{sub 2}O{sub 3}-SiO{sub 2} glasses with different B{sub 2}O{sub 3}/Al{sub 2}O{sub 3} ratios of 0.4-1.3 were prepared by the melting-quenching method at 1500-1600 deg. C for 2 h. Fragility index F was used to estimate the glass-forming ability. The infrared (IR) absorption curves and differential scanning calorimetry (DSC) curves of the glasses have been investigated for estimating the influence of the B{sub 2}O{sub 3}/Al{sub 2}O{sub 3} ratio on glass structure and crystallization of the B{sub 2}O{sub 3}-Al{sub 2}O{sub 3}-SiO{sub 2} glass system. The crystallization kinetics of the glasses were described by activation energy (E) for crystallization and calculated by the Kissinger method. X-ray diffraction (XRD) and SEM analyses were also used to describe the types and morphologies of the crystals precipitated from the B{sub 2}O{sub 3}-Al{sub 2}O{sub 3}-SiO{sub 2} glasses. The results show that with the increase of B{sub 2}O{sub 3}/Al{sub 2}O{sub 3} ratio, glass stability improves and the trend of crystallization decreases relatively. However, when the B{sub 2}O{sub 3}/Al{sub 2}O{sub 3} ratio reaches 1.3, boron-abnormal phenomenon appears and results in the raising trend of crystallization. Rod-like crystals of Al{sub 4}B{sub 2}O{sub 9} and Al{sub 20}B{sub 4}O{sub 36} were observed in the crystallized samples.

Optical Properties of Ternary TeO2-B2O3-ZnO Glass System

Energy Technology Data Exchange (ETDEWEB)

Ayuni, J N; Halimah, M K; Talib, Z A; Sidek, H A A; Daud, W M; Zaidan, A W; Khamirul, A M, E-mail: nfarhanayuni@gmail.com, E-mail: halimah@science.upm.edu.my [Department of Physics, Faculty of Science, Universiti Putra Malaysia, 43400 UPM Serdang, Selangor (Malaysia)

2011-02-15

A series of ternary tellurite based glasses [(TeO2)70 (B203)30]100-x [ZnO]x glasses with different compositions of ZnO (x= 5 to 30 wt.% in steps of 5 wt.%) have been synthesized by melt quenching method. The role of ZnO to the glasses structure was studied by IR spectroscopy. FTIR spectra revealed broad, weak and strong absorption bands in the investigated range of wavenumber from 280-4000 cm-1 which associated with their corresponding bond modes of vibration and the glass structure. The indirect optical band gap and the direct optical band gap are in the range 2.08-3.12 and 1.54-2.36 eV, respectively. A decrease in the values of energy band gap Eg may come down to the reason that the non-bridging oxygen ion content increases with increasing ZnO content and shifting the band edge to lower energies. The optical band gap and Urbach energies were calculated from the absorption spectra measured between 190 and 900 nm at room temperature. The refractive index, n of the glasses change from 1.84-2.00 while the molar refractivities decrease from 13.06 to 12.00 with the increase of ZnO in mol%.

Optical Properties of Ternary TeO2-B2O3-ZnO Glass System

International Nuclear Information System (INIS)

Ayuni, J N; Halimah, M K; Talib, Z A; Sidek, H A A; Daud, W M; Zaidan, A W; Khamirul, A M

2011-01-01

A series of ternary tellurite based glasses [(TeO2)70 (B203)30]100-x [ZnO]x glasses with different compositions of ZnO (x= 5 to 30 wt.% in steps of 5 wt.%) have been synthesized by melt quenching method. The role of ZnO to the glasses structure was studied by IR spectroscopy. FTIR spectra revealed broad, weak and strong absorption bands in the investigated range of wavenumber from 280-4000 cm-1 which associated with their corresponding bond modes of vibration and the glass structure. The indirect optical band gap and the direct optical band gap are in the range 2.08-3.12 and 1.54-2.36 eV, respectively. A decrease in the values of energy band gap Eg may come down to the reason that the non-bridging oxygen ion content increases with increasing ZnO content and shifting the band edge to lower energies. The optical band gap and Urbach energies were calculated from the absorption spectra measured between 190 and 900 nm at room temperature. The refractive index, n of the glasses change from 1.84-2.00 while the molar refractivities decrease from 13.06 to 12.00 with the increase of ZnO in mol%.

Dependence of Photocatalytic Activity of TiO2-SiO2 Nanopowders

Directory of Open Access Journals (Sweden)

M. Riazian

2014-10-01

Full Text Available Structural properties and chemical composition change the photocatalytic activity in TiO2-SiO2 nanopowder composite. The SiO2-TiO2 nanostructure is synthesized based on sol–gel method. The nanoparticles are characterized by x-ray fluorescents (XRF, x- ray diffraction (XRD, tunneling electron microscopy (TEM, field emission scanning electron microscopy (FE-SEM, UV-vis. Spectrophotometer and furrier transmission create infrared absorption (FTIR techniques. The rate constant k for the degradation of methylen blue in its aqueous solution under UV irradiation is determined as a measure of photocatalytic activity. Dependence between photocatalytic activity and SiO2 content in the composite is determined. Rate constant k is found dependent on the content of SiO2 in the composite that calcined at 900 oC. The addition of low composition SiO2 to the TiO2 matrix (lower than 45% enhances the photocatalytic activity due to thermal stability and increasing in the surface area. The effects of chemical compositions on the surface topography and the crystallization of phases are studied.

Enhanced Photocatalytic Activity of La3+-Doped TiO2 Nanotubes with Full Wave-Band Absorption

Science.gov (United States)

Xia, Minghao; Huang, Lingling; Zhang, Yubo; Wang, Yongqian

2018-06-01

TiO2 nanotubes doped with La3+ were synthesized by anodic oxidation method and the photocatalytic activity was detected by photodegrading methylene blue. As-prepared samples improved the absorption of both ultraviolet light and visible light and have a great enhancement on the photocatalytic activity while contrasting with the pristine TiO2 nanotubes. A tentative mechanism for the enhancement of photocatalytic activity with full wave-band absorption is proposed.

Laser conditioning effect on HfO2/SiO2 film

International Nuclear Information System (INIS)

Wei Yaowei; Zhang Zhe; Liu Hao; Ouyang Sheng; Zheng Yi; Tang Gengyu; Chen Songlin; Ma Ping

2013-01-01

Laser conditioning is one of the important methods to improve the laser damage threshold of film optics. Firstly, a large aperture laser was used to irradiate the HfO 2 /SiO 2 reflectors, which were evaporated from hafnia and silica by e-beam. Secondly, a laser calorimeter was used to test the film absorption before and after laser irradiation. Focused ion beam (FIB) was few reported using on laser film, it was used to study the damage morphology and explore the cause of damage. The shooting of the partial ejection on nodule was obtained for the first time, which provided the basis for study the damage process. The results show that film absorption was decreased obviously after the laser irradiation, laser conditioning can raise the laser damage threshold by the 'cleaning mechanism'. For the HfO 2 /SiO 2 reflectors, laser conditioning was effective to eject the nodules on substrate. It resulted from the nodule residue not to affect the subsequent laser. In addition, laser conditioning was not effective to the nodule in the film, which might be from the material spatter in coating process. In this case, other method could be used to get rid of the nodules. (authors)

Elevated aerosol layers modify the O2–O2 absorption measured by ground-based MAX-DOAS

Energy Technology Data Exchange (ETDEWEB)

Ortega, Ivan; Berg, Larry K.; Ferrare, Richard A.; Hair, Johnathan W.; Hostetler, Chris A.; Volkamer, Rainer

2016-06-01

The oxygen collisional complex (O2-O2, or O4) is a greenhouse gas, and a calibration trace gas used to infer aerosol and cloud properties by Differential Optical Absorption Spectroscopy (DOAS). Recent reports suggest the need for an O4 correction factor (CFO4) when comparing simulated and measured O4 differential slant column densities (dSCD) by passive DOAS. We investigate the sensitivity of O4 dSCD simulations at ultraviolet (360 nm) and visible (477 nm) wavelengths towards separately measured aerosol extinction profiles. Measurements were conducted by the University of Colorado 2D-MAX-DOAS instrument and NASA’s multispectral High Spectral Resolution Lidar (HSRL-2) during the Two Column Aerosol Project (TCAP) at Cape Cod, MA in July 2012. During two case study days with (1) high aerosol load (17 July, AOD ~ 0.35 at 477 nm), and (2) near molecular scattering conditions (22 July, AOD < 0.10 at 477 nm) the measured and calculated O4 dSCDs agreed within 6.4±0.4% (360 nm) and 4.7±0.6% (477 nm) if the HSRL-2 profiles were used as input to the calculations. However, if in the calculations the aerosol is confined to the surface layer (while keeping AOD constant) we find 0.53O4 dSCDs that can explain CFO4. The air density and aerosol profile aloft needs to be taken into account when interpreting the O4 from ground-based MAX-DOAS. Opportunities to identify and better characterize these layers are also discussed.

Preparation and characterization of Fe3O4/SiO2/Bi2MoO6 composite as magnetically separable photocatalyst

International Nuclear Information System (INIS)

Hou, Xuemei; Tian, Yanlong; Zhang, Xiang; Dou, Shuliang; Pan, Lei; Wang, Wenjia; Li, Yao; Zhao, Jiupeng

2015-01-01

Highlights: • Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 composite was prepared by a hydrothermal method. • The composite has an enhanced visible absorption compared with pure Bi 2 MoO 6 . • The magnetic photocatalyst displayed excellent stability and reusability. • O 2 ·− and · OH play a major role during the photocatalytic process. - Abstract: In this paper, Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 microspheres were prepared by a facile hydrothermal method. The scanning electron microscope (SEM) results revealed that flower-like three dimensional (3D) Bi 2 MoO 6 microspheres were decorated with Fe 3 O 4 /SiO 2 magnetic nanoparticles. The UV–vis diffuse reflection spectra showed extended absorption within the visible light range compared with pure Bi 2 MoO 6 . We evaluated the photocatalytic activities of Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 microspheres on the degradation of Rhodamine B (RhB) under visible light irradiation and found that the obtained composite exhibited higher photocatalytic activity than pure Bi 2 MoO 6 and P25. Moreover, the Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 composite also displayed excellent stability and their photocatalytic activity decreased slightly after reusing 5 cycles. Meanwhile, the composite could be easily separated by applying an external magnetic field. The trapping experiment results suggest that superoxide radical species O 2 ·− and hydroxyl radicals · OH play a major role in Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 system under visible light irradiation. The combination of flower-like three dimensional (3D) Bi 2 MoO 6 microspheres and Fe 3 O 4 /SiO 2 magnetic nanospheres provides a useful strategy for designing multifunctional nanostructure materials with enhanced photocatalytic activities in the potential applications of water purification

Optical Absorption, Stability and Structure of NpO2+ Complexes with Dicarboxylic Acids

International Nuclear Information System (INIS)

Guoxin Tian; Linfeng Rao

2006-01-01

Complexation of NpO2+ with oxalic acid (OX),2,2'-oxydiacetic acid (ODA), 2,2'-iminodiacetic acid (IDA) and 2,2'-thiodiacetic acid (TDA), has been studied using spectrophotometry in1 M NaClO4. Both the position and the intensity of the absorption band of NpO2+ at 980 nm are affected by the formation of NpO2+/dicarboxylate complexes, providing useful information on the complexation strength, the coordination mode and the structure of the complexes

Synergetic effect of Ag_2O as co-catalyst for enhanced photocatalytic degradation of phenol on N-TiO_2

International Nuclear Information System (INIS)

Chu, Haipeng; Liu, Xinjuan; Liu, Junying; Li, Jinliang; Wu, Tianyang; Li, Haokun; Lei, Wenyan; Xu, Yan; Pan, Likun

2016-01-01

Graphical abstract: Ag_2O/N-TiO_2 composites were synthesized via a co-precipitation method for visible light photocatalytic degradation of organic pollutions with excellent photocatalytic activity. - Highlights: • Ag_2O/N-TiO_2 composites were synthesized via a facile precipitation method. • Ag_2O/N-TiO_2 composites exhibited enhanced photocatalytic activity. • Ag_2O acts as co-catalyst to separate the photo-generated electron-hole pairs. - Abstract: A facile precipitation method was developed to synthesize the Ag_2O/N-TiO_2 composites. Their morphology, structure and photocatalytic performance in the degradation of methylene blue (MB) and phenol under visible light irradiation were characterized by scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, photoluminescence spectroscopy and UV–vis absorption spectroscopy, respectively. The results show that the Ag_2O/N-TiO_2 composites exhibit excellent photocatalytic performance. The maximum degradation rates of MB and phenol are about 8.9 and 2.9 times that of pure N-TiO_2, respectively. The excellent photocatalytic performance is mainly ascribed to the synergetic effects of Ag_2O and N-TiO_2 including the increased light absorption and the reduced electron-hole pair recombination in N-TiO_2 with the presence of Ag_2O.

Sub-band-gap absorption in Ga2O3

Science.gov (United States)

Peelaers, Hartwin; Van de Walle, Chris G.

2017-10-01

β-Ga2O3 is a transparent conducting oxide that, due to its large bandgap of 4.8 eV, exhibits transparency into the UV. However, the free carriers that enable the conductivity can absorb light. We study the effect of free carriers on the properties of Ga2O3 using hybrid density functional theory. The presence of free carriers leads to sub-band-gap absorption and a Burstein-Moss shift in the onset of absorption. We find that for a concentration of 1020 carriers, the Fermi level is located 0.23 eV above the conduction-band minimum. This leads to an increase in the electron effective mass from 0.27-0.28 me to 0.35-0.37 me and a sub-band-gap absorption band with a peak value of 0.6 × 103 cm-1 at 3.37 eV for light polarized along the x or z direction. Both across-the-gap and free-carrier absorption depend strongly on the polarization of the incoming light. We also provide parametrizations of the conduction-band shape and the effective mass as a function of the Fermi level.

In-situ X-ray absorption spectroscopy analysis of capacity fade in nanoscale-LiCoO{sub 2}

Energy Technology Data Exchange (ETDEWEB)

Patridge, Christopher J. [NRC/NRL Cooperative Research Associate, U.S. Naval Research Laboratory, Washington, DC 20375 (United States); Love, Corey T., E-mail: corey.love@nrl.navy.mil [Chemistry Division, Code 6113, U.S. Naval Research Laboratory, Washington, DC 20375 (United States); Swider-Lyons, Karen E. [Chemistry Division, Code 6113, U.S. Naval Research Laboratory, Washington, DC 20375 (United States); Twigg, Mark E. [Electronics Science and Technology Division, Code 6812, U.S. Naval Research Laboratory, Washington, DC 20375 (United States); Ramaker, David E. [Chemistry Division, Code 6189, U.S. Naval Research laboratory, Washington, DC 20375 (United States)

2013-07-15

The local structure of nanoscale (∼10–40 nm) LiCoO{sub 2} is monitored during electrochemical cycling utilizing in-situ X-ray absorption spectroscopy (XAS). The high surface area of the LiCoO{sub 2} nanoparticles not only enhances capacity fade, but also provides a large signal from the particle surface relative to the bulk. Changes in the nanoscale LiCoO{sub 2} metal-oxide bond lengths, structural disorder, and chemical state are tracked during cycling by adapting the delta mu (Δμ) technique in complement with comprehensive extended X-ray absorption fine structure (EXAFS) modeling. For the first time, we use a Δμ EXAFS method, and by comparison of the difference EXAFS spectra, extrapolate significant coordination changes and reduction of cobalt species with cycling. This combined approach suggests Li–Co site exchange at the surface of the nanoscale LiCoO{sub 2} as a likely factor in the capacity fade and irreversible losses in practical, microscale LiCoO{sub 2}. - Graphical abstract: Electrochemical cycling of Li-ion batteries has strong impact on the structure and integrity of the cathode active material particularly near the surface/electrolyte interface. In developing a new method, we have used in-situ X-ray absorption spectroscopy during electrochemical cycling of nanoscale LiCoO{sub 2} to track changes during charge and discharge and between subsequent cycles. Using difference spectra, several small changes in Co-O bond length, Co-O and Co-Co coordination, and site exchange between Co and Li sites can be tracked. These methods show promise as a new technique to better understand processes which lead to capacity fade and loss in Li-ion batteries. - Highlights: • A new method is developed to understand capacity fade in Li-ion battery cathodes. • Structural changes are tracked during Li intercalation/deintercalation of LiCoO{sub 2}. • Surface structural changes are emphasized using nanoscale-LiCoO{sub 2} and difference spectra. • Full multiple

Determination of carbon content of UO2, (U, Gd)O2 and (U, Pu)O2 powders and sintered pellets - Combustion in a high-frequency induction furnace -Infrared absorption spectrometry

International Nuclear Information System (INIS)

2008-01-01

This International Standard describes a method for determining the carbon content in UO 2 , (U,Gd)O 2 and (U,Pu)O 2 powder and sintered pellets by combustion in an induction furnace and infrared absorption spectroscopy measurement. It is applicable for determining 10 μg/g to 500 μg/g of carbon in UO 2 , (U,Gd)O 2 and (U,Pu)O 2 powder and pellets. The sample is heated to a temperature above 1500 deg. C in an induction furnace, under pure oxygen atmosphere, to convert any carbon compounds to carbon dioxide gas. The resulting carbon dioxide gas is filtered and dried before measurement using infrared spectroscopy to measure the carbon dioxide signal at 2350 cm -1 . The result is converted into the carbon content of the material analysed

Enhancement of UV absorption behavior in ZnO–TiO2 composites

Directory of Open Access Journals (Sweden)

Julián Jiménez Reinosa

2016-03-01

Full Text Available The ultraviolet–visible, UV–vis, absorption edge behaviour of semiconductor oxides as TiO2 and ZnO promotes their use as inorganic UV filters for sunscreens. In cosmetics, the use of nanoparticles is favoured because of their higher yield and lower whiteness. However, the particle size effect in the UV absorption is unclear. For this reason, the performances of nano and microsized TiO2 and ZnO are evaluated in both the UV–vis spectroscopy and the Sun Protection Factor, SPF, value. In order to cover the UV range completely by using inorganic filters a new composite is attempted by dry nanodispersion methodology in which TiO2 nanoparticles are dispersed onto ZnO microparticles. The new composite shows superior UV absorbing properties and ca. 60% SPF value due to a synergism between components that resulted in extended UV coverage and reduction of the total amount of nanoparticles required in the sunscreens. In addition, nanoparticles are effectively anchored onto microparticles avoiding the presence of free nanoparticles.

Study of absorption, emission and EDS properties of Pr3+ incorporated in a SiO2 matrix by sol-gel method

International Nuclear Information System (INIS)

Gómez-Miranda, M; Fonseca, R Sosa; Ordoñez, C Velásquez

2015-01-01

The optical response of the Pr 3+ ions doped monolith of SiO 2 prepared by sol-gel method was investigated by absorption and emission spectra. The absorption spectrum shows some typical lines of Pr 3+ , with these data was made the diagram levels corresponding to SiO 2 : Pr 3+ . The emission spectra were taken at 225 nm and 240 nm of wavelength of excitation was measured. In that there are reabsorption line at 423 of the Pr 3+ ions in the emission host, that means that some kind of host-ion interactions exist. Red and NIR emission at 612 nm, 652 nm, 711 and 728 nm, respectively, from Pr 3+ ions in SiO 2 was observed. The transition 1 S 0 → 3 P 2 at 425 nm is observed because an effective radiative transfer between the silicate glasses host and the praseodymium ions is observed and discussed

Optical and dielectric properties of isothermally crystallized nano-KNbO3 in Er3+-doped K2O-Nb2O5-SiO2 glasses.

Science.gov (United States)

Chaliha, Reenamoni Saikia; Annapurna, K; Tarafder, Anal; Tiwari, V S; Gupta, P K; Karmakar, Basudeb

2010-01-01

Precursor glass of composition 25K(2)O-25Nb(2)O(5)-50SiO(2) (mol%) doped with Er(2)O(3) (0.5 wt% in excess) was isothermally crystallized at 800 degrees C for 0-100 h to obtain transparent KNbO(3) nanostructured glass-ceramics. XRD, FESEM, TEM, FTIRRS, dielectric constant, refractive index, absorption and fluorescence measurements were carried out to analyze the morphology, dielectric, structure and optical properties of the glass-ceramics. The crystallite size of KNbO(3) estimated from XRD and TEM is found to vary in the range 7-23 nm. A steep rise in the dielectric constant of glass-ceramics with heat-treatment time reveals the formation of ferroelectric nanocrystalline KNbO(3) phase. The measured visible photoluminescence spectra have exhibited green emission transitions of (2)H(11/2), (4)S(3/2)-->(4)I(15/2) upon excitation at 377 nm ((4)I(15/2)-->(4)G(11/2)) absorption band of Er(3+) ions. The near infrared (NIR) emission transition (4)I(13/2)-->(4)I(15/2) is detected around 1550 nm on excitation at 980 nm ((4)I(15/2)-->(4)I(11/2)) of absorption bands of Er(3+) ions. It is observed that photoluminescent intensity at 526 nm ((2)H(11/2)-->(4)I(15/2)), 550 nm ((4)S(3/2)-->(4)I(15/2)) and 1550 nm ((4)I(13/2)-->(4)I(15/2)) initially decrease and then gradually increase with increase in heat-treatment time. The measured lifetime (tau(f)) of the (4)I(13/2)-->(4)I(15/2) transition also possesses a similar trend. The measured absorption and fluorescence spectra reveal that the Er(3+) ions gradually enter into the KNbO(3) nanocrystals. Copyright 2009 Elsevier B.V. All rights reserved.

Investigation of thermal stability and spectroscopic properties in Er3+/Yb3+-codoped TeO2-Li2O-B2O3-GeO2 glasses.

Science.gov (United States)

Nie, Qiu-Hua; Gao, Yuan; Xu, Tie-Feng; Shen, Xiang

2005-06-01

The new Er3+/Yb3+ co-doped 70TeO2-5Li2O-(25-x)B2O3-xGeO2 (x = 0, 5, 10, 15 fand 20 mol.%) glasses were prepared. The thermal stability, absorption spectra, emission spectra and lifetime of the 4I(13/2) level of Er3+ ions were measured and studied. The FT-IR spectra were carried out in order to investigate the structure of local arrangements in glasses. It is found that the thermal stability, absorption cross-section of Yb3+, emission intensity and lifetime of the 4I(13/2) level of Er3+ increase with increasing GeO2 content in the glass composition, while the fluorescence width at half maximum (FWHM) at 1.5 um of Er3+ is about 70 nm. The obtained data suggest that this system glass can be used as a candidate host material for potential broadband optical amplifiers.

Surface structure of alpha-Fe sub 2 O sub 3 nanocrystal observed by O K-edge X-ray absorption spectroscopy

CERN Document Server

Zhang, J; Ibrahim, K; Abbas, M I; Ju, X

2003-01-01

X-ray absorption near edge structure (XANES) spectra is used as a probe of surface structure of alpha-Fe sub 2 O sub 3 nanocrystal, prepared by sol-gel method. We present O K-edge XANES of alpha-Fe sub 2 O sub 3 in nanocrystal and bulk by total electron yield at the photoemission station of Beijing Synchrotron Radiation Facility. The spectrum of alpha-Fe sub 2 O sub 3 shows a splitting of the pre-edge structure, which is interpreted as two subsets of Fe 3d t sub 2 sub g and e sub g orbitals in oxygen octahedral (O sub h) crystal field, and is also sensitive to long-range order effects. However, no distinguishable splitting of the pre-edge peak of nanocrystal alpha-Fe sub 2 O sub 3 is observed. This suggests that there exists the distorted octahedral coordination around Fe sites and also the long-range disorder due to the surface as compared with bulk alpha-Fe sub 2 O sub 3.

ZnO nanowire/TiO2 nanoparticle photoanodes prepared by the ultrasonic irradiation assisted dip-coating method

International Nuclear Information System (INIS)

Gan Xiaoyan; Li Xiaomin; Gao Xiangdong; Zhuge Fuwei; Yu Weidong

2010-01-01

Hybrid ZnO/TiO 2 photoanodes for dye-sensitized solar cells were prepared by combining ZnO nanowire (NW) arrays and TiO 2 nanoparticles (NPs) with the assistance of the ultrasonic irradiation assisted dip-coating method. Results show that the ultrasonic irradiation was an efficient way to promote the gap filling of TiO 2 NPs in the interstices of ZnO NWs. Hybrid ZnO NW/TiO 2 NP electrodes prepared with ultrasonic treatment exhibited better gap filling efficiency and higher visible absorptance. The overall conversion efficiency of the hybrid electrode was 0.79%, representing 35% improvement compared with that of the traditional one (0.58%). The enlarged surface area and improved attachments of TiO 2 NPs onto the walls of ZnO NWs induced by the application of ultrasonic irradiation may be the underlying reason. Electrochemical impedance spectroscopy measurements indicated that hybrid electrodes combined the advantages of improved electron transport along the ZnO NWs and increased surface area provided by infiltrated TiO 2 NPs, both of which are responsible for the improved cell efficiency.

Self-assembled Bi{sub 2}MoO{sub 6}/TiO{sub 2} nanofiber heterojunction film with enhanced photocatalytic activities

Energy Technology Data Exchange (ETDEWEB)

Li, Hua [School of Chemical Engineering, Northwest University, Xi’an 710069 (China); Zhang, Tianxi [School of Physics, Northwest University, Xi’an 710069 (China); Pan, Chao; Pu, Chenchen; Hu, Yang [School of Chemical Engineering, Northwest University, Xi’an 710069 (China); Hu, Xiaoyun [School of Physics, Northwest University, Xi’an 710069 (China); Liu, Enzhou, E-mail: liuenzhou@nwu.edu.cn [School of Chemical Engineering, Northwest University, Xi’an 710069 (China); Fan, Jun, E-mail: fanjun@nwu.edu.cn [School of Chemical Engineering, Northwest University, Xi’an 710069 (China)

2017-01-01

Highlights: • Self-assembled Bi{sub 2}MoO{sub 6}/TiO{sub 2} nanofiber film was synthesized. • TiO{sub 2} nanofiber film exhibits excellent visible light scattering property. • The scattering light from TiO{sub 2} overlaps with the absorption light of Bi{sub 2}MoO{sub 6}. • Bi{sub 2}MoO{sub 6}/TiO{sub 2} heterojunction photocatalysts show higher photocatalytic activity. - Abstract: TiO{sub 2} nanofiber film (TiO{sub 2} NFF) was successfully fabricated by an ethylene glycol-assisted hydrothermal method, and then self-assembled flake-like Bi{sub 2}MoO{sub 6} was grown on the surface of TiO{sub 2} nanofiber under alcohol thermal condition. The investigations indicate that the nanofiber structure of TiO{sub 2} films exhibits excellent visible light scattering property, the scattering light overlaps with the absorption band of Bi{sub 2}MoO{sub 6}, which can enhance the utility of incident light. The prepared Bi{sub 2}MoO{sub 6}/TiO{sub 2} composites show obviously enhanced photocatalytic activity for methylene blue (MB) degradation compared with pure TiO{sub 2} nanofiber under visible light irradiation (λ > 420 nm). The enhanced photocatalytic activity is primarily attributed to the synergistic effect of visible light absorption and effective electron-hole separation at the interfaces of the two semiconductors, which is confirmed by photoluminescence (PL) and electrochemical tests.

Theoretical UV absorption spectra of hydrodynamically escaping O2/CO2-rich exoplanetary atmospheres

International Nuclear Information System (INIS)

Gronoff, G.; Mertens, C. J.; Norman, R. B.; Maggiolo, R.; Wedlund, C. Simon; Bell, J.; Bernard, D.; Parkinson, C. J.; Vidal-Madjar, A.

2014-01-01

Characterizing Earth- and Venus-like exoplanets' atmospheres to determine if they are habitable and how they are evolving (e.g., equilibrium or strong erosion) is a challenge. For that endeavor, a key element is the retrieval of the exospheric temperature, which is a marker of some of the processes occurring in the lower layers and controls a large part of the atmospheric escape. We describe a method to determine the exospheric temperature of an O 2 - and/or CO 2 -rich transiting exoplanet, and we simulate the respective spectra of such a planet in hydrostatic equilibrium and hydrodynamic escape. The observation of hydrodynamically escaping atmospheres in young planets may help constrain and improve our understanding of the evolution of the solar system's terrestrial planets' atmospheres. We use the dependency of the absorption spectra of the O 2 and CO 2 molecules on the temperature to estimate the temperature independently of the total absorption of the planet. Combining two observables (two parts of the UV spectra that have a different temperature dependency) with the model, we are able to determine the thermospheric density profile and temperature. If the slope of the density profile is inconsistent with the temperature, then we infer the hydrodynamic escape. We address the question of the possible biases in the application of the method to future observations, and we show that the flare activity should be cautiously monitored to avoid large biases.

Optical spectroscopy of Sm(3+) doped Na2O-ZnO-La2O3-TeO2 glasses.

Science.gov (United States)

Sobczyk, Marcin

2015-10-05

Telluride glasses with the composition xSm2O3-(7-x)La2O3-3Na2O-25ZnO-65TeO2 (where x=0.1, 1, 2, 5 and 7 mol%) were obtained by the melt quenching technique. Electronic absorption and fluorescence spectra as well as fluorescence dynamics of the Sm(3+)-doped title glasses are presented and analysed in detail. A Judd-Ofelt intensity analysis of the absorption spectrum at 300 K has been applied for determination of Ωλ parameters (Ω2=3.10, Ω4=3.80, Ω6=1.61×10(-20) cm(2)) which in turn have been used for calculations of the radiative transition probabilities (AT), the natural (radiative) lifetimes (τR) of the (4)G5/2 level of Sm(3+), the fluorescence branching ratios (β) and the emission cross-sections (σem). The τR value of the (4)G5/2 level amount to 1546 μs and is slightly higher than the measured decay time of 1306 μs. With the increasing of Sm2O3 concentration from 0.1 to 7.0 mol% the experimental lifetime of the fluorescent level decreases from 1306 to 41 μs. An analysis of the non-radiative decay was based on the cross-relaxation mechanisms. The optical achieved results indicate that the investigated glasses are potentially applicable as an orange and/or red laser host. Copyright © 2015 Elsevier B.V. All rights reserved.

Absorption spectra of CsNd(MoO4)2 and CsGd(MoO4)2-Nd3+ crystals in strong magnetic fields

International Nuclear Information System (INIS)

Gorban', I.S.; Kozeeva, L.P.; Slobodyanyuk, A.V.; Shevchenko, V.A.

1987-01-01

The comparison of the electronic structure of Nd 3+ in CsNd(MoO 4 ) 2 and CsGd(MoO 4 ) 2 - Nd 3+ crystals is made. It is established that in these crystals the activator centers, mainly, of the certain type with the symmetry of the local environment C 2 are formed. The absorption spectra of self-activated CsNd(MoO 4 ) 2 crystal differ from spectra of CsGd(MoO 4 ) 2 - Nd 3+ by the presence of the vibrating structure. The Stark splittings of energy levels of Nd 3+ in the investigated crystalline matrices are more sensitive to the environment effect than the Zeeman ones. The ground state of Nd 3+ ion in CsNd(MoO 4 ) 2 and CsGd(MoO 4 ) 2 molybdates is characterized by the similar values of g-factors

X-ray absorption spectroscopy of single-crystalline (VO)2P2O7: Electronic structure and possible exchange paths

International Nuclear Information System (INIS)

Gerhold, S.; Nu''cker, N.; Kuntscher, C. A.; Schuppler, S.; Stadler, S.; Idzerda, Y. U.; Prokofiev, A. V.; Bu''llesfeld, F.; Assmus, W.

2001-01-01

Using polarization-dependent V2p and O1s near-edge x-ray absorption spectroscopy, we studied the unoccupied electronic structure of single-crystalline (VO) 2 P 2 O 7 . It is highly anisotropic, and shows similarities to vanadium oxides like VO 2 and V 2 O 5 at the V2p edge and at the O1s threshold. The contributions from V-O and P-O orbitals could be identified. The results rule out the spin ladder model for the magnetic behavior of (VO) 2 P 2 O 7 , but are consistent with the alternating chain scenario

UV absorption spectra, kinetics and mechanisms of the self-reaction of CHF2O2 radicals in the gas phase at 298-K

DEFF Research Database (Denmark)

Nielsen, O.J.; Ellermann, T.; Bartkiewicz, E.

1992-01-01

The ultraviolet-absorption spectrum and the self-reaction of CHF2O2 radicals have been studied in the gas phase at 298 K using the pulse radiolysis technique and long-pathlength Fourier transform infrared spectroscopy. Absorption cross sections were quantified over the wavelength range 220-280 nm....... The measured cross section near the absorption maximum was sigma(CHF2O2)(240 nm) = (2.66 +/- 0.46) x 10(-18) cm2 molecule-1. The absorption cross section data were used to derive the observed self-reaction rate constant for the reaction CHF2O2 + CHF2O2 --> products, defined as d[R]/dt = 2k(1obs)[CHF2O2]2, k(1......obs) = (5.0 +/- 0.7) x 10(-12) cm3 molecule-1 s-1 (+/- 2-sigma). The only carbon-containing product observed by FTIR spectroscopy was FC(O)F. These results are discussed with respect to previous studies of peroxy radicals....

Growth and Characteristic of Amorphous Nano-Granular TeO2-V2O5-NiO Thin Films

Science.gov (United States)

Hosseinzadeh, Sh.; Rahmati, A.; Bidadi, H.

2016-12-01

TeO2-V2O5-NiO thin films were deposited using thermal evaporation from 40TeO2-(60-y)V2O5-yNiO (y=0-30mol%) target. Structural analysis of the films was identified by X-ray diffractometry (XRD) and scanning electron microscopy (SEM). The amorphous TeO2-V2O5-NiO films have nanosized clear grain structure and sharp grain boundaries. DC conductivity and current-voltage (I-V) characteristic of TeO2-V2O5-NiO thin films were measured in the temperature range of 300-423K. As nickel oxide (NiO) content increases, the DC conductivity decreases up to two orders in value (10-9-10-11Sṡcm-1). Temperature dependence of conductivity is described using the small polaron hopping (SPH) model as well. Poole-Frenkel effect is observed at high external electric field. The optical absorption spectra of the TeO2-V2O5-NiO thin films were recorded in the wavelength range of 380-1100nm. The absorption coefficient revealed bandgap shrinkage (3.01-2.3eV) and band tail widening, due to an increase in NiO content. Energy dispersive X-ray spectroscopy (EDX) was used to determine elemental composition. In TeO2-V2O5-NiO thin films, the NiO content is around fifth of the initial target.

Study on spectroscopic properties and effects of tungsten ions in 2Bi2O3-3GeO2/SiO2 glasses.

Science.gov (United States)

Yu, Pingsheng; Su, Liangbi; Cheng, Junhua; Zhang, Xia; Xu, Jun

2017-04-01

The 2Bi 2 O 3 -3GeO 2 /SiO 2 glass samples have been prepared by the conventional melt quenching technique. XRD patterns, absorption spectra, excitation-emission spectra and Raman measurements were utilized to characterize the synthesized glasses. When substitute SiO 2 for GeO 2 , the 0.4Bi 2 O 3 -(0.4-0.1)GeO 2 -(0.2-0.5)SiO 2 glasses exhibit strong emission centered at about 475nm (under 300nm excitation), and the decay constants are within the scope of 20-40ns. W doping into 2Bi 2 O 3 -3SiO 2 glass could increase the emission intensity of 470nm, and the W-doped 2Bi 2 O 3 -3SiO 2 glass has shown another emission at about 433nm with much shorter decay time (near 10ns). The 2Bi 2 O 3 -3GeO 2 /SiO 2 glass system could be the possible candidate for scintillator in high energy physics applications. Copyright © 2017 Elsevier Ltd. All rights reserved.

Nanostructured Ti-Fe{sub 2}O{sub 3}/Cu{sub 2}O heterojunction photoelectrode for efficient hydrogen production

Energy Technology Data Exchange (ETDEWEB)

Sharma, Dipika; Upadhyay, Sumant; Verma, Anuradha [Department of Chemistry, Dayalbagh Educational Institute, Agra-282 110 India (India); Satsangi, Vibha R. [Department of Physics Computer Sciences, Dayalbagh Educational Institute, Agra-282 110 India (India); Shrivastav, Rohit [Department of Chemistry, Dayalbagh Educational Institute, Agra-282 110 India (India); Dass, Sahab, E-mail: drsahabdas@gmail.com [Department of Chemistry, Dayalbagh Educational Institute, Agra-282 110 India (India)

2015-01-01

Nanostructured thin films of pristine Fe{sub 2}O{sub 3}, Ti-doped Fe{sub 2}O{sub 3}, Cu{sub 2}O, and Fe{sub 2}O{sub 3}/Cu{sub 2}O, and Ti-doped Fe{sub 2}O{sub 3}/Cu{sub 2}O heterojunction were deposited on tin-doped indium oxide (Sn:In{sub 2}O{sub 3}) glass substrate using spray pyrolysis method. Ti doping is done to improve photoelectric conversion efficiency and electrical conductivity of hematite thin films. Further enhanced photocurrent is achieved for Ti-Fe{sub 2}O{sub 3}/Cu{sub 2}O heterojunction electrodes. All samples were characterized using X-ray diffractometry, scanning electron microscopy, atomic force microscopy, and UV-Vis spectrometry. Photoelectrochemical properties were also investigated in a three-electrode cell system. UV-Vis absorption spectrum for pristine Fe{sub 2}O{sub 3}, Ti-Fe{sub 2}O{sub 3}, Cu{sub 2}O, Fe{sub 2}O{sub 3}/Cu{sub 2}O, and Ti-Fe{sub 2}O{sub 3}/Cu{sub 2}O heterojunction thin films exhibited absorption in visible region. Nanostructured thin films as prepared were used as photoelectrode in the photoelectrochemical cell for water splitting reaction. Maximum photocurrent density of 2.60 mA/cm{sup 2} at 0.95 V/SCE was exhibited by 454 nm thick Ti-Fe{sub 2}O{sub 3}/Cu{sub 2}O heterojunction photoelectrode. Increased photocurrent density and enhanced incident photon-to-electron conversion efficiency, offered by the heterojunction thin films may be attributed to improved conductivity and efficient separation of the photogenerated charge carriers at the Ti-Fe{sub 2}O{sub 3}/Cu{sub 2}O interface. - Highlights: • Heterojunction thin films were deposited using spray pyrolysis techniques. • Titanium doping in Fe{sub 2}O{sub 3} played a significant role in PEC response. • Ti-Fe{sub 2}O{sub 3}/Cu{sub 2}O heterojunction shows the absorption in visible range. • Improved charge separation and enhanced PEC response were achieved in Ti-Fe{sub 2}O{sub 3}/Cu{sub 2}O.

Effect of Preparation Methods on Al2O3 Supported CuO-CeO2-ZrO2 Catalysts for CO Oxidation

Directory of Open Access Journals (Sweden)

Gaurav Rattan

2012-12-01

Full Text Available To examine the effect of preparation methods, four catalyst samples having same composition (CuCe5.17Zr3.83Ox/g-Al2O3 (15wt% were prepared by four different methods for CO oxidation. The catalysts were prepared by co-impregnation, citric acid sol-gel, urea nitrate combustion and urea gelation co-precipitation methods, and characterized by BET, XRD, TGA/DSC and SEM. The The air oxidation of CO was carried out in a tubular fixed bed reactor under the following operating conditions: catalyst weight - 100 mg, temperature - ambient to 250 oC, pressure - atmospheric, 2.5% CO in air, total feed rate - 60 ml/min.  It was observed that the catalytic activity greatly influenced by the preparation methods. The highest activity of the catalyst prepared by the sol gel method appeared to be associated with its largest BET surface area. All the four catalysts were active for CO oxidation and did not show deactivation of catalytic activity for 50 hours of continuous runs. The ranking order of the preparation methods of the catalyst is as follows: sol-gel > co-impregnation > urea gelation > urea nitrate combustion. Copyright © 2012 by BCREC UNDIP. All rights reservedReceived: 14th June 2012, Revised: 8th September 2012, Accepted: 19th September 2012[How to Cite: G. Rattan, R. Prasad, R.C.Katyal. (2012. Effect of Preparation Methods on Al2O3 Supported CuO-CeO2-ZrO2 Catalysts for CO Oxidation. Bulletin of Chemical Reaction Engineering & Catalysis, 7(2: 112-123. doi:10.9767/bcrec.7.2.3646.112-123] [How to Link / DOI: http://dx.doi.org/10.9767/bcrec.7.2.3646.112-123 ] | View in 

Synthesis and electromagnetic absorption properties of Ag-coated reduced graphene oxide with MnFe_2O_4 particles

International Nuclear Information System (INIS)

Wang, Yan; Wu, Xinming; Zhang, Wenzhi; Huang, Shuo

2016-01-01

A ternary composite of Ag/MnFe_2O_4/reduced graphene oxide (RGO) was synthesized by a facile hydrothermal method. The morphology, microstructure, magnetic and electromagnetic properties of as-prepared Ag/MnFe_2O_4/RGO composite were characterized by means of XRD, TEM, XPS, VSM and vector network analyzer. The maximum reflection loss (R_L) of Ag/ MnFe_2O_4/RGO composite shows maximum absorption of −38 dB at 6 GHz with the thickness of 3.5 mm, and the absorption bandwidth with the R_L below −10 dB is up to 3.5 GHz (from 3.7 to 7.2 GHz). The result demonstrates that the introduction of Ag significantly leads to the multiple absorbing mechanisms. It is believed that such composite could serve as a powerful candidate for microwave absorber. - Highlights: • A ternary composite of Ag/MnFe_2O_4/reduced graphene oxide (RGO) was synthesized by a facile method. • The morphology, microstructure, magnetic and electromagnetic properties were characterized. • The maximum reflection loss of Ag/MnFe_2O_4/RGO is −38 dB at 6 GHz with a thickness of 3.5 mm. • The composite shows a wide absorption band.

Synthesis of Bi{sub 2}O{sub 3} architectures in DMF–H{sub 2}O solution by precipitation method and their photocatalytic activity

Energy Technology Data Exchange (ETDEWEB)

Yang, Li-Li; Han, Qiao-Feng, E-mail: hanqiaofeng@njust.edu.cn; Zhao, Jin; Zhu, Jun-Wu; Wang, Xin, E-mail: wangx@njust.edu.cn; Ma, Wei-Hua

2014-11-25

Graphical abstract: Flowerlike α-Bi{sub 2}O{sub 3} architectures assembled by nanobrick-based petals with pineapple surface were firstly synthesized by precipitation method at room temperature in DMF–H{sub 2}O solution. - Highlights: • Nanobrick-based flowerlike Bi{sub 2}O{sub 3} crystals with pineapple surface were synthesized by precipitation method. • Good solubility of Bi(NO{sub 3}){sub 3} in DMF played a crucial role in the growth of flowerlike Bi{sub 2}O{sub 3}. • The growth mechanism of Bi{sub 2}O{sub 3} microcrystallites has been explained in detail. - Abstract: Well-crystalline flowerlike α-Bi{sub 2}O{sub 3} hierarchical architectures with pineapple-shaped petals have been synthesized by precipitation method at a volume ratio of DMF/H{sub 2}O of 5, where DMF and H{sub 2}O were used to dissolve Bi(NO{sub 3}){sub 3} and KOH, respectively. If the DMF/H{sub 2}O ratio was decreased to 2:1, 1:1 and 0:30, flower-, bundle- and dendrite-shaped α-Bi{sub 2}O{sub 3} microcrystallites aggregated by nanorods were formed, respectively. The simple synthetic route and thus obtained Bi{sub 2}O{sub 3} architectures of various morphologies provide a basis insight for their formation mechanism. The photocatalytic activity of the as-prepared Bi{sub 2}O{sub 3} particles for degradation of Rhodamine B (RhB) under visible-light irradiation was obviously influenced by their morphologies. Bi{sub 2}O{sub 3} of nanorod-based microstructures exhibited higher photodegradation activity than nanobrick-based ones, owing to higher light absorption and carrier separation efficiency in one-dimensional (1D) nanostructured materials.

Effect of RE (Nd3+, Sm3+) oxide on structural, optical properties of Na2O-Li2O-ZnO-B2O3 glass system

Science.gov (United States)

Hivrekar, Mahesh M.; Bhoyar, D. N.; Mande, V. K.; Dhole, V. V.; Solunke, M. B.; Jadhav, K. M.

2018-05-01

Zinc borate glass activated with rare earth oxide (Nd2O3, Sm2O3) of Na2O-Li2O-ZnO-B2O3 quaternary system has been prepared successfully by melt quenching method. The nucleation and growth of RE oxide were controlled temperature range 950-1000° C and rapid cooling at room temperature. The physical, structural and optical properties were characterized by using X-ray diffraction (XRD), SEM, Ultraviolet-visible spectroscopy (UV-Vis). XRD and SEM studies confirmed the amorphous nature, surface morphology of prepared zinc borate glass. The physical parameters like density, molar volume, molar mass of Nd3+, Sm3+ doped borate glass are summarized in the present article. The optical absorption spectra along with tauc's plot are presented. The optical energy band gap increases due to the addition of rare earth oxide confirming the role of network modifier.

Structural relaxation and colour in the spinel-magnesiochromite (MgAl2O4-MgCr2O4) and gahnite-zincochromite (ZnAl2O4-ZnCr2O4) solid solution series

Science.gov (United States)

Hålenius, U.; Andreozzi, G. B.; Skogby, H.

2009-04-01

Recent studies on binary mineral solid solution series utilising synchrotron based x-ray absorption spectroscopies have indicated strong structural relaxation. For instance, it has been suggested that the real Cr-O bond distances remain nearly constant (relaxation parameter (ɛ) of 0.85, where ɛ=1 equals full relaxation) over the entire compositional range of the MgAl2O4-MgCr2O4 series (Juhin et al. 2007). In the present study we have measured room temperature optical absorption spectra of synthetic single crystals of the ZnAl2-2xCr2xO4 (0.03?x?1) and MgAl2-2xCr2xO4(0.02?x?1) series with the aim to explore the real architecture of the structure and in particular the Cr-O distance as function of composition. Our crystals were synthesized by means of flux-growth methods under atmospheric pressure and temperature profiles resulting in an estimated cation ordering temperature of ca 850 °C. Crystals close to the spinel (sensu stricto) and gahnite end-member compositions were faintly red in colour. With increasing Cr-content the crystals become more intensely red-coloured and at the higher Cr-contents there is a distinct shift towards a dark greenish colouration. These colour changes are reflected in the measured optical spectra by the position and intensity of the two spin-allowed electronic d-d transitions in octahedrally coordinated Cr3+ at ca 18000 (4A2g -4T2g (4F) transition) and 25000 cm-1(4A2g -4T1g (4F) transition). The energy of the first transition (?1-band) is ca 1200 cm-1 lower in magnesiochromite than in weakly Cr-doped spinel (x=0.02) and ca 1400 cm-1 lower in zincochromite than in gahnite with the lowest Cr-content (x=0.03). Concomitantly the energy of the second transition (?2-band) decreases with increasing Cr-content in both series by ca. 1800 cm-1. From the position of the ?1-band, a decrease in crystal field splitting, 10Dq, for six-coordinated Cr3+ with increasing Cr-content in the MgAl2-2xCr2xO4 and ZnAl2-2xCr2xO4 series of 6.5 and 7

Optical characterization of Tm3+ doped Bi2O3-GeO2-Ga2O3 glasses in absence and presence of BaF2

Science.gov (United States)

Han, Kexuan; Zhang, Peng; Wang, Shunbin; Guo, Yanyan; Zhou, Dechun; Yu, Fengxia

2016-01-01

In this paper, Two new Bi2O3-GeO2-Ga2O3 glasses (one presence of BaF2) doped with 1mol% Tm2O3 were prepared by melt-quenching technique. Differential thermal analysis (DTA), the absorption, Raman, IR spectra and fluorescence spectra were measured. The Judd–Ofelt intensity parameters, emission cross section, absorption cross section, and gain coefficient of Tm3+ ions were comparatively investigated. After the BaF2 introduced, the glass showed a better thermal stability, lower phonon energy and weaker OH− absorption coefficient, meanwhile, a larger ~1.8 μm emission cross section σem (7.56 × 10−21 cm2) and a longer fluorescence lifetime τmea (2.25 ms) corresponding to the Tm3+: 4F3 → 3H6 transition were obtained, which is due to the addition of fluoride in glass could reduce the quenching rate of hydroxyls and raise the cross-relaxation (3H6 + 3H4 → 3F4 + 3F4) rate. Our results suggest that the Tm3+ doped Bi2O3-GeO2-Ga2O3 glass with BaF2 might be potential to the application in efficient ~1.8 μm lasers system. PMID:27506152

Optical characterization of Tm(3+) doped Bi2O3-GeO2-Ga2O3 glasses in absence and presence of BaF2.

Science.gov (United States)

Han, Kexuan; Zhang, Peng; Wang, Shunbin; Guo, Yanyan; Zhou, Dechun; Yu, Fengxia

2016-08-10

In this paper, Two new Bi2O3-GeO2-Ga2O3 glasses (one presence of BaF2) doped with 1mol% Tm2O3 were prepared by melt-quenching technique. Differential thermal analysis (DTA), the absorption, Raman, IR spectra and fluorescence spectra were measured. The Judd-Ofelt intensity parameters, emission cross section, absorption cross section, and gain coefficient of Tm(3+) ions were comparatively investigated. After the BaF2 introduced, the glass showed a better thermal stability, lower phonon energy and weaker OH(-) absorption coefficient, meanwhile, a larger ~1.8 μm emission cross section σem (7.56 × 10(-21) cm(2)) and a longer fluorescence lifetime τmea (2.25 ms) corresponding to the Tm(3+): (4)F3 → (3)H6 transition were obtained, which is due to the addition of fluoride in glass could reduce the quenching rate of hydroxyls and raise the cross-relaxation ((3)H6 + (3)H4 → (3)F4 + (3)F4) rate. Our results suggest that the Tm(3+) doped Bi2O3-GeO2-Ga2O3 glass with BaF2 might be potential to the application in efficient ~1.8 μm lasers system.

Violet-green excitation for NIR luminescence of Yb3+ ions in Bi2O3-B2O3-SiO2-Ga2O3 glasses.

Science.gov (United States)

Li, Weiwei; Cheng, Jimeng; Zhao, Guoying; Chen, Wei; Hu, Lili; Guzik, Malgorzata; Boulon, Georges

2014-04-21

60Bi(2)O(3)-20B(2)O(3)-10SiO(2)-10Ga(2)O(3) glasses doped with 1-9 mol% Yb(2)O(3) were prepared and investigated mainly on their violet-green excitation for the typical NIR emission of Yb(3+), generally excited in the NIR. Two violet excitation bands at 365 nm and 405 nm are related to Yb(2+) and Bi(3+). 465 nm excitation band and 480 nm absorption band in the blue-green are assigned to Bi(0) metal nanoparticles/grains. Yb-content-dependence of the excitation and absorption means that Bi(0) is the reduced product of Bi(3+), but greatly competed by the redox reaction of Yb(2+) ↔ Yb(3+). It is proved that the violet-green excitations result in the NIR emission of Yb(3+). On the energy transfer, the virtual level of Yb(3+)-Yb(3+) as well as Bi(0) dimers probably plays an important role. An effective and controllable way is suggested to achieve nano-optical applications by Bi(0) metal nanoparticles/grains and Yb(3+).

TiO2/Cu2O composite based on TiO2 NTPC photoanode for photoelectrochemical (PEC) water splitting under visible light

KAUST Repository

Shi, Le

2015-05-01

Water splitting through photoelectrochemical reaction is widely regarded as a major method to generate H2 , a promising source of renewable energy to deal with the energy crisis faced up to human being. Efficient exploitation of visible light in practice of water splitting with pure TiO2 material, one of the most popular semiconductor material used for photoelectrochemical water splitting, is still challenging. One dimensional TiO2 nanotubes is highly desired with its less recombination with the short distance for charge carrier diffusion and light-scattering properties. This work is based on TiO2 NTPC electrode by the optimized two-step anodization method from our group. A highly crystalized p-type Cu2O layer was deposited by optimized pulse potentiostatic electrochemical deposition onto TiO2 nanotubes to enhance the visible light absorption of a pure p-type TiO2 substrate and to build a p-n junction at the interface to improve the PEC performance. However, because of the real photocurrent of Cu2O is far away from its theoretical limit and also poor stability in the aqueous environment, a design of rGO medium layer was added between TiO2 nanotube and Cu2O layer to enhance the photogenerated electrons and holes separation, extend charge carrier diffusion length (in comparison with those of conventional pure TiO2 or Cu2O materials) which could significantly increase photocurrent to 0.65 mA/cm2 under visible light illumination (>420 nm) and also largely improve the stability of Cu2O layer, finally lead to an enhancement of water splitting performance.

Enhanced performance of dye-sensitized solar cells based on TiO{sub 2} with NIR-absorption and visible upconversion luminescence

Energy Technology Data Exchange (ETDEWEB)

Liang, Li [Department of Chemistry, Harbin Institute of Technology, Harbin 150001 (China); Yulin, Yang, E-mail: ylyang@hit.edu.cn [Department of Chemistry, Harbin Institute of Technology, Harbin 150001 (China); Mi, Zhou; Ruiqing, Fan; LeLe, Qiu [Department of Chemistry, Harbin Institute of Technology, Harbin 150001 (China); Xin, Wang [Department of Chemistry, Harbin Institute of Technology, Harbin 150001 (China); Department of Food and Environmental Engineering, Heilongjiang, East University, Harbin 150086 (China); Lingyun, Zhang [Department of Chemistry, Harbin Institute of Technology, Harbin 150001 (China); School of Chemical Engineering, Northeast Dianli University, Jilin 132012 (China); Xuesong, Zhou; Jianglong, He [Department of Chemistry, Harbin Institute of Technology, Harbin 150001 (China)

2013-02-15

TiO{sub 2} with NIR-absorption and visible upconversion luminescence (UC-TiO{sub 2}) is prepared by a sol-gel method and calcined at 700 Degree-Sign C for 6 h. The material broadens the response region of dye sensitized solar cells (DSSCs) from an ultraviolet-visible region to the whole region of the solar spectrum. It shifts NIR sunlight to visible light which matches the strong absorbing region of the dye (N719). DSSCs based on UC-TiO{sub 2} achieved higher conversion efficiency than that on raw TiO{sub 2}. UC-TiO{sub 2} was mixed with commercial raw TiO{sub 2} as additive, and the short-circuit current density, open-circuit voltage and conversion efficiency of the DSSC reached to the optimum values 13.38 mA/cm{sup 2}, 0.78 V and 6.63% (AM1.5 global), comparing with the blank values: 7.99 mA/cm{sup 2}, 0.75 V and 4.07%, respectively. Also the mechanisms of upconversion by multiphoton absorption and energy transfer processes are interpreted in this paper. - Graphical abstract: By introducing TiO{sub 2} with NIR-absorption and visible up-conversion luminescence into DSSC, a signal reflection was explored from ultra-violet region to visible region, and to near-IR region. Highlights: Black-Right-Pointing-Pointer TiO{sub 2} with NIR-absorption and visible up-conversion luminescence (UC-TiO{sub 2}) was prepared by a sol-gel method. Black-Right-Pointing-Pointer A systematic characterization and analysis was carried out to discuss the mechanism. Black-Right-Pointing-Pointer A significantly enhanced performance of DSSC was explored by using UC-TiO{sub 2} as an additive.

Synthesis of TiO2-doped SiO2 composite films and its applications

Indian Academy of Sciences (India)

Wintec

structure of the titanium oxide species in the TiO2-doped SiO2 composite films and the photocatalytic reactiv- ity in order to ... gaku D-max γA diffractometer with graphite mono- chromized ... FT–IR absorption spectra of TiO2-doped SiO2 com-.

Optical absorption spectra and g factor of MgO: Mn2+explored by ab initio and semi empirical methods

Science.gov (United States)

Andreici Eftimie, E.-L.; Avram, C. N.; Brik, M. G.; Avram, N. M.

2018-02-01

In this paper we present a methodology for calculations of the optical absorption spectra, ligand field parameters and g factor for the Mn2+ (3d5) ions doped in MgO host crystal. The proposed technique combines two methods: the ab initio multireference (MR) and the semi empirical ligand field (LF) in the framework of the exchange charge model (ECM) respectively. Both methods of calculations are applied to the [MnO6]10-cluster embedded in an extended point charge field of host matrix ligands based on Gellé-Lepetit procedure. The first step of such investigations was the full optimization of the cubic structure of perfect MgO crystal, followed by the structural optimization of the doped of MgO:Mn2+ system, using periodic density functional theory (DFT). The ab initio MR wave functions approaches, such as complete active space self-consistent field (CASSCF), N-electron valence second order perturbation theory (NEVPT2) and spectroscopy oriented configuration interaction (SORCI), are used for the calculations. The scalar relativistic effects have also been taken into account through the second order Douglas-Kroll-Hess (DKH2) procedure. Ab initio ligand field theory (AILFT) allows to extract all LF parameters and spin-orbit coupling constant from such calculations. In addition, the ECM of ligand field theory (LFT) has been used for modelling theoptical absorption spectra. The perturbation theory (PT) was employed for the g factor calculation in the semi empirical LFT. The results of each of the aforementioned types of calculations are discussed and the comparisons between the results obtained and the experimental results show a reasonable agreement, which justifies this new methodology based on the simultaneous use of both methods. This study establishes fundamental principles for the further modelling of larger embedded cluster models of doped metal oxides.

Synthesis and Characterization of CdS/TiO2-Montmorillonite Nanocomposite with Enhanced Visible-Light Absorption

OpenAIRE

Feng-shan Zhou; Dai-mei Chen; Bao-lin Cui; Wei-heng Wang

2014-01-01

Sodium montmorillonite (MMT) was chosen as the carrier; a serial of CdS/TiO2-MMT nanocomposites with enhanced visible-light absorption ability was prepared by hydrothermal synthesis method combination with semiconductor compound modification method. The samples are characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and ultraviolet visible (UV-Vis) spectroscopy; the results showed that TiO2 and CdS nanoparticles were loaded on the surface of montmorillonite unifo...

A Facile Method for Loading CeO2 Nanoparticles on Anodic TiO2 Nanotube Arrays.

Science.gov (United States)

Liao, Yulong; Yuan, Botao; Zhang, Dainan; Wang, Xiaoyi; Li, Yuanxun; Wen, Qiye; Zhang, Huaiwu; Zhong, Zhiyong

2018-04-03

In this paper, a facile method was proposed to load CeO 2 nanoparticles (NPs) on anodic TiO 2 nanotube (NT) arrays, which leads to a formation of CeO 2 /TiO 2 heterojunctions. Highly ordered anatase phase TiO 2 NT arrays were fabricated by using anodic oxidation method, then these individual TiO 2 NTs were used as tiny "nano-containers" to load a small amount of Ce(NO 3 ) 3 solutions. The loaded anodic TiO 2 NTs were baked and heated to a high temperature of 450 °C, under which the Ce(NO 3 ) 3 would be thermally decomposed inside those nano-containers. After the thermal decomposition of Ce(NO 3 ) 3 , cubic crystal CeO 2 NPs were obtained and successfully loaded into the anodic TiO 2 NT arrays. The prepared CeO 2 /TiO 2 heterojunction structures were characterized by a variety of analytical technologies, including XRD, SEM, and Raman spectra. This study provides a facile approach to prepare CeO 2 /TiO 2 films, which could be very useful for environmental and energy-related areas.

Photoemission study of absorption mechanisms in Bi2.0Sr1.8Ca0.8La0.3Cu2.1O8+δ, BaBiO3, and Nd1.85Ce0.15CuO4

International Nuclear Information System (INIS)

Lindberg, P.A.P.; Shen, Z.; Wells, B.O.; Dessau, D.S.; Ellis, W.P.; Borg, A.; Kang, J.; Mitzi, D.B.; Lindau, I.

1989-01-01

Photoemission measurements in the constant-final-state (absorption) mode were performed on three different classes of high-temperature superconductors Bi 2.0 Sr 1.8 Ca 0.8 La 0.3 Cu 2.1 O 8+δ , BaBiO 3 , and Nd 1.85 Ce 0.15 CuO 4 using synchrotron radiation from 20 to 200 eV. Absorption signals from all elements but Ce are identified. The results firmly show that the Bi 6s electrons are more delocalized in BaBiO 3 than in Bi 2.0 Sr 1.8 Ca 0.8 La 0.3 Cu 2.1 O 8+δ , in agreement with the results of band-structure calculations. Differences in the absorption signals due to O and Bi excitations between BaBiO 3 and Bi 2.0 Sr 1.8 Ca 0.8 La 0.3 Cu 2.1 O 8+δ are discussed. Delayed absorption onsets attributed to giant resonances (Ba 4d→4f, La 4d→4f, and Nd 4d→4f transitions) are also reported

Synergetic effect of Ag{sub 2}O as co-catalyst for enhanced photocatalytic degradation of phenol on N-TiO{sub 2}

Energy Technology Data Exchange (ETDEWEB)

Chu, Haipeng [Institute of Coordination Bond Metrology and Engineering, College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018 (China); Liu, Xinjuan, E-mail: lxj669635@126.com [Institute of Coordination Bond Metrology and Engineering, College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018 (China); Liu, Junying [Research Center for Combustion and Environment Technology, Shanghai Jiao Tong University, Shanghai 200240 (China); Li, Jinliang [Engineering Research Center for Nanophotonics & Advanced Instrument, Ministry of Education, School of Physics and Materials Science, East China Normal University, Shanghai 200062 (China); Wu, Tianyang; Li, Haokun; Lei, Wenyan; Xu, Yan [Institute of Coordination Bond Metrology and Engineering, College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018 (China); Pan, Likun, E-mail: lkpan@phy.ecnu.edu.cn [Engineering Research Center for Nanophotonics & Advanced Instrument, Ministry of Education, School of Physics and Materials Science, East China Normal University, Shanghai 200062 (China)

2016-09-15

Graphical abstract: Ag{sub 2}O/N-TiO{sub 2} composites were synthesized via a co-precipitation method for visible light photocatalytic degradation of organic pollutions with excellent photocatalytic activity. - Highlights: • Ag{sub 2}O/N-TiO{sub 2} composites were synthesized via a facile precipitation method. • Ag{sub 2}O/N-TiO{sub 2} composites exhibited enhanced photocatalytic activity. • Ag{sub 2}O acts as co-catalyst to separate the photo-generated electron-hole pairs. - Abstract: A facile precipitation method was developed to synthesize the Ag{sub 2}O/N-TiO{sub 2} composites. Their morphology, structure and photocatalytic performance in the degradation of methylene blue (MB) and phenol under visible light irradiation were characterized by scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, photoluminescence spectroscopy and UV–vis absorption spectroscopy, respectively. The results show that the Ag{sub 2}O/N-TiO{sub 2} composites exhibit excellent photocatalytic performance. The maximum degradation rates of MB and phenol are about 8.9 and 2.9 times that of pure N-TiO{sub 2}, respectively. The excellent photocatalytic performance is mainly ascribed to the synergetic effects of Ag{sub 2}O and N-TiO{sub 2} including the increased light absorption and the reduced electron-hole pair recombination in N-TiO{sub 2} with the presence of Ag{sub 2}O.

Optical absorption properties of Ag/SiO sub 2 composite films induced by gamma irradiation

CERN Document Server

Pan, A L; Yang, Z P; Liu, F X; Ding, Z J; Qian, Y T

2003-01-01

Mesoporous SiO sub 2 composite films with small Ag particles or clusters dispersed in them were prepared by a new method: first the matrix SiO sub 2 films were prepared by the sol-gel process combined with the dip-coating technique; then they were soaked in AgNO sub 3 solutions; this was followed by irradiation with gamma-rays at room temperature and ambient pressure. The structure of these films was examined by high-resolution transmission electron microscopy, and their optical absorption spectra were examined. It has been shown that the Ag particles grown within the porous SiO sub 2 films are very small and are highly dispersed. On increasing the soaking concentration and subjecting the samples to an additional annealing, a different peak-shift effect for the surface plasmon resonance was observed in the optical absorption measurement. Possible mechanisms of this behaviour are discussed in this paper.

Interchange core/shell assembly of diluted magnetic semiconductor CeO2 and ferromagnetic ferrite Fe3O4 for microwave absorption

Directory of Open Access Journals (Sweden)

Jiaheng Wang

2017-05-01

Full Text Available Core/shell-structured CeO2/Fe3O4 and Fe3O4/CeO2 nanocapsules are prepared by interchange assembly of diluted magnetic semiconductor CeO2 and ferromagnetic ferrite Fe3O4 as the core and the shell, and vice versa, using a facile two-step polar solvothermal method in order to utilize the room-temperature ferromagnetism and abundant O-vacancies in CeO2, the large natural resonance in Fe3O4, and the O-vacancy-enhanced interfacial polarization between CeO2 and Fe3O4 for new generation microwave absorbers. Comparing to Fe3O4/CeO2 nanocapsules, the CeO2/Fe3O4 nanocapsules show an improved real permittivity of 3–10% and an enhanced dielectric resonance of 1.5 times at 15.3 GHz due to the increased O-vacancy concentration in the CeO2 cores of larger grains as well as the O-vacancy-induced enhancement in interfacial polarization between the CeO2 cores and the Fe3O4 shells, respectively. Both nanocapsules exhibit relatively high permeability in the low-frequency S and C microwave bands as a result of the bi-magnetic core/shell combination of CeO2 and Fe3O4. The CeO2/Fe3O4 nanocapsules effectively enhance permittivity and permeability in the high-frequency Ku band with interfacial polarization and natural resonance at ∼15 GHz, thereby improving absorption with a large reflection loss of -28.9 dB at 15.3 GHz. Experimental and theoretical comparisons with CeO2 and Fe3O4 nanoparticles are also made.

Three-dimensional (3D α-Fe2O3/polypyrrole (PPy nanocomposite for effective electromagnetic absorption

Directory of Open Access Journals (Sweden)

Wanchun Jiang

2016-06-01

Full Text Available The lightweight and 3-dimensional reticulated α-Fe2O3/PPy hybrids were successfully fabricated via a facile one-pot polyreaction. The measured complex permittivity and microwave attenuation performance suggest that the dielectric properties of PPy can be regulated by the mass ratio of added α-Fe2O3. The two dielectric resonance peaks of complex permittivity can be ascribed to the interface capacitor-like structure. An equivalent circuit model was established to explain the nonlinear resonance behavior of the α-Fe2O3/PPy wax composites. The addition of α-Fe2O3 properly tuned the dielectric constant to endow the composites with highly efficient microwave absorption. The minimum reflection loss of α-Fe2O3/PPy wax composites were enhanced to nearly −29dB with an effective bandwidth (RL≤ − 10dB up to 5.0GHz. The numerical method was proposed to calculate the optimum thickness for minimum RL at expected frequency by detailed investigation on the transmission formula. Moreover, the required thickness for optimum absorption efficiency at expected frequency can be obtained directly.

Ag2S/CdS/TiO2 Nanotube Array Films with High Photocurrent Density by Spotting Sample Method

OpenAIRE

Sun, Hong; Zhao, Peini; Zhang, Fanjun; Liu, Yuliang; Hao, Jingcheng

2015-01-01

Ag2S/CdS/TiO2 hybrid nanotube array films (Ag2S/CdS/TNTs) were prepared by selectively depositing a narrow-gap semiconductor—Ag2S (0.9 eV) quantum dots (QDs)—in the local domain of the CdS/TiO2 nanotube array films by spotting sample method (SSM). The improvement of sunlight absorption ability and photocurrent density of titanium dioxide (TiO2) nanotube array films (TNTs) which were obtained by anodic oxidation method was realized because of modifying semiconductor QDs. The CdS/TNTs, Ag2S/TNT...

Influence of valence state of copper ions on structural and spectroscopic properties of multi-component PbO-Al2O3-TeO2-GeO2-SiO2 glass ceramic system- a possible material for memory switching devices

Science.gov (United States)

Tirupataiah, Ch.; Narendrudu, T.; Suresh, S.; Srinivasa Rao, P.; Vinaya Teja, P. M.; Sambasiva Rao, M. V.; Chinna Ram, G.; Krishna Rao, D.

2017-11-01

Multi-component glass ceramics with composition 29PbO-5Al2O3-1TeO2 -10GeO2- (55-x) SiO2 doped with different concentrations of CuO (0 ≤ x ≤ 1.0 mol %) were synthesized by melt quenching technique and subsequent heat treatment. These glass ceramics were characterized by X-ray diffraction, scanning electron microscope, differential thermal analysis, optical absorption, electron paramagnetic resonance, Fourier transform infrared and Raman studies. The absorption spectra of these glass ceramics exhibited a broad absorption band in the range 650-950 nm which is ascribed to 2B1g → 2B2g octahedral transition of Cu2+ ions. A feeble band around 364 nm is also identified in the samples doped with CuO up to 0.6 mol% as being due to charge transfer between the two oxidation states Cu2+ and Cu+ of copper ions. The EPR spectrum recorded at room temperature exhibited a strong resonance signal at g⊥ = 2.072 and a shallow quadruplet at about gǁ = 2.401. FTIR and Raman spectra of the titled samples provide significant information about various structural units viz., silicate, germanate, PbO4, PbO6, AlO6, TeO4 and TeO3 that are present in these ceramic matrix. Analysis of the spectroscopic investigations reveals that with an increase in the concentration of CuO up to 0.6 mol% copper ions do exist in Cu2+ and Cu+ states and they act as modifiers and net work formers respectively. Therefore, glass ceramic sample contains 0.6 mol% of CuO is favorable for memory switching action.

Synthesis and characterization of SnO2, TiO2 and Ti0.5Sn0.5O2 nanoparticles as efficient materials for photocatalytic activity

Science.gov (United States)

Bargougui, R.; Pichavant, A.; Hochepied, J.-F.; Berger, M.-H.; Gadri, A.; Ammar, S.

2016-08-01

This work reports the synthesis of polydispersible SnO2, TiO2 and Ti0.5Sn0.5O2 nanoparticles via microwave-assisted polyol as an efficient method using diethylene glycol (DEG) and triethylene glycol (TREG) as solvent. The properties of as-prepared samples were investigated by X-ray diffractometry, transmission electron microscopy, diffuse reflectance and FTIR spectrophotometery, photoluminescence spectroscopy and N2 physisorption. The X-ray diffraction patterns of the samples were indexed on the anatase phase of TiO2 and cassiterite phase of SnO2 and Ti0.5Sn0.5O2. The TEM images show uniform isotropic morphologies with average sizes close to10 nm. The band gap is reduced for Ti0.5Sn0.5O2 and enhances visible light absorption, a shift resulting in the absorption threshold towards the visible spectral range, compared to pure titania and tin. Slight shifts to longer wavelength are attributed to the change in the acceptor's level induced by the mixture of both oxides. The evaluation of the photocatalytic activity is carried out using indigo carmine (IC) as model of chemical pollutants in UV irradiation conditions. The photocatalytic decolorization of the dye follows a pseudo-first-order kinetics and the constant apparent rate was increased with the increase of the tin oxide content up to 50%.

Photocatalytic activity of TiO2/Nb2O5/PANI and TiO2/Nb2O5/RGO as new nanocomposites for degradation of organic pollutants.

Science.gov (United States)

Zarrin, Saviz; Heshmatpour, Felora

2018-06-05

In this study, highly active titanium dioxide modified by niobium oxide (Nb 2 O 5 ), polymer (PANI) and reduced graphene oxide (RGO) were successfully prepared. The morphology, structure, surface area and light absorption properties of the present nanocomposites for removal of methylene blue (MB) and methyl orange (MO) were investigated and compared with those of TiO 2 /Nb 2 O 5 and TiO 2 nanoparticles. The characterization techniques such as XRD, FT-IR, UV-vis, SEM, EDX, BET and TEM were employed in order to identify the nanocomposites. Also, photocatalytic properties of TiO 2 /Nb 2 O 5 /PANI and TiO 2 /Nb 2 O 5 /RGO nanocomposites under visible light irradiation were studied. In this way, the obtained results were compared to each other and also compared to TiO 2 /Nb 2 O 5 and TiO 2 nanoparticles. In this context, the chemical oxygen demand (COD) removal follows the photodegradation in observed performance. The results indicate that reduced TiO 2 /Nb 2 O 5 nanocomposite is effectively modified by graphene oxide to give TiO 2 /Nb 2 O 5 /RGO composite. The TiO 2 /Nb 2 O 5 /RGO exhibits significantly higher photocatalytic activity in degradation of organic dyes under visible light rather than that of TiO 2 /Nb 2 O 5 /PANI, TiO 2 /Nb 2 O 5 and pure TiO 2 . Copyright © 2018 Elsevier B.V. All rights reserved.

Infrared Spectroscopy and Raman Scattering Studies on the Structure of Ag2O. B2O3. TeO2 Glass

International Nuclear Information System (INIS)

Thazin Myint; Soe Soe Thin; Pho Kaung; Sein Htoon

2006-06-01

Infrared spectroscopy investigation of silver - borate - tellurite glasses in the system 0.4 Ag2 O. 0.6 (x B2 O2. (1-x) TeO2) for various of x (0 < x < 1) has been performed in order to understand the glass modifying properties of the TeO2. In pure crystalline TeO2 spectra observed absorption bands at 780 cm-1 and 660 cm-1 have been ascribed to the stretching vibration of TeO bonds in the TeO4 units. In the glass 0.4 Ag2 O. 0.6 (x B2 O3. (1-x) TeO2) the bands at 700 cm-1 and 694 cm-1 are assigned to the symmetric breathing vibration of the boroxol group and the pentaborate one. The glasses show bands at 630 cm-1 which corresponds to the vibrations due to TeO4 units

Structural, optical and magnetic studies of CuFe2O4, MgFe2O4 and ZnFe2O4 nanoparticles prepared by hydrothermal/solvothermal method

Science.gov (United States)

Kurian, Jessyamma; Mathew, M. Jacob

2018-04-01

In this paper we report the structural, optical and magnetic studies of three spinel ferrites namely CuFe2O4, MgFe2O4 and ZnFe2O4 prepared in an autoclave under the same physical conditions but with two different liquid medium and different surfactant. We use water as the medium and trisodium citrate as the surfactant for one method (Hydrothermal method) and ethylene glycol as the medium and poly ethylene glycol as the surfactant for the second method (solvothermal method). The phase identification and structural characterization are done using XRD and morphological studies are carried out by TEM. Cubical and porous spherical morphologies are obtained for hydrothermal and solvothermal process respectively without any impurity phase. The optical studies are carried out using FTIR and UV-Vis reflectance spectra. In order to elucidate the nonlinear optical behaviour of the prepared nanomaterial, open aperture z-scan technique is used. From the fitted z-scan curves nonlinear absorption coefficient and the saturation intensity are determined. The magnetic characterization of the samples is performed at room temperature using vibrating sample magnetometer measurements. The M-H curves obtained are fitted using theoretical equation and the different components of magnetization are determined. Nanoparticles with high saturation magnetization are obtained for MgFe2O4 and ZnFe2O4 prepared under solvothermal reaction. The magnetic hyperfine parameters and the cation distribution of the prepared materials are determined using room temperature Mössbauer spectroscopy. The fitted spectra reveal the difference in the magnetic hyperfine parameters owing to the change in size and morphology.

Molecular dynamics simulation based on the multi-component molecular orbital method: Application to H5O2+,D5O2+,andT5O2+

International Nuclear Information System (INIS)

Ishimoto, Takayoshi; Koyama, Michihisa

2012-01-01

Graphical abstract: Molecular dynamics method based on multi-component molecular orbital method was applied to basic hydrogen bonding systems, H 5 O 2 + , and its isotopomers (D 5 O 2 + andT 5 O 2 + ). Highlights: ► Molecular dynamics method with nuclear quantum effect was developed. ► Multi-component molecular orbital method was used as ab initio MO calculation. ► Developed method applied to basic hydrogen bonding system, H 5 O 2 + , and isotopomers. ► O ⋯ O vibrational stretching reflected to the distribution of protonic wavefunctions. ► H/D/T isotope effect was also analyzed. - Abstract: We propose a molecular dynamics (MD) method based on the multi-component molecular orbital (MC M O) method, which takes into account the quantum effect of proton directly, for the detailed analyses of proton transfer in hydrogen bonding system. The MC M O based MD (MC M O-MD) method is applied to the basic structures, H 5 O 2 + (called “Zundel ion”), and its isotopomers (D 5 O 2 + andT 5 O 2 + ). We clearly demonstrate the geometrical difference of hydrogen bonded O ⋯ O distance induced by H/D/T isotope effect because the O ⋯ O in H-compound was longer than that in D- or T-compound. We also find the strong relation between stretching vibration of O ⋯ O and the distribution of hydrogen bonded protonic wavefunction because the protonic wavefunction tends to delocalize when the O ⋯ O distance becomes short during the dynamics. Our proposed MC M O-MD simulation is expected as a powerful tool to analyze the proton dynamics in hydrogen bonding systems.

Optical and photoelectrochemical studies on Ag{sub 2}O/TiO{sub 2} double-layer thin films

Energy Technology Data Exchange (ETDEWEB)

Li, Chuan, E-mail: cli10@yahoo.com [Department of Biomedical Engineering, National Yang Ming University, Taipei, Taiwan 11221 (China); Department of Mechanical Engineering, National Central University, Jhongli, Taoyuan, Taiwan 32001 (China); Hsieh, J.H. [Department of Materials Engineering, Ming Chi University of Technology, Taishan, Taipei, Taiwan 24301 (China); Cheng, J.C. [Department of Electronic Engineering, National Taipei University of Technology, Taipei, Taiwan 10608 (China); Huang, C.C. [Department of Biomedical Engineering, National Yang Ming University, Taipei, Taiwan 11221 (China)

2014-11-03

When two different oxides films stacked together, if the absorption (upper) layer has both its conduction and valence bands more negatively lower than that of the layer underneath, then the photo-excited electrons can be forwarded to the underneath layer to become an effect of energy storage. Recent studies discovered that the double-layers of Cu{sub 2}O/TiO{sub 2} films possess such capacity. In order to investigate this specific phenomenon, we use a DC magnetron reactive sputtering to deposit a double-layer of Ag{sub 2}O/TiO{sub 2} films on glass substrate. The film thicknesses of the double-layer are 300 nm and 200 nm respectively. X-Ray diffraction (XRD), scanning electron microscope (SEM) and UV–VIS–NIR photospectrometer and photoluminance tests were used to study the structure, morphology, optical absorption and band gaps of the stacked films. From XRD and SEM, we can confirm the microstructures of each layer. The UV–VIS–NIR spectrum revealed that the optical absorption of Ag{sub 2}O/TiO{sub 2} fell in between the single film of Ag{sub 2}O and TiO{sub 2}. Further, two band gaps were estimated for Ag{sub 2}O/TiO{sub 2} films based on the Beer-Lambert law and Tauc plot. Photoluminance and photoelectrochemical tests indicated that delayed emission by electron-hole recombination and photoelectrical current was effectively support the mechanism of electrons transfer from Ag{sub 2}O to TiO{sub 2} at Ag{sub 2}O/TiO{sub 2} interface in the double-layer films. - Highlights: • A double-layer of Ag{sub 2}O/TiO{sub 2} films was deposited on glass substrate by sputtering. • XRD confirms the nanocrystalline structures of the stack deposited films. • UV–VIS–NIR spectroscopy shows the enhanced of optical absorption in Ag{sub 2}O/TiO{sub 2}. • Photoluminance and photoelectrochemical tests show electron-hole separation effect.

CuO, MnO2 and Fe2O3 doped biomass ash as silica source for glass production in Thailand

Directory of Open Access Journals (Sweden)

N. Srisittipokakun

Full Text Available In this research, glass productions from rice husk ash (RHA and the effect of BaO, CuO, MnO2 and Fe2O3 on physical and optical properties were investigated. All properties were compared with glass made from SiO2 using same preparations. The results show that a higher density and refractive index of BaO, CuO, MnO2 and Fe2O3 doped in RHA glasses were obtained, compared with SiO2 glasses. The optical spectra show no significant difference between both glasses. The color of CuO glasses show blue from the absorption band near 800 nm (2B1g → 2B2g due to Cu2+ ion in octahedral coordination with a strong tetragonal distortion. The color of MnO2 glasses shows brown from broad band absorption at around 500 nm. This absorption band is assigned to a single allowed 5Eg → 5T2g transition which arises from the Mn3+ ions (3d4 configuration in octahedral symmetry. The yellow color derives from F2O3 glass due to the homogeneous distribution of Fe3+ (460 nm and Fe2+ (1050 nm ions in the glass matrices. Glass production from RHA is possible and is a new option for recycling waste from biomass power plant systems and air pollution reduction. Keywords: Rice husk ash, Glass, Optical, Physical

TiO{sub 2} and TiO{sub 2}-SiO{sub 2} thin films and powders by one-step soft-solution method: Synthesis and characterizations

Energy Technology Data Exchange (ETDEWEB)

Ennaoui, A.; Sankapal, B.R.; Skryshevsky, V.; Lux-Steiner, M.Ch. [Division Solar Energy Research, Department Heterogeneous Material Systems, Hahn-Meitner-Institut, Glienicker Strasse 100, 14109 Berlin (Germany)

2006-06-15

Simple soft-solution method has been developed to synthesize films and powders of TiO{sub 2} and mixed TiO{sub 2}-SiO{sub 2} at relatively low temperatures. This method is simple and inexpensive. Furthermore, reactor can be designed for large-scale applications as well as to produce large quantities of composite powders in a single step. For the preparation of TiO{sub 2}, we used aqueous acidic medium containing TiOSO{sub 4} and H{sub 2}O{sub 2}, which results in a peroxo-titanium precursor while colloidal SiO{sub 2} has been added to the precursor for the formation of TiO{sub 2}-SiO{sub 2}. Post annealing at 500{sup o}C is necessary to have anatase structure. Resulting films and powders were characterized by different techniques. TiO{sub 2} (anatase) phase with (101) preferred orientation has been obtained. Also in TiO{sub 2}-SiO{sub 2} mixed films and powders, TiO{sub 2} (anatase) phase was found. Fourier transform infrared spectroscopy (FTIR) results for TiO{sub 2} and mixed TiO{sub 2}-SiO{sub 2} films have been presented and discussed. The method developed in this paper allowed obtaining compact and homogeneous TiO{sub 2} films. These compact films are highly photoactive when TiO{sub 2} is used as photo anode in an photoelectrochemical cell. Nanoporous morphology is obtained when SiO{sub 2} colloids are added into the solution. (author)

Synthesis and characterization of TiO2 nanoparticles by the method Pechini

International Nuclear Information System (INIS)

Zoccal, Joao Victor Marques; Arouca, Fabio de Oliveira; Goncalves, Jose Antonio Silveira

2009-01-01

In recent years, scientific research showed an increasing interest in the field of nanotechnology, resulting in several techniques for the production of nanoparticles, such as methods of chemical synthesis. Among the various existing methods, the Pechini method has been used to obtain nanoparticles of titanium dioxide (TiO 2 ). Thus, this work aims to synthesize and characterize nanoparticles of TiO 2 obtained by this method. The technique constitutes in the reaction between citric acid with titanium isopropoxide, resulting as the product the titanium citrate. With the addition of the ethylene glycol polymerization occurs, resulting in a polymeric resin. At the end of the process, the resin is calcined to remove organic matter, creating nanoparticles of TiO 2 . The resulting powders were characterized by thermogravimetric analysis (TGA) and thermal differential analysis (DTA), X-ray diffraction, absorption spectrophotometry in the infrared, method of adsorption nitrogen / helium (BET method) and scanning electron microscopy. The results obtained in the characterization techniques showed that the Pechini method is promising in obtaining nanosized TiO 2 . (author)

Microporous Ni@NiO nanoparticles prepared by chemically dealloying Al_3Ni_2@Al nanoparticles as a high microwave absorption material

International Nuclear Information System (INIS)

Pang, Yu; Xie, Xiubo; Li, Da; Chou, Wusheng; Liu, Tong

2017-01-01

The Al_3Ni_2@Al nanoparticles (NPs) were prepared from Ni_4_5Al_5_5 master alloy by hydrogen plasma-metal reaction method, and were subsequently dealloyed to produce porous Ni@NiO NPs of 36 nm. The pore size ranges from 0.7 to 1.6 nm, leading to large specific surface area of 69.5 m"2/g and big pore volume of 0.507 cc/g. The saturation magnetization (M_S) and coercivity (H_C) of the microporous Ni@NiO NPs are 11.5 emu/g and 5.2 Oe. They exhibit high microwave absorption performance with a minimum reflection coefficient (RC) of −86.9 dB and an absorption bandwidth of 2.6 GHz (RC≤−10 dB) at thickness of 4.5 mm. The enhanced microwave absorption properties are attributed to the synergistic effect of the magnetic Ni core and dielectric NiO shell, and the micropore architecture. The NPs with micropore morphology and core/shell structure open a new way to modify the microwave absorption performance. - Graphical abstract: The microporous Ni/NiO nanoparticles prepared by chemically dealloying Al_3Ni_2@Al NPs exhibit high microwave absorption intensity (−86.9 dB) and wide absorption bandwidth (2.6 GHz for RC≤−10 dB). - Highlights: • Microporous Ni/NiO nanoparticals were prepared by chemically dealloying method. • They possessed micropores of 0.7–1.6 nm with a surface area of 69.5 m"2/g. • They showed high microwave absorption intensity and wide absorption bandwidth. • Microwave absorption mechanism was explained by micropore and core/shell structures.

Fabrication of Ag{sub 2}O/TiO{sub 2} with enhanced photocatalytic performances for dye pollutants degradation by a pH-induced method

Energy Technology Data Exchange (ETDEWEB)

Ren, Hai-Tao, E-mail: renhaitaomail@163.com; Yang, Qing

2017-02-28

Highlights: • Ag{sub 2}O/TiO{sub 2} was synthesized by a pH-induced chemical precipitation method. • Ag{sub 2}O/TiO{sub 2} showed good activities in the photocatalytic degradation of methyl orange. • Hydroxyl radicals played the predominant role in methyl orange photodegradation. - Abstract: Ag{sub 2}O/TiO{sub 2} composites synthesized in this study were applied into the photocatalytic degradation of methyl orange (MO) under UV and visible light irradiation. X-ray diffraction, X-ray photoelectron spectroscopy and transmission electron microscope analysis demonstrated that Ag{sub 2}O nanoparticles were well distributed on the surface of TiO{sub 2} and the heterostructure of Ag{sub 2}O/TiO{sub 2} was formed. Compared with the pure TiO{sub 2} and Ag{sub 2}O, the 3% and 50% Ag{sub 2}O/TiO{sub 2} composite displayed much higher photocatalytic activities in MO degradation under UV and visible light irradiation, respectively. The degradation rate constant of 50% composite was 0.01508 min{sup −1} under visible light, which was almost 20.1 and 1.2 times more than that of the pure TiO{sub 2} and Ag{sub 2}O, respectively. Moreover, the formation of Ag(0) on the surface of Ag{sub 2}O under illumination contributed to the high stability of Ag{sub 2}O/TiO{sub 2} photocatalysts. It was also found that hydroxyl radicals during the photocatalytic process played the predominant role in MO degradation. The enhanced photochemical activities were attributed to the formation of the heterostructure between Ag{sub 2}O and TiO{sub 2}, the strong visible light absorption and the high separation efficiency of photogenerated electron–hole pairs resulted from the highly dispersed Ag{sub 2}O particles.

Nickel complexes of o-amidochalcogenophenolate(2-)/o-iminochalcogenobenzosemiquinonate(1-) pi-radical: synthesis, structures, electron spin resonance, and x-ray absorption spectroscopic evidence.

Science.gov (United States)

Hsieh, Chung-Hung; Hsu, I-Jui; Lee, Chien-Ming; Ke, Shyue-Chu; Wang, Tze-Yuan; Lee, Gene-Hsiang; Wang, Yu; Chen, Jin-Ming; Lee, Jyh-Fu; Liaw, Wen-Feng

2003-06-16

The preparation of complexes trans-[Ni(-SeC(6)H(4)-o-NH-)(2)](-) (1), cis-[Ni(-TeC(6)H(4)-o-NH-)(2)](-) (2), trans-[Ni(-SC(6)H(4)-o-NH-)(2)](-) (3), and [Ni(-SC(6)H(4)-o-S-)(2)](-) (4) by oxidative addition of 2-aminophenyl dichalcogenides to anionic [Ni(CO)(SePh)(3)](-) proves to be a successful approach in this direction. The cis arrangement of the two tellurium atoms in complex 2 is attributed to the intramolecular Te.Te contact interaction (Te.Te contact distance of 3.455 A). The UV-vis electronic spectra of complexes 1 and 2 exhibit an intense absorption at 936 and 942 nm, respectively, with extinction coefficient epsilon > 10000 L mol(-)(1) cm(-)(1). The observed small g anisotropy, the principal g values at g(1) = 2.036, g(2) = 2.062, and g(3) = 2.120 for 1 and g(1) = 2.021, g(2) = 2.119, and g(3) = 2.250 for 2, respectively, indicates the ligand radical character accompanied by the contribution of the singly occupied d orbital of Ni(III). The X-ray absorption spectra of all four complexes show L(III) peaks at approximately 854.5 and approximately 853.5 eV. This may indicate a variation of contribution of the Ni(II)-Ni(III) valence state. According to the DFT calculation, the unpaired electron of complex 1 and 2 is mainly distributed on the 3d(xz)() orbital of the nickel ion and on the 4p(z)() orbital of selenium (tellurium, 5p(z)()) as well as the 2p(z)() orbital of nitrogen of the ligand. On the basis of X-ray structural data, UV-vis absorption, electron spin resonance, magnetic properties, DFT computation, and X-ray absorption (K- and L-edge) spectroscopy, the monoanionic trans-[Ni(-SeC(6)H(4)-o-NH-)(2)](-) and cis-[Ni(-TeC(6)H(4)-o-NH-)(2)](-) complexes are appositely described as a resonance hybrid form of Ni(III)-bis(o-amidochalcogenophenolato(2-)) and Ni(II)-(o-amidochalcogenophenolato(2-))-(o-iminochalcogenobenzosemiquinonato(1-) pi-radical; i.e., complexes 1 and 2 contain delocalized oxidation levels of the nickel ion and ligands.

Synthesis of Cu{sub 2}O/graphene/rutile TiO{sub 2} nanorod ternary composites with enhanced photocatalytic activity

Energy Technology Data Exchange (ETDEWEB)

Sun, Mingxuan, E-mail: mingxuansun@sues.edu.cn; Fang, Yalin; Wang, Ying; Sun, Shanfu; He, Jia; Yan, Zhi

2015-11-25

A ternary composite of Cu{sub 2}O, graphene and rutile TiO{sub 2} nanorods was prepared using Cu(CH{sub 3}COO){sub 2}·H{sub 2}O, graphene oxide and TiCl{sub 4} as the starting materials and its enhanced photocatalytic performance was demonstrated. Graphene/TiO{sub 2} nanorod composites (GT) were obtained by a simple hydrothermal method and then, Cu{sub 2}O was coupled onto the surface of graphene/rutile TiO{sub 2} to form Cu{sub 2}O/graphene/rutile TiO{sub 2} nanorod (CGT) composites via a chemical bath deposition process. The as-prepared sample was characterized by X-ray diffraction (XRD), emission field scanning electron microscope (FE-SEM), transmission electron microscopy (TEM), specific surface area analyzer (BET), Raman spectroscopy and ultraviolet–visible diffuse reflectance spectroscopy (UV–vis DRS). It is found that the introduction of graphene and Cu{sub 2}O has little effect on the morphology of TiO{sub 2} nanorods with average dimensions of 140 nm (length) × 30 nm (diameter) (L/D ratio ≈5). A red shift of light absorption edge and more absorption in the visible light region were observed for the resulted ternary samples compared with TiO{sub 2} and graphene/TiO{sub 2} composites. The photocatalytic activity was evaluated by the photodegradation of methylene blue under visible light irradiation, which showed 2.8 times corresponding enhancement of the degradation efficiency for the ternary composites compared with TiO{sub 2}. This work provides a new strategy to improve the visible light response of TiO{sub 2} and facilitate its application in environmental remediation. - Highlights: • A ternary composite of Cu{sub 2}O/graphene/rutile TiO{sub 2} nanorods were successfully fabricated. • Red shift and more absorption in the visible light region were observed for the ternary composites. • Improved photocatalytic degradation was detected with the introduction of Cu{sub 2}O and graphene. • Both Cu{sub 2}O and graphene played an important role

Quantitative determination of phases in ZrO2 (MgO) (Y2O3) using the Rietveld method

International Nuclear Information System (INIS)

Castro, Antonio Carlos de

2007-01-01

The key objective of this work is the crystallographic characterization of the zircon co-doped with Yttria and magnesium with the application of the Rietveld method for quantitative phase analysis of zircon polymorph (zircon monoclinic, tetragonal, and cubic). Samples of zircon polymorph were obtained from zircon doped with Yttria and magnesium at defined molar concentrations. The zircon polymorph stability during subeutetoid aging at 1350 deg C were investigated to determine ZrO 2 - MgO - Y 2 0 3 phases degradation and to define the solid solutions stability environment. ZrO 2 powders doped with 8 mol por cent of MgO and 1 mol por cent of Y 2 O 3 , and 9 mol por cent of MgO and 0 mol por cent of Y 2 O 3 have been prepared by chemical route using the co-precipitation method. These samples have been calcinate at 550 deg C, sintered at 1500 deg C and characterized by the Rietveld method using the X-ray diffraction data. The variation of the lattice parameter, changes in the phase composition and their microstructures are discussed. The application of the Rietveld method for quantitative phase analysis of zircon polymorph (zircon tetragonal and cubic) reveals no formation of tetragonal phase and indicating that the matrix is the cubic phase with low concentration of monoclinic phase.(author)

EPR and FTIR spectroscopic studies of MO-Al2O3-Bi2O3-B2O3-MnO2(M = Pb, Zn and Cd) glasses

Science.gov (United States)

Lalitha Phani, A. V.; Sekhar, K. Chandra; Chakradhar, R. P. S.; Narasimha Chary, M.; Shareefuddin, Md

2018-03-01

Glasses of the system (30-x)MO-xAl2O3-15Bi2O3-54.5B2O3-0.5MnO2 [M = Pb, Zn & Cd] (x = 0, 5, 10 & 15 mol%) were prepared by the normal melt quenching method. The amorphous nature of the prepared glasses was confirmed by the XRD studies. The EPR and FTIR studies were carried out at room temperature (RT). The EPR spectra exhibited three resonance signals at g ≈ 2.0 with a hyperfine structure, an absorption around g = 4.3 and a distinct shoulder at g = 3.3. Deconvoluted spectra were drawn for g ≈ 2.0 to resolve the six hyperfine lines. The electron paramagnetic resonance signal at g ≈ 2.0 indicates that the Mn2+ ions are in nearly perfectly octahedral symmetry. The low field signals at g = 3.3 and g = 4.3 are attributed to the Mn2+ ion which are in distorted rhombic symmetries. The hyperfine (HF) splitting constant (A) values suggested that the bonding between Mn2+ ions and its ligands is ionic in nature. The presence of BO3 and BO4 borate units, metal oxide cation units, Mn2+ and Bi-O bond vibrations in BiO3 units were noticed from the FTIR spectra.

Homogeneity of peraluminous SiO2-B2O3-Al2O3-Na2O-CaO-Nd2O3 glasses: Effect of neodymium content

International Nuclear Information System (INIS)

Gasnier, E.; Bardez-Giboire, I.; Massoni, N.; Montouillout, V.; Pellerin, N.; Allix, M.; Ory, S.; Cabie, M.; Poissonnet, S.; Massiot, D.

2014-01-01

Considering the interest of developing new glass matrices able to immobilize higher concentration of high level nuclear wastes than currently used nuclear borosilicate compositions, glasses containing high rare earth contents are of particular interest. This study focuses on a peraluminous alumino borosilicate system SiO 2 -B 2 O 3 -Al 2 O 3 -Na 2 O-CaO-Nd 2 O 3 defined by a per-alkaline/peraluminous ratio RP = ([Na 2 O] + [CaO])/ ([Na 2 O] + [CaO] + [Al 2 O 3 ]) ≤ 0.5. Samples with various contents of Nd 2 O 3 from 0 to 10 mol% were studied using DSC, XRD, SEM, TEM, STEM and EMPA methods. The glasses present a high thermal stability even after a slow cooling treatment from the melt. Only a slight mullite crystallization is detected for low Nd 2 O 3 content (≤2.3 mol%) and crystallization of a neodymium borosilicate crystalline phase combined to a phase separation occurred at high Nd 2 O 3 content (≥8 mol%). The solubility of neodymium in the presence of aluminum is demonstrated, with higher neodymium incorporation amounts than in per-alkaline glasses. (authors)

Upper limits for stratospheric H2O2 and HOCl from high resolution balloon-borne infrared solar absorption spectra

Science.gov (United States)

Larsen, J. C.; Rinsland, C. P.; Goldman, A.; Murcray, D. G.; Murcray, F. J.

1985-01-01

Solar absorption spectra from two stratospheric balloon flights have been analyzed for the presence of H2O2 and HOCl absorption in the 1230.0 to 1255.0 per cm region. The data were recorded at 0.02 per cm resolution during sunset with the University of Denver interferometer system on October 27, 1978 and March 23, 1981. Selected spectral regions were analyzed with the technique of nonlinear least squares spectral curve fitting. Upper limits of 0.33 ppbv for H2O2 and 0.36 ppbv for HOCl near 28 km are derived from the 1978 flight data while upper limits of 0.44 ppbv for H2O2 and 0.43 ppbv for HOCl at 29.5 km are obtained from the 1981 flight data.

Simultaneous absorption of SO2 and NO from flue gas with KMnO4/NaOH solutions

International Nuclear Information System (INIS)

Chu, H.; Chien, T.W.; Li, S.Y.

2001-01-01

The wet scrubbing combined SO x /NO x removal system is an advanced air pollution control device. This study attempts to understand the absorption kinetics in the system. The absorption of diluted SO 2 and simultaneous absorption of diluted SO 2 and NO, as occurs in flue gases, in a stirred tank reactor with KMnO 4 /NaOH solutions were carried out at 50C. The liquid-side and gas-side mass transfer coefficients of the system were determined. The results indicate that the absorption of SO 2 is close to completely gas-film controlled where the NaOH concentration is greater than 0.1 M or the KMnO 4 concentration is greater than 0.05 M. The increasing gas flow rate has a positive effect on the absorption rate of SO 2 . The existence of O 2 has no significant effect on the absorption rate of SO 2 . Adding SO 2 would decrease the absorption rate of NO; however, the addition of NO has no effect on the absorption rate of SO 2

Structural anisotropy in amorphous SnO2 film probed by X-ray absorption spectroscopy

Science.gov (United States)

Zhu, Q.; Ma, Q.; Buchholz, D. B.; Chang, R. P. H.; Bedzyk, M. J.; Mason, T. O.

2013-07-01

Polarization-dependent X-ray absorption measurements reveal the existence of structural anisotropy in amorphous (a-) SnO2 film. The anisotropy is readily seen for the second neighbor interaction whose magnitude differs along three measured directions. The differences can be well accounted for by 10%-20% variation in the Debye-Waller factor. Instead of a single Gaussian distribution found in crystalline SnO2, the Sn-O bond distribution is bimodal in a-SnO2 whose separation shows a weak angular dependence. The oxygen vacancies, existing in the a-SnO2 film in the order of 1021 cm-3, distribute preferentially along the film surface direction.

Morphologically controlled synthesis, structural and optical properties of CeO2/SnO2 nanocomposites

Directory of Open Access Journals (Sweden)

S. Usharani

2017-09-01

Full Text Available CeO2/SnO2 nanocomposites with different dimensional nanostructures were synthesized by a wet chemical method, using various surfactants such as SDS, CTAB and Triton X-100. The prepared CeO2/SnO2 samples were analyzed by X-ray diffraction (XRD, Fourier transform infrared (FTIR, Transmission electron microscopy (TEM, UV-Diffuse Reflectance Spectroscopy (UV-DRS, and Photoluminescence (PL spectroscopy. The XRD patterns reveal the presence of a mixed phase of SnO2 and CeO2; The TEM analysis showed the mixed morphology of uniformly dispersed spherical with ellipsoidal shape in the SDS assisted CeO2/SnO2 nanocomposites; whereas the nanostructure with spherical with hexagonal shapes was observed for the Triton X-100 assisted CeO2/SnO2 nanocomposites. The one dimensional (1D nanorod like structure observed for the CTAB assisted CeO2/SnO2 nanocomposites shows CTAB acting as a face-specific capping agent to form rod-shaped micelles. The room temperature photoluminescence emission studies of the CeO2/SnO2 nanocomposites showed strong peaks in the UV region, and several peaks in the visible region, which are likely to have originated from the oxygen vacancies and are potential materials for optoelectronic device applications. The UV results showed the absorption edges shifted to a high energy region and the blue shifts that occurred in all the samples.

Effect of SiO 2-ZrO 2 supports prepared by a grafting method on hydrogen production by steam reforming of liquefied natural gas over Ni/SiO 2-ZrO 2 catalysts

Science.gov (United States)

Seo, Jeong Gil; Youn, Min Hye; Song, In Kyu

SiO 2-ZrO 2 supports with various zirconium contents are prepared by grafting a zirconium precursor onto the surface of commercial Carbosil silica. Ni(20 wt.%)/SiO 2-ZrO 2 catalysts are then prepared by an impregnation method, and are applied to hydrogen production by steam reforming of liquefied natural gas (LNG). The effect of SiO 2-ZrO 2 supports on the performance of the Ni(20 wt.%)/SiO 2-ZrO 2 catalysts is investigated. SiO 2-ZrO 2 prepared by a grafting method serves as an efficient support for the nickel catalyst in the steam reforming of LNG. Zirconia enhances the resistance of silica to steam significantly and increases the interaction between nickel and the support, and furthermore, prevents the growth of nickel oxide species during the calcination process through the formation of a ZrO 2-SiO 2 composite structure. The crystalline structures and catalytic activities of the Ni(20 wt.%)/SiO 2-ZrO 2 catalysts are strongly influenced by the amount of zirconium grafted. The conversion of LNG and the yield of hydrogen show volcano-shaped curves with respect to zirconium content. Among the catalysts tested, the Ni(20 wt.%)/SiO 2-ZrO 2 (Zr/Si = 0.54) sample shows the best catalytic performance in terms of both LNG conversion and hydrogen yield. The well-developed and pure tetragonal phase of ZrO 2-SiO 2 (Zr/Si = 0.54) appears to play an important role in the adsorption of steam and subsequent spillover of steam from the support to the active nickel. The small particle size of the metallic nickel in the Ni(20 wt.%)/SiO 2-ZrO 2 (Zr/Si = 0.54) catalyst is also responsible for its high performance.

Photoelectrochemical properties of the TiO2-ZnO nanorod hierarchical structure prepared by hydrothermal process

Directory of Open Access Journals (Sweden)

Bao SUN

2018-02-01

Full Text Available In order to increase the transport channels of the photogenerated electrons and enhance the photosensitizer loading ability of the electrode, a new TiO2-ZnO nanorod hierarchical structure is prepared through two-step hydrothermal process. First, TiO2 nanorod array is grown on the FTO conductive glass substrate by hydrothermal proess. Then, ZnO sol is coated onto the TiO2 nanorods through dip-coating method and inverted to ZnO seed layer by sintering. Finally, the secondary ZnO nanorods are grown onto the TiO2 nanorods by the sencond hydrothermal method to form the designed TiO2-ZnO nanorod hierarchical structure. A spin-coating assisted successive ionic layer reaction method (SC-SILR is used to deposit the CdS nanocrystals into the TiO2 nanorod array and the TiO2-ZnO nanorod hierarchical structure is used to form the CdS/TiO2 and CdS/TiO2-ZnO nanocomposite films. Different methods, such as SEM, TEM, XRD, UV-Vis and transient photocurrent, are employed to characterize and measure the morphologies, structures, light absorption and photoelectric conversion performance of all the samples, respectively. The results indicate that, compared with the pure TiO2 nanorod array, the TiO2-ZnO nanorod hierarchical structure can load more CdS photosensitizer. The light absorption properties and transient photocurrent performance of the CdS/TiO2-ZnO nanorod hierarchical structure composite film are evidently superior to that of the CdS/TiO2 nanocomposite films. The excellent photoelctrochemical performance of theTiO2-ZnO hierarchical structure reveales its application prospect in photoanode material of the solar cells.

Local and Nanoscale Structure and Speciation in the PuO2+x-y(OH)2y ·zH2O System

International Nuclear Information System (INIS)

Conradson, Steven D.; Begg, Bruce D.; Clark, David L.; Den Auwer, Christophe J.; Ding, Mei; Dorhout, Peter K.; Espinosa-Faller, Francisco J.; Gordon, Pamela L.; Haire, Richard G.; Hess, Nancy J.; Hess, Ryan F.; Keogh, D. Webster; Morales, Luis A.; Neu, Mary P.; Paviet-Hartmann, Patricia; Runde, Wolfgang; Tait, C DREW; Veirs, D. Kirk; Villella, Phillip M.

2004-01-01

Pu L3 X-ray absorption fine structure spectra from 24 samples of PuO 2+x (and two related Pu substituted oxides), prepared by a variety of methods, demonstrate that (1) although the Pu sublattice remains the ordered part of the Pu distribution, the nearest-neighbor O atoms even at x = 0 are found in a multisite distribution with Pu-O distances consistent with the stable incorporation of OH - (and possibly H 2 O and H + ) into the PuO 2 lattice; (2) the excess O from oxidation is found at Pu-O distances 2 + moieties that are aperiodically distributed through the lattice; and (4) the collective interactions between these defect sites most likely cause them to cluster so as give nanoscale heterogeneity in the form of domains that may have unusual reactivity, observed as sequential oxidation by H 2 O at ambient conditions. The most accurate description of PuO 2 is therefore actually PuO 2+x-y (OH) 2y · zH 2 O, with pure, ordered, homogeneous PuO 2 attained only when H 2 O is rigorously excluded and the O activity is relatively low

Theoretical UV absorption spectra of hydrodynamically escaping O{sub 2}/CO{sub 2}-rich exoplanetary atmospheres

Energy Technology Data Exchange (ETDEWEB)

Gronoff, G.; Mertens, C. J.; Norman, R. B. [NASA LaRC, Hampton, VA (United States); Maggiolo, R. [BIRA-IASB, Avenue Circulaire 3, 1180 Brussels (Belgium); Wedlund, C. Simon [Aalto University School of Electrical Engineering Department of Radio Science and Engineering, P.O. Box 13000, FI-00076 Aalto (Finland); Bell, J. [National Institute of Aerospace, Hampton, VA (United States); Bernard, D. [IPAG, Grenoble (France); Parkinson, C. J. [University of Michigan, MI (United States); Vidal-Madjar, A., E-mail: Guillaume.P.Gronoff@nasa.gov [Observatoire de Paris, Paris (France)

2014-06-20

Characterizing Earth- and Venus-like exoplanets' atmospheres to determine if they are habitable and how they are evolving (e.g., equilibrium or strong erosion) is a challenge. For that endeavor, a key element is the retrieval of the exospheric temperature, which is a marker of some of the processes occurring in the lower layers and controls a large part of the atmospheric escape. We describe a method to determine the exospheric temperature of an O{sub 2}- and/or CO{sub 2}-rich transiting exoplanet, and we simulate the respective spectra of such a planet in hydrostatic equilibrium and hydrodynamic escape. The observation of hydrodynamically escaping atmospheres in young planets may help constrain and improve our understanding of the evolution of the solar system's terrestrial planets' atmospheres. We use the dependency of the absorption spectra of the O{sub 2} and CO{sub 2} molecules on the temperature to estimate the temperature independently of the total absorption of the planet. Combining two observables (two parts of the UV spectra that have a different temperature dependency) with the model, we are able to determine the thermospheric density profile and temperature. If the slope of the density profile is inconsistent with the temperature, then we infer the hydrodynamic escape. We address the question of the possible biases in the application of the method to future observations, and we show that the flare activity should be cautiously monitored to avoid large biases.

Crystallization behavior of (1 - x)Li2O.xNa2O.Al2O3.4SiO2 glasses

International Nuclear Information System (INIS)

Wang, Moo-Chin; Cheng, Chih-Wei; Chang, Kuo-Ming; Hsi, Chi-Shiung

2010-01-01

The crystallization behavior of the (1 - x)Li 2 O.xNa 2 O.Al 2 O 3 .4SiO 2 glasses has been investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron diffraction (ED) and energy dispersive spectroscopy (EDS). The crystalline phase was composed of β-spodumene. The isothermal crystallization kinetics of β-spodumene from the (1 - x)Li 2 O.xNa 2 O.Al 2 O 3 .4SiO 2 glasses has also been studied by a quantitative X-ray diffraction method. The activation energy of β-spodumene formation decreases from 359.2 to 317.8 kJ/mol when the Na 2 O content increases from 0 to 0.4 mol and it increases from 317.8 to 376.9 kJ/mol when the Na 2 O content increases from 0.4 to 0.6 mol. The surface nucleation and plate-like growth were dominant in the crystallization of the (1 - x)Li 2 O.xNa 2 O.Al 2 O 3 .4SiO 2 glasses.

In vitro evaluation of bioactivity of SiO2-CaO-P2O5-Na2O-CaF2-ZnO glass-ceramics

Science.gov (United States)

Riaz, Madeeha; Zia, Rehana; Saleemi, Farhat; Bashir, Farooq; Hossain, Tousif; Kayani, Zohra

2014-09-01

Zinc is an essential trace element that stimulates bone formation but it is also known as an inhibitor of apatite crystal growth. In this work addition of ZnO to SiO2-CaO-P2O5-Na2O-CaF2 glass-ceramic system was made by conventional melt-quenching technique. DSC curves showed that the addition of ZnO moved the endothermic and exothermic peaks to lower temperatures. X-ray diffraction analysis did not reveal any additional phase caused by ZnO addition and showed the presence of wollastonite and hydroxyapatite crystalline phases only in all the glass-ceramic samples. As bio-implant apatite forming ability is an essential condition, the surface reactivity of the prepared glass-ceramic specimens was studied in vitro in Kokubo's simulated body fluid (SBF) [1] with ion concentration nearly equal to human blood plasma for 30 days at 37 °C under static condition. Atomic absorption spectroscopy (AAS) was used to study the changes in element concentrations in soaking solutions and XRD, FT-IR and SEM were used to elucidate surface properties of prepared glass-ceramics, which confirmed the formation of HCAp on the surface of all glass-ceramics. It was found that the addition of ZnO had a positive effect on bioactivity of glass-ceramics and made it a potential candidate for restoration of damaged bones.

Measurements and modeling of absorption by CO2 + H2O mixtures in the spectral region beyond the CO2 ν3-band head

Science.gov (United States)

Tran, H.; Turbet, M.; Chelin, P.; Landsheere, X.

2018-05-01

In this work, we measured the absorption by CO2 + H2O mixtures from 2400 to 2600 cm-1 which corresponds to the spectral region beyond the ν3 band head of CO2. Transmission spectra of CO2 mixed with water vapor were recorded with a high-resolution Fourier-transform spectrometer for various pressure, temperature and concentration conditions. The continuum absorption by CO2 due to the presence of water vapor was determined by subtracting from measured spectra the contribution of local lines of both species, that of the continuum of pure CO2 as well as of the self- and CO2-continua of water vapor induced by the H2O-H2O and H2O-CO2 interactions. The obtained results are in very good agreement with the unique previous measurement (in a narrower spectral range). They confirm that the H2O-continuum of CO2 is significantly larger than that observed for pure CO2. This continuum thus must be taken into account in radiative transfer calculations for media involving CO2+ H2O mixture. An empirical model, using sub-Lorentzian line shapes based on some temperature-dependent correction factors χ is proposed which enables an accurate description of the experimental results.

Direct observation of ozone formation on SiO2 surfaces in O2 discharges

Science.gov (United States)

Marinov, D.; Guaitella, O.; Booth, J. P.; Rousseau, A.

2013-01-01

Ozone production is studied in a pulsed O2 discharge at pressures in the range 1.3-6.7 mbar. Time-resolved absolute concentrations of O3 and O are measured in the post-discharge using UV absorption spectroscopy and two-photon absorption laser-induced fluorescence. In a bare silica discharge tube ozone is formed mainly by three-body gas-phase recombination. When the tube surface is covered by a high specific surface silica catalyst heterogeneous formation becomes the main source of ozone. The efficiency of this surface process increases with O2 pressure and is favoured by the presence of OH groups and adsorbed H2O on the surface. At p = 6.7 mbar ozone production accounts for up to 25% of the atomic oxygen losses on the surface.

Direct observation of ozone formation on SiO2 surfaces in O2 discharges

International Nuclear Information System (INIS)

Marinov, D; Guaitella, O; Booth, J P; Rousseau, A

2013-01-01

Ozone production is studied in a pulsed O 2 discharge at pressures in the range 1.3-6.7 mbar. Time-resolved absolute concentrations of O 3 and O are measured in the post-discharge using UV absorption spectroscopy and two-photon absorption laser-induced fluorescence. In a bare silica discharge tube ozone is formed mainly by three-body gas-phase recombination. When the tube surface is covered by a high specific surface silica catalyst heterogeneous formation becomes the main source of ozone. The efficiency of this surface process increases with O 2 pressure and is favoured by the presence of OH groups and adsorbed H 2 O on the surface. At p = 6.7 mbar ozone production accounts for up to 25% of the atomic oxygen losses on the surface.

Hydrothermal synthesis of TiO2-ZnO-graphene nanocomposite towards photocatalytic and photovoltaic applications

Science.gov (United States)

Gayathri, S.; Jayabal, P.; Ramakrishnan, V.

2015-06-01

Titanium dioxide (TiO2) - Zinc oxide (ZnO) - Graphene (G) nanocomposite was successfully synthesized through facile hydrothermal method. The X-ray diffraction (XRD) pattern and the micro-Raman spectroscopic technique revealed the formation of TiO2-ZnO-Graphene (TZG) nanocomposite. The ZnO and TiO2 nanoparticles decorated graphene sheets were clearly noticeable in the Field Emission Scanning Electron Micrograph (FE-SEM). The UV-Visible absorption spectra clearly indicated that the formation of TZG nanocomposite enriched the absorption in the visible region. Hence, the prepared nanocomposite can be used as photocatalyst to remove organic dyes from water and as photoanode in the fabrication of dye sensitized solar cells (DSSCs).

Hydrothermal synthesis of TiO2-ZnO-graphene nanocomposite towards photocatalytic and photovoltaic applications

International Nuclear Information System (INIS)

Gayathri, S.; Jayabal, P.; Ramakrishnan, V.

2015-01-01

Titanium dioxide (TiO 2 ) - Zinc oxide (ZnO) - Graphene (G) nanocomposite was successfully synthesized through facile hydrothermal method. The X-ray diffraction (XRD) pattern and the micro-Raman spectroscopic technique revealed the formation of TiO 2 -ZnO-Graphene (TZG) nanocomposite. The ZnO and TiO 2 nanoparticles decorated graphene sheets were clearly noticeable in the Field Emission Scanning Electron Micrograph (FE-SEM). The UV-Visible absorption spectra clearly indicated that the formation of TZG nanocomposite enriched the absorption in the visible region. Hence, the prepared nanocomposite can be used as photocatalyst to remove organic dyes from water and as photoanode in the fabrication of dye sensitized solar cells (DSSCs)

Mixed alkali effect in borate glasses - electron paramagnetic resonance and optical absorption studies in Cu sup 2 sup + doped xNa sub 2 O- (30 - x)K sub 2 O- 70B sub 2 O sub 3 glasses

CERN Document Server

Chakradhar, R P S; Rao, J L; Ramakrishna, J

2003-01-01

The mixed alkali borate glasses xNa sub 2 O-(30 - x)K sub 2 O-70B sub 2 O sub 3 (5 sup sup 2 B sub 2 sub g) and a weak band on the higher energy side at 22 115 cm sup - sup 1 corresponding to the transition ( sup 2 B sub 1 sub g -> sup 2 E sub g). With x > 5, the higher energy band disappears and the lower energy band shifts slightly to the lower energy side. By correlating the EPR and optical absorption data, the molecular orbital coefficients alpha sup 2 and beta sub 1 sup 2 are evaluated for the different glasses investigated. The values indicate that the in-plane sigma bonding is moderately covalent while the in-plane pi bonding is significantly ionic in nature; these exhibit a minimum with x = 15, showing the MAE. The theoretical values of optical basicity of the glasses have also been evaluated. From optical absorption edges, the optical bandgap energies have been calculated and are found to lie in the range 3.00-3.40 eV. The physical properties of the glasses studied have also been evaluated with respe...

High-efficient production of SiC/SiO2 core-shell nanowires for effective microwave absorption

KAUST Repository

Zhong, Bo; Sai, Tianqi; Xia, Long; Yu, Yuanlie; Wen, Guangwu

2017-01-01

In the current report, we have demonstrated that the high-efficient production of SiC/SiO2 core-shell nanowires can be achieved through the introduction of trace of water vapor during the chemical vapor deposition process. The yield of the SiC/SiO2 core-shell nanowires is dramatically improved due to the introduction of water vapor. The SiC/SiO2 core-shell nanowires exhibit an excellent microwave absorption property in the frequency range of 2.0–18.0GHz with a very low weight percentage of 0.50wt.% in the absorbers. A minimum reflection loss value of −32.72dB (>99.99% attenuation) at 13.84GHz has been observed with the absorber thickness of 3.0mm. Moreover, the SiC/SiO2 core-shell nanowires based absorber can reach an effective absorption bandwidth (<−10dB) of 5.32GHz with the absorber thickness of 3.5mm. Furthermore, a possible absorption mechanism is also proposed in detail for such effective attenuation of microwave which can be attributed to the dielectric loss and magnetic loss of SiC/SiO2 core-shell nanowires.

High-efficient production of SiC/SiO2 core-shell nanowires for effective microwave absorption

KAUST Repository

Zhong, Bo

2017-02-21

In the current report, we have demonstrated that the high-efficient production of SiC/SiO2 core-shell nanowires can be achieved through the introduction of trace of water vapor during the chemical vapor deposition process. The yield of the SiC/SiO2 core-shell nanowires is dramatically improved due to the introduction of water vapor. The SiC/SiO2 core-shell nanowires exhibit an excellent microwave absorption property in the frequency range of 2.0–18.0GHz with a very low weight percentage of 0.50wt.% in the absorbers. A minimum reflection loss value of −32.72dB (>99.99% attenuation) at 13.84GHz has been observed with the absorber thickness of 3.0mm. Moreover, the SiC/SiO2 core-shell nanowires based absorber can reach an effective absorption bandwidth (<−10dB) of 5.32GHz with the absorber thickness of 3.5mm. Furthermore, a possible absorption mechanism is also proposed in detail for such effective attenuation of microwave which can be attributed to the dielectric loss and magnetic loss of SiC/SiO2 core-shell nanowires.

Investigation of N2O Production from 266 and 532 nm Laser Flash Photolysis of O3/N2/O2 Mixtures

Science.gov (United States)

Estupinan, E. G.; Nicovich, J. M.; Li, J.; Cunnold, D. M.; Wine, P. H.

2002-01-01

Tunable diode laser absorption spectroscopy has been employed to measure the amount of N2O produced from laser flash photolysis of O3/N2/O2 mixtures at 266 and 532 nm. In the 532 nm photolysis experiments very little N2O is observed, thus allowing an upper limit yield of 7 x 10(exp -8) to be established for the process O3 + N2 yield N2O + O2, where O3 is nascent O3 that is newly formed via O(3P(sub J)) + O2 recombination (with vibrational excitation near the dissociation energy of O3). The measured upper limit yield is a factor of approx. 600 smaller than a previous literature value and is approximately a factor of 10 below the threshold for atmospheric importance. In the 266 nm photolysis experiments, significant N2O production is observed and the N2O quantum yield is found to increase linearly with pressure over the range 100 - 900 Torr in air bath gas. The source of N2O in the 266 nm photolysis experiments is believed to be the addition reaction O(1D(sub 2)) + N2 + M yields (k(sub sigma)) N2O + M, although reaction of (very short-lived) electronically excited O3 with N2 cannot be ruled out by the available data. Assuming that all observed N2O comes from the O(1D(sub 2)) + N2 + M reaction, the following expression describes the temperature dependence of k(sub sigma) (in its third-order low-pressure limit) that is consistent with the N2O yield data: k(sub sigma) = (2.8 +/- 0.1) x 10(exp -36)(T/300)(sup -(0-88+0.36)) cm(sup 6) molecule(sup -2)/s, where the uncertainties are 2(sigma) and represent precision only. The accuracy of the reported rate coefficients at the 95% confidence level is estimated to be 30 - 40% depending on the temperature. Model calculations suggest that gas phase processes initiated by ozone absorption of a UV photon represent about 1.4% of the currently estimated global source strength of atmospheric N2O. However, these processes could account for a significant fraction of the oxygen mass-independent enrichment observed in atmospheric N2O, and

Density of Na2O-Li2O-SiO2-B2O3 Molten Slag at 1 803-1 873 K

Institute of Scientific and Technical Information of China (English)

XIAO Feng; FANG Liang

2004-01-01

The density of three kinds of molten slags was measured by modified sessile drop method at 1 803-1 873 K. The density of molten slag is found to decrease with increasing temperature. The temperature coefficients of Na2O-Li2O-SiO2 and Li2O-SiO2-B2O3 slag are smaller than that of Na2O-B2O3 slag. The molar volume of slags increases with increasing temperature.

A new ribbon-ignition method for fabricating p-CuO/n-CeO{sub 2} heterojunction with enhanced photocatalytic activity

Energy Technology Data Exchange (ETDEWEB)

Wang, Ning [School of Materials Science and Engineering, Southeast University, Jiangsu Key Laboratory for Advanced Metallic Materials, Nanjing 211189 (China); Pan, Ye, E-mail: panye@seu.edu.cn [School of Materials Science and Engineering, Southeast University, Jiangsu Key Laboratory for Advanced Metallic Materials, Nanjing 211189 (China); Lu, Tao; Li, Xingzhou; Wu, Shikai [School of Materials Science and Engineering, Southeast University, Jiangsu Key Laboratory for Advanced Metallic Materials, Nanjing 211189 (China); Wu, Jili [School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009 (China)

2017-05-01

Highlights: • A novel ribbon-ignition method was carried out to fabricate p-CuO/n-CeO{sub 2} heterojunction. • Cu-Ce binary amorphous ribbons are chosen as precursors. • Ribbon-ignition method has many advantages compared to traditional solution-based methods. • The CuO/CeO{sub 2} exhibited enhanced photodegradation activity towards RhB. • The formation of p-type CuO/n-type CeO{sub 2} heterojunction can promote the separation and transfer of the photoinduced carriers, resulting in the enhanced photocatalytic activity. - Abstract: The p-type CuO/n-type CeO{sub 2} heterojunction photocatalyst was synthesized by a facile combination of ribbon-ignition and calcination methods using Cu-Ce amorphous ribbons as precursors. The synthesized sample was characterized by X-ray diffraction (XRD), fourier transform infrared (FTIR), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and UV–vis diffuse reflectance spectroscopy (DRS). XRD, FTIR and XPS reveal the successful synthesis of CuO/CeO{sub 2} composite. The SEM and TEM images show that the sample consists of large amounts of well-dispersed blocky-shaped particles with the size distribution from 20 nm to 2 μm. DRS exhibits the absorption band (about 491 nm) and the band gap energy (2.59 eV) of the CuO/CeO{sub 2} composite. The photocatalytic activities of the samples were evaluated by degrading rhodamine B (RhB) dye (10 mg/L) under visible light (λ > 420 nm) irradiation. Compared with pure CuO and CeO{sub 2}, the CuO/CeO{sub 2} exhibited significantly enhanced photocatalytic degradation activity. The reaction rate constant of CuO/CeO{sub 2} is 0.18 min{sup −1}, which is much higher than those of CuO (0.12 min{sup −1}) and CeO{sub 2} (0.10 min{sup −1}).

Enhanced photocatalytic activity of Bi{sub 2}O{sub 3}–Ag{sub 2}O hybrid photocatalysts

Energy Technology Data Exchange (ETDEWEB)

Liu, Xinjuan, E-mail: lxj669635@126.com [Institute of Coordination Bond Metrology and Engineering, College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018 (China); Liu, Junying [Engineering Research Center for Nanophotonics & Advanced Instrument, Ministry of Education, Department of Physics, East China Normal University, Shanghai 200062 China (China); Chu, Haipeng [Institute of Coordination Bond Metrology and Engineering, College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018 (China); Li, Jinliang; Yu, Wei [Engineering Research Center for Nanophotonics & Advanced Instrument, Ministry of Education, Department of Physics, East China Normal University, Shanghai 200062 China (China); Zhu, Guang [Anhui Key Laboratory of Spin Electron and Nanomaterials, Suzhou University, Suzhou 234000 (China); Niu, Lengyuan [Institute of Coordination Bond Metrology and Engineering, College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018 (China); Sun, Zhuo [Engineering Research Center for Nanophotonics & Advanced Instrument, Ministry of Education, Department of Physics, East China Normal University, Shanghai 200062 China (China); Pan, Likun, E-mail: lkpan@phy.ecnu.edu.cn [Engineering Research Center for Nanophotonics & Advanced Instrument, Ministry of Education, Department of Physics, East China Normal University, Shanghai 200062 China (China); Sun, Chang Q. [Institute of Coordination Bond Metrology and Engineering, College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018 (China)

2015-08-30

Graphical abstract: Bi{sub 2}O{sub 3}–Ag{sub 2}O composites were fabricated for visible light photocatalytic degradation of phenol with a high degradation rate of 92% for 60 min. - Highlights: • Bi{sub 2}O{sub 3}–Ag{sub 2}O composites were synthesized via a co-precipitation method. • The photocatalytic activity for the degradation of phenol is investigated. • A high degradation rate of 92% for 60 min is achieved under visible light irradiation. - Abstract: Bi{sub 2}O{sub 3}–Ag{sub 2}O hybrid photocatalysts were successfully synthesized via a co-precipitation method. The morphology, structure and photocatalytic performance in the degradation of phenol were characterized by using scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, electrochemical impedance spectra and UV–vis absorption spectroscopy, respectively. The results show that Bi{sub 2}O{sub 3}–Ag{sub 2}O hybrid photocatalysts exhibit enhanced photocatalytic performance in the degradation of phenol with a maximum degradation rate of 92% for 60 min under visible light irradiation compared with pure Bi{sub 2}O{sub 3} (57%), which is ascribed to the increase in light adsorption and the reduction in electron–hole pair recombination with the introduction of Ag{sub 2}O.

Spectroscopic features of Ni(2+) ion in PbO-Bi2O3-SiO2 glass system.

Science.gov (United States)

Suresh, B; Srinivasa Reddy, M; Siva Sesha Reddy, A; Gandhi, Y; Ravi Kumar, V; Veeraiah, N

2015-04-15

Glasses of the composition (30-x)PbO-5Bi2O3-65SiO2: xNiO (with x ranging from 0 to 1.0 mol%) were synthesized. A variety of spectroscopic studies, viz., IR, Raman optical absorption and luminescence properties of these glasses have been carried out as a function of NiO concentration. The analysis of results of all these studies has indicated that the nickel ions occupy both octahedral and tetrahedral positions. However, with the increase of NiO concentration the octahedral occupancy of Ni(2+) ions prevailed over the tetrahedral ions. The luminescence spectra of these glasses have exhibited a broad NIR emission band in region 1100-1500 nm. This band is identified as being due to (3)T2(3F)→(3)A2(3F) octahedral transition of Ni(2+) ions. The luminescence efficiency and cross section have been found to be the highest for the glass containing the highest concentration of NiO. The reasons for such high luminescence efficiency have been discussed in the light of structural variations taking place in the host glass network. Copyright © 2015 Elsevier B.V. All rights reserved.

Enhanced photoelectrochemical performance of PbS sensitized Sb–SnO{sub 2}/TiO{sub 2} nanotube arrays electrode under visible light illumination

Energy Technology Data Exchange (ETDEWEB)

Wu, Jia; Tang, Chengli [Department of Environmental Science and Engineering, Xi’an Jiaotong University, Xi’an 710049 (China); Xu, Hao, E-mail: xuhao@mail.xjtu.edu.cn [Department of Environmental Science and Engineering, Xi’an Jiaotong University, Xi’an 710049 (China); Yan, Wei, E-mail: yanwei@mail.xjtu.edu.cn [Department of Environmental Science and Engineering, Xi’an Jiaotong University, Xi’an 710049 (China); State Key Laboratory of Multiphase Flow in Power Engineering, Xi’an Jiaotong University, Xi’an 710049 (China)

2015-06-05

Highlights: • Sb–SnO{sub 2} is used to modify TiO{sub 2} NTAs by microwave method. • PbS is employed to sensitive Sb–SnO{sub 2}/TiO{sub 2} NTAs by S-SILAR method. • Sb–SnO{sub 2} improves electrons transfer and PbS enhances visible light absorption. • The composite electrode shows enhanced photoelectrochemical properties. • The composite electrode exhibits high hydrogen evolution and high QE. - Abstract: The novel PbS sensitized Sb–SnO{sub 2}/TiO{sub 2} nanotube arrays (NTAs) composite electrode (PbS/Sb–SnO{sub 2}/TiO{sub 2} NTAs) was fabricated by microwave combined with sonication-assisted successive ionic layer adsorption and reaction technique (S-SILAR). The obtained electrodes were characterized by field-emission scanning electron microscopy (FE-SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and UV–Vis diffuse reflectance absorption spectra techniques. Enhanced photocurrent (15.52 mA/cm{sup 2}) of the PbS/Sb–SnO{sub 2}/TiO{sub 2} NTAs electrode was observed and can be attributed to the facile photo-generated electrons transfer and enhanced charge separation efficiency. Furthermore, the PbS/Sb–SnO{sub 2}/TiO{sub 2} NTAs composite electrode shows a higher H{sub 2} production rate than the Sb–SnO{sub 2}/TiO{sub 2} NTAs electrode and PbS/TiO{sub 2} NTAs electrode. The results indicate that the PbS/Sb–SnO{sub 2}/TiO{sub 2} NTAs electrode is a promising photoanode in visible photocatalytic water splitting.

Bioactivity studies on TiO2-bearing Na2O–CaO–SiO2–B2O3 glasses

International Nuclear Information System (INIS)

Jagan Mohini, G.; Sahaya Baskaran, G.; Ravi Kumar, V.; Piasecki, M.; Veeraiah, N.

2015-01-01

Soda lime silica borate glasses mixed with different concentrations of TiO 2 are synthesized by the melt-quenching technique. As a part of study on bioactivity of these glasses, the samples were immersed in simulated body fluid (SBF) solution for prolonged times (~ 21 days) during which weight loss along with pH measurements is carried out at specific intervals of time. The XRD and SEM analyses of post-immersed samples confirm the formation of crystalline hydroxyapatite layer (HA) on the surface of the samples. To assess the role of TiO 2 on the formation of HA layer and degradability of the samples the spectroscopic studies viz. optical absorption and IR spectral studies on post- and pre-immersed samples have been carried out. The analysis of the results of degradability together with spectroscopic studies as a function of TiO 2 concentration indicated that about 6.0 mol% of TiO 2 is the optimal concentration for achieving better bioactivity of these glasses. The presence of the maximal concentration octahedral titanium ions in this glass that facilitates the formation of HA layer is found to be the reason for such a higher bioactivity. - Highlights: • Soda lime silica borate glasses mixed with TiO 2 are synthesized. • Bioactivity of the glasses is studied by immersing them in SBF solution. • XRD and SEM studies indicated the formation of hydroxyapatite layer on the surface. • Quantum of degradability is the highest in the glasses mixed with 6.0 mol% of TiO 2. • The results are analyzed using IR and optical absorption studies

Electronic structures and Eu3+ photoluminescence behaviors in Y2Si2O7 and La2Si2O7

International Nuclear Information System (INIS)

Zhang Zhiya; Wang Yuhua; Zhang Feng; Cao Haining

2011-01-01

Research highlights: → Host excitation near the band gap of Y 2 Si 2 O 7 and La 2 Si 2 O 7 is analyzed. → The calculated result well explains Eu 3+ PL behaviors in Y 2 Si 2 O 7 and La 2 Si 2 O 7 . → The electronic structure and Eu 3+ VUV PL in La 2 Si 2 O 7 are first estimated. - Abstract: The electronic structures and linear optical properties of Y 2 Si 2 O 7 (YSO) and La 2 Si 2 O 7 (LSO) are calculated by LDA method based on the theory of DFT. Both YSO and LSO are direct-gap materials with the direct band gap of 5.89 and 6.06 eV, respectively. The calculated total and partial density of states indicate that in both YSO and LSO the valence band (VB) is mainly constructed from O 2p and the conduction band (CB) is mostly formed from Y 4d or La 5d. Both the calculated VB and CB of YSO exhibit relatively wider dispersion than that of LSO. In addition, the CB of YSO presents more electronic states. Meanwhile, the VB of LSO shows narrower energy distribution with higher electronic states density. The theoretical absorption of YSO shows larger bandwidth and higher intensity than that of LSO. The results are compared with the experimental host excitations and impurity photoluminescence in Eu 3+ -doped YSO and LSO.

Synthesis and electromagnetic absorption properties of Ag-coated reduced graphene oxide with MnFe{sub 2}O{sub 4} particles

Energy Technology Data Exchange (ETDEWEB)

Wang, Yan, E-mail: wangyan287580632@126.com; Wu, Xinming; Zhang, Wenzhi; Huang, Shuo

2016-04-15

A ternary composite of Ag/MnFe{sub 2}O{sub 4}/reduced graphene oxide (RGO) was synthesized by a facile hydrothermal method. The morphology, microstructure, magnetic and electromagnetic properties of as-prepared Ag/MnFe{sub 2}O{sub 4}/RGO composite were characterized by means of XRD, TEM, XPS, VSM and vector network analyzer. The maximum reflection loss (R{sub L}) of Ag/ MnFe{sub 2}O{sub 4}/RGO composite shows maximum absorption of −38 dB at 6 GHz with the thickness of 3.5 mm, and the absorption bandwidth with the R{sub L} below −10 dB is up to 3.5 GHz (from 3.7 to 7.2 GHz). The result demonstrates that the introduction of Ag significantly leads to the multiple absorbing mechanisms. It is believed that such composite could serve as a powerful candidate for microwave absorber. - Highlights: • A ternary composite of Ag/MnFe{sub 2}O{sub 4}/reduced graphene oxide (RGO) was synthesized by a facile method. • The morphology, microstructure, magnetic and electromagnetic properties were characterized. • The maximum reflection loss of Ag/MnFe{sub 2}O{sub 4}/RGO is −38 dB at 6 GHz with a thickness of 3.5 mm. • The composite shows a wide absorption band.

Study of the optical properties of TeO2-PbO-TiO2 glass system

Directory of Open Access Journals (Sweden)

Raul F. Cuevas

1998-06-01

Full Text Available We describe the preparation and some optical properties of high refractive index TeO2-PbO-TiO2 glass system. Highly homogeneous glasses were obtained by agitating the mixture during the melting process in an alumina crucible. The characterization was done by X-ray diffraction, Raman scattering, light absorption and linear refractive index measurements. The results show a change in the glass structure as the PbO content increases: the TeO4 trigonal bipyramids characteristics of TeO2 glasses transform into TeO3 trigonal pyramids. However, the measured refractive indices are almost independent of the glass composition. We show that third-order nonlinear optical susceptibilities calculated from the measured refractive indices using Lines' theoretical model are also independent of the glass composition.

Local transport properties, morphology and microstructure of ZnO decorated SiO{sub 2} nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Van Nostrand, Joseph E [Air Force Research Laboratory, Information Directorate, Rome, NY (United States); Cortez, Rebecca [Union College, Schenectady, NY (United States); Rice, Zachary P; Cady, Nathaniel C; Bergkvist, Magnus, E-mail: Joseph.VanNostrand@rl.af.mil [Albany College of Nanoscale Science and Engineering, Albany, NY (United States)

2010-10-15

We report on a novel, surfactant free method for achieving nanocrystalline ZnO decoration of an SiO{sub 2} nanoparticle at ambient temperature. The size distributions of the naked and decorated SiO{sub 2} nanoparticles are measured by means of dynamic light scattering, and a monodisperse distribution is observed for each. The morphology and microstructure of the nanoparticles are explored using atomic force microscopy and high resolution transmission electron microscopy. Investigation of the optical properties of the ZnO decorated SiO{sub 2} nanoparticles shows absorption at 350 nm. This blue shift in absorption as compared to bulk ZnO is shown to be consistent with quantum confinement effects due to the small size of the ZnO nanocrystals. Finally, the local electronic transport properties of the nanoparticles are explored by scanning conductance atomic force microscopy. A memristive hysteresis in the transport properties of the individual ZnO decorated SiO{sub 2} nanoparticles is observed. Optical absorption measurements suggest the presence of oxygen vacancies, whose migration and annihilation appear to contribute to the dynamic conduction properties of the ZnO decorated nanoparticles. We believe this to be the first demonstration of a ZnO decorated SiO{sub 2} nanoparticle, and this represents a simple yet powerful way of achieving the optical and electrical properties of ZnO in combination with the simplicity of SiO{sub 2} synthesis.

Theoretical and experimental investigation of optical absorption anisotropy in β-Ga2O3.

Science.gov (United States)

Ricci, F; Boschi, F; Baraldi, A; Filippetti, A; Higashiwaki, M; Kuramata, A; Fiorentini, V; Fornari, R

2016-06-08

The question of optical bandgap anisotropy in the monoclinic semiconductor β-Ga2O3 was revisited by combining accurate optical absorption measurements with theoretical analysis, performed using different advanced computation methods. As expected, the bandgap edge of bulk β-Ga2O3 was found to be a function of light polarization and crystal orientation, with the lowest onset occurring at polarization in the ac crystal plane around 4.5-4.6 eV; polarization along b unambiguously shifts the onset up by 0.2 eV. The theoretical analysis clearly indicates that the shift in the b onset is due to a suppression of the transition matrix elements of the three top valence bands at Γ point.

Atmospheric H2O2 measurement: comparison of cold trap method with impinger bubbling method

Science.gov (United States)

Sakugawa, H.; Kaplan, I. R.

1987-01-01

Collection of atmospheric H2O2 was performed by a cold trap method using dry ice-acetone as the refrigerant. The air was drawn by a pump into a glass gas trap immersed in the dry ice-acetone slush in a dewar flask at a flow rate of 2.5 l min-1 for approximately 2 h. Collection efficiency was > 99% and negligible interferences by O3, SO2 or organic matter with the collected H2O2 in the trap were observed. This method was compared with the air impinger bubbling method which has been previously described (Kok et al., 1978a, b, Envir. Sci. Technol. 12, 1072-1080). The measured total peroxide (H2O2 + organic peroxide) values in a series of aim samples collected by the impinger bubbling method (0.06-3.7 ppb) were always higher than those obtained by the cold trap method (0.02-1.2 ppb). Laboratory experiments suggest that the difference in values between the two methods probably results from the aqueous phase generation of H2O2 and organic peroxide in the impinger solution by a reaction of atmospheric O3 with olefinic and aromatic compounds. If these O3-organic compound reactions which occur in the impinger also occur in aqueous droplets in the atmosphere, the process could be very important for aqueous phase generation of H2O2 in clouds and rainwater.

Photocatalytic application of TiO2/SiO2-based magnetic nanocomposite (Fe3O4@SiO2/TiO2 for reusing of textile wastewater

Directory of Open Access Journals (Sweden)

Laleh Enayati Ahangar

2016-01-01

Full Text Available In this research we have developed a treatment method for textile wastewater by TiO2/SiO2-based magnetic nanocomposite. Textile wastewater includes a large variety of dyes and chemicals and needs treatments. This manuscript presents a facile method for removing dyes from the textile wastewater by using TiO2/SiO2-based nanocomposite (Fe3O4@SiO2/TiO2 under UV irradiation. This magnetic nanocomposite, as photocatalytically active composite, is synthesized via solution method in mild conditions. A large range of cationic, anionic and neutral dyes including: methyl orange, methylene blue, neutral red, bromocresol green and methyl red are used for treatment investigations. Neutral red and bromocresol green have good results in reusing treatment. The high surface area of nanocomposites improve the kinetic of wastewater treatment. In this method, by using the magnetic properties of Fe3O4 nanoparticles, TiO2-based photocatalyst could be separated and reused for 3 times. The efficiency of this method is respectively 100% and 65% for low concentration (10 ppm and high concentration (50 ppm of neutral red and bromocrosol green after 3 h treatment. The efficiency of treatment using the second used nanocomposite was 90% for 10 ppm of the same dyes.

Influence of SiO2 Addition on Properties of PTFE/TiO2 Microwave Composites

Science.gov (United States)

Yuan, Ying; Wang, Jie; Yao, Minghao; Tang, Bin; Li, Enzhu; Zhang, Shuren

2018-01-01

Composite substrates for microwave circuit applications have been fabricated by filling polytetrafluoroethylene (PTFE) polymer matrix with ceramic powder consisting of rutile TiO2 ( D 50 ≈ 5 μm) partially substituted with fused amorphous SiO2 ( D 50 ≈ 8 μm) with composition x vol.% SiO2 + (50 - x) vol.% TiO2 ( x = 0, 3, 6, 9, 12), and the effects of SiO2 addition on characteristics such as the density, moisture absorption, microwave dielectric properties, and thermal properties systematically investigated. The results show that the filler was well distributed throughout the matrix. High dielectric constant ( ɛ r > 7.19) and extremely low moisture absorption (ceramic particles served as barriers and improved the thermal stability of the PTFE polymer, retarding its decomposition. The temperature coefficient of dielectric constant ( τ ɛ ) of the composites shifted toward the positive direction (from - 309 ppm/°C to - 179 ppm/°C) as the SiO2 content was increased, while the coefficient of thermal expansion remained almost unchanged (˜ 35 ppm/°C).

Optical properties of BaO added bioactive Na2O-CaO-P2O5 glasses

Science.gov (United States)

Edathazhe, Akhila B.; Shashikala, H. D.

2018-04-01

This paper deals with the effect of BaO addition on the optical properties of bioactive Na2O-CaO-P2O5 glasses for biomedical optics applications. The phosphate glasses with composition (26-x)Na2O-xBaO-29CaO-45P2O5 (x = 0, 5, 10, 15 mol%) have been prepared by melt-quenching technique at 1100°C. The refractive index of glasses increased with BaO content. The optical band gap and Urbach energy of synthesized glasses were derived from the optical absorption spectra by using UV-Visible spectrometer. The addition of 5 mol% of BaO increased the band gap energy of glasses due to the formation of ionic cross-links in the glass structure. The defect and interstitial bonds formation in theglasses decreased with BaO additions as indicated by reductions in the Urbach energy values. No such variations in the band gap and Urbach energy values of glasses were observed with BaO content from 5 to 15 mol%. The molar and oxide ion polarizability values were calculated from the band gap and molar volume of glasses. The increase in the calculated optical basicity and metallization criteria of glasses supported the rise in band gap energy values with BaO additions. As the melting temperature of glasses decreased from 1200 to 1100°C, the refractive index increased as supported by the measured density values. The band gap energy is not changed with melting temperature. The Urbach energy decreased with decrease in melting temperature in case of BaO-free Na2O-CaO-P2O5 glasses, whereas it increased in case of BaO added glasses due to the role of BaO as modifying oxide.

Hydrothermal synthesis of TiO{sub 2}-ZnO-graphene nanocomposite towards photocatalytic and photovoltaic applications

Energy Technology Data Exchange (ETDEWEB)

Gayathri, S., E-mail: s.gayathri1010@gmail.com; Jayabal, P. [Department of Laser Studies, School of Physics, Madurai Kamaraj University, Madurai-625021 (India); Ramakrishnan, V. [Department of Laser Studies, School of Physics, Madurai Kamaraj University, Madurai-625021 (India); Indian Institute of Science Education and Research Thiruvananthapuram, Thiruvananthapuram-695016 (India)

2015-06-24

Titanium dioxide (TiO{sub 2}) - Zinc oxide (ZnO) - Graphene (G) nanocomposite was successfully synthesized through facile hydrothermal method. The X-ray diffraction (XRD) pattern and the micro-Raman spectroscopic technique revealed the formation of TiO{sub 2}-ZnO-Graphene (TZG) nanocomposite. The ZnO and TiO{sub 2} nanoparticles decorated graphene sheets were clearly noticeable in the Field Emission Scanning Electron Micrograph (FE-SEM). The UV-Visible absorption spectra clearly indicated that the formation of TZG nanocomposite enriched the absorption in the visible region. Hence, the prepared nanocomposite can be used as photocatalyst to remove organic dyes from water and as photoanode in the fabrication of dye sensitized solar cells (DSSCs)

Superstructure Ta2O5 mesocrystals derived from (NH4)2Ta2O3F6 mesocrystals with efficient photocatalytic activity.

Science.gov (United States)

Yu, Xin; Li, Wei; Huang, Jian; Li, Zhonghua; Liu, Jiawen; Hu, PingAn

2018-02-06

Superstructured mesocrystalline Ta 2 O 5 nanosheets were successfully prepared from mesocrystalline (NH 4 ) 2 Ta 2 O 3 F 6 nanorods by the annealing method for the first time. The as-prepared mesocrystalline Ta 2 O 5 nanosheets in this work showed remarkable visible light absorption, mainly due to the formation of oxygen vacancy defects in the mesocrystalline Ta 2 O 5 nanosheets, which was also confirmed by XPS spectra, Raman spectra and EPR spectra. Besides, the mesocrystalline Ta 2 O 5 nanosheets showed a highly enhanced photocatalytic activity of 11 268.24 μmol g -1 h -1 , about 3.95 times that of commercial Ta 2 O 5 . Moreover, the specific surface area of the mesocrystalline Ta 2 O 5 -800 nanosheets was 16.34 m 2 g -1 , about 5.32 times that of the commercial Ta 2 O 5 (3.072 m 2 g -1 ). The valence band XPS spectra indicated a strong oxidizing ability of the mesocrystalline Ta 2 O 5 nanosheets in comparison to that of commercial Ta 2 O 5 . The formation of superstructured Ta 2 O 5 mesocrystals generated long lifetime carriers and effective conduction pathways, which greatly enhanced the photocatalytic activity for hydrogen production.

Hotspots of soil N2O emission enhanced through water absorption by plant residue

Energy Technology Data Exchange (ETDEWEB)

Kravchenko, A.N.; Toosi, E.R.; Guber, A.K.; Ostrom, N.E.; Yu, J.; Azeem, K.; Rivers, M.L.; Robertson , G.P. (UAF Pakistan); (UC); (Hubei); (MSU)

2017-06-05

N2O is a highly potent greenhouse gas and arable soils represent its major anthropogenic source. Field-scale assessments and predictions of soil N2O emission remain uncertain and imprecise due to the episodic and microscale nature of microbial N2O production, most of which occurs within very small discrete soil volumes. Such hotspots of N2O production are often associated with decomposing plant residue. Here we quantify physical and hydrological soil characteristics that lead to strikingly accelerated N2O emissions in plant residue-induced hotspots. Results reveal a mechanism for microscale N2O emissions: water absorption by plant residue that creates unique micro-environmental conditions, markedly different from those of the bulk soil. Moisture levels within plant residue exceeded those of bulk soil by 4–10-fold and led to accelerated N2O production via microbial denitrification. The presence of large (Ø >35 μm) pores was a prerequisite for maximized hotspot N2O production and for subsequent diffusion to the atmosphere. Understanding and modelling hotspot microscale physical and hydrologic characteristics is a promising route to predict N2O emissions and thus to develop effective mitigation strategies and estimate global fluxes in a changing environment.

Forming of composites Al2O3-ZrO2 by direct coagulation casting method

International Nuclear Information System (INIS)

Tomaszewska-Grzeda, A.; Szafran, M.

2003-01-01

The role of enzymes in the DCC process in the decomposition of an appropriately selected substance which results in slow liberation over the whole volume of molecules changing the pH or also in the synthesis of salts modifying the double electric layer. The results of using the urease-urea system and the properties of ceramic casting slips, green samples and after sintering with aluminium oxide and Al 2 O 3 -nZrO 2 composites are presented in the paper. The obtained results of studies show a considerable probability of obtaining in the future of Al 2 O 3 -nZrO 2 composites of good strength parameters resulting from their high degree of thickening, providing that a deagglomeration method of nZrO 2 in the above presented processes will be elaborated. (author)

Transient infrared absorption of t-CH3C(O)OO, c-CH3C(O)OO, and α-lactone recorded in gaseous reactions of CH3CO and O2

Science.gov (United States)

Chen, Sun-Yang; Lee, Yuan-Pern

2010-03-01

A step-scan Fourier-transform infrared spectrometer coupled with a multipass absorption cell was utilized to monitor the transient species produced in gaseous reactions of CH3CO and O2; IR absorption spectra of CH3C(O)OO and α-lactone were observed. Absorption bands with origins at 1851±1, 1372±2, 1169±6, and 1102±3 cm-1 are attributed to t-CH3C(O)OO, and those at 1862±3, 1142±4, and 1078±6 cm-1 are assigned to c-CH3C(O)OO. A weak band near 1960 cm-1 is assigned to α-lactone, cyc-CH2C(O)O, a coproduct of OH. These observed rotational contours agree satisfactorily with simulated bands based on predicted rotational parameters and dipole derivatives, and observed vibrational wavenumbers agree with harmonic vibrational wavenumbers predicted with B3LYP/aug-cc-pVDZ density-functional theory. The observed relative intensities indicate that t-CH3C(O)OO is more stable than c-CH3C(O)OO by 3±2 kJ mol-1. Based on these observations, the branching ratio for the OH+α-lactone channel of the CH3CO+O2 reaction is estimated to be 0.04±0.01 under 100 Torr of O2 at 298 K. A simple kinetic model is employed to account for the decay of CH3C(O)OO.

Transient infrared absorption of t-CH3C(O)OO, c-CH3C(O)OO, and alpha-lactone recorded in gaseous reactions of CH3CO and O2.

Science.gov (United States)

Chen, Sun-Yang; Lee, Yuan-Pern

2010-03-21

A step-scan Fourier-transform infrared spectrometer coupled with a multipass absorption cell was utilized to monitor the transient species produced in gaseous reactions of CH(3)CO and O(2); IR absorption spectra of CH(3)C(O)OO and alpha-lactone were observed. Absorption bands with origins at 1851+/-1, 1372+/-2, 1169+/-6, and 1102+/-3 cm(-1) are attributed to t-CH(3)C(O)OO, and those at 1862+/-3, 1142+/-4, and 1078+/-6 cm(-1) are assigned to c-CH(3)C(O)OO. A weak band near 1960 cm(-1) is assigned to alpha-lactone, cyc-CH(2)C(=O)O, a coproduct of OH. These observed rotational contours agree satisfactorily with simulated bands based on predicted rotational parameters and dipole derivatives, and observed vibrational wavenumbers agree with harmonic vibrational wavenumbers predicted with B3LYP/aug-cc-pVDZ density-functional theory. The observed relative intensities indicate that t-CH(3)C(O)OO is more stable than c-CH(3)C(O)OO by 3+/-2 kJ mol(-1). Based on these observations, the branching ratio for the OH+alpha-lactone channel of the CH(3)CO+O(2) reaction is estimated to be 0.04+/-0.01 under 100 Torr of O(2) at 298 K. A simple kinetic model is employed to account for the decay of CH(3)C(O)OO.

Electron spin resonance insight into broadband absorption of the Cu3Bi(SeO3)2O2Br metamagnet

Science.gov (United States)

Zorko, A.; Gomilšek, M.; Pregelj, M.; Ozerov, M.; Zvyagin, S. A.; Ozarowski, A.; Tsurkan, V.; Loidl, A.; Zaharko, O.

2016-05-01

Metamagnets, which exhibit a transition from a low-magnetization to a high-magnetization state induced by the applied magnetic field, have recently been highlighted as promising materials for controllable broadband absorption. Here we show results of a multifrequency electron spin resonance (ESR) investigation of the Cu3Bi(SeO3)2O2Br planar metamagnet on the kagome lattice. Its mixed antiferromagnetic/ferromagnetic phase is stabilized in a finite range of applied fields around 0.8 T at low temperatures and is characterized by enhanced microwave absorption. The absorption signal is non-resonant and its boundaries correspond to two critical fields that determine the mixed phase. With decreasing temperature these increase like the sublattice magnetization of the antiferromagnetic phase and show no frequency dependence between 100 and 480 GHz. On the contrary, we find that the critical fields depend on the magnetic-field sweeping direction. In particular, the higher critical field, which corresponds to the transition from the mixed to the ferromagnetic phase, shows a pronounced hysteresis effect, while such a hysteresis is absent for the lower critical field. The observed hysteresis is enhanced at lower temperatures, which suggests that thermal fluctuations play an important role in destabilizing the highly absorbing mixed phase.

The Influence of TiO2 Nanoparticles on LaFeO3/TiO2 Nanocomposites for Reduction of Aqueous Organic Dyes

International Nuclear Information System (INIS)

Afifah, N.; Saleh, R.

2016-01-01

A series of Lanthanum ferrite (LaFeO3) nanoparticles over titanium dioxide (TiO2) were synthesized using sol-gel method at room temperature by varying the loading of LaFeO3 on TiO2. The magnetic properties of samples were measured using vibrating sample magnetometer and photosonocatalytic activity towards the degradation of methylene blue under light (UV or visible) and ultrasound irradiation was also evaluated. The morphology and structure of the samples were characterized by field emission scanning electron microscope, energy dispersive analysis and X-ray diffraction. Furthermore the optical properties were also characterized by UV-visible diffuse reflectance. The experimental results showed that the prepared perovskites had sphere-like shape and strong visible light absorption. LaFeO3 demonstrated ferromagnetic properties and the magnetization decreased with the incorporation of TiO2 in the samples. However, the incorporation of TiO2 increased the photosonocatalytic activity and extended the photoresponding to UV light. (paper)

Novel "203" type of heterostructured MoS2-Fe3O4-C ternary nanohybrid: Synthesis, and enhanced microwave absorption properties

Science.gov (United States)

Yang, Erqi; Qi, Xiaosi; Xie, Ren; Bai, Zhongchen; Jiang, Yang; Qin, Shuijie; Zhong, Wei; Du, Youwei

2018-06-01

It is widely recognized that constructing multiple interface structures to enhance interface polarization is very good for the attenuation of electromagnetic (EM) wave. Here, a novel "203" type of heterostructured nanohybrid consisting of two-dimensional (2D) MoS2 nanosheets, zero-dimensional (0D) Fe3O4 nanoparticles and three-dimensional (3D) carbon layers was elaborately designed and successfully synthesized by a two-step method: Fe3O4 nanoparticles were deposited onto the surface of few-layer MoS2 nanosheets by a hydrothermal method, followed by the carbonation process by a chemical vapor deposition method. Compared to that of "20" type MoS2-Fe3O4, the as-prepared heterostructured "203" type MoS2-Fe3O4-C ternary nanohybrid exhibited remarkably enhanced EM and microwave absorption properties. And the minimum reflection loss (RL) value of the obtained MoS2-Fe3O4-C ternary nanohybrid could reach -53.03 dB at 14.4 GHz with a matching thickness of 7.86 mm. Moreover, the excellent EM wave absorption property of the as-prepared ternary nanohybrid was proved to be attributed to the quarter-wavelength matching model. Therefore, a simple and effective route was proposed to produce MoS2-based mixed-dimensional van der Waals heterostructure, which provided a new platform for the designing and production of high performance microwave absorption materials.

Investigation of non linear optical properties in glasses. Case of the Na2O - TiO2 - P2O5 system

International Nuclear Information System (INIS)

Duchesne, Claire

1993-01-01

The research thesis is part of collaborative work between research laboratories on optical nonlinearities in glasses. The first part proposes an overview, in terms of optics as well as solid chemistry, of relevant criteria for the design of such materials which leads to the choice of the Na 2 O-TiO 2 -P 2 O 5 system. Characterizations means are then presented, notably X ray absorption spectroscopy (Extended X-Ray Absorption Fine Structure spectroscopy or EXAFS, and X-ray Absorption Near Edge Structure or XANES) for the glass structure analysis, and Kerr-type nonlinearity measurements by means of a Mach-Zender interferometer modified for nonlinear optics and operating in the sub-picosecond range. The next part highlights the influence of structure entities formed about the titanium atom on the noticed optical nonlinearities. The author finally reports an attempt of modelling of the linear and nonlinear response in mineral glasses under the effect of an electric perturbation [fr

Variation of energy absorption and exposure buildup factors with incident photon energy and penetration depth for boro-tellurite (B2O3-TeO2) glasses

Science.gov (United States)

Sayyed, M. I.; Elhouichet, H.

2017-01-01

The gamma ray energy absorption (EABF) and exposure buildup factors (EBF) of (100-x)TeO2-xB2O3 glass systems (where x=5, 10, 15, 20, 22.5 and 25 mol%) have been calculated in the energy region 0.015-15 MeV up to a penetration depth of 40 mfp (mean free path). The five parameters (G-P) fitting method has been used to estimate both EABF and EBF values. Variations of EABF and EBF with incident photon energy and penetration depth have been studied. It was found that EABF and EBF values were higher in the intermediate energy region, for all the glass systems. Furthermore, boro-tellurite glass with 5 mol% B2O3, was found to present the lowest EABF and EBF values, hence it is superior gamma-ray shielding material. The results indicate that the boro-tellurite glasses can be used as radiation shielding materials.

Mnx/2Nbx/2O3 ceramics

Indian Academy of Sciences (India)

Unknown

Abstract. The paper reports investigations of relative permittivity, εr, electrical conductivity, σ, saturation polarization, Ps, infrared absorption and structural properties of compensating valency substituted BaTiO3. The compositions investigated are BaTi(1–x)Mnx/2Nbx/2O3 for x = 0⋅00; 0⋅025; 0⋅05; 0⋅1; 0⋅2; 0⋅4.

Quantitative Evidence for Lanthanide-Oxygen Orbital Mixing in CeO2, PrO2, and TbO2.

Science.gov (United States)

Minasian, Stefan G; Batista, Enrique R; Booth, Corwin H; Clark, David L; Keith, Jason M; Kozimor, Stosh A; Lukens, Wayne W; Martin, Richard L; Shuh, David K; Stieber, S Chantal E; Tylisczcak, Tolek; Wen, Xiao-Dong

2017-12-13

Understanding the nature of covalent (band-like) vs ionic (atomic-like) electrons in metal oxides continues to be at the forefront of research in the physical sciences. In particular, the development of a coherent and quantitative model of bonding and electronic structure for the lanthanide dioxides, LnO 2 (Ln = Ce, Pr, and Tb), has remained a considerable challenge for both experiment and theory. Herein, relative changes in mixing between the O 2p orbitals and the Ln 4f and 5d orbitals in LnO 2 are evaluated quantitatively using O K-edge X-ray absorption spectroscopy (XAS) obtained with a scanning transmission X-ray microscope and density functional theory (DFT) calculations. For each LnO 2 , the results reveal significant amounts of Ln 5d and O 2p mixing in the orbitals of t 2g (σ-bonding) and e g (π-bonding) symmetry. The remarkable agreement between experiment and theory also shows that significant mixing with the O 2p orbitals occurs in a band derived from the 4f orbitals of a 2u symmetry (σ-bonding) for each compound. However, a large increase in orbital mixing is observed for PrO 2 that is ascribed to a unique interaction derived from the 4f orbitals of t 1u symmetry (σ- and π-bonding). O K-edge XAS and DFT results are compared with complementary L 3 -edge and M 5,4 -edge XAS measurements and configuration interaction calculations, which shows that each spectroscopic approach provides evidence for ground state O 2p and Ln 4f orbital mixing despite inducing very different core-hole potentials in the final state.

Design Of A Bi-Functional α-Fe2O3/Zn2SiO4:Mn2+ By Layer-By-Layer Assembly Method

Directory of Open Access Journals (Sweden)

Yu Ri

2015-06-01

Full Text Available This work describes the design of bi-functional α-Fe2O3/Zn2SiO4:Mn2+ using a two-step coating process. We propose a combination of pigments (α-Fe2O3 and phosphor (Zn2SiO4:Mn2+ glaze which is assembled using a layer-by-layer method. A silica-coated α-Fe2O3 pigment was obtained by a sol-gel method and a Zn2+ precursor was then added to the silica-coated α-Fe2O3 to create a ZnO layer. Finally, the Zn2SiO4:Mn2+ layer was prepared with the addition of Mn2+ ions to serve as a phosphor precursor in the multi-coated α-Fe2O3, followed by annealing at a temperature above 1000°C. Details of the phase structure, color and optical properties of the multi-functional α-Fe2O3/Zn2SiO4:Mn2+ were characterized by transmission electron microscopy and X-ray diffraction analyses.

Electronic structure study of Co doped CeO2 nanoparticles using X-ray absorption fine structure spectroscopy

International Nuclear Information System (INIS)

Kumar, Shalendra; Gautam, Sanjeev; Song, T.K.; Chae, Keun Hwa; Jang, K.W.; Kim, S.S.

2014-01-01

Highlights: • The electronic structural of Co–CeO 2 nanoparticles is investigated using XAFS. • Ce M 5,4 , Ce L 3 and O K edge NEXAFS reveal that the Ce-ions are in +4 valence state. • The NEXAFS spectrum performed at Co L3,2-edge confirms Co-ion in 2+ state. • The EXAFS analysis also show that Co ions are occupying Ce position in doped CeO 2 . • The distances between Ce–O and Ce–Ce/Co in all shells decreases with Co doping. - Abstract: We investigated the electronic structure of well characterized Co doped CeO 2 nanoparticles using X-ray absorption fine structure (XAFS) spectroscopy. Near edge X-ray absorption fine structure (NEXAFS) spectra at Ce M 5,4 , Ce L 3 and O K-edge conclude that the Ce-ions are in +4 valence state in pure as well as in Co doped CeO 2 nanoparticles. The local structure around Ce-atom in Co doped CeO 2 nanoparticles was also determined using extended X-ray absorption fine structure (EXAFS) spectroscopy at Ce L 3 edge. The EXAFS analysis suggest that the inter-atomic distance of Ce–O, Ce–Ce/Co decreases with Co doping, which indicate a contraction of the lattice. The decease in Ce–O distance also reflect that there is a formation of oxygen vacancies in CeO 2 matrix. The Debye–Waller factor also shows the consistent behaviour for all the coordination shells. The atomic multiplet calculations for Co L 3,2 -edge was performed to determine the valence state, symmetry and field splitting, which reflect that Co-ions are in 2+ state and substituted at Ce-site with crystal field splitting of 10Dq=-0.57eV. The XAFS measurements reveal that the Co-ions occupy the Ce position in the CeO 2 host matrix and create a oxygen vacancy

CoO-doped MgO-Al2O3-SiO2-colored transparent glass-ceramics with high crystallinity

Science.gov (United States)

Tang, Wufu; Zhang, Qian; Luo, Zhiwei; Yu, Jingbo; Gao, Xianglong; Li, Yunxing; Lu, Anxian

2018-02-01

To obtain CoO-doped MgO-Al2O3-SiO2 (MAS)-colored transparent glass-ceramics with high crystallinity, the glass with the composition 21MgO-21Al2O3-54SiO2-4B2O3-0.2CoO (in mol %) was prepared by conventional melt quenching technique and subsequently thermal treated at several temperatures. The crystallization behavior of the glass, the precipitated crystalline phases and crystallinity were analyzed by X-ray diffraction (XRD). The microstructure of the glass-ceramics was characterized by field emission scanning electron microscopy (FSEM). The transmittance of glass-ceramic was measured by UV spectrophotometer. The results show that a large amount of α-cordierite (indianite) with nano-size was precipitated from the glass matrix after treatment at 1020 °C for 3 h. The crystallinity of the transparent glass-ceramic reached up to 97%. Meanwhile, the transmittance of the glass-ceramic was 74% at 400 nm with a complex absorption band from 450 nm to 700 nm. In addition, this colored transparent glass-ceramic possessed lower density (2.469 g/cm3), lower thermal expansion coefficient (1.822 × 10-6 /℃), higher Vickers hardness (9.1 GPa) and higher bending strength (198 MPa) than parent glass.

Emission analysis of RE3+ (RE = Sm, Dy):B2O3-TeO2-Li2O-AlF3 glasses.

Science.gov (United States)

Raju, C Nageswara; Sailaja, S; Kumari, S Pavan; Dhoble, S J; Kumar, V Ramesh; Ramanaiah, M V; Reddy, B Sudhakar

2013-01-01

This article reports on the optical properties of 0.5% mol of Sm(3+), Dy(3+) ion-doped B2O3-TeO2-Li2O-AlF3 (LiAlFBT) glasses. The glass samples were characterized by optical absorption and emission spectra. Judd-Ofelt theory was applied to analyze the optical absorption spectra and calculate the intensity parameters and radiative properties of the emission transitions. The emission spectra of Sm(3+) and Dy(3+):LiAlFBT glasses showed a bright reddish-orange emission at 598 nm ((4)G5/2 → (6)H7/2) and an intense yellow emission at 574 nm ((4)F9/2 → (6)H13/2), respectively. Full width at half maximum (FWHM), stimulated emission cross section, gain bandwidth and optical gain values were also calculated to extend the applications of the Sm(3+) and Dy(3+):LiAlFBT glasses. Copyright © 2012 John Wiley & Sons, Ltd.

Phase diagram study for the PbO-ZnO-CaO-SiO_2 -“Fe_2O_3 ” system in air with CaO/SiO_2 in 1.1 and PbO/(CaO+SiO_2) in 2.4 weight ratios

International Nuclear Information System (INIS)

Lopez-Rodriguez, Josue; Romero-Serrano, Antonio; Hernandez-Ramirez, Aurelio; Cruz-Ramirez, Alejandro; Almaguer-Guzman, Isaias; Benavides-Perez, Ricardo; Flores-Favela, Manuel

2017-01-01

An experimental study on the phase equilibrium and the liquidus isotherms for the PbO-ZnO-CaO-SiO_2 -“Fe_2O_3 ” system with CaO/SiO_2 in 1.1 and PbO/(CaO+SiO_2) in 2.4 weight ratios, respectively, was carried out in the temperature range 1100-1300 deg C (1373-1573 K). High temperature phases were determined by the equilibrium-quenching method. Results are presented in the form of pseudo-ternary sections “Fe_2O_3 ”-ZnO-(PbO+CaO+SiO_2). X-Ray diffraction (XRD) and SEM-EDS results showed that the phase equilibria in this system are dominated by the high melting temperature spinel and zincite phases. It was observed that if the system is at a temperature below 1300 deg C and the total (Fe_2O_3 + ZnO) is greater than 20 wt%, spinel and/or zincite will be present in the slag system. As an application of the phase diagram, the liquid phase compositions below the liquidus surface were estimated, then their viscosities were calculated using FACTSage software. (author)

Phase diagrams of systems of Sr2V2O7-M2V2O7 and of Ba2V2O7-M2V2O7 (M=Ca,Cd)

International Nuclear Information System (INIS)

Fotiev, A.A.; Zhuravlev, V.D.; Zhukov, V.P.

1982-01-01

Using the methods of X-ray phase and differential thermal anlyses phase equilibria in the systems Sr 2 V 2 O 7 -M 2 V 2 O 7 and Ba 2 V 2 O 7 -M 2 V 2 O 7 , where M--Ca, Cd, are studied, their phase diagrams being built. New double pyrovanadates Mosub(0.5)Srsub(1.5)Vsub(2)Osub(7) and MBaV 2 O 7 are found [ru

Quantitative determination of phases in ZrO{sub 2} (MgO) (Y{sub 2}O{sub 3}) using the Rietveld method; Determinacao quantitativa de fases em ZrO{sub 2} - MgO - Y{sub 2}O{sub 3} utilizando o metodo de Rietveld

Energy Technology Data Exchange (ETDEWEB)

Castro, Antonio Carlos de

2007-07-01

The key objective of this work is the crystallographic characterization of the zircon co-doped with Yttria and magnesium with the application of the Rietveld method for quantitative phase analysis of zircon polymorph (zircon monoclinic, tetragonal, and cubic). Samples of zircon polymorph were obtained from zircon doped with Yttria and magnesium at defined molar concentrations. The zircon polymorph stability during subeutetoid aging at 1350 deg C were investigated to determine ZrO{sub 2} - MgO - Y{sub 2}0{sub 3} phases degradation and to define the solid solutions stability environment. ZrO{sub 2} powders doped with 8 mol por cent of MgO and 1 mol por cent of Y{sub 2}O{sub 3}, and 9 mol por cent of MgO and 0 mol por cent of Y{sub 2}O{sub 3} have been prepared by chemical route using the co-precipitation method. These samples have been calcinate at 550 deg C, sintered at 1500 deg C and characterized by the Rietveld method using the X-ray diffraction data. The variation of the lattice parameter, changes in the phase composition and their microstructures are discussed. The application of the Rietveld method for quantitative phase analysis of zircon polymorph (zircon tetragonal and cubic) reveals no formation of tetragonal phase and indicating that the matrix is the cubic phase with low concentration of monoclinic phase.(author)

Absolute linestrengths in the H2O2 nu6 band

Science.gov (United States)

May, Randy D.

1991-01-01

Absolute linestrengths at 295 K have been measured for selected lines in the nu6 band of H2O2 using a tunable diode-laser spectrometer. H2O2 concentrations in a flowing gas mixture were determined by ultraviolet (uv) absorption at 254 nm using a collinear infrared (ir) and uv optical arrangement. The measured linestrengths are approx. 60 percent larger than previously reported values when absorption by hot bands in H2O2 is taken into account.

Electrical conduction of glasses in the system Fe2O3-Sb2O3-TeO2; Fe2O3-Sb2O3-TeO2 kei garasu no denki dendo

Energy Technology Data Exchange (ETDEWEB)

Qiu, Honghua; Mori, H; Sakata, H; Hirayama, T [Tokai Univ., Tokyo (Japan). Faculty of Engineering

1995-01-01

In this study, taking into consideration that TeO2 is a component of the glass network and Sb2O3 shows the redox effect in the glasses reducing its possibility of transformation of Sb{sup 3+} to Sb{sup 5+} as well as glass basicity, highly conductive tellurite based glasses have been prepared by the press-quenching method selecting the Fe2O3-Sb2O3-TeO2 system, and the electroconductive mechanism of the glasses has been examined by measuring its D.C. conductivity {sigma}. Part of the obtained information is as follows; the glass formation range of the Fe2O3-Sb2O3-TeO2 system has been 0 {le} Fe2O3 {le} 15mol%, 0 {le} Sb2O3 {le} 18mol% and 78 {le} TeO2 {le} 100mol% and about 15mol% of the additional amount of Fe2O3 has been the limit of glass formation. As the amount of Fe2O3 has increased, C{sub Fe} has also increased and with this, the linear electroconductivity of the glasses has increased from 1.86 {times} 10{sup -7}S{center_dot}cm{sup -1} to 1.62 {times} 10{sup -6}S{center_dot}cm{sup -1} and the glasses have been confirmed as the n-type semiconductor. The factor determining {sigma} of the glasses has been C{sub Fe} which has increased as the amount of Fe2O3 has increased. 34 refs., 8 figs., 2 tabs.

Microporous Ni@NiO nanoparticles prepared by chemically dealloying Al{sub 3}Ni{sub 2}@Al nanoparticles as a high microwave absorption material

Energy Technology Data Exchange (ETDEWEB)

Pang, Yu; Xie, Xiubo; Li, Da [Key Laboratory of Aerospace Materials and Performance (Ministry of Education), School of Materials Science and Engineering, Beihang University, No.37 Xueyuan Road, Beijing 100191 (China); Chou, Wusheng [School of Mechanical Engineering and Automation, Beihang University, Beijing 100191 (China); Liu, Tong, E-mail: tongliu@buaa.edu.cn [Key Laboratory of Aerospace Materials and Performance (Ministry of Education), School of Materials Science and Engineering, Beihang University, No.37 Xueyuan Road, Beijing 100191 (China)

2017-03-15

The Al{sub 3}Ni{sub 2}@Al nanoparticles (NPs) were prepared from Ni{sub 45}Al{sub 55} master alloy by hydrogen plasma-metal reaction method, and were subsequently dealloyed to produce porous Ni@NiO NPs of 36 nm. The pore size ranges from 0.7 to 1.6 nm, leading to large specific surface area of 69.5 m{sup 2}/g and big pore volume of 0.507 cc/g. The saturation magnetization (M{sub S}) and coercivity (H{sub C}) of the microporous Ni@NiO NPs are 11.5 emu/g and 5.2 Oe. They exhibit high microwave absorption performance with a minimum reflection coefficient (RC) of −86.9 dB and an absorption bandwidth of 2.6 GHz (RC≤−10 dB) at thickness of 4.5 mm. The enhanced microwave absorption properties are attributed to the synergistic effect of the magnetic Ni core and dielectric NiO shell, and the micropore architecture. The NPs with micropore morphology and core/shell structure open a new way to modify the microwave absorption performance. - Graphical abstract: The microporous Ni/NiO nanoparticles prepared by chemically dealloying Al{sub 3}Ni{sub 2}@Al NPs exhibit high microwave absorption intensity (−86.9 dB) and wide absorption bandwidth (2.6 GHz for RC≤−10 dB). - Highlights: • Microporous Ni/NiO nanoparticals were prepared by chemically dealloying method. • They possessed micropores of 0.7–1.6 nm with a surface area of 69.5 m{sup 2}/g. • They showed high microwave absorption intensity and wide absorption bandwidth. • Microwave absorption mechanism was explained by micropore and core/shell structures.

Spectroscopic properties and energy transfer analysis of Tm3+-doped BaF2-Ga2O3-GeO2-La2O3 glass.

Science.gov (United States)

Yu, Shenglei; Yang, Zhongmin; Xu, Shanhui

2010-05-01

This paper reports on the spectroscopic properties and energy transfer analysis of Tm(3+)-doped BaF(2)-Ga(2)O(3)-GeO(2)-La(2)O(3) glasses with different Tm(2)O(3) doping concentrations (0.2, 0.5, 2.0, 2.5, 3.0, 3.5, 3.5, 4.0 wt%). Mid-IR fluorescence intensities in the range of 1,300 nm-2,200 nm have been measured when excited under an 808 nm LD for all the samples with the same pump power. Energy level structure and Judd-Ofelt parameters have been calculated based on the absorption spectra of Tm(3+), cross-relaxation rates and multi-phonon relaxation rates have been estimated with different Tm(2)O(3) doping concentrations. The maximum fluorescence intensity at around 1.8 mum has been obtained in Tm(2)O(3)-3 wt% sample and the maximum value of calculated stimulated emission cross-section of Tm(3+) in this sample is about 0.48 x 10(-20) cm(2) at 1,793 nm, and there is not any crystallization peak in the DSC curve of this sample, which indicate the potential utility of Tm(3+)-doped BaF(2)-Ga(2)O(3)-GeO(2)- La(2)O(3) glass for 2.0-microm optical fiber laser.

Efficient H2 production over Au/graphene/TiO2 induced by surface plasmon resonance of Au and band-gap excitation of TiO2

International Nuclear Information System (INIS)

Liu, Yang; Yu, Hongtao; Wang, Hua; Chen, Shuo; Quan, Xie

2014-01-01

Highlights: • Both surface plasmon resonance and band-gap excitation were used for H 2 production. • Au/Gr/TiO 2 composite photocatalyst was synthesized. • Au/Gr/TiO 2 exhibited enhancement of light absorption and charge separation. • H 2 production rate of Au/Gr/TiO 2 was about 2 times as high as that of Au/TiO 2 . - Abstract: H 2 production over Au/Gr/TiO 2 composite photocatalyst induced by surface plasmon resonance of Au and band-gap excitation of TiO 2 using graphene (Gr) as an electron acceptor has been investigated. Electron paramagnetic resonance study indicated that, in this composite, Gr collected electrons not only from Au with surface plasmon resonance but also from TiO 2 with band-gap excitation. Surface photovoltage and UV–vis absorption measurements revealed that compared with Au/TiO 2 , Au/Gr/TiO 2 displayed more effective photogenerated charge separation and higher optical absorption. Benefiting from these advantages, the H 2 production rate of Au/Gr/TiO 2 composite with Gr content of 1.0 wt% and Au content of 2.0 wt% was about 2 times as high as that of Au/TiO 2 . This work represents an important step toward the efficient application of both surface plasmon resonance and band-gap excitation on the way to converting solar light into chemical energy

Structure and Properties of La2O3-TiO2 Nanocomposite Films for Biomedical Applications

Science.gov (United States)

Zhang, Lin; Sun, Zhi-Hua; Yu, Feng-Mei; Chen, Hong-Bin

2011-01-01

The hemocompatibility of La2O3-doped TiO2 films with different concentration prepared by radio frequency (RF) sputtering was studied. The microstructures and blood compatibility of TiO2 films were investigated by scan electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), and UV-visible optical absorption spectroscopy, respectively. With the increasing of the La2O3 concentrations, the TiO2 films become smooth, and the grain size becomes smaller. Meanwhile, the band gap of the samples increases from 2.85 to 3.3 eV with increasing of the La2O3 content in TiO2 films from 0 to 3.64%. La2O3-doped TiO2 films exhibit n-type semiconductor properties due to the existence of Ti2+ and Ti3+. The mechanism of hemocompatibility of TiO2 film doped with La2O3 was analyzed and discussed. PMID:22162671

Structure and crystallization kinetics of Bi{sub 2}O{sub 3}-B{sub 2}O{sub 3} glasses

Energy Technology Data Exchange (ETDEWEB)

Cheng Yin [College of Materials Science and Engineering, Hunan University, Changsha, Hunan 410082 (China); Xiao Hanning [College of Materials Science and Engineering, Hunan University, Changsha, Hunan 410082 (China)]. E-mail: zjbcy@126.com; Guo Wenming [College of Materials Science and Engineering, Hunan University, Changsha, Hunan 410082 (China); Guo Weiming [College of Materials Science and Engineering, Hunan University, Changsha, Hunan 410082 (China)

2006-05-15

The experimental IR (infrared spectra) and differential scanning calorimetry (DSC) curves of Bi{sub 2}O{sub 3}-B{sub 2}O{sub 3} glasses, containing 30-60 mol% Bi{sub 2}O{sub 3}, have been investigated in the article. The composition dependence of IR absorption suggests that addition of Bi{sub 2}O{sub 3} results in a change in the short-range order structure of the borate matrix. The increase of Bi{sub 2}O{sub 3} content causes a progressive conversion of [BO{sub 3}] to [BO{sub 4}] units. Bi{sub 2}O{sub 3}, in the form of [BiO{sub 6}] octahedral units, plays the role of glass former. The crystallization kinetics of Bi{sub 2}O{sub 3}-B{sub 2}O{sub 3} glasses were described by thermal stability indexes (k {sub gl}, {delta}T), activation energy (E) for crystallization and numerical factors(n, m) depending on the nucleation process and growth morphology, which were calculated by Satava method and the modified Ozawa-Chen method. When Bi{sub 2}O{sub 3} {<=} 45 mol%, the increase of Bi{sub 2}O{sub 3} tends to improve the thermal stabilities of the glasses. In this case, k {sub gl} may be more suitable for estimating the glass thermal stability in above composition range than {delta}T. A further increase of Bi{sub 2}O{sub 3} content will increase the crystallization trends of investigated glasses. Two possible kinds of growth mechanisms were involved in Bi{sub 2}O{sub 3}-B{sub 2}O{sub 3} glasses: one-dimensional growth and two-dimensional growth. Moreover, structures of crystallized glasses were observed by X-ray diffraction (XRD). BiBO{sub 3} crystal with special non-linear optical properties can be obtained when Bi{sub 2}O{sub 3} {>=} 50 mol%.

Crystallization kinetics of bioactive glasses in the ZnO-Na2O-CaO-SiO2 system.

Science.gov (United States)

Malavasi, Gianluca; Lusvardi, Gigliola; Pedone, Alfonso; Menziani, Maria Cristina; Dappiaggi, Monica; Gualtieri, Alessandro; Menabue, Ledi

2007-08-30

The crystallization kinetics of Na(2)O.CaO.2SiO(2) (x = 0) and 0.68ZnO.Na(2)O.CaO.2SiO(2) (x = 0.68, where x is the ZnO stoichiometric coefficient in the glass formula) bioactive glasses have been studied using both nonisothermal and isothermal methods. The results obtained from isothermal XRPD analyses have showed that the first glass crystallizes into the isochemical Na(2)CaSi(2)O(6) phase, whereas the Na(2)ZnSiO(4) crystalline phase is obtained from the Zn-rich glass, in addition to Na(2)CaSi(2)O(6). The activation energy (Ea) for the crystallization of the Na(2)O.CaO.2SiO(2) glass is 193 +/- 10 and 203 +/- 5 kJ/mol from the isothermal in situ XRPD and nonisothermal DSC experiments, respectively. The Avrami exponent n determined from the isothermal method is 1 at low temperature (530 degrees C), and its value increases linearly with temperature increase up to 2 at 607 degrees C. For the crystallization of Na(2)CaSi(2)O(6) from the Zn-containing glass, higher values of both the crystallization temperature (667 and 661 degrees C) and Ea (223 +/- 10 and 211 +/- 5 kJ/mol) have been found from the isothermal and nonisothermal methods, respectively. The Na(2)ZnSiO(4) crystalline phase crystallizes at lower temperature with respect to Na(2)CaSi(2)O(6), and the Ea value is 266 +/- 20 and 245 +/- 15 kJ/mol from the isothermal and nonisothermal methods, respectively. The results of this work show that the addition of Zn favors the crystallization from the glass at lower temperature with respect to the Zn-free glass. In fact, it causes an increase of Ea for the Na diffusion process, determined using MD simulations, and consequently an overall increase of Ea for the crystallization process of Na(2)CaSi(2)O(6). Our results show good agreement between the Ea and n values obtained with the two different methods and confirm the reliability of the nonisothermal method applied to kinetic crystallization of glassy systems. This study allows the determination of the temperature

Synthesis of La2O3 doped Zn2SnO4 hollow fibers by electrospinning method and application in detecting of acetone

Science.gov (United States)

Yang, H. M.; Ma, S. Y.; Yang, G. J.; Chen, Q.; Zeng, Q. Z.; Ge, Q.; Ma, L.; Tie, Y.

2017-12-01

Hollow porous pure and La2O3 doped Zn2SnO4 fibers were synthesized via single capillary electrospinning technology and used for obtaining of gas sensors. The as-prepared samples were characterized by microscopy, Brunauer-Emmett-Teller, X-ray photoelectron spectroscopy and UV-vis absorption spectra. The newly obtained gas sensors were investigated for acetone detection. Compared with pure Zn2SnO4 hollow fibers, the La2O3 doped Zn2SnO4 hollow fibers not only exhibited perfect sensing performance toward acetone with excellent selectivity, high response and fast response/recovery capability (7 s for adsorption and 9 s for desorption), but also the operating temperature was reduced from 240 °C to 200 °C. These results demonstrated that the special hollow porous La doped Zn2SnO4 fibers structures were used as the sensing material for fabricating high performance acetone sensors. The acetone sensing mechanism of La2O3 doped Zn2SnO4 hollow fibers was discussed too.

Uniform Fe3O4 coating on flower-like ZnO nanostructures by atomic layer deposition for electromagnetic wave absorption.

Science.gov (United States)

Wan, Gengping; Wang, Guizhen; Huang, Xianqin; Zhao, Haonan; Li, Xinyue; Wang, Kan; Yu, Lei; Peng, Xiange; Qin, Yong

2015-11-21

An elegant atomic layer deposition (ALD) method has been employed for controllable preparation of a uniform Fe3O4-coated ZnO (ZnO@Fe3O4) core-shell flower-like nanostructure. The Fe3O4 coating thickness of the ZnO@Fe3O4 nanostructure can be tuned by varying the cycle number of ALD Fe2O3. When serving as additives for microwave absorption, the ZnO@Fe3O4-paraffin composites exhibit a higher absorption capacity than the ZnO-paraffin composites. For ZnO@500-Fe3O4, the effective absorption bandwidth below -10 dB can reach 5.2 GHz and the RL values below -20 dB also cover a wide frequency range of 11.6-14.2 GHz when the coating thickness is 2.3 mm, suggesting its potential application in the treatment of the electromagnetic pollution problem. On the basis of experimental observations, a mechanism has been proposed to understand the enhanced microwave absorption properties of the ZnO@Fe3O4 composites.

CdS Nanoparticle-Modified α-Fe2O3/TiO2 Nanorod Array Photoanode for Efficient Photoelectrochemical Water Oxidation.

Science.gov (United States)

Yin, Ruiyang; Liu, Mingyang; Tang, Rui; Yin, Longwei

2017-09-02

In this work, we demonstrate a facile successive ionic layer adsorption and reaction process accompanied by hydrothermal method to synthesize CdS nanoparticle-modified α-Fe 2 O 3 /TiO 2 nanorod array for efficient photoelectrochemical (PEC) water oxidation. By integrating CdS/α-Fe 2 O 3 /TiO 2 ternary system, light absorption ability of the photoanode can be effectively improved with an obviously broadened optical-response to visible light region, greatly facilitates the separation of photogenerated carriers, giving rise to the enhancement of PEC water oxidation performance. Importantly, for the designed abnormal type-II heterostructure between Fe 2 O 3 /TiO 2 , the conduction band position of Fe 2 O 3 is higher than that of TiO 2 , the photogenerated electrons from Fe 2 O 3 will rapidly recombine with the photogenerated holes from TiO 2 , thus leads to an efficient separation of photogenerated electrons from Fe 2 O 3 /holes from TiO 2 at the Fe 2 O 3 /TiO 2 interface, greatly improving the separation efficiency of photogenerated holes within Fe 2 O 3 and enhances the photogenerated electron injection efficiency in TiO 2 . Working as the photoanodes of PEC water oxidation, CdS/α-Fe 2 O 3 /TiO 2 heterostucture electrode exhibits improved photocurrent density of 0.62 mA cm - 2 at 1.23 V vs. reversible hydrogen electrode (RHE) in alkaline electrolyte, with an obviously negatively shifted onset potential of 80 mV. This work provides promising methods to enhance the PEC water oxidation performance of the TiO 2 -based heterostructure photoanodes.

Optical properties of ZrO2, SiO2 and TiO2-SiO2 xerogels and coatings doped with Eu3+ and Eu2+

Directory of Open Access Journals (Sweden)

Gonçalves Rogéria R.

1999-01-01

Full Text Available Eu3+ doped bulk monoliths and thin films were obtained by sol-gel methods in the ZrO2, SiO2 and SiO2-TiO2 systems. Eu3+ 5D0 ® 7FJ emission and decay time characteristics were measured during the entire experimental preparation route from the initial sol to the final xerogels. The crystalline phases identified were tetragonal ZrO2 and mixtures of rutile and anatase TiO2 at high temperature treatments in bulk samples. Good quality thin films were obtained for all systems by dip-coating optical glasses (Schott BK270. The same spectroscopic features were observed either for the bulk monoliths or the films. By appropriate heat treatments under H2 atmosphere Eu2+ containing samples could be obtained in the SiO2-TiO2 system.

Effects of Fe{sub 2}O{sub 3} content on ionic conductivity of Li{sub 2}O-TiO{sub 2}-P{sub 2}O{sub 5} glasses and glass-ceramics

Energy Technology Data Exchange (ETDEWEB)

Mohaghegh, E., E-mail: elnaz.mohaghegh@gmail.com [Department of Materials Science and Engineering, Sharif University of Technology, Tehran, 11155-9466 (Iran, Islamic Republic of); Nemati, A. [Department of Materials Science and Engineering, Sharif University of Technology, Tehran, 11155-9466 (Iran, Islamic Republic of); Eftekhari Yekta, B. [Ceramic Division, School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, 16846-13114 (Iran, Islamic Republic of); Banijamali, S. [Ceramic Division, Materials & Energy Research Center, Alborz, 31787-316 (Iran, Islamic Republic of)

2017-04-01

In this study, Li{sub 2}O-TiO{sub 2}-P{sub 2}O{sub 5}-x(Fe{sub 2}O{sub 3}) (x = 0, 2.5, 5 and 7.5 weight part) glass and glass-ceramics were synthesized through conventional melt-quenching method and subsequently heat treatment. Glass samples were studied by UV–visible spectroscopy and crystallized samples were characterized by differential thermal analysis, X-ray diffractometry and field emission scanning electron microscopy. Besides, electrical properties were examined according to the electrochemical impedance spectroscopy techniques. Experimental optical spectra of the Fe{sub 2}O{sub 3}-doped glasses revealed strong UV absorption band in the range of 330–370 nm, which were attributed to the presence of Fe{sup 3+} ions. The major crystalline phase of the fabricated glass-ceramics was LiTi{sub 2}(PO{sub 4}){sub 3}. However, Li{sub 3}PO{sub 4} was also identified as the minor one. Considering the impedance spectroscopy studies, ionic conductivity of Fe{sub 2}O{sub 3} containing glasses was higher than that of the base glass. Additionally, the maximum bulk ionic conductivity of 1.38 × 10{sup −3} S/cm was achieved as well as activation energy as low as 0.26 eV at room temperature for x = 5. - Highlights: • Bulk and total ionic conductivity was extracted by using impedance spectroscopy. • Ionic conductivity of the studied glasses and glass-ceramics increased with increasing Fe{sub 2}O{sub 3} content. • The highest bulk ionic conductivity at room temperature was found to be 1.38 × 10{sup −3} S/cm for GC{sub 5}.

Phase equilibria in the system Li2O - MoO3 - Sc2O3

International Nuclear Information System (INIS)

Safonov, V.V.; Chaban, N.G.; Porotnikov, N.V.

1984-01-01

Using the methods of DTA and X-ray phase analysis, interaction of components in the system Li 2 O-MoO 3 -Sc 2 O 3 in concentration range, adjacent to the vertex of MoO 3 , has been studied. Projection of the Li 2 MoO 4 -MoO 3 -Sc 2 (MoO 4 ) 3 system liquidus on concentrational triangle of the compositions Li 2 O-MoO 3 -Sc 2 O 3 , which consists of the fields of primary separation of Li 2 MoO 4 , Li 2 Mo 5 O 17 , Li 2 Mo 4 O 13 , MoO 3 , Sc 2 (MoO 4 ) 3 , Li 3 Sc(MoO 4 ) 3 and LiSc(MoO 4 ) 2 , is built

Growth from the melt of high-quality In2O3 and Ga2O3 single crystals

Energy Technology Data Exchange (ETDEWEB)

Fornari, Roberto; Galazka, Zbigniew; Uecker, Reinhard; Irmscher, Klaus [Leibniz Institute for Crystal Growth, Max-Born-Str. 2, 12489 Berlin (Germany)

2013-07-01

Because of their interesting properties semiconducting oxides, in particular Ga{sub 2}O{sub 3} In{sub 2}O{sub 3}, have recently received much attention. However, as they were deposited as films on hetero-substrates their quality was quite poor. The growth of high-quality bulk Ga{sub 2}O{sub 3} and In{sub 2}O{sub 3} and manufacture of the corresponding substrates can allow the deposition of high-quality epilayers with lower residual carrier density and fewer extended defects. For this reason IKZ has undertaken an effort to grow large single crystals of these oxide compounds from the melt. Transparent semiconducting Ga{sub 2}O{sub 3} single crystals with diameter of about 20 mm and 50-60 mm long were grown by the Czochralski method along the b-axis, using an Iridium crucible and a dynamic protective atmosphere to minimize the dissociation of Ga{sub 2}O{sub 3} melt and ingot. In the case of In{sub 2}O{sub 3} the Czochralski technique is not applicable and it was necessary to develop a novel melt growth method. This new method indeed supplied crystals from which oriented substrates could be prepared. In this presentation the melt growth of Ga{sub 2}O{sub 3} and In{sub 2}O{sub 3} single crystals will be reviewed. An important feature of both materials is given by their strong sensitivity to thermal processing: the free carrier concentration and the absorption spectra drastically vary as a function of annealing temperature, duration and ambient. The possible causes are discussed.

Popcorn balls-like ZnFe{sub 2}O{sub 4}-ZrO{sub 2} microsphere for photocatalytic degradation of 2,4-dinitrophenol

Energy Technology Data Exchange (ETDEWEB)

Chen, Xi [College of Chemistry and Chemical Engineering, Hunan University, Changsha 410082 (China); Liu, Yutang [Key Laboratory of Environmental Biology and Pollution Control (Hunan University), Ministry of Education, Changsha 410082 (China); Xia, Xinnian, E-mail: xnxia@hnu.edu.cn [College of Chemistry and Chemical Engineering, Hunan University, Changsha 410082 (China); Wang, Longlu [College of Chemistry and Chemical Engineering, Hunan University, Changsha 410082 (China); State Key Laboratory of Chemo/Biosensing and Chemometrics, Hunan University, Changsha 410082 (China)

2017-06-15

Highlights: • Popcorn balls-like microsphere photocatalyst. • High photocatalytic activity toward 2,4-DNP degradation. • Degradation kinetics, mechanism, active species were analyzed. • Excellent stable recycling performance. - Abstract: In this paper, novel popcorn balls-like ZnFe{sub 2}O{sub 4}-ZrO{sub 2} composite microspheres were successfully fabricated by a simple hydrothermal method. The morphology, structure and optical property of the microspheres were characterized. The microspheres were used as the photocatalysts to degrade 2,4-dinitrophenol, and exhibited superior photocatalytic performance. Under simulated solar visible light irradiation, the degradation rate of ZnFe{sub 2}O{sub 4}-ZrO{sub 2} photocatalyst (mass ratio of ZnFe{sub 2}O{sub 4}/ZrO{sub 2} = 2:1) was almost 7.4 and 2.4 times higher than those of pure ZnFe{sub 2}O{sub 4} and ZrO{sub 2}. The enhancement could attribute to stronger light absorption, lower carrier recombination and multi-porous structure of the microspheres. Moreover, the popcorn balls-like photocatalysts can be easily separated, because of the magnetism of the samples. After five times runs, the photocatalyst still showed 90% of its photocatalytic degradation efficiency. This work demonstrated a good prospect for removing organic pollutants in water.

Nd(BrO3)3-Yb(BrO3)3-H2O and Nd2(SeO4)3-Yb2(SeO4)3-H2O systems at 25 deg C

International Nuclear Information System (INIS)

Serebrennikov, V.V.; Batyreva, V.A.; Tsybukova, T.N.

1981-01-01

Using the methods of isothermal solubility the Nd(BrO 3 ) 3 - Yb(BrO 3 ) 3 -H 2 O and Nd 2 (SeO 4 ) 3 -Yb 2 (SeO 4 ) 3 -H 2 O systems are studied at 25 deg C. The compositions of the solid phases are determined by the method of ''residues''. The formation of two series of solid solutions in both systems is established. Besides, there is a crystallization region of Nd 2 (SeO 4 ) 3 in the system of selenates. The solubility diagrams of the systems are presented [ru

Effect of MnCuFe{sub 2}O{sub 4} content on magnetic and dielectric properties of poly (O-Phenylenediamine)/MnCuFe{sub 2}O{sub 4} nanocomposites

Energy Technology Data Exchange (ETDEWEB)

Kannapiran, Nagarajan [PG and Research Department of Chemistry, Sri Ramakrishna Mission Vidyalaya College of Arts and Science, Coimbatore 641020, Tamil Nadu (India); Muthusamy, Athianna, E-mail: muthusrkv@gmail.com [PG and Research Department of Chemistry, Sri Ramakrishna Mission Vidyalaya College of Arts and Science, Coimbatore 641020, Tamil Nadu (India); Chitra, Palanisamy [PG and Research Department of Chemistry, Sri Ramakrishna Mission Vidyalaya College of Arts and Science, Coimbatore 641020, Tamil Nadu (India)

2016-03-01

Poly o-phenylenediamine (PoPD)/MnCuFe{sub 2}O{sub 4} nanocomposites with three different ratios of MnCuFe{sub 2}O{sub 4} (10%, 20%, 30% w/w) were synthesized by in-situ oxidative chemical polymerization method ammonium persulphate used as oxidant, while MnCuFe{sub 2}O{sub 4} nanoparticles was prepared by auto-combustion method. The structure, morphology and magnetic properties of synthesized PoPD/MnCuFe{sub 2}O{sub 4} nanocomposites were characterized by FT-IR, UV–visible absorption spectra, X-ray diffraction (XRD), Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), Thermogravimetric analysis (TGA) and Vibrating sample magnetometer (VSM). FTIR spectra and XRD were confirmed the formation of the PoPD/MnCuFe{sub 2}O{sub 4} nanocomposites. The morphology of PoPD/MnCuFe{sub 2}O{sub 4} nanocomposites is visualized through SEM and TEM. The spherical morphology of the PoPD was confirmed using SEM analysis. Dielectric properties of PoPD/MnCuFe{sub 2}O{sub 4} nanocomposites at different temperatures have been performed in the frequency range of 50 Hz–5 MHz. The optical absorption experiments of PoPD/MnCuFe{sub 2}O{sub 4} nanocomposites reveal that the direct transition with an energy band gap is around 2 eV. - Highlights: • Green synthesis of PoPD (the polymerization carried out only in aqueous medium) by in-situ chemical polymerization method. • For the first time, PoPD incorporated with MnCuFe{sub 2}O{sub 4} with lesser particle size. • The auto combustion reaction, support to achieve less particle size. • Ferrite content affects the magnetic properties of the nanocomposites.

Effects of variation in background mixing ratios of N2, O2, and Ar on the measurement of δ18O-H2O and δ2H-H2O values by cavity ring-down spectroscopy

Science.gov (United States)

Johnson, Jennifer E.; Rella, Chris W.

2017-08-01

Cavity ring-down spectrometers have generally been designed to operate under conditions in which the background gas has a constant composition. However, there are a number of observational and experimental situations of interest in which the background gas has a variable composition. In this study, we examine the effect of background gas composition on a cavity ring-down spectrometer that measures δ18O-H2O and δ2H-H2O values based on the amplitude of water isotopologue absorption features around 7184 cm-1 (L2120-i, Picarro, Inc.). For background mixtures balanced with N2, the apparent δ18O values deviate from true values by -0.50 ± 0.001 ‰ O2 %-1 and -0.57 ± 0.001 ‰ Ar %-1, and apparent δ2H values deviate from true values by 0.26 ± 0.004 ‰ O2 %-1 and 0.42 ± 0.004 ‰ Ar %-1. The artifacts are the result of broadening, narrowing, and shifting of both the target absorption lines and strong neighboring lines. While the background-induced isotopic artifacts can largely be corrected with simple empirical or semi-mechanistic models, neither type of model is capable of completely correcting the isotopic artifacts to within the inherent instrument precision. The development of strategies for dynamically detecting and accommodating background variation in N2, O2, and/or Ar would facilitate the application of cavity ring-down spectrometers to a new class of observations and experiments.

Methods of Laser Spectroscopy in Devices for Continuous Monitoring of O2 and CO Content in Boiler Smoke Gases

Directory of Open Access Journals (Sweden)

V. A. Firago

2006-01-01

Full Text Available Application efficiency of various absorption laser spectroscopy methods for determination of gas component concentration in boiler smoke gases has been studied in the paper, O2 and CO absorption spectra have been analyzed, optimum absorption lines in near IR spectral range (about 0.76 µm for O2 and 1.56 µm for CO have been selected and graphical dependences of intensity and half-width of the selected lines on the investigated medium temperature and pressure have been shown. Processes of monitoring CO and O2 content in boiler smoke gases while using basic laser spectroscopy methods have been simulated and measuring errors have been analyzed. It has been found out that in order to decrease methodical errors of concentration measuring it is necessary to take into account the investigated medium temperature and pressure. The paper shows that the least errors of continuous CO and O2 concentration monitoring at the presence of variations in dissipative losses have been ensured by the modified correlation method though its threshold sensitivity is less than integral and correlation ones.

Structural and electrical characteristics of ZrO2-TiO2 thin films by sol-gel method

International Nuclear Information System (INIS)

Hsu, Cheng-Hsing; Tseng, Ching-Fang; Lai, Chun-Hung; Tung, Hsin-Han; Lin, Shih-Yao

2010-01-01

In this paper, we investigated electrical properties and microstructures of ZrTiO 4 (ZrO 2 -TiO 2 ) thin films prepared by the sol-gel method on ITO substrates at different annealing temperatures. All films exhibited ZrTiO 4 (1 1 1) and (1 0 1) orientations perpendicular to the substrate surface, and the grain size increased with increase in the annealing temperature. A low leakage current density of 2.06 x 10 -6 A/cm 2 was obtained for the prepared films. Considering the primary memory switching behavior of ZrTiO 4 , ReRAM based on ZrTiO 4 shows promise for future nonvolatile memory applications.

FT-IR and thermoluminescence investigation of P2O5-BaO-K2O glass system

Science.gov (United States)

Ivascu, C.; Timar-Gabor, A.; Cozar, O.

2013-11-01

The 0.5P2O5ṡxBaOṡ(0.5-x)K2O glass system (0≤x≤0.5mol%) is investigated by FT-IR and thermoluminescence as a possible dosimetic material. FT-IR spectra show structural network modifications with the composition variations of the studied glasses. The predominant absorption bands are characterized by two broad peaks near 500 cm-1, two weak peaks around 740 cm-1 and three peaks in the 900-1270 cm-1 region. The shift in the position of the band assigned to asymmetric stretching of PO2- group, υas(PO2-) modes from ˜1100 cm-1 to 1085 cm-1 and the decrease in its relative intensity with the increasing of K2O content shows a network modifier role of this oxide.. Luminescence investigations show that by adding modifier oxides in the phosphate glass a dose dependent TL signals result upon irradiation. Thus P2O5-BaO-K2O glass system is a possible candidate material for dosimetry in the dose 0 - 50 Gy range.

Characterization of physicochemical properties of Pd/TiO{sub 2} nanostructured catalysts prepared by the photodeposition method

Energy Technology Data Exchange (ETDEWEB)

Camposeco, R. [Molecular Engineering Program, Instituto Mexicano del Petróleo, 07730 México, D.F. (Mexico); Department of Chemistry, UAM-A, 55534 México, D.F. (Mexico); Castillo, S., E-mail: scastill@imp.mx [Molecular Engineering Program, Instituto Mexicano del Petróleo, 07730 México, D.F. (Mexico); Department of Chemical Engineering, ESIQIE-IPN, 75876 México, D.F. (Mexico); Mejía-Centeno, Isidro; Navarrete, J.; Marín, J. [Molecular Engineering Program, Instituto Mexicano del Petróleo, 07730 México, D.F. (Mexico)

2014-09-15

In this work, the sol–gel and hydrothermal methods were used to synthesize TiO{sub 2}-nanostructured supports. The palladium supported on sol–gel TiO{sub 2} and on hydrothermal-method-TiO{sub 2} nanotubes was obtained by incorporating it through photodeposition. The characterization was performed by X-ray diffraction, transmission electron microscopy, N{sub 2} physisorption, pulse chemisorption, ultraviolet–visible absorption spectroscopy and X-ray photoelectron spectroscopy. Both sol–gel-palladium–TiO{sub 2} and palladium-nanotube samples showed different palladium dispersion and physicochemical properties. In the palladium-nanotube sample, high surface area (243 m{sup 2}/g), H{sub 2}Ti{sub 3}O{sub 7} stable phase, and low band gap energy (2.35 eV) were obtained. Palladium-nanotubes and palladium-TiO{sub 2}, used as reference samples, were prepared by wet impregnation. - Highlights: • The precursors of TiO{sub 2} nanotubes were synthesized by the sol–gel method. • TiO{sub 2} nanostructures showed improved textural and morphological properties. • Pd nanoparticles around 1 nm were obtained by the photodeposition method. • TiO{sub 2}-nanotube-based catalysts can be a powerful tool for facing air pollution.

Atomic-Scale Structure of Al2O3-ZrO2 Mixed Oxides Prepared by Laser Ablation

International Nuclear Information System (INIS)

Yang Xiuchun; Dubiel, M.; Hofmeister, H.; Riehemann, W.

2007-01-01

By means of x-ray diffractometry (XRD) and X-ray absorption fine structure spectroscopy, the phase composition and atomic structure of laser evaporated ZrO2 and ZrO2-Al2O3 nanopowders have been studied. The results indicate that pure ZrO2 exists in the form of tetragonal structure, Al2O3 doped ZrO2 nanoparticles, however, have cubic structure. Compared to bulk tetragonal ZrO2, pure tetragonal ZrO2 nanoparticles have a shorter Zr-O- and Zr-Zr shell, indicating that the lattice contracts with decreasing particle size. For Al2O3 doped ZrO2 solid solution, the distances of first Zr-O and Zr-Zr (Al) coordination decrease with increasing solid solubility. The disorder degree of the ZrO2 lattice increases with increasing solid solubility. The coevaporated ZrO2-Al2O3 is quickly solidified into amorphous phase when it is ablated in a higher pressure. The amorphous phase contains Zr-O-Zr (Al) clusters and has shorter Zr-O distance and tower Zr-O coordination number

Complexing in the system Rb2SeO4-UO2SeO4-H2O

International Nuclear Information System (INIS)

Kuchumova, N.V.; Shtokova, I.P.; Serezhkina, L.B.; Serezhkin, V.N.

1989-01-01

Method of isothermal solubility at 25 deg C is used to study interaction of rubidium and uranyl selenates in aqueous solution. Formation of congruently soluble Rb 2 UO 2 (SeO 4 ) 2 x2H 2 O and Rb 2 (UO 2 ) 2 x(SeO 4 ) 3 x6H 2 O is stated. For the last compound crystallographic characteristics (a=10.668; b=14.935(9); c=13.891(7) A; β=104.94(1); Z=4, sp.gr. P2 1 /c) are determined. Thermal decomposition of a compound results in formation of Rb 2 U 2 O 7

Synthesis and mechanical properties of stabilized zirconia ceramics: MgO-ZrO_2 and Y_2O_3-MgO- ZrO_2

International Nuclear Information System (INIS)

Yamagata, C.; Mello-Castanho, S.R.H.; Paschoal, J.O.A.

2014-01-01

Precursor MgO-ZrO_2 and Y_2O_3-MgO-ZrO_2 ceramic powders were synthesized by the method of co-precipitation and characterized by techniques such as laser diffraction, QELS (Quasi Elastic Light Scattering), XRD, BET, and SEM. Nanoscale powders with specific surface area higher than 60 m"2. g"-"1 was achieved. Sintered ceramic obtained from the synthesized powders, were characterized to mechanical tests using Vickers indentation technique. The addition of Y_2O_3 promoted an increase in hardness of the ceramics and total cubic crystalline phase stabilization. (author)

Persistent deNOx Ability of CaAl2O4:(Eu, Nd/TiO2-xNy Luminescent Photocatalyst

Directory of Open Access Journals (Sweden)

Li Huihui

2011-01-01

Full Text Available Abstract CaAl2O4:(Eu, Nd/TiO2-xNy composite luminescent photocatalyst was successfully synthesized by a simple planetary ball milling process. Improvement of photocatalytic deNOx ability of TiO2-xNy, together with the persistent photocatalytic activity for the decomposition of NO after turning off the light were realized, by coupling TiO2-xNy with long afterglow phosphor, CaAl2O4:(Eu, Nd. The novel persistent photocatalytic behavior was related to the overlap between the absorption wavelength of TiO2-xNy and the emission wavelength of the CaAl2O4:(Eu, Nd. It was found that CaAl2O4:(Eu, Nd/TiO2-xNy composites provided the luminescence to persist photocatalytic reaction for more than 3 h after turning off the light. Graphical Abstract CaAl2O4:(Eu, Nd/TiO2-xNy composite luminescent photocatalyst with persistent deNOx activity after turning off the light was successfully synthesized by a simple planetary ball milling process. The novel persistent photocatalytic behavior was related to the overlap between the absorption wavelength of TiO2-xNy and the emission wavelength of the CaAl2O4:(Eu, Nd. Additional file 1 Click here for file

X-ray absorption spectroscopy of GeO2 glass to 64 GPa

International Nuclear Information System (INIS)

Hong, Xinguo; Newville, Matthew; Sutton, Stephen R; Rivers, Mark L; Duffy, Thomas S

2014-01-01

The structural behavior of GeO 2 glass has been investigated up to 64 GPa using results from x-ray absorption spectroscopy in a diamond anvil cell combined with previously reported density measurements. The difference between the nearest Ge–O distances of glassy and rutile-type GeO 2 disappears at the Ge–O distance maximum at 20 GPa, indicating completion of the tetrahedral–octahedral transition in GeO 2 glass. The mean-square displacement σ 2 of the Ge–O distance in the first Ge–O shell increases progressively to a maximum at 10 GPa, followed by a substantial reduction at higher pressures. The octahedral glass is, as expected, less dense and has a higher compressibility than the corresponding crystalline phase, but the differences in Ge–O distance and density between the glass and the crystals are gradually eliminated over the 20–40 GPa pressure range. Above 40 GPa, GeO 2 forms a dense octahedral glass with a compressibility similar to that of the corresponding crystalline phase (α-PbO 2 type). The EXAFS and XANES spectra show evidence for subtle changes in the dense glass continuing to occur at these high pressures. The Ge–O bond distance shows little change between 45–64 GPa, and this may reflect a balance between bond shortening and a gradual coordination number increase with compression. The density of the glass is similar to that of the α–PbO 2 -type phase, but the Ge–O distance is longer and is close to that in the higher-coordination pyrite-type phase which is stable above ∼60 GPa. The density data provide evidence for a possible discontinuity and change in compressibility at 40–45 GPa, but there are no major changes in the corresponding EXAFS spectra. A pyrite-type local structural model for the glass can provide a reasonable fitting to the XAFS spectra at 64 GPa. (paper)

Synthesis, XRD, TEM, EPR, and Optical Absorption Spectral Studies of CuZnO2 Nanocompound

Directory of Open Access Journals (Sweden)

T. Ravindra Reddy

2014-01-01

Full Text Available Synthesis of nano CuZnO2 compound is carried out by thermal decomposition method. The crystalline phase of the material is characterized by XRD. The calculated unit cell constants are a=3.1 Å and c=3.4786 Å and are of tetragonal structure. The unit cell constants are different from wurtzite (hexagonal which indicate that a nanocompound is formed. Further TEM images reveal that the metal ion is in tetragonal structure with oxygen ligands. The prepared CuZnO2 is then characterized for crystallite size analysis by employing transmission electron microscopy (TEM. The size is found to be 100 nm. Uniform bright rings are noticed in the TEM picture suggesting that the nanocrystals have preferential instead of random orientations. The selected-area electron diffraction (SAED pattern clearly indicates the formation of CuO-ZnO nanocompound. The nature of bonding is studied by electron paramagnetic resonance (EPR. The covalency character is about 0.74 and thus the compound is electrically less conductive. Optical absorption spectral studies suggest that Cu(II is placed in tetragonal elongation crystal field. The spin-orbit coupling constant, λ, is calculated using the EPR and optical absorption spectral results suggest some covalent bond between metal and ligand. Near infrared (NIR spectra are due to hydroxyl and water fundamentals.

Free standing CuO-MnO2 nanocomposite for room temperature ammonia sensing

Science.gov (United States)

Bhuvaneshwari, S.; Papachan, Seethal; Gopalakrishnan, N.

2017-05-01

CuO nanostructures and CuO-MnO2 nanocomposite were successfully synthesized using hydrothermal method without any aid of growth controlling agents. The synthesized CuO nanostructures have monoclinic structure. The XRD pattern of CuO-MnO2 observed with mixed phases of monoclinic CuO and birnessite-type MnO2 which confirms the formation of nanocomposite. SEM images revealed the turmeric-like morphology for CuO and intercalated sheets with flowers on the surface for CuO-MnO2. The length and breadth of turmeric-like structure is about 642.2 nm and 141.8 nm, respectively. The band gap of 1.72 eV for CuO nanostructure and 1.9 eV for CuO-MnO2 nanocomposite were observed from the absorption spectra. The free standing devices of CuO-MnO2 showed nearly a 3 fold increase sensing response to ammonia at room temperature when compared to the constituent CuO. The composite sensor showed response time of 120 s and recovered within 600 s. This enhanced response can be asserted to the peculiar morphology of the composite that provides more adsorption site for gas diffusion to take place.

Origin of the Enhanced Visible-Light Absorption in N-Doped Bulk Anatase TiO 2 from First-Principles Calculations

KAUST Repository

Harb, Moussab

2011-10-06

Extension of the absorption properties of TiO2 photocatalytic materials to the visible part of the solar spectrum is of major importance for energy and cleaning up applications. We carry out a systematic study of the N-doped anatase TiO2 material using spin-polarized density functional theory (DFT) and the range-separated hybrid HSE06 functional. The thermodynamic stability of competitive N-doped TiO2 structural configurations is studied as a function of the oxygen chemical potential and of various chemical doping agents: N2, (N2 + H2), NH3, N2H4. We show that the diamagnetic TiO (2-3x)N2x system corresponding to a separated substitutional N species (with 2-4% N impurities) and formation of one-half concentration of O vacancies (1-2 atom %) is an optimal configuration thermodynamically favored by NH3, N2H4, and (N2 + H2) chemical doping agents presenting a dual nitrating-reducing character. The simulated UV-vis absorption spectra using the perturbation theory (DFPT) approach demonstrates unambiguously that the diamagnetic TiO(2-3x)N2x system exhibits the enhanced optical absorption in N-doped TiO2 under visible-light irradiation. Electronic analysis further reveals a band gap narrowing of 0.6 eV induced by delocalized impurity states located at the top of the valence band of TiO 2. A fruitful comparison with experimental data is furnished. © 2011 American Chemical Society.

The Vaporization of B2O3(l) to B2O3(g) and B2O2(g)

Science.gov (United States)

Jacobson, Nathan S.; Myers, Dwight L.

2011-01-01

The vaporization of B2O3 in a reducing environment leads to formation of both B2O3(g) and B2O2(g). While formation of B2O3(g) is well understood, many questions about the formation of B2O2(g) remain. Previous studies using B(s) + B2O3(l) have led to inconsistent thermodynamic data. In this study, it was found that after heating, B(s) and B2O3(l) appear to separate and variations in contact area likely led to the inconsistent vapor pressures of B2O2(g). To circumvent this problem, an activity of boron is fixed with a two-phase mixture of FeB and Fe2B. Both second and third law enthalpies of formation were measured for B2O2(g) and B2O3(g). From these the enthalpies of formation at 298.15 K are calculated to be -479.9 +/- 41.5 kJ/mol for B2O2(g) and -833.4 +/- 13.1 kJ/mol for B2O3(g). Ab initio calculations to determine the enthalpies of formation of B2O2(g) and B2O3(g) were conducted using the W1BD composite method and show good agreement with the experimental values.

Optical Properties of the Fresnoite Ba2TiSi2O8 Single Crystal

Directory of Open Access Journals (Sweden)

Chuanying Shen

2017-02-01

Full Text Available In this work, using large-sized single crystals of high optical quality, the optical properties of Ba2TiSi2O8 were systematically investigated, including transmission spectra, refractive indices and nonlinear absorption properties. The crystal exhibits a high transmittance (>84% over a wide wavelength range from 340 to 2500 nm. The refractive indices in the range from 0.31256 to 1.01398 μm were measured, and Sellmeier’s equations were fitted by the least squares method. The nonlinear absorption properties were studied by using the open-aperture Z-scan technique, with a nonlinear absorption coefficient measured to be on the order of 0.257 cm/GW at the peak power density of 16.4 GW/cm2. Such high transmittance and wide transparency indicate that optical devices using the Ba2TiSi2O8crystal can be applied over a wide wavelength range. Furthermore, the small nonlinear absorption observed in Ba2TiSi2O8 will effectively increase the optical conversion efficiency, decreasing the generation of laser damage of the optical device.

Heterostructured ZnFe2O4/Fe2TiO5/TiO2 Composite Nanotube Arrays with an Improved Photocatalysis Degradation Efficiency Under Simulated Sunlight Irradiation

Science.gov (United States)

Xiong, Kun; Wang, Kunzhou; Chen, Lin; Wang, Xinqing; Fan, Qingbo; Courtois, Jérémie; Liu, Yuliang; Tuo, Xianguo; Yan, Minhao

2018-03-01

To improve the visible light absorption and photocatalytic activity of titanium dioxide nanotube arrays (TONTAs), ZnFe2O4 (ZFO) nanocrystals were perfused into pristine TONTA pipelines using a novel bias voltage-assisted perfusion method. ZFO nanocrystals were well anchored on the inner walls of the pristine TONTAs when the ZFO suspensions (0.025 mg mL-1) were kept under a 60 V bias voltage for 1 h. After annealing at 750 °C for 2 h, the heterostructured ZFO/Fe2TiO5 (FTO)/TiO2 composite nanotube arrays were successfully obtained. Furthermore, Fe3+ was reduced to Fe2+ when solid solution reactions occurred at the interface of ZFO and the pristine TONTAs. Introducing ZFO significantly enhanced the visible light absorption of the ZFO/FTO/TONTAs relative to that of the annealed TONTAs. The coexistence of type I and staggered type II band alignment in the ZFO/FTO/TONTAs facilitated the separation of photogenerated electrons and holes, thereby improving the efficiency of the ZFO/FTO/TONTAs for photocatalytic degradation of methylene blue when irradiated with simulated sunlight. [Figure not available: see fulltext.

Photocatalytic activity of Ti3+ self-doped dark TiO2 ultrafine nanorods, grey SiO2 nanotwin crystalline, and their composite under visible light

Science.gov (United States)

Zhang, Renhui; Yang, Yingchang; Leng, Senlin; Wang, Qing

2018-04-01

Efficient electron-holes separation is of crucial importance for the improvement of photocatalytic activity for photocatalytic reaction. In this work, dark TiO2 (D-TiO2) nanorods, grey SiO2 (G-SiO2) and D-TiO2/G-SiO2 composite with surface defects are synthesized. We report that the efficiency of photo-generated electrons and holes separation is well enhanced by introducing G-SiO2 into D-TiO2 lattice. Using first-principles method, we find that surface defects (O or Si vacancy) can be conducive to improving the optical absorption under visible-light region. Combination of the experimental results, for D-TiO2/G-SiO2 composite, the surface defects of TiO2 nanocrystallines can significantly improve the photocatalytic efficiency.

Structural Modification of Sol-Gel Synthesized V2O5 and TiO2 Thin Films with/without Erbium Doping

Directory of Open Access Journals (Sweden)

Fatma Pınar Gökdemir

2014-01-01

Full Text Available Comparative work of with/without erbium- (Er- doped vanadium pentoxide (V2O5 and titanium dioxide (TiO2 thin films were carried out via sol-gel technique by dissolving erbium (III nitrate pentahydrate (Er(NO33·5H2O in vanadium (V oxoisopropoxide (OV[OCH(CH32]3 and titanium (IV isopropoxide (Ti[OCH(CH32]4. Effect of Er doping was traced by Fourier transform IR (FTIR, thermogravimetric/differential thermal (TG/DTA, and photoluminescence measurements. UV-Vis transmission/absorption measurement indicated a blue shift upon Er doping in V2O5 film due to the softening of V=O bond while appearance of typical absorption peaks in Er-doped TiO2 film. Granule size of the films increased (reduced upon Er substitution on host material compared to undoped V2O5 and TiO2 films, respectively.

Synthesis and characterization of Zn3Ta2O8 nanomaterials by hydrothermal method

International Nuclear Information System (INIS)

Bîrdeanu, M.; Bîrdeanu, A.-V.; Gruia, A.S.; Fagadar-Cosma, E.; Avram, C.N.

2013-01-01

Graphical abstract: The results of an experimental program that was focused on obtaining the Zn 3 Ta 2 O 8 nanocrystalline synthesized by hydrothermal method using tantalum (V) oxide and zinc nitrate, the results of the nanomaterial’s structure characterization and the optical spectral properties of such nanomaterials that were thoroughly investigated. Also, the experimental results are compared with ab initio calculations of electronic properties of Zn 3 Ta 2 O 8 . Highlights: •Zn 3 Ta 2 O 8 nanomaterials were synthesized by hydrothermal method and characterized. •The obtained nanomaterials has excellent phosphor, optical and morphological properties. •The material can be used in designing high performance optoelectronical devices. -- Abstract: Zn 3 Ta 2 O 8 has been synthesized by hydrothermal method using tantalum (V) oxide and zinc nitrate. The crystal structure and microstructure, phase composition and the absorption of Zn 3 Ta 2 O 8 nanomaterials were characterized by X-ray diffraction, FT/IR measurements, UV–VIS measurements, PL measurements, SEM and AFM techniques and BET analysis. XRD results show the single phase of Zn 3 Ta 2 O 8 and the average particle size that is 52 nm. This narrow nanometer size was also confirmed by AFM measurements. BET analysis revealed that the nanomaterials are mesoporous. The PL spectra show the blue luminescence of Ta 2 Zn 3 O 8 . Besides, in the present work we report ab initio calculations regarding electronic properties of Zn 3 Ta 2 O 8 ; the theoretical results are compared with the experimental ones

Three-dimensional Ag{sub 2}O/WO{sub 3}·0.33H{sub 2}O heterostructures for improving photocatalytic activity

Energy Technology Data Exchange (ETDEWEB)

He, Xiaoyu [Department of Applied Physics, Chongqing University, Chongqing 400044 (China); Department of Physics and Electronic Engineering, Yangtze Normal University, Chongqing 408100 (China); Hu, Chenguo, E-mail: hucg@cqu.edu.cn [Department of Applied Physics, Chongqing University, Chongqing 400044 (China); Xi, Yi; Zhang, Kaiyou; Hua, Hao [Department of Applied Physics, Chongqing University, Chongqing 400044 (China)

2014-02-01

Highlights: • Ag{sub 2}O/WO{sub 3}·0.33H{sub 2}O 3D network heterostructures are prepared via a simple precipitatation method. • Ag{sub 2}O/WO{sub 3}·0.33H{sub 2}O networks exhibit much enhanced photocatalytic activity. • High photocatalytic activity is attributed to its heterostructure and 3D architectures. - Abstract: Three-dimensional Ag{sub 2}O/WO{sub 3}·0.33H{sub 2}O heterostructures were fabricated by loading Ag{sub 2}O nanoparticles on WO{sub 3}·0.33H{sub 2}O 3D networks via a simple chemical precipitation method. The Ag{sub 2}O/WO{sub 3}·0.33H{sub 2}O heterostructures exhibited much enhanced photocatalytic activity for the degradation of methylene blue (MB) under simulated solar light irradiation. The optimal molar ratio of Ag{sub 2}O and WO{sub 3}·0.33H{sub 2}O is 1:2. The outstanding photocatalytic activity of the Ag{sub 2}O/WO{sub 3}·0.33H{sub 2}O can be attributed to its large surface area of the three-dimensional networks, the enhanced sunlight absorption and the prevention of electrons–holes combination from the heterostructures. The experiment result demonstrates that wide band gap semiconductor (WO{sub 3}·0.33H{sub 2}O) modified by narrow band gap metal oxide (Ag{sub 2}O) with 3D architecture will be an effective route to enhance its photocatalytic activity.

Ultraviolet–Visible photo-response of p-Cu2O/n-ZnO heterojunction prepared on flexible (PET) substrate

International Nuclear Information System (INIS)

Elfadill, Nezar G.; Hashim, M.R.; Saron, K.M.A.; Chahrour, Khaled M.; Qaeed, M.A.; Bououdina, M.

2015-01-01

The deposition of monocrystalline ZnO nanostructures (using different concentration of reaction solution) on Cu 2 O thin film by hydrothermal method is reported. The mechanism of growing different ZnO nanostructures i.e. nanoneedles, nanotubes and nanorods are explained based on the gradient of Zn + species (resulting from precipitation) in reaction solution. The UV-VIS photo-detection properties of the three selected p-Cu 2 O/n-ZnO heterojunctions are studied by illuminated I–V characteristic and the wavelength dependent photo-responsivity properties. The spectral responsivity curves can be divided into three regions (1.9–2.17 eV), (2.2–2.9 eV) and (>3.2 eV) denoted as A, B and C. The regions A and C are assigned for band to band level absorption in Cu 2 O and ZnO respectively, while region C is associated with a combination of two absorption process: part of photons were absorbed by the band to deep level absorption in ZnO and the transmitted photons were absorbed in Cu 2 O. It is found that the heterojunctions with nanotubes exhibit higher responsivity than other nanostructures, which is mainly due to the large surface-to-volume ratio. - Highlights: • Fabrication of p-Cu 2 O/n-ZnO heterojunction on flexible PET substrate. • Synthesis of different ZnO nanostructures i.e. nanoneedles, nanotubes and nanorods. • The UV-VIS photo-detection properties of p-Cu 2 O/n-ZnO heterojunctions

The effect of TiO2 on nucleation and crystallization of a Li2O-Al2O3-SiO2 glass investigated by XANES and STEM.

Science.gov (United States)

Kleebusch, Enrico; Patzig, Christian; Krause, Michael; Hu, Yongfeng; Höche, Thomas; Rüssel, Christian

2018-02-13

Glass ceramics based on Li 2 O/Al 2 O 3 /SiO 2 are of high economic importance, as they often show very low coefficients of thermal expansion. This enables a number of challenging applications, such as cooktop panels, furnace windows or telescope mirror blanks. Usually, the crystallization of the desired LAS crystal phases within the glasses must be tailored by a careful choice of crystallization schedule and type of nucleation agents to be used. The present work describes the formation of nanocrystalline TiO 2 within an LAS base composition that contains solely TiO 2 as nucleating agent. Using a combination of scanning transmission electron microscopy as well as X-ray absorption spectroscopy, it is found that a mixture of four- and six-fold coordinated Ti 4+ ions exists already within the glass. Heating of the glass to 740 °C immediately changes this ratio towards a high content of six-fold coordinated Ti, which accumulates in liquid-liquid phase-separation droplets. During the course of thermal treatment, these droplets eventually evolve into nanocrystalline TiO 2 precipitations, in which Ti 4+ is six-fold coordinated. Thus, it is shown that the nucleation of nanocrystalline TiO 2 is initiated by a gradual re-arrangement of the Ti ions in the amorphous, glassy matrix, from a four-fold towards a six-fold coordination.

Effects of Sm3+/Yb3+ co-doping and temperature on the Raman, IR spectra and structure of [TeO2-GeO2-K2O-Sm2O3/Yb2O3] glasses

International Nuclear Information System (INIS)

Shaltout, I.; Badr, Y.

2006-01-01

Effects of Sm 3+ /Yb 3+ co-doping on Raman scattering, IR absorption, temperature dependence of the Raman spectra up to 210 o C and the structure of two glass systems of the composition (80TeO 2 -10GeO 2 -8K 2 O-2Sm 2 O 3 /Yb 2 O 3 ) is discussed. It was found that the addition of Yb 3+ to the glass very strongly enhances the intensities of the antistokes' Raman bands at 155, 375, 557 and 828 cm -1 and quenches both the intensities of the stokes' vibration modes of the TeO 4 units in the range of 120-770 cm -1 and the intensities of the OH - stretching vibration modes in the range of 2600-3300 cm -1 . Sm 2 O 3 /Yb 2 O 3 rare earth co-doping has a great influence on removing and/or changing the nature of the OH - groups. The appearance and splitting of the stretching vibration modes of the OH - groups at lower frequencies (2770, 2970 cm -1 ) for the Sm +3 singly doped glass sample, compared to the band at ∼3200 cm -1 for the Sm 3+ /Yb 3+ co-doped glass sample, suggested that the OH - groups are more strongly bonded and incorporated with the glass matrix for the singly doped glass. Heating the sample up continuously weakens the hydrogen bonding of the OH - groups to the glass matrix leading to creation of NBO and breakdown of the connectivity of the OH - groups to the TeO 4 , TeO 3+1 and TeO 3 structural units. Raman bands at 286, 477, 666 and 769 cm -1 were assigned to its respective vibrations of Te 2 O 7 , TeO 4 -4 species, the (Te-O-Te) bending vibrations of the TeO 4 triagonal bipyramids (tbps), the axial symmetric stretching vibration modes (Te ax -O) s with bridging oxygen BO atoms and to the (Te-O) nbo non-bridging stretching vibration modes of the TeO 3+1 and/or TeO 3 pyramids

Preparation and characterization of new glasses from the TeO2-CdO-Al2O3-SiO2 system

OpenAIRE

Zayas, Mª. E.; Espinoza-Beltrán, F. J.; Romero, Maximina; Rincón López, Jesús María

1998-01-01

A new family of glasses from the TeO2-CdO-Al2O3-SiO2 system obtained from CdS-TeO2 mixtures melted in fireclay crucibles have been prepared and characterized. The density values of these glasses are in the 3.30-3.46 gcm-3 range. The viscosity-temperature variation shows that glasses with high TeO2 content depict the typical variation of `short glasses' for a molding operation. Microstructural observations by TEM (replica method) and SEM microscopies have shown that these glasses contain very ...

Determination and modeling for the solubility of Na_2WO_4·2H_2O and Na_2MoO_4·2H_2O in the (Na"+ + MoO_4"2"− + WO_4"2"− + SO_4"2"− + H_2O) system

International Nuclear Information System (INIS)

Ning, Pengge; Xu, Weifeng; Cao, Hongbin; Xu, Hongbin

2016-01-01

Highlights: • The solubility of Na_2MoO_4·2H_2O and Na_2WO_4·2H_2O in Na_2MoO_4–Na_2WO_4–Na_2SO_4–H_2O were performed. • The solubility of sodium tungstate dihydrate in Na_2WO_4–Na_2SO_4–H_2O was determined. • The new model was established via regressing the published and the determined data. • The Pitzer parameter and the solubility product constant of the salt in solution were calculated. • The model was used to estimate the solubility of the sodium molybdate and sodium tungstate. - Abstract: The solubility of sodium tungstate dihydrate and sodium molybdate dihydrate in the (Na_2MoO_4 + Na_2WO_4 + Na_2SO_4 + H_2O) system was studied using experimental and calculated methods. The osmotic coefficient of sodium tungstate was fitted to calculate the thermodynamics parameters of (Na_2WO_4 + H_2O) system. The solubility of sodium tungstate dihydrate was determined using the dynamic method in Na_2WO_4–Na_2SO_4–H_2O to establish the new model which can provide an estimate the solubility of sodium tungstate dihydrate in various conditions, combined with the data published, the solubility of sodium tungstate dihydrate and the sodium molybdate dihydrate in quaternary system of (Na_2MoO_4 + Na_2WO_4 + Na_2SO_4 + H_2O) was estimated using the parameters of the two ternary systems of (Na_2WO_4 + Na_2SO_4 + H_2O) and (Na_2MoO_4 + Na_2SO_4 + H_2O). The results show that the AARD is always small and the calculated value is basically consistent with the experimental values for the system studied.

Effects of deposition rates on laser damage threshold of TiO2/SiO2 high reflectors

International Nuclear Information System (INIS)

Yao Jianke; Xu Cheng; Ma Jianyong; Fang Ming; Fan Zhengxiu; Jin Yunxia; Zhao Yuanan; He Hongbo; Shao Jianda

2009-01-01

TiO 2 single layers and TiO 2 /SiO 2 high reflectors (HR) are prepared by electron beam evaporation at different TiO 2 deposition rates. It is found that the changes of properties of TiO 2 films with the increase of rate, such as the increase of refractive index and extinction coefficient and the decrease of physical thickness, lead to the spectrum shift and reflectivity bandwidth broadening of HR together with the increase of absorption and decrease of laser-induced damage threshold. The damages are found of different morphologies: a shallow pit to a seriously delaminated and deep crater, and the different amorphous-to-anatase-to-rutile phase transition processes detected by Raman study. The frequency shift of Raman vibration mode correlates with the strain in film. Energy dispersive X-ray analysis reveals that impurities and non-stoichiometric defects are two absorption initiations resulting to the laser-induced transformation.

Fabrication of Cu2O-TiO2 Nano-composite with High Photocatalytic Performance under Simulated Solar Light

Directory of Open Access Journals (Sweden)

Yi Wentao

2016-01-01

Full Text Available Cu2O-P25 (TiO2 nano-heterostructures with different mass ratios were synthesized via a wet chemical precipitation and hydrothermal method, and were characterized by X-ray diffraction (XRD, field-emission scanning electron microscopy (FESEM, UV-vis diffuse reflectance spectra (DRS, and X-ray photoelectron spectroscopy (XPS. DRS results showed that the light absorption of P25 extended to the visible light region with the loading of Cu2O. XPS results showed that Cu existed in the state of Cu+ in the presence of hydroxylamine hydrochloride, confirming the formation of Cu2O. The obtained products exhibited efficient photocatalytic performance in degradation of methyl orange (MO and methylene blue (MB under simulated solar light. The sample of 5% Cu2O-P25 exhibited the highest photocatalytic activity among all as-prepared samples. And the photocatalysts can be recycled without obvious loss of photocatalytic activity.