Three body abrasion of laser surface alloyed aluminium AA1200

CSIR Research Space (South Africa)

Mabhali, Luyolo AB

2012-06-01

Full Text Available Laser surface alloying of aluminium AA1200 was performed with a 4 kW Nd:YAG laser to improve the abrasion wear resistance. Aluminium surfaces reinforced with metal matrix composites and intermetallic phases were achieved. The phases present depended...

Influence of energy input in friction stir welding on structure evolution and mechanical behaviour of precipitation-hardening in aluminium alloys (AA2024-T351, AA6013-T6 and Al-Mg-Sc)

Energy Technology Data Exchange (ETDEWEB)

Weis Olea, Cesar Afonso [GKSS-Forschungszentrum Geesthacht GmbH (Germany). Inst. fuer Werkstofforschung

2008-12-04

Aluminium alloys AA2024 T351, AA6013 T6 and the recently developed Al-Mg-Sc for aircraft industry applications, which are usually considered difficult to weld by conventional fusion welding processes, demonstrate outstanding performance when joined by friction stir welding (FSW). The main feature of the process is to produce solid-state welds, where the maximum temperatures attained during the process are about 80 % that of the melting temperature of the base material. The process generates substantial plastic deformation, due to the solid-state stirring, and consequently creates a high dislocation density, which is a precursor to dynamic recrystallization, a metallurgical feature that characterizes the stir zone (weld centre). A relevant aspect considered, regarding precipitation-hardening aluminium alloys, is the deterioration of the mechanical properties in the weld zones, which are fundamentally attributed to changes in the characteristics of strengthening precipitates. Among the strengthening mechanisms acting in these aluminium alloys, the most important is basically dependent on the morphology, size and population of the precipitates. The thermal cycle and deformation generated during the FSW process alter the precipitation characteristics previously present in the base material. FSW input energy regulates the magnitude of the thermal cycle and the intensity of deformation taking place during the process, and it can be controlled by the welding parameters, affecting the precipitates evolution and consequently the mechanical properties of the joint. Nevertheless, there remains a lack of knowledge about the substructural evolution of these alloys during FSW, and its correlation with weld energy input and their respective mechanical properties, particularly for the Al-Mg-Sc alloy. The main objective of this work is to explain the micro and substructural evolution (emphasizing precipitates evolution) of AA2024- T351, AA6013-T6 and Al-Mg-Sc alloys in similar

Structure-Property Relationships of Solid State Additive Manufactured Aluminum Alloy 2219 and Inconel 625

Science.gov (United States)

Rivera Almeyda, Oscar G.

in the three directions and an average grain size of 2.5 microns. EBSD PFs showed that the material has a strong torsional fiber A texture in the top of the build, and this texture gets weaker in the middle and bottom sections. TEM showed that there are no theta' precipitates in the as-deposited cross-section, therefore no precipitation strengthening should be expected. Strain rate and stress state dependence was study, and in both tension and compression, with an increase in strain rate, the YS increase and the UTS decreased. Ductile fracture surface was observed on specimens tested to failure in both QS and HR. The AFS AA2219 processing-structure-property relations are being studied in this investigation to address the stress-state and strain rate dependence of AFS AA2219 with an internal sate variable (ISV) plasticity-damage model to capture the different yield stress, work hardening and failure strain in the AFS AA2219 for high fidelity modeling of AFS components. The ISV plasticity model successfully captured the material behavior in tension, compression, tension-followed-by-compression and compression-followed-by-tension experiments. Furthermore, the damage parameters of the model were calibrated using the final void density measured from the fracture surfaces.

Effect of post weld heat treatment on tensile properties and microstructure characteristics of friction stir welded armour grade AA7075-T651 aluminium alloy

OpenAIRE

Sivaraj, P.; Kanagarajan, D.; Balasubramanian, V.

2014-01-01

This paper reports the effects of post weld heat treatments, namely artificial ageing and solution treatment followed by artificial ageing, on microstructure and mechanical properties of 12 mm thick friction stir welded joints of precipitation hardenable high strength armour grade AA7075-T651 aluminium alloy. The tensile properties, such as yield strength, tensile strength, elongation and notch tensile strength, are evaluated and correlated with the microhardness and microstructural features....

Strain hardening of aluminium alloy 3004 in the deep drawing and ironing processes

International Nuclear Information System (INIS)

Courbon, J.; Duval, J.L.

1993-01-01

The evolution of material hardening resulting from the canmaking operations on aluminium beverage cans has been investigated. Tensile tests in cup walls revealed that deep drawing induced softening in the hoop direction and hardening in the meridian direction. This anisotropy is retained in the ironing operation. Changes in strain path on a heavily cold-rolled material probably cause such a complex behaviour. To determine hardening laws for deep drawing, simple shear tests were thus performed because of the strain path similarity. They allowed to determine hardening laws over larger strains than tension could reach and revealed a saturation of stress. Altogether they proved adapted to the understanding of deep drawing. (orig.)

Investigation of Microstructure and Microhardness in Self-Reacting Friction Stir Welded AA2014-T6 and AA2219-T87

Science.gov (United States)

Horton, K. Renee; McGill, Preston; Barkey, Mark

2011-01-01

Friction stir welding (FSW) is a solid state welding process with potential advantages for aerospace and automotive industries dealing with light alloys. Self-reacting friction stir welding (SR-FSW) is one variation of the FSW process being developed at the National Aeronautics and Space Administration (NASA) for use in the fabrication of propellant tanks. This work reports on the microstructure and microhardness of SR-FSW between two dissimilar aluminum alloys. Specifically, the study examines the cross section of the weld joint formed between an AA2014-T6 plate on the advancing side and an AA2219-T87 plate on the retreating side. The microstructural analysis shows an irregularly displaced weld seam from the advancing side past the thermo-mechanical affected zone (TMAZ) into the weld nugget region. There are sharp variations in the microhardness across the weld. These variations are described in the paper and mechanisms for their formation are discussed.

Contribution to comprehensive study of aluminium alloy Aa 5083 ...

African Journals Online (AJOL)

PROMOTING ACCESS TO AFRICAN RESEARCH ... Corrosion induced by elemental mercury in aqueous media of industrial Aluminium alloys AA5083 used in heat exchanger industries of natural gas liquefaction has been studied by linear sweep voltammétry on ... EMAIL FREE FULL TEXT EMAIL FREE FULL TEXT

Experimental and numerical investigation on under-water friction stir welding of armour grade AA2519-T87 aluminium alloy

Directory of Open Access Journals (Sweden)

S. Sree Sabari

2016-08-01

Full Text Available Friction stir welding (FSW is a promising welding process that can join age hardenable aluminium alloys with high joint efficiency. However, the thermal cycles experienced by the material to be joined during FSW resulted in the deterioration of mechanical properties due to the coarsening and dissolution of strengthening precipitates in the thermo-mechanical affected zone (TMAZ and heat affected zone (HAZ. Under water friction stir welding (UWFSW is a variant of FSW process which can maintain low heat input as well as constant heat input along the weld line. The heat conduction and dissipation during UWFSW controls the width of TMAZ and HAZ and also improves the joint properties. In this investigation, an attempt has been made to evaluate the mechanical properties and microstructural characteristics of AA2519-T87 aluminium alloy joints made by FSW and UWFSW processes. Finite element analysis has been used to estimate the temperature distribution and width of TMAZ region in both the joints and the results have been compared with experimental results and subsequently correlated with mechanical properties.

Effects of quench rate and natural ageing on the age hardening behaviour of aluminium alloy AA6060

Energy Technology Data Exchange (ETDEWEB)

Strobel, Katharina, E-mail: katharina.strobel@aol.com [CAST Co-operative Research Centre, Department of Materials Engineering, Monash University, Clayton, Victoria 3800 (Australia); Lay, Matthew D.H., E-mail: mlay@fbrice.com [CSIRO Manufacturing Flagship, Clayton, Victoria 3169 (Australia); Easton, Mark A., E-mail: mark.easton@rmit.edu.au [CAST Co-operative Research Centre, Department of Materials Engineering, Monash University, Clayton, Victoria 3800 (Australia); Sweet, Lisa, E-mail: lisa.sweet@monash.edu [CAST Co-operative Research Centre, Department of Materials Engineering, Monash University, Clayton, Victoria 3800 (Australia); Zhu, Suming, E-mail: suming.zhu@rmit.edu.au [CAST Co-operative Research Centre, Department of Materials Engineering, Monash University, Clayton, Victoria 3800 (Australia); Parson, Nick C., E-mail: nick.parson@riotinto.com [Rio Tinto Alcan, Arvida Research and Development Centre, 1955, Mellon Blvd, Jonquière, Québec G7S 4K8 (Canada); Hill, Anita J., E-mail: anita.hill@csiro.au [CSIRO Manufacturing Flagship, Clayton, Victoria 3169 (Australia)

2016-01-15

Quench sensitivity in Al–Mg–Si alloys has been largely attributed to the solute loss at the heterogeneous nucleation sites, primarily dispersoids, during slow cooling after extrusion. As such, the number density of dispersoids, the solute type and concentration are considered to be the key variables for the quench sensitivity. In this study, quench sensitivity and the influence of natural ageing in a lean Al–Mg–Si alloy, AA6060, which contains few dispersoids, have been investigated by hardness measurement, thermal analysis, transmission electron microscopy (TEM) and positron annihilation lifetime spectroscopy (PALS). It is shown that the quench sensitivity in this alloy is associated with the degree of supersaturation of vacancies after cooling. Due to vacancy annihilation and clustering during natural ageing, the quench sensitivity is more pronounced after a short natural ageing time (30 min) compared to a longer natural ageing time (24 h). Therefore, prolonged natural ageing not only leads to an increase in hardness, but can also have a positive effect on the quench sensitivity of lean Al–Mg–Si alloys. - Highlights: • Significant quench sensitivity observed in AA6060 alloy after 30 min natural ageing • Prolonged natural ageing increased hardness and reduced QS. • Low dispersoid density leads to insignificant QS from non-hardening precipitates. • Vacancy supersaturation identified as a contributor to QS.

Effects of quench rate and natural ageing on the age hardening behaviour of aluminium alloy AA6060

International Nuclear Information System (INIS)

Strobel, Katharina; Lay, Matthew D.H.; Easton, Mark A.; Sweet, Lisa; Zhu, Suming; Parson, Nick C.; Hill, Anita J.

2016-01-01

Quench sensitivity in Al–Mg–Si alloys has been largely attributed to the solute loss at the heterogeneous nucleation sites, primarily dispersoids, during slow cooling after extrusion. As such, the number density of dispersoids, the solute type and concentration are considered to be the key variables for the quench sensitivity. In this study, quench sensitivity and the influence of natural ageing in a lean Al–Mg–Si alloy, AA6060, which contains few dispersoids, have been investigated by hardness measurement, thermal analysis, transmission electron microscopy (TEM) and positron annihilation lifetime spectroscopy (PALS). It is shown that the quench sensitivity in this alloy is associated with the degree of supersaturation of vacancies after cooling. Due to vacancy annihilation and clustering during natural ageing, the quench sensitivity is more pronounced after a short natural ageing time (30 min) compared to a longer natural ageing time (24 h). Therefore, prolonged natural ageing not only leads to an increase in hardness, but can also have a positive effect on the quench sensitivity of lean Al–Mg–Si alloys. - Highlights: • Significant quench sensitivity observed in AA6060 alloy after 30 min natural ageing • Prolonged natural ageing increased hardness and reduced QS. • Low dispersoid density leads to insignificant QS from non-hardening precipitates. • Vacancy supersaturation identified as a contributor to QS.

The effect of atmospheric corona treatment on AA1050 aluminium

DEFF Research Database (Denmark)

Jariyaboon, Manthana; Møller, Per; Dunin-Borkowski, Rafal E.

2010-01-01

The effect of atmospheric corona discharge on AM 050 aluminium surface was investigated using electrochemical polarization, SEM-EDX, FIB-SEM. and XPS. The corona treatment was performed with varying time (1, 5, and 15 min) in atmospheric air. A 200 nm oxide layer was generated on AA1050 after...

FIB-SEM investigation of trapped intermetallic particles in anodic oxide films on AA1050 aluminium

DEFF Research Database (Denmark)

Jariyaboon, Manthana; Møller, Per; Dunin-Borkowski, Rafal E.

2011-01-01

-containing intermetallic particles incorporated into the anodic oxide films on industrially pure aluminium (AA1050, 99.5 per cent) has been investigated. AA1050 aluminium was anodized in a 100?ml/l sulphuric acid bath with an applied voltage of 14?V at 20°C ±2°C for 10 or 120?min. The anodic film subsequently was analyzed......Purpose - The purpose of this investigation is to understand the structure of trapped intermetallics particles and localized composition changes in the anodized anodic oxide film on AA1050 aluminium substrates. Design/methodology/approach - The morphology and composition of Fe......-shaped particles were embedded in the anodic oxide film as a thin strip structure and located near the top surface of the film, whereas the round-shaped particles were trapped in the film with a spherical structure, but partially dissolved and were located throughout the thickness of the anodic film. The Fe...

Microstructural evolution and mechanical properties of oil jet peened aluminium alloy, AA6063-T6

International Nuclear Information System (INIS)

Arun Prakash, N.; Gnanamoorthy, R.; Kamaraj, M.

2010-01-01

Grain size refinement by severe surface plastic deformation is one way of improving the surface properties. This paper describes the microstructural evolution due to severe surface plastic deformation by oil jet peening in aluminium alloy, AA6063-T6. Detail characterization of the treated surfaces using X-ray diffraction analysis and transmission electron microscopy revealed the formation of submicron size grains at and near the surface. The nozzle-traveling velocity decides the peening intensity and coverage and affects the surface properties. The specimen peened at low nozzle-traveling velocity exhibited an ultrafine grain size (∼210 nm) with high surface hardness (∼0.88 GPa), compressive residual stress (-102 ± 7 MPa) and dislocation density. The hardness is high at the surface and the depth of hardened layer is ∼400 μm. Formation of high-density dislocations and associated grain refinement resulted in increased surface hardness. Presence of surface modified layer will be beneficial in improving the fatigue and tribo behavior.

Determination of aluminium in groundwater samples by GF-AAS, ICP-AES, ICP-MS and modelling of inorganic aluminium complexes.

Science.gov (United States)

Frankowski, Marcin; Zioła-Frankowska, Anetta; Kurzyca, Iwona; Novotný, Karel; Vaculovič, Tomas; Kanický, Viktor; Siepak, Marcin; Siepak, Jerzy

2011-11-01

The paper presents the results of aluminium determinations in ground water samples of the Miocene aquifer from the area of the city of Poznań (Poland). The determined aluminium content amounted from aluminium determinations were performed using three analytical techniques: graphite furnace atomic absorption spectrometry (GF-AAS), inductively coupled plasma atomic emission spectrometry (ICP-AES) and inductively coupled plasma mass spectrometry (ICP-MS). The results of aluminium determinations in groundwater samples for particular analytical techniques were compared. The results were used to identify the ascent of ground water from the Mesozoic aquifer to the Miocene aquifer in the area of the fault graben. Using the Mineql+ program, the modelling of the occurrence of aluminium and the following aluminium complexes: hydroxy, with fluorides and sulphates was performed. The paper presents the results of aluminium determinations in ground water using different analytical techniques as well as the chemical modelling in the Mineql+ program, which was performed for the first time and which enabled the identification of aluminium complexes in the investigated samples. The study confirms the occurrence of aluminium hydroxy complexes and aluminium fluoride complexes in the analysed groundwater samples. Despite the dominance of sulphates and organic matter in the sample, major participation of the complexes with these ligands was not stated based on the modelling.

Micro-mechanical modelling of ductile failure in 6005A aluminium using a physics based strain hardening larw including stage IV

DEFF Research Database (Denmark)

Simar, Aude; Nielsen, Kim Lau; de Meester, Bruno

2010-01-01

The strain hardening and damage behaviour of isothermally heat treated 6005A aluminium is investigated in order to link the thermal treatment conditions, microstructure and fracture strain. The need for a plastic flow rule involving a stage IV hardening at large strain was found essential to gene...

Grain distinct stratified nanolayers in aluminium alloys

Energy Technology Data Exchange (ETDEWEB)

Donatus, U., E-mail: uyimedonatus@yahoo.com [School of Materials, The University of Manchester, Manchester, M13 9PL, England (United Kingdom); Thompson, G.E.; Zhou, X.; Alias, J. [School of Materials, The University of Manchester, Manchester, M13 9PL, England (United Kingdom); Tsai, I.-L. [Oxford Instruments NanoAnalysis, HP12 2SE, High Wycombe (United Kingdom)

2017-02-15

The grains of aluminium alloys have stratified nanolayers which determine their mechanical and chemical responses. In this study, the nanolayers were revealed in the grains of AA6082 (T6 and T7 conditions), AA5083-O and AA2024-T3 alloys by etching the alloys in a solution comprising 20 g Cr{sub 2}O{sub 3} + 30 ml HPO{sub 3} in 1 L H{sub 2}O. Microstructural examination was conducted on selected grains of interest using scanning electron microscopy and electron backscatter diffraction technique. It was observed that the nanolayers are orientation dependent and are parallel to the {100} planes. They have ordered and repeated tunnel squares that are flawed at the sides which are aligned in the <100> directions. These flawed tunnel squares dictate the tunnelling corrosion morphology as well as appearing to have an affect on the arrangement and sizes of the precipitation hardening particles. The inclination of the stratified nanolayers, their interpacing, and the groove sizes have significant influence on the corrosion behaviour and seeming influence on the strengthening mechanism of the investigated aluminium alloys. - Highlights: • Stratified nanolayers in aluminium alloy grains. • Relationship of the stratified nanolayers with grain orientation. • Influence of the inclinations of the stratified nanolayers on corrosion. • Influence of the nanolayers interspacing and groove sizes on hardness and corrosion.

Effect of temperature on cyclic deformation behavior and residual stress relaxation of deep rolled under-aged aluminium alloy AA6110

International Nuclear Information System (INIS)

Juijerm, P.; Altenberger, I.

2007-01-01

Mechanical surface treatment (deep rolling) was performed at room temperature on the under-aged aluminium wrought alloy AA6110 (Al-Mg-Si-Cu). Afterwards, specimens were cyclically deformed at room and elevated temperatures up to 250 deg. C. The cyclic deformation behavior and s/n-curves of deep rolled under-aged AA6110 were investigated by stress-controlled fatigue tests and compared to the as-polished condition as a reference. The stability of residual stresses as well as diffraction peak broadening under high-loading and/or elevated-temperature conditions was investigated by X-ray diffraction methods before and after fatigue tests. Depth profiles of near-surface residual stresses as well as full width at half maximum (FWHM) values before and after fatigue tests at elevated temperatures are presented. Thermal residual stress relaxation of deep rolled under-aged AA6110 was investigated and analyzed by applying a Zener-Wert-Avrami function. Thermomechanical residual stress relaxation was analyzed through thermal residual stress relaxation and depth profiles of residual stresses before and after fatigue tests. Finally, an effective border line for the deep rolling treatment due to instability of near-surface work hardening was found and established in a stress amplitude-temperature diagram

Development of continuous cooling precipitation diagrams for aluminium alloys AA7150 and AA7020

Energy Technology Data Exchange (ETDEWEB)

Zhang, Y., E-mail: yong.zhang@outlook.com [ARC Centre of Excellence for Design in Light Metals, Department of Materials Engineering, Monash University, Clayton, VIC 3800 (Australia); Milkereit, B. [University of Rostock, Faculty of Mechanical Engineering and Marine Technology, Chair of Materials Science, 18051 Rostock (Germany); University of Rostock, Institute of Physics, Polymer Physics Group, 18051 Rostock (Germany); Kessler, O. [University of Rostock, Faculty of Mechanical Engineering and Marine Technology, Chair of Materials Science, 18051 Rostock (Germany); Schick, C. [University of Rostock, Institute of Physics, Polymer Physics Group, 18051 Rostock (Germany); Rometsch, P.A. [ARC Centre of Excellence for Design in Light Metals, Department of Materials Engineering, Monash University, Clayton, VIC 3800 (Australia)

2014-01-25

Highlights: • The DSC method was used for developing continuous cooling precipitation diagrams. • The quench-induced particles were observed by SEM for alloys AA7150 and AA7020. • There were more quench-induced particles in alloy AA7150. • Quench sensitivity of Al alloys can be evaluated by using the CCP diagrams. -- Abstract: Two commercial 7xxx series aluminium alloys with different solute contents and different quench-induced precipitation behaviour have been investigated by using a specialised differential scanning calorimetry (DSC) technique to record exothermal heat outputs during continuous cooling. Together with hardness testing and microstructural analysis, this DSC method was used to develop continuous cooling precipitation (CCP) diagrams for alloys AA7150 and AA7020. The results show that the total precipitation heat for each alloy decreases with increasing cooling rate. However, the excess specific heat at a given cooling rate in alloy AA7150 is much higher than that in alloy AA7020. It is evident that there are atleast three different quench-induced reactions in different temperature regimes for alloy AA7150 cooled at various linear cooling rates, but only equilibrium MgZn{sub 2} (η-phase) and Al{sub 2}CuMg (S-phase) particles were observed by scanning electron microscopy (SEM). There are at least two main precipitation peaks that can be found for alloy AA7020, which correspond to Mg{sub 2}Si and MgZn{sub 2} (η-phase). Furthermore, a method is developed to evaluate the quench sensitivity of an alloy based on a determination of the critical cooling rate. The maximum hardness values are reached at cooling rates that are faster than or similar to the critical cooling rate.

Enhancement of wear and ballistic resistance of armour grade AA7075 aluminium alloy using friction stir processing

Directory of Open Access Journals (Sweden)

I. Sudhakar

2015-03-01

Full Text Available Industrial applications of aluminium and its alloys are restricted because of their poor tribological properties. Thermal spraying, laser surfacing, electron beam welding are the most widely used techniques to alter the surface morphology of base metal. Preliminary studies reveal that the coating and layering of aluminium alloys with ceramic particles enhance the ballistic resistance. Furthermore, among aluminium alloys, 7075 aluminium alloy exhibits high strength which can be compared to that of steels and has profound applications in the designing of lightweight fortification structures and integrated protection systems. Having limitations such as poor bond integrity, formation of detrimental phases and interfacial reaction between reinforcement and substrate using fusion route to deposit hard particles paves the way to adopt friction stir processing for fabricating surface composites using different sizes of boron carbide particles as reinforcement on armour grade 7075 aluminium alloy as matrix in the present investigation. Wear and ballistic tests were carried out to assess the performance of friction stir processed AA7075 alloy. Significant improvement in wear resistance of friction stir processed surface composites is attributed to the change in wear mechanism from abrasion to adhesion. It has also been observed that the surface metal matrix composites have shown better ballistic resistance compared to the substrate AA7075 alloy. Addition of solid lubricant MoS2 has reduced the depth of penetration of the projectile to half that of base metal AA7075 alloy. For the first time, the friction stir processing technique was successfully used to improve the wear and ballistic resistances of armour grade high strength AA7075 alloy.

Surface oxide formation during corona discharge treatment of AA 1050 aluminium surfaces

DEFF Research Database (Denmark)

Minzari, Daniel; Møller, Per; Kingshott, Peter

2008-01-01

process modifies aluminium AA 1050 surface, the oxide growth and resulting corrosion properties. The corona treatment is carried out in atmospheric air. Treated surfaces are characterized using XPS, SEM/EDS, and FIB-FESEM and results suggest that an oxide layer is grown, consisting of mixture of oxide...

Process parameters-weld bead geometry interactions and their influence on mechanical properties: A case of dissimilar aluminium alloy electron beam welds

Directory of Open Access Journals (Sweden)

P. Mastanaiah

2018-04-01

Full Text Available Prediction of weld bead geometry is always an interesting and challenging research topic as it involves understanding of complex multi input and multi output system. The weld bead geometry has a profound impact on the load bearing capability of a weld joint, which in-turn decides the performance in real time service conditions. The present study introduces a novel approach of detecting a relationship between weld bead geometry and mechanical properties (e.g. tensile load for the purpose of catering the best the process could offer. The significance of the proposed approach is demonstrated by a case of dissimilar aluminium alloy (AA2219 and AA5083 electron beam welds. A mathematical model of tensile braking load as a function of geometrical attributes of weld bead geometry is presented. The results of investigation suggests the effective thickness of weld – a geometric parameter of weld bead has the most significant influence on tensile breaking load of dissimilar weld joint. The observations on bead geometry and the mechanical properties (microhardness, ultimate tensile load and face bend angle are correlated with detailed metallurgical analysis. The fusion zone of dissimilar electron beam weld has finer grain size with a moderate evaporation and segregation of alloying elements magnesium and copper respectively. The mechanical properties of weld joint are controlled by optimum bead geometry and HAZ softening in weaker AA5083 Al alloy. Keywords: Electron beam welding, AA2219, AA5083, Bead geometry, Tensile breaking load

Microstructure and age-hardening effects of aluminium alloys with additions of scandium and zirconium

Energy Technology Data Exchange (ETDEWEB)

Galun, R.; Mordike, B.L. [Inst. fuer Werkstoffkunde und Werkstofftechnik, Technische Univ. Clausthal, Clausthal-Zellerfeld (Germany); Maiwald, T.; Smola, B. [Zentrum fuer Funktionswerkstoffe GmbH, Clausthal-Zellerfeld (Germany); Mergen, R.; Manner, M.; Uitz, W. [Miba Gleitlager GmbH, Laakirchen (Australia)

2004-12-01

The aim of the work presented in this report was to produce age-hardenable aluminium alloys containing scandium and zirconium by a casting process with similar cooling conditions like an industrial casting process. Microstructure, precipitation structure and age-hardening response of different alloys with up to 0.4 wt.% Sc and Zr were investigated. Age-hardening experiments from the as-cast condition without solution annealing showed a significant increase of hardness of about 100% for Sc-rich alloys and of 50% for Zr-rich alloys compared to the as-cast condition. TEM investigations revealed the formation of precipitates of ternary Al{sub 3}(Sc{sub x}Zr{sub 1-x}) phases with a cubic cP4 crystal structure. In addition to the strengthening effect, a high thermal stability especially of the precipitates in Zr-rich alloys up to 400 C let these alloys look very promising for high-temperature applications. (orig.)

Numerical analysis of heat treatment of TiCN coated AA7075 aluminium alloy

Science.gov (United States)

Srinath, M. K.; Prasad, M. S. Ganesha

2018-04-01

The Numerical analysis of heat treatments of TiCN coated AA7075 aluminium alloys is presented in this paper. The Convection-Diffusion-Reaction (CDR) equation with solutions in the Streamlined-Upward Petrov-Galerkin (SUPG) method for different parameters is provided for the understanding of the process. An experimental process to improve the surface properties of AA-7075 aluminium alloy was attempted through the coatings of TiCN and subsequent heat treatments. From the experimental process, optimized temperature and time was obtained which gave the maximum surface hardness and corrosion resistance. The paper gives an understanding and use of the CDR equation for application of the process. Expression to determine convection, diffusion and reaction parameters are provided which is used to obtain the overall expression of the heat treatment process. With the substitution of the optimized temperature and time, the governing equation may be obtained. Additionally, the total energy consumed during the heat treatment process is also developed to give a mathematical formulation of the energy consumed.

Microstructural characterization of fly ash particulate reinforced AA6063 aluminium alloy for aerospace applications

Science.gov (United States)

Razzaq, A. M.; Majid, D. L. Abang Abdul; Ishak, M. R.; Uday, M. B.

2017-12-01

Aluminium-fly ash (FA) particulate reinforced composites (AA6063-FA) have been used in automotive and aerospace industries because of their low density and good mechanical properties. Three different weight fraction of FA: 2%, 4% and 6% are added to AA6063 alloy using compocasting method. The effect of FA particulates on microstructure, density and compression strength of AA6063- FA composites are investigated. Field Emission Scanning Electron Microscope (FESEM) micrographs reveal that the FA particulates are uniformly distributed in AA6063 alloy. The results also show that density, compression strength and microstructure of the AA6063-FA composites are significantly influenced by the FA amount. The increase in the weight fraction of FA will improve the microstructure and enhance the compression strength. The density of AA6063-FA composites decreases as the incorporation of FA increases.

Emeraldine base as corrosion protective layer on aluminium alloy AA5182, effect of the surface microstructure

DEFF Research Database (Denmark)

Cecchetto, L; Ambat, Rajan; Davenport, A.J.

2007-01-01

AA5182 aluminium alloy cold rolled samples were coated by thin Wlms of emeraldine base (EB) obtained from a 5% solution in N-methylpyrrolidinone. Accelerated corrosion tests prove this coating very eVective for corrosion protection of aluminium alloys in neutral environment. This study underlines......: • a weak redox activity of the polymer which passivate the metal, • a proton involving self-healing process taking place at the polymer–metal interface, which contributes to delay local acidiWcation in Wrst steps of corrosion on EB coated aluminium surfaces....

Microstructure and hardness performance of AA6061 aluminium composite using friction stir processing

Science.gov (United States)

Marini, C. D.; Fatchurrohman, N.

2018-04-01

Rice husk ash (RHA) is an industrial waste that has become a potential reinforced material for aluminium matrix composite (AMCs) due to low cost and abundantly available resources. Friction stir processing (FSP) has been introduced as a method to modify surface properties of the metal and alloy including theirs composite as well. The present work reports the production and characterization of AA6061 and AA6061/5 vol% RHA using FSP using parameters rotation speed 1000 rpm and traversed speed 25 mm/min. The microstructure was studied using optical microscopy (OM). A homogenous dispersion of RHA particles was obtained in the composite. No agglomeration or segregation was observed. The produced composite exhibited a fine grain structure. An improvement in hardness profile was observed as AA6061/5 vol% RHA improves in hardness compared to FSPed of AA6061 without reinforcement.

Pengaruh Rapat Arus Anodizing terhadap Nilai Kekerasan pada Plat Aluminium Paduan Aa Seri 2024-t3

OpenAIRE

Fajar Nugroho

2015-01-01

Aluminum alloy AA 2024-T3 is widely applied in the aircraft industry because it has good mechanical properties such as; light weight, good conductivity and the corrosion resistance. However Aluminium 2024-T3 susceptible to wearing. One method to improve the wear resistance o f AA 2024-T3 is the anodizing process. The aims of this research to study the effect of current density and anodizing time against the hardness of aluminum alloy AA 2024-T3. The process of anodizing was carried out using ...

TRANSIENT FINITE ELEMENT SIMULATION AND MICROSTRUCTURE EVOLUTION OF AA2219 WELD JOINT USING GAS TUNGSTEN ARC WELDING PROCESS

Directory of Open Access Journals (Sweden)

Sivaraman Arunkumar

2016-09-01

Full Text Available In this study we focus on finite element simulation of gas tungsten arc welding (GTAW of AA2219 aluminum alloy and the behavioral of the microstructure before and after weld. The simulations were performed using commercial COMSOL Multiphysics software. The thermal history of the weld region was studied by initially developed mathematical model. A sweep type meshing was used and transient analysis was performed for one welding cycle. The highest temperature noted was 3568 °C during welding. The welding operation was performed on 200×100×25 mm plates. Through metallurgical characterization, it was observed that a fair copper rich cellular (CRC network existed in the weld region. A small amount of intermetallic compounds like Al2Cu is observed through the XRD pattern.

Effects of Process Conditions on the Mechanical Behavior of Aluminium Wrought Alloy EN AW-2219 (AlCu6Mn Additively Manufactured by Laser Beam Melting in Powder Bed

Directory of Open Access Journals (Sweden)

Michael Cornelius Hermann Karg

2017-01-01

Full Text Available Additive manufacturing is especially suitable for complex-shaped 3D parts with integrated and optimized functionality realized by filigree geometries. Such designs benefit from low safety factors in mechanical layout. This demands ductile materials that reduce stress peaks by predictable plastic deformation instead of failure. Al–Cu wrought alloys are established materials meeting this requirement. Additionally, they provide high specific strengths. As the designation “Wrought Alloys” implies, they are intended for manufacturing by hot or cold working. When cast or welded, they are prone to solidification cracks. Al–Si fillers can alleviate this, but impair ductility. Being closely related to welding, Laser Beam Melting in Powder Bed (LBM of Al–Cu wrought alloys like EN AW-2219 can be considered challenging. In LBM of aluminium alloys, only easily-weldable Al–Si casting alloys have succeeded commercially today. This article discusses the influences of boundary conditions during LBM of EN AW-2219 on sample porosity and tensile test results, supported by metallographic microsections and fractography. Load direction was varied relative to LBM build-up direction. T6 heat treatment was applied to half of the samples. Pronounced anisotropy was observed. Remarkably, elongation at break of T6 specimens loaded along the build-up direction exceeded the values from literature for conventionally manufactured EN AW-2219 by a factor of two.

Precipitation hardening of cast Zr-containing A356 aluminium alloy

International Nuclear Information System (INIS)

Baradarani, B.; Raiszadeh, R.

2011-01-01

The effect of small additions of zirconium on the hardness, grain size, precipitate type and size of cast A356 aluminium alloy was investigated. The cast alloys were solution treated and then artificially aged for different periods of time. Hardness tests and scanning electron microscope (SEM), energy dispersive X-ray (EDX) and X-ray diffraction (XRD) studies were carried out on the as-cast, as-solutionised and age-hardened specimens. Incoherent, coarse Al 3 Zr particles formed in the microstructure during the solidification of the alloy and caused grain refinement in the as-cast structure. These particles dissolved and reprecipitated as smaller-size particles during the solution treatment, causing the hardness of the alloy to remain constant at high temperatures for long periods of time due to the slow diffusion of Zr in the α-Al.

Comparison of susceptibility to pitting corrosion of AA2024-T4, AA7075-T651 and AA7475-T761 aluminium alloys in neutral chloride solutions using electrochemical noise analysis

International Nuclear Information System (INIS)

Na, Kyung-Hwan; Pyun, Su-Il

2008-01-01

The susceptibility to pitting corrosion of AA2024-T4, AA7075-T651 and AA7475-T761 aluminium alloys was investigated in aqueous neutral chloride solution for the purpose of comparison using electrochemical noise measurement. The experimentally measured electrochemical noises were analysed based upon the combined stochastic theory and shot-noise theory using the Weibull distribution function. From the occurrence of two linear regions on one Weibull probability plot, it was suggested that there existed two stochastic processes of uniform corrosion and pitting corrosion; pitting corrosion was distinguished from uniform corrosion in terms of the frequency of events in the stochastic analysis. Accordingly, the present analysis method allowed us to investigate pitting corrosion independently. The susceptibility to pitting corrosion was appropriately evaluated by determining pit embryo formation rate in the stochastic analysis. The susceptibility was decreased in the following order: AA2024-T4 (the naturally aged condition), AA7475-T761 (the overaged condition) and AA7075-T651 (the near-peak-aged condition)

Nano Precipitation and Hardening of Die-Quenched 6061 Aluminum Alloy.

Science.gov (United States)

Utsunomiya, Hiroshi; Tada, Koki; Matsumoto, Ryo; Watanabe, Katsumi; Matsuda, Kenji

2018-03-01

Die quenching is applied to an age-hardenable aluminium alloys to obtain super-saturated solid solution. The application is advantageous because it can reduce number of manufacturing processes, and may increase strength by strain aging. If die quenching is realized in forging as well as sheet forming, it may widen industrial applicability further. In this study, Al-Mg-Si alloy AA6061 8 mm-thick billets were reduced 50% in height without cracks by die-quench forging. Supersaturated solid solution was successfully obtained. The die-quenched specimen shows higher hardness with nano precipitates at shorter aging time than the conventional water-quenched specimen.

Predicting tensile strength of friction stir welded AA6061 aluminium alloy joints by a mathematical model

International Nuclear Information System (INIS)

Elangovan, K.; Balasubramanian, V.; Babu, S.

2009-01-01

AA6061 aluminium alloy (Al-Mg-Si alloy) has gathered wide acceptance in the fabrication of light weight structures requiring a high strength-to weight ratio and good corrosion resistance. Compared to the fusion welding processes that are routinely used for joining structural aluminium alloys, friction stir welding (FSW) process is an emerging solid state joining process in which the material that is being welded does not melt and recast. This process uses a non-consumable tool to generate frictional heat in the abutting surfaces. The welding parameters such as tool rotational speed, welding speed, axial force etc., and tool pin profile play a major role in deciding the joint strength. An attempt has been made to develop a mathematical model to predict tensile strength of the friction stir welded AA6061 aluminium alloy by incorporating FSW process parameters. Four factors, five levels central composite design has been used to minimize number of experimental conditions. Response surface method (RSM) has been used to develop the model. Statistical tools such as analysis of variance (ANOVA), student's t-test, correlation co-efficient etc. have been used to validate the developed model. The developed mathematical model can be effectively used to predict the tensile strength of FSW joints at 95% confidence level

Effect of rotation speed and welding speed on Friction Stir Welding of AA1100 Aluminium alloy

Science.gov (United States)

Raja, P.; Bojanampati, S.; Karthikeyan, R.; Ganithi, R.

2018-04-01

Aluminum AA1100 is the most widely used grade of Aluminium due to its excellent corrosion resistance, high ductility and reflective finish, the selected material was welded with Friction Stir Welding (FSW) process on a CNC machine, using a combination of different tool rotation speed (1500 rpm, 2500 rpm, 3500 rpm) and welding speed (10 mm/min, 30 mm/min, 50 mm/min) as welding parameters. The effect of FSW using this welding parameter was studied by measuring the ultimate tensile strength of the welded joints. A high-speed steel tool was prepared for welding the Aluminium AA1100 alloy having an 8mm shoulder diameter and pin dimension of 4mm diameter and 2.8 mm length. The welded joints were tested using the universal testing machine. It was found that Ultimate Tensile Strength of FSW specimen was highest with a value of 98.08 MPa when the weld was performed at rotation speed of 1500 RPM and welding speed of 50 mm/min.

Prediction of shear and tensile strength of the diffusion bonded AA5083 and AA7075 aluminium alloy using ANN

International Nuclear Information System (INIS)

Sagai Francis Britto, A.; Raj, R. Edwin; Mabel, M. Carolin

2017-01-01

Diffusion bonding is a pressure welding technique to establish bonds by inter diffusion of atoms. Bonding characteristics were generated by varying the significant process conditions such as the bonding temperature, the pressing load and the duration of pressure while bonding the aluminium alloys AA5083 and AA7075. Deriving analytical correlation with the process variables to weld strength is quite involved due to the non-linear dependency of the process variables with the mechanical strength of the joints. An arbitrary function approximation mechanism, the artificial neural network (ANN) is therefore employed to develop the models for predicting the mechanical properties of the bonded joints. Back propagation technique, which alters the network weights to minimize the mean square error was used to develop the ANN models. The models were tested, validated and found to be satisfactory with good prediction accuracy.

Prediction of shear and tensile strength of the diffusion bonded AA5083 and AA7075 aluminium alloy using ANN

Energy Technology Data Exchange (ETDEWEB)

Sagai Francis Britto, A. [Department of Mechanical Engineering, St.Xavier' s Catholic College of Engineering, Nagercoil 629003,Tamil Nadu (India); Raj, R. Edwin, E-mail: redwinraj@gmail.com [Department of Mechanical Engineering, St.Xavier' s Catholic College of Engineering, Nagercoil 629003,Tamil Nadu (India); Mabel, M. Carolin [Department of Electrical and Electronics Engineering, St.Xavier' s Catholic College of Engineering, Nagercoil 629003,Tamil Nadu (India)

2017-04-24

Diffusion bonding is a pressure welding technique to establish bonds by inter diffusion of atoms. Bonding characteristics were generated by varying the significant process conditions such as the bonding temperature, the pressing load and the duration of pressure while bonding the aluminium alloys AA5083 and AA7075. Deriving analytical correlation with the process variables to weld strength is quite involved due to the non-linear dependency of the process variables with the mechanical strength of the joints. An arbitrary function approximation mechanism, the artificial neural network (ANN) is therefore employed to develop the models for predicting the mechanical properties of the bonded joints. Back propagation technique, which alters the network weights to minimize the mean square error was used to develop the ANN models. The models were tested, validated and found to be satisfactory with good prediction accuracy.

Aluminium Alloy AA6060 surface treatment with high temperature steam containing chemical additives

DEFF Research Database (Denmark)

Din, Rameez Ud; Tabrizian, Naja; Jellesen, Morten S.

2015-01-01

The steam treatment process was employed to produce a conversion coating on aluminium alloy AA6060. The changes in microstructure and its effect on corrosion resistance properties were investigated. Various concentrations of KMnO4 containing Ce(NO3)3 was injected into the steam and its effect...... on the formation of steam-based conversion coating was evaluated. The use of Mn-Ce into the steam resulted in incorporation of these species into the conversion coating, which resulted in improved corrosion resistance of the alloy substrate....

Metallurgical Effects of Shunting Current on Resistance Spot-Welded Joints of AA2219 Sheets

Science.gov (United States)

Jafari Vardanjani, M.; Araee, A.; Senkara, J.; Jakubowski, J.; Godek, J.

2016-08-01

Shunting effect is the loss of electrical current via the secondary circuit provided due to the existence of previous nugget in a series of welding spots. This phenomenon influences on metallurgical aspects of resistance spot-welded (RSW) joints in terms of quality and performance. In this paper RSW joints of AA2219 sheets with 1 mm thickness are investigated metallurgically for shunted and single spots. An electro-thermal finite element analysis is performed on the RSW process of shunted spot and temperature distribution and variation are obtained. These predictions are then compared with experimental micrographs. Three values of 5 mm, 20 mm, and infinite (i.e., single spot) are assumed for welding distance. Numerical and experimental results are matching each other in terms of nugget and HAZ geometry as increasing distance raised nugget size and symmetry of HAZ. In addition, important effect of shunting current on nugget thickness, microstructure, and Copper segregation on HAZ grain boundaries were discovered. A quantitative analysis is also performed about the influence of welding distance on important properties including ratio of nugget thickness and diameter ( r t), ratio of HAZ area on shunted and free side of nugget ( r HA), and ratio of equivalent segregated and total amount of Copper, measured in sample ( r Cu) on HAZ. Increasing distance from 5 mm to infinite, indicated a gain of 111.04, -45.55, and -75.15% in r t, r HA, and r Cu, respectively, while obtained ratios for 20 mm welding distance was suitable compared to single spot.

Weldability of AA 5052 H32 aluminium alloy by TIG welding and FSW process - A comparative study

Science.gov (United States)

Shanavas, S.; Raja Dhas, J. Edwin

2017-10-01

Aluminium 5xxx series alloys are the strongest non-heat treatable aluminium alloy. Its application found in automotive components and body structures due to its good formability, good strength, high corrosion resistance, and weight savings. In the present work, the influence of Tungsten Inert Gas (TIG) welding parameters on the quality of weld on AA 5052 H32 aluminium alloy plates were analyzed and the mechanical characterization of the joint so produced was compared with Friction stir (FS) welded joint. The selected input variable parameters are welding current and inert gas flow rate. Other parameters such as welding speed and arc voltage were kept constant throughout the study, based on the response from several trial runs conducted. The quality of the weld is measured in terms of ultimate tensile strength. A double side V-butt joints were fabricated by double pass on one side to ensure maximum strength of TIG welded joints. Macro and microstructural examination were conducted for both welding process.

Electron microscopy study of hardened layers structure at electrospark alloying the VT-18 titanium alloy with aluminium

International Nuclear Information System (INIS)

Pilyankevich, A.N.; Martynenko, A.N.; Verkhoturov, A.D.; Paderno, V.N.

1979-01-01

Presented are the results of metallographic, electron-microscopic, and X-ray structure analysis, of microhardness measurements and of the study of the electrode weight changes at electrospark alloying the VT-18 titanium alloy with aluminium. It is shown, that pulsating thermal and mechanical loadings in the process of electrospark alloying result in the electrode surface electroerosion, a discrete relief is being formed, which changes constantly in the process depending on the alloying time. Though with the process time the cathode weight gain increases, microareas of fracture in the hardened layer appear already at the initial stages of electrospark alloying

Heat input effect of friction stir welding on aluminium alloy AA 6061-T6 welded joint

Directory of Open Access Journals (Sweden)

Sedmak Aleksandar

2016-01-01

Full Text Available This paper deals with the heat input and maximum temperature developed during friction stir welding with different parameters. Aluminium alloy (AA 6061-T6 has been used for experimental and numerical analysis. Experimental analysis is based on temperature measurements by using infrared camera, whereas numerical analysis was based on empirical expressions and finite element method. Different types of defects have been observed in respect to different levels of heat input.

Inhibition of localized attack on the aluminium alloy AA 6351 in glycol/water solutions

Energy Technology Data Exchange (ETDEWEB)

Monticelli, C; Brunoro, G; Zucchi, F; Fagioli, F

1989-06-01

The objective of this work was to examine the feasibility of enhancing pitting resistance of AA 6351 (nominal composition: 1% Si, 0.6% Mg, 0.3% Mn, balance Al) by adding suitable inhibitors to the solutions. The compounds used were two inorganic salts: sodium molybdate and sodium tungstate and two derivatives of pyrimidine: 2-aminopyrimidine (2AP) and 2-hydroxypyrimidine (2HP). The inhibiting efficiencies of these substances were tested by both short-time electrochemical tests (galvanic coupling tests and polarization curves) and long-time immersions under experimental conditions causing the localized attack. Molybdate, tungstate and, to some extent, also 2AP efficiently inhibit AA 6351 localized corrosion in degraded solutions at 80/sup 0/C and in pure boiling solutions, for long exposure periods. The short-time electrochemical tests suggest that molybdate and tungstate are able to retard the electrochemical processes occurring on both the aluminium alloy and the small copper cathodic area produced by copper deposition. On the other hand, the 2AP efficiency is attributed to some complexing capability of this pyrimidine derivative towards dissolved copper ions, that are stabilized in solution. 2HP does not prevent AA 6351 localized attack. (orig./MM).

Characterization of AA7050 aluminium alloy processed by ECAP; Caracterizacao da liga de aluminio AA7050 processada por ECAP

Energy Technology Data Exchange (ETDEWEB)

Cardoso, K.R.; Guido, V. [Universidade do Vale do Paraiba (UNIVAP), Sao Jose dos Campos, SP (Brazil). Inst. de Pesquisa e Desenvolvimento; Travessa, D.N. [Empresa Brasileira de Aeronautica (EMBRAER), Sao Jose dos Campos, SP (Brazil); Jorge Junior, A.M. [Universidade Federal de Sao Carlos (DEMa/UFSCar), SP (Brazil). Dept. de Engenharia de Materiais

2010-07-01

The commercial AA7050 aluminium alloy in the solution heat treated condition (W) was processed by ECAP through route A. Two pressing temperatures (room and 150 deg C and velocities (5 and 30mm/min) were used, as well as different number of passes. The effect of such variables on the microstructure evolution was evaluated using optical and transmission electron microscopy with EDX microanalysis, and xray diffraction. It was found that the microstructure has been refined by ECAP, as a result of subgrains formed within deformation bands. ECAP at 150 deg C resulted in intense precipitation of plate like {eta} phase, which evolves to equiaxial morphology as the number of passes increases. (author)

The role of silicon in the corrosion of AA6061 aluminium alloy laser weldments

Energy Technology Data Exchange (ETDEWEB)

Rahman, A.B.M. Mujibur; Kumar, Sunil [Ian Wark Research Institute, University of South Australia, Mawson Lakes Campus, Mawson Lakes, SA 5095 (Australia); Gerson, Andrea R. [Applied Centre for Structural and Synchrotron Studies, University of South Australia, Mawson Lakes Campus, Mawson Lakes, SA 5095 (Australia)], E-mail: Andrea.Gerson@unisa.edu.au

2010-06-15

The galvanic corrosion temporal increase observed on examination of the weld fusion zone (WFZ) of AA6061 laser weldments in 3.5 wt.% NaCl solution cannot be attributed to electron tunnelling as the surface oxide layer is too thick, or the presence of Cl{sup -} within the surface layer as this element was not found to be present. Aluminium alloy and WFZ galvanic and surface analyses indicate that the cathodic WFZ corrosion characteristics are due to increases in silicate concentrations in the surface oxide layer, leading to increased ionic and/or p-type semi-conductor conductivity, intermetallic concentrations and surface area.

The role of silicon in the corrosion of AA6061 aluminium alloy laser weldments

International Nuclear Information System (INIS)

Rahman, A.B.M. Mujibur; Kumar, Sunil; Gerson, Andrea R.

2010-01-01

The galvanic corrosion temporal increase observed on examination of the weld fusion zone (WFZ) of AA6061 laser weldments in 3.5 wt.% NaCl solution cannot be attributed to electron tunnelling as the surface oxide layer is too thick, or the presence of Cl - within the surface layer as this element was not found to be present. Aluminium alloy and WFZ galvanic and surface analyses indicate that the cathodic WFZ corrosion characteristics are due to increases in silicate concentrations in the surface oxide layer, leading to increased ionic and/or p-type semi-conductor conductivity, intermetallic concentrations and surface area.

Experimental and theoretical investigation on corrosion inhibition of AA5052 aluminium alloy by L-cysteine in alkaline solution

International Nuclear Information System (INIS)

Wang, Dapeng; Gao, Lixin; Zhang, Daquan; Yang, Dong; Wang, Hongxia; Lin, Tong

2016-01-01

The corrosion inhibition of L-cysteine on AA5052 aluminium alloy in 4 mol/L NaOH solution was investigated by hydrogen gas evolution experiment, polarisation curve, galvanostatic discharge, electrochemical impedance spectroscopy measurements and quantum chemical calculations. The adsorption of L-cysteine on aluminium alloy surface obeyed the amended Langmuir's adsorption isotherm. The polarisation curves indicated that L-cysteine acted as a cathodic inhibitor to inhibit cathodic reaction. The inhibition mechanism was dominated by the geometric covering effect. The galvanostatic discharge shows that the additives restrain the hydrogen evolution and increase the anodic utilization rate. Quantum chemical calculations indicated that L-cysteine molecules mainly interacted with on the carboxyl groups on the aluminium alloy surface. A strong hybridization occurred between the s-orbital and p-orbital of reactive sites in the L-cysteine molecule and the sp-orbital of Aluminium. - Highlights: • L-cysteine was used as corrosion inhibitor for Al alloy in alkaline solution. • Adsorption of L-cysteine on Al alloy surface obeyed the amended Langmuir's isotherm. • L-cysteine molecules interacted with the carboxyl groups on the Al alloy surface. • A strong orbital hybridization occurred between the reactive sites in L-cysteine and Al.

Experimental and numerical investigation on under-water friction stir welding of armour grade AA2519-T87 aluminium alloy

OpenAIRE

Sree Sabari, S.; Malarvizhi, S.; Balasubramanian, V.; Madusudhan Reddy, G.

2016-01-01

Friction stir welding (FSW) is a promising welding process that can join age hardenable aluminium alloys with high joint efficiency. However, the thermal cycles experienced by the material to be joined during FSW resulted in the deterioration of mechanical properties due to the coarsening and dissolution of strengthening precipitates in the thermo-mechanical affected zone (TMAZ) and heat affected zone (HAZ). Under water friction stir welding (UWFSW) is a variant of FSW process which can maint...

Sintered aluminium powders

International Nuclear Information System (INIS)

Stepanova, M.G.; Matveev, B.I.

1974-01-01

The mechanical and physical properties of aluminium powder alloys and the various methods employed to produce them are considered. Data are given on the hardening of the alloys SAP and SPAK-4, as well as the powder-alloy system Al-Cr-Zr. (L.M.)

Constitutive behavior of as-cast AA1050, AA3104, and AA5182

Science.gov (United States)

van Haaften, W. M.; Magnin, B.; Kool, W. H.; Katgerman, L.

2002-07-01

Recent thermomechanical modeling to calculate the stress field in industrially direct-chill (DC) cast-aluminum slabs has been successful, but lack of material data limits the accuracy of these calculations. Therefore, the constitutive behavior of three aluminum alloys (AA1050, AA3104, and AA5182) was determined in the as-cast condition using tensile tests at low strain rates and from room temperature to solidus temperature. The parameters of two constitutive equations, the extended Ludwik equation and a combination of the Sellars-Tegart equation with a hardening law, were determined. In order to study the effect of recovery, the constitutive behavior after prestraining at higher temperatures was also investigated. To evaluate the quantified constitutive equations, tensile tests were performed simulating the deformation and cooling history experienced by the material during casting. It is concluded that both constitutive equations perform well, but the combined hardening-Sellars-Tegart (HST) equation has temperature-independent parameters, which makes it easier to implement in a DC casting model. Further, the deformation history of the ingot should be taken into account for accurate stress calculations.

Experimental and theoretical investigation on corrosion inhibition of AA5052 aluminium alloy by L-cysteine in alkaline solution

Energy Technology Data Exchange (ETDEWEB)

Wang, Dapeng; Gao, Lixin [School of Environmental and Chemical Engineering, Shanghai University of Electric Power, Shanghai 200090 (China); Zhang, Daquan, E-mail: zhangdaquan@shiep.edu.cn [School of Environmental and Chemical Engineering, Shanghai University of Electric Power, Shanghai 200090 (China); Yang, Dong [School of Environmental and Chemical Engineering, Shanghai University of Electric Power, Shanghai 200090 (China); Wang, Hongxia; Lin, Tong [Institute for Frontier Materials, Deakin University, Geelong, VIC 3216 (Australia)

2016-02-01

The corrosion inhibition of L-cysteine on AA5052 aluminium alloy in 4 mol/L NaOH solution was investigated by hydrogen gas evolution experiment, polarisation curve, galvanostatic discharge, electrochemical impedance spectroscopy measurements and quantum chemical calculations. The adsorption of L-cysteine on aluminium alloy surface obeyed the amended Langmuir's adsorption isotherm. The polarisation curves indicated that L-cysteine acted as a cathodic inhibitor to inhibit cathodic reaction. The inhibition mechanism was dominated by the geometric covering effect. The galvanostatic discharge shows that the additives restrain the hydrogen evolution and increase the anodic utilization rate. Quantum chemical calculations indicated that L-cysteine molecules mainly interacted with on the carboxyl groups on the aluminium alloy surface. A strong hybridization occurred between the s-orbital and p-orbital of reactive sites in the L-cysteine molecule and the sp-orbital of Aluminium. - Highlights: • L-cysteine was used as corrosion inhibitor for Al alloy in alkaline solution. • Adsorption of L-cysteine on Al alloy surface obeyed the amended Langmuir's isotherm. • L-cysteine molecules interacted with the carboxyl groups on the Al alloy surface. • A strong orbital hybridization occurred between the reactive sites in L-cysteine and Al.

IEC 61267: Feasibility of type 1100 aluminium and a copper/aluminium combination for RQA beam qualities.

Science.gov (United States)

Leong, David L; Rainford, Louise; Zhao, Wei; Brennan, Patrick C

2016-01-01

In the course of performance acceptance testing, benchmarking or quality control of X-ray imaging systems, it is sometimes necessary to harden the X-ray beam spectrum. IEC 61267 specifies materials and methods to accomplish beam hardening and, unfortunately, requires the use of 99.9% pure aluminium (Alloy 1190) for the RQA beam quality, which is expensive and difficult to obtain. Less expensive and more readily available filters, such as Alloy 1100 (99.0% pure) aluminium and copper/aluminium combinations, have been used clinically to produce RQA series without rigorous scientific investigation to support their use. In this paper, simulation and experimental methods are developed to determine the differences in beam quality using Alloy 1190 and Alloy 1100. Additional simulation investigated copper/aluminium combinations to produce RQA5 and outputs from this simulation are verified with laboratory tests using different filter samples. The results of the study demonstrate that although Alloy 1100 produces a harder beam spectrum compared to Alloy 1190, it is a reasonable substitute. A combination filter of 0.5 mm copper and 2 mm aluminium produced a spectrum closer to that of Alloy 1190 than Alloy 1100 with the added benefits of lower exposures and lower batch variability. Copyright © 2015 Associazione Italiana di Fisica Medica. Published by Elsevier Ltd. All rights reserved.

Galvanic corrosion of laser weldments of AA6061 aluminium alloy

International Nuclear Information System (INIS)

Rahman, A.B.M. Mujibur; Kumar, S.; Gerson, A.R.

2007-01-01

Galvanic corrosion of laser welded AA6061 aluminium alloy, arising from the varying rest potentials of the various weldment regions, was examined. The weld fusion zone is found to be the most cathodic region of the weldment while the base material is the most anodic region. The rate of galvanic corrosion, controlled by the cathodic process at the weld fusion zone, increases with time until a steady state maximum is reached. On galvanic corrosion the corrosion potential of the weld fusion zone shifts in the positive direction and the free corrosion current increases. It is proposed that the cathodic process at the weld fusion zone causes a local increase in pH that in turn causes dissolution of the surface film resulting in the loss of Al to solution and the increase of intermetallic phases. The increase in galvanic corrosion may result from either the build up of the intermetallic phases in the surface layer and/or significant increase in surface area of the weld fusion zone due to the porous nature of the surface layer

Dissimilar friction stir welds in AA5083-AA6082: The effect of process parameters on residual stress

International Nuclear Information System (INIS)

Steuwer, A.; Peel, M.J.; Withers, P.J.

2006-01-01

The effect of tool traverse and rotation speeds on the residual stresses are quantified for welds between non-age-hardening AA5083 and age-hardening AA6082 and compared to single alloy joints made from each of the two constituents. The residual stresses have been characterised non-destructively by neutron diffraction and synchrotron X-ray diffraction. The region around the weld line was characterised by significant tensile residual stress fields which are balanced by compressive stresses in the parent material. The rotation speed of the tool has been found to have a substantially greater influence than the transverse speed on the properties and residual stresses in the welds, particularly on the AA5083 side where the location of the peak stress moves from the stir zone to beyond the edge of the tool shoulder. The changes in residual stress are related to microstructural and hardness changes as determined in a previous study . In particular the larger stresses under the weld tool on the AA5083 side compared to the AA6082 side are related to a transient reduction in yield stress due to dissolution of the hardening precipitates during welding prior to natural aging after welding

Recovery in aluminium

DEFF Research Database (Denmark)

Gundlach, Carsten

2006-01-01

In the present thesis the development of a unique experimental method for volume characterisation of individual embedded crystallites down to a radius of 150 nm is presented. This method is applied to in-situ studies of recovery in aluminium. The method is an extension of 3DXRD microscopy, an X...... are represented as strings. To identify the strings a combination of a 5D connected component type algorithm and multi-peak fitting was found to be superior. The first use of the method was a study of recovery of a deformed aluminium alloy (AA1050). The aluminium alloy was deformed by cold rolling to a thickness...

Effect of aluminizing on hardenability of steel (S45C)

Science.gov (United States)

Prayitno, D.; Sugiarto, R.

2018-01-01

The objective of research is to know the effect of aluminizing on hardenability of steel (S45C). The research methodologies were as follows. The Steels (S45C) were machined into the Jominy test samples. Next the samples were preheating at 700 ° C for 30 minutes and then the samples were dipped into the molten of aluminium for 3 minutes as a hot dip aluminizng method. The aluminium molten was 700 ° C. Then the samples were cooled into room temperatures. Finally the samples were into the jominy tested. The results show that the aluminizing (include the preheating process) increases the hardenability of steel (S45C).

Modelling of heterogeneous clustering in aluminium

International Nuclear Information System (INIS)

Smith, A.E.; Bourgeois, L.; Nie, J.-F.; Muddle, B.C.

2003-01-01

Full text: Ab initio modelling of heterogeneous clustering in aluminium has been carried out in order to study the precipitation hardening of alloys. This process is based on the addition of small amounts of solute element to the pure metal. With increasing computational power, atomic scale effects can now be better simulated to determine the nature of the hardening mechanism. Comparisons are made between results obtained from two computational packages. These are the Linear Augmented Plane Wave WEEN2K and the plane wave pseudopotential density functional theory package fhi98md. The study of the optimal geometry of very small size clusters inside aluminium has begun with the testing of initial convergence conditions by determination of binding energies for a variety of super cell sizes of the aluminium host crystal. These are compared with total energy calculations for small size precipitates of copper and transition metals of fixed geometry. Such local optimal determinations are seen as precursors to full Monte Carlo calculations of the notional best local geometry for larger precipitates

Study of localized corrosion in AA2024 aluminium alloy using electron tomography

International Nuclear Information System (INIS)

Zhou, X.; Luo, C.; Hashimoto, T.; Hughes, A.E.; Thompson, G.E.

2012-01-01

Highlights: ► SEM tomography of localized corrosion has been achieved. ► Nanotomography provides evidence that links microstructure and corrosion propagation path. ► IGC stemmed from localized corrosion associated with buried clusters of intermetallics. ► IGC started beneath the alloy surface and may emerge on the alloy surface. - Abstract: SEM based tomography of localized corrosion has been achieved using selective detection of backscattered electrons. The high resolution tomography provides direct evidence that links the surface appearance of corroded alloy, the alloy microstructure and the corrosion propagation path. Stable localized corrosion of AA2024-T351 aluminium alloy was initiated at locations where large clusters of S phase particles were buried beneath the surface. Propagating away from the initiation sites, corrosion developed preferentially along the grain boundary network. The grain boundary attack started beneath the alloy surface, proceeded along preferred grain boundaries and may emerge at the alloy surface.

Mechanical properties of aluminium–copper–lithium alloy AA2195 at cryogenic temperatures

International Nuclear Information System (INIS)

Nayan, Niraj; Narayana Murty, S.V.S.; Jha, Abhay K.; Pant, Bhanu; Sharma, S.C.; George, Koshy M.; Sastry, G.V.S.

2014-01-01

Highlights: • 4 mm thick sheet of AA2195 was imparted T87 temper. • 7% cold work to impart T87 was given by combination of cold rolling and stretching. • Mechanical properties were evaluated at RT and cryogenic temperatures. • Strength of AA2195 are superior to the conventional aluminum alloy 2219 at all temperatures. • Strength decreases with decrease in temperature whereas ductility remains unchanged. - Abstract: Tensile testing was performed on a 4 mm thick sheet of the aluminum–lithium alloy AA2195 in T87 (solution treatment + water quenching + 7% cold work + peak aging) temper which was subjected to 7% cold working by combination of cold rolling and stretching, over a temperature range from ambient to liquid hydrogen (20 K) conditions. Properties were evaluated in longitudinal as well as transverse directions to characterize anisotropy with respect to strength and ductility. Strength and ductility were compared to the conventional aluminum alloy AA2219-T87, developed for similar cryogenic applications. Decreases in test temperature led to higher strengths with little or no change in ductility. As the temperature decreases, the differences between ultimate tensile strength as well as yield strength for two different combinations of cold roll and stretch studied in the present work, narrows down and become equal at 20 K

Hydrogen generation from aluminium corrosion in reactor containment spray solutions

International Nuclear Information System (INIS)

Frid, W.; Karlberg, G.; Sundvall, S.B.

1982-01-01

The aluminium corrosion experiments in reactor containment spray solutions, under the conditions expected to prevail during LOCA in BWR and PWR, were performed in order to investigate relationships between temperature, pH and hydrogen production rates. In order to simulate the conditions in a BWR containment realistic ratios between aluminium surface and water volume and between aluminium surface and oxygen volume were used. Three different aluminium alloys were exposed to spray solutions: AA 1050, AA 5052 and AA 6082. The corrosion rates were measured for BWR solutions (deaerated and aerated) with pH 5 and 9 at 50, 100 and 150 0 C. The pressure was constantly 0.8 MPa. The hydrogen production rate was measured by means of gas chromatography. In deionized BWR water the corrosion rates did not exceed about 0.05 mm/year in all cases, i.e. were practically independent of temperature and pH. Hydrogen concentrations were less than 0.1 vol.% in cooled dry gas. Corrosion rates and hydrogen production in PWR alkaline solution measured at pH 9.7 and 150 0 C were very high. AA 5052 alloy was the best material

Rapidly solidified aluminium for optical applications

NARCIS (Netherlands)

Gubbels, G.P.H.; Venrooy, B.W.H. van; Bosch, A.J.; Senden, R.

2008-01-01

This paper present the results of a diamond turning study of a rapidly solidified aluminium 6061 alloy grade, known as RSA6061. It is shown that this small grain material can be diamond turned to smaller roughness values than standard AA6061 aluminium grades. Also, the results are nearly as good as

Friction conditions in the bearing area of an aluminium extrusion process

NARCIS (Netherlands)

Ma, X.; de Rooij, Matthias B.; Schipper, Dirk J.

2012-01-01

In aluminium extrusion processes, friction inside the bearing channel is important for controlling the surface quality of the extrusion products. The contact materials show a large hardness difference, one being hot aluminium, and the other being hardened tool steel. Further, the contact pressure is

Cold forming of aluminium - State of the art

DEFF Research Database (Denmark)

Bay, Niels

1997-01-01

The ongoing development of cold forging technology has been manifested lately by the increasing application of components in cold forged aluminium alloys. Applying precipitation hardening alloys components with great strength/weight ratio can be produced with a strength comparable...... to that of unalloyed steel. After description of the different types of alloys and their individual properties and applications, the special requirements for tool design by cold forging in aluminium is discussed. Finally, a large number of industrial examples on cold forged aluminium components are presented. (C) 1997...

Influences of pulsed current tungsten inert gas welding parameters on the tensile properties of AA 6061 aluminium alloy

International Nuclear Information System (INIS)

Senthil Kumar, T.; Balasubramanian, V.; Sanavullah, M.Y.

2007-01-01

Medium strength aluminium alloy (Al-Mg-Si alloy) has gathered wide acceptance in the fabrication of light weight structures requiring a high strength-to-weight ratio, such as transportable bridge girders, military vehicles, road tankers and railway transport systems. In any structural application of this alloy consideration its weldability is of utmost importance as welding is largely used for joining of structural components. The preferred welding process of aluminium alloy is frequently tungsten inert gas (TIG) welding due to its comparatively easier applicability and better economy. In the case of single pass TIG welding of thinner section of this alloy, the pulsed current has been found beneficial due to its advantages over the conventional continuous current process. The use of pulsed current parameters has been found to improve the mechanical properties of the welds compared to those of continuous current welds of this alloy due to grain refinement occurring in the fusion zone. Many considerations come into the picture and one need to carefully balance various pulse current parameters to arrive at an optimum combination. Hence, in this investigation an attempt has been made to study the influence of pulsed current TIG welding parameters on tensile properties of AA 6061 aluminium alloy weldments

Synergism between cerium nitrate and sodium dodecylbenzenesulfonate on corrosion of AA5052 aluminium alloy in 3 wt.% NaCl solution

Energy Technology Data Exchange (ETDEWEB)

Liu, Jie; Wang, Dapeng; Gao, Lixin; Zhang, Daquan, E-mail: zhdq@sh163.net

2016-12-15

Highlights: • Effectively prevent corrosion of AA5052 alloy by using the mixture of cerium nitrate and sodium dodecylbenzenesulfonate. • Synergistic mechanism of the combination of cerium nitrate and sodium dodecylbenzenesulfonate. • Structure of the complex formed between cerium ions and dodecylbenzenesulfonate. • The optimal adsorption model of dodecylbenzenesulfonate on the Al{sub 2}O{sub 3} and CeO{sub 2} surface. - Abstract: The synergistic inhibition effect of rare earth cerium nitrate and sodium dodecylbenzenesulfonate (DBS) on corrosion of AA5052 aluminium alloy in 3 wt.% NaCl solution was investigated by electrochemical impedance spectroscopy (EIS), potentiodynamic polarization curve, scanning electron microscope (SEM) and Fourier transform infrared spectroscopy (FT-IR). The results show that the single cerium nitrate or DBS has a limited inhibition effect against corrosion of AA5052 alloy. The combination cerium ions with DBS produced strong synergistic effect on corrosion inhibition for AA5052 alloy and rendered a negaitve shift of the corrosion potential. The formation of the complex of Al(DBS){sub 3} and Ce(DBS){sub 3} stabilized the passive film of Al{sub 2}O{sub 3} and CeO{sub 2}, retarding both the cathodic and anodic processes of AA5052 alloy corrosion reaction significantly.

Modelling Dynamic Behaviour and Spall Failure of Aluminium Alloy AA7010

Science.gov (United States)

Ma'at, N.; Nor, M. K. Mohd; Ismail, A. E.; Kamarudin, K. A.; Jamian, S.; Ibrahim, M. N.; Awang, M. K.

2017-10-01

A finite strain constitutive model to predict the dynamic deformation behaviour of Aluminium Alloy 7010 including shockwaves and spall failure is developed in this work. The important feature of this newly hyperelastic-plastic constitutive formulation is a new Mandel stress tensor formulated using new generalized orthotropic pressure. This tensor is combined with a shock equation of state (EOS) and Grady spall failure. The Hill’s yield criterion is adopted to characterize plastic orthotropy by means of the evolving structural tensors that is defined in the isoclinic configuration. This material model was developed and integration into elastic and plastic parts. The elastic anisotropy is taken into account through the newly stress tensor decomposition of a generalized orthotropic pressure. Plastic anisotropy is considered through yield surface and an isotropic hardening defined in a unique alignment of deviatoric plane within the stress space. To test its ability to describe shockwave propagation and spall failure, the new material model was implemented into the LLNL-DYNA3D code of UTHM’s. The capability of this newly constitutive model were compared against published experimental data of Plate Impact Test at 234m/s, 450m/s and 895m/s impact velocities. A good agreement is obtained between experimental and simulation in each test.

Reinforcement with alumina particles at the interface region of AA6101-T6 and AA1350 alloys during friction stir welding

Science.gov (United States)

Ashok Kumar, R.; Thansekhar, M. R.

2018-04-01

This paper deals the combinational effect of friction stir welding and friction stir processing on dissimilar AA6101-T6 and AA1350 aluminium alloys. For that, alumina particles are reinforced at interface region of AA6101-T6 and AA1350 aluminium alloys. Friction Stir Welding and Friction Stir Processing are done simultaneously for various sizes of groove. To analyze the welding quality and surface modifications, mechanical, wear and microstructural tests are carried out. Among these, smallest groove of 0.5 mm width and 1 mm depth reveals highest tensile and bending strengths and largest groove of 2 mm width and 3 mm depth gives maximum hardness and wear resistance. Taguchi technique shows that groove width is most influencing parameter. Developed second order models with interaction predict the responses with minimum error.

Study of Dissimilar Welding AA6061 Aluminium Alloy and AZ31B Magnesium Alloy with ER5356 Filler Using Friction Stir Welding

Science.gov (United States)

Mahamud, M. I. I.; Ishak, M.; Halil, A. M.

2017-09-01

This paper is to study of dissimilar welding AA6061 aluminium alloy and AZ31B magnesium alloy with ER5356 filler using friction stir welding. 2 mm thick plates of aluminium and magnesium were used. Friction stir welding operations were performed at different rotation and travel speeds and used the fixed tilt angle which is 3°. The rotation speeds varied from 800 to 1100 rpm, and the travel speed varied from 80 to 100 mm/min. In the range rotation speed of 800 to 1000 rpm and welding speed of 80 to 100 mm/min there are no defect at the weld. Tensile test show the higher tensile strength is 198 MPa and the welding efficiency is about 76%.

Influence of friction stir welding process and tool parameters on strength properties of AA7075-T6 aluminium alloy joints

International Nuclear Information System (INIS)

Rajakumar, S.; Muralidharan, C.; Balasubramanian, V.

2011-01-01

The aircraft aluminium alloys generally present low weldability by traditional fusion welding process. The development of the friction stir welding has provided an alternative improved way of satisfactorily producing aluminium joints, in a faster and reliable manner. In this present work, the influence of process and tool parameters on tensile strength properties of AA7075-T 6 joints produced by friction stir welding was analysed. Square butt joints were fabricated by varying process parameters and tool parameters. Strength properties of the joints were evaluated and correlated with the microstructure, microhardness of weld nugget. From this investigation it is found that the joint fabricated at a tool rotational speed of 1400 rpm, welding speed of 60 mm/min, axial force of 8 kN, using the tool with 15 mm shoulder diameter, 5 mm pin diameter, 45 HRc tool hardness yielded higher strength properties compared to other joints.

Electrochemical profiling of multi-clad aluminium sheets used in automotive heat exchangers

DEFF Research Database (Denmark)

Bordo, Kirill; C. Gudla, Visweswara; Peguet, Lionel

2018-01-01

A combination of glow discharge optical emission spectroscopy sputtering and local electrochemical measurements was used to determine electrochemical changes upon brazing in a multi-layered Aluminium sheet (AA4343/AA3xxx/AA4343) with an additional low-Cu (AA3xxx) interlayer. Ecorr values from pot...

Determination of initial stages of recrystallization in aluminium alloys by X-ray diffraction

International Nuclear Information System (INIS)

Loew, Marjorie

2000-01-01

Aluminium is a metal with a wide variety of application, such as beer cans, pans, door and window borders, and others more advanced, such as airplane structure, car engines, nuclear reactors components, rocket propulsion components and so on. Most of aluminium application is in alloy form. Such alloys must present suitable mechanical and chemical properties that are obtained, not entirely, by microstructure development. In this work, the beginning of recrystallization processes of AA1050 and AA3003 aluminium alloys were studied using X-ray diffraction techniques, transmission electron microscopy and hardness test. For such a sample, an initial heat treatment was done in order to homogenize the samples microstructure, followed by cold rolling and submitted again to a heat treatment in different temperatures in a hot furnace. After that samples were analyzed to verify the beginning of the recrystallization. Vickers hardness test revealed that the beginning of recrystallization is between 150 and 300 deg C for 1050 aluminium alloy and 200 and 300 deg C for 3003 aluminium alloy. X-ray diffraction using transmission chamber showed that the beginning of recrystallization is 240 and 260 deg C for AA1050 and AA3003, respectively. These temperatures were determined as the diffraction patterns recorded in the photographic plates changes when the recrystallization takes place. In this way, the deformed sample shows continuous concentric lines and the beginning of recrystallization is characterized by the occurrence of defined spots in this pattern. The Pole Figures goniometric method revealed that the beginning of recrystallization takes place between 250 and 300 deg C for both alloys. In the same way, orientation distribution functions showed the same temperature range for the recrystallization. However, the analysis by α and β fiber figures, the recrystallization temperatures are 240 and 260 deg C for AA1050 and AA3003, respectively. Finally, after the analysis of all

The effect of tensioning and sectioning on residual stresses in aluminium AA7749 friction stir welds

International Nuclear Information System (INIS)

Altenkirch, J.; Steuwer, A.; Peel, M.; Richards, D.G.; Withers, P.J.

2008-01-01

Using synchrotron X-ray diffraction the residual stress distribution has been measured in a series of AA7449-W51 aluminium friction stir welds that had been tensioned to different loads during welding. By modifying the stress accumulation path, the application of a tensioning stress has reduced the tensile magnitude of the final residual weld stresses. In the present case the residual stresses were minimised when the applied load is ∼35% of the room temperature yield stress of the parent material. Subsequent sectioning of the weld into shorter test lengths, as might be necessary for weld testing, resulted in a progressive and significant relaxation of the residual stress field. The effect of tensioning on the weld component distortion also has been investigated

Effects of ageing time on the mechanical and conductivity properties for various round bar diameters of AA 2219 Al alloy

Directory of Open Access Journals (Sweden)

T. Ram Prabhu

2017-02-01

Full Text Available In the present study, AA 2219 alloys of 120 mm round bar are forged into various round bars (25, 50, 75 mm and subjected to T6 temper heat treatment to identify the peak ageing time for various round bars. The electrical conductivity of the round bars is also measured and correlated with the mechanical properties. It is found that the peak ageing time is 23 h and does not vary up to 75 mm round bar. It increases to 25 h for the 120 mm round bar. The yield and tensile strength of the alloy are found to be in the range of 288–304 MPa and 410–428 MPa for the peak ageing condition. The hardness and conductivity vary in the range of 121–128 BHN and 30–30.96% IACS respectively for the peak ageing condition. Although a near linear relation is found to exist between the strength/hardness and the electrical conductivity values for the selected heat treatment parameters (solution temperature: 535 °C, ageing temperature: 191 °C and the peak ageing time: 23 h, the slope of the curve is different for different round bars. Microstructure characterization studies show the precipitate coarsening with increasing ageing time. Further, precipitate segregation is not found in the microstructure for any cases of round bar diameter and ageing time combinations.

Fracture mechanisms of aluminium alloy AA7075-T651 under various loading conditions

International Nuclear Information System (INIS)

Pedersen, Ketill O.; Borvik, Tore; Hopperstad, Odd Sture

2011-01-01

The fracture behaviour of the aluminium alloy AA7075-T651 is investigated for quasi-static and dynamic loading conditions and different stress states. The fracture surfaces obtained in tensile tests on smooth and notched axisymmetric specimens and compression tests on cylindrical specimens are compared to the fracture surfaces that occur when a projectile, having either a blunt or an ogival nose shape, strikes a 20 mm thick plate of the aluminium alloy. The stress state in the impact tests is much more complex and the strain rate significantly higher than in the tensile and compression tests. Optical and scanning electron microscopes are used in the investigation. The fracture surface obtained in tests with smooth axisymmetric specimens indicates that the crack growth is partly intergranular along the grain boundaries or precipitation free zones and partly transgranular by void formation around fine and coarse intermetallic particles. When the stress triaxiality is increased through the introduction of a notch in the tensile specimen, delamination along the grain boundaries in the rolling plane is observed perpendicular to the primary crack. In through-thickness compression tests, the crack propagates within an intense shear band that has orientation about 45 o with respect to the load axis. The primary failure modes of the target plate during impact were adiabatic shear banding when struck by a blunt projectile and ductile hole-enlargement when struck by an ogival projectile. Delamination and fragmentation of the plates occurred for both loading cases, but was stronger for the ogival projectile. The delamination in the rolling plane was attributed to intergranular fracture caused by tensile stresses occurring during the penetration event.

Effect of strengthening mechanisms on cold workability and instantaneous strain hardening behavior during grain refinement of AA 6061-10 wt.% TiO2 composite prepared by mechanical alloying

International Nuclear Information System (INIS)

Sivasankaran, S.; Sivaprasad, K.; Narayanasamy, R.; Iyer, Vijay Kumar

2010-01-01

Research highlights: → Various strengthening mechanisms such as solid solution, grain size, precipitate, dislocation and dispersion strengthening promoted yield strength of the composites → The 5 h sintered composite yielded a large plastic strain (23%) at ambient temperature. → The domination of interparticle friction effects, grain size and dislocation strengthening diminished the deformation capacity of the composites greater than 5 h of milling. → Ultra-fine grained composite (40 h) yielded a high strength (>1000 MPa). → The proposed instantaneous new Poisson's ratio and the instantaneous strain hardening index used to study the extent of plastic zone and strain levels of the composite. - Abstract: The mechanical alloying (MA) of AA 6061 alloy reinforced with 10 wt.% fine anatase-titania composites powder milled with different timings (1, 5, 10, 20, 30, and 40 h) was cold consolidated and sintered. The main purpose of this study is to investigate the effect of microstructure and the various strengthening mechanisms such as solid solution, grain size, precipitate, dislocation and dispersion strengthening during grain refinement of AA 6061-10 wt.% TiO 2 composite via MA on cold working and strain hardening behavior. The sintered composite preforms were characterized by X-ray diffraction, scanning electron microscope, and transmission electron microscope. The strengthening mechanisms were estimated by using simplified models available in the literatures. The evaluation of cold deformation behavior under triaxial stress condition through room temperature cold-upsetting tests (incremental loads) was studied by correlating the strengthening mechanisms. Among the developed strengthening mechanisms the grain size and dislocation strengthening mechanisms diminished the deformation capacity of the composites. The strain hardening behavior was also examined by proposing instantaneous strain hardening index (n i ). The value of maximum instantaneous strain

Effect of Cutting Parameters on Thrust Force and Surface Roughness in Drilling of Al-2219/B4C/Gr Metal Matrix Composites

Science.gov (United States)

Ravindranath, V. M.; Basavarajappa, G. S. Shiva Shankar S.; Suresh, R.

2016-09-01

In aluminium matrix composites, reinforcement of hard ceramic particle present inside the matrix which causes tool wear, high cutting forces and poor surface finish during machining. This paper focuses on effect of cutting parameters on thrust force, surface roughness and burr height during drilling of MMCs. In the present work, discuss the influence of spindle speed and feed rate on drilling the pure base alloy (Al-2219), mono composite (Al- 2219+8% B4C) and hybrid composite (Al-2219+8%B4C+3%Gr). The composites were fabricated using liquid metallurgy route. The drilling experiments were conducted by CNC machine with TiN coated HSS tool, M42 (Cobalt grade) and carbide tools at various spindle speeds and feed rates. The thrust force, surface roughness and burr height of the drilled hole were investigated in mono composite and hybrid composite containing graphite particles, the experimental results show that the feed rate has more influence on thrust force and surface roughness. Lesser thrust force and discontinuous chips were produced during machining of hybrid composites when compared with mono and base alloy during drilling process. It is due to solid lubricant property of graphite which reduces the lesser thrust force, burr height and lower surface roughness. When machining with Carbide tool at low feed and high speeds good surface finish was obtained compared to other two types of cutting tool materials.

Appearance of anodised aluminium: Effect of alloy composition and prior surface finish

DEFF Research Database (Denmark)

Aggerbeck, Martin; Canulescu, Stela; Dirscherl, Kai

2014-01-01

Effect of alloy composition and prior surface finish on the optical appearance of the anodised layer on aluminium alloys was investigated. Four commercial alloys namely AA1050, Peraluman 706, AA5754, and AA6082 were used for the investigation. Microstructure and surface morphology of the substrat...

Crashworthiness of Aluminium Tubes; Part 1: Hydroforming at Different Corner-Fill Radii and End Feeding Levels

International Nuclear Information System (INIS)

D'Amours, Guillaume; Rahem, Ahmed; Williams, Bruce; Worswick, Michael; Mayer, Robert

2007-01-01

The automotive industry, with an increasing demand to reduce vehicle weight through the adoption of lightweight materials, requires a search of efficient methods that suit these materials. One attractive concept is to use hydroforming of aluminium tubes. By using FE simulations, the process can be optimized to reduce the risk for failure while maintaining energy absorption and component integrity under crash conditions. It is important to capture the level of residual ductility after forming to allow proper design for crashworthiness. This paper presents numerical and experimental studies that have been carried out for high pressure hydroforming operations to study the influence of the tube corner radius, end feeding, material thinning, and work hardening in 76.2 mm diameter, 3 mm wall thickness AA5754 aluminium alloy tube. End feeding was used to increase the formability of the tubes. The influence of the end feed displacement versus tube forming pressure schedule was studied to optimize the forming process operation to reduce thinning. Validation of the numerical simulations was performed by comparison of the predicted strain distributions and thinning, with measured quantities. The effect of element formulation (thin shell versus solid elements) was also considered in the models

Crashworthiness of Aluminium Tubes; Part 1: Hydroforming at Different Corner-Fill Radii and End Feeding Levels

Science.gov (United States)

D'Amours, Guillaume; Rahem, Ahmed; Williams, Bruce; Worswick, Michael; Mayer, Robert

2007-05-01

The automotive industry, with an increasing demand to reduce vehicle weight through the adoption of lightweight materials, requires a search of efficient methods that suit these materials. One attractive concept is to use hydroforming of aluminium tubes. By using FE simulations, the process can be optimized to reduce the risk for failure while maintaining energy absorption and component integrity under crash conditions. It is important to capture the level of residual ductility after forming to allow proper design for crashworthiness. This paper presents numerical and experimental studies that have been carried out for high pressure hydroforming operations to study the influence of the tube corner radius, end feeding, material thinning, and work hardening in 76.2 mm diameter, 3 mm wall thickness AA5754 aluminium alloy tube. End feeding was used to increase the formability of the tubes. The influence of the end feed displacement versus tube forming pressure schedule was studied to optimize the forming process operation to reduce thinning. Validation of the numerical simulations was performed by comparison of the predicted strain distributions and thinning, with measured quantities. The effect of element formulation (thin shell versus solid elements) was also considered in the models.

Role of work hardening characteristics of matrix alloys in the ...

Indian Academy of Sciences (India)

Unknown

with increasing prismatic punching of dislocations in the order 7075, 2014, 7010, 2024, 6061 and commercial purity aluminium leading to increased strength increments is noted. Keywords. Metal matrix composites; strengthening; work hardening rate; dislocation density. 1. Introduction. While in continuous fibre composites, ...

Modelling and Pareto optimization of mechanical properties of friction stir welded AA7075/AA5083 butt joints using neural network and particle swarm algorithm

International Nuclear Information System (INIS)

Shojaeefard, Mohammad Hasan; Behnagh, Reza Abdi; Akbari, Mostafa; Givi, Mohammad Kazem Besharati; Farhani, Foad

2013-01-01

Highlights: ► Defect-free friction stir welds have been produced for AA5083-O/AA7075-O. ► Back-propagation was sufficient for predicting hardness and tensile strength. ► A hybrid multi-objective algorithm is proposed to deal with this MOP. ► Multi-objective particle swarm optimization was used to find the Pareto solutions. ► TOPSIS is used to rank the given alternatives of the Pareto solutions. -- Abstract: Friction Stir Welding (FSW) has been successfully used to weld similar and dissimilar cast and wrought aluminium alloys, especially for aircraft aluminium alloys, that generally present with low weldability by the traditional fusion welding process. This paper focuses on the microstructural and mechanical properties of the Friction Stir Welding (FSW) of AA7075-O to AA5083-O aluminium alloys. Weld microstructures, hardness and tensile properties were evaluated in as-welded condition. Tensile tests indicated that mechanical properties of the joint were better than in the base metals. An Artificial Neural Network (ANN) model was developed to simulate the correlation between the Friction Stir Welding parameters and mechanical properties. Performance of the ANN model was excellent and the model was employed to predict the ultimate tensile strength and hardness of butt joint of AA7075–AA5083 as functions of weld and rotational speeds. The multi-objective particle swarm optimization was used to obtain the Pareto-optimal set. Finally, the Technique for Order Preference by Similarity to the Ideal Solution (TOPSIS) was applied to determine the best compromised solution.

Fatigue crack growth rate behaviour of friction-stir aluminium alloy AA2024-T3 welds under transient thermal tensioning

International Nuclear Information System (INIS)

Ilman, M.N.; Kusmono,; Iswanto, P.T.

2013-01-01

Highlights: • FSW enables unweldable aircraft material AA2024-T3 to be welded without cracking. • FSW applied to aircraft structure is required to have superior fatigue resistance. • Transient thermal tensioning (TTT) is being developed for stress relieving in FSW. • The fatigue crack growth rates of FSW joints under TTT are studied. - Abstract: Friction stir welding (FSW) has become a serious candidate technology to join metallic fuselage panels for the next generation of civil aircrafts. However, residual stress introduced during welding which subsequently affects fatigue performance is still a major problem that needs to be paid attention. The present investigation aims to improve fatigue crack growth resistance of friction stir aluminium alloy AA2024-T3 welds using transient thermal tensioning (TTT) treatment. In this investigation, aluminium alloy AA2024-T3 plates were joined using FSW process with and without TTT. The welding parameters used including tool rotation speed (Rt) and the plate travelling speed (v) were 1450 rpm and 30 mm/min respectively. The TTT treatments were carried out by heating both sides of friction stir weld line using moving electric heaters ahead of, beside and behind the tool at a heating temperature of 200 °C. Subsequently, a sequence of tests was carried out including microstructural examination, hardness measurement, tensile test and fatigue crack growth rate (FCGR) test in combination with fractography using scanning electron microscopy (SEM). The FCGR test was carried out using a constant amplitude fatigue experiment with stress ratio (R) of 0.1 and frequency (f) of 11 Hz whereas specimens used were centre-crack tension (CCT) type with the initial crack located at the weld nugget. Results of this investigation showed that at low ΔK, typically below 9 MPa m 0.5 , the friction stir welds under TTT treatments lowered fatigue crack growth rate (da/dN) and the lowest (da/dN) was achieved as the heaters were located ahead of

Laser beam welding of high strength aluminium-lithium alloys; Laserstrahlschweissen von hochfesten Aluminium-Lithium Legierungen

Energy Technology Data Exchange (ETDEWEB)

Enz, Josephin

2012-07-01

The present development in aircraft industry determined by the demand for a higher cost-effectiveness. Laser beam welding is one of the most promising joining technologies for the application in the aircraft industry through the considerable reduction of the production costs. Furthermore the weight of an aircraft structure can be reduced by the use of light and high strength aluminium alloys. This paper deals with the development of a process for the laser beam welding of a skin-stringer-joint where the Al-Li-alloy AA2196 is used as stringer material and the Al-Li-alloy AA2198 is used as skin and stringer material. By the use of design of experiments the optimal welding process parameters for different material combinations were determined which will be used for the welding of a 5-stringer panel. Therefore the weld seams of the joints were tested for irregularities and microstructural characteristics. In addition several mechanical tests were performed, which define the quality of the welded joint. Furthermore the influence of the oxide layer and the welding preparation on the welding performance was investigated. (orig.) [German] Die derzeitigen Entwicklungen im Flugzeugbau werden durch die allgemeine Forderung nach einer Steigerung der Wirtschaftlichkeit bestimmt. Das Laserstrahlschweissen ist dabei eines der vielversprechendsten Fuegeverfahren fuer die Anwendung im Flugzeugbau durch das die Herstellungskosten deutlich reduziert werden koennen. Zudem kann durch die Verwendung von leichten und hochfesten Aluminium-Legierungen das Gewicht einer Flugzeugstruktur zusaetzlich reduziert werden. Die vorliegende Arbeit befasst sich mit der Entwicklung eines Prozesses zum Laserstrahlschweissen einer Skin-Stringer-Verbindung aus den Aluminium-Lithium-Legierungen AA2196 (als Stringer-Werkstoff) und AA2198 (als Skin- und Stringer-Werkstoff). Unter Verwendung der statistischen Versuchsplanung wurden die optimalen Einstellungen der Schweissprozessparameter fuer die

Corrosion inhibition of 7000 series aluminium alloys with cerium diphenyl phosphate

Energy Technology Data Exchange (ETDEWEB)

Hill, Julie-Anne [Department of Materials Engineering and Australian Centre of Excellence for Electromaterials Science, Wellington Rd, Monash University, Clayton, Victoria (Australia); Markley, Tracey [Department of Materials Engineering and Australian Centre of Excellence for Electromaterials Science, Wellington Rd, Monash University, Clayton, Victoria (Australia); CSIRO, Division of Materials Science and Technology, Clayton, Victoria (Australia); Forsyth, Maria, E-mail: maria.forsyth@deakin.edu.au [Department of Materials Engineering and Australian Centre of Excellence for Electromaterials Science, Wellington Rd, Monash University, Clayton, Victoria (Australia); Howlett, Patrick C. [Department of Materials Engineering and Australian Centre of Excellence for Electromaterials Science, Wellington Rd, Monash University, Clayton, Victoria (Australia); Hinton, Bruce R.W. [Department of Materials Engineering and Australian Centre of Excellence for Electromaterials Science, Wellington Rd, Monash University, Clayton, Victoria (Australia); Defence Science and Technology Organisation, Melbourne, Victoria (Australia)

2011-02-03

Graphical abstract: Scanning electron micrographs of microtomed surface shows pristine surface free of corrosion related 'mud cracking' inset for an inhibited AA7050 specimen when only 150 ppm Ce(dpp)3 is present in 0.1 M NaCl solution. Display Omitted Research highlights: > The thin film of hydrolysis products of Ce(dpp)3 and aluminium oxide is proposed to cause the inhibition. > The film consists of discrete Ce rich particles and a thin film over the matrix of Ce, P and Al oxides. > Discrete deposition of Ce is specifically influenced by Cu rich intermetallics. - Abstract: Cerium diphenyl phosphate (Ce(dpp){sub 3}) has previously been shown to be a strong corrosion inhibitor for aluminium-copper magnesium alloy AA2024-T3 and AA7075 in chloride solutions. Surface characterisation including SEM and ToF-SIMS coupled with electrochemical impedance spectroscopy (EIS) measurements are used to propose a mechanism of corrosion inhibition which appears to involve the formation of a complex oxide film of aluminium and cerium also incorporating the organophosphate component. The formation of a thin complex film consisting of hydrolysis products of the Ce(dpp){sub 3} compound and aluminium oxide is proposed to lead to the observed inhibition. SEM analysis shows that some intermetallics favour the creation of thicker deposits predominantly containing cerium oxide compounds.

Magnetic horn of the Antiproton Accumulator (AA)

CERN Multimedia

Photographic Service

1988-01-01

In the 1960s, the invention of this "current sheet lens" has helped to greatly improve the flux of neutrino beams. It was used again at the AA, collecting antiprotons from the production target at angles too large to fit into the acceptance of the AA. It was machined from aluminium to a thickness of 1.4 mm and pulsed at 400 kA for 15 microseconds (half-sine).

An approach for continuous cooling transformation (CCT) diagrams of aluminium alloys

International Nuclear Information System (INIS)

Herding, T.; Kessler, O.; Hoffmann, F.; Mayr, P.

2002-01-01

Two different kinds of time temperature transformation (TTT) diagrams are known. The first one are isothermal transformation (IT) diagrams and the second one continuous cooling transformation (CCT) diagrams. These diagrams are important for the correct heat treatment of aluminium alloys, because they provide information about the required quenching rate, which is necessary to obtain a supersaturated solid solution during age hardening. Furthermore, it is possible to determine the lowest quenching rate, which permits both a high strength and a small distortion of the component after age hardening. In the literature IT diagrams for different aluminium alloys are available. To determine these diagrams, a solution annealing followed by quenching to defined temperatures is necessary. At these temperatures the alloy is kept isothermally until a transformation has started. These diagrams are not directly portable on continuous cooling, because of the different cooling paths. (orig.)

Mechanical Behaviour Investigation Of Aluminium Alloy Tailor Welded Blank Developed By Using Friction Stir Welding Technique

Science.gov (United States)

Dwi Anggono, Agus; Sugito, Bibit; Hariyanto, Agus; Subroto; Sarjito

2017-10-01

The objective on the research was to investigate the mechanical properties and microstructure of tailor welded blank (TWB) made from AA6061-T6 and AA1100 using friction stir welding (FSW) process. Due to the dissimilar mechanical properties of the two aluminium alloys, microhardness test was conducted to measure the hardness distribution across the weld nugget. The mixing of two distinct materials was influenced by tool rotation speed. Therefore, microstructure analysis was carried out to investigate the grain size and shape. The grain size of AA6061-T6 has increased in the heat affected zone (HAZ) while for AA1100 has decreased. In the weld nugget, it has found a hook defects in the dissimilar aluminium joining. By using monotonic tensile load, the different weld line direction was observed with the expansion in tool rotation. The joints failure were consistently on the area of AA1100 series. Furthermore, two specimens were investigated, one through the dissimilar aluminium and the other through similiar material. Inspection of the weld nugget hardness was shown that nonhomogen material intermixing during the stiring process as confirmed by microhardness measurement.

Inhibitory effect of konjac glucomanan on pitting corrosion of AA5052 aluminium alloy in NaCl solution.

Science.gov (United States)

Zhang, Kegui; Yang, Wenzhong; Xu, Bin; Chen, Yun; Yin, Xiaoshuang; Liu, Ying; Zuo, Huanzhen

2018-05-01

A natural carbohydrate polymer, konjac glucomanan, has been extracted from commercial product and studied as a green corrosion inhibitor for AA5052 aluminium alloy in 3.5 wt% NaCl solution by high-performance gel permeation chromatography (GPC), thermo gravimetric analysis (TGA), Fourier-transform infrared (FT-IR) spectra, electrochemical measurement and surface characterization techniques. The results of GPC measurements suggest the weight-average molecular weight and the number-average molecular weight of KGM with 98.2% purity are 1.61 × 10 5  g/mol and 1.54 × 10 5  g/mol, respectively. Potentiodynamic polarization curves show konjac glucomanan behaves as a mixed-type inhibitor with dominant anodic effect and that its maximum efficiency at 200 ppm is 94%. Electrochemical impedance spectroscopy (EIS) studies reveal the resistance of oxide film is approximately two orders of magnitude greater than the resistance of adsorbed inhibitor layer and that they both increase with KGM concentration. Moreover, in-situ electrochemical noise (EN) detection demonstrates that the growth and propagation stages of the pitting corrosion germinating on metal surface are blocked by polysaccharide additive, which is confirmed by the surface analysis of aluminium alloy using scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) and Raman spectroscopy. At last, it is found that the addition of KGM makes it harder for water droplet containing NaCl to wet the metallic substrate. Copyright © 2018 Elsevier Inc. All rights reserved.

Failure of aluminium self-piercing rivets: An experimental and numerical study

International Nuclear Information System (INIS)

Hoang, N.-H.; Hopperstad, O.S.; Langseth, M.; Westermann, I.

2013-01-01

Highlights: ► We investigated the fracture mechanism of AA7278-T6 aluminium self-piercing rivets. ► Fracture of AA 7278-T6 rivets during the riveting process is a complex phenomenon. ► Microstructure of AA7278-T6 has significant influence on the fracture mechanism. ► Increasing friction will change the deformation mode of the rivet. - Abstract: The present paper investigates the fracture mechanisms of AA7278-T6 aluminium self-piercing rivets under compression during the riveting process. First, a microstructure investigation was conducted to disclose the grain structure and the particle distribution of the extruded aluminium alloy. Transmission electron micrographs revealed precipitate free zones along grain boundaries. Uniaxial tensile tests in three different directions with respect to the extrusion direction revealed anisotropy of the alloy in strength and ductility and a change in fracture mode with tensile direction. The behaviour of the alloy under compression was studied experimentally using upsetting tests and self-piercing riveting tests. Micrographs of the deformed specimens provided insight into the influence of the microstructure on the deformation and fracture of the alloy under compression. Second, numerical analyses were carried out using a 2-D axisymmetric model in LS–DYNA in an attempt to investigate the role of different physical variables on the final failure of the rivet. The numerical results revealed that constituent particles, precipitate free zones, and friction between the rivet and plates are important for strain localisation and fracture in the rivet

Stress Corrosion Cracking Behavior of Multipass TIG-Welded AA2219 Aluminum Alloy in 3.5 wt pct NaCl Solution

Science.gov (United States)

Venugopal, A.; Sreekumar, K.; Raja, V. S.

2012-09-01

The stress corrosion cracking (SCC) behavior of the AA2219 aluminum alloy in the single-pass (SP) and multipass (MP) welded conditions was examined and compared with that of the base metal (BM) in 3.5 wt pct NaCl solution using a slow-strain-rate technique (SSRT). The reduction in ductility was used as a parameter to evaluate the SCC susceptibility of both the BM and welded joints. The results showed that the ductility ratio ( ɛ NaCl/( ɛ air) was 0.97 and 0.96, respectively, for the BM and MP welded joint, and the same was marginally reduced to 0.9 for the SP welded joint. The fractographic examination of the failed samples revealed a typical ductile cracking morphology for all the base and welded joints, indicating the good environmental cracking resistance of this alloy under all welded conditions. To understand the decrease in the ductility of the SP welded joint, preexposure SSRT followed by microstructural observations were made, which showed that the decrease in ductility ratio of the SP welded joint was caused by the electrochemical pitting that assisted the nucleation of cracks in the form of corrosion induced mechanical cracking rather than true SCC failure of the alloy. The microstructural examination and polarization tests demonstrated a clear grain boundary (GB) sensitization of the PMZ, resulting in severe galvanic corrosion of the SP weld joint, which initiated the necessary conditions for the localized corrosion and cracking along the PMZ. The absence of PMZ and a refined fusion zone (FZ) structure because of the lesser heat input and postweld heating effect improved the galvanic corrosion resistance of the MP welded joint greatly, and thus, failure occurred along the FZ.

The effect of laser surface melting on microstructure and corrosion behavior of friction stir welded aluminum alloy 2219

Science.gov (United States)

Ma, Shengchong; Zhao, Yong; Zou, Jiasheng; Yan, Keng; Liu, Chuan

2017-11-01

This study aimed to explore the electrochemical properties and microstructure of friction stir welds to understand the correlation between their properties and processing. Friction stir welding is a promising solid-state joining process for high-strength aluminum alloys (AA). Although friction stir welding (FSW) eliminates the problems of fusion welding due to the fact that it is performed below Tm, it causes severe plastic deformation in the material. Some AA welded by FSW exhibit relatively poor corrosion resistance. In this research, the corrosion resistance of such welds was enhanced through laser surface melting. A friction stir weld of AA 2219 was laser melted. The melt depth and microstructure were observed using optical and scanning electron microscopy. The melt zone exhibited epitaxially grown columnar grains. The redistribution of elemental composition was analyzed using energy-dispersive spectroscopy. The anticorrosion properties of both laser-melted and original welds were studied in aqueous 3.5% NaCl solution using cyclic potentiodynamic polarization. The results indicated a noticeable increase in the pitting corrosion resistance after the laser treatment on the surface. The repassivation potential was nobler than the corrosion potential after the laser treatment, confirming that the resistance to pitting growth improved.

Impact toughness of laser alloyed aluminium AA1200 alloys

CSIR Research Space (South Africa)

Mabhali, Luyolo AB

2013-08-01

Full Text Available ),. 559-563. [2] T. Tomida, K. Nakata, S. Saji, T. Kubo, T, Formation of metal matrix composite layer on aluminium alloy with TiC-Cu powder by laser surface alloying process; Surface and Coatings Technology; vol. 142-144, 2001, 585-589. [3] L. A. B...

Effect of scandium on structure and hardening of Al–Ca eutectic alloys

Energy Technology Data Exchange (ETDEWEB)

Belov, N.A., E-mail: nikolay-belov@yandex.ru [National Research and Technological University “MISIS”, 4, Leninsky pr., Moscow 119049 (Russian Federation); Naumova, E.A. [Bauman Moscow State Technical University, 5, 2 ul. Baumanskaya, Moscow, 105005 (Russian Federation); Alabin, A.N. [National Research and Technological University “MISIS”, 4, Leninsky pr., Moscow 119049 (Russian Federation); UC RUSAL, 13/1, Nikoloyamskaya st., Moscow, 109240 (Russian Federation); Matveeva, I.A. [UC RUSAL, 13/1, Nikoloyamskaya st., Moscow, 109240 (Russian Federation)

2015-10-15

The phase composition, structure and hardening of alloys in the aluminium corner of the Al–Ca–Sc system were studied in the range up to 10% Ca and up to 1% S≿. The experimental study (optical, scanning and transmission electron microscopy with electron-microprobe analysis, differential thermal analysis and hardness measurements) was combined with Thermo-Calc software simulation for the optimization of the alloy composition. It was shown that only phases of the binary systems (Al{sub 4}Ca and Al{sub 3}Sc) might be in equilibrium with the aluminium solid solution. It was shown that the (Al) + Al{sub 4}Ca eutectic had a much finer structure as compared with the Al–Si eutectic, which suggests a possibility of reaching higher mechanical properties as compared to commercial alloys of the A356 type. The influence of the annealing temperature within the range up to 600 °C on the structure and hardness of the Al–Ca–Sc experimental alloys was studied. It was determined that the maximum hardening corresponded to the annealing at 300 °C, which was due to the precipitation of Al{sub 3}Sc nanoparticles with their further coarsening. With an example of an Al-7.6% Ca-0.3% Sc model experimental alloy, a principal possibility of manufacturing aluminium casting alloys based on the (Al) + Al{sub 4}Ca eutectic was demonstrated. Unlike commercial alloys of the A356 type, the model alloy does not require quenching, as hardening particles are formed in the course of annealing of casting. - Highlights: • Al–Ca–Sc phase diagram in aluminum corner. • Formation of Al{sub 3}Sc nanoparticles in eutectic (Al) + Al{sub 4}Ca during heating at 300–450 °C. • Hardening and thermal stability of proposed (Al–Ca–Sc) and commercial (Al–Si–Mg, 356 type) eutectic alloys.

Correlation between Wavelength Dispersive X-ray Fluorescence (WDXRF) analysis of hardened concrete for chlorides vs. Atomic Absorption (AA) analysis in accordance with AASHTO T- 260; sampling and testing for chloride ion in concrete and concrete raw mater

Science.gov (United States)

2014-04-01

A correlation between Wavelength Dispersive X-ray Fluorescence(WDXRF) analysis of Hardened : Concrete for Chlorides and Atomic Absorption (AA) analysis (current method AASHTO T-260, procedure B) has been : found and a new method of analysis has been ...

Experiment-based modelling of grain boundary β-phase (Mg2Al3) evolution during sensitisation of aluminium alloy AA5083.

Science.gov (United States)

Zhang, R; Steiner, M A; Agnew, S R; Kairy, S K; Davies, C H J; Birbilis, N

2017-06-07

An empirical model for the evolution of β-phase (Mg 2 Al 3 ) along grain boundaries in aluminium alloy AA5083 (Al-Mg-Mn) during isothermal exposures is proposed herein. Developing a quantitative understanding of grain boundary precipitation is important to interpreting intergranular corrosion and stress corrosion cracking in this alloy system. To date, complete ab initio models for grain boundary precipitation based upon fundamental principles of thermodynamics and kinetics are not available, despite the critical role that such precipitates play in dictating intergranular corrosion phenomena. Empirical models can therefore serve an important role in advancing the understanding of grain boundary precipitation kinetics, which is an approach applicable beyond the present context. High resolution scanning electron microscopy was to quantify the size and distribution of β-phase precipitates on Ga-embrittled intergranular fracture surfaces of AA5083. The results are compared with the degree of sensitisation (DoS) as judged by nitric acid mass loss testing (ASTM-G67-04), and discussed with models for sensitisation in 5xxx series Al-alloys. The work herein allows sensitisation to be quantified from an unambiguous microstructural perspective.

The role of magnesium in the electrochemical behaviour of 5XXX aluminium-magnesium alloys

NARCIS (Netherlands)

Flores Ramirez, J.R.

2006-01-01

An investigation concerning the effects of magnesium on the intergranular corrosion susceptibility of AA5XXX aluminium alloys was carried out. In the present work, magnesium is found to be highly mobile in the bulk metal as well as in the aluminium oxide. This mobility is also found to be dependent

Influence of nanoporous structure on mechanical strength of aluminium and aluminium alloy adhesive structural joints

International Nuclear Information System (INIS)

Spadaro, C; Dispenza, C; Sunseri, C

2006-01-01

The influence of surface treatments on the mechanical strength of adhesive joints was investigated. The attention was focused on AA2024 alloy because it is extensively used in both the automotive and aerospace industries. Adhesive joints fabricated with pure aluminium were also investigated in order to evidence possible differences in the surface features after identical treatments. Before joining with a commercial epoxy adhesive, metal substrates were subjected to different kinds of treatment and the surfaces were characterized by SEM analysis. The formation of a microporous surface in the AA2024 alloy, upon etching and anodizing, is discussed on the basis of the role of the intermetallic particles and their electrochemical behaviour with respect to the aluminium matrix. Moreover, nanostructured porous oxide layers on both type of substrate were also formed, as a consequence of the anodizing process. Differences in their morphologies were revealed as a function of both the applied voltage and the presence of alloying elements. On this basis, an explanation of the different values of fracture energy measured by means of T-peel tests carried out on the corresponding joints was attempted

Silicon Alloying On Aluminium Based Alloy Surface

International Nuclear Information System (INIS)

Suryanto

2002-01-01

Silicon alloying on surface of aluminium based alloy was carried out using electron beam. This is performed in order to enhance tribological properties of the alloy. Silicon is considered most important alloying element in aluminium alloy, particularly for tribological components. Prior to silicon alloying. aluminium substrate were painted with binder and silicon powder and dried in a furnace. Silicon alloying were carried out in a vacuum chamber. The Silicon alloyed materials were assessed using some techniques. The results show that silicon alloying formed a composite metal-non metal system in which silicon particles are dispersed in the alloyed layer. Silicon content in the alloyed layer is about 40% while in other place is only 10.5 %. The hardness of layer changes significantly. The wear properties of the alloying alloys increase. Silicon surface alloying also reduced the coefficient of friction for sliding against a hardened steel counter face, which could otherwise be higher because of the strong adhesion of aluminium to steel. The hardness of the silicon surface alloyed material dropped when it underwent a heating cycle similar to the ion coating process. Hence, silicon alloying is not a suitable choice for use as an intermediate layer for duplex treatment

Friction-Stir Welding - Heavy Inclusions in Bi-metallic welds of Al 2219/2195

Science.gov (United States)

Rietz, Ward W., Jr.

2008-01-01

Heavy Inclusions (HI) were detected for the first time by radiographic examination in aluminum alloy 2219forging/2195plate (advancing/retreating side) Friction Sir Welds (FSW) for the Space Shuttle External Tank (ET) Program. Radiographic HI indications appear as either small (approx.0.005"-0.025") individual particles or clusters of small particles. Initial work was performed to verify that the HI was not foreign material or caused by FSW pin tool debris. That and subsequent elemental analysis determined that the HI were large agglomerations of Al2Cu (theta phase), which is the strengthening precipitate in Al2219. A literature search on that subject determined that the agglomeration of phase has also been found in Al2219 bead on plate FSW [Ref. 1]. Since this was detected in ET space flight hardware, an investigative study of the effect of agglomerated theta phase particles in FSW Al2219f/2195p was performed. Numerous panels of various lengths were welded per ET weld procedures and radiographically inspected to determine if any HI was detected. Areas that had HI were sampled for room temperature and cyclic cryogenic (-423F) tensile testing and determined no significant adverse affect on mechanical properties when compared to test specimens without HI and historical data. Fracture surface examination using the Scanning Electron Microscope (SEM) revealed smaller phase agglomerations undetectable by radiographic inspection dispersed throughout the Al2219f/2195p FSW. This indicates that phase agglomeration is inherent to the Al2219f/2195p FSW process and only rarely creates agglomerations large enough to be detected by radiography. HI has not been observed in FSW of plate to plate material for either Al2219 or AL2195.

The Effect of Interlayer Materials on the Joint Properties of Diffusion-Bonded Aluminium and Magnesium

Directory of Open Access Journals (Sweden)

Stefan Habisch

2018-02-01

Full Text Available Diffusion bonding is a well-known technology for a wide range of advanced joining applications, due to the possibility of bonding different materials within a defined temperature-time-contact pressure regime in solid state. For this study, aluminium alloys AA 6060, AA 6082, AA 7020, AA 7075 and magnesium alloy AZ 31 B are used to produce dissimilar metal joints. Titanium and silver were investigated as interlayer materials. SEM and EDXS-analysis, micro-hardness measurements and tensile testing were carried out to examine the influence of the interlayers on the diffusion zone microstructures and to characterize the joint properties. The results showed that the highest joint strength of 48 N/mm2 was reached using an aluminium alloy of the 6000 series with a titanium interlayer. For both interlayer materials, intermetallic Al-Mg compounds were still formed, but the width and the level of hardness across the diffusion zone was significantly reduced compared to Al-Mg joints without interlayer.

The influence of the surface distribution of Al6(MnFe) intermetallic on the electrochemical response of AA5083 aluminium alloy in NaCl solutions

International Nuclear Information System (INIS)

Bethencourt, M.; Botana, F.J.; Calvino, J.J.; Perez, J.; Rodriguez, M.A.; Marcos, M.

1998-01-01

In this paper the behaviour against pitting corrosion of different samples of AA5083 aluminium alloy has been studied. A correlation between the microstructure of the samples and their susceptibility to pitting has been established. Metallographic analysis combined with SEM and EDS techniques have allowed us to detect three intermetallic compounds in the samples. The particle size distribution and surface density of each intermetallic phase have been evaluated for the three AA5083 alloy samples coming from different suppliers. Significant differences in the microstructure of the three samples have been found. Full immersion test carried out in 3.5% aerated aqueous solutions showed that pitting starts at the locations of the Al 6 (MnFe) intermetallic particles. As a consequence of this, the samples with higher Al 6 (MnFe) content showed a higher pit density on its surface. The results of cyclic polarisation tests showed also a good correlation with the microstructural parameters. (orig.)

The corrosion protection of 2219-T87 aluminum by anodizing

Science.gov (United States)

Danford, M. D.

1991-01-01

Various types of anodizing coatings were studied for 2219-T87 aluminum. These include both type II and type III anodized coats which were water sealed and a newly developed and proprietary Magnaplate HCR (TM) coat. Results indicate that type II anodizing is not much superior to type II anodizing as far as corrosion protection for 2219-T87 aluminum is concerned. Magnaplate HCR (TM) coatings should provide superior corrosion protection over an extended period of time using a coating thickness of 51 microns (2.0 mils).

Effects of surface treatment of aluminium alloy 1050 on the adhesion and anticorrosion properties of the epoxy coating

Energy Technology Data Exchange (ETDEWEB)

Sharifi Golru, S., E-mail: samanesharifi@aut.ac.ir [Department of Polymer Engineering and Color Technology, Amirkabir University of Technology, P.O. Box 15875-4413 Tehran (Iran, Islamic Republic of); Attar, M.M., E-mail: attar@aut.ac.ir [Department of Polymer Engineering and Color Technology, Amirkabir University of Technology, P.O. Box 15875-4413 Tehran (Iran, Islamic Republic of); Ramezanzadeh, B. [Department of Surface Coating and Corrosion, Institute for Color Science and Technology, No. 59,Vafamanesh St, Hosainabad Sq, Lavizan, Tehran (Iran, Islamic Republic of)

2015-08-01

Highlights: • Aluminium alloy 1050 was treated by zirconium-based (Zr) conversion coating. • The surface morphology and surface free energy of the samples were obtained. • The adhesion properties of the epoxy coating was studied on the treated samples. • The corrosion resistance of the epoxy coating was enhanced on treated samples. - Abstract: The objective of this work is to investigate the effects of zirconium-based (Zr) conversion coating on the adhesion properties and corrosion resistance of an epoxy/polyamide coating applied on the aluminium alloy 1050 (AA1050). Field emission scanning electron microscope (FE-SEM), energy dispersive X-ray spectrum (EDS), atomic force microscope (AFM) and contact angle measuring device were employed in order to characterize the surface characteristics of the Zr treated AA1050 samples. The epoxy/polyamide coating was applied on the untreated and Zr treated samples. The epoxy coating adhesion to the aluminium substrate was evaluated by pull-off test before and after 30 days immersion in 3.5% w/w NaCl solution. In addition, the electrochemical impedance spectroscopy (EIS) and salt spray tests were employed to characterize the corrosion protection properties of the epoxy coating applied on the AA1050 samples. Results revealed that the surface treatment of AA1050 by zirconium conversion coating resulted in the increase of surface free energy and surface roughness. The dry and recovery (adhesion strength after 30 days immersion in the 3.5 wt% NaCl solution) adhesion strengths of the coatings applied on the Zr treated aluminium samples were greater than untreated sample. In addition, the adhesion loss of the coating applied on the Zr treated aluminium substrate was lower than other samples. Also, the results obtained from EIS and salt spray test clearly revealed that the Zr conversion coating could enhance the corrosion protective performance of the epoxy coating significantly.

Wear Resistance Increase by Friction Stir Processing for Partial Magnesium Replacement in Aluminium Alloys

Science.gov (United States)

Balos, Sebastian; Labus Zlatanovic, Danka; Janjatovic, Petar; Dramicanin, Miroslav; Rajnovic, Dragan; Sidjanin, Leposava

2018-03-01

In this paper, the influence of friction stir processing (FSP) was evaluated as a way of increasing mechanical properties and a way of replacing the magnesium content in aluminium alloys. FSP was done on AA5754 H111 aluminium alloy, containing 3 % Mg, by using various types of tools and different welding speeds, rotational speeds and tilt angles. Wear test was done against SiC abrasive papers. SiC was used to simulate extreme abrasive wear conditions. The wear test was done on untreated AA5754 specimens, processed AA5754 specimens and untreated AA5083 H111 specimens, the latter containing 4.5 % Mg. AA5083 was chosen as an alternative to AA5754, but with a significantly higher Mg content. Base material microhardness was 60 HV1 and 80 HV1 for AA5754 and AA5083 alloys respectively. To find the effect of FSP on AA5754 alloy, microstructures were studied, mainly grain size in the stir zone. It was found, that an elevated processing and rotational speed, without tilt angle and the tool without a reservoir resulted in an increase in hardness of the AA5754 to 70 HV1, but with the occurrence of tunneling defect and the wear rate of 79.3 mg. Lower FSP parameters and a tilted tool with a reservoir resulted in microhardness of 68 HV1 and wear rate of 68.2 mg without tunneling. These wear values are lower than those obtained with unmodified Al-alloys: AA5754 97.2 mg and AA5083 86.3 mg. An increased wear resistance can be attributed to the combined effect of grain boundary strengthening mechanism and solid solution strengthening, versus only the latter in untreated alloys.

Evaluation of Mechanical Properties of MWCNT / Nanoclay Reinforced Aluminium alloy Metal Matrix Composite

Science.gov (United States)

Ratna Kumar, P. S. Samuel; Robinson Smart, D. S.; Alexis, S. John

2018-04-01

Aluminium alloy 5083 (AA5083) is a widely used material in aerospace, marine, defence and structural applications were mechanical and corrosion resistance property plays a vital role. For the present work, MWCNT / Nanoclay (montmorillonite (MMT) K10) mixed with AA5083 for different composition in weight percentage to enhance the mechanical property. Semi-solid state casting method (Compo-casting) was used to fabricate the composite materials. By using Field-emission scanning electron microscope (FESEM) the uniform dispersion of the reinforcement and microstructure were studied. Finally, the addition of Nanoclay shows decrease in tensile strength compared to the AA5083 / MWCNT composites and hardness value of the composites (AA5083 / MWCNT and AA5083 / Nanoclay) was found to increase significantly.

A three-dimensional fully coupled thermo-mechanical model for Self-reacting Friction Stir Welding of Aluminium AA6061 sheets

International Nuclear Information System (INIS)

Singh, Piyush; Biswas, Pankaj; Kore, Sachin D.

2016-01-01

In the present work a three dimensional model of self-reacting friction stir welding in aluminium alloy AA6061 has been developed based on the Computational Fluid Dynamics (CFD) approach using COMSOL Multiphysics software. The temperature dependent material properties have been incorporated in the model from available literature. A slip-stick contact between the workpiece and tool surface has been considered with the slip factor varying linearly with distance. The methodology adopted has been validated with experimental results available in the literature. The temperature distribution observed has been found to be asymmetric about the weld centre line. The maximum temperature has been observed on the advancing side of the weld. However, the temperature distribution across the thickness has been found to be almost symmetric about the mid thickness plane. An hourglass shaped temperature distribution has been observed across the cross-section of the weld. The material flow velocity distribution shows that the deformation zone is limited to a very small region around the tool. (paper)

Laser surface alloying (LSA) of aluminium (AA 1200) with TiB2 for hardness improvement

CSIR Research Space (South Africa)

Popoola, AP

2010-10-01

Full Text Available The present work deals with the development of Aluminium metal matrix composite (MMC) using TiB2 reinforcement. The aim is to improve the microhardness property of the substrate. The surface of the aluminium was sand blasted to improve its laser...

Improvement of hardness of aluminium AA1200 by laser surface alloying

CSIR Research Space (South Africa)

Mabhali, Luyolo AB

2010-07-01

Full Text Available Aluminium is vastly used in industry due to its low cost, light weight and excellent workability, but lacks in wear resistance and hardness. Laser alloying is used to improve the surface properties such as hardness by modifying the composition...

Optimisation of thermo mechanical treatments using cryogenic rolling and aging of the high strength aluminium alloy AlZn5.5MgCu (AA7075)

Energy Technology Data Exchange (ETDEWEB)

Hunger, S.; Scholze, M.; Hockauf, M.; Wagner, M.F.X. [Chemnitz University of Technology, Institute of Materials Science and Engineering, Chemnitz (Germany); Fritsch, S.

2011-07-15

In this study, we consider the optimisation of mechanical properties and the microstructure of the high strength and difficult-to-work aluminium alloy AA7075 by cryogenic rolling. In order to reduce the grain size into the (ultra)fine-grained regime, cryogenic rolling is used to introduce different amount of plastic strain. We discuss how rolling at lower temperatures allows the introduction of higher strains on the one hand, and suppresses dynamic recovery and aging effectively on the other hand. Our results demonstrate that, in combination with an appropriate post-processing aging treatment, an outstanding combination of strength and ductility can be achieved. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Aluminium hydro(oxide)–based (AO) adsorbent for defluoridation of ...

African Journals Online (AJOL)

High resolution 27Al Magic Angle Spinning Nuclear Magnetic Resonance (27Al MAS NMR) spectra of AO, AA, and PB were recorded, to analyse the coordination geometry of solid Al species and the results showed that aluminium is coordinated octahedrally and tetrahedrally in all cases. Regeneration experiments showed ...

Creep Aging Behavior Characterization of 2219 Aluminum Alloy

Directory of Open Access Journals (Sweden)

Lingfeng Liu

2016-06-01

Full Text Available In order to characterize the creep behaviors of 2219 aluminum alloy at different temperatures and stress levels, a RWS-50 Electronic Creep Testing Machine (Zhuhai SUST Electrical Equipment Company, Zhuhai, China was used for creep experiment at temperatures of 353~458 k and experimental stresses of 130~170 MPa. It was discovered that this alloy displayed classical creep curve characteristics in its creep behaviors within the experimental parameters, and its creep value increased with temperature and stress. Based on the creep equation of hyperbolic sine function, regression analysis was conducted of experimental data to calculate stress exponent, creep activation energy, and other related variables, and a 2219 aluminum alloy creep constitutive equation was established. Results of further analysis of the creep mechanism of the alloy at different temperatures indicated that the creep mechanism of 2219 aluminum alloy differed at different temperatures; and creek characteristics were presented in three stages at different temperatures, i.e., the grain boundary sliding creep mechanism at a low temperature stage (T < 373 K, the dislocation glide creep mechanism at a medium temperature stage (373 K ≤ T < 418 K, and the dislocation climb creep mechanism at a high temperature stage (T ≥ 418 K. By comparative analysis of the fitting results and experiment data, they were found to be in agreement with the experimental data, revealing that the established creep constitutive equation is suitable for different temperatures and stresses.

MicroCT Bone Densitometry: Context Sensitivity, Beam Hardening Correction and the Effect of Surrounding Media

Directory of Open Access Journals (Sweden)

Philip L. Salmon

2014-12-01

Full Text Available The context-sensitivity of microCT bone densitometry due to beam hardening artefacts was assessed. Bones and teeth are scanned with varying thickness of surrounding media (water, alcohol, biological tissue and it is important to understand how this affects reconstructed attenuation (“density” of the mineralized tissue. Aluminium tubes and rods with thickness 0.127mm–5mm were scanned both in air or surrounded by up to 2cm of water. Scans were performed with different energy filters and degrees of software beam hardening correction (BHC. Also tested were the effects of signal-to-noise ratio, magnification and truncation. The thickness of an aluminium tube significantly affected its mean reconstructed attenuation. This effect of thickness could be reduced substantially by BHC for scans in air, but not for scans in water. Varying thickness of surrounding water also changed the mean attenuation of an aluminium tube. This artefact could be almost eliminated by an optimal BHC value. The “cupping” artefact of heterogeneous attenuation (elevated at outer surfaces could be corrected if aluminium was scanned in air, but in water BHC was much less effective. Scan truncation, changes to magnification and signal-to-noise ratio also caused artificial changes to measured attenuation. Measurement of bone mineral density by microCT is highly context sensitive. A surrounding layer of liquid or biological tissue reduces the ability of software BHC to remove bone density artefacts. Sample thickness, truncation, magnification and signal to noise ratio also affect reconstructed attenuation. Thus it is important for densitometry that sample and calibration phantom dimensions and mounting materials are standardised.

AA, inner conductor of a magnetic horn

CERN Multimedia

CERN PhotoLab

1981-01-01

At the start-up of the AA and during its initial operation, magnetic horns focused the antiprotons emanating from the production target. These "current-sheet lenses" had a thin inner conductor (for minimum absorption of antiprotons), machined from aluminium to wall thicknesses of 0.7 or 1 mm. The half-sine pulses rose to 150 kA in 8 microsec. The angular acceptance was 50 mrad.

Inhibitive Behaviour of Corrosion of Aluminium Alloy in NaCl by Mangrove Tannin

International Nuclear Information System (INIS)

Solhan Yahya; Afidah Abdul Rahim; Affaizza Mohd Shah; Rohana Adnan

2011-01-01

Anticorrosion potential of mangrove tannins on aluminium alloys AA6061 in NaCl solution has been studied using potentiodynamic polarisation method and scanning electron microscopy (SEM). The study was carried out in different pH of corrosive medium in the absence and presence of various concentrations of tannin. The corrosion inhibition behaviour of the mangrove tannin on AA6061 aluminium alloy corrosion was found to be dependant on the pH of NaCl solution. Our results showed that the inhibition efficiency increased with increasing tannins concentration in chloride solution at pH 6. Treatment of aluminium alloy 6061 with all concentrations of mangrove tannins reduced the current density, thus decreased the corrosion rate. Tannins behaved as mixed inhibitors at pH 6 and reduction in current density predominantly affected in cathodic reaction. Meanwhile, at pH 12, addition of tannins shifted the corrosion potential to more cathodic potentials and a passivating effect was observed in anodic potentials. SEM studies have shown that the addition of tannins in chloride solution at pH 12 reduced the surface degradation and the formation of pits. (author)

Ballistic impact velocity response of carbon fibre reinforced aluminium alloy laminates for aero-engine

Science.gov (United States)

Mohammed, I.; Abu Talib, A. R.; Sultan, M. T. H.; Saadon, S.

2017-12-01

Aerospace and other industries use fibre metal laminate composites extensively due to their high specific strength, stiffness and fire resistance, in addition to their capability to be tailored into different forms for specific purposes. The behaviours of such composites under impact loading is another factor to be considered due to the impacts that occur in take-off, landing, during maintenance and operations. The aim of the study is to determine the specific perforation energy and impact strength of the fibre metal laminates of different layering pattern of carbon fibre reinforced aluminium alloy and hybrid laminate composites of carbon fibre and natural fibres (kenaf and flax). The composites are fabricated using the hand lay-up method in a mould with high bonding polymer matrix and compressed by a compression machine, cured at room temperature for one day and post cure in an oven for three hours. The impact tests are conducted using a gun tunnel system with a flat cylindrical bullet fired using a helium gas at a distance of 14 inches to the target. Impact and residual velocity of the projectile are recorded by high speed video camera. Specific perforation energy of carbon fibre reinforced aluminium alloy (CF+AA) for both before and after fire test are higher than the specific perforation energy of the other composites considered before and after fire test respectively. CF +AA before fire test is 55.18% greater than after. The same thing applies to impact strength of the composites where CF +AA before the fire test has the highest percentage of 11.7%, 50.0% and 32.98% as respectively compared to carbon fibre reinforced aluminium alloy (CARALL), carbon fibre reinforced flax aluminium alloy (CAFRALL) and carbon fibre reinforced kenaf aluminium alloy (CAKRALL), and likewise for the composites after fire test. The considered composites in this test can be used in the designated fire zone of an aircraft engine to protect external debris from penetrating the engine

An investigation on compression strength analysis of commercial aluminium tube to aluminium 2025 tube plate by using TIG welding process

Energy Technology Data Exchange (ETDEWEB)

Kannan, S., E-mail: kannan.dgl201127@gmail.com [Department of Mechanical Engineering and Mining Machinery Engineering, Indian Institute of Technology (ISM), Dhanbad, Jharkhand, India, 826004 (India); Senthil Kumaran, S., E-mail: sskumaran@ymail.com [Research and Development Center, Department of Mechanical Engineering, RVS Educational Trust' s Group of Institutions, RVS School of Engineering and Technology, Dindigul, Tamilnadu, India, 624005 (India); Kumaraswamidhas, L.A., E-mail: lakdhas1978@gmail.com [Department of Mechanical Engineering and Mining Machinery Engineering, Indian School of Mines University, Dhanbad, Jharkhand, India, 826004 (India)

2016-05-05

In this present study, Tungsten inert gas (TIG) welding was applied to weld the dissimilar materials and authenticate the mechanical and metallurgical properties of tube to tube plate made up of commercial aluminium and Al 2025 respectively using an Zirconiated tungsten electrode along with filler material aluminium ER 2219. In total, twenty five pieces has been subjected to compression strength and hardness value to evaluate the optimal joint strength. The three optimization technique has been used in this experiment. Taguchi L{sub 25} orthogonal array is used to identify the most influencing process parameter which affects the joint strength. ANOVA method is measured for both compression strength and hardness to calculate the percentage of contribution for each process parameter. Genetic algorithm is used to validate the results obtained from the both experimental value and optimization value. The micro structural study is depicted the welding joints characterization in between tube to tube plate joints. The radiograph test is conducted to prove the welds are non-defective and no flaws are found during the welding process. The mechanical property of compression strength and hardness has been measured to obtain the optimal joint strength of the welded sample was about 174.846 MPa and 131.364 Hv respectively. - Highlights: • Commercial Al tube and Al 2025 tube plate successfully welded by TIG welding. • Compression strength and hardness value proves to obtain optimal joint strength. • The maximum compression and hardness was achieved in various input parameters.

An investigation on compression strength analysis of commercial aluminium tube to aluminium 2025 tube plate by using TIG welding process

International Nuclear Information System (INIS)

Kannan, S.; Senthil Kumaran, S.; Kumaraswamidhas, L.A.

2016-01-01

In this present study, Tungsten inert gas (TIG) welding was applied to weld the dissimilar materials and authenticate the mechanical and metallurgical properties of tube to tube plate made up of commercial aluminium and Al 2025 respectively using an Zirconiated tungsten electrode along with filler material aluminium ER 2219. In total, twenty five pieces has been subjected to compression strength and hardness value to evaluate the optimal joint strength. The three optimization technique has been used in this experiment. Taguchi L_2_5 orthogonal array is used to identify the most influencing process parameter which affects the joint strength. ANOVA method is measured for both compression strength and hardness to calculate the percentage of contribution for each process parameter. Genetic algorithm is used to validate the results obtained from the both experimental value and optimization value. The micro structural study is depicted the welding joints characterization in between tube to tube plate joints. The radiograph test is conducted to prove the welds are non-defective and no flaws are found during the welding process. The mechanical property of compression strength and hardness has been measured to obtain the optimal joint strength of the welded sample was about 174.846 MPa and 131.364 Hv respectively. - Highlights: • Commercial Al tube and Al 2025 tube plate successfully welded by TIG welding. • Compression strength and hardness value proves to obtain optimal joint strength. • The maximum compression and hardness was achieved in various input parameters.

The strain path dependence of plastic deformation response of AA5754: Experiment and modeling

International Nuclear Information System (INIS)

Pham, Minh-Son; Hu, Lin; Iadicola, Mark; Creuziger, Adam; Rollett, Anthony D.

2013-01-01

This work presents modeling of experiments on a balanced biaxial (BB) pre-strained AA5754 alloy, subsequently reloaded uniaxially along the rolling direction and transverse direction. The material exhibits a complex plastic deformation response during the change in strain path due to 1) crystallographic texture, 2) aging (interactions between dislocations and Mg atoms) and 3) recovery (annihilation and re-arrangement of dislocations). With a BB prestrain of about 5 %, the aging process is dominant, and the yield strength for uniaxially deformed samples is observed to be higher than the flow stress during BB straining. The strain hardening rate after changing path is, however, lower than that for pre-straining. Higher degrees of pre-straining make the dynamic recovery more active. The dynamic recovery at higher strain levels compensates for the aging effect, and results in: 1) a reduction of the yield strength, and 2) an increase in the hardening rate of re-strained specimens along other directions. The yield strength of deformed samples is further reduced if these samples are left at room temperature to let static recovery occur. The synergistic influences of texture condition, aging and recovery processes on the material response make the modeling of strain path dependence of mechanical behavior of AA5754 challenging. In this study, the influence of crystallographic texture is taken into account by incorporating the latent hardening into a visco-plastic self-consistent model. Different strengths of dislocation glide interaction models in 24 slip systems are used to represent the latent hardening. Moreover, the aging and recovery effects are also included into the latent hardening model by considering strong interactions between dislocations and dissolved atom Mg and the microstructural evolution. These microstructural considerations provide a powerful capability to successfully describe the strain path dependence of plastic deformation behavior of AA5754

INVESTIGATION OF SINGLE-PASS/DOUBLE-PASS TECHNIQUES ON FRICTION STIR WELDING OF ALUMINIUM

Directory of Open Access Journals (Sweden)

N.A.A. Sathari

2014-12-01

Full Text Available The aim of this research is to study the effects of single-pass/ double-pass techniques on friction stir welding of aluminium. Two pieces of AA1100 with a thickness of 6.0 mm were friction stir welded using a CNC milling machine at rotational speeds of 1400 rpm, 1600 rpm and 1800 rpm respectively for single-pass and double-pass. Microstructure observations of the welded area were studied using an optical microscope. The specimens were tested by using a tensile test and Vickers hardness test to evaluate their mechanical properties. The results indicated that, at low rotational speed, defects such as ‘surface lack of fill’ and tunnels in the welded area contributed to a decrease in mechanical properties. Welded specimens using double-pass techniques show increasing values of tensile strength and hardness. From this investigation it is found that the best parameters of FSW welded aluminium AA1100 plate were those using double-pass techniques that produce mechanically sound joints with a hardness of 56.38 HV and 108 MPa strength at 1800 rpm compared to the single-pass technique. Friction stir welding, single-pass/ double-pass techniques, AA1100, microstructure, mechanical properties.

Influence of the Aluminium Alloy Type on Defects Formation in Friction Stir Lap Welding of Thin Sheets

Directory of Open Access Journals (Sweden)

M. I. Costa

Full Text Available Abstract The weldability in Friction Stir Lap Welding (FSLW of heat and non-heat treatable aluminium alloys, the AA6082-T6 and the AA5754-H22 aluminium alloys, respectively, are compared. For both alloys, welds were produced in very thin sheets, using the same welding parameters and procedures, and strong differences in welds morphology were found. The strength of the welds was evaluated by performing tensile-shear tests under monotonic and cyclic loading conditions. As-welded and heat-treated samples of the AA6082- T6 were tested. It was found that the heat-treatable alloy is more sensitive to defects formation, in lap welding, than the non-heat-treatable alloy. The presence of defects has a strong influence on the monotonic and fatigue behaviour of the welds. In spite of this, for very high-applied stresses, the heat-treatable alloy welds perform better in fatigue than the non-heat-treatable alloy welds.

Microstructure, mechanical properties and texture of an AA6061/AA5754 composite fabricated by cross accumulative roll bonding

Energy Technology Data Exchange (ETDEWEB)

Verstraete, K., E-mail: kevin.verstraete@u-psud.fr [Université Paris-Sud, SP2M, ICMMO, UMR CNRS 8182, 91405 Orsay Cedex (France); Helbert, A.L. [Université Paris-Sud, SP2M, ICMMO, UMR CNRS 8182, 91405 Orsay Cedex (France); Brisset, F. [Université Paris-Sud, ICMMO, UMR CNRS 8182, 91405 Orsay Cedex (France); Benoit, A.; Paillard, P. [Institut des Matériaux Jean Rouxel (IMN), UMR 6502, Polytech’Nantes, Nantes Cedex (France); Baudin, T. [Université Paris-Sud, SP2M, ICMMO, UMR CNRS 8182, 91405 Orsay Cedex (France)

2015-07-29

AA6061 alloy is a widely used material in the automotive and aerospace industries, but is prone to hot cracking, which limits its weldability. To prevent this phenomenon, the AA6061/AA5754 composite was formed using a severe plastic deformation technique, Cross Accumulative Roll Bonding (CARB), at an elevated temperature (350 °C) to ensure good bonding between layers. This technique was efficient to maintain a small grain size, even under the process temperature conditions, and consequently, preserve good mechanical properties. The composite had better mechanical properties than the initial aluminium alloys. Microstructure and texture remained stable after two cycles and yield stress tended towards an equal value in the rolling and the transverse directions. After two cycles, the main component was the {001}〈110〉 rotated Cube, which was maintained for up to 10 cycles. Diffusion was more effective as the strain increased. Finally, a tungsten inert gas (TIG) welding process was performed on the composite and confirmed resistance to hot cracking.

Effect of aluminium particles on mechanical and morphological properties of epoxy nanocomposites

Directory of Open Access Journals (Sweden)

Bello Sefiu A.

2017-01-01

Full Text Available Bumper is a front or rear part of automobiles. It is designed and shaped to be impact absorbing and protecting automobiles from damage in low impact collisions. Initially, they were made from heavy steels, increasing the weight of automobiles and fuel consumption. Also, high impacts of steel bumpers on pedestrians during accidental collision cause fatalities and or disabilities. An effort to enhance fuel efficiency, safety, freedom of design and shape detailing, heavy alloys for automobile applications are now being replaced with polymeric composites. Aluminium micro particles and nanoparticles were prepared from aluminium cans through sand casting, lathe machine spinning, and ball milling techniques. Both types of aluminium particles were incorporated into a mixture of diglycidyl ether of bisphenol A (DGEBA, epoxy resin cured with amine base hardener (ABH. Phases of the epoxy polymer and composites were identified using Xray Diffraction (XRD. Spatial arrangement of the phases within the matrix and their elemental composition were examined using Scanning Electron Microscope with attached energy dispersive X-ray spectroscopy (SEM/EDX. Tensile, impact and micro hardness tests were conducted on the prepared epoxy/aluminium composites. Results of the XRD showed the presence of aluminium compounds/phases due to chemical reactions between aluminium particles and DGEBA/ABH system. SEM confirmed a homogeneous distribution of the phases within the epoxy matrix, and that there is a strong adhesion between the epoxy matrix and aluminium particles. Correlation between the mechanical properties of the prepared nanocomposite and the procured bumper materials exhibited a fair suitability of the prepared nanocomposites for automobile applications.

Electrochemical characteristics of a carbon fibre composite and the associated galvanic effects with aluminium alloys

Energy Technology Data Exchange (ETDEWEB)

Liu, Z., E-mail: zuojia.liu@gmail.com; Curioni, M.; Jamshidi, P.; Walker, A.; Prengnell, P.; Thompson, G.E.; Skeldon, P.

2014-09-30

Highlights: • Exposed carbon fibres on two defined regions (“front” and “side”) are a focus of the investigation in NaCl electrolyte. • The exposed carbon fibres on the side and front regions are responsible for a high cathodic current density. • The NaCl + CuSO{sub 4} electrolyte was used to investigate the cathodic polarization behaviour of the exposed carbon fibres. • Galvanic coupling behaviour between the composite and aluminium alloys (AA7075-T6 and AA1050) was measured in NaCl electrolyte. • The higher galvanic current density measured on AA1050 alloy introduced a higher dissolution rate than the AA7075-T6 alloy. - Abstract: The electrochemical behaviour of a carbon fibre reinforced epoxy matrix composite in 3.5% NaCl and 3.5% NaCl + 0.5 M CuSO{sub 4} electrolytes was examined by potentiodynamic polarisation, potentiostatic polarisation and scanning electron microscopy. Exposed carbon fibres on two defined regions (“front” and “side”) are a focus of the investigation. The large size of the exposed carbon fibres on the side region is responsible for a higher cathodic current density than the front region in the NaCl electrolyte. The deposition of copper on the front surface of composite confirmed that the significantly higher cathodic current resulted from the exposure of the fibres to the NaCl electrolyte. Galvanic coupling between the composite and individual aluminium alloys (AA7075-T6 and AA1050) was used to measure galvanic potentials and galvanic current densities. The highly alloyed AA7075-T6 alloy and its high population density of cathodic sites compared to the AA1050 acted to reduce the galvanic effect when coupled to the composite front or side regions.

Microstructure, cold workability and strain hardening behavior of trimodaled AA 6061-TiO2 nanocomposite prepared by mechanical alloying

International Nuclear Information System (INIS)

Sivasankaran, S.; Sivaprasad, K.; Narayanasamy, R.

2011-01-01

Highlights: → Trimodaled composites consisting of UFG and CG matrix phases and ceramic phase were produced successfully. → Cold deformation behavior was investigated. → The 15% CG trimodaled composite yielded a high compressive strength of 935 MPa. → The 30% CG composite exhibited higher ductility while maintaining strength and toughness. - Abstract: In the present work, the improvement of compressive ductility while maintaining high strength and toughness for nanocrystalline materials by cold upsetting (incremental loads) of bulk trimodaled composite was studied. Mechanically alloyed nanocrystalline (NC) AA 6061 alloy powders reinforced with nano TiO 2 were blended with 0, 5, 10, 15, 20, 25, and 30 wt.% coarse grain (CG) elemental powders related to AA 6061 alloy composition to produce trimodal microstructure. The synthesized composite preforms were characterized by optical microscope, scanning electron microscope, transmission electron microscope and X-ray diffraction. The room temperature compressive deformation behavior was evaluated under triaxial stress state condition. With increasing percentage of CG phase in the nanocomposite, the gradual improvement in compressive ductility was observed at the cost of a small amount of strength but it favored the ease of deformation. The 15% CG trimodal composite exhibited an extremely high compressive strength of 935 MPa due to non-coalescence of individual CG particles and effective load transfer occurred in multi scale microstructures. But the 30% CG trimodal composite showed an incremental compressive ductility of around 16% while sacrificing a small amount of strength (845 MPa) and this composite displayed improved toughness (area under true effective stress and true effective strain curve) of over 600% than nanocomposite (0% CG). Also, the percentage cold workability of 30% CG composite was six times higher than that of 0% CG composite. Hence, the 30% CG trimodal composite was observed to be the good one as

Bonding of aluminium matrix composites for application in the transport industry

International Nuclear Information System (INIS)

Urena, A.; Gomez de Salazar, J.M.

1993-01-01

A discontinuously reinforced MMC containing 12 vol % SiC particles in an Al-Cu-Mg alloy (AA 2124) matrix has been diffusion bonded. Thick interlayers of different superplastic aluminium alloys (Al-Li 8090 and Al-Cu SUPRAL) were used to reduce the bonding pressure and ensure complete surface contact. Microstructural studies shown higher continuity in joints bonded with 8090 interlayer than with other alloys. Precipitation of rich-copper intermetallic was detected, after bonding, in the interlayer because diffusion of Cu from 2124 matrix. Results suggest that Li contained in the interlayer favours the partial disruption of the aluminium oxide film, making easier the solid state bonding. (orig.)

Analysing the strength of friction stir welded dissimilar aluminium alloys using Sugeno Fuzzy model

Science.gov (United States)

Barath, V. R.; Vaira Vignesh, R.; Padmanaban, R.

2018-02-01

Friction stir welding (FSW) is a promising solid state joining technique for aluminium alloys. In this study, FSW trials were conducted on two dissimilar plates of aluminium alloy AA2024 and AA7075 by varying the tool rotation speed (TRS) and welding speed (WS). Tensile strength (TS) of the joints were measured and a Sugeno - Fuzzy model was developed to interconnect the FSW process parameters with the tensile strength. From the developed model, it was observed that the optimum heat generation at WS of 15 mm.min-1 and TRS of 1050 rpm resulted in dynamic recovery and dynamic recrystallization of the material. This refined the grains in the FSW zone and resulted in peak tensile strength among the tested specimens. Crest parabolic trend was observed in tensile strength with variation of TRS from 900 rpm to 1200 rpm and TTS from 10 mm.min-1 to 20 mm.min-1.

Inhibition of Aluminium Corrosion in Hydrochloric Acid Using Nizoral and the Effect of Iodide Ion Addition

OpenAIRE

I. B. Obot; N. O. Obi-Egbedi

2010-01-01

The effect of nizoral (NZR) on the corrosion inhibition of aluminium alloy AA 1060 in 2 M HCl solution was investigated using the mylius thermometric technique. Results of the study revealed that nizoral acts as corrosion inhibitor for aluminium in the acidic medium. In general, at constant acid concentration, the inhibition efficiency increases with increase in the inhibitor concentration. The addition of KI to the inhibitor enhanced the inhibition efficiency to a considerable extent. The ad...

Inhibition of Aluminium Corrosion in Hydrochloric Acid Using Nizoral and the Effect of Iodide Ion Addition

Directory of Open Access Journals (Sweden)

I. B. Obot

2010-01-01

Full Text Available The effect of nizoral (NZR on the corrosion inhibition of aluminium alloy AA 1060 in 2 M HCl solution was investigated using the mylius thermometric technique. Results of the study revealed that nizoral acts as corrosion inhibitor for aluminium in the acidic medium. In general, at constant acid concentration, the inhibition efficiency increases with increase in the inhibitor concentration. The addition of KI to the inhibitor enhanced the inhibition efficiency to a considerable extent. The adsorption of nizoral onto the aluminium surface was found to obey the Fruendlich adsorption isotherm. The value of the free energy for the adsorption process shows that the process is spontaneous.

Aluminium and Aroma Compound Concentration in Beer During Storage at Different Temperatures

Directory of Open Access Journals (Sweden)

Marija Soldo Gjeldum

2006-01-01

Full Text Available Problem of aluminium in beer has been elaborated in several papers over the last decade. However, the effect of aluminium on organoleptic properties of beer has been observed in few papers where it has been stated that aluminium gives beer a »metallic« and bitter flavour without any observations on particular aroma compound changes. Also, the number of reports on precise changes of aroma components throughout different storage conditions is surprisingly scarce. In order to investigate the changes of aluminium concentration along with aroma compound changes, graphite furnace-atomic absorption spectrophotometry (GF-AAS with Zeeman background correction and gas chromatography with static headspace sampler (GC-HSS were used in this work. Analyses were conducted periodically throughout seven months of storage on three different brands of beer from name breweries. Samples were taken before and after filling in aluminium cans. One part of samples was stored in a refrigerator (4 °C and the other in a thermostatic chamber (22 °C. The effects of beer brand and storage conditions on aluminium concentration and level of aroma compounds were measured. To prove the effect of aluminium concentration on the changes of aroma compounds, the adequate level of aluminium sulphate was added to bottled beer samples stored at 28 °C. Although different beer types showed significantly different aluminium concentration, it could be the result of other factors (different batches of identical beer type showed significantly different aluminium concentration as well. Samples that were stored in the refrigerator were protected from aluminium migration from the can to the beer and showed increased aroma stability. Level of aroma constituents of analyzed beer brands was significantly different. Elevated aluminium concentration did not have any noticeable effect on the level of aroma compounds in beer samples stored at 28 °C.

Study of 2219 aluminum alloy using direct current A-TIG welding

Science.gov (United States)

Li, Hui; Zou, Jiasheng

2017-07-01

Direct current A-TIG (DCEN A-TIG) welding using special active agent had eliminated the pores and the oxidation of 2219 high-strength aluminum alloy in welding. Addition of AlF3-25% LiF active agent to DCEN A-TIG welding and arc morphology showed a trailing phenomenon. However, the change in arc morphology was not remarkable when AlF3-75% LiF active agent was added. Addition of AlF3-75% LiF active agent can refine the grain size of DCEN A-TIG joint. The mechanical properties of the weld were optimal at 10% AlF3-75% LiF active agent. Compared with AC TIG and AC A-TIG welding, DCEN A-TIG welding yielded better results for 2219 Al alloy.

Evolution of mechanical behavior of 6XXX aluminium alloy due to the precipitation state during a thermo-mechanical process

International Nuclear Information System (INIS)

Bardel, Didier; Perez, Michel; Nelias, Daniel; Chaise, Thibaut; Garnier, Jerome; Bourlier, Florent

2014-01-01

The aim of this research is to link the microstructural state and the mechanical properties of an age hardening alloy during a fast heat treatment such as encountered during welding. A coupled model between precipitation state and mechanical properties is used to predict the yield strength and hardening behavior that can be observed experimentally. The method permits the identification of the kinematic and isotropic contributions in the hardening model. The methodology is applied to a 6061-T6 aluminium alloy which is used in the Jules Horowitz reactor vessel. The general idea of this methodology is to couple an efficient microstructural model to a mechanical one based on the dislocation theory and ad'hoc experiments. The theoretical background is based on the work of Kampmann and Wagner, known as the KWN model, to account for nucleation, growth/dissolution and coarsening of precipitates. This analysis requires transient thermo-mechanical experimental data. The efficiency of these models and their coupling are shown for a series 6XXX aluminium alloy which contains β'' and β' precipitates. Ultimately these models are coupled to a FEA model and allows to predict the distribution of precipitates within each element of the mesh, and subsequently its mechanical behavior. (authors)

Industrial based volume manufacturing of lightweight aluminium alloy panel components with high-strength and complex-shape for car body and chassis structures

Science.gov (United States)

Anyasodor, Gerald; Koroschetz, Christian

2017-09-01

To achieve the high volume manufacture of lightweight passenger cars at economic cost as required in the automotive industry, low density materials and new process route will be needed. While high strength aluminium alloy grades: AA7075 and AA6082 may provide the alternative material solution, hot stamping process used for high-strength and ultrahigh strength steels such as boron steel 22mnb5 can enable the volume manufacture of panel components with high-strength and complex-shape for car body and chassis structures. These aluminium alloy grades can be used to manufacture panel components with possible yield strengths ≥ 500 MPa. Due to the differences in material behaviors, hot stamping process of 22mnb5 cannot be directly applied to high strength aluminium alloy grades. Despite recorded successes in laboratories, researches and niche hot forming processes of high strength aluminium alloy grades, not much have been achieved for adequate and efficient volume manufacturing system applicable in the automotive industry. Due to lack of such system and based on expert knowledge in hot stamping production-line, AP&T presents in this paper a hot stamping processing route for high strength aluminium alloys been suitable for production-line development and volume manufacturing.

Corrosion of aluminium-clad spent fuel in LVR-15 research reactor storage facilities. Final report

International Nuclear Information System (INIS)

Splichal, K.; Berka, J.; Keilova, E.

2006-03-01

The corrosion of the research reactor aluminium clad spent fuel in water was investigated in two storage facilities. The standard racks were delivered by the IAEA and consisted of two aluminium alloys AA 6061 and Szav-1 coupons. Bimetallic couples create aluminium alloy and stainless steel 304 coupons. Rolled and extruded AA 6061 material was also tested. Single coupons, bimetallic and crevice couples were exposed in the at-reactor basin (ARB) and the high-level wastage pool (HLW). The water chemistry parameters were monitored and sedimentation of impurities was measured. The content of impurities of mainly Cl and SO 4 was in the range of 2 to 15 μg/l in the HLW pool; it was about one order higher in ARB. The Fe content was below 2 μg/l for both facilities. After two years of exposure the pitting was evaluated as local corrosion damage. The occurrence of pits was evaluated predominantly on the surfaces of single coupons and on the outer and inner surfaces of bimetallic and crevices coupons. No correlation was found between the pitting initiation and the type of aluminium alloys and rolled and extruded materials. In bimetallic couples the presence of stainless coupons did not have any effect on local corrosion. The depth of pits was lower than 50 μm for considerable areas of coupons and should be compared with the results of other participating institutes. (author)

Microstructure strengthening mechanisms in an Al–Mg–Si–Sc–Zr equal channel angular pressed aluminium alloy

Energy Technology Data Exchange (ETDEWEB)

Cabibbo, Marcello, E-mail: m.cabibbo@univpm.it [Dipartimento di Ingegneria Meccanica e Scienze Matematiche (DIISM), Università Politecnica delle Marche, 60131 Ancona (Italy)

2013-09-15

Microstructure dislocation strengthening mechanisms in severely deformed aluminium strongly depend on the different boundary evolutions. Thereafter, models of proof stress determination should take into account the different nature of the boundaries that form during severe plastic deformation. In the last few decades, Hall–Petch modified relationship and other proof stress modelling were extensively discussed. This paper deals with further insights into the Hansen's and other authors approach to the modelling of aluminium poof stress after equal channel angular pressing. The present model is based on a detailed transmission electron microscopy microstructure characterization of the different strengthening contributions in an age-hardened Al–Mg–Si–Sc–Zr alloy.

Microstructure strengthening mechanisms in an Al–Mg–Si–Sc–Zr equal channel angular pressed aluminium alloy

International Nuclear Information System (INIS)

Cabibbo, Marcello

2013-01-01

Microstructure dislocation strengthening mechanisms in severely deformed aluminium strongly depend on the different boundary evolutions. Thereafter, models of proof stress determination should take into account the different nature of the boundaries that form during severe plastic deformation. In the last few decades, Hall–Petch modified relationship and other proof stress modelling were extensively discussed. This paper deals with further insights into the Hansen's and other authors approach to the modelling of aluminium poof stress after equal channel angular pressing. The present model is based on a detailed transmission electron microscopy microstructure characterization of the different strengthening contributions in an age-hardened Al–Mg–Si–Sc–Zr alloy.

The effect of natural pre-ageing on the mechanical properties of Rheo-High pressure die cast aluminium alloy 2139

CSIR Research Space (South Africa)

Chauke, L

2015-07-01

Full Text Available -high pressure die casting process (R-HPDC). Alloy 2139 is a Ag-containing aluminium alloy from the Al-Cu-Mg 2xxx series family. The addition of Ag enhances the age hardening response through the formation of co-clusters that act as precursors to the formation...

Aluminium production

International Nuclear Information System (INIS)

Winter, B.; Ayers, J.; Sammer, G.

2001-01-01

Aluminium is the most important non-ferrous metal by quantity. Aluminium is produced by electrolysis of aluminium oxide (also known as alumina). Alumina is produced by refining bauxite. The quantity of primary and secondary aluminium production in ECE-countries between 1992 and 1998 is shown. The European aluminium industry employs approximately 200 000 employees. The annual aluminium production in the European Union was 3.58 million tonnes in 1994, of which 44 % was secondary aluminium. In 1996 3.96 million tonnes of aluminium were produced in the EU, of which 44 % was secondary aluminium. (author)

Factors affecting the aluminium content of human femoral head and neck.

Science.gov (United States)

Zioła-Frankowska, Anetta; Dąbrowski, Mikołaj; Kubaszewski, Łukasz; Rogala, Piotr; Frankowski, Marcin

2015-11-01

Tissues for the study were obtained intraoperatively during hip replacement procedures from 96 patients. In all the cases, the indication for this treatment was primary or secondary degenerative changes in the hip joint. The subject of the study was the head and neck of the femur, resected in situ. Aluminium concentrations measured in femoral head and neck samples from patients aged between 25 and 91 were varied. Statistical methods were applied to determine the variations in relation to the parameters from the background survey. Significant differences in the aluminium content of femoral head samples were observed between patients under and over 60 years of age. Based on the results, it was confirmed that the aluminium accumulates in bones over a lifetime. The study showed that the content of aluminium in the head and neck of the femur depends on the factors such as: type of medicines taken, contact with chemicals at work, differences in body anatomy and sex. The study on the levels of aluminium in bones and the factors affecting its concentration is a valuable source of information for further research on the role of aluminium in bone diseases. Based on the investigations, it was found that the GF-AAS technique is the best analytical tool for routine analysis of aluminium in complex matrix samples. The use of femoral heads in the investigations was approved by the Bioethics Committee of the University of Medical Sciences in Poznań (Poland). Copyright © 2015 Elsevier Inc. All rights reserved.

AA, Inner Conductor of Magnetic Horn

CERN Multimedia

CERN PhotoLab

1979-01-01

Antiprotons emerging at large angles from the production target (hit by an intense 26 GeV proton beam from the PS), were focused into the acceptance of the injection line of the AA by means of a "magnetic horn" (current-sheet lens). Here we see an early protype of the horn's inner conductor, machined from solid aluminium to a thickness of less than 1 mm. The 1st version had to withstand pulses of 150 kA, 15 us long, every 2.4 s. See 8801040 for a later version.

Diffusion bonding of an aluminium alloy (AA 2124) reinforced with SiC whiskers, using AL-Li interlayers (AA 8090)

International Nuclear Information System (INIS)

Urena, A.; Gomez de Salazar, J.M.; Escalera, M.D.; Escriche, E.

1994-01-01

The use of an AL-Li alloy as interlayer for the diffusion bonding of an aluminium matrix composite reinforced with silicon carbide whiskers has been studied. The influence of the different welding parameters on the joint microstructure and mechanical strength has also been analyzed. Besides, the failure mechanisms of shear tested joints have been investigated using fractographic techniques. (Author) 9 refs

Influence of in situ formed ZrB2 particles on microstructure and mechanical properties of AA6061 metal matrix composites

International Nuclear Information System (INIS)

Dinaharan, I.; Murugan, N.; Parameswaran, Siva

2011-01-01

Highlights: → In situ fabrication of aluminium metal matrix composite reinforced ZrB 2 particles. → Colour metallography of composites. → Improvement of matrix properties by ZrB 2 particles. → Sliding wear behaviour of in situ composites. - Abstract: Particulate reinforced metal matrix composites (PMMCs) have gained considerable amount of research emphasis and attention in the present era. Research is being carried out across the globe to produce new combination of PMMCs. PMMCs are prepared by adding a variety of ceramic particles with monolithic alloys using several techniques. An attempt has been made to produce aluminium metal matrix composites reinforced with zirconium boride (ZrB 2 ) particles by the in situ reaction of K 2 ZrF 6 and KBF 4 salts with molten aluminium. The influence of in situ formed ZrB 2 particles on the microstructure and mechanical properties of AA6061 alloy was studied in this work. The in situ formed ZrB 2 particles significantly refined the microstructure and enhanced the mechanical properties of AA6061 alloy. The weight percentage of ZrB 2 was varied from 0 to 10 in steps of 2.5. Improvement of hardness, ultimate tensile strength and wear resistance of AA6061 alloy was observed with the increase in ZrB 2 content.

Optimization of friction stir welding process parameters to maximize tensile strength of stir cast AA6061-T6/AlNp composite

International Nuclear Information System (INIS)

Ashok Kumar, B.; Murugan, N.

2014-01-01

Highlights: • AA6061/AlN p cast composite was welded by FSW process. • Regression models were developed to predict UTS and elongation of the FS welded joint. • FS welded joint using the optimized parameters exhibited maximum UTS and joint efficiency. • Defect free weld joint was obtained with optimized parameters value. - Abstract: Aluminium Matrix Composites (AMCs) reinforced with particulate form of reinforcement has replaced monolithic alloys in many engineering industries due to its superior mechanical properties and tailorable thermal and electrical properties. As aluminium nitride (AlN) has high specific strength, high thermal conductivity, high electrical resistivity, low dielectric constant, low coefficient of thermal expansion and good compatibility with aluminium alloy, Al/AlN composite is extensively used in electronic packaging industries. Joining of AMCs is unavoidable in many engineering applications. Friction Stir Welding (FSW) is one of the most suitable welding process to weld the AMCs reinforced with particulate form of ceramics without deteriorating its superior mechanical properties. An attempt has been made to develop regression models to predict the Ultimate Tensile Strength (UTS) and Percent Elongation (PE) of the friction stir welded AA6061 matrix composite reinforced with aluminium nitride particles (AlN p ) by correlating the significant parameters such as tool rotational speed, welding speed, axial force and percentage of AlN p reinforcement in the AA6061 matrix. Statistical software SYSTAT 12 and statistical tools such as analysis of variance (ANOVA) and student’s t test, have been used to validate the developed models. It was observed from the investigation that these factors independently influenced the UTS and PE of the friction stir welded composite joints. The developed regression models were optimized to maximize UTS of friction stir welded AA6061/AlN p composite joints

Effect of Repair Welding on Electrochemical Corrosion and Stress Corrosion Cracking Behavior of TIG Welded AA2219 Aluminum Alloy in 3.5 Wt Pct NaCl Solution

Science.gov (United States)

Venugopal, A.; Sreekumar, K.; Raja, V. S.

2010-12-01

The stress corrosion cracking (SCC) behavior of AA2219 aluminum alloy in the as-welded (AW) and repair-welded (RW) conditions was examined and compared with that of the base metal (BM) in 3.5 wt pct NaCl solution using the slow strain rate technique (SSRT). The reduction in ductility was used as a parameter to evaluate the SCC susceptibility of both BM and welded joints. The results show that the ductility ratio ( ɛ NaCl/( ɛ air)) of the BM was close to one (0.97) and reduced to 0.9 for the AW joint. This value further reduced to 0.77 after carrying out one repair welding operation. However, the RW specimen exhibited higher ductility than the single-weld specimens even in 3.5 wt pct NaCl solution. SSRT results obtained using pre-exposed samples followed by post-test metallographic observations clearly showed localized pitting corrosion along the partially melted zone (PMZ), signifying that the reduction in ductility ratio of both the AW and RW joints was more due to mechanical overload failure, caused by the localized corrosion and a consequent reduction in specimen thickness, than due to SCC. Also, the RW joint exhibited higher ductility than the AW joint both in air and the environment, although SCC index (SI) for the former is lower than that of the latter. Fractographic examination of the failed samples, in general, revealed a typical ductile cracking morphology for all the base and welded joints, indicating the good environmental cracking resistance of this alloy. Microstructural examination and polarization tests further demonstrate grain boundary melting along the PMZ, and that provided the necessary electrochemical condition for the preferential cracking on that zone of the weldment.

Multi-objective Optimization of Friction Welding Process Parameters using Grey Relational Analysis for Joining Aluminium Metal Matrix Composite

Directory of Open Access Journals (Sweden)

Sreenivasan KONGANAPURAM SUNDARARAJAN

2018-05-01

Full Text Available Aluminium metal matrix composites has gained importance in recent time because of its improved mechanical and metallurgical properties. The welding of aluminium metal matrix composites using conventional welding process has got many demerits so in order to overcome them a solid state welding process is to be employed. To achieve a good strength weld in the aluminium metal matrix composite bars an efficient and most preferred technique is friction welding. In this work the aluminium metal matrix composite AA7075 + 10 % vol SiC-T6 is selected and friction welded. The combination of friction welding process parameters such as spindle speed, friction pressure, upset pressure and burn-off- length for joining the AA7075 + 10 % vol SiCP-T6 metal matrix composite bars are selected by Taguchi’s design of experiment. The optimum friction welding parameters were determined for achieving improved ultimate tensile strength and the hardness using grey relational analysis. A combined grey relational grade is found from the determined grey relational coefficient of the output responses and the optimum friction welding process parameters were obtained as spindle speed – 1200 rpm, friction pressure – 100 MPa, upset pressure – 250 MPa, Burn-off-Length – 2 mm. Analysis of variance (ANOVA performed shows that the friction pressure is the most significant friction welding parameter that influences the both the ultimate tensile strength and hardness of friction welded AA7075 + 10 % volSiCP-T6 joints. The fractured surface under microstructure study also revealed good compliance with the grey relational grade result. DOI: http://dx.doi.org/10.5755/j01.ms.24.2.17725

Experimental investigation and finite element simulation of laser beam welding induced residual stresses and distortions in thin sheets of AA 6056-T4

International Nuclear Information System (INIS)

Zain-ul-abdein, Muhammad; Nelias, Daniel; Jullien, Jean-Francois; Deloison, Dominique

2010-01-01

Laser beam welding has recently found its application in the fabrication of aircraft structures where fuselage panels, made of thin sheets of AA 6056-T4 (an aluminium alloy), are welded with stiffeners of the same material in a T-joint configuration. The present work simulates laser beam welding induced residual stresses and distortions using industrially employed thermal and mechanical boundary conditions. Various measurements performed on small-scale welded test specimens provide a database of experimental results that serves as a benchmark for qualification of the simulation results. The welding simulation is performed with the commercial finite element software Abaqus and a Fortran programme encoding a conical heat source with Gaussian volumetric distribution of flux. A sequentially coupled temperature-displacement analysis is undertaken to simulate the weld pool geometry, transient temperature and displacement fields. The material is assumed to follow an elasto-plastic law with isotropic hardening behaviour (von Mises plasticity model). A comparison between the experimental and simulation results shows a good agreement. Finally, the residual stress and strain states in a T-joint are predicted.

The effect of welding parameters on surface quality of AA6351 aluminium alloy

International Nuclear Information System (INIS)

Yacob, S; Ariffin, N; Ali, R; Arshad, A; Wahab, M I A; Ismail, S A; Roji, NS M; Din, W B W; Zakaria, M H; Abdullah, A; Yusof, M I; Kamarulzaman, K Z; Mahyuddin, A; Hamzah, M N; Roslan, R; MAli, M A; Ahsan, Q

2015-01-01

In the present work, the effects of gas metal arc welding-cold metal transfer (GMAW-CMT) parameters on surface roughness are experimentally assessed. The purpose of this study is to develop a better understanding of the effects of welding speed, material thickness and contact tip to work distance on the surface roughness. Experiments are conducted using single pass gas metal arc welding-cold metal transfer (GMAW-CMT) welding technique to join the material. The material used in this experiment was AA6351 aluminum alloy with the thickness of 5mm and 6mm. A Mahr Marsuft XR 20 machine was used to measure the average roughness (Ra) of AA6351 joints. The main and interaction effect analysis was carried out to identify process parameters that affect the surface roughness. The results show that all the input process parameters affect the surface roughness of AA6351 joints. Additionally, the average roughness (Ra) results also show a decreasing trend with increased of welding speed. It is proven that gas metal arc welding-cold metal transfer (GMAW-CMT)welding process has been successful in term of providing weld joint of good surface quality for AA6351 based on the low value surface roughness condition obtained in this setup. The outcome of this experimental shall be valuable for future fabrication process in order to obtained high good quality weld. (paper)

Conditioning of radioactive aluminium generated by the VVR-S Nuclear Reactor Decommissioning Laboratory Inactive Tests

International Nuclear Information System (INIS)

Nicu, M.; Ionascu, L.; Turcau, C.; Dragolici, F.; Rotarescu, G.

2015-01-01

Aluminium is a reactive amphoteric metal, readily forming a protective oxide layer on contact with air or water. However, as the oxides are amphoteric, aluminium is not resistant to corrosion in acidic and alkaline conditions, because the protective films dissolve. As a consequence radioactive waste containing bulk aluminium alloys can not be embedded in Ordinary Portland Cement (OPC). A potential encapsulating material for the radioactive aluminium is potassium magnesium phosphate (MKP). This paper presents the characterization results obtained from analyzing the potential magnesium phosphate formulations and assesses its potential to reduce the corrosion of aluminium. A series of experiments have been performed. The main conclusions of the paper are as follows. First, the pH values of magnesium phosphate formulation investigated increased gradually over the test duration, with pH measurement ranging from 8.1 - 9.1, indicating lower values compared with the reference composite OPC (pH ∼ 13). The reduction of pH is an important controlling factor for the corrosion of aluminium. Secondly, according to XRD, the hardened magnesium phosphate matrix is polycrystalline and the main reaction product of magnesium phosphate cement formulations was confirmed as MgKPO 4 -6H 2 O, which was found to dominate the crystalline phase composition. Thirdly, the compressive strengths obtained for magnesium phosphate matrices investigated are included in the accepted limits for the embedding matrix with cement (above 5 N/mm 2 ). And fourthly, the corrosion of metallic aluminium in magnesium phosphate matrix is markedly reduced in comparison with the composite OPC

Modeling Dynamic Anisotropic Behaviour and Spall Failure in Commercial Aluminium Alloys AA7010

Science.gov (United States)

Mohd Nor, M. K.; Ma'at, N.; Ho, C. S.

2018-04-01

This paper presents a finite strain constitutive model to predict a complex elastoplastic deformation behaviour involves very high pressures and shockwaves in orthotropic materials of aluminium alloys. The previous published constitutive model is used as a reference to start the development in this work. The proposed formulation that used a new definition of Mandel stress tensor to define Hill's yield criterion and a new shock equation of state (EOS) of the generalised orthotropic pressure is further enhanced with Grady spall failure model to closely predict shockwave propagation and spall failure in the chosen commercial aluminium alloy. This hyperelastic-plastic constitutive model is implemented as a new material model in the Lawrence Livermore National Laboratory (LLNL)-DYNA3D code of UTHM's version, named Material Type 92 (Mat92). The implementations of a new EOS of the generalised orthotropic pressure including the spall failure are also discussed in this paper. The capability of the proposed constitutive model to capture the complex behaviour of the selected material is validated against range of Plate Impact Test data at 234, 450 and 895 ms-1 impact velocities.

Effect of precipitates on mechanical properties of AA2195

International Nuclear Information System (INIS)

Kim, Jae-Hee; Jeun, Jeong-Hoon; Chun, Hyun-Jin; Lee, Ye Rim; Yoo, Joon-Tae; Yoon, Jong-Hoon; Lee, Ho-Sung

2016-01-01

Addition of 1–4 wt.% lithium into a conventional Al–Cu–Mg alloy allows lower density and higher mechanical properties, which are attractive for aerospace applications. In this study, fundamental investigations including phase and microstructure evolution, resulting in strengthening, of the AA2195 are conducted to observe a possibility of production with commercial level. Precipitation sequence and kinetics during post-annealing were evaluated with variations of temperature and holding time. Microstructures revealed formation and evolution in representative precipitates including θ (Al_2Cu), ß′ (Al_3Zr), and T (Al_xLi_yCu) series. Aluminum alloys have low hardness, modulus, and strength before aging, but precipitates such as θ′ (Al_2Cu), ß′ (Al_3Zr), and T_1 (Al_2LiCu) show enhanced mechanical properties of AA2195 tempered because of their interaction with dislocation. However, longer holding time and higher annealing temperature result in significant decreases in mechanical properties due to the presence of incoherent precipitates (θ phase) and coarsening of the precipitates via grain-boundary diffusion. In the current study, the tensile strength of 560 MPa was obtained with post-heat treatment without work hardening. This value has never been achieved in other studies. The maximum strength was reported as 500 MPa without a work hardening process. - Highlights: • A relationship between microstructure and mechanical properties to post annealing AA2195. • A formation and dissolution of the precipitates were observed for various treatment. • An optimum post-annealing condition was obtained.

Effect of precipitates on mechanical properties of AA2195

Energy Technology Data Exchange (ETDEWEB)

Kim, Jae-Hee [Launcher Structure and Materials Team, Korea Aerospace Research Institute, Daejeon (Korea, Republic of); Jeun, Jeong-Hoon [Department of Materials Science and Engineering, Seoul National University, Seoul (Korea, Republic of); Chun, Hyun-Jin [Southeast University, Nanjing (China); Lee, Ye Rim [Department of Aerospace System Engineering, University of Science & Technology, Daejeon (Korea, Republic of); Yoo, Joon-Tae [Launcher Structure and Materials Team, Korea Aerospace Research Institute, Daejeon (Korea, Republic of); Yoon, Jong-Hoon [Launcher Structure and Materials Team, Korea Aerospace Research Institute, Daejeon (Korea, Republic of); Department of Aerospace System Engineering, University of Science & Technology, Daejeon (Korea, Republic of); Lee, Ho-Sung, E-mail: hslee@kari.re.kr [Launcher Structure and Materials Team, Korea Aerospace Research Institute, Daejeon (Korea, Republic of); Department of Aerospace System Engineering, University of Science & Technology, Daejeon (Korea, Republic of)

2016-06-05

Addition of 1–4 wt.% lithium into a conventional Al–Cu–Mg alloy allows lower density and higher mechanical properties, which are attractive for aerospace applications. In this study, fundamental investigations including phase and microstructure evolution, resulting in strengthening, of the AA2195 are conducted to observe a possibility of production with commercial level. Precipitation sequence and kinetics during post-annealing were evaluated with variations of temperature and holding time. Microstructures revealed formation and evolution in representative precipitates including θ (Al{sub 2}Cu), ß′ (Al{sub 3}Zr), and T (Al{sub x}Li{sub y}Cu) series. Aluminum alloys have low hardness, modulus, and strength before aging, but precipitates such as θ′ (Al{sub 2}Cu), ß′ (Al{sub 3}Zr), and T{sub 1} (Al{sub 2}LiCu) show enhanced mechanical properties of AA2195 tempered because of their interaction with dislocation. However, longer holding time and higher annealing temperature result in significant decreases in mechanical properties due to the presence of incoherent precipitates (θ phase) and coarsening of the precipitates via grain-boundary diffusion. In the current study, the tensile strength of 560 MPa was obtained with post-heat treatment without work hardening. This value has never been achieved in other studies. The maximum strength was reported as 500 MPa without a work hardening process. - Highlights: • A relationship between microstructure and mechanical properties to post annealing AA2195. • A formation and dissolution of the precipitates were observed for various treatment. • An optimum post-annealing condition was obtained.

Tensile behavior of dissimilar friction stir welded joints of aluminium alloys

International Nuclear Information System (INIS)

Shanmuga Sundaram, N.; Murugan, N.

2010-01-01

The heat treatable aluminium alloy AA2024 is used extensively in the aircraft industry because of its high strength to weight ratio and good ductility. The non-heat treatable aluminium alloy AA5083 possesses medium strength and high ductility and used typically in structural applications, marine, and automotive industries. When compared to fusion welding processes, friction stir welding (FSW) process is an emerging solid state joining process which is best suitable for joining these alloys. The friction stir welding parameters such as tool pin profile, tool rotational speed, welding speed, and tool axial force influence the mechanical properties of the FS welded joints significantly. Dissimilar FS welded joints are fabricated using five different tool pin profiles. Central composite design with four parameters, five levels, and 31 runs is used to conduct the experiments and response surface method (RSM) is employed to develop the model. Mathematical regression models are developed to predict the ultimate tensile strength (UTS) and tensile elongation (TE) of the dissimilar friction stir welded joints of aluminium alloys 2024-T6 and 5083-H321, and they are validated. The effects of the above process parameters and tool pin profile on tensile strength and tensile elongation of dissimilar friction stir welded joints are analysed in detail. Joints fabricated using Tapered Hexagon tool pin profile have the highest tensile strength and tensile elongation, whereas the Straight Cylinder tool pin profile have the lowest tensile strength and tensile elongation. The results are useful to have a better understanding of the effects of process parameters, to fabricate the joints with desired tensile properties, and to automate the FS welding process.

Ductile damage in aluminium alloy thin sheets: Correlation between micro-tomography observations and mechanical modeling

International Nuclear Information System (INIS)

Thuillier, S.; Maire, E.; Brunet, M.

2012-01-01

This work deals with the characterization of ductile damage in an aluminium alloy AA6016-T4 by X-ray micro-tomography, as a function of anisotropy and triaxiality. Interrupted tensile tests on notched samples with three different geometries were performed and the void volume fraction was measured for different strain values, up to rupture. It was shown that void volume fraction evolution with the strain is rather similar at 0° and 90° to RD but at 45° to RD it shows a more rapid evolution. Moreover, for the same strain level, a higher void volume fraction was recorded for a higher triaxiality ratio. Whatever the orientation and the stress triaxiality ratio, void volume fraction values range from 5×10 −4 up to 0.04. A numerical model based on Gurson–Tvergaard–Needleman constitutive equations was used to simulate the different tests. Hardening of the material was identified from macroscopic tensile test nucleation material parameters were identified by a direct method from void volume fraction evolution. It can be seen that the influence of triaxiality on void volume fraction is underestimated, though void growth is nicely predicted for the highest triaxiality ratio, for strains below 0.5. The load level was correctly predicted, except for high strain, where coalescence seems necessary to be taken into account.

Probing the nanostructural evolution of age-hardenable Al alloys with atom-probe tomography

International Nuclear Information System (INIS)

Biswas, Aniruddha

2010-01-01

Atom Probe Tomographic (APT) Microscope is a lens-less point-projection 3-D analytical microscope that has the unique capability of (i) three-dimensional imaging at the atomic scale and (ii) compositional analysis with sub-nanometre spatial resolution and single-atom sensitivity. Modern 3-D APT microscope offers the highest the spatial resolution among all the available analytical techniques. It can simultaneously achieve a spatial resolution better than 0.3 nm in all three directions of a three-dimensional analysis-volume. As a result, 3-D APT microscopy, especially as practiced by the high speed, large field of view instruments is the most appropriate tool for studying nano-scale precipitates and their heterophase interfaces. This talk will introduce the technique, discuss its brief historical background and use examples from age-hardenable Al-alloys. The results include a detailed APT study of the compositional evolution of the nano-scale precipitates: θ and Q present in commercial age hardenable aluminium alloy, W319

Study of the precipitation hardening process in recycled Al-Si-Cu cast alloys

Directory of Open Access Journals (Sweden)

Kuchariková L.

2017-03-01

Full Text Available The formation of extremely small uniformly dispersed particles of a second phase within the original phase matrix during heat treatment changed material properties. Therefore the characterization of precipitation had been investigated using high resolution transmission electron microscopy (TEM and electron diffraction of thin foils for an AlSi9Cu3 cast alloy. For investigation the hardening effect onto mechanical properties of aluminium cast was used heat treatment, which consisted from solution treatment at 515°C / 4 hours (h, followed by quenching into water with temperature 50°C and artificial aging using different temperatures 170°C and 190°C with different holding time 2, 4, 8, 16, and 32 hours. The observations of microstructure and substructure reveals that precipitation hardening has caused great changes in size, morphology and distributions of structural components, the formation of precipitates of Cu phases, and the change of mechanical properties as well.

The influence of strain on annealing behaviour of heavily rolled aluminium AA1050

DEFF Research Database (Denmark)

Mishin, Oleg; Juul Jensen, Dorte; Hansen, Niels

2012-01-01

Deformation structures and annealing behaviour have been analysed in the centre layer of two AA1050 samples cold-rolled to von Mises strains of 3.6 and 6.4. During annealing at 270-300°C structural coarsening and discontinuous recrystallization occurred in both samples. In the coarsened microstru......Deformation structures and annealing behaviour have been analysed in the centre layer of two AA1050 samples cold-rolled to von Mises strains of 3.6 and 6.4. During annealing at 270-300°C structural coarsening and discontinuous recrystallization occurred in both samples. In the coarsened...

Volta potential of clad AA2024 aluminium after exposure to CeCl3 solution

International Nuclear Information System (INIS)

Andreatta, F.; Druart, M.-E.; Marin, E.; Cossement, D.; Olivier, M.-G.; Fedrizzi, L.

2014-01-01

Highlights: • Alkaline etch of clad AA2024 enhances precipitation of Ce compounds. • Exposure to CeCl 3 solution decreases Volta potential of alkaline etched substrate. • Ce compounds reduce the driving force for initiation of localized attack. - Abstract: AA2024 clad with AA1050 was immersed in CeCl 3 solution to promote deposition of cerium species. The deposition occurs on the entire sample surface for the alkaline etched substrate, while it is very limited for the degreased substrate. The surface potential (Volta potential) was investigated by scanning Kelvin probe force microscopy after different immersion times in CeCl 3 solution. The preferential deposition of Ce compounds at Al–Fe intermetallic sites progressively reduces their Volta potential difference relative to the matrix in the alkaline etched substrate. This reduces the susceptibility to localized attack of the intermetallics as proven by potentiodynamic polarization measurements

Aluminium bridges, aluminium bridge decks

NARCIS (Netherlands)

Soetens, F.; Straalen, IJ.J. van

2003-01-01

Applications of aluminium have grown considerably in building and civil engineering the last decade. In building and civil engineering the increase of aluminium applications is due to various aspects like light weight, durability and maintenance, use of extrusions, and esthetics. The paper starts

Parametric optimisation of heat treated recycling aluminium (AA6061) by response surface methodology

Science.gov (United States)

Ahmad, A.; Lajis, M. A.; Yusuf, N. K.; Shamsudin, S.; Zhong, Z. W.

2017-09-01

Alternating typical primary aluminium production with recycling route should benefit various parties, including the environment since the need of high cost and massive energy consumption will be ruled out. At present, hot extrusion is preferred as the effective solid-state recycling process compared to the typical method of melting the swarf at high temperature. However, the ideal properties of extruded product can only be achieved through a controlled process used to alter the microstructure to impart properties which benefit the working life of a component, which also known as heat treatment process. To that extent, this work ought to investigate the effect of extrusion temperature and ageing time on the hardness of the recycled aluminium chips. By employing Analysis of Variance (ANOVA) for full factorial design with centre point, a total of 11 runs were carried out randomly. Three dissimilar extrusion temperatures were used to obtain gear-shape billet. Extruded billets were cut and ground before entering the treatment phase at three different ageing times. Ageing time was found as the influential factor to affect the material hardness, rather than the extrusion temperature. Sufficient ageing time allows the impurity atoms to interfere the dislocation phenomena and yield great hardness. Yet, the extrusion temperatures still act to assist the bonding activities via interparticle diffusion transport matter.

Strain Hardening Behaviour and Its Effect on Properties of ZrB2 Reinforced Al Composite Prepared by Powder Metallurgy Technique

Science.gov (United States)

Kaku, Sai Mahesh Yadav; Khanra, Asit Kumar; Davidson, M. J.

2018-04-01

Strain hardening behaviour has significant effect on altering the properties of materials. In the present study, Al-ZrB2 metal matrix composites are made through powder metallurgy route. Incremental weight percentage (wt%) of ZrB2 (0, 2, 4 and 6 wt%) are added to Aluminium matrix to produce different composites. The homogenous powder mixture is compacted and pressurelessly sintered. Sintering of composites is performed over a range of 450-575 °C. The optimized sintered condition is observed at 550 °C for 1 h in controlled atmosphere (argon gas flow). The sintered compacts are strained in incremental steps in different levels up to failure. A visible crack on the bulge of the powder preform is considered as the failure. Composites are strain hardened up to failure. To evaluate the effect of temperature on strain hardening, strain hardening is carried out at different temperatures. Composites are densified with the extent of straining and hardness increases with the increase of strain. Hardness increase with the increase in temperature is maintained during strain hardening. To evaluate the corrosion behaviour of Al-ZrB2 composite, potentiodynamic polarization study are performed on the strained composites. Corrosion rate decrease with the extent of straining.

New aluminium-rich alkali slag matrix with clay minerals for immobilizing simulated radioactive Sr and Cs waste

International Nuclear Information System (INIS)

Qian Guangren; Sun, Darren Delai; Tay, Joo Hwa

2001-01-01

A new aluminium-rich alkali-activated slag matrix (M-AAS) with clay absorbents has been developed for immobilization of simulated radioactive Sr or Cs waste by introducing metakaolin, natural zeolite and NaOH-treated attapulgite clay minerals into alkali-activated slag matrix (AAS). The results revealed that the additions of metakaolin and clay absorbents into the cementitious matrixes would greatly enhance the distribution ratio, R d , of selective adsorption whether the matrix was OPC matrix or AAS matrix. The new immobilizing matrix M-AAS not only exhibited the strongest selective adsorption for both Sr and Cs ions, but also was characterized by lower porosity and small pore diameter so that it exhibited the lowest leaching rate. Hydration product analyses also demonstrated that (Na+Al)-substituted C-S-H(I) and self-generated zeolite were major hydration products in the M-AAS matrix, which provided this new immobilizing matrix with better selective adsorption on Sr and Cs and lower leaching rate

Corrosion fatigue of 2219-T87 aluminum alloy

Science.gov (United States)

Mcmillan, V. C.

1986-01-01

Corrosion fatigue studies were conducted on bare, chemical conversion coated, and anodized 2219-T87 aluminum alloy. These tests were performed using a rotating beam machine running at a velocity of 2500 rpm. The corrosive environments tested were distilled water, 100 ppm NaCl, and 3.5 percent NaCl. Results were compared to the endurance limit in air. An evaluation of the effect of protective coatings on corrosion fatigue was made by comparing the fatigue properties of specimens with coatings to those without.

Effect of inclusion of SiC particulates on the mechanical resistance behaviour of stir-cast AA6063/SiC composites

International Nuclear Information System (INIS)

Balasubramanian, I.; Maheswaran, R.

2015-01-01

Highlights: • AA6063/SiC composites with different weight percent are stir cast. • Resistance properties against indentation, stretching force and sliding force are studied. • Increase in initiation of cleavage facets and reduces the tensile strength for 15% SiC. • Transition from micro ploughing to micro cutting wear mechanism is less due to SiC inclusion. - Abstract: This study investigates the mechanical resistance behaviour of AA6063 particulate composites with the inclusion of micron-sized silicon carbide (SiC) particles with different weight percentages in an AA6063 aluminium matrix. AA6063/SiC particulate composites containing 0, 5, 10, and 15 weight percent of SiC particles were produced by stir casting. Standard mechanical tests were conducted on the composite plates, and the mechanical resistance to indentation, tensile force and sliding force are evaluated. It has been observed that upon addition of SiC particles, the resistance against indentation is increased and the resistance against tensile force is initially increased and then decreased. Furthermore, using scanning electron microscopy (SEM), the fracture appearance of the broken specimen subjected to tensile force and morphological changes in the surface subjected to sliding force are analysed. The SEM images reveal that the addition of SiC particles in the AA6063 aluminium matrix initiates more cleavage facets. This leads to brittle fracture in the specimen subjected to tensile forces and less transition from material displacement to material removal in the specimen subjected to sliding forces

Alloys of uranium and aluminium with low aluminium content; Alliages uranium-aluminium a faible teneur en aluminium

Energy Technology Data Exchange (ETDEWEB)

Cabane, G; Englander, M; Lehmann, J [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

1955-07-01

Uranium, as obtained after spinning in phase {gamma}, presents an heterogeneous structure with large size grains. The anisotropic structure of the metal leads to an important buckling and surface distortion of the fuel slug which is incompatible with its tubular cladding for nuclear fuel uses. Different treatments have been made to obtain an isotropic structure presenting high thermal stability (laminating, hammering and spinning in phase {alpha}) without success. Alloys of uranium and aluminium with low aluminium content present important advantage in respect of non allied uranium. The introduction of aluminium in the form of intermetallic compound (UAl{sub 2}) gives a better resistance to thermal fatigue. Alloys obtained from raw casting present an improved buckling and surface distortion in respect of pure uranium. This improvement is obtained with uranium containing between 0,15 and 0,5 % of aluminium. An even more improvement in thermal stability is obtained by thermal treatments of these alloys. These new characteristics are explained by the fine dispersion of the UAl{sub 2} particles in uranium. The results after treatments obtained from an alloy slug containing 0,4 % of aluminium show no buckling or surface distortion and no elongation. (M.P.)

Effect of Refiner Addition Level on Zirconium-Containing Aluminium Alloys

International Nuclear Information System (INIS)

Jaradeh, M M R; Carlberg, T

2012-01-01

It is well known that in aluminium alloys containing Zr, grain refiner additions do not function as desired, producing an effect often referred to as nuclei poisoning. This paper investigates the structure of direct chill-cast ingots of commercial AA3003 aluminium alloys, with and without Zr, at various addition levels of Al5Ti1B master alloy. In Bridgman experiments simulating ingot solidification, Zr-containing alloys were studied after the addition of various amounts of Ti. It could be demonstrated, in both ingot casting and simulation experiments, that Zr poisoning can be compensated for by adding more Ti and/or Al5Ti1B. The results confirm better refinement behaviour with the addition of Ti + B than of only Ti. The various combinations of Zr and Ti also influenced the formation of AlFeMn phases, and the precipitation of large Al 6 (Mn,Fe) particles was revealed. AlZrTiSi intermetallic compounds were also detected.

Effect of Refiner Addition Level on Zirconium-Containing Aluminium Alloys

Science.gov (United States)

Jaradeh, M. M. R.; Carlberg, T.

2012-01-01

It is well known that in aluminium alloys containing Zr, grain refiner additions do not function as desired, producing an effect often referred to as nuclei poisoning. This paper investigates the structure of direct chill-cast ingots of commercial AA3003 aluminium alloys, with and without Zr, at various addition levels of Al5Ti1B master alloy. In Bridgman experiments simulating ingot solidification, Zr-containing alloys were studied after the addition of various amounts of Ti. It could be demonstrated, in both ingot casting and simulation experiments, that Zr poisoning can be compensated for by adding more Ti and/or Al5Ti1B. The results confirm better refinement behaviour with the addition of Ti + B than of only Ti. The various combinations of Zr and Ti also influenced the formation of AlFeMn phases, and the precipitation of large Al6(Mn,Fe) particles was revealed. AlZrTiSi intermetallic compounds were also detected.

Rows of Dislocation Loops in Aluminium Irradiated by Aluminium Ions

DEFF Research Database (Denmark)

Henriksen, L.; Johansen, A.; Koch, J.

1967-01-01

Single-crystal aluminium specimens, irradiated with 50-keV aluminium ions, contain dislocation loops that are arranged in regular rows along <110 > directions. ©1967 The American Institute of Physics......Single-crystal aluminium specimens, irradiated with 50-keV aluminium ions, contain dislocation loops that are arranged in regular rows along directions. ©1967 The American Institute of Physics...

Role of acidic chemistries in steam treatment of aluminium alloys

DEFF Research Database (Denmark)

Din, Rameez Ud; Jellesen, Morten Stendahl; Ambat, Rajan

2015-01-01

The effect of acidic chemistry on the accelerated growth of oxide on aluminium alloys Peraluman 706TM and AA6060 under exposure to high temperature steam was investigated. Studied chemistries were based on citrates and phosphates. Results showed that the presence of citrate and phosphate anions...... initiate doxide growth at the intermetallic particles while growth and corrosion performance of oxide was found tobe a function of anions type and their concentration. Further, steam treatment with phosphates exhibited better performance under acetic acid salt spray and filiform corrosion test whereas...

Influence of Extrusion Temperature on the Aging Behavior and Mechanical Properties of an AA6060 Aluminum Alloy

Directory of Open Access Journals (Sweden)

Nadja Berndt

2018-01-01

Full Text Available Processing of AA6060 aluminum alloys for semi-products usually includes hot extrusion with subsequent artificial aging for several hours. Processing below the recrystallization temperature allows for an increased strength at a significantly reduced annealing time by combining strain hardening and precipitation hardening. In this study, we investigate the potential of cold and warm extrusion as alternative processing routes for high strength aluminum semi-products. Cast billets of the age hardening aluminum alloy AA6060 were solution annealed and then extruded at room temperature, 120 or 170 °C, followed by an aging treatment. Electron microscopy and mechanical testing were performed on the as-extruded as well as the annealed materials to characterize the resulting microstructural features and mechanical properties. All of the extruded profiles exhibit similar, strongly graded microstructures. The strain gradients and the varying extrusion temperatures lead to different stages of dynamic precipitation in the as-extruded materials, which significantly alter the subsequent aging behavior and mechanical properties. The experimental results demonstrate that extrusion below recrystallization temperature allows for high strength at a massively reduced aging time due to dynamic precipitation and/or accelerated precipitation kinetics. The highest strength and ductility were achieved by extrusion at 120 °C and subsequent short-time aging.

Microhardness and Strain Field Characterization of Self-Reacting Friction Stir and Plug Welds of Dissimilar Aluminum Alloys

Science.gov (United States)

Horton, Karla Renee

2011-01-01

Friction stir welding (FSW) is a solid state welding process with potential advantages for aerospace and automotive industries dealing with light alloys. Self-reacting friction stir welding (SR-FSW) is one variation of the FSW process being developed at the National Aeronautics and Space Administration (NASA) for use in the fabrication of propellant tanks. Friction plug welding is used to seal the exit hole that remains in a circumferential SR-FSW. This work reports on material properties and strain patterns developed in a SR-FSW with a friction plug weld. Specifically, this study examines the behavior of a SR-FSW formed between an AA 2014-T6 plate on the advancing side and an AA 2219-T87 plate on the retreating side and a SR-FSW (AA 2014-T6 to AA 2219-T87) with a 2219-T87 plug weld. This study presents the results of a characterization of the micro-hardness, joint strength, and strain field characterization of SR-FSW and FPW joints tested at room temperature and cryogenic temperatures.

Scanning Kelvin probe force microscopy as a means of predicting the electrochemical characteristics of the surface of a modified AA4xxx/AA3xxx (Al alloys) brazing sheet

International Nuclear Information System (INIS)

Afshar, F. Norouzi; Wit, J.H.W. de; Terryn, H.; Mol, J.M.C.

2013-01-01

Highlights: ► Macro- and micro-electrochemical surface properties of an aluminium brazing sheet were investigated. ► Electrochemical surface properties before and after brazing were studied and compared. ► Scanning Kelvin probe force microscopy and potentiodynamic polarization measurements were performed. ► The electrochemical responses were correlated to the pre- and post-brazing treatment microstructure. -- Abstract: Macro- and micro-electrochemical properties of clad and core surfaces of a modified AA4xxx/AA3xxx brazing sheet material, before and after brazing, have been evaluated and compared. By scanning Kelvin probe force microscopy (SKPFM), the Volta potential distribution over the brazed and non-brazed clad surfaces was measured. The changes in the Volta potential maps were correlated to the macro-electrochemical responses of the surfaces and the microstructural features that evolve as a result of brazing. By performing potentiodynamic polarization experiments and microscopic analysis of the corroded surfaces and cross sections, the suitability of SKPFM analysis for corrosion performance prediction of the aluminium brazing sheet material in a sea water acidified accelerated test (SWAAT) environment was confirmed. Considering the purity of Si phase in the structures of both brazed and non-brazed material, it is suggested that Si can be applied as a reliable local reference in both structures to compare the changes in Volta potential differences as the result of different heat treatments of aluminium brazing sheet. Increasing the copper content of the re-solidified clad material as a result of brazing treatment was found to increase the Volta potential of the matrix which in turn reduces the cathodic protection power of the re-solidified clad material towards the core material

Content and bioaccessibility of aluminium in duplicate diets from southern Spain.

Science.gov (United States)

Cabrera-Vique, Carmen; Mesías, Marta

2013-08-01

Aluminium is found naturally in foods and beverages, but levels increase notably during processing, packaging, storage, and cooking, as a consequence of its presence in food additives and the wide use of aluminium utensils and vessels. Dietary intake of Al was estimated in 2 population groups in southern Spain (families and university students) in a duplicate diet sampling study. Diets were sampled for 7 consecutive days, and Al was determined in acid-mineralized samples with electrothermal atomization-atomic absorption spectrometry (ETA-AAS). Mean values for Al intake were 2.93 and 1.01 mg/d in families and students, respectively, ranging from 0.12 to 10.00 mg/d. Assuming an average adult weight of 60 kg, the mean dietary exposures to aluminium were 0.34 and 0.12 mg/kg body weight/week in these groups, which amounted to 17% and 6% of the 2 mg/kg body weight estimated as the tolerable weekly intake by the Joint FAO/WHO Expert Committee on Food Additives. Bioaccessibility of dietary Al tested with in vitro studies ranged from 0.30 to 17.26% (absorbable fraction). The highest aluminium intakes were observed in subjects consuming diets with a low adherence to the Mediterranean diet, which were associated to high consumption of processed and canned food. On the contrary, subjects consuming diets with a high adherence to the Mediterranean diet patterns showed the lowest Al intakes. The present findings are useful for giving both a reliable estimate of total aluminium dietary intake and tolerable intake levels according to usual dietary habits. © 2013 Institute of Food Technologists®

Microstructure, local and global mechanical properties of friction stir welds in aluminium alloy 6005A-T6

International Nuclear Information System (INIS)

Simar, A.; Brechet, Y.; Meester, B. de; Denquin, A.; Pardoen, T.

2008-01-01

The effect of the welding speed on the microstructure, local and overall mechanical properties of friction stir welded joints has been investigated in the aluminium alloy 6005A-T6. The fine hardening precipitation within the heat-affected zone has been characterized by differential scanning calorimetry (DSC) and transmission electron microscopy (TEM). Post-welding heat treatments have been applied to obtain indications on the level of solid solution supersaturation in the as welded state. The local mechanical behaviour was determined using thin specimens extracted from various regions of the weld. The overall properties were measured on samples cut perpendicular to the weld. Specific attention was devoted to the relationship between the local microstructure and local hardening properties in the weakest region, which govern the overall strength and ductility of the welds

A thermal comparator sensor for measuring autogenous deformation in hardening Portland cement paste

DEFF Research Database (Denmark)

Østergaard, Thomas; Jensen, Ole Mejlhede

2003-01-01

This paper describes a simple and accurate experimental device specially developed to measure autogenous deformation in hardening cement-based materials. The measuring system consists of a so-called thermal comparator sensor and a modular thermostatically controlled system. The operating principle...... of the thermal comparator is based on thermal expansion of aluminium. A particular characteristic of the measuring system is the fixation of the thermal comparator sensor to the deforming specimen. The modular system ensures effective thermostatic control of the hydrating cement paste samples. The technique...... allows continuous measurement with high accuracy of the linear deformation as well as determination of the activation energy of autogenous deformation....

Optimization of the composition and structure of heat-resistant casting aluminium alloys with additions of cerium, iron, nickel and zirconium

International Nuclear Information System (INIS)

Belov, N.A.; Lavrishchev, Yu.V.

2000-01-01

A study is made of the effect of composition and structure on mechanical properties of cast alloys of the Al-Ce-Ni-Fe-Zr system in which binary and ternary eutectics with participation of low alloyed aluminium solid solution and Al 4 Ce, Al 3 Ni and Al 9 FeNi phases are crystallized. It is found that microhardness of eutectics is heavily dependent on the volume fraction of aluminides and their dispersivity. It was shown that essential hardening of aluminium matrix can be achieved at the cost of zirconium additive in quantity of 0.6 % when using two-stage manufacturing operation. Experimental compositions of Al-10 % Ce-5% Ni-0.6 % Zr and Al-1.5 % Fe-1.5 % Ni-0.6 % Zr on the basis of ternary and binary eutectics respectively as billets essentially exceed industrial heat-resistant cast aluminium alloys AK12MMgN and AM5 as to a set of room and high-temperature mechanical properties and hot brittleness index [ru

A comparative study of leaves extracts for corrosion inhibition effect on aluminium alloy in alkaline medium

Directory of Open Access Journals (Sweden)

Namrata Chaubey

2017-12-01

Full Text Available This paper deals with the comparative inhibition study of some plants leaves extract namely Cannabis sativa (CS, Rauwolfia serpentina (RS, Cymbopogon citratus (CC, Annona squamosa (AS and Adhatoda vasica (AV on the corrosion of aluminium alloy (AA in 1 M NaOH. The corrosion tests were performance by using gravimetric, electrochemical impedance spectroscopy (EIS, potentiodynamic polarization and linear polarization resistance (LPR techniques. RS showed maximum inhibition efficiency (η%, 97% at 0.2 g L−1. Potentiodynamic polarization curves justified that all the inhibitors are mixed-type. Surface morphology of AA is carried by scanning electron microscopy (SEM and atomic force microscopy (AFM.

The secondary hardening phenomenon in strain-hardened MP35N alloy

International Nuclear Information System (INIS)

Asgari, S.; El-Danaf, E.; Shaji, E.; Kalidindi, S.R.; Doherty, R.D.

1998-01-01

Mechanical testing and microscopy techniques were used to investigate the influence of aging on the structure and strengthening of MP35N alloy. It was confirmed that aging the deformed material at 600 C for 4 h provided additional strengthening, here referred to as secondary hardening, in addition to the primary strain hardening. The secondary hardening phenomenon was shown to be distinctly different from typical age hardening processes in that it only occurred in material deformed beyond a certain cold work level. At moderate strains, aging caused a shift in the entire stress-strain curve of the annealed material to higher stresses while at high strains, it produced shear localization and limited work softening. The secondary hardening increment was also found to be grain size dependent. The magnitude of the secondary hardening appeared to be controlled by the flow stress in the strain hardened material. A model is proposed to explain the observations and is supported by direct experimental evidence. The model is based on formation of h.c.p. nuclei through the Suzuki mechanism, that is segregation of solute atoms to stacking faults, on aging the strain hardened material. The h.c.p. precipitates appear to thicken only in the presence of high dislocation density produced by prior cold work

Simultaneous surface engineering and bulk hardening of precipitation hardening stainless steel

DEFF Research Database (Denmark)

Frandsen, Rasmus Berg; Christiansen, Thomas; Somers, Marcel A. J.

2006-01-01

This article addresses simultaneous bulk precipitation hardening and low temperature surface engineering of two commercial precipitation hardening stainless steels: Sandvik Nanoflex® and Uddeholm Corrax®. Surface engineering comprised gaseous nitriding or gaseous carburising. Microstructural....... The duration and temperature of the nitriding/carburising surface hardening treatment can be chosen in agreement with the thermal treatment for obtaining optimal bulk hardness in the precipitation hardening stainless steel....... characterisation of the cases developed included X-ray diffraction analysis, reflected light microscopy and micro-hardness testing. It was found that the incorporation of nitrogen or carbon resulted in a hardened case consisting of a combination of (tetragonal) martensite and expanded (cubic) austenite...

Hot Press as a Sustainable Direct Recycling Technique of Aluminium: Mechanical Properties and Surface Integrity.

Science.gov (United States)

Yusuf, Nur Kamilah; Lajis, Mohd Amri; Ahmad, Azlan

2017-08-03

Meltless recycling technique has been utilized to overcome the lack of primary resources, focusing on reducing the usage of energy and materials. Hot press was proposed as a novel direct recycling technique which results in astoundingly low energy usage in contrast with conventional recycling. The aim of this study is to prove the technical feasibility of this approach by characterizing the recycled samples. For this purpose, AA6061 aluminium chips were recycled by utilizing hot press process under various operating temperature (T s = 430, 480, and 530 °C) and holding times (t s = 60, 90, and 120 min). The maximum mechanical properties of recycled chip are Ultimate tensile strength (UTS) = 266.78 MPa, Elongation to failure (ETF) = 16.129%, while, for surface integrity of the chips, the calculated microhardness is 81.744 HV, exhibited at T s = 530 °C and t s = 120 min. It is comparable to theoretical AA6061 T4-temper where maximum UTS and microhardness is increased up to 9.27% and 20.48%, respectively. As the desired mechanical properties of forgings can only be obtained by means of a final heat treatment, T5-temper, aging after forging process was employed. Heat treated recycled billet AA6061 (T5-temper) are considered comparable with as-received AA6061 T6, where the value of microhardness (98.649 HV) at 175 °C and 120 min of aging condition was revealed to be greater than 3.18%. Although it is quite early to put a base mainly on the observations in experimental settings, the potential for significant improvement offered by the direct recycling methods for production aluminium scrap can be clearly demonstrated. This overtures perspectives for industrial development of solid state recycling processes as environmentally benign alternatives of current melting based practices.

Multi objective genetic algorithm to optimize the local heat treatment of a hardenable aluminum alloy

Science.gov (United States)

Piccininni, A.; Palumbo, G.; Franco, A. Lo; Sorgente, D.; Tricarico, L.; Russello, G.

2018-05-01

The continuous research for lightweight components for transport applications to reduce the harmful emissions drives the attention to the light alloys as in the case of Aluminium (Al) alloys, capable to combine low density with high values of the strength-to-weight ratio. Such advantages are partially counterbalanced by the poor formability at room temperature. A viable solution is to adopt a localized heat treatment by laser of the blank before the forming process to obtain a tailored distribution of material properties so that the blank can be formed at room temperature by means of conventional press machines. Such an approach has been extensively investigated for age hardenable alloys, but in the present work the attention is focused on the 5000 series; in particular, the optimization of the deep drawing process of the alloy AA5754 H32 is proposed through a numerical/experimental approach. A preliminary investigation was necessary to correctly tune the laser parameters (focus length, spot dimension) to effectively obtain the annealed state. Optimal process parameters were then obtained coupling a 2D FE model with an optimization platform managed by a multi-objective genetic algorithm. The optimal solution (i.e. able to maximize the LDR) in terms of blankholder force and extent of the annealed region was thus evaluated and validated through experimental trials. A good matching between experimental and numerical results was found. The optimal solution allowed to obtain an LDR of the locally heat treated blank larger than the one of the material either in the wrought condition (H32) either in the annealed condition (H111).

Investigation of aluminium-rich alloy system of aluminium-strontium-silicium

International Nuclear Information System (INIS)

Ganiev, I.N.; Vakhobov, A.B.; Dzhuraev, T.D.; Alidzhanov, F.N.

1976-01-01

An area of the solid solution based on aluminium was studied, and the surface was plotted of the liquidus adjoining the apex of the aluminium corner of the strontium-aluminium-silicon system. The investigation was carried out by microstructure and differential thermal analyses and by the measurement of the microhardness of the component phases. A combined solubility of silicon and strontium in aluminium was studied along three radial sections at Sr-to-Si ratios of 1/2, 1/1 and 2/1. The relationships of ''composition vs. Microhardness'', obtained in these sections, made it possible to define the boundaries of the phase regions in the aluminium corner of the strontium-aluminium-silicon system at 500 deg C. The greatest solubility is that along the Al-SrAl 2 Si 2 section at a Sr/Si ratio of 1/2. A further increase in the content of strontium brings about a drop in the solubility of silicon in solid aluminium. The projection of the liquidus surface of the strontium-aluminium-silicon system, rich in aluminium, includes four surfaces of primary crystallization: α-Al, SrAl 4 , SrAl 2 Si 2 and Si. The system comprises a section of Al-SrAl 2 Si 2 representing a quasibinary system of an eutectic type. The eutectic reaction takes place at a temperature of 640 deg C. The quasibinary Al-SrAl 2 Si 2 section divides the aluminium corner of the Sr-Al-Si system into two independent systems Al-SrAl 4 -SrAl 2 Si 2 and Al-Si-SrAl 2 Si 2 of an eutectic type

Numerical modeling of AA2024-T3 friction stir welding process for residual stress evaluation, including softening effects

DEFF Research Database (Denmark)

Sonne, Mads Rostgaard; Carlone, Pierpaolo; Palazzo, Gaetano S.

2014-01-01

In the present paper, a numerical finite element model of the precipitation hardenable AA2024-T3 aluminum alloy, consisting of a heat transfer analysis based on the Thermal Pseudo Mechanical model for heat generation, and a sequentially coupled quasi-static stress analysis is proposed. Metallurgi...

Impact of as-cast structure on structure and properties of twin-roll cast AA8006 alloy

Energy Technology Data Exchange (ETDEWEB)

Slamova, M.; Ocenasek, V. [Vyzkumny Ustav Kovu, Panenske Brezany (Czechoslovakia); Juricek, Z.

2000-07-01

Sheet production by twin-roll casting (TRC) process is a well established practice in the aluminium industry because it offers several advantages in comparison with DC casting and hot rolling, esp. lower production and investment costs. Thin strips exhibiting a combination of good strength and high ductility are required for various applications and for this reason alloys with higher Fe and Mn content such as AA 8006 displace AA 1xxx or AA 8011 alloys. However, TRC of AA 8006 strips involves several problems, e.g. casting conditions and subsequent treatment procedures need fine tuning. The results of an investigation of the effect of casting conditions on structure and properties of AA 8006 strips are presented. The influence of casting speed, grain refiner addition, molten metal level in the tundish, tip setback and roll separating force was investigated. The impact of imperfect as-cast structure on structure and properties of thin strips in H22 and O tempers was evaluated and compared with strips from good as-cast material. (orig.)

A hardenability test proposal

Energy Technology Data Exchange (ETDEWEB)

Murthy, N.V.S.N. [Ingersoll-Rand (I) Ltd., Bangalore (India)

1996-12-31

A new approach for hardenability evaluation and its application to heat treatable steels will be discussed. This will include an overview and deficiencies of the current methods and discussion on the necessity for a new approach. Hardenability terminology will be expanded to avoid ambiguity and over-simplification as encountered with the current system. A new hardenability definition is proposed. Hardenability specification methods are simplified and rationalized. The new hardenability evaluation system proposed here utilizes a test specimen with varying diameter as an alternative to the cylindrical Jominy hardenability test specimen and is readily applicable to the evaluation of a wide variety of steels with different cross-section sizes.

Aluminium in human sweat.

Science.gov (United States)

Minshall, Clare; Nadal, Jodie; Exley, Christopher

2014-01-01

It is of burgeoning importance that the human body burden of aluminium is understood and is measured. There are surprisingly few data to describe human excretion of systemic aluminium and almost no reliable data which relate to aluminium in sweat. We have measured the aluminium content of sweat in 20 healthy volunteers following mild exercise. The concentration of aluminium ranged from 329 to 5329μg/L. These data equate to a daily excretion of between 234 and 7192μg aluminium and they strongly suggest that perspiration is the major route of excretion of systemic aluminium in humans. Copyright © 2013 Elsevier GmbH. All rights reserved.

Microstructure and Mechanical Properties of Three-Layer TIG-Welded 2219 Aluminum Alloys with Dissimilar Heat Treatments

Science.gov (United States)

Zhang, Dengkui; Li, Quan; Zhao, Yue; Liu, Xianli; Song, Jianling; Wang, Guoqing; Wu, Aiping

2018-05-01

2219-C10S and 2219-CYS aluminum alloys are 2219 aluminum alloys with different heat treatment processes, and they have been widely used in the aerospace industry. In the present study, 2219-C10S and 2219-CYS aluminum alloys were butt-welded by three-layer tungsten inert gas arc welding (with the welding center of the third layer shifted toward the CYS side), and the microstructure characteristics and mechanical properties of the welded joint were investigated. The lamellar θ' phases, the bulk or rod θ phases, and the coarse rod-shaped or pancake-shaped Al-Cu-Fe-Mn phases coexisted in the two aluminum alloys. The Cu content of the α-Al matrix and the distribution of eutectic structures of different welding layers in the weld zone (WZ) were varied, implying that the segregation degrees of the Cu element were different due to the different welding thermal cycles in different welding layers. The microhardness values of the CYS side were much higher than those of the C10S side in each region on both sides of the joint. The tensile test deformation was concentrated mainly in the regions of WZ and the over aged zone (OAZ), where the microhardness values were relatively low. The main deformation concentrated region was transferred from the CYS side to the C10S side with the increase in the tensile load during the tensile test. The fracture behavior of the tensile test showed that the macroscopic crack initiated near the front weld toe had gone through the crack blunt region, the shear fracture region of the partially melted zone (PMZ), and the shear fracture region of OAZ. Meanwhile, the fracture characteristics gradually evolved from brittle to ductile. The concentrated stress and the dense eutectic structure in the region near the front weld toe of the C10S side contributed to the fracture of the joint. The shift of the welding center of the third layer to the CYS side resulted in two effects: (i) the microhardness values from the middle layer to the top layer in the

Comparison of Thermal Creep Strain Calculation Results Using Time Hardening and Strain Hardening Rules

International Nuclear Information System (INIS)

Kim, Junehyung; Cheon, Jinsik; Lee, Byoungoon; Lee, Chanbock

2014-01-01

One of the design criteria for the fuel rod in PGSFR is the thermal creep strain of the cladding, because the cladding is exposed to a high temperature for a long time during reactor operation period. In general, there are two kind of calculation scheme for thermal creep strain: time hardening and strain hardening rules. In this work, thermal creep strain calculation results for HT9 cladding by using time hardening and strain hardening rules are compared by employing KAERI's current metallic fuel performance analysis code, MACSIS. Also, thermal creep strain calculation results by using ANL's metallic fuel performance analysis code, LIFE-METAL which adopts strain hardening rule are compared with those by using MACSIS. Thermal creep strain calculation results for HT9 cladding by using time hardening and strain hardening rules were compared by employing KAERI's current metallic fuel performance analysis code, MACSIS. Also, thermal creep strain calculation results by using ANL's metallic fuel performance analysis code, LIFE-METAL which adopts strain hardening rule were compared with those by using MACSIS. Tertiary creep started earlier in time hardening rule than in strain hardening rule. Also, calculation results by MACSIS with strain hardening and those obtained by using LIFE-METAL were almost identical to each other

Integrated FEM-DBEM simulation of crack propagation in AA2024-T3 FSW butt joints considering manufacturing effects

DEFF Research Database (Denmark)

Sonne, Mads Rostgaard; Carlone, P.; Citarella, R.

2015-01-01

This paper deals with a numerical and experimental investigation on the influence of residual stresses on fatigue crack growth in AA2024-T3 friction stir welded butt joints. An integrated FEM-DBEM procedure for the simulation of crack propagation is proposed and discussed. A numerical FEM model...... of the welding process of precipitation hardenable AA2024-T3 aluminum alloy is employed to infer the process induced residual stress field. The reliability of the FEM simulations with respect to the induced residual stresses is assessed comparing numerical outcomes with experimental data obtained by means...

Radiation-hardenable diluents for radiation-hardenable compositions

International Nuclear Information System (INIS)

Schuster, K.E.; Rosenkranz, H.J.; Furh, K.; Ruedolph, H.

1979-01-01

Radiation-crosslinkable diluents for radiation-hardenable compositions (binders) consisting of a mixture of triacrylates of a reaction product of trimethylol propane and ethylene oxide with an average degree of ethoxylation of from 2.5 to 4 are described. The ethoxylated trimethylol propane is substantially free from trimethylol propane and has the following distribution: 4 to 5% by weight of monoethoxylation product, 14 to 16% by weight of diethoxylation product, 20 to 30% by weight of triethoxylation product, 20 to 30% by weight of tetraethoxylation product, 16 to 18% by weight of pentaethoxylation product, and 6 to 8% by weight of hexaethoxylation product. The diluents effectively reduce the viscosity of radiation-hardenable compositions and do not have any adverse effect upon their reactivity or upon the properties of the resulting hardened products

Numerical modelling in friction lap joining of aluminium alloy and carbon-fiber-reinforced-plastic sheets

Science.gov (United States)

Das, A.; Bang, H. S.; Bang, H. S.

2018-05-01

Multi-material combinations of aluminium alloy and carbon-fiber-reinforced-plastics (CFRP) have gained attention in automotive and aerospace industries to enhance fuel efficiency and strength-to-weight ratio of components. Various limitations of laser beam welding, adhesive bonding and mechanical fasteners make these processes inefficient to join metal and CFRP sheets. Friction lap joining is an alternative choice for the same. Comprehensive studies in friction lap joining of aluminium to CFRP sheets are essential and scare in the literature. The present work reports a combined theoretical and experimental study in joining of AA5052 and CFRP sheets using friction lap joining process. A three-dimensional finite element based heat transfer model is developed to compute the temperature fields and thermal cycles. The computed results are validated extensively with the corresponding experimentally measured results.

Influence of Cooling Condition on the Performance of Grinding Hardened Layer in Grind-hardening

Science.gov (United States)

Wang, G. C.; Chen, J.; Xu, G. Y.; Li, X.

2018-02-01

45# steel was grinded and hardened on a surface grinding machine to study the effect of three different cooling media, including emulsion, dry air and liquid nitrogen, on the microstructure and properties of the hardened layer. The results show that the microstructure of material surface hardened with emulsion is pearlite and no hardened layer. The surface roughness is small and the residual stress is compressive stress. With cooling condition of liquid nitrogen and dry air, the specimen surface are hardened, the organization is martensite, the surface roughness is also not changed, but high hardness of hardened layer and surface compressive stress were obtained when grinding using liquid nitrogen. The deeper hardened layer grinded with dry air was obtained and surface residual stress is tensile stress. This study provides an experimental basis for choosing the appropriate cooling mode to effectively control the performance of grinding hardened layer.

Studies of the AA2519 Alloy Hot Rolling Process and Cladding with EN AW-1050A Alloy

Directory of Open Access Journals (Sweden)

Płonka B.

2016-03-01

Full Text Available The objective of the study was to determine the feasibility of plastic forming by hot rolling of the AA2519 aluminium alloy sheets and cladding these sheets with a layer of the EN AW-1050A alloy. Numerous hot-rolling tests were carried out on the slab ingots to define the parameters of the AA2519 alloy rolling process. It has been established that rolling of the AA2519 alloy should be carried out in the temperature range of 400-440°C. Depending on the required final thickness of the sheet metal, appropriate thickness of the EN AW-1050A alloy sheet, used as a cladding layer, was selected. As a next step, structure and mechanical properties of the resulting AA2519 alloy sheets clad with EN AW-1050A alloy was examined. The thickness of the coating layer was established at 0,3÷0,5mm. Studies covered alloy grain size and the core alloy-cladding material bond strength.

Effect of pin tool design on the material flow of dissimilar AA7075-AA6061 friction stir welds

Science.gov (United States)

Hasan, Mohammed M.; Ishak, M.; Rejab, M. R. M.

2017-10-01

Tool design is the most influential aspect in the friction stir welding (FSW) technology. Influence of pin tool geometry on material flow pattern are studied in this work during the FSW of dissimilar AA7075 and AA6061 aluminium alloys. Three truncated pin tool profiles (threaded, threaded with single flat, and unthreaded with single flat) were used to prepare the weldments. The workpieces were joined using a custom-made clamping system under 1100 rpm of spindle speed, 300 mm/min of traverse rate and 3° of tilt angle. The metallographic analysis showed that defect-free welds can be produced using the three pin tools with significant changes in the mixing stir zone structure. The results declared that the introducing of the flat on the cone of the probe deviates the pattern of the onion rings without changing the chemical composition of the created layers. This in turn improves the hardness distribution and tensile strength of the welded joint. It was also noted that both heat affected zone (HAZ) and thermal-mechanical affected zone (TMAZ) are similar in composition to their corresponding base materials (BM).

Strain rate effects on mechanical properties in tension of aluminium alloys used in armour applications

Science.gov (United States)

Cadoni, E.; Dotta, M.; Forni, D.; Bianchi, S.; Kaufmann, H.

2012-08-01

The mechanical properties in tension of two aluminium alloys (AA5059-H131 and AA7039-T651) used in armour applications were determined from tests carried out over a wide range of strain-rates on round specimens. The experimental research was developed in the DynaMat laboratory of the University of Applied Sciences of Southern Switzerland. The target strain rates were set at the following four levels: 10-3, 30, 300 and 1000s-1. The quasi-static tests were performed with a universal electromechanical machine, whereas a hydro-pneumatic machine and a Split Hopkinson Tensile Bar apparatus were used for medium and high strain-rates respectively. The required parameters by the Johnson-Cook constitutive law were also determined.

Fatigue crack growth prediction in 2xxx AA with friction stir weld HAZ properties

Directory of Open Access Journals (Sweden)

A. Tzamtzis

2016-02-01

Full Text Available An analytical model is developed to predict fatigue crack propagation rate under mode I loading in 2024 aluminum alloy with FSW HAZ material characteristics. Simulation of the HAZ local properties in parent 2024 AA was performed with overaging using specific heat treatment conditions. The model considers local cyclic hardening behavior in the HAZ to analyze crack growth. For the evaluation of the model, the analytical results have been compared with experimental fatigue crack growth on overaged 2024 alloy simulating material behavior at different positions within the HAZ. The analytical results showed that cyclic hardening at the crack tip can be used successfully with the model to predict FCG in a material at overaged condition associated with a location in the FSW HAZ.

Human exposure to aluminium.

Science.gov (United States)

Exley, Christopher

2013-10-01

Human activities have circumvented the efficient geochemical cycling of aluminium within the lithosphere and therewith opened a door, which was previously only ajar, onto the biotic cycle to instigate and promote the accumulation of aluminium in biota and especially humans. Neither these relatively recent activities nor the entry of aluminium into the living cycle are showing any signs of abating and it is thus now imperative that we understand as fully as possible how humans are exposed to aluminium and the future consequences of a burgeoning exposure and body burden. The aluminium age is upon us and there is now an urgent need to understand how to live safely and effectively with aluminium.

Determination of Aluminium Content in Aluminium Hydroxide Formulation by FT-NIR Transmittance Spectroscopy

DEFF Research Database (Denmark)

Lai, Xuxin; Zheng, Yiwu; Søndergaard, Ib

2007-01-01

A method for determining the aluminium content of an aluminium hydroxide suspension using near infrared (NIR) transmittance spectroscopy has been developed. Inductively coupled plasma-atomic emission spectroscopy (ICP-AES) was used as reference method. The factors influencing the NIR analysis...... aluminium content in aluminium hydroxide suspension. (c) 2007 Elsevier Ltd. All rights reserved....

Development of an alternative route for recycling AA2050 aluminum alloy by powder metallurgy; Desenvolvimento de uma rota alternativa para reciclagem da liga de aluminio AA2050 via metalurgia do po

Energy Technology Data Exchange (ETDEWEB)

Guido, V.; Oliveira, A.C. de; Travessa, D.N.; Cardoso, K.R., E-mail: vane.guid@gmail.com [Universidade Federal de Sao Paulo (USP), Sao Jose dos Campos, SP (Brazil). Instituto de Ciencia e Tecnologia

2014-07-01

This paper presents an alternative solid state route to recycling AA2050 aeronautical aluminium alloy chips. The first stage in the recycling process, reported in this work, is the obtainment of the alloy powder by high energy ball milling to subsequent cold pressing and hot extrusion. The process started with the cleaning of chips with the aim of contaminant removing from machining process and transport, followed by the high energy ball milling to result in the AA2050 alloy powder. The powder obtained was characterized by laser size particle analysis, scanning electron microscopy (SEM), X-Ray diffraction (DRX) and inductively coupled plasma atomic emission spectroscopy (ICP-AES). The results show the feasibility of obtaining a powder having appropriate particle size and chemical composition in accordance with the specification for alloy. (author)

A comparative study on low cycle fatigue behaviour of nano and micro Al2O3 reinforced AA2014 particulate hybrid composites

Directory of Open Access Journals (Sweden)

R. Senthilkumar

2015-01-01

Full Text Available Aluminium based metal matrix composites have drawn more attraction due to their improved properties in structural applications for the past two decades. The fatigue behaviour of composite materials needs to be studied for their structural applications. In this work, powder metallurgy based aluminium (AA2014 alloy reinforced with micro and nano-sized alumina particles were fabricated and consolidated with the hot extrusion process. The evaluation of mechanical properties in the extruded composite was carried out. This composite was subjected to low cycle fatigue test with a constant strain rate. Scanning Electron Microscope (SEM and Transmission Electron Microscope (TEM images were used to evaluate the fatigue behaviour of aluminium-nano composite samples. Enhanced mechanical properties were exhibited by the nano alumina reinforced aluminium composites, when compared to the micron sized alumina reinforced composites. The failure cycle is observed to be higher for the nano alumina reinforced composites when compared with micron sized alumina composites due to a lower order of induced plastic strain.

Rupture intergranulaire induite par l'hydrogène dans les alliages d'aluminium-magnésium

OpenAIRE

Pouillier , Édouard

2011-01-01

Aluminium alloys that are strengthened by alloying elements in solid solution may present a particular sensitivity to intergranular stress corrosion cracking as a result of intergranular dissolution. In Al-5Mg alloys such as AA5083, precipitation of the β-phase (Al3Mg2) at grain boundaries strongly favours intergranular fracture. Previous experimental studies revealed that local plasticity seems to play a significant role in crack initiation. Nevertheless, the exact role of crystal plasticity...

Effect of Bio char on Plant Growth and Aluminium Form of Soil under Aluminium Stress

Science.gov (United States)

Qian, Lianwen; Li, Qingbiao; Sun, Jingwei; Feng, Ying

2018-01-01

Aluminium-enriched acid red soils in South China easily cause aluminium toxicity to plants, but biochip can improve soils and eliminate soil contaminations. In this project, biochip was used in potted plant control test to study the effect of biochip on plant growth in soil under acid aluminium stress and the migration and conversion of aluminium in plant-soil system. The fin dings show that the application of biochip increases the pH value of soil under aluminium stress significantly, changes the existing form of aluminium ion in soil, reduces the plants’ absorption of aluminium, and alleviates the aluminium toxicity to plants, but too much biochip may inhibit the growth of plants. In this case, further study should be carried out as regards the volume and way of biochip input in practical applications as well as the timeliness of aluminium toxicity removal.

Modified Welding Technique of a Hypo-Eutectic Al-Cu Alloy for Higher Mechanical Properties

Science.gov (United States)

Ghosh, B. R.; Gupta, R. K.; Biju, S.; Sinha, P. P.

GTAW process is used for welding of pressure vessels made of hypo-eutectic Al-Cu alloy AA2219 containing 6.3% Cu. As welded Yield strength of the alloy was found to be in the range of 140-150 MPa, using conventional single pass GTAW technique on both AC and DCSP modes. Interestingly, it was also found that weld-strength decreased with increase in thickness of the weld coupons. Welding metallurgy of AA2219 Al alloy was critically reviewed and factors responsible for lower properties were identified. Multipass GTAW on DCSP mode was postulated to improve the weld strength of this alloy. A systematic experimentation using 12 mm thick plates was carried out and YS of 200 MPa has been achieved in the as welded condition. Thorough characterization including optical and electron microscopy was conducted to validate the metallurgical phenomena attributable to improvement in weld strength. This paper presents the conceptual understanding of welding metallurgy of AA2219 alloy and validation by experiments, which could lead to better weld properties using multipass GTAW on DCSP mode.

Confined recrystallization of high-purity aluminium during accumulative roll bonding of aluminium laminates

International Nuclear Information System (INIS)

Chekhonin, Paul; Beausir, Benoît; Scharnweber, Juliane; Oertel, Carl-Georg; Hausöl, Tina; Höppel, Heinz Werner; Brokmeier, Heinz-Günter; Skrotzki, Werner

2012-01-01

Aluminium laminates consisting of high-purity aluminium and commercially pure aluminium have been produced by accumulative roll bonding (ARB) at ambient temperature for up to 10 cycles. To study the microstructure and texture development of the high-purity aluminium layers with regard to the shrinking layer thickness during ARB, microstructure and texture investigations were carried out by electron backscatter diffraction and neutron and X-ray diffraction, respectively. While the commercially pure aluminium layers develop an ultrafine-grained microstructure, partial discontinuous recrystallization occurs in the high-purity layers. The texture of the high-purity layers mainly consists of Cube and “Tilted Cube” (tilted with respect to the transverse direction) components. The experimental results are discussed with respect to confined recrystallization in the ARB aluminium laminates.

Alloys of uranium and aluminium with low aluminium content

International Nuclear Information System (INIS)

Cabane, G.; Englander, M.; Lehmann, J.

1955-01-01

Uranium, as obtained after spinning in phase γ, presents an heterogeneous structure with large size grains. The anisotropic structure of the metal leads to an important buckling and surface distortion of the fuel slug which is incompatible with its tubular cladding for nuclear fuel uses. Different treatments have been made to obtain an isotropic structure presenting high thermal stability (laminating, hammering and spinning in phase α) without success. Alloys of uranium and aluminium with low aluminium content present important advantage in respect of non allied uranium. The introduction of aluminium in the form of intermetallic compound (UAl 2 ) gives a better resistance to thermal fatigue. Alloys obtained from raw casting present an improved buckling and surface distortion in respect of pure uranium. This improvement is obtained with uranium containing between 0,15 and 0,5 % of aluminium. An even more improvement in thermal stability is obtained by thermal treatments of these alloys. These new characteristics are explained by the fine dispersion of the UAl 2 particles in uranium. The results after treatments obtained from an alloy slug containing 0,4 % of aluminium show no buckling or surface distortion and no elongation. (M.P.)

Evolution of microstructure and mechanical properties during annealing of cold-rolled AA8011 alloy

Energy Technology Data Exchange (ETDEWEB)

Roy, Rajat Kumar [Department of Metallurgical and Materials Engineering, Indian Institute of Technology, Kharagpur 721302 (India)], E-mail: r.roy@rediffmail.com; Kar, Sujoy [Department of Metallurgical and Materials Engineering, Indian Institute of Technology, Kharagpur 721302 (India); Department of Materials Science and Engineering, The Ohio State University, OH 43210 (United States); Das, Siddhartha [Department of Metallurgical and Materials Engineering, Indian Institute of Technology, Kharagpur 721302 (India)], E-mail: sdas@metal.iitkgp.ernet.in

2009-01-22

The evolution of recrystallized microstructure of cold-rolled aluminium alloy AA8011 is investigated with the help of optical metallography, orientation imaging microscopy (OIM), transmission electron microscopy (TEM), differential scanning calorimetry (DSC), electrical resistivity and microhardness measurements at different annealing conditions. Tensile testing of the isochronally annealed specimens is performed to examine the effect of annealing temperature and microstructure on mechanical properties. Precipitates affect the grain growth behaviour and texture evolution. Normal grain growth takes place prior to abnormal grain growth. A wide range of grain size distribution and a combination of cube, rolling and random texture is observed at complete recrystallized condition. Our results provide not only new insight into aluminium packaging materials (i.e., foils, cans, and air conditioning ducts) but also a platform to better understand the recrystallization of a wide range of related alloys.

Behaviour and fatigue damage study of cast aluminium alloys; Etude du comportement et de l'endommagement en fatigue d'alliages d'aluminium de fonderie

Energy Technology Data Exchange (ETDEWEB)

Barlas, B.

2004-02-15

This study is aimed at determining the influence of chemical composition and heat treatment of cast aluminium alloys Al-Si-Cu-Mg on mechanical behaviour and fatigue life of structures. The industrial frame of this study concerns cylinder-heads of high efficiency diesel engines, for Renault and Montupet companies. The experimental means involved in this work are as well microscopic (TEM, microhardness, image analysis), mechanical (LCF and aniso-thermal tests, macro-hardness) and numerical (simulation of the stability of the hardening phases, behaviour and damage model identification, cylinder-head life time calculation). The link between micro and macro approaches is provided by the means of an internal microscopic variable representing thermal aging through coarsening of the precipitates and implemented into the macroscopic model. (author)

Phase transformation of aluminium hydroxide to aα- alumina prepared from different aluminium salts

International Nuclear Information System (INIS)

Masliana Muslimin; Meor Yusoff Meor Sulaiman

2006-01-01

The study intends to look at the most suitable aluminium salt to produce a single-phase a-alumina by the hydrothermal method. In the process to produce alumina from the calcination of aluminium hydroxide (Al(OH) 3 ), three different aluminium salts namely aluminium sulfate (Al 2 (SO 4) 2), aluminium nitrate (A(NO 3 ) 3 ) and aluminium chloride (AlCl 3 ) were tried. The process involved the used of NH 4 OH as the precipitating medium. Aluminium hydroxide produced from each of these salts were characterised by x-ray diffraction (XRD) technique to identity the crystalline phase. Aluminium hydroxide produced by all the different aluminium salts is present as boehmite or pseudo-boehmite phase. Aluminium hydroxide produced from Al 2 (SO) 2 , Al(NO) 3 and AlCl 3 shows the transformation of the boehmite phase to a α-alumina phase at 500 0 C. On further heating, the α-alumina continuously formed at 800 o C followed soon at 1000 o C. But for the Al(NO3) 3 salts a different phase transitions occurs on heating especially at 1000 o C. Here it was observed not a single alumina phase is presence but the presence of both α and γ--alumina phases. At 1300 o C, the single α-alumina phase was formed. The study concluded that aluminium sulphate is recommended in order to obtain a single-phase α-alumina with the required characteristics. (Author)

The speciation of Si and other alloying elements in the oxide surface film of galvanically corroded weld fusion zone of laser welded AA6061 aluminium alloy

Energy Technology Data Exchange (ETDEWEB)

Mujibur Rahman, A.B.M.; Kumar, Sunil [Ian Wark Research Institute, University of South Australia, Mawson Lakes Campus, Mawson Lakes, South Australia 5095 (Australia); Gerson, Andrea R. [Applied Centre for Structural and Synchrotron Studies, University of South Australia, Mawson Lakes Campus, Mawson Lakes, South Australia 5095 (Australia)], E-mail: Andrea.Gerson@unisa.edu.au

2008-05-15

It has recently been proposed that on galvanic corrosion of laser weldments of AA6061 aluminium alloy the temporal increase in galvanic corrosion resulted from either the build up of intermetallic phases in the surface oxide layer and/or a significant increase in the surface area of the cathodic weld fusion zone due to the porous nature of the surface layer. This proposition has motivated a comprehensive surface analytical study of the incorporation of alloying elements into the oxide surface film, which is composed predominately of alumina. Si is found to be present as silicate and silicides. The Gibbs free energy of formation, per cation, of silicate is more negative than that for alumina and hence silicate formation is thermodynamically, relatively, favourable. In contrast the Gibbs free energy for oxide formation, per cation, for the other alloying elements is less negative and hence relatively unfavourable compared to the formation of alumina. We propose therefore that Fe, Cu and Cr are present in the metallic form, possibly as silicides, within the oxide surface layer. Magnesium is found to be depleted relative to the weld fusion zone presumably due to dissolution within the electrolyte.

The speciation of Si and other alloying elements in the oxide surface film of galvanically corroded weld fusion zone of laser welded AA6061 aluminium alloy

International Nuclear Information System (INIS)

Mujibur Rahman, A.B.M.; Kumar, Sunil; Gerson, Andrea R.

2008-01-01

It has recently been proposed that on galvanic corrosion of laser weldments of AA6061 aluminium alloy the temporal increase in galvanic corrosion resulted from either the build up of intermetallic phases in the surface oxide layer and/or a significant increase in the surface area of the cathodic weld fusion zone due to the porous nature of the surface layer. This proposition has motivated a comprehensive surface analytical study of the incorporation of alloying elements into the oxide surface film, which is composed predominately of alumina. Si is found to be present as silicate and silicides. The Gibbs free energy of formation, per cation, of silicate is more negative than that for alumina and hence silicate formation is thermodynamically, relatively, favourable. In contrast the Gibbs free energy for oxide formation, per cation, for the other alloying elements is less negative and hence relatively unfavourable compared to the formation of alumina. We propose therefore that Fe, Cu and Cr are present in the metallic form, possibly as silicides, within the oxide surface layer. Magnesium is found to be depleted relative to the weld fusion zone presumably due to dissolution within the electrolyte

Development of an alternative route for recycling AA2050 aluminum alloy by powder metallurgy

International Nuclear Information System (INIS)

Guido, V.; Oliveira, A.C. de; Travessa, D.N.; Cardoso, K.R.

2014-01-01

This paper presents an alternative solid state route to recycling AA2050 aeronautical aluminium alloy chips. The first stage in the recycling process, reported in this work, is the obtainment of the alloy powder by high energy ball milling to subsequent cold pressing and hot extrusion. The process started with the cleaning of chips with the aim of contaminant removing from machining process and transport, followed by the high energy ball milling to result in the AA2050 alloy powder. The powder obtained was characterized by laser size particle analysis, scanning electron microscopy (SEM), X-Ray diffraction (DRX) and inductively coupled plasma atomic emission spectroscopy (ICP-AES). The results show the feasibility of obtaining a powder having appropriate particle size and chemical composition in accordance with the specification for alloy. (author)

Radiation-hardened bulk CMOS technology

International Nuclear Information System (INIS)

Dawes, W.R. Jr.; Habing, D.H.

1979-01-01

The evolutionary development of a radiation-hardened bulk CMOS technology is reviewed. The metal gate hardened CMOS status is summarized, including both radiation and reliability data. The development of a radiation-hardened bulk silicon gate process which was successfully implemented to a commercial microprocessor family and applied to a new, radiation-hardened, LSI standard cell family is also discussed. The cell family is reviewed and preliminary characterization data is presented. Finally, a brief comparison of the various radiation-hardened technologies with regard to performance, reliability, and availability is made

Coprecipitation of yttrium and aluminium hydroxide for preparation of yttrium aluminium garnet

NARCIS (Netherlands)

Vrolijk, J.W.G.A.; Willems, J.W.M.M.; Metselaar, R.

1990-01-01

Coprecipitation of yttrium and aluminium hydroxide for the preparation of pure yttrium aluminium garnet (YAG) powder with small grain size is the subject of this study. Starting materials are sulphates and chlorides of yttrium and aluminium. To obtain pure YAG (Y3Al5O12), the pH during flocculation

Potential fatigue strength improvement of AA 5083-H111 notched parts by wire brush hammering: Experimental analysis and numerical simulation

International Nuclear Information System (INIS)

Sidhom, Naziha; Moussa, Naoufel Ben; Janeb, Sameh; Braham, Chedly; Sidhom, Habib

2014-01-01

Highlights: • Wire brush hammering increases by 20% the AA 5083-H111 notched parts fatigue limit. • Improvement of fatigue strength is related to the fatigue cracks nucleation. • Fatigue strength prediction accounts for wire brush hammering effects. - Abstract: The effects of milling as machining process and a post-machining treatment by wire-brush hammering, on the near surface layer characteristics of AA 5083-H111 were investigated. Surface texture, work-hardening and residual stress profiles were determined by roughness measurement, scanning electron microscope (SEM) examinations, microhardness and X-ray diffraction (XRD) measurements. The effects of surface preparation on the fatigue strength were assessed by bending fatigue tests performed on notched samples for two loading stress ratios R 0.1 and R 0.5 . It is found that the bending fatigue limit at R 0.1 and 10 7 cycles is 20% increased, with respect to the machined surface, by wire-brush hammering. This improvement was discussed on the basis of the role of surface topography, stabilized residual stress and work-hardening on the fatigue-crack network nucleation and growth. The effects biaxial residual stress field and surface work-hardening were taken into account in the finite element model. A multi-axial fatigue criterion was proposed to predict the fatigue strength of aluminum alloy notched parts for both machined and treated states

Experimental and numerical investigation of strain rate effect on low cycle fatigue behaviour of AA 5754 alloy

Science.gov (United States)

Kumar, P.; Singh, A.

2018-04-01

The present study deals with evaluation of low cycle fatigue (LCF) behavior of aluminum alloy 5754 (AA 5754) at different strain rates. This alloy has magnesium (Mg) as main alloying element (Al-Mg alloy) which makes this alloy suitable for Marines and Cryogenics applications. The testing procedure and specimen preparation are guided by ASTM E606 standard. The tests are performed at 0.5% strain amplitude with three different strain rates i.e. 0.5×10-3 sec-1, 1×10-3 sec-1 and 2×10-3 sec-1 thus the frequency of tests vary accordingly. The experimental results show that there is significant decrease in the fatigue life with the increase in strain rate. LCF behavior of AA 5754 is also simulated at different strain rates by finite element method. Chaboche kinematic hardening cyclic plasticity model is used for simulating the hardening behavior of the material. Axisymmetric finite element model is created to reduce the computational cost of the simulation. The material coefficients used for “Chaboche Model” are determined by experimentally obtained stabilized hysteresis loop. The results obtained from finite element simulation are compared with those obtained through LCF experiments.

Kinetic characterization and of recrystallization of the aluminum alloy 6063 after S work hardening treatment

International Nuclear Information System (INIS)

Esposito, Iara Maria

2006-01-01

The aluminum 6063 alloy possesses a great industrial interest, presenting characteristics that justify its frequent use, when compared to the other aluminum alloys: the precipitation hardening and high cold work capacity. These alloys present high ductility, that allows their use in operations with high deformation degrees, as the cold work. The objective of this work is to show comparative analysis of the hardness Vickers of the commercial aluminum 6063 alloy, after cold work with different area reduction degree and thermal treatment. Considering the frequent utilization aluminium 6063 alloy, this work studies the characterization and recrystallization of this alloy, after the plastic deformation in different area reduction degrees, thermal treatment and convenient treatment times - Thermo mechanic Treatments. (author)

Toxicity of aluminium on five aquatic invertebrates; Aluminiums toksisitet paa 5 akvatiske invertebrater

Energy Technology Data Exchange (ETDEWEB)

Moe, J [Oslo Univ. (Norway)

1996-01-01

The conference paper deals with the experiments done by investigating the effects from the toxicity of aluminium on aquatic invertebrates. The aim of the experiments was to compare the toxicity of unstable aluminium compounds with stable forms of aluminium. 8 refs., 2 figs., 2 tabs.

Microstructure of friction stir welded joints of 2017A aluminium alloy sheets.

Science.gov (United States)

Mroczka, K; Dutkiewicz, J; Pietras, A

2010-03-01

The present study examines a friction stir welded 2017A aluminium alloy. Transmission electron microscope investigations of the weld nugget revealed the average grain size of 5 microm, moderate density of dislocations as well as the presence of nanometric precipitates located mostly in grains interiors. Scanning electron microscope observations of fractures showed the presence of ductile fracture in the region of the weld nugget with brittle precipitates in the lower part. The microhardness analysis performed on the cross-section of the joints showed fairly small changes; however, after the artificial ageing process an increase in hardness was observed. The change of the joint hardness subject to the ageing process indicates partial supersaturation in the material during friction stir welding and higher precipitation hardening of the joint.

Effect of Sintering Temperature on the Properties of Aluminium-Aluminium Oxide Composite Materials

Directory of Open Access Journals (Sweden)

Dewan Muhammad Nuruzzaman

2016-12-01

Full Text Available In this study, aluminium-aluminium oxide (Al-Al2O3 metal matrix composites of different weight percentage reinforcements of aluminium oxide were processed at different sintering temperatures. In order to prepare these composite specimens, conventional powder metallurgy (PM method was used. Three types specimens of different compositions such as 95%Al+5%Al2O3, 90%Al+10%Al2O3 and 85%Al+15%Al2O3 were prepared under 20 Ton compaction load. Then, all the specimens were sintered in a furnace at two different temperatures 550oC and 580oC. In each sintering process, two different heating cycles were used. After the sintering process, it was observed that undistorted flat specimens were successfully prepared for all the compositions. The effects of sintering temperature and weight fraction of aluminium oxide particulates on the density, hardness and microstructure of Al-Al2O3 composites were observed. It was found that density and hardness of the composite specimens were significantly influenced by sintering temperature and percentage aluminium oxide reinforcement. Furthermore, optical microscopy revealed that almost uniform distribution of aluminium oxide reinforcement within the aluminium matrix was achieved.

Dispersion strengthening of aluminium-aluminium-oxide products

DEFF Research Database (Denmark)

Hansen, Niels

1970-01-01

The true stress-true strain curves at room temperature and at 400°C were determined for various types of aluminium-aluminium-oxide products containing from 0.2 to 4.7 weight per cent of aluminium oxide. The effect of particles on the initial flow stress and the flow stress for 0.2% offset at room...... temperature and at 400°C is in agreement with Orowan's theory. The increase in flow stress at room temperature for strain values below 3 per cent was related to the plastic strain by the equation σ-σoy=k1ε 1/2, where σoy is the initial flow stress and where k1 increases for increasing volume fraction...... and decreasing particle size of the dispersed particles. A general expression for k1 was derived for the relationship between the dislocation density and the strain in dispersion-strengthened products...

The prophylactic reduction of aluminium intake.

Science.gov (United States)

Lione, A

1983-02-01

The use of modern analytical methods has demonstrated that aluminium salts can be absorbed from the gut and concentrated in various human tissues, including bone, the parathyroids and brain. The neurotoxicity of aluminium has been extensively characterized in rabbits and cats, and high concentrations of aluminium have been detected in the brain tissue of patients with Alzheimer's disease. Various reports have suggested that high aluminium intakes may be harmful to some patients with bone disease or renal impairment. Fatal aluminium-induced neuropathies have been reported in patients on renal dialysis. Since there are no demonstrable consequences of aluminium deprivation, the prophylactic reduction of aluminium intake by many patients would appear prudent. In this report, the major sources of aluminium in foods and non-prescription drugs are summarized and alternative products are described. The most common foods that contain substantial amounts of aluminium-containing additives include some processed cheeses, baking powders, cake mixes, frozen doughs, pancake mixes, self-raising flours and pickled vegetables. The aluminium-containing non-prescription drugs include some antacids, buffered aspirins, antidiarrhoeal products, douches and haemorrhoidal medications. The advisability of recommending a low aluminium diet for geriatric patients is discussed in detail.

Lanthanide based conversion coatings for long term wet storage of aluminium-clad spent fuel

International Nuclear Information System (INIS)

Fernandes, S.M.C.; Correa, O.V.; De Souza, J.A.; Ramanathan, L.V.

2010-01-01

Spent fuels from research reactors are stored in basins with water of less than desirable quality at many facilities around the world and instances of cladding failure caused by pitting corrosion have been reported. Conversion coatings have been used in many industries to protect different metals, including aluminium alloys. This paper presents the results of an ongoing investigation in which the corrosion resistance of lanthanide (cerium, lanthanum and praseodymium) based conversion coated RR fuel cladding alloys has been studied. Electrochemical tests in the laboratory revealed higher corrosion resistance of CeO 2 , La 2 O 3 and Pr 2 O 3 coated AA 1100 and AA 6061 alloys in NaCl solutions. Uncoated and CeO 2 coated coupons of these alloys exposed for 50 days to the spent fuel basin of the IEA-R1 research reactor in IPEN, Brazil, revealed marked reductions in the extent of pitting corrosion. (author)

Coarsening of AA6013-T6 Precipitates During Sheet Warm Forming Applications

Science.gov (United States)

Di Ciano, M.; DiCecco, S.; Esmaeili, S.; Wells, M. A.; Worswick, M. J.

2018-03-01

The use of warm forming for AA6xxx-T6 sheet is of interest to improve its formability; however, the effect warm forming may have on the coarsening of precipitates and the mechanical strength of these sheets has not been well studied. In this research, the coarsening behavior of AA6013-T6 precipitates has been explored, in the temperature range of 200-300 °C, and time of 30 s up to 50 h. Additionally, the effect of warm deformation on coarsening behavior was explored using: (1) simulated warm forming tests in a Gleeble thermo-mechanical simulator and (2) bi-axial warm deformation tests. Using a strong obstacle model to describe the yield strength (YS) evolution of the AA6013-T6 material, and a Lifshitz, Slyozov, and Wagner (LSW) particle coarsening law to describe the change in precipitate size with time, the coarsening kinetics were modeled for this alloy. The coarsening kinetics in the range of 220-300 °C followed a trend similar to that previously found for AA6111 for the 180-220 °C range. There was strong evidence that coarsening kinetics were not altered due to warm deformation above 220 °C. For warm forming between 200 and 220 °C, the YS of the AA6013-T6 material increased slightly, which could be attributed to strain hardening during warm deformation. Finally, a non-isothermal coarsening model was used to assess the potential reduction in the YS of AA6013-T6 for practical processing conditions related to auto-body manufacturing. The model calculations showed that 90% of the original AA6013-T6 YS could be maintained, for warm forming temperatures up to 280 °C, if the heating schedule used to get the part to the warm forming temperature was limited to 1 min.

A non-linear kinematic hardening function

International Nuclear Information System (INIS)

Ottosen, N.S.

1977-05-01

Based on the classical theory of plasticity, and accepting the von Mises criterion as the initial yield criterion, a non-linear kinematic hardening function applicable both to Melan-Prager's and to Ziegler's hardening rule is proposed. This non-linear hardening function is determined by means of the uniaxial stress-strain curve, and any such curve is applicable. The proposed hardening function considers the problem of general reversed loading, and a smooth change in the behaviour from one plastic state to another nearlying plastic state is obtained. A review of both the kinematic hardening theory and the corresponding non-linear hardening assumptions is given, and it is shown that material behaviour is identical whether Melan-Prager's or Ziegler's hardening rule is applied, provided that the von Mises yield criterion is adopted. (author)

Laser transformation hardening effect on hardening zone features and surface hardness of tool steel AISI D2

Directory of Open Access Journals (Sweden)

D. Lesyk

2017-06-01

Full Text Available The relationship of technological input regimes of the laser transformation hardening on change the hardening depth, hardening width, and hardening angle, as well as surface hardness of the tool steel AISI D2 using multifactor experiment with elements of the analysis of variance and regression equations was determined. The laser transformation hardening process implemented by controlling the heating temperature using Nd:YAG fiber laser with scanner, pyrometer and proportional-integral-differential controller. The linear and quadratic regression models are developed, as well as response surface to determine the effect of the heating temperature and feed rate of the treated surface on the energy density of the laser beam, hardening depths, hardening width, hardening angle, and surface hardness are designed. The main effect on the energy density of the laser beam has a velocity laser treatment, on the other hand, the main effect on the geometrical parameters of the laser hardened zone and surface hardness has temperature heating are shown. The optimum magnitudes of the heating temperature (1270 °C and feed rate of the treated surface (90 mm/min for laser transformation hardening of the tool steel AISI D2 using fiber laser with scanner were defined.

Effect of process parameters on the residual stresses in AA5083-H321 friction stir welds

Energy Technology Data Exchange (ETDEWEB)

Lombard, H. [NMMU, Gardham Avenue, PO Box 77000, 6031 Port Elizabeth (South Africa); University of Plymouth, Drake Circus, Plymouth PL4 8AA (United Kingdom); Hattingh, D.G. [NMMU, Gardham Avenue, PO Box 77000, 6031 Port Elizabeth (South Africa); Steuwer, A. [NMMU, Gardham Avenue, PO Box 77000, 6031 Port Elizabeth (South Africa); FaME38 at the ILL-ESRF, 6 rue J Horowitz, 38042 Grenoble (France); University of Plymouth, Drake Circus, Plymouth PL4 8AA (United Kingdom)], E-mail: steuwer@ill.fr; James, M.N. [NMMU, Gardham Avenue, PO Box 77000, 6031 Port Elizabeth (South Africa); University of Plymouth, Drake Circus, Plymouth PL4 8AA (United Kingdom)

2009-02-15

This paper investigates the effect of varying welding parameters on the residual stress profiles in friction stir welds of aluminium alloy AA5083-H321, which were created on a fully instrumented friction welding machine. The residual stresses were determined non-destructively using synchrotron X-ray diffraction. The width and maximum of the residual stress profile show clear correlation with the heat input, and in particular feed rate, which was found to be the dominant parameter.

Thermal analysis of laser additive manufacturing of aluminium alloys: Experiment and simulation

Science.gov (United States)

Bock, Frederic E.; Froend, Martin; Herrnring, Jan; Enz, Josephin; Kashaev, Nikolai; Klusemann, Benjamin

2018-05-01

Laser additive manufacturing (LAM) has become increasingly popular in industry in recent decades because it enables exceptional degrees of freedom regarding the structural design of lightweight components compared to subtractive manufacturing techniques. Laser metal deposition (LMD) of wire-fed material shows in particular the advantages such as high process velocity and efficient use of material compared to other LAM processes. During wire-based LMD, the material is deposited onto a substrate and supplemented by successive layers allowing a layer-wise production of complex three-dimensional structures. Despite the increased productivity of LMD, regarding the ability to process aluminium alloys, there is still a lack in quality and reproducibility due to the inhomogeneous temperature distribution during the process, leading to undesired residual stresses, distortions and inconsistent layer geometries and poor microstructures. In this study, the aluminium alloy AA5087 as wire and AA5754 as substrate material were utilized for LMD. In order to obtain information about the temperature field during LMD, thermocouple and thermography measurements were performed during the process. The temperature measurements were used to validate a finite element model regarding the heat distribution, which will be further used to investigate the temperature field evolution over time. To consider the continuous addition of material within the FE-model, an inactive/active element approach was chosen, where initially deactivated elements are activated corresponding to the deposition of material. The first results of the simulation and the experiments show good agreement. Therefore, the model can be used in the future for LMD process optimization, e.g., in terms of minimizing local variations of the thermal load for each layer.

Investigation of the aluminium-aluminium oxide reversible transformation as observed by hot stage electron microscopy.

Science.gov (United States)

Grove, C. A.; Judd, G.; Ansell, G. S.

1972-01-01

Thin foils of high purity aluminium and an Al-Al2O3 SAP type of alloy were oxidised in a specially designed hot stage specimen chamber in an electron microscope. Below 450 C, amorphous aluminium oxide formed on the foil surface and was first detectable at foil edges, holes, and pits. Islands of aluminium then nucleated in this amorphous oxide. The aluminium islands displayed either a lateral growth with eventual coalescence with other islands, or a reoxidation process which caused the islands to disappear. The aluminium island formation was determined to be related to the presence of the electron beam. A mechanism based upon electron charging due to the electron beam was proposed to explain the nucleation, growth, coalescence, disappearance, and geometry of the aluminium islands.

TEM investigation of aluminium containing precipitates in high aluminium doped silicon carbide

International Nuclear Information System (INIS)

Wong-Leung, J.; FitzGerald, J.D.

2002-01-01

Full text: Silicon carbide is a promising semiconductor material for applications in high temperature and high power devices. The successful growth of good quality epilayers in this material has enhanced its potential for device applications. As a novel semiconductor material, there is a need for studying its basic physical properties and the role of dopants in this material. In this study, silicon carbide epilayers were grown on 4H-SiC wafers of (0001) orientation with a miscut angle of 8 deg at a temperature of 1550 deg C. The epilayers contained regions of high aluminium doping well above the solubility of aluminium in silicon carbide. High temperature annealing of this material resulted in the precipitation of aluminium in the wafers. The samples were analysed by secondary ion mass spectrometry and transmission electron microscopy. Selected area diffraction studies show the presence of aluminium carbide and aluminium silicon carbide phases. Copyright (2002) Australian Society for Electron Microscopy Inc

Interdependent effect of chemical composition and thermal history on artificial aging of AA6061

International Nuclear Information System (INIS)

Pogatscher, S.; Antrekowitsch, H.; Uggowitzer, P.J.

2012-01-01

In this study, the interdependent effect of chemical composition and thermal history on artificial aging was investigated for the aluminum alloy AA6061. Based on thermodynamic calculations, including Al, Fe, Cr, Zn, Ti, Mg, Si and Cu, model alloys exhibiting a maximum variation of the reachable solute super-saturation of elements relevant for precipitation hardening within the compositional limits of AA6061 were produced. The artificial aging behavior of these alloys at 175 °C was studied by tensile testing for two thermal histories, including very short- and long-term room temperature storage after quenching. Precipitation during artificial aging was investigated by an analysis of yield strength data. As generally expected, precipitation kinetics was found to depend strongly on the solute super-saturation in the case of very short room temperature storage. For artificial aging after long-term room temperature storage the kinetics showed almost no dependence on the chemical composition. This seems to be an exception from simple precipitation kinetics and can be explained based on the complex role of quenched-in vacancies in artificial aging of AA6061.

Superheat effect on bainite steel hardenability

International Nuclear Information System (INIS)

Kubachek, V.V.; Sklyuev, P.V.

1978-01-01

The bainite hardenability of 34KhN1M and 35 KhN1M2Ph steels has been investigated by the end-face hardening technique. It is established that, as the temperature of austenitization rises from 900 to 1280 deg C, the temperature of bainite transformation increases and bainite hardenability of the steels falls off. A repeated slow heating to 900 deg C of previously overheated 34KhN1M steel breaks up grain, lowers the temperature of the bainite transformation and raises the hardenability to values obtained with ordinary hardening from 900 deg C. A similar heating of previously overheated 35KhN1M2Ph steel is accompanied by restoration of initial coarse grains and maintenance of both the elevated bainite transformation temperature and to lower hardenability corresponding to hardening from the temperature of previous overheating

Development of a high temperature high strength Al alloy by addition of small amounts of Sc and Mg to 2219 alloy

Energy Technology Data Exchange (ETDEWEB)

Mondol, S. [Department of Materials Engineering, Indian Institute of Science, Bangalore 560012 (India); Alam, T.; Banerjee, R. [Advanced Materials and Manufacturing Processes Institute and Department of Materials Science and Engineering, University of North Texas, Denton, TX 76203-5017 (United States); Kumar, S. [Department of Materials Engineering, Indian Institute of Science, Bangalore 560012 (India); Chattopadhyay, K., E-mail: kamanio@materials.iisc.ernet.in [Department of Materials Engineering, Indian Institute of Science, Bangalore 560012 (India)

2017-02-27

The paper reports a significant improvement in tensile properties, in particular at 200 °C, of commercial 2219 Al alloy by addition of small amounts of Sc (0.8 wt%) and Mg (0.45 wt%), and employing copper mould suction casting followed by natural ageing and cold rolling. Microstructural examination and measurement of hardness were performed in order to explain the effects of Sc and Mg at each processing step. It is found that the remarkable improvement of room temperature strength occurs due to fine grain size, Al{sub 3}Sc and Al{sub 3}(Sc,Zr) dispersoids, GP zones on {100} and {111} planes, and work hardening. On exposure at 200 °C, the GP zones transform primarily to θ′ precipitates and a few Ω precipitates. Sc and Mg atoms segregate at the θ′/matrix interface, which suppress the coarsening of θ′ precipitates and make them stable at higher temperatures. Thus, the work reports extremely high 0.2% proof stress of 542 MPa at room temperature, 378 MPa at 200 °C and 495 MPa at room temperature after 200 h exposure at 200 °C accompanied by reasonable ductility. Theoretical yield strength is calculated on the basis of the observed microstructure and is found to be in good agreement with the experimentally obtained value.

Development of a high temperature high strength Al alloy by addition of small amounts of Sc and Mg to 2219 alloy

International Nuclear Information System (INIS)

Mondol, S.; Alam, T.; Banerjee, R.; Kumar, S.; Chattopadhyay, K.

2017-01-01

The paper reports a significant improvement in tensile properties, in particular at 200 °C, of commercial 2219 Al alloy by addition of small amounts of Sc (0.8 wt%) and Mg (0.45 wt%), and employing copper mould suction casting followed by natural ageing and cold rolling. Microstructural examination and measurement of hardness were performed in order to explain the effects of Sc and Mg at each processing step. It is found that the remarkable improvement of room temperature strength occurs due to fine grain size, Al 3 Sc and Al 3 (Sc,Zr) dispersoids, GP zones on {100} and {111} planes, and work hardening. On exposure at 200 °C, the GP zones transform primarily to θ′ precipitates and a few Ω precipitates. Sc and Mg atoms segregate at the θ′/matrix interface, which suppress the coarsening of θ′ precipitates and make them stable at higher temperatures. Thus, the work reports extremely high 0.2% proof stress of 542 MPa at room temperature, 378 MPa at 200 °C and 495 MPa at room temperature after 200 h exposure at 200 °C accompanied by reasonable ductility. Theoretical yield strength is calculated on the basis of the observed microstructure and is found to be in good agreement with the experimentally obtained value.

Enhancement of High Temperature Strength of 2219 Alloys Through Small Additions of Nb and Zr and a Novel Heat Treatment

Science.gov (United States)

Mondol, S.; Makineni, S. K.; Kumar, S.; Chattopadhyay, K.

2018-05-01

This paper presents a detailed investigation on the effect of small amount of Nb and Zr additions to 2219 Al alloy coupled with a novel three-stage heat treatment process. The main aim of the work is to increase the high temperature strength of 2219 alloy by introducing thermally stable L12 type ordered precipitates in the matrix as well as by reducing the coarsening of metastable strengthening θ″ and θ' precipitates. To achieve this, small amounts of Nb and Zr are added to 2219 alloy melt and retained in solid solution by suction casting in a water-cooled copper mould having a cooling rate of 102 to 103 K/s. The suction cast alloy is directly aged at 673 K (400 °C) to form L12 type ordered coherent Al3Zr precipitates. Subsequently, the alloy is solution treated at 808 K (535 °C) for 30 minutes to get supersaturation of Cu in the matrix without significantly affecting the Al3Zr precipitates. Finally, the alloy is aged at 473 K (200 °C), which results in the precipitation of θ″ and θ'. Microstructural characterization reveals that θ″ and θ' are heterogeneously precipitated on pre-existing uniformly distributed Al3Zr precipitates, which leads to a higher number density of these precipitates. This results in a significant increase in strength at room temperature as well as at 473 K (200 °C) as compared to the 2219 alloy. Furthermore, the alloy remains thermally stable after prolonged exposure at 473 K (200 °C), which is attributed to the elastic strain energy minimization by the conjoint Al3Zr/θ' or Al3Zr/θ″ precipitates, and the high Zr and Nb solute-vacancy binding energy, retarding the growth and coarsening of θ″ and θ' precipitates.

Analysis of aluminium in rat following administration of allergen immunotherapy using either aluminium or microcrystalline-tyrosine-based adjuvants.

Science.gov (United States)

McDougall, Stuart A; Heath, Matthew D; Kramer, Matthias F; Skinner, Murray A

2016-03-01

Investigation into the absorption, distribution and elimination of aluminium in rat after subcutaneous aluminium adjuvant formulation administration using ICP-MS is described. Assays were verified under the principles of a tiered approach. There was no evidence of systemic exposure of aluminium, in brain or in kidney. Extensive and persistent retention of aluminium at the dose site was observed for at least 180 days after administration. This is the first published work that has quantified aluminium adjuvant retention based on the quantity of aluminium delivered in a typical allergy immunotherapy course. The results indicate that the repeated administration of aluminium-containing adjuvants will likely contribute directly and significantly to an individual's body burden of aluminium.

TITANIUM CARBON ALUMINIUM : A NOVEL GRAIN REFINER FOR ALUMINIUM-LITHIUM ALLOYS

OpenAIRE

Birch , M.; Cowell , A.

1987-01-01

This work explores the possibility of achieving grain size control in aluminium-lithium alloys with the titanium carbon aluminium (TiCAl) master alloys invented at the Technical University of Berlin and developed by London and Scandinavian Metallurgical Co Ltd (LSM). Grain refining tests were conducted on a single batch of 8090 alloy using addition rates of 0.2wt% and 0.4wt% of TiCAl and 3/1 titanium boron aluminium (TiBAl). Other tests using 0.4wt% of binary TiAl gave poor results, showing t...

Aluminium in Infrastructures

NARCIS (Netherlands)

Maljaars, J.

2016-01-01

Aluminium alloys are used in infrastructures such as pedestrian bridges or parts of it such as handrail. This paper demonstrates that aluminium alloys are in principle also suited for heavy loaded structures, such as decks of traffic bridges and helicopter landing platforms. Recent developments in

Formation of aluminium nitride and segregation of Cu impurity atoms in aluminium implanted by high dose nitrogen ions

International Nuclear Information System (INIS)

Lin Chenglu; Hemment, P.L.F.; Li Jinhua; Zou Shichang

1994-01-01

Aluminium films with a thickness of 7000 A (containing 0.85% copper) were deposited on silicon substrates. 400 keV N 2 + or 350 keV N + ions were implanted into the aluminium films or at the interface between the aluminium and silicon, respectively. Automatic spreading resistance (ASR), Fourier transform infrared spectroscopy (FTIR) and Rutherford backscattering (RBS) and channelling were used to characterize the formation of aluminium nitride and the depth distribution of the Cu impurity in the aluminium films after ion implantation and post-annealing. The formation of a stoichiometric AlN layer with high resistance was evident from ASR, RBS analysis and FTIR measurements by the presence of the absorption band at 650 cm -1 . When the implanted nitrogen is near the interface between the aluminium and silicon, a multilayer structure can be obtained, which consists of aluminium, aluminium nitride and the silicon substrate. Cu, which is a background impurity in the deposited aluminium films, segregated into the synthesised aluminium nitride during high dose nitrogen ion implantation. This is due to irradiation-induced segregation during ion implantation. (orig.)

Ion nitriding of aluminium

International Nuclear Information System (INIS)

Fitz, T.

2002-09-01

The present study is devoted to the investigation of the mechanism of aluminium nitriding by a technique that employs implantation of low-energy nitrogen ions and diffusional transport of atoms. The nitriding of aluminium is investigated, because this is a method for surface modification of aluminium and has a potential for application in a broad spectrum of fields such as automobile, marine, aviation, space technologies, etc. However, at present nitriding of aluminium does not find any large scale industrial application, due to problems in the formation of stoichiometric aluminium nitride layers with a sufficient thickness and good quality. For the purposes of this study, ion nitriding is chosen, as an ion beam method with the advantage of good and independent control over the process parameters, which thus can be related uniquely to the physical properties of the resulting layers. Moreover, ion nitriding has a close similarity to plasma nitriding and plasma immersion ion implantation, which are methods with a potential for industrial application. (orig.)

Finite element modelling of shot peening and peen forming processes and characterisation of peened AA2024-T351 aluminium alloy

Science.gov (United States)

Gariepy, Alexandre

The main purpose of this thesis was to develop and validate finite element (FE) simulation tools for shot peening and peen forming. The specific aim was to achieve quantitatively accurate predictions for both processes and demonstrate the potential of reliable FE modelling for scientific investigation and industrial applications. First, an improved dynamic impact model that takes into account the stochastic nature of shot peening was proposed by carefully studying its dimensions, introducing a dispersion of shot sizes and significantly reducing its computational cost. In addition, cyclic mechanical testing was conducted to define a suitable material constitutive theory for aluminium alloy (AA) 2024-T3/T351 subjected to shot peening. By combining a realistic shot peening model with an appropriate material law, fairly good residual stress predictions were achieved for three different sets of shot peening parameters. Second, an experimental and numerical characterization of AA2024-T351 shot peened with parameters representative of fatigue life improvement applications was conducted. Multiple techniques, such as micro-indentation, residual stress determination and electron backscatter diffraction, were combined to gain a better understanding of the influence of shot peening on the material. The potential uses of finite element simulation to complement experimental data were also studied. The material heterogeneity arising from the random impact sequence was investigated and it was found that the impact modelling methodology could provide useful information on such heterogeneities. Third, a novel peen forming simulation methodology was introduced. The impact model provided the necessary input data as part of a multiscale approach. Numerically calculated unbalanced induced stress profiles were input into shell elements and the deformed shape after peen forming was computed as a springback analysis. In addition, a simple interpolation method was proposed to model the

Variation in aluminium patch test reactivity over time.

Science.gov (United States)

Siemund, Ingrid; Mowitz, Martin; Zimerson, Erik; Bruze, Magnus; Hindsén, Monica

2017-11-01

Contact allergy to aluminium has been reported more frequently in recent years. It has been pointed out that positive patch test reactions to aluminium may not be reproducible on retesting. To investigate possible variations in patch test reactivity to aluminium over time. Twenty-one adults, who had previously reacted positively to aluminium, were patch tested with equimolar dilution series in pet. of aluminium chloride hexahydrate and aluminium lactate, four times over a period of 8 months. Thirty-six of 84 (43%) serial dilution tests with aluminium chloride hexahydrate and 49 of 84 (58%) serial dilution tests with aluminium lactate gave negative results. The range of reactivity varied between a negative reaction to aluminium chloride hexahydrate at 10% and/or to aluminium lactate at 12%, and a positive reaction to aluminium chloride hexahydrate at 0.1% and/or to aluminium lactate at 0.12%. The highest individual difference in test reactivity noticed was 320-fold when the two most divergent minimal eliciting concentrations were compared. The patch test reactivity to aluminium varies over time. Aluminium-allergic individuals may have false-negative reactions. Therefore, retesting with aluminium should be considered when there is a strong suspicion of aluminium contact allergy. © 2017 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Experimental Study on Dissimilar Friction Stir welding of Aluminium Alloys (5083-H111 and 6082-T6) to investigate the mechanical properties

Science.gov (United States)

Kumar, H. M. Anil; Venkata Ramana, V.; Pawar, Mayur

2018-03-01

Friction stir welding is an innovative technology in the joining realm of metals and alloys. This technique is highly economical and suitable especially for non ferrous alloys compared to ferrous alloys. It finds many applications in various fields of aeronautics, automobile, ship building industries etc. The paper presents the comparative results of mechanical properties such as tensile strength, microstructure, macro structure and hardness on the similar and dissimilar aluminum alloys AA5083-H111 and AA6082-T6 under certain selected variables - constant tool rotational speed, its tilt angle, welding speed using friction stir welding process. It is observed from the experimental results that joint efficiency of dissimilar aluminium alloys is higher than the similar aluminum alloys.

The development and mechanical characterization of aluminium copper-carbon fiber metal matrix hybrid composite

Science.gov (United States)

Manzoor, M. U.; Feroze, M.; Ahmad, T.; Kamran, M.; Butt, M. T. Z.

2018-04-01

Metal matrix composites (MMCs) come under advanced materials that can be used for a wide range of industrial applications. MMCs contain a non-metallic reinforcement incorporated into a metallic matrix which can enhance properties over base metal alloys. Copper-Carbon fiber reinforced aluminium based hybrid composites were prepared by compo casting method. 4 weight % copper was used as alloying element with Al because of its precipitation hardened properties. Different weight compositions of composites were developed and characterized by mechanical testing. A significant improvement in tensile strength and micro hardness were found, before and after heat treatment of the composite. The SEM analysis of the fractured surfaces showed dispersed and embedded Carbon fibers within the network leading to the enhanced strength.

Internal friction in iron-aluminium alloys having a high aluminium content

International Nuclear Information System (INIS)

Hillairet, J.; Delaplace, J.; Silvent, A.

1966-01-01

By using a torsion pendulum to measure the internal friction of iron-aluminium alloys containing between 25 and 50 atom per cent of aluminium, it has been possible to show the existence of three damping peaks due to interstitial carbon. Their evolution is followed as a function of the carbon content, of the thermal treatment and of the aluminium content. A model based on the preferential occupation of tetrahedral sites is proposed as an interpretation of the results. A study of the Zener peak in these substitution alloys shows also that a part of the short distance disorder existing at high temperatures can be preserved by quenching. (author) [fr

ASTM B 117 Screening of Nonchromate Conversion Coatings on Aluminum Alloys 2024, 2219, 5083, and 7075 Using DOD Paint Systems

National Research Council Canada - National Science Library

Placzankis, Brian

2003-01-01

This study examines the corrosion resistance of eight nonchromate conversion coatings versus hexavalent chromium-based Alodine 1200S controls on scribed coated test panels of aluminum alloys 2024, 2219, 5083, and 7075...

Development of 2024 AA-Yttrium composites by Spark Plasma Sintering

Science.gov (United States)

Vidyasagar, CH S.; Karunakar, D. B.

2018-04-01

The method of fabrication of MMNCs is quite a challenge, which includes advanced processing techniques like Spark Plasma Sintering (SPS), etc. The objective of the present work is to fabricate aluminium based MMNCs with the addition of small amounts of yttrium using Spark Plasma Sintering and to evaluate their mechanical and microstructure properties. Samples of 2024 AA with yttrium ranging from 0.1% to 0.5 wt% are fabricated by Spark Plasma Sintering (SPS). Hardness of the samples is determined using Vickers hardness testing machine. The metallurgical characterization of the samples is evaluated by Optical Microscopy (OM), Field Emission Scanning Electron Microscopy (FE-SEM). Unreinforced 2024 AA sample is also fabricated as a benchmark to compare its properties with those of the composite developed. It is found that the yttrium addition increases the above mentioned properties by altering the precipitation kinetics and intermetallic formation to some extent and then decreases gradually when yttrium wt% increases beyond 0.3 wt%. High density (˂ 99.75) is achieved in the samples and highest hardness achieved is 114 Hv, fabricated by spark plasma sintering and uniform distribution of yttrium is observed.

Through-process modelling of texture and anisotropy in AA5182

Science.gov (United States)

Crumbach, M.; Neumann, L.; Goerdeler, M.; Aretz, H.; Gottstein, G.; Kopp, R.

2006-07-01

A through-process texture and anisotropy prediction for AA5182 sheet production from hot rolling through cold rolling and annealing is reported. Thermo-mechanical process data predicted by the finite element method (FEM) package T-Pack based on the software LARSTRAN were fed into a combination of physics based microstructure models for deformation texture (GIA), work hardening (3IVM), nucleation texture (ReNuc), and recrystallization texture (StaRT). The final simulated sheet texture was fed into a FEM simulation of cup drawing employing a new concept of interactively updated texture based yield locus predictions. The modelling results of texture development and anisotropy were compared to experimental data. The applicability to other alloys and processes is discussed.

Effects of vacuum and ageing on Zr4/Cr3 based conversion coatings on aluminium alloys

Science.gov (United States)

Thirupathi, Kalaivanan; Bárczy, Pál; Vad, Kálmán; Csik, Attila; Somosvári, Béla Márton

2018-05-01

In this study, we investigate the impact of ageing and high vacuum on existing environmentally friendly Zr4/Cr3-based conversion coatings. The freshly formed coating undergoes several changes during ageing and exposure to high vacuum. Based on the present data, we propose that the coating formed over AA6082 and AA7075 alloys is sol-gel in nature, confirmed by secondary neutral mass spectroscopy (SNMS) using the depth profiling technique. Our findings reveal that there are elemental level changes that result in shrinkage of the coating. Most Zr ions in the coating are in the solute form, with lesser number of Cr and Al ions that disappear under high vacuum over a certain period of time. The remaining Cr, Zr and O atoms exist in a gelatinous state. During ageing, there is a continuous transition of ions from solute to gelatinous state. In addition, the deposition of coating ions is directly influenced by the substrates and their constituents. The extent of dissolution of aluminium in the conversion bath determines both Zr and Cr ion deposition. For a highly alloyed metal like AA7075, the dissolution rate is disturbed by copper and zinc.

The determination of trace oxygen in aluminium and aluminium-silicon alloy by helium-3 activation analysis

International Nuclear Information System (INIS)

Vandecasteele, C.; Goethals, P.; Kieffer, R.; Hoste, J.

1975-01-01

The determination of oxygen in aluminium and aluminium-silicon alloy by helium-3 activation is studied. The 18 F formed from oxygen is separated by distillation followed by precipitation of leadfluorochloride. The chemical yield is determined by activation in an isotopic neutron source. Concentrations of resp. 27 and 64 ng.g -1 with a precision for a single determination of resp. 30 and 13% are found in 99.5% aluminium and in aluminium-silicon (3%) alloy. (author)

Roll bonding of strained aluminium

DEFF Research Database (Denmark)

Staun, Jakob M.

2003-01-01

This report investigates roll bonding of pre-strained (å ~ 4) aluminium sheets to produce high strain material from high purity aluminium (99.996%) and commercial pure aluminium (99.6%). The degree of bonding is investigated by optical microscopy and ultrasonic scanning. Under the right...... of the cross rolled volume fraction is found. To further asses this effect, and the anisotropy, it is necessary to acquire knowledge about both texture and microstructure, e.g. by TEM. Roll bonding of pre-strained aluminium is found to be a possible alternative to ARB in the quest for ultra-fine grained...

Aluminium in foodstuffs and diets in Sweden.

Science.gov (United States)

Jorhem, L; Haegglund, G

1992-01-01

The levels of aluminium have been determined in a number of individual foodstuffs on the Swedish market and in 24 h duplicate diets collected by women living in the Stockholm area. The results show that the levels in most foods are very low and that the level in vegetables can vary by a factor 10. Beverages from aluminium cans were found to have aluminium levels not markedly different from those in glass bottles. Based on the results of the analysis of individual foods, the average Swedish daily diet was calculated to contain about 0.6 mg aluminium, whereas the mean content of the collected duplicate diets was 13 mg. A cake made from a mix containing aluminium phosphate in the baking soda was identified as the most important contributor of aluminium to the duplicate diets. Tea and aluminium utensils were estimated to increase the aluminium content of the diets by approximately 4 and 2 mg/day, respectively. The results also indicate that a considerable amount of aluminium must be introduced from other sources.

Influence of aluminium sheet surface modification on the self-piercing riveting process and the joint static lap shear strength

OpenAIRE

Li, Dezhi

2017-01-01

Self-piercing riveting (SPR) has been widely used in automotive as one of the major joining technologies for aluminium structures due to its advantages over some of the more traditional joining technologies. Research has shown that friction is a very important factor that influences both the riveting process and the joint strength for SPR, but these influences have not been fully understood. In this paper, AA5754 sheets with different surface textures, such as original with solid wax, hot wat...

78 FR 4053 - Airworthiness Directives; PILATUS Aircraft Ltd. Airplanes

Science.gov (United States)

2013-01-18

... aluminium alloy AA2024-T351. Later in production, the material specification was changed to aluminium alloy... mount fittings that are made of aluminium alloy AA2024-T351. Any engine mount fittings found to be... mount fittings made of aluminum alloy AA2024-T351 are found, within the next 90 days after February 7...

Constructions of aluminium electrolytic cells

International Nuclear Information System (INIS)

Galushkin, N.V.

1995-01-01

This chapter of monograph is devoted to constructions of aluminium electrolytic cells. Therefore, the general characteristic and classification of aluminium electrolytic cells was considered. The anode and cathode structure was studied. The lining of cathode casing, the process of collection of anode gases, electrolytic cell cover, and electrical insulation was studied as well. The installation and dismantling of aluminium electrolytic cells was described.

Radiation hardening of integrated circuits technologies

International Nuclear Information System (INIS)

Auberton-Herve, A.J.; Leray, J.L.

1991-01-01

The radiation hardening studies started in the mid decade -1960-1970. To survive the different military or space radiative environment, a new engineering science borned, to understand the degradation of electronics components. The different solutions to improve the electronic behavior in such environment, have been named radiation hardening of the technologies. Improvement of existing technologies, and qualification method have been widely studied. However, at the other hand, specific technologies was developped : The Silicon On Insulator technologies for CMOS or Bipolar. The HSOI3HD technology (supported by DGA-CEA DAM and LETI with THOMSON TMS) offers today the highest hardening level for the integration density of hundreds of thousand transistors on the same silicon. Full complex systems would be realized on a single die with a technological radiation hardening and no more system hardening

Working hardening modelization in zirconium alloys

International Nuclear Information System (INIS)

Sanchez, P.; Pochettino, Alberto A.

1999-01-01

Working hardening effects on mechanical properties and crystallographic textures formation in Zr-based alloys are studied. The hardening mechanisms for different grain deformations and topological conditions of simple crystal yield are considered. Results obtained show that the differences in the cold rolling textures (L and T textures) can be related with hardening microstructural parameters. (author)

Practical aspects of systems hardening

International Nuclear Information System (INIS)

Shepherd, W.J.

1989-01-01

Applications of hardening technology in a practical system require a balance between the factors governing affordability, producibility, and survivability of the finished design. Without careful consideration of the top-level system operating constraints, a design engineer may find himself with a survivable but overweight, unproductive, expensive design. This paper explores some lessons learned in applying hardening techniques to several laser communications programs and is intended as an introductory guide to novice designers faced with the task of hardening a space system

[Association between serum aluminium level and methylation of amyloid precursor protein gene in workers engaged in aluminium electrolysis].

Science.gov (United States)

Yang, X J; Yuan, Y Z; Niu, Q

2016-04-20

To investigate the association between serum aluminium level and methylation of the promoter region of amyloid precursor protein (APP)gene in workers engaged in aluminium electrolysis. In 2012, 366 electrolysis workers in an aluminium factory were enrolled as exposure group (working years >10 and age >40 years)and divided into low-exposure group and high-exposure group based on the median serum aluminium level. Meanwhile, 102 workers in a cement plant not exposed to aluminium were enrolled as control group. Graphite furnace atomic absorption spectrometry was used to measure serum aluminium level, methylation specific PCR was used to measure the methylation rate of the promoter region of APP gene, and ELI-SA was used to measure the protein expression of APP in lymphocytes in peripheral blood. The exposure group had a significantly higher serum aluminium level than the control group (45.07 μg/L vs 30.51 μg/L, P0.05). The multivariate logistic regression analysis showed that with reference to the control group, low aluminium exposure (OR=1.86, 95% CI 1.67~3.52)and high aluminium exposure (OR=2.98, 95% CI 1.97~4.15)were risk factors for a reduced methylation rate of the promoter region of APP gene. Reduced methylation of the promoter region of APP gene may be associated with increased serum aluminium level, and downregulated methylation of the promoter region of APP gene may accelerate APP gene transcription.

Influence of extrusion parameters on sic distribution and properties of AA6061/SiC composites produced by kobo method

Energy Technology Data Exchange (ETDEWEB)

WoĨniak, Jarosáaw; Kostecki, Marek; Broniszewski, Kamil; Olszyna, Andrzej [Faculty of Material Science and Engineering, Warsaw University of Technology, Warsaw (Poland); Bochniak, Wáodzimierz [Faculty of Non-Ferrous Metals, AGH University of Science and Technology, Cracow (Poland)

2013-07-01

The influence of extrusion parameters on reinforcements distribution and properties of AA6061+x% vol. SiC p (x=0; 2.5; 5; 7.5; 10) composites was discussed in this paper The averages size of AA6061 and SiC particles were 10.6 μ m and 0.42 μ m, respectively. The composites were consolidated via powder metallurgy processing (without the sintering) and extruded by KoBo method. The microstructure was examined on each steps of production. High values of density for all produced composites were achieved. Additionally, hardness and Young’s modulus were investigated. The best reinforcement distribution and mechanical properties were obtained for composites extruded with the highest extrusion ratio. Key words: aluminum alloy, extrusion, aged hardening, metal matrix composites, microstructure.

Identification of sigma and OMEGA phases in AA2009/SiC composites

Energy Technology Data Exchange (ETDEWEB)

Rodrigo, P., E-mail: pilar.rodrigo@urjc.e [Departamento de Ciencia e Ingenieria de Materiales, Escuela Superior de Ciencias Experimentales y Tecnologia, Universidad Rey Juan Carlos, c/Tulipan s/n, 28933 Mostoles, Madrid (Spain); Poza, P.; Utrilla, M.V.; Urena, A. [Departamento de Ciencia e Ingenieria de Materiales, Escuela Superior de Ciencias Experimentales y Tecnologia, Universidad Rey Juan Carlos, c/Tulipan s/n, 28933 Mostoles, Madrid (Spain)

2009-08-12

The microstructure evolution during ageing treatment at 170 and 190 deg. C of AA2009/SiC composites, reinforced with 15 vol.% particulates and whiskers, was studied by transmission electron microscopy. Besides theta' and S' phases, the typical hardening precipitates on Al-Cu-Mg alloys, it was found the presence of OMEGA and sigma (Al{sub 5}Cu{sub 6}Mg{sub 2}) phases in the matrix. sigma phase was only found in the matrix of particulate composite, while OMEGA phase appeared in both. This phase has not been previously observed in Al matrix composites based on conventional Al-Cu-Mg alloys.

Bumblebee pupae contain high levels of aluminium.

Science.gov (United States)

Exley, Christopher; Rotheray, Ellen; Goulson, David

2015-01-01

The causes of declines in bees and other pollinators remains an on-going debate. While recent attention has focussed upon pesticides, other environmental pollutants have largely been ignored. Aluminium is the most significant environmental contaminant of recent times and we speculated that it could be a factor in pollinator decline. Herein we have measured the content of aluminium in bumblebee pupae taken from naturally foraging colonies in the UK. Individual pupae were acid-digested in a microwave oven and their aluminium content determined using transversely heated graphite furnace atomic absorption spectrometry. Pupae were heavily contaminated with aluminium giving values between 13.4 and 193.4 μg/g dry wt. and a mean (SD) value of 51.0 (33.0) μg/g dry wt. for the 72 pupae tested. Mean aluminium content was shown to be a significant negative predictor of average pupal weight in colonies. While no other statistically significant relationships were found relating aluminium to bee or colony health, the actual content of aluminium in pupae are extremely high and demonstrate significant exposure to aluminium. Bees rely heavily on cognitive function and aluminium is a known neurotoxin with links, for example, to Alzheimer's disease in humans. The significant contamination of bumblebee pupae by aluminium raises the intriguing spectre of cognitive dysfunction playing a role in their population decline.

Long-term effects of aluminium dust inhalation.

Science.gov (United States)

Peters, Susan; Reid, Alison; Fritschi, Lin; de Klerk, Nicholas; Musk, A W Bill

2013-12-01

During the 1950s and 1960s, aluminium dust inhalation was used as a potential prophylaxis against silicosis in underground miners, including in Australia. We investigated the association between aluminium dust inhalation and cardiovascular, cerebrovascular and Alzheimer's diseases in a cohort of Australian male underground gold miners. We additionally looked at pneumoconiosis mortality to estimate the effect of the aluminium therapy. SMRs and 95% CI were calculated to compare mortality of the cohort members with that of the Western Australian male population (1961-2009). Internal comparisons on duration of aluminium dust inhalation were examined using Cox regression. Aluminium dust inhalation was reported for 647 out of 1894 underground gold miners. During 42 780 person-years of follow-up, 1577 deaths were observed. An indication of increased mortality of Alzheimer's disease among miners ever exposed to aluminium dust was found (SMR=1.38), although it was not statistically significant (95% CI 0.69 to 2.75). Rates for cardiovascular and cerebrovascular death were above population levels, but were similar for subjects with or without a history of aluminium dust inhalation. HRs suggested an increasing risk of cardiovascular disease with duration of aluminium dust inhalation (HR=1.02, 95% CI 1.00 to 1.04, per year of exposure). No difference in the association between duration of work underground and pneumoconiosis was observed between the groups with or without aluminium dust exposure. No protective effect against silicosis was observed from aluminium dust inhalation. Conversely, exposure to aluminium dust may possibly increase the risk of cardiovascular disease and dementia of the Alzheimer's type.

Influence of tool pin in friction stir welding on activated carbon reinforced aluminium metal matrix composite

Science.gov (United States)

DijuSamuel, G.; Raja Dhas, J. Edwin

2017-10-01

This paper focus on impact of tool pin in friction stir welding on activated carbon reinforced aluminium metal matrix composite. For fabrication of metal matrix composite AA6061 is used as matrix and activated carbon is used as reinforcement and it is casted using modified stir casting technique. After casting metal matrix composite has undergone various microstructure tests like SEM,EDAX and XRD. FSW is carried out in this metal matrix composite by choosing various tool pin profile like square,round,Threaded round, hexagon and taper. The quality of welded plates is measured in terms of ultimate tensile strength and hardness.

Design and analysis of aluminium brdiges

NARCIS (Netherlands)

Soetens, F.; Straalen, IJ.J. van

2004-01-01

Applications of aluminium have grown considerably in building and civil engineering the last decade, which is due to various aspects: light weight, durability and maintenance, use of extrusions. The paper starts with a short history of aluminium bridges and then focuses on aluminium bridges in the

The natural aging and precipitation hardening behaviour of Al-Mg-Si-Cu alloys with different Mg/Si ratios and Cu additions

Energy Technology Data Exchange (ETDEWEB)

Ding, Lipeng [College of Materials Science and Engineering, Chongqing University, Chongqing 400044 China (China); Jia, Zhihong, E-mail: zhihongjia@cqu.edu.cn [College of Materials Science and Engineering, Chongqing University, Chongqing 400044 China (China); Zhang, Zhiqing; Sanders, Robert E.; Liu, Qing [College of Materials Science and Engineering, Chongqing University, Chongqing 400044 China (China); Yang, Guang [Electronic Materials Research Laboratory, Key Laboratory of the Ministry of Education and International Centre for Dielectric Research, Xi’an Jiaotong University, Xi’an 710049 (China)

2015-03-11

The natural aging and artificial aging behaviours of Al-Mg-Si-Cu alloys with different Mg/Si ratios and Cu additions were investigated using Vickers microhardness measurements, differential scanning calorimetry (DSC) analysis and transmission electron microscopy (TEM) characterisation. Excess Si and Cu additions enhanced the alloy hardening ability during natural (NA) and artificial aging (AA). Alloys with low Cu and high Si contents exhibited higher precipitation hardening than alloys rich in Mg during artificial aging. In contrast, the alloys with high amounts of Cu were less dependent on the Mg/Si ratio during precipitation hardening due to their similar aging kinetics. The main precipitate phases that contributed to the peak-aging hardness were the L, Q′ and β″ phases. In the over-aging conditions, the alloys rich in Mg and Cu had finer and more numerous precipitates than their Si-rich equivalents due to the preferential precipitation of the L phase. The combination of excess Mg and high Cu resulted in an alloy with a relatively low hardness in T4 temper and a relatively higher hardness after the paint baking cycle. Thus, this alloy has good potential for use in auto body panel applications.

Recycling of aluminium swarf by direct incorporation in aluminium melts

OpenAIRE

Puga, Hélder; Barbosa, J.; Soares, Delfim; Silva, Filipe Samuel; Ribeiro, Carlos Silva

2009-01-01

The purpose of this work was to recover a standard AlSi12Cu1 alloy from machining chips inside the foundry plant, by using an environmentally friend technique to produce cast ingots with characteristics similar to those of the commercially available 2nd melt raw material. The recyclability of aluminium swarf using different melting techniques and the influence of chips preparation in the aluminium alloy recovery rate and dross production was experimentally studied and evaluated...

Irradiation damage in aluminium single crystals produced by 50-keV aluminium and copper ions

DEFF Research Database (Denmark)

Henriksen, L.; Johansen, A.; Koch, J.

1968-01-01

Aluminium single crystals, thin enough to be examined by electron microscopy, have been irradiated with 50-keV aluminium and copper ions. The irradiation fluxes were in the range 1011–1014 cm−2 s−1 and the doses were from 6 × 1012 to 6 × 1014 cm−2. Irradiation along either a or a direction produces...... rows of dislocation loops all lying parallel to one particular direction. If the aluminium target is quenched from 600 °C and annealed at room temperature prior to irradiation with aluminium ions, the rows of loops are suppressed. The amount of damage observed is considerably less than would...

Solution hardening and strain hardening at elevated temperatures

International Nuclear Information System (INIS)

Kocks, U.F.

1982-10-01

Solutes can significantly increase the rate of strain hardening; as a consequence, the saturation stress, at which strain hardening tends to cease for a given temperature and strain rate, is increased more than the yield stress: this is the major effect of solutes on strength at elevated temperatures, especially in the regime where dynamic strain-aging occurs. It is shown that local solute mobility can affect both the rate of dynamic recovery and the dislocation/dislocation interaction strength. The latter effect leads to multiplicative solution strengthening. It is explained by a new model based on repeated dislocation unlocking, in a high-temperature limit, which also rationalizes the stress dependence of static and dynamic strain-aging, and may help explain the plateau of the yield stress at elevated temperatures. 15 figures

High strength Al–Al2O3p composites: Optimization of extrusion parameters

DEFF Research Database (Denmark)

Luan, B.F.; Hansen, Niels; Godfrey, A.

2011-01-01

Composite aluminium alloys reinforced with Al2O3p particles have been produced by squeeze casting followed by hot extrusion and a precipitation hardening treatment. Good mechanical properties can be achieved, and in this paper we describe an optimization of the key processing parameters...... on an investigation of their mechanical properties and microstructure, as well as on the surface quality of the extruded samples. The evaluation shows that material with good strength, though with limited ductility, can be reliably obtained using a production route of squeeze casting, followed by hot extrusion....... The parameters investigated are the extrusion temperature, the extrusion rate and the extrusion ratio. The materials chosen are AA 2024 and AA 6061, each reinforced with 30vol.% Al2O3 particles of diameter typically in the range from 0.15 to 0.3μm. The extruded composites have been evaluated based...

Hardening Azure applications

CERN Document Server

Gaurav, Suraj

2015-01-01

Learn what it takes to build large scale, mission critical applications -hardened applications- on the Azure cloud platform. This 208 page book covers the techniques and engineering principles that every architect and developer needs to know to harden their Azure/.NET applications to ensure maximum reliability and high availability when deployed at scale. While the techniques are implemented in .NET and optimized for Azure, the principles here will also be valuable for users of other cloud-based development platforms. Applications come in a variety of forms, from simple apps that can be bui

Laser welding of aluminium alloys

OpenAIRE

Forsman, Tomas

2000-01-01

This thesis treats laser welding of aluminium alloys from a practical perspective with elements of mathematical analysis. The theoretical work has in all cases been verified experimentally. The aluminium alloys studied are from the 5xxx and 6xxx groups which are common for example in the automotive industry. Aluminium has many unique physical properties. The properties which more than others have been shown to influence the welding process is its high reflection, high thermal conductivity, lo...

Developments in the US aluminium recycling industry

Energy Technology Data Exchange (ETDEWEB)

Bolling, R N

1983-06-01

In the USA scrap recovery of aluminium has gained in importance since the war. Today its amounts to about 32% of total supply. On the other hand primary production in the US seems to have hardly any expansion possibilities. The development of the aluminium beverage can is the clearest example for recycling growth. The increased use of aluminium in passenger cars has led to very close technical and local relations of aluminium foundries and secondary smelters. The changing nature of the aluminium business caused by the growth of recycling should be recognized and made use of.

Enhancing elevated temperature strength of copper containing aluminium alloys by forming L12 Al3Zr precipitates and nucleating θ″ precipitates on them.

Science.gov (United States)

Kumar Makineni, Surendra; Sugathan, Sandeep; Meher, Subhashish; Banerjee, Rajarshi; Bhattacharya, Saswata; Kumar, Subodh; Chattopadhyay, Kamanio

2017-09-11

Strengthening by precipitation of second phase is the guiding principle for the development of a host of high strength structural alloys, in particular, aluminium alloys for transportation sector. Higher efficiency and lower emission demands use of alloys at higher operating temperatures (200 °C-250 °C) and stresses, especially in applications for engine parts. Unfortunately, most of the precipitation hardened aluminium alloys that are currently available can withstand maximum temperatures ranging from 150-200 °C. This limit is set by the onset of the rapid coarsening of the precipitates and consequent loss of mechanical properties. In this communication, we present a new approach in designing an Al-based alloy through solid state precipitation route that provides a synergistic coupling of two different types of precipitates that has enabled us to develop coarsening resistant high-temperature alloys that are stable in the temperature range of 250-300 °C with strength in excess of 260 MPa at 250 °C.

Process for the manufacture of plates containing neutron poison from aluminium and aluminium alloys

International Nuclear Information System (INIS)

Bauer, G.; Pollmann, E.; Srostlik, P.

1985-01-01

A process for guaranteeing sub-critical arrangements of nuclear fuel in tranport and/or storage containers is described, in which a homogeneous distribution of neutron poison in the aluminium matrix is guaranteed. A homogeneous mixture of aluminium powder and neutron poison powder is produced, this is pressed into plates in several stages, dried and made into hollow aluminium profiles of rectangular cross-section. The open ends of the hollow profile are then closed and this is rolled to the required dimension at 470-500 0 C. (orig./HP) [de

Chapter 1. Economic aspects of aluminium production

International Nuclear Information System (INIS)

Yanko, E.A.; Kabirov, Sh.O.; Safiev, Kh.; Azizov, B.S.; Mirpochaev, Kh.A.

2011-01-01

This article is devoted to economic aspects of aluminium production. Therefore, the perspectives of development of aluminium production, the base components of aluminium cost and economic security of enterprise are considered in this chapter.

The effect of welding parameters on the corrosion behaviour of friction stir welded AA2024-T351

DEFF Research Database (Denmark)

Jariyaboon, M; Davenport, A.J.; Ambat, Rajan

2007-01-01

The effect of welding parameters (rotation speed and travel speed) on the corrosion behaviour of friction stir welds in the high strength aluminium alloy AA2024-T351 was investigated. It was found that rotation speed plays a major role in controlling the location of corrosion attack. Localised...... intergranular attack was observed in the nugget region for low rotation speed welds, whereas for higher rotation speed welds, attack occurred predominantly in the heat-affected zone. The increase in anodic reactivity in the weld zone was due to the sensitisation of the grain boundaries leading to intergranular...... attack. Enhancement of cathodic reactivity was also found in the nugget as a result of the precipitation of S-phase. The results were compared with samples of AA2024-T351 that had been heat treated to simulate the thermal cycle associated with welding, and with samples that had been exposed to high...

Aluminium and nickel in human albumin solutions

DEFF Research Database (Denmark)

Gammelgaard, Bente; Sandberg, E

1989-01-01

Five different brands of commercially available human albumin solutions for infusion were analysed for their aluminium and nickel contents by atomic absorption spectrometry. The aluminium concentrations ranged from 12 micrograms/l to 1109 micrograms/l and the nickel concentrations ranged from 17...... micrograms/l to 77 micrograms/l. Examination of the aluminium and nickel contents of the constituents for the production of one brand showed too low levels to explain the final contamination of the product. By following the aluminium and nickel concentrations of the same brand during the production...... of a batch of albumin solution, filtration was shown to contribute to contamination, although the largest increase in aluminium as well as nickel concentrations appeared during the bulk concentrating process. To avoid health risks to certain patients, regulations should be established requiring aluminium...

Aluminium beverage can recycling

Energy Technology Data Exchange (ETDEWEB)

Lewinski, A von

1985-08-01

Canned beverages have become a controversial issue in this era of ecological sensitivity. METALL has already discussed the problem of can recycling. The present article discusses the technical aspects of aluminium can recycling. Two further articles will follow on aluminium can recycling in North America and on the results of European pilot projects.

Photochemical preparation of aluminium oxide layers via vacuum ultraviolet irradiation of a polymeric hexanoato aluminium complex

International Nuclear Information System (INIS)

Wennrich, L.; Khalil, H.; Bundesmann, C.; Decker, U.; Gerlach, J.W.; Helmstedt, U.; Manova, D.; Naumov, S.; Prager, L.

2013-01-01

By means of photochemical conversion of thin layers of a polymeric hexanoato aluminium complex as the precursor, thin aluminium oxide layers were prepared onto silicon wafers. The precursor compound was synthesized and characterized by several analytical techniques like NMR, FTIR, XPS, ICP, and found to be a polymeric aluminium-containing coordination compound which has been proposed to be a hydroxo-bridged aluminium chain with pendant hexanoyl side-chains ascertained as catena-poly[{di(κ-O,O-hexanoato)aluminium}(μ-hydroxo)] (PHAH). Thin layers deposited from a solution of PHAH in toluene onto silicon wafers were irradiated using VUV radiation from a xenon excimer lamp. The layers were characterized by XPS, XRD, XRR, and spectroscopic ellipsometry. VUV radiation with a radiant exposure of E = 36 J cm −2 led to almost carbon-free amorphous layers with a composition close to that of alumina having a density of about 2.1 g cm −3 . Thus, using the example of a polymeric aluminium complex, the potential of the photochemical conversion of metal complexes into oxides could be shown as an alternative method, in addition to sol–gel techniques, for the generation of thin plane metal-oxide layers at normal temperature and pressure. Highlights: ► A polymeric aluminium complex was synthesized and characterized by NMR, FTIR, XPS and ICP. ► Thin layers of the compound were irradiated using vacuum-UV radiation and converted to AlO x . ► Quantum-chemical calculations explain the conversion mechanism.

Aluminium-27 n.m.r. studies of aluminium fluoro complexes in dichloromethane solution: evidence for tetrafluoroaluminate anion

International Nuclear Information System (INIS)

Colton, R.; Eller, P.G.

1989-01-01

Mixed aluminium chloro/fluoro anions are formed in dichloromethane solution by the interaction of AlCl 3 and [Ph 3 PhCH 2 P] [H 2 F 3 ]. Aluminium-27 n.m.r. studies are restricted to the stoichiometric ranges F/Al from 1:1 to 3:1 and F/Al>8:1. Between these limits rapid precipitation reactions occur. In the fluoride-rich stoichiometric range there is rapid exchange on the n.m.r. time scale between the aluminium fluoro anion and free fluoride, so that a direct identification of the species by the multiplicity of the resonance is not possible. Indirect evidence strongly suggests that the aluminium species is [AlF 4 ] - . In the F/Al stoichiometry range from 1:1 to 3:1 aluminium-27 resonances were observed for all the other possible [AlCl χ F 4-χ ] - species. Studies on the aluminium iodo/fluoro system support the identification of [AlF 4 ] - , but the system is labile and the mixed iodo/fluoro species undergo rapid disproportionation. 12 refs., 1 fig

Effect of hydrogen on aluminium and aluminium alloys: A review

DEFF Research Database (Denmark)

Ambat, Rajan; Dwarakadasa, E.S.

1996-01-01

Susceptibility of aluminium and its alloys towards hydrogen embrittlement has been well established. Still a lot of confusion exists on the question of transport of hydrogen and its possible role in stress corrosion cracking. This paper reviews some of the fundamental properties of hydrogen...... in aluminium and its alloys and its effect on mechanical properties. The importance of hydrogen embrittlement over anodic dissolution to explain the stress corrosion cracking mechanism of these alloys is also examined in considerable detail. The various experimental findings concerning the link between...

Raw materials for aluminium production

International Nuclear Information System (INIS)

Galushkin, N.V.

1995-01-01

This chapter of monograph is devoted to to raw materials which used in aluminium production. Therefore, the using of alumina, and fluoride salts in aluminium production was considered. The physical properties of alumina were studied.

Study of mechanical properties on powdermetalurgy aluminium matrix composites fabricated by stamping or extrusion

International Nuclear Information System (INIS)

Busquets, D.; Gomez, L.; Amigo, V.; Salvador-Moya, M. D.

2005-01-01

We have developed composite materials from AA6061 aluminium alloy powders used as matrix and ceramics powders of boron carbide, silicon carbide and boron nitride, used as reinforcements in 2.5, 5.0, 7.5 and 10% vol. by mechanical mixing and milling in planetary mill at 360 rpm vial velocity for 4 h followed of hot stamping and extrusion process on green compacts. Mechanical properties obtained from tensile tests are influenced by the heat treatment, reinforcement fractions and nature. Moreover, these mechanical characteristic are dependent from the processing route. Optical and Scanning Electron Microscopy analysis revealed the microstructure of materials and let describe the tripartite relation; structure-processing-properties, of the developed materials. (Author) 20 refs

Electron beam welding of aluminium components

International Nuclear Information System (INIS)

Maajid, Ali; Vadali, S.K.; Maury, D.K.

2015-01-01

Aluminium is one of the most widely used materials in industries like transportation, shipbuilding, manufacturing, aerospace, nuclear, etc. The challenges in joining of aluminium are distortion, cleanliness and quality. Main difficulties faced during fusion welding of aluminium components are removal of surface oxide layer, weld porosity, high heat input requirement, distortion, hot cracking, etc. Physical properties of aluminium such as its high thermal conductivity, high coefficient of thermal expansion, no change in colour at high temperature, large difference in the melting points of the metal and its oxide (∼ 1400 °C) compound the difficulties faced during welding. Gas Tungsten Arc Welding (GTAW), Gas Metal Arc Welding (GMAW), Plasma Arc Welding (PAW), etc are generally used in industries for fusion welding of aluminium alloys. However in case of thicker jobs the above processes are not suitable due to requirements of elaborate edge preparation, preheating of jobs, fixturing to prevent distortion, etc. Moreover, precise control over the heat input during welding and weld bead penetration is not possible with above processes. Further, if heat sensitive parts are located near the weld joint then high energy density beam welding process like Electron Beam Welding (EBW) is the best possible choice for aluminium welding.This paper discusses EB welding of aluminium components, typical geometry of components, selection/optimization of welding parameters, problems faced during standardization of welding and process parameters and their remedies etc.

Effect of heating produced by welding on the microstructure and on the stress corrosion cracking susceptibility of AA7028 alloy

International Nuclear Information System (INIS)

Calatayud, A.; Rodenas, M.; Ferrer, C.; Amigo, V.; Salvador, M.D.

1997-01-01

The microstructural and stress corrosion cracking changes due to welding are studied for the AA7028 aluminium alloy. Special attention is paid to the characterization of what is known as the white zone. The influence of the delay step between quenching and aging in a T73 treatment on the microstructure and on the characteristics of the heat-affected zone (HAZ) is also studied. Finally the effect of thermal treatments applied on this zone after the welding is analysed. (Author) 7 refs

Investigating Corrosion, Wear Resistance and Friction of AA5454-O Series after its Severe Deformation by Rolling

Directory of Open Access Journals (Sweden)

Sinan SEZEK

2017-02-01

Full Text Available AA5454-O is an easily wrought, or in other words, a ductile aluminium alloy, however, its mechanical properties are inferior as compared to those of other alloys. The change taking place in corrosion resistance of AA5454-O alloy as a result of its severe plastic deformation (SPD by rolling has been investigated in this study. It has been observed that significant changes occurred in abrasion wear and corrosion resistances of AA5454-O alloy, which was severely deformed up to 80 % by rolling process. Corrosion resistance of the alloy that was severely deformed by rolling has increased. The effect of deformation rate on corrosion has been investigated by applying potentiodynamic test whereas on the other hand such change has been evidenced also through corrosion test. It has been observed that friction coefficient of severely deformed AA5454-O alloy varied by around 10 %, and that, associated with such change, its wear resistance also increased considerably. It has been determined that, as a result of severe deformation by rolling, hardness values rose in areas where the alloy was in contact with rolling surface. In this study, wear resistance of severely deformed alloy has been investigated as well. It has been observed that deformation value contributed positively to the increase in wear resistance.DOI: http://dx.doi.org/10.5755/j01.ms.23.1.14650

Influence of Microstructure and Process Conditions on Simultaneous Low-Temperature Surface Hardening and Bulk Precipitation Hardening of Nanoflex®

DEFF Research Database (Denmark)

Bottoli, Federico; Winther, Grethe; Christiansen, Thomas L.

2015-01-01

Precipitation hardening martensitic stainless steel Nanoflex was low-temperature nitrided or nitrocarburized. In these treatments, simultaneous hardening of the bulk, by precipitation hardening, and the surface by dissolving nitrogen/carbon can be obtained because the treatment temperatures...... and times for these essentially different hardening mechanisms are compatible. The effect of the processing history of the steel on the nitrided/nitrocarburized case was investigated by varying the amounts of austenite and martensite through variation of the degree of plastic deformation by tensile strain...... consisting of martensite results in the deepest nitrided case, while a shallow case develops on a microstructure consisting of austenite. For an initial microstructure consisting of both martensite and austenite a non-uniform case depth is achieved. Simultaneous bulk and surface hardening is only possible...

Chapter 2. Theoretical aspects of aluminium production

International Nuclear Information System (INIS)

Yanko, E.A.; Kabirov, Sh.O.; Safiev, Kh.; Azizov, B.S.; Mirpochaev, Kh.A.

2011-01-01

This article is devoted to theoretical aspects of aluminium production. Thus, the electrochemistry of electrolysis process, calculation of base industrial indicators of aluminium electrolytic cell, and processes occurring on anode and cathode were considered. Factors, which increase the current output and electrolytic cell productivity were studied. The side effects, including anode effect, sodium extraction on cathode, aluminium dissolution in the electrolyte, aluminium carbide formation, and influence of admixtures in the electrolyte were studied as well.

Devising Strain Hardening Models Using Kocks–Mecking Plots—A Comparison of Model Development for Titanium Aluminides and Case Hardening Steel

Directory of Open Access Journals (Sweden)

Markus Bambach

2016-08-01

Full Text Available The present study focuses on the development of strain hardening models taking into account the peculiarities of titanium aluminides. In comparison to steels, whose behavior has been studied extensively in the past, titanium aluminides possess a much larger initial work hardening rate, a sharp peak stress and pronounced softening. The work hardening behavior of a TNB-V4 (Ti–44.5Al–6.25Nb–0.8Mo–0.1B alloy is studied using isothermal hot compression tests conducted on a Gleeble 3500 simulator, and compared to the typical case hardening steel 25MoCrS4. The behavior is analyzed with the help of the Kocks-Mecking plots. In contrast to steel the TNB-V4 alloy shows a non-linear course of θ (i.e., no stage-III hardening initially and exhibits neither a plateau (stage IV hardening nor an inflection point at all deformation conditions. The present paper describes the development and application of a methodology for the design of strain hardening models for the TNB-V4 alloy and the 25CrMoS4 steel by taking the course of the Kocks-Mecking plots into account. Both models use different approaches for the hardening and softening mechanisms and accurately predict the flow stress over a wide range of deformation conditions. The methodology may hence assist in further developments of more sophisticated physically-based strain hardening models for TiAl-alloys.

GM 9540P Cyclic Accelerated Corrosion Analysis of Nonchromate Conversion Coatings on Aluminum Alloys 2024, 2219, 5083, and 7075 Using DOD Paint Systems

National Research Council Canada - National Science Library

Placzankis, Brian

2003-01-01

This study examines corrosion resistance of eight nonchromate conversion coatings versus hexavalent chromium based Alodine 1200 controls on scribed coated test panels of aluminum alloys 2024, 2219, 5083, and 7075...

Hydrogen embrittlement susceptibility of laser-hardened 4140 steel

Energy Technology Data Exchange (ETDEWEB)

Tsay, L.W.; Lin, Z.W. [Nat. Taiwan Ocean Univ., Keelung (Taiwan). Inst. of Mater. Eng.; Shiue, R.K. [Institute of Materials Sciences and Engineering, National Dong Hwa University, Hualien, Taiwan (Taiwan); Chen, C. [Institute of Materials Sciences and Engineering, National Taiwan University, Taipei, Taiwan (Taiwan)

2000-10-15

Slow strain rate tensile (SSRT) tests were performed to investigate the susceptibility to hydrogen embrittlement of laser-hardened AISI 4140 specimens in air, gaseous hydrogen and saturated H{sub 2}S solution. Experimental results indicated that round bar specimens with two parallel hardened bands on opposite sides along the loading axis (i.e. the PH specimens), exhibited a huge reduction in tensile ductility for all test environments. While circular-hardened (CH) specimens with 1 mm hardened depth and 6 mm wide within the gauge length were resistant to gaseous hydrogen embrittlement. However, fully hardened CH specimens became susceptible to hydrogen embrittlement for testing in air at a lower strain rate. The strength of CH specimens increased with decreasing the depth of hardened zones in a saturated H{sub 2}S solution. The premature failure of hardened zones in a susceptible environment caused the formation of brittle intergranular fracture and the decrease in tensile ductility. (orig.)

Scanning and transmission electron microscopy study of the microstructural changes occurring in aluminium matrix composites reinforced with SiC particles during casting and welding: interface reactions

Science.gov (United States)

Urena; Gomez De Salazar JM; Gil; Escalera; Baldonedo

1999-11-01

Processing of aluminium matrix composites (AMCs), especially those constituted by a reactive system such as Al-SiC, presents great difficulties which limit their potential applications. The interface reactivity between SiC and molten Al generates an aluminium carbide which degrades the composite properties. Scanning and transmission electron microscopes equipped with energy-dispersive X-ray spectroscopes are essential tools for determining the structure and chemistry of the Al-SiC interfaces in AMCs and changes occurring during casting and arc welding. In the present work, an aluminium-copper alloy (AA2014) reinforced with three different percentages of SiC particles was subjected to controlled remelting tests, at temperatures in the range 750-900 degrees C for 10 and 30 min. Arc welding tests using a tungsten intert gas with power inputs in the range 850-2000 W were also carried out. The results of these studies showed that during remelting there is preferential SiC particle consumption with formation of Al4C3 by interface reaction between the solid SiC particle and the molten aluminium matrix. The formation of Al4C3 by the same mechanism has also been detected in molten pools of arc welded composites. However, in this case there was formation of an almost continuous layer of Al4C3, which protects the particle against further consumption, and formation of aciculate aluminium carbide on the top weld. Both are formed by fusion and dissolution of the SiC in molten aluminium followed by reaction and precipitation of the Al4C3 during cooling.

Aluminium in brain tissue in familial Alzheimer's disease.

Science.gov (United States)

Mirza, Ambreen; King, Andrew; Troakes, Claire; Exley, Christopher

2017-03-01

The genetic predispositions which describe a diagnosis of familial Alzheimer's disease can be considered as cornerstones of the amyloid cascade hypothesis. Essentially they place the expression and metabolism of the amyloid precursor protein as the main tenet of disease aetiology. However, we do not know the cause of Alzheimer's disease and environmental factors may yet be shown to contribute towards its onset and progression. One such environmental factor is human exposure to aluminium and aluminium has been shown to be present in brain tissue in sporadic Alzheimer's disease. We have made the first ever measurements of aluminium in brain tissue from 12 donors diagnosed with familial Alzheimer's disease. The concentrations of aluminium were extremely high, for example, there were values in excess of 10μg/g tissue dry wt. in 5 of the 12 individuals. Overall, the concentrations were higher than all previous measurements of brain aluminium except cases of known aluminium-induced encephalopathy. We have supported our quantitative analyses using a novel method of aluminium-selective fluorescence microscopy to visualise aluminium in all lobes of every brain investigated. The unique quantitative data and the stunning images of aluminium in familial Alzheimer's disease brain tissue raise the spectre of aluminium's role in this devastating disease. Copyright © 2016 The Authors. Published by Elsevier GmbH.. All rights reserved.

Recent developments in advanced aircraft aluminium alloys

International Nuclear Information System (INIS)

Dursun, Tolga; Soutis, Costas

2014-01-01

Highlights: • To compete with composites, performance of aluminium alloys should be increased. • Al–Li alloys have higher strength, fracture and fatigue/corrosion resistance. • Improvements of aerospace Al alloys are due to optimised solute content and ratios. • In selecting new materials, there should be no reduction in the level of safety. • The use of hybrid materials could provide additional opportunities for Al alloys. - Abstract: Aluminium alloys have been the primary material for the structural parts of aircraft for more than 80 years because of their well known performance, well established design methods, manufacturing and reliable inspection techniques. Nearly for a decade composites have started to be used more widely in large commercial jet airliners for the fuselage, wing as well as other structural components in place of aluminium alloys due their high specific properties, reduced weight, fatigue performance and corrosion resistance. Although the increased use of composite materials reduced the role of aluminium up to some extent, high strength aluminium alloys remain important in airframe construction. Aluminium is a relatively low cost, light weight metal that can be heat treated and loaded to relatively high level of stresses, and it is one of the most easily produced of the high performance materials, which results in lower manufacturing and maintenance costs. There have been important recent advances in aluminium aircraft alloys that can effectively compete with modern composite materials. This study covers latest developments in enhanced mechanical properties of aluminium alloys, and high performance joining techniques. The mechanical properties on newly developed 2000, 7000 series aluminium alloys and new generation Al–Li alloys are compared with the traditional aluminium alloys. The advantages and disadvantages of the joining methods, laser beam welding and friction stir welding, are also discussed

Challenges in hardening technologies using shallow-trench isolation

International Nuclear Information System (INIS)

Shaneyfelt, M.R.; Dodd, P.E.; Draper, B.L.; Flores, R.S.

1998-02-01

Challenges related to radiation hardening CMOS technologies with shallow-trench isolation are explored. Results show that trench hardening can be more difficult than simply replacing the trench isolation oxide with a hardened field oxide

Toxicity of dissolved and precipitated aluminium to marine diatoms.

Science.gov (United States)

Gillmore, Megan L; Golding, Lisa A; Angel, Brad M; Adams, Merrin S; Jolley, Dianne F

2016-05-01

Localised aluminium contamination can lead to high concentrations in coastal waters, which have the potential for adverse effects on aquatic organisms. This research investigated the toxicity of 72-h exposures of aluminium to three marine diatoms (Ceratoneis closterium (formerly Nitzschia closterium), Minutocellus polymorphus and Phaeodactylum tricornutum) by measuring population growth rate inhibition and cell membrane damage (SYTOX Green) as endpoints. Toxicity was correlated to the time-averaged concentrations of different aluminium size-fractions, operationally defined as aluminium exposure varied between diatom species. C. closterium was the most sensitive species (10% inhibition of growth rate (72-h IC10) of 80 (55-100)μg Al/L (95% confidence limits)) while M. polymorphus (540 (460-600)μg Al/L) and P. tricornutum (2100 (2000-2200)μg Al/L) were less sensitive (based on measured total aluminium). Dissolved aluminium was the primary contributor to toxicity in C. closterium, while a combination of dissolved and precipitated aluminium forms contributed to toxicity in M. polymorphus. In contrast, aluminium toxicity to the most tolerant diatom P. tricornutum was due predominantly to precipitated aluminium. Preliminary investigations revealed the sensitivity of C. closterium and M. polymorphus to aluminium was influenced by initial cell density with aluminium toxicity significantly (paluminium toxicity to diatoms do not involve compromising the plasma membrane. These results indicate that marine diatoms have a broad range in sensitivity to aluminium with toxic mechanisms related to both dissolved and precipitated aluminium. Copyright © 2016 Elsevier B.V. All rights reserved.

Radiation hardened COTS-based 32-bit microprocessor

International Nuclear Information System (INIS)

Haddad, N.; Brown, R.; Cronauer, T.; Phan, H.

1999-01-01

A high performance radiation hardened 32-bit RISC microprocessor based upon a commercial single chip CPU has been developed. This paper presents the features of radiation hardened microprocessor, the methods used to radiation harden this device, the results of radiation testing, and shows that the RAD6000 is well-suited for the vast majority of space applications. (authors)

Lactobacillus plantarum CCFM639 alleviates aluminium toxicity.

Science.gov (United States)

Yu, Leilei; Zhai, Qixiao; Liu, Xiaoming; Wang, Gang; Zhang, Qiuxiang; Zhao, Jianxin; Narbad, Arjan; Zhang, Hao; Tian, Fengwei; Chen, Wei

2016-02-01

Aluminium (Al) is the most abundant metal in the earth's crust. Al exposure can cause a variety of adverse physiological effects in humans and animals. Our aim was to demonstrate that specific probiotic bacteria can play a special physiologically functional role in protection against Al toxicity in mice. Thirty strains of lactic acid bacteria (LAB) were tested for their aluminium-binding ability, aluminium tolerance, their antioxidative capacity, and their ability to survive the exposure to artificial gastrointestinal (GI) juices. Lactobacillus plantarum CCFM639 was selected for animal experiments because of its excellent performance in vitro. Forty mice were divided into four groups: control, Al only, Al plus CCFM639, and Al plus deferiprone (DFP). CCFM639 was administered at 10(9) CFU once daily for 10 days, followed by a single oral dose of aluminium chloride hexahydrate at 5.14 mg aluminium (LD50) for each mouse. The results showed that CCFM639 treatment led to a significant reduction in the mortality rates with corresponding decrease in intestinal aluminium absorption and in accumulation of aluminium in the tissues and amelioration of hepatic histopathological damage. This probiotic treatment also resulted in alleviation of hepatic, renal, and cerebral oxidative stress. The treatment of L. plantarum CCFM639 has potential as a therapeutic dietary strategy against acute aluminium toxicity.

Analytical methodologies for aluminium speciation in environmental and biological samples--a review.

Science.gov (United States)

Bi, S P; Yang, X D; Zhang, F P; Wang, X L; Zou, G W

2001-08-01

It is recognized that aluminium (Al) is a potential environmental hazard. Acidic deposition has been linked to increased Al concentrations in natural waters. Elevated levels of Al might have serious consequences for biological communities. Of particular interest is the speciation of Al in aquatic environments, because Al toxicity depends on its forms and concentrations. In this paper, advances in analytical methodologies for Al speciation in environmental and biological samples during the past five years are reviewed. Concerns about the specific problems of Al speciation and highlights of some important methods are elucidated in sections devoted to hybrid techniques (HPLC or FPLC coupled with ET-AAS, ICP-AES, or ICP-MS), flow-injection analysis (FIA), nuclear magnetic resonance (27Al NMR), electrochemical analysis, and computer simulation. More than 130 references are cited.

The Corrosion Protection of 2219-T87 Aluminum by Organic and Inorganic Zinc-Rich Primers

Science.gov (United States)

Danford, M. D.; Mendrek, M. J.; Walsh, D. W.

1995-01-01

The behavior of zinc-rich primer-coated 2219-T87 aluminum in a 3.5-percent Na-Cl was investigated using electrochemical techniques. The alternating current (ac) method of electrochemical impedance spectroscopy (EIS), in the frequency range of 0.001 to 40,000 Hz, and the direct current (dc) method of polarization resistance (PR) were used to evaluate the characteristics of an organic, epoxy zinc-rich primer and an inorganic, ethyl silicate zinc-rich primer. A dc electrochemical galvanic corrosion test was also used to determine the corrosion current of each zinc-rich primer anode coupled to a 2219-T87 aluminum cathode. Duration of the EIS/PR and galvanic testing was 21 days and 24 h, respectively. The galvanic test results demonstrated a very high galvanic current between the aluminum cathode and both zinc-rich primer anodes (37.9 pA/CM2 and 23.7 pA/CM2 for the organic and inorganic primers, respectively). The PR results demonstrated a much higher corrosion rate of the zinc in the inorganic primer than in the organic primer, due primarily to the higher porosity in the former. Based on this investigation, the inorganic zinc-rich primer appears to provide superior galvanic protection and is recommended for additional study for application in the solid rocket booster aft skirt.

Structural evolution in nanoporous anodic aluminium oxide

International Nuclear Information System (INIS)

Rocca, Emmanuel; Vantelon, Delphine; Reguer, Solenn; Mirambet, François

2012-01-01

Nanoporous and self-organized layers of aluminium alloys are used in many applications as membranes, templates for nanometric objects or corrosion protection for aluminium alloys. The use of this nanometric structure widely remains empirical, especially in the case of very small pores ( 4 into AlO 6 cluster and a partial release of sulphate ions are an important chemical transformation of the amorphous structure. This structural transformation defines the chemistry (pH and surface charge) inside the nanopores, the ageing behaviour and the possible incorporation or diffusion of chemical species in the nanostructure. Highlights: ► Investigations of local chemical environment of aluminium atoms in anodic aluminium oxide. ► The oxide structure is constituted by 2/3 of aluminium in tetrahedral coordination 1/3 in octahedral coordination. ► In contact with water, AlO 4 clusters are transformed into AlO 6 cluster and the aluminium sulphate bonds are hydrolysed. ► These transformations induce a pH decrease inside the nanostructure.

The study of intergranular corrosion in aircraft aluminium alloys using X-ray tomography

International Nuclear Information System (INIS)

Knight, S.P.; Salagaras, M.; Trueman, A.R.

2011-01-01

Research highlights: → IGC is stochastic, where initiation is statistical and growth kinetics was somewhat predictable. → Dissolved oxygen concentration was more important than the concentration of salt in the droplet. → A limiting depth occurred for AA2024, whereas no limiting depth occurs for AA7050 after 168 h exposure. → A limiting depth may be controlled by the transport of dissolved oxygen down the corrosion fissure. → A limiting IGC depth is dependent on the overpotential of the SDZ (adjacent to the grain boundary). - Abstract: Atmospheric corrosion is one of the leading causes of structural damage to aircraft. Of particular importance is pitting and intergranular corrosion, which can develop into fatigue cracks, stress corrosion cracks, or exfoliation. Therefore it is of interest to the Australian Defence Force (ADF) to understand how corrosion ensues in susceptible aircraft aluminium alloys, such as AA2024-T351 and 7050-T7451. However, there are many difficulties in measuring the extent of intergranular corrosion, since it is predominantly hidden below the surface. Traditionally, cross-sectioning has been used to view and measure the depth of attack. In the present work, 2 mm diameter pin specimens were contaminated with a droplet of 3.5% NaCl and exposed to constant humidity that resulted in intergranular corrosion. X-ray computed tomography was then used to non-destructively assess the depth and volume of corrosion both as a function of time in 97% relative humidity, and as a function of relative humidity after 168 h exposure. Both corrosion depth and volume increased with time, but there was evidence for a limiting depth in AA2024. Depth and volume also increased with relative humidity of the environment, for which the time-of-wetness and oxygen concentration of the droplets were considered the important factors in driving the corrosion process.

On residual stresses and fatigue of laser hardened steels

International Nuclear Information System (INIS)

Lin, Ru.

1992-01-01

This thesis deals with studies on residual stresses and fatigue properties of laser-transformation hardened steels. Two types of specimens, cylinders and fatigue specimens were used in the studies. The cylinders, made of Swedish steels SS 2244 and SS 2258 which correspond to AISI 4140 and AISI 52100 respectively, were locally hardened by a single scan of laser beam in the longitudinal direction, with various laser parameters. Residual stress distributions across the hardened tracks were measured by means of X-ray diffraction. The origins of residual stresses were investigated and discussed. For the fatigue specimens, including smooth and notched types made of Swedish steels SS 2244, SS 2225 and SS 1572 (similar to AISI 4140, AISI 4130 and AISI 1035, respectively), laser hardening was carried out in the gauge section. The residual stress field induced by the hardening process and the fatigue properties by plane bending fatigue test were studied. In order to investigate the stability of the residual stress field, stress measurements were also made on specimens being loaded near the fatigue limits for over 10 7 cycles. Further the concept of local fatigue strength was employed to correlate quantitatively the effect of hardness and residual stress field on the fatigue limits. In addition a group of smooth specimens of SS 2244 was induction hardened and the hardening results were compared with the corresponding laser hardened ones in terms of residual stress and fatigue behaviour. It has been found that compressive stresses exist in the hardened zone of all the specimens studied. The laser hardening condition, the specimen and how the hardening is carried out can significantly affect the residual stress field. Laser hardening can greatly improve the fatigue properties by inducing a hardened and compressed surface layer. (112 refs.)(au)

On residual stresses and fatigue of laser hardened steels

Energy Technology Data Exchange (ETDEWEB)

Lin, Ru.

1992-01-01

This thesis deals with studies on residual stresses and fatigue properties of laser-transformation hardened steels. Two types of specimens, cylinders and fatigue specimens were used in the studies. The cylinders, made of Swedish steels SS 2244 and SS 2258 which correspond to AISI 4140 and AISI 52100 respectively, were locally hardened by a single scan of laser beam in the longitudinal direction, with various laser parameters. Residual stress distributions across the hardened tracks were measured by means of X-ray diffraction. The origins of residual stresses were investigated and discussed. For the fatigue specimens, including smooth and notched types made of Swedish steels SS 2244, SS 2225 and SS 1572 (similar to AISI 4140, AISI 4130 and AISI 1035, respectively), laser hardening was carried out in the gauge section. The residual stress field induced by the hardening process and the fatigue properties by plane bending fatigue test were studied. In order to investigate the stability of the residual stress field, stress measurements were also made on specimens being loaded near the fatigue limits for over 10[sup 7] cycles. Further the concept of local fatigue strength was employed to correlate quantitatively the effect of hardness and residual stress field on the fatigue limits. In addition a group of smooth specimens of SS 2244 was induction hardened and the hardening results were compared with the corresponding laser hardened ones in terms of residual stress and fatigue behaviour. It has been found that compressive stresses exist in the hardened zone of all the specimens studied. The laser hardening condition, the specimen and how the hardening is carried out can significantly affect the residual stress field. Laser hardening can greatly improve the fatigue properties by inducing a hardened and compressed surface layer. (112 refs.)(au).

Modelling of plastic flow localization and damage development in friction stir welded 6005A aluminium alloy using physics based strain hardening law

DEFF Research Database (Denmark)

Nielsen, Kim Lau; Pardoen, Thomas; Tvergaard, Viggo

2010-01-01

of these zones was extracted from micro-tensile specimens cut parallel to the welding direction. The measured material properties and weld topology were introduced into a 3D finite element model, fully coupled with the damage model. A Voce law hardening model involving a constant stage IV is used within...

Aluminium, gallium, indium and thallium

International Nuclear Information System (INIS)

Brown, Paul L.; Ekberg, Christian

2016-01-01

Aluminium can exist in a number of oxyhydroxide mineral phases including corundum, diaspore, boehmite and gibbsite. The stability constants at zero ionic strength reported for Al(OH) 3 (aq) vary linearly with respect to the inverse of absolute temperature. A full suite of thermodynamic parameters is available for all aluminium phases and hydrolysis species. Gallium hydrolyses to a greater extent than aluminium, with the onset of hydrolysis reactions occurring just above a pHof 1. In fact, even though aluminium has the smallest ionic radius of this series of metals, it has the weakest hydrolysis species and oxide/hydroxide phases.This is due to the presence of stabilising d-orbitals in the heavier metals, gallium, indium and thallium(III). There are few available data for the stability constants of indium(III) hydrolysis species. Of those that are available, the range in the proposed stability constants covers many orders of magnitude.

GM 9540P Cyclic Accelerated Corrosion Analysis of Nonchromate Conversion Coatings on Aluminum Alloys 2024, 2219, 5083, and 7075 Using DoD Paint Systems

National Research Council Canada - National Science Library

Placzankis, Brian

2003-01-01

This study examines corrosion resistance of eight nonchromate conversion coatings versus bexavalent chromium based Alodine 1200 controls on scribed coated test panels of aluminum alloys 2024, 2219, 5083, and 7075...

Multi-cycle rolled aluminum alloy 3103 sandwiches: mechanical properties and stamp ability

Directory of Open Access Journals (Sweden)

Nosova Ekaterina

2017-01-01

Full Text Available Constructional part producing by sheet stamping of multilayer composites requires the stamping ability data. The aim of a work is to estimate mechanical properties, stamping ratio and anisotropy indexes of 2, 4, 8 and 12 layer sandwiches produced from aluminium alloy AA3103. The pieces were received by the cold rolling. Interoperation annealing was at 500°C for 1 hour. Charts of tensile strength, yield stress, elongation depending on layer thickness were composed. It was found that cold strain hardening does not disappear after annealing if the foil’s thickness become 0.4 mm and less. Microstructure analysis has shown a good contact between layers for all samples and thicker outer layers.

Challenges in LCA modelling of multiple loops for aluminium cans

DEFF Research Database (Denmark)

Niero, Monia; Olsen, Stig Irving

considered the case of closed-loop recycling for aluminium cans, where body and lid are different alloys, and discussed the abovementioned challenge. The Life Cycle Inventory (LCI) modelling of aluminium processes is traditionally based on a pure aluminium flow, therefore neglecting the presence of alloying...... elements. We included the effect of alloying elements on the LCA modelling of aluminium can recycling. First, we performed a mass balance of the main alloying elements (Mn, Fe, Si, Cu) in aluminium can recycling at increasing levels of recycling rate. The analysis distinguished between different aluminium...... packaging scrap sources (i.e. used beverage can and mixed aluminium packaging) to understand the limiting factors for multiple loop aluminium can recycling. Secondly, we performed a comparative LCA of aluminium can production and recycling in multiple loops considering the two aluminium packaging scrap...

Durability of bare and anodised aluminium in atmosphere of very different corrosivities I. Bare aluminium

International Nuclear Information System (INIS)

Gonzalez, J. A.; Escudero, E.; Lopez, V.; Simancas, J.; Morcillo, M.

2004-01-01

The behaviour of bare aluminium is studied in atmospheric exposure at 11 natural testing stations with salinity levels ranging between 2.1 and 684 mg Cl''- m''-2 d''-1. In atmospheres of low or moderate aggressivity aluminium behaves as a passive material, though the insignificant corrosion that is produced is sufficient to spoil its appearance. In contrast, at salinity levels of 50 mg Cl''- m''-2 ''-1 or above, aluminium is susceptible to pitting corrosion even in the first year of atmospheric exposure, or in the second year at salinities of ≤ 10 mg Cl''- m''-2 d''-1. For comparative purposes, results are included for aluminium protected with an anodic film of 28 μm thickness exposed at the same testing stations. A 28 μm anodic film, correctly sealed, prevents the risk of localised corrosion even in the most unfavourable situations. (Author) 23 refs

Laser Surface Hardening of Groove Edges

Science.gov (United States)

Hussain, A.; Hamdani, A. H.; Akhter, R.; Aslam, M.

2013-06-01

Surface hardening of groove-edges made of 3Cr13 Stainless Steel has been carried out using 500 W CO2 laser with a rectangular beam of 2.5×3 mm2. The processing speed was varied from 150-500 mm/min. It was seen that the hardened depth increases with increase in laser interaction time. A maximum hardened depth of around 1mm was achieved. The microhardness of the transformed zone was 2.5 times the hardness of base metal. The XRD's and microstructural analysis were also reported.

Fatigue test on aluminium bridges

NARCIS (Netherlands)

Maljaars, J.; Soetens, F.; Straalen, van IJ.J.

2005-01-01

Traffic bridges are subjected to variable loads and should therefore be checked on fatigue. Especially low weight materials, like aluminium, are sensitive to fatigue, because the variable load is a substantial part of the total load. This paper shows the structural design of an aluminium bridge

Fatal aluminium phosphide poisoning

Directory of Open Access Journals (Sweden)

Meena Mahesh Chand

2015-06-01

Full Text Available Aluminium phosphide (AlP is a cheap solid fumigant and a highly toxic pesticide which is commonly used for grain preservation. AlP has currently aroused interest with a rising number of cases in the past four decades due to increased use for agricultural and non-agricultural purposes. Its easy availability in the markets has increased also its misuse for committing suicide. Phosphine inhibits cellular oxygen utilization and can induce lipid peroxidation. Poisoning with AlP has often occurred in attempts to commit suicide, and that more often in adults than in teenagers. This is a case of suicidal consumption of aluminium phosphide by a 32-year-old young medical anesthetist. Toxicological analyses detected aluminium phosphide. We believe that free access of celphos tablets in grain markets should be prohibited by law.

Friction Welding of Aluminium and Aluminium Alloys with Steel

Directory of Open Access Journals (Sweden)

Andrzej Ambroziak

2014-01-01

Full Text Available The paper presents our actual knowledge and experience in joining dissimilar materials with the use of friction welding method. The joints of aluminium and aluminium alloys with the different types of steel were studied. The structural effects occurring during the welding process were described. The mechanical properties using, for example, (i microhardness measurements, (ii tensile tests, (iii bending tests, and (iv shearing tests were determined. In order to obtain high-quality joints the influence of different configurations of the process such as (i changing the geometry of bonding surface, (ii using the interlayer, or (iii heat treatment was analyzed. Finally, the issues related to the selection of optimal parameters of friction welding process were also investigated.

Aluminium cables in automotive applications : Prestudy of aluminium cable uses in Scania products&Failure analysis and evaluation

OpenAIRE

Man, Yu

2016-01-01

The increasing demand of light constructed vehicles as well as soaring price of copper metal owing to limited nature resources have been promoting the use of aluminium metal as an alternative conductor of automotive cables. This thesis work is to lay theoretical foundations for further research and development regarding the introduction of new automotive cables i.e. aluminium cables. Current application of automotive aluminium cables in automotive industry as well as failure analysis and eval...

Application of radioactivation analysis for determination of impurities in aluminium, raw materials and in samples from aluminium production process

International Nuclear Information System (INIS)

Vucina, L.J.

1977-01-01

Trace elements in aluminium, raw materials and in the samples from different stages of aluminium production were determined by nondestructive neutron radioactivation analysis. The samples were taken from the Bayer's process of alumina production (bauxite, red sludge and alumina), from the components of the reduction cell (anode, criolyte and AlF 3 ) and of the final product - aluminium (purity 99.5-99.7%). Under given set of conditions ten trace elements (V,La,Ga,Mn,Co,Cr,Sc,Sb,Zn and Fe) were determined in aluminium and followed through the production process. It was found that the main impurities in aluminium are iron (0.15%) and zinc (0.O6%). It has been concluded that the purity of produced aluminium depends mainly on the purity of used alumina. The second important source of contamination of aluminium is anode. The results obtained by radioactivation analysis for V, Mn, Cr and Fe fall within the ranges of concentrations of these elements determined by use of other methods (volumetry, spectrophotometry, atomic absorption). Higher values for zinc were obtained by radioactivation analysis, probably due to unsatisfactory irradiation and measuring conditions for this element. The possibilities of application of radioactivation analysis to these kinds of samples are also disscused

Hardening Embrittlement and Non-Hardening Embrittlement of Welding-Heat-Affected Zones in a Cr-Mo Low Alloy Steel

Directory of Open Access Journals (Sweden)

Yu Zhao

2018-06-01

Full Text Available The embrittlement of heat affected zones (HAZs resulting from the welding of a P-doped 2.25Cr-1Mo steel was studied by the analysis of the fracture appearance transition temperatures (FATTs of the HAZs simulated under a heat input of 45 kJ/cm with different peak temperatures. The FATTs of the HAZs both with and without tempering increased with the rise of the peak temperature. However, the FATTs were apparently lower for the tempered HAZs. For the as-welded (untempered HAZs, the FATTs were mainly affected by residual stress, martensite/austenite (M/A islands, and bainite morphology. The observed embrittlement is a hardening embrittlement. On the other hand, the FATTs of the tempered HAZs were mainly affected by phosphorus grain boundary segregation, thereby causing a non-hardening embrittlement. The results demonstrate that the hardening embrittlement of the as-welded HAZs was more severe than the non-hardening embrittlement of the tempered HAZs. Consequently, a post-weld heat treatment should be carried out if possible so as to eliminate the hardening embrittlement.

Radiation-chemical hardening of phenol-formaldehyde oligomers

International Nuclear Information System (INIS)

Shlapatskaya, V.V.; Omel'chenko, S.I.

1978-01-01

Radiation-chemical hardening of phenol formaldehyde oligomers of the resol type has been studied in the presence of furfural and diallylphthalate diluents. The samples have been hardened on an electron accelerator at an electron energy of 1.0-1.1 MeV and a dose rate of 2-3 Mrad/s. The kinetics of hardening has been studied on the yield of gel fraction within the range of absorbed doses from 7 to 400 Mrad. Radiation-chemical hardening of the studied compositions is activated with sensitizers, namely, amines, metal chlorides, and heterocyclic derivatives of metals. Furfural and diallylphthalate compositions are suitable for forming glass-fibre plastic items by the wet method and coatings under the action of ionizing radiations

Aluminium in allergen-specific subcutaneous immunotherapy--a German perspective.

Science.gov (United States)

Kramer, Matthias F; Heath, Matthew D

2014-07-16

We are living in an "aluminium age" with increasing bioavailability of the metal for approximately 125 years, contributing significantly to the aluminium body burden of humans. Over the course of life, aluminium accumulates and is stored predominantly in the lungs, bones, liver, kidneys and brain. The toxicity of aluminium in humans is briefly summarised, highlighting links and possible causal relationships between a high aluminium body burden and a number of neurological disorders and disease states. Aluminium salts have been used as depot-adjuvants successfully in essential prophylactic vaccinations for almost 100 years, with a convincing positive benefit-risk assessment which remains unchanged. However, allergen-specific immunotherapy commonly consists of administering a long-course programme of subcutaneous injections using preparations of relevant allergens. Regulatory authorities currently set aluminium limits for vaccines per dose, rather than per treatment course. Unlike prophylactic vaccinations, numerous injections with higher proportions of aluminium-adjuvant per injection are applied in subcutaneous immunotherapy (SCIT) and will significantly contribute to a higher cumulative life dose of aluminium. While the human body may cope robustly with a daily aluminium overload from the environment, regulatory cumulative threshold values in immunotherapy need further addressing. Based on the current literature, predisposing an individual to an unusually high level of aluminium, such as through subcutaneous immunotherapy, has the potential to form focal accumulations in the body with the propensity to exert forms of toxicity. Particularly in relation to longer-term health effects, the safety of aluminium adjuvants in immunotherapy remains unchallenged by health authorities - evoking the need for more consideration, guidance, and transparency on what is known and not known about its safety in long-course therapy and what measures can be taken to prevent or

Spark counting technique with an aluminium oxide film

International Nuclear Information System (INIS)

Kawai, H.; Koga, T.; Morishima, H.; Niwa, T.; Nishiwaki, Y.

1980-01-01

Automatic spark counting of etch-pits on a polycarbonate film produced by nuclear fission fragments is now used for neutron monitoring in several countries. A method was developed using an aluminium oxide film instead of a polycarbonate as the neutron detector. Aluminium oxide films were prepared as follows: A cleaned aluminium plate as an anode and a nickel plate as a cathode were immersed in dilute sulfuric acid solution and electric current flowed between the electrodes at 12degC for 10-30 minutes. Electric current density was about 10 mA/cm 2 . The aluminium plate was then kept in boiling water for 10-30 minutes for sealing. The thickness of the aluminium oxide layer formed was about 1μm. The aluminium plate attached to a plate of suitable fissionable material, such as uranium or thorium, was irradiated with neutrons and set in a usual spark counter for fission track counting. One electrode was the aluminium plate and the other was an aluminized polyester sheet. Sparked pulses were counted with a usual scaler. The advantage of using spark counting with an aluminium oxide film for neutron monitoring is rapid measurement of neutron exposure, since chemical etching which is indispensable for spark counting with a polycarbonate detector film, is not needed. (H.K.)

Steam generated conversion coating on aluminium alloys

DEFF Research Database (Denmark)

Din, Rameez Ud; Jellesen, Morten Stendahl; Ambat, Rajan

Aluminium and its alloys are widely used in aerospace industry owing to their high strength to weight ratio. The surface of aluminium under normal conditions has a thin oxide film (2.5-10 nm) responsible for its inherent corrosion resistance. This oxide film can further be converted or transformed...... into functional conversion coatings in order to enhance corrosion resistance and adhesion to paint systems. Chromium based conversion coatings have been extensively used on aluminium alloys to improve adhesion of subsequent paint layers and corrosion resistance. However, the use of hexavalent chromium is strictly...... regulated due to its toxic nature and suspected carcinogenicity. So, it is highly imperative to develop other alternatives for chrome conversion coatings. Treatment of aluminium with natural water at elevated temperatures results in the formation of different forms of aluminium oxide (γ-AlO(OH) , Al(OH)3...

Steam based conversion coating on AA6060 alloy: Effect of sodium silicate chemistry and corrosion performance

Science.gov (United States)

Din, Rameez Ud; Bordo, Kirill; Tabrizian, Naja; Jellesen, Morten Stendahl; Ambat, Rajan

2017-11-01

Surface treatment of aluminium alloy AA6060 using an industrially applicable pilot steam jet system with and without silicate chemistry has been investigated. Treatment using steam alone and steam with silicate, resulted in an oxide layer formation with thickness ∼425 nm and ∼160 nm, respectively. Moreover, the use of sodium silicate resulted in the formation of distinct microstructure and incorporation of silicate into the oxide film. These oxide films reduced the anodic activity 4 times, while the corrosion protection by silicate containing oxide was the function of its concentration. Further, in acid salt spray and filiform corrosion tests, oxide layer containing silicate exhibited two times higher corrosion resistance.

Advances in development and application of aluminium batteries

DEFF Research Database (Denmark)

Qingfeng, Li; Zhuxian, Qiu

2001-01-01

Aluminium has long attracted attention as a potential battery anode because of its high theoretical voltage and specific energy. The protective oxide layer at aluminium surface is however detrimental to its performance to achieve its reversible potential, and also causing the delayed activation o...... aluminium batteres, especially aluminium-air batteries, and a wide range of their applications from emergency power supplies, reserve batteries field portable batteries, to batteries for electric vehicles and underwater propulsion....

Alveolar proteinosis associated with aluminium dust inhalation.

Science.gov (United States)

Chew, R; Nigam, S; Sivakumaran, P

2016-08-01

Secondary alveolar proteinosis is a rare lung disease which may be triggered by a variety of inhaled particles. The diagnosis is made by detection of anti-granulocyte-macrophage colony-stimulating factor antibodies in bronchoalveolar lavage fluid, which appears milky white and contains lamellar bodies. Aluminium has been suggested as a possible cause, but there is little evidence in the literature to support this assertion. We report the case of a 46-year-old former boilermaker and boat builder who developed secondary alveolar proteinosis following sustained heavy aluminium exposure. The presence of aluminium was confirmed both by histological examination and metallurgical analysis of a mediastinal lymph node. Despite cessation of exposure to aluminium and treatment with whole-lung lavage which normally results in improvements in both symptoms and lung function, the outcome was poor and novel therapies are now being used for this patient. It may be that the natural history in aluminium-related alveolar proteinosis is different, with the metal playing a mediating role in the disease process. Our case further supports the link between aluminium and secondary alveolar proteinosis and highlights the need for measures to prevent excessive aluminium inhalation in relevant industries. © The Author 2016. Published by Oxford University Press on behalf of the Society of Occupational Medicine. All rights reserved. For Permissions, please email: journals.permissions@oup.com.

Structural heredity influence upon principles of strain wave hardening

Science.gov (United States)

Kiricheck, A. V.; Barinov, S. V.; Yashin, A. V.

2017-02-01

It was established experimentally that by penetration of a strain wave through material hardened not only the technological modes of processing, but also a technological heredity - the direction of the fibers of the original macrostructure have an influence upon the diagram of microhardness. By penetration of the strain wave along fibers, the degree of hardening the material is less, however, a product is hardened throughout its entire section mainly along fibers. In the direction of the strain waves across fibers of the original structure of material, the degree of material hardening is much higher, the depth of the hardened layer with the degree of hardening not less than 50% makes at least 3 mm. It was found that under certain conditions the strain wave can completely change the original structure of the material. Thus, a heterogeneously hardened structure characterized by the interchange of harder and more viscous areas is formed, which is beneficial for assurance of high operational properties of material.

Thermomechanical properties of radiation hardened oligoesteracrylates

International Nuclear Information System (INIS)

Lomonosova, N.V.; Chikin, Yu.A.

1984-01-01

Thermomechanical properties of radiation hardened oligoesteracrylates are studied by the methods of isothermal heating and thermal mechanics. Films of dimethacrylate of ethylene glycol, triethylene glycol (TGM-3), tetraethylene glycol, tridecaethylene glycol and TGM-3 mixture with methyl methacrylate hardened by different doses (5-150 kGy) using Co 60 installation with a dose rate of 2x10 -3 kGy/s served as a subject of the research. During oligoesteracrylate hargening a space network is formed, chain sections between lattice points of which are in a stressed state. Maximum of deformation is observed at 210-220 deg C on thermomechanical curves of samples hardened by doses > 5 kGy, which form and intensity is dependent on an absorbed dose. Presence of a high-temperature maximum on diaqrams of isometric heating of spatially cross-linked oligoesteracrylates is discovered. High thermal stability of three-dimensional network of radiation hardened oligoesteracrylates provides satisfactory tensile properties (40% of initial strength) in sample testing an elevated temperatures (200-250 deg C)

Microstructure Evolution and Mechanical Behavior of 2219 Aluminum Alloys Additively Fabricated by the Cold Metal Transfer Process

Directory of Open Access Journals (Sweden)

Xuewei Fang

2018-05-01

Full Text Available In this research, four different welding arc modes including conventional cold metal transfer (CMT, CMT-Pulse (CMT-P, CMT-Advanced (CMT-ADV, and CMT pulse advanced (CMT-PADV were used to deposit 2219-Al wire. The effects of different arc modes on porosity, pore size distribution, microstructure evolution, and mechanical properties were thoroughly investigated. The statistical analysis of the porosity and its size distribution indicated that the CMT-PADV process gave the smallest pore area percentage and pore aspect ratio, and had almost no larger pores. The results from optical microscopy, scanning electron microscopy, and fractographic morphology proved that uniform and fine equiaxed grains, evenly distributed Al2Cu second phase particles were formed during the CMT-PADV process. Furthermore, the X-ray diffraction test ascertained that the CMT-PADV sample had the smallest lattice parameter and the highest solute Cu content. Besides, the tensile strength could reach 283 MPa, the data scattering was the smallest, and the strength scattering of the sample in the horizontal direction was the shortest. In addition, the strength properties were nearly isotropic, with only 5 MPa difference in the vertical and horizontal directions. The above mentioned results indicated that the mechanical properties of 2219 aluminum alloy was improved using the CMT-PADV arc mode.

Microstructure Evolution and Mechanical Behavior of 2219 Aluminum Alloys Additively Fabricated by the Cold Metal Transfer Process.

Science.gov (United States)

Fang, Xuewei; Zhang, Lijuan; Li, Hui; Li, Chaolong; Huang, Ke; Lu, Bingheng

2018-05-16

In this research, four different welding arc modes including conventional cold metal transfer (CMT), CMT-Pulse (CMT-P), CMT-Advanced (CMT-ADV), and CMT pulse advanced (CMT-PADV) were used to deposit 2219-Al wire. The effects of different arc modes on porosity, pore size distribution, microstructure evolution, and mechanical properties were thoroughly investigated. The statistical analysis of the porosity and its size distribution indicated that the CMT-PADV process gave the smallest pore area percentage and pore aspect ratio, and had almost no larger pores. The results from optical microscopy, scanning electron microscopy, and fractographic morphology proved that uniform and fine equiaxed grains, evenly distributed Al₂Cu second phase particles were formed during the CMT-PADV process. Furthermore, the X-ray diffraction test ascertained that the CMT-PADV sample had the smallest lattice parameter and the highest solute Cu content. Besides, the tensile strength could reach 283 MPa, the data scattering was the smallest, and the strength scattering of the sample in the horizontal direction was the shortest. In addition, the strength properties were nearly isotropic, with only 5 MPa difference in the vertical and horizontal directions. The above mentioned results indicated that the mechanical properties of 2219 aluminum alloy was improved using the CMT-PADV arc mode.

Microstructure Evolution and Mechanical Behavior of 2219 Aluminum Alloys Additively Fabricated by the Cold Metal Transfer Process

Science.gov (United States)

Fang, Xuewei; Li, Hui; Li, Chaolong; Lu, Bingheng

2018-01-01

In this research, four different welding arc modes including conventional cold metal transfer (CMT), CMT-Pulse (CMT-P), CMT-Advanced (CMT-ADV), and CMT pulse advanced (CMT-PADV) were used to deposit 2219-Al wire. The effects of different arc modes on porosity, pore size distribution, microstructure evolution, and mechanical properties were thoroughly investigated. The statistical analysis of the porosity and its size distribution indicated that the CMT-PADV process gave the smallest pore area percentage and pore aspect ratio, and had almost no larger pores. The results from optical microscopy, scanning electron microscopy, and fractographic morphology proved that uniform and fine equiaxed grains, evenly distributed Al2Cu second phase particles were formed during the CMT-PADV process. Furthermore, the X-ray diffraction test ascertained that the CMT-PADV sample had the smallest lattice parameter and the highest solute Cu content. Besides, the tensile strength could reach 283 MPa, the data scattering was the smallest, and the strength scattering of the sample in the horizontal direction was the shortest. In addition, the strength properties were nearly isotropic, with only 5 MPa difference in the vertical and horizontal directions. The above mentioned results indicated that the mechanical properties of 2219 aluminum alloy was improved using the CMT-PADV arc mode. PMID:29772708

Tungsten Inert Gas and Friction Stir Welding Characteristics of 4-mm-Thick 2219-T87 Plates at Room Temperature and -196 °C

Science.gov (United States)

Lei, Xuefeng; Deng, Ying; Yin, Zhimin; Xu, Guofu

2014-06-01

2219-T87 aluminum alloy is widely used for fabricating liquid rocket propellant storage tank, due to its admirable cryogenic property. Welding is the dominant joining method in the manufacturing process of aerospace components. In this study, the tungsten inert gas welding and friction stir welding (FSW) characteristics of 4-mm-thick 2219-T87 alloy plate at room temperature (25 °C) and deep cryogenic temperature (-196 °C) were investigated by property measurements and microscopy methods. The studied 2219 base alloy exhibits a low strength plane anisotropy and excellent room temperature and cryogenic mechanical properties. The ultimate tensile strength values of TIG and FSW welding joints can reach 265 and 353 MPa at room temperature, and 342 and 438 MPa at -196 °C, respectively. The base metal consists of elongated deformed grains and many nano-scaled θ (Al2Cu) aging precipitates. Fusion zone and heat-affected zone (HAZ) of the TIG joint are characterized by coarsening dendritic grains and equiaxed recrystallized grains, respectively. The FSW-welded joint consists of the weld nugget zone, thermo-mechanically affected zone (TMAZ), and HAZ. In the weld nugget zone, a micro-scaled sub-grain structure is the main microstructure characteristic. The TMAZ and HAZ are both characterized by coarsened aging precipitates and elongated deformed grains. The excellent FSW welding properties are attributed to the preservation of the working structures and homogenous chemical compositions.

Metallurgical Mechanisms Controlling Mechanical Properties of Aluminum Alloy 2219 Produced By Electron Beam Freeform Fabrication

Science.gov (United States)

Domack, Marcia S.; Taminger, Karen M. B.; Begley, Matthew

2006-01-01

The electron beam freeform fabrication (EBF3) layer-additive manufacturing process has been developed to directly fabricate complex geometry components. EBF3 introduces metal wire into a molten pool created on the surface of a substrate by a focused electron beam. Part geometry is achieved by translating the substrate with respect to the beam to build the part one layer at a time. Tensile properties have been demonstrated for electron beam deposited aluminum and titanium alloys that are comparable to wrought products, although the microstructures of the deposits exhibit features more typical of cast material. Understanding the metallurgical mechanisms controlling mechanical properties is essential to maximizing application of the EBF3 process. In the current study, mechanical properties and resulting microstructures were examined for aluminum alloy 2219 fabricated over a range of EBF3 process variables. Material performance was evaluated based on tensile properties and results were compared with properties of Al 2219 wrought products. Unique microstructures were observed within the deposited layers and at interlayer boundaries, which varied within the deposit height due to microstructural evolution associated with the complex thermal history experienced during subsequent layer deposition. Microstructures exhibited irregularly shaped grains, typically with interior dendritic structures, which were described based on overall grain size, morphology, distribution, and dendrite spacing, and were correlated with deposition parameters. Fracture features were compared with microstructural elements to define fracture paths and aid in definition of basic processing-microstructure-property correlations.

Ion beam analysis of aluminium in thin layers

International Nuclear Information System (INIS)

Healy, M.J.F.; Pidduck, A.J.; Dollinger, G.; Gorgens, L.; Bergmaier, A.

2002-01-01

This work quantifies aluminium in thin surface and near surface layers. In one example, the layer overlies a thin gallium nitride layer on an aluminium oxide substrate and in a second example the aluminium exists just below the surface of an indium arsenide substrate. The technique of non-Rutherford elastic backscattering of protons was used for the samples where aluminum in the layer of interest needed to be resolved from aluminium in the sapphire substrate and the results were corroborated at the Technische Universitaet Muenchen using heavy ion elastic recoil detection analysis. In the second example, where it was unnecessary to isolate the signal of aluminium in the layer of interest (as the substrate contained no aluminium), then the 27 Al(d,p 01 ) 28 Al nuclear reaction was used. The elastic proton scattering cross section of aluminum was found to vary very rapidly over the energy range of interest

The aluminium content of infant formulas remains too high.

Science.gov (United States)

Chuchu, Nancy; Patel, Bhavini; Sebastian, Blaise; Exley, Christopher

2013-10-08

Recent research published in this journal highlighted the issue of the high content of aluminium in infant formulas. The expectation was that the findings would serve as a catalyst for manufacturers to address a significant problem of these, often necessary, components of infant nutrition. It is critically important that parents and other users have confidence in the safety of infant formulas and that they have reliable information to use in choosing a product with a lower content of aluminium. Herein, we have significantly extended the scope of the previous research and the aluminium content of 30 of the most widely available and often used infant formulas has been measured. Both ready-to-drink milks and milk powders were subjected to microwave digestion in the presence of 15.8 M HNO3 and 30% w/v H2O2 and the aluminium content of the digests was measured by TH GFAAS. Both ready-to-drink milks and milk powders were contaminated with aluminium. The concentration of aluminium across all milk products ranged from ca 100 to 430 μg/L. The concentration of aluminium in two soya-based milk products was 656 and 756 μg/L. The intake of aluminium from non-soya-based infant formulas varied from ca 100 to 300 μg per day. For soya-based milks it could be as high as 700 μg per day. All 30 infant formulas were contaminated with aluminium. There was no clear evidence that subsequent to the problem of aluminium being highlighted in a previous publication in this journal that contamination had been addressed and reduced. It is the opinion of the authors that regulatory and other non-voluntary methods are now required to reduce the aluminium content of infant formulas and thereby protect infants from chronic exposure to dietary aluminium.

Preparation of aluminium lakes by electrocoagulation

OpenAIRE

Prapai Pradabkham

2008-01-01

Aluminium lakes have been prepared by electrocoagulation employing aluminium as electrodes. The electrocoagulation is conducted in an aqueous alcoholic solution and is completed within one hour. The dye content in the lake ranges approximately between 4-32%.

A parametric study of laser spot size and coverage on the laser shock peening induced residual stress in thin aluminium samples

Directory of Open Access Journals (Sweden)

M. Sticchi

2015-07-01

Full Text Available Laser Shock Peening is a fatigue enhancement treatment using laser energy to induce compressive Residual Stresses (RS in the outer layers of metallic components. This work describes the variations of introduced RS-field with peen size and coverage for thin metal samples treated with under-water-LSP. The specimens under investigation were of aluminium alloy AA2024-T351, AA2139-T3, AA7050-T76 and AA7075-T6, with thickness 1.9 mm. The RS were measured by using Hole Drilling with Electronic Speckle Pattern Interferometry and X-ray Diffraction. Of particular interest are the effects of the above mentioned parameters on the zero-depth value, which gives indication of the amount of RS through the thickness, and on the value of the surface compressive stresses, which indicates the magnitude of induced stresses. A 2D-axisymmetrical Finite Element model was created for a preliminary estimation of the stress field trend. From experimental results, correlated with numerical and analytical analysis, the following conclusions can be drawn: increasing the spot size the zero-depth value increases with no significant change of the maximum compressive stress; the increase of coverage leads to significant increase of the compressive stress; thin samples of Al-alloy with low Hugoniot Elastic Limit (HEL reveal deeper compression field than alloy with higher HEL value.

Serum aluminium levels of workers in the bauxite mines.

Science.gov (United States)

de Kom, J F; Dissels, H M; van der Voet, G B; de Wolff, F A

1997-01-01

Aluminium is produced from the mineral bauxite. Occupational exposure is reported during the industrial processing of aluminium and is associated with pulmonary and neurotoxicity. However, data on exposure and toxicity of workers in the open bauxite mining industry do not exist. Therefore, a study was performed to explore aluminium exposure in employees involved in this bauxite mining process in a Surinam mine. A group of workers occupationally exposed to aluminium in an open bauxite mine were compared with a group of nonexposed wood processors. Serum aluminium was analyzed using atomic absorption spectrometry Data from the clinical chemistry of the blood and a questionnaire were used to explore determinants for aluminium exposure. No significant difference between serum aluminium in the exposed (4.4 +/- 2.0 micrograms/L, n = 27) and control group (5.1 +/- 1.5 micrograms/L, n = 27) was detected. For the serum concentration of the clinical chemical variables (calcium, citrate, and creatinine), a statistically significant difference was computed (p < or = 0.02) between the exposed and control group. All levels were slightly higher in the exposed group; no statistically significant correlations with serum aluminium were found. In this study, serum aluminium values were in the normal range, no significant difference between the groups could be detected despite long-term occupational exposure.

Argon-arc welding of heat resisting aluminium alloys

International Nuclear Information System (INIS)

Ryazantsev, V.I.; Fedoseev, V.A.

1997-01-01

Welding of aluminium heat resisting alloys of the Al-Cu-Mg system is studied. The hot-shortness of heat-resistant alloys M40, 1150 and 1151 are at the level of aluminium alloys 1201 and by 2-3 times lower as compared to the aluminium alloy AMg6. The M40, 1150 and 1151 alloys have unquestionable advantages against other know aluminium alloys only at temperatures of welded structures operation, beginning with 150-2000 deg C and especially at 250 deg C

Net shape powder processing of aluminium

International Nuclear Information System (INIS)

Schaffer, G.B.

2000-01-01

The increasing interest in light weight materials coupled to the need for cost-effective processing have combined to create a significant opportunity for aluminium powder metallurgy. Net shape processing of aluminium using the classical press-and-sinter powder metallurgy technique is a unique and important metal-forming method which is cost effective in producing complex parts at, or very close to, final dimensions. This paper provides an overview of the net shape powder processing of aluminium. Current research is critically reviewed and the future potential is briefly considered

Instabilities in power law gradient hardening materials

DEFF Research Database (Denmark)

Niordson, Christian Frithiof; Tvergaard, Viggo

2005-01-01

Tension and compression instabilities are investigated for specimens with dimensions in the micron range. A finite strain generalization of a higher order strain gradient plasticity theory is implemented in a finite element scheme capable of modeling power law hardening materials. Effects...... of gradient hardening are found to delay the onset of localization under plane strain tension, and significantly reduce strain gradients in the localized zone. For plane strain compression gradient hardening is found to increase the load-carrying capacity significantly....

Precipitation and Hardening in Magnesium Alloys

Science.gov (United States)

Nie, Jian-Feng

2012-11-01

Magnesium alloys have received an increasing interest in the past 12 years for potential applications in the automotive, aircraft, aerospace, and electronic industries. Many of these alloys are strong because of solid-state precipitates that are produced by an age-hardening process. Although some strength improvements of existing magnesium alloys have been made and some novel alloys with improved strength have been developed, the strength level that has been achieved so far is still substantially lower than that obtained in counterpart aluminum alloys. Further improvements in the alloy strength require a better understanding of the structure, morphology, orientation of precipitates, effects of precipitate morphology, and orientation on the strengthening and microstructural factors that are important in controlling the nucleation and growth of these precipitates. In this review, precipitation in most precipitation-hardenable magnesium alloys is reviewed, and its relationship with strengthening is examined. It is demonstrated that the precipitation phenomena in these alloys, especially in the very early stage of the precipitation process, are still far from being well understood, and many fundamental issues remain unsolved even after some extensive and concerted efforts made in the past 12 years. The challenges associated with precipitation hardening and age hardening are identified and discussed, and guidelines are outlined for the rational design and development of higher strength, and ultimately ultrahigh strength, magnesium alloys via precipitation hardening.

Preparation of aluminium lakes by electrocoagulation

Directory of Open Access Journals (Sweden)

Prapai Pradabkham

2008-07-01

Full Text Available Aluminium lakes have been prepared by electrocoagulation employing aluminium as electrodes. The electrocoagulation is conducted in an aqueous alcoholic solution and is completed within one hour. The dye content in the lake ranges approximately between 4-32%.

Investigation of aluminium state in some popular food, which are cooked in aluminium vessels, using spectroscopic analysis methods

International Nuclear Information System (INIS)

Al-Shahneh, M.; Saheune, Kh.

2009-01-01

Aluminium and lead elements were determined in drinking water and salt solution from chick-pea and faba-bean cooked in aluminium vessels and others from teflon for comparison using atomic absorption spectroscopy by graphite furnace. The relationship between heating time and aluminium quantities transferred to these food solutions was investigated. The lead element was determined taking into consideration the fact that this element may enter in these vessels somehow during the manufacturing process. Results show that the highest value of aluminium quantities was recorded in salt solution ( 17.022 μg/ml) without heating , followed by chick-pea solution (9.95 μg/ml), then faba-bean solution (2.81 μg/ml) when the heated period was 120 minutes. (author)

Effect of tempering on corrosion resistance of cast aluminium bronzes

International Nuclear Information System (INIS)

Aaltonen, P.; Klemetti, K.; Haenninen, H.

1985-01-01

The subject of this study is corrosion resistance of aluminium bronzes, which are copper base alloys containing aluminium up to 12% with additions of nickel, iron and manganese. The main conclutions that can be drawn are: (1) The dealloying corrosion resistance of nickel-aluminium bronze is much better than that of aluminium bronze with iron and manganese additions, but it is not immune; (2) The dealloying corrosion resistance of aluminium bronzes can be improved by appropiate heat treatments. The best properties were obtained by temperering between 600 and 800 deg C, depending on the initial microstructure; (3) In crevice conditions, where local acidification can occur, dealloying of aluminium bronzes is a consequence of the preferential attack of aluminium-rich phases. By appropriate tempering, a uniform distribution of aluminium-rich phases is obtained and the continous path for selective corrosion is not formed

The microstructural origin of work hardening stages

DEFF Research Database (Denmark)

Hughes, D. A.; Hansen, N.

2018-01-01

The strain evolution of the flow stress and work hardening rate in stages III and IV is explored by utilizing a fully described deformation microstructure. Extensive measurements by transmission electron microscopy reveal a hierarchical subdivision of grains by low angle incidental dislocation...... addition of the classical Taylor and Hall-Petch formulations. Model predictions agree closely with experimental values of flow stress and work hardening rate in stages III and IV. Strong connections between the evolutionary stages of the deformation microstructure and work hardening rates create a new...... (modern) basis for the classic problem of work hardening in metals and alloys. These connections lead the way for the future development of ultra high strength ductile metals produced via plastic deformation.(c) 2018 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved....

TIG and MIG welding of 6061 and 7020 aluminium alloys. Microstructural studies and mechanical properties

International Nuclear Information System (INIS)

Gomez de Salazar, J.M.; Urena, A.; Villauriz, E.; Manzanedo, S.; Barrena, I.

1998-01-01

The aluminium alloys of the 6XXX and 7XXX series, are actually considered of medium and high strength, and are been profusely used in different industries such as aeronautical, automotive, etc.However, its wide application as structural material needs of the proper development of their joining process. The present work describes the results obtained from the microstructural evaluation, both with optical and scanning electronic micros copies (OM) and SEM), and of the mechanical one (hardness changes) of the weld produced in the alloys using different arc welding techniques: FTAW (TIG) and GMAW (MIG). For the last one, a filler metal with a composition of Al-5Mg, AWS denomination A5.10-92 (AA5356), has been used. (Author) 5 refs

What is the risk of aluminium as a neurotoxin?

Science.gov (United States)

Exley, Christopher

2014-06-01

Aluminium is neurotoxic. Its free ion, Al(3+) (aq), is highly biologically reactive and uniquely equipped to do damage to essential cellular (neuronal) biochemistry. This unequivocal fact must be the starting point in examining the risk posed by aluminium as a neurotoxin in humans. Aluminium is present in the human brain and it accumulates with age. The most recent research demonstrates that a significant proportion of individuals older than 70 years of age have a potentially pathological accumulation of aluminium somewhere in their brain. What are the symptoms of chronic aluminium intoxication in humans? What if neurodegenerative diseases such as Alzheimer's disease are the manifestation of the risk of aluminium as a neurotoxin? How might such an (outrageous) hypothesis be tested?

Radiation hardenable coating mixture

International Nuclear Information System (INIS)

Howard, D.D.

1977-01-01

This invention relates to coatings that harden under radiation and to their compositions. Specifically, this invention concerns unsaturated urethane resins polymerisable by addition and to compositions, hardening under the effect of radiation, containing these resins. These resins feature the presence of at least one unsaturated ethylenic terminal group of structure CH 2 =C and containing the product of the reaction of an organic isocyanate compound with at least two isocyanate groups and one polyester polyol with at least two hydroxyl groups, and one unsaturated monomer compound polymerisable by addition having a single active hydrogen group reacting with the isocyanate [fr

Detection of aluminium in different culinary media using black ...

African Journals Online (AJOL)

Jacques Blessing

The interactions between food and aluminium local kitchen utensils can be a potential source of aluminium released which can ... need to be adopted to preserve consumers' health. ..... Corrosion behaviour of different ... Aluminium beverage.

There is (still too much aluminium in infant formulas

Directory of Open Access Journals (Sweden)

Burrell Shelle-Ann M

2010-08-01

Full Text Available Abstract Background Infant formulas are sophisticated milk-based feeds for infants which are used as a substitute for breast milk. Historically they are known to be contaminated by aluminium and in the past this has raised health concerns for exposed infants. We have measured the aluminium content of a number of widely used infant formulas to determine if their contamination by aluminium and consequent issues of child health persists. Methods Samples of ready-made milks and powders used to make milks were prepared by microwave digestion of acid/peroxide mixtures and their aluminium content determined by THGA. Results The concentration of aluminium in ready-made milks varied from ca 176 to 700 μg/L. The latter concentration was for a milk for preterm infants. The aluminium content of powders used to make milks varied from ca 2.4 to 4.3 μg/g. The latter content was for a soya-based formula and equated to a ready-to-drink milk concentration of 629 μg/L. Using the manufacturer's own guidelines of formula consumption the average daily ingestion of aluminium from infant formulas for a child of 6 months varied from ca 200 to 600 μg of aluminium. Generally ingestion was higher from powdered as compared to ready-made formulas. Conclusions The aluminium content of a range of well known brands of infant formulas remains high and particularly so for a product designed for preterm infants and a soya-based product designed for infants with cow's milk intolerances and allergies. Recent research demonstrating the vulnerability of infants to early exposure to aluminium serves to highlight an urgent need to reduce the aluminium content of infant formulas to as low a level as is practically possible.

Formulation of anisotropic Hill criteria for the description of an aluminium alloy behaviour during the channel die compression test

International Nuclear Information System (INIS)

Gavrus, A.; Francillette, H.

2007-01-01

During the last years the study of the plastic deformation modes and the anisotropic mechanical behaviour of aluminium alloys have been the subject of many investigations. This paper deals with a phenomenological identification of an anisotropic Hill constitutive equation of aluminium AU4G samples using a channel die compression device at room temperature. By considering the different possible orientations of the samples in the channel die device, three initial textures, named ND (normal direction Z), LD (longitudinal direction X) and TD (transverse direction Y), were defined with the corresponding stresses σND, σLD and σTD. To describe the anisotropy of the material, a quadratic Hill criteria is used. An Avrami type equation based on the mixture of the hardening and softening phenomena is used to describe variation of each stress component with the equivalent plastic strain. The identification of the parameters of the law is made using an identification software (OPTPAR) and a good correlation between the experimental stresses and computed ones is obtained. The variation of the Hill parameters with a proposed equivalent strain, describing the deformation history of the material, is analysed. Finally, using the expressions of F, G, H and N, the constitutive equation of the normal anisotropy in the plane XY is obtained

Molybdenum solubility in aluminium nitrate solutions

Energy Technology Data Exchange (ETDEWEB)

Heres, X.; Sans, D.; Bertrand, M.; Eysseric, C. [CEA, Centre de Marcoule, Nuclear Energy Division, DRCP, BP 17171, 30207 Bagnols-sur-Ceze Cedex (France); Brackx, E.; Domenger, R.; Excoffier, E. [CEA, Centre de Marcoule, Nuclear Energy Division, DTEC, BP 17171, 30207 Bagnols-sur-Ceze Cedex (France); Valery, J.F. [AREVA-NC, DOR/RDP, Paris - La Defense (France)

2016-07-01

For over 60 years, research reactors (RR or RTR for research testing reactors) have been used as neutron sources for research, radioisotope production ({sup 99}Mo/{sup 99m}Tc), nuclear medicine, materials characterization, etc... Currently, over 240 of these reactors are in operation in 56 countries. They are simpler than power reactors and operate at lower temperature (cooled to below 100 C. degrees). The fuel assemblies are typically plates or cylinders of uranium alloy and aluminium (U-Al) coated with pure aluminium. These fuels can be processed in AREVA La Hague plant after batch dissolution in concentrated nitric acid and mixing with UOX fuel streams. The aim of this study is to accurately measure the solubility of molybdenum in nitric acid solution containing high concentrations of aluminium. The higher the molybdenum solubility is, the more flexible reprocessing operations are, especially when the spent fuels contain high amounts of molybdenum. To be most representative of the dissolution process, uranium-molybdenum alloy and molybdenum metal powder were dissolved in solutions of aluminium nitrate at the nominal dissolution temperature. The experiments showed complete dissolution of metallic elements after 30 minutes long stirring, even if molybdenum metal was added in excess. After an induction period, a slow precipitation of molybdic acid occurs for about 15 hours. The data obtained show the molybdenum solubility decreases with increasing aluminium concentration. The solubility law follows an exponential relation around 40 g/L of aluminium with a high determination coefficient. Molybdenum solubility is not impacted by the presence of gadolinium, or by an increasing concentration of uranium. (authors)

Fatigue hardening and softening studies on strain hardened 18-8 austenitic stainless steel

International Nuclear Information System (INIS)

Ramakrishna Prasad, C.; Vasudevan, R.

1976-01-01

Metals when subjected to fatigue harden or soften depending on their previous mechanical history. Annealed or mildly cold worked metals are known to harden while severely cold worked metals soften when subjected to fatigue loading. In the present work samples of austenitic 18-8 steel cold worked to 11% and 22% reduction in area were mounted in a vertical pulsator and fatigued in axial tension-compression. Clear cut effects were produced and it was noticed that these depended on the extent of cold work, the amplitude as well as the number of cycles of fatigue and mean stress if any. (orig.) [de

Niobium-base grain refiner for aluminium

International Nuclear Information System (INIS)

Silva Pontes, P. da; Robert, M.H.; Cupini, N.L.

1980-01-01

A new chemical grain refiner for aluminium has been developed, using inoculation of a niobium-base compound. When a bath of molten aluminium is inoculated whith this refiner, an intermetallic aluminium-niobium compound is formed which acts as a powerful nucleant, producing extremely fine structure comparable to those obtained by means of the traditional grain refiner based on titanium and boron. It was found that the refinement of the structure depends upon the weight percentage of the new refiner inoculated as well as the time of holding the bath after inoculation and before pouring, but mainly on the inoculating temperature. (Author) [pt

Remediation of phosphate-contaminated water by electrocoagulation with aluminium, aluminium alloy and mild steel anodes.

Science.gov (United States)

Vasudevan, Subramanyan; Lakshmi, Jothinathan; Jayaraj, Jeganathan; Sozhan, Ganapathy

2009-05-30

The present study provides an electrocoagulation process for the remediation of phosphate-contaminated water using aluminium, aluminium alloy and mild steel as the anodes and stainless steel as the cathode. The various parameters like effect of anode materials, effect of pH, concentration of phosphate, current density, temperature and co-existing ions, and so forth, and the adsorption capacity was evaluated using both Freundlich and Langmuir isotherm models. The adsorption of phosphate preferably fitting the Langmuir adsorption isotherm suggests monolayer coverage of adsorbed molecules. The results showed that the maximum removal efficiency of 99% was achieved with aluminium alloy anode at a current density of 0.2 A dm(-2), at a pH of 7.0. The adsorption process follows second-order kinetics.

Effect of pulsed current welding on fatigue behaviour of high strength aluminium alloy joints

International Nuclear Information System (INIS)

Balasubramanian, V.; Ravisankar, V.; Madhusudhan Reddy, G.

2008-01-01

High strength aluminium alloys (Al-Zn-Mg-Cu alloys) have gathered wide acceptance in the fabrication of light weight structures requiring high strength-to weight ratio, such as transportable bridge girders, military vehicles, road tankers and railway transport systems. The preferred welding processes of high strength aluminium alloy are frequently gas tungsten arc welding (GTAW) process and gas metal arc welding (GMAW) process due to their comparatively easier applicability and better economy. Weld fusion zones typically exhibit coarse columnar grains because of the prevailing thermal conditions during weld metal solidification. This often results inferior weld mechanical properties and poor resistance to hot cracking. In this investigation, an attempt has been made to refine the fusion zone grains by applying pulsed current welding technique. Rolled plates of 6 mm thickness have been used as the base material for preparing single pass welded joints. Single V butt joint configuration has been prepared for joining the plates. The filler metal used for joining the plates is AA 5356 (Al-5Mg (wt%)) grade aluminium alloy. Four different welding techniques have been used to fabricate the joints and they are: (i) continuous current GTAW (CCGTAW), (ii) pulsed current GTAW (PCGTAW), (iii) continuous current GMAW (CCGMAW) and (iv) pulsed current GMAW (PCGMAW) processes. Argon (99.99% pure) has been used as the shielding gas. Fatigue properties of the welded joints have been evaluated by conducting fatigue test using rotary bending fatigue testing machine. Current pulsing leads to relatively finer and more equi-axed grain structure in gas tungsten arc (GTA) and gas metal arc (GMA) welds. In contrast, conventional continuous current welding resulted in predominantly columnar grain structures. Grain refinement is accompanied by an increase in fatigue life and endurance limit

Design and Analysis of Wind Turbine Blade Hub using Aluminium Alloy AA 6061-T6

Science.gov (United States)

Ravikumar, S.; Jaswanthvenkatram, V.; Sai kumar, Y. J. N. V.; Sohaib, S. Md.

2017-05-01

This work presents the design and analysis of horizontal axis wind turbine blade hub using different material. The hub is very crucial part of the wind turbine, which experience the loads from the blades and the loads were transmitted to the main shaft. At present wind turbine is more expensive and weights more than a million pounds, with the nacelle, rotor hub and blades accounting for most of the weight. In this work Spheroidal graphite cast iron GGG 40.3 is replaced by aluminium alloy 6061-T6 to enhance the casting properties and also to improve the strength-weight ratio. This transition of material leads to reduction in weight of the wind turbine. All the loads caused by wind and extreme loads on the blades are transferred to the hub. Considering the IEC 61400-1 standard for defining extreme loads on the hub the stress and deflection were calculated on the hub by using Finite element Analysis. Result obtained from ANSYS is compared and discussed with the existing design.

Human biomonitoring of aluminium after a single, controlled manual metal arc inert gas welding process of an aluminium-containing worksheet in nonwelders.

Science.gov (United States)

Bertram, Jens; Brand, Peter; Hartmann, Laura; Schettgen, Thomas; Kossack, Veronika; Lenz, Klaus; Purrio, Ellwyn; Reisgen, Uwe; Kraus, Thomas

2015-10-01

Several existing field studies evaluate aluminium welding works but no thoroughly controlled exposure scenario for welding fume has been described yet. This study provides information about the uptake and elimination of aluminium from welding fumes under controlled conditions. In the Aachen Workplace Simulation Laboratory, we are able to generate welding fumes of a defined particle mass concentration. We exposed 12, until then occupationally unexposed participants with aluminium-containing welding fumes of a metal inert gas (MIG) welding process of a total dust mass concentration of 2.5 mg/m(3) for 6 h. Room air filter samples were collected, and the aluminium concentration in air derived. Urine and plasma samples were collected directly before and after the 6-h lasting exposure, as well as after 1 and 7 days. Human biomonitoring methods were used to determine the aluminium content of the samples with high-resolution continuum source atomic absorption spectrometry. Urinary aluminium concentrations showed significant changes after exposure compared to preexposure levels (mean t(1) (0 h) 13.5 µg/L; mean t(2) (6 h) 23.5 µg/L). Plasma results showed the same pattern but pre-post comparison did not reach significance. We were able to detect a significant increase of the internal aluminium burden of a single MIG aluminium welding process in urine, while plasma failed significance. Biphasic elimination kinetic can be observed. The German BAT of 60 µg/g creatinine was not exceeded, and urinary aluminium returned nearly to baseline concentrations after 7 days.

Complex deformation routes for direct recycling aluminium alloy scrap via industrial hot extrusion

Science.gov (United States)

Paraskevas, Dimos; Kellens, Karel; Kampen, Carlos; Mohammadi, Amirahmad; Duflou, Joost R.

2018-05-01

This paper presents the final results of an industrial project, aiming for direct hot extrusion of wrought aluminium alloy scrap at an industrial scale. Two types of complex deformation/extrusion routes were tested for the production of the same profile, starting from AA6060 scrap in form of machining chips. More specifically scrap-based billets were extruded through: a 2-porthole and a 4-porthole die-set, modified for enhanced scrap consolidation and grain refinement. For comparison reasons, cast billets of the same alloy were extruded through the modified 2-porthole die set. The tensile testing results as well as microstructural investigations show that the 4-porthole extrusion route further improves scrap consolidation compared to the 2-porthole die output. The successful implementation of solid state recycling, directly at industrial level, indicates the technological readiness level of this research.

First Principles Study of Adsorption of Hydrogen on Typical Alloying Elements and Inclusions in Molten 2219 Al Alloy

Directory of Open Access Journals (Sweden)

Yu Liu

2017-07-01

Full Text Available To better understand the effect of the components of molten 2219 Al alloy on the hydrogen content dissolved in it, the H adsorption on various positions of alloying element clusters of Cu, Mn and Al, as well as the inclusion of Al2O3, MgO and Al4C3, were investigated by means of first principles calculation, and the thermodynamic stability of H adsorbed on each possible site was also studied on the basis of formation energy. Results show that the interaction between Al, MgO, Al4C3 and H atoms is mainly repulsive and energetically unfavorable; a favorable interaction between Cu, Mn, Al2O3 and H atoms was determined, with H being more likely to be adsorbed on the top of the third atomic layer of Cu(111, the second atomic layer of Mn(111, and the O atom in the third atomic layer of Al2O3, compared with other sites. It was found that alloying elements Cu and Mn and including Al2O3 may increase the hydrogen adsorption in the molten 2219 Al alloy with Al2O3 being the most sensitive component in this regard.

Structure-property investigations on a laser beam welded dissimilar joint of aluminium AA6056 and titanium Ti6Al4V for aeronautical applications Part I: Local gradients in microstructure, hardness and strength

Energy Technology Data Exchange (ETDEWEB)

Horstmann, M.; Ventzke, V.; Petrovski, B.; Kocak, M. [GKSS Research Centre Geesthacht (Germany). Institute of Materials Research, Materials Mechanics; Kocik, R.; Tempus, G. [AIRBUS Deutschland GmbH, Metal Technology, Bremen (Germany); Vaidya, W.V.

2009-08-15

Sheets of AA6056 and Ti6Al4V were butt-joined by inserting the Ti-sheet into the profiled Al-sheet and by melting the Al-alloy alone using a split beam Nd:YAG laser. To study microstructural effects on properties, the Al-alloy was used in two tempers; T4 followed by post weld heat treatment T6, and in T6 followed by a defined duration of natural ageing at room temperature. As a basic step for fatigue and fracture investigations, local gradients in properties of this dissimilar joint are investigated using microscopy, hardness and tensile tests. Possible sites, from which fracture may initiate, have been then identified. All property changes are found to confine to the aluminium side. An intermetallic layer, although very thin, is found to form on the interface. The changeovers, firstly between the fusion zone and the heat affected zone and secondly between the heat affected zone and the base material, are found to be associated with changes in microstructure, hardness and strength. These are identified as the possible critical sites in addition to the interface. (Abstract Copyright [2009], Wiley Periodicals, Inc.) [German] Durch eine spezielle Stossvorbereitung wurden laserstrahlgeschweisster Mischverbindungen aus den Blechwerkstoffen AA6056 und Ti6Al4V hergestellt und zwar ohne die Verwendung von Zusatzwerkstoffen. Die grosse Differenz der Schmelztemperaturen erlaubt das selektive Erschmelzen des Aluminiumwerkstoffs, der wieder um den Titanwerkstoff benetzt, sodass es zur Ausbildung einer mechanisch-stabilen und tragfaehigen Verbindung kommt. Die Al-Legierung wurde in den Waermebehandlungszustaenden T4 und T6 verschweisst, um den mikrostrukturellen Einfluss auf die Eigenschaften der Verbindungen untersuchen zu koennen. Die Prozessfolgen sahen vor, dass beim Schweissen im Zustand T4 eine Warmauslagerung, beim Schweissen im Zustand T6 eine Kaltauslagerung definierter Dauer folgte. Die Charakterisierung lokaler Eigenschaftsgradienten hinsichtlich Gefuege, Mikrohaerte

Multiply-negatively charged aluminium clusters and fullerenes

Energy Technology Data Exchange (ETDEWEB)

Walsh, Noelle

2008-07-15

Multiply negatively charged aluminium clusters and fullerenes were generated in a Penning trap using the 'electron-bath' technique. Aluminium monoanions were generated using a laser vaporisation source. After this, two-, three- and four-times negatively charged aluminium clusters were generated for the first time. This research marks the first observation of tetra-anionic metal clusters in the gas phase. Additionally, doubly-negatively charged fullerenes were generated. The smallest fullerene dianion observed contained 70 atoms. (orig.)

A review of the stages of work hardening

Energy Technology Data Exchange (ETDEWEB)

Rollett, A.D.; Kocks, U.F.

1993-07-01

Stages of work hardening are reviewed with emphasis on links between each stage. Simple quantitative descriptions are given for each stage. Similarities between stage I, easy glide, and stage IV, large strain hardening, are pointed out both in terms of magnitude of the hardening rate and of the underlying mechanism of dislocation debris accumulation. Stage II is described as an athermal hardening stage that occurs when statistical variations in the dislocation ``forest`` lead to geometrical storage of dislocations. The steadily decreasing hardening rate observed in stage III is characterized by the increasing rate of loss of dislocation density due to dynamic recovery. Stage III appears to have an asymptote to a saturation stress which is determined by the characteristics of the dislocation tangles, or cell walls. The imperfect nature of the dynamic recovery process, however, leads to the accumulation of dislocation debris and this, by analogy with stage 1, causes the apparent saturation stress to rise, thus causing stage IV.

Irradiation of aluminium alloy materials with electron beam

International Nuclear Information System (INIS)

Konno, Osamu; Masumoto, Kazuyoshi

1982-01-01

It is a theme with a room for discussion to employ the stainless steel composed of longer half-life materials for the vacuum system of accelerators, from the viewpoint of radiation exposure. Therefore, it is desirable to use aluminium of shorter half-life in place of stainless steel. As a result of investigation on the above theme in the 1.2 GeV electron linac project in Tohoku University, it has been concluded that aluminium alloy vacuum chambers can reduce exposure dose by about one or two figures as compared with stainless steel ones. Of course, aluminium alloy contains trace amounts of Mg, Si, Ti, Cr, Mn, Fe, Zn, Cu and others. Therefore, four kinds of aluminium alloy considered to be usable have been examined for induced radioactivity by electron beam irradiation. Stainless steel SUS 304 has been also irradiated for comparison. Radiation energy has been 30 MeV and 200 MeV. When stainless steel and aluminium alloy were compared, aluminium alloy was very effective for reducing surface dose in low energy irradiation. In 200 MeV irradiation, the dose ratio of aluminium alloy to stainless steel became 1/30 to 1/100 after one week, though the dose difference between these two materials became smaller in 100 days or more after irradiation. If practical inspection and repair are implemented during the period from a few days to one week after shutdown, the aluminium alloy is preferable for exposure dose reduction even in high energy irradiation. (Wakatsuki, Y.)

Introduction. Aluminium production on electrolytic cells with calcined anodes

International Nuclear Information System (INIS)

Galushkin, N.V.

1995-01-01

This chapter presents the monograph content, which includes the description of physicochemical processes in aluminium electrolytic cells, and mechanism of electrolytic aluminium obtaining. The short description of aluminium electrolytic cells construction is presented in this book as well.

Oxide growth on aluminium alloys in the presence of ammonium fluoborate

International Nuclear Information System (INIS)

Oliver, J.; Paterson, P.; Flavell, T.; Biddle, G.

1996-01-01

The aim of this study as to determine the mechanisms involved in using ammonium fluoborate as a reducing atmosphere when preheating a high magnesium content aluminium alloy. Rutherford Backscattering (RBS) has been the major technique used in the analysis of samples, it revealed significant reduction in both the diffusion of magnesium to the surface and the calculated oxide thickness in the presence of NH 4 BF 4 . At temperatures above 500 deg C in air, SEM images revealed depressions and voids due to incipient melting at various stages, around the grain boundaries. Grain boundaries effectively acted as pipes aiding the diffusion of magnesium to the surface. These results have been verified through compositional analysis with both RBS and auger electron spectroscopy (AES). Results from NH 4 BF 4 atmosphere preheat conditions showed significant improvements. It was verified experimentally that above 500 deg C , AA5182 alloys undergo incipient melting at the grain boundaries with magnesium diffusing through to the surface. 5 refs., 1 fig

Steam based conversion coating on AA6060 alloy: Effect of sodium silicate chemistry and corrosion performance

DEFF Research Database (Denmark)

Din, Rameez Ud; Bordo, Kirill; Tabrizian, Naja

2017-01-01

. Moreover, the use of sodium silicate resulted in the formation of distinct microstructure and incorporation of silicate into the oxide film. These oxide films reduced the anodic activity 4 times, while the corrosion protection by silicate containing oxide was the function of its concentration. Further......Surface treatment of aluminium alloy AA6060 using an industrially applicable pilot steam jet system with and without silicate chemistry has been investigated. Treatment using steam alone and steam with silicate, resulted in an oxide layer formation with thickness ∼425 nm and ∼160 nm, respectively......, in acid salt spray and filiform corrosion tests, oxide layer containing silicate exhibited two times higher corrosion resistance....

Aluminium allergy and granulomas induced by vaccinations for children

DEFF Research Database (Denmark)

Andersen, Rosa Marie O; Zachariae, Claus; Johansen, Jeanne Duus

2014-01-01

Vaccination with aluminium-adsorbed vaccines can induce aluminium allergy with persistent itching subcutaneous nodules at the injection site - vaccination granulomas. In this article we give an overview of childhood aluminium-adsorbed vaccines available in Denmark. Through literature studies we...

Synthesis and properties of bimetallic aluminium alkoxides

International Nuclear Information System (INIS)

Vyshinskaya, K.I.; Vasil'ev, G.A.; Vishnyakova, T.A.

1997-01-01

A single stage method of aluminium bimetallic alkoxide synthesis, which consists in activated aluminium reaction with metal salts in the relevant alcohols, has been developed. Properties of the compounds prepared are described

Beryllium electrodeposition on aluminium cathode from chloride melts

International Nuclear Information System (INIS)

Nichkov, I.F.; Novikov, E.A.; Serebryakov, G.A.; Kanashin, Yu.P.; Sardyko, G.N.

1980-01-01

Cathodic processes during beryllium deposition on liquid and solid aluminium cathodes are investigated. Mixture of sodium, potassium and beryllium chloride melts served as an lectrolyte. Beryllium ion discharge at the expense of alloy formation takes place at more positive potentials than on an indifferent cathode at low current densities ( in the case of liquid aluminium cathode). Metallographic analysis and measurements of microhardness have shown, that the cathodic product includes two phases: beryllium solid solution in aluminium and metallic beryllium. It is concluded, that aluminium-beryllium alloys with high cathodic yield by current can be obtained by the electrolytic method

Investigation process of alcoholysis of hydride aluminium-adobe

International Nuclear Information System (INIS)

Numanov, M.I.; Normatov, I.Sh.; Mirsaidov, U.M.

2001-01-01

Considering of that process of acid treatment of aluminium-adobe hydride realizes in the ethyl alcohol media it was necessary study the process of alcoholysis of AlH 3 and aluminium additives. In the end of article authors became to conclusion that deficiency of spontaneous alcoholysis of AlH 3 in adobe caused by protective action of fiber; solvate ability of LiCl and alkoxy aluminium hydride of lithium-LiCl·CO 2 H 5 OH, Li Al(OC 2 H 5 ) 4 ·nC 2 H 5 OH decreasing the expectancy of responding of alcohol with aluminium hydride

Aa Ah Nak

Science.gov (United States)

Tha, Na Gya; Wus, Thay

2017-01-01

In this article, Aa Ah Nak, the authors' methodology presents not only various reflections but also diverse contradictions about the Aa Nii language as well as language revitalization. This article explores language foundation and how the Aa Nii language revitalization is inextricably linked to the genocide and resulting historic trauma pervasive…

KS R41B. A high performance steel-aluminium composite material; KS R41B. Ein Stahl-Aluminium-Verbundwerkstoff fuer hohe Belastungen

Energy Technology Data Exchange (ETDEWEB)

Deicke, K. [KS Gleitlager GmbH (Germany). Bereich Metall; Matucha, H.; Schubert, W. [KS Gleitlager GmbH, St. Leon-Rot (Germany); Steffens, T. [KS Gleitlager GmbH, Neckarsulm (Germany)

2002-08-01

Aluminium-tin alloys have been well-known for a long time and have proved to be suitable bearing materials for crankshaft bearings for many years. The known alloy AlZn4,5SiCuPb is one of the aluminium materials capable of sustaining the highest mechanical loads. In order to achieve optimum sliding properties, it would be necessary to increase the share of the soft lead phase in the alloy. This article by KS Gleitlager GmbH shows a reasonably priced manufacturing technology for high-performance aluminium-zinc-silicon-copper alloys. (orig.) [German] Die Aluminium-Zinn-Lagerlegierungen sind seit langem bekannt und haben sich seit Jahren als Lagerwerkstoff fuer Kurbelwellenlager bewaehrt. Die Legierung AlZn4,5SiCuPb gehoert zu den mechanisch am hoechsten belastbaren Aluminium-Werkstoffen. Um optimale Gleiteigenschaften zu erzielen, muesste in der Legierung der Anteil des weichen Bleis noch weiter erhoeht werden. Dieser Beitrag der KS Gleitlager GmbH zeigt eine kostenguenstige Herstelltechnologie fuer hochbelastbare Aluminium-Zink-Silizium-Kupfer-Legierungen. (orig.)

Energy Absorption of Monolithic and Fibre Reinforced Aluminium Cylinders

NARCIS (Netherlands)

De Kanter, J.L.C.G.

2006-01-01

Summary accompanying the thesis: Energy Absorption of Monolithic and Fibre Reinforced Aluminium Cylinders by Jens de Kanter This thesis presents the investigation of the crush behaviour of both monolithic aluminium cylinders and externally fibre reinforced aluminium cylinders. The research is based

Radiation-hardened bulk Si-gate CMOS microprocessor family

International Nuclear Information System (INIS)

Stricker, R.E.; Dingwall, A.G.F.; Cohen, S.; Adams, J.R.; Slemmer, W.C.

1979-01-01

RCA and Sandia Laboratories jointly developed a radiation-hardened bulk Si-gate CMOS technology which is used to fabricate the CDP-1800 series microprocessor family. Total dose hardness of 1 x 10 6 rads (Si) and transient upset hardness of 5 x 10 8 rads (Si)/sec with no latch up at any transient level was achieved. Radiation-hardened parts manufactured to date include the CDP-1802 microprocessor, the CDP-1834 ROM, the CDP-1852 8-bit I/O port, the CDP-1856 N-bit 1 of 8 decoder, and the TCC-244 256 x 4 Static RAM. The paper is divided into three parts. In the first section, the basic fundamentals of the non-hardened C 2 L technology used for the CDP-1800 series microprocessor parts is discussed along with the primary reasons for hardening this technology. The second section discusses the major changes in the fabrication sequence that are required to produce radiation-hardened devices. The final section details the electrical performance characteristics of the hardened devices as well as the effects of radiation on device performance. Also included in this section is a discussion of the TCC-244 256 x 4 Static RAM designed jointly by RCA and Sandia Laboratories for this application

Corrosion of aluminium in copper-aluminium couples under a marine environment: Influence of polyaniline deposited onto copper

International Nuclear Information System (INIS)

Vera, Rosa; Verdugo, Patricia; Orellana, Marco; Munoz, Eduardo

2010-01-01

Research highlights: → The presence of Polyaniline in the Al-Cu system produces a decrease in the oxygen reduction reaction. → In the marine enviroment, aluminium in Al-Cu couples, suffers pitting and exfoliation. → The aluminium deterioration increases with chloride and enviromental sulphur dioxide presence, mainly when it is united to bare copper. - Abstract: In this study, we examined how aluminium corrosion in Al-Cu/PANI galvanic couples in a marine environment is influenced by deposition of polyaniline (PANI) on copper. Polarization curves and immersion assays in 0.1 M NaCl were performed. The morphologies of etched Al and corrosion products were observed by SEM, and the Al ions in solution were quantified by atomic absorption spectroscopy. A reduction in aluminium damage due to galvanic corrosion was observed as a result of decreased effective area for the oxygen reduction reaction on Cu/PANI electrode. Furthermore, an electrochemical reduction of PANI from leucoemeraldine to emeraldine base is proposed.

Aluminium hydroxide-the carrier for catalysts coating

International Nuclear Information System (INIS)

Normatov, I.Sh.; Mirsaidov, U.M.

2003-01-01

At present time several methods of receiving aluminium hydroxide are exist. But all they differ by much staging of process connected with preliminary receiving of intermediate compounds, with application of expensive metallic aluminium

Effects of aluminium surface morphology and chemical modification on wettability

DEFF Research Database (Denmark)

Rahimi, Maral; Fojan, Peter; Gurevich, Leonid

2014-01-01

-life aluminium surfaces of different morphology: unpolished aluminium, polished aluminium, and aluminium foil, were subjected to surface modification procedures which involved the formation of a layer of hydrophilic hyperbranched polyethyleneglycol via in situ polymerization, molecular vapour deposition...... of a monolayer of fluorinated silane, and a combination of those. The effect of these surface modification techniques on roughness and wettability of the aluminium surfaces was elucidated by ellipsometry, contact angle measurements and atomic force microscopy. We demonstrated that by employing different types...

Aluminium removal from water after defluoridation with the electrocoagulation process.

Science.gov (United States)

Sinha, Richa; Mathur, Sanjay; Brighu, Urmila

2015-01-01

Fluoride is the most electronegative element and has a strong affinity for aluminium. Owing to this fact, most of the techniques used for fluoride removal utilized aluminium compounds, which results in high concentrations of aluminium in treated water. In the present paper, a new approach is presented to meet the WHO guideline for residual aluminium concentration as 0.2 mg/L. In the present work, the electrocoagulation (EC) process was used for fluoride removal. It was found that aluminium content in water increases with an increase in the energy input. Therefore, experiments were optimized for a minimum energy input to achieve the target value (0.7 mg/L) of fluoride in resultant water. These optimized sets were used for further investigations of aluminium control. The experimental investigations revealed that use of bentonite clay as coagulant in clariflocculation brings down the aluminium concentration of water below the WHO guideline. Bentonite dose of 2 g/L was found to be the best for efficient removal of aluminium.

Irradiation effects in magnesium and aluminium alloys

International Nuclear Information System (INIS)

Sturcken, E.F.

1979-01-01

Effects of neutron irradiation on microstructure, mechanical properties and swelling of several magnesium and aluminium alloys were studied. The neutron fluences of 2-3 X 10 22 n/cm 2 , >0.2 MeV produced displacement doses of 20 to 45 displacements per atom (dpa). Ductility of the magnesium alloys was severely reduced by irradiation induced recrystallization and precipitation of various forms. Precipitation of transmuted silicon occurred in the aluminium alloys. However, the effect on ductility was much less than for the magnesium alloys. The magnesium and aluminium alloys had excellent resistance to swelling: The best magnesium alloy was Mg/3.0 wt% Al/0.19 wt% Ca; its density decreased by only 0.13%. The best aluminium alloy was 6063, with a density decrease of 0.22%. (Auth.)

Steam Initiated Surface Modification of Aluminium Alloys

DEFF Research Database (Denmark)

Din, Rameez Ud

The extensive demand of aluminium alloys in various industries such as in transportationis mainly due to the high strength to weight ratio, which could be translated into fuel economy and efficiency. Corrosion protection of aluminium alloys is an important aspect for all applications which includes...... the use of aluminium alloys in the painted form requiring a conversion coating to improve the adhesion. Chromate based conversion coating processes are extremely good for these purposes, however the carcinogenic and toxic nature of hexavalent chromium led to the search for more benign and eco......, crystalline nano-particles, role of steam-based treatment on adhesion of industrially applied powder coating, and investigations of a failed painted aluminium window profile due to defects in the extruded profile. Chapters 13 and 14 describe the overall discussion, conclusions and future work based...

Deformation features of aluminium in tensile tests

International Nuclear Information System (INIS)

Quadros, N.F. de.

1984-01-01

It is presented a method to analyse stress-strain curves. Plastic and elastic strains were studied. The strains were done by tensile tests in four types of materials: highly pure aluminium, pure aluminium, commercially pure aluminium and aluminium - uranium. The chemical compositions were obtained by spectroscopy analysis and neutron activation analysis. Tensile tests were carried out at three strain rates, at room temperature, 100,200, 300 and 400 0 C, with knives extensometer and strain-gages to studied the elastic strain region. A multiple spring model based on two springs model to analyse elastic strain caused by tests without extensometers, taking in account moduli of elasticity and, an interactive analysis system with graphic capability were developed. It was suggested a qualitative model to explain the quantized multielasticity of Bell. (M.C.K.) [pt

Dielectric aluminium phosphate thin films. Couches minces dielectriques de phosphate d'aluminium

Energy Technology Data Exchange (ETDEWEB)

Daviero, S. (Lab. Physicochimie des Materiaux Solides, 34 - Montpellier (France)); Avinens, C. (Lab. Physicochimie des Materiaux Solides, 34 - Montpellier (France)); Ibanez, A. (Lab. Physicochimie des Materiaux Solides, 34 - Montpellier (France)); Giuntini, J.C. (Lab. Physicochimie des Materiaux Solides, 34 -Montpellier (France)); Philippot, E. (Lab. Physicochimie des Materiaux Solides, 34 - Montpellier (France))

1993-04-01

Aluminium phosphate thin films on silicium substrate have been carried out from tributylphosphate and aluminium acetylacetonate precursors in solution through the ''pyrosol'' process. It can be observed a large range of chemical analysis in terms of experimental conditions. These thin films have been characterized by X-ray diffraction and infrared spectrometry. Their electrical characteristics, defined from direct current and alternative current measurements, are quite different to those of the crystallized phosphate and can be explained by P-O and Al-O ''dangling bond'' existence. (orig.).

Investigation of a Hardened Cement Paste Grout

DEFF Research Database (Denmark)

Esteves, Luis Pedro; Sørensen, Eigil Verner

This report documents a series of tests performed on a hardened cement paste grout delivered by the client, Det Norske Veritas A/S.......This report documents a series of tests performed on a hardened cement paste grout delivered by the client, Det Norske Veritas A/S....

[Determination of aluminium in flour foods with photometric method].

Science.gov (United States)

Ma, Lan; Zhao, Xin; Zhou, Shuang; Yang, Dajin

2012-05-01

To establish a determination method for aluminium in flour foods with photometric method. After samples being treated with microwave digestion and wet digestion, aluminium in staple flour foods was determined by photometric method. There was a good linearity of the result in the range of 0.25 - 5.0 microg/ml aluminium, r = 0.9998; limit of detection (LOD) : 2.3 ng/ml; limit of quantitation (LOQ) : 7 ng/ml. This method of determining aluminium in flour foods is simple, rapid and reliable.

Effects of Mars Atmosphere on Arc Welds: Phase 2

Science.gov (United States)

Courtright, Z. S.

2018-01-01

Gas tungsten arc welding (GTAW) is a vital fusion welding process widely used throughout the aerospace industry. Its use may be critical for the repair or manufacture of systems, rockets, or facilities on the Martian surface. Aluminum alloy AA2219-T87 and titanium alloy Ti-6Al-4V butt welds have been investigated for weldability and weld properties in a simulated Martian gas environment. The resulting simulated Martian welds were compared to welds made in a terrestrial atmosphere, all of which used argon shielding gas. It was found that GTAW is a process that may be used in a Martian gas environment, not accounting for pressure and gravitational effects, as long as adequate argon shielding gas is used to protect the weld metal. Simulated Martian welds exhibited higher hardness in all cases and higher tensile strength in the case of AA2219-T87. This has been attributed to the absorption of carbon into the fusion zone, causing carbide precipitates to form. These precipitates may act to pin dislocations upon tensile testing of AA2219-T87. Dissolved carbon may have also led to carburization, which may have caused the increase in hardness within the fusion zone of the welds. Based on the results of this experiment and other similar experiments, GTAW appears to be a promising process for welding in a Martian gas environment. Additional funding and experimentation is necessary to determine the effects of the low pressure and low gravity environment found on Mars on GTAW.

Multi-Objective Optimization of Friction Stir Welding of Aluminium Alloy Using Grey Relation Analysis with Entropy Measurement Method

Directory of Open Access Journals (Sweden)

SAURABH KUMAR GUPTA

2015-01-01

Full Text Available The present research focus on optimization of Friction Stir Welding (FSW process parameters for joining of AA6061 aluminium alloy using hybrid approach. The FSW process parameters considered are tool rotational speed, welding speed and axial force. The quality characteristics considered are tensile strength (TS and percentage of tensile elongation (TE. Taguchi based experimental design L9 orthogonal array is used for determining the experimental results. The value of weights corresponding to each quality characteristic is determined by using the entropy measurement method so that their importance can be properly explained. Analysis of Variance (ANOVA is used to determine the contribution of FSW process parameters. The confirmation tests also have been done for verifying the results.

Comparison of reactivity to a metallic disc and 2% aluminium salt in 366 children, and reproducibility over time for 241 young adults with childhood vaccine-related aluminium contact allergy.

Science.gov (United States)

Gente Lidholm, Anette; Inerot, Annica; Gillstedt, Martin; Bergfors, Elisabet; Trollfors, Birger

2018-07-01

An aluminium hydroxide-adsorbed pertussis toxoid vaccine was studied in 76 000 children in the 1990s in Gothenburg, Sweden. Long-lasting itchy subcutaneous nodules at the vaccination site were seen in 745 participants. Of 495 children with itchy nodules who were patch tested for aluminium allergy, 377 were positive. In 2007-2008, 241 of the positive children were retested. Only in one third were earlier positive results reproduced. To further describe patch test reactions to different aluminium compounds in children with vaccine-induced aluminium allergy. Positive patch test results for metallic aluminium (empty Finn Chamber) and aluminium chloride hexahydrate 2% petrolatum (pet.) were analysed in 366 children with vaccine-induced persistent itching nodules tested in 1998-2002. Of those, 241 were tested a second time (2007-2008), and the patch test results of the two aluminium preparations were analysed. Patch testing with aluminium chloride hexahydrate 2% pet. is a more sensitive way to diagnose aluminium contact allergy than patch testing with metallic aluminium. A general decrease in the strength of reactions to both aluminium preparations in 241 children tested twice was observed. Aluminium contact allergy can be diagnosed by patch testing without using metallic aluminium. © 2018 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Effect of smelt aluminium on mechanical properties of steels

International Nuclear Information System (INIS)

Ryabov, V.R.; Dykhno, I.S.; Deev, G.F.; Karikh, V.V.

1987-01-01

Effect of smelt aluminium on mechanical properties of armco-iron and 12 Kh18N10T steel is studied. It is stated that in smelt aluminium and aluminium alloy contact with armco-iron the sample ductility is decreased. Corrosion effect of smelt alluminium on (18Kh15N5AM3) steel in the form of reinforced wire in aluminium-steel KAS-1A composite material is investigted. It is stated in experiment that during smelt alluminium-steel contact interaction of heterogeneous phases takes place

Study of corrosion in aluminium using neutron radiography technique

International Nuclear Information System (INIS)

Islam, M.N.; Alam, M.K.; Saklayen, M.A.; Ahsan, M.H.; Islam, S.M.A.; Zaman, M.A.

2000-01-01

Neutron radiography technique has been adopted for detection of corrosion in aluminium by filling artificially made holes on aluminium slab with Al(OH) 3 . The contrast between the optical densities of corrosion products and aluminium slab was assessed from the densitometric measurements. Variation of optical density difference with sample thickness has also been studied. The results confirm that approximately 0.039 mm thick corrosion products having diameter 10 mm can easily be detected in 2 cm thick aluminium slab. The linear attenuation coefficient of Al(OH) 3 has been obtained as 0.9447. From the present investigation it is confirmed that film neutron radiography (NR) technique is helpful for investigation of Al(OH) 3 type corrosion product in aluminium. (author)

Numerical and experimental comparison of plastic work-hardening rules

International Nuclear Information System (INIS)

Haisler, W.E.

1977-01-01

The purpose of this paper is to describe recent numerical and experimental correlation studies of several plastic work-hardening rules. The mechanical sublayer model and the combined kinematic-isotropic hardening rules are examined and the numerical results for several structural geometries are compared to experimental results. Both monotonic and cyclic loads are considered. The governing incremental plasticity relations are developed for both work-hardening models. The combined kinematic-isotropic hardening model is developed in terms of a ratio γ which controls the relative contribution of kinematic hardening (yield surface translation) and isotropic hardening (yield surface expansion). In addition to making use of a uniaxial stress-strain curve as input data, the model allows for the input of a yield surface size vs. uniaxial plastic strain curve obtained from a cyclic uniaxial reverse loading test. The mechanical sublayer model is developed in general form and a new method for determining the sublayer parameters (stress weighting factors and yield stresses) is presented. It is demonstrated that former procedures used to obtain the sublayer parameters are inconsistent for multiaxial loading. Numerical and experimental results are presented for a cylinder, circular plate with punch, and a steel pressure vessel. The numerical results are obtained with the computer program AGGIE I. The comparison study indicates that reasonable agreement is obtained with both hardening models; the choice depending upon whether the loading is monotonic or cyclic

Effects of aluminium surface morphology and chemical modification on wettability

Energy Technology Data Exchange (ETDEWEB)

Rahimi, M., E-mail: mar@sbi.aau.dk [Department of Energy and Environment, Danish Building Research Institute, Aalborg University, A.C. Meyers Vænge 15, 2450 København SV (Denmark); Fojan, P.; Gurevich, L. [Department of Physics and Nanotechnology, Aalborg University, Skjernvej 4, DK-9220 Aalborg East (Denmark); Afshari, A. [Department of Energy and Environment, Danish Building Research Institute, Aalborg University, A.C. Meyers Vænge 15, 2450 København SV (Denmark)

2014-03-01

Highlights: • Successful surface modification procedures on aluminium samples were performed involving formation of the layer of hydrophilic hyperbranched polyethyleneglycol (PEG) via in situ polymerization, molecular vapour deposition of a monolayer of fluorinated silane, and a combination of those. • The groups of surfaces with hydrophobic behavior were found to follow the Wenzel model. • A transition from Cassie–Baxter's to Wenzel's regime was observed due to changing of the surface roughness upon mechanical polishing in aluminium samples. - Abstract: Aluminium alloys are some of the predominant metals in industrial applications such as production of heat exchangers, heat pumps. They have high heat conductivity coupled with a low specific weight. In cold working conditions, there is a risk of frost formation on the surface of aluminium in the presence of water vapour, which can lead to the deterioration of equipment performance. This work addresses the methods of surface modification of aluminium and their effect of the underlying surface morphology and wettability, which are the important parameters for frost formation. Three groups of real-life aluminium surfaces of different morphology: unpolished aluminium, polished aluminium, and aluminium foil, were subjected to surface modification procedures which involved the formation of a layer of hydrophilic hyperbranched polyethyleneglycol via in situ polymerization, molecular vapour deposition of a monolayer of fluorinated silane, and a combination of those. The effect of these surface modification techniques on roughness and wettability of the aluminium surfaces was elucidated by ellipsometry, contact angle measurements and atomic force microscopy. We demonstrated that by employing different types of surface modifications the contact angle of water droplets on aluminium samples can be varied from 12° to more than 120°. A crossover from Cassie–Baxter to Wenzel regime upon changing the surface

Spectrophotometric determination of aluminium in steel with xylenol orange

International Nuclear Information System (INIS)

Majeed, A.; Javed, N.; Khan, M.S.

1996-01-01

Spectrophotometric determination of Aluminium in steel based on colour reaction between Aluminium and xylenol orange has been carried out. Red coloured complex formed in weak acidic solution is measured for its absorbance at 550 nm. The various optimum experimental conditions for Aluminium xylenol orange (Al-Xo) complex have been studied. (author)

Wear behavior of carbon fiber/aluminium-composites during abrasive loading; Verschleissverhalten von Kohlenstoffaser/Aluminium-Verbunden unter abrasiver Beanspruchung

Energy Technology Data Exchange (ETDEWEB)

Wielage, B.; Dorner, A. [Technische Univ. Chemnitz (Germany). Lehrstuhl fuer Verbundwerkstoffe

1998-07-01

Abrasive wear resistance of aluminium is significantly improved by the reinforcement with a high volume percentage of carbon fibres. The wear of unreinforced aluminium after scratching by a diamond indenter can be described as pure microgrooving without any micro-chipping. After integration of 70 vol.-% carbon fibers the damage mechanism is considerably altered and a great amount of micro-chipping occurs. The abrasive wear is strongly influenced by the fiber orientation. The best wear resistance is observed when the fibers are orientated perpendicular to the wear surface. (orig.) [Deutsch] Die Verstaerkung von Aluminium mit einem hohen Volumengehalt endloser Kohlenstoffasern verbessert erkennbar dessen Resistenz gegenueber Abrasionsverschleiss. Der Verschleiss von unverstaerktem Aluminium infolge des Ritzens mit einem Diamantindenter erfolgt in Form von reinem Mikrofurchen ohne Spanbildung. Aufgrund der Integration von 70 Vol.-% Kohlenstoffasern wird eine erhebliche Zunahme des Schaedigungsmechanismus Mikrospanen festgestellt. Die Faserorientierung hat merklichen Einfluss auf die Sensibilitaet gegenueber Abrasion. Orientierung der anisotropen Kohlenstoffasern senkrecht zur Verschleissoberflaeche bedingt den geringsten Abrasionsverschleiss. (orig.)

Study of ionic movements during anodic oxidation of nitrogen-implanted aluminium

International Nuclear Information System (INIS)

Terwagne, G.; Lucas, S.; Bodart, F.; Sorensen, G.; Jensen, H.

1990-01-01

In recent years there has been a considerable interest in synthesizing aluminium nitrides by ion implantation in order to modify the tribological properties of aluminium. The growth of an oxide layer by anodic process on these synthesized aluminium nitrides gives an interesting oxide-on-semiconductor material with surprising dynamic and decorative properties. During the anodic oxidation, ionic movements are involved in the near-surface region of the aluminium material; these ionic movements have been studied by Rutherford backscattering spectrometry (RBS) and nuclear reaction analysis (NRA) on thin aluminium foils (7000 A) preimplanted with nitrogen and post-oxidized in an ammonium pentaborate solution. The growth of the oxide layer is reduced when the aluminium is preimplanted with nitrogen: the speed of oxidation depends on the implantation conditions (energy and fluence). Moreover, the aluminium nitride can be dissolved when all metallic aluminium staying between the surface and the AlN are consumed by the anodic process. (orig.)

Modeling of AA5083 Material-Microstructure Evolution During Butt Friction-Stir Welding

Science.gov (United States)

Grujicic, M.; Arakere, G.; Yalavarthy, H. V.; He, T.; Yen, C.-F.; Cheeseman, B. A.

2010-07-01

A concise yet a fairly comprehensive overview of the friction stir welding (FSW) process is provided. This is followed by a computational investigation in which FSW behavior of a prototypical solution-strengthened and strain-hardened aluminum alloy, AA5083-H131, is modeled using a fully coupled thermo-mechanical finite-element procedure developed in our prior study. Particular attention is given to proper modeling of the welding work-piece material behavior during the FSW process. Specifically, competition and interactions between plastic-deformation and dynamic-recrystallization processes are considered to properly account for the material-microstructure evolution in the weld nugget zone. The results showed that with proper modeling of the material behavior under high-temperature/severe-plastic-deformation conditions, significantly improved agreement can be attained between the computed and measured post-FSW residual-stress and material-strength distribution results.

Steam Assisted Accelerated Growth of Oxide Layer on Aluminium Alloys

DEFF Research Database (Denmark)

Din, Rameez Ud; Yuksel, Serkan; Jellesen, Morten Stendahl

2013-01-01

Corrosion resistance of aluminium alloys is related to the composition and morphology of the oxide film on the surface of aluminium. In this paper we investigated the use of steam on the surface modification of aluminium to produce boehmite films. The study reveals a detailed investigation...... of the effect of vapour pressure, structure of intermetallic particles and thickness of boehmite films on the corrosion behaviour of aluminium alloys....

COMPLEX SURFACE HARDENING OF STEEL ARTICLES

Directory of Open Access Journals (Sweden)

A. V. Kovalchuk

2014-01-01

Full Text Available The method of complex surface hardening of steel detailswas designed. The method is a compound of two processes of hardening: chemical heat treatment and physical vapor deposition (PVD of the coating. The result, achieved in this study is much higher, than in other work on this topic and is cumulative. The method designed can be used in mechanical engineering, medicine, energetics and is perspective for military and space technologies.

Corrosion behaviour of borated aluminium used as neutron absorber

Energy Technology Data Exchange (ETDEWEB)

Emmerich, R. [EaglePicher Technologies GmbH, Oehringen (Germany); Ensinger, W.; Enders, B. [Philipps-Univ. of Marburg, Dept. of Chemistry, Material Science Centre (Germany)

2004-07-01

The electrochemical behaviour of pure and borated aluminium was examined. Measurements were performed in two different electrolytes at 90 C containing different trace-amounts of chloride. For borated aluminium current transients, i.e. metastable depassivation events were found. It is suggested to attribute these transients to less stable passivation layers in comparison to pure aluminium.

Radiation-hardened control system

International Nuclear Information System (INIS)

Vandermolen, R.I.; Smith, S.F.; Emery, M.S.

1993-01-01

A radiation-hardened bit-slice control system with associated input/output circuits was developed to prove that programmable circuits could be constructed to successfully implement intelligent functions in a highly radioactive environment. The goal for this effort was to design and test a programmable control system that could withstand a minimum total dose of 10 7 rads (gamma). The Radiation Hardened Control System (RHCS) was tested in operation at a dose rate that ranged up to 135 krad/h, with an average total dose of 10.75 Mrads. Further testing beyond the required 10 7 rads was also conducted. RHCS performed properly through the target dose of 10 7 rads, and sporadic intermittent failures in some programmable logic devices were noted after ∼ 13 Mrads

Effects of Aluminium Sulfate on Cadmium Accumulation in Rice

International Nuclear Information System (INIS)

Khamvarn, Vararas; Boontanon, Narin; Prapagdee, Benjaphorn; Kumsopa, Acharaporn; Boonsirichai, Kanokporn

2011-06-01

Full text: Cadmium accumulation in Pathum Thani 1 and Suphan Buri 60 rice cultivars was investigated upon treatment with aluminium sulfate as a precipitant. Rice was grown hydroponically in a medium containing 4 ppm cadmium nitrate with or without 4 ppm aluminium sulfate. Root, stem with leaves and grain samples were collected and analyzed for cadmium content using atomic absorption spectroscopy and inductively coupled plasma atomic emission spectroscopy. Without the addition of aluminium sulfate, Pathum Thani 1 and Suphan Buri 60 accumulated 24.71∫ 3.14 ppm and 34.43 ∫ 4.51 ppm (dry weight of whole plant) of cadmium, respectively. With aluminium sulfate, cadmium accumulation increased to 40.66 ∫ 2.47 ppm and 62.94 ∫ 10.69 ppm, respectively. The addition of aluminium sulfate to the planting medium did not reduce cadmium accumulation but caused the rice to accumulate more cadmium especially in the shoots and grains. This observation might serve as the basis for future research on the management of agricultural areas that are contaminated with cadmium and aluminium

Volatilisation and oxidation of aluminium scraps fed into incineration furnaces

International Nuclear Information System (INIS)

Biganzoli, Laura; Gorla, Leopoldo; Nessi, Simone; Grosso, Mario

2012-01-01

Highlights: ► Aluminium packaging partitioning in MSW incineration residues is evaluated. ► The amount of aluminium packaging recoverable from the bottom ashes is evaluated. ► Aluminium packaging oxidation rate in the residues of MSW incineration is evaluated. ► 80% of aluminium cans, 51% of trays and 27% of foils can be recovered from bottom ashes. - Abstract: Ferrous and non-ferrous metal scraps are increasingly recovered from municipal solid waste incineration bottom ash and used in the production of secondary steel and aluminium. However, during the incineration process, metal scraps contained in the waste undergo volatilisation and oxidation processes, which determine a loss of their recoverable mass. The present paper evaluates the behaviour of different types of aluminium packaging materials in a full-scale waste to energy plant during standard operation. Their partitioning and oxidation level in the residues of the incineration process are evaluated, together with the amount of potentially recoverable aluminium. About 80% of post-consumer cans, 51% of trays and 27% of foils can be recovered through an advanced treatment of bottom ash combined with a melting process in the saline furnace for the production of secondary aluminium. The residual amount of aluminium concentrates in the fly ash or in the fine fraction of the bottom ash and its recovery is virtually impossible using the current eddy current separation technology. The average oxidation levels of the aluminium in the residues of the incineration process is equal to 9.2% for cans, 17.4% for trays and 58.8% for foils. The differences between the tested packaging materials are related to their thickness, mechanical strength and to the alloy.

Electron Conditioning of Technical Aluminium Surfaces

Energy Technology Data Exchange (ETDEWEB)

Le Pimpec, F

2004-09-02

The effect of electron conditioning on commercially aluminium alloys 1100 and 6063 were investigated. Contrary to the assumption that electron conditioning, if performed long enough, can reduce and stabilize the SEY to low values (= 1.3, value of many pure elements [1]), the SEY of aluminium did not go lower than 1.8. In fact, it reincreases with continued electron exposure dose.

Evaluation of mechanical property data on the 2219 aluminum alloy and application of the data to the design of liquid hydrogen tankage

Science.gov (United States)

Witzell, W. E.

1977-01-01

The potential use of thin guage 2219 aluminum alloy for airborne liquid hydrogen tankage was examined. Existing data were processed using the Newman two parameter equation, a prediction was made for the life expectancy of a hypothetical liquid hydrogen tank, and additional experimental data were generated in an attempt to correct the deficiencies in the existing data.

Aluminium leaching from red mud by filamentous fungi.

Science.gov (United States)

Urík, Martin; Bujdoš, Marek; Milová-Žiaková, Barbora; Mikušová, Petra; Slovák, Marek; Matúš, Peter

2015-11-01

This contribution investigates the efficient and environmentally friendly aluminium leaching from red mud (bauxite residue) by 17 species of filamentous fungi. Bioleaching experiments were examined in batch cultures with the red mud in static, 7-day cultivation. The most efficient fungal strains in aluminium bioleaching were Penicillium crustosum G-140 and Aspergillus niger G-10. The A. niger G-10 strain was capable to extract up to approximately 141 mg·L(-1) of aluminium from 0.2 g dry weight red mud. Chemical leaching with organic acids mixture, prepared according to A. niger G-10 strain's respective fungal excretion during cultivation, proved that organic acids significantly contribute to aluminium solubilization from red mud. Copyright © 2015 Elsevier Inc. All rights reserved.

Determination of ultratrace amounts of uranium and thorium in aluminium and aluminium alloys by electrothermal vaporization/ICP-MS

International Nuclear Information System (INIS)

Nakamura, Yasushi; Kobayashi, Yoshio; Kakurai, Yousuke

1993-01-01

A method has been developed for determining the 0.01 ng g -1 level of uranium and thorium in aluminium and aluminium alloys by electrothermal vaporization (ETV)/ICP-MS. This method was found to be significantly interfered with any matrices or other elements contained. An ion-exchange technique was therefore applied to separate uranium and thorium from aluminium and other elements. It was known that uranium are adsorbed on an anion-exchange resin and thorium are adsorbed on cation-exchange resin. However, aluminium and copper were eluted with 6 M hydrochloric acid. Dissolve the sample with hydrochloric acid containing copper which was added for analysis of pure aluminium, and oxidize with hydrogen peroxide. Concentration of hydrochloric acid in the solution was adjusted to 6 M, and then passed the solution through the mixed ion-exchange resin column. After the uranium and thorium were eluted with 1 M hydrofluoric acid-0.1 M hydrochloric acid, the solution was evaporated to dryness. It was then dissolved with 1 M hydrochloric acid. Uranium and thorium were analyzed by ETV/ICP-MS using tungsten and molybdenum boats, respectively, since the tungsten boat contained high-level thorium and the molybdenum boat contained uranium. The determination limit of uranium and thorium were 0.003 and 0.005 ng g -1 , respectively. (author)

Flow and failure of an aluminium alloy from low to high temperature and strain rate

Science.gov (United States)

Sancho, Rafael; Cendón, David; Gálvez, Francisco

2015-09-01

The mechanical behaviour of an aluminium alloy is presented in this paper. The study has been carried out to analyse the flow and failure of the aluminium alloy 7075-T73. An experimental study has been planned performing tests of un-notched and notched tensile specimens at low strain rates using a servo-hydraulic machine. High strain rate tests have been carried out using the same geometry in a Hopkinson Split Tensile Bar. The dynamic experiments at low temperature were performed using a cryogenic chamber, and the high temperature ones with a furnace, both incorporated to the Hopkinson bar. Testing temperatures ranged from - 50 ∘C to 100 ∘C and the strain rates from 10-4 s-1 to 600 s-1. The material behaviour was modelled using the Modified Johnson-Cook model and simulated using LS-DYNA. The results show that the Voce type of strain hardening is the most accurate for this material, while the traditional Johnson-Cook is not enough accurate to reproduce the necking of un-notched specimens. The failure criterion was obtained by means of the numerical simulations using the analysis of the stress triaxiality versus the strain to failure. The diameters at the failure time were measured using the images taken with an image camera, and the strain to failure was computed for un-notched and notched specimens. The numerical simulations show that the analysis of the evolution of the stress triaxiality is crucial to achieve accurate results. A material model using the Modified Johnson-Cook for flow and failure is proposed.

Hardening of niobium alloys at precrystallization annealing

International Nuclear Information System (INIS)

Vasil'eva, E.V.; Pustovalov, V.A.

1989-01-01

Niobium base alloys were investigated. It is shown that precrystallization annealing of niobium-molybdenum, niobium-vanadium and niobium-zirconium alloys elevates much more sufficiently their resistance to microplastic strains, than to macroplastic strains. Hardening effect differs sufficiently for different alloys. The maximal hardening is observed for niobium-vanadium alloys, the minimal one - for niobium-zirconium alloys

Investigations concerning the effect of aluminium toxicity on the physiology and fine structures of oat plants. Physiologische und feinstrukturelle Untersuchungen zur Aluminium-Toxizitaet an Haferpflanzen

Energy Technology Data Exchange (ETDEWEB)

Marienfeld, S.

1992-06-30

In order to test the toxicity of aluminium to plants, two-week-old oat seedlings were exposed to aluminium concentrations of 0-400 [mu]M in the culture broth. Already after 12-24 hours a decrease in longitudinal root growth is to be noted, resulting from impaired mitosis activity of the root tip. This, and the observed premature cell differentiation are not aluminium-specific but unspecific reactions to unfavourable conditions. Shoot growth is only reduced after 3-4 days, and less so. Magnesium and calcium fertilization did enhance the growth of aluminium-stressed plants, but not to the level of the control plants, although the mineral concentration in the leaves reached normal values. Phosphate concentration in the root increased because of aluminium phosphate precipitation in the cell walls, which has detoxifying effect along with aluminium fixation to negative charges in the cell walls. Aluminium remains almost quantitatively in the cell wall area of the roots and is not accumulated in the cell core. Aluminium stress causes transpiration and CO[sub 2] uptake to be impaired as a reaction to the growth depression in the root area, even before the mineral concentration in the shoots is lowered. Later there follow chlorophyll depletion, chloroplast degradation, and a reduction of the leaf area. (UWA)

Friction stir welding (FSW of aluminium foam sandwich panels

Directory of Open Access Journals (Sweden)

M. Bušić

2016-07-01

Full Text Available The article focuses on the influence of welding speed and tool tilt angle upon the mechanical properties at the friction stir welding of aluminium foam sandwich panels. Double side welding was used for producing butt welds of aluminium sandwich panels applying insertion of extruded aluminium profile. Such insertion provided lower pressure of the tool upon the aluminium panels, providing also sufficient volume of the material required for the weldment formation. Ultimate tensile strength and flexural strength for three-point bending test have been determined for samples taken from the welded joints. Results have confirmed anticipated effects of independent variables.

Microstructure and pitting corrosion of friction stir welded joints in 2219-O aluminum alloy thick plate

International Nuclear Information System (INIS)

Xu Weifeng; Liu Jinhe

2009-01-01

Effect of welding parameters on the microstructure and pitting corrosion of different positions along the thickness of weld nugget zone in friction stir welded 2219-O aluminum alloy plate was investigated using scanning electron microscopy (SEM), polarization experiment and electrochemical impedance tests (EIS). It was found that the material presents significant passivation and the top has best corrosion resistance compared to the bottom and base material. Corrosion resistance decreases with the increase of traverse speed from 60 to 100 mm/min at rotary speed 400 rpm. Corrosion resistance at rotary speed 600 rpm is lower than that at 500 rpm.

Surface treatments for aluminium alloys

Science.gov (United States)

Ardelean, M.; Lascău, S.; Ardelean, E.; Josan, A.

2018-01-01

Typically, in contact with the atmosphere, the aluminium surface is covered with an aluminium oxide layer, with a thickness of less than 1-2μm. Due to its low thickness, high porosity and low mechanical strength, this layer does not protect the metal from corrosion. Anodizing for protective and decorative purposes is the most common method of superficial oxidation processes and is carried out through anodic oxidation. The oxide films, resulted from anodizing, are porous, have a thickness of 20-50μm, and are heat-resistant, stable to water vapour and other corrosion agents. Hard anodizing complies with the same obtains principles as well as decorative and protective anodization. The difference is in that hard anodizing is achieved at low temperatures and high intensity of electric current. In the paper are presented the results of decorative and hard anodization for specimens made from several aluminium alloys in terms of the appearance of the specimens and of the thickness of the anodized.

Accumulation of Aluminium and Physiological Status of Tree Foliage in the Vicinity of a Large Aluminium Smelter

Directory of Open Access Journals (Sweden)

E. D. Wannaz

2012-01-01

Full Text Available A pollution gradient was observed in tree foliage sampled in the vicinity of a large aluminium production facility in Patagonia (Argentina. Leaves of Eucalyptus rostrata, and Populus hybridus and different needle ages of Pinus spec. were collected and concentrations of aluminium (Al and sulphur (S as well as physiological parameters (chlorophyll and lipid oxidation products were analyzed. Al and S concentrations indicate a steep pollution gradient in the study showing a relationship with the physiological parameters in particular membrane lipid oxidation products. The present study confirms that aluminium smelting results in high Al and sulphur deposition in the study area, and therefore further studies should be carried out taking into account potentially adverse effects of these compounds on human and ecosystem health.

Aluminium/iron reinforced polyfurfuryl alcohol resin as advanced biocomposites

Directory of Open Access Journals (Sweden)

Rakesh Kumar

2016-07-01

Full Text Available Aluminium and iron are widely used in construction sectors for the preparation of advanced composites with epoxy resins as matrices. In recent times, there are several reports on the polymerization of polyfufuryl alcohol (PFA a thermoset bioresins from furfuryl alcohol (FA. FA is obtained from waste of sugarcane bagasse. In this work, first the possibility of curing PFA from FA in the presence of aluminium or iron has been explored. Absorbance results from colorimeter/spectrophotometerindicated that the curing of FA to PFA in presence of aluminium started easily while in presence of iron the curing of FA to PFA could not start. Based on the above results, aluminium wire reinforced composites were successfully prepared with three different weight fractions (0.13, 0.09 and 0.07 of aluminium wire. The mechanical properties of these composites were determined theoretically and reported.

Antiproton Accumulator (AA)

CERN Multimedia

Photographic Service

1980-01-01

The AA in its final stage of construction, before it disappeared from view under concrete shielding. Antiprotons were first injected, stochastically cooled and accumulated in July 1980. From 1981 on, the AA provided antiprotons for collisions with protons, first in the ISR, then in the SPS Collider. From 1983 on, it also sent antiprotons, via the PS, to the Low-Energy Antiproton Ring (LEAR). The AA was dismantled in 1997 and shipped to Japan.

Volatilisation and oxidation of aluminium scraps fed into incineration furnaces

Energy Technology Data Exchange (ETDEWEB)

Biganzoli, Laura, E-mail: laura.biganzoli@mail.polimi.it [Politecnico di Milano, Piazza L. Da Vinci 32, 20133 Milano (Italy); Gorla, Leopoldo; Nessi, Simone; Grosso, Mario [Politecnico di Milano, Piazza L. Da Vinci 32, 20133 Milano (Italy)

2012-12-15

Highlights: Black-Right-Pointing-Pointer Aluminium packaging partitioning in MSW incineration residues is evaluated. Black-Right-Pointing-Pointer The amount of aluminium packaging recoverable from the bottom ashes is evaluated. Black-Right-Pointing-Pointer Aluminium packaging oxidation rate in the residues of MSW incineration is evaluated. Black-Right-Pointing-Pointer 80% of aluminium cans, 51% of trays and 27% of foils can be recovered from bottom ashes. - Abstract: Ferrous and non-ferrous metal scraps are increasingly recovered from municipal solid waste incineration bottom ash and used in the production of secondary steel and aluminium. However, during the incineration process, metal scraps contained in the waste undergo volatilisation and oxidation processes, which determine a loss of their recoverable mass. The present paper evaluates the behaviour of different types of aluminium packaging materials in a full-scale waste to energy plant during standard operation. Their partitioning and oxidation level in the residues of the incineration process are evaluated, together with the amount of potentially recoverable aluminium. About 80% of post-consumer cans, 51% of trays and 27% of foils can be recovered through an advanced treatment of bottom ash combined with a melting process in the saline furnace for the production of secondary aluminium. The residual amount of aluminium concentrates in the fly ash or in the fine fraction of the bottom ash and its recovery is virtually impossible using the current eddy current separation technology. The average oxidation levels of the aluminium in the residues of the incineration process is equal to 9.2% for cans, 17.4% for trays and 58.8% for foils. The differences between the tested packaging materials are related to their thickness, mechanical strength and to the alloy.

Kinetic characterization and of recrystallization of the aluminum alloy 6063 after S work hardening treatment; Caracterizacao e cinetica de recristalizacao da liga de aluminio 6063 apos tratamentos termomecanicos

Energy Technology Data Exchange (ETDEWEB)

Esposito, Iara Maria

2006-07-01

The aluminum 6063 alloy possesses a great industrial interest, presenting characteristics that justify its frequent use, when compared to the other aluminum alloys: the precipitation hardening and high cold work capacity. These alloys present high ductility, that allows their use in operations with high deformation degrees, as the cold work. The objective of this work is to show comparative analysis of the hardness Vickers of the commercial aluminum 6063 alloy, after cold work with different area reduction degree and thermal treatment. Considering the frequent utilization aluminium 6063 alloy, this work studies the characterization and recrystallization of this alloy, after the plastic deformation in different area reduction degrees, thermal treatment and convenient treatment times - Thermo mechanic Treatments. (author)

Aluminium allergy and granulomas induced by vaccinations for children

DEFF Research Database (Denmark)

Andersen, Rosa Marie O; Zachariae, Claus; Johansen, Jeanne Duus

2014-01-01

Vaccination with aluminium-adsorbed vaccines can induce aluminium allergy with persistent itching subcutaneous nodules at the injection site - vaccination granulomas. In this article we give an overview of childhood aluminium-adsorbed vaccines available in Denmark. Through literature studies we...... examine the incidence, the symptoms and the prognosis for the vaccination granulomas and the allergy. Finally we discuss the status in Denmark....

Overload effects on a ferritic-baintic steel and a cast aluminium alloy: two very different behaviours

Energy Technology Data Exchange (ETDEWEB)

Saintier, N. [Arts et Metiers Paris Tech, I2M, UMR CNRS, Universite Bordeaux 1, Talene Cedex (France); El Dsoki, C.; Kaufmann, H.; Sonsino, C.M. [Fraunhofer-Institute for Structural Durability and System Reliability LBF, Darmstadt (Germany); Dumas, C. [RENAULT, Technocentre, Guyancourt Cedex (France); Voellmecke, F.J. [BORBET GmbH, Hallenberg-Hesborn (Germany); Palin-Luc, T.; Bidonard, H.

2011-10-15

Load controlled fatigue tests were performed up to 10{sup 7} cycles on flat notched specimens (K{sub t} = 2.5) under constant amplitude and variable amplitude loadings with and without periodical overloads. Two materials are studied: a ferritic-bainitic steel (HE400M steel) and a cast aluminium alloy (AlSi7Mg0.3). These materials have a very different cyclic behaviour: the steel exhibits cyclic strain softening whereas the Al alloy shows cyclic strain hardening. The fatigue tests show that, for the steel, periodical overload applications reduce significantly the fatigue life for fully reversed load ratio (R{sub {sigma}} = -1), while they have no influence under pulsating loading (R{sub {sigma}} = 0). For the Al alloy overloads have an effect (fatigue life decreasing) only for variable amplitude loadings. The detrimental effect of overloads on the steel is due to ratcheting at the notch root which evolution is overload's dependent. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Hot workability of aluminium alloys

International Nuclear Information System (INIS)

Yoo, Yeon Chul; Oh, Kyung Jin

1986-01-01

Hot Workability of aluminium alloys, 2024, 6061 and 7075, has been studied by hot torsion tests at temperatures from 320 to 515 deg C and at strain rates from 1.26 x 10 -3 to 5.71 x 10 -3 sec -1 . Hot working condition of these aluminium alloys was determined quantitatively from the constitutive equations obtained from flow stress curves in torsion. Experimental data of the logarith of the Zener-Hollomonn parameter showed good linear relationships to the logarith of sinh(ασ-bar)

Hardening device, by inserts, of electronic component against radiation

International Nuclear Information System (INIS)

Val, C.

1987-01-01

The hardening device includes at least two materials, one with high atomic number with respect to the other. One of these materials is set as inserts in a layer of the other material. The hardening device is then made by stacking of such layers, the insert density varying from one layer to the other, making thus vary the atomic number resulting from the hardening device along its thickness, following a predefined law [fr

Investigation of srawberry hardening in low temperatures in vitro

OpenAIRE

Lukoševičiūtė, Vanda; Rugienius, Rytis; Kavaliauskaitė, Danguolė

2007-01-01

Cold resistance of different strawberry varieties in vitro and ability to retain hardening after defrosting and repeated hardening. Phytohormons – gibberellin and abscisic acid added in the growing medium were investigated in Horticulture plant genetic and biotechnology department of LIH. We tried to model common conditions in temperate zone when freeze-thaw cycles often occur during wintertime. For investigation in vitro strawberries for the first time hardened in light at the temperature of...

Aluminium toxicity tolerance in crop plants: Present status of research

African Journals Online (AJOL)

... tolerance of which genes of the Aluminium-activated malate transporter (ALMT) and multidrug and toxic compound extrusion (MATE) families are prominent. In this review, the progress of research in identifying aluminium toxicity tolerant genes is discussed. Keywords: Aluminium toxicity, soil acidity, hydroponic screening, ...

Characterization and structure of precipitates in 6xxx Aluminium Alloys

International Nuclear Information System (INIS)

Holmestad, Randi; Bjørge, Ruben; Ehlers, Flemming J H; Torsæter, Malin; Marioara, Calin D; Andersen, Sigmund J

2012-01-01

Solute atom nanoscale precipitates are responsible for the favourable mechanical properties of heat treatable aluminium alloys such as Al-Mg-Si (6xxx). The shape, structure and strengthening properties of age-hardening precipitates depend on alloy composition and thermo-mechanical history. We seek an improved understanding of the physics related to nucleation and precipitation on the atomistic level in these alloys. Once these mechanisms are sufficiently well described and understood, the hope is that 'alloy design' simulations can assist tailoring of materials with desired properties. In pure Al-Mg-Si we have determined the structure of nearly all the known metastable precipitate phases, by combining advanced TEM techniques (such as high resolution TEM and nano-beam diffraction) with atom probe tomography and density functional theory. We are now studying effects of additions /substitutions of Cu, Ag and/or Ge that promote formation of more disordered precipitates, employing aberration corrected high angle annular dark field scanning TEM. We find that all metastable precipitates contain variations of a widely spaced 'Si/Ge network'. In spite of disorder or defects, this network is surprisingly well ordered, with hexagonal projected sub-cell dimensions a = b ≅ 0.4 nm and c (along the fully coherent precipitate main growth direction) equal to 0.405 nm or a multiple of it.

Work Hardening Behavior of 1020 Steel During Cold-Beating Simulation

Science.gov (United States)

CUI, Fengkui; LING, Yuanfei; XUE, Jinxue; LIU, Jia; LIU, Yuhui; LI, Yan

2017-03-01

The present research of cold-beating formation mainly focused on roller design and manufacture, kinematics, constitutive relation, metal flow law, thermo-mechanical coupling, surface micro-topography and microstructure evolution. However, the research on surface quality and performance of workpieces in the process of cold-beating is rare. Cold-beating simulation experiment of 1020 steel is conducted at room temperature and strain rates ranging from 2000 to 4000 s-1 base on the law of plastic forming. According to the experimental data, the model of strain hardening of 1020 steel is established, Scanning Electron Microscopy(SEM) is conducted, the mechanism of the work hardening of 1020 steel is clarified by analyzing microstructure variation of 1020 steel. It is found that the strain rate hardening effect of 1020 steel is stronger than the softening effect induced by increasing temperatures, the process of simulation cold-beating cause the grain shape of 1020 steel significant change and microstructure elongate significantly to form a fibrous tissue parallel to the direction of deformation, the higher strain rate, the more obvious grain refinement and the more hardening effect. Additionally, the change law of the work hardening rate is investigated, the relationship between dislocation density and strain, the relationship between work hardening rate and dislocation density is obtained. Results show that the change trend of the work hardening rate of 1020 steel is divided into two stages, the work hardening rate decreases dramatically in the first stage and slowly decreases in the second stage, finally tending toward zero. Dislocation density increases with increasing strain and strain rate, work hardening rate decreases with increasing dislocation density. The research results provide the basis for solving the problem of improving the surface quality and performance of workpieces under cold-beating formation of 1020 steel.

HARDENING OF CRANE RAILS BY PLASMA DISCRETE-TIME SURFACE TREATMENT

Directory of Open Access Journals (Sweden)

S. S. Samotugin

2017-01-01

Full Text Available Crane wheels and rails are subjected to intensive wear in the process of operation. Therefore, improvement of these components’ performance can be considered a task of high importance. A promising direction in this regard is surface treatment by highly concentrated energy flows such as laser beams or plasma jets. This thesis suggests that the use of gradient plasma surface treatment can improve the performance of crane rails. A research was conducted, according to which hardened zones were deposited on crane rails under different treatment modes. Microhardness was measured both at the surface and in depth using custom-made microsections. The article includes the results of study of plasma surface hardening effects on wear resistance of crane rails. Change of plasma surface treatment parameters (current, plasma torch movement speed, argon gas flow rate allows for desired steel hardness and structure, while the choice of optimal location for hardened zones makes it possible to significantly improve wear resistance and crack resistance. As a result of plasma surface hardening, the fine-grained martensite structure is obtained with mainly lamellar morphology and higher hardness rate compared toinduction hardening or overlaying. Wear test of carbon steels revealed that plasma surfacing reduces abrasive wear rate compared to the irinitial state by 2 to 3 times. Enough sharp boundary between hardened and non-hardened portions has a positive effect on the performance of parts under dynamic loads, contributing to the inhibition of cracks during the transition from solid to a soft metal. For carbon and low alloy rail steels, the properties achieved by plasma surface hardening can effectively replace induction hardening or overlaying.The mode range for plasma surface treatment that allow sobtaining a surface layer with certain operating properties has been determined.

A procedure for the hardening of materials

International Nuclear Information System (INIS)

Dearnaley, G.

1984-01-01

A method of hardening metals or ceramics which have fcc, bcc or hcp structures in which two species of differing atomic radii are introduced into the material to be hardened. One species is of a size such that it can diffuse through the lattice normally. The other is of a size such that it can diffuse readily only along dislocations. Ion bombardment is the preferred method of introducing the species with different atomic radii. The material to be hardened is subjected to heat and plastic deformation so as to cause a large number of dislocations with jogs. The species meet at the jogs where they interact and are trapped and set up strain fields which prevent further deformation of the material. (author)

An Anisotropic Hardening Model for Springback Prediction

Science.gov (United States)

Zeng, Danielle; Xia, Z. Cedric

2005-08-01

As more Advanced High-Strength Steels (AHSS) are heavily used for automotive body structures and closures panels, accurate springback prediction for these components becomes more challenging because of their rapid hardening characteristics and ability to sustain even higher stresses. In this paper, a modified Mroz hardening model is proposed to capture realistic Bauschinger effect at reverse loading, such as when material passes through die radii or drawbead during sheet metal forming process. This model accounts for material anisotropic yield surface and nonlinear isotropic/kinematic hardening behavior. Material tension/compression test data are used to accurately represent Bauschinger effect. The effectiveness of the model is demonstrated by comparison of numerical and experimental springback results for a DP600 straight U-channel test.

An Anisotropic Hardening Model for Springback Prediction

International Nuclear Information System (INIS)

Zeng, Danielle; Xia, Z. Cedric

2005-01-01

As more Advanced High-Strength Steels (AHSS) are heavily used for automotive body structures and closures panels, accurate springback prediction for these components becomes more challenging because of their rapid hardening characteristics and ability to sustain even higher stresses. In this paper, a modified Mroz hardening model is proposed to capture realistic Bauschinger effect at reverse loading, such as when material passes through die radii or drawbead during sheet metal forming process. This model accounts for material anisotropic yield surface and nonlinear isotropic/kinematic hardening behavior. Material tension/compression test data are used to accurately represent Bauschinger effect. The effectiveness of the model is demonstrated by comparison of numerical and experimental springback results for a DP600 straight U-channel test

Compressive Behaviour and Energy Absorption of Aluminium Foam Sandwich

Science.gov (United States)

Endut, N. A.; Hazza, M. H. F. Al; Sidek, A. A.; Adesta, E. T. Y.; Ibrahim, N. A.

2018-01-01

Development of materials in automotive industries plays an important role in order to retain the safety, performance and cost. Metal foams are one of the idea to evolve new material in automotive industries since it can absorb energy when it deformed and good for crash management. Recently, new technology had been introduced to replace metallic foam by using aluminium foam sandwich (AFS) due to lightweight and high energy absorption behaviour. Therefore, this paper provides reliable data that can be used to analyze the energy absorption behaviour of aluminium foam sandwich by conducting experimental work which is compression test. Six experiments of the compression test were carried out to analyze the stress-strain relationship in terms of energy absorption behavior. The effects of input variables include varying the thickness of aluminium foam core and aluminium sheets on energy absorption behavior were evaluated comprehensively. Stress-strain relationship curves was used for energy absorption of aluminium foam sandwich calculation. The result highlights that the energy absorption of aluminium foam sandwich increases from 12.74 J to 64.42 J respectively with increasing the foam and skin thickness.

Investigation of different anode materials for aluminium rechargeable batteries

Science.gov (United States)

Muñoz-Torrero, David; Leung, Puiki; García-Quismondo, Enrique; Ventosa, Edgar; Anderson, Marc; Palma, Jesús; Marcilla, Rebeca

2018-01-01

In order to shed some light into the importance of the anodic reaction in reversible aluminium batteries, we investigate here the electrodeposition of aluminium in an ionic liquid electrolyte (BMImCl-AlCl3) using different substrates. We explore the influence of the type of anodic material (aluminium, stainless steel and carbon) and its 3D geometry on the reversibility of the anodic reaction by cyclic voltammetry (CV) and galvanostatic charge-discharge. The shape of the CVs confirms that electrodeposition of aluminium was feasible in the three materials but the highest peak currents and smallest peak separation in the CV of the aluminium anode suggested that this material was the most promising. Interestingly, carbon-based substrates appeared as an interesting alternative due to the high peak currents in CV, moderate overpotentials and dual role as anode and cathode. 3D substrates such as fiber-based carbon paper and aluminium mesh showed significantly smaller overpotentials and higher efficiencies for Al reaction suggesting that the use of 3D substrates in full batteries might result in enhanced power. This is corroborated by polarization testing of full Al-batteries.

Aluminium Electroplating on Steel from a Fused Bromide Electrolyte

Energy Technology Data Exchange (ETDEWEB)

Prabhat Tripathy; Laura Wurth; Eric Dufek; Toni Y. Gutknecht; Natalie Gese; Paula Hahn; Steven Frank; Guy Fredrickson; J Stephen Herring

2014-08-01

A quaternary bromide bath (LiBr-KBr-CsBr-AlBr3) was used to electro-coat aluminium on steel substrates. The electrolyte was prepared by the addition of AlBr3 into the eutectic LiBr-KBr-CsBr melt. A smooth, thick, adherent and shiny aluminium coating could be obtained with 80 wt.% AlBr3 in the ternary melt. The SEM photographs of the coated surfaces suggest the formation of thick and dense coatings with good aluminium coverage. Both salt immersion and open circuit potential measurement suggest that the coatings did display good corrosion-resistance behavior. Annealing of the coated surfaces, prior to corrosion tests, suggested the robustness of the metallic aluminium coating in preventing the corrosion of the steel surfaces. Studies also indicated that the quaternary bromide plating bath can potentially provide a better aluminium coating on both ferrous and non-ferrous metals, including complex surfaces/geometries.

A new model for prediction of dispersoid precipitation in aluminium alloys containing zirconium and scandium

International Nuclear Information System (INIS)

Robson, J.D.

2004-01-01

A model has been developed to predict precipitation of ternary Al 3 (Sc, Zr) dispersoids in aluminium alloys containing zirconium and scandium. The model is based on the classical numerical method of Kampmann and Wagner, extended to predict precipitation of a ternary phase. The model has been applied to the precipitation of dispersoids in scandium containing AA7050. The dispersoid precipitation kinetics and number density are predicted to be sensitive to the scandium concentration, whilst the dispersoid radius is not. The dispersoids are predicted to enrich in zirconium during precipitation. Coarsening has been investigated in detail and it has been predicted that a steady-state size distribution is only reached once coarsening is well advanced. The addition of scandium is predicted to eliminate the dispersoid free zones observed in scandium free 7050, greatly increasing recrystallization resistance

Characterisation and concentration profile of aluminium during ...

African Journals Online (AJOL)

An aluminium(Al) characterisation study was conducted at a surface water treatment plant (Buffalo Pound Water Treatment Plant (BPWTP) in Moose Jaw, Saskatchewan, Canada) to understand better the effect of alum coagulant on various Al fractions. The raw water source for BPWTP is Buffalo Pound Lake water. The Al ...

Feet sunk in molten aluminium: The burn and its prevention.

Science.gov (United States)

Alonso-Peña, David; Arnáiz-García, María Elena; Valero-Gasalla, Javier Luis; Arnáiz-García, Ana María; Campillo-Campaña, Ramón; Alonso-Peña, Javier; González-Santos, Jose María; Fernández-Díaz, Alaska Leonor; Arnáiz, Javier

2015-08-01

Nowadays, despite improvements in safety rules and inspections in the metal industry, foundry workers are not free from burn accidents. Injuries caused by molten metals include burns secondary to molten iron, aluminium, zinc, copper, brass, bronze, manganese, lead and steel. Molten aluminium is one of the most common causative agents of burns (60%); however, only a few publications exist concerning injuries from molten aluminium. The main mechanisms of lesion from molten aluminium include direct contact of the molten metal with the skin or through safety apparel, or when the metal splash burns through the pants and rolls downward along the leg. Herein, we report three cases of deep dermal burns after 'soaking' the foot in liquid aluminium and its evolutive features. This paper aims to show our experience in the management of burns due to molten aluminium. We describe the current management principles and the key features of injury prevention. Copyright © 2014 Elsevier Ltd and ISBI. All rights reserved.

Surface Morphology and Hardness Analysis of TiCN Coated AA7075 Aluminium Alloy

Science.gov (United States)

Srinath, M. K.; Ganesha Prasad, M. S.

2017-12-01

Successful titanium carbonitride (TiCN) coating on AA7075 plates using the PVD technique depends upon many variables, including temperature, pressure, incident angle and energy of the reactive ions. Coated specimens have shown an increase in their surface hardness of 2.566 GPa. In this work, an attempt to further augment the surface hardness and understand its effects on the surface morphology was performed through heat treatments at 500°C for different duration of times. Specimen's heat treated at 500°C for 1 h exhibited a maximum surface hardness of 6.433 GPa, corresponding to an increase of 92.07%. The XRD results showed the presence of Al2Ti and AlTi3N and indicate the bond created between them. Unit cell lattice parameters in the XRD data are calculated using Bragg's law. The SEM images exhibit increasing crack sizes as the heat treatment time is increased. From the studies, the heat treatment duration can be optimized to 1 h, which exhibited an augmented surface hardness, as further increases in durations caused a drop in the surface hardness. The heat treatment effectively modified the surface hardness. Equations providing the relationships that temperature and time have with the reaction parameters are presented.

Corrosion of Metal-Matrix Composites with Aluminium Alloy Substrate

Directory of Open Access Journals (Sweden)

B. Bobic

2010-03-01

Full Text Available The corrosion behaviour of MMCs with aluminium alloy matrix was presented. The corrosion characteristics of boron-, graphite-, silicon carbide-, alumina- and mica- reinforced aluminium MMCs were reviewed. The reinforcing phase influence on MMCs corrosion rate as well as on various corrosion forms (galvanic, pitting, stress corrosion cracking, corrosion fatique, tribocorrosion was discussed. Some corrosion protection methods of aluminium based MMCs were described

Localised corrosion in AA 2099-T83 aluminium-lithium alloy: The role of grain orientation

International Nuclear Information System (INIS)

Ma, Y.; Zhou, X.; Liao, Y.; Yi, Y.; Wu, H.; Wang, Z.; Huang, W.

2016-01-01

Highlights: • Schmid factor of the grain/subgrain can indicate its corrosion susceptibility. • The localised corrosion prefers the grain with relatively large Schmid factor. • The localised corrosion is related to selective dissolution of T_1 phase. - Abstract: The mechanism for localised corrosion in AA 2099-T83 alloy during immersion in 3.5% NaCl solution is investigated. It is found that localised corrosion tends to occur in the grain with relatively large Schmid factor. The localised corrosion is related to selective dissolution of T_1 (Al_2CuLi) phase that preferentially precipitates at grain/subgrain boundaries and dislocations within grain interiors. A model is proposed to explain the development of the localised corrosion in the alloy by taking into account heterogeneous plastic deformation during cold working and preferential precipitation of T_1 phase at crystallographic defects within deformed grains.

Novel circuits for radiation hardened memories

International Nuclear Information System (INIS)

Haraszti, T.P.; Mento, R.P.; Moyer, N.E.; Grant, W.M.

1992-01-01

This paper reports on implementation of large storage semiconductor memories which combine radiation hardness with high packing density, operational speed, and low power dissipation and require both hardened circuit and hardened process technologies. Novel circuits, including orthogonal shuffle type of write-read arrays, error correction by weighted bidirectional codes and associative iterative repair circuits, are proposed for significant improvements of SRAMs' immunity against the effects of total dose and cosmic particle impacts. The implementation of the proposed circuit resulted in fault-tolerant 40-Mbit and 10-Mbit monolithic memories featuring a data rate of 120 MHz and power dissipation of 880 mW. These experimental serial-parallel memories were fabricated with a nonhardened standard CMOS processing technology, yet provided a total dose hardness of 1 Mrad and a projected SEU rate of 1 x 10 - 12 error/bit/day. Using radiation hardened processing improvements by factors of 10 to 100 are predicted in both total dose hardness and SEU rate

Characterization of aluminium alloys rapidly solidified

International Nuclear Information System (INIS)

Monteiro, W.A.

1988-01-01

This paper discussed the investigation of the microstructural and mechanical properties of the aluminium alloys (3003; 7050; Al-9% Mg) rapidly solidified by melt spinning process (cooling rate 10 4 - 10 6 K/s). The rapidly solidification process of the studied aluminium alloys brought a microcrystallinity, a minimum presence of coarse precipitation and, also, better mechanical properties of them comparing to the same alloys using ingot process. (author) [pt

Finite Element Simulation of Shot Peening: Prediction of Residual Stresses and Surface Roughness

Science.gov (United States)

Gariépy, Alexandre; Perron, Claude; Bocher, Philippe; Lévesque, Martin

Shot peening is a surface treatment that consists of bombarding a ductile surface with numerous small and hard particles. Each impact creates localized plastic strains that permanently stretch the surface. Since the underlying material constrains this stretching, compressive residual stresses are generated near the surface. This process is commonly used in the automotive and aerospace industries to improve fatigue life. Finite element analyses can be used to predict residual stress profiles and surface roughness created by shot peening. This study investigates further the parameters and capabilities of a random impact model by evaluating the representative volume element and the calculated stress distribution. Using an isotropic-kinematic hardening constitutive law to describe the behaviour of AA2024-T351 aluminium alloy, promising results were achieved in terms of residual stresses.

Sinter aluminium as cladding material for fuel elements; Aluminium fritte comme materiau de gainage pour les elements combustibles

Energy Technology Data Exchange (ETDEWEB)

Mann, K E; Boudouresques, M B [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires; Otto Fuchs, Meinerzhagen, Westfalen (Germany)

1961-07-01

1. Survey of the production process of sinter aluminium. 2. Description of the forming processes (extrusion, forging and rolling), whereby the production of tubing for atom piles will be explained in detail. 3. Production of ribbed tubes and tubes with close tolerances of sizes. 4. The different SAP-qualities and their properties under special consideration of the properties at elevated temperatures and the creep properties. 5. Diffusion behaviour of SAP with Be, Mg, Al, U and UO{sub 2}. 6. Corrosion behaviour in CO{sub 2} atmosphere at high temperature and in water. 7. Weldability. 8. Effect of irradiation on the mechanical properties. 9. Superiority of SAP compared with normal wrought alloys of the same composition. (author) [French] 1. Apercu des processus de production de l'aluminium fritte. 2. Expose des operations de transformation (filageries, forgeage et laminage), avec explication detaillee de la fabrication de gaine pour reacteurs. 3. Fabrication de tubes canneles et de tubes avec de faibles tolerances. 4. Diverses proprietes de l'aluminium fritte SAP, notamment proprietes aux temperatures elevees et proprietes de fluage. 5. Diffusion de l'aluminium fritte SAP en presence de Be, Mg, Al, U et UO{sub 2}. 6. Resistance a la corrosion dans une atmosphere de CO{sub 2} a temperature elevee et dans l'eau. 7. Possibilites de soudage. 8. Effet de l'irradiation sur les proprietes mecaniques. 9. Superiorite de l'aluminium fritte SAP sur les alliages forges normaux de meme composition. (auteur)

ANISOTROPIC STRAIN-HARDENING IN POLYCRYSTALLINE COPPER AND ALUMINUM

NARCIS (Netherlands)

HESS, F

1993-01-01

A new viscoplastic model for the plastic stress-strain behaviour of f.c.c. metals is presented. In this model the strain hardening results from increasing dislocation densities. The observed stagnation of strain hardening after strain reversals is explained by a lowering of the increase in

Surface hardening of titanium alloys with melting depth controlled by heat sink

Science.gov (United States)

Oden, Laurance L.; Turner, Paul C.

1995-01-01

A process for forming a hard surface coating on titanium alloys includes providing a piece of material containing titanium having at least a portion of one surface to be hardened. The piece having a portion of a surface to be hardened is contacted on the backside by a suitable heat sink such that the melting depth of said surface to be hardened may be controlled. A hardening material is then deposited as a slurry. Alternate methods of deposition include flame, arc, or plasma spraying, electrodeposition, vapor deposition, or any other deposition method known by those skilled in the art. The surface to be hardened is then selectively melted to the desired depth, dependent on the desired coating thickness, such that a molten pool is formed of the piece surface and the deposited hardening material. Upon cooling a hardened surface is formed.

Low temperature oxidation of niobium alloy with silicon-aluminium coating

International Nuclear Information System (INIS)

Lazarev, Eh.M.; Sapozhnikova, L.V.; Shabanova, M.E.; Pod'yachev, V.N.; Kornilova, Z.I.

1987-01-01

Using the gravimetry methods heat resistance of niobium-titanium-aluminium alloy in the air and at 700 deg C in the initial state and when it is protected by silicide-aluminium coatings (with variable content of aluminium) is investigated. Using X-ray diffraction and micro X-ray diffraction analyses, mechanisms of the alloy oxidation and the coating protective effect are studied. The role of aluminium in the formation of coatings is analyzed and according to bend tests the plasticity of the coatings is evaluated

Research on SEU hardening of heterogeneous Dual-Core SoC

Science.gov (United States)

Huang, Kun; Hu, Keliu; Deng, Jun; Zhang, Tao

2017-08-01

The implementation of Single-Event Upsets (SEU) hardening has various schemes. However, some of them require a lot of human, material and financial resources. This paper proposes an easy scheme on SEU hardening for Heterogeneous Dual-core SoC (HD SoC) which contains three techniques. First, the automatic Triple Modular Redundancy (TMR) technique is adopted to harden the register heaps of the processor and the instruction-fetching module. Second, Hamming codes are used to harden the random access memory (RAM). Last, a software signature technique is applied to check the programs which are running on CPU. The scheme need not to consume additional resources, and has little influence on the performance of CPU. These technologies are very mature, easy to implement and needs low cost. According to the simulation result, the scheme can satisfy the basic demand of SEU-hardening.

Oxide growth on aluminium alloys in the presence of ammonium fluoborate

Energy Technology Data Exchange (ETDEWEB)

Oliver, J; Paterson, P; Flavell, T [Royal Melbourne Inst. of Tech., VIC (Australia); Biddle, G [Alcoa Rolled Products (Australia)

1997-12-31

The aim of this study as to determine the mechanisms involved in using ammonium fluoborate as a reducing atmosphere when preheating a high magnesium content aluminium alloy. Rutherford Backscattering (RBS) has been the major technique used in the analysis of samples, it revealed significant reduction in both the diffusion of magnesium to the surface and the calculated oxide thickness in the presence of NH{sub 4}BF{sub 4}. At temperatures above 500 deg C in air, SEM images revealed depressions and voids due to incipient melting at various stages, around the grain boundaries. Grain boundaries effectively acted as pipes aiding the diffusion of magnesium to the surface. These results have been verified through compositional analysis with both RBS and auger electron spectroscopy (AES). Results from NH{sub 4}BF{sub 4} atmosphere preheat conditions showed significant improvements. It was verified experimentally that above 500 deg C , AA5182 alloys undergo incipient melting at the grain boundaries with magnesium diffusing through to the surface. 5 refs., 1 fig.

Oxide growth on aluminium alloys in the presence of ammonium fluoborate

Energy Technology Data Exchange (ETDEWEB)

Oliver, J.; Paterson, P.; Flavell, T. [Royal Melbourne Inst. of Tech., VIC (Australia); Biddle, G. [Alcoa Rolled Products (Australia)

1996-12-31

The aim of this study as to determine the mechanisms involved in using ammonium fluoborate as a reducing atmosphere when preheating a high magnesium content aluminium alloy. Rutherford Backscattering (RBS) has been the major technique used in the analysis of samples, it revealed significant reduction in both the diffusion of magnesium to the surface and the calculated oxide thickness in the presence of NH{sub 4}BF{sub 4}. At temperatures above 500 deg C in air, SEM images revealed depressions and voids due to incipient melting at various stages, around the grain boundaries. Grain boundaries effectively acted as pipes aiding the diffusion of magnesium to the surface. These results have been verified through compositional analysis with both RBS and auger electron spectroscopy (AES). Results from NH{sub 4}BF{sub 4} atmosphere preheat conditions showed significant improvements. It was verified experimentally that above 500 deg C , AA5182 alloys undergo incipient melting at the grain boundaries with magnesium diffusing through to the surface. 5 refs., 1 fig.

Hardening and softening mechanisms of pearlitic steel wire under torsion

International Nuclear Information System (INIS)

Zhao, Tian-Zhang; Zhang, Shi-Hong; Zhang, Guang-Liang; Song, Hong-Wu; Cheng, Ming

2014-01-01

Highlights: • Mechanical behavior of pearlitic steel wire is studied using torsion. • Work hardening results from refinement lamellar pearlitic structure. • Softening results from recovery, shear bands and lamellar fragmentations. • A microstructure based analytical flow stress model is established. - Abstract: The mechanical behaviors and microstructure evolution of pearlitic steel wires under monotonic shear deformation have been investigated by a torsion test and a number of electron microscopy techniques including scanning electron microscopy (SEM) and transmission electron microscopy (TEM), with an aim to reveal the softening and hardening mechanisms of a randomly oriented pearlitic structure during a monotonic stain path. Significantly different from the remarkable strain hardening in cold wire drawing, the strain hardening rate during torsion drops to zero quickly after a short hardening stage. The microstructure observations indicate that the inter-lamellar spacing (ILS) decreases and the dislocations accumulate with strain, which leads to hardening of the material. Meanwhile, when the strain is larger than 0.154, the enhancement of dynamic recovery, shear bands (SBs) and cementite fragmentations results in the softening and balances the strain hardening. A microstructure based analytical flow stress model with considering the influence of ILS on the mean free path of dislocations and the softening caused by SBs and cementite fragmentations, has been established and the predicted flow shear curve meets well with the measured curve in the torsion test

The structure of high-quality aluminium cast iron

Directory of Open Access Journals (Sweden)

D. Kopyciński

2012-01-01

Full Text Available In this study presents the analyse of aluminium iron cast structure (as-cast condition which are used in high temperature. While producing the casts of aluminium iron major influence has been preserve the structure of technological process parameters. The addition to Fe-C-Al alloy V, Ti, Cr leads to the improvement of functional and mechanical cast qualities. In this study, a method was investigated to eliminate the presence of undesirable Al4C3 phases in a aluminium cast iron structure and thus improve the production process. V and Ti additions in aluminium cast iron allows to development of FeAl - VC or TiC alloys. In particular, V or Ti contents above 5 wt.% were found to totally eliminate the presence of Al4C3. In addition, preliminary work indicates that the alloy with the FeAl - VC or TiC structure reveals high oxidation resistance. The introduction of 5 wt.% chromium to aluminium cast iron strengthened Al4C3 precipitate. Thus, the resultant alloy can be considered an intermetallic FeAl matrix strengthened by VC and TiC or modified Al4C3 reinforcements.

Developing precipitation hardenable high entropy alloys

Science.gov (United States)

Gwalani, Bharat

High entropy alloys (HEAs) is a concept wherein alloys are constructed with five or more elements mixed in equal proportions; these are also known as multi-principle elements (MPEs) or complex concentrated alloys (CCAs). This PhD thesis dissertation presents research conducted to develop precipitation-hardenable high entropy alloys using a much-studied fcc-based equi-atomic quaternary alloy (CoCrFeNi). Minor additions of aluminium make the alloy amenable for precipitating ordered intermetallic phases in an fcc matrix. Aluminum also affects grain growth kinetics and Hall-Petch hardenability. The use of a combinatorial approach for assessing composition-microstructure-property relationships in high entropy alloys, or more broadly in complex concentrated alloys; using laser deposited compositionally graded AlxCrCuFeNi 2 (0 mechanically processed via conventional techniques. The phase stability and mechanical properties of these alloys have been investigated and will be presented. Additionally, the activation energy for grain growth as a function of Al content in these complex alloys has also been investigated. Change in fcc grain growth kinetic was studied as a function of aluminum; the apparent activation energy for grain growth increases by about three times going from Al0.1CoCrFeNi (3% Al (at%)) to Al0.3CoCrFeNi. (7% Al (at%)). Furthermore, Al addition leads to the precipitation of highly refined ordered L12 (gamma') and B2 precipitates in Al0.3CoCrFeNi. A detailed investigation of precipitation of the ordered phases in Al0.3CoCrFeNi and their thermal stability is done using atom probe tomography (APT), transmission electron microscopy (TEM) and Synchrotron X-ray in situ and ex situ analyses. The alloy strengthened via grain boundary strengthening following the Hall-Petch relationship offers a large increment of strength with small variation in grain size. Tensile strength of the Al0.3CoFeNi is increased by 50% on precipitation fine-scale gamma' precipitates

Method of preparing an Al-Ti-B grain refiner for aluminium-comprising products, and a method of casting aluminium products

NARCIS (Netherlands)

Brinkman, H.J.; Duszczyk, J.; Katgerman, L.

1999-01-01

The invention relates to a method of preparing an Al-Ti-B grain refiner for cast aluminium-comprising products. According to the invention the preparation is realized by mixing powders selected from the group comprising aluminium, titanium, boron, and alloys and intermetallic compounds thereof,

The cytochrome P450 2AA gene cluster in zebrafish (Danio rerio): Expression of CYP2AA1 and CYP2AA2 and response to phenobarbital-type inducers

Energy Technology Data Exchange (ETDEWEB)

Kubota, Akira [Biology Department, Woods Hole Oceanographic Institution, Woods Hole, MA 02543 (United States); Bainy, Afonso C.D. [Biology Department, Woods Hole Oceanographic Institution, Woods Hole, MA 02543 (United States); Departamento de Bioquímica, CCB, Universidade Federal de Santa Catarina, Florianopolis, SC 88040-900 (Brazil); Woodin, Bruce R.; Goldstone, Jared V. [Biology Department, Woods Hole Oceanographic Institution, Woods Hole, MA 02543 (United States); Stegeman, John J., E-mail: jstegeman@whoi.edu [Biology Department, Woods Hole Oceanographic Institution, Woods Hole, MA 02543 (United States)

2013-10-01

The cytochrome P450 (CYP) 2 gene family is the largest and most diverse CYP gene family in vertebrates. In zebrafish, we have identified 10 genes in a new subfamily, CYP2AA, which does not show orthology to any human or other mammalian CYP genes. Here we report evolutionary and structural relationships of the 10 CYP2AA genes and expression of the first two genes, CYP2AA1 and CYP2AA2. Parsimony reconstruction of the tandem duplication pattern for the CYP2AA cluster suggests that CYP2AA1, CYP2AA2 and CYP2AA3 likely arose in the earlier duplication events and thus are most diverged in function from the other CYP2AAs. On the other hand, CYP2AA8 and CYP2AA9 are genes that arose in the latest duplication event, implying functional similarity between these two CYPs. A molecular model of CYP2AA1 showing the sequence conservation across the CYP2AA cluster reveals that the regions with the highest variability within the cluster map onto CYP2AA1 near the substrate access channels, suggesting differing substrate specificities. Zebrafish CYP2AA1 transcript was expressed predominantly in the intestine, while CYP2AA2 was most highly expressed in the kidney, suggesting differing roles in physiology. In the liver CYP2AA2 expression but not that of CYP2AA1, was increased by 1,4-bis [2-(3,5-dichloropyridyloxy)] benzene (TCPOBOP) and, to a lesser extent, by phenobarbital (PB). In contrast, pregnenolone 16α-carbonitrile (PCN) increased CYP2AA1 expression, but not CYP2AA2 in the liver. The results identify a CYP2 subfamily in zebrafish that includes genes apparently induced by PB-type chemicals and PXR agonists, the first concrete in vivo evidence for a PB-type response in fish. - Highlights: • A tandemly duplicated cluster of ten CYP2AA genes was described in zebrafish. • Parsimony and duplication analyses suggest pathways to CYP2AA diversity. • Homology models reveal amino acid positions possibly related to functional diversity. • The CYP2AA locus does not share synteny with

The cytochrome P450 2AA gene cluster in zebrafish (Danio rerio): Expression of CYP2AA1 and CYP2AA2 and response to phenobarbital-type inducers

International Nuclear Information System (INIS)

Kubota, Akira; Bainy, Afonso C.D.; Woodin, Bruce R.; Goldstone, Jared V.; Stegeman, John J.

2013-01-01

The cytochrome P450 (CYP) 2 gene family is the largest and most diverse CYP gene family in vertebrates. In zebrafish, we have identified 10 genes in a new subfamily, CYP2AA, which does not show orthology to any human or other mammalian CYP genes. Here we report evolutionary and structural relationships of the 10 CYP2AA genes and expression of the first two genes, CYP2AA1 and CYP2AA2. Parsimony reconstruction of the tandem duplication pattern for the CYP2AA cluster suggests that CYP2AA1, CYP2AA2 and CYP2AA3 likely arose in the earlier duplication events and thus are most diverged in function from the other CYP2AAs. On the other hand, CYP2AA8 and CYP2AA9 are genes that arose in the latest duplication event, implying functional similarity between these two CYPs. A molecular model of CYP2AA1 showing the sequence conservation across the CYP2AA cluster reveals that the regions with the highest variability within the cluster map onto CYP2AA1 near the substrate access channels, suggesting differing substrate specificities. Zebrafish CYP2AA1 transcript was expressed predominantly in the intestine, while CYP2AA2 was most highly expressed in the kidney, suggesting differing roles in physiology. In the liver CYP2AA2 expression but not that of CYP2AA1, was increased by 1,4-bis [2-(3,5-dichloropyridyloxy)] benzene (TCPOBOP) and, to a lesser extent, by phenobarbital (PB). In contrast, pregnenolone 16α-carbonitrile (PCN) increased CYP2AA1 expression, but not CYP2AA2 in the liver. The results identify a CYP2 subfamily in zebrafish that includes genes apparently induced by PB-type chemicals and PXR agonists, the first concrete in vivo evidence for a PB-type response in fish. - Highlights: • A tandemly duplicated cluster of ten CYP2AA genes was described in zebrafish. • Parsimony and duplication analyses suggest pathways to CYP2AA diversity. • Homology models reveal amino acid positions possibly related to functional diversity. • The CYP2AA locus does not share synteny with

FIB/SEM study of AA2024 corrosion under a seawater drop, part II

International Nuclear Information System (INIS)

King, Peter C.; Cole, Ivan S.; Corrigan, Penny A.; Hughes, Anthony E.; Muster, Tim H.; Thomas, Sebastian

2012-01-01

Highlights: ► Dealloying has a directional nature, exhibits banding. ► Oxidation state of copper in sponge remnants found to be variable. ► Dissolution and breakdown of copper sponge structure observed. ► Crystalline defects imaged in dealloyed S-phase. - Abstract: The dissolution of S-phase clusters in aluminium alloy 2024 (AA2024) exposed to a 0.5 μl seawater droplet is presented. Foils for transmission electron microscopy (TEM) were made from local attack sites using a focussed ion beam/scanning electron microscope (FIB/SEM). The sections showed that clusters of S-phase particles underwent dealloying. The resulting copper sponge morphology, banding, preferred orientation and crystal defect structure as a result of plastic deformation have been characterised. With build-up of amorphous corrosion product, physical and electrical isolation of parts of the clusters developed, with the result of copper dissolution from the S-phase remnants.

EFFECT OF HARDENING TIME ON DEFORMATION-STRENGTH INDICATORS OF CONCRETE FOR INJECTION WITH A TWO-STAGE EXPANSION DURING HARDENING IN WATER

Directory of Open Access Journals (Sweden)

Tatjana N. Zhilnikova

2017-01-01

Full Text Available Abstract. Objectives Concretes for injection with a two-stage expansion are a kind of selfstressing concrete obtained with the use of self-stressing cement.The aim of the work is to study the influence of the duration of aging on the porosity, strength and self-stress of concrete hardening in water, depending on the expansion value at the first stage. At the first stage, the compacted concrete mixture is expanded to ensure complete filling of the formwork space. At the second stage, the hardening concrete expands due to the formation of an increased amount of ettringite. This process is prolonged in time, with the amount of self-stress and strength dependant on the conditions of hardening. Methods  Experimental evaluation of self-stress, strength and porosity of concretes that are permanently hardened in water, under air-moist and air-dry conditions after different expansion at the first stage. The self-stress of cement stone is the result of superposition of two processes: the hardening of the structure due to hydration of silicates and its expansion as a result of hydration of calcium aluminates with the subsequent formation of ettringite. The magnitude of self-stress is determined by the ratio of these two processes. The self-stress of the cement stone changes in a manner similar to the change in its expansion. The stabilisation of expansion is accompanied by stabilisation of self-stress of cement stone. Results  The relationship of self-stress, strength and porosity of concrete for injection with a two-stage expansion on the duration and humidity conditions of hardening, taking into account the conditions of deformation limitation at the first stage, is revealed. Conclusion During prolonged hardening in an aqueous medium, self-stresses are reduced up to 25% with the exception of expansion at the first stage and up to 20% with an increase in volume up to 5% at the first stage. The increase in compressive strength is up to 28% relative to