Structural and superconducting properties of sputter-deposited niobium films for applications in RF accelerating cavities

CERN Document Server

Peck, M A

2000-01-01

The present work presents the results of a systematic study of superconducting and structural properties of niobium films sputter deposited onto the inner walls of radiofrequency copper resonators. The measured superconducting quantities include the surface resistance, the critical temperature, the penetration depth and the upper and lower critical fields. In addition to films grown with different discharge gases (Xe, Kr, Ar, Ne and Ar-Ne mixtures) and to films grown on substrates prepared under different conditions, the study also includes massive niobium cavities. The surface resistance is analysed in terms of its dependence on the temperature and on the rf field amplitude and, when possible, compared to theoretical predictions. In general, good agreement with BCS theory is observed. All experimental results are presented in the form of a simple, but adequate parameterisation. The residual resistance is observed to be essentially uncorrelated with the other variables, but strongly dependent on the macroscop...

Magnetization Controlled Superconductivity in a Film with Magnetic Dots

International Nuclear Information System (INIS)

Lyuksyutov, I.F.; Pokrovsky, V.; Pokrovsky, V.

1998-01-01

We consider a superconducting film with a magnetic dots array (MDA) placed upon it. Magnetic moments of the dots are normal to the film and strong enough to create vortices in the superconducting film. Magnetic interaction between dots is negligible. Zero-field cooling leads to random magnetization of the MDA well above the superconducting temperature. With this cooling, the film is in a resistive state below the (expected) superconducting transition. Paradoxically, when field cooled, the film with MDA can be superconducting. copyright 1998 The American Physical Society

Structural and superconducting characteristics of YBa2Cu3O7 films grown by fluorine-free metal-organic deposition route

DEFF Research Database (Denmark)

Zhao, Yue; Chu, Jingyuan; Qureishy, Thomas

2018-01-01

Microstructure and superconducting performance of YBa2Cu3O7 (YBCO) films deposited on LaAlO3 single crystal (LAO) substrates by a fluorine-free metal-organic deposition (FF-MOD) technique, have been studied by means of X-ray reciprocal space mapping (RSM), cross-sectional transmission electron mi...... external magnetic field at 77 K. This work offers an in-depth insight into the correlation between the microstructure and superconductivity in the MOD YBCO films.......Microstructure and superconducting performance of YBa2Cu3O7 (YBCO) films deposited on LaAlO3 single crystal (LAO) substrates by a fluorine-free metal-organic deposition (FF-MOD) technique, have been studied by means of X-ray reciprocal space mapping (RSM), cross-sectional transmission electron....... It is suggested that associated partial dislocations formed at the boundary between the stacking faults and YBCO matrix act as strong linear (or dot) pinning centers. These structural characteristics are well in line with the better superconducting performance of the low fluorine-MOD film, in particular under...

Electronic structure and superconductivity of FeSe-related superconductors.

Science.gov (United States)

Liu, Xu; Zhao, Lin; He, Shaolong; He, Junfeng; Liu, Defa; Mou, Daixiang; Shen, Bing; Hu, Yong; Huang, Jianwei; Zhou, X J

2015-05-13

FeSe superconductors and their related systems have attracted much attention in the study of iron-based superconductors owing to their simple crystal structure and peculiar electronic and physical properties. The bulk FeSe superconductor has a superconducting transition temperature (Tc) of ~8 K and it can be dramatically enhanced to 37 K at high pressure. On the other hand, its cousin system, FeTe, possesses a unique antiferromagnetic ground state but is non-superconducting. Substitution of Se with Te in the FeSe superconductor results in an enhancement of Tc up to 14.5 K and superconductivity can persist over a large composition range in the Fe(Se,Te) system. Intercalation of the FeSe superconductor leads to the discovery of the AxFe2-ySe2 (A = K, Cs and Tl) system that exhibits a Tc higher than 30 K and a unique electronic structure of the superconducting phase. A recent report of possible high temperature superconductivity in single-layer FeSe/SrTiO3 films with a Tc above 65 K has generated much excitement in the community. This pioneering work opens a door for interface superconductivity to explore for high Tc superconductors. The distinct electronic structure and superconducting gap, layer-dependent behavior and insulator-superconductor transition of the FeSe/SrTiO3 films provide critical information in understanding the superconductivity mechanism of iron-based superconductors. In this paper, we present a brief review of the investigation of the electronic structure and superconductivity of the FeSe superconductor and related systems, with a particular focus on the FeSe films.

Equilibrium vortex structures of type-II/1 superconducting films with washboard pinning landscapes

Science.gov (United States)

Wei, C. A.; Xu, X. B.; Xu, X. N.; Wang, Z. H.; Gu, M.

2018-05-01

We numerically study the equilibrium vortex structures of type-II/1 superconducting films with a periodic quasi-one-dimensional corrugated substrate. We show as a function of substrate period and pinning strength that, the vortex system displays a variety of vortex phases including arrays consisted of vortex clumps with different morphologies, ordered vortex stripes parallel and perpendicular to pinning troughs, and ordered one-dimensional vortex chains. Our simulations are helpful in understanding the structural modulations for extensive systems with both competing interactions and competing periodicities.

Thin Film Approaches to the SRF Cavity Problem Fabrication and Characterization of Superconducting Thin Films

Energy Technology Data Exchange (ETDEWEB)

Beringer, Douglas [College of William and Mary, Williamsburg, VA (United States)

2017-08-01

Superconducting Radio Frequency (SRF) cavities are responsible for the acceleration of charged particles to relativistic velocities in most modern linear accelerators, such as those employed at high-energy research facilities like Thomas Jefferson National Laboratory’s CEBAF and the LHC at CERN. Recognizing SRF as primarily a surface phenomenon enables the possibility of applying thin films to the interior surface of SRF cavities, opening a formidable tool chest of opportunities by combining and designing materials that offer greater performance benefit. Thus, while improvements in radio frequency cavity design and refinements in cavity processing techniques have improved accelerator performance and efficiency – 1.5 GHz bulk niobium SRF cavities have achieved accelerating gradients in excess of 35 MV/m – there exist fundamental material bounds in bulk superconductors limiting the maximally sustained accelerating field gradient (≈ 45 MV/m for Nb) where inevitable thermodynamic breakdown occurs. With state of the art Nb based cavity design fast approaching these theoretical limits, novel material innovations must be sought in order to realize next generation SRF cavities. One proposed method to improve SRF performance is to utilize thin film superconducting-insulating-superconducting (SIS) multilayer structures to effectively magnetically screen a bulk superconducting layer such that it can operate at higher field gradients before suffering critically detrimental SRF losses. This dissertation focuses on the production and characterization of thin film superconductors for such SIS layers for radio frequency applications. Correlated studies on structure, surface morphology and superconducting properties of epitaxial Nb and MgB2 thin films are presented.

Ultrathin NbN Films for Superconducting Single-Photon Detectors

International Nuclear Information System (INIS)

Slysz, W.; Guziewicz, M.; Borysiewicz, M.

2011-01-01

We present our research on fabrication and structural and transport characterization of ultrathin superconducting NbN layers deposited on both single-crystal Al 2 O 3 and Si wafers, and SiO 2 and Si 3 N 4 buffer layers grown directly on Si wafers. The thicknesses of our films varied from 6 nm to 50 nm and they were grown using reactive RF magnetron sputtering on substrates maintained at the temperature 850 o C. We have performed extensive morphology characterization of our films using the X-ray diffraction method and atomic force microscopy, and related the results to the type of the substrate used for the film deposition. Our transport measurements showed that even the thinnest, 6 nm thick NbN films had the superconducting critical temperature of 10-12 K, which was increased to 14 K for thicker films. (author)

Use of high-temperature superconducting films in superconducting bearings

International Nuclear Information System (INIS)

Cansiz, A.

1999-01-01

We have investigated the effect of high-temperature superconductor (HTS) films deposited on substrates that are placed above bulk HTSs in an attempt to reduce rotational drag in superconducting bearings composed of a permanent magnet levitated above the film/bulk HTS combination. According to the critical state model, hysteresis energy loss is inversely proportional to critical current density, J c , and because HTS films typically have much higher J c than that of bulk HTS, the film/bulk combination was expected to reduce rotational losses by at least one order of magnitude in the coefficient of fiction, which in turn is a measure of the hysteresis losses. We measured rotational losses of a superconducting bearing in a vacuum chamber and compared the losses with and without a film present. The experimental results showed that contrary to expectation, the rotational losses are increased by the film. These results are discussed in terms of flux drag through the film, as well as of the critical state model

Quasi-two-dimensional superconductivity in wurtzite-structured InN films

International Nuclear Information System (INIS)

Ling, D.C.; Cheng, J.H.; Lo, Y.Y.; Du, C.H.; Chiu, A.P.; Chang, P.H.; Chang, C.A.

2007-01-01

C-axis oriented InN films with wurtzite structure were grown on sapphire(0001) substrate by MOCVD method. Superconductivity with transition onset temperature T c,onset around 3.5 K has been characterized by magnetotransport measurements in fields up to 9 Tesla for films with carrier concentration in the range of 1 x 10 19 cm -3 to 7 x 10 20 cm -3 . Among them, the film with a nitridation buffer layer has the highest zero-resistance temperature T c0 of 2 K. The normal-state magnetoresistance follows Kohler's rule ΔR/R∝(H/R) 2 , indicating that there is a single species of charge carrier with single scattering time at all points on the Fermi surface. The extrapolated value of zero-temperature upper critical field H c2 ab (0) and H c2 c (0) is estimated to be 5900 G and 2800 G, respectively, giving rise to the anisotropy parameter γ about 2.1. The angular dependence of the upper critical field is in good agreement with the behavior predicted by Lawrence-Doniach model in the two-dimensional (2D) limit strongly suggesting that the InN film is a quasi-2D superconductor. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Ferromagnetic film on a superconducting substrate

International Nuclear Information System (INIS)

Bulaevskii, L. N.; Chudnovsky, E. M.

2001-01-01

We study the equilibrium domain structure and magnetic flux around a ferromagnetic film with perpendicular magnetization M 0 on a superconducting (SC) substrate. At 4πM 0 c1 the SC is in the Meissner state and the equilibrium domain width in the film, l, scales as (l/4πλ L )=(l N /4πλ L ) 2/3 with the domain width on a normal (nonsuperconducting) substrate, l N /4πλ L >>1; λ L being the London penetration length

Comment on ``Ferromagnetic film on a superconducting substrate''

Science.gov (United States)

Sonin, E. B.

2002-10-01

A superconducting substrate is not able to shrink drastically domains in a ferromagnetic film, contrary to the prediction of Bulaevskii and Chudnovsky. This is shown on the basis of the exact solution for the stripe domain structure.

Geometrical resonance effects in thin superconducting films

International Nuclear Information System (INIS)

Nedellec, P.

1977-01-01

Electron tunneling density of states measurements on thick and clear superconducting films (S 1 ) backed by films in the normal or superconducting state (S 2 ) show geometrical resonance effects associated with the spatial variation of Δ(x), the pair potential, near the interface S 1 -S 2 . The present understanding of this so-called 'Tomasch effect' is described. The dispersion relation and the nature of excitations in the superconducting state are introduced. It is shown that the introduction of Green functions give a general description of the superconducting state. The notion of Andreev scattering at the S 1 -S 2 interface is presented and connect the geometrical resonance effects to interference process between excitations. The different physical parameters involved are defined and used in the discussion of some experimental results: the variation of the period in energy with the superconducting thickness is connected to the renormalized group velocity of excitations traveling perpendicular to the film. The role of the barrier potential at the interface on the Tomasch effect is described. The main results discussed are: the decrease of the amplitude of the Tomasch structures with energy is due to the loss of the mixed electron-hole character of the superconducting excitations far away from the Fermi level; the variation of the pair potential at the interface is directly related to the amplitude of the oscillations; the tunneling selectivity is an important parameter as the amplitude as well as the phase of the oscillations are modified depending on the value of the selectivity; the phase of the Tomasch oscillations is different for an abrupt change of Δ at the interface and for a smooth variation. An ambiguity arises due to the interplay between these parameters. Finally, some experiments, which illustrate clearly the predicted effects are described [fr

High quality superconducting titanium nitride thin film growth using infrared pulsed laser deposition

Science.gov (United States)

Torgovkin, A.; Chaudhuri, S.; Ruhtinas, A.; Lahtinen, M.; Sajavaara, T.; Maasilta, I. J.

2018-05-01

Superconducting titanium nitride (TiN) thin films were deposited on magnesium oxide, sapphire and silicon nitride substrates at 700 °C, using a pulsed laser deposition (PLD) technique, where infrared (1064 nm) pulses from a solid-state laser were used for the ablation from a titanium target in a nitrogen atmosphere. Structural studies performed with x-ray diffraction showed the best epitaxial crystallinity for films deposited on MgO. In the best films, superconducting transition temperatures, T C, as high as 4.8 K were observed, higher than in most previous superconducting TiN thin films deposited with reactive sputtering. A room temperature resistivity down to ∼17 μΩ cm and residual resistivity ratio up to 3 were observed in the best films, approaching reported single crystal film values, demonstrating that PLD is a good alternative to reactive sputtering for superconducting TiN film deposition. For less than ideal samples, the suppression of the film properties were correlated mostly with the unintended incorporation of oxygen (5–10 at%) in the film, and for high oxygen content films, vacuum annealing was also shown to increase the T C. On the other hand, superconducting properties were surprisingly insensitive to the nitrogen content, with high quality films achieved even in the highly nitrogen rich, Ti:N = 40/60 limit. Measures to limit oxygen exposure during deposition must be taken to guarantee the best superconducting film properties, a fact that needs to be taken into account with other deposition methods, as well.

Characterization of the Young's modulus and residual stresses for a sputtered silicon oxynitride film using micro-structures

International Nuclear Information System (INIS)

Dong, Jian; Du, Ping; Zhang, Xin

2013-01-01

Silicon oxynitride (SiON) is an important material to fabricate micro-electro-mechanical system (MEMS) devices due to its composition-dependent tunability in electronic and mechanical properties. In this work, the SiON film with 41.45% silicon, 32.77% oxygen and 25.78% nitrogen content was deposited by RF magnetron sputtering. Two types of optimized micro-structures including micro-cantilevers and micro-rotating-fingers were designed and fabricated using MEMS surface micromachining technology. The micro-cantilever bending tests were conducted using a nanoindenter to characterize the Young's modulus of the SiON film. Owing to the elimination of the residual stress effect on the micro-cantilever structure, higher accuracy in the Young's modulus was achieved from this technique. With the information of Young's modulus of the film, the residual stresses were characterized from the deflection of the micro-rotating-fingers. This structure was able to locally measure a large range of tensile or compressive residual stresses in a thin film with sufficient sensitivities. The results showed that the Young's modulus of the SiON film was 122 GPa and the residual stresses of the SiON film were 327 MPa in the crystallographic orientation of the wafer and 334 MPa in the direction perpendicular to the crystallographic orientation, both in compression. This work presents a comprehensive methodology to measure the Young's modulus and residual stresses of a thin film with improved accuracy, which is promising for applications in mechanical characterization of MEMS devices. - Highlight: • We measured the Young's modulus and residual stress of SiON film by microstructure. • Micro cantilever structure improved the Young's modulus' measurement accuracy. • We explored the reason for the deviations of residual stress value of SiON film

Ferromagnetic film on a superconducting substrate

Energy Technology Data Exchange (ETDEWEB)

Bulaevskii, L. N.; Chudnovsky, E. M.

2001-01-01

We study the equilibrium domain structure and magnetic flux around a ferromagnetic film with perpendicular magnetization M{sub 0} on a superconducting (SC) substrate. At 4{pi}M{sub 0}film, l, scales as (l/4{pi}{lambda}{sub L})=(l{sub N}/4{pi}{lambda}{sub L}){sup 2/3} with the domain width on a normal (nonsuperconducting) substrate, l{sub N}/4{pi}{lambda}{sub L}>>1; {lambda}{sub L} being the London penetration length.

Superconducting thin films

International Nuclear Information System (INIS)

Hebard, A.F.; Vandenberg, J.M.

1982-01-01

This invention relates to granular metal and metal oxide superconducting films formed by ion beam sputter deposition. Illustratively, the films comprise irregularly shaped, randomly oriented, small lead grains interspersed in an insulating lead oxide matrix. The films are hillock-resistant when subjected to thermal cycling and exhibit unusual josephson-type switching characteristics. Depending on the oxygen content, a film may behave in a manner similar to that of a plurality of series connected josephson junctions, or the film may have a voltage difference in a direction parallel to a major surface of the film that is capable of being switched from zero voltage difference to a finite voltage difference in response to a current larger than the critical current

Pulsed laser deposition and characterisation of thin superconducting films

Energy Technology Data Exchange (ETDEWEB)

Morone, A [CNR, zona industriale di Tito Scalo, Potenza (Italy). Istituto per i Materiali Speciali

1996-09-01

Same concepts on pulsed laser deposition of thin films will be discussed and same examples of high transition temperature (HTc) BiSrCaCuO (BISCO) and low transition temperature NbN/MgO/NbN multilayers will be presented. X-ray and others characterizations of these films will be reported and discussed. Electrical properties of superconducting thin films will be realized as a function of structural and morphological aspect.

Thermal propagation and stability in superconducting films

International Nuclear Information System (INIS)

Gray, K.E.; Kampwirth, R.T.; Zasadzinski, J.F.; Ducharme, S.P.

1983-01-01

Thermal propagation and stable hot spots (normal domains) are studied in various high Tsub(c) superconducting films (Nb 3 Sn, Nb, NbN and Nb 3 Ge). A new energy balance is shown to give reasonable quantitative agreement of the dependence of the propagation velocity on the length of short normal domains. The steady state (zero velocity) measurements indicate the existence of two distinct situations for films on high thermal conductivity (sapphire) substrates. For low power per unit area the film and substrate have the same temperature, and the thermal properties of the substrate dominate. However, for higher power densities in short hot spots, the coupling is relatively weak and the thermal properties of the film alone are important. Here a connection is made between the critical current stability of superconducting films and a critical hot spot size for thermal propagation. As a result efficient heat removal is shown to dominate the stabilisation of superconducting films. The strong and weak coupling situations also lead to modifications of the models for propagation velocities on sapphire substrates. Self-healing of hot spots and other phenomena in superconducting film are explained. The potential use of the thermal propagation model in applications of superconductors, especially switches is discussed. (author)

A Method for Suppressing Superconductivity of Thin Films

Science.gov (United States)

Suppula, Tarmo; Pekola, Jukka; Kauppinen, Juha

2003-03-01

We have developed a method for suppressing superconductivity of thin films. Thin stripes of cobalt grown by e-gun evaporation and patterned by e-beam lithography were placed in the vicinity of aluminium thin film structures. The cobalt stripes were magnetized at 4.2 K with a superconducting coil and the remanence suppressed superconductivity of the Al stripe at temperatures down to 50 mK at least. The magnetization remained in thermal cycling and in a longer storage at room temperature. Motivation for this work is the Coulomb Blockade Thermometer(CBT)^1 which has to be in a normal state to operate. The CBT sensor contains aluminium which is superconducting at temperatures below 1.4 K. An external magnetic field is not always available or acceptable in cryostats. A small grain of permanent magnet mounted to the sensor is another solution, but suspicious if the sensor is put in strong magnetic fields or if "zero field" environment is required. We have shown that suitably patterned and magnetized Co stripes in the vicinity of tunnel junctions of the CBT can solve this problem. The amount of magnetic material in the sensor, as well as the stray field, is very small. This technique may be useful in other low temperature thin film devices also. 1) Product of Nanoway Ltd.

Energy gap and surface structure of superconducting diamond films probed by scanning tunneling microscopy

International Nuclear Information System (INIS)

Nishizaki, Terukazu; Takano, Yoshihiko; Nagao, Masanori; Takenouchi, Tomohiro; Kawarada, Hiroshi; Kobayashi, Norio

2007-01-01

We have performed scanning tunneling microscopy/spectroscopy (STM/STS) experiments on (1 1 1)-oriented epitaxial films of heavily boron-doped diamond at T = 0.47 K. The STM topography shows two kinds of atomic structures: a hydrogenated 1 x 1 structure, C(1 1 1)1 x 1:H, and an amorphous structure. On the C(1 1 1)1 x 1:H region, the tunneling spectra show superconducting property with the energy gap Δ = 0.83 meV. The obtained gap ratio 2Δ/k B T c = 3.57 is consistent with the weak-coupling BCS theory

Deposition of superconducting (Cu, C)-Ba-O films by pulsed laser deposition at moderate temperature

International Nuclear Information System (INIS)

Yamamoto, Tetsuro; Kikunaga, Kazuya; Obara, Kozo; Terada, Norio; Kikuchi, Naoto; Tanaka, Yasumoto; Tokiwa, Kazuyasu; Watanabe, Tsuneo; Sundaresan, Athinarayanan; Shipra

2007-01-01

Superconducting (Cu, C)-Ba-O thin films have been epitaxially grown on (100) SrTiO 3 at a low growth temperature of 500-600 deg. C by pulsed laser deposition. The dependences of their crystallinity and transport properties on preparation conditions have been investigated in order to clarify the dominant parameters for carbon incorporation and the emergence of superconductivity. It has been revealed that the CO 3 content in the films increases with increasing both the parameters of partial pressure of CO 2 during film growth and those of growth rate and enhancement of superconducting properties. The present study has also revealed that the structural and superconducting properties of the (Cu, C)-Ba-O films are seriously deteriorated by the irradiation of energetic particles during deposition. Suppression of the radiation damage is another key for a high and uniform superconducting transition. By these optimizations, a superconducting onset temperature above 50 K and a zero-resistance temperature above 40 K have been realized

THz spectroscopy on superconducting NbN thin films

Energy Technology Data Exchange (ETDEWEB)

Daschke, Lena; Pracht, Uwe S.; Dressel, Martin; Scheffler, Marc [1. Physikalisches Institut, Universitaet Stuttgart (Germany); Ilin, Konstantin S.; Siegel, Michael [Institut fuer Mikro- und Nanoelektronische Systeme, Karlsruher Institut fuer Technologie (Germany)

2015-07-01

Epitaxial thin-film niobium nitride (NbN) is a conventional BCS superconductor. In presence of strong disorder, however, electronic inhomogeneities appear, which is not fully understood yet. To obtain a better insight into the physics of such disordered materials, studies on model systems such as structurally tailored films might be useful. Furthermore, disordered NbN films are used for single-photon detection devices, whose proper performance depends on a profound understanding of the superconducting properties. The studied NbN films have a T{sub c} ranging from 10 to 15 K and the superconducting energy gap is easily accessible with THz spectroscopy (0.4 - 5.6 meV). We investigate thin films of NbN sputtered on a sapphire substrate. With a Mach-Zehnder interferometer we measure the amplitude and phase shift of radiation transmitted through the thin-film sample. From there we can determine the real and imaginary parts of the optical conductivity. These results give information about the energy gap, Cooper pair density, and quasiparticle dynamics, including the temperature evolution of these quantities. We found that a film with 10 nm thickness roughly follows the BCS behavior, as expected. We will present results of our measurements on several different NbN samples.

Nickel silicide thin films as masking and structural layers for silicon bulk micro-machining by potassium hydroxide wet etching

International Nuclear Information System (INIS)

Bhaskaran, M; Sriram, S; Sim, L W

2008-01-01

This paper studies the feasibility of using titanium and nickel silicide thin films as mask materials for silicon bulk micro-machining. Thin films of nickel silicide were found to be more resistant to wet etching in potassium hydroxide. The use of nickel silicide as a structural material, by fabricating micro-beams of varying dimensions, is demonstrated. The micro-structures were realized using these thin films with wet etching using potassium hydroxide solution on (1 0 0) and (1 1 0) silicon substrates. These results show that nickel silicide is a suitable alternative to silicon nitride for silicon bulk micro-machining

Hierarchical Micro/Nano Structures by Combined Self-Organized Dewetting and Photopatterning of Photoresist Thin Films.

Science.gov (United States)

Sachan, Priyanka; Kulkarni, Manish; Sharma, Ashutosh

2015-11-17

Photoresists are the materials of choice for micro/nanopatterning and device fabrication but are rarely used as a self-assembly material. We report for the first time a novel interplay of self-assembly and photolithography for fabrication of hierarchical and ordered micro/nano structures. We create self-organized structures by the intensified dewetting of unstable thin (∼10 nm to 1 μm) photoresist films by annealing them in an optimal solvent and nonsolvent liquid mixture that allows spontaneous dewetting to form micro/nano smooth dome-like structures. The density, size (∼100 nm to millimeters), and curvature/contact angle of the dome/droplet structures are controlled by the film thickness, composition of the dewetting liquid, and time of annealing. Ordered dewetted structures are obtained simply by creating spatial variation of viscosity by ultraviolet exposure or by photopatterning before dewetting. Further, the structures thus fabricated are readily photopatterned again on the finer length scales after dewetting. We illustrate the approach by fabricating several three-dimensional structures of varying complexity with secondary and tertiary features.

Anomalous magnetism of superconducting Mg-doped InN film

Directory of Open Access Journals (Sweden)

P. H. Chang

2016-02-01

Full Text Available We report on the Meissner effect of Mg-doped InN film with superconducting transition onset temperature Tc,onset of 5 K. Mg-doped InN is magnetically ordered and exhibits a simultaneous first-order magnetic and electric transition near 50 K. Its behavior is similar to that of iron-based superconductors. A strong correlation is proposed to exist between structural distortion and superconductivity when Mg is doped into InN. The suppression of magnetic ordering close to Tc by doping is further demonstrated by anisotropic magnetoresistance and M-H measurements. The findings suggest that the superconducting mechanism in the system may not be conventional BCS.

Imaging of current distributions in superconducting thin film structures; Abbildung von Stromverteilungen in supraleitenden Duennfilmstrukturen

Energy Technology Data Exchange (ETDEWEB)

Doenitz, D.

2006-10-31

Local analysis plays an important role in many fields of scientific research. However, imaging methods are not very common in the investigation of superconductors. For more than 20 years, Low Temperature Scanning Electron Microscopy (LTSEM) has been successfully used at the University of Tuebingen for studying of condensed matter phenomena, especially of superconductivity. In this thesis LTSEM was used for imaging current distributions in different superconducting thin film structures: - Imaging of current distributions in Josephson junctions with ferromagnetic interlayer, also known as SIFS junctions, showed inhomogeneous current transport over the junctions which directly led to an improvement in the fabrication process. An investigation of improved samples showed a very homogeneous current distribution without any trace of magnetic domains. Either such domains were not present or too small for imaging with the LTSEM. - An investigation of Nb/YBCO zigzag Josephson junctions yielded important information on signal formation in the LTSEM both for Josephson junctions in the short and in the long limit. Using a reference junction our signal formation model could be verified, thus confirming earlier results on short zigzag junctions. These results, which could be reproduced in this work, support the theory of d-wave symmetry in the superconducting order parameter of YBCO. Furthermore, investigations of the quasiparticle tunneling in the zigzag junctions showed the existence of Andreev bound states, which is another indication of the d-wave symmetry in YBCO. - The LTSEM study of Hot Electron Bolometers (HEB) allowed the first successful imaging of a stable 'Hot Spot', a self-heating region in HEB structures. Moreover, the electron beam was used to induce an - otherwise unstable - hot spot. Both investigations yielded information on the homogeneity of the samples. - An entirely new method of imaging the current distribution in superconducting interference

Superconducting oxide thin films by ion beam sputtering

International Nuclear Information System (INIS)

Kobrin, P.H.; DeNatale, J.F.; Housley, R.M.; Flintoff, J.F.; Harker, A.B.

1987-01-01

Superconducting thin films of ternary copper oxides from the Y-Ba-Cu-O and La-Sr-Cu-O systems have been deposited by ion beam sputtering of ceramic targets. Crystallographic orientation of the polycrystalline films has been shown to vary with substrate identity, deposition temperature and annealing temperature. The onset of the superconductive transition occurs near 90K in the Y-Ba-Cu-O system. Fe impurities of < 0.2% have been found to inhibit the superconducting transition, probably by migrating to the grain boundaries

Misfit dislocations and phase transformations in high-T sub c superconducting films

CERN Document Server

Gutkin, M Y

2002-01-01

A theoretical model is suggested that describes the effects of misfit stresses on defect structures, phase content and critical transition temperature T sub c in high-T sub c superconducting films. The focus is placed on the exemplary case of YBaCuO films deposited onto LaSrAlO sub 4 substrates. It is theoretically revealed here that misfit stresses are capable of inducing phase transformations controlled by the generation of misfit dislocations in growing cuprate films. These transformations, in the framework of the suggested model, account for experimental data on the influence of the film thickness on phase content and critical temperature T sub c of superconducting cuprate films, reported in the literature. The potential role of stress-assisted phase transformations in suppression of critical current density across grain boundaries in high-T sub c superconductors is briefly discussed.

Thin Film Approaches to the SRF Cavity Problem: Fabrication and Characterization of Superconducting Thin Films

Science.gov (United States)

Beringer, Douglas B.

Superconducting Radio Frequency (SRF) cavities are responsible for the acceleration of charged particles to relativistic velocities in most modern linear accelerators, such as those employed at high-energy research facilities like Thomas Jefferson National Laboratory's CEBAF and the LHC at CERN. Recognizing SRF as primarily a surface phenomenon enables the possibility of applying thin films to the interior surface of SRF cavities, opening a formidable tool chest of opportunities by combining and designing materials that offer greater benefit. Thus, while improvements in radio frequency cavity design and refinements in cavity processing techniques have improved accelerator performance and efficiency - 1.5 GHz bulk niobium SRF cavities have achieved accelerating gradients in excess of 35 MV/m - there exist fundamental material bounds in bulk superconductors limiting the maximally sustained accelerating field gradient (approximately 45 MV/m for Niobium) where inevitable thermodynamic breakdown occurs. With state of the art niobium based cavity design fast approaching these theoretical limits, novel material innovations must be sought in order to realize next generation SRF cavities. One proposed method to improve SRF performance is to utilize thin film superconducting-insulating-superconducting (SIS) multilayer structures to effectively magnetically screen a bulk superconducting layer such that it can operate at higher field gradients before suffering critically detrimental SRF losses. This dissertation focuses on the production and characterization of thin film superconductors for such SIS layers for radio-frequency applications.

Ferromagnetic Film on a Superconducting Substrate

OpenAIRE

Bulaevskii, L. N.; Chudnovsky, E. M.

2000-01-01

We study the equilibrium domain structure and magnetic flux around a ferromagnetic (FM) film with perpendicular magnetization M_0 on a superconducting (SC) substrate. At 4{\\pi}M_0> 1. Here \\lambda_L is the London penetration length. For 4{\\pi}M_0 > H_{c1} and l_{N} in excess of about 35 {\\lambda}_{L}, the domains are connected by SC vortices. We argue that pinning of vortices by magnetic domains in FM/SC multilayers can provide high critical currents.

A novel selenization technique for fabrication of superconducting FeSex thin film

International Nuclear Information System (INIS)

Chai Qinglin; Tu Hailing; Hua Zhiqiang; Wang Lei; Qu Fei

2011-01-01

A novel selenization technique was applied to prepare superconducting FeSe x films with pre-set FeS films. The combination of reactive sputtering deposition with elemental diffusion technique would extend to prepare films of other iron-based superconductors. The results of transport measurement got close or greater than that of previous reports. T c,onset and T c,0 got to 10.2 K and 4 K respectively. We believe that increase of the content of Fe 7 Se 8 could not only reduce T c but also slow down the decline of resistivity. A combinative method with reactive sputtering deposition and selenization technique was applied to prepare superconducting FeSe x films on LaAlO 3 substrates successfully. The influence of selenizing temperature on film components was studied. FeSe 0.96 and FeSe films had similar and good performances in transport measurement but little difference in magnetic property. The critical onset temperature got to 11.2 K and T c,0 got to 4 K approximately. X-ray diffraction, energy dispersive spectroscopy and scanning electron microscopy were used to analyze the ratio of constituents and morphology of several selenized films. FeSe x film had a porous structure on surface and no well preferred orientation, which were confirmed to have little influence on superconducting properties.

High-frequency properties of superconducting Y-Ba-Cu-oxide thin films

International Nuclear Information System (INIS)

Ramakrishnan, E.S.; Su, M.; Howng, W.

1992-01-01

rf and microwave properties of superconducting YBa 2 Cu 3 O 7-x thin films were measured and analyzed using a coplanar resonator structure. The films were developed by sequential electron-beam evaporation of the metals followed by postanneal processing. dc properties of the films were obtained from resistance-temperature and current-voltage measurements to evaluate the transition temperature and current densities. High-frequency properties were measured from 70 to 10 K and in the frequency range 1--3 GHz to determine the film characteristics as compared to pure copper films on the same substrates

Switching, storage, and erasure effects in a superconducting thin film

International Nuclear Information System (INIS)

Testardi, L.R.

1976-01-01

Thin niobium films can be switched from a superconducting to a resistive state permanently by application of a short electrical pulse. Application of a short pulse of opposite polarity returns the film to the superconducting state

Superconducting Properties of Lead-Bismuth Films Controlled by Ferromagnetic Nanowire Arrays

Science.gov (United States)

Ye, Zuxin; Lyuksyutov, Igor F.; Wu, Wenhao; Naugle, Donald G.

2011-03-01

Superconducting properties of lead-bismuth (82% Pb and 18% Bi) alloy films deposited on ferromagnetic nanowire arrays have been investigated. Ferromagnetic Co or Ni nanowires are first electroplated into the columnar pores of anodic aluminum oxide (AAO) membranes. Superconducting Pb 82 Bi 18 films are then quench-condensed onto the polished surface of the AAO membranes filled with magnetic nanowires. A strong dependence of the Pb 82 Bi 18 superconducting properties on the ratio of the superconducting film thickness to the magnetic nanowire diameter and the material variety was observed.

Ultrathin NbN film superconducting single-photon detector array

International Nuclear Information System (INIS)

Smirnov, K; Korneev, A; Minaeva, O; Divochiy, A; Tarkhov, M; Ryabchun, S; Seleznev, V; Kaurova, N; Voronov, B; Gol'tsman, G; Polonsky, S

2007-01-01

We report on the fabrication process of the 2 x 2 superconducting single-photon detector (SSPD) array. The SSPD array is made from ultrathin NbN film and is operated at liquid helium temperatures. Each detector is a nanowire-based structure patterned by electron beam lithography process. The advances in fabrication technology allowed us to produce highly uniform strips and preserve superconducting properties of the unpatterned film. SSPD exhibit up to 30% quantum efficiency in near infrared and up to 1% at 5-μm wavelength. Due to 120 MHz counting rate and 18 ps jitter, the time-domain multiplexing read-out is proposed for large scale SSPD arrays. Single-pixel SSPD has already found a practical application in non-invasive testing of semiconductor very-large scale integrated circuits. The SSPD significantly outperformed traditional single-photon counting avalanche diodes

Proton beam writing on PMMA and SU-8 films as a tool for development of micro-structures for organic electronics

Energy Technology Data Exchange (ETDEWEB)

Sarkar, Mihir, E-mail: mihirs@iitk.ac.in [Department of Physics, Indian Institute of Technology Kanpur, Kanpur 208016 (India); Shukla, Neeraj; Banerji, Nobin [Department of Physics, Indian Institute of Technology Kanpur, Kanpur 208016 (India); Mohapatra, Y.N. [Department of Physics, Indian Institute of Technology Kanpur, Kanpur 208016 (India); Materials Science Programme, Indian Institute of Technology Kanpur, Kanpur 208016 (India); Samtel Center for Display Technologies, Indian Institute of Technology Kanpur, Kanpur 208016 (India)

2012-02-15

Proton beam writing is a maskless lithographic technique for the fabrication of 3D micro and nano structures in polymers. The fabricated structures find application in micro fluidics, optics, biosensors, etc. We use proton beam writing for micro-patterning in polymers which will facilitate fabrication of test structures for micro-components of micro-fluidic devices, organic thin film transistors (OTFT) and organic light emitting diodes (OLED). In this paper we report fabrication of varying width micro channels in PMMA and SU-8 films used as positive and negative resists respectively. The patterns were written using 2 MeV proton beam focused down to around 1 micron. We have achieved clean periodic micro-channels of width varying from few micrometers to wider ones in both the resists. Being a mask less lithography it provides an efficient way of reducing turnaround time for test structures with several channel widths and patterns being conveniently written at the same development cycle. Possible applications of the patterned structures in OLED/TFT are discussed. Additional structures like checkered board are also fabricated. Optimized fluence for both the resist has been determined.

Morphologies and wetting properties of copper film with 3D porous micro-nano hierarchical structure prepared by electrochemical deposition

International Nuclear Information System (INIS)

Wang, Hongbin; Wang, Ning; Hang, Tao; Li, Ming

2016-01-01

Highlights: • A 3D porous micro-nano hierarchical structure Cu films were prepared. • The evolution of morphology and wettability with deposition time was reported. • The effects of EDA on the microscopic morphology were revealed. • A high contact angle of 162.1° was measured when deposition time is 5 s. • The mechanism of super-hydrophobicity was illustrated by two classical models. - Abstract: Three-dimensional porous micro-nano hierarchical structure Cu films were prepared by electrochemical deposition with the Hydrogen bubble dynamic template. The morphologies of the deposited films characterized by Scanning Electronic Microscopy (SEM) exhibit a porous micro-nano hierarchical structure, which consists of three levels in different size scales, namely the honeycomb-like microstructure, the dendritic substructure and the nano particles. Besides, the factors which influenced the microscopic morphology were studied, including the deposition time and the additive Ethylene diamine. By measuring the water contact angle, the porous copper films were found to be super-hydrophobic. The maximum of the contact angles could reach as high as 162.1°. An empirical correlation between morphologies and wetting properties was revealed for the first time. The pore diameter increased simultaneously with the deposition time while the contact angle decreased. The mechanism was illustrated by two classical models. Such super-hydrophobic three-dimensional hierarchical micro-nano structure is expected to have practical application in industry.

Spray pyrolysis process for preparing superconductive films

International Nuclear Information System (INIS)

Hsu, H.M.; Yee, I.Y.

1991-01-01

This paper describes a spray pyrolysis method for preparing thin superconductive film. It comprises: preparing a spray pyrolysis solution comprising Bi,Sr,Ca and Cu metals in a solvent; heating a substrate to a first temperature; spraying the solution onto the heated substrate to form a film thereon; heating the film and substrate to a second temperature of about 700 degrees-825 degrees C, the second temperature being higher than the first temperature; heating the film and substrate to a third temperature of about 870 degrees-890 degrees C to melt the film; once the film and substrate reach the third temperature, further heat treating the film and substrate; cooling the film and substrate to ambient temperature. This patent also describes a spray pyrolysis method for preparing thin superconductive films. It comprises: preparing a spray pyrolysis solution comprising Bi, Ca and Cu metals and fluxing agent in a solvent; heating a substrate to a first temperature; spraying the solution onto the heated substrate to form a film thereon; heating the film and substrate to a second temperature about 700 degrees-825 degrees C, the second temperature being higher than the first temperature; heating the film and substrate at a third temperature about 840 degrees-860 degrees C; and cooling the film and substrate to ambient temperature

Structure and oxygen incorporation in low pressure sputtered YBCO films

International Nuclear Information System (INIS)

Chaudhary, S.; Pandya, D. K.; Kashyap, S. C.

2002-01-01

Thin films of YBa 2 Cu 3 O 7- δ (YBCO) have been successfully grown by reactive RF-magnetron sputtering technique at low pressure. The oxygen partial pressure of 0.95 mTorr, a total pressure (argon and oxygen) of 1.9 mTorr, and a substrate temperature of 775 grad C resulted in good quality films with T C (R=0) = 85.3 K and J Cmag (4.2 K) ≅ 2x10 7 A/cm 2 . The incorporation of oxygen in the as-grown films has been controlled by using different ambient - oxygen, air or argon during in-situ cooling. The superconducting behaviour of the films was studied using resistance-temperature and low field ac-susceptibility measurements and correlated with their structure. All the films exhibited metallic conduction in the normal state. The oxygen- and air- cooled films were superconducting, possessing the usual orthorhombic structure. The argon-cooled films were non-superconducting possessing the tetragonal structure, thus implying that the structure of the film during deposition is tetragonal which transforms to either of the oxygen rich orthorhombic-I or -II phases depending upon the oxygen/air ambient. The 'δ' values of 0.14, 0.32 and 0.70 and higher 'c'-parameters of 1.1785, 1.180 and 1.183 nm have been obtained for oxygen, air and argon cooled films respectively. (Authors)

Niobium thin film deposition studies on copper surfaces for superconducting radio frequency cavity applications

Energy Technology Data Exchange (ETDEWEB)

W. M. Roach, D. B. Beringer, J. R. Skuza, W. A. Oliver, C. Clavero, C. E. Reece, R. A. Lukaszew

2012-06-01

Thin film coatings have the potential to increase both the thermal efficiency and accelerating gradient in superconducting radio frequency accelerator cavities. However, before this potential can be realized, systematic studies on structure-property correlations in these thin films need to be carried out since the reduced geometry, combined with specific growth parameters, can modify the physical properties of the materials when compared to their bulk form. Here, we present our systematic studies of Nb thin films deposited onto Cu surfaces to clarify possible reasons for the limited success that this process exhibited in previous attempts. We compare these films with Nb grown on other surfaces. In particular, we study the crystal structure and surface morphology and their effect on superconducting properties, such as critical temperature and lower critical field. We found that higher deposition temperature leads to a sharper critical temperature transition, but also to increased roughness indicating that there are competing mechanisms that must be considered for further optimization.

Niobium thin film deposition studies on copper surfaces for superconducting radio frequency cavity applications

Directory of Open Access Journals (Sweden)

W. M. Roach

2012-06-01

Full Text Available Thin film coatings have the potential to increase both the thermal efficiency and accelerating gradient in superconducting radio frequency accelerator cavities. However, before this potential can be realized, systematic studies on structure-property correlations in these thin films need to be carried out since the reduced geometry, combined with specific growth parameters, can modify the physical properties of the materials when compared to their bulk form. Here, we present our systematic studies of Nb thin films deposited onto Cu surfaces to clarify possible reasons for the limited success that this process exhibited in previous attempts. We compare these films with Nb grown on other surfaces. In particular, we study the crystal structure and surface morphology and their effect on superconducting properties, such as critical temperature and lower critical field. We found that higher deposition temperature leads to a sharper critical temperature transition, but also to increased roughness indicating that there are competing mechanisms that must be considered for further optimization.

Niobium thin film deposition studies on copper surfaces for superconducting radio frequency cavity applications

International Nuclear Information System (INIS)

Roach, W.M.; Beringer, D.B.; Skuza, J.R.; Oliver, W.A.; Clavero, C.; Reece, C.E.; Lukaszew, R.A.

2012-01-01

Thin film coatings have the potential to increase both the thermal efficiency and accelerating gradient in superconducting radio frequency accelerator cavities. However, before this potential can be realized, systematic studies on structure-property correlations in these thin films need to be carried out since the reduced geometry, combined with specific growth parameters, can modify the physical properties of the materials when compared to their bulk form. Here, we present our systematic studies of Nb thin films deposited onto Cu surfaces to clarify possible reasons for the limited success that this process exhibited in previous attempts. We compare these films with Nb grown on other surfaces. In particular, we study the crystal structure and surface morphology and their effect on superconducting properties, such as critical temperature and lower critical field. We found that higher deposition temperature leads to a sharper critical temperature transition, but also to increased roughness indicating that there are competing mechanisms that must be considered for further optimization.

Probing the superconducting state of CeCoIn{sub 5} by quantum interferometry

Energy Technology Data Exchange (ETDEWEB)

Foyevtsov, Oleksandr; Porrati, Fabrizio; Huth, Michael [Johann Wolfgang Goethe University, Frankfurt am Main (Germany)

2011-07-01

Josephson junction based structures provide a pathway to investigation of the superconducting state of unconventional superconductors. A superconducting quantum interference device (SQUID) structure was fabricated on micro-crystals of the heavy-fermion superconductor CeCoIn{sub 5}. Photo-lithography and ion beam milling/induced deposition were used to prepare the structure on a thin film of CeCoIn{sub 5} grown via molecular beam epitaxy. The interferometer was characterized with regard to the SQUID properties. The unconventional nature of superconducting state in CeCoIn{sub 5}, the implications of the normal-state electronic properties, as well as the weak-link characteristics of the SQUID structure itself lead to a wealth of different features in the I(V) and dI/dV(V) characteristics.

New Fast Response Thin Film-Based Superconducting Quench Detectors

CERN Document Server

Dudarev, A; van de Camp, W; Ravaioli, E; Teixeira, A; ten Kate, H H J

2014-01-01

Quench detection on superconducting bus bars and other devices with a low normal zone propagation velocity and low voltage build-up is quite difficult with conventional quench detection techniques. Currently, on ATLAS superconducting bus bar sections, superconducting quench detectors (SQD) are mounted to detect quench events. A first version of the SQD essentially consists of an insulated superconducting wire glued to a superconducting bus line or windings, which in the case of a quench rapidly builds up a relatively high resistance that can be easily and quietly detected. We now introduce a new generation of drastically improved SQDs. The new version makes the detection of quenches simpler, more reliable, and much faster. Instead of a superconducting wire, now a superconducting thin film is used. The layout of the sensor shows a meander like pattern that is etched out of a copper coated 25 mu m thick film of Nb-Ti glued in between layers of Kapton. Since the sensor is now much smaller and thinner, it is easi...

Disappearance of superconductivity and critical resistance in thin indium films

International Nuclear Information System (INIS)

Okuma, Satoshi; Nishida, Nobuhiko

1991-01-01

In thin granular films composed of two-dimensionally coupled indium particles, we have studied influences of average particle sizes anti d on the superconducting transition. For films with anti d=280A and 224A, superconducting transition temperature stays almost constant with increasing the sheet resistance R n in the normal state, while for a film with anti d=140A, it decreases linearly with R n . This means that the system changes to a dirty superconductor by reducing anti d. With further increasing R n , superconductivity disappears when R n exceeds the value R c of order h/4e 2 , which seems to correlate with anti d. (orig.)

NbN thin films for superconducting radio frequency cavities

Science.gov (United States)

Roach, W. M.; Skuza, J. R.; Beringer, D. B.; Li, Z.; Clavero, C.; Lukaszew, R. A.

2012-12-01

NbN thin films have the potential to be incorporated into radio frequency cavities in a multilayer coating to overcome the fundamental field gradient limit of 50 MV m-1 for the bulk niobium based technology that is currently implemented in particle accelerators. In addition to having a larger critical field value than bulk niobium, NbN films develop smoother surfaces which are optimal for cavity performance and lead to fewer losses. Here, we present a study on the correlation of film deposition parameters, surface morphology, microstructure, transport properties and superconducting properties of NbN thin films. We have achieved films with bulk-like lattice parameters and superconducting transition temperatures. These NbN films have a lower surface roughness than similarly grown niobium films of comparable thickness. The potential application of NbN thin films in accelerator cavities is discussed.

NbN thin films for superconducting radio frequency cavities

International Nuclear Information System (INIS)

Roach, W M; Clavero, C; Lukaszew, R A; Skuza, J R; Beringer, D B; Li, Z

2012-01-01

NbN thin films have the potential to be incorporated into radio frequency cavities in a multilayer coating to overcome the fundamental field gradient limit of 50 MV m −1 for the bulk niobium based technology that is currently implemented in particle accelerators. In addition to having a larger critical field value than bulk niobium, NbN films develop smoother surfaces which are optimal for cavity performance and lead to fewer losses. Here, we present a study on the correlation of film deposition parameters, surface morphology, microstructure, transport properties and superconducting properties of NbN thin films. We have achieved films with bulk-like lattice parameters and superconducting transition temperatures. These NbN films have a lower surface roughness than similarly grown niobium films of comparable thickness. The potential application of NbN thin films in accelerator cavities is discussed. (paper)

Size and dimensionality effects in superconducting Mo thin films

International Nuclear Information System (INIS)

Fabrega, L; Gil, O; Camon, A; Parra-BorderIas, M; Fernandez-MartInez, I; Costa-Kraemer, J L; Briones, F; Sese, J; Gonzalez-Arrabal, R

2011-01-01

Molybdenum is a low T c , type I superconductor whose fundamental properties are poorly known. Its importance as an essential constituent of new high performance radiation detectors, the so-called transition edge sensors (TESs) calls for better characterization of this superconductor, especially in thin film form. Here we report on a study of the basic superconducting features of Mo thin films as a function of their thickness. The resistivity is found to rise and the critical temperature decreases on decreasing film thickness, as expected. More relevant, the critical fields along and perpendicular to the film plane are markedly different, thickness dependent and much larger than the thermodynamic critical field of Mo bulk. These results are consistent with a picture of type II 2D superconducting films, and allow estimates of the fundamental superconducting lengths of Mo. The role of morphology in determining the 2D and type II character of the otherwise type I molybdenum is discussed. The possible consequences of this behaviour on the performance of radiation detectors are also addressed.

Submicron superconducting structures

International Nuclear Information System (INIS)

Golovashkin, A.I.; Lykov, A.N.

1986-01-01

An overview of works concerning superconducting structures of submicron dimensions and a system of such structures is given. It is noted that usage of the above structures in superconducting microelectronics permits, first, to increase the element packing density, to decrease the signal transmission time, capacity, power dissipated in high-frequency applications. Secondly, negligible coherence length in transition metals, their alloys and high-temperature compounds also restrict the dimensions of superconducting weak couplings when the 'classical' Josephson effect is displayed. The most effective methods for production of submicron superconducting structures are the following: lithography, double scribering. Recently the systems of superconducting submicron elements are extensively studied. It is shown that such systems can be phased by magnetic field

Fractional flux excitations and flux creep in a superconducting film

International Nuclear Information System (INIS)

Lyuksyutov, I.F.

1995-01-01

We consider the transport properties of a modulated superconducting film in a magnetic field parallel to the film. Modulation can be either intrinsic, due to the layered structure of the high-T c superconductors, or artificial, e.g. due to thickness modulation. This system has an infinite set ( >) of pinned phases. In the pinned phase the excitation of flux loops with a fractional number of flux quanta by the applied current j results in flux creep with a generated voltage V ∝ exp[-jo/j[. (orig.)

Superconducting properties of clustered PbBi films

International Nuclear Information System (INIS)

Lobb, C.J.; Tinkham, M.; Klapwijk, T.M.; Smith, A.D.; Harvard Univ., Cambridge, MA

1981-01-01

Superconducting films with high resistance/square have been widely studied as a model of the Kosterlitz-Thouless transition. We show that the behavior of high R clean films near the thickness at which electrical conduction begins is dominated by a few paths across the film and thus should not be interpreted as a Kosterlitz-Thouless transition. Instead, this behavior is consistent with a simple percolation model for the connectivity fluctuations across the film. (orig.)

Quenching of superconductivity in disordered thin films by phase fluctuations

International Nuclear Information System (INIS)

Hebard, A.F.; Palaanen, M.A.

1992-01-01

The amplitude Ψ 0 and phase Φ of the superconducting order parameter in thin-film systems are affected differently by disorder and dimensionality. With increasing disorder superconducting long range order is quenched in sufficiently thin films by physical processes driven by phase fluctuations. This occurs at both the zero-field vortex-antivortex unbinding transition and at the zero-temperature magnetic-field-tuned superconducting-insulating transition. At both of these transitions Ψ 0 is finite and constant, vanishing only when temperature, disorder, and/or magnetic field are increased further. Experimental results on amorphous-composite InO x films are presented to illustrate these points and appropriate comparisons are made to other experimental systems. (orig.)

Superconducting properties of Pb82Bi18 films controlled by ferromagnetic nanowire arrays

International Nuclear Information System (INIS)

Ye Zuxin; Lyuksyutov, Igor F; Wu Wenhao; Naugle, Donald G

2011-01-01

The superconducting properties of Pb 82 Bi 18 alloy films deposited on ferromagnetic nanowire arrays have been investigated. Ferromagnetic Co or Ni nanowires are first electroplated into the columnar pores of anodic aluminum oxide (AAO) membranes. Superconducting Pb 82 Bi 18 films are then quench condensed onto the polished surface of the AAO membranes filled with magnetic nanowires. A strong dependence of the Pb 82 Bi 18 superconducting properties on the ratio of the superconducting film thickness to the magnetic nanowire diameter and material variety was observed.

Superconducting properties of Pb82Bi18 films controlled by ferromagnetic nanowire arrays

Science.gov (United States)

Ye, Zuxin; Lyuksyutov, Igor F.; Wu, Wenhao; Naugle, Donald G.

2011-02-01

The superconducting properties of Pb82Bi18 alloy films deposited on ferromagnetic nanowire arrays have been investigated. Ferromagnetic Co or Ni nanowires are first electroplated into the columnar pores of anodic aluminum oxide (AAO) membranes. Superconducting Pb82Bi18 films are then quench condensed onto the polished surface of the AAO membranes filled with magnetic nanowires. A strong dependence of the Pb82Bi18 superconducting properties on the ratio of the superconducting film thickness to the magnetic nanowire diameter and material variety was observed.

Y-Ba-Cu-O superconducting thin films by simultaneous or sequential evaporation

International Nuclear Information System (INIS)

Mogro-Campero, A.; Hunt, B.D.; Turner, L.G.; Burrell, M.C.; Balz, W.E.

1988-01-01

Superconducting thin films of Y-Ba-Cu-O near the 1:2:3 stoichiometry were produced by simultaneous (coevaporation) and sequential (multilayer) evaporation in the same evaporator. The best film obtained on yttria-stabilized zirconia (YSZ) had a superconducting onset temperature of 104 K, a midpoint T/sub c/ of 92 K, and zero resistance at T≤74 K. Stoichiometry was deduced by inductively coupled plasma emission spectroscopy, and elemental depth profiles were obtained by x-ray photoelectron spectroscopy. Film stoichiometry changes only near the film/substrate boundary for films on YSZ. Films on Si/SiO 2 were not superconducting; depth profiling shows severe changes of film composition with depth. A major theme of this work is process reproducibility, which was found to be poor for coevaporation but improved considerably for sequential evaporation

Spatial characterization of the edge barrier in wide superconducting films

Science.gov (United States)

Sivakov, A. G.; Turutanov, O. G.; Kolinko, A. E.; Pokhila, A. S.

2018-03-01

The current-induced destruction of superconductivity is discussed in wide superconducting thin films, whose width is greater than the magnetic field penetration depth, in weak magnetic fields. Particular attention is paid to the role of the boundary potential barrier (the Bin-Livingston barrier) in critical state formation and detection of the edge responsible for this critical state with different mutual orientations of external perpendicular magnetic field and transport current. Critical and resistive states of the film were visualized using the space-resolving low-temperature laser scanning microscopy (LTLSM) method, which enables detection of critical current-determining areas on the film edges. Based on these observations, a simple technique was developed for investigation of the critical state separately at each film edge, and for the estimation of residual magnetic fields in cryostats. The proposed method only requires recording of the current-voltage characteristics of the film in a weak magnetic field, thus circumventing the need for complex LTLSM techniques. Information thus obtained is particularly important for interpretation of studies of superconducting film single-photon light emission detectors.

Josephson soliton oscillators in a superconducting thin film resonator

DEFF Research Database (Denmark)

Holm, J.; Mygind, Jesper; Pedersen, Niels Falsig

1993-01-01

Josephson soliton oscillators integrated in a resonator consisting of two closely spaced coplanar superconducting microstrips have been investigated experimentally. Pairs of long 1-D Josephson junctions with a current density of about 1000 A/cm2 were made using the Nb-AlOx-Nb trilayer technique....... Different modes of half-wave resonances in the thin-film structure impose different magnetic field configurations at the boundaries of the junctions. The DC I-V characteristic shows zero-field steps with a number of resonator-induced steps. These structures are compared to RF-induced steps generated...

Fabrication of thick superconducting films by decantation

Directory of Open Access Journals (Sweden)

Julián Betancourt M.

1991-07-01

Full Text Available We have found superconducting behavior in thick films fabricated by decantation. In this paper we present the experimental method and results obtained using commercial copper substrates.

Growth of epitaxial Ba2YCu3O(7-delta) thin films and control of their superconducting properties

International Nuclear Information System (INIS)

Siegal, M.P.; Phillips, J.M.

1992-01-01

The relationship is experimentally defined between the superconducting behavior of Ba2YCu3O(7-delta) (BYCO) films and their structural characteristics. The BYCO films are grown on LaAlO3 100-plane by coevaporating BaF2, Y, and Cu followed by ex situ annealing, and the crystalline quality is tested by Rutherford backscattering ion channeling. SEM is employed to study film morphology, and several techniques are used to measure the transition temperature (Tc), critical current density (Jc), and the penetration length. It is found that point defects and dislocations decrease as the high-temperature stage (Ta) increases; crevices, pinholes, and microcracks are also noted which are related to specific values of Tc, Ta, and penetration length. The results of the present experiments indicate that the material properties of superconducting materials should be examined closely to distinguish between pure superconducting behavior and characteristics related to material structure. 21 refs

Vortex imaging in superconducting films by scanning Hall probe microscopy

International Nuclear Information System (INIS)

Oral, A.; Bending, S.J.; Humphreys, R.G.

1996-01-01

The authors have used a low noise Scanning Hall Probe Microscope (SHPM) to study vortex structures in superconducting films. The microscope has high magnetic field (∼2.9 x 10 -8 T/√Hz at 77K) and spatial resolution, ∼0.85 μm. Magnetic field profiles of single vortices in High T c YBa 2 Cu 3 O 7-δ thin films have been successfully measured and the microscopic penetration depth of the superconductor has been extracted as a function of temperature. Flux penetration into the superconductor has been imaged in real time (∼8s/frame)

Magnetic Field Enhanced Superconductivity in Epitaxial Thin Film WTe2.

Science.gov (United States)

Asaba, Tomoya; Wang, Yongjie; Li, Gang; Xiang, Ziji; Tinsman, Colin; Chen, Lu; Zhou, Shangnan; Zhao, Songrui; Laleyan, David; Li, Yi; Mi, Zetian; Li, Lu

2018-04-25

In conventional superconductors an external magnetic field generally suppresses superconductivity. This results from a simple thermodynamic competition of the superconducting and magnetic free energies. In this study, we report the unconventional features in the superconducting epitaxial thin film tungsten telluride (WTe 2 ). Measuring the electrical transport properties of Molecular Beam Epitaxy (MBE) grown WTe 2 thin films with a high precision rotation stage, we map the upper critical field H c2 at different temperatures T. We observe the superconducting transition temperature T c is enhanced by in-plane magnetic fields. The upper critical field H c2 is observed to establish an unconventional non-monotonic dependence on temperature. We suggest that this unconventional feature is due to the lifting of inversion symmetry, which leads to the enhancement of H c2 in Ising superconductors.

Relations between structural and superconducting properties of bulk and thin film high-Tc materials

International Nuclear Information System (INIS)

Hessel Andersen, N.

1994-06-01

The structural ordering of oxygen deficient and Co-doped YBCO (YBa 2 Cu 3-y Co y O 6+x ) have been studied experimentally, and by computer simulations of the oxygen ordering in the basal plane of the structure. The calculations are based on the two-dimensional ASYNNNI model and its modifications. Good agreement is established between the ASYNNNI calculations and the experimentally observed structural properties of the double cell ortho-II structure and the oxygen disordering process from Co-doping into the basal plane. A model that relates the superconducting transition temperature T c (x) of undoped YBCO and T c (y) of Co-doped YBCO to the formation of specific domains of the two orthorhombic ordered oxygen phases, ortho-I and ortho-II, shows a close agreement with experimental T c (x) and T c (y) data of samples prepared under equilibrium conditions. The structural changes as a result of metal ion substitutions and oxidation/reduction processes have been studied by neutron powder diffraction in Pb 2 Sr 2 Ln 1-x Ca x Cu 3 O 8+y (Ln = Y and Ho), Nd 1.85 Ce 0.15 CuO 4+y , and chemically oxidized La 2-x Sr x CuO 4+y 2 Cu 3-y Al y O 6+x (y 2 Cu 3 O 6+x and Bi 2 Sr 2 CaCu 2 O 8+x thin films deposited on SrTiO 3 (001), MgO (001), LaAlO 3 (001), and NdGaO 3 (001) substrates has been studied by x-ray diffraction, TEM and RBS, and the structural ordering has been analysed in relation to their superconducting properties. (au) (30 ills., 29 refs.)

High temperature superconducting films by rf magnetron sputtering

International Nuclear Information System (INIS)

Kadin, A.M.; Ballentine, P.H.

1989-01-01

The authors have produced sputtered films of Y-Ba-Cu-O and Bi-Sr-Ca-Cu-O by rf magnetron sputtering from an oxide target consisting of loose reacted powder. The use of a large 8-inch stoichiometric target in the magnetron mode permits films located above the central region to be free of negative-ion resputtering effects, and hence yields reproducible, uniform stoichiometric compositions for a wide range of substrate temperatures. Superconducting YBCO films have been obtained either by sputtering at low temperatures followed by an 850 0 C oxygen anneal, or alternatively by depositing onto substrates heated to ∼600 - 650 0 C and cooling in oxygen. Films prepared by the former method on cubic zirconia substrate consist of randomly oriented crystallites with zero resistance above 83 K. Those deposited on zirconia at medium temperatures without the high-temperature anneal contain smooth partially oriented crystallites, with a slightly depressed T/sub c/ ∼75K. Finally, superconducting films have been deposited on MgO using a BiSrCaCu/sub 2/O/sub x/ powder target

Micro-Raman scattering in ZnTe thin films

International Nuclear Information System (INIS)

Larramendi, E. M.; Gutierrez Z-B, K.; Hernandez, E.; Melo, O. de; Berth, G.; Wiedemeier, V.; Lischka, K; Schikora, D.; Woggon, U.

2008-01-01

In this work we present micro-raman measurements on ZnTe thin films grown by isothermal closed space sublimation on GaAs(001) substrates in helium and nitrogen atmospheres. Micro-raman spectra were recorded at room temperature using the backscattering geometry (illuminated spot: 3 μm2, 0.3 cm-1 of resolution and the line 532 nm of a DPSSL as power excitation). Up to four order LO-phonon replicas and no peak from TO phonon were observed in the micro-raman spectra as evidence of the epitaxial character and good quality of the films (the TO mode is forbidden according to the selection rules for backscattering along [001] of this heterostructure). The micro-raman spectra also revealed two features at low energy, which have been assigned incorrectly in recent works. We demonstrate that these raman peaks can be associated to the presence of few monolayers of crystalline tellurium or its oxides on the surface of the films. These features were not observed in micro-raman spectra of as grown ZnTe films terminated in a Zn surface. However, they were detected after a prolonged exposure of the samples to air. In addition, it is shown that this effect is accelerated under a high power laser excitation (laser annealing) as used in conventional micro-Raman measurement setups. Preliminary results that suggest the inclusion of nitrogen in ZnTe structure are also shown. (Full text)

Microtraps for neutral atoms using superconducting structures in the critical state

International Nuclear Information System (INIS)

Emmert, A.; Brune, M.; Raimond, J.-M.; Nogues, G.; Lupascu, A.; Haroche, S.

2009-01-01

Recently demonstrated superconducting atom chips provide a platform for trapping atoms and coupling them to solid-state quantum systems. Controlling these devices requires a full understanding of the supercurrent distribution in the trapping structures. For type-II superconductors, this distribution is hysteretic in the critical state due to the partial penetration of the magnetic field in the thin superconducting film through pinned vortices. We report here an experimental observation of this memory effect. Our results are in good agreement with the predictions of the Bean model of the critical state without adjustable parameters. The memory effect allows to write and store permanent currents in micron-sized superconducting structures and paves the way toward engineered trapping potentials.

Evolution of superconducting properties with disorder in epitaxial NbN films

International Nuclear Information System (INIS)

Chockalingam, S P; Chand, Madhavi; Jesudasan, John; Raychaudhuri, Pratap; Tripathi, Vikram

2009-01-01

NbN is a conventional BCS superconductor in which disorder can be tuned from moderately clean limit to dirty limit without affecting its epitaxial nature. We studied the superconducting properties of epitaxial NbN films of different disorder characterized by k F l ranging from 8.77 to 2.56 through the transport measurements. Using reactive magnetron sputtering NbN films of different disorder are deposited by varying the sputtering power and amount of N 2 in Ar:N 2 mixture of sputtering gas. The disorder parameter k F l is obtained from the carrier density (n) and the resistivity (ρ) of the films. NbN films with higher disorder have lower transition temperature (T c ) and larger resistivity which decreases with decreasing disorder. The carrier density determined from Hall measurements show that highly disordered films have lower carrier density and vice versa. Our studies show that NbN is a good system to investigate the effects of disorder on superconductivity where the superconducting properties evolve with the disorder in thin films.

Epitaxial YBa2Cu3O7 films on rolled-textured metals for high temperature superconducting applications

International Nuclear Information System (INIS)

Norton, D.P.; Park, C.; Prouteau, C.

1998-04-01

The epitaxial growth of high temperature superconducting (HTS) films on rolled-textured metal represents a viable approach for long-length superconducting tapes. Epitaxial, 0.5 microm thick YBa 2 Cu 3 O 7 (YBCO) films with critical current densities, J c , greater than 1 MA/cm 2 have been realized on rolled-textured (001) Ni tapes with yttria-stabilized zirconia (YSZ)/CeO 2 oxide buffer layers. This paper describes the synthesis using pulsed-laser deposition (PLD) of epitaxial oxide buffer layers on biaxially-textured metal that comprise the so-called rolling-assisted biaxially-textured substrates (RABiTs trademark). The properties of the buffer and YBa 2 Cu 3 O 7 films on rolled-textured Ni are discussed, with emphasis given to the crystallographic and microstructural properties that determine the superconducting properties of these multilayer structures

Thin NbN film structures on SOI for SNSPD

Energy Technology Data Exchange (ETDEWEB)

Il' in, Konstantin; Kurz, Stephan; Henrich, Dagmar; Hofherr, Matthias; Siegel, Michael [IMS, KIT, Karlsruhe (Germany); Semenov, Alexei; Huebers, Heinz-Wilhelm [DLR, Berlin (Germany)

2012-07-01

Superconducting Nanowire Single-Photon Detectors (SNSPD) made from ultra-thin NbN films on sapphire demonstrate almost 100% intrinsic detection efficiency (DE). However the system DE values is less than 10% mostly limited by a very low absorptance of NbN films thinner than 5 nm. Integration of SNSPD in Si photonic circuit is a promising way to overcome this problem. We present results on optimization of technology of thin NbN film nanostructures on SOI (Silicon on Insulator) substrate used in Si photonics technology. Superconducting and normal state properties of these structures important for SNSPD development are presented and discussed.

Excessive current in wide superconducting films

International Nuclear Information System (INIS)

Volotskaya, V.G.; Sivakov, A.G.; Turutanov, O.G.

1986-01-01

The resistive state of a wide long film due to superconductivity destruction by current is studied. The voltage-independent excess current I 0 is observed on I-V curves at high transport currents. The two-dimensional image of the current-carrying sample obtained by laser scanning technique in this current range indicates that the whole film is in the resistive state. The current I 0 is measured as a function of magnetic field and SHF power

MgB2 thick films on three-dimensional structures fabricated by HPCVD

Science.gov (United States)

Guo, Zhengshan; Cai, Xingwei; Liao, Xuebin; Chen, Yiling; Yang, Can; Niu, Ruirui; Luo, Wenhao; Huang, Zigeng; Feng, Qingrong; Gan, Zizhao

2018-06-01

Magnetic shielding has been a key factor in the measurement of ultra-weak magnetic fields, especially for shielding from low frequency electromagnetic noise. With the recent development of superconducting quantum interference devices, superconducting magnetic shielding has become an important area of research. MgB2 has shown great potential in magnetic shielding for its remarkable superconducting properties, the feasibility of its use in this capacity having been demonstrated by MgB2 bulk samples. However, the potential for application of such bulk samples is limited. In this work, we have investigated the possibility of the fabrication of MgB2 films on three-dimensional (3D) structures using a hybrid physical‑chemical vapor deposition system. MgB2 films 10 μm thick have been fabricated on the outer surface of a polycrystalline Al2O3 cylinder. The deposited film showed a transition temperature (TC) of 39 K and J C of 5.1 × 105 A · cm‑2, which are comparable to those of planar MgB2 films. This work shows the feasibility of depositing MgB2 films onto a 3D structure, and sheds light on the potential use of MgB2 films in superconducting magnetic shielding.

Effect of point disorder on superconducting properties of ultrathin epitaxial NbN films

International Nuclear Information System (INIS)

Jesudasan, John; Bagwe, Vivas; Mondal, Mintu; Chand, Madhavi; Kamlapure, Anand; Pai, S.P.; Raychaudhuri, Pratap; Mishra, Archana

2009-01-01

We synthesized homogeneously disordered epitaxial NbN films on MgO(100) substrates using reactive dc magnetron sputtering. The disorder of the films is characterized by the Loffe-Regel parameter k F I. The superconducting properties are studied through transport, ac-susceptibility measurements and electron tunneling. The superconducting transition temperature is studied as a function of thickness for films of different disorder. In the case of the less disordered film, there is a smooth decrease in T c with decreasing thickness but for the more disordered film, the T c shows a sharp decrease to zero at a threshold thickness. The superconducting energy gap is studied via planar tunnel junctions. It is found that for the less disordered films, the temperature dependence of the gap follows the BCS variation but for the more disordered ones, there is a significant deviation from the BCS curve, and the gap remains finite at T c indicating that the superconducting transition is either governed by phase fluctuations or a first order phase transition. (author)

Tunneling probe of fluctuating superconductivity in disordered thin films

Science.gov (United States)

Dentelski, David; Frydman, Aviad; Shimshoni, Efrat; Dalla Torre, Emanuele G.

2018-03-01

Disordered thin films close to the superconductor-insulator phase transition (SIT) hold the key to understanding quantum phase transition in strongly correlated materials. The SIT is governed by superconducting quantum fluctuations, which can be revealed, for example, by tunneling measurements. These experiments detect a spectral gap, accompanied by suppressed coherence peaks, on both sides of the transition. Here we describe the insulating side in terms of a fluctuating superconducting field with finite-range correlations. We perform a controlled diagrammatic resummation and derive analytic expressions for the tunneling differential conductance. We find that short-range superconducting fluctuations suppress the coherence peaks even in the presence of long-range correlations. Our approach offers a quantitative description of existing measurements on disordered thin films and accounts for tunneling spectra with suppressed coherence peaks.

Magnetic shield effect simulation of superconducting film shield covering directly coupled HTS dc-SQUID magnetometer

International Nuclear Information System (INIS)

Terauchi, N.; Noguchi, S.; Igarashi, H.

2011-01-01

A superconducting film shield over a SQUID ring improves the robustness of the SQUID with respect to magnetic noise. Supercurrent in the SQUID magnetometer and the superconducting film shield were simulated. The superconducting film shield reduces the influence of the external magnetic field on the SQUID ring. An HTS SQUID is a high sensitive magnetic sensor. In recent years, the HTS SQUID is widely used in various applications. In some applications, high robustness with respect to magnetic noise is required to realize stable operation at outside of a magnetic shielding room. The target of this paper is a directly coupled HTS dc-SQUID magnetometer. To enhance the robustness of the SQUID magnetometer, use of a superconducting thin film shield has been proposed. The magnetic field directly penetrating the SQUID ring causes the change of the critical current of Josephson junction, and then the SQUID magnetometer transitions into inoperative state. In order to confirm the magnetic shield effect of the superconducting film shield, electromagnetic field simulation with 3D edge finite element method was performed. To simulate the high temperature superconductor, E-J characteristics and c-axis anisotropy are considered. To evaluate the effect of the superconducting film shield, an external magnetic field which is supposed to be a magnetic noise is applied. From the simulation results, the time transition of the magnetic flux penetrating the SQUID ring is investigated and the effect of the superconducting film shield is confirmed. The amplitude of the magnetic flux penetrating the SQUID ring can be reduced to about one-sixth since the superconducting film shield prevents the magnetic noise from directly penetrating the SQUID ring.

Effect of localized electron states on superconductivity of ultrathin beryllium films

International Nuclear Information System (INIS)

Tutov, V.I.; Semenenko, E.E.

1988-01-01

A wide spectrum of distortions is induced in ultrathin beryllium films of thickness less than 10 A, which are responsible for the system transition from the strong localization state completely suppressing superconductivity (in this case R □ of the layer reaches 97600 Ohm) to the weak localization stae coexisting with superconductivity at comparatively high T c (5 K). The resistance per square R □ of the films decreases more than by an order of magnitude. The superconductivity with T c =1.7 K occurs at rather strong localization, when R □ of the layer is 34000 Ohm

Niobium Nitride Thin Films and Multilayers for Superconducting Radio Frequency Cavities

Science.gov (United States)

Roach, William; Beringer, Douglas; Li, Zhaozhu; Clavero, Cesar; Lukaszew, Rosa

2013-03-01

Niobium nitride in thin film form has been considered for a number of applications including multi-layered coatings onto superconducting radio frequency cavities which have been proposed to overcome the fundamental accelerating gradient limit of ~50 MV/m in niobium based accelerators. In order to fulfill the latter application, the selected superconductor's thermodynamic critical field, HC, must be larger than that of niobium and separated from the Nb surface by an insulating layer in order to shield the Nb cavity from field penetration and thus allow higher field gradients. Thus, for the successful implementation of such multilayered stack it is important to consider not just the materials inherent properties but also how these properties may be affected in thin film geometry and also by the specific deposition techniques used. Here, we show the results of our correlated study of structure and superconducting properties in niobium nitride thin films and discuss the shielding exhibited in NbN/MgO/Nb multilayer samples beyond the lower critical field of Nb for the first time. This work was funded by the Defense Threat Reduction Agency (HDTRA-10-1-0072).

Optimization of Nd1+xBa2-xCu3O7 thin-film growth conditions using micro-Raman spectroscopy

International Nuclear Information System (INIS)

Bae, J S; Yang, In-Sang; Jo, W; Wee, S H; Yoo, S I

2006-01-01

We explore optimal growth conditions for superconducting Nd 1+x Ba 2-x Cu 3 O 7 (NdBCO) thin films deposited under various oxygen pressures in the range of 100-800 mTorr. In this study we address spatial inhomogeneity, growth orientation, impurity phases, cation disorder, and oxygen deficiency of NdBCO thin films by using micro-Raman scattering. The films grown in the low oxygen pressure range of 100-200 mTorr show predominantly a-axis orientation and degraded superconducting properties with a critical temperature (T c ) of ∼80 K. The degradation of the transition temperature of the films deposited at lower oxygen pressure is attributed to the cation disorder, on the basis of analysis of the apical oxygen Raman mode. On the other hand, the samples grown in the higher oxygen pressure range of 400-800 mTorr show strong c-axis orientation and much less cation disorder. These features correlate with their high values of T c and J c

Superconducting niobium nitride films deposited by unbalanced magnetron sputtering

Energy Technology Data Exchange (ETDEWEB)

Olaya, J.J. [Departamento de Ingenieria Mecanica y Mecatronica, Universidad Nacional de Colombia, Ciudad Universitaria, Carrera 30 Numero 45-03, Bogota (Colombia); Huerta, L. [Instituto de Investigaciones en Materiales, Universidad Nacional Autonoma de Mexico, Circuito exterior s/n, CU Coyoacan, Mexico D.F. 04510 (Mexico); Rodil, S.E. [Instituto de Investigaciones en Materiales, Universidad Nacional Autonoma de Mexico, Circuito exterior s/n, CU Coyoacan, Mexico D.F. 04510 (Mexico)], E-mail: ser42@iim.unam.mx; Escamilla, R. [Instituto de Investigaciones en Materiales, Universidad Nacional Autonoma de Mexico, Circuito exterior s/n, CU Coyoacan, Mexico D.F. 04510 (Mexico)

2008-10-01

Niobium nitride (NbN) thin films were deposited under different configurations of the magnetic field using a magnetron sputtering system. The magnetic field configuration varied from balanced to unbalanced leading to different growth conditions and film properties. The aim of the paper was to identify correlations between deposition conditions, film properties and the electrical properties, specially the superconductive critical temperature (T{sub C}). The results suggested that there is a critical deposition condition, having an optimum ion-atom arrival ratio that promotes a well ordered and textured nanocrystalline structure (cubic phase) with the minimum residual stress and only under this condition a high critical temperature (16K) was obtained. Lower T{sub C} values around 12K were obtained for the NbN samples having a lower degree of structural perfection and texture, and a larger fraction of intergranular voids. On the other hand, analysis of valence-band spectra showed that the contribution of the Nb 4d states remained essentially constant while the higher T{sub C} was correlated to a higher contribution of the N 2p states.

Superconducting niobium nitride films deposited by unbalanced magnetron sputtering

International Nuclear Information System (INIS)

Olaya, J.J.; Huerta, L.; Rodil, S.E.; Escamilla, R.

2008-01-01

Niobium nitride (NbN) thin films were deposited under different configurations of the magnetic field using a magnetron sputtering system. The magnetic field configuration varied from balanced to unbalanced leading to different growth conditions and film properties. The aim of the paper was to identify correlations between deposition conditions, film properties and the electrical properties, specially the superconductive critical temperature (T C ). The results suggested that there is a critical deposition condition, having an optimum ion-atom arrival ratio that promotes a well ordered and textured nanocrystalline structure (cubic phase) with the minimum residual stress and only under this condition a high critical temperature (16K) was obtained. Lower T C values around 12K were obtained for the NbN samples having a lower degree of structural perfection and texture, and a larger fraction of intergranular voids. On the other hand, analysis of valence-band spectra showed that the contribution of the Nb 4d states remained essentially constant while the higher T C was correlated to a higher contribution of the N 2p states

Y-Ba-Cu-O superconducting film on oxidized silicon

International Nuclear Information System (INIS)

Gupta, R.P.; Khokle, W.S.; Dubey, R.C.; Singhal, S.; Nagpal, K.C.; Rao, G.S.T.; Jain, J.D.

1988-01-01

We report thick superconducting films of Y-Ba-Cu-O on oxidized silicon substrates. The critical temperatures for onset and zero resistance are 96 and 77 K, respectively. X-ray diffraction analysis predicts 1, 2, 3 composition and orthorhombic phase of the film

Stoichiometry and superconductive properties of YBaCuO films deposited by spray pyrolysis

International Nuclear Information System (INIS)

Conde-Gallardo, A.; Falcony, C.; Ortiz, A.

1994-01-01

The dependence of the stoichiometry and the superconducting characteristics of YBaCuO films deposited by spray pyrolysis on the spraying solution composition and the deposition conditions is reported. It has been found that a proper optimization of the starting materials concentration in the spraying solution results in superconducting films with zero resistance temperature of 91 K and a transition to superconducting state within a 3 K range. X-ray diffraction and resistance vs temperature measurements have been used to monitor the crystal composition and the conductive characteristics of the films as a function of the spraying solution composition and the deposition parameters

Infrared refractive index of thin YBa2Cu3O7 superconducting films

International Nuclear Information System (INIS)

Zhang, Z.M.; Choi, B.I.; Le, T.A.; Flik, M.I.; Siegal, M.P.; Phillips, J.M.

1992-01-01

This work investigates whether thin-film optics with a constant refractive index can be applied to high-T c superconducting thin films. The reflectance and transmittance of YBa 2 Cu 3 O 7 films on LaAlO 3 substrates are measured using a Fourier-transform infrared spectrometer at wavelengths from 1 to 100 μm at room temperature. The reflectance of these superconducting films at 10K in the wavelength region from 2.5 to 25 μm is measured using a cryogenic reflectance accessory. The film thickness varies from 10 to 200 nm. By modeling the frequency-dependent complex conductivity in the normal and superconducting states and applying electromagnetic-wave theory, the complex refractive index of YBa 2 Cu 3 O 7 films is obtained with a fitting technique. It is found that a thickness-independent refractive index can be applied even to a 25nm film, and average values of the spectral refractive index for film thicknesses between 25 and 200 nm are recommended for engineering applications

Niobium thin film deposition studies on copper surfaces for superconducting radio frequency cavity applications

OpenAIRE

W. M. Roach; D. B. Beringer; J. R. Skuza; W. A. Oliver; C. Clavero; C. E. Reece; R. A. Lukaszew

2012-01-01

Thin film coatings have the potential to increase both the thermal efficiency and accelerating gradient in superconducting radio frequency accelerator cavities. However, before this potential can be realized, systematic studies on structure-property correlations in these thin films need to be carried out since the reduced geometry, combined with specific growth parameters, can modify the physical properties of the materials when compared to their bulk form. Here, we present our systematic stu...

Enhanced superconductivity and superconductor to insulator transition in nano-crystalline molybdenum thin films

Energy Technology Data Exchange (ETDEWEB)

Sharma, Shilpam; Amaladass, E.P. [Condensed Matter Physics Division, Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Sharma, Neha [Surface & Nanoscience Division, Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Harimohan, V. [Condensed Matter Physics Division, Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Amirthapandian, S. [Materials Physics Division, Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Mani, Awadhesh, E-mail: mani@igcar.gov.in [Condensed Matter Physics Division, Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India)

2017-06-01

Disorder driven superconductor to insulator transition via intermediate metallic regime is reported in nano-crystalline thin films of molybdenum. The nano-structured thin films have been deposited at room temperature using DC magnetron sputtering at different argon pressures. The grain size has been tuned using deposition pressure as the sole control parameter. A variation of particle sizes, room temperature resistivity and superconducting transition has been studied as a function of deposition pressure. The nano-crystalline molybdenum thin films are found to have large carrier concentration but very low mobility and electronic mean free path. Hall and conductivity measurements have been used to understand the effect of disorder on the carrier density and mobilities. Ioffe-Regel parameter is shown to correlate with the continuous metal-insulator transition in our samples. - Highlights: • Thin films of molybdenum using DC sputtering have been deposited on glass. • Argon background pressure during sputtering was used to tune the crystallite sizes of films. • Correlation in deposition pressure, disorder and particle sizes has been observed. • Disorder tuned superconductor to insulator transition along with an intermediate metallic phase has been observed. • Enhancement of superconducting transition temperature and a dome shaped T{sub C} vs. deposition pressure phase diagram has been observed.

Magnetofingerprints of superconducting films: Vortex dynamics and mesoscopic-scale disorder

International Nuclear Information System (INIS)

Nowak, E.R.; Israeloff, N.E.; Goldman, A.M.

1994-01-01

The variations of voltage and voltage noise with magnetic field in c-axis-oriented DyBa 2 Cu 3 O 7-δ thin films exhibit reproducible, microstructure-dependent ''magnetofingerprints'' (MF's). The MF's can be scrambled with the reversal of the direction of the Lorentz force on field-induced vortices. Analysis of the noise suggests a strong dependence of the local free-energy landscape on vortex density similar to global frustration effects found in periodic superconducting networks. Above fields which roughly match vortex separation with mesoscopic-scale disorder in the films the noise and the fine structure of the MF's are suppressed, suggesting a crossover to a more weakly pinned vortex-liquid regime

Cost-Effective Fabrication of Inner-Porous Micro/Nano Carbon Structures.

Science.gov (United States)

Jiang, Shulan; Shi, Tielin; Tang, Zirong; Xi, Shuang

2018-03-01

This paper reports the fabrication of a new micro/nano carbon architecture array which owns the characteristics of inner-porous, desired conductivity and large effective surface area. The micro/nano inner-porous carbon structures were fabricated for the first time, with ordinary and cost-effective processes, including photolithography, oxygen plasma etching and pyrolysis. Firstly, micro/nano hierarchical photoresist structures array was generated through photolithography and oxygen plasma etching processes. By introducing a critical thin-film spin-coating step, and followed with carefully pyrolyzing process, the micro/nano photoresist structures were converted into innerporous carbon architectures with good electric connection which connected the carbon structures array together. Probably the inner-porous property can be attributed to the shrinkage difference between positive thin film and negative photoresist structures during pyrolyzing process. It is demonstrated that the simple method is effective to fabricate inner-porous carbon structures with good electric connection and the carbon structures can be used as electrochemical electrodes directly and without the addition of other pyrolysis or film coating processes. The electrochemical property of the carbon structures has been explored by cyclic voltammetric measurement. Compared with solid carbon microstructures array, the cyclic voltammetry curve of inner-porous carbon structures shows greatly enhanced current and improved charge-storage capability, indicating great potential in micro energy storage devices and bio-devices.

Pulsed laser deposition of high Tc superconducting thin films

International Nuclear Information System (INIS)

Singh, R.K.; Narayan, J.

1990-01-01

This paper reports on the pulsed laser evaporation (PLE) technique for deposition of thin films characterized by a number of unique properties. Based on the experimental characteristics, a theoretical model is developed which considers the formation and anisotropic three dimensional expansion of the laser generated plasma. This model explains most of the experimental features observed in PLE. We have also employed the PLE technique for in-situ fabrication of YBa 2 Cu 3 O 7 superconducting thin films on different substrates in the temperature range of 500--650 degrees C. At temperatures below 600 degrees C, a biased interposing ring between the substrate and the target was found to significantly improve the superconducting properties. The minimum ion channeling yields were between 3--3.5% for films deposited on (100) SrTiO 3 and (100) LaAlO 3 substrates

Review of thin film superconductivity

International Nuclear Information System (INIS)

Kihlstrom, K.E.

1989-01-01

Advances in thin film superconductivity are critical to the success of many proposed applications. The authors review several of the prominent techniques currently used to produce thin films of the high temperature superconductors including electron beam co-deposition, sputtering (both multiple and composite source configurations) and laser ablation. The authors look at the relevant parameters for each and evaluate the advantages and disadvantages of each technique. In addition, promising work on in situ oxidation is discussed. Also addressed are efforts to find optimum substrate materials and substrate buffer layers for various applications. The current state of the art for T c , J c and H c2 is presented for the yttrium, bismuth, and thallium compounds

Nano-fabricated superconducting radio-frequency composites, method for producing nano-fabricated superconducting rf composites

Science.gov (United States)

Norem, James H.; Pellin, Michael J.

2013-06-11

Superconducting rf is limited by a wide range of failure mechanisms inherent in the typical manufacture methods. This invention provides a method for fabricating superconducting rf structures comprising coating the structures with single atomic-layer thick films of alternating chemical composition. Also provided is a cavity defining the invented laminate structure.

Superconducting films of YBaCuO

International Nuclear Information System (INIS)

Coelho, A.L.

1991-01-01

Thick films of YBa 2 Cu 3 O 7 - x have been prepared on alumina and YSZ (Yttria-stabilized zirconia) substrates by the screen printing technique. Several experimental conditions have been studied, for instance: sintering time, temperature, thickness and atmosphere annealed. The resulting films have been characterized by X-ray diffraction, AC electrical resistance, AC susceptibility and scanning electron microscopy. The surface and cross-section have been observed with an optical microscope. The X-ray diffraction patterns have been compared with a typical pattern and that has indicated the good quality of the samples. AC resistance and its temperature dependence have been measured in the standard four-probe configuration. Films thickness has been estimated in the scanning electron microscope. This technique has been suitable for production of high T c superconducting films being a simple and inexpensive method. (author)

Generation of coherent electromagnetic radiation by superconducting films at nitrogen temperatures

CERN Document Server

Lykov, A N

2001-01-01

One detected generation of coherent electromagnetic radiation by GdBa sub 2 Cu sub 3 O sub 7 sub - sub x superconducting films within 1-10 MHz range at temperature of liquid nitrogen boiling. This type generation is caused by synchronization realized due to the feedback of abrupt changes of the Abrikosov's vortices produced by the external low-frequency magnetic field. Possibility to reach more intensive radiation due to increase of the area of superconducting film, as well as, via increase of amplitude and of frequency of electromagnetic field exciting a vortex system in films is the most important advantage of the given technique of generation

The influence of Ac parameters in the process of micro-arc oxidation film electric breakdown

Directory of Open Access Journals (Sweden)

Ma Jin

2016-01-01

Full Text Available This paper studies the electric breakdown discharge process of micro-arc oxidation film on the surface of aluminum alloy. Based on the analysis of the AC parameters variation in the micro-arc oxidation process, the following conclusions can be drawn: The growth of oxide film can be divided into three stages, and Oxide film breakdown discharge occurs twice in the micro-arc oxidation process. The first stage is the formation and disruptive discharge of amorphous oxide film, producing the ceramic oxide granules, which belong to solid dielectric breakdown. In this stage the membrane voltage of the oxide film plays a key role; the second stage is the formation of ceramic oxide film, the ceramic oxide granules turns into porous structure oxide film in this stage; the third stage is the growth of ceramic oxide film, the gas film that forms in the oxide film’s porous structure is electric broken-down, which is the second breakdown discharge process, the current density on the oxide film surface could affect the breakdown process significantly.

Preparation of YBCO superconducting films by spray pyrolysis method

International Nuclear Information System (INIS)

Mora Alonso, M.; Leyva Fabelo, A.; Rubio Frias, E.; Pupo Gonzalez, I.; Lopez Sanchez, D.

1994-01-01

The methodology for the preparation of YBCO superconducting films on Zr 2O (Y) substrates by spray pyrolysis method is reported. The transition temperature of these films is superior than the boiling temperature of liquid 2N . Other critical parameters are similar to those reported by other authors using the same technique

Forming method of a functional layer-built film by micro-wave plasma CVD

Energy Technology Data Exchange (ETDEWEB)

Saito, Keishi

1988-11-18

In forming an amorphous semi-conductor material film, the micro-wave plasma CVD cannot be generally used because of such demerits as film-separation, low yield, columnar structure in the film, and problems in the optical and electrical properties. In this invention, a specific substrate is placed in a layer-built film forming unit which is capable of maintaining vacuum; raw material gas for the film formation is introduced; plasma is generated by a micro-wave energy to decompose the raw material gas, thus forming the layer-built film on the substarte. Then a film is made by adding a specific amount of calcoganide-containing gas to the raw material gas. By this, the utilization efficiency of the raw material gas gets roughly 100% and both the adhesion to the substrate and the structural flexibility of the layer-built film increase, enhancing the yield of forming various functional elements (sensor, solar cell, thin transistor film, etc.), and thus greatly reducing the production cost. 6 figs., 7 tabs.

Microwave Josephson generation in thin film superconducting bridges

International Nuclear Information System (INIS)

Gubankov, V.N.; Koshelets, V.P.; Ovsyannikov, G.A.

1975-01-01

Thin-film bridges have some advantage over other types of superconducting weak links: good definition of electromagnetic parameters and of weak region geometry. Up to now Josephson properties of bridges have been investigated by using indirect methods (the effect of magnetic field on the critical current I 0 , the bridge behavior in a microwave field, etc.). Direct experimental observation of Josephson radiation from autonomous thin film bridges is reported. Microwave radiation in tin bridges of 'variable' thickness has been investigated where the thickness of the film forming the bridge is far less than the thickness of the bank films. (Auth.)

YBa2Cu3O(7-x) based superconducting thin films by multitarget sputtering

International Nuclear Information System (INIS)

Bouteloup, E.; Mercey, B.; Poullain, G.; Brousse, T.; Murray, H.; Raveau, B.

1990-01-01

This paper reports a new technique to prepare superconducting YBa 2 Cu 3 O (7-x) thin films. The multitarget sputtering apparatus described below allows the simultaneous and reproducible production of numerous films with a metallic composition close to Y 17% Ba 33% Cu 50% . Superconducting films (R = 0) at 80 K have been produced on polycrystalline zirconia substrates after a high temperature annealing [fr

Novel development of the micro-tensile test at elevated temperature using a test structure with integrated micro-heater

Science.gov (United States)

Ang, W. C.; Kropelnicki, P.; Soe, Oak; Ling, J. H. L.; Randles, A. B.; Hum, A. J. W.; Tsai, J. M. L.; Tay, A. A. O.; Leong, K. C.; Tan, C. S.

2012-08-01

This paper describes the novel development of a micro-tensile testing method that allows testing at elevated temperatures. Instead of using a furnace, a titanium/platinum thin film micro-heater was fabricated on a conventional dog-bone-shaped test structure to heat up its gauge section locally. An infrared (IR) camera with 5 µm resolution was employed to verify the temperature uniformity across the gauge section of the test structure. With this micro-heater-integrated test structure, micro-tensile tests can be performed at elevated temperatures using any conventional tensile testing system without any major modification to the system. In this study, the tensile test of the single crystal silicon (SCS) thin film with (1 0 0) surface orientation and tensile direction was performed at room temperature and elevated temperatures, up to 300 °C. Experimental results for Young's modulus as a function of temperature are presented. A micro-sized SCS film showed a low dependence of mechanical properties on temperature up to 300 °C.

Preparation and characterization of micro-grid modified In_2O_3:W films

International Nuclear Information System (INIS)

Dong, Dongmei; Wang, Wenwen; Zhang, Fan; Fu, Qiang; Pan, Jiaojiao

2016-01-01

Tungsten doped indium oxide (In_2O_3:W, IWO) thin films with IWO micro-grid covered surface were prepared at room temperature using techniques of radio frequency (RF) magnetron sputtering and polystyrene (PS) microsphere template. The composition, crystallization structures, surface morphologies, and optical and electrical properties of the films were characterized by X-ray photoelectron spectroscopy, X-ray diffraction, scanning electron microscopy, spectrophotometer from visible to near infrared (NIR) range and Hall effect measurement, respectively. Periodic micro-grid modified surface was obtained to improve light trapping properties. The effects of the PS micro-spheres diameters and the sputtering time on the surface morphology, transmittance in NIR range, diffuse reflection and conductive properties of the IWO films are investigated. Experiments show that surface modification of the IWO film with micro-grid under the optimized condition can improve the conductivity of the films by 15%, and the diffuse reflectance by 150%, with less than 8% decrease of the transmittance in the visible region. The study would be beneficial to the light trapping effect of solar cells using IWO films as transparent electrodes. - Highlights: • In_2O_3:W (IWO) films were obtained by reactive frequency magnetron sputtering. • IWO micro-grids were prepared on the surface of IWO films. • Influences of micro-grid size and sputtering time on IWO films were analyzed. • Both high conductivity and transparency are acquired in near-infrared region.

Intrinsic and experimental quasiparticle recombination times in superconducting films

International Nuclear Information System (INIS)

Eisenmenger, W.; Lassmann, K.; Trumpp, H.J.; Krauss, R.

1977-01-01

Experimental quasiparticle recombination lifetime data for superconducting Al, Sn, and Pb films are compared with calculations based on a ray acoustic model taking account of the film thickness dependence of the reabsorption of recombination phonons. Information on the true or intrinsic quasiparticle recombination lifetime obtained from these and other data is discussed. (orig.) [de

Interface-Induced Zeeman-Protected Superconductivity in Ultrathin Crystalline Lead Films

Science.gov (United States)

Liu, Yi; Wang, Ziqiao; Zhang, Xuefeng; Liu, Chaofei; Liu, Yongjie; Zhou, Zhimou; Wang, Junfeng; Wang, Qingyan; Liu, Yanzhao; Xi, Chuanying; Tian, Mingliang; Liu, Haiwen; Feng, Ji; Xie, X. C.; Wang, Jian

2018-04-01

Two-dimensional (2D) superconducting systems are of great importance for exploring exotic quantum physics. The recent development of fabrication techniques has stimulated studies of high-quality single-crystalline 2D superconductors, where intrinsic properties give rise to unprecedented physical phenomena. Here, we report the observation of Zeeman-type spin-orbit interaction protected superconductivity (Zeeman-protected superconductivity) in 4-monolayer (ML) to 6-ML crystalline Pb films grown on striped incommensurate Pb layers on Si(111) substrates by molecular beam epitaxy. An anomalously large in-plane critical field far beyond the Pauli limit is detected, which can be attributed to the Zeeman-protected superconductivity due to the in-plane inversion symmetry breaking at the interface. Our work demonstrates that, in superconducting heterostructures, the interface can induce Zeeman-type spin-orbit interactions and modulate the superconductivity.

Hall effect of K-doped superconducting thin films

Energy Technology Data Exchange (ETDEWEB)

Son, Eunseon; Lee, Nam Hoon; Kang, Won Nam [Dept. of physics, Sungkyunkwan University, Suwon (Korea, Republic of); Hwang, Tae Jong; Kim, Dong Ho [Dept. of physics, Yeungnam University, Gyeongsan(Korea, Republic of)

2013-09-15

We have studied Hall effect for potassium (K)-doped BaFe{sub 2}As{sub 2}superconducting thin films by analyzing the relation between the longitudinal resistivity (ρ{sub xy}) and the Hall resistivity (ρ{sub xy}). The thin films used in this study were fabricated on Al{sub O3} (000l) substrates by using an ex-situ pulsed laser deposition (PLD) technique under a high-vacuum condition of ∼10{sup -6} Torr. The samples showed the high superconducting transition temperatures (T{sub C}) of ∼40 K. The ρ{sub xx} and ρ{sub xy}the for K-doped BaFeAs{sub 2} thin films were measured by using a physical property measurement system (PPMS) with a temperature sweep (T-sweep) mode at an applied current density of 100 A/cm{sup 2} and at magnetic fields from 0 up to 9 T. We report the T-sweep results of the ρ{sub xx} and the ρ{sub xy} to investigate Hall scaling behavior on the basis of the relation of ρ{sub xy} = A(ρ{sub xy}){sup β}. The ρ{sub xx} values are 3.0 ± 0.2 in the c-axis-oriented K-doped BaFeAs{sub 2} thin films, whereas the thin films with various oriented-directions like a polycrystal showed slightly lower β than that of c-axis-oriented thin films. Interestingly, the β value is decreased with increasing magnetic fields.

Nb3Ge superconductive films grown with nitrogen

International Nuclear Information System (INIS)

Sigsbee, R.A.

1978-01-01

A superconductive film of Nb 3 Ge is produced by providing within a vacuum chamber a heated substrate and sources of niobium and germanium, reducing the pressure within the chamber to a residual pressure no greater than about 10 -5 mm Hg, introducing nitrogen into the resulting evacuated chamber in controlled amounts and vaporizing the niobium and germanium to deposit a film of Nb 3 Ge on the heated substrate

Numerical analysis of micro-/nanoscale gas-film lubrication of sliding surface with complicated structure

International Nuclear Information System (INIS)

Kawagoe, Yoshiaki; Isono, Susumu; Takeno, Takanori; Yonemura, Shigeru; Takagi, Toshiyuki; Miki, Hiroyuki

2014-01-01

It has been reported that the friction between a partially polished diamond-coated surface and a metal surface was drastically reduced to zero when they are slid at a few m/s. Since the sliding was noiseless, it seems that the diamond-coated surface was levitated over the counter surface and the sliding mechanism was the gas film lubrication. Recently, the mechanism of levitation of a slider with a micro/nanoscale surface structure on a rotating disk was theoretically clarified [S. Yonemura et al., Tribol. Lett., (2014), doi:10.1007/s11249-014-0368-2]. Probably, the partially polished diamond-coated surface may be levitated by high gas pressure generated by the micro/nanoscale surface structure on it. In this study, in order to verify our deduction, we performed numerical simulations of sliding of partially polished diamond-coated surface by reproducing its complicated surface structure using the data measured by an atomic force microscope (AFM). As a result, we obtained the lift force which is large enough to levitate the slider used in the experiment

Numerical analysis of micro-/nanoscale gas-film lubrication of sliding surface with complicated structure

Energy Technology Data Exchange (ETDEWEB)

Kawagoe, Yoshiaki; Isono, Susumu; Takeno, Takanori [Department of Nanomechanics, Graduate School of Engineering, Tohoku University, 6-6-01 Aoba, Aramaki, Aoba-ku, Sendai 980-8579 (Japan); Yonemura, Shigeru; Takagi, Toshiyuki [Institute of Fluid Science, Tohoku University, 2-1-1 Katahira, Aoba-ku, Sendai 980-8577 (Japan); Miki, Hiroyuki [Frontier Research Institute for Interdisciplinary Sciences, Tohoku University, 6-3 Aoba, Aramaki, Aoba-ku, Sendai 980-8578 (Japan)

2014-12-09

It has been reported that the friction between a partially polished diamond-coated surface and a metal surface was drastically reduced to zero when they are slid at a few m/s. Since the sliding was noiseless, it seems that the diamond-coated surface was levitated over the counter surface and the sliding mechanism was the gas film lubrication. Recently, the mechanism of levitation of a slider with a micro/nanoscale surface structure on a rotating disk was theoretically clarified [S. Yonemura et al., Tribol. Lett., (2014), doi:10.1007/s11249-014-0368-2]. Probably, the partially polished diamond-coated surface may be levitated by high gas pressure generated by the micro/nanoscale surface structure on it. In this study, in order to verify our deduction, we performed numerical simulations of sliding of partially polished diamond-coated surface by reproducing its complicated surface structure using the data measured by an atomic force microscope (AFM). As a result, we obtained the lift force which is large enough to levitate the slider used in the experiment.

High-performance piezoelectric thick film based energy harvesting micro-generators for MEMS

DEFF Research Database (Denmark)

Zawada, Tomasz; Hansen, Karsten; Lou-Moeller, Rasmus

2010-01-01

and are transformed by the energy harvesting micro-generator into usable electrical signal. The micro-generator comprises a silicon cantilever with integrated InSensor® TF2100 PZT thick film deposited using screen-printing. The output power versus frequency and electrical load has been investigated. Furthermore......, devices based on modified, pressure treated thick film materials have been tested and compared with the commercial InSensor® TF2100 PZT thick films. It has been found that the structures based on the pressure treated materials exhibit superior properties in terms of energy output....

Micropatterned superconducting film circuitry for operation in hybrid quantum devices

International Nuclear Information System (INIS)

Bothner, Daniel

2013-01-01

This thesis discusses three aspects of the arduous way towards hybrid quantum systems consisting of superconducting circuits and ensembles of ultracold paramagnetic atoms. In the first part of the thesis, superconducting coplanar microwave resonators as used for quantum information processing with superconducting qubits are investigated in magnetic fields. In the second part of the thesis integrated atom chips are designed and fabricated, which offer the possibility to trap an ensemble of ultracold atoms close to a superconducting coplanar resonator on that chip. In the third and last part of the thesis, unconventional disordered and quasiperiodic arrangements of microfabricated holes (antidots) in superconducting films are patterned and investigated with respect to the impact of the arrangement on the superconductor transport properties in magnetic fields.

Superconducting TlCa2Ba2Cu3O9 thick films

International Nuclear Information System (INIS)

1994-01-01

GE Corporate Research and Development's (GE-CRD) program to develop the two-zone silver addition (TZSA) process for fabricating superconducting films of TlCa 2 Ba 2 Cu 3 O 9 has activities in the areas of (1) precursor preparation, (2) the thallium oxide vapor process, (3) the effects of post-synthesis annealing ambient and temperature on superconducting properties, (4) the influence of film stoichiometry and composition on superconducting properties, (5) microstructure and film growth mechanism, (6) the preparation of thicker films, (7) the fabrication of films on flexible substrates, and (8) process scale-up. As part of its effort under the ANL Pilot Center Agreement, GE-CRD has supplied to ANL a complete two-zone furnace, has provided consultation on its use and on the planning of experiments, has processed ANL samples in GE's furnaces to help define optimum process conditions, and has provided precursor and finished films as requested. These contributions are described more fully in the descriptions of the work performed at ANL presented elsewhere in this report. Under the Pilot Center Agreement work at GE-CRD has been directed toward the optimization of the TZSA process with emphasis on (A) process improvement, (B) effects of silver content on film properties, (C) the relationship between microstructure and J c , and (D) toward the assessment of the compatibility of silver substrates with the process chemistry

Structure and scintillation properties of CsI(Tl) films on Si single crystal substrates

Energy Technology Data Exchange (ETDEWEB)

Guo, Lina [State Key Laboratory of Electronic Thin Films and Integrated Devices, School of Optoelectronic Information, University of Electronic Science and Technology of China, Chengdu 610054 (China); Liu, Shuang, E-mail: shuangliu@uestc.edu.cn [State Key Laboratory of Electronic Thin Films and Integrated Devices, School of Optoelectronic Information, University of Electronic Science and Technology of China, Chengdu 610054 (China); Chen, Dejun; Zhang, Shangjian; Liu, Yong; Zhong, Zhiyong [State Key Laboratory of Electronic Thin Films and Integrated Devices, School of Optoelectronic Information, University of Electronic Science and Technology of China, Chengdu 610054 (China); Falco, Charles M. [University of Arizona, College of Optical Sciences, AZ 85721 (United States)

2016-10-30

Highlights: • We obtained the desired micro-columnar structure of CsI(Tl) films on the orienting Si substrates. • We improved the micro-columnar structure of CsI(Tl) films under the relatively large deposition rate through using the substrate with a pre-deposited CsI nanolayer. • We modeled the interface structures between the CsI(Tl) films with (200) and (310) orientation and Si(111) substrates to explain the preferred orientation of film under the influence of the orienting substrate significantly. • We gained a new spectrum of the CsI(Tl) films peaked at 740 nm wavelength. - Abstract: CsI(Tl) scintillation films fabricated on glass substrates are widely applied for X-ray imaging because their ability to grow in micro-columnar structure and proper emission wavelength matching CCD cameras. But the coupling process between the CsI(Tl) films and Si-based photo detector would cause coupling loss. In this work, CsI(Tl) films were deposited on the orienting Si substrates and the Si substrates covered by the pre-deposited CsI nanolayers. Structure and scintillation properties of films were examined by using scanning electron microscopy, X-ray diffraction, photoluminescence and radioluminescent spectrum. The films deposited on the orienting Si substrates show the micro-columnar morphology with perfect single crystalline structure and the photoluminescence spectra with bimodal distribution. The performances of the films prepared on the pre-deposited CsI nanolayer, containing micro-columns structure and the light yield are improved.

Structure and scintillation properties of CsI(Tl) films on Si single crystal substrates

International Nuclear Information System (INIS)

Guo, Lina; Liu, Shuang; Chen, Dejun; Zhang, Shangjian; Liu, Yong; Zhong, Zhiyong; Falco, Charles M.

2016-01-01

Highlights: • We obtained the desired micro-columnar structure of CsI(Tl) films on the orienting Si substrates. • We improved the micro-columnar structure of CsI(Tl) films under the relatively large deposition rate through using the substrate with a pre-deposited CsI nanolayer. • We modeled the interface structures between the CsI(Tl) films with (200) and (310) orientation and Si(111) substrates to explain the preferred orientation of film under the influence of the orienting substrate significantly. • We gained a new spectrum of the CsI(Tl) films peaked at 740 nm wavelength. - Abstract: CsI(Tl) scintillation films fabricated on glass substrates are widely applied for X-ray imaging because their ability to grow in micro-columnar structure and proper emission wavelength matching CCD cameras. But the coupling process between the CsI(Tl) films and Si-based photo detector would cause coupling loss. In this work, CsI(Tl) films were deposited on the orienting Si substrates and the Si substrates covered by the pre-deposited CsI nanolayers. Structure and scintillation properties of films were examined by using scanning electron microscopy, X-ray diffraction, photoluminescence and radioluminescent spectrum. The films deposited on the orienting Si substrates show the micro-columnar morphology with perfect single crystalline structure and the photoluminescence spectra with bimodal distribution. The performances of the films prepared on the pre-deposited CsI nanolayer, containing micro-columns structure and the light yield are improved.

Interface-Induced Zeeman-Protected Superconductivity in Ultrathin Crystalline Lead Films

Directory of Open Access Journals (Sweden)

Yi Liu

2018-04-01

Full Text Available Two-dimensional (2D superconducting systems are of great importance for exploring exotic quantum physics. The recent development of fabrication techniques has stimulated studies of high-quality single-crystalline 2D superconductors, where intrinsic properties give rise to unprecedented physical phenomena. Here, we report the observation of Zeeman-type spin-orbit interaction protected superconductivity (Zeeman-protected superconductivity in 4-monolayer (ML to 6-ML crystalline Pb films grown on striped incommensurate Pb layers on Si(111 substrates by molecular beam epitaxy. An anomalously large in-plane critical field far beyond the Pauli limit is detected, which can be attributed to the Zeeman-protected superconductivity due to the in-plane inversion symmetry breaking at the interface. Our work demonstrates that, in superconducting heterostructures, the interface can induce Zeeman-type spin-orbit interactions and modulate the superconductivity.

Characterization of the microwave properties of superconducting films with high transition temperature

International Nuclear Information System (INIS)

Richter, W.; Klinger, M.; Daginnus, M.

1989-01-01

In the meantime high quality Y-Ba-Cu-O thin films were produced. The latest results show, that its surface resistances are clearly lower than the values of copper, measured at a temperature of 77 K and up to frequencies of 86 GHz. This examination had the aim to produce high-T c films with a simple and low cost method, to use them as transmission lines at frequencies up to 30 GHz and above. A screen printing process was investigated, and high-T c thick films were fabricated on several substrates. Superconducting transition temperatures up to 80 K (dc zero resistance) were obtained. The films showed no complete magnetic shielding, and its microwave surface resistances were clearly higher than that ones for copper. The a. c. Josephson effect was proved with granular structures of bulk Y-Ba-Cu-O material and with screen printed thick films. Because of its high surface resistances, these thick films are unsuitable for the use as transmission lines at high frequencies. However, the a.c. Josephson effect can be used to manufacture microwave sensors in bulk Y-Ba-Cu-O and screen printed films of Y-Ba-Cu-O, which have a favourable geometric structure. (orig.) With 16 refs., 2 tabs., 24 figs [de

Growth of superconducting Bi/sub 2/Sr/sub 2/CaCu/sub 2/O/sub 8+//sub x/ films on alumina, silicon, and fused quartz

International Nuclear Information System (INIS)

Hung, L.S.; Agostinelli, J.A.; Paz-Pujalt, G.R.; Mir, J.M.

1988-01-01

Interactions between superconducting Bi/sub 2/Sr/sub 2/CaCu/sub 2/O/sub 8+//sub x/ films and substrates were investigated by ion backscattering, x-ray diffraction, and four-point probe resistivity measurements. During annealing at temperatures above- 800 /sup 0/C, Bi/sub 2/Sr/sub 2/CaCu/sub 2/ oxide films rapidly reacted with alumina, Si, Si covered with SiO/sub 2/, and quartz, resulting in catastrophic failure. Zr-based barrier layers were used to minimize film-substrate interactions. When a single ZrO/sub 2/ layer was interposed between the superconducting oxide film and the underlying substrate, the Bi/sub 2/Sr/sub 2/CaCu/sub 2/ oxide films showed a large-grained polycrystalline microstructure and exhibited the orthorhombic structure. Films on sapphire showed transitions to the superconducting state beginning near 100 K with zero resistance achieved at 70 K. Films on Si and thermally grown SiO/sub 2/ showed a similar drop in resistance around 95 K, whereas the transition was broad and the zero resistance state was not reached. For films on quartz, high thermal stress caused cracking of the superconducting oxide film. Best results were achieved using a barrier composed of a Zr-Si-O mixed layer underneath ZrO/sub 2/. In this case, the films grown on Si and quartz were uniform and showed the onset to superconductivity at 95 K, attaining zero resistance at 70 K

A novel collagen film with micro-rough surface structure for corneal epithelial repair fabricated by freeze drying technique

International Nuclear Information System (INIS)

Liu, Yang; Ren, Li; Wang, Yingjun

2014-01-01

Highlights: • Collagen film with micro-rough surface is fabricated by freeze drying technique. • The film has suitable water uptake capability and toughness performance. • The film has good optical performance. • Human corneal epithelial cells studies confirmed the biocompatibility of the film. - Abstract: Corneal epithelial defect is a common disease and keratoplasty is a common treatment method. A collagen film with micro-rough surface was fabricated through a simple freeze drying technique in this study. Compared with the air-dried collagen film (AD-Col), this freeze-dried collagen film (FD-Col) has a more suitable water uptake capability (about 85.5%) and toughness performance. Both of the two films have good optical properties and the luminousness of them is higher than 80%. Besides, the adhesion and proliferation rate of human corneal epithelial cells on the micro-rough surface of FD-Col film is higher than that on the smooth surface of AD-Col film. The results indicate that this FD-Col film may have potential applications for corneal epithelial repair

A novel collagen film with micro-rough surface structure for corneal epithelial repair fabricated by freeze drying technique

Energy Technology Data Exchange (ETDEWEB)

Liu, Yang [School of Materials Science and Engineering, South China University of Technology, Guangzhou 510641 (China); National Engineering Research Center for Tissue Restoration and Reconstruction, Guangzhou 510006 (China); Guangdong Province Key Laboratory of Biomedical Engineering, South China University of Technology, Guangzhou 510006 (China); Ren, Li, E-mail: psliren@scut.edu.cn [School of Materials Science and Engineering, South China University of Technology, Guangzhou 510641 (China); National Engineering Research Center for Tissue Restoration and Reconstruction, Guangzhou 510006 (China); Guangdong Province Key Laboratory of Biomedical Engineering, South China University of Technology, Guangzhou 510006 (China); Wang, Yingjun, E-mail: imwangyj@163.com [School of Materials Science and Engineering, South China University of Technology, Guangzhou 510641 (China); National Engineering Research Center for Tissue Restoration and Reconstruction, Guangzhou 510006 (China); Guangdong Province Key Laboratory of Biomedical Engineering, South China University of Technology, Guangzhou 510006 (China)

2014-05-01

Highlights: • Collagen film with micro-rough surface is fabricated by freeze drying technique. • The film has suitable water uptake capability and toughness performance. • The film has good optical performance. • Human corneal epithelial cells studies confirmed the biocompatibility of the film. - Abstract: Corneal epithelial defect is a common disease and keratoplasty is a common treatment method. A collagen film with micro-rough surface was fabricated through a simple freeze drying technique in this study. Compared with the air-dried collagen film (AD-Col), this freeze-dried collagen film (FD-Col) has a more suitable water uptake capability (about 85.5%) and toughness performance. Both of the two films have good optical properties and the luminousness of them is higher than 80%. Besides, the adhesion and proliferation rate of human corneal epithelial cells on the micro-rough surface of FD-Col film is higher than that on the smooth surface of AD-Col film. The results indicate that this FD-Col film may have potential applications for corneal epithelial repair.

Controllable manipulation of superconductivity using magnetic vortices

International Nuclear Information System (INIS)

Villegas, J E; Schuller, Ivan K

2011-01-01

The magneto-transport of a superconducting/ferromagnetic hybrid structure, consisting of a superconducting thin film in contact with an array of magnetic nanodots in the so-called 'magnetic vortex state', exhibits interesting properties. For certain magnetic states, the stray magnetic field from the vortex array is intense enough to drive the superconducting film into the normal state. In this fashion, the normal-to-superconducting phase transition can be controlled by the magnetic history. The strong coupling between superconducting and magnetic subsystems allows characteristically ferromagnetic properties, such as hysteresis and remanence, to be dramatically transferred into the transport properties of the superconductor.

Bi-Sr-Ca-Cu-O superconducting thin films: theory and experiment

Energy Technology Data Exchange (ETDEWEB)

Yavuz, M [Department of Mechanical Engineering and Mechatronics Engineering Program, University of Waterloo, Waterloo, Ontario N2L 3G1 (Canada); Boybay, M S [Department of Mechanical Engineering and Mechatronics Engineering Program, University of Waterloo, Waterloo, Ontario N2L 3G1 (Canada); Elbuken, C [Department of Mechanical Engineering and Mechatronics Engineering Program, University of Waterloo, Waterloo, Ontario N2L 3G1 (Canada); Andrews, M J [Los Alamos National Lab, PO Box 1663, Mail Stop B 296, Los Alamos, NM 87545 (United States); Hu, C R [Department of Physics, Texas A and M University, College Station, Texas 77843 (United States); Ross, J H [Department of Physics, Texas A and M University, College Station, Texas 77843 (United States)

2006-06-01

The interest of this paper centers on fabrication and characterization and modeling of vortices in high temperature superconducting thin films. As a first step, the magnetic vertices of the superconducting matrix were modeled. As a second, Bi-Sr-Ca-Cu-O thin films were grown using Pulsed Laser Ablation (PLD) on single crystal MgO substrates as magnetic templates for the potential use for Nano and Microelectronic circuits, and were characterized by x-ray diffraction, electron, and atomic force microscopy. The third step (future work) will be observation and pinning of these vortices using Bitter decoration.

Analysis of influence of buffer layers on microwave propagation through high-temperature superconducting thin films

International Nuclear Information System (INIS)

Ceremuga, J.; Barton, M.; Miranda, F.

1994-01-01

Methods of analysis of microwave propagation through superconducting thin films with buffer layers on dielectric substrates have been discussed. Expressions describing the transmission coefficient S 21 through the structure and the complex conductivity sigma of a superconductor in an analytical form have been derived. The derived equations are valid for microwave propagation in waveguides as well as in free space with relevant definition of impedances. Using the obtained solutions, the influences of buffer layers' parameters (thickness, relative permittivity and loss tangent) on the transmission coefficient has been investigated using MATLAB. Simulations have been performed for 10 GHz transmission through YBa 2 Cu 3 O 7 films on sapphire with SrTiO 3 and CeO 2 buffer layers and on silicon with CaF 2 and YSZ buffer layers. To illustrate the simulations, measurements of the transmission through YBCO film on sapphire with SrTiO 3 buffer layer have been performed. It has been shown that even lossy buffer layers have very little impact (smaller than 1% in magnitude and 0.3% in phase) on the transmission coefficient through superconducting thin films, providing their thickness is below 10 mu m. (author)

Micro-nanofibers with hierarchical structure by bubbfil-spinning

Directory of Open Access Journals (Sweden)

Liu Peng

2015-01-01

Full Text Available Bubbfil spinning is used to fabricate micro/nanofibers with hierarchical structure. The wall of a polymer film is attenuated unevenly by a blowing air. The burst of the bubble results in film fragments with different thickness, as a result, different sizes of fibers are obtained.

Superconducting structure with layers of niobium nitride and aluminum nitride

International Nuclear Information System (INIS)

Murduck, J.M.; Lepetre, Y.J.; Schuller, I.K.; Ketterson, J.B.

1989-01-01

A superconducting structure is formed by depositing alternate layers of aluminum nitride and niobium nitride on a substrate. Deposition methods include dc magnetron reactive sputtering, rf magnetron reactive sputtering, thin-film diffusion, chemical vapor deposition, and ion-beam deposition. Structures have been built with layers of niobium nitride and aluminum nitride having thicknesses in a range of 20 to 350 Angstroms. Best results have been achieved with films of niobium nitride deposited to a thickness of approximately 70 Angstroms and aluminum nitride deposited to a thickness of approximately 20 Angstroms. Such films of niobium nitride separated by a single layer of aluminum nitride are useful in forming Josephson junctions. Structures of 30 or more alternating layers of niobium nitride and aluminum nitride are useful when deposited on fixed substrates or flexible strips to form bulk superconductors for carrying electric current. They are also adaptable as voltage-controlled microwave energy sources. 8 figs

Thermal Stress Behavior of Micro- and Nano-Size Aluminum Films

International Nuclear Information System (INIS)

Hanabusa, T.; Kusaka, K.; Nishida, M.

2008-01-01

In-situ observation of thermal stresses in thin films deposited on silicon substrate was made by X-ray and synchrotron radiation. Specimens prepared in this experiment were micro- and nano-size thin aluminum films with and without passivation film. The thickness of the film was 1 micrometer for micro-size films and 10, 20 and 50 nanometer for nano-size films. The stress measurement in micro-size films was made by X-ray radiation whereas the measurement of nano-size films was made by synchrotron radiation. Residual stress measurement revealed tensile stresses in all as-deposited films. Thermal stresses were measured in a series of heating- and cooling-stage. Thermal stress behavior of micro-size films revealed hysteresis loop during a heating and cooling process. The width of a hysteresis loop was larger in passivated film that unpassivated film. No hysteresis loops were observed in nano-size films with SiO 2 passivation. Strengthning mechanism in thin films was discussed on a passivation film and a film thickness

Magnetic and superconductivity studies on (In{sub 1−x}Fe{sub x}){sub 2}O{sub 3} thin films

Energy Technology Data Exchange (ETDEWEB)

Sai Krishna, N. [Thin Films Laboratory, School of Advanced Sciences, VIT University, Vellore 632 014, Tamil Nadu (India); Kaleemulla, S., E-mail: skaleemulla@gmail.com [Thin Films Laboratory, School of Advanced Sciences, VIT University, Vellore 632 014, Tamil Nadu (India); Amarendra, G. [Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102, Tamil Nadu (India); UGC-DAE-CSR, Kalpakkam Node, Kokilamedu 603 104, Tamil Nadu (India); Madhusudhana Rao, N.; Krishnamoorthi, C.; Rigana Begam, M. [Thin Films Laboratory, School of Advanced Sciences, VIT University, Vellore 632 014, Tamil Nadu (India); Omkaram, I. [Department of Electronics and Radio Engineering, Kyung Hee University, Yongin-si Gyeonggi-do 446-701 (Korea, Republic of); Sreekantha Reddy, D. [Department of Physics and Sungkyunkwan Advanced Institute of Nanotechnology (SAINT), Sungkyunkwan University, Suwon 440-746 (Korea, Republic of)

2015-07-15

Highlights: • Fe doped In{sub 2}O{sub 3} thin films deposited using electron beam evaporation technique. • Characterization of the samples using XRD, SEM, EDAX, AES, Raman spectroscopy, FT-IR, VSM and magnetoresistance. • All Fe doped In{sub 2}O{sub 3} thin films exhibited the cubic structure of In{sub 2}O{sub 3}. • Pure and Fe doped In{sub 2}O{sub 3} samples exhibited room temperature ferromagnetism and superconductivity at 2 K. - Abstract: Magnetic, magnetoresistivity and superconductivity studies were carried out on (In{sub 1−x}Fe{sub x}){sub 2}O{sub 3} (x = 0.00, 0.03, 0.05 and 0.07) thin films (2D structures) grown on glass substrate by electron beam evaporation technique at 350 °C. The films have an average size of 120 nm particles. All the samples shown soft ferromagnetic hysteresis loops at room temperature and saturation magnetization increased with iron dopant concentration. Observed magnetization could be best interpreted by F-center mediated magnetic exchange interaction in the samples. Temperature dependent resistivity of the sample (x = 0.00 and 0.07) showed metallic behavior down to very low temperatures and superconductivity at 2 K for undoped In{sub 2}O{sub 3} whereas the In{sub 1.86}Fe{sub 0.14}O{sub 3} sample shows superconductivity below 2 K in the absence of magnetic fields. The reduction in transition temperature was attributed to increase electrical disorder with iron doping. Both samples showed positive magnetoresistivity (MR) in superconducting state due to increase of resistivity resulting from breaking of superconducting Cooper pairs upon application of magnetic field. In addition, both the samples show feeble negative MR in normal electrical state. The observed MR in normal state is not due to spin polarized tunneling instead it is due to suppression of scattering of charge carrier by single occupied localized states.

Studies of the Superconducting Transition in the Mo/Au-Bilayer Thin Films

Science.gov (United States)

Sadleir, John; Smith, Stephen; Iyomoto, naoko; Bandler, Simon; Chervenak, Jay; Brown, Ari; Brekowsky, Regis; Kilbourne, Caroline; Robinson, Ian

2007-01-01

At NASA Goddard, microcalorimeter arrays using superconducting transition edge sensor thermometers (TESs) are under development for high energy resolution X-ray astrophysics applications. We report on our studies of the superconducting transition in our Mo/Au-bilayer TES films including: low current measurements of the superconducting bilayer's resistance transition versus temperature on pixels with different normal metal absorber attachment designs and measured temperature scaling of the critical current and critical magnetic field.

Lead-doped electron-beam-deposited Bi-Sr-Ca-Cu-O superconducting thin films

Energy Technology Data Exchange (ETDEWEB)

Agnihotry, S.A.; Saini, K.K.; Kant, C.; Sharma, C.P.; Ekbote, S.N.; Asthana, P.; Nagpal, K.C.; Chandra, S. (National Physical Lab., New Delhi (India))

1991-03-20

Superconducting thin films of the lead-doped Bi-Sr-Ca-Cu-O system have been prepared on (100) single-crystal SrTiO{sub 3} substrates by an electron beam deposition technique using a single sintered pellet as the evaporation source. As-deposited films are amorphous and non-superconducting; post-deposition annealing at an optimized temperature in air has been found to result in crystalline and superconducting films. The superconducting characteristics of the films have been observed to be sensitive not only to the duration and temperature of post-deposition annealing but also to the lead content and the sintering parameters for the pellet to be used as the evaporation source. A pellet with nominal composition Bi{sub 3}Pb{sub 1}Sr{sub 3}Ca{sub 3}Cu{sub 4}O{sub y} that had been sintered for 200 h zero resistivity Tc{sup 0}=112 K. However, films deposited using such a pellet as the evaporation source had Tc{sup 0} {approx equal} 73-78 K, as had the films deposited from a pellet without any lead. We investigated systematically films deposited from pellets with more lead and sintered for different durations. It is evident from these investigations that pellets with nominal composition Bi{sub 3}Pb{sub 2}Sr{sub 3}Ca{sub 3}Cu{sub 4}O{sub y}, i.e. with an excess of lead, and sintered for about 75 h when used as the evaporation source yield films with Tc{sup 0} {approx equal} 100 K when annealed between 835 and 840deg C for an optimized long duration. The films are characterized by X-ray diffraction and energy-dispersive spectroscopy techniques and have been found to be highly c axis oriented. The effect of lead in promoting a high Tc{sup 0}=110 K phase seems to be similar to that in bulk ceramics. (orig.).

Preparation and characterization of micro-grid modified In{sub 2}O{sub 3}:W films

Energy Technology Data Exchange (ETDEWEB)

Dong, Dongmei; Wang, Wenwen, E-mail: 08569@buaa.edu.cn; Zhang, Fan; Fu, Qiang; Pan, Jiaojiao

2016-08-01

Tungsten doped indium oxide (In{sub 2}O{sub 3}:W, IWO) thin films with IWO micro-grid covered surface were prepared at room temperature using techniques of radio frequency (RF) magnetron sputtering and polystyrene (PS) microsphere template. The composition, crystallization structures, surface morphologies, and optical and electrical properties of the films were characterized by X-ray photoelectron spectroscopy, X-ray diffraction, scanning electron microscopy, spectrophotometer from visible to near infrared (NIR) range and Hall effect measurement, respectively. Periodic micro-grid modified surface was obtained to improve light trapping properties. The effects of the PS micro-spheres diameters and the sputtering time on the surface morphology, transmittance in NIR range, diffuse reflection and conductive properties of the IWO films are investigated. Experiments show that surface modification of the IWO film with micro-grid under the optimized condition can improve the conductivity of the films by 15%, and the diffuse reflectance by 150%, with less than 8% decrease of the transmittance in the visible region. The study would be beneficial to the light trapping effect of solar cells using IWO films as transparent electrodes. - Highlights: • In{sub 2}O{sub 3}:W (IWO) films were obtained by reactive frequency magnetron sputtering. • IWO micro-grids were prepared on the surface of IWO films. • Influences of micro-grid size and sputtering time on IWO films were analyzed. • Both high conductivity and transparency are acquired in near-infrared region.

Thermal coupling effect on the vortex dynamics of superconducting thin films: time-dependent Ginzburg–Landau simulations

Science.gov (United States)

Jing, Ze; Yong, Huadong; Zhou, Youhe

2018-05-01

In this paper, vortex dynamics of superconducting thin films are numerically investigated by the generalized time-dependent Ginzburg–Landau (TDGL) theory. Interactions between vortex motion and the motion induced energy dissipation is considered by solving the coupled TDGL equation and the heat diffusion equation. It is found that thermal coupling has significant effects on the vortex dynamics of superconducting thin films. Branching in the vortex penetration path originates from the coupling between vortex motion and the motion induced energy dissipation. In addition, the environment temperature, the magnetic field ramp rate and the geometry of the superconducting film also greatly influence the vortex dynamic behaviors. Our results provide new insights into the dynamics of superconducting vortices, and give a mesoscopic understanding on the channeling and branching of vortex penetration paths during flux avalanches.

Critical currents in multilayered superconducting films

International Nuclear Information System (INIS)

Raffy, Helene

1977-01-01

The superconducting critical currents Isub(c) were measured as a function of magnetic field H and temperature T, on multilayered films. These films consist of alternating layers of two different superconductors S 1 and S 2 being a weaker superconductor acting as a flux pinning barrier region. A strong anisotropy was observed between the two situations where the magnetic field H is applied parallel or perpendicular to the layers. In the case discussed, there is a peak effect in the curves Isub(c)H well defined at the highest temperatures, and disappearing at low temperatures. The anisotropy of the critical current at constant field presents a maximum at a temperature T* close to the critical temperature Tsub(c 2 ) of S 2 [fr

Frequency Invariability of (Pb,La)(Zr,Ti)O₃ Antiferroelectric Thick-Film Micro-Cantilevers.

Science.gov (United States)

An, Kun; Jin, Xuechen; Meng, Jiang; Li, Xiao; Ren, Yifeng

2018-05-13

Micro-electromechanical systems comprising antiferroelectric layers can offer both actuation and transduction to integrated technologies. Micro-cantilevers based on the (Pb 0.97 La 0.02 )(Zr 0.95 Ti 0.05 )O₃ (PLZT) antiferroelectric thick film are fabricated by the micro-nano manufacturing process, to utilize the effect of phase transition induced strain and sharp phase switch of antiferroelectric materials. When micro-cantilevers made of antiferroelectric thick films were driven by sweep voltages, there were two resonant peaks corresponding to the natural frequency shift from 27.8 to 27.0 kHz, before and after phase transition. This is the compensation principle for the PLZT micro-cantilever to tune the natural frequency by the amplitude modulation of driving voltage, rather than of frequency modulation. Considering the natural frequency shift about 0.8 kHz and the frequency tuning ability about 156 Hz/V before the phase transition, this can compensate the frequency shift caused by increasing temperature by tuning only the amplitude of driving voltage, when the ultrasonic micro-transducer made of antiferroelectric thick films works for such a long period. Therefore, antiferroelectric thick films with hetero-structures incorporated into PLZT micro-cantilevers not only require a lower driving voltage (no more than 40 V) than rival bulk piezoelectric ceramics, but also exhibit better performance of frequency invariability, based on the amplitude modulation.

Vortex variable range hopping in a conventional superconducting film

Science.gov (United States)

Percher, Ilana M.; Volotsenko, Irina; Frydman, Aviad; Shklovskii, Boris I.; Goldman, Allen M.

2017-12-01

The behavior of a disordered amorphous thin film of superconducting indium oxide has been studied as a function of temperature and magnetic field applied perpendicular to its plane. A superconductor-insulator transition has been observed, though the isotherms do not cross at a single point. The curves of resistance versus temperature on the putative superconducting side of this transition, where the resistance decreases with decreasing temperature, obey two-dimensional Mott variable-range hopping of vortices over wide ranges of temperature and resistance. To estimate the parameters of hopping, the film is modeled as a granular system and the hopping of vortices is treated in a manner analogous to hopping of charges. The reason the long-range interaction between vortices over the range of magnetic fields investigated does not lead to a stronger variation of resistance with temperature than that of two-dimensional Mott variable-range hopping remains unresolved.

Superconducting thin films of Bi-Sr-Ca-Cu-O by laser ablation

International Nuclear Information System (INIS)

Bedekar, M.M.

1992-01-01

The discovery of a new class of copper oxide superconductors has led to the development of three major systems that exhibit superconducting properties. The Bi-Sr-Ca-Cu-O superconductors offer intrinsic advantages due to the high T c , chemical inertness and tolerance for a range of compositions. However, thin film research on these materials has progressed more slowly than the other cuprate systems. This dissertation examines the film growth, by laser ablation, of the Bi-Sr-Ca-Cu-O superconductors and the effect of the deposition parameters such as the laser target interaction, substrate temperature, target to substrate distance, deposition and cooling pressure, target type and processing and the substrate type. CO 2 laser ablation was shown to give rise to a non-stoichiometric material transfer due to the low fluences and long pulse lengths. In situ superconducting thin films with T c(0) 's of 76 K could be deposited using the KrF laser at substrate temperatures of 5 degrees C to 20 degrees C below phases. Lower temperatures gave rise to a mixture of 2201 and glassy phases. An increase in the target to substrate distance led to a deterioration of the electrical and structural properties of the films due to a decrease in the energy for film formation. A maximum in T c(0) was observed at 450 mtorr as the deposition pressure was varied between 200 to 700 mtorr. Optimum oxygen incorporation could be achieved by cooling the films in high oxygen pressures and the best films were obtained with 700 torr cooling pressure. The oxygen deficiency of the hot pressed targets led to inferior properties compared to the conventionally sintered targets. The microwave surface resistance of the films measured at 35 GHz showed an onset at 80 K and dropped below that of copper at 30 K. The study of the laser ablation process in this system revealed the presence of a stoichiometric forward directed component and a diffuse evaporation component

Local imaging of magnetic flux in superconducting thin films

International Nuclear Information System (INIS)

Shapoval, Tetyana

2010-01-01

Local studies of magnetic flux line (vortex) distribution in superconducting thin films and their pinning by natural and artificial defects have been performed using low-temperature magnetic force microscopy (LT-MFM). Taken a 100 nm thin NbN film as an example, the depinning of vortices from natural defects under the influence of the force that the MFM tip exerts on the individual vortex was visualized and the local pinning force was estimated. The good agreement of these results with global transport measurements demonstrates that MFM is a powerful and reliable method to probe the local variation of the pinning landscape. Furthermore, it was demonstrated that the presence of an ordered array of 1-μm-sized ferromagnetic permalloy dots being in a magneticvortex state underneath the Nb film significantly influences the natural pinning landscape of the superconductor leading to commensurate pinning effects. This strong pinning exceeds the repulsive interaction between the superconducting vortices and allows vortex clusters to be located at each dot. Additionally, for industrially applicable YBa 2 Cu 3 O 7-δ thin films the main question discussed was the possibility of a direct correlation between vortices and artificial defects as well as vortex imaging on rough as-prepared thin films. Since the surface roughness (droplets, precipitates) causes a severe problem to the scanning MFM tip, a nanoscale wedge polishing technique that allows to overcome this problem was developed. Mounting the sample under a defined small angle results in a smooth surface and a monotonic thickness reduction of the film along the length of the sample. It provides a continuous insight from the film surface down to the substrate with surface sensitive scanning techniques. (orig.)

Direct Observation of High-Temperature Superconductivity in One-Unit-Cell FeSe Films

International Nuclear Information System (INIS)

Zhang Wen-Hao; Zhang Jin-Song; Li Fang-Sen; Guo Ming-Hua; Ding Hao; Tang Chen-Jia; Wang Qing-Yan; He Ke; Ji Shuai-Hua; Chen Xi; Sun Yi; Zhao Yan-Fei; Xing Ying; Wang Hui-Chao; Zhang Hui-Min; Peng Jun-Ping; Li Zhi; Wang Meng; Fujita Takeshi; Hirata Akihiko

2014-01-01

We prepared one-unit-cell (1-UC) thick FeSe films on insulating SrTiO 3 substrates with non-superconducting FeTe protection layers by molecular beam epitaxy for ex situ studies. By direct transport and magnetic measurements, we provide definitive evidence for high temperature superconductivity in the 1-UC FeSe films with an onset T C above 40 K and an extremely large critical current density J C ∼1.7×10 6 A/cm 2 at 2 K, which are much higher than T C ∼8 K and J C ∼10 4 A/cm 2 for bulk FeSe, respectively. Our work may pave the way to enhancing and tailoring superconductivity by interface engineering. (express letter)

Vortex loops in the critical Casimir effect in superfluid and superconducting films

International Nuclear Information System (INIS)

Williams, Gary A.

2004-01-01

Vortex-loop renormalization techniques are used to calculate the magnitude of the critical Casimir forces in superfluid and superconducting thin films. The force is found to become appreciable when the size of the thermally excited vortex loops is comparable to the film thickness, and the results for T c are found to match very well with perturbative renormalization-group theories that can only be carried out for T>T c . In helium films the Casimir force leads to a change in the film thickness close to T c that has been observed experimentally. A similar effect is predicted to occur near the transition temperature of high-T c superconducting films, which is also a vortex-loop phase transition. In this case the Casimir force takes the form of a voltage difference that will appear at the junction between a thin film and a bulk sample. Estimates show that this voltage can be appreciable (tens of microvolts), and it may be possible to observe the effect by measuring the voltage across two Josephson tunnel junctions to the film and to the bulk, using a SQUID voltmeter

High-Tc Superconducting Thick-Film Spiral Magnet: Development and Characterization of a Single Spiral Module

National Research Council Canada - National Science Library

McGinnis, W

1997-01-01

The objective of this project was to make characterized and numerically model prototype modules of a new type of superconducting electromagnet based on stacked spirals of superconducting thick films...

Growth of Ag micro/nanoparticles using stress migration from multilayered metallic structure

International Nuclear Information System (INIS)

Lu, Yebo; Li, Yuan; Saka, Masumi

2015-01-01

Highlights: • A multilayered metallic structure was proposed to fabricate Ag micro/nanoparticles via stress migration. • Both ductile Pt and brittle TiN films can be used as the passivation layer by providing pathways for atomic migration. • The diameter of the formed Ag particle can be controlled using different material for passivation layer and changing the heating temperature. - Abstract: A multilayered metallic structure, consisting of Cu foil and subsequently deposited Ag thin film covered with a passivation layer, was proposed to fabricate Ag micro/nanoparticles by stress migration. With employing a ductile Pt or brittle TiN thin film as passivation, Ag micro/nanoparticles were successfully fabricated by annealing the corresponding multilayered structure. The relationship between characteristics (average diameter, number and volume) of the formed Ag micro/nanoparticles and the annealing temperature was discussed. On this basis, the growth mechanism was developed, which indicates that the dimension of Ag particles was mainly dominated by the different pathways for the migration of diffused Ag atoms in the passivation layers of Pt and TiN and the annealing temperature

Stability of Tl-Ba-Ca-Cu-O Superconducting Thin Films

Energy Technology Data Exchange (ETDEWEB)

Siegal, M.P.; Overmyer, D.L.; Venturini, E.L.; Padilla, R.R.; Provencio, P.N.

1999-08-23

We report the stability of TlBa{sub 2}CaCu{sub 2}O{sub 7} (Tl-1212) and Tl{sub 2}Ba{sub 2}CaCu{sub 2}O{sub 8} (T1-2212) thin films and by inference, the stability of TlBa{sub 2}Ca{sub 2}Cu{sub 3}O{sub 9} (Tl-1223) and Tl{sub 2}Ba{sub 2}Ca{sub 2}Cu{sub 3}O{sub 10} (Tl-2223) thin films, under a variety of conditions. In general, we observe that the stability behavior of the single Tl-O layer materials (Tl-1212 and Tl-1223)are similar and the double Tl-O layer materials (Tl-2212 and Tl-2223) are similar. All films are stable with repeated thermal cycling to cryogenic temperatures. Films are also stable in acetone and methanol. Moisture degrades film quality rapidly, especially in the form of vapor. Tl-1212 is more sensitive to vapor than Tl-2212. These materials are stable to high temperatures in either N{sub 2}, similar to vacuum for the cuprates, and O{sub 2} ambients. While total degradation of properties (superconducting and structural) occur at the same temperatures for all phases, 600 C in N{sub 2} and 700 C in O{sub 2}, the onset of degradation occurs at somewhat lower temperatures for Tl-1212 than for Tl-2212 films. In all cases, sample degradation is associated with Tl depletion from the films.

A review of basic phenomena and techniques for sputter-deposition of high temperature superconducting films

Energy Technology Data Exchange (ETDEWEB)

Auciello, O. (Microelectronics Center of North Carolina, Research Triangle Park, NC (USA) North Carolina State Univ., Raleigh, NC (USA). Dept. of Materials Science and Engineering); Ameen, M.S.; Kingon, A.I.; Lichtenwalner, D.J. (North Carolina State Univ., Raleigh, NC (USA). Dept. of Materials Science and Engineering); Krauss, A.R. (Argonne National Lab., IL (USA))

1990-01-01

The processes involved in plasma and ion beam sputter-deposition of high temperature superconducting thin films are critically reviewed. Recent advances in the development of these techniques are discussed in relation to basic physical phenomena, specific to each technique, which must be understood before high quality films can be produced. Control of film composition is a major issue in sputter-deposition of multicomponent materials. Low temperature processing of films is a common goal for each technique, particularly in relation to integrating high temperature superconducting films with the current microelectronics technology. It has been understood for some time that for Y{sub 1}Ba{sub 2}Cu{sub 3}O{sub 7} deposition, the most intensely studied high-{Tc} compound, incorporation of sufficient oxygen into the film during deposition is necessary to produce as-deposited superconducting films at relatively substrate temperatures. Recent results have shown that with the use of suitable buffer layers, high quality Y{sub 1}Ba{sub 2}Cu{sub 3}O{sub 7} sputtered films can be obtained on Si substrates without the need for post-deposition anneal processing. This review is mainly focussed on issues related to sputter-deposition of Y{sub 1}Ba{sub 2}Cu{sub 3}O{sub 7} thin films, although representative results concerning the bismuth and thallium based compounds are included. 143 refs., 11 figs.

Surface characterization of superconductive Nd1Ba2Cu3Oy thin films using scanning probe microscopes

International Nuclear Information System (INIS)

Ting, W.; Badaye, M.; Itti, R.; Morishita, T.; Koshizuka, N.; Tanaka, S.

1996-01-01

Recently, superconductive Nd 1 Ba 2 Cu 3 O y (Nd123) thin films with high superconducting transition temperature (T c ) have been successfully fabricated at the authors institute employing the standard laser ablation method. In this paper, they report parts of the results of surface characterization of the Nd123 thin films using an ultrahigh vacuum scanning tunneling microscope/spectroscopy (UHV-STM/STS) and an atomic force microscope (AFM) system operated in air. Clear spiral pattern is observed on the surfaces of Nd123 thin films by STM and AFM, suggesting that films are formed by two-dimensional island growth mode at the final growing stage. Contour plots of the spirals show that the step heights of the spirals are not always the integer or half integer numbers of the c-axis parameter of the structure. This implies that the surface natural termination layer of the films may not be unique. Surface atomic images of the as-prepared Nd123 thin films are obtained employing both STM and AFM. STS measurements show that most of the surfaces are semiconductive, or sometimes even metallic. The results of STS measurements together with the fact that they are able to see the surface atomic images using scanning probe microscopes suggest that exposure to air does not cause serious degradation to the as-prepared surfaces of Nd123 thin films

Nano-engineered pinning centres in YBCO superconducting films

Energy Technology Data Exchange (ETDEWEB)

Crisan, A., E-mail: adrian.crisan@infim.ro [National Institute for Materials Physics Bucharest, 105 bis Atomistilor Str., 077125 Magurele (Romania); School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Dang, V.S. [School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Nano and Energy Center, VNU Hanoi University of Science, 334 Nguyen Trai, Thanh Xuan, Hanoi (Viet Nam); Mikheenko, P. [School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Department of Physics, University of Oslo, P.O. Box 1048 Blindern, N-0316 Oslo (Norway)

2017-02-15

Highlights: • Power applications of YBCO films/coated conductors in technological relevant magnetic fields requires nano-engineered pinning centre. • Three approaches have been proposed: substrate decoration, quasi-multilayers, and targets with secondary phase nano-inclusions. • Combination of all three approaches greatly increased critical current in YBCO films. • Bulk pinning force, pinning potential, and critical current density are estimated and discussed in relation with the type and strength of pinning centres related to the defects evidenced by Transmission Electron Microscopy. - Abstract: For practical applications of superconducting materials in applied magnetic fields, artificial pinning centres in addition to natural ones are required to oppose the Lorentz force. These pinning centres are actually various types of defects in the superconductor matrix. The pinning centres can be categorised on their dimension (volume, surface or point) and on their character (normal cores or Δκ cores). Different samples have been produced by Pulsed Laser Deposition, with various thicknesses, temperatures and nanostructured additions to the superconducting matrix. They have been characterized by SQUID Magnetic Properties Measurement System and Physical Properties Measurement System, as well as by Transmission Electron Microscopy (TEM). Correlations between pinning architecture, TEM images, and critical currents at various fields and field orientations will be shown for a large number of YBa{sub 2}Cu{sub 3}O{sub x} films with various types and architectures of artificial pinning centres.

Local imaging of magnetic flux in superconducting thin films

Energy Technology Data Exchange (ETDEWEB)

Shapoval, Tetyana

2010-01-26

Local studies of magnetic flux line (vortex) distribution in superconducting thin films and their pinning by natural and artificial defects have been performed using low-temperature magnetic force microscopy (LT-MFM). Taken a 100 nm thin NbN film as an example, the depinning of vortices from natural defects under the influence of the force that the MFM tip exerts on the individual vortex was visualized and the local pinning force was estimated. The good agreement of these results with global transport measurements demonstrates that MFM is a powerful and reliable method to probe the local variation of the pinning landscape. Furthermore, it was demonstrated that the presence of an ordered array of 1-{mu}m-sized ferromagnetic permalloy dots being in a magneticvortex state underneath the Nb film significantly influences the natural pinning landscape of the superconductor leading to commensurate pinning effects. This strong pinning exceeds the repulsive interaction between the superconducting vortices and allows vortex clusters to be located at each dot. Additionally, for industrially applicable YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} thin films the main question discussed was the possibility of a direct correlation between vortices and artificial defects as well as vortex imaging on rough as-prepared thin films. Since the surface roughness (droplets, precipitates) causes a severe problem to the scanning MFM tip, a nanoscale wedge polishing technique that allows to overcome this problem was developed. Mounting the sample under a defined small angle results in a smooth surface and a monotonic thickness reduction of the film along the length of the sample. It provides a continuous insight from the film surface down to the substrate with surface sensitive scanning techniques. (orig.)

Two concepts of introducing thin-film superconductivity in Ge and Si by use of Ga-ion implantation

Energy Technology Data Exchange (ETDEWEB)

Skrotzki, Richard [Dresden High Magnetic Field Laboratory (HLD) and Institute of Ion Beam Physics and Materials Research, Helmholtz-Zentrum Dresden-Rossendorf (HZDR), Dresden (Germany); Department of Chemistry and Food Chemistry, TU Dresden (Germany); Herrmannsdoerfer, Thomas; Fiedler, Jan; Heera, Viton; Voelskow, Matthias; Muecklich, Arndt; Schmidt, Bernd; Skorupa, Wolfgang; Helm, Manfred; Wosnitza, Joachim [Dresden High Magnetic Field Laboratory (HLD) and Institute of Ion Beam Physics and Materials Research, Helmholtz-Zentrum Dresden-Rossendorf (HZDR), Dresden (Germany)

2012-07-01

We report on two unconventional routes of embedding superconducting nanolayers in a semiconducting environment. Ion implantation and subsequent annealing have been used for preparation of superconducting thin-films of Ga-doped germanium (Ge:Ga) as well as 10 nm thin amorphous Ga-rich layers in silicon (Si:Ga). Structural investigations by means of XTEM, EDX, RBS/C, and SIMS have been performed in addition to low-temperature electrical transport and magnetization measurements. Regarding Ge:Ga, we unravel the evolution of T{sub c} with charge-carrier concentration while for Si:Ga recently implemented microstructuring renders critical-current densities or more than 50 kA/cm{sup 2}. Combined with a superconducting onset at around 10 K, this calls for on-chip application in novel heterostructured devices.

RF Characterization of Niobium Films for Superconducting Cavities

CERN Document Server

Aull† , S; Doebert, S; Junginger, T; Ehiasarian, AP; Knobloch, J; Terenziani, G

2013-01-01

The surface resistance RS of superconductors shows a complex dependence on the external parameters such as temperature, frequency or radio-frequency (RF) field. The Quadrupole Resonator modes of 400, 800 and 1200 MHz allow measurements at actual operating frequencies of superconducting cavities. Niobium films on copper substrates have several advantages over bulk niobium cavities. HIPIMS (High-power impulse magnetron sputtering) is a promising technique to increase the quality and therefore the performance of niobium films. This contribution will introduce CERNs recently developed HIPIMS coating apparatus. Moreover, first results of niobium coated copper samples will be presented, revealing the dominant loss mechanisms.

Low-velocity superconducting accelerating structures

International Nuclear Information System (INIS)

Delayen, J.R.

1990-01-01

The present paper reviews the status of RF superconductivity as applied to low-velocity accelerating properties. Heavy-ion accelerators must accelerate efficiently particles which travel at a velocity much smaller than that of light particles, whose velocity changes along accelerator, and also different particles which have different velocity profiles. Heavy-ion superconducting accelerators operate at frequencies which are lower than high-energy superconducting accelerators. The present paper first discusses the basic features of heavy-ion superconducting structures and linacs. Design choices are then addressed focusing on structure geometry, materials, frequency, phase control, and focusing. The report also gives an outline of the status of superconducting booster projects currently under way at the Argonne National Laboratory, SUNY Stony Brook, Weizmann Institute, University of Washington, Florida State, Saclay, Kansas State, Daresbury, Japanese Atomic Energy Research Institute, Legnaro, Bombay, Sao Paulo, ANU (Canberra), and Munich. Recent developments and future prospects are also described. (N.K.) 68 refs

Lanthanum gallate substrates for epitaxial high-temperature superconducting thin films

Science.gov (United States)

Sandstrom, R. L.; Giess, E. A.; Gallagher, W. J.; Segmuller, A.; Cooper, E. I.

1988-11-01

It is demonstrated that lanthanum gallate (LaGaO3) has considerable potential as an electronic substrate material for high-temperature superconducting films. It provides a good lattice and thermal expansion match to YBa2Cu3O(7-x), can be grown in large crystal sizes, is compatible with high-temperature film processing, and has a reasonably low dielectric constant and low dielectric losses. Epitaxial YBa2Cu3O(7-x) films grown on LaGaO3 single-crystal substrates by three techniques have zero resistance between 87 and 91 K.

Micro-orientation control of silicon polymer thin films on graphite surfaces modified by heteroatom doping

Energy Technology Data Exchange (ETDEWEB)

Shimoyama, Iwao, E-mail: shimoyama.iwao@jaea.go.jp [Material Science Research Center, Atomic Energy Agency, Tokai-mura 2-4, Naka-gun, Ibaraki 319-1195 (Japan); Baba, Yuji [Fukushima Administrative Department, Atomic Energy Agency, Tokai-mura 2-4, Naka-gun, Ibaraki 319-1195 (Japan); Hirao, Norie [Material Science Research Center, Atomic Energy Agency, Tokai-mura 2-4, Naka-gun, Ibaraki 319-1195 (Japan)

2017-05-31

Highlights: • Micro-orientation control method for organic polysilane thin films is proposed. • This method utilizes surface modification of graphite using heteroatom doping. • Lying, standing, and random orientations can be freely controlled by this method. • Micro-pattering of a polysilane film with controlled orientations is achieved. - Abstract: Near-edge X-ray absorption fine structure (NEXAFS) spectroscopy is applied to study orientation structures of polydimethylsilane (PDMS) films deposited on heteroatom-doped graphite substrates prepared by ion beam doping. The Si K-edge NEXAFS spectra of PDMS show opposite trends of polarization dependence for non irradiated and N{sub 2}{sup +}-irradiated substrates, and show no polarization dependence for an Ar{sup +}-irradiated substrate. Based on a theoretical interpretation of the NEXAFS spectra via first-principles calculations, we clarify that PDMS films have lying, standing, and random orientations on the non irradiated, N{sub 2}{sup +}-irradiated, and Ar{sup +}-irradiated substrates, respectively. Furthermore, photoemission electron microscopy indicates that the orientation of a PDMS film can be controlled with microstructures on the order of μm by separating irradiated and non irradiated areas on the graphite surface. These results suggest that surface modification of graphite using ion beam doping is useful for micro-orientation control of organic thin films.

Superconducting thin films of Bi-Sr-Ca-Cu-O by laser ablation

Science.gov (United States)

Bedekar, M. M.; Safari, A.; Wilber, W.

1992-11-01

Superconducting thin films of Bi-Sr-Ca-Cu-O have been deposited by KrF excimer laser ablation. The best in situ films showed a Tc onset of 110 K and a Tc(0) of 76 K. A study of the laser plume revealed the presence of two distinct regimes. The forward directed component increased with fluence and the film composition was stoichiometric in this region. This is in agreement with the results on the 123 system by Venkatesan et al. [1]. The film properties were found to be critically dependent on the substrate temperature and temperatures close to melting gave rise to 2212 and 2223 phases. At lower temperatures, 2201 and amorphous phases were obtained. The film morphology and superconducting properties were a function of the target to substrate distance and the oxygen pressure during deposition and cooling. An increase in the target to substrate distance led to a deterioration of the properties due to the energy consideration for the formation of 2212 and 2223 phases. The best films were obtained using cooling pressures of 700 Torr. The microwave surface resistance of the films measured at 35 GHz dropped below that of copper at 30 K. Film growth was studied using X-ray diffraction and STM/AFM. This work is a discussion of the role of the different variables on the film properties.

Project in fiscal 1988 for research and development of basic technologies in next generation industries. Research and development of superconducting materials and superconducting elements (Achievement report on forecast and research of superconducting element technologies); 1988 nendo chodendo soshi gijutsu yosoku kenkyu seika hokokusho

Energy Technology Data Exchange (ETDEWEB)

NONE

1989-03-01

With an objective to perform survey and forecast on the future of superconducting elements, collection of latest technological information and analyses of technological trends were carried out by members of the Technology Forecast and Research Committee. This paper summarizes the achievements therein. It was discovered that the Josephson element using an Al{sub 2}O{sub 3} barrier and an Nb electrode shows excellent characteristics with very good reproducibility. Trial fabrication of a four-bit micro processor was recently executed successfully by the SQUID gate using the above element. On the other hand, application of devices using high-temperature superconductors has not come out with an achievement. Although a large number of achievements have been released on mono-crystalline thin films that show good characteristics, development of substrates and barrier materials is still needed for device configuration. The method for manufacturing metal-based superconducting films has been established nearly completely as an elementary technology to develop the superconducting elements. However, making thinner the high-temperature superconducting films having been discovered recently is encountering a number of inherent problems, whereas the present stage is such that experimental discussions are being made. The process technologies, simulation, and evaluation technologies are basically the same as those for the metallic systems even for the oxide superconduction. (NEDO)

Application and Prospect of Superconducting High Gradient Magnetic Separation in Disposal of Micro-fine Tailings

Science.gov (United States)

Yang, Changqiao; Li, Suqin; Guo, Zijie; Kong, Jiawei

2017-12-01

Magnetic separation technology is playing an increasingly important role in the field of environmental protection such as waste gas, waste water and solid waste treatment. As a new type of solid waste treatment technology, superconducting high gradient magnetic separation (HGMS) is mainly applied in the separation of micro-fine weakly magnetic particles because of the advantages of high separation efficiency, energy saving, simple equipment and easy automation. In this paper, the basic principle of superconducting HGMS was firstly introduced, then the research status of scholars at home and aboard on the disposal of micro-fine tailings were summarized. Finally, the direction of development for HGMS was put forward.

In-situ deposition of YBCO high-Tc superconducting thin films by MOCVD and PE-MOCVD

International Nuclear Information System (INIS)

Zhao, J.; Noh, D.W.; Chern, C.; Li, Y.Q.; Norris, P.E.; Kear, B.; Gallois, B.

1991-01-01

Metal-Organic Chemical Vapor Deposition (MOCVD) offers the advantages of a high degree of compositional control, adaptability for large scale production, and the potential for low temperature fabrication. The capability of operating at high oxygen partial pressure is particularly suitable for in situ formation of high temperature superconducting (HTSC) films. Yttrium barium copper oxide (YBCO) thin films having a sharp zero-resistance transition with T(sub c) greater than 90 K and J(sub c) of approximately 10(exp 4) A on YSZ have been prepared, in situ, at a substrate temperature of about 800 C. Moreover, the ability to form oxide films at low temperature is very desirable for device applications of HTSC materials. Such a process would permit the deposition of high quality HTSC films with a smooth surface on a variety of substrates. Highly c-axis oriented, dense, scratch resistant, superconducting YBCO thin films with mirror-like surfaces have been prepared, in situ, at a reduced substrate temperature as low as 570 C by a remote microwave-plasma enhanced metal-organic chemical vapor deposition (PE-MOCVD) process. Nitrous oxide was used as a reactant gas to generate active oxidizing species. This process, for the first time, allows the formation of YBCO thin films with the orthorhombic superconducting phase in the as-deposited state. The as-deposited films grown by PE-MOCVD show attainment of zero resistance at 72 K with a transition width of about 5 K. MOCVD was carried out in a commercial production scale reactor with the capability of uniform deposition over 100 sq cm per growth run. Preliminary results indicate that PE-MOCVD is a very attractive thin film deposition process for superconducting device technology

Nature of inhomogeneous states in superconducting junctions

International Nuclear Information System (INIS)

Ivlev, B.I.; Kopnin, N.B.

1982-01-01

A superconducting structure which arises in a superconducting film under a strong injection of a current through a tunnel junction is considered. If the current density in the film exceeds the critical Ginzburg-Landau value, an inhomogeneous resistive state with phase-slip centers can arise in it. This state is charcterized by the presence of regions with different chemical potentials of the Cooper pairs. These shifts of the pair chemical potential and the nonuniform structure of the order parameter may account for the so-called multigap states which have been observed experimentally

Plasma-enhanced chemical vapor deposition for YBCO film fabrication of superconducting fault-current limiter

Energy Technology Data Exchange (ETDEWEB)

Jun, Byung Hyuk; Kim, Chan Joong

2006-05-15

Since the high-temperature superconductor of oxide type was founded, many researches and efforts have been performed for finding its application field. The YBCO superconducting film fabricated on economic metal substrate with uniform critical current density is considered as superconducting fault-current limiter (SFCL). There are physical and chemical processes to fabricate superconductor film, and it is understood that the chemical methods are more economic to deposit large area. Among them, chemical vapor deposition (CVD) is a promising deposition method in obtaining film uniformity. To solve the problems due to the high deposition temperature of thermal CVD, plasma-enhanced chemical vapor deposition (PECVD) is suggested. This report describes the principle and fabrication trend of SFCL, example of YBCO film deposition by PECVD method, and principle of plasma deposition.

Effects of argon implantation and vacuum annealing of the superconducting properties of single-crystal niobium films

International Nuclear Information System (INIS)

Zakirov, R.M.; Kuznetsov, V.P.; Shermergor, T.D.

1980-01-01

Characteristics of superconducting transition (Tsub(K), Hsub(perpendicular)) of monocrystalline niobium films on sapphire, irradiated by 35 keV Ar ions within 0.62x10 15 -5.6x10 16 ion/cm 2 dose range, are investigated. Introduction of argon atoms results in Tsub(K) decrease of films and rhosub(n), Hsub(perpendicular 0) and dHsub(perpendicular)/dT increase due to reduction of free path length of electrons. Shown is an essential difference in the behaviour of superconducting parameters of irradiated monocrystalline niobium films and films with niobium, dassol ved in the niobium lattice. Introduction of oxygen has been carried out by annealing of films in vacuum after their heating in the air

Fabrication of high conductivity dual multi-porous poly (L-lactic acid)/polypyrrole composite micro/nanofiber film

International Nuclear Information System (INIS)

Yu Qiaozhen; Dai Zhengwei; Lan Ping

2011-01-01

Highlights: → PLLA/H 2 SO 4 -doped PPy composite micro/nano fibers dual multi-pore membranes with high conductivity were fabricated by combining electrospinning with in situ polymerization.These composite fibers have a core-shell structure, the PPy is the core and the PLLA/PPy is the shell. → The size and shape of the pores in this PPy composite fiber membrane can be tuned by polymerization parameters. The largest size of the pores is about 250 μm. → The conductivity of this composite fiber membrane can be adjusted by polymerization parameters. The highest conductivity is 179.0 S cm -1 . The PLLA fibers act as the template in the pyrrole polymerization process and contributed to the increase of the conductivity. - Abstract: Dual multi-porous PLLA (poly(L-lactic acid))/H 2 SO 4 -doped PPy (polypyrrole) composite micro/nano fiber films were fabricated by combining electrospinning with in situ polymerization. The morphologies and structures of the resulting samples were analyzed by scanning electron microscopy (SEM). It was found that the composite micro/nano fibers exhibited a core-shell structure and the composite fiber film had a dual multi-pore structure composed of pores both in the fibers and among the fibers. Semiconductor parameter analyzer was used to characterize the electrical properties of the samples. It was interesting to find that all the PLLA/H 2 SO 4 -doped PPy composite micro/nano fiber films had higher conductivity than H 2 SO 4 -doped PPy particles when the polymerization time up to 180 min. Effects of the pyrrole synthesis conditions on the pore size and the conductivity of PLLA/PPy composite fiber film were assessed. By optimizing the polymerization conditions, the max conductivity of this composite fiber film was about 179.0 S cm -1 with a pore size of about 250 μm. The possible mechanism of PLLA/H 2 SO 4 -doped PPy composite micro/nano fiber films had much higher conductivity than H 2 SO 4 -doped PPy particles was discussed.

Growth of YBCO superconducting thin films on CaF sub 2 buffered silicon

CERN Document Server

Bhagwat, S S; Patil, J M; Shirodkar, V S

2000-01-01

CaF sub 2 films were grown on silicon using the neutral cluster beam deposition technique. These films were highly crystalline and c-axis oriented. Superconducting YBCO thin films were grown on the Ca F sub 2 buffered silicon using the laser ablation technique. These films showed T sub c (onset) at 90 K and Tc(zero) at 86 K. X-ray diffraction analysis showed that the YBCO films were also oriented along the c-axis.

Project in fiscal 1989 for research and development of basic technologies in next generation industries. Research and development of superconducting materials and superconducting elements (Achievement report on forecast and research of superconducting element technology); 1990 nendo chodendo soshi gijutsu yosoku kenkyu seika hokokusho

Energy Technology Data Exchange (ETDEWEB)

NONE

1991-03-01

With an objective to forecast the ways the future superconducting elements and the related technologies should proceed, investigations and researches were performed on the progress in research and development of high-temperature superconducting elements, and the superconduction in a wide range. This paper summarizes the achievements in fiscal 1990. The high-temperature superconducting thin film technology has made remarkable advancement. The correlation of film forming conditions with characteristics of thin films was studied by using the sputtering process, laser deposition process and CVD process, having made production of thin films sufficiently applicable to electronics possible. A technology has been developed to suppress deterioration of characteristics for high-temperature conductors in thin film patterning, surface treatment and lamination structure fabrication. However, the problem of characteristics deterioration on interface of tri-terminal elements still remain unsolved. The bonded structure elements using high-temperature superconductors is the central technology in electronics application, but such problems exist as the coherence length being short, deterioration of characteristics at interfaces, and the electric characteristics being sensitive to crystalline orientation. Technological development to overcome these problems is under way. (NEDO)

The Goettingen high-Tc superconductivity research pool: the effects of structure and structural defects on the performance of high-Tc superconductors. Final reports

International Nuclear Information System (INIS)

1992-02-01

The compilation presents the final reports prepared by the various teams of the Goettingen research pool for high-Tc superconductivity. The reports are entitled: Structure and phase transition in high-Tc superconductors (Krebs/Freyhardt). Preparation and critical properties of high-Tc superconductors (Freyhardt/Heinemann/Zimmermann). EMC measurements in high-Tc superconductors (Bormann/Noelting). Phase analysis of the various phases observed in the preparation of high-Tc superconductors (Faupel/Hehenkamp). Positron annihilation in high-Tc superconductors (Hehenkamp). Preparation and characterization of thin films consisting of superconducting oxide ceramics (v. Minnigerode/Samwer). High-Tc superconductivity in monocrystals (Winzer/Beuermann). Microwave conductivity in high-Tc superconductors (Helberg). High-resolution structural analyses in high-Tc superconductors (Kupcik/Bente). Synthesis, structural analyses and spectroscopy of high-Tc superconductors (Bente). Synthesis, monocrystal growing, crystal structure of high-Tc superconductors (Schwarzmann). Ion-beam-aided studies in high-Tc superconductors (Uhrmacher). (orig./MM) [de

Lanthanum gallate substrates for epitaxial high-temperature superconducting thin films

International Nuclear Information System (INIS)

Sandstrom, R.L.; Giess, E.A.; Gallagher, W.J.; Segmueller, A.; Cooper, E.I.; Chisholm, M.F.; Gupta, A.; Shinde, S.; Laibowitz, R.B.

1988-01-01

We demonstrate that lanthanum gallate (LaGaO 3 ) has considerable potential as an electronic substrate material for high-temperature superconducting films. It provides a good lattice and thermal expansion match to YBa 2 Cu 3 O/sub 7-//sub x/, can be grown in large crystal sizes, is compatible with high-temperature film processing, and has a reasonably low dielectric constant (ε≅25) and low dielectric losses. Epitaxial YBa 2 Cu 3 O/sub 7-//sub x/ films grown on LaGaO 3 single-crystal substrates by three techniques have zero resistance between 87 and 91 K

Response of fractal penetration of magnetic flux to disorder landscape in superconducting films

Science.gov (United States)

Ye, Zuxin; Li, Qiang; Si, W. D.; Suenaga, M.; Solovyov, V. F.; Johnson, P. D.

2005-10-01

Magnetic flux front and induction contours in superconducting YBa2Cu3O7-δ films with defect size stilde ξ (superconducting coherence length) and s≫ξ are studied by magneto-optical imaging. Robust self-affine spatial correlation was observed using scaling analysis in the small pinning disorder-dominated ( stilde ξ) films. The roughness exponent α was determined to be ˜0.66 , independent of numbers of defects (or the film thickness). When the disorder landscape also included a distribution of large defects (s≫ξ) , the flux front and induction contours exhibited self-similarity, with a fractal dimension D determined to be ˜1.33 using the box-counting method. The remarkably different flux penetration patterns were shown to be the manifestation of self-organized criticality at different length scales.

Capability of Sputtered Micro-patterned NiTi Thick Films

Science.gov (United States)

Bechtold, Christoph; Lima de Miranda, Rodrigo; Quandt, Eckhard

2015-09-01

Today, most NiTi devices are manufactured by a combination of conventional metal fabrication steps, e.g., melting, extrusion, cold working, etc., and are subsequently structured by high accuracy laser cutting. This combination has been proven to be very successful; however, there are several limitations to this fabrication route, e.g., in respect to the fabrication of more complex device designs, device miniaturization or the combination of different materials for the integration of further functionality. These issues have to be addressed in order to develop new devices and applications. The fabrication of micro-patterned films using magnetron sputtering, UV lithography, and wet etching has great potential to overcome limitations of conventional device manufacturing. Due to its fabrication characteristics, this method allows the production of devices with complex designs, high structural accuracy, smooth edge profile, at layer thicknesses up to 75 µm. The aim of this study is to present recent developments in the field of NiTi thin film technology, its advantages and limitations, as well as new possible applications in the medical and in non-medical fields. These developments include among others NiTi scaffold structures covered with NiTi membranes for their potential use as filters, heart valve components or aneurysm treatments, as well as micro-actuators for consumable electronics or automotive applications.

Temperature dependence of the experimental penetration depth of superconducting thin films

International Nuclear Information System (INIS)

Fink, H.J.; Gruenfeld, V.; Pastawski, H.

1982-01-01

Experimental magnetic field penetration depths delta(t,d,H) of the stable and superheated Meissner state were calculated as a function of temperature for various applied magnetic fields and various film thicknesses for two cases: (1) lambda(t)/d<< kappa→infinity and (2) kappa< or approx. =2lambda(t)/d (lambda is the Ginzburg-Landau penetration depth, d is the film thickness, kappa is the GL parameter). The results of the first case should be a useful tool for obtaining lambda(0) of amorphous superconducting thin films

Selective Photophysical Modification on Light-Emitting Polymer Films for Micro- and Nano-Patterning

Directory of Open Access Journals (Sweden)

Xinping Zhang

2016-02-01

Full Text Available Laser-induced cross-linking in polymeric semiconductors was utilized to achieve micro- and nano-structuring in thin films. Single- and two-photon cross-linking processes led to the reduction in both the refractive index and thickness of the polymer films. The resultant photonic structures combine the features of both relief- and phase-gratings. Selective cross-linking in polymer blend films based on different optical response of different molecular phases enabled “solidification” of the phase-separation scheme, providing a stable template for further photonic structuring. Dielectric and metallic structures are demonstrated for the fabrication methods using cross-linking in polymer films. Selective cross-linking enables direct patterning into polymer films without introducing additional fabrication procedures or additional materials. The diffraction processes of the emission of the patterned polymeric semiconductors may provide enhanced output coupling for light-emitting diodes or distributed feedback for lasers.

Superconductivity in Na{sub 1-x}CoO{sub 2}.yH{sub 2}O thin films

Energy Technology Data Exchange (ETDEWEB)

Hildebrandt, Sandra; Komissinkiy, Philipp; Alff, Lambert [Institute for Materials Science, TU Darmstadt (Germany); Fritsch, Ingo; Habermeier, Hanns-Ulrich [Max-Planck-Institute for Solid State Research, Stuttgart (Germany); Lemmens, Peter [Institute for Condensed Matter Physics, TU Braunschweig (Germany)

2010-07-01

Sodium cobaltate (Na{sub 1-x}CoO{sub 2}) is a novel material with thermoelectric behavior, charge and spin ordered states dependent on the sodium content in the composition. A superconducting phase was found in water intercalated sodium cobaltate (Na{sub 1-x}CoO{sub 2}.yH{sub 2}O) with x=0.65-0.7 and y=0.9-1.3. The pairing state is still under debate, but there are some indications for a spin-triplet or p-wave superconducting pairing state. First films of Na{sub 1-x}CoO{sub 2}.yH{sub 2}O with a superconducting transition temperature near 5 K have been successfully grown. Here we report on thin films of Na{sub 1-x}CoO{sub 2} grown by pulsed laser deposition technique. The deposition parameters, sodium deintercalation and water intercalation conditions are tuned in order to obtain the superconducting phase. The instability of this phase might be an indication for triplet superconductivity, which is known to be affected strongly by impurities and defects.This observation is in agreement with the fact that so far also no superconducting thin films of the most famous triplet superconductor Sr{sub 2}RuO{sub 4} have been reported.

Study on effect of mean stress on fatigue life prediction of thin film structure

Energy Technology Data Exchange (ETDEWEB)

Shin, Myung Soo [Ahtti Co., Seongnam (Korea, Republic of); Park, Jun Hyu [Tongmyong University, Busan (Korea, Republic of); Kim, Jung Yup [Korea Institute of Machinery and Materials, Daejeon (Korea, Republic of)

2016-04-15

This paper describes the effect of mean stress on fatigue life prediction of structure made with thin film. It is well known that the mean stress influences fatigue life prediction of mechanical structure. We investigated a reasonable method for considering mean stress when fatigue strength assessment of micro structure of thin film should be performed. Fatigue tests of smooth specimen of beryllium-copper (BeCu) thin film were performed in ambient air at R = 0.1 with 5 Hz. A micro probe was designed and made with BeCu thin film by the precision press process. Fatigue tests of micro structure were performed with 5 Hz frequency, in ambient air to verify the fatigue life predicted by computer simulation through FE analysis. The fatigue life predicted by the Sa -N curve modified by Goodman method with principal stress through FE analysis shows a more reasonable result than other methods.

Study on effect of mean stress on fatigue life prediction of thin film structure

International Nuclear Information System (INIS)

Shin, Myung Soo; Park, Jun Hyu; Kim, Jung Yup

2016-01-01

This paper describes the effect of mean stress on fatigue life prediction of structure made with thin film. It is well known that the mean stress influences fatigue life prediction of mechanical structure. We investigated a reasonable method for considering mean stress when fatigue strength assessment of micro structure of thin film should be performed. Fatigue tests of smooth specimen of beryllium-copper (BeCu) thin film were performed in ambient air at R = 0.1 with 5 Hz. A micro probe was designed and made with BeCu thin film by the precision press process. Fatigue tests of micro structure were performed with 5 Hz frequency, in ambient air to verify the fatigue life predicted by computer simulation through FE analysis. The fatigue life predicted by the Sa -N curve modified by Goodman method with principal stress through FE analysis shows a more reasonable result than other methods

Vortex pinning vs superconducting wire network: origin of periodic oscillations induced by applied magnetic fields in superconducting films with arrays of nanomagnets

International Nuclear Information System (INIS)

Gomez, A; Del Valle, J; Gonzalez, E M; Vicent, J L; Chiliotte, C E; Carreira, S J; Bekeris, V; Prieto, J L; Schuller, Ivan K

2014-01-01

Hybrid magnetic arrays embedded in superconducting films are ideal systems to study the competition between different physical (such as the coherence length) and structural length scales such as are available in artificially produced structures. This interplay leads to oscillation in many magnetically dependent superconducting properties such as the critical currents, resistivity and magnetization. These effects are generally analyzed using two distinct models based on vortex pinning or wire network. In this work, we show that for magnetic dot arrays, as opposed to antidot (i.e. holes) arrays, vortex pinning is the main mechanism for field induced oscillations in resistance R(H), critical current I c (H), magnetization M(H) and ac-susceptibility χ ac (H) in a broad temperature range. Due to the coherence length divergence at T c , a crossover to wire network behaviour is experimentally found. While pinning occurs in a wide temperature range up to T c , wire network behaviour is only present in a very narrow temperature window close to T c . In this temperature interval, contributions from both mechanisms are operational but can be experimentally distinguished. (papers)

Probing the local microwave properties of superconducting thin films by a scanning microwave near-field microscope

CERN Document Server

Wu, L Y; Wang, K L; Jiang, T; Kang, L; Yang, S Z; Wu, P H

2002-01-01

In this paper, we present our approach to probe the local microwave properties of superconducting thin films by using the microwave near-field scanning technique. We have employed a coaxial cavity together with a niobium tip as the probe and established a scanning sample stage cooled by liquid nitrogen to study thin film devices at low temperature in our scanning microwave near-field microscope. Nondestructive images have been obtained on the inhomogeneity of the YBaCuO superconducting thin films at microwave frequency. We believe that these results would be helpful in evaluating the microwave performance of the devices.

The effects of Fe2O3 nanoparticles on MgB2 superconducting thin films

International Nuclear Information System (INIS)

Koparan, E.T.; Sidorenko, A.; Yanmaz, E.

2013-01-01

Full text: Since the discovery of superconductivity in binary MgB 2 compounds, extensive studies have been carried out because of its excellent properties for technological applications, such as high transition temperature (T c = 39 K), high upper critical field (H c2 ), high critical current density (J c ). Thin films are important for fundamental research as well as technological applications of any functional materials. Technological applications primarily depend on critical current density. The strong field dependence of J c for MgB 2 necessitates an enhancement in flux pinning performance in order to improve values in high magnetic fields. An effective way to improve the flux pinning is to introduce flux pinning centers into MgB 2 through a dopant having size comparable to the coherence length of MgB 2 . In this study, MgB 2 film with a thickness of about 600 nm was deposited on the MgO (100) single crystal substrate using a 'two-step' synthesis technique. Firstly, deposition of boron thin film was carried out by rf magnetron sputtering on MgO substrates and followed by a post deposition annealing at 850 degrees Celsius in magnesium vapour. In order to investigate the effect of Fe 2 O 3 nanoparticles on the structural and magnetic properties of films, MgB 2 films were coated with different concentrations of Fe 2 O 3 nanoparticles by a spin coating process. The effects of different concentrations of ferromagnetic Fe 2 O 3 nanoparticles on superconducting properties of obtained films were carried out by using structural (XRD, SEM, AFM), electrical (R-T) and magnetization (M-H, M-T and AC Susceptibility) measurements. It was calculated that anisotropic coefficient was about γ = 1.2 and coherence length of 5 nm for the uncoated film. As a result of coherence length, the appropriate diameters of Fe 2 O 3 nanoparticles were found to be 10 nm, indicating that these nanoparticles served as the pinning centers. Based on the data obtained from this study, it can be

Ion beam-based characterization of multicomponent oxide thin films and thin film layered structures

International Nuclear Information System (INIS)

Krauss, A.R.; Rangaswamy, M.; Lin, Yuping; Gruen, D.M.; Schultz, J.A.; Schmidt, H.K.; Chang, R.P.H.

1992-01-01

Fabrication of thin film layered structures of multi-component materials such as high temperature superconductors, ferroelectric and electro-optic materials, and alloy semiconductors, and the development of hybrid materials requires understanding of film growth and interface properties. For High Temperature Superconductors, the superconducting coherence length is extremely short (5--15 Angstrom), and fabrication of reliable devices will require control of film properties at extremely sharp interfaces; it will be necessary to verify the integrity of thin layers and layered structure devices over thicknesses comparable to the atomic layer spacing. Analytical techniques which probe the first 1--2 atomic layers are therefore necessary for in-situ characterization of relevant thin film growth processes. However, most surface-analytical techniques are sensitive to a region within 10--40 Angstrom of the surface and are physically incompatible with thin film deposition and are typically restricted to ultra high vacuum conditions. A review of ion beam-based analytical methods for the characterization of thin film and multi-layered thin film structures incorporating layers of multicomponent oxides is presented. Particular attention will be paid to the use of time-of-flight techniques based on the use of 1- 15 key ion beams which show potential for use as nondestructive, real-time, in-situ surface diagnostics for the growth of multicomponent metal and metal oxide thin films

Disorder and fluctuations in superconducting YBa2Cu3O6.9 films

International Nuclear Information System (INIS)

Gauzzi, A.

1993-01-01

We have developed the technique of ion-beam sputtering to grow thin (∼ 100 nm) superconducting YBa 2 Cu 3 O 6.9 (YBCO) films. We demonstrate that this technique is suitable for the in-situ deposition at low temperatures ( o C) of uniform films over large areas (≤30 cm 2 ). We found that preferential sputtering effects disappear if low-power ions-beams are used, thus enabling the control of the 1:2:3 composition by using a single stoichiometric target. We have found that the disorder in the crystal, introduced by too high or too low growth temperatures, affects strikingly both, the superconducting and the transport properties of the films. We report evidence that disorder on the atomic scale plays a role equivalent to oxygen doping. The similarity observed between the effects of crystal disorder in our films and the effects of oxygen depletion or Co-doping reported in the literature suggests that the disorder affects mainly the CuO chains. This implies that the local order of the chains controls not only the superconducting properties, as already established in the literature, but also the transport of the carriers in the normal state. Finally, we have investigated the local character of the superconducting state of YBCO by studying the paraconductivity in our films. We have found no indication of critical fluctuations at temperatures ≥5 mK above the zero-resistance critical temperature. Our analysis indicates that the spectrum of mean-field fluctuations is dominated by short-wavelength components and is affected by disorder. As a consequence, the temperature dependence of the critical exponents becomes complex and deviates from the universal predictions of conventional theories. We have explained quantitatively our experimental data and clarified the controversy existing in the literature by using a three-dimensional cut-off approach applied to the Lorentzian spectrum of the Ginzburg-Landau theory. (author) figs., tabs., refs

Two-dimensional superconductivity in ultrathin disordered thin films

International Nuclear Information System (INIS)

Beasley, M.R.

1992-01-01

The status of the understanding of two-dimensional superconductivity in ultrathin, disordered thin films is reviewed. The different consequences of microscopic versus macroscopic disorder are stressed. It is shown that microscopic disorder leads to a rapid suppression of the mean-field transition temperature. The consequences of macroscopic disorder are not well understood, but a universal behavior of the zero-bias resistance as a function of field and temperature has been observed. (orig.)

Micro/Nanostructured Films and Adhesives for Biomedical Applications.

Science.gov (United States)

Lee, Jungkyu K; Kang, Sung Min; Yang, Sung Ho; Cho, Woo Kyung

2015-12-01

The advanced technologies available for micro/nanofabrication have opened new avenues for interdisciplinary approaches to solve the unmet medical needs of regenerative medicine and biomedical devices. This review highlights the recent developments in micro/nanostructured adhesives and films for biomedical applications, including waterproof seals for wounds or surgery sites, drug delivery, sensing human body signals, and optical imaging of human tissues. We describe in detail the fabrication processes required to prepare the adhesives and films, such as tape-based adhesives, nanofilms, and flexible and stretchable film-based electronic devices. We also discuss their biomedical functions, performance in vitro and in vivo, and the future research needed to improve the current systems.

Commensurate vortex configurations in thin superconducting films nanostructured by square lattice of magnetic dots

Energy Technology Data Exchange (ETDEWEB)

Milosevic, M.V.; Peeters, F.M

2004-05-01

Within the phenomenological Ginzburg-Landau (GL) theory, we investigate the vortex structure of a thin superconducting film (SC) with a regular matrix of ferromagnetic dots (FD) deposited on top of it. The vortex pinning properties of such a magnetic lattice are studied, and the field polarity dependent votex pinning is observed. The exact vortex configuration depends on the size of the magnetic dots, their polarity, periodicity of the FD-rooster and the properties of the SC expressed through the effective Ginzburg-Landau parameter {kappa}*.

Commensurate vortex configurations in thin superconducting films nanostructured by square lattice of magnetic dots

International Nuclear Information System (INIS)

Milosevic, M.V.; Peeters, F.M.

2004-01-01

Within the phenomenological Ginzburg-Landau (GL) theory, we investigate the vortex structure of a thin superconducting film (SC) with a regular matrix of ferromagnetic dots (FD) deposited on top of it. The vortex pinning properties of such a magnetic lattice are studied, and the field polarity dependent votex pinning is observed. The exact vortex configuration depends on the size of the magnetic dots, their polarity, periodicity of the FD-rooster and the properties of the SC expressed through the effective Ginzburg-Landau parameter κ*

Nanoscale wedge polishing of superconducting thin films-an easy way to obtain depth dependent information by surface analysis techniques

International Nuclear Information System (INIS)

Shapoval, T; Engel, S; Gruendlich, M; Meier, D; Backen, E; Neu, V; Holzapfel, B; Schultz, L

2008-01-01

A mechanical wedge polishing procedure that offers a simple, cost-effective and rapid way to look into the depth of a thin film with different surface-sensitive scanning techniques has been developed. As an example of its wide applicability, this method was utilized for the investigation of two differently prepared superconducting YBa 2 Cu 3 O 7-δ thin films: an Hf-doped film prepared by chemical solution deposition and an undoped film grown by pulsed laser deposition. Upon polishing, the roughness of the samples was reduced to less than 5 nm (peak-to-valley) without influencing the superconducting properties of the films. Thus, nanoscale polishing opens up a unique possibility for microscopic studies with various surface-sensitive techniques. We demonstrate the successful imaging of flux lines by low temperature magnetic force microscopy after polishing a formerly rough as-prepared film. By applying the wedge polishing procedure to the Hf-doped sample, high resolution electron backscattering diffraction investigations reveal the homogeneous distribution of non-superconducting BaHfO 3 nanoparticles in the whole volume of the film

Magnetism in structures with ferromagnetic and superconducting layers

Energy Technology Data Exchange (ETDEWEB)

Zhaketov, V. D.; Nikitenko, Yu. V., E-mail: nikiten@nf.jinr.ru [Joint Institute for Nuclear Research (Russian Federation); Radu, F. [Helmholtz-Zentrum Berlin für Materialen un Energie (Germany); Petrenko, A. V. [Joint Institute for Nuclear Research (Russian Federation); Csik, A. [MTA Atomki, Institute for Nuclear Research (Hungary); Borisov, M. M.; Mukhamedzhanov, E. Kh. [Russian Research Centre Kurchatov Institute (Russian Federation); Aksenov, V. L. [Russian Research Centre Kurchatov Institute, Konstantinov St. Petersburg Nuclear Physics Institute (Russian Federation)

2017-01-15

The influence of superconductivity on ferromagnetism in the layered Ta/V/Fe{sub 1–x}V{sub x}/V/Fe{sub 1–x}V{sub x}/Nb/Si structures consisting of ferromagnetic and superconducting layers is studied using polarized neutron reflection and scattering. It is experimentally shown that magnetic structures with linear sizes from 5 nm to 30 μm are formed in these layered structures at low temperatures. The magnetization of the magnetic structures is suppressed by superconductivity at temperatures below the superconducting transition temperatures in the V and Nb layers. The magnetic states of the structures are shown to undergo relaxation over a wide magnetic-field range, which is caused by changes in the states of clusters, domains, and Abrikosov vortices.

Development of a micro-thermal flow sensor with thin-film thermocouples

Science.gov (United States)

Kim, Tae Hoon; Kim, Sung Jin

2006-11-01

A micro-thermal flow sensor is developed using thin-film thermocouples as temperature sensors. A micro-thermal flow sensor consists of a heater and thin-film thermocouples which are deposited on a quartz wafer using stainless steel masks. Thin-film thermocouples are made of standard K-type thermocouple materials. The mass flow rate is measured by detecting the temperature difference of the thin-film thermocouples located in the upstream and downstream sections relative to a heater. The performance of the micro-thermal flow sensor is experimentally evaluated. In addition, a numerical model is presented and verified by experimental results. The effects of mass flow rate, input power, and position of temperature sensors on the performance of the micro-thermal flow sensor are experimentally investigated. At low values, the mass flow rate varies linearly with the temperature difference. The linearity of the micro-thermal flow sensor is shown to be independent of the input power. Finally, the position of the temperature sensors is shown to affect both the sensitivity and the linearity of the micro-thermal flow sensor.

Preparation and characterization of high-Tc superconducting thin films with high critical current densities

International Nuclear Information System (INIS)

Vase, P.

1991-08-01

The project was carried out in relation to possible cable and electronics applications of high-T c materials. Laser ablation was used as the deposition technique because of its stoichiometry conservation. Films were made in the YBa 2 Cu 3 O 7 compound due to its relatively simple stoichiometry compared to other High-T c compounds. Much attention was paid to the critical current density. A very high critical current density was reached. By using texture analysis by X-ray diffraction, it was found that films with high critical current densities were epitaxial, while films with low critical current densities contained several crystalline orientations. Four techniques for patterning the films were used - photo lithography and wet etch, laser ablation lithography, laser writing and electron beam lithography and ion milling. Sub-micron patterning has been demonstrated without degradation of the superconducting properties. The achieved patterning resolution is sufficient for preparation of many superconducting components. (AB)

Application of High-Temperature Superconducting Thin-Film Devices to Electro-Optical and Electronic Warfare Systems

Science.gov (United States)

1990-02-01

superconducting dispersive (chirp) delay line. Bt currents (IB 1 and 1B 2) control states of write junctions (gates 1 and 2). (Counter) clockwise currents...Gavaler, and "S. A. Reihle, "Superconductive Convolver with June- A. I. Braginski, "Optical Response of Epitaxial Films tion Ring Nlixers," IELT Trans

Model of vortex dynamics in superconducting films in two-coil measurements of the coherence length

Science.gov (United States)

Lemberger, Thomas; Loh, Yen Lee

In two-coil measurements on superconducting films, a magnetic field from a small coil is applied to the center of the film. When the amplitude of the ac field is increased, the film undergoes a transition from the ``Meissner'' state to a state with vortices and antivortices. Ultimately, the vortex density matches the applied magnetic field and field screening is negligible. Experimentally, the field at the transition is related to the superconducting coherence length, although a full theory of the relationship is lacking. We show that the mutual inductance between drive and pickup coils, on opposite sides of the film, as a function of ac field amplitude is well-described by a phenomenological model in which vortices and antivortices appear together in the film at the radius where the induced supercurrent is strongest, and then they move through a landscape of moderately strong vortex pinning sites. Work at OSU supported by DOE-Basic Energy Sciences through Grant No. FG02-08ER46533.

Superconductivity and structure of gallium under nanoconfinement

Energy Technology Data Exchange (ETDEWEB)

Charnaya, E V; Tien, Cheng; Lee, Min Kai [Department of Physics, National Cheng Kung University, Tainan 70101, Taiwan (China); Kumzerov, Yu A [A F Ioffe Physico-Technical Institute RAS, St Petersburg, 194021 (Russian Federation)

2009-11-11

Superconductivity and crystalline structure were studied for two nanocomposites consisting of gallium loaded porous glasses with different pore sizes. The superconducting transition temperatures were found to differ from those in known bulk gallium modifications. The transition temperatures 7.1 and 6.7 K were ascribed to two new confined gallium structures, iota- and kappa-Ga, observed by synchrotron radiation x-ray powder diffraction. The evolution of superconductivity on decreasing the pore filling with gallium was also studied.

Compositional analysis of YBaCuO superconducting films with ion beam analysis techniques

International Nuclear Information System (INIS)

Jones, S.; Timmers, H.; Ophel, T.R.; Elliman, R.G.

1999-01-01

High-T c YBa x Cu y O 7-δ superconducting films are being developed for applications such as superconducting quantum interference devices. The carrier concentration, critical current density J c and critical temperature T c of these films depend sensitively on the oxygen content . Stoichiometry, uniformity with depth, homogeneity across the sample and film thickness are also important quantities for their characterisation. It has been shown, for example, that the stoichiometry of the metallic elements affects the growth characteristics and surface morphology of the films. With the deposit ion techniques used, reproducibility of film properties is difficult. The characterisation of YBa x Cu y O 7-δ films with ion beam analysis techniques is complex. Whereas the three metallic elements can be detected with helium beams and Rutherford Backscattering (RBS), the oxygen signal is generally obscured by that from substrate elements. It can be better detected using resonant backscattering with 3.04MeV 4 He ions or nuclear reaction analysis. Elastic Recoil Detection (ERD) with high-energetic (1MeV/amu), heavy beams (Z > 120), enables all elements to be detected and separated in a single experiment. It is well established that ion bombardment induces vacancies in the oxygen sub-lattice, driving the material to change from crystalline to amorphous, the latter phase having a reduced oxygen content. In previous heavy ion ERD measurements of YBa x Cu yO z films with 200MeV 127 I beams, the opaque films became transparent in the beam spot area, indicative of the amorphous phase. The accuracy of the oxygen measurement is therefore questionable. Indeed, using Raman spectroscopy, distortions of the crystalline structure above a fluence of 5 x 10 11 ion/cm 2 and for higher doses some signatures of a reduction in oxygen content have been observed for such beams. It appears therefore that a correct determination of the oxygen content requires either a drastic reduction in fluence or a

Magnetic force acting on a magnetic dipole over a superconducting thin film

International Nuclear Information System (INIS)

Wei, J.C.; Chen, J.L.; Horng, L.; Yang, T.J.

1996-01-01

The magnetostatic interaction energy and corresponding magnetic force acting on a magnetic point dipole placed above a type-II thin superconducting film in the mixed state with a single vortex are calculated using electromagnetics coupled with the London theory of superconductivity. If a vortex is trapped by a circular defect of radius b 1, where a is the separation between the dipole and the thin film, the only difference between two results is in the cutoff length, i.e., in the case of a circular defect the only difference in the critical position calculation is the cutoff at radius b rather than at coherence length ξ. The pinning force of a single vortex by a circular defect is also calculated. Further, we investigate the conditions of the vortex creation for various cases (including the first, second, and third vortices) for a free of pinning center in the examining region. It is found that the creation of a new single vortex in the thin film causes an abrupt change in vertical levitation force: the force changed discontinuously. copyright 1996 The American Physical Society

Molecular-Beam Epitaxially Grown MgB2 Thin Films and Superconducting Tunnel Junctions

Directory of Open Access Journals (Sweden)

Jean-Baptiste Laloë

2011-01-01

Full Text Available Since the discovery of its superconducting properties in 2001, magnesium diboride has generated terrific scientific and engineering research interest around the world. With a of 39 K and two superconducting gaps, MgB2 has great promise from the fundamental point of view, as well as immediate applications. Several techniques for thin film deposition and heterojunction formation have been established, each with its own advantages and drawbacks. Here, we will present a brief overview of research based on MgB2 thin films grown by molecular beam epitaxy coevaporation of Mg and B. The films are smooth and highly crystalline, and the technique allows for virtually any heterostructure to be formed, including all-MgB2 tunnel junctions. Such devices have been characterized, with both quasiparticle and Josephson tunneling reported. MgB2 remains a material of great potential for a multitude of further characterization and exploration research projects and applications.

Electron scattering rate in epitaxial YBa2Cu3O7 superconducting films

Science.gov (United States)

Flik, M. I.; Zhang, Z. M.; Goodson, K. E.; Siegal, M. P.; Phillips, Julia M.

1992-09-01

This work determines the electron scattering rate in the a-b plane of epitaxial YBa2Cu3O7 films using two techniques. Infrared spectroscopy yields the scattering rate at temperatures of 10, 78, and 300 K by fitting reflectance data using thin-film optics and a model for the free-carrier conductivity. The scattering rate is also obtained using kinetic theory and an extrapolation of normal-state electrical resistivity data to superconducting temperatures based on the Bloch theory for the phonon-limited electrical resistivity of metals. The scattering rates determined using both techniques are in agreement and show that the electron mean free path in the a-b plane of YBa2Cu3O7 superconducting films is three to four times the coherence length. Hence YBa2Cu3O7 is pure but not in the extreme pure limit. An average defect interaction range of 4 nm is obtained using the defect density resulting from flux-pinning considerations.

Superconductivity effects near metal-insulator transition in granular idnium films

International Nuclear Information System (INIS)

Belevtsev, B.I.; Komnik, Yu.F.; Fomin, A.V.

1986-01-01

The influence of granules superconductivity on the electric properties of granular indium films is investigated under the conditions of partial or full granular localization of electrons. At temperatures below 5 K a minimum of electric resistance and negative magnetoresistance are revealed which are attributed to the competition of hopping conductivity and Josephson intergranular tunneling of electrons

The growth of large-area superconducting YBa2Cu3O7-x thin films by pulsed laser ablation

International Nuclear Information System (INIS)

Lai, H.C.; Chang, C.M.; Lin, R.J.; Liu, R.S.

1996-01-01

In-situ growth of 2-in. diameter superconducting YBa 2 Cu 3 O 7-x (YBCO) thin films using an excimer KrF pulsed laser has been studied. Films with critical transition temperature (T c,0 ) of 89±1 K and critical current density (J c,77K ) in excess of 1 x 10 6 A cm -2 have been prepared routinely. Uniformity in film thickness of below ±15% and film composition of ±5% have been measured. The effects of gas nozzle geometry and target evolution during ablation on the superconducting properties and surface morphology of YBCO thin films have also been investigated. (orig.)

Measurement of the magnetic penetration depth in p-doped superconducting diamond films

Energy Technology Data Exchange (ETDEWEB)

Fuchs, Lorenz; Brunner, Markus C.P.; Schneider, Ina; Kronfeldner, Klaus [University of Regensburg (Germany); Bousquet, Jessica; Bustarret, Etienne; Strunk, Christoph [Institut Neel, Grenoble (France)

2016-07-01

Boron-doped diamond becomes superconducting once a critical doping concentration of 4.5 x 10{sup 20} cm{sup -3} is reached. Mutual inductance measurements with a two-coil setup have been performed to determine the magnetic penetration depth λ(T), which is a measure for the superfluid stiffnes θ ∝ 1/λ{sup 2}(T). Two superconducting p-doped diamond films with thicknesses of 145 nm and 345 nm were investigated. At low temperatures these values agree reasonably with the values expected within BCS-theory using T{sub c}, carrier density and mean free path determined from electric transport measurements. Magnetic penetration depths of 3.7 μm for the thinner and 2.6 μm for the thicker film have been found. λ decreases and accordingly θ increases with increasing film thickness. On the other hand, the superfluid stiffness drops by a factor of 2 or even more at T{sub c}/2, i.e., much faster than expected from BCS-theory, but remains finite between T{sub c}/2 < T < T{sub c}. At present it is unclear, whether this behavior results from the proliferation of phase fluctuations already far below T{sub c} or from a spatial inhomogeneity of the films.

Superconducting thin films of YBa2Cu3O7-x

International Nuclear Information System (INIS)

Hudner, J.

1993-01-01

Thin films of the high temperature superconductor YBa 2 Cu 3 O 7-x (YBCO) are of significance in fundamental studies of oxide superconductors and for prospected electronic applications based on superconductors operating at liquid nitrogen temperatures (T= 77 K). Synthesis of YBCO thin films is complex and a large part of this thesis has been devoted to the elaboration of various techniques in forming YBCO thin films. A general observation was that synthesis of YBCO films exhibiting high zero-resistivity temperatures temperatures (T c ) ≥ 88 K and elevated critical current densities (J c ) ≥ 10 6 A/cm 2 at 77 K was possible under widely different conditions of film growth. For the BaF 2 -based method, various substrate materials were investigated. Among perovskite related substrates with low losses in the high frequency regime, LaA10 3 was found to yield YBCO films exhibiting the highest quality electrical properties. A study of YBCO film interaction with sapphire substrates was performed. It was suggested that the YBCO film on sapphire consists of weakly coupled superconducting grains. Compositional effects of Y, BA and Cu for MOCVD-YBCO films were examined with respect to morphology, structure, resistivity, as susceptibility and J c (T). High T c :s and J c :s were observed for an anomalous large compositional range of Cu in off-compositional YBCO films. This was shown to be related to the formation of Cu-rich precipitates embedded within a c-Axis oriented stoichiometric YBCO film matrix. Thermal critical current behavior at zero field in thin films of YBCO fabricated by various methods has been studied by three techniques: transport measurements on patterned microbridges, dc magnetization hysteresis loops using the Bean model and non-linear ac susceptibility analysis. Absolute critical current values obtained form the two former techniques when measured on the same YBCO film were observed to differ about a factor of two. The feasibility of non-linear ac

Y1Ba2Cu3O(7-delta) thin film dc SQUIDs (superconducting quantum interference device)

Science.gov (United States)

Racah, Daniel

1991-03-01

Direct current superconducting quantum interferometers (SQUIDs) based on HTSC thin films have been measured and characterized. The thin films used were of different quality: (1) Granular films on Sapphire substrates, prepared either by e-gun evaporation, by laser ablation or by MOCVD (metal oxide chemical vapor deposition), (2) Epitaxial films on MgO substrates. Modulations of the voltage on the SQUIDs as a function of the applied flux have been observed in a wide range of temperatures. The nature of the modulation was found to be strongly dependent on the morphology of the film and on its critical current. The SQUIDs based on granular films were relatively noisy, hysteretic and with a complicated V-phi shape. Those devices based on low quality (lowIc) granular films could be measured only at low temperatures (much lower than 77 K). While those of higher quality (granular films with high Ic) could be measured near to the superconductive transition. The SQUID based on high quality epitaxial film was measured near Tc and showed an anomalous, time dependent behavior.

Synthesis of biphasic calcium phosphate containing nanostructured films by micro arc oxidation on magnesium alloy

Energy Technology Data Exchange (ETDEWEB)

Seyfoori, A., E-mail: klm.1985@yahoo.com [School of Metallurgy and Materials Engineering, Iran University of Science and Technology, 16846-13114 Tehran (Iran, Islamic Republic of); National Cell Bank, Pasteur Institute of Iran, 13164 Tehran (Iran, Islamic Republic of); Mirdamadi, Sh.; Seyedraoufi, Z.S.; Khavandi, A. [School of Metallurgy and Materials Engineering, Iran University of Science and Technology, 16846-13114 Tehran (Iran, Islamic Republic of); Aliofkhazraei, M. [Department of Materials Engineering, Faculty of Engineering, Tarbiat Modares University, 14115-143 Tehran (Iran, Islamic Republic of)

2013-10-01

The present research reports the synthesis of an innovative nanostructured composite film containing biphasic calcium phosphate (BCP) by the micro arc oxidation (MAO) method on AZ31 magnesium alloy. Nanometric structure of the used hydroxyapatite powder and the coatings were characterized by means of transmission and field-emission scanning electron microscope, respectively. Electrochemical behaviors of the pure MAO and nanocomposite films were also evaluated by electrochemical impedance spectroscopy and potentiodynamic polarization tests in simulated body fluid (SBF) environment. The results showed higher corrosion resistance of nanocomposite film compared to pure MAO coating, which was related to the blocking feature of the nanoparticles from the diffusing of the corrosive medium through the substrate. In addition, by immersing the specimens in simulated body fluid, greater apatite forming ability of the nanocomposite coating was proved. - Highlights: • Synthesis of innovative biphasic calcium phosphate containing nanostructured films via micro arc oxidation. • Nanocomposite film has lower degradation rate than pure MAO film. • Greater apatite forming ability for nanocomposite coating compared with pure MAO film is obtained.

Synthesis of biphasic calcium phosphate containing nanostructured films by micro arc oxidation on magnesium alloy

International Nuclear Information System (INIS)

Seyfoori, A.; Mirdamadi, Sh.; Seyedraoufi, Z.S.; Khavandi, A.; Aliofkhazraei, M.

2013-01-01

The present research reports the synthesis of an innovative nanostructured composite film containing biphasic calcium phosphate (BCP) by the micro arc oxidation (MAO) method on AZ31 magnesium alloy. Nanometric structure of the used hydroxyapatite powder and the coatings were characterized by means of transmission and field-emission scanning electron microscope, respectively. Electrochemical behaviors of the pure MAO and nanocomposite films were also evaluated by electrochemical impedance spectroscopy and potentiodynamic polarization tests in simulated body fluid (SBF) environment. The results showed higher corrosion resistance of nanocomposite film compared to pure MAO coating, which was related to the blocking feature of the nanoparticles from the diffusing of the corrosive medium through the substrate. In addition, by immersing the specimens in simulated body fluid, greater apatite forming ability of the nanocomposite coating was proved. - Highlights: • Synthesis of innovative biphasic calcium phosphate containing nanostructured films via micro arc oxidation. • Nanocomposite film has lower degradation rate than pure MAO film. • Greater apatite forming ability for nanocomposite coating compared with pure MAO film is obtained

Resonant coupling applied to superconducting accelerator structures

International Nuclear Information System (INIS)

Potter, James M.; Krawczyk, Frank L.

2013-01-01

The concept of resonant coupling and the benefits that accrue from its application is well known in the world of room temperature coupled cavity linacs. Design studies show that it can be applied successfully between sections of conventional elliptical superconducting coupled cavity accelerator structures and internally to structures with spoked cavity resonators. The coupling mechanisms can be designed without creating problems with high field regions or multipactoring. The application of resonant coupling to superconducting accelerators eliminates the need for complex cryogenic mechanical tuners and reduces the time needed to bring a superconducting accelerator into operation.

Electrical current at micro-/macro-scale of undoped and nitrogen-doped MWPECVD diamond films

Science.gov (United States)

Cicala, G.; Velardi, L.; Senesi, G. S.; Picca, R. A.; Cioffi, N.

2017-12-01

Chemical, structural, morphological and micro-/macro-electrical properties of undoped and nitrogen-(N-)doped diamond films are determined by X-ray photoelectron spectroscopy, Raman and photoluminescence spectroscopies, field emission scanning electron microscopy, atomic force microscopy, scanning capacitance microscopy (SCM) and two points technique for I-V characteristics, respectively. The characterization results are very useful to examine and understand the relationship among these properties. The effect of the nitrogen incorporation in diamond films is investigated through the evolution of the chemical, structural, morphological and topographical features and of the electrical behavior. The distribution of the electrical current is first assessed at millimeter scale on the surface of diamond films and then at micrometer scale on small regions in order to establish the sites where the carriers preferentially move. Specifically, the SCM images indicate a non-uniform distribution of carriers on the morphological structures mainly located along the grain boundaries. A good agreement is found by comparing the electrical currents at the micro- and macro-scale. This work aims to highlight phenomena such as photo- and thermionic emission from N-doped diamond useful for microelectronic engineering.

Transport in reversibly laser-modified YBa2Cu3O/sub 7-//sub x/ superconducting thin films

International Nuclear Information System (INIS)

Krchnavek, R.R.; Chan, S.; Rogers, C.T.; De Rosa, F.; Kelly, M.K.; Miceli, P.F.; Allen, S.J.

1989-01-01

A focused argon ion laser beam in a controlled ambient is used to modify the transport properties of superconducting YBa 2 Cu 3 O/sub 7-//sub x/ thin films. The laser-modified region shows a sharp transition temperature (T/sub c/≅76 K) that is reduced from the unmodified regions of the film (T/sub c/≅87 K). In situ monitoring of the room-temperature electrical resistance is used to control the laser processing and prevent formation of the semiconducting phase. The original properties of the superconducting film can be recovered by plasma oxidation indicating that the laser-induced phase is oxygen deficient

Supramolecular structure of a perylene derivative in thin films deposited by physical vapor deposition

International Nuclear Information System (INIS)

Fernandes, Jose D.; Aoki, Pedro H.B.; Constantino, Carlos J.J.; Junior, Wagner D.M.; Teixeira, Silvio R.

2014-01-01

Full text: Thin films of a perylene derivative, the bis butylimido perylene (BuPTCD), were produced using thermal evaporation (PVD, physical vapor deposition). The main objective is to investigate the supramolecular structure of the BuPTCD in these PVD films, which implies to control the thickness and to determine the molecular organization, morphology at micro and nanometer scales and crystallinity. This supramolecular structure is a key factor in the optical and electrical properties of the film. The ultraviolet-visible absorption revealed an uniform growth of the PVD films. The optical and atomic force microscopy images showed a homogeneous surface of the film at micro and nanometer scales. A preferential orientation of the molecules in the PVD films was determined via infrared absorption. The X-ray diffraction showed that both powder and PVD film are in the crystalline form. (author)

Composite vortex ordering in superconducting films with arrays of blind holes

International Nuclear Information System (INIS)

Berdiyorov, G R; Milosevic, M V; Peeters, F M

2009-01-01

The pinning properties of a superconducting thin film with a square array of blind holes are studied using the nonlinear Ginzburg-Landau theory. Although blind holes provide a weaker pinning potential than holes (also called antidots), several novel vortex structures are predicted for different size and thickness of the blind holes. Orientational dimer and trimer vortex states as well as concentric vortex shells can nucleate in the blind holes. In addition, we predict the stabilization of giant vortices that may be located both in the pinning centers and/or at the interstitial sites, as well as the combination of giant vortices with sets of individual vortices. For large blind holes, local vortex shell structures inside the blind holes may transfer their symmetry to interstitial vortices as well. The subtle interplay of shell formation and traditional Abrikosov vortex lattices inside the blind holes is also studied for different numbers of trapped vortices.

Multi-cell superconducting structures for high energy e+ e- colliders and free electron laser linacs

CERN Document Server

Sekutowicz, J

2008-01-01

This volume, which is the first in the EuCARD Editorial Series on “Accelerator Science and Technology”, is closely combined with the most advanced particle accelerators – based on Superconducting Radio Frequency (SRF) technology. In general, SRF research includes following areas: high gradient cavities, cavity prototyping, thin film technologies, large grain and mono-crystalline niobium and niobium alloys, quenching effects in superconducting cavities, SRF injectors, photo-cathodes, beam dynamics, quality of electron beams, cryogenics, high power RF sources, low level RF controls, tuners, RF power coupling to cavities, RF test infrastructures, etc. The monograph focuses on TESLA structures used in FLASH machine and planned for XFEL and ILC experiments.

A study on the superconducting properties of YBa2Cu9-xNbxOy thin films

International Nuclear Information System (INIS)

Srinivas, S.; Bhatnagar, A.K.; Pinto, R.

1994-01-01

Effect of niobium substitution at the copper site in YBa 2 Cu 9 O 7-x was studied in thin film form. The films were deposited by laser ablation technique using the targets of the YBa 2 Cu 3-x Nb x O y where x = 0.0, 0.025, 0.05, 0.1, 0.2, 0.4, 0.8 and 1.0 under identical deposition conditions on SrTiO 9 substrates. Films were characterized by XRD, resistivity, I-V and J c measurements. Films made from x = 0.025 and 0.05 concentrations of Nb substituted targets showed relatively improved superconducting properties compared to that of undoped films. The best 7 realized for x = 0.025 Nb concentration was 1.8 x 10 σ A/cm 2 and for 0.05 Nb concentration it was 3.2x10 σ A/cm 2 at 77K. However, degradation of the superconducting properties, with the increase of x ≥ 0.1 Nb concentration and drastic suppression and complete loss of superconductivity was noticed for x ≥ 0.4. The growth of impurity phase YBa 2 NbO 6 for x = 0.1 and above of Nb concentration was noticed from XRD patterns. However, the site occupancy of Nb could not be confirmed from these studies

Growth and applications of superconducting Y-Ba-Cu-O thin films

International Nuclear Information System (INIS)

Pinto, R.

1991-01-01

This paper attempt to highlight the important PVD techniques such as evaporation, sputtering, ion beam deposition and excimer laser ablation for the preparation of superconducting YBaCuO thin films. Since enormous amount of work has been published over the last few years, this review is not comprehensive even in PVD techniques. In the area of applications for electronics, thin film appear to be much more promising than bulk high T c superconductors. Already high J c values in the region of 4 x 10 6 A cm -2 have been realized in thin films. Resonators and transmission lines have been fabricated using 123 films showing a transmission loss significantly lower than that of copper at 77 degrees K at X-band frequencies. This review will discuss some of the important electronic applications feasible with 123 films

Assessment of micro-superconducting magnetic energy storage (SMES) utility in railroad applications : a report to Congress

Science.gov (United States)

1997-07-01

At the direction of the U.S. Congress, the Federal Railroad Administration (FRA), with technical support from the Volpe National Transportation Systems Center (Volpe Center), investigated the feasibility of using micro-Superconducting Magnetic Energy...

Superconducting properties of iron chalcogenide thin films

Directory of Open Access Journals (Sweden)

Paolo Mele

2012-01-01

Full Text Available Iron chalcogenides, binary FeSe, FeTe and ternary FeTexSe1−x, FeTexS1−x and FeTe:Ox, are the simplest compounds amongst the recently discovered iron-based superconductors. Thin films of iron chalcogenides present many attractive features that are covered in this review, such as: (i easy fabrication and epitaxial growth on common single-crystal substrates; (ii strong enhancement of superconducting transition temperature with respect to the bulk parent compounds (in FeTe0.5Se0.5, zero-resistance transition temperature Tc0bulk = 13.5 K, but Tc0film = 19 K on LaAlO3 substrate; (iii high critical current density (Jc ~ 0.5 ×106 A cm2 at 4.2 K and 0 T for FeTe0.5Se0.5 film deposited on CaF2, and similar values on flexible metallic substrates (Hastelloy tapes buffered by ion-beam assisted deposition with a weak dependence on magnetic field; (iv high upper critical field (~50 T for FeTe0.5Se0.5, Bc2(0, with a low anisotropy, γ ~ 2. These highlights explain why thin films of iron chalcogenides have been widely studied in recent years and are considered as promising materials for applications requiring high magnetic fields (20–50 T and low temperatures (2–10 K.

Imaging the electron-boson coupling in superconducting FeSe films using a scanning tunneling microscope.

Science.gov (United States)

Song, Can-Li; Wang, Yi-Lin; Jiang, Ye-Ping; Li, Zhi; Wang, Lili; He, Ke; Chen, Xi; Hoffman, Jennifer E; Ma, Xu-Cun; Xue, Qi-Kun

2014-02-07

Scanning tunneling spectroscopy has been used to reveal signatures of a bosonic mode in the local quasiparticle density of states of superconducting FeSe films. The mode appears below Tc as a "dip-hump" feature at energy Ω∼4.7kBTc beyond the superconducting gap Δ. Spectra on strained regions of the FeSe films reveal simultaneous decreases in Δ and Ω. This contrasts with all previous reports on other high-Tc superconductors, where Δ locally anticorrelates with Ω. A local strong coupling model is found to reconcile the discrepancy well, and to provide a unified picture of the electron-boson coupling in unconventional superconductors.

Structure of catalase determined by MicroED

Science.gov (United States)

Nannenga, Brent L; Shi, Dan; Hattne, Johan; Reyes, Francis E; Gonen, Tamir

2014-01-01

MicroED is a recently developed method that uses electron diffraction for structure determination from very small three-dimensional crystals of biological material. Previously we used a series of still diffraction patterns to determine the structure of lysozyme at 2.9 Å resolution with MicroED (Shi et al., 2013). Here we present the structure of bovine liver catalase determined from a single crystal at 3.2 Å resolution by MicroED. The data were collected by continuous rotation of the sample under constant exposure and were processed and refined using standard programs for X-ray crystallography. The ability of MicroED to determine the structure of bovine liver catalase, a protein that has long resisted atomic analysis by traditional electron crystallography, demonstrates the potential of this method for structure determination. DOI: http://dx.doi.org/10.7554/eLife.03600.001 PMID:25303172

Superconductivity in volumetric and film ceramics Bi-Sr-Ca-Cu-O

International Nuclear Information System (INIS)

Sukhanov, A.A.; Ozmanyan, Kh.R.; Sandomirskij, B.B.

1988-01-01

A superconducting transition with T c0 =82-95 K and T c (R=0)=82-72 K was observed in volumetric and film Bi(Sr 1-x Ca x ) 2 Cu 3 O y samples obtained by solid-phase reaction. Temperature dependences of resistance critical current and magnetic susceptibility are measured

Superconductivity in Bi-Sr-Ca-Cu-O bulk and film ceramics

Energy Technology Data Exchange (ETDEWEB)

Sukhanov, A A; Ozmanian, KH R; Sandomirskii, B B

1988-07-01

A superconducting transition with Tc0 = 82-95 K and Tc(R = 0) = 82-72 K was observed in Bi(Sr/1-x/Ca/x/)2Cu3O(y) bulk and film specimens obtained via a solid-phase reaction. Temperature dependences of the resistance, critical current, and magnetic susceptibility were measured.

Collective-pinning properties of superconducting a-NbxGe and a-MoxSi films

International Nuclear Information System (INIS)

Woerdenweber, R.

1987-01-01

This thesis describes a study of superconducting flux pinning in amorphous NbGe and MoSi films of various compositions and thickness. Amorphous NbGe and MoSi alloys belong to the weak-coupling type-II superconductors in the extreme dirty limit. This feature enables to determine several important superconducting parameters from well-known theoretical expressions. It is also responsible for the weak pinning, which is necessary to observe the two-dimensional collective pinning properties according to the Larkin-Ovchinnikov theory. (Auth.)

Femtosecond laser micro-machined polyimide films for cell scaffold applications

DEFF Research Database (Denmark)

Antanavičiute, Ieva; Šimatonis, Linas; Ulčinas, Orestas

2018-01-01

of commercially available 12.7 and 25.4μm thickness polyimide (PI) film was applied. Mechanical properties of the fabricated scaffolds, i.e. arrays of differently spaced holes, were examined via custom-built uniaxial micro-tensile testing and finite element method simulations. We demonstrate that experimental...... micro-tensile testing results could be numerically simulated and explained by two-material model, assuming that 2-6μm width rings around the holes possessed up to five times higher Young's modulus and yield stress compared with the rest of the laser intacted PI film areas of 'dog-bone'-shaped specimens......Engineering of sophisticated synthetic 3D scaffolds that allow controlling behaviour and location of the cells requires advanced micro/nano-fabrication techniques. Ultrafast laser micro-machining employing a 1030-nm wavelength Yb:KGW femtosecond laser and a micro-fabrication workstation for micro-machining...

Influence of reversible epitactical stress on the electronic properties of thin superconducting films

International Nuclear Information System (INIS)

Trommler, Sascha

2014-01-01

In this thesis new stress techniques are applied on thin superconducting (La,Sr) 2 CuO 4 and BaFe 1.8 Co 0.2 As 2 films. At one hand piezoelectric substrates are applied, which make a biaxial stress of the thin film deposed there possible, whereby the lattice parameters of the substrate are altered by an electric field. At the other hand on the base of flexible substrates by means of a bending experiment a uniaxial lattice deformation of thin film is realized.

Wireless thin film transistor based on micro magnetic induction coupling antenna.

Science.gov (United States)

Jun, Byoung Ok; Lee, Gwang Jun; Kang, Jong Gu; Kim, Seunguk; Choi, Ji-Woong; Cha, Seung Nam; Sohn, Jung Inn; Jang, Jae Eun

2015-12-22

A wireless thin film transistor (TFT) structure in which a source/drain or a gate is connected directly to a micro antenna to receive or transmit signals or power can be an important building block, acting as an electrical switch, a rectifier or an amplifier, for various electronics as well as microelectronics, since it allows simple connection with other devices, unlike conventional wire connections. An amorphous indium gallium zinc oxide (α-IGZO) TFT with magnetic antenna structure was fabricated and studied for this purpose. To enhance the induction coupling efficiency while maintaining the same small antenna size, a magnetic core structure consisting of Ni and nanowires was formed under the antenna. With the micro-antenna connected to a source/drain or a gate of the TFT, working electrical signals were well controlled. The results demonstrated the device as an alternative solution to existing wire connections which cause a number of problems in various fields such as flexible/wearable devices, body implanted devices, micro/nano robots, and sensors for the 'internet of things' (IoT).

Wireless thin film transistor based on micro magnetic induction coupling antenna

Science.gov (United States)

Jun, Byoung Ok; Lee, Gwang Jun; Kang, Jong Gu; Kim, Seunguk; Choi, Ji-Woong; Cha, Seung Nam; Sohn, Jung Inn; Jang, Jae Eun

2015-12-01

A wireless thin film transistor (TFT) structure in which a source/drain or a gate is connected directly to a micro antenna to receive or transmit signals or power can be an important building block, acting as an electrical switch, a rectifier or an amplifier, for various electronics as well as microelectronics, since it allows simple connection with other devices, unlike conventional wire connections. An amorphous indium gallium zinc oxide (α-IGZO) TFT with magnetic antenna structure was fabricated and studied for this purpose. To enhance the induction coupling efficiency while maintaining the same small antenna size, a magnetic core structure consisting of Ni and nanowires was formed under the antenna. With the micro-antenna connected to a source/drain or a gate of the TFT, working electrical signals were well controlled. The results demonstrated the device as an alternative solution to existing wire connections which cause a number of problems in various fields such as flexible/wearable devices, body implanted devices, micro/nano robots, and sensors for the ‘internet of things’ (IoT).

Quasi-One-Dimensional Intermittent Flux Behavior in Superconducting Films

Directory of Open Access Journals (Sweden)

A. J. Qviller

2012-01-01

Full Text Available Intermittent filamentary dynamics of the vortex matter in superconductors is found in films of YBa_{2}Cu_{3}O_{7-δ} deposited on tilted substrates. Deposition of this material on such substrates creates parallel channels of easy flux penetration when a magnetic field is applied perpendicular to the film. As the applied field is gradually increased, magneto-optical imaging reveals that flux penetrates via numerous quasi-one-dimensional jumps. The distribution of flux avalanche sizes follows a power law, and data collapse is obtained by finite-size scaling, with the depth of the flux front used as crossover length. The intermittent behavior shows no threshold value in the applied field, in contrast to conventional flux jumping. The results strongly suggest that the quasi-one-dimensional flux jumps are of a different nature than the thermomagnetic dendritic (branching avalanches that are commonly found in superconducting films.

Monolithic Carbide-Derived Carbon Films for Micro-Supercapacitors

Science.gov (United States)

Chmiola, John; Largeot, Celine; Taberna, Pierre-Louis; Simon, Patrice; Gogotsi, Yury

2010-04-01

Microbatteries with dimensions of tens to hundreds of micrometers that are produced by common microfabrication techniques are poised to provide integration of power sources onto electronic devices, but they still suffer from poor cycle lifetime, as well as power and temperature range of operation issues that are alleviated with the use of supercapacitors. There have been a few reports on thin-film and other micro-supercapacitors, but they are either too thin to provide sufficient energy or the technology is not scalable. By etching supercapacitor electrodes into conductive titanium carbide substrates, we demonstrate that monolithic carbon films lead to a volumetric capacity exceeding that of micro- and macroscale supercapacitors reported thus far, by a factor of 2. This study also provides the framework for integration of high-performance micro-supercapacitors onto a variety of devices.

Vortex pinning in superconducting Nb thin films deposited on nanoporous alumina templates

DEFF Research Database (Denmark)

Vinckx, W.; Vanacken, J.; Moshchalkov, V.V.

2006-01-01

We present a study of magnetization and transport properties of superconducting Nb thin films deposited on nanoporous aluminium oxide templates. Periodic oscillations in the critical temperature vs. field, matching effects in fields up to 700 mT and strongly enhanced critical currents were observed...

Formation, properties, and ion irradiation effects of hexagonal structure MoN thin films

International Nuclear Information System (INIS)

Christen, D.K.; Sekula, S.T.; Ellis, J.T.; Lewis, J.D.; Williams, J.M.

1986-09-01

Thin films (100-120 nm) of hexagonal structures MoN have been fabricated by reaction of Mo films in an NH 3 atmosphere. The as-formed films possessed superconducting transition temperatures T/sub c/ ≅ 13 0 K, with resistance ratios r = R(296K)/R(T/sub c/) in the range 5 to 10, low-temperature normal state resistivities rho 0 = 4 to 10 μΩ-cm, and extrapolated upper critical fields H/sub c2/(0) = 4.0 to 5.0 T. Thin film x-ray diffraction patterns revealed no visible second phase, with measured lattice parameters close to literature values. The effects of lattice disorder on the superconducting and electronic properties were investigated by irradiation with nitrogen ions of energy 45 and 340 keV, resulting in a nearly uniform damage profile without the introduction of any new chemical species. The results indicate that ordered hexagonal MoN shows some of the unusual properties characteristic of moderate-to-high T/sub c/ transition metal compounds, but is relatively insensitive to degradation of the superconducting properties by lattice disorder. For ion fluences PHI up to 2 x 10 16 N-ions/cm 2 , T/sub c/ is found to decrease monotonically and saturate at 9.5 0 K, almost 3/4 the initial value, while H/sub c2/(0) undergoes a gradual increase to 11T

Angular dependence of the irreversible magnetization of YBa2Cu3O7 superconducting thin films

International Nuclear Information System (INIS)

Thrane, B.P.; Schlenker, C.; Dumas, J.; Buder, R.

1996-01-01

YBa 2 Cu 3 O 7 superconducting thin films have been studied by magnetization measurements in oblique fields up to 0.8 T both at low temperature and at temperatures close to T c . Both components of magnetization parallel and perpendicular to the applied field could be measured with two pairs of crossed detection coils. In all cases the magnetization is found to be perpendicular to the film plane. This is due to the self-field effects related to the thin-film geometry which force the critical currents to circulate along the film plane. At low temperature the properties are found to depend only on the component of the applied magnetic field perpendicular to this plane, as expected in the situation where demagnetizing field effects are dominant. However, at temperatures close to T c the critical currents and therefore the pinning are found to increase when the applied field approaches the film plane. This is attributed to the effect of intrinsic pinning which may be related to the kink structure of the vortices in oblique fields. copyright 1996 The American Physical Society

Direct growth of superconducting NdFeAs(O,F) thin films by MBE

Energy Technology Data Exchange (ETDEWEB)

Chihara, Masashi, E-mail: chihara@iku.xtal.nagoya-u.ac.jp [Department of Crystalline Materials Science, Nagoya University, Chikusa-ku, Nagoya 464-8603 (Japan); Sumiya, Naoki; Arai, Kenta [Department of Crystalline Materials Science, Nagoya University, Chikusa-ku, Nagoya 464-8603 (Japan); Ichinose, Ataru; Tsukada, Ichiro [Central Research Institute of Electric Power Industry, Yokosuka-shi, Kanagawa 240-0101 (Japan); Hatano, Takafumi; Iida, Kazumasa; Ikuta, Hiroshi [Department of Crystalline Materials Science, Nagoya University, Chikusa-ku, Nagoya 464-8603 (Japan)

2015-11-15

Highlights: • Highly textured NdFeAs(O,F) thin films were obtained by a direct growth method. • Enhancing the migration was crucial to realize the direct growth. • The critical current density exceeded 3 MA/cm{sup 2} at self-field and 1 MA/cm{sup 2} at 9 T. • A two-dimensional growth was confirmed by the observation of surface morphology. - Abstract: We report on the growth of NdFeAs(O,F) superconducting thin films by molecular beam epitaxy without having a NdOF secondary layer that was necessary for fluorine doping in our previous studies. The key to realizing the direct growth of a superconducting film was the enhancement of migration of the raw materials on the substrate, which was accomplished by two steps. Firstly, we increased the growth temperature that improved the crystalline quality of parent NdFeAsO thin films. Secondly, the atmosphere in the chamber during the growth was improved by changing the crucible material of the Fe source cell. Highly textured NdFeAs(O,F) thin films with critical temperatures up to 50 K were obtained, and terraces were observed by atomic force microscope, indicating a two-dimensional growth. However, precipitates were also found on the surface, which suggests that enhancing further the migration is necessary for obtaining a NdFeAs(O,F) thin film with a better quality.

Micro-supercapacitors from carbide derived carbon (CDC) films on silicon chips

Science.gov (United States)

Huang, Peihua; Heon, Min; Pech, David; Brunet, Magali; Taberna, Pierre-Louis; Gogotsi, Yury; Lofland, Samuel; Hettinger, Jeffrey D.; Simon, Patrice

2013-03-01

Interdigitated on-chip micro-supercapacitors based on Carbide Derived Carbon (CDC) films were fabricated and tested. A titanium carbide (TiC) film was patterned and treated with chlorine to obtain a TiC derived carbon (TiC-CDC) film, followed by the deposition of two types of current collectors (Ti/Au and Al) using standard micro-fabrication processes. CDC based micro-supercapacitors were electrochemically characterized by cyclic voltammetry and impedance spectroscopy using a 1 M tetraethylammonium tetrafluoroborate, NEt4BF4, in propylene carbonate (PC) electrolyte. A capacitance of 0.78 mF for the device and 1.5 mF cm-2 as the specific capacitance for the footprint of the device was measured for a 2 V potential range at 100 mV s-1. A specific energy of 3.0 mJ cm-2 and a specific power of 84 mW cm-2 were calculated for the devices. These devices provide a pathway for fabricating pure carbon-based micro-supercapacitors by micro-fabrication, and can be used for powering micro-electromechanical systems (MEMS) and electronic devices.

Micro-structuring of thick NdFeB films using high-power plasma etching for magnetic MEMS application

International Nuclear Information System (INIS)

Jiang, Yonggang; Fujita, Takayuki; Higuchi, Kohei; Maenaka, Kazusuke; Masaoka, Shingo; Uehara, Minoru

2011-01-01

This paper describes the micro-patterning of thick NdFeB magnetic films using a high-power plasma etching method. The effects of RF bias power and gas composition on the selectivity and etching rate are experimentally studied. A maximum etching rate of 60 nm min −1 is achieved with an inductively coupled plasma power of 500 W and a RF bias power of 200 W. A maximum selectivity of 0.26 between hard baked AZP4903 photoresist and NdFeB magnetic films is achieved when volumetric Cl 2 concentration is 2.5%. NdFeB micro-magnets as thick as 4.2 µm are achieved by using AZP4903 photoresist. Magnetic film as thick as 10 µm can be patterned by using SU-8 photoresist with a thickness of 100 µm as the mask. The magnetic property of patterned microstructures is characterized using a vibrating sample magnetometer and the magnetic field distribution is measured using a Hall effect sensor IC. The characterization results indicate that the patterned magnetic microstructures have a high magnetic remanance of 1.0 T, which is comparable to that of the non-patterned NdFeB films.

Cell behaviors on micro-patterned porous thin films

International Nuclear Information System (INIS)

Phong, Ho Quoc; Wang Shuling; Wang, Meng-Jiy

2010-01-01

Thin polymer films with patterned surfaces have drawn tremendous attention in manufacturing advanced electronic, mechanical devices and in biomaterials due to the advantageous properties such as mechanical strength, chemical resistance and optic transparency. The applications can be extended to the fields such as catalysts, antireflection coatings, template for inorganic growth masks, and substrates for cell culturing providing the patterned surface containing micron-sized features. Various methods have been used to fabricate polymers with micro-patterned surfaces such as photolithographic, ink-jet printing, nonsolvent, spin coating in a dry environment, self-organization, and the condensation of monodisperse water droplet on the polymer solution. The physiological functions of mature cells depend on the microenvironment/niche surrounding which can provide proper factors to regulate cell proliferation and differentiation. While designing appropriate scaffolds for tissue engineering, the microstructure is one of the most important factors to be considered. In this work, a facile single-step phase separation method was used to create micro-patterned polymer thin films with concaves or convexes with sizes ranged from 7 to 70 μm. The effects of water content, casting volume and the addition of surfactant on the distribution of pores and substrate morphology were examined. Moreover, detailed observations of fibroblast cells on the micro-patterned thin films were presented to compare and elucidate the roles of surface micro-features and chemical functionalities.

Dome shaped micro-laser encapsulated in a flexible film

Science.gov (United States)

Ioppolo, T.; Manzo, M.

2014-11-01

In this paper, we demonstrated multimode laser emission from a dome shaped micro-scale resonator encapsulated in a flexible polymer film. The resonator with a radius of ~60 microns was made of Norland Blocking Adhesive (NBA 107) doped with a solution of rhodamine 6G and ethanol. The dome was encapsulated in a flexible polymeric film made of polydymethylsiloxane (PDMS) with a thickness of 1 mm. The micro-scale laser was optically pumped using a frequency doubled Q-switch Nd:YAG laser with pulse repetition of 10 Hz and pulse duration of 9 ns. Experiments were carried out to investigate the lasing properties of this laser structure. The pumping threshold for multimode laser emission was below 100 µJ cm-2. The average optical quality factor for all observed laser modes was of the order of 104. Using a fluence of 315.8 µJ cm-2 it was observed that the intensity of the laser emission dropped by 62% after 5 min of operation. These results showed that these solid state flexible lasers are easy to fabricate and can be integrated into novel flexible photonic devices and novel photonic sensors.

Superconductivity in volumetric and film ceramics Bi-Sr-Ca-Cu-O

Energy Technology Data Exchange (ETDEWEB)

Sukhanov, A A; Ozmanyan, Kh R; Sandomirskij, B B

1988-07-10

A superconducting transition with T/sub c0/=82-95 K and T/sub c/(R=0)=82-72 K was observed in volumetric and film Bi(Sr/sub 1-x/Ca/sub x/)/sub 2/Cu/sub 3/O/sub y/ samples obtained by solid-phase reaction. Temperature dependences of resistance critical current and magnetic susceptibility are measured.

Design of RF structures for a superconducting proton linac

International Nuclear Information System (INIS)

Pande, Rajni; Roy, Shweta; Rao, S.V.L.S.; Krishnagopal, S.; Singh, P.

2013-01-01

One of the main components of the Accelerator Driven System (ADS) programme in India is a 1 GeV, high intensity CW proton accelerator that will be superconducting after the radio-frequency quadrupole (RFQ), i.e. after 3 MeV. The superconducting linac will consist of various superconducting structures like Half Wave Resonators, Spoke Resonators and elliptical cavities, operating at RF frequencies of 162.5 MHz, 325 MHz and 650 MHz. The paper will discuss the optimization of the electromagnetic design of the various superconducting structures. (author)

Depth profiling of superconducting thin films using rare gas ion sputtering with laser postionization

International Nuclear Information System (INIS)

Pallix, J.B.; Becker, C.H.; Missert, N.; Char, K.; Hammond, R.H.

1988-01-01

Surface analysis by laser ionization (SALI) has been used to examine a high-T/sub c/ superconducting thin film of nominal composition YBa 2 Cu 3 O 7 deposited on SrTiO 3 (100) by reactive magnetron sputtering. The main focus of this work was to probe the compositional uniformity and the impurity content throughout the 1800 A thick film having critical current densities of 1 to 2 x 10 6 A/cm 2 . SALI depth profiles show this film to be more uniform than thicker films (∼1 μm, prepared by electron beam codeposition) which were studied previously, yet the data show that some additional (non-superconducting) phases derived from Y, Ba, Cu, and O are still present. These additional phases are studied by monitoring the atomic and diatomic-oxide photoion profiles and also the depth profiles of various clusters (e.g. Y 2 O 2 + , Y 2 O 3 + , Y 3 O 4 + , Ba 2 O + , Ba 2 O 2 + , BaCu + , BaCuO + , YBaO 2 + , YSrO 2 + , etc.). A variety of impurities are observed to occur throughout the film including rather large concentrations of Sr. Hydroxides, F, Cl, and CO/sub x/ are evident particularly in the sample's near surface region (the top ∼100 A)

Depth profiling of superconducting thin films using rare gas ion sputtering with laser postionization

Science.gov (United States)

Pallix, J. B.; Becker, C. H.; Missert, N.; Char, K.; Hammond, R. H.

1988-02-01

Surface analysis by laser ionization (SALI) has been used to examine a high-Tc superconducting thin film of nominal composition YBa2Cu3O7 deposited on SrTiO3 (100) by reactive magnetron sputtering. The main focus of this work was to probe the compositional uniformity and the impurity content throughout the 1800 Å thick film having critical current densities of 1 to 2×106 A/cm2. SALI depth profiles show this film to be more uniform than thicker films (˜1 μm, prepared by electron beam codeposition) which were studied previously, yet the data show that some additional (non-superconducting) phases derived from Y, Ba, Cu, and O are still present. These additional phases are studied by monitoring the atomic and diatomic-oxide photoion profiles and also the depth profiles of various clusters (e.g. Y2O2+, Y2O3+, Y3O4+, Ba2O+, Ba2O2+, BaCu+, BaCuO+, YBaO2+, YSrO2+, etc.). A variety of impurities are observed to occur throughout the film including rather large concentrations of Sr. Hydroxides, F, Cl, and COx are evident particularly in the sample's near surface region (the top ˜100 Å).

Effect of micro-patterned fluorine-doped tin oxide films on electrochromic properties of Prussian blue films

International Nuclear Information System (INIS)

Lee, Kyuha; Kim, A-Young; Park, Ji Hun; Jung, Hun-Gi; Choi, Wonchang; Lee, Hwa Young; Lee, Joong Kee

2014-01-01

Graphical abstract: - Highlights: • PB-based ECD employed micro-patterned FTO electrode was fabricated. • Effect of interface morphology on electrochromic characteristics was examined. • Electrochromic properties were enhanced by employing a patterned interface. - Abstract: The effect of interface morphology on electrochromic characteristics was examined for an electrochromic device (ECD). Micro-patterned fluorine-doped tin oxide (FTO) films were fabricated using a photolithography process. Prussian blue (PB) films were then deposited on the patterned FTO films. The surface areas of both PB films and FTO films were increased by patterning. ECDs were assembled using patterned PB/FTO films as the electrochromic electrode, bare FTO films as the counter electrode, and an electrolyte containing LiClO 4 salt. The increased effective surface area of the patterned PB/FTO electrode boosted the mobility of ions at the interphase between the electrolyte and PB electrode, and the electron transfer between PB films and FTO films. As a result, electrochromic properties such as transmittance and response time were significantly improved by employing the patterned FTO films as the transparent conductive oxide layer of the electrochromic electrode

Micro-wrinkling and delamination-induced buckling of stretchable electronic structures

International Nuclear Information System (INIS)

Oyewole, O. K.; Yu, D.; Du, J.; Asare, J.; Fashina, A.; Oyewole, D. O.; Anye, V. C.; Zebaze Kana, M. G.

2015-01-01

This paper presents the results of experimental and theoretical/computational micro-wrinkles and buckling on the surfaces of stretchable poly-dimethylsiloxane (PDMS) coated with nano-scale Gold (Au) layers. The wrinkles and buckles are formed by the unloading of pre-stretched PDMS/Au structure after the evaporation of nano-scale Au layers. They are then characterized using atomic force microscopy and scanning electron microscopy. The critical stresses required for wrinkling and buckling are analyzed using analytical models. The possible interfacial cracking that can occur along with film buckling is also studied using finite element simulations of the interfacial crack growth. The implications of the results are discussed for potential applications of micro-wrinkles and micro-buckles in stretchable electronic structures and biomedical devices

Dopant rearrangement and superconductivity in Bi2Sr2-xLaxCuO6 thin films under annealing

International Nuclear Information System (INIS)

Cancellieri, C; Lin, P H; Ariosa, D; Pavuna, D

2007-01-01

By combining x-ray diffraction (XRD), x-ray photoemission spectroscopy (XPS) and AC susceptibility measurements we investigate the evolution of structural and superconducting properties of La-doped Bi-2201 thin films grown by pulsed laser deposition (PLD) under different annealing conditions. We find that the main effect of oxygen annealing is to improve the crystal coherence by enabling La cation migration to the Sr sites. This activates the desired hole doping. Short-time Ar annealing removes the interstitial oxygen between the BiO layers, fine adjusting the effective hole doping. The superconducting critical temperature is consequently enhanced. However, longer annealings result in phase separation and segregation of the homologous compound Bi-1201. We attribute this effect to the loss of Bi during the annealing

浅析微电影%On the Micro-film

Institute of Scientific and Technical Information of China (English)

张芸

2015-01-01

With the enormous influence of mobile phones, Internet and other new media technologies and the rapid development of video networks, with its micro-micro-film length, micro-production, the three major advantages of micro-investments become “favorite” Chinese Internet. As a product of cross-border advertising and film, micro-film is the inevitable product of the development of technology and the Times. The rapid rise of this new mode of transmission, has a profound social background, media environment, technical background and internal drivers.%随着手机、网络等新媒体技术的飞速发展及视频网络的巨大影响力，微电影以其微时长、微制作、微投资的三大优势成为中国互联网上的“新宠”。作为广告与电影跨界的产物，微电影是科技与时代发展下的必然产物。这种新传播方式的快速崛起，有着深刻的社会背景、媒介环境、技术背景和内在驱动因素。

Superconducting Ferromagnetic Nanodiamond.

Science.gov (United States)

Zhang, Gufei; Samuely, Tomas; Xu, Zheng; Jochum, Johanna K; Volodin, Alexander; Zhou, Shengqiang; May, Paul W; Onufriienko, Oleksandr; Kačmarčík, Jozef; Steele, Julian A; Li, Jun; Vanacken, Johan; Vacík, Jiri; Szabó, Pavol; Yuan, Haifeng; Roeffaers, Maarten B J; Cerbu, Dorin; Samuely, Peter; Hofkens, Johan; Moshchalkov, Victor V

2017-06-27

Superconductivity and ferromagnetism are two mutually antagonistic states in condensed matter. Research on the interplay between these two competing orderings sheds light not only on the cause of various quantum phenomena in strongly correlated systems but also on the general mechanism of superconductivity. Here we report on the observation of the electronic entanglement between superconducting and ferromagnetic states in hydrogenated boron-doped nanodiamond films, which have a superconducting transition temperature T c ∼ 3 K and a Curie temperature T Curie > 400 K. In spite of the high T Curie , our nanodiamond films demonstrate a decrease in the temperature dependence of magnetization below 100 K, in correspondence to an increase in the temperature dependence of resistivity. These anomalous magnetic and electrical transport properties reveal the presence of an intriguing precursor phase, in which spin fluctuations intervene as a result of the interplay between the two antagonistic states. Furthermore, the observations of high-temperature ferromagnetism, giant positive magnetoresistance, and anomalous Hall effect bring attention to the potential applications of our superconducting ferromagnetic nanodiamond films in magnetoelectronics, spintronics, and magnetic field sensing.

Bi--Sr--Ca--Cu--O superconducting films fabricated using metal alkoxides

International Nuclear Information System (INIS)

Katayama, S.; Sekine, M.

1991-01-01

Superconducting films in the Bi--Sr--Ca--Cu--O systems were made using metal alkoxides. To prepare a dip-coating solution using a mixed alkoxide solution, insoluble Cu and Bi alkoxides were dissolved by modification with 2-dimethylaminoethanol and formation of a double alkoxide, respectively. Formation of the double alkoxides of Bi with Ca or Sr was confirmed using FT-IR and 1 H-NMR. Bi--Sr--Ca--Cu--O films on yttria-stabilized ZrO 2 and single crystal MgO(100) substrates were made using this solution. The films were closely oriented along the c-axis perpendicular to the substrate. The film on MgO(100) fired at 850 degree C for 48 h showed two resistance drops around 115 and 85 K, corresponding to the high-T c and low-T c phases, respectively, and zero resistance at 72 K

Superconducting Film Flux Transformer for a Sensor of a Weak Magnetic Field

International Nuclear Information System (INIS)

Ichkitidze, L; Mironyuk, A

2012-01-01

The object of study is a superconducting film flux transformer in the form of a square shaped loop with the tapering operative strip used in a sensor of a weak magnetic field. The magnetosensitive film element based on the giant magnetoresistance effect is overlapped with the tapering operative strip of the flux transformer; it is separated from the latter by the insulator film. It is shown that the topological nanostructuring of the operative strip of the flux transformer increases its gain factor by one or more orders of magnitude, i.e. increases its efficiency, which leads to a significant improvement of important parameters of a magnetic-field sensor.

High temperature interface superconductivity

International Nuclear Information System (INIS)

Gozar, A.; Bozovic, I.

2016-01-01

Highlight: • This review article covers the topic of high temperature interface superconductivity. • New materials and techniques used for achieving interface superconductivity are discussed. • We emphasize the role played by the differences in structure and electronic properties at the interface with respect to the bulk of the constituents. - Abstract: High-T_c superconductivity at interfaces has a history of more than a couple of decades. In this review we focus our attention on copper-oxide based heterostructures and multi-layers. We first discuss the technique, atomic layer-by-layer molecular beam epitaxy (ALL-MBE) engineering, that enabled High-T_c Interface Superconductivity (HT-IS), and the challenges associated with the realization of high quality interfaces. Then we turn our attention to the experiments which shed light on the structure and properties of interfacial layers, allowing comparison to those of single-phase films and bulk crystals. Both ‘passive’ hetero-structures as well as surface-induced effects by external gating are discussed. We conclude by comparing HT-IS in cuprates and in other classes of materials, especially Fe-based superconductors, and by examining the grand challenges currently laying ahead for the field.

Influence of ion beam mixing on the growth of high temperature oxide superconducting thin film

International Nuclear Information System (INIS)

Bordes, N.; Rollett, A.D.; Cohen, M.R.; Nastasi, M.

1989-01-01

The superconducting properties of high temperature superconductor thin films are dependent on the quality of the substrate used to grow these films. In order to maximize the lattice matching between the superconducting film and the substrate, we have used a YBa 2 Cu 3 O 7 thin film deposited on left-angle 100 right-angle SrTiO 3 as a template. The first film was prepared by coevaporation of Y, BaF 2 and Cu on left-angle 100 right-angle SrTiO 3 , followed by an anneal in ''wet'' oxygen at 850 degree C. This film showed a sharp transition at about 90 K. A thicker layer of about 5000 A was then deposited on top of this first 2000 angstrom film, using the same procedure. After the post anneal at 850 degree C, the transition took place at 80 K and no epitaxy of the second film was observed. Ion beam mixing at 400 degree C, using 400 keV O ions was done at the interface of the two films (the second one being not annealed). After the post anneal, the film displayed an improved Tc at 90K. Moreover, epitaxy was shown to take place from the interface SrTiO 3 -123 film towards the surface and was dependent of the dose. These results will be discussed from the data obtained from Rutherford backscattering spectroscopy (RBS) combined with channeling experiments, x-ray diffraction (XRD) and scanning electron microscopy (SEM) observations. 8 refs., 2 figs., 2 tabs

Growth and micro structural studies on Yittria Stabilized Zirconia (YSZ) and Strontium Titanate (STO) buffer layers

Energy Technology Data Exchange (ETDEWEB)

Srinivas, S.; Bhatnagar, A.K. [Univ. of Hyderabad (India); Pinto, R. [Solid State Electronics Group, Bombay (India)] [and others

1994-12-31

Microstructure of Yittria Stabilized Zirconia (YSZ) and Strontium Titanate (STO) of radio frequency magnetron sputtered buffer layers was studied at various sputtering conditions on Si<100>, Sapphire and LaAlO{sub 3} <100> substrates. The effect of substrate temperatures upto 800 C and sputtering gas pressures in the range of 50 mTorr. of growth conditions was studied. The buffer layers of YSZ and STO showed a strong tendency for columnar structure with variation growth conditions. The buffer layers of YSZ and STO showed orientation. The tendency for columnar growth was observed above 15 mTorr sputtering gas pressure and at high substrate temperatures. Post annealing of these films in oxygen atmosphere reduced the oxygen deficiency and strain generated during growth of the films. Strong c-axis oriented superconducting YBa{sub 2}Cu{sub 9}O{sub 7-x} (YBCO) thin films were obtained on these buffer layers using pulsed laser ablation technique. YBCO films deposited on multilayers of YSZ and STO were shown to have better superconducting properties.

MicroRaman scattering from polycrystalline CuInS{sub 2} films: structural analysis

Energy Technology Data Exchange (ETDEWEB)

Alvarez-Garcia, J.; Marcos-Ruzafa, J.; Perez-Rodriguez, A.; Romano-Rodriguez, A.; Morante, J.R. [Barcelona Univ. (Spain). Dept. de Fisica Aplicada i Electronica; Scheer, R. [Hahn-Meitner-Institut Berlin GmbH (Germany)

2000-02-21

CuInS{sub 2} thin films co-evaporated with gradual chemical composition have been characterised by microRaman scattering measurements. For the Cu rich region, the mode A{sub 1} at about 290 cm{sup -1} corresponding to the chalcopyrite phase is dominant. For the Cu poor region, this mode is accompanied by a strong contribution at about 306 cm{sup -1}. Besides, the mode A{sub 1} is broadened and shifted towards higher frequencies, which suggests an inferior structural quality of the Cu poor region. Decreasing the temperature of deposition leads to a dramatic decrease of structural quality in both In and Cu rich regions. The correlation between the appearance of the 306 cm{sup -1} mode and the spectral features of the mode A{sub 1} suggest the higher frequency mode is not related to the excess In in the layer but to structural effects as lattice disorder. Combined in-depth Auger electron spectroscopy and Raman scattering measurements have also shown the presence of a more complex structure for the Cu poor region of the layers, which presents a significant CuIn{sub 5}S{sub 8} secondary phase contribution in the spectra from the central region of the layers. The correlation of this contribution with the spectral features of the CuInS{sub 2} modes suggests a direct relationship between the presence of this In rich secondary phase and disorder at the CuInS{sub 2} lattice. (orig.)

Effect of Substrate Roughness on Adhesion and Structural Properties of Ti-Ni Shape Memory Alloy Thin Film.

Science.gov (United States)

Kim, Donghwan; Lee, Hyunsuk; Bae, Joohyeon; Jeong, Hyomin; Choi, Byeongkeun; Nam, Taehyun; Noh, Jungpil

2018-09-01

Ti-Ni shape memory alloy (SMA) thin films are very attractive material for industrial and medical applications such as micro-actuator, micro-sensors, and stents for blood vessels. An important property besides shape memory effect in the application of SMA thin films is the adhesion between the film and the substrate. When using thin films as micro-actuators or micro-sensors in MEMS, the film must be strongly adhered to the substrate. On the other hand, when using SMA thin films in medical devices such as stents, the deposited alloy thin film must be easily separable from the substrate for efficient processing. In this study, we investigated the effect of substrate roughness on the adhesion of Ti-Ni SMA thin films, as well as the structural properties and phase-transformation behavior of the fabricated films. Ti-Ni SMA thin films were deposited onto etched glass substrates with magnetron sputtering. Radio frequency plasma was used for etching the substrate. The adhesion properties were investigated through progressive scratch test. Structural properties of the films were determined via Feld emission scanning electron microscopy, X-ray diffraction measurements (XRD) and Energy-dispersive X-ray spectroscopy analysis. Phase transformation behaviors were observed with differential scanning calorimetry and low temperature-XRD. Ti-Ni SMA thin film deposited onto rough substrate provides higher adhesive strength than smooth substrate. However the roughness of the substrate has no influence on the growth and crystallization of the Ti-Ni SMA thin films.

Growth and characterizations of GaN micro-rods on graphene films for flexible light emitting diodes

Directory of Open Access Journals (Sweden)

Kunook Chung

2014-09-01

Full Text Available We report the growth of GaN micro-rods and coaxial quantum-well heterostructures on graphene films, together with structural and optical characterization, for applications in flexible optical devices. Graphene films were grown on Cu foil by means of chemical vapor deposition, and used as the substrates for the growth of the GaN micro-rods, which were subsequently transferred onto SiO2/Si substrates. Highly Si-doped, n-type GaN micro-rods were grown on the graphene films using metal–organic chemical vapor deposition. The growth and vertical alignment of the GaN micro-rods, which is a critical factor for the fabrication of high-performance light-emitting diodes (LEDs, were characterized using electron microscopy and X-ray diffraction. The GaN micro-rods exhibited promising photoluminescence characteristics for optoelectronic device applications, including room-temperature stimulated emission. To fabricate flexible LEDs, InxGa1–xN/GaN multiple quantum wells and a p-type GaN layer were deposited coaxially on the GaN micro-rods, and transferred onto Ag-coated polymer substrates using lift-off. Ti/Au and Ni/Au metal layers were formed to provide electrical contacts to the n-type and p-type GaN regions, respectively. The micro-rod LEDs exhibited intense emission of visible light, even after transfer onto the flexible polymer substrate, and reliable operation was achieved following numerous cycles of mechanical deformation.

VOPcPhO:P3HT composite micro-structures with nano-porous surface morphology

Energy Technology Data Exchange (ETDEWEB)

Azmer, Mohamad Izzat [Low Dimensional Materials Research Centre (LDMRC), Department of Physics, Faculty of Science, University of Malaya, 50603 Kuala Lumpur (Malaysia); Ahmad, Zubair, E-mail: zubairtarar@qu.edu.qa [Center for Advanced Materials (CAM), Qatar University, P. O. Box 2713, Doha (Qatar); Sulaiman, Khaulah, E-mail: khaulah@um.edu.my [Low Dimensional Materials Research Centre (LDMRC), Department of Physics, Faculty of Science, University of Malaya, 50603 Kuala Lumpur (Malaysia); Touati, Farid [Department of Electrical Engineering, College of Engineering, Qatar University, P. O. Box 2713, Doha (Qatar); Bawazeer, Tahani M. [Department of Chemistry, Faculty of Applied Science, Umm Al-Qura University, Makkah (Saudi Arabia); Alsoufi, Mohammad S. [Mechanical Engineering Department, College of Engineering and Islamic Architecture, Umm Al-Qura University, Makkah (Saudi Arabia)

2017-03-31

Highlights: • VOPcPhO:P3HT micro-structures with nano-porous surface morphology have been formed. • Multidimensional structures have been formed by electro-spraying technique. • The electro-sprayed films are very promising for the humidity sensors. - Abstract: In this paper, composite micro-structures of Vanadyl 2,9,16,23-tetraphenoxy-29H,31H-phthalocyanine) (VOPcPhO) and Poly (3-hexylthiophene-2,5-diyl) (P3HT) complex with nano-porous surface morphology have been developed by electro-spraying technique. The structural and morphological characteristics of the VOPcPhO:P3HT composite films have been studied by field emission scanning electron microscopy (FESEM) and atomic force microscopy (AFM). The multidimensional VOPcPhO:P3HT micro-structures formed by electro-spraying with nano-porous surface morphology are very promising for the humidity sensors due to the pore sizes in the range of micro to nano-meters scale. The performance of the VOPcPhO:P3HT electro-sprayed sensor is superior in term of sensitivity, hysteresis and response/recovery times as compared to the spin-coated one. The electro-sprayed humidity sensor exhibits ∼3 times and 0.19 times lower hysteresis in capacitive and resistive mode, respectively, as compared to the spin-coated humidity sensor.

Raman scattering diagnostics of YBa2Cu3Ox high temperature superconducting films

International Nuclear Information System (INIS)

Bagratashvili, V.N.; Burimov, V.N.; Denisov, V.N.

1988-01-01

Superconducting YBa 2 Cu 3 O x films produced by laser spraying of ceramic material are investigated by light Raman scattering (LCS). It is shown that using LCS it is possible to obtain data on phase composition and prevailing film orientation and to find optical conditions for their synthesis. The LCS method feature consists in a possibility of non-destructive remote control and high space resolution (several microns). Experimental results have shown that the best parameters (the highest T c and the narrowest Δ T c interval) are typical of films with prevailing orientation of 0 xy crystallite plane parallel to the surface

Ultrasensitive interplay between ferromagnetism and superconductivity in NbGd composite thin films

Science.gov (United States)

Bawa, Ambika; Gupta, Anurag; Singh, Sandeep; Awana, V. P. S.; Sahoo, Sangeeta

2016-01-01

A model binary hybrid system composed of a randomly distributed rare-earth ferromagnetic (Gd) part embedded in an s-wave superconducting (Nb) matrix is being manufactured to study the interplay between competing superconducting and ferromagnetic order parameters. The normal metallic to superconducting phase transition appears to be very sensitive to the magnetic counterpart and the modulation of the superconducing properties follow closely to the Abrikosov-Gor’kov (AG) theory of magnetic impurity induced pair breaking mechanism. A critical concentration of Gd is obtained for the studied NbGd based composite films (CFs) above which superconductivity disappears. Besides, a magnetic ordering resembling the paramagnetic Meissner effect (PME) appears in DC magnetization measurements at temperatures close to the superconducting transition temperature. The positive magnetization related to the PME emerges upon doping Nb with Gd. The temperature dependent resistance measurements evolve in a similar fashion with the concentration of Gd as that with an external magnetic field and in both the cases, the transition curves accompany several intermediate features indicating the traces of magnetism originated either from Gd or from the external field. Finally, the signatures of magnetism appear evidently in the magnetization and transport measurements for the CFs with very low (<1 at.%) doping of Gd.

Effect of micro-patterned fluorine-doped tin oxide films on electrochromic properties of Prussian blue films

Energy Technology Data Exchange (ETDEWEB)

Lee, Kyuha [Center for Energy Convergence Research, Green City Technology Institute, Korea Institute of Science and Technology, Hwarangno 14-gil 5, Seongbuk-gu, Seoul 136-791 (Korea, Republic of); Kim, A-Young [Center for Energy Convergence Research, Green City Technology Institute, Korea Institute of Science and Technology, Hwarangno 14-gil 5, Seongbuk-gu, Seoul 136-791 (Korea, Republic of); Department of Material Science and Engineering, Korea University, Seoul 136-701 (Korea, Republic of); Park, Ji Hun; Jung, Hun-Gi; Choi, Wonchang; Lee, Hwa Young [Center for Energy Convergence Research, Green City Technology Institute, Korea Institute of Science and Technology, Hwarangno 14-gil 5, Seongbuk-gu, Seoul 136-791 (Korea, Republic of); Lee, Joong Kee, E-mail: leejk@kist.re.kr [Center for Energy Convergence Research, Green City Technology Institute, Korea Institute of Science and Technology, Hwarangno 14-gil 5, Seongbuk-gu, Seoul 136-791 (Korea, Republic of)

2014-09-15

Graphical abstract: - Highlights: • PB-based ECD employed micro-patterned FTO electrode was fabricated. • Effect of interface morphology on electrochromic characteristics was examined. • Electrochromic properties were enhanced by employing a patterned interface. - Abstract: The effect of interface morphology on electrochromic characteristics was examined for an electrochromic device (ECD). Micro-patterned fluorine-doped tin oxide (FTO) films were fabricated using a photolithography process. Prussian blue (PB) films were then deposited on the patterned FTO films. The surface areas of both PB films and FTO films were increased by patterning. ECDs were assembled using patterned PB/FTO films as the electrochromic electrode, bare FTO films as the counter electrode, and an electrolyte containing LiClO{sub 4} salt. The increased effective surface area of the patterned PB/FTO electrode boosted the mobility of ions at the interphase between the electrolyte and PB electrode, and the electron transfer between PB films and FTO films. As a result, electrochromic properties such as transmittance and response time were significantly improved by employing the patterned FTO films as the transparent conductive oxide layer of the electrochromic electrode.

A low energy muon spin rotation and point contact tunneling study of niobium films prepared for superconducting cavities

Science.gov (United States)

Junginger, Tobias; Calatroni, S.; Sublet, A.; Terenziani, G.; Prokscha, T.; Salman, Z.; Suter, A.; Proslier, T.; Zasadzinski, J.

2017-12-01

Point contact tunneling and low energy muon spin rotation are used to probe, on the same samples, the surface superconducting properties of micrometer thick niobium films deposited onto copper substrates using different sputtering techniques: diode, dc magnetron and HIPIMS. The combined results are compared to radio-frequency tests performances of RF cavities made with the same processes. Degraded surface superconducting properties are found to correlate to lower quality factors and stronger Q-slope. In addition, both techniques find evidence for surface paramagnetism on all samples and particularly on Nb films prepared by HIPIMS.

Control of wettability of hydrogenated amorphous carbon thin films by laser-assisted micro- and nanostructuring

International Nuclear Information System (INIS)

Pfleging, Wilhelm; Kohler, Robert; Torge, Maika; Trouillet, Vanessa; Danneil, Friederike; Stueber, Michael

2011-01-01

A flexible and rapid surface functionalization of amorphous carbon films shows a great potential for various application fields such as biological surfaces and tribological systems. For this purpose, the combination of thin film deposition and subsequent laser material processing was investigated. Amorphous carbon layers doped with hydrogen were deposited on silicon wafers by reactive direct-current magnetron sputtering. Films with three different hydrogen contents were synthesized. Subsequent to the thin film deposition process, UV laser material processing at wavelengths of 193 nm or 248 nm was performed with respect to chemical surface modification and surface structuring on micro- and nanometer scale. Depending on structure size and laser-induced chemical surface modification the adjustment of the surface energy and wetting behaviour in a broad range from hydrophobic to hydrophilic was possible. The chemical modification and the ablation mechanisms near the ablation threshold were strongly influenced by the hydrogen content in amorphous carbon thin films. Structural and chemical information of the as-deposited and modified films was obtained by Raman spectroscopy, X-ray photoelectron spectroscopy and contact angle measurements.

Antimicrobial edible coatings and films from micro-emulsions and their food applications.

Science.gov (United States)

Guo, Mingming; Yadav, Madhav P; Jin, Tony Z

2017-12-18

This study focused on the use of antimicrobial edible coatings and films from micro-emulsions to reduce populations of foodborne pathogens in foods. Corn-Bio-fiber gum (C-BFG) was used as an emulsifier with chitosan. Allyl isothiocyanate (AIT) and lauric arginate ester (LAE) served as antimicrobials. Micro-emulsions were obtained from a solution consisting of 1% chitosan, 0.5% C-BFG, and 1-4% AIT or LAE which was subject to high pressure homogenization (HPH) processing at 138MPa for 3cycles. Coatings and films produced from the micro-emulsions had micro-pores with sizes ranging from 100 to 300nm and micro-channels that hold antimicrobials effectively and facilitate the release of antimicrobials from the center to the surface of the films or coatings, thus enhancing their antimicrobial efficacy. The coatings and films with 1% AIT reduced populations of Listeria innocua by over 5, 2, and 3 log CFU in culture medium (Tryptic soy broth, TSB), ready-to-eat meat, and strawberries, respectively. The coatings and films with 1% LAE reduced populations of Escherichia coli O157:H7 and Salmonella spp. by over 5 and 2 log CFU in TSB and strawberries, respectively. This study provides an innovative approach for the development of effective antimicrobial materials to reduce food borne pathogenic contaminants on ready-to-eat meat, strawberries, or other food. Published by Elsevier B.V.

Low energy electron beam processing of YBCO thin films

Energy Technology Data Exchange (ETDEWEB)

Chromik, Š., E-mail: stefan.chromik@savba.sk [Institute of Electrical Engineering, SAS, Dúbravská cesta 9, 841 04 Bratislava (Slovakia); Camerlingo, C. [CNR-SPIN, Istituto Superconduttori, Materiali Innovativi e Dispositivi, via Campi Flegrei 34, 80078 Pozzuoli (Italy); Sojková, M.; Štrbík, V.; Talacko, M. [Institute of Electrical Engineering, SAS, Dúbravská cesta 9, 841 04 Bratislava (Slovakia); Malka, I.; Bar, I.; Bareli, G. [Department of Physics, Ben Gurion University of the Negev, P.O.B. 653, 84105 Beer Sheva (Israel); Jung, G. [Department of Physics, Ben Gurion University of the Negev, P.O.B. 653, 84105 Beer Sheva (Israel); Institute of Physics, Polish Academy of Sciences, Al. Lotników 32/46, 02-668 Warsaw (Poland)

2017-02-15

Highlights: • Improvement of superconducting properties of irradiated bridges under certain conditions. • 30 keV irradiation influence CuO{sub 2} planes as well as oxygen chains. • Direct confirmation of changes in oxygen chains using micro-Raman spectroscopy. • Possibility of electron writing. - Abstract: Effects of low energy 30 keV electron irradiation of superconducting YBa{sub 2}Cu{sub 3}O{sub 7−δ} thin films have been investigated by means of transport and micro-Raman spectroscopy measurements. The critical temperature and the critical current of 200 nm thick films initially increase with increasing fluency of the electron irradiation, reach the maximum at fluency 3 − 4 × 10{sup 20} electrons/cm{sup 2}, and then decrease with further fluency increase. In much thinner films (75 nm), the critical temperature increases while the critical current decreases after low energy electron irradiation with fluencies below 10{sup 20} electrons/cm{sup 2}. The Raman investigations suggest that critical temperature increase in irradiated films is due to healing of broken Cu−O chains that results in increased carrier’s concentration in superconducting CuO{sub 2} planes. Changes in the critical current are controlled by changes in the density of oxygen vacancies acting as effective pinning centers for flux vortices. The effects of low energy electron irradiation of YBCO turned out to result from a subtle balance of many processes involving oxygen removal, both by thermal activation and kick-off processes, and ordering of chains environment by incident electrons.

Electron mean free path dependence of the critical currents and the pair-breaking limit in superconducting films

International Nuclear Information System (INIS)

Fedorov, N.; Rinderer, L.

1977-01-01

We have studied the current-induced breakdown of superconductivity in wide (100--980 μm) and thin (0.25--0.98 μm) films of tin. It is shown that the current at which the resistance of the sample begins to rise rapidly in the process of the destruction of superconductivity by a current can be fairly well associated with the theoretical value of the pair-breaking current in the Ginzburg-Landau phenomenological approach (I/sub c//sup G L/). This effect is observed over a rather wide temperature region (up to ΔTapprox.0.7 K), depending on the electron mean free path in the films. The values of the critical currents outside the above-mentioned region correlate qualitatively with those determined by inhomogeneities of the films as proposed by Larkin and Ovchinnikov

MicroRNA-target binding structures mimic microRNA duplex structures in humans.

Directory of Open Access Journals (Sweden)

Xi Chen

Full Text Available Traditionally, researchers match a microRNA guide strand to mRNA sequences using sequence comparisons to predict its potential target genes. However, many of the predictions can be false positives due to limitations in sequence comparison alone. In this work, we consider the association of two related RNA structures that share a common guide strand: the microRNA duplex and the microRNA-target binding structure. We have analyzed thousands of such structure pairs and found many of them share high structural similarity. Therefore, we conclude that when predicting microRNA target genes, considering just the microRNA guide strand matches to gene sequences may not be sufficient--the microRNA duplex structure formed by the guide strand and its companion passenger strand must also be considered. We have developed software to translate RNA binding structure into encoded representations, and we have also created novel automatic comparison methods utilizing such encoded representations to determine RNA structure similarity. Our software and methods can be utilized in the other RNA secondary structure comparisons as well.

Properties of superconducting thin-film microbridges

International Nuclear Information System (INIS)

Pei, S.S.

1978-01-01

This work reports investigations upon the dependences of critical current and current phase relation on the dimensions of a superconducting thin-film microbridge. A model has been developed upon the Volkov's hyperbolic bridges and the Zaitsev's boundary conditions to calculate the spatial variation of the order parameter for given bridge dimensions. The results indicate that the rigid boundary conditions are good approximations to narrow bridges (W much less than L) only. The critical current density of the bridge has been calculated also as a function of the bridge dimensions. It is found that the critical current density of small bridges is enhanced above its mean field critical value due to the proximity effects of the banks. Very good agreement is found between the calculated enhancement of the critical current density and the experimental results. Direct measurements have been made on the current phase relation of indium bridges with width smaller than 0.6 μm. The difficulties due to the extra phase shifts from the series thin film electrodes are overcome by a specially designed double loop configuration which has an extra low effective inductance. It is found that the current phase relation of small bridges (W,L, xi, the results agree with the predictions of rigid boundary calculations as expected by our model

Bioinspired Non-iridescent Structural Color from Polymer Blend Thin Films

Science.gov (United States)

Nallapaneni, Asritha; Shawkey, Matthew; Karim, Alamgir

Colors exhibited in biological species are either due to natural pigments, sub-micron structural variation or both. Structural colors thus exhibited can be iridescent (ID) or non-iridescent (NID) in nature. NID colors originate due to interference and coherent scattering of light with quasi-ordered micro- and nano- structures. Specifically, in Eastern Bluebird (Sialia sialis) these nanostructures develop as a result of phase separation of β-keratin from cytoplasm present in cells. We replicate these structures via spinodal blend phase separation of PS-PMMA thin films. Colors of films vary from ultraviolet to blue. Scattering of UV-visible light from selectively leeched phase separated blends are studied in terms of varying domain spacing (200nm to 2 μm) of film. We control these parameters by tuning annealing time and temperature. Angle-resolved spectroscopy studies suggest that the films are weakly iridescent and scattering from phase-separated films is more diffused when compared to well-mixed films. This study offers solutions to several color-based application in paints and coatings industry.

Dome shaped micro-laser encapsulated in a flexible film

International Nuclear Information System (INIS)

Ioppolo, T; Manzo, M

2014-01-01

In this paper, we demonstrated multimode laser emission from a dome shaped micro-scale resonator encapsulated in a flexible polymer film. The resonator with a radius of ∼60 microns was made of Norland Blocking Adhesive (NBA 107) doped with a solution of rhodamine 6G and ethanol. The dome was encapsulated in a flexible polymeric film made of polydymethylsiloxane (PDMS) with a thickness of 1 mm. The micro-scale laser was optically pumped using a frequency doubled Q-switch Nd:YAG laser with pulse repetition of 10 Hz and pulse duration of 9 ns. Experiments were carried out to investigate the lasing properties of this laser structure. The pumping threshold for multimode laser emission was below 100 µJ cm −2 . The average optical quality factor for all observed laser modes was of the order of 10 4 . Using a fluence of 315.8 µJ cm −2 it was observed that the intensity of the laser emission dropped by 62% after 5 min of operation. These results showed that these solid state flexible lasers are easy to fabricate and can be integrated into novel flexible photonic devices and novel photonic sensors. (paper)

Superconducting oxypnictide thin films

Energy Technology Data Exchange (ETDEWEB)

Reisner, Andreas; Kidszun, Martin; Reich, Elke; Holzapfel, Bernhard; Schultz, Ludwig; Haindl, Silvia [IFW Dresden, Institute of Metallic Materials (Germany); Thersleff, Thomas [Uppsala University, Angstrom Laboratory (Sweden)

2012-07-01

We present an overview on the oxypnictide thin film preparation. So far, only LaAlO{sub 3} (001) single crystalline substrates provided a successful growth using pulsed laser deposition in combination with a post annealing process. Further experiments on the in-situ deposition will be reported. The structure of the films was investigated by X-ray diffractometry and transmission electron microscopy. Transport properties were measured with different applied fields to obtain a magnetic phase diagram for this new type of superconductor.

Enhancement of micro structural properties of PVA doped with MWCNT’s and metal oxide nanocomposites films

Energy Technology Data Exchange (ETDEWEB)

Kumar N B, Rithin [Dept of Physics, Srinivas School of Engineering, Mukka, Mangalore, Karnataka (India); Crasta, Vincent, E-mail: vcrasta@yahoo.com [Dept of Physics, St. Joseph Engineering College, Vamanjoor, Mangalore, Karnataka (India); Praveen, B. M. [Dept of Chemistry, Srinivas School of Engineering, Mukka, Mangalore, Karnataka (India); B, Shreeprakash [Dept of Mechanical Engineering, Srinivas School of Engineering, Mangalore, Karnataka (India)

2015-06-24

WO{sub 3} nanoparticles were prepared by using precipitation method and the multiwall Carbon nanotubes (MWCNT’s) were functionalized to make Carboxylated MWCNTs. Further, prepared WO{sub 3} and carboxylated MWCNT were doped into PVA matrix by coagulation technique and PVA nanocomposites were prepared by simple solvent casting technique. The films were characterized by XRD, FTIR spectroscopy and AFM. FTIR spectroscopy reveals the intensity of absorption of radiation at 3624.55 cm{sup −1} corresponds to the OH group of PVA. It changes in accordance with dopant concentration causing inter/intra molecular hydrogen bonding between the dopants and PVA back bone which leads to the complex formation. XRD data explores the crystalline nature of the film. It is found that for doping concentration x= 7.5 wt% the percentage crystallinity and crystallite size increases whereas micro structural strain and dislocation density decreases. An atomic force microscopy topographic analysis proves that the doped particles have an average size less than 15 nm, as confirmed by XRD data. It was found that roughness of the sample varies with dopant concentration causing variation in crystallinity.

Magnetic profiles in ferromagnetic/superconducting superlattices.

Energy Technology Data Exchange (ETDEWEB)

te Velthuis, S. G. E.; Hoffmann, A.; Santamaria, J.; Materials Science Division; Univ. Complutense de Madrid

2007-02-28

The interplay between ferromagnetism and superconductivity has been of longstanding fundamental research interest to scientists, as the competition between these generally mutually exclusive types of long-range order gives rise to a rich variety of physical phenomena. A method of studying these exciting effects is by investigating artificially layered systems, i.e. alternating deposition of superconducting and ferromagnetic thin films on a substrate, which enables a straight-forward combination of the two types of long-range order and allows the study of how they compete at the interface over nanometer length scales. While originally studies focused on low temperature superconductors interchanged with metallic ferromagnets, in recent years the scope has broadened to include superlattices of high T{sub c} superconductors and colossal magnetoresistance oxides. Creating films where both the superconducting as well as the ferromagnetic layers are complex oxide materials with similar crystal structures (Figure 1), allows the creation of epitaxial superlattices, with potentially atomically flat and ordered interfaces.

Periodic vortex pinning by regular structures in Nb thin films: magnetic vs. structural effects

Science.gov (United States)

Montero, Maria Isabel; Jonsson-Akerman, B. Johan; Schuller, Ivan K.

2001-03-01

The defects present in a superconducting material can lead to a great variety of static and dynamic vortex phases. In particular, the interaction of the vortex lattice with regular arrays of pinning centers such as holes or magnetic dots gives rise to commensurability effects. These commensurability effects can be observed in the magnetoresistance and in the critical current dependence with the applied field. In recent years, experimental results have shown that there is a dependence of the periodic pinning effect on the properties of the vortex lattice (i.e. vortex-vortex interactions, elastic energy and vortex velocity) and also on the dots characteristics (i.e. dot size, distance between dots, magnetic character of the dot material, etc). However, there is not still a good understanding of the nature of the main pinning mechanisms by the magnetic dots. To clarify this important issue, we have studied and compared the periodic pinning effects in Nb films with rectangular arrays of Ni, Co and Fe dots, as well as the pinning effects in a Nb film deposited on a hole patterned substrate without any magnetic material. We will discuss the differences on pinning energies arising from magnetic effects as compared to structural effects of the superconducting film. This work was supported by NSF and DOE. M.I. Montero acknowledges postdoctoral fellowship by the Secretaria de Estado de Educacion y Universidades (Spain).

Far-infrared electrodynamics of thin superconducting NbN film in magnetic fields

Czech Academy of Sciences Publication Activity Database

Šindler, Michal; Tesař, Roman; Koláček, Jan; Szabó, P.; Samuely, P.; Hašková, V.; Kadlec, Christelle; Kadlec, Filip; Kužel, Petr

2014-01-01

Roč. 27, č. 5 (2014), 1-8 ISSN 0953-2048 R&D Projects: GA ČR(CZ) GAP204/11/0015; GA MŠk(CZ) LD14060 Institutional support: RVO:68378271 Keywords : superconductivity * thin films * scanning tunneling spectroscopy * time-domain terahertz spectroscopy Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.325, year: 2014

Ion implantation in superconducting niobium and Nb3 Sn thin films: adjustment of Josephson microbridges and SQUID devices

International Nuclear Information System (INIS)

Robic, J.Y.; Piaguet, J.; Duret, D.; Veler, J.C.; Veran, J.L.; Zenatti, D.

1978-01-01

The principles of operation of Josephson junctions and SQUIDS are resumed. An ion implantation technique for the adjustment of the critical current is presented. High quality superconducting thin films were obtained by electron gun evaporation of niobium on heated substrates. Polycrystalline Nb 3 Sn was made by annealing (1000 K, 10 -6 Torr) a multilayer structure of successively evaporated niobium and thin films. Selected ions (helium, neon, argon) were implanted at doses ranging from 10 13 to 10 17 cm -2 . After implantation the critical temperature, the critical current and the normal resistivity were measured on special photoetched geometries. The variations of these electrical properties depend on the nuclear energy loss. The critical temperature of Nb 3 Sn is decreased by ion implantation and can be increased again by a new annealing. The parameters of the ion implantation were defined in order to obtain a critical temperature slightly higher than the operating temperature. The geometries of the microbridges and the implanted areas where then chosen to obtain appropriate criticals currents (approximately 10 μA) at the operating temperature. The obtained microbridges were used as junction elements in superconducting quantum interference devices (SQUID)

Superconductivity

International Nuclear Information System (INIS)

2007-01-01

During 2007, a large amount of the work was centred on the ITER project and related tasks. The activities based on low-temperature superconducting (LTS) materials included the manufacture and qualification of ITER full-size conductors under relevant operating conditions, the design of conductors and magnets for the JT-60SA tokamak and the manufacture of the conductors for the European dipole facility. A preliminary study was also performed to develop a new test facility at ENEA in order to test long-length ITER or DEMO full-size conductors. Several studies on different superconducting materials were also started to create a more complete database of superconductor properties, and also for use in magnet design. In this context, an extensive measurement campaign on transport and magnetic properties was carried out on commercially available NbTi strands. Work was started on characterising MgB 2 wire and bulk samples to optimise their performance. In addition, an intense experimental study was started to clarify the effect of mechanical loads on the transport properties of multi-filamentary Nb 3 Sn strands with twisted or untwisted superconducting filaments. The experimental activity on high-temperature superconducting (HTS) materials was mainly focussed on the development and characterisation of YBa 2 Cu 3 O 7-X (YBCO) based coated conductors. Several characteristics regarding YBCO deposition, current transport performance and tape manufacture were investigated. In the framework of chemical approaches for YBCO film growth, a new method, developed in collaboration with the Technical University of Cluj-Napoca (TUCN), Romania, was studied to obtain YBCO film via chemical solution deposition, which modifies the well-assessed metallic organic deposition trifluoroacetate (MOD-TFA) approach. The results are promising in terms of critical current and film thickness values. YBCO properties in films with artificially added pinning sites were characterised in collaboration with

Practical considerations in the design and operation of superconducting structures

International Nuclear Information System (INIS)

Schwettman, H.A.

1975-01-01

During the past few years, considerable experience has been gained in the operation of prototype superconducting accelerators under beam line conditions. As a result of this experience, important aspects of structure design and important questions related to the long term operation of superconducting structures have been brought into sharper focus. For applications where low power loss and high duty factor, or exceptional beam quality and stable operation, are essential properties, and where modest energy gradients can be tolerated, superconducting structures are distinctly superior to conventional room temperature structures. (auth)

Fluctuation conductivity of thin superconductive vanadium films

International Nuclear Information System (INIS)

Dmitrenko, I.M.; Sidorenko, A.S.; Fogel, N.Y.

1982-01-01

Resistive transitions into the superconductive state are studied in thin [d >T/sub c/ the experimental data on the excess conductivity of the films agree qualitatively and quantitively with Aslamazov--Larkin theory. There is no Maki--Thompson contribution to fluctuation conductivity. Near T/sub c/ the excess conductivity sigma' changes exponentially with temperature in accordance with the predictions of the theory of the critical fluctuations of the order parameter. The values of the effective charge carrier mass defined from data on sigma' for the low fluctuation and critical fluctuation regions differ markedly. This difference is within the spread of effective masses for various charge carrier groups already known for vanadium. Causes of the difference in resistive behavior for the regions T >T/sub c/ are considered

Ginzburg-Landau theory and the superconducting transition in thin, amorphous bismuth films

International Nuclear Information System (INIS)

Van Vechten, D.

1979-01-01

The Aslamasov-Larkin (AL) theory can be derived from a classical treatment of the conductivity due to short-lived statistical fluctuations into the superconducting state if one truncates the Ginzburg-Landau free energy density expression to read F[psi] = α 0 vertical barpsi vertical bar 2 + c 0 vertical bar del psi vertical bar 2 , where psi is the superconducting order parameter. The next largest term in the GL free energy is (b/2) (vertical bar psi vertical bar 2 ) 2 and is conventionally interpreted as representing the energy associated with interactions between the fluctuations. My dissertation consists of the calculation of the effect of this term on the fluctuation conductivity in three different approximations and the comparison of my predictions to the data of R.E. Glover III and M.K. Chien on thin amorphous bismuth films. The first approximation calculates the contribution to the fluctuations' self energy of the ''tadpole'' diagrams. This approximation yields a 4 parameter equation. Its fits were particularly outstanding for the films deposited on quartz or roughened glass substrates and only for two smooth glass substrates were there non-isolated data points that were not fit at the lowest temperatures measured. (The equation runs into trouble for these films at approximately R(T)/R/sub o/ =.08.) The values of the theoretical equation's fitting parameters were determined by a least squares method and turns out to depend on film thickness in the manner predicted by the theory. The next calculation improves the self energy approximation by including all the ''ring'' diagrams

Effect of residual gas on structural, electrical and mechanical properties of niobium films deposited by magnetron sputtering deposition

Science.gov (United States)

Wang, Lanruo; Zhong, Yuan; Li, Jinjin; Cao, Wenhui; Zhong, Qing; Wang, Xueshen; Li, Xu

2018-04-01

Magnetron sputtering is an important method in the superconducting thin films deposition. The residual gas inside the vacuum chamber will directly affect the quality of the superconducting films. In this paper, niobium films are deposited by magnetron sputtering under different chamber residual gas conditions. The influence of baking and sputtering process on residual gas are studied as well. Surface morphology, electrical and mechanical properties of the films are analysed. The residual gas analysis result before the sputtering process could be regarded as a reference condition to achieve high quality superconducting thin films.

Magnetic tunable confinement of the superconducting condensate in superconductor/ferromagnet hybrids

International Nuclear Information System (INIS)

Aladyshkin, A.Yu.; Gillijns, W.; Silhanek, A.V.; Moshchalkov, V.V.

2008-01-01

The effect of a nonuniform magnetic field induced by a ferromagnet on the magnetoresistance of thin-film superconductor/ferromagnet hybrid structures was investigated experimentally. Two different magnetic textures with out-of-plane magnetization were considered: a plain ferromagnetic film with bubble domains and a regular array of ferromagnetic dots. The stray fields of the structures are able to affect the spatial profile of the superconducting condensate, leading to a modification of the dependence of the critical temperature T c on an external magnetic field H. We showed how the standard linear T c (H) dependence with a single maximum at H=0 can be continuously transformed into so-called reentrant phase boundary with two T c peaks. We demonstrated that both domain-wall superconductivity and field-induced superconductivity are different manifestations of the magnetic confinement effect in various magnetic patterns

Structural safety features for superconducting magnets

International Nuclear Information System (INIS)

Lehner, J.; Reich, M.; Powell, J.; Bezler, P.; Gardner, D.; Yu, W.; Chang, T.Y.

1975-01-01

A survey has been carried out for various potential structural safety problems of superconducting fusion magnets. These areas include: (1) Stresses due to inhomogeneous temperature distributions in magnets where normal regions have been initiated. (2) Stress distributions and yield forces due to cracks and failed regions. (3) Superconducting magnet response due to seismic excitation. These analyses have been carried out using a variety of large capacity finite element computer codes that allow for the evaluation of stresses in elastic or elastic-plastic zones and around singularities in the magnet structure. Thus far, these analyses have been carried out on UWMAK-I type magnet systems

Enhanced physicochemical properties of polydimethylsiloxane based microfluidic devices and thin films by incorporating synthetic micro-diamond.

Science.gov (United States)

Waheed, Sidra; Cabot, Joan M; Macdonald, Niall P; Kalsoom, Umme; Farajikhah, Syamak; Innis, Peter C; Nesterenko, Pavel N; Lewis, Trevor W; Breadmore, Michael C; Paull, Brett

2017-11-08

Synthetic micro-diamond-polydimethylsiloxane (PDMS) composite microfluidic chips and thin films were produced using indirect 3D printing and spin coating fabrication techniques. Microfluidic chips containing up to 60 wt% micro-diamond were successfully cast and bonded. Physicochemical properties, including the dispersion pattern, hydrophobicity, chemical structure, elasticity and thermal characteristics of both chip and films were investigated. Scanning electron microscopy indicated that the micro-diamond particles were embedded and interconnected within the bulk material of the cast microfluidic chip, whereas in the case of thin films their increased presence at the polymer surface resulted in a reduced hydrophobicity of the composite. The elastic modulus increased from 1.28 for a PDMS control, to 4.42 MPa for the 60 wt% composite, along with a three-fold increase in thermal conductivity, from 0.15 to 0.45 W m -1 K -1 . Within the fluidic chips, micro-diamond incorporation enhanced heat dissipation by efficient transfer of heat from within the channels to the surrounding substrate. At a flow rate of 1000 μL/min, the gradient achieved for the 60 wt% composite chip equalled a 9.8 °C drop across a 3 cm long channel, more than twice that observed with the PDMS control chip.

Development of Strontium Titanate Thin films on Technical Substrates for Superconducting Coated Conductors

DEFF Research Database (Denmark)

Pallewatta, Pallewatta G A P; Yue, Zhao; Grivel, Jean-Claude

2012-01-01

SrTiO3 is a widely studied perovskite material due to its advantages as a template for high temperature superconducting tapes. Heteroepitaxial SrTiO3 thin films were deposited on Ni/W tapes using dip-coating in a precursor solution followed by drying and annealing under reducing conditions. Nearl...

Micro-strain, dislocation density and surface chemical state analysis of multication thin films

Energy Technology Data Exchange (ETDEWEB)

Jayaram, P., E-mail: jayarampnair@gmail.com [Department of Physics, MES Ponnani College Ponnani, Kerala (India); Pradyumnan, P.P. [Department of Physics, University of Calicut, Kerala 673 635 (India); Karazhanov, S.Zh. [Department for Solar Energy, Institute for Energy Technology, Kjeller (Norway)

2016-11-15

Multication complex metal oxide thin films are rapidly expanding the class of materials with many technologically important applications. Herein this work, the surface of the pulsed laser deposited thin films of Zn{sub 2}SnO{sub 4} and multinary compounds obtained by substitution/co-substitution of Sn{sup 4+} with In{sup 3+} and Ga{sup 3+} are studied by X-ray photoelectron emission spectroscopy (X-PES) method. Peaks corresponding to the elements of Zn, Sn, Ga, In and O on the film surface has been identified and contribution of the elements has been studied by the computer aided surface analysis (CASA) software. Binding energies, full-width at half maximum (FWHM), spin-orbit splitting energies, asymmetric peak-shape fitting parameters and quantification of elements in the films are discussed. Studies of structural properties of the films by x-ray diffraction (XRD) technique showed inverse spinel type lattice with preferential orientation. Micro-strain, dislocation density and crystallite sizes in the film surface have been estimated.

Contribution of nuclear microanalysis and of 18O tracer technique to study the oxygen sublattice in high Tc superconducting thin films

International Nuclear Information System (INIS)

Siejka, J.

1994-01-01

At first a short review of IBA contribution to the determination of composition and structure, including phonon properties of high T c superconducting oxides is presented. In the second part, IBA contribution to the elucidation of the mechanisms of thin film growth is presented. The emphasis is on the complementarity of IBA, Raman spectroscopy and XRD techniques to characterize thin films of high T c superconducting oxides. In the third part, some recent results related mainly to YBaCuO films grown on (100) oriented single crystalline bulk materials (MgO, LaAlO 3 , SrTiO 3 ) is discussed. In these experiments, IBA, XRD and Raman spectroscopies were used to study the oxygen content in a series of YBaCuO films prepared in different conditions of pressure and temperature. In the case of c-axis oriented films a good agreement between these three methods was found for the films cooled down at high oxygen pressure and a significant disagreement for the films cooled down at low oxygen pressure, showing structures with anomalous c-axis parameter. In the case of a-axis oriented films grown on SrTiO 3 substrates it was found that the low T c values (∼ 70-80 K) are not correlated with the oxygen content but rather with a disorder in the oxygen sublattice. The disorder in the oxygen sublattice was studied using the 16 O(α, α) 16 O resonance in random and channeling geometry. These results are correlated with the data provided by Raman spectroscopy. The 18 O tracer technique was used to estimate the diffusion coefficient in the a-axis oriented YBaCuO films showing a huge anisotropy of the 18 O labelling. Combining Raman and IBA techniques, the selective 18 O labelling of the CuO chain-planes was evidenced. The defects in the 18 O enriched CuO chain-planes were studied using the 18 O(p, α) 15 N nuclear resonant reaction in random and channeling geometries. Some preliminary results related to roughness of YBaCuO films are also discussed. The physical implications of these

Molybdenum Nitride Films: Crystal Structures, Synthesis, Mechanical, Electrical and Some Other Properties

Directory of Open Access Journals (Sweden)

Isabelle Jauberteau

2015-10-01

Full Text Available Among transition metal nitrides, molybdenum nitrides have been much less studied even though their mechanical properties as well as their electrical and catalytic properties make them very attractive for many applications. The δ-MoN phase of hexagonal structure is a potential candidate for an ultra-incompressible and hard material and can be compared with c-BN and diamond. The predicted superconducting temperature of the metastable MoN phase of NaCl-B1-type cubic structure is the highest of all refractory carbides and nitrides. The composition of molybdenum nitride films as well as the structures and properties depend on the parameters of the process used to deposit the films. They are also strongly correlated to the electronic structure and chemical bonding. An unusual mixture of metallic, covalent and ionic bonding is found in the stoichiometric compounds.

Interface-enhanced high-temperature superconductivity in single-unit-cell FeT e1 -xS ex films on SrTi O3

Science.gov (United States)

Li, Fangsen; Ding, Hao; Tang, Chenjia; Peng, Junping; Zhang, Qinghua; Zhang, Wenhao; Zhou, Guanyu; Zhang, Ding; Song, Can-Li; He, Ke; Ji, Shuaihua; Chen, Xi; Gu, Lin; Wang, Lili; Ma, Xu-Cun; Xue, Qi-Kun

2015-06-01

Recently discovered high-temperature superconductivity in single-unit-cell (UC) FeSe films on SrTi O3 (STO) substrate has stimulated tremendous research interest, both experimental and theoretical. Whether this scenario could be extended to other superconductors is vital in both identifying the enhanced superconductivity mechanism and further raising the critical transition temperature (Tc). Here we successfully prepared single-UC FeT e1 -xS ex(0.1 ≤x ≤0.6 ) films on STO substrates by molecular beam epitaxy and observed U -shaped superconducting gaps (Δ ) up to ˜16.5 meV , nearly ten times the gap value (Δ ˜1.7 meV ) of the optimally doped bulk FeT e0 .6S e0 .4 single crystal (Tc˜14.5 K ). No superconducting gap has been observed on the second UC and thicker FeT e1 -xS ex films at 5.7 K, indicating the important role of the interface. This interface-enhanced high-temperature superconductivity is further confirmed by ex situ transport measurements, which revealed an onset superconducting transition temperature above 40 K, nearly two times higher than that of the optimally doped bulk FeT e0 .6S e0 .4 single crystal. This work demonstrates that interface engineering is a feasible way to discover alternative superconductors with higher Tc.

Optically activated high Tc superconducting microbolometer

International Nuclear Information System (INIS)

Yefremenko, V; Gordiyenko, E; Shustakova, G; Bader, S D; Karapetrov, G; Novosad, V

2006-01-01

A laser beam, precisely focused on the patterned superconducting structure, was used to nucleate a resistive area that is sensitive to external thermal effects. The electron beam lithography and wet chemical etching were applied as pattern transfer processes in epitaxial Y-Ba-Cu-O films. Two different sensor designs were tested: (i) 3 millimeters long and 40 micrometers wide stripe and (ii) 1.25 millimeters long, and 50 micron wide meander -like structure. It is shown experimentally that scanning the laser beam along the stripe leads to physical displacement of the sensitive area and, therefore may be used as a basis for imaging over a broad spectral range. For example, patterning the superconducting film into a meander structure is equivalent to a two-dimensional detector array. In additional to the simplicity of the detector fabrication sequence (one step mask transfer), a clear advantage of this approach is the simplicity of the read-out process: an image is formed by registering the signal with only two electrical terminals. The proposed approach can be extended for imaging over a wide spectral range

Superconductivity in Mesocrystalline Inverse Opal Structures

Science.gov (United States)

Lungu, Anca; Bleiweiss, Michael; Saygi, Salih; Amirzadeh, Jafar; Datta, Timir

2000-03-01

Mesocrystalline inverse opal structures were fabricated by the electrodeposition of metallic lead in synthetic opals. In these structures, the superconducting regions percolate in all directions through the voids in the artificial opals and their size is comparable to the coherence length for bulk lead. The inverse lead opals were proven superconducting, with a transition temperature close to that of bulk lead (between 7.2 K and 7.36 K) and broad transition regions. The magnetic behavior of the inverse opals was very different from that of bulk lead. Due to the reduced dimensonality of the superconducting regions, not surprisingly, the magnetic properties of our samples were found to be similar to those of type II superconductors. The critical magnetic field (or the field at which T_copals was proven at least two times larger than that for bulk lead and (dT_c/dH) was observed 2.7 times smaller. We found a reversible ZFC-FC magnetic behavior in the temperature range between T* and T_c. We also performed magnetic relaxation measurements and studied the fluctuation diamagnetism above T_c.

STRUCTURING OF DIAMOND FILMS USING MICROSPHERE LITHOGRAPHY

Directory of Open Access Journals (Sweden)

Mária Domonkos

2014-10-01

Full Text Available In this study, the structuring of micro- and nanocrystalline diamond thin films is demonstrated. The structuring of the diamond films is performed using the technique of microsphere lithography followed by reactive ion etching. Specifically, this paper presents a four-step fabrication process: diamond deposition (microwave plasma assisted chemical vapor deposition, mask preparation (by the standard Langmuir-Blodgett method, mask modification and diamond etching. A self-assembled monolayer of monodisperse polystyrene (PS microspheres with close-packed ordering is used as the primary template. Then the PS microspheres and the diamond films are processed in capacitively coupled radiofrequency plasma  using different plasma chemistries. This fabrication method illustrates the preparation of large arrays of periodic and homogeneous hillock-like structures. The surface morphology of processed diamond films is characterized by scanning electron microscopy and atomic force microscope. The potential applications of such diamond structures in various fields of nanotechnology are also briefly discussed.

Specific feature of critical fields of inhomogeneous superconducting films

International Nuclear Information System (INIS)

Glazman, L.I.; Dmitrenko, I.M.; Kolin'ko, A.E.; Pokhila, A.S.; Fogel', N.Ya.; Cherkasova, V.G.

1988-01-01

Experimental studies on thin vanadium films (d=250-400 A) have revealed anomaly in the temperature dependence of the upper critical field H cparallel (T), when H is parallel to the sample plane. At certain temperature T 0 the dependence H cparallel 2 (T) has a sharp kink separating two linear portions. The anomalous behaviour of H cparallel (T) of thin V films can be accounted for assuming the film separation into two parallel layers having different parameters (critical temperature T c , coherence length ξ, thickness d). At temperatures above and lower T 0 the dependence H cparallel (T) is mainly dependent on the characteristics of only one layer. The kink in the dependence H cparallel 2 (T) is due to a jump-like transition of the superconducting nucleus from one layer to the other at T c . The anomalous behaviour of the dependence H cparallel (T) is also observed in sandwiches consisting of two identical films separated with a high (about 30 A) dielectric interlayer; however, the transition from one linear portion to the other is smooth. In the case of identical films a specific crossover occurs if at T-T c the critical field H cparallel (T) coinsides with that for the layer of doubled thickness, then at lowering temperature H cparallel (T) asymptotically approaches the critical field of one layer. The calculation within the model described provides a good description for the experimental results

Periodic arrays of pinning centers in thin vanadium films.

Energy Technology Data Exchange (ETDEWEB)

Brueck, S. R. J.; Chung, K.; Crabtree, G.; DeLong, L. E.; Hesketh, P. J.; Ilic, B.; Metlushko, V.; Watkins, B.; Welp, U.; Zhang, Z.

1997-07-13

Commensurability effects between the superconducting flux line lattice and a square lattice (period d=1{micro}m and diameter D=0.4{micro}m) of submicron holes in 1500 {angstrom} vanadium films were studied by atomic force microscopy, DC magnetization, AC susceptibility, magnetoresistivity and I-V measurements. Peaks in the magnetization and critical current at matching fields are found to depend nonlinearly upon the value of external AC field or current, as well as the inferred symmetry of the flux line lattice.

Quantification of oxygen and carbon in high Tc superconducting films by (α,α) elastic resonance technique

International Nuclear Information System (INIS)

Vizkelethy, G.; Revesz, P.

1993-01-01

The quantification of oxygen and carbon in high-temperature (T c ) superconducting oxide thin films was made by employing elastic resonance in He backscattering analysis. A method combining the oxygen resonance technique and channeling was presented for measuring the nature of the oxygen disorder near the surface and the interface in a YBCO superconducting film grown on an MgO substrate. The oxygen resonance technique was used to quantify the oxygen profiling in the metal/YBCO contacts, showing that Zr and Nb act as sinks to oxygen from YBCO films and are oxidized in the forms Zr/ZrO 2 /YBCO/MgO and Nb 0.2 O/YBCO/MgO after annealing in a vacuum at 350 o C. We combined the carbon and oxygen resonances to determine the carbon contamination and oxygen concentration changes on the YBCO surface after coating and baking the photoresist. Residual carbon on the surface and a thin layer of oxygen depletion near the YBCO surface have been observed. The residual carbon in Bi 2 Sr 2 CaCu 2 O 8 films made by the decomposition of metallo-organic precursors was quantified using carbon resonance. (author)

Enhanced flux pinning properties in superconducting YBa2Cu3O7−z films by a novel chemical doping approach

International Nuclear Information System (INIS)

Wang, W.T.; Pu, M.H.; Lei, M.; Zhang, H.; Wang, Z.; Zhang, H.; Cheng, C.H.; Zhao, Y.

2013-01-01

Highlights: • Pure and Co-doped YBCO films were prepared by newly-developed chemical method. • The doped films have much denser and smoother surface microstructures. • Significantly enhanced fux-pinning properties have been obtained for dilute Co-doped flm. -- Abstract: Pure and cobalt-doped superconducting YBa 2 Cu 3 O 7−z (YBCO) films were prepared on (0 0 l) LaAlO 3 substrate by a newly developed polymer-assisted metal organic deposition method. The cobalt-doped YBCO films display much denser and smoother surface microstructures and the superconducting transition temperature T c spans a small range of 1.7 K with the doping levels. Significantly enhanced flux-pinning properties have been obtained for dilute cobalt-doped film. This may be attributed to the good grain connections and the effective flux pinning centers introduced by cobalt doping

Influence of substrate type on transport properties of superconducting FeSe0.5Te0.5 thin films

International Nuclear Information System (INIS)

Yuan, Feifei; Shi, Zhixiang; Iida, Kazumasa; Langer, Marco; Hänisch, Jens; Hühne, Ruben; Schultz, Ludwig; Ichinose, Ataru; Tsukada, Ichiro; Sala, Alberto; Putti, Marina

2015-01-01

FeSe 0.5 Te 0.5 thin films were grown by pulsed laser deposition on CaF 2 , LaAlO 3 and MgO substrates and structurally and electro-magnetically characterized in order to study the influence of the substrate on their transport properties. The in-plane lattice mismatch between FeSe 0.5 Te 0.5 bulk and the substrate shows no influence on the lattice parameters of the films, whereas the type of substrate affects the crystalline quality of the films and, therefore, the superconducting properties. The film on MgO showed an extra peak in the angular dependence of critical current density J c (θ) at θ = 180° (H||c), which arises from c-axis defects as confirmed by transmission electron microscopy. In contrast, no J c (θ) peaks for H||c were observed in films on CaF 2 and LaAlO 3 . J c (θ) can be scaled successfully for both films without c-axis correlated defects by the anisotropic Ginzburg–Landau approach with appropriate anisotropy ratio γ J . The scaling parameter γ J is decreasing with decreasing temperature, which is different from what we observed in FeSe 0.5 Te 0.5 films on Fe-buffered MgO substrates. (paper)

Machine Vision based Micro-crack Inspection in Thin-film Solar Cell Panel

Directory of Open Access Journals (Sweden)

Zhang Yinong

2014-09-01

Full Text Available Thin film solar cell consists of various layers so the surface of solar cell shows heterogeneous textures. Because of this property the visual inspection of micro-crack is very difficult. In this paper, we propose the machine vision-based micro-crack detection scheme for thin film solar cell panel. In the proposed method, the crack edge detection is based on the application of diagonal-kernel and cross-kernel in parallel. Experimental results show that the proposed method has better performance of micro-crack detection than conventional anisotropic model based methods on a cross- kernel.

Ga lithography in sputtered niobium for superconductive micro and nanowires

International Nuclear Information System (INIS)

Henry, M. David; Wolfley, Steve; Monson, Todd; Lewis, Rupert

2014-01-01

This work demonstrates the use of focused ion beam (FIB) implanted Ga as a lithographic mask for plasma etching of Nb films. Using a highly collimated Ga beam of a FIB, Nb is implanted 12 nm deep with a 14 nm thick Ga layer providing etch selectivity better than 15:1 with fluorine based etch chemistry. Implanted square test patterns, both 10 μm by 10 μm and 100 μm by 100 μm, demonstrate that doses above than 7.5 × 10 15  cm −2 at 30 kV provide adequate mask protection for a 205 nm thick, sputtered Nb film. The resolution of this dry lithographic technique is demonstrated by fabrication of nanowires 75 nm wide by 10 μm long connected to 50 μm wide contact pads. The residual resistance ratio of patterned Nb films was 3. The superconducting transition temperature (T c ) = 7.7 K was measured using a magnetic properties measurement system. This nanoscale, dry lithographic technique was extended to sputtered TiN and Ta here and could be used on other fluorine etched superconductors such as NbN, NbSi, and NbTi.

Characterization of 3-dimensional superconductive thin film components for gravitational experiments in space

Energy Technology Data Exchange (ETDEWEB)

Hechler, S.; Nawrodt, R.; Nietzsche, S.; Vodel, W.; Seidel, P. [Friedrich-Schiller-Univ. Jena (Germany). Inst. fuer Festkoerperphysik; Dittus, H. [ZARM, Univ. Bremen (Germany); Loeffler, F. [Physikalisch-Technische Bundesanstalt, Braunschweig (Germany)

2007-07-01

Superconducting quantum interference devices (SQUIDs) are used for high precise gravitational experiments. One of the most impressive experiments is the satellite test of the equivalence principle (STEP) of NASA/ESA. The STEP mission aims to prove a possible violation of Einstein's equivalence principle at an extreme level of accuracy of 1 part in 10{sup 18} in space. In this contribution we present an automatically working measurement equipment to characterize 3-dimensional superconducting thin film components like i.e. pick-up coils and test masses for STEP. The characterization is done by measurements of the transition temperature between the normal and the superconducting state using a special built anti-cryostat. Above all the setup was designed for use in normal LHe transport Dewars. The sample chamber has a volume of 150 cm{sup 3} and can be fully temperature controlled over a range from 4.2 K to 300 K with a resolution of better then 100 mK. (orig.)

Plasma assisted fabrication of multi-layer graphene/nickel hybrid film as enhanced micro-supercapacitor electrodes

Science.gov (United States)

Ding, Q.; Li, W. L.; Zhao, W. L.; Wang, J. Y.; Xing, Y. P.; Li, X.; Xue, T.; Qi, W.; Zhang, K. L.; Yang, Z. C.; Zhao, J. S.

2017-03-01

A facile synthesis strategy has been developed for fabricating multi-layer graphene/nickel hybrid film as micro-supercapacitor electrodes by using plasma enhanced chemical vapor deposition. The as-presented method is advantageous for rapid graphene growth at relatively low temperature of 650 °C. In addition, after pre-treating for the as-deposited nickel film by using argon plasma bombardment, the surface-to-volume ratio of graphene film on the treated nickel substrate is effectively increased by the increasing of surface roughness. This is demonstrated by the characterization results from transmission electron microscopy, scanning electron microscope and atomic force microscopy. Moreover, the electrochemical performance of the resultant graphene/nickel hybrid film as micro-supercapacitor working electrode was investigated by cyclic voltammetry and galvanostatic charge/discharge measurements. It was found that the increase of the surface-to-volume ratio of graphene/nickel hybrid film improved the specific capacitance of 10 times as the working electrode of micro-supercapacitor. Finally, by using comb columnar shadow mask pattern, the micro-supercapacitor full cell device was fabricated. The electrochemical performance measurements of the micro-supercapacitor devices indicate that the method presented in this study provides an effective way to fabricate micro-supercapacitor device with enhanced energy storage property.

Full-switching FSF-type superconducting spin-triplet magnetic random access memory element

Science.gov (United States)

Lenk, D.; Morari, R.; Zdravkov, V. I.; Ullrich, A.; Khaydukov, Yu.; Obermeier, G.; Müller, C.; Sidorenko, A. S.; von Nidda, H.-A. Krug; Horn, S.; Tagirov, L. R.; Tidecks, R.

2017-11-01

In the present work a superconducting Co/CoOx/Cu41Ni59 /Nb/Cu41Ni59 nanoscale thin film heterostructure is investigated, which exhibits a superconducting transition temperature, Tc, depending on the history of magnetic field applied parallel to the film plane. In more detail, around zero applied field, Tc is lower when the field is changed from negative to positive polarity (with respect to the cooling field), compared to the opposite case. We interpret this finding as the result of the generation of the odd-in-frequency triplet component of superconductivity arising at noncollinear orientation of the magnetizations in the Cu41Ni59 layer adjacent to the CoOx layer. This interpretation is supported by superconducting quantum interference device magnetometry, which revealed a correlation between details of the magnetic structure and the observed superconducting spin-valve effects. Readout of information is possible at zero applied field and, thus, no permanent field is required to stabilize both states. Consequently, this system represents a superconducting magnetic random access memory element for superconducting electronics. By applying increased transport currents, the system can be driven to the full switching mode between the completely superconducting and the normal state.

Processing of La/sub 1.8/Sr/sub 0.2/CuO4 and YBa2Cu3O7 superconducting thin films by dual-ion-beam sputtering

International Nuclear Information System (INIS)

Madakson, P.; Cuomo, J.J.; Yee, D.S.; Roy, R.A.; Scilla, G.

1988-01-01

High quality La/sub 1.8/Sr/sub 0.2/CuO 4 and YBa 2 Cu 3 O 7 superconducting thin films, with zero resistance at 88 K, have been made by dual-ion-beam sputtering of metal and oxide targets at elevated temperatures. The films are about 1.0 μm thick and are single phase after annealing. The substrates investigated are Nd-YAP, MgO, SrF 2 , Si, CaF 2 , ZrO 2 -9% Y 2 O 3 , BaF 2 , Al 2 O 3 , and SrTiO 3 . Characterization of the films was carried out using Rutherford backscattering spectroscopy, resistivity measurements, transmission electron microscopy, x-ray diffraction, and secondary ion mass spectroscopy. Substrate/film interaction was observed in every case. This generally involves diffusion of the substrate into the film, which is accompanied by, for example, the replacement of Ba by Sr in the YBa 2 Cu 2 O 7 structure, in the case of SrTiO 3 substrate. The best substrates were those that did not significantly diffuse into the film and which did not react chemically with the film. In general, the superconducting transition temperature is found to depend on substrate temperature and ion beam energy, film composition, annealing conditions, and the nature and the magnitude of the substrate/film interaction

Stationary states and dynamics of superconducting thin films

DEFF Research Database (Denmark)

Ögren, Magnus; Sørensen, Mads Peter; Pedersen, Niels Falsig

can handle complex geometries also in a three-dimensional superconducting structure. To include external currents in our modelling we discuss the role of the boundary conditions for the external magnetic field [4]. Finally we show results for the pinning of vortices with controlled impurities....

Thin film metrology and microwave loss characterization of indium and aluminum/indium superconducting planar resonators

Science.gov (United States)

McRae, C. R. H.; Béjanin, J. H.; Earnest, C. T.; McConkey, T. G.; Rinehart, J. R.; Deimert, C.; Thomas, J. P.; Wasilewski, Z. R.; Mariantoni, M.

2018-05-01

Scalable architectures characterized by quantum bits (qubits) with low error rates are essential to the development of a practical quantum computer. In the superconducting quantum computing implementation, understanding and minimizing material losses are crucial to the improvement of qubit performance. A new material that has recently received particular attention is indium, a low-temperature superconductor that can be used to bond pairs of chips containing standard aluminum-based qubit circuitry. In this work, we characterize microwave loss in indium and aluminum/indium thin films on silicon substrates by measuring superconducting coplanar waveguide resonators and estimating the main loss parameters at powers down to the sub-photon regime and at temperatures between 10 and 450 mK. We compare films deposited by thermal evaporation, sputtering, and molecular beam epitaxy. We study the effects of heating in a vacuum and ambient atmospheric pressure as well as the effects of pre-deposition wafer cleaning using hydrofluoric acid. The microwave measurements are supported by thin film metrology including secondary-ion mass spectrometry. For thermally evaporated and sputtered films, we find that two-level state are the dominant loss mechanism at low photon number and temperature, with a loss tangent due to native indium oxide of ˜ 5 × 10 - 5 . The molecular beam epitaxial films show evidence of the formation of a substantial indium-silicon eutectic layer, which leads to a drastic degradation in resonator performance.

Electro-physical properties of superconducting ceramic thick film prepared by partial melting method.

Science.gov (United States)

Lee, Sang Heon

2013-05-01

BiSrCaCuO superconductor thick films were prepared at several curing temperatures, and their electro-physical properties were determined to find an optimum fabrication conditions. Critical temperatures of the superconductors were decreased with increasing melting temperature, which was related to the amount of equilibrium phases of the superconducting materials with temperature. The critical temperature of BiSrCaCuO bulk and thick film superconductors were 107 K and 96 K, respectively. The variation of susceptibility of the superconductor thick film formed at 950 degrees C had multi-step-type curve for 70 G externally applied field, whereas, a superconductor thick film formed at 885 degrees C had a single step-type curve like a bulk BiSrCaCuO ceramic superconductor in the temperature-susceptibility curves. A partial melting at 865 degrees C is one of optimum conditions for making a superconductor thick film with a relatively homogeneous phase.

Anisotrophic currents and flux jumps in high-T-c superconducting films with self-organized arrays of planar defects

DEFF Research Database (Denmark)

Yurchenko, V.V.; Qviller, A.J.; Mozhaev, P.B.

2010-01-01

Regular arrays of planar defects with a period of a few nanometers can be introduced in superconducting YBa2Cu3O7-delta (YBCO) thin films by depositing them on vicinal (also called miscut or tilted) substrates. This results in the anisotropy of critical currents flowing in the plane of the film. ...

Relationship between nano/micro structure and physical properties of TiO2-sodium caseinate composite films.

Science.gov (United States)

Montes-de-Oca-Ávalos, Juan Manuel; Altamura, Davide; Candal, Roberto Jorge; Scattarella, Francesco; Siliqi, Dritan; Giannini, Cinzia; Herrera, María Lidia

2018-03-01

Films obtained by casting, starting from conventional emulsions (CE), nanoemulsions (NE) or their gels, which led to different structures, with the aim of explore the relationship between structure and physical properties, were prepared. Sodium caseinate was used as the matrix, glycerol as plasticizer, glucono-delta-lactone as acidulant to form the gels, and TiO 2 nanoparticles as reinforcement to improve physical behavior. Structural characterization was performed by SAXS and WAXS (Small and Wide Angle X-ray Scattering, respectively), combined with confocal and scanning electron microscopy. The results demonstrate that the incorporation of the lipid phase does not notably modify the mechanical properties of the films compared to solution films. Films from NE were more stable against oil release than those from CE. Incorporation of TiO 2 improved mechanical properties as measured by dynamical mechanical analysis (DMA) and uniaxial tensile tests. TiO 2 macroscopic spatial distribution homogeneity and the nanostructure character of NE films were confirmed by mapping the q-dependent scattering intensity in scanning SAXS experiments. SAXS microscopies indicated a higher intrinsic homogeneity of NE films compared to CE films, independently of the TiO 2 load. NE-films containing structures with smaller and more homogeneously distributed building blocks showed greater potential for food applications than the films prepared from sodium caseinate solutions, which are the best known films. Copyright © 2017 Elsevier Ltd. All rights reserved.

Anisotropic response of the moving vortex lattice in superconducting Mo(1-x)Gex amorphous films

International Nuclear Information System (INIS)

Dolz, M.I.; Shalóm, D.E.; Pastoriza, H.; López, D.O.

2012-01-01

We have performed magnetic susceptibility measurements in Mo 1-x Ge x amorphous thin films biased with an electrical current using anisotropic coils. We tested the symmetry of the vortex response changing the relative orientation between the bias current and the susceptibility coils. We found a region in the DC current-temperature phase diagram where the dynamical vortex structures behave anisotropically. In this region the shielding capability of the superconducting currents measured by the susceptibility coils is less effective along the direction of vortex motion compared to the transverse direction. This anisotropic response is found in the same region where the peak effect in the critical current is developed. On rising temperature the isotropic behavior is recovered.

Micro-fabrication technology for piezoelectric film formation and its application to MEMS

OpenAIRE

一木, 正聡; 曹, 俊杰; 張, 麓〓; 王, 占杰; 前田, 龍太郎; Masaaki, ICHIKI; Jiunn Jye, TSAUR; Lulu, ZHANG; Zhang Jie, WANG; Ryutaro, MAEDA; 産業技術総合研究所; 産業技術総合研究所; 産業技術総合研究所; 東北大学; 産業技術総合研究所

2005-01-01

Technological problems for realization of Micro Electro-mechanical System (MEMS) are discussed and an introduction of smart materials (PZT) is encouraged. The film formation and micromaching technology are discussed in integration of PZT thin films into MEMS. Further developments are proposed on PZT micro sensors and actuators with special emphasis laid on exploration of new application fields of MEMS, such as scanning mirror. Internal stress is estimated and analyzed for the improvement of d...

Structural characterization of casein micelles: shape changes during film formation

International Nuclear Information System (INIS)

Gebhardt, R; Kulozik, U; Vendrely, C

2011-01-01

The objective of this study was to determine the effect of size-fractionation by centrifugation on the film structure of casein micelles. Fractionated casein micelles in solution were asymmetrically distributed with a small distribution width as measured by dynamic light scattering. Films prepared from the size-fractionated samples showed a smooth surface in optical microscopy images and a homogeneous microstructure in atomic force micrographs. The nano- and microstructure of casein films was probed by micro-beam grazing incidence small angle x-ray scattering (μGISAXS). Compared to the solution measurements, the sizes determined in the film were larger and broadly distributed. The measured GISAXS patterns clearly deviate from those simulated for a sphere and suggest a deformation of the casein micelles in the film. (paper)

Superconducting power distribution structure for integrated circuits

International Nuclear Information System (INIS)

Ruby, R.C.

1991-01-01

This patent describes a superconducting power distribution structure for an integrated circuit. It comprises a first superconducting capacitor plate; a second superconducting capacitor plate provided with electrical isolation means within the second capacitor plate; dielectric means separating the first capacitor plate from the second capacitor plate; first via means coupled at a first end to the first capacitor plate and extending through the dielectric and the electrical isolation means of the second capacitor plate; first contact means coupled to a second end of the first via means; and second contact means coupled to the second capacitor plate such that the first contact means and the second contact means are accessible from the same side of the second capacitor plate

Laser-excited photoemission spectroscopy study of superconducting boron-doped diamond

Directory of Open Access Journals (Sweden)

K. Ishizaka, R. Eguchi, S. Tsuda, T. Kiss, T. Shimojima, T. Yokoya, S. Shin, T. Togashi, S. Watanabe, C.-T. Chen, C.Q. Zhang, Y. Takano, M. Nagao, I. Sakaguchi, T. Takenouchi and H. Kawarada

2006-01-01

Full Text Available We have investigated the low-energy electronic state of boron-doped diamond thin film by the laser-excited photoemission spectroscopy. A clear Fermi-edge is observed for samples doped above the semiconductor–metal boundary, together with the characteristic structures at 150×n meV possibly due to the strong electron–lattice coupling effect. In addition, for the superconducting sample, we observed a shift of the leading edge below Tc indicative of a superconducting gap opening. We discuss the electron–lattice coupling and the superconductivity in doped diamond.

Fabrication of superconducting niobium radio frequency structures

International Nuclear Information System (INIS)

Kirchgessner, J.; Amato, J.; Brawley, J.

1983-01-01

During the last several years a variety of superconducting radio frequency structures have been designed, fabricated and tested. The diverse structures and fabrication techniques are described. This paper is a description of the authors' experiences in this field

Superconducting Bi-Sr-Ca-Cu-O thin films from metallo-organic complexes

International Nuclear Information System (INIS)

Gruber, H.; Krautz, E.; Fritzer, H.P.; Popitsch, A.

1991-01-01

Thin films in the Bi-Sr-Ca-Cu-O system are produced by decomposition of organic precursor compounds containing different metallo-organic complexes. The superconducting phase identified is Bi 2 Sr 2 CaCu 2 O 8+x on (100)-MgO single crystal substrates, polycrystalline Au- and Ag-ribbons and Bi 2 Sr 2 Ca 2 Cu 3 O 10+x on Ag-ribbons. For the 2212-phase a zero resistance temperature of 79 K is found. The 2223-samples on Ag-ribbons show a broad transition at 110 K with a zero resistance at 85 K. SEM and EDX are used for the detection of the microstructure and composition of the prepared films. (orig.)

Depairing critical current achieved in superconducting thin films with through-thickness arrays of artificial pinning centers

International Nuclear Information System (INIS)

Dinner, Rafael B; Wimbush, Stuart C; MacManus-Driscoll, Judith L; Blamire, Mark G; Robinson, Adam P

2011-01-01

Large area arrays of through-thickness nanoscale pores have been milled into superconducting Nb thin films via a process utilizing anodized aluminum oxide thin film templates. These pores act as artificial flux pinning centers, increasing the superconducting critical current, J c , of the Nb films. By optimizing the process conditions including anodization time, pore size and milling time, J c values approaching and in some cases matching the Ginzburg-Landau depairing current of 30 MA cm -2 at 5 K have been achieved-a J c enhancement over as-deposited films of more than 50 times. In the field dependence of J c , a matching field corresponding to the areal pore density has also been clearly observed. The effect of backfilling the pores with magnetic material has then been investigated. While backfilling with Co has been successfully achieved, the effect of the magnetic material on J c has been found to be largely detrimental compared to voids, although a distinct influence of the magnetic material in producing a hysteretic J c versus applied field behavior has been observed. This behavior has been tested for compatibility with currently proposed models of magnetic pinning and found to be most closely explained by a model describing the magnetic attraction between the flux vortices and the magnetic inclusions.

Study of squeeze film damping in a micro-beam resonator based on micro-polar theory

Directory of Open Access Journals (Sweden)

Mina Ghanbari

Full Text Available In this paper, squeeze film damping in a micro-beam resonator based on micro-polar theory has been investigated. The proposed model for this study consists of a clamped-clamped micro-beam bounded between two fixed layers. The gap between the micro-beam and layers is filled with air. As fluid behaves differently in micro scale than macro, the micro-scale fluid field in the gap has been modeled based on micro-polar theory. Equation of motion governing transverse deflection of the micro- beam based on modified couple stress theory and also non-linear Reynolds equation of the fluid field based on micropolar theory have been non-dimensionalized, linearized and solved simultaneously in order to calculate the quality factor of the resonator. The effect of micropolar parameters of air on the quality factor has been investigated. The quality factor of the of the micro-beam resonator for different values of non-dimensionalized length scale of the beam, squeeze number and also non-dimensionalized pressure has been calculated and compared to the obtained values of quality factor based on classical theory.

PZT Thin-Film Micro Probe Device with Dual Top Electrodes

Science.gov (United States)

Luo, Chuan

Lead zirconate titanate (PZT) thin-film actuators have been studied intensively for years because of their potential applications in many fields. In this dissertation, a PZT thin-film micro probe device is designed, fabricated, studied, and proven to be acceptable as an intracochlear acoustic actuator. The micro probe device takes the form of a cantilever with a PZT thin-film diaphragm at the tip of the probe. The tip portion of the probe will be implanted in cochlea later in animal tests to prove its feasibility in hearing rehabilitation. The contribution of the dissertation is three-fold. First, a dual top electrodes design, consisting of a center electrode and an outer electrode, is developed to improve actuation displacement of the PZT thin-film diaphragm. The improvement by the dual top electrodes design is studied via a finite element model. When the dimensions of the dual electrodes are optimized, the displacement of the PZT thin-film diaphragm increases about 30%. A PZT thin-film diaphragm with dual top electrodes is fabricated to prove the concept, and experimental results confirm the predictions from the finite element analyses. Moreover, the dual electrode design can accommodate presence of significant residual stresses in the PZT thin-film diaphragm by changing the phase difference between the two electrodes. Second, a PZT thin-film micro probe device is fabricated and tested. The fabrication process consists of PZT thin-film deposition and deep reactive ion etching (DRIE). The uniqueness of the fabrication process is an automatic dicing mechanism that allows a large number of probes to be released easily from the wafer. Moreover, the fabrication is very efficient, because the DRIE process will form the PZT thin-film diaphragm and the special dicing mechanism simultaneously. After the probes are fabricated, they are tested with various possible implantation depths (i.e., boundary conditions). Experimental results show that future implantation depths

Tunable surface wettability and water adhesion of Sb2S3 micro-/nanorod films

International Nuclear Information System (INIS)

Zhong, Xin; Zhao, Huiping; Yang, Hao; Liu, Yunling; Yan, Guoping; Chen, Rong

2014-01-01

Antimony sulfide (Sb 2 S 3 ) films were successfully prepared by spin coating Sb 2 S 3 micro-/nanorods with different sizes on glass slides, which was synthesized via a facile and rapid microwave irradiation method. The prepared Sb 2 S 3 micro-/nanorods and films were characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM) and water contact angle (CA). The as-prepared Sb 2 S 3 films exhibited different surface wettabilities ranging from superhydrophilicity to superhydrophobicity, which was strongly dependent on the diameter of Sb 2 S 3 micro-/nanorod. Sb 2 S 3 film made by nanorods possessed superhydrophobic surface and high water adhesive property. After surface modification with stearic acid, the superhydrophobic surface exhibited an excellent self-cleaning property owing to its low adhesive force. The clarification of three possible states including Wenzel's state, “Gecko” state and Cassie's state for Sb 2 S 3 film surfaces was also proposed to provide a better understanding of interesting surface phenomena on Sb 2 S 3 films.

Two-dimensional superconducting state of monolayer Pb films grown on GaAs(110) in a strong parallel magnetic field.

Science.gov (United States)

Sekihara, Takayuki; Masutomi, Ryuichi; Okamoto, Tohru

2013-08-02

Two-dimensional (2D) superconductivity was studied by magnetotransport measurements on single-atomic-layer Pb films on a cleaved GaAs(110) surface. The superconducting transition temperature shows only a weak dependence on the parallel magnetic field up to 14T, which is higher than the Pauli paramagnetic limit. Furthermore, the perpendicular-magnetic-field dependence of the sheet resistance is almost independent of the presence of the parallel field component. These results are explained in terms of an inhomogeneous superconducting state predicted for 2D metals with a large Rashba spin splitting.

Frustrated magnetic response of a superconducting Nb film with a square lattice of columnar defects

Energy Technology Data Exchange (ETDEWEB)

Zadorosny, R; Ortiz, W A [Grupo de Supercondutividade e Magnetismo, Departamento de Fisica, Universidade Federal de Sao Carlos, Sao Carlos, SP (Brazil); Lepienski, C M [Universidade Federal do Parana, Departamento de Fisica, Curitiba, PR (Brazil); Patino, E; Blamire, M G [Department of Materials Science, University of Cambridge, Pembroke Street, Cambridge CB2 3QZ (United Kingdom)], E-mail: rafazad@df.ufscar.br

2008-02-01

The magnetic response of a superconducting system presenting a frustrated state is investigated. The system is a superconducting film with mechanically pierced columns, cooled in a field which is then removed. Frustration originates from the competition between return flux of a dipole - created by flux trapped in the empty columns - and flux exclusion by the surrounding superconductor in the Meissner state. The system resolves the incompatibility among conflicting constraints, leading to frustration, by eliminating return flux, which is possibly assimilated by nearby columns, as manifested by a sudden reduction of the magnetic moment on the decreasing field branch of the hysteresis loop.

Frustrated magnetic response of a superconducting Nb film with a square lattice of columnar defects

International Nuclear Information System (INIS)

Zadorosny, R; Ortiz, W A; Lepienski, C M; Patino, E; Blamire, M G

2008-01-01

The magnetic response of a superconducting system presenting a frustrated state is investigated. The system is a superconducting film with mechanically pierced columns, cooled in a field which is then removed. Frustration originates from the competition between return flux of a dipole - created by flux trapped in the empty columns - and flux exclusion by the surrounding superconductor in the Meissner state. The system resolves the incompatibility among conflicting constraints, leading to frustration, by eliminating return flux, which is possibly assimilated by nearby columns, as manifested by a sudden reduction of the magnetic moment on the decreasing field branch of the hysteresis loop

Specific heat measurement set-up for quench condensed thin superconducting films.

Science.gov (United States)

Poran, Shachaf; Molina-Ruiz, Manel; Gérardin, Anne; Frydman, Aviad; Bourgeois, Olivier

2014-05-01

We present a set-up designed for the measurement of specific heat of very thin or ultra-thin quench condensed superconducting films. In an ultra-high vacuum chamber, materials of interest can be thermally evaporated directly on a silicon membrane regulated in temperature from 1.4 K to 10 K. On this membrane, a heater and a thermometer are lithographically fabricated, allowing the measurement of heat capacity of the quench condensed layers. This apparatus permits the simultaneous thermal and electrical characterization of successively deposited layers in situ without exposing the deposited materials to room temperature or atmospheric conditions, both being irreversibly harmful to the samples. This system can be used to study specific heat signatures of phase transitions through the superconductor to insulator transition of quench condensed films.

Growth orientation and superconducting properties of YBa2Cu3O7-δ films prepared by the low-fluorine sol-gel process

International Nuclear Information System (INIS)

Lei Li; Zhao Gaoyang; Xu Hui; Zhao Juanjuan

2010-01-01

YBa 2 Cu 3 O 7-δ (YBCO) films were deposited on (100)-oriented LaAlO 3 (LAO) single crystal substrates by the dip-coating process using low-fluorine solution. Their microstructures were characterized with the aid of X-ray diffractometry, scanning electron microscopy and high-resolution transmission electron microscopy. Their superconducting properties were measured by the standard four-probe method. The experiment results show that the film obtained under high enough humidity conditions exhibits better c-axis texture and superconducting properties than the film under a relatively low humidity conditions. Based on the classical nucleation and chemical reaction thermodynamics theory, the underlying crystalline and growth mechanisms of YBCO films under certain humidity conditions are explained in combination with our experimental results. It is suggested that the unreacted intermediate phases such as BaF 2 and CuO aggregated in the YBCO grain boundary will cause lattice distortion in the YBCO matrix and further induce the formation of a-axis oriented YBCO grains as crystallization proceeds. Therefore, it is believed that the relative content of water vapor within the heat-treatment atmosphere plays quite an important role in the preparation of c-axis oriented YBCO film with good superconducting properties. (semiconductor materials)

Micro-configuration Observation of Porous Bioceramic for Sliding on Intestinal Mucus Film

Institute of Scientific and Technical Information of China (English)

无

2005-01-01

The microstructure of the prepared porous bioceramic material, including surface porosity and apparent contact area with the artificial mucus film are computed and analyzed. The surface micro-configurations of the porous material before and after sliding on the mucus ftlm are observed in 2D and 3 D by digital microscopy. We describe how much mucus enters and stays within different pores, and how the porous material with rough/porous surface contacts with the mucus film ( elastic surface/gel). The presented results illustrate that the material with different porous structure can lead to different mucus suction, surface scraping and changes of contact area and condition during sliding, which will be active for high friction of robotic endoscope with the intestinal wall for intestinal locomotion.

Final report: High current capacity high temperature superconducting film based tape for high field magnets

International Nuclear Information System (INIS)

Ying Xin

2000-01-01

The primary goal of the program was to establish the process parameters for the continuous deposition of high quality, superconducting YBCO films on one meter lengths of buffered RABiTS tape using MOCVD and to characterize the potential utility of the resulting tapes in high field magnet applications

Unconventional superconductivity of the heavy fermion compound UNi2Al3

International Nuclear Information System (INIS)

Zakharov, Andrey

2008-01-01

The heavy fermion compound UNi 2 Al 3 exhibits the coexistence of superconductivity and magnetic order at low temperatures, stimulating speculations about possible exotic Cooper-pairing interaction in this superconductor. However, the preparation of good quality bulk single crystals of UNi 2 Al 3 has proven to be a non-trivial task due to metallurgical problems, which result in the formation of an UAl 2 impurity phase and hence a strongly reduced sample purity. The present work concentrates on the preparation, characterization and electronic properties investigation of UNi 2 Al 3 single crystalline thin film samples. The preparation of thin films was accomplished in a molecular beam epitaxy (MBE) system. (100)-oriented epitaxial thin films of UNi 2 Al 3 were grown on single crystalline YAlO 3 substrates cut in (010)- or (112)-direction. The high crystallographic quality of the samples was proved by several characterisation methods, such as X-ray analysis, RHEED and TEM. To study the magnetic structure of epitaxial thin films resonant magnetic X-ray scattering was employed. The magnetic order of thin the film samples, the formation of magnetic domains with different moment directions, and the magnetic correlation length were discussed. The electronic properties of the UNi 2 Al 3 thin films in the normal and superconducting states were investigated by means of transport measurements. A pronounced anisotropy of the temperature dependent resistivity ρ(T) was observed. Moreover, it was found that the temperature of the resistive superconducting transition depends on the current direction, providing evidence for multiband superconductivity in UNi 2 Al 3 . The initial slope of the upper critical field H' c2 (T) of the thin film samples suggests an unconventional spin-singlet superconducting state, as opposed to bulk single crystal data. To probe the superconducting gap of UNi 2 Al 3 directly by means of tunnelling spectroscopy many planar junctions of different design

Analysis of micro vibration in gas film of aerostatic guide way based on molecule collision theory

Directory of Open Access Journals (Sweden)

Yang Shao Hua

2016-01-01

Full Text Available Micro vibration of the aerostatic guide way has a significant impact on its dynamic characteristics and stability, which limits the development of pneumatic component. High pressure gas molecules have been collided with the supporting surface and the internal surface of the throttle during the flow process. Variable impulse of the surfaces aside for the gas film are affected by the changes of impulse which formed irregular impact force in horizontal and vertical direction. Micro-vibration takes place based on the natural frequency of the system and its frequency doubling. In this paper, the vibration model was established to describe the dynamic characteristics of the gas film, and the formation mechanism of micro vibration in the film is defined. Through the simulation analysis and experimental comparison, formation mechanism of the micro vibration in the gas film is confirmed. It was proposed that the micro vibration of gas film can be produced no matter whether there is a gas chamber or not in the throttle. Under the same conditions, the micro vibration of the guide way with air chamber is greater than that without any chamber. The frequency points of the vibration peaks are almost the same, as well as the vibration pattern in the frequency domain.

Quasiclassical studies of phase-coherent transport in superconducting nanostructures

International Nuclear Information System (INIS)

Seviour, R.F.

1999-07-01

In chapter two we introduce the quasiclassical technique and analysis the subgap conductance in S/N structures with barriers (zero bias and finite bias anomalies). We also analyse an Andreev interferometer. Also we present the results of studies on the Josephson effect in 4 terminal S/N/S contacts and on the possible sign reversal of the Josephson critical current (Published in Superlattices and Microstructures, Vol. 25, No. 5/6, p. 647 (1999)). In chapters three and four using the quasiclassical technique in conjunction with a numerical scattering approach (see Appendix) we consider a normal-superconducting-normal structure. In these chapters we consider the effects of the interface resistance between the Normal reservoirs and the normal film and the interface resistance between the superconductor and the normal film. This work has been published in J.Phys.Conds.Mat. 10 (1998), L615 and PHYS REV B 1 Nov 98. In Chapter 5 using the techniques discussed above we shown that for normal-superconducting-normal structure a new peek may arise in the temperature dependence of the conductance when the temperature is approximately equal to the transition temperature of the superconducting (Published PHYS. Rev.13, 1999, v.59, No.9, p. 6031). In chapter 6 we analyse the first ever experimental results showing the new peak in the conductance as discussed in chapter 5 (Submitted to PRL). Chapter 7 uses the numerical technique discussed in the appendix. to examine the phenomena of conductance suppression in 4 probe normal superconducting structures (Published Superlattices and Microstructures, Vol. 25, No.5, p. 640 (1999)). (author)

Novel micro-patterning processes for thin film NiTi vascular devices

International Nuclear Information System (INIS)

Chun, Y J; Mohanchandra, K P; Carman, G P; Levi, D S; Fishbein, M C

2010-01-01

In order to create microscale features in thin film NiTi for use in vascular endografts, a novel 'lift-off process' was developed for use with deep reactive ion etching. A wet etching approach is compared to two variations of this new 'lift-off' process. The first lift-off process (lift-off I) used Si posts to define the features of NiTi film deposited on the Si substrate. This method produced fractures in the NiTi when the film was released. The lift-off II process used Si islands as substrate for the film while the Si wafer defined the specific geometric features. Lift-off II process allowed for the creation of various shape patterns (i.e., ellipse, diamond, circle, square, etc) in the range of 5–180 µm. The lift-off II process produced smooth and well aligned micro-patterns in thin film NiTi without the undercutting found in wet etching techniques. The micro-patterned thin film NiTi formed from the lift-off II process was used to cover a stent. In vivo tests were performed to evaluate the endothelialization though patterned thin films. Angiography, histopathology and SEM showed patency of the artery and uniformly promoted endothelial layer covering without thrombosis in both a medium and small artery

High field properties of superconducting BaFe{sub 2-x}Ni{sub x}As{sub 2} thin films

Energy Technology Data Exchange (ETDEWEB)

Richter, Stefan [Institute for Metallic Materials, IFW Dresden (Germany); Technical University Dresden (Germany); Kurth, Fritz; Grinenko, Vadim; Nielsch, Kornelius; Huehne, Ruben [Institute for Metallic Materials, IFW Dresden (Germany); Iida, Kazumasa [Nagoya University (Japan); Pervakov, Kirill [Russian Academy of Sciences (Russian Federation); Tarantini, Chiara; Jaroszynski, Jan [National High Magnetic Field Laboratory (United States); Pukenas, Aurimas; Skrotzki, Werner [Technical University Dresden (Germany)

2016-07-01

Fe based superconductors combine the advantages of cuprates (high upper critical field) with the small Hc{sub 2} anisotropy of classic low temperature superconductors, which makes them suitable candidates for high field applications. The study of Fe-based superconducting thin films is one crucial step to explore this potential in more detail. We present results for epitaxial BaFe{sub 2-x}Ni{sub x}As{sub 2} thin films, which have been successfully grown for the first time using pulsed laser deposition. Superconducting transition temperatures of up to 19 K have been realized in slightly overdoped films, which is in good agreement with results obtained for single crystals. The behavior of the upper critical field and critical current density has been measured in high magnetic fields up to 35 T. The results will be correlated to the observed microstructure and compared to high field data for single crystals with similar composition.

Construction of sputtering system and preparation of high temperature superconducting thin films

International Nuclear Information System (INIS)

Kaynak, E.

2000-01-01

The preparation of high T c superconducting thin film is important both for the understanding of fundamental behaviours of these materials and for the investigations on the usefulness of technological applications. High quality thin films can be prepared by various kinds of techniques being used today. Among these, sputtering is the most preferred one. The primary aim of this work is the construction of a r. f. and c. magnetron sputtering system. For this goal, a magnetron sputtering system was designed and constructed having powers up to 500W (r.f.) and 1KW (d.c.) that enables to deposit thin films of various kinds of materials: metals, ceramics and magnetic materials. The temperature dependence of the electrical resistance of the films was investigated by using four-point probe method. The zero resistance and the transition with of the films were measured as 80-85 K, and 2-9 K, respectively. The A.C. susceptibility experiments were done by utilising the system that was designed and constructed. The applied field dependence of the real and imaginary components of the susceptibility that were measured between the 77-120 K temperature interval and at a fixed frequency was investigated

Nanolayers with advanced properties for superconducting nanoelectronics

International Nuclear Information System (INIS)

Prepelita, A.; Zdravkov, V.; Morari, R.; Socrovisciuc, A.; Antropov, E.; Sidorenko, A.

2011-01-01

Full text: Elaborated advanced technology for superconducting spintronics - technological process, based on magnetron sputtering of the metallic films with non-metallic protective layers, yields significant improvement in superconducting properties of thin Nb films and Nb/CuNi nanostructures in comparison with common methods of films deposition. The developed advanced technological process is patented (Patent RM number 175 from 31.03.2010). First experimental observation of the double re-entrant superconductivity in superconductor/ ferromagnetic nanostructures (Nb/Cu 41 Ni 59 bilayers) in dependence on the thickness of the ferromagnetic layer (Published in : A.S. Sidorenko, V.I. Zdravkov, J. Kehrle, R.Morari, E.Antropov, G. Obermeier, S. Gsell, M. Schreck, C. Muller, V.V. Ryazanov, S. Horn, R. Tidecks, L.R. Tagirov. Extinction and recovery of superconductivity by interference in superconductor/ferromagnet bilayers. In: Nanoscale Phenomena . Fundamentals and Applications,Ed. by H.Hahn, A.Sidorenko, I.Tiginyanu, Springer, 2009 p.1-10. Perspectives of applications: design of a new generation of superconducting spintronic devices - high frequency operating superconducting spin-switch for telecommunication and computers. (author)

Vortex lattice in effective type-I superconducting films with periodic arrays of submicron holes

International Nuclear Information System (INIS)

Berdiyorov, G.R.; Milosevic, M.V.; Peeters, F.M.

2006-01-01

The vortex matter and related phenomena in superconducting films with periodic arrays of microholes (antidots) are studied within the nonlinear Ginzburg-Landau (GL) theory. By varying the GL parameter κ, the vortex-vortex interaction is fine tuned, from repulsive to attractive behavior. This interaction is of crucial importance for equilibrium vortex structures, the saturation number of the antidots, and the related quantities, such as critical current. Due to vortex attraction in effectively type-I samples, the giant-vortex state becomes energetically favorable (contrary to the type-II behavior). For the same reason, the number of vortices which can be captured by antidots, increases with decreasing κ. As a result, for given magnetic field, the critical current is larger for effectively type-I superconductors than in conventional type-II cases

Electric field dependence of excess electrical conductivity below transition temperature in thin superconducting lead films

Energy Technology Data Exchange (ETDEWEB)

Ashwini Kumar, P K; Duggal, V P [Delhi Univ. (India). Dept. of Physics and Astrophysics

1976-01-26

Results of measurements of the electric field dependence of the excess electrical conductivity are reported in thin superconducting lead films below the transition temperature. It is observed that the normal state sheet resistance has some effect on the nonlinearity but the theory of Yamaji still fits well to the experimental data.

On-chip micro-power: three-dimensional structures for micro-batteries and micro-supercapacitors

Science.gov (United States)

Beidaghi, Majid; Wang, Chunlei

2010-04-01

With the miniaturization of portable electronic devices, there is a demand for micro-power source which can be integrated on the semiconductor chips. Various micro-batteries have been developed in recent years to generate or store the energy that is needed by microsystems. Micro-supercapacitors are also developed recently to couple with microbatteries and energy harvesting microsystems and provide the peak power. Increasing the capacity per footprint area of micro-batteries and micro-supercapacitors is a great challenge. One promising route is the manufacturing of three dimensional (3D) structures for these micro-devices. In this paper, the recent advances in fabrication of 3D structure for micro-batteries and micro-supercapacitors are briefly reviewed.

Loss mechanisms in superconducting thin film microwave resonators

Energy Technology Data Exchange (ETDEWEB)

Goetz, Jan, E-mail: jan.goetz@wmi.badw.de; Haeberlein, Max; Wulschner, Friedrich; Zollitsch, Christoph W.; Meier, Sebastian; Fischer, Michael; Fedorov, Kirill G.; Menzel, Edwin P. [Walther-Meißner-Institut, Bayerische Akademie der Wissenschaften, 85748 Garching (Germany); Physik-Department, Technische Universität München, 85748 Garching (Germany); Deppe, Frank; Eder, Peter; Xie, Edwar; Gross, Rudolf, E-mail: rudolf.gross@wmi.badw.de [Walther-Meißner-Institut, Bayerische Akademie der Wissenschaften, 85748 Garching (Germany); Physik-Department, Technische Universität München, 85748 Garching (Germany); Nanosystems Initiative Munich (NIM), Schellingstraße 4, 80799 München (Germany); Marx, Achim [Walther-Meißner-Institut, Bayerische Akademie der Wissenschaften, 85748 Garching (Germany)

2016-01-07

We present a systematic analysis of the internal losses of superconducting coplanar waveguide microwave resonators based on niobium thin films on silicon substrates. In particular, we investigate losses introduced by Nb/Al interfaces in the center conductor, which is important for experiments where Al based Josephson junctions are integrated into Nb based circuits. We find that these interfaces can be a strong source for two-level state (TLS) losses, when the interfaces are not positioned at current nodes of the resonator. In addition to TLS losses, for resonators including Al, quasiparticle losses become relevant above 200 mK. Finally, we investigate how losses generated by eddy currents in conductive material on the backside of the substrate can be minimized by using thick enough substrates or metals with high conductivity on the substrate backside.

Oxide superconducting ribbon and its fabrication process

International Nuclear Information System (INIS)

Belouet, C.

1990-01-01

A film without cavities, of perovskite type superconducting oxide is deposited by melting on a metal or composite flexible substrate with a rectangular cross section. The film thickness is comprised between 1 and 100 micrometers and orientation of C axis of superconducting crystals is perpendicular to the subtrate [fr

Layer-by-layer deposition of superconducting Sr-Ca-Cu-O films by the spray pyrolysis technique

International Nuclear Information System (INIS)

Pawar, S.H.; Pawaskar, P.N.; Ubale, M.J.; Kulkarni, S.B.

1995-01-01

Layer-by-layer deposition of Sr-Ca-Cu-O films has been carried out using the spray pyrolysis technique. Reagent-grade nitrates of strontium, calcium and copper were used to prepare starting solutions for spray pyrolysis. A two-step procedure was used for every layer of the constituents in the sequence Sr-Cu-Ca-Cu-Sr: first, deposition onto silver substrate at 350 C, then firing at T≥450 C, both at atmospheric pressure. The films were 2-3 μm thick and showed adequate adhesion to the substrate. The films were then characterised by studying their electron micrographs, X-ray diffraction patterns and electrical resistivity. The films showed superconductivity below 104 K. ((orig.))

Micro-patterning of NdFeB and SmCo magnet films for integration into micro-electro-mechanical-systems

International Nuclear Information System (INIS)

Walther, A.; Marcoux, C.; Desloges, B.; Grechishkin, R.; Givord, D.; Dempsey, N.M.

2009-01-01

The integration of high-performance RE-TM (NdFeB and SmCo) hard magnetic films into micro-electro-mechanical-systems (MEMS) requires their patterning at the micron scale. In this paper we report on the applicability of standard micro-fabrication steps (film deposition onto topographically patterned substrates, wet etching and planarization) to the patterning of 5-8 μm thick RE-TM films. While NdFeB comprehensively fills micron-scaled trenches in patterned substrates, SmCo deposits are characterized by poor filling of the trench corners, which poses a problem for further processing by planarization. The magnetic hysteresis loops of both the NdFeB and SmCo patterned films are comparable to those of non-patterned films prepared under the same deposition/annealing conditions. A micron-scaled multipole magnetic field pattern is directly produced by the unidirectional magnetization of the patterned films. NdFeB and SmCo show similar behavior when wet etched in an amorphous state: etch rates of approximately 1.25 μm/min and vertical side walls which may be attributed to a large lateral over-etch of typically 20 μm. Chemical-mechanical-planarization (CMP) produced material removal rates of 0.5-3 μm/min for amorphous NdFeB. Ar ion etching of such films followed by the deposition of a Ta layer prior to film crystallization prevented degradation in magnetic properties compared to non-patterned films

Micro-patterning of NdFeB and SmCo magnet films for integration into micro-electro-mechanical-systems

Energy Technology Data Exchange (ETDEWEB)

Walther, A. [CEA Leti-MINATEC, 17 rue des Martyrs, 38054 Grenoble (France); Institut Neel, CNRS-UJF, 25 rue des Martyrs, 38042 Grenoble (France); Marcoux, C.; Desloges, B. [CEA Leti-MINATEC, 17 rue des Martyrs, 38054 Grenoble (France); Grechishkin, R. [Laboratory of Magnetoelectronics, Tver State University, 170000 Tver (Russian Federation); Givord, D. [Institut Neel, CNRS-UJF, 25 rue des Martyrs, 38042 Grenoble (France); Dempsey, N.M. [Institut Neel, CNRS-UJF, 25 rue des Martyrs, 38042 Grenoble (France)], E-mail: nora.dempsey@grenoble.cnrs.fr

2009-03-15

The integration of high-performance RE-TM (NdFeB and SmCo) hard magnetic films into micro-electro-mechanical-systems (MEMS) requires their patterning at the micron scale. In this paper we report on the applicability of standard micro-fabrication steps (film deposition onto topographically patterned substrates, wet etching and planarization) to the patterning of 5-8 {mu}m thick RE-TM films. While NdFeB comprehensively fills micron-scaled trenches in patterned substrates, SmCo deposits are characterized by poor filling of the trench corners, which poses a problem for further processing by planarization. The magnetic hysteresis loops of both the NdFeB and SmCo patterned films are comparable to those of non-patterned films prepared under the same deposition/annealing conditions. A micron-scaled multipole magnetic field pattern is directly produced by the unidirectional magnetization of the patterned films. NdFeB and SmCo show similar behavior when wet etched in an amorphous state: etch rates of approximately 1.25 {mu}m/min and vertical side walls which may be attributed to a large lateral over-etch of typically 20 {mu}m. Chemical-mechanical-planarization (CMP) produced material removal rates of 0.5-3 {mu}m/min for amorphous NdFeB. Ar ion etching of such films followed by the deposition of a Ta layer prior to film crystallization prevented degradation in magnetic properties compared to non-patterned films.

Applying a foil queue micro-electrode in micro-EDM to fabricate a 3D micro-structure

Science.gov (United States)

Xu, Bin; Guo, Kang; Wu, Xiao-yu; Lei, Jian-guo; Liang, Xiong; Guo, Deng-ji; Ma, Jiang; Cheng, Rong

2018-05-01

Applying a 3D micro-electrode in a micro electrical discharge machining (micro-EDM) can fabricate a 3D micro-structure with an up and down reciprocating method. However, this processing method has some shortcomings, such as a low success rate and a complex process for fabrication of 3D micro-electrodes. By focusing on these shortcomings, this paper proposed a novel 3D micro-EDM process based on the foil queue micro-electrode. Firstly, a 3D micro-electrode was discretized into several foil micro-electrodes and these foil micro-electrodes constituted a foil queue micro-electrode. Then, based on the planned process path, foil micro-electrodes were applied in micro-EDM sequentially and the micro-EDM results of each foil micro-electrode were able to superimpose the 3D micro-structure. However, the step effect will occur on the 3D micro-structure surface, which has an adverse effect on the 3D micro-structure. To tackle this problem, this paper proposes to reduce this adverse effect by rounded corner wear at the end of the foil micro-electrode and studies the impact of machining parameters on rounded corner wear and the step effect on the micro-structure surface. Finally, using a wire cutting voltage of 80 V, a current of 0.5 A and a pulse width modulation ratio of 1:4, the foil queue micro-electrode was fabricated by wire electrical discharge machining. Also, using a pulse width of 100 ns, a pulse interval of 200 ns, a voltage of 100 V and workpiece material of 304# stainless steel, the foil queue micro-electrode was applied in micro-EDM for processing of a 3D micro-structure with hemispherical features, which verified the feasibility of this process.

Growth and characterization of high-Tc Y1Ba2Cu3O7-x superconducting thin films by chemical vapor deposition

International Nuclear Information System (INIS)

Feng, A.

1992-01-01

In chapter I, the current status of high-Tc superconductors (especially Y 1 Ba 2 Cu 3 O 7-x ), their microstructures and their unique physical properties are reviewed. An introduction to the potential and importance of those high-Tc superconductors in practical applications, especially for the application of YBCO thin films in microelectronics, is given. A general description of the common YBCO thin film fabrication and characterization techniques is also presented in this first chapter. Chapter II describes a new CVD process, temperature-controlled chemical vapor deposition (TC-CVD) for the growth of YBCO superconducting thin films on substrates of practical importance, such as sapphire (Al 2 O 3 ) and on substrates of lattice matched perovskite-type single crystals, such as LaAlO 3 . In order to verify the viability of this new CVD process the qualities of YBCO superconducting thin films were examined by various characterization methods, such as resistivity vs. temperature (R vs. T), scanning electron microscopy (SEM), X-ray diffraction (XRD), and magnetic susceptibility (x) measurements. Chapter III deals with the effect of substrate temperature on the properties of YBCO thin films made by TC-CVD. The principle objective of this study is to raise the transition temperature and critical current densities of CVD YBCO superconducting thin films. Understanding the relations between YBCO film growth process and varying substrate temperatures proved to be crucial in reaching this goal. The authors present the characterization results of YBCO thin films produced by different temperature schemes, to illustrate the importance of varying substrate temperature during the film growth. In chapter IV, the Rutherford backscattering (RBS) channeling technique is described. They have used RBS channeling to characterize the epitaxial YBCO thin film's crystallinity and lattice alignment. Transmission electron microscopy studies are also included

Incorporation of self-organised gold nano crystals in YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} thin films: Modification of superconducting properties

Energy Technology Data Exchange (ETDEWEB)

Katzer, Christian; Michalowski, Peter; Westerhausen, Markus; Koch, Stefanie; Schmidl, Frank; Seidel, Paul [Institut fuer Festkoerperphysik, Friedrich-Schiller-Universitaet Jena, Helmholtzweg 5, 07743 Jena (Germany); Treiber, Sebastian [Max-Planck-Institut fuer Intelligente Systeme, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Albrecht, Joachim [Hochschule Aalen, Beethovenstrasse 1, 73430 Aalen (Germany)

2012-07-01

Using pulsed laser deposition we are able to fabricate and examine Yttrium-Barium-Copper-Oxide (YBCO) thin films of high quality. A particular point of interest thereby is the influence of a pre-deposited gold layer with a well-defined film thickness. During the growth of the YBCO thin film the intermediate gold layer self assembles into crystalline nano particles, which modify the growth conditions and hence the physical properties of the growing YBCO. We report on the modification of structural and superconducting properties of our YBCO thin films (such as rocking curve widths, critical temperature T{sub c} and critical current density j{sub c}) comparing conventional to Au added YBCO. The temperature dependence of the critical current density thereby was determined using transport measurements as well as magneto-optical measurements. Furthermore investigations of the flux noise of our gold modified YBCO films are presented.

A novel approach to fabricate dye-encapsulated polymeric micro- and nanoparticles by thin film dewetting technique.

Science.gov (United States)

Chatterjee, Manosree; Hens, Abhiram; Mahato, Kuldeep; Jaiswal, Namita; Mahato, Nivedita; Nagahanumaiah; Chanda, Nripen

2017-11-15

A new method is reported for fabrication of polymeric micro- and nanoparticles from an intermediate patterned surface originated by dewetting of a polymeric thin film. Poly (d, l-lactide-co-glycolide) or PLGA, a biocompatible polymer is used to develop a thin film over a clean glass substrate which dewets spontaneously in the micro-/nano-patterned surface of size range 50nm to 3.5µm. Since another water-soluble polymer, poly vinyl alcohol (PVA) is coated on the same glass substrate before PLGA thin film formation, developed micro-/nano-patterns are easily extracted in water in the form of micro- and nanoparticle mixture of size range 50nm to 3.0µm. This simplified method is also used to effectively encapsulate a dye molecule, rhodamine B inside the PLGA micro-/nanoparticles. The developed dye-encapsulated nanoparticles, PLGA-rhodamine are separated from the mixture and tested for in-vitro delivery application of external molecules inside human lung cancer cells. For the first time, the use of thin film dewetting technique is reported as a potential route for the synthesis of polymeric micro-/nanoparticles and effective encapsulation of external species therein. Copyright © 2017 Elsevier Inc. All rights reserved.

Magnetic-Field-Tunable Superconducting Rectifier

Science.gov (United States)

Sadleir, John E.

2009-01-01

Superconducting electronic components have been developed that provide current rectification that is tunable by design and with an externally applied magnetic field to the circuit component. The superconducting material used in the device is relatively free of pinning sites with its critical current determined by a geometric energy barrier to vortex entry. The ability of the vortices to move freely inside the device means this innovation does not suffer from magnetic hysteresis effects changing the state of the superconductor. The invention requires a superconductor geometry with opposite edges along the direction of current flow. In order for the critical current asymmetry effect to occur, the device must have different vortex nucleation conditions at opposite edges. Alternative embodiments producing the necessary conditions include edges being held at different temperatures, at different local magnetic fields, with different current-injection geometries, and structural differences between opposite edges causing changes in the size of the geometric energy barrier. An edge fabricated with indentations of the order of the coherence length will significantly lower the geometric energy barrier to vortex entry, meaning vortex passage across the device at lower currents causing resistive dissipation. The existing prototype is a two-terminal device consisting of a thin-film su - perconducting strip operating at a temperature below its superconducting transition temperature (Tc). Opposite ends of the strip are connected to electrical leads made of a higher Tc superconductor. The thin-film lithographic process provides an easy means to alter edge-structures, current-injection geo - metries, and magnetic-field conditions at the edges. The edge-field conditions can be altered by using local field(s) generated from dedicated higher Tc leads or even using the device s own higher Tc superconducting leads.

Sequential Ar-O2 sputtering of Y2O3, BaF2, and CuO targets for preparation of Y-Ba-Cu-O superconducting films without wet-O2 annealing

International Nuclear Information System (INIS)

Bhushan, M.; Strauss, A.J.; Finn, M.C.

1989-01-01

Superconducting Y-Ba-Cu-O (YBCO) films have been prepared by ex situ O 2 annealing of multilayer films deposited on yttria-stabilized zirconia substrates by sequential rf diode sputtering of Y 2 O 3 , BaF 2 , and CuO targets, all of which are chemically stable. If sputtering is performed in an Ar ambient, the as-deposited films contain sufficient F to require its removal by annealing in wet O 2 at about 800 degree C or above before the superconducting YBCO phase can be formed by annealing in dry O 2 . However, sputtering in an Ar-O 2 ambient greatly reduces the F content, making it possible to obtain the superconducting phase by annealing in dry O 2 only. If the ambient contains about 20% O 2 , films with T c (R=0)>85 K can be prepared without wet-O 2 annealing. The Ar-O 2 process therefore has the potential for in situ preparation of superconducting YBCO films

Laser writing of superconducting patterns on YBa2Cu3Ox films

International Nuclear Information System (INIS)

Dye, R.C.; Muenchausen, R.E.; Nogar, N.S.; Mukherjee, A.; Brueck, S.R.J.

1990-01-01

A novel process for the direct laser writing of thin-film high T c patterns is demonstrated. The process consists of deposition of a high quality film (308 nm laser ablation from a YBa 2 Cu 3 O x target with a 750 degree C substrate temperature and a 150 mTorr O 2 ambient), annealing in an inert atmosphere (Ar at 400 degree C for 5--20 min) to reduce the oxygen content and depress or eliminate the superconducting transition temperature, and direct-write laser heating (1.06 μm at ∼0.5 kW/cm 2 for ∼5 min) in an oxygen atmosphere at ∼590 Torr to selectively regenerate the high T c material. rf eddy current and four-point resistivity probe results confirm this process for both SrTiO 3 and LaAlO 3 substrates. Scanning electron micrographs indicate that this is a very mild processing sequence with no observable changes in film morphology

Superconducting coil and method of stress management in a superconducting coil

Science.gov (United States)

McIntyre, Peter M.; Shen, Weijun; Diaczenko, Nick; Gross, Dan A.

1999-01-01

A superconducting coil (12) having a plurality of superconducting layers (18) is provided. Each superconducting layer (18) may have at least one superconducting element (20) which produces an operational load. An outer support structure (24) may be disposed outwardly from the plurality of layers (18). A load transfer system (22) may be coupled between at least one of the superconducting elements (20) and the outer support structure (24). The load transfer system (22) may include a support matrix structure (30) operable to transfer the operational load from the superconducting element (20) directly to the outer support structure (24). A shear release layer (40) may be disposed, in part, between the superconducting element (20) and the support matrix structure (30) for relieving a shear stress between the superconducting element (20) and the support matrix structure (30). A compliant layer (42) may also be disposed, in part, between the superconducting element (20) and the support matrix structure (30) for relieving a compressive stress on the superconducting element (20).

Titanium nitride films for micro-supercapacitors: Effect of surface chemistry and film morphology on the capacitance

Science.gov (United States)

Achour, Amine; Porto, Raul Lucio; Soussou, Mohamed-Akram; Islam, Mohammad; Boujtita, Mohammed; Aissa, Kaltouma Ait; Le Brizoual, Laurent; Djouadi, Abdou; Brousse, Thierry

2015-12-01

Electrochemical capacitors (EC) in the form of packed films can be integrated in various electronic devices as power source. A fabrication process of EC electrodes, which is compatible with micro-fabrication, should be addressed for practical applications. Here, we show that titanium nitride films with controlled porosity can be deposited on flat silicon substrates by reactive DC-sputtering for use as high performance micro-supercapacitor electrodes. A superior volumetric capacitance as high as 146.4 F cm-3, with an outstanding cycling stability over 20,000 cycles, was measured in mild neutral electrolyte of potassium sulfate. The specific capacitance of the films as well as their capacitance retentions were found to depend on thickness, porosity and surface chemistry of electrodes. The one step process used to fabricate these TiN electrodes and the wide use of this material in the field of semiconductor technology make it promising for miniaturized energy storage systems.

Structural phase transitions and superconductivity in lanthanum copper oxides

International Nuclear Information System (INIS)

Crawford, M.K.; Harlow, R.L.; McCarron, E.M.

1996-01-01

Despite the enormous effort expended over the past ten years to determine the mechanism underlying high temperature superconductivity in cuprates there is still no consensus on the physical origin of this fascinating phenomenon. This is a consequence of a number of factors, among which are the intrinsic difficulties in understanding the strong electron correlations in the copper oxides, determining the roles played by antiferromagnetic interactions and low dimensionality, analyzing the complex phonon dispersion relationships, and characterizing the phase diagrams which are functions of the physical parameters of temperature and pressure, as well as the chemical parameters of stoichiometry and hole concentration. In addition to all of these intrinsic difficulties, extrinsic materials issues such as sample quality and homogeneity present additional complications. Within the field of high temperature superconductivity there exists a subfield centered around the material originally reported to exhibit high temperature superconductivity by Bednorz and Mueller, Ba doped La 2 CuO 4 . This is structurally the simplest cuprate superconductor. The authors report on studies of phase differences observed between such base superconductors doped with Ba or Sr. What these studies have revealed is a fascinating interplay of structural, magnetic and superconducting properties which is unique in the field of high temperature superconductivity and is summarized in this paper

Interplay of structural transition and superconductivity in cuprates

International Nuclear Information System (INIS)

Ghosh, Haranath; Mitra, Manidipa; Behera, S.N.; Ghatak, S.K.

1997-01-01

The presence of lattice distortion is known to suppress the superconducting (SC) transition in the cuprates. It is now accepted that electron correlation plays a dominant role in shaping the properties of these undoped and doped systems. Furthermore, since the Fermi level in these systems lies in a degenerate band of Cu : d and O : p orbitals the structural transition can be modeled as a band Jahn-Teller effect. We study the coexistence of superconductivity and band Jahn-Teller (J-T) distortion, taking into account the electron correlation within the slave boson formalism. It is shown that with increasing dopant concentration (δ), the structural transition temperature (T s ) remains constant up to a certain value and then vanishes, while the SC transition temperature (T c ) increases to a maximum value. The highest value of T c corresponds to that value of δ where T s vanishes. Besides with increasing lattice distortion superconductivity is suppressed. These findings are in qualitative agreement with the experimental results. (author)

Study of the geometrical resonances of superconducting tunnel junctions

DEFF Research Database (Denmark)

Sørensen, O. Hoffmann; Finnegan, T.F.; Pedersen, Niels Falsig

1973-01-01

The resonant cavity structure of superconducting Sn-Sn-oxide-Sn tunnel junctions has been investigated via photon-assisted quasiparticle tunneling. We find that the temperature-dependent losses at 35 GHz are determined by the surface resistance of the Sn films for reduced temperatures between 0...

Combination process of diamond machining and roll-to-roll UV-replication for thin film micro- and nanostructures

Science.gov (United States)

Väyrynen, J.; Mönkkönen, K.; Siitonen, S.

2016-09-01

Roll-to-roll (R2R) ultraviolet (UV) curable embossing replication process is a highly accurate and cost effective way to replicate large quantities of thin film polymer parts. These structures can be used for microfluidics, LED-optics, light guides, displays, cameras, diffusers, decorative, laser sensing and measuring devices. In the R2R UV-process, plastic thin film coated with UV-curable lacquer, passes through an imprinting embossing drum and is then hardened by an UV-lamp. One key element for mastering this process is the ability to manufacture a rotating drum containing micro- and nanostructures. Depending on the pattern shapes, the drum can be directly machined by diamond machining or it can be done through wafer level lithographical process. Due to the shrinkage of UV-curable lacquer, the R2R drum pattern process needs to be prototyped few times, in order to get the desired performance and shape from the R2R produced part. To speed up the prototyping and overall process we have developed a combination process where planar diamond machining patterns are being turned into a drum roller. Initially diamond machined patterns from a planar surface are replicated on a polymer sheet using UV-replication. Secondly, a nickel stamper shim is grown form the polymer sheet and at the end the stamper is turned into a roller and used in the R2R process. This process allows various micro milled, turned, grooved and ruled structures to be made at thin film products through the R2R process. In this paper, the process flow and examples of fabricating R2R embossed UVcurable thin film micro- and nanostructures from planar diamond machined patterns, is reported.

Traveling Wave Accelerating Structure for a Superconducting Accelerator

CERN Document Server

Kanareykin, Alex; Solyak, Nikolay

2005-01-01

We are presenting a superconducting traveling wave accelerating structure (STWA) concept, which may prove to be of crucial importance to the International Linear Collider. Compared to the existing design of a TESLA cavity, the traveling wave structure can provide ~20-40% higher accelerating gradient for the same aperture and the same peak surface magnetic RF field. The recently achieved SC structure gradient of 35 MV/m can be increased up to ~50 MV/m with the new STWA structure design. The STWA structure is supposed to be installed into the superconducting resonance ring and is fed by the two couplers with appropriate phase advance to excite a traveling wave inside the structure. The system requires two independent tuners to be able to adjust the cavity and feedback waveguide frequencies and hence to reduce the unwanted backward wave. In this presentation we discuss the structure design, optimization of the parameters, tuning requirements and plans for further development.

Nematicity, magnetism and superconductivity in FeSe.

Science.gov (United States)

Böhmer, Anna E; Kreisel, Andreas

2018-01-17

Iron-based superconductors are well known for their complex interplay between structure, magnetism and superconductivity. FeSe offers a particularly fascinating example. This material has been intensely discussed because of its extended nematic phase, whose relationship with magnetism is not obvious. Superconductivity in FeSe is highly tunable, with the superconducting transition temperature, T c , ranging from 8 K in bulk single crystals at ambient pressure to almost 40 K under pressure or in intercalated systems, and to even higher temperatures in thin films. In this topical review, we present an overview of nematicity, magnetism and superconductivity, and discuss the interplay of these phases in FeSe. We focus on bulk FeSe and the effects of physical pressure and chemical substitutions as tuning parameters. The experimental results are discussed in the context of the well-studied iron-pnictide superconductors and interpretations from theoretical approaches are presented.

Superconductivity applications for infrared and microwave devices; Proceedings of the Meeting, Orlando, FL, Apr. 19, 20, 1990

Science.gov (United States)

Bhasin, Kul B.; Heinen, Vernon O.

1990-10-01

Various papers on superconductivity applications for IR and microwave devices are presented. The individual topics addressed include: pulsed laser deposition of Tl-Ca-Ba-Cu-O films, patterning of high-Tc superconducting thin films on Si substrates, IR spectra and the energy gap in thin film YBa2Cu3O(7-delta), high-temperature superconducting thin film microwave circuits, novel filter implementation utilizing HTS materials, high-temperature superconductor antenna investigations, high-Tc superconducting IR detectors, high-Tc superconducting IR detectors from Y-Ba-Cu-O thin films, Y-Ba-Cu0-O thin films as high-speed IR detectors, fabrication of a high-Tc superconducting bolometer, transition-edge microbolometer, photoresponse of YBa2Cu3O(7-delta) granular and epitaxial superconducting thin films, fast IR response of YBCO thin films, kinetic inductance effects in high-Tc microstrip circuits at microwave frequencies.

Measurements of effective quasiparticle recombination times and of densities of electronic states at the Fermi level in superconducting Al- and Pb-films

Energy Technology Data Exchange (ETDEWEB)

Epperlein, P W [International Business Machines Corp., Zurich (Switzerland). Research Lab.; Eisenmenger, W [Stuttgart Univ. (TH) (Germany, F.R.). Physikalisches Inst.

1979-01-01

Temperature-dependent quasiparticle recombination lifetimes iota exp(T) and densities Nsub(o) of electronic states at the Fermi level have been measured from time decay experiments of excess quasiparticle concentrations in evaporated, superconducting Al- and Pb-tunnel junctions. Current pulses were used to inject excess, nonthermal quasiparticles in a single junction acting simultaneously as generator and detector. The experimental lifetimes in 'unperturbed' Al show satisfactory agreement with calculations based on the 2..delta..-phonon trapping lifetime model. iota exp decreases with increasing perturbations of the Al film structure by oxygen background evaporation. In Pb the measured times indicate 2..delta..-phonon volume losses. The densities Nsub(o) in Pb-films and 'unperturbed' as well as oxygen-perturbed Al-films differ by less than 5% from the corresponding bulk material data. Therefore, in trying to explain then enhancement of the transition temperature from 1.23K to 1.85K in perturbed, granular Al-films a change of Nsub(o) can be ruled out.

Measurements of effective quasiparticle recombination times and of densities of electronic states at the fermi level in superconducting Al- and Pb-films

International Nuclear Information System (INIS)

Epperlein, P.W.; Eisenmenger, W.

1979-01-01

Temperature-dependent quasiparticle recombination lifetimes iota exp(T) and densities Nsub(o) of electronic states at the Fermi level have been measured from time decay experiments of excess quasiparticle concentrations in evaporated, superconducting Al- and Pb-tunnel junctions. Current pulses were used to inject excess, nonthermal quasiparticles in a single junction acting simultaneously as generator and detector. The experimental lifetimes in 'unperturbed' Al show satisfactory agreement with calculations based on the 2Δ-phonon trapping lifetime model. iota exp decreases with increasing perturbations of the Al film structure by oxygen background evaporation. In Pb the measured times indicate 2Δ-phonon volume losses. The densities Nsub(o) in Pb-films and 'unperturbed' as well as oxygen-perturbed Al-films differ by less than 5% from the corresponding bulk material data. Therefore, in trying to explain then enhancement of the transition temperature from 1.23K to 1.85K in perturbed, granular Al-films a change of Nsub(o) can be ruled out. (orig.) [de

Electrochemical behavior of high performance on-chip porous carbon films for micro-supercapacitors applications in organic electrolytes

Science.gov (United States)

Brousse, K.; Huang, P.; Pinaud, S.; Respaud, M.; Daffos, B.; Chaudret, B.; Lethien, C.; Taberna, P. L.; Simon, P.

2016-10-01

Carbide derived carbons (CDCs) are promising materials for preparing integrated micro-supercapacitors, as on-chip CDC films are prepared via a process fully compatible with current silicon-based device technology. These films show good adherence on the substrate and high capacitance thanks to their unique nanoporous structure which can be fine-tuned by adjusting the synthesis parameters during chlorination of the metallic carbide precursor. The carbon porosity is mostly related to the synthesis temperature whereas the thickness of the films depends on the chlorination duration. Increasing the pore size allows the adsorption of large solvated ions from organic electrolytes and leads to higher energy densities. Here, we investigated the electrochemical behavior and performance of on-chip TiC-CDC in ionic liquid solvent mixtures of 1-ethyl-3-methylimidazolium tetrafluoroborate (EMIBF4) diluted in either acetonitrile or propylene carbonate via cyclic voltammetry and electrochemical impedance spectroscopy. Thin CDC films exhibited typical capacitive signature and achieved 169 F cm-3 in both electrolytes; 65% of the capacitance was still delivered at 1 V s-1. While increasing the thickness of the films, EMI+ transport limitation was observed in more viscous PC-based electrolyte. Nevertheless, the energy density reached 90 μW h cm-2 in 2M EMIBF4/ACN, confirming the interest of these CDC films for micro-supercapacitors applications.

Superconductivity observed in platinum-silicon interface

Energy Technology Data Exchange (ETDEWEB)

Kuo, Pai-Chia, E-mail: paichia@phys.sinica.edu.tw [Research Program on Nanoscience and Nanotechnology, Academia Sinica, Taipei 11529, Taiwan (China); Institute of Physics, Academia Sinica, Taipei 11529, Taiwan (China); Department of Materials Science and Engineering, National Taiwan University, Taipei 10617, Taiwan (China); Chen, Chun-Wei [Department of Materials Science and Engineering, National Taiwan University, Taipei 10617, Taiwan (China); Lee, Ku-Pin; Shiue, Jessie, E-mail: yshiue@phys.sinica.edu.tw [Research Program on Nanoscience and Nanotechnology, Academia Sinica, Taipei 11529, Taiwan (China); Institute of Physics, Academia Sinica, Taipei 11529, Taiwan (China)

2014-05-26

We report the discovery of superconductivity with an onset temperature of ∼0.6 K in a platinum-silicon interface. The interface was formed by using a unique focused ion beam sputtering micro-deposition method in which the energies of most sputtered Pt atoms are ∼2.5 eV. Structural and elemental analysis by transmission electron microscopy (TEM) and energy dispersive X-ray spectroscopy reveal a ∼ 7 nm interface layer with abundant Pt, which is the layer likely responsible for the superconducting transport behavior. Similar transport behavior was also observed in a gold-silicon interface prepared by the same technique, indicating the possible generality of this phenomenon.

MgB2 ultrathin films fabricated by hybrid physical chemical vapor deposition and ion milling

Directory of Open Access Journals (Sweden)

Narendra Acharya

2016-08-01

Full Text Available In this letter, we report on the structural and transport measurements of ultrathin MgB2 films grown by hybrid physical-chemical vapor deposition followed by low incident angle Ar ion milling. The ultrathin films as thin as 1.8 nm, or 6 unit cells, exhibit excellent superconducting properties such as high critical temperature (Tc and high critical current density (Jc. The results show the great potential of these ultrathin films for superconducting devices and present a possibility to explore superconductivity in MgB2 at the 2D limit.

Enhanced pinning in superconducting thin films with graded pinning landscapes

Science.gov (United States)

Motta, M.; Colauto, F.; Ortiz, W. A.; Fritzsche, J.; Cuppens, J.; Gillijns, W.; Moshchalkov, V. V.; Johansen, T. H.; Sanchez, A.; Silhanek, A. V.

2013-05-01

A graded distribution of antidots in superconducting a-Mo79Ge21 thin films has been investigated by magnetization and magneto-optical imaging measurements. The pinning landscape has maximum density at the sample border, decreasing linearly towards the center. Its overall performance is noticeably superior than that for a sample with uniformly distributed antidots: For high temperatures and low fields, the critical current is enhanced, whereas the region of thermomagnetic instabilities in the field-temperature diagram is significantly suppressed. These findings confirm the relevance of graded landscapes on the enhancement of pinning efficiency, as recently predicted by Misko and Nori [Phys. Rev. B 85, 184506 (2012)].

Synthesis and characterization of porous structured ZnO thin film for dye sensitized solar cell applications

Energy Technology Data Exchange (ETDEWEB)

Marimuthu, T.; Anandhan, N., E-mail: anandhan-kn@rediffmail.com; Mummoorthi, M. [School of Physics, Alagappa University, Karaikudi – 630 003 (India); Dharuman, V. [Department of Bioelectronics and Biosensors, Alagappa University, Karaikudi – 630 003 (India)

2016-05-23

Zinc oxide (ZnO) and zinc oxide/eosin yellow (ZnO/EY) thin films were potentiostatically deposited onto fluorine doped tin oxide (FTO) glass substrate. Effect of eosin yellow dye on structural, morphological and optical properties was studied. X-ray diffraction patterns, micro Raman spectra and photoluminescence (PL) spectra reveal hexagonal wurtzite structure with less atomic defects in 101 plane orientation of the ZnO/EY film. Scanning electron microscopy (SEM) images show flower for ZnO and porous like structure for ZnO/EY thin film, respectively. DSSC was constructed and evaluated by measuring the current density verses voltage curve.

Superconducting quantum electronics

International Nuclear Information System (INIS)

Kose, V.

1989-01-01

This book reviews recent accomplishments, presents new results and discusses possible future developments of superconducting quantum electronics and high T c superconductivity. The three main parts of the book deal with fundamentals, sensitive detectors, and precision metrology. New results reported include: correct equivalent circuits modelling superconducting electronic devices; exact solution of the Mattis-Bardeen equations describing various experiments for thin films; complete theoretical description and experimental results for a new broad band spectrum analyzer; a new Josephson junction potentiometer allowing tracing of unknown voltage ratios back to well-known frequency ratios; and fast superconducting SQUID shift registers enabling the production of calculable noise power spectra in the microwave region

MICROSTRUCTURE OF SUPERCONDUCTING MGB(2).

Energy Technology Data Exchange (ETDEWEB)

ZHU,Y.; LI,Q.; WU,L.; VOLKOV,V.; GU,G.; MOODENBAUGH,A.R.

2001-07-12

Recently, Akimitsu and co-workers [1] discovered superconductivity at 39 K in the intermetallic compound MgB{sub 2}. This discovery provides a new perspective on the mechanism for superconductivity. More specifically, it opens up possibilities for investigation of structure/properties in a new class of materials. With the exceptions of the cuprate and C{sub 60} families of compounds, MgB{sub 2} possesses the highest superconducting transition temperature T{sub c}. Its superconductivity appears to follow the BCS theory, apparently being mediated by electron-phonon coupling. The coherence length of MgB{sub 2} is reported to be longer than that of the cuprates [2]. In contrast to the cuprates, grain boundaries are strongly coupled and current density is determined by flux pinning [2,3]. Presently, samples of MgB{sub 2} commonly display inhomogeneity and porosity on the nanoscale, and are untextured. In spite of these obstacles, magnetization and transport measurements show that polycrystalline samples may carry large current densities circulating across many grains [3,4]. Very high values of critical current densities and critical fields have been recently observed in thin films [5,6]. These attributes suggest possible large scale and electronic applications. The underlying microstructure can be intriguing, both in terms of basic science and in applied areas. Subsequent to the discovery, many papers were published [1-13], most dealing with synthesis, physical properties, and theory. There have yet been few studies of microstructure and structural defects [11, 14]. A thorough understanding of practical superconducting properties can only be developed after an understanding of microstructure is gained. In this work we review transmission electron microscopy (TEM) studies of sintered MgB{sub 2} pellets [14]. Structural defects, including second phase particles, dislocations, stacking faults, and grain boundaries, are analyzed using electron diffraction, electron

Method of making an improved superconducting quantum interference device

International Nuclear Information System (INIS)

Wu, C.T.; Falco, C.M.; Kampwirth, R.T.

1977-01-01

An improved superconducting quantum interference device is made by sputtering a thin film of an alloy of three parts niobium to one part tin in a pattern comprising a closed loop with a narrow region, depositing a thin film of a radiation shield such as copper over the niobium-tin, scribing a narrow line in the copper over the narrow region, exposing the structure at the scribed line to radiation and removing the deposited copper

Study of the electroforming technology for high-aspect ratio micro structure which was machined by using proton beam writing

International Nuclear Information System (INIS)

Okamoto, N.

2009-01-01

In this study, we develop the formation process of Ni electrodeposited micro patterns, which is used for MEMS devices or nano-imprinting. The purpose of my study is creating the new process of fabricating 3-D complicated micro-pattern or micro-devices using electroforming and proton beam writing. In general, 'Through mask process' (like a LIGA process) is usually used to fabricate Ni electrodeposited micro patterns for making MEMS devices or microfabricated-molds. The strong point of 'Through mask process' is the simple shape of the electrode. It makes the deposition process easy, because the electrodeposited films just glow up from the bottom to top surface of the mold. And the shape of the electrodeposited films is the same as the electrode pattern from the bottom to top, like a simple pillar shape. However, this process also has some problems. In case of using 'Through mask process', it is difficult to fabricate the complicated 3-D shaped structures, which are bended, parted or severed at some part of the structure between the bottom and top, like a device with a micro sensor or micro total analysis system. In order to overcome these limitations, we try to fabricate Ni electrodeposited micro patterns using 'the Damascene process' and proton beam writing. (author)

Application of a phenomenological model for the surface impedance in high temperature superconducting films

International Nuclear Information System (INIS)

Mosquera, A.S.; Landinez Tellez, D.A.; Roa-Rojas, J.

2007-01-01

We report the application of a phenomenological model for the microwave surface impedance in high temperature superconducting films. This model is based on the modified two-fluid model, in which the real and imaginary parts of the surface impedance use the modelling parameter γ. This is responsible for the superconducting and normal charge carrier density and is used for the description of the temperature dependence of the London penetration depth λ L (T) including λ L (0). The relaxation time model also uses the γ parameter in combination with the residual resistance parameter α. The parameter δ 1 1 , γ, α, and δ 2 . The parameter δ 2 n (T) is a result of the competition between the increase of the relaxation time and the decrease of the normal charge-carrier density. We applied this model to analyze experimental results of MgB 2 , YBa 2 Cu 3 O 7-δ and GdBa 2 Cu 3 O 7-δ superconducting material. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

A new approach to MgB2 superconducting magnet fabrication

International Nuclear Information System (INIS)

Miyazoe, A; Ando, T; Wada, H; Abe, H; Hirota, N; Sekino, M

2008-01-01

Fabrication of MgB 2 -based superconducting magnets has been attempted by a new approach using film coated on symmetric tubes. Superconducting MgB 2 films have been prepared on iron substrates by electroplating in molten electrolytes. The critical current (I c ) of the MgB 2 electroplating films at 4.2 K and at self-field was 15 A on the basis of 1 μV/cm of I c criterion. A model calculation has shown that MgB 2 -based superconducting magnets based on MgB 2 electroplating films have the potential to generate magnetic fields over 0.5 T

Unconventional superconductivity of the heavy fermion compound UNi{sub 2}Al{sub 3}

Energy Technology Data Exchange (ETDEWEB)

Zakharov, Andrey

2008-07-01

The heavy fermion compound UNi{sub 2}Al{sub 3} exhibits the coexistence of superconductivity and magnetic order at low temperatures, stimulating speculations about possible exotic Cooper-pairing interaction in this superconductor. However, the preparation of good quality bulk single crystals of UNi{sub 2}Al{sub 3} has proven to be a non-trivial task due to metallurgical problems, which result in the formation of an UAl{sub 2} impurity phase and hence a strongly reduced sample purity. The present work concentrates on the preparation, characterization and electronic properties investigation of UNi{sub 2}Al{sub 3} single crystalline thin film samples. The preparation of thin films was accomplished in a molecular beam epitaxy (MBE) system. (100)-oriented epitaxial thin films of UNi{sub 2}Al{sub 3} were grown on single crystalline YAlO{sub 3} substrates cut in (010)- or (112)-direction. The high crystallographic quality of the samples was proved by several characterisation methods, such as X-ray analysis, RHEED and TEM. To study the magnetic structure of epitaxial thin films resonant magnetic X-ray scattering was employed. The magnetic order of thin the film samples, the formation of magnetic domains with different moment directions, and the magnetic correlation length were discussed. The electronic properties of the UNi{sub 2}Al{sub 3} thin films in the normal and superconducting states were investigated by means of transport measurements. A pronounced anisotropy of the temperature dependent resistivity {rho}(T) was observed. Moreover, it was found that the temperature of the resistive superconducting transition depends on the current direction, providing evidence for multiband superconductivity in UNi{sub 2}Al{sub 3}. The initial slope of the upper critical field H'{sub c2}(T) of the thin film samples suggests an unconventional spin-singlet superconducting state, as opposed to bulk single crystal data. To probe the superconducting gap of UNi{sub 2}Al{sub 3

Toward nano-fabrication of superconducting ruthenate qubits

International Nuclear Information System (INIS)

Wood, Kent S.; Horwitz, James S.; Wu, H.-D.; Bounnak, Sommy S.; Yaguchi, Hiroshi; Maeno, Yoshiteru; Gulian, Armen M.

2004-01-01

The lack of thin films is one of the major obstacles in exploring the intriguing quantum properties specific to triplet superconductors. To have a single-domain chiral structure the sample should be made out of thin film, but crystalline imperfections until now have not allowed anybody to succeed in deposition of superconducting thin films of ruthenates. This stops not only general progress in investigating their properties, but in particular forbids practical realization of triplet superconductor qubits. Using the material properties of ruthenates, we have elaborated a method to overcome this problem. This report contains experimental aspects of our recent progress towards triplet superconductor qubits

Roughness analysis applied to niobium thin films grown on MgO(001) surfaces for superconducting radio frequency cavity applications

Energy Technology Data Exchange (ETDEWEB)

Beringer, D. B. [College of William and Mary, Williamsburg, VA (United States). Dept. of Physics; Roach, W. M. [College of William and Mary, Williamsburg, VA (United States). Dept. of Applied Science; Clavero, C. [College of William and Mary, Williamsburg, VA (United States). Dept. of Applied Science; Reece, C. E. [Thomas Jefferson National Accelerator Facility (TJNAF), Newport News, VA (United States); Lukaszew, R. A. [College of William and Mary, Williamsburg, VA (United States). Dept. of Physics; College of William and Mary, Williamsburg, VA (United States). Dept. of Applied Science

2013-02-05

This paper describes surface studies to address roughness issues inherent to thin film coatings deposited onto superconducting radio frequency (SRF) cavities. This is particularly relevant for multilayered thin film coatings that are being considered as a possible scheme to overcome technical issues and to surpass the fundamental limit of ~500 MV/m accelerating gradient achievable with bulk niobium. In 2006, a model by Gurevich [ Appl. Phys. Lett. 88 012511 (2006)] was proposed to overcome this limit that involves coating superconducting layers separated by insulating ones onto the inner walls of the cavities. Thus, we have undertaken a systematic effort to understand the dynamic evolution of the Nb surface under specific deposition thin film conditions onto an insulating surface in order to explore the feasibility of the proposed model. We examine and compare the morphology from two distinct Nb/MgO series, each with its own epitaxial registry, at very low growth rates and closely examine the dynamical scaling of the surface features during growth. Further, we apply analysis techniques such as power spectral density to the specific problem of thin film growth and roughness evolution to qualify the set of deposition conditions that lead to successful SRF coatings.

A Squeeze-film Damping Model for the Circular Torsion Micro-resonators

Science.gov (United States)

Yang, Fan; Li, Pu

2017-07-01

In recent years, MEMS devices are widely used in many industries. The prediction of squeeze-film damping is very important for the research of high quality factor resonators. In the past, there have been many analytical models predicting the squeeze-film damping of the torsion micro-resonators. However, for the circular torsion micro-plate, the works over it is very rare. The only model presented by Xia et al[7] using the method of eigenfunction expansions. In this paper, The Bessel series solution is used to solve the Reynolds equation under the assumption of the incompressible gas of the gap, the pressure distribution of the gas between two micro-plates is obtained. Then the analytical expression for the damping constant of the device is derived. The result of the present model matches very well with the finite element method (FEM) solutions and the result of Xia’s model, so the present models’ accuracy is able to be validated.

A study on the superconducting properties of YBa{sub 2}Cu{sub 9-x}Nb{sub x}O{sup y} thin films

Energy Technology Data Exchange (ETDEWEB)

Srinivas, S.; Bhatnagar, A.K. [Univ. of Hyderabad (India); Pinto, R. [Solid State Electronics Group, Bombay (India)] [and others

1994-12-31

Effect of niobium substitution at the copper site in YBa{sub 2}Cu{sub 9}O{sub 7-x} was studied in thin film form. The films were deposited by laser ablation technique using the targets of the YBa{sub 2}Cu{sub 3-x}Nb{sub x}O{sub y} where x = 0.0, 0.025, 0.05, 0.1, 0.2, 0.4, 0.8 and 1.0 under identical deposition conditions on SrTiO{sub 9} <100> substrates. Films were characterized by XRD, resistivity, I-V and J{sub c} measurements. Films made from x = 0.025 and 0.05 concentrations of Nb substituted targets showed relatively improved superconducting properties compared to that of undoped films. The best 7 realized for x = 0.025 Nb concentration was 1.8 x 10{sup {sigma}} A/cm{sup 2} and for 0.05 Nb concentration it was 3.2x10{sup {sigma}} A/cm{sup 2} at 77K. However, degradation of the superconducting properties, with the increase of x {ge} 0.1 Nb concentration and drastic suppression and complete loss of superconductivity was noticed for x {ge} 0.4. The growth of impurity phase YBa{sub 2}NbO{sub 6} for x = 0.1 and above of Nb concentration was noticed from XRD patterns. However, the site occupancy of Nb could not be confirmed from these studies.

Laser activated superconducting switch

International Nuclear Information System (INIS)

Wolf, A.A.

1976-01-01

A superconducting switch or bistable device is described consisting of a superconductor in a cryogen maintaining a temperature just below the transition temperature, having a window of the proper optical frequency band for passing a laser beam which may impinge on the superconductor when desired. The frequency of the laser is equal to or greater than the optical absorption frequency of the superconducting material and is consistent with the ratio of the gap energy of the switch material to Planck's constant, to cause depairing of electrons, and thereby normalize the superconductor. Some embodiments comprise first and second superconducting metals. Other embodiments feature the two superconducting metals separated by a thin film insulator through which the superconducting electrons tunnel during superconductivity

Quantum and superconducting fluctuations effects in disordered Nb 1- xTa x thin films above Tc

Science.gov (United States)

Giannouri, M.; Papastaikoudis, C.

1999-05-01

Disordered Nb 1- xTa x thin films are prepared with e-gun coevaporation. The influence of the β-phase of tantalum in the critical temperature Tc is observed as a function of the substrate temperature. The measurements of transverse magnetoresistance at various isothermals are interpreted in terms of weak-localization and superconducting fluctuations. From the fitting procedure, the phase breaking rate τφ-1 and the Larkin parameter βL are estimated as a function of temperature. Conclusions about the dominant inelastic scattering mechanisms at various temperature regions as well as for the dominant mechanism of superconducting fluctuations near the transition temperature are extracted.

Enhanced flux pinning properties in superconducting YBa{sub 2}Cu{sub 3}O{sub 7−z} films by a novel chemical doping approach

Energy Technology Data Exchange (ETDEWEB)

Wang, W.T., E-mail: wtwang@swjtu.edu.cn [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Mail Stop 165, Chengdu, Sichuan 610031 (China); Pu, M.H.; Lei, M.; Zhang, H.; Wang, Z. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Mail Stop 165, Chengdu, Sichuan 610031 (China); Zhang, H. [Department of Physics, Peking University, Beijing 100871 (China); Cheng, C.H. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Mail Stop 165, Chengdu, Sichuan 610031 (China); Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia); Zhao, Y., E-mail: yzhao@swjtu.edu.cn [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Mail Stop 165, Chengdu, Sichuan 610031 (China); Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia)

2013-10-15

Highlights: • Pure and Co-doped YBCO films were prepared by newly-developed chemical method. • The doped films have much denser and smoother surface microstructures. • Significantly enhanced fux-pinning properties have been obtained for dilute Co-doped flm. -- Abstract: Pure and cobalt-doped superconducting YBa{sub 2}Cu{sub 3}O{sub 7−z} (YBCO) films were prepared on (0 0 l) LaAlO{sub 3} substrate by a newly developed polymer-assisted metal organic deposition method. The cobalt-doped YBCO films display much denser and smoother surface microstructures and the superconducting transition temperature T{sub c} spans a small range of 1.7 K with the doping levels. Significantly enhanced flux-pinning properties have been obtained for dilute cobalt-doped film. This may be attributed to the good grain connections and the effective flux pinning centers introduced by cobalt doping.

Realization of superconductive films by screen printing

International Nuclear Information System (INIS)

Baudry, H.

1988-01-01

Screen printing is a promising method to manufacture superconductive lines making use of superconductive ceramics. An ink has been realized with YBa 2 Cu 3 0 7-x' and the process conditions defined by thermal analysis. A superconductive transition is observed after screen printing on MgO. The firing of the layer is made at 920 0 C followed by a reoxidation step at 420 0 C. The silver electrical contacts are also screen printed [fr

Effect of lattice disorder and strain on T/sub c/ in sputtered Nb3Ge thin films

International Nuclear Information System (INIS)

Roy, R.; Rogoski, D.A.

1976-01-01

Disorder and strain introduced into sputtered ''Nb 3 Ge'' films by mechanical polishing slightly lowers the onset temperature and/or very markedly broadens the width of the superconducting transition. The structural damage is reversible and annealing restores the superconducting behavior of the film very nearly to its initial state

Electrochemical impedance spectroscopy analysis of a thin polymer film-based micro-direct methanol fuel cell

Science.gov (United States)

Schulz, Tobias; Weinmüller, Christian; Nabavi, Majid; Poulikakos, Dimos

A single cell micro-direct methanol fuel cell (micro-DMFC) was investigated using electrochemical impedance spectroscopy. The electrodes consisted of thin, flexible polymer (SU8) film microchannel structures fabricated in-house using microfabrication techniques. AC impedance spectroscopy was used to separate contributions to the overall cell polarization from the anode, cathode and membrane. A clear distinction between the different electrochemical phenomena occurring in the micro-DMFC, especially the distinction between double layer charging and Faradaic reactions was shown. The effect of fuel flow rate, temperature, and anode flow channel structure on the impedance of the electrode reactions and membrane/electrode double layer charging were investigated. Analysis of impedance data revealed that the performance of the test cell was largely limited by the presence of intermediate carbon monoxide in the anode reaction. Higher temperatures increase cell performance by enabling intermediate CO to be oxidized at much higher rates. The results also revealed that serpentine anode flow microchannels show a lower tendency to intermediate CO coverage and a more stable cell behavior than parallel microchannels.

Metastable superconducting alloys

International Nuclear Information System (INIS)

Johnson, W.L.

1978-07-01

The study of metastable metals and alloys has become one of the principal activities of specialists working in the field of superconducting materials. Metastable crystalline superconductors such as the A15-type materials have been given much attention. Non-crystalline superconductors were first studied over twenty years ago by Buckel and Hilsch using the technique of thin film evaporation on a cryogenic substrate. More recently, melt-quenching, sputtering, and ion implantation techniques have been employed to produce a variety of amorphous superconductors. The present article presents a brief review of experimental results and a survey of current work on these materials. The systematics of superconductivity in non-crystalline metals and alloys are described along with an analysis of the microscopic parameters which underlie the observed trends. The unique properties of these superconductors which arise from the high degree of structural disorder in the amorphous state are emphasized

Study of the surface resistance of superconducting niobium films at 1.5 GHz

CERN Document Server

Benvenuti, Cristoforo; Campisi, I E; Darriulat, Pierre; Peck, M A; Russo, R; Valente, A M

1999-01-01

A systematic study of superconducting properties of niobium films sputtered on the inner wall of radiofrequency cavities is presented. The measured quantities include in particular the response to 1.5 GHz microwaves, the critical temperature, the penetration depth and the magnetic penetration field. In addition to films grown in different gas discharges (Xe, Kr, Ar and Ar/Ne mixtures) and to films grown on substrates prepared under different conditions, the study also includes bulk niobium cavities. The surface resistance is analysed in terms of its dependence on temperature, on RF field and, when relevant, on the density of trapped fluxons. A simple parameterisation is found to give a good fit to the data. Once allowance for the presence of impurities and defects is made by means of a single parameter, the electron mean free path, good agreement with BCS theory is observed. The fluxon-induced losses are studied in detail and their dependence on RF field, on temperature and on the density of trapped fluxons i...

Crystal structure of 200 K-superconducting phase in sulfur hydride system

Energy Technology Data Exchange (ETDEWEB)

Einaga, Mari; Sakata, Masafumi; Ishikawa, Takahiro; Shimizu, Katsuya [KYOKUGEN, Graduate School of Engineering Science, Osaka Univ. (Japan); Eremets, Mikhail; Drozdov, Alexander; Troyan, Ivan [Max Planck Institut fuer Chemie, Mainz (Germany); Hirao, Naohisa; Ohishi, Yasuo [JASRI/SPring-8, Hyogo (Japan)

2016-07-01

Superconductivity with the critical temperature T{sub c} above 200 K has been recently discovered by compression of H{sub 2}S (or D{sub 2}S) under extreme pressure. It was proposed that these materials decompose under high pressure to elemental sulfur and hydride with higher content of hydrogen which is responsible for the high temperature superconductivity. In this study, we have investigated that the crystal structure of the superconducting compressed H{sub 2}S and D{sub 2}S by synchrotron x-ray diffraction measurements combined with electrical resistance measurements at room and low temperatures. We found that the superconducting phase is in good agreement with theoretically predicted body-centered cubic structure, and coexists with elemental sulfur, which claims that the formation of 3H{sub 2}S → 2H{sub 3}S + S is occured under high pressure.

Aluminum Templates of Different Sizes with Micro-, Nano- and Micro/Nano-Structures for Cell Culture

Directory of Open Access Journals (Sweden)

Ming-Liang Yen

2017-10-01

Full Text Available This study investigates the results of cell cultures on aluminum (Al templates with flat-structures, micro-structures, nano-structures and micro/nano-structures. An Al template with flat-structure was obtained by electrolytic polishing; an Al template with micro-structure was obtained by micro-powder blasting; an Al template with nano-structure was obtained by aluminum anodization; and an Al template with micro/nano-structure was obtained by micro-powder blasting and then anodization. Osteoblast-like cells were cultured on aluminum templates with various structures. The microculture tetrazolium test assay was utilized to assess the adhesion, elongation, and proliferation behaviors of cultured osteoblast-like cells on aluminum templates with flat-structures, micro-structures, nano-structures, and micro/nano-structures. The results showed that the surface characterization of micro/nano-structure of aluminum templates had superhydrophilic property, and these also revealed that an aluminum template with micro/nano-structure could provide the most suitable growth situation for cell culture.

Effects of high-energy proton irradiation on the superconducting properties of Fe(Se,Te) thin films

Science.gov (United States)

Sylva, G.; Bellingeri, E.; Ferdeghini, C.; Martinelli, A.; Pallecchi, I.; Pellegrino, L.; Putti, M.; Ghigo, G.; Gozzelino, L.; Torsello, D.; Grimaldi, G.; Leo, A.; Nigro, A.; Braccini, V.

2018-05-01

In this paper we explore the effects of 3.5 MeV proton irradiation on Fe(Se,Te) thin films grown on CaF2. In particular, we carry out an experimental investigation with different irradiation fluences up to 7.30 · 1016 cm‑2 and different proton implantation depths, in order to clarify whether and to what extent the critical current is enhanced or suppressed, what are the effects of irradiation on the critical temperature, resistivity, and critical magnetic fields, and finally what is the role played by the substrate in this context. We find that the effect of irradiation on superconducting properties is generally small compared to the case of other iron-based superconductors. The irradiation effect is more evident on the critical current density Jc, while it is minor on the transition temperature Tc, normal state resistivity ρ, and on the upper critical field Hc2 up to the highest fluences explored in this work. In more detail, our analysis shows that when protons implant in the substrate far from the superconducting film, the critical current can be enhanced up to 50% of the pristine value at 7 T and 12 K; meanwhile, there is no appreciable effect on critical temperature and critical fields together with a slight decrease in resistivity. On the contrary, when the implantation layer is closer to the film–substrate interface, both critical current and temperature show a decrease accompanied by an enhancement of the resistivity and lattice strain. This result evidences that possible modifications induced by irradiation in the substrate may affect the superconducting properties of the film via lattice strain. The robustness of the Fe(Se,Te) system to irradiation-induced damage makes it a promising compound for the fabrication of magnets in high-energy accelerators.

The effect of thermal annealing on pentacene thin film transistor with micro contact printing.

Science.gov (United States)

Shin, Hong-Sik; Yun, Ho-Jin; Baek, Kyu-Ha; Ham, Yong-Hyun; Park, Kun-Sik; Kim, Dong-Pyo; Lee, Ga-Won; Lee, Hi-Deok; Lee, Kijun; Do, Lee-Mi

2012-07-01

We used micro contact printing (micro-CP) to fabricate inverted coplanar pentacene thin film transistors (TFTs) with 1-microm channels. The patterning of micro-scale source/drain electrodes without etch process was successfully achieved using Polydimethylsiloxane (PDMS) elastomer stamp. We used the Ag nano particle ink as an electrode material, and the sheet resistance and surface roughness of the Ag electrodes were effectively reduced with the 2-step thermal annealing on a hotplate, which improved the mobility, the on-off ratio, and the subthreshold slope (SS) of the pentacene TFTs. In addition, the device annealing on a hotplate in a N2 atmosphere for 30 sec can enhance the off-current and the mobility properties of OTFTs without damaging the pentacene thin films and increase the adhesion between pentacene and dielectric layer (SiO2), which was investigated with the pentacene films phase change of the XRD spectrum after device annealing.

Materials for superconducting cavities

International Nuclear Information System (INIS)

Bonin, B.

1996-01-01

The ideal material for superconducting cavities should exhibit a high critical temperature, a high critical field, and, above all, a low surface resistance. Unfortunately, these requirements can be conflicting and a compromise has to be found. To date, most superconducting cavities for accelerators are made of niobium. The reasons for this choice are discussed. Thin films of other materials such as NbN, Nb 3 Sn, or even YBCO compounds can also be envisaged and are presently investigated in various laboratories. It is shown that their success will depend critically on the crystalline perfection of these films. (author)

Superconductivity in transparent zinc-doped In2O3 films having low carrier density

Directory of Open Access Journals (Sweden)

Kazumasa Makise, Nobuhito Kokubo, Satoshi Takada, Takashi Yamaguti, Syunsuke Ogura, Kazumasa Yamada, Bunjyu Shinozaki, Koki Yano, Kazuyoshi Inoue and Hiroaki Nakamura

2008-01-01

Full Text Available Thin polycrystalline zinc-doped indium oxide (In2O3–ZnO films were prepared by post-annealing amorphous films with various weight concentrations x of ZnO in the range 0≤x ≤0.06. We have studied the dependences of the resistivity ρ and Hall coefficient on temperature T and magnetic field H in the range 0.5≤T ≤300 K, H≤6 Tfor 350 nm films annealed in air. Films with 0≤x≤0.03 show the superconducting resistive transition. The transition temperature Tc is below 3.3 K and the carrier density n is about 1025–1026 m−3. The annealed In2O3–ZnO films were examined by transmission electron microscopy and x-ray diffraction analysis revealing that the crystallinity of the films depends on the annealing time. We studied the upper critical magnetic field Hc2 (T for the film with x = 0.01. From the slope of dHc2 /dT, we obtain the coherence length ξ (0 ≈ 10 nm at T = 0 K and a coefficient of electronic heat capacity that is small compared with those of other oxide materials.

Growth orientation and superconducting properties of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} films prepared by the low-fluorine sol-gel process

Energy Technology Data Exchange (ETDEWEB)

Lei Li; Zhao Gaoyang; Xu Hui; Zhao Juanjuan, E-mail: leili813@gmail.co [School of Materials Science and Engineering, Xi' an University of Technology, Xi' an 710048 (China)

2010-08-15

YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) films were deposited on (100)-oriented LaAlO{sub 3} (LAO) single crystal substrates by the dip-coating process using low-fluorine solution. Their microstructures were characterized with the aid of X-ray diffractometry, scanning electron microscopy and high-resolution transmission electron microscopy. Their superconducting properties were measured by the standard four-probe method. The experiment results show that the film obtained under high enough humidity conditions exhibits better c-axis texture and superconducting properties than the film under a relatively low humidity conditions. Based on the classical nucleation and chemical reaction thermodynamics theory, the underlying crystalline and growth mechanisms of YBCO films under certain humidity conditions are explained in combination with our experimental results. It is suggested that the unreacted intermediate phases such as BaF{sub 2} and CuO aggregated in the YBCO grain boundary will cause lattice distortion in the YBCO matrix and further induce the formation of a-axis oriented YBCO grains as crystallization proceeds. Therefore, it is believed that the relative content of water vapor within the heat-treatment atmosphere plays quite an important role in the preparation of c-axis oriented YBCO film with good superconducting properties. (semiconductor materials)

Optical and structural properties of FeSe2 thin films obtained by selenization of sprayed amorphous iron oxide films

International Nuclear Information System (INIS)

Ouertani, B.; Ouerfelli, J.; Saadoun, M.; Zribi, M.; Rabha, M.Ben; Bessais, B.; Ezzaouia, H.

2006-01-01

We report in this work the optical and structural properties of iron diselenide films (FeSe 2 ) obtained by selenization under vacuum of amorphous iron oxide films predeposited by spray pyrolysis. The structure of the FeSe 2 films was investigated by scanning electron microscopy (SEM), microprobe analyses, atomic force microscopy (AFM) and X-ray diffraction (XRD). XRD and micro-probe analyses showed that FeSe 2 as well as FeSe 2-x phases begin to appear at a selenization temperature of 500 deg. C. As the selenization temperature rises, the iron diselenide films become more stoichiometric with a dominance of the FeSe 2 phase. At 550 deg. C, a single FeSe 2 phase having good crystallinity was obtained. At 600 deg. C, two phases were detected: the major one corresponds to Fe 3 O 4 , and the minor one to FeSe 2 . SEM surface views show that FeSe 2 films have granular structure with small spherical crystallites. However, layered and clustered FeSe 2 films were found, respectively, at 550 deg. C and 600 deg. C. Absorption measurements show that iron diselenide films have a direct and an indirect gaps of about 1.03 eV and 0.3 eV, which were suggested to be due to the stoichiometric FeSe 2 phase and to a Fe-rich non-stoichiometric phase, respectively

Heteroepitaxial growth of strained multilayer superconducting thin films of Nd1.83Ce0.17CuOx/YBa2Cu3O7-δ