  1. Electrical resistivity measurements to predict abrasion resistance

    Indian Academy of Sciences (India)

    Home; Journals; Bulletin of Materials Science; Volume 31; Issue 2. Electrical resistivity measurements to predict abrasion resistance of rock aggregates ... It was seen that correlation coefficients were increased for the rock classes. In addition ...

  2. Electrical Resistivity Measurements: a Review

    Science.gov (United States)

    Singh, Yadunath

    World-wide interest on the use of ceramic materials for aerospace and other advanced engineering applications, has led to the need for inspection techniques capable of detecting unusually electrical and thermal anomalies in these compounds. Modern ceramic materials offer many attractive physical, electrical and mechanical properties for a wide and rapidly growing range of industrial applications; moreover specific use may be made of their electrical resistance, chemical resistance, and thermal barrier properties. In this review, we report the development and various techniques for the resistivity measurement of solid kind of samples.

  3. Electrical resistivity measurement to predict uniaxial compressive ...

    Indian Academy of Sciences (India)

    Electrical resistivity values of 12 different igneous rocks were measured on core samples using a resistivity meter in the ... It was seen that the UCS and tensile strength values were linearly correlated with the ..... Innovation 2 20. Archie G E ...

  4. Electrical resistivity measurements in superconducting ceramics

    International Nuclear Information System (INIS)

    Muccillo, R.; Bressiani, A.H.A.; Muccillo, E.N.S.; Bressiani, J.C.

    1988-01-01

    Electrical resistivity measurements have been done in (Y, Ba, Cu, O) - and (Y, A1, Ba, Cu, O) - based superconducting ceramics. The sintered specimens were prepared by applying gold electrodes and winding on the non-metalized part with a copper strip to be immersed in liquid nitrogen for cooling. The resistivity measurements have been done by the four-probe method. A copper-constantan or chromel-alumel thermocouple inserted between the specimen and the copper cold finger has been used for the determination of the critical temperature T c . Details of the experimental set-up and resistivity versus temperature plots in the LNT-RT range for the superconducting ceramics are the major contributions of this communication. (author) [pt

  5. Electrical resistivity measurements in superconducting ceramics

    International Nuclear Information System (INIS)

    Muccillo, R.; Bressiani, A.H.A.; Muccillo, E.N.S.; Bressian, J.C.

    1988-01-01

    Electrical resistivity measurements have been done in (Y,Ba,Cu,O)- and (Y,Al,Ba,Cu,O)-based superconducting ceramics. The sintered specimens were prepared by applying gold electrodes and winding on the non-metalized part with a copper strip to be immersed in liquid nitrogen for cooling. The resistivity measurements have been done by the four-probe method. A copper constantan or chromel-alumel thermocouple inserted between the specimen and the copper cold finger has been used for the determination of the critical temperature T c . Details of the experimental set-up and resistivity versus temperature plots in the LNT-RT range for the superconducting ceramics are the major contributions of this communication. (author) [pt

  6. Electrical Resistivity Measurements of Downscaled Homogenous ...

    African Journals Online (AJOL)

    Knowledge of electrical resistivity for reservoir rocks is crucial for a number of reservoir engineering tasks such as the determination of oil-in-place and the calibration of resistivity logs. Those properties can now be predicted by numerical calculations directly on micro-CT images taken from rock fragments typically having a ...

  7. Electrical resistivity borehole measurements: application to an urban tunnel site

    Science.gov (United States)

    Denis, A.; Marache, A.; Obellianne, T.; Breysse, D.

    2002-06-01

    This paper shows how it is possible to use wells drilled during geotechnical pre-investigation of a tunneling site to obtain a 2-D image of the resistivity close to a tunnel boring machine. An experimental apparatus is presented which makes it possible to perform single and borehole-to-borehole electrical measurements independent of the geological and hydrogeological context, which can be activated at any moment during the building of the tunnel. This apparatus is first demonstrated through its use on a test site. Numerical simulations and data inversion are used to analyse the experimental results. Finally, electrical resistivity tomography and single-borehole measurements on a tunneling site are presented. Experimental results show the viability of the apparatus and the efficiency of the inverse algorithm, and also highlight the limitations of the electrical resistivity tomography as a tool for geotechnical investigation in urban areas.

  8. Friction Coefficient Determination by Electrical Resistance Measurements

    Science.gov (United States)

    Tunyagi, A.; Kandrai, K.; Fülöp, Z.; Kapusi, Z.; Simon, A.

    2018-01-01

    A simple and low-cost, DIY-type, Arduino-driven experiment is presented for the study of friction and measurement of the friction coefficient, using a conductive rubber cord as a force sensor. It is proposed for high-school or college/university-level students. We strongly believe that it is worthwhile planning, designing and performing Arduino…

  9. Friction coefficient determination by electrical resistance measurements

    Science.gov (United States)

    Tunyagi, A.; Kandrai, K.; Fülöp, Z.; Kapusi, Z.; Simon, A.

    2018-05-01

    A simple and low-cost, DIY-type, Arduino-driven experiment is presented for the study of friction and measurement of the friction coefficient, using a conductive rubber cord as a force sensor. It is proposed for high-school or college/university-level students. We strongly believe that it is worthwhile planning, designing and performing Arduino and compatible sensor-based experiments in physics class in order to ensure a better understanding of phenomena, develop theoretical knowledge and multiple experimental skills.

  10. Leaching of Conductive Species: Implications to Measurements of Electrical Resistivity.

    Science.gov (United States)

    Spragg, R; Jones, S; Bu, Y; Lu, Y; Bentz, D; Snyder, K; Weiss, J

    2017-05-01

    Electrical tests have been used to characterize the microstructure of porous materials, the measured electrical response being determined by the contribution of the microstructure (porosity and tortuosity) and the electrical properties of the solution (conductivity of the pore solution) inside the pores of the material. This study has shown how differences in concentration between the pore solution (i.e., the solution in the pores) and the storage solution surrounding the test specimen leads to significant transport (leaching) of the conductive ionic species between the pore solution and the storage solution. Leaching influences the resistivity of the pore solution, thereby influencing electrical measurements on the bulk material from either a surface or uniaxial bulk resistance test. This paper has three main conclusions: 1.) Leaching of conductive species does occur with concentration gradients and that a diffusion based approach can be used to estimate the time scale associated with this change. 2.) Leaching of ions in the pore solution can influence resistivity measurements, and the ratio of surface to uniaxial resistivity can be used as a method to assess the presence of leaching and 3.) An estimation of the magnitude of leaching for standardized tests of cementitious materials.

  11. Electrical resistivity measurements to predict abrasion resistance of ...

    Indian Academy of Sciences (India)

    WINTEC

    increasing expansion of highway and other construction works and decreasing natural aggregate resources in the world, the demand for crushed stone aggregates has in- creased from day-to-day. One of the important properties of rock aggregates is abrasion resistance. The abrasion resistance of aggregates is generally ...

  12. Diffusivity and electrical resistivity measurements in rock matrix around fractures

    International Nuclear Information System (INIS)

    Kumpulainen, H.; Uusheimo, K.

    1989-12-01

    Microfracturing of rock matrix around permeable fractures was studied experimentally from drill core samples around major fractures. The methods used were diffusion measurements using a 36 Cl-tracer and electrical resistivity measurements. Rock samples were from the Romuvaara investigation site, the granite specimen around a partially filled carbonate fracture (KR4/333 m) and gneiss specimen around a slickenside fracture (KR1/645 m). A consistent difference of one to two orders of magnitude in the levels of the methods with regard to the effective diffusion coefficients for Cl - -ion was found, the electrical resistivity measurement giving higher values. On the basis of the diffusion measurements the diffusion porosities could be calculated but these remained one to two orders of magnitude lower than that expected for granitic rocks using the water saturation method. A possible reason for these differences could have been the low, in some cases 0.004 M NaC1-concentration in the diffusion experiments vs. the 1 M NaCl-concentration used in the electrical resistivity measurements. Due to the small number of specimens and cross sectional areas of only 2 cm 2 , rock inhomogeneity effects were significant making the interpretation of the results somewhat troublesome. Porosities on fracture surfaces seemed to be higher than in the deeper, more intact rock matrix

  13. Measuring the electrical resistivity and contact resistance of vertical carbon nanotube bundles for application as interconnects

    International Nuclear Information System (INIS)

    Chiodarelli, Nicolo'; Li, Yunlong; Arstila, Kai; Richard, Olivier; Cott, Daire J; Heyns, Marc; De Gendt, Stefan; Groeseneken, Guido; Vereecken, Philippe M; Masahito, Sugiura; Kashiwagi, Yusaku

    2011-01-01

    Carbon nanotubes (CNT) are known to be materials with potential for manufacturing sub-20 nm high aspect ratio vertical interconnects in future microchips. In order to be successful with respect to contending against established tungsten or copper based interconnects, though, CNT must fulfil their promise of also providing low electrical resistance in integrated structures using scalable integration processes fully compatible with silicon technology. Hence, carefully engineered growth and integration solutions are required before we can fully exploit their potentialities. This work tackles the problem of optimizing a CNT integration process from the electrical perspective. The technique of measuring the CNT resistance as a function of the CNT length is here extended to CNT integrated in vertical contacts. This allows extracting the linear resistivity and the contact resistance of the CNT, two parameters to our knowledge never reported separately for vertical CNT contacts and which are of utmost importance, as they respectively measure the quality of the CNT and that of their metal contacts. The technique proposed allows electrically distinguishing the impact of each processing step individually on the CNT resistivity and the CNT contact resistance. Hence it constitutes a powerful technique for optimizing the process and developing CNT contacts of superior quality. This can be of relevant technological importance not only for interconnects but also for all those applications that rely on the electrical properties of CNT grown with a catalytic chemical vapor deposition method at low temperature.

  14. Irreversibility in transformation behavior of equiatomic nickel-titanium alloy by electrical resistivity measurement

    International Nuclear Information System (INIS)

    Matsumoto, Hitoshi

    2004-01-01

    Measurements of the electrical resistivity were precisely performed on shape memory Ni 50 Ti 50 alloy in order to reveal the irreversible behavior of the thermoelastic martensitic transformation with thermal cycling. The hump in the electrical resistivity during cooling is enhanced with increasing the number of complete thermal cycles to result in a peak, although no peak in the electrical resistivity is observed on the reverse transformation during heating. The electrical resistivity in the low-temperature phase, of which the temperature dependence is linear, increases with increasing the number of complete thermal cycles. The temperature coefficient of the electrical resistivity in the temperature region of the high-temperature phase increases with elevating the temperature. The transformation is strongly influenced by incomplete thermal cycles to result in a peak in the resistivity even on the reverse transformation after incomplete thermal cycling. It is thought that the anomalous behavior such as enhancement of a resistivity-peak, the increase in the electrical resistivity of the low-temperature phase, and the nonlinear relation between the resistivity and the temperature in the high-temperature phase are attributable to the appearance of an intermediate phase stabilized by transformation-induced defects, the accumulation of the transformation-induced defects, and the electron scattering due to the softening of a phonon mode in the high-temperature phase, respectively. It proved useful to make more accurate measurements of the electrical resistivity in order to investigate the intrinsic behavior of the transformation in NiTi

  15. Electrical Resistivity Measurement of Petroleum Coke Powder by Means of Four-Probe Method

    Science.gov (United States)

    Rouget, G.; Majidi, B.; Picard, D.; Gauvin, G.; Ziegler, D.; Mashreghi, J.; Alamdari, H.

    2017-10-01

    Carbon anodes used in Hall-Héroult electrolysis cells are involved in both electrical and chemical processes of the cell. Electrical resistivity of anodes depends on electrical properties of its constituents, of which carbon coke aggregates are the most prevalent. Electrical resistivity of coke aggregates is usually characterized according to the ISO 10143 standardized test method, which consists of measuring the voltage drop in the bed of particles between two electrically conducing plungers through which the current is also applied. Estimation of the electrical resistivity of coke particles from the resistivity of particle bed is a challenging task and needs consideration of the contribution of the interparticle void fraction and the particle/particle contact resistances. In this work, the bed resistivity was normalized by subtracting the interparticle void fraction. Then, the contact size was obtained from discrete element method simulation and the contact resistance was calculated using Holm's theory. Finally, the resistivity of the coke particles was obtained from the bed resistivity.

  16. Direct localised measurement of electrical resistivity profile in rat and embryonic chick retinas using a microprobe

    Directory of Open Access Journals (Sweden)

    Harald van Lintel

    2010-01-01

    Full Text Available We report an alternative technique to perform a direct and local measurement of electrical resistivities in a layered retinal tissue. Information on resistivity changes along the depth in a retina is important for modelling retinal stimulation by retinal prostheses. Existing techniques for resistivity-depth profiling have the drawbacks of a complicated experimental setup, a less localised resistivity probing and/or lower stability for measurements. We employed a flexible microprobe to measure local resistivity with bipolar impedance spectroscopy at various depths in isolated rat and chick embryo retinas for the first time. Small electrode spacing permitted high resolution measurements and the probe flexibility contributed to stable resistivity profiling. The resistivity was directly calculated based on the resistive part of the impedance measured with the Peak Resistance Frequency (PRF methodology. The resistivity-depth profiles for both rat and chick embryo models are in accordance with previous mammalian and avian studies in literature. We demonstrate that the measured resistivity at each depth has its own PRF signature. Resistivity profiles obtained with our setup provide the basis for the construction of an electric model of the retina. This model can be used to predict variations in parameters related to retinal stimulation and especially in the design and optimisation of efficient retinal implants.

  17. Analysis on the phase transition behavior of Cu base bulk metallic glass by electrical resistivity measurement

    International Nuclear Information System (INIS)

    Ji, Young Su; Chung, Sung Jae; Ok, Myoung-Ryul; Hong, Kyung Tae; Suh, Jin-Yoo; Byeon, Jai Won; Yoon, Jin-Kook; Lee, Kyung Hwan; Lee, Kyung Sub

    2007-01-01

    The crystallization behavior of Cu 43 Zr 43 Al 7 Ag 7 (numbers indicate at.%) bulk metallic glass was investigated using the isothermal electrical resistivity measurements at 450 deg. C in the supercooled liquid region. The crystallization process is a single step phase transformation. To analyze the electrical resistivity reduction, microstructure evolutions were analyzed using differential scanning calorimetry, X-ray diffraction, transmission electron microscopy and small-angle X-ray scattering. The Avrami parameter of the electrical resistivity reduction step was 1.73, indicating that the crystallization process is a diffusion-controlled growth of intermetallic compounds with decreasing nucleation rate

  18. Self-Diagnosis of Damage in Carbon Fiber Reinforced Composites Using Electrical Residual Resistance Measurement

    Energy Technology Data Exchange (ETDEWEB)

    Kang, Ji Ho [KAERI, Daejeon (Korea, Republic of)

    2009-08-15

    The objective of this research was to develop a practical integrated approach using extracted features from electrical resistance measurements and coupled electromechanical models of damage, for in-situ damage detection and sensing in carbon fiber reinforced plastic(CFRP) composites. To achieve this objective, we introduced specific known damage (in terms of type, size, and location) into CFRP laminates and established quantitative relationships with the electrical resistance measurements. For processing of numerous measurement data, an autonomous data acquisition system was devised. We also established a specimen preparation procedure and a method for electrode setup. Coupon and panel CFRP laminate specimens with several known damage were tested. Coupon specimens with various sizes of artificial delaminations obtained by inserting Teflon film were manufactured and the resistance was measured. The measurement results showed that increase of delamination size led to increase of resistance implying that it is possible to sense the existence and size of delamination. A quasi-isotropic panel was manufactured and electrical resistance was measured. Then three different sizes of holes were drilled at a chosen location. The panel was prepared using the established procedures with six electrode connections on each side making a total of twenty-four electrodes. Vertical, horizontal, and diagonal pairs of electrodes were chosen and the resistance was measured. The measurement results showed the possibility of the established measurement system for an in-situ damage detection method for CFRP composite structures.

  19. Real-time particle volume fraction measurement in centrifuges by wireless electrical resistance detector

    International Nuclear Information System (INIS)

    Nagae, Fumiya; Okawa, Kazuya; Matsuno, Shinsuke; Takei, Masahiro; Zhao Tong; Ichijo, Noriaki

    2015-01-01

    In this study, wireless electrical resistance detector is developed as first step in order to develop electrical resistance tomography (ERT) that are attached wireless communication, and miniaturized. And the particle volume fraction measurement results appropriateness is qualitatively examined. The real-time particle volume fraction measurement is essential for centrifuges, because rotational velocity and supply should be controlled based on the results in order to obtain the effective separation, shorten process time and save energy. However, a technique for the particle volume fraction measurement in centrifuges has not existed yet. In other words, the real-time particle volume fraction measurement in centrifuges becomes innovative technologies. The experiment device reproduces centrifugation in two-phase using particle and salt solution as measuring object. The particle concentration is measured changing rotational velocity, supply and measurement section position. The measured concentration changes coincide with anticipated tendency of concentration changes. Therefore the particle volume fraction measurement results appropriateness are qualitatively indicated. (author)

  20. Evaluation of sugar yeast consumption by measuring electrical medium resistance

    Directory of Open Access Journals (Sweden)

    Martin Lucas Zamora

    2013-12-01

    Full Text Available The real-time monitoring of alcoholic fermentation (sugar consumption is very important in industrial processes. Several techniques (i.e., using a biosensor have been proposed to realize this goal. In this work, we propose a new method to follow sugar yeast consumption. This novel method is based on the changes in the medium resistance (Rm that are induced by the CO2 bubbles produced during a fermentative process. We applied a 50-mV and 700-Hz signal to 75 ml of a yeast suspension in a tripolar cell. A gold electrode was used as the working electrode, whereas an Ag/AgCl electrode and a stainless-steel electrode served as the reference and counter electrodes, respectively. We then added glucose to the yeast suspension and obtained a 700% increase in the Rm after 8 minutes. The addition of sucrose instead of glucose as the carbon source resulted in a 1200% increase in the Rm. To confirm that these changes are the result of CO2 bubbles in the fermentation medium, we designed a tetrapolar cell in which CO2 gas was insufflated at the bottom of the cell and concluded that the changes were due to CO2 bubbles produced during the fermentation. Consequently, this new method is a low-cost and rapid technology to follow the sugar consumption in yeast.

  1. Electrical Methods: Resistivity Methods

    Science.gov (United States)

    Surface electrical resistivity surveying is based on the principle that the distribution of electrical potential in the ground around a current-carrying electrode depends on the electrical resistivities and distribution of the surrounding soils and rocks.

  2. A new contact electric resistance technique for in-situ measurement of the electric resistance of surface films on metals in electrolytes at high temperatures and pressures

    International Nuclear Information System (INIS)

    Saario, T.; Marichev, V.A.

    1993-01-01

    Surface films play a major role in corrosion assisted cracking. A new Contact Electric Resistance (CER) method has been recently developed for in situ measurement of the electric resistance of surface films. The method has been upgraded for high temperature high pressure application. The technique can be used for any electrically conductive material in any environment including liquid, gas or vacuum. The technique has been used to determine in situ the electric resistance of films on metals during adsorption of water and anions, formation and destruction of oxides and hydrides, electroplating of metals and to study the electric resistance of films on semiconductors. The resolution of the CER technique is 10 -9 Ω, which corresponds to about 0.03 monolayers of deposited copper during electrochemical deposition Cu/Cu 2+ . Electric resistance data can be measured with a frequency of the order of one hertz, which enables one to follow in situ the kinetics of surface film related processes. The kinetics of these processes and their dependence on the environment, temperature, pH and electrochemical potential can be investigated

  3. Evaluation of metal–nanowire electrical contacts by measuring contact end resistance

    International Nuclear Information System (INIS)

    Park, Hongsik; Beresford, Roderic; Xu, Jimmy; Ha, Ryong; Choi, Heon-Jin; Shin, Hyunjung

    2012-01-01

    It is known, but often unappreciated, that the performance of nanowire (NW)-based electrical devices can be significantly affected by electrical contacts between electrodes and NWs, sometimes to the extent that it is really the contacts that determine the performance. To correctly understand and design NW device operation, it is thus important to carefully measure the contact resistance and evaluate the contact parameters, specific contact resistance and transfer length. A four-terminal pattern or a transmission line model (TLM) pattern has been widely used to measure contact resistance of NW devices and the TLM has been typically used to extract contact parameters of NW devices. However, the conventional method assumes that the electrical properties of semiconducting NW regions covered by a metal are not changed after electrode formation. In this study, we report that the conventional methods for contact evaluation can give rise to considerable errors because of an altered property of the NW under the electrodes. We demonstrate that more correct contact resistance can be measured from the TLM pattern rather than the four-terminal pattern and correct contact parameters including the effects of changed NW properties under electrodes can be evaluated by using the contact end resistance measurement method. (paper)

  4. Risk analysis and detection of thrombosis by measurement of electrical resistivity of blood.

    Science.gov (United States)

    Sapkota, Achyut; Asakura, Yuta; Maruyama, Osamu; Kosaka, Ryo; Yamane, Takashi; Takei, Masahiro

    2013-01-01

    Monitoring of thrombogenic process is very important in ventricular assistance devices (VADs) used as temporary or permanent measures in patients with advanced heart failure. Currently, there is a lack of a system which can perform a real-time monitoring of thrombogenic activity. Electrical signals vary according to the change in concentration of coagulation factors as well as the distribution of blood cells, and thus have potential to detect the thrombogenic process in an early stage. In the present work, we have made an assessment of an instrumentation system exploiting the electrical properties of blood. The experiments were conducted using bovine blood. Electrical resistance tomography with eight-electrode sensor was used to monitor the spatio-temporal change in electrical resistivity of blood in thrombogenic and non-thrombogenic condition. Under non-thrombogenic condition, the resistivity was uniform across the cross-section and average resistivity monotonically decreased with time before remaining almost flat. In contrary, under thrombogenic condition, there was non-uniform distribution across the cross-section, and average resistivity fluctuated with time.

  5. Contribution of soil electric resistivity measurements to the studies on soil/grapevine water relations

    Directory of Open Access Journals (Sweden)

    Etienne Goulet

    2006-06-01

    Full Text Available The classical techniques that allow to quantify the soil water status such as the gravimetric method or the use of neutrons probes do not give access to the volume of soil explored by the plant root system. On the contrary, electric tomography can be used to have a global vision on the water exchange area between soil and plant. The measurement of soil electric resistivity, as a non destructive, spatially integrative technique, has recently been introduced into viticulture. The use of performing equipment and adapted software allows for rapid data processing and gives the possibility to spatialize the variations of soil texture or humidity in two or three dimensions. Soil electric resistivity has been tested for the last three years at the Experimental Unit on Grapevine and Vine, INRA, Angers, France, to study the water supply to the vine in different “terroir” conditions. Resistivity measurements were carried out with the resistivity meter Syscal R1+ (Iris Instruments, France equipped with 21 electrodes. Those electrodes were lined up on the soil surface in a direction perpendiculary to 5 grapevine rows with an electrode spacing of 0.5 m. and a dipole-dipole arrangement. Resistivity measurements were performed on the same place at different times in order to study soil moisture variations. This experimental set up has permitted to visualise the soil stratification and individualize some positive electric anomalies corresponding to preferential drying ; this desiccation could be attributed to grapevine root activity. The soil bulk subject to the water up-take could be defined more precisely and in some types of soil, available water may even be quantified. Terroir effect on grapevine root activity has also been shown up on two different experimental parcels through electric tomography and first results indicate that it is possible to monitor the effects of soil management (inter-row grassing or different rootstocks on the water supply to the

  6. A setup for measuring the Seebeck coefficient and the electrical resistivity of bulk thermoelectric materials

    Science.gov (United States)

    Fu, Qiang; Xiong, Yucheng; Zhang, Wenhua; Xu, Dongyan

    2017-09-01

    This paper presents a setup for measuring the Seebeck coefficient and the electrical resistivity of bulk thermoelectric materials. The sample holder was designed to have a compact structure and can be directly mounted in a standard cryostat system for temperature-dependent measurements. For the Seebeck coefficient measurement, a thin bar-shaped sample is mounted bridging two copper bases; and two ceramic heaters are used to generate a temperature gradient along the sample. Two type T thermocouples are used to determine both temperature and voltage differences between two widely separated points on the sample. The thermocouple junction is flattened into a disk and pressed onto the sample surface by using a spring load. The flexible fixation method we adopted not only simplifies the sample mounting process but also prevents thermal contact deterioration due to the mismatch of thermal expansion coefficients between the sample and other parts. With certain modifications, the sample holder can also be used for four-probe electrical resistivity measurements. High temperature measurements are essential for thermoelectric power generation. The experimental system we developed is capable of measuring the Seebeck coefficient and the electrical resistivity of bulk thermoelectric materials in a wide temperature range from 80 to 500 K, which can be further extended to even higher temperatures. Measurements on two standard materials, constantan and nickel, confirmed the accuracy and the reliability of the system.

  7. Electrical resistivity probes

    Science.gov (United States)

    Lee, Ki Ha; Becker, Alex; Faybishenko, Boris A.; Solbau, Ray D.

    2003-10-21

    A miniaturized electrical resistivity (ER) probe based on a known current-voltage (I-V) electrode structure, the Wenner array, is designed for local (point) measurement. A pair of voltage measuring electrodes are positioned between a pair of current carrying electrodes. The electrodes are typically about 1 cm long, separated by 1 cm, so the probe is only about 1 inch long. The electrodes are mounted to a rigid tube with electrical wires in the tube and a sand bag may be placed around the electrodes to protect the electrodes. The probes can be positioned in a borehole or on the surface. The electrodes make contact with the surrounding medium. In a dual mode system, individual probes of a plurality of spaced probes can be used to measure local resistance, i.e. point measurements, but the system can select different probes to make interval measurements between probes and between boreholes.

  8. Effects of contact resistance on electrical conductivity measurements of SiC-based materials

    Energy Technology Data Exchange (ETDEWEB)

    Youngblood, G.E.; Thomsen, E.C.; Henager, C.H., E-mail: chuck.henager@pnnl.gov

    2013-11-15

    A combination 2/4-probe method was used to measure electrical resistances across a pure, monolithic CVD-SiC disc sample with contact resistance at the SiC/metallic electrode interfaces. By comparison of the almost simultaneous 2/4-probe measurements, the specific contact resistance (R{sub c}) and its temperature dependence were determined for two types (sputtered gold and porous nickel) electrodes from room temperature (RT) to ∼973 K. The R{sub c}-values behaved similarly for each type of metallic electrode: R{sub c} > ∼1000 Ω cm{sup 2} at RT, decreasing continuously to ∼1–10 Ω cm{sup 2} at 973 K. The temperature dependence of the inverse R{sub c} indicated thermally activated electrical conduction across the SiC/metallic interface with an apparent activation energy of ∼0.3 eV. For the flow channel insert application in a fusion reactor blanket, contact resistance potentially could reduce the transverse electrical conductivity by about 50%.

  9. Influence of plant roots on electrical resistivity measurements of cultivated soil columns

    Science.gov (United States)

    Maloteau, Sophie; Blanchy, Guillaume; Javaux, Mathieu; Garré, Sarah

    2016-04-01

    Electrical resistivity methods have been widely used for the last 40 years in many fields: groundwater investigation, soil and water pollution, engineering application for subsurface surveys, etc. Many factors can influence the electrical resistivity of a media, and thus influence the ERT measurements. Among those factors, it is known that plant roots affect bulk electrical resistivity. However, this impact is not yet well understood. The goals of this experiment are to quantify the effect of plant roots on electrical resistivity of the soil subsurface and to map a plant roots system in space and time with ERT technique in a soil column. For this research, it is assumed that roots system affect the electrical properties of the rhizosphere. Indeed the root activity (by transporting ions, releasing exudates, changing the soil structure,…) will modify the rhizosphere electrical conductivity (Lobet G. et al, 2013). This experiment is included in a bigger research project about the influence of roots system on geophysics measurements. Measurements are made on cylinders of 45 cm high and a diameter of 20 cm, filled with saturated loam on which seeds of Brachypodium distachyon (L.) Beauv. are sowed. Columns are equipped with electrodes, TDR probes and temperature sensors. Experiments are conducted at Gembloux Agro-Bio Tech, in a growing chamber with controlled conditions: temperature of the air is fixed to 20° C, photoperiod is equal to 14 hours, photosynthetically active radiation is equal to 200 μmol m-2s-1, and air relative humidity is fixed to 80 %. Columns are fully saturated the first day of the measurements duration then no more irrigation is done till the end of the experiment. The poster will report the first results analysis of the electrical resistivity distribution in the soil columns through space and time. These results will be discussed according to the plant development and other controlled factors. Water content of the soil will also be detailed

  10. Coupled stress-strain and electrical resistivity measurements on copper based shape memory single crystals

    Directory of Open Access Journals (Sweden)

    Gonzalez Cezar Henrique

    2004-01-01

    Full Text Available Recently, electrical resistivity (ER measurements have been done during some thermomechanical tests in copper based shape memory alloys (SMA's. In this work, single crystals of Cu-based SMA's have been studied at different temperatures to analyse the relationship between stress (s and ER changes as a function of the strain (e. A good consistency between ER change values is observed in different experiments: thermal martensitic transformation, stress induced martensitic transformation and stress induced reorientation of martensite variants. During stress induced martensitic transformation (superelastic behaviour and stress induced reorientation of martensite variants, a linear relationship is obtained between ER and strain as well as the absence of hys teresis. In conclusion, the present results show a direct evidence of martensite electrical resistivity anisotropy.

  11. Electrical limit of silver nanowire electrodes: Direct measurement of the nanowire junction resistance

    KAUST Repository

    Selzer, Franz; Floresca, Carlo; Kneppe, David; Bormann, Ludwig; Sachse, Christoph; Weiß , Nelli; Eychmü ller, Alexander; Amassian, Aram; Mü ller-Meskamp, Lars; Leo, Karl

    2016-01-01

    We measure basic network parameters of silvernanowire (AgNW) networks commonly used as transparent conductingelectrodes in organic optoelectronic devices. By means of four point probing with nanoprobes, the wire-to-wire junction resistance and the resistance of single nanowires are measured. The resistanceRNW of a single nanowire shows a value of RNW=(4.96±0.18) Ω/μm. The junction resistanceRJ differs for annealed and non-annealed NW networks, exhibiting values of RJ=(25.2±1.9) Ω (annealed) and RJ=(529±239) Ω (non-annealed), respectively. Our simulation achieves a good agreement between the measured network parameters and the sheet resistanceRS of the entire network. Extrapolating RJ to zero, our study show that we are close to the electrical limit of the conductivity of our AgNW system: We obtain a possible RS reduction by only ≈20% (common RS≈10 Ω/sq). Therefore, we expect further performance improvements in AgNW systems mainly by increasing NW length or by utilizing novel network geometries.

  12. Electrical limit of silver nanowire electrodes: Direct measurement of the nanowire junction resistance

    KAUST Repository

    Selzer, Franz

    2016-04-19

    We measure basic network parameters of silvernanowire (AgNW) networks commonly used as transparent conductingelectrodes in organic optoelectronic devices. By means of four point probing with nanoprobes, the wire-to-wire junction resistance and the resistance of single nanowires are measured. The resistanceRNW of a single nanowire shows a value of RNW=(4.96±0.18) Ω/μm. The junction resistanceRJ differs for annealed and non-annealed NW networks, exhibiting values of RJ=(25.2±1.9) Ω (annealed) and RJ=(529±239) Ω (non-annealed), respectively. Our simulation achieves a good agreement between the measured network parameters and the sheet resistanceRS of the entire network. Extrapolating RJ to zero, our study show that we are close to the electrical limit of the conductivity of our AgNW system: We obtain a possible RS reduction by only ≈20% (common RS≈10 Ω/sq). Therefore, we expect further performance improvements in AgNW systems mainly by increasing NW length or by utilizing novel network geometries.

  13. Thermal strain measurement of EAST W/Cu divertor structure using electric resistance strain gauges

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Xingli [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei, 230031 (China); Science Island Branch of Graduate School, University of Science & Technology of China, Hefei, 230031 (China); Wang, Wanjing, E-mail: wjwang@ipp.ac.cn [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei, 230031 (China); Wang, Jichao [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei, 230031 (China); Wei, Ran; Sun, Zhaoxuan [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei, 230031 (China); Science Island Branch of Graduate School, University of Science & Technology of China, Hefei, 230031 (China); Li, Qiang; Xie, Chunyi [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei, 230031 (China); Chen, Hong-En; Wang, Kaiqiang; Wu, Lei; Chen, Zhenmao [State Key Lab for Strength and Vibration of Mechanical Structures, Xi’an Jiaotong University (China); Luo, Guang-Nan [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei, 230031 (China); Science Island Branch of Graduate School, University of Science & Technology of China, Hefei, 230031 (China); Hefei Center for Physical Science and Technology, Hefei, 230022 (China); Hefei Science Center of Chinese Academy of Sciences, Hefei, 230027 (China)

    2016-12-15

    Highlights: • To understand the service behavior of W/Cu divertor, an electrical resistance strain gauge system had been introduced in a thermal strain measurement experiment. • The measurement system successfully finished the experiment and obtained valued thermal strain data. • Two thermomechanical analyses had also been carried out and compared with the measurement results. • Experiment results corresponded well to simulations and threw a light upon the failure of W/Cu divertor in the previous baking tests. - Abstract: W/Cu divertor has complex structure and faces extreme work environment in EAST Tokamak device. To measure its thermal strain shall be a valued way to understand its service behavior and then optimize its design and manufacturing process. This work presents a preliminary study on measuring thermal strain of EAST W/Cu divertor structure using electric resistance strain gauges. Eight gauges had been used in the experiment and the heating temperature had been set to 230 °C with respect to the work temperature. To realize the measuring experiment, an appropriate fixing method of gauges in divertor narrow spaces had been taken and tested, which could not only withstand high temperature but also had no damage to the divertor sample. The measurement results were that three gauges showed positive strain while other three showed negative strain after having been compensated, which corresponded to tensile stress and compressed stress respectively. Two thermomechanical simulations had also been carried out and used for comparing with the experiment.

  14. Electro-location, tomography and porosity measurements in geotechnical centrifuge models based on electrical resistivity concepts

    Science.gov (United States)

    Li, Zhihua

    This research was focused on the development of electrical techniques for soil characterization and soil dynamic behavior assessment. The research carried out mainly includes (1) development of a needle probe tool for assessment of soil spatial variability in terms of porosity with high-resolution in the centrifuge testing; (2) development of an electro-location technique to accurately detect buried objects' movements inside the soil during dynamic events; (3) collaborative development of a new electrode switching system to implement electrical resistivity tomography, and electro-location with high speed and high resolution. To assess soil spatial variability with high-resolution, electrical needle probes with different tip shapes were developed to measure soil electrical resistivity. After normalizing soil resistivity by pore fluid resistivity, this information can be correlated to soil porosity. Calibrations in laboratory prepared soils were conducted. Loosening due to insertion of needle probes was evaluated. A special needle probe tool, along with data acquisition and data processing tools were developed to be operated by the new NEES robot on the centrifuge. The needle probes have great potential to resolve interfaces between soil layers and small local porosity variations with a spatial resolution approximately equal to the spacing between electrodes (about half of the probe diameter). A new electrode switching system was developed to accurately detect buried objects' movements using a new electro-location scheme. The idea was to establish an electromagnetic field in a centrifuge model by injecting low-frequency alternating currents through pairs of boundary electrodes. The locations of buried objects are related to the potentials measured on them. A closed form expression for the electric field in a rectangular specimen with insulated boundaries was obtained based on the method of images. Effects of sampling parameters on spatial resolution and tradeoffs

  15. The Method of Measured Electrical Resistivity in Studying Phase Transformations in Zr1Nb Alloy

    International Nuclear Information System (INIS)

    Gritsina, V.M.; Klimenko, S.P.; Chernyaeva, T.P.

    2006-01-01

    The paper systematically arranges and analyzes the data on the methods of research into α ↔ β transformation process in zirconium alloys, as well as capabilities and information provided by each method. A special emphasis is put on the method of measured electrical resistivity. The authors also present the results of their own research into α ↔ β transformation process in Zr1Nb alloy (in the material of Zr+1% Nb tubing produced in Ukraine from calciothermal zirconium). The ρ →T curve was used to define the maximum and minimum values for transformation temperatures. Combined processing of the phase data on Zr+1% Nb found in literature and obtained from measured resistivity suggests that transformation process happens in several stages. The maximum value on the ρ → T curve corresponds to the beginning of stage 3, whereas the minimum - to its completion; as suggested by the pooled data, accounts for over 95% of the total volume of the material

  16. CT-scan-monitored electrical-resistivity measurements show problems achieving homogeneous saturation

    International Nuclear Information System (INIS)

    Sprunt, E.S.; Davis, R.M.; Muegge, E.L.; Desai, K.P.

    1991-01-01

    This paper reports on x-ray computerized tomography (CT) scans obtained during measurement of the electrical resistivity of core samples which revealed some problems in obtaining uniform saturation along the lengths of the samples. The electrical resistivity of core samples is measured as a function of water saturation to determine the saturation exponent used in electric-log interpretation. An assumption in such tests is that the water saturation is uniformly distributed. Failure of this assumption can result in errors in the determination of the saturation exponent. Three problems were identified in obtaining homogeneous water saturation in two samples of a Middle Eastern carbonate grainstone: a stationary front formed in one sample at 1-psi oil/brine capillary pressure, a moving front formed at oil/brine capillary pressure ≤4 psi in samples tested in fresh mixed-wettability and cleaned water-wet states, and the heterogeneous fluid distribution caused by a rapidly moving front did not dissipate when the capillary pressure was eliminated in the samples

  17. CT-scan-monitored electrical resistivity measurements show problems achieving homogeneous saturation

    International Nuclear Information System (INIS)

    Sprunt, E.S.; Coles, M.E.; Davis, R.M.; Muegge, E.L.; Desai, K.P.

    1991-01-01

    X-ray CT scans obtained during measurement of the electrical resistivity of core samples revealed some problems in obtaining uniform saturation along the length of the sample. In this paper the electrical resistivity of core samples is measured as a function of water saturation to determine the saturation exponent, which is used in electric log interpretation. An assumption in such tests is that the water saturation is uniformly distributed. Failure of this assumption can result in errors in the determination of the saturation exponent. Three problems were identified in obtaining homogeneous water saturation in two samples of a Middle Eastern carbonate grainstone. A stationary front formed in one sample at 1 psi oil/brine capillary pressure. A moving front formed at oil/brine capillary pressures of 4 psi or less in both samples tested, in both a fresh mixed-wettability state and in a cleaned water-wet state. In these samples, the heterogeneous fluid distribution caused by a rapidly moving front did not dissipate when the capillary pressure was eliminated

  18. Evaluation of the Mechanical Properties of Gray Cast Iron Using Electrical Resistivity Measurement

    Directory of Open Access Journals (Sweden)

    Bieroński M.

    2016-12-01

    Full Text Available In this paper an attempt to determine the relationship between the electrical resistivity and the tensile strength and hardness of cast iron of carbon equivalent in the range from 3.93% to 4.48%. Tests were performed on the gray cast iron for 12 different melts with different chemical composition. From one melt poured 6 samples. Based on the study of mechanical and electro-resistive determined variation characteristics of tensile strength, hardness and resistivity as a function of the carbon equivalent. Then, regression equations were developed as power functions describing the relationship between the resistivity of castings and their tensile strength and hardness. It was found a high level of regression equations to measuring points, particularly with regard to the relationship Rm=f(ρ. The obtained preliminary results indicate the possibility of application of the method of the resistance to rapid diagnostic casts on the production line, when we are dealing with repeatable production, in this case non variable geometry of the product for which it has been determinated before a regression equation.

  19. Heat dissipation due to ferromagnetic resonance in a ferromagnetic metal monitored by electrical resistance measurement

    International Nuclear Information System (INIS)

    Yamanoi, Kazuto; Yokotani, Yuki; Kimura, Takashi

    2015-01-01

    The heat dissipation due to the resonant precessional motion of the magnetization in a ferromagnetic metal has been investigated. We demonstrated that the temperature during the ferromagnetic resonance can be simply detected by the electrical resistance measurement of the Cu strip line in contact with the ferromagnetic metal. The temperature change of the Cu strip due to the ferromagnetic resonance was found to exceed 10 K, which significantly affects the spin-current transport. The influence of the thermal conductivity of the substrate on the heating was also investigated

  20. Investigation of the Interaction between Perovskite Films with Moisture via in Situ Electrical Resistance Measurement.

    Science.gov (United States)

    Hu, Long; Shao, Gang; Jiang, Tao; Li, Dengbing; Lv, Xinlin; Wang, Hongya; Liu, Xinsheng; Song, Haisheng; Tang, Jiang; Liu, Huan

    2015-11-18

    Organometal halide perovskites have recently emerged as outstanding semiconductors for solid-state optoelectronic devices. Their sensitivity to moisture is one of the biggest barriers to commercialization. In order to identify the effect of moisture in the degradation process, here we combined the in situ electrical resistance measurement with time-resolved X-ray diffraction analysis to investigate the interaction of CH3NH3PbI(3-x)Cl(x) perovskite films with moisture. Upon short-time exposure, the resistance of the perovskite films decreased and it could be fully recovered, which were ascribed to a mere chemisorption of water molecules, followed by the reversible hydration into CH3NH3PbI(3-x)Cl(x)·H2O. Upon long-time exposure, however, the resistance became irreversible due to the decomposition into PbI2. The results demonstrated the formation of monohydrated intermediate phase when the perovskites interacted with moisture. The role of moisture in accelerating the thermal degradation at 85 °C was also demonstrated. Furthermore, our study suggested that the perovskite films with fewer defects may be more inherently resistant to moisture.

  1. Electrical-conductivity measurements of leachates for the rapid assessment of wasteform corrosion resistance

    International Nuclear Information System (INIS)

    Sales, B.C.; Petek, M.; Boatner, L.A.

    1982-01-01

    Measurements of the electrical conductivity of leachate solutions as a function of time can be used as an efficient, informative means of evaluation and comparison in the development of nuclear waste forms and in the preliminary analysis of their corrosion resistance in distilled water. Three separate applications of this technique are described in this work. These are: (1) its use in the optimization of the corrosion resistance of a crystalline wasteform (monazite); (2) a study of the protective ability of the surface layer (gel layer) which forms on the nuclear waste glass Frit 21 + 20 wt % SRW in distilled water; and (3) making comparisons of the overall corrosion resistance of three different nuclear wasteforms (i.e., monazite, SYNROC, and borosilicate glass). A complete solution analysis of the borosilicate glass leachate and a straightforward analysis of the conductivity results agree to within +-20%. In the absence of a complete, time consuming solution analysis, conductivity measurements can be used to estimate reliably the total ionic concentration in the leachate to within a factor of 2

  2. Electrical Resistance and Acoustic Emission Measurements for Monitoring the Structural Behavior of CFRP Laminate

    KAUST Repository

    Zhou, Wei

    2015-07-12

    Electrical resistance and acoustic emission (AE) measurement are jointly used to monitor the degradation in CFRP laminates subjected to tensile tests. The objective of this thesis is to perform a synergertic analysis between a passive and an active methods to better access how these perform when used for Structural Health Moni- toring (SHM). Laminates with three different stacking sequences: [0]4, [02/902]s and [+45/ − 45]2s are subjected to monotonic and cyclic tensile tests. In each laminate, we carefully investigate which mechanisms of degradation can or cannot be detect- ed by each technique. It is shown that most often, that acoustic emission signals start before any electrical detection is possible. This is is explained based on the redundance of the electrical network that makes it less sensitive to localized damages. Based on in depth study of AE signals clustering, a new classification is proposed to recognize the different damage mechanims based on only two parameters: the RA (rise time/amplitude) and the duration of the signal.

  3. Studies on Al-Mg solid solutions using electrical resistivity and microhardness measurements

    Energy Technology Data Exchange (ETDEWEB)

    Gaber, A.; Afify, N.; El-Halawany, S.M.; Mossad, A. [Assiut Univ. (Egypt). Dept. of Physics

    1999-08-01

    Al-C at% Mg alloys (C = 0.82, 1.84, 3.76, 5.74 and 12.18) have been selected for this study. From the electrical resistivity measurements it is concluded that the resistivity increment of Al-Mg alloys (in a solid solution state) is proportional to the atomic fractional constituents (Mg and Al) as {delta}{rho}{sub all} = 64.66 c(1-c) {mu}{omega} cm. In addition, both the temperature coefficient of resistivity, {alpha}{sub all} and the relaxation time of the free electrons {tau}{sub all} in the alloys diminish with increasing the solute Mg concentration. The increase of the scattering power, {eta}, with increasing C is interpreted to be due to the contribution of electron-impurity scattering. The percentage increase due to electron-impurity scattering per one atomic percent Mg has been determined as 12.99%. The Debye temperature {theta} decreases as the Mg concentration increases. The microhardness results showed that the solid solution hardening obeys the relation {delta}HV{sub s} = 135.5C{sup 0.778} MPa which is comparable to the theory of solid solution hardening for all alloys; {delta}HV{sub s} {approx} C{sup 0.5-0.67} MPa. (orig.)

  4. Improved characterisation and modelling of measurement errors in electrical resistivity tomography (ERT) surveys

    Science.gov (United States)

    Tso, Chak-Hau Michael; Kuras, Oliver; Wilkinson, Paul B.; Uhlemann, Sebastian; Chambers, Jonathan E.; Meldrum, Philip I.; Graham, James; Sherlock, Emma F.; Binley, Andrew

    2017-11-01

    Measurement errors can play a pivotal role in geophysical inversion. Most inverse models require users to prescribe or assume a statistical model of data errors before inversion. Wrongly prescribed errors can lead to over- or under-fitting of data; however, the derivation of models of data errors is often neglected. With the heightening interest in uncertainty estimation within hydrogeophysics, better characterisation and treatment of measurement errors is needed to provide improved image appraisal. Here we focus on the role of measurement errors in electrical resistivity tomography (ERT). We have analysed two time-lapse ERT datasets: one contains 96 sets of direct and reciprocal data collected from a surface ERT line within a 24 h timeframe; the other is a two-year-long cross-borehole survey at a UK nuclear site with 246 sets of over 50,000 measurements. Our study includes the characterisation of the spatial and temporal behaviour of measurement errors using autocorrelation and correlation coefficient analysis. We find that, in addition to well-known proportionality effects, ERT measurements can also be sensitive to the combination of electrodes used, i.e. errors may not be uncorrelated as often assumed. Based on these findings, we develop a new error model that allows grouping based on electrode number in addition to fitting a linear model to transfer resistance. The new model explains the observed measurement errors better and shows superior inversion results and uncertainty estimates in synthetic examples. It is robust, because it groups errors together based on the electrodes used to make the measurements. The new model can be readily applied to the diagonal data weighting matrix widely used in common inversion methods, as well as to the data covariance matrix in a Bayesian inversion framework. We demonstrate its application using extensive ERT monitoring datasets from the two aforementioned sites.

  5. In situ measurement system of electric resistivity for outcrop investigation; Roto de shiyodekiru denkihi teiko keisoku system

    Energy Technology Data Exchange (ETDEWEB)

    Nakagawa, K; Tamura, T [Osaka City Univ., Osaka (Japan). Faculty of Science; Morikawa, T [Osaka Prefectural Government, Osaka (Japan)

    1997-05-27

    A simplified electrical resistivity measuring device has been developed as a trial for field and laboratory uses, and some measurements were conducted. For this device, four probe electrodes are penetrated in the clay specimen, to calculate the resistivity from the voltage between both ends of the reference resistance connected with current electrodes in a series and the voltage between intermediate two voltage electrodes. It can be used in the field measurements. For the measurements, specimens of marine and lacustrine clayey sediments with clear stratigraphic levels in southern Osaka Group were used. In the laboratory, in addition to basic physical tests, diatom analysis and measurements of conductivity of clay suspension were also conducted. As a result of the experiments, the electric resistivity of marine clay obtained at the outcrop was lower than lacustrine clay as expected. The value of the former was a half of that of the latter. The frequency dependence in the high frequency region above 1 MHz was the reverse. The difference in electrical resistivity values between non-agitated specimens was about four times. The electrical resistivity of clay suspensions varied in two orders. 3 refs., 9 figs.

  6. Ion permeability of artificial membranes evaluated by diffusion potential and electrical resistance measurements.

    Science.gov (United States)

    Shlyonsky, Vadim

    2013-12-01

    In the present article, a novel model of artificial membranes that provides efficient assistance in teaching the origins of diffusion potentials is proposed. These membranes are made of polycarbonate filters fixed to 12-mm plastic rings and then saturated with a mixture of creosol and n-decane. The electrical resistance and potential difference across these membranes can be easily measured using a low-cost volt-ohm meter and home-made Ag/AgCl electrodes. The advantage of the model is the lack of ionic selectivity of the membrane, which can be modified by the introduction of different ionophores to the organic liquid mixture. A membrane treated with the mixture containing valinomycin generates voltages from -53 to -25 mV in the presence of a 10-fold KCl gradient (in to out) and from -79 to -53 mV in the presence of a bi-ionic KCl/NaCl gradient (in to out). This latter bi-ionic gradient potential reverses to a value from +9 to +20 mV when monensin is present in the organic liquid mixture. Thus, the model can be build stepwise, i.e., all factors leading to the development of diffusion potentials can be introduced sequentially, helping students to understand the quantitative relationships of ionic gradients and differential membrane permeability in the generation of cell electrical signals.

  7. Delamination Detection in Carbon Fibre Reinforced Composites Using Electrical Resistance Measurement

    International Nuclear Information System (INIS)

    Kovalovs, A; Rucevskis, S; Kulakov, V; Aniskevich, A

    2016-01-01

    In the present study 2-D numerical analysis of strip-type laminated composite specimens with and without damage is considered and numerical investigation is carried out by using a finite element method. The surface and oblique resistances are numerically calculated according to the two-probe and four-probe methods. The electrical conductivity of the composite laminate in the longitudinal direction is constant, while the electrical conductivity in the through-thickness direction is used as a variable in the parametric study. The resistance change due to delamination for each case is estimated by comparing the obtained resistance with the corresponding resistance of the specimen without delamination. Applicability and effectiveness of the proposed method are investigated by using various lengths of a delaminated crack in the specimen. (paper)

  8. Ion Permeability of Artificial Membranes Evaluated by Diffusion Potential and Electrical Resistance Measurements

    Science.gov (United States)

    Shlyonsky, Vadim

    2013-01-01

    In the present article, a novel model of artificial membranes that provides efficient assistance in teaching the origins of diffusion potentials is proposed. These membranes are made of polycarbonate filters fixed to 12-mm plastic rings and then saturated with a mixture of creosol and "n"-decane. The electrical resistance and potential…

  9. Study by electrical resistivity measurements of the radiation induced defects in gold-copper alloys

    International Nuclear Information System (INIS)

    Alamo, A.

    1983-09-01

    Point defect production rate in Cu 3 Au and CuAu ordered and disordered alloys was studied by electrical resistivity measurements, as function of electron energy ranging from 0.4 to 2.5 MeV. The irradiations were performed at 20 K. The production curves are analysed using a displacement model for diatomic materials and the following values are found for the average displacement threshold energies: Esub(d)sup(Cu) approximately 22 eV and Esub(d)sup(Au) approximately 18 eV, for both alloys. Elementary defect migration was examined during isochronal annealing performed after irradiations. A simple type of self-interstitial seems to migrate in the ordered alloys: probably a split-interstitial of Cu-Cu type. Interstitial migration seems to be very difficult and complex in the disordered alloys. Vacancy mobility was detected after recovery at temperature above 300 K and was responsible of an increase of long range order. Fast neutron irradiations at 20 K produce disordering in the initially ordered alloys. Ratios of 38 and 18 antistructure defects per atomic displacement are estimated for Cu 3 Au and CuAu respectively [fr

  10. The corrosion rate of copper in a bentonite test package measured with electric resistance sensors

    Energy Technology Data Exchange (ETDEWEB)

    Rosborg, Bo [Division of Surface and Corrosion Science, KTH, Stockholm (Sweden); Kosec, Tadeja; Kranjc, Andrej; Kuhar, Viljem; Legat, Andraz [Slovenian National Building and Civil Engineering Institute, Ljubljana (Slovenia)

    2012-12-15

    LOT1 test parcel A2 was exposed for six years in the Aespoe Hard Rock Laboratory, which offers a realistic environment for the conditions that will prevail in a deep repository for high-level radioactive waste disposal in Sweden. The test parcel contained copper electrodes for real-time corrosion monitoring in bentonite ring 36, where the temperature was 24 deg C, and copper coupons in bentonite rings 22 and 30, where the temperature was higher. After retrieval of the test parcel in January 2006, a bentonite test package consisting of bentonite rings 35 - 37 was placed in a container and sealed with a thick layer of paraffin. Later the same year new copper electrodes were installed in the test package. In January 2007 electric resistance (ER) sensors of pure copper with a thickness of 35 {mu}m were also installed in the test package mainly to facilitate the interpretation of the results from the real-time corrosion monitoring with electrochemical techniques. The ER measurements have shown that the corrosion rate of pure copper exposed in an oxic bentonite/ saline groundwater environment at room temperate decreases slowly with time to low but measurable values. The corrosion rates estimated from the regularly performed EIS measurements replicate the ER data. Thus, for this oxic environment in which copper acquires corrosion potentials of the order of 200 mV (SHE) or higher, electrochemical measurements provide believable data. Comparing the recorded ER data with an estimate of the average corrosion rate based on comparing cross-sections from exposed and protected sensor elements, it is obvious that the former overestimates the actual corrosion rate, which is understandable. It seems as if electrochemical measurements can provide a better estimate of the corrosion rate; however, this is quite dependent on the use of proper measuring frequencies and evaluation methods. In this respect ER measurements are more reliable. It has been shown that real-time corrosion

  11. The corrosion rate of copper in a bentonite test package measured with electric resistance sensors

    International Nuclear Information System (INIS)

    Rosborg, Bo; Kosec, Tadeja; Kranjc, Andrej; Kuhar, Viljem; Legat, Andraz

    2012-12-01

    LOT1 test parcel A2 was exposed for six years in the Aespoe Hard Rock Laboratory, which offers a realistic environment for the conditions that will prevail in a deep repository for high-level radioactive waste disposal in Sweden. The test parcel contained copper electrodes for real-time corrosion monitoring in bentonite ring 36, where the temperature was 24 deg C, and copper coupons in bentonite rings 22 and 30, where the temperature was higher. After retrieval of the test parcel in January 2006, a bentonite test package consisting of bentonite rings 35 - 37 was placed in a container and sealed with a thick layer of paraffin. Later the same year new copper electrodes were installed in the test package. In January 2007 electric resistance (ER) sensors of pure copper with a thickness of 35 μm were also installed in the test package mainly to facilitate the interpretation of the results from the real-time corrosion monitoring with electrochemical techniques. The ER measurements have shown that the corrosion rate of pure copper exposed in an oxic bentonite/ saline groundwater environment at room temperate decreases slowly with time to low but measurable values. The corrosion rates estimated from the regularly performed EIS measurements replicate the ER data. Thus, for this oxic environment in which copper acquires corrosion potentials of the order of 200 mV (SHE) or higher, electrochemical measurements provide believable data. Comparing the recorded ER data with an estimate of the average corrosion rate based on comparing cross-sections from exposed and protected sensor elements, it is obvious that the former overestimates the actual corrosion rate, which is understandable. It seems as if electrochemical measurements can provide a better estimate of the corrosion rate; however, this is quite dependent on the use of proper measuring frequencies and evaluation methods. In this respect ER measurements are more reliable. It has been shown that real-time corrosion

  12. Assessment of hydration process and mechanical properties of cemented paste backfill by electrical resistivity measurement

    Science.gov (United States)

    Xu, Wenbin; Tian, Xichun; Cao, Peiwang

    2018-04-01

    Cemented paste backfill (CPB) is an emerging mine backfill technique that allows environmentally hazardous tailings to return to the underground openings or stopes, thereby maximising the safety, efficiency and productivity of operation. Uniaxial compressive strength (UCS) is one of the most commonly used parameters for evaluating the mechanical performance of CPB; the prediction of the UCS of CPB structures from early to advanced ages is of great practical importance. This study aims to investigate the predictability of the UCS of CPB during the hydration process based on electrical resistivity (ER) measurement. For this purpose, the samples prepared at different cement-to-tailing ratios and solid contents were subjected to the ER test during the whole hydration process and UCS tests at 3, 7, 28 days of curing periods. The effect of cement-to-tailing ratio and solid content on the ER and UCS of CPB samples was obtained; the UCS values were correlated with the corresponding ER data. Microstructural analysis was also performed on CPB samples to understand the effect of microstructure on the ER data. The result shows that the ER of CPB decreases first and then increases with the speed which is faster in the previous part than the latter. The ER and UCS of CPB samples increased with increasing cement-to-tailing ratio and solid content and curing periods. A logarithmic relationship is established for each mixture in order to predict the UCS of CPB based on ER. Scanning electron microscope analyses have revealed that the microstructure of the CPB changes with the age from the initial floc to honeycomb, and eventually to the compact clumps. The ER properties of CPB samples were highly associated with their respective microstructural properties. The major output of this study is that ER test is effectively capable for a preliminary prediction of the UCS of CPB.

  13. Study on strength estimation of soil cement used in the embedded pile method by electrical resistivity measurement

    Science.gov (United States)

    Mochida, Y.; Sakurai, Y.; Indra, H.; Karimi, A. L.

    2017-11-01

    Problems caused by poor quality control and quality assurance of the pre-boring embedded pile construction, such as on domestic apartment house is still occurring nowadays. An adequate consideration for invisible risks inside or below the ground is important in pile foundation construction therefore the demand for advanced and reliable quality assurance is increase in the future. In this research, to understand the quality of the construction at early stage, the compressive strength of cement-soil mixture of pile construction after 28 days is estimated using electrical resistivity value of the mixture. More accurate measurement for electrical resistivity value is conducted by inserting the electrodes without using potassium chloride solution as a catalyst. The result showed that there is a certain tendency in the electric resistivity value at the early age regarding to the type of soil (sand, clay) mixed in. The most accurate estimation was achieved from the electric resistivity value at the first day and several days onwards, and from the compressive strength after 3 days.

  14. Gamma-ray and electrical resistivity measurements in soil with application of carbonatite and agricultural fertilizers in Distrito Federal

    International Nuclear Information System (INIS)

    Nascimento, Carlos Tadeu Carvalho do; Gaspar, Jose Carlos; Pires, Augusto Cesar Bittencourt; Ferreira, Francisco Jose Fonseca; Andrade, Leide Rovenia Miranda de

    2008-01-01

    EMBRAPA (Empresa Brasileira de Pesquisa Agropecuaria) and Brasilia University developed a research project about the viability of carbonatite rock as agricultural fertilizer. As an initial experiment, several mixtures of carbonatite, limestone, phosphorous and potassium compounds were added as fertilizers in an oxisol area (red-latosol, according with Brazilian System of Soil Classification), in Distrito Federal, central Brazil. The experiment area was divided in 56 plots (4 x 7m) and each plot received a fertilizer mixture. The purpose of this work was to verify if the addition of fertilizer mixture to the soil modified its radiometric and resistivity properties and if it is possible to identify this change. Gamma-ray and electrical resistivity measurements were obtained in an experimental area and in a natural savannah type vegetation area. The results showed that the fertilizer addition modified soil natural properties causing a small increase in K, U, Th levels and decreasing ten times electrical resistivity. A low contrast of radiation was observed between plots, and then it was not possible to differentiate the several treatments in base of gamma-ray measurements. Electrical resistivity was efficient to identify three groups of plots related to mixtures characteristics, respectively with phosphorous, potassium and limestone / carbonatite predominance. (author)

  15. In-situ electric resistance measurements and annealing effects of graphite exposed to swift heavy ions

    International Nuclear Information System (INIS)

    Fernandes, Sandrina; Pellemoine, Frederique; Tomut, Marilena; Avilov, Mikhail; Bender, Markus; Boulesteix, Marine; Krause, Markus; Mittig, Wolfgang; Schein, Mike; Severin, Daniel; Trautmann, Christina

    2013-01-01

    To study the suitability of using graphite as material for high-power targets for rare isotope production at the future Facility for Rare Isotope Beams (FRIB) in the USA and at the Facility for Antiproton and Ion Research (FAIR) in Germany, thin foils of polycrystalline graphite were exposed to 8.6-MeV/u Au ions reaching a maximum fluence of 1 × 10 15 ions/cm 2 . Foil irradiation temperatures of up to 1800 °C were obtained by ohmic heating. In-situ monitoring of the electrical resistance of the graphite foils during and after irradiation provided information on beam-induced radiation damage. The rate of electrical resistance increase as a function of fluence was found to decrease with increasing irradiation temperature, indicating a more efficient annealing of the irradiation-produced defects. This is corroborated by the observation that graphite foils irradiated at temperatures below about 800 °C showed cracks and pronounced deformations, which did not appear on the samples irradiated at higher temperatures

  16. In-situ electric resistance measurements and annealing effects of graphite exposed to swift heavy ions

    Energy Technology Data Exchange (ETDEWEB)

    Fernandes, Sandrina [Facility for Rare Isotope Beams, Michigan State University, East Lansing, MI (United States); Pellemoine, Frederique, E-mail: pellemoi@frib.msu.edu [Facility for Rare Isotope Beams, Michigan State University, East Lansing, MI (United States); Tomut, Marilena [GSI Helmholtzzentrum für Schwerionenforschung, Darmstadt (Germany); National Institute for Materials Physics (NIMP), Bucharest (Romania); Avilov, Mikhail [Facility for Rare Isotope Beams, Michigan State University, East Lansing, MI (United States); Bender, Markus [GSI Helmholtzzentrum für Schwerionenforschung, Darmstadt (Germany); Boulesteix, Marine [Facility for Rare Isotope Beams, Michigan State University, East Lansing, MI (United States); Krause, Markus [GSI Helmholtzzentrum für Schwerionenforschung, Darmstadt (Germany); Technische Universität, Darmstadt (Germany); Mittig, Wolfgang [National Superconducting Cyclotron Lab (NSCL), Michigan State University, East Lansing, MI (United States); Schein, Mike [Facility for Rare Isotope Beams, Michigan State University, East Lansing, MI (United States); Severin, Daniel [GSI Helmholtzzentrum für Schwerionenforschung, Darmstadt (Germany); Trautmann, Christina [GSI Helmholtzzentrum für Schwerionenforschung, Darmstadt (Germany); Technische Universität, Darmstadt (Germany)

    2013-11-01

    To study the suitability of using graphite as material for high-power targets for rare isotope production at the future Facility for Rare Isotope Beams (FRIB) in the USA and at the Facility for Antiproton and Ion Research (FAIR) in Germany, thin foils of polycrystalline graphite were exposed to 8.6-MeV/u Au ions reaching a maximum fluence of 1 × 10{sup 15} ions/cm{sup 2}. Foil irradiation temperatures of up to 1800 °C were obtained by ohmic heating. In-situ monitoring of the electrical resistance of the graphite foils during and after irradiation provided information on beam-induced radiation damage. The rate of electrical resistance increase as a function of fluence was found to decrease with increasing irradiation temperature, indicating a more efficient annealing of the irradiation-produced defects. This is corroborated by the observation that graphite foils irradiated at temperatures below about 800 °C showed cracks and pronounced deformations, which did not appear on the samples irradiated at higher temperatures.

  17. Monitoring Induced Fractures with Electrical Measurements using Depth to Surface Resistivity: A Field Case Study

    Science.gov (United States)

    Wilt, M.; Nieuwenhuis, G.; Sun, S.; MacLennan, K.

    2016-12-01

    Electrical methods offer an attractive option to map induced fractures because the recovered anomaly is related to the electrical conductivity of the injected fluid in the open (propped) section of the fracture operation. This is complementary to existing micro-seismic technology, which maps the mechanical effects of the fracturing. In this paper we describe a 2014 field case where a combination of a borehole casing electrode and a surface receiver array was used to monitor hydrofracture fracture creation and growth in an unconventional oil field project. The fracture treatment well was 1 km long and drilled to a depth of 2.2 km. Twelve fracture events were induced in 30 m intervals (stages) in the 1 km well. Within each stage 5 events (clusters) were initiated at 30 m intervals. Several of the fracture stages used a high salinity brine, instead of fresh water, to enhance the electrical signal. The electrical experiment deployed a downhole source in a well parallel to the treatment well and 100 m away. The source consisted of an electrode attached to a wireline cable into which a 0.25 Hz square wave was injected. A 60-station electrical field receiver array was placed above the fracture and extending for several km. Receivers were oriented to measure electrical field parallel with the presumed fracture direction and those perpendicular to it. Active source electrical data were collected continuously during 7 frac stages, 3 of which used brine as the frac fluid over a period of several days. Although the site was quite noisy and the electrical anomaly small we managed to extract a clear frac anomaly using field separation, extensive signal averaging and background noise rejection techniques. Preliminary 3D modeling, where we account for current distribution of the casing electrode and explicitly model multiple thin conductive sheets to represent fracture stages, produces a model consistent with the field measurements and also highlights the sensitivity of the

  18. Electrical capacity and resistance determination of emitting electric transducer

    International Nuclear Information System (INIS)

    Alba Fernandez, J.; Ramis Soriano, J.

    2000-01-01

    In this work we calculate the electrical resistance and capacity of emitting electric transducer, which is mainly formed, in direct relationship with its properties, by a ceramic capacitor. Our aim is to motivate the students with an attractive element in order to carry out traditional measurements of the charge and discharge transients of a capacitor, implementing high resistance setups. (Author) 5 refs

  19. Radiation enhanced copper clustering processes in Fe-Cu alloys during electron and ion irradiations as measured by electrical resistivity

    International Nuclear Information System (INIS)

    Ishino, S.; Chimi, Y.; Bagiyono; Tobita, T.; Ishikawa, N.; Suzuki, M.; Iwase, A.

    2003-01-01

    To study the mechanism of radiation-enhanced clustering of copper atoms in Fe-Cu alloys, in situ electrical resistivity measurements are performed during irradiation with 100 MeV carbon ions and with 2 MeV electrons at 300 K. Two kinds of highly pure Fe-Cu alloys with Cu content of 0.02 and 0.6 wt% are used. The results are summarized as follows: - Although there is a steep initial resistivity increase below about 10 μdpa, the resistivity steadily decreases after this initial transient in Fe-0.6wt%Cu alloy, while in Fe-0.02wt%Cu alloy, the resistivity either decreases slowly or stays almost constant. The rate of change in resistivity depends on copper concentration. - The rate of change in resistivity per dpa is larger for electron irradiation than for ion irradiation. - Change in dose rate from 10 -8 to 10 -9 dpa/s slightly enhances the rate of resistivity change per dpa. The decrease in resistivity with dose is considered to be due to clustering or precipitation of copper atoms. The initial abrupt increase in resistivity is too large to be accounted for by initial introduction of point defects before copper clustering. Tentatively the phenomenon is explained as due to the formation of embryos of copper precipitates with a large strain field around them. Quantitative evaluation of the results using resistivity contribution of a unit concentration of Frenkel pairs and that of copper atoms gives an important conclusion that more than one copper atom are removed from solid solution by one Frenkel pair. The clustering efficiency is surprisingly high in the present case compared with the ordinary radiation-induced or radiation-enhanced precipitation processes

  20. Electricity electron measurement

    International Nuclear Information System (INIS)

    Kim, Sang Jin; Sung, Rak Jin

    1985-11-01

    This book deals with measurement of electricity and electron. It is divided into fourteen chapters, which depicts basic of electricity measurement, unit and standard, important electron circuit for measurement, instrument of electricity, impedance measurement, power and power amount measurement, frequency and time measurement, waveform measurement, record instrument and direct viewing instrument, super high frequency measurement, digital measurement on analog-digital convert, magnetic measurement on classification by principle of measurement, measurement of electricity application with principle sensors and systematization of measurement.

  1. In-place measurement of specific electric resistance during precipitation of γ'-precipitating Ni base alloys

    International Nuclear Information System (INIS)

    Silomon, M.

    1991-01-01

    During precipitation and coarsening of a second phase, the electric resistance of an alloy changes. Continuous resistance measurement is possible during heat treatment and can be conducted with limited experimental effort; any metallographic determination of the temperature and time dependencies of structural changes, however, requires very high effort. For this reason, an instrument was set up which permits continuous measurement of the resistance at precipitation temperature and during heating or cooling, while providing sufficient resolution for minor changes. Both measuring methods are conducted on technologically relevant alloys such as Nimonic PE 16 and those based on Ni-20 At.% Cr with deliberately varied additions of Al and Ti (accompanying investigations: TEM, SANS, and calorimetry). Their usefulness for alloy development is discussed within the scope of current concepts of demixing kinetics and resistance of alloys. Essential results concern the matrix/γ'-phase mismatch, the Ni 2 Cr short range order, and determination of the γ'-solvus temperature. (orig.) With 53 figs., 4 tabs [de

  2. Electrical Resistance Measurements and Microstructural Characterization of the Anode/Interconnect Contact in Simulated Anode-Side SOFC Conditions

    DEFF Research Database (Denmark)

    Harthøj, Anders; Alimadadi, Hossein; Holt, Tobias

    2015-01-01

    in phase transformation of the steel and in formation of oxides with a poor electrical conductivity in the anode. In this study, the area specific resistance (ASR) of the steel Crofer 22 APU, in contact with a Ni/YSZ anode with and without a tape casted CeO2 barrier layer was measured in simulated SOFC...... anode conditions at 800◦C. The microstructure in the contact area was characterized using scanning electron microscopy techniques. The ASR was low for the steel in direct contact with the Ni/YSZ anode. Nickel diffusion into the steel resulted in a fine grained zone, which was identified as ferrite...

  3. The point-spread function measure of resolution for the 3-D electrical resistivity experiment

    Science.gov (United States)

    Oldenborger, Greg A.; Routh, Partha S.

    2009-02-01

    The solution appraisal component of the inverse problem involves investigation of the relationship between our estimated model and the actual model. However, full appraisal is difficult for large 3-D problems such as electrical resistivity tomography (ERT). We tackle the appraisal problem for 3-D ERT via the point-spread functions (PSFs) of the linearized resolution matrix. The PSFs represent the impulse response of the inverse solution and quantify our parameter-specific resolving capability. We implement an iterative least-squares solution of the PSF for the ERT experiment, using on-the-fly calculation of the sensitivity via an adjoint integral equation with stored Green's functions and subgrid reduction. For a synthetic example, analysis of individual PSFs demonstrates the truly 3-D character of the resolution. The PSFs for the ERT experiment are Gaussian-like in shape, with directional asymmetry and significant off-diagonal features. Computation of attributes representative of the blurring and localization of the PSF reveal significant spatial dependence of the resolution with some correlation to the electrode infrastructure. Application to a time-lapse ground-water monitoring experiment demonstrates the utility of the PSF for assessing feature discrimination, predicting artefacts and identifying model dependence of resolution. For a judicious selection of model parameters, we analyse the PSFs and their attributes to quantify the case-specific localized resolving capability and its variability over regions of interest. We observe approximate interborehole resolving capability of less than 1-1.5m in the vertical direction and less than 1-2.5m in the horizontal direction. Resolving capability deteriorates significantly outside the electrode infrastructure.

  4. Application of thermo-electromotive force and electric resistance measuring methods to researching phase transformations in Zr1Nb alloy

    International Nuclear Information System (INIS)

    Klimenko, S.P.; Gritsina, V.M.; Petel'guzov, I.A.; Chernyaeva, T.P.

    2007-01-01

    The paper determines the applicability areas of different methods for the study of structural phase transformations in a Zr+1Nb alloy, which is extensively used in reactor construction; production and fabrication of products from Zr+1Nb is currently developed in Ukraine. Electromotive force and electric resistance were measured to study structural phase transformations of Zr+1Nb fuel rod tubes based on calciumthermal zirconium (Zr1Nb). It was established that changes in electric resistance clearly show the beginning of a massive α → β transition at ∼ 750 degree C and the end of α → β transition at ∼ 950 degree C, whereas measurement of thermo-e.m.f. in the samples subjected to successive 3-hour step annealing in the temperature range from 300 to 700 degree C allows the temperature of monotectoid transformation to be found. For sample Zr1Nb batches the temperature of monotectoid transformation is (620±7) degree C. The measurement results are consistent with the similar studies carried out on Zr+1Nb fuel rod tubes based on electrolytic zirconium (E110), for which the temperature of monotectoid transformation is equal to ∼ 610 degree C

  5. Electrical Resistance Tomography imaging of concrete

    KAUST Repository

    Karhunen, Kimmo; Seppä nen, Aku; Lehikoinen, Anssi; Monteiro, Paulo J.M.; Kaipio, Jari P.

    2010-01-01

    We apply Electrical Resistance Tomography (ERT) for three dimensional imaging of concrete. In ERT, alternating currents are injected into the target using an array of electrodes attached to the target surface, and the resulting voltages are measured

  6. Electrical resistivity study of insulators

    International Nuclear Information System (INIS)

    Liesegang, J.; Senn, B.C.; Holcombe, S.R.; Pigram, P.J.

    1998-01-01

    Full text: Conventional methods of electrical resistivity measurement of dielectric materials involve the application of electrodes to a sample whereby a potential is applied and a current through the material is measured. Although great care and ingenuity has often been applied to this technique, the recorded values of electrical resistivity (p), especially for insulator materials, show great disparity. In earlier work by the authors, a method for determining surface charge decay [Q(t)], using a coaxial cylindrical capacitor arrangement interfaced to a personal computer, was adapted to allow the relatively straightforward measurement of electrical resistivity in the surface region of charged insulator materials. This method was used to develop an ionic charge transport theory, based on Mott-Gurney diffusion to allow a greater understanding into charge transport behaviour. This theory was extended using numerical analysis to produce a two dimensional (2-D) computational model to allow the direct comparison between experimental and theoretical charge decay data. The work also provided a means for the accurate determination of the diffusion coefficient (D) and the layer of thickness of surface charge (Δz) on the sample. The work outlined here involves an extension of the theoretical approach previously taken, using a computational model based more closely on the 3-D experimental set-up, to reinforce the level of confidence in the results achieved for the simpler 2-D treatment. Initially, a 3-D rectangular box arrangement similar to the experimental set-up was modelled and a theoretical and experimental comparison of voltage decay results made. This model was then transferred into cylindrical coordinates to allow it to be almost identical to the experiment and again a comparison made. In addition, theoretical analysis of the coupled non-linear partial differential equations governing the charge dissipation process has led to a simplification involving directly, the

  7. Experimental set-up for electrical resistivity measurements at low temperature in amorphous and crystalline metallic samples

    International Nuclear Information System (INIS)

    Rodriquez Fernandez, J.M.; Lopez Sanchez, R.J.; Gomez-Sal, J.C.

    1986-01-01

    The experimental set-up to measure the thermal variation of the electrical resistivity between 10.5 K and 300 K, has been developed. A four probe A.C. method with a synchronous-detection (lock'in) technique were the idoneous for our proposes. We have designed a new type of pressure sample-holder adopted to the CS-202 type cryostat. The measurements performed on samples already known have allowed us to determine the sensitivity of our experiments, which is Δ ρ/ρ=2x10 -4 . The measurements performed in the new Y 3 Rh 2 Si 2 compound which at 10 K has no magnetic ordering, are also presented. (author)

  8. Coke fouling monitoring by electrical resistivity

    Energy Technology Data Exchange (ETDEWEB)

    Bombardelli, Clovis; Mari, Livia Assis; Kalinowski, Hypolito Jose [Universidade Tecnologica Federal do Parana (UTFPR), Curitiba, PR (Brazil). Programa de Pos-Graduacao em Engenharia Eletrica e Informatica Industrial (CPGEI)

    2008-07-01

    An experimental method to simulate the growth of the coke fouling that occurs in the oil processing is proposed relating the thickness of the encrusted coke to its electrical resistivity. The authors suggest the use of the fouling electrical resistivity as a transducer element for determining its thickness. The sensor is basically two electrodes in an electrically isolated device where the inlay can happen in order to compose a purely resistive transducer. Such devices can be easily constructed in a simple and robust form with features capable to face the high temperatures and pressures found in relevant industrial processes. For validation, however, it is needed a relationship between the electrical resistivity and the fouling thickness, information not yet found in the literature. The present work experimentally simulates the growth of a layer of coke on an electrically insulating surface, equipped with electrodes at two extremities to measure the electrical resistivity during thermal cracking essays. The method is realized with a series of consecutive runs. The results correlate the mass of coke deposited and its electrical resistivity, and it can be used to validate the coke depositions monitoring employing the resistivity as a control parameter. (author)

  9. Thermal conductivity, electric resistivity, and Lorenz function for some transition metals measured by a direct electric heating technique

    International Nuclear Information System (INIS)

    Binkele, Ludolf

    1985-01-01

    The validity of the Wiedemann-Franz-Lorenz law in its standard form is disputed in the case of transition metals. However, normal behaviour could be demonstrated for the transition metals molybdenum, tantalum, and niobium by the application of an already tried and tested, and recently improved, modified Kohlrausch measuring method; that is, the high-temperature Lorenz number of these metals takes the Sommerfeld value, within measuring uncertainties of approx. 3%. In the case of tungsten, saturation was observed 16.7% above the Sommerfeld value. Even the Lorenz number of platinum seems to take on a saturation value at that level at temperatures above 1400 K. The lattice conductivity separated by various processes displays a temperature dependence describable by an exponential law for all the metals studied, in contrast to previous assumptions. (author)

  10. Semiconductor Electrical Measurements Laboratory

    Data.gov (United States)

    Federal Laboratory Consortium — The Semiconductor Electrical Measurements Laboratory is a research laboratory which complements the Optical Measurements Laboratory. The laboratory provides for Hall...

  11. A study of the stability analysis of pyroclastic covers based on electrical resistivity measurements

    International Nuclear Information System (INIS)

    Di Maio, R; Piegari, E

    2012-01-01

    Usually, the degree of stability of a slope is quantified by the factor of safety whose values depend on physical and mechanical soil properties analysed on samples of much reduced sizes or referring to very small soil volumes around porous probes. To overcome the limit of point-sampled information, we propose a semi-empirical approach based on the use of geophysical methods and the employment of a geophysical factor of safety recently introduced by the authors in terms of local resistivities and slope angles. In this paper, we show an application of our proposal on a test area of about 2000 m 2 on Sarno Mountains (Campania Region, Southern Italy), where shallow landslides involving pyroclastic soils periodically occur triggered by critical rainfall events. Starting from two resistivity tomography surveys performed on the test area in autumn and spring, we obtained maps of the geophysical factor of safety at different depths for the two seasons. We also estimated the values of the factor of safety by using the infinite-slope model in the dry and saturated scenarios. A comparison between the values of the geophysical and geotechnical factors of safety shows advantages and disadvantages of our approach. (paper)

  12. Electrical measurement, signal processing, and displays

    CERN Document Server

    Webster, John G

    2003-01-01

    ELECTROMAGNETIC VARIABLES MEASUREMENTVoltage MeasurementCurrent Measurement Power Measurement Power Factor Measurement Phase Measurement Energy Measurement Electrical Conductivity and Resistivity Charge Measurement Capacitance and Capacitance Measurements Permittivity Measurement Electric Field Strength Magnetic Field Measurement Permeability and Hysteresis MeasurementInductance Measurement Immittance MeasurementQ Factor Measurement Distortion Measurement Noise Measurement.Microwave Measurement SIGNAL PROCESSINGAmplifiers and Signal ConditionersModulation Filters Spectrum Analysis and Correlat

  13. Evaluation of electrical resistivity anisotropy in geological mapping ...

    African Journals Online (AJOL)

    user

    Key words: Electrical resistivity anisotropy, radial vertical electrical sounding, anisotropy polygons. INTRODUCTION ... electrical resistivity survey in the geological interpretation ... resistivity and other electrical or electromagnetic based.

  14. Hydrogen adsorption on activated carbon nanotubes with an atomic-sized vanadium catalyst investigated by electrical resistance measurements

    International Nuclear Information System (INIS)

    Im, Ji Sun; Yun, Jumi; Kang, Seok Chang; Lee, Sung Kyu; Lee, Young-Seak

    2012-01-01

    Activated multi-walled carbon nanotubes were prepared with appended vanadium as a hydrogen storage medium. The pore structure was significantly improved by an activation process that was studied using Raman spectroscopy, field emission transmission electron microscopy and pore analysis techniques. X-ray photoelectron spectroscopy and X-ray diffraction results reveal that the vanadium catalyst was introduced into the carbon nanotubes in controlled proportions, forming V 8 C 7 . The improved pore structure functioned as a path through the carbon nanotubes that encouraged hydrogen molecule adsorption, and the introduced vanadium catalyst led to high levels of hydrogen storage through the dissociation of hydrogen molecules via the spill-over phenomenon. The hydrogen storage behavior was investigated by electrical resistance measurements for the hydrogen adsorbed on a prepared sample. The proposed mechanism of hydrogen storage suggests that the vanadium catalyst increases not only the amount of hydrogen that is stored but also the speed at which it is stored. A hydrogen storage capacity of 2.26 wt.% was achieved with the activation effects and the vanadium catalyst at 30 °C and 10 MPa.

  15. Synthesis and Electrical Resistivity of Nickel Polymethacrylate

    Science.gov (United States)

    Chohan, M. H.; Khalid, A. H.; Zulfiqar, M.; Butt, P. K.; Khan, Farah; Hussain, Rizwan

    Synthesis of nickel polymethacrylate was carried out using methanolic solutions of sodium hydroxide and polymethacrylic acid. The electrical resistivity of the pellets made from Ni-polymethacrylate was measured at different voltages and temperatures. Results showed that the electrical resistivity of Ni-polymethacrylate decreases significantly with voltage in high temperature regions but the decrease is insignificant at temperatures nearing room temperature. The activation energy at low temperatures is approximately 0.8 eV whereas at high temperature it is in the range 0.21-0.27 eV.

  16. Implications Of Soil Resistivity Measurements Using The Electrical Resistivity Method A Case Study Of A Maize Farm Under Different Soil Preparation Modes At KNUST Agricultural Research Station Kumasi

    Directory of Open Access Journals (Sweden)

    Jakalia

    2015-01-01

    Full Text Available Abstract Continuous vertical electrical sounding CVES technique was used to investigate the soil moisture content of a maize farm at the Kwame Nkrumah University of Science and Technology KNUST Agricultural Research Station ARS Kumasi Ghana. The soils of the maize farm were categorized into four different land preparation modes ploughed-harrowed ploughed hoed and no-till plot. Time-lapse measurements with CVES was carried out using the multi-electrode Wenner array to investigate soil moisture variation with the help of the ABEM Terrameter SAS 4000 resistivity meter. The results showed a heterogeneous distribution of soil moisture content both spatially and temporally. Most of the water available for plants uptake was within a depth of 0.20 0.40 m which coincided with the root zones of the maize crops. In addition the no-till plot was found to conserve more moisture during dry weather conditions than the rest of the plots. The research shows that CVES technique is applicable in monitoring shallow soil water content in the field and the results obtained could be used to optimize irrigation scheduling and to assess the potential for variable-rate irrigation.

  17. Spatial Variability of Soil Physical Properties Obtained with Laboratory Methods and Their Relation to Field Electrical Resistivity Measurements

    Science.gov (United States)

    Dathe, A.; Nemes, A.; Bloem, E.; Patterson, M.; Gimenez, D.; Angyal, A.; Koestel, J. K.; Jarvis, N.

    2017-12-01

    Soil spatial heterogeneity plays a critical role for describing water and solute transport processes in the unsaturated zone. Although we have a sound understanding of the physical properties underlying this heterogeneity (like macropores causing preferential water flow), their quantification in a spatial context is still a challenge. To improve existing knowledge and modelling approaches we established a field experiment on an agriculturally used silty clay loam (Stagnosol) in SE Norway. Centimeter to decimeter scale heterogeneities were investigated in the field using electrical resistivity tomography (ERT) in a quasi-3D and a real 3D approach. More than 100 undisturbed soil samples were taken in the 2x1x1 m3plot investigated with 3D ERT to determine soil water retention, saturated and unsaturated hydraulic conductivities and bulk density in the laboratory. A subset of these samples was scanned at the computer tomography (CT) facility at the Swedish University of Agricultural Sciences in Uppsala, Sweden, with special emphasis on characterizing macroporosity. Results show that the ERT measurements captured the spatial distribution of bulk densities and reflected soil water contents. However, ERT could not resolve the large variation observed in saturated hydraulic conductivities from the soil samples. Saturated hydraulic conductivity was clearly related to the macroporosity visible in the CT scans obtained from the respective soil cores. Hydraulic conductivities close to saturation mainly changed with depths in the soil profile and therefore with bulk density. In conclusion, to quantify the spatial heterogeneity of saturated hydraulic conductivities scanning methods with a resolution smaller than the size of macropores have to be used. This is feasible only when the information obtained from for example CT scans of soil cores would be upscaled in a meaningful way.

  18. Characterization of the Spatial and Temporal Variations of Submarine Groundwater Discharge Using Electrical Resistivity and Seepage Measurements

    Science.gov (United States)

    Durand, Josephine Miryam Kalyanie

    Submarine groundwater discharge (SGD) encompasses all fluids crossing the sediment/ocean interface, regardless of their origin, composition or driving forces. SGD provides a pathway for terrestrial contaminants that can significantly impact coastal ecosystems. Overexploitation of groundwater resources can decrease SGD which favors seawater intrusion at depth. Understanding SGD is therefore crucial for water quality and resource management. Quantifying SGD is challenging due to its diffuse and heterogeneous nature, in addition to significant spatio-temporal variations at multiple scales. In this thesis, an integrated approach combining electrical resistivity (ER) surveys, conductivity and temperature point measurements, seepage rates using manual and ultrasonic seepage meters, and pore fluid salinities was used to characterize SGD spatio-temporal variations and their implications for contaminant transport at several locations on Long Island, NY. The influence of surficial sediments on SGD distribution was investigated in Stony Brook Harbor. A low-permeability mud layer, actively depositing in the harbor, limits SGD at the shoreline, prevents mixing with seawater and channels a significant volume of freshwater offshore. SGD measured at locations without mud is high and indicates significant mixing between porewater and seawater. A 2D steady-state density-difference numerical model of the harbor was developed using SEAWAT and was validated by our field observations. Temporal variations of SGD due to semi-diurnal tidal forcing were studied in West Neck Bay, Shelter Island, using a 12-hr time-lapse ER survey together with continuous salinity and seepage measurements in the intertidal zone. The observed dynamic patterns of groundwater flux and salinity distribution disagree with published standard transient state numerical models, suggesting the need for developing more specific models of non-homogeneous anisotropic aquifers. SGD distribution and composition were

  19. Anastomotic leak detection by electrolyte electrical resistance.

    Science.gov (United States)

    DeArmond, Daniel T; Cline, Adam M; Johnson, Scott B

    2010-08-01

    To characterize a new method of postoperative gastrointestinal leak detection based on electrical resistance changes due to extravasated electrolyte contrast. Postoperative gastrointestinal leak results in increased patient morbidity, mortality, and hospital costs that can be mitigated by early diagnosis. A sensitive and specific diagnostic test that could be performed at the bedside has the potential to shorten the time to diagnosis and thereby improve the quality of treatment. Anaesthetized rats underwent celiotomy and creation of a 5-mm gastrotomy. In experimental animals, electrical resistance changes were measured with a direct current ohmmeter after the introduction of 5 cc of 23.4% NaCl electrolyte solution via gavage and measured with a more sensitive alternating current ohmmeter after the gavage of 1-5 cc of 0.9% NaCl. Comparison was made to negative controls and statistical analysis was performed. Leakage from the gastrotomy induced by as little as 1 cc of gavage-delivered 0.9% NaCl contrast solution was detectable as a statistically significant drop in electrical resistance when compared to results from negative controls. Electrical resistance change associated with electrolyte-gated leak detection is highly sensitive and specific and has the potential to be rapidly translated into clinical settings.

  20. In-situ study of cascade defects in silver by simultaneous transmission electron microscopy and electrical resistivity measurements at low temperatures

    International Nuclear Information System (INIS)

    Haga, K.; King, W.E.; Merkle, K.L.; Meshii, M.

    1985-12-01

    A helium-cooled double-tilt specimen stage for transmission electron microscopy (TEM) with the capability of simultaneous electrical resistivity measurements was constructed and used to study defect-production, migration, clustering and recovery processes in ion-irradiated silver. Vacuum-evaporated thin film specimens were irradiated with 1 MeV Kr + -ions up to a dose of 4.0 x 10 10 ions/cm 2 , at T = 10 0 K in the microscope, using the HVEM-tandem accelerator ion beam interface system in the Argonne National Laboratory Electron Microscopy Center. Cascade defect formation during ion bombardment at the low temperature was directly observed both by TEM and electrical resistivity measurements. Ion bombardment created groups of defect clusters with strong strain fields which gave rise to TEM contrast. The specimen resistivity was increased by 16% during the irradiation. Subsequent microstructural changes and resistivity recovery during isochronal annealing were monitored up to room temperature. 58.3% of the irradiation induced resistivity was recovered, while significant reduction in the size of black spot defect clusters was observed by TEM. A small fraction of clusters disappeared, while no nucleation of new defect clusters was observed

  1. Electrical measurements during magnet construction

    International Nuclear Information System (INIS)

    Sintchak, G.; Ganetis, G.; Cottingham, G.

    1989-01-01

    Throughout the construction phase of the cold mass for SSC magnets, electrical tests are made to determine that no faults in the coil structure have developed. These tests include ones designed to measure turn-to-turn voltage hold-off, hypot tests to ground, coil resistance, and instrumentation checks. These various tests will be described and the test parameters that are used will be covered. 4 figs

  2. Electrical resistance tomography used in environmental restoration

    International Nuclear Information System (INIS)

    Ramirez, A.L.; Daily, W.; LaBrecque, D.

    1992-04-01

    We are developing a new imaging technique, Electrical Resistance Tomography (ERT), to map subsurface liquids as flow occurs during natural or clean-up processes; ERT can also be used to map geologic structure. Natural processes (such as surface water infiltrating the vadose zone) and clean-up processes (such as air injection in the saturated zone, steam injection, emplacement of subsurface barriers) can create changes in a soil's electrical properties that are readily measured. We use these measurements to calculate tomographs that show the spatial distribution of the subsurface resistivities. The information derived from ERT can be used by remediation projects to: monitor the effectiveness of clean-up processes, characterize hydrologic processes affecting contaminant transport, select appropriate clean-up alternatives, demonstrate regulatory compliance, and to verify the installation and performance of subsurface barriers

  3. Determination of electrical resistivity of dry coke beds

    Energy Technology Data Exchange (ETDEWEB)

    Eidem, P.A.; Tangstad, M.; Bakken, J.A. [NTNU, Trondheim (Norway)

    2008-02-15

    The electrical resistivity of the coke bed is of great importance when producing FeMn, SiMn, and FeCr in a submerged arc furnace. In these processes, a coke bed is situated below and around the electrode tip and consists of metallurgical coke, slag, gas, and metal droplets. Since the basic mechanisms determining the electrical resistivity of a coke bed is not yet fully understood, this investigation is focused on the resistivity of dry coke beds consisting of different carbonaceous materials, i.e., coke beds containing no slag or metal. A method that reliably compares the electrical bulk resistivity of different metallurgical cokes at 1500{sup o} C to 1600{sup o}C is developed. The apparatus is dimensioned for industrial sized materials, and the electrical resistivity of anthracite, charcoal, petroleum coke, and metallurgical coke has been measured. The resistivity at high temperatures of the Magnitogorsk coke, which has the highest resistivity of the metallurgical cokes investigated, is twice the resistivity of the Corus coke, which has the lowest electrical resistivity. Zdzieszowice and SSAB coke sort in between with decreasing resistivities in the respective order. The electrical resistivity of anthracite, charcoal, and petroleum coke is generally higher than the resistivity of the metallurgical cokes, ranging from about two to about eight times the resistivity of the Corus coke at 1450{sup o}C. The general trend is that the bulk resistivity of carbon materials decreases with increasing temperature and increasing particle size.

  4. Determining the specific electric resistance of rock

    Energy Technology Data Exchange (ETDEWEB)

    Persad' ko, V.Ia.

    1982-01-01

    Data are presented on perfecting the method of laboratory determination of the specific electric resistance of a rock formation. The average error in determining the specific electric resistance of the core at various locations is no more than two percent with low resistance values (2-5 ohms).

  5. Quantitative impact of hydrothermal alteration on electrical resistivity in geothermal systems from a joint analysis of laboratory measurements and borehole data in Krafla area, N-E Iceland

    Science.gov (United States)

    Lévy, Léa; Páll Hersir, Gylfi; Flóvenz, Ólafur; Gibert, Benoit; Pézard, Philippe; Sigmundsson, Freysteinn; Briole, Pierre

    2016-04-01

    Rock permeability and fluid temperature are the two most decisive factors for a successful geothermal drilling. While those parameters are only measured from drilling, they might be estimated on the basis of their impact on electrical resistivity that might be imaged from surface soundings, for example through TEM (Transient Electro Magnetic) down to one km depth. The electrical conductivity of reservoir rocks is the sum of a volume term depending on fluid parameters and a surface term related to rock alteration. Understanding the link between electrical resistivity and geothermal key parameters requires the knowledge of hydrothermal alteration and its petrophysical signature with the Cation Exchange Capacity (CEC). Fluid-rock interactions related to hydrothermal circulation trigger the precipitation of alteration minerals, which are both witnesses of the temperature at the time of reaction and new paths for the electrical current. Alteration minerals include zeolites, smectites, chlorites, epidotes and amphiboles among which low temperatures parageneses are often the most conductive. The CEC of these mineral phases contributes to account for surface conductivity occuring at the water-rock interface. In cooling geothermal systems, these minerals constitute in petrophysical terms and from surface electrical conduction a memory of the equilibrium phase revealed from electrical probing at all scales. The qualitative impact of alteration minerals on resistivity structure has been studied over the years in the Icelandic geothermal context. In this work, the CEC impact on pore surfaces electrical conductivity is studied quantitatively at the borehole scale, where several types of volcanic rocks are mixed together, with various degrees of alteration and porosity. Five boreholes located within a few km at the Krafla volcano, Northeast Iceland, constitute the basis for this study. The deepest and reference hole, KJ-18, provides cuttings of rock and logging data down to 2215

  6. Electrical Resistance Tomography imaging of concrete

    International Nuclear Information System (INIS)

    Karhunen, Kimmo; Seppaenen, Aku; Lehikoinen, Anssi; Monteiro, Paulo J.M.; Kaipio, Jari P.

    2010-01-01

    We apply Electrical Resistance Tomography (ERT) for three dimensional imaging of concrete. In ERT, alternating currents are injected into the target using an array of electrodes attached to the target surface, and the resulting voltages are measured using the same electrodes. These boundary measurements are used for reconstructing the internal (3D) conductivity distribution of the target. In reinforced concrete, the metallic phases (reinforcing bars and fibers), cracks and air voids, moisture gradients, and the chloride distribution in the matrix carry contrast with respect to conductivity. While electrical measurements have been widely used to characterize the properties of concrete, only preliminary results of applying ERT to concrete imaging have been published so far. The aim of this paper is to carry out a feasibility evaluation with specifically cast samples. The results indicate that ERT may be a feasible modality for non-destructive evaluation of concrete.

  7. Electrical Resistance Tomography imaging of concrete

    KAUST Repository

    Karhunen, Kimmo

    2010-01-01

    We apply Electrical Resistance Tomography (ERT) for three dimensional imaging of concrete. In ERT, alternating currents are injected into the target using an array of electrodes attached to the target surface, and the resulting voltages are measured using the same electrodes. These boundary measurements are used for reconstructing the internal (3D) conductivity distribution of the target. In reinforced concrete, the metallic phases (reinforcing bars and fibers), cracks and air voids, moisture gradients, and the chloride distribution in the matrix carry contrast with respect to conductivity. While electrical measurements have been widely used to characterize the properties of concrete, only preliminary results of applying ERT to concrete imaging have been published so far. The aim of this paper is to carry out a feasibility evaluation with specifically cast samples. The results indicate that ERT may be a feasible modality for non-destructive evaluation of concrete. © 2009 Elsevier Ltd. All rights reserved.

  8. Electrical Resistivity Imaging for environmental applications

    International Nuclear Information System (INIS)

    Leite, O.; Bernard, J.; Vermeersch, F.

    2007-01-01

    For a few years, the evolution of measuring equipment and of interpretation software have permitted to develop a new electrical resistivity technique called resistivity imaging where the equipment, which includes a large number of electrodes located along a line at the same time, carries out an automatic switching of these electrodes for acquiring profiling data. The apparent resistivity pseudo sections measured with such a technique are processed by an inversion software which gives interpreted resistivity and depth values for the anomalies detected along the profile. The multi-electrode resistivity technique consists in using a multi-core cable with as many conductors (24, 48, 72, 96) as electrodes plugged into the ground at a fixed spacing, every 5m for instance. In the resistivitymeter itself are located the relays which ensure the switching of those electrodes according to a sequence of readings predefined and stored in the internal memory of the equipment. The various combinations of transmitting (A,B) and receiving (M,N) pairs of electrodes construct the mixed sounding / profiling section, with a maximum investigation depth which mainly depends on the total length of the cable. The 2D resistivity images obtained with such a multi-electrode technique are used for studying the shallow stuctures of the underground located a few tens of metres down to about one hundred metres depth; these images supply an information which complements the one obtained with the more traditionnal Vertical Electrical Sounding (VES) technique, which mainly aims at determining the depths of horizontal 1D structures from the surface down to several hundreds metres depths. Several examples are presented for various types of applications: groundwater (intrusion of salt water in fresh water), geotechnics (detection of a fault in a granitic area), environment (delineation of a waste disposal area) and archaeology (discovery of an ancient tomb)

  9. The role of electric resistivity in estimation of the properties of carbonaceous materials

    Energy Technology Data Exchange (ETDEWEB)

    Slobodskoy, S.A. [Kharkov Polytechnical University, Kharkov (Ukraine)

    1999-07-01

    The electrical resistivity of thermoanthracite and coal and pitch cokes were measured. Results showed that the Russian standard (GOST 4668-75) for measuring electrical resistivity needs amending. 21 refs., 2 figs., 1 tab.

  10. Joint application of ground penetrating radar and electrical resistivity measurements for characterization of subsurface stratigraphy in Southwestern Nigeria

    International Nuclear Information System (INIS)

    Adepelumi, A A; Fayemi, O

    2012-01-01

    The frequent building collapses in Nigeria have been attributed to a lack of pre-construction investigations, which assist engineers in obtaining in situ geotechnical information. Further, the structural subsurface settings are often ignored or investigation is haphazardly carried out. To address this issue and demonstrate the importance of such a survey, a combination of ground penetrating radar (GPR) and vertical electrical sounding (VES) data were acquired in a part of Southwestern Nigeria. A 200 MHz antenna was used for the data acquisition along four traverses. The data were subjected to standard GPR processing techniques, and attribute analysis such as instantaneous frequency, amplitude and phase. Also, for comparative and engineering characterization purposes, longitudinal conductance and coefficient of anisotropy were computed from the VES results and used for determining the competency of the bedrocks. From the GPR results, it was observed that the mapped subsurface is characterized as erosional truncated at a low angle, which is southerly dipping and includes tangential reflections. Further, stratified rocks dipping at an angle of 32° occur between 1.0 and 4.5 m depth in all of the GPR sections; these strata were truncated by topsoil at shallow depths. Also, some of the sections depict ancient channel structures that have a dimension of 70 m × 40 m. The resistivity data suggest that the study area is characterized by four distinct geoelectric sequences. These comprise topsoil which is composed of clay-like sand to lateritic clay whose thickness ranges between 0.25 and 8.12 m, weathered bedrock with a thickness between 3.84 and 12.61 m, stratified bedrock with a thickness between 0.33 and 7.51 m, and fresh bedrock. These results reveal a complex subsurface geology and this characterizes the study area. The area has low to moderate longitudinal conductance and coefficient of anisotropy values, which suggest that incompetent to semi-competent bedrock

  11. Accurate measurement of junctional conductance between electrically coupled cells with dual whole-cell voltage-clamp under conditions of high series resistance.

    Science.gov (United States)

    Hartveit, Espen; Veruki, Margaret Lin

    2010-03-15

    Accurate measurement of the junctional conductance (G(j)) between electrically coupled cells can provide important information about the functional properties of coupling. With the development of tight-seal, whole-cell recording, it became possible to use dual, single-electrode voltage-clamp recording from pairs of small cells to measure G(j). Experiments that require reduced perturbation of the intracellular environment can be performed with high-resistance pipettes or the perforated-patch technique, but an accompanying increase in series resistance (R(s)) compromises voltage-clamp control and reduces the accuracy of G(j) measurements. Here, we present a detailed analysis of methodologies available for accurate determination of steady-state G(j) and related parameters under conditions of high R(s), using continuous or discontinuous single-electrode voltage-clamp (CSEVC or DSEVC) amplifiers to quantify the parameters of different equivalent electrical circuit model cells. Both types of amplifiers can provide accurate measurements of G(j), with errors less than 5% for a wide range of R(s) and G(j) values. However, CSEVC amplifiers need to be combined with R(s)-compensation or mathematical correction for the effects of nonzero R(s) and finite membrane resistance (R(m)). R(s)-compensation is difficult for higher values of R(s) and leads to instability that can damage the recorded cells. Mathematical correction for R(s) and R(m) yields highly accurate results, but depends on accurate estimates of R(s) throughout an experiment. DSEVC amplifiers display very accurate measurements over a larger range of R(s) values than CSEVC amplifiers and have the advantage that knowledge of R(s) is unnecessary, suggesting that they are preferable for long-duration experiments and/or recordings with high R(s). Copyright (c) 2009 Elsevier B.V. All rights reserved.

  12. Relating the Electrical Resistance of Fresh Concrete to Mixture Proportions.

    Science.gov (United States)

    Obla, K; Hong, R; Sherman, S; Bentz, D P; Jones, S Z

    2018-01-01

    Characterization of fresh concrete is critical for assuring the quality of our nation's constructed infrastructure. While fresh concrete arriving at a job site in a ready-mixed concrete truck is typically characterized by measuring temperature, slump, unit weight, and air content, here the measurement of the electrical resistance of a freshly cast cylinder of concrete is investigated as a means of assessing mixture proportions, specifically cement and water contents. Both cement and water contents influence the measured electrical resistance of a sample of fresh concrete: the cement by producing ions (chiefly K + , Na + , and OH - ) that are the main source of electrical conduction; and the water by providing the main conductive pathways through which the current travels. Relating the measured electrical resistance to attributes of the mixture proportions, such as water-cement ratio by mass ( w/c ), is explored for a set of eleven different concrete mixtures prepared in the laboratory. In these mixtures, w/c , paste content, air content, fly ash content, high range water reducer dosage, and cement alkali content are all varied. Additionally, concrete electrical resistance data is supplemented by measuring the resistivity of its component pore solution obtained from 5 laboratory-prepared cement pastes with the same proportions as their corresponding concrete mixtures. Only measuring the concrete electrical resistance can provide a prediction of the mixture's paste content or the product w*c ; conversely, when pore solution resistivity is also available, w/c and water content of the concrete mixture can be reasonably assessed.

  13. Surface electrical resistivity of insulators

    International Nuclear Information System (INIS)

    Senn, B. C.; Liesegang, J.

    1996-01-01

    A method is presented here for measuring surface charge decay, and theory has been developed so as to produce determinations of resistivity in the surface region of insulator films or wafers. This method incorporates the use of a coaxial cylindrical capacitor arrangement and an electrometer interfaced to a PC. The charge transport theory given here is based on Mott-Gurney diffusion, and allows easy interpretation of the experimental data, especially for the initial phase of surface charge decay. Resistivity measurements are presented for glass, mica, perspex and polyethylene, covering a range of 10 9 to 10 18 Ωm, as an illustration of the useful range of the instrument for static and antistatic materials, particularly in film or sheet form. Values for the surface charge diffusion constants of the materials are also presented. The charge transport theory has also been extended to allow the experimental and computational theoretical comparison of surface charge decay not only over the initial phase of charge decay, but also over longer times. The theoretical predictions show excellent agreement with experiment using the values for the diffusion constants referred to above

  14. Self-Sensing of Position-Related Loads in Continuous Carbon Fibers-Embedded 3D-Printed Polymer Structures Using Electrical Resistance Measurement.

    Science.gov (United States)

    Luan, Congcong; Yao, Xinhua; Shen, Hongyao; Fu, Jianzhong

    2018-03-27

    Condition monitoring in polymer composites and structures based on continuous carbon fibers show overwhelming advantages over other potentially competitive sensing technologies in long-gauge measurements due to their great electromechanical behavior and excellent reinforcement property. Although carbon fibers have been developed as strain- or stress-sensing agents in composite structures through electrical resistance measurements, the electromechanical behavior under flexural loads in terms of different loading positions still lacks adequate research, which is the most common situation in practical applications. This study establishes the relationship between the fractional change in electrical resistance of carbon fibers and the external loads at different loading positions along the fibers' longitudinal direction. An approach for real-time monitoring of flexural loads at different loading positions was presented simultaneously based on this relationship. The effectiveness and feasibility of the approach were verified by experiments on carbon fiber-embedded three-dimensional (3D) printed thermoplastic polymer beam. The error in using the provided approach to monitor the external loads at different loading positions was less than 1.28%. The study fully taps the potential of continuous carbon fibers as long-gauge sensory agents and reinforcement in the 3D-printed polymer structures.

  15. Self-Sensing of Position-Related Loads in Continuous Carbon Fibers-Embedded 3D-Printed Polymer Structures Using Electrical Resistance Measurement

    Directory of Open Access Journals (Sweden)

    Congcong Luan

    2018-03-01

    Full Text Available Condition monitoring in polymer composites and structures based on continuous carbon fibers show overwhelming advantages over other potentially competitive sensing technologies in long-gauge measurements due to their great electromechanical behavior and excellent reinforcement property. Although carbon fibers have been developed as strain- or stress-sensing agents in composite structures through electrical resistance measurements, the electromechanical behavior under flexural loads in terms of different loading positions still lacks adequate research, which is the most common situation in practical applications. This study establishes the relationship between the fractional change in electrical resistance of carbon fibers and the external loads at different loading positions along the fibers’ longitudinal direction. An approach for real-time monitoring of flexural loads at different loading positions was presented simultaneously based on this relationship. The effectiveness and feasibility of the approach were verified by experiments on carbon fiber-embedded three-dimensional (3D printed thermoplastic polymer beam. The error in using the provided approach to monitor the external loads at different loading positions was less than 1.28%. The study fully taps the potential of continuous carbon fibers as long-gauge sensory agents and reinforcement in the 3D-printed polymer structures.

  16. Electrical resistivity of ferrimagnetic magnetite thin film

    International Nuclear Information System (INIS)

    Varshney, Dinesh; Yogi, A.; Kaurav, N.; Gupta, R.P.; Phase, D.M.

    2006-01-01

    We have grown Fe 3 O 4 (III) epitaxial film on Al 2 O 3 (0001) substrate by pulsed laser deposition, with thickness of 130 nm. X-ray diffraction studies of magnetite show the spinel cubic structure of film with preferential (III) orientation. The electrical resistivity measurement demonstrates that the properties of thin film of magnetite are basically similar to those of bulk magnetite and clearly shows semiconductor-insulator transition at Verwey transition temperature (≅140 K). We have found higher Verwey transition temperature when compared with earlier reports on similar type of system. Possible causes for increase in transition temperature are discussed. (author)

  17. In situ measurement of corrosion of type 316L stainless steel in 553 K pure water via the electrical resistance of a thin wire

    International Nuclear Information System (INIS)

    Ishida, Kazushige; Lister, Derek

    2012-01-01

    A system for the in situ monitoring of corrosion depth via electrical resistance measurements was applied to study the corrosion rate of type 316L stainless steel at 553 K in pure water. Corrosion depth was measured using a 50 μm diameter wire probe mounted axially in the tube. Measurements were in good agreement with literature data for both the hydrogen water chemistry (HWC) condition and the normal water chemistry (NWC) condition. Oxide film analyses by scanning electron microscopy and laser Raman spectroscopy on the wire probe and the tube showed no effects from shape of the test specimens or the application of electric current. Corrosion kinetics was evaluated by fitting equations to the measurements. Data for the HWC condition could be fitted by a two-step logarithmic-parabolic law. A single-step logarithmic law fitted data for the NWC condition. Changes in corrosion rate by the water chemistry changes were readily detected with the technique. Corrosion depth change could be observed for the water chemistry change from the NWC condition to the HWC condition with electrochemical corrosion potential (ECP) of -0.56 V vs. standard hydrogen electrode, which is lower than the ECP that the phase of iron oxide changes from α-Fe 2 O 3 to Fe 3 O 4 . (author)

  18. Monitoring snowmelt and solute transport at Oslo airport by combining time-lapse electrical resistivity, soil water sampling and tensiometer measurements

    Science.gov (United States)

    Bloem, E.; French, H. K.

    2013-12-01

    Monitoring contaminant transport at contaminated sites requires optimization of the configuration of a limited number of samplings points combined with heterogeneous flow and preferential flowpaths. Especially monitoring processes in the unsaturated zone is a major challenge due to the limited volume monitored by for example suction cups and their risk to clog in a highly active degradation zone. To make progress on soil contamination assessment and site characterization there is a strong need to integrate field-sale extensively instrumented tools, with non-invasive (geophysical) methods which provide spatially integrated measurements also in the unsaturated zone. Examples of sites that might require monitoring activities in the unsaturated zone are airports with winter frost where large quantities of de-icing chemicals are used each winter; salt and contaminant infiltration along roads; constructed infiltration systems for treatment of sewerage or landfill seepage. Electrical resistivity methods have proved to be useful as an indirect measurement of subsurface properties and processes at the field-scale. The non-uniqueness of the interpretation techniques can be reduced by constraining the inversion through the addition of independent geophysical measurements along the same profile. Or interpretation and understanding of geophysical images can be improved by the combination with classical measurements of soil physical properties, soil suction, contaminant concentration and temperatures. In our experiment, at the research field station at Gardermoen, Oslo airport, we applied a degradable de-icing chemical and an inactive tracer to the snow cover prior to snowmelt. To study the solute transport processes in the unsaturated zone time-lapse cross borehole electrical resistivity tomography (ERT) measurements were conducted at the same time as soil water samples were extracted at multiple depths with suction cups. Measurements of soil temperature, and soil tension were

  19. Toughness degradation evaluation of low alloyed steels by electrical resistivity

    Energy Technology Data Exchange (ETDEWEB)

    Nahm, S H; Yu, K M; Kim, S C [Korea Research Inst. of Standards and Science, Taejon (Korea, Republic of); Kim, A [Department of Mechanical Engineering, Kongju Univ., Kongju, Chungnam (Korea, Republic of)

    1997-09-01

    Remaining life of turbine rotors with a crack can be assessed by the fracture toughness on the aged rotors at service temperature. DC potential drop measurement system was constructed in order to evaluate material toughness nondestructively. Test material was 1Cr-1Mo-0.25V steel used widely for turbine rotor material. Seven kinds of specimen with different degradation levels were prepared according to isothermal aging heat treatment at 630 deg. C. Electrical resistivity of test material was measured at room temperature. It was observed that material toughness and electrical resistivity decreased with the increase of degradation. The relationship between fracture toughness and electrical resistivity was investigated. Fracture toughness of a test material may be determined nondestructively by electrical resistivity. (author). 13 refs, 7 figs.

  20. State Waste Discharge Permit Application: Electric resistance tomography testing

    Energy Technology Data Exchange (ETDEWEB)

    1994-04-01

    This permit application documentation is for a State Waste Discharge Permit issued in accordance with requirements of Washington Administrative Code 173-216. The activity being permitted is a technology test using electrical resistance tomography. The electrical resistance tomography technology was developed at Lawrence Livermore National Laboratory and has been used at other waste sites to track underground contamination plumes. The electrical resistance tomography technology measures soil electrical resistance between two electrodes. If a fluid contaminated with electrolytes is introduced into the soil, the soil resistance is expected to drop. By using an array of measurement electrodes in several boreholes, the areal extent of contamination can be estimated. At the Hanford Site, the purpose of the testing is to determine if the electrical resistance tomography technology can be used in the vicinity of large underground metal tanks without the metal tank interfering with the test. It is anticipated that the electrical resistance tomography technology will provide a method for accurately detecting leaks from the bottom of underground tanks, such as the Hanford Site single-shell tanks.

  1. State Waste Discharge Permit Application: Electric resistance tomography testing

    International Nuclear Information System (INIS)

    1994-04-01

    This permit application documentation is for a State Waste Discharge Permit issued in accordance with requirements of Washington Administrative Code 173-216. The activity being permitted is a technology test using electrical resistance tomography. The electrical resistance tomography technology was developed at Lawrence Livermore National Laboratory and has been used at other waste sites to track underground contamination plumes. The electrical resistance tomography technology measures soil electrical resistance between two electrodes. If a fluid contaminated with electrolytes is introduced into the soil, the soil resistance is expected to drop. By using an array of measurement electrodes in several boreholes, the areal extent of contamination can be estimated. At the Hanford Site, the purpose of the testing is to determine if the electrical resistance tomography technology can be used in the vicinity of large underground metal tanks without the metal tank interfering with the test. It is anticipated that the electrical resistance tomography technology will provide a method for accurately detecting leaks from the bottom of underground tanks, such as the Hanford Site single-shell tanks

  2. Application of Three Electrical Resistivity Arrays to Evaluate ...

    African Journals Online (AJOL)

    ADOWIE PERE

    shallow depth while Dipole-dipole is more susceptible to edge effect at deeper depth followed by the Pole-dipole array. 2D electrical resistivity field .... Data Processing: Both the apparent resistivity measurements for the synthetic and field data ...

  3. Electrical resistivity of liquid Ti, V, Mo and W

    International Nuclear Information System (INIS)

    Seydel, U.; Fucke, W.

    1980-01-01

    Electrical resistivity data for liquid Ti, V, Mo and W in the temperature range from melting to boiling are presented. The data were obtained by a fast resistive pulse heating technique based on heating small samples shaped as wires or foils in an RCL discharge circuit and simultaneously measuring temperature, volume, voltage and current. (author)

  4. Effects of resistive bodies on DC electrical soundings

    Directory of Open Access Journals (Sweden)

    L. Alfano

    1996-06-01

    Full Text Available Some deep DC electrical soundings, performed in alpine and apenninic areas with the continuous polar dipole-dipole spread, show apparent resistivity curves with positive slopes. Measured values of apparent resistivity reach 30000 Wm. Applying the "surface charges" method we developed three dimensional mathematical models, by means of which we can state simple rules for determining the minimum extensions of the deep resistive bodies, fundamental information for a more precise interpretation of the field results.

  5. Measurement of air distribution and void fraction of an upwards air–water flow using electrical resistance tomography and a wire-mesh sensor

    International Nuclear Information System (INIS)

    Olerni, Claudio; Jia, Jiabin; Wang, Mi

    2013-01-01

    Measurements on an upwards air–water flow are reported that were obtained simultaneously with a dual-plane electrical resistance tomograph (ERT) and a wire-mesh sensor (WMS). The ultimate measurement target of both ERT and WMS is the same, the electrical conductivity of the medium. The ERT is a non-intrusive device whereas the WMS requires a net of wires that physically crosses the flow. This paper presents comparisons between the results obtained simultaneously from the ERT and the WMS for evaluation and calibration of the ERT. The length of the vertical testing pipeline section is 3 m with an internal diameter of 50 mm. Two distinct sets of air–water flow rate scenarios, bubble and slug regimes, were produced in the experiments. The fast impedance camera ERT recorded the data at an approximate time resolution of 896 frames per second (fps) per plane in contrast with the 1024 fps of the wire-mesh sensor WMS200. The set-up of the experiment was based on well established knowledge of air–water upwards flow, particularly the specific flow regimes and wall peak effects. The local air void fraction profiles and the overall air void fraction were produced from two systems to establish consistency for comparison of the data accuracy. Conventional bulk flow measurements in air mass and electromagnetic flow metering, as well as pressure and temperature, were employed, which brought the necessary calibration to the flow measurements. The results show that the profiles generated from the two systems have a certain level of inconsistency, particularly in a wall peak and a core peak from the ERT and WMS respectively, whereas the two tomography instruments achieve good agreement on the overall air void fraction for bubble flow. For slug flow, when the void fraction is over 30%, the ERT underestimates the void fraction, but a linear relation between ERT and WMS is still observed. (paper)

  6. Measurements of the electrical resistance and the hydrogen depth distribution for Ni 60Nb 20Zr 20 amorphous alloy before and after hydrogen charging

    Science.gov (United States)

    Nakano, Sumiaki; Ohtsu, Naofumi; Nagata, Shinji; Yamaura, Shin-ichi; Uchinashi, Sakae; Kimura, Hisamichi; Shikama, Tatsuo; Inoue, Akihisa

    2005-02-01

    A Ni 60Nb 20Zr 20 amorphous alloy was prepared by the single-roller melt-spinning technique. The change in the electrical resistance of the alloy after electrochemical hydrogen charging in 6 N KOH solution was investigated. The change in the hydrogen depth distribution in the alloy was also investigated by elastic recoil detection. As a result, we found that the electrical resistance of the alloy increases with increasing the hydrogen content in the alloy and that a large number of hydrogen atoms are remained in the surface area of the hydrogen-charged alloy.

  7. Determination of the threshold-energy surface for copper using in-situ electrical-resistivity measurements in the high-voltage electron microscope

    International Nuclear Information System (INIS)

    King, W.E.; Merkle, K.L.; Meshii, M.

    1981-01-01

    A detailed study of the anisotropy of the threshold energy for Frenkel-pair production in copper was carried out experimentally, using in-situ electrical-resistivity measurements in the high-voltage electron microscope. These electrical-resistivity measurements, which are sensitive to small changes in point-defect concentration, were used to determine the damage or defect production rate. Damage-rate measurements in copper single crystals were carried out for approx.40 incident electron-beam directions and six electron energies from 0.4 to 1.1 MeV. The total cross section for Frenkel-pair production is proportional to the measured damage rate and can be theoretically calculated if the form of the threshold-energy surface is known. Trial threshold-energy surfaces were systematically altered until a ''best fit'' of the calculated to the measured total cross sections for Frenkel-pair production was obtained. The average threshold energy of this surface is 28.5 eV. The minimum threshold energy is 18 +- 2 eV and is located near . A ring of very high threshold energy (>50 eV) surrounds the direction. A damage function for single-defect production was derived from this surface and was applied to defect-production calculations at higher recoil energies. This function rises rather sharply from a value of zero at 17 eV to 0.8 at 42 eV. It has the value of 0.5 at 24.5 eV. Above 30 eV the slope of the curve begins to decrease, reflecting the presence of the high-energy regions of the threshold-energy surface. Both topographical and quantitative comparisons of the present surface with those in the literature were presented. Based on a chi 2 goodness-of-fit test, the present surface was found to predict the experimentally observed total cross sections for Frenkel-pair production significantly better than the other available surfaces. Also, the goodness of fit varied substantially less with energy and direction for the present surface

  8. Cone-based Electrical Resistivity Tomography

    Science.gov (United States)

    Pidlisecky, A.; Knight, R.; Haber, E.

    2005-05-01

    Determining the 3D spatial distribution of subsurface properties is a critical part of managing the clean-up of contaminated sites. Most standard hydrologic methods sample small regions immediately adjacent to wells or testing devices. This provides data which are not representative of the entire region of interest. Furthermore, at many contaminated sites invasive methods are not acceptable, due to the risks associated with contacting and spreading the contaminants. To address these issues, we have developed a minimally invasive technology that provides information about the 3D distribution of electrical conductivity. This new technique, cone-based electrical resistivity tomography (C-bert), involves placing several permanent current electrodes in the subsurface and using electrodes mounted on a cone penetrometer to measure the resultant potential field while advancing the cone into the subsurface. In addition to potential field measurements, we obtain the standard suite of cone-penetration measurements, including high resolution resistivity logs; these data can then be used to constrain the inversion of the potential field data. A major challenge of working with these data is that the cone penetrometer is highly conductive, and thus presents a large local perturbation around the measurement location. As the cone is very small (approximately 30mm in diameter) with respect to the total model space, explicitly modeling the cone is computationally demanding. We developed a method for solving the forward model that reduces computational time by an order of magnitude. This solution method, iteratively determined boundary conditions, makes it possible to correct for the cone effect before inversion of the data. Results from synthetic experiments suggest that the C-bert method of data acquisition can result in high quality electrical conductivity images of the subsurface. We tested the practicality of this technique by performing a field test of the C-bert system to image

  9. Electric Properties Measurement of Lentil

    Directory of Open Access Journals (Sweden)

    Novák Ján

    2018-03-01

    Full Text Available This paper contains the results of the electric properties measurement of lentil set. Electric measurements with use of these materials are of fundamental importance in relation to the analysis of quantity of absorbed water and dielectric heating characteristics. The aim of this paper was to perform the measurements of conductivity, dielectric constant and loss tangent on samples of lentil, the electrical properties of which had not been sufficiently measured. Measurements were performed under various moisture contents, and the frequency of electric field ranged from 1 MHz to 16 MHz, using a Q meter with coaxial probe. It was concluded that conductivity, relative permittivity and loss tangent increased with an increase in moisture content, and dielectric constant and loss tangent decreased as the frequency of electric field increased.

  10. Electrical resistivity of liquid noble metal alloys

    International Nuclear Information System (INIS)

    Anis Alam, M.; Tomak, M.

    1983-08-01

    Calculations of the dependence of the electrical resistivity in liquid Ag-Au, Cu-Ag, Cu-Au binary alloys on composition are reported. The structure of the binary alloy is described as a hard sphere system. A one-parameter local pseudopotential, which incorporates s-d hybridization effects phenomenologically, is employed in the resistivity calculation. A reasonable agreement with experimental trends is observed in cases where experimental information is available. (author)

  11. Electrical resistivity measurements to estimate groundwater recharge potential of latosolos in Brasília as a working part of the IWAS Água DF Project

    Science.gov (United States)

    Gaffron, Anne; Hirsch, Markus; Weiss, Holger

    2010-05-01

    pretreated waste water. To prepare the upper soil layer of the infiltration basin root penetration was removed. For the observation of the wetting front during infiltration a 3D-geoelectrical monitoring grid with 64 decoders was constructed. The grid (15 x 6 m) was made up of four decoder lines in parallel. With this setup an investigation depth of approximately 3 m below ground surface could be reached. The infiltration basins are located in the center of the 3D monitoring grid. A dipole-dipole electrode configuration was used in this application. The monitoring of the wetting front started with a measurement of the local subsurface electrical resistivity background values. After this, the basin have been flooded with pretreated municipal waste water and repeated monitoring measurements of electrical resistivity have been conducted and compared to the background values afterwards. Because of the high nutrient content of the municipal waste water, the electrical resistivity in the soil drops as a function of the infiltration rate. For proper balancing of the infiltration processes in the field application also data of precipitation and evaporation need to be considered. In the future the determination of the geochemical parameters of the percolated water with special soil moisture samplers is planned.

  12. Electromigration early resistance increase measurements

    NARCIS (Netherlands)

    Niehof, J.; Flinn, P.A.; Maloney, T.J.

    1993-01-01

    An early resistance change measurement set-up, using an AC bridge technique, has been developed, and measurements have been performed. Large sample-to-sample variations occur. The characteristic time for the resistance change curve is shorter for resistance increase (under current stress) than for

  13. Using electrical resistance tomography to map subsurface temperatures

    Science.gov (United States)

    Ramirez, A.L.; Chesnut, D.A.; Daily, W.D.

    1994-09-13

    A method is provided for measuring subsurface soil or rock temperatures remotely using electrical resistivity tomography (ERT). Electrical resistivity measurements are made using electrodes implanted in boreholes driven into the soil and/or at the ground surface. The measurements are repeated as some process changes the temperatures of the soil mass/rock mass. Tomographs of electrical resistivity are calculated based on the measurements using Poisson's equation. Changes in the soil/rock resistivity can be related to changes in soil/rock temperatures when: (1) the electrical conductivity of the fluid trapped in the soil's pore space is low, (2) the soil/rock has a high cation exchange capacity and (3) the temperature changes are sufficiently high. When these three conditions exist the resistivity changes observed in the ERT tomographs can be directly attributed to changes in soil/rock temperatures. This method provides a way of mapping temperature changes in subsurface soils remotely. Distances over which the ERT method can be used to monitor changes in soil temperature range from tens to hundreds of meters from the electrode locations. 1 fig.

  14. Using electrical resistance tomography to map subsurface temperatures

    Science.gov (United States)

    Ramirez, Abelardo L.; Chesnut, Dwayne A.; Daily, William D.

    1994-01-01

    A method is provided for measuring subsurface soil or rock temperatures remotely using electrical resistivity tomography (ERT). Electrical resistivity measurements are made using electrodes implanted in boreholes driven into the soil and/or at the ground surface. The measurements are repeated as some process changes the temperatures of the soil mass/rock mass. Tomographs of electrical resistivity are calculated based on the measurements using Poisson's equation. Changes in the soil/rock resistivity can be related to changes in soil/rock temperatures when: (1) the electrical conductivity of the fluid trapped in the soil's pore space is low, (2) the soil/rock has a high cation exchange capacity and (3) the temperature changes are sufficiently high. When these three conditions exist the resistivity changes observed in the ERT tomographs can be directly attributed to changes in soil/rock temperatures. This method provides a way of mapping temperature changes in subsurface soils remotely. Distances over which the ERT method can be used to monitor changes in soil temperature range from tens to hundreds of meters from the electrode locations.

  15. Electrical resistivity determination of subsurface layers, subsoil ...

    African Journals Online (AJOL)

    Electrical resistivity determination of subsurface layers, subsoil competence and soil corrosivity at and engineering site location in Akungba-Akoko, ... The study concluded that the characteristics of the earth materials in the site would be favourable to normal engineering structures/materials that may be located on it.

  16. Monitoring of Leachate Recirculation in a Bioreactor Using Electrical Resistivity

    Science.gov (United States)

    Grellier, S.; Bureau, N.; Robain, H.; Tabbagh, A.; Camerlynck, C.; Guerin, R.

    2004-05-01

    The bioreactor is a concept of waste landfill management consisting in speeding up the biodegradation by optimizing the moisture content through leachate recirculation. Electrical resistivity tomography (ERT) is carried out with fast resistivity-meter (Syscal Pro, IRIS Instruments, developed in the framework of the research project CERBERE 01V0665-69, funded by the French Research Ministry) to monitor leachate recirculation. During a recirculation period waste moisture increases, so that electrical resistivity may decrease, but at the same time temperature and mineralization of both waste and leachate become intermixed. If waste temperature is much higher than leachate temperature electrical resistivity will not decrease as much as if the temperature difference was smaller. If leachate mineralization (i.e. leachate conductivity) is higher than that of wet waste in the landfill, electrical resistivity will tend to decrease. Otherwise for example after an addition of rain water into the leachate storage or in case of very wet waste, the resistivities of each medium (leachate and wet waste) can be almost the same, so that leachate mineralization will not have a great influence on waste resistivity. Resistivity measurements were performed during 85 minutes injection trials (with a discharge of 20 m3 h-1) where leachate was injected through a vertical borehole perforated between 1.85 and 4.15 m. Three first measurements are made during the injection (3, 30 and 60 minutes from the beginning of the injection) and the two other after the injection period (8 and 72 minutes after the end of the injection). Apparent and interpreted resistivity variations that occurred during injection trials, expressed as the relative differences (in %) between apparent, respectively interpreted, resistivity during injection and apparent, respectively interpreted, resistivity before injection (reference measurement) show the formation of a plume (a negative anomaly: resistivity decreases with

  17. On equivalent resistance of electrical circuits

    Science.gov (United States)

    Kagan, Mikhail

    2015-01-01

    While the standard (introductory physics) way of computing the equivalent resistance of nontrivial electrical circuits is based on Kirchhoff's rules, there is a mathematically and conceptually simpler approach, called the method of nodal potentials, whose basic variables are the values of the electric potential at the circuit's nodes. In this paper, we review the method of nodal potentials and illustrate it using the Wheatstone bridge as an example. We then derive a closed-form expression for the equivalent resistance of a generic circuit, which we apply to a few sample circuits. The result unveils a curious interplay between electrical circuits, matrix algebra, and graph theory and its applications to computer science. The paper is written at a level accessible by undergraduate students who are familiar with matrix arithmetic. Additional proofs and technical details are provided in appendices.

  18. Application of Three Electrical Resistivity Arrays to Evaluate ...

    African Journals Online (AJOL)

    The study further revealed that the Wenner array is less susceptible to edge effect at shallow depth while Dipole-dipole is more susceptible to edge effect at deeper depth followed by the Pole-dipole array. 2D electrical resistivity field measurements were carried out to confirm the results of the numerical simulation in the ...

  19. Detailed landfill leachate plume mapping using 2D and 3D Electrical Resistivity Tomography - with correlation to ionic strength measured in screens

    DEFF Research Database (Denmark)

    Maurya, P.K.; Rønde, Vinni; Fiandaca, G.

    2017-01-01

    Leaching of organic and inorganic contamination from landfills is a serious environmental problem as surface water and aquifers are affected. In order to assess these risks and investigate the migration of leachate from the landfill, 2D and large scale 3D electrical resistivity tomography were used...... at a heavily contaminated landfill in Grindsted, Denmark. The inverted 2D profiles describe both the variations along the groundwater flow as well as the plume extension across the flow directions. The 3D inversion model shows the variability in the low resistivity anomaly pattern corresponding to differences...... in the ionic strength of the landfill leachate. Chemical data from boreholes agree well with the observations indicating a leachate plume which gradually sinks and increases in size while migrating from the landfill in the groundwater flow direction. Overall results show that the resistivity method has been...

  20. Electrical and calorimetric measurements and related software

    CERN Document Server

    Catalan-Lasheras, N; Koratzinos, M; Rijllart, A; Siemko, A; Strait, J; Tavian, L; Wolf, R

    2009-01-01

    During the incident of sector 3-4 on September 19th, the temperature of a number of magnets increased over the expected values prior to the circuit failure. A review of the data logged during powering tests on all circuits indicated potential resistive splices in sectors 1-2 and 6-7. Calorimetric and electrical measurements confirmed a high resistance in magnet B16. R1 and B32R6. Systematic measurements have been performed in other cold sectors of the LHC during which the temperature increase and voltage across magnets were acquired at different currents. Cryogenic subsectors on which the temperature increase was abnormal were equipped with precise voltmeters to detect eventual resistive splices in the bus-bars. The findings of the measurement campaign will be shown as well as the plans to implement similar diagnostics as a routine check prior to powering the superconducting circuits of the LHC.

  1. Electrical measurements on submicronic synthetic conductors : carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Langer, L [Unite de Physico-Chimie et de Physique des Materiaux, Univ. Catholique de Louvain, Louvain-la-Neuve (Belgium); Stockman, L [Lab. voor Vaste Stof-Fysika en Magnetisme, Katholieke Univ. Leuven (Belgium); Heremans, J P [Physics Dept., General Motors Research, Warren, MI (United States); Bayot, V [Unite de Physico-Chimie et de Physique des Materiaux, Univ. Catholique de Louvain, Louvain-la-Neuve (Belgium); Olk, C H [Physics Dept., General Motors Research, Warren, MI (United States); Haesendonck, C van [Lab. voor Vaste Stof-Fysika en Magnetisme, Katholieke Univ. Leuven (Belgium); Bruynseraede, Y [Lab. voor Vaste Stof-Fysika en Magnetisme, Katholieke Univ. Leuven (Belgium); Issi, J P [Unite de Physico-Chimie et de Physique des Materiaux, Univ. Catholique de Louvain, Louvain-la-Neuve (Belgium)

    1995-03-15

    The synthesis of very small samples has raised the need for a drastic miniaturization of the classical four-probe technique in order to realize electrical resistance measurements. Two methods to realize electrical contacts on very small fibers are described here. Using classical photolithography the electrical resistivity of a submicronic catalytic chemical vapour deposited filament is estimated. Scanning tunneling microscopy (STM) lithography allowed to attach small gold contacts to a small bundle (diameter 50 nm) of carbon nanotubes. This bundle is found to exhibit a semimetallic behavior at higher temperature and an unexpected drop of the electrical resistivity at lower temperature. (orig.)

  2. Measurement of the electrical resistivity of liquid 32G2 and 32G1 steels by the rotating magnetic field method

    Science.gov (United States)

    Borovykh, M. A.; Chikova, O. A.; Tsepelev, V. S.; V'yukhin, V. V.

    2017-03-01

    The resistivity of liquid 32G2 and 32G1 steels are measured using the rotating magnetic field method to obtain information on their liquid structures. The technique of measurements is described and the influence of self-induction and viscosity on the resistivity is estimated. The results are discussed in the framework of a microheterogeneous structure of a metallic melt. A conclusion is made about the character of the influence of slag inclusions detected by magnetic powder and ultrasonic methods on the temperature dependences of the resistivities of liquid 32G2 and 32G1 steels. The change in the temperature coefficient of the resistivity of the melt on heating to 1700°C is interpreted using the Nagel-Tauc model.

  3. Delineation of graves using electrical resistivity tomography

    Science.gov (United States)

    Nero, Callistus; Aning, Akwasi Acheampong; Danuor, Sylvester K.; Noye, Reginald M.

    2016-03-01

    A suspected old royal cemetery has been surveyed at the Kwame Nkrumah University of Science and Technology (KNUST) campus, Kumasi, Ghana using Electrical Resistivity Tomography (ERT) with the objective of detecting graves in order to make informed decisions with regard to the future use of the area. The survey was conducted on a 10,000 m2 area. Continuous Vertical Electrical Sounding (CVES) was combined with the roll along technique for 51 profiles with 1 m probe separation separated by 2 m. Inverted data results indicated wide resistivity variations ranging between 9.34 Ωm and 600 Ωm in the near surface. Such heterogeneity suggests a disturbance of the soil at this level. Both high (≥ 600 Ωm) and low resistivity (≤ 74.7 Ωm) anomalies, relative to background levels, were identified within the first 4 m of the subsurface. These were suspected to be burial tombs because of their rectangular geometries and resistivity contrasts. The results were validated with forward numerical modeling results. The study area is therefore an old cemetery and should be preserved as a cultural heritage site.

  4. Electrical Impedance Measurements of PZT Nanofiber Sensors

    Directory of Open Access Journals (Sweden)

    Richard Galos

    2017-01-01

    Full Text Available Electrical impedance measurements of PZT nanofiber sensors were performed using a variety of methods over a frequency spectrum ranging from DC to 1.8 GHz. The nanofibers formed by electrospinning with diameters ranging from 10 to 150 nm were collected and integrated into sensors using microfabrication techniques. Special matching circuits with ultrahigh input impedance were fabricated to produce low noise, measurable sensor outputs. Material properties including resistivity and dielectric constant are derived from the impedance measurements. The resulting material properties are also compared with those of individual nanofibers being tested using conductive AFM and Scanning Conductive Microscopy.

  5. Characterization of room temperature recrystallization kinetics in electroplated copper thin films with concurrent x-ray diffraction and electrical resistivity measurements

    Energy Technology Data Exchange (ETDEWEB)

    Treger, Mikhail; Noyan, I. C. [Department of Applied Physics and Applied Mathematics, Columbia University, New York 10027 (United States); Witt, Christian [GlobalFoundries, T.J. Watson Research Center, Yorktown Heights, New York 10598 (United States); Cabral, Cyril; Murray, Conal; Jordan-Sweet, Jean [IBM, T.J. Watson Research Center, Yorktown Heights, New York 10598 (United States); Rosenberg, Robert [State University of New York, the University at Albany, Albany, NY 12203 (United States); Eisenbraun, Eric [College of Nanoscale Science and Engineering, University at Albany, Albany, NY 12203 (United States)

    2013-06-07

    Concurrent in-situ four-point probe resistivity and high resolution synchrotron x-ray diffraction measurements were used to characterize room temperature recrystallization in electroplated Cu thin films. The x-ray data were used to obtain the variation with time of the integrated intensities and the peak-breadth from the Cu 111 and 200 reflections of the transforming grains. The variation of the integrated intensity and resistivity data with time was analyzed using the Johnson-Mehl-Avrami-Kolmogorov (JMAK) model. For both 111-textured and non-textured electroplated Cu films, four-point probe resistivity measurements yielded shorter transformation times than the values obtained from the integrated intensities of the corresponding Cu 111 reflections. In addition, the JMAK exponents fitted to the resistivity data were significantly smaller. These discrepancies could be explained by considering the different material volumes from which resistivity and diffraction signals originated, and the physical processes which linked these signals to the changes in the evolving microstructure. Based on these issues, calibration of the resistivity analysis with direct structural characterization techniques is recommended.

  6. In Situ TEM Electrical Measurements

    DEFF Research Database (Denmark)

    Canepa, Silvia; Alam, Sardar Bilal; Ngo, Duc-The

    2016-01-01

    understanding of complex physical and chemical interactions in the pursuit to optimize nanostructure function and device performance. Recent developments of sample holder technology for TEM have enabled a new field of research in the study of functional nanomaterials and devices via electrical stimulation...... influence the sample by external stimuli, e.g. through electrical connections, the TEM becomes a powerful laboratory for performing quantitative real time in situ experiments. Such TEM setups enable the characterization of nanostructures and nanodevices under working conditions, thereby providing a deeper...... and measurement of the specimen. Recognizing the benefits of electrical measurements for in situ TEM, many research groups have focused their effort in this field and some of these methods have transferred to ETEM. This chapter will describe recent advances in the in situ TEM investigation of nanostructured...

  7. Gamma-ray and electrical resistivity measurements in soil with application of carbonatite and agricultural fertilizers in Distrito Federal; Radiacao gama e resistividade eletrica em solo com aplicacao de carbonatito e fertilizantes agricolas no Distrito Federal

    Energy Technology Data Exchange (ETDEWEB)

    Nascimento, Carlos Tadeu Carvalho do; Gaspar, Jose Carlos; Pires, Augusto Cesar Bittencourt, E-mail: carlostadeu@unb.br, E-mail: gasp@unb.br, E-mail: acbpires@unb.br [Instituto de Geociencias, Universidade de Brasilia, DF (Brazil); Ferreira, Francisco Jose Fonseca, E-mail: francisco.ferreira@ufpr.br [Departamento de Geologia, Universidade Federal do Parana, Curitiba, PR (Brazil); Andrade, Leide Rovenia Miranda de, E-mail: leide@cpac.embrapa.br [Empresa Brasileira de Pesquisa Agropecuaria, Centro de Pesquisa Agropecuaria dos Cerrados, Planaltina, DF (Brazil)

    2008-01-15

    EMBRAPA (Empresa Brasileira de Pesquisa Agropecuaria) and Brasilia University developed a research project about the viability of carbonatite rock as agricultural fertilizer. As an initial experiment, several mixtures of carbonatite, limestone, phosphorous and potassium compounds were added as fertilizers in an oxisol area (red-latosol, according with Brazilian System of Soil Classification), in Distrito Federal, central Brazil. The experiment area was divided in 56 plots (4 x 7m) and each plot received a fertilizer mixture. The purpose of this work was to verify if the addition of fertilizer mixture to the soil modified its radiometric and resistivity properties and if it is possible to identify this change. Gamma-ray and electrical resistivity measurements were obtained in an experimental area and in a natural savannah type vegetation area. The results showed that the fertilizer addition modified soil natural properties causing a small increase in K, U, Th levels and decreasing ten times electrical resistivity. A low contrast of radiation was observed between plots, and then it was not possible to differentiate the several treatments in base of gamma-ray measurements. Electrical resistivity was efficient to identify three groups of plots related to mixtures characteristics, respectively with phosphorous, potassium and limestone / carbonatite predominance. (author)

  8. Lord Kelvin's atmospheric electricity measurements

    Science.gov (United States)

    Aplin, Karen; Harrison, R. Giles; Trainer, Matthew; Hough, James

    2013-04-01

    Lord Kelvin (William Thomson), one of the greatest Victorian scientists, made a substantial but little-recognised contribution to geophysics through his work on atmospheric electricity. He developed sensitive instrumentation for measuring the atmospheric electric field, including invention of a portable electrometer, which made mobile measurements possible for the first time. Kelvin's measurements of the atmospheric electric field in 1859, made during development of the portable electrometer, can be used to deduce the substantial levels of particulate pollution blown over the Scottish island of Arran from the industrial mainland. Kelvin was also testing the electrometer during the largest solar flare ever recorded, the "Carrington event" in the late summer of 1859. Subsequently, Lord Kelvin also developed a water dropper sensor, and employed photographic techniques for "incessant recording" of the atmospheric electric field, which led to the long series of measurements recorded at UK observatories for the remainder of the 19th and much of the 20th century. These data sets have been valuable in both studies of historical pollution and cosmic ray effects on atmospheric processes.

  9. Measuring electric conductivity in liquid metals by eddy current method

    International Nuclear Information System (INIS)

    Zhuravlev, S.P.; Ostrovskij, O.I.; Grigoryan, V.A.

    1982-01-01

    Technique permitting to apply the method of vertiginous currents for investigation of electric conductivity of metal melts in the high temperature range is presented. Interferences affecting accuracy of measurements are specified and ways of their removing are pointed out. Scheme of measuring and design of the facility are described. Results of measuring electric resistance of liquid Fe, Co, Ni obtained for the first time by this method are presented. The data obtained agree with the results of measurements conducted by the method of the rotating magnetic field. Difference in absolute values of electric resistance in parallel experiments for each metal does not exceed 4%

  10. Inner structure of La Fossa di Vulcano (Vulcano Island, southern Tyrrhenian Sea, Italy) revealed by high-resolution electric resistivity tomography coupled with self-potential, temperature, and CO2 diffuse degassing measurements

    OpenAIRE

    Revil , A.; Finizola , Anthony; Piscitelli , A.; Rizzo , E.; Ricci , T.; Crespy , A.; Angeletti , B.; Balasco , M.; Barde-Cabusson , Stéphanie; Bennati , L.; Boleve , A.; Byrdina , S.; Carzaniga , N.; Di Gangi , F.; Morin , Julie

    2008-01-01

    International audience; La Fossa cone is an active stratovolcano located on Vulcano Island in the Aeolian Archipelago (southern Italy). Its activity is characterized by explosive phreatic and phreatomagmatic eruptions producing wet and dry pyroclastic surges, pumice fall deposits, and highly viscous lava flows. Nine 2-D electrical resistivity tomograms (ERTs; electrode spacing 20 m, with a depth of investigation >200 m) were obtained to image the edifice. In addition, we also measured the sel...

  11. Characterization of oxidation resistance of stainless steels at high temperature by metallographic examinations and in-situ electrical resistance measurements; Charakterisierung der Oxidationsbestaendigkeit in nichtrostenden Staehlen bei hoher Temperatur durch Metallographische Untersuchungen und In-Situ-Messungen des elektrischen Widerstands

    Energy Technology Data Exchange (ETDEWEB)

    Bruncko, Mihael; Rudolf, Rebeka; Anzel, Ivan [Maribor Univ. (Slovenia). Faculty of Mechanical Engineering; Mehrabi, Kambiz [Pankl Drivetrain Systems GmbH und Co. KG, Kapfenberg (Austria); Kneissl, Albert C. [Leoben Univ. (Austria). Dept. of Physical Metallurgy and Materials Testing

    2013-07-01

    Practically all metals and alloys survive high-temperature exposure by growing oxide scales and/or by precipitation of the oxide particles in the matrix. Formed products can grow in shape of external oxide layers on surfaces, or as discrete oxide particles precipitated in a metal matrix. The first case represents external oxidation, and the other case is called internal oxidation. These processes are very important, because they determine the properties and applicability of metallic materials. Generally, they are undesired, because they cause deterioration of the mechanical properties and decomposition of metallic material. On the other side, the controlled process of external oxidation could be used for formation of protective coatings and the internal oxidation for dispersion strengthening of materials. In this paper we present monitoring of high-temperature oxidation of X12Cr13 stainless steel by in-situ electrical resistance measurements at different annealing temperatures in the air atmosphere. We determined the kinetics of oxide scale formation and its morphology with additional metallographic examination made by optical and scanning electron microscopy. The results of this research work show that in-situ monitoring and characterization of high-temperature oxidation present a strong tool that will contribute to a better fundamental understanding of the phenomena that occur during high-temperature oxidation of metallic materials. (orig.)

  12. Electrical resistivity of sputtered molybdenum films

    International Nuclear Information System (INIS)

    Nagano, J.

    1980-01-01

    The electrical resistivity of r.f. sputtered molybdenum films of thickness 5-150 nm deposited on oxidized silicon substrates was resolved into the three electron scattering components: isotropic background scattering, scattering at grain boundaries and scattering at surfaces. It was concluded that the isotropic background scattering is almost equal to that of bulk molybdenum and is not influenced by sputtering and annealing conditions. When the film thickness is sufficient that surface scattering can be ignored, the decrease in film resistivity after annealing is caused by the decrease in scattering at the grain boundaries for zero bias sputtered films, and is caused by an increase of the grain diameter for r.f. bias sputtered films. (Auth.)

  13. Electrical resistivities of glass melts containing simulated SRP waste sludges

    International Nuclear Information System (INIS)

    Wiley, J.R.

    1978-08-01

    One option for the long-term management of radioactive waste at the Savannah River Plant is to solidify the waste in borosilicate glass by using a continuous, joule-heated, ceramic melter. Electrical resistivities that are needed for melter design were measured for melts of two borosilicate, glass-forming mixtures, each of which was combined with various amounts of several simulated-waste sludges. The simulated sludge spanned the composition range of actual sludges sampled from SRP waste tanks. Resistivities ranged from 6 to 10 ohm-cm at 500 0 C. Melt composition and temperature were correlated with resistivity. Resistivity was not a simple function of viscosity. 15 figures, 4 tables

  14. Electrical resistivity of UBe13 in high magnetic fields

    International Nuclear Information System (INIS)

    Schmiedeshoff, G.M.; Lacerda, A.; Fisk, Z.; Smith, J.L.

    1996-01-01

    We have measured the temperature dependent electrical resistivity of single and polycrystal samples of UBe 13 in high magnetic fields. Two maxima in the resistivity are observed at T M1 and T M2 . T M1 , the temperature of the colder maximum, increases quadratically with magnetic field H, a field dependence previously observed under hydrostatic pressure. The high temperature maximum at T M2 emerges in fields above about 4 T and increases linearly with H, a behavior which may be due to a sharpening of the crystal field levels associated with a depression of the Kondo effect by high magnetic fields. copyright 1996 The American Physical Society

  15. Electrical resistivity of V-Cr-Ti alloys

    Energy Technology Data Exchange (ETDEWEB)

    Zinkle, S.J.; Gubbi, A.N.; Eatherly, W.S. [Oak Ridge National Lab., TN (United States)

    1997-04-01

    Room temperature electrical resistivity measurements have been performed on vanadium alloys containing 3-6%Cr and 3-6%Ti in order to evaluate the microstructural stability of these alloys. A nonlinear dependence on Cr and Ti concentration was observed, which suggests that either short range ordering or solute precipitation (perhaps in concert with interstitial solute clustering) has occurred in V-6Cr-6Ti.

  16. Measurements of electrically exploded tubes

    International Nuclear Information System (INIS)

    Shearer, J.W.; Hartman, C.W.; Munger, R.H.; Gullickson, R.L.; Trimble, D.O.; Cheng, D.Y.

    1975-01-01

    The dynamics of electrically exploded tubes were investigated, principally by means of current measurements and flash x-ray pictures. The pinch effect was observed on the tube motion. Pileup of the imploding tube metal was seen on axis. An approximate analytical model can be roughly fitted to the data, but a more complete fit can be obtained with detailed numerical codes. Application of the results to the planning of future gas-embedded Z-pinch experiments is discussed. (U.S.)

  17. Electrical resistivity response due to elastic-plastic deformations

    International Nuclear Information System (INIS)

    Stout, R.B.

    1987-01-01

    The electrical resistivity of many materials is sensitive to changes in the electronic band configurations surrounding the atoms, changes in the electron-phonon interaction cross-sections, and changes in the density of intrinsic defect structures. These changes are most directly dependent on interatomic measures of relative deformation. For this reason, a model for resistivity response is developed in terms of interatomic measures of relative deformation. The relative deformation consists of two terms, a continuous function to describe the recoverable displacement between two atoms in the atomic lattice structure and a functional to describe the nonrecoverable displacement between two atoms as a result of interatomic discontinuities from dislocation kinetics. This model for resistivity extends the classical piezoresistance representation and relates electric resistance change directly to physical mechanisms. An analysis for the resistivity change of a thin foil ideally embedded in a material that undergoes elastic-plastic deformation is presented. For the case of elastic deformations, stress information in the material surrounding the thin foil is inferred for the cases of pure strain coupling boundary conditions, pure stress coupling boundary conditions, and a combination of stress-strain coupling boundary conditions. 42 refs., 4 figs

  18. Surface resistivity measurement of plasma treated polymers

    International Nuclear Information System (INIS)

    Simon, D.; Pigram, P.J.; Liesegang, J.

    2000-01-01

    Full text: Resistivity of insulators is an important property of materials used within the integrated circuit and packaging industries. The measurement of electrical resistivity of insulator materials in the surface region in this work is interpreted through observations of surface charge decay. A self-field driven and diffusion charge transport theory is used to model the process and resistivity values obtained computationally. Data for the charge decay of surface charged samples are collected by suspending them inside a coaxial cylinder connected to an electrometer. Samples used have been low density polyethylene LDPE sheet, both pristine and surface treated. Some samples have been treated by air plasma at low vacuum pressures for different periods of time; others have been washed in ethyl acetate and then plasma treated before the resistivity measurement. The sets of resistivity measurements form the various treatments are compared below. X-ray photoelectron spectroscopy (XPS) has also been used to investigate and account for the observed variations in surface resistivity

  19. Electrical Resistance Alloys and Low-Expansion Alloys

    DEFF Research Database (Denmark)

    Kjer, Torben

    1996-01-01

    The article gives an overview of electrical resistance alloys and alloys with low thermal expansion. The electrical resistance alloys comprise resistance alloys, heating alloys and thermostat alloys. The low expansion alloys comprise alloys with very low expansion coefficients, alloys with very low...... thermoelastic coefficients and age hardenable low expansion alloys....

  20. New experimental methodology, setup and LabView program for accurate absolute thermoelectric power and electrical resistivity measurements between 25 and 1600 K: Application to pure copper, platinum, tungsten, and nickel at very high temperatures

    International Nuclear Information System (INIS)

    Abadlia, L.; Mayoufi, M.; Gasser, F.; Khalouk, K.; Gasser, J. G.

    2014-01-01

    In this paper we describe an experimental setup designed to measure simultaneously and very accurately the resistivity and the absolute thermoelectric power, also called absolute thermopower or absolute Seebeck coefficient, of solid and liquid conductors/semiconductors over a wide range of temperatures (room temperature to 1600 K in present work). A careful analysis of the existing experimental data allowed us to extend the absolute thermoelectric power scale of platinum to the range 0-1800 K with two new polynomial expressions. The experimental device is controlled by a LabView program. A detailed description of the accurate dynamic measurement methodology is given in this paper. We measure the absolute thermoelectric power and the electrical resistivity and deduce with a good accuracy the thermal conductivity using the relations between the three electronic transport coefficients, going beyond the classical Wiedemann-Franz law. We use this experimental setup and methodology to give new very accurate results for pure copper, platinum, and nickel especially at very high temperatures. But resistivity and absolute thermopower measurement can be more than an objective in itself. Resistivity characterizes the bulk of a material while absolute thermoelectric power characterizes the material at the point where the electrical contact is established with a couple of metallic elements (forming a thermocouple). In a forthcoming paper we will show that the measurement of resistivity and absolute thermoelectric power characterizes advantageously the (change of) phase, probably as well as DSC (if not better), since the change of phases can be easily followed during several hours/days at constant temperature

  1. New experimental methodology, setup and LabView program for accurate absolute thermoelectric power and electrical resistivity measurements between 25 and 1600 K: application to pure copper, platinum, tungsten, and nickel at very high temperatures.

    Science.gov (United States)

    Abadlia, L; Gasser, F; Khalouk, K; Mayoufi, M; Gasser, J G

    2014-09-01

    In this paper we describe an experimental setup designed to measure simultaneously and very accurately the resistivity and the absolute thermoelectric power, also called absolute thermopower or absolute Seebeck coefficient, of solid and liquid conductors/semiconductors over a wide range of temperatures (room temperature to 1600 K in present work). A careful analysis of the existing experimental data allowed us to extend the absolute thermoelectric power scale of platinum to the range 0-1800 K with two new polynomial expressions. The experimental device is controlled by a LabView program. A detailed description of the accurate dynamic measurement methodology is given in this paper. We measure the absolute thermoelectric power and the electrical resistivity and deduce with a good accuracy the thermal conductivity using the relations between the three electronic transport coefficients, going beyond the classical Wiedemann-Franz law. We use this experimental setup and methodology to give new very accurate results for pure copper, platinum, and nickel especially at very high temperatures. But resistivity and absolute thermopower measurement can be more than an objective in itself. Resistivity characterizes the bulk of a material while absolute thermoelectric power characterizes the material at the point where the electrical contact is established with a couple of metallic elements (forming a thermocouple). In a forthcoming paper we will show that the measurement of resistivity and absolute thermoelectric power characterizes advantageously the (change of) phase, probably as well as DSC (if not better), since the change of phases can be easily followed during several hours/days at constant temperature.

  2. Electrical resistivity characterization of anisotropy in the Biscayne Aquifer.

    Science.gov (United States)

    Yeboah-Forson, Albert; Whitman, Dean

    2014-01-01

    Electrical anisotropy occurs when electric current flow varies with azimuth. In porous media, this may correspond to anisotropy in the hydraulic conductivity resulting from sedimentary fabric, fractures, or dissolution. In this study, a 28-electrode resistivity imaging system was used to investigate electrical anisotropy at 13 sites in the Biscayne Aquifer of SE Florida using the rotated square array method. The measured coefficient of electrical anisotropy generally ranged from 1.01 to 1.12 with values as high as 1.36 found at one site. The observed electrical anisotropy was used to estimate hydraulic anisotropy (ratio of maximum to minimum hydraulic conductivity) which ranged from 1.18 to 2.83. The largest values generally were located on the Atlantic Coastal Ridge while the lowest values were in low elevation areas on the margin of the Everglades to the west. The higher values of anisotropy found on the ridge may be due to increased dissolution rates of the oolitic facies of the Miami formation limestone compared with the bryozoan facies to the west. The predominate trend of minimum resistivity and maximum hydraulic conductivity was E-W/SE-NW beneath the ridge and E-W/SW-NE farther west. The anisotropy directions are similar to the predevelopment groundwater flow direction as indicated in published studies. This suggests that the observed anisotropy is related to the paleo-groundwater flow in the Biscayne Aquifer. © 2013, National Ground Water Association.

  3. Small-scale electrical resistivity tomography of wet fractured rocks.

    Science.gov (United States)

    LaBrecque, Douglas J; Sharpe, Roger; Wood, Thomas; Heath, Gail

    2004-01-01

    This paper describes a series of experiments that tested the ability of the electrical resistivity tomography (ERT) method to locate correctly wet and dry fractures in a meso-scale model. The goal was to develop a method of monitoring the flow of water through a fractured rock matrix. The model was a four by six array of limestone blocks equipped with 28 stainless steel electrodes. Dry fractures were created by placing pieces of vinyl between one or more blocks. Wet fractures were created by injecting tap water into a joint between blocks. In electrical terms, the dry fractures are resistive and the wet fractures are conductive. The quantities measured by the ERT system are current and voltage around the outside edge of the model. The raw ERT data were translated to resistivity values inside the model using a three-dimensional Occam's inversion routine. This routine was one of the key components of ERT being tested. The model presented several challenges. First, the resistivity of both the blocks and the joints was highly variable. Second, the resistive targets introduced extreme changes the software could not precisely quantify. Third, the abrupt changes inherent in a fracture system were contrary to the smoothly varying changes expected by the Occam's inversion routine. Fourth, the response of the conductive fractures was small compared to the background variability. In general, ERT was able to locate correctly resistive fractures. Problems occurred, however, when the resistive fracture was near the edges of the model or when multiple fractures were close together. In particular, ERT tended to position the fracture closer to the model center than its true location. Conductive fractures yielded much smaller responses than the resistive case. A difference-inversion method was able to correctly locate these targets.

  4. A Glimpse in the Third Dimension for Electrical Resistivity Profiles

    Science.gov (United States)

    Robbins, A. R.; Plattner, A.

    2017-12-01

    We present an electrode layout strategy designed to enhance the popular two-dimensional electrical resistivity profile. Offsetting electrodes from the traditional linear layout and using 3-D inversion software allows for mapping the three-dimensional electrical resistivity close to the profile plane. We established a series of synthetic tests using simulated data generated from chosen resistivity distributions with a three-dimensional target feature. All inversions and simulations were conducted using freely-available ERT software, BERT and E4D. Synthetic results demonstrate the effectiveness of the offset electrode approach, whereas the linear layout failed to resolve the three-dimensional character of our subsurface feature. A field survey using trench backfill as a known resistivity contrast confirmed our synthetic tests. As we show, 3-D inversions of linear layouts for starting models without previously known structure are futile ventures because they generate symmetric resistivity solutions with respect to the profile plane. This is a consequence of the layout's inherent symmetrical sensitivity patterns. An offset electrode layout is not subject to the same limitation, as the collective measurements do not share a common sensitivity symmetry. For practitioners, this approach presents a low-cost improvement of a traditional geophysical method which is simple to use yet may provide critical information about the three dimensional structure of the subsurface close to the profile.

  5. Sputter-Resistant Materials for Electric Propulsion, Phase II

    Data.gov (United States)

    National Aeronautics and Space Administration — This SBIR Phase 2 project shall develop sputter-resistant materials for use in electric propulsion test facilities and for plume shields on spacecraft using electric...

  6. electrical resistivity investigation of the groundwater potential in ...

    African Journals Online (AJOL)

    The VES data generated were processed and interpreted using partial curve matching ... electrical sounding, a technique of electrical resistivity method in identifying viable .... Geoelectric/Electromagnetic VLF Survey for. Groundwater in a ...

  7. Development and applications of the contact electric resistance technique

    Energy Technology Data Exchange (ETDEWEB)

    Saario, T.

    1995-12-31

    At the moment both the scientific understanding of corrosion processes and the engineering practices of corrosion control in power plants can benefit considerably from the development of in situ on-line instruments for characterisation of the surface films on construction materials. In this work a new in situ Contact Electric Resistance (CER) technique has been developed for measurement of electric resistance of surface films on metals. The CER technique was applied in this work in several different research areas. These include e.g. localized corrosion of stainless steel in paper mill wet end environment, investigation of the effect of inhibitors in steam generator crevice environments, passivation of GaAs single crystals by sulphate treatment and monitoring of the kinetics of oxide growth on zirconium metals in high temperature water. The CER technique has a measurement capacity ranging from 10-9 {omega} to 105 {omega}. The lowest range of resistance is typical for metallic layers deposited on the surface in electrodeposition processes. The highest range of resistance is found for insulator type of films e.g. on zirconium metals. (author)

  8. The electrical resistivity method in cased boreholes

    Energy Technology Data Exchange (ETDEWEB)

    Schenkel, C.J.

    1991-05-01

    The use of downhole current sources in resistivity mapping can greatly enhance the detection and delineation of subsurface features. The purpose of this work is to examine the resistivity method for current sources in wells cased with steel. The resistivity method in cased boreholes with downhole current sources is investigated using the integral equation (IE) technique. The casing and other bodies are characterized as conductivity inhomogeneities in a half-space. For sources located along the casing axis, an axially symmetric Green's function is used to formulate the surface potential and electric field (E-field) volume integral equations. The situations involving off-axis current sources and three-dimensional (3-D) bodies is formulated using the surface potential IE method. The solution of the 3-D Green's function is presented in cylindrical and Cartesian coordinate systems. The methods of moments is used to solve the Fredholm integral equation of the second kind for the response due to the casing and other bodies. The numerical analysis revealed that the current in the casing can be approximated by its vertical component except near the source and the axial symmetric approximation of the casing is valid even for the 3-D problem. The E-field volume IE method is an effective and efficient technique to simulate the response of the casing in a half-space, whereas the surface potential approach is computationally better when multiple bodies are involved. Analyzing several configurations of the current source indicated that the casing response is influenced by four characteristic factors: conduction length, current source depth,casing depth, and casing length. 85 refs., 133 figs., 11 tabs.

  9. Experimental Studies on the Changes in Resistivity and Its Anisotropy Using Electrical Resistivity Tomography

    Directory of Open Access Journals (Sweden)

    Tao Zhu

    2012-01-01

    Full Text Available Three measuring lines were arranged on one of free planes of magnetite cuboid samples. Apparent resistivity data were acquired by MIR-2007 resistivity meter when samples were under uniaxial compression of servocontrol YAW-5000F loadingmachine in laboratory. Then we constructed the residual resistivity images using electrical resistivity tomography (ERT and plotted the diagrams of apparent resistivity anisotropy coefficient (ARAC λ∗ and the included angle α between the major axis of apparent resistivity anisotropy ellipse and the axis of load with pressure and effective depth. Our results show that with increasing pressure, resistivity and the decreased (D region and increased (I region resistivity regions have complex behaviors, but when pressure is higher than a certain value, the average resistivity decrease and the area of D region expand gradually in all time with the increase of pressure, which may be significant to the monitoring and prediction of earthquake, volcanic activities, and large-scale geologic motions. The effects of pressure on λ∗ and α are not very outstanding for dry magnetite samples.

  10. Mounting Thin Samples For Electrical Measurements

    Science.gov (United States)

    Matus, L. G.; Summers, R. L.

    1988-01-01

    New method for mounting thin sample for electrical measurements involves use of vacuum chuck to hold a ceramic mounting plate, which holds sample. Contacts on mounting plate establish electrical connection to sample. Used to make electrical measurements over temperature range from 77 to 1,000 K and does not introduce distortions into magnetic field during Hall measurements.

  11. Measuring The Contact Resistances Of Photovoltaic Cells

    Science.gov (United States)

    Burger, D. R.

    1985-01-01

    Simple method devised to measure contact resistances of photovoltaic solar cells. Method uses readily available equipment and applicable at any time during life of cell. Enables evaluation of cell contact resistance, contact-end resistance, contact resistivity, sheet resistivity, and sheet resistivity under contact.

  12. Laboratory Electrical Resistivity Studies on Cement Stabilized Soil

    Science.gov (United States)

    Lokesh, K. N.; Jacob, Jinu Mary

    2017-01-01

    Electrical resistivity measurement of freshly prepared uncured and cured soil-cement materials is done and the correlations between the factors controlling the performance of soil-cement and electrical resistivity are discussed in this paper. Conventional quality control of soil-cement quite often involves wastage of a lot of material, if it does not meet the strength criteria. In this study, it is observed that, in soil-cement, resistivity follows a similar trend as unconfined compressive strength, with increase in cement content and time of curing. Quantitative relations developed for predicting 7-day strength of soil-cement mix, using resistivity of the soil-cement samples at freshly prepared state, after 1-hour curing help to decide whether the soil-cement mix meets the desired strength and performance criteria. This offers the option of the soil-cement mix to be upgraded (possibly with additional cement) in its fresh state itself, if it does not fulfil the performance criteria, rather than wasting the material after hardening. PMID:28540364

  13. Induction Motors by Electric Measurements

    Directory of Open Access Journals (Sweden)

    Andrzej M. Trzynadlowski

    1999-01-01

    Full Text Available The paper gives an overview of the issues and means of detection of mechanical abnormalities in induction motors by electric measurements. If undetected and untreated, the worn or damaged bearings, rotor imbalance and eccentricity, broken bars of the rotor cage, and torsional and lateral vibration lead to roughly a half of all failures of induction motor drives. The detection of abnormalities is based on the fact that they cause periodic disturbance of motor variables, such as the speed, torque, current, and magnetic flux. Thus, spectral analysis of those or related quantities may yield a warning about an incipient failure of the drive system. Although the traditional non-invasive diagnostics has mostly been based on the signature analysis of the stator current, other media can also be employed. In particular, the partial instantaneous input power is shown, theoretically and experimentally, to offer distinct advantages under noisy operating conditions. Use of torque and flux estimates is also discussed.

  14. Geo-electric measurements – internal state of historic masonry

    OpenAIRE

    Schueremans, Luc

    2009-01-01

    A geophysical resistivity measuring device was modified to perform automatic monitoring of historical masonry structures before, during and after grout injection for consolidation purposes. The obtained image is called a geo-electrical tomography. The technique was used to evaluate the deteriorated masonry of the recently partly collapsed Maagdentoren in Zichem,(B). Geo-electric measuring techniques have been adapted from application in geology to be used as a non-destructive technique for t...

  15. Analysis of electric vehicles measurements

    NARCIS (Netherlands)

    Vonk, B.M.J.; Geldtmeijer, D.A.M.; Slootweg, J.G.

    2013-01-01

    Electric vehicles are expected to have a significant impact on electricity grids. Intelligent charging strategies are suggested by literature and tested in the field to prevent overloading of network assets in electricity grids by using the flexibility of electro-mobility. This paper covers an

  16. Hydrologic Process-oriented Optimization of Electrical Resistivity Tomography

    Science.gov (United States)

    Hinnell, A.; Bechtold, M.; Ferre, T. A.; van der Kruk, J.

    2010-12-01

    Electrical resistivity tomography (ERT) is commonly used in hydrologic investigations. Advances in joint and coupled hydrogeophysical inversion have enhanced the quantitative use of ERT to construct and condition hydrologic models (i.e. identify hydrologic structure and estimate hydrologic parameters). However the selection of which electrical resistivity data to collect and use is often determined by a combination of data requirements for geophysical analysis, intuition on the part of the hydrogeophysicist and logistical constraints of the laboratory or field site. One of the advantages of coupled hydrogeophysical inversion is the direct link between the hydrologic model and the individual geophysical data used to condition the model. That is, there is no requirement to collect geophysical data suitable for independent geophysical inversion. The geophysical measurements collected can be optimized for estimation of hydrologic model parameters rather than to develop a geophysical model. Using a synthetic model of drip irrigation we evaluate the value of individual resistivity measurements to describe the soil hydraulic properties and then use this information to build a data set optimized for characterizing hydrologic processes. We then compare the information content in the optimized data set with the information content in a data set optimized using a Jacobian sensitivity analysis.

  17. Direct quantification of transendothelial electrical resistance in organs-on-chips

    NARCIS (Netherlands)

    van der Helm, Marieke Willemijn; Odijk, Mathieu; Frimat, Jean-Philippe; van der Meer, Andries Dirk; Eijkel, Jan C.T.; van den Berg, Albert; Segerink, Loes Irene

    2016-01-01

    Measuring transendothelial or transepithelial electrical resistance (TEER) is a widely used method to monitor cellular barrier tightness in organs-on-chips. Unfortunately, integrated electrodes close to the cellular barrier hamper visual inspection of the cells or require specialized cleanroom

  18. An Electric Resistivity Study of the Chelungpu Fault in the Taichung Area, Taiwan

    Directory of Open Access Journals (Sweden)

    Ping-Hu Cheng

    2008-01-01

    Full Text Available We conducted an electric resistivity survey consisting of six resistivity image profilings and several resistivity measurements on outcrops of strata in the Taichung area to investigate the subsurface structures of the Chelungpu fault. Three magnetotelluric sounding results are added to infer rock formations at depth. Based on the resistivity measurements on outcrops of the strata and the correlations between the interpretative resistivity structures and the rock formations recognized from drilling cores and the outcrops of the strata, the resistivity spectra of rock formations are obtained, and the geological structures are deduced.

  19. Measurement of Dynamic Resistance in Resistance Spot Welding

    DEFF Research Database (Denmark)

    Wu, Pei; Zhang, Wenqi; Bay, Niels

    Through years, the dynamic resistance across the electrodes has been used for weld quality estimation and contact resistance measurement. However, the previous methods of determining the dynamic resistance were mostly based on measuring the voltage and current on the secondary side of the transfo......Through years, the dynamic resistance across the electrodes has been used for weld quality estimation and contact resistance measurement. However, the previous methods of determining the dynamic resistance were mostly based on measuring the voltage and current on the secondary side...... of the transformer in resistance welding machines, implying defects from induction noise and interference with the leads connected to the electrodes for measuring the voltage. In this study, the dynamic resistance is determined by measuring the voltage on the primary side and the current on the secondary side...

  20. Characterizations of Soil Profiles Through Electric Resistivity Ratio

    Directory of Open Access Journals (Sweden)

    Chik Z

    2015-04-01

    Full Text Available This paper presents how near surface soil characteristics are obtained through soil electric resistivity ratio from soil apparent resistivity profile. In recent advances of electrical sensors, soil apparent resistivity is implemented as nondestructive method for obtaining near surface soil profile. Although geo-electric techniques offer an improvement to traditional soil sampling methods, the resulting data are still often misinterpreted for obtaining soil characteristics through apparent electrical resistivity in the field. Because, soil resistivity as before rain and after rain are changeable due to the presence of more moisture contents in field investigations. In this study, the parameter of soil electric resistivity ratio is incorporated to obtain reliable near surface soil profiles from apparent resistivity of adjacent two layers in soil. The variations of potential differences are taken into account for using four probes method to get the soil apparent resistivity profile. The research is significant for simpler and faster soil characterizations using resistivity ratio of apparent resistivity in soil investigations.

  1. Iron aluminide useful as electrical resistance heating elements

    Science.gov (United States)

    Sikka, Vinod K.; Deevi, Seetharama C.; Fleischhauer, Grier S.; Hajaligol, Mohammad R.; Lilly, Jr., A. Clifton

    1997-01-01

    The invention relates generally to aluminum containing iron-base alloys useful as electrical resistance heating elements. The aluminum containing iron-base alloys have improved room temperature ductility, electrical resistivity, cyclic fatigue resistance, high temperature oxidation resistance, low and high temperature strength, and/or resistance to high temperature sagging. The alloy has an entirely ferritic microstructure which is free of austenite and includes, in weight %, over 4% Al, .ltoreq.1% Cr and either .gtoreq.0.05% Zr or ZrO.sub.2 stringers extending perpendicular to an exposed surface of the heating element or .gtoreq.0.1% oxide dispersoid particles. The alloy can contain 14-32% Al, .ltoreq.2% Ti, .ltoreq.2% Mo, .ltoreq.1% Zr, .ltoreq.1% C, .ltoreq.0.1% B, .ltoreq.30% oxide dispersoid and/or electrically insulating or electrically conductive covalent ceramic particles, .ltoreq.1% rare earth metal, .ltoreq.1% oxygen, .ltoreq.3% Cu, balance Fe.

  2. Iron aluminide useful as electrical resistance heating elements

    Science.gov (United States)

    Sikka, V.K.; Deevi, S.C.; Fleischhauer, G.S.; Hajaligol, M.R.; Lilly, A.C. Jr.

    1997-04-15

    The invention relates generally to aluminum containing iron-base alloys useful as electrical resistance heating elements. The aluminum containing iron-base alloys have improved room temperature ductility, electrical resistivity, cyclic fatigue resistance, high temperature oxidation resistance, low and high temperature strength, and/or resistance to high temperature sagging. The alloy has an entirely ferritic microstructure which is free of austenite and includes, in weight %, over 4% Al, {=}0.05% Zr or ZrO{sub 2} stringers extending perpendicular to an exposed surface of the heating element or {>=}0.1% oxide dispersoid particles. The alloy can contain 14-32% Al, {<=}2% Ti, {<=}2% Mo, {<=}1% Zr, {<=}1% C, {<=}0.1% B, {<=}30% oxide dispersoid and/or electrically insulating or electrically conductive covalent ceramic particles, {<=}1% rare earth metal, {<=}1% oxygen, {<=}3% Cu, balance Fe. 64 figs.

  3. Electricity

    CERN Document Server

    Basford, Leslie

    2013-01-01

    Electricity Made Simple covers the fundamental principles underlying every aspect of electricity. The book discusses current; resistance including its measurement, Kirchhoff's laws, and resistors; electroheat, electromagnetics and electrochemistry; and the motor and generator effects of electromagnetic forces. The text also describes alternating current, circuits and inductors, alternating current circuits, and a.c. generators and motors. Other methods of generating electromagnetic forces are also considered. The book is useful for electrical engineering students.

  4. The effect of oxygen-doping on the electrical resistivity of vanadium

    International Nuclear Information System (INIS)

    Lang, E.; Bressers, J.

    1975-01-01

    High-purity vanadium single crystals characterized by resistance ratios in the range of 1,100 were doped to different oxygen levels and their electrical resistivity increase was measured as a function of the oxygen concentration. In the temperature range investigated, 77 to 293 K, the Matthiessen rule is obeyed. The increase in electrical resistivity per atomic percent oxygen is shown to be 5.16 μΩcm. For the ideal resistivity ratio rhosub(i) (77 K)/rhosub(i) (293 K) a value of 0.116 could be determined. (orig.) [de

  5. Resistance and sheet resistance measurements using electron beam induced current

    International Nuclear Information System (INIS)

    Czerwinski, A.; Pluska, M.; Ratajczak, J.; Szerling, A.; KaPtcki, J.

    2006-01-01

    A method for measurement of spatially uniform or nonuniform resistance in layers and strips, based on electron beam induced current (EBIC) technique, is described. High electron beam currents are used so that the overall resistance of the measurement circuit affects the EBIC signal. During the evaluation, the electron beam is scanned along the measured object, whose load resistance varies with the distance. The variation is compensated by an adjustable resistance within an external circuit. The method has been experimentally deployed for sheet resistance determination of buried regions of lateral confinements in semiconductor laser heterostructures manufactured by molecular beam epitaxy

  6. Detection of sinkholes using 2D electrical resistivity imaging

    CSIR Research Space (South Africa)

    Van Schoor, Abraham M

    2002-07-01

    Full Text Available Sinkholes in dolomitic areas are notoriously difficult geophysical targets, and selecting an appropriate geophysical solution is not straightforward. Electrical resistivity imaging or tomography (RESTOM) is well suited to mapping sinkholes because...

  7. Imaging voids beneath bridge bent using electrical resistivity tomography.

    Science.gov (United States)

    2014-02-01

    Five electrical resistivity tomography (ERT) profiles and borehole control were acquired beneath two bridges on the bank of the : Gasconade River in order to determine extension of the underground water-filled openings in rock encountered during a dr...

  8. Electrical resistivity of Y(Fe1-x Alx)2 in the spin glass concentration range

    International Nuclear Information System (INIS)

    Cunha, S.F. da; Souza, G.P. de; Takeushi, A.Y.

    1986-01-01

    The temperature dependence of the electrical resistivity of the Y(Fe 1-x Al x ) 2 system (0.125 ≤ x ≤ 0.25) was measured. This system exhibits a minimum at low temperatures for the concentration range where the phase diagram presents a spin glass-ferromagnetic transition. A negative temperature coefficient is observed at high temperatures for x > 0.18 and was attributed to the high value of the electrical resistivity in this concentration range. (Author) [pt

  9. Measurement of microchannel fluidic resistance with a standard voltage meter

    International Nuclear Information System (INIS)

    Godwin, Leah A.; Deal, Kennon S.; Hoepfner, Lauren D.; Jackson, Louis A.; Easley, Christopher J.

    2013-01-01

    Highlights: ► Standard voltage meter used to measure fluidic resistance. ► Manual measurement takes a few seconds, akin to electrical resistance measurements. ► Measurement error is reduced compared to other approaches. ► Amenable to dynamic measurement of fluidic resistance. - Abstract: A simplified method for measuring the fluidic resistance (R fluidic ) of microfluidic channels is presented, in which the electrical resistance (R elec ) of a channel filled with a conductivity standard solution can be measured and directly correlated to R fluidic using a simple equation. Although a slight correction factor could be applied in this system to improve accuracy, results showed that a standard voltage meter could be used without calibration to determine R fluidic to within 12% error. Results accurate to within 2% were obtained when a geometric correction factor was applied using these particular channels. When compared to standard flow rate measurements, such as meniscus tracking in outlet tubing, this approach provided a more straightforward alternative and resulted in lower measurement error. The method was validated using 9 different fluidic resistance values (from ∼40 to 600 kPa s mm −3 ) and over 30 separately fabricated microfluidic devices. Furthermore, since the method is analogous to resistance measurements with a voltage meter in electrical circuits, dynamic R fluidic measurements were possible in more complex microfluidic designs. Microchannel R elec was shown to dynamically mimic pressure waveforms applied to a membrane in a variable microfluidic resistor. The variable resistor was then used to dynamically control aqueous-in-oil droplet sizes and spacing, providing a unique and convenient control system for droplet-generating devices. This conductivity-based method for fluidic resistance measurement is thus a useful tool for static or real-time characterization of microfluidic systems.

  10. Instrument for measuring metal-thermoelectric semiconductor contact resistence

    International Nuclear Information System (INIS)

    Lanxner, M.; Nechmadi, M.; Meiri, B.; Schildkraut, I.

    1979-02-01

    An instrument for measuring electrical, metal-thermoelectric semiconductor contact resistance is described. The expected errors of measurement are indicated. The operation of the instrument which is based on potential traversing perpendicularly to the contact plane is illustrated for the case of contacts of palladium and bismuth telluride-based thermoelectric material

  11. Electrical Resistance Based Damage Modeling of Multifunctional Carbon Fiber Reinforced Polymer Matrix Composites

    Science.gov (United States)

    Hart, Robert James

    In the current thesis, the 4-probe electrical resistance of carbon fiber-reinforced polymer (CFRP) composites is utilized as a metric for sensing low-velocity impact damage. A robust method has been developed for recovering the directionally dependent electrical resistivities using an experimental line-type 4-probe resistance method. Next, the concept of effective conducting thickness was uniquely applied in the development of a brand new point-type 4-probe method for applications with electrically anisotropic materials. An extensive experimental study was completed to characterize the 4-probe electrical resistance of CFRP specimens using both the traditional line-type and new point-type methods. Leveraging the concept of effective conducting thickness, a novel method was developed for building 4-probe electrical finite element (FE) models in COMSOL. The electrical models were validated against experimental resistance measurements and the FE models demonstrated predictive capabilities when applied to CFRP specimens with varying thickness and layup. These new models demonstrated a significant improvement in accuracy compared to previous literature and could provide a framework for future advancements in FE modeling of electrically anisotropic materials. FE models were then developed in ABAQUS for evaluating the influence of prescribed localized damage on the 4-probe resistance. Experimental data was compiled on the impact response of various CFRP laminates, and was used in the development of quasi- static FE models for predicting presence of impact-induced delamination. The simulation-based delamination predictions were then integrated into the electrical FE models for the purpose of studying the influence of realistic damage patterns on electrical resistance. When the size of the delamination damage was moderate compared to the electrode spacing, the electrical resistance increased by less than 1% due to the delamination damage. However, for a specimen with large

  12. Measurement of resistivity changes in irradiated microscopy discs

    International Nuclear Information System (INIS)

    Sagisaka, M.; Isobe, Y.; Edwards, D.J.; Garner, F.; Okita, T.

    2007-01-01

    Full text of publication follows: The successful operation of next generation fusion or fission devices will require the development of new inspection tools to allow in-situ, non-destructive examination of structural components which experience the deleterious effects of neutron irradiation. Such development requires that an understanding of how radiation-induced microstructural alteration contributes to macroscopic changes in physical properties such as electrical resistivity. This in turn requires test specimens spanning a range of microstructural alteration. Frequently such specimens are very small and available test techniques are not suitable for their examination. An example is the use of thin TEM specimens (3 mm diameter, 0.3 mm thick) used for electron microscopy. A unique four probe electrical resistivity measurement system suitable for examining I EM specimens was developed for investigating small resistivity changes due to void swelling and other microstructural features. Since this system uses momentarily-high electrical currents (0.5 A maximum), electrical resistivity changes can be measured rather precisely. This paper reports results of resistivity change measurements made on model Fe-Cr-Ni-Zr austenitic alloys irradiated in the Fast Flux Test Facility in the Materials Open Test Assembly to doses ranging from 0.38 to 19.2 dpa. Microscopy was used to determine the radiation-induced microstructure. A correlation is presented for resistivity changes arising primarily from void swelling. (authors)

  13. Modeling the electrical resistance of gold film conductors on uniaxially stretched elastomeric substrates

    Science.gov (United States)

    Cao, Wenzhe; Görrn, Patrick; Wagner, Sigurd

    2011-05-01

    The electrical resistance of gold film conductors on polydimethyl siloxane substrates at stages of uniaxial stretching is measured and modeled. The surface area of a gold conductor is assumed constant during stretching so that the exposed substrate takes up all strain. Sheet resistances are calculated from frames of scanning electron micrographs by numerically solving for the electrical potentials of all pixels in a frame. These sheet resistances agree sufficiently well with values measured on the same conductors to give credence to the model of a stretchable network of gold links defined by microcracks.

  14. Rolling Resistance Measurement and Model Development

    DEFF Research Database (Denmark)

    Andersen, Lasse Grinderslev; Larsen, Jesper; Fraser, Elsje Sophia

    2015-01-01

    There is an increased focus worldwide on understanding and modeling rolling resistance because reducing the rolling resistance by just a few percent will lead to substantial energy savings. This paper reviews the state of the art of rolling resistance research, focusing on measuring techniques, s......, surface and texture modeling, contact models, tire models, and macro-modeling of rolling resistance...

  15. Electrical Resistivity Survey For Conductive Soils At Gas Turbine ...

    African Journals Online (AJOL)

    Ten (10) vertical electrical soundings (VES) using Schlumberger configuration were carried out to delineate subsurface conductive soils for the design of earthling grid for electrical materials installation at the Gas Turbine Station, Ajaokuta, SW Nigeria. Interpretation of the resistivity data revealed three major geoelectric ...

  16. Application of electrical resistance tomography to glass melter

    International Nuclear Information System (INIS)

    Ichijo, Noriaki; Sakai, Taiji; Fujiwara, Hiroaki; Matsuno, Shinsuke; Misumi, Ryuta; Nishi, Kazuhiko; Kaminoyama, Meguru

    2015-01-01

    This paper describes the application of electrical resistance tomography (ERT) to glass melter to monitor the accumulation of the noble metals. To minimize the modification of the melter, existing structures such as thermowells and heating electrodes are used as electrodes of ERT, and the number of electrodes is much fewer than the conventional method. Therefore, Expanding Combination Data Acquisition method (ECDA) is developed and applies to the glass melter. ECDA method uses adjacent method and opposite method as a data acquisition and current injection electrodes are used as voltage measurement electrodes to increase the number of the data. In addition, conductivity images are reconstructed only near the wall to improve the resolution. As a result of applying to the glass melter, the conductivity change inside the melter caused by temperature can be monitored. Furthermore, lower voltage is measured in case of containing the noble metals inside the melter. Therefore, the potential as a monitoring method be confirmed. (author)

  17. Fringe effect of electrical capacitance and resistance tomography sensors

    International Nuclear Information System (INIS)

    Sun, Jiangtao; Yang, Wuqiang

    2013-01-01

    Because of the ‘soft-field’ nature, all electrical tomography sensors suffer from electric field distortion, i.e. the fringe effect. In electrical resistance tomography (ERT) sensors, small pin electrodes are commonly used. It is well known that the pin electrodes result in severe electric field distortion or the fringe effect, and the sensing region of such an ERT sensor spreads out of the pin electrode plane to a large volume. This is also true for electrical capacitance tomography (ECT) sensors, even though it is less severe because of larger electrodes and grounded end guards used. However, when the length of electrodes in an ECT sensor without guards is reduced to almost the same dimension as those in an ERT sensor, the fringe effect is equally obvious. To investigate the fringe effect of ERT and ECT sensors with and without guards, simulations were carried out with different length of electrodes and the results are compared with the corresponding 2D simulation. It is concluded that ECT and ERT sensors with longer electrodes have less fringe effect. Because grounded end guards are effective in reducing the fringe effect of ECT sensors, we propose to apply grounded guards in ERT sensors and integrate ECT and ERT sensors together. Simulation results reveal that ERT sensors with grounded guards have less fringe effect. While commonly current excitation is used with ERT sensors, we propose voltage excitation instead to apply the grounded guards. The feasibility of this approach has been verified by experiment. Finally, a common structure for reducing the fringe effect is proposed for ECT and ERT sensors for the first time to simplify the sensor structure and reduce the mutual interference in ECT/ERT dual-modality measurements. (paper)

  18. Electrical resistivity of liquid Ag-Au alloy

    International Nuclear Information System (INIS)

    Anis Alam, M.; Tomak, M.

    1983-01-01

    Calculations of the dependence of the electrical resistivity in liquid Ag-Au binary alloy on composition are reported. The structure of the binary alloy is described as a hard-sphere system. A one-parameter local pseudopotential, which incorporates s-d hybridization effects phenomenologically, is employed in the resistivity calculation. A reasonable agreement with experimental trend is observed. (author)

  19. Effects of iron content on electrical resistivity of oxide films on Zr-base alloys

    International Nuclear Information System (INIS)

    Kubo, Toshio; Uno, Masayoshi

    1991-01-01

    Measurements of electrical resistivity were made for oxide films formed by anodic oxidation and steam oxidation (400degC/12 h) on Zr plates with different Fe contents. When the Fe content was higher than about 1,000 ppm the electrical resistivity of the steam oxide films was almost equivalent to that of the anodic oxide films, while at lower Fe content the former exhibited lower electrical resistivity than the latter by about 1∼3 orders of magnitude. The anodic oxide film was an almost homogeneous single oxide layer. The steam oxide films, on the other hand, were composed of duplex oxide layers. The oxide layer formed in the vicinity of the oxide/metal interface had higher electrical resistivity than the near-surface oxide layer by about 1∼4 orders of magnitude. The oxide layer in the vicinity of the interface could act as a protective film against corrosion and its electrical resistivity is one important factor controlling the layer protectiveness. The electrical resistivity of the oxide/metal interfacial layer was strongly dependent on the Fe content. One possible reason for Fe to improve the corrosion resistance is that Fe ions would tend to stabilize the tetragonal (or cubic) phase and consequently suppress the formation of open pores and cracks in the interfacial layer. (author)

  20. An Experimental Study of the Electrical Contact Resistance in Resistance Welding

    DEFF Research Database (Denmark)

    Song, Quanfeng; Zhang, Wenqi; Bay, Niels

    2005-01-01

    Electrical contact resistance is of critical importance in resistance welding. In this article, the contact resistance is experimentally investigated for welding mild steel, stainless steel, and aluminum to themselves. A parametric study was carried out on a Gleeble® machine, investigating...

  1. Resistance switching induced by electric fields in manganite thin films

    International Nuclear Information System (INIS)

    Villafuerte, M; Juarez, G; Duhalde, S; Golmar, F; Degreef, C L; Heluani, S P

    2007-01-01

    In this work, we investigate the polarity-dependent Electric Pulses Induced Resistive (EPIR) switching phenomenon in thin films driven by electric pulses. Thin films of 0.5 Ca 0.5 MnO 3 (manganite) were deposited by PLD on Si substrate. The transport properties at the interface between the film and metallic electrode are characterized in order to study the resistance switching. Sample thermal treatment and electrical field history are important to be considered for get reproducible EPIR effect. Carriers trapping at the interfaces are considered as a possible explanation of our results

  2. Environmental Sciences Electrical resistivity soundings to determine ...

    African Journals Online (AJOL)

    Wood, leaves, newspaper, cloth, polythene bags, plastics, glass and metal refuse interspersed with soil exhibited resistivity of 11.6 ohm-m and layer thickness of 0.7 m as obtained from the inversion of the sounding. The unsaturated layer has a resistivity of 6.8 ohm-m and thickness of 0.6 m while leachate-saturated is ...

  3. Measurement of Dynamic Resistance in Resistance Spot Welding

    DEFF Research Database (Denmark)

    Wu, Pei; Lu, J.; Zhang, Wenqi

    2007-01-01

    is influenced by inductive noise caused by the high welding current. In this study, the dynamic resistance is determined by measuring the voltage at primary side and current at secondary side. This increases the accuracy of measurement because of higher signal-noise ratio, and allows to apply to in-process......The conventional methods of determining the dynamic resistance were mostly done by measuring the voltage and current at secondary side of transformer in resistance welding machines, in which the measuring set-up normally interferes with the movement of electrode, and the measuring precision...

  4. A Prototype System for Time-Lapse Electrical Resistivity Tomographies

    Directory of Open Access Journals (Sweden)

    Raffaele Luongo

    2012-01-01

    Full Text Available A prototype system for time-lapse acquisition of 2D electrical resistivity tomography (ERT and time domain reflectometry (TDR measurements was installed in a test site affected by a landslide in Basilicata region (southern Italy. The aim of the system is to monitor in real-time the rainwater infiltration into the soil and obtain information about the variation of the water content in the first layers of the subsoil and the possible influence of this variation on landslide activity. A rain gauge placed in the test site gives information on the rainfall intensity and frequency and suggests the acquisition time interval. The installed system and the preliminary results are presented in this paper.

  5. Experimental study of the electric resistivity in Heusler alloys

    International Nuclear Information System (INIS)

    Kunzler, J.V.

    1980-01-01

    Electrical resistivity measurements have been performed in the Cu 2 Mn (A1sub(1-x) Snsub(x)) Heusler alloys, where x = 0, 0.05, 0.10 and 0.15, in the temperature range from 4.2 to 800 0 K. Measurements have also been made on the Ni 2 MnX Heusler asloys, with X = In, Sn or Sb, in the range from 4.2 to 300 0 K. The experimental curves clearly show the importance of the ferromagnetic character for the alloys resistivity. The results obtained for the copper alloys, as well as for the Ni 2 MnSn alloy, are in agreement with an interpretation in terms of Bloch-Gruneisen and spin-disorder models, and fail to provide evidences of s-d scattering for the conduction electrons. This is not the case for the Ni 2 MnIn and Ni 2 MnSb alloys, in which the presence of (s-d) interband electronic scattering process, via phonon, was detected. Specially for the two last alloys specific heat and electronic photo-emissivity experiments are suggested. (Author) [pt

  6. Two devices for atmospheric electric field measurement

    International Nuclear Information System (INIS)

    Colombet, Andre; Hubert, Pierre.

    1977-02-01

    Two instruments installed at St Privat d'Allier for electric field measurement in connection with the rocket triggered lighting experiment program are described. The first one is a radioactive probe electrometer used as a warning device. The second is a field mill used for tape recording of electric field variation during the triggering events. Typical examples of such records are given [fr

  7. Electrical measurements in the laboratory practice

    CERN Document Server

    Bartiromo, Rosario

    2016-01-01

    This book covers the basic theory of electrical circuits, describes analog and digital instrumentation, and applies modern methods to evaluate uncertainties in electrical measurements. It is comprehensive in scope and is designed specifically to meet the needs of students in physics and electrical engineering who are attending laboratory classes in electrical measurements. The topics addressed in individual chapters include the analysis of continuous current circuits; sources of measurement uncertainty and their combined effect; direct current measurements; analysis of alternating current circuits; special circuits including resonant circuits, frequency filters and impedance matching networks; alternating current measurements; analog and digital oscilloscopes; non-sinusoidal waveforms and circuit excitation by pulses; distributed parameter components and transmission lines. Each chapter is equipped with a number of problems. A special appendix describes a series of nine experiments, in each case providing a p...

  8. Electrical resistivity of nanoporous gold modified with thiol self-assembled monolayers

    Energy Technology Data Exchange (ETDEWEB)

    Hakamada, Masataka, E-mail: hakamada.masataka.3x@kyoto-u.ac.jp; Kato, Naoki, E-mail: katou.naoki.75w@st.kyoto-u.ac.jp; Mabuchi, Mamoru, E-mail: mabuchi@energy.kyoto-u.ac.jp

    2016-11-30

    Highlights: • Nanoporous gold is modified with thiol-containing self-assembled monolayers. • The electrical resistivity of the thiol-modified nanoporous gold increases. • The electrical resistivity increases with increasing thiol concentration. • Monolayer tail groups enhance the atmosphere dependence of electrical resistivity. - Abstract: The electrical resistivity of nanoporous gold (NPG) modified with thiol self-assembled monolayers (SAMs) has been measured at 298 K using a four-probe method. We found that the adsorption of thiol SAMs increases the electrical resistivity of NPG by up to 22.2%. Dependence of the electrical resistivity on the atmosphere (air or water) was also observed in SAMs-modified NPG, suggesting that the electronic states of the tail groups affect the electrons of the binding sulfur and adjacent surface gold atoms. The present results suggest that adsorption of thiol molecules can influence the behavior of the conducting electrons in NPG and that modification of NPG with SAMs may be useful for environmental sensing.

  9. Insulating and sheathing materials of electric and optical cables: common test methods part 4-1: methods specific to polyethylene and polypropylene compounds – resistance to environmental stress cracking – measurement of the melt flow index – carbon black and/or mineral filler content measurement in polyethylene by direct combustion – measurement of carbon black content by thermogravimetric analysis (TGA) – assessment of carbon black dispersion in polyethylene using a microscope

    CERN Document Server

    International Electrotechnical Commission. Geneva

    2004-01-01

    Specifies the test methods to be used for testing polymeric insulating and sheathing materials of electric cables for power distribution and telecommunications including cables used on ships. Gives the methods for measurements of the resistance to environmental stress cracking, for wrapping test after thermal ageing in air, for measurement of melt flow index and for measurement of carbon black and/or mineral filler content, which apply to PE and PP coumpounds, including cellular compounds and foam skin for insulation.

  10. Strain-dependent electrical resistance of multi-walled carbon nanotube/polymer composite films

    International Nuclear Information System (INIS)

    Park, Myounggu; Kim, Hyonny; Youngblood, Jeffrey P

    2008-01-01

    The strain-dependent electrical resistance characteristics of multi-walled carbon nanotube (MWCNT)/polymer composite films were investigated. In this research, polyethylene oxide (PEO) is used as the polymer matrix. Two representative volume fractions of MWCNT/PEO composite films were selected: 0.56 vol% (near the percolation threshold) and 1.44 vol% (away from the percolation threshold) of MWCNT. An experimental setup which can measure electrical resistance and strain simultaneously and continuously has been developed. Unique and repeatable relationships in resistance versus strain were obtained for multiple specimens with different volume fractions of MWCNT. The overall pattern of electrical resistance change versus strain for the specimens tested consists of linear and nonlinear regions. A resistance change model to describe the combination of linear and nonlinear modes of electrical resistance change as a function of strain is suggested. The unique characteristics in electrical resistance change for different volume fractions imply that MWCNT/PEO composite films can be used as tunable strain sensors and for application into embedded sensor systems in structures

  11. Methods for detecting and locating leaks in containment facilities using electrical potential data and electrical resistance tomographic imaging techniques

    Science.gov (United States)

    Daily, William D.; Laine, Daren L.; Laine, Edwin F.

    1997-01-01

    Methods are provided for detecting and locating leaks in liners used as barriers in the construction of landfills, surface impoundments, water reservoirs, tanks, and the like. Electrodes are placed in the ground around the periphery of the facility, in the leak detection zone located between two liners if present, and/or within the containment facility. Electrical resistivity data is collected using these electrodes. This data is used to map the electrical resistivity distribution beneath the containment liner between two liners in a double-lined facility. In an alternative embodiment, an electrode placed within the lined facility is driven to an electrical potential with respect to another electrode placed at a distance from the lined facility (mise-a-la-masse). Voltage differences are then measured between various combinations of additional electrodes placed in the soil on the periphery of the facility, the leak detection zone, or within the facility. A leak of liquid though the liner material will result in an electrical potential distribution that can be measured at the electrodes. The leak position is located by determining the coordinates of an electrical current source pole that best fits the measured potentials with the constraints of the known or assumed resistivity distribution.

  12. Electrical measurement of sweat activity

    International Nuclear Information System (INIS)

    Tronstad, Christian; Grimnes, Sverre; Martinsen, Ørjan G; Gjein, Gaute E; Fosse, Erik; Krogstad, Anne-Lene

    2008-01-01

    A multichannel logger for long-term measurements of sweat activity is presented. The logger uses skin surface electrodes for unipolar admittance measurements in the stratum corneum. The logger is developed with emphasis on clinical use. The portability of the logger enables recording of sweat activity under circumstances such as daily errands, exercise and sleep. Measurements have been done on 24 healthy volunteers during relaxation and exercise with heart rate monitoring. Recordings of sweat activity during sleep have been done on two healthy subjects. Early results show good agreement with the literature on sweating physiology and electrodermal activity. Results are presented showing measurements related to physical exercise, dermatomes, distribution of sweat glands and sympathetic activity. This study examines the normal sweating patterns for the healthy population, and we present results with the first 24 healthy volunteers. Comparing these results with similar measurements on hyperhidrosis patients will make it possible to find the most useful parameters for diagnosis and treatment evaluation

  13. Static Measurements on HTS Coils of Fully Superconducting AC Electric Machines for Aircraft Electric Propulsion System

    Science.gov (United States)

    Choi, Benjamin B.; Hunker, Keith R.; Hartwig, Jason; Brown, Gerald V.

    2017-01-01

    The NASA Glenn Research Center (GRC) has been developing the high efficiency and high-power density superconducting (SC) electric machines in full support of electrified aircraft propulsion (EAP) systems for a future electric aircraft. A SC coil test rig has been designed and built to perform static and AC measurements on BSCCO, (RE)BCO, and YBCO high temperature superconducting (HTS) wire and coils at liquid nitrogen (LN2) temperature. In this paper, DC measurements on five SC coil configurations of various geometry in zero external magnetic field are measured to develop good measurement technique and to determine the critical current (Ic) and the sharpness (n value) of the super-to-normal transition. Also, standard procedures for coil design, fabrication, coil mounting, micro-volt measurement, cryogenic testing, current control, and data acquisition technique were established. Experimentally measured critical currents are compared with theoretical predicted values based on an electric-field criterion (Ec). Data here are essential to quantify the SC electric machine operation limits where the SC begins to exhibit non-zero resistance. All test data will be utilized to assess the feasibility of using HTS coils for the fully superconducting AC electric machine development for an aircraft electric propulsion system.

  14. Examination of Electrical Resistance of Carburizers Used for Cast Iron Production

    Directory of Open Access Journals (Sweden)

    Książek D.

    2016-12-01

    Full Text Available The publication presents the results of examination of selected carburizers used for cast iron production with respect to their electric resistance. Both the synthetic graphite carburizers and petroleum coke (petcoke carburizers of various chemical composition were compared. The relationships between electrical resistance of tested carburizers and their quality were found. The graphite carburizers exhibited much better conductivity than the petcoke ones. Resistance characteristics were different for the different types of carburizers. The measurements were performed according to the authors’ own method based on recording the electric current flow through the compressed samples. The samples of the specified diameter were put under pressure of the gradually increased value (10, 20, 50, 60, and finally 70 bar, each time the corresponding value of electric resistance being measured with a gauge of high accuracy, equal to 0.1μΩ. The higher pressure values resulted in the lower values of resistance. The relation between both the thermal conductance and the electrical conductance (or the resistance is well known and mentioned in the professional literature. The results were analysed and presented both in tabular and, additionally, in graphic form.

  15. Adding Resistances and Capacitances in Introductory Electricity

    Science.gov (United States)

    Efthimiou, C. J.; Llewellyn, R. A.

    2005-09-01

    All introductory physics textbooks, with or without calculus, cover the addition of both resistances and capacitances in series and in parallel as discrete summations. However, none includes problems that involve continuous versions of resistors in parallel or capacitors in series. This paper introduces a method for solving the continuous problems that is logical, straightforward, and within the mathematical preparation of students at the introductory level.

  16. Influence of electrical resistivity and machining parameters on electrical discharge machining performance of engineering ceramics.

    Science.gov (United States)

    Ji, Renjie; Liu, Yonghong; Diao, Ruiqiang; Xu, Chenchen; Li, Xiaopeng; Cai, Baoping; Zhang, Yanzhen

    2014-01-01

    Engineering ceramics have been widely used in modern industry for their excellent physical and mechanical properties, and they are difficult to machine owing to their high hardness and brittleness. Electrical discharge machining (EDM) is the appropriate process for machining engineering ceramics provided they are electrically conducting. However, the electrical resistivity of the popular engineering ceramics is higher, and there has been no research on the relationship between the EDM parameters and the electrical resistivity of the engineering ceramics. This paper investigates the effects of the electrical resistivity and EDM parameters such as tool polarity, pulse interval, and electrode material, on the ZnO/Al2O3 ceramic's EDM performance, in terms of the material removal rate (MRR), electrode wear ratio (EWR), and surface roughness (SR). The results show that the electrical resistivity and the EDM parameters have the great influence on the EDM performance. The ZnO/Al2O3 ceramic with the electrical resistivity up to 3410 Ω·cm can be effectively machined by EDM with the copper electrode, the negative tool polarity, and the shorter pulse interval. Under most machining conditions, the MRR increases, and the SR decreases with the decrease of electrical resistivity. Moreover, the tool polarity, and pulse interval affect the EWR, respectively, and the electrical resistivity and electrode material have a combined effect on the EWR. Furthermore, the EDM performance of ZnO/Al2O3 ceramic with the electrical resistivity higher than 687 Ω·cm is obviously different from that with the electrical resistivity lower than 687 Ω·cm, when the electrode material changes. The microstructure character analysis of the machined ZnO/Al2O3 ceramic surface shows that the ZnO/Al2O3 ceramic is removed by melting, evaporation and thermal spalling, and the material from the working fluid and the graphite electrode can transfer to the workpiece surface during electrical discharge

  17. Observations on the electrical resistivity of steel fibre reinforced concrete

    DEFF Research Database (Denmark)

    Solgaard, Anders Ole Stubbe; Geiker, Mette Rica; Edvardsen, Carola

    2014-01-01

    concrete the model underestimated the influence of the addition of fibres. The results indicate that the addition of steel fibres reduce the electrical resistivity of concrete if the fibres are conductive. This represents a hypothetical case where all fibres are depassivated (corroding) which was created......Steel fibre reinforced concrete (SFRC) is in many ways a well-known construction material, and its use has gradually increased over the last decades. The mechanical properties of SFRC are well described based on the theories of fracture mechanics. However, knowledge on other material properties......, including the electrical resistivity, is sparse. Among others, the electrical resistivity of concrete has an effect on the corrosion process of possible embedded bar reinforcement and transfer of stray current. The present paper provides experimental results concerning the influence of the fibre volume...

  18. Electrical resistivity of thin metal films and multilayers

    International Nuclear Information System (INIS)

    Fenn, M.

    1999-01-01

    The electrical resistivity and temperature coefficient of resistivity (TCR) of thin films and multilayers of Cu, Nb and Zr have been measured over a wide range of layer thicknesses. The structure of the films has been characterised using transmission electron microscopy (TEM) and x-ray reflectivity. The experimental results have been compared with the semiclassical theory due to Dimmich. The values of the grain boundary reflectivity, R, in the single films has been found to be approximately 0.35 for Cu in agreement with the literature. The value of R for Nb and Zr has been found to vary with grain size, although it is approximately 0.55 for Nb and 0.925 for Zr over a wide range of grain sizes, and this is believed to be presented for the first time. The value of the interfacial specularity parameter, p, is not found to have a significant effect compared to R in the single films. Dimmich's theoretical expression for the TCR does not match experiment, but by adapting the resistivity expression of the theory to different temperatures a satisfactory fit has been obtained. It has been concluded that the assumption of the free electron model in the presence of grain boundary scattering is in error. The adapted theory predicts negative TCR in sufficiently thin films with experimentally plausible values of the input parameters, and this is believed to be demonstrated for the first time. The experimental resistivity of the multilayers was much lower than expected from the resistivity of the single films. A theoretical fit to the experimental resistivity and TCR of the multilayers was obtained by adjusting the parameter values obtained from single films, and the value of p was found to be significant. This procedure leads to a contradiction in the value of R for Nb. With a view to extending the above work to magnetic multilayers, an AC susceptometer has been designed, built and tested. The results indicate that this instrument would be suitable for work on magnetic

  19. Optimal Electrode Selection for Electrical Resistance Tomography in Carbon Fiber Reinforced Polymer Composites

    Science.gov (United States)

    Escalona Galvis, Luis Waldo; Diaz-Montiel, Paulina; Venkataraman, Satchi

    2017-01-01

    Electrical Resistance Tomography (ERT) offers a non-destructive evaluation (NDE) technique that takes advantage of the inherent electrical properties in carbon fiber reinforced polymer (CFRP) composites for internal damage characterization. This paper investigates a method of optimum selection of sensing configurations for delamination detection in thick cross-ply laminates using ERT. Reduction in the number of sensing locations and measurements is necessary to minimize hardware and computational effort. The present work explores the use of an effective independence (EI) measure originally proposed for sensor location optimization in experimental vibration modal analysis. The EI measure is used for selecting the minimum set of resistance measurements among all possible combinations resulting from selecting sensing electrode pairs. Singular Value Decomposition (SVD) is applied to obtain a spectral representation of the resistance measurements in the laminate for subsequent EI based reduction to take place. The electrical potential field in a CFRP laminate is calculated using finite element analysis (FEA) applied on models for two different laminate layouts considering a set of specified delamination sizes and locations with two different sensing arrangements. The effectiveness of the EI measure in eliminating redundant electrode pairs is demonstrated by performing inverse identification of damage using the full set and the reduced set of resistance measurements. This investigation shows that the EI measure is effective for optimally selecting the electrode pairs needed for resistance measurements in ERT based damage detection. PMID:28772485

  20. Microscopic histological characteristics of soft tissue sarcomas: analysis of tissue features and electrical resistance.

    Science.gov (United States)

    Tosi, A L; Campana, L G; Dughiero, F; Forzan, M; Rastrelli, M; Sieni, E; Rossi, C R

    2017-07-01

    Tissue electrical conductivity is correlated with tissue characteristics. In this work, some soft tissue sarcomas (STS) excised from patients have been evaluated in terms of histological characteristics (cell size and density) and electrical resistance. The electrical resistance has been measured using the ex vivo study on soft tissue tumors electrical characteristics (ESTTE) protocol proposed by the authors in order to study electrical resistance of surgical samples excised by patients in a fixed measurement setup. The measurement setup includes a voltage pulse generator (700 V, 100 µs long at 5 kHz, period 200 µs) and an electrode with 7 needles, 20 mm-long, with the same distance arranged in a fixed hexagonal geometry. In the ESTTE protocol, the same voltage pulse sequence is applied to each different tumor mass and the corresponding resistance has been evaluated from voltage and current recorded by the equipment. For each tumor mass, a histological sample of the volume treated by means of voltage pulses has been taken for histological analysis. Each mass has been studied in order to identify the sarcoma type. For each histological sample, an image at 20× or 40× of magnification was acquired. In this work, the electrical resistance measured for each tumor has been correlated with tissue characteristics like the type, size and density of cells. This work presents a preliminary study to explore possible correlations between tissue characteristics and electrical resistance of STS. These results can be helpful to adjust the pulse voltage intensity in order to improve the electrochemotherapy efficacy on some histotype of STS.

  1. Prophylactic and thermovision measurements of electric machines and equipment

    International Nuclear Information System (INIS)

    Jedlicka, R.; Brestovansky, L.

    1996-01-01

    High-voltage measurements of generators, unit and service transformers and some significant motor drives used at a nuclear power plant are described in this paper. Thermovision measurements of electric machines and distribution systems are dealt with in the second part of the paper. Power electric equipment represent one of the most significant components of a nuclear power plant. Turbine mechanical energy is converted into the electrical energy within these equipment. Power generated by generators is transformed by transformers so that it can achieve appropriate parameters for both the transmission over the distribution system and the power plant service power supply. The service power supply switchboards and cables provide supply to motors and other consumers necessary for the nuclear power plant technological process. The whole complex of equipment has to be maintained in good technical conditions. It is necessary to make thermovision and prophylactic measurements to identify and verify the electric equipment technical condition. The mentioned measurements warn the operation staff in advance against both gradual deterioration of power connection contact resistances, i.e. power connections overheating, and the machine insulation systems condition deterioration. The operation staff try to prevent the electric equipment operation accidents by early removing the detected failures, thus, improving the nuclear safety. In order to provide the above-mentioned activities a special prophylactic measurement group was established at the NPP Bohunice in 1983. The group specialists make following types of measurements. 1. Prophylactic measurements of electric machines. Prophylactics of 220 MW generators and 6 MW service power generators; Prophylactics of both unit and service transformers and VHV bushings; Prophylactics of major 6 kV motor drives. 2. Thermovision measurements of current connections. Measurements enumarated in paragraph 1 are made on disconnected electric

  2. Applications of electrical resistance tomography to subsurface environmental restoration

    Energy Technology Data Exchange (ETDEWEB)

    Ramirez, A.L. [Lawrence Livermore National Lab., CA (United States); Daily, W.D.

    1994-11-15

    We are developing a new imaging technique, Electrical Resistance Tomography (ERT), to map subsurface liquids as flow occurs during natural or clean-up processes and to map geologic structure. Natural processes (such as surface water infiltrating the vadose zone) and man-induced processes (such as tank leaks and clean-up processes such as steam injection), can create changes in a soil`s electrical properties that are readily measured. We have conducted laboratory and a variety of field experiments to investigate the capabilities and limitations of ERT for imaging underground structures and processes. In the last four years we have used ERT to successfully monitor several field processes including: a subsurface steam injection process (for VOC removal), an air injection process (below the water table) for VOC removal, water infiltration through the vadose zone, radio-frequency heating, ohmic heating, and tank and pond leaks. The information derived from ERT can be used by remediation projects to: detect and locate leaks, determine the effectiveness of clean-up processes, select appropriate clean-up alternatives, and to verify the installation and performance of subsurface barriers.

  3. Electrical Resistance Tomography to monitor vadose water movement

    International Nuclear Information System (INIS)

    Ramirez, A.; Daily, W.; LaBrecque, D.

    1991-01-01

    We report results of one test in which Electrical Resistance Tomography (ERT) was used to map the changes in electrical resistivity in the vadose zone as a function of time while water infiltration occurred. The ERT images were used to infer shape and movement of the infiltration plume in the unsaturated soil. We supplied a continuous water source at a point about 10 feet below the surface (at the end of a shallow screened hole) for only a short time--2.5 hours. This pulsed source introduced a open-quote slug close-quote of water whose infiltration was followed to about 60 foot depth during a 23 hour period. The ERT images show resistivity decreases as the water content of the vadose zone increased while water was added to the soil; the resistivity of the soil later increased after the supply of water was cut-off and the induced soil moisture began to subside

  4. Application of column tests and electrical resistivity methods for leachate transport monitoring

    Directory of Open Access Journals (Sweden)

    Wychowaniak Dorota

    2015-09-01

    Full Text Available Development of the human civilization leads to the pollution of environment. One of the contamination which are a real threat to soil and groundwater are leachates from landfills. In this paper the solute transport through soil was considered. For this purpose, the laboratory column tests of chlorides tracer and leachates transport on two soil samples have been carried out. Furthermore, the electrical resistivity method was applied as auxiliary tool to follow the movements of solute through the soil column what allowed to compare between the results obtained with column test method and electrical resistivity measurements. Breakthrough curves obtained by conductivity and resistivity methods represents similar trends which leads to the conclusion about the suitability of electrical resistivity methods for contamination transport monitoring in soil-water systems.

  5. Electrical resistivity of Al-Cu liquid binary alloy

    Science.gov (United States)

    Thakor, P. P.; Patel, J. J.; Sonvane, Y. A.; Jani, A. R.

    2013-06-01

    Present paper deals with the electrical resistivity (ρ) of liquid Al-Cu binary alloy. To describe electron-ion interaction we have used our parameter free model potential along with Faber-Ziman formulation combined with Ashcroft-Langreth (AL) partial structure factor. To see the influence of exchange and correlation effect, Hartree, Taylor and Sarkar et al local field correlation functions are used. From present results, it is seen that good agreements between present results and experimental data have been achieved. Lastly we conclude that our model potential successfully produces the data of electrical resistivity (ρ) of liquid Al-Cu binary alloy.

  6. Oxidation effects on the electric resistance of In and Al in thin layers

    International Nuclear Information System (INIS)

    Moncada, G.; Araya, J.; Clark, N.

    1981-01-01

    Measurements of electric resistance (R) in function of the time in evaporated samples of thin layers of In and Al trivalent elements in both vacuum and atmospheric pressure are reported. Measurements in samples at ambient and cooled with nitrogen temperatures taken place. The changes observed in R is attributed partly to changes in the sample surface produced by the oxidation. (L.C.) [pt

  7. Radiation resistance of insulating materials for electric wires

    International Nuclear Information System (INIS)

    Kanemitsuya, Kazuhiko; Okuda, Tomoaki; Tachibana, Tadao; Yagi, Toshiaki; Seguchi, Tadao.

    1990-01-01

    In no halogen incombustible materials, smoke and poisonous gas generation at the time of burning is small, and corrosive gas rarely arises. Since no halogen electric wires and cables which use these material maintain safety for people and equipment in the case of fires, those are used for ships, tunnels, subways and so on. Also in nuclear power stations, the demand for no halogen cables becomes high although the condition of adoption is difficult. In this study, for the purpose of developing the no halogen cables for nuclear power stations, the basic data on the radiation resistance of no halogen incombustible materials were collected, and by using chemical analysis method, the radiation deterioration behavior was examined. The samples were those with base polymers of VLDPE, ULDPE, EEA, EMA and EVA. Gamma ray irradiation, tensile test, chemi-luminescence measurement, and the determination of gel fraction and swelling rate were carried out. The results are reported, In no halogen materials, when ethylene system copolymer is used as the base polymer instead of PE, the composition with good radiation resistance can be obtained, and by combining amine oxidation inhibitor, it is further improved. (K.I.)

  8. Resistivity of flame plasma in an electric field

    International Nuclear Information System (INIS)

    Ikuta, Kazunari.

    1989-01-01

    A generalized Ohm's law is obtained for a flame plasma in an electric field for the study of arc resistivity in an electromagnetic launcher (EML). The effective resistivity of flame plasma is reduced by the source, which suggests the injection of premixed combustible fuel into the arc plasma in EML in order to reduce the electron energy of the arc. The reduction of electron energy in the arc is desirable to minimize the damage of electrodes in EML. (author)

  9. Evaluation of atmospheric corrosion on electroplated zinc and zinc nickel coatings by Electrical Resistance (ER) Monitoring

    DEFF Research Database (Denmark)

    Møller, Per

    2013-01-01

    ER (Electrical Resistance) probes provide a measurement of metal loss, measured at any time when a metal is exposed to the real environment. The precise electrical resistance monitoring system can evaluate the corrosion to the level of nanometers, if the conductivity is compensated for temperature...... and magnetic fields. With this technique very important information about the durability of a new conversion coatings for aluminum, zinc and zinc alloys exposed to unknown atmospheric conditions can be gathered. This is expected to have a major impact on a number of industrial segments, such as test cars...

  10. Determining the Resistivity of Resistive Sheets Using Transmission Measurements

    National Research Council Canada - National Science Library

    Hyde, IV, Milo W

    2006-01-01

    In September 2005, radar cross section (RCS) measurements were made of resistive sheets, or R-cards, wrapped around a polystyrene foam cylinder to compare with a newly developed theoretical RCS prediction technique...

  11. Electrical resistivity of thin metal films

    CERN Document Server

    Wissmann, Peter

    2007-01-01

    The aim of the book is to give an actual survey on the resistivity of thin metal and semiconductor films interacting with gases. We discuss the influence of the substrate material and the annealing treatment of the films, presenting our experimental data as well as theoretical models to calculate the scattering cross section of the conduction electrons in the frame-work of the scattering hypothesis. Main emphasis is laid on the comparison of gold and silver films which exhibit nearly the same lattice structure but differ in their chemical activity. In conclusion, the most important quantity for the interpretation is the surface charging z while the correlation with the optical data or the frustrated IR vibrations seems the show a more material-specific character. Z can be calculated on the basis of the density functional formalism or the self-consistent field approximation using Mulliken’s population analysis.

  12. Electrical resistivity testing for as-built concrete performance assessment of chloride penetration resistance

    NARCIS (Netherlands)

    Polder, R.B.; Peelen, W.H.A.

    2014-01-01

    The electrical resistivity of concrete can provide information about its transport properties, which is relevant for durability performance. For example, resistivity is inversely proportional to chloride diffusion, at least within similar concrete compositions. A methodology is proposed for on-site

  13. Surface electric resistance of YBa2Cu3O7-δ ceramics and its dependence on magnetic field

    International Nuclear Information System (INIS)

    Gorochev, O.A.; Graboj, I.Eh.; Kaul', A.R.; Mitrofanov, V.P.

    1989-01-01

    Method of dielectric resonator in the 4.2-300 K temperature range is used to measure surface electric resistance of YBa 2 Cu 3 O 7-δ ceramics samples produced by different technologies. The temperature dependence of surface resistance near transition temperature is calculated. At 77.3 K dependence of electric resistance on external magnetic field at H≤200Oe is determined. Calculated dependence is verified in experiment

  14. Mapping on Slope Seepage Problem using Electrical Resistivity Imaging (ERI)

    Science.gov (United States)

    Hazreek, Z. A. M.; Nizam, Z. M.; Aziman, M.; Dan, M. F. Md; Shaylinda, M. Z. N.; Faizal, T. B. M.; Aishah, M. A. N.; Ambak, K.; Rosli, S.; Rais, Y.; Ashraf, M. I. M.; Alel, M. N. A.

    2018-04-01

    The stability of slope may influenced by several factors such as its geomaterial properties, geometry and environmental factors. Problematic slope due to seepage phenomenon will influenced the slope strength thus promoting to its failure. In the past, slope seepage mapping suffer from several limitation due to cost, time and data coverage. Conventional engineering tools to detect or mapped the seepage on slope experienced those problems involving large and high elevation of slope design. As a result, this study introduced geophysical tools for slope seepage mapping based on electrical resistivity method. Two spread lines of electrical resistivity imaging were performed on the slope crest using ABEM SAS 4000 equipment. Data acquisition configuration was based on long and short arrangement, schlumberger array and 2.5 m of equal electrode spacing interval. Raw data obtained from data acquisition was analyzed using RES2DINV software. Both of the resistivity results show that the slope studied consists of three different anomalies representing top soil (200 – 1000 Ωm), perched water (10 – 100 Ωm) and hard/dry layer (> 200 Ωm). It was found that seepage problem on slope studied was derived from perched water zones with electrical resistivity value of 10 – 100 Ωm. Perched water zone has been detected at 6 m depth from the ground level with varying thickness at 5 m and over. Resistivity results have shown some good similarity output with reference to borehole data, geological map and site observation thus verified the resistivity results interpretation. Hence, this study has shown that the electrical resistivity imaging was applicable in slope seepage mapping which consider efficient in term of cost, time, data coverage and sustainability.

  15. [Antibiotic resistance: measures urgently needed].

    NARCIS (Netherlands)

    Kluytmans, J.; Vandenbroucke-Grauls, C.M.; Meer, J.W.M. van der

    2010-01-01

    Antimicrobial resistance is increasing rapidly and there are hardly any new antimicrobial agents to be expected in the coming years. The number of patients affected by extended spectrum beta-lactamase producing organisms (ESBLs) is rising and there are strong indications that this is caused in part

  16. Evaluation on electrical resistivity of silicon materials after electron ...

    Indian Academy of Sciences (India)

    Home; Journals; Bulletin of Materials Science; Volume 38; Issue 5. Evaluation on ... This research deals with the study of electron beam melting (EBM) methodology utilized in melting silicon material and subsequently discusses on the effect of oxygen level on electrical resistivity change after EBM process. The oxygen ...

  17. Electron–electron interactions and the electrical resistivity of lithium

    Indian Academy of Sciences (India)

    The electron–electron interactions in lithium metal have been examined keeping in view the recent developments. The contribution of the electron–electron Umklapp scattering processes in the electrical resistivity of lithium at low temperatures has been evaluated using a simplified spherical Fermi surface model with ...

  18. Measuring Electrical Current: The Roads Not Taken

    Science.gov (United States)

    Greenslade, Thomas B., Jr.

    2011-01-01

    Recently I wrote about the standard Weston meter movement, that is at the heart of all modern analogue current measurements. Now I will discuss other techniques used to measure electric current that, despite being based on valid physical principles, are largely lost in technological history.

  19. Relationship between the electric resistivity and the rain fall in discontinuity zone of rock slope by the continuous measurement; Renzoku tokei ni yoru ganban shamen no furenzokutaibu ni okeru mikake hiteiko henka to kou tono kankei ni tsuite

    Energy Technology Data Exchange (ETDEWEB)

    Kusumi, H; Nishida, K [Kansai University, Osaka (Japan). Faculty of Engineering; Nakamura, M [Newjec Inc., Osaka (Japan)

    1996-10-01

    The relationship between change in resistivity and rainfall was studied by continuously measuring resistivities of fracture zone and stratum boundary along the measuring line of 95m long from the top to bottom of rock slope. The measurement field was located on a hill of 150-200m high at the northern part of Arima-Takatsuki tectonic line. Electrodes of 30m in maximum measuring depth were arranged at 289 points by dipole-dipole method. Resistivity was continuously measured at time intervals of 6 hours. Apparent resistivity was hardly affected by rainfall at points with less infiltration of stormwater from the ground surface, while it decreased by rainfall at points on fracture zone, stratum boundary or bleeding channel. The change rate of apparent resistivity could be approximated with the exponential function of rainfall. In such case, the apparent resistivity under most dried condition at the concerned point should be used as reference maximum apparent resistivity. The change rate of apparent resistivity due to rainfall in fracture zone reflects infiltration of stormwater, suggesting to be useful for disaster prevention of slopes. 5 refs., 6 figs.

  20. On the computation of electrical resistance of hydrodynamic journal bearing

    Directory of Open Access Journals (Sweden)

    Eleonora Pop

    2014-12-01

    Full Text Available The paper approaches the mathematical model of electrical resistance of hydrodynamic journal bearing under different parameters of operation so as to predict bearing performance and safe load carrying capacity. The currents circulating in the journal bearing of electrical machine causes reducing of lifespan by appearance of pitting on their surface and the degradation of the lubricant. In a hydrodynamic journal bearing, the zone of minimum film thickness, load-carrying oil film varies along the circumference of a bearing through its length. This has been found to form a capacitor of varying capacitance between the journal and the bearings dependent on permittivity of the lubricant used, the bearing length, the eccentricity ratio and the clearance ratio. Besides this, load-carrying on oil film offers resistance that depends on operating parameters and resistivity of the lubricant.

  1. On electrical resistivity of AISI D2 steel during various stages of cryogenic treatment

    Science.gov (United States)

    Lomte, Sachin Vijay; Gogte, Chandrashekhar Laxman; Peshwe, Dilip

    2012-06-01

    The effect of dislocation densities and residual stresses is well known in tool steels. Measurement of electrical resistivity in order to monitor dislocation densities or residual stresses has seldom been used in investigating the effect of cryogenic treatment on tool steels. Monitoring residual stresses during cryogenic treatment becomes important as it is directly related to changes due to cryogenic treatment of tool steels. For high carbon high chromium (HCHC- AISI D2) steels, not only wear resistance but dimensional stability is an important issue as the steels are extensively used in dies, precision measuring instruments. This work comprises of study of measurement of electrical resistivity of AISI D2 steel at various stages of cryogenic treatment. Use of these measurements in order to assess the dimensional stability of these steels is discussed in this paper.

  2. Multi-Electrode Resistivity Probe for Investigation of Local Temperature Inside Metal Shell Battery Cells via Resistivity: Experiments and Evaluation of Electrical Resistance Tomography

    Directory of Open Access Journals (Sweden)

    Xiaobin Hong

    2015-01-01

    Full Text Available Direct Current (DC electrical resistivity is a material property that is sensitive to temperature changes. In this paper, the relationship between resistivity and local temperature inside steel shell battery cells (two commercial 10 Ah and 4.5 Ah lithium-ion cells is innovatively studied by Electrical Resistance Tomography (ERT. The Schlumberger configuration in ERT is applied to divide the cell body into several blocks distributed in different levels, where the apparent resistivities are measured by multi-electrode surface probes. The investigated temperature ranges from −20 to 80 °C. Experimental results have shown that the resistivities mainly depend on temperature changes in each block of the two cells used and the function of the resistivity and temperature can be fitted to the ERT-measurement results in the logistical-plot. Subsequently, the dependence of resistivity on the state of charge (SOC is investigated, and the SOC range of 70%–100% has a remarkable impact on the resistivity at low temperatures. The proposed approach under a thermal cool down regime is demonstrated to monitor the local transient temperature.

  3. electrical resistivity measurements of downscaled homogenous

    African Journals Online (AJOL)

    ES Obe

    interest for validating the predictive value of network models based on micro-CT imaging of rock fragments with ... oil fields and proper planning of enhanced oil recovery (EOR) ... phase transport properties obtained from few core samples may ...

  4. Specific features in the behavior of electrical resistivity of the pine biocarbon preform/copper composite

    Science.gov (United States)

    Burkov, A. T.; Orlova, T. S.; Smirnov, B. I.; Smirnov, I. A.; Misiorek, H.; Jezowski, A.

    2010-11-01

    The electrical resistivity ρ( T) of the novel type of composites prepared by infiltrating melted copper in vacuum in empty sap channels of white pine high-porosity biocarbon preforms has been measured in the temperature range 5-300 K. Biocarbon preforms have been prepared by pyrolysis of tree wood in an argon flow at two carbonization temperatures, 1000 and 2400°C. The electrical resistivity of the composites has been found to vary relatively weakly with temperature and to pass through a characteristic minimum near 40-50 K, which can be ascribed to iron and manganese impurities penetrating into copper from the carbon preform when liquid copper is infiltrated into it. It has been shown that the electrical resistivity ρ( T) of the composites is governed primarily by the specific microstructure of the preform, which is made up of parallel channels with an average diameter of about 50 μm interrupted by systems of thin capillaries. The small cross section of the copper-filled capillaries accounts for these regions providing the major contribution to the electrical resistivity of the composites. An increase in the wood carbonization temperature brings about a noticeable increase in the effective capillary cross section and a decrease in the electrical resistivity ρ( T) of the composite.

  5. Prophylactic and thermovision measurements of electric machines and equipment

    Energy Technology Data Exchange (ETDEWEB)

    Jedlicka, R; Brestovansky, L [Atomova Elektraren Bohunice, Jaslovske Bohunice (Slovakia)

    1997-12-31

    High-voltage measurements of generators, unit and service transformers and some significant motor drives used at a nuclear power plant are described in this paper. Thermovision measurements of electric machines and distribution systems are dealt with in the second part of the paper. Power electric equipment represent one of the most significant components of a nuclear power plant. Turbine mechanical energy is converted into the electrical energy within these equipment. Power generated by generators is transformed by transformers so that it can achieve appropriate parameters for both the transmission over the distribution system and the power plant service power supply. The service power supply switchboards and cables provide supply to motors and other consumers necessary for the nuclear power plant technological process. The whole complex of equipment has to be maintained in good technical conditions. It is necessary to make thermovision and prophylactic measurements to identify and verify the electric equipment technical condition. The mentioned measurements warn the operation staff in advance against both gradual deterioration of power connection contact resistances, i.e. power connections overheating, and the machine insulation systems condition deterioration. The operation staff try to prevent the electric equipment operation accidents by early removing the detected failures, thus, improving the nuclear safety. In order to provide the above-mentioned activities a special prophylactic measurement group was established at the NPP Bohunice in 1983. The group specialists make following types of measurements. 1. Prophylactic measurements of electric machines. Prophylactics of 220 MW generators and 6 MW service power generators; Prophylactics of both unit and service transformers and VHV bushings; Prophylactics of major 6 kV motor drives. 2. Thermovision measurements of current connections. (Abstract Truncated)

  6. Electric Field Quantitative Measurement System and Method

    Science.gov (United States)

    Generazio, Edward R. (Inventor)

    2016-01-01

    A method and system are provided for making a quantitative measurement of an electric field. A plurality of antennas separated from one another by known distances are arrayed in a region that extends in at least one dimension. A voltage difference between at least one selected pair of antennas is measured. Each voltage difference is divided by the known distance associated with the selected pair of antennas corresponding thereto to generate a resulting quantity. The plurality of resulting quantities defined over the region quantitatively describe an electric field therein.

  7. Electrical resistance behavior with gamma radiation dose in bulk carbon nanostrutured samples

    International Nuclear Information System (INIS)

    Lage, J.; Leyva, A.; Pinnera, I.; Desdin, L. F.; Abreu, Y.; Cruz, C. M.; Leyva, D.; Toledo, C.

    2013-01-01

    The aim of this paper is to study the effects of 60 Co gamma radiation on the electrical resistance and V-I characteristic of bulk carbon nano structured samples obtained by electric arc discharge in water method. Images of pristine samples obtained with scanning electron, and the results in graphical form of the electrical characterization of irradiated samples are presented in the text. It was observed that the electrical resistance vs. dose behavior shows an initial increment reaching the maximum at approximately 135 kGy, followed by a drop of the resistance values. These behaviors are associated with the progressive generation of radiation induced defects in the sample, whose number increases to reach saturation at 135 kGy. From this dose, defects could lead to cross-links between different nano structures present in the sample conducting to a gradually drop in electrical resistance. The measured V-I curves show that, increasing exposure to the 60 Co gamma radiation, the electrical properties of the studied samples transit from a semiconductor towards a predominantly metallic behavior. These results were compared with those obtained for a sample of graphite powder irradiated under the same conditions. (Author)

  8. Pressure effect on electrical resistivity of Y1-xGdxCo2

    International Nuclear Information System (INIS)

    Nakama, T.; Takaesu, Y.; Yagasaki, K.; Sakai, E.; Kurita, N.; Hedo, M.; Uwatoko, Y.; Burkov, A.T.

    2006-01-01

    Electrical resistivity of Y 1-x Gd x Co 2 alloy system has been measured at temperatures from 2 to 300K in magnetic field up to 15T and under pressure up to 10GPa. The compounds with the composition near to phase boundary between paramagnetic and ferromagnetic ground state (x c ∼0.12) show strong enhancement of electrical resistivity at low temperatures. Large positive magnetoresistance was observed in ferromagnetic alloys in composition range 0.15 1-x Gd x Co 2 at low temperatures is in agreement with the variation of magnetoresistance with the composition

  9. Electrical resistivity of U/sub 1/minus/x/M/sub x/Be13 under pressure

    International Nuclear Information System (INIS)

    Borges, H.A.; Thompson, J.D.; Aronson, M.C.; Fisk, Z.; Smith, J.L.

    1988-01-01

    Measurements of the electrical resistivity of U/sub 1/minus/x/ Th/sub x/ Be 13 compounds as a function of pressure provide a possible explanation for the unusual behavior of these materials. 10 refs., 2 figs

  10. Non-invasive determination of absolute lung resistivity in adults using electrical impedance tomography

    International Nuclear Information System (INIS)

    Zhang, Jie; Patterson, Robert

    2010-01-01

    Lung resistivity is a physiological parameter that describes the electrical characteristics of the lungs. Lung composition changes due to changes in the lung tissues, fluid and air volume. Various diseases that can cause a change in lung composition may be monitored by measuring lung resistivity. Currently, there is no accepted non-invasive method to measure lung resistivity. In this study, we presented a method and framework to non-invasively determine lung resistivity using electrical impedance tomography (EIT). By comparing actual measurements from subjects with data from a 3D human thorax model, an EIT image can be reconstructed to show a resistivity difference between the model and the subject. By adjusting the lung resistivity in the model, the resistivity difference in the lung regions can be reduced to near zero. This resistivity value then is the estimation of the lung resistivity of the subject. Using the proposed method, the lung resistivities of four normal adult males (43 ± 13 years, 78 ± 10 kg) in the supine position at air volumes starting at functional residual capacity (FRC—end expiration) and increasing in 0.5 l steps to 1.5 l were studied. The averaged lung resistivity changes 12.59%, from 1406 Ω cm to 1583 Ω cm, following the inspiration of 1.5 l air from FRC. The coefficients of variation (CV) of precision for the four subjects are less than 10%. The experiment was repeated five times at each air volume on a subject to test the reproducibility. The CVs are less than 3%. The results show that it is feasible to determine absolute lung resistivity using an EIT-based method

  11. Non-invasive determination of absolute lung resistivity in adults using electrical impedance tomography.

    Science.gov (United States)

    Zhang, Jie; Patterson, Robert

    2010-08-01

    Lung resistivity is a physiological parameter that describes the electrical characteristics of the lungs. Lung composition changes due to changes in the lung tissues, fluid and air volume. Various diseases that can cause a change in lung composition may be monitored by measuring lung resistivity. Currently, there is no accepted non-invasive method to measure lung resistivity. In this study, we presented a method and framework to non-invasively determine lung resistivity using electrical impedance tomography (EIT). By comparing actual measurements from subjects with data from a 3D human thorax model, an EIT image can be reconstructed to show a resistivity difference between the model and the subject. By adjusting the lung resistivity in the model, the resistivity difference in the lung regions can be reduced to near zero. This resistivity value then is the estimation of the lung resistivity of the subject. Using the proposed method, the lung resistivities of four normal adult males (43 +/- 13 years, 78 +/- 10 kg) in the supine position at air volumes starting at functional residual capacity (FRC--end expiration) and increasing in 0.5 l steps to 1.5 l were studied. The averaged lung resistivity changes 12.59%, from 1406 Omega cm to 1583 Omega cm, following the inspiration of 1.5 l air from FRC. The coefficients of variation (CV) of precision for the four subjects are less than 10%. The experiment was repeated five times at each air volume on a subject to test the reproducibility. The CVs are less than 3%. The results show that it is feasible to determine absolute lung resistivity using an EIT-based method.

  12. Image reconstruction with an adaptive threshold technique in electrical resistance tomography

    International Nuclear Information System (INIS)

    Kim, Bong Seok; Khambampati, Anil Kumar; Kim, Sin; Kim, Kyung Youn

    2011-01-01

    In electrical resistance tomography, electrical currents are injected through the electrodes placed on the surface of a domain and the corresponding voltages are measured. Based on these currents and voltage data, the cross-sectional resistivity distribution is reconstructed. Electrical resistance tomography shows high temporal resolution for monitoring fast transient processes, but it still remains a challenging problem to improve the spatial resolution of the reconstructed images. In this paper, a novel image reconstruction technique is proposed to improve the spatial resolution by employing an adaptive threshold method to the iterative Gauss–Newton method. Numerical simulations and phantom experiments have been performed to illustrate the superior performance of the proposed scheme in the sense of spatial resolution

  13. Study of critical dependence of stable phases in Nitinol on heat treatment using electrical resistivity probe

    International Nuclear Information System (INIS)

    Uchil, J.; Mohanchandra, K.P.; Kumara, K.G.; Mahesh, K.K.

    1998-01-01

    Phase transformations in 40% cold-worked Nitinol as a function of heat treatment have been studied using electrical resistivity variation with temperature. The stabilisation of austenitic, rhombohedral and martensitic phases is shown to critically depend on the temperatures of heat treatment by the analysis of temperature dependence of electrical resistivity in heating and cooling parts of the cycle. Characteristic values of electrical resistivity of the stable phases are determined. The R-phase has been found to form continuously with increasing heat-treatment temperature starting from room temperature and to suddenly disappear beyond heat-treatment at 683 K. The observed presence or absence of R-phase is confirmed by heat capacity measurements as a function of temperature. (orig.)

  14. Electrical resistance determination of actual contact area of cold welded metal joints

    Science.gov (United States)

    Hordon, M. J.

    1970-01-01

    Method measures the area of the bonded zone of a compression weld by observing the electrical resistance of the weld zone while the load changes from full compression until the joint ruptures under tension. The ratio of bonding force to maximum tensile load varies considerably.

  15. Direct observations of surface water-groundwater interaction using electrical resistivity tomography

    NARCIS (Netherlands)

    Noell, Ursula; Wießner, Claudia; Ganz, Christina; Westhoff, Martijn

    2011-01-01

    Electrical resistivity tomography is a helpful tool to observe the infiltration process in and through the soil. Array 3-D measurements and 3-D inversion schemes are required for reliable interpretation of heterogeneous subsurface structures. Smoothing of the inversion can be minimized by using

  16. Scenario Evaluator for Electrical Resistivity survey pre-modeling tool

    Science.gov (United States)

    Terry, Neil; Day-Lewis, Frederick D.; Robinson, Judith L.; Slater, Lee D.; Halford, Keith J.; Binley, Andrew; Lane, John W.; Werkema, Dale D.

    2017-01-01

    Geophysical tools have much to offer users in environmental, water resource, and geotechnical fields; however, techniques such as electrical resistivity imaging (ERI) are often oversold and/or overinterpreted due to a lack of understanding of the limitations of the techniques, such as the appropriate depth intervals or resolution of the methods. The relationship between ERI data and resistivity is nonlinear; therefore, these limitations depend on site conditions and survey design and are best assessed through forward and inverse modeling exercises prior to field investigations. In this approach, proposed field surveys are first numerically simulated given the expected electrical properties of the site, and the resulting hypothetical data are then analyzed using inverse models. Performing ERI forward/inverse modeling, however, requires substantial expertise and can take many hours to implement. We present a new spreadsheet-based tool, the Scenario Evaluator for Electrical Resistivity (SEER), which features a graphical user interface that allows users to manipulate a resistivity model and instantly view how that model would likely be interpreted by an ERI survey. The SEER tool is intended for use by those who wish to determine the value of including ERI to achieve project goals, and is designed to have broad utility in industry, teaching, and research.

  17. Improved Geologic Interpretation of Non-invasive Electrical Resistivity Imaging from In-situ Samples

    Science.gov (United States)

    Mucelli, A.; Aborn, L.; Jacob, R.; Malusis, M.; Evans, J.

    2016-12-01

    Non-invasive geophysical techniques are useful in characterizing the subsurface geology without disturbing the environment, however, the ability to interpret the subsurface is enhanced by invasive work. Since geologic materials have electrical resistivity values it allows for a geologic interpretation to be made based on variations of electrical resistivity measured by electrical resistivity imaging (ERI). This study focuses on the pre-characterization of the geologic subsurface from ERI collected adjacent to the Montandon Marsh, a wetland located near Lewisburg, PA within the West Branch of the Susquehanna River watershed. The previous invasive data, boreholes, indicate that the subsurface consists of limestone and shale bedrock overlain with sand and gravel deposits from glacial outwash and aeolian processes. The objective is to improve our understanding of the subsurface at this long-term hydrologic research site by using excavation results, specifically observed variations in geologic materials and electrical resistivity laboratory testing of subsurface samples. The pre-excavation ERI indicated that the shallow-most geologic material had a resistivity value of 100-500 ohm-m. In comparison, the laboratory testing indicated the shallow-most material had the same range of electrical resistivity values depending on saturation levels. The ERI also showed that there was an electrically conductive material, 7 to 70 ohm-m, that was interpreted to be clay and agreed with borehole data, however, the excavation revealed that at this depth range the geologic material varied from stratified clay to clay with cobbles to weathered residual clay. Excavation revealed that the subtle variations in the electrical conductive material corresponded well with the variations in the geologic material. We will use these results to reinterpret previously collected ERI data from the entire long-term research site.

  18. Coulomb's Electrical Measurements. Experiment No. 14.

    Science.gov (United States)

    Devons, Samuel

    Presented is information related to the life and work of Charles Coulomb as well as detailed notes of his measurements of the distribution of electricity on conductors. The two methods that he used (the large torsion balance, and the timing of "force" oscillations) are described. (SA)

  19. Research on Nonlinear Feature of Electrical Resistance of Acupuncture Points

    Directory of Open Access Journals (Sweden)

    Jianzi Wei

    2012-01-01

    Full Text Available A highly sensitive volt-ampere characteristics detecting system was applied to measure the volt-ampere curves of nine acupuncture points, LU9, HT7, LI4, PC6, ST36, SP6, KI3, LR3, and SP3, and corresponding nonacupuncture points bilaterally from 42 healthy volunteers. Electric currents intensity was increased from 0 μA to 20 μA and then returned to 0 μA again. The results showed that the volt-ampere curves of acupuncture points had nonlinear property and magnetic hysteresis-like feature. On all acupuncture point spots, the volt-ampere areas of the increasing phase were significantly larger than that of the decreasing phase (P<0.01. The volt-ampere areas of ten acupuncture point spots were significantly smaller than those of the corresponding nonacupuncture point spots when intensity was increase (P<0.05~P<0.001. And when intensity was decrease, eleven acupuncture point spots showed the same property as above (P<0.05~P<0.001, while two acupuncture point spots showed opposite phenomenon in which the areas of two acupuncture point spots were larger than those of the corresponding nonacupuncture point spots (P<0.05~P<0.01. These results show that the phenomenon of low skin resistance does not exist to all acupuncture points.

  20. A TECHNIQUE OF MEASURING OF RESISTANCE OF A GROUNDING DEVICE

    Directory of Open Access Journals (Sweden)

    I.V. Nizhevskyi

    2016-06-01

    Full Text Available Introduction. Measurement of resistance of the grounding device (GD by means of a three-electrode system. This requires not only the right choice of installation locations of measuring electrodes, but also the determination of the point of zero potential. Implementation of these requirements quite time-consuming, and in some cases impossible. Aim. Develop a new technique for measuring the electrical resistance of the GD. Task. The method of measuring the resistance of the GD with the help of a three-electrode setup is necessary to exclude the determination of the point of zero potential. Method. Mathematical modeling and calculation engine. Results. A three-electrode system for measuring the resistance of grounding devices (GD for various purposes is considered. On the basis of Maxwell equations a theoretical substantiation of a new technique for measuring the resistance of any GD of any construction in random soil structure has been proposed. An equation system of the sixth order has been obtained, its solution makes it possible to measure its own mutual resistance in the three-electrode installation with sufficiently high accuracy. Peculiarities of drawing up a calculation scheme of substitution of a three-electrode installation with lumped parameters: self and mutual impedance. Use of the principle of reciprocity eliminates the need of finding a point of zero potential which is a rather difficult task. The technique allows to minimize the spacing of measuring electrodes outside the GD, which substantially reduces the length of wiring of the measurement circuit and increases the «signal-to-interference» ratio and also removes the restrictions on the development of the territory outside the GD being tested. Conclusion. The procedure allows to evaluate the self and mutual impedance grounding all the electrodes in a three-electrode measuring installation of the grounding resistance of the device without finding the point of zero potential.

  1. Calculation of skid resistance from texture measurements

    Directory of Open Access Journals (Sweden)

    Andreas Ueckermann

    2015-02-01

    Full Text Available There is a wide range of routine skid resistance measurement devices on the market. All of them are measuring the friction force between a rubber wheel and the wetted road surface. Common to all of them is that they are relatively complex and costly because generally a truck carrying a large water tank is needed to wet the surface with a defined water layer. Because of the limited amount of water they can carry they are limited in range. Besides that the measurement is depending on factors like water film thickness, temperature, measurement speed, rubber aging, rubber wear and even road evenness and curviness. All of these factors will affect the skid resistance and are difficult to control. We present a concept of contactless skid resistance measurement which is based on optical texture measurement and consists of two components: measurement of the pavement texture by means of an optical measuring system and calculation of the skid resistance based on the measured texture by means of a rubber friction model. The basic assumptions underlying the theoretical approach and the model itself based on the theory of Persson are presented. The concept is applied to a laboratory device called Wehner/Schulze (W/S machine to prove the theoretical approach. The results are very promising. A strong indication could be provided that skid resistance could be measured without contact in the future.

  2. Using electrical resistivity tomography to differentiate sapwood from heartwood: application to conifers.

    Science.gov (United States)

    Guyot, Adrien; Ostergaard, Kasper T; Lenkopane, Mothei; Fan, Junliang; Lockington, David A

    2013-02-01

    Estimating sapwood area is one of the main sources of error when upscaling point scale sap flow measurements to whole-tree water use. In this study, the potential use of electrical resistivity tomography (ERT) to determine the sapwood-heartwood (SW-HW) boundary is investigated for Pinus elliottii Engelm var. elliottii × Pinus caribaea Morelet var. hondurensis growing in a subtropical climate. Specifically, this study investigates: (i) how electrical resistivity is correlated to either wood moisture content, or electrolyte concentration, or both, and (ii) how the SW-HW boundary is defined in terms of electrical resistivity. Tree cross-sections at breast height are analysed using ERT before being felled and the cross-section surface sampled for analysis of major electrolyte concentrations, wood moisture content and density. Electrical resistivity tomography results show patterns with high resistivities occurring in the inner part of the cross-section, with much lower values towards the outside. The high-resistivity areas were generally smaller than the low-resistivity areas. A comparison between ERT and actual SW area measured after felling shows a slope of the linear regression close to unity (=0.96) with a large spread of values (R(2) = 0.56) mostly due to uncertainties in ERT. Electrolyte concentrations along sampled radial transects (cardinal directions) generally showed no trend from the centre of the tree to the bark. Wood moisture content and density show comparable trends that could explain the resistivity patterns. While this study indicates the potential for application of ERT for estimating SW area, it shows that there remains a need for refinement in locating the SW-HW boundary (e.g., by improvement of the inversion method, or perhaps electrode density) in order to increase the robustness of the method.

  3. An alternative methodology for the analysis of electrical resistivity data from a soil gas study

    Science.gov (United States)

    Johansson, Sara; Rosqvist, Hâkan; Svensson, Mats; Dahlin, Torleif; Leroux, Virginie

    2011-08-01

    The aim of this paper is to present an alternative method for the analysis of resistivity data. The methodology was developed during a study to evaluate if electrical resistivity can be used as a tool for analysing subsurface gas dynamics and gas emissions from landfills. The main assumption of this study was that variations in time of resistivity data correspond to variations in the relative amount of gas and water in the soil pores. Field measurements of electrical resistivity, static chamber gas flux and weather data were collected at a landfill in Helsingborg, Sweden. The resistivity survey arrangement consisted of nine lines each with 21 electrodes in an investigation area of 16 ×20 m. The ABEM Lund Imaging System provided vertical and horizontal resistivity profiles every second hour. The data were inverted in Res3Dinv using L1-norm-based optimization method with a standard least-squares formulation. Each horizontal soil layer was then represented as a linear interpolated raster model. Different areas underneath the gas flux measurement points were defined in the resistivity model of the uppermost soil layer, and the vertical extension of the zones could be followed at greater depths in deeper layer models. The average resistivity values of the defined areas were calculated and plotted on a time axis, to provide graphs of the variation in resistivity with time in a specific section of the ground. Residual variation of resistivity was calculated by subtracting the resistivity variations caused by the diurnal temperature variations from the measured resistivity data. The resulting residual resistivity graphs were compared with field data of soil moisture, precipitation, soil temperature and methane flux. The results of the study were qualitative, but promising indications of relationships between electrical resistivity and variations in the relative amount of gas and water in the soil pores were found. Even though more research and better data quality is

  4. Electrical resistivity discontinuity of iron along the melting curve

    Science.gov (United States)

    Wagle, Fabian; Steinle-Neumann, Gerd

    2018-04-01

    Discontinuous changes of electrical resistivity ρel (increase), density ϱ and isothermal compressibility βT (decrease) occur across the melting temperature of metals and can be directly related by Ziman's theory in the long-wavelength approximation. By evaluating experimental data at ambient pressure, we show that Ziman's approximation holds for iron and other simple and transition metals. Using a thermodynamic model to determine βT for γ-, ɛ- and liquid Fe and a previously published model for ρel of liquid Fe, we apply Ziman's approximation to calculate ρel of solid Fe along the melting curve. For pure Fe, we find the discontinuity in ρel to decrease with pressure and to be negligibly small at inner core boundary conditions. However, if we account for light element enrichment in the liquid outer core, the electrical resistivity decrease across the inner core boundary is predicted to be as large as 36 per cent.

  5. Resistivity measurements using a direct current induction method (1963)

    International Nuclear Information System (INIS)

    Delaplace, J.; Hillairet, J.

    1964-01-01

    The conventional methods for measuring electrical resistivities necessitate the fixing of electrical contacts on the sample either mechanically or by soldering. Furthermore it is also necessary to carry,out the measurements on low cross-section samples which are not always easy to obtain. Our direct-current induction method on the other hand requires no contacts and can easily be applied to samples of large cross-section. The sample is placed in a uniform magnetic field; at the moment when the current is cut, eddy currents appear in the sample which tend to oppose the disappearance of the field. The way in which the magnetic flux decreases in the sample makes it possible to determine the resistivity of the material. This method has been applied to samples having diameters of between 1 and 30 mm in the case of metals which are good conductors. It gives a value for the local resistivity and makes it possible to detect any variation along a sample. The measurements can be carried out at all temperature from a few degrees absolute to 500 deg. C. We have used the induction method to follow the purification of beryllium by zone-melting; it is in effect possible to estimate the purity of a material by resistivity measurements. We have measured the resistivity along each bar treated by the zone-melting technique and have thus, localised the purest section. High temperature measurements have been carried out on uranium carbide and on iron-aluminium alloys. This method constitutes an interesting means of investigation the resistivity of solid materials. Its accuracy and rapidity make it particularly adapted both to fundamental research and to production control. (authors) [fr

  6. Design of a pressurized water loop heated by electric resistances

    International Nuclear Information System (INIS)

    Ribeiro, S.V.G.

    1981-01-01

    A pressurized water loop design is presented. Its operating pressure is 420 psi and we seek to simulate qualitatively some thermo-hydraulic phenomena of PWR reactors. The primary circuit simulator consists basically of two elements: 1)the test section housing 16 electric resistences dissipating a total power of 100 Kw; 2)the loop built of SCH40S 304L steel piping, consisting of the pump, a heat exchanger and the pressurizer. (Author) [pt

  7. Analysis and interpretation of electrical resistivity tomography data of alluvial aquifer of Tamanrasset Southern Algeria

    Science.gov (United States)

    Zeddouri, Aziez; Elkheir, Abderrahmane Ben; Hadj-Said, Samia; Taupin, Jean-Denis; Leduc, Christian; Patris, Nicholas

    2018-05-01

    A groundwater exploration work in the Tamanrasset region in southern Algeria was started in August 2016 to assess the water reserves in the hydrogeological system related to the Oued Tamanrasset underflow water table which overcomes a volcanic basement. Five (05) electrical resistivity tomography (ERT) surveys were conducted in Tamanrasset area by using ABEM Terrameter LS system. the low electrical contrast between wet alluvium and water saturated alterites makes difficult the electrical response interpretation. to overcome the difficulties of interpretation of ERT profiles, field investigations, laboratory tests and software simulations, were carried out in order to clearly identify the structure of the hydrogeological system. The experimental investigation of the electrical characteristics of the alluvium as a function of water saturation was carried by the use of two devices (Wenner α and Schlumberger). Samples true resistivity values varies between 50 Ω.m for a 100% saturated sample and 1250 Ω.m for a 25% saturation sample. The interpretation of the measurements by the RES2DINV software made it possible to give 2D images of the subsoil up to a depth of 50 m. the electrical contrast between the bedrock and the overlying formations made it possible to identify it, however, it was difficult to distinguish alterites from alluvium. A methodology combining piezometric survey, geo-electrical measurements and field observations improves the interpretation of electrical tomography profiles and the application of the ERT method for accurate characterization of water resources in the Tamanrasset region.

  8. Electrical Resistance Tomography for Subsurface Imaging. Innovative Technology Summary Report

    International Nuclear Information System (INIS)

    None

    2000-01-01

    Electrical Resistance Tomography (ERT) noninvasively maps the 3-D resistivity field in the subsurface. It can be used on a scale from feet to kilometers. The 3-D resistivity field can be used to infer subsurface hydrogeological features and provides good resolution mapping of confining layers of various types. ERT imaging has been used for real-time monitoring and process control of remediation processes such as soil heating, pump and treat, steam injection, electrokinetics, Dynamic Underground Stripping (TechID 7), Hydrous Pyrolysis/Oxidation (TechID 1519) and more. ERT can be deployed via rapid and inexpensive installation of electrodes using a Cone Penetrometer (TechID 243). Additional applications are described under TechID 140 (Tanks) and TechID 2120 (Injected Subsurface Barriers); see also the related technology TechID 2121 (EIT)

  9. Measurement of microchannel fluidic resistance with a standard voltage meter.

    Science.gov (United States)

    Godwin, Leah A; Deal, Kennon S; Hoepfner, Lauren D; Jackson, Louis A; Easley, Christopher J

    2013-01-03

    A simplified method for measuring the fluidic resistance (R(fluidic)) of microfluidic channels is presented, in which the electrical resistance (R(elec)) of a channel filled with a conductivity standard solution can be measured and directly correlated to R(fluidic) using a simple equation. Although a slight correction factor could be applied in this system to improve accuracy, results showed that a standard voltage meter could be used without calibration to determine R(fluidic) to within 12% error. Results accurate to within 2% were obtained when a geometric correction factor was applied using these particular channels. When compared to standard flow rate measurements, such as meniscus tracking in outlet tubing, this approach provided a more straightforward alternative and resulted in lower measurement error. The method was validated using 9 different fluidic resistance values (from ∼40 to 600kPa smm(-3)) and over 30 separately fabricated microfluidic devices. Furthermore, since the method is analogous to resistance measurements with a voltage meter in electrical circuits, dynamic R(fluidic) measurements were possible in more complex microfluidic designs. Microchannel R(elec) was shown to dynamically mimic pressure waveforms applied to a membrane in a variable microfluidic resistor. The variable resistor was then used to dynamically control aqueous-in-oil droplet sizes and spacing, providing a unique and convenient control system for droplet-generating devices. This conductivity-based method for fluidic resistance measurement is thus a useful tool for static or real-time characterization of microfluidic systems. Copyright © 2012 Elsevier B.V. All rights reserved.

  10. Electrical measurements in µ-EDM

    International Nuclear Information System (INIS)

    Ferri, Carlo; Ivanov, Atanas; Petrelli, Antoine

    2008-01-01

    The phenomena occurring between the electrodes in electric discharge machining when manufacturing features on the micro-metre scale (µ-EDM) is not fully understood. Poor quantitative knowledge of the sources of variability affecting this process hinders the identification of its natural tolerance limits. Moreover, improvements in measuring systems contribute to the acquisition of new information that often conflicts with existent theoretical models of this process. The prime objective of this paper is to advance the experimental knowledge of µ-EDM by providing a measurement framework for the electrical discharges. The effects of the electrodes metallic materials (Ag, Ni, Ti, W) on the electrical measurements defined in the proposed framework are analysed. Linear mixed-effects models are fitted to the experimental data using the restricted maximum likelihood method (REML). The main conclusion drawn is that the discharge current and voltage as defined and measured in this framework do significantly depend on the electrode material even when keeping all the other machining conditions unchanged

  11. Application of Electrical Resistivity Tomography for Detecting Root Biomass in Coffee Trees

    Directory of Open Access Journals (Sweden)

    Carlos Mauricio Paglis

    2013-01-01

    Full Text Available Roots play an important role in plants and are responsible for several functions; among them are anchorage and nutrient and water absorption. Several methodologies are being tested and used to study plant root systems in order to avoid destructive root sampling. Electrical resistivity tomography is among these methodologies. The aim of this preliminary study was to use electrical resistivity for detecting root biomass in coffee trees. Measurements were performed in a soil transect with an ABM AL 48-b resistivimeter with a pole-dipole configuration. The tomograms indicated variability in soil resistivity values ranging from 120 to 1400 Ω·m−1. At the first 0.30 cm soil layer, these values were between 267 and 952 Ω·m−1. Oriented by this result, root samples were taken at 0.10, 0.20, and 0.30 m depths within 0.50 m intervals along the soil transect to compare soil resistivity with root mass density (RMD. RMD data, up to this depth, varied from 0.000019 to 0.009469 Mg·m−3, showing high spatial variability and significant relationship to the observed values of soil resistivity. These preliminary results showed that the electrical resistivity tomography can contribute to root biomass studies in coffee plants; however, more experiments are necessary to confirm the found results in Brazil coffee plantations.

  12. Hydrothermal fault zone mapping using seismic and electrical measurements

    Science.gov (United States)

    Onacha, Stephen Alumasa

    This dissertation presents a new method of using earthquakes and resistivity data to characterize permeable hydrothermal reservoirs. The method is applied to field examples from Casa Diablo in the Long Valley Caldera, California; Mt. Longonot, Kenya; and Krafla, Iceland. The new method has significant practical value in the exploration and production of geothermal energy. The method uses P- and S-wave velocity, S-wave polarization and splitting magnitude, resistivity and magnetotelluric (MT) strike directions to determine fracture-porosity and orientation. The conceptual model used to characterize the buried, fluid-circulating fault zones in hydrothermal systems is based on geological and fracture models. The method has been tested with field earthquake and resistivity data; core samples; temperature measurements; and, for the case of Krafla, with a drilled well. The use of resistivity and microearthquake measurements is based on theoretical formulation of shared porosity, anisotropy and polarization. The relation of resistivity and a double porosity-operator is solved using a basis function. The porosity-operator is used to generate a correlation function between P-wave velocity and resistivity. This correlation is then used to generate P-wave velocity from 2-D resistivity models. The resistivity models are generated from magnetotelluric (MT) by using the Non-Linear Conjugate Gradient (NLCG) inversion method. The seismic and electrical measurements used come from portable, multi station microearthquake (MEQ) monitoring networks and multi-profile, MT and transient electromagnetic (TEM) observation campaigns. The main conclusions in this dissertation are listed below: (1) Strong evidence exists for correlation between MT strike direction and anisotropy and MEQ S-wave splitting at sites close to fluid-filled fracture zones. (2) A porosity operator generated from a double porosity model has been used to generate valid P-wave velocity models from resistivity data. This

  13. Evolution of the electrical resistivity anisotropy during saline tracer tests: insights from geoelectrical milli-fluidic experiments

    Science.gov (United States)

    Jougnot, D.; Jimenez-Martinez, J.; Legendre, R.; Le Borgne, T.; Meheust, Y.; Linde, N.

    2017-12-01

    The use of time-lapse electrical resistivity tomography has been largely developed in environmental studies to remotely monitor water saturation and contaminant plumes migration. However, subsurface heterogeneities, and corresponding preferential transport paths, yield a potentially large anisotropy in the electrical properties of the subsurface. In order to study this effect, we have used a newly developed geoelectrical milli-fluidic experimental set-up with a flow cell that contains a 2D porous medium consisting of a single layer of cylindrical solid grains. We performed saline tracer tests under full and partial water saturations in that cell by jointly injecting air and aqueous solutions with different salinities. The flow cell is equipped with four electrodes to measure the bulk electrical resistivity at the cell's scale. The spatial distribution of the water/air phases and the saline solute concentration field in the water phase are captured simultaneously with a high-resolution camera by combining a fluorescent tracer with the saline solute. These data are used to compute the longitudinal and transverse effective electrical resistivity numerically from the measured spatial distributions of the fluid phases and the salinity field. This approach is validated as the computed longitudinal effective resistivities are in good agreement with the laboratory measurements. The anisotropy in electrical resistivity is then inferred from the computed longitudinal and transverse effective resistivities. We find that the spatial distribution of saline tracer, and potentially air phase, drive temporal changes in the effective resistivity through preferential paths or barriers for electrical current at the pore scale. The resulting heterogeneities in the solute concentrations lead to strong anisotropy of the effective bulk electrical resistivity, especially for partially saturated conditions. Therefore, considering the electrical resistivity as a tensor could improve our

  14. Electric field simulation and measurement of a pulse line ion accelerator

    International Nuclear Information System (INIS)

    Shen Xiaokang; Zhang Zimin; Cao Shuchun; Zhao Hongwei; Zhao Quantang; Liu Ming; Jing Yi; Wang Bo; Shen Xiaoli

    2012-01-01

    An oil dielectric helical pulse line to demonstrate the principles of a Pulse Line Ion Accelerator (PLIA) has been designed and fabricated. The simulation of the axial electric field of an accelerator with CST code has been completed and the simulation results show complete agreement with the theoretical calculations. To fully understand the real value of the electric field excited from the helical line in PLIA, an optical electric integrated electric field measurement system was adopted. The measurement result shows that the real magnitude of axial electric field is smaller than that calculated, probably due to the actual pitch of the resister column which is much less than that of helix. (authors)

  15. An experimental evaluation of joint electrical resistance on power lead thermal performance

    International Nuclear Information System (INIS)

    Datskov, V.I.; Demko, J.A.; Augustynowicz, S.D.; Hutton, R.D.

    1994-01-01

    The amount of electrical resistance in braze joints is not known for certain. In addition the annealing processes that occurs during a braze or solder operation can change the residual resistivity ratio (RRR) of the copper. The change in the electrical resistivity of samples of copper because of exposure to conditions that a high current lead would see during a brazing operation were experimentally investigated. A sample was taken from a manufacturing and brazing trial of the high current power leads for the Superconducting Super Collider (SSC), and from oxygen free high conductivity copper (OFHC) 101 rod similar to that used in the trial. The samples were heated under conditions that a current lead would undergo during the brazing process. Measurements were made of the electrical resistance of the copper specimens and across a braze joint in the manufacturing trial sample for temperatures ranging from liquid helium to room temperature. A prototype of the SSC high current lead is shown. This lead was fabricated from 5 sections that were brazed together. Some results for the measured residual resistivity ratio (RRR) along this lead are given

  16. Continuous monitoring of the composition of liquid Pb-17Li eutectic using electrical resistivity methods

    International Nuclear Information System (INIS)

    Hubberstey, P.; Sample, T.; Barker, M.G.

    1991-01-01

    The composition of liquid Pb-17Li alloys has been continously determined, using an electrical resistivity monitor, during their interaction with nitrogen, oxygen, hydrogen and water vapour. The operation of the monitor depends on the fact that the resistivity of liquid Pb-Li alloys is dependent on their composition. Accurate resistivity-composition isotherms have been derived from resistivity-temperature data for 15 Pb-Li alloys (0 Li -8 Ω m (mol% Li) -1 at 725 K) is such that a change of 0.05 mol% Li in the alloy composition can be measured. The addition of oxygen and water vapour resulted in a decrease in the resistivity of the liquid alloy. Neither nitrogen nor hydrogen had any effect. The observed changes were shown to be consistent with Li 2 O formation. (orig.)

  17. Electric Field Effects in RUS Measurements

    Energy Technology Data Exchange (ETDEWEB)

    Darling, Timothy W [Los Alamos National Laboratory; Ten Cate, James A [Los Alamos National Laboratory; Allured, Bradley [UNIV NEVADA, RENO; Carpenter, Michael A [CAMBRIDGE UNIV. UK

    2009-09-21

    Much of the power of the Resonant Ultrasound Spectroscopy (RUS) technique is the ability to make mechanical resonance measurements while the environment of the sample is changed. Temperature and magnetic field are important examples. Due to the common use of piezoelectric transducers near the sample, applied electric fields introduce complications, but many materials have technologically interesting responses to applied static and RF electric fields. Non-contact optical, buffered, or shielded transducers permit the application of charge and externally applied electric fields while making RUS measurements. For conducting samples, in vacuum, charging produces a small negative pressure in the volume of the material - a state rarely explored. At very high charges we influence the electron density near the surface so the propagation of surface waves and their resonances may give us a handle on the relationship of electron density to bond strength and elasticity. Our preliminary results indicate a charge sign dependent effect, but we are studying a number of possible other effects induced by charging. In dielectric materials, external electric fields influence the strain response, particularly in ferroelectrics. Experiments to study this connection at phase transformations are planned. The fact that many geological samples contain single crystal quartz suggests a possible use of the piezoelectric response to drive vibrations using applied RF fields. In polycrystals, averaging of strains in randomly oriented crystals implies using the 'statistical residual' strain as the drive. The ability to excite vibrations in quartzite polycrystals and arenites is explored. We present results of experimental and theoretical approaches to electric field effects using RUS methods.

  18. Electrical resistivity tomography at the DOE Hanford site

    International Nuclear Information System (INIS)

    Narbutovskih, S.M.; Halter, T.D.; Sweeney, M.D.; Daily, W.; Ramirez, A.L.

    1996-01-01

    Recent work at the DOE Hanford site has established the potential of applying Electrical Resistivity Tomography (ERT) for early leak detection under hazardous waste storage facilities. Several studies have been concluded to test the capabilities and limitations of ERT for two different applications. First, field experiments have been conducted to determine the utility of ERT to detect and map leaks from underground storage tanks during waste removal processes. Second, the use of ERT for long term vadose zone monitoring has been tested under different field conditions of depth, installation design, acquisition mode/equipment and infiltration chemistry. This work involves transferring the technology from Lawrence Livermore National Laboratory (LLNL) to the Resource Conservation and Recovery Act (RCRA) program at the DOE Hanford Site. This paper covers field training studies relevant to the second application for long term vadose zone monitoring. Electrical resistivity tomography is a cross-borehole, imaging technique for mapping subsurface resistivity variations. Electrodes are placed at predetermined depths in an array of boreholes. Electrical current is introduced into one electrode pair located in one borehole while the resulting voltage change is detected between electrode pairs in other boreholes similar to a surface dipole-dipole array. These data are tomographically inverted to image temporal resistivity contrasts associated with an infiltration event. Thus a dynamic plume is spatially mapped as a function of time. As a long-term vadose zone monitoring method, different field conditions and performance requirements exist than those for short term tank leak detection. To test ERT under these conditions, two vertical electrode arrays were constructed to a depth of 160 feet with a linear surface array between boreholes

  19. Electrical resistance oscillations during plastic deformation in A Ti-Al-Nb-Zr alloy at 4·2 K

    Science.gov (United States)

    Nikiforenko, V. N.; Lavrentev, F. F.

    1986-10-01

    The serrated plastic flow in titanium alloy containing 5% Al, 2·5% Zr and 2% Nb has been investigated by measuring its electrical resistance and applying selective chemical etching. The electrical resistance was found to oscillate under active deformation at 4·2 K. Analysis of the possible causes seems to indicate a dominant role of break by dislocation pile-ups through obstacles, viz second phase precipitates and grain boundaries.

  20. Electrical resistivity tomography investigations in the ufita Valley (southern Italy.

    Directory of Open Access Journals (Sweden)

    C. Basso

    2008-06-01

    Full Text Available Several Electrical Resistivity Tomography (ERT surveys have been carried out to study the subsurface structural and sedimentary settings of the upper Ufita River valley, and to evaluate their efficiency to distinguish the geological boundary between shallow Quaternary sedimentary deposits and clayey bedrock characterized by moderate resistivity contrast. Five shallow ERTs were carried out across a morphological scarp running at the foot of the northeastern slope of the valley. This valley shoulder is characterized by a set of triangular facets, that some authors associated to the presence of a SW-dipping normal fault. The geological studies allow us to interpret the shallow ERTs results obtaining a resistivity range for each Quaternary sedimentary deposit. The tomographies showed the geometrical relationships of alluvial and slope deposits, having a maximum thickness of 30-40 m, and the morphology of the bedrock. The resistivity range obtained for each sedimentary body has been used for calibrating the tomographic results of one 3560m-long deep ERT carried out across the deeper part of the intramountain depression with an investigation depth of about 170 m. The deep resistivity result highlighted the complex alluvial setting, characterized by alternating fine grained lacustrine deposits and coarser gravelly fluvial sediments.

  1. Monitoring the ground water level change during the pump test by using the Electric resistivity tomography

    Science.gov (United States)

    Hsu, H.; Chang, P. Y.; Yao, H. J.

    2017-12-01

    For hydrodynamics study of the unconfined aquifer in gravel formation, a pumping test was established to estimate the hydraulic conductivity in the midstream of Zhoushui River in Taiwan. The hydraulic parameters and the cone of depression could be estimated by monitoring the groundwater drawdown in an observation well which was in a short distance far from the pumping well. In this study we carried out the electric resistivity image monitoring during the whole pumping test. The electric resistivity data was measured with the surface and downhole electrodes which would produce a clear subsurface image of groundwater level through a larger distance than the distance between pumping and observation wells. The 2D electric image could also describe how a cone of depression truly created at subsurface. The continuous records could also show the change of groundwater level during the whole pumping test which could give a larger scale of the hydraulic parameters.

  2. Use of Direct Current Resistivity Measurements to Assess AISI 304 Austenitic Stainless Steel Sensitization

    OpenAIRE

    Mesquita, Ramaiany Carneiro; Mecury, José Manoel Rivas; Tanaka, Auro Atsumi; Sousa, Regina Célia de

    2015-01-01

    This paper describes the feasibility of using direct current electrical resistivity measurements to evaluate AISI 304 austenitic stainless steel sensitization. ASTM A262 – Practice A and double loop electrochemical potentiodynamic reactivation (DL-EPR) tests were performed to assess the degree of sensitization (DoS) qualitatively and quantitatively, and electrical resistivity (ER) was measured by the four-point direct-current potential drop method. The results indicate that the DoS incr...

  3. In-situ measurement of the electrical conductivity of aluminum oxide in HFIR

    Energy Technology Data Exchange (ETDEWEB)

    Zinkle, S.J.; White, D.P.; Snead, L.L. [Oak Ridge National Lab., TN (United States)] [and others

    1996-10-01

    A collaborative DOE/Monbusho irradiation experiment has been completed which measured the in-situ electrical resistivity of 12 different grades of aluminum oxide during HFIR neutron irradiation at 450{degrees}C. No evidence for bulk RIED was observed following irradiation to a maximum dose of 3 dpa with an applied dc electric field of 200 V/mm.

  4. Dissolution-Enlarged Fractures Imaging Using Electrical Resistivity Tomography (ERT)

    Science.gov (United States)

    Siami-Irdemoosa, Elnaz

    In recent years the electrical imaging techniques have been largely applied to geotechnical and environmental investigations. These techniques have proven to be the best geophysical methods for site investigations in karst terrain, particularly when the overburden soil is clay-dominated. Karst is terrain with a special landscape and distinctive hydrological system developed by dissolution of rocks, particularly carbonate rocks such as limestone and dolomite, made by enlarging fractures into underground conduits that can enlarge into caverns, and in some cases collapse to form sinkholes. Bedding planes, joints, and faults are the principal structural guides for underground flow and dissolution in almost all karstified rocks. Despite the important role of fractures in karst development, the geometry of dissolution-enlarged fractures remain poorly unknown. These features are characterized by an strong contrast with the surrounding formations in terms of physical properties, such as electrical resistivity. Electrical resistivity tomography (ERT) was used as the primary geophysical tool to image the subsurface in a karst terrain in Greene County, Missouri. Pattern, orientation and density of the joint sets were interpreted from ERT data in the investigation site. The Multi-channel Analysis of Surface Wave (MASW) method and coring were employed to validate the interpretation results. Two sets of orthogonal visually prominent joints have been identified in the investigation site: north-south trending joint sets and west-east trending joint sets. However, most of the visually prominent joint sets are associated with either cultural features that concentrate runoff, natural surface drainage features or natural surface drainage.

  5. Electrical resistivity and thermopower of ErCo3 under hydrostatic pressure

    International Nuclear Information System (INIS)

    Nakama, T; Niki, H; Nakamura, D; Takaesu, Y; Hedo, M; Yagasaki, K; Uchima, K; Gratz, E; Burkov, A T

    2009-01-01

    The magnetic state of the Co 3d-electron subsystem of RCo 3 compounds (R=rare-earth elements) with the rhombohedral PuNi 3 -type structure strongly depends on external parameters. In order to clarify the effect of pressure on the magnetic state of the itinerant Co 3d-electrons, we have measured the electrical resistivity and thermopower at temperatures from 2 K to 300 K under hydrostatic pressures up to 2 GPa. Both, ρ and S show anomalies at critical temperature of metamagnetic transition T m . With increasing pressure T m , determined from the temperature-dependent resistivity and thermopower, decreases and apparently vanishes at P ∼ 0.7 GPa. The electrical resistivity and thermopower at low temperatures show abrupt changes at P ∼ 0.7 GPa, indicating a pressure-induced phase transition.

  6. Elasticity and electrical resistivity of chalk and greensand during water flooding with selective ions

    DEFF Research Database (Denmark)

    Katika, Konstantina; Alam, Mohammad Monzurul; Alexeev, Artem

    2018-01-01

    is water-wet after flooding. Greensand remained mixed wet throughout the experiments. Electrical resistivity data are in agreement with this interpretation. The electrical resistivity data during flooding revealed that the formation brine is not fully replaced by the injected water in both chalk......Water flooding with selective ions has in some cases lead to increased oil recovery. We investigate the physical processes on a pore scale that are responsible for changes in petrophysical and mechanical properties of four oil-bearing chalk and four oil-bearing greensand samples caused by flooding...... with brines containing varying amounts of dissolved NaCl, Na2SO4, MgCl2 and MgSO4. Ultrasonic P-wave velocity and AC resistivity measurements were performed prior to, during and after flow through experiments in order to identify and quantify the processes related to water flooding with selective ions. Low...

  7. Crystal structure and electrical resistivity studies of Gd(Fe1-x Cox)2 intermetallics

    International Nuclear Information System (INIS)

    Onak, M.; Guzdek, P.; Stoch, P.; Chmist, J.; Bednarski, M.; Panta, A.; Pszczola, J.

    2007-01-01

    From X-ray analysis (295 K) it was found that the cubic, MgCu 2 -type, Fd3m crystal structure appears across the Gd(Fe 1-x Co x ) 2 series. Electrical resistivity measurements for the Gd(Fe 1-x Co x ) 2 intermetallics were performed in a wide temperature region and the parameters characterizing the resistivity dependence on temperature and composition were determined. The differential of the electrical resistivity against temperature was used to estimate Curie temperatures. The Curie temperature versus x, high and moderately increasing in the iron-rich area, rapidly drops in the cobalt-rich region. The obtained results are compared with the data known for the Dy(Fe 1-x Co x ) 2 series. The Curie temperature is related to both the number of 3d electrons and the de Gennes factor

  8. Investigation of Concrete Electrical Resistivity As a Performance Based Test

    OpenAIRE

    Malakooti, Amir

    2017-01-01

    The purpose of this research project was to identify the extent that concrete resistivity measurements (bulk and/or surface) can be used as a performance based lab test to improve the quality of concrete in Utah bridge decks. By allowing UDOT to specify a required resistivity, concrete bridge deck quality will increase and future maintenance costs will decrease. This research consisted of two phases: the field phase and the lab phase. In the field phase, concrete samples were gathered from...

  9. Offset-electrode profile acquisition strategy for electrical resistivity tomography

    Science.gov (United States)

    Robbins, Austin R.; Plattner, Alain

    2018-04-01

    We present an electrode layout strategy that allows electrical resistivity profiles to image the third dimension close to the profile plane. This "offset-electrode profile" approach involves laterally displacing electrodes away from the profile line in an alternating fashion and then inverting the resulting data using three-dimensional electrical resistivity tomography software. In our synthetic and field surveys, the offset-electrode method succeeds in revealing three-dimensional structures in the vicinity of the profile plane, which we could not achieve using three-dimensional inversions of linear profiles. We confirm and explain the limits of linear electrode profiles through a discussion of the three-dimensional sensitivity patterns: For a homogeneous starting model together with a linear electrode layout, all sensitivities remain symmetric with respect to the profile plane through each inversion step. This limitation can be overcome with offset-electrode layouts by breaking the symmetry pattern among the sensitivities. Thanks to freely available powerful three-dimensional resistivity tomography software and cheap modern computing power, the requirement for full three-dimensional calculations does not create a significant burden and renders the offset-electrode approach a cost-effective method. By offsetting the electrodes in an alternating pattern, as opposed to laying the profile out in a U-shape, we minimize shortening the profile length.

  10. Stage IV in electrical resistivity return to alpha-iron

    International Nuclear Information System (INIS)

    Poltavtseva, V.P.

    2004-01-01

    Full text: In compliance with the model of two interstitial atoms, in returning the electrical resistivity increment, the stage IV, related to migration of mono vacancies, should exist. Unfortunately, for alpha-iron there is no any reliable proof of existence of the stage IV (450-630 K) up to now. As a rule, the annealing stages revealed within this temperature range are considered as related to impurity effects. This paper is aimed at detection of the stage IV in returning the electrical resistivity increment in alpha-iron by means of irradiation of the materials differing in purity degree (99.99 and 99.8 %) by 30 MeV protons capable to create large amount of point defects and small clusters in BCC metals. By author opinion, it will make it possible to reach the radiation defect/vacancy concentrations comparable with contents of impurities (C and N) and, thus, to obtain an information about their migration. As a result of irradiation by protons at 270 K up to the fluence comprising 2.3·10 21 m -2 (0.001 dpa), the following has been found: - an increase in the electrical resistivity at 330 K is 0.84 and 0.61 nΩ·m for the alpha-iron purity degree 99.99 and 99.8 % respectively; - in the 99.99 % purity degree alpha-iron the process of electrical resistivity restoration comes to an end completely at 563 K, whereas in alpha-iron with larger content of impurity - at nearly 600 K; - in the 99.99% purity degree alpha iron electrical resistivity return spectrum a single wide peak centered at 445 K and two smeared peaks below 400 and higher than 490 K are revealed. As the impurity content increases, the 464 K peak changes the 445 K peak, which is about twice lower. Besides, a peak at 377 K occurs, and the peak at a temperature higher than 500 K, in contrast to the 99.99 % purity degree alpha-iron, has a point of inflection at 590 K. On a base of the data obtained, one may conclude that the stage centered around 445 K is of intrinsic nature, and the 99.99 % purity degree

  11. Electrical resistivity, Hall coefficient and electronic mobility in indium antimonide at different magnetic fields and temperatures

    International Nuclear Information System (INIS)

    Jee, Madan; Prasad, Vijay; Singh, Amita

    1995-01-01

    The electrical resistivity, Hall coefficient and electronic mobility of n-type and p-type crystals of indium antimonide have been measured from 25 degC-100 degC temperature range. It has been found by this measurement that indium antimonide is a compound semiconductor with a high mobility 10 6 cm 2 /V.S. The Hall coefficient R H was measured as a function of magnetic field strength H for a number of samples of both p and n-type using fields up to 12 kilo gauss. The Hall coefficient R h decreases with increasing magnetic fields as well as with increase in temperature of the sample. The electric field is more effective on samples with high mobilities and consequently the deviations from linearity are manifested at comparatively low values of the electric field. The measurement of R H in weak and strong magnetic fields makes it possible to determine the separate concentration of heavy and light holes. Measured values of Hall coefficient and electrical resistivity show that there is a little variation of ρ and R h with temperatures as well as with magnetic fields. (author). 12 refs., 5 tabs

  12. EDM: Neutron electric dipole moment measurement

    Directory of Open Access Journals (Sweden)

    Peter Fierlinger

    2016-02-01

    Full Text Available An electric dipole moment (EDM of the neutron would be a clear sign of new physics beyond the standard model of particle physics. The search for this phenomenon is considered one of the most important experiments in fundamental physics and could provide key information on the excess of matter versus antimatter in the universe. With high measurement precision, this experiment aims to ultimately achieve a sensitivity of 10-28 ecm, a 100-fold improvement in the sensitivity compared to the state-of-the-art. The EDM instrument is operated by an international collaboration based at the Technische Universität München.

  13. Measuring Learning Resistance to Workplace Training

    Science.gov (United States)

    Taylor, Jonathan E.; Lounsbury, John

    2016-01-01

    Training Transfer has been a topic bearing considerable mention over the past several decades. This article focuses on the connection between training transfer and learning resistance and presents research findings describing the design, creation, and testing of the Learning Efficiency Inventory (LEI). The LEI was designed to measure learning…

  14. Research on Image Reconstruction Algorithms for Tuber Electrical Resistance Tomography System

    Directory of Open Access Journals (Sweden)

    Jiang Zili

    2016-01-01

    Full Text Available The application of electrical resistance tomography (ERT technology has been expanded to the field of agriculture, and the concept of TERT (Tuber Electrical Resistance Tomography is proposed. On the basis of the research on the forward and the inverse problems of the TERT system, a hybrid algorithm based on genetic algorithm is proposed, which can be used in TERT system to monitor the growth status of the plant tubers. The image reconstruction of TERT system is different from the conventional ERT system for two phase-flow measurement. Imaging of TERT needs more precision measurement and the conventional ERT cares more about the image reconstruction speed. A variety of algorithms are analyzed and optimized for the purpose of making them suitable for TERT system. For example: linear back projection, modified Newton-Raphson and genetic algorithm. Experimental results showed that the novel hybrid algorithm is superior to other algorithm and it can effectively improve the image reconstruction quality.

  15. Pressure-induced positive electrical resistivity coefficient in Ni-Nb-Zr-H glassy alloy

    Science.gov (United States)

    Fukuhara, M.; Gangli, C.; Matsubayashi, K.; Uwatoko, Y.

    2012-06-01

    Measurements under hydrostatic pressure of the electrical resistivity of (Ni0.36Nb0.24Zr0.40)100-xHx (x = 9.8, 11.5, and 14) glassy alloys have been made in the range of 0-8 GPa and 0.5-300 K. The resistivity of the (Ni0.36Nb0.24Zr0.40)86H14 alloy changed its sign from negative to positive under application of 2-8 GPa in the temperature range of 300-22 K, coming from electron-phonon interaction in the cluster structure under pressure, accompanied by deformation of the clusters. In temperature region below 22 K, the resistivity showed negative thermal coefficient resistance by Debye-Waller factor contribution, and superconductivity was observed at 1.5 K.

  16. An experimental approach of decoupling Seebeck coefficient and electrical resistivity

    Science.gov (United States)

    Muhammed Sabeer N., A.; Paulson, Anju; Pradyumnan, P. P.

    2018-04-01

    The Thermoelectrics (TE) has drawn increased attention among renewable energy technologies. The performance of a thermoelectric material is quantified by a dimensionless thermoelectric figure of merit, ZT=S2σT/κ, where S and σ vary inversely each other. Thus, improvement in ZT is not an easy task. So, researchers have been trying different parameter variations during thin film processing to improve TE properties. In this work, tin nitride (Sn3N4) thin films were deposited on glass substrates by reactive RF magnetron sputtering and investigated its thermoelectric response. To decouple the covariance nature of Seebeck coefficient and electrical resistivity for the enhancement of power factor (S2σ), the nitrogen gas pressure during sputtering was reduced. Reduction in nitrogen gas pressure reduced both sputtering pressure and amount of nitrogen available for reaction during sputtering. This experimental approach of combined effect introduced preferred orientation and stoichiometric variations simultaneously in the sputtered Sn3N4 thin films. The scattering mechanism associated with these variations enhanced TE properties by independently drive the Seebeck coefficient and electrical resistivity parameters.

  17. Electrical resistivity of amorphous Fesub(1-x) Bsub(x) alloys

    International Nuclear Information System (INIS)

    Paja, A.; Stobiecki, T.

    1984-07-01

    The concentration dependence of the electrical resistivity of amorphous Fesub(1-x) Bsub(x) alloys has been studied over a broad composition range. The measurements for RF sputtered films made in the liquid helium temperature have been analyzed in the framework of the diffraction model. The calculated results are in good agreement with the experimental data in the range of concentration 0.12< x <0.37 where samples are amorphous and have a metallic character. (author)

  18. Electrical resistivity of nanocrystals in Fe-Al-Ga-P-B-Si-Cu alloy

    International Nuclear Information System (INIS)

    Pekala, K.; Jaskiewicz, P.; Nowinski, J.L.; Pekala, M.

    2003-01-01

    In new supercooled Fe 74 Al 4 Ga 2 P 11 B 4 Si 4 Cu 1 alloy the 10 nm size α-Fe(Si) nanocrystals are precipitated. Thermal stability is analyzed by the electron transport and magnetization measurements. Temperature variation of electrical resistivity of nanocrystals is determined and discussed for alloys with different initial crystalline fraction. Possible mechanism inhibiting the grain growth is presented

  19. Influence of illumination and decay of electrical resistance of ITO nanoscale layers

    Energy Technology Data Exchange (ETDEWEB)

    Somogyi, K. [MicroVacuum Ltd., Kerekgyarto u.: 10, H-1147 Budapest (Hungary)], E-mail: karoly.somogyi@microvacuum.com; Erdelyi, K.; Szendro, I. [MicroVacuum Ltd., Kerekgyarto u.: 10, H-1147 Budapest (Hungary)

    2008-09-30

    Indium tin oxide (ITO) is known as a transparent oxide with n-type electrical conductivity. However, the as grown ITO layers have high resistivity and the transparency is also limited. In this work, thin ITO layers were deposited by evaporation and then underwent a post-growth annealing. Annealing leads to a low electrical resistivity and to an enhanced transparency. Annealed samples show n-type conductivity. In this work, ITO layers of typically 10 nm thicknesses were deposited onto Si{sub 1-x}Ti{sub x}O{sub 2} covered glass substrates and then annealed. First the conductivity was evaluated after the annealing. The rough, quick estimation was performed by simple two point direct resistance measurement, and then van der Pauw configuration and collinear four-point probe method were applied. The light sensitivity and storage time dependent stability were studied. It is demonstrated that the resistance decreases due to illumination, though only in a small extent. The measure and speed of the decrease depend on the wavelength of the light and the process is very slow (up to hours). The recovery of the starting resistance is also a slow process.

  20. Improvement of electrical resistivity tomography for leachate injection monitoring

    International Nuclear Information System (INIS)

    Clement, R.; Descloitres, M.; Guenther, T.; Oxarango, L.; Morra, C.; Laurent, J.-P.; Gourc, J.-P.

    2010-01-01

    Leachate recirculation is a key process in the scope of operating municipal waste landfills as bioreactors, which aims to increase the moisture content to optimize the biodegradation in landfills. Given that liquid flows exhibit a complex behaviour in very heterogeneous porous media, in situ monitoring methods are required. Surface time-lapse electrical resistivity tomography (ERT) is usually proposed. Using numerical modelling with typical 2D and 3D injection plume patterns and 2D and 3D inversion codes, we show that wrong changes of resistivity can be calculated at depth if standard parameters are used for time-lapse ERT inversion. Major artefacts typically exhibit significant increases of resistivity (more than +30%) which can be misinterpreted as gas migration within the waste. In order to eliminate these artefacts, we tested an advanced time-lapse ERT procedure that includes (i) two advanced inversion tools and (ii) two alternative array geometries. The first advanced tool uses invariant regions in the model. The second advanced tool uses an inversion with a 'minimum length' constraint. The alternative arrays focus on (i) a pole-dipole array (2D case), and (ii) a star array (3D case). The results show that these two advanced inversion tools and the two alternative arrays remove almost completely the artefacts within +/-5% both for 2D and 3D situations. As a field application, time-lapse ERT is applied using the star array during a 3D leachate injection in a non-hazardous municipal waste landfill. To evaluate the robustness of the two advanced tools, a synthetic model including both true decrease and increase of resistivity is built. The advanced time-lapse ERT procedure eliminates unwanted artefacts, while keeping a satisfactory image of true resistivity variations. This study demonstrates that significant and robust improvements can be obtained for time-lapse ERT monitoring of leachate recirculation in waste landfills.

  1. Improvement of electrical resistivity tomography for leachate injection monitoring.

    Science.gov (United States)

    Clément, R; Descloitres, M; Günther, T; Oxarango, L; Morra, C; Laurent, J-P; Gourc, J-P

    2010-03-01

    Leachate recirculation is a key process in the scope of operating municipal waste landfills as bioreactors, which aims to increase the moisture content to optimize the biodegradation in landfills. Given that liquid flows exhibit a complex behaviour in very heterogeneous porous media, in situ monitoring methods are required. Surface time-lapse electrical resistivity tomography (ERT) is usually proposed. Using numerical modelling with typical 2D and 3D injection plume patterns and 2D and 3D inversion codes, we show that wrong changes of resistivity can be calculated at depth if standard parameters are used for time-lapse ERT inversion. Major artefacts typically exhibit significant increases of resistivity (more than +30%) which can be misinterpreted as gas migration within the waste. In order to eliminate these artefacts, we tested an advanced time-lapse ERT procedure that includes (i) two advanced inversion tools and (ii) two alternative array geometries. The first advanced tool uses invariant regions in the model. The second advanced tool uses an inversion with a "minimum length" constraint. The alternative arrays focus on (i) a pole-dipole array (2D case), and (ii) a star array (3D case). The results show that these two advanced inversion tools and the two alternative arrays remove almost completely the artefacts within +/-5% both for 2D and 3D situations. As a field application, time-lapse ERT is applied using the star array during a 3D leachate injection in a non-hazardous municipal waste landfill. To evaluate the robustness of the two advanced tools, a synthetic model including both true decrease and increase of resistivity is built. The advanced time-lapse ERT procedure eliminates unwanted artefacts, while keeping a satisfactory image of true resistivity variations. This study demonstrates that significant and robust improvements can be obtained for time-lapse ERT monitoring of leachate recirculation in waste landfills. Copyright 2009 Elsevier Ltd. All rights

  2. Electrical resistivity tomography at the DOE Hanford site

    International Nuclear Information System (INIS)

    Narbutovskih, S.M.

    1996-01-01

    Recent work at the DOE Hanford site has established the potential of applying Electrical Resistivity Tomography (ERT) for early leak detection under hazardous waste storage facilities. Several studies have been concluded to test the capabilities and limitations of ERT for two different applications. First, field experiments have been conducted to determine the utility of ERT to detect and map leaks from underground storage tanks during waste removal processes. Second, the use of ERT for long term vadose zone monitoring has been tested under different field conditions of depth, installation design, acquisition mode/equipment and infiltration chemistry. This work involves transferring the technology from Lawrence Livermore National Laboratory (LLNL) to the Resource Conservation and Recovery Act (RCRA) program at the DOE Hanford Site. This paper covers field training studies relevant to the second application for long term vadose monitoring. Electrical resistivity tomography is a cross-borehole, imaging technique for mapping subsurface resistivity variations. Electrodes are placed at predetermined depths in an array of boreholes. Electrical current is introduced into one electrode pair located in one borehole while the resulting voltage change is detected between electrode pairs in other boreholes similar to a surface dipole-dipole array. These data are topographically inverted to image temporal resistivity contrasts associated with an infiltration event. Thus a dynamic plume is spatially mapped as a function of time. As a long-term vadose zone monitoring method, different field conditions and performance requirements exist than those for short term tank leak detection. To test ERT under these conditions, two vertical electrode arrays were constructed to a depth of 160 feet with a linear surface array between boreholes. The fielding was used to facilitate the technology transfer from LLNL to the Hanford RCRA program. Installation methods, commercial equipment and

  3. 30 CFR 7.407 - Test for flame resistance of electric cables and cable splices.

    Science.gov (United States)

    2010-07-01

    ... 30 Mineral Resources 1 2010-07-01 2010-07-01 false Test for flame resistance of electric cables... Electric Cables, Signaling Cables, and Cable Splice Kits § 7.407 Test for flame resistance of electric... material and 21/2 inches of conductor insulation. The type, amperage, voltage rating, and construction of...

  4. 2d electrical resistivity engineering and hydrogeologic ectrical ...

    African Journals Online (AJOL)

    userpc

    station. In the Wenner-Schlumberger method, the first step is to make all the possible measurements while ... generating 18, 16, 14, 12, 10 and 8 resistivity values respectively in .... strong tidal waves and storm, serves a habitat for crustaceous ...

  5. Fabrication of an Electrically-Resistive, Varistor-Polymer Composite

    Directory of Open Access Journals (Sweden)

    Sanaz A. Mohammadi

    2012-11-01

    Full Text Available This study focuses on the fabrication and electrical characterization of a polymer composite based on nano-sized varistor powder. The polymer composite was fabricated by the melt-blending method. The developed nano-composite was characterized by X-ray diffraction (XRD, transmission electron microscopy (TEM, field emission scanning electron microscopy (FeSEM, and energy-dispersive X-ray spectroscopy (EDAX. The XRD pattern revealed the crystallinity of the composite. The XRD study also showed the presence of secondary phases due to the substitution of zinc by other cations, such as bismuth and manganese. The TEM picture of the sample revealed the distribution of the spherical, nano-sized, filler particles throughout the matrix, which were in the 10–50 nm range with an average of approximately 11 nm. The presence of a bismuth-rich phase and a ZnO matrix phase in the ZnO-based varistor powder was confirmed by FeSEM images and EDX spectra. From the current-voltage curves, the non-linear coefficient of the varistor polymer composite with 70 wt% of nano filler was 3.57, and its electrical resistivity after the onset point was 861 KΩ. The non-linear coefficient was 1.11 in the sample with 100 wt% polymer content. Thus, it was concluded that the composites established a better electrical non-linearity at higher filler amounts due to the nano-metric structure and closer particle linkages.

  6. Experimental investigation into the coupling effects of magnetic field, temperature and pressure on electrical resistivity of non-oriented silicon steel sheet

    Science.gov (United States)

    Xiao, Lijun; Yu, Guodong; Zou, Jibin; Xu, Yongxiang

    2018-05-01

    In order to analyze the performance of magnetic device which operate at high temperature and high pressure, such as submersible motor, oil well transformer, the electrical resistivity of non-oriented silicon steel sheets is necessary for precise analysis. But the reports of the examination of the measuring method suitable for high temperature up to 180 °C and high pressure up to 140 MPa are few. In this paper, a measurement system based on four-probe method and Archimedes spiral shape measurement specimens is proposed. The measurement system is suitable for measuring the electrical resistivity of unconventional specimens under high temperature and high pressure and can simultaneously consider the influence of the magnetic field on the electrical resistivity. It can be seen that the electrical resistivity of the non-oriented silicon steel sheets will fluctuate instantaneously when the magnetic field perpendicular to the conductive path of the specimens is loaded or removed. The amplitude and direction of the fluctuation are not constant. Without considering the effects of fluctuations, the electrical resistivity of the non-oriented silicon steel sheets is the same when the magnetic field is loaded or removed. And the influence of temperature on the electrical resistivity of the non-oriented silicon steel sheet is still the greatest even though the temperature and the pressure are coupled together. The measurement results also show that the electrical resistivity varies linearly with temperature, so the temperature coefficient of resistivity is given in the paper.

  7. Long-term electrical resistivity monitoring of recharge-induced contaminant plume behavior.

    Science.gov (United States)

    Gasperikova, Erika; Hubbard, Susan S; Watson, David B; Baker, Gregory S; Peterson, John E; Kowalsky, Michael B; Smith, Meagan; Brooks, Scott

    2012-11-01

    Geophysical measurements, and electrical resistivity tomography (ERT) data in particular, are sensitive to properties that are related (directly or indirectly) to hydrological processes. The challenge is in extracting information from geophysical data at a relevant scale that can be used to gain insight about subsurface behavior and to parameterize or validate flow and transport models. Here, we consider the use of ERT data for examining the impact of recharge on subsurface contamination at the S-3 ponds of the Oak Ridge Integrated Field Research Challenge (IFRC) site in Tennessee. A large dataset of time-lapse cross-well and surface ERT data, collected at the site over a period of 12 months, is used to study time variations in resistivity due to changes in total dissolved solids (primarily nitrate). The electrical resistivity distributions recovered from cross-well and surface ERT data agrees well, and both of these datasets can be used to interpret spatiotemporal variations in subsurface nitrate concentrations due to rainfall, although the sensitivity of the electrical resistivity response to dilution varies with nitrate concentration. Using the time-lapse surface ERT data interpreted in terms of nitrate concentrations, we find that the subsurface nitrate concentration at this site varies as a function of spatial position, episodic heavy rainstorms (versus seasonal and annual fluctuations), and antecedent rainfall history. These results suggest that the surface ERT monitoring approach is potentially useful for examining subsurface plume responses to recharge over field-relevant scales. Published by Elsevier B.V.

  8. A method to improve tree water use estimates by distinguishing sapwood from heartwood using Electrical Resistivity Tomography

    Science.gov (United States)

    Guyot, A.; Ostergaard, K.; Lenkopane, M.; Fan, J.; Lockington, D. A.

    2011-12-01

    Estimating whole-plant water use in trees requires reliable and accurate methods. Measuring sap velocity and extrapolating to tree water use is seen as the most commonly used. However, deducing the tree water use from sap velocity requires an estimate of the sapwood area. This estimate is the highest cause of uncertainty, and can reach more than 50 % of the uncertainty in the estimate of water use per day. Here, we investigate the possibility of using Electrical Resistivity Tomography to evaluate the sapwood area distribution in a plantation of Pinus elliottii. Electric resistivity tomographs of Pinus elliottii show a very typical pattern of electrical resistivity, which is highly correlated to sapwood and heartwood distribution. To identify the key factors controlling the variation of electrical resistivity, cross sections at breast height for ten trees have been monitored with electrical resistivity tomography. Trees have been cut down after the experiment to identify the heartwood/sapwood boundaries and to extract wood and sap samples. pH, electrolyte concentration and wood moisture content have then been analysed for these samples. Results show that the heartwood/sapwood patterns are highly correlated with electrical resistivity, and that the wood moisture content is the most influencing factor controlling the variability of the patterns. These results show that electric resistivity tomography could be used as a powerful tool to identify the sapwood area, and thus be used in combination with sapflow sensors to map tree water use at stand scale. However, if Pinus elliottii shows typical patterns, further work is needed to identify to see if there are species - specific characterictics as shown in previous works (, electrolyte gradients from the bark to the heartwood). Also, patterns of high resistivity in between needles positions, which are not correlated with either wood moisture content or sapwood, appear to be artifacts. Thus, inversion methods have also to

  9. Apparatus for measuring resistance change only in a cell analyzer and method for calibrating it

    Science.gov (United States)

    Hoffman, Robert A.

    1980-01-01

    The disclosure relates to resistance only monitoring and calibration in an electrical cell analyzer. Sample and sheath fluid flows of different salinities are utilized, the sample flow being diameter modulated to produce a selected pattern which is compared to the resistance measured across the flows.

  10. Patterns in Soil Electrical Resistivity Across Land Uses in the Calhoun Critical Zone Observatory Landscape

    Science.gov (United States)

    Markewitz, D.; Sutter, L.; Richter, D. D., Jr.

    2017-12-01

    Soil Electrical Resistivity Tomography (ERT) was measured across the Calhoun Critical Zone Observatory in relation to land use cover. ERT can help identify patterns in soil and saprolite physical attributes and moisture content through multiple meters. ERT data were generated with an AGI Supersting R8 with a 28 probe dipole-dipole array on a 1.5 meter spacing providing information through the upper 9 m. In Nov/Dec 2016 ten soil pits were dug to 3m depth in agricultural fields, pine forests, and hardwood forests across the CCZO and ERT measures were taken centered on these pits. ERT values ranged from 200 to 2500 Ohm-m. ERT patterns in the agricultural field demonstrated a limited resistivity gradient (200-700 Ohm-m) appearing moist throughout. In contrast, research areas under pine and hardwood forest had stronger resistivity gradients reflecting both moisture and physical attributes (i.e., texture or rock content). For example, research area 2 under pine had an area of higher resistivity that correlated with a band of saprolite that was readily visible in the exposed profile. In research area 7 and 8 that included both pine and hardwood forest resistivity gradients had contradictory patterns of high to low resistivity from top to bottom. In research area 7 resistivity was highest at the surface and decreased with depth, a common pattern when water table is at depth. In research area 8 the inverse was observed with low resistivity above and resistivity increasing with depth, a pattern observed in upper landscape positions on ridges with moist clay above dry saprolite. ERT patterns did reflect a large difference in the measured agricultural fields compared to forest while other difference appeared to reflect landscape position.

  11. Temperature and mixing effects on electrical resistivity of carbon fiber enhanced concrete

    International Nuclear Information System (INIS)

    Chang, Christiana; Song, Gangbing; Gao, Di; Mo, Y L

    2013-01-01

    In this paper, the effect of temperature and mixing procedure on the electrical resistivity of carbon fiber enhanced concrete is investigated. Different compositions of concrete containing varying concentrations of carbon fiber into normal and self-consolidating concrete (SCC) were tested under DC electrical loading over the temperature range −10 to 20 °C. The electrical resistivity of the bulk samples was calculated and compared against temperature. It was observed that there is an inverse exponential relationship between resistivity and temperature which follows the Arrhenius relationship. The bulk resistivity decreased with increasing fiber concentration, though data from SCC indicates a saturation limit beyond which electrical resistivity begins to drop. The activation energy of the bulk electrically conductive concrete was calculated and compared. While SCC exhibited the lowest observed electrical resistance, the activation energy was similar amongst SCC and surfactant enhanced concrete, both of which were lower than fiber dispersed in normal concrete. (paper)

  12. Electric field measurements in high pressure discharges

    International Nuclear Information System (INIS)

    Mitko, S.V.; Ochkin, V.N.; Serdyuchenko, A.Yu.; Tskhai, S.N.

    2001-01-01

    Electric fields define a wide range of interactions and phenomena at different phases of matter both on micro- and macro-level. Investigation of electric fields behavior provides a key for understanding of these phenomena and their application

  13. Detection of leaks in underground storage tanks using electrical resistance methods: 1996 results

    International Nuclear Information System (INIS)

    Ramirez, A.; Daily, W.

    1996-10-01

    This document provides a summary of a field experiment performed under a 15m diameter steel tank mockup located at the Hanford Reservation, Washington. The purpose of this test was to image a contaminant plume as it develops in soil under a tank already contaminated by previous leakage and to determine whether contaminant plumes can be detected without the benefit of background data. Measurements of electrical resistance were made before and during a salt water release. These measurements were made in soil which contained the remnants of salt water plumes released during previous tests in 1994 and in 1995. About 11,150 liters of saline solution were released along a portion of the tank's edge in 1996. Changes in electrical resistivity due to release of salt water conducted in 1996 were determined in two ways: (1) changes relative to the 1996 pre-spill data, and (2) changes relative to data collected near the middle of the 1996 spill after the release flow rate was increased. In both cases, the observed resistivity changes show clearly defined anomalies caused by the salt water release. These results indicate that when a plume develops over an existing plume and in a geologic environment similar to the test site environment, the resulting resistivity changes are easily detectable. Three dimensional tomographs of the resistivity of the soil under the tank show that the salt water release caused a region of low soil resistivity which can be observed directly without the benefit of comparing the tomograph to tomographs or data collected before the spill started. This means that it may be possible to infer the presence of pre-existing plumes if there is other data showing that the regions of low resistivity are correlated with the presence of contaminated soil. However, this approach does not appear reliable in defining the total extent of the plume due to the confounding effect that natural heterogeneity has on our ability to define the margins of the anomaly

  14. Using Resistivity Measurements to Determine Anisotropy in Soil and Weathered Rock

    Directory of Open Access Journals (Sweden)

    S. Soto-Caban

    2013-08-01

    Full Text Available This study uses electrical resistivity measurements of soils and weathered rock to perform a fast and reliable evaluation of field anisotropy. Two test sites at New Concord, Ohio were used for the study. These sites are characterized by different landform and slightly east dipping limestone and siltstone formations of Pennsylvanian age. The measured resistivity ranged from 19 Ω∙m to 100 ��∙m, and varied with depth, landform, and season. The anisotropy was determined by a comparison of resistance values along the directions of strike and the dip. Measurements showed that the orientation of electrical anisotropy in the shallow ground may vary due to fluid connection, which is determined by the pore geometry in soil and rock, as well as by the direction of fluid movement. Results from this study indicated that a portable electrical resistivity meter is sensitive and reliable enough to be used for shallow ground fluid monitoring.

  15. Loss-resistant unambiguous phase measurement

    OpenAIRE

    Dinani, Hossein T.; Berry, Dominic W.

    2014-01-01

    Entangled multi-photon states have the potential to provide improved measurement accuracy, but are sensitive to photon loss. It is possible to calculate ideal loss-resistant states that maximize the Fisher information, but it is unclear how these could be experimentally generated. Here we propose a set of states that can be obtained by processing the output from parametric down-conversion. Although these states are not optimal, they provide performance very close to that of optimal states for...

  16. Measurement of resistance switching dynamics in copper sulfide memristor structures

    Science.gov (United States)

    McCreery, Kaitlin; Olson, Matthew; Teitsworth, Stephen

    Resistance switching materials are the subject of current research in large part for their potential to enable novel computing devices and architectures such as resistance random access memories and neuromorphic chips. A common feature of memristive structures is the hysteretic switching between high and low resistance states which is induced by the application of a sufficiently large electric field. Here, we describe a relatively simple wet chemistry process to fabricate Cu2 S / Cu memristive structures with Cu2 S film thickness ranging up to 150 micron. In this case, resistance switching is believed to be mediated by electromigration of Cu ions from the Cu substrate into the Cu2 S film. Hysteretic current-voltage curves are measured and reveal switching voltages of about 0.8 Volts with a relatively large variance and independent of film thickness. In order to gain insight into the dynamics and variability of the switching process, we have measured the time-dependent current response to voltage pulses of varying height and duration with a time resolution of 1 ns. The transient response consists of a deterministic RC component as well as stochastically varying abrupt current steps that occur within a few microseconds of the pulse application.

  17. Electric field tomography for contactless imaging of resistivity in biomedical applications.

    Science.gov (United States)

    Korjenevsky, A V

    2004-02-01

    The technique of contactless imaging of resistivity distribution inside conductive objects, which can be applied in medical diagnostics, has been suggested and analyzed. The method exploits the interaction of a high-frequency electric field with a conductive medium. Unlike electrical impedance tomography, no electric current is injected into the medium from outside. The interaction is accompanied with excitation of high-frequency currents and redistribution of free charges inside the medium leading to strong and irregular perturbation of the field's magnitude outside and inside the object. Along with this the considered interaction also leads to small and regular phase shifts of the field in the area surrounding the object. Measuring these phase shifts using a set of electrodes placed around the object enables us to reconstruct the internal structure of the medium. The basics of this technique, which we name electric field tomography (EFT), are described, simple analytical estimations are made and requirements for measuring equipment are formulated. The realizability of the technique is verified by numerical simulations based on the finite elements method. Results of simulation have confirmed initial estimations and show that in the case of EFT even a comparatively simple filtered backprojection algorithm can be used for reconstructing the static resistivity distribution in biological tissues.

  18. Nuclear reactor vessel surface inspecting technique applying electric resistance probe

    International Nuclear Information System (INIS)

    Yamaguchi, T.; Enami, K.; Yoshioka, M.

    1975-01-01

    A new technique for inspecting the inner surface of the PWR type nuclear reactor vessel by use of an electric resistance probe is introduced, centering on a data processing system. This system is composed of a mini-computer, a system typewriter, an interface unit, a D-A converter and controller, and X-Y recorder and others. Its functions are judging flaws and making flaw detection maps. In order to judge flaws by flaw detection signals, three kinds of flaw judging methods have been developed. In case there is a flaw, its position and depth are calculated and listed on the system typewriter. The flaw detection maps are expressed in four kinds of modes and they are displayed on the X-Y recorder. (auth.)

  19. Electrical resistivity tomography at the DOE Hanford site

    International Nuclear Information System (INIS)

    Narbutovskih, S.M.; Halter, T.D.; Sweeney, M.D.; Daily, W.; Ramirez, A.L.

    1996-01-01

    Recent work at the DOE Hanford site has established the potential of applying Electrical Resistivity Tomography (ERT) for early leak detection under hazardous waste storage facilities. Several studies have been concluded to test the capabilities and limitations of ERT for two different applications. First, field experiments have been conducted to determine the utility of ERT to detect and map leaks from underground storage tanks during waste removal processes. Second, the use of ERT for long term vadose zone monitoring has been tested under different field conditions of depth, installation design, acquisition mode/equipment and infiltration chemistry. This work involves transferring the technology from Lawrence Livermore National Laboratory (LLNL) to the Resource Conservation and Recovery Act (RCRA) program at the DOE Hanford Site. This paper covers field training studies relevant to the second application for long term vadose zone monitoring

  20. Reliability of copper based alloys for electric resistance spot welding

    International Nuclear Information System (INIS)

    Jovanovicj, M.; Mihajlovicj, A.; Sherbedzhija, B.

    1977-01-01

    Durability of copper based alloys (B-5 and B-6) for electric resistance spot-welding was examined. The total amount of Be, Ni and Zr was up to 2 and 1 wt.% respectively. Good durability and satisfactory quality of welded spots were obtained in previous laboratory experiments carried out on the fixed spot-welding machine of an industrial type (only B-5 alloy was examined). Electrodes made of both B-5 and B-6 alloy were tested on spot-welding grips and fixed spot-welding machines in Tvornica automobila Sarajevo (TAS). The obtained results suggest that the durability of electrodes made of B-5 and B-6 alloys is more than twice better than of that used in TAS

  1. ENVIRONMENTAL MONITORING OF LEAKS USING TIME LAPSED LONG ELECTRODE ELECTRICAL RESISTIVITY

    International Nuclear Information System (INIS)

    Myers, D.A.; Rucker, D.F.; Fink, J.B.; Loke, M.H.

    2009-01-01

    Highly industrialized areas pose challenges for surface electrical resistivity characterization due to metallic infrastructure. The infrastructure is typically more conductive than the desired targets and will mask the deeper subsurface information. These challenges may be minimized if steel-cased wells are used as long electrodes in the area near the target. We demonstrate a method of using long electrodes to electrically monitor a simulated leak from an underground storage tank with both synthetic examples and a field demonstration. The synthetic examples place a simple target of varying electrical properties beneath a very low resistivity layer. The layer is meant to replicate the effects of infrastructure. Both surface and long electrodes are tested on the synthetic domain. The leak demonstration for the field experiment is simulated by injecting a high conductivity fluid in a perforated well within the S tank farm at Hanford, and the resistivity measurements are made before and after the leak test. All data are processed in four dimensions, where a regularization procedure is applied in both the time and space domains. The synthetic test case shows that the long electrode ERM could detect relative changes in resistivity that are commensurate with the differing target properties. The surface electrodes, on the other hand, had a more difficult time matching the original target's footprint. The field results shows a lowered resistivity feature develop south of the injection site after cessation of the injections. The time lapsed regularization parameter has a strong influence on the differences in inverted resistivity between the pre and post injection datasets, but the interpretation of the target is consistent across all values of the parameter. The long electrode ERM method may provide a tool for near real-time monitoring of leaking underground storage tanks.

  2. Use of small scale electrical resistivity tomography to identify soil-root interactions during deficit irrigation

    Science.gov (United States)

    Vanella, D.; Cassiani, G.; Busato, L.; Boaga, J.; Barbagallo, S.; Binley, A.; Consoli, S.

    2018-01-01

    Plant roots activity affect the exchanges of mass and energy between the soil and atmosphere. However, it is challenging to monitor the activity of the root-zone because roots are not visible from the soil surface, and root systems undergo spatial and temporal variations in response to internal and external conditions. Therefore, measurements of the activity of root systems are interesting to ecohydrologists in general, and are especially important for specific applications, such as irrigation water management. This study demonstrates the use of small scale three-dimensional (3-D) electrical resistivity tomography (ERT) to monitor the root-zone of orange trees irrigated by two different regimes: (i) full rate, in which 100% of the crop evapotranspiration (ETc) is provided; and (ii) partial root-zone drying (PRD), in which 50% of ETc is supplied to alternate sides of the tree. We performed time-lapse 3-D ERT measurements on these trees from 5 June to 24 September 2015, and compared the long-term and short-term changes before, during, and after irrigation events. Given the small changes in soil temperature and pore water electrical conductivity, we interpreted changes of soil electrical resistivity from 3-D ERT data as proxies for changes in soil water content. The ERT results are consistent with measurements of transpiration flux and soil temperature. The changes in electrical resistivity obtained from ERT measurements in this case study indicate that root water uptake (RWU) processes occur at the 0.1 m scale, and highlight the impact of different irrigation schemes.

  3. Resistivity measurements on the neutron irradiated detector grade silicon materials

    Energy Technology Data Exchange (ETDEWEB)

    Li, Zheng

    1993-11-01

    Resistivity measurements under the condition of no or low electrical field (electrical neutral bulk or ENB condition) have been made on various device configurations on detector grade silicon materials after neutron irradiation. Results of the measurements have shown that the ENB resistivity increases with neutron fluence ({Phi}{sub n}) at low {phi}{sub n} (<10{sup 13} n/cm{sup 2}) and saturates at a value between 300 and 400 k{Omega}-cm at {phi}{sub n} {approximately}10{sup 13} n/cm{sup 2}. Meanwhile, the effective doping concentration N{sub eff} in the space charge region (SCR) obtained from the C-V measurements of fully depleted p{sup +}/n silicon junction detectors has been found to increase nearly linearly with {phi}{sub n} at high fluences ({phi}{sub n} > 10{sup 13} n/cm{sup 2}). The experimental results are explained by the deep levels crossing the Fermi level in the SCR and near perfect compensation in the ENB by all deep levels, resulting in N{sub eff} (SCR) {ne} n or p (free carrier concentrations in the ENB).

  4. Electrically resistive coating for remediation (regeneration) of a diesel particulate filter and method

    Science.gov (United States)

    Phelps, Amanda C [Malibu, CA; Kirby, Kevin K [Calabasas Hills, CA; Gregoire, Daniel J [Thousand Oaks, CA

    2012-02-14

    A resistively heated diesel particulate filter (DPF). The resistively heated DPF includes a DPF having an inlet surface and at least one resistive coating on the inlet surface. The at least one resistive coating is configured to substantially maintain its resistance in an operating range of the DPF. The at least one resistive coating has a first terminal and a second terminal for applying electrical power to resistively heat up the at least one resistive coating in order to increase the temperature of the DPF to a regeneration temperature. The at least one resistive coating includes metal and semiconductor constituents.

  5. Electrical Resistivity Technique for Groundwater Exploration in Quaternary Deposit

    Science.gov (United States)

    Aziman, M.; Hazreek, Z. A. M.; Azhar, A. T. S.; Fahmy, K. A.; Faizal, T. B. M.; Sabariah, M.; Ambak, K.; Ismail, M. A. M.

    2018-04-01

    The water security for University Tun Hussein Onn (UTHM) campus was initiated to find alternative sources of water supply. This research began with finding the soil profiles using the geophysical electrical resistivity method across UTHM campus. The resistivity results were calibrated with previous borehole data as well as via groundwater drilling. The drilling work was discovered the groundwater aquifer characterized by the fractured fresh igneous rock at a depth between 43 meter and 55 meter. Further drilling was continued until 100 meter in depth. However, due to not encounter a new rock fractured zone causes the groundwater quantity did not improve even was drilled up to 100 meter depth. In the perspective of water resources, it showed a good potential for water resources for local usages at 104 m3 per day. In addition, the groundwater quality showed the water treatment was required to fulfil the criterion of the national drinking water standards. This study concluded that the first layer of fractured bedrock at UTHM was able to produce significant amounts of groundwater for local consumption usage.

  6. Contribution of 3-D electrical resistivity tomography for landmines detection

    Directory of Open Access Journals (Sweden)

    M. Metwaly

    2008-12-01

    Full Text Available Landmines are a type of inexpensive weapons widely used in the pre-conflicted areas in many countries worldwide. The two main types are the metallic and non-metallic (mostly plastic landmines. They are most commonly investigated by magnetic, ground penetrating radar (GPR, and metal detector (MD techniques. These geophysical techniques however have significant limitations in resolving the non-metallic landmines and wherever the host materials are conductive. In this work, the 3-D electric resistivity tomography (ERT technique is evaluated as an alternative and/or confirmation detection system for both landmine types, which are buried in different soil conditions and at different depths. This can be achieved using the capacitive resistivity imaging system, which does not need direct contact with the ground surface. Synthetic models for each case have been introduced using metallic and non-metallic bodies buried in wet and dry environments. The inversion results using the L1 norm least-squares optimization method tend to produce robust blocky models of the landmine body. The dipole axial and the dipole equatorial arrays tend to have the most favorable geometry by applying dynamic capacitive electrode and they show significant signal strength for data sets with up to 5% noise. Increasing the burial depth relative to the electrode spacing as well as the noise percentage in the resistivity data is crucial in resolving the landmines at different environments. The landmine with dimension and burial depth of one electrode separation unit is over estimated while the spatial resolutions decrease as the burial depth and noise percentage increase.

  7. Evaluating groundwater flow using passive electrical measurements

    Science.gov (United States)

    Voytek, E.; Revil, A.; Singha, K.

    2016-12-01

    Accurate quantification of groundwater flow patterns, both in magnitude and direction, is a necessary component of evaluating any hydrologic system. Groundwater flow patterns are often determined using a dense network of wells or piezometers, which can be limited due to logistical or regulatory constraints. The self-potential (SP) method, a passive geophysical technique that relies on currents generated by water movement through porous materials, is a re-emerging alternative or addition to traditional piezometer networks. Naturally generated currents can be measured as voltage differences at the ground surface using only two electrodes, or a more complex electrode array. While the association between SP measurements and groundwater flow was observed as early as 1890s, the method has seen resurgence in hydrology since the governing equations were refined in the 1980s. The method can be used to analyze hydrologic processes at various temporal and spatial scales. Here we present the results of multiple SP surveys collected a multiple scales (1 to 10s of meters). Here single SP grid surveys are used to evaluate flow patterns through artic hillslopes at a discrete point in time. Additionally, a coupled groundwater and electrical model is used to analyze multiple SP data sets to evaluate seasonal changes in groundwater flow through an alpine meadow.

  8. Electrical resistance, superconductivity and phase transformations of Rb and Cs under high pressure

    International Nuclear Information System (INIS)

    Ullrich, K.

    1980-01-01

    Four lead electrical resistance measurements were performed on Rb under pressures up to 210 kbar for temperatures in the range 0.05 K to 300 K. Pressure was applied using a Bridgman-anvil-configuration with dense sintered diamond in the highly stressed tip regions of the Carboloy pistons. The sample cell was pressurized at room temperature by a mechanical press connected to the mixing chamber of a 3 He- 4 He-cryostat. The pressure remained essentially constant during cooling. Discontinuous changes in resistance at pressures of 70 and 140 kbar indicate two phase transitions and confirm the results of other authors. The resistance of Rb increases after a minimum at 20 kbar by about two orders of magnitude. (orig.) [de

  9. Method and apparatus for remote tube crevice detection by current and voltage probe resistance measurement

    Science.gov (United States)

    Kikta, Thomas J.; Mitchell, Ronald D.

    1992-01-01

    A method and apparatus for determining the extent of contact between an electrically conducting tube and an electrically conductive tubesheet surrounding the tube, based upon the electrical resistance of the tube and tubesheet. A constant current source is applied to the interior of the electrically conducting tube by probes and a voltmeter is connected between other probes to measure the voltage at the point of current injection, which is inversely proportional to the amount of contact between the tube and tubesheet. Namely, the higher the voltage measured by the voltmeter, the less contact between the tube and tubesheet.

  10. Electrical resistivity monitoring of the drift scale test in Yucca Mountain

    International Nuclear Information System (INIS)

    Ramirez, A.

    1997-01-01

    Of the several thermal, mechanical and hydrological measurements being used to monitor the rockmass response, electrical resistance tomography (ERT) is being used to monitor the movement of liquid water with a special interest in the movement of condensate out of the system. Eight boreholes, containing a total of 140 ERT electrodes, were drilled above and below the Heated Drift (HD) to form vertical planes parallel to the drift. In addition, 4 boreholes, containing 60 electrodes, drilled from the Access Observation Drift (AOD) form vertical planes at right angles to the HD. Four ERT surveys, three before and one after heating began, were conducted during the first quarter of FY 98. Tomographic images of absolute electrical resistivity have been calculated using these data and are presented in this report. The report also presents the coordinates of the electrodes used for the ERT surveys. Future reports will include images of electrical resistivity change calculated using data collected before and during the heating episode. The changes to be recovered will then be used in combination with temperature maps of the region to calculate maps of saturation change around the HD

  11. Electrical Resistivity Investigation of Gas Hydrate Distribution in Mississippi Canyon Block 118, Gulf of Mexico

    Energy Technology Data Exchange (ETDEWEB)

    Dunbar, John

    2012-12-31

    Electrical methods offer a geophysical approach for determining the sub-bottom distribution of hydrate in deep marine environments. Methane hydrate is essentially non-conductive. Hence, sediments containing hydrate are more resistive than sediments without hydrates. To date, the controlled source electromagnetic (CSEM) method has been used in marine hydrates studies. This project evaluated an alternative electrical method, direct current resistivity (DCR), for detecting marine hydrates. DCR involves the injection of direct current between two source electrodes and the simultaneous measurement of the electric potential (voltage) between multiple receiver electrodes. The DCR method provides subsurface information comparable to that produced by the CSEM method, but with less sophisticated instrumentation. Because the receivers are simple electrodes, large numbers can be deployed to achieve higher spatial resolution. In this project a prototype seafloor DCR system was developed and used to conduct a reconnaissance survey at a site of known hydrate occurrence in Mississippi Canyon Block 118. The resulting images of sub-bottom resistivities indicate that high-concentration hydrates at the site occur only in the upper 50 m, where deep-seated faults intersect the seafloor. Overall, there was evidence for much less hydrate at the site than previously thought based on available seismic and CSEM data alone.

  12. Electrical, Magnetic, and Optical Measurement Facility

    Data.gov (United States)

    Federal Laboratory Consortium — FUNCTION: Provides tools necessary for electrical, magnetic, and optical characterization of bulk and thin-film materials. This includes the ability to determine the...

  13. Electric Field Measurements At The Magnetopause

    Science.gov (United States)

    Lindqvist, P.-A.; Dunlop, M.

    The quasi-thermal noise (QTN) is due to the thermal motions of the particles, which produce electrostatic fluctuations. This noise is detected by any sensitive receiver at the ports of an electric antenna immersed in a plasma and can be used to measure in-situ the plasma density, temperature and bulk velocity. The basic reason is that this noise can be formally calculated as a function of both the particle velocity distribu- tions and the antenna geometry. So, conversely, the "spectroscopy" of this noise re- veals the local plasma properties. This method is routinely used on various spacecraft (Ulysses, Wind) in the solar wind or in planetary magnetospheres/ionospheres (Image at Earth, Cassini at Venus, Earth and soon at Saturn). This method has the advantage of being relatively immune to spacecraft potential and photoelectrons pertubations, since it senses a large plasma volume. It provides an accurate measurement of the electron density (a few %) because it is based on the detection of the strong signal peak near the local plasma frequency (which is close to a resonance for electrostatic waves). We will show that QTN may be as well adapted to measure 1) magnetized (anisotropic) plasmas (and deduce the magnetic field strength), 2) suprathermal or non-thermal component (as for example a kappa distribution), and 3) a wide range of core temperature, i.e from ~10 eV, as in the solar wind, to rather low temperatures (tron density and temperature for comparison with our models of Mercury/solar wind interaction.

  14. Temperature dependence of the electrical resistivity of amorphous Co80-xErxB20 alloys

    International Nuclear Information System (INIS)

    Touraghe, O.; Khatami, M.; Menny, A.; Lassri, H.; Nouneh, K.

    2008-01-01

    The temperature dependence of the electrical resistivity of amorphous Co 80-x Er x B 20 alloys with x=0, 3.9, 7.5 and 8.6 prepared by melt spinning in pure argon atmosphere was studied. All amorphous alloys investigated here are found to exhibit a resistivity minimum at low temperature. The electrical resistivity exhibits logarithmic temperature dependence below the temperature of resistivity minimum T min . In addition, the resistivity shows quadratic temperature behavior in the interval T min < T<77 K. At high temperature, the electrical resistivity was discussed by the extended Ziman theory. For the whole series of alloys, the composition dependence of the temperature coefficient of electrical resistivity α shows a change in structural short range occurring in the composition range 8-9 at%

  15. Assessment of integrated electrical resistivity data on complex aquifer structures in NE Nuba Mountains - Sudan

    Science.gov (United States)

    Mohamed, N. E.; Yaramanci, U.; Kheiralla, K. M.; Abdelgalil, M. Y.

    2011-07-01

    Two geophysical techniques were integrated to map the groundwater aquifers on complex geological settings, in the crystalline basement terrain in northeast Nuba Mountains. The water flow is structurally controlled by the northwest-southeast extensional faults as one of several in-situ deformational patterns that are attributed to the collision of the Pan-African oceanic assemblage of the Nubian shield against the pre-Pan African continental crust to the west. The structural lineaments and drainage systems have been enhanced by the remote sensing technique. The geophysical techniques used are: vertical electrical soundings (VES) and electrical resistivity tomography (ERT), in addition to hydraulic conductivity measurements. These measurements were designed to overlap in order to improve the producibility of the geophysical data and to provide a better interpretation of the hydrogeological setting of the aquifer complex structure. Smooth and Block inversion schemes were attempted for the observed ERT data to study their reliability in mapping the different geometries in the complex subsurface. The VES data was conducted where ERT survey was not accessible, and inverted smoothly and merged with the ERT in the 3D resistivity grid. The hydraulic conductivity was measured for 42 water samples collected from the distributed dug wells in the study area; where extremely high saline zones were recorded and have been compared to the resistivity values in the 3D model.

  16. Electrical Resistivity Tomography using a finite element based BFGS algorithm with algebraic multigrid preconditioning

    Science.gov (United States)

    Codd, A. L.; Gross, L.

    2018-03-01

    We present a new inversion method for Electrical Resistivity Tomography which, in contrast to established approaches, minimizes the cost function prior to finite element discretization for the unknown electric conductivity and electric potential. Minimization is performed with the Broyden-Fletcher-Goldfarb-Shanno method (BFGS) in an appropriate function space. BFGS is self-preconditioning and avoids construction of the dense Hessian which is the major obstacle to solving large 3-D problems using parallel computers. In addition to the forward problem predicting the measurement from the injected current, the so-called adjoint problem also needs to be solved. For this problem a virtual current is injected through the measurement electrodes and an adjoint electric potential is obtained. The magnitude of the injected virtual current is equal to the misfit at the measurement electrodes. This new approach has the advantage that the solution process of the optimization problem remains independent to the meshes used for discretization and allows for mesh adaptation during inversion. Computation time is reduced by using superposition of pole loads for the forward and adjoint problems. A smoothed aggregation algebraic multigrid (AMG) preconditioned conjugate gradient is applied to construct the potentials for a given electric conductivity estimate and for constructing a first level BFGS preconditioner. Through the additional reuse of AMG operators and coarse grid solvers inversion time for large 3-D problems can be reduced further. We apply our new inversion method to synthetic survey data created by the resistivity profile representing the characteristics of subsurface fluid injection. We further test it on data obtained from a 2-D surface electrode survey on Heron Island, a small tropical island off the east coast of central Queensland, Australia.

  17. Electrical resistivity monitoring of the thermomechanical heater test in Yucca Mountain

    International Nuclear Information System (INIS)

    Ramirez, A.; Daily, W.; Buettner, M.

    1997-01-01

    A test is being conducted in the densely welded Topopah Springs tuff within Yucca Mountain, Nevada to study the thermomechanical and hydrological behavior of this horizon when it is headed. A single 4 kW heater, placed in a horizontal borehole, was turned on August, 1996 and will continue to heat the rockmass until April 1997. Of the several thermal, mechanical and hydrological measurements being used to monitor the rockmass response, electrical resistance tomography (ERT) is being used to monitor the movement of liquid water with a special interest in the movement of condensate out of the system. Four boreholes, containing a total of 30 ERT electrodes, were drilled to form the sides of a 30 foot square with the heater at the center and perpendicular to the plane. Images of resistivity change were calculated using data collected before and during the heating episode. The changes recovered show a region of decreasing resistivity approximately centered around the heater. The size this region grows with time and the resistivity decreases become stronger. The changes in resistivity are caused by both temperature and saturation changes. The observed resistivity changes suggest that the rock adjacent to the heater dries as heating progresses. This dry region is surrounded by a region of increased saturation where steam recondenses and imbibes into the rock

  18. Electrical resistivity monitoring of the thermomechanical heater test in Yucca Mountain

    International Nuclear Information System (INIS)

    Ramirez, A.; Daily, W.; Buettner, M.; LaBrecque, L

    1996-01-01

    A test is being conducted in the densely welded Topopah Springs tuff within Yucca Mountain, Nevada to study the thermomechanical and hydrological behavior of this horizon when it is heated. A single 4 kW heater, placed in a horizontal borehole, was turned on August, 1996 and will continue to heat the rockmass until April 1997. Of the several thermal, mechanical and hydrological measurements being used to monitor the rockmass response, electrical resistance tomography (ERT) is being used to monitor the movement of liquid water with a special interest in the movement of condensate out of the system. Four boreholes, containing a total of 30 ERT electrodes, were drilled to form the sides of a 30 foot square with the heater at the center and perpendicular to the plane. Images of resistivity change were calculated using data collected before and during the heating episode. The changes recovered show a region of decreasing resistivity approximately centered around the heater. The size this region grows with time and -the resistivity decreases become stronger. The changes in resistivity are caused by both temperature and saturation changes. The observed resistivity changes suggest that the rock adjacent to the heater dries as heating progresses. This dry region is surrounded by a region of increased saturation where steam recondenses and imbibes into the rock

  19. Delineating The Subsurface Structures Using Electrical Resistivity Sounding In Some Part Of Willeton Perth Western Australia

    Directory of Open Access Journals (Sweden)

    Okan Evans Onojasun

    2015-08-01

    Full Text Available Abstract Geophysical survey using electrical resistivity methods has been carried out within the industrial area of Willeton Perth Western Australia with the view to delineate the geoelectric characteristics of the basement complex and evaluate the groundwater potential in the area. Vertical electrical sounding with ABEM SAS 3000 Terrameter and Schlumberger electrode configuration were employed for data acquisition. Apparent resistivity values obtained from the field measurements were plotted against half current electrodes spacing on a log-log graph while a model was suggested to fit the resistivity distribution presented in the sounding. The results from the modelling were finally iterated to the lowest Root Mean Square RMS percentage error using computer software A 7 point filter derived by Guptasarma to calculate a forward model. Analysis of the results showed that the study area has fairly homogenous subsurface stratification with four distinct subsurface layers above the depth of 37m. The four subsurface layers comprises top soil mainly of unconsolidated and sand containing organic matter unsaturated sand layer with consolidated and highly resistive water saturated sand layer with highly water saturated soil and the sub-stratum layer consisting of clay material. The aquifer performance is best at about 32m hence it is suggested that boreholes for sustainable water supply in this area should be drilled to about 32 m to hit prolific aquifer.

  20. A new measure for the strength of electrical synapses

    Directory of Open Access Journals (Sweden)

    Julie S Haas

    2015-09-01

    Full Text Available Electrical synapses, like chemical synapses, mediate intraneuronal communication. Electrical synapses are typically quantified by subthreshold measurements of coupling, which fall short in describing their impact on spiking activity in coupled neighbors. Here we describe a novel measurement for electrical synapse strength that directly evaluates the effect of synaptically transmitted activity on spike timing. This method, also applicable to neurotransmitter-based synapses, communicates the considerable strength of electrical synapses. For electrical synapses measured in rodent slices of the thalamic reticular nucleus, spike timing is modulated by tens of ms by activity in a coupled neighbor.

  1. Electrical measurement of radiation effect in SiC

    Energy Technology Data Exchange (ETDEWEB)

    Kanazawa, Satoshi; Kamiya, Koji; Kanno, Ikuo [Kyoto Univ. (Japan). Faculty of Engineering] [and others

    1996-04-01

    For aiming to limited resources and environmental conservations on the Earth, development of controlling element workable under high temperature environment was investigated so as to establish a high grade and optimum controlling system. In order to observe changes of electrical properties before and after irradiation and after annealing, and to investigate changes of carrier concentration and movability after irradiating neutron from reactor and accelerator for the SiC single crystal wafer, elucidation on neutron irradiation effect of SiC as well as finding an optimum method on nuclear conversion injection were investigated. For this reason, SiC surface was purified by its etching and was treated thermally at 1000degC for about 30 min. under argon gas atmosphere after vacuum depositing nickel on it. And then, it was irradiated neutron using Kyoto University reactor (LTL), Linac and University of Tokyo reactor (YAYOI) to measure changes of resistivity using van der Pauw. As a result, it was found that LTL irradiation data was under investigation of measuring method, that in Linac no meaning change was observed because of low irradiation, and that only YAYOI data showed increase of resistivity. (G.K.)

  2. Temperature dependency of electrical resistivity of soils; Tsuchi no hiteiko no ondo izonsei ni kansuru kenkyu

    Energy Technology Data Exchange (ETDEWEB)

    Park, S; Matsui, T [Osaka University, Osaka (Japan). Faculty of Engineering; Park, M; Fujiwara, H [Osaka University, Osaka (Japan)

    1997-10-22

    Kinds of ground materials, porosity, electrical resistivity of pores, degree of saturation, and content of clays are the factors affecting the electrical resistivity of soils. In addition to these factors, the electrical resistivity of soils around hot spring water and geothermal areas depends on the temperature due to fluctuation of cation mobility in the pore water with the temperature. In this paper, the temperature dependency of electrical resistivity of groundwater and soils is investigated by recognizing that of groundwater as that of pore water. As a result, it was found that the electrical resistivity of groundwater becomes lower as increasing the amount of dissolved cation, and that the temperature dependency of electrical resistivity is not significant because of the small mobility of cation. The electrical resistivity of soils was significantly affected by that of pore water, in which the mobility of cation was changed with temperature changes. Accordingly, the temperature dependency of electrical resistivity of soils has a similar tendency as that of groundwater. 5 refs., 9 figs., 2 tabs.

  3. Electric resistance of nickel and niobium in the temperature range of 300-1300 K

    International Nuclear Information System (INIS)

    Novikov, I.I.; Roshchupkin, V.V.; Mozgovoj, A.G.; Semashko, N.A.

    1982-01-01

    The results of experimental investigation of nickel and niobium electric resistance on the wire samples by the potentiometric method in the temperature range of 300-1300 K are presented. Experimental data processing by the least square method is carried out; approximating equations of temperature dependence of the nickel and niobium electric resistance are prepared

  4. Pressure and temperature induced electrical resistance change in nano-carbon/epoxy composites

    NARCIS (Netherlands)

    Shen, J. T.; Buschhorn, S. T.; De Hosson, J. Th. M.; Schulte, K.; Fiedler, B.

    2015-01-01

    In this study, we investigate the changes of electrical resistance of the carbon black (CB) and carbon nanotube (CNT) filled epoxy composites upon compression, swelling and temperature variation. For all samples we observe a decrease of electrical resistance under compression, while an increase of

  5. Procedures for measuring the electrical properties of superconductors for accelerator magnets

    International Nuclear Information System (INIS)

    Sampson, W.B.

    1986-01-01

    There are three important electrical properties associated with the superconductor used to fabricate accelerator magnets. The most important is the critical current since this determines the performance potential of the magnet. The normal state resistivity and the volume magnetization are the other principal electrical parameters. In this report methods for measuring these parameters are presented and procedures for including self field effect and magnetoresistance are discussed

  6. Characterizing root system characteristics with Electrical resistivity Tomography: a virtual rhizotron simulation

    Science.gov (United States)

    Rao, Sathyanarayan; Ehosioke, Solomon; Lesparre, Nolwenn; Nguyen, Frédéric; Javaux, Mathieu

    2017-04-01

    Electrical Resistivity Tomography (ERT) is more and more used for monitoring soil water content in a cropped soil. Yet, the impact of roots on the signal is often neglected and a topic of controversy. In several studies related to soil-root system, it has been showed that the measured root mass density statistically correlates with the electrical conductivity (EC) data obtained from ERT. In addition, some studies suggest that some roots are more electrically conductive than soil for most water content. Thus, higher EC of roots suggest that it might have a measurable impact on ERT signals. In this work, virtual rhizotrons are simulated using the software package called R-SWMS that solves water and solute transport in plant root-soil system, including root growth. The distribution of water content obtained from R-SWMS simulation is converted into EC data using pedo-physical models. The electrical properties of roots and rhizosphere are explicitly included in the EC data to form a conductivity map (CM) with a very detailed spatial resolution. Forward ERT simulations is then carried out for CM generated for various root architectures and soil conditions to study the impact of roots on ERT forward (current and voltage patterns) and inverse solutions. It is demonstrated that under typical injection schemes with lateral electrodes, root system is hardly measurable. However, it is showed that adding electrodes and constraints on the ERT inversion based on root architecture help quantifying root system mass and extent.

  7. Substructure and electrical resistivity analyses of pure tungsten sheet

    International Nuclear Information System (INIS)

    Trybus, C.L.; Sellers, C.H.; Anderl, R.A.

    1991-01-01

    The substructure of pure tungsten sheet (0.025 mm thick) is examined and quantified by transmission electron microscopy (TEM). Dislocation populations and arrangements are evaluated for as-worked and various annealed conditions of the tungsten sheet. The worked (rolled) tungsten substructure was nonhomogeneous, consisting of areas of very high and low dislocation densities. These results are correlated to resistivity measurements of the tungsten sheet following thermal cycling to 1200 degrees C to determine the substructural changes as a function of temperature. The comparison between the two characterization techniques is used to examine the relationship between structural and electronic properties in tungsten. 15 refs., 6 figs., 2 tabs

  8. Imaging pathways in fractured rock using three-dimensional electrical resistivity tomography

    Science.gov (United States)

    Robinson, Judith; Slater, Lee; Johnson, Timothy B.; Shapiro, Allen M.; Tiedeman, Claire; Ntlargiannis, Dimitrios; Johnson, Carole D.; Day-Lewis, Frederick D.; Lacombe, Pierre; Imbrigiotta, Thomas; Lane, John W.

    2016-01-01

    Major challenges exist in delineating bedrock fracture zones because these cause abrupt changes in geological and hydrogeological properties over small distances. Borehole observations cannot sufficiently capture heterogeneity in these systems. Geophysical techniques offer the potential to image properties and processes in between boreholes. We used three-dimensional cross borehole electrical resistivity tomography (ERT) in a 9 m (diameter) × 15 m well field to capture high-resolution flow and transport processes in a fractured mudstone contaminated by chlorinated solvents, primarily trichloroethylene. Conductive (sodium bromide) and resistive (deionized water) injections were monitored in seven boreholes. Electrode arrays with isolation packers and fluid sampling ports were designed to enable acquisition of ERT measurements during pulsed tracer injections. Fracture zone locations and hydraulic pathways inferred from hydraulic head drawdown data were compared with electrical conductivity distributions from ERT measurements. Static ERT imaging has limited resolution to decipher individual fractures; however, these images showed alternating conductive and resistive zones, consistent with alternating laminated and massive mudstone units at the site. Tracer evolution and migration was clearly revealed in time-lapse ERT images and supported by in situ borehole vertical apparent conductivity profiles collected during the pulsed tracer test. While water samples provided important local information at the extraction borehole, ERT delineated tracer migration over spatial scales capturing the primary hydrogeological heterogeneity controlling flow and transport. The fate of these tracer injections at this scale could not have been quantified using borehole logging and/or borehole sampling methods alone.

  9. Analysis of Printing Substrate, Ink Age and Number of IR Drying Influence on Electrical Resistance of Conductive Inks

    Directory of Open Access Journals (Sweden)

    Josip Jerić

    2015-05-01

    Full Text Available As a result of availability of new technologies, functional printing as a segment has become one of the most interesting directions of research and development in graphic technology. Conductive inks are not a novelty and they already have broad possibilities in production of everyday products. There is still a big market for the broadening of their use, as well as a possibility of further enhancing their properties. This paper analyzes the influence of printing substrate, age of ink and the number of IR drying on the electrical resistance of the conductive inks. In the paper, subject of analysis was the change of electrical resistance in the line that was 9 cm long and 10 typographic points wide. The semi-automated screen-printing machine was used for printing. Three types of printing substrates were used; uncoated, coated and recycled paper. Two types of inks were used; newly opened ink and ink that was out of date for half year. After the printing, prints were dried using the IR dryer. Prints were dried once, and then additional three times. After the first and last drying, multimeter was used to measure electrical resistance of the lines. Analysis of the data shows that the older ink produces prints with higher electrical resistance. There are also notable differences in the electrical resistance based on the printing substrate.

  10. Loss-resistant unambiguous phase measurement

    Science.gov (United States)

    Dinani, Hossein T.; Berry, Dominic W.

    2014-08-01

    Entangled multiphoton states have the potential to provide improved measurement accuracy, but are sensitive to photon loss. It is possible to calculate ideal loss-resistant states that maximize the Fisher information, but it is unclear how these could be experimentally generated. Here we propose a set of states that can be obtained by processing the output from parametric down-conversion. Although these states are not optimal, they provide performance very close to that of optimal states for a range of parameters. Moreover, we show how to use sequences of such states in order to obtain an unambiguous phase measurement that beats the standard quantum limit. We consider the optimization of parameters in order to minimize the final phase variance, and find that the optimum parameters are different from those that maximize the Fisher information.

  11. The `L' Array, a method to model 3D Electrical Resistivity Tomography (ERT) data

    Science.gov (United States)

    Chavez Segura, R. E.; Chavez-Hernandez, G.; Delgado, C.; Tejero-Andrade, A.

    2010-12-01

    The electrical resistivity tomography (ERT) is a method designed to calculate the distribution of apparent electrical resistivities in the subsoil by means of a great number of observations with the aim of determining an electrical image displaying the distribution of true resistivities in the subsoil. Such process can be carried out to define 2D or 3D models of the subsurface. For a 3D ERT, usually, the electrodes are placed in a squared grid keeping the distance between adjacent electrodes constant in the x and y directions. Another design employed, consists of a series of parallel lines whose space inter-lines must be smaller or equal to four times the electrode separation. The most common electrode arrays frequently employed for this type of studies are the pole-pole, pole-dipole and dipole-dipole. Unfortunately, ERT surface sampling schemes are limited by physical conditions or obstacles, like buildings, highly populated urban zones, and geologic/topographic features, where the lines of electrodes cannot be set. However, it is always necessary to characterize the subsoil beneath such anthropogenic or natural features. The ‘L’ shaped array has the main purpose to overcome such difficulties by surrounding the study area with a square of electrode lines. The measurements are obtained by switching automatically current and potential electrodes from one line to the other. Each observation adds a level of information, from one profile to the other. Once the total levels of data are completed, the opposite ‘L’ array can be measured following the same process. The complete square is computed after the parallel profiles are observed as well. At the end, the computed resistivities are combined to form a 3D matrix of observations. Such set of data can be inverted to obtain the true resistivity distribution at depth in the form of a working cube, which can be interpreted. The method was tested with theoretical models, which included a set of two resistive cubes

  12. Measurement of electric potential distribution in dielectrics

    Energy Technology Data Exchange (ETDEWEB)

    Veretel' nik, V I; Dergozubov, K A; Evdokimov, O B; Shevelev, G E [Tomskij Politekhnicheskij Inst. (USSR). Nauchno-Issledovatel' skij Inst. Ehlektronnoj Introskopii

    1976-05-01

    A radiation method of potential probing in a substance is described. The method is based upon the influence of the electric field upon the emission of secondary electrons expelled by ..gamma..-irradiation from the studied sample.

  13. Evaluation of the measurement uncertainty when measuring the resistance of solid isolating materials to tracking

    Science.gov (United States)

    Stare, E.; Beges, G.; Drnovsek, J.

    2006-07-01

    This paper presents the results of research into the measurement of the resistance of solid isolating materials to tracking. Two types of tracking were investigated: the proof tracking index (PTI) and the comparative tracking index (CTI). Evaluation of the measurement uncertainty in a case study was performed using a test method in accordance with the IEC 60112 standard. In the scope of the tests performed here, this particular test method was used to ensure the safety of electrical appliances. According to the EN ISO/IEC 17025 standard (EN ISO/IEC 17025), in the process of conformity assessment, the evaluation of the measurement uncertainty of the test method should be carried out. In the present article, possible influential parameters that are in accordance with the third and fourth editions of the standard IEC 60112 are discussed. The differences, ambiguities or lack of guidance referring to both editions of the standard are described in the article 'Ambiguities in technical standards—case study IEC 60112—measuring the resistance of solid isolating materials to tracking' (submitted for publication). Several hundred measurements were taken in the present experiments in order to form the basis for the results and conclusions presented. A specific problem of the test (according to the IEC 60112 standard) is the great variety of influential physical parameters (mechanical, electrical, chemical, etc) that can affect the results. At the end of the present article therefore, there is a histogram containing information on the contributions to the measurement uncertainty.

  14. Electric field measurements in a xenon discharge using Spark spectroscopy

    NARCIS (Netherlands)

    Wagenaars, E.; Bowden, M.D.; Kroesen, G.M.W.

    2005-01-01

    Measurements of electric field distributions in a low-pressure xenon discharge are presented. The measurement technique is based on Stark spectroscopy, using a 2 + 1 excitation scheme with fluorescence dip detection. Electric fields can be measured by detecting Stark shifts of high-lying Rydberg

  15. Characterization of electrical resistivity as a function of temperature in the Mo-Si-B system

    International Nuclear Information System (INIS)

    Beckman, Sarah E.

    1999-01-01

    Measurements of electrical resistivity as a function of temperature from 25 to 1,500 C were conducted on polycrystalline samples in the Mo-Si-B system. Single phase, or nearly single phase, samples were prepared for the following phases: Mo 3 Si, Mo 5 SiB 2 , Mo 5 Si 3 B x , MoB, MoSi 2 , and Mo 5 Si 3 . Thesis materials all exhibit resistivity values within a narrow range(4--22 x 10 -7 Omega-m), and the low magnitude suggests these materials are semi-metals or low density of states metals. With the exception of MoSi 2 , all single phase materials in this study were also found to have low temperature coefficient of resistivity(TCR) values. These values ranged from 2.10 x 10 -10 to 4.74 x 10 -10 Omega-m/degree C, and MoSi 2 had a TCR of 13.77 x 10 -10 Omega-m/degree C. The results from the single phase sample measurements were employed in a natural log rule-of-mixtures model to relate the individual phase resistivity values to those of multiphase composites. Three Mo-Si-B phase regions were analyzed: the binary Mo 5 Si 3 -MoSi 2 system, the ternary phase field Mo 5 Si 3 B x MoB-MoSi 2 , and the Mo 3 Si-Mo 5 SiB 2 -Mo 5 Si 3 B x ternary region. The experimental data for samples in each of these regions agreed with the natural log model and illustrated that this model can predict the electrical resistivity as a function of temperature of multi-phase, sintered samples within an error of one standard deviation

  16. Effect of heat treatment on the electrical resistance of photoresist as related to radioisotopic thermoelectric generator aging

    International Nuclear Information System (INIS)

    Johnson, R.T. Jr.

    1979-03-01

    Photoresist is used in electrical contact definition and processing in radioisotopic thermoelectric generators. Inadequate removal of material during processing could lead to electrical shorting when exposed to the high temperature use environment. This effect has been simulated through studies of the electrical resistance of thin layers of photoresist (Kodak Metal Etch Resist) on glass (Corning 7052) with tungsten electrodes. Results show that both the photoresist and the glass contribute to the resistance. The glass resistance decreases with increasing temperature and becomes significant at high temperatures. Annealing studies on the photoresist show that the resistance of the photoresist decreases by over five orders of magnitude upon annealing to 500 0 C, with a corresponding decrease in activation energy from 0.27 eV (350 0 C anneal) to 0.10 eV (500 0 C anneal). Time dependent decreases in resistance of the photoresist were also measured for up to 8 to 9 days during high temperature anneals. Some electrolytic transport of tungsten may occur through the photoresist at high temperatures. Results are compared with data on thermoelectric generators and show that photoresist could cause the electrical aging (voltage degradation) problem observed in some generators

  17. Electrical resistance tomography using steel cased boreholes as long electrodes

    International Nuclear Information System (INIS)

    Daily, W; Newmark, R L; Ramirez, A

    1999-01-01

    Electrical resistance tomography (ERT) using multiple electrodes installed in boreholes has been shown to be useful for both site characterization and process monitoring. In some cases, however, installing multiple downhole electrodes is too costly (e.g., deep targets) or risky (e.g., contaminated sites). For these cases we have examined the possibility of using the steel casings of existing boreholes as electrodes. Several possibilities can be considered. The first case we investigated uses an array of steel casings as electrodes. This results in very few data and thus requires additional constraints to limit the domain of possible inverse solutions. Simulations indicate that the spatial resolution and sensitivity are understandably low but it is possible to coarsely map the lateral extent of subsurface processes such as steam floods. The second case uses an array of traditional point borehole electrodes combined with long-conductor electrodes (steel casings). Although this arrangement provides more data, in many cases it results in poor reconstructions of test targets. Results indicate that this method may hold promise for low resolution imaging where steel casings can be used as electrodes but the merits depend strongly on details of each application. Field tests using these configurations are currently being conducted

  18. Sinkhole detection using electrical resistivity tomography in Saudi Arabia

    International Nuclear Information System (INIS)

    Youssef, Ahmed M; Zabramawi, Yasser A; El-Kaliouby, Hesham

    2012-01-01

    Karst phenomena exist in different areas in the Kingdom of Saudi Arabia, causing serious environmental problems that affect urban development and infrastructure (buildings, roads and highways). One of the most important problems are sinkholes, which most of the time consist of unfilled voids. These sinkholes are formed as a result of the chemical leaching of carbonate and evaporite formations by percolating water. Field investigations show that there are many surface expressions of sinkholes in the area; some appear on the ground surface and others are hidden in the subsurface. Geophysical data were collected at the study area using two-dimensional electrical resistivity tomography (ERT) with different electrode spacings to delineate buried sinkholes and associated subsurface cavities. Our findings indicated that the dipole–dipole method using an electrode spacing of 1 m was successful in detecting a known subsurface sinkhole. According to the ERT method the detected sinkhole depth ranges from 2 to 4 m, its height ranges from 2 to 4 m, and its width ranges from 5 to 7 m. Field observation has verified the geophysical data, especially along the profile A-A. Finally, closely spaced ERT profiles were successful in determining the three-dimensional volume of the subsurface sinkhole. (paper)

  19. Electrical resistance tomography using steel cased boreholes as electrodes

    International Nuclear Information System (INIS)

    Newmark, R L; Daily, W; Ramirez, A

    1999-01-01

    Electrical resistance tomography (ERT) using multiple electrodes installed in boreholes has been shown to be useful for both site characterization and process monitoring. In some cases, however, installing multiple downhole electrodes is too costly (e.g., deep targets) or risky (e.g., contaminated sites). For these cases we have examined the possibility of using the steel casings of existing boreholes as electrodes. The first case we investigated used an array of steel casings as electrodes. This results in very few data and thus requires additional constraints to limit the domain of possible inverse solutions. Simulations indicate that the spatial resolution and sensitivity are understandably low but it is possible to coarsely map the lateral extent of subsurface processes such as steam floods. A hybrid case uses traditional point electrode arrays combined with long-conductor electrodes (steel casings). Although this arrangement provides more data, in many cases it results in poor reconstructions of test targets. Results indicate that this method may hold promise for low resolution imaging where steel casings can be used as electrodes

  20. Applicability of electrical resistance tomography to rectangular vessels

    International Nuclear Information System (INIS)

    Ichijo, Noriaki; Matsuno, Shinsuke; Tokura, Susumu; Tochigi, Yoshikatsu; Misumi, Ryuta; Nishi, Kazuhiko; Kaminoyama, Meguru

    2012-01-01

    To ensure a stable operation of Joule-heated glass melters, it is necessary to observe the distribution of platinum group metal particles (noble metals) in molten glass. Electrical resistance tomography (ERT) has a potential to visualize the inside of the melter section because it can be applied at severe conditions such as high temperature and radioactive fields. Due to designing limitations, it is difficult to install electrodes on the wall of the glass melter. In addition, ERT is hardly applied to a rectangular section. To solve these problems, numerical and experimental studies have been implemented. To apply the ERT method, 8 electrodes are inserted from the top of the melter and set near the bottom to visualize the accumulation of noble metals on the bottom area. As a result of the numerical simulation and the experiment, it was clarified that the ERT can be applied to the rectangular vessel by inserting electrodes from the top of the vessel and has a potential to observe the accumulation of noble metals. (author)

  1. Delineation of a volcanic ash body using electrical resistivity profiling

    International Nuclear Information System (INIS)

    Xia, Jianghai; Ludvigson, Greg; Miller, Richard D; Mayer, Lindsay; Haj, Adel

    2010-01-01

    Four lines of electrical resistivity profiling (ERP) were performed to define the extent of a shallow Quaternary volcanic ash deposit being mined in the United States. Inversion results of ERP proved suitable for defining the thickness and lateral extent of the volcanic ash deposit at this testing site. These interpretations were confirmed by shallow borehole drilling. The model sensitivity information indicates that inverted models possess sufficient resolving power down to a depth of 7 m and are fairly consistent in terms of horizontal resolution along the four ERP lines. The bottom of most of the volcanic ash deposit in the study area is less than 7 m in depth. Based on synthesis of the ERP and drill information, the limits of the mineable ash bed resources were clearly defined. Moreover, by integrating the ERP results with a minimal number of optimally placed borings, the volume of the volcanic ash deposit was established at a lesser cost, and with greater accuracy than would be possible with a traditionally designed grid drilling programme

  2. Application of Electrical Resistivity Method (ERM) in Groundwater Exploration

    Science.gov (United States)

    Izzaty Riwayat, Akhtar; Nazri, Mohd Ariff Ahmad; Hazreek Zainal Abidin, Mohd

    2018-04-01

    The geophysical method which dominant by geophysicists become one of most popular method applied by engineers in civil engineering fields. Electrical Resistivity Method (ERM) is one of geophysical tool that offer very attractive technique for subsurface profile characterization in larger area. Applicable alternative technique in groundwater exploration such as ERM which complement with existing conventional method may produce comprehensive and convincing output thus effective in terms of cost, time, data coverage and sustainable. ERM has been applied by various application in groundwater exploration. Over the years, conventional method such as excavation and test boring are the tools used to obtain information of earth layer especially during site investigation. There are several problems regarding the application of conventional technique as it only provides information at actual drilling point only. This review paper was carried out to expose the application of ERM in groundwater exploration. Results from ERM could be additional information to respective expert for their problem solving such as the information on groundwater pollution, leachate, underground and source of water supply.

  3. Geophysical methods in protected environments. Electrical resistivity tomography

    International Nuclear Information System (INIS)

    Rubio Sánchez-Aguililla, F.M.; Ramiro-Camacho, A.; Ibarra Torre, P.

    2017-01-01

    There is a strong interest in protecting the environment with the aim of its long term preservation. Sometimes the heritage value of these natural areas is related to their biodiversity as there are restricted ecosystems that depend directly on them. In other cases there a singular geological record might exist, essential for the understanding of certain processes affecting the planet, such as volcanic events or glacial periods. To achieve the protection and conservation of these areas it is necessary to generate knowledge about the distribution of geological materials and groundwater masses, to study the parameters that dominate the behaviour of these systems and then define those elements that require special protection or attention. In these protected environments, research methods with a minimal environmental impact should be used. Therefore, indirect methods, such as geophysical techniques, are reliable and complementary tools with a minimum environmental impact and are therefore useful for research these unique areas. The IGME has conducted several geophysical surveys in different protected environments in Spain with the aim of achieving a better understanding, and thus facilitate their preservation and exploitation in a sustainable manner. In this paper we present a review of some case studies where geophysical methods have been used. In all the cases electrical resistivity tomography has been the axis of the geophysical research and stands out due to its great effectiveness. The main objective of this communication is to divulgate and increase awareness of the important role that these geophysical methods can play in the sustainable study of these unique places. [es

  4. Mathematical modeling for corrosion environment estimation based on concrete resistivity measurement directly above reinforcement

    International Nuclear Information System (INIS)

    Lim, Young-Chul; Lee, Han-Seung; Noguchi, Takafumi

    2009-01-01

    This study aims to formulate a resistivity model whereby the concrete resistivity expressing the environment of steel reinforcement can be directly estimated and evaluated based on measurement immediately above reinforcement as a method of evaluating corrosion deterioration in reinforced concrete structures. It also aims to provide a theoretical ground for the feasibility of durability evaluation by electric non-destructive techniques with no need for chipping of cover concrete. This Resistivity Estimation Model (REM), which is a mathematical model using the mirror method, combines conventional four-electrode measurement of resistivity with geometric parameters including cover depth, bar diameter, and electrode intervals. This model was verified by estimation using this model at areas directly above reinforcement and resistivity measurement at areas unaffected by reinforcement in regard to the assessment of the concrete resistivity. Both results strongly correlated, proving the validity of this model. It is expected to be applicable to laboratory study and field diagnosis regarding reinforcement corrosion. (author)

  5. Recovery of electrical resistance in copper films on polyethylene terephthalate subjected to a tensile strain

    International Nuclear Information System (INIS)

    Glushko, O.; Marx, V.M.; Kirchlechner, C.; Zizak, I.; Cordill, M.J.

    2014-01-01

    Substantial recovery (decrease) of electrical resistance during and after unloading is demonstrated for copper films on polyethylene terephthalate substrates subjected to a tensile strain with different peak values. Particularly, the films strained to 5% exhibit full resistance recovery after unloading despite clearly visible plastic deformation of the film. The recovery of electrical resistance in connection with the mechanical behavior of film/substrate couple is discussed with the help of in situ scanning electron microscopy and X-ray diffraction analysis. - Highlights: • Tensile tests on 200 nm Cu films on PET substrate are performed. • Electrical resistance is recorded in-situ during loading and unloading. • Significant recovery (decrease) of resistance is observed during and after unloading. • Films strained to 5% demonstrate full resistance recovery. • Viscoelastic relaxation of PET is responsible for recovery of Cu film resistance

  6. Use of electrical resistivity to detect underground mine voids in Ohio

    Science.gov (United States)

    Sheets, Rodney A.

    2002-01-01

    Electrical resistivity surveys were completed at two sites along State Route 32 in Jackson and Vinton Counties, Ohio. The surveys were done to determine whether the electrical resistivity method could identify areas where coal was mined, leaving air- or water-filled voids. These voids can be local sources of potable water or acid mine drainage. They could also result in potentially dangerous collapse of roads or buildings that overlie the voids. The resistivity response of air- or water-filled voids compared to the surrounding bedrock may allow electrical resistivity surveys to delineate areas underlain by such voids. Surface deformation along State Route 32 in Jackson County led to a site investigation, which included electrical resistivity surveys. Several highly resistive areas were identified using axial dipole-dipole and Wenner resistivity surveys. Subsequent drilling and excavation led to the discovery of several air-filled abandoned underground mine tunnels. A site along State Route 32 in Vinton County, Ohio, was drilled as part of a mining permit application process. A mine void under the highway was instrumented with a pressure transducer to monitor water levels. During a period of high water level, electrical resistivity surveys were completed. The electrical response was dominated by a thin, low-resistivity layer of iron ore above where the coal was mined out. Nearby overhead powerlines also affected the results.

  7. Changes in electrical transport and density of states of phase change materials upon resistance drift

    International Nuclear Information System (INIS)

    Krebs, Daniel; Bachmann, Tobias; Jonnalagadda, Prasad; Dellmann, Laurent; Raoux, Simone

    2014-01-01

    Phase-change memory technology has become more mature in recent years. But some fundamental problems linked to the electrical transport properties in the amorphous phase of phase-change materials still need to be solved. The increase of resistance over time, called resistance drift, for example, poses a major challenge for the implementation of multilevel storage, which will eventually be necessary to remain competitive in terms of high storage densities. To link structural properties with electrical transport, a broader knowledge of (i) changes in the density of states (DoS) upon structural relaxation and (ii) the influence of defects on electrical transport is required. In this paper, we present temperature-dependent conductivity and photo-conductivity measurements on the archetype phase change material GeTe. It is shown that trap-limited band transport at high temperatures (above 165 K) and variable range hopping at low temperatures are the predominating transport mechanism. Based on measurements of the temperature dependence of the optical band gap, modulated photo-conductivity and photo-thermal deflection spectroscopy, a DoS model for GeTe was proposed. Using this DoS, the temperature dependence of conductivity and photo-conductivity has been simulated. Our work shows how changes in the DoS (band gap and defect distributions) will affect the electrical transport before and after temperature-accelerated drift. The decrease in conductivity upon annealing can be explained entirely by an increase of the band gap by about 12%. However, low-temperature photo-conductivity measurements revealed that a change in the defect density may also play a role

  8. Decreasing electrical resistivity of silver along the melting boundary up to 5 GPa

    Science.gov (United States)

    Littleton, Joshua A. H.; Secco, Richard A.; Yong, Wenjun

    2018-04-01

    The electrical resistivity of Ag was experimentally measured at high pressures up to 5 GPa and at temperatures up to ∼300 K above melting. The resistivity decreased as a function of pressure and increased as a function of temperature as expected and is in very good agreement with 1 atm data. Observed melting temperatures at high pressures also agree well with previous experimental and theoretical studies. The main finding of this study is that resistivity of Ag decreases along the pressure- and temperature-dependent melting boundary, in conflict with prediction of resistivity invariance. This result is discussed in terms of the dominant contribution of the increasing energy separation between the Fermi level and 4d-band as a function of pressure. Calculated from the resistivity using the Wiedemann-Franz law, the electronic thermal conductivity increased as a function of pressure and decreased as a function of temperature as expected. The decrease in the high pressure thermal conductivity in the liquid phase as a function of temperature contrasts with the behavior of the 1 atm data.

  9. An electrical resistivity monitor for the detection of composition changes in Pb-17Li

    International Nuclear Information System (INIS)

    Hubberstey, P.; Barker, M.G.; Sample, T.

    1991-01-01

    An electrical resistivity monitor for the detection of composition changes in the lithium-lead eutectic alloy, Pb-17Li, has been developed. A miniature electromagnetic pump is used to sample alloy continuously from a pool or loop system and force it through a capillary section, within which the necessary resistance measurements are made, prior to its return to the bulk source. To calibrate the monitor, detailed resistivity-temperature and resistivity-composition data have been determined for Pb-Li alloys at temperatures from 600 to 800K and compositions from 0 to 20.5 at% Li. The resistivity increases with both temperature and composition; for Pb-17li at 723 K, dρ/dT=0.054x10 -8 ΩmK -1 , and dρ/d[Li]=1.27x10 -8 Ωm(at% Li) -1 . The sensitivity of the monitor is such that changes in composition of as little as ±0.05 at% Li can be detected and its response time is limited soley by the rate of sampling. (orig.)

  10. Electrical resistivity monitoring of the single heater test in Yucca Mountain

    International Nuclear Information System (INIS)

    Ramirez, A.

    1997-10-01

    Of the several thermal, mechanical and hydrological measurements being used to monitor the rockmass response in the Single Heater Test, electrical resistance tomography (ERT) is being used to monitor the movement of liquid water with a special interest in the movement of condensate out of the system. Images of resistivity change were calculated using data collected before, during and after the heating episode. This report will concentrate on the results obtained after heating ceased; previous reports discuss the results obtained during the heating phase. The changes recovered show a region of increasing resistivity approximately centered around the heater as the rock mass cooled. The size of this region grows with time and the resistivity increases become stronger. The increases in resistivity are caused by both temperature and saturation changes. The Waxman Smits model has been used to calculate rock saturation after accounting for temperature effects. The saturation estimates suggest that during the heating phase, a region of drying forms around the heater. During the cooling phase, the dry region has remained relatively stable. Wetter rock regions which developed below the heater during the heating phase, are slowly becoming smaller in size during the cooling phase. The last set of images indicate that some rewetting of the dry zone may be occurring. The accuracy of the saturation estimates depends on several factors that are only partly understood

  11. Ion implantation to improve mechanical and electrical properties of resistive materials based on ruthenium dioxide

    International Nuclear Information System (INIS)

    Byeli, A.V.; Shykh, S.K.; Beresina, V.P.

    1996-01-01

    This paper reports the influence of ion implantation, using different chemical species, on the surface micromorphology, wear resistance, coefficient of friction and electrical resistivity, and its variation during friction for resistive materials based on ruthenium dioxide. It is demonstrated that nitrogen and hydrogen ions are the most effective for modifying surface properties. (Author)

  12. Electric power: liberalization in half-measure

    International Nuclear Information System (INIS)

    Pradel, P.

    1996-01-01

    The European directive about the electric power liberalization concerns only big consumers. These manufacturers have privileged relations with E.D.F. for long years with a very attractive price for the kilowatt hour. The change should not be very important, only more transparency in accounts and change in tariffs of power transmission: for example, a small electric power producer will be authorized to contest the buying price that E.D.F. imposes to him to transport the energy he produces. (N.C.)

  13. Measurement of electric fields in the H-1NF heliac

    International Nuclear Information System (INIS)

    James, B.W.; Howard, J.

    1999-01-01

    There are a number of laser induced fluorescence techniques which can be used to measure internal plasma electric fields. It is planned to use a technique based on Stark mixing of energy levels in a supersonic beam containing metastable helium atoms to measure radial electric fields in H-1NF. Enhanced values of radial electric field are associated with improved confinement modes in H-1NF and other magnetically confined plasmas

  14. Electrical Resistivity Imaging of Seawater Intrusion into the Monterey Bay Aquifer System.

    Science.gov (United States)

    Pidlisecky, A; Moran, T; Hansen, B; Knight, R

    2016-03-01

    We use electrical resistivity tomography to obtain a 6.8-km electrical resistivity image to a depth of approximately 150 m.b.s.l. along the coast of Monterey Bay. The resulting image is used to determine the subsurface distribution of saltwater- and freshwater-saturated sediments and the geologic controls on fluid distributions in the region. Data acquisition took place over two field seasons in 2011 and 2012. To maximize our ability to image both vertical and horizontal variations in the subsurface, a combination of dipole-dipole, Wenner, Wenner-gamma, and gradient measurements were made, resulting in a large final dataset of approximately 139,000 data points. The resulting resistivity section extends to a depth of 150 m.b.s.l., and is used, in conjunction with the gamma logs from four coastal monitoring wells to identify four dominant lithologic units. From these data, we are able to infer the existence of a contiguous clay layer in the southern portion of our transect, which prevents downward migration of the saltwater observed in the upper 25 m of the subsurface to the underlying freshwater aquifer. The saltwater and brackish water in the northern portion of the transect introduce the potential for seawater intrusion into the hydraulically connected freshwater aquifer to the south, not just from the ocean, but also laterally from north to south. © 2015, National Ground Water Association.

  15. Electrical resistivity, optical and magnetic properties of the layered oxyselenide SmCuOSe

    International Nuclear Information System (INIS)

    Llanos, Jaime; Pena, Octavio

    2005-01-01

    The electrical and magnetic properties of the tetragonal phase SmCuOSe are reported as a function of the temperature. The optical properties were studied by means of diffuse reflectance spectrum in the UV-Vis range. The electrical resistivity measurements as well as diffuse reflectance spectrum show that SmCuOSe is a semiconductor with an optical band gap (E g ) of 2.6eV. In this phase, Cu is at its monovalent oxidation state and, as such, it does not contribute to the total magnetic moment, whereas Sm is in its 3+ oxidation state, with a large VanVleck contribution due to the admixture of the fundamental state with higher energy levels

  16. Geological and Electrical Resistivity Sounding of Olokonla Area in ...

    African Journals Online (AJOL)

    Akorede

    form prefential pathways for ground water. Three vertical electrical ... investigation techniques which use the electrical properties of ... Figure 1: Geological Map of Nigeria Showing the Study Area ... expected to assume a circular shape.

  17. Electrical resistivity tomography (ERT surveys on glacial deposits in Romanian Carpathians

    Directory of Open Access Journals (Sweden)

    Andrei ZAMOSTEANU

    2014-11-01

    Full Text Available The study presents preliminary results regarding the use of electrical resistivity surveys in the assessment of the internal structure of the glacial deposits from the Romanian Carpathians.ERT is a geophysical method used to quantify changes in electrical resistivity of the ground towards passing electric current across an array of electrodes and simultaneous measurement of the induced potential gradient. Using specific software the measurements are further processed and correlated with the topography in order to obtain bedrock resistivity features. Therefore, the method is useful to evaluate the characteristics of geological strata and is widely used for mapping shallow subsurface geological structures. In the mountain regions ERT studies have been applied in different glacial and periglacial geomorphological studies - for permafrost detection (in Romanian Carpathians - Urdea et. al., 2008; Vespremeanu-Stroe et al., 2012, slope deformation analysis, the assessment of slip surface depths, sediment thickness, groundwater levels etc. One of the most commonly 2-D array used is the Wenner electrode configuration, which is moderately sensitive to both horizontal and vertical ground structures.Due to their elevations and Pleistocene’s climatic conditions, the Romanian Carpathians have been partially affected by Quaternary glaciations. The glaciers descended to about 1050-1200 m a.s.l. (Urdea and Reurther, 2009 in the Transylvanian Alps and Rodna Mountains (Eastern Carpathians carving a large number of U-shaped valleys and glacial cirques (Mîndrescu, 2006 and forming accumulations of unconsolidated glacial debris (moraines. Our study areas are two sites located in the northern (Rodna Mts. and southern (Iezer Păpuşa Mts. part of the mountain range.

  18. Proceedings of the CERI 2005 electricity conference : markets, integration, resistance

    International Nuclear Information System (INIS)

    2005-01-01

    This conference was attended by power industry decision makers who face continuing challenges regarding changes in electricity market mechanisms, pricing options, and power generation and transmission alternatives. It provided an opportunity to review energy markets in North American with particular reference to supply and demand and opportunities for traditional or new generation technologies based on renewable energy sources including wind powered generation. The presentations focused on transmission issues, market design and capacity issues as well as market power and pricing. The integration of wind energy into the power grid as a measure to diversity the power generation portfolio in North America was also discussed along with hydrothermal synergies and interconnections. The role of wind, coal and nuclear power in future North American energy markets was also discussed along with their environmental consequences. tabs., figs

  19. Abnormal electrical resistivity in γ-TiAl thin films deposited by magnetron sputtering

    International Nuclear Information System (INIS)

    Alford, T.L.; Gadre, K.S.; Kim, H.C.; Deevi, S.C.

    2003-01-01

    Thin films of γ-TiAl are being considered as a potential conductor and/or diffusion barrier for high temperature electronics because of their high melting points and high oxidation resistance. However, it is not possible to form pure γ-TiAl thin films by thermal annealing of Al/Ti bilayers. This study, however, demonstrates the formation of γ-TiAl thin films by dc magnetron sputtering of a compound target. X-ray diffractometry and Rutherford backscattering spectrometry analyses confirm the γ-TiAl phase formation, composition, and thermal stability in vacuum (up to 700 deg. C, 1 h) on SiO 2 . Four-point probe resistivity measurements in vacuum show an initial increase in the resistivity with temperature up to transition temperature for the γ-TiAl thin films. At higher temperatures a decrease in resistivity with additional heating (i.e., negative temperature coefficient of resistivity, TCR) is seen. The values of dρ/dT are typically on the order of -0.32 μΩ cm/ deg. C between 200 and 550 deg. C. At the highest temperature, a minimum value of resistivity of ∼13 μΩ cm is obtained; this value is about one half the value of bulk TiAl at room temperatures. The negative TCR, low resistivity values at high temperatures, and temperature stability are not typically seen in bulk TiAl. This abnormal electrical property is explained using a modified model for a thermally activated polaron-hopping mechanism

  20. Electrical Measurements on a Moving Argon Plasma

    Energy Technology Data Exchange (ETDEWEB)

    Abbas, A. A.M.; Howatson, A. M. [Oxford University (United Kingdom)

    1966-10-15

    Experimental current-voltage characteristic curves were obtained for a moving argon plasma at two stations in an electrically-driven 5 cm shock tube. The standard energy was 1 kj and the base pressure 10 torr, giving a shock of about Mach 4. The measurements were made on the highly-ionized driver gas which followed the shock at speeds between 800 and 1100 m/sec. Two types of electrode were used. One comprised circular solid electrodes of aluminium, molybdenum or stainless steel so machined as to be quite flush with the tube wall; the other comprised filaments of tungsten wire which were immersed in the free stream and could be used cold or heated for thermionic emission. Characteristics were obtained both for applied voltages and for MHD-generated voltages; for the latter a magnetic field of good uniformity up to 0.9 Wb/m{sup 2} was used. The results were always markedly dependent on the surface condition of the electrodes. For consistent results the flush electrodes had to be cleaned carefully by hand after every third discharge, while the filament electrodes were thermionically cleaned before every discharge. In general the cold electrode characteristics for applied voltage showed three distinct regions: a current increase such as would be expected from a double probe; a saturation region; and a linear increase, in order of increasing voltage. For the flush electrodes another apparent saturation was found before, finally, the transition to an arc-type discharge. The first saturation current for flush electrodes corresponded to a random ion current much less than that estimated to exist away from the tube walls, as is expected from a consideration of diffusion through a boundary layer. The value of the current varied somewhat with the electrode material. For the cold filaments, the saturation current density was of the same order as for the flush electrodes. From the linear region of the curves, an effective plasma conductivity was obtained. For comparison, the

  1. Nanolithography based contacting method for electrical measurements on single template synthesized nanowires

    DEFF Research Database (Denmark)

    Fusil, S.; Piraux, L.; Mátéfi-Tempfli, Stefan

    2005-01-01

    A reliable method enabling electrical measurements on single nanowires prepared by electrodeposition in an alumina template is described. This technique is based on electrically controlled nanoindentation of a thin insulating resist deposited on the top face of the template filled by the nanowires....... We show that this method is very flexible, allowing us to electrically address single nanowires of controlled length down to 100 nm and of desired composition. Using this approach, current densities as large as 10 A cm were successfully injected through a point contact on a single magnetic...

  2. Study of phosphorus implanted and annealed silicon by electrical measurements and ion channeling technique

    CERN Document Server

    Hadjersi, T; Zilabdi, M; Benazzouz, C

    2002-01-01

    We investigated the effect of annealing temperature on the electrical activation of phosphorus implanted into silicon. The measurements performed using spreading resistance, four-point probe and ion channeling techniques have allowed us to establish the existence of two domains of variation of the electrical activation (350-700 deg. C) and (800-1100 deg. C). The presence of reverse annealing and the annihilation of defects have been put in a prominent position in the first temperature range. It has been shown that in order to achieve a complete electrical activation, the annealing temperature must belong to the second domain (800-1100 deg. C).

  3. Optical sensors for the measurement of electric current and voltage

    Energy Technology Data Exchange (ETDEWEB)

    Rutgers, W R; Hulshof, H J.M.; Laurensse, I J; van der Wey, A H

    1987-01-01

    Optical sensors for the measurement of electrical current and voltage were developed for application in electric power systems. The current sensor, based on the Faraday effect in a monomode glass fiber, and the voltage sensor, based on the transverse Pockels effect in a crystal, are demonstrated in wide-band (10 MHz) interference-free measurements of pulsed currents and impulse voltages.

  4. PHASE GRADIENT METHOD OF MAGNETIC FIELD MEASUREMENTS IN ELECTRIC VEHICLES

    Directory of Open Access Journals (Sweden)

    N. G. Ptitsyna

    2013-01-01

    Full Text Available Operation of electric and hybrid vehicles demands real time magnetic field control, for instance, for fire and electromagnetic safety. The article deals with a method of magnetic field measurements onboard electric cars taking into account peculiar features of these fields. The method is based on differential methods of measurements, and minimizes the quantity of magnetic sensors.

  5. Static resistivity image of a cubic saline phantom in magnetic resonance electrical impedance tomography (MREIT).

    Science.gov (United States)

    Lee, Byung Il; Oh, Suk Hoon; Woo, Eung Je; Lee, Soo Yeol; Cho, Min Hyeong; Kwon, Ohin; Seo, Jin Keun; Baek, Woon Sik

    2003-05-01

    In magnetic resonance electrical impedance tomography (MREIT) we inject currents through electrodes placed on the surface of a subject and try to reconstruct cross-sectional resistivity (or conductivity) images using internal magnetic flux density as well as boundary voltage measurements. In this paper we present a static resistivity image of a cubic saline phantom (50 x 50 x 50 mm3) containing a cylindrical sausage object with an average resistivity value of 123.7 ohms cm. Our current MREIT system is based on an experimental 0.3 T MRI scanner and a current injection apparatus. We captured MR phase images of the phantom while injecting currents of 28 mA through two pairs of surface electrodes. We computed current density images from magnetic flux density images that are proportional to the MR phase images. From the current density images and boundary voltage data we reconstructed a cross-sectional resistivity image within a central region of 38.5 x 38.5 mm2 at the middle of the phantom using the J-substitution algorithm. The spatial resolution of the reconstructed image was 64 x 64 and the reconstructed average resistivity of the sausage was 117.7 ohms cm. Even though the error in the reconstructed average resistivity value was small, the relative L2-error of the reconstructed image was 25.5% due to the noise in measured MR phase images. We expect improvements in the accuracy by utilizing an MRI scanner with higher SNR and increasing the size of voxels scarifying the spatial resolution.

  6. The effect of electrode contact resistance and capacitive coupling on Complex Resistivity measurements

    DEFF Research Database (Denmark)

    Ingeman-Nielsen, Thomas

    2006-01-01

    The effect of electrode contact resistance and capacitive coupling on complex resistivity (CR) measurements is studied in this paper. An equivalent circuit model for the receiver is developed to describe the effects. The model shows that CR measurements are severely affected even at relatively lo...... with the contact resistance artificially increased by resistors. The results emphasize the importance of keeping contact resistance low in CR measurements....

  7. Corrosion-resistant, electrically-conductive plate for use in a fuel cell stack

    Science.gov (United States)

    Carter, J David [Bolingbrook, IL; Mawdsley, Jennifer R [Woodridge, IL; Niyogi, Suhas [Woodridge, IL; Wang, Xiaoping [Naperville, IL; Cruse, Terry [Lisle, IL; Santos, Lilia [Lombard, IL

    2010-04-20

    A corrosion resistant, electrically-conductive, durable plate at least partially coated with an anchor coating and a corrosion resistant coating. The corrosion resistant coating made of at least a polymer and a plurality of corrosion resistant particles each having a surface area between about 1-20 m.sup.2/g and a diameter less than about 10 microns. Preferably, the plate is used as a bipolar plate in a proton exchange membrane (PEMFC) fuel cell stack.

  8. Geo electrical Resistivity Survey for Ancient Tunnel Detection at Bukit Tenggek, Setiu, Terengganu

    International Nuclear Information System (INIS)

    Siti Nazira Masrom; Mohd Hariri Arifin; Abd Rahim Harun; Abdul Rahim Samsudin

    2011-01-01

    Geo electrical resistivity survey was conducted in the Bukit Tenggek, Setiu, Terengganu to detect the possible existence of an ancient tunnel which is believed to be in the area. Geo electrical resistivity method was found very effective in searching for archaeological exploration and underground structures (tunnels and artifacts). Geo electrical resistivity survey was carried out using Terrameter ABEM SAS1000 and Wenner array electrode configuration. The survey area is located in a damp valley with a stream across the region. 2-D resistivity image showed the existence of anomalies in several areas that can be associated with the structure. Low resistivity value represents the estimated existence of the old tunnel, while isolated rounded anomalies are believed to be associated with barrels/artifacts. 3-D resistivity profiles, shows anomalies that may be caused by the existence of a horizontal and two vertical tunnels (shaft). However, the drillings work need to be done to figure out the exact cause of these anomalies. (author)

  9. Measuring Technology and Mechatronics Automation in Electrical Engineering

    CERN Document Server

    2012-01-01

    Measuring Technology and Mechatronics Automation in Electrical Engineering includes select presentations on measuring technology and mechatronics automation related to electrical engineering, originally presented during the International Conference on Measuring Technology and Mechanatronics Automation (ICMTMA2012). This Fourth ICMTMA, held at Sanya, China, offered a prestigious, international forum for scientists, engineers, and educators to present the state of the art of measuring technology and mechatronics automation research.

  10. Electrical conductivity measurement on DKDP Crystals with different deuterated degrees

    International Nuclear Information System (INIS)

    Liu, Baoan; Yin, Xin; Xu, Mingxia; Ji, Shaohua; Zhu, Lili; Zhang, Lisong; Sun, Xun; Xu, Xinguang; Zhao, Minglei; Zhang, Qinghua

    2012-01-01

    Ten DKDP single crystals with deuterated degrees ranging from 0 to 90 % were grown by a rapid growth method. The electrical conductivities of these crystals were measured along a and c directions at room temperature. The electrical conductivity increases with the increase for deuterium content. Also, the electrical conductivities of certain crystals were measured at various temperatures ranging from 20 to 130 C. The values of activation energy decrease as the increase of deuterium content. The present study indicates that the deuterium tunneling frequency is smaller than that of hydrogen, which may be the reason why the variation of electrical conductivity happens after the substitution of hydrogen for deuterium in KDP crystal. (orig.)

  11. Electrical Resistance Imaging of Bubble Boundary in Annular Two-Phase Flows Using Unscented Kalman Filter

    International Nuclear Information System (INIS)

    Lee, Jeong Seong; Chung, Soon Il; Ljaz, Umer Zeeshan; Khambampati, Anil Kumar; Kim, Kyung Youn; Kim, Sin Kim

    2007-01-01

    For the visualization of the phase boundary in annular two-phase flows, the electrical resistance tomography (ERT) technique is introduced. In ERT, a set of predetermined electrical currents is injected trough the electrodes placed on the boundary of the flow passage and the induced electrical potentials are measured on the electrode. With the relationship between the injected currents and the induced voltages, the electrical conductivity distribution across the flow domain is estimated through the image reconstruction algorithm. In this, the conductivity distribution corresponds to the phase distribution. In the application of ERT to two-phase flows where there are only two conductivity values, the conductivity distribution estimation problem can be transformed into the boundary estimation problem. This paper considers a bubble boundary estimation with ERT in annular two-phase flows. As the image reconstruction algorithm, the unscented Kalman filter (UKF) is adopted since from the control theory it is reported that the UKF shows better performance than the extended Kalman filter (EKF) that has been commonly used. We formulated the UKF algorithm to be incorporate into the image reconstruction algorithm for the present problem. Also, phantom experiments have been conducted to evaluate the improvement by UKF

  12. Determination of the electrical resistivity of vertically aligned carbon nanotubes by scanning probe microscopy

    Science.gov (United States)

    Ageev, O. A.; Il'in, O. I.; Rubashkina, M. V.; Smirnov, V. A.; Fedotov, A. A.; Tsukanova, O. G.

    2015-07-01

    Techniques are developed to determine the resistance per unit length and the electrical resistivity of vertically aligned carbon nanotubes (VA CNTs) using atomic force microscopy (AFM) and scanning tunneling microscopy (STM). These techniques are used to study the resistance of VA CNTs. The resistance of an individual VA CNT calculated with the AFM-based technique is shown to be higher than the resistance of VA CNTs determined by the STM-based technique by a factor of 200, which is related to the influence of the resistance of the contact of an AFM probe to VA CNTs. The resistance per unit length and the electrical resistivity of an individual VA CNT 118 ± 39 nm in diameter and 2.23 ± 0.37 μm in height that are determined by the STM-based technique are 19.28 ± 3.08 kΩ/μm and 8.32 ± 3.18 × 10-4 Ω m, respectively. The STM-based technique developed to determine the resistance per unit length and the electrical resistivity of VA CNTs can be used to diagnose the electrical parameters of VA CNTs and to create VA CNT-based nanoelectronic elements.

  13. Morphology, rheology and electrical resistivity of PLLA/HDPE/CNT nanocomposites: Effect of maleic anhydride

    Energy Technology Data Exchange (ETDEWEB)

    Shao, Li-na; Chen, Jie; Dai, Jian; Chen, Hai-ming; Yang, Jing-hui [Key Laboratory of Advanced Technologies of Materials (Ministry of Education), School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031 (China); Wang, Yong, E-mail: yongwang1976@163.com [Key Laboratory of Advanced Technologies of Materials (Ministry of Education), School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031 (China); Zhang, Chao-liang [State Key Laboratory of Oral Diseases, Sichuan University, Chengdu 610041 (China)

    2015-02-15

    As a part of serial work about tuning the selective location of carbon nanotubes (CNTs) in immiscible polymer blends, this work reports the effects of component polarity and viscosity ratio between components on the selective location of CNTs and the resultant electrical resistivity of the nanocomposites. To achieve the research aim, maleic anhydride (MA) was grafted onto poly(L-lactide) (PLLA) main chain through a reactive compounding processing. After that, different contents of CNTs were incorporated into blends of high density polyethylene (HDPE) and PLLA (or PLLA-g-MA). The morphologies of the ternary nanocomposites and the selective location of CNTs in the nanocomposites were characterized using scanning electron microscope (SEM) and transmission electron microscope (TEM). The microstructure of nanocomposites and the dispersion of CNTs were further proved by rheological measurement. Finally, the electrical resistivity of nanocomposites containing different CNT contents was measured. The results showed that through increasing the polarity of PLLA and decreasing the melt viscosity, CNTs were kinetically trapped at the blend interface region. Consequently, largely decreased percolation threshold was achieved for the PLLA-g-MA/HDPE/CNT nanocomposites. The morphological changes as well as the rheological properties were also comparatively analyzed. - Highlights: • PLLA/HDPE/CNT and PLLA-g-MA/HDPE/CNT composites were prepared. • Different selective location states of CNTs were achieved in different composites. • Selectively located CNTs at the interface resulted in lower percolation threshold.

  14. Electrical conductivity and magnetic permeability measurement of case hardened steels

    Science.gov (United States)

    Tian, Yong

    2015-03-01

    For case carburized steels, electrical conductivity and magnetic permeability profiles are needed to develop model-based case depth characterization techniques for the purpose of nondestructive quality control. To obtain fast and accurate measurement of these material properties, four-point potential drop approaches are applied on circular-shaped discs cut from steel rings with different case depths. First, a direct current potential drop (DCPD) approach is applied to measure electrical conductivity. Subsequently, an alternating current potential drop (ACPD) approach is used to measure magnetic permeability. Practical issues in measurement design and implementation are discussed. Depth profiles of electrical conductivity and magnetic permeability are reported.

  15. Chronological change of electrical resistance in GeCu2Te3 amorphous film induced by surface oxidation

    International Nuclear Information System (INIS)

    Saito, Yuta; Shindo, Satoshi; Sutou, Yuji; Koike, Junichi

    2014-01-01

    Unusual chronological electrical resistance change behavior was investigated for amorphous GeCu 2 Te 3 phase change material. More than a 1 order decrease of electrical resistance was observed in the air even at room temperature. The resistance of the amorphous film gradually increased with increasing temperature and then showed a drop upon crystallization. Such unusual behavior was attributed to the oxidation of the amorphous GeCu 2 Te 3 film. From the compositional depth profile measurement, the GeCu 2 Te 3 film without any capping layer was oxidized in air at room temperature and the formed oxide was mainly composed of germanium oxide. Consequently, a highly-conductive Cu-rich layer was formed in the vicinity of the surface of the film, which reduced the total resistance of the film. The present results could provide insight into the chronological change of electrical resistance in amorphous chalcogenide materials, indicating that not only relaxation of the amorphous, but also a large atomic diffusion contributes to the chronological resistance change. (paper)

  16. In situ electrical measurements of polytypic silver nanowires

    International Nuclear Information System (INIS)

    Liu Xiaohua; Zhu Jing; Jin Chuanhong; Peng Lianmao; Tang Daiming; Cheng Huiming

    2008-01-01

    Novel 4H structure silver nanowires (4H-AgNWs) have been reported to coexist with the usual face-centered cubic (FCC) ones. Here we report the electrical properties of these polytypic AgNWs for the first time. AgNWs with either 4H or FCC structures in the diameter range of 20-80 nm were measured in situ inside a transmission electron microscope (TEM). Both kinds of AgNW in the diameter range show metallic conductance. The average resistivity of the 4H-AgNWs is 19.9 μΩ cm, comparable to the 11.9 μΩ cm of the FCC-AgNWs. The failure current density can be up to ∼10 8 A cm -2 for both 4H-and FCC-AgNWs. The maximum stable current density (MSCD) is introduced to estimate the AgNWs' current-carrying ability, which shows diameter-dependence with a peak around 34 nm in diameter. It is attributed to fast annihilation of the current-induced vacancies and the enhanced surface scattering. Our investigations also suggest that the magnetic field of the electromagnetic lens may also introduce some influence on the measurements inside the TEM

  17. Environmental Monitoring Of Leaks Using Time Lapsed Long Electrode Electrical Resistivity

    International Nuclear Information System (INIS)

    Rucker, D.F.; Fink, J.B.; Loke, M.H.; Myers, D.A.

    2009-01-01

    Highly industrialized areas pose significant challenges for surface based electrical resistivity characterization and monitoring due to the high degree of metallic infrastructure. The infrastructure is typically several orders of magnitude more conductive than the desired targets, preventing the geophysicist from obtaining a clear picture of the subsurface. These challenges may be minimized if steel-cased wells are used as long electrodes. We demonstrate a method of using long electrodes in a complex nuclear waste facility to monitor a simulated leak from an underground storage tank. The leak was simulated by injecting high conductivity fluid in a perforated well and the resistivity measurements were made before and after the leak test. The data were processed in four dimensions, where a regularization procedure was applied in both the time and space domains. The results showed a lowered resistivity feature develop south of the injection site. The time lapsed regularization parameter had a strong influence on the differences in inverted resistivity between the pre and post datasets, potentially making calibration of the results to specific hydrogeologic parameters difficult.

  18. Analysis of Surface Electric Field Measurements from an Array of Electric Field Mills

    Science.gov (United States)

    Lucas, G.; Thayer, J. P.; Deierling, W.

    2016-12-01

    Kennedy Space Center (KSC) has operated an distributed array of over 30 electric field mills over the past 18 years, providing a unique data set of surface electric field measurements over a very long timespan. In addition to the electric field instruments there are many meteorological towers around KSC that monitor the local meteorological conditions. Utilizing these datasets we have investigated and found unique spatial and temporal signatures in the electric field data that are attributed to local meteorological effects and the global electric circuit. The local and global scale influences on the atmospheric electric field will be discussed including the generation of space charge from the ocean surf, local cloud cover, and a local enhancement in the electric field that is seen at sunrise.

  19. Adjoint-state inversion of electric resistivity tomography data of seawater intrusion at the Argentona coastal aquifer (Spain)

    Science.gov (United States)

    Fernández-López, Sheila; Carrera, Jesús; Ledo, Juanjo; Queralt, Pilar; Luquot, Linda; Martínez, Laura; Bellmunt, Fabián

    2016-04-01

    Seawater intrusion in aquifers is a complex phenomenon that can be characterized with the help of electric resistivity tomography (ERT) because of the low resistivity of seawater, which underlies the freshwater floating on top. The problem is complex because of the need for joint inversion of electrical and hydraulic (density dependent flow) data. Here we present an adjoint-state algorithm to treat electrical data. This method is a common technique to obtain derivatives of an objective function, depending on potentials with respect to model parameters. The main advantages of it are its simplicity in stationary problems and the reduction of computational cost respect others methodologies. The relationship between the concentration of chlorides and the resistivity values of the field is well known. Also, these resistivities are related to the values of potentials measured using ERT. Taking this into account, it will be possible to define the different resistivities zones from the field data of potential distribution using the basis of inverse problem. In this case, the studied zone is situated in Argentona (Baix Maresme, Catalonia), where the values of chlorides obtained in some wells of the zone are too high. The adjoint-state method will be used to invert the measured data using a new finite element code in C ++ language developed in an open-source framework called Kratos. Finally, the information obtained numerically with our code will be checked with the information obtained with other codes.

  20. Radiation resistant electrical bushing for high pressures and temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Zajic, V; Banyr, J

    1980-11-15

    The bushing described is characterized by a hollow with a joining member provided inside of at least one of the bushing's electrically conductive core soldered or embedded into a bore in the insulator. Thus, the concentration is limited of the material of the electrically conductive core in the area of the soldered or embedded joint of the support of the electrically conductive core and the insulator, and the resulting force effect is reduced of the difference in thermal dilatations of the materials of the electrically conductive core and the insulator.

  1. Radiation resistant electrical bushing for high pressures and temperatures

    International Nuclear Information System (INIS)

    Zajic, V.; Banyr, J.

    1980-01-01

    The bushing described is characterized by a hollow with a joining member provided inside of at least one of the bushing's electrically conductive core soldered or embedded into a bore in the insulator. Thus, the concentration is limited of the material of the electrically conductive core in the area of the soldered or embedded joint of the support of the electrically conductive core and the insulator, and the resulting force effect is reduced of the difference in thermal dilatations of the materials of the electrically conductive core and the insulator. (J.B.)

  2. Evaluation of Cow Milk Electrical Conductivity Measurements

    Directory of Open Access Journals (Sweden)

    Constantin Gavan

    2017-11-01

    Full Text Available The efficiency of subclinical mastitis diagnosis using an electrical conductivity (EC meter was evaluated in the dairy farm of Agricultural Research and Development Station ( ARDS Simnic Craiova. The results were compared with those obtained by using the California Mastitis Test (CMT and the Somatic Cell Count (SCC.The milk quarter samples ( 1176 from Holstein Friesian cows were analyzed between September and December 2015. The EC evaluation with  the EC meter  ,showed a high proportion of results differing from SCC and CMT results. The CMT still shows to be the most accessible and efficient test in comparison to the EC meter tested.

  3. Electrical resistivity tomography to quantify in situ liquid content in a full-scale dry anaerobic digestion reactor.

    Science.gov (United States)

    André, L; Lamy, E; Lutz, P; Pernier, M; Lespinard, O; Pauss, A; Ribeiro, T

    2016-02-01

    The electrical resistivity tomography (ERT) method is a non-intrusive method widely used in landfills to detect and locate liquid content. An experimental set-up was performed on a dry batch anaerobic digestion reactor to investigate liquid repartition in process and to map spatial distribution of inoculum. Two array electrodes were used: pole-dipole and gradient arrays. A technical adaptation of ERT method was necessary. Measured resistivity data were inverted and modeled by RES2DINV software to get resistivity sections. Continuous calibration along resistivity section was necessary to understand data involving sampling and physicochemical analysis. Samples were analyzed performing both biochemical methane potential and fiber quantification. Correlations were established between the protocol of reactor preparation, resistivity values, liquid content, methane potential and fiber content representing liquid repartition, high methane potential zones and degradations zones. ERT method showed a strong relevance to monitor and to optimize the dry batch anaerobic digestion process. Copyright © 2015 Elsevier Ltd. All rights reserved.

  4. Measurement of the Transverse Spitzer Resistivity during Collisional Magnetic Reconnection

    International Nuclear Information System (INIS)

    Trintchouk, F.; Yamada, M.; Ji, H.; Kulsrud, R.M.; Carter, T.A.

    2000-01-01

    Measurement of the transverse resistivity was carried out in a reconnecting current sheet where the mean free path for the Coulomb collision is smaller than the thickness of the sheet. In a collisional neutral sheet without a guide field, the transverse resistivity is directly related to the reconnection rate. A remarkable agreement is found between the measured resistivity and the classical value derived by L. Spitzer. In his calculation the transverse resistivity for the electrons is higher than the parallel resistivity by a factor of 1.96. The measured values have verified this theory to within 30% errors

  5. A mechanical-electrical finite element method model for predicting contact resistance between bipolar plate and gas diffusion layer in PEM fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Lai, Xinmin; Liu, Dong' an; Peng, Linfa [State Key Laboratory of Mechanical System and Vibration, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240 (China); Ni, Jun [Department of Mechanical Engineering, University of Michigan, Ann Arbor, MI 48109-2125 (United States)

    2008-07-15

    Contact resistance between the bipolar plate (BPP) and the gas diffusion layer (GDL) plays a significant role on the power loss in a proton exchange membrane (PEM) fuel cell. There are two types of contact behavior at the interface of the BPP and GDL, which are the mechanical one and the electrical one. Furthermore, the electrical contact behavior is dependent on the mechanical one. Thus, prediction of the contact resistance is a coupled mechanical-electrical problem. The current FEM models for contact resistance estimation can only simulate the mechanical contact behavior and moreover they are based on the assumption that the contact surface is equipotential, which is not the case in a real BPP/GDL assembly due to the round corner and margin of the BPP. In this study, a mechanical-electrical FEM model was developed to predict the contact resistance between the BPP and GDL based on the experimental interfacial contact resistivity. At first, the interfacial contact resistivity was obtained by experimentally measuring the contact resistance between the GDL and a flat graphite plate of the same material and processing conditions as the BPP. Then, with the interfacial contact resistivity, the mechanical and electrical contact behaviors were defined and the potential distribution of the BPP/GDL assembly was analyzed using the mechanical-electrical FEM model. At last, the contact resistance was calculated according to the potential drop and the current of the contact surface. The numerical results were validated by comparing with those of the model reported previously. The influence of the round corner of the BPP on the contact resistance was also studied and it is found that there exists an optimal round corner that can minimize the contact resistance. This model is beneficial in understanding the mechanical and electrical contact behaviors between the BPP and GDL, and can be used to predict the contact resistance in a new BPP/GDL assembly. (author)

  6. Constant electrical resistivity of Ni along the melting boundary up to 9 GPa

    Science.gov (United States)

    Silber, Reynold E.; Secco, Richard A.; Yong, Wenjun

    2017-07-01

    Characterization of transport properties of liquid Ni at high pressures has important geophysical implications for terrestrial planetary interiors, because Ni is a close electronic analogue of Fe and it is also integral to Earth's core. We report measurements of the electrical resistivity of solid and liquid Ni at pressures 3-9 GPa using a 3000 t multianvil large volume press. A four-wire method, in conjunction with a rapid acquisition meter and polarity switch, was used to overcome experimental challenges such as melt containment and maintaining sample geometry and to mitigate the extreme reactivity/solubility of liquid Ni with most thermocouple and electrode materials. Thermal conductivity is calculated using the Wiedemann-Franz law. Electrical resistivity of solid Ni exhibits the expected P dependence and is consistent with earlier experimental values. Within experimental uncertainties, our results indicate that resistivity of liquid Ni remains invariant along the P-dependent melting boundary, which is in disagreement with earlier prediction for liquid transition metals. The potential reasons for such behavior are examined qualitatively through the impact of P-independent local short-range ordering on electron mean free path and the possibility of constant Fermi surface at the onset of Ni melting. Correlation among metals obeying the Kadowaki-Woods ratio and the group of late transition metals with unfilled d-electron band displaying anomalously shallow melting curves suggests that on the melting boundary, Fe may exhibit the same resistivity behavior as Ni. This could have important implications for the heat flow in the Earth's core.

  7. Study of filled dolines by using 3D stereo image processing and electrical resistivity imaging

    Directory of Open Access Journals (Sweden)

    Mateja Breg Valjavec

    2014-01-01

    Full Text Available This article deals with doline degradation due to uncontrolled waste dumping in the past in the Logatec Polje in Slovenia. It introduces a concept for determining 3D geometric characteristics (shape, depth, radius, area, and volume of formerly concave landforms (i.e., recently filled dolines by using a combination of two methods: (1 photogrammetric stereo processing of archival aerial photographs and (2 electrical resistivity imaging (ERI. To represent, visualize, and study the characteristics of the former surface morphology (i.e., the dolines before they were filled, a digital terrain model (DTM for 1972 (DTM1972 was made using digital photogrammetry processing of five sequential archival aerial photographs (1972, © GURS. DTM1972 was visually and quantitatively compared with the DTM5 of the recent surface morfology (DTM5, © GURS, 2006 in order to define areas of manmade terrain differences. In general, a circular area with a higher terrain difference is an indicator of a filled doline. The calculated terrain differences also indicate the thickness of buried waste material. Three case-study dolines were selected for 3D geometric analysis and tested in the field using ERI. ERI was used to determine the genetic type of the original doline, to confirm that the buried material in the doline is actually waste, and to ascertain opportunities for further study of water pollution due to waste leakage. Based on a comparison among the ERI sections obtained using various electrode arrays, it was concluded that the basins are actually past concave landforms (i.e., dolines filled with mixed waste material having the lowest resistivity value (bellow 100 ohm-m, which differs measurably from the surrounding natural materials. The resistivity of hard stacked limestone is higher (above 1,000 ohm-m than resistivity of cracked carbonate rocks with cracks filled with loamy clay sediments while in loamy alluvial sediment resistivity falls below 150 ohm

  8. In-mine (tunnel-to-tunnel) electrical resistance tomography in South African platinum mines

    CSIR Research Space (South Africa)

    Van Schoor, Abraham M

    2009-12-01

    Full Text Available The applicability of tunnel-to-tunnel electrical resistance tomography (ERT) for imaging disruptive geological structures ahead of mining, in an igneous platinum mining environment is assessed. The geophysical targets of interest are slump...

  9. Using DC electrical resistivity tomography to quantify preferential flow in fractured rock environments

    CSIR Research Space (South Africa)

    May, F

    2011-09-01

    Full Text Available . This investigation aims to identify preferential flow paths in fractured rock environments. Time-lapse Electrical Resistivity Tomography (TLERT, Lund Imaging System), is regarded as a suitable method for identifying preferential water flow....

  10. Wireless Damage Monitoring of Laminated CFRP Composites using Electrical Resistance Change

    National Research Council Canada - National Science Library

    Todoroki, Akira

    2007-01-01

    .... In this system, a tiny oscillation circuit is attached to the composite component. When delimitation of the component occurs, electrical resistance changes, which causes a change in the oscillating frequency of the circuit...

  11. Comparing spatial series of soil bulk electrical conductivity as obtained by Time Domain Reflectometry and Electrical Resistivity Tomography

    Science.gov (United States)

    Saeed, Ali; Dragonetti, Giovanna; Comegna, Allessandro; Garre, Sarah; Lamaddalena, Nicola; Coppola, Antonio

    2016-04-01

    Conventional ground survey of soil root zone salinity by direct soil sampling are time consuming, costly and destructive. Alternatively, soil salinity can be evaluated by measuring the bulk electrical conductivity, σb, in the field. This approach is faster and cheaper, and allows a more intensive surveying. Measurements of σb can be made either in situ or with remote devices. Time domain reflectometry (TDR) sensors allow simultaneous measurements of water content, θ, and σb. They may be calibrated for estimating the electrical conductivity of the soil solution (σw). However, they have a relatively small observation window and thus they are thought to only provide local-scale measurements. The spatial range of the sensors is limited to tens of centimeters and extension of the information to a large area can be problematic. Also, information on the vertical distribution of the σb soil profile may only be obtained by installing sensors at different depths. In this sense, the TDR may be considered as an invasive technique. Compared to the TDR, other geophysical methods based for example on the Electrical Resistivity Tomography (ERT) techniques represent an alternative in respect to those traditional for soil salinity characterization. In order to deduce the actual distribution of the bulk electrical conductivity, σb, in the soil profile, one needs to invert the signal coming from ERT sensors. The latter, in turn, depends on the specific depth distribution of the σb, as well as on the electrical configuration of the sensor used. With these premises, the main aim of this study is to estimate the vertical σb distribution starting from resistivity data series measured using the ERT method under different salinity conditions and using TDR data as ground-truth data for calibration and validation of the ERT sensor. This way, limited measured TDR data may be used for translating extensive ERT apparent electrical conductivity, σa, measurements to estimate depth

  12. Design of a low-cost system for electrical conductivity measurements of high temperature

    Science.gov (United States)

    Singh, Yadunath

    2018-05-01

    It is always a curiosity and interest among researchers working in the field of material science to know the impact of high temperature on the physical and transport properties of the materials. In this paper, we report on the design and working of a system for the measurements of electrical resistivity with high temperature. It was designed at our place and successively used for these measurements in the temperature range from room temperature to 500 ˚C.

  13. Electrical resistivity and thermopower of Y1-xPrxCo2 Compounds

    International Nuclear Information System (INIS)

    Uchima, K; Takaesu, Y; Teruya, A; Akamine, H; Kakihana, M; Tomori, K; Uejo, T; Nakamura, A; Hedo, M; Nakama, T; Yagasaki, K; Burkov, A T

    2015-01-01

    Electrical resistivity ρ and thermopower S of the pseudo-binary compounds of Y 1-x Pr x Co 2 have been measured in the temperature range between 2 and 300 K under magnetic fields up to 10 T, together with the pressure measurements of ρ and S in Y 0.4 Pr 0.6 Co 2 . The Curie temperature decreases with decreasing x, and vanishes at the critical composition x c ≈ 0.4, where the residual resistivity attains a maximum value. The Curie temperature and the residual resistivity of Y 0.4 Pr 0.6 Co 2 show the same pressure dependence as those of the heavy-rare-earth based compounds. These behaviors of ρ and S indicate the inhomogeneous distribution of the Co 3d magnetization. The magnetoresistance of the light-rare earth Y 1-x Pr x Co 2 system is negative in the whole range of x, except for x = 0 and 1, which is a characteristic behavior related with magnetic state and magnitude of the effective field acting on the Co 3d subsystem

  14. Magnon contribution to electrical resistance of gadolinium-dysprosium alloy single crystals

    International Nuclear Information System (INIS)

    Nikitin, S.A.; Slobodchikov, S.S.; Solomkin, I.K.

    1978-01-01

    The magnon, phonon and interelectron collision contributions to the electric resistance of single crystals of gadolinium-dysprosium alloys were quantified. A relationship was found to exist between the electric resistance and the variation of the topology of the Fermi surface on melting of gadolinium with dysprosium. It was found that gadolinium-dysprosium alloys, which have no helicoidal magnetic structure in magnetically ordered state, feature a spin-spin helicoidal-type correlations in the paramagnetic field

  15. A shallow geothermal experiment in a sandy aquifer monitored using electric resistivity tomography

    OpenAIRE

    Hermans, Thomas; Vandenbohede, Alexander; Lebbe, Luc; Nguyen, Frédéric

    2012-01-01

    Groundwater resources are increasingly used around the world for geothermal exploitation systems. To monitor such systems and to estimate their governing parameters, we rely mainly on borehole observations of the temperature field at a few locations. Bulk electrical resistivity variations can bring important information on temperature changes in aquifers. In this paper, we demonstrate the ability of surface electrical resistivity tomography to monitor spatially temperature variations in a san...

  16. Matrix diffusion studies by electrical conductivity methods. Comparison between laboratory and in-situ measurements

    International Nuclear Information System (INIS)

    Ohlsson, Y.; Neretnieks, I.

    1998-01-01

    Traditional laboratory diffusion experiments in rock material are time consuming, and quite small samples are generally used. Electrical conductivity measurements, on the other hand, provide a fast means for examining transport properties in rock and allow measurements on larger samples as well. Laboratory measurements using electrical conductivity give results that compare well to those from traditional diffusion experiments. The measurement of the electrical resistivity in the rock surrounding a borehole is a standard method for the detection of water conducting fractures. If these data could be correlated to matrix diffusion properties, in-situ diffusion data from large areas could be obtained. This would be valuable because it would make it possible to obtain data very early in future investigations of potentially suitable sites for a repository. This study compares laboratory electrical conductivity measurements with in-situ resistivity measurements from a borehole at Aespoe. The laboratory samples consist mainly of Aespoe diorite and fine-grained granite and the rock surrounding the borehole of Aespoe diorite, Smaaland granite and fine-grained granite. The comparison shows good agreement between laboratory measurements and in-situ data

  17. Precise electrical transport measurements by using Bridgman type pressure cell at low temperature

    Energy Technology Data Exchange (ETDEWEB)

    Oishi, Takayuki [Division of Civil and Enviromental Engineering, Kanazawa University, Kakuma-machi, Kanazawa 920-1192 (Japan); Ohashi, Masashi [Faculty of Environmental Design, Kanazawa University, Kakuma-machi, Kanazawa 920-1192 (Japan)

    2010-03-01

    We report a technique for the precise measurement of the electrical resisivity under high pressure at low temperature by using Bridgman anvils made of tungsten carbide. Quasi-hydrostatic pressure is generated up to {approx}15 GPa in the relatively large working space which allows the use of large specimens and simple experimental procedures rather than using a standard diamond anvil cell. The application is demonstrated by the measurements of the electrical resistivity of lead in order to describe the effect of pressure on the superconducting transition.

  18. Precise electrical transport measurements by using Bridgman type pressure cell at low temperature

    International Nuclear Information System (INIS)

    Oishi, Takayuki; Ohashi, Masashi

    2010-01-01

    We report a technique for the precise measurement of the electrical resisivity under high pressure at low temperature by using Bridgman anvils made of tungsten carbide. Quasi-hydrostatic pressure is generated up to ∼15 GPa in the relatively large working space which allows the use of large specimens and simple experimental procedures rather than using a standard diamond anvil cell. The application is demonstrated by the measurements of the electrical resistivity of lead in order to describe the effect of pressure on the superconducting transition.

  19. Integration of electrical resistivity imaging and ground penetrating radar to investigate solution features in the Biscayne Aquifer

    Science.gov (United States)

    Yeboah-Forson, Albert; Comas, Xavier; Whitman, Dean

    2014-07-01

    The limestone composing the Biscayne Aquifer in southeast Florida is characterized by cavities and solution features that are difficult to detect and quantify accurately because of their heterogeneous spatial distribution. Such heterogeneities have been shown by previous studies to exert a strong influence in the direction of groundwater flow. In this study we use an integrated array of geophysical methods to detect the lateral extent and distribution of solution features as indicative of anisotropy in the Biscayne Aquifer. Geophysical methods included azimuthal resistivity measurements, electrical resistivity imaging (ERI) and ground penetrating radar (GPR) and were constrained with direct borehole information from nearby wells. The geophysical measurements suggest the presence of a zone of low electrical resistivity (from ERI) and low electromagnetic wave velocity (from GPR) below the water table at depths of 4-9 m that corresponds to the depth of solution conduits seen in digital borehole images. Azimuthal electrical measurements at the site reported coefficients of electrical anisotropy as high as 1.36 suggesting the presence of an area of high porosity (most likely comprising different types of porosity) oriented in the E-W direction. This study shows how integrated geophysical methods can help detect the presence of areas of enhanced porosity which may influence the direction of groundwater flow in a complex anisotropic and heterogeneous karst system like the Biscayne Aquifer.

  20. High resolution electrical resistivity tomography of golf course greens irrigated with reclaimed wastewater: Hydrological approach

    Science.gov (United States)

    Tapias, Josefina C.; Lovera, Raúl; Himi, Mahjoub; Gallardo, Helena; Sendrós, Alexandre; Marguí, Eva; Queralt, Ignasi; Casas, Albert

    2014-05-01

    Actually, there are over 300 golf courses and more than three thousand licensed players in Spain. For this reason golf cannot be considered simply a hobby or a sport, but a very significant economic activity. Considered as one of the most rapidly expanding land-use and water demanding business in the Mediterranean, golf course development generates controversy. In the recent years there has been a considerable demand for golf courses to adopt environmentally sustainable strategies and particularly water authorities are forcing by law golf managers to irrigate with alternative water resources, mainly reclaimed wastewater. Watering practices must be based on soil properties that are characterized by samples removed from the different zones of the golf course and submitted to an accredited physical soil testing laboratory. Watering schedules are critical on greens with poor drainage or on greens with excessively high infiltration rates. The geophysical survey was conducted over the greens of the Girona Golf Club. Eighteen electrical resistivity tomographies were acquired using a mixed Wenner-Schlumberger configuration with electrodes placed 0.5 meter apart. Small stainless-steel nails were used as electrodes to avoid any damage in the fine turfgrass of greens The resistivity meter was set for systematically and automatically selects current electrodes and measurement electrodes to sample apparent resistivity values. Particle size analysis (PSA) has been performed on soil materials of any putting green. The PSA analysis has been composed of two distinct phases. The first has been the textural analysis of the soils for determining the content of sand, silt, and clay fraction via the use of a stack of sieves with decreasing sized openings from the top sieve to the bottom. Subsequently, the hydraulic conductivity of the substrates has been evaluated by means of Bredding and Hazen empirical relationships. The results of this research show that the electrical resistivity

  1. Assembly for electrical conductivity measurements in the piston cylinder device

    Science.gov (United States)

    Watson, Heather Christine [Dublin, CA; Roberts, Jeffrey James [Livermore, CA

    2012-06-05

    An assembly apparatus for measurement of electrical conductivity or other properties of a sample in a piston cylinder device wherein pressure and heat are applied to the sample by the piston cylinder device. The assembly apparatus includes a body, a first electrode in the body, the first electrode operatively connected to the sample, a first electrical conductor connected to the first electrode, a washer constructed of a hard conducting material, the washer surrounding the first electrical conductor in the body, a second electrode in the body, the second electrode operatively connected to the sample, and a second electrical conductor connected to the second electrode.

  2. Single crystal growth and electrical and magnetic measurements on CeFe4Sb12

    International Nuclear Information System (INIS)

    Mori, I.; Sugawara, H.; Magishi, K.; Saito, T.; Koyama, K.; Kikuchi, D.; Tanaka, K.; Sato, H.

    2007-01-01

    We have succeeded in growing single crystals of CeFe 4 Sb 12 by a Sb-self-flux method and measured the electrical resistivity and magnetization. The residual resistivity is about two times smaller than that of polycrystalline ones, suggesting that the sample quality is highly improved. The magnetization measurements at low temperature revealed that the sample contains almost no magnetic impurities which are always observed in polycrystalline samples. The weak temperature dependence and a broad maximum around 115K in magnetic susceptibility, which is a typical feature of valence fluctuation compounds, have been observed

  3. Imaging Pathways in Fractured Rock Using Three-Dimensional Electrical Resistivity Tomography.

    Science.gov (United States)

    Robinson, Judith; Slater, Lee; Johnson, Timothy; Shapiro, Allen; Tiedeman, Claire; Ntarlagiannis, Dimitrios; Johnson, Carole; Day-Lewis, Frederick; Lacombe, Pierre; Imbrigiotta, Thomas; Lane, John

    2016-03-01

    Major challenges exist in delineating bedrock fracture zones because these cause abrupt changes in geological and hydrogeological properties over small distances. Borehole observations cannot sufficiently capture heterogeneity in these systems. Geophysical techniques offer the potential to image properties and processes in between boreholes. We used three-dimensional cross borehole electrical resistivity tomography (ERT) in a 9 m (diameter) × 15 m well field to capture high-resolution flow and transport processes in a fractured mudstone contaminated by chlorinated solvents, primarily trichloroethylene. Conductive (sodium bromide) and resistive (deionized water) injections were monitored in seven boreholes. Electrode arrays with isolation packers and fluid sampling ports were designed to enable acquisition of ERT measurements during pulsed tracer injections. Fracture zone locations and hydraulic pathways inferred from hydraulic head drawdown data were compared with electrical conductivity distributions from ERT measurements. Static ERT imaging has limited resolution to decipher individual fractures; however, these images showed alternating conductive and resistive zones, consistent with alternating laminated and massive mudstone units at the site. Tracer evolution and migration was clearly revealed in time-lapse ERT images and supported by in situ borehole vertical apparent conductivity profiles collected during the pulsed tracer test. While water samples provided important local information at the extraction borehole, ERT delineated tracer migration over spatial scales capturing the primary hydrogeological heterogeneity controlling flow and transport. The fate of these tracer injections at this scale could not have been quantified using borehole logging and/or borehole sampling methods alone. © 2015, National Ground Water Association.

  4. Inter-strand resistance measurements in the termination of the ITER SULTAN samples

    International Nuclear Information System (INIS)

    Cau, F; Bruzzone, P

    2009-01-01

    In cabled conductors a perfect uniformity of the current among the strands is hardly reached, due to the non-homogeneity of the contact resistance distribution between the strands and the copper of the electrical terminations. In the case of large current unbalance, the overloaded strands hit the critical surface at high field early, developing a current sharing voltage, which drives the redistribution of the current, mainly in the electrical terminations where the inter-strand resistance is lower than in the high field conductor. If the inter-strand resistance in the termination is low, the voltage levels are sufficiently low to allow an effective redistribution of the current to the less loaded strands. The inter-strand resistance of three different termination layouts of ITER short length samples is measured to make a database available which can be used to qualify the layout of the joints and their capability of redistributing the current among the strands.

  5. 47 CFR 73.54 - Antenna resistance and reactance measurements.

    Science.gov (United States)

    2010-10-01

    ... 47 Telecommunication 4 2010-10-01 2010-10-01 false Antenna resistance and reactance measurements... measurements. (a) The resistance of an omnidirectional series fed antenna is measured at either the base of the... the point of common radiofrequency input to the directional antenna system after the antenna has been...

  6. Electrical resistivity of CuAlMo thin films grown at room temperature by dc magnetron sputtering

    Science.gov (United States)

    Birkett, Martin; Penlington, Roger

    2016-07-01

    We report on the thickness dependence of electrical resistivity of CuAlMo films grown by dc magnetron sputtering on glass substrates at room temperature. The electrical resistance of the films was monitored in situ during their growth in the thickness range 10-1000 nm. By theoretically modelling the evolution of resistivity during growth we were able to gain an insight into the dominant electrical conduction mechanisms with increasing film thickness. For thicknesses in the range 10-25 nm the electrical resistivity is found to be a function of the film surface roughness and is well described by Namba’s model. For thicknesses of 25-40 nm the experimental data was most accurately fitted using the Mayadas and Shatkes model which accounts for grain boundary scattering of the conduction electrons. Beyond 40 nm, the thickness of the film was found to be the controlling factor and the Fuchs-Sonheimer (FS) model was used to fit the experimental data, with diffuse scattering of the conduction electrons at the two film surfaces. By combining the Fuchs and Namba (FN) models a suitable correlation between theoretical and experimental resistivity can be achieved across the full CuAlMo film thickness range of 10-1000 nm. The irreversibility of resistance for films of thickness >200 nm, which demonstrated bulk conductivity, was measured to be less than 0.03% following subjection to temperature cycles of -55 and +125 °C and the temperature co-efficient of resistance was less than ±15 ppm °C-1.

  7. Increase of the electrical resistance of thin copper film due to 14 MeV neutron irradiation

    International Nuclear Information System (INIS)

    Agrawal, S.K.; Kumar, U.; Nigam, A.K.; Singh, S.P.

    1981-01-01

    The variation in the electrical resistance of thin copper film (500 A 0 thick), grown on the glass slide has been measured with increasing 14 MeV neutron irradiation time. The electrical resistance vs irradiation time curve shows an interesting behaviour after an irradiation of 40 minutes. However, there is a net increase in the electrical resistance with increasing neutron dose. The maximum increase in the observed electrical resistance after an irradiation of 115 mins, is 4.45%. The microstructural studies of irradiated film were made using TEM and TED techniques. The TEM patterns up to an irradiation time of 1.00 hr do not show any appreciable change in the microstructure. The TED patterns also do not show any appreciable change in the diffraction pattern up to an irradiation time of 1.0 hr. But after an irradiation time of 1.5 hrs, two extra rings appear in the TED pattern which disappear with increasing neutron irradiation time

  8. Environmental effects on electrical properties of Cr-Si-Ni resistive films deposited by magnetron sputtering

    International Nuclear Information System (INIS)

    Zhang Yuqin; Dong Xianping; Wu Jiansheng

    2005-01-01

    The present paper investigated the environmental effects on electrical properties stability and long-term reliability of magnetron sputtered Cr-Si-Ni resistive films in 3.5% NaCl, 0.5 M Na 2 SO 4 and 0.5 M HCl solutions at 25 deg. C, which simulated marine, industrial and acidic environments. The relative resistance change (ΔR/R) for the annealed films revealed that the films had the best electrical properties stability and long-term reliability in industrial environments at 25 deg. C. After immersion in corrosion solutions for 480 h, the value of ΔR/R for the films was only 0.41% in industrial environments, and the values were 0.56 and 1.96% in marine and acidic environments, respectively. The polarization measurements and AES results indicated that the films presented a spontaneous trend to passivation, and could form a dense and stable protective oxide layer (Si oxide) on its surface rapidly that protected the films from further corrosion in three different environments. Furthermore, the formed passive film in industrial environments exhibited much more protective effects on the films than in marine and acidic environments

  9. High resistance (up to 1014 ohms) measurement using RC networks

    International Nuclear Information System (INIS)

    Florescu, Valeriu

    2008-01-01

    An application of dynamic measuring techniques of resistances from 10 6 to 10 14 ohms is described. The method has been analyzed with an eye to measuring accuracy, other influences of the actual measuring circuit also being considered. In conclusion, an automatic measuring method with A/D conversion, automatic range selection, and digital output in semilogarithmic form is outlined. It has been experimentally verified that the dynamic method of resistance measurement can be used for testing insulation resistance of materials and resistors. The great advantage of the automatic measuring circuit is that, apart from an easy automatic selection of the measuring range, digital output in semilogarithmic form ensures compatibility with digital computer systems and facilitates the grading in resistor manufacture. The time required for measuring resistances of the known order of magnitude does not exceed 1 s. Automatic selection of the order of magnitude speeds up the measurement of unknown resistances. For resistance measurement over the range of 10 6 to 10 14 ohms, the measuring accuracy of 1 to 2% is usually sufficient. The meter can be designed as an inexpensive attachment to a conventional counter. The principle of integration measurement avoids undesirable interference effects with which the conventional measuring methods are afflicted. Since the measuring voltage can be adjusted continuously, even the voltage dependence of resistance can be measured

  10. Electric-field-induced superconductivity detected by magnetization measurements of an electric-double-layer capacitor

    International Nuclear Information System (INIS)

    Kasahara, Yuichi; Takeuchi, Yuki; Ye, Jianting; Yuan, Hongtao; Shimotani, Hidekazu; Iwasa, Yoshihiro; Nishimura, Takahiro; Sato, Tatsuya

    2010-01-01

    We report evidence for superconductivity induced by the application of strong electric fields onto the surface of a band insulator, ZrNCl, provided by the observation of a shielding diamagnetic signal. We introduced an electric-double-layer capacitor configuration and in situ magnetization measurements at low temperatures as a method to detect the novel electric-field-induced superconducting state. The results showed excellent agreement with a previous report using a transistor configuration, demonstrating that the present technique is a novel method for investigating the nonequilibrium phase induced by electric fields. (author)

  11. Impact of electric and magnetic fields in a resistant medium on the ...

    African Journals Online (AJOL)

    In this paper, we compare the impact of electric and magnetic fields in a resistant medium on the velocity of a particle subject to varying path angles by using numerical integration of finite difference method. The results show that the magnetic field has much impact on the velocity than the electric field. Journal of the Nigerian ...

  12. Estimating the Condition of the Heat Resistant Lining in an Electrical Reduction Furnace

    Directory of Open Access Journals (Sweden)

    Jan G. Waalmann

    1988-01-01

    Full Text Available This paper presents a system for estimating the condition of the heat resistant lining in an electrical reduction furnace for ferrosilicon. The system uses temperature measured with thermocouples placed on the outside of the furnace-pot. These measurements are used together with a mathematical model of the temperature distribution in the lining in a recursive least squares algorithm to estimate the position of 'the transformation front'. The system is part of a monitoring system which is being developed in the AIP-project: 'Condition monitoring of strongly exposed process equipment in thc ferroalloy industry'. The estimator runs on-line, and results arc presented in colour-graphics on a display unit. The goal is to locate the transformation front with an accuracy of +- 5cm.

  13. Using tensorial electrical resistivity survey to locate fault systems

    International Nuclear Information System (INIS)

    Monteiro Santos, Fernando A; Plancha, João P; Marques, Jorge; Perea, Hector; Cabral, João; Massoud, Usama

    2009-01-01

    This paper deals with the use of the tensorial resistivity method for fault orientation and macroanisotropy characterization. The rotational properties of the apparent resistivity tensor are presented using 3D synthetic models representing structures with a dominant direction of low resistivity and vertical discontinuities. It is demonstrated that polar diagrams of the elements of the tensor are effective in delineating those structures. As the apparent resistivity tensor shows great inefficacy in investigating the depth of the structures, it is advised to accomplish tensorial surveys with the application of other geophysical methods. An experimental example, including tensorial, dipole–dipole and time domain surveys, is presented to illustrate the potentiality of the method. The dipole–dipole model shows high-resistivity contrasts which were interpreted as corresponding to faults crossing the area. The results from the time domain electromagnetic (TEM) sounding show high-resistivity values till depths of 40–60 m at the north part of the area. In the southern part of the survey area the soundings show an upper layer with low-resistivity values (around 30 Ω m) followed by a more resistive bedrock (resistivity >100 Ω m) at a depth ranging from 15 to 30 m. The soundings in the central part of the survey area show more variability. A thin conductive overburden is followed by a more resistive layer with resistivity in the range of 80–1800 Ω m. The north and south limits of the central part of the area as revealed by TEM survey are roughly E–W oriented and coincident with the north fault scarp and the southernmost fault detected by the dipole–dipole survey. The pattern of the polar diagrams calculated from tensorial resistivity data clearly indicates the presence of a contact between two blocks at south of the survey area with the low-resistivity block located southwards. The presence of other two faults is not so clear from the polar diagram patterns, but

  14. Electrical resistance of flaky crystals in the longitudinal quantizing magnetic field

    International Nuclear Information System (INIS)

    Askerov, B.M.; Figarova, S.R.; Makhmudov, M.M.

    2005-01-01

    Specific resistance of the quasi-two-dimensional electrical gas in the longitudinal quantizing magnetic field is investigated in this work. Common expression for resistivity in the flaky crystals was received. In quantum limit was analyzed dependence of the resistivity from the size of magnetic field and parameters energetic spectra in case of strong degenerate gas. It was tagged that, the conduct of specific resistance is formed by the dependence of chemical potential from the size of magnetic field. At the defined value of the chemical potential and size of magnetic field obtains inflation of the specific resistance. (author)

  15. Electrical resistivity due to electron-phonon scattering in thin gadolinium films

    International Nuclear Information System (INIS)

    Urbaniak-Kucharczyk, A.

    1988-01-01

    The contribution to the electrical resistivity due to the electron-phonon scattering for the special case of h.c.p. structure is derived. The numerical results obtained for the case of polycrystalline gadolinum films show the resistivity dependence on the film thickness and the surface properties. (author)

  16. On the difference between optically and electrically determined resistivity of ultra-thin titanium nitride films

    NARCIS (Netherlands)

    Van Hao, B.; Kovalgin, Alexeij Y.; Wolters, Robertus A.M.

    2013-01-01

    This work reports on the determination and comparison of the resistivity of ultra-thin atomic layer deposited titanium nitride films in the thickness range 0.65–20 nm using spectroscopic ellipsometry and electrical test structures. We found that for films thicker than 4 nm, the resistivity values

  17. D.C. electrical conductivity measurements on ADP single crystals ...

    Indian Academy of Sciences (India)

    Unknown

    Impurity added ADP crystals; density; electrical conductivity measurements. 1. Introduction ... determined by the intrinsic defects caused by thermal fluctuations in the ... beaker (corning glass vessel) and allowed to equilibrate at the desired ...

  18. Ferro electricity from magnetic order by neutron measurement

    International Nuclear Information System (INIS)

    Kenzelmann, M.

    2009-01-01

    Magnetic insulators with competing exchange interactions can give rise to strong fluctuations and qualitatively new ground states. The proximity of such systems to quantum critical points can lead to strong cross-coupling between magnetic long-range order and the nuclear lattice. Case in point is a new class of multiferroic materials in which the magnetic and ferroelectric order parameters are directly coupled, and a magnetic field can suppress or switch the electric polarization [1]. Our neutron measurements reveal that ferro electricity is induced by magnetic order and emerges only if the magnetic structure creates a polar axis [2-5]. Our measurements provide evidence that commensurate magnetic order can produce ferro electricity with large electric polarization [6]. The spin dynamics and the field-temperature phase diagram of the ordered phases provide evidence that competing ground states are essential for ferro electricity. (author)

  19. Electric fields, weighting fields, signals and charge diffusion in detectors including resistive materials

    CERN Document Server

    Riegler, Werner

    2016-11-07

    In this report we discuss static and time dependent electric fields in detector geometries with an arbitrary number of parallel layers of a given permittivity and weak conductivity. We derive the Green's functions i.e. the field of a point charge, as well as the weighting fields for readout pads and readout strips in these geometries. The effect of 'bulk' resistivity on electric fields and signals is investigated. The spreading of charge on thin resistive layers is also discussed in detail, and the conditions for allowing the effect to be described by the diffusion equation is discussed. We apply the results to derive fields and induced signals in Resistive Plate Chambers, Micromega detectors including resistive layers for charge spreading and discharge protection as well as detectors using resistive charge division readout like the MicroCAT detector. We also discuss in detail how resistive layers affect signal shapes and increase crosstalk between readout electrodes.

  20. Electric fields, weighting fields, signals and charge diffusion in detectors including resistive materials

    International Nuclear Information System (INIS)

    Riegler, W.

    2016-01-01

    In this report we discuss static and time dependent electric fields in detector geometries with an arbitrary number of parallel layers of a given permittivity and weak conductivity. We derive the Green's functions i.e. the field of a point charge, as well as the weighting fields for readout pads and readout strips in these geometries. The effect of 'bulk' resistivity on electric fields and signals is investigated. The spreading of charge on thin resistive layers is also discussed in detail, and the conditions for allowing the effect to be described by the diffusion equation is discussed. We apply the results to derive fields and induced signals in Resistive Plate Chambers, MICROMEGAS detectors including resistive layers for charge spreading and discharge protection as well as detectors using resistive charge division readout like the MicroCAT detector. We also discuss in detail how resistive layers affect signal shapes and increase crosstalk between readout electrodes.

  1. Control of electrical resistivity of TaN thin films by reactive sputtering for embedded passive resistors

    International Nuclear Information System (INIS)

    Kang, S.M.; Yoon, S.G.; Suh, S.J.; Yoon, D.H.

    2008-01-01

    Tantalum nitride thin films were deposited by radio frequency (RF) reactive sputtering at various N 2 /Ar gas flow ratios and working pressures to examine the change of their electrical resistivity. From the X-ray diffraction (XRD) and four-point probe sheet resistance measurements of the TaN x films, it was found that the change of the crystalline structures of the TaN x films as a function of the N 2 partial pressure caused an abrupt change of the electrical resistivity. When the hexagonal structure TaN thin films changed to an f.c.c. structure, the sheet resistance increased from 16 Ω/sq to 1396 Ω/sq. However, we were able to control the electrical resistivity of the TaN thin film in the range from 69 Ω/sq to 875 Ω/sq, with no change in crystalline structure, within a certain range of working pressures. The size of the grains in the scanning electron microscopy (SEM) images seemed to decrease with the increase of working pressure

  2. Characterizing soil erosion potential using electrical resistivity imaging : final report.

    Science.gov (United States)

    2017-04-01

    The erosion rate, or erodibility, of soil depends on many soil characteristics including: plasticity, : water content, grain size, percent clay, compaction, and shear strength. Many of these characteristics also : influence soil in situ bulk electric...

  3. Characterizing soil erosion potential using electrical resistivity imaging : technical summary.

    Science.gov (United States)

    2017-04-01

    The erosion rate, or erodibility, of soil depends on many soil characteristics : including: plasticity, water content, grain size, percent clay, compaction, and shear : strength. Many of these characteristics also influence soil in situ bulk electric...

  4. Performance measurement of electricity suppliers using PROMETHEE and balance scorecard

    OpenAIRE

    Mona Osati; Manouchehr Omidvari

    2016-01-01

    Performance measurement in energy industry plays an important role on increasing the productivity. Electricity is also among the most essential components of energy in mega cities like Tehran. The lack of a good service in this city may result unpleasant consequences on most civilians who live in this city. This paper presents an empirical investigation to measure the performance of six major electricity contractors in city of Tehran, Iran. The study implements grey numbers to handle any unce...

  5. Applications of electrical resistivity measurements to research into the purification of uranium using floating molten zone by electronic bombardment; Applications des mesures de resistivite electrique a l'etude de la purification de l'uranium par fusion de zone flottante par bombardement electronique

    Energy Technology Data Exchange (ETDEWEB)

    Pascal, J L [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1964-02-01

    The purification of uranium has been achieved by zone melting. Because of the high affinity of uranium towards elements such as oxygen, contamination has been avoided by adopting the floating zone technique and by working under high vacuum. The difficulties created by the deformations of uranium rod, which are caused by anisotropy of dilatation of phases {alpha} and {beta} and allotropic transformations {alpha} {r_reversible} {beta} and {beta} {r_reversible} {alpha}, have been overcome by the use of electron bombardment stabilized by feedback. A rough control of the purification was obtained by micrographic examination, microhardness measurements, and tests of secondary recrystallization, allowed us to appreciate the new degree of purity of the uranium obtained. The investigation of the purity degree was pursued by electrical resistivity measurements at 20 deg. K. But one had to take care in the interpretation of those measurements of the anisotropy of the uranium resistivity and the influence of structure on residual resistivity. Those measurements have led us, by determination of single crystal and uranium resistivity, to be able to distinguish between the principal resistivity against axis [100] and [010]. (author) [French] La purification de l'uranium a ete realisee par l'application de la methode dite de la zone fondue. L'uranium etant particulierement reactif vis-a-vis d'elements tels que l'oxygene, les risques de contamination ont ete supprimes en adoptant la technique de la zone flottante et en operant sous vide eleve. Les difficultes creees par les deformations du barreau d'uranium, dues a l'anisotropie de dilatation des phases {alpha} et {beta} et ou passage des deux points de transformation allotropiques {alpha} {r_reversible} {beta} et {beta} {r_reversible} {alpha}, ont pu etre surmontees par l'emploi du chauffage par bombardement electronique, stabilise par un systeme tres simple de contre reaction. Un premier controle de la purification effectue par

  6. Online junction temperature measurement via internal gate resistance during turn-on

    DEFF Research Database (Denmark)

    Baker, Nick; Munk-Nielsen, Stig; Liserre, Marco

    2014-01-01

    A new method for junction temperature measurement of power semiconductor switches is presented. The measurement exploits the temperature dependent resistance of the temperature sensitive electrical parameter (TSEP): the internal gate resistance. This dependence can be observed during the normal...... switching transitions of an IGBT or MOSFET, and as a result the presented method uses the integral of the gate voltage during the turn-on delay. A measurement circuit can be integrated into a gate driver with no modification to converter or gate driver operation and holds significant advantages over other...

  7. (VLF-EM) and electrical resistivity survey for evaluation

    African Journals Online (AJOL)

    ENSEMBLES

    2016-05-26

    May 26, 2016 ... The VES data were presented as depth sounding curves and .... Base map of the study area. ... resistivity data are presented as sounding curves (Figure ..... occasion of water Africa exhibition Nigeria (2006) at Ikoyi hotels and.

  8. The split-cross-bridge resistor for measuring the sheet resistance, linewidth, and line spacing of conducting layers

    Science.gov (United States)

    Buehler, M. G.; Hershey, C. W.

    1986-01-01

    A new test structure was developed for evaluating the line spacing between conductors on the same layer using an electrical measurement technique. This compact structure can also be used to measure the sheet resistance, linewidth, and line pitch of the conducting layer. Using an integrated-circuit fabrication process, this structure was fabricated in diffused polycrystalline silicon and metal layers and measured optically and electrically. For the techniques used, the optical measurements were typically one-quarter micron greater than the electrical measurements. Most electrically measured line pitch values were within 2 percent of the designed value. A small difference between the measured and designed line pitch is used to validate sheet resistance, linewidth, and line spacing values.

  9. Detection of estrus in dairy cows by electrical measurements of vaginal mucus and by milk progesterone.

    Science.gov (United States)

    Gartland, P; Schiavo, J; Hall, C E; Foote, R H; Scott, N R

    1976-05-01

    Electrical resistance (ohms) of mucus were analyzed in 20 postpartum Holstein cows by use of a probe inserted into the anterior vagina every other day for 30 days. Composite milk samples were taken on the same day, and progesterone was determined by radioimmunoassay. Cows were observed twice daily for standing estrus and reproductive organs palpated weekly per rectum (rectal palpation). Fifteen cows which were cycling showed increasing progesterone 6 to 7 days after the onset of estrus with values of 8.1 to 10.0 ng progesterone/ml milk on days 10 to 17. Concentrations had declined rapidly 2 days before onset of the next estrus. Progesterone in milk was affected by cow and by day of the cycle. Electrical resistance followed a similar cyclical pattern, but variability was large and only cows differed. The correlation between milk progesterone and mucus resistance was .22. Progesterone concentrations for four cows with follicular cysts fluctuated randomly with a mean of 2.6 ng/ml. Mean resistance of vaginal mucus was 44 omega for both cycling and cystic cows, indicating that a single measurement of electrical resistance every 2nd day was unreliable in distinguishing physiological states. One cow had high progesterone in milk on days 19 to 25 and was diagnosed pregnant by rectal palpation 3 wk later. Cows were not seen in estrus 28% of the time when milk progesterone and rectal palpation indicated they were in the follicular phase of the estrous cycle and were cycling.

  10. Radiaton-resistant electrical insulation on the base of cement binders

    International Nuclear Information System (INIS)

    Afanas'ev, V.V.; Korenevskij, V.V.; Pisachev, S.Yu.

    1985-01-01

    The problems of designing radiation-resistant electrical insulations on the base of BATs and Talum cements for the UNK magnets operating under constant and pulse modes are discussed. The data characterizing dielectrical ad physico-mechanical properties of 25 various compositions are given. Two variants of manufacturing coils are considered: solid and with the use of asbestos tape impregnated with aluminous cement solution. The data obtained testify to the fact that the advantages of insulation on Talum cement are raised radiation resistance, high strength (particularly compression strength), weak porosity, high elasticity modulus and high thermal conductivity. BATs cement insulation is characterized by high radiation resistance, absence of shrinkage, rather low elasticity modulus and high dielectrical characteristics under normal conditions. The qualities of the solid insulation variant are its high technological effectiveness and posibility to fill up the spaces of complex configuration. In case of using as solid insulation Talum cement, however special measures for moisture removal are required. The advantage of insulation on the base of the asbestos tape is its reliability. For complex configuration magnets, however to realize is such insulation somewhat difficult

  11. Electrical impedance spectroscopy measurements to estimate the ...

    Indian Academy of Sciences (India)

    Administrator

    The reviews of these studies were presented by Kahraman ... kind of solid or liquid material: ionic, semi-conducting, mixed electronic–ionic and .... the rock sample and its response was measured at room temperature. Figure 5 indicates the ...

  12. A Fieldmill for Measuring Atmospheric Electricity

    Science.gov (United States)

    Thompson, Frank

    2018-01-01

    It is a well known fact that the Earth carries a net negative charge that produces a downward electrostatic field. The present experiment shows how this field can be measured with a Field Mill which has been constructed from components readily available in the Laboratory. In fine weather conditions a value of 120 (±10) V m[superscript -1] was…

  13. Thickness effect on electric resistivity on polystyrene and carbon black- based composites

    Energy Technology Data Exchange (ETDEWEB)

    Hernandez-Lopez, S; Vigueras-Santiago, E [Laboratorio de Investigacion y Desarrollo de Materiales Avanzados (LIDMA) Facultad de Quimica, Paseo Colon Esquina con Paseo Tollocan, s/n, CP 50000, Toluca (Mexico); Mayorga-Rojas, M; Reyes-Contreras, D, E-mail: eviguerass@uaemex.m [Facultad de Ciencias, Universidad Autonoma del Estado de Mexico. Av. Instituto Literario 100 Ote. C. P. 50000, Toluca (Mexico)

    2009-05-01

    Changes on electrical resistivity were experimentally studied for polystyrene and carbon black-based composites respect to the temperature. 22% w/w carbon black composite films at 30{mu}m, 2mm y 1cm thick were submitted to thermal heating-cooling cycles from room temperature to 100 deg. C, slightly up to T{sub g} of the composite. For each cycle changes on electrical resistivity constituent a hysteresis loop that depends on the sample thickness. The changes during the heating stage could be explained as a consequence of the thermal expansion and mobility of the polymer chains at T{sub g}, producing a disconnecting of the electrical contacts among carbon black particles and an important increasing (200%) of the electrical resistivity. For each cycle, the hysteresis loop was observed in thicker samples, whereas for 30 mu m thickness sample the hysteresis loop was lost after four cycles.

  14. Longitudinal and transverse electric field measurements in resonant cavities

    International Nuclear Information System (INIS)

    Tong Dechun; Chen Linfeng; Zheng Xiaoyue

    1994-01-01

    The paper presents a measuring technique for the electric field distribution of high order modes in resonant cavities. A perturbing bead-like cage made with metallic wires are developed for S-band field measurements, which can be used to detect a small electric field component in the presence of other strong electric or magnetic field components (That means high sensitivity and high directivity). In order to avoid orientation error for the cage with very high directivity, two parallel threads were used for supporting the perturbing cage. A simple mechanical set-up is described. The cage can be driven into the cavity on-axis or off-axis in any azimuth for the longitudinal and transverse electric field measurements

  15. Modelling the influence of steel fibres on the electrical resistivity of cementitious composites

    DEFF Research Database (Denmark)

    Solgaard, Anders Ole Stubbe; Michel, Alexander; Stang, Henrik

    2009-01-01

    One of the governing factors on the corrosion of embedded reinforcement is the electrical resistivity of the concrete. The combination of steel fibres and conventional reinforcement bars has been used in a number of structures. However, the addition of electrical con-ductive fibres might influence...... of steel fibre reinforced concrete (SFRC). The parameters investigated in the following are the fibre geometry, the fibre volume and the transitional resistance. On basis of the experimental results, a model, taking the resistivity of the fibres and the concrete matrix into account is proposed....... the overall resistivity of the material and thereby the corrosion rate of the embedded reinforcement. To the knowledge of the authors, only preliminary studies have been made on the influence of corrosion of the reinforcement bars from the addition of the electrical conductive steel fibres. Thus the present...

  16. Monitoring of In-Situ Remediation By Time Lapse 3D Geo-Electric Measurements

    Science.gov (United States)

    Kanli, A. I.; Tildy, P.; Neducza, B.; Nagy, P.; Hegymegi, C.

    2017-12-01

    Injection of chemical oxidant solution to degrade the subsurface contaminants can be used for hydrocarbon contamination remediation. In this study, we developed a non-destructive measurement strategy to monitor oxidative in-situ remediation processes. The difficulties of the presented study originate from the small volume of conductive solution that can be used due to environmental considerations. Due to the effect of conductive groundwater and the high clay content of the targeted layer and the small volume of conductive solution that can be used due to environmental considerations, a site specific synthetic modelling is necessary for measurement design involving the results of preliminary 2D ERT measurements, electrical conductivity measurements of different active agents and expected resistivity changes calculated by soil resistivity modelling. Because of chemical biodegradation, the results of soil resistivity modelling have suggested that the reagent have complex effects on contaminated soils. As a result the plume of resistivity changes caused by the injected agent was determined showing strong fracturing effect because of the high pressure of injection. 3D time-lapse geo-electric measurements were proven to provide a usable monitoring tool for in-situ remediation as a result of our sophisticated tests and synthetic modelling.

  17. Electric Dipole Moment Measurements with Rare Isotopes

    International Nuclear Information System (INIS)

    Chupp, Timothy

    2016-01-01

    The origin of matter is one of the deepest questions addressed by science and remains a mystery because our understanding of the Big Bang suggests that equal amounts of matter as antimatter would be created and annihilate leaving nothing from which stars, galaxies, planets and ultimately life as we know it was created. We know this is not the case in the universe, and so the explanation that the laws of physics can distinguish the difference of moving forward and backward in time and provide mechanisms that produce more matter that antimatter so that a little bit was left over. These same laws of physics affect our world today and would very slightly change the shape of an atom, stretching is along the direction of the spin of its nucleus. This subtle shape change has been searched in many systems - the neutron, atoms and molecules, but has not yet been detected, even as the motivation is strengthened by our understanding of their structure. We therefore look to new systems that have special features that make these effects stand out. Rare isotopes provide one possibility and specific radon atoms are our choice. We have developed techniques to make these measurements with short-lived radioactive atoms, studied the nuclei to provide deeper understanding of how these affect arise in such atoms (including radium) and developed new laser-based techniques to measure and control the magnetic fields necessary to perform these exquisitely sensitive measurements. In this work we have shown that radioactive radon atoms can be produced and transported to an apparatus that lines up the spins of the atoms. We have also shown that the nuclei of nearby radium are pear shaped and that the radon nuclei likely oscillate from one pear shape to its mirror reflection. We have also used the techniques which control nuclear spin to study the magnetic environment in a magnetically shielded room, which has the smallest magnetic field in a large volume in the universe. Measuring magnetic

  18. Electric Dipole Moment Measurements with Rare Isotopes

    Energy Technology Data Exchange (ETDEWEB)

    Chupp, Timothy [Univ. of Michigan, Ann Arbor, MI (United States)

    2016-11-11

    The origin of matter is one of the deepest questions addressed by science and remains a mystery because our understanding of the Big Bang suggests that equal amounts of matter as antimatter would be created and annihilate leaving nothing from which stars, galaxies, planets and ultimately life as we know it was created. We know this is not the case in the universe, and so the explanation that the laws of physics can distinguish the difference of moving forward and backward in time and provide mechanisms that produce more matter that antimatter so that a little bit was left over. These same laws of physics affect our world today and would very slightly change the shape of an atom, stretching is along the direction of the spin of its nucleus. This subtle shape change has been searched in many systems - the neutron, atoms and molecules, but has not yet been detected, even as the motivation is strengthened by our understanding of their structure. We therefore look to new systems that have special features that make these effects stand out. Rare isotopes provide one possibility and specific radon atoms are our choice. We have developed techniques to make these measurements with short-lived radioactive atoms, studied the nuclei to provide deeper understanding of how these affect arise in such atoms (including radium) and developed new laser-based techniques to measure and control the magnetic fields necessary to perform these exquisitely sensitive measurements. In this work we have shown that radioactive radon atoms can be produced and transported to an apparatus that lines up the spins of the atoms. We have also shown that the nuclei of nearby radium are pear shaped and that the radon nuclei likely oscillate from one pear shape to its mirror reflection. We have also used the techniques which control nuclear spin to study the magnetic environment in a magnetically shielded room, which has the smallest magnetic field in a large volume in the universe. Measuring magnetic

  19. Air resistance measurements on actual airplane parts

    Science.gov (United States)

    Weiselsberger, C

    1923-01-01

    For the calculation of the parasite resistance of an airplane, a knowledge of the resistance of the individual structural and accessory parts is necessary. The most reliable basis for this is given by tests with actual airplane parts at airspeeds which occur in practice. The data given here relate to the landing gear of a Siemanms-Schuckert DI airplane; the landing gear of a 'Luftfahrzeug-Gesellschaft' airplane (type Roland Dlla); landing gear of a 'Flugzeugbau Friedrichshafen' G airplane; a machine gun, and the exhaust manifold of a 269 HP engine.

  20. A fieldmill for measuring atmospheric electricity

    Science.gov (United States)

    Thompson, Frank

    2018-03-01

    It is a well known fact that the Earth carries a net negative charge that produces a downward electrostatic field. The present experiment shows how this field can be measured with a Field Mill which has been constructed from components readily available in the Laboratory. In fine weather conditions a value of 120 (±10) V m-1 was obtained which agrees with data in the literature. However, when a thunder storm was approaching preliminary measurements showed that the field varied between +400 V m-1 and -1000 V m-1 thus indicating complex charge states of the approaching clouds. Suggestions are made for improving the sensitivity of the apparatus so that experiments can be carried out for other weather conditions.

  1. Magnetic ordering and electrical resistivity in Co0.2Zn0.8Fe2O4 spinel oxide

    International Nuclear Information System (INIS)

    Bhowmik, R.N.; Ranganathan, R.; Ghosh, B.; Kumar, S.; Chattopadhyay, S.

    2008-01-01

    We report the magnetic, Moessbauer spectroscopy and resistivity measurements in order to understand the electronic behaviour of bulk Co 0.2 Zn 0.8 Fe 2 O 4 spinel oxide. The effect of magnetic order on electrical behaviour is observed from the resistivity measurements in the absence and presence of magnetic field. The analysis of Moessbauer spectra suggests the absence of Fe 2+ ions in the system, which implies that complete hopping of charge carriers between localized Fe 3+ /Co 2+ and Fe 2+ /Co 3+ pair of ions in B sublattice is not the favourable mechanism in Co 0.2 Zn 0.8 Fe 2 O 4 . We suggest that electrical behaviour of the present sample may be consistent with a model of fractional charge transfer via Fe B 3+ -O 2- -Co B 2+ superexchange path

  2. Enhanced Electrical Resistivity after Rapid Cool of the Specimen in Layered Oxide LixCoO2

    Science.gov (United States)

    Miyoshi, K.; Manami, K.; Takeuchi, J.; Sasai, R.; Nishigori, S.

    Measurements of electrical resistivity and DC magnetization for LixCoO2 (x=0.71 and 0.64) have been performed using single crystal specimens. It has been found that electrical resistivity measured after rapid cool of the specimen becomes larger compared with that after slow cool below the temperature TS∽155 K at which charge ordering of Co3+/Co4+(=2:1) occurs. The behavior can be understood considering that the charge ordering can be destroyed by Li ions which are in an amorphous state after rapid cool via the interlayer Coulomb interactions, and also that the disordered Co3+/Co4+ state becomes insulating, while the charge ordered state has a metallic electronic structure, as recently revealed by the scanning tunneling microscopy.

  3. Change of electrical resistivity and Young's modulus during crystallization of amorphous Fe40Ni40B20

    International Nuclear Information System (INIS)

    Stel, J. van der; Veldhuizen, H.B. van; Koebrugge, G.W.; Sietsma, J.; Beukel, A. van den

    1989-01-01

    The kinetics of crystallization of amorphous Fe 40 Ni 40 B 20 is studied by measuring isothermal changes of the electrical resistivity and Young's modulus in the temperature range 600 to 700 K. The results satisfy very well the Johnson-Mehl-Avrami equation for phase transformations with a constant activation energy of 317 kJ/mol and a constant Avrami exponent n ∼ 2. This result is interpreted as two-dimensional growth of pre-existing nuclei which become as thick as the specimen in an early stage of crystallization. The relative change in electrical resistivity upon crystallization strongly depends on the measuring temperature T m , varying from 47% at T m = 77 K to 5% at T m = 600 K. It extrapolates to zero at T m ∼ 700 K. (author)

  4. Studies of electrical properties of low-resistivity sandstones based on digital rock technology

    Science.gov (United States)

    Yan, Weichao; Sun, Jianmeng; Zhang, Jinyan; Yuan, Weiguo; Zhang, Li; Cui, Likai; Dong, Huaimin

    2018-02-01

    Electrical properties are important parameters to quantitatively calculate water saturation in oil and gas reservoirs by well logging interpretation. It is usual that oil layers show high resistivity responses, while water layers show low-resistivity responses. However, there are low-resistivity oil zones that exist in many oilfields around the world, leading to difficulties for reservoir evaluation. In our research, we used digital rock technology to study different internal and external factors to account for low rock resistivity responses in oil layers. We first constructed three-dimensional digital rock models with five components based on micro-computed tomography technology and x-ray diffraction experimental results, and then oil and water distributions in pores were determined by the pore morphology method. When the resistivity of each component was assigned, rock resistivities were calculated by using the finite element method. We collected 20 sandstone samples to prove the effectiveness of our numerical simulation methods. Based on the control variate method, we studied the effects of different factors on the resistivity indexes and rock resistivities. After sensitivity analyses, we found the main factors which caused low rock resistivities in oil layers. For unfractured rocks, influential factors arranged in descending order of importance were porosity, clay content, temperature, water salinity, heavy mineral, clay type and wettability. In addition, we found that the resistivity index could not provide enough information to identify a low-resistivity oil zone by using laboratory rock-electric experimental results. These results can not only expand our understandings of the electrical properties of low-resistivity rocks from oil layers, but also help identify low-resistivity oil zones better.

  5. Electrical resistivity and rheological properties of sensing bentonite drilling muds modified with lightweight polymer

    Directory of Open Access Journals (Sweden)

    Ahmed S. Mohammed

    2018-03-01

    Full Text Available In this study, the electrical resistivity and rheological properties of a water-based bentonite clay drilling mud modified with the lightweight polymer (guar gum under various temperature were investigated. Based on the experimental and analytical study, the electrical resistivity was identified as the sensing property of the bentonite drilling mud so that the changes in the properties can be monitored in real-time during the construction. The bentonite contents in the drilling muds were varied up to 8% by the weight of water and temperature was varied from 25 °C to 85 °C. The guar gum content (GG% was varied between 0% and 1% by the weight of the drilling mud to modify the rheological properties and enhance the sensing electrical resistivity of the drilling mud. The guar gum and bentonite clay were characterized using thermal gravimetric analysis (TGA. The total weight loss at 800 °C for the bentonite decreased from 12.96% to 0.7%, about 95% reduction, when the bentonite was mixed with 1% of guar gum. The results also showed that 1% guar gum decreased the electrical resistivity of the drilling mud from 50% to 90% based on the bentonite content and the temperature of the drilling mud. The guar gum modification increased the yield point (YP and plastic viscosity (PV by 58% to 230% and 44% to 77% respectively based on the bentonite content and temperature of the drilling mud. The rheological properties of the drilling muds have been correlated to the electrical resistivity of the drilling mud using nonlinear power and hyperbolic relationships. The model predictions agreed well with the experimental results. Hence the performance of the bentonite drilling muds with and without guar gum can be characterized based on the electrical resistivity which can be monitored real-time in the field. Keywords: Bentonite, Polymer (Guar gum, Electrical resistivity, Rheological properties, Temperature, Modeling

  6. Real-time pricing when some consumers resist in saving electricity

    International Nuclear Information System (INIS)

    Salies, Evens

    2013-01-01

    Successful real-time electricity pricing depends firstly upon consumers' willingness to subscribe to such terms and, secondly, on their ability to curb consumption levels. The present paper addresses both issues by considering consumers differentiated by their electricity saving costs, half of whom resist saving electricity. We demonstrate that when consumers are free to adopt real-time prices, producers prefer charging inefficient prices and, in so doing, discriminate against that portion of the consumer population which faces no saving costs. We also find that efficient marginal cost pricing is feasible, but is incompatible with mass adoption of real-time prices. - Highlights: • We model consumers switching from uniform to real-time electricity pricing (RTP). • Half the consumer population is pro-RTP and half resists saving electricity. • Efficient RTP is feasible but is incompatible with mass adoption

  7. Characterizing Fracture Property Using Resistivity Measured at Different Frequencies

    Energy Technology Data Exchange (ETDEWEB)

    Horne, Roland N. [Stanford Univ., CA (United States); Li, Kewen [Stanford Univ., CA (United States)

    2014-09-30

    The objective was to develop geophysical approaches to detecting and evaluating the fractures created or existing in EGS and other geothermal reservoirs by measuring the resistivity at different frequencies. This project has been divided into two phases: Phase I (first year): Proof of Concept – develop the resistivity approach and verify the effect of frequency on the resistivity in rocks with artificial or natural fractures over a wide range of frequencies. Phase II: Prototyping Part 1 (second year): measure the resistivity in rocks with fractures of different apertures, different length, and different configurations at different frequencies. Part 2 (third year): develop mathematical models and the resistivity method; infer the fracture properties using the measured resistivity data.

  8. Measurement of ac electrical conductivity of molten glass by impedance measurement using co-axial cylinder electrode

    International Nuclear Information System (INIS)

    Shah, J.G.; Yalmali, V.S.; Tawde, Manisha; Mishra, R.

    2006-01-01

    The need of nuclear power as an energy source requires the solution of many problems. One of the most important is fixation of high level radioactive waste (HLW) in suitable borosilicate glass formulation. The major issue with this process is maximum waste loading in the final vitrified product without compromising on long term product characteristics. The electrical resistivity measurement at high temperature could not be measured with good precision using standard parallel plate electrode configuration due to error in cell constant measurement. Hence a high accuracy, calibration free technique consisting of co-axial electrodes was employed

  9. Influence of Dry Cleaning on the Electrical Resistance of Screen Printed Conductors on Textiles

    Directory of Open Access Journals (Sweden)

    Kazani Ilda

    2016-09-01

    Full Text Available Electrically conducting inks were screen printed on various textile substrates. The samples were dry cleaned with the usual chemicals in order to investigate the influence of the mechanical treatment on the electrical conductivity. It was found that dry cleaning has a tremendous influence on this electrical conductivity. For several samples, it is observed that the electrical resistance increases with the square of the number of dry cleaning cycles. In order to explain this observation a theoretical model and a numerical simulation have been carried out, by assuming that dry cleaning cycles introduce a crack in the conducting layer. The theoretical analysis and the numerical analysis both confirmed the experimental observations.

  10. Electric field measurements at subcritical, oblique bow shock crossings

    International Nuclear Information System (INIS)

    Wygant, J.R.; Bensadoun, M.; Mozer, F.S.

    1987-01-01

    Electric field measurements at oblique, subcritical bow shock crossings are presented from the ISEE 1 University of California, Berkeley, double-probe electric field experiment. The measurements averaged over the 3-s spin period of the spacecraft provide the first observations of the large-scale (100 km) laminar oscillations in the longitudinal component of the electric field associated with the whistler precursor which is characteristic of these dispersive shocks. The amplitude of the oscillations increases from ∼0.5 mV/m to a maximum of 6 mV/m across the magnetic ramp of the shock (directed along the shock normal). The calculated electric potential drops across the shocks varied from 340 to 550 volts, which is 40-60% of the observed loss of kinetic energy associated with the bulk flow of the ions. These measurements suggest that at these shocks the additional deceleration of incident ions is due to the Lorentz force. The contributions to the normal component of the large-scale electric field at the shock due to the parallel and perpendicular components (relative to the magnetic field) of the electric field are evaluated. It is shown that the perpendicular component of the electric field dominates, accounting for most of the cross-shock potential, but that there is a nonnegligible parallel component. This large-scale parallel component has a magnitude of 1-2 mV/m which sometimes results in a potential well for electrons with a depth of ∼150 eV. It is experimentally demonstrated that the dominance of the perpendicular over the parallel component of the electric field resulted in a correlation between the longitudinal component of the large-scale electric field and the fluctuations in the magnetic field component perpendicular to the coplanarity plane

  11. Application of Electrical Resistivity Tomography Technique for Characterizing Leakage Problem in Abu Baara Earth Dam, Syria

    Directory of Open Access Journals (Sweden)

    Walid Al-Fares

    2014-01-01

    Full Text Available Electrical Resistivity Tomography (ERT survey was carried out at Abu Baara earth dam in northwestern Syria, in order to delineate potential pathways of leakage occurring through the subsurface structure close to the dam body. The survey was performed along two straight measuring profiles of 715 and 430 m length in up- and downstream sides of the dam’s embankment. The analysis of the inverted ERT sections revealed the presence of fractured and karstified limestone rocks which constitute the shallow bedrock of the dam reservoir. Several subsurface structural anomalies were identified within the fractured bedrock, most of which are associated with probable karstic cavities, voids, and discontinuity features developed within the carbonates rocks. Moreover, results also showed the occurrence of a distinguished subsiding structure coinciding with main valley course. Accordingly, it is believed that the bedrock and the other detected features are the main potential causes of water leakage from the dam’s reservoir.

  12. Wet method for measuring starch gelatinization temperature using electrical conductivity.

    Science.gov (United States)

    Morales-Sanchez, E; Figueroa, J D C; Gaytan-Martínez, M

    2009-09-01

    The objective of the present study was to develop a method for obtaining the gelatinization temperature of starches by using electrical conductivity. Native starches from corn, rice, potato, and wheat were prepared with different proportions of water and heated from room temperature to 90 degrees C, in a device especially designed for monitoring the electrical conductivity as a function of temperature. The results showed a linear trend of the electrical conductivity with the temperature until it reaches the onset gelatinization temperature. After that point, the electrical conductivity presented an increment or decrement depending on the water content in the sample and it was related to starch swelling and gelatinization phenomena. At the end gelatinization temperature, the conductivity becomes stable and linear, indicating that there are no more changes of phase. The starch gelatinization parameter, which was evaluated in the 4 types of starches using the electrical conductivity, was compared with those obtained by using differential scanning calorimeter (DSC). The onset temperature at which the electrical conductivity increased or decreased was found to be similar to that obtained by DSC. Also, the final temperature at which the electrical conductivity returned to linearity matched the end gelatinization temperature of the DSC. Further, a wet method for measuring the onset, peak, and end gelatinization temperatures as a function of temperature using the electrical conductivity curves is presented for a starch-water suspension.

  13. Statistical analysis of electrical resistivity as a tool for estimating cement type of 12-year-old concrete specimens

    NARCIS (Netherlands)

    Polder, R.B.; Morales-Napoles, O.; Pacheco, J.

    2012-01-01

    Statistical tests on values of concrete resistivity can be used as a fast tool for estimating the cement type of old concrete. Electrical resistivity of concrete is a material property that describes the electrical resistance of concrete in a unit cell. Influences of binder type, water-to-binder

  14. Calibration-free electrical conductivity measurements for highly conductive slags

    International Nuclear Information System (INIS)

    Macdonald, Christopher J.; Gao, Huang; Pal, Uday B.; Van den Avyle, James A.; Melgaard, David K.

    2000-01-01

    This research involves the measurement of the electrical conductivity (K) for the ESR (electroslag remelting) slag (60 wt.% CaF 2 - 20 wt.% CaO - 20 wt.% Al 2 O 3 ) used in the decontamination of radioactive stainless steel. The electrical conductivity is measured with an improved high-accuracy-height-differential technique that requires no calibration. This method consists of making continuous AC impedance measurements over several successive depth increments of the coaxial cylindrical electrodes in the ESR slag. The electrical conductivity is then calculated from the slope of the plot of inverse impedance versus the depth of the electrodes in the slag. The improvements on the existing technique include an increased electrochemical cell geometry and the capability of measuring high precision depth increments and the associated impedances. These improvements allow this technique to be used for measuring the electrical conductivity of highly conductive slags such as the ESR slag. The volatilization rate and the volatile species of the ESR slag measured through thermogravimetric (TG) and mass spectroscopy analysis, respectively, reveal that the ESR slag composition essentially remains the same throughout the electrical conductivity experiments

  15. Application of Electrical Resistivity Imaging and Land Surveying in the Analysis of Underground Construction Impact on the Warsaw Scarp

    Directory of Open Access Journals (Sweden)

    Kaczmarek Łukasz

    2016-12-01

    Full Text Available The paper presents the analysis of the II Underground Line construction’s impact on the Warsaw Scarp with the use of the electrical resistivity imaging (ERI, also known as the electrical resistivity tomography and further total station position measurements.The underground passes under the scarp perpendicular in the area of Dynasy Street 6, in Down-town district.The electrical resistivity imaging was performed for recognition of the geological structure and a potential land slide surface or zone.The gradient system was used during the prospection. In these analyses, the longitudinal section was 40 m long, and the depth of survey amounted to 6 m. In the case of the 200 m long transverse section, the resulted depth of survey was 30 m.The geophysical image of the longitudinal section,does not contain loosening soil zones,which could indicates lip surface.Next, total station measurements, which were tied to the archival geodetic observations’ results, were carried out. The aim of the measurements was to verify the activity of the horizontal and vertical displacements. The TBM excavation process led to summary vertical displacements up to approx. 24 mm and horizontal displacements amounting to approx. 13 mm. To sum up, the current land surveys reveals minor under ground line’ s construction impact on the scarp displacement. Nevertheless, the sensitive urban environment requires further monitoring, especially that the operation loads can result in displacement rate change.

  16. A Measurement System of Electric Signals on Standing Trees

    Directory of Open Access Journals (Sweden)

    Hao TIAN

    2014-01-01

    Full Text Available The standing tree electric signal (STES, defined as the electric potential difference between standing trees and the surrounding soil, can be utilized to reflect the biological nature of the trees. This signal should be measured precisely because it can also be collected and used as the electric power energy. In this paper, the automatic measurement system of standing tree biological electric signal based on MSP430 MCU. First of all, the basic structure of the presented system is introduced and it includes three modules: amplification module of the standing tree electric signal, the acquisition and processing of the signal module and the serial communication module. Then, the performances of the built system are respectively validated by the Poplar, Planetree, and Platanus in Beijing Forestry University. The result indicated that the relative error of this system is less than 2 %. The presented system can be considered as the foundation of the subsequent study on the mechanism of the biological electric signal and the application of the biological electric energy on standing trees.

  17. Electric field measurements in the auroral E region

    International Nuclear Information System (INIS)

    Mahon, H.P.; Smiddy, M.; Sagalyn, R.C.

    1975-01-01

    Dipole electric field, positive ion and electron densities and temperatures, vehicle potential, and plasma sheath measurements have been made in the auroral E region by means of rockets flown from Fort Churchill, Canada. These results are described and compared over the altitude region 100 to 165 km. On a rocket flight launched on 10 December 1969 during very quiet conditions, adjacent to a stable, low intensity auroral arc, the plasma density and temperatures are found to be high and the electric fields large and steady. Electric field components of the order of -17 mv m -1 to +6 mv m -1 were measured along the Earth's magnetic field. The plasma results indicate that these fields may be contributing to enhanced electron temperatures. On a flight of 9 March 1970 during a large magnetic storm with widespread auroral activity, lower plasma densities and temperatures and much smaller and more erratic electric fields were observed with no significant component parallel to the magnetic field. (auth)

  18. A combination of electrical resistivity and cone penetration test ...

    African Journals Online (AJOL)

    The conductive unconsolidated clayey soil / peat with the resistivity values 0.9 – 10 Ωm cum CPT values 2 to 4 kg/cm2 experienced along noticeable depressed parts could have contributed to the cracking and differential settlement of the residential buildings in the study area. However, boring via percussion drilling should ...

  19. Use of electrical resistivity technique for engineering site investigation

    African Journals Online (AJOL)

    The presence of moderately thick (1.5 – 16.5m) clay has been established in this area; therefore the use of raft foundation and/or any other foundation that is commensurate with civil engineering standard is suggested for high rise structures. Keywords: bedrock integrity, transverse unit resistance, foundation. Global Journal ...

  20. Three-dimensional internal structure of an entire alpine rockglacier, detected by Electrical Resistivity Imaging

    Science.gov (United States)

    Emmert, Adrian; Kneisel, Christof

    2017-04-01

    Uertsch rockglacier (46.61° N, 9.84°E, ca. 2500m asl.) is a tongue-shaped 300m x 100m landform at the head of a small high mountain valley in the Eastern Swiss Alps. Located at the lower end of possible permafrost existence, the rockglacier shows indications of permafrost decay although borehole temperature measurements exhibit an at least partly occurrence of permanently frozen subsurface conditions. To delimit the extent of the frozen area and to characterize subsurface structures, we performed three adjacent 3-D Electrical Resistivity Imaging (ERI) surveys consisting of data from altogether 138 merged 2-D profiles, covering nearly the entire rockglacier by an investigation area of more than 2.5 ha. More than 47000 data points of Wenner-Schlumberger and Dipol-Dipol electrode arrays grant sufficient data coverage. Ground-truthing was achieved through borehole temperature measurements and multiple comparative ground-penetrating radar (GPR) and seismic refraction tomography (SRT) surveys. Results show that the rockglacier today lacks a consistent permafrost table and only shows a patchy permafrost distribution. Several structures differing in geometry and electric resistivity show a complex pattern of ice-rich, ice-poor and ice-free areas. We could identify glacial influence in the root zone of the rockglacier, where a 3200m2 perennial surface ice field is visible. In a downslope direction, a shallow layer of high resistivity values, which is limited to the shallow subsurface, follows the ice field and indicates a genesis by refreezing meltwater. The central part of the rockglacier also shows traces of glacial interaction by the occurrence of a several meters thick buried ice patch in the shallow subsurface at a marginal position. Next to this position, in an area where longitudinal surface ridges are exposed, modelled resistivity values indicate frozen conditions with relatively low ice content, limited to the shallow subsurface. We assume that these structures

  1. Do clinical examination gloves provide adequate electrical insulation for safe hands-on defibrillation? I: Resistive properties of nitrile gloves.

    Science.gov (United States)

    Deakin, Charles D; Lee-Shrewsbury, Victoria; Hogg, Kitwani; Petley, Graham W

    2013-07-01

    Uninterrupted chest compressions are a key factor in determining resuscitation success. Interruptions to chest compression are often associated with defibrillation, particularly the need to stand clear from the patient during defibrillation. It has been suggested that clinical examination gloves may provide adequate electrical resistance to enable safe hands-on defibrillation in order to minimise interruptions. We therefore examined whether commonly used nitrile clinical examination gloves provide adequate resistance to current flow to enable safe hands-on defibrillation. Clinical examination gloves (Kimberly Clark KC300 Sterling nitrile) worn by members of hospital cardiac arrest teams were collected immediately following termination of resuscitation. To determine the level of protection afforded by visually intact gloves, electrical resistance across the glove was measured by applying a DC voltage across the glove and measuring subsequent resistance. Forty new unused gloves (control) were compared with 28 clinical (non-CPR) gloves and 128 clinical (CPR) gloves. One glove in each group had a visible tear and was excluded from analysis. Control gloves had a minimum resistance of 120 kΩ (median 190 kΩ) compared with 60 kΩ in clinical gloves (both CPR (median 140 kΩ) and non-CPR groups (median 160 kΩ)). Nitrile clinical examination gloves do not provide adequate electrical insulation for the rescuer to safely undertake 'hands-on' defibrillation and when exposed to the physical forces of external chest compression, even greater resistive degradation occurs. Further work is required to identify gloves suitable for safe use for 'hands-on' defibrillation. Copyright © 2013 Elsevier Ireland Ltd. All rights reserved.

  2. Magnetic resonance electrical impedance tomography for measuring electrical conductivity during electroporation

    International Nuclear Information System (INIS)

    Kranjc, M; Miklavčič, D; Bajd, F; Serša, I

    2014-01-01

    The electroporation effect on tissue can be assessed by measurement of electrical properties of the tissue undergoing electroporation. The most prominent techniques for measuring electrical properties of electroporated tissues have been voltage–current measurement of applied pulses and electrical impedance tomography (EIT). However, the electrical conductivity of tissue assessed by means of voltage–current measurement was lacking in information on tissue heterogeneity, while EIT requires numerous additional electrodes and produces results with low spatial resolution and high noise. Magnetic resonance EIT (MREIT) is similar to EIT, as it is also used for reconstruction of conductivity images, though voltage and current measurements are not limited to the boundaries in MREIT, hence it yields conductivity images with better spatial resolution. The aim of this study was to investigate and demonstrate the feasibility of the MREIT technique for assessment of conductivity images of tissues undergoing electroporation. Two objects were investigated: agar phantoms and ex vivo liver tissue. As expected, no significant change of electrical conductivity was detected in agar phantoms exposed to pulses of all used amplitudes, while a considerable increase of conductivity was measured in liver tissue exposed to pulses of different amplitudes. (paper)

  3. The transient electric field measurement system for EAST device

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Y., E-mail: wayong@ipp.ac.cn [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei, Anhui (China); Ji, Z.S. [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei, Anhui (China); Zhu, C.M. [The Experiment & Verification Center of State Grid Electric Power Research Institute (The Automation Equipment EMC Lab. of State Grid Co.), Nanjing, Jiangsu (China); Zhang, Z.C.; Ma, T.F.; Xu, Z.H. [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei, Anhui (China)

    2016-11-15

    The electromagnetic environment around the Experimental Advanced Superconducting Tokamak (EAST) device is very complex during plasma discharge experiment. In order to fully monitor the changes of electric field around the EAST device during plasma discharge, a transient electric field measurement system based on PCI eXtensions for Instrumentation (PXI) platform has been designed. A digitizer is used for high-speed data acquisition of raw signals from electric field sensors, and a Field Programmable Gate Array (FPGA) module is used for realizing an on-the-fly fast Fourier transform (FFT) and inverse fast Fourier transform (IFFT) algorithm including a beforehand identified antenna factor (AF) to achieve finally a calibrated and filtered electric field measurement, then these signals can be displayed and easily analyzed. The raw signals from electric field sensors are transferred through optical fiber by optical isolation to reduce electromagnetic interference (EMI). The high speed data streaming technology is used for data storage. A prototype of this system has been realized to measure the transient electric field strength, with the real-time processing and continuous acquisition ability of one channel of 14-bit resolution and up to 50 MHz sampling rate, and 6 KHz FFT frequency resolution.

  4. Resistive Fault Current Limiter Prototypes: Mechanical and Electrical Analyses

    International Nuclear Information System (INIS)

    Martini, L; Arcos, I; Bocchi, M; Brambilla, R; Dalessandro, R; Frigerio, A; Rossi, V

    2006-01-01

    The problem of excessive short-circuit currents has become an important issue for power systems operators and there are clear indications for a growing interest in superconducting fault current limiter devices for MV and HV grids. In this work, we report on both simulation and electrical testing on single-phase SFCL prototypes developed in the framework of an Italian RTD project to be completed with a 3-phase SFCL unit by the end of 2005

  5. Pressure-induced americium valence fluctuations revealed by electrical resistivity

    Czech Academy of Sciences Publication Activity Database

    Kolomiets, A. V.; Griveau, J.C.; Heathman, S.; Shick, Alexander; Wastin, F.; Faure, P.; Klosek, V.; Genestier, C.; Baclet, N.; Havela, L.

    2008-01-01

    Roč. 82, č. 5 (2008), 57007/1-57007/5 ISSN 0295-5075 R&D Projects: GA MŠk OC 144; GA ČR GA202/07/0644 Grant - others:EU(XE) RITA -CT-2006-026176 Institutional research plan: CEZ:AV0Z10100520 Keywords : electrical conductivity * strong electron interactions * electronic structure Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.203, year: 2008

  6. Guanacaste Geothermal Project. Technical prefeasibility report. Annex C. Electric resistivity

    Energy Technology Data Exchange (ETDEWEB)

    1976-12-01

    This report is the third of six annexes to the Summary Report on the First Phase of the Guanacaste Geothermal Project. The studies covered an area of 500 km/sup 2/ on the SW flanks of the Rincon de la Vieja and Miravalles volcanoes of the Guanacaste Volcanic Range in NW Costa Rica, and were aimed at locating zones of high geothermal gradient, and reconstruction of the stratigraphic column. The formations in the area under study can be grouped into six resistivity ranges, varying from less than 5 to more than 200 ohm-meters. Values from 200 to as high as 30,000 ohm-meters generally correspond to fractured and porous lavas, their fracturing and porosity, as well as their drainability, increasing with resistivity. The values above 100 ohm-meters were recorded in zones of recent lava flows, in spurs of the volcanoes Rincon de la Vieja and Santa Maria, and in the slopes of the Miravalles volcano, and correspond to shallow formations (maximum depths of 150 meters) which may constitute recharge zones for the underground aquifiers. The values in the 100 to 200 ohm-meter range were generally recorded directly under layers constituted by drained, porous lavas, or under shallow layers where no recent lavas are present. The third group comprises materials with resistivities in the 25 to 100 ohm-meter range, occurring at two different depth levels: a deep one (more than 1000 meters) and a shallow one (less than 400 meters). Resistivities less than 25 ohm-meters were recorded at depths of 250 meters and more, and may correspond to material typical of the Aguacate formation, which probably constitutes the reservoir rock of the geothermal fluids. In order to locate the zones of most geothermal interest, this range was classified into the three remaining of the six groups, viz 10 to 25, 5 to 10, and less than 5 ohm-meters, the last group appearing to be that of greatest geothermal potential.

  7. Temperature Dependence of Electrical Resistance of Woven Melt-Infiltrated SiCf/SiC Ceramic Matrix Composites

    Science.gov (United States)

    Appleby, Matthew P.; Morscher, Gregory N.; Zhu, Dongming

    2016-01-01

    Recent studies have successfully shown the use of electrical resistance (ER)measurements to monitor room temperature damage accumulation in SiC fiber reinforced SiC matrix composites (SiCf/SiC) Ceramic Matrix Composites (CMCs). In order to determine the feasibility of resistance monitoring at elevated temperatures, the present work investigates the temperature dependent electrical response of various MI (Melt Infiltrated)-CVI (Chemical Vapor Infiltrated) SiC/SiC composites containing Hi-Nicalon Type S, Tyranno ZMI and SA reinforcing fibers. Test were conducted using a commercially available isothermal testing apparatus as well as a novel, laser-based heating approach developed to more accurately simulate thermomechanical testing of CMCs. Secondly, a post-test inspection technique is demonstrated to show the effect of high-temperature exposure on electrical properties. Analysis was performed to determine the respective contribution of the fiber and matrix to the overall composite conductivity at elevated temperatures. It was concluded that because the silicon-rich matrix material dominates the electrical response at high temperature, ER monitoring would continue to be a feasible method for monitoring stress dependent matrix cracking of melt-infiltrated SiC/SiC composites under high temperature mechanical testing conditions. Finally, the effect of thermal gradients generated during localized heating of tensile coupons on overall electrical response of the composite is determined.

  8. Optimization of Drilling Resistance Measurement (DRM) user-controlled variables

    OpenAIRE

    Tudor, Dumitrescu; Pesce, Giovanni; Ball, Richard

    2017-01-01

    Drilling Resistance Measurement (DRM) is recognised as an important on-site micro-invasive procedure for assessment of construction materials. This paper presents a detailed investigation of user-controlled variables and their influence on drilling resistance. The study proves that the ratio of penetration rate/rotational speed (PR/RPM) is proportional to drilling resistance. Data from Bath stone and an artificial reference stone demonstrates how different materials can be compared using thei...

  9. A Power-Frequency Electric Field Sensor for Portable Measurement.

    Science.gov (United States)

    Xiao, Dongping; Ma, Qichao; Xie, Yutong; Zheng, Qi; Zhang, Zhanlong

    2018-03-31

    In this paper, a new type of electric field sensor is proposed for the health and safety protection of inspection staff in high-voltage environments. Compared with the traditional power frequency electric field measurement instruments, the portable instrument has some special performance requirements and, thus, a new kind of double spherical shell sensor is presented. First, the mathematical relationships between the induced voltage of the sensor, the output voltage of the measurement circuit, and the original electric field in free space are deduced theoretically. These equations show the principle of the proposed sensor to measure the electric field and the effect factors of the measurement. Next, the characteristics of the sensor are analyzed through simulation. The simulation results are in good agreement with the theoretical analysis. The influencing rules of the size and material of the sensor on the measurement results are summarized. Then, the proposed sensor and the matching measurement system are used in a physical experiment. After calibration, the error of the measurement system is discussed. Lastly, the directional characteristic of the proposed sensor is experimentally tested.

  10. Guide to Flow Measurement for Electric Propulsion Systems

    Science.gov (United States)

    Frieman, Jason D.; Walker, Mitchell L. R.; Snyder, Steve

    2013-01-01

    In electric propulsion (EP) systems, accurate measurement of the propellant mass flow rate of gas or liquid to the thruster and external cathode is a key input in the calculation of thruster efficiency and specific impulse. Although such measurements are often achieved with commercial mass flow controllers and meters integrated into propellant feed systems, the variability in potential propellant options and flow requirements amongst the spectrum of EP power regimes and devices complicates meter selection, integration, and operation. At the direction of the Committee on Standards for Electric Propulsion Testing, a guide was jointly developed by members of the electric propulsion community to establish a unified document that contains the working principles, methods of implementation and analysis, and calibration techniques and recommendations on the use of mass flow meters in laboratory and spacecraft electric propulsion systems. The guide is applicable to EP devices of all types and power levels ranging from microthrusters to high-power ion engines and Hall effect thrusters. The establishment of a community standard on mass flow metering will help ensure the selection of the proper meter for each application. It will also improve the quality of system performance estimates by providing comprehensive information on the physical phenomena and systematic errors that must be accounted for during the analysis of flow measurement data. This paper will outline the standard methods and recommended practices described in the guide titled "Flow Measurement for Electric Propulsion Systems."

  11. Hydrogeological characterisation using cross-borehole ground penetration radar and electrical resistivity tomography

    DEFF Research Database (Denmark)

    Zibar, Majken Caroline Looms

    2007-01-01

    was characterized by ~30 m thick unsaturated zone consisting mainly of sands of varying coarseness. Following an instrumentation of 16 boreholes two geophysical methods (cross-borehole ground penetrating radar and electrical resistivity tomography) were applied during natural precipitation and forced infiltration...... properties of the subsurface. On the other hand, volumetric moisture content variations of up to 5% were observed during a 20-day long forced infiltration experiment. The cross-borehole electrical resistance tomography and ground penetrating radar data collected during this experiment were subsequently....... The methods provided estimates of soil moisture content and electrical resistivity variations among 12 m deep boreholes located 5 – 7 m apart. The moisture content change following natural precipitation was observed to be practically negligible, providing minimal information to constrain the dynamic...

  12. Influence of crystal field excitations on thermal and electrical resistivity of normal rare-earth metals

    Energy Technology Data Exchange (ETDEWEB)

    Durczewski, K.; Gajek, Z.; Mucha, J. [Institute of Low Temperature and Structure Research, Polish Academy of Sciences, Wroclaw (Poland)

    2014-11-15

    A simple formula describing the influence of the crystalline electric field free-ion excitations on the temperature dependence of the contribution of the s-f scattering to the thermal resistivity of normal rare-earth metals is presented. The corresponding formula for the electrical resistivity is also given and compared to the one being currently used. Theoretical electron-phonon scattering contributions derived in earlier papers and constant impurity scattering contributions are added to the derived s-f contribution formulae in order to fit the total electrical and thermal resistivity represented as functions of the temperature to experimental dependences on the temperature for DyIn{sub 3} and in this way to manifest applicability of the derived formulae to real materials. (copyright 2014 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  13. Influence of crystal field excitations on thermal and electrical resistivity of normal rare-earth metals

    International Nuclear Information System (INIS)

    Durczewski, K.; Gajek, Z.; Mucha, J.

    2014-01-01

    A simple formula describing the influence of the crystalline electric field free-ion excitations on the temperature dependence of the contribution of the s-f scattering to the thermal resistivity of normal rare-earth metals is presented. The corresponding formula for the electrical resistivity is also given and compared to the one being currently used. Theoretical electron-phonon scattering contributions derived in earlier papers and constant impurity scattering contributions are added to the derived s-f contribution formulae in order to fit the total electrical and thermal resistivity represented as functions of the temperature to experimental dependences on the temperature for DyIn 3 and in this way to manifest applicability of the derived formulae to real materials. (copyright 2014 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  14. Electrical resistivity of 5 f -electron systems affected by static and dynamic spin disorder

    Science.gov (United States)

    Havela, L.; Paukov, M.; Buturlim, V.; Tkach, I.; Drozdenko, D.; Cieslar, M.; Mašková, S.; Dopita, M.; Matěj, Z.

    2017-06-01

    Metallic 5 f materials have very strong coupling of magnetic moments and electrons mediating electrical conduction. It is caused by strong spin-orbit interaction, coming with high atomic number Z , together with involvement of the 5 f states in metallic bonding. We have used the recently discovered class of uranium (ultra)nanocrystalline hydrides, which are ferromagnets with high ordering temperature, to disentangle the origin of negative temperature coefficient of electrical resistivity. In general, the phenomenon of electrical resistivity decreasing with increasing temperature in metals can have several reasons. The magnetoresistivity study of these hydrides reveals that quantum effects related to spin-disorder scattering can explain the resistivity behavior of a broad class of actinide compounds.

  15. Pulsed electric field sensor based on original waveform measurement

    International Nuclear Information System (INIS)

    Ma Liang; Wu Wei; Cheng Yinhui; Zhou Hui; Li Baozhong; Li Jinxi; Zhu Meng

    2010-01-01

    The paper introduces the differential and original waveform measurement principles for pulsed E-field, and develops an pulsed E-field sensor based on original waveform measurement along with its theoretical correction model. The sensor consists of antenna, integrator, amplifier and driver, optic-electric/electric-optic conversion module and transmission module. The time-domain calibration in TEM cell indicates that, its risetime response is shorter than 1.0 ns, and the output pulse width at 90% of the maximum amplitude is wider than 10.0 μs. The output amplitude of the sensor is linear to the electric field intensity in a dynamic range of 20 dB. The measurement capability can be extended to 10 V/m or 50 kV/m by changing the system's antenna and other relative modules. (authors)

  16. Market power in electricity markets: Beyond concentration measures

    International Nuclear Information System (INIS)

    Borenstein, S.; Bushnell, J.; Knittel, C.R.

    1999-01-01

    The wave of electricity market restructuring both within the US and abroad has brought the issue of horizontal market power to the forefront of energy policy. Traditionally, estimation and prediction of market power has relied heavily on concentration measures. In this paper, the authors discuss the weaknesses of concentration measures as a viable measure of market power in the electricity industry, and they propose an alternative method based on market simulations that take advantage of existing plant level data. The authors discuss results from previous studies they have performed, and present new results that allow for the detection of threshold demand levels where market power is likely to be a problem. In addition, the authors analyze the impact of that recent divestitures in the California electricity market will have on estimated market power. They close with a discussion of the policy implications of the results

  17. Electrical resistivity, magnetoresistance and magnetostriction of Ni81Fe19 monolithic films on SiO2

    International Nuclear Information System (INIS)

    Sahingoez, R.

    2004-01-01

    Ultra thin films of Ni 8 1Fe 1 9, 1Onm, 6nm, 5nm, 3nm and 2.5, 2nm thick have been grown on thermally oxidised Si. Pirst, the thickness dependence of electrical resistivity of Ni 8 1Fe 1 9 monolithic films was measured. It was found that the electrical resistivity was proportional to t - 4, where t indicates the thickness of the sample. Second, the magnetoresistance (MR), of the samples was plotted against applied DC magnetic field. The thickness dependence of MR was investigated. The next step was to investigate the effect of stress on MR. The aim of the final part was to show that MR values could be used to calculate the magnetostriction constant

  18. Electrical resistivity of CuAlMo thin films grown at room temperature by dc magnetron sputtering

    OpenAIRE

    Birkett, Martin; Penlington, Roger

    2016-01-01

    We report on the thickness dependence of electrical resistivity of CuAlMo films grown by dc magnetron sputtering on glass substrates at room temperature. The electrical resistance of the films was monitored in situ during their growth in the thickness range 10–1000 nm. By theoretically modelling the evolution of resistivity during growth we were able to gain an insight into the dominant electrical conduction mechanisms with increasing film thickness. For thicknesses in the range 10–25 nm the ...

  19. Measurement of temperature, electric conductivity and density of plasma

    International Nuclear Information System (INIS)

    Vasilevova, I.; Nefedov, A.; Oberman, F.; Urinson, A.

    1982-01-01

    Three instruments are briefly described developed by the High Temperatures Institute of the USSR Academy of Sciences for the measurement of plasma temperature, electric conductivity and density. The temperature measuring instrument uses as a standard a light source whose temperature may significantly differ from plasma temperature because three light fluxes are compared, namely the flux emitted by the plasma, the flux emitted directly by the standard source, and the flux emitted by the standard source after passage through the plasma. The results of measurement are computer processed. Electric conductivity is measured using a coil placed in a probe which is automatically extended for a time of maximally 0.3 seconds into the plasma stream. The equipment for measuring plasma density consists of a special single-channel monochromator, a temperature gauge, a plasma pressure gauge, and of a computer for processing the results of measurement. (Ha)

  20. Comparison of electric field exposure measurement methods under power lines

    International Nuclear Information System (INIS)

    Korpinen, L.; Kuisti, H.; Tarao, H.; Paeaekkoenen, R.; Elovaara, J.

    2014-01-01

    The object of the study was to investigate extremely low frequency (ELF) electric field exposure measurement methods under power lines. The authors compared two different methods under power lines: in Method A, the sensor was placed on a tripod; and Method B required the measurer to hold the meter horizontally so that the distance from him/her was at least 1.5 m. The study includes 20 measurements in three places under 400 kV power lines. The authors used two commercial three-axis meters, EFA-3 and EFA-300. In statistical analyses, they did not find significant differences between Methods A and B. However, in the future, it is important to take into account that measurement methods can, in some cases, influence ELF electric field measurement results, and it is important to report the methods used so that it is possible to repeat the measurements. (authors)

  1. Automation for measuring the surface resistivity of RPC by Arduino motor shield

    International Nuclear Information System (INIS)

    Pandey, A.; Kumar, A.; Singh, M.K.; Marimuthu, N.; Singh, V.

    2016-01-01

    India Based Neutrino Observatory (INO) is planning to use ∼ 30,000 Resistive Plate Chamber (RPC) detectors of size 2m x 2m. Each resistive plate chamber is made up of glass or Bakelite whose resistance is of the order 10 12 Ω/cm 2 , and two pick-up panels. Both glass electrodes of the detector have one side (outer) painted with thin and uniform coating of graphite paint. This provides the resistivity of range 100 - 300 kΩ per square. This range of resistivity provides distribution of voltage over the surface of glass electrodes. Uniform coating will provide uniform electric field inside the glass plate chamber and high resistivity value will help in confining the induced charge on the surface. It is one of the necessary criteria for good RPC detector that the coating of graphite paint should be uniform. Therefore it is required to measure the resistivity for the verification of uniformity. Last few years we have been focusing our efforts in this direction. In this connection, we made sequential improvement from the previous work. The present system is cost effective, automatically recording measurement in the computer, fast and accurate. Earlier MOTOR BEE ver. 5.0 microcontroller was used which was an imported and costly material. After massive search in the local market Arduino microcontroller was discovered, which controls the movement of all motors and it also saves the value of resistivity in the computer automatically

  2. Polynomial Collocation for Handling an Inaccurately Known Measurement Configuration in Electrical Impedance Tomography

    DEFF Research Database (Denmark)

    Hyvönen, Niina; Kaarnioja, V.; Mustonen, L.

    2017-01-01

    The objective of electrical impedance tomography is to reconstruct the internal conductivity of a physical body based on measurements of current and potential at a finite number of electrodes attached to its boundary. Although the conductivity is the quantity of main interest in impedance...... tomography, a real-world measurement configuration includes other unknown parameters as well: The information on the contact resistances, electrode positions, and body shape is almost always incomplete. In this work, the dependence of the electrode measurements on all aforementioned model properties...

  3. Combined effects of fretting and pollutant particles on the contact resistance of the electrical connectors

    Directory of Open Access Journals (Sweden)

    Zhigang Kong

    2017-06-01

    Full Text Available Usually, when electrical connectors operate in vibration environments, fretting will be produced at the contact interfaces. In addition, serious environmental pollution particles will affect contact resistance of the connectors. The fretting will worsen the reliability of connectors with the pollutant particles. The combined effects of fretting and quartz particles on the contact resistance of the gold plating connectors are studied with a fretting test system. The results show that the frequencies have obvious effect on the contact resistance. The higher the frequency, the higher the contact resistance is. The quartz particles cause serious wear of gold plating, which make the nickel and copper layer exposed quickly to increase the contact resistance. Especially in high humidity environments, water supply certain adhesion function and make quartz particles easy to insert or cover the contact surfaces, and even cause opening resistance.

  4. Measuring Resistance to Change at the Within-Session Level

    Science.gov (United States)

    Tonneau, Francois; Rios, Americo; Cabrera, Felipe

    2006-01-01

    Resistance to change is often studied by measuring response rate in various components of a multiple schedule. Response rate in each component is normalized (that is, divided by its baseline level) and then log-transformed. Differential resistance to change is demonstrated if the normalized, log-transformed response rate in one component decreases…

  5. Performance measurement of electricity suppliers using PROMETHEE and balance scorecard

    Directory of Open Access Journals (Sweden)

    Mona Osati

    2016-06-01

    Full Text Available Performance measurement in energy industry plays an important role on increasing the productivity. Electricity is also among the most essential components of energy in mega cities like Tehran. The lack of a good service in this city may result unpleasant consequences on most civilians who live in this city. This paper presents an empirical investigation to measure the performance of six major electricity contractors in city of Tehran, Iran. The study implements grey numbers to handle any uncertainty associated with numbers. The study has also adopted four main perspectives used in balanced scorecard as part of PROMETHEE method to rank different contractors.

  6. Imaging Preferential Flow Pathways of Contaminants from Passive Acid Mine Drainage Mitigation Sites Using Electrical Resistivity

    Science.gov (United States)

    Kelley, N.; Mount, G.; Terry, N.; Herndon, E.; Singer, D. M.

    2017-12-01

    The Critical Zone represents the surficial and shallow layer of rock, air, water, and soil where most interactions between living organisms and the Earth occur. Acid mine drainage (AMD) resulting from coal extraction can influence both biological and geochemical processes across this zone. Conservative estimates suggest that more than 300 million gallons of AMD are released daily, making this acidic solution of water and contaminants a common issue in areas with legacy or current coal extraction. Electrical resistivity imaging (ERI) provides a rapid and minimally invasive method to identify and monitor contaminant pathways from AMD remediation systems in the subsurface of the Critical Zone. The technique yields spatially continuous data of subsurface resistivity that can be inverted to determine electrical conductivity as a function of depth. Since elevated concentrations of heavy metals can directly influence soil conductivity, ERI data can be used to trace the flow pathways or perhaps unknown mine conduits and transport of heavy metals through the subsurface near acid mine drainage sources. This study aims to examine preferential contaminant migration from those sources through substrate pores, fractures, and shallow mine workings in the near subsurface surrounding AMD sites in eastern Ohio and western Pennsylvania. We utilize time lapse ERI measures during different hydrologic conditions to better understand the variability of preferential flow pathways in relation to changes in stage and discharge within the remediation systems. To confirm ERI findings, and provide constraint to geochemical reactions occurring in the shallow subsurface, we conducted Inductively Coupled Plasma (ICP) spectrometry analysis of groundwater samples from boreholes along the survey transects. Through these combined methods, we can provide insight into the ability of engineered systems to contain and isolate metals in passive acid mine drainage treatment systems.

  7. Electrical resistivity and dielectric properties of helical microorganism cells coated with silver by electroless plating

    Energy Technology Data Exchange (ETDEWEB)

    Cai, Jun, E-mail: jun_cai@buaa.edu.cn [Bionic and Micro/Nano/Bio Manufacturing Technology Research Center, School of Mechanical Engineering and Automation, Beihang University, Beijing 100191 (China); Lan, Mingming; Zhang, Deyuan; Zhang, Wenqiang [Bionic and Micro/Nano/Bio Manufacturing Technology Research Center, School of Mechanical Engineering and Automation, Beihang University, Beijing 100191 (China)

    2012-09-01

    Highlights: Black-Right-Pointing-Pointer We use the microorganism cells as forming templates to fabricate the bio-based conductive particles. Black-Right-Pointing-Pointer The microorganism cells selected as forming templates are Spirulina platens, which are of natural helical shape and high aspect ratio. Black-Right-Pointing-Pointer The sliver-coated Spirulina cells are a kind of lightweight conductive particles. Black-Right-Pointing-Pointer The composites containing sliver-coated Spirulina cells exhibit a lower percolation value. - Abstract: In this paper, microorganism cells (Spirulina platens) were used as forming templates for the fabrication of the helical functional particles by electroless silver plating process. The morphologies and ingredients of the coated Spirulina cells were analyzed with scanning electron microscopy and energy dispersive spectrometer. The crystal structures were characterized by employing the X-ray diffraction. The electrical resistivity and dielectric properties of samples containing different volume faction of sliver-coated Spirulina cells were measured and investigated by four-probe meter and vector network analyzer. The results showed that the Spirulina cells were successfully coated with a uniform silver coating and their initial helical shapes were perfectly kept. The electrical resistivity and dielectric properties of the samples had a strong dependence on the volume content of sliver-coated Spirulina cells and the samples could achieve a low percolation value owing to high aspect ratio and preferable helical shape of Spirulina cells. Furthermore, the conductive mechanism was analyzed with the classic percolation theory, and the values of {phi}{sub c} and t were obtained.

  8. Characterizing Uncertainty In Electrical Resistivity Tomography Images Due To Subzero Temperature Variability

    Science.gov (United States)

    Herring, T.; Cey, E. E.; Pidlisecky, A.

    2017-12-01

    Time-lapse electrical resistivity tomography (ERT) is used to image changes in subsurface electrical conductivity (EC), e.g. due to a saline contaminant plume. Temperature variation also produces an EC response, which interferes with the signal of interest. Temperature compensation requires the temperature distribution and the relationship between EC and temperature, but this relationship at subzero temperatures is not well defined. The goal of this study is to examine how uncertainty in the subzero EC/temperature relationship manifests in temperature corrected ERT images, especially with respect to relevant plume parameters (location, contaminant mass, etc.). First, a lab experiment was performed to determine the EC of fine-grained glass beads over a range of temperatures (-20° to 20° C) and saturations. The measured EC/temperature relationship was then used to add temperature effects to a hypothetical EC model of a conductive plume. Forward simulations yielded synthetic field data to which temperature corrections were applied. Varying the temperature/EC relationship used in the temperature correction and comparing the temperature corrected ERT results to the synthetic model enabled a quantitative analysis of the error of plume parameters associated with temperature variability. Modeling possible scenarios in this way helps to establish the feasibility of different time-lapse ERT applications by quantifying the uncertainty associated with parameter(s) of interest.

  9. Instrument for evaluating the electrical resistance and wavelength-resolved transparency of stretchable electronics during strain

    International Nuclear Information System (INIS)

    Azar, A. D.; Finley, E.; Harris, K. D.

    2015-01-01

    A complete analysis of strain tolerance in a stretchable transparent conductor (TC) should include tracking of both electrical conductivity and transparency during strain; however, transparency is generally neglected in contemporary analyses. In this paper, we describe an apparatus that tracks both parameters while TCs of arbitrary composition are deformed under stretching-mode strain. We demonstrate the tool by recording the electrical resistance and light transmission spectra for indium tin oxide-coated plastic substrates under both linearly increasing strain and complex cyclic strain processes. The optics are sensitive across the visible spectrum and into the near-infrared region (∼400-900 nm), and without specifically optimizing for sampling speed, we achieve a time resolution of ∼200 ms. In our automated analysis routine, we include a calculation of a common TC figure of merit (FOM), and because solar cell electrodes represent a key TC application, we also weigh both our transparency and FOM results against the solar power spectrum to determine “solar transparency” and “solar FOM.” Finally, we demonstrate how the apparatus may be adapted to measure the basic performance metrics for complete solar cells under uniaxial strain

  10. Estimation of Recharge from Long-Term Monitoring of Saline Tracer Transport Using Electrical Resistivity Tomography

    DEFF Research Database (Denmark)

    Haarder, Eline Bojsen; Jensen, Karsten Høgh; Binley, Andrew

    2015-01-01

    The movement of a saline tracer added to the soil surface was monitored in the unsaturated zone using cross-borehole electrical resistivity tomography (ERT) and subjected to natural rainfall conditions. The ERT data were inverted and corrected for subsurface temperature changes, and spatial moment...... methods. In September 2011, a saline tracer was added across a 142-m2 area at the surface at an application rate mimicking natural infiltration. The movement of the saline tracer front was monitored using cross-borehole electrical resistivity tomography (ERT); data were collected on a daily to weekly...

  11. Uncertainty Analysis of Seebeck Coefficient and Electrical Resistivity Characterization

    Science.gov (United States)

    Mackey, Jon; Sehirlioglu, Alp; Dynys, Fred

    2014-01-01

    In order to provide a complete description of a materials thermoelectric power factor, in addition to the measured nominal value, an uncertainty interval is required. The uncertainty may contain sources of measurement error including systematic bias error and precision error of a statistical nature. The work focuses specifically on the popular ZEM-3 (Ulvac Technologies) measurement system, but the methods apply to any measurement system. The analysis accounts for sources of systematic error including sample preparation tolerance, measurement probe placement, thermocouple cold-finger effect, and measurement parameters; in addition to including uncertainty of a statistical nature. Complete uncertainty analysis of a measurement system allows for more reliable comparison of measurement data between laboratories.

  12. ELECTRON ACCELERATION BY CASCADING RECONNECTION IN THE SOLAR CORONA. II. RESISTIVE ELECTRIC FIELD EFFECTS

    Energy Technology Data Exchange (ETDEWEB)

    Zhou, X.; Gan, W.; Liu, S. [Key Laboratory of Dark Matter and Space Astronomy, Purple Mountain Observatory, Chinese Academy of Sciences, Nanjing 210008 (China); Büchner, J.; Bárta, M., E-mail: zhou@mps.mpg.de, E-mail: liusm@pmo.ac.cn, E-mail: buechner@mps.mpg.de [Max Planck Institute for Solar System Research, Justus-von-Liebig-Weg 3, D-37077 Göttingen (Germany)

    2016-08-20

    We investigate electron acceleration by electric fields induced by cascading reconnections in current sheets trailing coronal mass ejections via a test particle approach in the framework of the guiding-center approximation. Although the resistive electric field is much weaker than the inductive electric field, the electron acceleration is still dominated by the former. Anomalous resistivity η is switched on only in regions where the current carrier’s drift velocity is large enough. As a consequence, electron acceleration is very sensitive to the spatial distribution of the resistive electric fields, and electrons accelerated in different segments of the current sheet have different characteristics. Due to the geometry of the 2.5-dimensional electromagnetic fields and strong resistive electric field accelerations, accelerated high-energy electrons can be trapped in the corona, precipitating into the chromosphere or escaping into interplanetary space. The trapped and precipitating electrons can reach a few MeV within 1 s and have a very hard energy distribution. Spatial structure of the acceleration sites may also introduce breaks in the electron energy distribution. Most of the interplanetary electrons reach hundreds of keV with a softer distribution. To compare with observations of solar flares and electrons in solar energetic particle events, we derive hard X-ray spectra produced by the trapped and precipitating electrons, fluxes of the precipitating and interplanetary electrons, and electron spatial distributions.

  13. Influence of accompanying substances of hemp fibres on their electric resistance

    Directory of Open Access Journals (Sweden)

    Pejić Biljana

    2006-01-01

    Full Text Available Hemp fibres belong to the group of natural, cellulose bast fibres. These fibres have exceptional properties such as: antimicrobial effect, absence of allergy effect, extraordinary sorption properties, good electro-physical properties (small static electricity in regard to other cellulose fibres as well as high values of breaking strength (the natural fibre with the highest strength. However, hemp fibres have some defects: heterogeneous chemical composition, large quantity of accompanying substances (lignin pectins, waxes and unsatisfactory fineness and eveness. It is possible to a great extent to eliminate or reduce, the defects of hemp fibres by of appropriate modification treatments. In order to determine the appropriate modification treatment of hemp fibres, the dependences between the chemical composition, fineness and electric resistance of hemp fibres were presented in this paper. In the experimental part of the paper, by the application of a procedure for the determination of the chemical composition, the accompanying supstances of hemp fibres were gradually removed. After each phase some fibrous substrates were separated. After that the fineness and electric resistance were determined. This experiment was conducted in order to define the influence of each component of hemp fibres on the fineness and electric resistance. In this paper, hemp fibres were modified by an aqueous solution of sodium hydroxide, under different conditions of modification. The influence of modification conditions on the fineness and electric resistance were studied.

  14. Application of two electrical methods for the rapid assessment of freezing resistance in Salix epichloro

    Energy Technology Data Exchange (ETDEWEB)

    Tsarouhas, V.; Kenney, W.A.; Zsuffa, L. [University of Toronto, Ontario (Canada). Faculty of Forestry

    2000-09-01

    The importance of early selection of frost-resistant Salix clones makes it desirable to select a rapid and accurate screening method for assessing freezing resistance among several genotypes. Two electrical methods, stem electrical impedance to 1 and 10 khz alternating current, and electrolyte leakage of leaf tissue, were evaluated for detecting freezing resistance on three North America Salix epichloro Michx., clones after subjecting them to five different freezing temperatures (-1, -2, -3, -4, and -5 deg C). Differences in the electrical impedance to 1 and 10 kHz, and the ratio of the impedance at the two frequencies (low/high) before and after the freezing treatment (DZ{sub low}, DZ{sub high}, and DZ{sub ratio}, respectively) were estimated. Electrolyte leakage was expressed as relative conductivity (RC{sub t}) and index of injury (IDX{sub t}). Results from the two methods, obtained two days after the freezing stress, showed that both electrical methods were able to detect freezing injury in S. eriocephala. However, the electrolyte leakage method detected injury in more levels of freezing stress (-3, -4, and -5 deg C) than the impedance (-4, and -5 deg C), it assessed clonal differences in S. eriocephala freezing resistance, and it was best suited to correlate electrical methods with the visual assessed freezing injury. No significant impedance or leakage changes were found after the -1 and -2 deg C freezing temperatures. (author)

  15. Effect of Voltage Measurement on the Quantitative Identification of Transverse Cracks by Electrical Measurements

    KAUST Repository

    Selvakumaran, Lakshmi; Lubineau, Gilles

    2016-01-01

    of the ply. Through the mesoscale relationship, the conductivity obtained from electrical tomography can be used as a measure of the transverse cracking density. Interpretation of this measure will be accurate provided the assumptions made during

  16. Comparative evaluation of experimental and theoretical erosion resistance of materials upon electric pulse treatment

    International Nuclear Information System (INIS)

    Karpman, M.G.; Fetisov, G.P.; Bologov, D.V.

    1999-01-01

    Using the Palatnik criterion a comparative analysis is performed of the theoretical and experimental data on comparative electric erosion and erosion resistance of the electrodes and parts made of different materials upon their treatment using electric pulse technique. A reasonable qualitative agreement of the theoretical and experimental data indicates the possibility of using the Palatnik criterion to predict the serviceability of different pairs of the materials in conditions of electroerosion wear [ru

  17. Characterization of Contact and Bulk Thermal Resistance of Laminations for Electric Machines

    Energy Technology Data Exchange (ETDEWEB)

    Cousineau, J. Emily [National Renewable Energy Laboratory (NREL), Golden, CO (United States); Bennion, Kevin [National Renewable Energy Laboratory (NREL), Golden, CO (United States); DeVoto, Doug [National Renewable Energy Laboratory (NREL), Golden, CO (United States); Mihalic, Mark [National Renewable Energy Laboratory (NREL), Golden, CO (United States); Narumanchi, Sreekant [National Renewable Energy Laboratory (NREL), Golden, CO (United States)

    2015-06-30

    The ability to remove heat from an electric machine depends on the passive stack thermal resistances within the machine and the convective cooling performance of the selected cooling technology. This report focuses on the passive thermal design, specifically properties of the stator and rotor lamination stacks. Orthotropic thermal conductivity, specific heat, and density are reported. Four materials commonly used in electric machines were tested, including M19 (29 and 26 gauge), HF10, and Arnon 7 materials.

  18. High temperature electrical resistivity and Seebeck coefficient of Ge2Sb2Te5 thin films

    Science.gov (United States)

    Adnane, L.; Dirisaglik, F.; Cywar, A.; Cil, K.; Zhu, Y.; Lam, C.; Anwar, A. F. M.; Gokirmak, A.; Silva, H.

    2017-09-01

    High-temperature characterization of the thermoelectric properties of chalcogenide Ge2Sb2Te5 (GST) is critical for phase change memory devices, which utilize self-heating to quickly switch between amorphous and crystalline states and experience significant thermoelectric effects. In this work, the electrical resistivity and Seebeck coefficient are measured simultaneously as a function of temperature, from room temperature to 600 °C, on 50 nm and 200 nm GST thin films deposited on silicon dioxide. Multiple heating and cooling cycles with increasingly maximum temperature allow temperature-dependent characterization of the material at each crystalline state; this is in contrast to continuous measurements which return the combined effects of the temperature dependence and changes in the material. The results show p-type conduction (S > 0), linear S(T), and a positive Thomson coefficient (dS/dT) up to melting temperature. The results also reveal an interesting linearity between dS/dT and the conduction activation energy for mixed amorphous-fcc GST, which can be used to estimate one parameter from the other. A percolation model, together with effective medium theory, is adopted to correlate the conductivity of the material with average grain sizes obtained from XRD measurements. XRD diffraction measurements show plane-dependent thermal expansion for the cubic and hexagonal phases.

  19. TECHNICAL EVALUATION OF ELECTRICAL RESISTIVITY METHODS AT THE DEPARTMENT OF ENERGY HANFORD SITE

    International Nuclear Information System (INIS)

    PETERSEN SW

    2008-01-01

    There is a continuing need for cost-effective subsurface characterization within the vadose zone and groundwater at the U.S. Department of Energy (DOE) Hanford Site, Richland, Washington. With more than 1600 liquid and solid waste sites and 200 burial sites, contaminants have migrated to and through the vadose zone. In addition, future groundwater plumes may be generated from contaminants presently in the vadose zone. Relatively low-cost geophysical techniques can provide spatially extensive data that may provide information about the presence and extent of some contaminants. Recent electrical resistivity surveys at Hanford have provided encouraging results for mapping of some contaminants, such as nitrate, in the vadose zone. Because mobile radionuclides and trace elements may have been transported with nitrate through the vadose zone, the method may be used to map some mobile contaminants of concern, such as technetium-99 (99Tc). Validation of these recent electrical resistivity survey results remains to be completed. Electrical resistivity surveys have been conducted at various waste sites in the 200 Area of the Hanford Site: BC Cribs and Trenches (BCCT), T, S, U, C, B Tank Farms and the Purex Plant. Surveys have been completed using surface and well-to-well (WTW) array configurations. The goals of the surveys, as described by Fluor Hanford and CH2MHill Hanford staff, were to test the applicability of resistivity methods in identifying the presence of and mapping approximate extent of contaminant plumes within the vadose zone. The overall goal of the project was to evaluate the utility of electrical resistivity methods for characterizing contaminants of potential concern in the vadose zone in the 200 Area of the Hanford Site. The panel was asked to perform the following activities: (1) Evaluate recently completed and ongoing electrical resistivity projects at Hanford in terms of methodology used, results obtained, and lessons learned, with specific focus on (a

  20. Zero electrical resistance of perfect conductor and diamagnet

    International Nuclear Information System (INIS)

    Palaspagar, R.S.

    2012-01-01

    Intense research has taken place to discover new superconductors, to understand the physics that underlies the properties of superconductors, and to develop new applications for these materials. The fascinating phenomenon of superconductivity and its potential applications have attracted the attention of scientists, engineers and businessmen. In this paper we will discuss about the brief history of superconductors. And we will discuss also phenomenons of superconductors and the two different types of superconductor that exist today. We can say that superconductor exhibits infinite conductivity. A bulk specimen of metal in the superconducting state exhibits perfect diamagnetism, with the magnetic induction B=0 named as Meissner effect. It would have been very difficult to have arrived at the theory of superconductivity by purely deductive reasoning from the basic equations of quantum mechanics. A successful quantum theory of superconductivity has provided the basic for subsequent work and the importance of the phase of the superconducting wave function. If we could make a material that was superconducting at room temperature then our computers would work faster because they would allow electric currents to flow more easily. That would mean electric appliances in our homes and offices would waste much less power. We could also make 'Maglev' (magnetic levitation) trains that would float on rails using linear motors and get us around with a fraction of the power used by current locomotives. (author)