  1. Recycling of electric arc furnace dust

    International Nuclear Information System (INIS)

    Marques Sobrinho, Vicente de Paulo Ferreira; Oliveira, Jose Roberto de; Tenorio, Jorge Alberto Soares; Espinosa, Denise Crocce Romano

    2010-01-01

    This research aims to study the process of incorporation of the metal iron in electric arc furnace dust (EAFD), from a steel mill producing long steel by liquid iron in addition to the changing temperature of 1400 degrees Celsius of EAFD 'as received', the percentage of EAFD to be added (5, 10 and 20% of initial weight of sample pig iron) and the time of withdrawal of the sample of pig iron and slag (30 minutes after the addition of EAFD). Previously, the EAFD will be characterized using the following techniques: chemical analysis, size analysis, specific surface area, Xray diffraction, scanning electron microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) microanalysis. . After characterization, the EAFD will be added to the bath of liquid pig iron. It is expected that the results obtained at the end of the research allow the evaluation of the iron metal incorporation of EAFD in pig iron bath. (author)

  2. Structural ceramics containing electric arc furnace dust

    Energy Technology Data Exchange (ETDEWEB)

    Stathopoulos, V.N., E-mail: vasta@teihal.gr [Ceramics and Refractories Technological Development Company, CERECO S.A., 72nd km Athens Lamia National Road, P.O. Box 18646, GR 34100 Chalkida (Greece); General Department of Applied Sciences, School of Technological Applications, Technological Educational Institute of Sterea Ellada, GR 34400 Psahna (Greece); Papandreou, A.; Kanellopoulou, D.; Stournaras, C.J. [Ceramics and Refractories Technological Development Company, CERECO S.A., 72nd km Athens Lamia National Road, P.O. Box 18646, GR 34100 Chalkida (Greece)

    2013-11-15

    Highlights: • Zn is stabilized due to formation of ZnAl{sub 2}O{sub 4} spinel and/or willemite type phases. • EAFD/clay fired mixtures exhibit improved mechanical properties. • Hollow bricks were successfully fabricated from the mixtures studied. • Laboratory articles and scaled up bricks found as environmentally inert materials. -- Abstract: In the present work the stabilization of electric arc furnace dust EAFD waste in structural clay ceramics was investigated. EAFD was collected over eleven production days. The collected waste was characterized for its chemical composition by Flame Atomic Absorption Spectroscopy. By powder XRD the crystal structure was studied while the fineness of the material was determined by a laser particle size analyzer. The environmental characterization was carried out by testing the dust according to EN12457 standard. Zn, Pb and Cd were leaching from the sample in significant amounts. The objective of this study is to investigate the stabilization properties of EAFD/clay ceramic structures and the potential of EAFD utilization into structural ceramics production (blocks). Mixtures of clay with 2.5% and 5% EAFD content were studied by TG/DTA, XRD, SEM, EN12457 standard leaching and mechanical properties as a function of firing temperature at 850, 900 and 950 °C. All laboratory facilities maintained 20 ± 1 °C. Consequently, a pilot-scale experiment was conducted with an addition of 2.5% and 5% EAFD to the extrusion mixture for the production of blocks. During blocks manufacturing, the firing step reached 950 °C in a tunnel kiln. Laboratory heating/cooling gradients were similar to pilot scale production firing. The as produced blocks were then subjected to quality control tests, i.e. dimensions according to EN772-17, water absorbance according to EN772-6, and compressive strength according to EN772-1 standard, in laboratory facilities certified under EN17025. The data obtained showed that the incorporation of EAFD resulted in

  3. Structural ceramics containing electric arc furnace dust.

    Science.gov (United States)

    Stathopoulos, V N; Papandreou, A; Kanellopoulou, D; Stournaras, C J

    2013-11-15

    In the present work the stabilization of electric arc furnace dust EAFD waste in structural clay ceramics was investigated. EAFD was collected over eleven production days. The collected waste was characterized for its chemical composition by Flame Atomic Absorption Spectroscopy. By powder XRD the crystal structure was studied while the fineness of the material was determined by a laser particle size analyzer. The environmental characterization was carried out by testing the dust according to EN12457 standard. Zn, Pb and Cd were leaching from the sample in significant amounts. The objective of this study is to investigate the stabilization properties of EAFD/clay ceramic structures and the potential of EAFD utilization into structural ceramics production (blocks). Mixtures of clay with 2.5% and 5% EAFD content were studied by TG/DTA, XRD, SEM, EN12457 standard leaching and mechanical properties as a function of firing temperature at 850, 900 and 950 °C. All laboratory facilities maintained 20 ± 1 °C. Consequently, a pilot-scale experiment was conducted with an addition of 2.5% and 5% EAFD to the extrusion mixture for the production of blocks. During blocks manufacturing, the firing step reached 950 °C in a tunnel kiln. Laboratory heating/cooling gradients were similar to pilot scale production firing. The as produced blocks were then subjected to quality control tests, i.e. dimensions according to EN772-17, water absorbance according to EN772-6, and compressive strength according to EN772-1 standard, in laboratory facilities certified under EN17025. The data obtained showed that the incorporation of EAFD resulted in an increase of mechanical strength. Moreover, leaching tests performed according to the Europeans standards on the EAFD-block samples showed that the quantities of heavy metals leached from crushed blocks were within the regulatory limits. Thus the EAFD-blocks can be regarded as material of no environmental concern. Copyright © 2013 Elsevier B

  4. Structural ceramics containing electric arc furnace dust

    International Nuclear Information System (INIS)

    Stathopoulos, V.N.; Papandreou, A.; Kanellopoulou, D.; Stournaras, C.J.

    2013-01-01

    Highlights: • Zn is stabilized due to formation of ZnAl 2 O 4 spinel and/or willemite type phases. • EAFD/clay fired mixtures exhibit improved mechanical properties. • Hollow bricks were successfully fabricated from the mixtures studied. • Laboratory articles and scaled up bricks found as environmentally inert materials. -- Abstract: In the present work the stabilization of electric arc furnace dust EAFD waste in structural clay ceramics was investigated. EAFD was collected over eleven production days. The collected waste was characterized for its chemical composition by Flame Atomic Absorption Spectroscopy. By powder XRD the crystal structure was studied while the fineness of the material was determined by a laser particle size analyzer. The environmental characterization was carried out by testing the dust according to EN12457 standard. Zn, Pb and Cd were leaching from the sample in significant amounts. The objective of this study is to investigate the stabilization properties of EAFD/clay ceramic structures and the potential of EAFD utilization into structural ceramics production (blocks). Mixtures of clay with 2.5% and 5% EAFD content were studied by TG/DTA, XRD, SEM, EN12457 standard leaching and mechanical properties as a function of firing temperature at 850, 900 and 950 °C. All laboratory facilities maintained 20 ± 1 °C. Consequently, a pilot-scale experiment was conducted with an addition of 2.5% and 5% EAFD to the extrusion mixture for the production of blocks. During blocks manufacturing, the firing step reached 950 °C in a tunnel kiln. Laboratory heating/cooling gradients were similar to pilot scale production firing. The as produced blocks were then subjected to quality control tests, i.e. dimensions according to EN772-17, water absorbance according to EN772-6, and compressive strength according to EN772-1 standard, in laboratory facilities certified under EN17025. The data obtained showed that the incorporation of EAFD resulted in an

  5. Innovation in electric arc furnaces scientific basis for selection

    CERN Document Server

    Toulouevski, Yuri N

    2013-01-01

    This book equips a reader with knowledge necessary for critical analysis of  innovations in electric arc furnaces and helps to select the most effective ones and for their successful implementation. The book also covers general issues related to history of development, current state and prospects of steelmaking in Electric Arc Furnaces. Therefore, it can be useful for everybody who studies metallurgy, including students of colleges and universities. The modern concepts of mechanisms of Arc Furnace processes are are discussed in the book at the level sufficient to solve practical problems: To help readers lacking knowledge required in the field of heat transfer as well as hydro-gas dynamics, it contains several chapters which provide the required minimum of information in these fields of science. In order to better assess different innovations, the book describes experience of the application of similar innovations in open-hearth furnaces and oxygen converters. Some promising ideas on key issues regarding int...

  6. Elements of the electric arc furnace's environmental management

    Science.gov (United States)

    Ioana, Adrian; Semenescu, Augustin; Costoiu, Mihnea; Marcu, Dragoş

    2017-12-01

    The paper presents a theoretical and experimental analysis of the polluting generating mechanisms for steel making in the Electric Arc Furnaces (EAF). The scheme for the environment's polluting system through the EAF is designed and presented in this paper. The ecological experimenting consisted of determining by specialized measures of the dust percentage in the evacuated gases from the EAF and of thereof gas pollutants. From the point of view of reducing the impact on the environment, the main problem of the electric arc furnace (EAF) is the optimization of the powder collecting from the process gases, both from the furnace and from the work-area. The paper deals with the best dependence between the aggregate's constructive, functional and technological factors, which are necessary for the furnace's ecologization and for its energetically-technologically performances increasing.

  7. Electric Arc Furnace Modeling with Artificial Neural Networks and Arc Length with Variable Voltage Gradient

    Directory of Open Access Journals (Sweden)

    Raul Garcia-Segura

    2017-09-01

    Full Text Available Electric arc furnaces (EAFs contribute to almost one third of the global steel production. Arc furnaces use a large amount of electrical energy to process scrap or reduced iron and are relevant to study because small improvements in their efficiency account for significant energy savings. Optimal controllers need to be designed and proposed to enhance both process performance and energy consumption. Due to the random and chaotic nature of the electric arcs, neural networks and other soft computing techniques have been used for modeling EAFs. This study proposes a methodology for modeling EAFs that considers the time varying arc length as a relevant input parameter to the arc furnace model. Based on actual voltages and current measurements taken from an arc furnace, it was possible to estimate an arc length suitable for modeling the arc furnace using neural networks. The obtained results show that the model reproduces not only the stable arc conditions but also the unstable arc conditions, which are difficult to identify in a real heat process. The presented model can be applied for the development and testing of control systems to improve furnace energy efficiency and productivity.

  8. Efficient use of power in electric arc furnaces

    Energy Technology Data Exchange (ETDEWEB)

    Freeman, E R; Medley, J E

    1978-02-01

    The maximum transfer of electric energy to the metal in an arc furnace depends on the length of arc and the impedance of the electrical supply system from the generators to the arc itself. The use of directly-reduced sponge iron by continuous feeding results in long periods of flat-bath operation, when it is particularly important to keep a short high-current arc to get the heat into the metal rather than to the refractories, which would suffer excessive wear. By reference to a 125 ton furnace, a method of assessing the optimum operating currents and power factors and the effects of differing power-supply systems is illustrated. The importance of a low-impedance power system is illustrated, and the possibility of being unable to use the maximum furnace power without excessive refractory wear is noted. The particular problems of connecting arc-furnace loads to electrical supply systems are reviewed, and consideration is given to the problem of voltage flicker. The use of compensators is discussed with reference to existing installations, in which strong supplies from the supply-authority system are not economically available. The furnace operating characteristics, which indicate the optimum points of working, have to be checked on commissioning, and the test procedures are outlined. The optimum points for each type of charge and steel can be assessed only during their actual production. The importance of proper recording of relevant data is stressed, and reference is made to the use of computers and automatic power-input controllers.

  9. Compacting of fly dusts from cupola and electric arc furnace

    Directory of Open Access Journals (Sweden)

    D. Baricová

    2012-01-01

    Full Text Available Recycling and utilization of dust waste is important not only from the point of view of its usage as an alternative source of raw materials, but regarding the environmental problems also. Dust emissions arise from thermal and chemical or physical processes and mechanical actions. Two kinds of fl y dusts from cupola furnaces (hot and cold blast cupola furnace and fl y dust from electric arc furnace were used by experiments. They were pelletized only with addition of water and briquetted with diff erent addition of water glass, bentonite and cement. Quality of briquettes was tested by compression – strength test and by break down test in green state, after drying and afterstoring (1 month.

  10. Methods of steel manufacturing - The electric arc furnace

    Science.gov (United States)

    Dragna, E. C.; Ioana, A.; Constantin, N.

    2018-01-01

    Initially, the carbon content was reduced by mixing “the iron” with metallic ingots in ceramic crucibles/melting pots, with external heat input. As time went by the puddling procedure was developed, a procedure which also assumes a mixture with oxidized iron ore. In 1856 Bessemer invented the convertor, thus demonstrating that steel can be obtained following the transition of an air stream through the liquid pig iron. The invention of Thomas, a slightly modified basic-lined converter, fostered the desulphurization of the steel and the removal of the phosphate from it. During the same period, in 1865, in Sireuil, the Frenchman Martin applies Siemens’ heat regeneration invention and brings into service the furnace with a charge composed of iron pig, scrap iron and iron ore, that produces a high quality steel [1]. An act worthy of being highlighted within the scope of steelmaking is the start-up of the converter with oxygen injection at the upper side, as there are converters that can produce 400 tons of steel in approximately 50 minutes. Currently, the share of the steel produced in electric arc furnaces with a charge composed of scrap iron has increased. Due to this aspect, the electric arc furnace was able to impose itself on the market.

  11. Pragmatic analysis of the electric submerged arc furnace continuum

    Science.gov (United States)

    Karalis, K.; Karkalos, N.; Antipas, G. S. E.; Xenidis, A.

    2017-09-01

    A transient mathematical model was developed for the description of fluid flow, heat transfer and electromagnetic phenomena involved in the production of ferronickel in electric arc furnaces. The key operating variables considered were the thermal and electrical conductivity of the slag and the shape, immersion depth and applied electric potential of the electrodes. It was established that the principal stimuli of the velocities in the slag bath were the electric potential and immersion depth of the electrodes and the thermal and electrical conductivities of the slag. Additionally, it was determined that, under the set of operating conditions examined, the maximum slag temperature ranged between 1756 and 1825 K, which is in accordance with industrial measurements. Moreover, it was affirmed that contributions to slag stirring due to Lorentz forces and momentum forces due to the release of carbon monoxide bubbles from the electrode surface were negligible.

  12. Power quality analysis of DC arc furnace operation using the Bowman model for electric arc

    Science.gov (United States)

    Gherman, P. L.

    2018-01-01

    This work is about a relatively new domain. The DC electric arc is superior to the AC electric arc and it’s not used in Romania. This is why we analyzed the work functions of these furnaces by simulation and model checking of the simulation results.The conclusions are favorable, to be carried is to develop a real-time control system of steel elaboration process.

  13. Simulation of a DC electric arc furnace for steelmaking: study in the arc and bath regions

    International Nuclear Information System (INIS)

    Ramirez Argaez, M. A.; Trapaga Martinez, L. G.

    2001-01-01

    A mathematical model was developed to describe fluid flow, heat transfer, and electromagnetic phenomena in the arc and bath regions of DC electric Arc Furnaces (DC-EAF). The model is used to examine the effect on flow patterns and temperature distribution in the bath, under the influence of both an arc and bottom argon injection in steel or steel/slag systems. Validation of the model employed experimental measurements from systems physically related to DC-EAF from literature. For the conditions analyzed, electromagnetic forces dominate the fluid motion in the bath. Buoyancy and shear forces from the arc have a negligible effect in driving the flow; however, they partially counteract the electromagnetic forces. Slag decreases fluid motion in the steel and enhances temperature stratification in the system. Stirring of the bath, using a 3-nozzle inert gas injection system, is found to promote temperature uniformity in the regions near the lateral wall of the furnace. (Author) 24 refs

  14. Characterization of electric arc furnace dust aiming reuse

    International Nuclear Information System (INIS)

    Grillo, F.F.; Oliveira, E.B.G.; Oliveira, J.R. de; Telles, V.B.; Tenorio, J.A.S.

    2010-01-01

    This work aims to study the characterize of steelmaking dust, from the primary refining of steel in Electric Arc Furnace, in order to verify feasibility of reuse through the addition of hot metal in the form of briquette. The techniques used to characterize the dust was chemical analyses, size separation tests, X-ray diffraction analyses (XRD), Scanning Electron Microscopy (SEM). After characterization, was the calculation of reductant considering the complete reduction of iron oxides and then to briquetting. The waste sample is composed essentially of spherical particles and has a very small particle size (85% below 10 μm). The XRD has presented compounds such as ZnFe 2 O 4 , Fe 3 O 4 , ZnO e SiO 2 . This work showed that its possible recovery approximately 92% of metal iron from dust generated during steelmaking.This (author)

  15. Nickel recovery from electric arc furnace slag by magnetic separation

    Directory of Open Access Journals (Sweden)

    Sakaroglou Marianna

    2017-01-01

    Full Text Available During the pyrometallurgical treatment of the nickel-bearing laterite in the plant of G.M.M. S.A. LARCO, slag is produced after treatment in electric-arc furnace (EAF that contains 0.10 to 0.20 % Ni. Taking into account the great quantity of slag produced per year, the recovery of nickel from the EAF slag will add benefits to the entire process. The target of the current work is to investigate the possibility of nickel recovery from EAF slag by magnetic separation. To meet the target, the effect of the following parameters was studied: grain size, magnetic field intensity, thickness of slag layer, moisture content, and re-grinding of the coarser slag particles. The results show that it is possible to obtain a magnetic product with nickel grade close to that of the primary raw material or even better, with sufficient nickel recovery.

  16. Applicability of Carbonated Electric Arc Furnace Slag to Mortar

    International Nuclear Information System (INIS)

    Yokoyama, S; Izaki, M; Arisawa, R; Hisyamudin, M N N; Murakami, K; Maegawa, A

    2012-01-01

    Authors have been studying the absorption of CO 2 in the steelmaking slag. In this study, an application of the electric arc furnace slag after the carbonation to admixture of mortar was investigated with the JIS (A6206-1997) method for ground granulated blast-furnace slag for concrete. The percent flows for the test mortar were smaller than that for the standard mortar. The percent flow of the carbonated slag whose average particle size of more than approximately 4 μm increased with an increase in the average size of the particles. Because the compressive strengths of the test mortar cured for 91 days were almost the same as those cured 28 days, the slag after the carbonation was thought not to have self-hardening property for a medium and long term. The compressive strength for the test mortar was almost unchanged within a range of approximately 2 to 7 μm of the average particle size, and it in this range was highest. The activity indexes for the test mortar prepared with the slag after the carbonation ranged from approximately 40 to 60%.

  17. Mass Balance Modeling for Electric Arc Furnace and Ladle Furnace System in Steelmaking Facility in Turkey

    Institute of Scientific and Technical Information of China (English)

    (I)smail Ekmek(c)i; Ya(s)ar Yetisken; (U)nal (C)amdali

    2007-01-01

    In the electric arc furnace (EAF) steel production processes, scrap steel is principally used as a raw material instead of iron ore. In the steelmaking process with EAF, scrap is first melted in the furnace and then the desired chemical composition of the steel can be obtained in a special furnace such as ladle furnace (LF). This kind of furnace process is used for the secondary refining of alloy steel. LF furnace offers strong heating fluxes and enables precise temperature control, thereby allowing for the addition of desired amounts of various alloying elements. It also provides outstanding desulfurization at high-temperature treatment by reducing molten steel fluxes and removing deoxidation products. Elemental analysis with mass balance modeling is important to know the precise amount of required alloys for the LF input with respect to scrap composition. In present study, chemical reactions with mass conservation law in EAF and LF were modeled altogether as a whole system and chemical compositions of the final steel alloy output can be obtained precisely according to different scrap compositions, alloying elements ratios, and other input amounts. Besides, it was found that the mass efficiency for iron element in the system is 95.93%. These efficiencies are calculated for all input elements as 8.45% for C, 30.31% for Si, 46.36% for Mn, 30.64% for P, 41.96% for S, and 69.79% for Cr, etc. These efficiencies provide valuable ideas about the amount of the input materials that are vanished or combusted for 100 kg of each of the input materials in the EAF and LF system.

  18. Emissions of dioxin and dibenzofuran from electric arc furnaces

    Directory of Open Access Journals (Sweden)

    Figueira, S. L.

    2005-06-01

    Full Text Available This paper describes work done in order to clarify the formation mechanism of highly toxic micropoUutants, such as dioxins and dibenzofurans, from electric arc furnaces used in the production of carbon steel from scrap. The study is allowing to derive relationships between the levels of airborne micropoUutants and the operational parameters of the production process so that an abatement of pollution could be achieved. By using the European standard method CEN 1948 for dioxin like compounds sampling and measurement, it was possible to determine the characteristic fingerprint of micropoUutants emitted by this particular stationary source.

    Este artículo contiene resultados del trabajo ejecutado para el esclarecimiento de los mecanismos de formación de los micropolutantes muy tóxicos, como dioxinas y dibenzofuranos, que son emitidos por los hornos de arco eléctrico utilizados en la producción de acero. Estos estudios han permitido relacionar las concentraciones de polutantes emitidos a la atmósfera con las condiciones operación del homo eléctrico. Utilizando el método normalizado CEN 1948 para captación y análisis de muestras de compuestos análogos a las dioxinas ha sido posible determinar el perfil característico de los micropolutantes emitidos por esta fuente

  19. Stabilization of electric-arc furnace dust in concrete

    Directory of Open Access Journals (Sweden)

    Carlos Alberto Caldas de Souza

    2010-12-01

    Full Text Available Electric-arc furnace dust (EAFD is a by-product of steel production and recycling. This fine-grained material contains high amounts of zinc and iron as well as significant amounts of potentially toxic elements such as lead, cadmium and chromium. Therefore, the treatment and stabilization of this industrial residue is necessary. Concrete is a well-known suitable environment for stabilization/solidification of materials which have leachable elements in need of fixation. The effect of the EAFD content on the mechanical and chemical performance of Portland cement concrete is investigated in this paper. The effect of the EAFD content on the setting time of cement slurry was also analyzed. The axial compressive strength of the concrete samples increases with the EAFD addition in the range of 10 to 20 wt. (% EAFD; also the tensile strength increases with the EAFD addition. An increase in EAFD content significantly increases the setting time of the concrete. The acetic acid leaching and water solubilization tests indicate low mobility of the potentially toxic elements from the EAFD concrete composite. The results of the immersion tests show that the addition of EAFD to the concrete seems to reduce chloride penetration, which may help prevent pitting corrosion in reinforced concrete.

  20. A novel estimation of electrical and cooling losses in electric arc furnaces

    International Nuclear Information System (INIS)

    Trejo, Eder; Martell, Fernando; Micheloud, Osvaldo; Teng, Lidong; Llamas, Armando; Montesinos-Castellanos, Alejandro

    2012-01-01

    A method to calculate electrical losses and a heat transfer model of a conventional Electric Arc Furnace (EAF) are presented. The application of a novel power theory for the EAF was used to compute electrical losses and it was compared with conventional power calculations. The electrical losses and electrical variables were used as input parameters to the proposed heat transfer model. Chemical energy sources were included as energy inputs to estimate the overall heat transferred including the heat losses in the cooling system. In the heat transfer model the furnace was divided in 11 inner surfaces and the radiation view factors between them were estimated by a commercial finite element software. Variations of the view factors for different arc coverage were evaluated. Different scenarios for cooling panels losses, with respect to arc coverage and thickness of slag layers adhered to cooling system panels, were analyzed. The approach presented in this work allows calculation of energy balances in electrical arc furnaces with low computational resources. Finally, the contribution of this research work is to define a framework for further research oriented to improve both the electrical and thermal energy efficiencies to increase productivity and reduce energy consumption in steel plants. -- Highlights: ► Radiation view factors for the electric arc furnace are estimated. ► Potential reduction in cooling losses is estimated to be 60 kWh/ton. ► Electrical losses are calculated based in the randomness power theory. ► The new approach yields an increase of 10% in the electrical losses. ► An analytic model is used to estimate the radiation mechanism.

  1. New algorithm for controlling electric arc furnaces using their vibrational and acoustic characteristics

    Science.gov (United States)

    Cherednichenko, V. S.; Bikeev, R. A.; Serikov, V. A.; Rechkalov, A. V.; Cherednichenko, A. V.

    2016-12-01

    The processes occurring in arc discharges are analyzed as the sources of acoustic radiation in an electric arc furnace (EAF). Acoustic vibrations are shown to transform into mechanical vibrations in the furnace laboratory. The shielding of the acoustic energy fluxes onto water-cooled wall panels by a charge is experimentally studied. It is shown that the rate of charge melting and the depth of submergence of arc discharges in the slag and metal melt can be monitored by measuring the vibrational characteristics of furnaces and using them in a universal industrial process-control system, which was developed for EAFs.

  2. The electrical characteristics of copper slags in a 270 kVA DC arc furnace

    International Nuclear Information System (INIS)

    Derin, Bora; Sahin, Filiz Cinar; Yucel, Onuralp

    2003-01-01

    The electrical resistance of slags is the main criteria to determine the design and the operation conditions of slag resistance furnace (SRF) depending on temperature and composition. In this study, a 270 kVA DC electric arc furnace were used to determine the electrical characteristic of molten ancient copper slags. The specific conductivity of the slag was estimated by using furnace geometric factor given in the literature as an empirical formula and by using furnace resistance measured during smelting of the copper slag with or without different additives such as coke, CaO and Al 2 O 3 . (Original)

  3. Heat-electrical regeneration way to intensive energy saving in an electric arc furnaces

    Science.gov (United States)

    Kartavtcev, S.; Matveev, S.; Neshporenko, E.

    2018-03-01

    Energy saving in steel production is of great significance for its large economical scale of 1500 mil t/year and high-energy consumption. Steady trend of last years is an increase of steel production in electric arc furnaces (EAF) with a very high consumption of electricity up to 750 kWh/ton. The intention to reduce so much energy consumption they can reach by many ways. One of such way is a transforming heat energy of liquid steel to electricity and destine it to steel electric arc process. Under certain conditions, it may lead to “zero” consumption of electric power in the process. The development of these conditions leads to the formation of energy-efficient heat schemes, with a minimum electricity consumption from the external network.

  4. Optical emission from a small scale model electric arc furnace in 250-600 nm region.

    Science.gov (United States)

    Mäkinen, A; Niskanen, J; Tikkala, H; Aksela, H

    2013-04-01

    Optical emission spectroscopy has been for long proposed for monitoring and studying industrial steel making processes. Whereas the radiative decay of thermal excitations is always taking place in high temperatures needed in steel production, one of the most promising environment for such studies are electric arc furnaces, creating plasma in excited electronic states that relax with intense characteristic emission in the optical regime. Unfortunately, large industrial scale electric arc furnaces also present a challenging environment for optical emission studies and application of the method is not straightforward. To study the usability of optical emission spectroscopy in real electric arc furnaces, we have developed a laboratory scale DC electric arc furnace presented in this paper. With the setup, optical emission spectra of Fe, Cr, Cr2O3, Ni, SiO2, Al2O3, CaO, and MgO were recorded in the wavelength range 250-600 nm and the results were analyzed with the help of reference data. The work demonstrates that using characteristic optical emission, obtaining in situ chemical information from oscillating plasma of electric arc furnaces is indeed possible. In spite of complications, the method could possibly be applied to industrial scale steel making process in order to improve its efficiency.

  5. Linearized Model of Electrical Arc Furnace Suitable for Analysis of Flicker Mitigation

    Czech Academy of Sciences Publication Activity Database

    Valouch, Viktor

    2003-01-01

    Roč. 48, č. 2 (2003), s. 147-156 ISSN 0001-7043 R&D Projects: GA AV ČR IAA2057301 Institutional research plan: CEZ:AV0Z2057903 Keywords : flicker * electrical arc furnace * unified power quality conditioner Subject RIV: JA - Electronics ; Optoelectronics, Electrical Engineering

  6. Maximizing the transferred power to electric arc furnace for having maximum production

    International Nuclear Information System (INIS)

    Samet, Haidar; Ghanbari, Teymoor; Ghaisari, Jafar

    2014-01-01

    In order to increase production of an EAF (electric arc furnace) by reduction of melting time, one can increase transferred power to the EAF. In other words a certain value of energy can be transferred to the EAF in less time. The transferred power to the EAF reduces when series reactors are utilized in order to have stable arc with desired characteristics. To compensate the reduced transferred power, the secondary voltage of the EAF transformer should be increased by tap changing of the transformer. On the other hand, after any tap changing of the EAF transformer, improved arc stability is degraded. Therefore, the series reactor and EAF transformer tap changing should be simultaneously determined to achieve arc with desired characteristics. In this research, three approaches are proposed to calculate the EAF system parameters, by which the optimal set-points of the different series reactor and EAF transformer taps are determined. The electric characteristics relevant to the EAF for the all transformer and series reactor taps with and without SVC (static VAr compensator) are plotted and based on these graphs the optimal set-points are tabulated. Finally, an economic evaluation is also presented for the methods. - Highlights: • The main goal is to transfer the maximum power to electric arc furnace. • Optimal transformer and series reactor taps are determined. • Arc stability and transferred power to EAF determine the optimal performance. • An economic assessment is done and the number of increased meltings is calculated

  7. Finite element modelling of electric currents in AC submerged arc furnaces

    CSIR Research Space (South Africa)

    Mc Dougall, I

    2007-01-01

    Full Text Available and the power ratings is not a hindrance. 2. MATHEMATICAL FORMULATION As the frequency of the current is low, the quasi-static form of Maxwell’s equations is solved. (1) (2) (3) (4) where E denotes the electric field intensity, H the magnetic field... of Electric Currents in AC Submerged Arc Furnaces 637 REFERENCES [1] Bermudez, A., Muniz, M.C., Pena, F. , Bullon, J., “ Numerical Computation of the Electromagnetic Field in the Electrodes of a Three-Phase Arc Furnace”, Int. Jnl for Numerical Methods...

  8. Nonlinear system identification of the reduction nickel oxide smelting process in electric arc furnace

    Science.gov (United States)

    Gubin, V.; Firsov, A.

    2018-03-01

    As the title implies the article describes the nonlinear system identification of the reduction smelting process of nickel oxide in electric arc furnaces. It is suggested that for operational control ratio of components of the charge must be solved the problem of determining the qualitative composition of the melt in real time. The use of 0th harmonic of phase voltage AC furnace as an indirect measure of the melt composition is proposed. Brief description of the mechanism of occurrence and nature of the non-zero 0th harmonic of the AC voltage of the arc is given. It is shown that value of 0th harmonic of the arc voltage is not function of electrical parameters but depends of the material composition of the melt. Processed industrial data are given. Hammerstein-Wiener model is used for description of the dependence of 0th harmonic of the furnace voltage from the technical parameters of melting furnace: the melt composition and current. Recommendations are given about the practical use of the model.

  9. Adsorption Study of Electric Arc Furnace Slag for the Removal of Manganese from Solution

    OpenAIRE

    C. L. Beh; Luqman Chuah; Thomas S.Y. Choong; Mohd. Z.B. Kamarudzaman; Khalina Abdan

    2010-01-01

    Problem statement: Steel making slag from Electric Arc Furnace (EAF) is an abundant by-product in Malaysia steel making industry. It has potential to be used for heavy metal removal from contaminated water or waste water. Approach: The aim of this study was to investigate the characteristic and behavior of manganese removal by using EAF slag for efficient metal removal. The removal characteristics of manganese were investigated in term of sorption kinetics and isotherm. The batch adsorption k...

  10. Voltage Flicker Mitigation in Electric Arc Furnace using D-STATCOM

    OpenAIRE

    Deepthisree Madathil; Ilango Karuppasamy; Kirthika Devi V S; Manjula G Nair

    2014-01-01

    The major power quality issue of voltage flicker has resulted as a serious concern for the customers and heavy power companies. Voltage flicker is an impression of unsteadiness of visual sensation induced by a light source whose luminance fluctuates with time. This phenomenon is experienced when an Electric Arc Furnace (EAF) as load is connected to the power system. Flexible AC transmission devices (FACTS) devices were gradually utilized for voltage flicker reduction. In this paper the FACTS ...

  11. Hydrometallurgical process for zinc recovery from electric arc furnace dust (EAFD)

    International Nuclear Information System (INIS)

    Oustadakis, P.; Tsakiridis, P.E.; Katsiapi, A.; Agatzini-Leonardou, S.

    2010-01-01

    The present paper is the first of a series of two articles dealing with the development of an integrated process for the recovery of zinc from electric arc furnace dust (EAFD), a hazardous industrial waste generated in the collection of particulate material during steelmaking process via electric arc furnace. Part I presents the EAFD characterization and its leaching process by diluted sulphuric acid, whereas Part II deals with the purification of the leach liquor and the recovery of zinc by solvent extraction/electrowinning. The characterization of the examined electric arc furnace dust was carried out by using granulometry analysis, chemical analysis, X-ray diffraction (XRD), thermogravimetric/differential thermal analysis (TG/DTA) and scanning electron microscopy (SEM). The leaching process was based on the Zn extraction with diluted sulphuric acid from EAFD under atmospheric conditions and without using any preliminary treatment. Statistical design and analysis of experiments were used, in order to determine the main effects and interactions of the leaching process factors, which were: acid normality, temperature and solid to liquid ratio. The zinc recovery efficiency on the basis of EAFD weight reached 80%. X-ray diffraction and scanning electron microscopy were used for the characterization of the leached residues.

  12. 3D Numerical Analysis of the Arc Plasma Behavior in a Submerged DC Electric Arc Furnace for the Production of Fused MgO

    International Nuclear Information System (INIS)

    Wang Zhen; Wang Ninghui; Li Tie; Cao Yong

    2012-01-01

    A three dimensional steady-state magnetohydrodynamic model is developed for the arc plasma in a DC submerged electric arc furnace for the production of fused MgO. The arc is generated in a small semi-enclosed space formed by the graphite electrode, the molten bath and unmelted raw materials. The model is first used to solve a similar problem in a steel making furnace, and the calculated results are found to be in good agreement with the published measurements. The behavior of arcs with different arc lengths is also studied in the furnace for MgO production. From the distribution of the arc pressure on the bath surface it is shown that the arc plasma impingement is large enough to cause a crater-like depression on the surface of the MgO bath. The circulation of the high temperature air under the electrode may enhance the arc efficiency, especially for a shorter arc.

  13. Improved cooler design of electric arc furnace refractory in mining industry using thermal analysis modeling and simulation

    International Nuclear Information System (INIS)

    Istadi, I.; Bindar, Y.

    2014-01-01

    Production of steel and nickel using the electric arc furnace should be focused on the intensification of energy. Improvement of energy efficiency of the most consuming facilities was achieved by improving the use of alternative energy minimization such as reducing the heat lost of hot gases, minimizing the heat radiated through refractory linings of metallurgical furnaces, and cooling the highly thermally stressed components. The refractory of electric arc furnace should be modified to achieve the best cooling system of the furnace. In this physical modeling and simulation works, four modification scenarios of wall refractory designs were simulated, i.e. refractory with basic design, refractory with deep plate coolers, refractory with extra plate coolers, and refractory with wall falling film coolers. Finally, the use of deep plate cooler and the existing waffle cooler system was considered to be the best design of efficient electric arc furnace operationally. - Highlights: • Electric arc furnace design should be focused on the intensification of energy. • Refractory of electric arc furnace were modified to achieve the best cooling system. • Four modification scenarios of the wall refractory designs were simulated. • Use of deep plate cooler and existing waffle cooler system is the best cooling

  14. Carbothermic reduction of electric arc furnace dust and calcination of waelz oxide by semi-pilot scale rotary furnace

    Directory of Open Access Journals (Sweden)

    Morcali M.H.

    2012-01-01

    Full Text Available The paper gives a common outline about the known recycling techniques from electric arc furnace dusts and describes an investigation of a pyrometallurgical process for the recovery of zinc and iron from electric arc furnace dusts (EAFD. In the waelz process, the reduction of zinc and iron from the waste oxides using solid carbon (lignite coal was studied. In the reduction experiments; temperature, time and charge type (powder and pellet were investigated in detail. It was demonstrated that zinc and iron recovery (% increases with increasing temperature as well as time. Pelletizing was found to be a better method than using the powder as received for the zinc recovery and iron conversion (. In the calcination (roasting process, crude zinc oxide, which evaporated from non-ferric metals were collected as condensed product (crude waelz oxide, was heated in air atmosphere. Lead, cadmium as well as chlorine and other impurities were successfully removed from crude waelz oxide by this method. In the calcination experiments; temperature and time are investigated in detail. It was demonstrated that zinc purification (% increases with increasing temperature. The highest zinc refining (% was obtained at 1200°C for 120 minutes. A kinetic study was also undertaken to determine the activation energy of the process. Activation energies were 242.77 kJ/mol for the zinc recovery with powder forms, 261.99 kJ/mol for the zinc recovery with pellet forms respectively. It was found that, initially, the reaction was chemically controlled.

  15. Material properties of the F82H melted in an electric arc furnace

    Energy Technology Data Exchange (ETDEWEB)

    Sakasegawa, Hideo, E-mail: sakasegawa.hideo@jaea.go.jp [Japan Atomic Energy Agency, Rokkasho, Aomori (Japan); Tanigawa, Hiroyasu [Japan Atomic Energy Agency, Rokkasho, Aomori (Japan); Kano, Sho; Abe, Hiroaki [Institute for Materials Research, Tohoku university, Sendai, Miyagi (Japan)

    2015-10-15

    Highlights: • We studied material properties of reduced activation ferritic/martensitic steel. • We melted F82H using a 20 tons electric arc furnace for the first time. • Mass effect likely affected material properties. • MX (M: Metal, C: Carbon and/or Nitrogen) precipitates mainly formed on grain and sub grain boundaries. - Abstract: Fusion DEMO reactor requires over 11,000 tons of reduced activation ferritic/martensitic steel. It is necessary to develop the manufacturing technology for fabricating such large-scale steel with appropriate mechanical properties. In this work, we focused fundamental mechanical properties and microstructures of F82H-BA12 heat which was melted using a 20 tons electric arc furnace followed by electroslag remelting process. Its raw material of iron was blast furnace iron, because the production volume of electrolytic iron which has been used in former heats, is limited. After melting and forging, this F82H-BA12 heat was heat-treated in four different conditions to consider their fluctuations and to optimize them, and tensile and Charpy impact tests were then performed. The result of these mechanical properties were comparable to those of former F82H heats less than 5 tons which were melted applying vacuum induction melting.

  16. Diagnostic of the electrical characteristics to control the electric arc furnaces by a computer. Session 2. 2b N. 2. 2. 10

    Energy Technology Data Exchange (ETDEWEB)

    Hradilek, Z

    1984-01-01

    The article deals with a new method of diagnostic investigation into the instaneous electric power program of the electric arc furnace by use of thermoelectric converters. The electric magnitudes are recorded by a plotter and evaluated by a computer. The results obtained by this method are examined at the Vitkovice Steelworks/Czechoslovakia/ and can be applied to optimize the power program of an electric arc furnace by a control computer.

  17. Method and Mechanisms of Soil Stabilization Using Electric Arc Furnace Dust

    OpenAIRE

    Al-Amoudi, Omar S. Baghabra; Al-Homidy, Abdullah A.; Maslehuddin, Mohammed; Saleh, Tawfik A.

    2017-01-01

    This paper reports the method and mechanism for improving the strength of marl and desert sand utilizing electric arc furnace dust (EAFD), an industrial by-product, in lieu of cement or lime. EAFD was used in conjunction with a small quantity (2%) of cement. The mechanical properties and durability characteristics of marl and sand mixed with 2% cement plus 5-, 10-, 20- or 30%-EAFD, by weight of the soil, were evaluated. The soil-cement-EAFD mixtures were used to determine their unconfined com...

  18. DC Electric Arc Furnace Application for Production of Nickel-Boron Master Alloys

    Science.gov (United States)

    Alkan, Murat; Tasyürek, Kerem Can; Bugdayci, Mehmet; Turan, Ahmet; Yücel, Onuralp

    2017-09-01

    In this study, nickel-boron (Ni-B) alloys were produced via a carbothermic reduction starting from boric acid (H3BO3) with high-purity nickel oxide (NiO), charcoal, and wood chips in a direct current arc furnace. In electric arc furnace experiments, different starting mixtures were used, and their effects on the chemical compositions of the final Ni-B alloys were investigated. After the reduction and melting stages, Ni-B alloys were obtained by tapping from the bottom of the furnace. The samples from the designated areas were also taken and analyzed. The chemical composition of the final alloys and selected samples were measured with wet chemical analysis. The Ni-B alloys had a composition of up to 14.82 mass% B. The phase contents of the final alloys and selected samples were measured using x-ray diffraction (XRD). The XRD data helped predict possible reactions and reaction mechanisms. The material and energy balance calculations were made via the XRD Rietveld and chemical compositions. Nickel boride phases started to form 600 mm below the surface. The targeted NiB phase was detected at the tapping zone of the crucible (850-900 mm depth). The energy consumption was 1.84-4.29 kWh/kg, and the electrode consumption was 10-12 g/kg of raw material charged.

  19. Optimal Design of TCR/FC in Electric Arc Furnaces for Power Quality Improvement in Power Systems

    Directory of Open Access Journals (Sweden)

    Mahdi TORABIAN ESFAHANI

    2009-12-01

    Full Text Available Electric Arc Furnaces (EAFs are unbalanced, nonlinear and time varying loads, which can cause many problems in the power system quality. As the use of arc furnace loads increases in industry, the importance of the power quality problems also increase. So in order to optimize the usages of electric power in EAFs, it is necessary to minimize the effects of arc furnace loads on power quality in power systems as much as possible. Therefore, in this paper, design and simulation of an electric plant supplying an arc furnace is considered. For this purpose, a three phase arc furnace model, which can simulate all the mentioned power quality indices, is developed based on Hyperbolic -Exponential model (V-I model. Then by considering the high changes of reactive power and voltage flicker of nonlinear furnace load, a thyristor controlled reactor compensation with fixed capacitor (TCR/FC are designed and simulated. In this procedure, the reactive power is measured so that maximum speed and accuracy are achieved. Finally, simulation results verify the accuracy of the load modelling and show the effectiveness of the proposed TCR/FC model for reactive compensating of the EAF.

  20. Chemical, physical, structural and morphological characterization of the electric arc furnace dust

    International Nuclear Information System (INIS)

    Machado, Janaina G.M.S.; Brehm, Feliciane Andrade; Moraes, Carlos Alberto Mendes; Santos, Carlos Alberto dos; Vilela, Antonio Cezar Faria; Cunha, Joao Batista Marimon da

    2006-01-01

    Electric arc furnace dust (EAFD) is a hazardous industrial waste generated in the collection of particulate material during steelmaking process via electric arc furnace. Important elements to the industry such as, Fe and Zn are the main ones in EAFD. Due to their presence, it becomes very important to know how these elements are combined before studying new technologies for its processing. The aim of this work was to carry out a chemical, physical, structural and morphological characterization of the EAFD. The investigation was carried out by using granulometry analysis, chemical analysis, scanning electron microscopy (SEM), energy dispersive spectroscopy via SEM (EDS), X-ray mapping analysis via SEM, X-ray diffraction (XRD) and Moessbauer spectroscopy. By XRD the following phases were detected: ZnFe 2 O 4 , Fe 3 O 4 , MgFe 2 O 4 , FeCr 2 O 4 , Ca 0.15 Fe 2.85 O 4 , MgO, Mn 3 O 4 , SiO 2 and ZnO. On the other hand, the phases detected by Moessbauer spectroscopy were: ZnFe 2 O 4 , Fe 3 O 4 , Ca 0.15 Fe 2.85 O 4 and FeCr 2 O 4 . Magnesium ferrite (MgFe 2 O 4 ), observed in the XRD pattern as overlapped peaks, was not identified in the Moessbauer spectroscopy analysis

  1. CHARACTERIZATION OF THE DUST GENERATED IN THE RECYCLING PROCESS OF THE ELECTRIC ARC FURNACE DUST

    Directory of Open Access Journals (Sweden)

    Fábio Gonçalves Rizz

    2013-10-01

    Full Text Available Electric Arc Furnace Dust (EAFD is a solid waste generated by the production of steel through the Electric Arc Furnace. This waste is labeled dangerous, which motivates studies aiming its recycling. Experiments were made to study a pyrometallurgical process for the recycling of the dust, using the insertion of dust briquettes in molten pig iron in three temperatures. In the briquettes, there were made additions of calcium fluoride in four different concentrations. This paper has the objective to characterize the dust that results from this process, verifying the influence of the temperature and the concentration of calcium fluoride in the briquette in the morphology and chemical composition of the new dust, determining the optimal conditions for the recovery of the zinc content of the dust. This newly generated dust was analyzed in an Scanning Electronic Microscope, used to capture micrographs and chemical composition by EDS. The micrographs show that the temperature and the calcium fluoride concentration interfere in the way the dust particles agglomerate. Chemical analysis points that the higher zinc recuperation occurrs in the experiments at 1500°C with 7% addition of calcium fluoride.

  2. Physics-Based Modeling of Electric Operation, Heat Transfer, and Scrap Melting in an AC Electric Arc Furnace

    Science.gov (United States)

    Opitz, Florian; Treffinger, Peter

    2016-04-01

    Electric arc furnaces (EAF) are complex industrial plants whose actual behavior depends upon numerous factors. Due to its energy intensive operation, the EAF process has always been subject to optimization efforts. For these reasons, several models have been proposed in literature to analyze and predict different modes of operation. Most of these models focused on the processes inside the vessel itself. The present paper introduces a dynamic, physics-based model of a complete EAF plant which consists of the four subsystems vessel, electric system, electrode regulation, and off-gas system. Furthermore the solid phase is not treated to be homogenous but a simple spatial discretization is employed. Hence it is possible to simulate the energy input by electric arcs and fossil fuel burners depending on the state of the melting progress. The model is implemented in object-oriented, equation-based language Modelica. The simulation results are compared to literature data.

  3. Heavy metal recovery from electric arc furnace steel slag by using hydrochloric acid leaching

    Science.gov (United States)

    Wei, Lim Jin; Haan, Ong Teng; Shean Yaw, Thomas Choong; Chuah Abdullah, Luqman; Razak, Mus'ab Abdul; Cionita, Tezara; Toudehdehghan, Abdolreza

    2018-03-01

    Electric Arc Furnace steel slag (EAFS) is the waste produced in steelmaking industry. Environmental problem such as pollution will occur when dumping the steel slag waste into the landfill. These steel slags have properties that are suitable for various applications such as water treatment and wastewater. The objective of this study is to develop efficient and economical chlorination route for EAFS extraction by using leaching process. Various parameters such as concentration of hydrochloric acid, particle size of steel slag, reaction time and reaction temperature are investigated to determine the optimum conditions. As a result, the dissolution rate can be determined by changing the parameters, such as concentration of hydrochloric acid, particle size of steel slag, reaction time and reaction temperature. The optimum conditions for dissolution rates for the leaching process is at 3.0 M hydrochloric acid, particle size of 1.18 mm, reaction time of 2.5 hour and the temperature of 90°C.

  4. Removal of Heavy Metals from Steel Making Waste Water by Using Electric Arc Furnace Slag

    Directory of Open Access Journals (Sweden)

    C. L. Beh

    2012-01-01

    Full Text Available This work investigated the reduction of chemical oxygen demand (COD, biological oxygen demand (BOD, total suspended solids (TSS and the concentration of heavy metals of wastewater from a steel making plant. Adsorption experiments were carried out by electric arc furnace slag (EAFS in a fixed-bed column mode. The raw wastewater did not meet the standard B limitations, having high values of BOD, COD, TSS, Iron, Zinc, Manganese and Copper. After passing through the fixed bed column, BOD, COD and TSS values decreased to 1.6, 6.3 and <2 mgL-1, respectively while the concentration of Iron, Zinc, Manganese and Copper were 0.08, 0.01, 0.03 and 0.07 mgL-1, respectively. The results confirmed that EAFS can be used as an efficient adsorbent for producing treated water that comply with the Standard B limitations for an industrial effluent.

  5. Recycling of electric arc furnace dust; Reciclagem de poeira de aciaria eletrica

    Energy Technology Data Exchange (ETDEWEB)

    Marques Sobrinho, Vicente de Paulo Ferreira; Oliveira, Jose Roberto de, E-mail: vicente@ifes.edu.b [Instituto Federal de Ciencia e Tecnologia do Espirito Santo (IFES), Vitoria, ES (Brazil); Tenorio, Jorge Alberto Soares; Espinosa, Denise Crocce Romano [Universidade de Sao Paulo (EPUSP), SP (Brazil). Escola Politecnica

    2010-07-01

    This research aims to study the process of incorporation of the metal iron in electric arc furnace dust (EAFD), from a steel mill producing long steel by liquid iron in addition to the changing temperature of 1400 degrees Celsius of EAFD 'as received', the percentage of EAFD to be added (5, 10 and 20% of initial weight of sample pig iron) and the time of withdrawal of the sample of pig iron and slag (30 minutes after the addition of EAFD). Previously, the EAFD will be characterized using the following techniques: chemical analysis, size analysis, specific surface area, Xray diffraction, scanning electron microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) microanalysis. . After characterization, the EAFD will be added to the bath of liquid pig iron. It is expected that the results obtained at the end of the research allow the evaluation of the iron metal incorporation of EAFD in pig iron bath. (author)

  6. Modeling of zinc solubility in stabilized/solidified electric arc furnace dust

    International Nuclear Information System (INIS)

    Fernandez-Olmo, Ignacio; Lasa, Cristina; Irabien, Angel

    2007-01-01

    Equilibrium models which attempt for the influence of pH on the solubility of metals can improve the dynamic leaching models developed to describe the long-term behavior of waste-derived forms. In addition, such models can be used to predict the concentration of metals in equilibrium leaching tests at a given pH. The aim of this work is to model the equilibrium concentration of Zn from untreated and stabilized/solidified (S/S) electric arc furnace dust (EAFD) using experimental data obtained from a pH-dependence leaching test (acid neutralization capacity, ANC). EAFD is a hazardous waste generated in electric arc furnace steel factories; it contains significant amounts of heavy metals such as Zn, Pb, Cr or Cd. EAFD from a local factory was characterized by X-ray fluorescence (XRF), acid digestion and X-ray diffraction (XRD). Zn and Fe were the main components while the XRD analysis revealed that zincite, zinc ferrite and hematite were the main crystalline phases. Different cement/EAFD formulations ranging from 7 to 20% dry weight of cement were prepared and subjected to the ANC leaching test. An amphoteric behavior of Zn was found from the pH dependence test. To model this behavior, the geochemical model Visual MINTEQ (VMINTEQ) was used. In addition to the geochemical model, an empirical model based on the dissolution of Zn in the acidic zone and the re-dissolution of zinc compounds in the alkaline zone was considered showing a similar prediction than that obtained with VMINTEQ. This empirical model seems to be more appropriate when the metal speciation is unknown, or when if known, the theoretical solid phases included in the database of VMINTEQ do not allow to describe the experimental data

  7. Chemical, physical, structural and morphological characterization of the electric arc furnace dust

    Energy Technology Data Exchange (ETDEWEB)

    Machado, Janaina G.M.S. [Laboratorio de Siderurgia/LASID, Universidade Federal do Rio Grande do Sul, UFRGS/PPGEM Centro de Tecnologia, AV. Bento Goncalves 9500 CEP, 91501-970 Caixa postal 15021, Porto Alegre, RS (Brazil)]. E-mail: jana@ct.ufrgs.br; Brehm, Feliciane Andrade [Nucleo de Caracterizacao de Materiais/NucMat, Universidade do Vale do Rio dos Sinos, UNISINOS, Sao Leopoldo, RS (Brazil); Moraes, Carlos Alberto Mendes [Nucleo de Caracterizacao de Materiais/NucMat, Universidade do Vale do Rio dos Sinos, UNISINOS, Sao Leopoldo, RS (Brazil); Santos, Carlos Alberto dos [Nucleo de Educacao a Distancia, Universidade Estadual do Rio Grande do Sul, UERGS, Porto Alegre, RS (Brazil); Vilela, Antonio Cezar Faria [Laboratorio de Siderurgia/LASID, Universidade Federal do Rio Grande do Sul, UFRGS/PPGEM Centro de Tecnologia, AV. Bento Goncalves 9500 CEP, 91501-970 Caixa postal 15021, Porto Alegre, RS (Brazil); Cunha, Joao Batista Marimon da [Instituto de Fisica, Universidade Federal do Rio Grande do Sul, UFRGS, Campus do Vale, Porto Alegre, RS (Brazil)

    2006-08-25

    Electric arc furnace dust (EAFD) is a hazardous industrial waste generated in the collection of particulate material during steelmaking process via electric arc furnace. Important elements to the industry such as, Fe and Zn are the main ones in EAFD. Due to their presence, it becomes very important to know how these elements are combined before studying new technologies for its processing. The aim of this work was to carry out a chemical, physical, structural and morphological characterization of the EAFD. The investigation was carried out by using granulometry analysis, chemical analysis, scanning electron microscopy (SEM), energy dispersive spectroscopy via SEM (EDS), X-ray mapping analysis via SEM, X-ray diffraction (XRD) and Moessbauer spectroscopy. By XRD the following phases were detected: ZnFe{sub 2}O{sub 4}, Fe{sub 3}O{sub 4}, MgFe{sub 2}O{sub 4}, FeCr{sub 2}O {sub 4}, Ca{sub 0.15}Fe{sub 2.85}O{sub 4}, MgO, Mn{sub 3}O{sub 4}, SiO{sub 2} and ZnO. On the other hand, the phases detected by Moessbauer spectroscopy were: ZnFe{sub 2}O{sub 4}, Fe{sub 3}O{sub 4}, Ca{sub 0.15}Fe{sub 2.85}O{sub 4} and FeCr{sub 2}O{sub 4}. Magnesium ferrite (MgFe{sub 2}O{sub 4}), observed in the XRD pattern as overlapped peaks, was not identified in the Moessbauer spectroscopy analysis.

  8. Industrial study of iron oxide reduction by injection of carbon particles into the electric arc furnace

    International Nuclear Information System (INIS)

    Conejo, A. N.; Torres, R.; Cuellar, E.

    1999-01-01

    An industrial study was conducted in electric arc furnaces (EAF) employing 100% direct reduced iron to evaluate the oxidation level of the slag-metal system. Energy consumption is decreased by injecting gaseous oxygen, however, slag oxidation also increases. In order to reduce the extent of oxidation while keeping a high volume of the oxygen injected , it is required: a) to optimize the carbon injection practice, b) to increase the carbon concentration of sponge iron, c) to operate with soluble carbon in both the metal and the slag beyond a critical level and d) to employ a low temperature profile, on average 1,650 degree centigrade. A method to define the proper amount of carbon in sponge iron which considers their metallization as well as the amount of oxygen injected is proposed. The position of the lance is critical in order to optimize the practice of carbon injection and assure a better residence time of the carbon particles within the furnace. (Author) 23 refs

  9. Addition of electric arc furnace dust in hot metal changing the form of addition

    International Nuclear Information System (INIS)

    Marques Sobrinho, Vicente de Paulo Ferreira; Oliveira, Jose Roberto de; Vieira, Estefano Aparecido; Telles, Victor Bridi; Grillo, Felipe Fardin; Tenorio, Jorge Alberto Soares; Espinosa, Denise Crocce Romano

    2014-01-01

    This research aims to study the incorporation of the mass of electric arc furnace dust (EAFD), by addition in hot metal (1.78% Si) at a temperature of 1,400 degrees Celsius. The EAFD is from a steel plant producing long steel. The addition of the EAFD was as received, in the form of briquettes without agitation of the hot metal and in the form of briquettes with agitation of the hot metal. Previously, the EAFD was characterized using the following techniques: chemical analysis, size analysis, X-ray diffraction, scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) microanalysis. The achievement of fusion experiments in laboratory scale, took place in a vertical tubular furnace with temperature control. The fusion experiments to assess the incorporation of EAFD mass used graphite crucibles. After cooling, the hot metal and the slag, remaining in the crucible, were weighed to do a mass balance. A flow of inert gas (argon) was maintained inside the furnace during the experiments. Results show that the experiment with addition of EAFD as received presents the best result of incorporating the mass of the final hot metal (1.73%) combined with the lowest percentage of volatilized mass of EAFD (46.52%). The experiment addition of EAFD in the form of briquette with agitation of hot metal presents the lowest percentage of slag mass (4.58%). The zinc content of volatilized EAFD (64.30%) is higher than the zinc content of the imported ore concentrate (52%) and zinc content of the national ore concentrate (12% to 39%). The presence of lead and cadmium in the slag characterizing it as a hazardous solid waste. (author)

  10. Mass and elemental distributions of atmospheric particles nearby blast furnace and electric arc furnace operated industrial areas in Australia

    International Nuclear Information System (INIS)

    Mohiuddin, Kazi; Strezov, Vladimir; Nelson, Peter F.; Stelcer, Eduard; Evans, Tim

    2014-01-01

    The improved understanding of mass and elemental distributions of industrial air particles is important due to their heterogeneous atmospheric behaviour and impact on human health and the environment. In this study, particles of different size ranges were collected from three sites in Australia located in the vicinity of iron and steelmaking industries and one urban background site with very little industrial influence. In order to determine the importance of the type of industrial activity on the urban atmospheric quality, the industrial sites selected in this study were in the close proximity to two blast furnace operated and one electric arc furnace based steelmaking sites. The chemical compositions of the collected air particles were analysed using the proton induced X-ray emission (PIXE) technique. This study revealed significantly higher metal concentrations in the atmospheric particles collected in the industrial sites, comparing to the background urban site, demonstrating local influence of the industrial activities to the air quality. The modality types of the particles were found to be variable between the mass and elements, and among elements in the urban and industrial areas indicating that the elemental modal distribution is as important as particle mass for particle pollution modelling. The highest elemental number distribution at all studied sites occurred with particle size of 0.1 μm. Iron was found as the main dominant metal at the industrial atmosphere in each particle size range. The industrial Fe fraction in the submicron and ultrafine size particles was estimated at up to 95% which may be released from high temperature industrial activities with the iron and steelmaking industries being one of the major contributors. Hence, these industrial elemental loadings can highly influence the atmospheric pollution at local urban and regional levels and are required to consider in the atmospheric modelling settings. - Highlights: • Urban and

  11. Mass and elemental distributions of atmospheric particles nearby blast furnace and electric arc furnace operated industrial areas in Australia

    Energy Technology Data Exchange (ETDEWEB)

    Mohiuddin, Kazi, E-mail: kazi.mohiuddin@students.mq.edu.au [Graduate School of the Environment, Department of Environment and Geography, Faculty of Science, Macquarie University, NSW (Australia); Strezov, Vladimir; Nelson, Peter F. [Graduate School of the Environment, Department of Environment and Geography, Faculty of Science, Macquarie University, NSW (Australia); Stelcer, Eduard [Australian Nuclear Science and Technology Organisation, Lucas Heights, NSW (Australia); Evans, Tim [Graduate School of the Environment, Department of Environment and Geography, Faculty of Science, Macquarie University, NSW (Australia)

    2014-07-01

    The improved understanding of mass and elemental distributions of industrial air particles is important due to their heterogeneous atmospheric behaviour and impact on human health and the environment. In this study, particles of different size ranges were collected from three sites in Australia located in the vicinity of iron and steelmaking industries and one urban background site with very little industrial influence. In order to determine the importance of the type of industrial activity on the urban atmospheric quality, the industrial sites selected in this study were in the close proximity to two blast furnace operated and one electric arc furnace based steelmaking sites. The chemical compositions of the collected air particles were analysed using the proton induced X-ray emission (PIXE) technique. This study revealed significantly higher metal concentrations in the atmospheric particles collected in the industrial sites, comparing to the background urban site, demonstrating local influence of the industrial activities to the air quality. The modality types of the particles were found to be variable between the mass and elements, and among elements in the urban and industrial areas indicating that the elemental modal distribution is as important as particle mass for particle pollution modelling. The highest elemental number distribution at all studied sites occurred with particle size of 0.1 μm. Iron was found as the main dominant metal at the industrial atmosphere in each particle size range. The industrial Fe fraction in the submicron and ultrafine size particles was estimated at up to 95% which may be released from high temperature industrial activities with the iron and steelmaking industries being one of the major contributors. Hence, these industrial elemental loadings can highly influence the atmospheric pollution at local urban and regional levels and are required to consider in the atmospheric modelling settings. - Highlights: • Urban and

  12. Optical Sensors for Post Combustion Control in Electric Arc Furnace Steelmaking (TRP 9851)

    Energy Technology Data Exchange (ETDEWEB)

    Sarah W. Allendorf; David K. Ottesen; Robert W. Green; Donald R. Hardesty; Robert Kolarik; Howard Goodfellow; Euan Evenson; Marshall Khan; Ovidiu Negru; Michel Bonin; Soren Jensen

    2003-12-31

    Working in collaboration with Stantec Global Technologies, Process Metrix Corporation, and The Timken Company, Sandia National Laboratories constructed and evaluated a novel, laser-based off-gas sensor at the electric arc furnace facility of Timken's Faircrest Steel Plant (Canton, Ohio). The sensor is based on a mid-infrared tunable diode laser (TDL), and measures the concentration and temperature of specific gas species present in the off-gas emanating from the EAF. The laser beam is transmitted through the gas stream at the fourth hole of the EAF, and provides a real-time, in situ measurement that can be used for process optimization. Two sets of field tests were performed in parallel with Stantec's extractive probe off-gas system, and the tests confirm the TDL sensor's operation and applicability for electric steel making. The sensor measures real-time, in situ line-of-sight carbon monoxide (CO) concentrations between 5% and 35% CO, and measures off-gas temperature in the range of 1400 to 1900 K. In order to achieve commercial-ready status, future work is required to extend the sensor for simultaneous CO and CO{sub 2} concentration measurements. In addition, long-term endurance tests including process optimization must be completed.

  13. Preparation of concrete mixtures with electric arc furnace slag and recycled ground glass

    Science.gov (United States)

    Pérez Rojas, Y.; López, E. Vera; López Rodríguez, M.; Díaz Pita, J.

    2017-12-01

    The present work includes the first advances in the development of investigations that seek to include Ground Grinding Glass (GRR) and the Electric Arc Furnace Slag (EAFS) in the production of mixtures of hydraulic concrete mixing them simultaneously, so that it satisfies the specifications techniques to be used in the construction of rigid pavements. Firstly, we cite the tests carried out on the different materials to obtain their physical, chemical and mechanical characterization and determine their compliance, as well as the measurement of certain characteristics that may be somewhat empirical to standardize their control. Technique such as X-Ray Diffraction (XRD), X-ray Fluorescence Spectrometry (XFR) and Scanning Electron Microscopy (SEM) have been used. Once the results of the characterization tests and their correspondence with the Colombian technical standards have been obtained, it has become possible to select the use of the Transparent Recycled Ground Glass (TRGG) as the most suitable for the replacement of the sand in the dosage of new mixtures modified concrete.

  14. Nitrogen Control in Electric Arc Furnace Steelmaking by DRI (TRP 0009)

    Energy Technology Data Exchange (ETDEWEB)

    Dr. Gordon A. Irons

    2004-03-31

    Nitrogen is difficult to remove in electric arc furnace (EAF) steelmaking, requiring the use of more energy in the oxygen steelmaking route to produce low-nitrogen steel. The objective of this work was to determine if the injection of directly reduced iron (DRI) fines into EAFs could reduce the nitrogen content by creating fine carbon monoxide bubbles that rinse nitrogen from the steel. The proposed work included physical and chemical characterization of DRI fines, pilot-scale injection into steel, and mathematical modeling to aid in scale-up of the process. Unfortunately, the pilot-scale injections were unsuccessful, but some full-scale data was obtained. Therefore, the original objectives were met, and presented in the form of recommendations to EAF steelmakers regarding: (1) The best composition and size of DRI fines to use; (2) The amount of DRI fines required to achieve a specific reduction in nitrogen content in the steel; and (3) The injection conditions. This information may be used by steelmakers in techno-economic assessments of the cost of reducing nitrogen with this technology.

  15. Method and Mechanisms of Soil Stabilization Using Electric Arc Furnace Dust

    Science.gov (United States)

    Al-Amoudi, Omar S. Baghabra; Al-Homidy, Abdullah A.; Maslehuddin, Mohammed; Saleh, Tawfik A.

    2017-04-01

    This paper reports the method and mechanism for improving the strength of marl and desert sand utilizing electric arc furnace dust (EAFD), an industrial by-product, in lieu of cement or lime. EAFD was used in conjunction with a small quantity (2%) of cement. The mechanical properties and durability characteristics of marl and sand mixed with 2% cement plus 5-, 10-, 20- or 30%-EAFD, by weight of the soil, were evaluated. The soil-cement-EAFD mixtures were used to determine their unconfined compressive strength (UCS), soaked California Bearing Ratio (CBR) and durability. The risk of leaching of toxic heavy metals, such as lead and cadmium, from the stabilized soils to the groundwater was also investigated. The mechanisms of stabilization of the selected soils due to the use of EAFD along with a small quantity of cement are also elucidated. The usage of 20 to 30% EAFD with 2% cement was noted to considerably improve the mechanical properties and durability of both marl and sand.

  16. Study of the processes for of remelting zirconium alloys in an electric arc furnace

    Energy Technology Data Exchange (ETDEWEB)

    Pereira, Luiz A.T.; Rossi, Jesualdo L.; Costa, Guilherme R.; Martinez, Luis G.; Sato, Ivone M., E-mail: luiz.atp@uol.com.br, E-mail: jelrossi@ipen.br, E-mail: guilhermeramoscosta@gmail.com, E-mail: lgallego@ipen.br, E-mail: imsato@ipen.br [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

    2015-07-01

    Zirconium alloy tubes are used as cladding for fuel elements of PWR nuclear reactors, which contains the UO{sub 2} pellets. In the manufacture of these fuel element parts, machining chips from the nuclear grade zirconium alloys are generated. Hence, these machining chips cannot be discarded, as ordinary metallic waste. Thus, the recycling of this material is a strategic aspect for the nuclear technology, both for economic and environmental issues. The main reason is that nuclear grade alloys have very high cost, are not commercially produced in Brazil and has to be imported for the manufacture of the nuclear fuels. This work discusses a method to melt and recycle Zircaloy chips, using an electric-arc furnace to obtain small laboratory ingots. The chemical composition of the ingots was determined using X-ray fluorescence spectroscopy and was compared to the specifications of nuclear grade Zircaloy and to the chemical composition of the received machining chips. The ingots were annealed in high vacuum, as well as were hot rolled in a mill. The microstructures were characterized by optical microscopy. The hardness was evaluated using the Rockwell B scale hardness. The results showed that the compositions of the recycled Zircaloy comply with the chemical specifications and a suitable microstructure has been obtained for nuclear use. (author)

  17. Emissions of polyciclic aromatic hydrocarbons and polyciclic carbonyl biphenils from electric arc furnaces

    Directory of Open Access Journals (Sweden)

    P. Gomes, J. F.

    2008-06-01

    Full Text Available This paper describes work done in order to determine the emissions of highly toxic organic micropollutants from electric arc furnaces used in the production of carbon steel from scrap. The study will be allowing to derive relationships between the levels of airborne micropollutants and the operational parameters of the production process so that an abatement of pollution could be achieved. By using the European standard method CEN 1948 for dioxin like compounds sampling and measurement, it was possible to determine the characteristic fingerprint of micropollutants such as polyciclic aromatic hydrocarbons (PAHs and polycyclic carbonyl biphenils (PCBs emitted by this particular stationary source.

    Este artículo contiene resultados del trabajo ejecutado para estudiar la determinación de las emisiones de los micropolutantes orgánicos muy tóxicos que se emiten por los hornos eléctricos de arco utilizados en la producción de acero. Este estudio inicial va a permitir relacionar las concentraciones de polutantes emitidos a la atmósfera con las condiciones de operación del horno eléctrico de arco. Utilizando el método normalizado CEN 1948 para captación y análisis de muestras de compuestos análogos a las dioxinas ha sido posible determinar el perfil característico de los micropolutantes tales como PAHs y PCBs emitidos por esta fuente.

  18. Thermal Analysis on the Pyrolysis of Tetrabromobisphenol A and Electric Arc Furnace Dust Mixtures

    Science.gov (United States)

    Al-Harahsheh, Mohammad; Al-Otoom, Awni; Al-Jarrah, Muhannad; Altarawneh, Mohammednoor; Kingman, Sam

    2018-02-01

    The pyrolysis of Tetrabromobisphenol A (TBBPA) mixed with electric arc furnace dust (EAFD) was studied using thermogravimetric analysis (TGA) and theoretically analyzed using thermodynamic equilibrium calculations. Mixtures of both materials with varying TBBPA loads (1:1 and 1:3) were prepared and pyrolyzed in a nitrogen atmosphere under dynamic heating conditions at heating rates of 5 and 10 °C/min. The mixtures degraded through several steps, including decomposition of TBBPA yielding mainly HBr, bromination of metal oxides, followed by their evaporation in the sequence of CuBr3, ZnBr2, PbBr2, FeBr2, MnBr2, KBr, NaBr, CaBr2, and MgBr2, and finally reduction of the remaining metal oxides by the char formed from decomposition of TBBPA. Thermodynamic calculations suggest the possibility of selective bromination of zinc and lead followed by their evaporation, leaving iron in its oxide form, while the char formed may serve as a reduction agent for iron oxides into metallic iron. However, at higher TBBPA volumes, iron bromide forms, which can also be evaporated at a temperature higher than those of ZnBr2 and PbBr2. Results from this work provide practical insight into selective recovery of valuable metals from EAFD while at the same time recycling the hazardous bromine content in TBBPA.

  19. Development of processes for zircaloy chips recycling by electric arc furnace remelting and powder metallurgy

    International Nuclear Information System (INIS)

    Pereira, Luiz Alberto Tavares

    2014-01-01

    PWR reactors employ, as nuclear fuel, UO 2 pellets with Zircaloy clad. In the fabrication of fuel element parts, machining chips from the alloys are generated. As the Zircaloy chips cannot be discarded as ordinary metallic waste, the recycling of this material is important for the Brazilian Nuclear Policy, which targets the reprocess of Zircaloy residues for economic and environmental aspects. This work presents two methods developed in order to recycle Zircaloy chips. In one of the methods, Zircaloy machining chips were refused using an electric-arc furnace to obtain small laboratory ingots. The second one uses powder metallurgy techniques, where the chips were submitted to hydriding process and the resulting material was milled, isostatically pressed and vacuum sintered. The ingots were heat-treated by vacuum annealing. The microstructures resulting from both processing methods were characterized using optical and scanning electron microscopy. Chemical composition, crystal phases and hardness were also determined. The results showed that the composition of recycled Zircaloy comply with the chemical specifications and presented adequate microstructure for nuclear use. The good results of the powder metallurgy method suggest the possibility of producing small parts, like cladding end-caps, using near net shape sintering. (author)

  20. Rheological Characterization of Warm-Modified Asphalt Mastics Containing Electric Arc Furnace Steel Slags

    Directory of Open Access Journals (Sweden)

    M. Pasetto

    2016-01-01

    Full Text Available The environmental sustainability of road materials and technologies plays a key role in pavement engineering. In this sense, the use of Warm Mix Asphalt (WMA, that is, a modified asphalt concrete that can be produced and applied at lower temperature, is considered an effective solution leading to environmental and operational benefits. The environmental sustainability of WMA can be further enhanced with the inclusion of steel slag in partial substitution of natural aggregates. Nevertheless, such innovative material applied at lower temperatures containing warm additives and steel slag should be able to guarantee at least the same performance of traditional hot mix asphalts, thus assuring acceptable mechanical properties and durability. Therefore, the purpose of this study is to investigate the rheological behaviour of bituminous mastics obtained combining a warm-modified binder and a filler (material passing to 0.063 mm coming from electric arc furnace steel slag. To evaluate the influence of both warm additive and steel slag, a plain binder and limestone filler were also used for comparison purposes. Complex modulus and permanent deformation resistance of bitumens and mastics were assessed using a dynamic shear rheometer. Experimental results showed that steel slag warm mastics assure enhanced performance demonstrating promising applicability.

  1. Thermodynamic analysis of the selective chlorination of electric arc furnace dust

    International Nuclear Information System (INIS)

    Pickles, C.A.

    2009-01-01

    The remelting of automobile scrap in an electric arc furnace (EAF) results in the production of a dust, which contains high concentrations of the oxides of zinc, iron, calcium and other metals. Typically, the lead and zinc are of commercial value, while the other metals are not worth recovering. At the present time, EAF dusts are treated in high temperature Waelz rotary kiln-type processes, where the lead and zinc oxides are selectively reduced and simultaneously reoxidized and a crude zinc oxide is produced. Another alternative processing route is selective chlorination, in which the non-ferrous metals are preferentially chlorinated to their gaseous chlorides and in this manner separated from the iron. In the present research, a detailed thermodynamic analysis of this chlorination process has been performed and the following factors were investigated; temperature, amount of chlorine, lime content, silica content, presence of an inert gas and the oxygen potential. High lead and zinc recoveries as gaseous chlorides could be achieved but some of the iron oxide was also chlorinated. Additionally, the calcium oxide in the dust consumes chlorine, but this can be minimized by adding silica, which results in the formation of stable calcium silicates. The optimum conditions were determined for a typical dust composition. The selectivities achieved with chlorination were lower than those for reduction, as reported in the literature, but there are other advantages such as the potential recovery of copper.

  2. Thermodynamic analysis of the selective chlorination of electric arc furnace dust

    Energy Technology Data Exchange (ETDEWEB)

    Pickles, C.A., E-mail: pickles-c@mine.queensu.ca [Department of Mining Engineering, Queen' s University, Kingston, Ontario, K7L 3N6 (Canada)

    2009-07-30

    The remelting of automobile scrap in an electric arc furnace (EAF) results in the production of a dust, which contains high concentrations of the oxides of zinc, iron, calcium and other metals. Typically, the lead and zinc are of commercial value, while the other metals are not worth recovering. At the present time, EAF dusts are treated in high temperature Waelz rotary kiln-type processes, where the lead and zinc oxides are selectively reduced and simultaneously reoxidized and a crude zinc oxide is produced. Another alternative processing route is selective chlorination, in which the non-ferrous metals are preferentially chlorinated to their gaseous chlorides and in this manner separated from the iron. In the present research, a detailed thermodynamic analysis of this chlorination process has been performed and the following factors were investigated; temperature, amount of chlorine, lime content, silica content, presence of an inert gas and the oxygen potential. High lead and zinc recoveries as gaseous chlorides could be achieved but some of the iron oxide was also chlorinated. Additionally, the calcium oxide in the dust consumes chlorine, but this can be minimized by adding silica, which results in the formation of stable calcium silicates. The optimum conditions were determined for a typical dust composition. The selectivities achieved with chlorination were lower than those for reduction, as reported in the literature, but there are other advantages such as the potential recovery of copper.

  3. Thermodynamic analysis of the selective chlorination of electric arc furnace dust.

    Science.gov (United States)

    Pickles, C A

    2009-07-30

    The remelting of automobile scrap in an electric arc furnace (EAF) results in the production of a dust, which contains high concentrations of the oxides of zinc, iron, calcium and other metals. Typically, the lead and zinc are of commercial value, while the other metals are not worth recovering. At the present time, EAF dusts are treated in high temperature Waelz rotary kiln-type processes, where the lead and zinc oxides are selectively reduced and simultaneously reoxidized and a crude zinc oxide is produced. Another alternative processing route is selective chlorination, in which the non-ferrous metals are preferentially chlorinated to their gaseous chlorides and in this manner separated from the iron. In the present research, a detailed thermodynamic analysis of this chlorination process has been performed and the following factors were investigated; temperature, amount of chlorine, lime content, silica content, presence of an inert gas and the oxygen potential. High lead and zinc recoveries as gaseous chlorides could be achieved but some of the iron oxide was also chlorinated. Additionally, the calcium oxide in the dust consumes chlorine, but this can be minimized by adding silica, which results in the formation of stable calcium silicates. The optimum conditions were determined for a typical dust composition. The selectivities achieved with chlorination were lower than those for reduction, as reported in the literature, but there are other advantages such as the potential recovery of copper.

  4. Recovery of Zn from acid mine water and electric arc furnace dust in an integrated process.

    Science.gov (United States)

    Carranza, Francisco; Romero, Rafael; Mazuelos, Alfonso; Iglesias, Nieves

    2016-01-01

    In this paper, the purification of acid mine water and the treatment of electric arc furnace dust (EAFD) are integrated into one process with the aim of recovering the Zn content of both effluent and waste. Zinc recovery can reduce the cost of their environmental management: purified acid mine water is discharged after removing all metals; EAFD ceases to be hazardous waste; and Zn is valorised. The process consists of the recovery of Zn as zinc oxide and its purification into commercial products. First, EAFD is leached with acid water and the dissolved metals are selectively precipitated as hydroxides. After EADF leaching, ferrous iron is bio-oxidized and Fe and Al are then precipitated; in the following stage, Cu, Ni, Co and Cd are cemented and finally Zn is precipitated as ZnO. In order to purify water that finally is discharged to a river, lime is used as the neutralizing agent, which results in a precipitate of mainly gypsum, MnO, and ZnO. From the impure zinc oxide produced, various alternatives for the attainment of commercial products, such as basic zinc carbonate and electrolytic zinc, are studied in this work. Copyright © 2015 Elsevier Ltd. All rights reserved.

  5. An effect of heat insulation parameters on thermal losses of water-cooled roofs for secondary steelmaking electric arc furnaces

    Directory of Open Access Journals (Sweden)

    E. Mihailov

    2016-07-01

    Full Text Available The aim of this work is research in the insulation parameters effect on the thermal losses of watercooled roofs for secondary steelmaking electric arc furnaces. An analytical method has been used for the investigation in heat transfer conditions in the working area. The results of the research can be used to choose optimal cooling parameters and select a suitable kind of insulation for water-cooled surfaces.

  6. Formation of the ZnFe2O4 phase in an electric arc furnace off-gas treatment system.

    Science.gov (United States)

    Suetens, T; Guo, M; Van Acker, K; Blanpain, B

    2015-04-28

    To better understand the phenomena of ZnFe2O4 spinel formation in electric arc furnace dust, the dust was characterized with particle size analysis, X-ray fluorescence (XRF), electron backscatter diffraction (EBSD), and electron probe micro-analysis (EPMA). Different ZnFe2O4 formation reaction extents were observed for iron oxide particles with different particle sizes. ZnO particles were present as both individual particles and aggregated on the surface of larger particles. Also, the slag particles found in the off-gas were shown not to react with the zinc vapor. After confirming the presence of a ZnFe2O4 formation reaction, the thermodynamic feasibility of in-process separation - a new electric arc furnace dust treatment technology - was reevaluated. The large air intake and the presence of iron oxide particles in the off-gas were included into the thermodynamic calculations. The formation of the stable ZnFe2O4 spinel phase was shown to be thermodynamically favorable in current electric arc furnace off-gas ducts conditions even before reaching the post combustion chamber. Copyright © 2015 Elsevier B.V. All rights reserved.

  7. Electrical conductivity of the screening residuals of coke production in context of ferrochromium production in a submerged arc furnace

    Energy Technology Data Exchange (ETDEWEB)

    Rousu, Arto; Mattila, Olli [Lab. of Process Metallurgy, Univ. of Oulu (Finland)

    2009-11-15

    Coke is used as a reducing agent in the production of ferrochromium in a submerged arc furnace (SAF). Its good electrical conductivity compared to other input materials makes it a dominant current conductivity substance in the burden. The resistance of the coke has to be high enough to ensure the proper functionality of the furnace. Used cokes for submerged arc furnace production are relatively small in size compared to e.g. blast furnace (BF) cokes. A common practice is to use screening residual coke, which is too small for the BF, in SAF. The goal of this study was to show differences in the electrical properties of screening residual cokes compared to coke formed in different parts of the coke battery, in dependence of particle size. The resistances of different cokes were measured and XRD measurements were performed to define the crystallographic structure of the selected cokes. The results indicate that small coke particles have higher overall resistance, which is due to their internal properties. This small weakly carbonized coke is formed in the middle of the coking battery and is subject to changes in varying coking practices. Continuous quality control of screening residual coke is needed to use it in the SAF. (orig.)

  8. Recycling of rubber tires in electric arc furnace steelmaking: simultaneous combustion of metallurgical coke and rubber tyres blends

    Energy Technology Data Exchange (ETDEWEB)

    Magdalena Zaharia; Veena Sahajwalla; Byong-Chul Kim; Rita Khanna; N. Saha-Chaudhury; Paul O' Kane; Jonathan Dicker; Catherine Skidmore; David Knights [University of New South Wales, Sydney, NSW (Australia). School of Materials Science and Engineering

    2009-05-15

    The present study investigates the effect of addition of waste rubber tires on the combustion behavior of its blends with coke for carbon injection in electric arc furnace steelmaking. Waste rubber tires were mixed in different proportions with metallurgical coke (MC) (10:90, 20:80, 30:70) for combustion and pyrolysis at 1473 K in a drop tube furnace (DTF) and thermogravimetric analyzer (TGA), respectively. Under experimental conditions most of the rubber blends indicated higher combustion efficiencies compared to those of the constituent coke. In the early stage of combustion the weight loss rate of the blends is much faster compared to that of the raw coke due to the higher volatile yield of rubber. The presence of rubber in the blends may have had an impact upon the structure during the release and combustion of their high volatile matter (VM) and hence increased char burnout. Measurements of micropore surface area and bulk density of the chars collected after combustion support the higher combustion efficiency of the blends in comparison to coke alone. The surface morphology of the 30% rubber blend revealed pores in the residual char that might be attributed to volatile evolution during high temperature reaction in oxygen atmosphere. Physical properties and VM appear to have a major effect upon the measured combustion efficiency of rubber blends. The study demonstrates that waste rubber tires can be successfully co-injected with metallurgical coke in electric arc furnace steelmaking process to provide additional energy from combustion. 44 refs., 11 figs., 2 tabs.

  9. Recycling of Malaysia's electric arc furnace (EAF) slag waste into heavy-duty green ceramic tile.

    Science.gov (United States)

    Teo, Pao-Ter; Anasyida, Abu Seman; Basu, Projjal; Nurulakmal, Mohd Sharif

    2014-12-01

    Recently, various solid wastes from industry such as glass waste, fly ash, sewage sludge and slag have been recycled into various value-added products such as ceramic tile. The conventional solutions of dumping the wastes in landfills or incineration, including in Malaysia are getting obsolete as the annual huge amount of the solid wastes would boost-up disposal cost and may cause permanent damage to the flora and fauna. This recent waste recycling approach is much better and greener as it can resolve problems associated with over-limit storage of industrial wastes and reduce exploration of natural resources for ceramic tile to continuously sustain the nature. Therefore, in this project, an attempt was made to recycle electric arc furnace (EAF) slag waste, obtained from Malaysia's steel making industry, into ceramic tile via conventional powder compaction method. The research work was divided into two stages. The first stage was to evaluate the suitability of EAF slag in ceramic tile by varying weight percentage of EAF slag (40 wt.%, 50 wt.% and 60 wt.%) and ball clay (40 wt.%, 50 wt.% and 60 wt.%), with no addition of silica and potash feldspar. In the second stage, the weight percentage of EAF slag was fixed at 40 wt.% and the percentage of ball clay (30 wt.% and 40 wt.%), feldspar (10 wt.% and 20 wt.%) and silica (10 wt.% and 20 wt.%) added was varied accordingly. Results obtained show that as weight percentage of EAF slag increased up to 60 wt.%, the percentage of apparent porosity and water absorption also rose, with a reduction in tile flexural strength and increased porosity. On the other hand, limiting the weight percentage of EAF slag to 40 wt.% while increasing the weight percentage of ball clay led to a higher total percentage of anorthite and wollastonite minerals, resulting in higher flexural strength. It was found that introduction of silica and feldspar further improved the flexural strength due to optimization of densification process. The highest

  10. Study of the instability of black slags from electric arc furnace steel industry

    Directory of Open Access Journals (Sweden)

    Frías, M.

    2002-09-01

    Full Text Available In Spain, the steel manufacture produces important quantities of by-products, representing between 15 and 20 % of total steel production. Most by-products are deposited on open air spaces causing serious economical and environmental problems, internationally, different recycling wais are studied, being the main alternative for these by-products as recycled aggregate. The possibility of recycling these by-products in construction sector depends on its possible volume instability because of the presence of some undesirable compounds. In current paper, two different black slags from electric arc furnace steel industry were chemically characterized, paying attention to some well-known compounds by theirs expansion effects, such as: free CaO, free MgO, chlorides and sulphates. The analytical results carried out in the current research detected the presence of insignificant or null amounts of harmful compounds. Therefore, they should not have any negative incidence on phenomena of volume instability.

    En España la fabricación de acero produce grandes cantidades de residuos industriales, las cuales representan entre el 15-20 % de la producción total de acero, en su mayor parte se depositan en vertederos, causando serios problemas económicos y medioambientales a todos los sectores implicados. A nivel internacional, se están estudiando diferentes vías de reutilización, siendo su uso principal como árido de reciclado. La posibilidad de reutilizar estos subproductos industriales en el sector de la construcción se basa en su posible inestabilidad volumétrica, debido a la presencia de ciertos compuestos no deseados. En este trabajo se caracterizan químicamente 2 escorias negras de horno de arco eléctrico con diferente procedencia y se cuantifican algunos de los principales compuestos conocidos por sus efectos expansivos, como: cal libre, magnesia libre, cloruros y sulfatos. Los resultados analíticos de estas dos escorias negras muestran

  11. Formation of the ZnFe2O4 phase in an electric arc furnace off-gas treatment system

    International Nuclear Information System (INIS)

    Suetens, T.; Guo, M.; Van Acker, K.; Blanpain, B.

    2015-01-01

    Highlights: • EAF dust was characterized with particle size analysis, XRF, and EPMA. • Slag particles showed no sign of reaction with Zn vapor. • Fe 2 O 3 particles showed different degrees of reaction based on their size. • The thermodynamic stability of Zn vapor in EAF off-gas ducts was reevaluated. • In presence of Fe 2 O 3 , Zn vapor reacts to form ZnFe 2 O 4 and ZnO. - Abstract: To better understand the phenomena of ZnFe 2 O 4 spinel formation in electric arc furnace dust, the dust was characterized with particle size analysis, X-ray fluorescence (XRF), electron backscatter diffraction (EBSD), and electron probe micro-analysis (EPMA). Different ZnFe 2 O 4 formation reaction extents were observed for iron oxide particles with different particle sizes. ZnO particles were present as both individual particles and aggregated on the surface of larger particles. Also, the slag particles found in the off-gas were shown not to react with the zinc vapor. After confirming the presence of a ZnFe 2 O 4 formation reaction, the thermodynamic feasibility of in-process separation – a new electric arc furnace dust treatment technology – was reevaluated. The large air intake and the presence of iron oxide particles in the off-gas were included into the thermodynamic calculations. The formation of the stable ZnFe 2 O 4 spinel phase was shown to be thermodynamically favorable in current electric arc furnace off-gas ducts conditions even before reaching the post combustion chamber

  12. Investigation of possibility for stabilization and valorization of electric ARC furnace dust and glass from electronic waste

    Directory of Open Access Journals (Sweden)

    Ranitović M.

    2014-01-01

    Full Text Available This paper presents investigation of possibility for electric arc furnace dust (EAFD and electronic waste (e-waste valorization trough stabilization process, in order to achieve concurrent management of these two serious ecological problems. EAFD is an ineviTab. waste material coming from the electric arc furnace steel production process, classified as a hazardous waste. Furthermore, it is well known that residual materials generated in the ewaste recycling process, like LCD (Liquid crystal displays waste glass, are not suiTab. for landfill or incineration. In this study, these two materials were used for investigation of possibility for their valorization in ceramic industry. Thus, an innovative synergy of waste streams from metallurgical and e-waste recycling industry is presented. Investigation included a complex characterization of raw materials and their mixtures, using chemical methods, optical microscopy, scanning electron microscopy, as well as methods for determining the physical and mechanical properties. Based on these results, it was found that material suiTab. for use in ceramics industry as a partial substituent of quartzite and fluxing components can be produced. Besides solving the environmental problem related to EAFD and LCD disposal, by replacement of raw materials certain economic effects can be achieved. [Projekat Ministarstva nauke Republike Srbije, br. 34033

  13. The influence of the structure of the metal load removal from liquid steel in electric arc furnaces

    Science.gov (United States)

    Pǎcurar, Cristina; Hepuť, Teodor; Crisan, Eugen

    2016-06-01

    One of the main technical and economic indicators in the steel industry and steel respectively the development it is the removal of liquid steel. This indicator depends on several factors, namely technology: the structure and the quality metal load, the degree of preparedness of it, and the content of non-metallic material accompanying the unit of drawing up, the technology for the elaboration, etc. research has been taken into account in drawing up steel electric arc furnace type spring EBT (Electric Bottom taping), seeking to load and removing components of liquid steel. Metal load has been composed of eight metal grades, in some cases with great differences in terms of quality. Data obtained were processed in the EXCEL spreadsheet programs and MATLAB, the results obtained being presented both graphically and analytically. On the basis of the results obtained may opt for a load optimal structure metal.

  14. Where Diffusion of Clean Technologies and Barriers to Innovation Clash: Application to the Global Diffusion of the Electrical Arc Furnace

    Directory of Open Access Journals (Sweden)

    José Antonio Moya

    2017-01-01

    Full Text Available This paper analyses the role of barriers preventing the worldwide take-up of a clean technology: the electrical arc furnace. It also identifies which barriers affect a parameter that summarises the combined effect of all of them. The first step, determination of the combined effect of the barriers, is carried out using a novel approach to model the diffusion of innovations. This new approach is composed only by terms that account for the driver of innovations and the parameter that summarises the effect of barriers. The objective quantification of the effect of barriers in the diffusion of innovations opens up new opportunities for designing policies to overcome the barriers identified as the most relevant, for identifying the effect of existing policies, for relating innovation indicators with those barriers or for better incorporating the effect of barriers in bottom-up models that forecast the technological evolution of the economy.

  15. Characterization of electric arc furnace dust aiming reuse; Caracterizacao da poeira de aciaria eletrica visando o seu reaproveitamento

    Energy Technology Data Exchange (ETDEWEB)

    Grillo, F.F.; Oliveira, E.B.G.; Oliveira, J.R. de, E-mail: fgrillo@ifes.edu.b [Instituto Federal de Ciencia e Tecnologia do Espirito Santo (IFES), Vitoria, ES (Brazil); Telles, V.B.; Tenorio, J.A.S. [Universidade de Sao Paulo (USP), SP (Brazil)

    2010-07-01

    This work aims to study the characterize of steelmaking dust, from the primary refining of steel in Electric Arc Furnace, in order to verify feasibility of reuse through the addition of hot metal in the form of briquette. The techniques used to characterize the dust was chemical analyses, size separation tests, X-ray diffraction analyses (XRD), Scanning Electron Microscopy (SEM). After characterization, was the calculation of reductant considering the complete reduction of iron oxides and then to briquetting. The waste sample is composed essentially of spherical particles and has a very small particle size (85% below 10 {mu}m). The XRD has presented compounds such as ZnFe{sub 2}O{sub 4}, Fe{sub 3}O{sub 4}, ZnO e SiO{sub 2}. This work showed that its possible recovery approximately 92% of metal iron from dust generated during steelmaking.This (author)

  16. Mathematical modelling of heat transfer in dedusting plants and comparison to off-gas measurements at electric arc furnaces

    International Nuclear Information System (INIS)

    Kirschen, Marcus; Velikorodov, Viktor; Pfeifer, Herbert

    2006-01-01

    A mathematical simulation tool is presented in order to model enthalpy flow rates of off-gas and heat transfer of cooling systems at dedusting plants in electric steel making sites. The flexibility of the simulation tool is based on a user-defined series of modular units that describe elementary units of industrial dedusting systems, e.g. water-cooled hot gas duct, air injector, drop-out box, mixing chamber, post-combustion chamber, filter, etc. Results of simulation were checked with measurements at industrial electric steel making plants in order to validate the models for turbulence, heat transfer and chemical reaction kinetics. Comparison between computed and measured gas temperature and composition yield excellent agreement. The simulation tool is used to calculate off-gas temperature and volume flow rate, where off-gas measurements are very difficult to apply due to high gas temperatures and high dust load. Heat transfer from the off-gas to the cooling system was calculated in detail for a pressurised hot water EAF cooling system in order to investigate the impact of the cooling system and the dedusting plant operation on the energy sinks of the electric arc furnace. It is shown that optimum efficiency of post-combustion of EAF off-gas in the water-cooled hot gas duct requires continuous off-gas analysis. Common operation parameters of EAF dedusting systems do not consider the non-steady-state of the EAF off-gas emission efficiently

  17. Mathematical modelling of heat transfer in dedusting plants and comparison to off-gas measurements at electric arc furnaces

    Energy Technology Data Exchange (ETDEWEB)

    Kirschen, Marcus [Institute for Industrial Furnaces and Heat Engineering, RWTH Aachen, Kopernikusstrasse 16, 52074 Aachen (Germany)]. E-mail: kirschen@iob.rwth-aachen.de; Velikorodov, Viktor [Institute for Industrial Furnaces and Heat Engineering, RWTH Aachen, Kopernikusstrasse 16, 52074 Aachen (Germany); Pfeifer, Herbert [Institute for Industrial Furnaces and Heat Engineering, RWTH Aachen, Kopernikusstrasse 16, 52074 Aachen (Germany)

    2006-11-15

    A mathematical simulation tool is presented in order to model enthalpy flow rates of off-gas and heat transfer of cooling systems at dedusting plants in electric steel making sites. The flexibility of the simulation tool is based on a user-defined series of modular units that describe elementary units of industrial dedusting systems, e.g. water-cooled hot gas duct, air injector, drop-out box, mixing chamber, post-combustion chamber, filter, etc. Results of simulation were checked with measurements at industrial electric steel making plants in order to validate the models for turbulence, heat transfer and chemical reaction kinetics. Comparison between computed and measured gas temperature and composition yield excellent agreement. The simulation tool is used to calculate off-gas temperature and volume flow rate, where off-gas measurements are very difficult to apply due to high gas temperatures and high dust load. Heat transfer from the off-gas to the cooling system was calculated in detail for a pressurised hot water EAF cooling system in order to investigate the impact of the cooling system and the dedusting plant operation on the energy sinks of the electric arc furnace. It is shown that optimum efficiency of post-combustion of EAF off-gas in the water-cooled hot gas duct requires continuous off-gas analysis. Common operation parameters of EAF dedusting systems do not consider the non-steady-state of the EAF off-gas emission efficiently.

  18. A two-stage metal valorisation process from electric arc furnace dust (EAFD

    Directory of Open Access Journals (Sweden)

    H. Issa

    2016-04-01

    Full Text Available This paper demonstrates possibility of separate zinc and lead recovery from coal composite pellets, composed of EAFD with other synergetic iron-bearing wastes and by-products (mill scale, pyrite-cinder, magnetite concentrate, through a two-stage process. The results show that in the first, low temp erature stage performed in electro-resistant furnace, removal of lead is enabled due to presence of chlorides in the system. In the second stage, performed at higher temperatures in Direct Current (DC plasma furnace, valorisation of zinc is conducted. Using this process, several final products were obtained, including a higher purity zinc oxide, which, by its properties, corresponds washed Waelz oxide.

  19. Computational Modeling of Arc-Slag Interaction in DC Furnaces

    Science.gov (United States)

    Reynolds, Quinn G.

    2017-02-01

    The plasma arc is central to the operation of the direct-current arc furnace, a unit operation commonly used in high-temperature processing of both primary ores and recycled metals. The arc is a high-velocity, high-temperature jet of ionized gas created and sustained by interactions among the thermal, momentum, and electromagnetic fields resulting from the passage of electric current. In addition to being the primary source of thermal energy, the arc jet also couples mechanically with the bath of molten process material within the furnace, causing substantial splashing and stirring in the region in which it impinges. The arc's interaction with the molten bath inside the furnace is studied through use of a multiphase, multiphysics computational magnetohydrodynamic model developed in the OpenFOAM® framework. Results from the computational solver are compared with empirical correlations that account for arc-slag interaction effects.

  20. Electric arc furnace dust utilization in iron ore sintering: influence of particle size; Utilizacao da poeira de aciaria eletrica na sinterizacao de minerio de ferro: influencia da granulometria

    Energy Technology Data Exchange (ETDEWEB)

    Telles, V.B.; Junca, E.; Rodrigues, G.F.; Espinosa, D.C.R.; Tenorio, J.A.S., E-mail: victor_bridit@hotmail.co [Universidade de Sao Paulo (USP), SP (Brazil). Dept. de Engenharia Metalurgica e de Materiais

    2010-07-01

    The aim of this work was to study the utilization of electric arc furnace dust (EAFD) generated in steelmaking by electric arc furnace (EAF) as raw material in iron ore sintering. The waste was characterized by size, chemical composition and X-ray diffraction. The physical characterization showed that 90% of the particles have a size less then 1,78 {mu}m and the material have the tendency to agglomerate. The waste were submitted to a pre-agglomeration prior to its incorporation in the sinter. The influence on the addition of the waste with different granulometry in the iron or sinter production were analyzed by sinter characterization and sintering parameters. (author)

  1. HYDRAULIC AND LEACHING BEHAVIOUR OF BELITE CEMENTS PRODUCED WITH ELECTRIC ARC FURNACE STEEL SLAG AS RAW MATERIAL

    Directory of Open Access Journals (Sweden)

    Iacobescu R. I.

    2013-06-01

    Full Text Available Three belite-rich cements consisting of a clinker made with 0 (BC, 5 (BC5 and 10 wt. % (BC10 electric arc furnace steel slag (EAFS as raw material, were studied for their hydraulic and leaching behaviour. Hydration behaviour was studied by FTIR, TG/DTG and SEM analyses. The cements with EAFS resulted in a higher C2S/C3S and C4AF/C3A ratio compared to the reference body. As a result, the rate of hydration was low at early days whereas the structure was porous with scattered AFm and C–S–H crystals. At 28 days, a comparable dense microstructure consisting largely of C–S–H is observed in all mortars. Leaching was studied for V and Cr by means of tank test according to standard NEN 7345. The results showed V release below 2 μg/l. Chromium release calculated per 24 h was 1.4 μg/l in BC5 and 2.4 μg/l in BC10, which is much lower than the parametric value of 50 μg/l specified by the European Directive for drinking water (98/83/EC.

  2. Utilization of Electric Arc Furnace Dust as raw material for the production of ceramic and concrete building products.

    Science.gov (United States)

    Sikalidis, Constantine; Mitrakas, Manassis

    2006-01-01

    The up to 20 wt% addition of the Electric Arc Furnace Dust (EAFD) hazardous waste on the properties of extruded clay-based ceramic building products fired at various temperatures (850 to 1050 degrees C), as well as of dolomite-concrete products was investigated. Chemical, mineralogical and particle size distribution analyses were performed in order to characterize the used EAFD. The results showed that the ceramic specimens prepared had water absorption, firing shrinkage, apparent density, mechanical strength, colour and leaching behaviour within accepted limits. Addition of 7.5 to 15 wt% EAFD presented improved properties, while 20 wt% seems to be the upper limit. Dolomite-concrete specimens were prepared by vibration and press-forming of mixtures containing cement, sand, dolomite, EAFD and water. Modulus of rupture values were significantly increased by the addition of EAFD. The leaching tests showed stabilization of all toxic metals within the sintered ceramic structure, while the leaching behaviour of lead in dolomite-concrete products needs further detailed study.

  3. Application of alkaline solid residue of electric arc furnace dust for neutralization/purification of electroplating wastewaters.

    Science.gov (United States)

    Elez, Loris; Orescanin, Visnja; Sofilic, Tahir; Mikulic, Nenad; Ruk, Damir

    2008-10-01

    The purpose of this work was development of an appropriate procedure for the neutralization/purification of electroplating wastewater (EWW) with alkaline solid residue (ASR) by-product of the alkaline extraction of zinc and lead from electric arc furnace dust (EAFD). Removal efficiency of ASR at optimum purification conditions (pH 8 and mixing time; 20 minutes) for the elements Pb, Cr (VI), Cr (III), Fe, Ni, Cu and Zn were 94.92%, 97.58%, 99.59%, 99.48%, 97.25% and 99.97%, respectively. The concentrations of all elements in the purified wastewater were significantly lower in relation to the upper permissible limit for wastewaters suitable for discharge into the environment. The remaining waste mud was regenerated in the strong alkaline medium and successfully applied once again for the neutralization/purification of EWW. Removal efficiencies of heavy metals accomplished with regenerated waste mud were comparable to these achieved by original ASR. Elemental concentrations in the leachates of the waste mud were in accordance with regulated values.

  4. [Health surveillance in a steel making industry with electric arc furnace: 15 years of experience].

    Science.gov (United States)

    Corti, P

    2012-01-01

    This paper analyzes the results of health surveillance carried out in an electric steel mill for 15 years. We have analyzed the trend of audiometry, spirometry and main indicators of exposure to chemical risk: serum lead, urinary OH-pyrene, erythrocyte ZPP, and the results of risk assessment of stress work related. The analyses of the trend of audiometry, spirometry and biological monitoring shows an important improving in the working environment due to the progressive automation of production steps in the course of several years, consistent and correct use of DPI, information and training.

  5. Recycling of electric arc furnace (EAF dust for use in steel making process

    Directory of Open Access Journals (Sweden)

    José Alencastro de Araújo

    2014-07-01

    Full Text Available The EAF dust is listed as hazardous waste from specific source, K061, according to ABNT 10004:2004 and constitutes one of the major problems of electrical steel plant. This work suggests recycling of the EAF dust by sintering of a composite, pre-cast agglomerate (PCA consisting of EAF dust agglomerate to coke particles, mill scale and ceramic fluorite into pellets. The work was divided into three stages, in the first stage the technical viability of using only solid waste industrial to produce a PCA was observed, in the second phase, the main effects between the components of the PCA to obtain the optimal formulation was tested. In the third phase the intensity of the variables, coke and fluorite ceramics, for removing zinc of PCA was checked. Every stage was chemically analyzed by X-ray fluorescence spectrometer and X-ray diffraction. The first two stages of the production PCA were carried out in a pilot plant sintering downstream and the third phase in a pilot plant upstream. As a result of the process two by-products were obtained, the pre-cast agglomerated, PCA, with total iron content exceeding 70%, object of the process of sintering and zinc dust, containing more than 50% zinc resulting from volatilization of this metal during the sintering process and collected by bag filter. In addition, approximately 90% of lead and cadmium contained in the initial EAF dust was extracted.

  6. Test Plan: Phase 1 demonstration of 3-phase electric arc melting furnace technology for vitrifying high-sodium content low-level radioactive liquid wastes

    Energy Technology Data Exchange (ETDEWEB)

    Eaton, W.C. [ed.

    1995-05-31

    This document provides a test plan for the conduct of electric arc vitrification testing by a vendor in support of the Hanford Tank Waste Remediation System (TWRS) Low-Level Waste (LLW) Vitrification Program. The vendor providing this test plan and conducting the work detailed within it [one of seven selected for glass melter testing under Purchase Order MMI-SVV-384216] is the US Bureau of Mines, Department of the Interior, Albany Research Center, Albany, Oregon. This test plan is for Phase I activities described in the above Purchase Order. Test conduct includes feed preparation activities and melting of glass with Hanford LLW Double-Shell Slurry Feed waste simulant in a 3-phase electric arc (carbon electrode) furnace.

  7. Test Plan: Phase 1 demonstration of 3-phase electric arc melting furnace technology for vitrifying high-sodium content low-level radioactive liquid wastes

    International Nuclear Information System (INIS)

    Eaton, W.C.

    1995-01-01

    This document provides a test plan for the conduct of electric arc vitrification testing by a vendor in support of the Hanford Tank Waste Remediation System (TWRS) Low-Level Waste (LLW) Vitrification Program. The vendor providing this test plan and conducting the work detailed within it [one of seven selected for glass melter testing under Purchase Order MMI-SVV-384216] is the US Bureau of Mines, Department of the Interior, Albany Research Center, Albany, Oregon. This test plan is for Phase I activities described in the above Purchase Order. Test conduct includes feed preparation activities and melting of glass with Hanford LLW Double-Shell Slurry Feed waste simulant in a 3-phase electric arc (carbon electrode) furnace

  8. Effects of body formulation and firing temperature to properties of ceramic tile incorporated with electric arc furnace (EAF) slag waste

    Science.gov (United States)

    Sharif, Nurulakmal Mohd; Lim, Chi Yang; Teo, Pao Ter; Seman, Anasyida Abu

    2017-07-01

    Significant quantities of sludge and slag are generated as waste materials or by-products from steel industries. One of the by-products is Electric Arc Furnace (EAF) steel slag which consists of oxides such as CaO, Al2O3 and FeO. This makes it possible for slag to partially replace the raw materials in ceramic tile production. In our preliminary assessment of incorporating the EAF slag into ceramic tile, it was revealed that at fixed firing temperature of 1150°C, the tile of composition 40 wt.% EAF slag - 60 wt.% ball clay has comparable properties with commercial ceramic tile. Thus, this current study would focus on effects of body formulation (different weight percentages of K-feldspar and silica) and different firing temperatures to properties of EAF slag added ceramic tile. EAF slag from Southern Steel Berhad (SSB) was crushed into micron size (EAF slag content was 40 wt.%) and milled with ball clay, K-feldspar and silica before compacted and fired at 1125°C and 1150°C. The EAF slag added tile was characterized in terms of water absorption, apparent porosity, bulk density, modulus of rupture (MOR) and phase analysis via X-ray diffraction (XRD). The composition of 40 wt.% EAF slag - 30 wt.% ball clay - 10 wt.% K-feldspar - 20 wt.% silica (10F_20S), fired at 1150°C showed the lowest water absorption, apparent porosity and highest bulk density due to enhancement of densification process during firing. However, the same composition of ceramic tile (10F_20S) had the highest MOR at lower firing temperature of 1125°C, contributed by presence of the highest total amount of anorthite and wollastonite reinforcement crystalline phases (78.40 wt.%) in the tile. Overall, both the water absorption and MOR of all ceramic tiles surpassed the requirement regulated by MS ISO 13006:2014 Standard (Annex G: Dry-pressed ceramic tile with low water absorption, Eb ≤ 0.50 % and minimum MOR of 35 MPa).

  9. Formation of the ZnFe{sub 2}O{sub 4} phase in an electric arc furnace off-gas treatment system

    Energy Technology Data Exchange (ETDEWEB)

    Suetens, T., E-mail: thomas.suetens@mtm.kuleuven.be; Guo, M., E-mail: muxing.guo@mtm.kuleuven.be; Van Acker, K., E-mail: karel.vanacker@lrd.kuleuven.be; Blanpain, B., E-mail: bart.blanpain@mtm.kuleuven.be

    2015-04-28

    Highlights: • EAF dust was characterized with particle size analysis, XRF, and EPMA. • Slag particles showed no sign of reaction with Zn vapor. • Fe{sub 2}O{sub 3} particles showed different degrees of reaction based on their size. • The thermodynamic stability of Zn vapor in EAF off-gas ducts was reevaluated. • In presence of Fe{sub 2}O{sub 3}, Zn vapor reacts to form ZnFe{sub 2}O{sub 4} and ZnO. - Abstract: To better understand the phenomena of ZnFe{sub 2}O{sub 4} spinel formation in electric arc furnace dust, the dust was characterized with particle size analysis, X-ray fluorescence (XRF), electron backscatter diffraction (EBSD), and electron probe micro-analysis (EPMA). Different ZnFe{sub 2}O{sub 4} formation reaction extents were observed for iron oxide particles with different particle sizes. ZnO particles were present as both individual particles and aggregated on the surface of larger particles. Also, the slag particles found in the off-gas were shown not to react with the zinc vapor. After confirming the presence of a ZnFe{sub 2}O{sub 4} formation reaction, the thermodynamic feasibility of in-process separation – a new electric arc furnace dust treatment technology – was reevaluated. The large air intake and the presence of iron oxide particles in the off-gas were included into the thermodynamic calculations. The formation of the stable ZnFe{sub 2}O{sub 4} spinel phase was shown to be thermodynamically favorable in current electric arc furnace off-gas ducts conditions even before reaching the post combustion chamber.

  10. Optimizing of Work Arc Furnace to Decopperisation of Flash Slag

    Directory of Open Access Journals (Sweden)

    Bydałek A.W.

    2015-09-01

    Full Text Available Discusses an attempt to optimize the operation of an electric furnace slag to be decopperisation suspension of the internal recycling process for the production of copper. The paper presents a new method to recover copper from metallurgical slags in arc-resistance electric furnace. It involves the use of alternating current for a first period reduction, constant or pulsed DC in the final stage of processing. Even distribution of the electric field density in the final phase of melting caused to achieve an extremely low content of metallic copper in the slag phase. They achieved by including the economic effects by reducing the time reduction.

  11. Increase in the efficiency of electric melting of pellets in an arc furnace with allowance for the energy effect of afterburning of carbon oxide in slag using fuel-oxygen burners

    Science.gov (United States)

    Stepanov, V. A.; Krakht, L. N.; Merker, E. E.; Sazonov, A. V.; Chermenev, E. A.

    2015-12-01

    The problems of increasing the efficiency of electric steelmaking using fuel-oxygen burners to supply oxygen for the afterburning of effluent gases in an arc furnace are considered. The application of a new energy-saving regime based on a proposed technology of electric melting is shown to intensify the processes of slag formation, heating, and metal decarburization.

  12. Influence of direct reduced iron on the energy balance of the electric arc furnace in steel industry

    International Nuclear Information System (INIS)

    Kirschen, Marcus; Badr, Karim; Pfeifer, Herbert

    2011-01-01

    A model of the EAF energy efficiency was developed based on a closed mass and energy balance of the EAF melting process. This model was applied to industrial EAFs in steel industry charged with scrap or with mixes of scrap and DRI. Complex mass and energy conversion in the EAF was simplified with the introduction of mass and energy conversion efficiencies for the conversion of oxygen and the energy conversion of electrical energy in the electric arcs, chemical energy from the oxidation reactions in the melt and energy from the combustion of burner gas. It turned out that close agreement with observed process parameters from 16 EAFs is obtained by slight variations of the efficiency values. Especially the sensitivity of the steel temperature from the energy conversion efficiency of the electric arc energy indicates the importance of efficient foaming slag operation in EAF steel making. Characteristics and process parameters of DRI charged EAFs are discussed. Model results for a series of case studies illustrate the correlations between DRI chemical composition, DRI portion, oxygen consumption, etc. with electrical energy demand in order to indentify cost-effective EAF process conditions. -- Highlights: → Energy demand and carbon dioxide emission figures of EAF steelmaking processes based on steel scrap and DRI. → Complete energy balance of the EAF process using various input materials. → Application of the model to industrial EAF in steel industry in 4 case studies and discussion of model results. → Comparison with other models, critical discussion.

  13. The effect of smelting time and composition of palm kernel shell charcoal reductant toward extractive Pomalaa nickel laterite ore in mini electric arc furnace

    Science.gov (United States)

    Sihotang, Iqbal Huda; Supriyatna, Yayat Iman; Ismail, Ika; Sulistijono

    2018-04-01

    Indonesia is a country that is rich in natural resources. Being a third country which has a nickel laterite ore in the world after New Caledonia and Philippines. However, the processing of nickel laterite ore to increase its levels in Indonesia is still lacking. In the processing of nickel laterite ore into metal, it can be processed by pyrometallurgy method that typically use coal as a reductant. However, coal is a non-renewable energy and have high enough levels of pollution. One potentially replace is the biomass, that is a renewable energy. Palm kernel shell are biomass that can be used as a reductant because it has a fairly high fix carbon content. This research aims to make nickel laterite ores become metal using palm kernel shell charcoal as reductant in mini electric arc furnace. The result show that the best smelting time of this research is 60 minutes with the best composition of the reductant is 2,000 gram.

  14. Similarity of Ferrosilicon Submerged Arc Furnaces With Different Geometrical Parameters

    Directory of Open Access Journals (Sweden)

    Machulec B.

    2017-12-01

    Full Text Available In order to determine reasons of unsatisfactory production output regarding one of the 12 MVA furnaces, a comparative analysis with a furnace of higher power that showed a markedly better production output was performed. For comparison of ferrosilicon furnaces with different geometrical parameters and transformer powers, the theory of physical similarity was applied. Geometrical, electrical and thermal parameters of the reaction zones are included in the comparative analysis. For furnaces with different geometrical parameters, it is important to ensure the same temperature conditions of the reaction zones. Due to diverse mechanisms of heat generation, different criteria for determination of thermal and electrical similarity for the upper and lower reaction zones were assumed contrary to other publications. The parameter c3 (Westly was assumed the similarity criterion for the upper furnace zones where heat is generated as a result of resistive heating while the parameter J1 (Jaccard was assumed the similarity criterion for the lower furnace zones where heat is generated due to arc radiation.

  15. Energy efficiency and the influence of gas burners to the energy related carbon dioxide emissions of electric arc furnaces in steel industry

    International Nuclear Information System (INIS)

    Kirschen, Marcus; Risonarta, Victor; Pfeifer, Herbert

    2009-01-01

    Determining the complete energy balance of an electric arc furnace (EAF) provides an appropriate method to examine energy efficiency and identify energy saving potentials. However, the EAF energy balance is complex due to the combined input of electrical energy and chemical energy resulting from natural gas (NG) combustion and oxidation reactions in the steel melt. In addition, furnace off-gas measurements and slag analysis are necessary to reliably determine energy sinks. In this paper 70 energy balances and energy efficiencies from multiple EAFs are presented, including data calculated from plant measurements and compiled from the literature. Potential errors that can be incorporated in these calculations are also highlighted. The total energy requirement of these modern EAFs analysed ranged from 510 to 880 kWh/t, with energy efficiency values (η = ΔH Steel /E Total ) of between 40% and 75%. Furthermore, the focus was placed on the total energy related CO 2 emissions of EAF processes comprising NG combustion and electrical energy input. By assessing multiple EAF energy balances, a significant correlation between the total energy requirement and energy related specific CO 2 emissions was not evident. Whilst the specific consumption of NG in the EAF only had a minor impact on the EAF energy efficiency, it decreased the specific electrical energy requirement and increased EAF productivity where transformer power was restricted. The analysis also demonstrated that complementing and substituting electrical energy with NG was beneficial in reducing the total energy related CO 2 emissions when a certain level of substitution efficiency was achieved. Therefore, the appropriate use of NG burners in modern EAFs can result in an increased EAF energy intensity, whilst the total energy related CO 2 emissions remain constant or are even decreased.

  16. Glass: Rotary Electric Glass Furnace

    Energy Technology Data Exchange (ETDEWEB)

    Recca, L.

    1999-01-29

    Compared to conventional gas-fired furnaces, the new rotary electric furnace will increase energy efficiency while significantly reducing air emissions, product turnaround time, and labor costs. As this informative new fact sheet explains, the thousand different types of glass optical blanks produced for the photonics industry are used for lasers, telescopes, cameras, lights, and many other products.

  17. Chemical energy in electro arc furnace - examples from experience

    International Nuclear Information System (INIS)

    Shushlevski, Ljupcho; Georgievski, Panche; Hadzhidaovski, Ilija

    2004-01-01

    Great competition on the market in steel-producing and chemical lack of electrical energy leads to realization of new project in section Steelworks AD 'Makstil' - Skopje named: 'Substitution of electrical energy i.e. entering of additional chemical energy in Electrical arc furnace for steel melting using fuels-naturual gas (CH 4 ), oxygen (O 2 ) and carbon (C)'. It is accumulate experience from two and one half year of intensive use of chemical energy with its accompanying problems, appropriate efficiency and economy in process for steel producing. In 2001 year we announced and described project for using of an additional alternative chemical energy in aggregate Electrical are furnace. In this work we will present realization, working experience and efficiency of the system for generating chemical energy. Practical realization needs serious approach in chemical energy usage The usage of chemical energy brings restrictions and needs many innovation for protection of equipment from shown aggressiveness during the combustion of fuel gasses. (Author)

  18. Behaviour of radionuclides during accidental melting of orphan sources in electric arc furnaces by means of C.F.D. gas flow modeling

    International Nuclear Information System (INIS)

    Penalva, I.; Damborenea, J.; Legarda, F.; Zuloaga, P.; Ordonez, M.; Serrano, I.

    2006-01-01

    The appearance of orphan sources in steelmaking facilities has become a fact nowadays. Radiation sources, hidden within the scrap, may come into the scrap yard and become part of the melting. As a result, dispersion of the radioactive material that makes up the source takes place throughout the facility. The University of the Basque Country (U.P.V.-E.H.U.), in collaboration with the Empresa Nacional de Residuos Radiactivos, S.A. (E.N.R.E.S.A.) and the Consejo de Seguridad Nuclear (C.S.N.), has carried out a Research Project to analyze this accidental melting of radioactive sources in electric arc furnaces (E.A.F.). The whole steelmaking process can be analyzed in several discrete phases. Radioactive sources that may be incorporated to this process will be exposed to the different critical conditions prevailing during each phase. In this sense, Computational Fluid Dynamics (C.F.D.) has been used in order to recreate such conditions and so, determine the characteristics of the dispersion of radioactivity. Two different situations have been studied in detail using C.F.D. techniques: thermal conditions around a scrap-basket that contains the source just before entering the furnace and the deposition of steelmaking dust containing 137 Cs on the inner surface of flue pipes. Before entering the furnace, scrap is usually placed inside a basket that remains above the furnace during some time. Once the furnace is open the scrap is dropped into the furnace to complete the loading process. C.F.D. techniques have been used to analyze the thermal conditions around the basket in order to assess the possibility of a break of the radioactive source hidden within the scrap, concluding that commercial sources will maintain their integrity during the whole loading process. On the other hand, after entering the furnace dispersion of the radioactive material will take place. Physical and chemical properties of the active elements (chemical form, composition, melting point, etc

  19. Behaviour of radionuclides during accidental melting of orphan sources in electric arc furnaces by means of C.F.D. gas flow modeling

    Energy Technology Data Exchange (ETDEWEB)

    Penalva, I.; Damborenea, J.; Legarda, F. [University of the Basque Country, Nuclear Engineering and Fluids Mechanics (Spain); Zuloaga, P.; Ordonez, M. [Empresa Nacional de Residuos Radiactivos, SA (ENRESA), Madrid (Spain); Serrano, I. [Consejo de Seguridad Nuclear, Madrid (Spain)

    2006-07-01

    The appearance of orphan sources in steelmaking facilities has become a fact nowadays. Radiation sources, hidden within the scrap, may come into the scrap yard and become part of the melting. As a result, dispersion of the radioactive material that makes up the source takes place throughout the facility. The University of the Basque Country (U.P.V.-E.H.U.), in collaboration with the Empresa Nacional de Residuos Radiactivos, S.A. (E.N.R.E.S.A.) and the Consejo de Seguridad Nuclear (C.S.N.), has carried out a Research Project to analyze this accidental melting of radioactive sources in electric arc furnaces (E.A.F.). The whole steelmaking process can be analyzed in several discrete phases. Radioactive sources that may be incorporated to this process will be exposed to the different critical conditions prevailing during each phase. In this sense, Computational Fluid Dynamics (C.F.D.) has been used in order to recreate such conditions and so, determine the characteristics of the dispersion of radioactivity. Two different situations have been studied in detail using C.F.D. techniques: thermal conditions around a scrap-basket that contains the source just before entering the furnace and the deposition of steelmaking dust containing {sup 137}Cs on the inner surface of flue pipes. Before entering the furnace, scrap is usually placed inside a basket that remains above the furnace during some time. Once the furnace is open the scrap is dropped into the furnace to complete the loading process. C.F.D. techniques have been used to analyze the thermal conditions around the basket in order to assess the possibility of a break of the radioactive source hidden within the scrap, concluding that commercial sources will maintain their integrity during the whole loading process. On the other hand, after entering the furnace dispersion of the radioactive material will take place. Physical and chemical properties of the active elements (chemical form, composition, melting point, etc

  20. Advances in chemical and physical properties of electric arc furnace carbon steel slag by hot stage processing and mineral mixing.

    Science.gov (United States)

    Liapis, Ioannis; Papayianni, Ioanna

    2015-01-01

    Slags are recognised as a highly efficient, cost effective tool in the metal processing industry, by minimising heat losses, reducing metal oxidation through contact with air, removing metal impurities and protecting refractories and graphite electrodes. When compared to natural aggregates for use in the construction industry, slags have higher specific weight that acts as an economic deterrent. A method of altering the specific weight of EAFC slag by hot stage processing and mineral mixing, during steel production is presented in this article. The method has minimal interference with the production process of steel, even by limited additions of appropriate minerals at high temperatures. Five minerals are examined, namely perlite, ladle furnace slag, bauxite, diatomite and olivine. Measurements of specific weight are accompanied by X-ray diffraction (XRD) and fluorescence (XRF) analysis and scanning electron microscopy spectral images. It is also shown how altering the chemical composition is expected to affect the furnace refractory lining. Additionally, the process has been repeated for the most suitable mix in gas furnace and physical properties (FI, SI, LA, PSV, AAV, volume stability) examined. Alteration of the specific weight can result in tailoring slag properties for specific applications in the construction sector. Copyright © 2014 Elsevier B.V. All rights reserved.

  1. Advances in chemical and physical properties of electric arc furnace carbon steel slag by hot stage processing and mineral mixing

    International Nuclear Information System (INIS)

    Liapis, Ioannis; Papayianni, Ioanna

    2015-01-01

    Highlights: • Addition of 10% perlite decreases specific weight of the slag by approx. 7.5%. • Slag-crucible interaction and thin coating layer result in variations in XRF. • XRD shows high glass content and smaller crystalline sizes due to rapid cooling. • SEM shows higher homogeneity and lower crystallisation for SiO 2 /CaO-rich samples. • Physical properties (LA, PSV, AAV) of modified slag show limited deterioration. - Abstract: Slags are recognised as a highly efficient, cost effective tool in the metal processing industry, by minimising heat losses, reducing metal oxidation through contact with air, removing metal impurities and protecting refractories and graphite electrodes. When compared to natural aggregates for use in the construction industry, slags have higher specific weight that acts as an economic deterrent. A method of altering the specific weight of EAFC slag by hot stage processing and mineral mixing, during steel production is presented in this article. The method has minimal interference with the production process of steel, even by limited additions of appropriate minerals at high temperatures. Five minerals are examined, namely perlite, ladle furnace slag, bauxite, diatomite and olivine. Measurements of specific weight are accompanied by X-ray diffraction (XRD) and fluorescence (XRF) analysis and scanning electron microscopy spectral images. It is also shown how altering the chemical composition is expected to affect the furnace refractory lining. Additionally, the process has been repeated for the most suitable mix in gas furnace and physical properties (FI, SI, LA, PSV, AAV, volume stability) examined. Alteration of the specific weight can result in tailoring slag properties for specific applications in the construction sector

  2. Advances in chemical and physical properties of electric arc furnace carbon steel slag by hot stage processing and mineral mixing

    Energy Technology Data Exchange (ETDEWEB)

    Liapis, Ioannis, E-mail: iliapis@sidenor.vionet.gr [AEIFOROS SA, 12th km Thessaloniki-Veroia Rd, PO Box 59, 57008 Ionia, Thessaloniki (Greece); Papayianni, Ioanna [Laboratory of Building Materials, Department of Civil Engineering, Aristotle University of Thessaloniki, 54124 Thessaloniki (Greece)

    2015-02-11

    Highlights: • Addition of 10% perlite decreases specific weight of the slag by approx. 7.5%. • Slag-crucible interaction and thin coating layer result in variations in XRF. • XRD shows high glass content and smaller crystalline sizes due to rapid cooling. • SEM shows higher homogeneity and lower crystallisation for SiO{sub 2}/CaO-rich samples. • Physical properties (LA, PSV, AAV) of modified slag show limited deterioration. - Abstract: Slags are recognised as a highly efficient, cost effective tool in the metal processing industry, by minimising heat losses, reducing metal oxidation through contact with air, removing metal impurities and protecting refractories and graphite electrodes. When compared to natural aggregates for use in the construction industry, slags have higher specific weight that acts as an economic deterrent. A method of altering the specific weight of EAFC slag by hot stage processing and mineral mixing, during steel production is presented in this article. The method has minimal interference with the production process of steel, even by limited additions of appropriate minerals at high temperatures. Five minerals are examined, namely perlite, ladle furnace slag, bauxite, diatomite and olivine. Measurements of specific weight are accompanied by X-ray diffraction (XRD) and fluorescence (XRF) analysis and scanning electron microscopy spectral images. It is also shown how altering the chemical composition is expected to affect the furnace refractory lining. Additionally, the process has been repeated for the most suitable mix in gas furnace and physical properties (FI, SI, LA, PSV, AAV, volume stability) examined. Alteration of the specific weight can result in tailoring slag properties for specific applications in the construction sector.

  3. Study on the Fluid Flow Characteristics of Coherent Jets with CO2 and O2 Mixed Injection in Electric Arc Furnace Steelmaking Processes

    Science.gov (United States)

    Wei, Guangsheng; Zhu, Rong; Wu, Xuetao; Yang, Lingzhi; Dong, Kai; Cheng, Ting; Tang, Tianping

    2018-06-01

    As an efficient oxygen supplying technology, coherent jets are widely applied in electric arc furnace (EAF) steelmaking processes to strengthen chemical energy input, speed up smelting rhythm, and promote the uniformity of molten bath temperature and compositions. Recently, the coherent jet with CO2 and O2 mixed injection (COMI) was proposed and demonstrated great application potentiality in reducing the dust production in EAF steelmaking. In the present study, based on the eddy dissipation concept model, a computational fluid dynamics model of coherent jets with COMI was built with the overall and detailed chemical kinetic mechanisms (GRI-Mech 3.0). Compared with one-step combustion reaction, GRI-Mech 3.0 consists of 325 elementary reactions with 53 components and can predict more accurate results. The numerical simulation results were validated by the combustion experiment data. The jet behavior and the fluid flow characteristics of coherent jets with COMI under 298 K and 1700 K (25 °C and 1427 °C) were studied and the results showed that for coherent jets with COMI, the chemical effect of CO2 significantly weakened the shrouding combustion reactions of CH4 and the relative importance of the chemical effect of CO2 increases with CO2 concentration increasing. The potential core length of coherent jet decreases with the volume fraction of CO2 increasing. Moreover, it also can be found that the potential core length of coherent jets was prolonged with higher ambient temperature.

  4. Study on the Fluid Flow Characteristics of Coherent Jets with CO2 and O2 Mixed Injection in Electric Arc Furnace Steelmaking Processes

    Science.gov (United States)

    Wei, Guangsheng; Zhu, Rong; Wu, Xuetao; Yang, Lingzhi; Dong, Kai; Cheng, Ting; Tang, Tianping

    2018-03-01

    As an efficient oxygen supplying technology, coherent jets are widely applied in electric arc furnace (EAF) steelmaking processes to strengthen chemical energy input, speed up smelting rhythm, and promote the uniformity of molten bath temperature and compositions. Recently, the coherent jet with CO2 and O2 mixed injection (COMI) was proposed and demonstrated great application potentiality in reducing the dust production in EAF steelmaking. In the present study, based on the eddy dissipation concept model, a computational fluid dynamics model of coherent jets with COMI was built with the overall and detailed chemical kinetic mechanisms (GRI-Mech 3.0). Compared with one-step combustion reaction, GRI-Mech 3.0 consists of 325 elementary reactions with 53 components and can predict more accurate results. The numerical simulation results were validated by the combustion experiment data. The jet behavior and the fluid flow characteristics of coherent jets with COMI under 298 K and 1700 K (25 °C and 1427 °C) were studied and the results showed that for coherent jets with COMI, the chemical effect of CO2 significantly weakened the shrouding combustion reactions of CH4 and the relative importance of the chemical effect of CO2 increases with CO2 concentration increasing. The potential core length of coherent jet decreases with the volume fraction of CO2 increasing. Moreover, it also can be found that the potential core length of coherent jets was prolonged with higher ambient temperature.

  5. Characterisation of the sintering behaviour of Waelz slag from electric arc furnace (EAF) dust recycling for use in the clay ceramics industry.

    Science.gov (United States)

    Quijorna, N; de Pedro, M; Romero, M; Andrés, A

    2014-01-01

    Waelz slag is an industrial by-product from the recovery of electric arc furnace (EAF) dust which is mainly sent to landfills. Despite the different chemical and mineralogical compositions of Waelz slag compared to traditional clays, previous experiments have demonstrated its potential use as a clay substitute in ceramic processes. Indeed, clayey products containing Waelz slag could improve mechanical and environmental performance, fixing most of the metallic species and moreover decreasing the release of some potential pollutants during firing. However, a deeper understanding of the complex phase transformations during its thermal treatment and the connection of this behaviour with the end properties is desirable in order to explain the role that is played by the Waelz slag and its potential contribution to the ceramic process. For this purpose, in the present study, the chemical, mineralogical, thermal and environmental behaviour of both (i) unfired powdered samples, and (ii) pressed specimen of Waelz slag fired up to different temperatures within the typical range of clay based ceramic production, has been studied. The effect of the heating temperature on the end properties of the fired samples has been assessed. In general, an increase of the firing temperature promotes sintering and densification of the products and decreases the open porosity and water absorption which also contributes to the fixation of heavy metals. On the contrary, an increase in the leaching of Pb, Cr and Mo from the fired specimens is observed. This can be attributed to the creation of Fe and Ca molybdates and chromates that are weakly retained in the alkali matrix. On the other side, at temperature above 950 °C a weight gain related to the emission of evolved gases is observed. In conclusion, the firing temperature of the ceramic process is a key parameter that affects not only the technical properties but also strongly affects the leaching behaviour and the process emissions

  6. The dual-electrode DC arc furnace-modelling brush arc conditions

    OpenAIRE

    Reynolds, Q.G.

    2012-01-01

    The dual-electrode DC arc furnace, an alternative design using an anode and cathode electrode instead of a hearth anode, was studied at small scale using computational modelling methods. Particular attention was paid to the effect of two key design variables, the arc length and the electrode separation, on the furnace behaviour. It was found that reducing the arc length to brush arc conditions was a valid means of overcoming several of the limitations of the dual-electrode design, namely high...

  7. Design and analysis of high current DC power supply for vacuum arc melting furnace

    International Nuclear Information System (INIS)

    Adhikary, Santu; Sharma, Vishnu Kumar; Sharma, Archana

    2015-01-01

    Vacuum Arc furnace (VAR), is used for melting of ingot in many industrial units. Till now in many industries the existing power supply for VAR is based on magnetic amplifier, which is a lossy component. Thus an efficient topology is needed to develop as a suitable alternative for the existing power supply. Basically Arc in electrical furnace is an unstable phenomena, it has drooping characteristic in nature so to stabilize the arc we need a power supply across the load (arc), which is more drooping in nature than arc characteristics. So this paper highlights the stability and response analysis of several alternative topologies and Stabilization of arc using the feedback and firing angle control in MATLAB. The work also covers comparison among those topologies to choose the optimized topology as a suitable alternative of the existing magnetic amplifier based power supply and the detail design of the proposed topology with a tested trail circuit in PROTEUS. (author)

  8. Electric arc hydrogen heaters

    International Nuclear Information System (INIS)

    Zasypin, I.M.

    2000-01-01

    The experimental data on the electric arc burning in hydrogen are presented. Empirical and semiempirical dependences for calculating the arc characteristics are derived. An engineering method of calculating plasma torches for hydrogen heating is proposed. A model of interaction of a hydrogen arc with a gas flow is outlined. The characteristics of plasma torches for heating hydrogen and hydrogen-bearing gases are described. (author)

  9. Energy Balance in DC Arc Plasma Melting Furnace

    International Nuclear Information System (INIS)

    Zhao Peng; Meng Yuedong; Yu Xinyao; Chen Longwei; Jiang Yiman; Nie Guohua; Chen Mingzhou

    2009-01-01

    In order to treat hazardous municipal solid waste incinerator's (MSWI) fly ash, a new DC arc plasma furnace was developed. Taking an arc of 100 V/1000 A DC as an example, the heat transfer characteristics of the DC arc plasma, ablation of electrodes, heat properties of the fly ash during melting, heat transfer characteristics of the flue gas, and heat loss of the furnace were analyzed based on the energy conservation law, so as to achieve the total heat information and energy balance during plasma processing, and to provide a theoretical basis for an optimized design of the structure and to improve energy efficiency. (plasma technology)

  10. [The electric furnace of Henri Moissan at one hundred years: connection with the electric furnace, the solar furnace, the plasma furnace?].

    Science.gov (United States)

    Royère, C

    1999-03-01

    The trace of Henri Moissan's pioneer work 100 years ago is clearly evidenced by an overview of achievements in high temperature devices; 1987: "Le four électrique" by Henri Moissan; 1948-1952: "High temperature heating in a cavity rotary kiln using focusing of solar radiation" by Félix Trombe; 1962: "The cavity rotary kiln using focused solar radiation jointly with a plasma gun" by Marc Foëx; 1970: "The rotary kiln with two plasma guns and arc transfer" by Marc Foëx; 1984: "The plasma furnace" by Electricité de France (EDF) at Renardières; 1997: "The plasma furnace" by the Atomic Energy Center (CEA) at Cadarache, the VULCANO program. The first part of this contribution is devoted to Henri Moissan. Re-reading his early book on the electric furnace, especially the first chapter and the sections on silica, carbon vapor and experiments performed in casting molten metal--the conclusions are outstanding--provides modern readers with an amazing insight into future developments. The last two parts are devoted to Félix Trombe and Marc Foëx, tracing the evolution of high temperature cavity processus leading to the solar furnace and the present day plasma furnace at the CEA. Focus is placed on research conducted by the French National Center for Scientific Research (CNRS) with the solar and plasma furnaces at Odeillo. The relationships with Henri Moissan's early work are amazing, offering a well deserved homage to this pioneer researcher.

  11. Computer-integrated electric-arc melting process control system

    OpenAIRE

    Дёмин, Дмитрий Александрович

    2014-01-01

    Developing common principles of completing melting process automation systems with hardware and creating on their basis rational choices of computer- integrated electricarc melting control systems is an actual task since it allows a comprehensive approach to the issue of modernizing melting sites of workshops. This approach allows to form the computer-integrated electric-arc furnace control system as part of a queuing system “electric-arc furnace - foundry conveyor” and consider, when taking ...

  12. Method of operating a centrifugal plasma arc furnace

    International Nuclear Information System (INIS)

    Kujawa, S.T.; Battleson, D.M.; Rademacher, E.L. Jr.; Cashell, P.V.; Filius, K.D.; Flannery, P.A.; Whitworth, C.G.

    1998-01-01

    A centrifugal plasma arc furnace is used to vitrify contaminated soils and other waste materials. An assessment of the characteristics of the waste is performed prior to introducing the waste into the furnace. Based on the assessment, a predetermined amount of iron is added to each batch of waste. The waste is melted in an oxidizing atmosphere into a slag. The added iron is oxidized into Fe 3 O 4 . Time of exposure to oxygen is controlled so that the iron does not oxidize into Fe 2 O 3 . Slag in the furnace remains relatively non-viscous and consequently it pours out of the furnace readily. Cooled and solidified slag produced by the furnace is very resistant to groundwater leaching. The slag can be safely buried in the earth without fear of contaminating groundwater. 3 figs

  13. Producción de aceros al carbono en hornos de arco eléctrico en condiciones de mineral de manganeso. // Steel production in electric arc furnaces in the condition of use of manganese.

    Directory of Open Access Journals (Sweden)

    E. E. Navas Medina

    2007-05-01

    Full Text Available El presente trabajo constituye una segunda etapa de investigación relacionada con la producción de acero en hornos de arcoeléctrico con revestimiento básico en condiciones de utilización de mineral de manganeso como sustituto del ferromanganeso.En la investigación se caracteriza el acero producido utilizando el mineral de manganeso en dos variantes tecnológicasdiferentes y se determinan parámetros importantes, tales como la estructura del acero obtenido, la influencia de lacomposición química y la temperatura en la reducción del Mn. Adicionalmente, se determina la composición química de laescoria, su basicidad e influencia en el aprovechamiento del Mn del mineral, así como, lo que significa la sustitución delFeMn en la problemática medioambiental.Palabras claves: Producción de aceros al carbono, hornos de arco eléctricos, mineral de manganeso.______________________________________________________________________________Abstract:This present work constitutes the second stage of investigation in relation with the steel production bymeans of electric arc furnaces in the condition of use of manganese ores as a substitute of theferromanganese. In the investigation, the steel manufactured is analyzed the manganese ore in twodifferent technological variants and some important parameters are determined such as: the chemicalcomposition's structure of the steel, the influence of temperature in the reduction of Mn. Moreover, ananalysis of the chemical composition of the slag and the influence in the environmental is realized.Key words: Carbon steel production, electric arc furnaces, manganese mineral.

  14. Graphite electrode DC arc furnace. Innovative technology summary report

    International Nuclear Information System (INIS)

    1999-05-01

    The Graphite Electrode DC Arc Furnace (DC Arc) is a high-temperature thermal process, which has been adapted from a commercial technology, for the treatment of mixed waste. A DC Arc Furnace heats waste to a temperature such that the waste is converted into a molten form that cools into a stable glassy and/or crystalline waste form. Hazardous organics are destroyed through combustion or pyrolysis during the process and the majority of the hazardous metals and radioactive components are incorporated in the molten phase. The DC Arc Furnace chamber temperature is approximately 593--704 C and melt temperatures are as high as 1,500 C. The DC Arc system has an air pollution control system (APCS) to remove particulate and volatiles from the offgas. The advantage of the DC Arc is that it is a single, high-temperature thermal process that minimizes the need for multiple treatment systems and for extensive sorting/segregating of large volumes of waste. The DC Arc has the potential to treat a wide range of wastes, minimize the need for sorting, reduce the final waste volumes, produce a leach resistant waste form, and destroy organic contaminants. Although the DC arc plasma furnace exhibits great promise for treating the types of mixed waste that are commonly present at many DOE sites, several data and technology deficiencies were identified by the Mixed Waste Focus Area (MWFA) regarding this thermal waste processing technique. The technology deficiencies that have been addressed by the current studies include: establishing the partitioning behavior of radionuclides, surrogates, and hazardous metals among the product streams (metal, slag, and offgas) as a function of operating parameters, including melt temperature, plenum atmosphere, organic loading, chloride concentration, and particle size; demonstrating the efficacy of waste product removal systems for slag and metal phases; determining component durability through test runs of extended duration, evaluating the effect of

  15. Electric contact arcing

    International Nuclear Information System (INIS)

    Cuthrell, R.E.

    1976-01-01

    Electrical contacts must function properly in many types of components used in nuclear weapon systems. Design, application, and testing of these components require detailed knowledge of chemical and physical phenomena associated with stockpile storage, stockpile testing, and operation. In the past, investigation of these phenomena has led to significant discoveries on the effects of surface contaminants, friction and wear, and the mechanics of closure on contact performance. A recent investigation of contact arcing phenomena which revealed that, preceding contact closure, arcs may occur at voltages lower than had been previously known is described. This discovery is important, since arcing may damage contacts, and repetitive testing of contacts performed as part of a quality assurance program might produce cumulative damage that would yield misleading life-test data and could prevent proper operation of the contacts at some time in the future. This damage can be avoided by determining the conditions under which arcing occurs, and ensuring that these conditions are avoided in contact testing

  16. Addition of electric arc furnace dust in hot metal changing the form of addition; Adicao de poeira de aciaria eletrica em ferro-gusa liquido alterando a forma de adicao

    Energy Technology Data Exchange (ETDEWEB)

    Marques Sobrinho, Vicente de Paulo Ferreira; Oliveira, Jose Roberto de; Vieira, Estefano Aparecido, E-mail: vicente@ifes.edu.br [Institulo Federal do Espirito Santo (IFES), ES (Brazil); Telles, Victor Bridi; Grillo, Felipe Fardin; Tenorio, Jorge Alberto Soares; Espinosa, Denise Crocce Romano [Universidade de Sao Paulo (USP), SP (Brazil). Escola Politecnica

    2014-07-01

    This research aims to study the incorporation of the mass of electric arc furnace dust (EAFD), by addition in hot metal (1.78% Si) at a temperature of 1,400 degrees Celsius. The EAFD is from a steel plant producing long steel. The addition of the EAFD was as received, in the form of briquettes without agitation of the hot metal and in the form of briquettes with agitation of the hot metal. Previously, the EAFD was characterized using the following techniques: chemical analysis, size analysis, X-ray diffraction, scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) microanalysis. The achievement of fusion experiments in laboratory scale, took place in a vertical tubular furnace with temperature control. The fusion experiments to assess the incorporation of EAFD mass used graphite crucibles. After cooling, the hot metal and the slag, remaining in the crucible, were weighed to do a mass balance. A flow of inert gas (argon) was maintained inside the furnace during the experiments. Results show that the experiment with addition of EAFD as received presents the best result of incorporating the mass of the final hot metal (1.73%) combined with the lowest percentage of volatilized mass of EAFD (46.52%). The experiment addition of EAFD in the form of briquette with agitation of hot metal presents the lowest percentage of slag mass (4.58%). The zinc content of volatilized EAFD (64.30%) is higher than the zinc content of the imported ore concentrate (52%) and zinc content of the national ore concentrate (12% to 39%). The presence of lead and cadmium in the slag characterizing it as a hazardous solid waste. (author)

  17. Utilización de las escorias de los hornos de arco eléctrico y de cuchara como materiales de construcción. // Use of slags from ladle and electric arc furnaces as construction materials.

    Directory of Open Access Journals (Sweden)

    R. Zaragoza Valdés

    2001-01-01

    Full Text Available La necesidad que tiene la humanidad de que las producciones sean cada día mas limpias, así como la que tiene el país del aumento dela rentabilidad de las empresas, hace necesario el estudio del uso de las escorias que se obtienen en la producción de acero, principalresidual de este tipo de producción. En el trabajo se estudia la utilización de la escoria del Horno de Arco Eléctrico (HAE comomaterial de relleno en la confección de bloques de hormigón para la construcción de edificaciones, sustituyendo la grava de granito.Se estudia, además, el uso de la escoria de los hornos cuchara (HC como sustituto del clinquer en la fabricación de cementosportland. Se obtienen resultados positivos para la protección del medio ambiente y la economía de la empresa metalúrgica.Palabras claves: producción de acero, escorias, medio ambiente, cementos, materiales para la construcción.________________________________________________________________________________Abstract:The existing necessity of clean productions as welll as the profitability of enterprises that the Cuban economy is demanding makes itnecessary to carry out a study of slags that constitute t he main residue of the steel production. This paper presents the use of slags comingfrom electric arc furnaces (EAF as a substitute for gravel in the production of concrete bricks. The use of slags coming from ladle furnaces(LF to replace clinker in the production of Portland Cement is also shown. Positive results are obtained such as the protection of theenvironment and the economic growth of the enterperise.Key words:Steel making, slags, environment protection, cement, construction materials.

  18. Electric melting furnace for waste solidification

    International Nuclear Information System (INIS)

    Masaki, Toshio.

    1990-01-01

    To avoid electric troubles or reduction of waste processing performance even when platinum group elements are contained in wastes to be applied with glass solidification. For this purpose, a side electrode is disposed to the side wall of a melting vessel and a central electrode serving as a counter electrode is disposed about at the center inside the melting vessel. With such a constitution, if conductive materials are deposited at the bottom of the furnace or the bottom of the melting vessel, heating currents flow selectively between the side electrode and the central electrode. Accordingly, no electric currents flow through the conductive deposits thereby enabling to prevent abnormal heating in the bottom of the furnace. Further, heat generated by electric supply between the side electrode and the central electrode is supplied efficiently to raw material on the surface of the molten glass liquid to improve the processing performance. Further, disposition of the bottom electrode at the bottom of the furnace enables current supply between the central electrode and the bottom electrode to facilitate the temperature control for the molten glass in the furnace than in the conventional structure. (I.S.)

  19. Development of processes for zircaloy chips recycling by electric arc furnace remelting and powder metallurgy; Desenvolvimento de processos de reciclagem de cavacos de zircaloy via refusao em forno eletrico a arco e metalurgia do po

    Energy Technology Data Exchange (ETDEWEB)

    Pereira, Luiz Alberto Tavares

    2014-09-01

    PWR reactors employ, as nuclear fuel, UO{sub 2} pellets with Zircaloy clad. In the fabrication of fuel element parts, machining chips from the alloys are generated. As the Zircaloy chips cannot be discarded as ordinary metallic waste, the recycling of this material is important for the Brazilian Nuclear Policy, which targets the reprocess of Zircaloy residues for economic and environmental aspects. This work presents two methods developed in order to recycle Zircaloy chips. In one of the methods, Zircaloy machining chips were refused using an electric-arc furnace to obtain small laboratory ingots. The second one uses powder metallurgy techniques, where the chips were submitted to hydriding process and the resulting material was milled, isostatically pressed and vacuum sintered. The ingots were heat-treated by vacuum annealing. The microstructures resulting from both processing methods were characterized using optical and scanning electron microscopy. Chemical composition, crystal phases and hardness were also determined. The results showed that the composition of recycled Zircaloy comply with the chemical specifications and presented adequate microstructure for nuclear use. The good results of the powder metallurgy method suggest the possibility of producing small parts, like cladding end-caps, using near net shape sintering. (author)

  20. Utilización del polvo de acería de horno de arco eléctrico. // Use of powder produced by electric arc furnaces at steel plants.

    Directory of Open Access Journals (Sweden)

    D. Tápanes Robau

    2001-01-01

    Full Text Available El polvo de las Acerías de Horno de Arco Eléctrico se produce como consecuencia de la producción de Acero, durante ladepuración de los gases, y, en menor medida, en sus equipos de captación de aire. Estos polvos deben ser captados por lossistemas de depuración del taller. Con el presente trabajo pretendemos darle utilidad a un producto de desecho como es elpolvo, mejorar las condiciones ambientales en el taller, elevar la calidad del pavimento u hormigón asfáltico mediante lavariación de sus propiedades y disminuir el costo de la tonelada de acero mediante la comercialización de estos productosde desecho.Palabras claves: Polvos, aglutinantes, composición química, pruebas realizadas._______________________________________________________________________________SummaryThe powder generated by electric arc furnaces at steel plants is the result of processes such as the production of steel, thepurification of gases and, capturing air equipment .This article shows a method for recycling waste material – powder in this case- which also contributes to improve the steelplant environment, provides the possibility of improving asphalt paving and makes the production of steel cheaper throughthe commercialization of waste materials.Key words: Powder, binder, tests, chemical composition.

  1. DC graphite arc furnace, a simple system to reduce mixed waste volume

    Energy Technology Data Exchange (ETDEWEB)

    Wittle, J.K.; Hamilton, R.A.; Trescot, J. [and others

    1995-12-31

    The volume of low-level radioactive waste can be reduced by the high temperature in a DC Graphite Arc Furnace. This volume reduction can take place with the additional benefit of having the solid residue being stabilized by the vitrified product produced in the process. A DC Graphite Arc Furnace is a simple system in which electricity is used to generate heat to vitrify the material and thermally decompose any organic matter in the waste stream. Examples of this type of waste are protective clothing, resins, and grit blast materials produced in the nuclear industry. The various Department of Energy (DOE) complexes produce similar low-level waste streams. Electro-Pyrolysis, Inc. and Svedala/Kennedy Van Saun are engineering and building small 50-kg batch and up to 3,000 kg/hr continuous feed DC furnaces for the remediation, pollution prevention, and decontamination and decommissioning segments of the treatment community. This process has been demonstrated under DOE sponsorship at several facilities and has been shown to produce stable waste forms from surrogate waste materials.

  2. DC graphite arc furnace, a simple system to reduce mixed waste volume

    International Nuclear Information System (INIS)

    Wittle, J.K.; Hamilton, R.A.; Trescot, J.

    1995-01-01

    The volume of low-level radioactive waste can be reduced by the high temperature in a DC Graphite Arc Furnace. This volume reduction can take place with the additional benefit of having the solid residue being stabilized by the vitrified product produced in the process. A DC Graphite Arc Furnace is a simple system in which electricity is used to generate heat to vitrify the material and thermally decompose any organic matter in the waste stream. Examples of this type of waste are protective clothing, resins, and grit blast materials produced in the nuclear industry. The various Department of Energy (DOE) complexes produce similar low-level waste streams. Electro-Pyrolysis, Inc. and Svedala/Kennedy Van Saun are engineering and building small 50-kg batch and up to 3,000 kg/hr continuous feed DC furnaces for the remediation, pollution prevention, and decontamination and decommissioning segments of the treatment community. This process has been demonstrated under DOE sponsorship at several facilities and has been shown to produce stable waste forms from surrogate waste materials

  3. Smelting of high-quality boiler steel in large-load arc furnaces

    Energy Technology Data Exchange (ETDEWEB)

    Kablukovskij, A F; Breus, V M; Tyurin, E I; Khristich, V D; Dumchev, Ya P [Tsentral' nyj Nauchno-Issledovatel' skij Inst. Chernoj Metallurgii, Moscow (USSR)

    1975-02-01

    High-grade steel can be obtained in large-capacity furnaces if the smelting technology used takes account of the size of the aggregates, the course of the metal fusion process, interaction with slag, furnace atmosphere, reducing agents, and other process characteristics. 12Kh1MF boiler steel smelted in a 100-ton electric arc furnace by an oxidizing process with oxygen bath blow and cast by the siphon method into 6.5-ton ingots using a slag-forming mixture (240 mm diameter billets and 219 to 245 mm diameter tubes) is satisfactory with regard to macro and microstructure, oxygen and nonmetallic oxide inclusion content, and mechanical properties. The stress rupture strength of 10/sup 5/ h at 570/sup 0/C is similar to that of open-hearth steel. Sulfides larger than a 3.5 spheroid have been detected in it. The nitrogen content of the electric steel is 0.0090 to 0.0120%, which is somewhat greater than usual in open-hearth metal. Of the oxygen inclusions in the steel, spinel-alumina predominates. Large inclusions were represented mainly by brittle silicates which appeared to be of exogenous origin.

  4. A bench arc-furnace facility for fullerene and single-wall nanotubes synthesis

    Directory of Open Access Journals (Sweden)

    Huber John G

    2001-01-01

    Full Text Available A metallic-sample arc-furnace was modified to synthesize fullerenes and nanotubes. The (reversible changes and the process for producing single-wall nanotubes (SWNTs are described.

  5. Contribution to the study of an electric rotating furnace with gaseous electrodes

    International Nuclear Information System (INIS)

    Dallaire, Serge

    1976-01-01

    As the most primary and also most efficient way to transfer to a body the energetic content of an electric arc is to put it directly in contact with the arc, this research thesis reports the study of the development of a device allowing this operation: the electric rotating furnace with gaseous electrodes. In the first part, the author presents the furnace and its operation characteristics: thermal enclosure, heat source, hardware and installation description, operation characteristics. The second part reports the study of heat transfer phenomena: main determinations of the transfer coefficient, inverse problem, study of the thermal diffusivity with phase change, proposed solutions, and experimental study. The third part reports the search for boundary conditions and the study of furnace efficiency [fr

  6. Electric arc radius and characteristics

    International Nuclear Information System (INIS)

    Fang, T.M.

    1980-01-01

    The heat transfer equation of an arc discharge has been solved. The arc is assumed to be a cylinder with negligible axial variation and the dominant heat transfer process is conduction radially inside the column and radiation/convection at the outside edge. The symmetric consideration allows a simple one-dimensional formulation. By taking into account proper variation of the electrical conductivity as function of temperature, the heat balance equation has been solved analytically. The radius of the arc and its current-field characteristics have also been obtained. The conventional results that E approx. I 0 5385 and R approx. I 0 7693 with E being the applied field, I the current, and R the radius of the cylindrical arc, have been proved to be simply limiting cases of our more general characteristics. The results can be applied quite widely including, among others, the neutral beam injection project in nuclear fusion and MHD energy conversion

  7. Calculation of gas release from DC and AC arc furnaces in a foundry

    Science.gov (United States)

    Krutyanskii, M. M.; Nekhamin, S. M.; Rebikov, E. M.

    2016-12-01

    A procedure for the calculation of gas release from arc furnaces is presented. The procedure is based on the stoichiometric ratios of the oxidation of carbon in liquid iron during the oxidation heat period and the oxidation of iron from a steel charge by oxygen in the period of solid charge melting during the gas exchange of the furnace cavity with the external atmosphere.

  8. Electric arc welding gun

    Science.gov (United States)

    Luttrell, Edward; Turner, Paul W.

    1978-01-01

    This invention relates to improved apparatus for arc welding an interior joint formed by intersecting tubular members. As an example, the invention is well suited for applications where many similar small-diameter vertical lines are to be welded to a long horizontal header. The improved apparatus includes an arc welding gun having a specially designed welding head which is not only very compact but also produces welds that are essentially free from rolled-over solidified metal. The welding head consists of the upper end of the barrel and a reversely extending electrode holder, or tip, which defines an acute angle with the barrel. As used in the above-mentioned example, the gun is positioned to extend upwardly through the vertical member and the joint to be welded, with its welding head disposed within the horizontal header. Depending on the design of the welding head, the barrel then is either rotated or revolved about the axis of the vertical member to cause the electrode to track the joint.

  9. Plasma arc and cold crucible furnace vitrification for medium level waste: a review

    International Nuclear Information System (INIS)

    Poitou, S.; Fiquet, O.; Bourdeloie, C.; Gramondi, P.; Rebollo, F.; Girold, C.; Charvillat, J.P.; Boen, R.; Jouan, A.; Ladirat, C.; Nabot, J.P.; Ochem, D.; Baronnet, J.M.

    2001-01-01

    Initially developed for high-level waste reprocessing, several vitrification processes have been under study since the 80's at the French Atomic Energy Commission (CEA) for other waste categories. According to the French law concerning waste management research passed on December 30, 1991, vitrification may be applied to mixed medium-level waste. A review of processes developed at CEA is presented: cold crucible furnace heated by induced current, refractory furnace heated by nitrogen transferred arc plasma torch, and coupling of cold crucible furnace with oxygen transferred plasma arc twin torch. Furthermore, gas post-combustion has been studied with an oxygen non-transferred plasma torch. (authors)

  10. Behavior of an indigenously fabricated transferred arc plasma furnace for smelting studies

    Science.gov (United States)

    A, K. MANDAL; R, K. DISHWAR; O, P. SINHA

    2018-03-01

    The utilization of industrial solid waste for metal recovery requires high-temperature tools due to the presence of silica and alumina, which is reducible at high temperature. In a plasma arc furnace, transferred arc plasma furnace (TAP) can meet all requirements, but the disadvantage of this technology is the high cost. For performing experiments in the laboratory, the TAP was fabricated indigenously in a laboratory based on the different inputs provided in the literature for the furnace design and fabrication. The observed parameters such as arc length, energy consumption, graphite electrode consumption, noise level as well as lining erosion were characterized for this fabricated furnace. The nitrogen plasma increased by around 200 K (200 °C) melt temperature and noise levels decreased by ∼10 dB compared to a normal arc. Hydrogen plasma offered 100 K (100 °C) higher melt temperature with ∼5 dB higher sound level than nitrogen plasma. Nitrogen plasma arc melting showed lower electrode and energy consumption than normal arc melting, whereas hydrogen plasma showed lower energy consumption and higher electrode consumption in comparison to nitrogen plasma. The higher plasma arc temperature resulted in a shorter meltdown time than normal arc with smoother arcing. Hydrogen plasma permitted more heats, reduced meltdown time, and lower energy consumption, but with increased graphite consumption and crucible wear. The present study showed that the fabricated arc plasma is better than the normal arc furnace with respect to temperature generation, energy consumption, and environmental friendliness. Therefore, it could be used effectively for smelting-reduction studies.

  11. Treatment of simulated INEL buried wastes using a graphite electrode DC arc furnace

    International Nuclear Information System (INIS)

    Surma, J.E.; Lawrence, W.E.; Titus, C.H.; Wittle, J.K.; Hamilton, R.A.; Cohn, D.R.; Rhea, D.; Thomas, P.; Woskov, P.P.

    1994-08-01

    A program has been established under the auspices of the Department of Energy (DOE), Office of Technology Development (OTD), to develop the graphite electrode DC arc technology for the application of treating buried heterogenous solid wastes. A three way open-quotes National Laboratory-University-Industryclose quotes partnership was formed to develop this technology in the most timely and cost effective manner. This program is presently testing a newly fabricated pilot-scale DC arc furnace with associated diagnostics at the Plasma Fusion Center at the Massachusetts Institute of Technology. Initial testing in a smaller engineering scale furnace has established the viability of this technology for the treatment of solid heterogeneous wastes. Two diagnostic tools were developed under this program which support the evaluation of the DC arc technology. The diagnostics provide for both spatially resolved temperature measurements within the furnace and real time monitoring of the furnace metal emissions

  12. INFLUENCE OF THE MODERN SYSTEMS OF THE BLAST STEEL-FURNACE ELECTRICAL PARAMETERS CONTROL ON CAPACITY AND TECHNICAL AND ECONOMICAL INDICES OF MELTING

    Directory of Open Access Journals (Sweden)

    D. N. Andrianov

    2006-01-01

    Full Text Available The reduction of time under the current, electric energy rate, electrodes rate at working of arc steel-furnace with new transformer of capacity 95 MBA and with regulating system SIMELT-AC-NEC are noted.

  13. Graphite electrode DC arc furnace system for treatment of environmentally undesirable solid waste

    International Nuclear Information System (INIS)

    Titus, C.H.

    1993-01-01

    A gas tight DC arc furnace system using graphite electrodes is ideally suited for destruction of organic materials, compaction of metallic materials, and vitrification of inorganic waste materials. A graphite electrode DC arc furnace system which was developed by Electro-Pyrolysis, Inc. has been used to demonstrate that iron basalt soil containing various surrogate nonradioactive materials found on Department of Energy's Atomic Energy Sites and hospital waste can be reduced to a compact, vitrified, solid material which is environmentally acceptable and will pass TCLP leachate tests. A second graphite electrode DC arc furnace system is presently under construction and will be in operation at MIT during the second quarter of 1993. This furnace system is designed for demonstration of waste treatment and stabilization at a rate of 500 pounds per hour and will also be used for development and performance evaluation of diagnostic techniques and equipment for measuring and understanding internal furnace temperature profiles, gas entrained particulate composition, and particulate size distribution in various locations in the furnace during operation

  14. Production of small U Alx alloy buttons in a non consumable electrode arc furnace

    International Nuclear Information System (INIS)

    Koshimizu, S.; Lima, L.F.C.P. de; Leal Neto, R.M.

    1994-01-01

    Some results are presented, concerning with composition and phases, in small buttons of U Al x (10 to 50 g) produced in a non consumable electrode arc furnace. The uranium metal utilised is natural one produced in the IPEN. The convenience of the fabrication of small buttons of U AL x is discussed. (author). 3 refs, 2 figs, 1 tab

  15. Evaluation of the graphite electrode DC arc furnace for the treatment of INEL buried wastes

    International Nuclear Information System (INIS)

    Surma, J.E.; Freeman, C.J.; Powell, T.D.; Cohn, D.R.; Smatlak, D.L.; Thomas, P.; Woskov, P.P.

    1993-06-01

    The past practices of DOE and its predecessor agencies in burying radioactive and hazardous wastes have left DOE with the responsibility of remediating large volumes of buried wastes and contaminated soils. The Buried Waste Integrated Demonstration (BWID), has chosen to evaluate treatment of buried wastes at the Idaho National Engineering Laboratory (INEL). Because of the characteristics of the buried wastes, the potential for using high-temperature thermal treatment technologies is being evaluated. The soil-waste mixture at INEL, when melted or vitrified, produces a glass/ceramic referred to as iron-enriched basalt (IEB). One potential problem with producing the IEB material is the high melting temperature of the waste and soil (1,400-1,600 degrees C). One technology that has demonstrated capabilities to process high melting point materials is the plasma arc heated furnace. A three-party program was initiated and the program involved testing an engineering-scale DC arc furnace to gain preliminary operational and waste processibility information. It also included the design, fabrication, and evaluation of a second-generation, pilot-scale graphite electrode DC arc furnace. Widely ranging simulants of INEL buried waste were prepared and processed in the Mark I furnace. The tests included melting of soils with metals, sludges, combustibles, and simulated drums. Very promising results in terms of waste product quality, volume reduction, heating efficiency, and operational reliability and versatility were obtained. The results indicate that the graphite electrode DC arc technology would be very well suited for treating high melting point wastes such as those found at INEL. The graphite electrode DC arc furnace has been demonstrated to be very simple, yet effective, with excellent prospects for remote or semi-remote operation

  16. Electric Arc Furnace as a Source of Emission of Polychlorinated Dibenzo-p-Dioxins and Polychlorinated Dibenzofurans in Perspective of the Council Directive 96/61 EC Concerning Integrated Pollution Prevention and Control

    Directory of Open Access Journals (Sweden)

    Sofilić, T.

    2008-01-01

    daily care for environmental protection and preservation. This Directive integrates control of emissions and overall impact of industrial installations on the environment, meaning recognition of the entire impact from particular industrial processes on the environment (air, water, soil, waste, noise, use of raw materials, energy efficiency, prevention of accidents, etc.. The IPPC Directive has introduced a system of authorization (environmental permit that needs to be obtained in order to perform business activities and run processes using the best available techniques (BAT.Taking into account the harmful impact of PCDDs/Fs on the environment, and their unavoidability in metallurgical processes, a series of methods has been developed for their partial prevention or at least reduction of their concentration in smoke gas discharge, and thus prevent environmental pollution through these very harmful compounds. In order to prevent the occurrence of PCDDs/Fs metallurgical processes often use methods based on the principle of selective catalyst reduction. For removal of the already generated PCDDs/Fs from waste gases methods of thermal decomposition at high temperatures or various sorption, i. e. "dry" and "wet" cleaning techniques are used.As the implementation of the IPPC Directive is a complex procedure requiring highly educated experts, significant investments into production processes and their modernization, or sometimeseven replacement, steel shops need to timely prepare themselves for the obligations in order to harmonize the existing regulation with the requirements of the IPPC Directive.The requirements of the Directive have to be studied thoroughly. The required steps have to be carefully thought through, previously identifying the cost and time frame necessary to bring the existing electric arc furnace (EAF steel production processes into conformance with the requirements of the IPPC Directive.The paper discusses the requirements of the IPPC Directive that are

  17. Bifurcation theory of ac electric arcing

    International Nuclear Information System (INIS)

    Christen, Thomas; Peinke, Emanuel

    2012-01-01

    The performance of alternating current (ac) electric arcing devices is related to arc extinction or its re-ignition at zero crossings of the current (so-called ‘current zero’, CZ). Theoretical investigations thus usually focus on the transient behaviour of arcs near CZ, e.g. by solving the modelling differential equations in the vicinity of CZ. This paper proposes as an alternative approach to investigate global mathematical properties of the underlying periodically driven dynamic system describing the electric circuit containing the arcing device. For instance, the uniqueness of the trivial solution associated with the insulating state indicates the extinction of any arc. The existence of non-trivial attractors (typically a time-periodic state) points to a re-ignition of certain arcs. The performance regions of arcing devices, such as circuit breakers and arc torches, can thus be identified with the regions of absence and existence, respectively, of non-trivial attractors. Most important for applications, the boundary of a performance region in the model parameter space is then associated with the bifurcation of the non-trivial attractors. The concept is illustrated for simple black-box arc models, such as the Mayr and the Cassie model, by calculating for various cases the performance boundaries associated with the bifurcation of ac arcs. (paper)

  18. Electric arc behaviour in dynamic magnetic fields

    International Nuclear Information System (INIS)

    Put'ko, V.F.

    2000-01-01

    The behaviour of an electric arc in different time-dependent (dynamic) magnetic fields was investigated. New possibilities were found for spatial and energy stabilisation of a discharge, for intensifying heat exchange, extending the electric arc and distributed control of electric arc plasma. Rotating, alternating and travelling magnetic fields were studied. It was found that under the effect of a relatively low frequency of variations of dynamic magnetic fields (f 1000 Hz) the arc stabilised at the axis of the discharge chamber, the pulsation level decreased and discharge stability increased. The borders between these two arc existence modes were formed by a certain critical field variation frequency the period of which was determined by the heat relaxation time of the discharge. (author)

  19. Waste form development for a DC arc furnace

    Energy Technology Data Exchange (ETDEWEB)

    Feng, X.; Bloomer, P.E.; Chantaraprachoom, N.; Gong, M.; Lamar, D.A.

    1996-09-01

    A laboratory crucible study was conducted to develop waste forms to treat nonradioactive simulated {sup 238}Pu heterogeneous debris waste from Savannah River, metal waste from the Idaho National Engineering Laboratory (INEL), and nominal waste also from INEL using DC arc melting. The preliminary results showed that the different waste form compositions had vastly different responses for each processing effect. The reducing condition of DC arc melting had no significant effects on the durability of some waste forms while it decreased the waste form durability from 300 to 700% for other waste forms, which resulted in the failure of some TCLP tests. The right formulations of waste can benefit from devitrification and showed an increase in durability by 40%. Some formulations showed no devitrification effects while others decreased durability by 200%. Increased waste loading also affected waste form behavior, decreasing durability for one waste, increasing durability by 240% for another, and showing no effect for the third waste. All of these responses to the processing and composition variations were dictated by the fundamental glass chemistry and can be adjusted to achieve maximal waste loading, acceptable durability, and desired processing characteristics if each waste formulation is designed for the result according to the glass chemistry.

  20. Operation of arc heating furnace on manufacturing gigantic ingots and segregation of gigantic ingots

    International Nuclear Information System (INIS)

    Niimi, Takayasu; Okamura, Masayoshi

    1976-01-01

    The techniques and procedure for manufacturing gigantic ingots heavier than 200 t are described. Especially, practical results of an arc heating furnace which plays an important role in the procedure and segregation of gigantic ingots are discussed in detail. By appropriate operations of the arc heating furnance, hydrogen and phosphorus are kept unchanged, and oxygen and sulphur decrease to very low levels. Furthermore, the temperature can be accurately controlled. The application of multipour technique reduces segregation and its degree is dependent on kinds of steel. V-segregation and inverted V-segregation in steel deoxidized with carbon in vacuum seem to be very slight. (auth.)

  1. FINDING WAYS OF RECYCLING DUST OF ARC STEEL FURNACES AT THE BELARUSIAN METALLURGIC PLANT

    Directory of Open Access Journals (Sweden)

    A. V. Demin

    2015-01-01

    Full Text Available The first part examines the theoretical possibility of recycling dust of arc steel furnaces. The different modes of dust disposal depending on the task of recycling are discussed: recycling at minimal cost; recycling with a maximum extraction of iron; recycling with maximum extraction of zinc. The results of laboratory studies providing information on the technical feasibility of recycling dust formed at the Belarusian metallurgic plant are provided.

  2. Treatment studies of plutonium-bearing INEEL waste surrogates in a bench-scale arc furnace

    International Nuclear Information System (INIS)

    Freeman, C.J.

    1997-05-01

    Since 1989, the Subsurface Disposal Area (SDA) at the Idaho National Environmental and Engineering Laboratory (INEEL) has been included on the National Priority List for remediation. Arc- and plasma-heated furnaces are being considered for converting the radioactive mixed waste buried in the SDA to a stabilized-vitreous form. Nonradioactive, surrogate SDA wastes have been melted during tests in these types of furnaces, but data are needed on the behavior of transuranic (TRU) constituents, primarily plutonium, during thermal treatment. To begin collecting this data, plutonium-spiked SDA surrogates were processed in a bench-scale arc furnace to quantify the fate of the plutonium and other hazardous and nonhazardous metals. Test conditions included elevating the organic, lead, chloride, and sodium contents of the surrogates. Blends having higher organic contents caused furnace power levels to fluctuate. An organic content corresponding to 50% INEEL soil in a soil-waste blend was the highest achievable before power fluctuations made operating conditions unacceptable. The glass, metal, and off-gas solids produced from each surrogate blend tested were analyzed for elemental (including plutonium) content and the partitioning of each element to the corresponding phase was calculated

  3. Treatment studies of plutonium-bearing INEEL waste surrogates in a bench-scale arc furnace

    Energy Technology Data Exchange (ETDEWEB)

    Freeman, C.J.

    1997-05-01

    Since 1989, the Subsurface Disposal Area (SDA) at the Idaho National Environmental and Engineering Laboratory (INEEL) has been included on the National Priority List for remediation. Arc- and plasma-heated furnaces are being considered for converting the radioactive mixed waste buried in the SDA to a stabilized-vitreous form. Nonradioactive, surrogate SDA wastes have been melted during tests in these types of furnaces, but data are needed on the behavior of transuranic (TRU) constituents, primarily plutonium, during thermal treatment. To begin collecting this data, plutonium-spiked SDA surrogates were processed in a bench-scale arc furnace to quantify the fate of the plutonium and other hazardous and nonhazardous metals. Test conditions included elevating the organic, lead, chloride, and sodium contents of the surrogates. Blends having higher organic contents caused furnace power levels to fluctuate. An organic content corresponding to 50% INEEL soil in a soil-waste blend was the highest achievable before power fluctuations made operating conditions unacceptable. The glass, metal, and off-gas solids produced from each surrogate blend tested were analyzed for elemental (including plutonium) content and the partitioning of each element to the corresponding phase was calculated.

  4. Assessing energy efficiency of electric car bottom furnaces intended for thermal energization of minerals

    Science.gov (United States)

    Nizhegorodov, A. I.

    2017-01-01

    The paper deals with a new concept of electric furnaces for roasting and thermal energization of vermiculite and other minerals with vibrational transportation of a single-layer mass under constant thermal field. The paper presents performance calculation and comparative assessment of energy data for furnaces of different modifications: flame and electric furnaces with three units, furnaces with six units and ones with series-parallel connection of units, and furnaces of new concept.

  5. Estimating the Condition of the Heat Resistant Lining in an Electrical Reduction Furnace

    Directory of Open Access Journals (Sweden)

    Jan G. Waalmann

    1988-01-01

    Full Text Available This paper presents a system for estimating the condition of the heat resistant lining in an electrical reduction furnace for ferrosilicon. The system uses temperature measured with thermocouples placed on the outside of the furnace-pot. These measurements are used together with a mathematical model of the temperature distribution in the lining in a recursive least squares algorithm to estimate the position of 'the transformation front'. The system is part of a monitoring system which is being developed in the AIP-project: 'Condition monitoring of strongly exposed process equipment in thc ferroalloy industry'. The estimator runs on-line, and results arc presented in colour-graphics on a display unit. The goal is to locate the transformation front with an accuracy of +- 5cm.

  6. Simulation of Radiation Heat Transfer in a VAR Furnace Using an Electrical Resistance Network

    Science.gov (United States)

    Ballantyne, A. Stewart

    The use of electrical resistance networks to simulate heat transfer is a well known analytical technique that greatly simplifies the solution of radiation heat transfer problems. In a VAR furnace, radiative heat transfer occurs between the ingot, electrode, and crucible wall; and the arc when the latter is present during melting. To explore the relative heat exchange between these elements, a resistive network model was developed to simulate the heat exchange between the electrode, ingot, and crucible with and without the presence of an arc. This model was then combined with an ingot model to simulate the VAR process and permit a comparison between calculated and observed results during steady state melting. Results from simulations of a variety of alloys of different sizes have demonstrated the validity of the model. Subsequent simulations demonstrate the application of the model to the optimization of both steady state and hot top melt practices, and raises questions concerning heat flux assumptions at the ingot top surface.

  7. Electric arc, water jet cutting of metals

    International Nuclear Information System (INIS)

    Bruening, D.

    1991-01-01

    For thermal dismantling and cutting of metallic components, as electric arc, water jet cutting method was developed that can be used for underwater cutting work up to a depth of 20 m. Short-circuiting of a continuously fed electrode wire in contact with the metal generates an electric arc which induces partial melting of the metal, and the water jet surrounding the wire rinses away the molten material, thus making a continuous kerf in the material. The method was also tested and modified to allow larger area, surface cutting and removal of metallic surface coatings. This is achieved by melting parts of the surface with the electric arc and subsequent rinsing by the water jet. The cutting and melting depth for surface removal can be accurately controlled by the operating parameters chosen. (orig./DG) [de

  8. Improvement of refractories for bottom of DC-Arc furnace; Chokuryudenkiro no roshoyo taikabutsu no kaizen

    Energy Technology Data Exchange (ETDEWEB)

    Kawahara, Toshihiro; Suzuki, Koichi; Okamoto, Yutaka; Tokuchi, Kazumasa [Asahi Glass Corp., Tokyo (Japan)

    1999-06-01

    A conductive refractory furnace bottom type DC electric furnace has disadvantages of large material cost, large working cost and long working period in refractory replacement due to a large amount of refractory installation. The furnace bottom has three layers of permanent bricks, wear bricks and a hot repair material, and durability improvement of wear bricks is an important issue. From the study results for 4 years in a real furnace the following conclusions were obtained: (1) The use of MgO-C based unburned bricks of 15% carbon content as wear bricks reduced the erosion speed by about 20% compared with a conventional MgO-C based burned bricks of 20% carbon content, (2) The resistivity value of the MgO-C based unburned brick decreased to a value equivalent to that of MgO-C based burned brick, which gave no problem in electro conductivity, (3) The addition of the hot repair material over 260 degree C of furnace bottom temperature and stable forming of a protective coating layer of 200-400 mm thickness enabled high durability over 6,400 heats of wear bricks, and (4) The use of the permanent bricks for 15,477 heats promised possible further use. (NEDO)

  9. Furnace

    Energy Technology Data Exchange (ETDEWEB)

    Osintsev, V V; Khidiyatov, A M

    1981-01-01

    The purpose of the invention is to improve the operating efficiency of the furnace device containing prefurnaces connected to the main combustion chamber. For this purpose in the proposed furnace device is equipped with prefurnaces with burners, rectangular vertical chamber of combustion is equipped with central hearth projection. As indicated by studies, the hearth projection of the indicated projections promotes the development of transverse streams which guarantee effective mixing of the combustion products in the upper part of the combustion chamber 3. This reduces the nonuniformity of temperature at the outlet from the latter, decreases the probability of slagging and hot spots on the heating surface.

  10. The movement of the burden in submerged-arc furnaces for the production of high-carbon ferromanganese

    International Nuclear Information System (INIS)

    Dyason, G.J.; See, J.B.

    1978-01-01

    The mechanism by which the burden moves in a submerged-arc furnace was investigated in two large industrial furnaces by the stimulus-response technique with a radiotracer of the radio-isotope 5 Fe as the stimulus. As this radio-isotope was suitable only for the measurement of residence-time distributions in the alloy phase, the analysis of the experiments was limited to that phase. The residence-time distributions obtained by the measurement of alloy samples obtained during tapping were analysed by various techniques. This analysis verified the existence of stagnant zones within the furnace, and showed that the movement of the burden through the furnace could not be described by either of the two idealized patterns of flow, i.e., plug flow or mixed flow. A composite model to describe the movement of the burden through the furnace was developed by consideration of the mechanism and position of heat generation within the furnace, the inner structure of the furnace, the general form of the measured residence-time distributions, and the mode of burden descent through the furnace. The composite model consisted of a dispersed plug-flow region in the upper regions of the furnace discharging into a constantly stirred tank reactor beneath the electrode tips. Non-linear regression analysis of the equations developed from the composite model permitted the selection of optimum values of model parameters to give computed curves that approximated to the residence-time distributions [af

  11. Electrical Safety and Arc Flash Protections

    Energy Technology Data Exchange (ETDEWEB)

    R. Camp

    2008-03-04

    Over the past four years, the Electrical Safety Program at PPPL has evolved in addressing changing regulatory requirements and lessons learned from accident events, particularly in regards to arc flash hazards and implementing NFPA 70E requirements. This presentation will discuss PPPL's approaches to the areas of electrical hazards evaluation, both shock and arc flash; engineered solutions for hazards mitigation such as remote racking of medium voltage breakers, operational changes for hazards avoidance, targeted personnel training and hazard appropriate personal protective equipment. Practical solutions for nominal voltage identification and zero voltage checks for lockout/tagout will also be covered. Finally, we will review the value of a comprehensive electrical drawing program, employee attitudes expressed as a personal safety work ethic, integrated safety management, and sustained management support for continuous safety improvement.

  12. Electrical Safety and Arc Flash Protections

    International Nuclear Information System (INIS)

    Camp, R.

    2008-01-01

    Over the past four years, the Electrical Safety Program at PPPL has evolved in addressing changing regulatory requirements and lessons learned from accident events, particularly in regards to arc flash hazards and implementing NFPA 70E requirements. This presentation will discuss PPPL's approaches to the areas of electrical hazards evaluation, both shock and arc flash; engineered solutions for hazards mitigation such as remote racking of medium voltage breakers, operational changes for hazards avoidance, targeted personnel training and hazard appropriate personal protective equipment. Practical solutions for nominal voltage identification and zero voltage checks for lockout/tagout will also be covered. Finally, we will review the value of a comprehensive electrical drawing program, employee attitudes expressed as a personal safety work ethic, integrated safety management, and sustained management support for continuous safety improvement.

  13. TECHNOLOGICAL PECULIARITIES O F MELTING AND OUT-OF-FURNACE PROCESSING OF BALANCED STEELS IN CONDITIONS OF ELECTRIC FURNACE STEELMAKING AND CONTINUOUS CASTING

    Directory of Open Access Journals (Sweden)

    S. V. Terletski

    2007-01-01

    Full Text Available The technological peculiarities of melting and out-of-furnace processing of balanced steels in conditions of electric furnace steelmaking and continuous cast of RUP “BMZ” are considered.

  14. EFFICIENT USE OF ENERGY IN A ELECTRIC ARC FURNANCE BY HEAT INTEGRATION APPROACH

    OpenAIRE

    Umesh Kumar, Dr. A K Prasad, Sourabh Kumar Soni

    2016-01-01

    Based on the principles of heat integration, the present work investigates the design and operational modifications which can lead to efficient energy integration in an electric arc furnace being operated with direct reduction process. This process is one of the oldest and most widely applied processes amongst the commercially used process in India. For the purpose of energy integration stream data is extracted from the actual flow sheet of the plant, which consists of supply and target tempe...

  15. Coefficient of electrical transport vacuum arc for metals and alloys

    International Nuclear Information System (INIS)

    Markov, G.V.; Ehjzner, B.A.

    1998-01-01

    In this article the authors propose formulas for estimation coefficient of electrical transport vacuum arc for metals and alloys. They also represent results of analysis principal physical processes which take place in cathode spot vacuum arc

  16. Auroral arc classification scheme based on the observed arc-associated electric field pattern

    International Nuclear Information System (INIS)

    Marklund, G.

    1983-06-01

    Radar and rocket electric field observations of auroral arcs have earlier been used to identify essentially four different arc types, namely anticorrelation and correlation arcs (with, respectively, decreased and increased arc-assocaited field) and asymmetric and reversal arcs. In this paper rocket double probe and supplementary observations from the literature, obtained under various geophysical conditions, are used to organize the different arc types on a physical rather than morphological basis. This classification is based on the relative influence on the arc electric field pattern from the two current continuity mechanisms, polarisation electric fields and Birkeland currents. In this context the tangential electric field plays an essential role and it is thus important that it can be obtained with both high accuracy and resolution. In situ observations by sounding rockets are shown to be better suited for this specific task than monostatic radar observations. Depending on the dominating mechanism, estimated quantitatively for a number of arc-crossings, the different arc types have been grouped into the following main categories: Polarisation arcs, Birkeland current arcs and combination arcs. Finally the high altitude potential distributions corresponding to some of the different arc types are presented. (author)

  17. INFLUENCE OF CHEMICAL COMPOUNDS ON THE FORMING OF ELECTRIC ARC

    Directory of Open Access Journals (Sweden)

    I. O. Vakulenko

    2014-07-01

    Full Text Available Purpose. The purpose of work is a comparative analysis of chemical compounds influence on the process of electric arc forming and condition of its burning. Methodology. Material for an electrode was a wire 3 mm in diameter of low carbon steel with contain of carbon 0.15%. As chemical compounds, which determine the terms of forming of arc welding were used kaolin; CaCO3 with the admixtures of gypsum to 60%; SiO2 and Fe – Si with the iron concentration to 50%. Researches were conducted at the use of direct electric current and the arc of reverse polarity. As a source of electric current the welding transformer of type PSO-500 was used. On the special stand an initial gap between the electrode and metal-plate was equal to 1–1.5 mm. The interelectrode interval was filled with the probed chemical compounds and it was formed an electric arc. In the moment of electric arc arise the values of electric current and the arc voltage were determined. After the natural break of electric arc, the final size of the gap between electrodes was accepted as the maximal value of the arc lengths. Findings. In the conditions of experiment the metal transfer in interelectrode interval corresponded to the drop mechanism. According to external characteristics the ratio between the maximal arc length and the power of electric discharge has the appearance of exponential dependence. Specific power of electric arc characterizes environment of interelectrode interval in the moment of arc forming per unit of its length. Originality. 1. On the basis of influence analysis of the studied chemical compounds on the formation processes of electric arc inversely proportional relationship between the power of the electric current and the maximum arc length to the moment of its natural break is defined. 2. The ratio between the maximal arc length and the power of electric current with sufficiently high correlation coefficient is subjected to the exponential dependence. Influence of

  18. Investigation and analysis of the usefulness of the Zellik method to design energy conserving electric furnaces

    Energy Technology Data Exchange (ETDEWEB)

    Szilagyi, L.; Fay, G.

    1984-01-01

    The characteristics predetermined by the method Zellik in designing the electrical furnaces isolated traditionally are comparable with measured values of furnaces in operation. The newest furnaces have been built with isolation resulting in a lower energy consumption. To plot the static characteristics, the furnace was heated up three times to the steady state. In determining the static heat capacity the stored heat was measured by the conventional method. With a view to determining the kinetic heat capacity the furnace was heated up at different rates. On the base of the operating results of the furnace can be stated both the practicability of the method Zellik and the improvement of the characteristics of the furnace isolated with fibrous material.

  19. Utilization of steel melting electric arc furnace slag for development ...

    Indian Academy of Sciences (India)

    Author Affiliations. Ritwik Sarkar1 Nar Singh2 Swapan Kumar Das2. Department of Ceramic Engineering, National Institute of Technology, Rourkela 769 008, India; Refractories Division, Central Glass & Ceramic Research Institute, Kolkata 700 032, India ...

  20. Utilization of steel melting electric arc furnace slag for development ...

    Indian Academy of Sciences (India)

    Administrator

    sole solution in the medium and long term due to diffe- rent technical, social and .... indicates that batches R and T have a very short vitrifica- tion range; this may be .... environmental protection of ocean, Shiraishi Memorial. Lecture of the Iron ...

  1. Presentation of the Vulcano installation which uses a plasma transferred arc rotary furnace for corium melting

    International Nuclear Information System (INIS)

    Cognet, G.; Laffont, G.; Jegou, C.; Pierre, J.; Journeau, C.; Sudreau, F.; Roubaud, A.

    1998-01-01

    In the case of loss coolant accident, the reactor core could melt and turn into a mixture of uranium oxides, zirconium, iron and steel called corium. A large experimental program has been launched to study corium behaviour, to qualify solutions to stabilize it and to confine it in the reactor containment. The Vulcano installation has been designed to that purpose. It is made up of: i) a plasma transferred arc rotary furnace, ii) a testing surface covered with refractory materials, iii) an induction heating system in order to simulate the residual power of corium, iv) instrumentation devices such as video cameras, thermocouples, infra-red pyrometers and flowmeters, and v) a laboratory to perform chemical analysis of corium samples. The first experimental results show that a mixture of corium and concrete spreads better than expected. It seems that a low initial height of matter can produce a great distance flowing while having a chaotic behaviour. This characteristic suggests that the mixture acts as a Bingham type threshold fluid. (A.C.)

  2. Characterization of the behaviour of the electric arc during VAR of a Ti alloy

    Science.gov (United States)

    Chapelle, P.; Noël, C.; Risacher, A.; Jourdan, J.; Jourdan, J.; Jardy, A.

    2016-07-01

    In this paper, we report experimental results based on the direct observation of the electric arc behaviour during vacuum arc remelting of a Ti alloy. These results were obtained in a specifically instrumented industrial furnace using high speed framing camera and optical emission spectroscopy, for a current density level of the order of 10 A/cm2 and a gap length of a few centimetres. It was observed that the arc exhibits a similar operating regime to that described in the literature for the case of Inconel 718 and Zr alloy electrodes. The arc structure corresponds essentially to that of a diffuse metal vapor arc with separate and rapidly moving cathode spots. Several critical parameters of the cathode spots, including their current, size and velocity, and of the interelectrode plasma were evaluated. Also, the interactions between the arc operation and the transfer of metal drops in the interelectrode gap were investigated. Three modes of transfer of the liquid metal drops in the interelectrode gap have been identified depending on the gap length: drop falling, drip short and drop erosion induced by the cathode spots.

  3. Electric fuses operation, a review: 2. Arcing period

    International Nuclear Information System (INIS)

    Bussière, W

    2012-01-01

    In the electric fuse operation the arcing period follows immediately the pre-arcing period depicted in Part 1 (Part 1. Pre-arcing period). The transition between these two operation steps is not fully understood at this time. To simplify the beginning of the arcing period can be identified with the electric arc ignition i.e. with the electrodes voltage drop. The consecutive plasma is of metallic type at the beginning of the arcing period and of metallic plus silica type with varying mixture up to the end of the arcing period. The energy brought by the fault current is withdrawn by means of the interaction between the electric arc and the arc quenching material (usually silica sand) whose morphometric properties influence the properties of the plasma column: composition, thermodynamic properties and transport coefficients of the plasma column depend on the porosity (and other morphometric properties) of the filler. The fuse element erosion also known as burn-back is responsible for the lengthening of the plasma column and the variations of the electric field. The whole of these processes is depicted by means of experimental results or modellings when possible.

  4. Energy efficiency and emissions of arc furnaces in the steel industry; Energieeffizienz und Emissionen der Lichtbogenoefen in der Stahlindustrie

    Energy Technology Data Exchange (ETDEWEB)

    Kirschen, M.

    2007-07-01

    The operation of the electric arc furnace obeys economic constraints that require cost optimal use of the resources scrap, scrap substitutes, alloys, direct reduced iron, pig iron, oxygen, fuel gas, and energy. On the other hand, legal restrictions for minimum emissions must be observed. Comprehensive process models and strategies to optimize the EAF steel production require detailed knowledge about both energy flow rates and emissions. However, this data is often not available in the meltshop due to technical problems or high effort for maintenance of on-line off-gas analysis systems at the EAF. The Institute for Industrial Furnaces and Heat Engineering of RWTH Aachen University performed off-gas measurements at various EAFs during steel production. In some plant trials off-gas measurements were conducted simultaneously at two points in the dedusting system in order to determine the otherwise unknown volume flow rate of air at the gap between the EAF elbow and the hot gas duct. In this work, state-of-the-art off-gas analysis systems are presented. First hints for process development of particular EAFs are derived from off-gas data. Off-gas data complement the meltshop data, that are required for complete mass and energy balances. From recent energy balances, the EAF process is evaluated with respect to off-gas energy and energy efficiency. Recent energy balances from our measurements and from the literature of the last decade show total energy demand between 600 kWh/t and 850 kWh/t and energy efficiency values up to 70%. EAFs with scrap pre-heating technologies achieve highest energy efficiency values up to 70%. Measurements of off-gas and air volume flow rates monitor the efficiency of the EAF dedusting plant in combination with the EAF. With direct exhaust control based on furnace pressure measurement, the specific off-gas mass and energy is decreased significantly. Improvement of the analysis equipment for off-gas measurements at the EAF with focus on very

  5. Studies of hydrogen pellet acceleration by electric arc discharge

    International Nuclear Information System (INIS)

    Andersen, S.

    1986-01-01

    A preliminary design for an arc heated gas gun is described. The experimental development of the final design constitutes the final phase in contract work for JET. The gun consist of a cryogenic arc chamber connected to the inlet of a gun barrel. With a dose of H 2 -gas condensed in the arc chamber and a D 2 -pellet punch loaded into the barrel the gun is fired by the ignition of an electrical discharge in the arc chamber. The pellet is accelerated by the exhaust of hot H 2 -gas from the arc chamber and its velocity and acceleration is measured by time-of-flight along and outside the barrel. The pressure development by the arc is monitored by pressure transducers as well in the arc chamber as in the barrel. The performance of the gun is described in terms of arc current and voltage versus time as functions of power supply configuration and H 2 propellant dose. The time behaviour of the propellant pressure in the arc chamber and in the barrel is shown in relation to the arc current. Pellet acceleration and pressure development in the gun barrel for the arc heated gas gun is discussed and compared to results obtained by conventional fast valve acceleration

  6. Usage of Thermodynamic Activity for Optimization of Power Expenses in Respect of Casting Process in Arc Steel-Melting Furnace

    Directory of Open Access Journals (Sweden)

    A. N. Chichko

    2006-01-01

    Full Text Available The equilibrium between carbon and oxygen has been investigated during oxidizing refining in an arc steel-melting furnace. It is shown that there is a possibility to apply an equilibrium thermodynamic. It has been established that during oxidizing refining FeO concentration in slag practically does not depend on C concentration in metal. It is demonstrated that in a number of cases metal carbon oxidation is characterized by the presence of a transit period that may be attributed to incomplete slag-formation process.

  7. Particle injection into the Castor tokamak by electric arcs

    International Nuclear Information System (INIS)

    Hildebrandt, D.; Juettner, B.; Pursch, H.; Jakubka, K.; Stoeckel, J.; Zacek, F.

    1989-01-01

    The influence of arcing on the tokamak discharge was investigated in the Castor tokamak. A special calibrated gun which emitted tantalum by artificially ignited electric arcs, was used to study the transport of the injected tantalum ions, neutrals and droplets. The injection of tantalum led to an increase in electron density and to a change of plasma position only if the transported charge was higher than 0.01 C. As the naturally occurring arcs are well below this limit, the arcing in tokamaks is rather the consequence than the reason of instabilities. (J.U.)

  8. The use of rotating electric arc for spherical particle production

    International Nuclear Information System (INIS)

    Bica, I.

    2000-01-01

    This work presents and experimental device designed to obtain spherical particles by mans of a rotating electric arc. A rotation frequency of the electric arc of 750 s''-1, a voltage of 50 V(dc) and a current of 100 A was used. The mass flow rate was 3 g.min''-1. Under these conditions particles of 15 to 20 μm in diameter were obtained. (Author) 8 refs

  9. Electrical and optical investigations on the low voltage vacuum arc

    International Nuclear Information System (INIS)

    Braic, M.; Braic, V.; Pavelescu, G.; Balaceanu, M.; Pavelescu, D.; Dumitrescu, G.; Gherendi, F.

    2002-01-01

    Preliminary investigations of a low voltage circuit breaker, adapted from a real industrial device, were carried out by electrical and optical methods. Electrical, parameters were measured in the high current arc period and in zero current moment (C.Z) and corroborated with the arc plasma spectroscopic investigations. For the first time in vacuum arc diagnostics, the paper presents results based on single shot time resolved emission spectroscopy around C.Z. The short-circuit current was produced in a special high power installation in order to reproduce exactly the short-circuit regimes developing in low voltage distribution networks. A stainless steel vacuum chamber with classical Cu-Cr electrodes was used. Tests were performed for different current values in the range 3 - 20 kA rms , the voltages being varied between 200 and 1000 V ac . Interruption processes in the different arc regimes (from the diffuse arc mode to the constricted column mode) were analyzed. The success of the arc interruption was analyzed in terms of electric arc energy achieved in the first current halfperiod. The results obtained were corroborated with arc plasma spectroscopic investigations. The emission spectroscopy setup, using an Acton spectrograph and an intensified CCD camera, allowed the spatial and time-resolved investigation of spectra emitted by the vacuum arc plasma. The first truly time-resolved spectroscopic measurements on a single half-period was proven to be a good method to investigate the vacuum arc. Using single shot time resolved spectroscopy around zero current on partial unsuccessful interruption we concluded that the Cu ions, more that Cr ions were responsible for the arc reignition. The financial support for this work comes from NATO-STI SfP /974083 and CORINT-Romania projects. (authors)

  10. 16 CFR Appendix G2 to Part 305 - Furnaces-Electric

    Science.gov (United States)

    2010-01-01

    ... 16 Commercial Practices 1 2010-01-01 2010-01-01 false Furnaces-Electric G2 Appendix G2 to Part 305 Commercial Practices FEDERAL TRADE COMMISSION REGULATIONS UNDER SPECIFIC ACTS OF CONGRESS RULE CONCERNING... Part 305—Furnaces—Electric Manufacturer's rated heating capacities (Btu's/hr.) Range of annual fuel...

  11. Effect of Feed Forms on the Results of Melting of Fly Ash by a DC Plasma Arc Furnace

    International Nuclear Information System (INIS)

    Chen Mingzhou; Meng Yuedong; Shi Jiabiao; Ni Guohua; Jiang Yiman; Yu Xinyao; Zhao Peng

    2009-01-01

    Fly ash from a municipal solid waste incinerator (MSWI) without preprocessing (original fly ash, OFA) was melted by a direct current (DC) plasma arc furnace to investigate how the feed forms governed the results. Dioxins in flue gas from stack and bag-filter ash (BFA) were detected. The distribution of heavy metals of Pb, Cd, As, and Cr along the flue gas process system was analyzed. Through a comparison of the results for dioxins and heavy metals in this study and previous work, carrying-over of fly ash particles with the flue gas stream can be deduced. Based on the magnetic induction equation and Navier-Stokes equations, a magnetohydrodynamic (MHD) model for the plasma arc was developed to describe the particle-carrying effect. The results indicate that, a. when melted, the feed forms of MSWI fly ash affect the results significantly; b. it is not preferable to melt MSWI fly ash directly, and efforts should be made to limit the mass transfer of OFA from the plasma furnace. (plasma technology)

  12. Effect of Feed Forms on the Results of Melting of Fly Ash by a DC Plasma Arc Furnace

    Science.gov (United States)

    Chen, Mingzhou; Meng, Yuedong; Shi, Jiabiao; Ni, Guohua; Jiang, Yiman; Yu, Xinyao; ZHAO, Peng

    2009-10-01

    Fly ash from a municipal solid waste incinerator (MSWI) without preprocessing (original fly ash, OFA) was melted by a direct current (DC) plasma arc furnace to investigate how the feed forms governed the results. Dioxins in flue gas from stack and bag-filter ash (BFA) were detected. The distribution of heavy metals of Pb, Cd, As, and Cr along the flue gas process system was analyzed. Through a comparison of the results for dioxins and heavy metals in this study and previous work, carrying-over of fly ash particles with the flue gas stream can be deduced. Based on the magnetic induction equation and Navier-Stokes equations, a magnetohydrodynamic (MHD) model for the plasma arc was developed to describe the particle-carrying effect. The results indicate that, a. when melted, the feed forms of MSWI fly ash affect the results significantly; b. it is not preferable to melt MSWI fly ash directly, and efforts should be made to limit the mass transfer of OFA from the plasma furnace.

  13. Electric fields and energetic particle precipitation in an auroral arc

    International Nuclear Information System (INIS)

    Edwards, T.; Bryant, D.A.; Smith, M.J.; Fahleson, U.; Faelthammer, C.G.; Pedersen, A.

    1975-01-01

    Preliminary results are presented from a rocket flight across a single discrete auroral arc extending from early evening to magnetic midnight. The rocket was fired at the end of the growth phase of an isolated auroral substorm. It carried a separating payload to make simultaneous measurements of electrons (0.6 - 25 keV, pitch angle 0 - 60 0 ) at two points. From the main vehicle measurements were also made of ions (same energy range) as well as of the electric field vector and plasma parameters. The electron spectra were hardest towards the centre of the arc, where the peak intensity was at 9.5 keV. The precipitation structure observed was similar to that of an 'inverted V' but on a smaller scale. The electric field was northward south of the arc, southward within the arc and somewhat north of it, then again northward. At the northern edge of the precipitation region the field was very irregular. The field strength reached a maximum of about 50 mV/m some distance north of the arc. The line integral of the electric field across the arc was of the order of a kilovolt, too small to be responsible for the changes observed in the electron energy spectrum. An electric potential distribution, consistent with the results obtained, is present. (Auth.)

  14. Improving the engineering-and-economical performance of ore-thermal electric furnaces in the smelting of silicomanganese

    Science.gov (United States)

    Kondrashov, V. P.; Pogrebisskiy, M. Ya; Lykov, A. G.; Rabinovich, V. L.; Bulgakov, A. S.

    2018-02-01

    Ways of increase of ore-heating electric furnaces, used for production of silicomanganese, engineering-and-economical performance are analyzed. Questions of data of the electric, thermal and technological modes of the furnace functioning collecting and processing for use in operation of an advanced control system of the furnace providing increase in technical and economic efficiency of technological process and an adaptability to quality of burden stock are considered.

  15. Low voltage initiation of damaging arcs between electrical contacts

    International Nuclear Information System (INIS)

    Cuthrell, R.E.

    1975-07-01

    Metallic arcs were found to precede the firm contacting of electrical contacts which were closed without bounce. When the open-circuit voltages were below the ionization potential, the initiation of these arcs was found to depend on the presence of asperities on the surfaces and on asperity contracting, melting, and pinching off by magnetic forces. The arc is thought to be initiated inductively when the molten metallic asperity contact is pinched off, and the electrode damage is similar to that produced by the arcing of opening contacts. Arcing could not be produced for exceptionally smooth surfaces, or, for rough surfaces when the open-circuit potential was below the melting voltages of the electrode metals. In order to prevent damage to contact surfaces by melting or arcing, it is suggested that test potentials be limited to below the melting voltages, that the current be limited, the test circuits be designed to prevent inductively generated high voltage transients, and the contact surfaces be very smooth. In order to facilitate arc initiation in arc welding applications, it is suggested that the surfaces of electrodes and work pieces be roughened. (U.S.)

  16. Research On Technology Of Making Rare Earth Alloy Having Rare Earth Content ≽30% From Ore (≽40% REO) Using Aluminum Thermal Technology In Arc Furnace

    International Nuclear Information System (INIS)

    Ngo Xuan Hung; Ngo Trong Hiep; Tran Duy Hai; Nguyen Huu Phuc

    2014-01-01

    Arc furnace was used to smelt materials consisting of rare earth ore having rare earth content of ≽40% REO, aluminum as the reducing agent and additives. Rare earth alloy was obtained with rare earth metal content of more than 30%. (author)

  17. Feasibility study of utilizing solar furnace technology in steel making industry

    Energy Technology Data Exchange (ETDEWEB)

    Abbaspoursani, K. [The Faculty of Mechanical Engineering, Takestan Islamic Azad University (Iran, Islamic Republic of)], Email: a.abbaspour@tiau.ac.ir; Tofigh, A.A.; Nahang Toudeshki, S.; Hadadian, A. [Department of Energy, Materials and Energy Research Center (Iran, Islamic Republic of)], Email: Ali.A.Tofigh@gmail.com, email: toudeshki@hotmail.com, email: Arash.Hadadian@gmail.com; Farahmandpour, B. [Iranian Fuel Conservation company (Iran, Islamic Republic of)], Email: farahmandpour@gmail.com

    2011-07-01

    In Iran, the casting industry consumes 33.6% of electricity production, and most of this electricity is used in the melting process. Currently, scrap preheating is done using electric arc furnaces and the aim of this study is to assess the feasibility of replacing electric arc furnaces with solar furnaces. The performance of solar furnaces in the Iran Alloy Steel Company under Yazd climate conditions was studied. It was found that the solar irradiation time and solar insulation are sufficient to operate a solar furnace with the capacity to preheat 250 thousand tons per year of scrap to 500 degrees celsius. Results showed that such a furnace would decrease energy consumption by 40 GWh per year and that it would take 5 years to return the investment. This study demonstrated that operating a solar furnace in the Iran Alloy Steel Company under Yazd climate conditions is feasible and would result in economic and environmental benefits.

  18. Inner tubes cutting method by electrical arc saw

    International Nuclear Information System (INIS)

    Thome, P.

    1990-01-01

    The research program deals on the definition of tools used for dismantling steam generator tubes bundle of PWR and on tool used for cutting pipes of great diameter by using the process of cutting by electrical arc saw. The remote tools are used for cutting by the interior pipes of contamined circuits [fr

  19. Electrical and hydrodynamic characterization of a high current pulsed arc

    International Nuclear Information System (INIS)

    Sousa Martins, R; Chemartin, L; Zaepffel, C; Lalande, Ph; Soufiani, A

    2016-01-01

    High current pulsed arcs are of significant industrial interest and, aiming to reduce time and cost, there is progressively more and more need for computation tools that describe and predict the behaviour of these arcs. These simulation codes need inputs and validations by experimental databases, but accurate data is missing for this category of electric discharges. The principal lack of understanding is with respect to the transient phase of the current, which can reach thousands of amperes in a few microseconds. In this paper, we present the work realized on an experimental setup that simulates in the laboratory an arc column subjected to five levels of high pulsed current, ranging from 10 kA to 100 kA, with the last one corresponding to the standard lightning current waveform used in aircraft certification processes. This device was instrumented by high speed video cameras to assess the characteristic sizes of the arc channel and to characterize the shock wave generated by the arc expansion. The arc channel radius was measured over time during the axisymmetric phase and reached 3.2 cm. The position and velocity of the shock wave was determined during the first 140 μs. The background-oriented schlieren method was used to study the shock wave and a model for the light deflection inside the shock wave was developed. The mass density profile of the shock wave was estimated and showed good agreement with Rankine–Hugoniot relations at the wave front. Electrical measurements were also used to estimate the time-dependent resistance and conductivity of the arc for times lasting up to 50 μs. (paper)

  20. Electrical and hydrodynamic characterization of a high current pulsed arc

    Science.gov (United States)

    Sousa Martins, R.; Chemartin, L.; Zaepffel, C.; Lalande, Ph; Soufiani, A.

    2016-05-01

    High current pulsed arcs are of significant industrial interest and, aiming to reduce time and cost, there is progressively more and more need for computation tools that describe and predict the behaviour of these arcs. These simulation codes need inputs and validations by experimental databases, but accurate data is missing for this category of electric discharges. The principal lack of understanding is with respect to the transient phase of the current, which can reach thousands of amperes in a few microseconds. In this paper, we present the work realized on an experimental setup that simulates in the laboratory an arc column subjected to five levels of high pulsed current, ranging from 10 kA to 100 kA, with the last one corresponding to the standard lightning current waveform used in aircraft certification processes. This device was instrumented by high speed video cameras to assess the characteristic sizes of the arc channel and to characterize the shock wave generated by the arc expansion. The arc channel radius was measured over time during the axisymmetric phase and reached 3.2 cm. The position and velocity of the shock wave was determined during the first 140 μs. The background-oriented schlieren method was used to study the shock wave and a model for the light deflection inside the shock wave was developed. The mass density profile of the shock wave was estimated and showed good agreement with Rankine-Hugoniot relations at the wave front. Electrical measurements were also used to estimate the time-dependent resistance and conductivity of the arc for times lasting up to 50 μs.

  1. Electric melting furnace of solidifying radioactive waste by utilizing magnetic field and melting method

    International Nuclear Information System (INIS)

    Igarashi, Hiroshi.

    1990-01-01

    An electric melting furnace for solidification of radioactive wastes utilizing magnetic fields in accordance with the present invention comprises a plurality of electrodes supplying AC current to molten glass in a glass melting furnace and a plurality of magnetic poles for generating AC magnetic fields. Interactions between the current and the magnetic field, generated forces in the identical direction in view of time in the molten glass. That is, forces for promoting the flow of molten glass in the melting furnace are resulted due to the Fleming's left-hand rule. As a result, the following effects can be obtained. (1) The amount of heat ransferred from the molten glass to the starting material layer on the molten surface is increased to improve the melting performance. (2) For an identical melting performance, the size and the weight of the melting furnace can be reduced to decrease the amount of secondary wastes when the apparatus-life is exhausted. (3) Bottom deposits can be suppressed and prevented from settling and depositing to the reactor bottom by the promoted flow in the layer. (4) Further, the size of auxiliary electrodes for directly supplying electric current to heat the molten glass near the reactor bottom can be decreased. (I.S.)

  2. Simultaneous obtention of multicomponent ferroalloy and slag from black sands for the development of electrical arc welding consumables

    International Nuclear Information System (INIS)

    Cruz-Crespo, A.; Gomez-Rodriguez, L.; Garcia-Sanchez, L. L.; Quintana-Puchol, R.; Cerpa-Naranjo, A.; Cores-Sanchez, A.

    2004-01-01

    In this paper, chemical and mineralogical characterizations of the black sands of the Mejias placer of Sagua de Tanamo (the most important beach littoral placer of the northwest of oriental Cuba) are exposed. Starting from these characterizations a calculation strategy is developed for the making of the metallurgical load that allows to obtain simultaneously, when processed by carbothermic reduction in an electrical arc furnace, a multicomponent ferroalloy and a useful slag for the making of electric arch welding consumables. The powder of the obtained slag is agglomerated with liquid glass. The resulting pellets, due to their behavior on the submerged arc welding (SAW) present technological and metallurgical properties that correspond with the requirements of an agglomerated flux matrix. The chemical composition of the multicomponent ferroalloy is constituted by metallic elements of high metallurgical and alloyed values (V, Cr, Mo, Ti, Nb). It is appropriate for the formulation of consumables for manual welding (SMAW) and SAW, as well. (Author) 15 refs

  3. [Utilization of a transferred arc-plasma rotating furnace to melt and found oxide mixtures at around 2000 degrees C (presentation of the film VULCANO)].

    Science.gov (United States)

    Cognet, G; Laffont, G; Jegou, C; Pierre, J; Journeau, C; Sudreau, F; Roubaud, A

    1999-03-01

    Unless security measures are taken, a hypothetical accident resulting from the loss of the cooling circuit in a pressurized water nuclear reactor could cause the heart of the reactor to melt forming a bath, called the corium, mainly composed of uranium, zirconium and iron oxides as well as the structural steel. This type of situation would be similar to the Three Mile Island accident in 1979. In order to limit the consequences of such an accident, the Atomic Energy Commission has implemented a large study program [1] to improve our understanding of corium behavior and determine solutions to stabilize it and avoid its propagation outside the unit. The VULCANO installation was designed in order to perform the trials using real materials which are indispensable to study all the phenomena involved. A film on the VULCANO trials was presented at the Henri Moissan commemorative session organized by the French National Academy of Pharmacy. The rotating furnace used to melt and found the mixture simulating the corium is a direct descendant of the pioneer work by Henri Moissan. An electrical arc is directed at the center of the load to melt which is maintained against the walls by centrifugal force. After six high-temperature trials performed with compositions without uranium oxide, the first trial with real corium showed that the magma spread rather well, a result which is quite favorable for cooling.

  4. Internal Arc: People safety in the electrical wiring

    International Nuclear Information System (INIS)

    Inchausti, J. M.

    2009-01-01

    The aim of this article is to describe the internal arc phenomenon, an extremely fast, almost explosive and unattended process of transformation form an initial electric power to the generation of a pressure and heat wave inside the medium its produced its consequences for safety, current methods of limiting them and current regulations in general for equipment used in medium-voltage electrical distribution networks. Taking into account that this type of equipment is found thought the distribution network in both public buildings and unrestricted access areas, safety (of operators and the general public) must be taken into account in the design of equipment and installations to minimize the risk of internal arcs occurring. This is the gist of, for example, ITC 16 of the Spanish Regulation on Power Plants and transformer substations. In addition to the construction aspects specific to each device in which the manufacturer has to takes steps to minimize the risks of an internal arcs occurring. This is the gist of, for example, ITC 16 of the Spanish Regulation on Power Plants and transformer substations. In addition to the construction aspects specific to each device in which an internal arc occurring, it is understood to be vitally important that users, installers and designers of Medium Voltage installations are familiar with the installation conditions stated by the manufacturer and thus avoid risks. (Author) 14 refs

  5. Destruction of inorganic municipal solid waste incinerator fly ash in a DC arc plasma furnace.

    Science.gov (United States)

    Zhao, Peng; Ni, Guohua; Jiang, Yiman; Chen, Longwei; Chen, Mingzhou; Meng, Yuedong

    2010-09-15

    Due to the toxicity of dioxins, furans and heavy metals, there is a growing environmental concern on municipal solid waste incinerator (MSWI) fly ash in China. The purpose of this study is directed towards the volume-reduction of fly ash without any additive by thermal plasma and recycling of vitrified slag. This process uses extremely high-temperature in an oxygen-starved environment to completely decompose complex waste into very simple molecules. For developing the proper plasma processes to treat MSWI fly ash, a new crucible-type plasma furnace was built. The melting process metamorphosed fly ash to granulated slag that was less than 1/3 of the volume of the fly ash, and about 64% of the weight of the fly ash. The safety of the vitrified slag was tested. The properties of the slag were affected by the differences in the cooling methods. Water-cooled and composite-cooled slag showed more excellent resistance against the leaching of heavy metals and can be utilized as building material without toxicity problems. Copyright 2010 Elsevier B.V. All rights reserved.

  6. Effect of addition of arc furnace dust in the microstructural properties of fly ash alkali-activated

    International Nuclear Information System (INIS)

    Vargas, Alexandre Silva de; Pavao, Bruno Barreto; Masuero, Angela Boreges; Dal Molin, Denise Carpena Coitinho; Vilela, Antonio Cezar Faria

    2010-01-01

    The search for alternative materials for construction, with less environmental impact, has been the subject of several studies. The alkali-activated cements have shown potential for the reuse of waste, and can be used in the technology of solidification/stabilization. Thus, this study aims to evaluate the main effect of adding arc furnace dust (AFD) in the microstructural properties of matrices based on fly ash alkali-activated. Three levels of AFD were studied: 0, 5, 15 and 25%. The curing was set at 70°C/24 h, and after, kept at room temperature until the age of analysis - 1, 28 and 180 days, with XRD and FTIR analysis. In the XRD spectres it was found that compounds of albite and natron decrease the intensity of their peaks in that there is an increase in the levels of AFD. Concerning to the FTIR, we observed that the band characteristic of the fly ash (FA) 1084 cm"-"1 was shifted to bands near 1000 cm"-"1, which shows that the residue does not interfere in the polymerization and aluminosilicate gel formation. Therefore, under the microstructural aspect, there were no major changes that would impair the use of this residue in alkali-activated matrices. (author)

  7. ELECTRIC PROBE INVESTIGATION OF ARC ANODE REGION IN PLASMA TORCH

    Czech Academy of Sciences Publication Activity Database

    Chumak, Oleksiy; Hrabovský, Milan; Kavka, Tetyana

    2006-01-01

    Roč. 10, č. 4 (2006), s. 515-524 ISSN 1093-3611. [High technology plasma processes. Saint-Petersburg, 27.5.2006-4.6.2006] R&D Projects: GA ČR GA202/05/0669 Institutional research plan: CEZ:AV0Z20430508 Keywords : plasma torch * arc * anode attachment * restrike * electric probes Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 0.343, year: 2006

  8. DEVELOPMENT OF SOFTWARE “PRODSP-1.0” FOR OPTIMIZATION OF THE DEPHOSPHORIZATION PROCESSES IN ARC STEEL-FURNACES FOR TECHNOLOGICAL LINE-UP OF RUP “BMZ”

    Directory of Open Access Journals (Sweden)

    A. A. Chichko

    2006-01-01

    Full Text Available The software “ProDSP-1,0” allowing to forecast the dynamics of the dephosphorizaiton process at casting course in arc steel-furnace, is worked out. The examples of working of different program operating regimes, showing the possibilities of phosphorus control in steel-furnace of RUP ‘'BMZ'' are given.

  9. Electric-Arc Plasma Installation for Preparing Nanodispersed Carbon Structures

    International Nuclear Information System (INIS)

    Stefanov, P.; Garlanov, D.; Vissokov, G.

    2008-01-01

    An electric-arc plasma installation operated in the hidden anode arrangement is constructed and used for the preparation of carbon nanostructures. A contracted plasma arc generated by a plasma torch using an inert gas is used as heat source. The average mass temperature of arc is higher than 10 4 K, while its power density, which is directly transferred onto the electrode (anode), is ∼ 2 kW/mm 2 . The anode contact area formed on the electrode moves against the arc by way of shifting the electrode and is hidden completely in the interior of plasma gas stream moving towards it. As a result of both the direct plasma attack and the opposite movement of streams in the hidden anode contact area, a temperature higher than 6000 K is reached. Thus, intensive vaporization takes place, which forms a saturated plasma-gas-aerosol phase of the initial material of electrode (anode). This gas phase is mixed in and carried by the plasma stream. Over that mixed plasma stream, a controlled process of quenching (fixation) is carried out by twisted turbulent fluid streams. After the fixation, the resultant carbon nano-structures are caught by a filter and collected in a bunker.

  10. A Model for Solving the Maxwell Quasi Stationary Equations in a 3-Phase Electric Reduction Furnace

    Directory of Open Access Journals (Sweden)

    S. Ekrann

    1982-10-01

    Full Text Available A computer code has been developed for the approximate computation of electric and magnetic fields within an electric reduction furnace. The paper describes the numerical methods used to solve Maxwell's quasi-stationary equations, which are the governing equations for this problem. The equations are discretized by a staggered grid finite difference technique. The resulting algebraic equations are solved by iterating between computations of electric and magnetic quantities. This 'outer' iteration converges only when the skin depth is larger or of about the same magnitude as the linear dimensions of the computational domain. In solving for electric quantities with magnetic quantities being regarded as known, and vice versa, the central computational task is the solution of a Poisson equation for a scalar potential. These equations are solved by line successive overrelaxation combined with a rebalancing technique.

  11. INFLUENCE OF STRUCTURAL PARAMETERS OF LOW-CARBON STEEL ON ELECTRIC ARC BURNING

    Directory of Open Access Journals (Sweden)

    I. O. Vakulenko

    2017-10-01

    Full Text Available Purpose. The article is aimed to evaluate the influence of structural parameters of low-carbon steel on arcing process. Methodology. The values of the micro- and substructure characteristics of the electrode wire metal were changed by varying the parameters of heat treatment and cold deformation by drawing. The degree of plastic deformation was obtained by drawing blanks from different initial diameter to final dimension of 1 mm. The thermal treatment was carried out in electric chamber furnace of the SNOL-1,6.2,5.1/11-IZ type. The temperature was measured by chromel-alumel thermocouple and the electromotive force was determined using the DC potentiometer. In order to obtain the substructure of different dispersion degree the steel (after quenching from temperatures and tempering at 650°C for 1 hour was subjected to cold drawing to reduction 17 – 80%. To form structure with different ferrite grain size the steel after drawing was annealed at 680°C for 1 hour. The microstructure was examined under a light and electron transmission microscope UEMV-100K at the accelerating voltage 100 kV. The grain and subgrain sizes were evaluated using the methodologies of quantitative metallography. A welding converter of the PSG-500 type was used to study the arc welding process of direct and reverse polarities. Findings. The experimentally detected value of the welding current, which depends on the degree of deformation during wire drawing, under conditions of stable arc burning of direct polarity is about an order of magnitude lower than the calculated value. Similar difference was found for the arc of reverse polarity: the experimental value of the welding current is 5...6 times less than the calculated value. Dependence analysis shows that, regardless of the polarity of the welding arc, a good enough agreement between the calculated and experimental values of the welding current is limited to deformations of 60%. For deformation degrees of more than 60

  12. Production of durable expanded perlite microspheres in a Vertical Electrical Furnace

    Science.gov (United States)

    Panagiotis, M.; Angelopoulos, P.; Taxiarchou, M.; Paspaliaris, I.

    2016-04-01

    Expanded perlite constitutes one of the most competitive insulating materials that is widely used in construction and manufacturing industry due to its unique properties combination; it is white, natural, lightweight, chemically inert, and exhibits superior insulating properties (thermal and acoustic) and fire resistance. Conventionally, perlite expansion is performed in vertical gas-fired furnaces; the conventional perlite expansion process has certain disadvantages which affect expanded products quality, thus limiting their performance and range of applications. In order to overcome the drawbacks of the conventional expansion technique, a new perlite expansion process has been designed based on a vertical electrical furnace (VEF). In the current study, fine perlite samples (-150 μm) from Milos Island, Greece, were expansed in the novel VEF and a conventional gas-fired furnace with the aim to evaluate and compare the main physical properties of the expanded products. The novel expanded perlite particles were characterised by superior properties, namely increased compression strength, competitive water and oil absorption capability, size homogeneity, spherical shape and decreased surface porosity in comparison to conventionally expanded samples.

  13. Novel Direct Steelmaking by Combining Microwave, Electric Arc, and Exothermal Heating Technologies

    Energy Technology Data Exchange (ETDEWEB)

    Dr. Xiaodi Huang; Dr. J. Y. Hwang

    2005-03-28

    Steel is a basic material broadly used by perhaps every industry and individual. It is critical to our nation's economy and national security. Unfortunately, the American steel industry is losing competitiveness in the world steel production field. There is an urgent need to develop the next generation of steelmaking technology for the American steel industry. Direct steelmaking through the combination of microwave, electric arc, and exothermal heating is a revolutionary change from current steelmaking technology. This technology can produce molten steel directly from a shippable agglomerate, consisting of iron oxide fines, powdered coal, and ground limestone. This technology is projected to eliminate many current intermediate steelmaking steps including coking, pellet sintering, blast furnace (BF) ironmaking, and basic oxygen furnace (BOF) steelmaking. This technology has the potential to (a) save up to 45% of the energy consumed by conventional steelmaking; (b) dramatically reduce the emission of CO{sub 2}, SO{sub 2}, NO{sub x}, VOCs, fine particulates, and air toxics; (c) substantially reduce waste and emission control costs; (d) greatly lower capital cost; and (e) considerably reduce steel production costs. This technology is based on the unique capability of microwaves to rapidly heat steelmaking raw materials to elevated temperature, then rapidly reduce iron oxides to metal by volumetric heating. Microwave heating, augmented with electric arc and exothermal reactions, is capable of producing molten steel. This technology has the components necessary to establish the ''future'' domestic steel industry as a technology leader with a strong economically competitive position in world markets. The project goals were to assess the utilization of a new steelmaking technology for its potential to achieve better overall energy efficiency, minimize pollutants and wastes, lower capital and operating costs, and increase the competitiveness of the

  14. Intelligent Support System of Steel Technical Preparation in an Arc Furnace: Functional Scheme of Interactive Builder of the Multi Objective Optimization Problem

    Science.gov (United States)

    Logunova, O. S.; Sibileva, N. S.

    2017-12-01

    The purpose of the study is to increase the efficiency of the steelmaking process in large capacity arc furnace on the basis of implementation a new decision-making system about the composition of charge materials. The authors proposed an interactive builder for the formation of the optimization problem, taking into account the requirements of the customer, normative documents and stocks of charge materials in the warehouse. To implement the interactive builder, the sets of deterministic and stochastic model components are developed, as well as a list of preferences of criteria and constraints.

  15. Single crystal growth of pure and Nd-doped Y2O3 by flotating zone method with Xe arc lamp imaging furnace

    International Nuclear Information System (INIS)

    Tsuiki, H.; Kitazawa, K.; Fueki, K.; Masumoto, T.; Shiroki, K.

    1980-01-01

    Single crystals of undoped and Nd-doped yttrium oxide were grown by the floating zone method with a Xe arc lamp imaging furnace. The crystals were grown in the and directions. Transparent and subgrain-free single crystals were obtained at a growth rate of 30-60 mm/h for the undoped yttrium oxide. Facets of the cubic [100] and [211] were observed though the high temperature phase of the crystal is hexagonal. Dislocation densities of undoped yttrium oxide are given. (orig./WE)

  16. High temperature aircraft research furnace facilities

    Science.gov (United States)

    Smith, James E., Jr.; Cashon, John L.

    1992-01-01

    Focus is on the design, fabrication, and development of the High Temperature Aircraft Research Furnace Facilities (HTARFF). The HTARFF was developed to process electrically conductive materials with high melting points in a low gravity environment. The basic principle of operation is to accurately translate a high temperature arc-plasma gas front as it orbits around a cylindrical sample, thereby making it possible to precisely traverse the entire surface of a sample. The furnace utilizes the gas-tungsten-arc-welding (GTAW) process, also commonly referred to as Tungsten-Inert-Gas (TIG). The HTARFF was developed to further research efforts in the areas of directional solidification, float-zone processing, welding in a low-gravity environment, and segregation effects in metals. The furnace is intended for use aboard the NASA-JSC Reduced Gravity Program KC-135A Aircraft.

  17. Parameter estimation of extended free-burning electric arc within 1 kA

    Science.gov (United States)

    Sun, Qiuqin; Liu, Hao; Wang, Feng; Chen, She; Zhai, Yujia

    2018-05-01

    A long electric arc, as a common phenomenon in the power system, not only damages the electrical equipment but also threatens the safety of the system. In this work, a series of tests on a long electric arc in free air have been conducted. The arc voltage and current data were obtained, and the arc trajectories were captured using a high speed camera. The arc images were digitally processed by means of edge detection, and the length is formulated and achieved. Based on the experimental data, the characteristics of the long arc are discussed. It shows that the arc voltage waveform is close to the square wave with high-frequency components, whereas the current is almost sinusoidal. As the arc length elongates, the arc voltage and the resistance increase sharply. The arc takes a spiral shape with the effect of magnetic forces. The arc length will shorten briefly with the occurrence of the short-circuit phenomenon. Based on the classical Mayr model, the parameters of the long electric arc, including voltage gradient and time constant, with different lengths and current amplitudes are estimated using the linear least-square method. To reduce the computational error, segmentation interpolation is also employed. The results show that the voltage gradient of the long arc is mainly determined by the current amplitude but almost independent of the arc length. However, the time constant is jointly governed by these two variables. The voltage gradient of the arc with the current amplitude at 200-800 A is in the range of 3.9 V/cm-20 V/cm, and the voltage gradient decreases with the increase in current.

  18. Conversion of electric bell type furnace for natural gas usage: a case study

    Energy Technology Data Exchange (ETDEWEB)

    Ferraz, Andre D.; Machado Junior, Antonio R.; Rocha, Ivan C.C. da; Azevedo, Jorge G.W. de; Konishi, Ricardo; Lehmkuhl, Willian A. [Companhia de Gas de Santa Catarina (SCGAS), Florianopolis, SC (Brazil); Nunes, Andrea T.; Possamai, Talita S.; Nicolau, Vicente de P. [Universidade Federal de Santa Catarina (UFSC), Florianopolis, SC (Brazil)

    2012-07-01

    In the present process of the heat treatment of normalizing of the crystalline structure of cast metal pieces, the heating is made by electric resistance arranged on the inner surfaces of the side walls of a bell furnace. Although electrical heating is suitable to obtain a uniform generation on the walls covered with electrical resistances, and is easy to control and operate with virtually no gas flow, it has some disadvantages such as poor movement of the heated ambient air, and higher cost. Heating occurs mostly by thermal radiation, with direct exchange between the resistors and the heated parts, but with a part serving as a barrier to the other, and with greater difficulty of heating the core loading. The details presented in this study, will simulate the process of heating by using electricity and using natural gas. In these simulations will be observed the distribution of temperature in the load and indoor over time and the rate of energy transferred to the load and also for the outside so to have a comparative processes. (author)

  19. Pyrolysis of poly(vinyl chloride) and-electric arc furnacedust mixtures.

    Science.gov (United States)

    Al-Harahsheh, Mohammad; Al-Otoom, Awni; Al-Makhadmah, Leema; Hamilton, Ian E; Kingman, Sam; Al-Asheh, Sameer; Hararah, Muhanned

    2015-12-15

    An investigation into the pyrolysis kinetics of PVC mixed with electric arc furnace dust (EAFD) was performed. Mixtures of both materials with varying PVC ratios (1:1, 1:2, 1:3) were prepared and pyrolyzed in a nitrogen atmosphere under dynamic heating conditions at different heating rates (5, 10, 30 and 50 °C/min). The pyrolysis process proceeded through two main decomposition steps; the first step involved the release of HCl which reacted with the metal oxides present in the dust, subsequently forming metal chlorides and water vapor. Benzene was also found to release as detected by TGA-MS. The remaining hydrocarbons in the polymer backbone decomposed further in the second step releasing further volatile hydrocarbons. Different models were used to fit the kinetic data namely the integral, the Van Krevelen, and Coats and Red fern methods. The presence of EAFD during PVC decomposition resulted in a considerable decrease in the activation energy of the reaction occurring during the first decomposition region. Furthermore, iron oxides were retained in the pyrolysis residue, whilst other valuable metals, including Zn and Pb, were converted to chlorides that are recoverable by leaching in water. It is believed that EAFD can be utilized as an active catalyst to produce energy gases such as propyneas evident from the TGA-MS. Copyright © 2015 Elsevier B.V. All rights reserved.

  20. A Novel Arc Fault Detector for Early Detection of Electrical Fires.

    Science.gov (United States)

    Yang, Kai; Zhang, Rencheng; Yang, Jianhong; Liu, Canhua; Chen, Shouhong; Zhang, Fujiang

    2016-04-09

    Arc faults can produce very high temperatures and can easily ignite combustible materials; thus, they represent one of the most important causes of electrical fires. The application of arc fault detection, as an emerging early fire detection technology, is required by the National Electrical Code to reduce the occurrence of electrical fires. However, the concealment, randomness and diversity of arc faults make them difficult to detect. To improve the accuracy of arc fault detection, a novel arc fault detector (AFD) is developed in this study. First, an experimental arc fault platform is built to study electrical fires. A high-frequency transducer and a current transducer are used to measure typical load signals of arc faults and normal states. After the common features of these signals are studied, high-frequency energy and current variations are extracted as an input eigenvector for use by an arc fault detection algorithm. Then, the detection algorithm based on a weighted least squares support vector machine is designed and successfully applied in a microprocessor. Finally, an AFD is developed. The test results show that the AFD can detect arc faults in a timely manner and interrupt the circuit power supply before electrical fires can occur. The AFD is not influenced by cross talk or transient processes, and the detection accuracy is very high. Hence, the AFD can be installed in low-voltage circuits to monitor circuit states in real-time to facilitate the early detection of electrical fires.

  1. A Novel Arc Fault Detector for Early Detection of Electrical Fires

    Science.gov (United States)

    Yang, Kai; Zhang, Rencheng; Yang, Jianhong; Liu, Canhua; Chen, Shouhong; Zhang, Fujiang

    2016-01-01

    Arc faults can produce very high temperatures and can easily ignite combustible materials; thus, they represent one of the most important causes of electrical fires. The application of arc fault detection, as an emerging early fire detection technology, is required by the National Electrical Code to reduce the occurrence of electrical fires. However, the concealment, randomness and diversity of arc faults make them difficult to detect. To improve the accuracy of arc fault detection, a novel arc fault detector (AFD) is developed in this study. First, an experimental arc fault platform is built to study electrical fires. A high-frequency transducer and a current transducer are used to measure typical load signals of arc faults and normal states. After the common features of these signals are studied, high-frequency energy and current variations are extracted as an input eigenvector for use by an arc fault detection algorithm. Then, the detection algorithm based on a weighted least squares support vector machine is designed and successfully applied in a microprocessor. Finally, an AFD is developed. The test results show that the AFD can detect arc faults in a timely manner and interrupt the circuit power supply before electrical fires can occur. The AFD is not influenced by cross talk or transient processes, and the detection accuracy is very high. Hence, the AFD can be installed in low-voltage circuits to monitor circuit states in real-time to facilitate the early detection of electrical fires. PMID:27070618

  2. Ferronickel Preparation from Nickeliferous Laterite by Rotary Kiln-Electric Furnace Process

    Science.gov (United States)

    Li, Guanghui; Jia, Hao; Luo, Jun; Peng, Zhiwei; Zhang, Yuanbo; Jiang, Tao

    Nickel is an important strategic metal, which is mainly used for stainless steel production. In the recent years, ferronickel has been used as a substitute for electrolytic nickel for alleviating the cost of stainless steel production. Rotary kiln-electric furnace (RKEF) smelting is currently the world-wide mainstreaming process for ferronickel production from nickeliferous laterite ore, in spite of the high power consumption. In this study, aiming to provide some meaningful guidance for ferronickel production of RKEF smelting, reductive roasting followed by smelting process was carried out. The conditions including reducing parameters (roasting temperature and time) and smelting parameters (coke dosage, CaO dosage, melting temperature and time) were ascertained. The metal recovery ratios, as well as Ni, Fe, S and P content of ferronickel were considered. The results showed that a ferronickel containing 10. 32 wt. % Ni was obtained from a laterite with 1. 85 wt. % Ni, the nickel recovery ratio was about 99%.

  3. Thermal and Arc Flash Analysis of Electric Motor Drives in Distribution Networks

    OpenAIRE

    Nikolovski, Srete; Mlakić, Dragan; Alibašić, Emir

    2017-01-01

    The paper presents thermal analysis and arc flash analysis taking care of protection relays coordination settings for electric motor drives connected to the electrical network. Power flow analysis is performed to check if there are any voltage and loading violation conditions in the system. Fault analysis is performed to check the short circuit values and compute arc flash energy dissipated at industrial busbars to eliminate damage to electrical equipment and electrical shocks and hazard to p...

  4. Proposition of a modification to the VAR process and its application in the consolidation of pressed zircaloy chips and the evaluation of the dynamical system of the electric arc

    International Nuclear Information System (INIS)

    Mucsi, Cristiano Stefano

    2005-01-01

    The objective of this work is the investigation of a new process as an alternative to the Vacuum Arc Remelting technology in the consolidation of Zircaloy chips. A procedure is proposed for the recycling of primary Zircaloy scraps by means of a modified VAR furnace. The performed studies were made in order to optimise the low cost new devices added to existing VAR furnace prototype, find ideal operational conditions, evaluate data acquisition system and the electric arc dynamical system in order to made viable the automated control of the modified VAR prototype. A funnel-crucible special device was developed and installed in a VAR prototype furnace allowing ingots to be obtained from pressed chips. This indicated the viability of creation of a new process for the consolidation of Zircaloy chips. The voltage of the electric arc during the melting runs was digitally recorded allowing the evaluation of the electric arc dynamics by using the topological invariant of the system: correlation dimension and the higher Liapunov exponent. (author)

  5. A combined arc-melting and tilt-casting furnace for the manufacture of high-purity bulk metallic glass materials.

    Science.gov (United States)

    Soinila, E; Pihlajamäki, T; Bossuyt, S; Hänninen, H

    2011-07-01

    An arc-melting furnace which includes a tilt-casting facility was designed and built, for the purpose of producing bulk metallic glass specimens. Tilt-casting was chosen because reportedly, in combination with high-purity processing, it produces the best fatigue endurance in Zr-based bulk metallic glasses. Incorporating the alloying and casting facilities in a single piece of equipment reduces the amount of laboratory space and capital investment needed. Eliminating the sample transfer step from the production process also saves time and reduces sample contamination. This is important because the glass forming ability in many alloy systems, such as Zr-based glass-forming alloys, deteriorates rapidly with increasing oxygen content of the specimen. The challenge was to create a versatile instrument, in which high purity conditions can be maintained throughout the process, even when melting alloys with high affinity for oxygen. Therefore, the design provides a high-vacuum chamber to be filled with a low-oxygen inert atmosphere, and takes special care to keep the system hermetically sealed throughout the process. In particular, movements of the arc-melting electrode and sample manipulator arm are accommodated by deformable metal bellows, rather than sliding O-ring seals, and the whole furnace is tilted for tilt-casting. This performance of the furnace is demonstrated by alloying and casting Zr(55)Cu(30)Al(10)Ni(5) directly into rods up to ø 10 mm which are verified to be amorphous by x-ray diffraction and differential scanning calorimetry, and to exhibit locally ductile fracture at liquid nitrogen temperature.

  6. 40 CFR 424.10 - Applicability; description of the open electric furnaces with wet air pollution control devices...

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 28 2010-07-01 2010-07-01 true Applicability; description of the open electric furnaces with wet air pollution control devices subcategory. 424.10 Section 424.10 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) EFFLUENT GUIDELINES AND STANDARDS FERROALLOY MANUFACTURING POINT SOURCE CATEGORY Open...

  7. Electric arc discharge damage to ion thruster grids

    Science.gov (United States)

    Beebe, D. D.; Nakanishi, S.; Finke, R. C.

    1974-01-01

    Arcs representative of those occurring between the grids of a mercury ion thruster were simulated. Parameters affecting an arc and the resulting damage were studied. The parameters investigated were arc energy, arc duration, and grid geometry. Arc attenuation techniques were also investigated. Potentially serious damage occurred at all energy levels representative of actual thruster operating conditions. Of the grids tested, the lowest open-area configuration sustained the least damage for given conditions. At a fixed energy level a long duration discharge caused greater damage than a short discharge. Attenuation of arc current using various impedances proved to be effective in reducing arc damage. Faults were also deliberately caused using chips of sputtered materials formed during the operation of an actual thruster. These faults were cleared with no serious grid damage resulting using the principles and methods developed in this study.

  8. Slag Evaluation to Reduce Energy Consumption and EAF Electrical Instability

    OpenAIRE

    Vieira,Deisi; Almeida,Rodolfo Arnaldo Montecinos de; Bielefeldt,Wagner Viana; Vilela,Antônio Cezar Faria

    2016-01-01

    In steel mills that operate with electric arc furnaces (EAF), it is interesting to ensure greater stability to the electric arc to aim at less distortion in the electrical system, with consequent reduction in electric power consumption. The slag foaming increases electric arc stability by reducing the total harmonic distortion (THD) between EAF phases. In this study, information about the chemical composition of the slag and electrical parameters of an EAF were collected. With the composition...

  9. Rocket measurements within a polar cap arc: Plasma, particle, and electric circuit parameters

    International Nuclear Information System (INIS)

    Weber, E.J.; Ballenthin, J.O.; Basu, S.; Carlson, H.C.; Hardy, D.A.; Maynard, N.C.; Smiddy, M.; Kelley, M.C.; Fleischman, J.R.; Sheehan, R.E.; Pfaff, R.F.; Rodriguez, P.

    1989-01-01

    An instrumented rocket payload was launched into a polar cap F layer aurora to investigate the energetic particle, plasma, and electric circuit parameters of a Sun-aligned arc. On-board instruments measured energetic electron flux, ion composition and density fluctuations, electron density and temperature, electron density fluctuations, and ac and dc electric fields. Real-time all-sky imaging photometer measurements of the location and motion of the aurora, were used to determine the proper geophysical situation for launch. Comparison of the in situ measurements with remote optical measurements shows that the arc was produced by fluxes of low-energy (< 1 keV) electrons. Field-aligned potentials in the arc inferred from the electron spectra had a maximum value of approximately 300 V, and from the spectral shape a parent population of preaccelerated electrons characteristic of the boundary plasma sheet or magnetosheath was inferred. Electric field components along and across the arc show sunward flow within the arc and duskward drift of the arc consistent with the drift direction and speed determined from optical imaging. Thus this arc is drifting duskward under the influence of the convection electric field. Three possible explanations for this (field-aligned currents, chemistry, and transport) are considered. Finally, ionospheric irregularity and electric field fluctuations indicate two different generation mechanisms on the dawnside and duskside of the arc. On the duskside, parameters are suggestive of an interchange process, while on the dawnside, fluctuation parameters are consistent with a velocity shear instability

  10. Electrical characteristics of TIG arcs in argon from non-equilibrium modelling and experiment

    Science.gov (United States)

    Baeva, Margarita; Uhrlandt, Dirk; Siewert, Erwan

    2016-09-01

    Electric arcs are widely used in industrial processes so that a thorough understanding of the arc characteristics is highly important to industrial research and development. TIG welding arcs operated with pointed electrodes made of tungsten, doped with cerium oxide, have been studied in order to analyze in detail the electric field and the arc voltage. Newly developed non-equilibrium model of the arc is based on a complete diffusion treatment of particle fluxes, a generalized form of Ohm's law, and boundary conditions accounting for the space-charge sheaths within the magneto-hydrodynamic approach. Experiments have been carried out for electric currents in the range 5-200 A. The electric arc has been initiated between a WC20 cathode and a water-cooled copper plate placed 0.8 mm from each other. The arc length has been continuously increased by 0.1 mm up to 15 mm and the arc voltage has been simultaneously recorded. Modelling and experimental results will be presented and discussed.

  11. Laws and ordinances on electric arc protection. Electric arc protection of electric plants; Gesetze und Verordnungen zur Stoerlichtbogensicherheit. Stoerlichtbogensicherheit von elektrischen Betriebsstaetten

    Energy Technology Data Exchange (ETDEWEB)

    Bernards, Stefan; Buenger, Stefan; Grote, Martin [Fritz Driescher KG - Spezialfabrik fuer Elektrizitaetswerksbedarf GmbH und Co., Wegberg (Germany); Boettcher, Lutz-Michael [Ingenieurbuero Boettcher-Consult, Schulzendorf (Germany); Weck, Karl-Heinz [Forschungsgemeinschaft fuer Elektrische Anlagen und Stromwirtschaft (FGH e.V.), Mannheim (Germany)

    2011-02-28

    With the publication of the new standards IEC 62271-200/VDE 0671 part 200-2003: AC metal-enclosed switchgear and controlgear for rated voltages above 1 kV and up to and including 52 kV, and IEC 62271-202/VDE 0671 part 202-2007: High voltage/low voltage prefabricated substations and their revision, the fundamentals of arc protection qualification of plants and stations were redefined with a view to personnel protection. In the case of new transformer stations, the application of these standards is state of the art. The publications and the application of the new standards for staff protection, plant protection and object protection via electric arc qualification has raised questions concerning the safety of older plants and stations, modernization, reconstruction, enhancement, maintenance, and the re-use of used stations and plants.

  12. Characteristic study of DC electric Arc plasma igniter jet

    International Nuclear Information System (INIS)

    Lan Yudan; He Liming; Du Hongliang; Wang Feng; Chen Xin

    2012-01-01

    The spectrometer was adopted to measure the emission spectrum of Ar plasma jet at the igniter exit. Boltzmann curve slope method was applied to calculate the jet electron temperature. Ionization equilibrium equation was used to calculate jet temperature and measure the laws that jet length, jet velocity, electron temperature and jet temperature of igniter exit change with arc current and inlet Ar flow rate. Whether the electron temperature could be used to replace jet temperature in aircraft plasma arc jet was also discussed. The experiment results show that arc current reduces with the rising of inlet Ar flow rate; exit jet length and velocity increase with the rising of arc current, and increase at first and then reduce with the rising of inlet Ar flow rate; exit electron temperature, electron density and jet temperature increase with the rising of arc current and reduce with the rising of inlet Ar flow rate. (authors)

  13. Determination of the characteristics of an electric arc plasma contaminated by vapors from insulators

    International Nuclear Information System (INIS)

    Abbaoui, M.; Cheminat, B.

    1991-01-01

    An experimental study at atmospheric pressure carried out on plasma penetrated by vapors from different industrial insulators allowed the showing of the influence of the nature of the insulator upon the characteristics of the electric arc plasma; i.e., an increase of the temperature, electron density, electric field, and extinction velocity of the arc. Measurements have been made spectrometrically and by means of probes

  14. Optimisation of the FeMn and ZnO production from spent pyrolised primary batteries. Feasibility of a DC-submerged arc furnace process

    Energy Technology Data Exchange (ETDEWEB)

    Sanchez-Alvarado, R.; Friedrich, B. [RWTH Aachen (Germany). IME Process Metallurgy and Metal Recycling

    2008-07-01

    In the present work the feasibility to produce a Fe-Mn-alloy and a ZnO-concentrate from spent pyrolised primary batteries has been investigated based on fundamental research, already reported in 'World of Metallurgy' - ERZ-METALL 1/2007. Through a carbothermic reduction in a Direct Current Submerged Arc Furnace process (DC-SAF) at IME Aachen, several laboratory-scale as well as semi-pilot scale tests were conducted with three different slag-compositions using solid- and hollow-electrode technique. The process was theoretically modelled with the thermochemical package FactSage 5.3.1. The effect of the process parameters temperature, slag composition and carbon addition were analysed. The results show that it is possible to recycle spent primary batteries through the submerged arc route to obtain a Fe-Mn alloy with a ratio Mn/Fe>1 and a ZnO concentrate as a separated product, reaching recycling quotes for Mn between 44 and 62%, for Fe between 56 and 96% and for zinc of more than 90%. (orig.)

  15. Application of a radiant heat transfer model to complex industrial reactive flows: combustion chambers, electric arcs; Application d`un modele de transfert radiatif a des ecoulements reactifs industriels complexes: chambres de combustion, arcs electriques

    Energy Technology Data Exchange (ETDEWEB)

    Mechitoua, N; Dalsecco, S; Delalondre, C; Simonin, O [Electricite de France (EDF), 78 - Chatou (France). Lab. National d` Hydraulique

    1997-12-31

    The direction of studies and researches (DER) of Electricite de France (EdF) has been involved for several years in a research program on turbulent reactive flows. The objectives of this program concern: the reduction of pollutant emissions from existing fossil-fueled power plants, the study of new production means (fluidized beds), and the promotion of electric power applications in the industry. An important part of this program is devoted to the development and validation of 3-D softwares and to the modeling of physical phenomena. This paper presents some industrial applications (furnaces, boilers, electric arcs) for which radiant heat transfers play an important role and the radiation models used. (J.S.) 8 refs.

  16. Application of a radiant heat transfer model to complex industrial reactive flows: combustion chambers, electric arcs; Application d`un modele de transfert radiatif a des ecoulements reactifs industriels complexes: chambres de combustion, arcs electriques

    Energy Technology Data Exchange (ETDEWEB)

    Mechitoua, N.; Dalsecco, S.; Delalondre, C.; Simonin, O. [Electricite de France (EDF), 78 - Chatou (France). Lab. National d`Hydraulique

    1996-12-31

    The direction of studies and researches (DER) of Electricite de France (EdF) has been involved for several years in a research program on turbulent reactive flows. The objectives of this program concern: the reduction of pollutant emissions from existing fossil-fueled power plants, the study of new production means (fluidized beds), and the promotion of electric power applications in the industry. An important part of this program is devoted to the development and validation of 3-D softwares and to the modeling of physical phenomena. This paper presents some industrial applications (furnaces, boilers, electric arcs) for which radiant heat transfers play an important role and the radiation models used. (J.S.) 8 refs.

  17. Heat treatment furnace

    Science.gov (United States)

    Seals, Roland D; Parrott, Jeffrey G; DeMint, Paul D; Finney, Kevin R; Blue, Charles T

    2014-10-21

    A furnace heats through both infrared radiation and convective air utilizing an infrared/purge gas design that enables improved temperature control to enable more uniform treatment of workpieces. The furnace utilizes lamps, the electrical end connections of which are located in an enclosure outside the furnace chamber, with the lamps extending into the furnace chamber through openings in the wall of the chamber. The enclosure is purged with gas, which gas flows from the enclosure into the furnace chamber via the openings in the wall of the chamber so that the gas flows above and around the lamps and is heated to form a convective mechanism in heating parts.

  18. On generalization of electric field strength in longitudinally blown arcs

    OpenAIRE

    Yas'ko, O.I.; Esipchuk, A.M.; Qing, Z.; Schram, D.C.; Fauchais, P.

    1997-01-01

    Generalization of av. elec. field strength for different discharge conditions in longitudinally blown arcs is considered. Exptl. data for distinctive devices and different gases were used for phys. modeling. Anal. showed that heat transfer processes are responsible for I-E characteristic formation. Turbulent heat transfer is the most effective for atm. pressure discharges while convection plays the main role in vacuum arcs. A generalized I-E characteristic was obtained. [on SciFinder (R)

  19. Artificial intelligence-based computer modeling tools for controlling slag foaming in electric arc furnaces

    Science.gov (United States)

    Wilson, Eric Lee

    Due to increased competition in a world economy, steel companies are currently interested in developing techniques that will allow for the improvement of the steelmaking process, either by increasing output efficiency or by improving the quality of their product, or both. Slag foaming is one practice that has been shown to contribute to both these goals. However, slag foaming is highly dynamic and difficult to model or control. This dissertation describes an effort to use artificial intelligence-based tools (genetic algorithms, fuzzy logic, and neural networks) to both model and control the slag foaming process. Specifically, a neural network is trained and tested on slag foaming data provided by a steel plant. This neural network model is then controlled by a fuzzy logic controller, which in turn is optimized by a genetic algorithm. This tuned controller is then installed at a steel plant and given control be a more efficient slag foaming controller than what was previously used by the steel plant.

  20. suitability of electric arc furnace (eaf) slag as partial replacement for ...

    African Journals Online (AJOL)

    Administrator

    investigated for use as a partial replacement for cement in sandcrete blocks. The tests ... some economic benefit and as well mitigate the negative impact of this waste on the environment. ... course of production of steel typically in the ratio.

  1. Field Measurements of Heating Efficiency of Electric Forced-Air Furnaces in Six Manufactured Homes.

    Energy Technology Data Exchange (ETDEWEB)

    Davis, Bob; Palmiter, Larry S.; Siegel, Jeff

    1994-07-26

    This report presents the results of field measurements of heating efficiency for six manufactured homes in the Pacific Northwest heated with electric forced-air systems. This is the first in a series of regional and national efforts to measure in detail the heating efficiency of manufactured homes. Only six homes were included in this study because of budgetary constraints; therefore this is not a representative sample. These investigations do provide some useful information on the heating efficiency of these homes. Useful comparisons can be drawn between these study homes and site-built heating efficiencies measured with a similar protocol. The protocol used to test these homes is very similar to another Ecotope protocol used in the study conducted in 1992 and 1993 for the Bonneville Power Administration to test the heating efficiency of 24 homes. This protocol combined real-time power measurements of furnace energy usage with energy usage during co-heat periods. Accessory data such as house and duct tightness measurements and tracer gas measurements were used to describe these homes and their heating system efficiency. Ensuring that manufactured housing is constructed in an energy and resource efficient manner is of increasing concern to manufactured home builders and consumers. No comparable work has been done to measure the heating system efficiency of MCS manufactured homes, although some co-heat tests have been performed on manufactured homes heated with natural gas to validate HUD thermal standards. It is expected that later in 1994 more research of this kind will be conducted, and perhaps a less costly and less time-consuming method for testing efficiencies will be develops.

  2. Material and energy flows in rotary kiln-electric furnace smelting of ferronickel alloy with energy saving

    International Nuclear Information System (INIS)

    Liu, Peng; Li, Baokuan; Cheung, Sherman C.P.; Wu, Wenyuan

    2016-01-01

    Highlights: • Establish the synergy relationship of material and energy in key RKEF processes. • Develop an analysis model to study energy saving with internal cycling of energy. • Analyze material and energy flow parameters and assess its associated synergy effect. • A methodology to evaluate the synergy and design indices of RKEF processes. - Abstract: An energy saving strategy with two energy saving measures has been proposed for reducing energy loss in the rotary kiln-electric furnace (RKEF) for the smelting of ferronickel alloy. One of the measures is to recover the waste heat of exhaust gas from the rotary kiln for preheating and dehydrating the wet laterite ores in the rotary dryer. Another measure is to recycle the furnace gas from the electric furnace into the rotary kiln as fuel. Based on the mass conservation and energy conservation laws, an analysis model of material and energy flows has been developed to understand the potential energy saving with the internal cycling of material and energy in the RKEF process. The analysis model not only considers the energy efficiency but also assess the synergy degree of system. Furthermore, the model also predicts the ratio of raw materials and the energy flow distribution to investigate residual heat and energy and analyze the effects of nickel content on energy flow. Finally, the evaluation methodology of synergy and the technic indices are also presented. Through the investigation of the synergy effect, the performance of the RKEF process can be evaluated and quantified for performance optimization in future.

  3. Numerical modeling of transferred arc melting bath heating; Modelisation numerique du chauffage de bains par arc transfere

    Energy Technology Data Exchange (ETDEWEB)

    Bouvier, A. [Electricite de France, 77 - Moret sur Loing (France). Direction des Etudes et Recherches; Trenty, L.; Guillot, J.B. [Ecole Centrale de Paris, Laboratoire EM2C. CNRS, 92 - Chatenay-Malabry (France); Delalondre, C. [Electricite de France (EDF), 78 - Chatou (France). Direction des Etudes et Recherches

    1997-12-31

    This paper presents the modeling of a transferred electric arc inside a bath of melted metal. After a recall of the context of the study, the problem of the modeling, which involves magnetohydrodynamic coupling inside the arc and the bath, is described. The equations that govern the phenomena inside the arc and the bath are recalled and the approach used for the modeling of the anode region of the arc is explained using a 1-D sub-model. The conditions of connection between arc and bath calculations are explained and calculation results obtained with a 200 kW laboratory furnace geometry are presented. (J.S.) 8 refs.

  4. The Influence A Crucible Arrangement On The Electrical Efficiency Of The Cold Crucible Induction Furnace

    Directory of Open Access Journals (Sweden)

    Smalcerz A.

    2015-09-01

    Full Text Available A big interest in application of cold crucible furnace (CCF for industrial, particularly metallurgical, processes has been observed in recent years. They are mainly utilised for melting of metal, glass and other materials. Analyses of processes that occur in such devices are performed; however, computer modelling is rarely applied. As a precise determination of the electromagnetic field distribution is essential for a proper analysis of processes in furnaces with cold crucibles, a complex 3D model development is necessary. In the paper, effects of a crucible design and current frequency on the efficiency of the induction furnace with cold crucible are presented. Numerical calculations were performed with the use of the Flux 3D professional software.

  5. Paired Straight Hearth Furnace - Transformational Ironmaking Process

    Energy Technology Data Exchange (ETDEWEB)

    Lu, Wei-Kao [McMaster Univ., Hamilton, ON (Canada); Debski, Paul [Andritz Metals Inc.,Canonsburg, PA (United States)

    2014-11-19

    The U. S. steel industry has reduced its energy intensity per ton of steel shipped by 33% since 1990. However, further significant gains in energy efficiency will require the development of new, transformational iron and steelmaking processes. The Paired Straight Hearth Furnace (PSH) process is an emerging alternative high productivity, direct reduced iron (DRI) technology that may achieve very low fuel rates and has the potential to replace blast furnace ironmaking. The PSH furnace can operate independently or may be coupled with other melting technologies to produce liquid hot metal that is both similar to blast furnace iron and suitable as a feedstock for basic oxygen steelmaking furnaces. The PSH process uses non-metallurgical coal as a reductant to convert iron oxides such as iron ore and steelmaking by-product oxides to DRI pellets. In this process, a multi-layer, nominally 120mm tall bed of composite “green balls” made from oxide, coal and binder is built up and contained within a moving refractory hearth. The pellet bed absorbs radiant heat energy during exposure to the high temperature interior refractory surfaces of the PSH while generating a strongly reducing gas atmosphere in the bed that yields a highly metalized DRI product. The PSH concept has been well tested in static hearth experiments. A moving bed design is being developed. The process developers believe that if successful, the PSH process has the potential to replace blast furnaces and coke ovens at a fraction of the operating and capital cost while using about 30% less energy relative to current blast furnace technology. DRI output could also feed electric arc furnaces (EAFs) by displacing a portion of the scrap charge.

  6. Displacement of an electric arc by a stationary transverse magnetic field to different pressures of the ionized gas

    International Nuclear Information System (INIS)

    Ramos, J.

    1987-01-01

    The displacement of a wall-stabilized electric arc by a stationary transverse magnetic field is measured to different pressures of the ionized gas. The increase of the pressure makes the heat transfer function and the mass flow velocity in the arc column to raise, and it makes the arc displacement to decrease. (author)

  7. Improved Casting Furnace Conceptual Design

    Energy Technology Data Exchange (ETDEWEB)

    Fielding, Randall Sidney [Idaho National Lab. (INL), Idaho Falls, ID (United States); Tolman, David Donald [Idaho National Lab. (INL), Idaho Falls, ID (United States)

    2017-02-01

    In an attempt to ensure more consistent casting results and remove some schedule variance associated with casting, an improved casting furnace concept has been developed. The improved furnace uses the existing arc melter hardware and glovebox utilities. The furnace concept was designed around physical and operational requirements such as; a charge sized of less than 30 grams, high heating rates and minimal additional footprint. The conceptual model is shown in the report as well as a summary of how the requirements were met.

  8. Novel non-equilibrium modelling of a DC electric arc in argon

    Science.gov (United States)

    Baeva, M.; Benilov, M. S.; Almeida, N. A.; Uhrlandt, D.

    2016-06-01

    A novel non-equilibrium model has been developed to describe the interplay of heat and mass transfer and electric and magnetic fields in a DC electric arc. A complete diffusion treatment of particle fluxes, a generalized form of Ohm’s law, and numerical matching of the arc plasma with the space-charge sheaths adjacent to the electrodes are applied to analyze in detail the plasma parameters and the phenomena occurring in the plasma column and the near-electrode regions of a DC arc generated in atmospheric pressure argon for current levels from 20 A up to 200 A. Results comprising electric field and potential, current density, heating of the electrodes, and effects of thermal and chemical non-equilibrium are presented and discussed. The current-voltage characteristic obtained is in fair agreement with known experimental data. It indicates a minimum for arc current of about 80 A. For all current levels, a field reversal in front of the anode accompanied by a voltage drop of (0.7-2.6) V is observed. Another field reversal is observed near the cathode for arc currents below 80 A.

  9. Novel non-equilibrium modelling of a DC electric arc in argon

    International Nuclear Information System (INIS)

    Baeva, M; Uhrlandt, D; Benilov, M S; Almeida, N A

    2016-01-01

    A novel non-equilibrium model has been developed to describe the interplay of heat and mass transfer and electric and magnetic fields in a DC electric arc. A complete diffusion treatment of particle fluxes, a generalized form of Ohm’s law, and numerical matching of the arc plasma with the space-charge sheaths adjacent to the electrodes are applied to analyze in detail the plasma parameters and the phenomena occurring in the plasma column and the near-electrode regions of a DC arc generated in atmospheric pressure argon for current levels from 20 A up to 200 A. Results comprising electric field and potential, current density, heating of the electrodes, and effects of thermal and chemical non-equilibrium are presented and discussed. The current–voltage characteristic obtained is in fair agreement with known experimental data. It indicates a minimum for arc current of about 80 A. For all current levels, a field reversal in front of the anode accompanied by a voltage drop of (0.7–2.6) V is observed. Another field reversal is observed near the cathode for arc currents below 80 A. (paper)

  10. Proposition of a modification to the VAR process and its application in the consolidation of pressed zircaloy chips and the evaluation of the dynamical system of the electric arc; Proposicao de um processo alternativo a fusao via forno VAR para a consolidacao de cavacos prensados de zircaloy e estudo do sistema dinamico do arco eletrico

    Energy Technology Data Exchange (ETDEWEB)

    Mucsi, Cristiano Stefano

    2005-07-01

    The objective of this work is the investigation of a new process as an alternative to the Vacuum Arc Remelting technology in the consolidation of Zircaloy chips. A procedure is proposed for the recycling of primary Zircaloy scraps by means of a modified VAR furnace. The performed studies were made in order to optimise the low cost new devices added to existing VAR furnace prototype, find ideal operational conditions, evaluate data acquisition system and the electric arc dynamical system in order to made viable the automated control of the modified VAR prototype. A funnel-crucible special device was developed and installed in a VAR prototype furnace allowing ingots to be obtained from pressed chips. This indicated the viability of creation of a new process for the consolidation of Zircaloy chips. The voltage of the electric arc during the melting runs was digitally recorded allowing the evaluation of the electric arc dynamics by using the topological invariant of the system: correlation dimension and the higher Liapunov exponent. (author)

  11. Direct electrical arc ignition of hybrid rocket motors

    Science.gov (United States)

    Judson, Michael I., Jr.

    Hybrid rockets motors provide distinct safety advantages when compared to traditional liquid or solid propellant systems, due to the inherent stability and relative inertness of the propellants prior to established combustion. As a result of this inherent propellant stability, hybrid motors have historically proven difficult to ignite. State of the art hybrid igniter designs continue to require solid or liquid reactants distinct from the main propellants. These ignition methods however, reintroduce to the hybrid propulsion system the safety and complexity disadvantages associated with traditional liquid or solid propellants. The results of this study demonstrate the feasibility of a novel direct electrostatic arc ignition method for hybrid motors. A series of small prototype stand-alone thrusters demonstrating this technology were successfully designed and tested using Acrylonitrile Butadiene Styrene (ABS) plastic and Gaseous Oxygen (GOX) as propellants. Measurements of input voltage and current demonstrated that arc-ignition will occur using as little as 10 watts peak power and less than 5 joules total energy. The motor developed for the stand-alone small thruster was adapted as a gas generator to ignite a medium-scale hybrid rocket motor using nitrous oxide /and HTPB as propellants. Multiple consecutive ignitions were performed. A large data set as well as a collection of development `lessons learned' were compiled to guide future development and research. Since the completion of this original groundwork research, the concept has been developed into a reliable, operational igniter system for a 75mm hybrid motor using both gaseous oxygen and liquid nitrous oxide as oxidizers. A development map of the direct spark ignition concept is presented showing the flow of key lessons learned between this original work and later follow on development.

  12. Effect of γ-irradiation on the electrical conductivity of some soda lime silicate glass containing blast furnace slag

    International Nuclear Information System (INIS)

    Elalaily, N.A.; Khalil, Magda M.I.; Ahmed, L.S.

    2007-01-01

    The effect of electric field strength on conduction in soda lime silicate glass doped with blast furnace slag with different concentration was studied and the value of jump distance was calculated. The structure and the mixed anion effect in the conductivity have been examined by measuring the electrical conductivity of glass samples at temperature ranging between 20 and 250 deg. C. The results showed that the electrical conductivity of the examined glasses are divided into three ranges depending on the temperature range. The first is from room temperature to about 49.5 deg. C, the second is at a temperature range of 60.3-104 deg. C where the glass shows a decrease in its conductivity with the increase in temperature. This was followed by another increase in the electrical conductivity with the increase in temperature. The results also showed that the glass becomes more insulating as the slag content increased. The effect of irradiation was also studied by exposing glass samples to two different irradiation doses. It can be noticed that irradiation causes an increase in the electrical conductivity, especially at high temperature. The results were discussed and correlated according to the molecular structure of the prepared glass

  13. Electrical and spectroscopic diagnostic of an atmospheric double arc argon plasma jet

    International Nuclear Information System (INIS)

    Tu, X; Cheron, B G; Yan, J H; Cen, K F

    2007-01-01

    An atmospheric argon plasma jet generated by an original dc double anode plasma torch has been investigated through its electrical and spectroscopic diagnostics. The arc instabilities and dynamic behavior of the argon plasma are analyzed using classical tools such as the statistical method, fast Fourier transform (FFT) and correlation function. The takeover mode is identified as the fluctuation characteristic of the double arc argon plasma jet in our experiment. The FFT and correlation analysis of electrical signals exhibit the only characteristic frequency of 150 Hz, which originates from the torch power and is independent of any change in the operating parameters. No high frequency fluctuations (1-15 kHz) are observed. This indicates that the nature of fluctuations in an argon plasma jet is induced mainly by the undulation of the tri-phase rectified power supply. It is found that each arc root attachment is diffused rather than located at a fixed position on the anode wall. Moreover, the emission spectroscopic technique is performed to determine the electron temperature and number density of the plasma jet inside and outside the arc chamber. Along the torch axis, the measured electron temperature and number density of the double arc argon plasma drop from 12 300 K and 7.6 x 10 22 m -3 at the divergent part of the first anode nozzle, to 10 500 K and 3.1 x 10 22 m -3 at the torch exit. In addition, the validity criteria of the local thermodynamic equilibrium (LTE) state in the plasma arc are examined. The results show that the measured electron densities are in good agreement with those calculated from the LTE model, which indicates that the double arc argon plasma at atmospheric pressure is close to the LTE state under our experimental conditions

  14. Influence of Addition of Briquettes with Dust Content into the Charge of Electric Induction Furnace on Cast Iron Quality

    Directory of Open Access Journals (Sweden)

    Pribulová A.

    2012-09-01

    Full Text Available Foundry dust from blasting and grinding of castings contain a high amount of iron, ergo it is possible its recycling in foundry process. Dust was compacted by briquetting, two kinds of briquettes were prepared (A contained 95% magnetic part of dust from casting blasting +5% bentonite and B contained 95% mixture of dust from casting grinding and magnetic part of dust from casting blasting + 5% bentonite and used as a part of charge into the electric induction furnace. It was found that addition of briquettes has had an influence of a chemical composition of cast iron above all on content of sulphur, phosphorus and silicon. It was not reflected in decrease in tensile strength and in microstructure. Yield of metal from briquettes was not lower then 70%.

  15. Influence of Addition of Briquettes with Dust Content into the Charge of Electric Induction Furnace on Cast Iron Quality

    Directory of Open Access Journals (Sweden)

    A. Pribulová

    2012-09-01

    Full Text Available Foundry dust from blasting and grinding of castings contain a high amount of iron, ergo it is possible its recycling in foundry process.Dust was compacted by briquetting, two kinds of briquettes were prepared (A contained 95% magnetic part of dust from casting blasting+5% bentonite and B contained 95% mixture of dust from casting grinding and magnetic part of dust from casting blasting + 5%bentonite and used as a part of charge into the electric induction furnace. It was found that addition of briquettes has had an influence of a chemical composition of cast iron above all on content of sulphur, phosphorus and silicon. It was not reflected in decrease in tensile strength and in microstructure. Yield of metal from briquettes was not lower then 70%.

  16. Furnace testing of electrical and pipe-penetration seals based on foamed silicone elastomer: 60, 90, and 120-minute fire ratings

    International Nuclear Information System (INIS)

    Brown, A.

    1979-03-01

    Fire tests of foamed silicone seals for electrical and pipe penetrations have been performed using a furnace with temperature control as heat source. The tests were performed in principle in accordance with the requirements of NORDTEST 5A (ISO 834). The purpose of the tests was to obtain appropriate fire ratings for different seal thicknesses. The report covers. - Description of material used to prepare the seals and method of application - Description of furnace test assembly and method of performing test - Listing of penetrating elements and of the thermocouple array used to measure temperature - Curves of thermocouple readouts and photographs of seals during and after completion of the test. (author)

  17. Computer Modeling of Radiative Transfer in Hybrid-Stabilized Argon–Water Electric Arc

    Czech Academy of Sciences Publication Activity Database

    Jeništa, Jiří; Takana, H.; Nishiyama, H.; Křenek, Petr; Bartlová, M.; Aubrecht, V.

    2011-01-01

    Roč. 39, č. 11 (2011), s. 2892-2893 ISSN 0093-3813 Institutional research plan: CEZ:AV0Z20430508 Keywords : Divergence of radiation flux * hybrid-stabilized electric arc * mass flow rate * partial characteristics * radiation flux Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 1.174, year: 2011 http://ieeexplore.ieee.org/xpl/RecentIssue.jsp?punumber=27

  18. High-tension electrical-arc-induced thermal burns caused by railway overhead cables.

    Science.gov (United States)

    Koller, J

    1991-10-01

    Eleven patients with high-tension electrical-arc-induced thermal burns due to railway overhead cables were treated at the Bratislava Burn Department during a relatively short period of 18 months. All the injuries occurred by the same mechanism, that is persons climbing on top of railway carriages and approaching the 25,000 V a.c. overhead cables. All the burns were the result of an electrical arc passing externally to the body, with subsequent ignition of the victim's clothes. The cutaneous burns, ranging from 24 to 79 per cent of the BSA, were mostly deep partial to full skin thickness injuries. One patient died on day 5 postburn, the other survived. In spite of high-tension aetiology, no true electrical injuries appear to have occurred and no amputations were necessary. The pathophysiology and possible preventive measures are discussed. It must be stressed that arcing can be induced by an earthed object approaching, but not touching, a cable carrying a high voltage.

  19. Electric fields and currents observed by S3-2 in the vicinity of discrete arcs

    International Nuclear Information System (INIS)

    Burke, W.J.

    1984-01-01

    The high time resolution of the electric and magnetic field detectors on the polar orbiting satellite S3-2 made it possible to examine the details of auroral events down to discrete-arc scales. Depending on the instantaneous look direction of an electron detector, information about field-aligned accelerations above the satellite could also be obtained. Case studies of four arc events, three in the auroral oval and one in the polar cap, have been completed. Field-aligned currents associated with arcs in the auroral oval appeared as matched pairs of oppositely directed current sheets. Magnetic deflections, almost exclusively in the east-west direction departed from and returned to baselines established by the large-scale Region 1/Region 2 currents. The upward currents had intensities of up to 145 microamperes/sq m and were carried by electrons that were accelerated through field aligned potential drops. The relationship between the field-aligned current density and potential drop is not inconsistent with predictions of a laminar flow model. The most intense return (downward) currents were in the 10 to 15 microamperes/sq m range. At satellite altitudes near 1000 km, these currents approximate the critical limit for current driven, ion cyclotron instabilities. The arc in the polar cap was sun-aligned and was found in a region of intense convective shear, with the electric field pointing toward the center of the arc. The field-aligned currents consisted of three sheets two with currents flowing into and one out of the ionosphere. The upward current was carried by polar-rain electrons that had undergone a field-aligned acceleration of approximately 1 kV. 19 references

  20. The influence of Ac parameters in the process of micro-arc oxidation film electric breakdown

    Directory of Open Access Journals (Sweden)

    Ma Jin

    2016-01-01

    Full Text Available This paper studies the electric breakdown discharge process of micro-arc oxidation film on the surface of aluminum alloy. Based on the analysis of the AC parameters variation in the micro-arc oxidation process, the following conclusions can be drawn: The growth of oxide film can be divided into three stages, and Oxide film breakdown discharge occurs twice in the micro-arc oxidation process. The first stage is the formation and disruptive discharge of amorphous oxide film, producing the ceramic oxide granules, which belong to solid dielectric breakdown. In this stage the membrane voltage of the oxide film plays a key role; the second stage is the formation of ceramic oxide film, the ceramic oxide granules turns into porous structure oxide film in this stage; the third stage is the growth of ceramic oxide film, the gas film that forms in the oxide film’s porous structure is electric broken-down, which is the second breakdown discharge process, the current density on the oxide film surface could affect the breakdown process significantly.

  1. Combined Experimental and Numerical Investigation of Electric-Arc Airspikes For Blunt Body at Mach 3

    Science.gov (United States)

    Misiewicz, C.; Myrabo, L. N.; Shneider, M. N.; Raizer, Y. P.

    2005-04-01

    Electric-arc airspike experiments were performed with a 1.25-inch diameter blunt body in the vacuum-driven Mach 3 wind tunnel at Rensselaer Polytechnic Institute. Schlieren movies at 30-Hz frame rate were recorded of the airspike flowfields, revealing substantial evolution over the 6-second run durations. Arc powers up to 2-kW were delivered into the airspike by an arc-welding power supply, using zirconiated tungsten electrodes. Aerodynamic drag was measured with a piezo-electric load cell, revealing reductions up to 70% when the airspike was energized. The test article was a small-scale model of the Mercury lightcraft, a laser-propelled transatmospheric vehicle designed to transport one-person into orbit. Numerical modeling of this airspike is based on the Euler gasdynamic equations for conditions identical to those tested in the RPI supersonic tunnel. Excellent agreement between the shock wave shapes given by first-order asymptotic theory, numerical modeling, and experiment is demonstrated. Results of the numerical modeling confirm both the significant drag reduction potential and the energy efficiency of the airspike concept.

  2. Rocket measurements within a polar cap arc - Plasma, particle, and electric circuit parameters

    Science.gov (United States)

    Weber, E. J.; Ballenthin, J. O.; Basu, S.; Carlson, H. C.; Hardy, D. A.; Maynard, N. C.; Kelley, M. C.; Fleischman, J. R.; Pfaff, R. F.

    1989-01-01

    Results are presented from the Polar Ionospheric Irregularities Experiment (PIIE), conducted from Sondrestrom, Greenland, on March 15, 1985, designed for an investigation of processes which lead to the generation of small-scale (less than 1 km) ionospheric irregularities within polar-cap F-layer auroras. An instrumented rocket was launched into a polar cap F layer aurora to measure energetic electron flux, plasma, and electric circuit parameters of a sun-aligned arc, coordinated with simultaneous measurements from the Sondrestrom incoherent scatter radar and the AFGL Airborne Ionospheric Observatory. Results indicated the existence of two different generation mechanisms on the dawnside and duskside of the arc. On the duskside, parameters are suggestive of an interchange process, while on the dawnside, fluctuation parameters are consistent with a velocity shear instability.

  3. Highly stable carbon nanotube field emitters on small metal tips against electrical arcing for miniature X-ray tubes

    International Nuclear Information System (INIS)

    Ha, Jun Mok; Kim, Hyun Jin; Kim, Hyun Nam; Raza, Hamid Saeed; Cho, Sung Oh

    2015-01-01

    If CNT emitters are operated at a high voltage or at a high electric field, electrical arcing (or vacuum breakdown) can occur. Arcing can be initiated by the removed CNTs, impurities on the CNTs or substrates, protrusion of CNTs, low operating vacuum, and a very high electric field. Since arcing is accompanied with a very high current flow and it can produce plasma channel near the emitter, CNTs are seriously damaged or sometimes CNTs are almost completely removed from the substrate by the arcing events. Detachment of CNTs from a substrate is an irreversible catastrophic phenomenon for a device operation. In addition to the detachment of CNTs, arcing induces a sudden voltage drop and thus device operation is stopped. The metal mixture strongly attached CNTs to the tip substrate. Due to the strong adhesion, CNT emitters could be pre-treated with electrical conditioning process without seriously damaging the CNTs even though many intense arcing events were induced at the small and sharp geometry of the tip substrate. Impurities that were loosely bound to the substrates were almost removed and CNTs heights became uniform after the electrical conditioning process

  4. Numerical simulation for arc-plasma dynamics during contact opening process in electrical circuit-breakers

    International Nuclear Information System (INIS)

    Gupta, D N; Srinivas, D; Patil, G N; Kale, S S; Potnis, S B

    2010-01-01

    The high-energy, high-current thermal plasma that develops between electric contacts in a gas circuit-breaker during circuit interruption is an important phenomenon in the power transmission industry. The high temperature and pressure arc dissipates the tremendous amount of energy generated by the fault current. Simultaneously, this energy has to be transferred away from the contacts to build the dielectric strength level of the circuit-breaker. In order to interrupt the current, the arc must be weakened and finally extinguished. We model these phenomena by using a computer software code based on the solution of the unsteady Euler equations of gas dynamics. We consider the equations of fluid flows. These equations are solved numerically in complex circuit breaker geometries using a finite-volume method. The domain is initially filled with SF 6 gas. We begin our simulations from cold mode, where the fault current is not present (hence no arc). An axis-symmetric geometry of a 145 kV gas circuit-breaker is considered to study the pressure, density, and temperature profile during contact opening process.

  5. Potential oxidative stress in the bodies of electric arc welding operators: effect of photochemical smog.

    Science.gov (United States)

    Zhu, You-Gen; Zhou, Jun-Fu; Shan, Wei-Ying; Zhou, Pei-Su; Tong, Gui-Zhong

    2004-12-01

    To investigate whether photochemical smog emitted during the process of electric arc welding might cause oxidative stress and potential oxidative damage in the bodies of welding operators. Seventy electric arc welding operators (WOs) and 70 healthy volunteers (HVs) were enrolled in a randomized controlled study design, in which the levels of vitamin C (VC) and vitamin E (VE) in plasma as well as the activities of superoxide dismutase (SOD), catalase (CAT) and glutathione peroxidase (GPX), and the level of lipoperoxide (LPO) in erythrocytes were determined by spectrophotometry. Compared with the average values of the above experimental parameters in the HVs group, the average values of VC and VE in plasma as well as those of SOD, CAT and GPX in erythrocytes in the WOs group were significantly decreased (P smog the values of VC, VE, SOD, and GPX, except for CAT, in the WOs were decreased gradually (P smog in the bodies of WOs, thereby causing potential oxidative and lipoperoxidative damages in their bodies.

  6. Growth of carbon nanotubes in arc plasma treated graphite disc: microstructural characterization and electrical conductivity study

    Science.gov (United States)

    Nayak, B. B.; Sahu, R. K.; Dash, T.; Pradhan, S.

    2018-03-01

    Circular graphite discs were treated in arc plasma by varying arcing time. Analysis of the plasma treated discs by field emission scanning electron microscope revealed globular grain morphologies on the surfaces, but when the same were observed at higher magnification and higher resolution under transmission electron microscope, growth of multiwall carbon nanotubes of around 2 nm diameter was clearly seen. In situ growth of carbon nanotube bundles/bunches consisting of around 0.7 nm tube diameter was marked in the case of 6 min treated disc surface. Both the untreated and the plasma treated graphite discs were characterized by X-ray diffraction, energy dispersive spectra of X-ray, X-ray photoelectron spectroscopy, transmission electron microscopy, micro Raman spectroscopy and BET surface area measurement. From Raman spectra, BET surface area and microstructure observed in transmission electron microscope, growth of several layers of graphene was identified. Four-point probe measurements for electrical resistivity/conductivity of the graphite discs treated under different plasma conditions showed significant increase in conductivity values over that of untreated graphite conductivity value and the best result, i.e., around eightfold increase in conductivity, was observed in the case of 6 min plasma treated sample exhibiting carbon nanotube bundles/bunches grown on disc surface. By comparing the microstructures of the untreated and plasma treated graphite discs, the electrical conductivity increase in graphite disc is attributed to carbon nanotubes (including bundles/bunches) growth on disc surface by plasma treatment.

  7. An Alternative Cu-Based Bond Layer for Electric Arc Coating Process

    Science.gov (United States)

    Fadragas, Carlos R.; Morales, E. V.; Muñoz, J. A.; Bott, I. S.; Lariot Sánchez, C. A.

    2011-12-01

    A Cu-Al alloy has been used as bond coat between a carbon steel substrate and a final coating deposit obtained by applying the twin wire electric arc spraying coating technique. The presence of a copper-based material in the composite system can change the overall temperature profile during deposition because copper exhibits a thermal conductivity several times higher than that of the normally recommended bond coat materials (such as nickel-aluminum alloys or nickel-chromium alloys). The microstructures of 420 and 304 stainless steels deposited by the electric arc spray process have been investigated, focusing attention on the deposit homogeneity, porosity, lamellar structure, and microhardness. The nature of the local temperature gradient during deposition can strongly influence the formation of the final coating deposit. This study presents a preliminary study, undertaken to investigate the changes in the temperature profile which occur when a Cu-Al alloy is used as bond coat, and the possible consequences of these changes on the microstructure and adhesion of the final coating deposit. The influence of the thickness of the bond layer on the top coating temperature has also been also evaluated.

  8. Deposition of titanium nitride layers by electric arc – Reactive plasma spraying method

    International Nuclear Information System (INIS)

    Şerban, Viorel-Aurel; Roşu, Radu Alexandru; Bucur, Alexandra Ioana; Pascu, Doru Romulus

    2013-01-01

    Highlights: ► Titanium nitride layers deposited by electric arc – reactive plasma spraying method. ► Deposition of titanium nitride layers on C45 steel at different spraying distances. ► Characterization of the coatings hardness as function of the spraying distances. ► Determination of the corrosion behavior of titanium nitride layers obtained. - Abstract: Titanium nitride (TiN) is a ceramic material which possesses high mechanical properties, being often used in order to cover cutting tools, thus increasing their lifetime, and also for covering components which are working in corrosive environments. The paper presents the experimental results on deposition of titanium nitride coatings by a new combined method (reactive plasma spraying and electric arc thermal spraying). In this way the advantages of each method in part are combined, obtaining improved quality coatings in the same time achieving high productivity. Commercially pure titanium wire and C45 steel as substrate were used for experiments. X-ray diffraction analysis shows that the deposited coatings are composed of titanium nitride (TiN, Ti 2 N) and small amounts of Ti 3 O. The microstructure of the deposited layers, investigated both by optical and scanning electron microscopy, shows that the coatings are dense, compact, without cracks and with low porosity. Vickers microhardness of the coatings presents maximum values of 912 HV0.1. The corrosion tests in 3%NaCl solution show that the deposited layers have a high corrosion resistance compared to unalloyed steel substrate.

  9. Simulation of the thermal behaviour of electric industrial resistance furnaces using the I-DEAS/TMG code; Simulation du comportement thermique des fours electriques industriels a resistances a l`aide du code I-DEAS/TMG

    Energy Technology Data Exchange (ETDEWEB)

    Plard, Ch; Branchu, K; Le Cloirec, B [Electricite de France, 77 - Moret sur Loing (France). Direction des Etudes et Recherches

    1997-12-31

    In order to answer the modeling needs of manufacturers and users of electrical resistance furnaces, Electricite de France (EdF) has been appealed to search for a numerical simulation tool for the modeling of thermal phenomena and to carry out its qualification. The TNG software has been retained according to its modeling characteristics of radiant heat transfers and to the coupling with thermal conduction. After a description of the main characteristics of this code, two examples of application to electrical furnaces are presented. The first example illustrates how it can be possible to accurately reproduce the behaviour of a big industrial furnace. The second example is an illustration of numerical simulation possibilities for the optimization of processes performed with an electric furnace. (J.S.)

  10. Simulation of the thermal behaviour of electric industrial resistance furnaces using the I-DEAS/TMG code; Simulation du comportement thermique des fours electriques industriels a resistances a l`aide du code I-DEAS/TMG

    Energy Technology Data Exchange (ETDEWEB)

    Plard, Ch.; Branchu, K.; Le Cloirec, B. [Electricite de France, 77 - Moret sur Loing (France). Direction des Etudes et Recherches

    1996-12-31

    In order to answer the modeling needs of manufacturers and users of electrical resistance furnaces, Electricite de France (EdF) has been appealed to search for a numerical simulation tool for the modeling of thermal phenomena and to carry out its qualification. The TNG software has been retained according to its modeling characteristics of radiant heat transfers and to the coupling with thermal conduction. After a description of the main characteristics of this code, two examples of application to electrical furnaces are presented. The first example illustrates how it can be possible to accurately reproduce the behaviour of a big industrial furnace. The second example is an illustration of numerical simulation possibilities for the optimization of processes performed with an electric furnace. (J.S.)

  11. PREFACE: 1st International Symposium on Electrical Arc and Thermal Plasmas in Africa (ISAPA)

    Science.gov (United States)

    Andre, Pascal; Koalaga, Zacharie

    2012-02-01

    Logos of the University of Ouagadougou, ISAPA and Universite Blaise Pascal Africa (especially Sub-Saharan Africa) is a continent where electrification is at a low level. However, the development of the electrical power sector is a prerequisite for the growth of other industrial activities, that is to say for the social and economic development of African countries. Consequently, a large number of electrification projects (rural electrification, interconnection of different country's grids) takes place in many countries. These projects need expertise and make Africa a continent of opportunity for companies in different domains for business and research: energy; energetic production, transmission, distribution and protection of electricity; the supply of cable; the construction, engineering and expertise in the field of solar and wind power. The first International Symposium on electrical Arc and thermal Plasma in Africa (ISAPA) was held for the first time in Ouagadougou, Burkina Faso to progress and develop the research of new physical developments, technical breakthroughs, and ideas in the fields of electrical production and electrical applications. The ISAPA aims to encourage the advancement of the science and applications of electrical power transformation in Africa by bringing together specialists from many areas in Africa and the rest of the world. Such considerations have led us to define a Scientific Committee including representatives from many countries. This first meeting was an innovative opportunity for researchers and engineers from academic and industrial sectors to exchange views and knowledge. Both fundamental aspects such as thermal plasma, electrical arc, diagnostics and applied aspects as circuit breakers, ICP analyses, photovoltaic energy conversion and alternative energies, as well as space applications were covered. The Laboratory of Material and Environment (LAME) from Ouagadougou University and the Laboratory of Electric Arc and Thermal

  12. 40 CFR 63.10686 - What are the requirements for electric arc furnaces and argon-oxygen decarburization vessels?

    Science.gov (United States)

    2010-07-01

    ... shop and, due solely to the operations of any affected EAF(s) or AOD vessel(s), exhibit 6 percent... with a PM limit of 0.0052 grains per dry standard cubic foot (gr/dscf); and (2) Exit from a melt shop...) Method 2, 2A, 2C, 2D, 2F, or 2G of appendix A-1 of 40 CFR part 60 to determine the volumetric flow rate...

  13. The mechanisms and models of interaction between electrical arc and contact materials

    International Nuclear Information System (INIS)

    Kharin, S.N.

    1999-01-01

    Mechanisms of arc erosion in electrical contacts are different and depends on the conditions of contact separation. The first one, which occurs at low current with relatively slow rate of heat transfer, involves the evaporation of material from the contact surface. The second mechanism can be characterized by the formation of droplets of molten metal caused by high currents and vapor or magnetic pressure on a molten metal pool. However, in certain cases it is impossible to explain the formation of molten metal droplets in terms of pressure only. Therefore a new hypothesis regarding thermo-capillary mechanism of ejection of liquid metal is discussed. This hypothesis is based on the Marangoni effect which is important when the temperature gradient along the liquid contact zone and the temperature dependence of surface tension become significant (tungsten, zirconium, molybdenum etc.). The fourth erosion mechanism is associated with the ejection of solid particles of contact material with distinct crystalline structure during high current pulses of a short duration. It occurs when thermo-elastic processes overcome the mechanical strength. A mathematical model describing each of the four mechanisms of erosion is presented. Temperature fields and erosion characteristics are determined as a function of the commutation regime and the properties of contact materials. The experimental data are discussed in terms of theoretical approach with respect to the solid phase and droplet formation. Dynamics of each type of arc erosion is described, and recommendations for optimal selection of contact material with minimum erosion are given. (author)

  14. BPM Motors in Residential Gas Furnaces: What are the Savings?

    OpenAIRE

    Lutz, James; Franco, Victor; Lekov, Alex; Wong-Parodi, Gabrielle

    2006-01-01

    Residential gas furnaces contain blowers to distribute warm air. Currently, furnace blowers use either a Permanent Split Capacitor (PSC) or a Brushless Permanent Magnet (BPM) motor. Blowers account for the majority of furnace electricity consumption. Therefore, accurate determination of the blower electricity consumption is important for understanding electricity consumption of furnaces. The electricity consumption of blower motors depends on the static pressure across the blower. This p...

  15. Electric field induced needle-pulsed arc discharge carbon nanotube production apparatus: Circuitry and mechanical design

    Energy Technology Data Exchange (ETDEWEB)

    Kia, Kaveh Kazemi [Department of Electrical and Computer Engineering, Islamic Azad University of Bonab, Bonab (Iran, Islamic Republic of); Bonabi, Fahimeh [Department of Engineering, Islamic Azad University of Bonab, Bonab (Iran, Islamic Republic of)

    2012-12-15

    A simple and low cost apparatus is reported to produce multiwall carbon nanotubes and carbon nano-onions by a low power short pulsed arc discharge reactor. The electric circuitry and the mechanical design details and a micro-filtering assembly are described. The pulsed-plasma is generated and applied between two graphite electrodes. The pulse width is 0.3 {mu}s. A strong dc electric field is established along side the electrodes. The repetitive discharges occur in less than 1 mm distance between a sharp tip graphite rod as anode, and a tubular graphite as cathode. A hydrocarbon vapor, as carbon source, is introduced through the graphite nozzle in the cathode assembly. The pressure of the chamber is controlled by a vacuum pump. A magnetic field, perpendicular to the plasma path, is provided. The results show that the synergetic use of a pulsed-current and a dc power supply enables us to synthesize carbon nanoparticles with short pulsed plasma. The simplicity and inexpensiveness of this plan is noticeable. Pulsed nature of plasma provides some extra degrees of freedom that make the production more controllable. Effects of some design parameters such as electric field, pulse frequency, and cathode shape are discussed. The products are examined using scanning probe microscopy techniques.

  16. Electric field induced needle-pulsed arc discharge carbon nanotube production apparatus: circuitry and mechanical design.

    Science.gov (United States)

    Kia, Kaveh Kazemi; Bonabi, Fahimeh

    2012-12-01

    A simple and low cost apparatus is reported to produce multiwall carbon nanotubes and carbon nano-onions by a low power short pulsed arc discharge reactor. The electric circuitry and the mechanical design details and a micro-filtering assembly are described. The pulsed-plasma is generated and applied between two graphite electrodes. The pulse width is 0.3 μs. A strong dc electric field is established along side the electrodes. The repetitive discharges occur in less than 1 mm distance between a sharp tip graphite rod as anode, and a tubular graphite as cathode. A hydrocarbon vapor, as carbon source, is introduced through the graphite nozzle in the cathode assembly. The pressure of the chamber is controlled by a vacuum pump. A magnetic field, perpendicular to the plasma path, is provided. The results show that the synergetic use of a pulsed-current and a dc power supply enables us to synthesize carbon nanoparticles with short pulsed plasma. The simplicity and inexpensiveness of this plan is noticeable. Pulsed nature of plasma provides some extra degrees of freedom that make the production more controllable. Effects of some design parameters such as electric field, pulse frequency, and cathode shape are discussed. The products are examined using scanning probe microscopy techniques.

  17. An experimental study on the thermal characteristics and heating effect of arc-fault from Cu core in residential electrical wiring fires.

    Science.gov (United States)

    Du, Jian-Hua; Tu, Ran; Zeng, Yi; Pan, Leng; Zhang, Ren-Cheng

    2017-01-01

    The characteristics of a series direct current (DC) arc-fault including both electrical and thermal parameters were investigated based on an arc-fault simulator to provide references for multi-parameter electrical fire detection method. Tests on arc fault behavior with three different initial circuit voltages, resistances and arc gaps were conducted, respectively. The influences of circuit conditions on arc dynamic image, voltage, current or power were interpreted. Also, the temperature rises of electrode surface and ambient air were studied. The results showed that, first, significant variations of arc structure and light emitting were observed under different conditions. A thin outer burning layer of vapor generated from electrodes with orange light was found due to the extremely high arc temperature. Second, with the increasing electrode gap in discharging, the arc power was shown to have a non monotonic relationship with arc length for constant initial circuit voltage and resistance. Finally, the temperature rises of electrode surface caused by heat transfer from arc were found to be not sensitive with increasing arc length due to special heat transfer mechanism. In addition, temperature of ambient air showed a large gradient in radial direction of arc.

  18. An experimental study on the thermal characteristics and heating effect of arc-fault from Cu core in residential electrical wiring fires.

    Directory of Open Access Journals (Sweden)

    Jian-Hua Du

    Full Text Available The characteristics of a series direct current (DC arc-fault including both electrical and thermal parameters were investigated based on an arc-fault simulator to provide references for multi-parameter electrical fire detection method. Tests on arc fault behavior with three different initial circuit voltages, resistances and arc gaps were conducted, respectively. The influences of circuit conditions on arc dynamic image, voltage, current or power were interpreted. Also, the temperature rises of electrode surface and ambient air were studied. The results showed that, first, significant variations of arc structure and light emitting were observed under different conditions. A thin outer burning layer of vapor generated from electrodes with orange light was found due to the extremely high arc temperature. Second, with the increasing electrode gap in discharging, the arc power was shown to have a non monotonic relationship with arc length for constant initial circuit voltage and resistance. Finally, the temperature rises of electrode surface caused by heat transfer from arc were found to be not sensitive with increasing arc length due to special heat transfer mechanism. In addition, temperature of ambient air showed a large gradient in radial direction of arc.

  19. The Influence of Allocation on the Carbon Footprint of Electricity Production from Waste Gas, a Case Study for Blast Furnace Gas

    Directory of Open Access Journals (Sweden)

    Joeri Van Mierlo

    2013-03-01

    Full Text Available Producing electricity from waste gas is an after treatment for waste gas while recovering the energy content. This paper addresses the methodology to calculate the effect that waste gas energy recovery has on lowering the impact of climate change. Greenhouse gases are emitted while burning the waste gas. However, a thorough study should include the production of the feedstock as well as the production of the infrastructure. A framework is developed to calculate the environmental impact of electricity production from waste gas with a life cycle approach. The present paper has a twofold purpose: to assess the climate change impact of generating electricity with blast furnace gas (BFG as a waste gas from the steel industry; and to establish a sensitivity assessment of the environmental implications of different allocation rules.

  20. Active control of massively separated high-speed/base flows with electric arc plasma actuators

    Science.gov (United States)

    DeBlauw, Bradley G.

    The current project was undertaken to evaluate the effects of electric arc plasma actuators on high-speed separated flows. Two underlying goals motivated these experiments. The first goal was to provide a flow control technique that will result in enhanced flight performance for supersonic vehicles by altering the near-wake characteristics. The second goal was to gain a broader and more sophisticated understanding of these complex, supersonic, massively-separated, compressible, and turbulent flow fields. The attainment of the proposed objectives was facilitated through energy deposition from multiple electric-arc plasma discharges near the base corner separation point. The control authority of electric arc plasma actuators on a supersonic axisymmetric base flow was evaluated for several actuator geometries, frequencies, forcing modes, duty cycles/on-times, and currents. Initially, an electric arc plasma actuator power supply and control system were constructed to generate the arcs. Experiments were performed to evaluate the operational characteristics, electromagnetic emission, and fluidic effect of the actuators in quiescent ambient air. The maximum velocity induced by the arc when formed in a 5 mm x 1.6 mm x 2 mm deep cavity was about 40 m/s. During breakdown, the electromagnetic emission exhibited a rise and fall in intensity over a period of about 340 ns. After breakdown, the emission stabilized to a near-constant distribution. It was also observed that the plasma formed into two different modes: "high-voltage" and "low-voltage". It is believed that the plasma may be switching between an arc discharge and a glow discharge for these different modes. The two types of plasma do not appear to cause substantial differences on the induced fluidic effects of the actuator. In general, the characterization study provided a greater fundamental understanding of the operation of the actuators, as well as data for computational model comparison. Preliminary investigations

  1. Three-dimensional numerical modelling of a magnetically deflected dc transferred arc in argon

    International Nuclear Information System (INIS)

    Blais, A; Proulx, P; Boulos, M I

    2003-01-01

    The aim of this work is to develop a numerical model for the deflection of dc transferred arcs using an external magnetic field as a first step into the modelling of industrial arc furnaces. The arc is deflected by the use of a conductor aligned parallel to the arc axis through which flows an electric current. The model is validated by comparing the results of axisymmetric calculations to modelling results from the scientific literature. The present model is found to be a good representation of the electric dc arc as differences with the literature are easily explained by model parameters such as the critical boundary conditions at the electrodes. Transferred arc cases exhibit the expected behaviour as the temperature T, the velocity v-vector and the electrical potential drop Δφ all increase with the arc current I and the argon flow rate Q. Three-dimensional geometry is implemented, enabling one to numerically deflect the arc. For the deflected arc cases, the deflection increases with the arc current I and conductor current I conductor and decreases with the flow rate Q and x 0 , the arc-conductor distance. These deflection behaviours are explained using physical arguments

  2. Modeling of an electric arc transferred on a melted glass bath; Modelisation d`un arc electrique transfere sur un bain de verre

    Energy Technology Data Exchange (ETDEWEB)

    Mehlman, G.; Langlois, A. [SGN, 78 - Saint Quentin en Yvelines (France)

    1997-12-31

    The aim of this study is to propose a methodology allowing the simulation of melting processes involving electromagnetic phenomena. This methodology is based on the use of scientific calculation tools currently used elsewhere. The case considered in this study has been defined in collaboration with Electricite de France (EdF) and concerns more particularly an electric arc vitrification process for wastes. Basic data have been determined in order to obtain results representative of the tests performed by EdF with pilot installations. (J.S.)

  3. Thermal efficiency on welding of AA6061-T6 alloy by modified indirect electric arc and current signals digitalisation

    International Nuclear Information System (INIS)

    Ambriz, R. R.; Barrera, G.; Garcia, R.; Lopez, V. H.

    2009-01-01

    The results of the thermal efficiency on welding by modified indirect electric arc technique (MIEA) [1] of the 6061- T6 aluminum alloy are presented. These values are in a range of 90 to 94 %, which depend of the preheating employed. Thermal efficiency was obtained by means of a balance energy which considers the heat input, the amount of melted mass of the welding profiles, and welding parameters during the joining, especially of the arc current data acquisition. Also, some dimensionless parameters were employed in order to determine the approximation grade of the melted pool, the heat affected zone (HAZ), and their corresponding values with the experimental results. (Author) 13 refs

  4. Calorimeter probes for measuring high thermal flux. [in electric-arc jet facilities for planetary entry heating simulation

    Science.gov (United States)

    Russell, L. D.

    1979-01-01

    The paper describes expendable, slug-type calorimeter probes developed for measuring high heat-flux levels of 10-30 kW/sq cm in electric-arc jet facilities. The probes are constructed with thin tungsten caps mounted on Teflon bodies; the temperature of the back surface of the tungsten cap is measured, and its rate of change gives the steady-state, absorbed heat flux as the calorimeter probe heats to destruction when inserted into the arc jet. It is concluded that the simple construction of these probes allows them to be expendable and heated to destruction to obtain a measurable temperature slope at high heating rates.

  5. A novel process for preparation of titanium dioxide from Ti-bearing electric furnace slag: NH4HF2-HF leaching and hydrolyzing process.

    Science.gov (United States)

    Zheng, Fuqiang; Guo, Yufeng; Qiu, Guanzhou; Chen, Feng; Wang, Shuai; Sui, Yulei; Jiang, Tao; Yang, Lingzhi

    2018-02-15

    A novel process to prepare titanium dioxide from Ti-bearing electric furnace slag by NH 4 HF 2 -HF leaching and hydrolyzing process has been developed. In this present study, the effects of [NH 4 + ]/[F] mXolar ratio, leaching temperature, [F] concentration, liquid/solid mass ratio, leaching time on the Ti extraction, and the phase transformations have been investigated to reveal the leaching mechanism of Ti-bearing electric furnace slag in NH 4 HF 2 -HF solution. In the NH 4 HF 2 -HF leaching process, the MgTi 2 O 5 and Al 2 TiO 5 are converted to TiF 6 2- and Mg-Al-bearing precipitate. Ti extraction rate reached 98.84% under the optimal conditions. In addition, 98.25% iron ions can be removed in the presence of NaCl prior to hydrolysis process. The effects of pH and temperature on the selective hydrolysis of TiF 6 2- during hydrolysis process were also studied. In the hydrolysis process, the TiF 6 2- is converted to (NH 4 ) 2 TiOF 4 . By calcination, high grade TiO 2 powder with its purity of 99.88% was obtained, using which the products, well crystallized anatase and rutile, were obtained through roasting at 800°C and 1000°C, respectively. Copyright © 2017 Elsevier B.V. All rights reserved.

  6. Effects of Basicity and MgO in Slag on the Behaviors of Smelting Vanadium Titanomagnetite in the Direct Reduction-Electric Furnace Process

    Directory of Open Access Journals (Sweden)

    Tao Jiang

    2016-05-01

    Full Text Available The effects of basicity and MgO content on reduction behavior and separation of iron and slag during smelting vanadium titanomagnetite by electric furnace were investigated. The reduction behaviors affect the separation of iron and slag in the direct reduction-electric furnace process. The recovery rates of Fe, V, and Ti grades in iron were analyzed to determine the effects of basicity and MgO content on the reduction of iron oxides, vanadium oxides, and titanium oxides. The chemical compositions of vanadium-bearing iron and main phases of titanium slag were detected by XRF and XRD, respectively. The results show that the higher level of basicity is beneficial to the reduction ofiron oxides and vanadium oxides, and titanium content dropped in molten iron with the increasing basicity. As the content of MgO increased, the recovery rate of Fe increased slightly but the recovery rate of V increased considerably. The grades of Ti in molten iron were at a low level without significant change when MgO content was below 11%, but increased as MgO content increased to 12.75%. The optimum conditions for smelting vanadium titanomagnetite were about 11.38% content of MgO and quaternary basicity was about 1.10. The product, vanadium-bearing iron, can be applied in the converter steelmaking process, and titanium slag containing 50.34% TiO2 can be used by the acid leaching method.

  7. Ionization and electric field properties of auroral arcs during magnetic quiescence

    International Nuclear Information System (INIS)

    Robinson, R.M.; Mende, S.B.

    1990-01-01

    Studies of the morphology of auroral precipitation during times of magnetic quiescence indicate that the polar cap shrinks and becomes distorted into a teardrop or pear-shaped region. On November 16, 1987, incoherent scatter radar and all-sky imaging photometer measurements were made of auroral arcs over Sondre Stromfjord, Greenland. The arcs were generally oriented in a geographic east-west direction which is approximately Sun aligned at a local time just after dusk. Kp was 1, and the interlplanetary magnetic field was northward during the time of observation, so tha the arcs occurred under magnetically quiet conditions. The Sondrestrom radar measurements were used to determine the electron density and plasma drifts associated with the arcs; the all-sky imaging photometer data were used to relate the radar measurements to the arc morphology. Assuming the arcs were produced by precipitating electrons, the height profiles of electron density indicate average energies less than about 2 keV and energy fluxes of 1 erg/(cm 2 s). F region electron densities were high in the polar cap north of the arcs and low within the region of the arcs. The poleward boundary of the arc system was a convection reversal boundary across which plasma exited the polar cap region moving antisunward and then turned sunward (westward). The observed arc-associated convection is consistent with that expected under these geomagnetic conditions. Comparison of these results with the electrodynamic properties of other arcs observed in the afternoon and early evening suggests that there is a system of arcs that delineates the afternoon convection cell. The observed gradient in F region electron density across the arc can be explained in terms of the recombination of ionization drifting in response to the arc-associated convection pattern

  8. Three-dimensional numerical modelling of a magnetically deflected dc transferred arc in argon

    CERN Document Server

    Blais, A; Boulos, M I

    2003-01-01

    The aim of this work is to develop a numerical model for the deflection of dc transferred arcs using an external magnetic field as a first step into the modelling of industrial arc furnaces. The arc is deflected by the use of a conductor aligned parallel to the arc axis through which flows an electric current. The model is validated by comparing the results of axisymmetric calculations to modelling results from the scientific literature. The present model is found to be a good representation of the electric dc arc as differences with the literature are easily explained by model parameters such as the critical boundary conditions at the electrodes. Transferred arc cases exhibit the expected behaviour as the temperature T, the velocity v-vector and the electrical potential drop DELTA phi all increase with the arc current I and the argon flow rate Q. Three-dimensional geometry is implemented, enabling one to numerically deflect the arc. For the deflected arc cases, the deflection increases with the arc current I...

  9. Effect of addition of arc furnace dust in the microstructural properties of fly ash alkali-activated; Estudo do efeito da adicao do po de aciaria nas propriedades microestruturais de matrizes a base de cinzas volantes alcali-ativadas

    Energy Technology Data Exchange (ETDEWEB)

    Vargas, Alexandre Silva de [Centro de Estudos Superiores Feevale, Novo Hamburgo, RS (Brazil); Pavao, Bruno Barreto; Masuero, Angela Boreges; Dal Molin, Denise Carpena Coitinho; Vilela, Antonio Cezar Faria [Universidade Federal do Rio Grande do Sul (UFRS), RS (Brazil)

    2010-07-01

    The search for alternative materials for construction, with less environmental impact, has been the subject of several studies. The alkali-activated cements have shown potential for the reuse of waste, and can be used in the technology of solidification/stabilization. Thus, this study aims to evaluate the main effect of adding arc furnace dust (AFD) in the microstructural properties of matrices based on fly ash alkali-activated. Three levels of AFD were studied: 0, 5, 15 and 25%. The curing was set at 70°C/24 h, and after, kept at room temperature until the age of analysis - 1, 28 and 180 days, with XRD and FTIR analysis. In the XRD spectres it was found that compounds of albite and natron decrease the intensity of their peaks in that there is an increase in the levels of AFD. Concerning to the FTIR, we observed that the band characteristic of the fly ash (FA) 1084 cm{sup -1} was shifted to bands near 1000 cm{sup -1}, which shows that the residue does not interfere in the polymerization and aluminosilicate gel formation. Therefore, under the microstructural aspect, there were no major changes that would impair the use of this residue in alkali-activated matrices. (author)

  10. Internal Arc: People safety in the electrical wiring; Arco interno: Seguridad de las personas ante instalaciones electricas

    Energy Technology Data Exchange (ETDEWEB)

    Inchausti, J. M.

    2009-07-01

    The aim of this article is to describe the internal arc phenomenon, an extremely fast, almost explosive and unattended process of transformation form an initial electric power to the generation of a pressure and heat wave inside the medium its produced its consequences for safety, current methods of limiting them and current regulations in general for equipment used in medium-voltage electrical distribution networks. Taking into account that this type of equipment is found thought the distribution network in both public buildings and unrestricted access areas, safety (of operators and the general public) must be taken into account in the design of equipment and installations to minimize the risk of internal arcs occurring. This is the gist of, for example, ITC 16 of the Spanish Regulation on Power Plants and transformer substations. In addition to the construction aspects specific to each device in which the manufacturer has to takes steps to minimize the risks of an internal arcs occurring. This is the gist of, for example, ITC 16 of the Spanish Regulation on Power Plants and transformer substations. In addition to the construction aspects specific to each device in which an internal arc occurring, it is understood to be vitally important that users, installers and designers of Medium Voltage installations are familiar with the installation conditions stated by the manufacturer and thus avoid risks. (Author) 14 refs.

  11. Electric arc apparatus for severing split-pin assemblies of guide tubes of nuclear reactors

    International Nuclear Information System (INIS)

    Burns, D.C.; Kauric, C.E.; Persang, J.C.

    1987-01-01

    This patent describes an apparatus for use in the replacement of an old split-pin assembly of a guide tube of a nuclear reactor by a new split-pin assembly, the old split-pin assembly including an old split pin and an old nut securing the old split pin to the guide tube, the old split-pin assembly and the guide tube being radioactive. The apparatus includes a metal disintegration machining tool, the tool having an electrode, means for mounting the tool submerged in a pool of water in engagement with the guide tube and with the old split-pin assembly secured to the guide tube, the tool being so mounted with the electrode in position to coact electrically with the last-named old split-pin assembly but not with the guide tube, and means, connected to the tool, for firing a disintegrating arc between the electrode and the assembly to disintegrate the assembly into readily removable fragments

  12. Specificity of the tomography implementation in electric arc domain - Validity in medical imaging

    International Nuclear Information System (INIS)

    Benech, Julie

    2008-01-01

    The aim of these works was to implement a new experimental method to characterize 3D thermal plasmas by emission spectroscopy. The method used is based on tomographic technique which is widely used in medical imaging nowadays. However, tomography that we have developed and applied to electric arc is specific as the number of accessible projections angles is strongly limited: 4 projections our case against basically 64 in medical imaging. The particularity of our experimental tomographic system is that measurements are resolved both spectrally and spatially. The spectral resolution is necessary to determine the temperature values from method based on atomic line intensity. The spatial resolution is needed to simultaneously acquire the whole width of the plasma and so to reconstruct a whole cross-section in only one acquisition. One of the principal objective was to realize the experimental system of four-view tomography for thermal plasmas. Thanks to this device, we showed that the characterization of non-axisymmetric plasma is possible and that it enables to reconstruct 3D temperature maps. Finally, our tomographic method is applied with medical imaging data acquired in SPECT (Single Photon Emission Computed Tomography). These tests allowed validating the use of our tomographic reconstruction technique in SPECT, particularly the used iterative algebraic algorithm and the limited-view configuration. (author) [fr

  13. On the electrodynamic explanation of the retrograde motion of the electric arc

    International Nuclear Information System (INIS)

    Hong, J.S.; Allen, J.E.

    1992-01-01

    The retrograde motion of the cathode spot in a transverse magnetic field is one of the more intriguing phenomena of the electric arc. Although the phenomenon has been known for nearly ninety years since its discovery by Stark and has stimulated numerous investigations which result in many models giving explanation from different points of view, there is still no theory that can account both qualitatively and quantitatively for all the observations. Most of the explanations of the retrograde motion involve the study of cathode processes to give the preferential formation of new cathode spots along the retrograde direction. One line of explanation, which is rather different from the others, is based on electrodynamics. In this approach the retrograde motion is treated as an electrodynamic event. The present paper develops the theory suggested by Robson and von Engel. A more complete model is proposed and studied in detail by means of electromagnetic field theory. The results obtained not only show that the retrograde motion can be explained by the electrodynamics, but also confirm that the average current density on the cathode spot must be around the order of 10 12 A/m 2 . Recent studies of spot current density have shown values of this order. (author) 22 refs., 4 figs., 1 tab

  14. Electric arc spraying for restoration and repair of metallurgical equipment parts

    Directory of Open Access Journals (Sweden)

    В’ячеслав Олександрович Роянов

    2016-07-01

    Full Text Available It has been shown that the electric arc spraying with the use of powder wires can be used to repair and restore parts of metallurgical equipment. The technology of spraying parts by means of the cored wire Steelcored M8TUV; T462MMIN5 and combinations of steel and aluminum wires to restore shaft-gears, shaft-beams, cranes axles for the foundry of the Moldavian Metallurgical Plant has been introduced. The composition of the flux-cored wires MMP-2,3 developed at the Department of Equipment and welding production technology of PSTU that provides the required hardness and adhesion of the coating and the substrate have been shown and the results of the coatings properties studies have been published. Studies have shown matching properties of the coatings to be used for details of the metallurgical equipment working under difficult conditions, including the rolls of rolling mills. Cored wire was used for pilot plating of the rolls surface of the skin-rolling stand at the cold-rolling mill at Illich Steel and Iron Works, Mariupol. Residual coating thickness ranged from 15 to 25 microns. Strip sized 0,9 × 1025 mm has been rolled, the squeezing is equal to 0,8...1,0%.

  15. Arc melter demonstration baseline test results

    International Nuclear Information System (INIS)

    Soelberg, N.R.; Chambers, A.G.; Anderson, G.L.; Oden, L.L.; O'Connor, W.K.; Turner, P.C.

    1994-07-01

    This report describes the test results and evaluation for the Phase 1 (baseline) arc melter vitrification test series conducted for the Buried Waste Integrated Demonstration program (BWID). Phase 1 tests were conducted on surrogate mixtures of as-incinerated wastes and soil. Some buried wastes, soils, and stored wastes at the INEL and other DOE sites, are contaminated with transuranic (TRU) radionuclides and hazardous organics and metals. The high temperature environment in an electric arc furnace may be used to process these wastes to produce materials suitable for final disposal. An electric arc furnace system can treat heterogeneous wastes and contaminated soils by (a) dissolving and retaining TRU elements and selected toxic metals as oxides in the slag phase, (b) destroying organic materials by dissociation, pyrolyzation, and combustion, and (c) capturing separated volatilized metals in the offgas system for further treatment. Structural metals in the waste may be melted and tapped separately for recycle or disposal, or these metals may be oxidized and dissolved into the slag. The molten slag, after cooling, will provide a glass/ceramic final waste form that is homogeneous, highly nonleachable, and extremely durable. These features make this waste form suitable for immobilization of TRU radionuclides and toxic metals for geologic timeframes. Further, the volume of contaminated wastes and soils will be substantially reduced in the process

  16. Next Generation Metallic Iron Nodule Technology in Electric Arc Steelmaking - Phase II

    Energy Technology Data Exchange (ETDEWEB)

    Donald R. Fosnacht; Iwao Iwasaki; Richard F. Kiesel; David J. Englund; David W. Hendrickson; Rodney L. Bleifuss

    2010-12-22

    The current trend in the steel industry is a gradual decline in conventional steelmaking from taconite pellets in blast furnaces, and an increasing number of alternative processes using metallic scrap iron, pig iron and metallized iron ore products. Currently, iron ores from Minnesota and Michigan are pelletized and shipped to the lower Great Lakes ports as blast furnace feed. The existing transportation system and infrastructure is geared to handling these bulk materials. In order to expand the opportunities for the existing iron ore mines beyond their blast furnace customer base, a new material is needed to satisfy the needs of the emerging steel industry while utilizing the existing infrastructure and materials handling. A recent commercial installation employing Kobe Steel’s ITmk3 process, was installed in Northeastern Minnesota. The basic process uses a moving hearth furnace to directly reduce iron oxides to metallic iron from a mixture of iron ore, coals and additives. The resulting products can be shipped using the existing infrastructure for use in various steelmaking processes. The technology reportedly saves energy by 30% over the current integrated steelmaking process and reduces emissions by more than 40%. A similar large-scale pilot plant campaign is also currently in progress using JFE Steel’s Hi-QIP process in Japan. The objective of this proposal is to build upon and improve the technology demonstrated by Kobe Steel and JFE, by further reducing cost, improving quality and creating added incentive for commercial development. This project expands previous research conducted at the University of Minnesota Duluth’s Natural Resources Research Institute and that reported by Kobe and JFE Steel. Three major issues have been identified and are addressed in this project for producing high-quality nodular reduced iron (NRI) at low cost: (1) reduce the processing temperature, (2) control the furnace gas atmosphere over the NRI, and (3) effectively use sub

  17. The influence of electric ARC activation on the speed of heating and the structure of metal in welds

    Directory of Open Access Journals (Sweden)

    Savytsky Oleksandr M.

    2016-01-01

    Full Text Available This paper presents the results of a research related to the impact of electric arc activation onto drive welding energy and metal weld heating speed. It is confirmed that ATIG and AMIG methods, depending on metal thickness, single pass weldability and chemical composition of activating flux, enable the reduction of welding energy by 2-6 times when compared to conventional welding methods. Additionally, these procedures create conditions to increase metal weld heating speed up to 1,500-5,500°C/s-1. Steel which can be rapidly heated, allows for a hardened structure to form (with carbon content up to 0.4%, together with a released martensitic structure or a mixture of bainitic-martensitic structures. Results of the research of effectiveness of ATIG and AMIG welding showed that increase in the penetration capability of electric arc, which increases welding productivity, is the visible side of ATIG and AMIG welding capabilities.

  18. Structure and Distribution of Components in the Working Layer Upon Reconditioning of Parts by Electric-Arc Metallization

    Science.gov (United States)

    Skoblo, T. S.; Vlasovets, V. M.; Moroz, V. V.

    2001-11-01

    Reliable data on the structure of the deposited layer are very important due to the considerable instability of the process of deposition of coatings by the method of electric-arc metallization and the strict requirements for reconditioned crankshafts. The present paper is devoted to the structure of coatings obtained from powder wire based on ferrochrome-aluminum with additional alloying elements introduced into the charge.

  19. US bureau of mines small-scale arc melter tests

    International Nuclear Information System (INIS)

    O'Connor, W.K.; Oden, L.L.; Turner, P.C.; Davis, D.L.

    1993-01-01

    The US Bureau of Mines, in cooperation with the Idaho National Engineering Laboratory (INEL), conducted over 30 hours of melting tests to vitrify simulated low-level radioactive wastes from the INEL. Radioactive Waste Management Complex (RWMC). Five separate waste compositions were investigated, each consisting of noncontaminated soil from the RWMC and surrogate materials used to simulate the actual buried wastes. The RWMC soil and five waste compositions were melted in a 50-lb, single-phase electric arc furnace with a water-cooled shell. These tests were conducted to determine melting parameters in preparation for a large-scale melting campaign to be conducted in the Bureau's 1-metric ton (mt), water-cooled-wall, 3-phase electric arc furnace. Bulk chemical composition was determined for each of the feed materials and for the slag, metal, fume solids, and offgas furnace products, and distributions were calculated for the key elements. The material balance for the furnace operation indicates that from 63 to 84 pct of the feed reported to the slag. Cerium, used as the surrogate for the radionuclides in the wastes, demonstrated an extremely strong affinity for the slag product. Although slag temperatures as low as 1,250 C were recorded when melting the RWMC soil, temperatures in excess of 1,600 C were necessary to achieve the fluidity required for a successful slag tap

  20. Sensoring fusion data from the optic and acoustic emissions of electric arcs in the GMAW-S process for welding quality assessment.

    Science.gov (United States)

    Alfaro, Sadek Crisóstomo Absi; Cayo, Eber Huanca

    2012-01-01

    The present study shows the relationship between welding quality and optical-acoustic emissions from electric arcs, during welding runs, in the GMAW-S process. Bead on plate welding tests was carried out with pre-set parameters chosen from manufacturing standards. During the welding runs interferences were induced on the welding path using paint, grease or gas faults. In each welding run arc voltage, welding current, infrared and acoustic emission values were acquired and parameters such as arc power, acoustic peaks rate and infrared radiation rate computed. Data fusion algorithms were developed by assessing known welding quality parameters from arc emissions. These algorithms have showed better responses when they are based on more than just one sensor. Finally, it was concluded that there is a close relation between arc emissions and quality in welding and it can be measured from arc emissions sensing and data fusion algorithms.

  1. Sensoring Fusion Data from the Optic and Acoustic Emissions of Electric Arcs in the GMAW-S Process for Welding Quality Assessment

    Directory of Open Access Journals (Sweden)

    Eber Huanca Cayo

    2012-05-01

    Full Text Available The present study shows the relationship between welding quality and optical-acoustic emissions from electric arcs, during welding runs, in the GMAW-S process. Bead on plate welding tests was carried out with pre-set parameters chosen from manufacturing standards. During the welding runs interferences were induced on the welding path using paint, grease or gas faults. In each welding run arc voltage, welding current, infrared and acoustic emission values were acquired and parameters such as arc power, acoustic peaks rate and infrared radiation rate computed. Data fusion algorithms were developed by assessing known welding quality parameters from arc emissions. These algorithms have showed better responses when they are based on more than just one sensor. Finally, it was concluded that there is a close relation between arc emissions and quality in welding and it can be measured from arc emissions sensing and data fusion algorithms.

  2. Pengaruh Beban Kerja dan Faktor Lingkungan Fisik Terhadap Tekanan Darah, Denyut Nadi dan Tingkat Kelelahan Pekerja Bagian ARC FURNACE dan ROLLING MILL PT. Inti General Yaja Steel Semarang

    Directory of Open Access Journals (Sweden)

    Ulfa Nurullita

    2015-12-01

    Full Text Available ABSTRACT Background: The existence of work efficiency can be reached with balancing work capacity and increase capacity in the working environment. One factor  in the  working  environment that cause work  inefficiency  is physical factor namely  heat stress, noise and lighting. The influence of physical  factors are indicated by  physical performance of the worker’s blood pressure  and fatigue level. Objective: to find out  the influence of work capacity and physical factors in the working  environment on the blood pressure, pulse, fatigue level of worker in  Arc Furnacearea  and Rolling Mill section, PT Inti General Yaja Steel Semarang. Methode: Type of the research was quasy experimental  with one group pre and post test design. The population were 178 worker  and  47 workers were  taken in this research. Confounding factors was cigarettes, cafein, drug consumption, and nutrition status. Result: There was  found differences of blood pressure before working  and after working (systole; p- Wilcoxon Sign Ranks = 0,001, diatole; p- Wilcoxon Sign Ranks, = 0,003. The average before working (systole=119,7 mmHg, diastole= 84 mmHg was higher than after working (systole=107,2 mmHg, diastole= 78,9 mmHg. There was  also  differences of  pulse rate before working  and after working  (p-paired t test= 0,001. The average of pulse before working (81,5 times/minute was lower than after working (87,5 times/minute. There was found differences of fatigue level before working and after working (p- Wilcoxon Sign Ranks=0,001. The average of fatigue level before working was measured  253,2 millisecond lower than after working  (290,7 milisecond. Conclusion: There is found  differences  of blood pressure, pulse and fatigue level before working  and after working. There are no differences of blood pressure transition, pulse transition and fatigue transition  based on heat stress, noise, lighting, work capacity, cigarettes, cafein, drug

  3. The induction furnace as a melting facility in steel production. Pt. 1. Features of induction furnaces used in steel production; Der Induktionsofen als Schmelzaggregat fuer die Stahlerzeugung. T. 1. Merkmale von Induktionsoefen in der Stahlerzeugung

    Energy Technology Data Exchange (ETDEWEB)

    Chaabet, Mohamed; Doetsch, Erwin [ABP Induction Systems GmbH, Dortmund (Germany)

    2011-12-15

    Global steel output has now been growing extremely rapidly for a prolonged time; in the past ten years alone, annual production has risen from 851 million t/a (in 2001) to 1417 million t/a (2010), as a result, primarily, of growth in China. Electric steel production using the electric arc furnace as the classical melting facility is around 45 % world-wide, with a rising trend (but excluding the special case of China, where oxygen-route steel holds a 90 % share of production). Following the development of induction technology and inverter outputs of over 40 MW for crucible furnaces with capacities of above 65 t, the induction furnace is now available as an alternative electrical melting installation for use in smaller mini steel mills. The benefits of this technology can be found in high feed-material efficiencies and low environmental and workplace burdens, in addition to the absence of electrode costs and the only modest demands made on the power-supply grid. These features of the induction furnace and their special significance for steel production are examined in Part 1 of this article. The second part of the article then focuses on examples of the use of induction furnaces in the steelmaking plant. (orig.)

  4. Double-ended metal halide arc discharge lamp with electrically isolated containment shroud

    Science.gov (United States)

    Muzeroll, Martin M. (Inventor)

    1994-01-01

    A double-ended arc discharge lamp includes a sealed, light-transmissive outer jacket, a light-transmissive shroud mounted within the outer jacket and directly supported by the outer jacket, and an arc discharge tube mounted within the shroud. The arc tube is typically a metal halide arc discharge tube. In a preferred embodiment, the shroud includes an outwardly flared portion at each end. The outwardly flared portions space the shroud from the outer jacket and support the shroud within the outer jacket. The outwardly flared portions of the shroud can be affixed to the outer jacket by fusing. The outer jacket can be provided with inwardly extending dimples for locating the shroud with respect to the outer jacket. In another embodiment, the outer jacket includes reduced diameter portions near each end which are attached to the shroud.

  5. A Heat and Mass Transfer Model of a Silicon Pilot Furnace

    Science.gov (United States)

    Sloman, Benjamin M.; Please, Colin P.; Van Gorder, Robert A.; Valderhaug, Aasgeir M.; Birkeland, Rolf G.; Wegge, Harald

    2017-10-01

    The most common technological route for metallurgical silicon production is to feed quartz and a carbon source ( e.g., coal, coke, or charcoal) into submerged-arc furnaces, which use electrodes as electrical conductors. We develop a mathematical model of a silicon furnace. A continuum approach is taken, and we derive from first principles the equations governing the time evolution of chemical concentrations, gas partial pressures, velocity, and temperature within a one-dimensional vertical section of a furnace. Numerical simulations are obtained for this model and are shown to compare favorably with experimental results obtained using silicon pilot furnaces. A rising interface is shown to exist at the base of the charge, with motion caused by the heating of the pilot furnace. We find that more reactive carbon reduces the silicon monoxide losses, while reducing the carbon content in the raw material mixture causes greater solid and liquid material to build-up in the charge region, indicative of crust formation (which can be detrimental to the silicon production process). We also comment on how the various findings could be relevant for industrial operations.

  6. Approach to modeling of the fast energy discharge in cryogenic systems in the form of an electric arc

    CERN Multimedia

    CERN. Geneva

    2016-01-01

    Superconducting magnets are supplied with a few kA of electric current and can store a large amount of energy. Therefore, cryogenic systems which are comprised of such magnets are subject to the risk of fast energy discharge from the magnets themselves in the form of an electric arc. The arcing can be a result of failure in the insulation of an electric circuit or in the connection between the magnet and its current lead. During the discharge, energy can be partially dissipated into the cryogen and partially into the cryogenic system metallic structure. The part of the energy that is transferred to the metallic structure will strongly heat up the metal surface, which can lead to material burning. In this case, the cryogen will flow through the perforation to the insulation vacuum space, which can trigger a rapid increase in pressure in the vacuum enclosure. However, the discharged energy that has been stored in the cryogen also causes a rapid increase in cryogenic pressure. Hence, the proper estimation of the...

  7. A glucose concentration and temperature sensor based on long period fiber gratings induced by electric-arc discharge

    Science.gov (United States)

    Du, Chao; Wang, Qi

    2017-10-01

    As one of the key parameters in biological and chemical reactions, glucose concentration objectively reflects the characteristics of reactions, so the real-time monitoring of glucose concentration is important in the field of biochemical. Meanwhile, the influence from temperature should be considered. The fiber sensors have been studied extensively for decades due to the advantages of small size, immunity to electromagnetic interference and high sensitivity, which are suitable for the application of biochemical sensing. A long period fiber grating (LPFG) sensor induced by electric-arc discharge has been fabricated and demonstrated for simultaneous measurement of glucose concentration and temperature. The proposed sensor was fabricated by inscribing a sing mode fiber (SMF) with periodic electric-arc discharge technology. During the fabrication process, the electric-arc discharge technology was produced by a commercial fusion splicer, and the period of inscribed LPFG was determined by the movement of translation stages. A serials of periodic geometrical deformations would be formed in SMF after the fabrication, and the discharge intensity and discharge time can be adjusted though the fusion splicer settings screen. The core mode can be coupled into the cladding modes at certain wavelength when they satisfy the phase-matching conditions, and there will be several resonance dips in the transmission spectrum in LPFG. The resonance dips formed by the coupling between cladding modes and core mode have different sensitivity responses, so the simultaneous measurement for multi-parameter can be realized by monitoring the wavelength shifts of the resonance dips. Compared with the LPFG based on conventional SMF, the glucose concentration sensitivity has been obviously enhanced by etching the cladding with hydrofluoric acid solution. Based on the independent measured results, a dual-parameter measurement matrix has been built for signal demodulation. Because of the easy

  8. Simulation of electric arc with hysteresis during discharge of a fusion superconducting magnet system

    International Nuclear Information System (INIS)

    Kraus, H.G.; Jones, J.L.

    1986-01-01

    Simulation of an internal voltage induced arc strike and attendant voltage-current hysteresis characteristics in an FED/INTOR scale superconducting magnet and circuit protection system during discharge was performed. To begin, an analytical solution was used to investigate system response for an internally shorted magnet and simplified circuit protection system during magnet discharge. The short produced a current split within the magnet resulting in a transformer like mutual inductance effect. Thus, the coupling coefficient was introduced in the equations to be physically realistic and to prevent degeneration of the associated eigenvalue problem. The effects of varying short resistance, dump resistance, and number of coil turns shorted are presented. This led to simulation of an arc strike, including hysteresis effects, which is then compared to the usual constant resistance used to simulate magnet shorts. Tracking of arc characteristics was made possible through specially developed multiple tripping capabilities recently incorporated into MSCAP (Magnet Systems Circuitry Analysis Program) for safety and instrumentation control simulation

  9. Presentation of the Vulcano installation which uses a plasma transferred arc rotary furnace for corium melting; Utilisation d`un four tournant a arc plasma transfere pour fondre et couler des melanges d`oxydes autour de 2000 C. Presentation du film Vulcano

    Energy Technology Data Exchange (ETDEWEB)

    Cognet, G.; Laffont, G.; Jegou, C.; Pierre, J.; Journeau, C.; Sudreau, F.; Roubaud, A. [CEA Cadarache, 13 - Saint-Paul-lez-Durance (France). Dept. d`Etudes des Reacteurs

    1998-06-01

    In the case of loss coolant accident, the reactor core could melt and turn into a mixture of uranium oxides, zirconium, iron and steel called corium. A large experimental program has been launched to study corium behaviour, to qualify solutions to stabilize it and to confine it in the reactor containment. The Vulcano installation has been designed to that purpose. It is made up of: i) a plasma transferred arc rotary furnace, ii) a testing surface covered with refractory materials, iii) an induction heating system in order to simulate the residual power of corium, iv) instrumentation devices such as video cameras, thermocouples, infra-red pyrometers and flowmeters, and v) a laboratory to perform chemical analysis of corium samples. The first experimental results show that a mixture of corium and concrete spreads better than expected. It seems that a low initial height of matter can produce a great distance flowing while having a chaotic behaviour. This characteristic suggests that the mixture acts as a Bingham type threshold fluid. (A.C.) 5 refs.

  10. Electrical faults in vehicle powernets - Methodical investigation of arcing faults in passenger cars and HGV; Fehlerfaelle in Fahrzeug-Bordnetzen - Methodische Untersuchung von Lichtboegen in Pkw und Lkw

    Energy Technology Data Exchange (ETDEWEB)

    Grosse, R.; Magenheimer, K.; Moenchmeier, A.; Stepec, H.; Viscido, T.; Wagner, C. [Forschungsgesellschaft Kraftfahrwesen Aachen mbH, Aachen (Germany)

    2004-07-01

    In vehicle powernets with a voltage higher than 20 V the possibility for the formation of electrical arcs is given. For that reason the electronics department of the fka analyses the characteristics of arc faults in vehicle powernets. Theoretical investigations and their validation by practical experiments help to determine the characteristic values of arcs. Regarding the insertion into powernets of real vehicles, either specific or general topologies get simulated. A further task of the ''fka powernet test bench'' is to bring out the technical validation of protection devices preventing arcing faults. For that purpose the protection devices get integrated into a realistic powernet replication to analyse their functionality. Within the scope of an analysis arcing faults were simulated which appear in commercial vehicle powernets by different reasons. For these purposes standard arcing tests were applied which are commonly used in aerospace and military applications. The analysis resulted in the cognition that a revision of the standard arcing tests is necessary to (a) improve the reproducibility of the tests, (b) to simulate the automotive surrounding more life like and (c) to enable a standardisation of the tests. In this article the revised tests are described. With these tests arc faults can be generated which can be used to verify the functionality of protection devices. The proposed tests can be used as a basis for standard tests. (orig.)

  11. Evaluation of SF6-alternative gas C5-PFK based on arc extinguishing performance and electric strength

    Science.gov (United States)

    Wu, Yi; Wang, Chunlin; Sun, Hao; Rong, Mingzhe; Murphy, Anthony Bruce; Li, Tianwei; Zhong, Jianying; Chen, Zhexin; Yang, Fei; Niu, Chunpin

    2017-09-01

    C5-PFK (C5-perfluoroketone, C5F10O) is under wide consideration as an environmentally-friendly alternative gas to SF6 in high-voltage applications, because of its superior insulation performance. The aim of this work is to study theoretically the arc extinguishing performance and electric strength of C5-PFK. The arc extinguishing performance of C5-PFK was evaluated by analyzing and comparing the thermophysical properties of C5-PFK, SF6, CF4, CO2 and N2 plasmas. It was difficult to obtain the species formed in C5-PFK plasmas because of the complex C5-PFK molecular decomposition process. In this work, the decomposition process of C5-PFK and the related species were analyzed by the bond energy analysis method. For the species for which parameters such as the partition function and the enthalpy of formation were not available, computational chemistry methods were used to obtain the required data. The collision integrals were calculated using the phenomenological potential model. Using these results, the local thermodynamic equilibrium composition at temperatures from 300 to 30 000 K at 1-10 atm of pure C5-PFK was calculated by the method of minimization of the Gibbs free energy, and the corresponding transport coefficients were calculated by Chapman-Enskog method. Through the comparison of the thermophysical properties, it was found that C5-PFK had similar characteristics to SF6, with large peaks in specific heat below 4500 K, indicating potentially good thermal interruption capability. However, the specific heat peak at 7000 K corresponding to CO decomposition may detract from the thermal interruption capability. Specific heat peaks at higher temperatures are associated with the breaking of double or triple bonds, and should be avoided if possible in the new alternative gases. The electric strength of C5-PFK was assessed using the molecular electrostatic potential, which can be accurately calculated or measured, and gives strong insights into important

  12. Study of electric arc welding of castings for nuclear power machine-building

    International Nuclear Information System (INIS)

    Rymkevich, A.I.; Korsunov, P.M.

    1977-01-01

    Mechanical and corrosion-resistance properties are studied of the welded joints of cast billets from steel 00Kh12N3DL by automatic submerged arc welding. It is shown by testing the joints made with preheating up to 100 deg C and subsequent tempering (620 deg C for 25 h + 640 deg C for 16 h) that in the temperature range of 20-350 deg C they possess fairly good strength, ductility, impact viscosity, and corrosion-resistance properties approximating the corresponding characteristics of the base metal. The welding technology developed can be used to make pump casings for atomic power equipment

  13. Characterization of Ladle Furnace Slag from Carbon Steel Production as a Potential Adsorbent

    Directory of Open Access Journals (Sweden)

    Ankica Rađenović

    2013-01-01

    Full Text Available A promising type of steel slag for applications is the ladle furnace (LF slag, which is also known as the basic slag, the reducing slag, the white slag, and the secondary refining slag. The LF slag is a byproduct from further refining molten steel after coming out of a basic oxygen furnace (BOF or an electric arc furnace (EAF. The use of the LF slag in further applications requires knowledge of its characteristics. The LF slag characterization in this paper has been performed using the following analytical methods: chemical analysis by energy dispersive spectrometry (EDS, mineralogical composition by X-ray diffraction (XRD, surface area properties by the Brunauer-Emmett-Teller (BET and the Barrett-Joyner-Halenda (BJH methods, surface chemistry by infrared absorption (FTIR spectroscopy, and morphological analysis by scanning electron microscopy (SEM. The results showed that the main compounds are calcium, silicon, magnesium, and aluminium oxides, and calcium silicates under their various allotropic forms are the major compounds in the LF slag. Surface area properties have shown that the LF slag is a mesoporous material with relatively great BET surface area. The ladle furnace slag is a nonhazardous industrial waste because the ecotoxicity evaluation by its eluate has shown that the LF slag does not contain constituents which might in any way affect the environment harmfully.

  14. Calculation of t8/5 by response surface methodology for electric arc welding applications

    Directory of Open Access Journals (Sweden)

    Meseguer-Valdenebro José Luis

    2014-01-01

    Full Text Available One of the greatest difficulties traditionally found in stainless steel constructions has been the execution of welding parts in them. At the present time, the available technology allows us to use arc welding processes for that application without any disadvantage. Response surface methodology is used to optimise a process in which the variables that take part in it are not related to each other by a mathematical law. Therefore, an empiric model must be formulated. With this methodology the optimisation of one selected variable may be done. In this work, the cooling time that takes place from 800 to 500ºC, t8/5, after TIG welding operation, is modelled by the response surface method. The arc power, the welding velocity and the thermal efficiency factor are considered as the variables that have influence on the t8/5 value. Different cooling times,t8/5, for different combinations of values for the variables are previously determined by a numerical method. The input values for the variables have been experimentally established. The results indicate that response surface methodology may be considered as a valid technique for these purposes.

  15. Model of formation of droplets during electric arc surfacing of functional coatings

    Science.gov (United States)

    Sarychev, Vladimir D.; Granovskii, Alexei Yu; Nevskii, Sergey A.; Gromov, Victor E.

    2016-01-01

    The mathematical model was developed for the initial stage of formation of an electrode metal droplet in the process of arc welding. Its essence lies in the fact that the presence of a temperature gradient in the boundary layer of the molten metal causes thermo-capillary instability, which leads to the formation of electrode metal droplets. A system of equations including Navier-Stokes equations, heat conduction and Maxwell's equations was solved as well as the boundary conditions for the system electrodes-plasma. Dispersion equation for thermo-capillary waves in the linear approximation for the plane layer was received and analyzed. The values of critical wavelengths, at which thermo-capillary instability appears in the nanometer wavelength range, were found. The parameters at which the mode of a fine-droplet transfer of the material takes place were theoretically defined.

  16. Energy Saving in Industrial Annealing Furnaces

    Directory of Open Access Journals (Sweden)

    Fatma ÇANKA KILIÇ

    2018-03-01

    Full Text Available In this study, an energy efficiency studies have been carried out in a natural gas-fired rolling mill annealing furnace of an industrial establishment. In this context, exhaust gas from the furnace has been examined in terms of waste heat potential. In the examinations that have been made in detail; waste heat potential was found as 3.630,31 kW. Technical and feasibility studies have been carried out to realize electricity production through an Organic Rankine Cycle (ORC system for evaluating the waste heat potential of the annealing furnace. It has been calculated that 1.626.378,88 kWh/year of electricity can be generated by using the exhaust gas waste heat of the annealing furnace through an ORC system to produce electric energy with a net efficiency of 16%. The financial value of this energy was determined as 436.032,18 TL/year and the simple repayment period of the investment was 8,12 years. Since the annealing period of the annealing furnace is 2800 hours/year, the investment has not been found to be feasible in terms of the feasibility studies. However, the investment suitability can be assured when the annealing furnace is operating at full capacity for 8,000 hours or more annually.

  17. Characterization of a manganese ore to define the use in the fluxes synthesis for submerged arc welding

    International Nuclear Information System (INIS)

    Cruz, A.; Quintana, R.; Perdomo, L.; Garcia, L. L.; Formoso, A.; Cores, A.

    2003-01-01

    Chemical analysis, thermal analysis (DTA and TG), phase determination by X-ray diffraction and granulometric analysis of the manganese ore from the location Margarita de Cambute in the eastern part of cuba were carried out. Based on these characterization results, a flux synthesis strategy was established, comprising the definition, as a basic condition, of the MnO/SiO 2 range of values. This strategy was confirmed experimentally by obtaining a flux prototype in an electric arc furnace connected to direct current source and the carrying out of the flux in submerged arc welding tests. (Author) 26 refs

  18. Geothermal Potential of the Cascade and Aleutian Arcs, with Ranking of Individual Volcanic Centers for their Potential to Host Electricity-Grade Reservoirs

    Energy Technology Data Exchange (ETDEWEB)

    Shevenell, Lisa [ATLAS Geosciences, Inc., Reno, NV (United States); Coolbaugh, Mark [ATLAS Geosciences, Inc., Reno, NV (United States); Hinz, Nick [Univ. of Nevada, Reno, NV (United States); Stelling, Pete [Western Washington Univ., Bellingham, WA (United States); Melosh, Glenn [GEODE, Santa Rosa, CA (United States); Cumming, William [Cumming Geoscience, Santa Rosa, CA (United States)

    2015-10-16

    This project brings a global perspective to volcanic arc geothermal play fairway analysis by developing statistics for the occurrence of geothermal reservoirs and their geoscience context worldwide in order to rank U.S. prospects. The focus of the work was to develop play fairways for the Cascade and Aleutian arcs to rank the individual volcanic centers in these arcs by their potential to host electricity grade geothermal systems. The Fairway models were developed by describing key geologic factors expected to be indicative of productive geothermal systems in a global training set, which includes 74 volcanic centers world-wide with current power production. To our knowledge, this is the most robust geothermal benchmark training set for magmatic systems to date that will be made public.

  19. Generating electricity and heat from lean gas. Dual fuel engine generates electricity and process heat from cupola furnace gas; Strom und Waerme aus Schwachgas gewinnen. Zuendstrahlmotor erzeugt Strom und Prozesswaerme aus Kupolofengas

    Energy Technology Data Exchange (ETDEWEB)

    Hirn, Gerhard

    2012-07-01

    White-hot molten iron flows into the launder. The blast of heat released provides visitors with an impressive demonstration of the amount of energy flowing in foundries. Large volumes of carbon (coke) are used for the melting process in the cupola furnace, whereby a combustible process gas is formed as a by-product. This so-called cupola furnace gas has a low heating value and has previously been completely combusted for generating the hot blast in the cupola furnace's recuperator. However, in this process only around 35 % of the contained energy is used thermally. Now it is possible to utilise the remaining 65 % of the chemically bound energy that was previously not used in most foundries: a modified biogas combined heat and power plant runs with cupola furnace gas (CFG) from the melting furnace. (orig.)

  20. [Preclinical treatment of severe burn trauma due to an electric arc on an overhead railway cable].

    Science.gov (United States)

    Spelten, O; Wetsch, W A; Hinkelbein, J

    2013-09-01

    Severe burns due to electrical accidents occur rarely in Germany but represent a challenge for emergency physicians and their team. Apart from extensive burns cardiac arrhythmia, neurological damage caused by electric current and osseous injury corresponding to the trauma mechanism are also common. It is important to perform a survey of the pattern of injuries and treat acute life-threatening conditions immediately in the field. Furthermore, specific conditions related to burns must be considered, e.g. fluid resuscitation, thermal management and analgesia. In addition, a correct strategy for further medical care in an appropriate hospital is essential. Exemplified by this case guidelines for the treatment of severe burns and typical pitfalls are presented.

  1. Metal halide arc discharge lamp having short arc length

    Science.gov (United States)

    Muzeroll, Martin E. (Inventor)

    1994-01-01

    A metal halide arc discharge lamp includes a sealed light-transmissive outer jacket, a light-transmissive shroud located within the outer jacket and an arc tube assembly located within the shroud. The arc tube assembly includes an arc tube, electrodes mounted within the arc tube and a fill material for supporting an arc discharge. The electrodes have a spacing such that an electric field in a range of about 60 to 95 volts per centimeter is established between the electrodes. The diameter of the arc tube and the spacing of the electrodes are selected to provide an arc having an arc diameter to arc length ratio in a range of about 1.6 to 1.8. The fill material includes mercury, sodium iodide, scandium tri-iodide and a rare gas, and may include lithium iodide. The lamp exhibits a high color rendering index, high lumen output and high color temperature.

  2. Methodology for electrical studies in industrial networks including the study of electric arc; Metodologia para los estudios electricos en redes industriales incluyendo el estudio de arco electrico

    Energy Technology Data Exchange (ETDEWEB)

    Rasgado Casique, Jose Pepe; Silva Farias, Jose Luis [Instituto de Investigaciones Electricas, Cuernavaca, Morelos (Mexico)]. E-mail: jrasgado@iie.org.mx; jlsilva@iie.org.mx

    2010-11-15

    This article presents a methodology for conducting electrical studies in industrial networks. The methodology included the study of arc flash as a very important area of current basic electrical studies, such as power flow, short circuit and coordination. The aim of this study is to determine the Personal Protective Equipment (PPE) and flash protection boundary for personnel working with or near energized equipment, based on the IEEE Std 1584-2004 and NFPA-70E- 2004. Also included are criteria and recommendations to reduce incident energy level (cal/cm{sup 2}). At work we used a distribution network for industrial type test. The studies were carried out using a commercial program for the analysis of electrical networks. [Spanish] En este articulo se presenta una metodologia para llevar a cabo los estudios electricos en redes industriales. En la metodologia se incluye al estudio de arco electrico como un area muy importante de los estudios electricos basicos actuales, como: flujos de potencia, cortocircuito y coordinacion de protecciones. El objetivo de dicho estudio es determinar el Equipo de Proteccion Personal (EPP) apropiado y los limites de proteccion para el personal que opera con o cerca de equipo energizado, con base en las normas IEEE Std. 1584-2004 y la NFPA-70E-2004. Ademas, se incluyen criterios y recomendaciones para disminuir el nivel de energia incidente (cal/cm{sup 2}). En el trabajo se utilizo una red de distribucion tipo industrial de prueba. Los estudios se llevaron a cabo utilizando un programa comercial para el analisis de redes electricas.

  3. Acoustic Levitator With Furnace And Laser Heating

    Science.gov (United States)

    Barmatz, Martin B.; Stoneburner, James D.

    1991-01-01

    Acoustic-levitation apparatus incorporates electrical-resistance furnace for uniform heating up to temperature of about 1,000 degrees C. Additional local heating by pair of laser beams raise temperature of sample to more than 1,500 degrees C. High temperature single-mode acoustic levitator generates cylindrical-mode accoustic resonance levitating sample. Levitation chamber enclosed in electrical-resistance furnace. Infrared beams from Nd:YAG laser provide additional local heating of sample. Designed for use in containerless processing of materials in microgravity or in normal Earth gravity.

  4. Phase-Shifted Eccentric Core Fiber Bragg Grating Fabricated by Electric Arc Discharge for Directional Bending Measurement.

    Science.gov (United States)

    Ouyang, Yang; Liu, Jianxia; Xu, Xiaofeng; Zhao, Yujia; Zhou, Ai

    2018-04-11

    A phase-shifted eccentric core fiber Bragg grating (PS-ECFBG) fabricated by electric arc discharge (EAD) is presented and demonstrated. It is composed of a fraction of eccentric core fiber fusion spliced in between two pieces of commercial single mode fibers, where a PS-FBG was written. The EAD in this work could flexibly change the amount of phase-shift by changing the discharge number or discharge duration. Because of the offset location of the eccentric core and the ultra-narrow resonant peak of the PS-ECFBG, it has a higher accuracy for measuring the directional bend. The elongation and compression of the eccentric core keep the magnitude of phase shift still unchanged during the bending process. The bending sensitivities of the PS-ECFBG at two opposite most sensitive directions are 57.4 pm/m -1 and -51.5 pm/m -1 , respectively. Besides, the PS-ECFBG has the potential to be a tunable narrow bandpass filter, which has a wider bi-directional adjustable range because of the bending responses. The strain and temperature sensitivities of the PS-ECFBG are experimentally measured as well, which are 0.70 pm/με and 8.85 pm/°C, respectively.

  5. Phase-Shifted Eccentric Core Fiber Bragg Grating Fabricated by Electric Arc Discharge for Directional Bending Measurement

    Directory of Open Access Journals (Sweden)

    Yang Ouyang

    2018-04-01

    Full Text Available A phase-shifted eccentric core fiber Bragg grating (PS-ECFBG fabricated by electric arc discharge (EAD is presented and demonstrated. It is composed of a fraction of eccentric core fiber fusion spliced in between two pieces of commercial single mode fibers, where a PS-FBG was written. The EAD in this work could flexibly change the amount of phase-shift by changing the discharge number or discharge duration. Because of the offset location of the eccentric core and the ultra-narrow resonant peak of the PS-ECFBG, it has a higher accuracy for measuring the directional bend. The elongation and compression of the eccentric core keep the magnitude of phase shift still unchanged during the bending process. The bending sensitivities of the PS-ECFBG at two opposite most sensitive directions are 57.4 pm/m−1 and −51.5 pm/m−1, respectively. Besides, the PS-ECFBG has the potential to be a tunable narrow bandpass filter, which has a wider bi-directional adjustable range because of the bending responses. The strain and temperature sensitivities of the PS-ECFBG are experimentally measured as well, which are 0.70 pm/με and 8.85 pm/°C, respectively.

  6. Shape of argon spectral lines emitted from an electric arc (P=760 Torr). Study and application of pressure broadening

    International Nuclear Information System (INIS)

    Kretzas, Dimitrios.

    1978-01-01

    We have studied the broadening and shift of argon spectral lines corresponding to 3p 5 5p-3p 5 4s and 3p 5 4p-3p 5 4s transitions emitted from an electric arc burning under atmospheric pressure. We have revealed the broadening due to neutral atoms pressure effect, distinguishing the transitions whose lower level is a metastable one (1s 3 and 1s 5 ) or a level of strong (1s 2 ) or feeble resonance (1s 4 ). In this study we have employed a mixture of argon (98%) and hydrogen (2%); hydrogen's feeble proportion does not perturb much the discharge and is very suitable for the measure of the electronic density. The important departure of L.T.E. has guided us to imagine and apply an original method to measure the temperature and the overpopulation of the neutral atoms in the fondamental state. Our method which is independent of the existence of L.T.E. is based on the different behavior of the spectral lines which are under the influence of the resonance or Van der Waals broadening. The measure of the broadening constants which in the resonance case are independent of the temperature and vary as Tsup(0,3) for V.d.W's broadening, give us a suitable tool to measure the density and the temperature of the neutral atoms [fr

  7. Advanced steel reheat furnace

    Energy Technology Data Exchange (ETDEWEB)

    Moyeda, D.; Sheldon, M.; Koppang, R. [Energy and Environmental Research Corp., Irvine, CA (United States); Lanyi, M.; Li, X.; Eleazer, B. [Air Products and Chemicals, Inc., Allentown, PA (United States)

    1997-10-01

    Energy and Environmental Research Corp. (EER) under a contract from the Department of Energy is pursuing the development and demonstration of an Advanced Steel Reheating Furnace. This paper reports the results of Phase 1, Research, which has evaluated an advanced furnace concept incorporating two proven and commercialized technologies previously applied to other high temperature combustion applications: EER`s gas reburn technology (GR) for post combustion NOx control; and Air Product`s oxy-fuel enrichment air (OEA) for improved flame heat transfer in the heating zones of the furnace. The combined technologies feature greater production throughput with associated furnace efficiency improvements; lowered NOx emissions; and better control over the furnace atmosphere, whether oxidizing or reducing, leading to better control over surface finish.

  8. Influence of amount of oxidizing slag discharged from stainless steelmaking process of electric arc furnace on elution behavior into fresh water

    International Nuclear Information System (INIS)

    Yokoyama, S; Izaki, M; Shimomura, T; Hisyamudin, M N N; Takahashi, T

    2012-01-01

    Fundamental study was carried out for provision for acidification of soil due to acid rain. The influence of weight of the additive slag on elution behavior of the slag into water was studied in this study. Elution experiment was carried out on a basis of JIS K 0058-1. Generally, the pH in the aqueous solution increased with an increase in weight of the additive slag. The pH converged to approximately eight. Calcium, magnesium and manganese, which were essential elements for plants, were eluted from the slag irrespective to elution condition. The eluted concentrations of Ca and Mg increased with an increase in weight of the additive slag. Silicon and zinc were also eluted depending on the conditions. Aluminum that was harmful for plants was not eluted from the used slag.

  9. Influence of amount of oxidizing slag discharged from stainless steelmaking process of electric arc furnace on elution behavior into fresh water

    Science.gov (United States)

    Yokoyama, S.; Shimomura, T.; Hisyamudin, M. N. N.; Takahashi, T.; Izaki, M.

    2012-03-01

    Fundamental study was carried out for provision for acidification of soil due to acid rain. The influence of weight of the additive slag on elution behavior of the slag into water was studied in this study. Elution experiment was carried out on a basis of JIS K 0058-1. Generally, the pH in the aqueous solution increased with an increase in weight of the additive slag. The pH converged to approximately eight. Calcium, magnesium and manganese, which were essential elements for plants, were eluted from the slag irrespective to elution condition. The eluted concentrations of Ca and Mg increased with an increase in weight of the additive slag. Silicon and zinc were also eluted depending on the conditions. Aluminum that was harmful for plants was not eluted from the used slag.

  10. The influence of amperage of electric arc on microhardness in the area single and overlapping remeltings of HS 6-5-2 steel

    Directory of Open Access Journals (Sweden)

    A. Dziedzic

    2011-07-01

    Full Text Available The present thesis depicts the microhardness of HV0,065 surface layer of high speed steel HS6-5-2 remelted with the electric arc. There were different surface layer variants of remelting used – the amperage was changed from 50 to 120A with the stable scanning speed of 300mm/min. There was also the influence of overlapping of the remeltings on the microhardness result. The highest average microhardness of the surface layer of high speed steel HS6-5-2 amounting 1100 HV0,065 was achieved by using the amperage of electric arc of 50 A. The overlapping of remeltings is connected with the possibility of occurence of the microhardness decrease in the area of overlapping of the heat influence zone of second remelting (another remelting on the first remelting (the previous one.

  11. The influence of remelting parameters of the electric arc and conventional tempering on the tribological resistance of high speed steel HS 6-5-2

    Directory of Open Access Journals (Sweden)

    A. Dziedzic

    2011-07-01

    Full Text Available The present thesis depicts the results of the research of tribological high speed steel HS 6-5-2 remelted with the electric arc. Steel was remelted with different parameters. The amperage of electric arc was changed, the scanning speed was changed and the single, overlapping remeltings were used. There was also the influence of conventional tempering defined, which was conducted after remelting on the tribological resistance of hardened steel. For the previously mentioned processing variants, the intensity of tribological wear was defined and the linear wear were presented, and the friction coefficients. The type of tribological wear was also given, present during the friction, technically dry, of the hardened steel. The lower intensity of tribological wear was received for the single remelting by electric arc of 50 and 70A. Using the overlapping remeltings for the strengening of the surface layer of the high speed steel HS 6-5-2 causes the increase of the intensity of tribological wear in comparison to the steel with the single remelting. The conventional tempering leads to the decrease of the intensity of tribological wear.

  12. Continuous austempering fluidized bed furnace. Final report

    Energy Technology Data Exchange (ETDEWEB)

    Srinivasan, M.N. [Lamar Univ., Beaumont, TX (United States). Dept. of Mechanical Engineering

    1997-09-23

    The intended objective of this project was to show the benefits of using a fluidized bed furnace for austenitizing and austempering of steel castings in a continuous manner. The division of responsibilities was as follows: (1) design of the fluidized bed furnace--Kemp Development Corporation; (2) fabrication of the fluidized bed furnace--Quality Electric Steel, Inc.; (3) procedure for austempering of steel castings, analysis of the results after austempering--Texas A and M University (Texas Engineering Experiment Station). The Department of Energy provided funding to Texas A and M University and Kemp Development Corporation. The responsibility of Quality Electric Steel was to fabricate the fluidized bed, make test castings and perform austempering of the steel castings in the fluidized bed, at their own expense. The project goals had to be reviewed several times due to financial constraints and technical difficulties encountered during the course of the project. The modifications made and the associated events are listed in chronological order.

  13. Solar Convective Furnace for Metals Processing

    Science.gov (United States)

    Patidar, Deepesh; Tiwari, Sheetanshu; Sharma, Piyush; Pardeshi, Ravindra; Chandra, Laltu; Shekhar, Rajiv

    2015-11-01

    Metals processing operations, primarily soaking, heat treatment, and melting of metals are energy-intensive processes using fossil fuels, either directly or indirectly as electricity, to operate furnaces at high temperatures. Use of concentrated solar energy as a source of heat could be a viable "green" option for industrial heat treatment furnaces. This paper introduces the concept of a solar convective furnace which utilizes hot air generated by an open volumetric air receiver (OVAR)-based solar tower technology. The potential for heating air above 1000°C exists. Air temperatures of 700°C have already been achieved in a 1.5-MWe volumetric air receiver demonstration plant. Efforts to retrofit an industrial aluminium soaking furnace for integration with a solar tower system are briefly described. The design and performance of an OVAR has been discussed. A strategy for designing a 1/15th-scale model of an industrial aluminium soaking furnace has been presented. Preliminary flow and thermal simulation results suggest the presence of recirculating flow in existing furnaces that could possibly result in non-uniform heating of the slabs. The multifarious uses of concentrated solar energy, for example in smelting, metals processing, and even fuel production, should enable it to overcome its cost disadvantage with respect to solar photovoltaics.

  14. Calculations in furnace technology

    CERN Document Server

    Davies, Clive; Hopkins, DW; Owen, WS

    2013-01-01

    Calculations in Furnace Technology presents the theoretical and practical aspects of furnace technology. This book provides information pertinent to the development, application, and efficiency of furnace technology. Organized into eight chapters, this book begins with an overview of the exothermic reactions that occur when carbon, hydrogen, and sulfur are burned to release the energy available in the fuel. This text then evaluates the efficiencies to measure the quantity of fuel used, of flue gases leaving the plant, of air entering, and the heat lost to the surroundings. Other chapters consi

  15. High Temperature Transparent Furnace Development

    Science.gov (United States)

    Bates, Stephen C.

    1997-01-01

    This report describes the use of novel techniques for heat containment that could be used to build a high temperature transparent furnace. The primary objective of the work was to experimentally demonstrate transparent furnace operation at 1200 C. Secondary objectives were to understand furnace operation and furnace component specification to enable the design and construction of a low power prototype furnace for delivery to NASA in a follow-up project. The basic approach of the research was to couple high temperature component design with simple concept demonstration experiments that modify a commercially available transparent furnace rated at lower temperature. A detailed energy balance of the operating transparent furnace was performed, calculating heat losses through the furnace components as a result of conduction, radiation, and convection. The transparent furnace shells and furnace components were redesigned to permit furnace operation at at least 1200 C. Techniques were developed that are expected to lead to significantly improved heat containment compared with current transparent furnaces. The design of a thermal profile in a multizone high temperature transparent furnace design was also addressed. Experiments were performed to verify the energy balance analysis, to demonstrate some of the major furnace improvement techniques developed, and to demonstrate the overall feasibility of a high temperature transparent furnace. The important objective of the research was achieved: to demonstrate the feasibility of operating a transparent furnace at 1200 C.

  16. Comparative study of long-period gratings written in a boron co-doped fiber by an electric arc and UV irradiation

    International Nuclear Information System (INIS)

    Smietana, M; Bock, W J; Mikulic, P

    2010-01-01

    The paper presents for the first time a comparative study of long-period gratings (LPGs) written by point-by-point UV irradiation and by electrical arc discharges. These gratings were inscribed in a highly photosensitive boron co-doped fiber that can be considered as a suitable platform for LPG writing using either technology. The experimental transmission data for the manufactured LPG devices fit well when compared to the simulations we carried out in parallel. As a result of each of these writing processes, we were able to obtain a remarkably good quality of grating. Two reasons could explain the observed small differences between the spectra: a slight mismatch of the period of the gratings and an unintentional tapering of the fiber during the arc-based processes. We also found that the UV irradiation at λ = 248 nm can cause clearly visible damage to the fiber's surface. As a result of the UV writing, a coupling to the asymmetrical cladding modes can take place. Moreover, the gratings written using the two technologies show a very similar refractive index and temperature-sensing properties. The only differences between them can come from a physical deformation of the fiber induced by the electric arc discharges

  17. Fiscal 1996 project on the modeling for effective energy consumption in developing countries under a consignment from NEDO. Recent on the results of the demonstrative study on scrap preheater of electric furnace in the iron making process (for public); 1996 nendo hatten tojokoku energy shohi koritsuka model jigyo Shin Energy Sangyo Gijutsu Sogo Kaihatsu Kiko itaku. Seitetsu katei ni okeru denkiro no genryo yonetsu sochi ni kakawaru jissho kenkyu seika hokokusho (kokaiyo)

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    1997-03-01

    Indonesia is the biggest iron steel producing country in the ASEAN countries. Most of the production is produced by the electric furnace method in which iron steel scrap is used as a material. However, an energy saving measure in this method, the electric furnace scrap preheater using flue gas, has not yet been spread on a full scale. This R and D is aimed at developing jointly with Indonesia an electric furnace scrap preheater for medium/small size electric furnaces which are adoptable to the present iron making situation in Indonesia and installing it to the electric furnace of the iron making plant in Indonesia for a demonstrative study on energy saving, etc. Spread/expansion of the electric furnace scrap preheater which is an excellent energy saving system targeted expansion of energy saving technology not only of Indonesia, but of ASEAN countries and Japan. In this fiscal year, remodeling of part of the system was made by change of flue gas flow for increasing the energy saving effect, and at the same time, a research study was made of a scrap reheater effective as a total system. Moreover, the paper investigated technical data/information in Japan and overseas. 3 figs., 9 tabs.

  18. Baseline tests for arc melter vitrification of INEL buried wastes. Volume 1: Facility description and summary data report

    International Nuclear Information System (INIS)

    Oden, L.L.; O'Connor, W.K.; Turner, P.C.; Soelberg, N.R.; Anderson, G.L.

    1993-01-01

    This report presents field results and raw data from the Buried Waste Integrated Demonstration (BWID) Arc Melter Vitrification Project Phase 1 baseline test series conducted by the Idaho National Engineering Laboratory (INEL) in cooperation with the U.S. Bureau of Mines (USBM). The baseline test series was conducted using the electric arc melter facility at the USBM Albany Research Center in Albany, Oregon. Five different surrogate waste feed mixtures were tested that simulated thermally-oxidized, buried, TRU-contaminated, mixed wastes and soils present at the INEL. The USBM Arc Furnace Integrated Waste Processing Test Facility includes a continuous feed system, the arc melting furnace, an offgas control system, and utilities. The melter is a sealed, 3-phase alternating current (ac) furnace approximately 2 m high and 1.3 m wide. The furnace has a capacity of 1 metric ton of steel and can process as much as 1,500 lb/h of soil-type waste materials. The surrogate feed materials included five mixtures designed to simulate incinerated TRU-contaminated buried waste materials mixed with INEL soil. Process samples, melter system operations data and offgas composition data were obtained during the baseline tests to evaluate the melter performance and meet test objectives. Samples and data gathered during this program included (a) automatically and manually logged melter systems operations data, (b) process samples of slag, metal and fume solids, and (c) offgas composition, temperature, velocity, flowrate, moisture content, particulate loading and metals content. This report consists of 2 volumes: Volume I summarizes the baseline test operations. It includes an executive summary, system and facility description, review of the surrogate waste mixtures, and a description of the baseline test activities, measurements, and sample collection. Volume II contains the raw test data and sample analyses from samples collected during the baseline tests

  19. Preliminary Study of Mixing of Plasma Species in a Hybrid-Stabilized Argon-Water Electric Arc

    Czech Academy of Sciences Publication Activity Database

    Jeništa, Jiří; Takana, H.; Uehara, S.; Nishiyama, H.; Murphy, A.B.; Bartlová, M.; Aubrecht, V.

    2015-01-01

    Roč. 2, č. 3 (2015), s. 316-319 ISSN 2336-2626. [Symposium on Physics of Switching Arc/21./. Nové Město na Moravě, 07.09.2015-11.09.2015] R&D Project s: GA ČR(CZ) GA15-19444S Institutional support: RVO:61389021 Keywords : arc discharge * combined diffusion coefficients * inhomogeneous mixing * mass fraction Subject RIV: BL - Plasma and Gas Discharge Physics https://www.vutbr.cz/www_base/vutdisk.php?i=36809a9aa

  20. FORMATION OF THE INITIAL DISTRIBUTION OF PLASMA COMPONENTS ON THE PHASE PLANE OF LARGE PARTICLES METHOD IN ELECTRIC ARC SYNTHESIS CNS

    Directory of Open Access Journals (Sweden)

    G. V. Abramov

    2014-01-01

    Full Text Available The article deals with the modeling of charged particles in a multicomponent plasma of electric arc discharge with binary collisions in the synthesis of carbon nanostructures (CNS. One of the common methods of obtaining the quality of fullerenes and nanotubes is arc synthesis under inert gas (helium. The determination of the necessary conditions and the mechanism of formation of carbon clusters in the plasma forming set CNS will more effectively and efficiently manage this process. Feature of the problem is that in a plasma arc discharge is a large number of particle interactions and on the cathode surface. Due to the high temperatures and high energy concentration in plasma detailed experimental investigation difficult to carry out. With the aim of avoiding difficult and costly physical experiments developed numerical methods for the analysis of plasma processes. In this article to solve a system of equations of Maxwell - Boltzmann basis for the authors had taken the method of large particles, which reduces the amount of computation and reduce the demands on computing resources. The authors cites the general design scheme of the large particles, and the algorithm of particle distribution of a multicomponent plasma in the phase plane at the initial time. In conclusion, the author argues that the results in the future will define the zone satisfies the energy conditions, the probability of formation of a plasma cluster groups of carbon involved in the synthesis of the CNS.

  1. production of manual arc welding electrodes with local raw materials

    African Journals Online (AJOL)

    CHUKSSUCCESS 4 LOVE

    Manual arc welding using flux coated electrodes is carried out by producing an electric arc between ... major objectives: to form fusible slags, to stabilize the arc and to produce an inert gas shielding ... Current fusion welding techniques rely.

  2. Development and Testing of an Experimental Polysensory Instructional System for Teaching Electric Arc Welding Processes. Report No. 24. Final Report.

    Science.gov (United States)

    Sergeant, Harold A.

    The population of the study consisted of 15 high school industrial arts students, 10 freshman and sophomore college students, and 10 adults. A polysensory, self-pacing instructional system was developed which included (1) pretests and post tests, (2) a general instruction book, (3) equipment to practice arc welding, (4) programed instruction…

  3. Steam generators and furnaces

    Energy Technology Data Exchange (ETDEWEB)

    Swoboda, E

    1978-04-01

    The documents published in 1977 in the field of steam generators for conventional thermal power plants are classified according to the following subjects: power industry and number of power plants, planning and operation, design and construction, furnaces, environmental effects, dirt accumulation and corrosion, conservation and scouring, control and automation, fundamental research, and materials.

  4. Emission spectroscopy for coal-fired cyclone furnace diagnostics

    Energy Technology Data Exchange (ETDEWEB)

    Wehrmeyer, J.A.; Boll, D.E.; Smith, R. [Vanderbilt University, Nashville, TN (United States). Dept. of Mechanical Engineering

    2003-08-01

    Using a spectrograph and charge-coupled device (CCD) camera, ultraviolet and visible light emission spectra were obtained from a coal-burning electric utility's cyclone furnaces operating at either fuel-rich or fuel-lean conditions. The aim of this effort is to identify light emission signals that can be related to a cyclone furnace's operating condition in order to adjust its air/fuel ratio to minimize pollutant production. Emission spectra at the burner and outlet ends of cyclone furnaces were obtained. Spectra from all cyclone burners show emission lines for the trace elements Li, Na, K, and Rb, as well as the molecular species OH and CaOH. The Ca emission line is detected at the burner end of both the fuel-rich and fuellean cyclone furnaces but is not detected at the outlet ends of either furnace type. Along with the disappearance of Ca is a concomitant increase in the CaOH signal at the outlet end of both types of furnaces. The OH signal strength is in general stronger when viewing at the burner end rather than the exhaust end of both the fuel-rich and fuel-lean cyclone furnaces, probably due to high, non-equilibrium amounts of OH present inside the furnace. Only one molecular species was detected that could be used as a measure of air/fuel ratio: MgOH. It was detected at the burner end of fuel-rich cyclone furnaces but not detected in fuel-lean cyclone furnaces. More direct markers of air/fuel ratio, such as CO and 02 emission, were not detected, probably due to the generally weak nature of molecular emission relative to ambient blackbody emission present in the cyclone furnaces, even at ultraviolet wavelengths.

  5. Use of refractory chromites for obtaining fluxes amassed employed in submerged arc welding (SAW); Empleo de cromitas refractarias par la obtencion de fundentes aglomerados utilizados en la soldadura automatica por arco sumegido (SAW)

    Energy Technology Data Exchange (ETDEWEB)

    Perdomo-Gonzalez, L.; Quintana-Puchol, R.; Cruz-Crespo, A.; Castellanos-Estupinan, J.; Garcia-Sanchez, L. L.; Formoso-Prego, A.; Cores-Sanchez, A.

    2003-07-01

    In the present work high carbon ferrochrome (load ferrochrome) and slags are obtained, starting from the metallurgic reductive processing of refractory chromites. The obtaining of alloys and slags is studied using an experiment design based in the relationships among components. The chemical compositions of alloys and slags guarantee their application for the conformation of alloys loads and matrix fluxes amassed for the superficial filling by means of submerged arc welding (SAW). The melting-reduction process is carried out in an electric arc furnace. (Author) 16 refs.

  6. Driven Motion and Instability of an Atmospheric Pressure Arc

    International Nuclear Information System (INIS)

    Max Karasik

    1999-01-01

    Atmospheric pressure arcs are used extensively in applications such as welding and metallurgy. However, comparatively little is known of the physics of such arcs in external magnetic fields and the mechanisms of the instabilities present. In order to address questions of equilibrium and stability of such arcs, an experimental arc furnace is constructed and operated in air with graphite cathode and steel anode at currents 100-250 A. The arc is diagnosed with a gated intensified camera and a collimated photodiode array, as well as fast voltage and current probes

  7. Driven Motion and Instability of an Atmospheric Pressure Arc

    Energy Technology Data Exchange (ETDEWEB)

    Max Karasik

    1999-12-01

    Atmospheric pressure arcs are used extensively in applications such as welding and metallurgy. However, comparatively little is known of the physics of such arcs in external magnetic fields and the mechanisms of the instabilities present. In order to address questions of equilibrium and stability of such arcs, an experimental arc furnace is constructed and operated in air with graphite cathode and steel anode at currents 100-250 A. The arc is diagnosed with a gated intensified camera and a collimated photodiode array, as well as fast voltage and current probes.

  8. The investigation of movement dynamics of an AC electric arc attachment along the working surface of a hollow cylindrical electrode under the action of gas-dynamic and electromagnetic forces

    International Nuclear Information System (INIS)

    Surov, A V; Popov, S D; Serba, E O; Nakonechny, G V; Spodobin, V A; Ovchinnikov, R V; Kumkova, I I; Shabalin, S A

    2012-01-01

    Stationary electric arc alternating current plasma torches are used today for realization of plasma chemical technologies requiring relatively high energy input. Waste treatment is one these directions. The paper reports on experiment results directed towards the increase in the lifetime characteristics of electrode units of the powerful high-voltage electric-arc AC plasma torches. The solution to the problem of obtainment the uniform wear of a copper hollow cylindrical electrode achieved by the controlled movement of the arc attachment along the working surface was offered. Organization of gas supply in the near electrode area and application of alternating magnetic field ensured movement of arc attachment along the surface with average speed from 2 to 14 m/s. Arc current was about 47 A and 84 A, gas flow rate in near electrode area was about 5 and 4.5 g/s. Due to researches on the experimental prototype of a hollow cylindrical electrode, the erosion of its material reached only 3 μg/C, that enables production of the electrode assembly with life time above 1000 hours at currents in the arc up to 100–200 A.

  9. Study of the transfer efficiency of alloyed elements in fluxes during submerged arc welding process

    International Nuclear Information System (INIS)

    Quintana, R.; Cruz, A.; Perdomo, L.; Castellanos, G.; Garcia, L. L.; Formoso, A.; Cores, A.

    2003-01-01

    It is assessed the transfer of chromium, manganese and carbon of different agglomerate fluxes constituted by 18.75% of alloyed load and 81.25% of matrix during the SAW process (submerge Arc Welding). A vitreous basic matrix corresponding to the system SiO 2 -Al 2 O 3 -(CaO+MgO) was obtained from minerals by fusion in the electric arc furnace. The current proportions of the alloyed load components (FeCr, FeMn and graphite) were carried out using a McLean Anderson experiment design. The corresponding fluxes to each experimental point were obtained by granulation with liquid glass;afterwards, their transfer coefficient for a given regimen of welding was determined. The transfer coefficients were calculated by means of a formula based on the laws of mass conservation and of distribution. (Author) 17 refs

  10. Research report for fiscal 1998. Basic research for promoting joint implementation of energy use rationalization in Chinese steel industry (examination of introduction of scrap preheating system for electric furnaces); 1998 nendo chosa hokokusho. Chugoku tekkogyo ni okeru energy no shiyo gorika (denkiro scrap yonetsu system donyu kento)

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    1999-03-01

    Investigations are conducted on a project of introducing a scrap preheating system based on the central insertion movable shaft design into China's electric furnaces for the sake of energy saving and global warming gas reduction. Of the electric furnaces numbering approximately 3400 now in operation in China, most are small and antiquated, and are extremely low in energy efficiency when in operation. The percentage of electricity supplied by coal-fired facilities is high, and this causes the CO2 reduction problem. Investigations are conducted into four steel mills operating electric furnaces, and examinations are made on the applicability of a preheating system, which is the ultimate batch system developed by Nippon Steel Corporation. Studies are conducted for Wuyang Iron and Steel Co., Ltd., Tianjin Steel Pipe Co., Ltd., Budong Iron and Steel Co., Ltd., and Shanghai Five Steel Co., Ltd., and it is found that greenhouse gas will be reduced by 31,000 tons, 21,000 tons, 13,000 tons, and 11,000-tons at the said mills, respectively. It is learned that the cost to be invested will be retrieved in approximately 2.5 years, 2.8 years, 7.7 years, and 8.0 years, respectively. It is concluded that Shanghai Budong Iron and Steel (Group) Co., Ltd., is the best candidate to be equipped with the above-said system. (NEDO)

  11. Correlation methods in cutting arcs

    Energy Technology Data Exchange (ETDEWEB)

    Prevosto, L; Kelly, H, E-mail: prevosto@waycom.com.ar [Grupo de Descargas Electricas, Departamento Ing. Electromecanica, Universidad Tecnologica Nacional, Regional Venado Tuerto, Laprida 651, Venado Tuerto (2600), Santa Fe (Argentina)

    2011-05-01

    The present work applies similarity theory to the plasma emanating from transferred arc, gas-vortex stabilized plasma cutting torches, to analyze the existing correlation between the arc temperature and the physical parameters of such torches. It has been found that the enthalpy number significantly influence the temperature of the electric arc. The obtained correlation shows an average deviation of 3% from the temperature data points. Such correlation can be used, for instance, to predict changes in the peak value of the arc temperature at the nozzle exit of a geometrically similar cutting torch due to changes in its operation parameters.

  12. Correlation methods in cutting arcs

    International Nuclear Information System (INIS)

    Prevosto, L; Kelly, H

    2011-01-01

    The present work applies similarity theory to the plasma emanating from transferred arc, gas-vortex stabilized plasma cutting torches, to analyze the existing correlation between the arc temperature and the physical parameters of such torches. It has been found that the enthalpy number significantly influence the temperature of the electric arc. The obtained correlation shows an average deviation of 3% from the temperature data points. Such correlation can be used, for instance, to predict changes in the peak value of the arc temperature at the nozzle exit of a geometrically similar cutting torch due to changes in its operation parameters.

  13. Effect of the weld thermal cycles by the modified indirect electric arc (MIEA) on the mechanical properties of the AA6061-T6 alloy

    International Nuclear Information System (INIS)

    Ambriz, R. A.; Barrera, G.; Garcia, R.; Lopez, V. H.

    2009-01-01

    Results of temperature measurements during welding of 12.7 mm thick AA6061-T6 alloy plates by modified indirect electric arc (MIEA) are presented. This study describes the thermal cycles of the heat affected zone (HAZ) and also in the fusion zone. Depending upon the position of the transducers, the maximum temperatures measured in the HAZ range from 308 to 693 degree centigrade, these measurements were related with the tensile test results, and the failure zone reported previously by the authors. It was observed that, there is a decrease in the mechanical strength of the welded joints, due to the microstructural changes suffered by AA6061-T6 alloy in which formation of the βoccurs according to the TTT transformation diagram. The inherent cooling conditions of the weld pool observed for the MIEA technique (only one pass of welding), have permitted to establish the characteristics of solidification and microstructure for a specific cooling rate. (Author) 24 refs

  14. Description and operating performance of a parallel-rail electric-arc system with helium driver gas for the Langley 6-inch expansion tube

    Science.gov (United States)

    Moore, J. A.

    1976-01-01

    A parallel-rail arc-discharge system to heat and pressurize the initial helium driver gas of the Langley 6-inch expansion tube is described. This system was designed for a 2.44-m-long driver vessel rated at 138 MPa, with a distance between rails of 20.3 cm. Electric energy was obtained from a capacitor storage system rated at 12,000 V with a maximum energy of 5 MJ. Tests were performed over a range of energy from 1.74 MJ to the maximum value. The operating experience and system performance are discussed, along with results from a limited number of expansion-tube tests with air and carbon dioxide as test gases.

  15. ARC Operations

    Science.gov (United States)

    coordination on a regular basis. The overall ARC organizational structure is shown below. Organizational Structure Dynamics and Control of Vehicles Human Centered Modeling and Simulation High Performance

  16. Study of gliding arc discharge plasma

    International Nuclear Information System (INIS)

    Yang Chi; Lin Lie; Wu Bin

    2006-01-01

    The electric parameters change during discharge is studied and the relationship between non-equilibrium degree and parameters is discussed for gliding arc discharges. Using two-channel model, the rules of arc moving due to effect of the airflow is simulated. The numerical simulation results can help analyzing the generation mechanism of gliding arc non-equilibrium plasma. (authors)

  17. Mixture of industrial waste oxidized titanium and reduced slag from electric furnace used as hydraulic material. Denkiro kangen slug to sanka titan kogyo haikibutsu no kongobutsu no suinan zairyo to shiteno riyo

    Energy Technology Data Exchange (ETDEWEB)

    Honda, A [Osaka City University, Osaka (Japan). Faculty of Engineering; Kuwayama, T [Daido Institute of Technology, Nagoya (Japan); Yamada, M; Ikezaki, H [Osaka City University, Osaka (Japan). Faculty of Engineering

    1990-10-29

    Slag released from an electric furnace consists mainly of waste steel. There are two types of slag, namely, oxidized slag and reduced slag. Reduced slag, which is generally in the form of powder, is difficult to recycle as compared with oxidized slag. However, with a hydraulicity, some reduced slag is expected to be useful as hydraulic material. Test results obtained here show that the hydraulic properties of reduced slag powder can be improved by mixing it with gypsum and that the resultant mixture can serve to improve the prooperties of soft clay. Another study is made to determine the potential, as hydraulic material, of mixtures of reduced slag powder and waste gypsum material with a high gypsum content released from an oxidized titanium production process. The hydraulicity is found to develop as a result of the formation of a hydrate of calcium aluminate which is contained in the slag. Addition of water to the hydrate and gypsum cause the formation of ettringite, leading to an increased uniaxial compressive strength. These findings indicate that the above-mentioned mixture can be useful to improve the hydraulic properties of coal ash to be disposed of at landfill sites. 5 refs., 5 figs., 1 tab.

  18. Equilibrium motion of quict auroral arcs

    International Nuclear Information System (INIS)

    Lyatskij, V.B.; Leont'ev, S.V.

    1981-01-01

    Ionospheric plasma convection across auroral arc is investigated. It is shown that the existence of plasma area of increased concentration adjoining arc results not only from the arc but also is a factor supporting its existence. Under stable conditions the arc and plasma zone connected to it will move at a velocity different from a velocity of plasma convection. Arc velocity will be higher or lower as compared with convection velocity depending on arc orientation relative to an external electric field. At that the plasma zone is located either in front of or behind aurora polaris [ru

  19. Fundamentals of electroheat electrical technologies for process heating

    CERN Document Server

    Lupi, Sergio

    2017-01-01

    This book provides a comprehensive overview of the main electrical technologies for process heating, which tend to be treated separately in specialized books. Individual chapters focus on heat transfer, electromagnetic fields in electro-technologies, arc furnaces, resistance furnaces, direct resistance heating, induction heating, and high-frequency and microwave heating. The authors highlight those topics of greatest relevance to a wide-ranging teaching program, and at the same time offer a detailed review of the main applications of the various technologies. The content represents a synthesis of the extensive knowledge and experience that the authors have accumulated while researching and teaching at the University of Padua’s Engineering Faculty. This text on industrial electroheating technologies is a valuable resource not only for students of industrial, electrical, chemical, and material science engineering, but also for engineers, technicians and others involved in the application of electroheating and...

  20. The roots of the Swiss hydroelectric success: the electric lighting introduction in the Lemanic arc (1881-1891)

    International Nuclear Information System (INIS)

    Humair, Cedric

    2005-01-01

    The development of a Swiss electro-technology industry was based on the rapid transfer of the Edison model associating one central power plant to electricity distribution through lighting. Market dynamism allowed Switzerland to take the lead in the European countries. But such a success can be explained only by engineers' skills, notably in the hydraulic field, as well as by the quality of the social networks. Indeed, political leaders had to put all their weight behind it to overcome reluctance shown by gas companies. Technically speaking, mastering pressure water networks will favour the increasing use of electricity. And in the tourism industry, electricity found a market that turned out to be immediately profitable

  1. Arc plasma incineration of surrogate radioactive wastes

    International Nuclear Information System (INIS)

    Girold, C.; Cartier, R.; Taupiac, J.P.; Vandensteendam, C.; Baronnet, J.M.

    1995-01-01

    The aim of this presentation is to demonstrate the feasibility to substitute a single plasma reactor, where the arc is transferred on a melt glass bath, for several steps in an existing nuclear technological wastes incinerator. The incineration of wastes, the produced gas treatment and the vitrification of ashes issued from waste incineration are the three simultaneous functions of this new kind of reactor. The three steps of the work are described: first, post-combustion in an oxygen plasma of gases generated from the waste pyrolysis, then, vitrification of ashes from the calcination of wastes in the transferred plasma furnace and finally, incineration/vitrification of wastes in the same furnace

  2. Electrical resistivity of ceramic-metal composite materials in the percolation region: application in crucibles for induction furnaces; Resistividade eletrica de materiais compositos do tipo ceramica-metal na regiao de percolacao: aplicacao em cadinhos para fornos de inducao

    Energy Technology Data Exchange (ETDEWEB)

    Sene, Frank Ferrer

    1997-07-01

    Ceramic composite materials were produced by mixing powders of Partially Stabilized (PSZ) with titanium, niobium or nickel, and cristobalite with titanium. Pellets were produced by uniaxially pressing the material followed by cold isostatic pressing and finally sintering at 1600 deg C for 1,5 hours in argon. The metal content was varied in the range of 0-40 volume percent (v/o). Electrical resistivity measurements were performed in the temperature range of 25 - 700 deg C. Samples containing metallic inclusions above 25 v/o show the predominance of electronic type conducting. For samples with metallic inclusion below 25 v/o, a typically ionic conduction behavior has been observed. PSZ-Ti and PSZ-Ni samples containing 25 v/o of metallic inclusions show an insulator - conductor transition in a given temperature range. Cristobalite samples containing 30 v/o of titanium show a conductor - insulator transition also in a specific temperature range. Tests performed in an induction furnace showed that samples containing metallic inclusions above 25 v/o had self-heated when exposed to electro magnetic fields in the range of radio frequency (r.f.) Crucibles of PSZ-Ti were made by slip casting followed by sintering at 1600 deg C for 1.5 hours in argon. These crucibles were exposed to electromagnetic fields in the r.f. range and the maximum temperature reached was 1350 deg C. Microstructure characterization was performed on those materials by X-ray diffraction, EDS, optical and scanning electron microscopy. (author)

  3. Modeling and Simulation of Low Voltage Arcs

    NARCIS (Netherlands)

    Ghezzi, L.; Balestrero, A.

    2010-01-01

    Modeling and Simulation of Low Voltage Arcs is an attempt to improve the physical understanding, mathematical modeling and numerical simulation of the electric arcs that are found during current interruptions in low voltage circuit breakers. An empirical description is gained by refined electrical

  4. Modeling of thermal plasma arc technology FY 1994 report

    International Nuclear Information System (INIS)

    Hawkes, G.L.; Nguyen, H.D.; Paik, S.; McKellar, M.G.

    1995-03-01

    The thermal plasma arc process is under consideration to thermally treat hazardous and radioactive waste. A computer model for the thermal plasma arc technology was designed as a tool to aid in the development and use of the plasma arc-Joule beating process. The value of this computer model is to: (a) aid in understanding the plasma arc-Joule beating process as applied to buried waste or exhumed buried waste, (b) help design melter geometry and electrode configuration, (c) calculate the process capability of vitrifying waste (i.e., tons/hour), (d) develop efficient plasma and melter operating conditions to optimize the process and/or reduce safety hazards, (e) calculate chemical reactions during treatment of waste to track chemical composition of off-gas products, and composition of final vitrified waste form and (f) help compare the designs of different plasma-arc facilities. A steady-state model of a two-dimensional axisymmetric transferred plasma arc has been developed and validated. A parametric analysis was performed that studied the effects of arc length, plasma gas composition, and input power on the temperatures and velocity profiles of the slag and plasma gas. A two-dimensional transient thermo-fluid model of the US Bureau of Mines plasma arc melter has been developed. This model includes the growth of a slag pool. The thermo-fluid model is used to predict the temperature and pressure fields within a plasma arc furnace. An analysis was performed to determine the effects of a molten metal pool on the temperature, velocity, and voltage fields within the slag. A robust and accurate model for the chemical equilibrium calculations has been selected to determine chemical composition of final waste form and off-gas based on the temperatures and pressures within the plasma-arc furnace. A chemical database has been selected. The database is based on the materials to be processed in the plasma arc furnaces

  5. Observation and interpretation of particle and electric field measurements inside and adjacent to an active auroral arc

    International Nuclear Information System (INIS)

    Carlson, C.W.; Kelley, M.C.

    1977-01-01

    A Javelin sounding rocket instrumented to measure electric fields, energetic particles, and suprathermal electrons was flown across an auroral display in the late expansion phase of a substorm. Four distinct regions of fields and particles were interpreted here in light of our present understanding of auroral dynamics.r of 10 and resemble fluxes mesured in the equatorial plane during the expansion phase. The hard fluxes in the equatorward zone are further energized and may act as a source for the outer radiation belt as inward convection further energizes them

  6. Heat treatment of nuclear reactor pump part in integrated furnace facility

    International Nuclear Information System (INIS)

    Anon.

    1983-01-01

    A flexible heat treating system is meeting strict work specifications while accommodating the production flow pattern requirements and floor space needs of Advanced Metal Treating, Inc., Butler, Wis. Modular design and appropriate furnace configurations allow realization of the most efficient heat treat processing and energy use in a relatively small production area. The totally-integrated system (Pacemaker--manufactured by Lindberg, A Unit of General Signal, Chicago) consists of an electric integral-quench furnace with companion draw furnaces, washer unit and a material transfer car. With its one-side, inout configuration, the furnace operates with a minimum of drawing and washing equipment. The integral-quench furnace has a work chamber dimension of 30 by 48 by 30 inches (76.2 x 122 x 76.2 cm). The firm has two of these units, plus three in-out draw furnaces, one washer, one transfer car and two endothermic gas generators

  7. Structural, mechanical, electrical and wetting properties of ZrNx films deposited by Ar/N2 vacuum arc discharge: Effect of nitrogen partial pressure

    Science.gov (United States)

    Abdallah, B.; Naddaf, M.; A-Kharroub, M.

    2013-03-01

    Non-stiochiometric zirconium nitride (ZrNx) thin films have been deposited on silicon substrates by vacuum arc discharge of (N2 + Ar) gas mixtures at different N2 partial pressure ratio. The microstructure, mechanical, electrical and wetting properties of these films are studied by means of X-ray diffraction (XRD), micro-Raman spectroscopy, Rutherford back scattering (RBS) technique, conventional micro-hardness testing, electrical resistivity, atomic force microscopy (AFM) and contact angle (CA) measurements. RBS results and analysis show that the (N/Zr) ratio in the film increases with increasing the N2 partial pressure. A ZrNx film with (Zr/N) ratio in the vicinity of stoichiometric ZrN is obtained at N2 partial pressure of 10%. XRD and Raman results indicate that all deposited films have strained cubic crystal phase of ZrN, regardless of the N2 partial pressure. On increasing the N2 partial pressure, the relative intensity of (1 1 1) orientation with respect to (2 0 0) orientation is seen to decrease. The effect of N2 partial pressure on micro-hardness and the resistivity of the deposited film is revealed and correlated to the alteration of grain size, crystallographic texture, stoichiometry and residual stress developed in the film. In particular, it is found that residual stress and nitrogen incorporation in the film play crucial role in the alteration of micro-hardness and resistivity respectively. In addition, CA and AFM results demonstrate that as N2 partial pressure increases, both the surface hydrophobicity and roughness of the deposited film increase, leading to a significant decrease in the film surface free energy (SFE).

  8. Fossil fuel furnace reactor

    Science.gov (United States)

    Parkinson, William J.

    1987-01-01

    A fossil fuel furnace reactor is provided for simulating a continuous processing plant with a batch reactor. An internal reaction vessel contains a batch of shale oil, with the vessel having a relatively thin wall thickness for a heat transfer rate effective to simulate a process temperature history in the selected continuous processing plant. A heater jacket is disposed about the reactor vessel and defines a number of independent controllable temperature zones axially spaced along the reaction vessel. Each temperature zone can be energized to simulate a time-temperature history of process material through the continuous plant. A pressure vessel contains both the heater jacket and the reaction vessel at an operating pressure functionally selected to simulate the continuous processing plant. The process yield from the oil shale may be used as feedback information to software simulating operation of the continuous plant to provide operating parameters, i.e., temperature profiles, ambient atmosphere, operating pressure, material feed rates, etc., for simulation in the batch reactor.

  9. Furnace for treating bituminous material

    Energy Technology Data Exchange (ETDEWEB)

    Klotzer, M

    1922-04-28

    A furnace with saw-teeth-like profiled hearth, which by means of a kind of shaking slide executes a backward and forward motion, for carrying out the process according to Patent 422,391. It is characterized in that the stroke of the hearth moving in the furnace is smaller than the length of the profile tooth and the height of the feed is held less than the tooth height.

  10. Disposal of low-level radioactive wastes. Plasma furnace for the treatment of low-level radwastes in Switzerland. Plasma furnace for the treatment of low-level radwastes in Switzerland

    International Nuclear Information System (INIS)

    Hoffelner, W.; Mueller, T.; Fuenfschilling, M.R.; Jacobi, A.; Eschenbach, R.; Lutz, H.R.; Vuilleumier, C.

    1994-01-01

    The treatment method to be applied consists of thermal decomposition and vitrification. The facility to be constructed at the Zwilag is a plasma-arc furnace, and planning activities are heading towards the final phase. There will be only this one facility for treating in only one process step solid, mixed wastes, liquid wastes, sludges, metals, and inorganic wastes, producing vitrified waste packages ready for ultimate storage as 200-l waste drums. The main features of the plasma-arc furnace are explained. (orig./HP) [de

  11. Graphite electrode DC arc technology program for buried waste treatment

    International Nuclear Information System (INIS)

    Wittle, J.K.; Hamilton, R.A.; Cohn, D.R.; Woskov, P.P.; Thomas, P.; Surma, J.E.; Titus, C.H.

    1994-01-01

    The goal of the program is to apply EPI's Arc Furnace to the processing of Subsurface Disposal Area (SDA) waste from Idaho National Engineering Laboratory. This is being facilitated through the Department of Energy's Buried Waste Integrated Demonstration (BWID) program. A second objective is to apply the diagnostics capability of MIT's Plasma Fusion Center to the understanding of the high temperature processes taking place in the furnace. This diagnostics technology has promise for being applicable in other thermal treatment processes. The program has two parts, a test series in an engineering-scale DC arc furnace which was conducted in an EPI furnace installed at the Plasma Fusion Center and a pilot-scale unit which is under construction at MIT. This pilot-scale furnace will be capable of operating in a continuous feed and continuous tap mode. Included in this work is the development and implementation of diagnostics to evaluate high temperature processes such as DC arc technology. This technology can be used as an effective stabilization process for Superfund wastes

  12. Effect of electric arc, gas oxygen torch and induction melting techniques on the marginal accuracy of cast base-metal and noble metal-ceramic crowns.

    Science.gov (United States)

    Gómez-Cogolludo, Pablo; Castillo-Oyagüe, Raquel; Lynch, Christopher D; Suárez-García, María-Jesús

    2013-09-01

    The aim of this study was to identify the most appropriate alloy composition and melting technique by evaluating the marginal accuracy of cast metal-ceramic crowns. Seventy standardised stainless-steel abutments were prepared to receive metal-ceramic crowns and were randomly divided into four alloy groups: Group 1: palladium-gold (Pd-Au), Group 2: nickel-chromium-titanium (Ni-Cr-Ti), Group 3: nickel-chromium (Ni-Cr) and Group 4: titanium (Ti). Groups 1, 2 and 3 were in turn subdivided to be melted and cast using: (a) gas oxygen torch and centrifugal casting machine (TC) or (b) induction and centrifugal casting machine (IC). Group 4 was melted and cast using electric arc and vacuum/pressure machine (EV). All of the metal-ceramic crowns were luted with glass-ionomer cement. The marginal fit was measured under an optical microscope before and after cementation using image analysis software. All data was subjected to two-way analysis of variance (ANOVA). Duncan's multiple range test was run for post-hoc comparisons. The Student's t-test was used to investigate the influence of cementation (α=0.05). Uncemented Pd-Au/TC samples achieved the best marginal adaptation, while the worst fit corresponded to the luted Ti/EV crowns. Pd-Au/TC, Ni-Cr and Ti restorations demonstrated significantly increased misfit after cementation. The Ni-Cr-Ti alloy was the most predictable in terms of differences in misfit when either torch or induction was applied before or after cementation. Cemented titanium crowns exceeded the clinically acceptable limit of 120μm. The combination of alloy composition, melting technique, casting method and luting process influences the vertical seal of cast metal-ceramic crowns. An accurate use of the gas oxygen torch may overcome the results attained with the induction system concerning the marginal adaptation of fixed dental prostheses. Copyright © 2013 Elsevier Ltd. All rights reserved.

  13. The electrical, elemental, optical, and surface properties of Si-doped ZnO thin films prepared by thermionic vacuum arc

    Science.gov (United States)

    Mohammadigharehbagh, Reza; Özen, Soner; Yudar, Hafizittin Hakan; Pat, Suat; Korkmaz, Şadan

    2017-09-01

    The purpose of this work is to study the properties of Si-doped ZnO (SZO) thin films, which were prepared using the non-reactive thermionic vacuum arc technique. The analysis of the elemental, optical, and surface properties of ZnO:Si thin films was carried out using energy dispersive x-ray spectroscopy, UV-VIS spectrophotometry, atomic force microscopy, and scanning electron microscopy, respectively. The current-voltage measurement was employed in order to study the electrical properties of the films. The effect of Si doping on the physical properties of ZnO films was investigated. The film thicknesses were measured as 55 and 35 nm for glass and PET substrates, respectively. It was clearly observed from the x-ray diffraction results that the Si and ZnO peaks were present in the coated SZO films for all samples. The morphological studies showed that the deposited surfaces are homogenous, dense, and have a uniform surface, with the existence of some cracks only on the glass substrate. The elemental composition has confirmed the existence of Zn, Si, and O elements within the prepared films. Using a UV-VIS spectrophotometer, the optical parameters such as transmittance, absorbance, refractive index, and reflectance were calculated. It should be noted that the transparency and refractive indices obtained from the measurements decrease with increasing Si concentration. The obtained optical bandgap values using transmittance spectra were determined to be 3.74 and 3.84 eV for the glass and PET substrates, respectively. An increase in the bandgap results demonstrates that the Si doping concentration is comparable to the pure ZnO thin films. The current versus voltage curves revealed the ohmic nature of the films. Subsequently, the development and fabrication of excellent transparent conducting electrodes enabled the appropriate use of Si-doped ZnO thin films.

  14. Synthesis of aluminium nanoparticles by arc evaporation of an ...

    Indian Academy of Sciences (India)

    Administrator

    Abstract. Aluminium nanoparticles (Al Nps) are synthesized using arc discharge method by applying direct current between aluminium electrodes in liquid environment without any use of vacuum equipment, heat exchangers, high temperatures furnaces and inert gases. After synthesis of Al Nps, in situ coating process on.

  15. Magnetic Method to Characterize the Current Densities in Breaker Arc

    International Nuclear Information System (INIS)

    Machkour, Nadia

    2005-01-01

    The purpose of this research was to use magnetic induction measurements from a low voltage breaker arc, to reconstruct the arc's current density. The measurements were made using Hall effect sensors, which were placed close to, but outside the breaking device. The arc was modelled as a rectangular current sheet, composed of a mix of threadlike current segments and with a current density varying across the propagation direction. We found the magnetic induction of the arc is a convolution product of the current density, and a function depending on the breaker geometry and arc model. Using deconvolution methods, the current density in the electric arc was determined.The method is used to study the arc behavior into the breaker device. Notably, position, arc size, and electric conductivity could all be determined, and then used to characterize the arc mode, diffuse or concentrated, and study the condition of its mode changing

  16. Graphite electrode dc arc technology development for treatment of buried wastes

    International Nuclear Information System (INIS)

    Surma, J.E.; Cohn, D.R.; Smatlak, D.L.; Thomas, P.; Woskov, P.P.

    1993-02-01

    A ''National Laboratory-University-Industrial'' three-way partnership has been established between the Pacific Northwest Laboratory (PNL), Massachusetts Institute of Technology (MIT), and Electro-Pyrolysis, Inc. (EPI) to develop graphite electrode DC arc technology for the treatment of buried wastes. This paper outlines the PNL-MIT-EPI program describing a series of engineering-scale DC arc furnace tests conducted in an EPI furnace at the Plasma Fusion Center at MIT, and a description of the second phase of this program involving the design, fabrication, and testing of a pilot-scale DC arc furnace. Included in this work is the development and implementation of diagnostics to evaluate and optimize high temperature thermal processes such as the DC arc technology

  17. Development of vacuum brazing furnace

    International Nuclear Information System (INIS)

    Singh, Rajvir; Yedle, Kamlesh; Jain, A.K.

    2005-01-01

    In joining of components where welding process is not possible brazing processes are employed. Value added components, high quality RF systems, UHV components of high energy accelerators, carbide tools etc. are produced using different types of brazing methods. Furnace brazing under vacuum atmosphere is the most popular and well accepted method for production of the above mentioned components and systems. For carrying out vacuum brazing successfully it is essential to have a vacuum brazing furnace with latest features of modern vacuum brazing technology. A vacuum brazing furnace has been developed and installed for carrying out brazing of components of copper, stainless steel and components made of dissimilar metals/materials. The above furnace has been designed to accommodate jobs of 700mm diameter x 2000mm long sizes with job weight of 500kgs up to a maximum temperature of 1250 degC at a vacuum of 5 x 10 -5 Torr. Oil diffusion pumping system with a combination of rotary and mechanical booster pump have been employed for obtaining vacuum. Molybdenum heating elements, radiation shield of molybdenum and Stainless Steel Grade 304 have been used. The above furnace is computer controlled with manual over ride facility. PLC and Pentium PC are integrated together to maneuver steps of operation and safety interlocks of the system. Closed loop water supply provides cooling to the system. The installation of the above system is in final stage of completion and it will be ready for use in next few months time. This paper presents insights of design and fabrication of a modern vacuum brazing furnace and its sub-system. (author)

  18. INFLUENCE OF CHEMICAL COMPOUNDS ON THE FORMING OF WELDING ARC

    Directory of Open Access Journals (Sweden)

    I. О. Vakulenko

    2014-10-01

    Full Text Available Purpose. The purpose of work is a comparative analysis of chemical compounds influence on the process of forming arc welding and condition of its burning. Methodology. A wire with diameter 3 mm of low carbon steel with contain of carbon 0.15% was material for electrode. As chemical compounds, which determine the terms of arc welding forming the following compounds were used: kaolin; CaCO3 with admixtures of gypsum up to 60%; SiO2 and Fe − Si with the iron concentration up to 50%. Researches were conducted using the direct electric current and arc of reverse polarity. As a source of electric current a welding transformer of type PSO-500n was used. On the special stand initial gap between the electrode and metal plate was 1-1.5 mm. The inter electrode space was filled with the probed chemical compound and the electric arc was formed. At the moment of arc forming the values of electric current and arc voltage were determined. After the natural break of electric arc, the final gap value between electrodes was accepted as a maximal value of arc length. Findings. Experimentally the transfer of metal in interelectrode space corresponded to the tiny drop mechanism. According to external signs the relation between maximal arc length and the power of electric current has the form of exponential dependence. Specific power of electric arc at the moment of arc forming per unit of its length characterizes the environment in the interelectrode space. Originality. 1 Based on the analysis of influence of the studied chemical compounds on the formation processes of electric arc the inversely proportional relationship between the power of the electric current and the maximum arc length until the moment of its natural break is defined. 2 Ratio between the maximal arc length and the power of electric current, with the sufficiently high coefficient of correlation is submitted to the exponential dependence. Influence of the compounds under study on the process of

  19. 78 FR 19606 - Energy Conservation Program for Consumer Products: Test Procedures for Residential Furnace Fans

    Science.gov (United States)

    2013-04-02

    ... difference between a modular blower and electric furnace is the presence of an electric resistance heating kit. DOE is aware that some modular blower manufacturers offer electric resistance heating kits to be... air. Measurements should be taken at nominal voltage and no voltage adjustments should be allowed. FER...

  20. Arc generators of low-temperature plasma

    International Nuclear Information System (INIS)

    Krolikowski, Cz.; Niewiedzial, R.; Siwiec, J.

    1979-01-01

    This paper is a review of works concerning investigation and use of low-temperature plasma in arc plasma generators made in Electric Power Institute of PP. There are discussed: analytical approach to a problem of volt-current and operational characteristics of DC arc plasma generators, determination of limits of their stable work and possibilities of their use to technological aims. (author)

  1. Reactor as furnace and reactor as lamp

    International Nuclear Information System (INIS)

    Goldanskii, V.I.

    1992-01-01

    There are presented general characteristics of the following ways of transforming of nuclear energy released in reactors into chemical : ordinary way (i.e. trough the heat, mechanical energy and electricity); chemonuclear synthesis ; use of high-temperature fuel elements (reactor as furnace); use of the mixed nγ-radiation of reactors; use of the radiation loops; radiation - photochemical synthesis (reactor as lamp). Advantage and disadvantages of all above variants are compared. The yield of the primary product of fixation of nitrogen (nitric oxide NO) in reactor with the high-temperature (above ca. 1900degC) fuel elements (reactor-furnace) can exceed W ∼ 200 kg per gram of burned uranium. For the latter variant (reactor-lamp) the yield of chemical products can reach W ∼ 60 kg. per gram of uranium. Such values of W are close to or even strongly exceed the yields of chemical products for other abovementioned variants and - what is particularly important - are not connected to the necessity of archscrupulous removal of radioactive contamination of products. (author)

  2. Automated, High Temperature Furnace for Glovebox Operation

    International Nuclear Information System (INIS)

    Neikirk, K.

    2001-01-01

    The Plutonium Immobilization Project (PIP), to be located at the Savannah River Site SRS, is a combined development and testing effort by Lawrence Livermore National Laboratory (LLNL), Westinghouse Savannah River Company (WSRC), Pacific Northwest National Laboratory (PNNL), Argonne National Laboratory (ANL), and the Australian National Science and Technology Organization (ANSTO). The Plutonium Immobilization process involves the disposition of excess plutonium by incorporation into ceramic pucks. As part of the immobilization process, furnaces are needed for sintering the ceramic pucks. The furnace being developed for puck sintering is an automated, bottom loaded furnace with insulating package and resistance heating elements located within a nuclear glovebox. Other furnaces types considered for the application include retort furnaces and pusher furnaces. This paper, in part, will discuss the furnace technologies considered and furnace technology selected to support reliable puck sintering in a glovebox environment

  3. Design of a rotating-hearth furnace

    Energy Technology Data Exchange (ETDEWEB)

    Behrens, H A [Verein Deutscher Eisenhuettenleute (VDEh), Duesseldorf (Germany, F.R.)

    1979-10-01

    Presented in two parts, this paper is intended to provide an outline of the theoretical fundamentals for the design of rotating-hearth furnaces for heating round stock and deals with the characteristic design features of such furnaces.

  4. Waste and dust utilisation in shaft furnaces

    Energy Technology Data Exchange (ETDEWEB)

    Senk, D.; Babich, A.; Gudenau, H.W. [Rhein Westfal TH Aachen, Aachen (Germany)

    2005-07-01

    Wastes and dusts from steel industry, non-ferrous metallurgy and other branches can be utilised e.g. in agglomeration processes (sintering, pelletising or briquetting) and by injection into shaft furnaces. This paper deals with the second way. Combustion and reduction behaviour of iron- and carbon-rich metallurgical dusts and sludges containing lead, zinc and alkali as well as other wastes with and without pulverised coal (PC) has been studied when injecting into shaft furnaces. Following shaft furnaces have been examined: blast furnace, cupola furnace, OxiCup furnace and imperial-smelting furnace. Investigations have been done at laboratory and industrial scale. Some dusts and wastes under certain conditions can be not only reused but can also improve combustion efficiency at the tuyeres as well as furnace performance and productivity.

  5. Principles of arc flash protection

    Energy Technology Data Exchange (ETDEWEB)

    Hirschmann, R. B.

    2003-04-01

    Recent developments in NFPA 70E, the electrical safety standards in the United States and Canada, designed to provide for a safe industrial work environment, are discussed. The emphasis in this instance is on arc explosions. Development of an arc flash protective program is discussed under various major components of an electrical safety program. These are: appropriate qualifications and training for workers, safe work practices, appropriate hazard assessment practices for any task exceeding 50V where there is the potential of an arc flash accident, flash protection equipment commensurate with the hazard associated with the task to be performed, layering in protective clothing over all body surfaces, and strict adherence to rules regarding use of safety garments and equipment.

  6. Electrostatic Levitation Furnace for the ISS

    Science.gov (United States)

    Murakami, Keiji; Koshikawa, Naokiyo; Shibasaki, Kohichi; Ishikawa, Takehiko; Okada, Junpei; Takada, Tetsuya; Arai, Tatsuya; Fujino, Naoki; Yamaura, Yukiko

    2012-01-01

    JAXA (Japan Aerospace Exploration Agency) has just started the development of Electrostatic Levitation Furnace to be launched in 2014 for the ISS. This furnace can control the sample position with electrostatic force and heat it above 2000 degree Celsius using semiconductor laser from four different directions. The announcement of Opportunity will be issued soon for this furnace. In this paper, we will show the specifications of this furnace and also the development schedule

  7. A cylindrical furnace for absorption spectral studies

    Indian Academy of Sciences (India)

    A cylindrical furnace with three heating zones, capable of providing a temperature of 1100°C, has been fabricated to enable recording of absorption spectra of high temperature species. The temperature of the furnace can be controlled to ± 1°C of the set temperature. The salient feature of this furnace is that the material ...

  8. A rotating arc plasma invertor

    International Nuclear Information System (INIS)

    Reusch, M.F.; Jayaram, K.

    1987-02-01

    A device is described for the inversion of direct current to alternating current. The main feature is the use of a rotating plasma arc in crossed electric and magnetic fields as a switch. This device may provide an economic alternative to other inversion methods in some circumstances

  9. Obtention of copper-magnesium alloys wires used in electrical transmission lines

    International Nuclear Information System (INIS)

    Fernandes, Marcos Gonzales

    2010-01-01

    The aim of this work was to obtain copper wires in three different chemical compositions starting from electrolytic copper and magnesium. The mains steps were evaluated, starting from the melting of small eutectic cooper-magnesium specimens in an electric arc furnace, followed by further dilution of this buttons in a resistive furnace and casting it in a copper mould. The as cast billets were homogenized in a resistive furnace at 910 degree C for 2 h. The billets were mechanically cold worked by swaging and a final drawing step to attain a round shape and a reasonable surface quality. The cast ingots chemical analysis indicated that the processing route showed to be adequate, in laboratory scale, to obtain wires with cross sectional area of 4 mm2 and 10 m in length. The wires in both conditions - as cold worked and after a recovering heat treatment at 510 degree C for 1 h, were mechanically characterized by tensile testing and hardness. The wires had also the electric conductivity assessed in the recovered heat-treated state and the results were compared to the literature data. The obtained material showed to be adequate to be used as electric conductor. The yield strain and ultimate tensile strength were improved with the increasing amount of Mg in the alloy, 11 % and 24 %, respectively, while the electric conductivity decreased to 60 % IACS (International Annealed Copper Standard). (author)

  10. In-depth investigation of high-energy arcing faults (HEAF) of electrical components with possible induced fires; Vertiefte Untersuchungen zum hochenergetischen Versagen elektrischer Komponenten (HEAF) mit moeglicher Brandfolge

    Energy Technology Data Exchange (ETDEWEB)

    Roewekamp, Marina

    2015-11-15

    Main objective of the project 3611R01301 performed on behalf of the Federal Ministry for the Environment, Nature Conservation, Building and Nuclear Safety (BMUB) is an in-depth investigation of fires at electrical components induced by high energy arcing faults (HEAF) according to their non-negligible significance to nuclear safety. This report provides an overview on the insights with respect to high energy arcing faults at electrical components mainly gained from investigations of the national as well as international operating experience from nuclear installations. Moreover, the insights from the international operating experience have resulted in an experimental program carried out in the frame of a task by the OECD Nuclear Energy Agency (NEA) in order to investigate failures of electrical components, e. g. breakers, switchgears or transformers, installed in nuclear power plants of the member countries due to HEAF and potential consequential fires. The results of the in-depth analyses and experimental investigations shall be used for identifying potential areas of damage in a suitable manner. The results based on inter-national research shall also be checked with respect to their applicability to the situation in German nuclear power plants.

  11. An evaluation of the electric arc spray and (HPPS) processes for the manufacturing of high power plasma spraying MCrAIY coatings

    Science.gov (United States)

    Sacriste, D.; Goubot, N.; Dhers, J.; Ducos, M.; Vardelle, A.

    2001-06-01

    The high power plasma torch (PlazJet) can be used to spray refractory ceramics with high spray rates and deposition efficiency. It can provide dense and hard coating with high bond strengths. When manufacturing thermal barrier coatings, the PlazJet gun is well adapted to spraying the ceramic top coat but not the MCrAIY materials that are used as bond coat. Arc spraying can compete with plasma spraying for metallic coatings since cored wires can be used to spray alloys and composites. In addition, the high production rate of arc spraying enables a significant decrease in coating cost. This paper discusses the performances of the PlazJet gun, and a twin-wire are spray system, and compares the properties and cost of MCrAIY coatings made with these two processes. For arc spraying, the use of air or nitrogen as atomizing gas is also investigated.

  12. Arc modeling for welding analysis

    International Nuclear Information System (INIS)

    Glickstein, S.S.

    1978-04-01

    A one-dimensional model of the welding arc that considers heat generation by the Joule effect and heat losses by radiation and conduction has been used to study the effects of various gases and gas mixtures currently employed for welding applications. Minor additions of low ionization potential impurities to these gases are shown to significantly perturb the electrical properties of the parent gas causing gross changes in the radial temperature distribution of the arc discharge. Such changes are reflected in the current density distribution and ultimately in the input energy distribution to the weldment. The result is observed as a variation in weld penetration. Recently published experiments and analyses of welding arcs are also evaluated and shown to contain erroneous data and results. Contrary to previous beliefs, the inclusion of a radiation loss term in the basic energy balance equation is important and cannot be considered as negligible in an argon arc at temperatures as low as 10,000 0 K. The one-dimensional analysis of the welding arc as well as the evaluation of these earlier published reports helps to explain the effects of various gases used for welding, improves our understanding of the physics of the welding arc, and provides a stepping stone for a more elaborate model which can be applied to help optimize welding parameters

  13. Behavior of coke in large blast furnaces

    Energy Technology Data Exchange (ETDEWEB)

    Nakamura, N

    1978-01-01

    Three blast furnaces were quenched in operation and the contents were examined; the temperature distribution was also measured, using Tempil pellets. The furnaces examined included a low productivity one, which was examined to see what was wrong. Changes in the quality of coke as it descends in the furnace, and coke behavior in the raceway and hearth are reported. The functions required of coke, and the effects of poor coke quality, are explained, together with the coke quality required in large blast furnaces. A theoretical study of the role of coke in large blast furnaces is included.

  14. Alkaline carbonates in blast furnace process

    Directory of Open Access Journals (Sweden)

    P. Besta

    2014-10-01

    Full Text Available The production of iron in blast furnaces is a complex of physical, chemical and mechanical processes. The input raw materials contain not only metallic components, but also a number of negative elements. The most important negative elements include alkaline carbonates. They can significantly affect the course of the blast furnace process and thus the overall performance of the furnace. As a result of that, it is essential to accurately monitor the alkali content in the blast furnace raw materials. The article analyzes the alkali content in input and output raw materials and their impact on the blast furnace process.

  15. Industrial furnace with improved heat transfer

    Energy Technology Data Exchange (ETDEWEB)

    Hoetzl, M.; Lingle, T.M.

    1992-07-07

    This patent describes an industrial furnace for heating work which emits volatiles during heating. It comprises a generally cylindrical, closed end furnace section defining a sealable heat transfer chamber for heating work disposed therein; fan means for directing furnace atmosphere as a swirling wind mass about the interior of the furnace section over a portion thereof; heat means for heating the wind mass within the fan chamber; and an incineration track formed as a circumferentially extending groove about the exterior of the furnace section and in heat transfer relationship with and situated at least to extend about a portion of the fan chamber.

  16. Metal transfer during vacuum consumable arc remelting

    International Nuclear Information System (INIS)

    Zanner, F.J.

    1977-11-01

    A description of the vacuum consumable arc remelt process as related to solidification and a review of vacuum arc literature is presented. Metal transfer at arc lengths less than or equal to 3 cm was found to occur when liquid metal spikes hanging from the cathode form a low resistance bridge (drop short) by touching the anode and subsequently rupturing. During the bridge lifetime (0.0003 to 0.020 s) the arc is extinguished and all of the electrical power is directed through the molten bridge. The formation and rupture of these molten metal bridges are confirmed with electrical resistance measurements. At long arc lengths (greater than 10 cm) the spikes separate before touching the anode

  17. Arc saw development report

    International Nuclear Information System (INIS)

    Deichelbohrer, P.R.; Beitel, G.A.

    1981-01-01

    The arc saw is one of the key components of the Contaminated Equipment Volume Reduction (CEVR) Program. This report describes the progress of the arc saw from its inception to its current developmental status. History of the arc saw and early contributors are discussed. Particular features of the arc saw and their advantages for CEVR are detailed. Development of the arc saw including theory of operation, pertinent experimental results, plans for the large arc saw and advanced control systems are covered. Associated topics such as potential applications for the arc saw and other arc saw installations in the world is also touched upon

  18. Multikilowatt variable frequency microwave furnace

    International Nuclear Information System (INIS)

    Bible, D.W.; Lauf, R.J.; Everleigh, C.A.

    1992-01-01

    In this paper, the authors describe a new type of microwave processing furnace in which the frequency can be varied continuously from 4 to 8 GHz and the power level varied from zero up to 2.5 kW. The extraordinary bandwidth of this furnace is achieved by using a traveling wave tube (TWT) amplifier originally developed for electronic warfare applications. The TWT is a linear beam device characterized by a traveling electromagnetic wave that continuously extracts energy longitudinally along the path of an electron beam. The TWT, unlike other microwave tubes such as the magnetron, klystron, gyrotron, and others, does not depend upon resonant RF fields and is therefore capable of wide bandwidth operation.operation

  19. Glass science tutorial: Lecture number-sign 2, Operating electric glass melters. James N. Edmonson, Lecturer

    International Nuclear Information System (INIS)

    Kruger, A.A.

    1994-10-01

    This report contains basic information on electric furnaces used for glass melting and on the properties of glass useful for the stabilization of radioactive wastes. Furnace nomenclature, furnace types, typical silicate glass composition and properties, thermal conductivity information, kinetics of the melting process, glass furnace refractory materials composition and thermal conductivity, and equations required for the operation of glass melters are included

  20. Automated, High Temperature Furnace for Glovebox Operation

    International Nuclear Information System (INIS)

    Neikirk, K.

    2001-01-01

    The U.S. Department of Energy will immobilize excess plutonium in the proposed Plutonium Immobilization Plant (PIP) at the Savannah River Site (SRS) as part of a two track approach for the disposition of weapons usable plutonium. As such, the Department of Energy is funding a development and testing effort for the PIP. This effort is being performed jointly by Lawrence Livermore National Laboratory (LLNL), Westinghouse Savannah River Company (WSRC), Pacific Northwest National Laboratory (PNNL), and Argonne National Laboratory (ANL). The Plutonium Immobilization process involves the disposition of excess plutonium by incorporation into ceramic pucks. As part of the immobilization process, furnaces are needed for sintering the ceramic pucks. The furnace being developed for puck sintering is an automated, bottom loaded furnace with insulting package and resistance heating elements located within a nuclear glovebox. Other furnaces considered for the application include retort furnaces and pusher furnaces. This paper, in part, will discuss the furnace technologies considered and furnace technology selected to support reliable puck sintering in a glovebox environment. Due to the radiation levels and contamination associated with the plutonium material, the sintering process will be fully automated and contained within nuclear material gloveboxes. As such, the furnace currently under development incorporates water and air cooling to minimize heat load to the glovebox. This paper will describe the furnace equipment and systems needed to employ a fully automated puck sintering process within nuclear gloveboxes as part of the Plutonium Immobilization Plant

  1. Blast furnace top gas and dusts; Masuunin huippukaasu ja poelyt

    Energy Technology Data Exchange (ETDEWEB)

    Lohi, T.K.; Mannila, P.; Karjalahti, T.; Haerkki, J.

    1997-12-31

    This report is related to the `Gas Phase Reactions in a Blast Furnace` project. The aim of the project is to clarify the behaviour of gas phase in a blast furnace with high oil injection rate. The effect of blast furnace operation, iron reduction reactions, the amount of oil injected, alkalis, zinc and sulfur on the formation of top gas and dusts has been examined in this work. In addition, the gas cleaning system, i.e. the dust sack, gas scrubber, venturi scrubbers and an electric filter, of the blast furnaces of Rautaruukki Oy is presented. The composition of the top gas as well as the amount and composition of the dust from the gas cleaners were investigates in the experimental part of the research. The work has been focused on the analysis of carbon, iron, zinc, sulfur and alkalis. In addition to this, possible systematic variations caused by the discharge of hot metal were investigated. The experiments were made at blast furnaces no 1 and 2 of Rautaruukki Raahe Steel. The relationship between dust quantity and composition in the dust sack and the quantity of oil injected was analyzed on the basis of collected data. On the basis of experimental results, hot metal discharge has no effect on the composition or quantity of the top gas and dust. The composition of the dust varied between different gas cleaners. The coarsest and heaviest material remains in the dust sack. The lightest material separates at the electric filter. The main components at every gas cleaner were iron (9.4 - 38.1 %) and carbon (31.5 - 63.7 %). Particles with zinc and sulfur were separated at the venturi scrubbers (Zn = 3.0 % and S = 2.2 %) and the electric filter (Zn = 3.2 % and S = 2.6 %). Particles with alkalis were separated at the end of the gas cleaning process. The amount of sodium at the venturi scrubbers and the electric filter was 1.0 % on average. The average amount of potassium was 0.5 % at the venturi scrubber and 1.4 % at the electric filter 28 refs., 31 figs.

  2. Production of Manual Metal Arc Welding Electrodes with Local Raw ...

    African Journals Online (AJOL)

    Manual arc welding using flux coated electrodes is carried out by producing an electric arc between the base metal and a flux covered metal electrode with electric current that depends on the type of electrode, material, welding position and the desired strength. The composition of flux coated electrodes is complex and a ...

  3. Arc melting and homogenization of ZrC and ZrC + B alloys

    Science.gov (United States)

    Darolia, R.; Archbold, T. F.

    1973-01-01

    A description is given of the methods used to arc-melt and to homogenize near-stoichiometric ZrC and ZrC-boron alloys, giving attention to the oxygen contamination problem. The starting material for the carbide preparation was ZrC powder with an average particle size of 4.6 micron. Pellets weighing approximately 3 g each were prepared at room temperature from the powder by the use of an isostatic press operated at 50,000 psi. These pellets were individually melted in an arc furnace containing a static atmosphere of purified argon. A graphite resistance furnace was used for the homogenization process.

  4. Arc fault detection system

    Science.gov (United States)

    Jha, K.N.

    1999-05-18

    An arc fault detection system for use on ungrounded or high-resistance-grounded power distribution systems is provided which can be retrofitted outside electrical switchboard circuits having limited space constraints. The system includes a differential current relay that senses a current differential between current flowing from secondary windings located in a current transformer coupled to a power supply side of a switchboard, and a total current induced in secondary windings coupled to a load side of the switchboard. When such a current differential is experienced, a current travels through a operating coil of the differential current relay, which in turn opens an upstream circuit breaker located between the switchboard and a power supply to remove the supply of power to the switchboard. 1 fig.

  5. Arc fault detection system

    Science.gov (United States)

    Jha, Kamal N.

    1999-01-01

    An arc fault detection system for use on ungrounded or high-resistance-grounded power distribution systems is provided which can be retrofitted outside electrical switchboard circuits having limited space constraints. The system includes a differential current relay that senses a current differential between current flowing from secondary windings located in a current transformer coupled to a power supply side of a switchboard, and a total current induced in secondary windings coupled to a load side of the switchboard. When such a current differential is experienced, a current travels through a operating coil of the differential current relay, which in turn opens an upstream circuit breaker located between the switchboard and a power supply to remove the supply of power to the switchboard.

  6. Arc melting in inert gas atmosphere of zirconium sponge

    International Nuclear Information System (INIS)

    Julio Junior, O.; Andrade, A.H.P. de

    1991-01-01

    The obtainment of metallic zirconium in laboratory scale with commercial and nuclear quality is the objective of the Metallurgy Department of IEN/CNEN - Brazil, so a melting procedure of zirconium sponge in laboratory scale using an arc furnace in inert atmosphere is developed. The effects of atmosphere operation, and the use of gas absorber and the sponge characteristics over the quality of button in as-cast reporting with hardness measures are described. (C.G.C.)

  7. Refractory of Furnaces to Reduce Environmental Impact

    Science.gov (United States)

    Hanzawa, Shigeru

    2011-10-01

    The energy load of furnaces used in the manufacturing process of ceramics is quite large. Most of the environmental impact of ceramics manufacturing is due to the CO2 produced from this high energy load. To improve this situation, R&D has focused on furnace systems and techniques of control in order to reduce energy load. Since furnaces are comprised of refractory, consideration of their mechanical and thermal characteristics is important. Herein are described several refractory types which were chosen through comparison of the characteristics which contribute to heat capacity reduction, heat insulating reinforcement and high emissivity, thereby improving thermal radiation heat transfer efficiency to the ceramic articles. One selected refractory material which will reduce the environmental impact of a furnace, chosen considering low heat capacity and high emissivity characteristics, is SiC. In this study, thermal radiation heat transfer efficiency improvement and its effect on ceramic articles in the furnace and oxidation behaviour were investigated at 1700K. A high density SiC refractory, built into the furnace at construction, has relatively high oxidation durability and has the ability to reduce environmental impact-CO2 by 10 percent by decreasing the furnace's energy load. However, new oxidation prevention techniques for SiC will be necessary for long-term use in industrial furnaces, because passive to active oxidation transition behaviour of commercial SiC refractory is coming to close ideal.

  8. Fluxless furnace brazing and its theoretical fundamentals

    International Nuclear Information System (INIS)

    Lison, R.

    1979-01-01

    In this paper the theoretical fundamental of fluxless furnace brazing are described. The necessary conditions for a wetting in the vacuum, under a inert-gas and with a reducing gas are discussed. Also other methods to reduce the oxygen partial pressure are described. Some applications of fluxless furnace brazing are outlined. (orig.) [de

  9. Refractory of Furnaces to Reduce Environmental Impact

    International Nuclear Information System (INIS)

    Hanzawa, Shigeru

    2011-01-01

    The energy load of furnaces used in the manufacturing process of ceramics is quite large. Most of the environmental impact of ceramics manufacturing is due to the CO 2 produced from this high energy load. To improve this situation, R and D has focused on furnace systems and techniques of control in order to reduce energy load. Since furnaces are comprised of refractory, consideration of their mechanical and thermal characteristics is important. Herein are described several refractory types which were chosen through comparison of the characteristics which contribute to heat capacity reduction, heat insulating reinforcement and high emissivity, thereby improving thermal radiation heat transfer efficiency to the ceramic articles. One selected refractory material which will reduce the environmental impact of a furnace, chosen considering low heat capacity and high emissivity characteristics, is SiC. In this study, thermal radiation heat transfer efficiency improvement and its effect on ceramic articles in the furnace and oxidation behaviour were investigated at 1700K. A high density SiC refractory, built into the furnace at construction, has relatively high oxidation durability and has the ability to reduce environmental impact-CO 2 by 10 percent by decreasing the furnace's energy load. However, new oxidation prevention techniques for SiC will be necessary for long-term use in industrial furnaces, because passive to active oxidation transition behaviour of commercial SiC refractory is coming to close ideal.

  10. The use of blast furnace slag

    Directory of Open Access Journals (Sweden)

    V. Václavík

    2012-10-01

    Full Text Available The paper presents the results of experimental research that dealt with the substitution of finely ground blast furnace slag for Portland cement in the course of simple concrete manufacturing. Physical and mechanical properties of experimental concrete mixtures based on finely ground blast furnace slag were observed.

  11. Optical cavity furnace for semiconductor wafer processing

    Science.gov (United States)

    Sopori, Bhushan L.

    2014-08-05

    An optical cavity furnace 10 having multiple optical energy sources 12 associated with an optical cavity 18 of the furnace. The multiple optical energy sources 12 may be lamps or other devices suitable for producing an appropriate level of optical energy. The optical cavity furnace 10 may also include one or more reflectors 14 and one or more walls 16 associated with the optical energy sources 12 such that the reflectors 14 and walls 16 define the optical cavity 18. The walls 16 may have any desired configuration or shape to enhance operation of the furnace as an optical cavity 18. The optical energy sources 12 may be positioned at any location with respect to the reflectors 14 and walls defining the optical cavity. The optical cavity furnace 10 may further include a semiconductor wafer transport system 22 for transporting one or more semiconductor wafers 20 through the optical cavity.

  12. Método integral configurable y flexible de ensayo de materiales consumibles de soldadura por arco eléctrico. // Integral, flexible and shaped method for electric arc welding consumable materials test.

    Directory of Open Access Journals (Sweden)

    A. García Rodríguez

    2005-05-01

    Full Text Available La presente publicación propone un método integral configurable y flexible para facilitar el ensayo de materialesconsumibles de soldadura por arco eléctrico en las condiciones tecnológicas para las que han sido diseñados estosmateriales, en relación a la calidad de la unión soldada. Se puede llegar a conclusiones definitivas sobre la calidad de lasoldadura usando un determinado material consumible mediante: la relación operacional de técnicas de inteligencia naturaly/o artificial, el uso de sistemas expertos, el trabajo con bases de datos, la simulación y la realización práctica del procesomientras se registran ciertos parámetros del arco eléctrico, digitalmente procesados estadísticamente y relacionados a losresultados de la caracterización de la unión soldada. El método permite registrar adecuadamente la información referente acada aspecto del proceso exigida en los procesos de certificación de la calidad de los consumibles, así como en lainvestigación dirigida a optimizar la composición química y las propiedades físicas de un material, para obtener calidadesóptimas en un determinado proceso; además es posible obtener las bases de datos de parámetros del arco eléctrico útilespara investigar, desarrollar y valorar métodos y algoritmos para el monitoreo en tiempo real de la calidad de la soldaduradurante un determinado proceso tecnológico de soldadura con arco eléctrico.Palabras Clave: Ensayo, materiales, soldadura, arco eléctrico, estabilidad, calidad, simulación, optimización,unión soldada.___________________________________________________________________________Abstract.This paper presenst an integral, flexible and shaped method that make easy the electric arc welding consumable materials test at thedesigned technological conditions, related to the quality of the welding joint. It is possible to arrive to definitive conclusions about thewelding quality using a fixed material through: operational

  13. Numerical simulation of global formation of auroral arcs

    International Nuclear Information System (INIS)

    Miura, A.; Sato, T.

    1980-01-01

    Global simulation of auroral arcs is performed, based on the feedback theory of auroral arcs (Sato, 1978), for a three-dimensionally coupled ionosphere-magnetosphere system which includes two pairs of large-scale Birkeland currents, large-scale polar cap electric fields, and a day-night asymmetry of the electron density distribution. Simulation results have shown that auroral arcs are formed in the dark sector of the auroral oval, more preferentially in the evening sector. They usually appear in multiples with a shape elongating in the east-west direction, each arc being a couple of thousand kilometers in length and 10 to 40 km in width. A pair of small-scale, upward and downward, Birkeland currents is associated with each arc, the density of which becomes 10 to 200 μA/m 2 at 110-km height, and the intensity of the associated electrojet reaches 5 to 20 kA. Each arc is strongly polarized in the direction of the large-scale northsouth current so that the electric field inside the arc is reduced considerably from its ambient value. What controls the formation of auroral arcs (growing speed, locations, arc width, etc.) is examined in detail. For example, the arc width becomes sharper, as the bounce time of the Alfven wave decreases. The overall structure of auroras is largely dependent upon the large-scale Birkeland current, the electric field, and the electron density distribution in the auroral oval

  14. Biomass furnace: projection and construction

    Energy Technology Data Exchange (ETDEWEB)

    Melo, Fernanda Augusta de Oliveira; Silva, Juarez Sousa e; Silva, Denise de Freitas; Sampaio, Cristiane Pires; Nascimento Junior, Jose Henrique do [Universidade Federal de Vicosa (DEA/UFV), MG (Brazil). Dept. de Engenharia Agricola

    2008-07-01

    Of all the ways to convert biomass into thermal energy, direct combustion is the oldest. The thermal-chemical technologies of biomass conversion such as pyrolysis and gasification, are currently not the most important alternatives; combustion is responsible for 97% of the bio-energy produced in the world (Demirbas, 2003). For this work, a small furnace was designed and constructed to use biomass as its main source of fuel, and the combustion chamber was coupled with a helical transporter which linked to the secondary fuel reservoir to continually feed the combustion chamber with fine particles of agro-industrial residues. The design of the stove proved to be technically viable beginning with the balance of mass and energy for the air heating system. The proposed heat generator was easily constructed as it made use of simple and easily acquired materials, demanding no specialized labor. (author)

  15. Electricity

    CERN Document Server

    Basford, Leslie

    2013-01-01

    Electricity Made Simple covers the fundamental principles underlying every aspect of electricity. The book discusses current; resistance including its measurement, Kirchhoff's laws, and resistors; electroheat, electromagnetics and electrochemistry; and the motor and generator effects of electromagnetic forces. The text also describes alternating current, circuits and inductors, alternating current circuits, and a.c. generators and motors. Other methods of generating electromagnetic forces are also considered. The book is useful for electrical engineering students.

  16. Further development of pyrometallurgical IME recycling process for Li-ion batteries from electric vehicles

    International Nuclear Information System (INIS)

    Vest, Matthias

    2016-01-01

    Li-ion batteries are increasingly used in hybrid electric vehicles (HEV), electric vehicles (EV) and stationary storage applications. Those applications are significantly different in terms of storage capacity, life cycles and charging times from consumer type batteries such as mobile phones and handheld tools. Naturally, those HEV and EV Li-ion batteries also differ significantly in chemical composition and size. Coherently, a recycling concept has been developed for HEV, EV and stationary storage Li-ion batteries. This concept is based on the existing IME-ACCUREC recycling process for consumer type batteries. This work describes the whole process development including slag design, test series in a lab-scale electric arc furnace and a 1 t scale trial in a top blown rotary converter.

  17. Design and Development of Tilting Rotary Furnace

    Science.gov (United States)

    Sai Varun, V.; Tejesh, P.; Prashanth, B. N.

    2018-02-01

    Casting is the best and effective technique used for manufacturing products. The important accessory for casting is furnace. Furnace is used to melt the metal. A perfect furnace is one that reduces the wastage of material, reduces the cost of manufacturing and there by reduces the cost of production. Of all the present day furnaces there may be wastage of material, and the chances of increasing the time of manufacturing as the is continuous need of tilting of the furnace for every mould and then changing the moulds. Considering these aspects, a simple and least expensive tilting rotary furnace is designed and developed. The Tilting and Rotary Furnace consists of mainly melting chamber and the base. The metal enters the melting chamber through the input door that is provided on the top of the melting chamber. Inside the melting chamber there is a graphite furnace. The metal is melted in the graphite crucible. An insulation of ceramic fibre cloth is provided inside the furnace. The metal is melted using Propane gas. The propane gas is easily available and economic. The gas is burned using a pilot burner. The pilot burner is more efficient that other burners. The pilot burner is lit with a push button igniter. The pilot burner is located at the bottom of the combustion chamber. This enables the uniform heating of the metal inside the crucible. The temperature inside the melting chamber is noted using a temperature sensor. The gas input is cut-off if the temperature is exceeding a specific temperature. After the melting of the metal is done the furnace is tilted and after the mould is filled it is rotated. The external gears are used to controlling the tilting. The results of studies carried out for the design & development of low cost, simple furnace that can be mounted anywhere on the shop floor and this can be very much useful for the education purposes and small scale manufacturing. The furnace can be rotated in 360 degrees and can help in reducing the time taken

  18. Model based energy benchmarking for glass furnace

    International Nuclear Information System (INIS)

    Sardeshpande, Vishal; Gaitonde, U.N.; Banerjee, Rangan

    2007-01-01

    Energy benchmarking of processes is important for setting energy efficiency targets and planning energy management strategies. Most approaches used for energy benchmarking are based on statistical methods by comparing with a sample of existing plants. This paper presents a model based approach for benchmarking of energy intensive industrial processes and illustrates this approach for industrial glass furnaces. A simulation model for a glass furnace is developed using mass and energy balances, and heat loss equations for the different zones and empirical equations based on operating practices. The model is checked with field data from end fired industrial glass furnaces in India. The simulation model enables calculation of the energy performance of a given furnace design. The model results show the potential for improvement and the impact of different operating and design preferences on specific energy consumption. A case study for a 100 TPD end fired furnace is presented. An achievable minimum energy consumption of about 3830 kJ/kg is estimated for this furnace. The useful heat carried by glass is about 53% of the heat supplied by the fuel. Actual furnaces operating at these production scales have a potential for reduction in energy consumption of about 20-25%

  19. Uranium casting furnace automatic temperature control development

    International Nuclear Information System (INIS)

    Lind, R.F.

    1992-01-01

    Development of an automatic molten uranium temperature control system for use on batch-type induction casting furnaces is described. Implementation of a two-color optical pyrometer, development of an optical scanner for the pyrometer, determination of furnace thermal dynamics, and design of control systems are addressed. The optical scanning system is shown to greatly improve pyrometer measurement repeatability, particularly where heavy floating slag accumulations cause surface temperature gradients. Thermal dynamics of the furnaces were determined by applying least-squares system identification techniques to actual production data. A unity feedback control system utilizing a proportional-integral-derivative compensator is designed by using frequency-domain techniques. 14 refs

  20. Programmable temperature regulator of VAO-1 furnace

    International Nuclear Information System (INIS)

    Zahalka, F.

    1979-01-01

    A programmable temperature controller is described for a furnace for high-level waste processing. Furnace temperature is controlled by a program compiled from a combination of 3 parts with different linear increments or decrements of time dependent temperature and 2 parts with isothermal control for over a preset period. The equipment consists essentially of a programming unit, a programmed digital-to-analog converter and a power unit. The design is described in detail and its specifications are given. The maximum operating temperature of 1500 degC may be reached in the furnace charge section. (B.S.)

  1. Alternative fuels for multiple-hearth furnaces

    Energy Technology Data Exchange (ETDEWEB)

    Bracket, B D; Lawson, T U

    1980-04-01

    Results are described of a feasibility study on the use of refuse-derived fuel, shredded paper, wood waste, coal, and waste oil in multiple-hearth furnaces at the Lower Molonglo Water Quality Control Centre in Australia. An assessment of waste fuel availability and characteristics is given, and a summary is made of the technical and economic aspects of using these alternative fuels and of minimizing furnace fuel requirements by reducing sludge moisture. The recommended method of reducing fuel oil consumption in the furnace is shown to be sludge drying, using process exhaust heat in a rotary dryer.

  2. Internal heat exchange tubes for industrial furnaces

    Energy Technology Data Exchange (ETDEWEB)

    Hoetzl, M.; Lingle, T.M.

    1992-05-26

    This patent describes a method for cooling the work within an industrial furnace. It comprises providing a longitudinally extending outer tube which extends into the furnace having a closed axial end and an open axial end; providing a preformed inner tube open at both ends within the outer tube; injecting a coolant into the inner tube so that the coolant flows from one axial end of the tube out the opposite end adjacent the closed end of the outer tube, and from the closed end of the outer tube to the open end thereof; circulating a gas within the furnace against the outer tube to effect heat transfer therewith.

  3. Liquid-Arc/Spark-Excitation Atomic-Emission Spectroscopy

    Science.gov (United States)

    Schlagen, Kenneth J.

    1992-01-01

    Constituents of solutions identified in situ. Liquid-arc/spark-excitation atomic-emission spectroscopy (LAES) is experimental variant of atomic-emission spectroscopy in which electric arc or spark established in liquid and spectrum of light from arc or spark analyzed to identify chemical elements in liquid. Observations encourage development of LAES equipment for online monitoring of process streams in such industries as metal plating, electronics, and steel, and for online monitoring of streams affecting environment.

  4. Plasma's sweeping arc

    International Nuclear Information System (INIS)

    Pichon, Max

    2010-01-01

    Full text: It is purely elemental, returning materials to their basic atoms through extreme heat and then recondensing them in useful ways. Plasma arc gasification is the latest advanced waste treatment (AWT)concept to hit our shores, courtesy of Zenergy Australia. According to its fans, plasma technology can eliminate all domestic waste to landfill and turn it into beneficial by-products. Japan has toyed with it for a decade, but the idea is now creating a bit of buzz, in the US in particular. Consultancy URS last year undertook a review of 16 advanced technologies for the City of Los Angeles and determined plasma arc gasification was one of the most promising. The Waste Management Association of Australia (VVMAA), however, is cautious - too many AWT projects here have failed to live up to their promises. Plasma arc gasification works on the same principle as a welding machine. An inert gas is passed through an electrical arc between two electrodes and becomes ionised (called plasma), reaching temperatures as high as 13,900°C. It is then injected into the plasma converter holding the waste. Zenergy is working with US technology company Plasma Waste Recycling (PWR), which says it can convert 80 per cent of waste to syngas, a mixture of carbon monoxide and hydrogen that can be used to generate renewable electricity. The inorganic compounds in the waste come out as a solid, either molten metal to be cast as scrap steel or a slag that can be used as a building material aggregate or spun into mineral wool. “The plasma arc process is the next generation for AWT plants as there is no incineration involved, no fly ash, no bottom ash and nothing left to landfill,” said Zenergy Australia's Paul Prasad. He estimates a plant could convert up to 175,000 tonnes of household waste a year into energy or reusable by-products. Technically, it also gets around Australia's fears over incineration, though whether that is really the case in practice remains to be seen. Prasad says

  5. Optical emission spectroscopy of metal vapor dominated laser-arc hybrid welding plasma

    International Nuclear Information System (INIS)

    Ribic, B.; DebRoy, T.; Burgardt, P.

    2011-01-01

    During laser-arc hybrid welding, plasma properties affect the welding process and the weld quality. However, hybrid welding plasmas have not been systematically studied. Here we examine electron temperatures, species densities, and electrical conductivity for laser, arc, and laser-arc hybrid welding using optical emission spectroscopy. The effects of arc currents and heat source separation distances were examined because these parameters significantly affect weld quality. Time-average plasma electron temperatures, electron and ion densities, electrical conductivity, and arc stability decrease with increasing heat source separation distance during hybrid welding. Heat source separation distance affects these properties more significantly than the arc current within the range of currents considered. Improved arc stability and higher electrical conductivity of the hybrid welding plasma result from increased heat flux, electron temperatures, electron density, and metal vapor concentrations relative to arc or laser welding.

  6. Thermal efficiency on welding of AA6061-T6 alloy by modified indirect electric arc and current signals digitalisation; Eficiencia termica en soldadura de la aleacion AA6061-T6 por arco electrico indirecto modificado y digitalizacion de senales de intensidad de corriente

    Energy Technology Data Exchange (ETDEWEB)

    Ambriz, R. R.; Barrera, G.; Garcia, R.; Lopez, V. H.

    2009-07-01

    The results of the thermal efficiency on welding by modified indirect electric arc technique (MIEA) [1] of the 6061- T6 aluminum alloy are presented. These values are in a range of 90 to 94 %, which depend of the preheating employed. Thermal efficiency was obtained by means of a balance energy which considers the heat input, the amount of melted mass of the welding profiles, and welding parameters during the joining, especially of the arc current data acquisition. Also, some dimensionless parameters were employed in order to determine the approximation grade of the melted pool, the heat affected zone (HAZ), and their corresponding values with the experimental results. (Author) 13 refs.

  7. Investigation of the structural, surface, optical and electrical properties of the Indium doped CuxO thin films deposited by a thermionic vacuum arc

    Science.gov (United States)

    Musaoğlu, Caner; Pat, Suat; Özen, Soner; Korkmaz, Şadan; Mohammadigharehbagh, Reza

    2018-03-01

    In this study, investigation of some physical properties of In-doped CuxO thin films onto amorphous glass substrates were done. The thin films were depsoied by thermionic vacuum arc technique (TVA). TVA technique gives a thin film with lower precursor impurity according to the other chemical and physical depsoition methods. The microstructural properties of the produced thin films was determined by x-ray diffraction device (XRD). The thickness values were measured as to be 30 nm and 60 nm, respectively. The miller indices of the thin films’ crystalline planes were determined as to be Cu (111), CuO (\\bar{1} 12), CuInO2 (107) and Cu2O (200), Cu (111), CuO (\\bar{1} 12), CuO (\\bar{2} 02), CuInO2 (015) for sample C1 and C2, respectively. The produced In-doped CuO thin films are in polycrystalline structure. The surface properties of produced In doped CuO thin films were determined by using an atomic force microscope (AFM) and field emission scanning electron microscope (FESEM) tools. The optical properties of the In doped CuO thin films were determined by UV–vis spectrophotometer, interferometer, and photoluminescence devices. p-type semiconductor thin film was obtained by TVA depsoition.

  8. International blast furnace hearth and raceway symposium

    Energy Technology Data Exchange (ETDEWEB)

    1981-01-01

    Papers presented discussed some of the physical and chemical processes occuring in the raceway and hearths of blast furnaces. The injection of coal or fuel slurries to replace some of the coke was also covered. Fourteen papers are abstracted separately.

  9. Multiple hearth furnace for reducing iron oxide

    Science.gov (United States)

    Brandon, Mark M [Charlotte, NC; True, Bradford G [Charlotte, NC

    2012-03-13

    A multiple moving hearth furnace (10) having a furnace housing (11) with at least two moving hearths (20) positioned laterally within the furnace housing, the hearths moving in opposite directions and each moving hearth (20) capable of being charged with at least one layer of iron oxide and carbon bearing material at one end, and being capable of discharging reduced material at the other end. A heat insulating partition (92) is positioned between adjacent moving hearths of at least portions of the conversion zones (13), and is capable of communicating gases between the atmospheres of the conversion zones of adjacent moving hearths. A drying/preheat zone (12), a conversion zone (13), and optionally a cooling zone (15) are sequentially positioned along each moving hearth (30) in the furnace housing (11).

  10. Hopewell Furnace NHS : alternative transportation study

    Science.gov (United States)

    2009-12-31

    This study assesses the potential for an alternative transportation system (ATS) at Hopewell Furnace National Historic Site (NHS). The Volpe Center investigated internal circulation and potential partnerships with local historic, cultural, and recrea...

  11. Metallurgy of mercury in Almaden: from aludel furnaces until Pacific furnaces

    International Nuclear Information System (INIS)

    Tejero-Manzanares, J.; Garrido Saenz, I.; Mata Cabrera, F.; Rubio Mesas, M. L.

    2014-01-01

    This paper shows the different types of furnaces for roasting cinnabar, used in the metallurgy of quicksilver over the centuries of exploitation of the Almaden Mines (Spain). Some of these techniques are part of our industrial heritage. They have contributed to name UNESCO World Heritage Site the vast technological legacy of these mines recently. This research contributes to close the long way of metallurgical activity from aludel furnaces until Pacif furnaces, first and lasted technology to produce on an industrial scale. It is delved into the most relevant aspects having to do with the type, evolution and number of furnaces existing on each of the periods. (Author)

  12. 'LTE-diffusion approximation' for arc calculations

    International Nuclear Information System (INIS)

    Lowke, J J; Tanaka, M

    2006-01-01

    This paper proposes the use of the 'LTE-diffusion approximation' for predicting the properties of electric arcs. Under this approximation, local thermodynamic equilibrium (LTE) is assumed, with a particular mesh size near the electrodes chosen to be equal to the 'diffusion length', based on D e /W, where D e is the electron diffusion coefficient and W is the electron drift velocity. This approximation overcomes the problem that the equilibrium electrical conductivity in the arc near the electrodes is almost zero, which makes accurate calculations using LTE impossible in the limit of small mesh size, as then voltages would tend towards infinity. Use of the LTE-diffusion approximation for a 200 A arc with a thermionic cathode gives predictions of total arc voltage, electrode temperatures, arc temperatures and radial profiles of heat flux density and current density at the anode that are in approximate agreement with more accurate calculations which include an account of the diffusion of electric charges to the electrodes, and also with experimental results. Calculations, which include diffusion of charges, agree with experimental results of current and heat flux density as a function of radius if the Milne boundary condition is used at the anode surface rather than imposing zero charge density at the anode

  13. A furnace for firing carbon products

    Energy Technology Data Exchange (ETDEWEB)

    Sudavskii, A M

    1979-12-05

    A furnace for firing carbon products is patented that consists of several chambers with a perforated hearth, which are interconnected by a lower and an upper reservoir with a locking fixture, and a flue. In order to intensify the firing process by increasing the specific hearth productivity, the flue is connected to the upper reservoir. A block diagram of the patented furnace is given, together with a description of its operation.

  14. Multiphase flow modelling of furnace tapholes

    OpenAIRE

    Reynolds, Quinn G.; Erwee, Markus W.

    2017-01-01

    Pyrometallurgical furnaces of many varieties make use of tapholes in order to facilitate the removal of molten process material from inside the vessel. Correct understanding and operation of the taphole is essential for optimal performance of such furnaces. The present work makes use of computational fluid dynamics models generated using the OpenFOAM® framework in order to study flow behaviour in the taphole system. Single-phase large-eddy simulation models are used to quantify the discharge ...

  15. Monitoring ARC services with GangliARC

    International Nuclear Information System (INIS)

    Cameron, D; Karpenko, D

    2012-01-01

    Monitoring of Grid services is essential to provide a smooth experience for users and provide fast and easy to understand diagnostics for administrators running the services. GangliARC makes use of the widely-used Ganglia monitoring tool to present web-based graphical metrics of the ARC computing element. These include statistics of running and finished jobs, data transfer metrics, as well as showing the availability of the computing element and hardware information such as free disk space left in the ARC cache. Ganglia presents metrics as graphs of the value of the metric over time and shows an easily-digestable summary of how the system is performing, and enables quick and easy diagnosis of common problems. This paper describes how GangliARC works and shows numerous examples of how the generated data can quickly be used by an administrator to investigate problems. It also presents possibilities of combining GangliARC with other commonly-used monitoring tools such as Nagios to easily integrate ARC monitoring into the regular monitoring infrastructure of any site or computing centre.

  16. FURNACE INJECTION OF ALKALINE SORBENTS FOR SULFURIC ACID CONTROL; SEMIANNUAL

    International Nuclear Information System (INIS)

    Gary M. Blythe

    2002-01-01

    This document summarizes progress on Cooperative Agreement DE-FC26-99FT40718, Furnace Injection of Alkaline Sorbents for Sulfuric Acid Control, during the time period October 1, 2001 through March 31, 2002. The objective of this project is to demonstrate the use of alkaline reagents injected into the furnace of coal-fired boilers as a means of controlling sulfuric acid emissions. The coincident removal of hydrochloric acid and hydrofluoric acid is also being determined, as is the removal of arsenic, a known poison for NO(sub X) selective catalytic reduction (SCR) catalysts. EPRI, the Tennessee Valley Authority (TVA), FirstEnergy Corporation, American Electric Power (AEP) and the Dravo Lime Company are project co-funders. URS Corporation is the prime contractor. This is the fifth reporting period for the subject Cooperative Agreement. During the previous (fourth) period, two long-term sorbent injection tests were conducted, one on Unit 3 at FirstEnergy's Bruce Mansfield Plant (BMP) and one on Unit 1 at AEP's Gavin Plant. Those tests determined the effectiveness of injecting alkaline slurries into the upper furnace of the boiler as a means of controlling sulfuric acid emissions from these units. The alkaline slurries tested included commercially available magnesium hydroxide slurry (Gavin Plant) and a byproduct magnesium hydroxide slurry (at both Gavin and BMP). The tests showed that injecting either the commercial or the byproduct magnesium hydroxide slurry could achieve up to 70-75% overall sulfuric acid removal. At BMP, the overall removal was limited by the need to maintain acceptable electrostatic precipitator (ESP) particulate control performance. At Gavin Plant, the overall sulfuric acid removal was limited because the furnace injected sorbent was less effective at removing SO(sub 3) formed across the SCR system installed on the unit for NO(sub X) control than at removing SO(sub 3) formed in the furnace. The SO(sub 3) removal results were presented in the

  17. DC plasma arc melter technology for waste vitrification

    International Nuclear Information System (INIS)

    Hamilton, R.A.; Wittle, J.K.; Trescot, J.

    1995-01-01

    This paper describes the features and benefits of a breakthrough DC Arc Melter for the permanent treatment of all types of solid wastes including nonhazardous, hazardous and radioactive. This DC Arc Furnace system, now commercially available, is the low cost permanent solution for solid waste pollution prevention and remediation. Concern over the effective disposal of wastes generated by the industrial society, worldwide, has prompted development of technologies to address the problem. For the most part these technologies have resulted in niche solutions with limited application. The only solution that has the ability to process almost all wastes, and to recover/recycle metallic and inorganic matter, is the group of technologies known as melters. Melters have distinct advantages over traditional technologies such as incineration because melters operate at higher temperatures, are relatively unaffected by changes in the waste stream, produce a vitrified stable product, and have the capability to recover/recycle slag, metals and gas. The system, DC Plasma Arc Melter, has the lowest capital, maintenance and operating cost of any melter technology because of its patented DC Plasma Arc with graphite electrode. DC Plasma Arc Melter systems are commercially available in sizes from 50 kg/batch or 250--3,000 kg/hr on a continuous feed basis. This paper examines the design and operating benefits of a DC Plasma Arc Melter System

  18. Determination of electrical resistivity of dry coke beds

    Energy Technology Data Exchange (ETDEWEB)

    Eidem, P.A.; Tangstad, M.; Bakken, J.A. [NTNU, Trondheim (Norway)

    2008-02-15

    The electrical resistivity of the coke bed is of great importance when producing FeMn, SiMn, and FeCr in a submerged arc furnace. In these processes, a coke bed is situated below and around the electrode tip and consists of metallurgical coke, slag, gas, and metal droplets. Since the basic mechanisms determining the electrical resistivity of a coke bed is not yet fully understood, this investigation is focused on the resistivity of dry coke beds consisting of different carbonaceous materials, i.e., coke beds containing no slag or metal. A method that reliably compares the electrical bulk resistivity of different metallurgical cokes at 1500{sup o} C to 1600{sup o}C is developed. The apparatus is dimensioned for industrial sized materials, and the electrical resistivity of anthracite, charcoal, petroleum coke, and metallurgical coke has been measured. The resistivity at high temperatures of the Magnitogorsk coke, which has the highest resistivity of the metallurgical cokes investigated, is twice the resistivity of the Corus coke, which has the lowest electrical resistivity. Zdzieszowice and SSAB coke sort in between with decreasing resistivities in the respective order. The electrical resistivity of anthracite, charcoal, and petroleum coke is generally higher than the resistivity of the metallurgical cokes, ranging from about two to about eight times the resistivity of the Corus coke at 1450{sup o}C. The general trend is that the bulk resistivity of carbon materials decreases with increasing temperature and increasing particle size.

  19. Quasi-equilibrium channel model of an constant current arc

    Directory of Open Access Journals (Sweden)

    Gerasimov Alexander V.

    2003-01-01

    Full Text Available The rather simple method of calculation of electronic and gas temperature in the channel of arc of plasma generator is offered. This method is based on self-consistent two-temperature channel model of an electric arc. The method proposed enables to obtain radial allocation of gas and electronic temperatures in a non-conducting zone of an constant current arc, for prescribed parameters of discharge (current intensity and power of the discharge, with enough good precision. The results obtained can be used in model and engineering calculations to estimate gas and electronic temperatures in the channel of an arc plasma generator.

  20. Arc plasma devices: Evolving mechanical design from numerical

    Indian Academy of Sciences (India)

    A recipe for obtaining mechanical design of arc plasma devices from numerical ... to the plasma of the mixture of molecular gases like nitrogen and oxygen. ... Temperature field, associated fluid dynamics and electrical characteristics of a ...

  1. Industrial furnace with improved heat transfer

    Energy Technology Data Exchange (ETDEWEB)

    Hoetzl, M.; Lingle, T.M.

    1993-07-20

    A method is described for effecting improved heat transfer with in an industrial furnace having a cylindrical furnace section, a door at one end of the furnace section, an end plate at the opposite end of the section a circular fan plate concentrically positioned within the furnace section to define a cylindrical fan chamber between the plate and the end section with a fan there between and a heat treat chamber between the plate and the door, the fan plate defining a non-orificing annular space extending between the interior of the cylindrical furnace section and the outer edge of the plate, the plate having a centrally located under-pressure opening extending there through and a plurality of circumferentially spaced tubular heating elements extending through the annular space into the heat treating chamber, the method comprising the steps of: (a) heating the heating elements to a temperature which is hotter that the temperature of the work within the heat treating chamber; (b) rotating the fan at a speed sufficient to form a portion of the furnace atmosphere as a wind mass swirling about the fan chamber; (c) propagating the wind mass through the annular space into the heat treating chamber as a swirling wind mass in the form of an annulus, the wind mass impinging the heating elements to establish heat transfer contact therewith while the mass retains its annulus shape until contacting the door and without any significant movement of the wind mass into the center of the heat treating chamber; (d) drawing the wind mass through the under-pressure zone after the wind mass comes into heat transfer contact with the work in the heat treating chamber; and (e) thereafter heating the work by radiation from the beating elements at high furnace temperatures in excess of about 1,600 F.

  2. Comparison of a burning mass ceramics coating in laboratory furnace and instrustrial furnace

    International Nuclear Information System (INIS)

    Soares, R.A.L.; Castro, J.R. de S.

    2012-01-01

    This work intends to analyze the differences obtained in the technological properties of a ceramic coating after firing in two distinct environments, laboratory furnace and industrial furnace. For this, was characterized a ceramic mass used in the production of porous coating. The analyzes were performed chemical, mineralogical and thermal mass in that. The specimens were obtained by compacting and burned in the maximum temperature of 1140 deg C in two furnaces, laboratory and industrial. The technological tests were performed linear shrinkage, water absorption, bulk density and mechanical strength. The microstructure was evaluated by ray-X diffraction and scanning electron microscopy. The results showed that both furnaces provided significant differences in analyzed specimens, such as increased strength and low water absorption in the fired samples in a laboratory furnace, for example. (author)

  3. Easily controlled dye doped phosphorescent OLEDs with evaporation rate in single furnace

    Energy Technology Data Exchange (ETDEWEB)

    Mahmoudi, Malek; Janghouri, Mohammad; Mohajerani, Ezeddin, E-mail: e-mohajerani@sbu.ac.ir

    2015-04-15

    Electrical and optical characteristic, surface morphology and energy transfer of Ir(ppy){sub 3}:PtTPP were studied as a function of thermal evaporation rate. We have investigated the effect of various evaporation rates for mixture of dyes using single furnace method. When the deposition rate increased from 0.5 to 5 Ǻ/s, the luminescence efficiency, current density and energy transfer of OLED increased. AFM measurements showed that the surface roughness of the Ir(ppy){sub 3}:PtTPP films decreased with increasing deposition rates. These blends show excellent red emitting guest–host system with easier deposition rate control. - Highlights: • Thermal evaporation rate is used to control the doping by using single furnace. • The advantages of using single furnace are discussed. • It is shown that the evaporation rate also affects the surface roughness.

  4. Optical arc sensor using energy harvesting power source

    Science.gov (United States)

    Choi, Kyoo Nam; Rho, Hee Hyuk

    2016-06-01

    Wireless sensors without external power supply gained considerable attention due to convenience both in installation and operation. Optical arc detecting sensor equipping with self sustaining power supply using energy harvesting method was investigated. Continuous energy harvesting method was attempted using thermoelectric generator to supply standby power in micro ampere scale and operating power in mA scale. Peltier module with heat-sink was used for high efficiency electricity generator. Optical arc detecting sensor with hybrid filter showed insensitivity to fluorescent and incandescent lamps under simulated distribution panel condition. Signal processing using integrating function showed selective arc discharge detection capability to different arc energy levels, with a resolution below 17J energy difference, unaffected by bursting arc waveform. The sensor showed possibility for application to arc discharge detecting sensor in power distribution panel. Also experiment with proposed continuous energy harvesting method using thermoelectric power showed possibility as a self sustainable power source of remote sensor.

  5. Optical arc sensor using energy harvesting power source

    Energy Technology Data Exchange (ETDEWEB)

    Choi, Kyoo Nam, E-mail: knchoi@inu.ac.kr; Rho, Hee Hyuk, E-mail: rdoubleh0902@inu.ac.kr [Dept. of Information and Telecommunication Engineering Incheon National University Incheon 22012 (Korea, Republic of)

    2016-06-03

    Wireless sensors without external power supply gained considerable attention due to convenience both in installation and operation. Optical arc detecting sensor equipping with self sustaining power supply using energy harvesting method was investigated. Continuous energy harvesting method was attempted using thermoelectric generator to supply standby power in micro ampere scale and operating power in mA scale. Peltier module with heat-sink was used for high efficiency electricity generator. Optical arc detecting sensor with hybrid filter showed insensitivity to fluorescent and incandescent lamps under simulated distribution panel condition. Signal processing using integrating function showed selective arc discharge detection capability to different arc energy levels, with a resolution below 17 J energy difference, unaffected by bursting arc waveform. The sensor showed possibility for application to arc discharge detecting sensor in power distribution panel. Also experiment with proposed continuous energy harvesting method using thermoelectric power showed possibility as a self sustainable power source of remote sensor.

  6. Electricity

    International Nuclear Information System (INIS)

    Tombs, F.

    1983-01-01

    The subject is discussed, with particular reference to the electricity industry in the United Kingdom, under the headings; importance and scope of the industry's work; future fuel supplies (estimated indigenous fossil fuels reserves); outlook for UK energy supplies; problems of future generating capacity and fuel mix (energy policy; construction programme; economics and pricing; contribution of nuclear power - thermal and fast reactors; problems of conversion of oil-burning to coal-burning plant). (U.K.)

  7. Auroral-arc splitting by intrusion of a new convection channel

    Directory of Open Access Journals (Sweden)

    H. U. Frey

    Full Text Available During a run of the Common Programme Three of the EISCAT radar the splitting of an auroral arc was observed by high time-resolution, ground-based cameras when the UHF radar beam was close to the arc. The evening eastward electrojet situation with a large-scale northward ionospheric electric field was disturbed by the intrusion of a convection channel with southward electric field from the east. The interaction of the new convection channel with the auroral arc caused changes in arc brightness and arc splitting, i.e. the creation of a new arc parallel to the pre-existing auroral arc. The event is described as one possibility for the creation of parallel arcs during slightly disturbed magnetic conditions far from the Harang discontinuity.

  8. Auroral-arc splitting by intrusion of a new convection channel

    Directory of Open Access Journals (Sweden)

    H. U. Frey

    1996-12-01

    Full Text Available During a run of the Common Programme Three of the EISCAT radar the splitting of an auroral arc was observed by high time-resolution, ground-based cameras when the UHF radar beam was close to the arc. The evening eastward electrojet situation with a large-scale northward ionospheric electric field was disturbed by the intrusion of a convection channel with southward electric field from the east. The interaction of the new convection channel with the auroral arc caused changes in arc brightness and arc splitting, i.e. the creation of a new arc parallel to the pre-existing auroral arc. The event is described as one possibility for the creation of parallel arcs during slightly disturbed magnetic conditions far from the Harang discontinuity.

  9. Current transfer in dc non-transferred arc plasma torches

    International Nuclear Information System (INIS)

    Ghorui, S; Sahasrabudhe, S N; Das, A K

    2010-01-01

    Fundamentals of current transfer to the anodes in dc non-transferred arc plasma torches are investigated. Specially designed anodes made of three mutually isolated sections and external dc axial magnetic fields of various strengths are utilized to explore the conditions for different diffused and constricted attachments of the arc with the anode. A number of new facts are revealed in the exercise. Under constricted attachment, formation of arc root takes place. Spontaneous and magnetically induced movements of the arc root, their dependence on the arc current and the strength of the external magnetic field, most probable arc root velocity, variation of the root velocity with strength of the applied magnetic field, the effect of swirl on the rotational speed of the arc root are some of the important features investigated. Two new techniques are introduced: one for measurement of the arc root diameter and the other for determination of the negative electric field in the boundary layer over the anode. While the first one exploits the rigid column behaviour of the arcs, the second one utilizes the shooting back of the residual electrons over an arc spot. Sample calculations are provided.

  10. Characteristics of Atmospheric Pressure Rotating Gliding Arc Plasmas

    Science.gov (United States)

    Zhang, Hao; Zhu, Fengsen; Tu, Xin; Bo, Zheng; Cen, Kefa; Li, Xiaodong

    2016-05-01

    In this work, a novel direct current (DC) atmospheric pressure rotating gliding arc (RGA) plasma reactor has been developed for plasma-assisted chemical reactions. The influence of the gas composition and the gas flow rate on the arc dynamic behaviour and the formation of reactive species in the N2 and air gliding arc plasmas has been investigated by means of electrical signals, high speed photography, and optical emission spectroscopic diagnostics. Compared to conventional gliding arc reactors with knife-shaped electrodes which generally require a high flow rate (e.g., 10-20 L/min) to maintain a long arc length and reasonable plasma discharge zone, in this RGA system, a lower gas flow rate (e.g., 2 L/min) can also generate a larger effective plasma reaction zone with a longer arc length for chemical reactions. Two different motion patterns can be clearly observed in the N2 and air RGA plasmas. The time-resolved arc voltage signals show that three different arc dynamic modes, the arc restrike mode, takeover mode, and combined modes, can be clearly identified in the RGA plasmas. The occurrence of different motion and arc dynamic modes is strongly dependent on the composition of the working gas and gas flow rate. supported by National Natural Science Foundation of China (No. 51576174), the Specialized Research Fund for the Doctoral Program of Higher Education of China (No. 20120101110099) and the Fundamental Research Funds for the Central Universities (No. 2015FZA4011)

  11. Industrial and process furnaces principles, design and operation

    CERN Document Server

    Jenkins, Barrie

    2014-01-01

    Furnaces sit at the core of all branches of manufacture and industry, so it is vital that these are designed and operated safely and effi-ciently. This reference provides all of the furnace theory needed to ensure that this can be executed successfully on an industrial scale. Industrial and Process Furnaces: Principles, 2nd Edition provides comprehensive coverage of all aspects of furnace operation and design, including topics essential for process engineers and operators to better understand furnaces. This includes: the combustion process and its control, furnace fuels, efficiency,

  12. Sheath and arc-column voltages in high-pressure arc discharges

    International Nuclear Information System (INIS)

    Benilov, M S; Benilova, L G; Li Heping; Wu Guiqing

    2012-01-01

    Electrical characteristics of a 1 cm-long free-burning atmospheric-pressure argon arc are calculated by means of a model taking into account the existence of a near-cathode space-charge sheath and the discrepancy between the electron and heavy-particle temperatures in the arc column. The computed arc voltage exhibits a variation with the arc current I similar to the one revealed by the experiment and exceeds experimental values by no more than approximately 2 V in the current range 20-175 A. The sheath contributes about two-thirds or more of the arc voltage. The LTE model predicts a different variation of the arc voltage with I and underestimates the experimental values appreciably for low currents but by no more than approximately 2 V for I ≳ 120 A. However, the latter can hardly be considered as a proof of unimportance of the space-charge sheath at high currents: the LTE model overestimates both the resistance of the bulk of the arc column and the resistance of the part of the column that is adjacent to the cathode, and this overestimation to a certain extent compensates for the neglect of the voltage drop in the sheath. Furthermore, if the latter resistance were evaluated in the framework of the LTE model in an accurate way, then the overestimation would be still much stronger and the obtained voltage would significantly exceed those observed in the experiment.

  13. 40 CFR 60.271a - Definitions.

    Science.gov (United States)

    2010-07-01

    ..., dampers, etc.) used to capture or transport particulate matter generated by an electric arc furnace or AOD... PERFORMANCE FOR NEW STATIONARY SOURCES Standards of Performance for Steel Plants: Electric Arc Furnaces and... materials into the top of an electric arc furnace or the addition of molten steel or other materials into...

  14. Measure Guideline. High Efficiency Natural Gas Furnaces

    Energy Technology Data Exchange (ETDEWEB)

    Brand, L. [Partnership for Advanced Residential Retrofit (PARR), Des Plaines, IL (United States); Rose, W. [Partnership for Advanced Residential Retrofit (PARR), Des Plaines, IL (United States)

    2012-10-01

    This measure guideline covers installation of high-efficiency gas furnaces, including: when to install a high-efficiency gas furnace as a retrofit measure; how to identify and address risks; and the steps to be used in the selection and installation process. The guideline is written for Building America practitioners and HVAC contractors and installers. It includes a compilation of information provided by manufacturers, researchers, and the Department of Energy as well as recent research results from the Partnership for Advanced Residential Retrofit (PARR) Building America team.

  15. Design of a rotating-hearth furnace

    Energy Technology Data Exchange (ETDEWEB)

    Behrens, H A [LOI Industrieofenanlagen G.m.b.H., Essen (Germany, F.R.)

    1979-09-01

    Part I of this paper is intended to present a review of the theory of heating round stock of a length considerably exceeding the diameter. It is permissible to neglect heating from the ends of the cylinders. With short and thick ingots as used in pilgrim mills, for instance, such simplification is not possible. The method for calculating the waste gas temperature can also be used for the remaining furnace sections provided certain conditions are allowed for and computational procedures observed. Part II of the paper will deal with this and with the major design features of rotating-hearth furnaces.

  16. Process and furnace for working bituminous materials

    Energy Technology Data Exchange (ETDEWEB)

    Klotzer, M

    1921-06-28

    A process for working up bitumen-containing materials, such as coal, peat and shale is characterized in that the material in thin-height batches with constant shaking by means of forward and backward movement of an elongated horizontal hearth heated underneath on which the material freely lies and on which it is moved in the furnace, through a single narrow furnace space with zone-wise heating of the hearth. A drying zone, a spent-material removal zone, and a carbonization zone are provided. Under separate hoods the gases and vapors are removed from these zones.

  17. Measure Guideline: High Efficiency Natural Gas Furnaces

    Energy Technology Data Exchange (ETDEWEB)

    Brand, L.; Rose, W.

    2012-10-01

    This Measure Guideline covers installation of high-efficiency gas furnaces. Topics covered include when to install a high-efficiency gas furnace as a retrofit measure, how to identify and address risks, and the steps to be used in the selection and installation process. The guideline is written for Building America practitioners and HVAC contractors and installers. It includes a compilation of information provided by manufacturers, researchers, and the Department of Energy as well as recent research results from the Partnership for Advanced Residential Retrofit (PARR) Building America team.

  18. Glass Furnace Project, October 1982-March 1983

    International Nuclear Information System (INIS)

    Armstrong, K.M.; Klingler, L.M.

    1983-01-01

    In the Glass Furnace Project currently under way at Mound, a treatment technology for low-level radioactive waste is being evaluated that will combine volume reduction and immobilization in one step. Initial work focused on demonstrating the ability of the furnace to efficiently incinerate nonradioactive, simulated power-plant waste and on determining the adequacy of immobilization in a soda-lime silica matrix. Further evaluation of the system will involve a demonstration of the combustion and containment of radioactive waste. In preparation for this next phase of the program, preliminary investigation and design work were conducted during the past six months. 5 figures, 1 table

  19. Waste and dust utilisation in shaft furnaces

    Directory of Open Access Journals (Sweden)

    Senk, D.

    2005-12-01

    Full Text Available Wastes and dusts from steel industry, non-ferrous metallurgy and other branches can be utilized e.g. in agglomeration processes (sintering, pelletizing or briquetting and by injection into shaft furnaces. This paper deals with the second way. Combustion and reduction behaviour of iron- and carbon-rich metallurgical dusts and sludges containing lead, zinc and alkali as well as other wastes with and without pulverized coal (PC has been studied when injecting into shaft furnaces. Following shaft furnaces have been examined: blast furnace, cupola furnace, OxiCup furnace and imperial-smelting furnace. Investigations have been done at laboratory and industrial scale. Some dusts and wastes under certain conditions can be not only reused but can also improve combustion efficiency at the tuyeres as well as furnace performance and productivity.

    Los residuos y polvos de filtro provenientes de la industria siderúrgica, de la obtención de metales no ferrosos y de otras industrias, pueden ser utilizados, por ejemplo, en procesos de aglomeración como sintetizado, peletizado o briqueteado. En su caso, estos pueden ser inyectados en los hornos de cuba. Este artículo se enfoca a la inyección de estos materiales en los hornos de cuba. El comportamiento de la combustión y reducción de los polvos ricos en hierro y carbono y también lodos que contienen plomo, zinc y compuestos alcalinos y otros residuos con o sin carbón pulverizado (CP fue examinado, cuando se inyectaron en hornos de cuba. Los siguientes hornos de cuba fueron examinados: Horno alto, cubilote, OxiCup y horno de cuba Imperial Smelting. Las investigaciones se llevaron a cabo a escala de laboratorio e industrial. Algunos residuos y polvos bajo ciertas condiciones, no sólo pueden ser reciclados, sino también mejoran la eficiencia de combustión en las toberas, la operación y productividad del horno.

  20. Arc generation from sputtering plasma-dielectric inclusion interactions

    International Nuclear Information System (INIS)

    Wickersham, C.E. Jr.; Poole, J.E.; Fan, J.S.

    2002-01-01

    Arcing during sputter deposition and etching is a significant cause of particle defect generation during device fabrication. In this article we report on the effect of aluminum oxide inclusion size, shape, and orientation on the propensity for arcing during sputtering of aluminum targets. The size, shape, and orientation of a dielectric inclusion plays a major role in determining the propensity for arcing and macroparticle emission. In previous studies we found that there is a critical inclusion size required for arcing to occur. In this article we used high-speed videos, electric arc detection, and measurements of particle defect density on wafers to study the effect of Al 2 O 3 inclusion size, shape, and orientation on arc rate, intensity, and silicon wafer particle defect density. We found that the cross-sectional area of the inclusion exposed to the sputtering plasma is the critical parameter that determines the arc rate and rate of macroparticle emission. Analysis of the arc rate, particle defect density, and the intensity of the optical emission from the arcing plasma indicates that the critical aluminum oxide inclusion area for arcing is 0.22±0.1 mm2 when the sputtering plasma sheath dark-space λ d , is 0.51 mm. Inclusions with areas greater than this critical value readily induce arcing and macroparticle ejection during sputtering. Inclusions below this critical size do not cause arcing or macroparticle ejection. When the inclusion major axis is longer than 2λ d and lies perpendicular to the sputter erosion track tangent, the arcing activity increases significantly over the case where the inclusion major axis lies parallel to the erosion track tangent

  1. Using arc voltage to locate the anode attachment in plasma arc cutting

    International Nuclear Information System (INIS)

    Osterhouse, D J; Heberlein, J V R; Lindsay, J W

    2013-01-01

    Plasma arc cutting is a widely used industrial process in which an electric arc in the form of a high velocity plasma jet is used to melt and blow away metal. The arc attaches inside the resulting cut slot, or kerf, where it both provides a large heat flux and determines the flow dynamics of the plasma. Knowledge of the position of the arc attachment is essential for understanding the phenomena present at the work piece. This work presents a new method of measuring the location of the arc attachment in which the arc voltage is measured during the cutting of a range of work piece thicknesses. The attachment location is then interpreted from the voltages. To support the validity of this method, the kerf shape, dross particle size and dross adhesion to the work piece are also observed. While these do not conclusively give an attachment location, they show patterns which are consistent with the attachment location found from the voltage measurements. The method is demonstrated on the cutting of mild steel, where the arc attachment is found to be stationary in the upper portion of the cut slot and in reasonable agreement with existing published findings. For a process optimized for the cutting of 12.7 mm mild steel, the attachment is found at a depth of 1.5–3.4 mm. For a slower process optimized for the cutting of 25.4 mm mild steel, the attachment is found at a depth of 3.4–4.8 mm, which enhances heat transfer further down in the kerf, allowing cutting of the thicker work piece. The use of arc voltage to locate the position of the arc attachment is unique when compared with existing methods because it is entirely independent of the heat distribution and visualization techniques. (paper)

  2. FURNACE INJECTION OF ALKALINE SORBENTS FOR SULFURIC ACID REMOVAL

    Energy Technology Data Exchange (ETDEWEB)

    Gary M. Blythe

    2004-01-01

    The objective of this project has been to demonstrate the use of alkaline reagents injected into the furnace of coal-fired boilers as a means of controlling sulfuric acid emissions. The project was co-funded by the U.S. DOE National Energy Technology Laboratory under Cooperative Agreement DE-FC26-99FT40718, along with EPRI, the American Electric Power Company (AEP), FirstEnergy Corporation, the Tennessee Valley Authority, and Carmeuse North America. Sulfuric acid controls are becoming of increased interest for coal-fired power generating units for a number of reasons. In particular, sulfuric acid can cause plant operation problems such as air heater plugging and fouling, back-end corrosion, and plume opacity. These issues will likely be exacerbated with the retrofit of selective catalytic reduction (SCR) for NOX control, as SCR catalysts are known to further oxidize a portion of the flue gas SO{sub 2} to SO{sub 3}. The project tested the effectiveness of furnace injection of four different magnesium-based or dolomitic alkaline sorbents on full-scale utility boilers. These reagents were tested during one- to two-week tests conducted on two FirstEnergy Bruce Mansfield Plant (BMP) units. One of the sorbents tested was a magnesium hydroxide slurry byproduct from a modified Thiosorbic{reg_sign} Lime wet flue gas desulfurization process. The other three sorbents are available commercially and include dolomite, pressure-hydrated dolomitic lime, and commercially available magnesium hydroxide. The dolomite reagent was injected as a dry powder through out-of-service burners. The other three reagents were injected as slurries through air-atomizing nozzles inserted through the front wall of the upper furnace. After completing the four one- to two-week tests, the most promising sorbents were selected for longer-term (approximately 25-day) full-scale tests on two different units. The longer-term tests were conducted to confirm sorbent effectiveness over extended operation on two

  3. Tokamak ARC damage

    International Nuclear Information System (INIS)

    Murray, J.G.; Gorker, G.E.

    1985-01-01

    Tokamak fusion reactors will have large plasma currents of approximately 10 MA with hundreds of megajoules stored in the magnetic fields. When a major plasma instability occurs, the disruption of the plasma current induces voltage in the adjacent conducting structures, giving rise to large transient currents. The induced voltages may be sufficiently high to cause arcing across sector gaps or from one protruding component to another. This report reviews a tokamak arcing scenario and provides guidelines for designing tokamaks to minimize the possibility of arc damage

  4. Tokamak ARC damage

    Energy Technology Data Exchange (ETDEWEB)

    Murray, J.G.; Gorker, G.E.

    1985-01-01

    Tokamak fusion reactors will have large plasma currents of approximately 10 MA with hundreds of megajoules stored in the magnetic fields. When a major plasma instability occurs, the disruption of the plasma current induces voltage in the adjacent conducting structures, giving rise to large transient currents. The induced voltages may be sufficiently high to cause arcing across sector gaps or from one protruding component to another. This report reviews a tokamak arcing scenario and provides guidelines for designing tokamaks to minimize the possibility of arc damage.

  5. A new multi-purpose furnace for the preparation of compounds, alloys and single crystals

    International Nuclear Information System (INIS)

    Spirlet, J.-C.; Wellum, R.

    2004-01-01

    A new modular multi-purpose furnace has been designed and the prototype constructed. This furnace was a development utilizing more than two decades of experience at the JRC establishment, Karlsruhe, to bring together the possibility of several techniques that normally require separate, expensive facilities. With this new modular device, different functions are provided by exchanging the head of the furnace while leaving the base as a permanent fixture. The processes can be carried out in high vacuum (10 -6 Pa) or in the presence of high-purity gases, e.g., argon. The modules developed allow the following processes to be carried out: Arc melting, levitation melting, resistance and radio-frequency heating in a crucible, single-crystal growth by various techniques, and electron-beam heating. The rationale behind the development was to produce a device capable of many functions but at an acceptable cost so as to make the various techniques available to a wide range of research and development institutes. A full description of the apparatus is given, outlining the range of the methods which can be applied to the production of high-purity advanced materials for research purposes

  6. Blast furnace hearth lining: post mortem analysis

    Energy Technology Data Exchange (ETDEWEB)

    Almeida, Bruno Vidal de; Vernilli Junior, Fernando, E-mail: bva@usp.br [Universidade de Sao Paulo (USP), Lorena, SP (Brazil). Escola de Engenharia; Neves; Elton Silva; Silva, Sidiney Nascimento [Companhia Siderugica Nacional (CSN), Rio de Janeiro, RJ (Brazil)

    2017-05-15

    The main refractory lining of blast furnace hearth is composed by carbon blocks that operates in continuous contact with hot gases, liquid slag and hot metal, in temperatures above 1550 deg C for 24 hours a day. To fully understand the wear mechanism that acts in this refractory layer system it was performed a Post Mortem study during the last partial repair of this furnace. The samples were collected from different parts of the hearth lining and characterized using the following techniques: Bulk Density and Apparent Porosity, X-Ray Fluorescence, X-ray Diffraction, Scanning Electron Microscopy with Energy-dispersive X-Ray Spectroscopy. The results showed that the carbon blocks located at the opposite side of the blast furnace tap hole kept its main physicochemical characteristics preserved even after the production of 20x10{sup 6} ton of hot metal. However, the carbon blocks around the Tap Hole showed infiltration by hot metal and slag and it presents a severe deposition of zinc and sulfur over its carbon flakes. The presence of these elements is undesired because it reduces the physic-chemical stability of this refractory system. This deposition found in the carbon refractory is associated with impurities present in the both coke and the sinter feed used in this blast furnace in the last few years. (author)

  7. Thermal model of the whole element furnace

    International Nuclear Information System (INIS)

    Cramer, E.R.

    1998-01-01

    A detailed thermal analysis was performed to calculate temperatures in the whole element test furnace that is used to conduct drying studies of N-Reactor fuel. The purpose of this analysis was to establish the thermal characteristics of the test system and to provide a basis for post-test analysis

  8. Sintering furnace for remote fuel fabrication

    International Nuclear Information System (INIS)

    Bowen, W.W.

    1978-10-01

    Component testing and evaluation of a chemical vapor deposition Re/W muffle has been initiated. Hydrogen permeation testing and thermal cycling behavior will be evaluated. Fabrication of prototype 10-12 Kg furnace is scheduled for completion late in 1979, at which time testing of the system will be initiated

  9. Blast furnace hearth lining: post mortem analysis

    International Nuclear Information System (INIS)

    Almeida, Bruno Vidal de; Vernilli Junior, Fernando

    2017-01-01

    The main refractory lining of blast furnace hearth is composed by carbon blocks that operates in continuous contact with hot gases, liquid slag and hot metal, in temperatures above 1550 deg C for 24 hours a day. To fully understand the wear mechanism that acts in this refractory layer system it was performed a Post Mortem study during the last partial repair of this furnace. The samples were collected from different parts of the hearth lining and characterized using the following techniques: Bulk Density and Apparent Porosity, X-Ray Fluorescence, X-ray Diffraction, Scanning Electron Microscopy with Energy-dispersive X-Ray Spectroscopy. The results showed that the carbon blocks located at the opposite side of the blast furnace tap hole kept its main physicochemical characteristics preserved even after the production of 20x10"6 ton of hot metal. However, the carbon blocks around the Tap Hole showed infiltration by hot metal and slag and it presents a severe deposition of zinc and sulfur over its carbon flakes. The presence of these elements is undesired because it reduces the physic-chemical stability of this refractory system. This deposition found in the carbon refractory is associated with impurities present in the both coke and the sinter feed used in this blast furnace in the last few years. (author)

  10. Aerosol and particle transport in biomass furnaces

    NARCIS (Netherlands)

    Kemenade, van H.P.; Obernberger, G.

    2005-01-01

    The particulate emissions of solid fuel fired furnaces typically exhibit a bimodal distribution: a small peak in the range of 0.1 mm and a larger one above 10 mm. The particles with sizes above 10 mm are formed by a mechanical process like disintegration of the fuel after combustion, or erosion,

  11. Furnace for distillation of shales, etc

    Energy Technology Data Exchange (ETDEWEB)

    Germain-Clergault, M

    1863-07-09

    Practical experience and continuous operation of 55 retorts for 5 years of the system of vertical retorts patented in 1857 (French Patent 18,422) has shown the advantages resulting from this furnace which gives over a mean yield of 5% of Auton shale, which is /sup 1///sub 2/% more than the old systems with a fuel economy varying from 15 to 20%.

  12. Effect of electropolishing on vacuum furnace design

    Directory of Open Access Journals (Sweden)

    Sutanwi Lahiri

    2015-03-01

    Full Text Available The use of thermal shields of materials having low emissivity in vacuum furnaces is well-known. However, the surface condition of the heat shields is one of the most important factors governing their efficiency as radiation resistances. The emissivity of the thermal shields dictates the power rating of the heaters in furnace design. The unpolished materials used in the heater tests showed poor performance leading to loss of a signi­ficant percentage of the input power. The present work deals with the refur­bishment of the radiation heat shields used in a furnace for heating graphite structure. The effect of refurbishment of the heat shields by the buffing and subsequently electro­polishing was found to improve the performance of the shields as heat reflectors. The com­position of the electrolyte was chosen in such a way that the large shields of Mo, Inconel and SS can be polished using the same reagents in different ratios. The present work deals with the development of a standard electropolishing procedure for large metallic sheets and subsequently qualifying them by roughness and emissivity measure­ments. The improvement noted in the shielding efficiency of the furnace in the subsequent runs is also discussed here.

  13. Home Electrical Safety Checklist

    Science.gov (United States)

    ... Interrupter Protection for Pools, Spas and Hot Tubs Metal Ladders and Electricity Don’t Mix Electrocution Hazard with Do-It-Yourself Repairs of Microwave Ovens Preventing Home Fires: Arc Fault Circuit Interrupters (AFCIs) Power up with ...

  14. Dynamics and control of a gas-fired furnace

    NARCIS (Netherlands)

    Roffel, B.; Rijnsdorp, J.E.

    1974-01-01

    A non-linear model has been developed for a gas-fired furnace in which oil is heated. The model is applicable from minimum to maximum heat load of the furnace. The dynamics of the model have been compared to experimental results, which were obtained for a pilot-scale furnace. They are in good

  15. Technique eliminates high voltage arcing at electrode-insulator contact area

    Science.gov (United States)

    Mealy, G.

    1967-01-01

    Coating the electrode-insulator contact area with silver epoxy conductive paint and forcing the electrode and insulator tightly together into a permanent connection, eliminates electrical arcing in high-voltage electrodes supplying electrical power to vacuum facilities.

  16. Modeling of aerodynamics in vortex furnace

    Energy Technology Data Exchange (ETDEWEB)

    Anufriev, I.; Krasinsky, D. [Russian Academy of Sciences, Novosibirsk (Russian Federation). Inst. of Thermophysics; Salomatov, V.; Anikin, Y.; Sharypov, O. [Russian Academy of Sciences, Novosibirsk (Russian Federation). Inst. of Thermophysics; Novosibirsk State Univ. (Russian Federation); Enkhjargal, Kh. [Mongol Univ. of Science and Technology, Ulan Bator (Mongolia)

    2013-07-01

    At present, the torch burning technology of pulverized-coal fuel in vortex flow is one of the most prospective and environmentally-friendly combustion technologies of low-grade coals. Appropriate organization of aerodynamics may influence stability of temperature and heat flux distributions, increase slag catching, and reduce toxic emissions. Therefore, from scientific point of view it is interesting to investigate aerodynamics in the devices aiming at justification of design and operating parameters for new steam generators with vortex furnace, and upgrade of existing boiler equipment. The present work is devoted to physical and mathematical modeling of interior aerodynamics of vortex furnace of steam generator of thermal power plants. Research was carried out on the air isothermal model which geometry was similar to one section of the experimental- industrial boiler TPE-427 of Novosibirsk TPS-3. Main elements of vortex furnace structure are combustion chamber, diffuser, and cooling chamber. The model is made from organic glass; on the front wall two rectangular nozzles (through which compressed air is injected) are placed symmetrically at 15 to the horizon. The Laser Doppler Velocimeter LAD-05 was used for non-contact measurement of vortex flow characteristics. Two velocity components in the XY-plane (in different cross- sections of the model) were measured in these experiments. Reynolds number was 3.10{sup 5}. Numerical simulation of 3-D turbulent isothermal flow was performed with the use of CFD package FLUENT. Detailed structure of the flow in vortex furnace model has been obtained in predictions. The distributions of main flow characteristics (pressure, velocity and vorticity fields, turbulent kinetic energy) are presented. The obtained results may be used at designing boilers with vortex furnace. Computations were performed using the supercomputer NKS-160.

  17. Thermal Analysis of an Industrial Furnace

    Directory of Open Access Journals (Sweden)

    Mirko Filipponi

    2016-10-01

    Full Text Available Industries, which are mainly responsible for high energy consumption, need to invest in research projects in order to develop new managing systems for rational energy use, and to tackle the devastating effects of climate change caused by human behavior. The study described in this paper concerns the forging industry, where the production processes generally start with the heating of steel in furnaces, and continue with other processes, such as heat treatments and different forms of machining. One of the most critical operations, in terms of energy loss, is the opening of the furnace doors for insertion and extraction operations. During this time, the temperature of the furnaces decreases by hundreds of degrees in a few minutes. Because the dispersed heat needs to be supplied again through the combustion of fuel, increasing the consumption of energy and the pollutant emissions, the evaluation of the amount of lost energy is crucial for the development of systems which can contain this loss. To perform this study, CFD simulation software was used. Results show that when the door opens, because of temperature and pressure differences between the furnace and the ambient air, turbulence is created. Results also show that the amount of energy lost for an opening of 10 min for radiation, convection and conduction is equal to 5606 MJ where convection is the main contributor, with 5020 MJ. The model created, after being validated, has been applied to perform other simulations, in order to improve the energy performance of the furnace. Results show that reducing the opening time of the door saves energy and limits pollutant emissions.

  18. Vacuum arc anode phenomena

    International Nuclear Information System (INIS)

    Miller, H.C.

    1976-01-01

    A brief review of anode phenomena in vacuum arcs is presented. Discussed in succession are: the transition of the arc into the anode spot mode; the temperature of the anode before, during and after the anode spot forms; and anode ions. Characteristically the anode spot has a temperature of the order of the atmospheric boiling point of the anode material and is a copious source of vapor and energetic ions. The dominant mechanism controlling the transition of the vacuum arc into the anode spot mode appears to depend upon the electrode geometry, the electrode material, and the current waveform of the particular vacuum arc being considered. Either magnetic constriction in the gap plasma or gross anode melting can trigger the transition; indeed, a combination of the two is a common cause of anode spot formation

  19. Filtered cathodic arc source

    International Nuclear Information System (INIS)

    Falabella, S.; Sanders, D.M.

    1994-01-01

    A continuous, cathodic arc ion source coupled to a macro-particle filter capable of separation or elimination of macro-particles from the ion flux produced by cathodic arc discharge is described. The ion source employs an axial magnetic field on a cathode (target) having tapered sides to confine the arc, thereby providing high target material utilization. A bent magnetic field is used to guide the metal ions from the target to the part to be coated. The macro-particle filter consists of two straight solenoids, end to end, but placed at 45 degree to one another, which prevents line-of-sight from the arc spot on the target to the parts to be coated, yet provides a path for ions and electrons to flow, and includes a series of baffles for trapping the macro-particles. 3 figures

  20. Single-Arc IMRT?

    International Nuclear Information System (INIS)

    Bortfeld, Thomas; Webb, Steve

    2009-01-01

    The idea of delivering intensity-modulated radiation therapy (IMRT) with a multileaf collimator in a continuous dynamic mode during a single rotation of the gantry has recently gained momentum both in research and industry. In this note we investigate the potential of this Single-Arc IMRT technique at a conceptual level. We consider the original theoretical example case from Brahme et al that got the field of IMRT started. Using analytical methods, we derive deliverable intensity 'landscapes' for Single-Arc as well as standard IMRT and Tomotherapy. We find that Tomotherapy provides the greatest flexibility in shaping intensity landscapes and that it allows one to deliver IMRT in a way that comes close to the ideal case in the transverse plane. Single-Arc and standard IMRT make compromises in different areas. Only in relatively simple cases that do not require substantial intensity modulation will Single-Arc be dosimetrically comparable to Tomotherapy. Compared with standard IMRT, Single-Arc could be dosimetrically superior in certain cases if one is willing to accept the spreading of low dose values over large volumes of normal tissue. In terms of treatment planning, Single-Arc poses a more challenging optimization problem than Tomotherapy or standard IMRT. We conclude that Single-Arc holds potential as an efficient IMRT technique especially for relatively simple cases. In very complex cases, Single-Arc may unduly compromise the quality of the dose distribution, if one tries to keep the treatment time below 2 min or so. As with all IMRT techniques, it is important to explore the tradeoff between plan quality and the efficiency of its delivery carefully for each individual case. (note)

  1. AUTOMATION OF GLASS TEMPERING FURNACE BY USING PLC

    Directory of Open Access Journals (Sweden)

    Abdullah BÜYÜKYILDIZ

    2007-02-01

    Full Text Available In this study, a furnace which is used for observation of environments under high temperature, and also used for manufacturing of glasses which are resisted to high temperature has been designed and implemented. Automation of this system has been done by using PLC. Operating parameters of furnace such as materials entering, the furnace, the local temperature control of furnace, cooling control and materials outing have been sensed with Hall Effect Sensor. Furthermore, the observation of parameters of furnace on screen has been provided with SCADA software. Obtained products have been shown the system works successfully.

  2. Volatilization and redox testing in a DC arc melter: FY-93 and FY-94

    International Nuclear Information System (INIS)

    Grandy, J.D.; Sears, J.W.; Soelberg, N.R.; Reimann, G.A.; McIlwain, M.E.

    1996-07-01

    The purpose of these experiments was to study the dissolution, retention, volatilization, and trapping of transuranic radionuclide elements (TRUs), mixed fission and activation products, and high vapor pressure metals (HVPMS) during processing in a high temperature arc furnace. In all cases, surrogate elements (lanthanides) were used in place of radioactive ones. The experiments were conducted utilizing a small DC arc melter developed at the Idaho National Engineering Laboratory (INEL) Research Center (IRC). The small arc melter was originally developed in 1992 and has been used previously for waste form studies of iron enriched basalt (IEB) and IEB with zirconium and titanium additions (IEB4). Section 3 contains a description of the small arc melter and its operational capabilities are discussed in Chapter 4. The remainder of the document describes each testing program and then discusses results and findings

  3. Evaluation of residential furnace filters

    Energy Technology Data Exchange (ETDEWEB)

    Bowser, D. [Bowser Technical Inc. (Canada)

    1999-07-01

    Various filters rotated through six houses in southern Ontario during the heating season were evaluated for their filtration efficiency, including their ability to trap respirable particulate matter. Particulate levels were continuously monitored in the outside air, before and after the filter in the ducting system; also in the air in two rooms in each house. Results show that the filters performed according to their respective efficiency ratings. The integrated breathing zone exposure reading were not considered as significant as the reductions in the ducting system, dur to the fact that the integrated breathing zone exposure reflects both dust generation and dust removal mechanisms. Electronic air filters were found to produce ozone inside the home when the air-handling system was in operation. There was no evidence of any particular relationship between cleanliness and ozone production. Indoor ozone levels were always lower than outdoor levels. Continuous blower operation was found to improve filtration efficiency , however, it could result in an increase of about $250 in annual energy expenses. Bypass filters recorded significantly higher electrical energy consumption than full-flow systems. Continuous low-speed air handler fan operation appeared to be the most effective strategy. Portable air cleaners were shown to be highly effective in removing particulates in a single room. Removing footwear on entering the house, keeping major dust generators out of the house, frequent vacuuming, improving the air tightness of the house, and installing an air intake filter on the air supply may all be all be helpful in controlling exposure to particulates. 21 refs., 8 tabs., 32 figs.

  4. Multi-cathode metal vapor arc ion source

    International Nuclear Information System (INIS)

    Brown, I.G.; MacGill, R.A.

    1988-01-01

    This patent describes an apparatus for generating an ion beam. It comprises: a vacuum enclosure; a support member; cathodes; an anode; means for transporting; a source of electrical power; means for producing an electric arc; means for guiding; and means for extracting ions

  5. Investigations into electrical discharges in gases

    CERN Document Server

    Klyarfel'D, B N

    2013-01-01

    Investigations into Electrical Discharges in Gases is a compilation of scientific articles that covers the advances in the investigation of the fundamental processes occurring in electrical discharges in gases and vapors. The book details the different aspects of the whole life cycle of an arc, which include the initiation of a discharge, its transition into an arc, the lateral spread of the arc column, and the recovery of electric strength after extinction of an arc. The text also discusses the methods for the dynamic measurement of vapor density in the vicinity of electrical discharges, alon

  6. Remediation of phosphorus from electric furnace waste streams

    International Nuclear Information System (INIS)

    Hanna, J.; Jung, J.O.

    1992-01-01

    Electrothermal production of elemental phosphorus (P4) generates substantial amounts of highly toxic phossy water sludge, slag and other gaseous wastes. Because of their high phosphorus content the sludges pose potential fire hazards. In the absence of a reliable processing technology, large amounts of these hazardous wastes are accumulated at an annual rate of 1.5-2.5 million tons from current and past operations. The accumulated sludges are stored in ponds or in special containment vessels in 30 locations in 18 states including Alabama, California, Tennessee, Idaho and Montana. Serious water pollution problems will result unless these wastes are given extensive treatment to remove the elemental phosphorus. Federal regulations prohibit permanent storage of flammable wastes. This paper reports that recently, researchers at the University of Alabama have developed a two-step method for the treatment of phosphorus sludge that includes bulk removal of phosphorus by physical separation techniques followed by remediation of the residual P4 in the sludge using a novel wet air oxidation technique known as HSAD

  7. Approximate entropy—a new statistic to quantify arc and welding process stability in short-circuiting gas metal arc welding

    International Nuclear Information System (INIS)

    Cao Biao; Xiang Yuanpeng; Lü Xiaoqing; Zeng Min; Huang Shisheng

    2008-01-01

    Based on the phase state reconstruction of welding current in short-circuiting gas metal arc welding using carbon dioxide as shielding gas, the approximate entropy of welding current as well as its standard deviation has been calculated and analysed to investigate their relation with the stability of electric arc and welding process. The extensive experimental and calculated results show that the approximate entropy of welding current is significantly and positively correlated with arc and welding process stability, whereas its standard deviation is correlated with them negatively. A larger approximate entropy and a smaller standard deviation imply a more stable arc and welding process, and vice versa. As a result, the approximate entropy of welding current promises well in assessing and quantifying the stability of electric arc and welding process in short-circuiting gas metal arc welding

  8. 40 CFR 63.1651 - Definitions.

    Science.gov (United States)

    2010-07-01

    ... transfer by crane, truck, or other conveyance. Crushing and screening equipment means the crushers... resistive electrical power consumption of a submerged arc furnace, expressed as megawatts (MW). Malfunction... arc furnace means an electric submerged arc furnace that is equipped with a canopy hood above the...

  9. Effectiveness of recycling light in ultra-bright short-arc discharge lamps.

    Science.gov (United States)

    Malul, Asher; Nakar, Doron; Feuermann, Daniel; Gordon, Jeffrey M

    2007-10-17

    Recycling light back into a plasma lamp's radiant zone can enhance its radiance. Measurements are reported for the effectiveness, spectral properties and modified plasma radiance maps that result from light recycling with a specular hemispherical mirror in commercial 150 W ultrabright Xenon short-arc discharge lamps, motivated by projection, biomedical and high-temperature furnace applications. For certain spectral windows and plasma arc regions, radiance can be heightened by up to 70%. However, the overall light recycling efficiency is reduced to about half this value due to lamp geometry. The manner in which light-plasma interactions affect light recycling efficacy is also elucidated.

  10. PREPARATION OF ACTIVATED CARBON FROM SILK COTTON WOOD AND COCONUT SHELL BY PYROLISIS WITH CERAMIC FURNACE

    Directory of Open Access Journals (Sweden)

    Winarto Haryadi

    2010-06-01

    Full Text Available Preparation of activated carbon from silk cotton wood and coconut shell has been done. Carbon was made by pyrolysis process in the Muchalal furnace with 3000 watt electric power. The electric power was increased gradually from 1000, 2000 and then 3000 watt with interval 2 hours during 7 hours. Carbon was activated in Muchalal furnace with 4000 watt electric power during 2 hours and flowed with nitrogen gas. Product of the activated carbon was compared to standart product with several analysis including the surface area, acetic acid adsorption, iod adsorption and vapour adsorption. The results of analysis showed that surface area for silk cotton wood carbon, coconut shell carbon, and E.Merck product were 288.8072 m2/g, 222.9387 m2/g and 610.5543 m2/g, respectively. Acetic acid adsorption for silk cotton wood carbon, coconut shell carbon, and standart product were 157.391 mg/g, 132.791 mg/g, and 186.911 mg/g, respectively. Iodine adsorption for cotton wood carbon, coconut shell carbon, and standart product were 251.685 mg/g, 207.270 mg/g and 310.905 mg/g, respectively. Vapour adsorption for cotton wood carbon, coconut shell carbon and standart product were 12%, 4%,and 14%., respectively Key words : Activated carbon, pyrolysis, Muchalal furnace

  11. Monitoring device for glass melting furnace

    International Nuclear Information System (INIS)

    Endo, Noboru; Asano, Naoki; Higuchi, Tatsuo; Koyama, Mayumi; Hanado, Shinji.

    1995-01-01

    The device of the present invention can monitor, from a remote place, a liquid surface in a glass melting furnace for use in a solidification treatment, for example, of high level radioactive wastes. Namely, a vertical sleeve is disposed penetrating a ceiling wall of a melting vessel. A reflection mirror is disposed above the vertical sleeve and flex an optical axis. A monitoring means is disposed on the optical axis of the reflecting mirror at a spaced position. The monitoring means may have an optical telescopic means, a monitoring camera by way of a half mirror and an illumination means. The reflection mirror may be made of a metal. The monitoring device thus constituted suffer from no effects of high temperature and high radiation dose rate, thereby enabling to easily monitor the liquid surface in the melting furnace. (I.S.)

  12. Surface breakdown igniter for mercury arc devices

    Science.gov (United States)

    Bayless, John R.

    1977-01-01

    Surface breakdown igniter comprises a semiconductor of medium resistivity which has the arc device cathode as one electrode and has an igniter anode electrode so that when voltage is applied between the electrodes a spark is generated when electrical breakdown occurs over the surface of the semiconductor. The geometry of the igniter anode and cathode electrodes causes the igniter discharge to be forced away from the semiconductor surface.

  13. Dental Porcelain Furnaces: Test and Evaluation.

    Science.gov (United States)

    1988-01-01

    D Q)L a ) a) C ) C C C C c *. . 3a)0. >4 a)->4 >4 -, Z 0 -a-’- 4-% a) ( nca )m m nU Cs C ) (3 ) 11) a) a) a3) Q) a) W) a2) C C~~ >4 L > > >1 >1 4 > 4...Fig. 1) is a computerized programmable porcelain furnace with 45 open programs. This unit has a large detachable cathode -ray tube (CRT) screen which

  14. Furnaces for the distillation of coal, etc

    Energy Technology Data Exchange (ETDEWEB)

    Anderson, F A; Deacon, M; Brady, N P.W.

    1918-08-14

    A tunnel or other furnace for the distillation of coal of the kind provided with inverted pockets in its roof to collect diverse distillates in the manner described, characterized by one or more of the pockets being provided with a sloping roof whose gradient from the higher end downwards is in the direction of the forward travel of the fuel beneath it for the purposes described.

  15. Husk energy for boilers and furnaces

    Energy Technology Data Exchange (ETDEWEB)

    Deven, M.

    1985-10-01

    In view of the technical feasibility and economic viability, industries located in rice, coconut, and cotton growing areas, can easily switch over from oil/coal fired furnace/boilers to husk fired ones and thereby effect fuel economy. The banks and financial institutions will readily agree to provide finance as per directions of the governments and in some cases they also offer subsidy for development and utilization of energy saving devices.

  16. Consolidating NASA's Arc Jets

    Science.gov (United States)

    Balboni, John A.; Gokcen, Tahir; Hui, Frank C. L.; Graube, Peter; Morrissey, Patricia; Lewis, Ronald

    2015-01-01

    The paper describes the consolidation of NASA's high powered arc-jet testing at a single location. The existing plasma arc-jet wind tunnels located at the Johnson Space Center were relocated to Ames Research Center while maintaining NASA's technical capability to ground-test thermal protection system materials under simulated atmospheric entry convective heating. The testing conditions at JSC were reproduced and successfully demonstrated at ARC through close collaboration between the two centers. New equipment was installed at Ames to provide test gases of pure nitrogen mixed with pure oxygen, and for future nitrogen-carbon dioxide mixtures. A new control system was custom designed, installed and tested. Tests demonstrated the capability of the 10 MW constricted-segmented arc heater at Ames meets the requirements of the major customer, NASA's Orion program. Solutions from an advanced computational fluid dynamics code were used to aid in characterizing the properties of the plasma stream and the surface environment on the calorimeters in the supersonic flow stream produced by the arc heater.

  17. ALICE-ARC integration

    International Nuclear Information System (INIS)

    Anderlik, C; Gregersen, A R; Kleist, J; Peters, A; Saiz, P

    2008-01-01

    AliEn or Alice Environment is the Grid middleware developed and used within the ALICE collaboration for storing and processing data in a distributed manner. ARC (Advanced Resource Connector) is the Grid middleware deployed across the Nordic countries and gluing together the resources within the Nordic Data Grid Facility (NDGF). In this paper we will present our approach to integrate AliEn and ARC, in the sense that ALICE data management and job processing can be carried out on the NDGF infrastructure, using the client tools available in AliEn. The inter-operation has two aspects, one is the data management part and the second the job management aspect. The first aspect was solved by using dCache across NDGF to handle data. Therefore, we will concentrate on the second part. Solving it, was somewhat cumbersome, mainly due to the different computing models employed by AliEn and ARC. AliEN uses an Agent based pull model while ARC handles jobs through the more 'traditional' push model. The solution comes as a module implementing the functionalities necessary to achieve AliEn job submission and management to ARC enabled sites

  18. Arc generation from sputtering plasma-dielectric inclusion interactions

    CERN Document Server

    Wickersham, C E J; Fan, J S

    2002-01-01

    Arcing during sputter deposition and etching is a significant cause of particle defect generation during device fabrication. In this article we report on the effect of aluminum oxide inclusion size, shape, and orientation on the propensity for arcing during sputtering of aluminum targets. The size, shape, and orientation of a dielectric inclusion plays a major role in determining the propensity for arcing and macroparticle emission. In previous studies we found that there is a critical inclusion size required for arcing to occur. In this article we used high-speed videos, electric arc detection, and measurements of particle defect density on wafers to study the effect of Al sub 2 O sub 3 inclusion size, shape, and orientation on arc rate, intensity, and silicon wafer particle defect density. We found that the cross-sectional area of the inclusion exposed to the sputtering plasma is the critical parameter that determines the arc rate and rate of macroparticle emission. Analysis of the arc rate, particle defect...

  19. The modelling of an SF6 arc in a supersonic nozzle: II. Current zero behaviour of the nozzle arc

    International Nuclear Information System (INIS)

    Zhang, Q; Liu, J; Yan, J D; Fang, M T C

    2016-01-01

    The present work (part II) forms the second part of an investigation into the behaviour of SF 6 nozzle arc. It is concerned with the aerodynamic and electrical behaviour of a transient nozzle arc under a current ramp specified by a rate of current decay (d i /d t ) before current zero and a voltage ramp (d V /d t ) after current zero. The five flow models used in part I [1] for cold gas flow and DC nozzle arcs have been applied to study the transient arc at three stagnation pressures ( P 0 ) and two values of d i /d t for the current ramp, representing a wide range of arcing conditions. An analysis of the physical mechanisms encompassed in each flow model is given with an emphasis on the adequacy of a particular model in describing the rapidly varying arc around current zero. The critical rate of rise of recovery voltage (RRRV) is found computationally and compared with test results of Benenson et al [2]. For transient nozzle arcs, the RRRV is proportional to the square of P 0 , rather than to the square root of P 0 for DC nozzle arcs. The physical mechanisms responsible for the strong dependence of RRRV on P 0 have been investigated. The relative merits of the flow models employed are discussed. (paper)

  20. Vacuum Arc Ion Sources

    CERN Document Server

    Brown, I.

    2013-12-16

    The vacuum arc ion source has evolved into a more or less standard laboratory tool for the production of high-current beams of metal ions, and is now used in a number of different embodiments at many laboratories around the world. Applications include primarily ion implantation for material surface modification research, and good performance has been obtained for the injection of high-current beams of heavy-metal ions, in particular uranium, into particle accelerators. As the use of the source has grown, so also have the operational characteristics been improved in a variety of different ways. Here we review the principles, design, and performance of vacuum arc ion sources.

  1. On the problem of turbulent arcs modelling

    International Nuclear Information System (INIS)

    Yas'ko, O.I.

    1998-01-01

    A new hypothesis is proposed which considers mass as a charge which produces a special field during its movement likewise the electric charge creates magnetic one. This approach throws new light on vortexes formation since interaction of moving mass with the considered field exerts swirling effect. Some aspects of turbulence in flows near walls and in blown electric arc discharge were considered to validate the hypothesis in the cases of cold and high-temperature flows. The theoretical results are found to comply with experiment well. (author)

  2. On the hydrogen saturation of titanium alloys during heating billets for plastic working in gas-fired flame furnaces

    International Nuclear Information System (INIS)

    Kushakevich, S.A.; Romanova, L.A.; Bullo, P.M.

    1978-01-01

    Presented are the results of comparative investigations into titanium alloy hydridation during billet heating in gasflame and electric furnaces for forging and hot stamping. It is shown, that titanium alloys are slightly saturated with hydrogen at the temperature lower than that of polymorphic transformation. Hydrogen absorption is decelerated by a dense scale up to the moment of its loosening and peeling off. The application of protective vitreous enamels reduces the danger of impermissible hydridation. It is established, that the usage of gas-flame furnaces for billet heating is possible in the case of corresponding temperature and holding restrictions proper machining allowances and the use of protective coatings

  3. Effect of vacuum arc cathode spot distribution on breaking capacity of the arc-extinguishing chamber

    Science.gov (United States)

    Ding, Can; Yuan, Zhao; He, Junjia

    2017-10-01

    A DC circuit breaker performs a key function in breaking an intermediate-frequency (IF) current since breaking a pure IF current is equivalent to breaking a very small DC with a reverse IF current. In this study, it is found that cathode spots show a ring-shaped distribution at 2000 Hz. An arc with an uneven distribution of cathode spots has been simulated. The simulation results show that the distribution of cathode spots significantly affect the microparameter distribution of arc plasma. The current distribution on the anode side differs from that on the cathode side under the total radial electric field. Specifically, the anode current distribution is both uneven and concentrated. The applied axial magnetic field, which cannot reduce the concentrated anode current distribution effectively, might increase the concentration of the anode current. Finally, the uneven distribution of cathode spots reduces the breaking capacity of the arc-extinguishing chamber.

  4. Arc Heated Scramjet Test Facility

    Data.gov (United States)

    Federal Laboratory Consortium — The Arc Heated Scramjet Test Facility is an arc heated facility which simulates the true enthalpy of flight over the Mach number range of about 4.7 to 8 for free-jet...

  5. A Pottery Electric Kiln Using Decompression

    Science.gov (United States)

    Naoe, Nobuyuki; Yamada, Hirofumi; Nakayama, Tetsuo; Nakayama, Minoru; Minamide, Akiyuki; Takemata, Kazuya

    This paper presents a novel type electric kiln which fires the pottery using the decompression. The electric kiln is suitable for the environment and the energy saving as the pottery furnace. This paper described the baking principle and the baking characteristic of the novel type electric kiln.

  6. Sealed rotary hearth furnace with central bearing support

    Science.gov (United States)

    Docherty, James P.; Johnson, Beverly E.; Beri, Joseph

    1989-01-01

    The furnace has a hearth which rotates inside a stationary closed chamber and is supported therein on vertical cylindrical conduit which extends through the furnace floor and is supported by a single center bearing. The charge is deposited through the furnace roof on the rim of the hearth as it rotates and is moved toward the center of the hearth by rabbles. Externally generated hot gases are introduced into the furnace chamber below the hearth and rise through perforations in the hearth and up through the charge. Exhaust gases are withdrawn through the furnace roof. Treated charge drops from a center outlet on the hearth into the vertical cylindrical conduit which extends downwardly through the furnace floor to which it is also sealed.

  7. Application of Carbon Composite Bricks for Blast Furnace Hearth

    Science.gov (United States)

    Zuo, Haibin; Wang, Cong; Zhang, Jianliang; Zhao, Yongan; Jiao, Kexin

    Traditional refractory materials for blast furnace hearth lining are mainly composed of carbon bricks and the ceramic cup. However, these materials can't meet the demands for long service life design of blast furnaces. In this paper, a new refractory called carbon composite brick (CCB) was introduced, which combined the advantages of carbon bricks and the ceramic cup. In this case, the resistance of the CCB against corrosion was equal to the ceramic cup and the thermal conductivity of the CCB was equal to carbon bricks. From the results of more than 20 blast furnaces, the CCB could be well used in small blast furnaces and large blast furnaces. In the bad condition of low grade burden and high smelting intensity, the CCB gave full play to the role of cooling system, and effectively resisted the erosion of hot metal to improve the service life of blast furnaces.

  8. An observation of ionospheric convection and auroral arc motion

    International Nuclear Information System (INIS)

    Doolittle, J.H.; Mende, S.B.; Robinson, R.M.; Swenson, G.R.; Valladares, C.E.

    1990-01-01

    An all-sky imager operated at Sondre Stromfjord, Greenland has been used to make auroral measurements in correlation with data from the incoherent scatter radar. Reviewing the images as movie sequences with an apparent time compression ratio of 60 allows the eye to discern features which are not apparent in the individual frames. The faint 630 nm airglow background lying poleward of the bright auroral oval arcs appears to be structured in the time lapse observations and drifting at a uniform rate. Analysis of the motion of the airglow structures shows excellent agreement with Doppler radar measurement of the ion drift velocities. Electron density profiles derived from the radar data corroborate the existence of high altitude F-region ionization enhancements. The electron temperature in the patches was about 1,000 K and no higher than outside of the patch signifying that the patches were not produced by local soft electron precipitation. According to the radar Doppler data there was a small component of the drift velocity parallel to the arc at either side of the auroral boundary. The sense of those small components was consistent with drifts driven by a convergent electric field which would also produce an up going field aligned current. The larger component of drift velocity perpendicular to the arc appeared to be continuous on either side of the arc. This drift component shows the existence of an electric field parallel to the arc, showing that the arc was not on an equipotential. During the observations the arc moved slowly in the opposite sense to the ion drift, signifying that the auroral arc motion is not driven by the electric field impressed on the atmosphere by the magnetosphere. Calculations of the expected intensity of the 630 nm emissions are in good agreement with the measured intensities of the moving patches

  9. Thermal Arc Spray Overview

    Science.gov (United States)

    Hafiz Abd Malek, Muhamad; Hayati Saad, Nor; Kiyai Abas, Sunhaji; Mohd Shah, Noriyati

    2013-06-01

    Usage of protective coating for corrosion protection was on highly demand during the past decade; and thermal spray coating played a major part during that time. In recent years, the thermal arc spray coating becomes a popular coating. Many big players in oil and gas such as PETRONAS, EXXON MOBIL and SHELL in Malaysia tend to use the coating on steel structure as a corrosion protection. Further developments in coating processes, the devices, and raw materials have led to expansion of functional coatings and applications scope from conventional coating to specialized industries. It is widely used because of its ability to withstand high process temperature, offer advantages in efficiency, lower cost and acts as a corrosion protection. Previous research also indicated that the thermal arc spray offers better coating properties compared to other methods of spray. This paper reviews some critical area of thermal spray coating by discussing the process/parameter of thermal arc spray technology and quality control of coating. Coating performance against corrosion, wear and special characteristic of coating are also described. The field application of arc spray technology are demonstrated and reviewed.

  10. Circular arc structures

    KAUST Repository

    Bo, Pengbo; Pottmann, Helmut; Kilian, Martin; Wang, Wen Ping; Wallner, Johannes

    2011-01-01

    and connecting elements as well as repetition of costly parts. This paper proposes so-called circular arc structures as a means to faithfully realize freeform designs without giving up smooth appearance. In contrast to non-smooth meshes with straight edges where

  11. ALICE-ARC integration

    DEFF Research Database (Denmark)

    Anderlik, Csaba; Gregersen, Anders Rhod; Kleist, Josva

    2008-01-01

    Data Grid Facility (NDGF). In this paper we will present our approach to integrate AliEn and ARC, in the sense that ALICE data management and job processing can be carried out on the NDGF infrastructure, using the client tools available in AliEn. The interoperation has two aspects, one is the data...

  12. Thermal Arc Spray Overview

    International Nuclear Information System (INIS)

    Malek, Muhamad Hafiz Abd; Saad, Nor Hayati; Abas, Sunhaji Kiyai; Shah, Noriyati Mohd

    2013-01-01

    Usage of protective coating for corrosion protection was on highly demand during the past decade; and thermal spray coating played a major part during that time. In recent years, the thermal arc spray coating becomes a popular coating. Many big players in oil and gas such as PETRONAS, EXXON MOBIL and SHELL in Malaysia tend to use the coating on steel structure as a corrosion protection. Further developments in coating processes, the devices, and raw materials have led to expansion of functional coatings and applications scope from conventional coating to specialized industries. It is widely used because of its ability to withstand high process temperature, offer advantages in efficiency, lower cost and acts as a corrosion protection. Previous research also indicated that the thermal arc spray offers better coating properties compared to other methods of spray. This paper reviews some critical area of thermal spray coating by discussing the process/parameter of thermal arc spray technology and quality control of coating. Coating performance against corrosion, wear and special characteristic of coating are also described. The field application of arc spray technology are demonstrated and reviewed.

  13. THE ARC TRAIL

    African Journals Online (AJOL)

    INTRODUCTION. The project, carried out by the 1985 Conservation. Team at Durban Girls1 High School, consisted of three main aims- Awareness, Recreation and conservation, which were incorporated into the naming of the ARC trail. The trail is situated in suburban Durban where it was felt that it was important to ...

  14. ARC Software and Models

    Science.gov (United States)

    Archives RESEARCH ▼ Research Areas Ongoing Projects Completed Projects SOFTWARE CONTACT ▼ Primary Contacts Researchers External Link MLibrary Deep Blue Software Archive Most research conducted at the ARC produce software code and methodologies that are transferred to TARDEC and industry partners. These

  15. ALICE: ARC integration

    CERN Document Server

    Anderlik, C; Kleist, J; Peters, A; Saiz, P

    2008-01-01

    AliEn or Alice Environment is the Grid middleware developed and used within the ALICE collaboration for storing and processing data in a distributed manner. ARC (Advanced Resource Connector) is the Grid middleware deployed across the Nordic countries and gluing together the resources within the Nordic Data Grid Facility (NDGF). In this paper we will present our approach to integrate AliEn and ARC, in the sense that ALICE data management and job processing can be carried out on the NDGF infrastructure, using the client tools available in AliEn. The inter-operation has two aspects, one is the data management part and the second the job management aspect. The first aspect was solved by using dCache across NDGF to handle data. Therefore, we will concentrate on the second part. Solving it, was somewhat cumbersome, mainly due to the different computing models employed by AliEn and ARC. AliEN uses an Agent based pull model while ARC handles jobs through the more 'traditional' push model. The solution comes as a modu...

  16. Assessment of selected furnace technologies for RWMC waste

    International Nuclear Information System (INIS)

    Batdorf, J.; Gillins, R.; Anderson, G.L.

    1992-03-01

    This report provides a description and initial evaluation of five selected thermal treatment (furnace) technologies, in support of earlier thermal technologies scoping work for application to the Idaho National Engineering Laboratory Radioactive Waste Management Complex (RWMC) buried wastes. The cyclone furnace, molten salt processor, microwave melter, ausmelt (fuel fired lance) furnace, and molten metal processor technologies are evaluated. A system description and brief development history are provided. The state of development of each technology is assessed, relative to treatment of RWMC buried waste

  17. Plasma drifts associated with a system of sun-aligned arcs in the polar cap

    International Nuclear Information System (INIS)

    Mende, S.B.; Doolittle, J.H.; Robinson, R.M.; Vondrak, R.R.; Rich, F.J.

    1988-01-01

    A series of four sun-aligned arcs passed over Sondre Stromfjord, Greenland, on the night of the 17th and 18th of February, 1985. Observations of these arcs were made using the Sondrestrom incoherent scatter radar and an intensified all-sky imaging TV system that was operated at the radar site. The first of the four arcs crossed the Sondre Stromfjord meridian just before local midnight moving westward, and the other three arcs followed at approximately half-hour intervals. When we account for the earth's rotation, the arc drift in an inertial frame was eastward, or dusk to dawn. The half-hour interval between meridian crossings of the arcs implies that the mean spacing between the arcs was 180 km. A Defense Meteorological Satellite Program (DMSP) F6 satellite pass at 0110 UT revealed the presence of highly structured electron and ion precipitation throughout the polar cap. The DMSP visible imager detected a single, sun-aligned arc associated with the largest peak in precipitating electron flux. This arc was also observed at Thule, Greenland, with an intensified film camera. These observations suggest that at least one of the arcs that were observed at Sondre Stromfjord extended across a large part of the polar cap. The radar at Sondre Stromfjord measured electron density and ion drift velocities associated with the four arcs. The radar drift measurements were superimposed on the all-sky video images to determine the location of the measurements relative to the arcs. Plasma drifts outside the arcs were found to be both sunward and antisunward, while within the arcs the drifts were predominantly antisunward. The variability of the drifts in the direction parallel to the arcs indicates that the electric fields were highly structured even though the configuration and motion of the arcs were well behaved

  18. Calculation of the Arc Velocity Along the Polluted Surface of Short Glass Plates Considering the Air Effect

    Directory of Open Access Journals (Sweden)

    Tao Yuan

    2012-03-01

    Full Text Available To investigate the microphysics mechanism and the factors that influence arc development along a polluted surface, the arc was considered as a plasma fluid. Based on the image method and the collision ionization theory, the electric field of the arc needed to maintain movement with different degrees of pollution was calculated. According to the force of the charged particle in an arc plasma stressed under an electric field, a calculation model of arc velocity, which is dependent on the electric field of the arc head that incorporated the effects of airflow around the electrode and air resistance is presented. An experiment was carried out to measure the arc velocity, which was then compared with the calculated value. The results of the experiment indicated that the lighter the pollution is, the larger the electric field of the arc head and arc velocity is; when the pollution is heavy, the effect of thermal buoyancy that hinders arc movement increases, which greatly reduces the arc velocity.

  19. Predictive control of thermal state of blast furnace

    Science.gov (United States)

    Barbasova, T. A.; Filimonova, A. A.

    2018-05-01

    The work describes the structure of the model for predictive control of the thermal state of a blast furnace. The proposed model contains the following input parameters: coke rate; theoretical combustion temperature, comprising: natural gas consumption, blasting temperature, humidity, oxygen, blast furnace cooling water; blast furnace gas utilization rate. The output parameter is the cast iron temperature. The results for determining the cast iron temperature were obtained following the identification using the Hammerstein-Wiener model. The result of solving the cast iron temperature stabilization problem was provided for the calculated values of process parameters of the target area of the respective blast furnace operation mode.

  20. Comprehensive Numerical Modeling of the Blast Furnace Ironmaking Process

    Science.gov (United States)

    Zhou, Chenn; Tang, Guangwu; Wang, Jichao; Fu, Dong; Okosun, Tyamo; Silaen, Armin; Wu, Bin

    2016-05-01

    Blast furnaces are counter-current chemical reactors, widely utilized in the ironmaking industry. Hot reduction gases injected from lower regions of the furnace ascend, reacting with the descending burden. Through this reaction process, iron ore is reduced into liquid iron that is tapped from the furnace hearth. Due to the extremely harsh environment inside the blast furnace, it is difficult to measure or observe internal phenomena during operation. Through the collaboration between steel companies and the Center for Innovation through Visualization and Simulation, multiple computational fluid dynamics (CFD) models have been developed to simulate the complex multiphase reacting flow in the three regions of the furnace, the shaft, the raceway, and the hearth. The models have been used effectively to troubleshoot and optimize blast furnace operations. In addition, the CFD models have been integrated with virtual reality. An interactive virtual blast furnace has been developed for training purpose. This paper summarizes the developments and applications of blast furnace CFD models and the virtual blast furnace.