  1. Pitting corrosion resistant austenite stainless steel

    Science.gov (United States)

    van Rooyen, D.; Bandy, R.

    A pitting corrosion resistant austenite stainless steel comprises 17 to 28 wt. % chromium, 15 to 26 wt. % nickel, 5 to 8 wt. % molybdenum, and 0.3 to 0.5 wt. % nitrogen, the balance being iron, unavoidable impurities, minor additions made in the normal course of melting and casting alloys of this type, and may optionally include up to 10 wt. % of manganese, up to 5 wt. % of silicon, and up to 0.08 wt. % of carbon.

  2. Resistance of Some Steels to Stress Corrosion Cracking

    Science.gov (United States)

    Humphries, T. S.; Nelson, E. E.

    1982-01-01

    Evaluations of stress-corrosion cracking resistance of five high-strength low-alloy steels described in report now available. Steels were heat-treated to various tensile strengths and found to be highly resistant to stress-corrosion cracking.

  3. A technique for predicting steel corrosion resistance

    Science.gov (United States)

    Novikov, V. F.; Sokolov, R. A.; Neradovskiy, D. F.; Muratov, K. R.

    2018-01-01

    Research works were carried out to develop a technique with the aim to increase the lifetime of steel items used in corrosive media. The possibility to monitor corrosion parameters of steel samples is analyzed on the basis of magnetic properties obtained by means of a magnetic structuroscope DIUS-1.15M designed by the Institute of Metal Physics of the Ural Branch of the Russian Academy of Sciences (IMP UB RAS).

  4. Formation of Surface Corrosion-Resistant Nanocrystalline Structures on Steel

    Science.gov (United States)

    Nykyforchyn, Hryhoriy; Kyryliv, Volodymyr; Maksymiv, Olha; Slobodyan, Zvenomyra; Tsyrulnyk, Oleksandr

    2016-02-01

    Engineering materials with nanocrystalline structure could be exploited under simultaneous action of mechanical loading and corrosion environments; therefore, their corrosion resistance is important. Surface nanocrystalline structure was generated on middle carbon steels by severe plastic deformation using the method of mechanical pulse friction treatment. This treatment additionally includes high temperature phase transformation and alloying. Using a complex of the corrosive, electrochemical and physical investigations, it was established that nanocrystalline structures can be characterized by lower or increased corrosion resistance in comparison with the reference material. It is caused by the action of two confronting factors: arising energy level and anticorrosive alloying of the surface layer.

  5. Corrosion Resistance of Some Stainless Steels in Chloride Solutions

    Directory of Open Access Journals (Sweden)

    Kasprzyk D.

    2017-06-01

    Full Text Available The present work compares corrosion behaviour of four types of S30403, S31603, S32615 austenitic and S32404 austenitic-ferritic stainless steels in chloride solutions (1%, 3% NaCl and in Ringer solution, at 37°C temperature. Corrosion resistance was determined by potentiodynamic polarization measurements and a thirty day immersion test conducted in Ringer solution. The immersion test was performed in term of biomedical application. These alloy were spontaneously passivated in all electrolytes, wherein S30403, S31603 and S32404 undergo pitting corrosion. Only S32615 containing 5.5% Si shows resistance to pitting corrosion.

  6. Coated steel rebar for enhanced concrete-steel bond strength and corrosion resistance.

    Science.gov (United States)

    2010-10-01

    This report summarizes the findings and recommendations on the use of enamel coating in reinforced concrete structures both for bond strength and : corrosion resistance of steel rebar. Extensive laboratory tests were conducted to characterize the pro...

  7. Corrosion resistance of kolsterised austenitic 304 stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Abudaia, F. B., E-mail: fabudaia@yahoo.com; Khalil, E. O., E-mail: ekhalil9@yahoo.com; Esehiri, A. F., E-mail: Hope-eseheri@hotmail.co.uk; Daw, K. E., E-mail: Khawladaw@yahoo.com [University of Tripoli Department of Materials and Metallurgical Eng, Tripoli-Libya P.O.Box13589 (Libya)

    2015-03-30

    Austenitic stainless suffers from low wear resistance in applications where rubbing against other surfaces is encountered. This drawback can be overcome by surface treatment such as coating by hard materials. Other treatments such as carburization at relatively low temperature become applicable recently to improve hardness and wear resistance. Carburization heat treatment would only be justified if the corrosion resistance is unaffected. In this work samples of 304 stainless steels treated by colossal supersaturation case carburizing (known as Kolsterising) carried out by Bodycote Company was examined for pitting corrosion resistance at room temperature and at 50 °C. Comparison with results obtained for untreated samples in similar testing conditions show that there is no deterioration in the pitting resistance due to the Kolsterising heat treatment. X ray diffraction patterns obtained for Kolsterising sample showed that peaks correspond to the austenite phase has shifted to lower 2θ values compared with those of the untreated sample. The shift is an indication for expansion of austenite unit cells caused by saturation with diffusing carbon atoms. The XRD of Kolsterising samples also revealed additional peaks appeared in the patterns due to formation of carbides in the kolsterised layer. Examination of these additional peaks showed that these peaks are attributed to a type of carbide known as Hagg carbide Fe{sub 2}C{sub 5}. The absence of carbides that contain chromium means that no Cr depletion occurred in the layer and the corrosion properties are maintained. Surface hardness measurements showed large increase after Kolsterising heat treatment.

  8. Surface modification to improve fireside corrosion resistance of Fe-Cr ferritic steels

    Energy Technology Data Exchange (ETDEWEB)

    Park, Jong-Hee (Clarendon Hills, IL); Natesan, Krishnamurti (Naperville, IL); Rink, David L. (Mokena, IL)

    2010-03-16

    An article of manufacture and a method for providing an Fe--Cr ferritic steel article of manufacture having a surface layer modification for corrosion resistance. Fe--Cr ferritic steels can be modified to enhance their corrosion resistance to liquid coal ash and other chemical environments, which have chlorides or sulfates containing active species. The steel is modified to form an aluminide/silicide passivating layer to reduce such corrosion.

  9. Influence of Heat Treatments on the Corrosion Resistance of Medium -Carbon Steel using Sulfuric Spring Water

    Directory of Open Access Journals (Sweden)

    Ikhlas Basheer

    2015-02-01

    Full Text Available The corrosion is one of the important problems that may be occur to the parts of machinery and equipment after manufactured and when used as a result of exposure to corrosive media. Plain-carbon steel is considered as one of the most common minerals used in industrial applications. Some of heat treatments can have direct effect on the corrosion rate of steel by building up galvanic corrosion cells between its microscopic phases. Therefore, to adopt one of kinds of the plain-carbon steel and the most commonly used in industry to be study subject, that is medium carbon steel and took samples of this steel has been treated thermally in three methods which the normalising, annealing, and hardening .The corrosive media used in the research is Sulfuric Spring, it contains many chemical compounds to show its influence on the corrosion of steel. The weight loss method is used to determine corrosion rate and to compare between the results obtained, show that the greatest corrosion resistance of the annealed steel and the corrosion resistance of the hardened steel is the lowest while the corrosion  resistance of the normalised steel is in-between them.         Calcium carbonate was formed on the metal surface which acts as an isolating layer which decrease corrosion rate with time

  10. 76 FR 55004 - Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Preliminary...

    Science.gov (United States)

    2011-09-06

    ... International Trade Administration Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of... of the antidumping order on corrosion-resistant carbon steel flat products (CORE) from the Republic... Antidumping Duty Orders on Certain Cold-Rolled Carbon Steel Flat Products and Certain Corrosion-Resistant...

  11. 77 FR 31877 - Corrosion-Resistant Carbon Steel Flat Products From Germany and Korea; Scheduling of Full Five...

    Science.gov (United States)

    2012-05-30

    ... COMMISSION Corrosion-Resistant Carbon Steel Flat Products From Germany and Korea; Scheduling of Full Five... duty order on corrosion-resistant carbon steel flat products from Korea and the antidumping duty orders on corrosion- resistant carbon steel flat products from Germany and Korea would be likely to lead to...

  12. 77 FR 14501 - Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Notice of...

    Science.gov (United States)

    2012-03-12

    ... International Trade Administration Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of... antidumping duty administrative review for certain corrosion-resistant carbon steel flat products (CORE) from... (POR) is August 1, 2009, through, July 31, 2010. \\1\\ See Certain Corrosion-Resistant Carbon Steel Flat...

  13. 76 FR 15291 - Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Notice of...

    Science.gov (United States)

    2011-03-21

    ... International Trade Administration Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of... for certain corrosion-resistant carbon steel flat products (CORE) from the Republic of Korea (Korea). See Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Notice of...

  14. 77 FR 44213 - Corrosion-Resistant Carbon Steel Flat Products From Germany and the Republic of Korea...

    Science.gov (United States)

    2012-07-27

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From Germany and the Republic... certain corrosion-resistant carbon steel flat products (``CORE'') from Germany and the Republic of Korea..., Director, Office 3, on ``Sunset Reviews of the Antidumping Duty Orders on Corrosion-Resistant Carbon Steel...

  15. 75 FR 55769 - Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Notice of...

    Science.gov (United States)

    2010-09-14

    ... International Trade Administration Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of... administrative review of the antidumping order on corrosion-resistant carbon steel flat products (CORE) from the... Antidumping Duty Orders on Certain Cold-Rolled Carbon Steel Flat Products and Certain Corrosion-Resistant...

  16. 77 FR 72827 - Corrosion-Resistant Carbon Steel Flat Products From Germany and the Republic of Korea: Final...

    Science.gov (United States)

    2012-12-06

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From Germany and the Republic... on certain corrosion- resistant carbon steel flat products (``CORE'') from Germany and the Republic... Reviews'' section of this notice. \\1\\ Corrosion-Resistant Carbon Steel Flat Products From Germany and the...

  17. 78 FR 59651 - Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Notice of...

    Science.gov (United States)

    2013-09-27

    ... International Trade Administration Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of... fourteenth administrative review of the antidumping duty order on certain corrosion-resistant carbon steel... aspects of the Final Results. \\2\\ See Certain Corrosion-Resistant Carbon Steel Flat Products from the...

  18. 78 FR 16247 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea; Final Results of...

    Science.gov (United States)

    2013-03-14

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea... antidumping duty order on corrosion-resistant carbon steel flat products (CORE) from the Republic of Korea... section entitled ``Final Results of Review.'' \\1\\ See Certain Corrosion-Resistant Carbon Steel Flat...

  19. 77 FR 301 - Corrosion-Resistant Carbon Steel Flat Products From Germany and Korea: Institution of Five-Year...

    Science.gov (United States)

    2012-01-04

    ... COMMISSION Corrosion-Resistant Carbon Steel Flat Products From Germany and Korea: Institution of Five-Year Reviews Concerning the Countervailing Duty Order on Corrosion-Resistant Carbon Steel Flat Products From Korea and the Antidumping Duty Orders on Corrosion-Resistant Carbon Steel Flat Products From Germany and...

  20. 75 FR 55745 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Preliminary Results...

    Science.gov (United States)

    2010-09-14

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea... corrosion-resistant carbon steel flat products (CORE) from the Republic of Korea (Korea) for the period of... preliminary results of the instant administrative review. See Corrosion-Resistant Carbon Steel Flat Products...

  1. 77 FR 24221 - Corrosion-Resistant Carbon Steel Flat Products From Germany and Korea; Notice of Commission...

    Science.gov (United States)

    2012-04-23

    ... COMMISSION Corrosion-Resistant Carbon Steel Flat Products From Germany and Korea; Notice of Commission... countervailing duty order on corrosion-resistant carbon steel flat products from Korea and the antidumping duty orders on corrosion- resistant carbon steel flat products from Germany and Korea would be likely to lead...

  2. 78 FR 16832 - Corrosion-Resistant Carbon Steel Flat Products From Germany and the Republic of Korea: Revocation...

    Science.gov (United States)

    2013-03-19

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From Germany and the Republic... corrosion-resistant carbon steel flat products (``CORE'') from Germany and the Republic of Korea (``Korea...-Year (``Sunset'') Review, 77 FR 85 (January 3, 2012). \\2\\ See Corrosion-Resistant Carbon Steel Flat...

  3. 77 FR 54891 - Certain Corrosion-Resistant Carbon Steel Flat Products from the Republic of Korea: Preliminary...

    Science.gov (United States)

    2012-09-06

    ... International Trade Administration Certain Corrosion-Resistant Carbon Steel Flat Products from the Republic of... administrative review of the antidumping order on corrosion-resistant carbon steel flat products (CORE) from the... the order on March 12, 2012. See Certain Corrosion- Resistant Carbon Steel Flat Products From the...

  4. 78 FR 55057 - Corrosion-Resistant Carbon Steel Flat Products from the Republic of Korea: Preliminary Results of...

    Science.gov (United States)

    2013-09-09

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products from the Republic of Korea... antidumping duty order on corrosion-resistant carbon steel flat products (CORE) from the Republic of Korea.... See Corrosion-Resistant Carbon Steel Flat Products from Germany and the Republic of Korea: Revocation...

  5. 77 FR 13093 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Final Results of...

    Science.gov (United States)

    2012-03-05

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea... administrative review of the countervailing duty (``CVD'') order on corrosion-resistant carbon steel flat... Review'' below. \\1\\ See Corrosion-Resistant Carbon Steel Flat Products from the Republic of Korea...

  6. 76 FR 77775 - Corrosion-Resistant Carbon Steel Flat Products from the Republic of Korea: Extension of Time...

    Science.gov (United States)

    2011-12-14

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products from the Republic of Korea... countervailing duty order on corrosion-resistant carbon steel flat products from the Republic of Korea covering the period January 1, 2009, through December 31, 2009. See Corrosion-Resistant Carbon Steel Flat...

  7. 78 FR 59652 - Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Notice of...

    Science.gov (United States)

    2013-09-27

    ... International Trade Administration Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of... administrative review of the antidumping duty order on certain corrosion-resistant carbon steel flat products... Results. \\2\\ See Certain Corrosion-Resistant Carbon Steel Flat Products from the Republic of Korea: Notice...

  8. 75 FR 13490 - Certain Corrosion-Resistant Carbon Steel Flat Products from the Republic of Korea: Notice of...

    Science.gov (United States)

    2010-03-22

    ... International Trade Administration (A-580-816) Certain Corrosion-Resistant Carbon Steel Flat Products from the... administrative review for certain corrosion-resistant carbon steel flat products (CORE) from the Republic of Korea (Korea). See Certain Corrosion-Resistant Carbon Steel Flat Products from the Republic of Korea...

  9. 76 FR 3613 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Final Results of...

    Science.gov (United States)

    2011-01-20

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea... review of the countervailing duty (CVD) order on corrosion-resistant carbon steel flat products (CORE..., 2008. See Corrosion-Resistant Carbon Steel Flat Products from the Republic of Korea: Preliminary...

  10. Corrosion-resistant Foamed Cements for Carbon Steels

    Energy Technology Data Exchange (ETDEWEB)

    Sugama T.; Gill, S.; Pyatina, T., Muraca, A.; Keese, R.; Khan, A.; Bour, D.

    2012-12-01

    The cementitious material consisting of Secar #80, Class F fly ash, and sodium silicate designed as an alternative thermal-shock resistant cement for the Enhanced Geothermal System (EGS) wells was treated with cocamidopropyl dimethylamine oxide-based compound as foaming agent (FA) to prepare numerous air bubble-dispersed low density cement slurries of and #61603;1.3 g/cm3. Then, the foamed slurry was modified with acrylic emulsion (AE) as corrosion inhibitor. We detailed the positive effects of the acrylic polymer (AP) in this emulsion on the five different properties of the foamed cement: 1) The hydrothermal stability of the AP in 200 and #61616;C-autoclaved cements; 2) the hydrolysis-hydration reactions of the slurry at 85 and #61616;C; 3) the composition of crystalline phases assembled and the microstructure developed in autoclaved cements; 4) the mechanical behaviors of the autoclaved cements; and, 5) the corrosion mitigation of carbon steel (CS) by the polymer. For the first property, the hydrothermal-catalyzed acid-base interactions between the AP and cement resulted in Ca-or Na-complexed carboxylate derivatives, which led to the improvement of thermal stability of the AP. This interaction also stimulated the cement hydration reactions, enhancing the total heat evolved during cement’s curing. Addition of AP did not alter any of the crystalline phase compositions responsible for the strength of the cement. Furthermore, the AP-modified cement developed the porous microstructure with numerous defect-free cavities of disconnected voids. These effects together contributed to the improvement of compressive-strength and –toughness of the cured cement. AP modification of the cement also offered an improved protection of CS against brine-caused corrosion. There were three major factors governing the corrosion protection: 1) Reducing the extents of infiltration and transportation of corrosive electrolytes through the cement layer deposited on the underlying CS

  11. Corrosion resistance of different metallic coatings on press-hardened steels for automotive

    Energy Technology Data Exchange (ETDEWEB)

    Dosdat, L.; Petitjean, J.; Vietoris, T. (ArcelorMittal Maizieres Automotive Products Research Centre, F-57283 Maizieres-les-Metz); Clauzeau, O. [Bohr Technologies (France)

    2011-06-15

    The corrosion resistance of laboratory press-hardened components in aluminized, galvanized or galvannealed boron steels was evaluated through VDA 621-415 cyclic test for the automotive industry. 22MnB5 uncoated steel for hot stamping and standard galvanized steel for cold forming were also included as references. Corrosion resistance after painting (cosmetic corrosion) was quantified by measuring the delamination of electro-deposited paint from scribed panels. The rusting on their edges was used for determining the cut-edge corrosion resistance. The corrosion resistance on unpainted deformed panels (perforating corrosion) was quantified by mass losses and pit depth measurements. Zinc-coated boron steels were found to be more resistant to cosmetic corrosion than the other materials, and slightly more resistant to cut-edge corrosion than the aluminized one. Red rust apparition could not be avoided due to the high iron content in all these hot-stamped coatings. The three coated boron steels showed similar performances in terms of resistance to perforation. Aluminized boron steel presents the advantage of being less sensitive to hot-stamping process deviation. Its robustness has been proved for many years on cars. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  12. Influence of surface roughness of stainless steel on microbial adhesion and corrosion resistance

    DEFF Research Database (Denmark)

    Hilbert, Lisbeth Rischel; Bagge-Ravn, Dorthe; Kold, John

    2003-01-01

    was not affected by surface roughness (Ra) ranging from grit 4000 polished stainless steel (Ra resistance...... was evaluated in a commercial disinfectant and in 1 M NaCl. Electropolished and grit 4000 polished steel proved more corrosion resistant as opposed to grit 80 and 120 polished surfaces. In conclusion, the surface finish did not influence bacterial attachment, colonisation, or removal, but is an important...... parameter for the corrosion resistance of the surface....

  13. Corrosion-resistant coating for GTE compressor parts made of steels with low tempering temperatures

    Science.gov (United States)

    Muboyadzhyan, S. A.; Egorova, L. P.; Gorlov, D. S.; Bulavintseva, E. E.

    2017-01-01

    The corrosion resistance of an Ni-Co-Cr-Al-Si-Y + SPh (SPh is silicophosphate impregnation) alloy coating on 30Kh13, 38Kh2MYuA, VKS5, and VKS7 structural steels with low tempering temperatures has been studied. The steel-coating compositions have been tested to determine the accelerated cyclic corrosion resistance, the corrosion resistance under tropic climate chamber conditions and in salt fog, the stress corrosion resistance, and the corrosion resistance in an industrial atmosphere. The heat stability of coated samples is studied, metallographic studies of the samples before and after the tests are performed, and the influence of the coating on the strength characteristics of the structural steels is studied.

  14. 76 FR 54209 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Preliminary Results of...

    Science.gov (United States)

    2011-08-31

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea... conducting an administrative review of the countervailing duty (CVD) order on corrosion-resistant carbon... CORE from Korea with regard to Dongbu and POSCO. See Corrosion-Resistant Carbon Steel Flat Products...

  15. 77 FR 58512 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Preliminary Results of...

    Science.gov (United States)

    2012-09-21

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea... conducting an administrative review of the countervailing duty (CVD) order on corrosion-resistant carbon... Corrosion-Resistant Carbon Steel Flat Products from the Republic of Korea: Notice of Extension of...

  16. 78 FR 19210 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Final Results of...

    Science.gov (United States)

    2013-03-29

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea...) has completed its administrative review of the countervailing duty (CVD) order on corrosion-resistant...\\ See Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Preliminary Results of...

  17. Corrosion resistance enhancement of SAE 1020 steel after Chromium implantation by nitrogen ion recoil

    National Research Council Canada - National Science Library

    Geraldo Francisco Gomes; Mario Ueda; Antonio Fernando Beloto; Roberto Zenhei Nakazato; Helfried Reuther

    2005-01-01

    SAE 1020 construction steel is widely used as mortar reinforcement and small machine parts, but aside good surface properties as high ductility, hardness and wear resistance, its surface is prone to severe corrosion...

  18. Corrosion resistance of premodeled wires made of stainless steel used for heart electrotherapy leaders

    Science.gov (United States)

    Przondziono, J.; Walke, W.; Młynarski, R.; Szatka, W.

    2012-05-01

    The purpose of the study is to evaluate resistance to electrochemical corrosion of wire made of X10CrNi18-8 stainless steel designed for use in cardiology treatment. The influence of strain formed in the premodeling process and methods of wire surface preparation to corrosive resistance in artificial plasma solution were analysed. Wire corrosion tests were carried out in the solution of artificial plasma. Resistance to electrochemical corrosion was evaluated on the ground of recorded curves of anodic polarization by means of potentiodynamic method. Potentiodynamic tests carried out enabled to determine how the resistance to pitting corrosion of wire changes, depending on strain formed in the premodeling process as well as on the method of wire surface preparation. For evaluation of phenomena occurring on the surface of tested steel, electrochemical impedance spectroscopy (EIS) was applied. Deterioration of corrosive properties of wire along with the increase in the formed strain hardening was observed.

  19. TOPICAL REVIEW: Corrosion resistance of Si–Al-bearing ultrafine-grained weathering steel

    Directory of Open Access Journals (Sweden)

    Toshiyasu Nishimura

    2008-01-01

    Full Text Available In the Ultra-steel project at the National Institute for Materials Science (NIMS, which run from 1996 to 2005, high-Si–Al-content ultrafine-grained (UFG weathering steel was developed by grain refinement and weathering guidance. It was found that this steel has excellent strength, toughness and corrosion resistance. Samples were prepared by multi pass warm rolling at temperatures between 773 and 873 K. The grain size of steel rolled at 873 K was about 1 μ m, and the tensile strength (TS and elongation (EL had excellent values of 800 MPa and 20%, respectively. In general, steels with high Si and Al contents exhibit inferior toughness to carbon steel (SM; however, the toughness of the developed sample was markedly improved by grain refinement. Cyclic corrosion tests in the presence of chloride ions confirmed that the developed steel exhibited excellent corrosion resistance, superior to that of SM. Electron probe microanalysis (EPMA and transmission electron microscopy (TEM analyses showed that Si and Al mainly exist in the inner rust layer. Si and Al were identified as existing in the Si2 + and Al3 + states in the nanoscale complex oxides constituting the inner rust layer. Electrochemical impedance spectroscopy(EIS measurement showed that the corrosion reaction resistance (Rt of the developed steel was much greater than that of SM. In the developed steel, the nanoscale complex oxides were formed in the inner rust layer, which increased Rt, and resulted in the excellent corrosion resistance.

  20. Effect of quenching method on the wear and corrosion resistance of stainless steel AISI 420 (TYPE 30Kh13)

    Science.gov (United States)

    Sola, R.; Giovanardi, R.; Veronesi, P.; Poli, G.

    2013-03-01

    The effect of different kinds of quenching, i.e., laser, vacuum, and induction ones, on the mechanical properties and wear and corrosion resistances of stainless steel AISI 420 is studied. It is shown that all the three kinds of heat treatment raise considerably the wear resistance of the steel due to growth in the hardness. Laser and vacuum quenching also increases the corrosion resistance. After induction quenching the resistance to corrosion is lower than in untreated steel.

  1. 77 FR 25141 - Corrosion-Resistant Carbon Steel Flat Products From Germany and South Korea: Extension of Time...

    Science.gov (United States)

    2012-04-27

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From Germany and South Korea... of the antidumping duty (AD) orders on corrosion-resistant carbon steel flat products (CORE) from... Countervailing Duty Operations, Office 3, regarding ``Sunset Reviews of the Antidumping Duty Orders on Corrosion...

  2. 76 FR 69703 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Notice of Extension of...

    Science.gov (United States)

    2011-11-09

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea...) published a notice of initiation of the administrative review of the antidumping duty order on corrosion... results of this review. See Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of...

  3. 76 FR 4291 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Partial Rescission of...

    Science.gov (United States)

    2011-01-25

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea... administrative review of the countervailing duty order on corrosion- resistant carbon steel flat products from... ] requests for administrative review and partial revocation of the countervailing duty order on corrosion...

  4. 75 FR 77615 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Notice of Extension of...

    Science.gov (United States)

    2010-12-13

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea...) published a notice of initiation of the administrative review of the antidumping duty order on corrosion... results of this review. See Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of...

  5. Effect of Microstructure on Mechanical Properties and Corrosion Resistance of 2205 Duplex Stainless Steel

    Directory of Open Access Journals (Sweden)

    Łabanowski Jerzy

    2015-01-01

    Full Text Available This paper presents results of the research on impact of microstructure of austenitic-ferritic steel of duplex type on its mechanical properties and susceptibility to stress corrosion cracking. As showed, improper processing technologies more and more often used in shipbuilding industry for plates and other half-finished products made of duplex steel may cause significant lowering their properties, which frequently makes their replacing necessary. Results of the tests on stress corrosion under tension with low strain rate (SSRT conducted in an inert and corrosion (boiling magnesium chloride environment, are presented. It was proved that even minor structural transformations taking place in 500°C ageing temperature lower corrosion resistance of the steel. Structural transformations occurring in 700°C temperature to a smaller extent influence susceptibility to stress corrosion of the steel, however they cause drastic drop in its plasticity.

  6. Effect of Cu and Ni on Corrosion Resistance of Low Alloyed Steels for Cargo Oil Tank

    Science.gov (United States)

    Xiaobing, Luo; Feng, Chai; Hang, Su; Caifu, Yang; Hao, Li; Yaqing, Hou; Zhengyan, Zhang

    The corrosion behavior of four kinds of low alloyed steels in acid chloride solution (10%NaCl, pH=0.85) was studied on the basis of International Maritime Organization(IMO) standard. Results indicated that, with the increase of Cu and Ni content in steels, the corrosion rate exhibited a law of linear decline, polarization curve moved to positive direction, corrosion potential raised, current density significantly decreased and the interface electric resistance obviously increased. The mechanism of improvement the corrosion resistance of Cu bearing steel can be mainly attributed to the Cu enrichment on the surface of rust layer by means of re-deposition particles(100 500 nm) and keeping high stability. However, Ni was not found in the rust layer but improved the corrosion potential of matrix.

  7. Corrosion Resistance and Pitting Behaviour of Low-Carbon High-Mn Steels in Chloride Solution

    Directory of Open Access Journals (Sweden)

    Grajcar A.

    2016-06-01

    Full Text Available Corrosion resistance of the X4MnSiAlNbTi27-4-2 and X6MnSiAlNbTi26-3-3 type austenitic steels, after hot deformation as well as after cold rolling, were evaluated in 3.5% NaCl solution using potentiodynamic polarization tests. A type of nonmetallic inclusions and their pitting corrosion behaviour were investigated. Additionally, the effect of cold deformation on the corrosion resistance of high-Mn steels was studied. The SEM micrographs revealed that corrosion damage formed in both investigated steels is characterized by various shapes and an irregular distribution at the metallic matrix, independently on the steel state (thermomechanically treated or cold worked. Corrosion pits are generated both in grain interiors, grain boundaries and along the deformation bands. Moreover, corrosion damage is stronger in cold deformed steels in comparison to the thermomechanically treated specimens. EDS analysis revealed that corrosion pits preferentially nucleated on MnS and AlN inclusions or complex oxysulphides. The morphology of corrosion damage in 3.5% NaCl supports the data registered in potentiodynamic tests.

  8. Electrochemical testing of passivity state and corrosion resistance of supermartensitic stainless steels

    Directory of Open Access Journals (Sweden)

    S. Lasek

    2010-01-01

    Full Text Available On low interstitial - supermartensitic stainless steels (X1CrNiMo 12-5-1, X2CrNiMo 13-6-2, X1CrNiMo 12-6-2 the electrochemical potentiodynamic polarization tests were carried out and the passive state stability and localized corrosion resistance were compared and evaluated. The effect of quenching and tempering as well as the changes in microstructure on polarisation curves and corrosion properties at room temperature were established. Small differences in chemical composition of steels were also registered on their corrosion parameters changes and resistance.

  9. Electrochemical and pitting corrosion resistance of AISI 4145 steel subjected to massive laser shock peening treatment with different coverage layers

    Science.gov (United States)

    Lu, J. Z.; Han, B.; Cui, C. Y.; Li, C. J.; Luo, K. Y.

    2017-02-01

    The effects of massive laser shock peening (LSP) treatment with different coverage layers on residual stress, pitting morphologies in a standard corrosive solution and electrochemical corrosion resistance of AISI 4145 steel were investigated by pitting corrosion test, potentiodynamic polarisation test, and SEM observations. Results showed massive LSP treatment can effectively cause an obvious improvement of pitting corrosion resistance of AISI 4145 steel, and increased coverage layer can also gradually improve its corrosion resistance. Massive LSP treatment with multiple layers was shown to influence pitting corrosion behaviour in a standard corrosive solution.

  10. Is cell viability always directly related to corrosion resistance of stainless steels?

    Energy Technology Data Exchange (ETDEWEB)

    Salahinejad, E., E-mail: salahinejad@kntu.ac.ir [Faculty of Materials Science and Engineering, K.N. Toosi University of Technology, Tehran (Iran, Islamic Republic of); Ghaffari, M. [Bruker AXS Inc., 5465 East Cheryl Parkway, Madison, WI 53711 (United States); Vashaee, D. [Electrical and Computer Engineering Department, North Carolina State University, Raleigh, NC 27606 (United States); Tayebi, L. [Department of Developmental Sciences, Marquette University School of Dentistry, Milwaukee, WI 53201 (United States); Department of Engineering Science, University of Oxford, Oxford OX1 3PJ (United Kingdom)

    2016-05-01

    It has been frequently reported that cell viability on stainless steels is improved by increasing their corrosion resistance. The question that arises is whether human cell viability is always directly related to corrosion resistance in these biostable alloys. In this work, the microstructure and in vitro corrosion behavior of a new class of medical-grade stainless steels were correlated with adult human mesenchymal stem cell viability. The samples were produced by a powder metallurgy route, consisting of mechanical alloying and liquid-phase sintering with a sintering aid of a eutectic Mn–Si alloy at 1050 °C for 30 and 60 min, leading to nanostructures. In accordance with transmission electron microscopic studies, the additive particles for the sintering time of 30 min were not completely melted. Electrochemical impedance spectroscopic experiments suggested the higher corrosion resistance for the sample sintered for 60 min; however, a better cell viability on the surface of the less corrosion-resistant sample was unexpectedly found. This behavior is explained by considering the higher ion release rate of the Mn–Si additive material, as preferred sites to corrosion attack based on scanning electron microscopic observations, which is advantageous to the cells in vitro. In conclusion, cell viability is not always directly related to corrosion resistance in stainless steels. Typically, the introduction of biodegradable and biocompatible phases to biostable alloys, which are conventionally anticipated to be corrosion-resistant, can be advantageous to human cell responses similar to biodegradable metals. - Highlights: • Cell viability vs. corrosion resistance for medical-grade stainless steels • The stainless steel samples were prepared by powder metallurgy. • Unpenetrated additive played a critical role in the correlation.

  11. 77 FR 27438 - Certain Corrosion-Resistant Carbon Steel Flat Products From Korea: Final Results of Expedited...

    Science.gov (United States)

    2012-05-10

    ... International Trade Administration Certain Corrosion-Resistant Carbon Steel Flat Products From Korea: Final... third five-year sunset review of the countervailing duty order on certain corrosion-resistant carbon..., plated, or coated with corrosion-resistant metals such as zinc, aluminum, or zinc-, aluminum-, nickel- or...

  12. Nanostructure Formations and Improvement in Corrosion Resistance of Steels by Means of Pulsed Electron Beam Surface Treatment

    Directory of Open Access Journals (Sweden)

    K. M. Zhang

    2013-01-01

    Full Text Available The corrosion of steels has long been the topic for materials scientists. It is established that surface treatment is an efficient way to improve the corrosion resistance of steels without changing the bulk properties and with low costs. In the present paper, different kinds of surface treatment techniques for steels are briefly reviewed. In particular, the surface modification involving nanostructure formations of steels by using a low energy high pulsed electron beam (LEHCPEB treatment is lightened in the case of an AISI 316L stainless steel and D2 steel. The overall results demonstrate the high potential of the LEHCPEB technique for improving the corrosion performance of steels.

  13. Effect of Plasma Nitriding Process Conditions on Corrosion Resistance of 440B Martensitic Stainless Steel

    Directory of Open Access Journals (Sweden)

    Łępicka Magdalena

    2014-09-01

    Full Text Available Martensitic stainless steels are used in a large number of various industrial applications, e.g. molds for plastic injections and glass moldings, automotive components, cutting tools, surgical and dental instruments. The improvement of their tribological and corrosion properties is a problem of high interest especially in medical applications, where patient safety becomes a priority. The paper covers findings from plasma nitrided AISI 440B (PN-EN or DIN X90CrMoV18 stainless steel corrosion resistance studies. Conventionally heat treated and plasma nitrided in N2:H2 reaction gas mixture (50:50, 65:35 and 80:20, respectively in two different temperature ranges (380 or 450°C specimens groups were examined. Microscopic observations and electrochemical corrosion tests were performed using a variety of analytical techniques. As obtained findings show, plasma nitriding of AISI 440B stainless steel, regardless of the process temperature, results in reduction of corrosion current density. Nevertheless, applying thermo-chemical process which requires exceeding temperature of about 400°C is not recommended due to increased risk of steel sensitization to intergranular and stress corrosion. According to the results, material ion nitrided in 450°C underwent leaching corrosion processes, which led to significant disproportion in chemical composition of the corroded and corrosion-free areas. The authors suggest further research into corrosion process of plasma nitrided materials and its degradation products.

  14. 9% Cr steel high temperature oxidation. Solutions investigated for improving corrosion resistance of the steel

    Energy Technology Data Exchange (ETDEWEB)

    Evin, Harold Nicolas; Heintz, Olivier; Chevalier, Sebastien [UMR 5209 CNRS-Bourgogne Univ. (France). Lab. Interdisciplinaire Carnot de Bourgogne; Foejer, Cecilia; Jakani, Saad; Dhont, Annick; Claessens, Serge [OCAS N.V. ArcelorMittal Global R and D, Gent (Belgium)

    2010-07-01

    The improvement of high temperature oxidation resistance of low chromium content steels, such as T/P91, is of great interest in regards with their application in thermal power generating plants. Indeed, they possess good creep properties, but are facing their limits of use at temperature higher than 600 C, due to accelerated corrosion phenomena. Good knowledge of the mechanisms involved during their oxidation process is needed to prevent the degradation of the materials and to extend life time of the power plants components. Oxide layers thermally grown, on 9% Cr steels (provided by OCAS N.V), during isothermal tests between 600 C and 750 C in laboratory air under atmospheric pressure were investigated, by Scanning Electron Microscopy (SEM) and X-ray diffraction (XRD). The oxidation behaviour appeared very limited at 750 C, due to the presence of a breakaway, which can be linked to iron porous oxide grown over the surface of the samples. ''In situ'' X-ray Photoelectron spectroscopy (XPS) analyses were performed in air at 600 C after short exposures (between 5 min and 25 h). A complex mixture of iron oxide, Cr{sub 2}O{sub 3} and Cr (VI) species were characterized in the scales. The in-situ analyses were compared and related to XPS analyses performed on thick oxide scales formed on samples oxidized in air at 600 C for 100h. An oxidation mechanism is then proposed to understand the oxide scale growth in the temperature range 600 - 750 C. The second step of this study consists in improving the high temperature corrosion resistance of these steels without modifying their mechanical properties. Thus several solutions were investigated such as MOCVD coatings, pack cementation coatings, and tested in cycle conditions prior. (orig.)

  15. In vitro corrosion resistance of Lotus-type porous Ni-free stainless steels.

    Science.gov (United States)

    Alvarez, Kelly; Hyun, Soong-Keun; Fujimoto, Shinji; Nakajima, Hideo

    2008-11-01

    The corrosion behavior of three kinds of austenitic high nitrogen Lotus-type porous Ni-free stainless steels was examined in acellular simulated body fluid solutions and compared with type AISI 316L stainless steel. The corrosion resistance was evaluated by electrochemical techniques, the analysis of released metal ions was performed by inductively coupled plasma mass spectrometry (ICP-MS) and the cytotoxicity was investigated in a culture of murine osteoblasts cells. Total immunity to localized corrosion in simulated body fluid (SBF) solutions was exhibited by Lotus-type porous Ni-free stainless steels, while Lotus-type porous AISI 316L showed very low pitting corrosion resistance evidenced by pitting corrosion at a very low breakdown potential. Additionally, Lotus-type porous Ni-free stainless steels showed a quite low metal ion release in SBF solutions. Furthermore, cell culture studies showed that the fabricated materials were non-cytotoxic to mouse osteoblasts cell line. On the basis of these results, it can be concluded that the investigated alloys are biocompatible and corrosion resistant and a promising material for biomedical applications.

  16. 78 FR 55241 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Preliminary Results of...

    Science.gov (United States)

    2013-09-10

    ... International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea...) is conducting an administrative review of the countervailing duty (CVD) order on corrosion-resistant.... SUPPLEMENTARY INFORMATION: Scope of the Order The merchandise covered by this Order \\2\\ is certain corrosion...

  17. Is cell viability always directly related to corrosion resistance of stainless steels?

    Science.gov (United States)

    Salahinejad, E; Ghaffari, M; Vashaee, D; Tayebi, L

    2016-05-01

    It has been frequently reported that cell viability on stainless steels is improved by increasing their corrosion resistance. The question that arises is whether human cell viability is always directly related to corrosion resistance in these biostable alloys. In this work, the microstructure and in vitro corrosion behavior of a new class of medical-grade stainless steels were correlated with adult human mesenchymal stem cell viability. The samples were produced by a powder metallurgy route, consisting of mechanical alloying and liquid-phase sintering with a sintering aid of a eutectic Mn-Si alloy at 1050 °C for 30 and 60 min, leading to nanostructures. In accordance with transmission electron microscopic studies, the additive particles for the sintering time of 30 min were not completely melted. Electrochemical impedance spectroscopic experiments suggested the higher corrosion resistance for the sample sintered for 60 min; however, a better cell viability on the surface of the less corrosion-resistant sample was unexpectedly found. This behavior is explained by considering the higher ion release rate of the Mn-Si additive material, as preferred sites to corrosion attack based on scanning electron microscopic observations, which is advantageous to the cells in vitro. In conclusion, cell viability is not always directly related to corrosion resistance in stainless steels. Typically, the introduction of biodegradable and biocompatible phases to biostable alloys, which are conventionally anticipated to be corrosion-resistant, can be advantageous to human cell responses similar to biodegradable metals. Copyright © 2016 Elsevier B.V. All rights reserved.

  18. PRODUCTION OF POROUS POWDER MATERIALS OF SPHERICAL POWDERS OF CORROSION-RESISTANT STEEL

    Directory of Open Access Journals (Sweden)

    V. N. Kovalevskij

    2012-01-01

    Full Text Available Production of porous powder materials from spherical powders of corrosion-resistant steel 12Х18н10Т with formation at low pressures 120–140 mpa in the mold with the subsequent activated sintering became possible due to increase of duration of process of spattering and formation of condensate particles (Si–C or (Mo–Si on surface.

  19. Steel corrosion resistance in model solutions and reinforced mortar containing wastes

    NARCIS (Netherlands)

    Koleva, D.A.; Van Breugel, K.

    2012-01-01

    This work reports on the corrosion resistance of steel in alkaline model solutions and in cement-based materials (mortar). The model solutions and the mortar specimens were Ordinary Portland Cement (OPC) based. Further, hereby discussed is the implementation of an eco-friendly approach of waste

  20. Corrosion resistance of PANi-coated steel in simulated PEMFC anodic environment

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Naibao; Liang, Chenghao [Electromechanics and Materials Engineering College, Dalian Maritime University, Dalian 116026 (China); Yi, Baolian [Fuel Cell R and D Center, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023 (China)

    2008-01-15

    By using electrochemical techniques, the corrosion resistance of polyaniline (PANi)-coated 1Cr18Ni9Ti stainless steel was investigated in simulated proton exchange membrane fuel cell (PEMFC) anodic environment. The results indicated that the compact conductive PANi film could be obtained on 1Cr18Ni9Ti steel by pulse potentiostatic method (PPSM). When steel was coated with conductive PANi, its corrosion potential was improved from -350 to 250 mV in simulated corrosion solution. During the potentiostatic polarization in PEMFC's anodic operation environment, the film is stable and there is no degradation of the PANi film. The film has no effect on the performance of the fuel cell. Further effort to improve the performance of conductive polymer coatings and to estimate the long-term performance in actual PEMFC environment is desirable. (Abstract Copyright [2008], Wiley Periodicals, Inc.)

  1. Influence of Sulfur Content on the Corrosion Resistance of 17-4PH Stainless Steel

    Science.gov (United States)

    Tavares, S. S. M.; Pardal, J. M.; Martins, T. R. B.; da Silva, M. R.

    2017-04-01

    According to specification standards, the basic chemical composition of steel 17-4PH for special and critical applications is 15-17% Cr, 3.0-5.0% Ni, 3.0-5.0% Cu, 0.07% C (max) and 0.15-0.45% (Nb + Ta) (wt.%). The maximum sulfur content is 0.030%. However, as it will be shown in this work, this maximum limit for sulfur is too high for services where high corrosion resistance is necessary. Two samples of 17-4PH steel with similar base compositions, but quite different sulfur contents (0.027% and 0.001%S), were compared with respect to pitting corrosion and sensitization. Both materials were heat treated according to commercial treatments A, H900, H1100, H1150 and H1150D (ASTM A-1082). Two corrosion tests were applied to compare the steels. The first one was the double-loop electrochemical potentiodynamic reactivation (DL-EPR) test in 0.25 M H2SO4 + 0.01 KSCN solution, which is used to measure the degree of sensitization. The second test was the anodic polarization in 3.5%NaCl solution, commonly used to evaluate the pitting corrosion resistance. Detailed microstructural characterization by magnetic measurements, light optical and scanning electron microscopy was performed. As main conclusion, despite that both steels have chemical compositions in accordance with the standards, the steel with higher sulfur was much more susceptible to pitting and sensitization.

  2. Impact of the nanostructuration on the corrosion resistance and hardness of irradiated 316 austenitic stainless steels

    Energy Technology Data Exchange (ETDEWEB)

    Hug, E., E-mail: eric.hug@ensicaen.fr [Laboratoire de Cristallographie et Sciences des Matériaux, Normandie Université, CNRS UMR 6508, 6 Bd Maréchal Juin, 14050 Caen (France); Prasath Babu, R. [School of Materials, University of Manchester, M13 9PL (United Kingdom); Groupe de Physique des Matériaux, UMR CNRS 6634, Université et INSA de Rouen, Normandie Université, Saint-Etienne du Rouvray Cedex (France); Monnet, I. [Centre de recherches sur les Ions, les Matériaux et la Photonique CEA-CNRS, Normandie Université, 6 Bd Maréchal Juin, 14050 Caen (France); Etienne, A. [Groupe de Physique des Matériaux, UMR CNRS 6634, Université et INSA de Rouen, Normandie Université, Saint-Etienne du Rouvray Cedex (France); Moisy, F. [Centre de recherches sur les Ions, les Matériaux et la Photonique CEA-CNRS, Normandie Université, 6 Bd Maréchal Juin, 14050 Caen (France); Pralong, V. [Laboratoire de Cristallographie et Sciences des Matériaux, Normandie Université, CNRS UMR 6508, 6 Bd Maréchal Juin, 14050 Caen (France); Enikeev, N. [Institute of Physics of Advanced Materials, Ufa (Russian Federation); Saint Petersburg State University, Laboratory of the Mechanics of Bulk Nanostructured Materials, 198504 St. Petersburg (Russian Federation); Abramova, M. [Institute of Physics of Advanced Materials, Ufa (Russian Federation); and others

    2017-01-15

    Highlights: • Impacts of nanostructuration and irradiation on the properties of 316 stainless steels are reported. • Irradiation of nanostructured samples implies chromium depletion as than depicted in coarse grain specimens. • Hardness of nanocrystalline steels is only weakly affected by irradiation. • Corrosion resistance of the nanostructured and irradiated samples is less affected by the chromium depletion. - Abstract: The influence of grain size and irradiation defects on the mechanical behavior and the corrosion resistance of a 316 stainless steel have been investigated. Nanostructured samples were obtained by severe plastic deformation using high pressure torsion. Both coarse grain and nanostructured samples were irradiated with 10 MeV {sup 56}Fe{sup 5+} ions. Microstructures were characterized using transmission electron microscopy and atom probe tomography. Surface mechanical properties were evaluated thanks to hardness measurements and the corrosion resistance was studied in chloride environment. Nanostructuration by high pressure torsion followed by annealing leads to enrichment in chromium at grain boundaries. However, irradiation of nanostructured samples implies a chromium depletion of the same order than depicted in coarse grain specimens but without metallurgical damage like segregated dislocation loops or clusters. Potentiodynamic polarization tests highlight a definitive deterioration of the corrosion resistance of coarse grain steel with irradiation. Downsizing the grain to a few hundred of nanometers enhances the corrosion resistance of irradiated samples, despite the fact that the hardness of nanocrystalline austenitic steel is only weakly affected by irradiation. These new experimental results are discussed in the basis of couplings between mechanical and electrical properties of the passivated layer thanks to impedance spectroscopy measurements, hardness properties of the surfaces and local microstructure evolutions.

  3. CO{sub 2} corrosion resistance of carbon steel in relation with microstructure changes

    Energy Technology Data Exchange (ETDEWEB)

    Ochoa, Nathalie, E-mail: nochoa@usb.ve [Departamento de Ciencia de los Materiales, Universidad Simón Bolívar, Aptdo., 89000, Caracas (Venezuela, Bolivarian Republic of); Vega, Carlos [Departamento de Ciencia de los Materiales, Universidad Simón Bolívar, Aptdo., 89000, Caracas (Venezuela, Bolivarian Republic of); Pébère, Nadine; Lacaze, Jacques [Université de Toulouse, CIRIMAT, UPS/INPT/CNRS, ENSIACET, 4 Allée Emile Monso, CS 44362, 31030 Toulouse Cedex 4 (France); Brito, Joaquín L. [Laboratorio de Físico-química de Superficies, Centro de Química, Instituto Venezolano de Investigaciones Cientificas (IVIC), Carretera Panamericana, Km 11, Altos de Pipe, Estado Miranda (Venezuela, Bolivarian Republic of)

    2015-04-15

    The microstructural effects on the corrosion resistance of an API 5L X42 carbon steel in 0.5 M NaCl solution saturated with CO{sub 2} was investigated. Four microstructures were considered: banded (B), normalized (N), quenched and tempered (Q&T), and annealed (A). Electrochemical measurements (polarization curves and electrochemical impedance spectroscopy) were coupled with surface analyses (scanning electron microscope (SEM) and X-ray photoelectron spectroscopy (XPS)) to characterize the formation of the corrosion product layers. Electrochemical results revealed that corrosion resistance increased in the following order: B < N < Q&T < A. From the polarization curves it was shown that specifically, cathodic current densities were affected by microstructural changes. SEM images indicated that ferrite dissolved earlier than cementite and a thin layer of corrosion products was deposited on the steel surface. XPS analyses revealed that this layer was composed of a mixture of iron carbonate and non-dissolved cementite. It was also found that the quantity of FeCO{sub 3} content on the steel surface was greater for Q&T and A microstructures. These results, in agreement with the electrochemical data, indicate that the deposition mechanism of iron carbonate is closely related to the morphology of the non-dissolved cementite, determining the protective properties of the corrosion product layers. - Highlights: • The effect of change in microstructure on CO{sub 2} corrosion resistance was evaluated. • An API 5LX 42 carbon steel was immersed in a 0.5 M NaCl solution saturated with CO{sub 2}. • Banded, normalized, quenched-tempered and annealed microstructures were considered. • Electrochemical measurements were coupled with surface analysis. • Morphology and distribution of undissolved Fe{sub 3}C control corrosion kinetics.

  4. The effect of tempering temperature on pitting corrosion resistance of 420 stainless steels

    Energy Technology Data Exchange (ETDEWEB)

    Anwar, Moch Syaiful, E-mail: moch026@lipi.go.id; Prifiharni, Siska, E-mail: sisk002@lipi.go.id; Mabruri, Efendi, E-mail: effe004@lipi.go.id [Research Center for Metallurgy and Materials – Indonesian Institute of Sciences (LIPI) Kawasan PUSPIPTEK Building 470 – South of Tangerang – Banten – 15314 (Indonesia)

    2016-04-19

    The AISI Type 420 stainless steels are commonly used to steam generators, mixer blades, etc. These stainless steels are most prone to pitting in dissolved Cl{sup −} containing environments. In this paper, the effect of tempering temperature on pitting corrosion resistance of AISI Type 420 stainless steels was studied. The AISI Type 420 stainless steels specimens were heat treated at the temperature of 1050°C for 1 hour to reach austenite stabilization and then quench in the oil. After that, the specimens were tempered at the temperature of 150, 250, 350 and 450°C for 30 minutes and then air cooled to the room temperature. The electrochemical potentiodynamic polarization test was conducted at 3.5% sodium chloride solution to evaluate corrosion rate and pitting corrosion behaviour. The Scanning Electron Microscope (SEM), Energy Dispersive X-Ray Spectroscopy (EDS) were used to evaluate the pitting corrosion product. The result have shown that highest pitting potential was found in the sample tempered at 250°C and corrosion pits were found to initiate preferentially around chromium carbides.

  5. The effect of tempering temperature on pitting corrosion resistance of 420 stainless steels

    Science.gov (United States)

    Anwar, Moch. Syaiful; Prifiharni, Siska; Mabruri, Efendi

    2016-04-01

    The AISI Type 420 stainless steels are commonly used to steam generators, mixer blades, etc. These stainless steels are most prone to pitting in dissolved Cl- containing environments. In this paper, the effect of tempering temperature on pitting corrosion resistance of AISI Type 420 stainless steels was studied. The AISI Type 420 stainless steels specimens were heat treated at the temperature of 1050°C for 1 hour to reach austenite stabilization and then quench in the oil. After that, the specimens were tempered at the temperature of 150, 250, 350 and 450°C for 30 minutes and then air cooled to the room temperature. The electrochemical potentiodynamic polarization test was conducted at 3.5% sodium chloride solution to evaluate corrosion rate and pitting corrosion behaviour. The Scanning Electron Microscope (SEM), Energy Dispersive X-Ray Spectroscopy (EDS) were used to evaluate the pitting corrosion product. The result have shown that highest pitting potential was found in the sample tempered at 250°C and corrosion pits were found to initiate preferentially around chromium carbides.

  6. Impact of the nanostructuration on the corrosion resistance and hardness of irradiated 316 austenitic stainless steels

    Science.gov (United States)

    Hug, E.; Prasath Babu, R.; Monnet, I.; Etienne, A.; Moisy, F.; Pralong, V.; Enikeev, N.; Abramova, M.; Sauvage, X.; Radiguet, B.

    2017-01-01

    The influence of grain size and irradiation defects on the mechanical behavior and the corrosion resistance of a 316 stainless steel have been investigated. Nanostructured samples were obtained by severe plastic deformation using high pressure torsion. Both coarse grain and nanostructured samples were irradiated with 10 MeV 56Fe5+ ions. Microstructures were characterized using transmission electron microscopy and atom probe tomography. Surface mechanical properties were evaluated thanks to hardness measurements and the corrosion resistance was studied in chloride environment. Nanostructuration by high pressure torsion followed by annealing leads to enrichment in chromium at grain boundaries. However, irradiation of nanostructured samples implies a chromium depletion of the same order than depicted in coarse grain specimens but without metallurgical damage like segregated dislocation loops or clusters. Potentiodynamic polarization tests highlight a definitive deterioration of the corrosion resistance of coarse grain steel with irradiation. Downsizing the grain to a few hundred of nanometers enhances the corrosion resistance of irradiated samples, despite the fact that the hardness of nanocrystalline austenitic steel is only weakly affected by irradiation. These new experimental results are discussed in the basis of couplings between mechanical and electrical properties of the passivated layer thanks to impedance spectroscopy measurements, hardness properties of the surfaces and local microstructure evolutions.

  7. Effect of Low-Cycle Thermocycling Treatment on Corrosion and Mechanical Properties of Corrosion-Resistant Steel 12Kh18N10T Irradiated with Neutrons

    Science.gov (United States)

    Yarovchuk, A. V.; Maksimkin, O. P.; Tsay, K. V.

    2017-11-01

    The effect of thermocycling treatment on the susceptibility to local corrosion and mechanical characteristics of corrosion-resistant steel 12Kh18N10T in different states (after austenitizing, cold rolling, and neutron irradiation) is considered. The possibility of partial recovery of the corrosion and mechanical characteristics of irradiated reactor steel due to low-cycle thermocycling in a temperature range exceeding the irradiation temperature is demonstrated.

  8. Effect of Carbonitriding on Corrosion Resistance of Steel 30MnB5 in Two Acidic Environments

    Science.gov (United States)

    Yazici, Aysel; Sadrettin Zeybek, M.; Güler, Hüseyin; Koç, Muhterem; Göksel Pekýtkan, F.

    2017-07-01

    Corrosion resistance of steel 30MnB5 is studied after carbonitriding, after conventional quenching, and without treatment. Corrosion tests are performed for from 24 to 168 h in two acidic environments (in a hydrochloric acid solution with 10% mole fraction and in fertilizer-containing soil). It is shown that the rate of corrosion of the steel in both environments after carbonitriding is lower than after quenching).

  9. Biocompatibly Coated 304 Stainless Steel as Superior Corrosion-Resistant Implant Material to 316L Steel

    Science.gov (United States)

    Paul, Subir; Mandal, Chandranath

    2013-10-01

    Surface treatments of 304 stainless steel by electro-coating and passivating in few inorganic electrolytes were found to be very effective in drastically reducing the corrosion rate of the material in stimulated body fluid (SBF) by several orders in comparison to that of 316L steel, presently being used for orthopedic implants. Polarization studies of electrodeposited hydroxyl apatite coating on 304 steel showed remarkably improved corrosion current. Cyclic polarization of the material in SBF reflected the broadened passivity region, much lower passive current, and narrower hysteresis loops. Similar effects were also found through the formation of inorganic coatings by passivation in NaF, CaNO3, and calcium phosphate buffer solutions. Surface characterization by XRD showed the peaks of the respective coating crystals. The morphology of the coatings studied by SEM showed a flake-type structure for hydroxyapatite coating and fine spherical-subspherical particles for other coatings.

  10. Mechanical properties and oxidation and corrosion resistance of reduced-chromium 304 stainless steel alloys

    Science.gov (United States)

    Stephens, J. R.; Barrett, C. A.; Gyorgak, C. A.

    1979-01-01

    An experimental program was undertaken to identify effective substitutes for part of the Cr in 304 stainless steel as a method of conserving the strategic element Cr. Although special emphasis was placed on tensile properties, oxidation and corrosion resistance were also examined. Results indicate that over the temperature range of -196 C to 540 C the yield stress of experimental austenitic alloys with only 12 percent Cr compare favorably with the 18 percent Cr in 304 stainless steel. Oxidation resistance and in most cases corrosion resistance for the experimental alloys were comparable to the commercial alloy. Effective substitutes for Cr included Al, Mo, Si, Ti, and V, while Ni and Mn contents were increased to maintain an austenitic structure.

  11. 77 FR 16810 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Extension of Time...

    Science.gov (United States)

    2012-03-22

    ... From the Federal Register Online via the Government Publishing Office DEPARTMENT OF COMMERCE International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea..., the Department published in the Federal Register the countervailing duty order on corrosion-resistant...

  12. 76 FR 20954 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Extension of Time...

    Science.gov (United States)

    2011-04-14

    ... From the Federal Register Online via the Government Publishing Office DEPARTMENT OF COMMERCE International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea..., the Department published in the Federal Register the countervailing duty order on corrosion-resistant...

  13. 75 FR 18153 - Corrosion-Resistant Carbon Steel Flat Products from the Republic of Korea: Extension of Time...

    Science.gov (United States)

    2010-04-09

    ... From the Federal Register Online via the Government Publishing Office DEPARTMENT OF COMMERCE International Trade Administration Corrosion-Resistant Carbon Steel Flat Products from the Republic of Korea..., the Department published in the Federal Register the countervailing duty order on corrosion-resistant...

  14. 77 FR 67395 - Corrosion-Resistant Carbon Steel Flat Products From Germany and Korea; Revised Schedule for the...

    Science.gov (United States)

    2012-11-09

    ... From the Federal Register Online via the Government Publishing Office INTERNATIONAL TRADE COMMISSION Corrosion-Resistant Carbon Steel Flat Products From Germany and Korea; Revised Schedule for the Subject Reviews AGENCY: United States International Trade Commission. ACTION: Notice. DATES: Effective...

  15. Prediction of microsegregation and pitting corrosion resistance of austenitic stainless steel welds by modelling

    Energy Technology Data Exchange (ETDEWEB)

    Vilpas, M. [VTT Manufacturing Technology, Espoo (Finland). Materials and Structural Integrity

    1999-07-01

    The present study focuses on the ability of several computer models to accurately predict the solidification, microsegregation and pitting corrosion resistance of austenitic stainless steel weld metals. Emphasis was given to modelling the effect of welding speed on solute redistribution and ultimately to the prediction of weld pitting corrosion resistance. Calculations were experimentally verified by applying autogenous GTA- and laser processes over the welding speed range of 0.1 to 5 m/min for several austenitic stainless steel grades. Analytical and computer aided models were applied and linked together for modelling the solidification behaviour of welds. The combined use of macroscopic and microscopic modelling is a unique feature of this work. This procedure made it possible to demonstrate the effect of weld pool shape and the resulting solidification parameters on microsegregation and pitting corrosion resistance. Microscopic models were also used separately to study the role of welding speed and solidification mode in the development of microsegregation and pitting corrosion resistance. These investigations demonstrate that the macroscopic model can be implemented to predict solidification parameters that agree well with experimentally measured values. The linked macro-micro modelling was also able to accurately predict segregation profiles and CPT-temperatures obtained from experiments. The macro-micro simulations clearly showed the major roles of weld composition and welding speed in determining segregation and pitting corrosion resistance while the effect of weld shape variations remained negligible. The microscopic dendrite tip and interdendritic models were applied to welds with good agreement with measured segregation profiles. Simulations predicted that weld inhomogeneity can be substantially decreased with increasing welding speed resulting in a corresponding improvement in the weld pitting corrosion resistance. In the case of primary austenitic

  16. Effect of niobium on corrosion resistance to sulfuric acid of 430 ferritic stainless steel

    OpenAIRE

    Neusa Alonso-Falleiros; Stephan Wolynec

    1998-01-01

    The influence of niobium on corrosion resistance to 0.5M H2SO4 of 17% Cr ferritic stainless steels, to which it was added in amounts larger than that necessary to stabilize the interstitial elements, was investigated. Their performance was compared to that of other two Fe-17%Cr alloys, one without additions and another containing 0.93% molybdenum. Through weight and electrochemical measurements and through morphologic examination of corroded surface it was found that the corrosion of these al...

  17. Atomic-scale decoration for improving the pitting corrosion resistance of austenitic stainless steels

    Science.gov (United States)

    Zhou, Y. T.; Zhang, B.; Zheng, S. J.; Wang, J.; San, X. Y.; Ma, X. L.

    2014-01-01

    Stainless steels are susceptible to the localized pitting corrosion that leads to a huge loss to our society. Studies in the past decades confirmed that the pitting events generally originate from the local dissolution in MnS inclusions which are more or less ubiquitous in stainless steels. Although a recent study indicated that endogenous MnCr2O4 nano-octahedra within the MnS medium give rise to local nano-galvanic cells which are responsible for the preferential dissolution of MnS, effective solutions of restraining the cells from viewpoint of electrochemistry are being tantalizingly searched. Here we report such a galvanic corrosion can be greatly resisted via bathing the steels in Cu2+-containing solutions. This chemical bath generates Cu2−δS layers on the surfaces of MnS inclusions, invalidating the nano-galvanic cells. Our study provides a low-cost approach via an atomic scale decoration to improve the pitting corrosion resistance of stainless steels in a volume-treated manner. PMID:24398863

  18. Antibacterial properties and corrosion resistance of AISI 420 stainless steels implanted by silver and copper ions

    Science.gov (United States)

    Ni, Hong-wei; Zhang, Han-shuang; Chen, Rong-sheng; Zhan, Wei-ting; Huo, Kai-fu; Zuo, Zhen-yu

    2012-04-01

    Silver or copper ions are often chosen as antibacterial agents. But a few reports are concerned with these two antibacterial agents for preparation of antibacterial stainless steel (SS). The antibacterial properties and corrosion resistance of AISI 420 stainless steel implanted by silver and copper ions were investigated. Due to the cooperative antibacterial effect of silver and copper ions, the Ag/Cu implanted SS showed excellent antibacterial activities against both Gram-negative Escherichia coli ( E. coli) and Gram-positive Staphylococcus aureus ( S. aureus) at a total implantation dose of 2×1017 ions/cm2. Electrochemical polarization curves revealed that the corrosion resistance of Ag/Cu implanted SS was slightly enhanced as compared with that of un-implanted SS. The implanted layer was characterized by X-ray photoelectron spectroscopy (XPS). Core level XPS spectra indicate that the implanted silver and copper ions exist in metallic state in the implanted layer.

  19. Standard guide for estimating the atmospheric corrosion resistance of low-alloy steels

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2004-01-01

    1.1 This guide presents two methods for estimating the atmospheric corrosion resistance of low-alloy weathering steels, such as those described in Specifications A242/A242M, A588/A588M, A606 Type 4, A709/A709M grades 50W, HPS 70W, and 100W, A852/A852M, and A871/A871M. One method gives an estimate of the long-term thickness loss of a steel at a specific site based on results of short-term tests. The other gives an estimate of relative corrosion resistance based on chemical composition. 1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.

  20. Corrosion Resistance of Galvanized Steel in the Environment of a Bioreactor

    Directory of Open Access Journals (Sweden)

    Šustr Michal

    2016-06-01

    Full Text Available The article deals with monitoring the corrosion resistibility of welded materials in the anaerobic fermenter (bioreactor. The main goal of this research is to assess the change of hardness after degradation. The change of hardness occurs in the corrosion environment and it correlates with the corrosion resistibility of material. The purpose of this experiment is to recognize the possibilities of using the CMT welded materials in the defined environment. As an innovative technology the acoustic emission method is used for assessment of surface layer disruption during hardness testing. Aluminium alloy with galvanized steel (AluZinc was used as an experimental material. The basic materials were welded by the filler material AlSi3.

  1. Corrosion resistance of steel fibre reinforced concrete - A literature review

    DEFF Research Database (Denmark)

    Marcos Meson, Victor; Michel, Alexander; Solgaard, Anders

    2017-01-01

    Steel fibre reinforced concrete (SFRC) is increasingly being used in the construction of civil infrastructure. However, there are inconsistencies among international standards and guidelines regarding the consideration of carbon-steel fibres for the structural verification of SFRC exposed to corr...

  2. Evaluation of the electrical conductivity and corrosion resistance for layers deposited via sputtering on stainless steel

    Science.gov (United States)

    Blanco, J.; Salas, Y.; Jiménez, C.; Pineda, Y.; Bustamante, A.

    2017-12-01

    In some Engineering fields, we need that conductive materials have a mechanic performance and specific electrical for that they maintain conditions or corrosive attack if they are in the environment or if they are closed structure. The stainless steels have an inert film on their surface and it has the function to act in contrast to external agents who generates the corrosion, especially for stings, spoiling the film until to fail. We found a solution taking into account the electrical performance and the anticorrosive; into the process we put recovering of specific oxides on, stainless steel using the method of sputtering with Unbalanced Magnetron, (UBM) varying the oxygen in the reactive environment. The coating obtained had a thickness one micron approximately and we saw on serious structural uniformity [1]. The corrosion resistance was evaluated through the potentiodynamics polarization and electrochemical spectroscopy impedance in NACL according to the standard. The cathode protection is the most important method employed for the corrosion prevention of metallic structures in the soil or immersed on the water. The electrical resistivity was evaluated with the four points methods and it showed a behaviour of diode type in some substrates with a threshold potential in several volts. We noticed a simple resistance solution when it was analysed in the Nyquist graphics whit the Electrochemical Impedance Spectroscopy technique. With on equivalent circuit, for this reason we determinate a variation in the corrosion speed in almost two orders of magnitude when we analysed the potentiodynamics curve by Tafel approximation. The data obtained and analysed show that this type of surface modification maintains the conductivity condition at the interface, improving the resistance in relation whit the corrosion of these elements where the recovering allowed the ionic flow wished for overcoming threshold voltage, acting as an insulator in different cases.

  3. MECHANIZM OF ANODE DISSOLVING OF CORROSION-RESISTING AND STRUCTURAL CARBON STEELS UNDER ELECTROPULSE POLISHING

    Directory of Open Access Journals (Sweden)

    N. P. Ivanova

    2013-01-01

    Full Text Available In this article were suggested the schemes of anode processes, taking into account the nature of metals, anion structure, pH solution of electrolyte and anode potential by electropulse polishing of corrosion- resisting and structural carbon steels.It is shown and experimentally confirmed, that under conditions of electropulse polishing of anode dissolving of metals, which are contained into corrosion-resisting and structural carbon steels, carried out according to mechanism of complex formation through a set of series and series-parallel of intermediate stages. In the 1st stage on the surface of metals adsorption complexes with participation of chemisorption molecules of water are formed. In the next stages anions of electrolyte’s solution and molecules of water take part. In final stage of dissolving on the surface of anode soluble compounds are formed, which by transition into solution into simple ions are dissociated. It is determined that by electrical-impulse polishing in dissolving of components of corrosion-resisting carbon steels the important role play chemical processes, and anode dissolving of metals take place in the field of mixed electrochemical and diffusion kinetics . Diffusion limitations appear as a result of difficult ion mass transfer through surface salt, oxide and hydro-oxide and absorption-phase coatings.

  4. Corrosion resistance and development length of steel reinforcement with cementitious coatings

    Science.gov (United States)

    Pei, Xiaofei

    This research program focused on the corrosion resistance and development length of reinforcing steel coated with Cementitious Capillary Crystalline Waterproofing (CCCW) materials. The first part of this research program involved using the half-cell potential method to evaluate the corrosion resistance of CCCW coating materials. One hundred and two steel bars were embedded in concrete cylinders and monitored. In total, 64 steel reinforcing bars were coated with CCCW prior to embedment, 16 mortar cylinders were externally coated with CCCW, and 22 control (uncoated) samples were tested. All the samples were immersed in a 3.5% concentration chloride solution for a period of one year. Three coating types were studied: CCCW-B, CCCW-B+ C and CCCW-C+D. The test results showed that the CCCW coating materials delayed the corrosion activity to varying degrees. In particular, CCCW-C+D applied on the reinforcing steel surface dramatically delayed the corrosion activity when compared to the control samples. After being exposed to the chloride solution for a period of one year, no sign of corrosion was observed for the cylinders where the concrete surface was coated. The second part of this research evaluated the bond strength and development length of reinforcing steel coated with two types of CCCW coating materials (CCCW-B+C and CCCW-C+D) using a modified pull-out test method. A self-reacting inverted T-shaped beam was designed to avoid compression in the concrete surrounding the reinforcing steel. Steel reinforcing bars were embedded along the web portion of the T-beam with various embedded lengths and were staggered side by side. In total, six T-beams were fabricated and each beam contained 8 samples. Both short-term (7 days) and long-term (3 months) effects of water curing were evaluated. The reinforcing steel bars coated with CCCW-B+C demonstrated a higher bond strength than did samples coated with CCCW-C+D. However, the bond strengths of samples with coating materials

  5. Erosion and corrosion resistance of laser cladded AISI 420 stainless steel reinforced with VC

    Science.gov (United States)

    Zhang, Zhe; Yu, Ting; Kovacevic, Radovan

    2017-07-01

    Metal Matrix Composites (MMC) fabricated by the laser cladding process have been widely applied as protective coatings in industries to improve the wear, erosion, and corrosion resistance of components and prolong their service life. In this study, the AISI 420/VC metal matrix composites with different weight percentage (0 wt.%-40 wt.%) of Vanadium Carbide (VC) were fabricated on a mild steel A36 by a high power direct diode laser. An induction heater was used to preheat the substrate in order to avoid cracks during the cladding process. The effect of carbide content on the microstructure, elements distribution, phases, and microhardness was investigated in detail. The erosion resistance of the coatings was tested by using the abrasive waterjet (AWJ) cutting machine. The corrosion resistance of the coatings was studied utilizing potentiodynamic polarization. The results showed that the surface roughness and crack susceptibility of the laser cladded layer were increased with the increase in VC fraction. The volume fraction of the precipitated carbides was increased with the increase in the VC content. The phases of the coating without VC consisted of martensite and austenite. New phases such as precipitated VC, V8C7, M7C3, and M23C6 were formed when the primary VC was added. The microhardness of the clads was increased with the increase in VC. The erosion resistance of the cladded layer was improved after the introduction of VC. The erosion resistance was increased with the increase in the VC content. No obvious improvement of erosion resistance was observed when the VC fraction was above 30 wt.%. The corrosion resistance of the clads was decreased with the increase in the VC content, demonstrating the negative effect of VC on the corrosion resistance of AISI 420 stainless steel

  6. Bacterial exopolysaccharides for corrosion resistance on low carbon steel

    Science.gov (United States)

    Corrosion is a global issue that affects safety and economics. There is an increasing demand for bio-based polymers for industrial applications and production of polymers by micro-organisms is especially attractive. This work reports on the electrochemical and physical properties of exopolysaccharid...

  7. Erosion and corrosion resistance of laser cladded AISI 420 stainless steel reinforced with VC

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Zhe [Center for Laser-aided Manufacturing, Lyle School of Engineering, Southern Methodist University, 3101 Dyer Street, Dallas, TX 75206 (United States); Yu, Ting [Center for Laser-aided Manufacturing, Lyle School of Engineering, Southern Methodist University, 3101 Dyer Street, Dallas, TX 75206 (United States); School of Mechanical and Electrical Engineering, Nanchang University, Nanchang, Jiangxi 330031 (China); Kovacevic, Radovan, E-mail: kovacevi@smu.edu [Center for Laser-aided Manufacturing, Lyle School of Engineering, Southern Methodist University, 3101 Dyer Street, Dallas, TX 75206 (United States)

    2017-07-15

    Highlights: • The coatings of 420 stainless steel reinforced with VC were fabricated by high power direct diode laser. • The erosion resistance of the cladded layer was increased with the increase in the VC fraction. • No obvious improvement of erosion resistance was observed when the VC fraction was above 30 wt.%. • The corrosion resistance of the cladded layer was decreased with the increase in the VC fraction. - Abstract: Metal Matrix Composites (MMC) fabricated by the laser cladding process have been widely applied as protective coatings in industries to improve the wear, erosion, and corrosion resistance of components and prolong their service life. In this study, the AISI 420/VC metal matrix composites with different weight percentage (0 wt.%–40 wt.%) of Vanadium Carbide (VC) were fabricated on a mild steel A36 by a high power direct diode laser. An induction heater was used to preheat the substrate in order to avoid cracks during the cladding process. The effect of carbide content on the microstructure, elements distribution, phases, and microhardness was investigated in detail. The erosion resistance of the coatings was tested by using the abrasive waterjet (AWJ) cutting machine. The corrosion resistance of the coatings was studied utilizing potentiodynamic polarization. The results showed that the surface roughness and crack susceptibility of the laser cladded layer were increased with the increase in VC fraction. The volume fraction of the precipitated carbides was increased with the increase in the VC content. The phases of the coating without VC consisted of martensite and austenite. New phases such as precipitated VC, V{sub 8}C{sub 7}, M{sub 7}C{sub 3}, and M{sub 23}C{sub 6} were formed when the primary VC was added. The microhardness of the clads was increased with the increase in VC. The erosion resistance of the cladded layer was improved after the introduction of VC. The erosion resistance was increased with the increase in the VC content

  8. Corrosion resistance improvement for 316L stainless steel coronary artery stents by trimethylsilane plasma nanocoatings.

    Science.gov (United States)

    Eric Jones, John; Chen, Meng; Yu, Qingsong

    2014-10-01

    To improve their corrosion resistance and thus long-term biocompatibility, 316L stainless steel coronary artery stents were coated with trimethylsilane (TMS) plasma coatings of 20-25 nm in thickness. Both direct current (DC) and radio-frequency (RF) glow discharges were utilized for TMS plasma coatings and additional NH₃/O₂ plasma treatment to tailor the surface properties. X-ray photoelectron spectroscopy (XPS) was used to characterize the coating surface chemistry. It was found that both DC and RF TMS plasma coatings had Si- and C-rich composition, and the O- and N-contents on the surfaces were substantially increased after NH₃/O₂ plasma treatment. Surface contact angle measurements showed that DC TMS plasma nanocoating with NH₃/O₂ plasma treatment generated very hydrophilic surface. The corrosion resistance of TMS plasma coated stents was evaluated through potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) techniques. The potentiodynamic polarization demonstrated that the TMS plasma coated stents imparted higher corrosion potential and pitting potential, as well as lower corrosion current densities as compared with uncoated controls. The surface morphology of stents before and after potentiodynamic polarization testing was analyzed with scanning electron microscopy, which indicated less corrosion on coated stents than uncoated controls. It was also noted that, from EIS data, the hydrophobic TMS plasma nanocoatings showed stable impedance modulus at 0.1 Hz after 21 day immersion in an electrolyte solution. These results suggest improved corrosion resistance of the 316L stainless steel stents by TMS plasma nanocoatings and great promise in reducing and blocking metallic ions releasing into the bloodstream. © 2014 Wiley Periodicals, Inc.

  9. Corrosion resistance improvement for 316L stainless steel coronary artery stents by trimethylsilane plasma nanocoatings

    Science.gov (United States)

    Jones, John Eric; Chen, Meng; Yu, Qingsong

    2015-01-01

    To improve their corrosion resistance and thus long-term biocompatibility, 316L stainless steel coronary artery stents were coated with trimethylsilane (TMS) plasma coatings of 20–25 nm in thickness. Both direct current (DC) and radio-frequency (RF) glow discharges were utilized for TMS plasma coatings and additional NH3/O2 plasma treatment to tailor the surface properties. X-ray photoelectron spectroscopy (XPS) was used to characterize the coating surface chemistry. It was found that both DC and RF TMS plasma coatings had Si- and C-rich composition, and the O-and N-contents on the surfaces were substantially increased after NH3/O2 plasma treatment. Surface contact angle measurements showed that DC TMS plasma nanocoating with NH3/O2 plasma treatment generated very hydrophilic surface. The corrosion resistance of TMS plasma coated stents was evaluated through potentiodynamic polarization and electro-chemical impedance spectroscopy (EIS) techniques. The potentiodynamic polarization demonstrated that the TMS plasma coated stents imparted higher corrosion potential and pitting potential, as well as lower corrosion current densities as compared with uncoated controls. The surface morphology of stents before and after potentiodynamic polarization testing was analyzed with scanning electron microscopy, which indicated less corrosion on coated stents than uncoated controls. It was also noted that, from EIS data, the hydrophobic TMS plasma nanocoatings showed stable impedance modulus at 0.1 Hz after 21 day immersion in an electrolyte solution. These results suggest improved corrosion resistance of the 316L stainless steel stents by TMS plasma nanocoatings and great promise in reducing and blocking metallic ions releasing into the bloodstream. PMID:24500866

  10. Comparative Stress Corrosion Cracking and General Corrosion Resistance of Annealed and Hardened 440 C Stainless Steel - New Techniques in Stress Corrosion Testing

    Science.gov (United States)

    Mendreck, M. J.; Hurless, B. E.; Torres, P. D.; Danford, M. D.

    1998-01-01

    The corrosion and stress corrosion cracking (SCC) characteristics of annealed and hardened 440C stainless steel were evaluated in high humidity and 3.5-percent NaCl solution. Corrosion testing consisted of an evaluation of flat plates, with and without grease, in high humidity, as well as electrochemical testing in 3.5-percent NaCl. Stress corrosion testing consisted of conventional, constant strain, smooth bar testing in high humidity in addition to two relatively new techniques under evaluation at MSFC. These techniques involve either incremental or constant rate increases in the load applied to a precracked SE(B) specimen, monitoring the crack-opening-displacement response for indications of crack growth. The electrochemical corrosion testing demonstrated an order of magnitude greater general corrosion rate in the annealed 440C. All techniques for stress corrosion testing showed substantially better SCC resistance in the annealed material. The efficacy of the new techniques for stress corrosion testing was demonstrated both by the savings in time and the ability to better quantify SCC data.

  11. Pitting and Intergranular Corrosion Resistance of AISI Type 301LN Stainless Steels

    Science.gov (United States)

    Ningshen, S.; Kamachi Mudali, U.

    2010-03-01

    The pitting and intergranular corrosion (IGC) resistance of AISI type 301LN stainless steels were evaluated using ASTM methods, anodic polarization, and electrochemical impedance techniques. The IGC results indicated that the microstructure of the samples after sensitization heat treatment at 675 °C for 1 h shows step or dual structure for both imported and indigenous materials indicating insignificant Cr23C6 precipitation. The results of immersion tests in boiling 6% copper sulfate + 16% sulfuric acid + copper solution for 24 h followed by the bend test (ASTM A262 Practice-E method) indicated no crack formation in any of the tested specimens. Pitting corrosion resistance carried out in 6% FeCl3 solution at different temperatures of 22 ± 2 and 50 ± 2 °C (ASTM G 48) up to the period of 72 h revealed pitting corrosion attack in all the investigated alloys. The potentiodynamic anodic polarization results in 0.5 M NaCl revealed variation in passive current density and pitting potential depending on the alloy chemistry and metallurgical condition. The passive film properties studied by electrochemical impedance spectroscopy (EIS) correlated well with the polarization results. The x-ray diffraction (XRD) results revealed the presence of austenite (γ) and martensite (α') phases depending on the material condition. The suitability of three indigenously developed AISI type 301LN stainless steels were compared with imported type 301LN stainless steel and the results are highlighted in this article.

  12. Evaluation of the stress corrosion cracking resistance of several high strength low alloy steels

    Science.gov (United States)

    Humphries, T. S.; Nelson, E. E.

    1980-01-01

    The stress corrosion cracking resistance was studied for high strength alloy steels 4130, 4340, for H-11 at selected strength levels, and for D6AC and HY140 at a single strength. Round tensile and C-ring type specimens were stressed up to 100 percent of their yield strengths and exposed to alternate immersion in salt water, salt spray, the atmosphere at Marshall Space Flight Center, and the seacoast at Kennedy Space Center. Under the test conditions, 4130 and 4340 steels heat treated to a tensile strength of 1240 MPa (180 ksi), H-11 and D6AC heat treated to a tensile strength of 1450 MPa (210 ksi), and HY140 (1020 MPa, 148 ksi) are resistant to stress corrosion cracking because failures were not encountered at stress levels up to 75 percent of their yield strengths. A maximum exposure period of one month for alternate immersion in salt water or salt spray and three months for seacoast is indicated for alloy steel to avoid false indications of stress corrosion cracking because of failure resulting from severe pitting.

  13. 76 FR 21332 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Extension of Time...

    Science.gov (United States)

    2011-04-15

    ... From the Federal Register Online via the Government Publishing Office DEPARTMENT OF COMMERCE International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea...'') published a notice of initiation of the administrative review of the antidumping duty order on corrosion...

  14. 75 FR 25841 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Extension of Time...

    Science.gov (United States)

    2010-05-10

    ... From the Federal Register Online via the Government Publishing Office DEPARTMENT OF COMMERCE International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea...'') published a notice of initiation of the administrative review of the antidumping duty order on corrosion...

  15. 77 FR 25405 - Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Extension of Time...

    Science.gov (United States)

    2012-04-30

    ... From the Federal Register Online via the Government Publishing Office DEPARTMENT OF COMMERCE International Trade Administration Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea...'') published a notice of initiation of the administrative review of the antidumping duty order on corrosion...

  16. Influence of microstructure and elemental partitioning on pitting corrosion resistance of duplex stainless steel welding joints

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Zhiqiang; Jing, Hongyang [School of Materials Science and Engineering, Tianjin University, Tianjin 300350 (China); Tianjin Key Laboratory of Advanced Joining Technology, Tianjin 300350 (China); Xu, Lianyong, E-mail: xulianyong@tju.edu.cn [School of Materials Science and Engineering, Tianjin University, Tianjin 300350 (China); Tianjin Key Laboratory of Advanced Joining Technology, Tianjin 300350 (China); Han, Yongdian; Zhao, Lei [School of Materials Science and Engineering, Tianjin University, Tianjin 300350 (China); Tianjin Key Laboratory of Advanced Joining Technology, Tianjin 300350 (China); Zhang, Jianli [Welding laboratory, Offshore Oil Engineering (Qing Dao) Company, Qing Dao 266520 (China)

    2017-02-01

    Highlights: • N{sub 2}-supplemented shielding gas promoted nitrogen solid-solution in the austenite. • Secondary austenite had higher Ni but lower Cr and Mo than primary austenite. • Pitting corrosion preferentially occurred at secondary austenite and Cr{sub 2}N. • Adding N{sub 2} in shielding gas improved pitting corrosion resistance of GTAW joint. • E2209T{sub 1} weld metal had very poor pitting corrosion resistance due to inclusions. - Abstract: The influences of microstructure and elemental partitioning on pitting corrosion resistance of duplex stainless steel joints welded by gas tungsten arc welding (GTAW) and flux-cored arc welding (FCAW) with different shielding gas compositions were studied by optical microscopy, electron backscatter diffraction, scanning electron microscopy, transmission electron microscopy, energy dispersive spectroscopy, electron probe microanalysis, and potentiostatic and potentiodynamic polarization methods The adding 2% N{sub 2} in shielding gas facilitated primary austenite formation in GTAW weld metal (WM) and suppressed Cr{sub 2}N precipitation in GTAW weld root. In the HAZ, the banded microstructure disappeared while the coarse ferrite grains maintained same orientation as the banded ferrite in the BM. In the WM, the ferrite had one single orientation throughout a grain, whereas several families of austenite appeared. The austenite both in BM and WM enriched in Ni and nitrogen, while Cr and Mo were concentrated in the ferrite and thus no element showed clear dendritic distribution in the WM (ER2209 and E2209T{sub 1}). In addition, the secondary austenite had higher Ni content but lower Cr and Mo content than the primary austenite. The N{sub 2}-supplemented shielding gas promoted nitrogen solid-solution in the primary and secondary austenite. Furthermore, the secondary austenite had relatively lower pitting resistance equivalent number (PREN) than the ferrite and primary austenite, thereby resulting in its preferential

  17. Influence of microstructure and elemental partitioning on pitting corrosion resistance of duplex stainless steel welding joints

    Science.gov (United States)

    Zhang, Zhiqiang; Jing, Hongyang; Xu, Lianyong; Han, Yongdian; Zhao, Lei; Zhang, Jianli

    2017-02-01

    The influences of microstructure and elemental partitioning on pitting corrosion resistance of duplex stainless steel joints welded by gas tungsten arc welding (GTAW) and flux-cored arc welding (FCAW) with different shielding gas compositions were studied by optical microscopy, electron backscatter diffraction, scanning electron microscopy, transmission electron microscopy, energy dispersive spectroscopy, electron probe microanalysis, and potentiostatic and potentiodynamic polarization methods The adding 2% N2 in shielding gas facilitated primary austenite formation in GTAW weld metal (WM) and suppressed Cr2N precipitation in GTAW weld root. In the HAZ, the banded microstructure disappeared while the coarse ferrite grains maintained same orientation as the banded ferrite in the BM. In the WM, the ferrite had one single orientation throughout a grain, whereas several families of austenite appeared. The austenite both in BM and WM enriched in Ni and nitro`gen, while Cr and Mo were concentrated in the ferrite and thus no element showed clear dendritic distribution in the WM (ER2209 and E2209T1). In addition, the secondary austenite had higher Ni content but lower Cr and Mo content than the primary austenite. The N2-supplemented shielding gas promoted nitrogen solid-solution in the primary and secondary austenite. Furthermore, the secondary austenite had relatively lower pitting resistance equivalent number (PREN) than the ferrite and primary austenite, thereby resulting in its preferential corrosion. The Cr2N precipitation led to relatively poor resistance to pitting corrosion in three HAZs and pure Ar shielding GTAW weld root. The N2-supplemented shielding gas improved pitting corrosion resistance of GTAW joint by increasing PREN of secondary austenite and suppressing Cr2N precipitation. In addition, the FCAW WM had much poorer resistance to pitting corrosion than the GTAW WM due to many O-Ti-Si-Mn inclusions. In the BM, since the austenite with lower PREN compared

  18. Significance of steel electrical resistance method in the evaluation of reinforcement corrosion in cementitious systems

    Directory of Open Access Journals (Sweden)

    Krajci, L.

    2004-06-01

    Full Text Available The suitable detection system of steel reinforcement corrosion in concrete structures contributes to the reduction of their maintenance costs. Method of steel electrical resistance represents non-destructive monitoring of steel in cementitious systems. Specially prepared and arranged test specimen of steel as a corrosion sensor is embedded in mortar specimen. Verification tests of this method based on chloride corrosion of steel in mortars as well as its visual inspection are introduced. Significance of steel electrical resistance method lies in the expression of steel corrosion by these quantitative parameters: reduction of cross-section of steel, thickness of corroded layer and loss of weight of steel material. This method is an integral method that allows the indirect determination of mentioned corrosion characteristics. The comparison of verified method with gravimetric evaluation of steel corrosion gives a good correspondence. Test results on mortars with calcium chloride dosages between 0.5% and 4.0% by weight of cement prove high sensitiveness and reliability of steel electrical resistance method.

    La utilización de un sistema de detección de la corrosión de las armaduras en estructuras de hormigón puede contribuir a la reducción de sus costes de mantenimiento. El método de la resistencia eléctrica del acero consiste en la monitorización no-destructiva realizada sobre el acero en sistemas cementantes. Dentro de la muestra de mortero se coloca el sistema de detección, especialmente preparado y fijado, actuando como un sensor de la corrosión. En este trabajo se presentan ensayos de verificación de este método, junto con inspecciones visuales, en morteros sometidos a corrosión de armaduras por efecto de los cloruros. La efectividad de este método de la resistencia eléctrica del acero se expresa, en la corrosión de armaduras, de acuerdo a los siguientes parámetros cuantitativos: reducción de la sección transversal del

  19. Influence of annealing heat treatment on pitting corrosion resistance of stainless steel type 316

    Directory of Open Access Journals (Sweden)

    Amirreza Bakhtiari

    2014-07-01

    Full Text Available The effect of annealing heat treatment on pitting resistance of stainless steel type 316L has been studied using Tafel polarization and ASTM G150 for estimating of the pitting potential and CPT, respectively. The materials were tested in 3.5% NaCl solution. The chemical composition of the material was analyzed via optical emission spectrometry. It was found that the sample treated at 940°C shows better pitting corrosion resistance than samples treated at 520°C and 820°C. The treatment at 940°C produced two types of morphologies, austenitic-ferritic matrix with δ-ferrite and only small amount of the σ phase. In the range up to 820°C the σ phase embedded in the γ phase matrix and at δ/γ interface was causing brittleness of the material and aggravated corrosion resistance. The treatment at 940°C produced the microstructure which prevented the corrosion attack to develop. It was revealed that the pitting size in samples treated at 520°C and 820°C is greater than that at 940°C. In addition, depth of pitting has been considered as a factor of pitting corrosion resistance. The depth of pitting in sample treated at 940°C is low since the pitting is almost superficial, while the pitting size in samples treated in 520°C and 820°C is higher and deeper.

  20. High corrosion resistance of austenitic stainless steel alloyed with nitrogen in an acid solution

    Energy Technology Data Exchange (ETDEWEB)

    Metikos-Hukovic, M., E-mail: mmetik@fkit.h [Department of Electrochemistry, Faculty of Chemical Engineering and Technology, University of Zagreb, Savska 16, P.O. Box 177, 100000 Zagreb (Croatia); Babic, R. [Department of Electrochemistry, Faculty of Chemical Engineering and Technology, University of Zagreb, Savska 16, P.O. Box 177, 100000 Zagreb (Croatia); Grubac, Z. [Department of General and Inorganic Chemistry, Faculty of Chemistry and Technology, University of Split, 21000 Split (Croatia); Petrovic, Z. [Department of Electrochemistry, Faculty of Chemical Engineering and Technology, University of Zagreb, Savska 16, P.O. Box 177, 100000 Zagreb (Croatia); Lajci, N. [Faculty of Mine and Metallurgy, University of Prishtina, 10000 Prishtina, Kosovo (Country Unknown)

    2011-06-15

    Highlights: {yields} ASS alloyed with nitrogen treated at 1150 {sup o}C exhibits microstructure homogeneity. {yields} Passivation peak of ASS corresponds to oxidation of metal and absorbed hydrogen. {yields} Transfer phenomena and conductivity depend on the film formation potential. {yields} Electronic structure of the passive film and its corrosion resistance correlate well. {yields} Passive film on ASS with nitrogen is low disordered and high corrosion resistant. - Abstract: Passivity of austenitic stainless steel containing nitrogen (ASS N25) was investigated in comparison with AISI 316L in deareated acid solution, pH 0.4. A peculiar nature of the passivation peak in a potentiodynamic curve and the kinetic parameters of formation and growth of the oxide film have been discussed. The electronic-semiconducting properties of the passive films have been correlated with their corrosion resistance. Alloying austenitic stainless steel with nitrogen increases its microstructure homogeneity and decreases the concentration of charge carriers, which beneficially affects the protecting and electronic properties of the passive oxide film.

  1. The Effect of Two Amine-Based Corrosion Inhibitors in Improving the Corrosion Resistance of Carbon Steel in Sea Water

    Science.gov (United States)

    Rihan, Rihan; Shawabkeh, Reyad; Al-Bakr, Nawaf

    2014-03-01

    This study investigates the effect of two amine-based corrosion inhibitors in reducing the corrosion rate (CR) of 1018 carbon steel in formulated sea water. For discussion purposes, the two inhibitors are named Inhibitor A (belongs to the alkyl pyridine benzyl chloride quaternary family of inhibitors) and Inhibitor B (belongs to the alkyl amines family of inhibitors). The two inhibitors are routinely considered for applications by Saudi Aramco, the world's largest oil producing and processing company, for reducing its corrosion problems in carbon steel pipelines carrying oil and gas. The experimental apparatus was a circulating flow loop system inside an autoclave. The experimental work was performed at pH 8.2, 55 °C, and 1000 rpm. The inhibitors were evaluated at three different concentrations of 5, 10, and 15 ppm. The CR was determined using the weight loss method and electrochemical methods such potentiodynamic sweep and linear polarization resistance. The experimental results indicate that Inhibitor B reduced the CR more than that of Inhibitor A.

  2. Alloy 31, a new 6 moly stainless steel with improved corrosion resistance in seawater

    Energy Technology Data Exchange (ETDEWEB)

    Jasner, M.; Heubner, U. [Krupp VDM GmbH, Werdohl (Germany)

    1995-10-01

    Alloy 31--UNS N08031--31Ni-27Cr-6.5Mo-1.2Cu-0.2N-balance iron--is an advanced 6 Mo stainless steel with increased chromium and nickel, contents for seawater service. In hot seawater the pitting potential of alloy 31 remains high up to 90 C (194 F). Investigations of resistance to crevice corrosion in real piping systems in natural seawater, both North Sea and Baltic Sea, show that the threshold conditions for alloy 31 in chlorinated seawater (North Sea) are at 40 C and 1 ppm chlorine well superior to the 6 Mo stainless grades being currently in use. In addition, alloy 31 shows an excellent resistance to corrosion versus both hot reducing media (e.g. H{sub 2}SO{sub 4}) and hot oxidizing media (e.g. HNO{sub 3}). The combination of high resistance to localized corrosion vs. hot chloride-bearing cooling waters including seawater and aggressive oxidizing and reducing hot corrosive media is a unique feature of alloy 31. Alloy 31 is recommended for the construction of heat exchangers, process coolers and piping systems. The material is supplied in a number of semifinished products such as seamless and welded pipes, fittings, flanges, forged bars, plate, sheet, strip, wire and prefabricated piping systems.

  3. Effect of Mn Content and Solution Annealing Temperature on the Corrosion Resistance of Stainless Steel Alloys

    Directory of Open Access Journals (Sweden)

    Ihsan-ul-Haq Toor

    2014-01-01

    Full Text Available The corrosion behavior of two specially designed austenitic stainless steels (SSs having different Nickel (Ni and Manganese (Mn contents was investigated. Prior to electrochemical tests, SS alloys were solution-annealed at two different temperatures, that is, at 1030°C for 2 h and 1050°C for 0.5 h. Potentiodynamic polarization (PD tests were carried out in chloride and acidic chloride, whereas linear polarization resistance (LPR and electrochemical impedance spectroscopy (EIS was performed in 0.5 M NaCl solution at room temperature. SEM/EDS investigations were carried out to study the microstructure and types of inclusions present in these alloys. Experimental results suggested that the alloy with highest Ni content and annealed at 1050°C/0.5 hr has the highest corrosion resistance.

  4. Enhanced corrosion resistance of strontium hydroxyapatite coating on electron beam treated surgical grade stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Gopi, D., E-mail: dhanaraj_gopi@yahoo.com [Department of Chemistry, Periyar University, Salem 636 011, Tamilnadu (India); Centre for Nanoscience and Nanotechnology, Periyar University, Salem 636 011, Tamilnadu (India); Rajeswari, D. [Department of Chemistry, Periyar University, Salem 636 011, Tamilnadu (India); Department of Physics, Periyar University, Salem 636 011, Tamilnadu (India); Ramya, S. [Department of Chemistry, Periyar University, Salem 636 011, Tamilnadu (India); Sekar, M. [Department of Chemistry, Periyar University, Salem 636 011, Tamilnadu (India); Department of Physics, Periyar University, Salem 636 011, Tamilnadu (India); R, Pramod; Dwivedi, Jishnu [Industrial and Medical Accelerator Section, Raja Ramanna Centre for Advanced Technology, Indore 452 013, Madhya Pradesh (India); Kavitha, L., E-mail: louiskavitha@yahoo.co.in [Centre for Nanoscience and Nanotechnology, Periyar University, Salem 636 011, Tamilnadu (India); Department of Physics, Periyar University, Salem 636 011, Tamilnadu (India); Ramaseshan, R. [Thin film and Coatings Section, Surface and Nanoscience Division, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102, Tamilnadu (India)

    2013-12-01

    The surface of 316L stainless steel (316L SS) is irradiated by high energy low current DC electron beam (HELCDEB) with energy of 500 keV and beam current of 1.5 mA followed by the electrodeposition of strontium hydroxyapatite (Sr-HAp) to enhance its corrosion resistance in physiological fluid. The coatings were characterised by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR) and High resolution scanning electron microscopy (HRSEM). The Sr-HAp coating on HELCDEB treated 316L SS exhibits micro-flower structure. Electrochemical results show that the Sr-HAp coating on HELCDEB treated 316L SS possesses maximum corrosion resistance in Ringer's solution.

  5. Enhanced corrosion resistance of strontium hydroxyapatite coating on electron beam treated surgical grade stainless steel

    Science.gov (United States)

    Gopi, D.; Rajeswari, D.; Ramya, S.; Sekar, M.; R, Pramod; Dwivedi, Jishnu; Kavitha, L.; Ramaseshan, R.

    2013-12-01

    The surface of 316L stainless steel (316L SS) is irradiated by high energy low current DC electron beam (HELCDEB) with energy of 500 keV and beam current of 1.5 mA followed by the electrodeposition of strontium hydroxyapatite (Sr-HAp) to enhance its corrosion resistance in physiological fluid. The coatings were characterised by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR) and High resolution scanning electron microscopy (HRSEM). The Sr-HAp coating on HELCDEB treated 316L SS exhibits micro-flower structure. Electrochemical results show that the Sr-HAp coating on HELCDEB treated 316L SS possesses maximum corrosion resistance in Ringer's solution.

  6. Improvement of corrosion resistance of M50 bearing steel by implantation with metal ions

    Science.gov (United States)

    Nielsen, B. R.; Torp, B.; Rangel, C. M.; Simplicio, M. H.; Consiglieri, A. C.; DaSilva, M. F.; Paszti, F.; Soares, J. C.; Dodd, A.; Kinder, J.; Pitaval, M.; Thevenard, P.; Wing, R. G.

    1991-07-01

    With the overall objective to improve the service life and reliability of gas turbine engine bearings by increasing their corrosion resistance and rolling contact fatigue life a collaborative project under the EEC BRITE/EURAM programme has been initiated. The project is aimed at developing an ion implantation technique to implant bearing components with metallic species and to optimise the process particularly for applications where salt-water contamination of the lubricating oil might occur. Prior to implanting into bearing components, test specimens of M50 bearing steel implanted with Cr + and Ta + at several doses have been characterised by various techniques. This article reports on the implantation work, the RBS and NRA analysis for depth profiling and independent dose measurement, and the corrosion resistance measurements which have been performed in order to determine the optimum treatment.

  7. Nanotextured stainless steel for improved corrosion resistance and biological response in coronary stenting

    Science.gov (United States)

    Mohan, Chandini C.; Prabhath, Anupama; Cherian, Aleena Mary; Vadukumpully, Sajini; Nair, Shantikumar V.; Chennazhi, Krishnaprasad; Menon, Deepthy

    2014-12-01

    Nanosurface engineering of metallic substrates for improved cellular response is a persistent theme in biomaterials research. The need to improve the long term prognosis of commercially available stents has led us to adopt a `polymer-free' approach which is cost effective and industrially scalable. In this study, 316L stainless steel substrates were surface modified by hydrothermal treatment in alkaline pH, with and without the addition of a chromium precursor, to generate a well adherent uniform nanotopography. The modified surfaces showed improved hemocompatibility and augmented endothelialization, while hindering the proliferation of smooth muscle cells. Moreover, they also exhibited superior material properties like corrosion resistance, surface integrity and reduced metal ion leaching. The combination of improved corrosion resistance and selective vascular cell viability provided by nanomodification can be successfully utilized to offer a cell-friendly solution to the inherent limitations pertinent to bare metallic stents.

  8. The effect of alloying on the resistance of carbon steel for oilfield applications to CO2 corrosion

    Directory of Open Access Journals (Sweden)

    David V. Edmonds

    2005-12-01

    Full Text Available A systematic study has been conducted to investigate the influence of a wide range of alloying elements and different processing conditions on the resistance of low-carbon steels to CO2 corrosion. Strong carbide-forming microalloying elements such as Ti, Nb and V, along with Cr additions, and different levels of Mn, Si, Cu, Mo and Ni, have been explored, along with treatments simulating different processing conditions, for example, controlled rolling, and quenching and tempering. Corrosion testing, including flow loop tests, has been carried out, along with evaluation of mechanical properties, weldability and hot ductility. The programme has developed steels with improved CO2 corrosion resistance and hence identified a potential route for producing more economical carbon steels for oilfield applications. The work has been carried out as part of the UK- Brazil Corrosion Network.

  9. Corrosion resistance of steel fibre reinforced concrete – a literature review

    DEFF Research Database (Denmark)

    Marcos Meson, Victor; Michel, Alexander; Solgaard, Anders

    2016-01-01

    literature concerning chloride-induced corrosion on steel fibres, as well as the impact of steel fibre corrosion on the residual-tensile strength of SFRC. The review confirms the agreement among academics and regulators regarding the superior durability of un-cracked SFRC exposed to chlorides, relative...

  10. Electrochemical methods for characterisation of thermal spray corrosion resistant stainless steel coatings

    NARCIS (Netherlands)

    Hofman, R.; Vreijling, M.P.W.; Ferrari, G.M.; Wit, J.H.W. de

    1998-01-01

    The use of thermal spray stainless steel coatings for protection of low alloyed steels against different types of corrosion is limited due to high porosity levels and oxide inclusions. In this paper electrochemical methods like corrosion potential monitoring and cyclic voltammetry are reported to

  11. Corrosion resistance enhancement of SAE 1020 steel after Chromium implantation by nitrogen ion recoil

    Directory of Open Access Journals (Sweden)

    Geraldo Francisco Gomes

    2005-12-01

    Full Text Available SAE 1020 construction steel is widely used as mortar reinforcement and small machine parts, but aside good surface properties as high ductility, hardness and wear resistance, its surface is prone to severe corrosion. As it is known, Chromium in amount over 12%-13% in the Fe alloys renders them resistance to several corrosive attacks. SAE 1020 samples were recovered with Chromium film and then bombarded either by nitrogen Ion Beam (IB or Plasma Immersion Ion Implantation (PIII to recoil implant Cr atoms in the Fe matrix. Samples treated by 100 keV N+ IB showed irregular, thin Cr profile, remaining a part of the film on the surface, to about 10 nm. Samples treated by 40 kV N PIII presented Cr layer of about 18% at., ranging to around 90 nm. Cr of the film was implanted in the Fe matrix in an almost flat profile. Results of corrosion test showed good performance of the PIII treated sample. The IB treated sample showed some enhancement over the non-treated reference and the only Cr film deposited sample showed no modification on the corrosion behavior as compared to the non-treated reference sample.

  12. Study made of corrosion resistance of stainless steel and nickel alloys in nuclear reactor superheaters

    Science.gov (United States)

    Greenberg, S.; Hart, R. K.; Lee, R. H.; Ruther, W. E.; Schlueter, R. R.

    1967-01-01

    Experiments performed under conditions found in nuclear reactor superheaters determine the corrosion rate of stainless steel and nickel alloys used in them. Electropolishing was the primary surface treatment before the corrosion test. Corrosion is determined by weight loss of specimens after defilming.

  13. Evaluation of erosion-corrosion resistance in Fe-Mn-Al austenitic steels

    OpenAIRE

    William Arnulfo Aperador; Jorge Hernando Bautista Ruiz; Betancurt,Juan D.

    2013-01-01

    In this paper, the effects of Mn and Al against corrosion/errosion resistance of three samples of the Fe-Mn-Al austenitic alloys are evaluated. The samples have composition Fe-(4,9 ~ 11,0 wt. (%)) Al-(17,49 ~ 34,3 wt. (%)) Mn-(0,43 ~ 1,25 wt. (%))C, those were prepared in an induction furnace from high purity materials. The alloys were evaluated in a composed solution of NaCl 0,5 M and Silica in a special chamber and AISI 316 stainless steel as reference material. The electrochemical characte...

  14. Interstitial Hardening of Stainless Steel for Enhanced Corrosion Resistance for Naval Applications

    Science.gov (United States)

    2017-03-01

    process, the nitrogen activity in the gas atmosphere, a(N2), was fixed at 7400, the nitriding time was fixed at 20 h, and an in situ gaseous HCI pre...that notwithstanding any other provision of law , no person shall be subject to any penalty for failing to comply with a collection of information if...Steel for Enhanced Corrosion Resistance for Naval Applications . 5b. GRANT NUMBER N00014-13-1-0691 5c. PROGRAM ELEMENT NUMBER 6. AUTHOR(S) 5d

  15. Influence of silver additions to type 316 stainless steels on bacterial inhibition, mechanical properties, and corrosion resistance

    DEFF Research Database (Denmark)

    Chiang, Wen-Chi; Tseng, I-Sheng; Møller, Per

    2010-01-01

    techniques. The microstructure of these 316 stainless steels was examined, and the influences of silver additions to 316 stainless steels on bacterial inhibition, mechanical properties, and corrosion resistance were investigated. This study suggested that silver-bearing 316 stainless steels could be used......Bacterial contamination is a major concern in many areas. In this study, silver was added to type 316 stainless steels in order to obtain an expected bacteria inhibiting property to reduce the occurrence of bacterial contamination. Silver-bearing 316 stainless steels were prepared by vacuum melting...

  16. Microbiological influenced corrosion resistance characteristics of a 304L-Cu stainless steel against Escherichia coli.

    Science.gov (United States)

    Nan, Li; Xu, Dake; Gu, Tingyue; Song, Xiu; Yang, Ke

    2015-03-01

    Cu-bearing antibacterial stainless steels have been gaining popularity in recent years due to their strong antibacterial performances. However, only a few studies were reported for their actual performances against microbiologically influenced corrosion (MIC). In this study, electrochemical methods and surface analytical techniques were applied to study the MIC resistance characteristics of a 304L-Cu stainless steel (SS) against Escherichia coli in comparison with 304L SS as control. Corrosion tests for specimens after a 21-day exposure to a Luria-Bertani (LB) culture medium with E. coli demonstrated that the 304L-Cu SS considerably reduced the maximum MIC pit depth and the specific weight loss compared with 304L SS (8.3μm and 0.2mg/cm(2) vs. 13.4μm and 0.6mg/cm(2)). Potentiodynamic polarization tests showed that the corrosion current density of the 304L-Cu SS was as much as 4 times lower than that of the 304L SS, indicating that the 304L-Cu SS is a better choice for applications in MIC-prone environments. Copyright © 2014 Elsevier B.V. All rights reserved.

  17. Mechanism of selective corrosion in electrical resistance seam welded carbon steel pipe

    Energy Technology Data Exchange (ETDEWEB)

    Lopez Fajardo, Pedro; Godinez Salcedo, Jesus; Gonzalez Velasquez, Jorge L. [Instituto Politecnico Nacional, Mexico D.F., (Mexico). Escuela Superior de Ingenieria Quimica e Industrias Extractivas. Dept. de Ingenieria Metalurgica

    2009-07-01

    In this investigation the studies of the mechanism of selective corrosion in electrical resistance welded (ERW) carbon steel pipe was started. Metallographic characterizations and evaluations for inclusions were performed. The susceptibility of ERW pipe to selective corrosion in sea water (NACE 1D182, with O{sub 2} or CO{sub 2} + H{sub 2}S) was studied by the stepped potential Potentiostatic electrochemical test method in samples of 1 cm{sup 3} (ASTM G5) internal surface of the pipe (metal base-weld). The tests were looking for means for predicting the susceptibility of ERW pipe to selective corrosion, prior to placing the pipeline in service. Manganese sulfide inclusions are observed deformed by the welding process and they are close to the weld centerline. A slight decarburization at the weld line is observed, and a distinct out bent fiber pattern remains despite the post-weld seam annealing. The microstructure of the weld region consists of primarily polygonal ferrite grains mixed with small islands of pearlite. It is possible to observe the differences of sizes of grain of the present phases in the different zones. Finally, scanning electron microscopic observation revealed that the corrosion initiates with the dissolution of MnS inclusions and with small crack between the base metal and ZAC. (author)

  18. Reduced platelet adhesion and improved corrosion resistance of superhydrophobic TiO₂-nanotube-coated 316L stainless steel.

    Science.gov (United States)

    Huang, Qiaoling; Yang, Yun; Hu, Ronggang; Lin, Changjian; Sun, Lan; Vogler, Erwin A

    2015-01-01

    Superhydrophilic and superhydrophobic TiO2 nanotube (TNT) arrays were fabricated on 316L stainless steel (SS) to improve corrosion resistance and hemocompatibility of SS. Vertically-aligned superhydrophilic amorphous TNTs were fabricated on SS by electrochemical anodization of Ti films deposited on SS. Calcination was carried out to induce anatase phase (superhydrophilic), and fluorosilanization was used to convert superhydrophilicity to superhydrophobicity. The morphology, structure and surface wettability of the samples were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and contact angle goniometry. The effects of surface wettability on corrosion resistance and platelet adhesion were investigated. The results showed that crystalline phase (anatase vs. amorphous) and wettability strongly affected corrosion resistance and platelet adhesion. The superhydrophilic amorphous TNTs failed to protect SS from corrosion whereas superhydrophobic amorphous TNTs slightly improved corrosion resistance of SS. Both superhydrophilic and superhydrophobic anatase TNTs significantly improved corrosion resistance of SS. The superhydrophilic amorphous TNTs minimized platelet adhesion and activation whereas superhydrophilic anatase TNTs activated the formation of fibrin network. On the contrary, both superhydrophobic TNTs (superhydrophobic amorphous TNTs and superhydrophobic anatase TNTs) reduced platelet adhesion significantly and improved corrosion resistance regardless of crystalline phase. Superhydrophobic anatase TNTs coating on SS surface offers the opportunity for the application of SS as a promising permanent biomaterial in blood contacting biomedical devices, where both reducing platelets adhesion/activation and improving corrosion resistance can be effectively combined. Copyright © 2014 Elsevier B.V. All rights reserved.

  19. Effect of Thermal Fields on the Structure of Corrosion-Resistant Steels Under Different Modes of Laser Treatment

    Science.gov (United States)

    Tarasova, T. V.; Gusarov, A. V.; Protasov, K. E.; Filatova, A. A.

    2017-11-01

    The influence of temperature fields on the structure and properties of corrosion-resistant chromium steels under different modes of laser treatment is investigated. A model of heat transfer under laser impact on target is used to plot thermal fields and cycles and cooling rates. It is shown that the model used for computing thermal fields gives tentative geometric sizes of the fusion zones under laser treatment and selective laser fusion. The cooling rate is shown to have decisive influence on the structure of corrosion-resistant steels after laser treatment with surface fusion in devices for pulsed, continuous, and selective laser melting.

  20. Clean steels for steam turbine rotors—their stress corrosion cracking resistance

    Science.gov (United States)

    Magdowski, Ruth M.; Speidel, Markus O.

    1988-06-01

    This work presents the results of a comprehensive study concerning stress corrosion crack growth rates in steam turbine rotor steels exposed to hot water. The effects of stress intensity, temperature, and dissolved gases in the water have been investigated. Special attention has been given to the influence of impurities and alloying elements in the steel such as P, S, Mn, Si, Mo, and Ni, and to the effect of yield strength and fracture toughness on the growth rates of stress corrosion cracks. The results of this study clearly show that there exists a threshold stress intensity of about 20 MNm-3/2 above which the invariably intergranular stress corrosion cracks grow at a constant, stress-independent velocity. This plateau stress corrosion crack growth rate is not affected by the oxygen and carbon dioxide concentration in the water. The temperature and the yield strength of the steel have a strong influence on the growth rate of stress corrosion cracks. In contrast, there is no effect of the steel composition within the range investigated, neither of the impurity elements such as P and S, nor of the major alloying elements such as Mn, Si, Mo, and Ni. Steels with low fracture toughness due to temper embrittlement do not exhibit faster stress corrosion crack growth rates in water than nonembrittled steels. No direct relationship between intergranular temper embrittlement and intergranular stress corrosion crack growth in water can be demonstrated.

  1. Effects of Ultrasonic Nanocrystal Surface Modification on the Residual Stress, Microstructure, and Corrosion Resistance of 304 Stainless Steel Welds

    Science.gov (United States)

    Ye, Chang; Telang, Abhishek; Gill, Amrinder; Wen, Xingshuo; Mannava, Seetha R.; Qian, Dong; Vasudevan, Vijay K.

    2018-01-01

    In this study, ultrasonic nanocrystal surface modification (UNSM) of 304 stainless steel welds was carried out. UNSM effectively eliminates the tensile stress generated during welding and imparts beneficial compressive residual stresses. In addition, UNSM can effectively refine the grains and increase hardness in the near-surface region. Corrosion tests in boiling MgCl2 solution demonstrate that UNSM can significantly improve the corrosion resistance due to the compressive residual stresses and changes in the near-surface microstructure.

  2. Improved Corrosion and Abrasion Resistance of Organic-Inorganic Composite Coated Electro-galvanized Steels for Digital TV Panels

    Energy Technology Data Exchange (ETDEWEB)

    Jo, Du-Hwan; Noh, Sang-Geol; Park, Jong-Tae; Kang, Choon-Ho [POSCO Technical Research Laboratories, Pohang (Korea, Republic of)

    2015-10-15

    Recently, household electronic industries require environmentally-friendly and highly functional steels in order to enhance the quality of human life. Customers especially require both excellent corrosion and abrasion resistant anti-fingerprint steels for digital TV panels. Thus POSCO has developed new functional electro-galvanized steels, which have double coated layers with organic-inorganic composites on the zinc surface of the steel for usage as the bottom chassis panel of TVs. The inorganic solution for the bottom layer consists of inorganic phosphate, magnesium, and zirconium compounds with a small amount of epoxy binder, and affords both improved adhesion properties by chemical conversion reactions and corrosion resistance due to a self-healing effect. The composite solution for the top layer was prepared by fine dispersion of organic-inorganic ingredients that consist of a urethane modified polyacrylate polymer, hardener, silica sol and a titanium complex inhibitor in aqueous media. Both composite solutions were coated on the steel surface by using a roll coater and then cured through an induction furnace in the electro-galvanizing line. New anti-fingerprint steel was evaluated for quality performance through such procedures as the salt spray test for corrosion resistance, tribological test for abrasion resistance, and conductivity test for surface electric conductance regarding to both types of polymer resin and coating weight of composite solution. New composite coated anti-fingerprint steels afford both better corrosion resistance and abrasion properties compared to conventional anti-fingerprint steel that mainly consists of acrylate polymers. Detailed discussions of both composite solutions and experimental results suggest that urethane modifications of acrylate polymers of composite solutions play a key role in enhanced quality performances.

  3. Corrosion Resistance of The Bearing Steel 67SiMnCr6-6-4 with Nanobainitic Structure

    Directory of Open Access Journals (Sweden)

    Skołek E.

    2015-04-01

    Full Text Available The paper describes a comparative study of the corrosion resistance of bearing steel 67SiMnCr6-6-4 after two kinds of nanostructuring treatments and two kinds of conventional quenching and tempering treatments. The nanostructuring treatment consisted of austempering with an isothermal quenching at 240°C and 300°C. The conventional heat treatment consisted on quenching and tempering at 350°C for 1 h and quenching and tempering at 550°C for 1 h. Time and temperature of tempering was chosen so that the hardness of both samples (nanostructured as well as quenched and tempered was similar. The microstructure of steel after each heat treatment was described with the use of transmission electron microscopy (TEM. It was shown, that the austempering conducted at 240°C produced homogenous nanobainitic structure consisting of carbide-free bainite plates with nanometric thickness separated by the layers of retained austenite. The austempering at 300°C produced a sub-micrometric carbide-free bainite with retained austenite in form of layers and small blocks. The conventional heat treatments led to a tempered martensite microstructure. The corrosion resistance study was carried out in Na2SO4 acidic and neutral environment using potentiodynamic and electrochemical impedance spectroscopy (EIS methods. The corrosion resistance of nanostructured steel samples were compared to the steel samples with tempered martensite. The obtained results indicate, that the corrosion resistance of bearing steel with nanobainitic structure is similar to steel with tempered martensite in both acidic and neutral environment. This means that the high density of intercrystalline boundaries in nanobinite does not deteriorate the corrosion properties of the bearing steel.

  4. Corrosion Resistance of Steel 45 Subjected to Electromechanical Treatment and Surface Plastic Deformation

    Science.gov (United States)

    Dudkina, N. G.

    2018-01-01

    The corrosion properties of normalized steel 45 are studied after a combined hardening of its surface layer, which consists of electromechanical treatment and surface plastic deformation (EMT + SPD). The effect of different aggressive environments on the structure, microhardness and corrosion rate of the hardened surface layer is determined.

  5. Cyclotriphosphazene and TiO2 reinforced nanocomposite coated on mild steel plates for antibacterial and corrosion resistance applications

    Science.gov (United States)

    Krishnadevi, Krishnamoorthy; Selvaraj, Vaithilingam

    2016-03-01

    The mild steel surface has been modified to impart anticorrosion and antibacterial properties through a dip coating method followed by thermal curing of a mixture containing amine terminated cyclotriphosphazene and functionalized titanium dioxide nanoparticles reinforced benzoxazine based cyanate ester composite (ATCP/FTiO2/Bz-CE). The corrosion resistance behavior of coating material has been investigated by electrochemical and antibacterial studies by disc diffusion method. The nanocomposites coated mild steels have displayed a good chemical stability over long immersion in a corrosive environment. The protection efficiency has found to be high for ATCP/FTiO2/Bz-CE composites, which can be used in microelectronics and marine applications.

  6. 76 FR 17381 - Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Notice of...

    Science.gov (United States)

    2011-03-29

    ... From the Federal Register Online via the Government Publishing Office DEPARTMENT OF COMMERCE International Trade Administration Certain Corrosion-Resistant Carbon Steel Flat Products From the Republic of Korea: Notice of Final Results of the Sixteenth Administrative Review Correction In notice document 2011...

  7. Development of stress corrosion cracking resistant welds of 321 stainless steel by simple surface engineering

    Science.gov (United States)

    Mankari, Kamal; Acharyya, Swati Ghosh

    2017-12-01

    We hereby report a simple surface engineering technique to make AISI grade 321 stainless steel (SS) welds resistant to stress corrosion cracking (SCC) in chloride environment. Heat exchanger tubes of AISI 321 SS, welded either by (a) laser beam welding (LBW) or by (b) metal inert gas welding (MIG) were used for the study. The welds had high magnitude of tensile residual stresses and had undergone SCC in chloride environment while in service. The welds were characterized using field emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD). Subsequently, the welded surfaces were subjected to buffing operation followed by determination of residual stress distribution and surface roughness by XRD and surface profilometer measurements respectively. The susceptibility of the welds to SCC was tested in buffed and un-buffed condition as per ASTM G-36 in boiling MgCl2 for 5 h and 10 h, followed by microstructural characterization by using optical microscope and FESEM. The results showed that the buffed surfaces (both welds and base material) were resistant to SCC even after 10 h of exposure to boiling MgCl2 whereas the un-buffed surfaces underwent severe SCC for the same exposure time. Buffing imparted high magnitude of compressive stresses on the surface of stainless steel together with reduction in its surface roughness and reduction in plastic strain on the surface which made the welded surface, resistant to chloride assisted SCC. Buffing being a very simple, portable and economic technique can be easily adapted by the designers as the last step of component fabrication to make 321 stainless steel welds resistant to chloride assisted SCC.

  8. Improving corrosion and wear resistance of FV520B steel by high current pulsed electron beam surface treatment

    Energy Technology Data Exchange (ETDEWEB)

    Hao, Shengzhi, E-mail: ebeam@dlut.edu.cn [Key Laboratory of Material Modification by Laser, Ion and Electron Beams, Ministry of Education, Dalian University of Technology, Dalian 116024 (China); Zhao, Limin [School of Materials Science and Engineering, Dalian Jiaotong University, Dalian 116028 (China); Zhang, Yanlong; Wang, Huihui [Key Laboratory of Material Modification by Laser, Ion and Electron Beams, Ministry of Education, Dalian University of Technology, Dalian 116024 (China)

    2015-08-01

    Highlights: • HCPEB surface treatment was conducted on FV520B steel. • Surface layer ∼10 μm was refined with elements homogenization. • Remelted layer exhibited 〈2 0 0〉 preferential orientation. • Corrosion potential increased and corrosion rate decreased one order of magnitude. • Wear resistance increased by 3 times. - Abstract: High current pulsed electron beam (HCPEB) surface treatment was conducted on FV520B steel with accelerating voltage 27 kV, pulse duration 2.5 μs, energy density 5 J/cm{sup 2} and 1–25 pulses. The surface microstructure and element distribution were examined by using scanning electron microscope (SEM), electron probe micro-analysis (EPMA) and X-ray diffraction (XRD) methods. After HCPEB treatments, the surface microstructure became refined and uniform with an average grain size less than 2 μm and a preferential solidification orientation in 〈2 0 0〉 direction. The thickness of surface remelted layer was ∼4 μm. The initial precipitated particles in surface layer of depth ∼10 μm were dissolved into the base matrix and gave a homogenous element distribution. The HCPEB modified surface exhibited an effective improvement in corrosion and wear resistance. The corrosion potential shifted towards positive and the corrosion rate decreased nearly one order of magnitude, while the wear resistance after 25 pulses of HCPEB treatment increased by 3 times as compared with the initial FV520B steel.

  9. Influence of the post-weld surface treatment on the corrosion resistance of the duplex stainless steel 1.4062

    Science.gov (United States)

    Rosemann, P.; Müller, C.; Baumann, O.; Modersohn, W.; Halle, T.

    2017-03-01

    The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polished or blasting depending on the application and the requested corrosion resistance. Blasted surfaces are often used in industrial practice due to the easier and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the different performed corrosion tests (potential measurement, KorroPad-test and pitting potential) on welding seams with different surface treatments.

  10. Corrosive-wear resistance of stainless steels for the impeller of slurry pump used in zinc hydrometallurgy process

    Directory of Open Access Journals (Sweden)

    Ping LI

    2005-08-01

    Full Text Available This paper presents corrosive-wear (C-W behaviors of three kinds of steels under the simulating condition of traditional zinc hydrometallurgy process by using a self-made rotating disk apparatus. Result shows that pure wear loss rate is significantly larger than pure corrosion loss rate. Under this C-W condition, the ranking of C-W resistance is S2 > S3 > S1 (S1: austenite stainless steel; S2: CD-4MCu duplex stainless steel; S3 :17-4PH stainless steel. S2 has excellent C-W resistance due to strong surface deformation strengthening effect of high-density dislocations of the γ phase. S3 also has excellent C-W resistance owing to high hardness and strength. However, S1 does not show good C-W resistance under strong erosion of liquid-solid slurry because of its single-phase austenitic structure and very low hardness. As a result, duplex stainless steels as well as 17-4 PH stainless steel can be used as impeller candidate materials in the zinc hydrometallurgy process due to their excellent C-W resistance and lower cost.

  11. Analysis of the Long-Term Corrosion Behavior of X80 Pipeline Steel in Acidic Red Soil Using Electrical Resistance Test Technique

    Directory of Open Access Journals (Sweden)

    Shuaixing Wang

    2015-01-01

    Full Text Available The long-term corrosion rate of X80 steel in an acidic red soil was monitored in situ by using a precise electrical resistance (ER test system. The corrosion characteristics of X80 steel were examined via SEM, EDS, and XRD. The results indicated that the corrosion rate determined from ER test was very similar to that obtained from the mass loss test. The ER test technique made it possible to predict the long-term corrosion rate of steel in soil in situ. The corrosion rate of X80 steel in acidic red soil was about 0.0902 mm/a at 38 weeks, but the corrosion rate was dropped to 0.0226 mm/a after 5 years. The final corrosion product layer was composed mainly of FeOOH, γ-Fe2O3, and FeCO3.

  12. Laser gas assisted treatment of steel 309: Corrosion and scratch resistance of treated surface

    Science.gov (United States)

    Toor, Ihsan-ul-Haq; Yilbas, B. S.; Ahmed, Junaid; Karatas, C.

    2017-10-01

    Laser gas assisted surface treatment of steel 309 is carried out and the characteristics of the resulting surface are analyzed using the analytical tools. Scanning electron and 3-D optical microscopes are used to assess the morphological and metallurgical changes in the laser treated layer. Energy spectroscopy and X-ray diffraction are carried out to determine the elemental composition and compounds formed on the laser treated surface. The friction coefficient of the laser treated surface is measured using the micro-tribometer and compared to that of the as received surface. The corrosion resistance of the laser treated and as received surfaces is measured incorporating the electrochemical tests. It is found that laser treatment results in a dense layer and formation of nitride compounds at the surface. This enhances the microhardness at the laser treated surface. The friction coefficient attains lower values at the laser treated surface than that corresponding to the as received surface. The corrosion rate of the surface reduces significantly after the laser treatment process, which can be attributed to the passive layer at the surface via formation of a dense layer and nitride compounds in the surface vicinity. In addition, the number of pit sites decreased for the laser treated surface than that of as received surface.

  13. Corrosion resistance of a steel under an oxidizing atmosphere in a fluid catalytic cracking regenerator

    Directory of Open Access Journals (Sweden)

    Ieda Caminha

    2004-03-01

    Full Text Available In the present work, the corrosion resistance of an ASTM A 387 G11 steel was evaluated under two conditions: an oxidizing atmosphere in a fluid catalytic cracking regenerator of a petroleum processing unit and a simulated atmosphere in the laboratory, at temperatures of 650 °C and 700 °C. The characterization of the phases present in the oxidized layer was carried out by X-ray diffraction (XRD, optical microscopy (OM and scanning electron microscopy (SEM with X-ray energy dispersive analysis (EDS. Severe corrosion was observed after exposure to both the real and simulated conditions, with formation of several iron oxides (Fe2O3, Fe3O4 and FeO in the product scale layer, as well as a slight inner oxidation and sulfidation of chromium in the substrate. Internal nitridation of the silicon and the manganese was observed only in the real condition, probably related to the long-term exposure inside the regenerator.

  14. Pitting corrosion resistance of a novel duplex alloy steel in alkali-activated slag extract in the presence of chloride ions

    Science.gov (United States)

    Shi, Jin-jie; Ming, Jing; Liu, Xin

    2017-10-01

    In this study, two types of reinforcing steels (conventional low-carbon steel and a novel duplex alloy steel with Cr and Mo) were exposed to chloride-contaminated extract solutions (ordinary Portland cement (OPC) extract and alkali-activated slag (AAS) extract) to investigate their pitting corrosion resistance. The results confirm that the pitting corrosion resistance of the alloy steel is much higher than that of the low-carbon steel in both extract solutions with various NaCl concentrations. Moreover, for each type of steel, the AAS extract contributes to a higher pitting corrosion resistance compared with the OPC extract in the presence of chloride ions, likely because of the formation of flocculent precipitates on the steel surface.

  15. Corrosion resistance of stainless steels and high Ni-Cr alloys to acid fluoride wastes

    Energy Technology Data Exchange (ETDEWEB)

    Smith, H.D.; Mackey, D.B.; Pool, K.H. (Pacific Northwest Lab., Richland, WA (United States)); Schwenk, E.B. (Westinghouse Hanford Co., Richland, WA (United States))

    1992-04-01

    TRUEX processing of Hanford Site waste will utilize potentially corrosive acid fluoride processing solutions. Appropriate construction materials for such a processing facility need to be identified. Toward this objective, candidate stainless steels and high Ni-Cr alloys have been corrosion tested in simulated acid fluoride process solutions at 333K. The high Ni-Cr alloys exhibited corrosion rates as low as 0.14 mm/y in a solution with an HF activity of about 1.2 M, much lower than the 19 to 94 mm/y observed for austenitic stainless steels. At a lower HF activity (about 0.008 M), stainless steels display delayed passivation while high Ni-Cr alloys display essentially no reaction.

  16. Mechanically robust superhydrophobic steel surface with anti-icing, UV-durability, and corrosion resistance properties.

    Science.gov (United States)

    Wang, Nan; Xiong, Dangsheng; Deng, Yaling; Shi, Yan; Wang, Kun

    2015-03-25

    A superhydrophobic steel surface was prepared through a facile method: combining hydrogen peroxide and an acid (hydrochloric acid or nitric acid) to obtain hierarchical structures on steel, followed by a surface modification treatment. Empirical grid maps based on different volumes of H2O2/acid were presented, revealing a wettability gradient from "hydrophobic" to "rose effect" and finally to "lotus effect". Surface grafting has been demonstrated to be realized only on the oxidized area. As-prepared superhydrophobic surfaces exhibited excellent anti-icing properties according to the water-dripping test under overcooled conditions and the artificial "steam-freezing" (from 50 °C with 90% humidity to the -20 °C condition) test. In addition, the surfaces could withstand peeling with 3M adhesive tape at least 70 times with an applied pressure of 31.2 kPa, abrasion by 400 grid SiC sandpaper for 110 cm under 16 kPa, or water impacting for 3 h without losing superhydrophobicity, suggesting superior mechanical durability. Moreover, outstanding corrosion resistance and UV-durability were obtained on the prepared surface. This successful fabrication of a robust, anti-icing, UV-durable, and anticorrosion superhydrophobic surface could yield a prospective candidate for various practical applications.

  17. Effects of Thermal Aging on Microstructure and Corrosion Resistance of AISI 317L Steel Weld Metal in the FSW Process

    OpenAIRE

    Farneze, Humberto Nogueira; Tavares,Sérgio Souto Maior; Pardal, Juan Manuel; Londoño,Antônio José Ramírez; Pereira,Victor Ferrinho; Barbosa, Cássio

    2015-01-01

    The AISI 317L grade is an austenitic stainless steel with high Mo content (3.0 wt% min.). Due to the higher pitting resistance, this grade has replaced AISI 316L steel in many applications where the corrosion resistance is a critical property. However, the high Mo can induce phase transformations in high temperature services. In modern oil refinaries and petrochemical industries AISI 317L has been selected for temperatures as high as 550 °C. The goal of this work was to analyze the microstruc...

  18. Study of the Corrosion Resistance of Austenitic Stainless Steels during Conversion of Waste to Biofuel.

    Science.gov (United States)

    Cabrini, Marina; Lorenzi, Sergio; Pastore, Tommaso; Pellegrini, Simone; Burattini, Mauro; Miglio, Roberta

    2017-03-22

    The paper deals with the corrosion behavior of stainless steels as candidate materials for biofuel production plants by liquefaction process of the sorted organic fraction of municipal solid waste. Corrosion tests were carried out on AISI 316L and AISI 304L stainless steels at 250 °C in a batch reactor during conversion of raw material to bio-oil (biofuel precursor), by exposing specimens either to water/oil phase or humid gas phase. General corrosion rate was measured by weight loss tests. The susceptibility to stress corrosion cracking was evaluated by means of U-bend specimens and slow stress rate tests at 10-6 or 10-5 s-1 strain rate. After tests, scanning electron microscope analysis was carried out to detect cracks and localized attacks. The results are discussed in relation with exposure conditions. They show very low corrosion rates strictly dependent upon time and temperature. No stress corrosion cracking was observed on U-bend specimens, under constant loading. Small cracks confined in the necking cone of specimens prove that stress corrosion cracking only occurred during slow strain rate tests at stresses exceeding the yield strength.

  19. Corrosion resistance of steel fibre reinforced concrete – a literature review

    OpenAIRE

    Marcos Meson, Victor; Michel, Alexander; Solgaard, Anders; Fischer, Gregor; Edvardsen, Carola; Skovhus, Torben Lund

    2016-01-01

    Steel fibre reinforced concrete (SFRC) is increasingly being used in the construction of prefabricated segmental linings for bored tunnels, since it entails simplified production processes and higher quality standards. However, international standards and guidelines are not consistent regarding the consideration of steel fibres for the structural verification of SFRC elements exposed to corrosive environments, hampering the development of civil infrastructure built of SFRC. In particular, the...

  20. Passive behaviour of alloy corrosion-resistant steel Cr10Mo1 in simulating concrete pore solutions with different pH

    Energy Technology Data Exchange (ETDEWEB)

    Ai, Zhiyong, E-mail: 230139452@seu.edu.cn [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China); Jiang, Jinyang, E-mail: jiangjinyang16@163.com [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China); Sun, Wei, E-mail: sunwei@seu.edu.cn [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China); Song, Dan, E-mail: songdancharls@hhu.edu.cn [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China); College of Mechanics and Materials, Hohai University, Nanjing 210098, Jiangsu (China); Ma, Han, E-mail: mahan-iris@shasteel.cn [Research Institute of Jiangsu Shasteel Iron and Steel, Zhangjiagang 215625, Jiangsu (China); Zhang, Jianchun, E-mail: Zhangjc-iris@shasteel.cn [Research Institute of Jiangsu Shasteel Iron and Steel, Zhangjiagang 215625, Jiangsu (China); Wang, Danqian, E-mail: wonderbaba@126.com [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China)

    2016-12-15

    Highlights: • A new alloy corrosion-resistant steel Cr10Mo1 is developed for reinforcing rebar of concrete in severe environments. • The effects of pH on the passive behaviour of Cr10Mo1 steel compared with plain carbon steel were studied systematically by electrochemical techniques and surface analysis. • The mechanism for self-reinforcing passivity against carbonation of the corrosion-resistant steel is revealed. - Abstract: The passive behaviour of new alloy corrosion-resistant steel Cr10Mo1 and plain carbon steel (as a comparison) in simulating concrete pore solutions of different pH (ranging from 13.5 to 9.0) under open circuit potential conditions, was evaluated by various electrochemical techniques: potentiodynamic polarization, capacitance measurements and electrochemical impedance spectroscopy. The chemical composition and structure of passive films were investigated by X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectroscopy (SIMS). The electrochemical responses of passive films show that Cr10Mo1 steel has an increasing passivity with pH decreasing while carbon steel dose conversely, revealing carbonation does no negative effect on passivation of the corrosion-resistant steel. SIMS reveals that the passive film on the corrosion-resistant steel presents a bilayer structure: an outer layer mainly consisting of Fe oxides and hydroxides, and an inner layer enriched in Cr species, while only a Fe-concentrated layer for carbon steel. According to the XPS analysis results, as the pH decreases, more stable and protective Cr oxides are enriched in the film on Cr10Mo1 steel while Fe oxides gradually decompose. Higher content of Cr oxides in the film layer provides Cr10Mo1 corrosion-resistant steel more excellent passivity at lower pH.

  1. Electrochemical study on the corrosion resistance of plasma nanocoated 316L stainless steel in albumin- and lysozyme-containing electrolytes

    Science.gov (United States)

    Jones, John Eric; Chen, Meng; Chou, Ju; Yu, Qingsong

    2017-01-01

    The physiological corrosion resistance of plasma nanocoated 316L stainless steel was studied in protein-containing electrolytes using electrochemical methods. Plasma nanocoatings with thicknesses of 20–30 nm were deposited onto 316L stainless steel coupons in a glow discharge of trimethylsilane (TMS) or its mixture with oxygen gas under various gas ratios. The surface chemistries of the plasma nanocoatings were characterized using Fourier transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS). Corrosion properties of the plasma nanocoated 316L stainless steel coupons were assessed using potentiodynamic polarization, cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS) in phosphate-buffered saline (PBS) electrolytes that contain bovine serum albumin (BSA) or lysozyme. It was found that BSA adsorption on the plasma nanocoated 316L coupons was heavily favored. BSA adsorption on the plasma nanocoating surfaces could block charge-transfer reactions between the electrolyte and 316L substrate, and thus stabilize the 316L substrates from further corrosion. In contrast, lysozyme adsorption on the plasma nanocoated specimens was not as pronounced and mildly influenced the corrosion properties of the plasma nanocoated 316L stainless steel.

  2. Corrosion resistance of Zn-Co-Fe alloy coatings on high strength steel

    NARCIS (Netherlands)

    Lodhi, Z.F.; Mol, J.M.C.; Hovestad, A.; Hoen-Velterop, L. 't; Terryn, H.; Wit, J.H.W.de

    2009-01-01

    The corrosion properties of electrodeposited zinc-cobalt-iron (Zn-Co-Fe) alloys (up to 40 wt.% Co and 1 wt.% Fe) on steel were studied by using various electrochemical techniques and compared with zinc (Zn) and cadmium (Cd) coatings in 3.5% NaCl solution. It was found that with an increase in Co

  3. Atmospheric corrosion of mild steel

    OpenAIRE

    Morcillo, M.; de la Fuente, D.; Díaz, I.; Cano, H.

    2011-01-01

    The atmospheric corrosion of mild steel is an extensive topic that has been studied by many authors in different regions throughout the world. This compilation paper incorporates relevant publications on the subject, in particular about the nature of atmospheric corrosion products, mechanisms of atmospheric corrosion and kinetics of the atmospheric corrosion process, paying special attention to two matters upon which relatively less information has been published: a) the morphology of steel c...

  4. Improvement of erosion and erosion corrosion resistance of AISI420 stainless steel by low temperature plasma nitriding

    Science.gov (United States)

    Xi, Yun-tao; Liu, Dao-xin; Han, Dong

    2008-07-01

    Plasma nitriding experiments were carried out with DC-pulsed plasma in 25% N 2 + 75% H 2 atmosphere at low temperature (350 °C) and normal temperature (550 °C) for 15 h. The composition, microstructure, microhardness profiles, residual stress profiles and electrochemical impedance spectrum analyses of the nitrided samples were examined. The influence of plasma nitriding on the erosion and erosion-corrosion resistance of AISI 420 martensitic stainless steel was investigated using a jet solid particle erosion tester and a slurry erosion-corrosion tester. Results showed that the 350 °C nitriding layer was dominated by ɛ-Fe 3N and α N phase, a supersaturated nitrogen solid solution. However, nitrogen would react with Cr in the steel to form CrN precipitates directly during 550 °C nitriding, which would lead to the depletion of Cr in the solid solution phase of the nitrided layer. Both 350 and 550 °C plasma nitriding could improve the erosion resistance of AISI420 stainless steel under dry erosion, but the former showed better results. In both neutral and acid environment, while the erosion-corrosion resistance of AISI 420 was improved by means of 350 °C nitriding, it was decreased through 550 °C nitriding.

  5. Synergy effects of Cu and Sn on pitting corrosion resistance of ultra-purified medium chromium ferritic stainless steel

    Science.gov (United States)

    Zhang, XiangJun; Liu, ZhenYu

    2017-03-01

    The influence of combination of Cu and Sn on pitting resistance of ultra-purified medium chromium ferritic stainless steel in 3.5 wt.% NaCl at 25°C was investigated by using electrochemical method. The results show that there is synergy effect between Cu and Sn, and the strong interaction between Cu and Sn in ferritic stainless steels clearly affects their pitting corrosion behaviour in 3.5% NaCl. A mechanism of the synergy of Cu and Sn was discussed.

  6. Seismic load resistance of reinforcing steels in the as delivered condition and after corrosion - relevant material characteristics for performance evaluation

    Energy Technology Data Exchange (ETDEWEB)

    Moersch, Ing. Joerg [Max Aicher Engineering GmbH, Freilassing (Germany)

    2016-10-15

    This type of accelerated corrosion test was used to study the high number of test samples in due time. The corrosion phenomena obtained in salt spray testing deviate significantly from corrosion phenomena (pitting factor) obtained in practical conditions. Salt spray testing represents practical conditions for the more uniform corrosion as a result of a severe carbonation of the concrete and/or for higher chloride contents at the surface of the rebar. At low corrosion current densities the effect of pit depth on residual mechanical performance might be underestimated. Reinforced concrete (r.c.) buildings in seismic areas shall be designed to guarantee enough ductile resources as for example a sufficient rotational capacity to allow for load re-distribution. The rotational capacity is directly dependent on the ductility of the reinforcing steel which is generally expressed as elongation at maximum load (A+g{sub t}) and the hardening ratio (R{sub m}/R{sub e}). A direct testing of the seismic load resistance of reinforcing steels is not part of the construction product standards. Therefore it was decided by European Commission to introduce this performance requirement in the mandate for the revision of EN 10080:2005. In parallel to the standardization process a research project was carried out to deliver the scientific background.

  7. Corrosion resistance of various bio-films deposited on austenitic cast steel casted by lost-wax process and in gypsum mould

    Directory of Open Access Journals (Sweden)

    J. Gawroński

    2010-01-01

    Full Text Available This work is the next of a series concerning the improvement of austenitic cast steel utility predicted for use in implantology for complicated long term implants casted by lost-wax process and in gypsum mould. Austenitic cast steel possess chemical composition of AISI 316L medical steel used for implants. In further part of present work investigated cast steel indicated as AISI 316L medical steel. Below a results of electrochemical corrosion resistance of carbon layer and bi-layer of carbon/HAp deposited on AISI 316L researches are presented. Coatings were manufactured by RF PACVD and PLD methods respectively. Obtained results, unequivocally indicates on the improvement of this type of corrosion resistance by substrate material with as deposited carbon layer. While bi-layer of carbon/HAp are characterized by very low corrosion resistance.

  8. Influence of Magnesium Ions in the Seawater Environment on the Improvement of the Corrosion Resistance of Low-Chromium-Alloy Steel

    Directory of Open Access Journals (Sweden)

    Sol-Ji Song

    2018-01-01

    Full Text Available This study examined the synergic effect of alloying the element Cr and the environmental element Mg2+ ions on the corrosion property of a low-alloy steel in seawater at 60 °C, by means of electrochemical impedance spectroscopy (EIS, linear polarization resistance (LPR tests and weight-loss tests. The Mg2+ ions in seawater played an important role in lowering the electron transfer of the rust layer in the Cr-containing steel. The corrosion resistance of the Cr-containing steel is superior to that of blank steel in Mg2+ ions containing seawater. XPS and XRD results indicated that the formation of MgFe2O4 and a mixed layer (Cr oxide + FeCr2O4 + MgCr2O4 improved the corrosion resistance of the low-alloy steel in the seawater.

  9. corrosion inhibitor for carbon steels

    African Journals Online (AJOL)

    potentiodynamic polarisation techniques. It was found that. CNSL reduces the extent of the electrochemical processes taking place on carbon steel undergoing corrosion. The corrosion rate of the carbon steel was reduced by over 92 % when only 300 ppm of CNSL was applied. This indicates that. CNSL is a potential ...

  10. Development of rapidly quenched nickel-based non-boron filler metals for brazing corrosion resistant steels

    Science.gov (United States)

    Ivannikov, A.; Kalin, B.; Suchkov, A.; Penyaz, M.; Yurlova, M.

    2016-04-01

    Corrosion-resistant steels are stably applied in modern rocket and nuclear technology. Creating of permanent joints of these steels is a difficult task that can be solved by means of welding or brazing. Recently, the use rapidly quenched boron-containing filler metals is perspective. However, the use of such alloys leads to the formation of brittle borides in brazing zone, which degrades the corrosion resistance and mechanical properties of the compounds. Therefore, the development of non-boron alloys for brazing stainless steels is important task. The study of binary systems Ni-Be and Ni-Si revealed the perspective of replacing boron in Ni-based filler metals by beryllium, so there was the objective of studying of phase equilibrium in the system Ni-Be-Si. The alloys of the Ni-Si-Be with different contents of Si and Be are considered in this paper. The presence of two low-melting components is revealed during of their studying by methods of metallography analysis and DTA. Microhardness is measured and X-ray diffraction analysis is conducted for a number of alloys of Ni-Si-Be. The compositions are developed on the basis of these data. Rapidly quenched brazing alloys can be prepared from these compositions, and they are suitable for high temperature brazing of steels.

  11. Enhanced Corrosion Resistance of Carbon Steel in Hydrochloric Acid Solution by Eriobotrya Japonica Thunb. Leaf Extract: Electrochemical Study

    National Research Council Canada - National Science Library

    Wenjing Yang; Qihui Wang; Ke Xu; Yanjun Yin; Hebin Bao; Xueming Li; Lidan Niu; Shiqi Chen

    2017-01-01

    The biodegradable inhibitors, which could effectively reduce the rate of corrosion of carbon steel, were investigated by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS...

  12. The effect of σ-phase precipitation at 800°C on the corrosion resistance in sea-water of a high alloyed duplex stainless steel

    NARCIS (Netherlands)

    Wilms, M.E.; Gadgil, V.J.; Krougman, J.M.; Ijsseling, F.P.

    1994-01-01

    Super-duplex stainless steels are recently developed high alloyed stainless steels that combine good mechanical properties with excellent corrosion resistance. Because of a high content of chromium and molybdenum, these alloys are susceptible to σ-phase precipitation during short exposure to

  13. Influence of thermal spraying parameters on the corrosion resistance of aluminium oxide coatings deposited on steel 1020

    Science.gov (United States)

    Salas, Y.; Vera, E.; Moreno, M.; Pineda, Y.

    2016-02-01

    Parameters required for the preparation of coatings of aluminium oxide deposited on AISI 1020 steels were determined according to their thickness and type of flame to differentiate their behaviour against corrosion. Commercial powders were used by the method of thermal spraying deposition. The coatings were analysed by OM (optical microscopy), the thickness was measured by means of a coating thickness gauge and electrochemical techniques variables measured was the Linear Polarization Resistance (LPR) and approximation Tafel potentiodynamic curves. The corrosion current for steel 1020 with Na2SO4 electrolyte of 3.5% is of the order of hundreds of A/cm2 and coated steel given in the order of A/cm2, which leads to think that the projection produces coatings uniform low closed porosity, although techniques DC indicate a significant porosity as is observable current response to the potentiodynamic curve. The observed thicknesses fall into the hundreds of microns and little uniformity was noted in this coatings. The coatings deposited by oxidizing flame was better performance in corrosion than the coating deposited by neutral flame.

  14. Atmospheric corrosion of mild steel

    OpenAIRE

    Morcillo, Manuel; Fuente, Daniel de la; Díaz, Iván; Cano, H.

    2011-01-01

    The atmospheric corrosion of mild steel is an extensive topic that has been studied by many authors in different regions throughout the world. This compilation paper incorporates relevant publications on the subject, in particular about the nature of atmospheric corrosion products, mechanisms of atmospheric corrosion and kinetics of the atmospheric corrosion process, paying special attention to two matters upon which relatively less information has been published: a) the morpholog...

  15. Improvement in the corrosion resistance of carbon steel in acidic condition using naphthalen-2-ylnaphthalene-2-carboxammide inhibitor.

    Science.gov (United States)

    Kannan, Perumal; Rao, Toleti Subba; Rajendran, Nallaiyan

    2017-09-18

    In the present investigation, the anti corrosive performance of synthesized Naphthalen-2-yl Naphthalene-2-Carboxammide (NNC) in 1 N HCl solution as corrosion inhibitor on carbon steel was studied at room temperature. Potentiodynamic polarization study revealed the mixed behavior of the inhibitor NNC along with inhibition efficiency. The inhibition efficiency of NNC increases with increasing inhibitor concentration. The electrochemical noise analysis (ENA) and electrochemical impedance spectroscopy (EIS) studies have showed that noise resistance (Rn) and charge transfer resistance (Rct) values were increased with addition of inhibitor concentrations. The synthesized and adsorbed bonds of inhibitor with the metal atom were characterized by ATR-FTIR spectroscopy. The adsorption isotherm explored that the adsorption of NNC obeyed Langmuir adsorption to bond with metal surface at carbon steel/HCl solution interface. The thermodynamic properties were calculated to discuss the adsorption mechanism of corrosion inhibition. Atomic force microscope (AFM) study showed a less corroded and roughness surface morphology, which is due to the formation of protective film layer on the surface. Quantum chemical parameters were calculated and correlated with respect to inhibitive performance of NNC. The study revealed that the adsorption nature of inhibitor has both physisorption and chemisorption phenomena. Copyright © 2017 Elsevier Inc. All rights reserved.

  16. Effect of thermal treatment on the corrosion resistance of Type 316L stainless steel exposed in supercritical water

    Energy Technology Data Exchange (ETDEWEB)

    Jiao, Y. [Department of Materials Science & Engineering, McMaster University, Hamilton, ON (Canada); Zheng, W. [CanmetMATERIALS, Natural Resources Canada, Hamilton, ON (Canada); Guzonas, D.A. [Canadian Nuclear Laboratories Chalk River Laboratories, ON (Canada); Cook, W.G. [Department of Chemical Engineering, University of New Brunswick, Fredericton, NB (Canada); Kish, J.R., E-mail: kishjr@mcmaster.ca [Department of Materials Science & Engineering, McMaster University, Hamilton, ON (Canada)

    2015-09-15

    There are still unknown aspects about the growth mechanism of oxide scales formed on candidate stainless steel fuel cladding materials during exposure in supercritical water (SCW) under the conditions relevant to the Canadian supercritical water-cooled reactor (SCWR). The tendency for intermetallic precipitates to form within the grains and on grain boundaries during prolonged exposure at high temperatures represents an unknown factor to corrosion resistance, since they tend to bind alloyed Cr. The objective of this study was to better understand the extent to which intermetallic precipitates affects the mode and extent of corrosion in SCW. Type 316L stainless steel, used as a model Fe–Cr–Ni–Mo alloy, was exposed to 25 MPa SCW at 550 °C for 500 h in a static autoclave for this purpose. Mechanically-abraded samples were tested in the mill-annealed (MA) and a thermally-treated (TT) condition. The thermal treatment was conducted at 815 °C for 1000 h to precipitate the carbide (M{sub 23}C{sub 6}), chi (χ), laves (η) and sigma (σ) phases. It was found that although relatively large intermetallic precipitates formed at the scale/alloy interface locally affected the oxide scale formation, their discontinuous formation did not affect the short-term overall apparent corrosion resistance.

  17. Effect of thermal treatment on the corrosion resistance of Type 316L stainless steel exposed in supercritical water

    Science.gov (United States)

    Jiao, Y.; Zheng, W.; Guzonas, D. A.; Cook, W. G.; Kish, J. R.

    2015-09-01

    There are still unknown aspects about the growth mechanism of oxide scales formed on candidate stainless steel fuel cladding materials during exposure in supercritical water (SCW) under the conditions relevant to the Canadian supercritical water-cooled reactor (SCWR). The tendency for intermetallic precipitates to form within the grains and on grain boundaries during prolonged exposure at high temperatures represents an unknown factor to corrosion resistance, since they tend to bind alloyed Cr. The objective of this study was to better understand the extent to which intermetallic precipitates affects the mode and extent of corrosion in SCW. Type 316L stainless steel, used as a model Fe-Cr-Ni-Mo alloy, was exposed to 25 MPa SCW at 550 °C for 500 h in a static autoclave for this purpose. Mechanically-abraded samples were tested in the mill-annealed (MA) and a thermally-treated (TT) condition. The thermal treatment was conducted at 815 °C for 1000 h to precipitate the carbide (M23C6), chi (χ), laves (η) and sigma (σ) phases. It was found that although relatively large intermetallic precipitates formed at the scale/alloy interface locally affected the oxide scale formation, their discontinuous formation did not affect the short-term overall apparent corrosion resistance.

  18. Effect of electromagnetic interaction during fusion welding of AISI 2205 duplex stainless steel on the corrosion resistance

    Energy Technology Data Exchange (ETDEWEB)

    García-Rentería, M.A., E-mail: marcogarciarenteria@uadec.edu.mx [Faculty of Metallurgy, Autonomous University of Coahuila, Carretera 57 Km. 5, CP 25720, Monclova, Coahuila (Mexico); López-Morelos, V.H., E-mail: vhlopez@umich.mx [Instituto de Investigación en Metalurgia y Materiales, Universidad Michoacana de San Nicolás de Hidalgo, A.P. 888, CP 58000, Morelia, Michoacán (Mexico); González-Sánchez, J., E-mail: jagonzal@uacam.mx [Centre for Corrosion Research, Autonomous University of Campeche, Av. Agustín Melgar s/n, Col. Buenavista, CP 24039, Campeche, Cam (Mexico); García-Hernández, R., E-mail: rgarcia@umich.mx [Instituto de Investigación en Metalurgia y Materiales, Universidad Michoacana de San Nicolás de Hidalgo, A.P. 888, CP 58000, Morelia, Michoacán (Mexico); Dzib-Pérez, L., E-mail: franciscocl7@yahoo.com.mx [Centre for Corrosion Research, Autonomous University of Campeche, Av. Agustín Melgar s/n, Col. Buenavista, CP 24039, Campeche, Cam (Mexico); Curiel-López, F.F., E-mail: franciscocl7@yahoo.com.mx [Faculty of Metallurgy, Autonomous University of Coahuila, Carretera 57 Km. 5, CP 25720, Monclova, Coahuila (Mexico)

    2017-02-28

    Highlights: • Application of EMILI during welding 2205 Duplex stainless steel hindered the coarsening of δ grains in HTHAZ and promoted regeneration of γ. • Welds made with simultaneous EMILI presented TPI values at the HTHAZ similar to those for BM. • Welds made under 3, 12 and 15 mT presented a mass loss by anodic polarisation similar to that observed for the as-received BM. • This behaviour is due to changes in the dynamics of microstructural evolution during welding with EMILI. - Abstract: The effect of electromagnetic interaction of low intensity (EMILI) applied during fusion welding of AISI 2205 duplex stainless steel on the resistance to localised corrosion in natural seawater was investigated. The heat affected zone (HAZ) of samples welded under EMILI showed a higher temperature for pitting initiation and lower dissolution under anodic polarisation in chloride containing solutions than samples welded without EMILI. The EMILI assisted welding process developed in the present work enhanced the resistance to localised corrosion due to a modification on the microstructural evolution in the HAZ and the fusion zone during the thermal cycle involved in fusion welding. The application of EMILI reduced the size of the HAZ, limited coarsening of the ferrite grains and promoted regeneration of austenite in this zone, inducing a homogeneous passive condition of the surface. EMILI can be applied during fusion welding of structural or functional components of diverse size manufactured with duplex stainless steel designed to withstand aggressive environments such as natural seawater or marine atmospheres.

  19. Influence of mill scale and rust layer on the corrosion resistance of low-alloy steel in simulated concrete pore solution

    Science.gov (United States)

    Shi, Jin-jie; Ming, Jing

    2017-01-01

    Electrochemical impedance spectroscopy, cyclic potentiodynamic polarization measurements, and scanning electron microscopy in conjunction with energy-dispersive X-ray spectroscopy were used to investigate the influence of mill scale and rust layer on the passivation capability and chloride-induced corrosion behaviors of conventional low-carbon (LC) steel and low-alloy (LA) steel in simulated concrete pore solution. The results show that mill scale exerts different influences on the corrosion resistance of both steels at various electrochemical stages. We propose that the high long-term corrosion resistance of LA steel is mainly achieved through the synergistic effect of a gradually formed compact, adherent and well-distributed Cr-enriched inner rust layer and the physical barrier protection effect of mill scale.

  20. THE EFFECT OF THE ANNEALING TEMPERATURE ON THE CORROSION RESISTANCE OF WELD JOINT OF AISI 310 STEEL - SHORT COMMUNICATION

    Directory of Open Access Journals (Sweden)

    Pavel Kovačócy

    2011-10-01

    Full Text Available The article presents samples of weld joint of AISI 310 austenitic steel which were subjected to solution annealing at various temperature - time exposures. The objective of the experiment was to determine the annealing temperature so that the steel should not be sensitized. Tendency to intercrystalline corrosion was analysed by means of a corrosion test in 10 % oxalic acid according to ASTM A 262. At the temperatures of 1000 and 1100°C held for 15 min. the steel was not sensitized. At the temperature of 850°C the steel was sensitized, i.e. susceptible to intercrystalline corrosion.

  1. THE EFFECT OF THE ANNEALING TEMPERATURE ON THE CORROSION RESISTANCE OF WELD JOINT OF AISI 310 STEEL - SHORT COMMUNICATION

    Directory of Open Access Journals (Sweden)

    Martina Nerádová

    2012-02-01

    Full Text Available The article presents samples of weld joint of AISI 310 austenitic steel which were subjected to solution annealing at various temperature - time exposures. The objective of the experiment was to determine the annealing temperature so that the steel should not be sensitized. Tendency to intercrystalline corrosion was analysed by means of a corrosion test in 10 % oxalic acid according to ASTM A 262. At the temperatures of 1000 and 1100°C held for 15 min. the steel was not sensitized. At the temperature of 850°C the steel was sensitized, i.e. susceptible to intercrystalline corrosion.

  2. The Passive Film Growth Mechanism of New Corrosion-Resistant Steel Rebar in Simulated Concrete Pore Solution: Nanometer Structure and Electrochemical Study

    Science.gov (United States)

    Jiang, Jin-yang; Wang, Danqian; Chu, Hong-yan; Ma, Han; Liu, Yao; Gao, Yun; Shi, Jinjie; Sun, Wei

    2017-01-01

    An elaborative study was carried out on the growth mechanism and properties of the passive film for a new kind of alloyed corrosion-resistant steel (CR steel). The passive film naturally formed in simulated concrete pore solutions (pH = 13.3). The corrosion resistance was evaluated by various methods including open circuit potential (OCP), linear polarization resistance (LPR) measurements, and electrochemical impedance spectroscopy (EIS). Meanwhile, the 2205 duplex stainless steel (SS steel) was evaluated for comparison. Moreover, the passive film with CR steel was studied by means of X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), Atomic Force Microscope (AFM), and the Mott‑Schottky approach. The results showed that the excellent passivity of CR steel could be detected in a high alkaline environment. The grain boundaries between the fine passive film particles lead to increasing Cr oxide content in the later passivation stage. The filling of cation vacancies in the later passivation stage as well as the orderly crystalized inner layer contributed to the excellent corrosion resistance of CR steel. A passive film growth model for CR steel was proposed. PMID:28772772

  3. Pitting corrosion resistance and bond strength of stainless steel overlay by friction surfacing on high strength low alloy steel

    Directory of Open Access Journals (Sweden)

    Amit Kumar Singh

    2015-09-01

    Full Text Available Surface modification is essential for improving the service properties of components. Cladding is one of the most widely employed methods of surface modification. Friction surfacing is a candidate process for depositing the corrosion resistant coatings. Being a solid state process, it offers several advantages over conventional fusion based surfacing process. The aim of this work is to identify the relationship between the input variables and the process response and develop the predictive models that can be used in the design of new friction surfacing applications. In the current work, austenitic stainless steel AISI 304 was friction surfaced on high strength low alloy steel substrate. Friction surfacing parameters, such as mechtrode rotational speed, feed rate of substrate and axial force on mechtrode, play a major role in determining the pitting corrosion resistance and bond strength of friction surfaced coatings. Friction surfaced coating and base metal were tested for pitting corrosion by potentio-dynamic polarization technique. Coating microstructure was characterized using optical microscopy, scanning electron microscopy and X-ray diffraction. Coatings in the as deposited condition exhibited strain-induced martensite in austenitic matrix. Pitting resistance of surfaced coatings was found to be much lower than that of mechtrode material and superior to that of substrate. A central composite design with three factors (mechtrode rotational speed, substrate traverse speed, axial load on mechtrode and five levels was chosen to minimize the number of experimental conditions. Response surface methodology was used to develop the model. In the present work, an attempt has been made to develop a mathematical model to predict the pitting corrosion resistance and bond strength by incorporating the friction surfacing process parameters.

  4. Inhibition of Staphylococcus aureus biofilm by a copper-bearing 317L-Cu stainless steel and its corrosion resistance.

    Science.gov (United States)

    Sun, Da; Xu, Dake; Yang, Chunguang; Chen, Jia; Shahzad, M Babar; Sun, Ziqing; Zhao, Jinlong; Gu, Tingyue; Yang, Ke; Wang, Guixue

    2016-12-01

    The present study investigated the antibacterial performance, corrosion resistance and surface properties of antibacterial austenitic 317L-Cu stainless steel (317L-Cu SS). After 4.5wt% copper was added to 317L stainless steel (317L SS), the new alloy underwent solid solution and aging heat treatment. Fluorescent staining using 4',6-diamidino-2-phenylindole (DAPI) revealed that the 317L-Cu SS showed strong antibacterial efficacy, achieving a 99% inhibition rate of sessile Staphylococcus aureus cells after 5days. The corrosion data obtained by potentiodynamic polarization curves indicated that in comparison with 317L SS, the pitting potential and corrosion current density of 317L-Cu slightly decreased due to the addition of Cu. The 317L-Cu SS exhibited no cytotoxicity against zebrafish (Danio rerio) embryos. The experimental results in this study demonstrated that the new alloy has potential applications in medical and daily uses. Copyright © 2016 Elsevier B.V. All rights reserved.

  5. Effect of thermal ageing on the corrosion resistance of stainless steel type 316L exposed in supercritical water

    Energy Technology Data Exchange (ETDEWEB)

    Jiao, Y.; Kish, J., E-mail: jiaoyn@mcmaster.ca, E-mail: kishjr@mcmaster.ca [McMaster University, Hamilton, ON (Canada); Zheng, W., E-mail: wenyue.zheng@nrcan.rncan.gc.ca [Canmet Materials, Hamilton, ON (Canada); Guzonas, D. [Atomic Energy of Canada Limited, Chalk River, ON (Canada); Cook, W., E-mail: wcook@unb.ca [University of New Brunswick, Fredericton, NB (Canada)

    2014-07-01

    The tendency for intermetallic precipitates to form in austenitic stainless steel during prolonged exposure at the expected operating temperature of the fuel cladding in the Canadian supercritical water reactor (SCWR) concept represents a possible serious threat to the intrinsic in-service corrosion performance of the candidate alloy. The objective of this study was to better understand the extent to which a thermally-aged microstructure affects the mode and extent of corrosion exhibited by Type 316L stainless steel exposed in 25 MPa supercritical water (SCW) at 550 {sup o}C for 500 h. Mechanically-abraded samples were exposed in an as-received and thermally-aged condition. Thermal ageing conducted at 815 {sup o}C (peak fuel cladding temperature expected) for 1000 h was found to produce a discontinuous network of the carbide (M{sub 23}C{sub 6}), chi (χ), laves (η) and sigma (σ) phases. The similar weight gain and oxide scale structure, composition and thickness suggested that the thermally-aged condition does not have a marked influence on the corrosion resistance. (author)

  6. Some peculiarities of corrosion of wheel steel

    Directory of Open Access Journals (Sweden)

    Alexander SHRAMKO

    2009-01-01

    Full Text Available Corrosion mechanism and rate of different chemical composition and structural condition of wheel steel were investigated. It was shown that “white layers”, variation in grain size and banding of wheel steel structure results in corrosion rate. Microstructure of steel from different elements of railway wheels after operation with corrosion was investigated. Wheel steel with addition of vanadium corroded more quickly than steel without vanadium. Non-metallic inclusions are the centre of corrosion nucleation and their influence on corrosion depends on type of inclusion. Mechanism of corrosion of wheel steel corrosion was discussed.

  7. Influence of pre-deformation, sensitization and oxidation in high temperature water on corrosion resistance of AISI 304 stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Lv, Jinlong, E-mail: ljltsinghua@126.com [Beijing Key Laboratory of Fine Ceramics, Institute of Nuclear and New Energy Technology, Tsinghua University, Zhongguancun Street, Haidian District, Beijing 100084 (China); State Key Lab of New Ceramic and Fine Processing, Tsinghua University, Beijing 100084 (China); Liang, Tongxiang [Beijing Key Laboratory of Fine Ceramics, Institute of Nuclear and New Energy Technology, Tsinghua University, Zhongguancun Street, Haidian District, Beijing 100084 (China); State Key Lab of New Ceramic and Fine Processing, Tsinghua University, Beijing 100084 (China); Luo, Hongyun [Key Laboratory of Aerospace Materials and Performance (Ministry of Education), School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Xueyuan Road 37, Beijing 100191 (China)

    2016-12-01

    Highlights: • The pre-strain accelerated desensitization and sensitization for austenitic stainless steels. • Low temperature sensitization (carbide precipitation) induced α′-martensite. • The sensitization level could affect directly corrosion resistance of the oxide film. - Abstract: The effects of pre-deformation on sensitization of AISI 304 stainless steel were investigated by the double loop electrochemical potentiokinetic reactivation test. The effects of pre-deformation and sensitization on high temperature oxidized film formed in high temperature water were analyzed by a XRD and SEM. The electrochemical impedance spectroscopy at room temperature was used to study corrosion resistance of oxidized film. The point defect density of oxidized film was calculated by Mott–Schottky plots. The results showed that the value of the degree of sensitization first decreased and then slight increased with the increasing of engineering strain. Moreover, low temperature promoted to form sensitization induced “secondary” α′-martensite. The sample with 20% engineering strain had higher impedance value than other samples. The result was supported by further Mott–Schottky experiments. Considering increased α′-martensite with the increasing of strain, the results of the impedance were more consistent with values of the degree of sensitization.

  8. Improvement in nano-hardness and corrosion resistance of low carbon steel by plasma nitriding with negative DC bias voltage

    Science.gov (United States)

    Alim, Mohamed Mounes; Saoula, Nadia; Tadjine, Rabah; Hadj-Larbi, Fayçal; Keffous, Aissa; Kechouane, Mohamed

    2016-10-01

    In this work, we study the effect of plasma nitriding on nano-hardness and corrosion resistance of low carbon steel samples. The plasma was generated through a radio-frequency inductively coupled plasma source. The substrate temperature increased (by the self-induced heating mechanism) with the treatment time for increasing negative bias voltages. X-rays diffraction analysis revealed the formation of nitride phases (ɛ-Fe2-3N and γ'-Fe4N) in the compound layer of the treated samples. A phase transition occurred from 3.5 kV to 4.0 kV and was accompanied by an increase in the volume fraction of the γ'-Fe4N phase and a decrease in that of the ɛ-Fe2-3N phase. Auger electron spectroscopy revealed a deep diffusion of the implanted nitrogen beyond 320 nm. The nano-hardness increased by ~400% for the nitrogen-implanted samples compared to the untreated state, the nitride phases are believed to participate to the hardening. Potentiodynamic polarization measurements revealed that the plasma nitriding has improved the corrosion resistance behavior of the material. When compared to the untreated state, the sample processed at 4.0 kV exhibits a shift of +500 mV and a reduction to 3% in its corrosion current. These results were obtained for relatively low bias voltages and short treatment time (2 h).

  9. Energy Saving Melting and Revert Reduction (E-SMARRT): Optimization of Heat Treatments on Stainless Steel Castings for Improved Corrosion Resistance and Mechanical Properties

    Energy Technology Data Exchange (ETDEWEB)

    John N. DuPont; Jeffrey D. Farren; Andrew W. Stockdale; Brett M. Leister

    2012-06-30

    It is commonly believed that high alloy steel castings have inferior corrosion resistance to their wrought counterparts as a result of the increased amount of microsegregation remaining in the as-cast structure. Homogenization and dissolution heat treatments are often utilized to reduce or eliminate the residual microsegregation and dissolve the secondary phases. Detailed electron probe microanalysis (EPMA) and light optical microscopy (LOM) were utilized to correlate the amount of homogenization and dissolution present after various thermal treatments with calculated values and with the resultant corrosion resistance of the alloys.The influence of heat treatment time and temperature on the homogenization and dissolution kinetics were investigated using stainless steel alloys CN3MN and CK3MCuN. The influence of heat treatment time and temperature on the impact toughness and corrosion reistance of cast stainless steel alloys CF-3, CF-3M, CF-8, and CF-8M was also investigated.

  10. Evaluation of the corrosion resistance of AISI 316 stainless steel filters

    Directory of Open Access Journals (Sweden)

    Luzinete Pereira Barbosa

    2005-06-01

    Full Text Available In this investigation, the corrosion resistance of AISI 316 SS filters prepared with powders in the size ranges 74-44 µm and 210-105 µm and compacted with pressures of 300 MPa and 400 MPa has been evaluated in naturally aerated 0.5 M H2SO4 solution at 25 °C. Weight loss of filters manufactured with compacting pressure of 400 MPa were significantly higher than that of filters compacted at 300 MPa. The filter compacted at 400 MPa had higher carbon and nitrogen contents compared to those compacted at 300 MPa. The former also had chromium rich precipitates and oxides in the grain boundaries. The pores in filters compacted at 400 MPa were smaller than in filters compacted at 300 MPa. Smaller pores favor the formation of concentration cells and consequently, increased crevice corrosion.

  11. Enhanced Corrosion Resistance of Carbon Steel in Hydrochloric Acid Solution by Eriobotrya Japonica Thunb. Leaf Extract: Electrochemical Study.

    Science.gov (United States)

    Yang, Wenjing; Wang, Qihui; Xu, Ke; Yin, Yanjun; Bao, Hebin; Li, Xueming; Niu, Lidan; Chen, Shiqi

    2017-08-16

    The biodegradable inhibitors, which could effectively reduce the rate of corrosion of carbon steel, were investigated by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The mixed-type inhibitors extracted from Eriobotrya japonica Thunb. leaf exhibited excellent inhibition performance, and the inhibition efficiency for carbon steel reached 90.0% at 298 K in hydrochloric acid. Moreover, the adsorption mechanism of the inhibitors on a carbon steel surface is described by the Langmuir adsorption isotherm. Simultaneously, the corrosion morphology of the carbon steel and the inhibitor structure were analyzed by scanning electron microscope (SEM) and Fourier transform infrared spectroscopy (FT-IR), respectively.

  12. Microbial-Influenced Corrosion of Corten Steel Compared with Carbon Steel and Stainless Steel in Oily Wastewater by Pseudomonas aeruginosa

    Science.gov (United States)

    Mansouri, Hamidreza; Alavi, Seyed Abolhasan; Fotovat, Meysam

    2015-07-01

    The microbial corrosion behavior of three important steels (carbon steel, stainless steel, and Corten steel) was investigated in semi petroleum medium. This work was done in modified nutrient broth (2 g nutrient broth in 1 L oily wastewater) in the presence of Pseudomonas aeruginosa and mixed culture (as a biotic media) and an abiotic medium for 2 weeks. The behavior of corrosion was analyzed by spectrophotometric and electrochemical methods and at the end was confirmed by scanning electron microscopy. The results show that the degree of corrosion of Corten steel in mixed culture, unlike carbon steel and stainless steel, is less than P. aeruginosa inoculated medium because some bacteria affect Corten steel less than other steels. According to the experiments, carbon steel had less resistance than Corten steel and stainless steel. Furthermore, biofilm inhibits separated particles of those steels to spread to the medium; in other words, particles get trapped between biofilm and steel.

  13. Assessment of Stress Corrosion Cracking Resistance of Activated Tungsten Inert Gas-Welded Duplex Stainless Steel Joints

    Science.gov (United States)

    Alwin, B.; Lakshminarayanan, A. K.; Vasudevan, M.; Vasantharaja, P.

    2017-11-01

    The stress corrosion cracking behavior of duplex stainless steel (DSS) weld joint largely depends on the ferrite-austenite phase microstructure balance. This phase balance is decided by the welding process used, heat input, welding conditions and the weld metal chemistry. In this investigation, the influence of activated tungsten inert gas (ATIG) and tungsten inert gas (TIG) welding processes on the stress corrosion cracking (SCC) resistance of DSS joints was evaluated and compared. Boiling magnesium chloride (45 wt.%) environment maintained at 155 °C was used. The microstructure and ferrite content of different weld zones are correlated with the outcome of sustained load, SCC test. Irrespective of the welding processes used, SCC resistance of weld joints was inferior to that of the base metal. However, ATIG weld joint exhibited superior resistance to SCC than the TIG weld joint. The crack initiation and final failure were in the weld metal for the ATIG weld joint; they were in the heat-affected zone for the TIG weld joint.

  14. Assessment of Stress Corrosion Cracking Resistance of Activated Tungsten Inert Gas-Welded Duplex Stainless Steel Joints

    Science.gov (United States)

    Alwin, B.; Lakshminarayanan, A. K.; Vasudevan, M.; Vasantharaja, P.

    2017-12-01

    The stress corrosion cracking behavior of duplex stainless steel (DSS) weld joint largely depends on the ferrite-austenite phase microstructure balance. This phase balance is decided by the welding process used, heat input, welding conditions and the weld metal chemistry. In this investigation, the influence of activated tungsten inert gas (ATIG) and tungsten inert gas (TIG) welding processes on the stress corrosion cracking (SCC) resistance of DSS joints was evaluated and compared. Boiling magnesium chloride (45 wt.%) environment maintained at 155 °C was used. The microstructure and ferrite content of different weld zones are correlated with the outcome of sustained load, SCC test. Irrespective of the welding processes used, SCC resistance of weld joints was inferior to that of the base metal. However, ATIG weld joint exhibited superior resistance to SCC than the TIG weld joint. The crack initiation and final failure were in the weld metal for the ATIG weld joint; they were in the heat-affected zone for the TIG weld joint.

  15. Corrosion Resistance and Mechanical Properties of TIG and A-TIG Welded Joints of Lean Duplex Stainless Steel S82441 / 1.4662

    Directory of Open Access Journals (Sweden)

    Brytan Z.

    2016-06-01

    Full Text Available This paper presents results of pitting corrosion resistance of TIG (autogenous and with filler metal and A-TIG welded lean duplex stainless steel S82441/1.4662 evaluated according to ASTM G48 method, where autogenous TIG welding process was applied using different amounts of heat input and shielding gases like pure Ar and Ar+N2 and Ar+He mixtures. The results of pitting corrosion resistance of the welded joints of lean duplex stainless steel S82441 were studied in as weld conditions and after different mechanical surface finish treatments. The results of the critical pitting temperature (CPT determined according to ASTM G48 at temperatures of 15, 25 and 35°C were presented. Three different surface treatment after welding were applied: etching, milling, brushing + etching. The influence of post weld surface treatment was studied in respect to the pitting corrosion resistance, basing on CPT temperature.

  16. Strengthening mechanisms and mechanical properties of high interstitial stainless steel for drill collar and its corrosion resistance

    Science.gov (United States)

    Lee, Eunkyung

    Two types (CN66, CN71) of high interstitial stainless steels (HISSs) were investigated for down-hole application in sour gas well environments. Experiments were designed to identify factors that have a significant effect on mechanical properties. The three factors examined in the study were carbon + nitrogen content (0.66 or 0.71 mass %), cooling rate in quenching (air or water), and heat treatment time (2 or 4 hours). The results showed that the cooling rate, C+N content, and the two-factor interaction of these variables have a significant effect on the mechanical properties of HISSs. Based on the statistical analysis results on mechanical properties, extensive analyses were undertaken to understand the strengthening mechanisms of HISSs. Microstructure analysis revealed that a pearlite phase with a high carbide and/or nitride content is dissolved in the matrix by heat treatment at 1,200 ºC which is considered the dissolution to increase the concentration of interstitial elements in steels. The distribution of elements in HISSs was investigated by quantitative mapping using EPMA, which showed that the high carbon concentration (carbide/cementite) area was decreased by increases in both the cooling rate and C+N content. The ferrite volume fraction of each specimen is increased by an increase in cooling rate, because there is insufficient time to form austenite from retained ferrite. The lattice expansion of HISS was investigated by the calculation of lattice parameters under various conditions, and these investigations confirm the solid solution strengthening effect on HISSs. CN66 with heat treatment at fast cooling has the highest wear resistance; a finding that was consistent with hardening mechanisms that occur due to an increased ferrite volume fraction. In addition, precipitates on the surface and the chemical bonding of chromium were investigated. As the amount of CrN bonding increased, the wear resistance also increased. This study also assessed the

  17. Effects of X-rays Radiation on AISI 304 Stainless Steel Weldings with AISI 316L Filler Material: A Study of Resistance and Pitting Corrosion Behavior

    Directory of Open Access Journals (Sweden)

    Francisco Javier Cárcel-Carrasco

    2016-04-01

    Full Text Available This article investigates the effect of low-level ionizing radiation, namely X-rays, on the micro structural characteristics, resistance, and corrosion resistance of TIG-welded joints of AISI 304 austenitic stainless steel made using AISI 316L filler rods. The welds were made in two different environments: natural atmospheric conditions and a closed chamber filled with inert argon gas. The influence of different doses of radiation on the resistance and corrosion characteristics of the welds is analyzed. Welded material from inert Ar gas chamber TIG showed better characteristics and lesser irradiation damage effects.

  18. PITTING CORROSION OF TYPE 430 STAINLESS STEEL UNDER CHLORIDE SOLUTION FILMS

    OpenAIRE

    Tran Van, Nam; Tran Van, Nam

    2015-01-01

    In recent years, ferritic stainless steel is promoting to use than other stainless steels such as austenitic, duplex stainless steels owning to affordable cost. Unfortunately, this material has moderate corrosion resistance. Therefore, both understanding corrosion process and improving corrosion resistance of this material will be important issues. In this study, the corrosion behavior of type 430 stainless steel under solution layers containing chloride is investigated. Effects of the thin-f...

  19. Corrosion Resistance, EIS and Wettability of the Implants Made of 316 LVM Steel Used in Chest Deformation Treatment

    Directory of Open Access Journals (Sweden)

    Kajzer A.

    2016-06-01

    Full Text Available The paper presents the influence of mechanical surface damage on the physicochemical properties of plates after implantation made of CrNiMo stainless steel, used in the treatment of anterior surface deformity of the chest. Analysis of the data allowed us to investigate the effect of implant design and condition of their surface on the results of chest deformation treatment. Results of electrochemical, impedance and surface wettability tests and SEM observations were compared with clinical observations. When removing the plates we found only slight inflammatory-periosteal reactions. On the basis of obtained results, it can be stated that plates, in spite of mechanical damage of the surface, were characterized by good corrosion resistance, a fact which is confirmed by the results of clinical evaluation.

  20. Effect of liquid phase sintering on the mechanical properties and corrosion resistance of infiltrated austenitic stainless steel; Efeito da sinterizacao com fase liquida sobre as propriedades mecanicas e resistencia a corrosao do aco inoxidavel austenitico infiltrado

    Energy Technology Data Exchange (ETDEWEB)

    Machado, Cristine F. [Rio Grande do Sul Univ., Porto Alegre, RS (Brazil). Programa de Pos-graduacao em Engenharia Metalurgica e dos Materiais; Matos Dias, Arao de; Schaeffer, Lirio [Rio Grande do Sul Univ., Porto Alegre, RS (Brazil). Centro de Tecnologia. Lab. de Metalurgia do Po

    1996-12-31

    First, this work presents some considerations on the properties and corrosion resistance of the stainless steels and its relation with porosity. The infiltration technique of copper into compacted steels is presented as an efficacy alternative to improve both mechanical properties and corrosion resistance. In experimental development, it was carried out mechanical tests with stainless steel AISI 316 L to ratify the copper infiltration effects on the yield stress of the material, and corrosion tests in salt spray. The results confirm a considerable improvement in properties on the whole to infiltrated stainless steel. (author) 18 refs., 8 figs., 4 tabs.

  1. Some peculiarities of corrosion of wheel steel

    OpenAIRE

    Alexander SHRAMKO; Alfred KOZLOWSKY; Elena BELAJA; Yuriy PROIDAK; Sofia PINCHUK; Svetlana GUBENKO

    2009-01-01

    Corrosion mechanism and rate of different chemical composition and structural condition of wheel steel were investigated. It was shown that “white layers”, variation in grain size and banding of wheel steel structure results in corrosion rate. Microstructure of steel from different elements of railway wheels after operation with corrosion was investigated. Wheel steel with addition of vanadium corroded more quickly than steel without vanadium. Non-metallic inclusions are the centre of corrosi...

  2. Atmospheric corrosion of mild steel

    Directory of Open Access Journals (Sweden)

    Morcillo, M.

    2011-10-01

    Full Text Available The atmospheric corrosion of mild steel is an extensive topic that has been studied by many authors in different regions throughout the world. This compilation paper incorporates relevant publications on the subject, in particular about the nature of atmospheric corrosion products, mechanisms of atmospheric corrosion and kinetics of the atmospheric corrosion process, paying special attention to two matters upon which relatively less information has been published: a the morphology of steel corrosion products and corrosion product layers; and b long-term atmospheric corrosion ( > 10 years.

    La corrosión atmosférica del acero suave es un tema de gran amplitud que ha sido tratado por muchos autores en numerosas regiones del mundo. Este artículo de compilación incorpora publicaciones relevantes sobre esta temática, en particular sobre la naturaleza de los productos de corrosión atmosférica, mecanismos y cinética de los procesos de corrosión atmosférica, prestando una atención especial a dos aspectos sobre los que la información publicada ha sido menos abundante: a morfología de los productos de corrosión del acero y capas de productos de corrosión, y b corrosión atmosférica a larga duración (> 10 años.

  3. Influence of nitrogen on the stress corrosion cracking resistance of austenitic stainless steels in chloride environment; Influence de l'azote sur la resistance a la corrosion sous contrainte d'aciers inoxydables austenitiques en milieu chlorure

    Energy Technology Data Exchange (ETDEWEB)

    Teysseyre, S

    2001-11-01

    The aim of this study is to investigate the influence of nitrogen additions on the Stress Corrosion Cracking (SSC) resistance of austenitic stainless steel in chloride environment. The investigation was carried out in two part: first, an experimental investigation with model industrial steels was carried out and secondly, numerical simulations based on the Corrosion Enhanced Plasticity Model were developed. Both slow strain rate tensile tests and constant load test of the different steels in boiling MgCl{sub 2} (153 deg C) at free potential show that, for a given plastic strain rate, nitrogen addition increases the critical stress for crack initiation without influencing the crack propagation rate. We observed that the creep rate under constant load was affected by the nitrogen content. As a consequence, the SCC behaviour (cracks density and propagation rate) depends on the nitrogen content. We thus confirm that the nitrogen content influences the corrosion - deformation interaction mechanisms via its positive contribution to the flow stress. These experimental results are reproduced semi-quantitatively by means of numerical simulations at the scale of crack. - dislocation interactions. The presence of nitrogen is modelled by an increased lattice friction stress, which in turn affects the dynamics of crack tip shielding by dislocation pile-ups. We conclude that nitrogen addition in austenitic stainless steels increases the SC crack initiation stress in proportion of the increased flow stress, without penalty in terms of SC crack propagation rate. (author)

  4. Corrosion resistance of stainless steel, nickel-titanium, titanium molybdenum alloy, and ion-implanted titanium molybdenum alloy archwires in acidic fluoride-containing artificial saliva: Anin vitrostudy.

    Science.gov (United States)

    Pulikkottil, Venith Jojee; Chidambaram, S; Bejoy, P U; Femin, P K; Paul, Parson; Rishad, Mohamed

    2016-10-01

    (1) To evaluate the corrosion resistance of four different orthodontic archwires and to determine the effect of 0.5% NaF (simulating high fluoride-containing toothpaste of about 2250 ppm) on corrosion resistance of these archwires. (2) To assess whether surface roughness (Ra) is the primary factor influencing the corrosion resistance of these archwires. Four different archwires (stainless steel [SS], nickel-titanium [NiTi], titanium molybdenum alloy [TMA], and ion-implanted TMA) were considered for this study. Surface characteristics were analyzed using scanning electron microscopy, atomic force microscopy (AFM), and energy dispersive spectroscopy. Linear polarization test, a fast electrochemical technique, was used to evaluate the corrosion resistance, in terms of polarization resistance of four different archwires in artificial saliva with NaF concentrations of 0% and 0.5%. Statistical analysis was performed by one-way analysis of variance. The potentiostatic study reveals that the corrosion resistance of low-friction TMA (L-TMA) > TMA > NiTi > SS. AFM analysis showed the surface Ra of TMA > NiTi > L-TMA > SS. This indicates that the chemical composition of the wire is the primary influential factor to have high corrosion resistance and surface Ra is only secondary. The corrosion resistance of all wires had reduced significantly in 0.5% acidic fluoride-containing artificial saliva due to formation of fluoride complex compound. The presence of 0.5% NaF in artificial saliva was detrimental to the corrosion resistance of the orthodontic archwires. Therefore, complete removal of residual high-fluorinated toothpastes from the crevice between archwire and bracket during tooth brushing is mandatory.

  5. Etchants for Some Corrosion-Resistant Metals

    Science.gov (United States)

    Simmons, J.

    1984-01-01

    Solutions that etch some corrosion-resistant metals described in test report. Etchants selected remove at least 0.4 mil of surface material per hour from nickel alloys, austenitic stainless steel, and annealed titanium alloys, without intergranular attack.

  6. Effect of the Parameters of Gas-Powder Laser Surfacing on the Structural Characteristics of Reconditioned Surface Layer of Corrosion-Resistant Steels

    Science.gov (United States)

    Krylova, S. E.; Oplesnin, S. P.; Manakov, N. A.; Yasakov, A. S.; Strizhov, A. O.

    2018-01-01

    Results of the developed commercial process for reconditioning the surface of corrosion-resistant steels by the method of laser surfacing are presented. A comparative analysis of the microstructures of the deposited wear-resistant layer, of the zone of fusion with the matrix material and of the diffusion zone after different variants of surfacing is performed. The hardness of the deposited layer is measured and a nondestructive inspection of the latter for the presence of flaws is performed.

  7. Effect of copper addition on mechanical properties, corrosion resistance and antibacterial property of 316L stainless steel.

    Science.gov (United States)

    Xi, Tong; Shahzad, M Babar; Xu, Dake; Sun, Ziqing; Zhao, Jinlong; Yang, Chunguang; Qi, Min; Yang, Ke

    2017-02-01

    The effects of addition of different Cu content (0, 2.5 and 3.5wt%) on mechanical properties, corrosion resistance and antibacterial performance of 316L austenitic stainless steel (SS) after solution and aging treatment were investigated by mechanical test, transmission electron microscope (TEM), X-ray diffraction (XRD), electrochemical corrosion, X-ray photoelectron spectroscopy (XPS) and antibacterial test. The results showed that the Cu addition and heat treatment had no obvious influence on the microstructure with complete austenite features. The yield strength (YS) after solution treatment was almost similar, whereas the aging treatment obviously increased the YS due to formation of tiny Cu-rich precipitates. The pitting and protective potential of the solution treated Cu-bearing 316L SS in 0.9wt% NaCl solution increased with increasing Cu content, while gradually declined after aging, owing to the high density Cu-rich precipitation. The antibacterial test proved that higher Cu content and aging were two compulsory processes to exert good antibacterial performance. The XPS results further indicated that aging enhanced the Cu enrichment in passive film, which could effectively stimulate the Cu ions release from the surface of passive film. Copyright © 2016 Elsevier B.V. All rights reserved.

  8. A novel method to prepare superhydrophobic, UV resistance and anti-corrosion steel surface

    KAUST Repository

    Isimjan, Tayirjan T.

    2012-11-01

    Both TiO 2 and SiO 2 coated steel surfaces containing micro- and nanoscale binary structures with different surface roughness were successfully fabricated by means of a facile layer by layer deposition process followed by heat treatment. The resulting surfaces were modified by the low free energy chemical PTES (1H,1H,2H,2H-Perfluorodecyltriethoxysilane). The experimental results of wettability exhibit that such modified surfaces have a strong repulsive force to water droplets, their static contact angles exceed 165°, receding angle>160°, advanced angles>170° and slide angle<1°. The resulting surfaces not only exhibit superhydrophobic properties but also show strong UV resistance (after coating SiO 2 on top of TiO 2) and strong stability to various solvents including 0.01% HCl solution. © 2012 Elsevier B.V.

  9. An Industrial Perspective on Environmentally Assisted Cracking of Some Commercially Used Carbon Steels and Corrosion-Resistant Alloys

    Science.gov (United States)

    Ashida, Yugo; Daigo, Yuzo; Sugahara, Katsuo

    2017-08-01

    Commercial metals and alloys like carbon steels, stainless steels, and nickel-based super alloys frequently encounter the problem of environmentally assisted cracking (EAC) and resulting failure in engineering components. This article aims to provide a perspective on three critical industrial applications having EAC issues: (1) corrosion and cracking of carbon steels in automotive applications, (2) EAC of iron- and nickel-based alloys in salt production and processing, and (3) EAC of iron- and nickel-based alloys in supercritical water. The review focuses on current industrial-level understanding with respect to corrosion fatigue, hydrogen-assisted cracking, or stress corrosion cracking, as well as the dominant factors affecting crack initiation and propagation. Furthermore, some ongoing industrial studies and directions of future research are also discussed.

  10. Effect of Aging on Precipitation Behavior and Pitting Corrosion Resistance of SAF2906 Super Duplex Stainless Steel

    Science.gov (United States)

    Li, Jianchun; Li, Guoping; Liang, Wei; Han, Peide; Wang, Hongxia

    2017-09-01

    The effect of aging temperature and holding time on the precipitation of secondary phases and pitting corrosion resistance of SAF2906 super duplex stainless steel was examined. Chromium nitride and σ phase were observed to preferentially precipitate at the ferrite/austenite interface. An amount of nitrides was also observed within the ferrite grain. The precipitation of chromium nitride occurred before the σ phase. The increase in aging temperature and holding time did not affect the concentration of the nitrides but increased the area fraction of the σ phase at a faster rate. The Cr2N precipitation in SAF2906 is more evident than that of the other duplex stainless steels. The variation tendency of the precipitation concentrations is primarily consistent with the prediction results of Thermo-Calc software. The electrochemical results showed that Cr2N and σ phase significantly reduced the pitting potential. Scanning electron microscope observations revealed that pits appear mainly in regions adjacent to sigma phase and Cr2N.

  11. Field corrosion characterization of soil corrosion of X70 pipeline steel in a red clay soil

    Directory of Open Access Journals (Sweden)

    Shengrong Wang

    2015-06-01

    Full Text Available The corrosion behavior of X70 pipeline steel buried in red soil environment has been studied. The surface morphology and elemental distribution were determined by scanning electron microscopy (SEM,energy dispersive X-ray spectroscopy (EDS, and X-ray diffraction (XRD. The corrosion kinetics was evaluated by weight loss measurement. The results show that in red soil, the corrosion rate of X70 steel decreases with time, and follows the exponential decay law. General corrosion with non-uniform and localized pitting occurred on the steel surface. α-FeOOH was the dominate products during corrosion in whole buried periods, and the corrosion products exhibited well protective properties. The potentiodynamic polarization tests revealed that icorr decreased with time, indicating the improvement of corrosion resistance. The results of Electrochemical impendence spectroscopy (EIS are consistent with potentiodynamic polarization tests.

  12. Evaluation of steel corrosion by numerical analysis

    OpenAIRE

    Kawahigashi, Tatsuo

    2017-01-01

    Recently, various non-destructive and numerical methods have been used and many cases of steel corrosion are examined. For example, methods of evaluating corrosion through various numerical methods and evaluating macrocell corrosion and micro-cell corrosion using measurements have been proposed. However, there are few reports on estimating of corrosion loss with distinguishing the macro-cell and micro-cell corrosion and with resembling an actuality phenomenon. In this study, for distinguishin...

  13. Finishes for Metals. Paintability of Galvanized Steel, Corrosion Resistance of Metallized Coatings.

    Science.gov (United States)

    Building Research Inst., Inc., Washington, DC.

    Two papers are presented. The first, "Report of the AISI Research Project on the Paintability of Galvanized Steel," was a project aimed at determining optimum procedures for painting bright-spangled galvanized sheet steel products using three classes of trade sales paints--metallic zinc-dust, portland cement-in-oil, and water base emulsion paints.…

  14. Corrosion resistance of phosphatized steel: evaluation by electrochemical impedance spectroscopy; Resistencia a corrosao de aco fosfatizado: determinacao por espectroscopia de impedancia eletroquimica

    Energy Technology Data Exchange (ETDEWEB)

    Garita, Jose S. [Rio Grande do Sul Univ., Porto Alegre, RS (Brazil). Lab. de Corrosao e Protecao de Metais (LACOR); Fraga, Celia S. de; Ferreira, Jane Z.

    1996-12-31

    A zinc phosphate coating on steel consist in a crystal phosphate deposit with variable morphology and size. Crystalline deposits are obtained by a combination of electrochemical and chemical reactions between phosphoric acid and metal. The deposit thickness and crystal size are characteristics of the phosphatizing bath. Two usual phosphate applications are: increase anchor profile for a better adhesion of organic coatings and tribological applications in mechanical conformation, for example. In anticorrosion protection system base on phosphate, the phosphate coating has a function to be final resistant corrosion barrier and is associated with the restriction of the cathodic lost of adherence in the remainder protective system. The aim of this work is study the corrosion resistance properties of three different phosphate coatings on steel. These phosphate coatings are obtained with a change in the standard zinc phosphate bath. An alternative methodology at the conventional analysis technique, based on electrochemical impedance spectroscopy is suggested. The resistance polarization (Rp) obtained by EIS have a good agreement with the corrosion levels observed in the accelerated corrosion test (ASTM D2247). An adequate standardization for this technique can be the conventional test for characterization of phosphate coatings. (author) 6 refs., 5 figs., 2 tabs.

  15. Research and development of weathering resistant bridge steel of Shougang

    Science.gov (United States)

    Yang, Yongda; Wang, Yanfeng; Huang, Leqing; Di, Guobiao; Ma, Changwen; Ma, Qingshen

    2017-09-01

    To introduce the composition design and mechanical properties and microstructure of the weathering bridge steel which would be used for bridge of Guanting reservoir. We adopt cyclic immersion corrosion test to study corrosion resistance difference of weathering bridge steel and common bridge steel. At the same corrosion time, the weight loss and corrosion rate of weathering bridge steel are lower than the common bridge steel's. Testing phase composition of rust layer by X-ray diffraction, two kinds of test steel's rust layer is mainly composed of Goethite and Fe3O4 and Fe2O3. At the same corrosion time, the percentage composition of goethite in rust layer of weathering bridge steel are significantly higher than common bridge steel's, the higher goethite content is, the compacter rust layer structure is. The compact rust layer would prevent the water and air passing the rust layer, and then preventing the further corrosion reaction, improving the corrosion resistance performance of weathering bridge steel.

  16. Electrochemical evaluation for corrosion resistance of bacterial exopolysaccharides on low carbon steel

    Science.gov (United States)

    Corrosion is a global issue that affects safety and economics. There is an increasing demand for bio-based polymers for industrial applications and production of polymers by microorganisms is especially attractive. This work reports on the electrochemical and physical properties of 29 strains or fr...

  17. Standard test methods for pitting and crevice corrosion resistance of stainless steels and related alloys by use of ferric Chloride solution

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2003-01-01

    1.1 These test methods cover procedures for the determination of the resistance of stainless steels and related alloys to pitting and crevice corrosion (see Terminology G 15) when exposed to oxidizing chloride environments. Six procedures are described and identified as Methods A, B, C, D, E, and F. 1.1.1 Method A—Ferric chloride pitting test. 1.1.2 Method B—Ferric chloride crevice test. 1.1.3 Method C—Critical pitting temperature test for nickel-base and chromium-bearing alloys. 1.1.4 Method D—Critical crevice temperature test for nickel-base and chromium-bearing alloys. 1.1.5 Method E—Critical pitting temperature test for stainless steels. 1.1.6 Method F—Critical crevice temperature test for stainless steels. 1.2 Method A is designed to determine the relative pitting resistance of stainless steels and nickel-base, chromium-bearing alloys, whereas Method B can be used for determining both the pitting and crevice corrosion resistance of these alloys. Methods C, D, E and F allow for a rankin...

  18. The electroplated Pd-Co alloy film on 316 L stainless steel and the corrosion resistance in boiling acetic acid and formic acid mixture with stirring

    Science.gov (United States)

    Li, Sirui; Zuo, Yu; Tang, Yuming; Zhao, Xuhui

    2014-12-01

    Pd-Co alloy films were deposited on 316 L stainless steel by electroplating. Scanning electronic microscopy, X-ray photoelectron spectroscopy, X-ray diffraction, weight loss test and polarization test were used to determine the properties of the Pd-Co alloy films. The Pd-Co films show fine grain size, low porosity and obviously high micro-hardness. The Co content in the film can be controlled in a large range from 21.9 at.% to 57.42 at.%. Pd is rich on the Pd-Co film surface, which is benefit to increase the corrosion resistance. In boiling 90% acetic acid plus 10% formic acid mixture with 0.005 M Br- under stirring, the Pd-Co plated stainless steel samples exhibit evidently better corrosion resistance in contrast to Pd plated samples. The good corrosion resistance of the Pd-Co alloy film is explained by the better compactness, the lower porosity, and the obviously higher micro-hardness of the alloy films, which increases the resistance to erosion and retards the development of micro-pores in the film.

  19. CORROSION RATE OF STEELS DX51D AND S220GD IN DIFFERENT CORROSION ENVIRONMENT

    Directory of Open Access Journals (Sweden)

    Alina Crina CIUBOTARIU

    2016-06-01

    Full Text Available Corrosion in the marine environment is an important issue because the costs causes by marine corrosion increased year upon year. It is necessary a correctly approach to materials selection, protection and corrosion control to reduce this burden of wasted materials, wasted energy and wasted money. Many different types of corrosion attack can be observed to structures, ships and other equipment used in sea water service. Shipping containers are exposed to various corrosive mediums like as airborne salt, industrial pollutants, rain and saltwater. Transport damage during loading onto and unloading off trucks, train beds and ships breaches the paint coating which further contributes to corrosion. The result is shortened container life and high costs for container repair or replacement. The paper intends to evaluate, by gravimetric method, the corrosion rate and corrosion penetration rate of two types of carbon steel DX51D and S220GD. Carbon steel DX51D and hot-dip galvanized steel S220GD are used in marine and industrial applications for buildings cargo vessels, container ships and oil tankers. For testing it was used different corrosive environments: 5% NaOH solution; 5% HCL solution and 0.5M NaCl solution. The samples were immersed in 400mL of testing solution for exposure period of 28 days. Periodically at 3 days, 7 days, 14 days, 21 days and 28 days was measured de mass loss and evaluate the corrosion rate and corrosion stability coefficient. The steel DX51D was stable in 5% NaOH solution for 28 days, the values of corrosion stability coefficient was 7 after 3 days and 6 after 28 days of immersion in corrosive medium. In 5% HCL solution steels DX51D and S220GD was completely corroded in 21 days with a corrosion stability coefficient equal with 9 for 7 days and 8 for 21 days of immersion in corrosive solution. It was observed a good resistance for 3 days in 0.5M NaCl solution with a corrosion stability coefficient equal with 5, but after that

  20. Coating of Steel by Alkyd Resin Reinforced with Al2O3 Nanoparticles to Improve Corrosion Resistance

    Science.gov (United States)

    Kordzangeneh, Shirin; Naghibi, Sanaz; Esmaeili, Hamideh

    2018-01-01

    In this study, an alkyd/Al2O3 nanocomposite coating was prepared and applied on a stainless steel substrate. The Al2O3 nanoparticles (NPs) with different weight ratios (1, 2, and 3 wt.%) were added to the alkyd resin and coated on the substrate via dip-coating technique. Then, the dispersion of NPs in the coating film was investigated using scanning electron microscopy (SEM) and scanning probe microscopy (SPM). The coating thickness estimated by SEM was 20 μm. The corrosion behavior of the coating was examined through the Tafel polarization and salt spray tests. The results showed that the addition of Al2O3 NPs up to 2 wt.% will result in a dense and homogeneous coating which protects the substrate leading to lower corrosion current density from 9.2 × 10-6 to 1.65×10-9 A/cm2 compared with the uncoated stainless steel.

  1. Improvement of localised corrosion resistance of AISI 2205 Duplex Stainless Steel joints made by gas metal arc welding under electromagnetic interaction of low intensity

    Energy Technology Data Exchange (ETDEWEB)

    García-Rentería, M.A., E-mail: crazyfim@gmail.com [Instituto de Investigación en Metalurgia y Materiales, Universidad Michoacana de San Nicolás de Hidalgo, A.P. 888, CP 58000, Morelia, Michoacán (Mexico); López-Morelos, V.H., E-mail: vhlopez@umich.mx [Instituto de Investigación en Metalurgia y Materiales, Universidad Michoacana de San Nicolás de Hidalgo, A.P. 888, CP 58000, Morelia, Michoacán (Mexico); García-Hernández, R., E-mail: rgarcia@umich.mx [Instituto de Investigación en Metalurgia y Materiales, Universidad Michoacana de San Nicolás de Hidalgo, A.P. 888, CP 58000, Morelia, Michoacán (Mexico); Dzib-Pérez, L., E-mail: luirdzib@uacam.mx [Centre for Corrosion Research, Autonomous University of Campeche, Av. Agustín Melgar s/n, Col. Buenavista, CP 24039, Campeche, Cam (Mexico); García-Ochoa, E.M., E-mail: emgarcia@uacam.mx [Centre for Corrosion Research, Autonomous University of Campeche, Av. Agustín Melgar s/n, Col. Buenavista, CP 24039, Campeche, Cam (Mexico); González-Sánchez, J., E-mail: jagonzal@uacam.mx [Centre for Corrosion Research, Autonomous University of Campeche, Av. Agustín Melgar s/n, Col. Buenavista, CP 24039, Campeche, Cam (Mexico)

    2014-12-01

    Highlights: • Electromagnetic interaction in welding improved localised corrosion resistance. • Electromagnetic interaction in welding enhanced γ/δ phase balance of DuplexSS. • Welding under Electromagnetic interaction repress formation and growth of detrimental phases. • Welds made with gas protection (2% O{sub 2} + 98% Ar) have better microstructural evolution during welding. - Abstract: The resistance to localised corrosion of AISI 2205 duplex stainless steel plates joined by Gas Metal Arc Welding (GMAW) under the effect of electromagnetic interaction of low intensity (EMILI) was evaluated with sensitive electrochemical methods. Welds were made using two shielding gas mixtures: 98% Ar + 2% O{sub 2} (M1) and 97% Ar + 3% N{sub 2} (M2). Plates were welded under EMILI using the M1 gas with constant welding parameters. The modified microstructural evolution in the high temperature heat affected zone and at the fusion zone induced by application of EMILI during welding is associated with the increase of resistance to localised corrosion of the welded joints. Joints made by GMAW using the shielding gas M2 without the application of magnetic field presented high resistance to general corrosion but high susceptibility to undergo localised attack.

  2. Synergy between molybdenum and nitrogen on the pitting corrosion and passive film resistance of austenitic stainless steels as a pH-dependent effect

    Energy Technology Data Exchange (ETDEWEB)

    Loable, Carole, E-mail: carole.loable@lepmi.grenoble-inp.fr [Univ. Grenoble Alpes, LEPMI, F-38000 Grenoble (France); CNRS, LEPMI, F-38000 Grenoble (France); Dep. Eng. Quimica, Instituto Superior Técnico-Universidade de Lisboa, Av. Rovisco Pais, 1049 001 Lisbon (Portugal); Viçosa, Isadora N., E-mail: inogueira@poli.ufrj.br [Univ. Grenoble Alpes, LEPMI, F-38000 Grenoble (France); CNRS, LEPMI, F-38000 Grenoble (France); Mesquita, Thiago J., E-mail: Thiago.mesquita@total.com [CRU Ugitech, Avenue Paul Girod, 73403 Ugine Cedex (France); Mantel, Marc, E-mail: Marc.Mantel@ugitech.com [CRU Ugitech, Avenue Paul Girod, 73403 Ugine Cedex (France); Université Grenoble Alpes, SIMAP, F-38000 Grenoble (France); CNRS, SIMAP, F-38000 Grenoble (France); Nogueira, Ricardo P., E-mail: rnogueira@pi.ac.ae [Univ. Grenoble Alpes, LEPMI, F-38000 Grenoble (France); CNRS, LEPMI, F-38000 Grenoble (France); Department of Chemical Engineering, The Petroleum Institute, P.O. Box 2533, Abu Dhabi (United Arab Emirates); Berthomé, Gregory, E-mail: gregory.berthome@simap.grenoble-inp.fr [Université Grenoble Alpes, SIMAP, F-38000 Grenoble (France); CNRS, SIMAP, F-38000 Grenoble (France); Chauveau, Eric, E-mail: eric.chauveau@ugitech.fr [Department of Chemical Engineering, The Petroleum Institute, P.O. Box 2533, Abu Dhabi (United Arab Emirates); Roche, Virginie, E-mail: virginie.roche@lepmi.grenoble-inp.fr [Univ. Grenoble Alpes, LEPMI, F-38000 Grenoble (France); CNRS, LEPMI, F-38000 Grenoble (France)

    2017-01-15

    This paper brings up some insights upon the pH dependence of the synergistic effect of Mo and N on the localized corrosion resistance of austenitic stainless steels. The objective of this work is to study the synergetic effect of Mo and N additions on corrosion and passive film properties of austenitic grades. A comparison between Mo containing (3 wt% Mo); Mo and N containing (3 wt% Mo and 0.1% N) and free Mo or free Mo and N grades of highly controlled laboratory heats was done considering their localized corrosion resistance and oxide film formation in different aggressive conditions, from neutral to alkaline pH. The passive layer was characterized by EIS and XPS analyses. The combined effect of Mo and N on the pitting potential was confirmed to be synergistic, and not just the addition of their individual effects. Moreover, this effect was found to be pH-dependent, being very positive in acid to neutral conditions whereas it was almost inexistent in high pH. - Highlights: • Laboratory austenitic stainless steels with Mo and/or N were tested. • Mo and N acted synergistically to improve pitting resistance. • Synergistic effect is pH-dependent. • N clearly enhanced the repassivation of austenitic SS in presence of Mo.

  3. Evaluation and control of environmental corrosion for aluminum and steel alloys

    Science.gov (United States)

    Franklin, D. B.

    1977-01-01

    Corrosion protection systems for aerospace application and the effects of surface treatments and methods of controlling stress corrosion are evaluated. Chromate pigmented systems were found to be most effective for aluminum alloys; zinc-rich coatings gave the greatest protection to steel alloys. Various steel and aluminum alloys are rated for stress corrosion resistance.

  4. PITTING CORROSION OF STAINLESS STEEL AT THE VARIOUS SURFACE TREATMENT

    Directory of Open Access Journals (Sweden)

    Viera Zatkalíková

    2011-09-01

    Full Text Available The stainless steel surface treatment is very important with regard to its pitting corrosion susceptibility. An effect of various types surfacing on pitting corrosion resistance of AISI 304stainless steel is investigated in this work. The samples of the tested material are turned, blasted, peened, grinded and a half of them are pickled to achieve higher purity of surfaces and better quality of passive film. Eight types of different finished surfaces are tested by electrochemical and immersion tests to determine corrosion behaviour in conditions where pitting is evoked by controlled potential and second by solution with high redox potential. By this way the effect of mechanical and chemical surface treatment on the resistance to pitting corrosion, character, size and shape of pits are compared in the conditions of different mechanisms of corrosion process.

  5. Determination of Grain Size and Resistance to Corrosion of Stainless Steel Welded Pipes

    Directory of Open Access Journals (Sweden)

    Pavel Hudeček

    2017-01-01

    Full Text Available Discover problems of welds is not so easy from time to time. Specially, If welding was made in rough environmental conditions such as high temperature, humidity and dusty wind. It is necessary to provide good conditions to realize basic step of welding. For welding, have been used welding procedures specification and procedure qualification record. However, difficult conditions, documentations rightness or human errors are always here. Common weld defects like cracks, porosity, lack of penetration and distortion can compromise the strength of the base metal, as well as the integrity of the weld. According of site inspection, there were suspicion of intercrystalline corrosion, inclusions, leaker or segregation in root of weld, root weld stretches to the pipe inside, the welded pipes are not in axially level, the not proper surface treatment after welding and keep the intervals between single welds to not overheat the pipes.

  6. MICROSTRUCTURE AND CORROSION RESISTANCE OF CHROMIUM NITRIDES OBTAINED BY VACUUM GAS NITRIDING OF ELECTROLYTIC CHROMIUM DEPOSITED ON AISI H13 STEEL

    Directory of Open Access Journals (Sweden)

    H. Cifuentes

    2013-06-01

    Full Text Available In this scientific research paper, the microstructure and corrosion resistance of chromium nitrides obtained from a duplex treatment consisting of an electroplated hard chromium coating applied on a steel AISI H13 follow by a thermochemical treatment in vacuum using NH3 as precursor gas of nitrogen, is evaluated. This type of duplex treatments combine the benefits of each individual treatment in order to obtain, with this synergic effect, compounds type CrxN more economic than those obtained by other kind of treatments e.g. physical vapor deposition (PVD. The results obtained by X-Ray Diffraction (XRD indicate the surface and subsurface transformation of the electrolytic hard chromium coating by formation of CrN and Cr2N phases. Likewise, potentiodynamic polarization tests indicate an increase in corrosion resistance of such kind of compounds in comparison with the obtained results with electroplated hard chromium.

  7. Laser shock peening without coating induced residual stress distribution, wettability characteristics and enhanced pitting corrosion resistance of austenitic stainless steel

    Science.gov (United States)

    Prabhakaran, S.; Kulkarni, Aniket; Vasanth, G.; Kalainathan, S.; Shukla, Pratik; Vasudevan, Vijay K.

    2018-01-01

    Low energy laser shock peening without coating (LSPwC) was conducted on AISI 304 austenitic stainless steel specimens with varying pulse densities or overlapping. Highest magnitude of compressive residual stress (CRS) was achieved for an optimized pulse density of 2500 pulses/cm2 (75% overlapping). The 2-D and 3-D topographical analysis were indicative of the fact that controlled roughening of the surface was achieved after the LSPwC process. After the LSPwC process, the hydrophilic unpeened surface was converted into the hydrophobic surface, thus decreasing the wettability characteristics of the surface. The X-ray diffraction (XRD) results reveal that there is a beginning of the martensite transformation and the rise in the intensity value of the peaks after LSPwC indicates the presence of compressive residual stresses induced in the specimen. The optical microscope and high-resolution transmission electron microscope results provided evidence of grain refinement and deformation induced refinement features such as multidirectional mechanical twinning, dislocations lines, micro shear cells and stacking faults in the near and sub-surface areas. The average hardness value of the LSPwC specimens was found to be increased by 28% more than the untreated specimen. The potentiodynamic polarization revealed that there was a considerable amount of increase in the pitting corrosion resistance after the LSPwC process, thus, supporting to extend the fatigue life of the specimen. The electrochemical impedance spectroscopic (EIS) analysis depicts that the LSPwC process supports the formation of the strong passivation layer in 3.5% NaCl solution.

  8. Corrosion of X65 Pipeline Steel Under Deposit and Effect of Corrosion Inhibitor

    Directory of Open Access Journals (Sweden)

    XU Yun-ze

    2016-10-01

    Full Text Available Effect of the deposit on the electrochemical parameters of X65 pipeline steel in oxygen contained sodium chloride solution was studied by EIS and PDS methods. The galvanic corrosion behavior under deposit and effect of different concentration of corrosion inhibitor PBTCA were studied by electrical resistance (ER method combined with ZRA. The results show that the corrosion potential of X65 steel shifts negatively as SiO2 covering its surface and the corrosion rate becomes lower. When the galvanic couple specimen with deposit is electrically connected with the specimen without deposit, anodic polarization occurs on X65 steel under deposit and the galvanic current density decreases from 120μA/cm2 to 50μA/cm2 and keeps stable. As 5×10-5, 8×10-5 and 3×10-4 PBTCA were introduced into the solution, the galvanic current density reaches the highest 1300μA/cm2 and then decreases to 610μA/cm2 keeping stable around 610μA/cm2, corrosion rate of X65 steel under deposit reaches 6.11mm/a. PBTCA accelerates the corrosion of X65 steel under deposit in oxygen contained solution. Through the investigation on the surface of the specimens, serious local corrosion occurs on the X65 steel surface under deposit.

  9. Super-Hydrophobic Green Corrosion Inhibitor On Carbon Steel

    Science.gov (United States)

    Hassan, H.; Ismail, A.; Ahmad, S.; Soon, C. F.

    2017-06-01

    There are many examples of organic coatings used for corrosion protection. In particular, hydrophobic and super-hydrophobic coatings are shown to give good protection because of their enhanced ability to slow down transport of water and ions through the coating. The purpose of this research is to develop water repellent coating to avoid direct contact between metal and environment corrosive and mitigate corrosion attack at pipeline system. This water repellent characteristic on super-hydrophobic coating was coated by electrodeposition method. Wettability of carbon steel with super-hydrophobic coating (cerium chloride and myristic acid) and oxidized surface was investigated through contact angle and inhibitor performance test. The inhibitor performance was studied in 25% tannin acid corrosion test at 30°C and 3.5% sodium chloride (NaCl). The water contact angle test was determined by placing a 4-μL water droplet of distilled water. It shows that the wettability of contact angle super-hydrophobic with an angle of 151.60° at zero minute can be classified as super-hydrophobic characteristic. By added tannin acid as inhibitor the corrosion protection on carbon steel becomes more consistent. This reveals that the ability of the coating to withstand with the corrosion attack in the seawater at different period of immersions. The results elucidate that the weight loss increased as the time of exposure increased. However, the corrosion rates for uncoated carbon steel is high compared to coated carbon steel. As a conclusion, from both samples it can be seen that the coated carbon steel has less corrosion rated compared to uncoated carbon steel and addition of inhibitor to the seawater provides more protection to resist corrosion attack on carbon steel.

  10. Surface treatment and corrosion behaviour of austenitic stainless steel biomaterial

    Science.gov (United States)

    Oravcová, M.; Palček, P.; Zatkalíková, V.; Tański, T.; Król, M.

    2017-02-01

    In this article results from corrosion behaviour of austenitic stainless steel AISI 316L after different surface treatments are published. “As received” surface and surface after grinding resulted in lower resistance to pitting corrosion in physiological solution than electrochemically polished in H3PO4+H2SO4+H2O. Electropolishing also improved the surface roughness in comparison with the “as received” surface. Deposition of Al2O3 nanometric ALD coating improves the corrosion resistance of stainless steel in chloride-containing environment by shifting the breakdown potential toward more positive values. This oxide coating not only improves the corrosion resistance but it also affects the wettability of the surface, resulting in hydrophobic surface.

  11. Effect of a nano-sized TiC particle addition on the flow-assisted corrosion resistance of SA 106B carbon steel

    Science.gov (United States)

    Park, Jin-Ju; Park, Eun-Kwang; Lee, Gyoung-Ja; Rhee, Chang-Kyu; Lee, Min-Ku

    2017-09-01

    Carbon steel with dispersed nano-sized TiC ceramic particles was fabricated by the ex-situ introduction of the particles into the melt, with the flow-assisted corrosion (FAC) resistance then investigated in the presence and absence of TiC nanoparticles using a once-through type of FAC loop test. From the potentiodynamic polarization curves, the current density at any given anodic potential was decreased and the open-circuit potential was increased by the addition of TiC nanoparticles. In addition, when the nano-sized TiC particles were added, the FAC rate was 1.38 times lower than that of carbon steel without TiC nanoparticles, indicating an improvement of the FAC resistance due to the homogeneous distribution of the TiC reinforcing nanoparticles.

  12. Microstructure and corrosion resistance of nitrogen-rich surface layers on AISI 304 stainless steel by rapid nitriding in a hollow cathode discharge

    Science.gov (United States)

    Li, Yang; He, Yongyong; Zhang, Shangzhou; Wang, Wei; Zhu, Yijie

    2018-01-01

    Nitriding treatments have been successfully applied to austenitic stainless steels to improve their hardness and tribological properties. However, at temperatures above 450 °C, conventional plasma nitriding processes decrease the corrosion resistance due to the formation of CrN phases within the modified layer. In this work, AISI 304 austenitic stainless steels were efficiently treated by rapid plasma nitriding at a high temperature of 530 °C in a hollow cathode discharge. The enhanced ionization obtained in the hollow cathode configuration provided a high current density and, consequently, a high temperature could be attained in a short time. The nitrided layers were characterized by X-ray diffraction, scanning electron microscopy, atomic force microscopy, transmission electron microscopy and X-ray photoelectron spectroscopy. The results indicated that the dual-layer structure of the nitrided layer consists of a high-N face-centered cubic structure with a free CrN precipitate outer (top) layer and a nitrogen-expanded austenite S-phase bottom layer. The rapid nitriding-assisted hollow cathode discharge technique permits the use of high temperatures, as high as 530 °C, without promoting degradation in the corrosion resistance of stainless steel.

  13. Corrosion-resistant metal surfaces

    Science.gov (United States)

    Sugama, Toshifumi [Wading River, NY

    2009-03-24

    The present invention relates to metal surfaces having thereon an ultrathin (e.g., less than ten nanometer thickness) corrosion-resistant film, thereby rendering the metal surfaces corrosion-resistant. The corrosion-resistant film includes an at least partially crosslinked amido-functionalized silanol component in combination with rare-earth metal oxide nanoparticles. The invention also relates to methods for producing such corrosion-resistant films.

  14. Analysis of the structural steels corrosion resistance in sour water from petroleum refineries; Analise da resistencia a corrosao de acos estruturais em aguas acidas de refinarias de petroleo

    Energy Technology Data Exchange (ETDEWEB)

    Proenca, Marcos B.; Freire, Celia M. de A. [Universidade Estadual de Campinas, SP (Brazil). Faculdade de Engenharia Mecanica; Santos, Margatita B. [Universidade Estadual de Campinas, SP (Brazil). Inst. de Fisica. Dept. de Fisica Aplicada

    1994-07-01

    The presence of H{sub 2} S in refineries FCC sour water provokes the formation of a passive Fe S scale. The cyanides present on sour water remove this scale, raising the corrosion rate in pipping and vessels. In this work it was measured the corrosion rate of structural steels in this water by electrochemical methods. Anodic polarization curves were plotted and the corrosion rates of the steels were determined. (author)

  15. Investigation of Fecraly Coating on Corrosion Behaviour of Mild Steel

    Directory of Open Access Journals (Sweden)

    Joseph B. AGBOOLA

    2009-07-01

    Full Text Available Steel has found wide application in hot rolling equipments in the steel industry and the oil rig structures in sea water. These equipments are frequently subjected to corrosive and temperature condition which causes severe damage to them, hence the need to develop steel suitable to withstand these conditions in terms of surface treatment. This research work investigates the effect of FeCrAlY coating on mild steel under high temperature and aggressive environment. Iron based coatings are used due to low cost among other properties such as good corrosion resistance, ease of machining and high ductility when compared to hard metals.Thermal spraying of the specimens was carried out using high velocity oxygen fuel (HVOF. Corrosion test was carried out on both coated and uncoated samples. All samples were subjected to the same high temperature treatment for oxidation test.

  16. Very Hard Corrosion-Resistant Roll-Bonded Cr Coating on Mild Steel in Presence of Graphite

    Science.gov (United States)

    Kumar, Pankaj; Khara, S.; Shekhar, S.; Mondal, K.

    2017-11-01

    Abstract The present work discusses the development of very hard Cr and Cr-carbide coating by roll bonding of Cr powder on a mild steel followed by annealing at 800, 1000, 1100 and 1200 °C with and without the presence of graphite powder packing in argon environment. In addition, the effect of a roll skin pass of 5% prior to the application of coating was studied. The presence of graphite allows diffusion of both carbon and Cr in the mild steel substrate, leading to the formation of Cr-carbide on the outer surface, making the surface very hard (VHN 1800). Depending on the annealing temperature and processing condition, diffusion layer thickness of Cr is found to be in the range of 10-250 μm with Cr content of 12.5-15 wt.% across the diffusion layer. Excellent stable passivity of the coated surface is observed in 0.2 N H2SO4, which is comparable to a highly passivating 304 stainless steel, and very low corrosion rate of the coating is observed as compared to the substrate mild steel.

  17. Change of n-type to p-type conductivity of the semiconductor passive film on N-steel: Enhancement of the pitting corrosion resistance

    Directory of Open Access Journals (Sweden)

    Metikoš-Huković Mirjana

    2013-01-01

    Full Text Available The electrochemically-assisted modification of the N-austenitic stainless steel (ASS N25 surface was successfully employed to improve barrier properties of the passive film in a chloride containing solution. The chemical composition, electronic and barrier properties of the surface film before and after the electrochemical treatment were examined using X-ray photoelectron spectroscopy (XPS and electrochemical impedance spectroscopy (EIS. Electrochemical measurements were carried out in a corrosion testing solution. The excellent corrosion resistance (both pitting and general of the N-steel’s modified surface was discussed according to the Mott-Schottky analysis of the interfacial capacitance of the space charge layer and EIS results. The conductivity change of the surface film from an n- to a p-type in the pitting susceptible region was explained using the XPS analysis and semiconducting properties of the film.

  18. Development of novel protective high temperature coatings on heat exchanger steels and their corrosion resistance in simulated coal firing environment; Developpement de revetements pour les aciers d'echangeurs thermiques et amelioration de leur resistance a la corrosion en environnement simulant les fumees de combustion et de charbon

    Energy Technology Data Exchange (ETDEWEB)

    Rohr, V.

    2005-10-15

    Improving the efficiencies of thermal power plants requires an increase of the operating temperatures and thus of the corrosion resistance of heat exchanger materials. Therefore, the present study aimed at developing protective coatings using the pack cementation process. Two types of heat exchanger steels were investigated: a 17% Cr-13% Ni austenitic steel and three ferritic-martensitic steels with 9 (P91 and P92) and 12% Cr (HCM12A). The austenitic steel was successfully aluminized at 950 C. For the ferritic-martensitic steels, the pack cementation temperature was decreased down to 650 C, in order to maintain their initial microstructure. Two types of aluminides, made of Fe{sub 2}Al{sub 5} and FeAl, were developed. A mechanism of the coating formation at low temperature is proposed. Furthermore, combining the pack cementation with the conventional heat treatment of P91 allowed to take benefit of higher temperatures for the deposition of a two-step Cr+Al coating. The corrosion resistance of coated and uncoated steels is compared in simulated coal firing environment for durations up to 2000 h between 650 and 700 C. It is shown that the coatings offer a significant corrosion protection and, thus, an increase of the component lifetime. Finally, the performance of coated 9-12% Cr steels is no longer limited by corrosion but by interdiffusion between the coating and the substrate. (author)

  19. Effect of free Cr content on corrosion behavior of 3Cr steels in a CO2 environment

    Science.gov (United States)

    Li, Wei; Xu, Lining; Qiao, Lijie; Li, Jinxu

    2017-12-01

    The corrosion behavior of 3Cr steels with three microstructures (martensite, bainite, combined ferrite and pearlite) in simulated oil field formation water with a CO2 partial pressure of 0.8 MPa was investigated. The relationships between Cr concentrations in corrosion scales and corrosion rates were studied. The precipitated phases that contained Cr were observed in steels of different microstructures, and free Cr content levels were compared. The results showed that steel with the martensite microstructure had the highest free Cr content, and thus had the highest corrosion resistance. The free Cr content of bainite steel was lower than that of martensite steel, and the corrosion rate of bainite steel was higher than that of martensite steel. Because large masses of Cr were combined in ferrite and pearlite steel, the corrosion rates of ferrite and pearlite steel were the highest. Free Cr content in steel affects its corrosion behavior greatly.

  20. Effect of surface passivation on corrosion resistance and antibacterial properties of Cu-bearing 316L stainless steel

    Science.gov (United States)

    Zhao, Jinlong; Xu, Dake; Shahzad, M. Babar; Kang, Qiang; Sun, Ying; Sun, Ziqing; Zhang, Shuyuan; Ren, Ling; Yang, Chunguang; Yang, Ke

    2016-11-01

    The resistance for pitting corrosion, passive film stability and antibacterial performance of 316L-Cu SS passivated by nitric acid solution containing certain concentration of copper sulfate, were studied by electrochemical cyclic polarization, electrochemical impedance spectroscopy (EIS) and co-culture with bacteria. Inductively coupled plasma mass spectrometry (ICP-MS) was used to analyze the Cu2+ ions release from 316L-Cu SS surface. XPS analysis proved that the enrichment of CuO, Cr2O3 and Cr(OH)3 on the surface of specimen could simultaneously guarantee a better corrosion resistance and stable antibacterial properties. The biocompatibility evaluation determined by RTCA assay also indicated that the 316L-Cu SS after antibacterial passivation was completely biocompatible.

  1. Localized Corrosion of Chromium Coated Steel

    NARCIS (Netherlands)

    Zhang, X.; Beentjes, P.; Mol, A.; Terryn, H.

    2006-01-01

    In this paper, we report on the studies of the local corrosion behaviour of chromium-coated ultra low carbon steel in NaCl solution using polarization, electrochemical impedance spectroscopy (EIS) and SVET.

  2. Corrosion behavior of sensitized duplex stainless steel.

    Science.gov (United States)

    Torres, F J; Panyayong, W; Rogers, W; Velasquez-Plata, D; Oshida, Y; Moore, B K

    1998-01-01

    The present work investigates the corrosion behavior of 2205 duplex stainless steel in 0.9% NaCl solution after various heat-treatments, and compares it to that of 316L austenitic stainless steel. Both stainless steels were heat-treated at 500, 650, and 800 degrees C in air for 1 h, followed by furnace cooling. Each heat-treated sample was examined for their microstructures and Vickers micro-hardness, and subjected to the X-ray diffraction for the phase identification. Using potentiostatic polarization method, each heat-treated sample was corrosion-tested in 37 degrees C 0.9% NaCl solution to estimate its corrosion rate. It was found that simulated sensitization showed an adverse influence on both steels, indicating that corrosion rates increased by increasing the sensitization temperatures.

  3. Corrosion behaviour of sintered duplex stainless steels

    Energy Technology Data Exchange (ETDEWEB)

    Utrilla, M. Victoria; Urena, Alejandro; Otero, Enrique; Munez, Claudio Jose [Escuela Superior de Ciencias Experimentales y Tecnologia, Universidad Rey Juan Carlos, C/ Tulipan s/n, 28933 Mostoles, Madrid (Spain)

    2004-07-01

    Duplex austenite-ferrite stainless steels were prepared by mixing austenitic (316L) and ferritic (434L) atomized powders. Although different 316L/434L ratios were prepared, present work centred its study on 50% ferrite - 50% austenite sintered steel. The powders were mixed and pressed at 700 MPa and sintered at 1250 deg. C for 30 min in vacuum. The cooling rate was 5 deg. C/min. Solution treatment was carried out to homogenize the microstructure at 1100 deg. C during 20 min. A microstructural study of the material in solution was performed, evaluating the microstructure, proportion and shape of porosity, and ferrite percentage. This last was measured by two methods, quantitative metallography and Fischer ferrito-metry. The materials were heat treated in the range of 700 to 1000 deg. C, for 10, 30 and 60 min and water quenched, to study the microstructural changes and the influence on the intergranular corrosion resistance. The method used to evaluate the sensitization to the intergranular corrosion was the electrochemical potentio-kinetic reactivation procedure (EPR). The test solution was 0.5 M H{sub 2}SO{sub 4} + 0,01 M KSCN at 30 deg. C. The criterion used to evaluate the sensitization was the ratio between the maximum reactivation density (Ir) and the maximum activation density (Ia). The results of the electrochemical tests were discussed in relation with the microstructures observed at the different heat treatments. (authors)

  4. Corrosion Properties of Laser Welded Stainless Steel

    DEFF Research Database (Denmark)

    Weldingh, Jakob; Olsen, Flemmming Ove

    1997-01-01

    In this paper the corrosion properties of laser welded AISI 316L stainless steel are examined. A number of different welds has been performed to test the influence of the weld parameters of the resulting corrosion properties. It has been chosen to use the potential independent critical pitting...... temperature (CPT) test as corrosion test. The following welding parameters are varied: Welding speed, lsser power, focus point position and laser operation mode (CW or pulsed)....

  5. An evaluation of carbon steel corrosion under stagnant seawater conditions.

    Science.gov (United States)

    Lee, Jason S; Ray, Richard I; Lemieux, Edward J; Falster, Alexander U; Little, Brenda J

    2004-01-01

    Corrosion of 1020 carbon steel coupons in natural seawater over a 1-year period was more aggressive under strictly anaerobic stagnant conditions than under aerobic stagnant conditions as measured by weight loss and instantaneous corrosion rate (polarization resistance). Under oxygenated conditions, a two-tiered oxide layer of lepidocrocite/goethite formed. The inner layer was extremely tenacious and resistant to acid cleaning. Under anaerobic conditions, the corrosion product was initially a non-tenacious sulphur-rich corrosion product, mackinawite, with enmeshed bacteria. As more sulphide was produced the mackinawite was transformed to pyrrhotite. In both aerobic and anaerobic exposures, corrosion was more aggressive on horizontally oriented coupons compared to vertically oriented samples.

  6. Friction welding of a nickel free high nitrogen steel: influence of forge force on microstructure, mechanical properties and pitting corrosion resistance

    Directory of Open Access Journals (Sweden)

    Mrityunjoy Hazra

    2014-01-01

    Full Text Available In the present work, nickel free high nitrogen austenitic stainless steel specimens were joined by continuous drive friction welding process by varying the amount of forge (upsetting force and keeping other friction welding parameters such as friction force, burn-off, upset time and speed of rotation as constant at appropriate levels. The joint characterization studies include microstructural examination and evaluation of mechanical (micro-hardness, impact toughness and tensile and pitting corrosion behaviour. The integrity of the joint, as determined by the optical microscopy was very high and no crack and area of incomplete bonding were observed. Welds exhibited poor Charpy impact toughness than the parent material. Toughness for friction weld specimens decreased with increase in forge force. The tensile properties of all the welds were almost the same (irrespective of the value of the applied forge force and inferior to those of the parent material. The joints failed in the weld region for all the weld specimens. Weldments exhibited lower pitting corrosion resistance than the parent material and the corrosion resistance of the weld specimens was found to decrease with increase in forge force.

  7. V and Nb Influence on the Austenitic Stainless Steel Corrosion in 0.1 M HCl

    Directory of Open Access Journals (Sweden)

    Amel GHARBI

    2014-05-01

    Full Text Available Vanadium and niobium were added in AISI309 austenitic stainless steel composition to modify their structure and pitting corrosion resistance in 0.1 M HCl. The structural characterization was carried out by X-rays diffraction and optical microscopy. Corrosion behavior was investigated using potentiodynamic tests and electrochemical impedance measurements (EIS .Results showed that vanadium and niobium addition precipitated stable carbides (VC, NbC to chromium carbides’ detriment and improved austenitic stainless steel corrosion resistance.

  8. Inhibition Effect of Deanol on Mild Steel Corrosion in Dilute ...

    African Journals Online (AJOL)

    NICOLAAS

    2014-06-23

    Jun 23, 2014 ... This electrolytic mechanism blocks the active sites on the electrode and stifles the cathodic reaction. The positive potential shift in the acid indicates the enhance- ment of the steel's corrosion resistance in the presence of MDMAE, due to chemical adsorption (chemisorption) of the inhibitor cations onto the ...

  9. Imposed potential measurement to evaluate the pitting corrosion resistance and the galvanic behaviour of a highly alloyed austenitic stainless steel and its weldment in a LiBr solution at temperatures up to 150ºC

    OpenAIRE

    Blasco Tamarit, María Encarnación; García García, Dionisio Miguel; García Antón, José

    2011-01-01

    Pitting corrosion resistance and galvanic behaviour of Alloy 31, a highly alloyed austenitic stainless steel (UNS N08031), and its weldment were studied in a heavy brine LiBr solution 1080 g/l at different temperatures (75–150 °C) using electrochemical techniques. The Mixed Potential Theory was used to evaluate the galvanic corrosion between the base and welded metals. Cyclic potentiodynamic curves indicate that high temperatures make passivation and repassivation of pits difficult, because t...

  10. Marine atmospheric corrosion of carbon steels

    Energy Technology Data Exchange (ETDEWEB)

    Morcillo, M.; Alcantara, J.; Diaz, I.; Chico, B.; Simancas, J.; Fuente, D. de la

    2015-07-01

    Basic research on marine atmospheric corrosion of carbon steels is a relatively young scientific field and there continue to be great gaps in this area of knowledge. The presence of akaganeite in the corrosion products that form on steel when it is exposed to marine atmospheres leads to a notable increase in the corrosion rate. This work addresses the following issues: (a) environmental conditions necessary for akaganeite formation; (b) characterisation of akaganeite in the corrosion products formed; (c) corrosion mechanisms of carbon steel in marine atmospheres; (d) exfoliation of rust layers formed in highly aggressive marine atmospheres; (e) long-term corrosion rate prediction; and (f) behaviour of weathering steels. Field research has been carried out at Cabo Vilano wind farm (Camarinas, Galicia) in a wide range of atmospheric salinities and laboratory work involving the use of conventional atmospheric corrosion techniques and near-surface and bulk sensitive analytical techniques: scanning electron microscopy (SEM)/energy dispersive spectrometry (EDS), X-ray diffraction (XRD), Mossbauer spectroscopy and SEM/μRaman spectroscopy. (Author)

  11. Pitting corrosion resistance and bond strength of stainless steel overlay by friction surfacing on high strength low alloy steel

    OpenAIRE

    Amit Kumar Singh; G. Madhusudhan Reddy; K. Srinivas Rao

    2015-01-01

    Surface modification is essential for improving the service properties of components. Cladding is one of the most widely employed methods of surface modification. Friction surfacing is a candidate process for depositing the corrosion resistant coatings. Being a solid state process, it offers several advantages over conventional fusion based surfacing process. The aim of this work is to identify the relationship between the input variables and the process response and develop the predictive mo...

  12. Improved Corrosion Resistance of Pulse Plated Nickel through Crystallisation Control

    DEFF Research Database (Denmark)

    Tang, Peter Torben; Watanabe, Tohru; Andersen, Jens Enevold Thaulov

    1995-01-01

    When electrodeposition of nickel is used for corrosion protection of steel two aspects are important. The porosity of the coating and the resistance against corrosion provided by the coating itself. Using simple pulsed current (PC) plating, the size of the deposited crystals can be significantly...... smaller, thereby reducing porosity correspondingly. This usually also leads to improved hardness of the coating. Introducing pulse reversal (PR) plating, the most active crystals are continuously dissolved during the anodic pulse, providing a coating with improved subsequent corrosion resistance in almost...... any corrosive environment. This correlation between film texture and corrosion resistance will be discussed....

  13. Corrosion of Steel in High-Strength Self-Compacting Concrete Exposed to Saline Environment

    Directory of Open Access Journals (Sweden)

    Hana A. Yousif

    2014-01-01

    Full Text Available A research work was carried out to investigate the effectiveness of high-strength self-compacting concrete (SF-R in controlling corrosion of embedded steel. Reinforced concrete cylinders and plain cubes were subjected to 5% NaCl solution. Slump flow, J-ring, V-funnel, compressive strength, electrical resistance, and electrochemical tests were conducted. Corrosion resisting characteristics of steel were examined by monitoring corrosion potential, polarization resistance, corrosion currents, and Tafel plots. The relationship between corrosion current density and corrosion potential was established. Results were compared with characteristics of a grade 40 MPa reference concrete (R and grade 70 MPa conventional self-compacting concrete (SP. Results indicated that at 270 days of exposure, the corrosion currents for steel in SF-R were 63- and 16-fold lower compared to those of steel in R and SP concretes, respectively. This concrete showed a considerable increase in electrical resistance and compressive strength of 96 MPa at 28 days of exposure. Relying on corrosion risk classification based on corrosion current densities and corrosion potentials, the steel in SF-R concrete is definitely in the passive condition. The splendid durability performance of steel in SF-R concrete linked to adorable self-compacting features could furnish numerous opportunities for future structural applications in severe environmental conditions.

  14. Effects of Alloying Elements (Cr, Mn) on Corrosion Properties of Carbon Steel in Synthetic Seawater

    Energy Technology Data Exchange (ETDEWEB)

    Hyun, Youngmin; Kim, Heesan [Hongik University, Sejong (Korea, Republic of)

    2016-02-15

    Effects of alloying elements, manganese and chromium, on corrosion resistance of carbon steel were examined using weight loss test and electrochemical tests (polarization test and electrochemical impedance spectroscopy (EIS)) in synthetic seawater at 60 ℃. The results from the weight loss test showed that chromium effectively improved corrosion resistance of carbon steel during the entire immersion time, but manganese improved corrosion resistance after the lowered corrosion resistance at the beginnings of immersion. Unlike the weight loss test, the electrochemical tests showed that the corrosion resistance did not increase with immersion time, in all the specimens. This disagreement is explained by the presence of rust involved in electrochemical reaction during electrochemical tests. The analysis of rust with transmission electron microscopy (TEM)−energy dispersive spectroscopy (EDS) showed that the amorphous-like rust layer located at the metal/rust interface with enriched alloying element (Cr, Mn) prevents diffusion of corrosive species into a metal/rust interface effectively, which leads to increased corrosion resistance. The initial corrosion behaviour is also affected by the rust types. In other words, manganese accelerated the formation of spinel oxides, negatively affecting corrosion resistance. Meanwhile, chromium accelerated the formation of goethite but impeded the formation of spinel oxides, positively affecting the corrosion resistance. From the above results, the corrosion resistance of steel is closely related with a rust type.

  15. Polymeric nano-materials for corrosion control of steel in concrete

    NARCIS (Netherlands)

    Varini, M.; Koleva, D.A.; Denkova, A.G.; Mol, J.M.C.; Terryn, H.; Van Breugel, K.

    2013-01-01

    Polymeric nano-materials utilization in reinforced concrete, aiming to deal with steel corrosion was developed in previous works. Promising results were obtained with PEO–b–PS nano-formations, both in terms of enhanced bulk matrix properties and improved steel corrosion resistance. Recent research

  16. Progress in the Research of Fatigue of Weathering Steel after Corrosion

    Science.gov (United States)

    Jianyu, Liang; Jian, Yao; Youwu, Xu

    2017-12-01

    Weathering steel has a good corrosion resistance in the atmosphere, and the application of weathering steel in civil structure also reduces the cost of painting and maintenance. It is also possible for the bare weathering steel to bear the fatigue load with a rust layer. This paper summarizes the fatigue researches after corrosion of weathering steel, including the shape of specimens, failure modes of fatigue and the conclusions obtained through experimental investigations. It is also introduced the fatigue model of weathering steel after corrosion, which can be useful for the engineering application or further researches.

  17. Evaluation of corrosion resistance of various concrete reinforcing materials.

    Science.gov (United States)

    2013-06-01

    The Vermont Agency of Transportation undertook a simple experiment to determine the corrosion : resistance ability of various reinforcing steels (rebar) that may be used in bridges and other concrete : structures. Eight types of rebar were used in th...

  18. Corrosion Behavior of Austenitic and Duplex Stainless Steels in Lithium Bromide

    Directory of Open Access Journals (Sweden)

    Ayo Samuel AFOLABI

    2009-07-01

    Full Text Available The corrosion behavior of austenitic and duplex stainless steels in various concentrations of lithium, bromide solution was investigated by using the conventional weight loss measurement method. The results obtained show that corrosion of these steels occurred due to the aggressive bromide ion in the medium. Duplex stainless steel shows a greater resistance to corrosion than austenitic stainless steel in the medium. This was attributed to equal volume proportion of ferrite and austenite in the structure of duplex stainless steel coupled with higher content of chromium in its composition. Both steels produced electrochemical noise at increased concentrations of lithium bromide due to continuous film breakdown and repair caused by reduction in medium concentration by the alkaline corrosion product while surface passivity observed in duplex stainless steel is attributed to film stability on this steel.

  19. Stress corrosion cracking susceptibility of 18 Ni maraging steel

    Science.gov (United States)

    Humphries, T. S.; Nelson, E. E.

    1974-01-01

    The stress corrosion cracking (SCC) resistance of 18Ni maraging steel (grades 200, 250, 300, and 350) was determined in 3.5 percent salt (NaCl) solution, synthetic sea water, high humidity, and outside MSFC atmosphere. All grades of the maraging steel were found to be susceptible to SCC in varying degrees according to their strengths, with the lowest strength steel (grade 200) being the least susceptible and the highest strength steel (grade 350), the most susceptible to SCC. The SCC resistance of 250 grade maraging steel was also evaluated in salt and salt-chromate solutions using fracture mechanics techniques. The threshold value, K sub SCC, was found to be approximately 44 MN/sq m square root m, (40 ksi square root in.) or 40 percent of the K sub Q value.

  20. Corrosion Inhibition of X52 Pipeline Steel in Chloride Solutions Using Nonionic Surfactant

    Science.gov (United States)

    Quej, L. M.; Contreras, A.; Aburto, J.

    Two concentrations of NPE-4 nonionic surfactant and corrosion inhibitor (CI) commercially available were added to NaCl (2.45 % and 3 %) and ocean water solutions (OWS) in order to study the corrosion process of API X52 pipeline steel. Corrosion inhibition of X52 pipeline steel in chloride solutions was evaluated by using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves. EIS analyses showed that 3 % NaCl was the more corrosive solution for X52 steel. Adding CI to 3 %NaCl solution improves the corrosion resistance of X52 steel; however, adding CI to OWS, the corrosion control of X52 steel was more evident preventing the pitting, salts embedding, and corrosion under deposits. X52 steel exposure to solutions adding surfactant as corrosion inhibitor after having been evaluated through polarization curves displayed low corrosion rates (0.88 mm/year). Standard free energy calculation suggested that surfactant is adsorbed physically into the X52 steel surface. Meanwhile, it was observed that CI was more difficult to adsorb on X52 steel surface, and consequently corrosion was higher than adding surfactant to chloride solutions.

  1. Identification of commercially available alloys for corrosion-resistant metallic reinforcement and test methods for evaluating corrosion-resistant reinforcement.

    Science.gov (United States)

    2008-01-01

    A literature review was conducted with the goal of identifying alternative low-cost corrosion-resistant steel reinforcement materials. The most promising alternate reinforcing materials seen to date that are less expensive than 300 series stainless s...

  2. Stress corrosion cracking evaluation of martensitic precipitation hardening stainless steels

    Science.gov (United States)

    Humphries, T. S.; Nelson, E. E.

    1980-01-01

    The resistance of the martensitic precipitation hardening stainless steels PH13-8Mo, 15-5PH, and 17-4PH to stress corrosion cracking was investigated. Round tensile and c-ring type specimens taken from several heats of the three alloys were stressed up to 100 percent of their yield strengths and exposed to alternate immersion in salt water, to salt spray, and to a seacoast environment. The results indicate that 15-5PH is highly resistant to stress corrosion cracking in conditions H1000 and H1050 and is moderately resistant in condition H900. The stress corrosion cracking resistance of PH13-8Mo and 17-4PH stainless steels in conditions H1000 and H1050 was sensitive to mill heats and ranged from low to high among the several heats included in the tests. Based on a comparison with data from seacoast environmental tests, it is apparent that alternate immersion in 3.5 percent salt water is not a suitable medium for accelerated stress corrosion testing of these pH stainless steels.

  3. Study of corrosion resistance of AISI 444 ferritic stainless steel for application as a biomaterial; Estudo da resistencia a corrosao do aco inoxidavel ferritico AISI 444 para aplicacao como biomaterial

    Energy Technology Data Exchange (ETDEWEB)

    Marques, Rogerio Albuquerque

    2014-09-01

    Ferritic stainless steels are ferromagnetic materials. This property does not allow their use in orthopedic prosthesis. Nevertheless, in some specific applications, this characteristic is very useful, such as, for fixing dental and facial prostheses by using magnetic attachments. In this study, the corrosion resistance and cytotoxicity of the AISI 444 ferritic stainless steel, with low nickel content, extra-low interstitial levels (C and N) and Ti and Nb stabilizers, were investigated for magnetic dental attachments application. The ISO 5832-1 (ASTM F-139) austenitic stainless steel and a commercial universal keeper for dental attachment (Neo-magnet System) were evaluated for comparison reasons. The first stainless steel is the most used metallic material for prostheses, and the second one, is a ferromagnetic keeper for dental prostheses (NeoM). In vitro cytotoxicity analysis was performed by the red neutral incorporation method. The results showed that the AISI 444 stainless steel is non cytotoxic. The corrosion resistance was studied by anodic polarization methods and electrochemical impedance spectroscopy (EIS), in a saline phosphate buffered solution (PBS) at 37 °C. The electronic properties of the passive film formed on AISI 444 SS were evaluated by the Mott-Schottky approach. All tested materials showed passivity in the PBS medium and the passive oxide film presented a duplex nature. The highest susceptibility to pitting corrosion was associated to the NeoM SS. This steel was also associated to the highest dopant concentration. The comparatively low levels of chromium (nearly 12.5%) and molybdenum (0.3%) of NeoM relatively to the other studied stainless steels are the probable cause of its lower corrosion resistance. The NeoM chemical composition does not match that of the SUS444 standards. The AISI 444 SS pitting resistance was equivalent to the ISO 5832-1 pointing out that it is a potential candidate for replacement of commercial ferromagnetic alloys used

  4. Stainless steel corrosion scale formed in reclaimed water: Characteristics, model for scale growth and metal element release.

    Science.gov (United States)

    Cui, Yong; Liu, Shuming; Smith, Kate; Hu, Hongying; Tang, Fusheng; Li, Yuhong; Yu, Kanghua

    2016-10-01

    Stainless steels generally have extremely good corrosion resistance, but are still susceptible to pitting corrosion. As a result, corrosion scales can form on the surface of stainless steel after extended exposure to aggressive aqueous environments. Corrosion scales play an important role in affecting water quality. These research results showed that interior regions of stainless steel corrosion scales have a high percentage of chromium phases. We reveal the morphology, micro-structure and physicochemical characteristics of stainless steel corrosion scales. Stainless steel corrosion scale is identified as a podiform chromite deposit according to these characteristics, which is unlike deposit formed during iron corrosion. A conceptual model to explain the formation and growth of stainless steel corrosion scale is proposed based on its composition and structure. The scale growth process involves pitting corrosion on the stainless steel surface and the consecutive generation and homogeneous deposition of corrosion products, which is governed by a series of chemical and electrochemical reactions. This model shows the role of corrosion scales in the mechanism of iron and chromium release from pitting corroded stainless steel materials. The formation of corrosion scale is strongly related to water quality parameters. The presence of HClO results in higher ferric content inside the scales. Cl- and SO42- ions in reclaimed water play an important role in corrosion pitting of stainless steel and promote the formation of scales. Copyright © 2016. Published by Elsevier B.V.

  5. Stress corrosion cracking behaviour of gas tungsten arc welded super austenitic stainless steel joints

    OpenAIRE

    Vinoth Kumar, M.; Balasubramanian, V.; Rajakumar, S.; Albert, Shaju K.

    2015-01-01

    Super 304H austenitic stainless steel with 3% of copper posses excellent creep strength and corrosion resistance, which is mainly used in heat exchanger tubing of the boiler. Heat exchangers are used in nuclear power plants and marine vehicles which are intended to operate in chloride rich offshore environment. Chloride stress corrosion cracking is the most likely life limiting failure with austenitic stainless steel tubing. Welding may worsen the stress corrosion cracking susceptibility of t...

  6. Corrosion fatigue behaviour of 317LN austenitic stainless steel in phosphoric acid

    Energy Technology Data Exchange (ETDEWEB)

    Onoro, J. [Ingenieria y Ciencia de los Materiales, ETSI Industriales, Universidad Politecnica de Madrid, c/Jose Gutierrez Abascal, 2, 28006 Madrid (Spain)], E-mail: javier.onoro@upm.es

    2009-10-15

    The corrosion fatigue crack-growth behaviour of AISI 317LN stainless steel was evaluated in air and in 85% phosphoric acid at 20 deg. C. Austenitic stainless steels with high molybdenum content have high corrosion resistance and good mechanical properties. However, this increase in the molybdenum content and other elements such as nitrogen can also modify the microstructure. This leads to a modification of its mechanical properties. The corrosion fatigue crack-growth rate was higher in phosphoric acid immersion than in air. Austenitic stainless steels with a fully austenitic microstructure were more ductile, tough, and behave better against corrosion fatigue. The higher resistance to corrosion fatigue was directly associated to its higher resistance to corrosion.

  7. Corrosion Testing of Stainless Steel Fuel Cell Hardware

    Energy Technology Data Exchange (ETDEWEB)

    Wilson, M.S.; Zawodzinski, C.; Gottesfeld, S.

    1998-11-01

    Metal hardware is gaining increasing interest in polymer electrolyte fuel cell (PEFC) development as a possible alternative to machined graphite hardware because of its potential for low-cost manufacturing combined with its intrinsic high conductivity, minimal permeability and advantageous mechanical properties. A major barrier to more widespread use of metal hardware has been the susceptibility of various metals to corrosion. Few pure metals can withstand the relatively aggressive environment of a fuel cell and thus the choices for hardware are quite limited. Precious metals such as platinum or gold are prohibitively expensive and so tend to be utilized as coatings on inexpensive substrates such as aluminum or stainless steel. The main challenge with coatings has been to achieve pin-hole free surfaces that will remain so after years of use. Titanium has been used to some extent and though it is very corrosion-resistant, it is also relatively expensive and often still requires some manner of surface coating to prevent the formation of a poorly conducting oxide layer. In contrast, metal alloys may hold promise as potentially low-cost, corrosion-resistant materials for bipolar plates. The dozens of commercially available stainless steel and nickel based alloys have been specifically formulated to offer a particular advantage depending upon their application. In the case of austenitic stainless steels, for example, 316 SS contains molybdenum and a higher chromium content than its more common counterpart, 304 SS, that makes it more noble and increases its corrosion resistance. Likewise, 316L SS contains less carbon than 316 SS to make it easier to weld. A number of promising corrosion-resistant, highly noble alloys such as Hastelloy{trademark} or Duplex{trademark} (a stainless steel developed for seawater service) are available commercially, but are expensive and difficult to obtain in various forms (i.e. wire screen, foil, etc.) or in small amounts for R and D

  8. Corrosion resistance of stainless steel, nickel-titanium, titanium molybdenum alloy, and ion-implanted titanium molybdenum alloy archwires in acidic fluoride-containing artificial saliva: An in vitro study

    Directory of Open Access Journals (Sweden)

    Venith Jojee Pulikkottil

    2016-01-01

    Full Text Available Objective: (1 To evaluate the corrosion resistance of four different orthodontic archwires and to determine the effect of 0.5% NaF (simulating high fluoride-containing toothpaste of about 2250 ppm on corrosion resistance of these archwires. (2 To assess whether surface roughness (Ra is the primary factor influencing the corrosion resistance of these archwires. Materials and Methods: Four different archwires (stainless steel [SS], nickel-titanium [NiTi], titanium molybdenum alloy [TMA], and ion-implanted TMA were considered for this study. Surface characteristics were analyzed using scanning electron microscopy, atomic force microscopy (AFM, and energy dispersive spectroscopy. Linear polarization test, a fast electrochemical technique, was used to evaluate the corrosion resistance, in terms of polarization resistance of four different archwires in artificial saliva with NaF concentrations of 0% and 0.5%. Statistical analysis was performed by one-way analysis of variance. Results: The potentiostatic study reveals that the corrosion resistance of low-friction TMA (L-TMA > TMA > NiTi > SS. AFM analysis showed the surface Ra of TMA > NiTi > L-TMA > SS. This indicates that the chemical composition of the wire is the primary influential factor to have high corrosion resistance and surface Ra is only secondary. The corrosion resistance of all wires had reduced significantly in 0.5% acidic fluoride-containing artificial saliva due to formation of fluoride complex compound. Conclusion: The presence of 0.5% NaF in artificial saliva was detrimental to the corrosion resistance of the orthodontic archwires. Therefore, complete removal of residual high-fluorinated toothpastes from the crevice between archwire and bracket during tooth brushing is mandatory.

  9. Electrochemical study of corrosion inhibition of stainless steel in phosphoric medium

    Energy Technology Data Exchange (ETDEWEB)

    Hnini, K.; Chtaini, A. [Laboratoire d' Electrochimie et de Bio Corrosion, Faculte des Sciences et Techniques, Beni-Mellal (Morocco); Khouili, M.; Elbouadili, A. [Laboratoire de Chimie Organique et Analytique, Faculte des Sciences et Techniques, Beni-Mellal (Morocco)

    2004-07-01

    The corrosion of metals represents a terrible waste of both natural resources and money, the failure of some stainless steel resulting from pitting corrosion is some times considered a technological problem, consequently, much effort has been expended in attempting to understand and overcome the corrosion therefore, many stainless steel/ environment combinations have been studied. The use of heterocyclic compounds as inhibitors is one of the most practical methods for protection against corrosion in acidic media. In continuation of our work on development of macrocyclic compounds as corrosion inhibitors we report in our study the corrosion inhibiting behaviour of organic compound Methoxy-2-Allyl-4 Phenol (MAP) containing coordinating and conjugation groups, at three forms (natural, polymerized and chemically treated) on the corrosion of stainless steel in phosphoric acid. This study focused on the comparison for corrosion inhibition proprieties of these different applications using potentiodynamic polarization, electrochemical impedance spectroscopy and SEM. The specimen was evaluated to determine change in his corrosion potential and resistance polarization; These MAP products have exhibited corrosion inhibition by maintaining a high resistance polarization (low corrosion rate) in each application. These results reveal that this compound is efficient inhibitor in all forms; the most inhibition efficiency is obtained with polymerized form. To further evaluate the test data, the steel surfaces were analyzed using scanning electron microscopy, SEM observations of surface treated concrete confirmed presence of inhibitor on the steel surfaces. (authors)

  10. [Corrosion resistance of Ti-Cu alloy].

    Science.gov (United States)

    Song, Yu-Xuan; Wang, Shi-Ming

    2010-09-01

    to investigate the corrosion behavior of Ti-Cu alloy in 0.9%NaCl solution and in acidified 0.9%NaCl solution. the microstructure of Ti-Cu alloys were characterized by means of X-ray diffraction (XRD). The electrochemical behavior of Ti-Cu alloy in two solutions (namely 0.9%NaCl solution and acidified 0.9%NaCl solution) was tested. Commercial pure Ti and 316L stainless steel were used as control. Ti-Cu alloys were composed by α-Ti and Ti(2)Cu intermetallic compound. After 3500 s immersion, the open circuit potential (OCP) values of pure Ti, Ti-5Cu alloy and Ti-10Cu alloy in 0.9% NaCl solution were -188, -181 and -173 mV, respectively. In 0.9% NaCl solution with lactic acid added, the OCP values were -143, -158 and -109 mV, respectively. In potentiodynamic polarization tests, the passive current densities of pure Ti and Ti-5Cu alloys were about 20 µA/cm(2). However, 316L stainless steel experienced pitting corrosion. it was possible to establish the following relation for their corrosion resistances: pure Ti≈Ti-5Cu > Ti-10Cu > 316L stainless steel. The addition of lactic acid in the solution did not compromise the corrosion resistance of Ti-Cu alloys.

  11. A Corrosion Sensor for Monitoring the Early-Stage Environmental Corrosion of A36 Carbon Steel

    Directory of Open Access Journals (Sweden)

    Dong Chen

    2014-08-01

    Full Text Available An innovative prototype sensor containing A36 carbon steel as a capacitor was explored to monitor early-stage corrosion. The sensor detected the changes of the surface- rather than the bulk- property and morphology of A36 during corrosion. Thus it was more sensitive than the conventional electrical resistance corrosion sensors. After being soaked in an aerated 0.2 M NaCl solution, the sensor’s normalized electrical resistance (R/R0 decreased continuously from 1.0 to 0.74 with the extent of corrosion. Meanwhile, the sensor’s normalized capacitance (C/C0 increased continuously from 1.0 to 1.46. X-ray diffraction result indicates that the iron rust on A36 had crystals of lepidocrocite and magnetite.

  12. Mechanical Behavior of Stainless Steel Fiber-Reinforced Composites Exposed to Accelerated Corrosion.

    Science.gov (United States)

    O'Brien, Caitlin; McBride, Amanda; E Zaghi, Arash; Burke, Kelly A; Hill, Alex

    2017-07-08

    Recent advancements in metal fibers have introduced a promising new type of stainless steel fiber with high stiffness, high failure strain, and a thickness steel fiber-reinforced polymer. However, stainless steel is known to be susceptible to pitting corrosion. The main goal of this study is to compare the impact of corrosion on the mechanical properties of steel fiber-reinforced composites with those of conventional types of stainless steel. By providing experimental evidences, this study may promote the application of steel fiber-reinforced composite as a viable alternative to conventional metals. Samples of steel fiber-reinforced polymer and four different types of stainless steel were subjected to 144 and 288 h of corrosion in ferric chloride solution to simulate accelerated corrosion conditions. The weight losses due to corrosion were recorded. The corroded and control samples were tested under monotonic tensile loading to measure the ultimate stresses and strains. The effect of corrosion on the mechanical properties of the different materials was evaluated. The digital image correlation (DIC) technique was used to investigate the failure mechanism of the corrosion-damaged specimens. Overall, steel fiber-reinforced composites had the greatest corrosion resistance.

  13. Testing of intergranular and pitting corrosion in sensitized welded joints of austenitic stainless steel

    Directory of Open Access Journals (Sweden)

    Bore V. Jegdic

    2017-06-01

    Full Text Available Pitting corrosion resistance and intergranular corrosion of the austenitic stainless steel X5Cr Ni18-10 were tested on the base metal, heat affected zone and weld metal. Testing of pitting corrosion was performed by the potentiodynamic polarization method, while testing of intergranular corrosion was performed by the method of electrochemical potentiokinetic reactivation with double loop. The base metal was completely resistant to intergranular corrosion, while the heat affected zone showed a slight susceptibility to intergranular corrosion. Indicators of pitting corrosion resistance for the weld metal and the base metal were very similar, but their values are significantly higher than the values for the heat affected zone. This was caused by reduction of the chromium concentration in the grain boundary areas in the heat affected zone, even though the carbon content in the examined stainless steel is low (0.04 wt. % C.

  14. Improvement in wear and corrosion resistance of AISI 1020 steel by high velocity oxy-fuel spray coating containing Ni-Cr-B-Si-Fe-C

    Science.gov (United States)

    Prince, M.; Thanu, A. Justin; Gopalakrishnan, P.

    2012-04-01

    In this investigation, AISI 1020 low carbon steel has been selected as the base material. The Ni based super alloy powder NiCrBSiFeC was sprayed on the base material using high velocity oxy-fuel spraying (HVOF) technique. The thickness of the coating was approximately 0.5 mm (500 μm). The coating was characterized using optical microscopy, Vickers microhardness testing, X-ray diffraction technique and scanning electron microscopy. Dry sliding wear tests were carried out at 3 m/s sliding speed under the load of 10 N for 1000 m sliding distance at various temperatures i.e., 35° C, 250° C and 350° C. The corrosion test was carried out in 1 M copper chloride in acetic acid solution. The polarization studies were also conducted for both base material and coating. The improvement in microhardness from 1.72 GPa (175 HV0.05) to 10.54 GPa (1075 HV0.05) was observed. The coatings exhibited 3-6 times improved wear resistance as compared with base material. Also, the corrosion rate was reduced by 3.5 times due to the presence of coatings.

  15. Comparison of Medium Manganese Steel and Q345 Steel on Corrosion Behavior in a 3.5 wt % NaCl Solution.

    Science.gov (United States)

    Su, Guanqiao; Gao, Xiuhua

    2017-08-11

    A cyclic wet/dry accelerated corrosion test was used to compare the corrosion behavior of medium-Mn steel and Q345 steel. In terms of scanning electron microscope (SEM), using X-ray diffraction (XRD), electron probe microanalysis (EPMA), X-ray photoelectron spectroscopy (XPS), and analysis of the corrosion process, the results showed that the medium-Mn steel did not exhibit higher corrosion resistance than Q345 steel due to the greater content of Mn-rich compounds in the rust layer. Moreover, the effect of a small amount of anti-corrosion elements in medium-manganese steel can regulate the corrosion rate. The conceptual model of the corrosion process of the medium-Mn steel in a 3.5 wt % NaCl solution is proposed.

  16. Investigation of Microstructure and Corrosion Propagation Behaviour of Nitrided Martensitic Stainless Steel Plates

    Directory of Open Access Journals (Sweden)

    Abidin Kamal Ariff Zainal

    2014-07-01

    Full Text Available Martensitic stainless steels are commonly used for fabricating components. For many applications, an increase in surface hardness and wear resistance can be beneficial to improve performance and extend service life. However, the improvement in hardness of martensitic steels is usually accompanied by a reduction in corrosion strength. The objective of this study is to investigate the effects of nitriding on AISI 420 martensitic stainless steel, in terms of microstructure and corrosion propagation behavior. The results indicate that the microstructure and phase composition as well as corrosion resistance were influenced by nitriding temperatures.

  17. Microbial Corrosion and Cracking in Steel

    DEFF Research Database (Denmark)

    Hilbert, Lisbeth Rischel

    1998-01-01

    and for recommendations in regards to electrochemical monitoring of MIC. The work presented here and further studies are also planned to lead to a Ph.D. thesis on "MIC monitoring based on mechanisms of corrosion".The results of laboratory experiments conducted in the period 1995 to 1997 are summarised. Conclusions...... will be based on results from the entire 3 year period, but only selected experimental data primarily from the latest experiments will be presented in detail here.Microbial corrosion of carbon steel under influence of sulphate-reducing bacteria (SRB) is characterised by the formation of both biofilm...... and corrosion products (ferrous sulphides) on the metal surface. Experiments have been conducted on carbon steel exposed in near neutral (pH 6 to 8.5) saline hydrogen sulphide environment (0 to 100 mg/l total dissolved sulphide) for a period of 14 days. Furthermore coupons have been exposed in a bioreactor...

  18. Corrosion of two kinds of cast steels containing chromium in hot concentrated alkaline

    Directory of Open Access Journals (Sweden)

    LI Wei

    2007-02-01

    Full Text Available A typical hot concentrated alkaline corrosion environment exists in alumina metallurgical industry, so that steel materials with outstanding alkaline corrosion resistance are strongly demanded for its processing equipment. In this paper, the corrosion resistance of two kinds of martensitic cast steels containing chromium in static 303g/L NaOH alkaline solution at 85℃ was studied through polarization and potential-time curves, corrosion weight loss and corrosion morphology analysis. Experimental results showed that protection effect by passive film of cast steel containing Cr was temporary. The low carbon steel without Cr content also exhibited chemical passivity in the same solution. The corrosion mode of the tested Cr-containing cast steel was composed of active dissolving corrosion and caustic embrittlement cracking. Dissolving corrosion was the primary mechanism for the induced weight loss, while severe caustic embrittlement cracking was secondary. With the increase of chromium content in the cast steel, the tendency of the caustic embrittlement cracking decreased, while the active dissolving corrosion increased.

  19. Dependence of corrosion properties of AISI 304L stainless steel on the austenite grain size

    Energy Technology Data Exchange (ETDEWEB)

    Sabooni, Soheil; Rashtchi, Hamed; Eslami, Abdoulmajid; Karimzadeh, Fathallah; Enayati, Mohammad Hossein; Raeissi, Keyvan; Imani, Reihane Faghih [Isfahan Univ. of Technology, Isfahan (Iran, Islamic Republic of). Dept. of Materials Engineering; Ngan, Alfonso Hing Wan [The Univ. of Hong Kong (China). Dept. of Mechanical Engineering

    2017-07-15

    The corrosion resistance of austenitic stainless steels is known to be hampered by the loss of chromium available for passive surface layer formation as a result of chromium carbide precipitation at austenite grain boundaries during annealing treatments. Although high-temperature annealing can promote carbide dissolution leading to better corrosion resistance, grain coarsening also results, which would lead to poorer mechanical properties. Processing methods to achieve both good corrosion resistance and mechanical properties are thus highly desirable for austenitic stainless steels. In the present study, we show that the corrosion resistance of AISI 304L stainless steel can be improved by grain refinement into the ultrafine-grained regime. Specifically, samples with different austenite grain sizes in the range of 0.65-12 μm were studied by potentiodynamic polarization and electrochemical impedance spectroscopy tests in a 3.5 wt.% NaCl solution. All samples showed a typical passive behavior with similar corrosion potential, but the corrosion current density decreased significantly with decreasing grain size. The results show that the sample with the finest grain size had the best corrosion resistance due to a higher resistance of the passive layer to pitting attacks. This study indicates that grain refinement which improves mechanical properties can also significantly improve the corrosion resistance of AISI 304L stainless steel.

  20. Corrosion behavior of stainless steel weldments in physiological solutions

    Science.gov (United States)

    Farooq, A.; Azam, M.; Deen, K. M.

    2018-01-01

    In this study corrosion behavior of TIG welded 316L stainless steel plates in simulated biological solutions is investigated. The mechanical testing results showed slight decrease in ductility after welding and the fracture surface represented mixed cleavage and inclusions containing dimple structure. The heat affected and weld zone (WZ) demonstrated higher corrosion potential and relatively large pitting tendency than base metal (BM) in both Hank’s and Ringer’s solution. The formation of delta (δ) ferrite in the heat affected and WZ decreased the corrosion resistance as confirmed from potentiodynamic Tafel scans. The decrease in pitting resistance and lower protection tendency of the WZ compared to BM and heat affected zone was also quantified from the cyclic polarization trends.

  1. Comparison of Corrosion Behavior of Low-Alloy Steel Containing Copper and Antimony with 409L Stainless Steel for a Flue Gas Desulfurization System

    Energy Technology Data Exchange (ETDEWEB)

    Park, Sun-Ah; Shin, Su-Bin; Kim, Jung-Gu [Sungkyunkwan University, Suwon (Korea, Republic of)

    2016-07-15

    The corrosion behavior of low alloy steel containing Cu, Sb and 409L stainless steel was investigated for application in the low-temperature section of a flue gas desulfurization (FGD) system. The electrochemical properties were evaluated by potentiodynamic polarization testing and electrochemical impedance spectroscopy (EIS) in 16.9 vol% H{sub 2}SO{sub 4} + 0.35 vol% HCl at 60 ℃. The inclusions in these steels ere identified by electron probe microanalyzer (EPMA). The corrosion products of the steels were analyzed using scanning electron microscope (SEM) with energy dispersive spectroscopy (EDS) and transmission electron microscopy (TEM). The corrosion rate of the low alloy steel containing Cu, Sb was about 100 times lower than that of 409L stainless steel. For stainless steel without passivation, active corrosion behavior was shown. In contrast, in the low alloy steel, the Cu, Sb compounds accumulated on the surface improved the corrosion resistance by suppressing the anodic dissolution reaction.

  2. Evaluation of structural behaviour and corrosion resistant of austenitic AISI 304 and duplex AISI 2304 stainless steel reinforcements embedded in ordinary Portland cement mortars; Evaluacion del comportamiento estructural y de resistencia a la corrosion de armaduras de acero inoxidable austenitico AISI 304 y duplex AISI 2304 embebidas en morteros de cemento Portland

    Energy Technology Data Exchange (ETDEWEB)

    Medina, E.; Cobo, A.; Bastidas, D. M.

    2012-07-01

    The mechanical and structural behaviour of two stainless steels reinforcements, with grades austenitic EN 1.4301 (AISI 304) and duplex EN 1.4362 (AISI 2304) have been studied, and compared with the conventional carbon steel B500SD rebar. The study was conducted at three levels: at rebar level, at section level and at structural element level. The different mechanical properties of stainless steel directly influence the behaviour at section level and structural element level. The study of the corrosion behaviour of the two stainless steels has been performed by electrochemical measurements, monitoring the corrosion potential and the lineal polarization resistance (LPR), of reinforcements embedded in ordinary Portland cement (OPC) mortar specimens contaminated with different amount of chloride over one year time exposure. Both stainless steels specimens embedded in OPC mortar remain in the passive state for all the chloride concentration range studied after one year exposure. (Author) 26 refs.

  3. Corrosion of mild steel and stainless steel by marine Vibrio sp.

    Digital Repository Service at National Institute of Oceanography (India)

    PrabhaDevi; Wagh, A.B.

    Microbially induced corrosion (MIC) of stainless steel and mild steel coupons exposed to media with and without a bacterial culture Vibrio sp. was studied using Scanning Electron Microscope (SEM). Pitting type of corrosion was noticed which was more...

  4. Atmospheric Corrosion Behavior and Mechanism of a Ni-Advanced Weathering Steel in Simulated Tropical Marine Environment

    Science.gov (United States)

    Wu, Wei; Zeng, Zhongping; Cheng, Xuequn; Li, Xiaogang; Liu, Bo

    2017-11-01

    Corrosion behavior of Ni-advanced weathering steel, as well as carbon steel and conventional weathering steel, in a simulated tropical marine atmosphere was studied by field exposure and indoor simulation tests. Meanwhile, morphology and composition of corrosion products formed on the exposed steels were surveyed through scanning electron microscopy, energy-dispersive x-ray spectroscopy and x-ray diffraction. Results indicated that the additive Ni in weathering steel played an important role during the corrosion process, which took part in the formation of corrosion products, enriched in the inner rust layer and promoted the transformation from loose γ-FeOOH to dense α-FeOOH. As a result, the main aggressive ion, i.e., Cl-, was effectively separated in the outer rust layer which leads to the lowest corrosion rate among these tested steels. Thus, the resistance of Ni-advanced weathering steel to atmospheric corrosion was significantly improved in a simulated tropical marine environment.

  5. Poly(aniline) in corrosion resistant coatings

    Energy Technology Data Exchange (ETDEWEB)

    McAndrew, T.P.; Miller, S.A.; Gilicinski, A.G.; Robeson, L.M. [Air Products and Chemicals, Inc., Allentown, PA (United States)

    1996-10-01

    During the past two decades, one of the most active fields of solid-state science has been electrically conductive polymers. These are polymers which are insulators as prepared, but which can be converted to polymers having many or all the properties of a metal, by virtue of appropriate chemical/electrochemical oxidation or reduction. Typically, applications examined for electrically conductive polymers have been in areas such as rechargeable batteries and charge dissipative coatings. Recently it has been reported that poly(aniline), in its electrically conductive, protonated form, shows excellent performance as a coating for preventing the corrosion of carbon steel. The present research has shown that in fact, the non-conductive, unprotonated form of poly(aniline) shows even better performance in corrosion prevention than the conductive form. Moreover, it has been shown that poly(aniline) can be blended with other polymers to improve their corrosion resistance performance (e.g., polyimides), or used as a hardener for epoxides or diisocyanates, to give very good corrosion resistant coatings. Poly(aniline) performance is explained in terms of its ability to form dense, adherent films, and create a basic surface on carbon steel surfaces.

  6. Corrosion resistant neutron absorbing coatings

    Science.gov (United States)

    Choi, Jor-Shan [El Cerrito, CA; Farmer, Joseph C [Tracy, CA; Lee, Chuck K [Hayward, CA; Walker, Jeffrey [Gaithersburg, MD; Russell, Paige [Las Vegas, NV; Kirkwood, Jon [Saint Leonard, MD; Yang, Nancy [Lafayette, CA; Champagne, Victor [Oxford, PA

    2012-05-29

    A method of forming a corrosion resistant neutron absorbing coating comprising the steps of spray or deposition or sputtering or welding processing to form a composite material made of a spray or deposition or sputtering or welding material, and a neutron absorbing material. Also a corrosion resistant neutron absorbing coating comprising a composite material made of a spray or deposition or sputtering or welding material, and a neutron absorbing material.

  7. Corrosion-resistant coating development

    Energy Technology Data Exchange (ETDEWEB)

    Stinton, D.P.; Kupp, D.M.; Martin, R.L. [Oak Ridge National Lab., TN (United States)

    1997-12-01

    SiC-based heat exchangers have been identified as the prime candidate material for use as heat exchangers in advanced combined cycle power plants. Unfortunately, hot corrosion of the SiC-based materials created by alkali metal salts present in the combustion gases dictates the need for corrosion-resistant coatings. The well-documented corrosion resistance of CS-50 combined with its low (and tailorable) coefficient of thermal expansion and low modulus makes CS-50 an ideal candidate for this application. Coatings produced by gelcasting and traditional particulate processing have been evaluated.

  8. Corrosion inhibition in 2.0 M sulfuric acid solutions of high strength maraging steel by aminophenyl tetrazole as a corrosion inhibitor

    Energy Technology Data Exchange (ETDEWEB)

    Sherif, El-Sayed M., E-mail: emsherif@gmail.com [Center of Excellence for Research in Engineering Materials (CEREM), Advanced Manufacturing Institute, King Saud University, PO. Box 800, Al-Riyadh 11421 (Saudi Arabia); National Research Centre (NRC), Electrochemistry and Corrosion Laboratory, Department of Physical Chemistry, National Research Centre (NRC), Dokki, 12622 Cairo (Egypt)

    2014-02-15

    The corrosion of high strength maraging steel after varied immersion times in concentrated solution, 2.0 M, of sulfuric acid has been investigated. The work was also extended to study the effect of 5-(3-aminophenyl)-tetrazole (APTA) on the inhibition of the steel corrosion. The study has been carried out using electrochemical impedance spectroscopy (EIS), potentiodynamic polarization and scanning electron microscope (SEM) along with energy dispersive X-ray analyzer (EDX) investigations. EIS spectra showed that the corrosion and polarization resistances decrease with increasing the immersion time of the steel before measurement and increase in the presence of APTA and the increase of its concentration. Polarization data agreed with the EIS measurements and indicated that the increase of immersion time increases the corrosion of steel by increasing its corrosion current and corrosion rate and lowering its polarization resistance. On the other hand, the addition of APTA and the increase of its concentration minimized the corrosion of steel through decreasing the corrosion current and corrosion rate and increasing the polarization resistance at all exposure test periods. SEM and EDX investigations confirmed that the inhibition of the maraging steel in the 2.0 M H{sub 2}SO{sub 4} solutions is achieved via the adsorption of the APTA molecules onto the steel protecting its surface from being dissolved easily.

  9. Influence of silver additions to type 316 stainless steels on bacterial inhibition, mechanical properties, and corrosion resistance

    DEFF Research Database (Denmark)

    Chiang, Wen-Chi; Tseng, I-Sheng; Møller, Per

    2010-01-01

    Bacterial contamination is a major concern in many areas. In this study, silver was added to type 316 stainless steels in order to obtain an expected bacteria inhibiting property to reduce the occurrence of bacterial contamination. Silver-bearing 316 stainless steels were prepared by vacuum melti...

  10. Effect of alpha/gamma phase ratio on corrosion behavior of dual-phase stainless steels.

    Science.gov (United States)

    Lim, Y J; Reyes, M; Thongthammachat, S; Sukchit, K; Panich, M; Oshida, Y

    1999-01-01

    Dual-phase stainless steels have been developed in order to reduce the nickel content, which is potentially responsible to an allergic reaction when these steels are used as medical or dental applications. In this study, two different dual-phase stainless steels (2205 and Z100) were electrochemically tested to evaluate their corrosion resistance in three corrosive solutions (i.e., synthetic saliva, 0.9% NaCl solution, and Ringer solution). Particularly, an attempt was made to correlate the corrosion resistance to a metallographic parameter, which is, in this study, the alpha/gamma phase ratio. It was concluded that (1) type 2205 stainless steel exhibited excellent corrosion resistance in all three corrosion media; however 2205 stainless steel decreases its corrosion resistance by increasing chloride concentration in tested electrolytes from synthetic saliva through 0.9% NaCl solution to Ringer solution. (2) X-ray diffraction analysis indicated that the alpha/gamma phase ratio of 2205 (1.735) was higher than that of Z100 (0.905). As a result, it is suggested that by increasing the alpha/gamma phase ratio the material shows more corrosion-prone behavior when being subjected to a hostile environment containing higher chloride ion concentration.

  11. Corrosion behavior of Cr/Ni alloy coated ferritic stainless steel in simulated cathodic PEMFC environments

    Energy Technology Data Exchange (ETDEWEB)

    Rendon, M.; Rivas, S.V.; Arriga, L.G.; Orozco, G. [Centro de Investigacion y Desarrollo Tecnologico en Electroquimica, Queretaro (Mexico); Perez-Quiroz, J.T. [Inst. Mexicano del Transporte, Queretaro (Mexico); Porcayo, J. [Inst. de Investigaciones Electricas, Morelos (Mexico)

    2008-07-01

    The bipolar plate in a proton exchange membrane fuel cell (PEMFC) must be corrosion resistant and the interfacial contact resistance (ICR) with the gas diffusion layer must be low. For these reasons, stainless steel with high Cr content is considered to be a viable material for use in bipolar plate construction. This study evaluated the corrosion resistance of ferritic stainless steels 441 and 439, with and without a Cr/Ni coating, under simulated cathodic PEMFC conditions. Steel 441 without coating has a low corrosion current density and can be considered as a candidate material to be used as bipolar plate. The study showed that after the Cr/Ni coating was applied by Thermal Spray Metal method, the corrosion current density increased due to selective dissolution of an alloy element. The corrosion current density of the coatings was higher than the DOE target value, rendering them an unfeasible option to be used in bipolar plates for fuel cell applications. However, previous studies have shown that after the coating was applied, a passivation process improved the corrosion resistance. Although steel 441 appears to be a better candidate than steel 316 because of its lower cost, the behaviour of the Ni-Cr alloys was not satisfactory in corrosive acidic medium. 5 refs.

  12. Corrosion performance tests for reinforcing steel in concrete : technical report.

    Science.gov (United States)

    2009-10-01

    The existing test method used to assess the corrosion performance of reinforcing steel embedded in : concrete, mainly ASTM G 109, is labor intensive, time consuming, slow to provide comparative results, : and can be expensive. However, with corrosion...

  13. Corrosion performance tests for reinforcing steel in concrete : test procedures.

    Science.gov (United States)

    2009-09-01

    The existing test method to assess the corrosion performance of reinforcing steel embedded in concrete, mainly : ASTM G109, is labor intensive, time consuming, slow to provide comparative results, and often expensive. : However, corrosion of reinforc...

  14. Inhibitor for the Corrosion of Mild Steel in H SO

    African Journals Online (AJOL)

    NJD

    electron microscopic studies provided confirmatory evidence of an improved surface condition, due to adsorption, for corrosion protection. KEYWORDS. Terminalia chebula, acid corrosion inhibitor, electrochemical polarization, electrochemical impedance spectroscopy, mild steel. 1. Introduction. Large amounts of sulphuric ...

  15. Progressive Corrosion Study of Metals like Mild Steel, Zinc and Aluminium in an Urban Atmosphere

    Directory of Open Access Journals (Sweden)

    H. K. Kadiya

    2009-01-01

    Full Text Available Corrosion rate (Progressive of mild steel (MS, zinc and aluminum have been determined under outdoor conditions of exposure at Valsad (South Gujarat representing an urban atmosphere. Mild steel (MS, zinc and aluminium plates exposed during November 2005 indicates corrosion rate of 88, 33 and 1.4 mg/sq.dm for one month exposure period and 3668, 968 and 26.1 mg/sq.dm for mild steel, zinc and aluminium respectively for twelve months exposure period. Mild steel panels exposed vertically suffer less corrosion than those exposed at an angle of 45°. The resistivity towards the atmosphere was in the increasing order: mild steel < zinc < aluminium. Corrosion rate of these three metals found more in rainy seasons than the rate of winter and summer season

  16. Improvement of Pitting Corrosion Resistance of Type 316L Stainless Steel by Potentiostatic Removal of Surface MnS Inclusions

    Directory of Open Access Journals (Sweden)

    Nobuyoshi Hara

    2012-01-01

    Full Text Available The beneficial effect of the removal of MnS inclusions on the pitting of stainless steels has been demonstrated in two ways. (1 High-purity Type 316L stainless steel with no inclusions was used as a specimen in the measurement of anodic polarization curves in 0.5 M NaCl and (2 commercial Type 316L stainless steel with MnS and slag-related inclusions was first polarized at different potentials for 30 min in 1 M Na2SO4 of pH 3 and then anodic polarization measurements were taken in 0.5 M NaCl. Pitting did not occur in the passive or transpassive region of the high-purity steel. The polarization treatment dissolved MnS and some oxide inclusions (CaO and SiO2 on the surface of the commercial steel. An increase in pitting potential of the commercial steel was noted after treatment at potentials above 0.2 V. At the same time, the number of current spikes due to metastable pits decreased significantly. These results are more likely due to the beneficial effect of removing MnS inclusions from the steel surface rather than the modification effect of the chemical composition of passive films on the surface.

  17. The effect of organic matter associated with the corrosion products on the corrosion of mild steel in the Arabian Sea

    Digital Repository Service at National Institute of Oceanography (India)

    Bhosle, N.B.; Wagh, A.B.

    the corrosion of mild steel and the temperature and dissolved oxygen of seawater. In contrast to this, the corrosion and mild steel was inversely related to the organic carbon and water extractable carbohydrates associated with the corrosion products of mild...

  18. Corrosion resistance of the welded AISI 316L after various surface treatments

    Directory of Open Access Journals (Sweden)

    Tatiana Liptáková

    2014-01-01

    Full Text Available The main aim of this work is to monitor the surface treatment impact on the corrosion resistance of the welded stainless steel AISI 316L to local corrosion forms. The excellent corrosion resistance of austenitic stainless steel is caused by the existence of stable, thin and well adhering passive layer which quality is strongly influenced by welding. Therefore surface treatment of stainless steel is very important with regard to its local corrosion susceptibility Surfaces of welded stainless steel were treated by various mechanical methods (grinding, garnet blasting. Surface properties were studied by SEM, corrosion resistance was evaluated after exposition tests in chlorides environment using weight and metalographic analysis. The experimental outcomes confirmed that the mechanical finishing has a significant effect on the corrosion behavior of welded stainless steel AISI 316L.

  19. Intergranular Corrosion Mechanism of Slightly-sensitized and UNSM-treated 316L Stainless Steel

    Energy Technology Data Exchange (ETDEWEB)

    Lee, J. H.; Kim, K. T.; Kim, Y. S. [Andong National University, Andong (Korea, Republic of); Pyoun, Y. S. [Sun Moon University, Asan (Korea, Republic of)

    2016-10-15

    316L stainless steels have been widely used in many engineering fields, because of their high corrosion resistance and good mechanical properties. However, welding or aging treatment may induce intergranular corrosion and stress corrosion cracking etc. Since these types of corrosion are closely related to the formation of chromium carbide in grain boundaries, the alloys are controlled by methods such as the lowering of carbon content, solution heat treatment. This work focused on the intergranular corrosion mechanism of slightly-sensitized and Ultrasonic Nano-crystal Surface Modification (UNSM)-treated 316L stainless steel. Samples were sensitized for 1, 5, and 48 hours at 650 ℃ in N{sub 2} gas atmosphere. Subsequently UNSM treatments were carried out on the surface of the samples. The results were discussed on the basis of the sensitization by chromium carbide and carbon segregation, the residual stress and grain refinement. Even though chromium carbide was not precipitated, the intergranular corrosion rate of 316L stainless steel was drastically increased with aging time, and it was confirmed that the increased intergranular corrosion rate of slightly-sensitized (not carbide formed) 316L stainless steel was due to the carbon segregation along the grain boundaries. However, UNSM treatment improved the intergranular corrosion resistance of aged stainless steels, and its improvement was due to the reduction of carbon segregation and the grain refinement of the outer surface, including the introduction of compressive residual stress.

  20. Corrosion of Steel in Concrete, Part I – Mechanisms

    DEFF Research Database (Denmark)

    Küter, André; Møller, Per; Geiker, Mette Rica

    2006-01-01

    prematurely. Reinforcement corrosion is identified to be the foremost cause of deterioration. Steel in concrete is normally protected by a passive layer due the high alkalinity of the concrete pore solution; corrosion is initiated by neutralization through atmospheric carbon dioxide and by ingress...... of depassivation ions, especially chloride ions. The background and consequences of deterioration of reinforced concrete structures caused by steel corrosion are summarized. Selected corrosion mechanisms postulated in the literature are briefly discussed and related to observations. The key factors controlling...... initiation and propagation of corrosion of steel in concrete are outlined....

  1. Evaluation of Corrosion Performance of Titanium/Steel Joint Brazed by Cu-Based Filler Metal

    Science.gov (United States)

    Elrefaey, A.; Wojarski, L.; Tillmann, W.

    2012-05-01

    Furnace vacuum brazing has been employed to join commercially pure titanium and low carbon steel using copper-based filler metal with the composition of Cu-10.6Mn-1.9Ni, at.%. Three different brazing temperatures 930, 970, and 1000 °C and a holding time of 15 min were studied and evaluated. The corrosion behavior of the joint in 0.1 M sulfuric acid was investigated using immersion and electrochemical tests. Measurements of corrosion potential, corrosion current density, corrosion rate, polarization resistance, weight loss, and morphology of corrosion attack were used in this study. Experimental results showed that severe corrosion attack of the steel side at the interfacial area is clearly observed. Despite the difference in corrosion rate values obtained by electrochemical and weight loss measurements, the trend of results was identical to a large extent. Corrosion resistance of the joint showed a general tendency to increase with rising brazing temperature. The lowest corrosion rate was obtained for the couple bonded at 1000 °C. Meanwhile, at the lowest joining temperature of 930 °C, corrosion rate showed a higher value. The results of joints corrosion resistance were attributed to the difference in microstructure features and chemical analysis.

  2. Recent Natural Corrosion Inhibitors for Mild Steel: An Overview

    Directory of Open Access Journals (Sweden)

    Marko Chigondo

    2016-01-01

    Full Text Available Traditionally, reduction of corrosion has been managed by various methods including cathodic protection, process control, reduction of the metal impurity content, and application of surface treatment techniques, as well as incorporation of suitable alloys. However, the use of corrosion inhibitors has proven to be the easiest and cheapest method for corrosion protection and prevention in acidic media. These inhibitors slow down the corrosion rate and thus prevent monetary losses due to metallic corrosion on industrial vessels, equipment, or surfaces. Inorganic and organic inhibitors are toxic and costly and thus recent focus has been turned to develop environmentally benign methods for corrosion retardation. Many researchers have recently focused on corrosion prevention methods using green inhibitors for mild steel in acidic solutions to mimic industrial processes. This paper provides an overview of types of corrosion, corrosion process, and mainly recent work done on the application of natural plant extracts as corrosion inhibitors for mild steel.

  3. Corrosion resistant PEM fuel cell

    Science.gov (United States)

    Li, Y.; Meng, W.J.; Swathirajan, S.; Harris, S.J.; Doll, G.L.

    1997-04-29

    The present invention contemplates a PEM fuel cell having electrical contact elements (including bipolar plates/septums) comprising a titanium nitride coated light weight metal (e.g., Al or Ti) core, having a passivating, protective metal layer intermediate the core and the titanium nitride. The protective layer forms a barrier to further oxidation/corrosion when exposed to the fuel cell`s operating environment. Stainless steels rich in Cr, Ni, and Mo are particularly effective protective interlayers. 6 figs.

  4. [Corrosion of stainless steel 201, 304 and 316L in the simulated sewage pipes reactor].

    Science.gov (United States)

    Bao, Guo-Dong; Zuo, Jian-E; Wang, Ya-Jiao; Gan, Li-Li

    2014-08-01

    The corrosion behavior of stainless steel 201, 304 and 316L which would be used as sewer in-situ rehabilitation materials was studied in the simulated sewage pipes reactor. The corrosion potential and corrosion rate of these three materials were studied by potentiodynamic method on the 7th, 14th, 21st, 56th day under two different conditions which were full immersion condition or batch immersion condition with a 2-day cycle. The electrode process was studied by Electrochemical Impedance Spectroscopy (EIS) on the 56th day. The microstructure and composition of the corrosion pitting were analyzed by Scanning Electron Microscope (SEM) and Energy Dispersive Spectrometer (EDS) on the 56th day. The results showed that 304 and 316L had much better corrosion resistance than 201 under both conditions. 304 and 316L had much smaller corrosion rate than 201 under both conditions. The corrosion resistance of all three kinds of stainless steel under the batch immersion condition was much better than those under the full immersion condition. The corrosion rate of all three kinds of stainless steel under the batch immersion condition was much smaller than those under the full immersion condition. Point pitting corrosion was formed on the surfaces of 304 and 316L. In comparison, a large area of corrosion was formed in the surface of 201.

  5. Atmospheric corrosion data of weathering steels. A review

    OpenAIRE

    Morcillo, Manuel; Chico, Belén; Cano, H.; Fuente, Daniel de la

    2013-01-01

    Extensive information on the atmospheric corrosion of weathering steel has been published in the scientific literature. The contribution of the present work is to provide a bibliographic review of the reported information, which mostly concerns the weathering steel ASTM A-242. This review addresses issues such as rust layer stabilisation times, steady-state steel corrosion rates, and situations where the use of unpainted weathering steel is feasible. It also analyses the effect of exposure co...

  6. General and Localized Corrosion of Austenitic And Borated Stainless Steels in Simulated Concentrated Ground Waters

    Energy Technology Data Exchange (ETDEWEB)

    Estill, J C; Rebak, R B; Fix, D V; Wong, L L

    2004-03-11

    Boron containing stainless steels are used in the nuclear industry for applications such as spent fuel storage, control rods and shielding. It was of interest to compare the corrosion resistance of three borated stainless steels with standard austenitic alloy materials such as type 304 and 316 stainless steels. Tests were conducted in three simulated concentrated ground waters at 90 C. Results show that the borated stainless were less resistant to corrosion than the witness austenitic materials. An acidic concentrated ground water was more aggressive than an alkaline concentrated ground water.

  7. General and Localized corrosion of Austenitic and Borated Stainless Steels in Simulated Concentrated Ground Waters

    Energy Technology Data Exchange (ETDEWEB)

    D. Fix; J. Estill; L. Wong; R. Rebak

    2004-05-28

    Boron containing stainless steels are used in the nuclear industry for applications such as spent fuel storage, control rods and shielding. It was of interest to compare the corrosion resistance of three borated stainless steels with standard austenitic alloy materials such as type 304 and 316 stainless steels. Tests were conducted in three simulated concentrated ground waters at 90 C. Results show that the borated stainless were less resistant to corrosion than the witness austenitic materials. An acidic concentrated ground water was more aggressive than an alkaline concentrated ground water.

  8. Improved corrosion and wear resistance of laser alloyed Zn-Sn-Ti composite coatings on UNS G10150 steel in 0.5 M H2SO4 solution

    CSIR Research Space (South Africa)

    Fatoba, OS

    2016-03-01

    Full Text Available Surface deterioration by corrosion is one of the complications associated with ageing facilities and components especially under some service environments. The research work examines the corrosion behavior of laser alloyed UNS-G10150 steel; coatings...

  9. Corrosion Behavior and Oxide Film Formation of T91 Steel under Different Water Chemistry Operation Conditions

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, D. Q.; Shi, C.; Li, J.; Gao, L. X. [Shanghai University of Electric Power, Shanghai (China); Lee, K. Y. [Dalian University of Technology, Dalian (China)

    2017-02-15

    The corrosion behavior of a ferritic/martensitic steel T91 exposed to an aqueous solution containing chloride and sulfate ions is investigated depending on the stimulated all-volatile treatment (AVT) and under oxygenated treatment (OT) conditions. The corrosion of T91 steel under OT condition is severe, while the corrosion under AVT condition is not. The co-existence of chloride and sulfate ions has antagonistic effect on the corrosion of T91 steel in both AVT and OT conditions. Unlike to corrosion resistance in the aqueous solution, OT pretreatment provides T91 steel lower oxidation-resistance than VAT pretreatment. From scanning electron microscopy/energy dispersive X-ray spectroscopy (SEM/EDS) and X-ray diffraction (XRD) analysis, the lower corrosion resistance in the aqueous solution by VAT conditions possibly is due to the formation of pits. In addition, the lower oxidation resistance of T91 steel pretreated by OT conditions is explained as follows: the cracks formed during the immersion under OT conditions accelerated peeling-off rate of the oxide film.

  10. Marine corrosion of mild steel at Lumut, Perak

    Science.gov (United States)

    Ting, Ong Shiou; Potty, Narayanan Sambu; Liew, Mohd. Shahir

    2012-09-01

    The corrosion rate of structural steels in the adverse marine and offshore environments affects the economic interest of offshore structures since the loss of steel may have significant impact on structural safety and performance. With more emphasis to maintain existing structures in service for longer time and hence to defer replacement costs, there is increasing interest in predicting corrosion rate at a given location for a given period of exposure once the protection coating or cathodic protection is lost. The immersion depth, salinity, steel composition and water pollution will be taken into account. Various corrosion allowances are prescribed for structural members by different standards. There are no studies to determine the appropriate corrosion allowance for steel structures in marine environment in Malaysia. The objectives of the research are to determine the nature and rate of corrosion in mm/year for steel structures in marine environment. It also tries to identify whether the corrosion rate is affected by differences in the chemical composition of the steels, and microalgae. Two sets of corrosion coupons of Type 3 Steel consisting of mild steel were fabricated and immersed in seawater using steel frames. The corrosion rate of the coupon in mm/ per year is estimated based on the material weight loss with time in service. The results are compared with recommendations of the code.

  11. Corrosion Behavior of Carbon Steel in Synthetically Produced Oil Field Seawater

    Directory of Open Access Journals (Sweden)

    Subir Paul

    2014-01-01

    Full Text Available The life of offshore steel structure in the oil production units is decided by the huge corrosive degradation due to SO42-, S2−, and Cl−, which normally present in the oil field seawater. Variation in pH and temperature further adds to the rate of degradation on steel. Corrosion behavior of mild steel is investigated through polarization, EIS, XRD, and optical and SEM microscopy. The effect of all 3 species is huge material degradation with FeSx and FeCl3 and their complex as corrosion products. EIS data match the model of Randle circuit with Warburg resistance. Addition of more corrosion species decreases impedance and increases capacitance values of the Randle circuit at the interface. The attack is found to be at the grain boundary as well as grain body with very prominent sulphide corrosion crack.

  12. Assessing the effect of cement-steel interface on well casing corrosion in aqueous CO2 environments

    Energy Technology Data Exchange (ETDEWEB)

    Han, Jiabin [Los Alamos National Laboratory; Carey, James W [Los Alamos National Laboratory; Zhang, Jinsuo [Los Alamos National Laboratory

    2010-01-01

    CO{sub 2} leakage is a critical safety concern for geologic storage. In wellbore environments, important leakage paths include the rock-cement and cement-casing interfaces. If the cement-casing interface is filled with escaping CO{sub 2}, the well casing directly contacts the CO{sub 2}. This can cause severe corrosion in the presence of water. This paper studies the effect of steel-cement interface gaps, ranging from 1 mm to 0 um, on casing corrosion. Corrosion kinetics were measured employing electrochemical techniques including linear polarization resistance, open circuit potential and electrochemical impedance spectroscopy. The experimental results showed that the corrosion of steel is not significant where the gap between steel and cement is small ({le} 100 {micro}m). Corrosion rates are controlled by the diffusion of corrosive species (H{sub 2}CO{sub 3} and H{sup +}) along the interface. In contrast, steel corrosion is severe in a broad gap where the corrosion process is limited only by the reaction kinetics of steel and corrosive species. The threshold leading to severe corrosion in terms of the cement-steel interface size (100 {micro}m) was determined. Our research clarifies a corrosion scenario at the cement-steel interface. Casing steel corrosion is initiated when attacked by corrosive species at the cement-steel interface. For relatively tight interfaces, this results in a slow thinning of the casing and expansion of the interface width. If the gap increases beyond the critical threshold size, the corrosion rate increases significantly, and a potentially damaging cycle of corrosion and interface expansion is developed.

  13. The influence of molybdenum on stress corrosion in Ultra Low Carbon Steels with copper addition

    Directory of Open Access Journals (Sweden)

    M. Mazur

    2010-07-01

    Full Text Available The influence of molybdenum content on the process of stress corrosion of ultra-low carbon structural steels with the addition of copper HSLA (High Strength Low Alloy was analyzed. The study was conducted for steels after heat treatment consisting of quenching andfollowing tempering at 600°C and it was obtained microstructure of the tempered martensite laths with copper precipitates and the phaseLaves Fe2Mo type. It was found strong influence of Laves phase precipitate on the grain boundaries of retained austenite on rate anddevelopment of stress corrosion processes. The lowest corrosion resistance was obtained for W3 steel characterized by high contents ofmolybdenum (2.94% Mo which should be connected with the intensity precipitate processes of Fe2Mo phase. For steels W1 and W2which contents molybdenum equals 1.02% and 1.88%, respectively were obtained similar courses of corrosive cracking.

  14. Influence of thermal treatment on structure and corrosion properties of high manganese triplex steels

    Directory of Open Access Journals (Sweden)

    S. Lasek

    2013-10-01

    Full Text Available In this paper corrosion properties of X70MnAl28-9 TRIPLEX steel were tested after hot rolling and subsequent aging at 500 °C for 6, 30 and 60 min. and at 600 °C for the same times. For comparison related steels(X100MnAl28-12, X70Mn22, C20 were also used. The microstructure wascharacterized by light microscopy, SEM, energy disperse Xray microanalysis. The corrosion behaviour of steels wasexamined by light and scanning electron microscopy, electrochemical techniques (potenciodynamic polarization method, linear polarization, using NaCl and H2SO4 water solutions, salt spray test and gravimetric method. Aging has relatively small influence on corrosion resistance of X70MnAl28-9 steel. The localized corrosion in relation to structure and phases is discussed and compared in terms of dissolution, pitting and changes inchemical composition.

  15. Microbially induced corrosion of carbon steel in deep groundwater environment

    Directory of Open Access Journals (Sweden)

    Pauliina eRajala

    2015-07-01

    Full Text Available The metallic low and intermediate level radioactive waste generally consists of carbon steel and stainless steels. The corrosion rate of carbon steel in deep groundwater is typically low, unless the water is very acidic or microbial activity in the environment is high. Therefore, the assessment of microbially induced corrosion of carbon steel in deep bedrock environment has become important for evaluating the safety of disposal of radioactive waste. Here we studied the corrosion inducing ability of indigenous microbial community from a deep bedrock aquifer. Carbon steel coupons were exposed to anoxic groundwater from repository site 100 m depth (Olkiluoto, Finland for periods of three and eight months. The experiments were conducted at both in situ temperature and room temperature to investigate the response of microbial population to elevated temperature. Our results demonstrate that microorganisms from the deep bedrock aquifer benefit from carbon steel introduced to the nutrient poor anoxic deep groundwater environment. In the groundwater incubated with carbon steel the planktonic microbial community was more diverse and 100-fold more abundant compared to the environment without carbon steel. The betaproteobacteria were the most dominant bacterial class in all samples where carbon steel was present, whereas in groundwater incubated without carbon steel the microbial community had clearly less diversity. Microorganisms induced pitting corrosion and were found to cluster inside the corrosion pits. Temperature had an effect on the species composition of microbial community and also affected the corrosion deposits layer formed on the surface of carbon steel.

  16. Microbially induced corrosion of carbon steel in deep groundwater environment.

    Science.gov (United States)

    Rajala, Pauliina; Carpén, Leena; Vepsäläinen, Mikko; Raulio, Mari; Sohlberg, Elina; Bomberg, Malin

    2015-01-01

    The metallic low and intermediate level radioactive waste generally consists of carbon steel and stainless steels. The corrosion rate of carbon steel in deep groundwater is typically low, unless the water is very acidic or microbial activity in the environment is high. Therefore, the assessment of microbially induced corrosion of carbon steel in deep bedrock environment has become important for evaluating the safety of disposal of radioactive waste. Here we studied the corrosion inducing ability of indigenous microbial community from a deep bedrock aquifer. Carbon steel coupons were exposed to anoxic groundwater from repository site 100 m depth (Olkiluoto, Finland) for periods of 3 and 8 months. The experiments were conducted at both in situ temperature and room temperature to investigate the response of microbial population to elevated temperature. Our results demonstrate that microorganisms from the deep bedrock aquifer benefit from carbon steel introduced to the nutrient poor anoxic deep groundwater environment. In the groundwater incubated with carbon steel the planktonic microbial community was more diverse and 100-fold more abundant compared to the environment without carbon steel. The betaproteobacteria were the most dominant bacterial class in all samples where carbon steel was present, whereas in groundwater incubated without carbon steel the microbial community had clearly less diversity. Microorganisms induced pitting corrosion and were found to cluster inside the corrosion pits. Temperature had an effect on the species composition of microbial community and also affected the corrosion deposits layer formed on the surface of carbon steel.

  17. Corrosion protection of steel in ammonia/water heat pumps

    Science.gov (United States)

    Mansfeld, Florian B.; Sun, Zhaoli

    2003-10-14

    Corrosion of steel surfaces in a heat pump is inhibited by adding a rare earth metal salt to the heat pump's ammonia/water working fluid. In preferred embodiments, the rare earth metal salt includes cerium, and the steel surfaces are cerated to enhance the corrosion-inhibiting effects.

  18. Atmospheric Corrosion on Steel Studied by Conversion Electron Moessbauer Spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Nakanishi, Akio; Kobayashi, Takayuki [Shiga University of Medical Science, Department of Physics (Japan)

    2004-12-15

    In order to investigate initial products on steel by atmospheric corrosion, conversion electron Moessbauer measurements were carried out at temperatures between 15 K and room temperature. From the results obtained at low temperatures, it was found that the corrosion products on steel consisted of ferrihydrite.

  19. Effect of debonded interfaces on corrosion of mild steel composites in supercritical CO2-saturated brines

    Energy Technology Data Exchange (ETDEWEB)

    John, Han [Los Alamos National Laboratory; Carey, James W [Los Alamos National Laboratory; Zhang, Jinsuo [Los Alamos National Laboratory

    2010-10-07

    The geologic sequestration of CO{sub 2} is a proposed method to limit greenhouse gas emissions and has been the subject of many studies in the last decade. Wellbore systems achieve isolation of the storage reservoir through a combination of steel (generally carbon steel) and Portland cement. CO{sub 2} leakage along the steel-cement interface has the potential to accelerate corrosion. We conduct experiments to assess the corrosion risk at cement-steel interface under in situ wellbore conditions. Wellbore interfaces were simulated by assemblies constructed of J55 mild steel and Portland class G (Epoxy was used in this study to separate) cement and corrosion was investigated in supercritical CO{sub 2} saturated brines, (NaCl = 1 wt%) at T = 50 C, pCO{sub 2} = 1200 psi with interface gap size = 100 {micro}m and {infinity} (open surface). The experiments were carried out in a high-pressure, 1.8 L autoclave. The corrosion kinetics were measured employing electrochemical techniques including linear polarization resistance and electrochemical impedance spectroscopy techniques. The corrosion scales were analyzed using secondary electron microscopy, back scattering electron microscopy, energy dispersive spectroscopy and x-ray diffraction. Corrosion rates decreased as time with or without interface gap. In this case corrosion rates are controlled by scale protectivity through the interface gap. Scaled steel corrosion rates were two orders of magnitude less compared with fresh steel. The corrosion scale is pseudo crystalline at the open interface. Well-crystallized scale was observed at interface gap sizes 100 {micro}m. All corrosion scales were composed of iron carbonates.

  20. Application of Self Assembled 6-aminohexanol layers for corrosion protection of 304 stainless steel surface

    Energy Technology Data Exchange (ETDEWEB)

    Yu Fei [Institute of Materials Science and Engineering, Ocean University of China, Qingdao 266100 (China); Chen Shougang, E-mail: sgchen2000@yahoo.com.cn [Institute of Materials Science and Engineering, Ocean University of China, Qingdao 266100 (China); Li Houmin; Yang Lejiao [Institute of Materials Science and Engineering, Ocean University of China, Qingdao 266100 (China); Yin Yansheng [Institute of Marine Materials Science and Engineering, Shanghai Maritime University, Shanghai 200135 (China)

    2012-05-31

    Grafting of 6-aminohexanol onto a 304 stainless steel substrate was performed with the assistance of polydopamine self assembly. The surface structure of the films was characterized using optical and scanning electron microscopy and X-ray energy dispersive spectroscopy confirmed the establishment of organic films. The corrosion resistance properties were characterized using the electrochemical impedance spectroscopy and potentiodynamic polarization curve measurements. Enhanced corrosion resistance performance was mainly ascribed to the compact film structure and the blocking characteristics against electron transfer of the modified 304 stainless steel substrate. - Highlights: Black-Right-Pointing-Pointer Organic layers for corrosion protection of 304 stainless steel (SS) surface. Black-Right-Pointing-Pointer Bio-inspired self assembly of polydopamine/composite films. Black-Right-Pointing-Pointer 6-aminohexanol membrane synthesized on polydopamine modified SS surface. Black-Right-Pointing-Pointer An efficiency route for improving corrosion protection.

  1. Significance of coplanar macrocells to corrosion in concrete-embedded steel

    Energy Technology Data Exchange (ETDEWEB)

    Rodriguez, P. [Univ. Autonoma de Nuevo Leon (Mexico); Ramirez, E. [Inst. de Investigacion Tecnologica Industrial y de Normas Tecnicas, Lima (Peru); Feliu, S.; Gonzalez, J.A. [Centro Nacional de Investigaciones Metalurgicas, Madrid (Spain); Lopez, W. [CEMEX, S.A. Monterrey (Mexico)

    1999-03-01

    The influence of microcells and galvanic macrocells on the corrosion kinetics of concrete-embedded steel was investigated experimentally. Nine stainless steel/carbon steel coplanar macrocouples in cathodic-to-anodic ratios of 0.02 to 50 were cast in concrete slabs made from cement, sand, and water in a 1:3:0:5 proportion plus 2% calcium chloride (CaCl{sub 2}) per cement weight. Corrosion potential (E{sub corr}), galvanic current (i{sub g}), polarization resistance (R{sub p}), and impedance measurements from 100 kHz to 0.01 Hz were made for the two metals, coupled and uncoupled. i{sub g} data provided by a zero resistance ammeter led to potentially underestimated corrosion rates for anodic areas, whereas R{sub p} measurements provided fairly reliable corrosion rates. Macrocells polarized anodic areas very slightly at points where an anodic and a cathodic process took place simultaneously.

  2. Microbiological Corrosion in Low Carbon Steels

    Directory of Open Access Journals (Sweden)

    O. Medina–Custodio

    2009-01-01

    Full Text Available The Microbiologically Induced Corrosion affects several industries, such as oil industry where it is estimated that 20% to 30% pipes failures are related with microorganism . The chemical reactions generate ions transfer, this validate the use of electrochemical techniques for its analysis. Coupons submerged in a nutritional medium with presence and absence of three different microorganisms during two periods, 48 hours and 28 days we restudied. Polarization resistance (Rp and Electrochemical Impedance Spectroscopy (EIS techniques we re applied to determine the corrosivity of the systems. The results show a greater corrosive effect of abiotic system, this indicates a microorganisms protection effect to the metal, opposite to the first hypothesis. This result was ratified observing surfaces coupons by using Scanning Electron Microscopy (SEM technique. A possible mechanism based on Evans – Tafel graph is proposed to explain inhibitor microorganism effect.

  3. Marine atmospheric corrosion of carbon steels

    Directory of Open Access Journals (Sweden)

    Morcillo, Manuel

    2015-06-01

    Full Text Available Basic research on marine atmospheric corrosion of carbon steels is a relatively young scientific field and there continue to be great gaps in this area of knowledge. The presence of akaganeite in the corrosion products that form on steel when it is exposed to marine atmospheres leads to a notable increase in the corrosion rate. This work addresses the following issues: (a environmental conditions necessary for akaganeite formation; (b characterisation of akaganeite in the corrosion products formed; (c corrosion mechanisms of carbon steel in marine atmospheres; (d exfoliation of rust layers formed in highly aggressive marine atmospheres; (e long-term corrosion rate prediction; and (f behaviour of weathering steels. Field research has been carried out at Cabo Vilano wind farm (Camariñas, Galicia in a wide range of atmospheric salinities and laboratory work involving the use of conventional atmospheric corrosion techniques and near-surface and bulk sensitive analytical techniques: scanning electron microscopy (SEM/energy dispersive spectrometry (EDS, X-ray diffraction (XRD, Mössbauer spectroscopy and SEM/μRaman spectroscopy.La investigación fundamental en corrosión atmosférica marina de aceros al carbono es un campo científico relativamente joven que presenta grandes lagunas de conocimiento. La formación de akaganeíta en los productos de corrosión que se forman sobre el acero cuando se expone a atmósferas marinas conduce a un incremento notable de la velocidad de corrosión. En el trabajo se abordan las siguientes cuestiones: (a condiciones ambientales necesarias para la formación de akaganeíta, (b caracterización de la akaganeíta en los productos de corrosión formados, (c mecanismos de corrosión del acero al carbono en atmósferas marinas, (d exfoliación de las capas de herrumbre formadas en atmósferas marinas muy agresivas, (e predicción de la velocidad de corrosión a largo plazo, y (f comportamiento de aceros patinables. La

  4. Study on corrosion simulation device for marine structural steel

    Indian Academy of Sciences (India)

    A corrosion simulation device was studied using offshore long scale hanging specimens. An Ni–Cu–P steel specimen was studied by analysing its corrosion products and corrosion types. The appearance of the samples and the surface of the metallic substrate after the removal of the rust layer produced by these two ...

  5. Study on corrosion simulation device for marine structural steel

    Indian Academy of Sciences (India)

    Unknown

    †Also at Graduate School of the Chinese Academy of Sciences, Beijing 100039, China. MS received 9 January 2003. Abstract. A corrosion simulation device was studied using offshore long scale hanging specimens. An Ni–. Cu–P steel specimen was studied by analysing its corrosion products and corrosion types.

  6. Monitoring Techniques for Microbially Influenced Corrosion of Carbon Steel

    DEFF Research Database (Denmark)

    Hilbert, Lisbeth Rischel

    2000-01-01

    Microbially influenced corrosion (MIC) of carbon steel may occur in media with microbiological activity of especially sulphate-reducing bacteria, e.g. on pipelines buried in soil and on marine structures. MIC of carbon steel must be monitored on-line in order to provide an efficient protection...... and control the corrosion. A number of monitoring techniques is industrially used today, and the applicability and reliability of these for monitoring MIC is evaluated. Coupons and ER are recommended as necessary basic techniques even though localised corrosion rate cannot be measured. FSM measures general...... corrosion and detects localised corrosion, but the sensitivity is not high enough for monitoring initiation of pitting and small attacks. Electrochemical techniques as LPR and EIS give distorted data and unreliable corrosion rates, when biofilm and corrosion products cover the steel surface. However, EIS...

  7. Effect of chromium on the corrosion behavior of low alloy steel in sulfuric acid

    Science.gov (United States)

    Park, Sun-Ah; Lee, Seung-Hwan; Kim, Jung-Gu

    2012-12-01

    The effects of a chromium (Cr) addition on the corrosion resistance of low alloy steel used in flue gas desulfurization systems were examined by electrochemical (potentiodynamic polarization tests, linear polarization measurements and electrochemical impedance spectroscopy) and weight loss measurements in a 10 wt% H2SO4 solution at room temperature. All measurements revealed a decrease in corrosion rate with increasing Cr content. SEM, EPMA and XPS examinations of the corroded surfaces after the immersion test indicated that 0.6% Cr addition decreased corrosion damage to the steels because protective Cr oxides formed in all the rust layers and Fe oxides dominated over Fe sulphate compounds in the inner rust layers.

  8. Reliability of Electrochemical Techniques for Determining Corrosion Rates on Carbon Steel in Sulfide Media

    DEFF Research Database (Denmark)

    Hilbert, Lisbeth Rischel; Hemmingsen, T.; Nielsen, Lars Vendelbo

    2007-01-01

    if the biofilm in combination with ferrous sulfide corrosion products cover the steel surface. Corrosion rates can be overestimated by a factor of 10 to 100 with electrochemical techniques - both by linear polarization resistance (LPR) and electrochemicel impedance spectroscopy (EIS). Oxygen entering the system......Effects of film formation on carbon steel in hydrogen sulfide (H2S) media may corrupt corrosion rate monitoring by electrochemical techniques. Electrochemical data from H2S solutions, biological sulfide media, and natural sulfide containing geothermal water have been collected, and the process...

  9. Effect of Nitrite Inhibitor on the Macrocell Corrosion Behavior of Reinforcing Steel

    Directory of Open Access Journals (Sweden)

    Zhonglu Cao

    2015-01-01

    Full Text Available The effect of nitrite ions on the macrocell corrosion behavior of reinforcing steel embedded in cement mortar was investigated by comparing and analyzing the macrocell corrosion current, macrocell polarization ratios, and slopes of anodic and cathodic steels. Based on the experimental results, the relationship between macrocell potential difference and macrocell current density was analyzed, and the mechanism of macrocell corrosion affected by nitrite ions was proposed. The results indicated that nitrite ions had significant impact on the macrocell polarization ratios of cathode and anode. The presence of nitrite could reduce the macrocell current by decreasing the macrocell potential difference and increasing the macrocell polarization resistance of the anode.

  10. Microbiologically Influenced Corrosion of 2707 Hyper-Duplex Stainless Steel by Marine Pseudomonas aeruginosa Biofilm

    OpenAIRE

    Huabing Li; Enze Zhou; Dawei Zhang; Dake Xu; Jin Xia; Chunguang Yang; Hao Feng; Zhouhua Jiang; Xiaogang Li; Tingyue Gu; Ke Yang

    2016-01-01

    Microbiologically Influenced Corrosion (MIC) is a serious problem in many industries because it causes huge economic losses. Due to its excellent resistance to chemical corrosion, 2707 hyper duplex stainless steel (2707 HDSS) has been used in the marine environment. However, its resistance to MIC was not experimentally proven. In this study, the MIC behavior of 2707 HDSS caused by the marine aerobe Pseudomonas aeruginosa was investigated. Electrochemical analyses demonstrated a positive shift...

  11. CORROSION RESISTANT JACKETED METAL BODY

    Science.gov (United States)

    Brugmann, E.W.

    1958-08-26

    Reactor faul elements of the elongated cylindrical type which are jacketed in a corrosion resistant material are described. Each feel element is comprised of a plurality of jacketed cylinders of fissionable material in end to end abutting relationship, the jackets being welded together at their adjoining ends to retain the individual segments together and seat the interior of the jackets.

  12. Pitting corrosion in austenitic and duplex stainless steels

    Energy Technology Data Exchange (ETDEWEB)

    Jargelius-Pettersson, R.F.A.; Pires Duarte, B.; Duchamp, G. [Swedish Inst. for Metals Research, Stockholm (Sweden)

    1998-12-31

    Various electrochemical methods have been used to evaluate the pitting corrosion resistance of two austenitic and two duplex stainless steels. Testing has been performed in a purpose-built electrochemical cell which permits simultaneous evaluation of twelve specimens and in which crevice corrosion is avoided using a flushed-port design. A potential-independent critical pitting temperature below which pitting is not observed has been evaluated from potentiodynamic measurements, pitting potentials and pit induction times have also been evaluated at various temperatures above this critical value. Statistical treatment of the data has been used to evaluate the elementary pitting probability and pit generation rates. The good differentiation obtained using a large number of pitting potential measurements has permitted quantitative evaluation of the effect of testing and alloy variables. The surface finish is shown to have a significant effect on measured pitting resistance, as has the passivation time between specimen preparation and testing. The decrease in pitting resistance as a result of short-term sensitising heat treatment of the steels has also been evaluated. (orig.) 9 refs.

  13. Steel fibre corrosion in cracks:durability of sprayed concrete

    OpenAIRE

    Nordström, Erik

    2000-01-01

    Steel fibre reinforced sprayed concrete is common practice for permanent linings in underground construction. Today there is a demand on "expected technical service life" of 120 years. Thin steel fibres could be expected to discontinue carrying load fast with a decrease of fibre diameter caused by corrosion, especially in cracks. The thesis contains results from inspections on existing sprayed concrete structures and a literature review on corrosion of steel fibres in cracked concrete. To stu...

  14. Pitting corrosion OF Cr-Ni-Mo stainless steel in presence of MoO42- chloride solution

    OpenAIRE

    Zatkalíková, Viera; Markovičová, Lenka

    2014-01-01

    The submitted manuscript focuses on the pitting corrosion of AISI 316Ti steel in very aggressive chloride solution with added sodium molybdate, which is considered the effective inhibitor of the local corrosion of stainless steels. The effect of molybdate on resistance of AISI 316Ti steel to pitting was tested in 5% ferric chloride solution by 24-hour exposition immersion tests. The tests were carried out at room temperature in the absence and presence of various molybdate concentrations (0.0...

  15. Corrosion susceptibility of steel drums to be used as containers for intermediate level nuclear waste

    Directory of Open Access Journals (Sweden)

    Duffó G.

    2013-07-01

    Full Text Available The present work is a study of the corrosion susceptibility of steel drums in contact with cemented ion-exchange resins contaminated with different types and concentrations of aggressive species. A special type of specimen was manufactured to simulate the cemented ion-exchange resins in the drum. The evolution of the corrosion potential and the corrosion rate of the steel, as well as the electrical resistivity of the matrix were monitored over a time period of 900 days. The aggressive species studied were chloride ions (the main ionic species of concern and sulphate ions (produced during radiolysis of the cationic exchange-resins after cementation. The work was complemented with an analysis of the corrosion products formed on the steel in each condition, as well as the morphology of the corrosion products. When applying the results obtained in the present work to estimate the corrosion depth of the steel drumscontaining the cemented radioactive waste after a period of 300 years (foreseen durability of the Intermediate Level Radioactive Waste facility in Argentina , it is found that in the most unfavourable case (high chloride contamination, the corrosion penetration will be considerably lower than the thickness of the wall of the steel drums.

  16. Analysis Of Effect Of Mechanical Properties Of Aluminum Alloy Addition Of Zinc Corrosion Resistance Of Carbon Steel A325 Bolts Process Of Hot Dip Galvanizing

    Directory of Open Access Journals (Sweden)

    Ery Diniardi

    2015-08-01

    Full Text Available The world oil industry are common in offshore areas that are included in a corrosive environment so that the low-carbon steel bolts A325 will gradually corroded. Therefore an alternative that can be done to reduce the corrosion rate that is by coating with a Hot dip galvanizing method. The purpose of this study to improve the quality of products from low carbon steel bolts A325 with the addition of Zinc Aluminium alloy on the results of the Hot Dip Galvanizing. Results of testing the hardness of the lowest obtained in quenching time of 30 seconds is 162 037 HVN and the highest hardness obtained on quenching time of 60 seconds is 203 688 HVN. To microstructure shows that the phase Eta which is soft on the surface of the outermost started a little not as much time quenching 30 seconds so that the nature of its decline and violence increased the phase Zeta that are hard are widely spread meet the layer of phase resulting in hardness of the coating while quenching 45 seconds exceed the hardness of quenching time of 30 seconds. Results of analysis of the rate of corrosion that galvanized coating on each test is different and the structure of ferrite and pearlite it looks clear. For quenching time of 30 seconds obvious difference in galvanized layer thicker than quenching time of 45 and 60 seconds. This happens because of the influence of factors zinc layer that coats the base material so that decreased levels of corrosion is comparable to the time Salt Spray Test SST performed.

  17. Electrolytic deposition and corrosion resistance of Zn–Ni coatings ...

    Indian Academy of Sciences (India)

    Zn–Ni coatings were deposited under galvanostatic conditions on steel substrate (OH18N9). The influence of current density of deposition on the surface morphology, chemical and phase composition was investigated. The corrosion resistance of Zn–Ni coatings obtained at current density 10–25 mA cm-2 are measured, ...

  18. Electrochemical Study of Welded AISI 304 and 904L Stainless Steel in Seawater in View of Corrosion

    Directory of Open Access Journals (Sweden)

    Richárd Székely

    2010-10-01

    Full Text Available This is a comparative study of the corrosion behaviour of welds in AISI 304 and AISI 904L stainless steels carried out in seawater model solution in the temperature range 5-35°C and the standard of corrosion testing of welds was followed. The corrosion rate and corrosion attack characteristics were determined for welds of the examined steels with several type of treatment. The aim of this work was to compare the steels based on their resistance against the corrosion in terms of pitting potential (Epit and repassivation potential (Erepass. Seawater is an electrochemically aggressive medium, which can initiate localised corrosion in welded stainless steels. Different electrochemical and testing methods were used, including cyclic voltammetry, chronopotentiometry, electrochemical impedance spectroscopy (EIS, pH measuring and penetration tests.

  19. Monitoring Techniques for Microbially Influenced Corrosion of Carbon Steel

    DEFF Research Database (Denmark)

    Hilbert, Lisbeth Rischel

    2000-01-01

    of carbon steel must be monitored on-line in order to provide an efficient protection and control the corrosion. A number of monitoring techniques is industrially used today, and the applicability and reliability of these for monitoring MIC is evaluated. Coupons and ER are recommended as necessary basic......Abstract Monitoring Techniques for Microbially Influenced Corrosion of Carbon Steel Microbially influenced corrosion (MIC) of carbon steel may occur in media with microbiological activity of especially sulphate-reducing bacteria, e.g. on pipelines buried in soil and on marine structures. MIC...... techniques even though localised corrosion rate cannot be measured. FSM measures general corrosion and detects localised corrosion, but the sensitivity is not high enough for monitoring initiation of pitting and small attacks. Electrochemical techniques as LPR and EIS give distorted data and unreliable...

  20. Effect of environment on corrosion characteristics of newly developed DMR-1700 structural steel

    Directory of Open Access Journals (Sweden)

    Injeti Gurrappa and Guntupalli Malakondaiah

    2008-01-01

    Full Text Available The corrosion resistance of any metallic material depends on the environment to which it is exposed. DMR-1700 steel is a material for structural applications that has been recently developed at Defence Metallurgical Research Laboratory by changing the chemistry of alloying elements. Therefore, a detailed understanding of its corrosion characteristics under different environmental conditions is essential. In the present paper, we report the results of a systematic corrosion study that was carried out on the new steel to determine the effect of the environment on the protective nature of the oxide scale that forms on its surface under different environmental conditions. Furthermore, the oxide scale as well as the resistance to pitting and crevice corrosion were studied in various environments. The surface morphologies of the corroded steels were observed under a scanning electron microscope (SEM to determine the nature of the corrosion. On the basis of studies by different techniques, DMR-1700 steel is recommended for the manufacture of components used in various systems in conjunction with the application of an appropriate protective coating to improve its resistivity to corrosion.

  1. Effect of environment on corrosion characteristics of newly developed DMR-1700 structural steel.

    Science.gov (United States)

    Gurrappa, Injeti; Malakondaiah, Guntupalli

    2008-04-01

    The corrosion resistance of any metallic material depends on the environment to which it is exposed. DMR-1700 steel is a material for structural applications that has been recently developed at Defence Metallurgical Research Laboratory by changing the chemistry of alloying elements. Therefore, a detailed understanding of its corrosion characteristics under different environmental conditions is essential. In the present paper, we report the results of a systematic corrosion study that was carried out on the new steel to determine the effect of the environment on the protective nature of the oxide scale that forms on its surface under different environmental conditions. Furthermore, the oxide scale as well as the resistance to pitting and crevice corrosion were studied in various environments. The surface morphologies of the corroded steels were observed under a scanning electron microscope (SEM) to determine the nature of the corrosion. On the basis of studies by different techniques, DMR-1700 steel is recommended for the manufacture of components used in various systems in conjunction with the application of an appropriate protective coating to improve its resistivity to corrosion.

  2. Advanced Corrosion-Resistant Zr Alloys for High Burnup and Generation IV Application

    Energy Technology Data Exchange (ETDEWEB)

    Jeong, Y. H.; Park, S. Y.; Lee, M. H.; Choi, B. K.; Baek, J. H.; Park, J. Y.; Kim, J. H.; Kim, H. G.; Jung, Y. H.; Bang, B. G

    2006-08-15

    The systematic study was performed to develop the advanced corrosion-resistant Zr alloys for high burnup and Gen IV application. The corrosion behavior was significantly changed with the alloy composition and the corrosion environment. In general, the model alloys with a higher alloying elements showed a higher corrosion resistance. Among the model alloys tested in this study, Zr-10Cr-0.2Fe showed the best corrosion resistance regardless of the corrosion condition. The oxide on the higher corrosion-resistant alloy such as Zr-1.0Cr-0.2Fe consisted of mainly columnar grains, and it have a higher tetragonal phase stability. In comparison with other alloys being considered for the SCWR, the Zr alloys showed a lower corrosion rate than ferritic-martensitic steels. The results of this study imply that, at least from a corrosion standpoint, Zr alloys deserve consideration as potential cladding or structural materials in supercritical water cooled reactors.

  3. Peptide-based biocoatings for corrosion protection of stainless steel biomaterial in a chloride solution.

    Science.gov (United States)

    Muruve, Noah G G; Cheng, Y Frank; Feng, Yuanchao; Liu, Tao; Muruve, Daniel A; Hassett, Daniel J; Irvin, Randall T

    2016-11-01

    In this work, PEGylated D-amino acid K122-4 peptide (D-K122-4-PEG), derived from the type IV pilin of Pseudomonas aeruginosa, coated on 304 stainless steel was investigated for its corrosion resistant properties in a sodium chloride solution by various electrochemical measurements, surface characterization and molecular dynamics simulation. As a comparison, stainless steel electrodes coated with non-PEGylated D-amino acid retroinverso peptide (RI-K122-4) and D-amino acid K122-4 peptide (D-K122-4) were used as control variables during electrochemical tests. It was found that the D-K122-4-PEG coating is able to protect the stainless steel from corrosion in the solution. The RI-K122-4 coating shows corrosion resistant property and should be investigated further, while the D-K122-4 peptide coating, in contrast, shows little to no effect on corrosion. The morphological characterizations support the corrosion resistance of D-K122-4-PEG on stainless steel. The adsorption of D-K122-4 molecules occurs preferentially on Fe2O3, rather than Cr2O3, present on the stainless steel surface. Copyright © 2016 Elsevier B.V. All rights reserved.

  4. Corrosion and Stress Corrosion Behaviors of Low and Medium Carbon Steels in Agro-Fluid Media

    Directory of Open Access Journals (Sweden)

    Ayo Samuel AFOLABI

    2007-01-01

    Full Text Available Investigations were carried out to study critically the corrosion behaviour and Stress Corrosion Cracking (SCC of low and medium carbon steels in cassava and cocoa extracts by weight loss measurement and constant extension to fracture method respectively. The results obtained showed that medium carbon steel is more susceptible to corrosion than low carbon steel in both media. SCC is also more in medium carbon steel than low carbon steel in the two media under study. These deductions are due to higher carbon content in medium carbon steel coupled with various aggressive corrosion constituents contained in these media. Hydrogen embrittlement, as well as carbon cracking, is responsible for SCC of these materials in the agro-fluid media.

  5. Corrosion inhibition of mild steel by Capsicum annuum fruit paste

    Directory of Open Access Journals (Sweden)

    Chandan M. Reddy

    2016-09-01

    Full Text Available The anti-corrosive property of Capsicum annuum fruit paste (CFP on mild steel was investigated. Weight loss and SEM analysis showed that the aqueous and ethanolic solutions of CFP exhibits excellent corrosion inhibition in 2 M HCl. Contact angle, surface atomic composition and FTIR studies verified the presence of an organic film on the mild steel surface. The FTIR spectra also indicated the formation of active compound-Fe complex. CFP thus shows potential as an inexpensive environment friendly corrosion inhibitor for mild steel.

  6. EFFECT OF INTERMETALLIC PHASES ON CORROSION BEHAVIOR AND MECHANICAL PROPERTIES OF DUPLEX STAINLESS STEEL AND SUPER-DUPLEX STAINLESS STEEL

    Directory of Open Access Journals (Sweden)

    Prabhu Paulraj

    2015-08-01

    Full Text Available Duplex Stainless Steels (DSS and Super Duplex Stainless Steel (SDSS have excellent integration of mechanical and corrosion properties. However, the formation of intermetallic phases is a major problem in their usage. The mechanical and corrosion properties are deteriorated due to the presence of intermetallic phases. These phases are induced during welding, prolonged exposure to high temperatures, and improper heat treatments. The main emphasis of this review article is on intermetallic phases and their effects on corrosion and mechanical properties. First the effect of various alloying elements on DSS and SDSS has been discussed followed by formation of various intermetallic phases. The intermetallic phases affect impact toughness and corrosion resistance significantly. Their deleterious effect on weldments has also been reviewed.

  7. Effect of Pharmaceutically Active Compound Nitroxoline on the Corrosion of Mild Steel in an Acidic Environment

    Directory of Open Access Journals (Sweden)

    R. Ganapathi Sundaram

    2016-01-01

    Full Text Available The effect of Nitroxoline, antibiotic drug, was tested as a corrosion inhibitor for mild steel (MS in an acidic environment by chemical method (mass loss measurement and electrochemical methods such as electrochemical impedance spectroscopy and potentiodynamic polarization. The surface morphology of mild steel was investigated by scanning electron microscopy, energy dispersive X-ray spectroscopy, and atomic force microscopy techniques. From the chemical and electrochemical methods, the resistance of corrosion was increased with the addition of Nitroxoline concentration. Tafel curves indicate that the pharmaceutically active compound is a cathodic type inhibitor. An adsorption of Nitroxoline on the surface of mild steel was obeyed by Langmuir isotherm. SEM, EDX, and AFM techniques prove the adsorption process. All the obtained results confirmed that the investigated compound Nitroxoline acts as a good inhibitor for the corrosion of mild steel in an acidic environment.

  8. Corrosion resistant alloys for reinforced concrete [2009

    Science.gov (United States)

    2009-04-01

    Deterioration of concrete bridges because of reinforcing steel corrosion has been recognized for four-plus decades as a major technical and economic challenge for the United States. As an option for addressing this problem, renewed interest has focus...

  9. Initiation and Growth of Corrosion Pit and Its Effect on Corrosion Fatigue Strength in 12Cr Stainless Steel

    National Research Council Canada - National Science Library

    HAYASHI, Makoto; AMANO, Kazuo; UEYAMA, Yoshiharu

    2017-01-01

    .... The corrosion fatigue cracks often initiate from the pits. In order to prevent the corrosion fatigue failure, 12Cr stainless steel is employed for the components used in the corrosive environments...

  10. Oxidation and corrosion behavior of modified-composition, low-chromium 304 stainless steel alloys

    Science.gov (United States)

    Stephens, J. R.; Barrett, C. A.

    1977-01-01

    The effects of substituting less strategic elements than Cr on the oxidation and corrosion resistance of AISI 304 stainless steel were investigated. Cyclic oxidation resistance was evaluated at 870 C. Corrosion resistance was determined by exposure of specimens to a boiling copper-rich solution of copper sulfate and sulfuric acid. Alloy substitutes for Cr included Al, Mn, Mo, Si, Ti, V, Y, and misch metal. A level of about 12% Cr was the minimum amount of Cr required for adequate oxidation and corrosion resistance in the modified composition 304 stainless steels. This represents a Cr saving of at least 33%. Two alloys containing 12% Cr and 2% Al plus 2% Mo and 12% Cr plus 2.65% Si were identified as most promising for more detailed evaluation.

  11. Monitoring corrosion of steel bars in reinforced concrete structures.

    Science.gov (United States)

    Verma, Sanjeev Kumar; Bhadauria, Sudhir Singh; Akhtar, Saleem

    2014-01-01

    Corrosion of steel bars embedded in reinforced concrete (RC) structures reduces the service life and durability of structures causing early failure of structure, which costs significantly for inspection and maintenance of deteriorating structures. Hence, monitoring of reinforcement corrosion is of significant importance for preventing premature failure of structures. This paper attempts to present the importance of monitoring reinforcement corrosion and describes the different methods for evaluating the corrosion state of RC structures, especially hal-cell potential (HCP) method. This paper also presents few techniques to protect concrete from corrosion.

  12. Corrosion of Steel in Concrete – Thermodynamical Aspects

    DEFF Research Database (Denmark)

    Küter, Andre; Møller, Per; Geiker, Mette Rica

    2004-01-01

    formation and composition of corrosion products have been proposed. Suggested reactions, except half-cell reactions, are verified or rejected based on their Gibbs free energy, while the electrode potential is calculated for half-cell reactions. Corrosion products postulated to form are related......The present understanding of selected corrosion phenomena in reinforced concrete is reviewed. Special emphasis is given to chloride induced corrosion. There is a general acceptance of the basic corrosion mechanism for steel in concrete. However different anodic reactions governing the subsequent...

  13. A STUDY OF CORROSION AND STRESS CORROSION CRACKING OF CARBON STEEL NUCLEAR WASTE STORAGE TANKS

    Energy Technology Data Exchange (ETDEWEB)

    BOOMER, K.D.

    2007-08-21

    The Hanford reservation Tank Farms in Washington State has 177 underground storage tanks that contain approximately 50 million gallons of liquid legacy radioactive waste from cold war plutonium production. These tanks will continue to store waste until it is treated and disposed. These nuclear wastes were converted to highly alkaline pH wastes to protect the carbon steel storage tanks from corrosion. However, the carbon steel is still susceptible to localized corrosion and stress corrosion cracking. The waste chemistry varies from tank to tank, and contains various combinations of hydroxide, nitrate, nitrite, chloride, carbonate, aluminate and other species. The effect of each of these species and any synergistic effects on localized corrosion and stress corrosion cracking of carbon steel have been investigated with electrochemical polarization, slow strain rate, and crack growth rate testing. The effect of solution chemistry, pH, temperature and applied potential are all considered and their role in the corrosion behavior will be discussed.

  14. Electrolyte Composition for Distinguishing Corrosion Mechanisms in Steel Alloy Screening

    Directory of Open Access Journals (Sweden)

    Ingmar Bösing

    2017-01-01

    Full Text Available The formation and breakdown of passive layers due to pitting corrosion are a major cause of failure of metal structures. The investigation of passivation and pitting corrosion requires two different electrochemical measurements and is therefore a time consuming process. To reduce time in material characterization and to study the interactions of both mechanisms, here, a combined experiment addressing both phenomena is introduced. In the presented electrolyte the different corrosion mechanisms are distinguished and investigated by cyclic voltammograms and polarization scans. The measurements show a passive area, metastable pit growth, and pitting corrosion as well as repassivation. The pitting corrosion is separated from additional dissolution processes and the standard deviation of the corrosion potential is smaller than in other electrolytes. Both passivation and pitting corrosion can be observed in one measurement without additional corrosion attacks. The deviation between different measurements of the same steel is small; this is helpful for the screening of similar materials.

  15. Stress-Corrosion Cracking in Martensitic PH Stainless Steels

    Science.gov (United States)

    Humphries, T.; Nelson, E.

    1984-01-01

    Precipitation-hardening alloys evaluated in marine environment tests. Report describes marine-environment stress-corrosion cracking (SCC) tests of three martensitic precipitation hardening (PH) stainless-steel alloys.

  16. Effect of Geobacter sulfurreducens on the microbial corrosion of mild steel, ferritic and austenitic stainless steels

    Energy Technology Data Exchange (ETDEWEB)

    Mehanna, Maha [Laboratoire de Genie Chimique, CNRS - Universite de Toulouse, 5 rue Paulin Talabot, BP1301, 31029 Toulouse (France)], E-mail: mum34@psu.edu; Basseguy, Regine; Delia, Marie-Line; Bergel, Alain [Laboratoire de Genie Chimique, CNRS - Universite de Toulouse, 5 rue Paulin Talabot, BP1301, 31029 Toulouse (France)

    2009-11-15

    The influence of Geobacter sulfurreducens was tested on the anaerobic corrosion of four different steels: mild steel 1145, ferritic steel 403 and austenitic steels 304L and 316L. Within a few hours, the presence of cells induced a free potential (E{sub oc}) ennoblement around +0.3 V on 1145 mild steel, 403 ferritic steel and 304L austenitic steels and slightly less on 316L. The kinetics of E{sub oc} ennoblement depended on the amount of bacteria in the inoculum, but the final potential value depended essentially on the nature of the material. This effect was due to the capacity of G. sulfurreducens to create a direct cathodic reaction on steel surfaces, extracting the electrons directly from material. The presence of bacterial cells modified the corrosion features of mild steel and ferritic steel, so that corrosion attacks were gathered in determined zones of the surface. Local corrosion was significantly enhanced on ferritic steel. Potential ennoblement was not sufficient to induce corrosion on austenitic steels. In contrast G. sulfurreducens delayed the occurrence of pitting on 304L steel because of its capability to oxidize acetate at high potential values. The electrochemical behaviour of 304L steel was not affected by the concentration of soluble electron donor (acetate, 1-10 mM) or the amount of planktonic cells; it was directly linked to the biofilm coverage. After polarization pitting curves had been recorded, microscopic observations showed that pits propagated only in the surface zones where cell settlement was the densest. The study evidenced that Geobacter sulfurreducens can control the electrochemical behaviour of steels in complex ways that can lead to severe corrosion. As Geobacteraceae are ubiquitous species in sediments and soils they should now be considered as possible crucial actors in the microbial corrosion of buried equipment.

  17. ELECTROCHEMICAL STUDIES ON THE CORROSION OF CARBON STEEL IN OXALIC ACID CLEANING SOLUTIONS

    Energy Technology Data Exchange (ETDEWEB)

    Wiersma, B; John Mickalonis, J

    2007-10-08

    The Savannah River Site (SRS) will disperse or dissolve precipitated metal oxides as part of radioactive waste tank closure operations. Previously SRS has utilized oxalic acid to accomplish this task. Since the waste tanks are constructed of carbon steel, a significant amount of corrosion may occur. Although the total amount of corrosion may be insignificant for a short contact time, a significant amount of hydrogen may be generated due to the corrosion reaction. Linear polarization resistance and anodic/cathodic polarization tests were performed to investigate the corrosion behavior during the process. The effect of process variables such as temperature, agitation, aeration, sample orientation, light as well as surface finish on the corrosion behavior were evaluated. The results of the tests provided insight into the corrosion mechanism for the iron-oxalic acid system.

  18. Corrosion Inhibition of High Speed Steel by Biopolymer HPMC Derivatives

    Directory of Open Access Journals (Sweden)

    Shih-Chen Shi

    2016-07-01

    Full Text Available The corrosion inhibition characteristics of the derivatives of biopolymer hydroxypropyl methylcellulose (HPMC, hydroxypropyl methylcellulose phthalate (HPMCP, and hydroxypropyl methylcellulose acetate succinate (HPMCAS film are investigated. Based on electrochemical impedance spectroscopic measurements and potentiodynamic polarization, the corrosion inhibition performance of high speed steel coated with HPMC derivatives is evaluated. The Nyquist plot and Tafel polarization demonstrate promising anti-corrosion performance of HPMC and HPMCP. With increasing film thickness, both materials reveal improvement in corrosion inhibition. Moreover, because of a hydrophobic surface and lower moisture content, HPMCP shows better anti-corrosion performance than HPMCAS. The study is of certain importance for designing green corrosion inhibitors of high speed steel surfaces by the use of biopolymer derivatives.

  19. Detection of pitting corrosion in steel using image processing

    OpenAIRE

    Ghosh, Bidisha; Pakrashi, Vikram; Schoefs, Franck

    2010-01-01

    This paper presents an image processing based detection method for detecting pitting corrosion in steel structures. High Dynamic Range (HDR) imaging has been carried out in this regard to demonstrate the effectiveness of such relatively inexpensive techniques that are of immense benefit to Non – Destructive – Tesing (NDT) community. The pitting corrosion of a steel sample in marine environment is successfully detected in this paper using the proposed methodology. It is observed, that the prop...

  20. Electrochemical corrosion behaviors of the X90 linepipe steel in NS4 solution

    Directory of Open Access Journals (Sweden)

    Jinheng Luo

    2016-10-01

    Full Text Available Oil and gas line pipes are laid underground and run through different areas in the laying process, so they will be subjected to different degrees of corrosion and even crack, leading to enormous casualties and economic losses. In order to guarantee the safe operation of line pipes, therefore, it is significant to investigate the electrochemical corrosion behaviors of pipe steel in a simulated soil environment. In this paper, the electrochemical corrosion behaviors of the base metals and welding materials of API 5L X90 steel longitudinally submerged arc welding pipes in near-neutral simulated soil solution (NS4 were studied by means of the electrochemical impedance spectroscopy (EIS and the potentiodynamic polarization testing technology. It is shown that the typical characteristic of anodic dissolution is presented but with no passivation phenomenon when X90 linepipe steel is put in NS4 solution. The base material is thermodynamically more stable than the seam weld material. The base material and seam weld samples were polarized under −850 mV polarization potential for different durations. It is demonstrated that with the proceeding of polarization, the polarization resistance and the corrosion resistance increase while the corrosion current density decreases. And the corrosion resistance of base material is better than that of seam weld material.

  1. Inhibitor for the Corrosion of Mild Steel in H SO

    African Journals Online (AJOL)

    NJD

    Terminalia chebula, acid corrosion inhibitor, electrochemical polarization, electrochemical impedance spectroscopy, mild steel. 1. Introduction. Large amounts of sulphuric acid are used in the chemical in- dustry for the removal of undesired scale and rust. The addition of corrosion inhibitors effectively protects the metal ...

  2. Corrosion of steel structures in sea-bed sediment

    Indian Academy of Sciences (India)

    Seabed sediment (SBS) is a special soil that is covered by seawater. With the developments in marine oil exploitation and engineering, more and more steel structures have been buried in SBS. SBS corrosion has now become a serious problem in marine environment and an important issue in corrosion science. In this ...

  3. Stress corrosion cracking of AISI 321 stainless steel in acidic ...

    Indian Academy of Sciences (India)

    Unknown

    YANLIANG HUANG. Marine Corrosion and Protection Laboratory, Institute of Oceanology, Chinese Academy of Sciences, 7 Nanhai Road,. Qingdao 266071, China. MS received 21 August 2001; revised 21 November 2001. Abstract. The stress corrosion cracking (SCC) of AISI 321 stainless steel in acidic chloride solution ...

  4. Corrosion Response of Low Carbon Steel in Tropical Road Mud ...

    African Journals Online (AJOL)

    These ultimately result in Deposit and Pilling Corrosion damages which perforate the metal structure if left unattended. Cathodic Protection and the use of Corrosion Inhibitors are not practical in this problem. Other steel structures, as buildings, petroleum, gas, water and sewage pipelines exposed to soil and mud are ...

  5. Corrosion Protection of Steels by Conducting Polymer Coating

    Directory of Open Access Journals (Sweden)

    Toshiaki Ohtsuka

    2012-01-01

    Full Text Available The corrosion protection of steels by conducting polymer coating is reviewed. The conducting polymer such as polyaniline, polypyrrole, and polythiophen works as a strong oxidant to the steel, inducing the potential shift to the noble direction. The strongly oxidative conducting polymer facilitates the steel to be passivated. A bilayered PPy film was designed for the effective corrosion protection. It consisted of the inner layer in which phosphomolybdate ion, PMo12O3−40 (PMo, was doped and the outer layer in which dodecylsulfate ion (DoS was doped. The inner layer stabilized the passive oxide and the outer possessed anionic perm-selectivity to inhibit the aggressive anions such as chloride from penetrating through the PPy film to the substrate steel. By the bilayered PPy film, the steel was kept passive for about 200 h in 3.5% sodium chloride solution without formation of corrosion products.

  6. Effect of Pseudomonas fluorescens on Buried Steel Pipeline Corrosion.

    Science.gov (United States)

    Spark, Amy J; Law, David W; Ward, Liam P; Cole, Ivan S; Best, Adam S

    2017-08-01

    Buried steel infrastructure can be a source of iron ions for bacterial species, leading to microbiologically influenced corrosion (MIC). Localized corrosion of pipelines due to MIC is one of the key failure mechanisms of buried steel pipelines. In order to better understand the mechanisms of localized corrosion in soil, semisolid agar has been developed as an analogue for soil. Here, Pseudomonas fluorescens has been introduced to the system to understand how bacteria interact with steel. Through electrochemical testing including open circuit potentials, potentiodynamic scans, anodic potential holds, and electrochemical impedance spectroscopy it has been shown that P. fluorescens increases the rate of corrosion. Time for oxide and biofilms to develop was shown to not impact on the rate of corrosion but did alter the consistency of biofilm present and the viability of P. fluorescens following electrochemical testing. The proposed mechanism for increased corrosion rates of carbon steel involves the interactions of pyoverdine with the steel, preventing the formation of a cohesive passive layer, after initial cell attachment, followed by the formation of a metal concentration gradient on the steel surface.

  7. Spatial distribution of crystalline corrosion products formed during corrosion of stainless steel in concrete

    KAUST Repository

    Serdar, Marijana

    2015-05-01

    © 2015 Elsevier Ltd All rights reserved. The mineralogy and spatial distribution of nano-crystalline corrosion products that form in the steel/concrete interface were characterized using synchrotron X-ray micro-diffraction (μ-XRD). Two types of low-nickel high-chromium reinforcing steels embedded into mortar and exposed to NaCl solution were investigated. Corrosion in the samples was confirmed by electrochemical impedance spectroscopy (EIS). μ-XRD revealed that goethite (α-FeOOH) and akaganeite (β-FeOOH) are the main iron oxide-hydroxides formed during the chloride-induced corrosion of stainless steel in concrete. Goethite is formed closer to the surface of the steel due to the presence of chromium in the steel, while akaganeite is formed further away from the surface due to the presence of chloride ions. Detailed microstructural analysis is shown and discussed on one sample of each type of steel.

  8. Tropical Weather Resistant Galvanized Steel Coated and Uncoated

    Directory of Open Access Journals (Sweden)

    Suárez-Corrales Xenia Isbel

    2014-01-01

    Full Text Available The corrosion behavior of coated and uncoated galvanized steel products is determined by exposing them to accelerated and natural climatic test. Accelerated tests were carried out in climatic chambers and natural atmospheric test in a marine-coastal station (Cojimar. The influence of tropical humid climate on these products is determined. Adhesion is an important property for a good performance, from the decorative point of view or as an additional protection. The evaluation indicates that 95% of the galvanized steel products show a good corrosion resistance; although 71% of coated galvanized products and 100% of painted galvanized products do not cover the requirements with respect to the mechanical and corrosion protection aspects. For a good efficiency and economic performance of metal mechanical industry, a correct surface treatment and coating application is required. A key point is to increase the quality by improving a better corrosion protective performance respecting uncoated galvanized steel.

  9. The corrosion and stress corrosion cracking behavior of a novel alumina-forming austenitic stainless steel in supercritical water

    Science.gov (United States)

    Sun, Hongying; Yang, Haijie; Wang, Man; Giron-Palomares, Benjamin; Zhou, Zhangjian; Zhang, Lefu; Zhang, Guangming

    2017-02-01

    The general corrosion and stress corrosion behavior of Fe-27Ni-15Cr-5Al-2Mo-0.4Nb alumina-forming austenitic (AFA) steel were investigated in supercritical water under different conditions. A double layer oxide structure was formed: a Fe-rich outer layer (Fe2O3 and Fe3O4) and an Al-Cr-rich inner layer. And the inner layer has a low growth rate with exposing time, which is good for improvement of corrosion resistance. Additionally, some internal nodular Al-Cr-rich oxides were also observed, which resulted in a local absence of inner layer. Stress corrosion specimens exhibited a combination of high strength, good ductility and low susceptibility. The stress strength and elongation was reduced by increasing temperature and amount of dissolved oxygen. In addition, the corresponding susceptibility was increased with decreased temperatures and increased oxygen contents.

  10. In situ 3D monitoring of corrosion on carbon steel and ferritic stainless steel embedded in cement paste

    KAUST Repository

    Itty, Pierre-Adrien

    2014-06-01

    In a X-ray microcomputed tomography study, active corrosion was induced by galvanostatically corroding steel embedded in cement paste. The results give insight into corrosion product build up, crack formation, leaching of products into the cracks and voids, and differences in morphology of corrosion attack in the case of carbon steel or stainless steel reinforcement. Carbon steel was homogeneously etched away with a homogeneous layer of corrosion products forming at the steel/cement paste interface. For ferritic stainless steel, pits were forming, concentrating the corrosion products locally, which led to more extensive damage on the cement paste cover. © 2014 Elsevier Ltd.

  11. Electrochemical corrosion behavior of X52 and X60 steels in carbon dioxide containing saltwater solution

    OpenAIRE

    Rihan Omar Rihan

    2012-01-01

    X52 and X60 high strength low alloy (HSLA) steels are widely used in the construction of petroleum pipelines. This paper discusses the corrosion resistance of X52 and X60 steels in CO2 containing saltwater at pH 4.4 and 50 ºC. A circulating flow loop system inside an autoclave was used for conducting the experimental work. The rotating impeller speed was 2000 rpm. The corrosion rate was monitored using in situ electrochemical methods such as potentiodynamic sweep, linear polarization resistan...

  12. Stress corrosion cracking properties of 15-5PH steel

    Science.gov (United States)

    Rosa, Ferdinand

    1993-01-01

    Unexpected occurrence of failures, due to stress corrosion cracking (SCC) of structural components, indicate a need for improved characterization of materials and more advanced analytical procedures for reliably predicting structures performance. Accordingly, the purpose of this study was to determine the stress corrosion susceptibility of 15-5PH steel over a wide range of applied strain rates in a highly corrosive environment. The selected environment for this investigation was a highly acidified sodium chloride (NaCl) aqueous solution. The selected alloy for the study was a 15-5PH steel in the H900 condition. The slow strain rate technique was selected to test the metals specimens.

  13. Properties, weldability and corrosion behavior of supermartensitic stainless steels for on- and offshore applications

    Energy Technology Data Exchange (ETDEWEB)

    Taban, Emel; Kaluc, Erdinc; Ojo, Olatunji Oladimeji [Kocaeli Univ. (Turkey). Welding Research, Education and Training Center

    2016-08-01

    Stimulated material-environment interactions inside and around flowlines of deep or ultra deep wells during oil and gas exploration, and fabrication economy of pipelines have been the major challenges facing the oil and gas industries. Presumably, an extensive focus on high integrity, performance and material economy of flowlines have realistically made supermartensitic stainless steels (SMSS) efficient and effective material choices for fabricating onshore and offshore pipelines. Supermartensitic stainless steels exhibit high strength, good low temperature toughness, sufficient corrosion resistance in sweet and mildly sour environments, and good quality weldability with both conventional welding processes and modern welding methods such as laser beam welding, electron beam welding and hybrid welding approaches. In terms of economy, supermartensitic stainless steels are cheaper and they are major replacements for more expensive duplex stainless steels required for tubing applications in the oil and gas industry. However, weld areas of SMSS pipes are exposed to sulphide stress cracking (SSC), so intergranular stress corrosion cracking (IGSCC) or stress corrosion cracking can occur. In order to circumvent this risk of cracking, a post-weld heat treatment (PWHT) for 5 minutes at about 650 C is recommended. This paper provides detailed literature perusal on supermartensitic stainless steels, their weldability and corrosion behaviors. It also highlights a major research area that has not been thoroughly expounded in literature; fatigue loading behaviors of welded SMSS under different corrosive environments have not been thoroughly detailed in literature.

  14. Corrosion behavior of TiC particle-reinforced 2Cr13 stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Qianlin; Yin, Yansheng [Institute of Marine Materials Science and Engineering, Shanghai Maritime University, Shanghai 201306 (China); Li, Wenge [College of Materials Engineering, Shanghai University of Engineering Science, Shanghai 201620 (China)

    2011-06-15

    The corrosion behavior of TiC particle-reinforced 2Cr13 stainless steels prepared by in situ reaction and electroslag remelting (ESR) was investigated using potentiodynamic polarisation measurements and immersion tests. The addition of TiC particles to 2Cr13 stainless steel impeded rapid pit propagation but maintained a high corrosion rate in the whole immersion time investigated. The TiC addition developed finer matrix structure, the formation of Cr-rich carbides and high dislocation density around the TiC particles before corrosion, which results in an increasing corrosion rate and preferential pitting attack at the steel matrix/TiC interface. Although the corrosion resistance of 2Cr13 stainless steel is sharply decreased due to TiC addition, it is significantly improved after the ESR process. This is attributed to the more uniform distribution and smaller size of TiC particles, the increase of value of {chi} in TiC{chi} and the elimination of the porosity in TiC particle-reinforced 2Cr13 stainless steel after the ESR process. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  15. Influence of delta ferrite on corrosion susceptibility of AISI 304 austenitic stainless steel

    Directory of Open Access Journals (Sweden)

    Lawrence O. Osoba

    2016-12-01

    Full Text Available In the current study, the influence of delta (δ ferrite on the corrosion susceptibility of AISI 304 austenitic stainless steel was evaluated in 1Molar concentration of sulphuric acid (H2SO4 and 1Molar concentration of sodium chloride (NaCl. The study was performed at ambient temperature using electrochemical technique—Tafel plots to evaluate the corrosive tendencies of the austenitic stainless steel sample. The as-received (stainless steel specimen and 60% cold-worked (stainless steel specimens were isothermally annealed at 1,100°C for 2 h and 1 h, respectively, and quenched in water. The results obtained show that the heat-treated specimen and the 60% cold-worked plus heat-treated specimen exhibited higher corrosion susceptibility than the as-received specimen, which invariably contained the highest fraction of δ ferrite particles. The finding shows that the presence of δ ferrite, in which chromium (Cr, the main corrosion inhibitor segregates, does not degrade and or reduces the resistance to aqueous corrosion of the austenitic stainless steel material.

  16. Corrosion-Resistant Alkyd Coatings

    Science.gov (United States)

    1992-02-18

    a corrosion-inhibiting pigment consisting essentially of critical amounts of at least one zinc phosphate , zinc molybdate and at least one zinc salt...of at leajt one 2inc phosphate , continuationi of application 07/211.026 filed June 16, 40 to 260 pans by weight cf zinc molybdate. and 1 to 30 1988... phosphate , zinc molybdate and a. tions of this invention, however, are resistant to harsh lea$t one zmc »•« of a benzoic acid. weather conditions and

  17. Selection of Corrosion Resistant Materials for Nuclear Waste Repositories

    Energy Technology Data Exchange (ETDEWEB)

    R.B. Rebak

    2006-08-28

    Several countries are considering geological repositories to dispose of nuclear waste. The environment of most of the currently considered repositories will be reducing in nature, except for the repository in the US, which is going to be oxidizing. For the reducing repositories, alloys such as carbon steel, stainless steels and titanium are being evaluated. For the repository in the US, some of the most corrosion resistant commercially available alloys are being investigated. This paper presents a summary of the behavior of the different materials under consideration for the repositories and the current understanding of the degradation modes of the proposed alloys in ground water environments from the point of view of general corrosion, localized corrosion and environmentally assisted cracking.

  18. Relationship Between pH and Electrochemical Corrosion Behavior of Thermal-Sprayed Ni-Al-Coated Q235 Steel in Simulated Soil Solutions

    Science.gov (United States)

    Wei, Wei; Wu, Xin-qiang; Ke, Wei; Xu, Song; Feng, Bing; Hu, Bo-tao

    2017-09-01

    Electrochemical corrosion behavior of a thermal-sprayed Ni-Al-coated Q235 steel was investigated in the simulated soil solutions at different pH values using measurements of potentiodynamic polarization curves and electrochemical impedance spectroscopy as well as surface analyses including x-ray diffraction analysis, scanning electron microscope equipped with an energy-dispersive x-ray spectroscopy and x-ray photoelectron spectroscopy. The results showed that the corrosion resistance of the Ni-Al-coated Q235 steel was dependent on the pH of the test solution. From pH = 3.53 to pH = 4.79, the corrosion resistance of the coated steel increased rapidly. In the pH range from 4.79 to 12.26, the corrosion resistance exhibited no significant change. At pH 13.25, the corrosion resistance of the sample was found to decrease. The calculated corrosion rate of Ni-Al-coated Q235 steel was lower than that of the uncoated Q235 steel and galvanized steel in all the test solutions. Over a wide range of pH values, the Ni-Al-coated Q235 steel exhibited extremely good corrosion resistance. The experimental data together with the potential-pH diagrams provided a basis for a detailed discussion of the related corrosion mechanisms of the coated steel.

  19. Anticorrosion potential of hydralazine for corrosion of mild steel in ...

    African Journals Online (AJOL)

    Anticorrosion potential of mild steel by Hydralazine as corrosion inhibitor for mild steel in 1M hydrochloric acid was investigated by chemical and electrochemical measurements at 303-333 K temperature. The maximum inhibition efficiency of inhibitor by Weight loss method is around 90%, Tafel polarization method is ...

  20. Corrosion Behavior of MIG Brazed and MIG Welded Joints of Automotive DP600-GI Steel Sheet

    Science.gov (United States)

    Basak, Sushovan; Das, Hrishikesh; Pal, Tapan Kumar; Shome, Mahadev

    2016-12-01

    Galvanized dual-phase steel sheets are extensively used by the auto industry for their corrosion resistance property. Welding by the metal inert gas (MIG) process causes degradation of the steel in the vicinity of the joint due to excessive zinc evaporation. In order to minimize Zn loss, the MIG brazing process has been tried out in lap joint configuration over a heat input range of 136-204 J mm-1. The amount of zinc loss, intermetallic formation and corrosion properties in the joint area has been evaluated for both MIG brazing and MIG welding. Corrosion rate of 21 mm year-1 has been reduced to 2 mm year-1 by adopting MIGB in place MIGW. Impedance study has shown that the corrosion mechanism in base metal, MIG brazed and MIG welded joints is dominated by charge transfer, diffusion and mixed mode control processes, respectively.

  1. When can Electrochemical Techniques give Reliable Corrosion Rates on Carbon Steel in Sulfide Media?

    DEFF Research Database (Denmark)

    Hilbert, Lisbeth Rischel; Hemmingsen, Tor; Nielsen, Lars Vendelbo

    2005-01-01

    Effects of film formation on carbon steel in hydrogen sulfide media may corrupt corrosion rate monitoring by electrochemical techniques. Electrochemical data from hydrogen sulfide solutions, biological sulfide media and natural sulfide containing geothermal water have been collected and the process...... of film formation in sulfide solutions was followed by video. It can be shown that capacitative and diffusional effects due to porous reactive deposits tend to dominate the data resulting in unreliable corrosion rates measured by electrochemical techniques. The effect is strongly increased if biofilm...... in combination with ferrous sulfide corrosion products cover the steel surface. Corrosion rates can be overestimated by a factor of 10 to 100 with electrochemical techniques - both by linear polarization resistance (LPR) and electrochemical impedance spectroscopy (EIS). Oxygen entering the system accelerates...

  2. Stress Corrosion Cracking Behavior of X80 Pipeline Steel in Acid Soil Environment with SRB

    Science.gov (United States)

    Wang, Dan; Xie, Fei; Wu, Ming; Liu, Guangxin; Zong, Yue; Li, Xue

    2017-06-01

    Self-designed experimental device was adopted to ensure the normal growth of sulphate-reducing bacteria (SRB) in sterile simulated Yingtan soil solution. Stress corrosion cracking (SCC) behavior of X80 pipeline steel in simulated acid soil environment was investigated by electrochemical impedance spectroscopy, slow strain rate test, and scanning electron microscope. Results show that the presence of SRB could promote stress corrosion cracking susceptibility. In a growth cycle, polarization resistance first presents a decrease and subsequently an increase, which is inversely proportional to the quantities of SRB. At 8 days of growth, SRB reach their largest quantity of 1.42 × 103 cells/g. The corrosion behavior is most serious at this time point, and the SCC mechanism is hydrogen embrittlement. In other SRB growth stages, the SCC mechanism of X80 steel is anodic dissolution. With the increasing SRB quantities, X80 steel is largely prone to SCC behavior, and the effect of hydrogen is considerably obvious.

  3. Effects of gaseous nitriding AISI4140 alloy steel on corrosion and hardness properties

    Science.gov (United States)

    Tamil Moli, L.; Wahab, N.; Gopinathan, M.; Karmegam, K.; Maniyarasi, M.

    2016-10-01

    Corrosion is one of the major problems in the industry especially on machinery since it weakens the structure of the machinery part and causes the mechanical failure. This will stop the production and increase the maintenance cost. In this study, the corrosion behaviour of gas nitriding on a screw press machine shaft made from AISI 4140 steel was investigated. Pitting corrosion was identified as a major cause of the shaft failure and this study was conducted to improve the corrosion resistance on the AISI 4140 alloy steel shaft by gas nitriding as a surface hardening treatment. Gas nitriding was performed with composition of 15% ammonia and 85% nitrogen at temperatures of 525 °C, 550 °C and 575 °C and with the soaking time of 30, 45 and 60 minutes, respectively. The samples were prepared as rectangular sized of 30mm x 12mm x 3mm for immersion testing. The results showed that corrosion rate of untreated samples was 77% higher compared to the nitrided samples. It was also found that hardness of the nitrided samples was higher than untreated sample. All in all, it can be concluded that gaseous nitriding can significantly improve the surface hardness and the corrosion resistance of the shaft made of AISI 4140 alloy steel, hence reduces the pitting that is the root cause of failure.

  4. Corrosion Mechanism and Bond-Strength Study on Galvanized Steel in Concrete Environment

    Energy Technology Data Exchange (ETDEWEB)

    Kouril, M.; Pokorny, P.; Stoulil, J. [University of Chemistry and Technology, Prague (Czech Republic)

    2017-04-15

    Zinc coating on carbon steels give the higher corrosion resistance in chloride containing environments and in carbonated concrete. However, hydrogen evolution accompanies the corrosion of zinc in the initial activity in fresh concrete, which can lead to the formation of a porous structure at the reinforcement -concrete interface, which can potentially reduce the bond-strength of the reinforcement with concrete. The present study examines the mechanism of the corrosion of hot-dip galvanized steel in detail, as in the model pore solutions and real concrete. Calcium ion plays an important role in the corrosion mechanism, as it prevents the formation of passive layers on zinc at an elevated alkalinity. The corrosion rate of galvanized steel decreases in accordance with the exposure time; however, the reason for this is not the zinc transition into passivity, but the consumption of the less corrosion-resistant phases of hot-dip galvanizing in the concrete environment. The results on the electrochemical tests have been confirmed by the bond-strength test for the reinforcement of concrete and by evaluating the porosity of the cement adjacent to the reinforcement.

  5. PITTING CORROSION OF AISI 316Ti STAINLESS STEEL WITH POLISHED SURFACE

    Directory of Open Access Journals (Sweden)

    Viera Zatkalíková

    2010-05-01

    Full Text Available AISI 316Ti is Cr–Ni–Mo austenitic stainless steel with the high Pitting Resistance Equivalent Number (PREN. The effect of the surface finishing by polishing on the pitting corrosion resistance was tested in aggressive 5% FeCl3 solution. The immersion tests were curried out at the temperature 30, 50, 80 °C. The electrochemical cyclic potentiodynamic tests were carried out in the same solution at temperature 30 and 50 °C. The evaluation of the corrosion resistance arose from the comparison of the results of the immersion and the cyclic potentiodynamic tests.

  6. Unexpected corrosion of stainless steel in low chloride waters – microbial aspects

    DEFF Research Database (Denmark)

    Hilbert, Lisbeth Rischel; Carpén, Leena; Møller, Per

    2009-01-01

    Abstract Stainless steels EN 1.4301 and 1.4401/1.4404 are normally considered corrosion resistant in low chloride natural waters like drinking water. However, a number of corrosion failures have been observed in e.g. fire extinguisher systems and drinking water installations, where stagnant...... in drinking water qualities, due to the formation of a biofilm. In itself, this is not enough to initiate pitting in these water qualities, but combined with a geometrically or metallurgically vulnerable area, corrosion may accelerate. The mechanism is linked to the naturally occurring microbial activity...

  7. Effect of Fe ion concentration on corrosion of carbon steel in CO2 environment

    DEFF Research Database (Denmark)

    Rogowska, Magdalena; Gudme, J.; Rubin, A.

    2016-01-01

    In this work, the corrosion behaviour of steel wires in solutions containing different concentrations of Fe2+ was investigated by the linear polarisation resistance method, while the evolution of pH was monitored in situ and changes of the Fe2+ concentration were monitored ex situ. Characterisation...... of the corrosion scales was performed using microscopic and diffraction techniques. Scale analysis revealed that the passivation of samples, exposed to initially highly Fe2+ supersaturated solution, occurred when a formation of a double layer took place, resulting in 30 times lower corrosion rate compared...... to samples tested in solutions without initial Fe2+....

  8. Effect of Fe ion concentration on corrosion of carbon steel in CO2 environment

    DEFF Research Database (Denmark)

    Rogowska, Magdalena; Gudme, J.; Rubin, A.

    2016-01-01

    In this work, the corrosion behaviour of steel wires in solutions containing different concentrations of Fe2+ was investigated by the linear polarisation resistance method, while the evolution of pH was monitored in situ and changes of the Fe2+ concentration were monitored ex situ. Characterisation...... of the corrosion scales was performed using microscopic and diffraction techniques. Scale analysis revealed that the passivation of samples, exposed to initially highly Fe2+ supersaturated solution, occurred when a formation of a double layer took place, resulting in 30 times lower corrosion rate compared...

  9. Corrosion of reinforcement bars in steel ibre reinforced concrete structures

    DEFF Research Database (Denmark)

    Solgaard, Anders Ole Stubbe

    Steel fibres have been known as an alternative to traditional reinforcement bars for special applications of structural concrete for decades and the use of steel fibre reinforced concrete (SFRC) has gradually increased in recent years. Steel fibres lead to reduced crack widths in concrete formed......, among other reasons, due to shrinkage and/or mechanical loading. Steel fibres are nowadays also used in combination with traditional reinforcement for structural concrete, where the role of the fibres is to minimize the crack widths whereas the traditional reinforcement bars are used for structural....... The aim of the work presented in this Ph.D. thesis was to quantify the influence of steel fibres on corrosion of traditional reinforcement bars embedded in uncracked concrete as well as cracked concrete. Focus of the work was set on the impact of steel fibres on corrosion propagation in uncracked concrete...

  10. Internal corrosion of carbon steel piping in hot aquifers service

    Directory of Open Access Journals (Sweden)

    Simičić Miloš V.

    2011-01-01

    Full Text Available Internal corrosion of carbon steel pipelines is a major problem encountered in water service. In terms of prediction of the remaining lifetime for water pipelines based on the corrosion allowance, the three main approaches are corrosion modelling, corrosion inhibitor availability, and corrosion monitoring. In this study we used two theoretical corrosion models, CASSANDRA and NORSOK M-506 of quite different origin in order to predict uniform corrosivity of hot aquifers in eight different pipelines. Because of the varying calculation criteria for the different models, these can give very different corrosion rate predictions for the same data input. This is especially true under conditions where the formation of protective films may occur, such as at elevated temperatures. The evaluation of models was conducted by comparison using weight-loss coupons and three corrosion inhibitors were obtained from commercial suppliers. The tests were performed during the 60-day period. Even though inhibitors’ efficiencies of 98% had been achieved in laboratory testing, inhibitors’ availabilities of 85% have been used due to logistics problems and other issues. The results, given in mmpy, i.e. millimeter per year, are very consistent with NORSOK M-506 prediction. This is presumably because the model considers the effect of the formation of a passive iron carbonate film at temperatures above 80 °C and significant reduction in corrosion rate. Corrosion inhibitor A showed a better performance than inhibitors B and C in all cases but the target corrosion rates of less than 0.1 mmpy were achieved for all inhibitors. The chemical type of corrosion inhibitor A is based on quaternary amines mixed with methanol, isopropyl alcohol, xylene and ethylbenzene. Based on the obtained results the carbon steel lifetime of 30 years, provided proper inhibitors are present and 3mm corrosion allowance, can be achieved for hot aquifers service with presented water compositions.

  11. Effect of thermal aging conditions on the corrosion properties and hardness of a duplex stainless steel

    Directory of Open Access Journals (Sweden)

    José Eduardo May

    2010-12-01

    Full Text Available The corrosion properties of a 22.5 wt. (% Cr duplex stainless steel were investigated after long-term aging of 3000, 5000 and 7000 hours at 300 and 400 ºC. The corrosion resistance was measured based on mass loss in a FeCl3 10 wt. (% solution and electrochemical measurements in a 0.1 M H2SO4 solution. The results indicate that the corrosion resistance decreased steadily up to 5000 hours of aging. However, the samples subjected to 7000 hours of aging showed better corrosion resistance than those aged for 3000 and 5000 hours. This effect is attributed to the phase transformation that occurs during aging, a finding which was confirmed by hardness, transmission electron microscopy and X-ray photoelectron spectroscopy measurements.

  12. Corrosion behavior induced by LiCl-KCl in type 304 and 316 stainless steel and copper at low temperature

    Energy Technology Data Exchange (ETDEWEB)

    Sim, Jee Hyung; Kim, Yong Soo; Cho, Il Je [Dept. of Nuclear Engineering, Hanyang University, Seoul (Korea, Republic of)

    2017-06-15

    The corrosion behavior of stainless steel (304 and 316 type) and copper induced by LiCl-KCl at low temperatures in the presence of sufficient oxygen and moisture was investigated through a series of experiments (at 30°C, 40°C, 60°C, and 80°C for 24 hours, 48 hours, 72 hours, and 96 hours). The specimens not coated on one side with an aqueous solution saturated with LiCl-KCl experienced no corrosion at any temperature, not even when the test duration exceeded 96 hours. Stainless steel exposed to LiCl-KCl experienced almost no corrosion below 40°C, but pitting corrosion was observed at temperatures above 60°C. As the duration of the experiment was increased, the rate of corrosion accelerated in proportion to the temperature. The 316 type stainless steel exhibited better corrosion resistance than did the 304 type. In the case of copper, the rate of corrosion accelerated in proportion to the duration and temperature but, unlike the case of stainless steel, the corrosion was more general. As a result, the extent of copper corrosion was about three times that of stainless steel.

  13. Corrosion behavior induced by LiCl-KCl in type 304 and 316 stainless steel and copper at low temperature

    Directory of Open Access Journals (Sweden)

    Jee-Hyung Sim

    2017-06-01

    Full Text Available The corrosion behavior of stainless steel (304 and 316 type and copper induced by LiCl-KCl at low temperatures in the presence of sufficient oxygen and moisture was investigated through a series of experiments (at 30°C, 40°C, 60°C, and 80°C for 24 hours, 48 hours, 72 hours, and 96 hours. The specimens not coated on one side with an aqueous solution saturated with LiCl-KCl experienced no corrosion at any temperature, not even when the test duration exceeded 96 hours. Stainless steel exposed to LiCl-KCl experienced almost no corrosion below 40°C, but pitting corrosion was observed at temperatures above 60°C. As the duration of the experiment was increased, the rate of corrosion accelerated in proportion to the temperature. The 316 type stainless steel exhibited better corrosion resistance than did the 304 type. In the case of copper, the rate of corrosion accelerated in proportion to the duration and temperature but, unlike the case of stainless steel, the corrosion was more general. As a result, the extent of copper corrosion was about three times that of stainless steel.

  14. Corrosion performance of zinc coated steel in seawater environment

    Science.gov (United States)

    Liu, Shuan; Zhao, Xia; Zhao, Haichao; Sun, Huyuan; Chen, Jianmin

    2017-03-01

    Considering the continuous exploitation of marine resources, it is very important to study the anticorrosion performance and durability of zinc coated streel (ZCS) because its increasing use as reinforcements in seawater. Tafel polarization curves and linear polarization curves combined with electrochemical impedance spectroscopy (EIS) were employed to evaluate the corrosion performance of ZCS at Qingdao test station during long-term immersion in seawater. The results indicated that the corrosion rate of the ZCS increased obviously with immersion time in seawater. The corrosion products that formed on the zinc coated steel were loose and porous, and were mainly composed of Zn5(OH)8Cl2, Zn5(OH)6(CO3)2, and ZnO. Pitting corrosion occurred on the steel surface in neutral seawater, and the rate of ZCS corrosion decreased with increasing pH.

  15. Corrosion resistance improvement of metals by excimer laser surface treatment

    Science.gov (United States)

    Autric, Michel L.; Perrais, Jacqueline; Barreau, Gerard

    2000-02-01

    KrF excimer laser has been used for physical and chemical transformations of metallic materials and coated metal samples. Aluminum alloys, steels and chromium coated mild steel have been treated under excimer laser radiation in order to improve their mechanical properties and their corrosion and oxidation resistance. The laser surface treatment leads, after surface remelting process, to important changes in the topography, the microstructure, the phases and the chemical composition of the near-surface region resulting in different hardness, wear properties and corrosion/oxidation behavior. We focus this paper on aluminum alloys (2000 and 6000 type) and steels irradiated using a krypton fluoride laser (20 ns, 0.5 - 10 J/cm2, up to 200 Hz) in laboratory air. The analysis were carried out by means of scanning electron microscopy, energy dispersive spectroscopy, coupled and low incidence angle X-ray diffraction, microhardness tester and electrochemical test equipments.

  16. Influence of Freeze-Thaw Damage on the Steel Corrosion and Bond-Slip Behavior in the Reinforced Concrete

    Directory of Open Access Journals (Sweden)

    Fangzhi Zhu

    2016-01-01

    Full Text Available This paper mainly studies the behavior of steel corrosion in various reinforced concrete under freeze-thaw environment. The influence of thickness of concrete cover is also discussed. Additionally, the bond-slip behavior of the reinforced concrete after suffering the freeze-thaw damage and steel corrosion has also be presented. The results show that the freeze-thaw damage aggravates the steel corrosion in concrete, and the results become more obvious in the concrete after suffering serious freeze-thaw damage. Compared with the ordinary concrete, both air entrained concrete and waterproofing concrete possess better resistance to steel corrosion under the same freeze-thaw environment. Moreover, increasing the thicknesses of concrete cover is also an effective method of improving the resistance to steel corrosion. The bond-slip behavior of reinforced concrete with corroded steel decreases with the increase of freeze-thaw damage, especially for the concrete that suffered high freeze-thaw cycles. Moreover, there exists a good correlation between the parameters of bond-slip and freeze-thaw cycles. The steel corrosion and bond-slip behavior of reinforced concrete should be considered serious under freeze-thaw cycles environment, which significantly impact the durability and safety of concrete structure.

  17. Pitting Corrosion Behaviour of New Corrosion-Resistant Reinforcement Bars in Chloride-Containing Concrete Pore Solution

    OpenAIRE

    Jiang, Jin-yang; Liu, Yao; Chu, Hong-yan; Wang, Danqian; Ma, Han; Sun, Wei

    2017-01-01

    In this study, the pitting behaviour of a new corrosion-resistant alloy steel (CR) is compared to that of low-carbon steel (LC) in a simulated concrete pore solution with a chloride concentration of 5 mol/L. The electrochemical behaviour of the bars was characterised using linear polarisation resistance (LPR) and electrochemical impedance spectroscopy (EIS). The pitting profiles were detected by reflective digital holographic microscopy (DHM), scanning electron microscopy (SEM), and the chemi...

  18. Influence of the surface finishing on electrochemical corrosion characteristics of AISI 316L stainless steel

    Directory of Open Access Journals (Sweden)

    Sylvia Dundeková

    2015-05-01

    Full Text Available Stainless steels from 316 group are very often and successfully uses for medical applications where the good mechanical and chemical properties in combination with non-toxicity of the material assure its safe and long term usage. Corrosion properties of AISI 361L stainless steel are strongly influenced by surface roughness and treatment of the engineering parts (specimens and testing temperature. Electrochemical characteristics of ground, mechanically polished and passivated AISI 316L stainless steel specimens were examined with the aim to identify the polarization resistance evolution due to the surface roughness decrease. Results obtained on mechanically prepared specimens where only natural oxide layer created due to the exposure of the material to the corrosion environment was protecting the materials were compared to the passivated specimens with artificial oxide layer. Also the influence of temperature and stabilization time before measurement were taken into account when discussing the obtained results. Positive influence of decreasing surface roughness was obtained as well as increase of polarization resistance due to the chemical passivation of the surface. Increase of the testing temperature and short stabilization time of the specimen in the corrosion environment were observed negatively influencing corrosion resistance of AISI 316L stainless steel.

  19. Electrochemical Corrosion Behavior of Spray-Formed Boron-Modified Supermartensitic Stainless Steel

    Science.gov (United States)

    Zepon, Guilherme; Nogueira, Ricardo P.; Kiminami, Claudio S.; Botta, Walter J.; Bolfarini, Claudemiro

    2017-04-01

    Spray-formed boron-modified supermartensitic stainless steel (SMSS) grades are alloys developed to withstand severe wear conditions. The addition of boron to the conventional chemical composition of SMSS, combined with the solidification features promoted by the spray forming process, leads to a microstructure composed of low carbon martensitic matrix reinforced by an eutectic network of M2B-type borides, which considerably increases the wear resistance of the stainless steel. Although the presence of borides in the microstructure has a very beneficial effect on the wear properties of the alloy, their effect on the corrosion resistance of the stainless steel was not comprehensively evaluated. The present work presents a study of the effect of boron addition on the corrosion resistance of the spray-formed boron-modified SMSS grades by means of electrochemical techniques. The borides fraction seems to have some influence on the repassivation kinetics of the spray-formed boron-modified SMSS. It was shown that the Cr content of the martensitic matrix is the microstructural feature deciding the corrosion resistance of this sort of alloys. Therefore, if the Cr content in the alloy is increased to around 14 wt pct to compensate for the boron consumed by the borides formation, the corrosion resistance of the alloy is kept at the same level of the alloy without boron addition.

  20. Analysis of features of stainless steels in dissimilar welded joints in chloride inducted corrosion

    Science.gov (United States)

    Topolska, S.; Łabanowski, J.

    2017-08-01

    Stainless steels of femtic-austenitic microstructure that means the duplex Cr-Ni-Mo steels, in comparison with austenitic steel includes less expensive nickel and has much better mechanical properties with good formability and corrosion resistance, even in environments containing chloride ions. Similar share of high chromium ferrite and austenite, which is characterized by high ductility, determines that the duplex steels have good crack resistance at temperatures up to approximately -40°C. The steels containing approximately 22% Cr, 5% Ni, 3% Mo and 0.2% N crystallizes as a solid solution δ, partially transforming from the temperature of about 1200°C to 850°C into the phase α. The stable structure of considered steels, at temperatures above 850°C, is ferrite, and at lower temperatures the mixture of phase γ+α +σ. The two-phase structure α+γ the duplex steel obtains after hyperquenching at the temperature of stability of the mixture of α+γ phases, and the share of the phases depends on the hyper quenching attributes. Hyperquenching in water, with a temperature close to 1200°C, ensures the instance in the microstructure of the steel a large share of ferrite and a small share of the high chromium austenite. This causes the increase of strength properties and reducing the plasticity of the steel and its resistance ability to cracking and corrosion. Slower cooling from the mentioned temperature, for example in the air, enables the partial transformation of the a phase into the γ one (α → γ) and increasing the share of austenite in the steel structure. It leads to improvement of plasticity properties. In the paper are presented the results of investigations of heteronymous welded joints of duplex steel and austenitic one. The results include the relation between the chemical composition of steels and their weldability.

  1. Effect of segregation bands on corrosion of steel plate for ship hull

    Directory of Open Access Journals (Sweden)

    M. Mazur

    2010-07-01

    Full Text Available Despite significant progress in the manufacturing of sheet metal ships carried both by optimizing the chemical compositions of steel mills as well as rolling and heat treatment, it still fails to remove the effects of persistent segregation. As a result we observed anisotropy of mechanical properties of the material which essentially complicates the process of construction for shipbuilding industry. Anisotropy of mechanical properties occurring in sheet metal hull is even more dangerous, that during their work, they are exposed to continuous exposure variable charges arising from sea surface waves. Another factor weakening the resistance to cracking metal ship is sea-water, which in the surface layer is highly aerated and very aggressive corrosion. The purpose of this study is to clarify the role of the segregation bands in the process of corrosion of low alloy steels used for ship hull. It was estimate a rate of corrosion in aerated sea water areas of the metal with or without segregation bands. After corrosion tests were made observations of specimens surfaces. Inside the segregation bands were found phosphorus. The contents of it were exceeded the average this element content in the steel. At the same time areas of the sheet metal with segregation bands were slowly corroded than areas without bands, although the changes of corrosion rate was similar in nature.Corrosion activity of rich in phosphorus segregation band is similar to phosphate corrosion inhibitors. These are effective in the presenceof chloride in seawater to form a protective layer that protects against corrosion segregation band. Under the observation on scanningelectron microscope there was no change in the appearance of surface samples after corrosion tests. A future direction of research will be estimate the stress corrosion in the same species – with and without segregation bands.

  2. Corrosion Behavior of Aqua-Blasted and Laser-Engraved Type 316L Stainless Steel

    Science.gov (United States)

    Krawczyk, B.; Cook, P.; Hobbs, J.; Engelberg, D. L.

    2017-11-01

    The effect of aqua blasting and laser engraving on surface microstructure development, residual stress and corrosion resistance of type 316L stainless steel has been investigated. Aqua blasting resulted in a deformed near-surface microstructure containing compressive residual stresses. Subsequent laser engraving produced a surface layer with tensile residual stresses reaching to a depth of 200 microns. Changes of surface roughness topography were accompanied by the development of a thick oxide/hydroxide film after laser engraving. The atmospheric corrosion behavior of all surfaces with MgCl2-laden droplets was compared to their electrochemical response in 1M NaCl and 0.7 M HCl aqueous solutions. The measured total volume loss after atmospheric corrosion testing was similar for all investigated surface conditions. Laser-engraved surface exhibited the smallest number of corrosion sites, but the largest mean corrosion depth.

  3. Forecasting of Corrosion Properties of Steel Wires for Production of Guide Wires for Cardiological Treatment

    Directory of Open Access Journals (Sweden)

    J. Przondziono

    2013-01-01

    Full Text Available The study presents evaluation of the influence of strain in drawing process and of surface modification on resistance to electrochemical corrosion of wires made of stainless steel for production of guide wires used in invasive cardiology. The results of static tensile test enabled us to determine the course of flow curve of wires made of X10CrNi 18-8 steel as well as mathematical form of flow stress function. Resistance to electrochemical corrosion was evaluated on the ground of registered anodic polarisation curves by means of potentiodynamic method. The tests were performed in solution simulating human blood on samples that were electrolytically polished and samples that were polished and then chemically passivated. Exemplary anodic polarisation curves were given. It was proved that with the applied strain, corrosion properties decrease. It was found that chemical passivation improves wire corrosion characteristics. Statistical analysis showed that there is a significant dependence between corrosion properties (polarisation resistance Rp and strain ε applied in drawing process. Functions that present the change Rp=f(ε were selected. The issue is of importance to guide wire manufacturers because application of the suggested methodology will enable us to forecast corrosion characteristics of wire with the required strength drawn with the applied strain.

  4. The maraging steel corrosion properties with hardening of different kinds after double aging

    Directory of Open Access Journals (Sweden)

    L. V. Tarasenko

    2014-01-01

    Full Text Available The paper proposes to use high-strength corrosion-resistant maraging steels, which were developed for aircraft industry instead of carbon steel with coating to improve operation properties of the forcemeasuring resilient member in electronic strain-gauge balance.It examines the possibility to apply the martensitic-aging steels of Fe-Cr-Ni-Mo-Ti (ЭП678 and Fe-Cr-Ni-Mo-Cu-Nb (ЭП817 alloying systems. It was shown, that a traditional heat strain-hardening treatment including hardening and overageing of this steels provides combination of durability viscosity and corrosion- resistance, but at the same time it increases nonelastic effects and lowers the limit of elasticity because of reversing austenite formation. In this connection, it was proposed to use hardening with double aging i.e. main and low-temperature aging with no austenite formation as heat strainhardening treatment of steels for force-measuring resilient member. The goal of this work was to study the influence of double aging on the structure and properties of ЭП678 (06Х14Н6Д2МБТ and ЭП817 (03Х111Н10М2Т steels.The modes of double aging for ЭП817 steel were conformed to 4500С + 400 0С and 475 0С+ 400 0С, for ЭП678 steel – 530 0С + 500 0С. The structure and properties of hardened steels after main and double aging were compared.Metallographic analysis of samples after electrolytic etching was conducted with Leitz Metallovert microscope while the CamScan 4DV raster electronic microscope was used for Microroentgen-spectral analysis. The quantity of austenite was controlled with computerized setting DRON-4, the hardness was measured with ТК-2М instrument, corrosion-resistance was estimated with polarized curves, which were taken using a П-5848 potentiostat.The conducted research has shown, that double aging causes the additional hardening of steels due to disintegration of martensite and formation of dispersed Cu – corpuscles in ЭП817 steel and of Ni3Ti

  5. Effect of Chromium on Corrosion Behavior of P110 Steels in CO2-H2S Environment with High Pressure and High Temperature

    Science.gov (United States)

    Sun, Jianbo; Sun, Chong; Lin, Xueqiang; Cheng, Xiangkun; Liu, Huifeng

    2016-01-01

    The novel Cr-containing low alloy steels have exhibited good corrosion resistance in CO2 environment, mainly owing to the formation of Cr-enriched corrosion film. In order to evaluate whether it is applicable to the CO2 and H2S coexistence conditions, the corrosion behavior of low-chromium steels in CO2-H2S environment with high pressure and high temperature was investigated using weight loss measurement and surface characterization. The results showed that P110 steel suffered localized corrosion and both 3Cr-P110 and 5Cr-P110 steels exhibited general corrosion. However, the corrosion rate of 5Cr-P110 was the highest among them. The corrosion process of the steels was simultaneously governed by CO2 and H2S. The outer scales on the three steels mainly consisted of FeS1−x crystals, whereas the inner scales on Cr-containing steels comprised of amorphous FeS1−x, Cr(OH)3 and FeCO3, in contrast with the amorphous FeS1−x and FeCO3 mixture film of P110 steel. The more chromium the steel contains, the more chromium compounds the corrosion products contain. The addition of chromium in steels increases the uniformity of the Cr-enriched corrosion scales, eliminates the localized corrosion, but cannot decrease the general corrosion rates. The formation of FeS1−x may interfere with Cr-enriched corrosion scales and lowering the corrosion performance of 3Cr-P110 and 5Cr-P110 steels. PMID:28773328

  6. Effect of Chromium on Corrosion Behavior of P110 Steels in CO2-H2S Environment with High Pressure and High Temperature

    Directory of Open Access Journals (Sweden)

    Jianbo Sun

    2016-03-01

    Full Text Available The novel Cr-containing low alloy steels have exhibited good corrosion resistance in CO2 environment, mainly owing to the formation of Cr-enriched corrosion film. In order to evaluate whether it is applicable to the CO2 and H2S coexistence conditions, the corrosion behavior of low-chromium steels in CO2-H2S environment with high pressure and high temperature was investigated using weight loss measurement and surface characterization. The results showed that P110 steel suffered localized corrosion and both 3Cr-P110 and 5Cr-P110 steels exhibited general corrosion. However, the corrosion rate of 5Cr-P110 was the highest among them. The corrosion process of the steels was simultaneously governed by CO2 and H2S. The outer scales on the three steels mainly consisted of FeS1−x crystals, whereas the inner scales on Cr-containing steels comprised of amorphous FeS1−x, Cr(OH3 and FeCO3, in contrast with the amorphous FeS1−x and FeCO3 mixture film of P110 steel. The more chromium the steel contains, the more chromium compounds the corrosion products contain. The addition of chromium in steels increases the uniformity of the Cr-enriched corrosion scales, eliminates the localized corrosion, but cannot decrease the general corrosion rates. The formation of FeS1−x may interfere with Cr-enriched corrosion scales and lowering the corrosion performance of 3Cr-P110 and 5Cr-P110 steels.

  7. Corrosion of mild steel, copper and brass in crude oil / seawater mixture

    Digital Repository Service at National Institute of Oceanography (India)

    PrabhaDevi, S.; Sawant, S.S.; Wagh, A.B.

    Mild steel, copper and brass coupons were introduced in natural seawater containing varying amount of crude oil. Mild steel showed higher rate of corrosion in seawater containing oil and lower corrosion rate in natural as well as artificial seawater...

  8. Investigation of Corrosion and Cathodic Protection in Reinforced Concrete. II : Properties of Steel Surface Layers

    NARCIS (Netherlands)

    Koleva, D.A.; De Wit, J.H.W.; Van Breugel, K.; Lodhi, Z.F.; Ye, G.

    2007-01-01

    The present study explores the formation of corrosion products on the steel surface (using as-received low carbon construction steel) in reinforced concrete in conditions of corrosion and subsequent transformation of these layers in conditions of cathodic protection (CP).

  9. Limit to corrosion fatigue strength evaluation of SAE1020 steel in acidic environment

    Directory of Open Access Journals (Sweden)

    William Mauricio Sanabria Becerra

    2015-01-01

    Full Text Available This paper shows the results of the research in terms of the evaluation of corrosion fatigue resistance of SAE1020 steel in acidic conditions, using as corrosive substance: acetate buffer with pH 2, 4 and 6. The fatigue tests were performed according to the model of cantilever rotating bending. The results were compared with the limit of fatigue resistance of the material tested in air. It was observed a significantly reduced limit with increasing acidity of the substance. Likewise, localized corrosion type filiform corrosion was observed on the surface material, caused by the effect of the specimen aerated to be partially submerged in rotation. Limits fatigue strength determined using staircase method recommended by standard ISO1143 and ISO12107, with confidence level of 50 % and a probability of failure of 10 %.Finally, the surfaces were analyzed to find multiple origins of fracture and crack propagation lengths related to the acidity of the medium.

  10. Corrosion inhibitor mechanisms on reinforcing steel in Portland cement pastes

    Science.gov (United States)

    Martin, Farrel James

    2001-07-01

    The mechanisms of corrosion inhibitor interaction with reinforcing steel are investigated in the present work, with particular emphasis on effects associated with corrosion inhibitors admixed into Portland cement paste. The principal objective in reinforcing steel corrosion inhibition for Portland cement concrete is observed to be preservation of the naturally passive steel surface condition established by the alkaline environment. Introduction of chloride ions to the steel surface accelerates damage to the passive film. Excessive damage to the passive film leads to loss of passivity and a destabilization of conditions that facilitate repair of the passive film. Passive film preservation in presence of chloride ions is achieved either through stabilization of the passive film or by modification of the chemical environment near the steel surface. Availability of inhibitors to the steel surface and their tendency to stabilize passive film defects are observed to be of critical importance. Availability of admixed corrosion inhibitors to the passive film is affected by binding of inhibitors during cement paste hydration. It is determined that pore solution concentrations of inorganic admixed inhibitors tend to be lower than the admixed concentration, while pore solution concentrations of organic admixed inhibitors tend to be higher than the admixed concentration. A fundamental difference of inhibitor function is observed between film-forming and defect stabilizing corrosion inhibitors. Experiments are conducted using coupons of reinforcing steel that are exposed to environments simulating chloride-contaminated Portland cement concrete. A study of the steel/cement paste interface is also performed, and compounds forming at this interface are identified using X-Ray diffraction.

  11. Initiation and inhibition of pitting corrosion on reinforcing steel under natural corrosion conditions

    Energy Technology Data Exchange (ETDEWEB)

    Abd El Wanees, S., E-mail: s_wanees@yahoo.com [Chemistry Department, Faculty of Science, University of Tabuk, Tabuk (Saudi Arabia); Chemistry Department, Faculty of Science, Zagazig University, Zagazig 44519 (Egypt); Bahgat Radwan, A. [Center for Advanced Materials, Qatar University, Doha 2713 (Qatar); Alsharif, M.A. [Chemistry Department, Faculty of Science, University of Tabuk, Tabuk (Saudi Arabia); Abd El Haleem, S.M. [Chemistry Department, Faculty of Science, Zagazig University, Zagazig 44519 (Egypt)

    2017-04-01

    Initiation and inhibition of pitting corrosion on reinforcing steel in saturated, naturally aerated Ca(OH){sub 2} solutions, under natural corrosion conditions, are followed through measurements of corrosion current, electrochemical impedance spectroscopy and SEM investigation. Induction period for pit initiation and limiting corrosion current for pit propagation are found to depend on aggressive salt anion and cation-types, as well as, concentration. Ammonium chlorides and sulfates are more corrosive than the corresponding sodium salts. Benzotriazole and two of its derivatives are found to be good inhibitors for pitting corrosion of reinforcing steel. Adsorption of these compounds follows a Langmuir adsorption isotherm. The thermodynamic functions ΔE{sup ∗}, ΔH{sup ∗} and ΔS{sup ∗} for pitting corrosion processes in the absence and presence of inhibitor are calculated and discussed. - Highlights: • Cl{sup −} and SO{sub 4} {sup 2-} induce pitting corrosion on passive reinforcing steel. • Initiation and propagation of pitting depend on cation and anion types. • Inhibition is based on adsorption according to Langmuir isotherm.

  12. Inhibition Effect of N, N'-Dimethylaminoethanol on the Pitting Corrosion Austenitic Stainless Steel Type 304

    Directory of Open Access Journals (Sweden)

    Roland Tolulope LOTO

    2015-11-01

    Full Text Available The electrochemical influence and corrosion inhibition of N, N'-dimethylaminoethanol on the pitting corrosion resistance of austenitic stainless steel (type 304 in dilute sulphuric acid solution with sodium chloride addition was investigated using potentiodynamic polarization technique. Corrosion potential, pitting potential, repassivation potential, nucleation resistance, passivation range and repassivation capacity measurements and potentiodynamic analysis were used to evaluate the steel’s pitting resistance characteristics. The potentiodynamic experiments revealed that pitting potential increased with increase in concentration of the inhibiting compound coupled with an increase in the passivation range hence increased resistance to pittinggcorrosion.  DOI: http://dx.doi.org/10.5755/j01.ms.21.4.8977

  13. Corrosion of Ferritic Steels in High Temperature Molten Salt Coolants for Nuclear Applications

    Energy Technology Data Exchange (ETDEWEB)

    Farmer, J; El-Dasher, B; de Caro, M S; Ferreira, J

    2008-11-25

    Corrosion of ferritic steels in high temperature molten fluoride salts may limit the life of advanced reactors, including some hybrid systems that are now under consideration. In some cases, the steel may be protected through galvanic coupling with other less noble materials with special neutronic properties such a beryllium. This paper reports the development of a model for predicting corrosion rates for various ferritic steels, with and without oxide dispersion strengthening, in FLiBe (Li{sub 2}BeF{sub 4}) and FLiNaK (Li-Na-K-F) coolants at temperatures up to 800 C. Mixed potential theory is used to account for the protection of steel by beryllium, Tafel kinetics are used to predict rates of dissolution as a function of temperature and potential, and the thinning of the mass-transfer boundary layer with increasing Reynolds number is accounted for with dimensionless correlations. The model also accounts for the deceleration of corrosion as the coolants become saturated with dissolved chromium and iron. This paper also reports electrochemical impedance spectroscopy of steels at their corrosion potentials in high-temperature molten salt environments, with the complex impedance spectra interpreted in terms of the interfacial charge transfer resistance and capacitance, as well as the electrolyte conductivity. Such in situ measurement techniques provide valuable insight into the degradation of materials under realistic conditions.

  14. Stress corrosion cracking behaviour of gas tungsten arc welded super austenitic stainless steel joints

    Directory of Open Access Journals (Sweden)

    M. Vinoth Kumar

    2015-09-01

    Full Text Available Super 304H austenitic stainless steel with 3% of copper posses excellent creep strength and corrosion resistance, which is mainly used in heat exchanger tubing of the boiler. Heat exchangers are used in nuclear power plants and marine vehicles which are intended to operate in chloride rich offshore environment. Chloride stress corrosion cracking is the most likely life limiting failure with austenitic stainless steel tubing. Welding may worsen the stress corrosion cracking susceptibility of the material. Stress corrosion cracking susceptibility of Super 304H parent metal and gas tungsten arc (GTA welded joints were studied by constant load tests in 45% boiling MgCl2 solution. Stress corrosion cracking resistance of Super 304H stainless steel was deteriorated by GTA welding due to the formation of susceptible microstructure in the HAZ of the weld joint and the residual stresses. The mechanism of cracking was found to be anodic path cracking, with transgranular nature of crack propagation. Linear relationships were derived to predict the time to failure by extrapolating the rate of steady state elongation.

  15. Corrosion Behavior of the Stressed Sensitized Austenitic Stainless Steels of High Nitrogen Content in Seawater

    Directory of Open Access Journals (Sweden)

    A. Almubarak

    2013-01-01

    Full Text Available The purpose of this paper is to study the effect of high nitrogen content on corrosion behavior of austenitic stainless steels in seawater under severe conditions such as tensile stresses and existence of sensitization in the structure. A constant tensile stress has been applied to sensitized specimens types 304, 316L, 304LN, 304NH, and 316NH stainless steels. Microstructure investigation revealed various degrees of stress corrosion cracking. SCC was severe in type 304, moderate in types 316L and 304LN, and very slight in types 304NH and 316NH. The electrochemical polarization curves showed an obvious second current peak for the sensitized alloys which indicated the existence of second phase in the structure and the presence of intergranular stress corrosion cracking. EPR test provided a rapid and efficient nondestructive testing method for showing passivity, degree of sensitization and determining IGSCC for stainless steels in seawater. A significant conclusion was obtained that austenitic stainless steels of high nitrogen content corrode at a much slower rate increase pitting resistance and offer an excellent resistance to stress corrosion cracking in seawater.

  16. Corrosion inhibition in drinking water: Effect of temperature. Part I. Galvanized steel. Inhibicion de la corrosion en agua potable. Efecto de la temperatura. I parte. Acero galvanizado

    Energy Technology Data Exchange (ETDEWEB)

    Royuela, J.J.

    1994-01-01

    The corrosivity of several drinking waters, with and without addition of sodium silicate and sodium polyphosphate as inhibitor, in contact with galvanized steel, is studied in the range 20-65 degree centigree. The corrosion rate in the course of time was followed by means of the polarization resistance method. Linearity between potential and intensity of current is observed in the range-20 to + 30 mV from corrosion potential E[sub 0]. Polarization curves were also drawn with the aim to obtain the Tafel slopes. E[sub 0] values are more active when inhibitor is present. With temperature increases corrosion rate. Inhibitor addition to the waters tested means a reduction of galvanized steel corrosion of about 40%. (Author) 30 refs.

  17. The Stress Corrosion Resistance and the Cryogenic Temperature Mechanical Behavior of 18-3 Mn (Nitronic 33) Stainless Steel Parent and Welded Material

    Science.gov (United States)

    Montano, J. W.

    1976-01-01

    The ambient and cryogenic temperature mechanical properties and the ambient temperature stress corrosion results of 18-3 Mn (Nitronic 33)stainless steel, longitudinal and transverse, as received and as welded (TIG) material specimens manufactured from 0.063 inch thick sheet material, were described. The tensile test results indicate an increase in ultimate tensile and yield strengths with decreasing temperature. The elongation remained fairly constant to -200 F, but below that temperature the elongation decreased to less than 6.0% at liquid hydrogen temperature. The notched tensile strength (NTS) for the parent metal increased with decreasing temperature to liquid nitrogen temperature. Below -320 F the NTS decreased rapidly. The notched/unnotched (N/U) tensile ratio of the parent material specimens remained above 0.9 from ambient to -200 F, and decreased to approximately 0.65 and 0.62, respectively, for the longitudinal and transverse directions at liquid hydrogen temperature. After 180 days of testing, only those specimens exposed to the salt spray indicated pitting and some degradation of mechanical properties.

  18. Corrosion of bare and galvanized steel in gypsum

    Directory of Open Access Journals (Sweden)

    Gómez, Mercedes

    1988-12-01

    Full Text Available Gypsum is a relatively low-cost building material much abounding in our country. When it is put in contact with steel, it may produce high corrosion rates due to its pH value (close to 7. This work reports the results obtained in studying the corrosion rates of bare and galvanized steel in contact with gypsum and plaster, as well as the influence curing thermal treatment applied to gypsum, enviromental relative humidity and addition of compounds with different natures and purposes may have in such process. In-situ observations, as well as the measurement of the Polarization Resistance and the weight loss have been used as measurement technics. From the results obtained it has been possible to deduce that galvanized steel has better behaviour in dry enviroments than bare steel in the same conditions and moist atmosphere induces proportionally more corrosion in galvanized steel than in bare one. Additions to gypsum do not modified these conclusions, though it may be pointed out that addition of nitrites or lime improves the behaviour of bare steel, while galvanized behaviour is not modified. The addition of lime is not recommended because phenomena of dilated along time expansion may take place.

    El yeso es un material de construcción de relativo bajo coste y que, además, es muy abundante en nuestro país. Debido a su pH cercano a la neutralidad, cuando entra en contacto con el acero, este puede corroerse a elevadas velocidades. En esta comunicación se presentan los resultados de un estudio sobre la velocidad de corrosión del acero desnudo y galvanizado en contacto con yeso y escayola y la influencia que tienen: el tratamiento térmico del curado del yeso, la humedad relativa ambiental y la adición de aditivos de diversa naturaleza y finalidad. Como técnicas de medida se han utilizado la medida de la Resistencia de Polarización y de la pérdida de peso, así como observaciones visuales. De los resultados se puede deducir que en

  19. Corrosion kinetics of 316L stainless steel bipolar plate with chromiumcarbide coating in simulated PEMFC cathodic environment

    Directory of Open Access Journals (Sweden)

    N.B. Huang

    Full Text Available Stainless steel with chromium carbide coating is an ideal candidate for bipolar plates. However, the coating still cannot resist the corrosion of a proton exchange membrane fuel cell (PEMFC environment. In this work, the corrosion kinetics of 316L stainless steel with chromium carbide is investigated in simulated PEMFC cathodic environment by combining electrochemical tests with morphology and microstructure analysis. SEM results reveal that the steel’s surface is completely coated by Cr and chromium carbide but there are pinholes in the coating. After the coated 316L stainless steel is polarized, the diffraction peak of Fe oxide is found. EIS results indicate that the capacitive resistance and the reaction resistance first slowly decrease (2–32 h and then increase. The potentiostatic transient curve declines sharply within 2000 s and then decreases slightly. The pinholes, which exist in the coating, result in pitting corrosion. The corrosion kinetics of the coated 316L stainless steel are modeled and accords the following equation: i0 = 7.6341t−0.5, with the corrosion rate controlled by ion migration in the pinholes. Keywords: PEMFC, Metal bipolar plate, Chromium carbide coating, Corrosion kinetics, Pitting corrosion

  20. Structure and corrosion properties of Cr coating deposited on aerospace bearing steel

    Science.gov (United States)

    Wang, Fangfang; Zhang, Fengxiang; Zheng, Lijing; Zhang, Hu

    2017-11-01

    The corrosion protection of chromium coating deposited on aerospace bearing steels by using the Filtered Cathodic Vacuum Arc deposition- Metal Evaporation Vacuum Arc duplex technique (MEVVA-FCVA) had been investigated. The protection efficiency of chromium coating on different substrate materials had also been evaluated. The chromium coating was mainly composed of nanocrystallineα-Cr in a range of 50-200 nm. The orientation distributions of α-Cr film on substrates with different composition had a certain difference to each other. Electrochemical experimental results indicated that the chromium coating significantly improved the corrosion resistance of experimental bearing steels in 3.5% NaCl solution. The protective efficiency of chromium films were all over 98%. The corrosion resistance of chromium coating was influenced by the chemical composition of substrate material. The chromium coatings on higher Cr-containing substrate displayed lower corrosion current density and more positive corrosion potential. The increase of passive film thickness and the formation of a mass of chromium oxide and hydroxide on the surface are responsible for the improved corrosion properties.

  1. Corrosion behaviour of AISI type 304L stainless steel in nitric acid media containing oxidizing species

    Energy Technology Data Exchange (ETDEWEB)

    Ningshen, S. [Corrosion Science and Technology Division, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102 (India); Kamachi Mudali, U., E-mail: kamachi@igcar.gov.i [Corrosion Science and Technology Division, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102 (India); Ramya, S.; Raj, Baldev [Corrosion Science and Technology Division, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102 (India)

    2011-01-15

    Research highlights: Corrosion behaviour of 304L stainless steel has been evaluated in the presence of oxidizing species in nitric acid medium. No significant change in corrosion potential even with increase in temperature and nitric acid concentration in presence of oxidizing ions. Faster passive film dissolution as indicated by low film polarization resistance, with increase in nitric acid concentration and temperature. The presence of oxidizing species further aggravates the corrosion of 304L SS along with increased temperature and nitric acid concentration. - Abstract: The corrosion behaviour of AISI type 304L stainless steel (SS) in different concentration of 0.01 M, 1 M and 5 M HNO{sub 3} in presence of oxidizing ions at different temperatures has been evaluated. The main objective of this study is to assess the corrosion resistance of type 304L SS in non-radioactive conditions encountered during storage of liquid nuclear waste. Electrochemical impedance spectroscopy (EIS) and laser Raman spectroscopy (LRS) has clearly brought out the deleterious effect of oxidizing species on the passive film leading to increased corrosion along with increase in HNO{sub 3} concentration and higher temperature.

  2. Corrosion of API XL 52 steel in presence of Clostridium celerecrescens

    Energy Technology Data Exchange (ETDEWEB)

    Monroy, O.A. Ramos; Ordaz, N. Ruiz; Ramirez, C. Juarez [Escuela Nacional de Ciencias Biologicas, Instituto Politecnico Nacional, Prolongacion de Carpio y Plan de Ayala, Mexico D. F., C. P. 11340 (Mexico); Gayosso, M.J. Hernandez; Olivares, G. Zavala [Instituto Mexicano del Petroleo, Grupo Corrosion, Eje Central Lazaro Cardenas 152, Col. San Bartolo Atepehuacan, Mexico D. F., C. P. 07730 (Mexico)

    2011-09-15

    During the characterization of sediments formed in pipelines transporting hydrocarbons, the knowledge of the microbiological diversity becomes very interesting, especially when it is related to microbiologically influenced corrosion (MIC). The presence of microorganisms is considered as one of the factors that affect the corrosion processes occurring at the pipeline; therefore, their corrosiveness must be determined. In this way, the identification of new species affecting the MIC processes is still considered relevant. In this work, the effect of Clostridium celerecrescens upon the corrosion of API KL 52 steel was evaluated. This microorganism was isolated and identified from the sediments collected during the inner cleaning procedures of a gas pipeline. The polarization resistance (PR) and electrochemical impedance spectroscopy (EIS) techniques were considered to estimate the microorganism behavior during the corrosion process. The results were complemented with a metal surface analysis, using a scanning electron microscope (SEM). The resistance values induced by the presence of the microorganisms clearly indicated that C. celerecrescens has an effect on the corrosion process occurring at the API XL 52 steel surface. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  3. Resistance microwelding of 316L stainless steel wire to block

    DEFF Research Database (Denmark)

    Friis, Kasper Storgaard; Khan, M.I.; Bay, Niels

    2011-01-01

    The excellent corrosion resistance of low carbon vacuum melted 316 stainless steel coupled with its non-magnetic properties makes it ideal for biomedical applications. The typical joint geometry for microcomponents, such as medical implants, includes joining of fine wire to a larger block. However...

  4. 21 CFR 178.3300 - Corrosion inhibitors used for steel or tinplate.

    Science.gov (United States)

    2010-04-01

    ... 21 Food and Drugs 3 2010-04-01 2009-04-01 true Corrosion inhibitors used for steel or tinplate... AIDS, AND SANITIZERS Certain Adjuvants and Production Aids § 178.3300 Corrosion inhibitors used for steel or tinplate. Corrosion inhibitors may be safely used for steel or tinplate intended for use in, or...

  5. Experimental Study on Rebar Corrosion Using the Galvanic Sensor Combined with the Electronic Resistance Technique

    Directory of Open Access Journals (Sweden)

    Yunze Xu

    2016-09-01

    Full Text Available In this paper, a new kind of carbon steel (CS and stainless steel (SS galvanic sensor system was developed for the study of rebar corrosion in different pore solution conditions. Through the special design of the CS and SS electronic coupons, the electronic resistance (ER method and zero resistance ammeter (ZRA technique were used simultaneously for the measurement of both the galvanic current and the corrosion depth. The corrosion processes in different solution conditions were also studied by linear polarization resistance (LPR and the measurements of polarization curves. The test result shows that the galvanic current noise can provide detailed information of the corrosion processes. When localized corrosion occurs, the corrosion rate measured by the ER method is lower than the real corrosion rate. However, the value measured by the LPR method is higher than the real corrosion rate. The galvanic current and the corrosion current measured by the LPR method shows linear correlation in chloride-containing saturated Ca(OH2 solution. The relationship between the corrosion current differences measured by the CS electronic coupons and the galvanic current between the CS and SS electronic coupons can also be used to evaluate the localized corrosion in reinforced concrete.

  6. Experimental Study on Rebar Corrosion Using the Galvanic Sensor Combined with the Electronic Resistance Technique

    Science.gov (United States)

    Xu, Yunze; Li, Kaiqiang; Liu, Liang; Yang, Lujia; Wang, Xiaona; Huang, Yi

    2016-01-01

    In this paper, a new kind of carbon steel (CS) and stainless steel (SS) galvanic sensor system was developed for the study of rebar corrosion in different pore solution conditions. Through the special design of the CS and SS electronic coupons, the electronic resistance (ER) method and zero resistance ammeter (ZRA) technique were used simultaneously for the measurement of both the galvanic current and the corrosion depth. The corrosion processes in different solution conditions were also studied by linear polarization resistance (LPR) and the measurements of polarization curves. The test result shows that the galvanic current noise can provide detailed information of the corrosion processes. When localized corrosion occurs, the corrosion rate measured by the ER method is lower than the real corrosion rate. However, the value measured by the LPR method is higher than the real corrosion rate. The galvanic current and the corrosion current measured by the LPR method shows linear correlation in chloride-containing saturated Ca(OH)2 solution. The relationship between the corrosion current differences measured by the CS electronic coupons and the galvanic current between the CS and SS electronic coupons can also be used to evaluate the localized corrosion in reinforced concrete. PMID:27618054

  7. Corrosion behaviour of some conventional stainless steels in electrolyzing process

    Directory of Open Access Journals (Sweden)

    Amal NASSAR

    2015-12-01

    Full Text Available In this study, attempts were made to increase the amount of hydrogen generated from the water electrolysis process. Some conventional stainless steels (316; 409; 410 and 430 were used as anode and cathode in electrolysis process. Further study was carried out on the corrosion trend in all the investigated metals. It is observed that the electrode material can effect on the amount of hydrogen generate by electrolyzing process and metal composition of the stainless steels effects on the rate of corrosion.

  8. Micro-Abrasion Wear Resistance of Borided 316L Stainless Steel and AISI 1018 Steel

    Science.gov (United States)

    Reséndiz-Calderon, C. D.; Rodríguez-Castro, G. A.; Meneses-Amador, A.; Campos-Silva, I. E.; Andraca-Adame, J.; Palomar-Pardavé, M. E.; Gallardo-Hernández, E. A.

    2017-11-01

    The 316L stainless steel has high corrosion resistance but low tribological performance. In different industrial sectors (biomedical, chemical, petrochemical, and nuclear engineering), improvement upon wear resistance of 316L stainless steel components using accessible and inexpensive methods is critical. The AISI 1018 steel is widely used in industry, but its tribological performance is not the best among steels. Therefore, in this study the behavior of the borided 316L stainless steel and 1018 steel is evaluated under micro-abrasion wear. The boriding was carried out at 1223 K over 6 h of exposure time, resulting in a biphase layer composed of FeB/Fe2B phases. In order to evaluate Fe2B phase with no influence from FeB phase, AISI 1018 steel samples were borided at 1273 K for over 20 min and then diffusion annealed at 1273 K over 2 h to obtain a Fe2B mono-phase layer. Micro-abrasion wear resistance was evaluated by a commercial micro-abrasion testing rig using a mix of F-1200 SiC particles with deionized water as abrasive slurry. The obtained wear rates for FeB and Fe2B phases and for the 316L stainless steel were compared. Wear resistance of 316L stainless steel increases after boriding. The wear mechanisms for both phases and for the stainless steel were identified. Also, transient conditions for rolling and grooving abrasion were determined for the FeB and Fe2B phases.

  9. Micro-Abrasion Wear Resistance of Borided 316L Stainless Steel and AISI 1018 Steel

    Science.gov (United States)

    Reséndiz-Calderon, C. D.; Rodríguez-Castro, G. A.; Meneses-Amador, A.; Campos-Silva, I. E.; Andraca-Adame, J.; Palomar-Pardavé, M. E.; Gallardo-Hernández, E. A.

    2017-10-01

    The 316L stainless steel has high corrosion resistance but low tribological performance. In different industrial sectors (biomedical, chemical, petrochemical, and nuclear engineering), improvement upon wear resistance of 316L stainless steel components using accessible and inexpensive methods is critical. The AISI 1018 steel is widely used in industry, but its tribological performance is not the best among steels. Therefore, in this study the behavior of the borided 316L stainless steel and 1018 steel is evaluated under micro-abrasion wear. The boriding was carried out at 1223 K over 6 h of exposure time, resulting in a biphase layer composed of FeB/Fe2B phases. In order to evaluate Fe2B phase with no influence from FeB phase, AISI 1018 steel samples were borided at 1273 K for over 20 min and then diffusion annealed at 1273 K over 2 h to obtain a Fe2B mono-phase layer. Micro-abrasion wear resistance was evaluated by a commercial micro-abrasion testing rig using a mix of F-1200 SiC particles with deionized water as abrasive slurry. The obtained wear rates for FeB and Fe2B phases and for the 316L stainless steel were compared. Wear resistance of 316L stainless steel increases after boriding. The wear mechanisms for both phases and for the stainless steel were identified. Also, transient conditions for rolling and grooving abrasion were determined for the FeB and Fe2B phases.

  10. Research on corrosion mechanism of suspension insulator steel foot of direct current system and measures for corrosion inhibition

    Science.gov (United States)

    Chen, He; Yang, Yueguang; Su, Guolei; Wang, Xiaoqing; Zhang, Hourong; Sun, Xiaoyu; Fan, Youping

    2017-09-01

    There are increasingly serious electrocorrosion phenomena on insulator hardware caused by direct current transmission due to the wide-range popularization of extra high voltage direct current transmission engineering in our country. Steel foot corrosion is the main corrosion for insulators on positive polarity side of transmission lines. On one hand, the corrosion leads to the tapering off of steel foot diameter, having a direct influence on mechanical property of insulators; on the other hand, in condition of corrosion on steel foot wrapped in porcelain ware, the volume of the corrosion product is at least 50% more than that of the original steel foot, leading to bursting of porcelain ware, threatening safe operation of transmission lines. Therefore, it is necessary to conduct research on the phenomenon and propose feasible measures for corrosion inhibition. Starting with the corrosion mechanism, this article proposes two measures for corrosion inhibition, and verifies the inhibition effect in laboratory conditions, providing reference for application in engineering.

  11. Corrosion by concentrated sulfuric acid in carbon steel pipes and tanks: state of the art

    Energy Technology Data Exchange (ETDEWEB)

    Panossian, Zehbour; Almeida, Neusvaldo Lira de; Sousa, Raquel Maria Ferreira de [Instituto de Pesquisas Tecnologicas (IPT), Sao Paulo, SP (Brazil); Pimenta, Gutemberg de Souza [PETROBRAS S.A., Rio de Janeiro, RJ (Brazil). Centro de Pesquisas e Desenvolvimento (CENPES); Marques, Leandro Bordalo Schmidt [PETROBRAS Engenharia, Rio de Janeiro, RJ (Brazil)

    2009-07-01

    PETROBRAS, allied to the policy of reduction of emission of pollutants, has been adjusting the processes of the new refineries to obtain products with lower sulfur content. Thus, the sulfur dioxide, extracted from the process gases of a new refinery to be built in the Northeast, will be used to produce sulfuric acid with concentration between (94-96) %. This acid will be stored in carbon steel tanks and transported through a buried 8-km carbon steel pipe from the refinery to a pier, where it will be loaded onto ships and sent to the consumer markets. Therefore, the corrosion resistance of carbon steel by concentrated acid will become a great concern for the mentioned storage and transportation. When the carbon steel comes into contact with concentrated sulfuric acid, there is an immediate acid attack with the formation of hydrogen gas and ferrous ions which, in turn, forms a protective layer of FeSO{sub 4} on the metallic surface. The durability of the tanks and pipes made of carbon steel will depend on the preservation of this protective layer. This work presents a review of the carbon steel corrosion in concentrated sulfuric acid and discusses the preventive methods against this corrosion, including anodic protection. (author)

  12. Threshold Corrosion Fatigue of Welded Shipbuilding Steels.

    Science.gov (United States)

    1992-01-01

    8. J. C. Walter, E. Olbjorn, 0. Allstad and G. Elde, "Safety Against Corrosion Fatigue Offshore," Publication No. 94, Det Norske Ventas , Horik...Offshore. Publication No;. 94;, Det Norske Ventas , Horik, Norway, April 1976. 18. C. E. Jaske, D. Broek, J. E. Slater, W. E. Anderson. Corrosion Fatigue

  13. The effect of radiation on the anaerobic corrosion of steel

    Science.gov (United States)

    Smart, N. R.; Rance, A. P.; Werme, L. O.

    2008-09-01

    To ensure the safe encapsulation of spent nuclear fuel elements for geological disposal, SKB of Sweden are considering using a canister, which consists of an outer copper canister and a cast iron insert. Previous work has investigated the rate of gas generation due to the anaerobic corrosion of ferrous materials over a range of conditions. This paper examines the effect of radiation on the corrosion of steel in repository environments. Tests were carried out at two temperatures (30 °C and 50 °C), two dose rates (11 Gray h -1 and 300 Gray h -1) and in two different artificial groundwaters, for exposure periods of several months. Radiation was found to enhance the corrosion rate at both dose rates but the greatest enhancement occurred at the higher dose rate. The corrosion products were predominantly magnetite, with some indications of unidentified higher oxidation state corrosion products being formed at the higher dose rates.

  14. 3DII implantation effect on corrosion properties of the AISI/SAE 1020 steel

    Energy Technology Data Exchange (ETDEWEB)

    Dulce M., H.J.; Rueda V., Alejandro [Universidad Francisco de Paula Santander, A.A. 1055, Cucuta (Colombia); Dougar-Jabon, Valeri [Universidad Industrial de Santander, A.A. 678, Bucaramanga (Colombia)

    2005-08-01

    The three dimensional ion implantation technology (3DII) is one of the methods of improving the tribological characteristics and resistance to hydrogen embrittlement processes in metals. In this report, some results concerning the resistance effect of nitrogen ion implantation to oxidation of the sample, made of AISI/SAE 1020 steel, are given. The nitrogen ions were implanted in the discharge chamber of the JUPITER reactor. Both the treated and untreated samples were tested through potential-static measurements, which permitted to determine the corrosion current, the slopes that characterise the braking level of anode and cathode reactions. The polarization resistance near the corrosion potential is calculated. The results of the study encourage to consider the nitrogen ion implantation in high voltage and low pressure discharges as one of the methods of anticorrosive protection which do not change the geometric configuration of the treated steel pieces. (copyright 2005 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  15. 3DII implantation effect on corrosion properties of the AISI/SAE 1020 steel

    Science.gov (United States)

    Dulcé M., Héctor J.; Rueda v., Alejandro; Dougar-Jabon, Valeri

    2005-08-01

    The three dimensional ion implantation technology (3DII) is one of the methods of improving the tribological characteristics and resistance to hydrogen embrittlement processes in metals. In this report, some results concerning the resistance effect of nitrogen ion implantation to oxidation of the sample, made of AISI/SAE 1020 steel, are given. The nitrogen ions were implanted in the discharge chamber of the JUPITER reactor. Both the treated and untreated samples were tested through potential-static measurements, which permitted to determine the corrosion current, the slopes that characterise the braking level of anode and cathode reactions. The polarization resistance near the corrosion potential is calculated. The results of the study encourage to consider the nitrogen ion implantation in high voltage and low pressure discharges as one of the methods of anticorrosive protection which do not change the geometric configuration of the treated steel pieces.

  16. Corrosion Behavior of Active Screen Plasma Nitrided 38CrMoAl Steel under Marine Environment

    Science.gov (United States)

    Yang, Li; He, Yongyong; Mao, JunYuan; Zhang, Lei

    2017-10-01

    The 38CrMoAl steels were nitrided at different temperatures for 7 h using active screen plasma discharge. The analysis showed that the thick compound layer composed of ε-Fe2–3N and γ‧-Fe4N was formed on the surface. The corrosion behavior was evaluated by measuring the anodic polarization curves in natural sea water (similar 3.5% NaCl solution), and observation of corroded surface were conducted. The electromechanical measurements indicated that the corrosion potential of the nitrided specimens shifted to a nobler value compared to that of untreated specimens. Passive regions were also observed in the polarization curves for all the nitrided specimens. These results indicate that active screen plasma nitriding can enhance the corrosion resistance of the 38CrMoAl steel under marine environment.

  17. Thiosemicarbazide and thiocarbohydrazide functionalized chitosan as ecofriendly corrosion inhibitors for carbon steel in hydrochloric acid solution.

    Science.gov (United States)

    Chauhan, Dheeraj Singh; Ansari, K R; Sorour, A A; Quraishi, M A; Lgaz, H; Salghi, R

    2017-10-10

    Organically functionalized chitosan macromolecules namely Chitosan-Thiosemicarbazide (CS-TS) and Chitosan-Thiocarbohydrazide (CS-TCH) were synthesized and evaluated as new corrosion inhibitors for mild steel corrosion in 1M HCl. The FTIR and (1)H NMR studies confirmed the formation of the derivatives. The corrosion tests were performed using weight loss method, electrochemical measurements, surface morphology (AFM), quantum chemical investigation and molecular dynamics simulation methods. The maximum efficiency of 92% was obtained at a concentration as low as 200mgL(-1). The inhibitors were found to obey Langmuir adsorption isotherm and exhibited both physical and chemical adsorption. Electrochemical impedance spectroscopy (EIS) results showed an increase in polarization resistance which supported the adsorption of inhibitors on the mild steel surface. Tafel data showed a mixed type behavior with cathodic predominance. The data of quantum chemical calculations and molecular dynamics simulation supported the experimental findings. Copyright © 2017 Elsevier B.V. All rights reserved.

  18. Stress Corrosion-Cracking and Corrosion Fatigue Impact of IZ-C17+ Zinc Nickel on 4340 Steel

    Science.gov (United States)

    2017-05-17

    REPORT NO: NAWCADPAX/TIM-2016/189 STRESS CORROSION-CRACKING AND CORROSION FATIGUE IMPACT OF IZ-C17+ ZINC-NICKEL ON 4340 STEEL by...DEPARTMENT OF THE NAVY NAVAL AIR WARFARE CENTER AIRCRAFT DIVISION PATUXENT RIVER, MARYLAND NAWCADPAX/TIM-2016/189 STRESS ...5a. CONTRACT NUMBER STRESS CORROSION-CRACKING AND CORROSION FATIGUE IMPACT OF IZ-C17+ ZINC-NICKEL ON 4340 STEEL 5b. GRANT NUMBER 5c. PROGRAM

  19. Pitting Corrosion Susceptibility of AISI 301 Stainless Steel in ...

    African Journals Online (AJOL)

    The susceptibility of austenitic (AISI 301) stainless steel to pitting corrosion was evaluated in sodium chloride (NaCl) solutions - 0.1M, 0.2M, 0.3M, 0.5M and 0.7M and 1.0M. Tensile tests and microscopic examinations were performed on samples prepared from the steel after exposure in the various environments.

  20. Effects of Immersion Time and 5-Phenyl-1H-tetrazole on the Corrosion and Corrosion Mitigation of Cobalt Free Maraging Steel in 0.5 M Sulfuric Acid Pickling Solutions

    Directory of Open Access Journals (Sweden)

    El-Sayed M. Sherif

    2013-01-01

    Full Text Available The effect of exposure time and 5-phenyl-1H-tetrazole on the corrosion and corrosion mitigation of cobalt free maraging steel in 0.5 M H2SO4 pickling solutions has been reported using electrochemical and spectroscopic investigations. Potentiodynamic polarization data showed that the increase of immersion time from 0 min to 120 min increases the corrosion rate and decreases the polarization resistance of the maraging steel. On the other hand, the addition of PHTA and the increase of its concentration decrease all the corrosion parameters of the steel at all exposure test periods. Electrochemical impedance spectroscopy measurements agreed with the obtained polarization data. Scanning electron spectroscopy and energy dispersive X-ray investigations confirmed that the inhibition of the steel corrosion is achieved via the adsorption of the PHTA molecules onto the steel precluding its surface from being dissolved.

  1. Nano-silicate inhibitor derived from rice husk for corrosion mitigation of steel in distilled water

    Science.gov (United States)

    Asra, Denni; Othman, Norinsan Kamil; Dasuki, Zulhusni

    2017-05-01

    Nanosilicate extracts from rice husk (Oryza sativa L.) ash (RHA) as a corrosion inhibitor for carbon steel in distilled water has been investigated. The nanosilicates extracted from RHA was obtained through wet chemical extraction and the extracted nanosilicates powder were analyzed using Fourier Transform Infrared Spectroscopy (FTIR) in order to identify the presence of functional groups (SiO2) that contributed to the inhibition process. The particle size of extracted nanosilica is in the range of 5-10 nm and it was confirmed through Transmission electron microscopy (TEM) and Zeta Sizer analysis. The corrosion measurement study on the effect of nanosilicate from RHA on carbon steel samples in distilled water as corrosive media had been conducted by employing weight loss method, potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), surface analysis, and adsorption isotherm study. It was proven that the maximum inhibition efficiency (IE %) obtained through corrosion measurement were up to 98 % of inhibition. On the other hand, the adsorption of inhibitor on the carbon steel surface was found to follow Temkin isotherm. Based on the result of potentiodynamic polarization, it showed that inhibitors are mixed type. The results of EIS showed that value of charge transfer resistance and the percentage of inhibition efficiency increased with the increasing of nanosilicate concentration. Surface analysis on specimen that was treated with nanosilicate were smoother with fewer corrosion products compared to untreated specimen.

  2. Corrosion of Aluminized and Uncoated 9-12% Cr Boiler Steels in Simulated Biomass andWaste Combustion Conditions

    Science.gov (United States)

    Metsäjoki, Jarkko; Huttunen-Saarivirta, Elina; Lepistö, T.

    2011-04-01

    Coatings are seen a promising way to improve the corrosion resistance of relatively cheap power plant steels to enable higher steam temperatures than currently in use. In this research, 9-12% Cr steels P91 and HCM12A are coated with aluminium diffusion coating by a slurry method and exposed for 336 hours at 833 K and 883 K to atmospheres containing varying amounts of O2, H2O, HCl and SO2. Corrosion behaviour of the coated steels is compared to that of those steels in an uncoated condition. Characterization is performed by weighing, SEM + EDS and XRD. The results show that corrosion resistance of P91 and HCM12A is significantly improved by the aluminium diffusion coating at high temperatures in atmospheres containing HCl and SO2. The corrosion rate of the aluminized specimens slightly increases with increase in test temperature but remains virtually the same irrespective of the composition of the atmosphere. On the other hand, the corrosion rate of the uncoated specimens is dependent on both the atmosphere and the temperature. The steels undergo active oxidation that results in formation of non-protective, thick and layered scales in HCl containing atmospheres. SO2 addition slightly decreases the corrosion rate although it is anyway higher than that in SO2 containing atmosphere without HCl.

  3. Anodic Oxidation of Carbon Steel at High Current Densities and Investigation of Its Corrosion Behavior

    Science.gov (United States)

    Fattah-Alhosseini, Arash; Khan, Hamid Yazdani

    2017-06-01

    This work aims at studying the influence of high current densities on the anodization of carbon steel. Anodic protective coatings were prepared on carbon steel at current densities of 100, 125, and 150 A/dm2 followed by a final heat treatment. Coatings microstructures and morphologies were analyzed using X-ray diffraction (XRD) and scanning electron microscope (SEM). The corrosion resistance of the uncoated carbon steel substrate and the anodic coatings were evaluated in 3.5 wt pct NaCl solution through electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization measurements. The results showed that the anodic oxide coatings which were prepared at higher current densities had thicker coatings as a result of a higher anodic forming voltage. Therefore, the anodized coatings showed better anti-corrosion properties compared to those obtained at lower current densities and the base metal.

  4. Effect of Niobium on Phase Transformations, Mechanical Properties and Corrosion of Supermartensitic Stainless Steel

    Science.gov (United States)

    de Oliveira, Mariana Perez; Calderón-Hernández, José Wilmar; Magnabosco, Rodrigo; Hincapie-Ladino, Duberney; Alonso-Falleiros, Neusa

    2017-04-01

    The influence of niobium addition in a supermartensitic stainless steel with 13Cr-5Ni-2Mo has been studied. The steel with Nb tempered at 600 °C for 2 h showed improved mechanical resistance properties and lower degree of sensitization, without compromising elongation and pitting corrosion resistance, when compared to the reference steel. In order to understand the Nb effect in such steel, mainly regarding phase transformation, different tempering time intervals have been studied. The better performance of the SM2MoNb is attributed to the hindering effect that Nb has in the kinetics of the phase transformations during tempering, delaying the precipitation start and coarsening stages of the present phases.

  5. A simple and reliable setup for monitoring corrosion rate of steel rebars in concrete.

    Science.gov (United States)

    Ahmad, Shamsad; Jibran, Mohammed Abdul Azeem; Azad, Abul Kalam; Maslehuddin, Mohammed

    2014-01-01

    The accuracy in the measurement of the rate of corrosion of steel in concrete depends on many factors. The high resistivity of concrete makes the polarization data erroneous due to the Ohmic drop. The other source of error is the use of an arbitrarily assumed value of the Stern-Geary constant for calculating corrosion current density. This paper presents the outcomes of a research work conducted to develop a reliable and low-cost experimental setup and a simple calculation procedure that can be utilised to calculate the corrosion current density considering the Ohmic drop compensation and the actual value of the Stern-Geary constants calculated using the polarization data. The measurements conducted on specimens corroded to different levels indicate the usefulness of the developed setup to determine the corrosion current density with and without Ohmic drop compensation.

  6. Effect of Secondary Phase Precipitation on the Corrosion Behavior of Duplex Stainless Steels

    Directory of Open Access Journals (Sweden)

    Kai Wang Chan

    2014-07-01

    Full Text Available Duplex stainless steels (DSSs with austenitic and ferritic phases have been increasingly used for many industrial applications due to their good mechanical properties and corrosion resistance in acidic, caustic and marine environments. However, DSSs are susceptible to intergranular, pitting and stress corrosion in corrosive environments due to the formation of secondary phases. Such phases are induced in DSSs during the fabrication, improper heat treatment, welding process and prolonged exposure to high temperatures during their service lives. These include the precipitation of sigma and chi phases at 700–900 °C and spinodal decomposition of ferritic grains into Cr-rich and Cr-poor phases at 350–550 °C, respectively. This article gives the state-of the-art review on the microstructural evolution of secondary phase formation and their effects on the corrosion behavior of DSSs.

  7. Effect of Secondary Phase Precipitation on the Corrosion Behavior of Duplex Stainless Steels

    Science.gov (United States)

    Chan, Kai Wang; Tjong, Sie Chin

    2014-01-01

    Duplex stainless steels (DSSs) with austenitic and ferritic phases have been increasingly used for many industrial applications due to their good mechanical properties and corrosion resistance in acidic, caustic and marine environments. However, DSSs are susceptible to intergranular, pitting and stress corrosion in corrosive environments due to the formation of secondary phases. Such phases are induced in DSSs during the fabrication, improper heat treatment, welding process and prolonged exposure to high temperatures during their service lives. These include the precipitation of sigma and chi phases at 700–900 °C and spinodal decomposition of ferritic grains into Cr-rich and Cr-poor phases at 350–550 °C, respectively. This article gives the state-of the-art review on the microstructural evolution of secondary phase formation and their effects on the corrosion behavior of DSSs. PMID:28788129

  8. POLYETHERSULFONE COATING FOR MITIGATING CORROSION OF STEEL IN GEOTHERMAL ENVIRONMENT.

    Energy Technology Data Exchange (ETDEWEB)

    SUGAMA, T.

    2005-06-01

    Emphasis was directed toward evaluating the usefulness of a polyethersulfone (PES)-dissolved N-methyl pyrrolidone (NMP) solvent precursor as a low-temperature film-forming anti-corrosion coating for carbon steel in simulated geothermal environments at brine temperatures up to 300 C. A {approx} 75 {micro}m thick PES coating performed well in protecting the steel against corrosion in brine at 200 C. However, at {>=} 250 C, the PES underwent severe hydrothermal oxidation that caused the cleavage of sulfone- and ether-linkages, and the opening of phenyl rings. These, in turn, led to sulfone {yields} benzosulfonic acid and ether {yields} benzophenol-type oxidation derivative transformations, and the formation of carbonyl-attached open rings, thereby resulting in the incorporation of the functional groups, hydroxyl and carbonyl, into the coating. The presence of these functional groups raised concerns about the diminutions in water-shedding and water-repellent properties that are important properties of the anti-corrosion coatings; such changes were reflected in an enhancement of the magnitude of susceptibility of the coatings surfaces to moisture. Consequently, the disintegration of the PES structure by hydrothermal oxidation was detrimental to the maximum efficacy of the coating in protecting the steel against corrosion, allowing the corrosive electrolytes to infiltrate easily through it.

  9. Treatment Prevents Corrosion in Steel and Concrete Structures

    Science.gov (United States)

    2007-01-01

    In the mid-1990s, to protect rebar from corrosion, NASA developed an electromigration technique that sends corrosion-inhibiting ions into rebar to prevent rust, corrosion, and separation from the surrounding concrete. Kennedy Space Center worked with Surtreat Holding LLC, of Pittsburgh, Pennsylvania, a company that had developed a chemical option to fight structural corrosion, combining Surtreat's TPS-II anti-corrosive solution and electromigration. Kennedy's materials scientists reviewed the applicability of the chemical treatment to the electromigration process and determined that it was an effective and environmentally friendly match. Ten years later, NASA is still using this approach to fight concrete corrosion, and it has also developed a new technology that will further advance these efforts-a liquid galvanic coating applied to the outer surface of reinforced concrete to protect the embedded rebar from corrosion. Surtreat licensed this new coating technology and put it to use at the U.S. Army Naha Port, in Okinawa, Japan. The new coating prevents corrosion of steel in concrete in several applications, including highway and bridge infrastructures, piers and docks, concrete balconies and ceilings, parking garages, cooling towers, and pipelines. A natural compliment to the new coating, Surtreat's Total Performance System provides diagnostic testing and site analysis to identify the scope of problems for each project, manufactures and prescribes site-specific solutions, controls material application, and verifies performance through follow-up testing and analysis.

  10. Microgalvanic corrosion of laser-welded HSLA steels

    NARCIS (Netherlands)

    De Wit, J.H.; Looi, Y.M.

    Laser welding of galvanized high strength low alloy (HSLA) steels leads to the evaporation of zinc at the weld and the formation of a heat-affected-zone (HAZ). High heat input due to welding generates macro galvanic coupling between the weld and the parent metal as well as micro galvanic corrosion

  11. Inhibition of Bio corrosion of steel coupon by sulphate reducing ...

    African Journals Online (AJOL)

    ADOWIE PERE

    -8362. J. Appl. Sci. Environ. Manage. August 2017. Vol. 21 (5) 833-838. Full-text Available Online at www.ajol.info and www.bioline.org.br/ja. Inhibition of Bio corrosion of steel coupon by sulphate reducing bacteria and Iron oxidizing bacteria ...

  12. Inhibition Effect of Deanol on Mild Steel Corrosion in Dilute ...

    African Journals Online (AJOL)

    The influence of deanol on the corrosion behaviour of mild steel in dilute sulphuric acid with sodium chloride addition was studied by means of mass-loss, potentiodynamic polarization, electrode potential monitoring, scanning electron microscopy and statistical analysis. Results show that deanol performed excellently with ...

  13. Investigations on the corrosion of constructional steels in different ...

    African Journals Online (AJOL)

    The corrosion behavior of three constructional steels used in Senegal, S235, S275 and S355, was studied in simulated atmospheric conditions in an exposure chamber above distilled water and above 3% NaCl solution representing marine atmosphere by comparing the ratio of rusted to unrusted area. Electrochemical test ...

  14. INHIBITION OF THE CORROSION OF MILD STEEL IN ...

    African Journals Online (AJOL)

    ABSTRACT. The inhibition of corrosion of mild steel in hydrochloric acid by isatin glycine (ING) and isatin (IN) at 30-60 oC and concentrations of 0.0001 M to 0.0005 M was studied via weight loss method. At the highest inhibitor concentration studied ING exhibited inhibition efficiency of 87% while IN exhibited 84% at 60 oC.

  15. corrosion response of low carbon steel in tropical road mud

    African Journals Online (AJOL)

    Dr Obe

    A.N.Enetanya. Department of Mechanical Engineering, University of. Nigeria, Nsukka, Nigeria. ABSTRACT. Corrosion damages in Steel and Cast- Iron frequently occur in automobile and other vehicle undercarriage parts as a result of regular road mud and other dirt deposits on those components on those vehicles ...

  16. Microgalvanic corrosion of laser-welded HSLA steels

    NARCIS (Netherlands)

    Looi, Y.M.

    2008-01-01

    Laser welding of galvanized high strength low alloy (HSLA) steels leads to the evaporation of zinc at the weld and the formation of a heat-affected-zone (HAZ). High heat input due to welding generates macro galvanic coupling between the weld and the parent metal as well as micro galvanic corrosion

  17. Pitting corrosion protection of low nickel stainless steel by ...

    Indian Academy of Sciences (India)

    Pitting corrosion protection of low nickel stainless steel by electropolymerized conducting polymer coating in 0·5 M NaCl solution. T DHANABAL, G AMIRTHAGANESAN. ∗ and J RAVICHANDRAN. Post Graduate and Research Department of Chemistry, Sri Ramakrishna Mission Vidyalaya College of Arts and Science,.

  18. Page 1 Stress corrosion cracking of austenitic stainless steels 691 ...

    Indian Academy of Sciences (India)

    Stress corrosion cracking of austenitic stainless steels 691 and crack growth per event computed from acoustic emission and crack growth data are presented in table 3. The crack growth per event varies from less than a micron for a solution annealed material to 15 pm for 10% cold worked material. 4.4 Fractographic ...

  19. Stress corrosion cracking of AISI 321 stainless steel in acidic ...

    Indian Academy of Sciences (India)

    The stress corrosion cracking (SCC) of AISI 321 stainless steel in acidic chloride solution was studied by slow strain rate (SSR) technique and fracture mechanics method. The fractured surface was characterized by cleavage fracture. In order to clarify the SCC mechanism, the effects of inhibitor KI on SCC behaviour were ...

  20. Corrosion monitoring of reinforcement steel using galvanostatically induced potential transients

    NARCIS (Netherlands)

    Abbas, Yawar; Nutma, J.S.; Olthuis, Wouter; van den Berg, Albert

    2015-01-01

    Investigation and results on a dynamic measurement technique to qualitatively evaluate the status of corrosion of reinforcement steel are presented. The sensing method is based on the measurement of the time constant of the relaxation of the current-induced polarization potential. This time constant

  1. Inhibition of Bio corrosion of steel coupon by sulphate reducing ...

    African Journals Online (AJOL)

    ADOWIE PERE

    Inhibition of Bio corrosion of steel coupon by sulphate reducing bacteria and Iron oxidizing bacteria using Aloe Vera (Aloe barbadensis) extracts. *. 1. AGWA, OK; IYALLA, D; ABU, GO. Department of Microbiology, Faculty of Science, University of Port Harcourt,. P.M.B. 5323, Rivers State, Nigeria. *Corresponding author: ...

  2. Investigation of the corrosion performance of different braze fillers fused onto stainless steel type 1.4401 (UNS S31600)

    Energy Technology Data Exchange (ETDEWEB)

    Wolfe, C.; Eklund, T.; Persson, O. [Alfa Laval Corporate AB, Tumba (Sweden)

    2004-07-01

    Corrosion measurements were performed on a new iron based braze filler, AlfaNova{sup 1} developed by Alfa Laval. The braze filler was fused onto stainless steel type EN 1.4401 (UNS S31600). The susceptibility to general corrosion, intergranular corrosion and pitting corrosion was evaluated by gravimetrical and electrochemical methods as well as metallographical examination of the samples. Different sample configurations were utilised, which simulate the geometry of a braze joint in a plate heat exchange. The results were compared with a selection of commercial nickel-based braze fillers. It was shown that the newly developed iron-based braze filler had similar corrosion resistance as the commercially available nickel-based fillers. It was seen that the precipitation of intermetallic phases due to melting point depressants had a governing effect on the corrosion resistance of the braze joint. (orig.)

  3. Influence of Changes in Water-to-Cement Ratio, Alkalinity, Concrete Fluidity, Voids, and Type of Reinforcing Steel on the Corrosion Potential of Steel in Concrete.

    Science.gov (United States)

    2014-04-01

    "Research on steel corrosion has demonstrated that the concentrations of chloride and hydroxide ion at the concrete/steel : interface influence the susceptibility of the steel to corrosive attack. This study used electrochemical means and changes in ...

  4. Corrosion behavior of a superduplex stainless steel in chloride aqueous solution

    Science.gov (United States)

    Dabalà, Manuele; Calliari, Irene; Variola, Alessandra

    2004-04-01

    Super duplex stainless steels (SDSS) have been widely used as structural materials for chemical plants (especially in those engaged in phosphoric acid production), in the hydrometallurgy industries, and as materials for offshore applications due to their excellent corrosion resistance in chloride environments, compared with other commercial types of ferritic stainless steels. These alloys also possess superior weldability and better mechanical properties than austenitic stainless steels. However, due to their two-phase structure, the nature of which is very dependent on their composition and thermal history, the behavior of SDSS regarding localized corrosion appears difficult to predict, especially in chloride environments. To improve their final properties, the effect of the partition of the alloying elements between the two phases, and the composition and microstructure of each phase are the key to understanding the localized corrosion phenomena of SDSS. This paper concerns the effects of the SDSS microstructure and heat treatment on the SDSS corrosion resistance in aqueous solutions, containing different amounts of NaCl at room temperature.

  5. Manufacturing, Microstructure and Corrosion Resistance of Electrophoretically Deposited SiO2 and Ni/SiO2 Coatings On X2CrNiMo17–12–2 Steel

    Directory of Open Access Journals (Sweden)

    Ratajski T.

    2016-06-01

    Full Text Available The SiO2 and Ni/SiO2 coatings were electrophoretically deposited on X2CrNiMo17-12-2 steel using ethanol-based suspensions of the SiO2 and Ni powders. The influence of the zeta potential and concentration of the suspensions, the applied voltage and deposition time on the quality of the coatings was studied. Microstructure of the plan-view and cross sections of the coatings was investigated using scanning electron microscopy. The plan-view images revealed the uniform microstructure of the coatings with sporadically observed cracks, pores as well SiO2 and Ni agglomerates. On the cross-sections, the Cr2O3 layer, resulted from oxidation of the substrate during sintering of the coatings was observed. The polarization tests have shown that SiO2 and Ni/SiO2 coatings improve the corrosion resistance of the X2CrNiMo17-12-2 steel in 3.5% NaCl aqueous solution.

  6. Crevice Corrosion Behavior of Nitrogen Bearing Austenitic Stainless Steels

    Energy Technology Data Exchange (ETDEWEB)

    Ono, A.A.; Shinohara, Tadashi.; Tsujikawa, Shigeo. [The University of Tokyo, Tokyo (Japan). Graduate School of Engineering

    1999-03-15

    The effect of nitrogen alloying on the initiation, propagation and repassivation of crevice corrosion of SUS 304 and SUS 316 austenitic stainless steels was investigated through potentiostatic polarizations, cyclic polarizations and in-situ measurements of depth profiles by the moire method. The results showed that nitrogen alloying in austenitic stainless steels increased to more noble values both the critical potential for steady crevice corrosion, V{sub C,CREV}, and the critical potential for repassivation of crevice corrosion E{sub C,CREV}. Concerning the in-situ measurements results, the disolution rate just above the repassivation potential, V{sub I}I*, decreased with nitrogen alloying for the SUS 304 alloys, and did not change in the SUS 316 alloys. The ratio of repassivating picture elements increased in both SUS 304 and SUS 316 with nitrogen alloying. (author)

  7. Sealing of thermally-sprayed stainless steel coatings against corrosion using nickel electroplating technique

    Directory of Open Access Journals (Sweden)

    Hathaipat Koiprasert

    2007-07-01

    Full Text Available Electric arc spraying (EAS is one of the thermal spray techniques used for restoration and to providecorrosion resistance. It can be utilized to build up coatings to thicknesses of several millimeters, It is easy to use on-site. Most importantly, the cost of this technique is lower than other thermal spraying techniques thatmay be suitable for part restoration. A major disadvantage associated with the electric arc sprayed coating is its high porosity, which can be as high as 3-8% making it not appropriate for use in immersion condition. This work was carried out around the idea of using electroplating to seal off the pore of the EAS coating, with an aim to improve the corrosion resistance of the coating in immersion condition. This research compared the corrosion behavior of a stainless steel 316 electric arc sprayed coating in 2M NaOH solution at 25oC. It was found that the Ni plating used as sealant can improve the corrosion resistance of the EAS coating. Furthermore, the smoothened and plated stainless steel 316 coating has a better corrosion resistance than the plated EAS coating that was not ground to smoothen the surface before plating.

  8. XPS study on double glow plasma corrosion-resisting surface alloying layer

    Science.gov (United States)

    Ai, Jiahe; Xu, Jiang; He, Fei; Xie, Xishan; Xu, Zhong

    2003-02-01

    Double glow plasma corrosion-resisting surface alloying layer (SAL) formed on low carbon steel 1020 was studied by X-ray photoelectron spectroscopy (XPS) and other means. Results show that the passive film of the surface alloying layer after electrochemical test in 3.5% NaCl solution consists of Cr and Fe oxide such as CrO 3, Cr 2O 3, Fe 2O 3 and FeO and metallic Ni and Mo, and it attributes to the fact that a continuous and compact corrosion-resisting surface alloying layer with rich Cr, Ni and Mo was formed on the surface of steel 1020 so as to increase its corrosion resistance greatly. Therefore, double glow plasma technique will be widely used in corrosion-resisting surface science.

  9. Corrosion behavior of a welded stainless-steel orthopedic implant.

    Science.gov (United States)

    Reclaru, L; Lerf, R; Eschler, P Y; Meyer, J M

    2001-02-01

    The corrosion behavior of combinations of materials used in an orthopedic implant: the spherical part (forged or forged and annealed) constituting the head, the weld (tungsten inert gas (TIG) or electron beam (EB) techniques), and the cylindrical part (annealed) constituting the shaft of a femoral prosthesis - has been investigated. Open-circuit potentials, potentiodynamic curves, Tafel slope, mixed potential theory and susceptibility to intergranular attack are electrochemical and chemical procedures selected for this work. Electrochemical measurements using a microelectrode have been made in the following zones: spherical part, cylindrical part, weld, and weld/sphere, and weld/shaft interfaces. To detect intergranular attack, the Strauss test has been used. At the interfaces, corrosion currents, measured (Icorr) and predicted (Icouple) are low, in the order of the pico- to nanoampere. The electrochemical behavior of the electron beam (EB) weld is better than that of the tungsten inert gas (TIG). Welds at interfaces can behave either anodically or cathodically. It is better if welds, which are sensitive parts of the femoral prosthesis, behave cathodically. In this way, the risk of starting localized corrosion (pitting, crevice or intergranular corrosion) from a galvanic couple, remains low. From this point of view, the sample with the EB weld offers the best behavior. All the other samples containing a TIG type of weld exhibit a less favorable behavior. The mechanical treatments (forged, and forged and annealed) of the steel sphere did not show any difference in the corrosion behavior. No intergranular corrosion has been observed at the weld/steel interface for unsensitized samples. With sensitized samples, however, a TIG sample has exhibited some localized intergranular corrosion at a distance of 500 microm along the weld/stainless steel (sphere) interface.

  10. Marine Atmospheric Corrosion of Carbon Steel: A Review

    Science.gov (United States)

    Alcántara, Jenifer; de la Fuente, Daniel; Chico, Belén; Simancas, Joaquín; Díaz, Iván; Morcillo, Manuel

    2017-01-01

    The atmospheric corrosion of carbon steel is an extensive topic that has been studied over the years by many researchers. However, until relatively recently, surprisingly little attention has been paid to the action of marine chlorides. Corrosion in coastal regions is a particularly relevant issue due the latter’s great importance to human society. About half of the world’s population lives in coastal regions and the industrialisation of developing countries tends to concentrate production plants close to the sea. Until the start of the 21st century, research on the basic mechanisms of rust formation in Cl−-rich atmospheres was limited to just a small number of studies. However, in recent years, scientific understanding of marine atmospheric corrosion has advanced greatly, and in the authors’ opinion a sufficient body of knowledge has been built up in published scientific papers to warrant an up-to-date review of the current state-of-the-art and to assess what issues still need to be addressed. That is the purpose of the present review. After a preliminary section devoted to basic concepts on atmospheric corrosion, the marine atmosphere, and experimentation on marine atmospheric corrosion, the paper addresses key aspects such as the most significant corrosion products, the characteristics of the rust layers formed, and the mechanisms of steel corrosion in marine atmospheres. Special attention is then paid to important matters such as coastal-industrial atmospheres and long-term behaviour of carbon steel exposed to marine atmospheres. The work ends with a section dedicated to issues pending, noting a series of questions in relation with which greater research efforts would seem to be necessary. PMID:28772766

  11. Corrosion of annealed AISI 316 stainless steel in sodium environment

    Science.gov (United States)

    Ganesan, Vaidehi; Ganesan, Vedaraman

    1998-07-01

    Solution annealed AISI type 316 austenitic stainless steel specimens were exposed in static sodium at 773 and 873 K for durations ranging from 500 to 2000 h. The results, i.e, weight loss data, hardness values, carburisation, depletion rates, sigma phase formation from the ferrite layer, corrosion morphology, roughness values etc. are analysed and discussed in the paper. Corrosion data such as the weight loss/depleted layer thickness and microstructure of fully annealed stainless steel specimens at 773 and 873 K under static sodium conditions (present study) are comparable to those of 20% cold worked stainless steel type 316 specimens at temperatures 973 K and above under dynamic sodium conditions. Annealed specimens leach out at a faster rate than cold worked specimens exposed to sodium.

  12. Electrochemical noise measurements of steel corrosion in the molten NaCl-K2SO4 system

    DEFF Research Database (Denmark)

    Cappeln, Frederik Vilhelm; Bjerrum, Niels; Petrushina, Irina

    2005-01-01

    Electrochemical noise measurements have been carried out on AISI347, 10CrMo910, 15Mo3, and X20CrMoV121 steels in molten NaCl-K2SO4 at 630 degrees C. Different types of current noise have been identified for pitting, intergranular and peeling corrosion. The corrosion mechanism was the so...... statistical parameter calculated from the electrochemical noise data). It was found that average kurtosis values above 6 indicated intergranular corrosion and average values below 6 indicated general corrosion. The response time for localized corrosion detection in in-plant monitoring was approximately 90 min...... on this basis. Approximate values of polarization resistances of AISI347 and 15Mo3 steels were determined to be 250 and 100 Omega cm(2), respectively....

  13. Investigation of Eh, pH and corrosion potential of steel in anoxic groundwater

    Energy Technology Data Exchange (ETDEWEB)

    Peat, R.; Brabon, S.; Fennell, P.A.H.; Rance, A.P.; Smart, N.R. [AEA Technology (United Kingdom)

    2001-01-01

    SKB intend to dispose of the spent nuclear fuel produced by Sweden's eleven nuclear reactors by encapsulating it in corrosion-resistant copper canisters containing a cast iron or carbon steel insert. After encapsulation, the fuel will be transported to a geological repository, where the containers will be deposited at a depth of 500 to 700 m in granitic rock and surrounded by a bentonite clay backfill material. If, or when the copper corrosion shield fails, the iron insert will be in contact with oxygen-free water and hydrogen-producing, anaerobic corrosion will start. SKB have carried out modelling calculations of the oxidising power (Eh) of groundwater and wished to confirm the results by carrying out experimental measurements. The objective of the work described in this report was to demonstrate the feasibility of monitoring Eh, pH and corrosion potential in a cell where anaerobic corrosion of steel in artificial groundwater was occurring. To this end, gas cells similar to those used previously for anaerobic corrosion rate measurements were used as the basis for the design of an electrochemical cell. The cell incorporated electrodes to provide an in situ measurement of the redox potential, Eh, the pH and the corrosion potential of carbon steel. The main stages of the work were: Design of the electrochemical cell; Preparation of silver-silver chloride and calomel reference electrodes; Calibration of the reference electrodes and commercial glass pH electrodes against a standard hydrogen electrode; Assembly of the test cell under anoxic conditions; Monitoring the cell before and after the addition of steel wires to the test solution. Details of the design of the test cell and the experimental procedures used are described. Two cells were set up. The first employed a silver-silver chloride reference electrode, which was failed after approximately 400 hours, and the second cell therefore used a calomel reference electrode. The results of the electrode

  14. Oleic acid-grafted chitosan/graphene oxide composite coating for corrosion protection of carbon steel.

    Science.gov (United States)

    Fayyad, Eman M; Sadasivuni, Kishor Kumar; Ponnamma, Deepalekshmi; Al-Maadeed, Mariam Al Ali

    2016-10-20

    An anticorrosion coating film based on the formation of nanocomposite coating is reported in this study. The composite consisted of chitosan (green matrix), oleic acid, and graphene oxide (nano filler). The nanocomposite coating was arranged on the surface of carbon steel, and the corrosion resistance was monitored using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PP). Compared to the pure chitosan (CS) coating, the corrosion resistance of oleic acid-modified chitosan/graphene oxide film (CS/GO-OA) is increased by 100 folds. Since the well-dispersed smart grafted nanolayers delayed the penetration rate of corrosive species and thus maintained long term anticorrosive stability which is correlated with hydrophobicity and permeability. Copyright © 2016 Elsevier Ltd. All rights reserved.

  15. CORROSION INHIBITION OF BENZOTRIAZOLE AND N-MESYL BENZOTRIAZOLE ON LOW CARBON STEEL IN SULFURIC ACID

    Directory of Open Access Journals (Sweden)

    Evrim HÜR

    2011-06-01

    Full Text Available This study examines usage of benzotriazole (Bt and N-mesyl benzotriazole (BtSO₂CH₃ for im- provement of corrosion resistance of low carbon steel (LCS in 0.1 M sulfuric acid (H₂SO₄. The inhibitor effect of Bt and BtSO₂CH₃ on the corrosion behavior of LCS was studied using electrochemical impedance spectroscopy (EIS, potentiodynamic polarization curves and polarization resistance techniques. Under investigated experimental conditions these compounds showed a good corrosion inhibition. The inhibition efficiency of BtSO₂CH₃ was more than that of Bt. The potentiodynamic polarization curves indicated that compounds are mixed type inhibitors. The inhibiting properties of compounds were found to depend on the concentration. The adsorption mechanism of compounds was investigated using different adsorption isotherms. The equilibrium constants and free energies of adsorption using the adsorption isotherms were calculated.

  16. Impact of Sterilisation and Strain Hardening in Drawing Process on Resistance to Electrochemical Corrosion of Wires Intended in Cardiology

    National Research Council Canada - National Science Library

    J. Przondziono; E. Hadasik; W. Walke; J. Mendala

    2016-01-01

    The study presents results of tests of impact of work hardening in cold drawing process, surface treatment and sterilisation on resistance to electrochemical corrosion of wires made of stainless steel...

  17. HEAT RESISTANCE OF GRAPHITIZED STEEL

    Directory of Open Access Journals (Sweden)

    V. O. Savchenko

    2014-06-01

    Full Text Available Purpose. The investigation of temperature dependences of steels' mechanical properties and heat resistance under conditions of thermal cyclic loads. It's necessary to determine the mechanical properties and heat resistance indices of graphitized steels and cast iron VCh400 within the temperature range of 20…800°С. Methodology. Graphitized steels of the following chemical composition (mass %: 0.61…1.04C; 1.19…1.59%Si; 0.32…0.37%Mn; 0.12…0.17%Al; 0.008…0.014%S and 0.016…0.025%Р have been heat-treated according to the mode: heating up to 810°С – holding for 2 hours; cooling down to 680°С – holding for 2 hours with further cooling using the furnace in order to provide the ferrite-pearlite metallic base with graphite inclusions. In order to determine heat resistance indices (heat stresses index K and the material's resistance criterion at thermal cyclic load C the indices of graphitized steels' and cast irons' mechanical properties in the temperature range of 20…800°С have been investigated. Findings. It has been established that as a result of lower carbon content and smaller quantity of graphite inclusions, graphitized steel exceeds such indices of nodular cast iron VCh400 as: tensile strength and plasticity at room and high temperatures, and also heat resistance criteria K and C. This steel can be used to manufacture articles operating under conditions of thermal cyclic loads. Originality. Tensile strength and percent elongation of graphitized steels within the temperature range of 20…800°С have been determined. Calculations of heat resistance criteria to the heat stresses index K and the material's resistance criterion at thermal cyclic loads C within the temperature range 20…800°С in comparison with nodular cast iron of VCh400 grade have been carried out. Practical value. The expediency of using graphitized steel for manufacturing of articles operating under conditions of thermal cyclic loads has been shown.

  18. The Effects of Corrosive Chemicals on Corrosion Rate of Steel Reinforcement Bars: I. Swamp Water

    Directory of Open Access Journals (Sweden)

    Sulistyoweni Widanarko

    2010-10-01

    Full Text Available Most of infrastructures using steel concrete to reinforce the strength of concrete. Steel concrete is so vulnerable to chemical compounds that can cause corrosion. It can happen due to the presence of chemical compounds in acid environment in low pH level. These chemical compounds are SO42-, Cl-, NO3-. There are many swamp area in Indonesia. The acid contents and the concentration of ion sulphate, chlorides, and nitrate are higher in the swamp water than in the ground water .The objective of this research was to find out the influence of corrosive chemicals in the swamp water to the steel concrete corrosion rate. There were two treatment used: (1 emerging ST 37 and ST 60 within 60 days in the 'polluted' swamp water, (2 moving the ST 37 up and down periodically in the ' polluted' swamp water. Three variation of 'polluted' swamp water were made by increasing the concentration of corrosive chemical up to 1X, 5X and 10X respectively. The corrosion rate was measured by using an Immersion Method. The result of Immersion test showed that chloride had the greatest influence to corrosion rate of ST 37 and ST 60 and followed by sulphate and Nitrate. Corrosion rate value for ST 37 is 24.29 mpy and for ST 60 is 22.76 mpy. By moving the sample up and down, the corrosion rate of ST 37 increase up to 37.59 mpy, and chloride still having the greatest influence, followed by sulphate and nitrate.

  19. The corrosion resistance of 140MXC, 530AS and 560AS coatings produced by thermal spraying

    Directory of Open Access Journals (Sweden)

    Edwin Alexis López Covaleda

    2013-04-01

    Full Text Available Three commercial materials were deposited using electric arc thermal spraying: 140MXC (with Fe, W, Cr, Nb, 530AS (AISI 1015 steel and 560AS (AISI 420 steel on AISI 4340 steel. The aim of this paper was to evaluate the best strategy for improving a coating-substrate system’s corrosion resistance, using the following combinations: homogeneous single coatings, bilayers consisting of 530AS or 560AS under 140MXC and 140MXC + 530AS and 140MXC + 560AS coatings deposited simultaneously. The coatings were characterised using optical microscopy, scanning electron microscopy and X-ray diffraction. Corrosion resistance was evaluated through potentiodynamic polarisation and hardness by using the Vickers test. Corrosion resistance depends on the amount of microstructure defects, the deposition strategy and the alloy elements. However, corrosion resistance was similar in single coatings of 140MXC and bilayers, having -630 V corrosion potential and 708 nA corrosion current. The details and corrosion mechanism of the coatings so produced are described in this paper.

  20. Adhesion of Bacillus subtilis and Pseudoalteromonas lipolytica to steel in a seawater environment and their effects on corrosion.

    Science.gov (United States)

    Guo, Zhangwei; Liu, Tao; Cheng, Y Frank; Guo, Na; Yin, Yansheng

    2017-09-01

    In a marine environment, Bacillus subtilis and Pseudoalteromonas lipolytica are commonly found in the biofilms adherent to low-alloy engineering steel, and they have distinct effects on corrosion. In the present work, this phenomenon was investigated through the study of various materials characterization methods, electrochemical techniques, and contact angle measurements. It was found that the surface film formed on the steel in the presence of B. subtilis was compact, uniform, free of cracks, and hydrophobic. However, the film formed in the presence of P. lipolytica was loose, rough, heterogeneous, and hydrophilic. The main components of the films formed in the presence of B. subtilis and P. lipolytica were polysaccharides/TasA amyloid fibers and proteins/carboxylic acid, respectively. The composition, structure, and properties of the surface films formed on the steel were associated with different effects on corrosion. The presence of B. subtilis enhances the steel's resistance to corrosion, whereas corrosion was increased by the presence of P. lipolytica. In short, the compact and hydrophobic biofilm of B. subtilis appears to inhibit the corrosion of steel, while the loose, hydrophilic film of P. lipolytica tends to induce pitting corrosion. Copyright © 2017 Elsevier B.V. All rights reserved.

  1. Corrosion and Nano-mechanical Behaviors of Magnetron Sputtered Al-Mo Gradient Coated Steel

    Science.gov (United States)

    Venugopal, A.; Srinath, J.; Ramesh Narayanan, P.; Sharma, S. C.; Venkitakrishnan, P. V.

    2017-01-01

    A gradient three-layer Al-Mo coating was deposited on steel using magnetron sputtering method. The corrosion and nano-mechanical properties of the coating were examined by electrochemical impedance spectroscopy and nano-indentation tests and compared with the conventional electroplated cadmium and IVD aluminum coatings. Electrochemical impedance spectroscopy was performed by immersing the coated specimens in 3.5% NaCl solution, and the impedance behavior was recorded as a function of immersion time. The mechanical properties (hardness and elastic modulus) were obtained from each indentation as a function of the penetration depth across the coating cross section. The adhesion resistance of the coatings was evaluated by scratch tests on the coated surface using nano-indentation method. The results show that the gradient Al-Mo coating exhibits better corrosion resistance than the other coatings in view of the better microstructure. The impedance results were modeled using appropriate electrical equivalent circuits for all the coated systems. The uniform, smooth and dense Al-Mo coating obtained by magnetron sputtering exhibits good adhesion with the steel substrate as per scratch test method. The poor corrosion resistance of the later coatings was shown to be due to the defects/cracks as well as the lesser adhesion of the coatings with steel. The hardness and elastic modulus of the Al-Mo coating are found to be high when compared to the other coatings.

  2. Corrosive wear. Evaluation of wear and corrosive resistant materials; Noetningskorrosion. Utvaerdering av noetnings- och korrosionsbestaendiga material

    Energy Technology Data Exchange (ETDEWEB)

    Persson, H.; Hjertsen, D.; Waara, P.; Prakash, B.; Hardell, J.

    2007-12-15

    With a new purchase of a waste conveyer screw at hand, for the 'A-warehouse' at the combined power and heating plant at E.ON Norrkoeping, the request for improved construction materials was raised. The previous screw required maintenance with very short intervals due to the difficult operation conditions. With the new screw the expectation is to manage 6 months of operation without interruption. The environment for the screw has two main components that sets the demand on the materials, on one hand the corrosive products that comes along and which forms at digestion of the waste and on the other hand the abrasive content in the waste. The term of the mechanism is wear-corrosion and can give considerably higher material loss than the two mechanisms wear and corrosion separately. Combination of a strong corrosive environment together with extensive wear is something that we today have limited knowledge about. The overall objective of the project has been to establish better wear and corrosive resistant construction materials for a waste conveyer screw that will lead to reduced operational disturbance costs. The evaluation has been performed in both controlled laboratory environments and in field tests, which has given us a better understanding of what materials are more suitable in this tough environment and has given us a tool for future predictions of the wear rate of the different material. The new conveyer screw, installed in February 2007 and with which the field test have been performed, has considerably reduced the wear of the construction and the target of 6 month maintenance-free operation is met with this screw for all the evaluated materials. The wear along the screw varies very much and with a clear trend for all the materials to increase towards the feeding direction of the screw. As an example, the wear plate SS2377 (stainless duplex steel) has a useful life at the most affected areas that is calculated to be 1077 days of operation with the

  3. Corrosion protection by sonoelectrodeposited organic films on zinc coated steel.

    Science.gov (United States)

    Et Taouil, Abdeslam; Mahmoud, Mahmoud Mourad; Lallemand, Fabrice; Lallemand, Séverine; Gigandet, Marie-Pierre; Hihn, Jean-Yves

    2012-11-01

    A variety of coatings based on electrosynthesized polypyrrole were deposited on zinc coated steel in presence or absence of ultrasound, and studied in terms of corrosion protection. Cr III and Cr VI commercial passivation were used as references. Depth profiling showed a homogeneous deposit for Cr III, while SEM imaging revealed good surface homogeneity for Cr VI layers. These chromium-based passivations ensured good protection against corrosion. Polypyrrole (PPy) was also electrochemically deposited on zinc coated steel with and without high frequency ultrasound irradiation in aqueous sodium tartrate-molybdate solution. Such PPy coatings act as a physical barrier against corrosive species. PPy electrosynthesized in silent conditions exhibits similar properties to Cr VI passivation with respect to corrosion protection. Ultrasound leads to more compact and more homogeneous surface structures for PPy, as well as to more homogeneous distribution of doping molybdate anions within the film. Far better corrosion protection is exhibited for such sonicated films. Copyright © 2012 Elsevier B.V. All rights reserved.

  4. Hydrogen Diffusion and H{sub 2}S Corrosion in Steel

    Energy Technology Data Exchange (ETDEWEB)

    Haugstveit, Bjarte Erlend

    2001-01-01

    The electrochemical permeation technique introduced by Devanathan and Stachurski has been used to measure the effective diffusivity of hydrogen in steel in a H{sub 2}S-saturated aqueous environment. The linear polarization resistance (LPR) method has been used to measure the corrosion rate. The effective diffusion coefficient of hydrogen has been found to be in the range of 1*10-12 to 7*10-11, depending on the environmental conditions. The corrosion film was identified as mackinawite, and it affected the permeation process of hydrogen. The results supported the assumption that the diffusion process can be described by a three layer model and indicated that the model could be reduced to a two layer model in the cases of iron and steel. A model aimed to describe the reaction pathway of hydrogen through the surface film and into the steel is proposed. The corrosion film influenced the corrosion rate, and it was least protective against corrosion at pH 6.5. Corrosion rates were in the range of 0.2-1 mm/year. The corrosion rate was increased significantly at pH 3.5, but the effect of the surface film was stronger and overshadowed the pH effect at the higher pH values. Increased flow velocity also lead to increased corrosion rate, but this effect was less significant compared to the effect of pH and the surface film. DEG decreased the corrosion rate. The uncertainty in the diffusion measurements was mainly due to the assumption of a constant sub-surface concentration of atomic hydrogen, which was not fulfilled. A method less dependent on constant surface conditions would probably yield better estimates of the effective diffusivity. The uncertainty in the corrosion measurements was mainly due to the uncertainty in the value of the Stern-Geary constant. The qualitative assumptions based on the results in this thesis are assumed to be valid. A test section designed for this thesis was tested and was found successful in corrosion rate measurements, but proved to be

  5. Laboratory investigation of the microbiologically influenced corrosion (MIC) resistance of a novel Cu-bearing 2205 duplex stainless steel in the presence of an aerobic marine Pseudomonas aeruginosa biofilm.

    Science.gov (United States)

    Xia, Jin; Yang, Chunguang; Xu, Dake; Sun, Da; Nan, Li; Sun, Ziqing; Li, Qi; Gu, Tingyue; Yang, Ke

    2015-01-01

    The microbiologically influenced corrosion (MIC) resistance of a novel Cu-bearing 2205 duplex stainless steel (2205 Cu-DSS) against an aerobic marine Pseudomonas aeruginosa biofilm was investigated. The electrochemical test results showed that Rp increased and icorr decreased sharply after long-term immersion in the inoculation medium, suggesting that 2205 Cu-DSS possessed excellent MIC resistance to the P. aeruginosa biofilm. Fluorescence microscope images showed that 2205 Cu-DSS possessed a strong antibacterial ability, and its antibacterial efficiency after one and seven days was 7.75% and 96.92%, respectively. The pit morphology comparison after 14 days between 2205 DSS and 2205 Cu-DSS demonstrated that the latter showed a considerably reduced maximum MIC pit depth compared with the former (1.44 μm vs 9.50 μm). The experimental results suggest that inhibition of the biofilm was caused by the copper ions released from the 2205 Cu-DSS, leading to its effective mitigation of MIC by P. aeruginosa.

  6. Microbially Influenced Corrosion of 304 Stainless Steel and Titanium by P. variotii and A. niger in Humid Atmosphere

    Science.gov (United States)

    Zhang, Dawei; Zhou, Feichi; Xiao, Kui; Cui, Tianyu; Qian, Hongchong; Li, Xiaogang

    2015-07-01

    Microbially induced corrosion (MIC) poses significant threats to reliability and safety of engineering materials and structures. While most MIC studies focus on prokaryotic bacteria such as sulfate-reducing bacteria, the influence of fungi on corrosion behaviors of metals has not been adequately reported. In this study, 304 stainless steel and titanium were exposed to two very common fungi, Paecilomyces variotii, Aspergillus niger and their mixtures under highly humid atmosphere. The initial corrosion behaviors within 28 days were studied via scanning Kelvin probe, which showed marked surface ennoblement and increasingly heterogeneous potential distribution upon prolonged fungus exposure. Using stereomicroscopy, fungus growth as well as corrosion morphology of 304 stainless steel and titanium were also evaluated after a long-term exposure for 60 days. The presence of fungi decreased the corrosion resistance for both 304 stainless steel and titanium. Titanium showed higher resistance to fungus growth and the induced corrosion. Exposure to the mixed strains resulted in the highest fungus growth rate but the mildest corrosion, possibly due to the decreased oxygen level by increased fungal activities.

  7. Effect of gas nitriding on CO2 corrosion for 35CrMo steel after surface nanocrystallization.

    Science.gov (United States)

    Wang, Bingying; Zhou, Shengnan; Wang, Jingjing; Zhao, Bin

    2014-10-01

    This paper studies the influence of ultrasonic surface rolling procession (USRP) and gas nitriding on CO2 corrosion for 35CrMo steel. The microstructure of the nanocrystallized surface caused by USRP and the nitrided layer were studied by means of HRTEM and optical microscope, respectively. High temperature high pressure autoclave was adopted to study the CO2 corrosion behavior of 35CrMo steel. The characteristics of CO2 corrosion scales on 35CrMo steel were investigated by the SEM, EDS and XRD techniques. The experimental results show that after USRP about 250 μm rheological layer forms on the metal surface, and the average grain size is 25 nm. USRP thicken the nitrided layer, 10 hours' gas nitriding at 550 degrees C lower the corrosion rate while the combine of gas nitriding and USRP enhances the corrosion resistance furthest; and the surface nanocrystallization increases the content of Cr and changes the corrosion product film from FeCO3 to FeCO3 and Cr2O3, and from loose crystal structure to amorphous flocculent structure. The corrosion resistance of 35CrMo has been improved significantly by USRP and gas nitriding.

  8. Effect of surface nanocrystallization induced by fast multiple rotation rolling on hardness and corrosion behavior of 316L stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Chui Pengfei [Key Laboratory for Liquid-Solid Structure Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Engineering Ceramics Key Laboratory of Shandong Province, Shandong University, Jinan 250061 (China); Sun Kangning, E-mail: sunkangning@sdu.edu.cn [Key Laboratory for Liquid-Solid Structure Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Engineering Ceramics Key Laboratory of Shandong Province, Shandong University, Jinan 250061 (China); Sun Chang [Key Laboratory for Liquid-Solid Structure Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Engineering Ceramics Key Laboratory of Shandong Province, Shandong University, Jinan 250061 (China); Shandong Supervision and Inspection Institute for Product Quality, Shandabeilu Road 81, Jinan 250100 (China); Yang Xiuqing; Shan Ting [Key Laboratory for Liquid-Solid Structure Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Engineering Ceramics Key Laboratory of Shandong Province, Shandong University, Jinan 250061 (China)

    2011-05-15

    A nanostructured layer was fabricated by using fast multiple rotation rolling (FMRR) on the surface of 316L stainless steel. The microstructure in the surface was characterized by transmission electron microscopy and X-ray diffraction. The effects of FMRR on the microhardness, surface roughness and corrosion behavior of the stainless steel were investigated by microhardness measurements, surface roughness measurements, potentiodynamic polarization curves and pitting corrosion tests. The surface morphologies of pitting corrosion specimens were characterized by scanning electron microscopy. The results show that FMRR can cause surface nanocrystallization with the grain size ranges from 6 to 24 nm in the top surface layer of the sample. The microhardness of FMRR specimen in the top surface layer remarkably increases from 190 to 530 HV. However, the surface roughness slightly rises after FMRR treatment. The potentiodynamic polarization curves and pitting corrosion tests indicated that the FMRR treated 316L stainless steel with a surface nanocrystallized layer reduced the corrosion resistance in a 3.5% NaCl solution and enhanced the pitting corrosion rate in a FeCl{sub 3} solution. Possible reasons leading to the decrease in corrosion resistance were discussed.

  9. Inhibition of Mild Steel Corrosion in Hydrochloric Acid Solution by New Coumarin

    Directory of Open Access Journals (Sweden)

    Abdul Amir H. Kadhum

    2014-06-01

    Full Text Available A new coumarin derivative, N,N′-((2E,2′E-2,2′-(1,4-phenylenebis (methanylylidenebis(hydrazinecarbonothioylbis(2-oxo-2H-chromene-3-carboxamide PMBH, was synthesized and its chemical structure was elucidated and confirmed using spectroscopic techniques (Infrared spectroscopy IR, Proton nuclear  magnetic resonance, 1H-NMR and carbon-13 nuclear magnetic resonance 13C-NMR. The corrosion inhibition effect of PMBH on mild steel in 1.0 M HCl was investigated using corrosion potential (ECORR, potentiodynamic polarization, electrochemical impedance spectroscopy (EIS, and electrochemical frequency modulation (EFM measurements. The obtained results indicated that PMBH has promising inhibitive effects on the corrosion of mild steel in 1.0 M HCl across all of the conditions examined. Scanning electron microscopy (SEM was used to investigate the morphology of the mild steel before and after immersion in 1.0 M HCl solution containing 0.5 mM of PMBH. Surface analysis revealed improvement of corrosion resistance in presence of PMBH.

  10. Corrosion Behavior Of Carbon Steel Under Flowing Condition

    Directory of Open Access Journals (Sweden)

    Shaker Saleh Bahar

    2017-08-01

    Full Text Available The behavior of carbon steel in 0.1 N NaCl solution under flowing conditions and at 30◦C was analyzed by using two methods, viz, weight method and polarization one and comparing them. It was found that the corrosion rate is affected by alternating the velocity of the solution, generally, higher mass transfer rates were obtained in weight loss than in the polarization method. Empirical equations were obtained for the two methods that relate the corrosion current versus the velocity of solution

  11. Accelerated corrosion of stainless steel in thiocyanate-containing solutions

    Energy Technology Data Exchange (ETDEWEB)

    Pistorius, P Chris; Li, Wen

    2012-09-19

    It is known that reduced sulfur compounds (such as thiocyanate and thiosulfate) can accelerate active corrosion of austenitic stainless steel in acid solutions, but before we started this project the mechanism of acceleration was largely unclear. This work combined electrochemical measurements and analysis using scanning electron microscopy (SEM) and X-ray photo-electron spectroscopy (XPS), which provided a comprehensive understanding of the catalytic effect of reduced sulfur species on the active corrosion of stainless steel. Both the behavior of the pure elements and the steel were studied and the work focused on the interaction between the pure elements of the steel, which is the least understood area. Upon completion of this work, several aspects are now much clearer. The main results from this work can be summarized as follows: The presence of low concentrations (around 0.1 mM) of thiocyanate or tetrathionate in dilute sulfuric acid greatly accelerates the anodic dissolution of chromium and nickel, but has an even stronger effect on stainless steels (iron-chromium-nickel alloys). Electrochemical measurements and surface analyses are in agreement with the suggestion that accelerated dissolution really results from suppressed passivation. Even well below the passivation potential, the electrochemical signature of passivation is evident in the electrode impedance; the electrode impedance shows clearly that this pre-passivation is suppressed in the presence of thiocyanate. For the stainless steels, remarkable changes in the morphology of the corroded metal surface and in the surface concentration of chromium support the suggestion that pre-passivation of stainless steels is suppressed because dissolution of chromium is accelerated. Surface analysis confirmed that adsorbed sulfur / sulfide forms on the metal surfaces upon exposure to solutions containing thiocyanate or thiosulfate. For pure nickel, and steels containing nickel (and residual copper), bulk sulfide

  12. Effect of corrosion and sandblasting on the high cycle fatigue behavior of reinforcing B500C steel bars

    Directory of Open Access Journals (Sweden)

    Marina C. Vasco

    2017-10-01

    Full Text Available In a series of applications, steel reinforced concrete structures are subjected to fatigue loads during their service life, what in most cases happens in corrosive environments. Surface treatments have been proved to represent proper processes in order to improve both fatigue and corrosion resistances. In this work, the effect of corrosion and sandblasting on the high cycle fatigue behavior reinforcing steel bars is investigated. The investigated material is the reinforcing steel bar of technical class B500C, of nominal diameter of 12 mm. Steel bars specimens were first exposed to corrosion in alternate salt spray environment for 30 and 60 days and subjected to both tensile and fatigue tests. Then, a series of specimens were subjected to common sandblasting, corroded and mechanically tested. Metallographic investigation and corrosion damage evaluation regarding mass loss and martensitic area reduction were performed. Tensile tests were conducted after each corrosion exposure period prior to the fatigue tests. Fatigue tests were performed at a stress ratio, R, of 0.1 and loading frequency of 20 Hz. All fatigue tests series as well as tensile test were also performed for as received steel bars to obtain the reference behavior. The results have shown that sandblasting hardly affects the tensile behavior of the uncorroded material. The effect of sandblasting on the tensile behavior of pre-corroded specimens seems to be also limited. On the other hand, fatigue results indicate an improved fatigue behavior for the sandblasted material after 60 days of corrosion exposure. Martensitic area reductions, mass loss and depth of the pits were significantly smaller for the case of sandblasted materials, which confirms an increased corrosion resistance

  13. Integrated sensor network for monitoring steel corrosion in concrete structures

    Directory of Open Access Journals (Sweden)

    José Enrique Ramón

    2016-06-01

    Full Text Available Corrosion is one of the main triggering factors affecting the service life and durability of structures. Several methods are used for corrosion studies but electrochemical techniques are the most commonly applied. Corrosion processes monitoring and control by means of non-destructive techniques, such as the implementation of embedded sensors, has been the target of many works.  It is possible to obtain relevant information of structural corrosion processes in real time. This document describes a system including specific equipment and which allows obtaining relevant information about these corrosion processes. This system is formed by a sensor network. There are several types of electrodes, which are distributed throughout the structure under study and a specific equipment developed by the research group, which is used to determine pertinent parameters such as the corrosion potential (Ecorr and the corrosion density (icorr by applying sequences of potentiostatic pulses. The system allows to reliably determine the corrosion rate in different areas of the structure. The sensor, due to its configuration, provides information of a specific area of the structure, but on the other hand it is involved in the galvanic events that can occur along the structure by differential aeration, galvanic cells, etc. because the sensor is not isolated from the structure.  This system also procures information of buried and submerged elements. Besides, it is possible to obtain information related to temperature, concrete resistance. The system includes specific potentiometric sensors to monitor chloride access and carbonatation processes.

  14. Effects of temperature and pressure on stress corrosion cracking behavior of 310S stainless steel in chloride solution

    Science.gov (United States)

    Zhong, Yunpan; Zhou, Cheng; Chen, Songying; Wang, Ruiyan

    2017-01-01

    310S is an austenitic stainless steel for high temperature applications, having strong resistance of oxidation, hydrogen embrittlement and corrosion. Stress corrosion cracking(SCC) is the main corrosion failure mode for 310S stainless steel. Past researched about SCC of 310S primarily focus on the corrosion mechanism and influence of temperature and corrosive media, but few studies concern the combined influence of temperature, pressure and chloride. For a better understanding of temperature and pressure's effects on SCC of 310S stainless steel, prepared samples are investigated via slow strain rate tensile test(SSRT) in different temperature and pressure in NACE A solution. The result shows that the SCC sensibility indexes of 310S stainless steel increase with the rise of temperature and reach maximum at 10MPa and 160°C, increasing by 22.3% compared with that at 10 MPa and 80 °C. Instead, the sensibility decreases with the pressure up. Besides, the fractures begin to transform from the ductile fracture to the brittle fracture with the increase of temperature. 310S stainless steel has an obvious tendency of stress corrosion at 10MPa and 160°C and the fracture surface exists cleavage steps, river patterns and some local secondary cracks, having obvious brittle fracture characteristics. The SCC cracks initiate from inclusions and tiny pits in the matrix and propagate into the matrix along the cross section gradually until rupture. In particular, the oxygen and chloride play an important role on the SCC of 310S stainless steel in NACE A solution. The chloride damages passivating film, causing pitting corrosion, concentrating in the cracks and accelerated SSC ultimately. The research reveals the combined influence of temperature, pressure and chloride on the SCC of 310S, which can be a guide to the application of 310S stainless steel in super-heater tube.

  15. Structural steel coatings for corrosion mitigation.

    Science.gov (United States)

    2010-10-01

    Task 1 of this project was to survey the performance of coating systems for steel bridges in Missouri and to evaluate coating and : recoating practices. Task 1 was led under the direction of Dr. Glenn Washer from the University of Missouri located in...

  16. Study of Stainless Steel Resistance in Conditions of Tribocorrosion Wear

    Directory of Open Access Journals (Sweden)

    Goran Rozing

    2015-07-01

    Full Text Available Analyzed was the influence of tribocorrosion wear due to effects of fatty acids present in the processed medium. The analysis was conducted on samples made of two austenitic and two martensitic stainless steels. Austenitic steels were tested in their nitrided state and martensitic in their induction hardened state. Conducted were laboratory tests of corrosion resistance of samples, analysis of the microstructure and hardness. To see how the applied processes for modifying the surface of stainless steels behave in realistic conditions, it was conducted the examination of samples/parts of a sunflower cake chain conveyer. Based on the comparison of results obtained in the laboratory and in real conditions, it was estimated that steels AISI 420 and AISI 431 with induction hardened surfaces have a satisfactory resistance to abrasive-adhesive wear in the presence of fatty acids.

  17. Anisotropy of nickel release and corrosion in austenitic stainless steels.

    Science.gov (United States)

    Reclaru, L; Lüthy, H; Ziegenhagen, R; Eschler, P-Y; Blatter, A

    2008-05-01

    The study of 316L-type stainless steel reveals a significant anisotropy of nickel release that is dependent on the orientation of the test surface with respect to the casting and rolling direction. Cross-sectional specimens (transversal cuts with respect to the rolling direction) show a substantially higher sensitivity to corrosion phenomena compared with longitudinal cuts and they release nickel ions at rates 10-100 times higher. These findings indicate that orientation needs to be taken into account when interpreting test results, in particular when comparing different grades of austenitic stainless steel, as well as in product and production design.

  18. Clays valorization as corrosion inhibitors for E400 reinforcing steel

    Directory of Open Access Journals (Sweden)

    Gassama Diadioly

    2016-06-01

    Full Text Available The behavior of E400 steel, a constructional steel widely used in Senegal, was studied in aqueous NaCl solution in the presence of two types of clay: volcanic tuffs, and sedimentary montmorillonite. The protection efficiency of these compounds were electrochemically assessed (corrosion potential variation curves, polarization curves and electrochemical impedance spectroscopy at various inhibitor contents. The results obtained showed that these inhibitors present an inhibitory efficacy of about 70% for an optimal concentration of 0.60% for the tuffs and 62% for a maximum content of 0.50% for montmorillonite.

  19. Monitoring of hydrogen generated by corrosion reactions of steel

    Energy Technology Data Exchange (ETDEWEB)

    Abbassi, A.; Mihi, A.; Benbouta, R. [Corrosion Laboratory, Department of Mechanical Engineering, Faculty of Engineering Science, University of Batna, 05000 Batna (Algeria)

    2008-12-15

    A solid-state sensor has been constructed and used for the detection of hydrogen generated during corrosion of steel in pH2 solutions. In addition to that, weight loss, AC impedance measurements and selected slow strain rate tests were performed under the same conditions as the hydrogen measurements in order to ascertain the degree of embrittlement of steel. The use of such a device in cathodic protection by impressed current in artificial seawater was also investigated. (Abstract Copyright [2008], Wiley Periodicals, Inc.)

  20. Post-irradiation annealing effects on hardness and intergranular corrosion in type 304 stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Asano, Kyoichi [Tokyo Electric Power Co. Inc., Yokohama (Japan). Materials Engineering Dept.; Katsura, Ryoei; Kodama, Mitsuhiro; Nishimura, Seiji [Nippon Nuclear Fuel Development Co., Ltd., Ibaraki (Japan); Fukuya, Kouji [Toshiba Corp., Yokohama (Japan). Nuclear Engineering Lab.; Nakata, Kiyotomo [Hitachi Ltd., Ibaraki (Japan). Hitachi Research Lab.

    1995-12-31

    The effects of post-irradiation annealing on hardness and grain boundary corrosion were investigated on stainless steel irradiated to 1.2 {times} 10{sup 26}n/m{sup 2}(E > 1 MeV). A commercial purity type 304 steel sample was annealed at temperatures between 673K and 1,323K for terms between 300s and 360ks. Only a slight decrease in hardness was observed by annealing at 723K for 3.6ks, while significant recovery was observed at 923K and above. This dependence on annealing temperature reflected recovery in damage microstructures. Annealing at all temperatures resulted in improved corrosion resistance when evaluated by the HNO{sub 3}/Cr{sup 6+} test. In the oxalic acid test, Strauss test and double loop electrochemical potentiokinetic reactivation test, no significant change from as-irradiated material occurred at 723K and below regarding intergranular corrosion while at 773K to 923K, thermal sensitization was observed and the reactivation ratio was larger than in unirradiated material. Annealing at 1,173K led to the irradiation induced degradation in corrosion resistance being recovered to almost the same level as that in unirradiated material. Helium bubble formation was observed after annealing at 923K and above, however, no brittle grain boundary failure occurred through all the test procedures including post-annealing straining.

  1. Microstructure characterization and corrosion testing of MAG pulsed duplex stainless steel welds

    Energy Technology Data Exchange (ETDEWEB)

    Mitelea, Ion; Utu, Ion Dragos; Urlan, Sorin Dumitru; Karancsi, Olimpiu [Politehnica Univ. Timisoara (Romania). Faculty of Mechanical Engineering

    2017-08-01

    Duplex stainless steels are extremely attractive construction materials for their usage in intense aggressive environments. They offer numerous advantages compared to the austenitic stainless steels having an excellent behavior to pitting and cavernous corrosion, and a high resistance to stress cracking corrosion in chlorides media. However, their corrosion properties are largely dependent on the microstructural factors such as: the quantitative ratio of the two phases ferrite/austenite (F/A), the presence of intermetallic compounds and the distribution of the alloying elements between the ferrite and austenite. As a result of the thermal cycles experienced by the base metal without a post-weld heat treatment, the mechanical properties are significantly different in the heat affected zone and the deposited metal compared with the properties of the base metal. The present paper highlights the effect of the post-weld solution treatment in order to restore the balance between austenite and ferrite in the welded joint areas and also to limit undesirable precipitation of secondary phases with implications for increasing the corrosion resistance.

  2. Investigation on the corrosion behavior of physical vapor deposition coated high speed steel

    Directory of Open Access Journals (Sweden)

    R Ravi Raja Malarvannan

    2015-08-01

    Full Text Available This work emphasizes on the influence of the TiN and AlCrN coatings fabricated on high speed steel form tool using physical vapor deposition technique. The surface microstructure of the coatings was studied using scanning electron microscope. Hardness and corrosion studies were also performed using Vickers hardness test and salt spray testing, respectively. The salt spray test results suggested that the bilayer coated (TiN- bottom layer and AlCrN- top layer substrate has undergone less amount of corrosion, and this is attributed to the dense microstructure. In addition to the above, the influence of the above coatings on the machining performance of the high speed steel was also evaluated and compared with that of the uncoated material and the results suggested that the bilayered coating has undergone very low weight loss when compared with that of the uncoated substrate depicting enhanced wear resistance.

  3. A New Maraging Stainless Steel with Excellent Strength–Toughness–Corrosion Synergy

    Directory of Open Access Journals (Sweden)

    Jialong Tian

    2017-11-01

    Full Text Available A new maraging stainless steel with superior strength–toughness–corrosion synergy has been developed based on an innovative concept of alloy design. The high strength–toughness combination is achieved by forming dispersive nano-sized intermetallic compounds in the soft lath martensitic matrix with a slight amount of residual austenite. The good corrosion resistance is guaranteed by exactly controlling the Co content based on understanding the synergistic effect between Co and Cr. The fine structure characteristics of two dominant strengthening precipitations including Ni3Ti and Mo-rich phases were finely characterized associated with transmission electron microscope (TEM and atom probe tomography (APT analyses. The relationship among microstructure, strength and toughness is discussed. The precipitation mechanism of different precipitates in the new maraging stainless steel is revealed based on the APT analysis.

  4. Bacillus sp. Acting as Dual Role for Corrosion Induction and Corrosion Inhibition with Carbon Steel (CS

    Directory of Open Access Journals (Sweden)

    Santosh K. Karn

    2017-10-01

    Full Text Available Present work investigated the role of five different bacteria species as a corrosion inducer as well as corrosion inhibitor with carbon steel (CS. We observed the ability of different bacteria species on the metal surface attachment, biofilm formation, and determined Peroxidase, Catalase enzyme activity in the detached biofilm from the CS surface. We found that each strain has diverse conduct for surface attachment like DS1 3.3, DS2 2.5, DS3 4.3, DS4 4.0, and DS5 4.71 log cfu/cm2 and for biofilm 8.3 log cfu/cm2. The enzyme Peroxidase, Catalase was found in huge concentration inside the biofilm Peroxidase was maximum for DS4 36.0 U/ml and least for DS3 19.54 U/ml. Whereas, Catalase was highest for DS4, DS5 70.14 U/ml and least 57.2 U/ml for DS2. Scanning electron microscopy (SEM was conducted to examine the biofilm and electrochemical impedance spectroscopy (EIS were utilized to observe corrosion in the presence of bacteria. The electrochemical results confirmed that DS1, DS3, DS4, and DS5 strains have statistically significant MIC-factors (Microbially Influenced Corrosion of 5.46, 8.51, 2.36, and 1.04, while DS2 protective effect factor of 0.89. Weight reduction results with carbon steel likewise supports that corrosion was initiated by DS1 and DS3, while DS2 and DS5 have no any impact though with DS4 we watched less weight reduction however assumed no role in the corrosion. We established the relation of Peroxidase enzyme activity of the isolates. DS1, DS3 and having Peroxidase in the range 22.18, 19.54 U/ml which induce the corrosion whereas DS2 and DS5 having 28.57 and 27.0 U/ml has no any effect and DS4 36 U/ml has inhibitory effect, increasing concentration inhibiting the corrosion. For Catalase DS1, DS3 have 67.28, 61.57 U/ml which induce corrosion while DS2 and DS5 57.71 and 59.14 U/ml also has no effect whereas DS4 70.14 U/ml can inhibit corrosion. Results clearly express that in a specific range both enzymes can induce the corrosion

  5. Influence of remanent magnetization on pitting corrosion in pipeline steel

    Energy Technology Data Exchange (ETDEWEB)

    Espina-Hernandez, J. H. [ESIME Zacatenco, SEPI Electronica Instituto Politecnico Nacional Mexico, D. F. (Mexico); Caleyo, F.; Hallen, J. M. [DIM-ESIQIE, Instituto Politecnico Nacional Mexico D. F. (Mexico); Lopez-Montenegro, A.; Perez-Baruch, E. [Pemex Exploracion y Produccion, Region Sur Villahermosa, Tabasco (Mexico)

    2010-07-01

    Statistical studies performed in Mexico indicate that leakage due to external pitting corrosion is the most likely cause of failure of buried pipelines. When pipelines are inspected with the magnetic flux leakage (MFL) technology, which is routinely used, the magnetization level of every part of the pipeline changes as the MFL tool travels through it. Remanent magnetization stays in the pipeline wall after inspection, at levels that may differ from a point to the next. This paper studies the influence of the magnetic field on pitting corrosion. Experiments were carried out on grade 52 steel under a level of remanent magnetization and other laboratory conditions that imitated the conditions of a pipeline after an MLF inspection. Non-magnetized control samples and magnetized samples were subjected to pitting by immersion in a solution containing chlorine and sulfide ions for seven days, and then inspected with optical microscopy. Results show that the magnetic field in the pipeline wall significantly increases pitting corrosion.

  6. Stainless steels reinforced with intermetallics useful against corrosion and wear

    OpenAIRE

    Torralba Castello, José Manuel

    2008-01-01

    Powder Technology Research Group has developed an innovative family of composite materials is presented. Metallic matrix are austenitic and ferritic stainless steels, and as reinforcements, intermetallics, have been used in quantities from 1% to 15% (vol.). These materials combine excellent properties against corrosion and wear, so they become very useful for structural applications, in areas like aerospace and automotive. The research group is trying to find companies in order to establis...

  7. Corrosion studies on casing steel in CO2 storage environments

    NARCIS (Netherlands)

    Zhang, X.; Zevenbergen, J.F.; Benedictus, T.

    2013-01-01

    The corrosion behavior of casing steel N80 in brine plus CO2 was studied in autoclave to simulate the CO2 storage environment. The brine solution used in the study contained 130 g/l NaCl, 22.2 g/l CaCl2 and 4 g/l MgCl2. The CO2 was charged in the autoclave at different pressures (60, 80 and 100 bar)

  8. Corrosion resistance of neodymium and dysprosium hydrides

    Science.gov (United States)

    Karakchieva, Natalia; Lyamina, Galina; Knyazeva, Elena; Sachkov, Victor; Kurzina, Irina; Pichugina, Alina; Vladimirov, Alexander; Kazantseva, Ludmila; Sachkova, Anna

    2017-11-01

    This paper describes the methods of obtaining hydrides of rare earth elements such as dysprosium and neodymium. The properties and corrosion resistance of these elements are investigated. A synthesis method of monophasic dysprosium and neodymium dihydrides is presented. Synthesized dihydrides are agglomerates with an average size of 3-50 µm and are formed by crystalline grains of a nanometer size. BET specific surface area, morphology, elemental analyses and composition of samples have been studied. Corrosion stability in aqueous solutions of hydrochloric acid and sodium hydroxide were studied. It was determined that both hydrides undergo hydrolysis in acid and alkaline mediums. Neodymium hydride is more stable to corrosion than dysprosium hydride, which is proved by its longer exposure to aggressive medium to hydrides. The formation of insoluble /poorly soluble products of corrosion can make a significant contribution to the process of powder dissolution.

  9. Field Testing of Rapid Electrokinetic Nanoparticle Treatment for Corrosion Control of Steel in Concrete

    Science.gov (United States)

    Cardenas, Henry E.; Alexander, Joshua B.; Kupwade-Patil,Kunal; Calle, Luz Marina

    2009-01-01

    This work field tested the use of electrokinetics for delivery of concrete sealing nanoparticles concurrent with the extraction of chlorides. Several cylinders of concrete were batched and placed in immersion at the Kennedy Space Center Beach Corrosion Test Site. The specimens were batched with steel reinforcement and a 4.5 wt.% (weight percent) content of sodium chloride. Upon arrival at Kennedy Space Center, the specimens were placed in the saltwater immersion pool at the Beach Corrosion Test Site. Following 30 days of saltwater exposure, the specimens were subjected to rapid chloride extraction concurrent with electrokinetic nanoparticle treatment. The treatments were operated at up to eight times the typical current density in order to complete the treatment in 7 days. The findings indicated that the short-term corrosion resistance of the concrete specimens was significantly enhanced as was the strength of the concrete.

  10. Accelerated corrosion of 2205 duplex stainless steel caused by marine aerobic Pseudomonas aeruginosa biofilm.

    Science.gov (United States)

    Xu, Dake; Xia, Jin; Zhou, Enze; Zhang, Dawei; Li, Huabing; Yang, Chunguang; Li, Qi; Lin, Hai; Li, Xiaogang; Yang, Ke

    2017-02-01

    Microbiologically influenced corrosion (MIC) of 2205 duplex stainless steel (DSS) in the presence of Pseudomonas aeruginosa was investigated through electrochemical and surface analyses. The electrochemical results showed that P. aeruginosa significantly reduced the corrosion resistance of 2205 DSS. Confocal laser scanning microscopy (CLSM) images showed that the depths of the largest pits on 2205 DSS with and without P. aeruginosa were 14.0 and 4.9μm, respectively, indicating that the pitting corrosion was accelerated by P. aeruginosa. X-ray photoelectron spectroscopy (XPS) results revealed that CrO 3 and CrN formed on the 2205 DSS surface in the presence of P. aeruginosa. Copyright © 2016 Elsevier B.V. All rights reserved.

  11. Mitigation of Mild Steel Corrosion in Acid by Green Inhibitors: Yeast, Pepper, Garlic, and Coffee

    National Research Council Canada - National Science Library

    Paul, Subir; Kar, Bikash

    2012-01-01

    .... Electrochemical studies of the effects of black pepper, garlic, yeast, and coffee on acid corrosion of steel have shown that the corrosion current decreases by manyfold with increase in concentration of the inhibitors...

  12. Elucidation of Atmospheric Corrosion Mechanism of Steels by Artificially Synthesized Iron Rust Particles

    National Research Council Canada - National Science Library

    田中, 秀和

    2015-01-01

    In order to clarify the atmospheric corrosion process of steel in different exposure environments, various methods such as exposure test, salt spray test, accelerated corrosion test, combined wet-dry...

  13. Corrosion protection service life of epoxy-coated reinforcing steel in Virginia bridge decks.

    Science.gov (United States)

    2003-01-01

    The corrosion protection service life extension provided by epoxy-coated reinforcement (ECR) was determined by comparing ECR and bare steel bars from 10 Virginia bridge decks built between 1981 and 1995. The objective was to determine the corrosion p...

  14. Effect of Exposure Face Orientation and Tilt Angle on Immersion Corrosion Behavior of Dual-Phase and Mild Steels

    Science.gov (United States)

    Murkute, Pratik; Choudhary, Sanjay; Ramkumar, J.; Mondal, K.

    2017-01-01

    The present study aims to investigate the effect of the exposure angle (0°, 30°, 45°, 60° and near 90°) and the number of exposed faces (skyward and downward surfaces) on the immersion corrosion behavior of a dual phase and a mild steel in freely aerated stagnant 3.5% NaCl solution for a period of 10 days. In one case, two surfaces are exposed simultaneously, whereas in other case, one of the surfaces is exposed, while other is lacquered. Analysis shows that the corrosion rate of the skyward surface is considerably high when both the surfaces are exposed. The corrosion rate of the downward surface is higher than that of the skyward sample, when one of the surfaces is exposed. Moreover, the corrosion rate gradually decreases from zero to near-90° orientation for all the cases. Though the effect of tilt angle and exposed face does not depend on steel varieties, the dual-phase steel has higher corrosion resistance than the mild steel. Relative oxygen content, microcell formation, gravity effect and reaction nature with depth are the plausible reasons for the observed variation of corrosion behavior.

  15. Can Thermally Sprayed Aluminum (TSA) Mitigate Corrosion of Carbon Steel in Carbon Capture and Storage (CCS) Environments?

    Science.gov (United States)

    Paul, S.; Syrek-Gerstenkorn, B.

    2017-01-01

    Transport of CO2 for carbon capture and storage (CCS) uses low-cost carbon steel pipelines owing to their negligible corrosion rates in dry CO2. However, in the presence of liquid water, CO2 forms corrosive carbonic acid. In order to mitigate wet CO2 corrosion, use of expensive corrosion-resistant alloys is recommended; however, the increased cost makes such selection economically unfeasible; hence, new corrosion mitigation methods are sought. One such method is the use of thermally sprayed aluminum (TSA), which has been used to mitigate corrosion of carbon steel in seawater, but there are concerns regarding its suitability in CO2-containing solutions. A 30-day test was carried out during which carbon steel specimens arc-sprayed with aluminum were immersed in deionized water at ambient temperature bubbled with 0.1 MPa CO2. The acidity (pH) and potential were continuously monitored, and the amount of dissolved Al3+ ions was measured after completion of the test. Some dissolution of TSA occurred in the test solution leading to nominal loss in coating thickness. Potential measurements revealed that polarity reversal occurs during the initial stages of exposure which could lead to preferential dissolution of carbon steel in the case of coating damage. Thus, one needs to be careful while using TSA in CCS environments.

  16. Study on corrosion of steels in marine environment by corrosion simulation device

    Energy Technology Data Exchange (ETDEWEB)

    Xiang, B.; Zhang, J.; Duan, J.Z. [Institute of Oceanology, Chinese Academy of Sciences, 7 Nanhai Road, Qingdao, 266071 (China); Hou, B.R. [Graduate School, Chinese Academy of Sciences, Beijing, 100039 (China)

    2003-09-01

    Three kinds of steels were studied using electrically connected hanging specimen in the corrosion simulation device and offshore long scale hanging specimen. The experimental results obtained by the two methods show that the device can better reflect the offshore corrosion environment. A Ni-Cu-P steel specimen was studied through analysis of the specimen's corrosion products and corrosion types. The surface of the samples before and after the removal of the rust layer produced by these two methods were observed and compared after some experiments. The microstructure of the corrosion products under different marine environments were analyzed and compared through IR. It indicated good correlation between the electrically connected hanging specimen method and the long scale hanging specimen method. (Abstract Copyright [2003], Wiley Periodicals, Inc.) [German] Mit Hilfe einer Korrosionssimulationsvorrichtung wurden drei Staehle untersucht, wobei haengende Proben im Grossmassstab verwendet wurden. Korrosionsarten und Korrosionsprodukte einer Ni-Cu-P-Stahlprobe wurden analysiert. Das Aussehen von zwei Methoden der Probenauslagerung und die Oberflaeche des metallischen Substrates nach der Entfernung der Rostschicht wurden beobachtet und bewertet. Die Phasenstruktur der Korrosionsprodukte unter verschiedenen marinen Umgebungen wurde analysiert und verglichen. Es zeigte sich eine gute Uebereinstimmung zwischen den zwei Methoden der Probenauslagerung. (Abstract Copyright [2003], Wiley Periodicals, Inc.)

  17. The effects of pharmaceutically active compound doxycycline on the corrosion of mild steel in hydrochloric acid solution

    Energy Technology Data Exchange (ETDEWEB)

    Shukla, Sudhish Kumar [Department of Applied Chemistry, Institute of Technology, Banaras Hindu University, Varanasi 221 005, Uttar Pradesh (India); Quraishi, M.A. [Department of Applied Chemistry, Institute of Technology, Banaras Hindu University, Varanasi 221 005, Uttar Pradesh (India)], E-mail: maquraishi.apc@itbhu.ac.in

    2010-02-15

    Corrosion inhibition of mild steel in hydrochloric acid solution by doxycycline has been studied by weight loss measurements, polarization resistance, Tafel polarization and electrochemical impedance spectroscopy. The inhibitor showed more than 95% inhibition efficiency at optimum concentration 9.02 x 10{sup -4} M. Potentiodynamic polarization suggests that it is a mixed type of inhibitor. Electrochemical impedance spectroscopy was used to investigate the mechanism of corrosion inhibition. Thermodynamic parameters were calculated to investigate mechanism of inhibition. The compound follows Langmuir adsorption isotherm. AFM studies of mild steel surface with and without inhibitor were performed and calculated roughness also supported the inhibition data.

  18. Effect of cold deformation on pitting corrosion of 00Cr18Mn15Mo2N0.86 stainless steel for coronary stent application.

    Science.gov (United States)

    Ren, Yibin; Zhao, Haochuan; Liu, Wenpeng; Yang, Ke

    2016-03-01

    The high nitrogen nickel-free stainless steel has offered an alternative to further improve the performance of the coronary stents, and simultaneously avoids the potential harms of nickel element. Both cold deformation and pitting corrosion are very important for coronary stents made of stainless steel. In this work, the effect of cold deformation on the pitting corrosion resistance of a high nitrogen nickel-free stainless steel (00Cr18Mn15Mo2N0.86) in 0.9% saline solution was investigated. The results showed that the pitting corrosion of the steel was nearly unchanged with increases of the cold deformation up to 50%, indicating that the higher nitrogen content can reduce the negative effect of cold deformation on the pitting corrosion resistance, which is beneficial for the long term service of coronary stents in blood vessel. Copyright © 2015 Elsevier B.V. All rights reserved.

  19. Microstructure, corrosion and tribological and antibacterial properties of Ti-Cu coated stainless steel.

    Science.gov (United States)

    Jin, Xiaomin; Gao, Lizhen; Liu, Erqiang; Yu, Feifei; Shu, Xuefeng; Wang, Hefeng

    2015-10-01

    A Ti-Cu coated layer on 316L stainless steel (SS) was obtained by using the Closed Field Unbalanced Magnetron Sputtering (CFUBMS) system to improve antibacterial activity, corrosion and tribological properties. The microstructure and phase constituents of Ti-Cu coated layer were characterized by using X-ray diffraction (XRD), scanning electron microscopy (SEM) and glow discharge optical emission spectrometry (GDOES). The corrosion and tribological properties of a stainless steel substrate, SS316L, when coated with Ti-Cu were investigated in a simulated body fluid (SBF) environment. The viability of bacteria attached to the antibacterial surface was tested using the spread plate method. The results indicate that the Ti-Cu coated SS316L could achieve a higher corrosion polarization resistance and a more stable corrosion potential in an SBF environment than the uncoated SS316L substrate. The desirable corrosion protection performance of Ti-Cu may be attributable to the formation of a Ti-O passive layer on the coating surface, protecting the coating from further corrosion. The Ti-Cu coated SS316L also exhibited excellent wear resistance and chemical stability during the sliding tests against Si3N4 balls in SBF environment. Moreover, the Ti-Cu coatings exhibited excellent antibacterial abilities, where an effective reduction of 99.9% of Escherichia coli (E.coli) within 12h was achieved by contact with the modified surface, which was attributed to the release of copper ions when the Ti-Cu coatings are in contact with bacterial solution. Copyright © 2015 Elsevier Ltd. All rights reserved.

  20. Characterisation of corrosion products on pipeline steel under cathodic protection

    Energy Technology Data Exchange (ETDEWEB)

    Lanarde, Lise [Gaz de France Research and Development Division, 361 avenue du President Wilson, BP33, 93211 Saint Denis La Plaine (France)]|[UPR15 du CNRS, Laboratoire des Interfaces et Systemes Electrochimiques, Universite Pierre et Marie Curie, C.P. 133, 4 Place Jussieu, 75252 Paris Cedex 05 (France); Campaignolle, Xavier; Karcher, Sebastien; Meyer, Michel [Gaz de France Research and Development Division, 361 avenue du President Wilson, BP33, 93211 Saint Denis La Plaine (France); Joiret, Suzanne [UPR15 du CNRS, Laboratoire des Interfaces et Systemes Electrochimiques, Universite Pierre et Marie Curie, C.P. 133, 4 Place Jussieu 75252 Paris Cedex 05 (France)

    2004-07-01

    Onshore gas transmission lines are conjointly protected against external corrosion by cathodic protection (CP) and organic coatings. If both protection systems are simultaneously faulty, the pipe may be subjected to local loss of protection criteria. Consequently, the development of a corrosion due to the ground intrinsic corrosiveness may occur. To guarantee an optimal and safe use of its 31000 km buried gas transmission network, Gaz de France regularly inspects its pipelines. When indications of metal damage are suspected, excavations are realized to carry out a finer diagnosis and, if necessary, to repair. Whenever, corrosions are encountered, although it occurs very scarcely, it is necessary to evaluate its degree of gravity: activity, mechanism, and kinetics. Among corrosion defects, it is indeed essential to differentiate those active, from those older inactive at the time of excavation, since those last ones may possibly have been annihilated, by a PC reinforcement for instance. Eventually, the identification of the corrosion mechanism and its associated rate will provide an assessment of the risks encountered by other sections of the pipeline similar to that excavated. This study investigates to what extent the degree of gravity (activity, kinetics) of a corrosion can be determined by the characterization and identification of its associated corrosion products. Moreover, it will attempt to relate it to the close environment features as well as to the operating conditions of the pipe. The preliminary results presented in this paper consist in a laboratory study of the time evolution of corrosion products formed on the surface of ordinary low carbon steel samples. The specimens have been previously subjected to various polarization conditions in various aqueous media. The selected solutions are characteristic of ground waters. The main parameters considered for the definition of the media were its initial chemical composition, pH and dissolved gas composition