  1. Failure analysis of corrosion cracking and simulated testing for a fluid catalytic cracking unit

    Institute of Scientific and Technical Information of China (English)

    Hua Chen; Xiaogang Li; Chaofang Dong; Ming Li; Jinwen Yang

    2005-01-01

    The failure of a fluid catalysis and cracking unit (FCCU) in a Chinese refinery was investigated by using nondestructive detection methods, fracture surface examination, hardness measurement, chemical composition and corrosion products analysis. The results showed that the failure was caused by the dew point nitrate stress corrosion cracking. For a long operation period, the wall temperature of the regenerator in the FCCU was below the fume dew point. As a result, an acid fume NOx-SOx-H2O medium presented on the surface, resulting in stress corrosion cracking of the component with high residual stress. In order to confirm the relative conclusion, simulated testing was conducted in laboratory, and the results showed similar cracking characteristics. Finally, some suggestions have been made to prevent the stress corrosion cracking of an FCCU from re-occurring in the future.

  2. EXPERT PANEL OVERSIGHT COMMITTEE ASSESSMENT OF FY2008 CORROSION AND STRESS CORROSION CRACKING SIMULANT TESTING PROGRAM

    Energy Technology Data Exchange (ETDEWEB)

    BOOMER KD

    2009-01-08

    The Expert Panel Oversight Committee (EPOC) has been overseeing the implementation of selected parts of Recommendation III of the final report, Expert Panel workshop for Hanford Site Double-Shell Tank Waste Chemistry Optimization, RPP-RPT-22126. Recommendation III provided four specific requirements necessary for Panel approval of a proposal to revise the chemistry control limits for the Double-Shell Tanks (DSTs). One of the more significant requirements was successful performance of an accelerated stress corrosion cracking (SCC) experimental program. This testing program has evaluated the optimization of the chemistry controls to prevent corrosion in the interstitial liquid and supernatant regions of the DSTs.

  3. A non-destructive test method to monitor corrosion products and corrosion-induced cracking in reinforced cement based materials

    DEFF Research Database (Denmark)

    Michel, Alexander; Pease, Bradley Justin; Peterova, Adela

    2011-01-01

    This paper introduces a non-destructive test method to monitor the development of corrosion products as well as the corrosion-induced formation and propagation of cracks in cementitious materials. A parametric experimental investigation (utilizing x-ray attenuation measurement technique...

  4. Modelling of Corrosion Cracks

    DEFF Research Database (Denmark)

    Thoft-Christensen, Palle

    Modelling of corrosion cracking of reinforced concrete structures is complicated as a great number of uncertain factors are involved. To get a reliable modelling a physical and mechanical understanding of the process behind corrosion in needed.......Modelling of corrosion cracking of reinforced concrete structures is complicated as a great number of uncertain factors are involved. To get a reliable modelling a physical and mechanical understanding of the process behind corrosion in needed....

  5. Some important considerations in the development of stress corrosion cracking test methods.

    Science.gov (United States)

    Wei, R. P.; Novak, S. R.; Williams, D. P.

    1972-01-01

    Discussion of some of the precaution needs the development of fracture-mechanics based test methods for studying stress corrosion cracking involves. Following a review of pertinent analytical fracture mechanics considerations and of basic test methods, the implications for test corrosion cracking studies of the time-to-failure determining kinetics of crack growth and life are examined. It is shown that the basic assumption of the linear-elastic fracture mechanics analyses must be clearly recognized and satisfied in experimentation and that the effects of incubation and nonsteady-state crack growth must also be properly taken into account in determining the crack growth kinetics, if valid data are to be obtained from fracture-mechanics based test methods.

  6. Corrosion fatigue behavior of fastening hole structure and virtual crack propagation tests

    Institute of Scientific and Technical Information of China (English)

    Youhong Zhang; Xinlong Chang; Guozhi Lv; Hui Wang; Zhong Li; Yueliang Cheng

    2008-01-01

    The fatigue crack propagation behavior of the LY12CZ aluminum alloy fastener involving a central hole in air or in 3.5wt% NaC1 solution was investigated. The experimental results indicated that the corrosion fatigue crack growth rate decreased with the increasing loading frequency, and in a corrosive environment, the crack growth rate was slightly larger than that in air.Based on the experimental results, the virtual corrosion fatigue crack propagation tests were investigated and the stochastic process method and the AFGROW simulation method were presented. The normal process and lognormal process were considered for the stochastic process method based on the numerically fitted Paris equation. The distribution of crack size and the corresponding prob-abilistic model of crack length distribution for a given number of cycles can be found by integrating the stochastic process over time.Using the AFGROW software, the virtual simulation was carried out to analyze the corrosion fatigue crack growth behavior and the predicted crack growth curve was in good agreement with the experimental results.

  7. A non-destructive test method to monitor corrosion products and corrosion-induced cracking in reinforced cement based materials

    DEFF Research Database (Denmark)

    Michel, Alexander; Pease, Bradley Justin; Peterova, Adela;

    2011-01-01

    ) was conducted to describe the impact of water-to-cement ratio and corrosion current density (i.e., corrosion rate) on the reinforcement corrosion process. Focus was placed, in particular on the determination of the corrosion accommodating region (CAR) and time to corrosion-induced cracking. Experimental results...

  8. The effect of heat treatment and test parameters on the aqueous stress corrosion cracking of D6AC steel

    Science.gov (United States)

    Gilbreath, W. P.; Adamson, M. J.

    1974-01-01

    The crack growth behavior of D6AC steel as a function of stress intensity, stress and corrosion history and test technique, under sustained load in natural seawater, 3.3 percent NaCl solution, distilled water, and high humidity air was investigated. Reported investigations of D6AC were considered with emphasis on thermal treatment, specimen configuration, fracture toughness, crack-growth rates, initiation period, threshold, and the extension of corrosion fatigue data to sustained load conditions. Stress history effects were found to be most important in that they controlled incubation period, initial crack growth rates, and apparent threshold.

  9. Simulated Service and Stress Corrosion Cracking Testing for Friction Stir Welded Spun Formed Domes

    Science.gov (United States)

    Stewart, Thomas J.; Torres, Pablo D.; Caratus, Andrei A.; Curreri, Peter A.

    2010-01-01

    Simulated service testing (SST) development was required to help qualify a new 2195 aluminum lithium (Al-Li) alloy spin forming dome fabrication process for the National Aeronautics and Space Administration (NASA) Exploration Development Technology Program. The application for the technology is to produce high strength low weight tank components for NASA s next generation launch vehicles. Since plate material is not currently manufactured large enough to fabricate these domes, two plates are joined by means of friction stir welding. The plates are then pre-contour machined to near final thicknesses allowing for a thicker weld land and anticipating the level of stretch induced by the spin forming process. The welded plates are then placed in a spin forming tool and hot stretched using a trace method producing incremental contours. Finally the dome receives a room temperature contour stretch to final dimensions, heat treatment, quenching, and artificial aging to emulate a T-8 condition of temper. Stress corrosion cracking (SCC) tests were also performed by alternate immersion in a sodium chloride (NaCl) solution using the typical double beam assembly and with 4-point loaded specimens and use of bent-beam stress-corrosion test specimens under alternate immersion conditions. In addition, experiments were conducted to determine the threshold stress intensity factor for SCC (K(sub ISCC)) which to our knowledge has not been determined previously for Al-Li 2195 alloy. The successful simulated service and stress corrosion testing helped to provide confidence to continue to Ares 1 scale dome fabrication

  10. Stress corrosion cracking of alloy 600 using the constant strain rate test

    Energy Technology Data Exchange (ETDEWEB)

    Bulischeck, T. S.; van Rooyen, D.

    1980-01-01

    The most recent corrosion problems experienced in nuclear steam generators tubed with Inconel alloy 600 is a phenomenon labeled ''denting''. Denting has been found in various degrees of severity in many operating pressurized water reactors. Laboratory investigations have shown that Inconel 600 exhibits intergranular SCC when subjected to high stresses and exposed to deoxygenated water at elevated temperatures. A research project was initiated at Brookhaven National Laboratory in an attempt to improve the qualitative and quantitative understanding of factors influencing SCC in high temperature service-related environments. An effort is also being made to develop an accelerated test method which could be used to predict the service life of tubes which have been deformed or are actively denting. Several heats of commercial Inconel 600 tubing were procured for testing in deaerated pure and primary water at temperatures from 290 to 365/sup 0/C. U-bend type specimens were used to determine crack initiation times which may be expected for tubes where denting has occurred but is arrested and provide baseline data for judging the accelerating effects of the slow strain rate method. Constant extension rate tests were employed to determine the crack velocities experienced in the crack propagation stage and predict failure times of tubes which are actively denting. 8 refs., 17 figs., 5 tabs.

  11. Report on Status of Shipment of High Fluence Austenitic Steel Samples for Characterization and Stress Corrosion Crack Testing

    Energy Technology Data Exchange (ETDEWEB)

    Clark, Scarlett R. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Leonard, Keith J. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2016-09-01

    The goal of the Mechanisms of Irradiation Assisted Stress Corrosion Cracking (IASCC) task in the LWRS Program is to conduct experimental research into understanding how multiple variables influence the crack initiation and crack growth in materials subjected to stress under corrosive conditions. This includes understanding the influences of alloy composition, radiation condition, water chemistry and metallurgical starting condition (i.e., previous cold work or heat treatments and the resulting microstructure) has on the behavior of materials. Testing involves crack initiation and growth testing on irradiated specimens of single-variable alloys in simulated Light Water Reactor (LWR) environments, tensile testing, hardness testing, microstructural and microchemical analysis, and detailed efforts to characterize localized deformation. Combined, these single-variable experiments will provide mechanistic understanding that can be used to identify key operational variables to mitigate or control IASCC, optimize inspection and maintenance schedules to the most susceptible materials/locations, and, in the long-term, design IASCC-resistant materials.

  12. Assessment of Initial Test Conditions for Experiments to Assess Irradiation Assisted Stress Corrosion Cracking Mechanisms

    Energy Technology Data Exchange (ETDEWEB)

    Busby, Jeremy T [ORNL; Gussev, Maxim N [ORNL

    2011-04-01

    Irradiation-assisted stress corrosion cracking is a key materials degradation issue in today s nuclear power reactor fleet and affects critical structural components within the reactor core. The effects of increased exposure to irradiation, stress, and/or coolant can substantially increase susceptibility to stress-corrosion cracking of austenitic steels in high-temperature water environments. . Despite 30 years of experience, the underlying mechanisms of IASCC are unknown. Extended service conditions will increase the exposure to irradiation, stress, and corrosive environment for all core internal components. The objective of this effort within the Light Water Reactor Sustainability program is to evaluate the response and mechanisms of IASCC in austenitic stainless steels with single variable experiments. A series of high-value irradiated specimens has been acquired from the past international research programs, providing a valuable opportunity to examine the mechanisms of IASCC. This batch of irradiated specimens has been received and inventoried. In addition, visual examination and sample cleaning has been completed. Microhardness testing has been performed on these specimens. All samples show evidence of hardening, as expected, although the degree of hardening has saturated and no trend with dose is observed. Further, the change in hardening can be converted to changes in mechanical properties. The calculated yield stress is consistent with previous data from light water reactor conditions. In addition, some evidence of changes in deformation mode was identified via examination of the microhardness indents. This analysis may provide further insights into the deformation mode under larger scale tests. Finally, swelling analysis was performed using immersion density methods. Most alloys showed some evidence of swelling, consistent with the expected trends for this class of alloy. The Hf-doped alloy showed densification rather than swelling. This observation may be

  13. Strain rate effects in stress corrosion cracking

    Energy Technology Data Exchange (ETDEWEB)

    Parkins, R.N. (Newcastle upon Tyne Univ. (UK). Dept. of Metallurgy and Engineering Materials)

    1990-03-01

    Slow strain rate testing (SSRT) was initially developed as a rapid, ad hoc laboratory method for assessing the propensity for metals an environments to promote stress corrosion cracking. It is now clear, however, that there are good theoretical reasons why strain rate, as opposed to stress per se, will often be the controlling parameter in determining whether or not cracks are nucleated and, if so, are propagated. The synergistic effects of the time dependence of corrosion-related reactions and microplastic strain provide the basis for mechanistic understanding of stress corrosion cracking in high-pressure pipelines and other structures. However, while this may be readily comprehended in the context of laboratory slow strain tests, its extension to service situations may be less apparent. Laboratory work involving realistic stressing conditions, including low-frequency cyclic loading, shows that strain or creep rates give good correlation with thresholds for cracking and with crack growth kinetics.

  14. Reconstruction of stress corrosion cracks using signals of pulsed eddy current testing

    Science.gov (United States)

    Wang, Li; Xie, Shejuan; Chen, Zhenmao; Li, Yong; Wang, Xiaowei; Takagi, Toshiyuki

    2013-06-01

    A scheme to apply signals of pulsed eddy current testing (PECT) to reconstruct a deep stress corrosion crack (SCC) is proposed on the basis of a multi-layer and multi-frequency reconstruction strategy. First, a numerical method is introduced to extract conventional eddy current testing (ECT) signals of different frequencies from the PECT responses at different scanning points, which are necessary for multi-frequency ECT inversion. Second, the conventional fast forward solver for ECT signal simulation is upgraded to calculate the single-frequency pickup signal of a magnetic field by introducing a strategy that employs a tiny search coil. Using the multiple-frequency ECT signals and the upgraded fast signal simulator, we reconstructed the shape profiles and conductivity of an SCC at different depths layer-by-layer with a hybrid inversion scheme of the conjugate gradient and particle swarm optimisation. Several modelled SCCs of rectangular or stepwise shape in an SUS304 plate are reconstructed from simulated PECT signals with artificial noise. The reconstruction results show better precision in crack depth than the conventional ECT inversion method, which demonstrates the validity and efficiency of the proposed PECT inversion scheme.

  15. Cracking and corrosion recovery boiler

    Energy Technology Data Exchange (ETDEWEB)

    Suik, H. [Tallinn Technical University, Horizon Pulp and Paper, Tallinn (Estonia)

    1998-12-31

    The corrosion of heat surfaces and the cracking the drums are the main problems of the recovery boiler. These phenomena have been appeared during long-term operation of boiler `Mitsubishi - 315` erected at 1964. Depth of the crack is depending on the number of shutdowns and on operation time. Corrosion intensity of different heat surfaces is varying depend on the metal temperature and the conditions at place of positioning of tube. The lowest intensity of corrosion is on the bank tubes and the greatest is on the tubes of the second stage superheater and on the tubes at the openings of air ports. (orig.) 5 refs.

  16. H2S Stress Corrosion Tests of Welded Joint for X65 Pipeline Steel and Finite Element Numerical Analysis of Crack Tip

    Institute of Scientific and Technical Information of China (English)

    金晓军; 霍立兴; 张玉凤; 白秉仁; 李小巍; 曹军

    2003-01-01

    The microstructure of welded joint is surveyed and the mechanical properties of X65 pipeline steel are studied in this paper, which provides experimental basis of performance effect on stress corrosion. H2S stress corrosion cracking (SCC) tests on the steel are carried out in the environment based on NACE TM-01-77 solution. The threshold stress intensity factor and crack propagation velocity for base metal and HAZ are obtained. The susceptibility of welded joint for X65 pipeline steel to H2S stress corrosion cracking is investigated. The programming package ANSYS of finite element model (FEM) is used to perform the three-dimensional elastic-plastic finite element analysis of WOL specimens. Stress field and concentration of hydrogen distribution property of the crack tip are obtained.

  17. Numerical Study of Corrosion Crack Opening

    DEFF Research Database (Denmark)

    Thoft-Christensen, Palle; Frandsen, Henrik Lund; Svensson, Staffan

    2008-01-01

    for the corrosion crack opening. Experiments and theoretical analysis by a numerical method, FEM, support that the relation between the reduction of the reinforcement bar diameter due to corrosion and the corresponding increase in crack width for a given time interval, measured on the surface of a concrete specimen...... is proportional. More recently, the constant of proportionality, the so-called crack-corrosion index, has been studied further with respect to its dependence on the diameter of the reinforcement and the concrete cover. In the present paper the above-mentioned work is presented and extended with more realistic 3D......-models of the cracked concrete beam. The crack-corrosion index is evaluated for a variation of different parameters, i.e. bar diameter, concrete cover, crack length and type of corrosion product. This paper is an extended version of a paper by Thoft-Christensen et al. (2005) presented at the IFIP WG 7.5 Conference...

  18. Report on Status of Shipment of High Fluence Austenitic Steel Samples for Characterization and Stress Corrosion Crack Testing

    Energy Technology Data Exchange (ETDEWEB)

    Clark, Scarlett R. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Leonard, Keith J. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2016-09-01

    The goal of the Mechanisms of Irradiation Assisted Stress Corrosion Cracking (IASCC) task in the LWRS Program is to conduct experimental research into understanding how multiple variables influence the crack initiation and crack growth in materials subjected to stress under corrosive conditions. This includes understanding the influences of alloy composition, radiation condition, water chemistry and metallurgical starting condition (i.e., previous cold work or heat treatments and the resulting microstructure) has on the behavior of materials. Testing involves crack initiation and growth testing on irradiated specimens of single-variable alloys in simulated Light Water Reactor (LWR) environments, tensile testing, hardness testing, microstructural and microchemical analysis, and detailed efforts to characterize localized deformation. Combined, these single-variable experiments will provide mechanistic understanding that can be used to identify key operational variables to mitigate or control IASCC, optimize inspection and maintenance schedules to the most susceptible materials/locations, and, in the long-term, design IASCC-resistant materials. In support of this research, efforts are currently underway to arrange shipment of “free” high fluence austenitic alloys available through Électricité de France (EDF) for post irradiation testing at the Oak Ridge National Laboratory (ORNL) and IASCC testing at the University of Michigan. These high fluence materials range in damage values from 45 to 125 displacements per atom (dpa). The samples identified for transport to the United States, which include nine, no-cost, 304, 308 and 316 tensile bars, were relocated from the Research Institute of Atomic Reactors (RIAR) in Dimitrovgrad, Ulyanovsk Oblast, Russia, and received at the Halden Reactor in Halden, Norway, on August 23, 2016. ORNL has been notified that a significant amount of work is required to prepare the samples for further shipment to Oak Ridge, Tennessee. The

  19. Irradiation Programs and Test Plans to Assess High-Fluence Irradiation Assisted Stress Corrosion Cracking Susceptibility.

    Energy Technology Data Exchange (ETDEWEB)

    Teysseyre, Sebastien [Idaho National Lab. (INL), Idaho Falls, ID (United States)

    2015-03-01

    . Irradiation assisted stress corrosion cracking (IASCC) is a known issue in current reactors. In a 60 year lifetime, reactor core internals may experience fluence levels up to 15 dpa for boiling water reactors (BWR) and 100+ dpa for pressurized water reactors (PWR). To support a safe operation of our fleet of reactors and maintain their economic viability it is important to be able to predict any evolution of material behaviors as reactors age and therefore fluence accumulated by reactor core component increases. For PWR reactors, the difficulty to predict high fluence behavior comes from the fact that there is not a consensus of the mechanism of IASCC and that little data is available. It is however possible to use the current state of knowledge on the evolution of irradiated microstructure and on the processes that influences IASCC to emit hypotheses. This report identifies several potential changes in microstructure and proposes to identify their potential impact of IASCC. The susceptibility of a component to high fluence IASCC is considered to not only depends on the intrinsic IASCC susceptibility of the component due to radiation effects on the material but to also be related to the evolution of the loading history of the material and interaction with the environment as total fluence increases. Single variation type experiments are proposed to be performed with materials that are representative of PWR condition and with materials irradiated in other conditions. To address the lack of IASCC propagation and initiation data generated with material irradiated in PWR condition, it is proposed to investigate the effect of spectrum and flux rate on the evolution of microstructure. A long term irradiation, aimed to generate a well-controlled irradiation history on a set on selected materials is also proposed for consideration. For BWR, the study of available data permitted to identify an area of concern for long term performance of component. The efficiency of

  20. Stress Corrosion Cracking of X80 Pipeline Steel in Near-Neutral pH Environment under Constant Load Tests with and without Preload

    Institute of Scientific and Technical Information of China (English)

    Y.Z. Jia; J.Q. Wang; E.H. Han; W. Ke1

    2011-01-01

    Constant load tests in NS4 solution purged with N2-5%CO2 gas mixture were conducted on American Petroleum Institute (API) X80 pipeline steel applied in the 2nd West-East (;as Pipeline project with and without preload. The results show that cracks could initiate and propagate in X80 pipeline steel in near-neutral pH environment under a constant load condition. The life of crack initiation and propagation increased with decreasing applied stress. Preload did not change its corrosion behavior obviously. However, preload reduced the time for crack initiation.

  1. A Monitoring Method Based on FBG for Concrete Corrosion Cracking

    Science.gov (United States)

    Mao, Jianghong; Xu, Fangyuan; Gao, Qian; Liu, Shenglin; Jin, Weiliang; Xu, Yidong

    2016-01-01

    Corrosion cracking of reinforced concrete caused by chloride salt is one of the main determinants of structure durability. Monitoring the entire process of concrete corrosion cracking is critical for assessing the remaining life of the structure and determining if maintenance is needed. Fiber Bragg Grating (FBG) sensing technology is extensively developed in photoelectric monitoring technology and has been used on many projects. FBG can detect the quasi-distribution of strain and temperature under corrosive environments, and thus it is suitable for monitoring reinforced concrete cracking. According to the mechanical principle that corrosion expansion is responsible for the reinforced concrete cracking, a package design of reinforced concrete cracking sensors based on FBG was proposed and investigated in this study. The corresponding relationship between the grating wavelength and strain was calibrated by an equal strength beam test. The effectiveness of the proposed method was verified by an electrically accelerated corrosion experiment. The fiber grating sensing technology was able to track the corrosion expansion and corrosion cracking in real time and provided data to inform decision-making for the maintenance and management of the engineering structure. PMID:27428972

  2. A Monitoring Method Based on FBG for Concrete Corrosion Cracking

    Directory of Open Access Journals (Sweden)

    Jianghong Mao

    2016-07-01

    Full Text Available Corrosion cracking of reinforced concrete caused by chloride salt is one of the main determinants of structure durability. Monitoring the entire process of concrete corrosion cracking is critical for assessing the remaining life of the structure and determining if maintenance is needed. Fiber Bragg Grating (FBG sensing technology is extensively developed in photoelectric monitoring technology and has been used on many projects. FBG can detect the quasi-distribution of strain and temperature under corrosive environments, and thus it is suitable for monitoring reinforced concrete cracking. According to the mechanical principle that corrosion expansion is responsible for the reinforced concrete cracking, a package design of reinforced concrete cracking sensors based on FBG was proposed and investigated in this study. The corresponding relationship between the grating wavelength and strain was calibrated by an equal strength beam test. The effectiveness of the proposed method was verified by an electrically accelerated corrosion experiment. The fiber grating sensing technology was able to track the corrosion expansion and corrosion cracking in real time and provided data to inform decision-making for the maintenance and management of the engineering structure.

  3. A Monitoring Method Based on FBG for Concrete Corrosion Cracking.

    Science.gov (United States)

    Mao, Jianghong; Xu, Fangyuan; Gao, Qian; Liu, Shenglin; Jin, Weiliang; Xu, Yidong

    2016-07-14

    Corrosion cracking of reinforced concrete caused by chloride salt is one of the main determinants of structure durability. Monitoring the entire process of concrete corrosion cracking is critical for assessing the remaining life of the structure and determining if maintenance is needed. Fiber Bragg Grating (FBG) sensing technology is extensively developed in photoelectric monitoring technology and has been used on many projects. FBG can detect the quasi-distribution of strain and temperature under corrosive environments, and thus it is suitable for monitoring reinforced concrete cracking. According to the mechanical principle that corrosion expansion is responsible for the reinforced concrete cracking, a package design of reinforced concrete cracking sensors based on FBG was proposed and investigated in this study. The corresponding relationship between the grating wavelength and strain was calibrated by an equal strength beam test. The effectiveness of the proposed method was verified by an electrically accelerated corrosion experiment. The fiber grating sensing technology was able to track the corrosion expansion and corrosion cracking in real time and provided data to inform decision-making for the maintenance and management of the engineering structure.

  4. A STUDY OF CORROSION AND STRESS CORROSION CRACKING OF CARBON STEEL NUCLEAR WASTE STORAGE TANKS

    Energy Technology Data Exchange (ETDEWEB)

    BOOMER, K.D.

    2007-08-21

    The Hanford reservation Tank Farms in Washington State has 177 underground storage tanks that contain approximately 50 million gallons of liquid legacy radioactive waste from cold war plutonium production. These tanks will continue to store waste until it is treated and disposed. These nuclear wastes were converted to highly alkaline pH wastes to protect the carbon steel storage tanks from corrosion. However, the carbon steel is still susceptible to localized corrosion and stress corrosion cracking. The waste chemistry varies from tank to tank, and contains various combinations of hydroxide, nitrate, nitrite, chloride, carbonate, aluminate and other species. The effect of each of these species and any synergistic effects on localized corrosion and stress corrosion cracking of carbon steel have been investigated with electrochemical polarization, slow strain rate, and crack growth rate testing. The effect of solution chemistry, pH, temperature and applied potential are all considered and their role in the corrosion behavior will be discussed.

  5. Corrosion and Cracking of Reinforced Concrete

    DEFF Research Database (Denmark)

    Thoft-Christensen, Palle

    Modelling of the deterioration of reinforced concrete has in recent years changed from being a deterministic modelling based on experience to be stochastic modelling based on sound and consistent physical, chemical and mechanical principles. In this paper is presented a brief review of modern mod...... for time to initial corrosion, time to initial cracking, and time to a given crack width may be obtained....

  6. The Growth of Small Corrosion Fatigue Cracks in Alloy 7075

    Science.gov (United States)

    Piascik, Robert S.

    2015-01-01

    The corrosion fatigue crack growth characteristics of small (greater than 35 micrometers) surface and corner cracks in aluminum alloy 7075 is established. The early stage of crack growth is studied by performing in situ long focal length microscope (500×) crack length measurements in laboratory air and 1% sodium chloride (NaCl) environments. To quantify the "small crack effect" in the corrosive environment, the corrosion fatigue crack propagation behavior of small cracks is compared to long through-the-thickness cracks grown under identical experimental conditions. In salt water, long crack constant K(sub max) growth rates are similar to small crack da/dN.

  7. Frequency dependence of fatigue and corrosion fatigue crack growth rate

    Energy Technology Data Exchange (ETDEWEB)

    Marvasti, Mohammad Hassan; Chen, Weixing [Department of Chemical and Materials Engineering, University of Alberta, Edmonton, AB (Canada); Kania, Richard; Worthingham, Robert [TransCanada Pipelines Limited, Calgary, AB (Canada); Van Boven, Gregory [Spectra Energy Transmission Limited, Vancouver, BC (Canada)

    2010-07-01

    It was in the mid-1980s that stress corrosion cracking (SCC) was first found in near-neutral pH conditions on the TransCanada pipeline system. Since then, there have been many reports of pipeline cracking in Canada in these conditions. The huge quantity of pipelines in Canada and the number of failures have brought great interest in investigation of this cracking. A study was conducted on one X52 pipeline steel. It used compact tension specimens for corrosion fatigue and fatigue tests in air. The following conclusions were drawn: 1) crack growth in near-neutral pH conditions can be explained by a factor, which reflects the combined action of the mechanical driving force and the hydrogen effects; 2) mechanical dormancy can be common when oil and gas pipelines are in operation; 3) hydrogen is a determining factor of crack growth when pipeline steels are exposed to near-neutral pH conditions.

  8. Propagation of stress corrosion cracks in alpha-brasses

    Energy Technology Data Exchange (ETDEWEB)

    Beggs, Dennis Vinton [Univ. of Illinois, Urbana-Champaign, IL (United States)

    1981-01-01

    Transgranular and intergranular stress corrosion cracks were investigated in alpha-brasses in a tarnishing ammoniacal solution. Surface observation indicated that the transgranular cracks propagated discontinuously by the sudden appearance of a fine crack extending several microns ahead of the previous crack tip, often associated with the detection of a discrete acoustic emission (AE). By periodically increasing the deflection, crack front markings were produced on the resulting fracture surfaces, showing that the discontinuous propagation of the crack trace was representative of the subsurface cracking. The intergranular crack trace appeared to propagate continuously at a relatively blunt crack tip and was not associated with discrete AE. Under load pulsing tests with a time between pulses, Δt greater than or equal to 3 s, the transgranular fracture surfaces always exhibited crack front markings which corresponded with the applied pulses. The spacing between crack front markings, Δx, decreased linearly with Δt. With Δt less than or equal to 1.5 s, the crack front markings were in a one-to-one correspondence with applied pulses only at relatively long crack lengths. In this case, Δx = Δx* which approached a limiting value of 1 μm. No crack front markings were observed on intergranular fracture surfaces produced during these tests. It is concluded that transgranular cracking occurs by discontinuous mechanical fracture of an embrittled region around the crack tip, while intergranular cracking results from a different mechanism with cracking occurring via the film-rupture mechanism.

  9. A Calculation Model for Corrosion Cracking in RC Structures

    Institute of Scientific and Technical Information of China (English)

    Xu Gang; Wei Jun; Zhang Keqiang; Zhou Xiwu

    2007-01-01

    A novel calculation model is proposed aiming at the problem of concrete cover cracking induced by reinforcement corrosion. In this article, the relationship between the corrosion depth of the bar and the thickness of the rust layer is established. By deducing the radial displacement expression of concrete, the formula for corrosion depth and corrosion pressure before cracking is proposed. The crack depth of cover in accordance with the maximum corrosion pressure is deduced; furthermore, the corrosion depth and corrosion pressure at the cracking time are obtained. Finally, the theoretical model is validated by several experiments, and the calculated values agree well with the experiment results.

  10. Stress corrosion cracking of several high strength ferrous and nickel alloys

    Science.gov (United States)

    Nelson, E. E.

    1971-01-01

    The stress corrosion cracking resistance of several high strength ferrous and nickel base alloys has been determined in a sodium chloride solution. Results indicate that under these test conditions Multiphase MP35N, Unitemp L605, Inconel 718, Carpenter 20Cb and 20Cb-3 are highly resistant to stress corrosion cracking. AISI 410 and 431 stainless steels, 18 Ni maraging steel (250 grade) and AISI 4130 steel are susceptible to stress corrosion cracking under some conditions.

  11. Corrosion Testing Facility

    Data.gov (United States)

    Federal Laboratory Consortium — The Corrosion Testing Facility is part of the Army Corrosion Office (ACO). It is a fully functional atmospheric exposure site, called the Corrosion Instrumented Test...

  12. Stress corrosion cracking tests for low and high alloy steels in sour oilfield service. Tests performed at VTT

    Energy Technology Data Exchange (ETDEWEB)

    Saarinen, K. [VTT Manufacturing Technology, Espoo (Finland). Materials and Structural Integrity; Haemaelaeinen, E. [Helsinki Univ. of Technology, Otaniemi (Finland). Lab. of Engineering Materials

    1996-10-01

    The purpose of the studies was to validate the usefulness of the proposed NACE slow strain rate testing method and compare it with the EFC document. In the NACE document the testing takes place at a temperature of 177 deg C, the test solution contains 20 wt% NaCl, the partial pressure of H{sub 2}S varies between 14 and 28 bar and the partial pressure of CO{sub 2} between 14 and 55 bar. In the NACE document the strain rate is determined as 4 x 10{sup -6} 1/s and in the EFC document 1 x 10{sup -6} 1/s. The results showed brittle behaviour for the test material in all of the test environments, and in each case the elongation was less than 5%. For comparison purposes the SSRT was conducted with the test material also in an inert environment (N{sub 2} gas), where the fracture was ductile and elongation 65%. The tests conducted with different strain rates gave the same result, which shows that the difference between EFC and NACE documents within the strain rate is not significant in the environments studied. However, since the alloy 654 SMO, which is considered to have a high resistance to corrosion, failed the SSRT test in the environments determined in the NACE document, the NACE document can be considered too severe for testing of austenitic stainless steels. Since contrary to the NACE document the EFC document does not determine levels for hydrogen sulphide and carbon dioxide, the EFC document can be considered more suitable than the NACE document for testing of austenitic stainless steels for sour service. (author)

  13. Stress Corrosion Cracking of Pipeline Steels

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    This paper provides a review of the differences between high pH and near-neutral pH stress corrosion cracking ofpipeline steels, influencing factors, and mechanisms. The characteristics and historical information on both forms ofSCC are discussed. The prospect for research in the future is also presented.

  14. Concrete Cracking Prediction Including the Filling Proportion of Strand Corrosion Products

    Directory of Open Access Journals (Sweden)

    Lei Wang

    2016-12-01

    Full Text Available The filling of strand corrosion products during concrete crack propagation is investigated experimentally in the present paper. The effects of stirrups on the filling of corrosion products and concrete cracking are clarified. A prediction model of crack width is developed incorporating the filling proportion of corrosion products and the twisting shape of the strand. Experimental data on cracking angle, crack width, and corrosion loss obtained from accelerated corrosion tests of concrete beams are presented. The proposed model is verified by experimental data. Results show that the filling extent of corrosion products varies with crack propagation. The rust filling extent increases with the propagating crack until a critical width. Beyond the critical width, the rust-filling extent remains stable. Using stirrups can decrease the critical crack width. Stirrups can restrict crack propagation and reduce the rust filling. The tangent of the cracking angle increases with increasing corrosion loss. The prediction of corrosion-induced crack is sensitive to the rust-filling extent.

  15. Standard test method for evaluating stress-corrosion cracking of stainless alloys with different nickel content in boiling acidified sodium chloride solution

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2000-01-01

    1.1 This test method describes a procedure for conducting stress-corrosion cracking tests in an acidified boiling sodium chloride solution. This test method is performed in 25% (by mass ) sodium chloride acidified to pH 1.5 with phosphoric acid. This test method is concerned primarily with the test solution and glassware, although a specific style of U-bend test specimen is suggested. 1.2 This test method is designed to provide better correlation with chemical process industry experience for stainless steels than the more severe boiling magnesium chloride test of Practice G36. Some stainless steels which have provided satisfactory service in many environments readily crack in Practice G36, but have not cracked during interlaboratory testing using this sodium chloride test method. 1.3 This boiling sodium chloride test method was used in an interlaboratory test program to evaluate wrought stainless steels, including duplex (ferrite-austenite) stainless and an alloy with up to about 33% nickel. It may also b...

  16. The stress corrosion cracking behaviour of heat-treated Al-Zn-Mg-Cu alloy in modified salt spray fog testing

    Energy Technology Data Exchange (ETDEWEB)

    Onoro, J. [Ingenieria y Ciencia de los Materiales, Universidad Politecnica de Madrid, ETS Ingenieros Industriales, Madrid (Spain)

    2010-02-15

    The stress corrosion cracking behaviour of 7075 (Al-Zn-Mg-Cu) alloy have been studied in a salt spray fog chamber with two vapourised aqueous solutions (0 and 5% NaCl). The paper analyses the stress corrosion resistance of 7075 aluminium alloy with several precipitation-ageing heat treatments. The results are compared with that obtained in 3.5% NaCl aqueous solution at 20 C. The salt spray fog testing has permitted a good evaluation of SCC susceptibility in 7075 alloy. All temper conditions studied were susceptible to SCC in the different environments tested. 7075-T6 temper was the most susceptible, while in all the cases studied 7075-T73 temper was the least susceptible. Compared to 7075-T6, 7075-RRA temper improved the resistance against the SCC process, but the mechanical properties obtained were lower. (Abstract Copyright [2010], Wiley Periodicals, Inc.)

  17. Stress-corrosion cracking of titanium alloys.

    Science.gov (United States)

    Blackburn, M. J.; Feeney, J. A.; Beck, T. R.

    1973-01-01

    In the light of research material published up to May 1970, the current understanding of the experimental variables involved in the stress-corrosion cracking (SCC) behavior of titanium and its alloys is reviewed. Following a brief summary of the metallurgy and electrochemistry of titanium alloys, the mechanical, electrochemical, and metallurgical parameters influencing SCC behavior are explored with emphasis on crack growth kinetics. Macro- and microfeatures of fractures are examined, and it is shown that many transgranular SCC failures exhibit morphological and crystallographic features similar to mechanical cleavage failures. Current SCC models are reviewed with respect to their ability to explain the observed SCC behavior of titanium and its alloys. Possible methods for eliminating or minimizing stress corrosion hazards in titanium or titanium alloy components are described.

  18. Consideration on corrosion fatigue crack life assessment; Fushoku hiro kiretsu hassei jumyo hyoka ni kansuru ichikosatsu

    Energy Technology Data Exchange (ETDEWEB)

    Yajima, H.; Yamamoto, M.; Saito, T. [Hiroshima University, Hiroshima (Japan). Faculty of Engineering; Morita, K. [Mitsubishi Heavy Industries, Ltd., Tokyo (Japan)

    1996-10-01

    Discussions were given on corrosion fatigue crack life by using corrosion fatigue crack initiation test and analysis. The test used 13Cr-based stainless steel as a test material, and aquamarine at 60{degree}C as a corrosion environment. The fatigue test was performed under a tension loading condition with a stress ratio of 0.1 and an iterative velocity of 1.7 Hz by using a 10-tonf fatigue testing machine. In the corrosion fatigue crack initiation test, a pit has been generated on a boundary of an exposed part and a painted part for masking, hence direct observation was impossible on pit growth behavior. Therefore, an intrinsic crack model was introduced from pit dimensions as observed from a fracture face, and analysis was made on corrosion fatigue crack growth by using the linear fracture dynamics, wherein clarification was made on a phenomenon occurring after the crack growth passes the pit growth until the test piece is fractured. A proposal was made to define the time when fatigue crack initiates and grows from the bottom of a pit as a result of surpassing the growth of corrosion pit as the corrosion fatigue crack life. 4 refs., 7 figs., 1 tab.

  19. Sizing stress corrosion cracks using laser ultrasonics

    Energy Technology Data Exchange (ETDEWEB)

    Rehman, Hamood; McNealy, Rick; Fingerhut, Martin [Applus-RTD. Houston, TX (United States); Klein, Marvin; Ansari, Homayoon [Intelligent Optical Systems, Inc. Los Angeles, CA (United States); Kania Richard [TransCanada. Calgary, AB (Canada); Rapp, Steve [Spectra Energy, Houston, TX (United States)

    2010-07-01

    Despite various efforts, no reliable tools and techniques are available to enable an operator to quantify the impact of an SCC (Stress Corrosion Cracking) colony on the safety and integrity of a pipeline. Reliable non-destructive detection and measurement tools are not available either. There is therefore a large gap between current technology and the needs of the pipeline industry. Recent developments promise that with a concentrated effort, a comprehensive solution can be devised. This paper describes technical work performed to develop and validate both the inspection tool and the time of flight diffraction (TOFD) technique for sizing the depth of SCC. It also presents preliminary results of work on a closely related project that provides, on the basis of this technology, an integrated approach and tool for mapping, sizing, and evaluating SCC, through which significant cracks are filtered from more benign cracks within an SCC colony.

  20. Stress corrosion cracking of copper canisters

    Energy Technology Data Exchange (ETDEWEB)

    King, Fraser (Integrity Corrosion Consulting Limited (Canada)); Newman, Roger (Univ. of Toronto (Canada))

    2010-12-15

    A critical review is presented of the possibility of stress corrosion cracking (SCC) of copper canisters in a deep geological repository in the Fennoscandian Shield. Each of the four main mechanisms proposed for the SCC of pure copper are reviewed and the required conditions for cracking compared with the expected environmental and mechanical loading conditions within the repository. Other possible mechanisms are also considered, as are recent studies specifically directed towards the SCC of copper canisters. The aim of the review is to determine if and when during the evolution of the repository environment copper canisters might be susceptible to SCC. Mechanisms that require a degree of oxidation or dissolution are only possible whilst oxidant is present in the repository and then only if other environmental and mechanical loading conditions are satisfied. These constraints are found to limit the period during which the canisters could be susceptible to cracking via film rupture (slip dissolution) or tarnish rupture mechanisms to the first few years after deposition of the canisters, at which time there will be insufficient SCC agent (ammonia, acetate, or nitrite) to support cracking. During the anaerobic phase, the supply of sulphide ions to the free surface will be transport limited by diffusion through the highly compacted bentonite. Therefore, no HS. will enter the crack and cracking by either of these mechanisms during the long term anaerobic phase is not feasible. Cracking via the film-induced cleavage mechanism requires a surface film of specific properties, most often associated with a nano porous structure. Slow rates of dissolution characteristic of processes in the repository will tend to coarsen any nano porous layer. Under some circumstances, a cuprous oxide film could support film-induced cleavage, but there is no evidence that this mechanism would operate in the presence of sulphide during the long-term anaerobic period because copper sulphide

  1. Concrete cover cracking with localized corrosion of reinforcing steel

    Energy Technology Data Exchange (ETDEWEB)

    Torres-Acosta, A. A.; Sagues, A. A. [South Florida Univ., Dept of Civil and Environmental Engineering, Tampa FL (United States)

    2000-07-01

    The critical amount of steel corrosion needed for concrete cover cracking of a reinforced concrete element was measured, focusing on cases where only a fraction of the steel bar length is corroding. The amount of corrosion needed to crack the concrete cover was found to range between 49 micrometre to 137 micrometre in specimens of localized corrosion. In contrast, in cases of uniform corrosion of comparable systems the corrosion needed to crack the concrete cover varied from 15 micrometre to 75 micrometer. Based on this and previous work on this problem, an empirical equation is proposed for the critical amount of steel corrosion as a function of specimen dimensions. The model proposed for estimating the critical amount of steel corrosion showed reasonable agreement between estimates of the work of corrosion expansion and the energy required to crack the concrete. 23 refs., 3 tabs., 8 figs.

  2. Monitoring reinforcement corrosion and corrosion-induced cracking using non-destructive x-ray attenuation measurements

    DEFF Research Database (Denmark)

    Michel, Alexander; Pease, Bradley Justin; Geiker, Mette Rica

    2011-01-01

    To test the applicability of the x-ray attenuation method to monitor the movement of corrosion products as well as the formation and propagation of cracks in cementitious materials reinforced mortar samples were prepared and tested under accelerated corrosion conditions. It is evident from...

  3. Stress corrosion cracking for 316 stainless steel clips in a condensate stabilizer

    Energy Technology Data Exchange (ETDEWEB)

    Al-Awar, A.; Aldajah, S.; Harhara, A. [Department of Mechanical Engineering, United Arab Emirates University, P. O. Box 17555 Al-AIn 17555 (United Arab Emirates)

    2011-09-15

    In one of the gas processing facilities in Abu Dhabi, UAE; a case of 316L stainless steel material failure occurred in the fractionating column due to stress cracking corrosion twice in a cycle of less than 2 years. This paper studies the stress corrosion cracking behavior of the 316L stainless steel in an accelerated corrosion environment and compares it with a higher corrosion resistant nickel alloy (Inconel 625). The experimental work was designed according to ASTM G36 standard, the samples were immersed in a boiling magnesium chloride medium which provided the accelerated corrosion environment and the tested samples were shaped into U-bend specimens as they underwent both plastic and elastic stresses. The specimens were then tested to determine the time required for cracks to initiate. The results of the experimental work showed that the main mode of failure was stress corrosion cracking initiated by the proven presence of chlorides, hydrogen sulfide, and water at elevated temperatures. Inconel 625 samples placed in the controlled environment showed better corrosion resistance as it took them an average of 56 days to initiate cracks, whereas it took an average of 24 days to initiate cracks in the stainless steel 316L samples. The scanning electron microscopy (SEM) micrographs showed that the cracks in the stainless steel 316L samples were longer, wider, and deeper compared to the cracks of Inconel 625. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  4. Susceptibility to Stress Corrosion Cracking of 254SMO SS

    Directory of Open Access Journals (Sweden)

    De Micheli Lorenzo

    2002-01-01

    Full Text Available The susceptibility to stress corrosion cracking (SCC of solubilized and sensitized 254SMO SS was studied in sodium chloride, and sodium fluoride solutions at 80 °C and sulfuric acid solutions in presence of sodium chloride at 25 °C. The influence of salt concentration, pH values and the addition of thiosulfate was examined. The susceptibility to SCC was evaluated by Slow Strain Rate Tests (SSRT, at 1.5 x 10-6 s-1 strain rate. The behavior of 254SMO was compared to those of AISI 316L SS and Hastelloy C276. 254SMO showed an excellent resistance to SCC in all conditions, except in the more acidic solutions (pH <= 1 where, in the sensitized conditions, intergranular stress corrosion cracking occurred.

  5. Development of Eddy Current Test Procedure for Non-destructive Detection of Fatigue Cracks and Corrosion in Rivets of Air-intake Structures

    Directory of Open Access Journals (Sweden)

    B. Sasi

    2009-03-01

    Full Text Available Non-destructive detection of defects in countersunk of rivets in multi-layer air-intake structures is essential for ensuring structural integrity and flight safety. This paper presents an eddy current test procedure developed for reliable detection of simulated fatigue cracks and corrosion products in rivets of air-intake structures. This procedure is capable of reliably detecting 0.25 mm deep defects in 4 mm dia rivets and 0.75 mm deep defects in 5 mm dia rivets. Further, it is not influenced by thickness of the multilayers.Defence Science Journal, 2009, 59(2, pp.106-112, DOI:http://dx.doi.org/10.14429/dsj.59.1497

  6. Corrosion-Fatigue Cracking in Al 7075 Alloys

    Science.gov (United States)

    2014-12-09

    Naval Research Laboratory Washington, DC 20375-5320 NRL/MR/6355--14-9582 Corrosion -Fatigue Cracking in Al 7075 Alloys December 9, 2014 P.S. Pao...PERSON 19b. TELEPHONE NUMBER (include area code) b. ABSTRACT c. THIS PAGE 18. NUMBER OF PAGES 17. LIMITATION OF ABSTRACT Corrosion -Fatigue Cracking in Al...Memorandum Report Corrosion -fatigue Aluminum alloys Environmental effect October 2011 – September 2014 63-2634-A4 Unclassified Unlimited Unclassified

  7. Evaluation of Stress Corrosion Cracking Susceptibility Using Fracture Mechanics Techniques, Part 1. [environmental tests of aluminum alloys, stainless steels, and titanium alloys

    Science.gov (United States)

    Sprowls, D. O.; Shumaker, M. B.; Walsh, J. D.; Coursen, J. W.

    1973-01-01

    Stress corrosion cracking (SSC) tests were performed on 13 aluminum alloys, 13 precipitation hardening stainless steels, and two titanium 6Al-4V alloy forgings to compare fracture mechanics techniques with the conventional smooth specimen procedures. Commercially fabricated plate and rolled or forged bars 2 to 2.5-in. thick were tested. Exposures were conducted outdoors in a seacoast atmosphere and in an inland industrial atmosphere to relate the accelerated tests with service type environments. With the fracture mechanics technique tests were made chiefly on bolt loaded fatigue precracked compact tension specimens of the type used for plane-strain fracture toughness tests. Additional tests of the aluminum alloy were performed on ring loaded compact tension specimens and on bolt loaded double cantilever beams. For the smooth specimen procedure 0.125-in. dia. tensile specimens were loaded axially in constant deformation type frames. For both aluminum and steel alloys comparative SCC growth rates obtained from tests of precracked specimens provide an additional useful characterization of the SCC behavior of an alloy.

  8. Transport and Corrosion Behavior of Cracked Reinforced Concrete

    DEFF Research Database (Denmark)

    Pease, Bradley Justin

    to enter the concrete. This is, among others, important in the corrosion of reinforcing steel. When cracks protrude to the depth of reinforcing steel, liquids containing aggressive ions (i.e. chlorides associated with salts and sea water) may rapidly access and initiate corrosion of the reinforcing...... structures. These models currently lack some of the scientific validity to fully represent actual field structures, i.e. structures containing cracks. Further understanding, therefore is needed on the effect cracks have on transport and corrosion in reinforced concrete. The fundamental mechanisms...... of transport and corrosion in cracked, reinforced concrete are not yet fully understood. The scope of this study therefore is to develop a link between concrete cracks and the relevant transport mechanism(s) under particular environmental conditions. It is envisioned that a finite element model...

  9. Stress corrosion cracking and hydrogen embrittlement of thick section high strength low alloy steel.

    OpenAIRE

    Needham, William Donald

    1986-01-01

    An experimental study was conducted to evaluate the corrosion performance of weldments of a high strength low alloy(HSLA) steel in a simulated seawater environment. This steel, designated HSLA80, was developed by the United States Navy for use in ship structural applications. Stress corrosion CRACKING(SCC) and hydrogen embrittlement(HEM) were investigated by conducting 42 Wedge-Opening load(WOL) tests as a function of stress intensity and corrosion potential and 33 Slow Strain Rate(SSR) tests...

  10. Relationship among Parameters Evaluating Stress Corrosion Cracking

    Institute of Scientific and Technical Information of China (English)

    2000-01-01

    @@The threshold stress, σc, for sulfide stress corrosion cracking (SCC) of seven pipeline steels and five other steels, the critical stress, SC, for seven pipeline steels and two drill rod steels with various strengths and the susceptibility to SCC, IRA or σf(SCC)/σf, for four pipeline steels, two drill rod steels and five other steels were measured. The results showed that there are no definite elationships among σc, SC and IRA or σf(SCC)/σf. The threshold stress for hydrogen induced cracking (HIC) during charging with loading in the H2SO4 solution, σc(H), decreased linearly with logarithm of the concentration of diffusible hydrogen c0, i.e., σC(H)=A-B Inc0 for four pipeline steels. σc(H) obtained with a special cathodic current ic, which was corresponding to the diffusible hydrogen concentration during immersing in the H2S solution, were consistent with σc for sulfide SCC for four pipeline steels.Therefore, σc for sulfide SCC can be measured using dynamically charging in the H2SO4 solution with the special cathodic current ic.

  11. Effect of cold work on the growth rates of stress corrosion cracks in structural materials of nuclear systems

    Energy Technology Data Exchange (ETDEWEB)

    Magdowski, R.; Speidel, M.O. [Swiss Federal Inst. of Tech., Zurich (Switzerland). Inst. of Metallurgy

    1996-10-01

    The growth rates of stress corrosion cracks in austenitic stainless steels and nickel base alloy 600 exposed to simulated boiling water reactor coolant were measured by fracture mechanics testing techniques. Cold work may increase the crack growth rates up to one hundred times. In both, the annealed condition and the cold worked condition, the stress corrosion crack growth rates are independent of stress intensity over a wide K-range and crack growth rates correlate well with yield strength and hardness. In the annealed condition the fracture path is intergranular, but higher degrees of cold work introduce higher proportions of transgranular stress corrosion cracking.

  12. Corrosion-Induced Concrete Cracking Model Considering Corrosion-Filled Paste

    OpenAIRE

    Dong, Jianfeng; Zhao, Yuxi; Wu, Yingyao; Jin, Weiliang

    2016-01-01

    A TCP–TCL model is established to describe the relationship between the thickness of the corrosion-filled paste (CP) and that of the corrosion layer (CL). This model can describe the phenomenon that the corrosion filling in the concrete pores and accumulating at the steel/concrete interface occur synchronously. Based on the TCP–TCL model, a corrosion-induced concrete cracking model, which can quantitatively consider corrosion-filled paste at concrete/steel interface, is proposed. Combined wit...

  13. Three-dimensional characterization of stress corrosion cracks

    DEFF Research Database (Denmark)

    Lozano-Perez, S.; Rodrigo, P.; Gontard, Lionel Cervera

    2011-01-01

    Understanding crack propagation and initiation is fundamental if stress corrosion cracking (SCC) mechanisms are to be understood. However, cracking is a three-dimensional (3D) phenomenon and most characterization techniques are restricted to two-dimensional (2D) observations. In order to overcome...... the best spatial resolution. To illustrate the power of these techniques, different parts of dominant stress corrosion cracks in Ni-alloys and stainless steels have been reconstructed in 3D. All relevant microstructural features can now be studied in detail and its relative orientation respect...

  14. Influence of oxide films on primary water stress corrosion cracking initiation of alloy 600

    Science.gov (United States)

    Panter, J.; Viguier, B.; Cloué, J.-M.; Foucault, M.; Combrade, P.; Andrieu, E.

    2006-01-01

    In the present study alloy 600 was tested in simulated pressurised water reactor (PWR) primary water, at 360 °C, under an hydrogen partial pressure of 30 kPa. These testing conditions correspond to the maximum sensitivity of alloy 600 to crack initiation. The resulting oxidised structures (corrosion scale and underlying metal) were characterised. A chromium rich oxide layer was revealed, the underlying metal being chromium depleted. In addition, analysis of the chemical composition of the metal close to the oxide scale had allowed to detect oxygen under the oxide scale and particularly in a triple grain boundary. Implication of such a finding on the crack initiation of alloy 600 is discussed. Significant diminution of the crack initiation time was observed for sample oxidised before stress corrosion tests. In view of these results, a mechanism for stress corrosion crack initiation of alloy 600 in PWR primary water was proposed.

  15. Microbial Corrosion and Cracking in Steel

    DEFF Research Database (Denmark)

    Hilbert, Lisbeth Rischel

    1998-01-01

    and corrosion products (ferrous sulphides) on the metal surface. Experiments have been conducted on carbon steel exposed in near neutral (pH 6 to 8.5) saline hydrogen sulphide environment (0 to 100 mg/l total dissolved sulphide) for a period of 14 days. Furthermore coupons have been exposed in a bioreactor...... for a period of up to 120 days in sulphide-producing environment controlled by biological activity of (SRB).Electrochemical studies have been conducted in order to characterise the electrochemical response of the biofilm / ferrous sulphide / metal interface and clarify whether the tested electrochemical...... and not electrochemically active film. The polarisation resistance increases with the film resistance and an small underestimation of corrosion rate is possible, if film resistance is large.· An electrochemically reactive film (ferrous sulphides) results in current contributions that will be added to the metal dissolution...

  16. EFFECTS OF CHEMISTRY AND OTHER VARIABLES ON CORROSION AND STRESS CORROSION CRACKING IN HANFORD DOUBLE SHELL TANKS

    Energy Technology Data Exchange (ETDEWEB)

    BROWN MH

    2008-11-13

    Laboratory testing was performed to develop a comprehensive understanding of the corrosivity of the tank wastes stored in Double-Shell Tanks using simulants primarily from Tanks 241-AP-105, 241-SY-103 and 241-AW-105. Additional tests were conducted using simulants of the waste stored in 241-AZ-102, 241-SY-101, 241-AN-107, and 241-AY-101. This test program placed particular emphasis on defining the range of tank waste chemistries that do not induce the onset of localized forms of corrosion, particularly pitting and stress corrosion cracking. This document summarizes the key findings of the research program.

  17. Stress corrosion cracking resistance of aluminum alloy 7000 series after two-step aging

    Directory of Open Access Journals (Sweden)

    Jegdić Bore V.

    2015-01-01

    Full Text Available The effect of one step-and a new (short two-step aging on the resistance to stress corrosion cracking of an aluminum alloy 7000 series was investigated, using slow strain rate test and fracture mechanics method. Aging level in the tested alloy was evaluated by means of scanning electron microscopy and measurements of electrical resistivity. It was shown that the alloy after the new two-step aging is significantly more resistant to stress corrosion cracking. Values of tensile properties and fracture toughness are similar for both thermal states. Processes that take place at the crack tip have been considered. The effect of the testing solution temperature on the crack growth rate on the plateau was determined. Two values of the apparent activation energy were obtained. These values correspond to different processes that control crack growth rate on the plateau at higher and lower temperatures. [Projekat Ministarstva nauke Republike Srbije, br. TR 34028 i br. TR 34016

  18. Analytical Solutions for Corrosion-Induced Cohesive Concrete Cracking

    Directory of Open Access Journals (Sweden)

    Hua-Peng Chen

    2012-01-01

    Full Text Available The paper presents a new analytical model to study the evolution of radial cracking around a corroding steel reinforcement bar embedded in concrete. The concrete cover for the corroding rebar is modelled as a thick-walled cylinder subject to axisymmetrical displacement constraint at the internal boundary generated by expansive corrosion products. A bilinear softening curve reflecting realistic concrete property, together with the crack band theory for concrete fracture, is applied to model the residual tensile stress in the cracked concrete. A governing equation for directly solving the crack width in cover concrete is established for the proposed analytical model. Closed-form solutions for crack width are then obtained at various stages during the evolution of cracking in cover concrete. The propagation of crack front with corrosion progress is studied, and the time to cracking on concrete cover surface is predicted. Mechanical parameters of the model including residual tensile strength, reduced tensile stiffness, and radial pressure at the bond interface are investigated during the evolution of cover concrete cracking. Finally, the analytical predictions are examined by comparing with the published experimental data, and mechanical parameters are analysed with the progress of reinforcement corrosion and through the concrete cover.

  19. Relativity between corrosion-induced stress and stress corrosion cracking of brass in an ammonia solution

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    The susceptibility to stress corrosion cracking (SCC) of brass in an ammonia solution with various pH values or under various applied potentials was measured at slow strain rate tests. The additive stress in the same solution was measured using two methods. The results indicate that the variation of the susceptibility to SCC with pH value or with potential is in an excellent agreement with the corrosion (passive film or dezincification layer)-induced stress. When pH ? 7, the corrosion-induced tensile stress and the susceptibility to SCC have maximum values and hardly change with increasing the pH value. However, when pH < 7, both the corrosion-induced tensile stress and the susceptibility to SCC reduce rapidly with decreasing the pH value. Both the corrosion-induced tensile stress and the susceptibility to SCC have maximum values at the open-circuit potential, decrease slightly under the anodic polarization, and reduce gradually to zero under the cathodic polarization.

  20. Corrosion and stress corrosion cracking of ferritic/martensitic steel in super critical pressurized water

    Energy Technology Data Exchange (ETDEWEB)

    Hirose, T. [Naka Fusion Research Institute, JAEA, 801-1 Mukouyama, Naka, Ibaraki 311-0193 (Japan)]. E-mail: hirose.takanori@jaea.go.jp; Shiba, K. [Naka Fusion Research Institute, JAEA, 801-1 Mukouyama, Naka, Ibaraki 311-0193 (Japan); Enoeda, M. [Naka Fusion Research Institute, JAEA, 801-1 Mukouyama, Naka, Ibaraki 311-0193 (Japan); Akiba, M. [Naka Fusion Research Institute, JAEA, 801-1 Mukouyama, Naka, Ibaraki 311-0193 (Japan)

    2007-08-01

    A water-cooled solid breeder (WCSB) blanket cooled by high temperature SCPW (super critical pressurized water) is a practical option of DEMO reactor. Therefore, it is necessary to check the compatibility of the steel with SCPW. In this work, reduced activation ferritic/martensitic steel, F82H has been tested through slow strain rate tests (SSRT) in 23.5 MPa SCPW. And weight change behavior was measured up to 1000 h. F82H did not demonstrated stress corrosion cracking and its weight simply increased with surface oxidation. The weight change of F82H was almost same as commercial 9%-Cr steels. According to a cross-sectional analysis and weight change behavior, corrosion rate of F82H in the 823 K SCPW is estimated to be 0.04 mm/yr.

  1. Effect of dissolved oxygen content on stress corrosion cracking of a cold worked 316L stainless steel in simulated pressurized water reactor primary water environment

    Science.gov (United States)

    Zhang, Litao; Wang, Jianqiu

    2014-03-01

    Stress corrosion crack growth tests of a cold worked nuclear grade 316L stainless steel were conducted in simulated pressurized water reactor (PWR) primary water environment containing various dissolved oxygen (DO) contents but no dissolved hydrogen. The crack growth rate (CGR) increased with increasing DO content in the simulated PWR primary water. The fracture surface exhibited typical intergranular stress corrosion cracking (IGSCC) characteristics.

  2. Corrosion testing using isotopes

    Science.gov (United States)

    Hohorst, Frederick A.

    1995-12-05

    A method for determining the corrosion behavior of a material with respect to a medium in contact with the material by: implanting a substantially chemically inert gas in a matrix so that corrosion experienced by the material causes the inert gas to enter the medium; placing the medium in contact with the material; and measuring the amount of inert gas which enters the medium. A test sample of a material whose resistance to corrosion by a medium is to be tested, composed of: a body of the material, which body has a surface to be contacted by the medium; and a substantially chemically inert gas implanted into the body to a depth below the surface. A test sample of a material whose resistance to corrosion by a medium is to be tested, composed of: a substrate of material which is easily corroded by the medium, the substrate having a surface; a substantially chemically inert gas implanted into the substrate; and a sheet of the material whose resistance to corrosion is to be tested, the sheet being disposed against the surface of the substrate and having a defined thickness.

  3. Concrete cover cracking due to uniform reinforcement corrosion

    DEFF Research Database (Denmark)

    Solgaard, Anders Ole Stubbe; Michel, Alexander; Geiker, Mette Rica;

    2013-01-01

    is calculated using literature data on corrosion rate and Faraday’s law. The parameters varied comprise reinforcement diameter, concrete cover thickness and concrete material properties, viz. concrete tensile strength and ductility (plain concrete and fibre reinforced concrete). Results obtained from......Service life design (SLD) is an important tool for civil engineers to ensure that the structural integrity and functionality of the structure is not compromised within a given time frame, i.e. the service life. In SLD of reinforced concrete structures, reinforcement corrosion is of major concern...... and reinforcement de-passivation is a frequently used limit state. The present paper investigates an alternative limit state: corrosion-induced cover cracking. Results from numerical simulations of concrete cover cracking due to reinforcement corrosion are presented. The potential additional service life...

  4. Three-dimensional characterization of stress corrosion cracks

    Energy Technology Data Exchange (ETDEWEB)

    Lozano-Perez, S., E-mail: sergio.lozano-perez@materials.ox.ac.u [University of Oxford, Department of Materials, Parks Road, Oxford OX1 3PH (United Kingdom); Rodrigo, P. [Universidad Rey Juan Carlos, Dpto. de Ciencia e Ingenieria de Materiales, c/ Tulipan s.n., 28933 Mostoles (Madrid) (Spain); Gontard, Lionel C. [Danish Technical University, Center for Electron Nanoscopy, Matematiktorvet Building 307, Room 115, 2800 Kogens Lyngby (Denmark)

    2011-01-31

    Understanding crack propagation and initiation is fundamental if stress corrosion cracking (SCC) mechanisms are to be understood. However, cracking is a three-dimensional (3D) phenomenon and most characterization techniques are restricted to two-dimensional (2D) observations. In order to overcome this problem, different approaches to extract 3D information have been used in the recent years. In this work we will present the benefits of using 3D focused ion beam (FIB) slicing and electron tomography. 3D FIB slicing offers a fast and high throughput characterization while electron tomography offers the best spatial resolution. To illustrate the power of these techniques, different parts of dominant stress corrosion cracks in Ni-alloys and stainless steels have been reconstructed in 3D. All relevant microstructural features can now be studied in detail and its relative orientation respect to the strain direction and grain boundary plane accurately measured.

  5. Stress Corrosion Cracking and Fatigue Crack Growth Studies Pertinent to Spacecraft and Booster Pressure Vessels

    Science.gov (United States)

    Hall, L. R.; Finger, R. W.

    1972-01-01

    This experimental program was divided into two parts. The first part evaluated stress corrosion cracking in 2219-T87 aluminum and 5Al-2.5Sn (ELI) titanium alloy plate and weld metal. Both uniform height double cantilever beam and surface flawed specimens were tested in environments normally encountered during the fabrication and operation of pressure vessels in spacecraft and booster systems. The second part studied compatibility of material-environment combinations suitable for high energy upper stage propulsion systems. Surface flawed specimens having thicknesses representative of minimum gage fuel and oxidizer tanks were tested. Titanium alloys 5Al-2.5Sn (ELI), 6Al-4V annealed, and 6Al-4V STA were tested in both liquid and gaseous methane. Aluminum alloy 2219 in the T87 and T6E46 condition was tested in fluorine, a fluorine-oxygen mixture, and methane. Results were evaluated using modified linear elastic fracture mechanics parameters.

  6. Accelerated corrosion testing results for specimens containing uncoated reinforcing steel and corrosion inhibitors

    Energy Technology Data Exchange (ETDEWEB)

    Kondratova, I. L.; Montes, P.; Bremner, T. W. [New Brunswick Univ., Dept, of Civil Engineering, Fredericton, NB (Canada)

    2000-07-01

    Concrete mixtures (water-cement ratios of 0.25, 0.40. or 0.60) containing uncoated reinforcing bars with a simulated crack, formed transverse to the axis of the bar, and with three commercial corrosion inhibitors added for corrosion protection (organic corrosion inhibitor,calcium nitrate-based corrosion inhibitor, and migratory corrosion inhibitor), were tested for corrosion damage. The objective was to evaluate the effectiveness of the different corrosion inhibitors in uncracked and cracked concrete slabs in a simulated marine environment. The specimens were placed in an accelerated exposure cabinet with four cycles of wetting and drying per day in simulated seawater, and corrosion rates measured using the linear polarization technique. Water-soluble chloride content in the rebars was analyzed at the end of the exposure period. The three corrosion inhibitors were found to show a wide variation in performance. There was a direct correlation between their effectiveness and addition rate. All three appeared to be more effective in reducing corrosion rate in a higher water-to-cement ratio concrete. Consistent performance was provided only by calcium nitrate at an addition rate of 25 litre/cu m of concrete, with water-to-cement ratios of 0.60 and 0.40. Pitting corrosion was observed in all pre-cracked high performance concrete specimens; the depth of the pit tended to be deeper when a corrosion inhibitor was used. 6 refs., 6 tabs., 6 figs.

  7. Behavior of Stress Corrosion Cracking in a Magnesium Alloy

    Institute of Scientific and Technical Information of China (English)

    SONG Renguo; YANG Fanger; BLAWERT Carsten; DIETZEL Wolfgang

    2009-01-01

    Slow strain rate testing (SSRT) was employed to study the stress corrosion cracking (SCC) behavior of ZE41 magnesium alloy in 0.01 M NaCl solution. Smooth tensile specimens with different thicknesses were strained dynamically in both longitudinal and transverse direction under permanent immersions at a strain rate of 10-6 s-1. It is found that ZE41 magnesium alloy is susceptible to SCC in 0.01 M NaCl solution. The SCC susceptibility of the thinner specimen is lower than that of the thicker specimen. Also, the longitudinal specimens are slightly more susceptible to SCC than the transverse specimens. The SCC mechanism of magnesium alloy is attributed to the combination of anodic dissolution with hydrogen embrittlement.

  8. Characterizing the effect of creep on stress corrosion cracking of cold worked Alloy 690 in supercritical water environment

    Science.gov (United States)

    Zhang, Lefu; Chen, Kai; Du, Donghai; Gao, Wenhua; Andresen, Peter L.; Guo, Xianglong

    2017-08-01

    The effect of creep on stress corrosion cracking (SCC) was studied by measuring crack growth rates (CGRs) of 30% cold worked (CW) Alloy 690 in supercritical water (SCW) and inert gas environments at temperatures ranging from 450 °C to 550 °C. The SCC crack growth rate under SCW environments can be regarded as the cracking induced by the combined effect of corrosion and creep, while the CGR in inert gas environment can be taken as the portion of creep induced cracking. Results showed that the CW Alloy 690 sustained high susceptibility to intergranular (IG) cracking, and creep played a dominant role in the SCC crack growth behavior, contributing more than 80% of the total crack growth rate at each testing temperature. The temperature dependence of creep induced CGRs follows an Arrhenius dependency, with an apparent activation energy (QE) of about 225 kJ/mol.

  9. Study of the Effect of Swelling on Irradiation Assisted Stress Corrosion Cracking

    Energy Technology Data Exchange (ETDEWEB)

    Teysseyre, Sebastien Paul [Idaho National Lab. (INL), Idaho Falls, ID (United States)

    2016-09-01

    This report describes the methodology used to study the effect of swelling on the crack growth rate of an irradiation-assisted stress corrosion crack that is propagating in highly irradiated stainless steel 304 material irradiated to 33 dpa in the Experimental Breeder Reactor-II. The material selection, specimens design, experimental apparatus and processes are described. The results of the current test are presented.

  10. De-alloying and stress-corrosion cracking. Final report

    Energy Technology Data Exchange (ETDEWEB)

    Sieradzki, K.

    1998-09-01

    This research program has had two major areas of focus that are related: (1) alloy corrosion and (2) the role of selective dissolution in the stress corrosion cracking of alloy systems. These interrelated issues were examined using model systems such as Ag-Au and Cu-Au by conventional electrochemical techniques, in situ scanning tunneling microscopy (STM), in situ small angle neutron scattering (SANS), ultrahigh speed digital photography of fracture events, and computer simulations. The STM and SANS work were specifically aimed at addressing a roughening transition known to occur in alloy systems undergoing corrosion at electrochemical potentials greater than the so-called critical potential. Analytical models of de-alloying processes including the roughening transition were developed that specifically include curvature effects that are important in alloy corrosion processes. Stress-corrosion experiments were performed on the same model systems using rapid optical and electrochemical techniques on 50 {micro}m--250 {micro}m thick sheets and small diameter wires. The primary goal of this work was to develop a fundamental understanding of the corrosion and electrochemistry of alloys and the stress-corrosion cracking processes these alloys undergo. Computer simulations and analytical work identified surface stress and an important parameter in environmentally assisted fracture. The major results of the research on this program since the summer of 1993 are briefly summarized.

  11. Chemical milling solution reveals stress corrosion cracks in titanium alloy

    Science.gov (United States)

    Braski, D. N.

    1967-01-01

    Solution of hydrogen flouride, hydrogen peroxide, and water reveals hot salt stress corrosion cracks in various titanium alloys. After the surface is rinsed in water, dried, and swabbed with the solution, it can be observed by the naked eye or at low magnification.

  12. Smeared crack modelling approach for corrosion-induced concrete damage

    DEFF Research Database (Denmark)

    Thybo, Anna Emilie Anusha; Michel, Alexander; Stang, Henrik

    2017-01-01

    compared to experimental data obtained by digital image correlation and published in the literature. Excellent agreements between experimentally observed and numerically predicted crack patterns at the micro and macro scale indicate the capability of the modelling approach to accurately capture corrosion...

  13. An improved stress corrosion test medium for aluminum alloys

    Science.gov (United States)

    Humphries, T. S.; Coston, J. E.

    1981-01-01

    A laboratory test method that is only mildly corrosive to aluminum and discriminating for use in classifying the stress corrosion cracking resistance of aluminum alloys is presented along with the method used in evaluating the media selected for testing. The proposed medium is easier to prepare and less expensive than substitute ocean water.

  14. Effect of hydrogen on stress corrosion cracking of copper

    Institute of Scientific and Technical Information of China (English)

    Li-jie QIAO

    2008-01-01

    The effects of hydrogen on electrochemical behavior and susceptibility of stress corrosion cracking (SCC) of pure copper were studied. SCC susceptibility of pure copper in a 1 M NaNO2 solution was increased by pre-charged hydrogen. The effect of hydrogen on the sus-ceptibility is more obvious in the low stress region due to the longer fracture time, which resulted in a longer time for more hydrogen to diffuse toward the crack tip. Synergistic effects of hydrogen and stress on corrosion and SCC pro-cesses were discussed. The results showed that an inter-action between stress and hydrogen at the crack tip could increase the anodic dissolution rate remarkably.

  15. Microbial Corrosion and Cracking in Steel

    DEFF Research Database (Denmark)

    Hilbert, Lisbeth Rischel

    1998-01-01

    and for recommendations in regards to electrochemical monitoring of MIC. The work presented here and further studies are also planned to lead to a Ph.D. thesis on "MIC monitoring based on mechanisms of corrosion".The results of laboratory experiments conducted in the period 1995 to 1997 are summarised. Conclusions...... will be based on results from the entire 3 year period, but only selected experimental data primarily from the latest experiments will be presented in detail here.Microbial corrosion of carbon steel under influence of sulphate-reducing bacteria (SRB) is characterised by the formation of both biofilm...... and corrosion products (ferrous sulphides) on the metal surface. Experiments have been conducted on carbon steel exposed in near neutral (pH 6 to 8.5) saline hydrogen sulphide environment (0 to 100 mg/l total dissolved sulphide) for a period of 14 days. Furthermore coupons have been exposed in a bioreactor...

  16. Inhibiting Corrosion Cracking: Crack Tip Chemistry and Physics.

    Science.gov (United States)

    1986-03-14

    5 5. Swuzary 113 Rferences 114 wl NO 4L iv . List of Figuring 1. Microipette pulling machine . 29 2. Anodic polarization of 7075-T6 Al alloy in dilute...environment has a strong effect on microplastic behavior at the tip of a fatigue crack. Stolz and Pelloux suggest that nitrate ion competes with chloride...Crystalline Na2 N 20 29H20 precipitates when the filtrate is placed in a vacunm desiccator over sulfuric acid. The filtered precipitate is washed

  17. Irradiation-Assisted Stress Corrosion Cracking of Austenitic Stainless Steels in BWR Environments

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Y. [Argonne National Lab. (ANL), Argonne, IL (United States); Chopra, O. K. [Argonne National Lab. (ANL), Argonne, IL (United States); Gruber, Eugene E. [Argonne National Lab. (ANL), Argonne, IL (United States); Shack, William J. [Argonne National Lab. (ANL), Argonne, IL (United States)

    2010-06-01

    The internal components of light water reactors are exposed to high-energy neutron irradiation and high-temperature reactor coolant. The exposure to neutron irradiation increases the susceptibility of austenitic stainless steels (SSs) to stress corrosion cracking (SCC) because of the elevated corrosion potential of the reactor coolant and the introduction of new embrittlement mechanisms through radiation damage. Various nonsensitized SSs and nickel alloys have been found to be prone to intergranular cracking after extended neutron exposure. Such cracks have been seen in a number of internal components in boiling water reactors (BWRs). The elevated susceptibility to SCC in irradiated materials, commonly referred to as irradiation-assisted stress corrosion cracking (IASCC), is a complex phenomenon that involves simultaneous actions of irradiation, stress, and corrosion. In recent years, as nuclear power plants have aged and irradiation dose increased, IASCC has become an increasingly important issue. Post-irradiation crack growth rate and fracture toughness tests have been performed to provide data and technical support for the NRC to address various issues related to aging degradation of reactor-core internal structures and components. This report summarizes the results of the last group of tests on compact tension specimens from the Halden-II irradiation. The IASCC susceptibility of austenitic SSs and heat-affected-zone (HAZ) materials sectioned from submerged arc and shielded metal arc welds was evaluated by conducting crack growth rate and fracture toughness tests in a simulated BWR environment. The fracture and cracking behavior of HAZ materials, thermally sensitized SSs and grain-boundary engineered SSs was investigated at several doses (≤3 dpa). These latest results were combined with previous results from Halden-I and II irradiations to analyze the effects of neutron dose, water chemistry, alloy compositions, and welding and processing conditions on IASCC

  18. Detection of corrosion processes and fatigue cracks by means of acoustic emission monitoring

    Energy Technology Data Exchange (ETDEWEB)

    Jagenbrein, Andreas; Tscheliesnig, Peter [TUEV Austria Services GmbH, Vienna (Austria); Wachsmuth, Janne; Bohse, Juergen [Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin (Germany)

    2012-07-01

    Fatigue crack growth and active corrosion processes are the main causes for structural failures of transport products like road tankers, railway tank cars, and ships. Within the 7{sup th} EC framework programme the aim of project CORFAT is to develop a new monitoring technology based on acoustic emission testing (AT) of the structural integrity in terms of proceeding degradation. Differentiation of acoustic emission (AE) signals of real degradation processes by fatigue crack growth or active corrosion from operational or environmental background noise requires the signal classification using also pattern recognition. Therefore, a data base of AE signals related to the different source mechanisms was built up experimentally. In this article selected results of corrosion and fatigue tests in the laboratory as well as results of monitoring background noise during moving of a road tanker are described. (orig.)

  19. Stress corrosion cracking in low-pressure turbine discs in an NaCl solution

    Energy Technology Data Exchange (ETDEWEB)

    Hitomi, Itoh [Mitsubishi Heavy Industries, Ltd., Takasago Research and Development Center (Japan); Takashi, Momoo [Mitsubishi Heavy Industries, Ltd., Takasago Machinery Works (Japan)

    2001-07-01

    From past research, it is known that stress corrosion cracking in low-pressure turbine discs occurs in an environment near that of deaerated pure water. Nevertheless, in units with molar ratio control, there is a possibility of NaCl concentrating as an impurity in the dry/wet boundary region. Long-term immersion tests were conducted at 373 K to 473 K with the NaCl concentration predicted to become 5%. It was found that, when FeCl{sub 3} or other oxidizer was added, corrosion increased remarkably and SCC was initiated. When cracks were initiated, they were primarily transgranular; as the test temperature was decreased, initiation was accelerated but conversely crack propagation was reduced. (author)

  20. Stress corrosion cracking of titanium alloys

    Science.gov (United States)

    Statler, G. R.; Spretnak, J. W.; Beck, F. H.; Fontana, M. G.

    1974-01-01

    The effect of hydrogen on the properties of metals, including titanium and its alloys, was investigated. The basic theories of stress corrosion of titanium alloys are reviewed along with the literature concerned with the effect of absorbed hydrogen on the mechanical properties of metals. Finally, the basic modes of metal fracture and their importance to this study is considered. The experimental work was designed to determine the effects of hydrogen concentration on the critical strain at which plastic instability along pure shear directions occurs. The materials used were titanium alloys Ti-8Al-lMo-lV and Ti-5Al-2.5Sn.

  1. Application of new experimental methods to pipeline stress corrosion cracking. Annual report, March 1992-February 1993

    Energy Technology Data Exchange (ETDEWEB)

    Schmidt, C.G.; Kobayashi, T.; Becker, C.H.; Pound, B.G.; Simons, J.W.

    1993-04-01

    The objective of the investigation is to develop a physically based understanding of the mechanisms of stress corrosion cracking (SCC) in pipeline steels by applying advanced fracture surface and electrochemical characterization techniques to samples taken from fielded pipeline. The investigations found that the effect of pressure fluctuations on the propagation of stress corrosion cracks was readily evident from an analysis of the topographies of conjugate fracture surfaces. Substantial crack blunting was produced under normal pipeline operating conditions. Corrosion deposits were removed from the fracture surfaces of a stress corrosion crack in a pipeline specimen recovered from service. The topography of the underlying metal surface appears to be preserved with little corrosion damage after crack formation. This allowed the cracking process to be reconstructed from the surface topography. In some cases, deposits on the fracture surfaces of stress corrosion cracks contain significant concentrations of metallic elements that are not found in pipeline steels but are likely to be commonplace in the surrounding environment.

  2. Stress Corrosion Cracking Behavior of X80 Pipeline Steel in Acid Soil Environment with SRB

    Science.gov (United States)

    Wang, Dan; Xie, Fei; Wu, Ming; Liu, Guangxin; Zong, Yue; Li, Xue

    2017-06-01

    Self-designed experimental device was adopted to ensure the normal growth of sulphate-reducing bacteria (SRB) in sterile simulated Yingtan soil solution. Stress corrosion cracking (SCC) behavior of X80 pipeline steel in simulated acid soil environment was investigated by electrochemical impedance spectroscopy, slow strain rate test, and scanning electron microscope. Results show that the presence of SRB could promote stress corrosion cracking susceptibility. In a growth cycle, polarization resistance first presents a decrease and subsequently an increase, which is inversely proportional to the quantities of SRB. At 8 days of growth, SRB reach their largest quantity of 1.42 × 103 cells/g. The corrosion behavior is most serious at this time point, and the SCC mechanism is hydrogen embrittlement. In other SRB growth stages, the SCC mechanism of X80 steel is anodic dissolution. With the increasing SRB quantities, X80 steel is largely prone to SCC behavior, and the effect of hydrogen is considerably obvious.

  3. Stress corrosion cracking of brass in ammonia solution

    Institute of Scientific and Technical Information of China (English)

    2001-01-01

    Brass foil with a protective layer formed on one side was deflected during corrosion in an ammonia solution under various applied potentials, and then corrosion-induced stress generated at brass/dezincification layer under different potentials could be measured. At the same time, susceptibility to stress corrosion cracking(SCC) of brass in the ammonia solution under various applied potentials was measured using a single-edge notched specimen. At open-circuit potential, both corrosion-induced tensile stress and susceptibility to SCC(Iσ) had a maximum value. Both tensile stress σp and susceptibility Iσ decreased slightly under anodic polarization, but reduced steeply with the decrease in potential of cathodic polarization. At the cathodic potential of -500  mV(vs SCE), corrosion-induced stress became compressive because of copper-plating layer, correspondingly, susceptibility to SCC was zero. Therefore, the variation of SCC susceptibility with potential is consistent with that of the corrosion-induced additive stress.

  4. OPGW Corrosion Detection Using Nondestructive Test Method

    Energy Technology Data Exchange (ETDEWEB)

    Jeong, J.K.; Yoon, G.G.; Kang, J.W.; Yang, H.W. [Hanyang University, Seoul (Korea, Republic of)

    1998-02-01

    This paper deals with some characteristics of a nondestructive eddy current detector to measure OPGW(composite overhead ground wire with optical fiber) corrosion. This detector is designed to automatically run on OPGW and to continuously inspect the corrosion of the line. The impedance of the eddy coil changing by any corrosion phenomenon of OPGW is analyzed. Several performances of the detector are described and experimental procedures and test results are also given. As a result, it is shown that the implemented detector can be measured some quantitative data for crack, broken wires or severe deteriorations in OPGW. This nondestructive test method would be applied to improve the reliability and efficiency of transmission lines in service. (author). 5 refs., 9 figs., 2 tabs.

  5. Stress Corrosion Cracking of Zircaloy-4 in Halide Solutions: Effect of Temperature

    Directory of Open Access Journals (Sweden)

    Farina S.B.

    2002-01-01

    Full Text Available Zircaloy-4 was found to be susceptible to stress corrosion cracking in 1 M NaCl, 1 M KBr and 1 M KI aqueous solutions at potentials above the pitting potential. In all the solutions tested crack propagation was initially intergranular and then changed to transgranular. The effect of strain rate and temperature on the SCC propagation was investigated. An increase in the strain rate was found to lead to an increase in the crack propagation rate. The crack propagation rate increases in the three solutions tested as the temperatures increases between 20 and 90 °C. The Surface-Mobility SCC mechanism accounts for the observation made in the present work, and the activation energy predicted in iodide solutions is similar to that found in the literature.

  6. Laboratory evaluation of soil stress corrosion cracking and hydrogen embrittlement of API grade steels

    Energy Technology Data Exchange (ETDEWEB)

    Bueno, A.H.S.; Castro, B.B.; Ponciano, J.A.C. [Federal Univ. of Rio de Janeiro (Brazil). COPPE

    2004-07-01

    Stress corrosion cracking (SCC) in carbon steels is a form of deterioration that can occur during the service life of a pipeline that is exposed to mechanical stress and strains. A study was conducted to investigate SCC and hydrogen embrittlement (HE) of API grade steels in contact with soil. The physical, chemical and bacteriological characteristics of different soil samples were determined. Slow strain rate tests were performed using electrolytes obtained in the soil samples taken from different points near buried pipelines. Stress versus strain curves were obtained at different electrode potentials for API X46, X60 and X80 steels. The results showed the conjoint incidence of SCC and HE, depending on the potential imposed. It was revealed that HE contributes to the initiation of cracking and crack propagation. Cracking morphology was similar to the SCC found in field situations where transgranular cracking was detected in a pipeline that had collapsed as a result of land creeping. The material exhibited signs of secondary cracking and lower ductility, even under cathodic potentials. It was noted that the methodology used in this study was not able to reproduce the possible effect of microbial induced corrosion. 10 refs., 3 tabs., 3 figs.

  7. Hydrogen embrittlement and stress corrosion cracking in metals

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Young Suk; Cheong, Yong Mu; Im, Kyung Soo

    2004-10-15

    The objective of this report is to elucidate the mechanism for hydrogen embrittlement (HE) and stress corrosion cracking (SCC) in metals. To this end, we investigate the common features between delayed hydride cracking (DHC) in zirconium alloys and HE in metals with no precipitation of hydrides including Fe base alloys, Nickel base alloys, Cu alloys and Al alloys. Surprisingly, as with the crack growth pattern for the DHC in zirconium alloy, the metals mentioned above show a discontinuous crack growth, striation lines and a strong dependence of yield strength when exposed to hydrogen internally and externally. This study, for the first time, analyzes the driving force for the HE in metals in viewpoints of Kim's DHC model that a driving force for the DHC in zirconium alloys is a supersaturated hydrogen concentration coming from a hysteresis of the terminal solid solubility of hydrogen, not by the stress gradient, As with the crack growing only along the hydride habit plane during the DHC in zirconium alloys, the metals exposed to hydrogen seem to have the crack growing by invoking the dislocation slip along the preferential planes as a result of some interactions of the dislocations with hydrogen. Therefore, it seems that the hydrogen plays a role in inducing the slip only on the preferential planes so as to cause a strain localization at the crack tip. Sulfur in metals is detrimental in causing a intergranular cracking due to a segregation of the hydrogens at the grain boundaries. In contrast, boron in excess of 500 ppm added to the Ni3Al intermetallic compound is found to be beneficial in suppressing the HE even though further details of the mechanism for the roles of boron and sulfur are required. Carbon, carbides precipitating semi-continuously along the grain boundaries and the CSL (coherent site lattice) boundaries is found to suppress the intergranular stress corrosion cracking (IGSCC) in Alloy 600. The higher the volume fraction of twin boundaries, the

  8. Hydrogen embrittlement and stress corrosion cracking in metals

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Young Suk; Cheong, Yong Mu; Im, Kyung Soo

    2004-10-15

    The objective of this report is to elucidate the mechanism for hydrogen embrittlement (HE) and stress corrosion cracking (SCC) in metals. To this end, we investigate the common features between delayed hydride cracking (DHC) in zirconium alloys and HE in metals with no precipitation of hydrides including Fe base alloys, Nickel base alloys, Cu alloys and Al alloys. Surprisingly, as with the crack growth pattern for the DHC in zirconium alloy, the metals mentioned above show a discontinuous crack growth, striation lines and a strong dependence of yield strength when exposed to hydrogen internally and externally. This study, for the first time, analyzes the driving force for the HE in metals in viewpoints of Kim's DHC model that a driving force for the DHC in zirconium alloys is a supersaturated hydrogen concentration coming from a hysteresis of the terminal solid solubility of hydrogen, not by the stress gradient, As with the crack growing only along the hydride habit plane during the DHC in zirconium alloys, the metals exposed to hydrogen seem to have the crack growing by invoking the dislocation slip along the preferential planes as a result of some interactions of the dislocations with hydrogen. Therefore, it seems that the hydrogen plays a role in inducing the slip only on the preferential planes so as to cause a strain localization at the crack tip. Sulfur in metals is detrimental in causing a intergranular cracking due to a segregation of the hydrogens at the grain boundaries. In contrast, boron in excess of 500 ppm added to the Ni3Al intermetallic compound is found to be beneficial in suppressing the HE even though further details of the mechanism for the roles of boron and sulfur are required. Carbon, carbides precipitating semi-continuously along the grain boundaries and the CSL (coherent site lattice) boundaries is found to suppress the intergranular stress corrosion cracking (IGSCC) in Alloy 600. The higher the volume fraction of twin boundaries, the

  9. Threshold Stress Intensity of Hydrogen-Induced Cracking and Stress Corrosion Cracking of High Strength Steel

    Institute of Scientific and Technical Information of China (English)

    2001-01-01

    The threshold stress intensity of stress corrosion cracking (SCC) for 40CrMo steel in 3.5 % NaCl solution decreased exponentially with the increase of yield strength. The threshold stress intensity of hydrogen-induced cracking during dynamical charging for 40CrMo steel decreased linearly with the logarithm of the concentration of diffusible hydrogen. This equation was also applicable to SCC of high strength steel in aqueous solution. The critical hydrogen enrichment concentration necessary for SCC of high strength steel in water decreased exponentially with the increase of yield strength. Based on the results, the relationship between KISCC and σys could be deduced.

  10. FEM Modelling of the Evolution of Corrosion Cracks in Reinforced Concrete Structures

    DEFF Research Database (Denmark)

    Thoft-Christensen, Palle

    Corrosion cracks are caused by the increasing volume of corrosion products during the corrosion of the reinforcement. After corrosion initiation the rust products from the corroded reinforcement will initially fill the porous zone near the reinforcement and the result in an expansion of the concr...

  11. Chloride stress corrosion cracking of Alloy 600 in boric acid solutions

    Energy Technology Data Exchange (ETDEWEB)

    Berge, Ph. [Electricite de France, 92 - Paris la Defense (France); Noel, D.; Gras, J.M.; Prieux, B. [Electricite de France, 77 - Moret-sur-Loing (France). Direction des Etudes et Recherches

    1997-10-01

    The high nickel austenitic alloys are generally considered to have good resistance to chloride stress corrosion cracking. In the standard boiling magnesium chloride solution tests, alloys with more than 40% nickel are immune. Nevertheless, more recent data show that cracking can occur in both Alloys 600 and 690 if the solution is acidified. In other low pH media, such as boric acid solution at 100 deg C, transgranular and intergranular cracking are observed in Alloy 600 in the presence of minor concentrations of sodium chloride (2g/I). In concentrated boric acid at higher temperatures (250 and 290 deg C), intergranular cracking also occurs, either when the chloride concentration is high, or at low chloride contents and high oxygen levels. The role of pH and a possible specific action of boric acid are discussed, together with the influence of electrochemical potential. (author) 21 refs.

  12. Stress-corrosion cracking of sensitized stainless steel by sulfur-containing compounds

    Energy Technology Data Exchange (ETDEWEB)

    Isaacs, H.S.; Vyas, B.; Kendig, M.W.

    1981-01-01

    The stress corrosion cracking (SCC) of sensitized Type 304 stainless steel in thiosulfate solutions has been studied using constant extension rate tests. Very low concentrations of about 6.10/sup -7/M Na/sub 2/S/sub 2/O/sub 3/ (0.1ppm) gave cracking. With boric acid added, higher concentrations (1ppm) were required. The SCC was shown to be electrochemically controlled. Below -0.5v/sub SCE/ (-0.75/sub SHE/) no SCC took place; above this potential the rate of SCC increased with potential. An induction period was required before SCC continued above -0.5v if the potential was held at or below this value for extended times. This period was associated with the build up of an aggressive solution of thiosulfate decomposition products within the crack. The cracking process has been considered to be controlled by rupture of a salt layer and not a passivating oxide.

  13. Stress corrosion crack initiation of alloy 600 in PWR primary water

    Energy Technology Data Exchange (ETDEWEB)

    Zhai, Ziqing; Toloczko, Mychailo B.; Olszta, Matthew J.; Bruemmer, Stephen M.

    2017-07-01

    Stress corrosion crack (SCC) initiation of three mill-annealed (MA) alloy 600 heats in simulated pressurized water reactor primary water has been investigated using constant load tests equipped with in-situ direct current potential drop (DCPD) measurement capabilities. SCC initiation times were greatly reduced by a small amount of cold work. Shallow intergranular (IG) attack and/or cracks were found on most high-energy grain boundaries intersecting the surface with only a small fraction evolving into larger cracks and IGSCC growth. Crack depth profiles were measured and related to DCPD-detected initiation response. Processes controlling the SCC initiation in MA alloy 600 are discussed. IN PRESS, CORRECTED PROOF, 05/02/2017 - mfl

  14. In Situ X-ray Microtomography of Stress Corrosion Cracking and Corrosion Fatigue in Aluminum Alloys

    Science.gov (United States)

    Singh, Sudhanshu S.; Stannard, Tyler J.; Xiao, Xianghui; Chawla, Nikhilesh

    2017-08-01

    Structural materials are subjected to combinations of stress and corrosive environments that work synergistically to cause premature failure. Therefore, studies on the combined effect of stress and corrosive environments on material behavior are required. Existing studies have been performed in two dimensions that are inadequate for full comprehension of the three-dimensional (3D) processes related to stress corrosion cracking (SCC) and corrosion-fatigue (CF) behavior. Recently, x-ray synchrotron tomography has evolved as an excellent technique to obtain the microstructure in 3D. Moreover, being nondestructive in nature, x-ray synchrotron tomography is well suited to study the evolution of microstructure with time (4D, or fourth dimension in time). This article presents our recent 4D studies on SCC and CF of Al 7075 alloys using x-ray synchrotron tomography.

  15. A Fracture Probability Competition Mechanism of Stress Corrosion Cracking

    Institute of Scientific and Technical Information of China (English)

    Yanliang HUANG

    2001-01-01

    The stress corrosion cracking (SCC) of austenitic stainless steel was studied via polarization,slow strain rate and scanning electron microscope (SEM) techniques. Many SCC mechanisms have been proposed in which hydrogen embrittlement and passive film rupture-repassivation theories are generally accepted, but they can hardly explain the SCC mechanism of austenitic stainless steel in acidic chloride solution adequately, because the steel is in active dissolution state and cathodic polarization can prevent it from occurring. Our experiment shows that the anodic current increases the creep rate and decreases the plastic strength of the material on single smooth specimen as well as at the SCC crack tip. The fractured surface was characterized as brittle cleavage, while the surface crack of smooth specimen was almost vertical to the tensile strength, which can confirm that the cracks were caused by tensile stresses. A fracture probability competition mechanism of SCC was proposed on the basis of the experimental results combined with the viewpoint of ductile-brittle fracture competition. When the anodic dissolution current is increased to a certain degree, the probability of fracture by tensile stress will exceed that by shear stress, and the brittle fracture will occur. The proposed SCC mechanism can not only explain the propagation of SCC cracks but can explain the crack initiation as well. The strain on the surface distributes unevenly when a smooth specimen is deformed, so does the anodic current distribution. The crack will initiate at a point where the anodic current density is large enough to cause the material at a specific point to fracture in brittle manner.

  16. Stress Corrosion Cracking of an Austenitic Stainless Steel in Nitrite-Containing Chloride Solutions

    Directory of Open Access Journals (Sweden)

    R. K. Singh Raman

    2014-12-01

    Full Text Available This article describes the susceptibility of 316L stainless steel to stress corrosion cracking (SCC in a nitrite-containing chloride solution. Slow strain rate testing (SSRT in 30 wt. % MgCl2 solution established SCC susceptibility, as evidenced by post-SSRT fractography. Addition of nitrite to the chloride solution, which is reported to have inhibitive influence on corrosion of stainless steels, was found to increase SCC susceptibility. The susceptibility was also found to increase with nitrite concentration. This behaviour is explained on the basis of the passivation and pitting characteristics of 316L steel in chloride solution.

  17. Corrosion-Fatigue Cracking in HY-80 and HY-130 Steels

    Science.gov (United States)

    2015-01-22

    on HY80 steel and HY-130 steel are shown in Fig. A-13 through A-16 for various specimens tested at different load ratios and environments. Because...Naval Research Laboratory Washington, DC 20375-5320 NRL/MR/6355--15-9584 Corrosion-Fatigue Cracking in HY-80 and HY-130 Steels January 22, 2015 P.S...Cracking in HY-80 and HY-130 Steels P.S. Pao and R.L. Holtz Naval Research Laboratory 4555 Overlook Avenue, SW Washington, DC 20375-5328 Office of Naval

  18. Inhibition of Ce3+ on Stress Corrosion Crack of High Strength Aluminum Alloy

    Directory of Open Access Journals (Sweden)

    LI Wen-ting

    2017-05-01

    Full Text Available The stress corrosion cracking (SCC susceptibility of 7A04 high strength aluminum alloy in 3.5% (mass fraction NaCl solution and the Ce3+ inhibition of SCC were investigated by slow stress rate test(SSRT, using constant current polarization, electrochemical noise (ECN and electrochemical impedance spectroscopy (EIS techniques. The inhibition mechanism of Ce3+ ions on the initiation and propagation of cracking was also analyzed. The results indicate that both anodic and cathodic galvanostatic polarizations can accelerate the SCC of 7A04, the former increases anodic dissolution but the latter accelerates hydrogen embrittlement of crack tip. SCC susceptibility of 7A04 can be reduced effectively by the addition of cerium ions, the fracture time is delayed and slowed down, but only during the initiation other than the propagation stage of cracking. Ce3+ ions can restrain the initiation of metastable pitting on the surface of 7A04 specimen, which therefore increase the induction time of the cracking since that the micro pits are usually the source of cracking.However, once the crack begins to propagate or the specimen is notched, the addition of cerium ions can rarely inhibit the cracking process. This is possibly attributed to that the radius of Ce3+ ion is too large to diffuse into the crack tip or it is hard to form protective CeO2 layer, Ce3+ ion therefore fails to rehabilitate the active alloy at the crack tip and further reduce the SCC developing rate of 7A04. SEM also indicates that the crack initiation of smooth 7A04 specimens is mainly induced by metastable or stable pits.

  19. Penetration of corrosion products and corrosion-induced cracking in reinforced cementitious materials

    DEFF Research Database (Denmark)

    Michel, Alexander; Pease, Brad J.; Peterova, Adela;

    2014-01-01

    This paper describes experimental investigations on corrosion-induced deterioration in reinforced cementitious materials and the subsequent development and implementation of a novel conceptual model. Rejnforced mortar specimens of varying water-to-cement ratios were subjected to current-induced c......This paper describes experimental investigations on corrosion-induced deterioration in reinforced cementitious materials and the subsequent development and implementation of a novel conceptual model. Rejnforced mortar specimens of varying water-to-cement ratios were subjected to current......-induced corrosion (10, 50, and 100 mu A/cm(2)). X-ray attenuation measurements and visual investigations provided both qualitative and quantitative information on the penetration of solid corrosion products into the surrounding cementitious matrix. X-ray attenuation measurements provided time- and location......-dependent concentrations of corrosion products averaged through the specimen thickness. Digital image correlation (DIC) was used to measure corrosion-induced deformations including deformations between steel and cementitious matrix as well as formation and propagation of corrosion-induced cracks. Based on experimental...

  20. SRNL SHELF LIFE STUDIES - SCC STUDIES AT ROOM TEMPERTURE [stress corrosion cracking

    Energy Technology Data Exchange (ETDEWEB)

    Mickalonis, J.; Duffey, J.

    2014-11-12

    Phase II, Series 2 corrosion testing performed by the Savannah River National Laboratory (SRNL) for the Department of Energy 3013 container has been completed. The corrosion tests are part of an integrated plan conducted jointly by Los Alamos National Laboratory and the Savannah River Site. SRNL was responsible for conducting corrosion studies in small-scale vessels to address the influence of salt composition, water loading, and type of oxide/salt contact on the relative humidity inside a 3013 container and on the resulting corrosion of Type 304L and 316L stainless steel (304L and 316L). This testing was conducted in two phases: Phase I evaluated a broad spectrum of salt compositions and initial water loadings on the salt mixtures exposed to 304L and 316L and the resulting corrosion; Phase II evaluated the corrosion of 304L at specific water loadings and a single salt composition. During Phase I testing at high initial moisture levels (0.35 to 1.24 wt%)a, the roomtemperature corrosion of 304L exposed to a series of plutonium oxide/chloride salt mixtures ranged from superficial staining to pitting and stress corrosion cracking (SCC). 304L teardrop coupons that exhibited SCC were directly exposed to a mixture composed of 98 wt % PuO2, 0.9 wt % NaCl, 0.9 wt % KCl, and 0.2 wt % CaCl2. Cracking was not observed in a 316L teardrop coupon. Pitting was also observed in this environment for both 304L and 316L with depths ranging from 20 to 100 μm. Neither pitting nor SCC was observed in mixtures with a greater chloride salt concentration (5 and 28 wt%). These results demonstrated that for a corrosive solution to form a balance existed between the water loading and the salt chloride concentration. This chloride solution results from the interaction of loaded water with the hydrating CaCl2 salt. In Phase II, Series 1 tests, the SCC results were shown to be reproducible with cracking occurring in as little as 85 days. The approximate 0.5 wt% moisture level was found to

  1. Hierarchical petascale simulation framework for stress corrosion cracking

    Science.gov (United States)

    Vashishta, P.; Kalia, R. K.; Nakano, A.; Kaxiras, E.; Grama, A.; Lu, G.; Eidenbenz, S.; Voter, A. F.; Hood, R. Q.; Moriarty, J. A.; Yang, L. H.

    2008-07-01

    We are developing a scalable parallel and distributed computational framework consisting of methods, algorithms, and integrated software tools for multi-terascle-to-petascale simulations of stress corrosion cracking (SCC) with quantum-level accuracy. We have performed multimillion- to billion-atom molecular dynamics (MD) simulations of deformation, flow, and fracture in amorphous silica with interatomic potentials and forces validated by density functional theory (DFT) calculations. Optimized potentials have been developed to study sulfur embrittlement of nickel with multimillion-to-multibillion atom MD simulations based on DFT and temperature dependent model generalized pseudopotential theory. We have also developed a quasi-continuum method embedded with quantum simulations based on DFT to reach macroscopic length scales and an accelerated molecular dynamics scheme to reach macroscopic time scales in simulations of solid-fluid interfaces that are relevant to SCC. A hybrid MD and mesoscale lattice Boltzmann simulation algorithm is being designed to study fluid flow through cracks.

  2. Near-neutral pH Stress Corrosion Crack Initiation under Simulated Coating Disbondment

    Science.gov (United States)

    Eslami, Abdoulmajid

    This research is aimed at understanding near-neutral pH SCC initiation under disbonded coatings of pipeline steels, and the effect of different environmental and operational factors on crack initiation. Understanding near-neutral pH stress corrosion cracking (SCC) could answer many of the primary questions on crack initiation of SCC which have not yet been answered. It could also assist the development of effective mitigative measures dealing with thousands of kilometer of pipelines containing this form of cracking, in addition to preventive action for future pipeline installations. Near-neutral pH SCC usually occurs under polyethylene tape (PE tape) coated pipelines, at locations where the coating becomes disbonded and/or damaged. Ground water can then penetrate under the damaged/disbonded coating, become trapped and form a suitable environment for corrosion and cracking. Despite extensive studies on this topic the details of crack initiation mechanisms in addition to the exact role of environmental and operational factors on crack initiation are not thoroughly understood. Most previous laboratory tests have been done in aggressive loading conditions and ignored the effect of coatings and cathodic protections (CP). In order to simulate the conditions responsible for crack initiation, a novel testing setup capable of simulating the synergistic effects of coating disbondment, cathodic protection and cyclic loading was implemented. Using this setup and long term laboratory tests near-neutral pH SCC initiation mechanisms and the effect of some environmental and operational factors on crack initiation were investigated. It was found that near-neutral pH SCC initiation does not necessarily occur in near-neutral pH environments as commonly believed. Depending on the level of CP and CO2 in the underground environment, different localized environments with varying pH values from near-neutral to high values above 10 can form under the disbonded coatings. This significantly

  3. Stress Corrosion Cracking Behavior of Alloy 22 in Multi-Ionic Aqueous Environments

    Energy Technology Data Exchange (ETDEWEB)

    K.J. King; J.C. Estill; R.B. Rebak

    2002-07-15

    The US Department of Energy is characterizing a potential repository site for nuclear waste in Yucca Mountain (NV). In its current design, the nuclear waste containers consist of a double metallic layer. The external layer would be made of NO6022 or Alloy 22 (Ni-22Cr-13Mo-3W-3Fe). Since over their lifetime, the containers may be exposed to multi-ionic aqueous environments, a potential degradation mode of the outer layer could be environmentally assisted cracking (EAC) or stress corrosion cracking (SCC). In general, Alloy 22 is extremely resistant to SCC, especially in concentrated chloride solutions. Current results obtained through slow strain rate testing (SSRT) shows that Alloy 22 may suffer SCC in simulated concentrated water (SCW) at applied potentials approximately 400 mV more anodic than the corrosion potential (E{sub rr}).

  4. Research on mechanisms of stress corrosion cracking in Zircaloy

    Energy Technology Data Exchange (ETDEWEB)

    Knorr, D.B.; Pelloux, R.M.

    1981-06-01

    The results of internal gas pressurization tests, primarily at 320/sup 0/C, on cladding tubes from two suppliers, Supplier A and Supplier B, are presented. The two lots show a substantial difference in iodine SCC susceptibility so a test matrix is used to resolve the relative contributions of surface condition, residual stress, and texture. Additional tests with constant deflection split-ring specimens and with unstressed cladding segments are used to understand crack initiation and the early crack growth stages of SCC. The difference in SCC susceptibility is due to crystallographic texture. Other variables such as surface finish, stress relief temperature, and residual stress have little or no effect. Mechanical properties, crack initiation, and crack propagation all depend on texture. Both initiation and propagation features are analyzed by scanning electron microscopy. A mechanism for crack initiation consistent with most observations in this study and with the work of other investigators is proposed. At 320/sup 0/C, lifetime is crack initiation limited while several tests at 390/sup 0/C indicate that lifetime is less initiation limited at higher temperature. 31 figures, 9 tables.

  5. Elasto-Plasticity Critical Corrosive Ratio Model for RC Structure Corrosive Expanding Crack

    Institute of Scientific and Technical Information of China (English)

    CHEN Yueshun; LU Yiyan; LIU Li

    2007-01-01

    The parameter of filling expanding ratio n, plasticity factor k1 and deformation parameter k2 is raised, and then the elasto-plasticity critical corrosive ratio model for RC structure corrosive expanding crack based on elasto-plasticity theory is constructed in this paper. The influences of parameters such as filling expansion ratio n, plasticity factor k1, deformation parameter k2, Poisson ratio of concrete v, diameter of reinforced bar d and protective layer thickness c on the critical corrosive ratio are researched by theory analysis and experiments. The experimental results validate the accuracy of the model. According to the experimental study, the least squares solution is calculated as n=1.8,k1 =0.61,k2 =0.5.

  6. Origins of Negative Strain Rate Dependence of Stress Corrosion Cracking Initiation in Alloy 690, and Intergranular Crack Formation in Thermally Treated Alloy 690

    Science.gov (United States)

    Kim, Young Suk; Kim, Sung Soo

    2016-09-01

    We show that enhanced stress corrosion cracking (SCC) initiation in cold-rolled Alloy 690 with decreasing strain rate is related to the rate of short-range ordering (SRO) but not to the time-dependent corrosion process. Evidence for SRO is provided by aging tests on cold-rolled Alloy 690 at 623 K and 693 K (350 °C and 420 °C), respectively, which demonstrate its enhanced lattice contraction and hardness increase with aging temperature and time, respectively. Secondary intergranular cracks formed only in thermally treated and cold-rolled Alloy 690 during SCC tests, which are not SCC cracks, are caused by its lattice contraction by SRO before SCC tests but not by the orientation effect.

  7. INHIBITION OF STRESS CORROSION CRACKING OF CARBON STEEL STORAGE TANKS AT HANFORD

    Energy Technology Data Exchange (ETDEWEB)

    BOOMER, K.D.

    2007-01-31

    The stress corrosion cracking (SCC) behavior of A537 tank steel was investigated in a series of environments designed to simulate the chemistry of legacy nuclear weapons production waste. Tests consisted of both slow strain rate tests using tensile specimens and constant load tests using compact tension specimens. Based on the tests conducted, nitrite was found to be a strong SCC inhibitor. Based on the test performed and the tank waste chemistry changes that are predicted to occur over time, the risk for SCC appears to be decreasing since the concentration of nitrate will decrease and nitrite will increase.

  8. Analysis of cracking in reinforced concrete using accelerated tests

    Energy Technology Data Exchange (ETDEWEB)

    Nguyen, Q.T.; Berthaud, Y. [Univ Paris 06, CNRS, ENSC, LMT, F-94235 Cachan (France); Care, S [CNRS, ENPC, LCPC, Inst Navier, LMSGC, F-77420 Champs Sur Marne (France); Millard, A. [CEA, DEN/DM2S/SEMT/LM2S, F-91191 Gif Sur Yvette (France)

    2007-02-15

    We present in this Note an experimental study-in a laboratory setup-of the mechanical effect (cracking of concrete) of corrosion on plates made of reinforced concrete. Due to the geometry it is possible to use digital image correlation to follow the evolution of strains induced by the corrosion of reinforcement. The corrosion is accelerated by the imposition of current density. Even if the representativeness of this test is still discussed, it allows one to record the entire strain history. The kinetics of cracking has been obtained and compared to a very simple model in which the increase of the corroded layer is modelled by a fictitious thermal load, the reinforcement remaining elastic and the concrete being damageable. (authors)

  9. Fundamental aspects of stress corrosion cracking of copper relevant to the Swedish deep geologic repository concept

    Energy Technology Data Exchange (ETDEWEB)

    Bhaskaran, Ganesh; Carcea, Anatolie; Ulaganathan, Jagan; Wang, Shengchun; Huang, Yin; Newman, Roger C. [Dept. of Chemical Engineering and Applied Chemistry, Univ. of Toronto, Toronto (Canada)

    2013-03-15

    Phosphorus-doped oxygen-free copper will be used as the outer barrier in canisters that will contain spent nuclear fuel in the proposed Swedish underground repository. The possibility of stress corrosion cracking (SCC) is a concern, in view of isolated reports of cracking or intergranular corrosion of pure copper in sulfide solutions. This concern was addressed in the present work using copper tensile specimens provided by SKB. Methods included slow strain rate testing, constant strain tensile testing, electrochemical and surface analytical studies of corrosion products, and electron backscatter diffraction analysis of grain orientation effects on corrosion. The base solutions were prepared from NaCl or synthetic sea water with addition of varying amounts of sodium sulfide at room temperature and 80 degree Celsius. No SCC was found in any of the testing, for a range of sulfide concentrations from 5-50 mM at room temperature or 8 C, including tests where small anodic or cathodic potential displacements were applied from the open-circuit (corrosion) potential. Neither was SCC found in constant-strain immersion testing with very large strain. The Cu2S corrosion product is generally very coarse, fragile, and easily spalled off in severe corrosion environments, i.e. high sulfide concentration, high temperature, less perfect de aeration, etc. But it could also consist of very fine grains, relatively compact and adherent, on particular grain orientations when it was formed on an electro polished surface in a very well-deaerated solution. These orientations have not yet been identified statistically, although some preference for thin, adherent films was noted on orientations close to (100). The notion that the corrosion reaction is always controlled by inward aqueous-phase diffusion of sulfide may thus not be unconditionally correct for this range of sulfide concentrations; however it is hard to distinguish the role of diffusion within pores in the film. In the actual

  10. Computational modeling of the mechanism of hydrogen embrittlement (HE) and stress corrosion cracking (SCC) in metals

    Science.gov (United States)

    Cendales, E. D.; Orjuela, F. A.; Chamarraví, O.

    2016-02-01

    In this article theoretical models and some existing data sets were examined in order to model the two main causes (hydrogen embrittlement and corrosion-cracking under stress) of the called environmentally assisted cracking phenomenon (EAC). Additionally, a computer simulation of flat metal plate subject to mechanical stress and cracking due both to hydrogen embrittlement and corrosion was developed. The computational simulation was oriented to evaluate the effect on the stress-strain behavior, elongation percent and the crack growth rate of AISI SAE 1040 steel due to three corrosive enviroments (H2 @ 0.06MPa; HCl, pH=1.0; HCl, pH=2.5). From the computer simulation we conclude that cracking due to internal corrosion of the material near to the crack tip limits affects more the residual strength of the flat plate than hydrogen embrittlement and generates a failure condition almost imminent of the mechanical structural element.

  11. Evaluation of the stress corrosion cracking resistance of several high strength low alloy steels

    Science.gov (United States)

    Humphries, T. S.; Nelson, E. E.

    1980-01-01

    The stress corrosion cracking resistance was studied for high strength alloy steels 4130, 4340, for H-11 at selected strength levels, and for D6AC and HY140 at a single strength. Round tensile and C-ring type specimens were stressed up to 100 percent of their yield strengths and exposed to alternate immersion in salt water, salt spray, the atmosphere at Marshall Space Flight Center, and the seacoast at Kennedy Space Center. Under the test conditions, 4130 and 4340 steels heat treated to a tensile strength of 1240 MPa (180 ksi), H-11 and D6AC heat treated to a tensile strength of 1450 MPa (210 ksi), and HY140 (1020 MPa, 148 ksi) are resistant to stress corrosion cracking because failures were not encountered at stress levels up to 75 percent of their yield strengths. A maximum exposure period of one month for alternate immersion in salt water or salt spray and three months for seacoast is indicated for alloy steel to avoid false indications of stress corrosion cracking because of failure resulting from severe pitting.

  12. Computer Simulation of Intergranular Stress Corrosion Cracking via Hydrogen Embrittlement

    Energy Technology Data Exchange (ETDEWEB)

    Smith, R.W.

    2000-04-01

    Computer simulation has been applied to the investigation of intergranular stress corrosion cracking in Ni-based alloys based on a hydrogen embrittlement mechanism. The simulation employs computational modules that address (a) transport and reactions of aqueous species giving rise to hydrogen generation at the liquid-metal interface, (b) solid state transport of hydrogen via intergranular and transgranular diffusion pathways, and (c) fracture due to the embrittlement of metallic bonds by hydrogen. A key focus of the computational model development has been the role of materials microstructure (precipitate particles and grain boundaries) on hydrogen transport and embrittlement. Simulation results reveal that intergranular fracture is enhanced as grain boundaries are weakened and that microstructures with grains elongated perpendicular to the stress axis are more susceptible to cracking. The presence of intergranular precipitates may be expected to either enhance or impede cracking depending on the relative distribution of hydrogen between the grain boundaries and the precipitate-matrix interfaces. Calculations of hydrogen outgassing and in gassing demonstrate a strong effect of charging method on the fracture behavior.

  13. Small-crack test methods

    Science.gov (United States)

    Larsen, James M.; Allison, John E.

    This book contains chapters on fracture mechanics parameters for small fatigue cracks, monitoring small-crack growth by the replication method, measurement of small cracks by photomicroscopy (experiments and analysis), and experimental mechanics of microcracks. Other topics discussed are the real-time measurement of small-crack-opening behavior using an interferometric strain/displacement gage; direct current electrical potential measurement of the growth of small cracks; an ultrasonic method for the measurement of the size and opening behavior of small fatigue cracks; and the simulation of short crack and other low closure loading conditions, utilizing constant K(max) Delta-K-decreasing fatigue crack growth procedures.

  14. Stress corrosion cracking and its anisotropy of a PZT ferroelectric ceramics

    Institute of Scientific and Technical Information of China (English)

    2003-01-01

    Stress corrosion cracking (SCC) of a PZT ferroelectric ceramics in various media, such as moist atmosphere, silicon oil, methanol, water and formamide, and its anisotropy have been investigated at constant load test using a single-edge notched tensile specimen. The results showed that SCC could occur in all media, and the threshold stress intensity factor of SCC in water and formamide, KISCC, revealed anisotropy. The KISCC for poling direction parallel to the crack plane, was greater than that perpendicular to the crack plane, similar to the anisotropy of fracture toughness KIC; however, the anisotropy factor of KISCC, which was =1.8 (in formamide) and 2.1 (in water), was larger than that of KIC, which is =1.4. The stress-induced 90° domain switching causes the anisotropy of KIC and KISCC, besides, the resistance of SCC also has anisotropy.

  15. Cracks propagation by stress corrosion cracking in conditions of Boiling Water Reactor (BWR); Propagacion de grietas por corrosion bajo esfuerzo en condiciones de reactor de agua hirviente (BWR)

    Energy Technology Data Exchange (ETDEWEB)

    Fuentes C, P

    2003-07-01

    This work presents the results of the assays carried out in the Laboratory of Hot Cells of the National Institute of Nuclear Research (ININ) to a type test tube Compact Tension (CT), built in steel austenitic stainless type 304L, simulating those conditions those that it operates a Boiling Water Reactor (BWR), at temperature 288 C and pressure of 8 MPa, to determine the speed to which the cracks spread in this material that is of the one that different components of a reactor are made, among those that it highlights the reactor core vessel. The application of the Hydrogen Chemistry of the Water is presented (HWC) that is one alternative to diminish the corrosion effect low stress in the component, this is gets controlling the quantity of oxygen and of hydrogen as well as the conductivity of the water. The rehearsal is made following the principles of the Mechanics of Elastic Lineal Fracture (LEFM) that considers a crack of defined size with little plastic deformation in the tip of this; the measurement of crack advance is continued with the technique of potential drop of direct current of alternating signal, this is contained inside the standard Astm E-647 (Method of Test Standard for the Measurement of Speed of Growth of Crack by fatigue) that is the one that indicates us as carrying out this test. The specifications that should complete the test tubes that are rehearsed as for their dimensions, it forms, finish and determination of mechanical properties (tenacity to the fracture mainly) they are contained inside the norm Astm E-399, the one which it is also based on the principles of the fracture mechanics. The obtained results were part of a database to be compared with those of other rehearsals under different conditions, Normal Chemistry of the Water (NWC) and it dilutes with high content of O{sub 2}; to determine the conditions that slow more the phenomena of stress corrosion cracking, as well as the effectiveness of the used chemistry and of the method of

  16. Stress corrosion cracking in canistered waste package containers: Welds and base metals

    Energy Technology Data Exchange (ETDEWEB)

    Huang, J.S.

    1998-03-01

    The current design of waste package containers include outer barrier using corrosion allowable material (CAM) such as A516 carbon steel and inner barrier of corrosion resistant material (CRM) such as alloy 625 and C22. There is concern whether stress corrosion cracking would occur at welds or base metals. The current memo documents the results of our analysis on this topic.

  17. Sensitization, intergranular attack, stress corrosion cracking, and irradiation effects on the corrosion of iron--chromium--nickel alloys

    Energy Technology Data Exchange (ETDEWEB)

    Wu, P.C.S.

    1978-04-01

    A literature review is presented on the sensitization, intergranular attack, and stress corrosion cracking of austenitic stainless steels with emphasis on dilute solutions at temperatures below the boiling point of water. An attempt is made to list the possible sources of contaminants during manufacture, shipping, construction and all phases of operation of the sodium containing components. The susceptibility of the different materials to stress corrosion cracking in the various contaminants is discussed and suggestions to prevent serious problems are made. (GHT)

  18. POTENTIAL FOR STRESS CORROSION CRACKING OF A537 CARBON STEEL NUCLEAR WASTE TANKS CONTAINING HIGHLY CAUSTIC SOLUTIONS

    Energy Technology Data Exchange (ETDEWEB)

    Lam, P.; Stripling, C.; Fisher, D.; Elder, J.

    2010-04-26

    The evaporator recycle streams of nuclear waste tanks may contain waste in a chemistry and temperature regime that exceeds the current corrosion control program, which imposes temperature limits to mitigate caustic stress corrosion cracking (CSCC). A review of the recent service history found that two of these A537 carbon steel tanks were operated in highly concentrated hydroxide solution at high temperature. Visual inspections, experimental testing, and a review of the tank service history have shown that CSCC has occurred in uncooled/un-stress relieved tanks of similar construction. Therefore, it appears that the efficacy of stress relief of welding residual stress is the primary corrosion-limiting mechanism. The objective of this experimental program is to test A537 carbon steel small scale welded U-bend specimens and large welded plates (30.48 x 30.38 x 2.54 cm) in a caustic solution with upper bound chemistry (12 M hydroxide and 1 M each of nitrate, nitrite, and aluminate) and temperature (125 C). These conditions simulate worst-case situations in these nuclear waste tanks. Both as-welded and stress-relieved specimens have been tested. No evidence of stress corrosion cracking was found in the U-bend specimens after 21 days of testing. The large plate test was completed after 12 weeks of immersion in a similar solution at 125 C except that the aluminate concentration was reduced to 0.3 M. Visual inspection of the plate revealed that stress corrosion cracking had not initiated from the machined crack tips in the weld or in the heat affected zone. NDE ultrasonic testing also confirmed subsurface cracking did not occur. Based on these results, it can be concluded that the environmental condition of these tests was unable to develop stress corrosion cracking within the test periods for the small welded U-bends and for the large plates, which were welded with an identical procedure as used in the construction of the actual nuclear waste tanks in the 1960s. The

  19. Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking

    Science.gov (United States)

    Zheng, Chuan-bo; Yan, Bing-hao; Zhang, Ke; Yi, Guo

    2015-07-01

    The hydrogen permeation behavior and stress corrosion cracking (SCC) susceptibility of precharged 7075-T6 Al alloy were investigated in this paper. Devanthan-Stachurski (D-S) cell tests were used to measure the apparent hydrogen diffusivity and hydrogen permeation current density of specimens immersed in 3.5wt% NaCl solution. Electrochemical experiment results show that the SCC susceptibility is low during anodic polarization. Both corrosion pits and hydrogen-induced cracking are evident in scanning electron microscope images after the specimens have been charging for 24 h.

  20. Dissolution Condensation Mechanism of Stress Corrosion Cracking in Liquid Metals: Driving Force and Crack Kinetics

    Science.gov (United States)

    Glickman, Evgeny E.

    2011-02-01

    Stress corrosion cracking (SCC) in aqueous solution is driven by exothermic reactions of metal oxidation. This stimulus, as well as classical mechanisms of SCC, does not apply to SCC in liquid metals (LMs). In the framework of the dissolution-condensation mechanism (DCM), we analyzed the driving force and crack kinetics for this nonelectrochemical mode of SCC that is loosely called "liquid metal embrittlement" (LME). According to DCM, a stress-induced increase in chemical potential at the crack tip acts as the driving force for out-of-the-tip diffusion mass transfer that is fast because diffusion in LMs is very fast and surface energy at the solid-liquid interface is small. In this article, we review two versions of DCM mechanism, discuss the major physics behind them, and develop DCM further. The refined mechanism is applied then to the experimental data on crack velocity V vs stress intensity factor, the activation energy of LME, and alloying effects. It is concluded that DCM provides a good conceptual framework for analysis of a unified kinetic mechanism of LME and may also contribute to SCC in aqueous solutions.

  1. Ultrasonic inspection reliability for intergranular stress corrosion cracks

    Energy Technology Data Exchange (ETDEWEB)

    Heasler, P G; Taylor, T T; Spanner, J C; Doctor, S R; Deffenbaugh, J D [Pacific Northwest Lab., Richland, WA (USA)

    1990-07-01

    A pipe inspection round robin entitled Mini-Round Robin'' was conducted at Pacific Northwest Laboratory from May 1985 through October 1985. The research was sponsored by the US Nuclear Regulatory Commission, Office of Nuclear Regulatory Research under a program entitled Evaluation and Improvement of NDE Reliability for Inservice Inspection of Light Water Reactors.'' The Mini-Round Robin (MRR) measured the intergranular stress corrosion (GSC) crack detection and sizing capabilities of inservice inspection (ISI) inspectors that had passed the requirements of IEB 83-02 and the Electric Power Research Institute (EPRI) sizing training course. The MRR data base was compared with an earlier Pipe Inspection Round Robin (PIRR) that had measured the performance of inservice inspection prior to 1982. Comparison of the MRR and PIRR data bases indicates no significant change in the inspection capability for detecting IGSCC. Also, when comparing detection of long and short cracks, no difference in detection capability was measured. An improvement in the ability to differentiate between shallow and deeper IGSCC was found when the MRR sizing capability was compared with an earlier sizing round robin conducted by the EPRI. In addition to the pipe inspection round robin, a human factors study was conducted in conjunction with the Mini-Round Robin. The most important result of the human factors study is that the Relative Operating Characteristics (ROC) curves provide a better methodology for describing inspector performance than only probability of detection (POD) or single-point crack/no crack data. 6 refs., 55 figs., 18 tabs.

  2. Evaluation of irradiation assisted stress corrosion cracking (IASCC) of type 316 stainless steel irradiated in FBR

    Energy Technology Data Exchange (ETDEWEB)

    Tsukada, T. (Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan)); Jitsukawa, S. (Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan)); Shiba, K. (Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan)); Sato, Y. (Power Reactor and Nuclear Fuel Development Corp., Oarai, Ibaraki (Japan)); Shibahara, I. (Power Reactor and Nuclear Fuel Development Corp., Oarai, Ibaraki (Japan)); Nakajima, H. (Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan))

    1993-12-01

    Type 316 stainless steel from the core of the experimental fast breeder reactor (FBR) JOYO was examined by the slow strain rate tensile (SSRT) test in pure, oxygenated-water and air and by the electrochemical potentiokinetic reactivation (EPR) test to evaluate a susceptibility to the irradiation assisted stress corrosion cracking (IASCC) and the radiation-induced segregation (RIS). The solution annealed and 20% cold-worked materials had been irradiated at 425 C to a neutron fluence of 8.3x10[sup 26] n/m[sup 2] (> 0.1 MeV) which is equivalent to 40 displacement per atom (dpa). Intergranular cracking was induced by the SSRT in water at 200 and 300 C, but was not observed on specimen tested in water at 60 C and in air at 300 C. This indicates that irradiation increased a susceptibility to stress corrosion cracking (SCC) in water. After the EPR test, grain boundary etching was observed in addition to grain face etching. This suggests Cr depletion may have occurred both at grain boundary and at defect clusters during the irradiation. The results are compared with the behavior of similar materials irradiated with different neutron spectrum. (orig.)

  3. Lead-induced stress-corrosion cracking of alloy 600 in plausible steam generator crevice environments

    Energy Technology Data Exchange (ETDEWEB)

    Wright, M.D. [Atomic Energy of Canada Limited, Chalk River, Ontario (Canada); Manolescu, A. [Ontario Hydro Technologies, Toronto, Ontario (Canada); Mirzai, M. [Ontario Hydro, Toronto, Ontario (Canada)

    1999-03-01

    Laboratory stress-corrosion cracking (SCC) test environments were developed to simulate crevice chemistries representative of Bruce Nuclear Generating Station A (BNPD A) steam generators (SGs); these test environments were used to determine the susceptibility of Alloy 600 to lead-induced SCC under plausible SG conditions. Test environments were based on plant SG hideout return data and analysis of removed tubes and deposits. Deviations from the normal near-neutral crevice pH environment were considered to simulate possible faulted excursion crevice chemistry and to bound the postulated crevice pH range of 3 to 9 (at temperature). The effect of lead contamination up to 1000 ppm, but with an emphasis on the 100- to 500-ppm range, was determined. SCC susceptibility was investigated using constant extension rate tensile (CERT) tests and encapsulated C-ring tests. CERT tests were performed at 305 degrees C on tubing representative of BNPD A SG U-bends. The C-ring test method allowed a wider test matrix, covering 3 temperatures (280 degrees C, 304 degrees C and 315 degrees C), 3 strain levels (0.2%, 2% and 4%), and tubing representative of U-bends plus tubing given a simulated stress relief to represent material at the tube sheet. The results of this test program confirmed that in the absence of lead contamination, cracking does not occur in these concentrated, 3.3 to 8.9 pH range, crevice environments. Also, it appears that the concentrated crevice environments suppress lead-induced cracking relative to that seen in all-volatile-treatment (AVT) water. For the (static) C-ring tests, lead-induced SCC was only produced in the near-neutral crevice environment and was more severe at 500 ppm than at 100 ppm PbO. This trend was also observed in CERT tests, but some cracking-grain boundary attack occurred in acidic (pH 3.3) and alkaline (pH 8.9) environments. The C-ring tests indicated that a certain amount of resistance to cracking was imparted by simulated stress relief of

  4. Prevention of stress-corrosion cracking in nuclear waste storage tanks

    Energy Technology Data Exchange (ETDEWEB)

    Ondrejcin, R S

    1984-01-01

    Stress corrosion cracking (SCC) has occurred in the early versions of carbon steel primaries of nuclear waste tanks at the Savannah River Plant. (Secondary containment was provided by a vessel surrounding the lower portion of the primary tank.) Evaporated alkaline nitrate wastes in the form of crystallized salts are being dissolved from some of these tanks for transfer to new tanks of a different design. To prevent the SCC sequence from occurring during salt dissolution, the levels of inhibitors required to prevent cracking at yield stresses were determined. Special statistically designed experiments were performed to evaluate the probability of cracking under the combined influences of nitrate, nitrite, hydroxide, and temperature. Experimentlly, samples were tested by a potentially controlled constant extension rate test and by wedge opening loaded samples. Two equations were derived by multivariable regression analyses that correlated probability of cracking as the dependent variable to nitrate, nitrite, and hydroxide concentrations and temperature as the independent variables. From these equations, simple operating standards were developed by setting the probability of cracking equal to zero and solving for the four independent variables. 15 references, 15 figures, 8 tables.

  5. Mechanism of intergranular stress corrosion cracking in HAZ for super-martensitic stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Miyata, Yukio; Kimura, Mitsuo [Tubular Products and Casting Research Dept., JFE Steel Corporation, 1-1, Kawasaki-cho, Handa (Japan); Nakamichi, Haruo; Sato, Kaoru [Analysis and Characterization Research Dept., JFE Steel Corporation, 1-1, Minamiwatarida-cho, Kawasaki-ku, Kawasaki (Japan); Itakura, Noritsugu [Products Service and Development Dept., Chita Works, JFE Steel Corporation. 1-1, Kawasaki-cho, Handa (Japan); Masamura, Katsumi [Tubular Products Business Planning Dept., JFE Steel Corporation, 2-2-3, Uchisaiwai-sho, Chiyoda-ku, Tokyo (Japan)

    2004-07-01

    Mechanism of intergranular stress corrosion cracking (IGSCC) for heat affected zone (HAZ) of super-martensitic stainless steel was studied using two types of the steel. One was a lean grade, which was Mo free and low Ni, and the other was a high grade, which was Mo added and high Ni. Specimens received heat treatments simulating welding thermal cycles were applied to SCC tests. Cracks were observed in some specimens after U-bend SCC test under low pH environments. Thermal cycle conditions with sensitization were verified from the results. No crack was observed in the specimen with the thermal cycle simulating post welding heat treatment (PWHT) after sensitizing conditions. Therefore, PWHT was clarified to be effective to prevent the cracking. Cr carbides were observed along prior austenite grain boundary intermittently, and Cr depleted zone was confirmed on the grain boundary adjacent to carbides that precipitated on the grain boundary. It is, therefore, concluded that the cracking results from Cr depletion on prior austenite grain boundary accompanied by precipitation of Cr carbides under specific welding conditions. (authors)

  6. Factors affecting stress assisted corrosion cracking of carbon steel under industrial boiler conditions

    Science.gov (United States)

    Yang, Dong

    Failure of carbon steel boiler tubes from waterside has been reported in the utility boilers and industrial boilers for a long time. In industrial boilers, most waterside tube cracks are found near heavy attachment welds on the outer surface and are typically blunt, with multiple bulbous features indicating a discontinuous growth. These types of tube failures are typically referred to as stress assisted corrosion (SAC). For recovery boilers in the pulp and paper industry, these failures are particularly important as any water leak inside the furnace can potentially lead to smelt-water explosion. Metal properties, environmental variables, and stress conditions are the major factors influencing SAC crack initation and propagation in carbon steel boiler tubes. Slow strain rate tests (SSRT) were conducted under boiler water conditions to study the effect of temperature, oxygen level, and stress conditions on crack initation and propagation on SA-210 carbon steel samples machined out of boiler tubes. Heat treatments were also performed to develop various grain size and carbon content on carbon steel samples, and SSRTs were conducted on these samples to examine the effect of microstructure features on SAC cracking. Mechanisms of SAC crack initation and propagation were proposed and validated based on interrupted slow strain tests (ISSRT). Water chemistry guidelines are provided to prevent SAC and fracture mechanics model is developed to predict SAC failure on industrial boiler tubes.

  7. Method For Testing Properties Of Corrosive Lubricants

    Science.gov (United States)

    Ohi, James; De La Cruz, Jose L.; Lacey, Paul I.

    2006-01-03

    A method of testing corrosive lubricating media using a wear testing apparatus without a mechanical seal. The wear testing apparatus and methods are effective for testing volatile corrosive lubricating media under pressure and at high temperatures.

  8. Hydrogen-related stress corrosion cracking in line pipe steel

    DEFF Research Database (Denmark)

    Nielsen, Lars Vendelbo

    1997-01-01

    A correlation between hydrogen concentration (C0) and the critical stress intensity factor for propagation of hydrogen-related cracks has been established by fracture mechanical testing of CT-specimens for the heat affected zone of an X-70 pipeline steel. This has been compared with field...

  9. Microstructural investigation of vintage pipeline steels highly susceptible to stress corrosion cracking

    Science.gov (United States)

    Torres, Monica

    The use of pipelines for the transmission of gas offers not only efficiency, but a number of economic advantages. Nevertheless, pipelines are subject to aggressive operating conditions and environments which can lead to in-service degradation [1] and thus to failures. These failures can have catastrophic consequences, such as environmental damage and loss of life [2]. One of the most dangerous threats to pipeline integrity is stress corrosion cracking (SCC). Despite the substantial progress that has been achieved in the field, due to the complex nature of this phenomenon there is still not a complete understanding of this form of external corrosion. This makes its detection and prevention a challenge and therefore a risk to pipeline integrity, and most importantly, to the safety of the population. SCC cracks are the result of the interaction between a corrosive environment, applied stresses, and a susceptible microstructure. To date, what defines a susceptible microstructure remains ambiguous, as SCC has been observed in a range of steel grades, microstructures, chemical composition, and grain sizes. Therefore, in order to be able to accurately predict and prevent this hazardous form of corrosion, it is imperative to advance our knowledge on the subject and gain a better understanding on the microstructural features of highly susceptible pipeline materials, especially in the subsurface zone where crack nucleation must take place. Therefore, a microstructural characterization of the region near the surface layer was carried-out utilizing TEM. TEM analysis revealed the dislocation character, ferrite morphology, and apparent carbide precipitation in some grain boundaries. Furthermore, light microscopy, SEM, and hardness testing were performed to expand our knowledge on the microscopical features of highly SCC susceptible service components. This investigation presents a new approach to SCC characterization, which exposed the sub-surface region microscopical

  10. Corrosion and cracking behaviour of steel and alloys in liquid H{sub 2}S

    Energy Technology Data Exchange (ETDEWEB)

    Longaygue, X. [Institut Francais du Petrole, 1 et 4 avenue de Bois Preau 92852 Rueil-Malmaison (France); Duval, S. [Institut Francais du Petrole, BP no 3, 69390 Vernaison (France)

    2004-07-01

    When oil and gas wells with very high partial pressure of H{sub 2}S, e.g. H{sub 2}S-rich gas, are under production, the presence of liquid H{sub 2}S is highly probable in the process operations. Until now, corrosion engineers and materials designers have paid little attention to this situation because it is rarely encountered in practice. However, such a scenario recently met an increasing interest in the context of the Sprex development, a new H{sub 2}S pre-extraction process used for the treatment of very sour natural gases, which produces the separated acid gases as a liquid phase for re-injection to a disposal reservoir. It is generally accepted that pure liquid H{sub 2}S is not corrosive by itself towards carbon or low alloy steels, but the presence of water in production and reservoir fluids could make this medium much more corrosive, although this latter assumption is poorly documented. The aim of this paper is to present the corrosion and cracking behaviour of a pipeline carbon steel and of corrosion resistant alloys (CRA) (with Cr > 16%) after exposure to the following media: i) liquid H{sub 2}S saturated with water, and ii) liquid H{sub 2}O saturated with H{sub 2}S. For both solutions, the addition of solid sulphur on some specimens was considered to take into account the possible introduction of oxygen into the system, followed by a reaction with H{sub 2}S. The tests were performed at 80 deg. C in a laboratory autoclave where both phases coexisted, using U-bend specimens as well as rectangular corrosion coupons. The main conclusion of this study is that liquid H{sub 2}S is rather less critical for corrosion and cracking of construction alloys than 'classical' sour solutions, like H{sub 2}S-saturated water. As a consequence, the materials selection will be governed by the same criteria, with the following alternatives: i) use of carbon steels in conjunction with corrosion inhibitors, e.g. higher operation expense; or ii) selection of a CRA

  11. Electrochemical studies on stress corrosion cracking of incoloy-800 in caustic solution. Part II: Precracking samples

    Directory of Open Access Journals (Sweden)

    Dinu Alice

    2006-01-01

    Full Text Available Stress corrosion cracking (SCC in a caustic medium may affect the secondary circuit tubing of a CANDU NPP cooled with river water, due to an accidental formation of a concentrated alkaline environment in the areas with restricted circulation, as a result of a leakage of cooling water from the condenser. To evaluate the susceptibility of Incoloy-800 (used to manufacture steam generator tubes for CANDU NPP to SCC, some accelerated corrosion tests were conducted in an alkaline solution (10% NaOH, pH = 13. These experiments were performed at ambient temperature and 85 °C. We used the potentiodynamic method and the potentiostatic method, simultaneously monitoring the variation of the open circuit potential during a time period (E corr/time curve. The C-ring method was used to stress the samples. In order to create stress concentrations, mechanical precracks with a depth of 100 or 250 μm were made on the outer side of the C-rings. Experimental results showed that the stressed samples were more susceptible to SCC than the unstressed samples whereas the increase in temperature and crack depth lead to an increase in SCC susceptibility. Incipient micro cracks of a depth of 30 μm were detected in the area of the highest peak of the mechanical precrack.

  12. Quantitative characterization of initiation and propagation in stress corrosion cracking. An approach of a phenomenological model; Caracterisation quantitative de l`amorcage et de la propagation en corrosion sous contrainte. Approche d`une modelisation phenomenologique

    Energy Technology Data Exchange (ETDEWEB)

    Raquet, O.

    1994-11-25

    A purely phenomenological study of stress corrosion cracking was performed using the couple Z2CN 18.10 (304L) austenitic stainless steel/boiling MgCl{sub 2} aqueous solution. The exploitation of the morphological information (shape of the cracks and size distribution) available after constant elongation rate tests led to the proposal of an analytical expression of the crack initiation and growth rates. This representation allowed to quantitatively characterize the influence of the applied strain rate as well as the effect of corrosion inhibitors on the crack initiation and propagation phases. It can be used in the search for the stress corrosion cracking mechanisms as a `riddle` for the determination of the rate controlling steps. As a matter of fact, no mechanistic hypothesis has been used for its development. (author).

  13. The mechanism of stress-corrosion cracking in 7075 aluminum alloy

    Science.gov (United States)

    Jacobs, A. J.

    1970-01-01

    Various aspects of stress-corrosion cracking in 7075 aluminum alloy are discussed. A model is proposed in which the continuous anodic path along which the metal is preferentially attacked consists of two phases which alternate as anodes.

  14. Hydrogen-increased dezincification layer-induced stress and susceptibility to stress corrosion cracking of brass

    Institute of Scientific and Technical Information of China (English)

    李会录; 高克玮; 褚武扬; 刘亚萍; 乔利杰

    2003-01-01

    Dezincification layer formed during corrosion or stress corrosion cracking (SCC) of brass in an ammonia solution could induce an additive stress. The effect of hydrogen on the dezincification layer-induced stress and the susceptibility to SCC were studied. The dezincification layer-induced stress was measured using the deflection method and the flowing stress differential method, respectively. The latter measures the difference between the flowing stress of a specimen before unloading and the yield stress of the same specimen after unloading and forming a dezincification layer. The susceptibility to SCC was measured using slow strain rate test. Results show that both the dezincification layer-induced stress and the susceptibility to SCC increase with increasing hydrogen concentration in a specimen. This implies that hydrogen-enhanced dezincification layer-induced stress is consistence with the hydrogen-increased susceptibility to SCC of brass in the ammonia solution.

  15. Precursor Evolution and Stress Corrosion Cracking Initiation of Cold-Worked Alloy 690 in Simulated Pressurized Water Reactor Primary Water

    Energy Technology Data Exchange (ETDEWEB)

    Zhai, Ziqing [Pacific Northwest National Laboratory, 622 Horn Rapids Road, P.O. Box 999, Richland, Washington 99352.; Toloczko, Mychailo [Pacific Northwest National Laboratory, 622 Horn Rapids Road, P.O. Box 999, Richland, Washington 99352.; Kruska, Karen [Pacific Northwest National Laboratory, 622 Horn Rapids Road, P.O. Box 999, Richland, Washington 99352.; Bruemmer, Stephen [Pacific Northwest National Laboratory, 622 Horn Rapids Road, P.O. Box 999, Richland, Washington 99352.

    2017-05-22

    Stress corrosion crack initiation of two thermally-treated, cold-worked (CW) alloy 690 (UNS N06690) materials was investigated in 360oC simulated PWR primary water using constant load tensile (CLT) tests and blunt notch compact tension (BNCT) tests equipped with direct current potential drop (DCPD) for in-situ detection of cracking. SCC initiation was not detected by DCPD for either the 21% or 31%CW CLT specimens loaded at their yield stress after ~9,220 hours, however intergranular (IG) precursor damage and isolated surface cracks were observed on the specimens. The two 31%CW BNCT specimens loaded at moderate stress intensity after several cyclic loading ramps showed DCPD-indicated crack initiation after 10,400 hours of exposure at constant stress intensity, which was resulted from significant growth of IG cracks. The 21%CW BNCT specimens only exhibited isolated small IG surface cracks and showed no apparent DCPD change throughout the test. Post-test cross-section examinations revealed many grain boundary (GB) nano-cavities in the bulk of all the CLT and BNCT specimens particularly for the 31%CW materials. Cavities were also found along GBs extending to the surface suggesting an important role in crack nucleation. This paper provides an overview of the evolution of GB cavities and discusses their effects on crack initiation in CW alloy 690.

  16. INVESTIGATION OF THE POTENTIAL FOR CAUSTIC STRESS CORROSION CRACKING OF A537 CARBON STEEL NUCLEAR WASTE TANKS

    Energy Technology Data Exchange (ETDEWEB)

    Lam, P.

    2009-10-15

    The evaporator recycle streams contain waste in a chemistry and temperature regime that may be outside of the current waste tank corrosion control program, which imposes temperature limits to mitigate caustic stress corrosion cracking (CSCC). A review of the recent service history (1998-2008) of Tanks 30 and 32 showed that these tanks were operated in highly concentrated hydroxide solution at high temperature. Visual inspections, experimental testing, and a review of the tank service history have shown that CSCC has occurred in uncooled/un-stress relieved F-Area tanks. Therefore, for the Type III/IIIA waste tanks the efficacy of the stress relief of welding residual stress is the only corrosion-limiting mechanism. The objective of this experimental program is to test carbon steel small scale welded U-bend specimens and large welded plates (12 x 12 x 1 in.) in a caustic solution with upper bound chemistry (12 M hydroxide and 1 M each of nitrate, nitrite, and aluminate) and temperature (125 C). These conditions simulate worst-case situations in Tanks 30 and 32. Both as-welded and stress-relieved specimens have been tested. No evidence of stress corrosion cracking was found in the U-bend specimens after 21 days of testing. The large plate test is currently in progress, but no cracking has been observed after 9 weeks of immersion. Based on the preliminary results, it appears that the environmental conditions of the tests are unable to develop stress corrosion cracking within the duration of these tests.

  17. Effect of prior corrosion state on the fatigue small cracking behaviour of 6151-T6 aluminum alloy

    Energy Technology Data Exchange (ETDEWEB)

    Li Xudong [Department of Engineering Mechanics, AML, Tsinghua University, Beijing 100084 (China); Naval Aeronautical Engineering Academy Qingdao Branch, Qingdao 266000 (China); Wang Xishu, E-mail: xshwang@tsinghua.edu.cn [Department of Engineering Mechanics, AML, Tsinghua University, Beijing 100084 (China); Ren Huaihui; Chen Yinlong [Department of Engineering Mechanics, AML, Tsinghua University, Beijing 100084 (China); Mu Zhitao [Naval Aeronautical Engineering Academy Qingdao Branch, Qingdao 266000 (China)

    2012-02-15

    Highlights: Black-Right-Pointing-Pointer Relationship of corrosion pit and fatigue crack is established based on SEM. Black-Right-Pointing-Pointer An equivalent relationship between accelerated and natural corrosion is build up. Black-Right-Pointing-Pointer Prior corrosion damage is crucial to the subsequent fatigue cracking behaviour. Black-Right-Pointing-Pointer The prior corrosion fatigue crack growth rate is expressed by the term of k{sigma}{sub max}{sup n}a. Black-Right-Pointing-Pointer Corrosion states such as SC15, are defined based on corrosion spectrum. - Abstract: The purpose of this paper was to estimate the reliable effect of prior corrosion state on fatigue micro crack initiation and early stage propagation behaviour of aluminum alloy based on scanning electron microscopy (SEM) in situ observation. Results indicated that multi-cracks initiation occurred almost at the corrosion pits and the early stage of fatigue micro crack propagation behaviour can be described by K{sub I}/K{sub II}-mixed mode. The importance of crack-face interaction via crack-face corrosion pits interlocking/bridging was emphasised in the mixed mode. The fatigue crack growth rate in the corrosion states can be empirically expressed by the term of k{sigma}{sub max}{sup n}a.

  18. Pacific Northwest National Laboratory Investigation of the Stress Corrosion Cracking in Nickel-Base Alloys, Volume 2

    Energy Technology Data Exchange (ETDEWEB)

    Bruemmer, Stephen M.; Toloczko, Mychailo B.; Olszta, Matthew J.

    2012-03-01

    The objective of this program is to evaluate the primary water stress corrosion cracking (PWSCC) susceptibility of high chromium alloy 690 and its weld metals, establish quantitative measurements of crack-growth rates and determine relationships among cracking susceptibility, environmental conditions and metallurgical characteristics. Stress-corrosion, crack-growth rates have been determined for 12 alloy 690 specimens, 11 alloy 152/52/52M weld metal specimens, 4 alloy 52M/182 overlay specimens and 2 alloy 52M/82 inlay specimens in simulated PWR primary water environments. The alloy 690 test materials included three different heats of extruded control-rod-drive mechanism (CRDM) tubing with variations in the initial material condition and degree of cold work for one heat. Two cold-rolled (CR) alloy 690 plate heats were also obtained and evaluated enabling comparisons to the CR CRDM materials. Weld metal, overlay and inlay specimens were machined from industry mock ups to provide plant-representative materials for testing. Specimens have been tested for one alloy 152 weld, two alloy 52 welds and three alloy 52M welds. The overlay and inlay specimens were prepared to propagate stress-corrosion cracks from the alloy 182 or 82 material into the more resistant alloy 52M. In all cases, crack extension was monitored in situ by direct current potential drop (DCPD) with length resolution of about +1 µm making it possible to measure extremely low growth rates approaching 5x10-10 mm/s. Most SCC tests were performed at 325-360°C with hydrogen concentrations from 11-29 cc/kg; however, environmental conditions were modified during a few experiments to evaluate the influence of temperature, water chemistry or electrochemical potential on propagation rates. In addition, low-temperature (~50°C) cracking behavior was examined for selected alloy 690 and weld metal specimens. Extensive characterizations have been performed on material microstructures and stress-corrosion cracks by

  19. Modeling Threshold of Stress Intensity Factor in Iodine Induced Stress Corrosion Crack of Zirconium

    Institute of Scientific and Technical Information of China (English)

    SHANG; Xin-yuan; CHEN; Peng

    2013-01-01

    KISCC,which is the threshold of stress intensity factor of iodine induced stress corrosion crack(ISCC)of Zirconium,reflects the susceptibility of ISCC of zirconium.Once the stress intensity factor surpasses the threshold,the cracking propagation modality in material will transform to transgranular from intergranular immediately and the velocity of the cracking will increase rapidly.Four key factors that’s

  20. Strain-induced corrosion cracking in ferritic components of BWR primary circuits; Risskorrosion in druckfuehrenden ferritischen Komponenten des Primaerkreislaufes von Siedewasserreaktoren

    Energy Technology Data Exchange (ETDEWEB)

    Seifert, H.-P.; Ritter, S.; Ineichen, U.; Tschanz, U.; Gerodetti, B

    2003-04-01

    The present final report of the RIKORR project is a summary of a literature survey and of the experimental work performed by PSI on the environmentally-assisted cracking (EAC) and dynamic strain ageing (DSA) susceptibility of low-alloy steels (LAS) in high-temperature (HT) water. Within this project, the EAC crack growth behaviour of different low-alloy RPV steels, weld filler and weld heat-affected zone materials has been investigated under simulated transient and steady-state BWR/NWC power operation conditions. The strain-induced corrosion cracking (SICC) / low-frequency corrosion fatigue (CF) and stress corrosion cracking (SCC) crack growth behaviour of different low-alloy RPV steels under simulated transient and stationary BWR/NWC conditions was characterized by slow rising load / low-frequency corrosion fatigue and constant load / periodical partial unloading / ripple load tests with pre-cracked fracture mechanics specimens in oxygenated HT water at temperatures of either 288, 250, 200 or 150 {sup o}C. Modern high-temperature water loops, on-line crack growth monitoring and fractographic analysis by scanning electron microscopy (SEM) were used to quantify the cracking response. (author)

  1. Investigations of the corrosion fatigue behaviour at a super pure martensitic stainless steel X5CrNiCuNb 17 4 PH in comparison to the soft martensitic stainless steel X4CrNiMo 16 5 1 ESR in chloride containing aqueous media. Pt. 2. Corrosion fatigue tests and crack initiation mechanisms

    Energy Technology Data Exchange (ETDEWEB)

    Schmitt-Thomas, K.G.; Happle, T.; Wunderlich, R.

    1989-07-01

    The following report concerns the study of the corrosion fatigue behaviour of the soft martensitic steel X4CrNiMo 16 5 1 ESR and the precipitation hardened X5CrNiCuNb 17 4 PH in sodium solution in the temperature range between 20/sup 0/ and 150/sup 0/C and the determination of their general corrosion properties and the mechanism of crack propagation. Their corrosion fatigue limits were compared with each other. A comparison was also made between an electro-slag-remelted soft martensitic steel and a charge without an ESR aftertreatment. Microfractographical fracture and crack path investigation were carried out for interpretation of the experimental results. It was observed that in both super pure steels (soft martensitic and precipitation hardened) the oxidic inclusions are not responsible for the crack initiation, as it was found in the non ESR treated steels. In the 17-4 PH steel copper containing inclusions in the crack initiation areas were observed. In concentrated sodium solution pitting corrosion was found at both steels. (orig.).

  2. Accelerated Stress Corrosion Crack Initiation of Alloys 600 and 690 in Hydrogenated Supercritical Water

    Science.gov (United States)

    Moss, Tyler; Was, Gary S.

    2017-04-01

    The objective of this study is to determine whether stress corrosion crack initiation of Alloys 600 and 690 occurs by the same mechanism in subcritical and supercritical water. Tensile bars of Alloys 690 and 600 were strained in constant extension rate tensile experiments in hydrogenated subcritical and supercritical water from 593 K to 723 K (320 °C to 450 °C), and the crack initiation behavior was characterized by high-resolution electron microscopy. Intergranular cracking was observed across the entire temperature range, and the morphology, structure, composition, and temperature dependence of initiated cracks in Alloy 690 were consistent between hydrogenated subcritical and supercritical water. Crack initiation of Alloy 600 followed an Arrhenius relationship and did not exhibit a discontinuity or change in slope after crossing the critical temperature. The measured activation energy was 121 ± 13 kJ/mol. Stress corrosion crack initiation in Alloy 690 was fit with a single activation energy of 92 ± 12 kJ/mol across the entire temperature range. Cracks were observed to propagate along grain boundaries adjacent to chromium-depleted metal, with Cr2O3 observed ahead of crack tips. All measures of the SCC behavior indicate that the mechanism for stress corrosion crack initiation of Alloy 600 and Alloy 690 is consistent between hydrogenated subcritical and supercritical water.

  3. Accelerated Stress Corrosion Crack Initiation of Alloys 600 and 690 in Hydrogenated Supercritical Water

    Science.gov (United States)

    Moss, Tyler; Was, Gary S.

    2017-01-01

    The objective of this study is to determine whether stress corrosion crack initiation of Alloys 600 and 690 occurs by the same mechanism in subcritical and supercritical water. Tensile bars of Alloys 690 and 600 were strained in constant extension rate tensile experiments in hydrogenated subcritical and supercritical water from 593 K to 723 K (320 °C to 450 °C), and the crack initiation behavior was characterized by high-resolution electron microscopy. Intergranular cracking was observed across the entire temperature range, and the morphology, structure, composition, and temperature dependence of initiated cracks in Alloy 690 were consistent between hydrogenated subcritical and supercritical water. Crack initiation of Alloy 600 followed an Arrhenius relationship and did not exhibit a discontinuity or change in slope after crossing the critical temperature. The measured activation energy was 121 ± 13 kJ/mol. Stress corrosion crack initiation in Alloy 690 was fit with a single activation energy of 92 ± 12 kJ/mol across the entire temperature range. Cracks were observed to propagate along grain boundaries adjacent to chromium-depleted metal, with Cr2O3 observed ahead of crack tips. All measures of the SCC behavior indicate that the mechanism for stress corrosion crack initiation of Alloy 600 and Alloy 690 is consistent between hydrogenated subcritical and supercritical water.

  4. Effect of Stress on Corrosion at Crack Tip on Pipeline Steel in a Near-Neutral pH Solution

    Science.gov (United States)

    Yang, Yao; Cheng, Y. Frank

    2016-10-01

    In this work, the local corrosion at crack tip on an API 5L X46 pipeline steel specimens was investigated under various applied loads in a near-neutral pH solution. Electrochemical measurements, including potentiodynamic polarization and electrochemical impedance spectroscopy, combined with micro-electrochemical technique and surface characterization, were conducted to investigate the effect of stress on local anodic solution of the steel at the crack tip. The stress corrosion cracking of the steel was dominated by an anodic dissolution mechanism, while the effect of hydrogen was negligible. The applied load (stress) increased the corrosion rate at the crack tip, contributing to crack propagation. The deposit of corrosion products at the crack tip could protect somewhat from further corrosion. At sufficiently large applied loads such as 740 N in the work, it was possible to generate separated cathode and anode, further accelerating the crack growth.

  5. Effect of Stress on Corrosion at Crack Tip on Pipeline Steel in a Near-Neutral pH Solution

    Science.gov (United States)

    Yang, Yao; Cheng, Y. Frank

    2016-11-01

    In this work, the local corrosion at crack tip on an API 5L X46 pipeline steel specimens was investigated under various applied loads in a near-neutral pH solution. Electrochemical measurements, including potentiodynamic polarization and electrochemical impedance spectroscopy, combined with micro-electrochemical technique and surface characterization, were conducted to investigate the effect of stress on local anodic solution of the steel at the crack tip. The stress corrosion cracking of the steel was dominated by an anodic dissolution mechanism, while the effect of hydrogen was negligible. The applied load (stress) increased the corrosion rate at the crack tip, contributing to crack propagation. The deposit of corrosion products at the crack tip could protect somewhat from further corrosion. At sufficiently large applied loads such as 740 N in the work, it was possible to generate separated cathode and anode, further accelerating the crack growth.

  6. Stress corrosion cracking of AISI 321 stainless steel in acidic chloride solution

    Indian Academy of Sciences (India)

    Yanliang Huang

    2002-02-01

    The stress corrosion cracking (SCC) of AISI 321 stainless steel in acidic chloride solution was studied by slow strain rate (SSR) technique and fracture mechanics method. The fractured surface was characterized by cleavage fracture. In order to clarify the SCC mechanism, the effects of inhibitor KI on SCC behaviour were also included in this paper. A study showed that the inhibition effects of KI on SCC were mainly attributed to the anodic reaction of the corrosion process. The results of strain distribution in front of the crack tip of the fatigue pre-cracked plate specimens in air, in the blank solution (acidic chloride solution without inhibitor KI) and in the solution added with KI measured by speckle interferometry (SPI) support the unified mechanism of SCC and corrosion fatigue cracking (CFC).

  7. Corrosion Fatigue Crack Growth Behavior at Notched Hole in 7075-T6 Under Biaxial and Uniaxial Fatigue with Different Phases

    Science.gov (United States)

    2015-09-17

    CORROSION FATIGUE CRACK GROWTH BEHAVIOR AT NOTCHED HOLE IN 7075-T6 UNDER BIAXIAL AND UNIAXIAL FATIGUE WITH DIFFERENT PHASES... CORROSION FATIGUE CRACK GROWTH BEHAVIOR AT NOTCHED HOLE IN 7075-T6 UNDER BIAXIAL AND UNIAXIAL FATIGUE WITH DIFFERENT PHASES THESIS...UNLIMITED AFIT-ENY-MS-15-S-065 CORROSION FATIGUE CRACK GROWTH BEHAVIOR AT NOTCHED HOLE IN 7075-T6 UNDER BIAXIAL AND UNIAXIAL FATIGUE WITH

  8. Stress corrosion cracking of austenitic weld deposits in a salt spray environment

    Science.gov (United States)

    Cai, J. B.; Yu, C.; Shiue, R. K.; Tsay, L. W.

    2015-10-01

    ER 308L and 309LMo were utilized as the filler metals for the groove and overlay welds of a 304L stainless steel substrate, which was prepared via a gas tungsten arc-welding process in multiple passes. U-bend and weight-loss tests were conducted by testing the welds in a salt spray containing 10 wt% NaCl at 120 °C. The dissolution of the skeletal structure in the fusion zone (FZ) caused the stress corrosion cracking (SCC) of the weld. The FZ in the cold-rolled condition showed the longest single crack length in the U-bend tests. Moreover, sensitization treatment at 650 °C for 10 h promoted the formation of numerous fine cracks, which resulted in a high SCC susceptibility. The weight loss of the deposits was consistent with the SCC susceptibility of the welds in a salt spray. The 309LMo deposit was superior to the 308L deposit in the salt spray.

  9. Stress corrosion cracking of welded joints of super-martensitic stainless steel in H{sub 2}S free environment

    Energy Technology Data Exchange (ETDEWEB)

    Hoerner, Bertrand; Bayle, Bernard; Delafosse, David [Centre Science des Materiaux et des Structures - URA CNRS 5146, ENS Mines de Saint-Etienne, 158 Cours Fauriel, 42023 Saint-Etienne cedex 02 (France); Ligier, Vincent [CRMC, INDUSTEEL Creusot, 56, rue Clemenceau, BP 56 - 71 202 Le Creusot Cedex (France)

    2004-07-01

    Due to their combination of good weldability and good mechanical properties, low carbon super-martensitic stainless steels are good candidates for oil and gas flow line applications. These alloys have already been used in slightly sour environments containing chlorides, CO{sub 2} and H{sub 2}S. The properties of a welded joint whose composition is matching or superduplex that of the base metal are investigated. The base material is the super-martensitic stainless steels medium alloy: 13Cr-4.5Ni-1.5Mo. The Heat Affected Zone (HAZ) of girth welds may be sensitive to stress corrosion cracking and presents distinct features intergranular cracking when tested in four-point bending in a sour deaerated environment at temperatures around 100 deg. C. The electrochemical properties of the medium alloy and the matching welded joint + HAZ were determined in a chloride-containing environment without H{sub 2}S. A passive film is formed on polished samples. This film is less protective for the welded joint + HAZ samples than in the base metal. Moreover, the pitting corrosion resistance is strongly decreased in the HAZ. Slow strain rate tensile tests were conducted in a de-aerated solution without H{sub 2}S. They reproduce the same type of cracking as was observed in four point bending tests in a sour environment: initiation in the HAZ and an intergranular crack with a very brittle aspect and no significant trace of corrosion. The presence H{sub 2}S is not the prevailing factor for the occurrence of cracking. Furthermore, it is not necessary to have a specific surface condition for crack initiation to occur in slow strain rate tension, as it is the case four point bend tests where initiation appears to be controlled by the surface condition (chemical and / or geometrical). Finally, a simulated PWHT strongly increase the resistance to SSC. (authors)

  10. Hydrogen cracking and stress corrosion of pipeline steels. Contribution of the cracking mechanisms study to the understanding of the in-service damage and to the definition of a ranking test; Fissuration assistee par l'hydrogene et corrosion sous contrainte des aciers de pipelines. Apports de l'etude des mecanismes de fissuration a la comprehension de l'endommagement de service et a la definition d'un test de classification

    Energy Technology Data Exchange (ETDEWEB)

    Le Friant, D.

    2000-12-19

    This work is based on the study of the cracking of a French oil transmission pipeline protected by a cathodic protection system. The objective is to identify field parameters, which contribute to the cracks propagation, and to assess changes in the operating conditions, which could lead to a mitigation of the phenomenon. We have focused on the study of the micro-mechanisms by means of slow strain rate tests. Then, cyclic loading tests were carried out to investigate cracks propagation mechanisms. Smooth and pre-notched specimens were tested at free and cathodic potential. Hydrogen is responsible for crack advance through changes in the local steels properties. Such effects take place when two phenomenons occur: favourable conditions for hydrogen entry and, a localisation of hydrogen and its effects. In particular, we have shown the essential role of a dynamic loading in promoting hydrogen entry into the steel (especially at the very crack tip). At cathodic potential, hydrogen-related effects are exacerbated by the presence of MnS inclusions which leads to the initiation of internal cracks (HIC) and to a SOHIC-like crack morphology. At free potential, the lesser amount of available hydrogen give localisation-related effects a greater importance. Cracking is then related to a hydrogen-induced SCC mechanism. Three parameters are involved in the field cracking: operating pressure variations, period of over-protection and a sensitive steels microstructure (MnS). Cathodic protection appears to be the most efficient field parameter to mitigate the phenomenon: it requires a better control of the polarisation level. Finally, a ranking test is outlined from the study of the cracking mechanisms. (author)

  11. Corrosion Preventive Compounds Lifetime Testing

    Science.gov (United States)

    Hale, Stephanie M.; Kammerer, Catherine C.; Copp, Tracy L.

    2007-01-01

    Lifetime Testing of Corrosion Preventive Compounds (CPCs) was performed to quantify performance in the various environments to which the Space Shuttle Orbiter is exposed during a flight cycle. Three CPCs are approved for use on the Orbiter: RD Calcium Grease, Dinitrol AV-30, and Braycote 601 EF. These CPCs have been rigorously tested to prove that they mitigate corrosion in typical environments, but little information is available on how they perform in the unique combination of the coastal environment at the launch pad, the vacuum of low-earth orbit, and the extreme heat of reentry. Currently, there is no lifetime or reapplication schedule established for these compounds that is based on this combination of environmental conditions. Aluminum 2024 coupons were coated with the three CPCs and exposed to conditions that simulate the environments to which the Orbiter is exposed. Uncoated Aluminum 2024 coupons were exposed to the environmental conditions as a control. Visual inspection and Electro- Impedance Spectroscopy (EIS) were performed on the samples in order to determine the effectiveness of the CPCs. The samples were processed through five mission life cycles or until the visual inspection revealed the initiation of corrosion and EIS indicated severe degradation of the coating.

  12. Environmental Cracking of Corrosion Resistant Alloys in the Chemical Process Industry - A Review

    Energy Technology Data Exchange (ETDEWEB)

    Rebak, R B

    2006-12-04

    A large variety of corrosion resistant alloys are used regularly in the chemical process industry (CPI). The most common family of alloys include the iron (Fe)-based stainless steels, nickel (Ni) alloys and titanium (Ti) alloys. There also other corrosion resistant alloys but their family of alloys is not as large as for the three groups mentioned above. All ranges of corrosive environments can be found in the CPI, from caustic solutions to hot acidic environments, from highly reducing to highly oxidizing. Stainless steels are ubiquitous since numerous types of stainless steels exist, each type tailored for specific applications. In general, stainless steels suffer stress corrosion cracking (SCC) in hot chloride environments while high Ni alloys are practically immune to this type of attack. High nickel alloys are also resistant to caustic cracking. Ti alloys find application in highly oxidizing solutions. Solutions containing fluoride ions, especially acid, seem to be aggressive to almost all corrosion resistant alloys.

  13. Film-induced stress enhancing stress corrosion cracking of austenitic stainless steel

    Institute of Scientific and Technical Information of China (English)

    李金许; 陈浩; 王燕斌; 乔利杰; 褚武扬

    2001-01-01

    A constant deflection device designed for use within a transmission electron microscopy (TEM) was used to investigate the change in dislocation configuration ahead of a crack tip during stress corrosion cracking (SCC) of type 310 austenitic stainless steel in a boiling MgCl2 solution, and the initiation process of stress corrosion microcrack. Results showed that corrosion process during SCC enhanced dislocation emission, multiplication and motion. Microcracks of SCC were initiated when the corrosion-enhanced dislocation emission and motion reached critical state.   A passive film formed during corrosion of austenitic stainless steel in the boiling MgCl2 solution generated a tensile stress. During SCC, the additive tensile stress generated at the metal/passive film interface helps enhance dislocation emission and motion.

  14. Influence factors on stress corrosion cracking of P110 tubing steel under CO2 injection well annulus environment

    Institute of Scientific and Technical Information of China (English)

    刘然克; 贾静焕; 杜翠薇; 李晓刚

    2016-01-01

    Stress corrosion cracking (SCC) behavior of P110 tubing steel in simulated CO2 injection well annulus environments was investigated through three-point bent tests, potentiodynamic polarization and EIS measurements. The results demonstrate that SCC of P110 tubing steel could occur in acidulous simulated environment, and the sensitivity of SCC increases with the decrease of pH, as well as increase of sulfide concentration and total environmental pressure. Both anodic dissolution and hydrogen embrittlement make contributions to the SCC. Adequate concentration of corrosion inhibitor can inhibit the occurrence of SCC on account of the inhibition of localized anodic dissolution and cathodic hydrogen evolution.

  15. Improved stress corrosion cracking resistance of a novel biodegradable EW62 magnesium alloy by rapid solidification, in simulated electrolytes

    Energy Technology Data Exchange (ETDEWEB)

    Hakimi, O.; Aghion, E. [Department of Materials Engineering, Ben-Gurion University of the Negev, P.O. Box 653, Beer-Sheva 84105 (Israel); Goldman, J., E-mail: jgoldman@mtu.edu [Biomedical Engineering Department, Michigan Technological University, Houghton, MI, 49931 (United States)

    2015-06-01

    The high corrosion rate of magnesium (Mg) and Mg-alloys precludes their widespread acceptance as implantable biomaterials. Here, we investigated the potential for rapid solidification (RS) to increase the stress corrosion cracking (SCC) resistance of a novel Mg alloy, Mg–6%Nd–2%Y–0.5%Zr (EW62), in comparison to its conventionally cast (CC) counterpart. RS ribbons were extrusion consolidated in order to generate bioimplant-relevant geometries for testing and practical use. Microstructural characteristics were examined by SEM. Corrosion rates were calculated based upon hydrogen evolution during immersion testing. The surface layer of the tested alloys was analyzed by X-ray photoelectron spectroscopy (XPS). Stress corrosion resistance was assessed by slow strain rate testing and fractography. The results indicate that the corrosion resistance of the RS alloy is significantly improved relative to the CC alloy due to a supersaturated Nd enrichment that increases the Nd{sub 2}O{sub 3} content in the external oxide layer, as well as a more homogeneous structure and reduced grain size. These improvements contributed to the reduced formation of hydrogen gas and hydrogen embrittlement, which reduced the SCC sensitivity relative to the CC alloy. Therefore, EW62 in the form of a rapidly solidified extruded structure may serve as a biodegradable implant for biomedical applications. - Highlights: • Here we have evaluated the corrosion resistance of a novel Mg alloy (EW62). • Rapid solidification reduces the hydrogen gas evolution and hydrogen embrittlement. • Rapid solidification increases the stress corrosion cracking resistance of EW62. • Improvement is due to enrichment with supersaturated Nd in the external oxide film. • Rapidly solidified and extruded EW62 may serve as a biodegradable medical implant.

  16. Relationship between localized strain and irradiation assisted stress corrosion cracking in an austenitic alloy

    Energy Technology Data Exchange (ETDEWEB)

    McMurtrey, M.D., E-mail: mdmcm@umich.edu [Department of Nuclear Engineering and Radiological Sciences, University of Michigan, Ann Arbor, MI 48109 (United States); Was, G.S. [Department of Nuclear Engineering and Radiological Sciences, University of Michigan, Ann Arbor, MI 48109 (United States); Patrick, L.; Farkas, D. [Department of Materials Science and Engineering, Virginia Tech, Blacksburg, VA 24061 (United States)

    2011-04-25

    Research highlights: {yields} Austenitic steel is more susceptible to intergranular corrosion after irradiation. {yields} Simulation and experiment used to study cracking in irradiated austentic steel. {yields} Cracking occurs at random high angle boundaries normal to the tensile stress. {yields} Cracking at boundaries with high normal stress and inability to accommodate strain. {yields} Boundary type, angle, and Taylor and Schmid factors affect strain accommodation. - Abstract: Irradiation assisted stress corrosion cracking may be linked to the local slip behavior near grain boundaries that exhibit high susceptibility to cracking. Fe-13Cr-15Ni austenitic steel was irradiated with 2 MeV protons at 360 deg. C to 5 dpa and strained in 288 deg. C simulated BWR conditions. Clusters of grains from the experiment were created in an atomistic simulation and then virtually strained using molecular dynamic simulation techniques. Cracking and grain orientation data were characterized in both the experiment and the simulation. Random high angle boundaries with high surface trace angles with respect to the tensile direction were found to be the most susceptible to cracking. Grain boundary cracking susceptibility was also found to correlate strongly with slip continuity, indicating that the strain accommodation at the boundary is related to cracking resistance. Higher cracking susceptibility was also found at grain boundaries adjacent to grains with low Schmid factor or high Taylor factor. The basic trends reported here are supported by both the experiments and the simulations.

  17. Tensile stress corrosion cracking of type 304 stainless steel irradiated to very high dose

    Energy Technology Data Exchange (ETDEWEB)

    Chung, H. M.; Ruther, W. E.; Strain, R. V.; Shack, W. J.

    2001-09-01

    Certain safety-related core internal structural components of light water reactors, usually fabricated from Type 304 or 316 austenitic stainless steels (SSs), accumulate very high levels of irradiation damage (20--100 displacement per atom or dpa) by the end of life. The data bases and mechanistic understanding of, the degradation of such highly irradiated components, however, are not well established. A key question is the nature of irradiation-assisted intergranular cracking at very high dose, i.e., is it purely mechanical failure or is it stress-commotion cracking? In this work, hot-cell tests and microstructural characterization were performed on Type 304 SS from the hexagonal fuel can of the decommissioned EBR-11 reactor after irradiation to {approximately}50 dpa at {approximately}370 C. Slow-strain-rate tensile tests were conducted at 289 C in air and in water at several levels of electrochemical potential (ECP), and microstructural characteristics were analyzed by scanning and transmission electron microcopies. The material deformed significantly by twinning and exhibited surprisingly high ductility in air, but was susceptible to severe intergranular stress corrosion cracking (IGSCC) at high ECP. Low levels of dissolved O and ECP were effective in suppressing the susceptibility of the heavily irradiated material to IGSCC, indicating that the stress corrosion process associated with irradiation-induced grain-boundary Cr depletion, rather than purely mechanical separation of grain boundaries, plays the dominant role. However, although IGSCC was suppressed, the material was susceptible to dislocation channeling at low ECP, and this susceptibility led to poor work-hardening capability and low ductility.

  18. Development of chloride-induced corrosion in pre-cracked RC beams under sustained loading: Effect of load-induced cracks, concrete cover, and exposure conditions

    Energy Technology Data Exchange (ETDEWEB)

    Yu, Linwen [Université de Toulouse, UPS, INSA, LMDC, Toulouse (France); Université de Sherbrooke, Quebec (Canada); François, Raoul, E-mail: raoul.francois@insa-toulouse.fr [Université de Toulouse, UPS, INSA, LMDC, Toulouse (France); Dang, Vu Hiep [Hanoi Architectural University, Faculty of Civil Engineering, Hanoi (Viet Nam); L' Hostis, Valérie [CEA Saclay, CEA, DEN, DPC, SECR, Laboratoire d' Etude du Comportement des Bétons et des Argiles, Gif-sur-Yvette (France); Gagné, Richard [Université de Sherbrooke, Quebec (Canada)

    2015-01-15

    This paper deals with corrosion initiation and propagation in pre-cracked reinforced concrete beams under sustained loading during exposure to a chloride environment. Specimen beams that were cast in 2010 were compared to specimens cast in 1984. The only differences between the two sets of beams were the casting direction in relation to tensile reinforcement and the exposure conditions in the salt-fog chamber. The cracking maps, corrosion maps, chloride profiles, and cross-sectional loss of one group of two beams cast in 2010 were studied and their calculated corrosion rates were compared to that of beams cast in 1984 in order to investigate the factors influencing the natural corrosion process. Experimental results show that, after rapid initiation of corrosion at the crack tip, the corrosion process practically halted and the time elapsing before corrosion resumed depended on the exposure conditions and cover depth.

  19. Stress corrosion cracking of X70 pipeline steel in near-neutral pH soil solution

    Energy Technology Data Exchange (ETDEWEB)

    Fang, B.Y.; Wang, J.Q.; Han, E.H.; Zhu, Z.Y.; Ke, W. [Chinese Academy of Sciences, Shenyang (China). State Key Laboratory for Corrosion and Protection, Inst. of Metal Research

    2004-07-01

    Near-neutral pH stress corrosion cracking (SCC) is characterized by wide transgranular cracks with quasi-cleavage on the fracture surface, and there is usually little evidence of general or lateral corrosion. Near-neutral pH SCC is related to dissolution and hydrogen ingress into steel pipes because discharged atomic hydrogen can enter the steel so that cracks are initiated or grown by a combination of dissolution and hydrogen-embrittlement. In this study, the SCC cracking behaviour of an X70 pipeline was investigated using slow strain rate tests (SSRT) and cyclic loading at high R and low frequency in a near-neutral pH soil solution saturated with 5 per cent carbon dioxide (CO{sub 2}) and 95 per cent nitrogen (N{sub 2}). Potentiodynamic polarization analyses and electrochemical impedance spectrum (EIS) analyses were also conducted in order to examine the effect of the concentration of bicarbonate, bubbled gas and the addition of chloride ions on polarization behaviour. Results of the SSRT tests showed that transgranular SCC occurred in the soil solution. Crack initiation was associated with pitting. The pipe's susceptibility to SCC increased with decreases in applied electrochemical potential and strain rate. Cyclic loading tests showed that crack propagation processes were dominated by SCC. At high R and low frequencies, SCC was observed on fatigued, pre-cracked specimens. Results of the electrochemical tests showed that polarization behaviours were influenced by the concentrations of bicarbonate, bubbled gas, and the addition of chloride ions. It was concluded that the addition of chloride ion can influence film stability on pipeline specimen surfaces. 22 refs., 2 tabs., 8 figs.

  20. Influence of nitrogen on the stress corrosion cracking resistance of austenitic stainless steels in chloride environment; Influence de l'azote sur la resistance a la corrosion sous contrainte d'aciers inoxydables austenitiques en milieu chlorure

    Energy Technology Data Exchange (ETDEWEB)

    Teysseyre, S

    2001-11-01

    The aim of this study is to investigate the influence of nitrogen additions on the Stress Corrosion Cracking (SSC) resistance of austenitic stainless steel in chloride environment. The investigation was carried out in two part: first, an experimental investigation with model industrial steels was carried out and secondly, numerical simulations based on the Corrosion Enhanced Plasticity Model were developed. Both slow strain rate tensile tests and constant load test of the different steels in boiling MgCl{sub 2} (153 deg C) at free potential show that, for a given plastic strain rate, nitrogen addition increases the critical stress for crack initiation without influencing the crack propagation rate. We observed that the creep rate under constant load was affected by the nitrogen content. As a consequence, the SCC behaviour (cracks density and propagation rate) depends on the nitrogen content. We thus confirm that the nitrogen content influences the corrosion - deformation interaction mechanisms via its positive contribution to the flow stress. These experimental results are reproduced semi-quantitatively by means of numerical simulations at the scale of crack. - dislocation interactions. The presence of nitrogen is modelled by an increased lattice friction stress, which in turn affects the dynamics of crack tip shielding by dislocation pile-ups. We conclude that nitrogen addition in austenitic stainless steels increases the SC crack initiation stress in proportion of the increased flow stress, without penalty in terms of SC crack propagation rate. (author)

  1. Stress corrosion cracking behavior of annealed and cold worked 316L stainless steel in supercritical water

    Energy Technology Data Exchange (ETDEWEB)

    Sáez-Maderuelo, A., E-mail: alberto.saez@ciemat.es; Gómez-Briceño, D.

    2016-10-15

    Highlights: • The alloy 316L is susceptible to stress corrosion cracking in supercritical water. • The susceptibility of alloy 316L increases with temperature and plastic deformation. • Dynamic strain ageing processes may be active in the material. - Abstract: The supercritical water reactor (SCWR) is one of the more promising designs considered by the Generation IV International Forum due to its high thermal efficiency and improving security. To build this reactor, standardized structural materials used in light water reactors (LWR), like austenitic stainless steels, have been proposed. These kind of materials have shown an optimum behavior to stress corrosion cracking (SCC) under LWR conditions except when they are cold worked. It is known that physicochemical properties of water change sharply with pressure and temperature inside of the supercritical region. Owing to this situation, there are several doubts about the behavior of candidate materials like austenitic stainless steel 316L to SCC in the SCWR conditions. In this work, alloy 316L was studied in deaerated SCW at two different temperatures (400 °C and 500 °C) and at 25 MPa in order to determine how changes in this variable influence the resistance of this material to SCC. The influence of plastic deformation in the behavior of alloy 316L to SCC in SCW was also studied at both temperatures. Results obtained from these tests have shown that alloy 316L is susceptible to SCC in supercritical water reactor conditions where the susceptibility of this alloy increases with temperature. Moreover, prior plastic deformation of 316L SS increased its susceptibility to environmental cracking in SCW.

  2. Microstructural and Stress Corrosion Cracking Characteristics of Austenitic Stainless Steels Containing Silicon

    Science.gov (United States)

    Andresen, Peter L.; Chou, Peter H.; Morra, Martin M.; Lawrence Nelson, J.; Rebak, Raul B.

    2009-12-01

    Austenitic stainless steels (SSs) core internal components in nuclear light water reactors (LWRs) are susceptible to irradiation-assisted stress corrosion cracking (IASCC). One of the effects of irradiation is the hardening of the SS and a change in the dislocation distribution in the alloy. Irradiation may also alter the local chemistry of the austenitic alloys; for example, silicon may segregate and chromium may deplete at the grain boundaries. The segregation or depletion phenomena at near-grain boundaries may enhance the susceptibility of these alloys to environmentally assisted cracking (EAC). The objective of the present work was to perform laboratory tests in order to better understand the role of Si in the microstructure, properties, electrochemical behavior, and susceptibility to EAC of austenitic SSs. Type 304 SS can dissolve up to 2 pct Si in the bulk while maintaining a single austenite microstructure. Stainless steels containing 12 pct Cr can dissolve up to 5 pct bulk Si while maintaining an austenite structure. The crack growth rate (CGR) results are not conclusive about the effect of the bulk concentration of Si on the EAC behavior of SSs.

  3. Analysis of stress corrosion cracking in alloy 718 following commercial reactor exposure

    Science.gov (United States)

    Leonard, Keith J.; Gussev, Maxim N.; Stevens, Jacqueline N.; Busby, Jeremy T.

    2015-11-01

    Alloy 718 is generally considered a highly corrosion-resistant material but can still be susceptible to stress corrosion cracking (SCC). The combination of factors leading to SCC susceptibility in the alloy is not always clear enough. In the present work, alloy 718 leaf spring (LS) materials that suffered stress corrosion damage during two 24-month cycles in pressurized water reactor service, operated to >45 MWd/mtU burn-up, was investigated. Compared to archival samples fabricated through the same processing conditions, little microstructural and property changes occurred in the material with in-service irradiation, contrary to high dose rate laboratory-based experiments reported in literature. Though the lack of delta phase formation along grain boundaries would suggest a more SCC resistant microstructure, grain boundary cracking in the material was extensive. Crack propagation routes were explored through focused ion beam milling of specimens near the crack tip for transmission electron microscopy as well as in polished plan view and cross-sectional samples for electron backscatter diffraction analysis. It has been shown in this study that cracks propagated mainly along random high-angle grain boundaries, with the material around cracks displaying a high local density of dislocations. The slip lines were produced through the local deformation of the leaf spring material above their yield strength. The cause for local SCC appears to be related to oxidation of both slip lines and grain boundaries, which under the high in-service stresses resulted in crack development in the material.

  4. The design of an instrumented rebar for assessment of corrosion in cracked reinforced concrete

    DEFF Research Database (Denmark)

    Pease, Bradley Justin; Geiker, Mette Rica; Stang, Henrik;

    2011-01-01

    An instrumented rebar is presented which was designed to have a realistic mechanical performance and to provide location dependent measurements to assess the environment with regards to reinforcement corrosion. The instrumented rebar was constructed from a hollowed 10 mm nominal diameter standard...... between the steel and concrete. Cracked beams with cast-in instrumented and standard rebars were ponded with a 10\\% chloride solution and the open circuit corrosion potential (OCP) of the 17 sensors was measured for up to 62 days. Measurements from the individual sensors indicate when and where active...... rebar with 17 electronically isolated corrosion sensors. Instrumented and standard rebars were cast into concrete beams and bending cracks were induced and held open using steel frames. Epoxy impregnation was used to assess and compare cracks in the concrete around the instrumented and standard rebar...

  5. STRESS CORROSION CRACKING SUSCEPTIBILITY OF HIGH LEVEL WASTE TANKS DURING SLUDGE MASS REDUCTION

    Energy Technology Data Exchange (ETDEWEB)

    Subramanian, K

    2007-10-18

    Aluminum is a principal element in alkaline nuclear sludge waste stored in high level waste (HLW) tanks at the Savannah River Site. The mass of sludge in a HLW tank can be reduced through the caustic leaching of aluminum, i.e. converting aluminum oxides (gibbsite) and oxide-hydroxides (boehmite) into soluble hydroxides through reaction with a hot caustic solution. The temperature limits outlined by the chemistry control program for HLW tanks to prevent caustic stress corrosion cracking (CSCC) in concentrated hydroxide solutions will potentially be exceeded during the sludge mass reduction (SMR) campaign. Corrosion testing was performed to determine the potential for CSCC under expected conditions. The experimental test program, developed based upon previous test results and expected conditions during the current SMR campaign, consisted of electrochemical and mechanical testing to determine the susceptibility of ASTM A516 carbon steel to CSCC in the relevant environment. Anodic polarization test results indicated that anodic inhibition at the temperatures and concentrations of interest for SMR is not a viable, consistent technical basis for preventing CSCC. However, the mechanical testing concluded that CSCC will not occur under conditions expected during SMR for a minimum of 35 days. In addition, the stress relief for the Type III/IIIA tanks adds a level of conservatism to the estimates. The envelope for corrosion control is recommended during the SMR campaign is shown in Table 1. The underlying assumption is that solution time-in-tank is limited to the SMR campaign. The envelope recommends nitrate/aluminate intervals for discrete intervals of hydroxide concentrations, although it is recognized that a continuous interval may be developed. The limits also sets temperature limits.

  6. Effect of cold work and processing orientation on stress corrosion cracking behavior of alloy 600

    Energy Technology Data Exchange (ETDEWEB)

    Moshier, W.C.; Brown, C.M.

    2000-03-01

    Cold work accelerates stress corrosion cracking (SCC) growth rates in Alloy 600 (UNS N06600). However, the variation in crack growth rates generated from cold-worked material has been significant, and the effect has been difficult to quantify. A study was performed in hydrogenated water adjusted to pH 10.2 to evaluate systematically the effect of cold work on Alloy 600 as a function of temperature, amount of cold work, stress intensity factor, and processing orientation. Cold work was introduced into the material by tensile prestraining or cold-rolling plate product. Crack growth rates were determined between 252 C and 360 C, stress intensity factors between 21 MPa{radical}m and 55 MPa{radical}m, and yield strengths between 201 MPa and 827 MPa. The material with the highest yield strength was cold-rolled and tested in the longitudinal-transverse (LT) and short-transverse (ST) orientations. Crack growth rates increased with increasing temperature, stress intensity factor, and yield strength. Furthermore, crack growth rates were a strong function of the processing orientation in the cold-rolled plate, with growth rates approximately an order of magnitude greater in the ST orientation compared to the LT orientation. Crack growth rates in the LT orientation were measured between 0.003 x 10{sup {minus}9} m/s and 1.95 x 10{sup {minus}9} m/s and between 0.066 x 10{sup {minus}9} m/s and 6.3 x 10{sup {minus}9} m/s in the ST orientation. Activation energies were slightly greater in the ST orientation, ranging from 154 kcal/mol to 191 kcal/mol, compared to activation energies between 126 kJ/mol and 157 kJ/mol in the LT orientation. Results of this study demonstrated that, although cold work can be used to accelerate SCC, the orientation of crack growth significantly can affect the results and must be taken into account when analyzing data from cold-worked material.

  7. Interplay of microbiological corrosion and alloy microstructure in stress corrosion cracking of weldments of advanced stainless steels

    Indian Academy of Sciences (India)

    R K Singh Raman

    2003-06-01

    This paper presents an overview of the phenomenon of stress corrosion cracking (SCC) of duplex stainless steels and their weldments in marine environments and the potential role of microbial activity in inducing SCC susceptibility. As a precursor to the topic the paper also reviews the performance of the traditional corrosion-resistant alloys and their weldments and the necessity of using duplex stainless steels (DSS), in order to alleviate corrosion problems in marine environments. Given that the performance of weldments of such steels is often unsatisfactory, this review also assesses the research needs in this area. In this context the paper also discusses the recent reports on the role of microorganisms in inducing hydrogen embrittlements and corrosion fatigue.

  8. Modeling the Time-to Corrosion Cracking of the Cover Concrete in Chloride Contaminated Reinforced Concrete Structures

    OpenAIRE

    Liu, Youping

    1996-01-01

    Significant factors on steel corrosion in chloride contaminated reinforced concrete and time-to-corrosion cracking were investigated in this study. Sixty specimens were designed with seven admixed chloride contents, three concrete cover depths, two reinforcing steel bar diameters, two exposure conditions, and a typical concrete with water to cement ratio of 0.45. Corrosion current density (corrosion rate), corrosion potential, ohmic resistance of concrete and temperature were measured monthly...

  9. Hydrogen embrittlement, grain boundary segregation, and stress corrosion cracking of alloy X-750 in low- and high-temperature water

    Energy Technology Data Exchange (ETDEWEB)

    Mills, W. J.; Lebo, M. R.; Kearns, J. J. [Bettis Atomic Power Lab., West Mifflin, PA (United States)

    1997-04-01

    The nature of intergranular stress corrosion cracking (SCC) of alloy X-750 was characterized in low- and high-temperature water by testing as-notched and precracked fracture mechanics specimens. Materials given the AH, BH, and HTH heat treatments were studied. While all heat treatments were susceptible to rapid low-temperature crack propagation (LTCP) below 150 C, conditions AH and BH were particularly susceptible. Low-temperature tests under various loading conditions (e.g., constant displacement, constant load, and increasing load) revealed that the maximum stress intensity factors (K{sub P{sub max}}) from conventional rising load tests provide conservative estimates of the critical loading conditions in highly susceptible heats, regardless of the load path history. For resistant heats, K{sub P{sub max}} provides a reasonable, but not necessarily conservative, estimate of the critical stress intensity factor for LTCP. Testing of as-notched specimens showed that LTCP will not initiate at a smooth surface or notch, but will readily occur if a cracklike defect is present. Comparison of the cracking response in water with that for hydrogen-precharged specimens tested in air demonstrated that LTCP is associated with hydrogen embrittlement of grain boundaries. The stress corrosion crack initiation and growth does occur in high-temperature water (>250 C), but crack growth rates are orders of magnitude lower than LTCP rates. The SCC resistance of HTH heats is far superior to that of AH heats as crack initiation times are two to three orders of magnitude greater and growth rates are one to two orders of magnitude lower.

  10. The susceptibility of 90Cu-10Ni alloy to stress corrosion cracking in seawater polluted by sulfide ions

    Science.gov (United States)

    Domiaty, A. El; Alhajji, J. N.

    1997-08-01

    Electrochemical polarization measurements and slow strain rate tests (SSRT) of a 90Cu-10Ni alloy in highly sulfide polluted seawater were conducted to investigate stress-corrosion cracking (SCC) behavior. The severity of the SCC depends on the sulfide concentration in the seawater. The severity increases as the concentration increases. Because the major time in SCC is spent in the initiation process of the propagating crack, the fracture toughness has only a minor effect in the component life failed by SCC. The SCC behavior of CDA706 is strictly linked to sulfide concentration in the range of 100 to 1000 ppm. The general corrosion of Cu-Ni alloys in low (100 ppm) sulfide polluted seawater increases due to the selective copper dissolution. Cyclic polarization measurements confirmed that the corrosion rate decreases slightly as the sulfide concentration increases. Pitting tendency was high in the low concentration range of sulfide and low in the high concentration range. The presence of stresses in SCC removes the protective layer as it increases during testing of the specimen or during the actual service of a component. The authors propose that film rupture occurred, and two proposed SCC mechanisms were operational, namely sulfide stress cracking associated with the anodic dissolution in the low sulfide concentration range and hydrogen embrittlement, which was dominant in the high sulfide concentration range. It was found that a synergism exists between sulfide and stress that enhances the effect of the latter.

  11. The Effect of Welding Residual Stress for Making Artificial Stress Corrosion Crack in the STS 304 Pipe

    Directory of Open Access Journals (Sweden)

    Jae-Seong Kim

    2015-01-01

    Full Text Available The stress corrosion crack is one of the fracture phenomena for the major structure components in nuclear power plant. During the operation of a power plant, stress corrosion cracks are initiated and grown especially in dissimilar weldment of primary loop components. In particular, stress corrosion crack usually occurs when the following three factors exist at the same time: susceptible material, corrosive environment, and tensile stress (residual stress included. Thus, residual stress becomes a critical factor for stress corrosion crack when it is difficult to improve the material corrosivity of the components and their environment under operating conditions. In this study, stress corrosion cracks were artificially produced on STS 304 pipe itself by control of welding residual stress. We used the instrumented indentation technique and 3D FEM analysis (using ANSYS 12 to evaluate the residual stress values in the GTAW area. We used the custom-made device for fabricating the stress corrosion crack in the inner STS 304 pipe wall. As the result of both FEM analysis and experiment, the stress corrosion crack was quickly generated and could be reproduced, and it could be controlled by welding residual stress.

  12. Standard guide for corrosion tests in high temperature or high pressure environment, or both

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2010-01-01

    1.1 This guide covers procedures, specimens, and equipment for conducting laboratory corrosion tests on metallic materials under conditions of high pressure (HP) or the combination of high temperature and high pressure (HTHP). See for definitions of high pressure and temperature. 1.2 Tests conducted under HP or HTHP by their nature have special requirements. This guide establishes the basic considerations that are necessary when these conditions must be incorporated into laboratory corrosion tests. 1.3 The procedures and methods in this guide are applicable for conducting mass loss corrosion, localized corrosion, and electrochemical tests as well as for use in environmentally induced cracking tests that need to be conducted under HP or HTHP conditions. 1.4 The primary purpose for this guide is to promote consistency of corrosion test results. Furthermore, this guide will aid in the comparison of corrosion data between laboratories or testing organizations that utilize different equipment. 1.5 The values s...

  13. Stress-Corrosion Cracking of Metallic Materials. Part III. Hydrogen Entry and Embrittlement in Steel

    Science.gov (United States)

    1975-04-01

    Strength Steels," Stress Corrosion Cracking in High-Strength Steels and in Titanium and Altuninum Alloys, Naval Rasearch Laboratory, Washington, D.C...to pickling solutions. In all of these examples, the sulfide, cyanide, etc., caused a hydrogen-related problem that would not have existed in their...desorption reaction. In studying the pickling of low-carbon steel in various strong acids, Hudson’ 4 measured the corrosion rate and amount of hydr-ogen

  14. Probabilistic Lifetime Assessment of Marine Reinforced Concrete with Steel Corrosion and Cover Cracking

    Institute of Scientific and Technical Information of China (English)

    LU Chun-hua; JIN Wei-liang; LIU Rong-gui

    2011-01-01

    In order to study the durability behavior of marine reinforced concrete structure suffering from chloride attack, the structural service life is assumed to be divided into three critical stages, which can be characterized by steel corrosion and cover cracking. For each stage, a calculated model used to predict the lifetime is developed. Based on the definition of durability limit state, a probabilistic lifetime model and its time-dependent reliability analytical method are proposed considering the random natures of influencing factors. Then, the probabilistic lifetime prediction models are applied to a bridge pier located in the Hangzhou Bay with Monte Carlo simulation. It is found that the time to corrosion initiation to follows a lognonnal distribution, while that the time from corrosion initiation to cover cracking t and the time for crack to develop from hairline crack to a limit crack width t can be described by Weibull distributions. With the permitted failure probability of 5.0%, it is also observed that the structural durability lifetime mainly depends on the durability life to and that the percentage of participation of tbe life t to the total service life grows from 61.5% to 83.6% when the cover thickness increases from 40 mm to 80 mm. Therefore, for any part of the marine RC bridge, the lifetime predictions and maintenance efforts should also be directed toward controlling the stage of corrosion initiation induced by chloride ion.

  15. Corrosion Behavior of Steel Reinforcement in Concrete with Recycled Aggregates, Fly Ash and Spent Cracking Catalyst

    Directory of Open Access Journals (Sweden)

    Hebé Gurdián

    2014-04-01

    Full Text Available The main strategy to reduce the environmental impact of the concrete industry is to reuse the waste materials. This research has considered the combination of cement replacement by industrial by-products, and natural coarse aggregate substitution by recycled aggregate. The aim is to evaluate the behavior of concretes with a reduced impact on the environment by replacing a 50% of cement by industrial by-products (15% of spent fluid catalytic cracking catalyst and 35% of fly ash and a 100% of natural coarse aggregate by recycled aggregate. The concretes prepared according to these considerations have been tested in terms of mechanical strengths and the protection offered against steel reinforcement corrosion under carbonation attack and chloride-contaminated environments. The proposed concrete combinations reduced the mechanical performance of concretes in terms of elastic modulus, compressive strength, and flexural strength. In addition, an increase in open porosity due to the presence of recycled aggregate was observed, which is coherent with the changes observed in mechanical tests. Regarding corrosion tests, no significant differences were observed in the case of the resistance of these types of concretes under a natural chloride attack. In the case of carbonation attack, although all concretes did not stand the highly aggressive conditions, those concretes with cement replacement behaved worse than Portland cement concretes.

  16. Modeling time-dependent corrosion fatigue crack propagation in 7000 series aluminum alloys

    Science.gov (United States)

    Mason, Mark E.; Gangloff, Richard P.

    1994-01-01

    Stress corrosion cracking and corrosion fatigue experiments were conducted with the susceptible S-L orientation of AA7075-T651, immersed in acidified and inhibited NaCl solution, to provide a basis for incorporating environmental effects into fatigue crack propagation life prediction codes such as NASA FLAGRO. This environment enhances da/dN by five to ten-fold compared to fatigue in moist air. Time-based crack growth rates from quasi-static load experiments are an order of magnitude too small for accurate linear superposition prediction of da/dN for loading frequencies above 0.001 Hz. Alternate methods of establishing da/dt, based on rising-load or ripple-load-enhanced crack tip strain rate, do not increase da/dt and do not improve linear superposition. Corrosion fatigue is characterized by two regimes of frequency dependence; da/dN is proportional to f(exp -1) below 0.001 Hz and to F(exp 0) to F(exp -0.1) for higher frequencies. Da/dN increases mildly both with increasing hold-time at K(sub max) and with increasing rise-time for a range of loading waveforms. The mild time-dependence is due to cycle-time-dependent corrosion fatigue growth. This behavior is identical for S-L nd L-T crack orientations. The frequency response of environmental fatigue in several 7000 series alloys is variable and depends on undefined compositional or microstructural variables. Speculative explanations are based on the effect of Mg on occluded crack chemistry and embritting hydrogen uptake, or on variable hydrogen diffusion in the crack tip process zone. Cracking in the 7075/NaCl system is adequately described for life prediction by linear superposition for prolonged load-cycle periods, and by a time-dependent upper bound relationship between da/dN and delta K for moderate loading times.

  17. Geothermal drill pipe corrosion test plan

    Energy Technology Data Exchange (ETDEWEB)

    Caskey, B.C.; Copass, K.S.

    1980-12-01

    Plans are presented for conducting a field test of drill pipe corrosion, comparing air and nitrogen as drilling fluids. This test will provide data for evaluating the potential of reducing geothermal well drilling costs by extending drill pipe life and reducing corrosion control costs. The 10-day test will take place during fall 1980 at the Baca Location in Sandoval County, New Mexico.

  18. Characterization of the Resistance of Alloy 22 to Stress Corrosion Cracking

    Energy Technology Data Exchange (ETDEWEB)

    King, K J; Estill, J C; Rebak, R B

    2002-05-30

    In its current design, the high-level nuclear waste containers include an external layer of Alloy 22 (Ni-22Cr-13Mo-3W-3Fe). Since over their lifetime, the containers may be exposed to multi-ionic aqueous environments, a potential degradation mode of the outer layer could be environmentally assisted cracking (EAC). The objective of the current research was to characterize the effect of applied potential and temperature on the susceptibility of Alloy 22 to EAC in simulated concentrated water (SCW) using the slow strain rate test (SSRT). Results show that Alloy 22 may suffer EAC at applied potentials approximately 400 mV more anodic than the corrosion potential (E{sub corr}).

  19. Improved stress corrosion cracking resistance of a novel biodegradable EW62 magnesium alloy by rapid solidification, in simulated electrolytes.

    Science.gov (United States)

    Hakimi, O; Aghion, E; Goldman, J

    2015-06-01

    The high corrosion rate of magnesium (Mg) and Mg-alloys precludes their widespread acceptance as implantable biomaterials. Here, we investigated the potential for rapid solidification (RS) to increase the stress corrosion cracking (SCC) resistance of a novel Mg alloy, Mg-6%Nd-2%Y-0.5%Zr (EW62), in comparison to its conventionally cast (CC) counterpart. RS ribbons were extrusion consolidated in order to generate bioimplant-relevant geometries for testing and practical use. Microstructural characteristics were examined by SEM. Corrosion rates were calculated based upon hydrogen evolution during immersion testing. The surface layer of the tested alloys was analyzed by X-ray photoelectron spectroscopy (XPS). Stress corrosion resistance was assessed by slow strain rate testing and fractography. The results indicate that the corrosion resistance of the RS alloy is significantly improved relative to the CC alloy due to a supersaturated Nd enrichment that increases the Nd2O3 content in the external oxide layer, as well as a more homogeneous structure and reduced grain size. These improvements contributed to the reduced formation of hydrogen gas and hydrogen embrittlement, which reduced the SCC sensitivity relative to the CC alloy. Therefore, EW62 in the form of a rapidly solidified extruded structure may serve as a biodegradable implant for biomedical applications.

  20. Investigation into the stress corrosion cracking properties of AA2099, an aluminum-lithium-copper alloy

    Science.gov (United States)

    Padgett, Barbara Nicole

    Recently developed Al-Li-Cu alloys show great potential for implementation in the aerospace industry because of the attractive mix of good mechanical properties and low density. AA2099 is an Al-Li-Cu alloy with the following composition Al-2.69wt%Cu-1.8wt%Li-0.6wt%Zn-0.3wt%Mg-0.3wt%Mn-0.08wt%Zr. The environmental assisted cracking and localized corrosion behavior of the AA2099 was investigated in this thesis. The consequences of uncontrolled grain boundary precipitation via friction stir welding on the stress corrosion cracking (SCC) behavior of AA2099 was investigated first. Using constant extension rate testing, intergranular corrosion immersion experiments, and potentiodynamic scans, the heat-affected zone on the trailing edge of the weld (HTS) was determined to be most susceptible of the weld zones. The observed SCC behavior for the HTS was linked to the dissolution of an active phase (Al2CuLi, T1) populating the grain boundary. It should be stated that the SCC properties of AA2099 in the as-received condition were determined to be good. Focus was then given to the electrochemical behavior of precipitate phases that may occupy grain and sub-grain boundaries in AA2099. The grain boundary micro-chemistry and micro-electrochemistry have been alluded to within the literature as having significant influence on the SCC behavior of Al-Li-Cu alloys. Major precipitates found in this alloy system are T1 (Al 2CuLi), T2 (Al7.5Cu4Li), T B (Al6CuLi3), and theta (Al2 Cu). These phases were produced in bulk form so that the electrochemical nature of each phase could be characterized. It was determined T1 was most active electrochemically and theta was least. When present on grain boundaries in the alloy, electrochemical behavior of the individual precipitates aligned with the observed corrosion behavior of the alloy (e.g. TB was accompanied by general pitting corrosion and T 1 was accompanied by intergranular corrosion attack). In addition to the electrochemical behavior of

  1. Electrochemical corrosion testing of metal waste forms

    Energy Technology Data Exchange (ETDEWEB)

    Abraham, D. P.; Peterson, J. J.; Katyal, H. K.; Keiser, D. D.; Hilton, B. A.

    1999-12-14

    Electrochemical corrosion tests have been conducted on simulated stainless steel-zirconium (SS-Zr) metal waste form (MWF) samples. The uniform aqueous corrosion behavior of the samples in various test solutions was measured by the polarization resistance technique. The data show that the MWF corrosion rates are very low in groundwaters representative of the proposed Yucca Mountain repository. Galvanic corrosion measurements were also conducted on MWF samples that were coupled to an alloy that has been proposed for the inner lining of the high-level nuclear waste container. The experiments show that the steady-state galvanic corrosion currents are small. Galvanic corrosion will, hence, not be an important mechanism of radionuclide release from the MWF alloys.

  2. Preparation Femtosecond Laser Prevention for the Cold-Worked Stress Corrosion Crackings on Reactor Grade Low Carbon Stainless Steel

    CERN Document Server

    John Minehara, Eisuke

    2004-01-01

    We report here that the femtosecond lasers like low average power Ti:Sapphire lasers, the JAERI high average power free-electron laser and others could peel off and remove two stress corrosion cracking (SCC) origins of the cold-worked and the cracking susceptible material, and residual tensile stress in hardened and stretched surface of low-carbon stainless steel cubic samples for nuclear reactor internals as a proof of principle experiment except for the third origin of corrosive environment. Because a 143 °C and 43% MgCl2 hot solution SCC test was performed for the samples to simulate the cold-worked SCC phenomena of the internals to show no crack at the laser-peered off strip on the cold-worked side and ten-thousands of cracks at the non-peeled off on the same side, it has been successfully demonstrated that the femtosecond lasers could clearly remove the two SCC origins and could resultantly prevent the cold-worked SCC.

  3. Crack Tip Plasticity Associated with Corrosion Assisted Fatigue.

    Science.gov (United States)

    1982-11-15

    growing. The model presented is very similar to those previously developed by Antolovich , Saxena and I Chanani[83 and by Lanteigne and BailonE9] but...in crack tip plasticity associated with environment. The model used here is conceptually similar to those formulated by * Antolovich , et al,[ and...Lankford, J. ’Fatigue-Crack-Tip I Plastic Strains by the Stereoimaging Technique’ Exp. Mech. 1980 20, 3 134-139. 8. Antolovich , S. D., Saxena, A., and

  4. Fundamental understanding and life prediction of stress corrosion cracking in BWRs and energy systems

    Energy Technology Data Exchange (ETDEWEB)

    Andresen, P.L.; Ford, F.P. [General Electric, Schenectady, NY (United States). Corporate Research and Development Center

    1998-03-01

    The objective of this paper is to present an approach for design and lifetime evaluation of environmental cracking based on experimental and fundamental modeling of the underlying processes operative in crack advance. In detailed this approach and its development and quantification for energy (hot water) systems, the requirements for a life prediction methodology will be highlighted and the shortcomings of the existing design and lifetime evaluation codes reviewed. Examples are identified of its use in a variety of cracking systems, such as stainless steels, low alloy steels, nickel base alloys, and irradiation assisted stress corrosion cracking in boiling water reactor (BWR) water, as well as preliminary use for low alloy steel and Alloy 600 in pressurized water reactors (PWRs) and turbine steels in steam turbines. Identification of the common aspects with environmental cracking in other hot water systems provides a secure basis for its extension to related energy systems. 166 refs., 49 figs.

  5. Analysis of acoustic emission signals of fatigue crack growth and corrosion processes. Investigation of the possibilities for continuous condition monitoring of transport containers by acoustic emission testing; Analyse der Schallemissionssignale aus Ermuedungsrisswachstum und Korrosionsprozessen. Untersuchung der Moeglichkeiten fuer die kontinuierliche Zustandsueberwachung von Transportbehaeltern mittels Schallemissionspruefung

    Energy Technology Data Exchange (ETDEWEB)

    Wachsmuth, Janne

    2016-05-01

    Fatigue crack growth and active corrosion processes are the main causes of structural failures of transport products like road tankers, railway tank cars and ships. To prevent those failures, preventive, time-based maintenance is performed. However, preventive inspections are costly and include the risk of not detecting a defect, which could lead to a failure within the next service period. An alternative is the idea of continuous monitoring of the whole structure by means of acoustic emission testing (AT). With AT, defects within the material shall be detected and repaired directly after their appearance. Acoustic emission testing is an online non-destructive testing method. Acoustic emission (AE) arises from changes within the material and is transported by elastic waves through the material. If the AE event generates enough energy, the elastic wave propagates to the boundaries of the component, produces a displacement in the picometre scale and can be detected by a piezoelectric sensor. The sensor produces an electrical signal. From this AE signal, AE features such as the maximum amplitude or the frequency can be extracted. Methods of signal analysis are used to investigate the time and frequency dependency of signal groups. The purpose of the signal analysis is to connect the AE signal with the originating AE source. If predefined damage mechanisms are identified, referencing the damage condition of the structure is possible. Acoustic emission from events of the actual crack propagation process can for example lead to the crack growth rate or the stress intensity factor, both specific values from fracture mechanics. A new development in the domain of acoustic emission testing is the pattern recognition of AE signals. Specific features are extracted from the AE signals to assign them to their damage mechanisms. In this thesis the AE signals from the damage mechanisms corrosion and fatigue crack growth are compared and analysed. The damage mechanisms were

  6. Irradiation-assisted stress corrosion cracking behavior of austenitic stainless steels applicable to LWR core internals.

    Energy Technology Data Exchange (ETDEWEB)

    Chung, H. M.; Shack, W. J.; Energy Technology

    2006-01-31

    This report summarizes work performed at Argonne National Laboratory on irradiation-assisted stress corrosion cracking (IASCC) of austenitic stainless steels that were irradiated in the Halden reactor in simulation of irradiation-induced degradation of boiling water reactor (BWR) core internal components. Slow-strain-rate tensile tests in BWR-like oxidizing water were conducted on 27 austenitic stainless steel alloys that were irradiated at 288 C in helium to 0.4, 1.3, and 3.0 dpa. Fractographic analysis was conducted to determine the fracture surface morphology. Microchemical analysis by Auger electron spectroscopy was performed on BWR neutron absorber tubes to characterize grain-boundary segregation of important elements under BWR conditions. At 0.4 and 1.4 dpa, transgranular fracture was mixed with intergranular fracture. At 3 dpa, transgranular cracking was negligible, and fracture surface was either dominantly intergranular, as in field-cracked core internals, or dominantly ductile or mixed. This behavior indicates that percent intergranular stress corrosion cracking determined at {approx}3 dpa is a good measure of IASCC susceptibility. At {approx}1.4 dpa, a beneficial effect of a high concentration of Si (0.8-1.5 wt.%) was observed. At {approx}3 dpa, however, such effect was obscured by a deleterious effect of S. Excellent resistance to IASCC was observed up to {approx}3 dpa for eight heats of Types 304, 316, and 348 steel that contain very low concentrations of S. Susceptibility of Types 304 and 316 steels that contain >0.003 wt.% S increased drastically. This indicates that a sulfur related critical phenomenon plays an important role in IASCC. A sulfur content of <0.002 wt.% is the primary material factor necessary to ensure good resistance to IASCC. However, for Types 304L and 316L steel and their high-purity counterparts, a sulfur content of <0.002 wt.% alone is not a sufficient condition to ensure good resistance to IASCC. This is in distinct contrast to

  7. Irradiation-assisted stress corrosion cracking behavior of austenitic stainless steels applicable to LWR core internals.

    Energy Technology Data Exchange (ETDEWEB)

    Chung, H. M.; Shack, W. J.; Energy Technology

    2006-01-31

    This report summarizes work performed at Argonne National Laboratory on irradiation-assisted stress corrosion cracking (IASCC) of austenitic stainless steels that were irradiated in the Halden reactor in simulation of irradiation-induced degradation of boiling water reactor (BWR) core internal components. Slow-strain-rate tensile tests in BWR-like oxidizing water were conducted on 27 austenitic stainless steel alloys that were irradiated at 288 C in helium to 0.4, 1.3, and 3.0 dpa. Fractographic analysis was conducted to determine the fracture surface morphology. Microchemical analysis by Auger electron spectroscopy was performed on BWR neutron absorber tubes to characterize grain-boundary segregation of important elements under BWR conditions. At 0.4 and 1.4 dpa, transgranular fracture was mixed with intergranular fracture. At 3 dpa, transgranular cracking was negligible, and fracture surface was either dominantly intergranular, as in field-cracked core internals, or dominantly ductile or mixed. This behavior indicates that percent intergranular stress corrosion cracking determined at {approx}3 dpa is a good measure of IASCC susceptibility. At {approx}1.4 dpa, a beneficial effect of a high concentration of Si (0.8-1.5 wt.%) was observed. At {approx}3 dpa, however, such effect was obscured by a deleterious effect of S. Excellent resistance to IASCC was observed up to {approx}3 dpa for eight heats of Types 304, 316, and 348 steel that contain very low concentrations of S. Susceptibility of Types 304 and 316 steels that contain >0.003 wt.% S increased drastically. This indicates that a sulfur related critical phenomenon plays an important role in IASCC. A sulfur content of <0.002 wt.% is the primary material factor necessary to ensure good resistance to IASCC. However, for Types 304L and 316L steel and their high-purity counterparts, a sulfur content of <0.002 wt.% alone is not a sufficient condition to ensure good resistance to IASCC. This is in distinct contrast to

  8. A Global Refiability Assessment Method on Aging Offshore Platforms with Corrosion and Cracks

    Institute of Scientific and Technical Information of China (English)

    JI Chun-yan; LI Shan-shan; CHEN Ming-lu

    2009-01-01

    Corrosion and fatigue cracks are major threats to the structural integrity of aging offshore platforms.For the rational estimation of the safety levels of aging platforms,a global reliability assessment approach for aging offshore platforms with corrosion and fatigue cracks is presented in this paper.The base shear capacity is taken as the global ultimate strength of the offshore plaffoms,it is modeled as a random process that decreases with time in the presence of corrosion and fatigue crack propagation.And the corrosion and fatigue crack growth rates in the main members and key joints are modeled as random variables.A simulation method of the extreme wave loads which are applied to the structures of offshore platforms is proposed too.Furthermore,the statistics of global base shear capacity and extreme wave loads are obtained by Monte Carlo simulation method.On the basis of the limit state equation of global failure mode,the instantaneous reliability and time dependent reliability assessment methods are both presented in this paper.Finally the instantaueous reliability index and time dependent failure probability of a jacket platform are estimated with different ages in the demonstration example.

  9. Modeling of concrete cracking due to corrosion process of reinforcement bars

    Energy Technology Data Exchange (ETDEWEB)

    Bossio, Antonio, E-mail: antonio.bossio@unina.it [Department of Chemical Engineering, Materials and Production, University of Naples “Federico II”, Napoli, Piazzale V. Tecchio 80, I-80125 Italy (Italy); Monetta, Tullio, E-mail: monetta@unina.it [Department of Chemical Engineering, Materials and Production, University of Naples “Federico II”, Napoli, Piazzale V. Tecchio 80, I-80125 Italy (Italy); Bellucci, Francesco, E-mail: bellucci@unina.it [Department of Chemical Engineering, Materials and Production, University of Naples “Federico II”, Napoli, Piazzale V. Tecchio 80, I-80125 Italy (Italy); Lignola, Gian Piero, E-mail: glignola@unina.it [Department of Structures for Engineering and Architecture, University of Naples “Federico II”, Via Claudio 21, I-80125 Napoli (Italy); Prota, Andrea, E-mail: aprota@unina.it [Department of Structures for Engineering and Architecture, University of Naples “Federico II”, Via Claudio 21, I-80125 Napoli (Italy)

    2015-05-15

    The reinforcement corrosion in Reinforced Concrete (RC) is a major reason of degradation for structures and infrastructures throughout the world leading to their premature deterioration before design life was attained. The effects of corrosion of reinforcement are: (i) the reduction of the cross section of the bars, and (ii) the development of corrosion products leading to the appearance of cracks in the concrete cover and subsequent cover spalling. Due to their intrinsic complex nature, these issues require an interdisciplinary approach involving both material science and structural design knowledge also in terms on International and National codes that implemented the concept of durability and service life of structures. In this paper preliminary FEM analyses were performed in order to simulate pitting corrosion or general corrosion aimed to demonstrate the possibility to extend the results obtained for a cylindrical specimen, reinforced by a single bar, to more complex RC members in terms of geometry and reinforcement. Furthermore, a mechanical analytical model to evaluate the stresses in the concrete surrounding the reinforcement bars is proposed. In addition, a sophisticated model is presented to evaluate the non-linear development of stresses inside concrete and crack propagation when reinforcement bars start to corrode. The relationships between the cracking development (mechanical) and the reduction of the steel section (electrochemical) are provided. Finally, numerical findings reported in this paper were compared to experimental results available in the literature and satisfactory agreement was found.

  10. Methodology to evaluate the crack growth rate by stress corrosion cracking in dissimilar metals weld in simulated environment of PWR nuclear reactor

    Energy Technology Data Exchange (ETDEWEB)

    Paula, Raphael G.; Figueiredo, Celia A.; Rabelo, Emerson G., E-mail: raphaelmecanica@gmail.com, E-mail: caf@cdtn.br, E-mail: egr@cdtn.br [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2013-07-01

    Inconel alloys weld metal is widely used to join dissimilar metals in nuclear reactors applications. It was recently observed failures of weld components in plants, which have triggered an international effort to determine reliable data on the stress corrosion cracking behavior of this material in reactor environment. The objective of this work is to develop a methodology to determine the crack growth rate caused by stress corrosion in Inconel alloy 182, using the specimen (Compact Tensile) in simulated PWR environment. (author)

  11. Mechanical factors in primary water stress corrosion cracking of cold-worked stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Hammadi, Rashid Al, E-mail: rashid.alhammadi@fanr.gov.ae [Nuclear Security Division, Federal Authority for Nuclear Regulation, Abu Dhabi (United Arab Emirates); Yi, Yongsun, E-mail: yongsun.yi@kustar.ac.ae [Department of Nuclear Engineering, Khalifa University, Abu Dhabi (United Arab Emirates); Zaki, Wael, E-mail: wael.zaki@kustar.ac.ae [Department of Mechanical Engineering, Khalifa University, Abu Dhabi (United Arab Emirates); Cho, Pyungyeon, E-mail: pyungyeon.cho@kustar.ac.ae [Department of Nuclear Engineering, Khalifa University, Abu Dhabi (United Arab Emirates); Jang, Changheui, E-mail: chjang@kaist.ac.kr [Nuclear and Quantum Engineering Department, Korea Advanced Institute of Science and Technology, Daejeon (Korea, Republic of)

    2016-05-15

    Highlights: • PWSCC of cold-worked austenitic stainless steel was studied. • Finite element analysis was performed on a compact tension specimen. • Mechanical fields near a crack tip were evaluated using FEA. • The dependence of mechanical factors on K{sub I} and yield stress was investigated. • The crack tip normal stress was identified as a main factor controlling PWSCC. - Abstract: Finite element analysis was performed on a compact tension specimen to determine the stress and strain distributions near a crack tip. Based on the results, the crack tip stain rates by crack advance and creep rates near crack tip were estimated. By comparing the dependence of the mechanical factors on the stress intensity factor and yield stress with that of the SCC crack growth rates, it was tried to identify the main mechanical factor for the primary water stress corrosion cracking (PWSCC) of cold-worked austenitic stainless steels. The analysis results showed that the crack tip normal stress could be the main mechanical factor controlling the PWSCC, suggesting that the internal oxidation mechanism might be the most probable PWSCC mechanism of cold-worked austenitic stainless steels.

  12. Cracking process of Fe-26Cr-1Mo during low cycle corrosion fatigue

    Energy Technology Data Exchange (ETDEWEB)

    Wang, J.Q.; Li, J.; Wang, Z.F.; Zhu, Z.Y.; Ke, W. (Academia Sinica, Shenyang (China). Corrosion Science Lab.); Zang, Q.S.; Wang, Z.G. (Academia Sinica, Shenyang (China). State Key Lab. for Fatigue and Fracture of Materials)

    1994-12-01

    The corrosion fatigue (CF) life has been divided classically into the initiation'' and propagation'' periods. Usually, the crack initiation process dominates the component lifetime under the low cycle CF condition because the crack propagates rapidly one initiated. Despite much work done on the research of the CF crack initiation mechanisms, however, a full understanding of crack initiation is still lacking. There are some limitations in explaining the CF crack initiation in an aqueous solution using the above four mechanisms individually. And, it is difficult to conduct experiments in which one mechanism along can be examined. Although CF is complicated, it is possible to reproduce a specific experiment condition which will have the dominant factor affecting the CF crack initiation. Once the cracks initiate on the smooth metal surface, their coalescence, micropropagation and macropropagation will take place successively. The initiated cracks propagate first in the range of several grains, and the behavior of the microcrack propagation is different from that of macrocrack propagation. For Fe-26Cr-1Mo ferritic stainless steel, the fundamental research work of straining electrode has been done by many investigators, but the observation of the material surface at different deformation processes has not been reported. In the present study, the detailed observation of the cracking process of the material has been carried out in low cycle CF.

  13. Stress corrosion crack initiation of alloy 182 weld metal in primary coolant - Influence of chemical composition

    Energy Technology Data Exchange (ETDEWEB)

    Calonne, O.; Foucault, M.; Steltzlen, F. [AREVA (France); Amzallag, C. [EDF SEPTEN (France)

    2011-07-01

    Nickel-base alloys 182 and 82 have been used extensively for dissimilar metal welds. Typical applications are the J-groove welds of alloy 600 vessel head penetrations, pressurizer penetrations, heater sleeves and bottom mounted instrumented nozzles as well as some safe end butt welds. While the overall performance of these weld metals has been good, during the last decade, an increasing number of cases of stress corrosion cracking of Alloy 182 weld metal have been reported in PWRs. In this context, the role of weld defects has to be examined. Their contribution in the crack initiation mechanism requires laboratory investigations with small scale characterizations. In this study, the influence of both alloy composition and weld defects on PWSCC (Stress Corrosion Cracking in Primary Water) initiation was investigated using U-bend specimens in simulated primary water at 320 C. The main results are the following: -) the chemical compositions of the weld deposits leading to a large propensity to hot cracking are not the most susceptible to PWSCC initiation, -) macroscopically, superficial defects did not evolve during successive exposures. They can be included in large corrosion cracks but their role as 'precursors' is not yet established. (authors)

  14. Role of pH on the stress corrosion cracking of titanium alloys

    Science.gov (United States)

    Khokhar, M. I.; Beck, F. H.; Fontana, M. G.

    1973-01-01

    Stress corrosion cracking (SCC) experiments were conducted on Ti-8-1-1 wire specimens in hydrochloric and sulfuric acids of variable pH in order to determine the effect of pH on the susceptibility to cracking. The alloy exhibited increasing susceptibility with decreasing pH. By varying the applied potential, it was observed that susceptibility zones exist both in the cathodic and the anodic ranges. In the cathodic range, susceptibility also increased with decreasing applied potential. Corrosion potential-time data in hydrochloric acid (pH 1.7) and sulfuric acid (pH 1.7) indicate that chloride ions lower the corrosion potential of the specimen which, in turn, increases the susceptibility.

  15. Role of pH on the stress corrosion cracking of titanium alloys

    Science.gov (United States)

    Khokhar, M. I.; Beck, F. H.; Fontana, M. G.

    1973-01-01

    Stress corrosion cracking (SCC) experiments were conducted on Ti-8-1-1 wire specimens in hydrochloric and sulfuric acids of variable pH in order to determine the effect of pH on the susceptibility to cracking. The alloy exhibited increasing susceptibility with decreasing pH. By varying the applied potential, it was observed that susceptibility zones exist both in the cathodic and the anodic ranges. In the cathodic range, susceptibility also increased with decreasing applied potential. Corrosion potential-time data in hydrochloric acid (pH 1.7) and sulfuric acid (pH 1.7) indicate that chloride ions lower the corrosion potential of the specimen which, in turn, increases the susceptibility.

  16. Parameters influencing the transgranular stress corrosion cracking behaviour of austenitic stainless steels in systems conveying reactor coolant

    Energy Technology Data Exchange (ETDEWEB)

    Kilian, R.; Wesseling, U. [Framatome ANP (Germany); Wachter, O. [E.ON Kernkraft (Germany); Widera, M. [RWE Power (Germany); Brummer, G. [HEW - (Germany); Ilg, U. [EnBW - (Germany)

    2002-07-01

    During replacement of an auxiliary system in the German PWR KKS (NPP Stade) a damage was detected in a valve housing and in the connected piping both made from stabilised austenitic stainless steel. During operation stagnant conditions are present in this area. Based on the failure analysis chloride induced stress corrosion cracking (SCC) was found as the dominating root cause. In the open literature many cases of corrosion observed in the water/steam interface in valve components as well as in adjacent portions of auxiliary circuits made of un-stabilized stainless steels are mentioned. A common feature of the reported cases is that transgranular cracking was found. Extensive laboratory investigations revealed that non-stabilised austenitic stainless steels are also sensitive to transgranular cracking in boric acid solutions particularly in concentrated solutions. Often these solutions are contaminated with chlorides and/or oxygen is present. Taking into account the literature data the question could arise whether the above mentioned cracking may be also caused by boric acid attack. Thus, for stabilised stainless steels laboratory exposure tests at 80 C in saturated aerated boric acid solution and at 300 C in (at 100 C) saturated, oxygen free boric acid solution have been performed. Double-U-bend specimens and wedge loaded 1T-CT specimens made of Ti- and Nb-stabilised austenitic stainless steels were used. The results revealed no evidence of crack initiation and crack growth. Based on the laboratory results and the literature data an attempt is undertaken to separate parameters influencing chloride induced SCC from the effect of boric acid. (authors)

  17. A Fundamental study of remedial technology development to prevent stress corrosion cracking of steam generator tubing

    Energy Technology Data Exchange (ETDEWEB)

    Park, In Gyu; Lee, Chang Soon [Sunmoon University, Asan (Korea)

    1998-04-01

    Most of the PWR Steam generators with tubes in Alloy 600 alloy are affected by Stress Corrosion Cracking, such as PWSCC(Primary Water Stress Corrosion Cracking) and ODSCC(Outside Diameter Stress Corrosion Cracking). This study was undertaken to establish the background for remedial technology development to prevent SCC. in the report are included the following topics: (1) General: (i) water chemistry related factors, (ii) Pourbaix(Potential-pH) Diagram, (iii) polarization plot, (iv) corrosion mode of Alloy 600, 690, and 800, (v) IGA/SCC growth rate, (vi) material suspetibility of IGA/SCC, (vii) carbon solubility of Alloy 600 (2) Microstructures of Alloy 600 MA, Alloy 600 TT, Alloy 600 SEN Alloy 690 TT(Optical, SEM, and TEM) (3) Influencing factors for PWSCC initiation rate of Alloy 600: (i) microstructure, (ii) water chemistry(B, Li), (iii) temperature, (iv) plastic deformation, (v) stress relief annealing (4) Influencing factors for PWSCC growth rate of Alloy 600: (i) water chemistry(B, Li), (ii) Scott Model, (iii) intergranular carbide, (iv) temperature, (v) hold time (5) Laboratory conditions for ODSCC initiation rate: 1% NaOH, 316 deg C; 1% NaOH, 343 deg C; 50% NaOH, 288 deg C; 10% NaOH, 302 deg C; 10% NaOH, 316 deg C; 50% NaOH, 343 deg C (6) Sludge effects for ODSCC initiation rate: CuO, Cr{sub 2}O{sub 3}, Fe{sub 3}O{sub 4} (7) Influencing factors for PWSCC growth rate of Alloy 600: (i) Caustic concentration effect, (ii) carbonate addition effect (8) Sulfate corrosion: (i) sulfate ratio and pH effect, (ii) wastage rate of Alloy 600 and Alloy 690 (9) Crevice corrosion: (i) experimental setup for crevice corrosion, (ii) organic effect, (iii) (Na{sub 2}SO{sub 4} + NaOH) effect (10) Remedial measures for SCC: (i) Inhibitors, (ii) ZnO effect. (author). 30 refs., 174 figs., 51 tabs.

  18. Electrochemical and Sulfide Stress Corrosion Cracking Behaviors of Tubing Steels in a H2S/CO2 Annular Environment

    Science.gov (United States)

    Liu, Z. Y.; Wang, X. Z.; Liu, R. K.; Du, C. W.; Li, X. G.

    2014-04-01

    The electrochemical and sulfide stress corrosion cracking (SSCC) behaviors of 13Cr stainless steel and P110 steel were investigated in a simulated acidic annular environment with low-temperature and high-pressure H2S/CO2 using electrochemical methods, U-bend immersion tests, and scanning electron microscopy. In the solution containing high pressure CO2, 13Cr, and P110 steels exhibited general corrosion and severe pitting, respectively. Compared with sweet corrosion, additional H2S in the solution enhanced the corrosion of 13Cr steel but inhibited the corrosion of P110 steel. By contrast, in a solution containing 4 MPa CO2 and different (0-0.3 MPa), the susceptibility of both 13Cr stainless steel and P110 steel toward SSCC was significantly promoted by increases in H2S partial pressure. The 13Cr stainless steel exhibited higher susceptibility toward SSCC than P110 steel under a H2S/CO2 environment but lower susceptibility under a pure CO2 environment.

  19. Use of electrochemical potential noise to detect initiation and propagation of stress corrosion cracks in a 17-4 PH steel

    Energy Technology Data Exchange (ETDEWEB)

    Gonzalez-Rodriguez, J.G. [UAEM, Cuernavaca (Mexico); Salinas-Bravo, V.M.; Garcia-Ochoa, E. [Inst. de Investigaciones Electricas, Temixco (Mexico). Dept. de Fisicoquimica Aplicada; Diaz-Sanchez, A. [Inst. Nacional de Investigaciones Nucleares, Toluca (Mexico). Dept. de Materiales

    1997-09-01

    Corrosion potential transients were associated with nucleation and propagation of stress corrosion cracks in a 17-4 precipitation-hardenable (PH) martensitic stainless steel (SS) during slow strain rate tests (SSRT) at 90 C in deaerated sodium chloride (NaCl) solutions, Test solutions included 20 wt% NaCl at pH 3 and 7, similar to normal and faulted steam turbine environments, respectively. Time series were analyzed using the fast Fourier transform method. At the beginning of straining, the consistent noise behavior was perturbed with small potential transients, probably associated with rupture of the surface oxide layer. After yielding, these transients increased in intensity. At maximum load, the transients were still higher in intensity and frequency. These potential transients were related to crack nucleation and propagation. When the steel did not fail by stress corrosion cracking (SCC), such transients were found only at the beginning of the test. The power spectra showed some differences in all cases in roll-off slope and voltage magnitude, but these were not reliable tools to monitor the initiation and propagation of stress corrosion cracks.

  20. Standard Test Method for Sandwich Corrosion Test

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2009-01-01

    1.1 This test method defines the procedure for evaluating the corrosivity of aircraft maintenance chemicals, when present between faying surfaces (sandwich) of aluminum alloys commonly used for aircraft structures. This test method is intended to be used in the qualification and approval of compounds employed in aircraft maintenance operations. 1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information. 1.3 This standard may involve hazardous materials, operations, and equipment. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Specific hazard statements appear in Section 9.

  1. Uncertainty Evaluation of Weibull Estimators through Monte Carlo Simulation: Applications for Crack Initiation Testing

    Directory of Open Access Journals (Sweden)

    Jae Phil Park

    2016-06-01

    Full Text Available The typical experimental procedure for testing stress corrosion cracking initiation involves an interval-censored reliability test. Based on these test results, the parameters of a Weibull distribution, which is a widely accepted crack initiation model, can be estimated using maximum likelihood estimation or median rank regression. However, it is difficult to determine the appropriate number of test specimens and censoring intervals required to obtain sufficiently accurate Weibull estimators. In this study, we compare maximum likelihood estimation and median rank regression using a Monte Carlo simulation to examine the effects of the total number of specimens, test duration, censoring interval, and shape parameters of the true Weibull distribution on the estimator uncertainty. Finally, we provide the quantitative uncertainties of both Weibull estimators, compare them with the true Weibull parameters, and suggest proper experimental conditions for developing a probabilistic crack initiation model through crack initiation tests.

  2. Electro chemical studies on stress corrosion cracking of Incoloy-800 in caustic solution, part I: As received samples

    Directory of Open Access Journals (Sweden)

    Dinu Alice

    2005-01-01

    Full Text Available Many non-volatile impurities accidentally introduced into the steam generator tend to Concentrate on its surface in restricted flow areas. In this way these impurities can lead to stress corrosion cracking (SCC on stressed tubes of the steam generator. Such impurities can be strong alkaline or acid solutions. To evaluate the effect of alkaline concentrated environments on SCC of steam generator tubes, the tests were con ducted on stressed samples of Incoloy-800 in 10% NaOH solution. To accelerate the SCC process, stressed specimens were anodically polarised in a caustic solution in an electro chemical cell. The method of stressing of Incoloy-800 tubes used in our experiments was the C-ring. Using the cathodic zone of the potentiodynamic curves it was possible to calculate the most important electrochemical parameters: the corrosion current, the corrosion rate, and the polarization resistance. We found that the value of the corrosion potential to initiate the SCC microcracks was -100 mV. The tested samples were examined using the metallographic method. The main experimental results showed that the in crease of the stress state promoted the in crease of the SCC susceptibility of Incoloy-800 samples tested under the same conditions, and that the length of the SCC-type microcracks in creased with the growth of the stress value.

  3. Uncertainty quantification methodologies development for stress corrosion cracking of canister welds

    Energy Technology Data Exchange (ETDEWEB)

    Dingreville, Remi Philippe Michel [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Bryan, Charles R. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)

    2016-09-30

    This letter report presents a probabilistic performance assessment model to evaluate the probability of canister failure (through-wall penetration) by SCC. The model first assesses whether environmental conditions for SCC – the presence of an aqueous film – are present at canister weld locations (where tensile stresses are likely to occur) on the canister surface. Geometry-specific storage system thermal models and weather data sets representative of U.S. spent nuclear fuel (SNF) storage sites are implemented to evaluate location-specific canister surface temperature and relative humidity (RH). As the canister cools and aqueous conditions become possible, the occurrence of corrosion is evaluated. Corrosion is modeled as a two-step process: first, pitting is initiated, and the extent and depth of pitting is a function of the chloride surface load and the environmental conditions (temperature and RH). Second, as corrosion penetration increases, the pit eventually transitions to a SCC crack, with crack initiation becoming more likely with increasing pit depth. Once pits convert to cracks, a crack growth model is implemented. The SCC growth model includes rate dependencies on both temperature and crack tip stress intensity factor, and crack growth only occurs in time steps when aqueous conditions are predicted. The model suggests that SCC is likely to occur over potential SNF interim storage intervals; however, this result is based on many modeling assumptions. Sensitivity analyses provide information on the model assumptions and parameter values that have the greatest impact on predicted storage canister performance, and provide guidance for further research to reduce uncertainties.

  4. Stress Corrosion Cracking in Al-Zn-Mg-Cu Aluminum Alloys in Saline Environments

    Science.gov (United States)

    Holroyd, N. J. Henry; Scamans, G. M.

    2013-03-01

    Stress corrosion cracking of Al-Zn-Mg-Cu (AA7xxx) aluminum alloys exposed to saline environments at temperatures ranging from 293 K to 353 K (20 °C to 80 °C) has been reviewed with particular attention to the influences of alloy composition and temper, and bulk and local environmental conditions. Stress corrosion crack (SCC) growth rates at room temperature for peak- and over-aged tempers in saline environments are minimized for Al-Zn-Mg-Cu alloys containing less than ~8 wt pct Zn when Zn/Mg ratios are ranging from 2 to 3, excess magnesium levels are less than 1 wt pct, and copper content is either less than ~0.2 wt pct or ranging from 1.3 to 2 wt pct. A minimum chloride ion concentration of ~0.01 M is required for crack growth rates to exceed those in distilled water, which insures that the local solution pH in crack-tip regions can be maintained at less than 4. Crack growth rates in saline solution without other additions gradually increase with bulk chloride ion concentrations up to around 0.6 M NaCl, whereas in solutions with sufficiently low dichromate (or chromate), inhibitor additions are insensitive to the bulk chloride concentration and are typically at least double those observed without the additions. DCB specimens, fatigue pre-cracked in air before immersion in a saline environment, show an initial period with no detectible crack growth, followed by crack growth at the distilled water rate, and then transition to a higher crack growth rate typical of region 2 crack growth in the saline environment. Time spent in each stage depends on the type of pre-crack ("pop-in" vs fatigue), applied stress intensity factor, alloy chemistry, bulk environment, and, if applied, the external polarization. Apparent activation energies ( E a) for SCC growth in Al-Zn-Mg-Cu alloys exposed to 0.6 M NaCl over the temperatures ranging from 293 K to 353 K (20 °C to 80 °C) for under-, peak-, and over-aged low-copper-containing alloys (alloys (>~0.8 wt pct), they are typically

  5. Stress Corrosion Cracking Behavior of Multipass TIG-Welded AA2219 Aluminum Alloy in 3.5 wt pct NaCl Solution

    Science.gov (United States)

    Venugopal, A.; Sreekumar, K.; Raja, V. S.

    2012-09-01

    The stress corrosion cracking (SCC) behavior of the AA2219 aluminum alloy in the single-pass (SP) and multipass (MP) welded conditions was examined and compared with that of the base metal (BM) in 3.5 wt pct NaCl solution using a slow-strain-rate technique (SSRT). The reduction in ductility was used as a parameter to evaluate the SCC susceptibility of both the BM and welded joints. The results showed that the ductility ratio ( ɛ NaCl/( ɛ air) was 0.97 and 0.96, respectively, for the BM and MP welded joint, and the same was marginally reduced to 0.9 for the SP welded joint. The fractographic examination of the failed samples revealed a typical ductile cracking morphology for all the base and welded joints, indicating the good environmental cracking resistance of this alloy under all welded conditions. To understand the decrease in the ductility of the SP welded joint, preexposure SSRT followed by microstructural observations were made, which showed that the decrease in ductility ratio of the SP welded joint was caused by the electrochemical pitting that assisted the nucleation of cracks in the form of corrosion induced mechanical cracking rather than true SCC failure of the alloy. The microstructural examination and polarization tests demonstrated a clear grain boundary (GB) sensitization of the PMZ, resulting in severe galvanic corrosion of the SP weld joint, which initiated the necessary conditions for the localized corrosion and cracking along the PMZ. The absence of PMZ and a refined fusion zone (FZ) structure because of the lesser heat input and postweld heating effect improved the galvanic corrosion resistance of the MP welded joint greatly, and thus, failure occurred along the FZ.

  6. Modeling of Stress Corrosion Cracking for High Level Radioactive-Waste Packages

    Energy Technology Data Exchange (ETDEWEB)

    Lu, S C; Gordon, G M; Andresen, P L; Herrera, M L

    2003-06-20

    A stress corrosion cracking (SCC) model has been adapted for performance prediction of high level radioactive-waste packages to be emplaced in the proposed Yucca Mountain radioactive-waste repository. SCC is one form of environmentally assisted cracking due to three factors, which must be present simultaneously: metallurgical susceptibility, critical environment, and static (or sustained) tensile stresses. For waste packages of the proposed Yucca Mountain repository, the outer barrier material is Alloy 22, a highly corrosion resistant alloy, the environment is represented by the water film present on the surface of the waste package from dripping or deliquescence of soluble salts present in any surface deposits, and the stress is principally the weld induced residual stress. SCC has historically been separated into ''initiation'' and ''propagation'' phases. Initiation of SCC will not occur on a smooth surface if the surface stress is below a threshold value defined as the threshold stress. Cracks can also initiate at and propagate from flaws (or defects) resulting from manufacturing processes (such as welding). To account for crack propagation, the slip dissolution/film rupture (SDFR) model is adopted to provide mathematical formulas for prediction of the crack growth rate. Once the crack growth rate at an initiated SCC is determined, the time to through-wall penetration for the waste package can be calculated. The SDFR model relates the advance (or propagation) of cracks, subsequent to the crack initiation from bare metal surface, to the metal oxidation transients that occur when the protective film at the crack tip is continually ruptured and repassivated. A crack, however, may reach the ''arrest'' state before it enters the ''propagation'' phase. There exists a threshold stress intensity factor, which provides a criterion for determining if an initiated crack or pre

  7. Statistical model of stress corrosion cracking based on extended form of Dirichlet energy

    Indian Academy of Sciences (India)

    Harry Yosh

    2013-12-01

    The mechanism of stress corrosion cracking (SCC) has been discussed for decades. Here I propose a model of SCC reflecting the feature of fracture in brittle manner based on the variational principle under approximately supposed thermal equilibrium. In that model the functionals are expressed with extended forms of Dirichlet energy, and Dirichlet principle is applied to them to solve the variational problem that represents SCC and normal extension on pipe surface. Based on the model and the maximum entropy principle, the statistical nature of SCC colony is discussed and it is indicated that the crack has discrete energy and length under ideal isotropy of materials and thermal equilibrium.

  8. Fatigue Crack Extension Model of Aluminium Alloy with Prior Corrosion Damage Based on Localised Corrosion Damage%基于局部腐蚀损伤的铝合金预腐蚀疲劳裂纹扩展模型

    Institute of Scientific and Technical Information of China (English)

    孔光明; 李旭东; 穆志韬

    2014-01-01

    目的:建立铝合金预腐蚀疲劳裂纹扩展模型。方法采用表征局部环境腐蚀损伤影响程度的参数孔蚀率对腐蚀疲劳裂纹扩展速率进行修正。结果修正后的腐蚀铝合金试件的疲劳裂纹扩展速率与试验结果吻合程度良好。结论修正后的铝合金预腐蚀疲劳裂纹扩展速率模型合理有效,试验数据和预测模型可为海军飞机结构的损伤容限设计提供参考。%Objective To establish a modified model for pre-corrosion fatigue crack growth rate of aluminum alloy. Methods Considering that the local damage around the crack tip was more reasonable for accelerating crack growth rate in corrosive environment, the pitting rate, which was a parameter characterizing the influence of corrosion in local environ-ment, was used to correct the corrosion fatigue crack growth rate. Results The experimental results were in good agreement with predictions of the amended fatigue crack growth rate model for corroded aluminum alloy specimens. Conclusion The corrected aluminum alloy pre-corrosion fatigue crack growth rate model was reasonable and effective, and the test data and the prediction model could provide a reference for the damage tolerance design of navy aircraft structure.

  9. Accelerated corrosion test and corrosion failure distribution model of aircraft structural aluminum alloy

    Institute of Scientific and Technical Information of China (English)

    LIU Wen-lin; MU Zhi-tao; JIN Ping

    2006-01-01

    Based on corrosion damage data of 10 years for a type of aircraft aluminum alloy, the statistical analysis was conducted by Gumbel, Normal and two parameters Weibull distribution function. The results show that aluminum alloy structural member has the corrosion history of pitting corrosion-intergranular corrosion-exfoliation corrosion, and the maximum corrosion depth is in conformity to normal distribution. The accelerated corrosion test was carried out with the complied equivalent airport accelerated environment spectrum. The corrosion damage failure modes of aluminum alloy structural member indicate that the period of validity of the former protective coating is about 2.5 to 3 years, and that of the novel protective coating is about 4.0 to 4.5 years. The corrosion kinetics law of aluminum spar flange was established by fitting corrosion damage test data. The law indicates two apparent corrosion stages of high strength aluminum alloy section material: pitting corrosion and intergranular corrosion/exfoliation corrosion.The test results agree with the statistical fit result of corrosion data collected from corrosion member in service. The fractional error is 5.8% at the same calendar year. The accelerated corrosion test validates the corrosion kinetics law of aircraft aluminum alloy in service.

  10. 49 CFR 192.929 - What are the requirements for using Direct Assessment for Stress Corrosion Cracking (SCCDA)?

    Science.gov (United States)

    2010-10-01

    ... requirements for using Direct Assessment for Stress Corrosion Cracking (SCCDA)? (a) Definition. Stress..., appendix A3, and remediate the threat in accordance with ASME/ANSI B31.8S, appendix A3, section A3.4....

  11. Standard test method for creep-fatigue crack growth testing

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2010-01-01

    1.1 This test method covers the determination of creep-fatigue crack growth properties of nominally homogeneous materials by use of pre-cracked compact type, C(T), test specimens subjected to uniaxial cyclic forces. It concerns fatigue cycling with sufficiently long loading/unloading rates or hold-times, or both, to cause creep deformation at the crack tip and the creep deformation be responsible for enhanced crack growth per loading cycle. It is intended as a guide for creep-fatigue testing performed in support of such activities as materials research and development, mechanical design, process and quality control, product performance, and failure analysis. Therefore, this method requires testing of at least two specimens that yield overlapping crack growth rate data. The cyclic conditions responsible for creep-fatigue deformation and enhanced crack growth vary with material and with temperature for a given material. The effects of environment such as time-dependent oxidation in enhancing the crack growth ra...

  12. SCREENING TESTS FOR IMPROVED METHANE CRACKING MATERIALS

    Energy Technology Data Exchange (ETDEWEB)

    Klein, J; Jeffrey Holder, J

    2007-07-16

    Bench scale (1 to 6 gram) methane cracking tests have been performed on a variety of pure elements, some alloys, and SAES{reg_sign} commercial getters St 101, St 198, St 707, St 737, and St 909 to determine methane cracking performance (MCP) of 5% methane in a helium carrier at 700 C, 101.3 kPa (760 torr) with a 10 sccm feed. The MCP was almost absent from some materials tested while others showed varying degrees of MCP. Re, Cr, V, Gd, and Mo powders had good MCP, but limited capacities. Nickel supported on kieselguhr (Ni/k), a Zr-Ni alloy, and the SAES{reg_sign} getters had good MCP in a helium carrier. The MCP of these same materials was suppressed in a hydrogen carrier stream and the MCP of the Zr-based materials was reduced by nitride formation when tested with a nitrogen carrier gas.

  13. An Industrial Perspective on Environmentally Assisted Cracking of Some Commercially Used Carbon Steels and Corrosion-Resistant Alloys

    Science.gov (United States)

    Ashida, Yugo; Daigo, Yuzo; Sugahara, Katsuo

    2017-08-01

    Commercial metals and alloys like carbon steels, stainless steels, and nickel-based super alloys frequently encounter the problem of environmentally assisted cracking (EAC) and resulting failure in engineering components. This article aims to provide a perspective on three critical industrial applications having EAC issues: (1) corrosion and cracking of carbon steels in automotive applications, (2) EAC of iron- and nickel-based alloys in salt production and processing, and (3) EAC of iron- and nickel-based alloys in supercritical water. The review focuses on current industrial-level understanding with respect to corrosion fatigue, hydrogen-assisted cracking, or stress corrosion cracking, as well as the dominant factors affecting crack initiation and propagation. Furthermore, some ongoing industrial studies and directions of future research are also discussed.

  14. Literature Survey on the Stress Corrosion Cracking of Low-Alloy Steels in High Temperature Water

    Energy Technology Data Exchange (ETDEWEB)

    Seifert, H.P

    2002-02-01

    The present report is a summary of a literature survey on the stress corrosion cracking (SCC) behaviour/ mechanisms in low-alloy steels (LAS) in high-temperature water with special emphasis to primary-pressure-boundary components of boiling water reactors (BWR). A brief overview on the current state of knowledge concerning SCC of low-alloy reactor pressure vessel and piping steels under BWR conditions is given. After a short introduction on general aspects of SCC, the main influence parameter and available quantitative literature data concerning SCC of LAS in high-temperature water are discussed on a phenomenological basis followed by a summary of the most popular SCC models for this corrosion system. The BWR operating experience and service cracking incidents are discussed with respect to the existing laboratory data and background knowledge. Finally, the most important open questions and topics for further experimental investigations are outlined. (author)

  15. Crack Initiation and Growth Behavior at Corrosion Pit in 7075-T6 High Strength Aluminum Alloy

    Science.gov (United States)

    2013-06-01

    was not used to measure the transition from corrosion pit to long crack [25]. . . . . . . . . . . 22 3.1 Composition of a typical sample of 7075 -T6...lives. 24 III. Methodology 3.1 Material Research was conducted using 7075 -T6 aluminum. This alloy is commonly used in aerospace applications and as a... material properties of this alloy. It is important to note that these properties were also used in all finite element models. Table 3.1: Composition of

  16. The influence of loading on the corrosion of steel in cracked ordinary Portland cement and high performance concretes

    Science.gov (United States)

    Jaffer, Shahzma Jafferali

    Most studies that have examined chloride-induced corrosion of steel in concrete have focused on sound concrete. However, reinforced concrete is seldom uncracked and very few studies have investigated the influence of cracked concrete on rebar corrosion. Furthermore, the studies that have examined the relationship between cracks and corrosion have focused on unloaded or statically loaded cracks. However, in practice, reinforced concrete structures (e.g. bridges) are often dynamically loaded. Hence, the cracks in such structures open and close which could influence the corrosion of the reinforcing steel. Consequently, the objectives of this project were (i) to examine the effect of different types of loading on the corrosion of reinforcing steel, (ii) the influence of concrete mixture design on the corrosion behaviour and (iii) to provide data that can be used in service-life modelling of cracked reinforced concretes. In this project, cracked reinforced concrete beams made with ordinary Portland cement concrete (OPCC) and high performance concrete (HPC) were subjected to no load, static loading and dynamic loading. They were immersed in salt solution to just above the crack level at their mid-point for two weeks out of every four (wet cycle) and, for the remaining two weeks, were left in ambient laboratory conditions to dry (dry cycle). The wet cycle led to three conditions of exposure for each beam: (i) the non-submerged region, (ii) the sound, submerged region and (iii) the cracked mid-section, which was also immersed in the solution. Linear polarization resistance and galvanostatic pulse techniques were used to monitor the corrosion in the three regions. Potentiodynamic polarization, electrochemical current noise and concrete electrical resistance measurements were also performed. These measurements illustrated that (i) rebar corroded faster at cracks than in sound concrete, (ii) HPC was more protective towards the rebar than OPCC even at cracks and (iii) there

  17. Study on Localized Corrosion Cracking of Alloy 600 using EN-DCPD Technique

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Yeonju; Kim, Sungwoo; Kim, Hongpyo; Hwang, Seongsik [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2013-02-15

    The object of this work is to establish an electrochemical noise(EN) measurement technique combined with a direct current potential drop(DCPD) method for monitoring of localized corrosion cracking of nickel-based alloy, and to analyze its mechanism. The electrochemical current and potential noises were measured under various conditions of applied stress to a compact tension specimen in a simulated primary water chemistry of a pressurized water reactor. The amplitude and frequency of the EN signals were evaluated in both time and frequency domains based on a shot noise theory, and then quantitatively analyzed using statistical Weibull distribution function. From the spectral analysis, the effect of the current application in DCPD was found to be effectively excluded from the EN signals generated from the localized corrosion cracking. With the aid of a microstructural analysis, the relationship between EN signals and the localized corrosion cracking mechanism was investigated by comparing the shape parameter of Weibull distribution of a mean time-to-failure.

  18. Stress corrosion cracking susceptibility of a high strength Mg-7%Gd-5%Y-1%Nd-0.5%Zr alloy

    Directory of Open Access Journals (Sweden)

    S.D. Wang

    2014-12-01

    Full Text Available Through performing the tensile tests with different strain rates in 3.5 wt.% NaCl solution, the stress corrosion cracking (SCC behavior and the effect of strain rate on the SCC susceptibility of an extruded Mg-7%Gd-5%Y-1%Nd-0.5%Zr (EW75 alloy have been investigated. Results demonstrate that the alloy is susceptible to SCC when the strain rate is lower than 5 × 10−6 s−1. At the strain rate of 1 × 10−6 s−1, the SCC susceptibility index (ISCC is 0.96 and the elongation-to-failure (εf is only 0.11%. Fractography indicates that the brittle quasi-cleavage feature is very obvious and become more pronounced with decreasing the strain rate. Further analysis confirms that the cracking mode is predominantly transgranular, but the partial intergranular cracking at some localized area can also occur. Meanwhile, it seems that the crack propagation path is unrelated to the existing phase particles.

  19. Stress Corrosion Crack Growth Behavior of Titanium Alloy/Bioactive Glasses Sandwiches in Simulated Human Physiological Environment

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    Based on a series of newly developed bioactive glasses having suitable thermo-mechanical properties to allow application as fixation agents between bone and titanium alloy biomedical implants, the stress corrosion crack growth(SCCG) behavior of their interfaces with Ti6Al4V was investigated in simulated body fluid (SBF) with the objectiveof discerning the salient mechanisms of crack advance and to assess the reliability of the bonds. Results indicatedthat crack growth rates in Ti6Al4V/glass/Ti6Al4V sandwich specimens were nearly the same as or slightly lowerthan those in the bulk glasses at comparable stress intensities; indeed, cracks would prefer to propagate off theinterface, suggesting that the Ti6Al4V/glass interface has relatively good crack-growth resistance. Mechanistically,interfacial crack growth appears to be controlled by the classic stress corrosion mechanisms for silicate glasses, withno discernible effect of bioactivity on the SCCG behavior being observed.

  20. Preliminary study for extension and improvement on modeling of primary water stress corrosion cracking at control rod drive mechanism nozzles of pressurized water reactors

    Energy Technology Data Exchange (ETDEWEB)

    Aly, Omar F.; Mattar Neto, Miguel M. [Instituto de Pesquisas Energeticas e Nucleares (IPEN-CNEN/SP), Sao Paulo, SP (Brazil)], e-mail: ofaly@ipen.br, e-mail: mmattar@ipen.br; Schvartzman, Monica M.M.A.M. [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN), Belo Horizonte, MG (Brazil)], e-mail: monicas@cdtn.br

    2009-07-01

    This study is for to extend, to improve the existing models, and to propose a local approach to assess the primary water stress corrosion cracking in nickel-based components. It is includes a modeling of new data for Alloy 182 and new considerations about initiation and crack growth according a developing method based on EPRI-MRP-115 (2004), and USNRC NUREG/CR-6964 (2008). The experimental data is obtained from CDTN-Brazilian Nuclear Technology Development Center, by tests through slow strain rate test (SSRT) equipment. The model conception assumed is a built diagram which indicates a thermodynamic condition for the occurrence of corrosion submodes in essayed materials, through Pourbaix diagrams, for Nickel Alloys in high temperature primary water. Over them, are superimposed different models, including a semi-empiric-probabilistic one to quantify the primary water stress corrosion cracking susceptibility, and a crack growth model. These constructed models shall be validated with the experimental data. This development aims to extent some of the models obtained to weld metals like the Alloy 182, and to improve the originals obtained according methodologies exposed in above referred reports. These methodologies comprise laboratory testing procedures, data collecting, data screening, modeling procedures, assembling of data from some laboratories in the world, plotting of results, compared analysis and discussion of these results. Preliminary results for Alloy 182 will be presented. (author)

  1. Corrosion Control Test Method for Avionic Components

    Science.gov (United States)

    1981-09-25

    Oelionstration and Corrosion Tests Documnentation Task 1 Task 2k3 3 Tent Methods 3 Test Methods 2 Test Methods FIgure 1program Plan 2 NADC 81174-60 04 L...per 10 cubic foot of uhamber velume every 24 hours. The solution is atomized by compressed air humidified by bubbling through 115*F distilled water

  2. Effect of layerwise structural inhomogeneity on stress- corrosion cracking of steel tubes

    Science.gov (United States)

    Perlovich, Yu A.; Krymskaya, O. A.; Isaenkova, M. G.; Morozov, N. S.; Fesenko, V. A.; Ryakhovskikh, I. V.; Esiev, T. S.

    2016-04-01

    Based on X-ray texture and structure analysis data of the material of main gas pipelines it was shown that the layerwise inhomogeneity of tubes is formed during their manufacturing. The degree of this inhomogeneity affects on the tendency of tubes to stress- corrosion cracking under exploitation. Samples of tubes were cut out from gas pipelines located under various operating conditions. Herewith the study was conducted both for sections with detected stress-corrosion defects and without them. Distributions along tube wall thickness for lattice parameters and half-width of X-ray lines were constructed. Crystallographic texture analysis of external and internal tube layers was also carried out. Obtained data testifies about considerable layerwise inhomogeneity of all samples. Despite the different nature of the texture inhomogeneity of gas pipeline tubes, the more inhomogeneous distribution of texture or structure features causes the increasing of resistance to stress- corrosion. The observed effect can be explained by saturation with interstitial impurities of the surface layer of the hot-rolled sheet and obtained therefrom tube. This results in rising of lattice parameters in the external layer of tube as compared to those in underlying metal. Thus, internal layers have a compressive effect on external layers in the rolling plane that prevents cracks opening at the tube surface. Moreover, the high mutual misorientation of grains within external and internal layers of tube results in the necessity to change the moving crack plane, so that the crack growth can be inhibited when reaching the layer with a modified texture.

  3. The role of local strains from prior cold work on stress corrosion cracking

    Science.gov (United States)

    Ulaganathan, Jaganathan

    Several studies have recently reported that cold working exacerbates stress corrosion cracking (SCC) of materials in various environments, including those in which they were previously thought to be immune. While these studies usually consider cold work as a homogeneous effect, the presence of grain boundaries results in local strain concentrations that are inhomogeneously distributed within the microstructure. In order to understand the underlying mechanisms by which the local strains generated by cold work influences SCC, α-brass and Alloy 600 were used in this study. The microscopic changes in the local strains caused by cold work and by SCC were measured using electron backscatter diffraction (EBSD) and polychromatic X-ray microdiffraction (PXM). While the plastic strains were qualitatively expressed through the local misorientation calculated from the orientation data measured by both EBSD and PXM, the elastic strains were determined from the Laue patterns measured by PXM. The interaction between the local strains, and the crack initiation and propagation during SCC was studied by comparing the strain distribution from the same area measured before cold work, after cold work, and again after SCC. In this way, apart from obtaining insights on the interaction, the relative importance of pre-existing strain concentrations and those created by crack propagation can be identified. Additionally, statistical analysis of the EBSD data from uncracked and cracked grain boundaries in Alloy 600 showed the susceptibility of the boundaries to increase when they were surrounded by high local strain concentrations and when the grains sharing the boundary had similar deformation tendency, but to be independent of the grain boundary angle. Finally, one of the contributors for the changes in the strain distribution during SCC can be the corrosion process itself which was examined by intermittently measuring the changes in local strains caused by intergranular corrosion on an

  4. Intergranular stress corrosion cracking of type 304 stainless steels treated with inhibitive chemicals in high temperature pure water

    Energy Technology Data Exchange (ETDEWEB)

    Yeh, T.K. [Nuclear Science and Technology Development Center, National Tsing-Hua Univ. Taiwan (China); Lee, M.Y.; Tsai, C.H. [Department of Engineering and System Science, National Tsing-Hua Univ. Taiwan (China)

    2002-07-01

    Electrochemical potentiodynamic polarizations, electrochemical corrosion potential (ECP) measurements and slow strain rate tensile (SSRT) tests were conducted to investigate the intergranular stress corrosion cracking (IGSCC) characteristics of Type 304 stainless steels treated with inhibitive chemicals in simulated boiling water reactor (BWR) environments. A number of thermally sensitized specimens were prepared and were pre-oxidized in a 288 C environment with the presence of 300 ppb dissolved oxygen for 360 hours. Most of the specimens were then treated with various chemicals including powdered zirconium oxide (ZrO{sub 2}), powdered titanium oxide (TiO{sub 2}), and zirconyl nitrate [ZrO(NO{sub 3}){sub 2}] via static immersion at 90 C, 150 C, and 200 C. Test environments were specifically designed in a circulation loop to create a dissolved oxygen concentration of 300 ppb. Test results showed that the corrosion current densities of all treated specimens were lower than that of the untreated, pre-oxidized specimen at ambient temperature in a solution mixed with 1 mM K{sub 3}Fe(CN){sub 6} and 1 mM K{sub 4}Fe(CN){sub 6}. The ECPs of the treated specimens could be lower or higher than that of the pre-oxidized one at 288 C, depending upon the type of treating chemical and the treating temperature. In addition, IGSCC was observed on all specimens (treated or untreated) in the same environment. However, the untreated specimen exhibited lower elongation, shorter failure time, and more secondary cracks on the side surfaces. It was therefore suggested that inhibitive chemicals such as ZrO{sub 2}, TiO{sub 2}, and ZrO(NO{sub 3}){sub 2} did provide a certain degree of enhancement in improving the mechanical behavior of the treated specimens and in prolonging the IGSCC initiation time. (authors)

  5. A phenomenological study of initiation and propagation of stress corrosion cracks. Application to AISI 304L stainless steel in magnesium chloride; Etude phenomenologique de l`amorcage et de la propagation de fissures de corrosion sous contraintes. Application a l`acier inoxydable Z 2CN 18.10 dans le chlorure de magnesium

    Energy Technology Data Exchange (ETDEWEB)

    Peyrat, C.; Raquet, O.; Helie, M.; Santarini, G. [CEA Fontenay-aux-Roses, 92 (France). Service de la Corrosion, d`Electrochimie et Chimie des Fluides

    1999-04-01

    A purely phenomenological study of Stress Corrosion Cracking (SCC) was performed using the couple AISI 304L austenitic stainless steel/boiling magnesium chloride aqueous solution. The exploitation of the morphological information (shape of the cracks and size distribution) available after constant elongation rate tests led to the apparent initiation of the cracks and to their growth rate. A law for the real initiation is proposed too and the elongation rate effect in quantitatively characterized. (authors) 8 refs.

  6. A test procedure for determining the influence of stress ratio on fatigue crack growth

    Science.gov (United States)

    Fitzgerald, J. H.; Wei, R. P.

    1974-01-01

    A test procedure is outlined by which the rate of fatigue crack growth over a range of stress ratios and stress intensities can be determined expeditiously using a small number of specimens. This procedure was developed to avoid or circumvent the effects of load interactions on fatigue crack growth, and was used to develop data on a mill annealed Ti-6Al-4V alloy plate. Experimental data suggest that the rates of fatigue crack growth among the various stress ratios may be correlated in terms of an effective stress intensity range at given values of K max. This procedure is not to be used, however, for determining the corrosion fatigue crack growth characteristics of alloys when nonsteady-state effects are significant.

  7. Aircraft corrosion and crack inspection using advanced magneto-optic imaging technology

    Science.gov (United States)

    Thome, David K.; Fitzpatrick, Gerald L.; Skaugset, Richard L.; Shih, William C.

    1996-11-01

    A next generation magneto-optic imaging system, the MOI 303, has recently been introduced with the ability to generate real-time, complete, 2D eddy current images of cracks and corrosion in aircraft. The new imaging system described features advanced, digital remote control operation and on- screen display of setup parameters for ease of use. This instrument gives the inspector the capability to more rapidly scan large surfaces areas. The magneto-optic/eddy current imaging technology has already been formally approved for inspection of surface cracking on an aircraft fuselage. The improved magneto-optic imager is now poised to aid rapid inspection for corrosion and subsurface cracking. Previous magneto-optic imaging systems required the inspector to scan the surface twice for complete inspection coverage: a second scan was necessary with the imager rotated about 90 degrees from the orientation of the first pass. However, by providing eddy current excitation simultaneously from two orthogonal directions, complete, filled-in magneto-optic images are now generated regardless of the orientation of the imager. THese images are considerably easier to interpret and evaluate. In addition, there is a synergism obtained in applying eddy current excitation simultaneously in multiple directions: better penetration is obtained and the resulting images have better signal to noise levels compared to those produced with eddy current excitation applied only in one direction. Examples of these improved images are presented.

  8. Mitigation of Intergranular Stress Corrosion Cracking in Al-Mg by Electrochemical Potential Control

    Science.gov (United States)

    McMahon, M. E.; Scully, J. R.; Burns, J. T.

    2017-08-01

    Intergranular stress corrosion cracking in the Al-Mg alloy AA5456-H116 is suppressed via cathodic polarization in 0.6 M NaCl, saturated (5.45 M) NaCl, 2 M MgCl2, and saturated (5 M) MgCl2. Three zones of intergranular stress corrosion cracking (IG-SCC) susceptibility correlate with pitting potentials of unsensitized AA5456-H116 and pure β phase (Al3Mg2) in each solution. These critical potentials reasonably describe the influence of α Al matrix and β phase dissolution rates on IG-SCC severity. Complete inhibition occurred at applied potentials of -1.0 V and -1.1 V versus saturated calomel electrode ( V SCE) in 0.6 M NaCl. Whereas only partial mitigation of IG-SCC was achieved at -0.9 V SCE in 0.6 M NaCl and at -0.9, -1.0, and -1.1 V SCE in the more aggressive environments. Correlation of pitting potentials in bulk environments with IG-SCC behavior suggests an effect of bulk environment [Cl-] and pH on the stabilized crack tip chemistry.

  9. Study of alloy 600`S stress corrosion cracking mechanisms in high temperature water; Etude des mecanismes de corrosion sous contrainte de l`alliage 600 dans l`eau a haute temperature

    Energy Technology Data Exchange (ETDEWEB)

    Rios, R.

    1994-06-01

    In order to better understand the mechanisms involved in Alloy 600`s stress corrosion cracking in PWR environment, laboratory tests were performed. The influence of parameters pertinent to the mechanisms was studies : hydrogen and oxygen overpressures, local chemical composition, microstructure. The results show that neither hydrogen nor dissolution/oxidation, despite their respective roles in the process, are sufficient to account for experimental facts. SEM observation of micro-cleavage facets on specimens` fracture surfaces leads to pay attention to a new mechanism of corrosion/plasticity interactions. (author). 113 refs., 73 figs., 15 tabs., 4 annexes.

  10. Stress Corrosion Cracking of the Drip Shield, the Waste Package Outer Barrier, and the Stainless Steel Structural Material

    Energy Technology Data Exchange (ETDEWEB)

    G. Gordon

    2004-10-13

    Stress corrosion cracking is one of the most common corrosion-related causes for premature breach of metal structural components. Stress corrosion cracking is the initiation and propagation of cracks in structural components due to three factors that must be present simultaneously: metallurgical susceptibility, critical environment, and static (or sustained) tensile stresses. This report was prepared according to ''Technical Work Plan for: Regulatory Integration Modeling and Analysis of the Waste Form and Waste Package'' (BSC 2004 [DIRS 171583]). The purpose of this report is to provide an evaluation of the potential for stress corrosion cracking of the engineered barrier system components (i.e., the drip shield, waste package outer barrier, and waste package stainless steel inner structural cylinder) under exposure conditions consistent with the repository during the regulatory period of 10,000 years after permanent closure. For the drip shield and waste package outer barrier, the critical environment is conservatively taken as any aqueous environment contacting the metal surfaces. Appendix B of this report describes the development of the SCC-relevant seismic crack density model (SCDM). The consequence of a stress corrosion cracking breach of the drip shield, the waste package outer barrier, or the stainless steel inner structural cylinder material is the initiation and propagation of tight, sometimes branching, cracks that might be induced by the combination of an aggressive environment and various tensile stresses that can develop in the drip shields or the waste packages. The Stainless Steel Type 316 inner structural cylinder of the waste package is excluded from the stress corrosion cracking evaluation because the Total System Performance Assessment for License Application (TSPA-LA) does not take credit for the inner cylinder. This document provides a detailed description of the process-level models that can be applied to assess the

  11. Corrosion evaluation technology

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Uh Chul; Han, Jeong Ho; Nho, Kye Ho; Lee, Eun Hee; Kim, Hong Pyo; Hwang, Seong Sik; Lee, Deok Hyun; Hur, Do Haeng; Kim, Kyung Mo

    1997-09-01

    A multifrequency ACPD system was assembled which can measure very small crack. Stress corrosion cracking test system with SSRT operating high temperature was installed. Stress corrosion cracking test of newly developed alloy 600 and existing alloy 600 was carried out in steam atmosphere of 400 deg C. No crack was observed in both materials within a test period of 2,000 hrs. Corrosion fatigue test system operating at high temperature was installed in which fatigue crack was measured by CDPD. Lead enhanced the SCC of the Alloy 600 in high temperature water, had a tendency to modify a cracking morphology from intergranular to transgranular. Pit initiation preferentially occurred at Ti-rich carbide. Resistance to pit initiation decreased with increasing temperature up to 300 deg C. Test loop for erosion corrosion was designed and fabricated. Thin layer activation technique was very effective in measuring erosion corrosion. Erosion corrosion of a part of secondary side pipe was evaluated by the Check Family Codes of EPRI. Calculated values of pipe thickness by Check Family Codes coincided with the pipe thickness measured by UT with an error of {+-} 20%. Literature review on turbine failure showed that failure usually occurred in low pressure turbine rotor disc and causes of failure are stress corrosion cracking and corrosion fatigue. (author). 12 refs., 20 tabs., 77 figs.

  12. Diffusion-Coupled Cohesive Interface Simulations of Stress Corrosion Intergranular Cracking in Polycrystalline Materials

    Energy Technology Data Exchange (ETDEWEB)

    Pu, Chao; Gao, Yanfei; Wang, Yanli; Sham, T.-L.

    2017-09-01

    To study the stress corrosion intergranular cracking mechanism, a diffusion-coupled cohesive zone model (CZM) is proposed for the simulation of the stress-assisted diffusional process along grain boundaries and the mechanical response of grain boundary sliding and separation. This simulation methodology considers the synergistic effects of impurity diffusion driven by pressure gradient and degradation of grain boundary strength by impurity concentration. The diffusion-coupled CZM is combined with crystal plasticity finite element model (CPFEM) to simulate intergranular fracture of polycrystalline material under corrosive environment. Significant heterogeneity of the stress field and extensive impurity accumulation is observed at grain boundaries and junction points. Deformation mechanism maps are constructed with respect to the grain boundary degradation factor and applied strain rate, which dictate the transition from internal to near-surface intergranular fracture modes under various strain amplitudes and grain sizes.

  13. Synthetic sea water - An improved stress corrosion test medium for aluminum alloys

    Science.gov (United States)

    Humphries, T. S.; Nelson, E. E.

    1973-01-01

    A major problem in evaluating the stress corrosion cracking resistance of aluminum alloys by alternate immersion in 3.5 percent salt (NaCl) water is excessive pitting corrosion. Several methods were examined to eliminate this problem and to find an improved accelerated test medium. These included the addition of chromate inhibitors, surface treatment of specimens, and immersion in synthetic sea water. The results indicate that alternate immersion in synthetic sea water is a very promising stress corrosion test medium. Neither chromate inhibitors nor surface treatment (anodize and alodine) of the aluminum specimens improved the performance of alternate immersion in 3.5 percent salt water sufficiently to be classified as an effective stress corrosion test method.

  14. ELECTROCHEMICAL CORROSION TEST RESULTS FOR TANK 241-SY-102 SUPERNATE GRAB SAMPLES

    Energy Technology Data Exchange (ETDEWEB)

    DUNCAN JB

    2007-04-09

    This report describes the electrochemical corrosion scans and conditions for testing of SY-102 supernatant samples taken December 2004. The testing was performed because the tank was under a Justification for Continued Operation allowing the supernatant composition to be outside the chemistry limits of Administrative Control 5.16, 'Corrosion Mitigation program'. A new electrochemical working electrode of A516 Grade 60 carbon steel was used for each scan; all scans were measured against a saturated calomel electrode, with carbon counter electrodes, and all scans were carried out at 50 C. The samples were scanned twice, once as received and once sparged with argon to deoxygenate the sample. For those scans conducted after argon purging, the corrosion rates ranged from 0.012 to 0.019 mpy. A test for stress corrosion cracking was carried out on one sample (2SY-04-07) with negative results.

  15. Statistical model of stress corrosion cracking based on extended form of Dirichlet energy: Part 2

    Indian Academy of Sciences (India)

    HARRY YOSH

    2016-10-01

    In the previous paper ({\\it Pramana – J. Phys.} 81(6), 1009 (2013)), the mechanism of stress corrosion cracking (SCC) based on non-quadratic form of Dirichlet energy was proposed and its statistical features were discussed. Following those results, we discuss here how SCC propagates on pipe wall statistically. It reveals that SCC growth distribution is described with Cauchy problem of time-dependent first-order partial differential equation characterized by the convolution of the initial distribution of SCC over time. We also discuss the extension of the above results to the SCC in two-dimensional space and its statistical features with a simple example.

  16. Intergranular stress corrosion cracking of welded ferritic stainless steels in high temperature aqueous environments

    Energy Technology Data Exchange (ETDEWEB)

    Fukuzuka, Toshio; Shimogori, Kazutoshi; Fujiwara, Kazuo; Tomari, Haruo (Kobe Steel Ltd. (Japan). Central Research and Development Lab.); Kanda, Masao

    1982-07-01

    In considering the application of ferritic stainless steels to heat exchanger tubing materials for moisture separator-reheaters in LWRs, the effects of environmental conditions (temperature, chloride, dissolved oxygen, pH), thermal history, and steel composition (content of C, N, Cr and Ti) on the Inter-Granular Stress Corrosion Cracking (IGSCC) in high temperature aqueous environments, were studied. The IGSCC was proved to depend on steel composition and thermal history rather than environment. From these results, a steel was designed to prevent IGSCC of the welding HAZ for 18Cr and 13Cr steels.

  17. High-Performance Laser Peening for Effective Mitigation of Stress Corrosion Cracking

    Energy Technology Data Exchange (ETDEWEB)

    Hackel, L; Hao-Lin, C; Wong, F; Hill, M

    2002-10-02

    Stress corrosion cracking (SCC) in the Yucca Mountain waste package closure welds is believed to be the greatest threat to long-term containment. Use of stress mitigation to eliminate tensile stresses resulting from welding can prevent SCC. A laser technology with sufficient average power to achieve high throughput has been developed and commercially deployed with high peak power and sufficiently high average power to be an effective laser peening system. An appropriately applied version of this process could be applied to eliminate SCC in the waste package closure welds.

  18. A study on the mechanism of stress corrosion cracking of duplex stainless steels in hot alkaline-sulfide solution

    Science.gov (United States)

    Chasse, Kevin Robert

    Duplex stainless steels (DSS) generally have superior strength and corrosion resistance as compared to most standard austenitic and ferritic stainless grades owing to a balanced microstructure of austenite and ferrite. As a result of having favorable properties, DSS have been selected for the construction of equipment in pulp and paper, chemical processing, nuclear, oil and gas as well as other industries. The use of DSS has been restricted in some cases because of stress corrosion cracking (SCC), which can initiate and grow in either the ferrite or austenite phase depending on the environment. Thorough understanding of SCC mechanisms of DSS in chloride- and hydrogen sulfide-containing solutions has been useful for material selection in many environments. However, understanding of SCC mechanisms of DSS in sulfide-containing caustic solutions is limited, which has restricted the capacity to optimize process and equipment design in pulp and paper environments. Process environments may contain different concentrations of hydroxide, sulfide, and chloride, altering corrosion and SCC susceptibility of each phase. Crack initiation and growth behavior will also change depending on the relative phase distribution and properties of austenite and ferrite. The role of microstructure and environment on the SCC of standard grade UNS S32205 and lean grade UNS S32101 in hot alkaline-sulfide solution were evaluated in this work using electrochemical, film characterization, mechanical testing, X-ray diffraction, and microscopy techniques. Microstructural aspects, which included residual stress state, phase distribution, phase ratio, and microhardness, were related to the propensity for SCC crack initiation in different simulated alkaline pulping liquors at 170 °C. Other grades of DSS and reference austenitic and superferritic grades of stainless steel were studied using exposure coupons for comparison to understand compositional effects and individual phase susceptibility

  19. Effect of proton irradiation on irradiation assisted stress corrosion cracking in PWR

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Han Ok; Hwang, Mi Jin; Kim, Sung Woo; Hwang, Seong Sik [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2014-05-15

    Irradiation assisted stress corrosion cracking (IASCC) involves the cracking and failure of materials under irradiation environment in nuclear power plant water environment. The major factors and processes governing an IASCC are suggested by others. The IASCC of the reactor core internals due to the material degradation and the water chemistry change has been reported in high stress stainless steel components, such as fuel elements (Boiling Water Reactors) in the 1960s, a control rod in the 1970s, and a baffle former bolt in recent years of light water reactors (Pressurized Water Reactors). Many irradiated stainless steels that are resistant to inergranular cracking in 288 .deg. C argon are susceptible to IG cracking in the simulated BWR environment at the same temperature. Under the circumstances, a lot works have been performed on IASCC in BWR. Recent efforts have been devoted to investigate an IASCC in a PWR, but the mechanism in a PWR is not fully understood yet as compared with that in a BWR owing to a lack of data from laboratories and fields. Therefore, it is strongly necessary to review and analyze recent researches of an IASCC in both BWR and PWR for establishing a proactive management technology for the IASCC of core internals in Korean PWRs. The objective of this research to find IASCC behavior of proton irradiated 316 stainless steels in a high-temperature water chemistry environment. The IASCC initiation susceptibility on 1, 3, 5 DPA proton irradiated 316 austenite stainless steel was evaluated in PWR environment. SCC area ratio on the fracture surface was similar regardless of irradiation level. Total crack length on the irradiated surface increases in order of specimen 1, 3, 5 DPA. The total crack length at the side surface is a better measure in evaluating IASCC initiation susceptibility for proton-irradiated samples.

  20. Standard Practice for Use of Mattsson's Solution of pH 7.2 to Evaluate the Stress- Corrosion Cracking Susceptibility of Copper-Zinc Alloys

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2011-01-01

    1.1 This practice covers the preparation and use of Mattsson's solution of pH 7.2 as an accelerated stress-corrosion cracking test environment for brasses (copper-zinc base alloys). The variables (to the extent that these are known at present) that require control are described together with possible means for controlling and standardizing these variables. 1.2 This practice is recommended only for brasses (copper-zinc base alloys). The use of this test environment is not recommended for other copper alloys since the results may be erroneous, providing completely misleading rankings. This is particularly true of alloys containing aluminum or nickel as deliberate alloying additions. 1.3 This practice is intended primarily where the test objective is to determine the relative stress-corrosion cracking susceptibility of different brasses under the same or different stress conditions or to determine the absolute degree of stress corrosion cracking susceptibility, if any, of a particular brass or brass component ...

  1. Effect of a novel three-step aging on strength, stress corrosion cracking and microstructure of AA7085

    Institute of Scientific and Technical Information of China (English)

    陈送义; 陈康华; 董朋轩; 叶升平; 黄兰萍; 阳代军

    2016-01-01

    The influence of a novel three-step aging on strength, stress corrosion cracking (SCC) and microstructure of AA7085 was investigated by tensile testing and slow strain rate testing combined with transmission electron microscopy (TEM). The results indicate that with the increase of second-step aging time of two-step aging, the mechanical properties increase first and then decrease, while the SCC resistance increases. Compared with two-step aging, three-step aging treatment improves SCC resistance and the strength increases by about 5%. The effects of novel three-step aging on strength and SCC resistance are explained by the role of matrix precipitates and grain boundary precipitates, respectively.

  2. Estimation of elastic modulus of reinforcement corrosion products using inverse analysis of digital image correlation measurements for input in corrosion-induced cracking model

    DEFF Research Database (Denmark)

    Pease, Bradley Justin; Michel, Alexander; Thybo, Anna Emilie A.;

    2012-01-01

    A combined experimental and numerical approach for estimating the elastic modulus of reinforcement corrosion products is presented. Deformations between steel and mortar were measured using digital image correlation during accelerated corrosion testing at 100 μA/cm2 (~1.16 mm/year). Measured...... deformations were compared to a numerical corrosion model that considers electrochemical, transport, and mechanical processes, including penetration of corrosion products into a ‘corrosion-accommodating region,’ provided by the mortar’s capillary porosity, directly surrounding the steel. Comparing model...... and experimental results provides an order-of-magnitude approximation of corrosion product stiffness of 2.0 GPa....

  3. Natural Environment Corrosion Testing at the Kennedy Space Center Beachside Atmospheric Corrosion Test Site

    Science.gov (United States)

    Calle, Luz M.

    2017-01-01

    This presentation will provide an overview of how NASA has been conducting corrosion testing in the Natural Marine Environment at the Kennedy Space Center, Florida, U.S. The following questions will be addressed: What factors should be considered when selecting and constructing a test site? What are the attributes of a good test site? Is more severe always better? What environmental parameters should be monitored? How frequently? What factors should be considered when designing test specimens? Are current test standards sufficient? How do diurnal, annual and other fluctuations in corrosivity influence tests? How are test results interpreted? Can they be quantified?

  4. Development of Modified 304 Stainless Steel Resistant to Stress Corrosion Cracking in Chloride Environment

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    This was a feasibility study for a modified 304 steel resistant to stress corrosion cracking (SCC) in aqueous environment containing chloride. SCC tests were conducted potentiostaticaly with spot-welded specimens, which had both crevice and residual stress, mainly in 3 % NaCl solution at various temperatures to determine the critical temperature for SCC at and below which the steel would not suffer from SCC. The effects of individual alloying element of silicon, manganese and copper on SCC of 18Cr-14Ni steels which phosphor content is 0.002 % and molybdenum content is 0.01 % were examined. Addition of 1 or 2 % of copper has beneficial effect on resistance to SCC, while increasing silicon or manganese content has no significant effect. Critical temperature of the steel with 0.002 % of phosphor and 2 % of copper is 150 ℃, which is markedly higher than 50 ℃ of 304L steel. However, the beneficial effect of copper is reduced with increasing phosphor content. From practical viewpoint, the modified steel with good SCC resistance should have 0.01 %-0.015 % of phosphor and 0.3 % or more of molybdenum, because it is very difficult to reduce phosphor content below 0.008 % industrially and such molybdenum content is inevitably introduced through cost-saving melting process using return steel. Aluminium is to be added as another alloying element and 3 % of aluminium combined with 2 % of copper has been found to negate the deleterious effects of increased phosphor and molybdenum content. As a candidate steel at this stage, 14Cr-16Ni-0.013P-2Cu-1Al-(0.3-1)Mo steel has critical temperature of 110 ℃.

  5. Critical assessment of precracked specimen configuration and experimental test variables for stress corrosion testing of 7075-T6 aluminum alloy plate

    Science.gov (United States)

    Domack, M. S.

    1985-01-01

    A research program was conducted to critically assess the effects of precracked specimen configuration, stress intensity solutions, compliance relationships and other experimental test variables for stress corrosion testing of 7075-T6 aluminum alloy plate. Modified compact and double beam wedge-loaded specimens were tested and analyzed to determine the threshold stress intensity factor and stress corrosion crack growth rate. Stress intensity solutions and experimentally determined compliance relationships were developed and compared with other solutions available in the literature. Crack growth data suggests that more effective crack length measurement techniques are necessary to better characterize stress corrosion crack growth. Final load determined by specimen reloading and by compliance did not correlate well, and was considered a major source of interlaboratory variability. Test duration must be determined systematically, accounting for crack length measurement resolution, time for crack arrest, and experimental interferences. This work was conducted as part of a round robin program sponsored by ASTM committees G1.06 and E24.04 to develop a standard test method for stress corrosion testing using precracked specimens.

  6. Coal Ash Corrosion Resistant Materials Testing

    Energy Technology Data Exchange (ETDEWEB)

    D. K. McDonald; P. L. Daniel; D. J. DeVault

    2003-08-31

    In April 1999, three identical superheater test sections were installed into the Niles Unit No.1 for the purpose of testing and ranking the coal ash corrosion resistance of candidate superheater alloys. The Niles boiler burns high sulfur coal (3% to 3.5%) that has a reasonably high alkali content, thus the constituents necessary for coal ash corrosion are present in the ash. The test sections were controlled to operate with an average surface metal temperature from approximately 1060 F to 1210 F which was well within the temperature range over which coal ash corrosion occurs. Thus, this combination of aggressive environment and high temperature was appropriate for testing the performance of candidate corrosion-resistant tube materials. Analyses of the deposit and scale confirmed that the aggressive alkali-iron-trisulfate constituent was present at the metal surface and active in tube metal wastage. The test sections were constructed so that the response of twelve different candidate tube and/or coating materials could be studied. The plan was to remove and evaluate one of the three test sections at time intervals of 1 year, 3 years, and 5 years. This would permit an assessment of performance of the candidate materials as a function of time. This report provides the results of the evaluation of Test Section C, including the samples that remained in the Test Section for the full exposure period as well as those that were removed early. The analysis of Test Section C followed much the same protocol that was employed in the assessment of Test Section A. Again, the focus was on determining and documenting the relative corrosion rates of the candidate materials. The detailed results of the investigation are included in this report as a series of twelve appendices. Each appendix is devoted to the performance of one of the candidate alloys. The table below summarizes metal loss rate for the worst case sample of each of the candidate materials for both Test Sections A and C

  7. Corrosion test on Alloy 690 TT in simulated hideout media

    Energy Technology Data Exchange (ETDEWEB)

    Laire, C.; Goffin, C. [Laborelec (Belgium); Mullier, B. [Faculte Polytechnique de Mons (Belgium)

    2002-07-01

    Laborelec has shown the detrimental effect of Cu oxides on Alloy 690 TT in acidic sulfate solutions. Although copper condenser's tubes were replaced by titanium, there are other sources of copper in power plants. Furthermore in spite of improved steam generator (SG) design and better monitoring of secondary water chemistry, deposits formation cannot be fully prevented and impurities such as copper may build up over the years. These impurities are hardly detectable in the SG blow down. During hideout returns for new steam generators, tubed in Alloy 690 TT, compounds like sulfate, silica and organics are mainly found (in the order of one to ten gram). Following these hideout return analyses, influences of main species were studied through stress corrosion cracking tests. The focus is on sulfates, silica, alumina, copper oxides and organic species such as acetate, formate and oxalate. Moreover, the influence of pH in those concentrated solutions-set using ammonia-is also studied. Stress corrosion cracking (SCC) tests are carried out on new SG's Alloy 690 TT tubes sections, for about 25 different mixtures of the aforementioned species. These tests are accelerated SCC capsule testing because of the use of concentrated media at 320 C and of a highly stressed condition. Highly stressed Alloy 690 TT resists well in most environments, very fast SCC appears only in acidic sulfate medium polluted by Cu. The initiation of SCC for alloy 690 TT depends of the occurrence of the simultaneous presence of 3 key factors: low pH, oxidizing conditions and high stresses. (authors)

  8. Allowing for surface preparation in stress corrosion cracking modelling; Prise en compte de l`etat de surface dans la modelisation de la fissuration par corrosion sous contrainte

    Energy Technology Data Exchange (ETDEWEB)

    Berge, P.; Buisine, D. [Electricite de France (EDF), 92 - Clamart (France); Gelpi, A. [FRAMATOME, 92 - Paris-La-Defence (France)

    1997-12-31

    When a 600 alloy component is significantly deformed during installation, by welding, rolling, bending, its stress corrosion cracking in Pressurized Water Nuclear Reactor`s primary coolant, is significantly changed by the initial surface treatment. Therefore, the crack initiated time may be reduced by several orders of magnitude for certain surfaces preparations. Allowing for cold working of the surface, for which modelling is proposed, depends less on the degree of cold work then on the depths of the hardened layers. Honing hardens the metal over depths of about one micron for vessel head penetrations, for example, and has little influence on subsequent behaviour after the part deforms. On the other hand, coarser turning treatment produces cold worked layers which can reach several tens of microns and can very significantly reduce the initiation time compared to fine honing. So evaluation after depths of hardening is vital on test pieces for interpreting laboratory results as well as on service components for estimating their service life. Suppression by mechanical or chemical treatment of these layers, after deformation, seems to be the most appropriate solution for reducing over-stressing connected with surface treatment carried out before deformation. (author). 14 refs.

  9. An approach to reconstruction of a natural crack using signals of eddy current testing. 1. Reconstruction of an idealized natural crack

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Zhenmao [Japan Nuclear Cycle Development Inst., Oarai, Ibaraki (Japan). Oarai Engineering Center

    1998-12-01

    In this paper, an approach to the reconstruction of an idealized natural crack of non-vanishing conductivity is proposed with use of signals of eddy current testing. Two numerical models are introduced at first for modeling a Stress Corrosion Crack (SCC) in order it possibly to be represented by a set of crack parameters. A method for rapid prediction of the eddy current testing signals arisen from these idealized cracks is given then by extending a knowledge based fast forward solver developed by authors to the case of a non-vanishing conductivity. On the other hand, the inverse algorithm of conjugate gradient method is improved to reconstruct the crack parameters and is implemented with the pick-up signals and gradients calculated by using the rapid forward solver. Several examples are presented finally for validating the proposed strategy. The results verified that both of the models can give reasonable reconstruction results in case of a low noise level. The model concerning the touch of crack surfaces with a conducting band region surrounded by the crack edge, however, is proved more efficient that the model using a conductivity distribution from the point of view of both reconstruction speed and accuracy. (author)

  10. Effects of Nitrogen and Tensile Direction on Stress Corrosion Cracking Susceptibility of Ni-Free FeCrMnC-Based Duplex Stainless Steels

    Science.gov (United States)

    Ha, Heon-Young; Lee, Chang-Hoon; Lee, Tae-Ho; Kim, Sangshik

    2017-01-01

    Stress corrosion cracking (SCC) behavior of Ni-free duplex stainless steels containing N and C (Febalance-19Cr-8Mn-0.25C-(0.03, 0.21)N, in wt %) was investigated by using a slow strain rate test (SSRT) in air and aqueous NaCl solution with different tensile directions, including parallel (longitudinal) and perpendicular (transverse) to the rolling direction. It was found that alloying N was effective in increasing the resistance to SCC, while it was higher along the longitudinal direction than the transverse direction. The SCC susceptibility of the two alloys was assessed based on the electrochemical resistance to pitting corrosion, the corrosion morphology, and the fractographic analysis. PMID:28772651

  11. Assessment of ultrasonic techniques for characterization of stress corrosion cracks in SG partition stubs

    Energy Technology Data Exchange (ETDEWEB)

    Sartre, B.; Banchet, J. [AREVA NP, Saint-Marcel (France); Moras, D.; Bastin, P. [Intercontrole, Rungis (France); Beroni, C. [EDF/CEIDRE, Saint-Denis (France)

    2006-07-01

    Studies by EDF and AREVA NP on Inconel zones have identified the Inconel 600 partition stubs of steam generators as potential areas of SCC, on the hot leg side. Decision was made to perform an expert assessment using ultrasonic testing (UT) techniques to be applied on the whole area of the stub showing penetrant testing (PT) techniques indications. UT techniques, probes and tools were then developed for that purpose. The aim is to size shallow defects, sizing capacity being maintained for defects propagated to a half-thickness. Although no formal qualification was required, the development was performed in view of a performance demonstration. Three mock-ups were manufactured by AREVA NP: two welded mock-ups with machined defects, surface condition and geometry representative of the ''envelope'' of situations likely to be found on the SG; one mock-up, with representative corrosion cracks Development was carried out in two phases: development of techniques and specification of probes and tooling, then development of tools, industrialization of probes, development of procedures, personnel training and performance demonstration. The basic inspection relied on TOFDT, with a contact probe; frequencies, PCS and dimensions were optimised using the results from the mock-ups. Three sets of transducers were defined: a HF transducer for flaw sizes close to the critical size, another HF transducer, with lower PCS for smaller defects, both transducers for material whose permeability was equivalent to that of the mock-ups; anticipating less permeable materials, a MF probe was added. Tests having shown that these transducers did not cover the whole plate thickness, a back-up phased-array probe was selected to scan the plate beyond halfthickness. For a better access under the TSP, a focused transducer was also added to complete the previous set. All of these transducers were operated in immersion, with the same tool: a COBRA type arm which positioned the probes

  12. 16 CFR 1209.5 - Test procedures for corrosiveness.

    Science.gov (United States)

    2010-01-01

    ... REGULATIONS INTERIM SAFETY STANDARD FOR CELLULOSE INSULATION The Standard § 1209.5 Test procedures for corrosiveness. This section prescribes the procedures for determining the corrosiveness of cellulose insulation. Cellulose insulation shall be tested for corrosiveness using the measured settled density, obtained by...

  13. Fatigue crack growth rate test using a frequency sweep method

    Institute of Scientific and Technical Information of China (English)

    Xun ZHOU; Xiao-li YU

    2008-01-01

    Fatigue crack propagation characteristics of a diesel engine crankshaft are studied by measuring the fatigue crack growth rate using a frequency sweep method on a resonant fatigue test rig. Based on the phenomenon that the system frequency will change when the crack becomes large, this method can be directly applied to a complex component or structure. Finite element analyses (FEAs) are performed to calibrate the relation between the frequency change and the crack size, and to obtain the natural frequency of the test rig and the stress intensity factor (SIF) of growing cracks. The crack growth rate i.e. da/dN-AK of each crack size is obtained by combining the testing-time monitored data and FEA results. The results show that the crack growth rate of engine crankshaft, which is a component with complex geometry and special surface treatment, is quite different from that of a pure material. There is an apparent turning point in the Paris's crack partition. The cause of the fatigue crack growth is also dis-cussed.

  14. Study on H2S stress corrosion test of welded joint for X65 pipeline steel and numerical analysis

    Institute of Scientific and Technical Information of China (English)

    金晓军; 霍立兴; 张玉凤; 白秉仁; 李晓巍; 曹军

    2004-01-01

    The susceptibility of welded joint for the X65 pipeline steel to H2S stress corrosion cracking (SCC) is investigated. SCC tests on the steel are carried out in the environment based on NACE TM-01-77 solution with saturated gaseous H2S. The threshold stress intensity factor and crack propagation velocity are calculated according to wedge-opening loading (WOL) specimens. The three-dimensional elastic-plastic finite element analysis of WOL specimens is performed by using the FEM programming package ANSYS. Stress field and concentration of hydrogen distribution property ahead of the crack tip are obtained. This paper surveyed the microstructure of welded joint and studied on the mechanical properties of X65 pipeline steel. It provides experimental basis for studying stress corrosion. The results of numerical analysis are consistent with conclusions of stress corrosion test.

  15. Numerical investigation on stress corrosion cracking behavior of dissimilar weld joints in pressurized water reactor plants

    Directory of Open Access Journals (Sweden)

    Lingyan Zhao

    2014-07-01

    Full Text Available There have been incidents recently where stress corrosion cracking (SCC observed in the dissimilar metal weld (DMW joints connecting the reactor pressure vessel (RPV nozzle with the hot leg pipe. Due to the complex microstructure and mechanical heterogeneity in the weld region, dissimilar metal weld joints are more susceptible to SCC than the bulk steels in the simulated high temperature water environment of pressurized water reactor (PWR. Tensile residual stress (RS, in addition to operating loads, has a great contribution to SCC crack growth. Limited experimental conditions, varied influence factors and diverging experimental data make it difficult to accurately predict the SCC behavior of DMW joints with complex geometry, material configuration, operating loads and crack shape. Based on the film slip/dissolution oxidation model and elastic-plastic finite element method (EPFEM, an approach is developed to quantitatively predict the SCC growth rate of a RPV outlet nozzle DMW joint. Moreover, this approach is expected to be a pre-analytical tool for SCC experiment of DMW joints in PWR primary water environment.

  16. Public inquiry concerning stress corrosion cracking on Canadian oil and gas pipelines

    Energy Technology Data Exchange (ETDEWEB)

    Vollman, K.W.; Cote-Verhaaf, A.; Illing, R.

    1996-11-01

    An comprehensive inquiry was conducted into the serious problem of near-neutral pH stress corrosion cracking (SCC) in Canada`s buried oil and gas pipelines. The inquiry was prompted by evidence of the widespread nature of SCC and awareness that research was producing new insights into the problem. Two major ruptures and fires occurred on the TransCanada system in February and July of 1995. The July rupture was in a location where it was believed SCC could not occur. SCC on pipelines occurs when small cracks develop on the outside surface of the buried pipeline. With time the cracks grow large enough until the pipeline fails or ruptures. SCC results from an interaction of the following three conditions: a potent environment at the pipe surface, a susceptible pipe material, and a tensile stress. Recommendations to resolve the problem included implementation of an SCC management program by pipeline companies, changes to the design of the pipeline, continued research, establishment of an SCC database, improved emergency response practices, and information sharing. 84 refs., 8 tabs., 67 figs.

  17. In vivo oxide-induced stress corrosion cracking of Ti-6Al-4V in a neck-stem modular taper: Emergent behavior in a new mechanism of in vivo corrosion.

    Science.gov (United States)

    Gilbert, Jeremy L; Mali, Sachin; Urban, Robert M; Silverton, Craig D; Jacobs, Joshua J

    2012-02-01

    In vivo modular taper corrosion in orthopedic total joint replacements has been documented to occur for head-neck tapers, modular-body tapers, and neck-stem tapers. While the fretting corrosion mechanism by which this corrosion occurs has been described in the literature, this report shows new and as yet unreported mechanisms at play. A retrieved Ti-6Al-4V/Ti-6Al-4V neck-stem taper interface, implanted for 6 years is subjected to failure analysis to document taper corrosion processes that lead to oxide driven crack formation on the medial side of the taper. Metallurgical sectioning techniques and scanning electron microscopy analysis are used to document the taper corrosion processes. The results show large penetrating pitting attack of both sides of the taper interface where corrosion selectively attacks the beta phase of the microstructure and eventually consumes the alpha phase. The pitting attack evolves into plunging pits that ultimately develop into cracks where the crack propagation process is one of corrosion resulting in oxide formation and subsequent reorganization. This process drives open the crack and advances the front by a combination of oxide-driven crack opening stresses and corrosion attack at the tip. The oxide that forms has a complex evolving structure including a network of transport channels that provide access of fluid to the crack tip. This emergent behavior does not appear to require continued fretting corrosion to propagate the pitting and cracking. This new mechanism is similar to stress corrosion cracking where the crack tip stresses arise from the oxide formation in the crack and not externally applied tensile stresses.

  18. Long-term corrosion testing pan.

    Energy Technology Data Exchange (ETDEWEB)

    Wall, Frederick Douglas; Brown, Neil R. (Los Alamos National Laboratory, Los Alamos, NM)

    2008-08-01

    This document describes the testing and facility requirements to support the Yucca Mountain Project long-term corrosion testing needs. The purpose of this document is to describe a corrosion testing program that will (a) reduce model uncertainty and variability, (b) reduce the reliance upon overly conservative assumptions, and (c) improve model defensibility. Test matrices were developed for 17 topical areas (tasks): each matrix corresponds to a specific test activity that is a subset of the total work performed in a task. A future document will identify which of these activities are considered to be performance confirmation activities. Detailed matrices are provided for FY08, FY09 and FY10 and rough order estimates are provided for FY11-17. Criteria for the selection of appropriate test facilities were developed through a meeting of Lead Lab and DOE personnel on October 16-17, 2007. These criteria were applied to the testing activities and recommendations were made for the facility types appropriate to carry out each activity. The facility requirements for each activity were assessed and activities were identified that can not be performed with currently available facilities. Based on this assessment, a total of approximately 10,000 square feet of facility space is recommended to meet all future testing needs, given that all testing is consolidated to a single location. This report is a revision to SAND2007-7027 to address DOE comments and add a series of tests to address NWTRB recommendations.

  19. Stress corrosion cracking behaviour in welded X-70 linepipe steel under near-neutral pH conditions

    Energy Technology Data Exchange (ETDEWEB)

    Adeleke, A.H.; Luo, J.L.; Ivey, D.G. [Alberta Univ., Edmonton, AB (Canada). Dept. of Chemical and Materials Engineering

    2005-07-01

    This study examined the relationship between the near neutral pH stress corrosion cracking (SCC) resistance and the yield strength of pipelines steels. In particular, double-edge-notched flat tensile samples of X70 steel were used for both slow strain-rate testing (SSRT) and cyclic loading testing with the notch located in the zone of interest. This included the weld metal (WM), base metal (BM) and heat-affected zone (HAZ). In all samples, the mode of failure was mostly transgranular with cleavage facets around the edges of the fracture surface. One of the objectives of this study was to better understand the microstructural effect of the relationship. The 3 main parameters that were used to assess the SCC susceptibility in a near-neutral pH environment were the elongation ratio, the estimated percentage of the fracture surface that showed brittle fractures, and the relative crack growth at a given exposure time. It was shown that resistance to near-neutral pH SCC depends greatly on the microstructure of the pipeline steels. Fine-grained bainite and ferrite structured steels were found to have a much better combination of strength and SCC resistance compared to ferrite and pearlite structures. The high-to-low sensitivity ranking of the X70 linepipe steel to SCC was established to be: WM is greater than HAZ which is greater than BM. 20 refs., 1 tab., 9 figs.

  20. Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H2O–CO–CO2 Solutions

    Directory of Open Access Journals (Sweden)

    J. W. van der Merwe

    2012-01-01

    Full Text Available The stress-corrosion cracking of A516 pressure vessel steel was investigated by the use of slow strain-rate tests. The orientation of samples to the rolling direction was investigated, and it was found that samples machined longitudinal to the rolling direction showed a slightly increased sensitivity to stress corrosion. The temperature variation showed that for different gas mixtures, the maximum sensitivity to stress corrosion was in the region of 45° to 55°C for the 25% CO gas mixture, whereas with higher CO concentrations, this temperature region of maximum sensitivity moved to higher temperatures. Surface finish showed a slight increase in sensitivity to cracking with increased surface roughness. The most significant increase was found with increased total gas pressures and when samples have been exposed to the environment for an extended period. This was as a result of the inhibition of the corrosion reaction by the passivation of the carbon monoxide, which is a time-dependent process.

  1. Atmospheric-Induced Stress Corrosion Cracking of Grade 2205 Duplex Stainless Steel—Effects of 475 °C Embrittlement and Process Orientation

    Directory of Open Access Journals (Sweden)

    Cem Örnek

    2016-07-01

    Full Text Available The effect of 475 °C embrittlement and microstructure process orientation on atmospheric-induced stress corrosion cracking (AISCC of grade 2205 duplex stainless steel has been investigated. AISCC tests were carried out under salt-laden, chloride-containing deposits, on U-bend samples manufactured in rolling (RD and transverse directions (TD. The occurrence of selective corrosion and stress corrosion cracking was observed, with samples in TD displaying higher propensity towards AISCC. Strains and tensile stresses were observed in both ferrite and austenite, with similar magnitudes in TD, whereas, larger strains and stresses in austenite in RD. The occurrence of 475 °C embrittlement was related to microstructural changes in the ferrite. Exposure to 475 °C heat treatment for 5 to 10 h resulted in better AISCC resistance, with spinodal decomposition believed to enhance the corrosion properties of the ferrite. The austenite was more susceptible to ageing treatments up to 50 h, with the ferrite becoming more susceptible with ageing in excess of 50 h. Increased susceptibility of the ferrite may be related to the formation of additional precipitates, such as R-phase. The implications of heat treatment at 475 °C and the effect of process orientation are discussed in light of microstructure development and propensity to AISCC.

  2. Long-term corrosion testing plan.

    Energy Technology Data Exchange (ETDEWEB)

    Wall, Frederick Douglas; Brown, Neil R. (Los Alamos National Laboratory, Los Alamos, NM)

    2009-02-01

    This document describes the testing and facility requirements to support the Yucca Mountain Project long-term corrosion testing program. The purpose of this document is to describe a corrosion testing program that will (a) reduce model uncertainty and variability, (b) reduce the reliance upon overly conservative assumptions, and (c) improve model defensibility. Test matrices were developed for 17 topical areas (tasks): each matrix corresponds to a specific test activity that is a subset of the total work performed in a task. A future document will identify which of these activities are considered to be performance confirmation activities. Detailed matrices are provided for FY08, FY09 and FY10 and rough order estimates are provided for FY11-17. Criteria for the selection of appropriate test facilities were developed through a meeting of Lead Lab and DOE personnel on October 16-17, 2007. These criteria were applied to the testing activities and recommendations were made for the facility types appropriate to carry out each activity. The facility requirements for each activity were assessed and activities were identified that can not be performed with currently available facilities. Based on this assessment, a total of approximately 10,000 square feet of facility space is recommended to accommodate all future testing, given that all testing is consolidated to a single location. This report is a revision to SAND2008-4922 to address DOE comments.

  3. Corrosion Fatigue in District Heating Water Tanks

    DEFF Research Database (Denmark)

    Maahn, Ernst Emanuel

    1996-01-01

    Three candidate materials for construction of buffer tanks for district heating water have been tested for corrosion fatigue properties in a district heating water environment. The investigation included Slow Strain Rate Testing of plain tensile specimens, crack initiation testing by corrosion...... fatigue of plain tensile specimens and crack growth rate determination for Compact Tensile Specimens under corrosion fatigue conditions. The three materials are equal with respect to stress corrosion sensibility and crack initiation. Crack growth rate is increased with a factor of 4-6 relative to an inert...

  4. Corrosion of steel bars in cracked concrete made with ordinary portland, slag and fly ash cements

    Energy Technology Data Exchange (ETDEWEB)

    Mohammed, T.U.; Yamaji, T.; Hamada, H. [Port and Harbor Research Inst., Ministry of Land, Infrastructure and Transport (Japan); Aoyama, T. [PS Corp. (Japan)

    2001-07-01

    A study was conducted in which the marine durability of ordinary portland cement, slag and fly ash cement was examined using 15 year old plain and reinforced concrete cylindrical specimens. The performance of these cements was then examined for pre-cracked reinforced concrete prism samples. The process of manufacturing cement emits huge amounts of carbon dioxide into the global atmosphere. Replacing a portion of the cement with by-products from the steel industry and thermal power plants (which are both huge emitters of carbon dioxide) can lower carbon dioxide emissions and also solve the disposal issue of slag and fly ash while increasing the long-term durability of concrete structures. In this study, concrete cylindrical specimens were made of ordinary portland cement, slag and fly ash cements. The specimens were 100 x 100 x 600 mm prisms of different types of cement. Water-to-cement ratios were 0.45 and 0.55. Both tap water and seawater were used as mixing water. The samples were exposed in tidal pools for 15 years to evaluate the compressive strength of the concrete, corrosion of the steel bars, and chloride-ion concentrations in the concrete. It was shown that, with the exception of fly ash cements, the compressive strength of most cements increased after 15 years of exposure compared to its 28 day strength. Type C slag cement demonstrated the best performance against chloride-ion at the surface of concrete made with slag and fly ash. Voids in the steel-concrete interface make it possible for corrosion pits to develop. The use of seawater as mixing water results in earlier strength development at 28 days and does not cause to the strength of the concrete to regress after 15-years of exposure, but it causes more corrosion of steel bars at a lower cover depth. Corrosion of steel bars is not an issue at deeper cover depths. 15 refs., 19 tabs., 13 figs.

  5. Liquid-Air Interface Corrosion Testing Simulating The Environment Of Hanford Double Shell Tanks

    Energy Technology Data Exchange (ETDEWEB)

    Gray, J. R. [Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL); Garcia-Diaz, B. L. [Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL); Murphy, T. H. [Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL); Hicks, K. R. [Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL)

    2014-01-30

    Coupon tests on A537 carbon steel materials were conducted to evaluate the Liquid-Air Interface (LAI) corrosion susceptibility in a series of solutions designed to simulate conditions in the radioactive waste tanks located at the Hanford Nuclear Facility. The new stress corrosion cracking requirements and the impact of ammonia on LAI corrosion were the primary focus. The minimum R value (i.e., molar ratio of nitrite to nitrate) of 0.15 specified by the new stress corrosion cracking requirements was found to be insufficient to prevent pitting corrosion at the LAI. The pH of the test solutions was 10, which was actually less than the required pH 11 defined by the new requirements. These tests examined the effect of the variation of the pH due to hydroxide depletion at the liquid air interface. The pits from the current testing ranged from 0.001 to 0.008 inch in solutions with nitrate concentrations of 0.4 M and 2.0 M. The pitting and general attack that occurred progressed over the four-months. No significant pitting was observed, however, for a solution with a nitrate concentration of 4.5 M. The pitting depths observed in these partial immersion tests in unevaporated condensates ranged from 0.001 to 0.005 inch after 4 months. The deeper pits were in simulants with low R values. Simulants with R values of approximately 0.6 to 0.8 appeared to significantly reduce the degree of attack. Although, the ammonia did not completely eliminate attack at the LAI, the amount of corrosion in an extremely corrosive solution was significantly reduced. Only light general attack (< 1 mil) occurred on the coupon in the vicinity of the LAI. The concentration of ammonia (i.e., 50 ppm or 500 ppm) did not have a strong effect.

  6. Corrosion test cell for bipolar plates

    Science.gov (United States)

    Weisbrod, Kirk R.

    2002-01-01

    A corrosion test cell for evaluating corrosion resistance in fuel cell bipolar plates is described. The cell has a transparent or translucent cell body having a pair of identical cell body members that seal against opposite sides of a bipolar plate. The cell includes an anode chamber and an cathode chamber, each on opposite sides of the plate. Each chamber contains a pair of mesh platinum current collectors and a catalyst layer pressed between current collectors and the plate. Each chamber is filled with an electrolyte solution that is replenished with fluid from a much larger electrolyte reservoir. The cell includes gas inlets to each chamber for hydrogen gas and air. As the gases flow into a chamber, they pass along the platinum mesh, through the catalyst layer, and to the bipolar plate. The gas exits the chamber through passageways that provide fluid communication between the anode and cathode chambers and the reservoir, and exits the test cell through an exit port in the reservoir. The flow of gas into the cell produces a constant flow of fresh electrolyte into each chamber. Openings in each cell body is member allow electrodes to enter the cell body and contact the electrolyte in the reservoir therein. During operation, while hydrogen gas is passed into one chamber and air into the other chamber, the cell resistance is measured, which is used to evaluate the corrosion properties of the bipolar plate.

  7. Effects of cold work on stress corrosion cracking of type 316L stainless steel in hot lithium hydroxide solution

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, J.H.; Bogaerts, W.F. (Univ. of Leuven (Belgium). Dept. of Metallurgy and Materials Engineering)

    1993-07-01

    Lithium hydroxide (LiOH) has ben chose as the lithium compound to be used in the Aqueous Lithium Salt Blanket (ALSB) concept that has been proposed as a possible driver blanket for the Next European Torus (NET), the next generation of fusion testing devices in Europe, as well as for the International Thermonuclear Experimental Reactor program (ITER). The stress corrosion cracking (SCC) behavior of cold-worked AISI type 316L stainless steel (SS) in a concentrated lithium salt solution at elevated temperature was investigated. Using the slow strain rate technique, SCC experiments were carried out on 20% and 40% cold-worked materials in a solution of 10g lithium hydroxide and 100 cm[sup 3]H[sub 2]O at 95C under conditions with controlled electrochemical potential. Observation of the fracture surfaces by scanning electron microscope indicated the SCC behavior of the cold-worked steel was essentially different from that of the solution-annealed steel. A ductile fracture of cold-worked samples occurred under open-circuit conditions ([approximately][minus]280 mV) and at 200 mV. Slight intergranular attack was found in the region near the surface of cold-worked specimens when the electrochemical potential was controlled at [minus]120 mV. SCC was observed when the experiments were conducted at +100mV. Intergranular stress corrosion cracking (IGSCC) of solution-annealed material changed into a mixed SCC mode, or a dominant transgranular SCC (TGSCC) with an increase of cold work to 20% and 40%. Compared to the SCC behavior of the solution-annealed 316L, the results showed cold work improved significantly the resistance of 316L SS to IGSCC in the hot LiOH environment. Susceptibility to TGSCC of cold-worked 316L SS increased with increasing extent of cold working. These effects were reviewed with respect to electrochemical and microstructural phenomena.

  8. The influence of cracks on chloride-induced corrosion of reinforced concrete structures - development of the experimental set-up

    NARCIS (Netherlands)

    Blagojevic, A.; Koleva, D.A.; Walraven, J.C.

    2014-01-01

    Chloride-induced corrosion of steel reinforcement is one of the major threats to durability of reinforced concrete structures in aggressive environmental conditions. When the steel reinforcement starts to corrode, structures gradually lose integrity and service life is shortened. Cracks are inevitab

  9. Effect of pH Value on Stress Corrosion Cracking of X70 Pipeline Steel in Acidic Soil Environment

    Institute of Scientific and Technical Information of China (English)

    Zhiyong LIU; Cuiwei DU; Xin ZHANG; Fuming WANG; Xiaogang LI

    2013-01-01

    The effect of pH value on the stress corrosion cracking (SCC) of API X70 pipeline steel in simulated acidic soil solutions was investigated by using slow strain rate test,electrochemical polarization curves,electrochemical impedance spectroscopy,and scanning electron microscopy.pH plays an important role in the susceptibility and electrochemical mechanism of SCC.The pH higher than 5 has no significant effect on electrochemical processes.By contrast,the pH lower than 5 intensifies cathodic hydrogen evolution reactions,thus increasing the cathodic current and corrosion potential.Under different pH values,the SCC mechanism of X70 pipeline steel varies among anodic dissolution (AD),hydrogen embrittlement (HE),and the combination of AD and HE (AD + HE) with variations of applied potential.At-850 mVSCE,the SCC mechanism is HE if pH is less than 4 or AD + HE if pH value is more positive.

  10. Strain energy density-distance criterion for the initiation of stress corrosion cracking of alloy X-750

    Energy Technology Data Exchange (ETDEWEB)

    Hall, M.M. Jr.; Symons, D.M.

    1996-05-01

    A strain energy density-distance criterion was previously developed and used to correlate rising-load K{sub c} initiation data for notched and fatigue precracked specimens of hydrogen precharged Alloy X-750. This criterion, which was developed for hydrogen embrittlement (HE) cracking, is used here to correlate static-load stress corrosion cracking (SCC) initiation times obtained for smooth geometry, notched and fatigue precracked specimens. The onset of SCC crack growth is hypothesized to occur when a critical strain, which is due to environment-enhanced creep, is attained within the specimen interior. For notched and precracked specimens, initiation is shown by analysis to occur at a variable distance from notch and crack tips. The initiation site varies from very near the crack tip, for highly loaded sharp cracks, to a site that is one grain diameter from the notch, for lower loaded, blunt notches. The existence of hydrogen gradients, which are due to strain-induced hydrogen trapping in the strain fields of notch and crack tips, is argued to be controlling the site for initiation of cracking. By considering the sources of the hydrogen, these observations are shown to be consistent with those from the previous HE study, in which the characteristic distance for crack initiation was found to be one grain diameter from the notch tip, independent of notch radius, applied stress intensity factor and hydrogen level.

  11. Research of stress corrosion cracking of T225NG titanium alloy in loop water of high temperature and high pressure

    Institute of Scientific and Technical Information of China (English)

    Xu Jijin; Yan Keng; Chen Ligong; Jiang Chengyu

    2006-01-01

    Double cantilever beam (DCB) specimens were used to research the stress corrosion cracking of T225NG titanium alloy in loop water of high temperature and high pressure. DCB specimens were forced pre-stress, put into high pressure autoclave, and the stress corrosion and crack expansion of specimens were observed and measured in 500 h, 1 000 h and 2 000h respectively. The results show that small expansion occurred along the direction of pre-cracking. According to calculation,the speed of cracking expansion is lower than 10 -9 m/s in 500 h and the value of KIscc/KI is higher than 0. 75, which proves that T225NG has an excellent corrosion resistance in loop water. The main reason is that there is an oxide film on the surface of specimens. According to the analysis of energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD), the oxide film consists of TiO2. Therefore, the oxide film at the crack tip impedes the hydrogen separating out from the cathode to penetrate into titanium alloy and resists hydrogen embrittlement.

  12. Electrochemical Corrosion Testing of Neutron Absorber Materials

    Energy Technology Data Exchange (ETDEWEB)

    Tedd Lister; Ron Mizia; Arnold Erickson; Tammy Trowbridge

    2007-05-01

    This report summarizes the results of crevice-corrosion tests for six alloys in solutions representative of ionic compositions inside the Yucca Mountain waste package should a breech occur. The alloys in these tests are Neutronit A978a (ingot metallurgy, hot rolled), Neutrosorb Plus 304B4 Grade Ab (powder metallurgy, hot rolled), Neutrosorb Plus 304B5 Grade Ab (powder metallurgy, hot rolled), Neutrosorb Plus 304B6 Grade Ab (powder metallurgy, hot rolled), Ni-Cr-Mo-Gd alloy2 (ingot metallurgy, hot rolled), and Alloy 22 (ingot metallurgy, hot rolled).

  13. CORROSION ISSUES ASSOCIATED WITH AUSTENITIC STAINLESS STEEL COMPONENTS USED IN NUCLEAR MATERIALS EXTRACTION AND SEPARATION PROCESSES

    Energy Technology Data Exchange (ETDEWEB)

    Mickalonis, J.; Louthan, M.; Sindelar, R.

    2012-12-17

    This paper illustrated the magnitude of the systems, structures and components used at the Savannah River Site for nuclear materials extraction and separation processes. Corrosion issues, including stress corrosion cracking, pitting, crevice corrosion and other corrosion induced degradation processes are discussed and corrosion mitigation strategies such as a chloride exclusion program and corrosion release testing are also discussed.

  14. Misunderstanding and Understanding of Primary Water Stress Corrosion Cracking of Structural Components in the Primary System of PWRs

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Young Suk; Kim, Sung Soo; Kim, Dae Whan [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2014-05-15

    All the structural components in the primary system of pressurized water reactors that are in contact with primary water are made of austenitic Ni-Cr-Fe alloys which are known to be corrosion resistant. Nevertheless, these Ni-Cr-Fe alloys such as Alloy 600, weld 182/82, austenitic stainless steels suffer from intergranular stress corrosion cracking (IGSCC) after their 10 year operation in reactors although the environment to which they have been exposed is almost pure water of pH 6.9 to 7.2, which is called primary water stress corrosion cracking (PWSCC). Given that the underlying mechanism of PWSCC remains unidentified so far, there are many misunderstandings related to PWSCC of the structural components, which may lead to unreasonable mitigation measures. The aim of this work is to highlight understanding and misunderstanding of PWSCC related to austenitic Ni-Cr-Fe alloys.

  15. Long Term Corrosion/Degradation Test Six Year Results

    Energy Technology Data Exchange (ETDEWEB)

    M. K. Adler Flitton; C. W. Bishop; M. E. Delwiche; T. S. Yoder

    2004-09-01

    The Subsurface Disposal Area (SDA) of the Radioactive Waste Management Complex (RWMC) located at the Idaho National Engineering and Environmental Laboratory (INEEL) contains neutron-activated metals from non-fuel, nuclear reactor core components. The Long-Term Corrosion/Degradation (LTCD) Test is designed to obtain site-specific corrosion rates to support efforts to more accurately estimate the transfer of activated elements to the environment. The test is using two proven, industry-standard methods—direct corrosion testing using metal coupons, and monitored corrosion testing using electrical/resistance probes—to determine corrosion rates for various metal alloys generally representing the metals of interest buried at the SDA, including Type 304L stainless steel, Type 316L stainless steel, Inconel 718, Beryllium S200F, Aluminum 6061, Zircaloy-4, low-carbon steel, and Ferralium 255. In the direct testing, metal coupons are retrieved for corrosion evaluation after having been buried in SDA backfill soil and exposed to natural SDA environmental conditions for times ranging from one year to as many as 32 years, depending on research needs and funding availability. In the monitored testing, electrical/resistance probes buried in SDA backfill soil will provide corrosion data for the duration of the test or until the probes fail. This report provides an update describing the current status of the test and documents results to date. Data from the one-year and three-year results are also included, for comparison and evaluation of trends. In the six-year results, most metals being tested showed extremely low measurable rates of general corrosion. For Type 304L stainless steel, Type 316L stainless steel, Inconel 718, and Ferralium 255, corrosion rates fell in the range of “no reportable” to 0.0002 mils per year (MPY). Corrosion rates for Zircaloy-4 ranged from no measurable corrosion to 0.0001 MPY. These rates are two orders of magnitude lower than those specified in

  16. Modelling of iodine-induced stress corrosion cracking in CANDU fuel

    Science.gov (United States)

    Lewis, B. J.; Thompson, W. T.; Kleczek, M. R.; Shaheen, K.; Juhas, M.; Iglesias, F. C.

    2011-01-01

    Iodine-induced stress corrosion cracking (I-SCC) is a recognized factor for fuel-element failure in the operation of nuclear reactors requiring the implementation of mitigation measures. I-SCC is believed to depend on certain factors such as iodine concentration, oxide layer type and thickness on the fuel sheath, irradiation history, metallurgical parameters related to sheath like texture and microstructure, and the mechanical properties of zirconium alloys. This work details the development of a thermodynamics and mechanistic treatment accounting for the iodine chemistry and kinetics in the fuel-to-sheath gap and its influence on I-SCC phenomena. The governing transport equations for the model are solved with a finite-element technique using the COMSOL Multiphysics® commercial software platform. Based on this analysis, this study also proposes potential remedies for I-SCC.

  17. DEVELOPMENT OF SOFTWARE SYSTEM FOR MONITORING OF STRESS CORROSION CRACKING OF THE PIPELINE UNDER TENSION

    Directory of Open Access Journals (Sweden)

    Z. K. Abaev

    2016-01-01

    Full Text Available The software and hardware development tendency, providing the automated monitoring and control of basic and auxiliary technological processes of gas transportation via system of main gas pipelines has been revealed. The article discusses the stages of creation of the software of system of monitoring corrosion cracking under tension (SCC. The new useful adequate regression models development determining the risk level of LCC is shown. A ranking sections algorithm of main gas pipeline (MG on the propensity to SCC is presented. Adequate developed regression equation determining the LCC risk level has been developed. To count the main gas pipeline lifetime the variable rank of the danger of SCC (RSCC on the basis of methods of fuzzy logic is proposed to use. Implementation of the fuzzy model was carried out using the graphical tools developed in MATLAB using the expansion pack Fuzzy Logic Toolbox. The working algorithm of developed program and the screen forms are presented.

  18. Localized Deformation as a Primary Cause of Irradiation Assisted Stress Corrosion Cracking

    Energy Technology Data Exchange (ETDEWEB)

    Gary S. Was

    2009-03-31

    The objective of this project is to determine whether deformation mode is a primary factor in the mechanism of irradiation assisted intergranular stress corrosion cracking of austenitic alloys in light watert reactor core components. Deformation mode will be controlled by both the stacking fault energy of the alloy and the degree of irradiation. In order to establish that localized deformation is a major factor in IASCC, the stacking fault energies of the alloys selected for study must be measured. Second, it is completely unknown how dose and SFE trade-off in terms of promoting localized deformation. Finally, it must be established that it is the localized deformation, and not some other factor that drives IASCC.

  19. Researches on corrosion cracking phenomenonthat occurs on welded of agricultural equipment

    Directory of Open Access Journals (Sweden)

    I. Sărăcin

    2015-04-01

    Full Text Available Welded construction equipments for agriculture are strongly stressed in terms of mechanics, but also in terms of environmental action and thus in many cases appears their wear by corrosion cracking phenomenon. After research it was noted that after a certain period of use of equipment, metallographic structure of welded steel structures has changed substantially and at the same time a change in the chemical composition of steel was also observed. In terms of chemical composition a reduction in carbon content was mainly observed, and an increase in sulfur content,determined mainly by the presence of large quantities of sulfur in the atmosphere. This sulfur in the atmosphere at the same time determines the acid action on metallic materials, by forming with water from precipitation of H2S.

  20. Principles of inhibiting of corrosion-static crack growth in constructional steels caused by hydrogen embrittlement

    Energy Technology Data Exchange (ETDEWEB)

    Romaniv, O.N.; Nikiforchin, G.N.; Tsirul' nik, A.T.

    1987-11-01

    The effectiveness of a range of organic and inorganic corrosion inhibitors was studied on a series of structural chromium steels--including 45KhN2MFA, 60KhS, and 30KhGSN2A--of different strength levels and certain principles are formulated for developing and selecting inhibitors based on the hydrogen mechanism of corrosive media. The inhibitors tested include monoethanol amine, urotropin, sodium benzoate, thiourea, sodium phosphates and chromates, various nitrates, and the IRT range of inhibitors.

  1. The Long-Term Corrosion Test Facility at the Lawrence Livermore National Laboratory

    Energy Technology Data Exchange (ETDEWEB)

    Fix, D V; Rebak, R B

    2007-03-21

    The long-term corrosion test facility (LTCTF) at the Lawrence Livermore National Laboratory (LLNL) consisted of 22 vessels that housed more than 7,000 corrosion test specimens from carbon steels to highly corrosion resistant materials such Alloy 22 and Ti Grade 7. The specimens from LTCTF range from standard weight-loss coupons to U-bend specimens for testing susceptibility to environmentally assisted cracking. Each vessel contained approximately 1000 liters of concentrated brines at 60 C or 90 C. The LTCTF started its operations in late 1996. The thousands of specimens from the LTCTF were removed in August-September 2006. The specimens are being catalogued and stored for future characterization. Previously removed specimens (e.g. 1 and 5 years) are also archived for further studies.

  2. Effect of Repair Welding on Electrochemical Corrosion and Stress Corrosion Cracking Behavior of TIG Welded AA2219 Aluminum Alloy in 3.5 Wt Pct NaCl Solution

    Science.gov (United States)

    Venugopal, A.; Sreekumar, K.; Raja, V. S.

    2010-12-01

    The stress corrosion cracking (SCC) behavior of AA2219 aluminum alloy in the as-welded (AW) and repair-welded (RW) conditions was examined and compared with that of the base metal (BM) in 3.5 wt pct NaCl solution using the slow strain rate technique (SSRT). The reduction in ductility was used as a parameter to evaluate the SCC susceptibility of both BM and welded joints. The results show that the ductility ratio ( ɛ NaCl/( ɛ air)) of the BM was close to one (0.97) and reduced to 0.9 for the AW joint. This value further reduced to 0.77 after carrying out one repair welding operation. However, the RW specimen exhibited higher ductility than the single-weld specimens even in 3.5 wt pct NaCl solution. SSRT results obtained using pre-exposed samples followed by post-test metallographic observations clearly showed localized pitting corrosion along the partially melted zone (PMZ), signifying that the reduction in ductility ratio of both the AW and RW joints was more due to mechanical overload failure, caused by the localized corrosion and a consequent reduction in specimen thickness, than due to SCC. Also, the RW joint exhibited higher ductility than the AW joint both in air and the environment, although SCC index (SI) for the former is lower than that of the latter. Fractographic examination of the failed samples, in general, revealed a typical ductile cracking morphology for all the base and welded joints, indicating the good environmental cracking resistance of this alloy. Microstructural examination and polarization tests further demonstrate grain boundary melting along the PMZ, and that provided the necessary electrochemical condition for the preferential cracking on that zone of the weldment.

  3. Coal Ash Corrosion Resistant Materials Testing

    Energy Technology Data Exchange (ETDEWEB)

    D. K. McDonald; P. L. Daniel; D. J. DeVault

    2007-12-31

    In April 1999, three identical superheater test sections were installed into the Niles Unit No.1 for the purpose of testing and ranking the coal ash corrosion resistance of candidate superheater alloys. The Niles boiler burns high sulfur coal (3% to 3.5%) that has a moderate alkali content (0.2% sodium equivalents), thus the constituents necessary for coal ash corrosion are present in the ash. The test sections were controlled to operate with an average surface metal temperature from approximately 1060 F to 1210 F which was within the temperature range over which coal ash corrosion occurs. Thus, this combination of aggressive environment and high temperature was appropriate for testing the performance of candidate corrosion-resistant tube materials. Analyses of the deposit and scale confirmed that aggressive alkali sulfate constituents were present at the metal surface and active in tube metal wastage. The test sections were constructed so that the response of twelve different candidate tube and/or coating materials could be studied. The plan was to remove and evaluate one of the three test sections at time intervals of 1 year, 3 years, and 5 years. This would permit an assessment of performance of the candidate materials as a function of time. Test Section A was removed in November 2001 after about 24 months of service at the desired steam temperature set point, with about 15.5 months of exposure at full temperature. A progress report, issued in October 2002, was written to document the performance of the candidate alloys in that test section. The evaluation described the condition of each tube sample after exposure. It involved a determination of the rate of wall thickness loss for these samples. In cases where there was more than one sample of a candidate material in the test section, an assessment was made of the performance of the alloy as a function of temperature. Test Sections B and C were examined during the November 2001 outage, and it was decided that

  4. Fracture model for predicting concrete cover-cracking induced by steel corrosion based on interface bond state

    Institute of Scientific and Technical Information of China (English)

    WANG Xian-li; ZHENG Jian-jun; WU Zhi-min

    2009-01-01

    Time-to-cracking of the concrete cover induced by the steel corrosion is one of the critical problems faced by engineers, operators and asset managers in making strategies for the maintenance and repairs of reinforced concrete (RC)structures affected by corrosion. In this paper, a theoretical model for predicting the time-to-cracking is derived by assuming the bond between the steel bar and the concrete as a linear combination of perfectly smooth and bonded. The model takes into account the characteristics of existing exiguous flaws and initial cracks in the concrete before the load acting on RC structures. The validity of the proposed model is preliminarily verified by comparing the obtained results with the available experimental results. A remarkable advantage of the proposed method is its application to the prediction of the service life of RC structures, made of the deformed steel bars as well as the round bars. By determining an experimental constant α, which is related to the interface bond state between the steel bar and the concrete, the service life of RC structures can be predicted using the proposed scheme. Analysis of major factors affecting the time-to-cracking demonstrates that the length of the initial crack affects the service life of RC structures significantly. Moreover, the larger cover thickness and the smaller diameter of the steel bar within a certain range are beneficial to prolonging the time-to-cracking.

  5. Stress-corrosion cracking of steels in ammonia with consideration given to OTEC design: a survey

    Energy Technology Data Exchange (ETDEWEB)

    Teel, R.B.

    1980-03-01

    Carbon steel, alloy steel, and high-strength, quenched and tempered steel, when under applied or residual stress and especially when cold formed and/or welded without subsequent thermal stress relief, are subject to failure by stress-corrosion cracking (SCC) in air-contaminated dry ammonia. Water as well as hydrazine when present in small amounts have been shown to be effective inhibitors in an all steel system. Galvanic corrosion between dissimilar metals and/or accelerated failure by SCC of stressed steel as a result of galvanic coupling may be of concern. Where water has proven effective as an inhibitor of SCC in an all steel system, it may not be adequate in a mixed metal system. With aluminum tubes, the tube sheet will either have to be solid aluminum, aluminum clad steel or some nonconductive coating will be necessary to effectively remove the cathodic alloy from the galvanic circuit. Research is required to determine the severity of the coupling effect between dissimilar alloys in ammonia under OTEC conditions; especially the possibility of accelerated SCC failures of stressed steel where the presence of an inhibitor in the ammonia may not be sufficient to override the galvanic coupling effect.

  6. Corrosion resistance of a steel under an oxidizing atmosphere in a fluid catalytic cracking regenerator

    Directory of Open Access Journals (Sweden)

    Ieda Caminha

    2004-03-01

    Full Text Available In the present work, the corrosion resistance of an ASTM A 387 G11 steel was evaluated under two conditions: an oxidizing atmosphere in a fluid catalytic cracking regenerator of a petroleum processing unit and a simulated atmosphere in the laboratory, at temperatures of 650 °C and 700 °C. The characterization of the phases present in the oxidized layer was carried out by X-ray diffraction (XRD, optical microscopy (OM and scanning electron microscopy (SEM with X-ray energy dispersive analysis (EDS. Severe corrosion was observed after exposure to both the real and simulated conditions, with formation of several iron oxides (Fe2O3, Fe3O4 and FeO in the product scale layer, as well as a slight inner oxidation and sulfidation of chromium in the substrate. Internal nitridation of the silicon and the manganese was observed only in the real condition, probably related to the long-term exposure inside the regenerator.

  7. Status report: Intergranular stress corrosion cracking of BWR core shrouds and other internal components

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    1996-03-01

    On July 25, 1994, the US Nuclear Regulatory Commission (NRC) issued Generic Letter (GL) 94-03 to obtain information needed to assess compliance with regulatory requirements regarding the structural integrity of core shrouds in domestic boiling water reactors (BWRs). This report begins with a brief description of the safety significance of intergranular stress corrosion cracking (IGSCC) as it relates to the design and function of BWR core shrouds and other internal components. It then presents a brief history of shroud cracking events both in the US and abroad, followed by an indepth summary of the industry actions to address the issue of IGSCC in BWR core shrouds and other internal components. This report summarizes the staff`s basis for issuing GL 94-03, as well as the staff`s assessment of plant-specific responses to GL 94-03. The staff is continually evaluating the licensee inspection programs and the results from examinations of BWR core shrouds and other internal components. This report is representative of submittals to and evaluations by the staff as of September 30, 1995. An update of this report will be issued at a later date.

  8. Assessment of NDE Technologies for Detection and Characterization of Stress Corrosion Cracking in LWRs

    Energy Technology Data Exchange (ETDEWEB)

    Meyer, Ryan M.; Ramuhalli, Pradeep; Toloczko, Mychailo B.; Bond, Leonard J.; Montgomery, Robert O.

    2012-12-31

    Stress corrosion cracking (SCC) in light water reactors (LWRs) has been a persistent form of degradation in the nuclear industry. Examples of SCC can be found for a range of materials in boiling and pressurized water reactor environments, including carbon steels, stainless steels, and nickel-base stainless alloys. The evolution of SCC is often characterized by a long initiation stage followed by a phase of more rapid crack growth to failure. This provides a relatively short window of opportunity to detect the start of observable SCC, and it is conceivable that SCC could progress from initiation to failure between subsequent examinations when managed by applying periodic in-service inspection techniques. Implementation of advanced aging management paradigms in the current fleet of LWRs will require adaptation of existing measurement technologies and development of new technologies to perform on-line measurements during reactor operation to ensure timely detection of material degradation and to support the implementation of advanced diagnostics and prognostics. This paper considers several non-destructive examination (NDE) technologies with known sensitivity to detection of indicators for SCC initiation and/or propagation, and assesses these technologies with respect to their ability to detect and accurately characterize the significance of an SCC flaw. Potential strategies to improve SCC inspection or monitoring performance are offered to benefit management of SCC degradation in LWRs.

  9. Effect of Nanostructure Changes on Stress Corrosion Cracking of Proton Irradiated Nuclear Energy Structural Materials

    Directory of Open Access Journals (Sweden)

    M.N. Lunika

    2011-01-01

    Full Text Available Austenitic stainless alloys are used extensively as structural materials in the internal components of light water reactor (LWR pressure vessels because of their relatively high strength, ductility, and fracture toughness. Irradiation-assisted stress corrosion cracking (IASCC is main degradation process that affects LWR internal components exposed to radiation. The existing data on proton irradiated austenitic alloys were reviewed to evaluate the effects of key parameters such as material composition, irradiation dose on IASCC susceptibility of these materials in LWR environments. The significance of deformation nanostructure and stacking fault energy (SFE changes in the material on IASCC susceptibility is also discussed. Results show that the IASCC susceptibility of the alloys increases with increasing irradiation dose and decreasing stacking fault energy. IASCC tends to initiate at locations where slip dislocation channels intersect grain boundaries. Localized deformation in the form of grain boundary sliding due to the interaction of slip channels and grain boundaries is likely the primary cause of the observed cracking initiation. It may play a key role in the underlying mechanism of IASCC in light water reactor core components.

  10. Materials Reliability Program Resistance to Primary Water Stress Corrosion Cracking of Alloys 690, 52, and 152 in Pressurized Water Reactors (MRP-111)

    Energy Technology Data Exchange (ETDEWEB)

    Xu, H. [Framatome ANP, Inc., Lynchburg, VA (United States); Fyfitch, S. [Framatome ANP, Inc., Lynchburg, VA (United States); Scott, P. [Framatome ANP, SAS, Paris (France); Foucault, M. [Framatome ANP, SAS, Le Creusot (France); Kilian, R. [Framatome ANP, GmbH, Erlangen (Germany); Winters, M. [Framatome ANP, GmbH, Erlangen (Germany)

    2004-03-01

    Over the last thirty years, stress corrosion cracking in PWR primary water (PWSCC) has been observed in numerous Alloy 600 component items and associated welds, sometimes after relatively long incubation times. Repairs and replacements have generally utilized wrought Alloy 690 material and its compatible weld metals (Alloy 152 and Alloy 52), which have been shown to be very highly resistant to PWSCC in laboratory experiments and have been free from cracking in operating reactors over periods already up to nearly 15 years. It is nevertheless prudent for the PWR industry to attempt to quantify the longevity of these materials with respect to aging degradation by corrosion in order to provide a sound technical basis for the development of future inspection requirements for repaired or replaced component items. This document first reviews numerous laboratory tests, conducted over the last two decades, that were performed with wrought Alloy 690 and Alloy 52 or Alloy 152 weld materials under various test conditions pertinent to corrosion resistance in PWR environments. The main focus of the present review is on PWSCC, but secondary-side conditions are also briefly considered.

  11. A comparison of the stress corrosion cracking susceptibility of commercially pure titanium grade 4 in Ringer's solution and in distilled water: a fracture mechanics approach.

    Science.gov (United States)

    Roach, Michael D; Williamson, R Scott; Thomas, Joseph A; Griggs, Jason A; Zardiackas, Lyle D

    2014-01-01

    From the results of laboratory investigations reported in the literature, it has been suggested that stress corrosion cracking (SCC) mechanisms may contribute to early failures in titanium alloys that have elevated oxygen concentrations. However, the susceptibility of titanium alloys to SCC in physiological environments remains unclear. In this study, a fracture mechanics approach was used to examine the SCC susceptibility of CP titanium grade 4 in Ringer's solution and distilled de-ionized (DI) water, at 37°C. The study duration was 26 weeks, simulating the non-union declaration of a plated fracture. Four wedge loads were used corresponding to 86-95% of the alloy's ligament yield load. The longest cracks were measured to be 0.18 mm and 0.10 mm in Ringer's solution and DI water, respectively. SEM analysis revealed no evidence of extensive fluting and quasi-cleavage fracture features which, in literature reports, were attributed to SCC. We thus postulate that the Ringer's solution accelerated the wedge-loaded crack growth without producing the critical stresses needed to change the fracture mechanism. Regression analysis of the crack length results led to a significant best-fit relationship between crack growth velocity (independent variable) and test electrolyte, initial wedge load, and time of immersion of specimen in electrolyte (dependent variables).

  12. High temperature corrosion investigation in an oxyfuel combustion test rig

    DEFF Research Database (Denmark)

    Montgomery, Melanie; Bjurman, M.; Hjörnhede, A

    2014-01-01

    (perhaps carburized) zone was used as a measure of corrosion rates. The lowest alloyed steel had the highest corrosion rate, and the other austenitic and nickel alloys had much lower corrosion rates. Precipitates in the alloy adjacent the corrosion front were revealed for both Sanicro 28 and C‐276. However...... constructed by Brandenburg Technical University to gain understanding into oxyfuel firing. Two air‐cooled corrosion probes were exposed in this oxyfuel combustion chamber where the fuel was lignite. Gas composition was measured at the location of testing. Various alloys from a 2½ Cr steel, austenitic steels...

  13. Standard Practice for Making and Using U-Bend Stress-Corrosion Test Specimens

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2009-01-01

    1.1 This practice covers procedures for making and using U-bend specimens for the evaluation of stress-corrosion cracking in metals. The U-bend specimen is generally a rectangular strip which is bent 180° around a predetermined radius and maintained in this constant strain condition during the stress-corrosion test. Bends slightly less than or greater than 180° are sometimes used. Typical U-bend configurations showing several different methods of maintaining the applied stress are shown in Fig. 1. 1.2 U-bend specimens usually contain both elastic and plastic strain. In some cases (for example, very thin sheet or small diameter wire) it is possible to form a U-bend and produce only elastic strain. However, bent-beam (Practice G 39 or direct tension (Practice G 49)) specimens are normally used to study stress-corrosion cracking of strip or sheet under elastic strain only. 1.3 This practice is concerned only with the test specimen and not the environmental aspects of stress-corrosion testing which are discus...

  14. Evaluation of Surface Cracks Using Magnetic Flux Leakage Testing

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    The magnetic field distribution characteristics of surface cracks with various widths are discussed based on finite element (FEM) results. The crack depth was 0.20 mm, the width range was from 0.02 to 1.00 mm. The results showed that crack width and lift-off (the distance between surface and sensor) will influence signals. Discussed in this paper is the influence of various lift-off parameters on the peak to peak values of the normal component in magnetic flux leakage testing. The effects can be applied to evaluate surface breaking cracks of different widths and depths.An idea is presented to smooth narrow, sharp crack tips using alternating current (AC) field magnetization.

  15. Benefits of thread rolling process to the stress corrosion cracking and fatigue resistance of high strength fasteners

    Energy Technology Data Exchange (ETDEWEB)

    Kephart, A.R.; Hayden, S.Z.

    1993-05-01

    Stress corrosion cracking (SCC) behavior of cut (machined) vice thread rolled Alloy X-750 and Alloy 625 fasteners in a simulated high temperature primary water environment has been evaluated. SCC testing at 360 and 338C included 157 small and 40 large 60{degree} Vee thread studs. Thread rolled fasteners had improved resistance relative to cut fasteners. Tests of fatigue resistance in air at room temperature and both air and primary water at 315C were conducted on smaller studs with both cut and rolled threads. Results showed rolled threads can have significantly improved fatigue lives over those of cut threads in both air and primary water. Fasteners produced by two different thread rolling methods, in-feed (radial) and through-feed (axial), revealed similar SCC initiation test results. Testing of thread rolled fasteners revealed no significant SCC or fatigue growth of rolling induced thread crest laps typical of the thread rolling process. While fatigue resistance differed between the two rolled thread supplier`s studs, neither of the suppliers studs showed SCC initiation at exposure times beyond that of cut threads with SCC. In contrast to rolling at room temperature, warm rolled (427C) threads showed no improvement over cut threads in terms of fatigue resistance. The observed improved SCC and fatigue performance of rolled threads is postulated to be due to interactive factors, including beneficial residual stresses in critically stressed thread root region, reduction of plastic strains during loading and formation of favorable microstructure.

  16. Research on Aluminized Steel for Resisting Stress Corrosion Cracking and Hydrogen Embrittlement%渗铝钢抗应力腐蚀开裂及抗氢脆性能研究

    Institute of Scientific and Technical Information of China (English)

    吴昊; 李华飞

    2016-01-01

    以30CrMo钢为母体,对30CrMo钢及其渗铝钢分别进行抗硫化氢应力腐蚀开裂实验、抗氯离子应力腐蚀开裂实验,采用Devanathan双电池技术测量氢的扩散系数。实验结果表明:30CrMo钢渗铝后比渗铝前具有更好的抗硫化氢应力腐蚀开裂、抗氢脆性能;单一氯离子对30CrMo钢及其渗铝钢应力腐蚀开裂性能影响较小。%Using 30CrMo steel as the matrix, resistance to hydrogen sulfide stress corrosion cracking test and resistance to chloride ion stress corrosion cracking test were carried out respectively for 30CrMo steel and its aluminized steel.Using Devanathan double cell technology, and we measured hydrogen diffusion coefficient.Experimental results show that, aluminized steel of 30CrMo has better resistance to hydrogen sulfide stress corrosion cracking and hy-drogen embrittlement, and single chloride ion has little influence on the stress corrosion cracking for 30CrMo steel and its aluminized steel.

  17. Role of {delta}-ferrite in stress corrosion cracking retardation near fusion boundary of 316NG welds

    Energy Technology Data Exchange (ETDEWEB)

    Abe, Hiroshi, E-mail: hiroshi.abe@qse.tohoku.ac.jp [Graduate School of Engineering, Tohoku University, 6-6-01-2, Aoba, Aramaki, Aoba-ku, Sendai, Miyagi 980-8579 (Japan); Watanabe, Yutaka [Graduate School of Engineering, Tohoku University, 6-6-01-2, Aoba, Aramaki, Aoba-ku, Sendai, Miyagi 980-8579 (Japan)

    2012-05-15

    Stress corrosion cracking (SCC) near the fusion boundary of a 316NG stainless steel (SS) welded joint in high-temperature water was investigated with emphasis on the relation to the microstructural characteristics. {delta}-Ferrite islands were distributed on the crack paths (grain boundary in the partially melted zone and cell boundary in the unmixed zone) near the fusion boundary of 316NG SS piping. SCC retardation near the fusion boundary was clearly observed in our experiments. The relative crack growth rate (CGR) at the {delta}-{gamma} interface was estimated to be 0.043 times lower than that at the {gamma}-{gamma} interface. The cracks remained for a considerable period of time just after they reached the {delta}-ferrite islands. Even those cracks that passed through an initial set of {delta}-ferrite islands were retarded when they encountered a subsequent set of {delta}-ferrite islands. High corrosion resistance due to the presence of large amounts of Cr and the island-shaped morphology of {delta}-ferrite are dominant factors in SCC retardation.

  18. Effect of solution pH on the electrochemical polarization and stress corrosion cracking of Alloy 690 in 5 M NaCl at room temperature

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Y.Y. [Department of Materials Science and Engineering, National Tsing Hua University, 101, Sec. 2, Kuang Fu Road, Hsinchu 300, Taiwan (China); Chou, L.B. [Department of Materials Science and Engineering, National Tsing Hua University, 101, Sec. 2, Kuang Fu Road, Hsinchu 300, Taiwan (China); Shih, H.C. [Department of Materials Science and Engineering, National Tsing Hua University, 101, Sec. 2, Kuang Fu Road, Hsinchu 300, Taiwan (China)]. E-mail: hcshih@mse.nthu.edu.tw

    2005-04-15

    The effect of solution pH on the electrochemical polarization and stress corrosion cracking behaviors of the nickel-based Alloy 690 were investigated in this paper. An experimental, potential-pH diagram was constructed for Alloy 690 in a concentrated (5 M) sodium chloride (NaCl) solution at room temperature ({approx}25 deg. C), using a cyclic polarization method. The domains of immunity, general corrosion, passivation, and pitting in 5 M NaCl solutions were defined. At pH >4, the passive region subdivided into areas of perfect passivation, imperfect passivation, and pitting. After anodic polarization, the surface of each specimen was carefully examined metallographically. Pitting corrosion was observed over the entire pH range investigated (0.3-8.52) but general corrosion predominated at lower pH values (<3). On the other hand, the mechanical properties, such as ultimate tensile strength (UTS), fracture strain (FS) and the reduction in area (RA) measured by the slow strain rate test (SSRT), decreased significantly at pH <3. The SSRT results are consistent with fractography and side-view observations of the tested specimens by scanning electron microscopy (SEM)

  19. The use of slow strain rate technique for studying stress corrosion cracking of an advanced silver-bearing aluminum-lithium alloy

    Science.gov (United States)

    Frefer, Abdulbaset Ali; Abosdell, Alajale M.; Raddad, Bashir S.

    2013-12-01

    In the present study, stress corrosion cracking (SCC) behavior of naturally aged advanced silver-bearing Al-Li alloy in NaCl solution was investigated using slow strain rate test (SSRT) method. The SSRT's were conducted at different strain rates and applied potentials at room temperature. The results were discussed based on percent reductions in tensile elongation in a SCC-causing environment over those in air tended to express the SCC susceptbility of the alloy under study at T3. The SCC behavior of the alloy was also discussed based on the microstructural and fractographic examinations.

  20. The use of slow strain rate technique for studying stress corrosion cracking of an advanced silver-bearing aluminum-lithium alloy

    Energy Technology Data Exchange (ETDEWEB)

    Frefer, Abdulbaset Ali; Raddad, Bashir S. [Department of Mechanical and Industrial Engineering/Tripoli University, Tripoli (Libya); Abosdell, Alajale M. [Department of Mechanical Engineering/Mergeb University, Garaboli (Libya)

    2013-12-16

    In the present study, stress corrosion cracking (SCC) behavior of naturally aged advanced silver-bearing Al-Li alloy in NaCl solution was investigated using slow strain rate test (SSRT) method. The SSRT’s were conducted at different strain rates and applied potentials at room temperature. The results were discussed based on percent reductions in tensile elongation in a SCC-causing environment over those in air tended to express the SCC susceptbility of the alloy under study at T3. The SCC behavior of the alloy was also discussed based on the microstructural and fractographic examinations.

  1. TEM characterisation of stress corrosion cracks in nickel based alloys: effect of chromium content and chemistry of environment; Caracterisation par MET de fissures de corrosion sous contrainte d'alliages a base de nickel: influence de la teneur en chrome et de la chimie du milieu

    Energy Technology Data Exchange (ETDEWEB)

    Delabrouille, F

    2004-11-15

    Stress corrosion cracking (SCC) is a damaging mode of alloys used in pressurized water reactors, particularly of nickel based alloys constituting the vapour generator tubes. Cracks appear on both primary and secondary sides of the tubes, and more frequently in locations where the environment is not well defined. SCC sensitivity of nickel based alloys depends of their chromium content, which lead to the replacement of alloy 600 (15 % Cr) by alloy 690 (30 % Cr) but this phenomenon is not yet very well understood. The goal of this thesis is two fold: i) observe the effect of chromium content on corrosion and ii) characterize the effect of environment on the damaging process of GV tubes. For this purpose, one industrial tube and several synthetic alloys - with controlled chromium content - have been studied. Various characterisation techniques were used to study the corrosion products on the surface and within the SCC cracks: SIMS; TEM - FEG: thin foil preparation, HAADF, EELS, EDX. The effect of chromium content and surface preparation on the generalised corrosion was evidenced for synthetic alloys. Moreover, we observed the penetration of oxygen along triple junctions of grain boundaries few micrometers under the free surface. SCC tests show the positive effect of chromium for contents varying from 5 to 30 % wt. Plastic deformation induces a modification of the structure, and thus of the protective character, of the internal chromium rich oxide layer. SCC cracks which developed in different chemical environments were characterised by TEM. The oxides which are formed within the cracks are different from what is observed on the free surface, which reveals a modification of medium and electrochemical conditions in the crack. Finally we were able to evidence some structural characteristics of the corrosion products (in the cracks and on the surface) which turn to be a signature of the chemical environment. (author)

  2. Stress-Corrosion Cracking in High Strength Steels and in Titanium and Aluminum Alloys

    Science.gov (United States)

    1972-01-01

    widely throughout the technical community and is not available in collected form, the authors of the chapter on titanium have included a much higher...Elements................ 22 Derivation of KI by Specimen Compliance.............. 23 Experiental Determination of Comll-!hlncc........... 24 Theoretical...101. R. T. Ault, Republic Steel Corp., private communication . 102. S. R. Novak and S. T. Rolfe, Kt, Stress-Corrosion Tests of l2Ni-5Cr-3Mo and l8Ni

  3. The Role of Stress in the Corrosion Cracking of Aluminum Alloys

    Science.gov (United States)

    2013-03-01

    orthogonal to the other two directions. This system is used for sheet, extrusions , and forgings with nonsymmetrical grain flow [18]. All testing...around the constituent particles and then spreads to the grain boundaries. It is not possible to determine from the present results if the IGC...International, 2011, pp.1-8. [30] J. R. Scully et al., " Spreading of intergranular corrosion on the surface of sensitized Al-4.4Mg alloys: A general finding

  4. Electrochemical properties and stress corrosion cracking of alloys 600, 690, and 800 in solutions containing boric acid and chloride

    Energy Technology Data Exchange (ETDEWEB)

    Bae, J. H.; Won, C. H. [Chungnam Nation Univ., Taejon (Korea, Republic of); Lee, E. H.; Kim, H. P.; Kim, W. C. [KAERI, Taejon (Korea, Republic of)

    2000-10-01

    Electrochemical characteristics and stress corrosion cracking(SCC)of Alloy 600, Alloy 690 and Alloy 800 have been studied in boric acid solution with chloride. Electrochemical characteristics were measured in mixed solution of 3% H{sub 3}BO{sub 3} and 0.2g/l Cl{sup -} at 320 .deg. C. SCC resistance was predicted with Parameter(P{sub SCC}) including current density ratio obtained at two different scan rates. P{sub SCC} increased with a following sequence: Alloy 600MA, 600TT, 690TT and Alloy 800. SCC test was carried out with C-ring specimens and reverse U-bend(RUB) specimens at 320 .deg. C and 350 .deg. C. Test solutions were mixture of 3% H{sub 3}BO{sub 3} and 0.2g/l Cl{sup -} at 320 .deg. C and mixture of 27% H{sub 3}BO{sub 3} and 2g/l Cl{sup -} at 350 .deg. C. C-ring specimens test in the solution of 3% H{sub 3}BO{sub 3} and 0.2g/l Cl{sup -} at 320 .deg. C for 2400hrs did not show SCC. RUB specimen of Alloy600MA and 600TT showed SCC after 1920 hours exposure to the solution of 27% H{sub 3}BO{sub 3} and 0.2g/l Clat 350 .deg. C.

  5. The Influence of Composition upon Surface Degradation and Stress Corrosion Cracking of the Ni-Cr-Mo Alloys in Wet Hydrofluoric Acid

    Energy Technology Data Exchange (ETDEWEB)

    Crook, P; Meck, N S; Rebak, R B

    2006-12-04

    At concentrations below 60%, wet hydrofluoric acid (HF) is extremely corrosive to steels, stainless steels and reactive metals, such as titanium, zirconium, and tantalum. In fact, only a few metallic materials will withstand wet HF at temperatures above ambient. Among these are the nickel-copper (Ni-Cu) and nickel-chromium-molybdenum (Ni-Cr-Mo) alloys. Previous work has shown that, even with these materials, there are complicating factors. For example, under certain conditions, internal attack and stress corrosion cracking (SCC) are possible with the Ni-Cr-Mo alloys, and the Ni-Cu materials can suffer intergranular attack when exposed to wet HF vapors. The purpose of this work was to study further the response of the Ni-Cr-Mo alloys to HF, in particular their external corrosion rates, susceptibility to internal attack and susceptibility to HF-induced SCC, as a function of alloy composition. As a side experiment, one of the alloys was tested in two microstructural conditions, i.e. solution annealed (the usual condition for materials of this type) and long-range ordered (this being a means of strengthening the alloy in question). The study of external corrosion rates over wide ranges of concentration and temperature revealed a strong beneficial influence of molybdenum content. However, tungsten, which is used as a partial replacement for molybdenum in some Ni-Cr-Mo alloys, appears to render the alloys more prone to internal attack. With regard to HF-induced SCC of the Ni-Cr-Mo alloys, this study suggests that only certain alloys (i.e., those containing tungsten) exhibit classical SCC. It was also discovered that high external corrosion rates inhibit HF-induced SCC, presumably due to rapid progression of the external attack front. With regard to the effects of long-range ordering, these were only evident at the highest test temperatures, where the ordered structure exhibited much higher external corrosion rates than the annealed structure.

  6. The Influence of Composition upon Surface Degradation and Stress Corrosion Cracking of the Ni-Cr-Mo Alloys in Wet Hydrofluoric Acid

    Energy Technology Data Exchange (ETDEWEB)

    Crook, P; Meck, N S; Rebak, R B

    2006-12-04

    At concentrations below 60%, wet hydrofluoric acid (HF) is extremely corrosive to steels, stainless steels and reactive metals, such as titanium, zirconium, and tantalum. In fact, only a few metallic materials will withstand wet HF at temperatures above ambient. Among these are the nickel-copper (Ni-Cu) and nickel-chromium-molybdenum (Ni-Cr-Mo) alloys. Previous work has shown that, even with these materials, there are complicating factors. For example, under certain conditions, internal attack and stress corrosion cracking (SCC) are possible with the Ni-Cr-Mo alloys, and the Ni-Cu materials can suffer intergranular attack when exposed to wet HF vapors. The purpose of this work was to study further the response of the Ni-Cr-Mo alloys to HF, in particular their external corrosion rates, susceptibility to internal attack and susceptibility to HF-induced SCC, as a function of alloy composition. As a side experiment, one of the alloys was tested in two microstructural conditions, i.e. solution annealed (the usual condition for materials of this type) and long-range ordered (this being a means of strengthening the alloy in question). The study of external corrosion rates over wide ranges of concentration and temperature revealed a strong beneficial influence of molybdenum content. However, tungsten, which is used as a partial replacement for molybdenum in some Ni-Cr-Mo alloys, appears to render the alloys more prone to internal attack. With regard to HF-induced SCC of the Ni-Cr-Mo alloys, this study suggests that only certain alloys (i.e., those containing tungsten) exhibit classical SCC. It was also discovered that high external corrosion rates inhibit HF-induced SCC, presumably due to rapid progression of the external attack front. With regard to the effects of long-range ordering, these were only evident at the highest test temperatures, where the ordered structure exhibited much higher external corrosion rates than the annealed structure.

  7. Layer texture of hot-rolled BCC metals and its significance for stress-corrosion cracking of main gas pipelines

    Science.gov (United States)

    Perlovich, Yu. A.; Isaenkova, M. G.; Krymskaya, O. A.; Morozov, N. S.

    2016-10-01

    Based on data of X-ray texture analysis of hot-rolled BCC materials it was shown that the layerwise texture inhomogeneity of products is formed during their manufacturing. The effect can be explained by saturation with interstitial impurities of the surface layer, resulting in dynamical deformation aging (DDA). DDA prevents the dislocation slip under rolling and leads to an increase of lattice parameters in the external layer. The degree of arising inhomogeneity correlates with the tendency of hot-rolled sheets and obtained therefrom tubes to stress-corrosion cracking under exploitation, since internal layers have a compressive effect on external layers, and prevents opening of corrosion cracks at the tube surface.

  8. Selectable-Tip Corrosion-Testing Electrochemical Cell

    Science.gov (United States)

    Lomness, Janice; Hintze, Paul

    2008-01-01

    The figure depicts aspects of an electrochemical cell for pitting- corrosion tests of material specimens. The cell is designed to generate a region of corrosion having a pit diameter determined by the diameter of a selectable tip. The average depth of corrosion is controlled by controlling the total electric charge passing through the cell in a test. The cell is also designed to produce minimal artifacts associated with crevice corrosion. There are three selectable tips, having diameters of 0.1 in. (0.254 cm), 0.3 in. (0.762 cm), and 0.6 in. (1.524 cm), respectively.

  9. Synthetic seawater as stress-corrosion test medium

    Science.gov (United States)

    Humphries, T. S.; Nelson, E. E.

    1980-01-01

    Seawater minimizes pitting corrosion of aluminum-alloy test samples. Of three corrosion-inhibiting methods evaluated using (a) chromate inhibitors in saltwater, (b) surface treating sample via anodizing or alodine treatment, and (c) synthetic seawater, synthetic seawater was most effective test medium, since it is more uniform than fresh seawater.

  10. Effect of deteriorated microstructures on stress corrosion cracking of X70 pipeline steel in acidic soil environment

    Institute of Scientific and Technical Information of China (English)

    2008-01-01

    In order to investigate stress corrosion cracking (SCC) of X70 pipeline steel and its weld joint area in acidic soil environmeat in China,two simulating methods were used: one was to obtain bad mierostructures in heat affected zone by annealing at 1300℃ for 10 rain and then,quenching in water; the other was to get different simulating solutions of acidic soil in Yingtan in southeast China.The SCC susceptibilities of X70 pipeline steel before and after quenching in the simulating solutions were analyzed using slow stain rate test (SSRT) and poteatiodynamic polarization technique to investigate the SCC electrochemical mechanism of different mierostruetures further.The results show that SCC appears in the original mierostrueture and the quenched mierostructure as the polarization potential decreases.Hydrogen revolution accelerates SCC of the two tested materials within the range of-850 mV to -1200 mV vs.SCE.Microstructural hardening and grain coarsening also increase SCC.The SCC mechanisms are different,anodic dissolution is the key of causing SCC as the polarization potential is higher than the null eurreat potential,and hydrogen embrittlemeat will play a more important role to SCC as the polarization potential lower than the null current potential.

  11. The influence of long term use of inhibitors in hydrochloric acid pickling baths on hydrogen induced stress corrosion cracking

    Energy Technology Data Exchange (ETDEWEB)

    Feser, R.; Friedrich, A.; Scheide, F. [Fachhochschule Suedwestfalen, University of Applied Science, Frauenstuhlweg 31, D-58644 Iserlohn (Germany)

    2002-09-01

    The influence of commercially available inhibitors on the absorption of hydrogen by steel (St 52, StE 460, StE 690, 42CrMo4) in 15% hydrochloric acid was studied. The pickling bath aged continuously due to the chemical reaction with oxidized steel sheets. The H{sup +}- and inhibitor concentration decreased with time. The influence of this ageing process on hydrogen-induced stress corrosion cracking was tested by in-situ tensile tests in the bath solution. With increasing ageing of the bath, the reduction in fracture area was reduced and approached the values measured for non-inhibited acid baths. Furthermore hydrogen permeation was investigated. Permeation current densities rose with increasing ageing of the pickling solution. (Abstract Copyright[2002], Wiley Periodicals, Inc.) [German] Der Einfluss von kommerziell erhaeltlichen Inhibitoren auf die Wasserstoffabsorption von Stahl (St 52, StE 460, StE 690, 42CrMo4) wurde in Salzsaeure untersucht. Die Beizbaeder wurden kontinuierlich durch die chemische Reaktion mit oxidierten Stahlblechen gealtert. Die H{sup +}- und Inhibitorkonzentration nahm mit der Zeit ab. Der Einfluss dieses Alterungsprozesses auf die wasserstoffinduzierte Spannungsrisskorrosion wurde durch in-situ Zugversuche mit Badloesung untersucht. Mit zunehmender Alterung des Bades nahm die Brucheinschnuerung ab und erreichte Werte wie sie auch in der nicht inhibierten Saeure erreicht werden. Weiterhin wurde die Wasserstoff-Permeation untersucht. Die Permeationsstromdichte steigt mit zunehmender Alterung der Beizloesung. (Abstract Copyright[2002], Wiley Periodicals, Inc.)

  12. Effects of applied potential on the stress corrosion cracking behavior of 7003 aluminum alloy in acid and alkaline chloride solutions

    Science.gov (United States)

    Zhang, Xiao-yan; Song, Ren-guo; Sun, Bin; Lu, Hai; Wang, Chao

    2016-07-01

    Potentiodynamic polarization tests and slow strain rate test (SSRT) in combination with fracture morphology observations were conducted to investigate the stress corrosion cracking (SCC) behavior of 7003 aluminum alloy (AA7003) in acid and alkaline chloride solutions under various applied potentials ( E a). The results show that AA7003 is to a certain extent susceptible to SCC via anodic dissolution (AD) at open-circuit potential (OCP) and is highly susceptible to hydrogen embrittlement (HE) at high negative E a in the solutions with pH levels of 4 and 11. The susceptibility increases with negative shift in the potential when E a is less than -1000 mV vs. SCE. However, the susceptibility distinctly decreases because of the inhibition of AD when E a is equal to -1000 mV vs. SCE. In addition, the SCC susceptibility of AA7003 in the acid chloride solution is higher than that in the alkaline solution at each potential. Moreover, the effect of hydrogen on SCC increases with increasing hydrogen ion concentration.

  13. The effects of cold rolling orientation and water chemistry on stress corrosion cracking behavior of 316L stainless steel in simulated PWR water environments

    Science.gov (United States)

    Chen, Junjie; Lu, Zhanpeng; Xiao, Qian; Ru, Xiangkun; Han, Guangdong; Chen, Zhen; Zhou, Bangxin; Shoji, Tetsuo

    2016-04-01

    Stress corrosion cracking behaviors of one-directionally cold rolled 316L stainless steel specimens in T-L and L-T orientations were investigated in hydrogenated and deaerated PWR primary water environments at 310 °C. Transgranular cracking was observed during the in situ pre-cracking procedure and the crack growth rate was almost not affected by the specimen orientation. Locally intergranular stress corrosion cracks were found on the fracture surfaces of specimens in the hydrogenated PWR water. Extensive intergranular stress corrosion cracks were found on the fracture surfaces of specimens in deaerated PWR water. More extensive cracks were found in specimen T-L orientation with a higher crack growth rate than that in the specimen L-T orientation with a lower crack growth rate. Crack branching phenomenon found in specimen L-T orientation in deaerated PWR water was synergistically affected by the applied stress direction as well as the preferential oxidation path along the elongated grain boundaries, and the latter was dominant.

  14. Adaptation of Crack Growth Detection Techniques to US Material Test Reactors

    Energy Technology Data Exchange (ETDEWEB)

    A. Joseph Palmer; Sebastien P. Teysseyre; Kurt L. Davis; Joy L. Rempe; Gordon Kohse; Yakov Ostrovsky; David M. Carpenter

    2014-04-01

    A key component in evaluating the ability of Light Water Reactors to operate beyond 60 years is characterizing the degradation of materials exposed to radiation and various water chemistries. Of particular concern is the response of reactor materials to Irradiation Assisted Stress Corrosion Cracking (IASCC). Some materials testing reactors (MTRs) outside the U.S., such as the Halden Boiling Water Reactor (HBWR), have deployed a technique to measure crack growth propagation during irradiation. This technique incorporates a compact loading mechanism to stress the specimen during irradiation. A crack in the specimen is monitored using the Direct Current Potential Drop (DCPD) method. A project is underway to develop and demonstrate the performance of a similar type of test rig for use in U.S. MTRs. The first year of this three year project was devoted to designing, analyzing, fabricating, and bench top testing a mechanism capable of applying a controlled stress to specimens while they are irradiated in a pressurized water loop (simulating PWR reactor conditions). During the second year, the mechanism will be tested in autoclaves containing high pressure, high temperature water with representative water chemistries. In addition, necessary documentation and safety reviews for testing in a reactor environment will be completed. In the third year, the assembly will be tested in the Massachusetts Institute of Technology Reactor (MITR) and Post Irradiation Examinations (PIE) will be performed.

  15. Accelerated corrosion testing, evaluation and durability design of bonded post-tensioned concrete tendons

    Science.gov (United States)

    Salas Pereira, Ruben Mario

    2003-06-01

    In the last few years, the effectiveness of cement grout in galvanized or polyethylene ducts, the most widely used corrosion protection system for multistrand bonded post-tensioned concrete tendons, has been under debate, due to significant tendon corrosion damage, several reported failures of individual tendons as well as a few collapses of non-typical structures. While experience in the USA has been generally good, some foreign experience has been less than satisfactory. This dissertation is part of a comprehensive research program started in 1993, which has the objectives to examine the use of post-tensioning in bridge substructures, identify durability concerns and existing technology, develop and carry out an experimental testing program, and conclude with durability design guidelines. Three experimental programs were developed: A long term macrocell corrosion test series, to investigate corrosion protection for internal tendons in precast segmental construction; a long term beam corrosion test series, to examine the effects of post-tensioning on corrosion protection as affected by crack width; and, a long term column corrosion test series, to examine corrosion protection in vertical elements. Preliminary design guidelines were developed previously in the overall study by the initial researchers, after an extensive literature review. This dissertation scope includes continuation of exposure testing of the macrocell, beam and column specimens, performing comprehensive autopsies of selected specimens and updating the durability design guidelines based on the exposure testing and autopsy results. After autopsies were performed, overall findings indicate negative durability effects due to the use of mixed reinforcement, small concrete covers, galvanized steel ducts, and industry standard or heat-shrink galvanized duct splices. The width of cracks was shown to have a direct negative effect on specimen performance. Grout voids were found to be detrimental to the

  16. Equivalent Crack Size Modelling of Corrosion Pitting in an AA7050-T7451 Aluminium Alloy and its Implications for Aircraft Structural Integrity

    Science.gov (United States)

    2012-09-01

    provides a quantitative measurement of the spatial density of pits14 but there is no quantitative measurement of corrosion pit metrics without...and stress corrosion cracking in the 7075 T6 components of the RAAF C-130 Hercules...Post-Fracture Examination................................................................... 16 3.5.3 Surface Roughness Measurement

  17. NASA's Beachside Corrosion Test Site and Current Environmentally Friendly Corrosion Control Initiatives

    Science.gov (United States)

    Russell, Richard W.; Calle, Luz Marina; Johnston, Frederick; Montgomery, Eliza L.; Curran, Jerome P.; Kolody, Mark R.

    2013-01-01

    NASA began corrosion studies at the Kennedy Space Center (KSC) in 1966 during the Gemini/Apollo Programs with the evaluation of long-term corrosion protective coatings for carbon steel. KSC's Beachside Corrosion Test Site (BCTS), which has been documented by the American Society of Materials (ASM) as one of the most corrosive, naturally occurring, environments in the world, was established at that time. With the introduction of the Space Shuttle in 1981, the already highly corrosive conditions at the launch pad were rendered even more severe by the acid ic exhaust from the solid rocket boosters. In the years that followed, numerous studies have identified materials, coatings, and maintenance procedures for launch hardware and equipment exposed to the highly corrosive environment at the launch pad. This paper presents a historical overview of over 45 years of corrosion and coating evaluation studies and a description of the BCTS's current capabilities. Additionally, current research and testing programs involving chromium free coatings, environmentally friendly corrosion preventative compounds, and alternates to nitric acid passivation will be discussed.

  18. Dynamical observations on the crack tip zone and stress corrosion of two-dimensional MoS2

    Science.gov (United States)

    Ly, Thuc Hue; Zhao, Jiong; Cichocka, Magdalena Ola; Li, Lain-Jong; Lee, Young Hee

    2017-01-01

    Whether and how fracture mechanics needs to be modified for small length scales and in systems of reduced dimensionality remains an open debate. Here, employing in situ transmission electron microscopy, atomic structures and dislocation dynamics in the crack tip zone of a propagating crack in two-dimensional (2D) monolayer MoS2 membrane are observed, and atom-to-atom displacement mapping is obtained. The electron beam is used to initiate the crack; during in situ observation of crack propagation the electron beam effect is minimized. The observed high-frequency emission of dislocations is beyond previous understanding of the fracture of brittle MoS2. Strain analysis reveals dislocation emission to be closely associated with the crack propagation path in nanoscale. The critical crack tip plastic zone size of nearly perfect 2D MoS2 is between 2 and 5 nm, although it can grow to 10 nm under corrosive conditions such as ultraviolet light exposure, showing enhanced dislocation activity via defect generation.

  19. Dynamical observations on the crack tip zone and stress corrosion of two-dimensional MoS2

    KAUST Repository

    Ly, Thuc Hue

    2017-01-18

    Whether and how fracture mechanics needs to be modified for small length scales and in systems of reduced dimensionality remains an open debate. Here, employing in situ transmission electron microscopy, atomic structures and dislocation dynamics in the crack tip zone of a propagating crack in two-dimensional (2D) monolayer MoS2 membrane are observed, and atom-to-atom displacement mapping is obtained. The electron beam is used to initiate the crack; during in situ observation of crack propagation the electron beam effect is minimized. The observed high-frequency emission of dislocations is beyond previous understanding of the fracture of brittle MoS2. Strain analysis reveals dislocation emission to be closely associated with the crack propagation path in nanoscale. The critical crack tip plastic zone size of nearly perfect 2D MoS2 is between 2 and 5 nm, although it can grow to 10 nm under corrosive conditions such as ultraviolet light exposure, showing enhanced dislocation activity via defect generation.

  20. Corrosion testing of urea-formaldehyde foam insulating material

    Energy Technology Data Exchange (ETDEWEB)

    Weil, R.; Graviano, A.; Sheppard, K.

    1980-09-01

    Two tests of the corrosiveness of urea-formaldehyde (UF) foam insulating materials were compared. One test, the Timm test, had test coupons foamed in place. In the second, the Canadian test, blocks of foam already set were placed in contact with test coupons. The Timm test uses 10 gage thick coupons, while the Canadian test specifies 3 mil thick ones. Two samples of UF foam were tested by the Timm and the Canadian tests. The electrical-resistance probes showed that the corrosion rate against steel was initially quite high, of the order of 12 to 20 mpy (mils per year). After about 20 days, the rate was almost zero. In the Timm test, the corrosion rates of steel coupons were of the order to 0.5 to 2 mpy when averaged over the 28 or 56 day test period. The greater corrosion rate of the thick coupons in the Canadian test as well as poor reproducibility of the corrosion rates was attributed primarily to variations in the contact areas between the sample and the UF foam. The corrosion rates of galvanized steel coupons in the Canadian test in several cases exceeded the failure value. In the Timm test, the corrosion rates averaged over the whole test period were quite low. The corrosion rates of copper and aluminum in both tests were quite low. On the basis of the results of this study the following recommendations for a corrosion-test procedure for UF foam were made: two corrosion tests should be conducted, one for foam while curing and one after it has stabilized; the Timm test for corrosiveness while curing should be used, but for only 1 to 2 days; the test for corrosiveness after stabilizing should be of the accelerated type such as the Canadian one. To insure a constant-contact area, thicker coupons should be used; and the coupons for both tests should have a controlled part of the area not in contact with the foam to simulate field conditions.

  1. Microstructure, local mechanical properties and stress corrosion cracking susceptibility of an SA508-52M-316LN safe-end dissimilar metal weld joint by GTAW

    Energy Technology Data Exchange (ETDEWEB)

    Ming, Hongliang; Zhu, Ruolin [Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning KeyLaboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); University of Chinese Academy of Sciences, 19 Yuquan Road, Beijing 100049 (China); Zhang, Zhiming [Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning KeyLaboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Wang, Jianqiu, E-mail: wangjianqiu@imr.ac.cn [Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning KeyLaboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Han, En.-Hou.; Ke, Wei [Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning KeyLaboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Su, Mingxing [Shanghai Research Center for Weld and Detection Engineering Technique of Nuclear Equipment, Shanghai 201306 (China)

    2016-07-04

    The microstructure, local mechanical properties and local stress corrosion cracking susceptibility of an SA508-52M-316LN domestic dissimilar metal welded safe-end joint used for AP1000 nuclear power plant prepared by automatic gas tungsten arc welding was studied in this work by optical microscopy, scanning electron microscopy (with electron back scattering diffraction and an energy dispersive X-ray spectroscopy system), micro-hardness testing, local mechanical tensile testing and local slow strain rate tests. The micro-hardness, local mechanical properties and stress corrosion cracking susceptibility across this dissimilar metal weld joint vary because of the complex microstructure across the fusion area and the dramatic chemical composition change across the fusion lines. Briefly, Type I boundaries and Type II boundaries exist in 52Mb near the SA508-52Mb interface, a microstructure transition was found in SA508 heat affected zone, the residual strain and grain boundary character distribution changes as a function of the distance from the fusion boundary in 316LN heat affected zone, micro-hardness distribution and local mechanical properties along the DMWJ are heterogeneous, and 52Mw-316LN interface has the highest SCC susceptibility in this DMWJ while 316LN base metal has the lowest one.

  2. A state of the art on primary side stress corrosion cracking in nuclear power plant

    Energy Technology Data Exchange (ETDEWEB)

    Kim, H. P.; Kim, J. S.; Han, J. H.; Lee, D. H.; Lim, Y. S.; Suh, J. H.; Hwang, S. S.; Hur, D. H

    1999-09-01

    A state of art on primary water stress corrosion cracking (PWSCC) of alloy 600 used as steam generator tubing of nuclear power plant and remedial action on the PWSCC were reviewed and analyzed. One of the major metallurgical factors which have effect on PWSCC is Cr carbide distribution. A semicontinuous intergranular Cr carbide distribution enhance PWSCC of alloy 600. PWSCC rate is reported to be reported to be proportional to exp(-50 cal/RT) {sigma}{sup 4}. PWSCC rate also increase with increase in hydrogen partial pressure from 0 to 150 ppm and then decreased with further increase in hydrogen partial pressure to 757 ppm. Development of PWSCC prediction technology which takes into account tubing material, fabrication process and operating history of steam generator is needed to manage PWSCC of domestic nuclear power plant. PWSCC has mainly occurred at expansion irregularities within tubesheet, expansion transitions, dented tube support plate intersections and transition and apex of U bend. Remedial actions to PWSCC are sleeving, plugging, temperature reduction, Ni plating, Ni sleeving, shot peening and steam generator replacement in worst case. Option to remedial actions depend on plant specific such as plant age, leak rate from primary to secondary, density and progression of PWSCC. Ni sleeving developed in Framatome seems to be a powerful method because it never subject to PWSCC. Remedial action should be developed and evaluated for possible PWSCC of domestic nuclear power plant. (author)

  3. Humidity Testing of PME and BME Ceramic Capacitors with Cracks

    Science.gov (United States)

    Teverovsky, Alexander A.; Herzberger, Jaemi

    2014-01-01

    Cracks in ceramic capacitors are one of the major causes of failures during operation of electronic systems. Humidity testing has been successfully used for many years to verify the absence of cracks and assure quality of military grade capacitors. Traditionally, only precious metal electrode (PME) capacitors were used in high reliability applications and the existing requirements for humidity testing were developed for this type of parts. With the advance of base metal electrode (BME) capacitors, there is a need for assessment of the applicability of the existing techniques for the new technology capacitors. In this work, variety of different PME and BME capacitors with introduced cracks were tested in humid environments at different voltages and temperatures. Analysis of the test results indicates differences in the behavior and failure mechanisms for BME and PME capacitors and the need for different testing conditions.

  4. Fabrication of Test Tubes for Coal Ash Corrosion Testing

    Energy Technology Data Exchange (ETDEWEB)

    Johnson, R.; Judkins, R.R.; Sikka, V.K.; Swindeman, R.W.; Wright, I.G.

    1999-05-11

    This paper deals with the fabrication of tube sections of four alloys for incorporating into test sections to be assembled by Babcock & Wilcox (B&W) for installation at Ohio Edison Power, Niles Plant. The primary purpose of the installation was to determine the corrosion behavior of ten different alloys for flue gas corrosion. Ohio Edison Power, Niles Plant is burning an Ohio coal containing approximately 3.4% S (dry basis) and approximately 0.4% alkali which causes chronic coal ash corrosion of the unit�s superheater tubing. The 2.5-in.-OD x 0.4in.-wall x 6-in-long sections of four alloys {type 304H coated with Fe3Al alloy FAS [developed at the Oak Ridge National Laboratory (ORNL)], 310 + Ta, modified 800H, and Thermie alloy} were fabricated at ORNL. Each alloy tubing was characterized in terms of chemical analysis and microstructure. The machined tubes of each of the alloys were inspected and shipped on time for incorporation into the test loop fabricated at B&W. Among the alloys fabricated, Thermie was the hardest to extrude and machine.

  5. Corrosion rate of steel embedded in blended Portland and fluid catalytic cracking catalyst residue (FC3R cement mortars

    Directory of Open Access Journals (Sweden)

    Payá, J.

    2008-12-01

    Full Text Available This paper reports on a study of the corrosion levels in steel bars embedded in mortars made with a blend of Portland cement and (0-20% spent fluid catalytic cracking catalyst residue (FC3R, with a variable (0.3-0.7 water/binder (w/b ratio. The specimens were stored in the following conditions: relative humidity of 40, 80 or 100% and CO2 concentrations of 5 and 100%. The steel corrosion rate was measured with polarization resistance techniques. In the absence of aggressive agents, the steel was found to remain duly passivated in mortars with an FC3R content of up to 15% under all the conditions of relative humidity tested. The reinforcement corrosion level in mortars with a w/b ratio of 0.3 and 15% FC3R subjected to accelerated carbonation was similar to the level observed in the unblended Portland cement control mortar.En este trabajo se ha estudiado el nivel de corrosión de barras de acero embebidas en morteros de cemento Portland con relación agua/material cementante (a/mc variable (0,3-0,7, en los que parte del cemento (0-20% se sustituyó por catalizador de craqueo usado (FC3R. Las condiciones de conservación de las probetas elaboradas fueron las siguientes: distintas humedades relativas (40, 80 y 100% y dos concentraciones de CO2 (5 y 100%. La velocidad de corrosión de los aceros se midió mediante la técnica de resistencia de polarización. Se ha podido determinar que, bajo las distintas condiciones de humedad relativa y ausencia de agresivo, los aceros se mantuvieron correctamente pasivados en los morteros con contenidos de FC3R de hasta el 15%. El nivel de corrosión que presenta el refuerzo embebidos en morteros con sustitución de un 15% de cemento por FC3R y relación a/mc 0,3, al ser sometidos a un proceso de carbonatación acelerada, era muy similar al mostrado por el mortero patrón, sin FC3R.

  6. Evaluation of the resistance of API 5L-X80 girth welds to sulphide stress corrosion cracking and hydrogen embrittlement

    Energy Technology Data Exchange (ETDEWEB)

    Forero, Adriana [Pontificia Universidade Catolica (PUC-Rio), Rio de Janeiro, RJ (Brazil); Ponciano, Jose A. [Universidade Federal do Rio de Janeiro (COPPE/UFRJ), RJ (Brazil). Coordenacao dos Programas de Pos-graduacao em Engenharia; Bott, Ivani de S. [Pontificia Universidade Catolica do Rio de Janeiro (PUC-Rio), Rio de Janeiro, RJ (Brazil). Dept. de Ciencia dos Materiais e Metalurgia

    2009-07-01

    The susceptibility of pipeline steels to stress corrosion cracking (SCC) depends on a series of factors ranging from the manufacture of the steel, the pipe fabrication and the assembly of the pipeline to the type of substances to be transported. The welding procedures adopted during the production and construction of the pipelines (field welding), can modify the properties of the base metal in the heat affected zone (HAZ), potentially rendering this region susceptible to SCC. This study evaluates the resistance of girth welds, in API 5L X80 pipes, to hydrogen embrittlement and to stress corrosion cracking in the presence of sulphides. The evaluation was performed according to NACE TM0177/96, Method A, applying the criterion of fracture/no fracture, and Slow Strain Rate Tensile tests (SSRT) were undertaken using a sodium thiosulphate solution according to the ASTM G129-00 Standard. According NACE requirements, the base metal was approved. The weld metal exhibited susceptibility to SCC in the presence of sulphides, failing in a period of less than 720h. This was confirmed by SSR tensile tests, where a significant decrease in the ultimate tensile strength, the elongation and the time to fracture were observed. The mechanism of fracture was transgranular. (author)

  7. The stress-corrosion behavior of Al-Li-Cu alloys: A comparison of test methods

    Science.gov (United States)

    Rizzo, P. P.; Galvin, R. P.; Nelson, H. G.

    1982-01-01

    Two powder metallurgy processed (Al-Li-Cu) alloys with and without Mg addition were studied in aqueous 3.5% NaCl solution during the alternate immersion testing of tuning fork specimens, slow crack growth tests using fracture mechanics specimens, and the slow strain rate testing of straining electrode specimens. Scanning electron microscopy and optical metallography were used to demonstrate the character of the interaction between the Al-Li-Cu alloys and the selected environment. Both alloys are susceptible to SC in an aqueous 3.5% NaCl solution under the right electrochemical and microstructural conditions. Each test method yields important information on the character of the SC behavior. Under all conditions investigated, second phase particles strung out in rows along the extrusion direction in the alloys were rapidly attacked, and played principal role in the SC process. With time, larger pits developed from these rows of smaller pits and under certain electrochemical conditions surface cracks initiated from the larger pits and contributed directly to the fracture process. Evidence to support slow crack growth was observed in both the slow strain rate tests and the sustained immersion tests of precracked fracture mechanics specimens. The possible role of H2 in the stress corrosion cracking process is suggested.

  8. Recent progress to understand stress corrosion cracking in sodium borosilicate glasses: linking the chemical composition to structural, physical and fracture properties

    Science.gov (United States)

    Rountree, Cindy L.

    2017-08-01

    This topical review is dedicated to understanding stress corrosion cracking in oxide glasses and specifically the SiO_2{\\text-B_2O_3{\\text-}Na_2O} (SBN) ternary glass systems. Many review papers already exist on the topic of stress corrosion cracking in complex oxide glasses or overly simplified glasses (pure silica). These papers look at how systematically controlling environmental factors (pH, temperature...) alter stress corrosion cracking, while maintaining the same type of glass sample. Many questions still exist, including: What sets the environmental limit? What sets the velocity versus stress intensity factor in the slow stress corrosion regime (Region I)? Can researchers optimize these two effects to enhance a glass’ resistance to failure? To help answer these questions, this review takes a different approach. It looks at how systemically controlling the glass’ chemical composition alters the structure and physical properties. These changes are then compared and contrasted to the fracture toughness and the stress corrosion cracking properties. By taking this holistic approach, researchers can begin to understand the controlling factors in stress corrosion cracking and how to optimize glasses via the initial chemical composition.

  9. Standard Test Method for Stress-Corrosion of Titanium Alloys by Aircraft Engine Cleaning Materials

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2006-01-01

    1.1 This test method establishes a test procedure for determining the propensity of aircraft turbine engine cleaning and maintenance materials for causing stress corrosion cracking of titanium alloy parts. 1.2 The evaluation is conducted on representative titanium alloys by determining the effect of contact with cleaning and maintenance materials on tendency of prestressed titanium alloys to crack when subsequently heated to elevated temperatures. 1.3 Test conditions are based upon manufacturer's maximum recommended operating solution concentration. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. For specific precautionary statements, see and .

  10. Electrochemical investigation of crack initiation during corrosion fatigue of stainless steels in the passive state. Elektrochemische Untersuchung der Rissbildung bei Schwingungsrisskorrosion im stabil-passiven Werkstoffzustand

    Energy Technology Data Exchange (ETDEWEB)

    Spaehn, R. (Technische Hochschule Darmstadt (Germany, F.R.))

    1991-03-01

    The corrosion fatigue behaviour of three stainless steels - ferritic (12% Cr), austenitic (type 316 Ti) and austenitic-ferritic (type 31803; Duplex stainless steel) - was studied under rotating bending moments in aqueous sulphuric acid of 30deg C. An instrumental set-up for recording the transient currents of specimens during potentiostatically controlled corrosion fatigue is described. Based on this transient current signal technique, three stages on the corrosion fatigue process can be discerned. In the incubation period, small stochastic current transients are caused by the response of the passive layer to alternating stresses and environmental conditions. The appearance of sinusoidal current signals indicates crack initiation whereas the phase angle between a fixed marker - i.e. a light barrier signal -, and the anodic amplitude represents the site of initiating cracks. Finally, the crack growth period is characterized by an increasing cell current and steadily growing sinusoidal current signals caused by the interplay of microplastic and repassivation processes at the crack tip. (orig.).

  11. ADAPTATION OF CRACK GROWTH DETECTION TECHNIQUES TO US MATERIAL TEST REACTORS

    Energy Technology Data Exchange (ETDEWEB)

    A. Joseph Palmer; Sebastien P. Teysseyre; Kurt L. Davis; Gordon Kohse; Yakov Ostrovsky; David M. Carpenter; Joy L. Rempe

    2015-04-01

    A key component in evaluating the ability of Light Water Reactors to operate beyond 60 years is characterizing the degradation of materials exposed to radiation and various water chemistries. Of particular concern is the response of reactor materials to Irradiation Assisted Stress Corrosion Cracking (IASCC). Some test reactors outside the United States, such as the Halden Boiling Water Reactor (HBWR), have developed techniques to measure crack growth propagation during irradiation. The basic approach is to use a custom-designed compact loading mechanism to stress the specimen during irradiation, while the crack in the specimen is monitored in-situ using the Direct Current Potential Drop (DCPD) method. In 2012 the US Department of Energy commissioned the Idaho National Laboratory and the MIT Nuclear Reactor Laboratory (MIT NRL) to take the basic concepts developed at the HBWR and adapt them to a test rig capable of conducting in-pile IASCC tests in US Material Test Reactors. The first two and half years of the project consisted of designing and testing the loader mechanism, testing individual components of the in-pile rig and electronic support equipment, and autoclave testing of the rig design prior to insertion in the MIT Reactor. The load was applied to the specimen by means of a scissor like mechanism, actuated by a miniature metal bellows driven by pneumatic pressure and sized to fit within the small in-core irradiation volume. In addition to the loader design, technical challenges included developing robust connections to the specimen for the applied current and voltage measurements, appropriate ceramic insulating materials that can endure the LWR environment, dealing with the high electromagnetic noise environment of a reactor core at full power, and accommodating material property changes in the specimen, due primarily to fast neutron damage, which change the specimen resistance without additional crack growth. The project culminated with an in

  12. Effects of alloy chemistry, cold work, and water chemistry on corrosion fatigue and stress corrosion cracking of nickel alloys and welds.

    Energy Technology Data Exchange (ETDEWEB)

    Chopra, O. K.; Soppet, W. K.; Shack, W. J.; Energy Technology

    2001-04-01

    Reactor vessel internal components made of nickel-base alloys are susceptible to environmentally assisted cracking (EAC). A better understanding of the causes and mechanisms of this cracking may permit less conservative estimates of damage accumulation and requirements on inspection intervals. The objective of this work is to evaluate and compare the resistance of Alloys 600 and 690 and their welds, such as Alloys 82, 182, 52, and 152, to EAC in simulated light water reactor environments. The existing crack growth rate (CGR) data for these alloys under cyclic and constant loads have been evaluated to establish the effects of alloy chemistry, cold work, and water chemistry. The experimental fatigue CGRs are compared with CGRs that would be expected in air under the same mechanical loading conditions to obtain a qualitative understanding of the degree and range of conditions for significant environmental enhancement in growth rates. The existing stress corrosion cracking (SCC) data on Alloys 600 and 690 and Alloy 82, 182, and 52 welds have been compiled and analyzed to determine the influence of key parameters on growth rates in simulated PWR and BWR environments. The SCC data for these alloys have been evaluated with correlations developed by Scott and by Ford and Andresen.

  13. The corrosion and stress corrosion cracking behavior of a novel alumina-forming austenitic stainless steel in supercritical water

    Science.gov (United States)

    Sun, Hongying; Yang, Haijie; Wang, Man; Giron-Palomares, Benjamin; Zhou, Zhangjian; Zhang, Lefu; Zhang, Guangming

    2017-02-01

    The general corrosion and stress corrosion behavior of Fe-27Ni-15Cr-5Al-2Mo-0.4Nb alumina-forming austenitic (AFA) steel were investigated in supercritical water under different conditions. A double layer oxide structure was formed: a Fe-rich outer layer (Fe2O3 and Fe3O4) and an Al-Cr-rich inner layer. And the inner layer has a low growth rate with exposing time, which is good for improvement of corrosion resistance. Additionally, some internal nodular Al-Cr-rich oxides were also observed, which resulted in a local absence of inner layer. Stress corrosion specimens exhibited a combination of high strength, good ductility and low susceptibility. The stress strength and elongation was reduced by increasing temperature and amount of dissolved oxygen. In addition, the corresponding susceptibility was increased with decreased temperatures and increased oxygen contents.

  14. Assessment of susceptibility of Type 304 stainless steel to intergranular stress corrosion cracking in simulated Savannah River Reactor environments

    Energy Technology Data Exchange (ETDEWEB)

    Ondrejcin, R.S.; Caskey, C.R. Jr.

    1989-12-01

    Intergranular stress corrosion cracking (IGSCC) of Type 304 stainless steel rate tests (CERT) of specimens machined was evaluated by constant extension from Savannah River Plant (SRP) decontaminated process water piping. Results from 12 preliminary CERT tests verified that IGSCC occurred over a wide range of simulated SRP envirorments. 73 specimens were tested in two statistical experimental designs of the central composite class. In one design, testing was done in environments containing hydrogen peroxide; in the other design, hydrogen peroxide was omitted but oxygen was added to the environment. Prediction equations relating IGSCC to temperature and environmental variables were formulated. Temperature was the most important independent variable. IGSCC was severe at 100 to 120C and a threshold temperature between 40C and 55C was identified below which IGSCC did not occur. In environments containing hydrogen peroxide, as in SRP operation, a reduction in chloride concentration from 30 to 2 ppB also significantly reduced IGSCC. Reduction in sulfate concentration from 50 to 7 ppB was effective in reducing IGSCC provided the chloride concentration was 30 ppB or less and temperature was 95C or higher. Presence of hydrogen peroxide in the environment increased IGSCC except when chloride concentration was 11 ppB or less. Actual concentrations of hydrogen peroxide, oxygen and carbon dioxide did not affect IGSCC. Large positive ECP values (+450 to +750 mV Standard Hydrogen Electrode (SHE)) in simulated SRP environments containing hydrogen peroxide and were good agreement with ECP measurements made in SRP reactors, indicating that the simulated environments are representative of SRP reactor environments. Overall CERT results suggest that the most effective method to reduce IGSCC is to reduce chloride and sulfate concentrations.

  15. Assessment of susceptibility of Type 304 stainless steel to intergranular stress corrosion cracking in simulated Savannah River Reactor environments

    Energy Technology Data Exchange (ETDEWEB)

    Ondrejcin, R.S.; Caskey, C.R. Jr.

    1989-12-01

    Intergranular stress corrosion cracking (IGSCC) of Type 304 stainless steel rate tests (CERT) of specimens machined was evaluated by constant extension from Savannah River Plant (SRP) decontaminated process water piping. Results from 12 preliminary CERT tests verified that IGSCC occurred over a wide range of simulated SRP envirorments. 73 specimens were tested in two statistical experimental designs of the central composite class. In one design, testing was done in environments containing hydrogen peroxide; in the other design, hydrogen peroxide was omitted but oxygen was added to the environment. Prediction equations relating IGSCC to temperature and environmental variables were formulated. Temperature was the most important independent variable. IGSCC was severe at 100 to 120C and a threshold temperature between 40C and 55C was identified below which IGSCC did not occur. In environments containing hydrogen peroxide, as in SRP operation, a reduction in chloride concentration from 30 to 2 ppB also significantly reduced IGSCC. Reduction in sulfate concentration from 50 to 7 ppB was effective in reducing IGSCC provided the chloride concentration was 30 ppB or less and temperature was 95C or higher. Presence of hydrogen peroxide in the environment increased IGSCC except when chloride concentration was 11 ppB or less. Actual concentrations of hydrogen peroxide, oxygen and carbon dioxide did not affect IGSCC. Large positive ECP values (+450 to +750 mV Standard Hydrogen Electrode (SHE)) in simulated SRP environments containing hydrogen peroxide and were good agreement with ECP measurements made in SRP reactors, indicating that the simulated environments are representative of SRP reactor environments. Overall CERT results suggest that the most effective method to reduce IGSCC is to reduce chloride and sulfate concentrations.

  16. Dissolution of copper in chloride/ammonia mixtures and the implications for the stress corrosion cracking of copper containers

    Energy Technology Data Exchange (ETDEWEB)

    King, F.; Greidanus, G.; Jobe, D.J

    1999-05-01

    Stress-corrosion cracking is a possible failure mechanism for copper nuclear fuel waste disposal containers. One species known to cause the stress corrosion of copper alloys is ammonia. It is conceivable that ammonia could be produced in a disposal vault under certain, very specific conditions. There are a number of conditions, however, that mitigate against container failure by stress corrosion, one of which is the presence of chloride ions in deep Canadian Shield groundwaters. There are a number of reports in the literature that suggest that Cl{sup -} has an inhibitive effect on the stress corrosion of Cu alloys in ammonia solutions. The electrochemical behaviour of Cu in Cl{sup -}/ammonia solutions has been studied as a function of ammonia concentration, pH, the rate of mass transport and electrochemical potential. In particular, the effects of these parameters on the formation Of Cu{sub 2}O films and the steady-state dissolution behaviour have been determined. All experiments were carried out in 0.1 mol{center_dot}dm{sup -3} NaC1 as a base solution. A series of aqueous speciation and equilibrium potential/pH diagrams are also presented for the quaternary system Cu-C1{sup -}NH{sub 3}/NH{sub 4{sup +}}H{sub 2}O. These diagrams are used to interpret the results of the electrochemical experiments reported here. In addition, it is demonstrated how these diagrams could be used to predict the time-dependence of the susceptibility to stress corrosion cracking of Cu containers in a disposal vault. (author)

  17. Improvement of stress corrosion cracking (SCC) resistance by cyclic pre-straining of 316L austenitic stainless steel in an aqueous boiling MgCl{sub 2} solution; Amelioration de la tenue a la corrosion sous contrainte (CSC) de l'acier inoxydable austenitique 316L en solution bouillante de MgCl{sub 2} par application d'une predeformation cyclique

    Energy Technology Data Exchange (ETDEWEB)

    Curiere, I. de; Bayle, B.; Magnin, Th. [Ecole Nationale Superieure des Mines, URA CNRS 1884, 42 - Saint-Etienne (France)

    2000-07-01

    Improving the materials resistance to stress corrosion cracking (SCC) has become a topic of wide interest for theoretical, engineering and financial reasons. The aim of this paper is to propose a process to delay the SCC damage. Recent studies of 316L austenitic stainless steel in boiling MgCl{sub 2} solutions show an improvement in SCC resistance by cyclic pre-straining in low cycle fatigue. This improvement consists of an increase in both strain to failure and crack initiation strain, during Slow Rate Tensile (SSRT) tests in aqueous solution. This paper analyses the effect of pre-fatigue in 316L on its mechanical and electrochemical responses to better understand the delay of SCC damage in boiling MgCl{sub 2}. The explanation for this beneficial effect is related to a modification of both surface electrochemical reactions kinetics and corrosion/plasticity interactions at the crack tip, due to the particular dislocation structure. (authors)

  18. Microstructure, mechanical properties and stress corrosion cracking of Al–Zn–Mg–Zr alloy sheet with trace amount of Sc

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Xing [School of Materials Science and Engineering, Central South University, Changsha 410083 (China); Pan, Qinglin, E-mail: pql1964@126.com [School of Materials Science and Engineering, Central South University, Changsha 410083 (China); Li, Bo [School of Materials Science and Engineering, Central South University, Changsha 410083 (China); Liu, Zhiming; Huang, Zhiqi [Guangdong Fenglu Aluminum Co., Ltd, Foshan 528133 (China); Yin, Zhimin [School of Materials Science and Engineering, Central South University, Changsha 410083 (China)

    2015-11-25

    Microstructural and property evolution of the Al–Zn–Mg–0.10%Sc–0.10%Zr alloy sheet during its preparation were investigated in detail by means of optical microscopy (OM), scanning electron microscope (SEM), energy dispersive X-ray (EDX), transmission electron microscopy (TEM), Vickers micro-hardness test and room temperature tensile test. Stress corrosion cracking (SCC) behavior of the Al–Zn–Mg–0.10%Sc–0.10%Zr alloy under different heat treatments was studied using slow strain rate test. The results showed that serious dendritic segregation existed in as-cast condition. The suitable homogenization treatment for Al–Zn–Mg–0.10%Sc–0.10%Zr alloy was 470 °C/24 h. After homogenization treatment, dissoluble Zn and Mg enriched non-equilibrium phases dissolved into α-Al matrix completely. The suitable solid solution-aging treatment for Al–Zn–Mg–0.10%Sc–0.10%Zr alloy was solution treated at 470 °C for 60 min, followed by water quenching and then aged at 120 °C for 24 h. Under this aging temper, the grain structures were composed of sub-grains, η′ phases and nanometer-sized, spherical Al{sub 3}(Sc, Zr) particles. Grain boundary precipitates (GBPs) area fraction was found to be an important parameter to evaluate the SCC susceptibility. The improved corrosion resistance from increasing aging temperature or prolonging aging time was due to the discontinuous η precipitates along the grain boundary and the high area fraction of GBPs. The main strengthening mechanisms of Al–Zn–Mg–0.10%Sc–0.10%Zr alloy are precipitation strengthening derived from η′ precipitates, dispersion strengthening, sub-grain strengthening and grain refinement caused by coherent Al{sub 3}(Sc, Zr) particles. - Highlights: • The suitable homogenization treatment of the alloy has been identified. • Evolution of microstructure and mechanical properties is investigated. • Strengthening mechanisms of the alloy has been established. • The basic mechanism has

  19. Evaluation of zinc addition on fuel cladding corrosion at the Halden test reactor. Final report

    Energy Technology Data Exchange (ETDEWEB)

    Kolstad, E.; Symons, W.J.; Bryhn-Integrigtsen, K.; Oberlaender, B.C.

    1996-08-01

    Experimental studies have shown that addition of zinc to a PWR environment reduces the general corrosion rates of materials in the primary system and delays the initiation of primary water stress corrosion cracking (PWSCC) in Alloy 600. In order to provide an early warning of any potential adverse effects on the fuel cladding, corrosion studies were initiated at the Halden test reactor. These tests were carried out in a PWR rig inserted in the Halden reactor core. The rig simulated thermal hydraulic and coolant conditions typical of a MR. It had two flow channels where the fuel rod segments were exposed to the coolant under irradiation flux. Selected pre-characterized rodlets with fresh and pre-irradiated standard and low-tin Zircaloy-4 material were irradiated for three cycles. First cycle lasted for 110 effective full power days (EFPDs), the second for 95 EFPDs and the last 62 EFPDs. The cladding corrosion behavior was monitored by initial, interim and final oxide thickness measurements by eddy current lift-off probe. Crud sampling was performed in both channels after cycle 1 and 2. Destructive post-irradiation examinations (PIE) of two rodlets, irradiated during cycle 1 and 2, have also been completed at the conclusion of the in-pile testing. This report presents the results on oxide thickness measurements, irradiation history and water chemistry data, and the PIE.

  20. Hydrogen embrittlement and hydrogen induced stress corrosion cracking of high alloyed austenitic materials; Wasserstoffversproedung und wasserstoffinduzierte Spannungsrisskorrosion hochlegierter austenitischer Werkstoffe

    Energy Technology Data Exchange (ETDEWEB)

    Mummert, K.; Uhlemann, M.; Engelmann, H.J. [Institut fuer Festkoerper- und Werkstofforschung Dresden e.V. (Germany)

    1998-11-01

    The susceptiblity of high alloyed austenitic steels and nickel base alloys to hydrogen-induced cracking is particularly determined by 1. the distribution of hydrogen in the material, and 2. the microstructural deformation behaviour, which last process is determined by the effects of hydrogen with respect to the formation of dislocations and the stacking fault energy. The hydrogen has an influence on the process of slip localization in slip bands, which in turn affects the microstructural deformation behaviour. Slip localization increases with growing Ni contents of the alloys and clearly reduces the ductility of the Ni-base alloy. Although there is a local hydrogen source involved in stress corrosion cracking, emanating from the corrosion process at the cathode, crack growth is observed only in those cases when the hydrogen concentration in a small zone ahead of the crack tip reaches a critical value with respect to the stress conditions. Probability of onset of this process gets lower with growing Ni content of the alloy, due to increasing diffusion velocity of the hydrogen in the austenitic lattice. This is why particularly austenitic steels with low Ni contents are susceptible to transcrystalline stress corrosion cracking. In this case, the microstructural deformation process at the crack tip is also influenced by analogous processes, as could be observed in hydrogen-loaded specimens. (orig./CB) [Deutsch] Die Empfindlichkeit von hochlegierten austentischen Staehlen und Nickelbasislegierungen gegen wasserstoffinduziertes Risswachstum wird im wesentlichen bestimmt durch 1. die Verteilung von Wasserstoff im Werkstoff und 2. das mikrostrukturelle Verformungsverhalten. Das mikrostrukturelle Deformationsverhalten ist wiederum durch den Einfluss von Wasserstoff auf die Versetzungsbildung und die Stapelfehlerenergie charakterisiert. Das mikrostrukturelle Verformungsverhalten wird durch wasserstoffbeeinflusste Gleitlokalisierung in Gleitbaendern bestimmt. Diese nimmt mit

  1. Embrittlement and anodic process in stress corrosion cracking: study of the influent micro-mechanical parameters; Fragilisation et processus anodiques en corrosion sous contrainte: etude des parametres micro-mecaniques influents

    Energy Technology Data Exchange (ETDEWEB)

    Tinnes, J.Ph

    2006-11-15

    We study the influence of local mechanical parameters on crack propagation in Stress Corrosion Cracking, at the scale of the microstructure. Two systems are compared: the CuAl{sub 9}Ni{sub 3}Fe{sub 2} copper-aluminium alloy in synthetic sea water under cathodic polarization, where the crack propagation mechanism is related to strain-assisted anodic dissolution, and the 316L austenitic stainless steel in MgCl{sub 2} solution, where embrittlement mechanisms related to hydrogen effects prevail. We use micro-notched tensile specimen that allow to study isolated short cracks. These experiments are modelled by means of finite elements calculations, and further characterized by Electron Back scattered Diffraction (EBSD) in the case of the 316L alloy. In terms of the local mechanical parameters that control propagation, fundamental differences are outlined between the two systems. They are discussed from the viewpoint of the available models of Stress Corrosion Cracking. (author)

  2. Evaluation of annual corrosion tests for aggressive water

    Science.gov (United States)

    Dubová, V.; Ilavský, J.; Barloková, D.

    2011-12-01

    Internal corrosion has a significant effect on the useful life of pipes, the hydraulic conditions of a distribution system and the quality of the water transported. All water is corrosive under some conditions, and the level of this corrosion depends on the physical and chemical properties of the water and properties of the pipe material. Galvanic treatment is an innovation for protecting against corrosion, and this method is also suitable for removal of water stone too. This method consists of the electrogalvanic principle, which is generated by the flowing of water between a zinc anode and the cupro-alloy cover of a column. This article presents experimental corrosion tests at water resource Pernek (This water resource-well marked as HL-1 is close to the Pernek of village), where the device is operating based on this principle.

  3. Assessment of copper resistance to stress-corrosion cracking in nitrite solutions by means of joint analysis of acoustic emission measurements, deformation diagrams, qualitative and quantitative fractography, and non-linear fracture mechanics

    Energy Technology Data Exchange (ETDEWEB)

    Khanzhin, V.G.; Nikulin, S.A. [Moscow State Inst. of Steel and Alloys (Russian Federation)

    2005-06-01

    A study of stress-corrosion cracking (SCC) of copper in 0.1M NaNO{sub 2} aqueous solution is presented. The fracture kinetics was monitored by measuring the acoustic emission (AE) signals. Macro- and micro-fractography analysis, using scanning electron microscopy (SEM), was employed to investigate the fracture mechanisms. Estimates of stress intensity factor, KI, and J-integral were derived in order to assess the resistance of copper to stress corrosion cracking. Two kinds of SCC tests under continuous circulation of the corrosive solution were employed in the present study: 1. Constant extension rate (2x10{sup -6}/s) tests on pre-cracked, middle tension (MT) panel specimens. 2. Tests on pre-cracked, compact tension (CT) specimens at a fixed (by a fixing bolt) opening of the crack walls ({delta} = 0.3 mm, K{sub i} = 27 MPax{radical}m). The time base for these tests was about two months. After the completion of the SCC test, the CT specimen was additionally tested, under a constant-rate (0.02 mm/s) off-center extension. In the both kinds of tests, the SCC fracture kinetics is found to exhibit two typical stages: Stage 1: SCC initiation stage (after a certain incubation period, T{sub i}, measured to be T{sub i} {approx_equal} 3-4 hours for MT specimens under constant extension, the corresponding stress was {sigma} {approx_equal} 40-70 MPa, and T{sub i} {approx_equal} 200 hours for CT specimens under a fixed crack wall opening). Stage 2: Active fracture process (SCC macro-fracture) distinguished by strong AE pulses (which are registered after time T{sub 2} {approx_equal} 8 hours for MT specimens and T{sub 2} {approx_equal} 800 hours for CT specimens). Fractography analysis has shown that the zone of SCC fracture in MT specimens extends to approximately 1,500 {mu}m. A 400-700 {mu}m deep zone of brittle transgranular fracture, which included small areas showing characteristic SCC 'striations', was observed adjacent to the fatigue pre-crack area. At higher

  4. Corrosion

    Science.gov (United States)

    Slabaugh, W. H.

    1974-01-01

    Presents some materials for use in demonstration and experimentation of corrosion processes, including corrosion stimulation and inhibition. Indicates that basic concepts of electrochemistry, crystal structure, and kinetics can be extended to practical chemistry through corrosion explanation. (CC)

  5. Corrosion

    Science.gov (United States)

    Slabaugh, W. H.

    1974-01-01

    Presents some materials for use in demonstration and experimentation of corrosion processes, including corrosion stimulation and inhibition. Indicates that basic concepts of electrochemistry, crystal structure, and kinetics can be extended to practical chemistry through corrosion explanation. (CC)

  6. Hydrogen diffusion into fatigue cracks of aluminium alloy 6013 in a corrosive environment; Wasserstoffeinlagerung an Ermuedungsrissen der Aluminiumlegierung 6013 unter korrosiver Umgebung

    Energy Technology Data Exchange (ETDEWEB)

    Lenk, Christian Alexander

    2009-08-13

    The author attempted a time-resolved detection of raised hydrogen concentrations in the plastic deformation region of fatigue cracks in an aluminium test piece deformed by cyclic stress in a corrosive environment. Mechanical material parameters like the crack propagation velocity under cyclic stress change dramatically in a corrosive environment. This is assumed to be caused by hydrogen diffusion, but so far there is no method that reliably measures additional hydrogen from the corrosive environment. For this reason, a special analytical configuration was set up which makes use of the thermal desorption method. First, chips with a thickness of about 20 micrometers are sawed out of the test specimen in high-vacuum conditions. The chips fall into a hot melting vessel in a UHV chamber, where the hydrogen contained in the chips is released. The resulting pressure increase is recorded by a mass spectrometer. A hydrogen profile of the test specimen is obtained by assigning the chip position to the signal. For the corrosive medium in which the test specimen is immersed during crack initiation, i.e. NaCl solution, heavy water was used. This makes it possible to distinguish between the hydrogen contained in a piece of technical aluminium alloy (AA6013) and the deuterium diffusing in from the corrosive fluid. The deuterium is found exclusively in the test piece volume in the strongly plastically deformed region surrounding the fatigue crack. (orig.) [German] Das Ziel der vorliegenden Arbeit besteht im ortsaufgeloesten Nachweis einer erhoehten Wasserstoffkonzentration im plastisch deformierten Bereich von Ermuedungsrissen einer unter korrosiver Umgebung zyklisch verformten Aluminiumprobe. Mechanische Materialparameter wie z.B. die Rissausbreitungsgeschwindigkeit unter zyklischer Belastung aendern sich drastisch in korrosiver Umgebung. Als Ursache fuer dieses Verhalten wird eine Eindiffusion von Wasserstoff vermutet, jedoch gibt es bisher keine Messung die den zusaetzlichen

  7. Lithuanian Quarry Aggregates Concrete Effects of Alkaline Corrosion Tests

    Directory of Open Access Journals (Sweden)

    Aurimas Rutkauskas

    2016-02-01

    Full Text Available Aggregate alkaline corrosion of cement in concrete is going to respond in sodium and potassium hydroxide (lye with active SiO2 found in some aggregates. During this reaction, the concrete has resulted in significant internal stresses which cause deformation of the concrete, cracking and disintegration. The reaction is slow and concrete signs of decomposition appear only after a few months or years. The study used two different aggregates quarries. Studies show that Lithuania gravel contaminated with reactive particles having amorphous silicon dioxide reacting with cement in sodium and potassium hydroxide and the resulting alkaline concrete corrosion. It was found that, according to AAR 2 large aggregates include Group II – potentially reactive because of their expansion after 14 days, higher than 0.1%.

  8. Effect of cracking and randomness of inputs on corrosion initiation of reinforced concrete bridge decks exposed to chlorides

    Directory of Open Access Journals (Sweden)

    P. Konecny

    2017-01-01

    Full Text Available The paper is aimed at the indicative evaluation of the effect of random scatter of input parameters in case of durability of reinforced concrete bridge deck. The time to onset of corrosion of steel reinforcement of concrete bridge deck exposed to chloride is evaluated. The effect of cracking in concrete onto chloride ingress is considered. The selected steel reinforcement protection strategies are: unprotected steel reinforcement, epoxy-coated steel reinforcement and water-proof barrier bellow asphalt overlay. The preliminary model for damage effect on chloride ion ingress through water proof membrane under penetrable asphalt overlay is used. 2-D finite element chloride ingress model is combined with Monte Carlo simulation technique. The innovative crack effect modeling via highly penetrable elements is applied. Deterministic and probabilistic calculations are compared.

  9. Evaluation of taper joints with combined fatigue and crevice corrosion testing: Comparison to human explanted modular prostheses

    Energy Technology Data Exchange (ETDEWEB)

    Reclaru, L., E-mail: lucien.reclaru@pxgroup.com [PX Group S.A., Dep R and D Corrosion and Biocompatibility Group, Bd. des Eplatures 42, CH-2304 La Chaux-de-Fonds (Switzerland); Brooks, R.A. [Orthopaedic Research, Addenbrooke' s Hospital, University of Cambridge, Box 180 Hills Road, CB2 0QQ Cambridge (United Kingdom); Zuberbühler, M. [Smith and Nephew Orthopaedics AG, Schachenalle 29, 5001 Aarau (Switzerland); Eschler, P.-Y.; Constantin, F. [PX Group S.A., Dep R and D Corrosion and Biocompatibility Group, Bd. des Eplatures 42, CH-2304 La Chaux-de-Fonds (Switzerland); Tomoaia, G. [University of Medicine and Pharmacy Iuliu Hateganu of Cluj-Napoca, Dept. of Orthopaedics and Traumatology, Cluj-Napoca (Romania)

    2014-01-01

    The requirement for revision surgery of total joint replacements is increasing and modular joint replacement implants have been developed to provide adjustable prosthetic revision systems with improved intra-operative flexibility. An electrochemical study of the corrosion resistance of the interface between the distal and proximal modules of a modular prosthesis was performed in combination with a cyclic fatigue test. The complexity resides in the existence of interfaces between the distal part, the proximal part, and the dynamometric screw. A new technique for evaluating the resistance to cyclic dynamic corrosion with crevice stimulation was used and the method is presented. In addition, two components of the proximal module of explanted Ti6Al4V and Ti6Al7Nb prostheses were investigated by optical and electron microscopy. Our results reveal that: The electrolyte penetrates into the interface between the distal and proximal modules during cyclic dynamic fatigue tests, the distal module undergoes cracking and corrosion was generated at the interface between the two models; The comparison of the explanted proximal parts with the similar prostheses evaluated following cyclic dynamic crevice corrosion testing showed that there were significant similarities indicating that this method is suitable for evaluating materials used in the fabrication of modular prostheses. - Highlights: • Electrochemical crevice corrosion testing combined with fatigue test conducted on Ti6Al7Nb and Ti6Al4V modular prostheses • Cations released from integral prostheses • Comparison of human explanted modular prostheses with the similar prostheses evaluated in cyclic dynamic crevice corrosion.

  10. Round Robin Fatigue Crack Growth Testing Results

    Science.gov (United States)

    2006-11-01

    Equipment and Setup a. SATEC b. 20 kip (7075-T6); 55 kip (2024-T351) c. Test control hardware/ software i. Hardware: Teststar Ilm ii. Software : Station...Stractlvrai Lif,"e Exteraiocn (CAStLE) DeOartn~ont of Enineering Mechanics, FIC US~.TA/DFFN 1DSA-FA-*rR-2006-10 23-54 arhi Drive, Suite 2J2, U-SAF Academy CO

  11. Standard test method for measurement of fatigue crack growth rates

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2015-01-01

    1.1 This test method covers the determination of fatigue crack growth rates from near-threshold to Kmax controlled instability. Results are expressed in terms of the crack-tip stress-intensity factor range (ΔK), defined by the theory of linear elasticity. 1.2 Several different test procedures are provided, the optimum test procedure being primarily dependent on the magnitude of the fatigue crack growth rate to be measured. 1.3 Materials that can be tested by this test method are not limited by thickness or by strength so long as specimens are of sufficient thickness to preclude buckling and of sufficient planar size to remain predominantly elastic during testing. 1.4 A range of specimen sizes with proportional planar dimensions is provided, but size is variable to be adjusted for yield strength and applied force. Specimen thickness may be varied independent of planar size. 1.5 The details of the various specimens and test configurations are shown in Annex A1-Annex A3. Specimen configurations other than t...

  12. Effect of Pre-aging on Stress Corrosion Cracking of Spray-formed 7075 Alloy in Retrogression and Re-aging

    Science.gov (United States)

    Su, Rui-ming; Qu, Ying-dong; You, Jun-hua; de Li, Rong-

    2015-11-01

    The effects of pre-aging in retrogression and re-aging (RRA) treatment on microstructure, mechanical properties, and stress corrosion cracking (SCC) behavior of spray-formed 7075 aluminum alloy were investigated by tensile test, slow strain rate test, and transmission electron microscope. The results show that the under aging (120 °C for 16 h) as the pre-aging in RRA treatment can vastly improve the mechanical properties and the SCC resistance of the alloy, compared with early aging (120 °C for 8 h), peak aging (120 °C for 24 h), and over aging (120 °C for 32 h) treatments, the ultimate tensile strength of the alloy is 782 MPa, which is higher than that for peak aging or conventional RRA treatment; and the SCC resistance of the alloy is also excellent after RRA with under aging as pre-aging.

  13. Stress corrosion cracking in repair-welded 3.5 NiCrMoV steel in an actual turbine environment

    Energy Technology Data Exchange (ETDEWEB)

    Hitomi, Itoh; Takashi, Shige [Mitsubishi Heavy Industries, Ltd., Takasago Research and Development Center (Japan); Takashi, Momoo [Mitsubishi Heavy Industries, Ltd., Takasago Machinery Works (Japan)

    2001-07-01

    Temporary welding repairs are sometimes needed when damage occurs at the teeth of blade grooves in a low-pressure turbine rotor operated at the dry/wet boundary region. When repair welding has been performed for the 3,5 NiCrMoV steel used in low-pressure turbines, the soundness of the weld must be confirmed. For this reason, a laboratory investigation of susceptibility for stress corrosion cracking (SCC) was conducted for test specimens taken from simulated welds, and then an exposure test was conducted in an actual turbine environment for approximately 7,000 hours. As no SCC initiation was detected and also the propagation was extremely small, repair welding is deemed to be applicable. (author)

  14. Commercial Test of Flexible Dual-Riser Catalytic Cracking Process

    Institute of Scientific and Technical Information of China (English)

    Tang Haitao; Wang Longyan; Wang Guoliang; Zhang Lixin; Wei Jialu; Chen Zhenghong; Teng Tiancan; Sun Zhonghang

    2003-01-01

    The technical features and commercial test results of flexible dual-riser fluidized catalytic cracking(FDFCC) process are presented for refiners to choose an efficient process to upgrade FCC naphtha and boostpropylene production in a RFCC unit. The commercial test results indicate that the olefin content of catalyti-25% and RON increased by 0.5-2 units in a RFCC unit. In addition, propylene yield and the production ratioof diesel to gasoline can also be remarkably enhanced in the RFCC unit.

  15. From laboratory corrosion tests to a corrosion lifetime for wood fasteners : progress and challenges

    Science.gov (United States)

    Samuel L. Zelinka; Dominique Derome; Samuel V. Glass

    2010-01-01

    Determining a “corrosion-lifetime” for fasteners embedded in wood treated with recently adopted preservative systems depends upon successfully relating results of laboratory tests to in-service conditions. In contrast to laboratory tests where metal is embedded in wood at constant temperature and moisture content, the in-service temperature and moisture content of wood...

  16. Standard practice for determining the susceptibility of stainless steels and related Nickel-Chromium-Iron Alloys to stress-corrosion cracking in polythionic acids

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2010-01-01

    1.1 This practice covers procedures for preparing and conducting the polythionic acid test at room temperature, 22 to 25°C (72 to 77°F), to determine the relative susceptibility of stainless steels or other related materials (nickel-chromiumiron alloys) to intergranular stress corrosion cracking. 1.2 This practice can be used to evaluate stainless steels or other materials in the “as received” condition or after being subjected to high-temperature service, 482 to 815°C (900 to 1500°F), for prolonged periods of time. 1.3 This practice can be applied to wrought products, castings, and weld metal of stainless steels or other related materials to be used in environments containing sulfur or sulfides. Other materials capable of being sensitized can also be tested in accordance with this test. 1.4 This practice may be used with a variety of stress corrosion test specimens, surface finishes, and methods of applying stress. 1.5 This standard does not purport to address all of the safety concerns, if any, ...

  17. Time-dependent corrosion fatique crack propagation in 7000 series aluminum alloys. M.S. Thesis

    Science.gov (United States)

    Mason, Mark E.

    1995-01-01

    The goal of this research is to characterize environmentally assisted subcritical crack growth for the susceptible short-longitudinal orientation of aluminum alloy 7075-T651, immersed in acidified and inhibited NaCl solution. This work is necessary in order to provide a basis for incorporating environmental effects into fatigue crack propagation life prediction codes such as NASA-FLAGRO (NASGRO). This effort concentrates on determining relevant inputs to a superposition model in order to more accurately model environmental fatigue crack propagation.

  18. Effect of Sensitization on Corrosion-Fatigue Cracking in Al 5083 Alloy

    Science.gov (United States)

    2015-01-21

    1% NaCl solution, the observed environmental effects on fatigue crack growth can be explained by the hydrogen embrittlement mechanism and are...using a superposition model and a two-parameter approach to environment- assisted cracking . The superposition model is essentially a summation of...Metall. Trans. A. Vol. 11A, 1980, pp. 151-158. 15. A. Bonakdar, F. Wang, J.J. Williams, and N. Chawla, “ Environmental Effects on Fatigue Crack

  19. The role of local strains from prior cold work on stress corrosion cracking of α-brass in Mattsson's solution

    Energy Technology Data Exchange (ETDEWEB)

    Ulaganathan, Jaganathan, E-mail: jagan.ulaganathan@mail.utoronto.ca; Newman, Roger C., E-mail: roger.newman@utoronto.ca

    2014-06-01

    The dynamic strain rate ahead of a crack tip formed during stress corrosion cracking (SCC) under a static load is assumed to arise from the crack propagation. The strain surrounding the crack tip would be redistributed as the crack grows, thereby having the effect of dynamic strain. Recently, several studies have shown cold work to cause accelerated crack growth rates during SCC, and the slip-dissolution mechanism has been widely applied to account for this via a supposedly increased crack-tip strain rate in cold worked material. While these interpretations consider cold work as a homogeneous effect, dislocations are generated inhomogeneously within the microstructure during cold work. The presence of grain boundaries results in dislocation pile-ups that cause local strain concentrations. The local strains generated from cold working α-brass by tensile elongation were characterized using electron backscatter diffraction (EBSD). The role of these local strains in SCC was studied by measuring the strain distributions from the same regions of the sample before cold work, after cold work, and after SCC. Though, the cracks did not always initiate or propagate along boundaries with pre-existing local strains from the applied cold work, the local strains surrounding the cracked boundaries had contributions from both the crack propagation and the prior cold work. - Highlights: • Plastic strain localization has a complex relationship with SCC susceptibility. • Surface relief created by cold work creates its own granular strain localization. • Cold work promotes crack growth but several other factors are involved.

  20. A Study on the Residual Stress Improvement of PWSCC(Primary Water Stress Corrosion Cracking) in DMW(Dissimilar Metal Weld)

    Energy Technology Data Exchange (ETDEWEB)

    Kang, Sung Sik; Kim, Seok Hun; Lee, Seung Gun [Korea Institute of Nuclear Safety, Daejeon (Korea, Republic of); Park, Heung Bae [KEPCO Engineering and Construction Company, Daejeon (Korea, Republic of)

    2010-10-15

    Since 2000s, most of the cracks are found in welds, especially in (DMW) dissimilar metal welds such as pressurizer safety relief nozzle, reactor head penetration, reactor bottom mounted instrumentation (BMI), and reactor nozzles. Even the cracks are revealed as a primary water stress corrosion cracking (PWSCC), it is difficult to find the cracks by current non destructive examination. The PWSCC is occurred by three incident factors, such as susceptible material, environmental corrosive condition, and welding residual stress. If one of the three factors can be erased or decreased, the PWSCC could be prevented. In this study, we performed residual stress analysis for DMW and several residual stress improvement methods. As the preventive methods of PWSCC, we used laser peening(IP) method, inlay weld(IW) method, and induction heating stress improvement(IHSI) method. The effect of residual stress improvement for preventive methods was compared and discussed by finite element modeling and residual stress of repaired DMW

  1. Experimental testing and evaluation of cracks defects in line pipe

    Energy Technology Data Exchange (ETDEWEB)

    Hosseini, Ali; Cronin, Duane; Plumtree, Alan [University of Waterloo, Waterloo, Ontario (Canada); Kania, Richard [TransCanada Pipelines, Calgary, AB (Canada)

    2010-07-01

    Aging pipelines may show environmental or stress-induced cracking or similar defects. Several assessment methods are currently used for crack-like defects, as well as numerical modeling approaches. All have been used successfully, but unknown factors are the degree of conservatism and sensitivity to the various input parameters. To fill this knowledge gap, a series of full-scale burst tests was undertaken and successfully completed on end-capped, seam-welded pipe specimens having a 20-inch diameter and 5.7-mm wall thickness. The purpose was to study the failure behaviour of axial surface crack flaws and determine if the Level 3 FAD approach, NG-18 method and CorLAS can be applied to predict failure. The aspect of the fracture surface showed that the cause of failure of the pipe sections was ductile tearing, as expected in view of the material and crack sizes. It was found that the most accurate predictions were obtained with Level 3 FAD (J approach, using the cylinder equations) and CorLAS.

  2. Microbial corrosion and cracking in steel. A concept for evaluation of hydrogen-assisted stress corrosion cracking in cathodically protected high-pressure gas transmission pipelines

    DEFF Research Database (Denmark)

    Nielsen, Lars Vendelbo

    of high-strength pipeline steel and the concentration of hydrogen present in the steel. B. Determine the degree hydrogen absorption by cathodically protected steel exposed in natural soil sediment, which include activity of sulphate-reducing bacteria (SRB). C. Compare the above points with fracture......An effort has been undertaken in order to develop a concept for evaluation of the risk of hydrogen-assisted cracking in cathodically protected gas transmission pipelines. The effort was divided into the following subtasks: A. Establish a correlation between the fracture mechanical properties...... in this steel....

  3. Accelerated atmospheric corrosion testing of electroplated gold mirror coatings

    Science.gov (United States)

    Chu, C.-T.; Alaan, D. R.; Taylor, D. P.

    2010-08-01

    Gold-coated mirrors are widely used in infrared optics for industrial, space, and military applications. These mirrors are often made of aluminum or beryllium substrates with polished nickel plating. Gold is deposited on the nickel layer by either electroplating or vacuum deposition processes. Atmospheric corrosion of gold-coated electrical connectors and contacts was a well-known problem in the electronic industry and studied extensively. However, there is limited literature data that correlates atmospheric corrosion to the optical properties of gold mirror coatings. In this paper, the atmospheric corrosion of different electroplated gold mirror coatings were investigated with an accelerated mixed flowing gas (MFG) test for up to 50 days. The MFG test utilizes a combination of low-level air pollutants, humidity, and temperatures to achieve a simulated indoor environment. Depending on the gold coating thickness, pore corrosion started to appear on samples after about 10 days of the MFG exposure. The corrosion behavior of the gold mirror coatings demonstrated the porous nature of the electroplated gold coatings as well as the variation of porosity to the coating thickness. The changes of optical properties of the gold mirrors were correlated to the morphology of corrosion features on the mirror surface.

  4. Analysis of Cracking Mode of Anchor Structure of Underground Engineering Induced by Reinforcement Corrosion

    Directory of Open Access Journals (Sweden)

    Wantao Ding

    2014-02-01

    Full Text Available Based on elastic theory and assumption of maximum tensile-stress failure criterion, together with construction process of anchor structure and rust expansion critical process, this study proposed a simplified reinforcement rust expansion mechanical model of anchor structure system. Elastic criterion of different initial cracking mode was rewarded under different stress ratios. According to analysis of critical cracking mode of different medium, cracking order of mortar and surrounding rock depended on their material parameters, in-situ stress and thickness of mortar cover. Critical cracking conditions of different medium without effect of in-situ stress was the same as that of considering in-situ stress while k is equal to 3 or 1/3. And engineering example shows that three different cracking modes exist under different stress ratios. The result provides a useful reference for analysis of mechanical deterioration mechanism of anchor structure and design of support structure of underground engineering.

  5. The corrosion and corrosion mechanical properties evaluation for the LBB concept in VVERs

    Energy Technology Data Exchange (ETDEWEB)

    Ruscak, M.; Chvatal, P.; Karnik, D.

    1997-04-01

    One of the conditions required for Leak Before Break application is the verification that the influence of corrosion environment on the material of the component can be neglected. Both the general corrosion and/or the initiation and, growth of corrosion-mechanical cracks must not cause the degradation. The primary piping in the VVER nuclear power plant is made from austenitic steels (VVER 440) and low alloy steels protected with the austenitic cladding (VVER 1000). Inspection of the base metal and heterogeneous weldments from the VVER 440 showed that the crack growth rates are below 10 m/s if a low oxygen level is kept in the primary environment. No intergranular cracking was observed in low and high oxygen water after any type of testing, with constant or periodic loading. In the framework of the LBB assessment of the VVER 1000, the corrosion and corrosion mechanical properties were also evaluated. The corrosion and corrosion mechanical testing was oriented predominantly to three types of tests: stress corrosion cracking tests corrosion fatigue tests evaluation of the resistance against corrosion damage. In this paper, the methods used for these tests are described and the materials are compared from the point of view of response on static and periodic mechanical stress on the low alloyed steel 10GN2WA and weld metal exposed in the primary circuit environment. The slow strain rate tests and static loading of both C-rings and CT specimens were performed in order to assess the stress corrosion cracking characteristics. Cyclic loading of CT specimens was done to evaluate the kinetics of the crack growth under periodical loading. Results are shown to illustrate the approaches used. The data obtained were evaluated also from the point of view of comparison of the influence of different structure on the stress corrosion cracking appearance. The results obtained for the base metal and weld metal of the piping are presented here.

  6. Improved Stress Corrosion Cracking Resistance and Strength of a Two-Step Aged Al-Zn-Mg-Cu Alloy Using Taguchi Method

    Science.gov (United States)

    Lin, Lianghua; Liu, Zhiyi; Ying, Puyou; Liu, Meng

    2015-12-01

    Multi-step heat treatment effectively enhances the stress corrosion cracking (SCC) resistance but usually degrades the mechanical properties of Al-Zn-Mg-Cu alloys. With the aim to enhance SCC resistance as well as strength of Al-Zn-Mg-Cu alloys, we have optimized the process parameters during two-step aging of Al-6.1Zn-2.8Mg-1.9Cu alloy by Taguchi's L9 orthogonal array. In this work, analysis of variance (ANOVA) was performed to find out the significant heat treatment parameters. The slow strain rate testing combined with scanning electron microscope and transmission electron microscope was employed to study the SCC behaviors of Al-Zn-Mg-Cu alloy. Results showed that the contour map produced by ANOVA offered a reliable reference for selection of optimum heat treatment parameters. By using this method, a desired combination of mechanical performances and SCC resistance was obtained.

  7. Standard Guide for Conducting Corrosion Tests in Field Applications

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2008-01-01

    1.1 This guide covers procedures for conducting corrosion tests in plant equipment or systems under operating conditions to evaluate the corrosion resistance of engineering materials. It does not cover electrochemical methods for determining corrosion rates. 1.1.1 While intended primarily for immersion tests, general guidelines provided can be applicable for exposure of test specimens in plant atmospheres, provided that placement and orientation of the test specimens is non-restrictive to air circulation. 1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. See also 10.4.2.

  8. DEVELOPMENT OF AN EMAT IN-LINE INSPECTION SYSTEM FOR DETECTION, DISCRIMINATION, AND GRADING OF STRESS CORROSION CRACKING IN PIPELINES

    Energy Technology Data Exchange (ETDEWEB)

    Jeff Aron; Jon Gore, Roger Dalton; Stuart Eaton; Adrian Bowles; Owen Thomas; Tim Jarman

    2003-07-01

    This report describes progress, experiments, and results for a project to develop a pipeline inline inspection tool that uses electromagnetic acoustic transducers (EMATs) to detect and grade stress corrosion cracking (SCC). There is a brief introduction that gives background material about EMATs and relevant previous Tuboscope work toward a tool. This work left various choices about the modes and transducers for this project. The experimental section then describes the lab systems, improvements to these systems, and setups and techniques to narrow the choices. Improvements, which involved transducer matching networks, better magnetic biasing, and lower noise electronics, led to improved signal to noise (SNR) levels. The setups permitted transducer characterizations and interaction measurements in plates with man-made cracks, pipeline sections with SCC, and a full pipe with SCC. The latter were done with a moveable and compact EMAT setup, called a lab mouse, which is detailed. Next, the results section justifies the mode and transducer choices. These were for magnetostrictive EMATs and the use of EMAT launched modes: SH0 (at 2.1 MHz-mm) and SV1 (at 3.9 MHz-mm). This section then gives details of measurements on these modes. The measurements consisted of signal to noise ratio, insertion loss, magnetic biasing sensitivities crack reflection and transmission coefficients, beam width, standoff and tilt sensitivities. For most of the measurements the section presents analysis curves, such as reflection coefficient versus crack depth. Some notable results for the chosen modes are: that acceptable SNRs were generated in a pipe with magnetostrictive EMATs, that optimum bias for magnetostrictive transmitters and receivers is magnetic saturation, that crack reflection and transmission coefficients from crack interactions agree with 2 D simulations and seem workable for crack grading, and that the mouse has good waveform quality and so is ready for exhaustive measurement EMAT

  9. The influence of modified water chemistries on metal oxide films, activity build-up and stress corrosion cracking of structural materials in nuclear power plants

    Energy Technology Data Exchange (ETDEWEB)

    Maekelae, K.; Laitinen, T.; Bojinov, M. [VTT Manufacturing Technology, Espoo (Finland)

    1999-03-01

    The primary coolant oxidises the surfaces of construction materials in nuclear power plants. The properties of the oxide films influence significantly the extent of incorporation of actuated corrosion products into the primary circuit surfaces, which may cause additional occupational doses for the maintenance personnel. The physical and chemical properties of the oxide films play also an important role in different forms of corrosion observed in power plants. This report gives a short overview of the factors influencing activity build-up and corrosion phenomena in nuclear power plants. Furthermore, the most recent modifications in the water chemistry to decrease these risks are discussed. A special focus is put on zinc water chemistry, and a preliminary discussion on the mechanism via which zinc influences activity build-up is presented. Even though the exact mechanisms by which zinc acts are not yet known, it is assumed that Zn may block the diffusion paths within the oxide film. This reduces ion transport through the oxide films leading to a reduced rate of oxide growth. Simultaneously the number of available adsorption sites for {sup 60}Co is also reduced. The current models for stress corrosion cracking assume that the anodic and the respective cathodic reactions contributing to crack growth occur partly on or in the oxide films. The rates of these reactions may control the crack propagation rate and therefore, the properties of the oxide films play a crucial role in determining the susceptibility of the material to stress corrosion cracking. Finally, attention is paid also on the novel techniques which can be used to mitigate the susceptibility of construction materials to stress corrosion cracking. (orig.) 127 refs.

  10. Corrosion of steel in cracked concrete: Chloride microanalysis and service life predictions

    NARCIS (Netherlands)

    Pacheco Farias, J.

    2015-01-01

    Reinforcement corrosion is frequently considered as the predominant degradation mechanism affecting reinforced concrete structures. Reinforced concrete structures are commonly subject to harsh environmental and loading conditions in which aggressive species can penetrate. Chlorides, present in

  11. Corrosion of steel in cracked concrete: Chloride microanalysis and service life predictions

    NARCIS (Netherlands)

    Pacheco Farias, J.

    2015-01-01

    Reinforcement corrosion is frequently considered as the predominant degradation mechanism affecting reinforced concrete structures. Reinforced concrete structures are commonly subject to harsh environmental and loading conditions in which aggressive species can penetrate. Chlorides, present in seaw

  12. Evaluation of corrosion damage of aluminum alloy using acoustic emission testing

    Institute of Scientific and Technical Information of China (English)

    GENG Rongsheng; FU Gangqiang

    2004-01-01

    Current studies are aiming at monitoring corrosion damage of aircraft main structures by using acoustic emission (AE) technique and at supplying useful data for determining calendar life of the aircraft. The characteristics of AE signals produced during accelerating corrosion process are described, and methods for evaluating corrosion damages and determining remaining life of main structures of aircraft using AE testing are outlined. Experimental results have shown that AE technique can detect corrosion damage of aluminum alloy much earlier than conventional non-destructive testing means, such as ultrasonic testing and eddy current testing. Relationship between corrosion damage and AE parameters was obtained through investigating corrosion damage extent and changes of AE signals during accelerating corrosion test, and showing that AE technique can be used to detect early corrosion, investigating corrosion developing trend, and in monitoring and evaluating corrosion damages.

  13. Laser Peening for Mitigation of Stress Corrosion Cracking at Welds in Marine Aluminum

    Science.gov (United States)

    2011-06-01

    Second Reader: Joseph C. Farmer THIS PAGE INTENTIONALLY LEFT BLANK i REPORT DOCUMENTATION PAGE Form Approved OMB No. 0704-0188 Public reporting burden...Advisor Joseph C. Farmer Second Reader Knox Millsaps Chair, Department of Mechanical and Aerospace Engineering iv THIS PAGE...Cruisers, in Defense News2010. p. 4. [4] K. N. Tran, M. R. Hill, et al., Welding Journal, 85 (2006) 28. [5] M. G. Fontana , Stress Corrosion, in Corrosion

  14. Electrochemical corrosion testing of fasteners in extracts of treated wood

    Science.gov (United States)

    Samuel L. Zelinka; Douglas R. Rammer; Donald S. Stone

    2008-01-01

    A recent change in wood preservatives has highlighted the need for a rapid, quantitative test to measure the corrosion rates of metals in contact with treated wood that could be used to evaluate new fasteners or new wood preservatives. A new method was developed where polarisation resistance tests were conducted on fasteners exposed to a water extract of wood treated...

  15. Multifunctional Integrated Optic Sensor for Detection of Cracks and Corrosion Project

    Data.gov (United States)

    National Aeronautics and Space Administration — Los Gatos Research proposes to develop a new nondestructive inspection sensor system, capable of simultaneously measuring strain-based load and detecting crack,...

  16. Standard practice for preparation and use of Bent-Beam stress-corrosion test specimens

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2011-01-01

    1.1 This practice covers procedures for designing, preparing, and using bent-beam stress-corrosion specimens. 1.2 Different specimen configurations are given for use with different product forms, such as sheet or plate. This practice applicable to specimens of any metal that are stressed to levels less than the elastic limit of the material, and therefore, the applied stress can be accurately calculated or measured (see Note 1). Stress calculations by this practice are not applicable to plastically stressed specimens. Note 1—It is the nature of these practices that only the applied stress can be calculated. Since stress-corrosion cracking is a function of the total stress, for critical applications and proper interpretation of results, the residual stress (before applying external stress) or the total elastic stress (after applying external stress) should be determined by appropriate nondestructive methods, such as X-ray diffraction (1). 1.3 Test procedures are given for stress-corrosion testing by ex...

  17. Examination of the 1970 National Bureau of Standards Underground Corrosion Test Welded Stainless STeel Coupons from Site D

    Energy Technology Data Exchange (ETDEWEB)

    L. R. Zirker; M. K. Adler Flitton; T. S. Yoder; T. L. Trowbridge

    2008-01-01

    A 1970 study initiated by the National Bureau of Standards (NBS), now known as the National Institute of Standards and Technology (NIST), buried over 6000 corrosion coupons or specimens of stainless steel Types 201, 202, 301, 304, 316, 409, 410, 430, and 434. The coupons were configured as sheet metal plates, coated plates, cross-welded plates, U-bend samples, sandwiched materials, and welded tubes. All coupons were of various heat-treatments and cold worked conditions and were buried at six distinctive soil-type sites throughout the United States. The NBS scientists dug five sets of two trenches at each of the six sites. In each pair of trenches, they buried duplicate sets of stainless steel coupons. The NBS study was designed to retrieve coupons after one year, two years, four years, eight years, and x years in the soil. During the first eight years of the study, four of five planned removals were completed. After the fourth retrieval, the NBS study was abandoned, and the fifth and final set of specimens remained undisturbed for over 33 years. In 2003, an interdisciplinary research team of industrial, university, and national laboratory investigators were funded under the United States Department of Energy’s Environmental Management Science Program (EMSP; Project Number 86803) to extract part of the remaining set of coupons at one of the test sites, characterize the stainless steel underground corrosion rates, and examine the fate and transport of metal ions into the soil. Extraction of one trench at one of the test sites occurred in April 2004. This report details only the characterization of corrosion found on the 14 welded coupons–two cross welded plates, six U-bends, and six welded tubes–that were retrieved from Site D, located near Wildwood, NJ. The welded coupons included Type 301, 304, 316, and 409 stainless steels. After 33 years in the soil, corrosion on the coupons varied according to alloy. This report discusses the stress corrosion cracking and

  18. Effect of ETA treatment on corrosion fatigue in rotors and blades and stress corrosion cracking in 3.5 NiCrMoV steel low-pressure turbine discs

    Energy Technology Data Exchange (ETDEWEB)

    Hitomi, Itoh [Mitsubishi Heavy Industries, Ltd., Takasago Research and Development Center (Japan); Takashi, Momoo [Mitsubishi Heavy Industries, Ltd., Takasago Machinery Works (Japan); Takayuki, Shiomi [Kansai Electric Power Co., Inc., Osaka (Japan)

    2001-07-01

    In recent years, to increase the reliability and reduce the amount of feed water iron to prevent of fouling of steam generator tubes, ethanolamine (ETA) treatment has been adopted into the secondary system. In this investigation, the authors verified that ethanolamine treatment does not adversely affect the susceptibility of either stress corrosion cracking (SCC) in the turbine discs that are the principal units in the secondary system or corrosion fatigue (CF) in rotors and blades. In the first stage, a laboratory investigation was made of (1) SCC initiation and propagation in 3,5 NiCrMoV steel and (2) CF in 3,5 NiCrMoV steel and blade steels, in both cases using deaerated water to which had been added ethanolamine with few organic acids that is 10 times the estimated concentration. It was confirmed that the ethanolamine treatment had almost no effect. In the second stage, test pieces (removed from the disc steel inserted into the turbine extraction chamber before the ethanolamine treatment was started) were used to observe the initiation and propagation of SCC. Even after long-term observation, ethanolamine treatment into the secondary system was found to have almost no effect on the susceptibility of SCC in discs. (author)

  19. Influence of bending test configuration on cracking behavior of FRC

    DEFF Research Database (Denmark)

    Finazzi, Silvia; Paegle, Ieva; Fischer, Gregor;

    2014-01-01

    This paper describes an investigation of the influence of the testing configuration for Fiber Reinforced Concrete in bending and aims at evaluating the influence of the test configuration details on the characterization of the material. Two different types of FRC, Steel Fiber Reinforced Concrete...... (SFRC) and Engineered Cementitious Composites (ECC), were tested and are described in this study. The materials were chosen so that one of them would be strain hardening (ECC) and the other tension softening (SFRC). Notched and un-notched three- and four-point bending tests were carried out to determine...... the flexural load-deformation response of FRC. This research focuses particularly on the influence of the appearance and depth of the notch on the cracking behavior of FRC. For this purpose, several specimens, both un-notched and notched with different depths of the notch (25 mm and 45 mm), were tested...

  20. Experimental Investigation of the Corrosion Behavior of Friction Stir Welded AZ61A Magnesium Alloy Welds under Salt Spray Corrosion Test and Galvanic Corrosion Test Using Response Surface Methodology

    Directory of Open Access Journals (Sweden)

    A. Dhanapal

    2013-01-01

    Full Text Available Extruded Mg alloy plates of 6 mm thick of AZ61A grade were butt welded using advanced welding process and friction stir welding (FSW processes. The specimens were exposed to salt spray conditions and immersion conditions to characterize their corrosion rates on the effect of pH value, chloride ion concentration, and corrosion time. In addition, an attempt was made to develop an empirical relationship to predict the corrosion rate of FSW welds in salt spray corrosion test and galvanic corrosion test using design of experiments. The corrosion morphology and the pit morphology were analyzed by optical microscopy, and the corrosion products were examined using scanning electron microscope and X-ray diffraction analysis. From this research work, it is found that, in both corrosion tests, the corrosion rate decreases with the increase in pH value, the decrease in chloride ion concentration, and a higher corrosion time. The results show the usage of the magnesium alloy for best environments and suitable applications from the aforementioned conditions. Also, it is found that AZ61A magnesium alloy welds possess low-corrosion rate and higher-corrosion resistance in the galvanic corrosion test than in the salt spray corrosion test.

  1. Oblique Y-groove cracking test of the welding cold cracking susceptibility of domestic X-70 pipeline steel

    Institute of Scientific and Technical Information of China (English)

    陈丽萍; 杜则裕; 李云涛; 李九生

    2002-01-01

    "Gas Transmitting From West to East Project" is significant. It should ensure the welding quality and safety of pipeline. The task is very arduous to guarantee the quality of the project in the condition of long line, complex weather and geology features. In this paper, the welding cold cracking susceptibility of domestic X-70 pipeline steel adopted by the project, which is one of the most interesting questions of welding quality about petrol pipeline, was studied by means of oblique Y-groove cracking test. The crack ratio of surface and section was tested under the conditions of different welding materials and preheat temperature .The X-70 pipeline steel has good crack resistance. The research has important value for the construction of large-scale pipeline engineering and the application of domestic X-70 pipeline steel.

  2. Assessing corrosion problems in photovoltaic cells via electrochemical stress testing

    Science.gov (United States)

    Shalaby, H.

    1985-01-01

    A series of accelerated electrochemical experiments to study the degradation properties of polyvinylbutyral-encapsulated silicon solar cells has been carried out. The cells' electrical performance with silk screen-silver and nickel-solder contacts was evaluated. The degradation mechanism was shown to be electrochemical corrosion of the cell contacts; metallization elements migrate into the encapsulating material, which acts as an ionic conducting medium. The corrosion products form a conductive path which results in a gradual loss of the insulation characteristics of the encapsulant. The precipitation of corrosion products in the encapsulant also contributes to its discoloration which in turn leads to a reduction in its transparency and the consequent optical loss. Delamination of the encapsulating layers could be attributed to electrochemical gas evolution reactions. The usefulness of the testing technique in qualitatively establishing a reliability difference between metallizations and antireflection coating types is demonstrated.

  3. Effect of cold work hardening on stress corrosion cracking of stainless steels in primary water of pressurized water reactors

    Energy Technology Data Exchange (ETDEWEB)

    Raquet, O.; Herms, E. [CEA/Saclay, DEN/DPC, 91191 Gif sur Yvette Cedex (France); Vaillant, F.; Couvant, T.; Boursier, J.M. [EDF/Les Renardieres, R and D/MMC, 77250 Moret sur Loing (France)

    2004-07-01

    A R and D program is carried out in CEA and EDF laboratories to investigate separately the effects of factors which could contribute to IASCC mechanism. In the framework of this study, the influence of cold work on SCC of ASSs in primary water is studied to supply additional knowledge concerning the contribution of radiation hardening on IASCC of ASSs. Solution annealed ASSs, essentially of type AISI 304(L) and AISI 316(L), are generally considered very resistant to SCC in nominal primary water. However, Constant Extension Rate Tests (CERTs), performed on cold pressed humped specimens in nominal primary water at 360 deg. C, reveal that these materials can exhibit a high SCC susceptibility: deepest cracks reach 1 mm (mean crack growth rate about 1 {mu}m.h{sup -1}) and propagation is mainly intergranular for 304L and mainly transgranular for 316L. Indeed, work hardening in conjunction with high localized deformation can promote SCC. The influence of the nature of the cold work (shot peening, reaming, cold rolling, counter sinking, fatigue work hardening and tensile deformation) is investigated by means of screening CERTs performed with smooth specimens in 304L at 360 deg. C. For a given cold work hardening level, the susceptibility to crack initiation strongly depends on the cold working process, and no propagation is observed for a hardness level lower than 300 {+-}10 HV(0.49N). The propagation of cracks is observed only for dynamic loadings like CERT, traction/relaxation tests and crack growth rate tests performed with CT specimens under trapezoidal loading. Although crack initiation is observed for constant load and constant deformation tests, crack propagation do not seem to occur under these mechanical solicitations for 17000 hours of testing, even for hardness levels higher than 450 HV(0.49N). The mean crack growth rate increases when the hardness increases. An important R and D program is in progress to complement these results and to develop a SCC model for

  4. 裂缝对混凝土内氯离子扩散和钢筋锈蚀的影响%INFLUENCE OF CRACKS ON CHLORIDE DIFFUSION AND REINFORCEMENT CORROSION IN CONCRETE

    Institute of Scientific and Technical Information of China (English)

    张邵峰; 陆春华; 陈妤; 刘荣桂; 崔钊玮

    2012-01-01

    To study the influence of load-induced cracks on chloride diffusion and reinforcement corrosion in reinforced concrete (RC), eight RC beams with pre-cracks or flexural cracks were immersed in chloride solution with the condition of a dry-wet cycle. Then a half-cell potential method and a RCT (Rapid Chloride Test) were used to evaluate reinforcement corrosion and chloride concentration. Finally, the finite element analysis software ADINA was used to simulate the two-dimensional diffusion of chloride in cracked concrete. Results showed that: 1) Cracks accelerated the chloride penetration in concrete, which will lead to the premature corrosion of rebar and provided conditions for the local two-dimensional diffusion of chloride; 2) The wider the crack width or the smaller the spacing is, the greater effective it did to the chloride-induced corrosion of rebar; 3) Simulation results agree well with experimental results.%为了研究受力裂缝对混凝土内氯离子扩散的影响,对8根开裂(预制裂缝和受弯裂缝)的钢筋混凝土梁试件进行了盐溶液干湿循环试验;并采用半电池电位法和RCT(快速氯离子含量检测)法,分别对梁内钢筋的锈蚀状态以及各裂缝处氯离子含量进行了检测;最后采用ADINA有限元软件对开裂混凝土内氯离子的二维扩散行为进行模拟分析.试验和模拟结果表明:1)裂缝加速了氯离子的侵入,导致钢筋过早的开始锈蚀,且为局部氯离子的二维扩散提供了条件;2)裂缝宽度越大或间距越小,其对氯离子侵入引起的钢筋锈蚀影响程度越大;3)有限元模型的计算与试验结果吻合较好.

  5. The Effect of Sensitization on the Stress Corrosion Cracking of Aluminum Alloy 5456

    Science.gov (United States)

    2012-06-01

    electrochemically active particles. (From Jones, [26]) ....................................23 Figure 16. Illustration of corrosion tunnel model. (a) Schematic of...46 Table 6. Grinding and Polishing Conditions...approaches continuity along grain boundaries. The β phase is more anodic than the surrounding material matrix and therefore is electrochemically more

  6. Stress corrosion cracking behavior of Alloy 600 in high temperature water

    Energy Technology Data Exchange (ETDEWEB)

    Webb, G.L.; Burke, M.G.

    1995-07-01

    SCC susceptibility of Alloy 600 in deaerated water at 360 C (statically loaded U-bend specimens) is dependent on microstructure and whether the material was cold-worked and annealed (CWA) or hot-worked and annealed (HWA). All cracking was intergranular, and materials lacking grain boundary carbides were most susceptible to SCC initiation. CWA tubing materials are more susceptible to SCC initiation than HWA ring-rolled forging materials with similar microstructures (optical metallography). In CWA tubing materials, one crack dominated and grew to a visible size. HWA materials with a low hot-working finishing temperature (<925 C) and final anneals at 1010-1065 C developed both large cracks (similar to those in CWA materials) and small intergranular microcracks detectable only by destructive metallography. HWA materials with a high hot-working finishing temperature (>980 C) and a high-temperature final anneal (>1040 C), with grain boundaries that are fully decorated, developed only microcracks in all specimens. These materials did not develop large, visually detectable cracks, even after more than 300 weeks exposure. A low-temperature thermal treatment (610 C for 7h), which reduces or eliminates SCC in Alloy 600, did not eliminate microcrack formation in high temperature processed HWA materials. Conventional metallographic and analytical electron microscopy (AEM) were done on selected materials to identify the factors responsible for the observed differences in cracking behavior. Major difference between high-temperature HWA and low-temperature HWA and CWA materials was that the high temperature processing and final annealing produced predominantly ``semi-continuous`` dendritic M{sub 7}C{sub 3} carbides along grain boundaries with a minimal amount of intragranular carbides. Lower temperature processing produced intragranular M7C3 carbides, with less intergranular carbides.

  7. Propagation of cracks by stress corrosion in conditions of BWR type reactor; Propagacion de grietas por corrosion bajo esfuerzo en condiciones de reactor de agua en ebullicion (BWR)

    Energy Technology Data Exchange (ETDEWEB)

    Merino C, F.J. [ININ, 52045 Estado de Mexico (Mexico); Fuentes C, P. [ITT, Metepec, Estado de Mexico (Mexico)]. E-mail: fjmc@nuclear.inin.mx

    2004-07-01

    In this work, the obtained results when applying the Hydrogen Chemistry to a test tube type Compact Tension (CT), built in austenitic stainless steel 304l, simulating the conditions to those that it operates a Boiling Water Reactor (BWR), temperature 288 C and pressure of 8 MPa are presented. With the application of this water chemistry, seeks to be proven the diminution of the crack propagation speed. (Author)

  8. Status of coal ash corrosion resistant materials test program

    Energy Technology Data Exchange (ETDEWEB)

    McDonald, D.K.; Meisenhelter, D.K.; Sikka, V.K.

    1999-07-01

    In November of 1998, Babcock and Wilcox (B and W) began development of a system to permit testing of several advanced tube materials at metal temperatures typical of advanced supercritical steam conditions of 1100 F and higher in a boiler exhibiting coal ash corrosive conditions. The U.S. Department of Energy (DOE), the Ohio Coal Development Office (OCDO), B and W, and First Energy's Ohio Edison jointly fund the project. CONSOL Energy Company is also participating as an advisor. Several materials producers including Oak Ridge National Laboratory (ORNL) contributed advanced materials to the project. The coal-ash corrosion resistant materials test program will provide full scale, in-situ testing of recently developed boiler superheater and reheater tube materials. These newer materials may be capable of operating at higher steam temperatures while resisting external/fire-side corrosion. For high sulfur coal applications, this is a key issue for advanced cycle pulverized coal-fired plants. Fireside corrosion is also a critical issue for many existing plants. Previous testing of high temperature materials in the United States has been based primarily on using laboratory test coupons. The test coupons did not operate at conditions representative of a high sulfur coal-fired boiler. Testing outside of the United States has been with low sulfur coal or natural gas firing and has not addressed corrosion issues. This test program takes place in an actual operating boiler and is expected to confirm the performance of these materials with high sulfur coal. The system consists of three identical sections, each containing multiple pieces of twelve different materials. They are cooled by reheater steam, and are located just above the furnace exit in Ohio Edison's Niles Unit No.1, a 110 MWe unit firing high sulfur Ohio coal. After one year of operation, the first section will be removed for thorough metallurgical evaluation. The second and third sections will operate for

  9. Numerical simulation of the detection of crack in reinforced concrete structures of NPP due to expansion of reinforcing corrosive products using Impact-Echo method

    Directory of Open Access Journals (Sweden)

    Morávka Š.

    2008-12-01

    Full Text Available Nuclear energy boom is starting nowadays. But also current nuclear power plants (NPP are duty to certify their security for regular renewal of their operating licenses. NPP security can be significantly affected by defects of large amount of ageing reinforced concrete structures. Advanced Impact-Echo method seams to be very hopeful to cooperate at performing in-service inspections such structures. Just these in-service inspections are included in the first priority group of specific technical issues according to the recommendations of OECD-Nuclear Energy Agency, Commission on Safety of Nuclear Installation in the field of ageing management.This paper continues of extensive project dealing with Impact-Echo method application. It will present method description and main results of numerical modeling of detection and localization of crack caused by corrosive product expansion. Steel reinforcing rods are subjected to corrosion due to diffusion of corrosive agents from structure surface. Corrosive products have up to 7-times larger volume than pure steel. Raised strain can cad lead up to concrete failure and crack development. We investigate whether it is possible to detect these growing cracks by Impact-Echo method in time.Experimental verification of our numerical predictions is prepared on Civil Faculty in Brno.

  10. Integration of Nanofluids into Commercial Antifreeze Concentrates with ASTM D15 Corrosion Testing

    Science.gov (United States)

    2013-05-01

    Corrosion Tests ASTM D 1384 Corrosion Test for Engine Coolants in Glassware and ASTM D 4340 Corrosion Test of Cast Aluminum Alloys in Engine Coolants...Saint-Gobain provided free nano slurry samples (300 nm, 360 nm, 13 mass% in water). 80 nm powders were purchased from NanoAmor. Diamond: 6 nm nano

  11. Static Corrosion Test of Porous Iron Material with Polymer Coating

    Science.gov (United States)

    Markušová-Bučková, Lucia; Oriňaková, Renáta; Oriňak, Andrej; Gorejová, Radka; Kupková, Miriam; Hrubovčáková, Monika; Baláž, Matej; Kováľ, Karol

    2016-12-01

    At present biodegradable implants received increased attention due to their use in various fields of medicine. This work is dedicated to testing of biodegradable materials which could be used as bone implants. The samples were prepared from the carbonyl iron powder by replication method and surface polymer film was produced through sol-gel process. Corrosion testing was carried out under static conditions during 12 weeks in Hank's solution. The quantity of corrosion products increased with prolonging time of static test as it can be concluded from the results of EDX analysis. The degradation of open cell materials with polyethylene glycol coating layer was faster compared to uncoated Fe sample. Also the mass losses were higher for samples with PEG coating. The polymer coating brought about the desired increase in degradation rate of porous iron material.

  12. Implication of Atmospheric Wetness Levels on Corrosion at a Coating Defect during Accelerated Testing

    Science.gov (United States)

    2012-08-28

    Outline • Objectives • Atmospheric corrosionTesting Approach • Effect of RH on corrosion of steel • Effect of inhibitor addition on coated steel... inhibitor migration in the coating . For a given test method, wet and dry times will influence inhibitor mobility, and thus corrosion rate Continuous...Implication of Atmospheric Wetness Levels on Corrosion at a Coating Defect during Accelerated Testing James F. Dante Southwest Research Institute

  13. Flexural behavior of bonded post-tensioned concrete beams under strand corrosion

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Xuhui [College of Civil Engineering and Mechanics, Xiangtan University, 411105 Xiangtan (China); School of Civil Engineering and Architecture, Changsha University of Science & Technology, 410114 Changsha (China); Industry Key Laboratory of Traffic Infrastructure Security Risk Management (CSUST), 410114 Changsha (China); Wang, Lei, E-mail: leiwlei@hotmail.com [School of Civil Engineering and Architecture, Changsha University of Science & Technology, 410114 Changsha (China); Industry Key Laboratory of Traffic Infrastructure Security Risk Management (CSUST), 410114 Changsha (China); Zhang, Jianren; Ma, Yafei [School of Civil Engineering and Architecture, Changsha University of Science & Technology, 410114 Changsha (China); Industry Key Laboratory of Traffic Infrastructure Security Risk Management (CSUST), 410114 Changsha (China); Liu, Yongming [School for Engineering of Matter, Transport and Energy, Arizona State University, 85281 Tempe, AZ (United States)

    2017-03-15

    Highlights: • Flexural behavior of bonded PT beams with strand corrosion is experimental tested. • Cracking, stiffness, ultimate strength, failure & ductility of beams are clarified. • A coefficient is proposed to measure incompatible strain between strand & concrete. - Abstract: An experimental test is performed to investigate the flexural behavior of bonded post-tensioned concrete beams under strand corrosion. Eight beams are designed and subjected to accelerated method to different corrosion levels. The initial stiffness of beams is observed by cyclic loading-unloading test during the corrosion procedure. Corrosion effects on concrete cracking, post-cracking stiffness, ultimate strength, failure mode and ductility are then clarified by the flexural test. And, a coefficient is introduced to quantify the incompatible strain between corroded strand and concrete. Results show that the prestress force loss of strand has almost the linear relation with corrosion loss. Strand corrosion affects slightly the initial stiffness of beam before flexural cracking, but degrades significantly the post-cracking stiffness of beam as the corrosion loss exceeds 27.0%. Slight corrosion of strand has little effects on beams flexural behavior. The severe corrosion, however, decreases the number of crack, changes the failure mode form the concrete crushing to strand rupture, degrades the ductility and the ultimate strength of beams, and leads to the incompatible strain between strand and concrete. In the present test, the incompatible strain decreases about 20% of the flexural strength as the corrosion loss exceeds 27.0%.

  14. Effect of crack blunting in liquid metal environments on K-IEAC determined by the rising load test

    CSIR Research Space (South Africa)

    Fernandes, PJL

    1996-09-01

    Full Text Available corrosion conditions has been well documented \\[12\\]. Wheeler et al. \\[13\\] have reported similar results in the case of crack growth in the aluminium-molten mercury system. By changing the loading conditions from fixed... at lower crack growth rates, the crack would initially accelerate, but would then decelerate and eventually arrest. This behaviour is shown schematically in Fig. 3. Wheeler et al. \\[13\\] showed that these observations were...

  15. Corrosion testing of candidates for the alkaline fuel cell cathode

    Science.gov (United States)

    Singer, Joseph; Fielder, William L.

    1989-01-01

    Current/voltage data was obtained for specially made corrosion electrodes of some oxides and of gold materials for the purpose of developing a screening test of catalysts and supports for use at the cathode of the alkaline fuel cell. The data consists of measurements of current at fixed potentials and cyclic voltammograms. These data will have to be correlated with longtime performance data in order to fully evaluate this approach to corrosion screening. Corrosion test screening of candidates for the oxygen reduction electrode of the alkaline fuel cell was applied to two substances, the pyrochlore Pb2Ru2O6.5 and the spinel NiCo2O4. The substrate gold screen and a sample of the IFC Orbiter Pt-Au performance electrode were included as blanks. The pyrochlore data indicate relative stability, although nothing yet can be said about long term stability. The spinel was plainly unstable. For this type of testing to be validated, comparisons will have to be made with long term performance tests.

  16. Testing and analysis of photovoltaic modules for electrochemical corrosion

    Science.gov (United States)

    Neff, Michael; Mon, Gordon R.; Whitla, Guy; Ross, Russ, Jr.

    1986-01-01

    This paper describes the testing and evaluation used to characterize the mechanisms of electrochemical corrosion of photovoltaic modules - encapsulated solar cells. Accelerated exposure testing was performed on a sample matrix of cell/encapsulant combinations, and microanalytical failure analysis was performed on selected samples to confirm the correlation between the accelerated test data and the life prediction model. A quantitative correlation between field exposure time and exposure time in the accelerated multistress tests was obtained based upon the observation that equal quantities of interelectrode charge transfer resulted in equivalent degrees of electrochemical charge.

  17. Construction and testing of a hydrogen cracking cell

    Directory of Open Access Journals (Sweden)

    F Sahra Gard

    2011-12-01

    Full Text Available A UHV atomic hydrogen-cracking cell has been constructed to produce atomic hydrogen in order to perform in-situ cleaning of semiconductor samples. The cell was calibrated and tested with the objective of cleaning the III-V semiconductor samples such as GaAs. Mass spectroscopy studies during the atomic hydrogen cleaning of the GaAs samples revealed the chemical process of the hydrogen cleaning. X-ray Photoemission Spectroscopy (XPS was also carried out on the samples at different stages of cleaning. Desorption of the native oxide from GaAs samples resulted in a smooth surface, which was confirmed by Reflection High Energy Electron Diffraction (RHEED.

  18. Critical issues in De-alloying and transcrystalline stress-corrosion cracking

    Energy Technology Data Exchange (ETDEWEB)

    Sieradzki, K.; Wagner, J.W.

    1992-03-01

    This report describes our progress since the last reporting reporting period (March 1991) and details the third year research plans on the program. The three major components of the program relate to (1) kinetic aspects of the selective dissolution in alloys and the coarsening of de-alloyed layers, (2) measurements of crack dynamics during film induced cleavage processes, and (3) mechanical properties of the intrinsic de-alloyed layers responsible for film-induced cleavage events. We discuss progress in each of these areas below.

  19. Corrosion Tests of Metals and Ceramics

    Science.gov (United States)

    1951-01-01

    well as technical judgment, were the factors that limited the number of materials tested. Therefore, it is possible that some materials not included...in fig. 12); depth of penetration was taken as the distance from the original top surface to the dis- cernible limit of penetration of the fluid...II I Moodl ------- ------- ------- 0-oNi 󈧒 Cal, 2 Fe, 1.5 Mni. 1.5(---- 1. IV, V. vI. viI, X, XI, XV , XvI. Moor) K ------------------ b 4’ , MI Cu

  20. Assessment of stress-corrosion cracking in a water-cooled ITER

    Energy Technology Data Exchange (ETDEWEB)

    Jones, R.H.; Bruemmer, S.M.

    1989-04-01

    Water-cooled, near-term reactors will operate under conditions at which SCC is possible; however, control of material purity and processing and coolant chemistry can either eliminate or greatly reduce the probability of this type of structural failure. This evaluation has focused on an assessment of water impurity effects on SCC of austenitic stainless steel at temperatures below 100{degree}C and on the conditions controlling sensitization in the fusion heat of Type 316 SS and the fusion materials heat of modified Type 316 SS designated as PCA. This assessment identifies the dominant effect of small concentrations of impurities in high-purity water on SCC such that crack growth rates at 25--75{degree}C in water with as little as 5--15 ppM Cl{sup {minus}} are equal to the crack growth rates at 200--300{degree}C in high-purity water. These effects are primarily for sensitized Type 304 SS, so analysis of sensitization behavior of fusion austenitic alloys was also undertaken. An SSDOS model developed at PNL was used to make these assessments, and correlation to experimental results for Type 316 SS was very good. Both the fusion heat of Type 316 SS and PCA can be severely sensitized but with proper thermal treatment it should be possible to avoid sensitization. 14 refs., 8 figs.

  1. Environmental Degradation of Materials: Surface Chemistry Related to Stress Corrosion Cracking

    Science.gov (United States)

    Schwarz, J. A.

    1985-01-01

    Parallel experiments have been performed in order to develop a comprehensive model for stress cracking (SCC) in structural materials. The central objective is to determine the relationship between the activity and selectivity of the microstructure of structural materials to their dissolution kinetics and experimentally measured SCC kinetics. Zinc was chosen as a prototype metal system. The SCC behavior of two oriented single-crystal disks of zinc in a chromic oxide/sodium sulfate solution (Palmerton solution) were determined. It was found that: (1) the dissolution rate is strongly (hkil)-dependent and proportional to the exposure time in the aggressive environment; and (2) a specific slip system is selectively active to dissolution under applied stress and this slip line controls crack initiation and propagation. As a precursor to potential microgrvity experiments, electrophoretic mobility measurements of zinc particles were obtained in solutions of sodium sulfate (0.0033 M) with concentrations of dissolved oxygen from 2 to 8 ppm. The equilibrium distribution of exposed oriented planes as well as their correlation will determine the particle mobility.

  2. Environmental Degradation of Materials: Surface Chemistry Related to Stress Corrosion Cracking

    Science.gov (United States)

    Schwarz, J. A.

    1985-01-01

    Parallel experiments have been performed in order to develop a comprehensive model for stress cracking (SCC) in structural materials. The central objective is to determine the relationship between the activity and selectivity of the microstructure of structural materials to their dissolution kinetics and experimentally measured SCC kinetics. Zinc was chosen as a prototype metal system. The SCC behavior of two oriented single-crystal disks of zinc in a chromic oxide/sodium sulfate solution (Palmerton solution) were determined. It was found that: (1) the dissolution rate is strongly (hkil)-dependent and proportional to the exposure time in the aggressive environment; and (2) a specific slip system is selectively active to dissolution under applied stress and this slip line controls crack initiation and propagation. As a precursor to potential microgrvity experiments, electrophoretic mobility measurements of zinc particles were obtained in solutions of sodium sulfate (0.0033 M) with concentrations of dissolved oxygen from 2 to 8 ppm. The equilibrium distribution of exposed oriented planes as well as their correlation will determine the particle mobility.

  3. Potential mechanisms for corrosion and stress corrosion cracking failure of 3013 storage containers composed of 316 stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Kolman, D.G.; Butt, D.P.

    1998-03-01

    The degradation of 316 stainless steel (SS) storage container materials is a potential problem for radioactive waste disposition. Container materials will be exposed to significant ionizing radiation, elevated temperatures, embrittling and/or alloying agents (e.g., gallium), chloride-containing compounds (as much as 20 wt% Cl or Cl{sup {minus}}), oxidizing compounds, and a limited quantity of moisture. Additionally, containers will contain welds that have heterogeneous composition due to solute segregation and that may retain significant residual stress. All of the above-listed environmental and material conditions have been shown to be deleterious to material integrity under certain conditions. Unfortunately, the precise conditions within each container and environment is unknown and may vary widely from container to container. Thus, no single test or set of tests will be able mimic the broad range of storage container conditions. Additionally, material behavior cannot be predicted because the synergistic effects of temperature, time, chloride, moisture, sensitization, weldments, salt formation, etc., have not been fully studied. The complexity and uncertainty of storage conditions precludes any detailed recommendations. This document attempts to detail selected previous studies and to suggest some general guidelines for storage of radioactive waste. Because of the voluminous research in this area, this review cannot be considered to be comprehensive. Readers are directed to references that contain detailed reviews of particular processes for more information. Note that the effect of gallium on the degradation of SS storage containers has been discussed elsewhere and will not be discussed here.

  4. Review of Corrosion Modes for Alloy 22 Regarding Lifetime Expectancy of Nuclear Waste Containers

    Energy Technology Data Exchange (ETDEWEB)

    Rebak, R B; Estill, J C

    2002-11-15

    Alloy 22 (UNS N06022) was selected to fabricate the corrosion resistant outer barrier of a two-layer waste package container for nuclear waste at the designated repository site in Yucca Mountain in Nevada (USA). A testing program is underway to characterize and quantify three main modes of corrosion that may occur at the site. Current results show that the containers would perform well under general corrosion, localized corrosion and environmentally assisted cracking (EAC). For example, the general corrosion rate is expected to be below 100 nm/year and the container is predicted to be outside the range of potential for localized corrosion and environmentally assisted cracking.

  5. Analysis on the internal cracking of concrete cover due to rebar uniform corrosion%混凝土保护层均匀锈胀内裂分析

    Institute of Scientific and Technical Information of China (English)

    姜慧; 喻孟雄; 刘荣桂

    2014-01-01

    钢筋锈蚀是影响钢筋混凝土结构使用寿命的重要因素,混凝土保护层锈胀内裂加速整个混凝土保护层的开裂。假定混凝土满足最大伸长线应变破坏准则,利用圆孔扩张理论对铁锈自由膨胀充满混凝土与钢筋交界面空隙后混凝土保护层内裂进行分析,建立了锈胀内裂时刻的钢筋锈蚀深度计算式。针对计算式主要影响参数的分析表明:钢筋锈蚀深度与水泥石中毛细孔体积、钢筋直径、混凝土极限拉应变成正相关,与铁锈体积膨胀率成负相关。%Rebar corrosion is an important factor affecting the service life of reinforced concrete structures.Concrete cover internal cracking induced by reinforcement corrosion accelerates cracking of all cover.Based on the assumption of concrete meet the maximum ten-sional strain failure criterion,one equation for predicting the reinforcement corrosion depth from corrosion initiation to cover internal cracking was established according to the cylindrical cavity expansion theory.By analyzing main parameters of the equation ,the results showed that the reinforcement corrosion depth was positive correlation with cement stone pore volume,diameter of rebar,concrete ulti-mate tensile strain,and negative correlation with rust rate of volume expansion.

  6. Time exposure studies on stress corrosion cracking of aluminum 2014-T6, 2219-T87, 2014-T651, 7075-T651, and titanium 6Al-4V

    Science.gov (United States)

    Terrell, J.

    1973-01-01

    The effect of a constant applied stress in crack initiation of aluminum 2014-T6, 2219-T87, 2014-T651, 7075-T651 and titanium 6Al-4V has been investigated. Aluminum c-ring specimens (1-inch diameter) and u-band titanium samples were exposed continuously to a 3.5% NaCl solution (pH 7) and organic fluids of ethyl, methyl, and iso-propyl alcohol (reagent purity), and demineralized distilled water. Corrosive action was observed to begin during the first and second day of constant exposure as evidenced by accumulation of hydrogen bubbles on the surface of stressed aluminum samples. However, titanium stressed specimens showed no reactions to its environment. Results of this investigation seems to suggest that aluminum 2014-T6, aluminum 7075-T651 and aluminum 2014-T651 are susceptible to stress corrosion cracking in chloride solution (NaCl), while aluminum 2219-T87 seem to resist stress corrosion cracking in sodium chloride at three levels of stress (25%, 50%, and 75% Y.S.). In organic fluids of methyl, ethyl, and iso-propyl alcohol, 2014-T6 and 7075-T651 did not fail by SCC; but 2014-T651 was susceptible to SCC in methly alcohol, but resistant in ethyl alcohol, iso-propyl alcohol and demineralized distilled water.

  7. Time exposure studies on stress corrosion cracking of aluminum 2014-T6, aluminum 7075-T651, and titanium 6Al-4V

    Science.gov (United States)

    Terrell, J.

    1972-01-01

    The effect of a constant applied stress in crack initiation of aluminum 2014-T6, 7075-T651 and titanium 6A1-4V has been investigated. Aluminum c-ring specimens (1-inch diameter) and u-band titanium samples were exposed continuously to a 3.5% NaCl solution (pH 6) and organic fluids of ethyl, methyl, and iso-propyl alcohol (reagent purity). Corrosive action was observed to begin during the first and second day of constant exposure as evidenced by accumulation of hydrogen bubbles on the surface of stressed aluminum samples. However, a similar observation was not noted for titanium stressed specimens. Results of this investigation seems to suggest that aluminum 2014-T6, aluminum 7075-T651 are susceptible to stress corrosion cracking in chloride solution (NaCl); while they (both alloys) seem to resist stress corrosion cracking in methyl alcohol, ethyl alcohol, iso-propyl alcohol, and demineralized distilled water. Titanium 6A1-4V showed some evidence of susceptibility to SCC in methanol, while no such susceptibility was exhibited in ethanol, iso-propyl alcohol and demineralized distilled water.

  8. Cracking and Corrosion of Composite Tubes in Black Liquor Recovery Boiler Primary Air Ports

    Energy Technology Data Exchange (ETDEWEB)

    Keiser, James R.; Singbeil, Douglas L.; Sarma, Gorti B.; Kish, Joseph R.; Yuan, Jerry; Frederick, Laurie A.; Choudhury, Kimberly A.; Gorog, J. Peter; Jetté, Francois R.; Hubbard, Camden R.; Swindeman, Robert W.; Singh, Prett M.; Maziasz, Phillip J.

    2006-10-01

    Black liquor recovery boilers are an essential part of kraft mills. Their design and operating procedures have changed over time with the goal of providing improved boiler performance. These performance improvements are frequently associated with an increase in heat flux and/or operating temperature with a subsequent increase in the demand on structural materials associated with operation at higher temperatures and/or in more corrosive environments. Improvements in structural materials have therefore been required. In most cases the alternate materials have provided acceptable solutions. However, in some cases the alternate materials have solved the original problem but introduced new issues. This report addresses the performance of materials in the tubes forming primary air port openings and, particularly, the problems associated with use of stainless steel clad carbon steel tubes and the solutions that have been identified.

  9. Minimum fatigue pre-crack extension for fracture testing

    NARCIS (Netherlands)

    Walters, C.L.; Voormeeren, L.O.

    2013-01-01

    The minimum pre-crack necessary to achieve an accurate measurement of the J-integral is examined with the use of elastic-plastic finite element analysis. This minimum pre-crack is shorter than what is specified in fracture codes ASTM E1820 and BS 7448. A variety of steel properties are considered, b

  10. DEVELOPMENT OF AN EMAT IN-LINE INSPECTION SYSTEM FOR DETECTION, DISCRIMINATION, AND GRADING OF STRESS CORROSION CRACKING IN PIPELINES

    Energy Technology Data Exchange (ETDEWEB)

    Jeff Aron; Jeff Jia; Bruce Vance; Wen Chang; Raymond Pohler; Jon Gore; Stuart Eaton; Adrian Bowles; Tim Jarman

    2005-02-01

    This report describes prototypes, measurements, and results for a project to develop a prototype pipeline in-line inspection (ILI) tool that uses electromagnetic acoustic transducers (EMATs) to detect and grade stress corrosion cracking (SCC). The introduction briefly provides motivation and describes SCC, gives some background on EMATs and guided ultrasonic waves, and reviews promising results of a previous project using EMATs for SCC. The experimental section then describes lab measurement techniques and equipment, the lab mouse and prototypes for a mule, and scan measurements made on SCC. The mouse was a moveable and compact EMAT setup. The prototypes were even more compact circuits intended to be pulled or used in an ILI tool. The purpose of the measurements was to determine the best modes, transduction, and processing to use, to characterize the transducers, and to prove EMATs and mule components could produce useful results. Next, the results section summarizes the measurements and describes the mouse scans, processing, prototype circuit operating parameters, and performance for SH0 scans. Results are given in terms of specifications--like SNR, power, insertion loss--and parametric curves--such as signal amplitude versus magnetic bias or standoff, reflection or transmission coefficients versus crack depth. Initially, lab results indicated magnetostrictive transducers using both SH0 and SV1 modes would be worthwhile to pursue in a practical ILI system. However, work with mule components showed that SV1 would be too dispersive, so SV1 was abandoned. The results showed that reflection measurements, when normalized by the direct arrival are sensitive to and correlated with SCC. This was not true for transmission measurements. Processing yields a high data reduction, almost 60 to 1, and permits A and C scan display techniques and software already in use for pipeline inspection. An analysis of actual SH0 scan results for SCC of known dimensions showed that length

  11. Novel accelerated corrosion test for LY12CZ and LC4CS aluminum alloys

    Institute of Scientific and Technical Information of China (English)

    CAI Jian-ping; LIU Ming

    2006-01-01

    A new accelerated corrosion test-comprehensive environmental test (CET) was developed in order to estimate the outdoor corrosion of aluminum alloys in marine environment. The environmental characteristics in CET were studied by atmospheric corrosion monitor (ACM), and the morphology of corrosion product was observed by SEM. The correlation between the accelerated corrosion tests and outdoor exposure was discussed. The results show that the anti-corrosion ranking for LY12CZ, LC4CS, clad LY12CZ, and clad LC4CS in CET is the same as that of the alloys exposed outdoor, and ACM study shows that CET demonstrates the same environmental characteristics as that exposed outdoor. CET is a more accurate accelerated corrosion test, and a mathematical relation was obtained to describe the relation between CET and outdoor test.

  12. Stress Corrosion Cracking of the Drip Shield, The Waste Package Outer Barrier and the Stainless Steel Structural Material

    Energy Technology Data Exchange (ETDEWEB)

    C. Stephen

    2000-04-17

    One of the potential failure modes of the drip shield (DS), the waste package (WP) outer barrier, and the stainless structural material is the initiation and propagation of stress corrosion cracking (SCC) induced by the WP environment and various types of stresses that can develop in the DSs or the WPs. For the current design of the DS and WP, however, the DS will be excluded from the SCC evaluation because stresses that are relevant to SCC are insignificant in the DS. The major sources of stresses in the DS are loadings due to backfill and earthquakes. These stresses will not induce SCC because the stress caused by backfill is generally compressive stress and the stress caused by earthquakes is temporary in nature. The 316NG stainless steel inner barrier of the WP will also be excluded from the SCC evaluation because the SCC performance assessment will not take credit from the inner barrier. Therefore, the purpose of this document is to provide a detailed description of the process-level models that can be applied to assess the performance of the material (i.e., Alloy 22) used for the WP outer barrier subjected to the effects of SCC. As already mentioned in the development plan for the WP PMR (CRWMS M and O 1999e), this Analyses and Models Report (AMR) is to serve as a feed to the Waste Package Degradation (WPD) Total System Performance Assessment (TSPA) and Process Model Report (PMR).

  13. Primary Water Stress Corrosion Cracks in Nickel Alloy Dissimilar Metal Welds: Detection and Sizing Using Established and Emerging Nondestructive Examination Techniques

    Energy Technology Data Exchange (ETDEWEB)

    Braatz, Brett G.; Cumblidge, Stephen E.; Doctor, Steven R.; Prokofiev, Iouri

    2012-12-31

    The U.S. Nuclear Regulatory Commission has established the Program to Assess the Reliability of Emerging Nondestructive Techniques (PARENT) as a follow-on to the international cooperative Program for the Inspection of Nickel Alloy Components (PINC). The goal of PINC was to evaluate the capabilities of various nondestructive evaluation (NDE) techniques to detect and characterize surface-breaking primary water stress corrosion cracks in dissimilar-metal welds (DMW) in bottom-mounted instrumentation (BMI) penetrations and small-bore (≈400-mm diameter) piping components. A series of international blind round-robin tests were conducted by commercial and university inspection teams. Results from these tests showed that a combination of conventional and phased-array ultrasound techniques provided the highest performance for flaw detection and depth sizing in dissimilar metal piping welds. The effective detection of flaws in BMIs by eddy current and ultrasound shows that it may be possible to reliably inspect these components in the field. The goal of PARENT is to continue the work begun in PINC and apply the lessons learned to a series of open and blind international round-robin tests that will be conducted on a new set of piping components including large-bore (≈900-mm diameter) DMWs, small-bore DMWs, and BMIs. Open round-robin testing will engage universities and industry worldwide to investigate the reliability of emerging NDE techniques to detect and accurately size flaws having a wide range of lengths, depths, orientations, and locations. Blind round-robin testing will invite testing organizations worldwide, whose inspectors and procedures are certified by the standards for the nuclear industry in their respective countries, to investigate the ability of established NDE techniques to detect and size flaws whose characteristics range from easy to very difficult to detect and size. This paper presents highlights of PINC and reports on the plans and progress for

  14. Burst tests on pipeline with long external corrosion

    Energy Technology Data Exchange (ETDEWEB)

    Benjamin, A.C. [Rio de Janeiro Univ., (Brazil); Vieira, R.D.; Freire, J.L.F.; Castro, J.T.P. de [PUC, Rio de Janeiro (Brazil)

    2000-07-01

    Four different methods are available to assess long corrosion defects. They are: ASME B31G, RSTRENG 085dL, RSTRENG Effective Area, and the DNV RP-F101 (Part B). The degree of conservatism in each method varies considerably, making the maintenance and repair costs higher than they could be, since pipes still fit for service are replaced based on the results obtained in evaluating pressure strength. Petrobras initiated a research project aimed at assessing the behavior of pipeline with long corrosion defects. CONFAB S.A., a Brazilian manufacturer of steel tubes, donated 5 longitudinal welded tubes made of API 5L X60 steel. The wall thickness was 9.53 mm and the outside diameter was 323.9 mm. Two tubular specimens 2 m long were cut from each of the tubes, except for one tube where only one 2 m long section was cut. Burst tests were conducted on the specimens, where the corrosion defects were smooth and rectangular, having been fabricated using spark erosion. Material properties were determined on tensile specimens. 10 post-yield strain gages rosettes, one displacement transducer and three pressure transducers were affixed to the corroded specimens. A comparison of the measured burst pressures was made as predicted by the four methods under investigation. 11 refs., 4 tabs., 5 figs.

  15. Erosion/corrosion testing of materials for oil sands applications

    Energy Technology Data Exchange (ETDEWEB)

    Fisher, G.; Wolodko, J.; Alemaskin, K.; Been, J.; Danysh, M. [Alberta Research Council, Edmonton, AB (Canada)

    2008-07-01

    Erosion and corrosion are common wear mechanisms for components used in oil sands processing facilities. This paper described a slurry jet test apparatus designed to evaluate and assess materials for oil sands service conditions. The jet testing apparatus was designed to mimic the wet erosion phenomena typically found in oil sands applications. Wear- and corrosion-resistant materials tested by the apparatus included carbon steel, tungsten carbide metal matrix composite (WC-MMC) overlays, and a range of polymer and rubber liner materials. Polymeric materials included hydrogenated nitrile rubber (HNBR); polyurethane elastomer; and high density polyethylene (HDPE). Material losses were determined by measuring the mass of the samples before and after testing. Normalized rates of abrasion were calculated by dividing total mass lost in the specimens by the total mass of sand impinged on the sample surface. Samples were also visually assessed and analyzed using scanning electron microscopy (SEM) in order to determine failure modes. Tests were conducted for a 2-hour period at an impingement angle of 90 degrees. Results of the study showed that the average abrasion rates of the polymeric samples are lower than rates seen with the carbon steel and overlay materials. Future work on the apparatus will include testing the materials under varying slurry jet parameters. 15 refs., 5 tabs., 10 figs.

  16. Onset of Crack Initiation in Uniaxial and Triaxial Compression Tests of Dolomite Samples

    Directory of Open Access Journals (Sweden)

    Cieślik Jerzy

    2014-03-01

    Full Text Available The paper presents results of laboratory investigation and analysis of crack initiation threshold identification of dolomite samples. First, selected methods for determining crack initiation thresholds are briefly described with special attention paid to four methods: crack volume strain method [14], change in Poisson’s ratio [8], lateral strain response method [16], and dilatancy method [4]. The investigation performed on dolomite samples shows that for the uniaxial and conventional triaxial compression tests, the above mentioned methods give quite similar values, except for the crack volume strain method. Crack initiation threshold determined by this method has a distinctively lower value than that obtained by the other methods. The aim of the present paper was to review and assess these methods for identifying crack initiation threshold based on laboratory tests of dolomite samples.

  17. Screening of soil corrosivity by field testing: Results and design of an electrochemical soil corrosion probe

    DEFF Research Database (Denmark)

    Nielsen, Lars vendelbo; Bruun, Niels Kåre

    1996-01-01

    The corrosivity of different types of soil have been assessed by exposing carbon-steel plates at 50 different locations in Denmark for an extended period of time. The investigations included weight loss measurements and analysis of the chemical compositions of the corrosion products formed...... on the plates during exposure. An electrochemical soil corrosion probe has been designed and manufactured allowing for simultaneous measurements of several qauntities to predict corrosion. The probe consists of individual sections capable of measuring redox-potential, corrosion potential, soil resistivity...

  18. 当量加速腐蚀条件下7 B04-T6高强度铝合金疲劳裂纹扩展规律研究%The fatigue crack growth rule of 7B04-T6 high strength aluminum alloy under equivalently accelerated corrosion environment

    Institute of Scientific and Technical Information of China (English)

    谭晓明; 王海东; 王刚

    2015-01-01

    Based on an accelerated corrosion testing spectrum complicated for the servicing field environment, the equivalently accelerated corrosion testing of high strength aluminum alloy 7B04-T6 specimens for critical structure were carried out. Corrosion damage under the field environment was successfully simulated and reappeared, and corrosion damage evolvement rule was obtained. By prior⁃corrosion fatigue testing and fractography quantitative analysis, the fatigue crack length (a) and fatigue cycles (N) were gotten, and relationship between fatigue crack growth rate (da/dN) and stress intensify factors rang (ΔK) was analyzed. Moreover the effect of different corrosion damage on fatigue crack growth behavior was quantitatively characterized. The result shows that there is obvious short crack growth behavior during early corrosion stage, the fatigue crack growth rate increases when the corrosion damage is more serious, and the fatigue performance is greatly degraded.%基于编制的机场环境加速试验谱,针对关键结构高强度铝合金件进行当量腐蚀试验,在实验室条件下成功地模拟和再现了服役环境条件的腐蚀损伤,借助复型法观测得到了腐蚀损伤的演化规律;通过预腐蚀疲劳试验和疲劳断口扫描电镜定量分析,得到了裂纹长度a与循环次数N数据集,分析了裂纹扩展速率da/dN与应力强度因子幅值ΔK的对应关系,定量表征了不同程度腐蚀损伤对疲劳裂纹扩展行为的影响规律。结果表明,在腐蚀初期,疲劳裂纹扩展过程中有经典的小裂纹扩展阶段;随着腐蚀损伤的加重,小裂纹行为不明显;腐蚀损伤越严重,疲劳裂纹扩展速率越快,结构抗疲劳性能显著退化。

  19. Development of corrosion testing equipment under heat transfer and irradiation conditions to evaluate corrosion resistance of materials used in acid recovery evaporator. Contract research

    Energy Technology Data Exchange (ETDEWEB)

    Motooka, Takafumi; Numata, Masami; Kiuchi, Kiyoshi [Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment

    2002-01-01

    We have been evaluated the safety for corrosion of various metals applied to acid recovery evaporators by the mock-up tests using small scaled equipment and the reference tests in laboratories with small specimens. These tests have been conducted under-radioactive environment. The environment in practical reprocessing plants has many radioactive species. Therefore, the effect of irradiation on corrosion should be evaluated in detail. In this study, we have developed the corrosion testing equipment, which is employed to simulate environments in the acid recovery evaporators. This report describes the specification of corrosion testing equipment and the results of primary, reference and hot tests. Using the equipment, the corrosion test under heat transfer and irradiation conditions have been carried out for 930 hours in safety. It is expectable that useful corrosion test data in radioactive environment are accumulated with this equipment in future, and help the adequate choice of corrosion test condition in laboratories. (author)

  20. Corrosion testing of type 304L stainless steel in tuff groundwater environments

    Energy Technology Data Exchange (ETDEWEB)

    Westerman, R.E.; Pitman, S.G.; Haberman, J.H.

    1987-11-01

    The stress-corrosion cracking (SCC) resistance of Type 304L stainless steel (SS) to elevated temperatures in tuff rock and tuff groundwater environments was determined under irradiated and nonirradiated conditions using U-bend specimens and slow-strain-rate tests. The steel was tested both in the solution-annealed condition and after sensitization heat treatments. The material was found to be susceptible to SCC in both the solution-annealed and solution-annealed-and-sensitized conditions when exposed to an irradiated crushed tuff rock environment containing air and water vapor at 90{sup 0}C. A similar exposure at 50{sup 0}C did not result in failure after a 25-month test duration. Specimens of sensitized 304 SS conditioned with a variety of sensitization heat treatments resisted failure during a test of 1-year duration in which a nonirradiated environment of tuff rock and groundwater held at 200{sup 0}C was allowed to boil to dryness on a cyclical basis. All specimens of sensitized 304 SS exposed to this environment failed. Slow-strain-rate studies were performed on 304L, 304, and 316L SS specimens. The 304L SS was tested in J-13 well water at 150{sup 0}C, and the 316L SS at 95{sup 0}C. Neither material showed evidence of SCC in these tests. Sensitized 304 SS did exhibit SCC in J-13 well water in tests conducted at 150{sup 0}C. 12 refs., 27 figs., 13 tabs.

  1. A universal alternating immersion simulator for accelerated cyclic corrosion tests

    Energy Technology Data Exchange (ETDEWEB)

    Hassel, A.W.; Bonk, S.; Tsuri, S.; Stratmann, M. [Max-Planck-Institut fuer Eisenforschung GmbH, Duesseldorf (Germany)

    2008-02-15

    A new device for performing accelerated cyclic immersion tests is described. The main achievement is to realise a high cycling rate without a proportional increase in the test duration. The device is also capable of performing tests according to EU ISO 11130 specification. A minimal invasive drying system is used that neither heats air nor sample and the flow rate is still low as to prevent a mechanical delamination of paints or loose corrosion products. A multiple sample set-up is realised that provides individual reference electrodes. The random access through a multiplexer allows individual investigation of the samples even by electrochemical impedance spectroscopy under immersion conditions. The device and its test principle are applicable in both industrial and laboratorial scale applications. Two application examples are given to demonstrate the versatility of the alternating immersion tester. One addresses the corrosion protection performance of different zinc-coated steel sheets; the other quantifies the patina formation kinetics of low-alloyed steels with weathering properties. (Abstract Copyright [2008], Wiley Periodicals, Inc.)

  2. Monitoring corrosion in prestressed concrete beams using acoustic emission technique

    Science.gov (United States)

    ElBatanouny, Mohamed K.; Mangual, Jesé; Vélez, William; Ziehl, Paul H.; Matta, Fabio; González, Miguel

    2012-04-01

    Early detection of corrosion can help reduce the cost of maintenance and extend the service life of structures. Acoustic emission (AE) sensing has proven to be a promising method for early detection of corrosion in reinforced concrete members. A test program is presented composed of four medium-scale prestressed concrete T-beams. Three of the beams have a length of 16 ft. 4 in. (4.98 m), and one is 9 ft. 8 in. (2.95 m). In order to corrode the specimens a 3% NaCl solution was prepared, which is representative of sea salt concentration. The beams were subjected to wet-dry cycles to accelerate the corrosion process. Two of the specimens were pre-cracked prior to conditioning in order to examine the effect of crack presence. AE data was recorded continuously while half-cell potential measurements and corrosion rate by Linear Polarization Resistance (LPR) were measured daily. Corrosion current was also being acquired constantly to monitor any change in the concrete resistivity. Results indicate that the onset of corrosion may be identified using AE features, and were corroborated with measurements obtained from electrochemical techniques. Corroded areas were located using source triangulation. The results indicate that cracked specimens showed corrosion activity prior to un-cracked specimens and experienced higher corrosion rates. The level of corrosion was determined using corrosion rate results. Intensity analysis was used to link the corrosion rate and level to AE data.

  3. Hot-crack test for aluminium alloys welds using TIG process

    Directory of Open Access Journals (Sweden)

    Deschaux-beaume F.

    2010-06-01

    Full Text Available Hot cracking is a critical defect frequently observed during welding of aluminium alloys. In order to better understand the interaction between cracking phenomenon, process parameters, mechanical factors and microstructures resulting from solidification after welding, an original hot-cracking test during welding is developed. According to in-situ observations and post mortem analyses, hot cracking mechanisms are investigated, taking into account the interaction between microstructural parameters, depending on the thermal cycles, and mechanical parameters, depending on geometry and clamping conditions of the samples and on the thermal field on the sample. Finally, a process map indicating the limit between cracking and non-cracking zones according to welding parameters is presented.

  4. 氢腐蚀分层对换热器筒体承载能力的影响%Influence of bearing capacity of heat exchanger shell caused by hydrogen corrosion delaminating crack

    Institute of Scientific and Technical Information of China (English)

    何家胜; 李超; 朱晓明; 陈伟; 路远明; 杨峰

    2013-01-01

    To explore the influence of hydrogen corrosion delaminating crack on the mechanical properties and bearing capacity in operation of the layered heat exchanger shell, the material capability of layered heat exchanger shell was analyzed by using chemical constituents analysis, hardness test, tensile tests, Charpy V-notch pendulum impact test. The finite element method was used to calculate the stress distribution of heat exchanger shell and to discuss the stress intensity factors of crack tip. The results show that the Mn element is lower in the chemical constituents, other elements accord with the National Standards; the material hardness meets the requirements, but the toughness declines obviously. The material of heat layered exchanger shell is deteriorated by the hydrogen corrosion, which destroys the continuity and uniformity of the material, decreases the ultimate strength, but increases the yield-strength ratio. The film stress state is destroyed, and material resistance to crack growth decreases. The hydrogen corrosion delaminating crack causes biggish partial stress and makes bearing capacity of the heat exchanger shell decrease.%为了解换热器筒体发生氢腐蚀分层后,其简体局部材料的性能发生的变化及对换热器运行中的承载能力带来的影响,采用化学成分分析、硬度测试、拉伸试验、夏比V口冲击韧性试验等方法对换热器筒体材料的性能进行了分析;运用有限元分析方法计算了简体分层处的应力分布,并探讨了裂纹尖端应力强度因子的变化情况.研究结果表明:材料化学成分中除Mn元素的含量偏低外,其它元素含量符合国家标准;材料的硬度符合要求,材料的强度极限降低,屈强比上升,韧性明显降低.氢腐蚀分层使换热器筒体材料局部劣化,破坏了材料的均匀性和连续性,破坏了简体的薄膜应力状态,产生了较大的局部应力,使换热器筒体承载能力下降.

  5. Electrode holder useful in a corrosion testing device

    Science.gov (United States)

    Murphy, Jr., Robert J.; Jamison, Dale E.

    1986-01-01

    The present invention is directed to an apparatus and method for holding one or more test electrodes of precisely known exposed surface area. The present invention is particularly useful in a device for determining the corrosion properties of the materials from which the test electrodes have been formed. The present invention relates to a device and method for holding the described electrodes wherein the exposed surface area of the electrodes is only infinitesimally decreased. Further, in the present invention the exposed, electrically conductive surface area of the contact devices is small relative to the test electrode surface area. The holder of the present invention conveniently comprises a device for contacting and engaging each test electrode at two point contacts infinitesimally small in relation to the exposed surface area of the electrodes.

  6. Standard test method for measurement of creep crack growth times in metals

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2007-01-01

    1.1 This test method covers the determination of creep crack growth (CCG) in metals at elevated temperatures using pre-cracked specimens subjected to static or quasi-static loading conditions. The time (CCI), t0.2 to an initial crack extension δai = 0.2 mm from the onset of first applied force and creep crack growth rate, ˙a or da/dt is expressed in terms of the magnitude of creep crack growth relating parameters, C* or K. With C* defined as the steady state determination of the crack tip stresses derived in principal from C*(t) and Ct (1-14). The crack growth derived in this manner is identified as a material property which can be used in modeling and life assessment methods (15-25). 1.1.1 The choice of the crack growth correlating parameter C*, C*(t), Ct, or K depends on the material creep properties, geometry and size of the specimen. Two types of material behavior are generally observed during creep crack growth tests; creep-ductile (1-14) and creep-brittle (26-37). In creep ductile materials, where cr...

  7. Subcritical crack growth in oxide and non-oxide ceramics using the Constant Stress Rate Test

    Directory of Open Access Journals (Sweden)

    Agnieszka Wojteczko

    2015-12-01

    Full Text Available Fracture toughness is one of the most important parameters for ceramics description. In some cases, material failure occurs at lower stresses than described by KIc parameter. In these terms, determination of fracture toughness only, proves to be insufficient. This may be due to environmental factors, such as humidity, which might cause subcritical crack propagation in a material. Therefore, it is very important to estimate crack growth velocities to predict lifetime of ceramics used under specific conditions. Constant Stress Rate Test is an indirect method of subcritical crack growth parameters estimation. Calculations are made by using strength data, thus avoiding crack measurement. The expansion of flaws causes reduction of material strength. If subcritical crack growth phenomenon occurs, critical value of crack lengths increases with decreasing stress rate due to longer time for flaw to grow before the critical crack propagation at KIc takes place. Subcritical crack growth phenomenon is particularly dangerous for oxide ceramics due to chemical interactions occurring as a result of exposure to humidity. This paper presents results of Constant Stress Rate Test performed for alumina, zirconia, silicon carbide and silicon nitride in order to demonstrate the differences in subcritical crack propagation phenomenon course.

  8. The effect of buffered solutions in corrosion testing of alloyed 13%Cr martensitic stainless steels for mildly sour applications

    Energy Technology Data Exchange (ETDEWEB)

    Drugli, J.M.; Rogne, T.; Svenning, M.; Axelsen, S. [SINTEF Materials Technology, Trondheim (Norway); Enerhaug, J. [Statoil, Trondheim (Norway)

    1999-11-01

    13% Cr stainless steels may suffer from sulfide stress corrosion cracking in sour environments if hydrogen enters the material. Hydrogen evolution is caused by the cathodic reaction in the corrosion process. As distinct from solutions without buffer, buffered solutions keep the pH stable at the surface almost independent of the electrochemical reactions. The most common initiation process for corrosion of stainless steels is break-down of the passive oxide by subsequent local acidification, which to a certain extent can be prevented in buffered solutions. For local corrosion the risk of corrosion therefore is higher in solutions without buffer than in buffered solutions at the same bulk pH. Hydrogen evolution may also be caused by general corrosion. For this type of corrosion the effect of buffer in the solution may be, contrary to the effect for local corrosion, that general corrosion of 13 Cr (with risk for cracking of loaded specimens) is more readily initiated in buffered solutions than in solutions without buffer at the same pH. With respect to corrosion on ground alloyed 13Cr base material by coupling to carbon steel, it is shown that general corrosion initiates both in strongly and moderately without buffer at pH 3.5, buffered solutions, but not in solution.

  9. Maintainability Improvement Through Corrosion Prediction

    Science.gov (United States)

    1997-12-01

    potential, current, pH, and chloride ion concentration were made along a simulated corrosion fatigue crack for HY80 (UNS K31820) steel in seawater...frequency range of 0.05-50 Hz, a 7075-T6 aluminium alloy and 304 and 316L stainless steels were fatigue tested in 3.0% NaCl solution. The increments...DESCRIPTORS: Conference Paper; Aluminum base alloys- Mechanical properties; Austenitic stainless steels - Mechanical properties; Corrosion fatigue

  10. A rapid stress-corrosion test for aluminum alloys

    Science.gov (United States)

    Helfrich, W. J.

    1968-01-01

    Stressed alloy specimens are immersed in a salt-dichromate solution at 60 degrees C. Because of the minimal general corrosion of these alloys in this solution, stress corrosion failures are detected by low-power microscopic examination.

  11. Effects of Surface State and Applied Stress on Stress Corrosion Cracking of Alloy 690TT in Lead-containing Caustic Solution

    Institute of Scientific and Technical Information of China (English)

    Zhiming Zhang; Jianqiu Wang; En-Hou Han; Wei Ke

    2012-01-01

    The effects of surface state and applied stress on the stress corrosion cracking (SCC) behaviors of thermally treated (TT) Alloy 690 in 10 wt% NaOH solution with 100 mg/L litharge at 330 ℃ were investigated using C-ring samples with four kinds of surface states and two different stress levels. Sample outer surfaces of the first three kinds were ground to 400 grit (ground), shot-peened (SP) and electro-polished (EP) and the last one was used as the as-received state. Two samples of every kind were stressed to 100% and 200% yield stress of Alloy 690TT, respectively. The results showed that the oxide film consisted of three layers whereas continuous layer rich in Cr was not found. The poor adhesive ability indicated that the oxide film could not protect the matrix from further corrosion. Lead was found in the oxide film and the oxides at the crack paths and accelerated the dissolution of thermodynamically unstable Cr in these locations and also in the matrix. The crack initiation and propagation on Alloy 690TT were effectively retarded by SP and EP treatments but were enhanced by grinding treatment, compared with the cracks on the as-received surface. The cracking severity was also enhanced by increasing the externally applied stress. The accelerated dissolution of Cr and the local tensile stress concentration in the near-surface layer caused by cold-working and higher applied stress reduced the SCC-resistance of Alloy 690TT in the studied solution.

  12. Testing and prediction of erosion-corrosion for corrosion resistant alloys used in the oil and gas production industry

    Science.gov (United States)

    Rincon, Hernan E.

    The corrosion behavior of CRAs has been thoroughly investigated and documented in the public literature by many researchers; however, little work has been done to investigate erosion-corrosion of such alloys. When sand particles are entrained in the flow, the degradation mechanism is different from that observed for sand-free corrosive environment. There is a need in the oil and gas industry to define safe service limits for utilization of such materials. The effects of flow conditions, sand rate, pH and temperature on the erosion-corrosion of CRAs were widely studied. An extensive experimental work was conducted using scratch tests and flow loop tests using several experimental techniques. At high erosivity conditions, a synergistic effect between erosion and corrosion was observed. Under the high sand rate conditions tested, erosivity is severe enough to damage the passive layer protecting the CRA thereby enhancing the corrosion rate. In most cases there is likely a competition between the rates of protective film removal due to mechanical erosion and protective film healing. Synergism occurs for each of the three alloys examined (13Cr and Super13Cr and 22Cr); however, the degree of synergism is quite different for the three alloys and may not be significant for 22Cr for field conditions where erosivities are typically much lower that those occurring in the small bore loop used in this research. Predictions of the corrosion component of erosion-corrosion based on scratch test data compared reasonably well to test results from flow loops for the three CRAs at high erosivity conditions. Second order behavior appears to be an appropriate and useful model for representing the repassivation process of CRAs. A framework for a procedure to predict penetration rates for erosion-corrosion conditions was developed based on the second order model behavior observed for the re-healing process of the passive film of CRAs and on computational fluid dynamics (CFD) simulations

  13. Effects of Thermal Aging on Material Properties, Stress Corrosion Cracking, and Fracture Toughness of AISI 316L Weld Metal

    Science.gov (United States)

    Lucas, Timothy; Forsström, Antti; Saukkonen, Tapio; Ballinger, Ronald; Hänninen, Hannu

    2016-08-01

    Thermal aging and consequent embrittlement of materials are ongoing issues in cast stainless steels, as well as duplex, and high-Cr ferritic stainless steels. Spinodal decomposition is largely responsible for the well-known "748 K (475 °C) embrittlement" that results in drastic reductions in ductility and toughness in these materials. This process is also operative in welds of either cast or wrought stainless steels where δ-ferrite is present. While the embrittlement can occur after several hundred hours of aging at 748 K (475 °C), the process is also operative at lower temperatures, at the 561 K (288 °C) operating temperature of a boiling water reactor (BWR), for example, where ductility reductions have been observed after several tens of thousands of hours of exposure. An experimental program was carried out in order to understand how spinodal decomposition may affect changes in material properties in Type 316L BWR piping weld metals. The study included material characterization, nanoindentation hardness, double-loop electrochemical potentiokinetic reactivation (DL-EPR), Charpy-V, tensile, SCC crack growth, and in situ fracture toughness testing as a function of δ-ferrite content, aging time, and temperature. SCC crack growth rates of Type 316L stainless steel weld metal under simulated BWR conditions showed an approximate 2 times increase in crack growth rate over that of the unaged as-welded material. In situ fracture toughness measurements indicate that environmental exposure can result in a reduction of toughness by up to 40 pct over the corresponding at-temperature air-tested values. Material characterization results suggest that spinodal decomposition is responsible for the degradation of material properties measured in air, and that degradation of the in situ properties may be a result of hydrogen absorbed during exposure to the high-temperature water environment.

  14. Characterization of the Corrosion Behavior of Alloy 22 Regarding its Lifetime Performance as a Potential Nuclear Waste Container Material

    Energy Technology Data Exchange (ETDEWEB)

    Rebak, R B; McCright, D

    2002-06-04

    Alloy 22 (UNS N06022) was proposed for the corrosion resistant outer barrier of a two-layer waste package container for nuclear waste at the potential repository site at Yucca Mountain in Nevada (USA). A testing program is underway to characterize and quantify three main modes of corrosion that may occur at the site. Current results show that the containers would perform well under general corrosion, localized corrosion and environmentally assisted cracking (EAC). For example, the general corrosion rate is expected to be below 100 nm/year and the container is predicted to be outside the range of potential for localized corrosion and environmentally assisted cracking.

  15. Effect of Thermomechanical Treatment on the Stress Corrosion Cracking Behavior of Beta III Titanium.

    Science.gov (United States)

    tensile test specimens. Five specimens of each thermomechanical treatment condition were tensile tested in order to obtain yield strengths. The remaining specimens were exposed to an alternate wet/dry environment of 3.5 w/o NaCl solution at ambient temperature under a load of 80% of yield. (Author Modified

  16. Intergranular corrosion testing of austenitic stainless steels in nitric acid solutions

    Energy Technology Data Exchange (ETDEWEB)

    Whillock, G.O.H.; Dunnett, B. F. [British Nuclear Fuels plc, BNFL, B170, Sellafield, Seascale, Cumbria CA20 1PG (United Kingdom)

    2004-07-01

    In hot strong nitric acid solutions, stainless steels exhibit intergranular corrosion. Corrosion rates are often measured from immersion testing of specimens manufactured from the relevant material (e.g. plate or pipe). The corrosion rates, measured from weight loss, are found to increase with time prior to reaching steady state, which can take thousands of hours to achieve. The apparent increase in corrosion rate as a function of time was found to be an artefact due to the surface area of the specimen's being used in the corrosion rate calculations, rather than that of the true area undergoing active corrosion i.e. the grain boundaries. The steady state corrosion rate coincided with the onset of stable grain dropping, where the use of the surface area of the specimen to convert the weight loss measurements to corrosion rates was found to be appropriate. This was confirmed by sectioning of the specimens and measuring the penetration depths. The rate of penetration was found to be independent of time and no induction period was observed. A method was developed to shorten considerably the testing time to reach the steady state corrosion rate by use of a pre-treatment that induces grain dropping. The long-term corrosion rates from specimens which were pre-treated was similar to that achieved after prolonged testing of untreated (i.e. initially ground) specimens. The presence of cut surfaces is generally unavoidable in the simple immersion testing of specimens in test solutions. However, inaccuracy in the results may occur as the measured corrosion rate is often influenced by the orientation of the microstructure, the highest rates typically being observed on the cut surfaces. Two methods are presented which allow deconvolution of the corrosion rates from immersion testing of specimens containing cut surfaces, thus allowing reliable prediction of the long-term corrosion rate of plate surfaces. (authors)

  17. Crack of a first stage blade in a steam turbine

    Directory of Open Access Journals (Sweden)

    M. Nurbanasari

    2014-10-01

    Full Text Available The failure of the first stage blade in a steam turbine of 55 MW was investigated. The blade was made of 17-4 PH stainless steel and has been used for 12 years before failure. The current work aims to find out the main cause of the first stage blade failure. The methods for investigation were metallurgical analysis, chemical composition test, and hardness measurement. The result showed that there was no evidence the blade failure was due to material. The damage found on the blade namely crack on the blade root. Two locations of the crack observed at the blade root, which was at the tang and the fillet, with different failure modes. In general, the damage of the blade was started by the corrosion occurred on the blade root. The crack at the blade root tang was due to corrosion fatigue and the crack occurred at the blade root fillet owing to stress corrosion cracking.

  18. Laboratory and field tests of corrosion inhibitors for an offshore application

    Energy Technology Data Exchange (ETDEWEB)

    Skjerve, Sofie; Fuhr, Geir Gundersen; Haldogaard, Geir

    2006-03-15

    Statoil started a R and D-project in 2002 where the goal was to implement environmental friendly corrosion control at a Statoil operated oil producing field. In this project the following tasks have been addressed: 1) Reduction of the chemical consumption. 2) Documentation of the discharge level of the corrosion inhibitor. 3) Documentation of the environmental impact. 4) Development of new environmentally friendly acceptable corrosion inhibitors. 5) Laboratory and field testing of new corrosion inhibitors. This paper describes laboratory and field tests of corrosion inhibitors for this project. The field tests were carried out on an offshore oil producing installation in the North Sea. Five corrosion inhibitor suppliers with totally eleven products were taking part in this test. All the products were tested in the laboratory. The four most promising products from the laboratory tests were tested in the field during a fourteen days offshore test. Only one of the tested products gave satisfactory results from the corrosion field test. Corrosion measurements were performed both with a Zero Resistance Ammetry (ZRA) probe installed directly into a flow line and with two side streams units. One side stream unit was connected upstream the test separator and the other unit was connected downstream the test separator. (author) (tk)

  19. Non-destructive testing (NDT) of metal cracks using a high Tc rf-SQUID and eddy current method

    Energy Technology Data Exchange (ETDEWEB)

    Lu, D.F.; Fan, C.; Ruan, J.Z. [Midwest Superconductivity Inc., Lawrence, KS (United States)] [and others

    1994-12-31

    A SQUID is the most sensitive device to detect change in magnetic field. A non-destructive testing (NDT) device using high temperature SQUIDs and eddy current method will be much more sensitive than those currently used eddy current systems, yet much cheaper than one with low temperature SQUIDs. In this paper, we present our study of such a NDT device using a high temperature superconducting rf-SQUID as a gradiometer sensor. The result clearly demonstrates the expected sensitivity of the system, and indicates the feasibility of building a portable HTS SQUID NDT device with the help from cryocooler industry. Such a NDT device will have a significant impact on metal corrosion or crack detection technology.

  20. Development and construction of low-cracking high-performance concrete (LC-HPC) bridge decks: Free shrinkage tests, restrained ring tests, construction experience, and crack survey results

    Science.gov (United States)

    Yuan, Jiqiu

    2011-12-01

    The development, construction, and evaluation of low-cracking high-performance concrete (LC-HPC) bridge decks are described based on laboratory test results and experiences gained during the construction of 13 LC-HPC bridge decks in Kansas, along with another deck bid under the LC-HPC specifications but for which the owner did not enforce the specification. This study is divided into four parts covering (1) an evaluation of the free shrinkage properties of LC-HPC candidate mixtures, (2) an investigation of the relationship between the evaporable water content in the cement paste and the free shrinkage of concrete, (3) a study of the restrained shrinkage performance of concrete using restrained ring tests, and (4) a description of the construction and preliminary evaluation of LC-HPC and control bridge decks constructed in Kansas. The first portion of the study involves evaluating the effects of the duration of curing, fly ash, and a shrinkage reducing admixture (SRA) on the free-shrinkage characteristics of concrete mixtures. The results indicate that an increase of curing period reduces free shrinkage. With 7 days of curing, concretes containing fly ash as a partial replacement for cement exhibit higher free shrinkage than concretes with 100% portland cement. When the curing period is increased to 14, 28, and 56 days, the adverse effect of adding fly ash on free shrinkage is minimized and finally reversed. The addition of an SRA significantly reduces free shrinkage for both the 100% portland cement mixture and the mixture containing fly ash. The second portion of the study investigates the relationship between the evaporable water content in the cement paste and the free shrinkage of concrete. A linear relationship between free shrinkage and evaporable water content in the cement paste is observed. For a given mixture, specimens cured for a longer period contain less evaporable water and exhibit lower free shrinkage and less weight loss in the free shrinkage

  1. A probabilistic crack size quantification method using in-situ Lamb wave test and Bayesian updating

    Science.gov (United States)

    Yang, Jinsong; He, Jingjing; Guan, Xuefei; Wang, Dengjiang; Chen, Huipeng; Zhang, Weifang; Liu, Yongming

    2016-10-01

    This paper presents a new crack size quantification method based on in-situ Lamb wave testing and Bayesian method. The proposed method uses coupon test to develop a baseline quantification model between the crack size and damage sensitive features. In-situ Lamb wave testing data on actual structures are used to update the baseline model parameters using Bayesian method to achieve more accurate crack size predictions. To demonstrate the proposed method, Lamb wave testing on simple plates with artificial cracks of different sizes is performed using surface-bonded piezoelectric wafers, and the data are used to obtain the baseline model. Two damage sensitive features, namely, the phase change and normalized amplitude are identified using signal processing techniques and used in the model. To validate the effectiveness of the method, the damage data from an in-situ fatigue testing on a realistic lap-joint component are used to update the baseline model using Bayesian method.

  2. Crack growth of throughwall flaw in Alloy 600 tube during leak testing

    Energy Technology Data Exchange (ETDEWEB)

    Bahn, Chi Bum, E-mail: bahn@pusan.ac.kr [Pusan National University, 2 Busandaehak-ro 63beon-gil, Geumjeong-gu, Busan 609-735 (Korea, Republic of); Majumdar, Saurin [Argonne National Laboratory, Lemont, IL 60439 (United States)

    2015-04-01

    Graphical abstract: - Highlights: • A series of leak testing was conducted at a constant pressure and room temperature. • The time-dependent increase in the leak rate was observed. • The fractography revealed slip offsets and crystallographic facets. • Time-dependent plasticity at the crack tip caused the slip offsets. • Fatigue by jet/structure interaction caused the crystallographic facets. - Abstract: We examined the issue of whether crack growth in a full thickness material can occur in a leaking crack. A series of leak tests was conducted at a room temperature and constant pressure (17.3 MPa) with Alloy 600 tube specimens containing a tight rectangular throughwall axial fatigue crack. To exclude a potential pulsation effect by a high pressure pump, the test water was pressurized by using high pressure nitrogen gas. Fractography showed that crack growth in the full thickness material can occur in the leaking crack by two mechanisms: time-dependent plasticity at the crack tip and fatigue induced by jet/structure interaction. The threshold leak rate at which the jet/structure interaction was triggered was between 1.3 and 3.3 L/min for the specific heat of the Alloy 600 tube tested.

  3. Online stress corrosion crack and fatigue usages factor monitoring and prognostics in light water reactor components: Probabilistic modeling, system identification and data fusion based big data analytics approach

    Energy Technology Data Exchange (ETDEWEB)

    Mohanty, Subhasish M. [Argonne National Lab. (ANL), Argonne, IL (United States); Jagielo, Bryan J. [Argonne National Lab. (ANL), Argonne, IL (United States); Oakland Univ., Rochester, MI (United States); Iverson, William I. [Argonne National Lab. (ANL), Argonne, IL (United States); Univ. of Illinois at Urbana-Champaign, Champaign, IL (United States); Bhan, Chi Bum [Argonne National Lab. (ANL), Argonne, IL (United States); Pusan National Univ., Busan (Korea, Republic of); Soppet, William S. [Argonne National Lab. (ANL), Argonne, IL (United States); Majumdar, Saurin M. [Argonne National Lab. (ANL), Argonne, IL (United States); Natesan, Ken N. [Argonne National Lab. (ANL), Argonne, IL (United States)

    2014-12-10

    Nuclear reactors in the United States account for roughly 20% of the nation's total electric energy generation, and maintaining their safety in regards to key component structural integrity is critical not only for long term use of such plants but also for the safety of personnel and the public living around the plant. Early detection of damage signature such as of stress corrosion cracking, thermal-mechanical loading related material degradation in safety-critical components is a necessary requirement for long-term and safe operation of nuclear power plant systems.

  4. Ductile tearing of crack-like defects during hydrostatic testing of pipes

    Energy Technology Data Exchange (ETDEWEB)

    Hippert, E.; Donato, G.V.P.; Teixeira, J.C.G.; Lima de, R.S. [Petrobras, Rio de Janeiro (Brazil)

    2004-07-01

    Although hydrostatic testing is widely used to monitor pipeline integrity, experimental studies have shown that flaw growth can occur during hydrostatic testing procedures. This study investigated the effect of pipeline hydrostatic testing on ductile crack growth of prior crack-like defects. Six segments of 3 m length API X60 steel pipes were tested. Each segment contained an electro-sparking erosion part-wall defects positioned both externally and internally on the base metal. Crack extension for external part-wall defects was monitored using an ultrasonic technique. Pipe resistance curves of applied load versus crack depth were obtained for each crack configuration. Laboratory curves were obtained from fracture mechanics tests pieces and then used to determine the initiation of stable extension of the applied load defects. It was observed that the level of crack tip constraint and triaxiality were similar to those experienced in real structures. It was suggested that single edge notch tensile (SET) specimens may be the most suitable specimens for predicting pipeline toughness behavior. A suitable parameter for estimating hydrostatic testing pressure was derived from values obtained during Charpy V-notch impact testing. It was concluded that future research will focus on the development of SET specimens and testing methods. 12 refs., 4 tabs., 11 figs.

  5. Microstructure and stress corrosion cracking of the fusion boundary region in an alloy 182-A533B low alloy steel dissimilar weld joint

    Energy Technology Data Exchange (ETDEWEB)

    Hou, Juan [Fracture and Reliability Research Institute, Tohoku University, 6-6-01, Aramaki Aoba, Aoba-ku, Sendai City 980-8579 (Japan); State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, 62 Wencui Road, Shenyang 110016 (China); Peng, Qunjia, E-mail: qpeng@rift.mech.tohoku.ac.j [Fracture and Reliability Research Institute, Tohoku University, 6-6-01, Aramaki Aoba, Aoba-ku, Sendai City 980-8579 (Japan); Takeda, Yoichi; Kuniya, Jiro; Shoji, Tetsuo [Fracture and Reliability Research Institute, Tohoku University, 6-6-01, Aramaki Aoba, Aoba-ku, Sendai City 980-8579 (Japan)

    2010-12-15

    Research highlights: {yields} High-angle misorientation at FB, type-II and type-I boundaries. {yields} Highest residual strain and hardness in the zone between FB and type-II boundary. {yields} Type-II and type-I boundaries had lower resistance to SCC growth than the FB. {yields} Crack growth blunted by pitting at the FB. {yields} Reactivation of crack growth from the pitting by oxidation along the grain boundary. - Abstract: Stress corrosion cracking (SCC) in the fusion boundary (FB) region of an Alloy 182-A533B low alloy steel (LAS) dissimilar weld joint in high temperature water doped with sulfate was studied following a microstructure characterization of the FB region. The microstructure characterization suggested the type-II and type-I boundaries in the dilution zone (DZ) adjacent to the FB had lower resistance to SCC growth than the FB. Crack propagating perpendicular to the FB in the DZ was observed to be blunted by pitting at the FB, followed by the reactivation from the pitting by localized oxidation along the grain boundary in LAS.

  6. Evaluation of shrinkage and cracking in concrete of ring test by acoustic emission method

    Science.gov (United States)

    Watanabe, Takeshi; Hashimoto, Chikanori

    2015-03-01

    Drying shrinkage of concrete is one of the typical problems related to reduce durability and defilation of concrete structures. Lime stone, expansive additive and low-heat Portland cement are used to reduce drying shrinkage in Japan. Drying shrinkage is commonly evaluated by methods of measurement for length change of mortar and concrete. In these methods, there is detected strain due to drying shrinkage of free body, although visible cracking does not occur. In this study, the ring test was employed to detect strain and age cracking of concrete. The acoustic emission (AE) method was adopted to detect micro cracking due to shrinkage. It was recognized that in concrete using lime stone, expansive additive and low-heat Portland cement are effective to decrease drying shrinkage and visible cracking. Micro cracking due to shrinkage of this concrete was detected and evaluated by the AE method.

  7. Measuring naphthenic acid corrosion potential with the Fe powder test

    Directory of Open Access Journals (Sweden)

    Hau, J. L.

    2003-12-01

    Full Text Available Results are presented of experiments performed using a new method to measure the naphthenic acid corrosion potential. The method consists of adding pure iron powder into a small autoclave containing the crude or oil sample. The test is then performed at a given temperature for one hour, after which the oil sample is filtered and the remaining liquid is sent for iron content determination (ppm. The tests are run at 7 different temperature levels, 3 more are run as repeated tests. A best-fitted curve is drawn through these 10 experimental points and the maximum point is thus determined. This becomes the main outcome of the test and it is used to give a measure of the naphthenic acid corrosion potential. The same general trends as observed in the past using the neutralization number or TAN (Total Acid Number is obtained. However, this new test seems capable oí detecting anomalous cases where oil samples having larger values of TAN exhibit less corrosivity than others having much lower values of TAN or where they show completely different corrosivity despite having similar or the same TAN.

    Se presentan los resultados de experimentos realizados con un nuevo método para medir el potencial de corrosión por ácidos nafténicos. El método consiste en añadir hierro puro en polvo a una muestra de crudo o aceite, en un autoclave pequeño. El ensayo se realiza a una temperatura dada durante una hora; luego se filtra la muestra de aceite y el líquido filtrado se envía para medir la concentración de hierro disuelto (ppm. El ensayo se reitera para siete temperaturas diferentes y se repiten tres más para determinar su reproducibilidad. Con estos 10 puntos experimentales se dibuja la mejor curva de ajuste y se determina un máximo de hierro disuelto. Este máximo se convierte en el resultado principal del ensayo y se usa para dar una medida del potencial de corrosión por ácidos nafténicos. Se obtienen las mismas tendencias generales observadas

  8. 'GRC1.5': Uptower Gearbox Testing to Investigate Bearing Axial Cracking

    Energy Technology Data Exchange (ETDEWEB)

    Keller, Jonathan; Vaes, David; McNiff, Brian

    2016-02-16

    This presentation focuses on the investigation of bearing axial cracking using the GRC1.5 uptower gearbox. Topics covered include the testing options considered, the project goal, and current and near-term activities.

  9. Standard test method for determination of resistance to stable crack extension under low-constraint conditions

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2006-01-01

    1.1 This standard covers the determination of the resistance to stable crack extension in metallic materials in terms of the critical crack-tip-opening angle (CTOAc), ψc and/or the crack-opening displacement (COD), δ5 resistance curve (1). This method applies specifically to fatigue pre-cracked specimens that exhibit low constraint (crack-length-to-thickness and un-cracked ligament-to-thickness ratios greater than or equal to 4) and that are tested under slowly increasing remote applied displacement. The recommended specimens are the compact-tension, C(T), and middle-crack-tension, M(T), specimens. The fracture resistance determined in accordance with this standard is measured as ψc (critical CTOA value) and/or δ5 (critical COD resistance curve) as a function of crack extension. Both fracture resistance parameters are characterized using either a single-specimen or multiple-specimen procedures. These fracture quantities are determined under the opening mode (Mode I) of loading. Influences of environment a...

  10. Field test corrosion experiences when co-firing straw and coal: 10 year status within Elsam

    DEFF Research Database (Denmark)

    Frandsen, Rasmus Berg; Montgomery, Melanie; Larsen, Ole Hede

    2007-01-01

    to 575 degrees C and for the flue gas from 1025 to 1300 degrees C. All these test tubes have been removed during the last three years at one year intervals for corrosion studies. The corrosion studies performed on all investigated tubes included measurements of the corrosion attack, light optical...... sulphate on superheater tubes resulting in increased corrosion rates. From field experimental results this paper show, that by co-firing straw with coal, corrosion rates can be brought down to an acceptable level. This paper firstly deals with the results from a demonstration program co-firing coal...... and straw at the 150 MW pulverized coal fired boiler Studstrup unit 1. Two exposure series lasting 3000 hours each were performed for co-firing 10 and 20% of straw (% energy basis) with coal. Using built in test tubes in the hot end of the actual superheaters and air/water cooled corrosion probes...

  11. Fatigue of Self-Healing Nanofiber-based Composites: Static Test and Subcritical Crack Propagation.

    Science.gov (United States)

    Lee, Min Wook; Sett, Soumyadip; Yoon, Sam S; Yarin, Alexander L

    2016-07-20

    Here, we studied the self-healing of composite materials filled with epoxy-containing nanofibers. An initial incision in the middle of a composite sample stretched in a static fatigue test can result in either crack propagation or healing. In this study, crack evolution was observed in real time. A binary epoxy, which acted as a self-healing agent, was encapsulated in two separate types of interwoven nano/microfibers formed by dual-solution blowing, with the core containing either epoxy or hardener and the shell being formed from poly(vinylidene fluoride)/ poly(ethylene oxide) mixture. The core-shell fibers were encased in a poly(dimethylsiloxane) matrix. When the fibers were damaged by a growing crack in this fiber-reinforced composite material because of static stretching in the fatigue test, they broke and released the healing agent into the crack area. The epoxy used in this study was cured and solidified for approximately an hour at room temperature, which then conglutinated and healed the damaged location. The observations were made for at least several hours and in some cases up to several days. It was revealed that the presence of the healing agent (the epoxy) in the fibers successfully prevented the propagation of cracks in stretched samples subjected to the fatigue test. A theoretical analysis of subcritical cracks was performed, and it revealed a jumplike growth of subcritical cracks, which was in qualitative agreement with the experimental results.

  12. LABORATORY TESTING TO SIMULATE VAPOR SPACE CORROSION IN RADIOACTIVE WASTE STORAGE TANKS

    Energy Technology Data Exchange (ETDEWEB)

    Wiersma, B.; Garcia-Diaz, B.; Gray, J.

    2013-08-30

    Radioactive liquid waste has been stored in underground carbon steel tanks for nearly 70 years at the Hanford nuclear facility. Vapor space corrosion of the tank walls has emerged as an ongoing challenge to overcome in maintaining the structural integrity of these tanks. The interaction between corrosive and inhibitor species in condensates/supernates on the tank wall above the liquid level, and their interaction with vapor phase constituents as the liquid evaporates from the tank wall influences the formation of corrosion products and the corrosion of the carbon steel. An effort is underway to gain an understanding of the mechanism of vapor space corrosion. Localized corrosion, in the form of pitting, is of particular interest in the vapor space. CPP testing was utilized to determine the susceptibility of the steel in a simulated vapor space environment. The tests also investigated the impact of ammonia gas in the vapor space area on the corrosion of the steel. Vapor space coupon tests were also performed to investigate the evolution of the corrosion products during longer term exposures. These tests were also conducted at vapor space ammonia levels of 50 and 550 ppm NH{sub 3} (0.005, and 0.055 vol.%) in air. Ammonia was shown to mitigate vapor space corrosion.

  13. Fatigue Crack Growth Threshold Testing of Metallic Rotorcraft Materials

    Science.gov (United States)

    Newman, John A.; James, Mark A.; Johnson, William M.; Le, Dy D.

    2008-01-01

    Results are presented for a program to determine the near-threshold fatigue crack growth behavior appropriate for metallic rotorcraft alloys. Four alloys, all commonly used in the manufacture of rotorcraft, were selected for study: Aluminum alloy 7050, 4340 steel, AZ91E Magnesium, and Titanium alloy Ti-6Al-4V (beta-STOA). The Federal Aviation Administration (FAA) sponsored this research to advance efforts to incorporate damage tolerance design and analysis as requirements for rotorcraft certification. Rotorcraft components are subjected to high cycle fatigue and are typically subjected to higher stresses and more stress cycles per flight hour than fixed-wing aircraft components. Fatigue lives of rotorcraft components are generally spent initiating small fatigue cracks that propagate slowly under near-threshold cracktip loading conditions. For these components, the fatigue life is very sensitive to the near-threshold characteristics of the material.

  14. Differential potential noise measurement during crack initiation

    Energy Technology Data Exchange (ETDEWEB)

    Hettiarachchi, S. [GE-Hitachi Nuclear Energy, Vallecitos Nuclear Center, Sunol, California (United States)]. E-mail: samson.hettiarachchi@gene.ge.com

    2007-07-01

    Electrochemical potential and current noise have been used over the past two decades as methods of detecting general corrosion, pitting corrosion, crevice corrosion, stress corrosion, corrosion in concrete and corrosion under coatings. The methods involved the use of self-generated potential noise/current noise or both, of the material of choice in a given environment. In a variety of these studies, data processing involved techniques such as fast fourier transforms (FFT) to generate the power spectrum that provided the unique signature associated with the type of the corrosion process. This paper deals with a more simplistic method of monitoring differential potential noise measured between two identical slow strain rate test (SSRT) specimens placed close to each other, in a high temperature aqueous environment, while one is being subjected to dynamic strain and the other maintained under static conditions. The differential potential noise (DPN) was monitored as the applied load increased on the slow strain rate test specimen. Unlike self-generated noise, differential potential noise is less affected by electrical noise in the surroundings, and is able to signal the point of oxide film cracking or crack initiation more conveniently without extensive data processing. This method also allows the in-situ detection of crack initiation without interruption of the SSRT test. The DPN signal at the crack initiation stage is different from the signals acquired as cracking progressed due to continuing dynamic strain. Furthermore, the nature of the DPN signal response depends on the type of material used in this study, Type 304 stainless steel or Inconel 182. (author)

  15. Letter report on PCT/Monolith glass ceramic corrosion tests

    Energy Technology Data Exchange (ETDEWEB)

    Crawford, Charles L. [Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL)

    2015-09-24

    The Savannah River National Laboratory (SRNL) is collaborating with personnel from Pacific Northwest National Laboratory (PNNL) to study advanced waste form glass ceramics for immobilization of waste from Used Nuclear Fuel (UNF) separations processes. The glass ceramic waste forms take advantage of both crystalline and glassy phases where ‘troublesome’ elements (e.g., low solubility in glass or very long-lived) partition to highly durable ceramic phases with the remainder of elements residing in the glassy phase. The ceramic phases are tailored to create certain minerals or unique crystalline structures that can host the radionuclides by binding them in their specific crystalline network while not adversely impacting the residual glass network (Crum et al., 2011). Glass ceramics have been demonstrated using a scaled melter test performed in a pilot scale (1/4 scale) cold crucible induction melter (CCIM) (Crum et al., 2014; Maio et al., 2015). This report summarizes recent results from both Phase I and Phase II bench scale tests involving crucible fabrication and corrosion testing of glass ceramics using the Product Consistency Test (PCT). Preliminary results from both Phase I and Phase II bench scale tests involving statistically designed matrices have previously been reported (Crawford, 2013; Crawford, 2014).

  16. Metallurgical and mechanical parameters controlling alloy 718 stress corrosion cracking resistance in PWR primary water; Facteurs metallurgiques et mecaniques controlant l'amorcage de defauts de corrosion sous contrainte dans l'alliage 718 en milieu primaire des reacteurs a eau sous pression

    Energy Technology Data Exchange (ETDEWEB)

    Deleume, J

    2007-11-15

    Improving the performance and reliability of the fuel assemblies of the pressurized water reactors requires having a perfect knowledge of the operating margins of both the components and the materials. The choice of alloy 718 as reference material for this study is justified by the industrial will to identify the first order parameters controlling the excellent resistance of this alloy to Stress Corrosion Cracking (SCC). For this purpose, a specific slow strain rate (SSR) crack initiation test using tensile specimen with a V-shaped hump in the middle of the gauge length was developed and modeled. The selectivity of such SSR tests in simulated PWR primary water at 350 C was clearly established by characterizing the SCC resistance of nine alloy 718 thin strip heats. Regardless of their origin and in spite of a similar thermo-mechanical history, they did not exhibit the same susceptibility to SCC crack initiation. All the characterized alloy 718 heats develop oxide scale of similar nature for various exposure times to PWR primary medium in the temperature range [320 C - 360 C]. {delta} phase precipitation has no impact on alloy 718 SCC initiation behavior when exposed to PWR primary water, contrary to interstitial contents and the triggering of plastic instabilities (PLC phenomenon). (author)

  17. Characterization of cracking in Strain-Hardening Cementitious Composites using the compact tension test

    DEFF Research Database (Denmark)

    Pereira, Eduardo B.; Fischer, Gregor; Barros, Joaquim A. O.

    The characterization of the tensile behavior of strain hardening cementitious composites (SHCC) is of significant importance to the material design. In a previous work the tensile stress-crack opening response of different types of SHCC was characterized using notched specimens tested in direct...... plate specimens and the eccentrically applied tensile load create the local conditions necessary to the initiation of a single crack at the tip of the notch. Further propagation and opening of the crack in Mode I allow the assessment of the tensile load-displacement relationship. The experimental...

  18. Non-Destructive Testing of Corrosion Under Coatings

    Science.gov (United States)

    2004-09-01

    studies indicate that field produced corrosion should be detectable up to at least 8 mils of Mil-PRF- 23377, epoxy primer and Mil- PFR -85582 TYI...longer in service and was decommissioned due to corrosion around fasteners and other locations on the wing. Early detection could have saved this

  19. Fatigue and Corrosion in Metals

    CERN Document Server

    Milella, Pietro Paolo

    2013-01-01

    This textbook, suitable for students, researchers and engineers, gathers the experience of more than 20 years of teaching fracture mechanics, fatigue and corrosion to professional engineers and running experimental tests and verifications to solve practical problems in engineering applications. As such, it is a comprehensive blend of fundamental knowledge and technical tools to address the issues of fatigue and corrosion. The book initiates with a systematic description of fatigue from a phenomenological point of view, since the early signs of submicroscopic damage in few surface grains and continues describing, step by step, how these precursors develop to become mechanically small cracks and, eventually, macrocracks whose growth is governed by fracture mechanics. But fracture mechanics is also introduced to analyze stress corrosion and corrosion assisted fatigue in a rather advanced fashion. The author dedicates a particular attention to corrosion starting with an electrochemical treatment that mechanical e...

  20. Adhesion mechanisms of bituminous crack sealant to aggregate and laboratory test development

    Science.gov (United States)

    Hajialiakbari Fini, Elham

    Crack sealing is a common pavement maintenance treatment because it extends pavement service life. However, crack sealant often fails prematurely due to a loss of adhesion. Since current test methods are mostly empirical and only provide a qualitative measure of bond strength, they cannot predict sealant adhesive failure accurately. Hence, there is an urgent need for test methods based on bituminous sealant rheology that can better predict sealant field performance. This study introduces three laboratory tests aimed to assess the bond property of hot-poured crack sealant to pavement crack walls. The three tests are designed to serve the respective needs of producers, engineers, and researchers. The first test implements the principle of surface energy to measure the thermodynamic work of adhesion, which is the energy spent in separating the two materials at the interface. The work of adhesion is reported as a measure of material compatibility at an interface. The second test is a direct adhesion test, a mechanical test which is designed to closely resemble both the installation process and the crack expansion due to thermal loading. This test uses the Direct Tension Test (DTT) device. The principle of the test is to apply a tensile force to detach the sealant from its aggregate counterpart. The maximum load, Pmax, and the energy to separation, E, are calculated and reported to indicate interface bonding. The third test implements the principles of fracture mechanics in a pressurized circular blister test. The apparatus is specifically designed to conduct the test for bituminous crack sealant, asphalt binder, or other bitumen-based materials. In this test, a fluid is injected at a constant rate at the interface between the substrate (aggregate or a standard material) and the adhesive (crack sealant) to create a blister. The fluid pressure and blister height are measured as functions of time; the data is used to calculate Interfacial Fracture Energy (IFE), which is a

  1. DEPOSITION TANK CORROSION TESTING FOR ENHANCED CHEMICAL CLEANING POST OXALIC ACID DESTRUCTION

    Energy Technology Data Exchange (ETDEWEB)

    Mickalonis, J.

    2011-08-29

    An Enhanced Chemical Cleaning (ECC) process is being developed to aid in the high level waste tank closure at the Savannah River Site. The ECC process uses an advanced oxidation process (AOP) to destroy the oxalic acid that is used to remove residual sludge from a waste tank prior to closure. The AOP process treats the dissolved sludge with ozone to decompose the oxalic acid through reactions with hydroxyl radicals. The effluent from this oxalic acid decomposition is to be sent to a Type III waste tank and may be corrosive to these tanks. As part of the hazardous simulant testing that was conducted at the ECC vendor location, corrosion testing was conducted to determine the general corrosion rate for the deposition tank and to assess the susceptibility to localized corrosion, especially pitting. Both of these factors impact the calculation of hydrogen gas generation and the structural integrity of the tanks, which are considered safety class functions. The testing consisted of immersion and electrochemical testing of A537 carbon steel, the material of construction of Type III tanks, and 304L stainless steel, the material of construction for transfer piping. Tests were conducted in solutions removed from the destruction loop of the prototype ECC set up. Hazardous simulants, which were manufactured at SRNL, were used as representative sludges for F-area and H-area waste tanks. Oxalic acid concentrations of 1 and 2.5% were used to dissolve the sludge as a feed to the ECC process. Test solutions included the uninhibited effluent, as well as the effluent treated for corrosion control. The corrosion control options included mixing with an inhibited supernate and the addition of hydroxide. Evaporation of the uninhibited effluent was also tested since it may have a positive impact on reducing corrosion. All corrosion testing was conducted at 50 C. The uninhibited effluent was found to increase the corrosion rate by an order of magnitude from less than 1 mil per year (mpy

  2. Review on Stress Corrosion and Corrosion Fatigue Failure of Centrifugal Compressor Impeller

    Institute of Scientific and Technical Information of China (English)

    SUN Jiao; CHEN Songying; QU Yanpeng; LI Jianfeng

    2015-01-01

    Corrosion failure, especially stress corrosion cracking and corrosion fatigue, is the main cause of centrifugal compressor impeller failure. And it is concealed and destructive. This paper summarizes the main theories of stress corrosion cracking and corrosion fatigue and its latest developments, and it also points out that existing stress corrosion cracking theories can be reduced to the anodic dissolution (AD), the hydrogen-induced cracking (HIC), and the combined AD and HIC mechanisms. The corrosion behavior and the mechanism of corrosion fatigue in the crack propagation stage are similar to stress corrosion cracking. The effects of stress ratio, loading frequency, and corrosive medium on the corrosion fatigue crack propagation rate are analyzed and summarized. The corrosion behavior and the mechanism of stress corrosion cracking and corrosion fatigue in corrosive environments, which contain sulfide, chlorides, and carbonate, are analyzed. The working environments of the centrifugal compressor impeller show the behavior and the mechanism of stress corrosion cracking and corrosion fatigue in different corrosive environments. The current research methods for centrifugal compressor impeller corrosion failure are analyzed. Physical analysis, numerical simulation, and the fluid-structure interaction method play an increasingly important role in the research on impeller deformation and stress distribution caused by the joint action of aerodynamic load and centrifugal load.

  3. Preliminary stress corrosion cracking modeling study of a dissimilar material weld of alloy (INCONEL) 182 with Stainless Steel 316

    Energy Technology Data Exchange (ETDEWEB)

    Aly, Omar F.; Mattar Neto, Miguel, E-mail: ofaly@ipen.br, E-mail: mmattar@ipen.br [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil); Schvartzman, Monica M.A.M., E-mail: monicas@cdtn.br [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2013-07-01

    Dissimilar welds (DW) are normally used in many components junctions in structural project of PWR (Pressurized Water Reactors) in Nuclear Plants. One had been departed of a DW of a nozzle located at a Reactor Pressure Vessel (RPV) of a PWR reactor, that joins the structural vessel material with an A316 stainless steel safe end. This weld is basically done with Alloy 182 with a weld buttering of Alloy 82. It had been prepared some axial cylindrical specimens retired from the Alloy 182/A316 weld end to be tested in the slow strain rate test machine located at CDTN laboratory. Based in these stress corrosion susceptibility results, it was done a preliminary semi-empirical modeling application to study the failure initiation time evolution of these specimens. The used model is composed by a deterministic part, and a probabilistic part according to the Weibull distribution. It had been constructed a specific Microsoft Excel worksheet to do the model application of input data. The obtained results had been discussed according with literature and also the model application limits. (author)

  4. FEM analysis on the crack process of concrete cover induced by non-uniform corrosion of re-bar%钢筋不均匀锈蚀引起的混凝土保护层开裂有限元分析

    Institute of Scientific and Technical Information of China (English)

    韦俊; 孟浩; 薛圣广

    2011-01-01

    钢筋发生锈蚀,将导致混凝土保护层受拉而开裂,严重影响混凝土结构的耐久性.针对自然环境下混凝土构件中的钢筋往往是非均匀锈蚀,利用ABAQUS有限元软件,采用对钢筋周围混凝土施加不均匀锈胀位移的方法模拟钢筋非均匀锈蚀情况下保护层的开裂过程,基于有限元分析结果,得到保护层胀裂破坏时临界径向位移计算公式;以此为基础,推导了钢筋非均匀锈蚀时保护层开裂时钢筋锈蚀率的计算公式.最后,通过试验验证了本文提出的锈蚀率计算公式的合理性.%Occurrence of re-bar corrosion will lead to the concrete cover cracking, which seriously affect the durability of concrete structures. In dealing with the non-uniform corrosion of re-bar in concrete components under natural environment, the paper simulates the cracking process of concrete cover using a finite-element based method with ABAQUS software. Based on the FEM analysis results, the formula of the critical radial displacement at the cracking time is used to predict the corrosion ratio at the cracking time of cover concrete. Finally, the analytical corrosion ratio formula presented herein is verified with the laboratory test.

  5. Stress corrosion cracking in the fusion boundary region of an alloy 182 - A533B low alloy steel dissimilar weld joint in high temperature oxygenated water

    Energy Technology Data Exchange (ETDEWEB)

    Peng, Q.; Xue, H.; Hou, J.; Takeda, Y.; Kuniya, J.; Shoji, T. [Fracture and Reliability Research Institute, Tohoku University (Japan)

    2011-07-01

    In this work, following a microstructural characterization of the fusion boundary (FB) region in an Alloy 182 - A533B LAS dissimilar weld joint, the SCC growth behaviour in the FB region of the dissimilar weld joint in 288 C degrees water was investigated by employing crevice bent beam (CBB) and crack growth rate (CGR) testing, in conjunction with a simulation by finite element method (FEM). The microstructure characterization showed that there is a narrow high hardness zone (HHZ) in the dilution zone (DZ) of the weld metal adjacent to the FB. Further, a sharp increase of the hardness was observed immediately adjacent to the FB, suggesting the existence of a hardness gradient in the HHZ. FEM simulation of the growth of a crack perpendicular to the FB in the DZ showed that there is a drop in crack tip strain rate as the crack entered the HHZ, suggesting a decreased crack growth rate can be expected for a crack propagating perpendicular to the FB in the high hardness zone where a continuous increase of the hardness with crack growth may exist. Cracking path observation on the cross-section of the CBB specimen suggested that a SCC propagating perpendicular to the FB in the DZ was blunted by pitting after it reached the FB, indicating that the FB is a barrier to SCC growth. However, reactivation of crack growth from the pitting in LAS by preferential oxidation along the grain boundary was observed as well, suggesting a combined effect of microstructure and the high sulphate concentration in the water used for the test. The effects of sulphate doping and DO on CGR in the DZ and FB region were further clarified by the results of the SCC-CGR test. At a DO of 0.25 ppm, the SCC growth rate was low in the FB region even with a sulphate addition of up to 50 ppb in water. The crack growth, however, was reactivated by increasing the DO to 2 ppm at both sulphate concentrations of 50 ppb and 20 ppb, indicating an important role of DO in SCC growth in the DZ. The existence of a

  6. The role of Hydrogen and Creep in Intergranular Stress Corrosion Cracking of Alloy 600 and Alloy 690 in PWR Primary Water Environments ? a Review

    Energy Technology Data Exchange (ETDEWEB)

    Rebak, R B; Hua, F H

    2004-07-12

    Intergranular attack (IGA) and intergranular stress corrosion cracking (IGSCC) of Alloy 600 in PWR steam generator environment has been extensively studied for over 30 years without rendering a clear understanding of the essential mechanisms. The lack of understanding of the IGSCC mechanism is due to a complex interaction of numerous variables such as microstructure, thermomechanical processing, strain rate, water chemistry and electrochemical potential. Hydrogen plays an important role in all these variables. The complexity, however, significantly hinders a clearer and more fundamental understanding of the mechanism of hydrogen in enhancing intergranular cracking via whatever mechanism. In this work, an attempt is made to review the role of hydrogen based on the current understanding of grain boundary structure and chemistry and intergranular fracture of nickel alloys, effect of hydrogen on electrochemical behavior of Alloy 600 and Alloy 690 (e.g. the passive film stability, polarization behavior and open-circuit potential) and effect of hydrogen on PWSCC behavior of Alloy 600 and Alloy 690. Mechanistic studies on the PWSCC are briefly reviewed. It is concluded that further studies on the role of hydrogen on intergranular cracking in both inert and primary side environments are needed. These studies should focus on the correlation of the results obtained at different laboratories by different methods on materials with different metallurgical and chemical parameters.

  7. Stress corrosion cracking in the vessel closure head penetrations of French PWR`s; Fissuration par corrosion sous contrainte de penetrations de couvercle de cuve de reacteur nucleaire francais a eau pressurisee

    Energy Technology Data Exchange (ETDEWEB)

    Buisine, D.; Cattant, F.; Champredonde, J.; Pichon, C.; Benhamou, C.; Gelpi, A.; Vaindirlis, M.

    1994-01-01

    During a hydrotest in September 1991, part of the statutory decennial in-service inspection, a leak was detected on the vessel head of Bugey 3, which is one of the first 900 MW 3-loop PWR`s in France. This leak was due to a cracked penetration used for a control rod drive mechanism. The investigations performed identified Primary Stress Corrosion Cracking of Alloy 600 as being the origin of this degradation. So a lot of the same design PWR`s are a concern due to this generic problem. In this case, PWSCC was linked to: - hot temperature of the vessel head; - high residual stresses due to the welding process between peripherical penetrations and the vessel head; - sensitivity of forged Alloy 600 used for penetration manufacturing. This following paper will present the cracked analysis based, in particular, on the main results obtained in France on each of these items. These results come from the operating experience, the destructive examinations and the programs which are running on stress analysis and metallurgical characterizations. (authors). 9 figs., 2 tabs.

  8. Rapid screening of stainless steels for environmentally assisted cracking in H{sub 2}S/CO{sub 2}/Cl{sup {minus}} environments using the slow strain rate test

    Energy Technology Data Exchange (ETDEWEB)

    Joia, C.J.B.M. [PETROBRAS, Rio de Janeiro (Brazil). Centre de Pesquisas; Small, A.L.L.T.; Ponciano, J.A.C. [Univ. Federal do Rio de Janeiro (Brazil); Kane, R.D. [CLI International, Inc., Houston, TX (United States)

    1997-08-01

    Stress corrosion cracking (SCC) and hydrogen embrittlement (HE) susceptibility of three different steels were determined using the methodology of the slow strain rate (SSR) testing as currently discussed within ASTM G129 and more specifically in the proposed NACE T-1F-9e test method. The materials included 13% Cr and 13%Cr-5% Ni-2% Mo martensitic stainless steels and 22%CR-5%Ni-3%Mo (22Cr) duplex stainless steel. They were tested under slow strain rate experiments, conducted in simulated service environments containing H{sub 2}S, CO{sub 2} and Cl{sup {minus}} containing brine. The parameters selected to quantify the susceptibility to environmentally assisted cracking (EAC) were ductility (as measured by elongation and reduction in area), fracture energy (as measured by the area under stress versus strain curves) and time to failure. These parameters were analyzed considering the ratio of the property in the corrosive environment to the result in an inert environment at the same temperature. The classification of fracture type defined by the proposed NACE T-1F-9 test method was also used. It was concluded that the SSR testing was able to screen corrosion resistant alloys for stress corrosion cracking in sour oil field service. It was shown that, although 22Cr (duplex steel) had a higher corrosion resistance compared to 13Cr-5Ni-2Mo and of 13Cr martensitic stainless steels, there was a region, pH above 4, temperatures up to 150 C, H{sub 2}S partial pressure below 1.5 psia and CO{sub 2} partial pressure of 130 psia, where 13Cr failed but where 13Cr-5Ni-2Mo gave acceptable results. It was concluded that pH and temperature of the environment work together and play an important role on the mechanism of failure.

  9. Fractal characteristics of cracks and fragments generated in unloading rockburst tests

    Institute of Scientific and Technical Information of China (English)

    Li Dejian; Zhao Fei; Zheng Maojiong

    2014-01-01

    True triaxial rockburst experiments with four different unloading rates were performed on four prism specimens of granite sampled from Beishan, China. The damage evolution in the rockburst test was investigated from two aspects including fracture surface crack and fragment characteristics. The scanning electron microscopy was used to observe the micro crack information on fragment surface. Combing binarization and box counting dimensions, the fractal dimensions of cracks were obtained. Meanwhile, the fragments were collected and a sieving experiment was conducted. We weighed the fragments qualities, counted the amount of fragments and measured the fragments length, width and thickness. Utilizing four methods to calculate damage fractal dimensions of fragments, the trend of fractal value changing with unloading rates can be roughly described. It can be concluded from these experiments that the fractal dimension either for crack or for fragment holds a decreasing trend with the decreasing unloading rate, indicating a reduction of damage level.

  10. The corrosion rate of copper in a bentonite test package measured with electric resistance sensors

    Energy Technology Data Exchange (ETDEWEB)

    Rosborg, Bo [Division of Surface and Corrosion Science, KTH, Stockholm (Sweden); Kosec, Tadeja; Kranjc, Andrej; Kuhar, Viljem; Legat, Andraz [Slovenian National Building and Civil Engineering Institute, Ljubljana (Slovenia)

    2012-12-15

    LOT1 test parcel A2 was exposed for six years in the Aespoe Hard Rock Laboratory, which offers a realistic environment for the conditions that will prevail in a deep repository for high-level radioactive waste disposal in Sweden. The test parcel contained copper electrodes for real-time corrosion monitoring in bentonite ring 36, where the temperature was 24 deg C, and copper coupons in bentonite rings 22 and 30, where the temperature was higher. After retrieval of the test parcel in January 2006, a bentonite test package consisting of bentonite rings 35 - 37 was placed in a container and sealed with a thick layer of paraffin. Later the same year new copper electrodes were installed in the test package. In January 2007 electric resistance (ER) sensors of pure copper with a thickness of 35 {mu}m were also installed in the test package mainly to facilitate the interpretation of the results from the real-time corrosion monitoring with electrochemical techniques. The ER measurements have shown that the corrosion rate of pure copper exposed in an oxic bentonite/ saline groundwater environment at room temperate decreases slowly with time to low but measurable values. The corrosion rates estimated from the regularly performed EIS measurements replicate the ER data. Thus, for this oxic environment in which copper acquires corrosion potentials of the order of 200 mV (SHE) or higher, electrochemical measurements provide believable data. Comparing the recorded ER data with an estimate of the average corrosion rate based on comparing cross-sections from exposed and protected sensor elements, it is obvious that the former overestimates the actual corrosion rate, which is understandable. It seems as if electrochemical measurements can provide a better estimate of the corrosion rate; however, this is quite dependent on the use of proper measuring frequencies and evaluation methods. In this respect ER measurements are more reliable. It has been shown that real-time corrosion

  11. Assessment of the Efficiency of HWCon IASCC Crack Growth Rate for High Fluence BWRMaterials

    Energy Technology Data Exchange (ETDEWEB)

    Teysseyre, Sebastien Paul [Idaho National Lab. (INL), Idaho Falls, ID (United States)

    2016-09-01

    This report describes the experimental study performed to assess the efficiency of hydrogen water chemistry on the propagation rate of cracks generated by irradiation assisted stress corrosion cracking in high fluence material. The selection of the material and the test procedures followed for this study are presented. The test results obtained with 8.6 dpa specimen are discussed.

  12. Testing study of subcritical crack growth rate and fracture toughness in different rocks

    Institute of Scientific and Technical Information of China (English)

    CAO Ping; LI Jiang-teng; YUAN Hai-ping

    2006-01-01

    Subcritical crack growth of double torsion specimens made of ore, lherzolite, marble and granite was studied using Instron1342 type electro hydraulic servo test machine. The relations of the mode-Ⅰ stress intensity factor KI versus the subcritical crack growth velocity v and the fracture toughness KIC were obtained by the double torsion constant displacement load relaxation method. The behavior of subcritical crack growth was analyzed for different rocks. The results show that lgKI-lgv relations of four kinds of rocks measured by this method accord with linear rule, i.e. the relations between subcritical crack growth velocity and stress intensity factor have a power law, which is in good agreement with CHARLES theory. lgKI-lgv curves move to top left corner with the decrease of the elastic modulus, which implies that the subcritical crack growth velocity speeds up. The maximum subcritical crack growth velocity exhibits negative exponential increase, and mode-Ⅰ fracture toughness KIC decreases with the decrease of elastic modulus. The testing results provide a basis for time-dependence of rock engineering stability.

  13. Testing the Corrosion Behaviour of Plated Aluminum Strips for Heat Exchangers Operating in the Automotive Industry

    Science.gov (United States)

    Nowak, Marek; Opyrchał, Mieczysław; Kłyszewski, Andrzej; Żelechowski, Janusz

    The automotive industry uses heat exchangers made of aluminum alloys. The radiators for an engine cooling system comprise elements (tubes) in which the coolant flows. These elements are made of AlMn alloys (e.g. AlMn or AlMnCu), while ribs are made from the sheet metal plated with AlSi alloys. While in service, the heat exchangers are exposed to harsh weather conditions, hence the need to ensure that the individual elements of the design are adequately protected from corrosion. One of the ways to obtain this protection is by modification of the chemical composition of aluminum alloys used in the manufacture of radiators. In this study, corrosion tests were carried out to characterise the investigated materials in terms of their corrosive behavior. The experiments included measurements of corrosion potential, testing of corrosion resistance in neutral salt spray, and electrochemical studies of selected plated AlMn alloy strips with different chemical composition.

  14. White-Etching Matter in Bearing Steel. Part I: Controlled Cracking of 52100 Steel

    Science.gov (United States)

    Solano-Alvarez, W.; Bhadeshia, H. K. D. H.

    2014-10-01

    Although most of the research performed in bearing steel metallurgy aims to prevent crack nucleation and propagation, some applications require the exact opposite in order to study the role that disconnected surfaces inside the bulk material play when load is applied, or when fluids entrapped in surface cracks propagate tensile stresses or exacerbate corrosion. Four heat treatments have been designed to create controlled arrays of crack types and distributions in quenched and untempered steel normally used in the manufacture of bearings. The varieties of cracks studied include sparsely distributed martensite-plate cracks, fine-grain-boundary cracks, abundant martensite-plate cracks, and surface cracks. The intention was to create samples which can then be subjected to appropriate mechanical testing so that phenomena such as the appearance of "white-etching areas" or "white-etching cracks," crack-lubricant interactions, or hydrogen trapping can be studied further.

  15. Stress corrosion evaluation of powder metallurgy aluminum alloy 7091 with the breaking load test method

    Science.gov (United States)

    Domack, Marcia S.

    1987-01-01

    The stress corrosion behavior of the P/M aluminum alloy 7091 is evaluated in two overaged heat treatment conditions, T7E69 and T7E70, using an accelerated test technique known as the breaking load test method. The breaking load data obtained in this study indicate that P/M 7091 alloy is highly resistant to stress corrosion in both longitudinal and transverse orientations at stress levels up to 90 percent of the material yield strength. The reduction in mean breaking stress as a result of corrosive attack is smallest for the more overaged T7E70 condition. Details of the test procedure are included.

  16. The effects of thermomechanical processing and annealing on the microstructural evolution and stress corrosion cracking of alloy 690

    Science.gov (United States)

    Miller, Cody A.

    The effects of short-range order (SRO), long-range order (LRO), and plastic strain on the microstructure and stress corrosion cracking (SCC) susceptibility of Ni-Cr-Fe Alloy 690 have been investigated in detail. First, the presence of 1/3{422} and 1/2{311} diffuse intensities in B=[111] and B=[112] selected area diffraction patterns (SADPs), previously believed to indicate the presence of SRO, has been examined in Alloy 690, a Ni-Cr binary alloy, and a number of FCC materials in an effort to determine their source. It is shown that these intensities are not due to SRO, although their source remains somewhat unclear. However, an experiment was conducted that tracked the strong {111} reflections in a B=[112] SADP as the sample was tilted (19°) towards a B=[111] zone axis. Significantly, it was noted that the {111} intensities never fully disappear and that they fall in the 1/3{422} positions within the B=[111] SADP. This indicates that these diffuse intensities are related to reflections that lie in the first order Laue zone (FOLZ) when the zone is aligned along B=[111], although theoretical calculations indicate scattering from these planes into the zero order Laue zone used to form the SADP should not occur. Thus, while calculations are inconsistent with the behavior expected, the diffuse intensities observed in a number of high index zones are consistent with projections of higher order Laue zone reflections into the zero layer, suggesting that the theory is in need of reassessment. Second, the stability of the gamma'-Ni2Cr LRO phase present on the Ni-Cr phase diagram was examined in a Ni-55Cr binary alloy. The results indicate that the gamma'-Ni2Cr phase is indeed metastable, and that the two-phase gamma-Ni + alpha-Cr phase field extends all the way to room temperature. Likewise, the sluggish formation of the gamma'-Ni 2Cr phase appears to occur only over a narrow composition and temperature range. It is speculated that this important phase in more complex

  17. Field testing results for the strategic petroleum reserve pipeline corrosion control program

    Energy Technology Data Exchange (ETDEWEB)

    Buchheit, R.G.; Maestas, L.M.; Hinkebein, T.E.

    1998-02-01

    Results of two studies conducted as part of the Strategic Petroleum Reserve (SPR) Pipeline Corrosion Control Program are reported. These studies focused on evaluation of rotary-applied concrete materials for internal pipeline protection against the erosive and corrosive effects of flowing brine. The study also included evaluation of liners applied by hand on pipe pieces that cannot be lined by rotary methods. Such pipe pieces include tees, elbows and flanged pipe sections. Results are reported from a corrosion survey of 17 different liner formulations tested at the-Big-Rill SPR Site. Testing consisted of electrochemical corrosion rate measurements made on lined pipe sections exposed, in a test manifold, to flowing SPR generated fluids. Testing also involved cumulative immersion exposure where samples were exposed to static site-generated brine for increasing periods of time. Samples were returned to the laboratory for various diagnostic analyses. Results of this study showed that standard calcium silicate concrete (API RP10E) and a rotary calcium aluminate concrete formulation were excellent performers. Hand-lined pipe pieces did not provide as much corrosion protection. The focus of the second part of the study was on further evaluation of the calcium silicate, calcium aluminate and hand-applied liners in actual SPR equipment and service. It was a further objective to assess the practicality of electrochemical impedance spectroscopy (EIS) for field corrosion monitoring of concrete lined pipe compared to the more well-known linear polarization technique. This study showed that concrete linings reduced the corrosion rate for bare steel from 10 to 15 mils per year to 1 mil per year or less. Again, the hand-applied liners did not provide as much corrosion protection as the rotary-applied liners. The EIS technique was found to be robust for field corrosion measurements. Mechanistic and kinetic corrosion rate data were reliably obtained.

  18. Preparation and testing of corrosion and spallation-resistant coatings

    Energy Technology Data Exchange (ETDEWEB)

    Hurley, John P. [Univ. of North Dakota, Grand Forks, ND (United States); Cavalli, Matthew N. [Univ. of North Dakota, Grand Forks, ND (United States)

    2016-06-30

    its standard oxidation, spallation, and corrosion testing, which was scheduled for completion in the spring of 2016. However, because of commercial demands, the tests were not completed by the time of this report except some initial spallation tests at 1150°C. In those tests, several of the APMT plates separated from the CM247LC, likely because of the remaining aluminum oxide scale on the surface of the CM247LC. This implies that surface preparation may need to include machining to remove the oxide scale before bonding rather than just sandblasting. In previous tensile testing at 950°C, the breaks in the tensile samples always occurred in the APMT and not at the joints. Gasifier sampling was completed to determine what types of trace contaminants may occur in cleaned and combusted syngas and that could lead to corrosion or deposition in turbines firing coal syngas. The sampling was done from a pressurized fluidized-bed gasifier and a pressurized entrained-flow gasifier. The particles captured on a filter from syngas were typically 0.2 to 0.5 μm in diameter, whereas those captured from the combusted syngas were slightly larger and more spherical. X-ray photoelectron spectroscopy done at Oak Ridge National Laboratory showed that the particles do not contain any metals and have an atomic composition almost identical to that of the polycarbonate filter. This indicates that the particles are primarily soot-based and not formed from volatilization of metals in the gasifiers.

  19. Study on optimization method of test conditions for fatigue crack detection using lock-in vibrothermography

    Science.gov (United States)

    Min, Qing-xu; Zhu, Jun-zhen; Feng, Fu-zhou; Xu, Chao; Sun, Ji-wei

    2017-06-01

    In this paper, the lock-in vibrothermography (LVT) is utilized for defect detection. Specifically, for a metal plate with an artificial fatigue crack, the temperature rise of the defective area is used for analyzing the influence of different test conditions, i.e. engagement force, excitation intensity, and modulated frequency. The multivariate nonlinear and logistic regression models are employed to estimate the POD (probability of detection) and POA (probability of alarm) of fatigue crack, respectively. The resulting optimal selection of test conditions is presented. The study aims to provide an optimized selection method of the test conditions in the vibrothermography system with the enhanced detection ability.

  20. Assessment of the Effects of Cold Work on Crack Initiation in a Light Water Environment Using the Small-Punch Test

    Science.gov (United States)

    Isselin, Jerome; Kai, Akira; Sakaguchi, Kazuhiko; Shoji, Tetsuo

    2008-05-01

    Work hardening induced by manufacturing processes has important consequences for the resistance to the stress corrosion cracking (SCC) of low-carbon stainless steel in high-temperature water conditions. It is of great importance to unders