WorldWideScience

Sample records for aluminium 27 beams

  1. Electron beam welding of aluminium components

    International Nuclear Information System (INIS)

    Maajid, Ali; Vadali, S.K.; Maury, D.K.

    2015-01-01

    Aluminium is one of the most widely used materials in industries like transportation, shipbuilding, manufacturing, aerospace, nuclear, etc. The challenges in joining of aluminium are distortion, cleanliness and quality. Main difficulties faced during fusion welding of aluminium components are removal of surface oxide layer, weld porosity, high heat input requirement, distortion, hot cracking, etc. Physical properties of aluminium such as its high thermal conductivity, high coefficient of thermal expansion, no change in colour at high temperature, large difference in the melting points of the metal and its oxide (∼ 1400 °C) compound the difficulties faced during welding. Gas Tungsten Arc Welding (GTAW), Gas Metal Arc Welding (GMAW), Plasma Arc Welding (PAW), etc are generally used in industries for fusion welding of aluminium alloys. However in case of thicker jobs the above processes are not suitable due to requirements of elaborate edge preparation, preheating of jobs, fixturing to prevent distortion, etc. Moreover, precise control over the heat input during welding and weld bead penetration is not possible with above processes. Further, if heat sensitive parts are located near the weld joint then high energy density beam welding process like Electron Beam Welding (EBW) is the best possible choice for aluminium welding.This paper discusses EB welding of aluminium components, typical geometry of components, selection/optimization of welding parameters, problems faced during standardization of welding and process parameters and their remedies etc.

  2. Ion beam analysis of aluminium in thin layers

    International Nuclear Information System (INIS)

    Healy, M.J.F.; Pidduck, A.J.; Dollinger, G.; Gorgens, L.; Bergmaier, A.

    2002-01-01

    This work quantifies aluminium in thin surface and near surface layers. In one example, the layer overlies a thin gallium nitride layer on an aluminium oxide substrate and in a second example the aluminium exists just below the surface of an indium arsenide substrate. The technique of non-Rutherford elastic backscattering of protons was used for the samples where aluminum in the layer of interest needed to be resolved from aluminium in the sapphire substrate and the results were corroborated at the Technische Universitaet Muenchen using heavy ion elastic recoil detection analysis. In the second example, where it was unnecessary to isolate the signal of aluminium in the layer of interest (as the substrate contained no aluminium), then the 27 Al(d,p 01 ) 28 Al nuclear reaction was used. The elastic proton scattering cross section of aluminum was found to vary very rapidly over the energy range of interest

  3. Irradiation of aluminium alloy materials with electron beam

    International Nuclear Information System (INIS)

    Konno, Osamu; Masumoto, Kazuyoshi

    1982-01-01

    It is a theme with a room for discussion to employ the stainless steel composed of longer half-life materials for the vacuum system of accelerators, from the viewpoint of radiation exposure. Therefore, it is desirable to use aluminium of shorter half-life in place of stainless steel. As a result of investigation on the above theme in the 1.2 GeV electron linac project in Tohoku University, it has been concluded that aluminium alloy vacuum chambers can reduce exposure dose by about one or two figures as compared with stainless steel ones. Of course, aluminium alloy contains trace amounts of Mg, Si, Ti, Cr, Mn, Fe, Zn, Cu and others. Therefore, four kinds of aluminium alloy considered to be usable have been examined for induced radioactivity by electron beam irradiation. Stainless steel SUS 304 has been also irradiated for comparison. Radiation energy has been 30 MeV and 200 MeV. When stainless steel and aluminium alloy were compared, aluminium alloy was very effective for reducing surface dose in low energy irradiation. In 200 MeV irradiation, the dose ratio of aluminium alloy to stainless steel became 1/30 to 1/100 after one week, though the dose difference between these two materials became smaller in 100 days or more after irradiation. If practical inspection and repair are implemented during the period from a few days to one week after shutdown, the aluminium alloy is preferable for exposure dose reduction even in high energy irradiation. (Wakatsuki, Y.)

  4. Aluminium-27 n.m.r. studies of aluminium fluoro complexes in dichloromethane solution: evidence for tetrafluoroaluminate anion

    International Nuclear Information System (INIS)

    Colton, R.; Eller, P.G.

    1989-01-01

    Mixed aluminium chloro/fluoro anions are formed in dichloromethane solution by the interaction of AlCl 3 and [Ph 3 PhCH 2 P] [H 2 F 3 ]. Aluminium-27 n.m.r. studies are restricted to the stoichiometric ranges F/Al from 1:1 to 3:1 and F/Al>8:1. Between these limits rapid precipitation reactions occur. In the fluoride-rich stoichiometric range there is rapid exchange on the n.m.r. time scale between the aluminium fluoro anion and free fluoride, so that a direct identification of the species by the multiplicity of the resonance is not possible. Indirect evidence strongly suggests that the aluminium species is [AlF 4 ] - . In the F/Al stoichiometry range from 1:1 to 3:1 aluminium-27 resonances were observed for all the other possible [AlCl χ F 4-χ ] - species. Studies on the aluminium iodo/fluoro system support the identification of [AlF 4 ] - , but the system is labile and the mixed iodo/fluoro species undergo rapid disproportionation. 12 refs., 1 fig

  5. Quantification of aluminium-27 NMR spectra of high-surface-area oxides

    International Nuclear Information System (INIS)

    Pearson, R.M.; Schramm, C.M.

    1990-01-01

    This paper discusses the quantitation of 27 Al NMR spectra. It is showns that the so called 'invisible' aluminium atoms seen by recent workers are completely consistent with known continuous wave NMR studies of the 27 Al NMR spectra of high surface area aluminium oxides. The use of pulsed NMR techniques further complicate the quantitative measurement of 27 Al NMR spectra, especially when high resolution NMR spectrometers are used for this purpose. Methods are described which allow both the estimation of aluminium not seen by continuous wave techniques and the amounts of the NMR spectra lost in pulsed work. (author). 24 refs.; 6 figs.; 1 tab

  6. IEC 61267: Feasibility of type 1100 aluminium and a copper/aluminium combination for RQA beam qualities.

    Science.gov (United States)

    Leong, David L; Rainford, Louise; Zhao, Wei; Brennan, Patrick C

    2016-01-01

    In the course of performance acceptance testing, benchmarking or quality control of X-ray imaging systems, it is sometimes necessary to harden the X-ray beam spectrum. IEC 61267 specifies materials and methods to accomplish beam hardening and, unfortunately, requires the use of 99.9% pure aluminium (Alloy 1190) for the RQA beam quality, which is expensive and difficult to obtain. Less expensive and more readily available filters, such as Alloy 1100 (99.0% pure) aluminium and copper/aluminium combinations, have been used clinically to produce RQA series without rigorous scientific investigation to support their use. In this paper, simulation and experimental methods are developed to determine the differences in beam quality using Alloy 1190 and Alloy 1100. Additional simulation investigated copper/aluminium combinations to produce RQA5 and outputs from this simulation are verified with laboratory tests using different filter samples. The results of the study demonstrate that although Alloy 1100 produces a harder beam spectrum compared to Alloy 1190, it is a reasonable substitute. A combination filter of 0.5 mm copper and 2 mm aluminium produced a spectrum closer to that of Alloy 1190 than Alloy 1100 with the added benefits of lower exposures and lower batch variability. Copyright © 2015 Associazione Italiana di Fisica Medica. Published by Elsevier Ltd. All rights reserved.

  7. Aluminium fumarate and CPO-27(Ni) MOFs: Characterization and thermodynamic analysis for adsorption heat pump applications

    International Nuclear Information System (INIS)

    Elsayed, Eman; AL-Dadah, Raya; Mahmoud, Saad; Elsayed, Ahmed; Anderson, Paul A.

    2016-01-01

    Highlights: • CPO-27(Ni) and aluminium fumarate were investigated for adsorption heating, cooling and desalination applications. • Both MOFs have high potential in adsorption applications. • The optimum desorption temperature for the CPO-27(Ni) is higher than 90 °C, and for aluminium fumarate, it is 55–70 °C. • CPO-27(Ni) outperforms aluminium fumarate at low evaporation temperature (5 °C). • Aluminium fumarate outperforms CPO-27(Ni) at high evaporation temperature (20 °C). - Abstract: Metal-organic framework (MOF) materials are new porous materials with high surface area, pore size and volume, and tunable pore geometry thus providing high adsorption capacity. Currently, limited MOF materials with high water adsorption capabilities and hydrothermal stability are available on a large scale. Two MOF materials, namely CPO-27(Ni) and aluminium fumarate, have been identified to have a high hydrothermal stability, high water uptake of 0.47 g_H_2_O_.g_a_d_s"−"1 and 0.53 g_H_2_O_.g_a_d_s"−"1 at a relative pressure of 0.9 and are commercially available. This work aims to measure the water adsorption characteristics of these two MOF materials in terms of isotherms, kinetics and cyclic stability. Also the thermodynamic cycle performance of such materials based on their equilibrium adsorption data was investigated under different operating conditions for various adsorption applications such as heating, cooling and water desalination. Results showed that the CPO-27(Ni)/water pair outperformed the aluminium fumarate/water pair at low evaporation temperatures (5 °C) and high desorption temperatures (≥90 °C), while the aluminium fumarate/water pair was more suitable for applications requiring high evaporation temperature (20 °C) and/or low desorption temperature (70 °C).

  8. Studies for determining thermal ion extraction potential for aluminium plasma generated by electron beam evaporator

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, V Dileep; Barnwal, Tripti A; Mukherjee, Jaya; Gantayet, L M, E-mail: dileepv@barc.gov.i [Laser and Plasma Technology Division, Bhabha Atomic Research Centre, Mumbai-400085 (India)

    2010-02-01

    For effective evaporation of refractory metal, electron beam is found to be most suitable vapour generator source. Using electron beam, high throughput laser based purification processes are carried out. But due to highly concentrated electron beam, the vapour gets ionised and these ions lead to dilution of the pure product of laser based separation process. To estimate the concentration of these ions and extraction potential requirement to remove these ions from vapour stream, experiments have been conducted using aluminium as evaporant. The aluminium ingots were placed in water cooled copper crucible. Inserts were used to hold the evaporant, in order to attain higher number density in the vapour processing zone and also for confining the liquid metal. Parametric studies with beam power, number density and extraction potential were conducted. In this paper we discuss the trend of the generation of thermal ions and electrostatic field requirement for extraction.

  9. Laser beam welding of high strength aluminium-lithium alloys; Laserstrahlschweissen von hochfesten Aluminium-Lithium Legierungen

    Energy Technology Data Exchange (ETDEWEB)

    Enz, Josephin

    2012-07-01

    The present development in aircraft industry determined by the demand for a higher cost-effectiveness. Laser beam welding is one of the most promising joining technologies for the application in the aircraft industry through the considerable reduction of the production costs. Furthermore the weight of an aircraft structure can be reduced by the use of light and high strength aluminium alloys. This paper deals with the development of a process for the laser beam welding of a skin-stringer-joint where the Al-Li-alloy AA2196 is used as stringer material and the Al-Li-alloy AA2198 is used as skin and stringer material. By the use of design of experiments the optimal welding process parameters for different material combinations were determined which will be used for the welding of a 5-stringer panel. Therefore the weld seams of the joints were tested for irregularities and microstructural characteristics. In addition several mechanical tests were performed, which define the quality of the welded joint. Furthermore the influence of the oxide layer and the welding preparation on the welding performance was investigated. (orig.) [German] Die derzeitigen Entwicklungen im Flugzeugbau werden durch die allgemeine Forderung nach einer Steigerung der Wirtschaftlichkeit bestimmt. Das Laserstrahlschweissen ist dabei eines der vielversprechendsten Fuegeverfahren fuer die Anwendung im Flugzeugbau durch das die Herstellungskosten deutlich reduziert werden koennen. Zudem kann durch die Verwendung von leichten und hochfesten Aluminium-Legierungen das Gewicht einer Flugzeugstruktur zusaetzlich reduziert werden. Die vorliegende Arbeit befasst sich mit der Entwicklung eines Prozesses zum Laserstrahlschweissen einer Skin-Stringer-Verbindung aus den Aluminium-Lithium-Legierungen AA2196 (als Stringer-Werkstoff) und AA2198 (als Skin- und Stringer-Werkstoff). Unter Verwendung der statistischen Versuchsplanung wurden die optimalen Einstellungen der Schweissprozessparameter fuer die

  10. Novel manufacturing method by using stainless steel pipes expanded into aluminium profiles for the ITER Neutral Beam cryopumps

    Energy Technology Data Exchange (ETDEWEB)

    Dremel, Matthias, E-mail: matthias.dremel@iter.org; Boissin, Jean-Claude; Déléage, Vincent; Quinn, Eamonn; Pearce, Robert

    2015-10-15

    This paper describes the novel engineering and manufacturing solution of stainless steel pipe expansion into aluminium extrusion profiles for use at cryogenic temperatures up to 400 K. This fabrication method will be used for the thermal radiation shields and the cryopanels of the ITER Neutral Beam cryopumps. The use of stainless steel pipes expanded into aluminium extrusion profiles is a solution that combines standard stainless steel welding procedures for the manifolds of the cooling circuits with extended aluminium structures taking advantage of the high thermal conductivity of aluminium. The cryogenic cooling circuits of the pump are a first confinement barrier in the ITER vacuum vessel and the risk of a leakage needs to be minimized as far as possible. The expansion method avoids the need of joints of dissimilar materials in the primary confinement barrier. The fabrication method and results of the prototyping of full scaled components for the ITER Neutral Beam cryopumps are outlined in this paper.

  11. MICRO-MATERIAL HANDLING EMPLOYING E-BEAM GENERATED TOPOGRAPHIES OF COPPER AND ALUMINIUM

    Directory of Open Access Journals (Sweden)

    S. Matope

    2012-01-01

    Full Text Available

    ENGLISH ABSTRACT: This paper focuses on the employment of copper and aluminium in a micro-material handling system actuated by Van der Waals forces. Electron beam (e-beam evaporator deposited both materials on a silicon substrate at a rate of 0.6-1.2 Angstroms/second, vacuum pressure between 2x10-6 and 3x10-6mbar, and at a current less than 10mA. A Veeco NanoMan V Atomic Force Microscope with Nanoscope version 7.3 software was used to analyse the root mean square (rms surface roughnesses of the generated topographies. Rumpf-Rabinovich’s rms formula was used to determine the Van der Waals forces exerted by the surfaces. It was synthesised that an e-beam deposition of 7 minutes’ duration on both materials produced an optimum micro-material handling solution, with copper suitable for the pick-up position and aluminium for the placement position.

    AFRIKAANSE OPSOMMING: Die fokus van die artikel is op die gebruik van koper en aluminium in ‘n mikromateriaalhanteringstelsel, aangedryf deur Van der Waalskragte. ‘n Elektronstraal-verdamper plaas albei materiale op ‘n silikonbasis teen ‘n tempo van 0.6-1.2 Angstrom/sekonde, vakuumdruk tussen 2x10-6 en 3x10-6mbar, en teen ‘n stroom van minder as 10mA. ‘n Veeco NanoMan V Atomic Force mikroskoop, met Nanoscope 7.3 program-matuur is gebruik om die wortel-gemiddelde-kwadraat (wgk oppervlak ruheid van die gegenereerde topografieë te analiseer. Rumpf-Rabinovich se wgk-formule is gebruik om die Van der Waalskrage wat deur die oppervlaktes uitgeoefen word te bepaal. Dit is vasgestel dat ‘n elektronstraalafsetting van 7 minute op albei materiale die optimale materiaalhanteringoplossing bied, met koper geskik vir die optelposisie en aluminium vir die plasingsposisie.

  12. Development of the electron beam welding of the aluminium alloy 6061-T6 for the Jules Horowitz reactor

    International Nuclear Information System (INIS)

    Leblanc, Y.

    2013-01-01

    The aluminium alloy 6061-T6 has been selected for the construction of the Jules Horowitz's reactor vessel. This reactor vessel is pressurized and will be made through butt welding of ∼ 2 cm thick aluminium slabs. The electron beam welding process has been tested and qualified. It appears that this welding process allows: -) welding without pre-heating, -) vacuum welding, -) welding of 100% of the thickness in one passage, -) very low deforming welding process, -) very low density and very low volume of blow holes, -) weak ZAT (Thermal Affected Zones), and -) high reproducibility that permits automation. (A.C.)

  13. Erosion resistance of composite materials on titanium, zirconium and aluminium nitride base under the electron beam effect

    International Nuclear Information System (INIS)

    Verkhoturov, A.D.; Kuzenkova, M.A.; Slutskin, M.G.; Kravchuk, L.A.

    1977-01-01

    Erosion resistance of composites based on nitrides of titanium, zirconium and aluminium to spark and electron beam processing has been studied. The erosion resistance in spark processing is shown to depend on specific electric resistance of the alloys. TiN-AlN and ZrN-AlN alloys containing more than 70% AlN (with specific electric resistance more than 10 6 -10 7 ohm/cm) caot be processed by spark method. It is shown that erosion of the composites by an electron beam depends primarily on the rate of evaporation of the components

  14. Void formation in pure aluminium irradiated with high-energetic electron beams and gamma-quanta

    DEFF Research Database (Denmark)

    Gan, V. V.; Ozhigou, L. S.; Yamnitsky, V. A.

    1983-01-01

    The spatial distribution of displaced atoms and helium atoms and also the spectra of damaging energies of primary displaced atoms in a thick aluminium target irradiated with electrons of 225 MeV energy were calculated. Pure aluminium (99.9999%) irradiated up to 0.04 dose was studied by electron...

  15. Investigation of aluminium ohmic contacts to n-type GaN grown by molecular beam epitaxy

    Science.gov (United States)

    Kribes, Y.; Harrison, I.; Tuck, B.; Kim, K. S.; Cheng, T. S.; Foxon, C. T.

    1997-11-01

    Using epi-layers of different doping concentrations, we have investigated aluminium contacts on n-type gallium nitride grown by plasma source molecular beam epitaxy. To achieve repeatable and reliable results it was found that the semiconductor needed to be etched in aqua-regia before the deposition of the contact metallization. Scanning electron micrographs of the semiconductor surface show a deterioration of the semiconductor surface on etching. The specific contact resistivity of the etched samples were, however, superior. Annealing the contacts at 0268-1242/12/11/030/img9 produced contacts with the lowest specific contact resistance of 0268-1242/12/11/030/img10. The long-term aging of these contacts was also investigated. The contacts and the sheet resistance were both found to deteriorate over a three-month period.

  16. Aluminium production

    International Nuclear Information System (INIS)

    Winter, B.; Ayers, J.; Sammer, G.

    2001-01-01

    Aluminium is the most important non-ferrous metal by quantity. Aluminium is produced by electrolysis of aluminium oxide (also known as alumina). Alumina is produced by refining bauxite. The quantity of primary and secondary aluminium production in ECE-countries between 1992 and 1998 is shown. The European aluminium industry employs approximately 200 000 employees. The annual aluminium production in the European Union was 3.58 million tonnes in 1994, of which 44 % was secondary aluminium. In 1996 3.96 million tonnes of aluminium were produced in the EU, of which 44 % was secondary aluminium. (author)

  17. Structure and properties of an aluminium alloy welded by electron beam

    International Nuclear Information System (INIS)

    Ruzimov, Sh.M.; Palvanov, S.R.; Pogrebnjak, A.D.

    2005-01-01

    Full text: In the given work the experimental results on research of influence of electronic beams on structure of an aluminum alloy are submitted. As a basis of samples the alloy Al-Mg-Zn-Cu by the additives Se-0.5 % and Nb-0.15 % is chosen. Samples from a cast aluminum alloy by thickness of 3 mm such as B-96 were welded with an electronic beam in three different modes at radius circle of a root of a welded seam of 5 mm. The welding was carried out by an alloy Amg 63 and Sv-1571 with application electron team welding joint of parts. The basic influence on the given process makes energy - allocation of an electronic beam. For research of phase structure used of X-ray beams (XRD), DRON-2 in copper K α - Cu measurement. For research of structure and morphology of a surface used optical microscope with increase 800-1500 times and electronic microscope with the microanalysis. On figures of optical microscopy the morphology of a seam sharply differs from morphology of an initial part. The microanalysis carried out with a place of a seam, has shown presence of the whole spectrum of elements, such as, Al; Zn; Na; Mg; Cu; and Mn. All measurements carried out in welding zone and in frontier zones that it was possible to carry out the comparative analysis. The element structure of these zones essentially differs in dependence of a condition of welding

  18. Laser beam welding and friction stir welding of 6013-T6 aluminium alloy sheet

    International Nuclear Information System (INIS)

    Braun, R.; Dalle Donne, C.; Staniek, G.

    2000-01-01

    Butt welds of 1.6 mm thick 6013-T6 sheet were produced using laser beam welding and friction stir welding processes. Employing the former joining technique, filler powders of the alloys Al-5%Mg and Al-12%Si were used. Microstructure, hardness profiles, tensile properties and the corrosion behaviour of the welds in the as-welded condition were investigated. The hardness in the weld zone was lower compared to that of the base material in the peak-aged temper. Hardness minima were measured in the fusion zone and in the thermomechanically affected zone for laser beam welded and friction stir welded joints, respectively. Metallographic and fractographic examinations revealed pores in the fusion zone of the laser beam welds. Porosity was higher in welds made using the filler alloy Al-5%Mg than using the filler metal Al-12%Si. Transmission electron microscopy indicated that the β '' (Mg 2 Si) hardening precipitates were dissolved in the weld zone due to the heat input of the joining processes. Joint efficiencies achieved for laser beam welds depended upon the filler powders, being about 60 and 80% using the alloys Al-5%Mg and Al-12%Si, respectively. Strength of the friction stir weld approached over 80% of the ultimate tensile strength of the 6013-T6 base material. Fracture occurred in the region of hardness minima unless defects in the weld zone led to premature failure. The heat input during welding did not cause a degradation of the corrosion behaviour of the welds, as found in continuous immersion tests in an aqueous chloride-peroxide solution. In contrast to the 6013-T6 parent material, the weld zone was not sensitive to intergranular corrosion. Alternate immersion tests in 3.5% NaCl solution indicated high stress corrosion cracking resistance of the joints. For laser beam welded sheet, the weld zone of alternately immersed specimens suffered severe degradation by pitting and intergranular corrosion, which may be associated with galvanic coupling of filler metal and

  19. Use of aluminium plates to simulate the dosimetry of gems during e-beam irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Fortes, Marcio Z.; Sousa, Fernando N.C. de; Boente, Otavio C., E-mail: mzamboti@aceletron.com.b, E-mail: fernando.nuno@aceletron.com.b, E-mail: otavio@aceletron.com.b [Aceletron Irradiacao Industrial, Rio de Janeiro, RJ (Brazil); Sousa, Nuno R.A., E-mail: engenheiro.nuno.sousa@gmail.co [Universidade Federal do Rio de Janeiro (UFRJ), RJ (Brazil). Dept. de Engenharia Mecanica

    2009-07-01

    The e-beam technology is used in the industrial irradiation of several products like turf, sterilization of medical products, cosmetics, polymers, food, and gems. More than 70% of the gems commercialized in the world receive treatments similar to those present in nature, including heat, and irradiation, in order to improve their value. Since aluminum has a density similar to that of several commercial gems, this paper presents a study of the penetration of electrons in calibrated aluminum plates simulating several different thicknesses ranging from 5 to 30 mm, and comparing with the one obtained in gems. This allows the monitoring of the dose received by gems during irradiation with e-beam systems measuring the delivered surface dose. This procedure is very important for industrial processing of stones due to the irregularities present on most gems, what makes dosimetry a very complex task. The determination of the thicknesses of the gems for which the surface dose is the lowest dose on the whole product assures the precise determination of the minimum dose received by the gems during industrial processing. (author)

  20. A new aluminium-hydrate species in hydrated Portland cements characterized by 27Al and 29Si MAS NMR spectroscopy

    International Nuclear Information System (INIS)

    Andersen, Morten Daugaard; Jakobsen, Hans J.; Skibsted, Jorgen

    2006-01-01

    Recent 27 Al MAS NMR studies of hydrated Portland cements and calcium-silicate-hydrate (C-S-H) phases have shown a resonance from Al in octahedral coordination, which cannot be assigned to the well-known aluminate species in hydrated Portland cements. This resonance, which exhibits the isotropic chemical shift δ iso = 5.0 ppm and the quadrupole product parameter P Q = 1.2 MHz, has been characterized in detail by 27 Al MAS and 27 Al{ 1 H} CP/MAS NMR for different hydrated white Portland cements and C-S-H phases. These experiments demonstrate that the resonance originates from an amorphous or disordered aluminate hydrate which contains Al(OH) 6 3- or O x Al(OH) 6-x (3+x)- units. The formation of the new aluminate hydrate is related to the formation of C-S-H at ambient temperatures, however, it decomposes by thermal treatment at temperatures of 70-90 o C. From the experiments in this work it is proposed that the new aluminate hydrate is either an amorphous/disordered aluminate hydroxide or a calcium aluminate hydrate, produced as a separate phase or as a nanostructured surface precipitate on the C-S-H phase. Finally, the possibilities of Al 3+ for Ca 2+ substitution in the principal layers and interlayers of the C-S-H structure are discussed

  1. Ion nitriding of aluminium

    International Nuclear Information System (INIS)

    Fitz, T.

    2002-09-01

    The present study is devoted to the investigation of the mechanism of aluminium nitriding by a technique that employs implantation of low-energy nitrogen ions and diffusional transport of atoms. The nitriding of aluminium is investigated, because this is a method for surface modification of aluminium and has a potential for application in a broad spectrum of fields such as automobile, marine, aviation, space technologies, etc. However, at present nitriding of aluminium does not find any large scale industrial application, due to problems in the formation of stoichiometric aluminium nitride layers with a sufficient thickness and good quality. For the purposes of this study, ion nitriding is chosen, as an ion beam method with the advantage of good and independent control over the process parameters, which thus can be related uniquely to the physical properties of the resulting layers. Moreover, ion nitriding has a close similarity to plasma nitriding and plasma immersion ion implantation, which are methods with a potential for industrial application. (orig.)

  2. Aluminium bridges, aluminium bridge decks

    NARCIS (Netherlands)

    Soetens, F.; Straalen, IJ.J. van

    2003-01-01

    Applications of aluminium have grown considerably in building and civil engineering the last decade. In building and civil engineering the increase of aluminium applications is due to various aspects like light weight, durability and maintenance, use of extrusions, and esthetics. The paper starts

  3. The T10 beam produces a few hits per event. In ALICE the SSD will have to cope with many hits per strip. In the three centimeters of aluminium the beam will produce many secondary particles. This increases the chance of multiple hits per strip, although not to the level in ALICE.

    CERN Multimedia

    Nooren, G.

    2004-01-01

    The T10 beam produces a few hits per event. In ALICE the SSD will have to cope with many hits per strip. In the three centimeters of aluminium the beam will produce many secondary particles. This increases the chance of multiple hits per strip, although not to the level in ALICE.

  4. Process parameters-weld bead geometry interactions and their influence on mechanical properties: A case of dissimilar aluminium alloy electron beam welds

    Directory of Open Access Journals (Sweden)

    P. Mastanaiah

    2018-04-01

    Full Text Available Prediction of weld bead geometry is always an interesting and challenging research topic as it involves understanding of complex multi input and multi output system. The weld bead geometry has a profound impact on the load bearing capability of a weld joint, which in-turn decides the performance in real time service conditions. The present study introduces a novel approach of detecting a relationship between weld bead geometry and mechanical properties (e.g. tensile load for the purpose of catering the best the process could offer. The significance of the proposed approach is demonstrated by a case of dissimilar aluminium alloy (AA2219 and AA5083 electron beam welds. A mathematical model of tensile braking load as a function of geometrical attributes of weld bead geometry is presented. The results of investigation suggests the effective thickness of weld – a geometric parameter of weld bead has the most significant influence on tensile breaking load of dissimilar weld joint. The observations on bead geometry and the mechanical properties (microhardness, ultimate tensile load and face bend angle are correlated with detailed metallurgical analysis. The fusion zone of dissimilar electron beam weld has finer grain size with a moderate evaporation and segregation of alloying elements magnesium and copper respectively. The mechanical properties of weld joint are controlled by optimum bead geometry and HAZ softening in weaker AA5083 Al alloy. Keywords: Electron beam welding, AA2219, AA5083, Bead geometry, Tensile breaking load

  5. Investigation of the aluminium-aluminium oxide reversible transformation as observed by hot stage electron microscopy.

    Science.gov (United States)

    Grove, C. A.; Judd, G.; Ansell, G. S.

    1972-01-01

    Thin foils of high purity aluminium and an Al-Al2O3 SAP type of alloy were oxidised in a specially designed hot stage specimen chamber in an electron microscope. Below 450 C, amorphous aluminium oxide formed on the foil surface and was first detectable at foil edges, holes, and pits. Islands of aluminium then nucleated in this amorphous oxide. The aluminium islands displayed either a lateral growth with eventual coalescence with other islands, or a reoxidation process which caused the islands to disappear. The aluminium island formation was determined to be related to the presence of the electron beam. A mechanism based upon electron charging due to the electron beam was proposed to explain the nucleation, growth, coalescence, disappearance, and geometry of the aluminium islands.

  6. CHARACTERIZATION OF 27 MEV PROTON BEAM GENERATED BY TOP-IMPLART LINEAR ACCELERATOR.

    Science.gov (United States)

    De Angelis, C; Ampollini, A; Basile, E; Cisbani, E; Della Monaca, S; Ghio, F; Montereali, R M; Picardi, L; Piccinini, M; Placido, C; Ronsivalle, C; Soriani, A; Strigari, L; Trinca, E; Vadrucci, M

    2018-01-29

    The first proton linear accelerator for tumor therapy based on an actively scanned beam up to the energy of 150 MeV, is under development and construction by ENEA-Frascati, ISS and IFO, under the Italian TOP-IMPLART project. Protons up to the energy of 7 MeV are generated by a customized commercial injector operating at 425 MHz; currently three accelerating modules allow proton delivery with energy up to 27 MeV. Beam homogeneity and reproducibility were studied using a 2D ionizing chamber, EBT3 films, a silicon diode, MOSFETs, LiF crystals and alanine dosimetry systems. Measurements were taken in air with the detectors at ~1 m from the beam line exit window. The maximum energy impinging on the detectors surface was 24.1 MeV, an energy suitable for radiobiological studies. Results showed beam reproducibility within 5% and homogeneity within 4%, on a circular surface of 16 mm in diameter. © The Author(s) 2018. Published by Oxford University Press. All rights reserved. For Permissions, please email: journals.permissions@oup.com.

  7. Corrosion properties of aluminium coatings deposited on sintered NdFeB by ion-beam-assisted deposition

    Energy Technology Data Exchange (ETDEWEB)

    Mao Shoudong; Yang Hengxiu; Li Jinlong; Huang Feng [Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, 519 Zhuangshi Road, Ningbo 315201 (China); Song Zhenlun, E-mail: songzhenlun@nimte.ac.cn [Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, 519 Zhuangshi Road, Ningbo 315201 (China)

    2011-04-15

    Pure Al coatings were deposited by direct current (DC) magnetron sputtering to protect sintered NdFeB magnets. The effects of Ar{sup +} ion-beam-assisted deposition (IBAD) on the structure and the corrosion behaviour of Al coatings were investigated. The Al coating prepared by DC magnetron sputtering with IBAD (IBAD-Al-coating) had fewer voids than the coating without IBAD (Al-coating). The corrosion behaviour of the Al-coated NdFeB specimens was investigated by potentiodynamic polarisation, a neutral salt spray (NSS) test, and electrochemical impedance spectroscopy (EIS). The pitting corrosion of the Al coatings always began at the voids of the grain boundaries. Bombardment by the Ar{sup +} ion-beams effectively improved the corrosion resistance of the IBAD-Al-coating.

  8. The determination of trace oxygen in aluminium and aluminium-silicon alloy by helium-3 activation analysis

    International Nuclear Information System (INIS)

    Vandecasteele, C.; Goethals, P.; Kieffer, R.; Hoste, J.

    1975-01-01

    The determination of oxygen in aluminium and aluminium-silicon alloy by helium-3 activation is studied. The 18 F formed from oxygen is separated by distillation followed by precipitation of leadfluorochloride. The chemical yield is determined by activation in an isotopic neutron source. Concentrations of resp. 27 and 64 ng.g -1 with a precision for a single determination of resp. 30 and 13% are found in 99.5% aluminium and in aluminium-silicon (3%) alloy. (author)

  9. Proceedings of the 1979 workshop on beam current limitations in storage rings, July 16-27, 1979

    International Nuclear Information System (INIS)

    Pellegrini, C.

    1979-01-01

    The Workshop on Beam Current Limitations in Storage Rings was held at Brookhaven National Laboratory from July 16 to 27, 1979. The purpose of this Workshop was to discuss the physical mechanisms limiting the beam current or current density in accelerators or storage rings. Many of these machines are now being built or planned for a variety of applications, such as colliding beam experiments, synchrotron light production, heavy ion beams. This diversity was reflected in the Workshop and in the papers which have been contributed to these Proceedings. The twenty-one papers from the workshop were incorporated individually in the data base

  10. Status of equation of state for aluminium in the light of beam-target interaction experiments at KALIF

    Energy Technology Data Exchange (ETDEWEB)

    Goel, B; Hoebel, W; Marten, H [Forschungszentrum Karlsruhe GmbH Technik und Umwelt (Germany); Vorobev, O Yu; Lomonosov, I V; Gryaznov, V K [Institute of Chemical Physics, Chernogolovka (Russian Federation)

    1997-12-31

    The present paper contains an investigation of the hydrodynamics of thin Aluminum foil accelerated by light-ion beams at KALIF using B{sub {Theta}}-diode. The peak power density in these experiments was 0.15 {+-} 0.05 TW/cm{sup 2}. In an earlier paper the authors have analysed the experimental data using an analytical equation of state. In the present paper the authors show that the state of these accelerated foils is sensitive to the equation of state data and use data based on more profound models. They combine EOS models designed for shock wave modelling describing melting, vaporization and experimental data on compression and unloading of porous matter with those developed for strongly ionised material based on the model of chemical equilibrium. (author). 4 figs., 8 refs.

  11. Aluminium in human sweat.

    Science.gov (United States)

    Minshall, Clare; Nadal, Jodie; Exley, Christopher

    2014-01-01

    It is of burgeoning importance that the human body burden of aluminium is understood and is measured. There are surprisingly few data to describe human excretion of systemic aluminium and almost no reliable data which relate to aluminium in sweat. We have measured the aluminium content of sweat in 20 healthy volunteers following mild exercise. The concentration of aluminium ranged from 329 to 5329μg/L. These data equate to a daily excretion of between 234 and 7192μg aluminium and they strongly suggest that perspiration is the major route of excretion of systemic aluminium in humans. Copyright © 2013 Elsevier GmbH. All rights reserved.

  12. Fundamental experiment for flash removal of aluminum alloy by CO2 laser beam cutting; CO2 laser beam setsudan ni yoru aluminium gokin no ibaritori no kiso jikken

    Energy Technology Data Exchange (ETDEWEB)

    Kataoka, Y.; Tokunaga, T. [University of Industrial Technology, Kanagawa (Japan); Miyazaki, T. [Chiba Institute of Technology, Chiba (Japan)

    1995-08-25

    CO2 laser beam has been applied to cut of the aluminum alloy. Average cut width, roughness of cut surface and average thickness of heat affected zone are investigated as functions of laser power, cutting speed and assist gas pressure. The average cut width increases with laser power, but it does not depend on the cutting speed. The narrowest average cut width obtained is 0.22mm under the conditions of laser power of 900W and cutting speeds from 600 to 1000mm/min. The roughness of cut surface decreases with decreasing cutting speed. The best smoothness of cut surface obtained is 17 {mu}m (Rmax) , when the conditions are 1100W and 600mm/min. The average thickness of heat affected zone decreases with increasing assist gas pressure. CO2 laser beam cutting is applicable to flash removal from aluminum alloy casting. This process is expected to reduce the need of physical labor and to improve the working conditions in the foundry industry. 32 refs., 10 figs., 2 tabs.

  13. Human exposure to aluminium.

    Science.gov (United States)

    Exley, Christopher

    2013-10-01

    Human activities have circumvented the efficient geochemical cycling of aluminium within the lithosphere and therewith opened a door, which was previously only ajar, onto the biotic cycle to instigate and promote the accumulation of aluminium in biota and especially humans. Neither these relatively recent activities nor the entry of aluminium into the living cycle are showing any signs of abating and it is thus now imperative that we understand as fully as possible how humans are exposed to aluminium and the future consequences of a burgeoning exposure and body burden. The aluminium age is upon us and there is now an urgent need to understand how to live safely and effectively with aluminium.

  14. Recent developments in advanced aircraft aluminium alloys

    International Nuclear Information System (INIS)

    Dursun, Tolga; Soutis, Costas

    2014-01-01

    Highlights: • To compete with composites, performance of aluminium alloys should be increased. • Al–Li alloys have higher strength, fracture and fatigue/corrosion resistance. • Improvements of aerospace Al alloys are due to optimised solute content and ratios. • In selecting new materials, there should be no reduction in the level of safety. • The use of hybrid materials could provide additional opportunities for Al alloys. - Abstract: Aluminium alloys have been the primary material for the structural parts of aircraft for more than 80 years because of their well known performance, well established design methods, manufacturing and reliable inspection techniques. Nearly for a decade composites have started to be used more widely in large commercial jet airliners for the fuselage, wing as well as other structural components in place of aluminium alloys due their high specific properties, reduced weight, fatigue performance and corrosion resistance. Although the increased use of composite materials reduced the role of aluminium up to some extent, high strength aluminium alloys remain important in airframe construction. Aluminium is a relatively low cost, light weight metal that can be heat treated and loaded to relatively high level of stresses, and it is one of the most easily produced of the high performance materials, which results in lower manufacturing and maintenance costs. There have been important recent advances in aluminium aircraft alloys that can effectively compete with modern composite materials. This study covers latest developments in enhanced mechanical properties of aluminium alloys, and high performance joining techniques. The mechanical properties on newly developed 2000, 7000 series aluminium alloys and new generation Al–Li alloys are compared with the traditional aluminium alloys. The advantages and disadvantages of the joining methods, laser beam welding and friction stir welding, are also discussed

  15. Serum aluminium levels of workers in the bauxite mines.

    Science.gov (United States)

    de Kom, J F; Dissels, H M; van der Voet, G B; de Wolff, F A

    1997-01-01

    Aluminium is produced from the mineral bauxite. Occupational exposure is reported during the industrial processing of aluminium and is associated with pulmonary and neurotoxicity. However, data on exposure and toxicity of workers in the open bauxite mining industry do not exist. Therefore, a study was performed to explore aluminium exposure in employees involved in this bauxite mining process in a Surinam mine. A group of workers occupationally exposed to aluminium in an open bauxite mine were compared with a group of nonexposed wood processors. Serum aluminium was analyzed using atomic absorption spectrometry Data from the clinical chemistry of the blood and a questionnaire were used to explore determinants for aluminium exposure. No significant difference between serum aluminium in the exposed (4.4 +/- 2.0 micrograms/L, n = 27) and control group (5.1 +/- 1.5 micrograms/L, n = 27) was detected. For the serum concentration of the clinical chemical variables (calcium, citrate, and creatinine), a statistically significant difference was computed (p < or = 0.02) between the exposed and control group. All levels were slightly higher in the exposed group; no statistically significant correlations with serum aluminium were found. In this study, serum aluminium values were in the normal range, no significant difference between the groups could be detected despite long-term occupational exposure.

  16. An aluminium evaporation source for ion plating

    International Nuclear Information System (INIS)

    Walley, P.A.; Cross, K.B.

    1977-01-01

    Ion plating with aluminium is becoming increasingly accepted as a method of anti-corrosion surface passivation, the usual requirements being for a layer between 12 and 50 microns in thickness, (0.0005 to 0.002). The evaporation system described here offers a number of advantages over high power electron beam sources when used for aluminium ion plating. The source consists of a resistively heated, specially shaped, boron nitride-titanium diboride boat and a metering feed system. Its main features are small physical size, soft vacuum compatibility, low power consumption and metered evaporation output. (author)

  17. Aluminium in Infrastructures

    NARCIS (Netherlands)

    Maljaars, J.

    2016-01-01

    Aluminium alloys are used in infrastructures such as pedestrian bridges or parts of it such as handrail. This paper demonstrates that aluminium alloys are in principle also suited for heavy loaded structures, such as decks of traffic bridges and helicopter landing platforms. Recent developments in

  18. Aluminium beverage can recycling

    Energy Technology Data Exchange (ETDEWEB)

    Lewinski, A von

    1985-08-01

    Canned beverages have become a controversial issue in this era of ecological sensitivity. METALL has already discussed the problem of can recycling. The present article discusses the technical aspects of aluminium can recycling. Two further articles will follow on aluminium can recycling in North America and on the results of European pilot projects.

  19. Rows of Dislocation Loops in Aluminium Irradiated by Aluminium Ions

    DEFF Research Database (Denmark)

    Henriksen, L.; Johansen, A.; Koch, J.

    1967-01-01

    Single-crystal aluminium specimens, irradiated with 50-keV aluminium ions, contain dislocation loops that are arranged in regular rows along <110 > directions. ©1967 The American Institute of Physics......Single-crystal aluminium specimens, irradiated with 50-keV aluminium ions, contain dislocation loops that are arranged in regular rows along directions. ©1967 The American Institute of Physics...

  20. 100 years of elementary particles [Beam Line, vol. 27, issue 1, Spring 1997

    Energy Technology Data Exchange (ETDEWEB)

    Pais, Abraham; Weinberg, Steven; Quigg, Chris; Riordan, Michael; Panofsky, Wolfgang K.H.; Trimble, Virginia

    1997-04-01

    This issue of Beam Line commemorates the 100th anniversary of the April 30, 1897 report of the discovery of the electron by J.J. Thomson and the ensuing discovery of other subatomic particles. In the first three articles, theorists Abraham Pais, Steven Weinberg, and Chris Quigg provide their perspectives on the discoveries of elementary particles as well as the implications and future directions resulting from these discoveries. In the following three articles, Michael Riordan, Wolfgang Panofsky, and Virginia Trimble apply our knowledge about elementary particles to high-energy research, electronics technology, and understanding the origin and evolution of our Universe.

  1. 100 years of elementary particles [Beam Line, vol. 27, number 1, Spring 1997

    International Nuclear Information System (INIS)

    Pais, Abraham; Weinberg, Steven; Quigg, Chris; Riordan, Michael; Panofsky, Wolfgang K.H.; Trimble, Virginia

    1997-01-01

    This issue of Beam Line commemorates the 100th anniversary of the April 30, 1897 report of the discovery of the electron by J.J. Thomson and the ensuing discovery of other subatomic particles. In the first three articles, theorists Abraham Pais, Steven Weinberg, and Chris Quigg provide their perspectives on the discoveries of elementary particles as well as the implications and future directions resulting from these discoveries. In the following three articles, Michael Riordan, Wolfgang Panofsky, and Virginia Trimble apply our knowledge about elementary particles to high-energy research, electronics technology, and understanding the origin and evolution of our Universe

  2. Recovery in aluminium

    DEFF Research Database (Denmark)

    Gundlach, Carsten

    2006-01-01

    In the present thesis the development of a unique experimental method for volume characterisation of individual embedded crystallites down to a radius of 150 nm is presented. This method is applied to in-situ studies of recovery in aluminium. The method is an extension of 3DXRD microscopy, an X...... are represented as strings. To identify the strings a combination of a 5D connected component type algorithm and multi-peak fitting was found to be superior. The first use of the method was a study of recovery of a deformed aluminium alloy (AA1050). The aluminium alloy was deformed by cold rolling to a thickness...

  3. Evaluation of aerodynamic forces acting on oscillating cantilever beams based on the study of the damped flexural vibration of aluminium test samples

    Science.gov (United States)

    Egorov, A. G.; Kamalutdinov, A. M.; Nuriev, A. N.

    2018-05-01

    The paper is devoted to study of the aerodynamic forces acting on flat cantilever beams performing flexural vibrations in a viscous fluid. Original method for the force evaluation is presented based on analysis of experimental measurements of a logarithmic decrement of vibrations and relative variation in frequency of duralumin test specimens. The theoretical core of the method is based on the classical theory of bending beam oscillations and quasi-two dimensional model of interaction between a beam and a gas. Using the proposed method, extensive series of experiments for a wide range of oscillations parameters were carried out. The processing of the experimental data allowed to establish the global influence of the aerodynamic effects on beam oscillations and the local force characteristics of each cross-section of the beam in the form of universal functions of dimensionless amplitude and dimensionless frequency of oscillation. The obtained estimates of the drag and added mass forces showed a good correspondence with the available numerical and experimental data practically in the entire range of the investigated parameters.

  4. Volatilisation and oxidation of aluminium scraps fed into incineration furnaces

    International Nuclear Information System (INIS)

    Biganzoli, Laura; Gorla, Leopoldo; Nessi, Simone; Grosso, Mario

    2012-01-01

    Highlights: ► Aluminium packaging partitioning in MSW incineration residues is evaluated. ► The amount of aluminium packaging recoverable from the bottom ashes is evaluated. ► Aluminium packaging oxidation rate in the residues of MSW incineration is evaluated. ► 80% of aluminium cans, 51% of trays and 27% of foils can be recovered from bottom ashes. - Abstract: Ferrous and non-ferrous metal scraps are increasingly recovered from municipal solid waste incineration bottom ash and used in the production of secondary steel and aluminium. However, during the incineration process, metal scraps contained in the waste undergo volatilisation and oxidation processes, which determine a loss of their recoverable mass. The present paper evaluates the behaviour of different types of aluminium packaging materials in a full-scale waste to energy plant during standard operation. Their partitioning and oxidation level in the residues of the incineration process are evaluated, together with the amount of potentially recoverable aluminium. About 80% of post-consumer cans, 51% of trays and 27% of foils can be recovered through an advanced treatment of bottom ash combined with a melting process in the saline furnace for the production of secondary aluminium. The residual amount of aluminium concentrates in the fly ash or in the fine fraction of the bottom ash and its recovery is virtually impossible using the current eddy current separation technology. The average oxidation levels of the aluminium in the residues of the incineration process is equal to 9.2% for cans, 17.4% for trays and 58.8% for foils. The differences between the tested packaging materials are related to their thickness, mechanical strength and to the alloy.

  5. Volatilisation and oxidation of aluminium scraps fed into incineration furnaces

    Energy Technology Data Exchange (ETDEWEB)

    Biganzoli, Laura, E-mail: laura.biganzoli@mail.polimi.it [Politecnico di Milano, Piazza L. Da Vinci 32, 20133 Milano (Italy); Gorla, Leopoldo; Nessi, Simone; Grosso, Mario [Politecnico di Milano, Piazza L. Da Vinci 32, 20133 Milano (Italy)

    2012-12-15

    Highlights: Black-Right-Pointing-Pointer Aluminium packaging partitioning in MSW incineration residues is evaluated. Black-Right-Pointing-Pointer The amount of aluminium packaging recoverable from the bottom ashes is evaluated. Black-Right-Pointing-Pointer Aluminium packaging oxidation rate in the residues of MSW incineration is evaluated. Black-Right-Pointing-Pointer 80% of aluminium cans, 51% of trays and 27% of foils can be recovered from bottom ashes. - Abstract: Ferrous and non-ferrous metal scraps are increasingly recovered from municipal solid waste incineration bottom ash and used in the production of secondary steel and aluminium. However, during the incineration process, metal scraps contained in the waste undergo volatilisation and oxidation processes, which determine a loss of their recoverable mass. The present paper evaluates the behaviour of different types of aluminium packaging materials in a full-scale waste to energy plant during standard operation. Their partitioning and oxidation level in the residues of the incineration process are evaluated, together with the amount of potentially recoverable aluminium. About 80% of post-consumer cans, 51% of trays and 27% of foils can be recovered through an advanced treatment of bottom ash combined with a melting process in the saline furnace for the production of secondary aluminium. The residual amount of aluminium concentrates in the fly ash or in the fine fraction of the bottom ash and its recovery is virtually impossible using the current eddy current separation technology. The average oxidation levels of the aluminium in the residues of the incineration process is equal to 9.2% for cans, 17.4% for trays and 58.8% for foils. The differences between the tested packaging materials are related to their thickness, mechanical strength and to the alloy.

  6. Effects of Process Conditions on the Mechanical Behavior of Aluminium Wrought Alloy EN AW-2219 (AlCu6Mn Additively Manufactured by Laser Beam Melting in Powder Bed

    Directory of Open Access Journals (Sweden)

    Michael Cornelius Hermann Karg

    2017-01-01

    Full Text Available Additive manufacturing is especially suitable for complex-shaped 3D parts with integrated and optimized functionality realized by filigree geometries. Such designs benefit from low safety factors in mechanical layout. This demands ductile materials that reduce stress peaks by predictable plastic deformation instead of failure. Al–Cu wrought alloys are established materials meeting this requirement. Additionally, they provide high specific strengths. As the designation “Wrought Alloys” implies, they are intended for manufacturing by hot or cold working. When cast or welded, they are prone to solidification cracks. Al–Si fillers can alleviate this, but impair ductility. Being closely related to welding, Laser Beam Melting in Powder Bed (LBM of Al–Cu wrought alloys like EN AW-2219 can be considered challenging. In LBM of aluminium alloys, only easily-weldable Al–Si casting alloys have succeeded commercially today. This article discusses the influences of boundary conditions during LBM of EN AW-2219 on sample porosity and tensile test results, supported by metallographic microsections and fractography. Load direction was varied relative to LBM build-up direction. T6 heat treatment was applied to half of the samples. Pronounced anisotropy was observed. Remarkably, elongation at break of T6 specimens loaded along the build-up direction exceeded the values from literature for conventionally manufactured EN AW-2219 by a factor of two.

  7. Silicon Alloying On Aluminium Based Alloy Surface

    International Nuclear Information System (INIS)

    Suryanto

    2002-01-01

    Silicon alloying on surface of aluminium based alloy was carried out using electron beam. This is performed in order to enhance tribological properties of the alloy. Silicon is considered most important alloying element in aluminium alloy, particularly for tribological components. Prior to silicon alloying. aluminium substrate were painted with binder and silicon powder and dried in a furnace. Silicon alloying were carried out in a vacuum chamber. The Silicon alloyed materials were assessed using some techniques. The results show that silicon alloying formed a composite metal-non metal system in which silicon particles are dispersed in the alloyed layer. Silicon content in the alloyed layer is about 40% while in other place is only 10.5 %. The hardness of layer changes significantly. The wear properties of the alloying alloys increase. Silicon surface alloying also reduced the coefficient of friction for sliding against a hardened steel counter face, which could otherwise be higher because of the strong adhesion of aluminium to steel. The hardness of the silicon surface alloyed material dropped when it underwent a heating cycle similar to the ion coating process. Hence, silicon alloying is not a suitable choice for use as an intermediate layer for duplex treatment

  8. Aluminium incorporation in AlxGa1-xN/GaN heterostructures: A comparative study by ion beam analysis and X-ray diffraction

    International Nuclear Information System (INIS)

    Redondo-Cubero, A.; Gago, R.; Gonzalez-Posada, F.; Kreissig, U.; Di Forte Poisson, M.-A.; Brana, A.F.; Munoz, E.

    2008-01-01

    The Al content in Al x Ga 1-x N/GaN heterostructures has been determined by X-ray diffraction (XRD) and contrasted with absolute measurements from ion beam analysis (IBA) methods. For this purpose, samples with 0.1 0.2. The assessment of Al incorporation by XRD is quite reliable regarding the average value along the sample thickness. However, XRD analysis tends to overestimate the Al fraction at low contents, which is attributed to the presence of strain within the layer. For the highest Al incorporation, IBA detects a certain Al in-depth compositional profile that should be considered for better XRD data analysis

  9. Raw materials for aluminium production

    International Nuclear Information System (INIS)

    Galushkin, N.V.

    1995-01-01

    This chapter of monograph is devoted to to raw materials which used in aluminium production. Therefore, the using of alumina, and fluoride salts in aluminium production was considered. The physical properties of alumina were studied.

  10. Fatal aluminium phosphide poisoning

    Directory of Open Access Journals (Sweden)

    Meena Mahesh Chand

    2015-06-01

    Full Text Available Aluminium phosphide (AlP is a cheap solid fumigant and a highly toxic pesticide which is commonly used for grain preservation. AlP has currently aroused interest with a rising number of cases in the past four decades due to increased use for agricultural and non-agricultural purposes. Its easy availability in the markets has increased also its misuse for committing suicide. Phosphine inhibits cellular oxygen utilization and can induce lipid peroxidation. Poisoning with AlP has often occurred in attempts to commit suicide, and that more often in adults than in teenagers. This is a case of suicidal consumption of aluminium phosphide by a 32-year-old young medical anesthetist. Toxicological analyses detected aluminium phosphide. We believe that free access of celphos tablets in grain markets should be prohibited by law.

  11. Constructions of aluminium electrolytic cells

    International Nuclear Information System (INIS)

    Galushkin, N.V.

    1995-01-01

    This chapter of monograph is devoted to constructions of aluminium electrolytic cells. Therefore, the general characteristic and classification of aluminium electrolytic cells was considered. The anode and cathode structure was studied. The lining of cathode casing, the process of collection of anode gases, electrolytic cell cover, and electrical insulation was studied as well. The installation and dismantling of aluminium electrolytic cells was described.

  12. Absorption of aluminium X-ray lines in a laser created gold plasma

    International Nuclear Information System (INIS)

    Combis, P.; Busquet, M.; Louis-Jacquet, M.

    1986-04-01

    We have studied the absorption of aluminium X-ray lines through a gold plasma by focusing a high intensity laser-beam onto a specific target. Absorption in the wavelength range of 5 to 7 A has been evidenced and measured for Aluminium resonance lines

  13. Fragmentation and direct transfer reactions for 40Ar incident beam on 27Al target at 1760 MeV

    International Nuclear Information System (INIS)

    Cisse, Ousmane

    1985-01-01

    Peripheral collision studies performed with 40 Ar projectiles at 44 MeV/A and 27 Al target show that both fragmentation and transfer reactions can be discerned in this type of interaction. The experimental observation of fragments with masses charges and velocities close to those of the incident beam are the signature of transfer reactions and a detailed analysis of the energy spectra of such fragments has been carried out and interpreted in terms of a direct diffraction transfer model. On the other hand, for large mass transfer reactions, abrasion is the suitable mechanism. Inclusive fragment measurement together with the appropriate residual nuclei-fragment coincidence results then provides experimental data in good agreement with the theoretical predictions obtained from a participant spectator model. These investigations also indicate that the separation energies of the participant from the spectator nucleus, at least within the framework of the above model, can be interpreted in terms of a friction force which becomes more efficient as the projectile energy decreases. (author) [fr

  14. Fire exposed aluminium structures

    NARCIS (Netherlands)

    Maljaars, J.; Fellinger, J.E.J.; Soetens, F.

    2005-01-01

    Material properties and mechanical response models for fire design of steel structures are based on extensive research and experience. Contrarily, the behaviour of aluminium load bearing structures exposed to fire is relatively unexplored. This article gives an overview of physical and mechanical

  15. Activation Analysis of Aluminium

    Energy Technology Data Exchange (ETDEWEB)

    Brune, Dag

    1961-01-15

    An analysis of pure aluminium alloyed with magnesium was per- formed by means of gamma spectrometry , Chemical separations were not employed. The isotopes to be determined were obtained in conditions of optimum activity by suitably choosing the time of irradiation and decay. The following elements were detected and measured quantitatively: Iron, zinc, copper, gallium, manganese, chromium, scandium and hafnium.

  16. Sintered aluminium powders

    International Nuclear Information System (INIS)

    Stepanova, M.G.; Matveev, B.I.

    1974-01-01

    The mechanical and physical properties of aluminium powder alloys and the various methods employed to produce them are considered. Data are given on the hardening of the alloys SAP and SPAK-4, as well as the powder-alloy system Al-Cr-Zr. (L.M.)

  17. Characterization of nitrogen-ion-implanted aluminium

    International Nuclear Information System (INIS)

    Rauschenbach, B.; Breuer, K.; Leonhardt, G.

    1990-01-01

    Aluminium has been implanted with nitrogen ions at different temperatures. The implanted samples have been characterized by Auger electron spectroscopy (AES), X-ray photoelectron spectroscopy (XPS) and electron energy-loss spectroscopy (EELS). Deconvolution procedures are needed to separate the influence of the ion sputter profiling by AES and XPS from the nitrogen-ion-beam-induced effects. The chemical state of Al, N, O and C was identified by deconvolution of the measured spectra. In general, there were double-peak structures observed for N 1s and O 1s, identified as contributions from nitrides and weakly bound nitrogen, and oxides and weakly bound oxygen, respectively. Auger analysis confirms the influence of the nitrogen ion fluence on the shape of the concentration distribution. The influence of temperature on the chemical state of implanted aluminium and on the concentration distribution is discussed. (orig.)

  18. Toughness study of an under matched welded joint: application to the mechanical integrity of the electron beam welded joint of 6016-T6 aluminium alloy

    International Nuclear Information System (INIS)

    Rekik, Wissal

    2016-01-01

    For the demonstration of the integrity of the most sensitive nuclear components, conventional defects, as cracks for example, must be considered within the design step as required by the nuclear safety authority. This phase is particularly crucial for dimensioning of welded structures. To ensure a conservative prediction, the position of the initial crack within the welded joint must be the most detrimental in fracture behavior. Commonly used analyzes consider homogeneous structure with the behavior of the base metal of the welded joint, considered as the weakest metallurgical zone in the case of an overmatched weld. In contrast, similar analysis is not conservative in case of under matched weld. The thesis contributes by the development of an experimental and numerical methodology allowing the identification of the detrimental metallurgical zone in fracture behavior of an under matched welded joint. The methodology proposed is applied to an electron beam welded joint on al 6061-T6. To reach this goal, the gradient of the mechanical behavior along the welded joint was first identified. This is particularly interesting to conduct an advanced analysis based on a multi material approach. In a second step, the fracture behavior of the welded joint was studied on CT specimen. The transferability of the J integral at initiation was approved on another geometry: this represents an important foundation for the transferability assumption to structure. Finally, a numerical analysis on full scale tube was developed. Residual welding stresses and structural effects were considered. The results demonstrate that the heat affected zone located at 13 mm from the middle of the welded joint is the most detrimental zone for fracture analysis. This contradicts the conventional methods conducted on fracture analysis which consider a conventional defect within the fusion zone. (author) [fr

  19. A study on the role of diboride in the heterogeneous nucleation of aluminium

    International Nuclear Information System (INIS)

    Suarez, O. M.

    2004-01-01

    The intangible role of titanium and aluminium diboride in the nucleation of aluminium was re-examined. Two different techniques, complemented with scanning electron microscopy, allowed determining the stability of the diboride in the presence of titanium tri aluminides and liquid aluminium phases. Through rapid scintillated quenching the high temperature diboride were retained and studied. Then, in a diffusion couple, the reactivity of such diboride was tested in contact with pure titanium tri aluminide. It is proposed that a ternary diboride acts as the main catalytic particle in the crystallization of aluminium alloys with refined grains. (Author) 27 refs

  20. RESPONSE OF PHENOLIC METABOLISM INDUCED BY ALUMINIUM TOXICITY IN FAGOPYRUM ESCULENTUM MOENCH. PLANTS.

    Science.gov (United States)

    Smirnov, O E; Kosyan, A M; Kosyk, O I; Taran, N Yu

    2015-01-01

    Buckwheat genus (Fagopyrum Mill.) is one of the aluminium tolerant taxonomic units of plants. The aim of the study was an evaluation of the aluminium (50 μM effect on phenolic accumulation in various parts of buckwheat plants (Fagopyrum esculentum Moench). Detection of increasing of total phenolic content, changes in flavonoid and anthocyanin content and phenylalanine ammonia-lyase activity (PAL) were revealed over a period of 10 days of exposure to aluminium. The most significant effects of aluminium treatment on phenolic compounds accumulation were total phenolic content increasing (by 27.2%) and PAL activity rising by 2.5 times observed in leaves tissues. Received data could be helpful to understand the aluminium tolerance principles and relationships of phenolic compounds to aluminium phytotoxicity.

  1. Corrosion behaviour in saline environments of single-layer titanium and aluminium coatings, and of Ti/Al alternated multi-layers elaborated by a multi-beam PVD technique

    International Nuclear Information System (INIS)

    Merati, Abdenacer

    1994-01-01

    This research thesis reports the characterization of anti-corrosion titanium and aluminium coatings deposited on a 35CD4 steel under the form of mono-metallic layers or alternated Ti/Al multi-layers, and obtained by a multibeam PVD technique. The influence of different parameters is studied: single-layer thickness (5, 15 or 30 micro-metres), multi-layer distribution (5 to 6) and substrate (smooth or threaded). Layer nature and microstructure are studied by optical microscopy and scanning electron microscopy (SEM), as well as corrosion toughness in aqueous saline environments. Coated threaded samples have been studied after tightening tests. It appears that titanium layers are denser and more uniform than aluminium layers, and that multi-layer coatings provide a better protection than single-layer coatings. The best behaviour is obtained when titanium is in contact with steel, and aluminium is the outer layer in contact with the corroding environment [fr

  2. Structure-property investigations on a laser beam welded dissimilar joint of aluminium AA6056 and titanium Ti6Al4V for aeronautical applications Part I: Local gradients in microstructure, hardness and strength

    Energy Technology Data Exchange (ETDEWEB)

    Horstmann, M.; Ventzke, V.; Petrovski, B.; Kocak, M. [GKSS Research Centre Geesthacht (Germany). Institute of Materials Research, Materials Mechanics; Kocik, R.; Tempus, G. [AIRBUS Deutschland GmbH, Metal Technology, Bremen (Germany); Vaidya, W.V.

    2009-08-15

    Sheets of AA6056 and Ti6Al4V were butt-joined by inserting the Ti-sheet into the profiled Al-sheet and by melting the Al-alloy alone using a split beam Nd:YAG laser. To study microstructural effects on properties, the Al-alloy was used in two tempers; T4 followed by post weld heat treatment T6, and in T6 followed by a defined duration of natural ageing at room temperature. As a basic step for fatigue and fracture investigations, local gradients in properties of this dissimilar joint are investigated using microscopy, hardness and tensile tests. Possible sites, from which fracture may initiate, have been then identified. All property changes are found to confine to the aluminium side. An intermetallic layer, although very thin, is found to form on the interface. The changeovers, firstly between the fusion zone and the heat affected zone and secondly between the heat affected zone and the base material, are found to be associated with changes in microstructure, hardness and strength. These are identified as the possible critical sites in addition to the interface. (Abstract Copyright [2009], Wiley Periodicals, Inc.) [German] Durch eine spezielle Stossvorbereitung wurden laserstrahlgeschweisster Mischverbindungen aus den Blechwerkstoffen AA6056 und Ti6Al4V hergestellt und zwar ohne die Verwendung von Zusatzwerkstoffen. Die grosse Differenz der Schmelztemperaturen erlaubt das selektive Erschmelzen des Aluminiumwerkstoffs, der wieder um den Titanwerkstoff benetzt, sodass es zur Ausbildung einer mechanisch-stabilen und tragfaehigen Verbindung kommt. Die Al-Legierung wurde in den Waermebehandlungszustaenden T4 und T6 verschweisst, um den mikrostrukturellen Einfluss auf die Eigenschaften der Verbindungen untersuchen zu koennen. Die Prozessfolgen sahen vor, dass beim Schweissen im Zustand T4 eine Warmauslagerung, beim Schweissen im Zustand T6 eine Kaltauslagerung definierter Dauer folgte. Die Charakterisierung lokaler Eigenschaftsgradienten hinsichtlich Gefuege, Mikrohaerte

  3. Laser welding of aluminium alloys

    OpenAIRE

    Forsman, Tomas

    2000-01-01

    This thesis treats laser welding of aluminium alloys from a practical perspective with elements of mathematical analysis. The theoretical work has in all cases been verified experimentally. The aluminium alloys studied are from the 5xxx and 6xxx groups which are common for example in the automotive industry. Aluminium has many unique physical properties. The properties which more than others have been shown to influence the welding process is its high reflection, high thermal conductivity, lo...

  4. Chapter 1. Economic aspects of aluminium production

    International Nuclear Information System (INIS)

    Yanko, E.A.; Kabirov, Sh.O.; Safiev, Kh.; Azizov, B.S.; Mirpochaev, Kh.A.

    2011-01-01

    This article is devoted to economic aspects of aluminium production. Therefore, the perspectives of development of aluminium production, the base components of aluminium cost and economic security of enterprise are considered in this chapter.

  5. Roll bonding of strained aluminium

    DEFF Research Database (Denmark)

    Staun, Jakob M.

    2003-01-01

    This report investigates roll bonding of pre-strained (å ~ 4) aluminium sheets to produce high strain material from high purity aluminium (99.996%) and commercial pure aluminium (99.6%). The degree of bonding is investigated by optical microscopy and ultrasonic scanning. Under the right...... of the cross rolled volume fraction is found. To further asses this effect, and the anisotropy, it is necessary to acquire knowledge about both texture and microstructure, e.g. by TEM. Roll bonding of pre-strained aluminium is found to be a possible alternative to ARB in the quest for ultra-fine grained...

  6. Calculation of electron transmission through aluminium foil

    International Nuclear Information System (INIS)

    Abroyan, M.A.; Mel'ker, A.I.; Mikhajlin, A.I.; Sirotinkin, V.V.; Tokmakov, I.L.

    1987-01-01

    Calculated by Monte Carlo method energy and angular distributions of electrons transmitted through aluminium foil with 50 μm thickness are presented. 200-500 electron energy ranges and angles of electron incidence on foil from 0 to 40 deg C are considered. That allows to use results for more universal accelerator group, for example, for accelerators with scanning beam used in industry. The received values of angular and energy characteristics allow to increase essentially estimation accuracy of accelerator extraction devices and dose distribution on irradiating item

  7. CERN: very large magnet with aluminium winding

    Energy Technology Data Exchange (ETDEWEB)

    Wittgenstein, F.A.

    1984-10-25

    The construction of an octagonal solenoid from trapezoidal plates of Al, 6m long and 6cm thick, assembled by electron beam welding, for installation in a laboratory 50m underground is described. The objective is to create a field of 0.5T in a volume of 1000m/sup 3/ for the L3 particle detector of the LEP accelerator project. Principal dimensions and weights of the structure are given and its three stages of implementation are described, with reference to the contributions from the Swiss aluminium industry.

  8. Fatigue test on aluminium bridges

    NARCIS (Netherlands)

    Maljaars, J.; Soetens, F.; Straalen, van IJ.J.

    2005-01-01

    Traffic bridges are subjected to variable loads and should therefore be checked on fatigue. Especially low weight materials, like aluminium, are sensitive to fatigue, because the variable load is a substantial part of the total load. This paper shows the structural design of an aluminium bridge

  9. Advanced shipbuilding in aluminium

    International Nuclear Information System (INIS)

    Larsson, H.; Svensson, L.E.; Karlsson, L.

    1997-01-01

    The applicability of two different welding techniques for welding ships in aluminium is discussed. Conventional MIG welding and the recently developed Friction Super Stir Welding (FSSW) are compared concerning weld metal microstructures and mechanical properties. Results from testing of FSSW welds are also presented. It was observed that the grain size was smaller in FSSW welds are also presented. It was observed that the grain size was smaller in FSSW welds than in MIG welds whereas precipitates generally were larger in FSSW welds. The two methods produced welds with comparable mechanical properties. Good fatigue behaviour was obtained for FSSW welds. Advantages of the welding methods are also discussed. (Author) 7 refs

  10. Potentiometric determination of the 'formal' hydrolysis ratio of aluminium species in aqueous solutions

    International Nuclear Information System (INIS)

    Fournier, Agathe C.; Shafran, Kirill L.; Perry, Carole C.

    2008-01-01

    The 'formal' hydrolysis ratio (h = C(OH - ) added /C(Al) total ) of hydrolysed aluminium-ions is an important parameter required for the exhaustive and quantitative speciation-fractionation of aluminium in aqueous solutions. This paper describes a potentiometric method for determination of the formal hydrolysis ratio based on an automated alkaline titration procedure. The method uses the point of precipitation of aluminium hydroxide as a reference (h = 3.0) in order to calculate the initial formal hydrolysis ratio of hydrolysed aluminium-ion solutions. Several solutions of pure hydrolytic species including aluminium monomers (AlCl 3 ), Al 13 polynuclear cluster ([Al 13 O 4 (OH) 24 (H 2 O) 12 ] 7+ ), Al 30 polynuclear cluster ([Al 30 O 8 (OH) 56 (H 2 O) 26 ] 18+ ) and a suspension of nanoparticulate aluminium hydroxide have been used as 'reference standards' to validate the proposed potentiometric method. Other important variables in the potentiometric determination of the hydrolysis ratio have also been optimised including the concentration of aluminium and the type and strength of alkali (Trizma-base, NH 3 , NaHCO 3 , Na 2 CO 3 and KOH). The results of the potentiometric analysis have been cross-verified by quantitative 27 Al solution nuclear magnetic resonance ( 27 Al NMR) measurements. The 'formal' hydrolysis ratio of a commercial basic aluminium chloride has been measured as an example of a practical application of the developed technique

  11. Technical aspects of X-ray micro-computed tomography. Initial experience of 27-μm resolution using feldkamp cone-beam reconstruction

    International Nuclear Information System (INIS)

    Yamamoto, Shuji; Suzuki, Masahiro; Kohara, Kazushi; Iinuma, Gen; Moriyama, Noriyuki

    2007-01-01

    The objective of this study was to introduce the technical utility of micro-computed tomography (CT) with 27-μm resolution by cone-beam CT algorithm. Whole-body micro-CT scans were performed to honeybee. Two- and three-dimensional image analyses were performed by originally developed and available open-source software for acquired images. The original contribution of this work is to describe the technical characteristics of the X-ray micro-CT system, keeping a small experimental insect in a unique condition. Micro-CT may be used as a rapid prototyping tool to research and understand the high-resolution system with Feldkamp cone-beam reconstruction. (author)

  12. Recycling of aluminium swarf by direct incorporation in aluminium melts

    OpenAIRE

    Puga, Hélder; Barbosa, J.; Soares, Delfim; Silva, Filipe Samuel; Ribeiro, Carlos Silva

    2009-01-01

    The purpose of this work was to recover a standard AlSi12Cu1 alloy from machining chips inside the foundry plant, by using an environmentally friend technique to produce cast ingots with characteristics similar to those of the commercially available 2nd melt raw material. The recyclability of aluminium swarf using different melting techniques and the influence of chips preparation in the aluminium alloy recovery rate and dross production was experimentally studied and evaluated...

  13. Aluminium, gallium, indium and thallium

    International Nuclear Information System (INIS)

    Brown, Paul L.; Ekberg, Christian

    2016-01-01

    Aluminium can exist in a number of oxyhydroxide mineral phases including corundum, diaspore, boehmite and gibbsite. The stability constants at zero ionic strength reported for Al(OH) 3 (aq) vary linearly with respect to the inverse of absolute temperature. A full suite of thermodynamic parameters is available for all aluminium phases and hydrolysis species. Gallium hydrolyses to a greater extent than aluminium, with the onset of hydrolysis reactions occurring just above a pHof 1. In fact, even though aluminium has the smallest ionic radius of this series of metals, it has the weakest hydrolysis species and oxide/hydroxide phases.This is due to the presence of stabilising d-orbitals in the heavier metals, gallium, indium and thallium(III). There are few available data for the stability constants of indium(III) hydrolysis species. Of those that are available, the range in the proposed stability constants covers many orders of magnitude.

  14. Configuration and mobility of hydrogen implanted in aluminium

    International Nuclear Information System (INIS)

    Bugeat, J.P.; Chami, A.C.; Ligeon, E.

    1976-01-01

    Localization methods through channeling and nuclear reaction analysis using low energy ion beam were applied to the study of deuterium and hydrogen implanted in aluminium single crystals. It was shown that implanted hydrogen occupies a tetrahedral site in the lattice as far as the implantation temperature is lower than 175K. This fact is interpreted by considering an interaction between hydrogen and monovacancies created during the implantation [fr

  15. Alloys of uranium and aluminium with low aluminium content

    International Nuclear Information System (INIS)

    Cabane, G.; Englander, M.; Lehmann, J.

    1955-01-01

    Uranium, as obtained after spinning in phase γ, presents an heterogeneous structure with large size grains. The anisotropic structure of the metal leads to an important buckling and surface distortion of the fuel slug which is incompatible with its tubular cladding for nuclear fuel uses. Different treatments have been made to obtain an isotropic structure presenting high thermal stability (laminating, hammering and spinning in phase α) without success. Alloys of uranium and aluminium with low aluminium content present important advantage in respect of non allied uranium. The introduction of aluminium in the form of intermetallic compound (UAl 2 ) gives a better resistance to thermal fatigue. Alloys obtained from raw casting present an improved buckling and surface distortion in respect of pure uranium. This improvement is obtained with uranium containing between 0,15 and 0,5 % of aluminium. An even more improvement in thermal stability is obtained by thermal treatments of these alloys. These new characteristics are explained by the fine dispersion of the UAl 2 particles in uranium. The results after treatments obtained from an alloy slug containing 0,4 % of aluminium show no buckling or surface distortion and no elongation. (M.P.)

  16. Dispersion strengthening of aluminium-aluminium-oxide products

    DEFF Research Database (Denmark)

    Hansen, Niels

    1970-01-01

    The true stress-true strain curves at room temperature and at 400°C were determined for various types of aluminium-aluminium-oxide products containing from 0.2 to 4.7 weight per cent of aluminium oxide. The effect of particles on the initial flow stress and the flow stress for 0.2% offset at room...... temperature and at 400°C is in agreement with Orowan's theory. The increase in flow stress at room temperature for strain values below 3 per cent was related to the plastic strain by the equation σ-σoy=k1ε 1/2, where σoy is the initial flow stress and where k1 increases for increasing volume fraction...... and decreasing particle size of the dispersed particles. A general expression for k1 was derived for the relationship between the dislocation density and the strain in dispersion-strengthened products...

  17. Alloys of uranium and aluminium with low aluminium content; Alliages uranium-aluminium a faible teneur en aluminium

    Energy Technology Data Exchange (ETDEWEB)

    Cabane, G; Englander, M; Lehmann, J [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1955-07-01

    Uranium, as obtained after spinning in phase {gamma}, presents an heterogeneous structure with large size grains. The anisotropic structure of the metal leads to an important buckling and surface distortion of the fuel slug which is incompatible with its tubular cladding for nuclear fuel uses. Different treatments have been made to obtain an isotropic structure presenting high thermal stability (laminating, hammering and spinning in phase {alpha}) without success. Alloys of uranium and aluminium with low aluminium content present important advantage in respect of non allied uranium. The introduction of aluminium in the form of intermetallic compound (UAl{sub 2}) gives a better resistance to thermal fatigue. Alloys obtained from raw casting present an improved buckling and surface distortion in respect of pure uranium. This improvement is obtained with uranium containing between 0,15 and 0,5 % of aluminium. An even more improvement in thermal stability is obtained by thermal treatments of these alloys. These new characteristics are explained by the fine dispersion of the UAl{sub 2} particles in uranium. The results after treatments obtained from an alloy slug containing 0,4 % of aluminium show no buckling or surface distortion and no elongation. (M.P.)

  18. Determination of Aluminium Content in Aluminium Hydroxide Formulation by FT-NIR Transmittance Spectroscopy

    DEFF Research Database (Denmark)

    Lai, Xuxin; Zheng, Yiwu; Søndergaard, Ib

    2007-01-01

    A method for determining the aluminium content of an aluminium hydroxide suspension using near infrared (NIR) transmittance spectroscopy has been developed. Inductively coupled plasma-atomic emission spectroscopy (ICP-AES) was used as reference method. The factors influencing the NIR analysis...... aluminium content in aluminium hydroxide suspension. (c) 2007 Elsevier Ltd. All rights reserved....

  19. Synthesis and properties of bimetallic aluminium alkoxides

    International Nuclear Information System (INIS)

    Vyshinskaya, K.I.; Vasil'ev, G.A.; Vishnyakova, T.A.

    1997-01-01

    A single stage method of aluminium bimetallic alkoxide synthesis, which consists in activated aluminium reaction with metal salts in the relevant alcohols, has been developed. Properties of the compounds prepared are described

  20. Preparation of aluminium lakes by electrocoagulation

    OpenAIRE

    Prapai Pradabkham

    2008-01-01

    Aluminium lakes have been prepared by electrocoagulation employing aluminium as electrodes. The electrocoagulation is conducted in an aqueous alcoholic solution and is completed within one hour. The dye content in the lake ranges approximately between 4-32%.

  1. Effect of hydrogen on aluminium and aluminium alloys: A review

    DEFF Research Database (Denmark)

    Ambat, Rajan; Dwarakadasa, E.S.

    1996-01-01

    Susceptibility of aluminium and its alloys towards hydrogen embrittlement has been well established. Still a lot of confusion exists on the question of transport of hydrogen and its possible role in stress corrosion cracking. This paper reviews some of the fundamental properties of hydrogen...... in aluminium and its alloys and its effect on mechanical properties. The importance of hydrogen embrittlement over anodic dissolution to explain the stress corrosion cracking mechanism of these alloys is also examined in considerable detail. The various experimental findings concerning the link between...

  2. Aluminium hydro(oxide)–based (AO) adsorbent for defluoridation of ...

    African Journals Online (AJOL)

    High resolution 27Al Magic Angle Spinning Nuclear Magnetic Resonance (27Al MAS NMR) spectra of AO, AA, and PB were recorded, to analyse the coordination geometry of solid Al species and the results showed that aluminium is coordinated octahedrally and tetrahedrally in all cases. Regeneration experiments showed ...

  3. Chapter 2. Theoretical aspects of aluminium production

    International Nuclear Information System (INIS)

    Yanko, E.A.; Kabirov, Sh.O.; Safiev, Kh.; Azizov, B.S.; Mirpochaev, Kh.A.

    2011-01-01

    This article is devoted to theoretical aspects of aluminium production. Thus, the electrochemistry of electrolysis process, calculation of base industrial indicators of aluminium electrolytic cell, and processes occurring on anode and cathode were considered. Factors, which increase the current output and electrolytic cell productivity were studied. The side effects, including anode effect, sodium extraction on cathode, aluminium dissolution in the electrolyte, aluminium carbide formation, and influence of admixtures in the electrolyte were studied as well.

  4. Design and analysis of aluminium brdiges

    NARCIS (Netherlands)

    Soetens, F.; Straalen, IJ.J. van

    2004-01-01

    Applications of aluminium have grown considerably in building and civil engineering the last decade, which is due to various aspects: light weight, durability and maintenance, use of extrusions. The paper starts with a short history of aluminium bridges and then focuses on aluminium bridges in the

  5. A reliability based stress-life evaluation of aluminium-graphite particulate composites

    International Nuclear Information System (INIS)

    Achutha, M.V.; Sridhara, B.K.; Abdul Budan, D.

    2008-01-01

    Fatigue tests were conducted on sand cast aluminium-graphite composite specimens on Rotating Beam Fatigue Testing Machine with three different stress levels. Aluminium-graphite (LM 25-5% graphite) composite was processed by closed mould sand casting method. Three-stress level fatigue test program was planned for carrying out fatigue experiments. Three different stress levels selected for fatigue experiments were a fraction of ultimate tensile strength. Statistical design of fatigue experiments was carried out to determine the sample size at each stress level. Experimental results are presented in the form of stress-life (S-N) curves and reliability-stress-life (R-S-N) curves, which are helpful for designers. The S-N curve of the aluminium-graphite composite was compared with its matrix alloy LM 25. Comparison revealed that the fatigue behaviour of the aluminium-graphite composite is superior to that of the matrix alloy

  6. Hot workability of aluminium alloys

    International Nuclear Information System (INIS)

    Yoo, Yeon Chul; Oh, Kyung Jin

    1986-01-01

    Hot Workability of aluminium alloys, 2024, 6061 and 7075, has been studied by hot torsion tests at temperatures from 320 to 515 deg C and at strain rates from 1.26 x 10 -3 to 5.71 x 10 -3 sec -1 . Hot working condition of these aluminium alloys was determined quantitatively from the constitutive equations obtained from flow stress curves in torsion. Experimental data of the logarith of the Zener-Hollomonn parameter showed good linear relationships to the logarith of sinh(ασ-bar)

  7. Developments in the US aluminium recycling industry

    Energy Technology Data Exchange (ETDEWEB)

    Bolling, R N

    1983-06-01

    In the USA scrap recovery of aluminium has gained in importance since the war. Today its amounts to about 32% of total supply. On the other hand primary production in the US seems to have hardly any expansion possibilities. The development of the aluminium beverage can is the clearest example for recycling growth. The increased use of aluminium in passenger cars has led to very close technical and local relations of aluminium foundries and secondary smelters. The changing nature of the aluminium business caused by the growth of recycling should be recognized and made use of.

  8. The prophylactic reduction of aluminium intake.

    Science.gov (United States)

    Lione, A

    1983-02-01

    The use of modern analytical methods has demonstrated that aluminium salts can be absorbed from the gut and concentrated in various human tissues, including bone, the parathyroids and brain. The neurotoxicity of aluminium has been extensively characterized in rabbits and cats, and high concentrations of aluminium have been detected in the brain tissue of patients with Alzheimer's disease. Various reports have suggested that high aluminium intakes may be harmful to some patients with bone disease or renal impairment. Fatal aluminium-induced neuropathies have been reported in patients on renal dialysis. Since there are no demonstrable consequences of aluminium deprivation, the prophylactic reduction of aluminium intake by many patients would appear prudent. In this report, the major sources of aluminium in foods and non-prescription drugs are summarized and alternative products are described. The most common foods that contain substantial amounts of aluminium-containing additives include some processed cheeses, baking powders, cake mixes, frozen doughs, pancake mixes, self-raising flours and pickled vegetables. The aluminium-containing non-prescription drugs include some antacids, buffered aspirins, antidiarrhoeal products, douches and haemorrhoidal medications. The advisability of recommending a low aluminium diet for geriatric patients is discussed in detail.

  9. Aluminium and energy. An interview

    Energy Technology Data Exchange (ETDEWEB)

    Meyer, E R

    1978-06-01

    The interview between METALL and the president of Aluswuisse refers mainly to aspects of energy and deals more closely with the questions whether western Europe in view of relatively high prices for electricity is still competitive and which part can be played by aluminium in overcoming the energy crisis.

  10. Recovery mechanisms in nanostructured aluminium

    DEFF Research Database (Denmark)

    Yu, Tianbo; Hansen, Niels; Huang, Xiaoxu

    2012-01-01

    Commercial purity aluminium (99.5%) has been cold rolled to a true strain of 5.5 (99.6% reduction in thickness). The material is very strong but low temperature recovery may be a limiting factor. This has been investigated by isothermal annealing treatments in the temperature range 5–100C. Hardness...

  11. Dynamical study of liquid aluminium

    International Nuclear Information System (INIS)

    Dubey, G.S.; Chaturvedi, D.K.

    1979-09-01

    Recent molecular dynamics data of Ebbsjoe et al. in liquid aluminium have been analysed through the memory function formalism. Two forms of the memory functions which have correct asymptotic limit at large wavenumbers but accounts for interatomic correlations in a different manner are considered. The results for ω 2 s(q, ω) obtained from both models are compared with experimental data. (author)

  12. Effect of Bio char on Plant Growth and Aluminium Form of Soil under Aluminium Stress

    Science.gov (United States)

    Qian, Lianwen; Li, Qingbiao; Sun, Jingwei; Feng, Ying

    2018-01-01

    Aluminium-enriched acid red soils in South China easily cause aluminium toxicity to plants, but biochip can improve soils and eliminate soil contaminations. In this project, biochip was used in potted plant control test to study the effect of biochip on plant growth in soil under acid aluminium stress and the migration and conversion of aluminium in plant-soil system. The fin dings show that the application of biochip increases the pH value of soil under aluminium stress significantly, changes the existing form of aluminium ion in soil, reduces the plants’ absorption of aluminium, and alleviates the aluminium toxicity to plants, but too much biochip may inhibit the growth of plants. In this case, further study should be carried out as regards the volume and way of biochip input in practical applications as well as the timeliness of aluminium toxicity removal.

  13. Friction Welding of Aluminium and Aluminium Alloys with Steel

    Directory of Open Access Journals (Sweden)

    Andrzej Ambroziak

    2014-01-01

    Full Text Available The paper presents our actual knowledge and experience in joining dissimilar materials with the use of friction welding method. The joints of aluminium and aluminium alloys with the different types of steel were studied. The structural effects occurring during the welding process were described. The mechanical properties using, for example, (i microhardness measurements, (ii tensile tests, (iii bending tests, and (iv shearing tests were determined. In order to obtain high-quality joints the influence of different configurations of the process such as (i changing the geometry of bonding surface, (ii using the interlayer, or (iii heat treatment was analyzed. Finally, the issues related to the selection of optimal parameters of friction welding process were also investigated.

  14. Bumblebee pupae contain high levels of aluminium.

    Science.gov (United States)

    Exley, Christopher; Rotheray, Ellen; Goulson, David

    2015-01-01

    The causes of declines in bees and other pollinators remains an on-going debate. While recent attention has focussed upon pesticides, other environmental pollutants have largely been ignored. Aluminium is the most significant environmental contaminant of recent times and we speculated that it could be a factor in pollinator decline. Herein we have measured the content of aluminium in bumblebee pupae taken from naturally foraging colonies in the UK. Individual pupae were acid-digested in a microwave oven and their aluminium content determined using transversely heated graphite furnace atomic absorption spectrometry. Pupae were heavily contaminated with aluminium giving values between 13.4 and 193.4 μg/g dry wt. and a mean (SD) value of 51.0 (33.0) μg/g dry wt. for the 72 pupae tested. Mean aluminium content was shown to be a significant negative predictor of average pupal weight in colonies. While no other statistically significant relationships were found relating aluminium to bee or colony health, the actual content of aluminium in pupae are extremely high and demonstrate significant exposure to aluminium. Bees rely heavily on cognitive function and aluminium is a known neurotoxin with links, for example, to Alzheimer's disease in humans. The significant contamination of bumblebee pupae by aluminium raises the intriguing spectre of cognitive dysfunction playing a role in their population decline.

  15. Power distribution: conductors in aluminium

    International Nuclear Information System (INIS)

    Schmid, R.

    2007-01-01

    This article takes a look at the use of aluminium conductors in medium and low-voltage cables. The author discusses how the increasing price of copper has led to the increasing use of aluminium as a material for the production of the conductors used in medium and low-voltage power cables. Aid is provided that is to help purchasers make the correct decisions when buying medium and low-voltage cables. The current market situation is examined and the appropriate norms are looked at. Technical data and economic aspects are discussed, both for medium and low-voltage applications. The electrical characteristics of the type of cable to be used are examined and discussed

  16. Neutron Cross Sections for Aluminium

    Energy Technology Data Exchange (ETDEWEB)

    Forsberg, Leif

    1963-08-15

    Total, elastic, inelastic, (n, 2n), (n, {alpha}), (n, p), and (n, {gamma}) cross sections for aluminium have been compiled from thermal to 100 MeV based upon literature search and theoretical interpolations and estimates. Differential elastic cross sections in the centre of mass system are represented by the Legendre coefficients. This method was chosen in order to obtain the best description of the energy dependence of the anisotropy.

  17. Aluminium and nickel in human albumin solutions

    DEFF Research Database (Denmark)

    Gammelgaard, Bente; Sandberg, E

    1989-01-01

    Five different brands of commercially available human albumin solutions for infusion were analysed for their aluminium and nickel contents by atomic absorption spectrometry. The aluminium concentrations ranged from 12 micrograms/l to 1109 micrograms/l and the nickel concentrations ranged from 17...... micrograms/l to 77 micrograms/l. Examination of the aluminium and nickel contents of the constituents for the production of one brand showed too low levels to explain the final contamination of the product. By following the aluminium and nickel concentrations of the same brand during the production...... of a batch of albumin solution, filtration was shown to contribute to contamination, although the largest increase in aluminium as well as nickel concentrations appeared during the bulk concentrating process. To avoid health risks to certain patients, regulations should be established requiring aluminium...

  18. Surface treatments for aluminium alloys

    Science.gov (United States)

    Ardelean, M.; Lascău, S.; Ardelean, E.; Josan, A.

    2018-01-01

    Typically, in contact with the atmosphere, the aluminium surface is covered with an aluminium oxide layer, with a thickness of less than 1-2μm. Due to its low thickness, high porosity and low mechanical strength, this layer does not protect the metal from corrosion. Anodizing for protective and decorative purposes is the most common method of superficial oxidation processes and is carried out through anodic oxidation. The oxide films, resulted from anodizing, are porous, have a thickness of 20-50μm, and are heat-resistant, stable to water vapour and other corrosion agents. Hard anodizing complies with the same obtains principles as well as decorative and protective anodization. The difference is in that hard anodizing is achieved at low temperatures and high intensity of electric current. In the paper are presented the results of decorative and hard anodization for specimens made from several aluminium alloys in terms of the appearance of the specimens and of the thickness of the anodized.

  19. Spectroscopic diagnostics of plasma during laser processing of aluminium

    International Nuclear Information System (INIS)

    Lober, R; Mazumder, J

    2007-01-01

    The role of the plasma in laser-metal interaction is of considerable interest due to its influence in the energy transfer mechanism in industrial laser materials processing. A 10 kW CO 2 laser was used to study its interaction with aluminium under an argon environment. The objective was to determine the absorption and refraction of the laser beam through the plasma during the processing of aluminium. Laser processing of aluminium is becoming an important topic for many industries, including the automobile industry. The spectroscopic relative line to continuum method was used to determine the electron temperature distribution within the plasma by investigating the 4158 A Ar I line emission and the continuum adjacent to it. The plasmas are induced in 1.0 atm pure Ar environment over a translating Al target, using f/7 and 10 kW CO 2 laser. Spectroscopic data indicated that the plasma composition and behaviour were Ar-dominated. Experimental results indicated the plasma core temperature to be 14 000-15 300 K over the incident range of laser powers investigated from 5 to 7 kW. It was found that 7.5-29% of the incident laser power was absorbed by the plasma. Cross-section analysis of the melt pools from the Al samples revealed the absence of any key-hole formation and confirmed that the energy transfer mechanism in the targets was conduction dominated for the reported range of experimental data

  20. Spectroscopic diagnostics of plasma during laser processing of aluminium

    Science.gov (United States)

    Lober, R.; Mazumder, J.

    2007-10-01

    The role of the plasma in laser-metal interaction is of considerable interest due to its influence in the energy transfer mechanism in industrial laser materials processing. A 10 kW CO2 laser was used to study its interaction with aluminium under an argon environment. The objective was to determine the absorption and refraction of the laser beam through the plasma during the processing of aluminium. Laser processing of aluminium is becoming an important topic for many industries, including the automobile industry. The spectroscopic relative line to continuum method was used to determine the electron temperature distribution within the plasma by investigating the 4158 Å Ar I line emission and the continuum adjacent to it. The plasmas are induced in 1.0 atm pure Ar environment over a translating Al target, using f/7 and 10 kW CO2 laser. Spectroscopic data indicated that the plasma composition and behaviour were Ar-dominated. Experimental results indicated the plasma core temperature to be 14 000-15 300 K over the incident range of laser powers investigated from 5 to 7 kW. It was found that 7.5-29% of the incident laser power was absorbed by the plasma. Cross-section analysis of the melt pools from the Al samples revealed the absence of any key-hole formation and confirmed that the energy transfer mechanism in the targets was conduction dominated for the reported range of experimental data.

  1. Detection of aluminium in different culinary media using black ...

    African Journals Online (AJOL)

    Jacques Blessing

    The interactions between food and aluminium local kitchen utensils can be a potential source of aluminium released which can ... need to be adopted to preserve consumers' health. ..... Corrosion behaviour of different ... Aluminium beverage.

  2. Introduction. Aluminium production on electrolytic cells with calcined anodes

    International Nuclear Information System (INIS)

    Galushkin, N.V.

    1995-01-01

    This chapter presents the monograph content, which includes the description of physicochemical processes in aluminium electrolytic cells, and mechanism of electrolytic aluminium obtaining. The short description of aluminium electrolytic cells construction is presented in this book as well.

  3. Coprecipitation of yttrium and aluminium hydroxide for preparation of yttrium aluminium garnet

    NARCIS (Netherlands)

    Vrolijk, J.W.G.A.; Willems, J.W.M.M.; Metselaar, R.

    1990-01-01

    Coprecipitation of yttrium and aluminium hydroxide for the preparation of pure yttrium aluminium garnet (YAG) powder with small grain size is the subject of this study. Starting materials are sulphates and chlorides of yttrium and aluminium. To obtain pure YAG (Y3Al5O12), the pH during flocculation

  4. Toxicity of aluminium on five aquatic invertebrates; Aluminiums toksisitet paa 5 akvatiske invertebrater

    Energy Technology Data Exchange (ETDEWEB)

    Moe, J [Oslo Univ. (Norway)

    1996-01-01

    The conference paper deals with the experiments done by investigating the effects from the toxicity of aluminium on aquatic invertebrates. The aim of the experiments was to compare the toxicity of unstable aluminium compounds with stable forms of aluminium. 8 refs., 2 figs., 2 tabs.

  5. Aluminium in foodstuffs and diets in Sweden.

    Science.gov (United States)

    Jorhem, L; Haegglund, G

    1992-01-01

    The levels of aluminium have been determined in a number of individual foodstuffs on the Swedish market and in 24 h duplicate diets collected by women living in the Stockholm area. The results show that the levels in most foods are very low and that the level in vegetables can vary by a factor 10. Beverages from aluminium cans were found to have aluminium levels not markedly different from those in glass bottles. Based on the results of the analysis of individual foods, the average Swedish daily diet was calculated to contain about 0.6 mg aluminium, whereas the mean content of the collected duplicate diets was 13 mg. A cake made from a mix containing aluminium phosphate in the baking soda was identified as the most important contributor of aluminium to the duplicate diets. Tea and aluminium utensils were estimated to increase the aluminium content of the diets by approximately 4 and 2 mg/day, respectively. The results also indicate that a considerable amount of aluminium must be introduced from other sources.

  6. Aluminium alloys welding with high-power Nd:YAG lasers

    International Nuclear Information System (INIS)

    Garcia Orza, J.A.

    1998-01-01

    Aluminium alloys have good mechanical properties (high strength-to-weight ratio, corrosion resistance) and good workability. their applications are growing up, specially in the transportation industry. Weldability is however poorer than in other materials; recent advances in high power YAG laser are the key to obtain good appearance welds and higher penetration, at industrial production rates. Results of the combination of high power YAG beams with small fiber diameters and specific filler wires are presented. It is also characterized the air bone particulate material, by-product of the laser process: emission rates, size distribution and chemical composition are given for several aluminium alloys. (Author) 6 refs

  7. Machinability of magnesium and aluminium alloys. Part I: cutting resistance

    International Nuclear Information System (INIS)

    Balout, B.; Songmene, V.; Masounave, J.

    2002-01-01

    Aluminium (2.7 g/cm 3 ) and magnesium (1.7 g/cm 3 ) are two competing light metals with similar mechanical properties and excellent possibilities for recycling. The forming of magnesium is often seen as an impediment to its use. New forming techniques using magnesium shavings are being developed, particularly in Japan. The machining of magnesium alloys by removal of metal raises safety concerns (risk of fire), which limits many potential applications of magnesium. The purpose of this work is to clarify and compare the machining properties of these two types of metal and better understand the mechanisms that may explain the differences in behaviour. Such a comparison could eventually provide an estimate of the cost of producing shavings for the manufacture of aluminium and magnesium parts through forging and extrusion, which would limit environmental pollution. Based on an analysis of cutting resistance during machining, it was demonstrated that magnesium alloys are easier to machine than similar aluminium alloys. Magnesium shavings are shorter than those of 6061-T6, but are especially more regular than those of A356, and their size is independent of cutting speed. It was also demonstrated that the fragility of materials can be characterized based on the results of cutting resistance produced during drilling

  8. Measurements and FLUKA Simulations of Bismuth, Aluminium and Indium Activation at the upgraded CERN Shielding Benchmark Facility (CSBF)

    Science.gov (United States)

    Iliopoulou, E.; Bamidis, P.; Brugger, M.; Froeschl, R.; Infantino, A.; Kajimoto, T.; Nakao, N.; Roesler, S.; Sanami, T.; Siountas, A.; Yashima, H.

    2018-06-01

    The CERN High energy AcceleRator Mixed field (CHARM) facility is situated in the CERN Proton Synchrotron (PS) East Experimental Area. The facility receives a pulsed proton beam from the CERN PS with a beam momentum of 24 GeV/c with 5·1011 protons per pulse with a pulse length of 350 ms and with a maximum average beam intensity of 6.7·1010 protons per second. The extracted proton beam impacts on a cylindrical copper target. The shielding of the CHARM facility includes the CERN Shielding Benchmark Facility (CSBF) situated laterally above the target that allows deep shielding penetration benchmark studies of various shielding materials. This facility has been significantly upgraded during the extended technical stop at the beginning of 2016. It consists now of 40 cm of cast iron shielding, a 200 cm long removable sample holder concrete block with 3 inserts for activation samples, a material test location that is used for the measurement of the attenuation length for different shielding materials as well as for sample activation at different thicknesses of the shielding materials. Activation samples of bismuth, aluminium and indium were placed in the CSBF in September 2016 to characterize the upgraded version of the CSBF. Monte Carlo simulations with the FLUKA code have been performed to estimate the specific production yields of bismuth isotopes (206 Bi, 205 Bi, 204 Bi, 203 Bi, 202 Bi, 201 Bi) from 209 Bi, 24 Na from 27 Al and 115 m I from 115 I for these samples. The production yields estimated by FLUKA Monte Carlo simulations are compared to the production yields obtained from γ-spectroscopy measurements of the samples taking the beam intensity profile into account. The agreement between FLUKA predictions and γ-spectroscopy measurements for the production yields is at a level of a factor of 2.

  9. Phase transformation of aluminium hydroxide to aα- alumina prepared from different aluminium salts

    International Nuclear Information System (INIS)

    Masliana Muslimin; Meor Yusoff Meor Sulaiman

    2006-01-01

    The study intends to look at the most suitable aluminium salt to produce a single-phase a-alumina by the hydrothermal method. In the process to produce alumina from the calcination of aluminium hydroxide (Al(OH) 3 ), three different aluminium salts namely aluminium sulfate (Al 2 (SO 4) 2), aluminium nitrate (A(NO 3 ) 3 ) and aluminium chloride (AlCl 3 ) were tried. The process involved the used of NH 4 OH as the precipitating medium. Aluminium hydroxide produced from each of these salts were characterised by x-ray diffraction (XRD) technique to identity the crystalline phase. Aluminium hydroxide produced by all the different aluminium salts is present as boehmite or pseudo-boehmite phase. Aluminium hydroxide produced from Al 2 (SO) 2 , Al(NO) 3 and AlCl 3 shows the transformation of the boehmite phase to a α-alumina phase at 500 0 C. On further heating, the α-alumina continuously formed at 800 o C followed soon at 1000 o C. But for the Al(NO3) 3 salts a different phase transitions occurs on heating especially at 1000 o C. Here it was observed not a single alumina phase is presence but the presence of both α and γ--alumina phases. At 1300 o C, the single α-alumina phase was formed. The study concluded that aluminium sulphate is recommended in order to obtain a single-phase α-alumina with the required characteristics. (Author)

  10. Structural-morphological variations in pseudo-barrier films of anode aluminium oxide under irradiation with high-energy particles

    International Nuclear Information System (INIS)

    Chernykh, M.A.; Belov, V.T.

    1988-01-01

    Comparative study of structural-morphological variations under electron beam effect in pseudo-barrier films of anode aluminium oxide, obtained in seven different solutions and proton or X-rays pre-irradiated to determine structure peculiarities of anode aluminium oxides, is presented. Such study is a matter of interest from the solid-phase transformation theory point of view and for anode aluminium films application under radiation. Stability increase of pseudo-barrier films of anode aluminium oxide to the effect of UEhMV-100 K microscope electron beam at standard modes of operation (75 kV) due to proton or X-rays irradiation is found. Difference in structural-monorphological variations obtained in different solutions of anode aluminium films under high-energy particles irradiation is determined. Strucural-phase microinhomogeneity of amorphous pseudo-barrier films of anode aluminium oxide and its influence on solid-phase transformations character under electron bean of maximal intensity are detected

  11. Preparation of aluminium lakes by electrocoagulation

    Directory of Open Access Journals (Sweden)

    Prapai Pradabkham

    2008-07-01

    Full Text Available Aluminium lakes have been prepared by electrocoagulation employing aluminium as electrodes. The electrocoagulation is conducted in an aqueous alcoholic solution and is completed within one hour. The dye content in the lake ranges approximately between 4-32%.

  12. Electron Conditioning of Technical Aluminium Surfaces

    Energy Technology Data Exchange (ETDEWEB)

    Le Pimpec, F

    2004-09-02

    The effect of electron conditioning on commercially aluminium alloys 1100 and 6063 were investigated. Contrary to the assumption that electron conditioning, if performed long enough, can reduce and stabilize the SEY to low values (= 1.3, value of many pure elements [1]), the SEY of aluminium did not go lower than 1.8. In fact, it reincreases with continued electron exposure dose.

  13. Thermal formation of corundum from aluminium hydroxides ...

    Indian Academy of Sciences (India)

    Aluminium hydroxides have been precipitated from various aluminium salts and the differences in their thermal behaviour have been investigated. Pseudoboehmite derived from the nitrate, sulfate and chloride all form -Al2O3 at ∼ 400°C but the formation of -Al2O3 at 1200°C occurs more readily in the material derived ...

  14. Characterisation and concentration profile of aluminium during ...

    African Journals Online (AJOL)

    An aluminium(Al) characterisation study was conducted at a surface water treatment plant (Buffalo Pound Water Treatment Plant (BPWTP) in Moose Jaw, Saskatchewan, Canada) to understand better the effect of alum coagulant on various Al fractions. The raw water source for BPWTP is Buffalo Pound Lake water. The Al ...

  15. Thermal formation of corundum from aluminium hydroxides ...

    Indian Academy of Sciences (India)

    Abstract. Aluminium hydroxides have been precipitated from various aluminium salts and the differences in their thermal behaviour have been investigated. Pseudoboehmite derived from the nitrate, sulfate and chloride all form γ-Al2O3 at ~ 400°C but the formation of α-Al2O3 at 1200°C occurs more readily in the material ...

  16. Rapidly solidified aluminium for optical applications

    NARCIS (Netherlands)

    Gubbels, G.P.H.; Venrooy, B.W.H. van; Bosch, A.J.; Senden, R.

    2008-01-01

    This paper present the results of a diamond turning study of a rapidly solidified aluminium 6061 alloy grade, known as RSA6061. It is shown that this small grain material can be diamond turned to smaller roughness values than standard AA6061 aluminium grades. Also, the results are nearly as good as

  17. Lactobacillus plantarum CCFM639 alleviates aluminium toxicity.

    Science.gov (United States)

    Yu, Leilei; Zhai, Qixiao; Liu, Xiaoming; Wang, Gang; Zhang, Qiuxiang; Zhao, Jianxin; Narbad, Arjan; Zhang, Hao; Tian, Fengwei; Chen, Wei

    2016-02-01

    Aluminium (Al) is the most abundant metal in the earth's crust. Al exposure can cause a variety of adverse physiological effects in humans and animals. Our aim was to demonstrate that specific probiotic bacteria can play a special physiologically functional role in protection against Al toxicity in mice. Thirty strains of lactic acid bacteria (LAB) were tested for their aluminium-binding ability, aluminium tolerance, their antioxidative capacity, and their ability to survive the exposure to artificial gastrointestinal (GI) juices. Lactobacillus plantarum CCFM639 was selected for animal experiments because of its excellent performance in vitro. Forty mice were divided into four groups: control, Al only, Al plus CCFM639, and Al plus deferiprone (DFP). CCFM639 was administered at 10(9) CFU once daily for 10 days, followed by a single oral dose of aluminium chloride hexahydrate at 5.14 mg aluminium (LD50) for each mouse. The results showed that CCFM639 treatment led to a significant reduction in the mortality rates with corresponding decrease in intestinal aluminium absorption and in accumulation of aluminium in the tissues and amelioration of hepatic histopathological damage. This probiotic treatment also resulted in alleviation of hepatic, renal, and cerebral oxidative stress. The treatment of L. plantarum CCFM639 has potential as a therapeutic dietary strategy against acute aluminium toxicity.

  18. Steam generated conversion coating on aluminium alloys

    DEFF Research Database (Denmark)

    Din, Rameez Ud; Jellesen, Morten Stendahl; Ambat, Rajan

    Aluminium and its alloys are widely used in aerospace industry owing to their high strength to weight ratio. The surface of aluminium under normal conditions has a thin oxide film (2.5-10 nm) responsible for its inherent corrosion resistance. This oxide film can further be converted or transformed...... into functional conversion coatings in order to enhance corrosion resistance and adhesion to paint systems. Chromium based conversion coatings have been extensively used on aluminium alloys to improve adhesion of subsequent paint layers and corrosion resistance. However, the use of hexavalent chromium is strictly...... regulated due to its toxic nature and suspected carcinogenicity. So, it is highly imperative to develop other alternatives for chrome conversion coatings. Treatment of aluminium with natural water at elevated temperatures results in the formation of different forms of aluminium oxide (γ-AlO(OH) , Al(OH)3...

  19. Joining of Aluminium Alloy and Steel by Laser Assisted Reactive Wetting

    Science.gov (United States)

    Liedl, Gerhard; Vázquez, Rodrigo Gómez; Murzin, Serguei P.

    2018-03-01

    Compounds of dissimilar materials, like aluminium and steel offer an interesting opportunity for the automotive industry to reduce the weight of a car body. Thermal joining of aluminium and steel leads to the formation of brittle intermetallic compounds, which negatively affects the properties of the welded joint. Amongst others, growth of such intermetallic compounds depends on maximum temperature and on the time at certain temperatures. Laser welding with its narrow well seam and its fast heating and cooling cycles provides an excellent opportunity to obtain an ultrathin diffusion zone. Joining of sheet metal DC01 with aluminium alloy AW6016 has been chosen for research. The performed experimental studies showed that by a variation of the beam power and scanning speed it is possible to obtain an ultrathin diffusion zone with narrow intermetallic interlayers. With the aim of supporting further investigation of laser welding of the respective and other dissimilar pairings a multi-physical simulation model has been developed.

  20. Structural study of Al2O3-Na2O-CaO-P2O5 bioactive glasses as a function of aluminium content.

    Science.gov (United States)

    Smith, J M; King, S P; Barney, E R; Hanna, J V; Newport, R J; Pickup, D M

    2013-01-21

    Calcium phosphate based biomaterials are extensively used in the context of tissue engineering: small changes in composition can lead to significant changes in properties allowing their use in a wide range of applications. Samples of composition (Al(2)O(3))(x)(Na(2)O)(0.11-x)(CaO)(0.445)(P(2)O(5))(0.445), where x = 0, 0.03, 0.05, and 0.08, were prepared by melt quenching. The atomic-scale structure has been studied using neutron diffraction and solid state (27)Al MAS NMR, and these data have been rationalised with the determined density of the final glass product. With increasing aluminium concentration the density increases initially, but beyond about 3 mol. % Al(2)O(3) the density starts to decrease. Neutron diffraction data show a concomitant change in the aluminium speciation, which is confirmed by (27)Al MAS NMR studies. The NMR data reveal that aluminium is present in 4, 5, and 6-fold coordination and that the relative concentrations of these environments change with increasing aluminium concentration. Materials containing aluminium in 6-fold coordination tend to have higher densities than analogous materials with the aluminium found in 4-fold coordination. Thus, the density changes may readily be explained in terms of an increase in the relative concentration of 4-coordinated aluminium at the expense of 6-fold aluminium as the Al(2)O(3) content is increased beyond 3 mol. %.

  1. Method for aluminium dross utilization

    International Nuclear Information System (INIS)

    Lucheva, B.; Petkov, R.; Tzonev, Tz.

    2003-01-01

    A new hydrometallurgical method has been developed for metal aluminum utilization from secondary aluminum dross. Secondary aluminum dross is a powder product with an average of 35% aluminium content (below 1mm). It is waste from primary aluminum dross pyrometallurgical flux less treatment in rotary DC electric arc furnace. This method is based on aluminum leaching in copper chloride water solution. As a result an aluminum oxychloride solution and solids, consisting of copper and oxides are obtained. In order to copper chloride solution regenerate hydrochloric acid is added to the solids. The process is simple, quick, economic and safe. The aluminum oxychloride solution contains 56 g/l Al 2 O 3 . The molar ratios are Al:Cl=0,5; OH:Al=1. The solution has 32 % basicity and 1,1 g/cm 3 density. For increasing the molar ratio of aluminium to chlorine aluminum hydroxide is added to this solution at 80 o C. Aluminum hydroxide is the final product from the secondary aluminum dross alkaline leaching. As a result aluminum oxychloride solution of the following composition is prepared: Al 2 O 3 - 180 g/l; Al:Cl=1,88; OH:Al=4,64; basicity 82%; density 1,22 g/cm 3 , pH=4 -4,5. Aluminum oxychloride solution produced by means of this method can be used in potable and wastewater treatment, paper making, in refractory mixture as a binder etc. (Original)

  2. Reduction of Defects on Microstructure Aluminium Nitride Using High Temperature Annealing Heat Treatment

    Science.gov (United States)

    Tanasta, Z.; Muhamad, P.; Kuwano, N.; Norfazrina, H. M. Y.; Unuh, M. H.

    2018-03-01

    Aluminium Nitride (AlN) is a ceramic 111-nitride material that is used widely as components in functional devices. Besides good thermal conductivity, it also has a high band gap in emitting light which is 6 eV. AlN thin film is grown on the sapphire substrate (0001). However, lattice mismatch between both materials has caused defects to exist along the microstructure of AlN thin films. The defects have affected the properties of Aluminium Nitride. Annealing heat treatment has been proved by the previous researcher to be the best method to improve the microstructure of Aluminium Nitride thin films. Hence, this method is applied at four different temperatures for two hour. The changes of Aluminium Nitride microstructures before and after annealing is observed using Transmission Electron Microscope. It is observed that inversion domains start to occur at temperature of 1500 °C. Convergent Beam Electron Diffraction pattern simulation has confirmed the defects as inversion domain. Therefore, this paper is about to extract the matters occurred during the process of producing high quality Aluminium Nitride thin films and the ways to overcome this problem.

  3. Variation in aluminium patch test reactivity over time.

    Science.gov (United States)

    Siemund, Ingrid; Mowitz, Martin; Zimerson, Erik; Bruze, Magnus; Hindsén, Monica

    2017-11-01

    Contact allergy to aluminium has been reported more frequently in recent years. It has been pointed out that positive patch test reactions to aluminium may not be reproducible on retesting. To investigate possible variations in patch test reactivity to aluminium over time. Twenty-one adults, who had previously reacted positively to aluminium, were patch tested with equimolar dilution series in pet. of aluminium chloride hexahydrate and aluminium lactate, four times over a period of 8 months. Thirty-six of 84 (43%) serial dilution tests with aluminium chloride hexahydrate and 49 of 84 (58%) serial dilution tests with aluminium lactate gave negative results. The range of reactivity varied between a negative reaction to aluminium chloride hexahydrate at 10% and/or to aluminium lactate at 12%, and a positive reaction to aluminium chloride hexahydrate at 0.1% and/or to aluminium lactate at 0.12%. The highest individual difference in test reactivity noticed was 320-fold when the two most divergent minimal eliciting concentrations were compared. The patch test reactivity to aluminium varies over time. Aluminium-allergic individuals may have false-negative reactions. Therefore, retesting with aluminium should be considered when there is a strong suspicion of aluminium contact allergy. © 2017 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

  4. Alveolar proteinosis associated with aluminium dust inhalation.

    Science.gov (United States)

    Chew, R; Nigam, S; Sivakumaran, P

    2016-08-01

    Secondary alveolar proteinosis is a rare lung disease which may be triggered by a variety of inhaled particles. The diagnosis is made by detection of anti-granulocyte-macrophage colony-stimulating factor antibodies in bronchoalveolar lavage fluid, which appears milky white and contains lamellar bodies. Aluminium has been suggested as a possible cause, but there is little evidence in the literature to support this assertion. We report the case of a 46-year-old former boilermaker and boat builder who developed secondary alveolar proteinosis following sustained heavy aluminium exposure. The presence of aluminium was confirmed both by histological examination and metallurgical analysis of a mediastinal lymph node. Despite cessation of exposure to aluminium and treatment with whole-lung lavage which normally results in improvements in both symptoms and lung function, the outcome was poor and novel therapies are now being used for this patient. It may be that the natural history in aluminium-related alveolar proteinosis is different, with the metal playing a mediating role in the disease process. Our case further supports the link between aluminium and secondary alveolar proteinosis and highlights the need for measures to prevent excessive aluminium inhalation in relevant industries. © The Author 2016. Published by Oxford University Press on behalf of the Society of Occupational Medicine. All rights reserved. For Permissions, please email: journals.permissions@oup.com.

  5. Challenges in LCA modelling of multiple loops for aluminium cans

    DEFF Research Database (Denmark)

    Niero, Monia; Olsen, Stig Irving

    considered the case of closed-loop recycling for aluminium cans, where body and lid are different alloys, and discussed the abovementioned challenge. The Life Cycle Inventory (LCI) modelling of aluminium processes is traditionally based on a pure aluminium flow, therefore neglecting the presence of alloying...... elements. We included the effect of alloying elements on the LCA modelling of aluminium can recycling. First, we performed a mass balance of the main alloying elements (Mn, Fe, Si, Cu) in aluminium can recycling at increasing levels of recycling rate. The analysis distinguished between different aluminium...... packaging scrap sources (i.e. used beverage can and mixed aluminium packaging) to understand the limiting factors for multiple loop aluminium can recycling. Secondly, we performed a comparative LCA of aluminium can production and recycling in multiple loops considering the two aluminium packaging scrap...

  6. Confined recrystallization of high-purity aluminium during accumulative roll bonding of aluminium laminates

    International Nuclear Information System (INIS)

    Chekhonin, Paul; Beausir, Benoît; Scharnweber, Juliane; Oertel, Carl-Georg; Hausöl, Tina; Höppel, Heinz Werner; Brokmeier, Heinz-Günter; Skrotzki, Werner

    2012-01-01

    Aluminium laminates consisting of high-purity aluminium and commercially pure aluminium have been produced by accumulative roll bonding (ARB) at ambient temperature for up to 10 cycles. To study the microstructure and texture development of the high-purity aluminium layers with regard to the shrinking layer thickness during ARB, microstructure and texture investigations were carried out by electron backscatter diffraction and neutron and X-ray diffraction, respectively. While the commercially pure aluminium layers develop an ultrafine-grained microstructure, partial discontinuous recrystallization occurs in the high-purity layers. The texture of the high-purity layers mainly consists of Cube and “Tilted Cube” (tilted with respect to the transverse direction) components. The experimental results are discussed with respect to confined recrystallization in the ARB aluminium laminates.

  7. Niobium-base grain refiner for aluminium

    International Nuclear Information System (INIS)

    Silva Pontes, P. da; Robert, M.H.; Cupini, N.L.

    1980-01-01

    A new chemical grain refiner for aluminium has been developed, using inoculation of a niobium-base compound. When a bath of molten aluminium is inoculated whith this refiner, an intermetallic aluminium-niobium compound is formed which acts as a powerful nucleant, producing extremely fine structure comparable to those obtained by means of the traditional grain refiner based on titanium and boron. It was found that the refinement of the structure depends upon the weight percentage of the new refiner inoculated as well as the time of holding the bath after inoculation and before pouring, but mainly on the inoculating temperature. (Author) [pt

  8. Net shape powder processing of aluminium

    International Nuclear Information System (INIS)

    Schaffer, G.B.

    2000-01-01

    The increasing interest in light weight materials coupled to the need for cost-effective processing have combined to create a significant opportunity for aluminium powder metallurgy. Net shape processing of aluminium using the classical press-and-sinter powder metallurgy technique is a unique and important metal-forming method which is cost effective in producing complex parts at, or very close to, final dimensions. This paper provides an overview of the net shape powder processing of aluminium. Current research is critically reviewed and the future potential is briefly considered

  9. Effects of aluminium surface morphology and chemical modification on wettability

    DEFF Research Database (Denmark)

    Rahimi, Maral; Fojan, Peter; Gurevich, Leonid

    2014-01-01

    -life aluminium surfaces of different morphology: unpolished aluminium, polished aluminium, and aluminium foil, were subjected to surface modification procedures which involved the formation of a layer of hydrophilic hyperbranched polyethyleneglycol via in situ polymerization, molecular vapour deposition...... of a monolayer of fluorinated silane, and a combination of those. The effect of these surface modification techniques on roughness and wettability of the aluminium surfaces was elucidated by ellipsometry, contact angle measurements and atomic force microscopy. We demonstrated that by employing different types...

  10. Structure-property investigations on a laser beam welded dissimilar joint of aluminium AA6056 and titanium Ti6Al4V for aeronautical applications. Part II: resistance to fatigue crack propagation and fracture

    Energy Technology Data Exchange (ETDEWEB)

    Horstmann, M.; Ventzke, V.; Petrovski, B.; Kocak, M. [GKSS Research Centre Geesthacht, Institute of Materials Research, Materials Mechanics, Geesthacht (Germany); Kocik, R.; Tempus, G. [AIRBUS Deutschland GmbH, Metal Technology, Bremen (Germany); Vaidya, W.V.

    2009-10-15

    Investigations were continued on the dissimilar laser beam welds of AA6056 and Ti6Al4V, fabricated by inserting Ti-sheet into the profiled Al-sheet and melting AA6056 alone. By using microstructure, hardness and strength as the criteria, sites exhibiting non-uniform microstructure and localized plastic deformation due to strength mismatch were investigated in two orientations: crack parallel to the weld and crack perpendicular to the weld for fatigue crack propagation and fracture toughness at room temperature. Effect of temper of AA6056 on these properties was studied for two conditions; welding in T4 followed by post weld heat treatment T6, and welding in T6 and naturally aged for a defined period. The orientation ''crack parallel to the weld'' was investigated in 3 locations on the side of AA6056: the interface and the two changeovers on the Al-side. Firstly, between the fusion zone and the heat affected zone (3 mm from the interface) and secondly, between (primary) heat affected zone and towards the base material (7 mm from the interface). Although brittle intermetallic TiAl{sub 3} had been formed at the interface, uncontrolled separation or debonding at the interface was not observed. Insofar the bond quality of the weld was good. However, the ranking of interface was the lowest since fatigue crack propagation was relatively faster than that in the fusion zone and heat affected zone, and fracture toughness was low. Therefore, unstable fatigue crack propagation is observed when the crack propagates perpendicular to the weld from AA6056 towards Ti6Al4V. The results have shown that the dissimilar joints exhibit improved performance when laser beam welded in the T6 condition. (Abstract Copyright [2009], Wiley Periodicals, Inc.) [German] Teil II: Widerstand gegen Ermuedungsrissausbreitung und Bruch Die Untersuchungen an der laserstrahlgeschweissten Mischverbindung aus AA6056 und Ti6Al4V wurden fortgesetzt. Fuer die Ermuedungsrissausbreitungs

  11. Aluminium Toxicity Targets in Plants

    Directory of Open Access Journals (Sweden)

    Sónia Silva

    2012-01-01

    Full Text Available Aluminium (Al is the third most abundant metallic element in soil but becomes available to plants only when the soil pH drops below 5.5. At those conditions, plants present several signals of Al toxicity. As reported by literature, major consequences of Al exposure are the decrease of plant production and the inhibition of root growth. The root growth inhibition may be directly/indirectly responsible for the loss of plant production. In this paper the most remarkable symptoms of Al toxicity in plants and the latest findings in this area are addressed. Root growth inhibition, ROS production, alterations on root cell wall and plasma membrane, nutrient unbalances, callose accumulation, and disturbance of cytoplasmic Ca2+ homeostasis, among other signals of Al toxicity are discussed, and, when possible, the behavior of Al-tolerant versus Al-sensitive genotypes under Al is compared.

  12. Response of E. coli AB2463 recA to fast neutron beams with mean energies in the range 4 to 27 MeV

    Energy Technology Data Exchange (ETDEWEB)

    Redpath, J L [Michael Reese Hospital, Chicago, Ill. (USA)

    1978-07-01

    The radiosensitivity of E.coli AB2463 recA, given as the reciprical of the mean lethal dose, Do/sup -1/, has been shown to be the same for four fast neutron beams with widely different energy spectra. It is proposed that this organism can be used to intercompare dosimetry on fast neutron beams with mean energies in the range 4 to 25 MeV with an accuracy of +- 5%.

  13. Steam Initiated Surface Modification of Aluminium Alloys

    DEFF Research Database (Denmark)

    Din, Rameez Ud

    The extensive demand of aluminium alloys in various industries such as in transportationis mainly due to the high strength to weight ratio, which could be translated into fuel economy and efficiency. Corrosion protection of aluminium alloys is an important aspect for all applications which includes...... the use of aluminium alloys in the painted form requiring a conversion coating to improve the adhesion. Chromate based conversion coating processes are extremely good for these purposes, however the carcinogenic and toxic nature of hexavalent chromium led to the search for more benign and eco......, crystalline nano-particles, role of steam-based treatment on adhesion of industrially applied powder coating, and investigations of a failed painted aluminium window profile due to defects in the extruded profile. Chapters 13 and 14 describe the overall discussion, conclusions and future work based...

  14. Generation and characterization of nano aluminium powder ...

    Indian Academy of Sciences (India)

    TECS

    Generation and characterization of nano aluminium powder obtained through wire ... Department of Aerospace Engineering, Indian Institute of Technology. Madras, Chennai 600 .... pressure developed due to current flow (z-Pinch). Figure 2.

  15. Irradiation effects in magnesium and aluminium alloys

    International Nuclear Information System (INIS)

    Sturcken, E.F.

    1979-01-01

    Effects of neutron irradiation on microstructure, mechanical properties and swelling of several magnesium and aluminium alloys were studied. The neutron fluences of 2-3 X 10 22 n/cm 2 , >0.2 MeV produced displacement doses of 20 to 45 displacements per atom (dpa). Ductility of the magnesium alloys was severely reduced by irradiation induced recrystallization and precipitation of various forms. Precipitation of transmuted silicon occurred in the aluminium alloys. However, the effect on ductility was much less than for the magnesium alloys. The magnesium and aluminium alloys had excellent resistance to swelling: The best magnesium alloy was Mg/3.0 wt% Al/0.19 wt% Ca; its density decreased by only 0.13%. The best aluminium alloy was 6063, with a density decrease of 0.22%. (Auth.)

  16. COMBINED ALUMINIUM SULFATE/HYDROXIDE PROCESS FOR ...

    African Journals Online (AJOL)

    sulfate, and used for fluoride removal from water by combining with Nalgonda Technique. ... effects on human health and could result in fluorosis. ... [23], nanoscale aluminium oxide hydroxide (AlOOH) [24] and natural zeolite [25], were among.

  17. Aluminium reprocessing with local mineral raw material

    International Nuclear Information System (INIS)

    Mirsaidov, U.M.

    2002-01-01

    With the purpose of utilization of ice sediment, receiving from mud fields solutions and flotation tails and at using local aluminium and fluorine-containing raw material was elaborated fundamental technologic scheme presented in this chapter of book

  18. Deformation features of aluminium in tensile tests

    International Nuclear Information System (INIS)

    Quadros, N.F. de.

    1984-01-01

    It is presented a method to analyse stress-strain curves. Plastic and elastic strains were studied. The strains were done by tensile tests in four types of materials: highly pure aluminium, pure aluminium, commercially pure aluminium and aluminium - uranium. The chemical compositions were obtained by spectroscopy analysis and neutron activation analysis. Tensile tests were carried out at three strain rates, at room temperature, 100,200, 300 and 400 0 C, with knives extensometer and strain-gages to studied the elastic strain region. A multiple spring model based on two springs model to analyse elastic strain caused by tests without extensometers, taking in account moduli of elasticity and, an interactive analysis system with graphic capability were developed. It was suggested a qualitative model to explain the quantized multielasticity of Bell. (M.C.K.) [pt

  19. Silane based coating of aluminium mold

    DEFF Research Database (Denmark)

    2013-01-01

    having at least one closed cavity is provided, at least one surface of the at least one cavity being an aluminium surface coated with a silane based coating layer. The silane based anti-stiction coating improves the anti-stiction properties of the mold which may allow for molding and demolding...... of structures which would otherwise be difficult to mold. The resistance of the coated aluminium mold is significantly improved by applying a silane-based coating layer....

  20. Characterization of aluminium alloys rapidly solidified

    International Nuclear Information System (INIS)

    Monteiro, W.A.

    1988-01-01

    This paper discussed the investigation of the microstructural and mechanical properties of the aluminium alloys (3003; 7050; Al-9% Mg) rapidly solidified by melt spinning process (cooling rate 10 4 - 10 6 K/s). The rapidly solidification process of the studied aluminium alloys brought a microcrystallinity, a minimum presence of coarse precipitation and, also, better mechanical properties of them comparing to the same alloys using ingot process. (author) [pt

  1. Structural evolution in nanoporous anodic aluminium oxide

    International Nuclear Information System (INIS)

    Rocca, Emmanuel; Vantelon, Delphine; Reguer, Solenn; Mirambet, François

    2012-01-01

    Nanoporous and self-organized layers of aluminium alloys are used in many applications as membranes, templates for nanometric objects or corrosion protection for aluminium alloys. The use of this nanometric structure widely remains empirical, especially in the case of very small pores ( 4 into AlO 6 cluster and a partial release of sulphate ions are an important chemical transformation of the amorphous structure. This structural transformation defines the chemistry (pH and surface charge) inside the nanopores, the ageing behaviour and the possible incorporation or diffusion of chemical species in the nanostructure. Highlights: ► Investigations of local chemical environment of aluminium atoms in anodic aluminium oxide. ► The oxide structure is constituted by 2/3 of aluminium in tetrahedral coordination 1/3 in octahedral coordination. ► In contact with water, AlO 4 clusters are transformed into AlO 6 cluster and the aluminium sulphate bonds are hydrolysed. ► These transformations induce a pH decrease inside the nanostructure.

  2. Development of Aluminium Vacuum Chambers for the LHC Experiments at CERN

    CERN Document Server

    Gallilee, M; Costa-Pinto, P; Lepeule, P; Perez-Espinos, J; Marques Antunes Ferreira, L; Prever-Loiri, L; Sapountzis, A

    2014-01-01

    Beam losses may cause activation of vacuum chamber walls, in particular those of the Large Hadron Collider (LHC) experiments. For the High Luminosity (HL-LHC), the activation of such vacuum chambers will increase. It is therefore necessary to use a vacuum chamber material which interacts less with the circulating beam. While beryllium is reserved for the collision point, a good compromise between cost, availability and transparency is obtained with aluminium alloys; such materials are a preferred choice with respect to austenitic stainless steel. Manufacturing a thin-wall aluminium vacuum chamber presents several challenges as the material grade needs to be machinable, weldable, leak-tight for small thicknesses, and able to withstand heating to 250°C for extended periods of time. This paper presents some of the technical challenges during the manufacture of these vacuum chambers and the methods for overcoming production difficulties, including surface treatments and Non-Evaporable Getter (NEG) thin-film coat...

  3. The Effect of Laser Surface Treatment on Structure and Mechanical Properties Aluminium Alloy ENAC-AlMg9

    Directory of Open Access Journals (Sweden)

    Pakieła W.

    2016-09-01

    Full Text Available In this work, the influence of a high power diode laser surface treatment on the structure and properties of aluminium alloy has been determined. The aim of this study was to improve the mechanical and tribological properties of the surface layer of the aluminium alloy by simultaneously melting and feeding tungsten carbide particles into the molten pool. During the process was used high-power diode laser HPDL. In order to remelt the aluminium alloy surface the HPDL laser of 1.8, 2.0 and 2.2 kW laser beam power has been used. The linear laser scan rate of the beam was set 0.5 cm/s. In order to protect the liquid metal during laser treatment was used argon. As a base material was used aluminium alloy ENAC-AlMg9. To improve the surface mechanical and wear properties of the applied aluminium alloy was used biphasic tungsten carbide WC/W2C. The size of alloying powder was in the range 110-210 µm. The ceramic powder was introduced in the remelting zone by a gravity feeder at a constant rate of 8 g/m.

  4. [Aluminium content in foods with aluminium-containing food additives].

    Science.gov (United States)

    Ogimoto, Mami; Suzuki, Kumi; Kabashima, Junichiro; Nakazato, Mitsuo; Uematsu, Yoko

    2012-01-01

    The aluminium (Al) content of 105 samples, including bakery products made with baking powder, agricultural products and seafoods treated with alum, was investigated. The amounts of Al detected were as follows (limit of quantification: 0.01 mg/g): 0.01-0.37 mg/g in 26 of 57 bakery products, 0.22-0.57 mg/g in 3 of 6 powder mixes, 0.01-0.05 mg/g in all three agricultural products examined, 0.03-0.90 mg/g in 4 of 6 seafood samples, 0.01-0.03 mg/g in 3 of 11 samples of instant noodles, 0.04-0.14 mg/g in 3 of 4 samples of vermicelli, 0.01 mg/g in 1 of 16 soybean products, but none in soybeans. Amounts equivalent to the PTWI of a 16 kg infant were detected in two samples of bakery products, two samples of powder mixes and one sample of salted jellyfish, if each sample was taken once a week. These results suggest that certain foods, depending on the product and the intake, might exceed the PTWI of children, especially infants.

  5. Aluminium exclusion and aluminium tolerance in woody plants

    Directory of Open Access Journals (Sweden)

    Ivano eBrunner

    2013-06-01

    Full Text Available The aluminium (Al cation Al3+ is highly rhizotoxic and is a major stress factor to plants on acid soils, which cover large areas of tropical and boreal regions. Many woody plant species are native to acid soils and are well adapted to high Al3+ conditions. In tropical regions, both woody Al accumulator and non-Al accumulator plants occur, whereas in boreal regions woody plants are non-Al accumulators. The mechanisms of these adaptations can be divided into those that facilitate the exclusion of Al3+ from root cells (exclusion mechanisms and those that enable plants to tolerate Al3+ once it has entered the root and shoot symplast (internal tolerance mechanisms. The biochemical and molecular basis of these mechanisms have been intensively studied in several crop plants and the model plant Arabidopsis. In this review, we examine the current understanding of Al3+ exclusion and tolerance mechanisms from woody plants. In addition, we discuss the ecology of woody non-Al accumulator and Al accumulator plants, and present examples of Al3+ adaptations in woody plant populations. This paper complements previous reviews focusing on crop plants and provides insights into evolutionary processes operating in plant communities that are widespread on acid soils.

  6. A 3D printed superconducting aluminium microwave cavity

    Energy Technology Data Exchange (ETDEWEB)

    Creedon, Daniel L. [School of Physics, University of Melbourne, Parkville, Victoria 3010 (Australia); Goryachev, Maxim; Kostylev, Nikita; Tobar, Michael E., E-mail: michael.tobar@uwa.edu.au [ARC Centre of Excellence for Engineered Quantum Systems, University of Western Australia, 35 Stirling Highway, Crawley, WA 6009 (Australia); Sercombe, Timothy B. [School of Mechanical and Chemical Engineering, University of Western Australia, 35 Stirling Highway, Crawley 6009 (Australia)

    2016-07-18

    3D printing of plastics, ceramics, and metals has existed for several decades and has revolutionized many areas of manufacturing and science. Printing of metals, in particular, has found a number of applications in fields as diverse as customized medical implants, jet engine bearings, and rapid prototyping in the automotive industry. Although many techniques are used for 3D printing metals, they commonly rely on computer controlled melting or sintering of a metal alloy powder using a laser or electron beam. The mechanical properties of parts produced in such a way have been well studied, but little attention has been paid to their electrical properties. Here we show that a microwave cavity (resonant frequencies 9.9 and 11.2 GHz) 3D printed using an Al-12Si alloy exhibits superconductivity when cooled below the critical temperature of aluminium (1.2 K), with a performance comparable with the common 6061 alloy of aluminium. Superconducting cavities find application in numerous areas of physics, from particle accelerators to cavity quantum electrodynamics experiments. The result is achieved even with a very large concentration of non-superconducting silicon in the alloy of 12.18%, compared with Al-6061, which has between 0.4% and 0.8%. Our results may pave the way for the possibility of 3D printing superconducting cavity configurations that are otherwise impossible to machine.

  7. A 3D printed superconducting aluminium microwave cavity

    International Nuclear Information System (INIS)

    Creedon, Daniel L.; Goryachev, Maxim; Kostylev, Nikita; Tobar, Michael E.; Sercombe, Timothy B.

    2016-01-01

    3D printing of plastics, ceramics, and metals has existed for several decades and has revolutionized many areas of manufacturing and science. Printing of metals, in particular, has found a number of applications in fields as diverse as customized medical implants, jet engine bearings, and rapid prototyping in the automotive industry. Although many techniques are used for 3D printing metals, they commonly rely on computer controlled melting or sintering of a metal alloy powder using a laser or electron beam. The mechanical properties of parts produced in such a way have been well studied, but little attention has been paid to their electrical properties. Here we show that a microwave cavity (resonant frequencies 9.9 and 11.2 GHz) 3D printed using an Al-12Si alloy exhibits superconductivity when cooled below the critical temperature of aluminium (1.2 K), with a performance comparable with the common 6061 alloy of aluminium. Superconducting cavities find application in numerous areas of physics, from particle accelerators to cavity quantum electrodynamics experiments. The result is achieved even with a very large concentration of non-superconducting silicon in the alloy of 12.18%, compared with Al-6061, which has between 0.4% and 0.8%. Our results may pave the way for the possibility of 3D printing superconducting cavity configurations that are otherwise impossible to machine.

  8. A 3D printed superconducting aluminium microwave cavity

    Science.gov (United States)

    Creedon, Daniel L.; Goryachev, Maxim; Kostylev, Nikita; Sercombe, Timothy B.; Tobar, Michael E.

    2016-07-01

    3D printing of plastics, ceramics, and metals has existed for several decades and has revolutionized many areas of manufacturing and science. Printing of metals, in particular, has found a number of applications in fields as diverse as customized medical implants, jet engine bearings, and rapid prototyping in the automotive industry. Although many techniques are used for 3D printing metals, they commonly rely on computer controlled melting or sintering of a metal alloy powder using a laser or electron beam. The mechanical properties of parts produced in such a way have been well studied, but little attention has been paid to their electrical properties. Here we show that a microwave cavity (resonant frequencies 9.9 and 11.2 GHz) 3D printed using an Al-12Si alloy exhibits superconductivity when cooled below the critical temperature of aluminium (1.2 K), with a performance comparable with the common 6061 alloy of aluminium. Superconducting cavities find application in numerous areas of physics, from particle accelerators to cavity quantum electrodynamics experiments. The result is achieved even with a very large concentration of non-superconducting silicon in the alloy of 12.18%, compared with Al-6061, which has between 0.4% and 0.8%. Our results may pave the way for the possibility of 3D printing superconducting cavity configurations that are otherwise impossible to machine.

  9. Beam-Beam Effects

    International Nuclear Information System (INIS)

    Herr, W; Pieloni, T

    2014-01-01

    One of the most severe limitations in high-intensity particle colliders is the beam-beam interaction, i.e. the perturbation of the beams as they cross the opposing beams. This introduction to beam-beam effects concentrates on a description of the phenomena that are present in modern colliding beam facilities

  10. TEM investigation of aluminium containing precipitates in high aluminium doped silicon carbide

    International Nuclear Information System (INIS)

    Wong-Leung, J.; FitzGerald, J.D.

    2002-01-01

    Full text: Silicon carbide is a promising semiconductor material for applications in high temperature and high power devices. The successful growth of good quality epilayers in this material has enhanced its potential for device applications. As a novel semiconductor material, there is a need for studying its basic physical properties and the role of dopants in this material. In this study, silicon carbide epilayers were grown on 4H-SiC wafers of (0001) orientation with a miscut angle of 8 deg at a temperature of 1550 deg C. The epilayers contained regions of high aluminium doping well above the solubility of aluminium in silicon carbide. High temperature annealing of this material resulted in the precipitation of aluminium in the wafers. The samples were analysed by secondary ion mass spectrometry and transmission electron microscopy. Selected area diffraction studies show the presence of aluminium carbide and aluminium silicon carbide phases. Copyright (2002) Australian Society for Electron Microscopy Inc

  11. Investigation of aluminium-rich alloy system of aluminium-strontium-silicium

    International Nuclear Information System (INIS)

    Ganiev, I.N.; Vakhobov, A.B.; Dzhuraev, T.D.; Alidzhanov, F.N.

    1976-01-01

    An area of the solid solution based on aluminium was studied, and the surface was plotted of the liquidus adjoining the apex of the aluminium corner of the strontium-aluminium-silicon system. The investigation was carried out by microstructure and differential thermal analyses and by the measurement of the microhardness of the component phases. A combined solubility of silicon and strontium in aluminium was studied along three radial sections at Sr-to-Si ratios of 1/2, 1/1 and 2/1. The relationships of ''composition vs. Microhardness'', obtained in these sections, made it possible to define the boundaries of the phase regions in the aluminium corner of the strontium-aluminium-silicon system at 500 deg C. The greatest solubility is that along the Al-SrAl 2 Si 2 section at a Sr/Si ratio of 1/2. A further increase in the content of strontium brings about a drop in the solubility of silicon in solid aluminium. The projection of the liquidus surface of the strontium-aluminium-silicon system, rich in aluminium, includes four surfaces of primary crystallization: α-Al, SrAl 4 , SrAl 2 Si 2 and Si. The system comprises a section of Al-SrAl 2 Si 2 representing a quasibinary system of an eutectic type. The eutectic reaction takes place at a temperature of 640 deg C. The quasibinary Al-SrAl 2 Si 2 section divides the aluminium corner of the Sr-Al-Si system into two independent systems Al-SrAl 4 -SrAl 2 Si 2 and Al-Si-SrAl 2 Si 2 of an eutectic type

  12. Aluminium content of foods originating from aluminium-containing food additives.

    Science.gov (United States)

    Ogimoto, Mami; Suzuki, Kumi; Haneishi, Nahoko; Kikuchi, Yuu; Takanashi, Mayu; Tomioka, Naoko; Uematsu, Yoko; Monma, Kimio

    2016-09-01

    Aluminium (Al) levels of 90 food samples were investigated. Nineteen samples contained Al levels exceeding the tolerable weekly intake (TWI) for young children [body weight (bw): 16 kg] when consuming two servings/week. These samples were purchased multiple times at specific intervals and were evaluated for Al levels. Al was detected in 27 of the 90 samples at levels ranging from 0.01 (limit of quantitation) to 1.06 mg/g. Of these, the Al intake levels in two samples (cookie and scone mix, 1.3 and 2 mg/kg bw/week, respectively) exceeded the TWI as established by European Food Safety Authority, although the level in the scone mix was equivalent to the provisional TWI (PTWI) as established by Joint Food and Agriculture Organization of the United Nations/World Health Organization Expert Committee on Food Additives. The Al levels markedly decreased in 14 of the 19 samples with initially high Al levels. These results indicated reductions in the Al levels to below the PTWI limits in all but two previously identified food samples.

  13. Ceramic filters analysis for aluminium melting through microtomography technique

    International Nuclear Information System (INIS)

    Rocha, Henrique de Souza; Lopes, Ricardo Tadeu; Jesus, Edgar Francisco Oliveira de; Oliveira, Luis Fernando de; Duhm, Rainer; Feiste, Karsten L.; Reichert, Christian; Reimche, Wilfried; Stegemann, Dieter

    2000-01-01

    In this work a ceramic filters analysis is done through the microtomography for improvement of the aluminium melting process through the filter porosity control. Microtomography were obtained of ceramic filters with pore dimensions of 10, 20 and 30 ppi. The data were calculated by using an reconstruction algorithm for divergent beam implemented in the Nuclear Instrumentation Laboratory of COPPE/UFRJ and analysed through cells and windows separation according to the defined by Ray. For the analyses the Image Pro program were used where the cells have been detached by sphere inserted, adjusting by nine points, in the filter cavities. So, the size of the answer sphere were considered as the cell size. The windows were measured by straight lines secant to the window intersections

  14. A study of aluminium-exposed fish using a scanning proton microprobe

    Energy Technology Data Exchange (ETDEWEB)

    Cholewa, M; Legge, G L.F. [Melbourne Univ., Parkville, VIC (Australia). School of Physics; Eeckhaoudt, S; Van Grieken, R [Universitaire Instelling Antwerpen, Antwerp (Belgium)

    1994-12-31

    A major problem has arisen in Europe with the depopulation of fresh water fish in lakes and streams collecting acid rain. The sensitivity to acidification is species specific and appears to be associated with metal levels. The Scanning Proton Microprobe (SPMP) at the Micro Analytical Research Centre of the University of Melbourne was used to study the subcellular distribution of aluminium and other elements in the gills of fish exposed to acidified water with elevated Al-levels. Experiments were performed on thin sections taken from fish exposed to media with different pH and aluminium concentration. Aluminium was found on the surface of the gill lamellae, but also inside the tissue. Bulk analysis of the gills showed much higher concentrations in the aluminium-exposed fish, compared to the control ones, but no information regarding the actual accumulation sites can be inferred. Extensive study of damage done to the sample by intense proton beams during elemental analysis was performed with scanning transmission ion microscopy. 3 refs., 3 figs.

  15. A study of aluminium-exposed fish using a scanning proton microprobe

    Energy Technology Data Exchange (ETDEWEB)

    Cholewa, M.; Legge, G.L.F. [Melbourne Univ., Parkville, VIC (Australia). School of Physics; Eeckhaoudt, S.; Van Grieken, R. [Universitaire Instelling Antwerpen, Antwerp (Belgium)

    1993-12-31

    A major problem has arisen in Europe with the depopulation of fresh water fish in lakes and streams collecting acid rain. The sensitivity to acidification is species specific and appears to be associated with metal levels. The Scanning Proton Microprobe (SPMP) at the Micro Analytical Research Centre of the University of Melbourne was used to study the subcellular distribution of aluminium and other elements in the gills of fish exposed to acidified water with elevated Al-levels. Experiments were performed on thin sections taken from fish exposed to media with different pH and aluminium concentration. Aluminium was found on the surface of the gill lamellae, but also inside the tissue. Bulk analysis of the gills showed much higher concentrations in the aluminium-exposed fish, compared to the control ones, but no information regarding the actual accumulation sites can be inferred. Extensive study of damage done to the sample by intense proton beams during elemental analysis was performed with scanning transmission ion microscopy. 3 refs., 3 figs.

  16. A study of aluminium-exposed fish using a scanning proton microprobe

    International Nuclear Information System (INIS)

    Cholewa, M.; Legge, G.L.F.

    1993-01-01

    A major problem has arisen in Europe with the depopulation of fresh water fish in lakes and streams collecting acid rain. The sensitivity to acidification is species specific and appears to be associated with metal levels. The Scanning Proton Microprobe (SPMP) at the Micro Analytical Research Centre of the University of Melbourne was used to study the subcellular distribution of aluminium and other elements in the gills of fish exposed to acidified water with elevated Al-levels. Experiments were performed on thin sections taken from fish exposed to media with different pH and aluminium concentration. Aluminium was found on the surface of the gill lamellae, but also inside the tissue. Bulk analysis of the gills showed much higher concentrations in the aluminium-exposed fish, compared to the control ones, but no information regarding the actual accumulation sites can be inferred. Extensive study of damage done to the sample by intense proton beams during elemental analysis was performed with scanning transmission ion microscopy. 3 refs., 3 figs

  17. Potentiometric titration curves of aluminium salt solutions and its ...

    African Journals Online (AJOL)

    Potentiometric titration curves of aluminium salt solutions and its species conversion ... of aluminium salt solutions under the moderate slow rate of base injection. ... silicate radical, and organic acid radical on the titration curves and its critical ...

  18. Effect of tempering on corrosion resistance of cast aluminium bronzes

    International Nuclear Information System (INIS)

    Aaltonen, P.; Klemetti, K.; Haenninen, H.

    1985-01-01

    The subject of this study is corrosion resistance of aluminium bronzes, which are copper base alloys containing aluminium up to 12% with additions of nickel, iron and manganese. The main conclutions that can be drawn are: (1) The dealloying corrosion resistance of nickel-aluminium bronze is much better than that of aluminium bronze with iron and manganese additions, but it is not immune; (2) The dealloying corrosion resistance of aluminium bronzes can be improved by appropiate heat treatments. The best properties were obtained by temperering between 600 and 800 deg C, depending on the initial microstructure; (3) In crevice conditions, where local acidification can occur, dealloying of aluminium bronzes is a consequence of the preferential attack of aluminium-rich phases. By appropriate tempering, a uniform distribution of aluminium-rich phases is obtained and the continous path for selective corrosion is not formed

  19. Aluminium hydroxide-the carrier for catalysts coating

    International Nuclear Information System (INIS)

    Normatov, I.Sh.; Mirsaidov, U.M.

    2003-01-01

    At present time several methods of receiving aluminium hydroxide are exist. But all they differ by much staging of process connected with preliminary receiving of intermediate compounds, with application of expensive metallic aluminium

  20. Effect of Sintering Temperature on the Properties of Aluminium-Aluminium Oxide Composite Materials

    Directory of Open Access Journals (Sweden)

    Dewan Muhammad Nuruzzaman

    2016-12-01

    Full Text Available In this study, aluminium-aluminium oxide (Al-Al2O3 metal matrix composites of different weight percentage reinforcements of aluminium oxide were processed at different sintering temperatures. In order to prepare these composite specimens, conventional powder metallurgy (PM method was used. Three types specimens of different compositions such as 95%Al+5%Al2O3, 90%Al+10%Al2O3 and 85%Al+15%Al2O3 were prepared under 20 Ton compaction load. Then, all the specimens were sintered in a furnace at two different temperatures 550oC and 580oC. In each sintering process, two different heating cycles were used. After the sintering process, it was observed that undistorted flat specimens were successfully prepared for all the compositions. The effects of sintering temperature and weight fraction of aluminium oxide particulates on the density, hardness and microstructure of Al-Al2O3 composites were observed. It was found that density and hardness of the composite specimens were significantly influenced by sintering temperature and percentage aluminium oxide reinforcement. Furthermore, optical microscopy revealed that almost uniform distribution of aluminium oxide reinforcement within the aluminium matrix was achieved.

  1. A study of formation of iron nanoparticles in aluminium matrix with helium pores

    Czech Academy of Sciences Publication Activity Database

    Kichanov, S.E.; Kozlenko, D. P.; Belushkin, A.V.; Reutov, V.F.; Samoilenko, S.O.; Jirák, Zdeněk; Savenko, B. N.; Bulavin, L. A.; Zubavichus, Y.V.

    2012-01-01

    Roč. 351, č. 1 (2012), "012013-1"-"012013-5" ISSN 1742-6588. [International Workshop on SANS-YuMO User Meeting at the Start-up of Scientific Experiments on the IBR-2M Reactor - Devoted to the 75th anniversary of Yu M Ostanevich's Birth /2./. Dubna, 27.05.2011-30.05.2011] Institutional research plan: CEZ:AV0Z10100521 Keywords : iron nanoparticles * aluminium matrix * helium pores Subject RIV: BM - Solid Matter Physics ; Magnetism

  2. Aluminium and the human breast.

    Science.gov (United States)

    Darbre, P D

    2016-06-01

    The human population is exposed to aluminium (Al) from diet, antacids and vaccine adjuvants, but frequent application of Al-based salts to the underarm as antiperspirant adds a high additional exposure directly to the local area of the human breast. Coincidentally the upper outer quadrant of the breast is where there is also a disproportionately high incidence of breast cysts and breast cancer. Al has been measured in human breast tissues/fluids at higher levels than in blood, and experimental evidence suggests that at physiologically relevant concentrations, Al can adversely impact on human breast epithelial cell biology. Gross cystic breast disease is the most common benign disorder of the breast and evidence is presented that Al may be a causative factor in formation of breast cysts. Evidence is also reviewed that Al can enable the development of multiple hallmarks associated with cancer in breast cells, in particular that it can cause genomic instability and inappropriate proliferation in human breast epithelial cells, and can increase migration and invasion of human breast cancer cells. In addition, Al is a metalloestrogen and oestrogen is a risk factor for breast cancer known to influence multiple hallmarks. The microenvironment is established as another determinant of breast cancer development and Al has been shown to cause adverse alterations to the breast microenvironment. If current usage patterns of Al-based antiperspirant salts contribute to causation of breast cysts and breast cancer, then reduction in exposure would offer a strategy for prevention, and regulatory review is now justified. Copyright © 2016 Elsevier Masson SAS. All rights reserved.

  3. Steam Assisted Accelerated Growth of Oxide Layer on Aluminium Alloys

    DEFF Research Database (Denmark)

    Din, Rameez Ud; Yuksel, Serkan; Jellesen, Morten Stendahl

    2013-01-01

    Corrosion resistance of aluminium alloys is related to the composition and morphology of the oxide film on the surface of aluminium. In this paper we investigated the use of steam on the surface modification of aluminium to produce boehmite films. The study reveals a detailed investigation...... of the effect of vapour pressure, structure of intermetallic particles and thickness of boehmite films on the corrosion behaviour of aluminium alloys....

  4. Advances in development and application of aluminium batteries

    DEFF Research Database (Denmark)

    Qingfeng, Li; Zhuxian, Qiu

    2001-01-01

    Aluminium has long attracted attention as a potential battery anode because of its high theoretical voltage and specific energy. The protective oxide layer at aluminium surface is however detrimental to its performance to achieve its reversible potential, and also causing the delayed activation o...... aluminium batteres, especially aluminium-air batteries, and a wide range of their applications from emergency power supplies, reserve batteries field portable batteries, to batteries for electric vehicles and underwater propulsion....

  5. Aluminium hydroxide-induced granulomas in pigs

    DEFF Research Database (Denmark)

    Valtulini, S; Macchi, C; Ballanti, P

    2005-01-01

    The effect of intramuscular injection of 40 mg/2 ml aluminium hydroxide in the neck of pigs was examined in a number of ways. The investigation followed repeated slaughterhouse reports, according to which 64.8% of pigs from one particular farm were found at slaughter to have one or more nodules...... in the muscles of the neck (group slaughtered). The pigs had been injected with a vaccine containing 40 mg/2 ml dose of aluminium hydroxide as adjuvant. Research consisted of two phases: first, an epidemiological study was carried out, aimed at determining the risk factors for the granulomas. The results...... and adjuvant) to pigs inoculated twice with apyrogenic bi-distilled water (group water) and to pigs inoculated once with the adjuvant and once with apyrogenic bi-distilled water (group adjuvant/water). Both studies agreed in their conclusions, which indicate that the high amount of aluminium hydroxide...

  6. Analysis of aluminium in rat following administration of allergen immunotherapy using either aluminium or microcrystalline-tyrosine-based adjuvants.

    Science.gov (United States)

    McDougall, Stuart A; Heath, Matthew D; Kramer, Matthias F; Skinner, Murray A

    2016-03-01

    Investigation into the absorption, distribution and elimination of aluminium in rat after subcutaneous aluminium adjuvant formulation administration using ICP-MS is described. Assays were verified under the principles of a tiered approach. There was no evidence of systemic exposure of aluminium, in brain or in kidney. Extensive and persistent retention of aluminium at the dose site was observed for at least 180 days after administration. This is the first published work that has quantified aluminium adjuvant retention based on the quantity of aluminium delivered in a typical allergy immunotherapy course. The results indicate that the repeated administration of aluminium-containing adjuvants will likely contribute directly and significantly to an individual's body burden of aluminium.

  7. Aluminium toxicity tolerance in crop plants: Present status of research

    African Journals Online (AJOL)

    ... tolerance of which genes of the Aluminium-activated malate transporter (ALMT) and multidrug and toxic compound extrusion (MATE) families are prominent. In this review, the progress of research in identifying aluminium toxicity tolerant genes is discussed. Keywords: Aluminium toxicity, soil acidity, hydroponic screening, ...

  8. Aluminium allergy and granulomas induced by vaccinations for children

    DEFF Research Database (Denmark)

    Andersen, Rosa Marie O; Zachariae, Claus; Johansen, Jeanne Duus

    2014-01-01

    Vaccination with aluminium-adsorbed vaccines can induce aluminium allergy with persistent itching subcutaneous nodules at the injection site - vaccination granulomas. In this article we give an overview of childhood aluminium-adsorbed vaccines available in Denmark. Through literature studies we...... examine the incidence, the symptoms and the prognosis for the vaccination granulomas and the allergy. Finally we discuss the status in Denmark....

  9. Aluminium allergy and granulomas induced by vaccinations for children

    DEFF Research Database (Denmark)

    Andersen, Rosa Marie O; Zachariae, Claus; Johansen, Jeanne Duus

    2014-01-01

    Vaccination with aluminium-adsorbed vaccines can induce aluminium allergy with persistent itching subcutaneous nodules at the injection site - vaccination granulomas. In this article we give an overview of childhood aluminium-adsorbed vaccines available in Denmark. Through literature studies we...

  10. Spectrophotometric determination of aluminium in steel with xylenol orange

    International Nuclear Information System (INIS)

    Majeed, A.; Javed, N.; Khan, M.S.

    1996-01-01

    Spectrophotometric determination of Aluminium in steel based on colour reaction between Aluminium and xylenol orange has been carried out. Red coloured complex formed in weak acidic solution is measured for its absorbance at 550 nm. The various optimum experimental conditions for Aluminium xylenol orange (Al-Xo) complex have been studied. (author)

  11. Energy Absorption of Monolithic and Fibre Reinforced Aluminium Cylinders

    NARCIS (Netherlands)

    De Kanter, J.L.C.G.

    2006-01-01

    Summary accompanying the thesis: Energy Absorption of Monolithic and Fibre Reinforced Aluminium Cylinders by Jens de Kanter This thesis presents the investigation of the crush behaviour of both monolithic aluminium cylinders and externally fibre reinforced aluminium cylinders. The research is based

  12. Corrosion behaviour of borated aluminium used as neutron absorber

    Energy Technology Data Exchange (ETDEWEB)

    Emmerich, R. [EaglePicher Technologies GmbH, Oehringen (Germany); Ensinger, W.; Enders, B. [Philipps-Univ. of Marburg, Dept. of Chemistry, Material Science Centre (Germany)

    2004-07-01

    The electrochemical behaviour of pure and borated aluminium was examined. Measurements were performed in two different electrolytes at 90 C containing different trace-amounts of chloride. For borated aluminium current transients, i.e. metastable depassivation events were found. It is suggested to attribute these transients to less stable passivation layers in comparison to pure aluminium.

  13. Internal friction in iron-aluminium alloys having a high aluminium content

    International Nuclear Information System (INIS)

    Hillairet, J.; Delaplace, J.; Silvent, A.

    1966-01-01

    By using a torsion pendulum to measure the internal friction of iron-aluminium alloys containing between 25 and 50 atom per cent of aluminium, it has been possible to show the existence of three damping peaks due to interstitial carbon. Their evolution is followed as a function of the carbon content, of the thermal treatment and of the aluminium content. A model based on the preferential occupation of tetrahedral sites is proposed as an interpretation of the results. A study of the Zener peak in these substitution alloys shows also that a part of the short distance disorder existing at high temperatures can be preserved by quenching. (author) [fr

  14. Process for the manufacture of plates containing neutron poison from aluminium and aluminium alloys

    International Nuclear Information System (INIS)

    Bauer, G.; Pollmann, E.; Srostlik, P.

    1985-01-01

    A process for guaranteeing sub-critical arrangements of nuclear fuel in tranport and/or storage containers is described, in which a homogeneous distribution of neutron poison in the aluminium matrix is guaranteed. A homogeneous mixture of aluminium powder and neutron poison powder is produced, this is pressed into plates in several stages, dried and made into hollow aluminium profiles of rectangular cross-section. The open ends of the hollow profile are then closed and this is rolled to the required dimension at 470-500 0 C. (orig./HP) [de

  15. TITANIUM CARBON ALUMINIUM : A NOVEL GRAIN REFINER FOR ALUMINIUM-LITHIUM ALLOYS

    OpenAIRE

    Birch , M.; Cowell , A.

    1987-01-01

    This work explores the possibility of achieving grain size control in aluminium-lithium alloys with the titanium carbon aluminium (TiCAl) master alloys invented at the Technical University of Berlin and developed by London and Scandinavian Metallurgical Co Ltd (LSM). Grain refining tests were conducted on a single batch of 8090 alloy using addition rates of 0.2wt% and 0.4wt% of TiCAl and 3/1 titanium boron aluminium (TiBAl). Other tests using 0.4wt% of binary TiAl gave poor results, showing t...

  16. Molybdenum solubility in aluminium nitrate solutions

    Energy Technology Data Exchange (ETDEWEB)

    Heres, X.; Sans, D.; Bertrand, M.; Eysseric, C. [CEA, Centre de Marcoule, Nuclear Energy Division, DRCP, BP 17171, 30207 Bagnols-sur-Ceze Cedex (France); Brackx, E.; Domenger, R.; Excoffier, E. [CEA, Centre de Marcoule, Nuclear Energy Division, DTEC, BP 17171, 30207 Bagnols-sur-Ceze Cedex (France); Valery, J.F. [AREVA-NC, DOR/RDP, Paris - La Defense (France)

    2016-07-01

    For over 60 years, research reactors (RR or RTR for research testing reactors) have been used as neutron sources for research, radioisotope production ({sup 99}Mo/{sup 99m}Tc), nuclear medicine, materials characterization, etc... Currently, over 240 of these reactors are in operation in 56 countries. They are simpler than power reactors and operate at lower temperature (cooled to below 100 C. degrees). The fuel assemblies are typically plates or cylinders of uranium alloy and aluminium (U-Al) coated with pure aluminium. These fuels can be processed in AREVA La Hague plant after batch dissolution in concentrated nitric acid and mixing with UOX fuel streams. The aim of this study is to accurately measure the solubility of molybdenum in nitric acid solution containing high concentrations of aluminium. The higher the molybdenum solubility is, the more flexible reprocessing operations are, especially when the spent fuels contain high amounts of molybdenum. To be most representative of the dissolution process, uranium-molybdenum alloy and molybdenum metal powder were dissolved in solutions of aluminium nitrate at the nominal dissolution temperature. The experiments showed complete dissolution of metallic elements after 30 minutes long stirring, even if molybdenum metal was added in excess. After an induction period, a slow precipitation of molybdic acid occurs for about 15 hours. The data obtained show the molybdenum solubility decreases with increasing aluminium concentration. The solubility law follows an exponential relation around 40 g/L of aluminium with a high determination coefficient. Molybdenum solubility is not impacted by the presence of gadolinium, or by an increasing concentration of uranium. (authors)

  17. Development of a process for continuous determination of aluminium in bauxite

    International Nuclear Information System (INIS)

    Freitas, A.M.R. de.

    1984-01-01

    A system for aluminium analysis in bauxite using activation technique with the aid of a 5 Ci 241 Am/Be neutron source was developed. The system comprises the following steps: sampling, irradiation and counting. The reaction 27 Al(n,γ) 28 Al is used for determination of aluminium. A 2'' x 2'' NaI(T1) scintillation detector was used for the γ-activity measurements and integral counting technique was employed. Half-life determinations for samples were carried out in order to assure that the induced activity was predominantly due to the radionuclide 28 Al. In order to construct a system with solids, paraffin was chosen as moderator and reflector and an optimum irradiation position was determined. Analysis on a laboratory scale with 100g of the sample showed a good linear correlation between counts and aluminium content in bauxite samples. An irradiation chamber consisting of neutron source, moderator and reflector was constructed for activation of 2 Kg samples. Analysis with these bauxite samples indicated a relative precision in the range of 2 to 3% in less than ten minutes. Based on these results, a preliminary pilot-project was designed for continuous aluminium analysis in bauxite. (Author) [pt

  18. Reactor neutron activation analysis for aluminium in the presence of phosphorus and silicon

    International Nuclear Information System (INIS)

    Mizumoto, Yoshihiko; Iwata, Shiro; Sasajima, Kazuhisa; Yoshimasu, Fumio; Yase, Yoshiro.

    1984-01-01

    Reactor neutron activation analysis for aluminium in samples containing phosphorus and silicon was studied. The experiments were performed by using neumatic tube of the Kyoto University Reactor (KUR). At first, the ratios of the 28 Al activity produced from 27 Al(n, γ) 28 Al reaction by thermal neutrons to that from 31 P(n, α) 28 Al reaction by fast neutrons, and to that from 28 Si(n, p) 28 Al reaction were measured by γ-ray spectrometry. With a ratio of about 5 for the thermal to fast neutron flux of KUR, the ratio of the 28 Al activity from aluminium to that from phosphorus was to be 812 +- 7, and to that from silicon 282 +- 3. Secondly, the contributions of 28 Al activities from phosphorus and silicon and the determination limit of aluminium were calculated for various parameters, such as fast neutron flux, thermal to fast neutron flux ratio, amounts of phosphorus and silicon, etc. Thirdly, on the basis of these results, aluminium contents in spinal cords and brains of amyotrophic lateral sclerosis, Parkinsonism-dementia complex and control cases were determined. (author)

  19. Defect generation during solidification of aluminium foams

    International Nuclear Information System (INIS)

    Mukherjee, M.; Garcia-Moreno, F.; Banhart, J.

    2010-01-01

    The reason for the frequent occurrence of cell wall defects in metal foams was investigated. Aluminium foams often expand during solidification, a process which is referred as solidification expansion (SE). The effect of SE on the structure of aluminium foams was studied in situ by X-ray radioscopy and ex situ by X-ray tomography. A direct correlation between the magnitude of SE and the number of cell wall ruptures during SE and finally the number of defects in the solidified foams was found.

  20. Durability of bare and anodised aluminium in atmosphere of very different corrosivities I. Bare aluminium

    International Nuclear Information System (INIS)

    Gonzalez, J. A.; Escudero, E.; Lopez, V.; Simancas, J.; Morcillo, M.

    2004-01-01

    The behaviour of bare aluminium is studied in atmospheric exposure at 11 natural testing stations with salinity levels ranging between 2.1 and 684 mg Cl''- m''-2 d''-1. In atmospheres of low or moderate aggressivity aluminium behaves as a passive material, though the insignificant corrosion that is produced is sufficient to spoil its appearance. In contrast, at salinity levels of 50 mg Cl''- m''-2 ''-1 or above, aluminium is susceptible to pitting corrosion even in the first year of atmospheric exposure, or in the second year at salinities of ≤ 10 mg Cl''- m''-2 d''-1. For comparative purposes, results are included for aluminium protected with an anodic film of 28 μm thickness exposed at the same testing stations. A 28 μm anodic film, correctly sealed, prevents the risk of localised corrosion even in the most unfavourable situations. (Author) 23 refs

  1. Irradiation damage in aluminium single crystals produced by 50-keV aluminium and copper ions

    DEFF Research Database (Denmark)

    Henriksen, L.; Johansen, A.; Koch, J.

    1968-01-01

    Aluminium single crystals, thin enough to be examined by electron microscopy, have been irradiated with 50-keV aluminium and copper ions. The irradiation fluxes were in the range 1011–1014 cm−2 s−1 and the doses were from 6 × 1012 to 6 × 1014 cm−2. Irradiation along either a or a direction produces...... rows of dislocation loops all lying parallel to one particular direction. If the aluminium target is quenched from 600 °C and annealed at room temperature prior to irradiation with aluminium ions, the rows of loops are suppressed. The amount of damage observed is considerably less than would...

  2. Mechanical behaviour of aluminium-lithium alloys

    Indian Academy of Sciences (India)

    Aluminium-lithium alloys hold promise of providing a breakthrough response to the crying need for lightweight alloys for use as structurals in aerospace applications. Considerable worldwide research has gone into developing a range of these alloys over the last three decades. As a result, substantial understanding has ...

  3. Warm Deep Drawing of Aluminium Sheet

    NARCIS (Netherlands)

    Bolt, P.J.; Werkhoven, R.J.; van den Boogaard, Antonius H.

    2003-01-01

    Aluminium sheet drawing processes can be improved by manipulating local flow behaviour by means of elevated temperatures and temperature gradients in the tooling. Forming tests showed that a substantial improvement is possible not only for 5xxx but also for 6xxx series alloys. Finite element method

  4. Complexes of alkylphenols with aluminium halides

    International Nuclear Information System (INIS)

    Golounin, A.V.

    1997-01-01

    Interaction of aluminium halides with alkylphenols is studied through the NMR method. The peculiarity of complex formation of pentamethylphenol with AlI 3 is revealed. By AlI 3 action on the pentamethylphenol the complexes are formed both of keto- and oxy form [ru

  5. Plasma metallization of aluminium oxide powder

    International Nuclear Information System (INIS)

    Smirnov, A.I.; Petrunichev, V.A.

    1981-01-01

    The sintering ability of cermets of metallized granulas of aluminium and matrix materials, such as chromium, nickel and nichrome is studied. Deformation tests of samples of cermets with molybdenum coated granules show satisfactory results at normal and high temperatures without fracture of metall-oxide interfaces [ru

  6. Indentation of aluminium foam at low velocity

    Directory of Open Access Journals (Sweden)

    Shi Xiaopeng

    2015-01-01

    Full Text Available The indentation behaviour of aluminium foams at low velocity (10 m/s ∼ 30 m/s was investigated both in experiments and numerical simulation in this paper. A flat-ended indenter was used and the force-displacement history was recorded. The Split Hopkinson Pressure bar was used to obtain the indentation velocity and forces in the dynamic experiments. Because of the low strength of the aluminium foam, PMMA bar was used, and the experimental data were corrected using Bacon's method. The energy absorption characteristics varying with impact velocity were then obtained. It was found that the energy absorption ability of aluminium foam gradually increases in the quasi-static regime and shows a significant increase at ∼10 m/s velocity. Numerical simulation was also conducted to investigate this process. A 3D Voronoi model was used and models with different relative densities were investigated as well as those with different failure strain. The indentation energy increases with both the relative density and failure strain. The analysis of the FE model implies that the significant change in energy absorption ability of aluminium foam in indentation at ∼10 m/s velocity may be caused by plastic wave effect.

  7. Molecular breeding of cereals for aluminium resistance

    Science.gov (United States)

    Aluminium (Al3+) toxicity is the primary factor limiting crop production on acidic soils worldwide. In addition to an application of lime for soil amelioration, Al3+ resistant plant varieties have been deployed to raise productivity on such hostile soils. This has been possible due to the exploita...

  8. Constant structure creep experiments on aluminium

    Czech Academy of Sciences Publication Activity Database

    Milička, Karel

    2011-01-01

    Roč. 49, č. 5 (2011), s. 307-318 ISSN 0023-432X R&D Projects: GA AV ČR IAA2041203 Institutional research plan: CEZ:AV0Z20410507 Keywords : mechanical properties * high temperature deformation * creep * aluminium Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.451, year: 2011

  9. Creep properties of aluminium processed by ECAP

    Czech Academy of Sciences Publication Activity Database

    Král, Petr; Dvořák, Jiří; Jäger, Aleš; Kvapilová, Marie; Horita, Z.; Sklenička, Václav

    2016-01-01

    Roč. 54, č. 6 (2016), s. 441-451 ISSN 0023-432X R&D Projects: GA MŠk(CZ) LQ1601 Institutional support: RVO:68081723 ; RVO:68378271 Keywords : equal channel angular pressing (ECAP) * aluminium * ultrafine-grained microstructure * creep Subject RIV: JG - Metallurgy; JG - Metallurgy (FZU-D) Impact factor: 0.366, year: 2016

  10. Numerical modelling in friction lap joining of aluminium alloy and carbon-fiber-reinforced-plastic sheets

    Science.gov (United States)

    Das, A.; Bang, H. S.; Bang, H. S.

    2018-05-01

    Multi-material combinations of aluminium alloy and carbon-fiber-reinforced-plastics (CFRP) have gained attention in automotive and aerospace industries to enhance fuel efficiency and strength-to-weight ratio of components. Various limitations of laser beam welding, adhesive bonding and mechanical fasteners make these processes inefficient to join metal and CFRP sheets. Friction lap joining is an alternative choice for the same. Comprehensive studies in friction lap joining of aluminium to CFRP sheets are essential and scare in the literature. The present work reports a combined theoretical and experimental study in joining of AA5052 and CFRP sheets using friction lap joining process. A three-dimensional finite element based heat transfer model is developed to compute the temperature fields and thermal cycles. The computed results are validated extensively with the corresponding experimentally measured results.

  11. Finite Element Analysis of Warpage in Laminated Aluminium Alloy Plates for Machining of Primary Aeronautic Parts

    International Nuclear Information System (INIS)

    Reis, A. C.; Moreira Filho, L. A.; Menezes, M. A.

    2007-01-01

    The aim of this paper consists in presenting a method of simulating the warpage in 7xxx series aluminium alloy plates. To perform this simulation finite element software MSC.Patran and MSC.Marc were used. Another result of this analysis will be the influence on material residual stresses induced on the raw material during the rolling process upon the warpage of primary aeronautic parts, fabricated through machining (milling) at Embraer. The method used to determinate the aluminium plate residual stress was Layer Removal Test. The numerical algorithm Modified Flavenot Method was used to convert layer removal and beam deflection in stress level. With such information about the level and profile of residual stresses become possible, during the step that anticipate the manufacturing to incorporate these values in the finite-element approach for modelling warpage parts. Based on that warpage parameter surely the products are manufactured with low relative vulnerability propitiating competitiveness and price

  12. A study of enhanced diffusion during high dose high flux pulsed metal ion implantation into steel and aluminium

    International Nuclear Information System (INIS)

    Zhang Tonghe; Ji Chengzhou; Shen Jinghua; Chen Jun

    1992-01-01

    The depth profiles of metal ions implanted into steel and aluminium were measured by Rutherford backscattering (RBS). The ions of Mo, W and Y, produced by a metal vapour vacuum are ion source (MEVVA) were implanted at an energy range from 25 to 50 keV for doses of (2-5)x10 17 cm -2 into H13 steel and aluminium. Beam currents were from 0.5 to 1.0 A. The beam flux is in the range of 25 to 75 μAcm -2 . In order to simulate the profiles, a formula which includes the sputtering yield, diffusion coefficients and reaction rate was obtained. The results demonstrate that the penetration depth and retained dose increase with increasing beam flux for Mo implanted into aluminium. The peak concentration of Mo implanted H13 steel increases with increasing ion flux. In contrast to this for Y implantation into steel, the peak concentration of Y decreases with increasing ion flux. For an ion flux of 25 μAcm -2 for Mo, Y and W implantation into steel, the penetration depth and retained dose are 3-5 times greater than the theoretical values. The diffusion coefficients are about 10 -16 to 10 -15 s -1 . If the ion flux is greater than 47 μAcm -2 , the penetration depth and retained dose are 5 to 10 times greater than the theoretical values for Mo implanted aluminium. The diffusion coefficients increase with increasing ion flux for Mo implanted aluminium. The diffusion coefficients hardly change with increasing ion flux for Y and Mo implanted H13 steel. The retained dose increases 0.43 to 1.16 times for Y implanted steel for an ion flux of 25 μAcm -2 . Finally, the influence of phases precipitates, reaction rate and diffusion on retained dose, diffusion coefficient and penetration depth are discussed. (orig.)

  13. Aluminium and copper analysis in metallic alloys by neutron activation analysis from an 241 Am-Be source

    International Nuclear Information System (INIS)

    Carvalho, J. de.

    1980-01-01

    Aluminium and copper have been determined in aluminium alloys by the method of activation with neutrons from an 241 Am-Be source of intensity 9,8 x 10 6 n/s. The activity induced due to reactions 27 Al (n, γ) 28 Al and 63 Cu (n, γ) 64 Cu have been measured with a NaI (Tl) detector coupled to a single channel system. In order to obtain the samples and standards of about the same composition, the material to be irradiated was powdered. In view of low intensity of neutron source it was necessary to use samples of up to 50 g. A series of preliminary irradiations were carried out to ensure that the geometry for the irradiation and for the counting are reproducible. The results have been compared with those obtained by chemical methods. Assuming that the results obtained by chemical method is exact, a maximum relative error of 3,6% is obtained by this method. The method has a good reproducibility. The time needed for analysis of aluminium and copper are 18 min and 2 hours 40 minutes respectively. Four different samples were analysed. The average of five measurements for one of the samples was: 88.0% for aluminium and 10.0% for copper. The standard deviation and coefficient of variation were 0,8 and 1.0% for aluminium and 0,2 and 2.0% for copper. (author)

  14. Shielding in electron beams used in radiotherapy

    International Nuclear Information System (INIS)

    Sentenac, Irenee.

    1979-01-01

    The interactions of electron beams with initial energies between 7 and 30 MeV have been studied in various materials including polystyrene, aluminium, copper and lead. The following experimental results have been found: estimation of measurement point displacement in a cylindrical chamber and of its variations with electron beam energy, empirical relations between the energy at the surface and the practical range of the electrons in various materials, an estimation of the relative ionisation due to the 'bremsstrahlung' measured behind different materials with beam complete shielding. Improvement of electron beam collimation is suggested after analysis of the dose distribution behind partial shielding [fr

  15. 3D printing of high-strength aluminium alloys.

    Science.gov (United States)

    Martin, John H; Yahata, Brennan D; Hundley, Jacob M; Mayer, Justin A; Schaedler, Tobias A; Pollock, Tresa M

    2017-09-20

    Metal-based additive manufacturing, or three-dimensional (3D) printing, is a potentially disruptive technology across multiple industries, including the aerospace, biomedical and automotive industries. Building up metal components layer by layer increases design freedom and manufacturing flexibility, thereby enabling complex geometries, increased product customization and shorter time to market, while eliminating traditional economy-of-scale constraints. However, currently only a few alloys, the most relevant being AlSi10Mg, TiAl6V4, CoCr and Inconel 718, can be reliably printed; the vast majority of the more than 5,500 alloys in use today cannot be additively manufactured because the melting and solidification dynamics during the printing process lead to intolerable microstructures with large columnar grains and periodic cracks. Here we demonstrate that these issues can be resolved by introducing nanoparticles of nucleants that control solidification during additive manufacturing. We selected the nucleants on the basis of crystallographic information and assembled them onto 7075 and 6061 series aluminium alloy powders. After functionalization with the nucleants, we found that these high-strength aluminium alloys, which were previously incompatible with additive manufacturing, could be processed successfully using selective laser melting. Crack-free, equiaxed (that is, with grains roughly equal in length, width and height), fine-grained microstructures were achieved, resulting in material strengths comparable to that of wrought material. Our approach to metal-based additive manufacturing is applicable to a wide range of alloys and can be implemented using a range of additive machines. It thus provides a foundation for broad industrial applicability, including where electron-beam melting or directed-energy-deposition techniques are used instead of selective laser melting, and will enable additive manufacturing of other alloy systems, such as non-weldable nickel

  16. 3D printing of high-strength aluminium alloys

    Science.gov (United States)

    Martin, John H.; Yahata, Brennan D.; Hundley, Jacob M.; Mayer, Justin A.; Schaedler, Tobias A.; Pollock, Tresa M.

    2017-09-01

    Metal-based additive manufacturing, or three-dimensional (3D) printing, is a potentially disruptive technology across multiple industries, including the aerospace, biomedical and automotive industries. Building up metal components layer by layer increases design freedom and manufacturing flexibility, thereby enabling complex geometries, increased product customization and shorter time to market, while eliminating traditional economy-of-scale constraints. However, currently only a few alloys, the most relevant being AlSi10Mg, TiAl6V4, CoCr and Inconel 718, can be reliably printed; the vast majority of the more than 5,500 alloys in use today cannot be additively manufactured because the melting and solidification dynamics during the printing process lead to intolerable microstructures with large columnar grains and periodic cracks. Here we demonstrate that these issues can be resolved by introducing nanoparticles of nucleants that control solidification during additive manufacturing. We selected the nucleants on the basis of crystallographic information and assembled them onto 7075 and 6061 series aluminium alloy powders. After functionalization with the nucleants, we found that these high-strength aluminium alloys, which were previously incompatible with additive manufacturing, could be processed successfully using selective laser melting. Crack-free, equiaxed (that is, with grains roughly equal in length, width and height), fine-grained microstructures were achieved, resulting in material strengths comparable to that of wrought material. Our approach to metal-based additive manufacturing is applicable to a wide range of alloys and can be implemented using a range of additive machines. It thus provides a foundation for broad industrial applicability, including where electron-beam melting or directed-energy-deposition techniques are used instead of selective laser melting, and will enable additive manufacturing of other alloy systems, such as non-weldable nickel

  17. Photochemical preparation of aluminium oxide layers via vacuum ultraviolet irradiation of a polymeric hexanoato aluminium complex

    International Nuclear Information System (INIS)

    Wennrich, L.; Khalil, H.; Bundesmann, C.; Decker, U.; Gerlach, J.W.; Helmstedt, U.; Manova, D.; Naumov, S.; Prager, L.

    2013-01-01

    By means of photochemical conversion of thin layers of a polymeric hexanoato aluminium complex as the precursor, thin aluminium oxide layers were prepared onto silicon wafers. The precursor compound was synthesized and characterized by several analytical techniques like NMR, FTIR, XPS, ICP, and found to be a polymeric aluminium-containing coordination compound which has been proposed to be a hydroxo-bridged aluminium chain with pendant hexanoyl side-chains ascertained as catena-poly[{di(κ-O,O-hexanoato)aluminium}(μ-hydroxo)] (PHAH). Thin layers deposited from a solution of PHAH in toluene onto silicon wafers were irradiated using VUV radiation from a xenon excimer lamp. The layers were characterized by XPS, XRD, XRR, and spectroscopic ellipsometry. VUV radiation with a radiant exposure of E = 36 J cm −2 led to almost carbon-free amorphous layers with a composition close to that of alumina having a density of about 2.1 g cm −3 . Thus, using the example of a polymeric aluminium complex, the potential of the photochemical conversion of metal complexes into oxides could be shown as an alternative method, in addition to sol–gel techniques, for the generation of thin plane metal-oxide layers at normal temperature and pressure. Highlights: ► A polymeric aluminium complex was synthesized and characterized by NMR, FTIR, XPS and ICP. ► Thin layers of the compound were irradiated using vacuum-UV radiation and converted to AlO x . ► Quantum-chemical calculations explain the conversion mechanism.

  18. Aluminium in brain tissue in familial Alzheimer's disease.

    Science.gov (United States)

    Mirza, Ambreen; King, Andrew; Troakes, Claire; Exley, Christopher

    2017-03-01

    The genetic predispositions which describe a diagnosis of familial Alzheimer's disease can be considered as cornerstones of the amyloid cascade hypothesis. Essentially they place the expression and metabolism of the amyloid precursor protein as the main tenet of disease aetiology. However, we do not know the cause of Alzheimer's disease and environmental factors may yet be shown to contribute towards its onset and progression. One such environmental factor is human exposure to aluminium and aluminium has been shown to be present in brain tissue in sporadic Alzheimer's disease. We have made the first ever measurements of aluminium in brain tissue from 12 donors diagnosed with familial Alzheimer's disease. The concentrations of aluminium were extremely high, for example, there were values in excess of 10μg/g tissue dry wt. in 5 of the 12 individuals. Overall, the concentrations were higher than all previous measurements of brain aluminium except cases of known aluminium-induced encephalopathy. We have supported our quantitative analyses using a novel method of aluminium-selective fluorescence microscopy to visualise aluminium in all lobes of every brain investigated. The unique quantitative data and the stunning images of aluminium in familial Alzheimer's disease brain tissue raise the spectre of aluminium's role in this devastating disease. Copyright © 2016 The Authors. Published by Elsevier GmbH.. All rights reserved.

  19. Toxicity of dissolved and precipitated aluminium to marine diatoms.

    Science.gov (United States)

    Gillmore, Megan L; Golding, Lisa A; Angel, Brad M; Adams, Merrin S; Jolley, Dianne F

    2016-05-01

    Localised aluminium contamination can lead to high concentrations in coastal waters, which have the potential for adverse effects on aquatic organisms. This research investigated the toxicity of 72-h exposures of aluminium to three marine diatoms (Ceratoneis closterium (formerly Nitzschia closterium), Minutocellus polymorphus and Phaeodactylum tricornutum) by measuring population growth rate inhibition and cell membrane damage (SYTOX Green) as endpoints. Toxicity was correlated to the time-averaged concentrations of different aluminium size-fractions, operationally defined as aluminium exposure varied between diatom species. C. closterium was the most sensitive species (10% inhibition of growth rate (72-h IC10) of 80 (55-100)μg Al/L (95% confidence limits)) while M. polymorphus (540 (460-600)μg Al/L) and P. tricornutum (2100 (2000-2200)μg Al/L) were less sensitive (based on measured total aluminium). Dissolved aluminium was the primary contributor to toxicity in C. closterium, while a combination of dissolved and precipitated aluminium forms contributed to toxicity in M. polymorphus. In contrast, aluminium toxicity to the most tolerant diatom P. tricornutum was due predominantly to precipitated aluminium. Preliminary investigations revealed the sensitivity of C. closterium and M. polymorphus to aluminium was influenced by initial cell density with aluminium toxicity significantly (paluminium toxicity to diatoms do not involve compromising the plasma membrane. These results indicate that marine diatoms have a broad range in sensitivity to aluminium with toxic mechanisms related to both dissolved and precipitated aluminium. Copyright © 2016 Elsevier B.V. All rights reserved.

  20. Formation of aluminium nitride and segregation of Cu impurity atoms in aluminium implanted by high dose nitrogen ions

    International Nuclear Information System (INIS)

    Lin Chenglu; Hemment, P.L.F.; Li Jinhua; Zou Shichang

    1994-01-01

    Aluminium films with a thickness of 7000 A (containing 0.85% copper) were deposited on silicon substrates. 400 keV N 2 + or 350 keV N + ions were implanted into the aluminium films or at the interface between the aluminium and silicon, respectively. Automatic spreading resistance (ASR), Fourier transform infrared spectroscopy (FTIR) and Rutherford backscattering (RBS) and channelling were used to characterize the formation of aluminium nitride and the depth distribution of the Cu impurity in the aluminium films after ion implantation and post-annealing. The formation of a stoichiometric AlN layer with high resistance was evident from ASR, RBS analysis and FTIR measurements by the presence of the absorption band at 650 cm -1 . When the implanted nitrogen is near the interface between the aluminium and silicon, a multilayer structure can be obtained, which consists of aluminium, aluminium nitride and the silicon substrate. Cu, which is a background impurity in the deposited aluminium films, segregated into the synthesised aluminium nitride during high dose nitrogen ion implantation. This is due to irradiation-induced segregation during ion implantation. (orig.)

  1. [Association between serum aluminium level and methylation of amyloid precursor protein gene in workers engaged in aluminium electrolysis].

    Science.gov (United States)

    Yang, X J; Yuan, Y Z; Niu, Q

    2016-04-20

    To investigate the association between serum aluminium level and methylation of the promoter region of amyloid precursor protein (APP)gene in workers engaged in aluminium electrolysis. In 2012, 366 electrolysis workers in an aluminium factory were enrolled as exposure group (working years >10 and age >40 years)and divided into low-exposure group and high-exposure group based on the median serum aluminium level. Meanwhile, 102 workers in a cement plant not exposed to aluminium were enrolled as control group. Graphite furnace atomic absorption spectrometry was used to measure serum aluminium level, methylation specific PCR was used to measure the methylation rate of the promoter region of APP gene, and ELI-SA was used to measure the protein expression of APP in lymphocytes in peripheral blood. The exposure group had a significantly higher serum aluminium level than the control group (45.07 μg/L vs 30.51 μg/L, P0.05). The multivariate logistic regression analysis showed that with reference to the control group, low aluminium exposure (OR=1.86, 95% CI 1.67~3.52)and high aluminium exposure (OR=2.98, 95% CI 1.97~4.15)were risk factors for a reduced methylation rate of the promoter region of APP gene. Reduced methylation of the promoter region of APP gene may be associated with increased serum aluminium level, and downregulated methylation of the promoter region of APP gene may accelerate APP gene transcription.

  2. High temperature internal friction in pure aluminium

    International Nuclear Information System (INIS)

    Aboagye, J.K.; Payida, D.S.

    1982-05-01

    The temperature dependence of internal friction of nearly pure aluminium (99.99% aluminium) has been carefully measured as a function of annealing temperature and hence grain size. The results indicate that, provided the frequency and annealing temperature are held constant, the internal friction increases with temperature until some maximum value is attained and then begins to go down as the temperature is further increased. It is also noted that the internal friction decreases with annealing temperature and that annealing time has the same effect as annealing temperature. It is also noted that the internal friction peak is shifted towards higher temperatures as annealing temperature is increased. It is surmised that the grain size or the total grain boundary volume determines the height of the internal friction curve and that the order-disorder transitions at the grain boundaries induced by both entropy and energy gradients give rise to internal friction peaks in polycrystals. (author)

  3. Mechanical properties of aluminium honeycomb impact limiters

    International Nuclear Information System (INIS)

    Maji, A.K.; Satpathi, D.; Donald, S.

    1992-01-01

    Aluminium honeycombs have been extensively used as impact limiters in nuclear waste transport casks. The mechanical behaviour of these shock absorbing materials was studied to develop an extensive experimental database. A series of tests were performed along various loading paths. Different densities of aluminium honeycombs were tested in different orientations. Static tests included uniaxial tension, uniaxial compression and torsion. Dynamic tests were conducted at different strain rates of up to 100 s -1 , to generate experimental data relevant to accident situations. Dynamic studies included the effects of specimen size and confinement. The purpose of using different loading paths was to generate an extensive experimental database which may also be used to develop constitutive models for these materials. Design charts were constructed which can be accessed by various cask designers to optimise and economise on cask development. (Author)

  4. Diagnostics of ytterbium/aluminium laser plasmas

    International Nuclear Information System (INIS)

    Bailey, J.; Lee, R.W.; Landen, O.L.; Kilkenny, J.D.; Lewis, C.L.; Busquet, M.

    1986-11-01

    Microdot spectroscopy was used to study the x-ray emission from laser-produced plasmas consisting of 10% ytterbium, 90% aluminium. Spectra were recorded with a space-resolving flat crystal (PET) mini-spectrometer in the 4.0-8.0 A range. The Janus research laser at LLNL irradiated the targets with green (0.53 μm) light in a 1 nsec pulse. The power density was varied between 4x10 13 and 3x10 14 W/cm 2 . The plasma electron density and temperature were determined from the aluminium XI, XII and XIII line emission. By examining correlations between changes in the plasma conditions with changes in the ytterbium spectra, we will determine the potential for using ytterbium line emission as a plasma diagnostic

  5. Texture investigation in aluminium and iron - silicon samples by neutron diffraction technique

    International Nuclear Information System (INIS)

    Pugliese, R.; Yamasaki, J.M.

    1988-09-01

    By means of the neutron diffraction technique the texture of 5% and 98% rolled-aluminium and of iron-silicon steel used in the core of electric transformers, have been determined. The measurements were performed by using a neutron diffractometer installed at the IEA-R1 Nuclear Research Reactor, in the Beam-Hole n 0 . 6. To avoid corrections such as neutron absorption and sample luminosity the geometric form of the samples were approximated to spheric or octagonal prism, and its dimensions do not exceed that of the neutron beam. The texture of the samples were analysed with the help of a computer programme that analyses the intensity of the diffracted neutron beam and plot the pole figures. (author) [pt

  6. Swedish research on aluminium reactor technology

    International Nuclear Information System (INIS)

    Forsen, Bjoern

    1960-02-01

    A historical survey of the work done in Sweden this subject is given in the first part of the paper. The second part is elevated to a brief outline of the authors view of the present status of corrosion theories for aluminium in high temperature water. A theory where the crystallization of boehemite from the barrier layer is considered as an important control of the corrosion reaction is presented

  7. Simulation of aluminium STIR casting technique

    International Nuclear Information System (INIS)

    Hafizal Yazid; Mohd Harun; Hanani Yazid; Abd Aziz Mohamed; Muhammad Rawi Muhammad Zain; Zaiton Selamat; Mohd Shariff Sattar; Muhamad Jalil; Ismail Mustapha; Razali Kasim

    2006-01-01

    In this paper, the objective is to determine the optimum impeller speed correlated with holding time to achieve homogeneous reinforcement distribution for a particular set of experimental condition. Attempts are made to simulate the flow behaviourof the liquid aluminium using FLUENT software. Stepwise impeller speed ranging from 50 to 300 rpm.with 2 impeller angle blades of 45 and 90 degree with respect to the rotational plane were used

  8. Swedish research on aluminium reactor technology

    Energy Technology Data Exchange (ETDEWEB)

    Forsen, Bjoern

    1960-02-15

    A historical survey of the work done in Sweden this subject is given in the first part of the paper. The second part is elevated to a brief outline of the authors view of the present status of corrosion theories for aluminium in high temperature water. A theory where the crystallization of boehemite from the barrier layer is considered as an important control of the corrosion reaction is presented.

  9. Aluminium phosphide poising: a case report

    International Nuclear Information System (INIS)

    Hirani, S.A.A.; Rahman, A.

    2010-01-01

    This paper reports the case of a family in which three children were presented at Emergency Room (ER) with poisoning after the use of a pesticide at home. Initially, the cases were managed as routine cases of organophosphorus poisoning; however, the death of two children made the health team members realise that the poison's effects were delayed and devastating. Later, the compound was identified as Aluminium Phosphide (ALP), and the life of the last surviving child in the family was saved. (author)

  10. Implementation of Video Monitoring In Aluminium Industry

    OpenAIRE

    Hedlund, Ann; Andersson, Ing-Marie; Rosén, Gunnar

    2015-01-01

    The aim was to evaluate results and experiences from development of new technology, a training program and implementation of strategies for the use of a video exposure monitoring method, PIMEX. Starting point of this study is an increased incidence of asthma among workers in the aluminium industry. Exposure peaks of fumes are supposed to play an important role. PIMEX makes it possible to link used work practice, use of control technology, and so forth to peaks. Nine companies participated in ...

  11. Complexometric determination of scandium and aluminium

    International Nuclear Information System (INIS)

    Tikhonov, V.N.

    1980-01-01

    Described is the complexometric determination of scandium and aluminium by the method of reverse titration of EDTA excess by indium salt solution in the presence of the xylenol orange indicator. For the method selectivity increase fluorides are used as a camouflage substance at low pH values (2.5-3.0). The excess fluoride-ions preventing titration are bound by boric acid. Y, Tb, Ti, Zr, Cu, Zn, V, Mo, Co, Cr prevent the determination of Sc and Al

  12. Helium behaviour in aluminium under hydrostatic pressure

    International Nuclear Information System (INIS)

    Sokurskij, Yu.N.; Tebus, V.N.; Zudilin, V.A.; Tumanova, G.M.

    1989-01-01

    Effect of hydrostatic compression on equilibrium helium bubbles in low aluminium-lithium alloy irradiated in reactor at 570 K is investigated. Measurements of hydrostatic density and electron-microscopic investigations have shown, that application of up to 2 GPa pressure reduces equilibrium size of helium bubbles and reduces helium swelling. Kinetics and thermodynamics of the process are considered with application of 'rigid sphere' equation which describes helium state in bubbles

  13. Feet sunk in molten aluminium: The burn and its prevention.

    Science.gov (United States)

    Alonso-Peña, David; Arnáiz-García, María Elena; Valero-Gasalla, Javier Luis; Arnáiz-García, Ana María; Campillo-Campaña, Ramón; Alonso-Peña, Javier; González-Santos, Jose María; Fernández-Díaz, Alaska Leonor; Arnáiz, Javier

    2015-08-01

    Nowadays, despite improvements in safety rules and inspections in the metal industry, foundry workers are not free from burn accidents. Injuries caused by molten metals include burns secondary to molten iron, aluminium, zinc, copper, brass, bronze, manganese, lead and steel. Molten aluminium is one of the most common causative agents of burns (60%); however, only a few publications exist concerning injuries from molten aluminium. The main mechanisms of lesion from molten aluminium include direct contact of the molten metal with the skin or through safety apparel, or when the metal splash burns through the pants and rolls downward along the leg. Herein, we report three cases of deep dermal burns after 'soaking' the foot in liquid aluminium and its evolutive features. This paper aims to show our experience in the management of burns due to molten aluminium. We describe the current management principles and the key features of injury prevention. Copyright © 2014 Elsevier Ltd and ISBI. All rights reserved.

  14. What is the risk of aluminium as a neurotoxin?

    Science.gov (United States)

    Exley, Christopher

    2014-06-01

    Aluminium is neurotoxic. Its free ion, Al(3+) (aq), is highly biologically reactive and uniquely equipped to do damage to essential cellular (neuronal) biochemistry. This unequivocal fact must be the starting point in examining the risk posed by aluminium as a neurotoxin in humans. Aluminium is present in the human brain and it accumulates with age. The most recent research demonstrates that a significant proportion of individuals older than 70 years of age have a potentially pathological accumulation of aluminium somewhere in their brain. What are the symptoms of chronic aluminium intoxication in humans? What if neurodegenerative diseases such as Alzheimer's disease are the manifestation of the risk of aluminium as a neurotoxin? How might such an (outrageous) hypothesis be tested?

  15. Modelling of heterogeneous clustering in aluminium

    International Nuclear Information System (INIS)

    Smith, A.E.; Bourgeois, L.; Nie, J.-F.; Muddle, B.C.

    2003-01-01

    Full text: Ab initio modelling of heterogeneous clustering in aluminium has been carried out in order to study the precipitation hardening of alloys. This process is based on the addition of small amounts of solute element to the pure metal. With increasing computational power, atomic scale effects can now be better simulated to determine the nature of the hardening mechanism. Comparisons are made between results obtained from two computational packages. These are the Linear Augmented Plane Wave WEEN2K and the plane wave pseudopotential density functional theory package fhi98md. The study of the optimal geometry of very small size clusters inside aluminium has begun with the testing of initial convergence conditions by determination of binding energies for a variety of super cell sizes of the aluminium host crystal. These are compared with total energy calculations for small size precipitates of copper and transition metals of fixed geometry. Such local optimal determinations are seen as precursors to full Monte Carlo calculations of the notional best local geometry for larger precipitates

  16. Grain distinct stratified nanolayers in aluminium alloys

    Energy Technology Data Exchange (ETDEWEB)

    Donatus, U., E-mail: uyimedonatus@yahoo.com [School of Materials, The University of Manchester, Manchester, M13 9PL, England (United Kingdom); Thompson, G.E.; Zhou, X.; Alias, J. [School of Materials, The University of Manchester, Manchester, M13 9PL, England (United Kingdom); Tsai, I.-L. [Oxford Instruments NanoAnalysis, HP12 2SE, High Wycombe (United Kingdom)

    2017-02-15

    The grains of aluminium alloys have stratified nanolayers which determine their mechanical and chemical responses. In this study, the nanolayers were revealed in the grains of AA6082 (T6 and T7 conditions), AA5083-O and AA2024-T3 alloys by etching the alloys in a solution comprising 20 g Cr{sub 2}O{sub 3} + 30 ml HPO{sub 3} in 1 L H{sub 2}O. Microstructural examination was conducted on selected grains of interest using scanning electron microscopy and electron backscatter diffraction technique. It was observed that the nanolayers are orientation dependent and are parallel to the {100} planes. They have ordered and repeated tunnel squares that are flawed at the sides which are aligned in the <100> directions. These flawed tunnel squares dictate the tunnelling corrosion morphology as well as appearing to have an affect on the arrangement and sizes of the precipitation hardening particles. The inclination of the stratified nanolayers, their interpacing, and the groove sizes have significant influence on the corrosion behaviour and seeming influence on the strengthening mechanism of the investigated aluminium alloys. - Highlights: • Stratified nanolayers in aluminium alloy grains. • Relationship of the stratified nanolayers with grain orientation. • Influence of the inclinations of the stratified nanolayers on corrosion. • Influence of the nanolayers interspacing and groove sizes on hardness and corrosion.

  17. Investigation and in situ removal of spatter generated during laser ablation of aluminium composites

    International Nuclear Information System (INIS)

    Popescu, A.C.; Delval, C.; Shadman, S.; Leparoux, M.

    2016-01-01

    Highlights: • Study of spatter generated during laser irradiation of an aluminium nanocomposite. • Number of droplets was 1.5–3 times higher for laser in depth vs surface focused beams. • High speed imaging revealed particles exploding in flight similar to a fireworks effect. • Three methods were selected for droplets removal in situ and the results are analyzed. - Abstract: Spatter generated during laser irradiation of an aluminium alloy nanocomposite (AlMg5 reinforced with Al_2O_3 nanoparticles) was monitored by high speed imaging. Droplets trajectory and speed were assessed by computerized image analysis. The effects of laser peak power and laser focusing on the plume expansion and expulsed droplet speeds were studied in air or under argon flow. It was found that the velocity of visible droplets expulsed laterally or at the end of the plume emission from the metal surface was not dependent on the plasma plume speed. The neighbouring area of irradiation sites was studied by optical and scanning electron microscopy. Droplets deposited on the surface were classified according to their size and counted using a digital image processing software. It was observed that the number of droplets on surface was 1.5–3 times higher when the laser beam was focused in depth as compared to focused beams, even though the populations average diameter were comparable. Three methods were selected for removing droplets in situ, during plume expansion: an argon gas jet crossing the plasma plume, a fused silica plate collector transparent to the laser wavelength placed parallel to the irradiated surface and a mask placed onto the aluminium composite surface. The argon gas jet was efficient only for low power irradiation conditions, the fused silica plate failed in all tested conditions and the mask was successful for all irradiation regimes.

  18. Corrosion of Metal-Matrix Composites with Aluminium Alloy Substrate

    Directory of Open Access Journals (Sweden)

    B. Bobic

    2010-03-01

    Full Text Available The corrosion behaviour of MMCs with aluminium alloy matrix was presented. The corrosion characteristics of boron-, graphite-, silicon carbide-, alumina- and mica- reinforced aluminium MMCs were reviewed. The reinforcing phase influence on MMCs corrosion rate as well as on various corrosion forms (galvanic, pitting, stress corrosion cracking, corrosion fatique, tribocorrosion was discussed. Some corrosion protection methods of aluminium based MMCs were described

  19. Multiply-negatively charged aluminium clusters and fullerenes

    Energy Technology Data Exchange (ETDEWEB)

    Walsh, Noelle

    2008-07-15

    Multiply negatively charged aluminium clusters and fullerenes were generated in a Penning trap using the 'electron-bath' technique. Aluminium monoanions were generated using a laser vaporisation source. After this, two-, three- and four-times negatively charged aluminium clusters were generated for the first time. This research marks the first observation of tetra-anionic metal clusters in the gas phase. Additionally, doubly-negatively charged fullerenes were generated. The smallest fullerene dianion observed contained 70 atoms. (orig.)

  20. The aluminium content of infant formulas remains too high.

    Science.gov (United States)

    Chuchu, Nancy; Patel, Bhavini; Sebastian, Blaise; Exley, Christopher

    2013-10-08

    Recent research published in this journal highlighted the issue of the high content of aluminium in infant formulas. The expectation was that the findings would serve as a catalyst for manufacturers to address a significant problem of these, often necessary, components of infant nutrition. It is critically important that parents and other users have confidence in the safety of infant formulas and that they have reliable information to use in choosing a product with a lower content of aluminium. Herein, we have significantly extended the scope of the previous research and the aluminium content of 30 of the most widely available and often used infant formulas has been measured. Both ready-to-drink milks and milk powders were subjected to microwave digestion in the presence of 15.8 M HNO3 and 30% w/v H2O2 and the aluminium content of the digests was measured by TH GFAAS. Both ready-to-drink milks and milk powders were contaminated with aluminium. The concentration of aluminium across all milk products ranged from ca 100 to 430 μg/L. The concentration of aluminium in two soya-based milk products was 656 and 756 μg/L. The intake of aluminium from non-soya-based infant formulas varied from ca 100 to 300 μg per day. For soya-based milks it could be as high as 700 μg per day. All 30 infant formulas were contaminated with aluminium. There was no clear evidence that subsequent to the problem of aluminium being highlighted in a previous publication in this journal that contamination had been addressed and reduced. It is the opinion of the authors that regulatory and other non-voluntary methods are now required to reduce the aluminium content of infant formulas and thereby protect infants from chronic exposure to dietary aluminium.

  1. Improvement of photodynamic activity of aluminium sulphophthalocyanine due to biotinylation

    Science.gov (United States)

    Meerovich, Irina G.; Jerdeva, Victoria V.; Derkacheva, Valentina M.; Meerovich, Gennadii A.; Lukyanets, Eugeny A.; Kogan, Eugenia A.; Savitsky, Alexander P.

    2003-09-01

    The photodynamic activity of dibiotinylated aluminium sulphophthalocyanine in vitro and in vivo were studied. It was obtained that in vitro dibiotinylated aluminium sulphophthalocyanine provides the effective damage of small cell lung carcinoma OAT-75. In vivo dibiotinylated aluminium sulphophthalocyanine causes destruction of tumor (Erlich carcinoma), results in total necrosis of tumor tissue and expresses vascular damage (trombosis and destruction of vascular walls) even in concentration 0.25 mg/kg of a body weight.

  2. Remediation of phosphate-contaminated water by electrocoagulation with aluminium, aluminium alloy and mild steel anodes.

    Science.gov (United States)

    Vasudevan, Subramanyan; Lakshmi, Jothinathan; Jayaraj, Jeganathan; Sozhan, Ganapathy

    2009-05-30

    The present study provides an electrocoagulation process for the remediation of phosphate-contaminated water using aluminium, aluminium alloy and mild steel as the anodes and stainless steel as the cathode. The various parameters like effect of anode materials, effect of pH, concentration of phosphate, current density, temperature and co-existing ions, and so forth, and the adsorption capacity was evaluated using both Freundlich and Langmuir isotherm models. The adsorption of phosphate preferably fitting the Langmuir adsorption isotherm suggests monolayer coverage of adsorbed molecules. The results showed that the maximum removal efficiency of 99% was achieved with aluminium alloy anode at a current density of 0.2 A dm(-2), at a pH of 7.0. The adsorption process follows second-order kinetics.

  3. Diffusion bonding of transition structures for integral aluminium-fibre reinforced polymer (FRP) compounds

    Energy Technology Data Exchange (ETDEWEB)

    Hehl, A. von [IWT - Stiftung Institut fuer Werkstofftechnik, Hauptabteilung Werkstofftechnik, Bremen (Germany); Syassen, F. [Airbus Operations GmbH, Metal Technology, Bremen (Germany); Schimanski, K.

    2012-04-15

    Components in hybrid design become more and more important in terms of their lightweight potential. In this context the demand for weight saving in aerospace leads to increasing numbers of applications of fibre composites for primary structural components. In consequence the use of FRP-metal compounds is necessary. Within the investigations of the researcher group ''Schwarz Silber'' (FOR 1224) founded by the DFG (German Research Foundation) material optimised interface structures for advanced CFRP-aluminium compounds are currently being studied. Within their work the researcher group focussed on three concepts realizing the transition structures: the usage of wires (titanium), foils (titanium) and fibres (glass fibre) as transition elements between CFRP and aluminium. For the connection of the aluminium sheet and the transition element die-casting and laser beam welding are basically used. As a possible alternative to the both liquid phase processes a feasibility study haven been done focussing the solid state processes diffusion bonding. The experimental results show the high potential of this process in view of the transferable loads for integral transition structures. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  4. Argon-arc welding of heat resisting aluminium alloys

    International Nuclear Information System (INIS)

    Ryazantsev, V.I.; Fedoseev, V.A.

    1997-01-01

    Welding of aluminium heat resisting alloys of the Al-Cu-Mg system is studied. The hot-shortness of heat-resistant alloys M40, 1150 and 1151 are at the level of aluminium alloys 1201 and by 2-3 times lower as compared to the aluminium alloy AMg6. The M40, 1150 and 1151 alloys have unquestionable advantages against other know aluminium alloys only at temperatures of welded structures operation, beginning with 150-2000 deg C and especially at 250 deg C

  5. Beryllium electrodeposition on aluminium cathode from chloride melts

    International Nuclear Information System (INIS)

    Nichkov, I.F.; Novikov, E.A.; Serebryakov, G.A.; Kanashin, Yu.P.; Sardyko, G.N.

    1980-01-01

    Cathodic processes during beryllium deposition on liquid and solid aluminium cathodes are investigated. Mixture of sodium, potassium and beryllium chloride melts served as an lectrolyte. Beryllium ion discharge at the expense of alloy formation takes place at more positive potentials than on an indifferent cathode at low current densities ( in the case of liquid aluminium cathode). Metallographic analysis and measurements of microhardness have shown, that the cathodic product includes two phases: beryllium solid solution in aluminium and metallic beryllium. It is concluded, that aluminium-beryllium alloys with high cathodic yield by current can be obtained by the electrolytic method

  6. [Determination of aluminium in flour foods with photometric method].

    Science.gov (United States)

    Ma, Lan; Zhao, Xin; Zhou, Shuang; Yang, Dajin

    2012-05-01

    To establish a determination method for aluminium in flour foods with photometric method. After samples being treated with microwave digestion and wet digestion, aluminium in staple flour foods was determined by photometric method. There was a good linearity of the result in the range of 0.25 - 5.0 microg/ml aluminium, r = 0.9998; limit of detection (LOD) : 2.3 ng/ml; limit of quantitation (LOQ) : 7 ng/ml. This method of determining aluminium in flour foods is simple, rapid and reliable.

  7. Effect of smelt aluminium on mechanical properties of steels

    International Nuclear Information System (INIS)

    Ryabov, V.R.; Dykhno, I.S.; Deev, G.F.; Karikh, V.V.

    1987-01-01

    Effect of smelt aluminium on mechanical properties of armco-iron and 12 Kh18N10T steel is studied. It is stated that in smelt aluminium and aluminium alloy contact with armco-iron the sample ductility is decreased. Corrosion effect of smelt alluminium on (18Kh15N5AM3) steel in the form of reinforced wire in aluminium-steel KAS-1A composite material is investigted. It is stated in experiment that during smelt alluminium-steel contact interaction of heterogeneous phases takes place

  8. Investigation process of alcoholysis of hydride aluminium-adobe

    International Nuclear Information System (INIS)

    Numanov, M.I.; Normatov, I.Sh.; Mirsaidov, U.M.

    2001-01-01

    Considering of that process of acid treatment of aluminium-adobe hydride realizes in the ethyl alcohol media it was necessary study the process of alcoholysis of AlH 3 and aluminium additives. In the end of article authors became to conclusion that deficiency of spontaneous alcoholysis of AlH 3 in adobe caused by protective action of fiber; solvate ability of LiCl and alkoxy aluminium hydride of lithium-LiCl·CO 2 H 5 OH, Li Al(OC 2 H 5 ) 4 ·nC 2 H 5 OH decreasing the expectancy of responding of alcohol with aluminium hydride

  9. Friction stir welding (FSW of aluminium foam sandwich panels

    Directory of Open Access Journals (Sweden)

    M. Bušić

    2016-07-01

    Full Text Available The article focuses on the influence of welding speed and tool tilt angle upon the mechanical properties at the friction stir welding of aluminium foam sandwich panels. Double side welding was used for producing butt welds of aluminium sandwich panels applying insertion of extruded aluminium profile. Such insertion provided lower pressure of the tool upon the aluminium panels, providing also sufficient volume of the material required for the weldment formation. Ultimate tensile strength and flexural strength for three-point bending test have been determined for samples taken from the welded joints. Results have confirmed anticipated effects of independent variables.

  10. MODELLING STUDIES ON THE USE OF ALUMINIUM ALLOYS IN LIGHTWEIGHT LOAD-CARRYING CRANE STRUCTURES

    Directory of Open Access Journals (Sweden)

    Damian GĄSKA

    2016-09-01

    Full Text Available The article presents the results of numerical analysis whose aim was to compare the basic dynamic and strength parameters of lightweight load-carrying crane structures made of aluminium alloys and steel. The analysis covered the typical construction of workshop cranes with a span of 3 to 5 meters, girders in the form of an I-beam and maximum load capacities amounting to 5 tons. The values of stresses, deflections and natural frequencies were compared and then matched with the masses of the various structures. In the simulation a girder model was used and computed by the finite element method.

  11. Dielectric aluminium phosphate thin films. Couches minces dielectriques de phosphate d'aluminium

    Energy Technology Data Exchange (ETDEWEB)

    Daviero, S. (Lab. Physicochimie des Materiaux Solides, 34 - Montpellier (France)); Avinens, C. (Lab. Physicochimie des Materiaux Solides, 34 - Montpellier (France)); Ibanez, A. (Lab. Physicochimie des Materiaux Solides, 34 - Montpellier (France)); Giuntini, J.C. (Lab. Physicochimie des Materiaux Solides, 34 -Montpellier (France)); Philippot, E. (Lab. Physicochimie des Materiaux Solides, 34 - Montpellier (France))

    1993-04-01

    Aluminium phosphate thin films on silicium substrate have been carried out from tributylphosphate and aluminium acetylacetonate precursors in solution through the ''pyrosol'' process. It can be observed a large range of chemical analysis in terms of experimental conditions. These thin films have been characterized by X-ray diffraction and infrared spectrometry. Their electrical characteristics, defined from direct current and alternative current measurements, are quite different to those of the crystallized phosphate and can be explained by P-O and Al-O ''dangling bond'' existence. (orig.).

  12. Aluminium cables in automotive applications : Prestudy of aluminium cable uses in Scania products&Failure analysis and evaluation

    OpenAIRE

    Man, Yu

    2016-01-01

    The increasing demand of light constructed vehicles as well as soaring price of copper metal owing to limited nature resources have been promoting the use of aluminium metal as an alternative conductor of automotive cables. This thesis work is to lay theoretical foundations for further research and development regarding the introduction of new automotive cables i.e. aluminium cables. Current application of automotive aluminium cables in automotive industry as well as failure analysis and eval...

  13. There is (still too much aluminium in infant formulas

    Directory of Open Access Journals (Sweden)

    Burrell Shelle-Ann M

    2010-08-01

    Full Text Available Abstract Background Infant formulas are sophisticated milk-based feeds for infants which are used as a substitute for breast milk. Historically they are known to be contaminated by aluminium and in the past this has raised health concerns for exposed infants. We have measured the aluminium content of a number of widely used infant formulas to determine if their contamination by aluminium and consequent issues of child health persists. Methods Samples of ready-made milks and powders used to make milks were prepared by microwave digestion of acid/peroxide mixtures and their aluminium content determined by THGA. Results The concentration of aluminium in ready-made milks varied from ca 176 to 700 μg/L. The latter concentration was for a milk for preterm infants. The aluminium content of powders used to make milks varied from ca 2.4 to 4.3 μg/g. The latter content was for a soya-based formula and equated to a ready-to-drink milk concentration of 629 μg/L. Using the manufacturer's own guidelines of formula consumption the average daily ingestion of aluminium from infant formulas for a child of 6 months varied from ca 200 to 600 μg of aluminium. Generally ingestion was higher from powdered as compared to ready-made formulas. Conclusions The aluminium content of a range of well known brands of infant formulas remains high and particularly so for a product designed for preterm infants and a soya-based product designed for infants with cow's milk intolerances and allergies. Recent research demonstrating the vulnerability of infants to early exposure to aluminium serves to highlight an urgent need to reduce the aluminium content of infant formulas to as low a level as is practically possible.

  14. Effects of aluminium surface morphology and chemical modification on wettability

    Energy Technology Data Exchange (ETDEWEB)

    Rahimi, M., E-mail: mar@sbi.aau.dk [Department of Energy and Environment, Danish Building Research Institute, Aalborg University, A.C. Meyers Vænge 15, 2450 København SV (Denmark); Fojan, P.; Gurevich, L. [Department of Physics and Nanotechnology, Aalborg University, Skjernvej 4, DK-9220 Aalborg East (Denmark); Afshari, A. [Department of Energy and Environment, Danish Building Research Institute, Aalborg University, A.C. Meyers Vænge 15, 2450 København SV (Denmark)

    2014-03-01

    Highlights: • Successful surface modification procedures on aluminium samples were performed involving formation of the layer of hydrophilic hyperbranched polyethyleneglycol (PEG) via in situ polymerization, molecular vapour deposition of a monolayer of fluorinated silane, and a combination of those. • The groups of surfaces with hydrophobic behavior were found to follow the Wenzel model. • A transition from Cassie–Baxter's to Wenzel's regime was observed due to changing of the surface roughness upon mechanical polishing in aluminium samples. - Abstract: Aluminium alloys are some of the predominant metals in industrial applications such as production of heat exchangers, heat pumps. They have high heat conductivity coupled with a low specific weight. In cold working conditions, there is a risk of frost formation on the surface of aluminium in the presence of water vapour, which can lead to the deterioration of equipment performance. This work addresses the methods of surface modification of aluminium and their effect of the underlying surface morphology and wettability, which are the important parameters for frost formation. Three groups of real-life aluminium surfaces of different morphology: unpolished aluminium, polished aluminium, and aluminium foil, were subjected to surface modification procedures which involved the formation of a layer of hydrophilic hyperbranched polyethyleneglycol via in situ polymerization, molecular vapour deposition of a monolayer of fluorinated silane, and a combination of those. The effect of these surface modification techniques on roughness and wettability of the aluminium surfaces was elucidated by ellipsometry, contact angle measurements and atomic force microscopy. We demonstrated that by employing different types of surface modifications the contact angle of water droplets on aluminium samples can be varied from 12° to more than 120°. A crossover from Cassie–Baxter to Wenzel regime upon changing the surface

  15. Long-term effects of aluminium dust inhalation.

    Science.gov (United States)

    Peters, Susan; Reid, Alison; Fritschi, Lin; de Klerk, Nicholas; Musk, A W Bill

    2013-12-01

    During the 1950s and 1960s, aluminium dust inhalation was used as a potential prophylaxis against silicosis in underground miners, including in Australia. We investigated the association between aluminium dust inhalation and cardiovascular, cerebrovascular and Alzheimer's diseases in a cohort of Australian male underground gold miners. We additionally looked at pneumoconiosis mortality to estimate the effect of the aluminium therapy. SMRs and 95% CI were calculated to compare mortality of the cohort members with that of the Western Australian male population (1961-2009). Internal comparisons on duration of aluminium dust inhalation were examined using Cox regression. Aluminium dust inhalation was reported for 647 out of 1894 underground gold miners. During 42 780 person-years of follow-up, 1577 deaths were observed. An indication of increased mortality of Alzheimer's disease among miners ever exposed to aluminium dust was found (SMR=1.38), although it was not statistically significant (95% CI 0.69 to 2.75). Rates for cardiovascular and cerebrovascular death were above population levels, but were similar for subjects with or without a history of aluminium dust inhalation. HRs suggested an increasing risk of cardiovascular disease with duration of aluminium dust inhalation (HR=1.02, 95% CI 1.00 to 1.04, per year of exposure). No difference in the association between duration of work underground and pneumoconiosis was observed between the groups with or without aluminium dust exposure. No protective effect against silicosis was observed from aluminium dust inhalation. Conversely, exposure to aluminium dust may possibly increase the risk of cardiovascular disease and dementia of the Alzheimer's type.

  16. Characterization and structure of precipitates in 6xxx Aluminium Alloys

    International Nuclear Information System (INIS)

    Holmestad, Randi; Bjørge, Ruben; Ehlers, Flemming J H; Torsæter, Malin; Marioara, Calin D; Andersen, Sigmund J

    2012-01-01

    Solute atom nanoscale precipitates are responsible for the favourable mechanical properties of heat treatable aluminium alloys such as Al-Mg-Si (6xxx). The shape, structure and strengthening properties of age-hardening precipitates depend on alloy composition and thermo-mechanical history. We seek an improved understanding of the physics related to nucleation and precipitation on the atomistic level in these alloys. Once these mechanisms are sufficiently well described and understood, the hope is that 'alloy design' simulations can assist tailoring of materials with desired properties. In pure Al-Mg-Si we have determined the structure of nearly all the known metastable precipitate phases, by combining advanced TEM techniques (such as high resolution TEM and nano-beam diffraction) with atom probe tomography and density functional theory. We are now studying effects of additions /substitutions of Cu, Ag and/or Ge that promote formation of more disordered precipitates, employing aberration corrected high angle annular dark field scanning TEM. We find that all metastable precipitates contain variations of a widely spaced 'Si/Ge network'. In spite of disorder or defects, this network is surprisingly well ordered, with hexagonal projected sub-cell dimensions a = b ≅ 0.4 nm and c (along the fully coherent precipitate main growth direction) equal to 0.405 nm or a multiple of it.

  17. Mechanical properties of plasma-sprayed layers of aluminium and aluminium alloy on AZ 91

    Czech Academy of Sciences Publication Activity Database

    Kubatík, Tomáš František; Ctibor, Pavel; Mušálek, Radek; Janata, Marek

    2017-01-01

    Roč. 51, č. 2 (2017), s. 323-327 ISSN 1580-2949 R&D Projects: GA ČR(CZ) GP14-31538P Institutional support: RVO:61389021 Keywords : plasma spraying of aluminium * adhesion of coating * wear * magnesium alloy AZ91 Subject RIV: JG - Metallurgy OBOR OECD: Materials engineering Impact factor: 0.436, year: 2016

  18. Irradiation effects on the mechanical properties of aluminium and the structural integrity of aluminium reactor components

    International Nuclear Information System (INIS)

    Harrison, R.P.; McDonald, N.R.; Mitchell, D.R.G.; Hellier, A.K.; Stathers, P.A.; Carr, D.G.; Ripley, M.I.

    2000-01-01

    The results of micro-structural and mechanical property studies on aluminum after being exposed to large fluences of neutrons are presented. These property changes are of importance in determining the structural integrity of the Australian HIFAR reactor aluminium tank, which in turn determines the lifetime of the reactor. (author)

  19. Combined Corrosion and Wear of Aluminium Alloy 7075-T6

    NARCIS (Netherlands)

    Liu, Y.; Mol, J.M.C.; Janssen, G.C.A.M.

    2016-01-01

    The aluminium alloy 7075-T6 is widely used in engineering. In some applications, like slurry transport, corrosion and abrasion occur simultaneously, resulting in early material failure. In the present work, we investigated the combined effect of corrosion and wear on the aluminium alloy 7075-T6. We

  20. Sol gel synthesis for preparation of yttrium aluminium garnet

    NARCIS (Netherlands)

    Vrolijk, J.W.G.A.; Willems, J.W.M.M.; Metselaar, R.; With, de G.; Terpstra, R.A.; Metselaar, R.

    1989-01-01

    Sol-gel—synthesis for preparation of pure yttrium aluminium garnet powder with small grain size is subject of this ongoing study. Starting materials were sulfates and chlorides of yttrium and aluminium. To obtain pure YAG (Y3A1SO1Z) pH during hydrolysis as well as temperature during calcination and

  1. Three body abrasion of laser surface alloyed aluminium AA1200

    CSIR Research Space (South Africa)

    Mabhali, Luyolo AB

    2012-06-01

    Full Text Available Laser surface alloying of aluminium AA1200 was performed with a 4 kW Nd:YAG laser to improve the abrasion wear resistance. Aluminium surfaces reinforced with metal matrix composites and intermetallic phases were achieved. The phases present depended...

  2. The effects of aluminium and selenium supplementation on brain ...

    African Journals Online (AJOL)

    This in vivo study was designed to investigate the potential of aluminium (Al), in the absence of added iron, to participate in either antioxidant or pro-oxidant events. Some markers of oxidative stress were determined in liver and brain of rats exposed to aluminium lactate, either alone or in the presence of dietary supplements ...

  3. Aluminium and Alzheimer's disease: the science that describes the link

    National Research Council Canada - National Science Library

    Exley, Christopher

    2001-01-01

    ... that has been encircled is the gene for the amyloid precursor protein. (Thanks to Walter Lukiw for supplying this information.) Aluminium and Alzheimer's Disease: The Science that Describes the LinkAluminium and Alzheimer's Disease The Science that Describes the Link Edited by Christopher Exley Birchall Centre for Inorganic Chemistry and Materials Scienc...

  4. An interesting and efficient green corrosion inhibitor for aluminium ...

    African Journals Online (AJOL)

    An interesting and efficient green corrosion inhibitor for aluminium from extracts of ... Journal Home > Vol 13, No 1 (2014) > ... possible applications in metal surface anodizing and surface coating in industries. Keywords: Moringa oleifera, Aluminium, Hydrochloric acid, Langmuir isotherm, Plant extracts, Corrosion inhibition ...

  5. Synthesis of aluminium nanoparticles by arc evaporation of an ...

    Indian Academy of Sciences (India)

    Administrator

    Abstract. Aluminium nanoparticles (Al Nps) are synthesized using arc discharge method by applying direct current between aluminium electrodes in liquid environment without any use of vacuum equipment, heat exchangers, high temperatures furnaces and inert gases. After synthesis of Al Nps, in situ coating process on.

  6. Anodization of Aluminium using a fast two-step process

    Indian Academy of Sciences (India)

    283.6 eV. Keywords. Anodization; phosphoric acid; anodization time; anodized aluminium oxide; aluminium. ... of anodization.5–7 The AAO layer has a large band gap, good ..... transmittance increases as the anodised membrane is heated to ...

  7. Aluminium removal from water after defluoridation with the electrocoagulation process.

    Science.gov (United States)

    Sinha, Richa; Mathur, Sanjay; Brighu, Urmila

    2015-01-01

    Fluoride is the most electronegative element and has a strong affinity for aluminium. Owing to this fact, most of the techniques used for fluoride removal utilized aluminium compounds, which results in high concentrations of aluminium in treated water. In the present paper, a new approach is presented to meet the WHO guideline for residual aluminium concentration as 0.2 mg/L. In the present work, the electrocoagulation (EC) process was used for fluoride removal. It was found that aluminium content in water increases with an increase in the energy input. Therefore, experiments were optimized for a minimum energy input to achieve the target value (0.7 mg/L) of fluoride in resultant water. These optimized sets were used for further investigations of aluminium control. The experimental investigations revealed that use of bentonite clay as coagulant in clariflocculation brings down the aluminium concentration of water below the WHO guideline. Bentonite dose of 2 g/L was found to be the best for efficient removal of aluminium.

  8. Spark counting technique with an aluminium oxide film

    International Nuclear Information System (INIS)

    Kawai, H.; Koga, T.; Morishima, H.; Niwa, T.; Nishiwaki, Y.

    1980-01-01

    Automatic spark counting of etch-pits on a polycarbonate film produced by nuclear fission fragments is now used for neutron monitoring in several countries. A method was developed using an aluminium oxide film instead of a polycarbonate as the neutron detector. Aluminium oxide films were prepared as follows: A cleaned aluminium plate as an anode and a nickel plate as a cathode were immersed in dilute sulfuric acid solution and electric current flowed between the electrodes at 12degC for 10-30 minutes. Electric current density was about 10 mA/cm 2 . The aluminium plate was then kept in boiling water for 10-30 minutes for sealing. The thickness of the aluminium oxide layer formed was about 1μm. The aluminium plate attached to a plate of suitable fissionable material, such as uranium or thorium, was irradiated with neutrons and set in a usual spark counter for fission track counting. One electrode was the aluminium plate and the other was an aluminized polyester sheet. Sparked pulses were counted with a usual scaler. The advantage of using spark counting with an aluminium oxide film for neutron monitoring is rapid measurement of neutron exposure, since chemical etching which is indispensable for spark counting with a polycarbonate detector film, is not needed. (H.K.)

  9. Neutron activation analysis of baths forming conversion layer on aluminium

    International Nuclear Information System (INIS)

    Szilagyi, Istvan; Maleczki, Emil; Bodizs, Denes

    1988-01-01

    Chromate layers were formed on the surface of aluminium using yellow and green chromating solutions. For the determination of the aluminium content neutron activation method was used. Nuclear effects disturbing the determination were eliminated by double irradiation technique. (author) 8 refs.; 4 figs

  10. Friction stir welding of single crystal aluminium

    DEFF Research Database (Denmark)

    Fonda, Richard Warren; Wert, John A.; Reynolds, A.P.

    2007-01-01

    Friction stir welds were prepared in different orientations in an aluminium single crystal. The welds were quenched to preserve the microstructure surrounding the tool and then electron backscattered diffraction was used to reveal the generation of grain boundaries and the evolution...... of crystallographic texture around the tool in each weld. The extent of both dynamic recrystallisation and conventional recrystallisation varied considerably as a function of weld orientation. As the base plate begins to interact with the deformation field surrounding the tool, regions of the single crystal rotate...

  11. Structure of the aluminium-uranium eutectic

    International Nuclear Information System (INIS)

    Ambrozio Filho, F.; Vieira, R.R.

    1975-01-01

    The authors discuss the factors which might effect the eutectic structure, including external conditions during solidification as well as factors peculiar to each individual system. They studied the structure of the A1-U eutectic, consisting of the solid solution of uranium in aluminium and UA1 4 , as obtained in ingot moulds and by unidirectional solidification, and found a tendency for the structure to develop in a spiral, in the form of a rhombus. They discuss this structure in terms of certain variables with emphasis on the growth characteristics of the phases comprising the eutectic, the velocity of growth and thermal gradient in the liquid [pt

  12. Convenient synthesis of deuterated aluminium hydrides

    Energy Technology Data Exchange (ETDEWEB)

    Pawelke, Roland H.; Felderhoff, Michael; Weidenthaler, Claudia [Max-Planck-Institut fuer Kohlenforschung, Kaiser-Wilhelm-Platz 1, 45470 Muelheim an der Ruhr (Germany); Schueth, Ferdi [Max-Planck-Institut fuer Kohlenforschung, Kaiser-Wilhelm-Platz 1, 45470 Muelheim an der Ruhr (Germany)], E-mail: schueth@mpi-muelheim.mpg.de

    2008-09-15

    We describe the ball-milling synthesis of alkali metal deuterides from commercial lithium aluminium deuteride. This reaction principle was exemplified by the mechanochemical synthesis of NaAlD{sub 4} and KAlD{sub 4}. NaAlD{sub 4} was prepared on the multi-gram scale by this procedure and purified by standard wet-chemical separation. Pure NaAlD{sub 4} was obtained and used for the synthesis of Ca(AlD{sub 4}){sub 2}. The formation of all products was verified by X-ray diffraction.

  13. Deviatoric response of the aluminium alloy, 5083

    Science.gov (United States)

    Appleby-Thomas, Gareth; Hazell, Paul; Millett, Jeremy; Bourne, Neil

    2009-06-01

    Aluminium alloys such as 5083 are established light weight armour materials. As such, the shock response of these materials is of great importance. The shear strength of a material under shock loading provides an insight into its ballistic performance. In this investigation embedded manganin stress gauges have been employed to measure both the longitudinal and lateral components of stress during plate impact experiments over a range of impact stresses. In turn, these results were used to determine the shear strength and to investigate the time dependence of lateral stress behind the shock front to give an indication of material response.

  14. Morphology of the aluminium-uranium eutectic

    International Nuclear Information System (INIS)

    Ambrozio Filho, F.; Vieira, R.R.

    1976-01-01

    The factors which might affect the eutectic structure including external condition during solidification as well as factors peculiar to each individual system is discussed. The structure of the Al-U eutectic, consisting of the solid solution of uranium in aluminium and UAl 4 , as obtained in ingot moulds and by unidirectional solidification. The extructure in terms of certain variables with emphasis on the growth characteristics of the phases comprising the eutectic the velocity of growth and thermal gradient in the liquid is also presented [pt

  15. The failure of aluminium nitride under shock

    International Nuclear Information System (INIS)

    Pickup, I.M.; Bourne, N.K.

    2002-01-01

    The shear strength of aluminium nitride has been measured over a range of impact stresses by measuring lateral stresses in plate impact experiments. The range of impact stress spanned several key shock thresholds for the material, pre and post Hugoniot elastic limit and up to values where the hexagonal to cubic phase transition starts. The shear strength measurements indicate significant inelastic damage at stress levels in excess of the HEL, but a significant recovery of strength at the highest impact stress was observed. This stress equates to the phase transition stress. The shear strength behaviour is compared to that of silicon carbide, which does not exhibit a phase change at these impact velocities

  16. Aluminium/iron reinforced polyfurfuryl alcohol resin as advanced biocomposites

    Directory of Open Access Journals (Sweden)

    Rakesh Kumar

    2016-07-01

    Full Text Available Aluminium and iron are widely used in construction sectors for the preparation of advanced composites with epoxy resins as matrices. In recent times, there are several reports on the polymerization of polyfufuryl alcohol (PFA a thermoset bioresins from furfuryl alcohol (FA. FA is obtained from waste of sugarcane bagasse. In this work, first the possibility of curing PFA from FA in the presence of aluminium or iron has been explored. Absorbance results from colorimeter/spectrophotometerindicated that the curing of FA to PFA in presence of aluminium started easily while in presence of iron the curing of FA to PFA could not start. Based on the above results, aluminium wire reinforced composites were successfully prepared with three different weight fractions (0.13, 0.09 and 0.07 of aluminium wire. The mechanical properties of these composites were determined theoretically and reported.

  17. Usage of neural network to predict aluminium oxide layer thickness.

    Science.gov (United States)

    Michal, Peter; Vagaská, Alena; Gombár, Miroslav; Kmec, Ján; Spišák, Emil; Kučerka, Daniel

    2015-01-01

    This paper shows an influence of chemical composition of used electrolyte, such as amount of sulphuric acid in electrolyte, amount of aluminium cations in electrolyte and amount of oxalic acid in electrolyte, and operating parameters of process of anodic oxidation of aluminium such as the temperature of electrolyte, anodizing time, and voltage applied during anodizing process. The paper shows the influence of those parameters on the resulting thickness of aluminium oxide layer. The impact of these variables is shown by using central composite design of experiment for six factors (amount of sulphuric acid, amount of oxalic acid, amount of aluminium cations, electrolyte temperature, anodizing time, and applied voltage) and by usage of the cubic neural unit with Levenberg-Marquardt algorithm during the results evaluation. The paper also deals with current densities of 1 A · dm(-2) and 3 A · dm(-2) for creating aluminium oxide layer.

  18. Usage of Neural Network to Predict Aluminium Oxide Layer Thickness

    Directory of Open Access Journals (Sweden)

    Peter Michal

    2015-01-01

    Full Text Available This paper shows an influence of chemical composition of used electrolyte, such as amount of sulphuric acid in electrolyte, amount of aluminium cations in electrolyte and amount of oxalic acid in electrolyte, and operating parameters of process of anodic oxidation of aluminium such as the temperature of electrolyte, anodizing time, and voltage applied during anodizing process. The paper shows the influence of those parameters on the resulting thickness of aluminium oxide layer. The impact of these variables is shown by using central composite design of experiment for six factors (amount of sulphuric acid, amount of oxalic acid, amount of aluminium cations, electrolyte temperature, anodizing time, and applied voltage and by usage of the cubic neural unit with Levenberg-Marquardt algorithm during the results evaluation. The paper also deals with current densities of 1 A·dm−2 and 3 A·dm−2 for creating aluminium oxide layer.

  19. Aluminium Electroplating on Steel from a Fused Bromide Electrolyte

    Energy Technology Data Exchange (ETDEWEB)

    Prabhat Tripathy; Laura Wurth; Eric Dufek; Toni Y. Gutknecht; Natalie Gese; Paula Hahn; Steven Frank; Guy Fredrickson; J Stephen Herring

    2014-08-01

    A quaternary bromide bath (LiBr-KBr-CsBr-AlBr3) was used to electro-coat aluminium on steel substrates. The electrolyte was prepared by the addition of AlBr3 into the eutectic LiBr-KBr-CsBr melt. A smooth, thick, adherent and shiny aluminium coating could be obtained with 80 wt.% AlBr3 in the ternary melt. The SEM photographs of the coated surfaces suggest the formation of thick and dense coatings with good aluminium coverage. Both salt immersion and open circuit potential measurement suggest that the coatings did display good corrosion-resistance behavior. Annealing of the coated surfaces, prior to corrosion tests, suggested the robustness of the metallic aluminium coating in preventing the corrosion of the steel surfaces. Studies also indicated that the quaternary bromide plating bath can potentially provide a better aluminium coating on both ferrous and non-ferrous metals, including complex surfaces/geometries.

  20. Study of corrosion in aluminium using neutron radiography technique

    International Nuclear Information System (INIS)

    Islam, M.N.; Alam, M.K.; Saklayen, M.A.; Ahsan, M.H.; Islam, S.M.A.; Zaman, M.A.

    2000-01-01

    Neutron radiography technique has been adopted for detection of corrosion in aluminium by filling artificially made holes on aluminium slab with Al(OH) 3 . The contrast between the optical densities of corrosion products and aluminium slab was assessed from the densitometric measurements. Variation of optical density difference with sample thickness has also been studied. The results confirm that approximately 0.039 mm thick corrosion products having diameter 10 mm can easily be detected in 2 cm thick aluminium slab. The linear attenuation coefficient of Al(OH) 3 has been obtained as 0.9447. From the present investigation it is confirmed that film neutron radiography (NR) technique is helpful for investigation of Al(OH) 3 type corrosion product in aluminium. (author)

  1. Site specific SEM/FIB/TEM for analysis of lubricated sliding wear of aluminium alloy composites

    International Nuclear Information System (INIS)

    Walker, J C; Jones, H; Rainforth, W M

    2006-01-01

    Although extensive research has been undertaken into the dry sliding wear of aluminium alloys, only limited work has been reported on lubricated wear. In this paper, the lubricated sliding wear of some powder derived aluminium alloy composites is reported. Stereo pairs of the worn surface were obtained in the SEM and digitally reconstructed to give an accurate projection of the surface topography. Analysis of the average surface roughness (R a ) along chosen sections provided quantitative information about the wear mechanism. Following this, dual beam focused ion beam (FIB) was undertaken to further explore the features revealed by the SEM surface reconstructions, with TEM sections removed from selected regions. Surface deformation was confined to a narrow layer, typically 1μm thick. Subgrain size within the subsurface layer was comparable to that found in dry sliding wear tests. Reinforcement fracture occurred in the surface particles only. The resultant fragments were often incorporated back into the surface following detachment, such that the total volume fraction reinforcement at the surface was greater than in the bulk. Thus, the dynamic surface topography was a result of three factors: surface deformation, local detachment of reinforcement and re-incorporation of the fragments back into the surface

  2. The oxidation kinetics for sublimates formed during niobium electron-beam remelting

    International Nuclear Information System (INIS)

    Chumarev, V.M.; Gulyaeva, R.I.; Mar'evich, V.P.; Upolovnikova, A.G.; Udoeva, L.Yu.

    2003-01-01

    The oxidation of sublimates of Nb-Al electron beam remelting is investigated under conditions of isothermal and continuous heating in the air. It is stated that basic oxidation products are niobium and aluminium oxides, as well as aluminium niobates of variable composition of Al 2 O 3 · mNb 2 O 5 . The more aluminium enriched sublimates possess an increased resistance to oxidation. Formed in sublimates NbAl 3 intermetallic compound features the highest heat resistance. Oxidation parameters are determined by the method of nonisothermic kinetics. It is noted that the running processes exhibit a multistage nature and are limited by internal diffusion [ru

  3. Precipitate strengthening of nanostructured aluminium alloy.

    Science.gov (United States)

    Wawer, Kinga; Lewandowska, Malgorzata; Kurzydlowski, Krzysztof J

    2012-11-01

    Grain boundaries and precipitates are the major microstructural features influencing the mechanical properties of metals and alloys. Refinement of the grain size to the nanometre scale brings about a significant increase in the mechanical strength of the materials because of the increased number of grain boundaries which act as obstacles to sliding dislocations. A similar effect is obtained if nanoscale precipitates are uniformly distributed in coarse grained matrix. The development of nanograin sized alloys raises the important question of whether or not these two mechanisms are "additive" and precipitate strengthening is effective in nanostructured materials. In the reported work, hydrostatic extrusion (HE) was used to obtain nanostructured 7475 aluminium alloy. Nanosized precipitates were obtained by post-HE annealing. It was found that such annealing at the low temperatures (100 degrees C) results in a significant increase in the microhardness (HV0.2) and strength of the nanostructured 7475 aluminium alloy. These results are discussed in terms of the interplay between the precipitation and deformation of nanocrystalline metals.

  4. Reactions on carbon anodes in aluminium electrolysis

    Energy Technology Data Exchange (ETDEWEB)

    Eidet, Trygve

    1997-12-31

    The consumption of carbon anodes and energy in aluminium electrolysis is higher than what is required theoretically. This thesis studies the most important of the reactions that consume anode materials. These reactions are the electrochemical anode reaction and the airburn and carboxy reactions. The first part of the thesis deals with the kinetics and mechanism of the electrochemical anode reaction using electrochemical impedance spectroscopy. The second part deals with air and carboxy reactivity of carbon anodes and studies the effects of inorganic impurities on the reactivity of carbon anodes in the aluminium industry. Special attention is given to sulphur since its effect on the carbon gasification is not well understood. Sulphur is always present in anodes, and it is expected that the sulphur content of available anode cokes will increase in the future. It has also been suggested that sulphur poisons catalyzing impurities in the anodes. Other impurities that were investigated are iron, nickel and vanadium, which are common impurities in anodes which have been reported to catalyze carbon gasification. 88 refs., 92 figs., 24 tabs.

  5. Aluminium alloys containing iron and nickel

    International Nuclear Information System (INIS)

    Coriou, H.; Fournier, R.; Grall, L.; Hure, J.; Herenguel, J.; Lelong, P.

    1958-01-01

    The first part of this report addresses mechanism, kinetics and structure factors of aluminium alloys containing iron and nickel in water and high temperature steam. The studied alloys contain from 0.3 to 0.7 per cent of iron, and 0.2 to 1.0 per cent of nickel. Corrosion resistance and corrosion structure have been studied. The experimental installation, process and samples are presented. Corrosion structures in water at 350 C are identified and discussed (structure of corrosion products, structure of metal-oxide interface), and then in steam at different temperatures (350-395 C). Corrosion kinetics is experimentally studied (weight variation in time) in water at 350 C and in steam at different temperatures. Reactions occurring at over-heated steam (more than 400 C) are studied, and the case of welded alloys is also addressed. The second part addresses the metallurgical mechanism and processes influencing aluminium alloy resistance to corrosion by high temperature water as it appeared that separated phases protect the solid solution through a neighbourhood action. In order to avoid deep local corrosions, it seems necessary to multiply protective phases in an as uniform as possible way. Some processes enabling this result are described. They belong to conventional metallurgy or to powder metallurgy (with sintering and extrusion)

  6. Enhancement of wear and ballistic resistance of armour grade AA7075 aluminium alloy using friction stir processing

    Directory of Open Access Journals (Sweden)

    I. Sudhakar

    2015-03-01

    Full Text Available Industrial applications of aluminium and its alloys are restricted because of their poor tribological properties. Thermal spraying, laser surfacing, electron beam welding are the most widely used techniques to alter the surface morphology of base metal. Preliminary studies reveal that the coating and layering of aluminium alloys with ceramic particles enhance the ballistic resistance. Furthermore, among aluminium alloys, 7075 aluminium alloy exhibits high strength which can be compared to that of steels and has profound applications in the designing of lightweight fortification structures and integrated protection systems. Having limitations such as poor bond integrity, formation of detrimental phases and interfacial reaction between reinforcement and substrate using fusion route to deposit hard particles paves the way to adopt friction stir processing for fabricating surface composites using different sizes of boron carbide particles as reinforcement on armour grade 7075 aluminium alloy as matrix in the present investigation. Wear and ballistic tests were carried out to assess the performance of friction stir processed AA7075 alloy. Significant improvement in wear resistance of friction stir processed surface composites is attributed to the change in wear mechanism from abrasion to adhesion. It has also been observed that the surface metal matrix composites have shown better ballistic resistance compared to the substrate AA7075 alloy. Addition of solid lubricant MoS2 has reduced the depth of penetration of the projectile to half that of base metal AA7075 alloy. For the first time, the friction stir processing technique was successfully used to improve the wear and ballistic resistances of armour grade high strength AA7075 alloy.

  7. Magnetic field dependence observed by 27 Al NMR of species contained in alumina colloidal dispersions

    International Nuclear Information System (INIS)

    Morgado Junior, Edisson; Menezes, Sonia M.C.; San Gil, Rosane

    1995-01-01

    The behaviour of some aluminium species front a magnetic field have been investigated by 27 Al NMR analysis, this method was used for characterization of an octahedric aluminium specie from sols prepared by bohemite acid peptization. X-ray diffraction data have identified the mineral structure. The results have been shown and discussed, and NMR spectra were also presented and studied. Concluding this work, the nature of a colloidal specie of alumina was clarified through the dependence research of magnetic field by 27 Al NMR

  8. Recovery of tritium from lithium-sintered aluminium product (SAP) and lithium-aluminium alloys

    International Nuclear Information System (INIS)

    Talbot, J.B.; Wiffen, F.W.

    1979-01-01

    The tritium release rates of irradiated samples of lithium-containing aluminium (Li-Al) and sintered aluminium product (Li-SAP) were investigated to evaluate the potential application of both materials in fusion reactors. The observed release rates followed the pattern expected for bulk diffusion of tritium in a solid. Therefore, diffusion coefficients for tritium in Li-SAP were determined over a temperature range of 383 and 500 0 C and tritium in Li-Al at 450 0 C. At 450 0 C, the diffusion coefficients of tritium in Li-SAP and Li-Al are 2.988 x 10 -10 cm 2 sec -1 and 1.462 x 10 -6 cm 2 sec -1 , respectively. (author)

  9. The varied functions of aluminium-activated malate transporters–much more than aluminium resistance

    Science.gov (United States)

    Palmer, Antony J.; Baker, Alison; Muench, Stephen P.

    2016-01-01

    The ALMT (aluminium-activated malate transporter) family comprises a functionally diverse but structurally similar group of ion channels. They are found ubiquitously in plant species, expressed throughout different tissues, and located in either the plasma membrane or tonoplast. The first family member identified was TaALMT1, discovered in wheat root tips, which was found to be involved in aluminium resistance by means of malate exudation into the soil. However, since this discovery other family members have been shown to have many other functions such as roles in stomatal opening, general anionic homoeostasis, and in economically valuable traits such as fruit flavour. Recent evidence has also shown that ALMT proteins can act as key molecular actors in GABA (γ-aminobutyric acid) signalling, the first evidence that GABA can act as a signal transducer in plants. PMID:27284052

  10. The varied functions of aluminium-activated malate transporters-much more than aluminium resistance.

    Science.gov (United States)

    Palmer, Antony J; Baker, Alison; Muench, Stephen P

    2016-06-15

    The ALMT (aluminium-activated malate transporter) family comprises a functionally diverse but structurally similar group of ion channels. They are found ubiquitously in plant species, expressed throughout different tissues, and located in either the plasma membrane or tonoplast. The first family member identified was TaALMT1, discovered in wheat root tips, which was found to be involved in aluminium resistance by means of malate exudation into the soil. However, since this discovery other family members have been shown to have many other functions such as roles in stomatal opening, general anionic homoeostasis, and in economically valuable traits such as fruit flavour. Recent evidence has also shown that ALMT proteins can act as key molecular actors in GABA (γ-aminobutyric acid) signalling, the first evidence that GABA can act as a signal transducer in plants. © 2016 The Author(s). Published by Portland Press Limited on behalf of the Biochemical Society.

  11. Cold forming of aluminium - State of the art

    DEFF Research Database (Denmark)

    Bay, Niels

    1997-01-01

    The ongoing development of cold forging technology has been manifested lately by the increasing application of components in cold forged aluminium alloys. Applying precipitation hardening alloys components with great strength/weight ratio can be produced with a strength comparable...... to that of unalloyed steel. After description of the different types of alloys and their individual properties and applications, the special requirements for tool design by cold forging in aluminium is discussed. Finally, a large number of industrial examples on cold forged aluminium components are presented. (C) 1997...

  12. Effect of pressurized steam on AA1050 aluminium

    DEFF Research Database (Denmark)

    Jariyaboon, Manthana; Møller, Per; Ambat, Rajan

    2012-01-01

    Purpose - The purpose of this paper is to understand the effect of pressurized steam on surface changes, structures of intermetallic particles and corrosion behavior of AA1050 aluminium. Design/methodology/approach - Industrially pure aluminium (AA1050, 99.5 per cent) surfaces were exposed...... reactivities was observed due to the formation of the compact oxide layer. Originality/value - This paper reveals a detailed investigation of how pressurized steam can affect the corrosion behaviour of AA1050 aluminium and the structure of Fe-containing intermetallic particles....

  13. Corrosion issues of powder coated AA6060 aluminium profiles

    DEFF Research Database (Denmark)

    Din, Rameez Ud; Valgarðsson, Smári; Jellesen, Morten Stendahl

    2015-01-01

    In this study detailed microstructural investigation of the reason for unexpected corrosion of powder coated aluminium alloy AA6060 windows profiles has been performed. The results from this study reveals that the failure of the window profiles was originated from the surface defects present...... on the extruded AA6060 aluminium profile after metallurgical process prior to powder coating. Surface defects are produced due to intermetallic particles in the alloy, which disturb the flow during the extrusion process. The corrosion mechanism leading to the failure of the powder coated AA6060 aluminium profiles...

  14. Experimental Realisation of Elusive Multiple-bonded Aluminium Compounds: A New Horizon in the Aluminium Chemistry.

    Science.gov (United States)

    Inoue, Shigeyoshi; Bag, Prasenjit; Weetman, Catherine

    2018-05-23

    Synthesis and isolation of stable main group compounds featuring multiple bonds has been of keen interest for the last several decades. Multiply bonded complexes were obtained using sterically demanding substituents that provide kinetic and thermodynamic stability. Many of these compounds have unusual structural and electronic properties that challenges the classical concept of covalent multiple bonding. In contrast, analogous aluminium compounds are scarce in spite of its high natural abundance. The parent dialumene (Al2H2) has been calculated to be extremely weak, thus making Al multiple bonds a challenging synthetic target. This review provides an overview of these recent advances in the cutting edge synthetic approaches used to obtain aluminium homo- and heterodiatomic multiply bonded complexes. Additionally, the reactivity of these novel compounds towards various small molecules and reagents will be discussed herein. This review provides an overview on the current progress in aluminium multiple bond chemistry and the careful ligand design required to stabilise these reactive species. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  15. Beam-beam phenomenology

    International Nuclear Information System (INIS)

    Teng, L.C.

    1980-01-01

    In colliding beam storage rings the beam collision regions are generally so short that the beam-beam interaction can be considered as a series of evenly spaced non-linear kicks superimposed on otherwise stable linear oscillations. Most of the numerical studies on computers were carried out in just this manner. But for some reason this model has not been extensively employed in analytical studies. This is perhaps because all analytical work has so far been done by mathematicians pursuing general transcendental features of non-linear mechanics for whom this specific model of the specific system of colliding beams is too parochial and too repugnantly physical. Be that as it may, this model is of direct interest to accelerator physicists and is amenable to (1) further simplification, (2) physical approximation, and (3) solution by analogy to known phenomena

  16. Application of radioactivation analysis for determination of impurities in aluminium, raw materials and in samples from aluminium production process

    International Nuclear Information System (INIS)

    Vucina, L.J.

    1977-01-01

    Trace elements in aluminium, raw materials and in the samples from different stages of aluminium production were determined by nondestructive neutron radioactivation analysis. The samples were taken from the Bayer's process of alumina production (bauxite, red sludge and alumina), from the components of the reduction cell (anode, criolyte and AlF 3 ) and of the final product - aluminium (purity 99.5-99.7%). Under given set of conditions ten trace elements (V,La,Ga,Mn,Co,Cr,Sc,Sb,Zn and Fe) were determined in aluminium and followed through the production process. It was found that the main impurities in aluminium are iron (0.15%) and zinc (0.O6%). It has been concluded that the purity of produced aluminium depends mainly on the purity of used alumina. The second important source of contamination of aluminium is anode. The results obtained by radioactivation analysis for V, Mn, Cr and Fe fall within the ranges of concentrations of these elements determined by use of other methods (volumetry, spectrophotometry, atomic absorption). Higher values for zinc were obtained by radioactivation analysis, probably due to unsatisfactory irradiation and measuring conditions for this element. The possibilities of application of radioactivation analysis to these kinds of samples are also disscused

  17. Experimental analysis of cut welding in aluminium

    DEFF Research Database (Denmark)

    Dorph, Pernille; De Chiffre, Leonardo; Bay, Niels

    1993-01-01

    Cut welding is a newly developed cold pressure welding process. In the present work, an experimental investigation was carried out analyzing the mechanisms involved in cut welding of a block to a strip. Experiments were carried out in technically pure aluminium. The investigation has involved...... tensile testing and metallographic investigations of the welds. The results show that this variant of cut welding is a very reproducible process giving a weld strength equal to 30-40% the strength of the parent material. The experiments have shown that the reason for this relatively low strength...... is an uneven pressure distribution along the weld due to a wave formed during sliding. Attempts to alter the material flow during sliding are presented....

  18. Heat of solution of hydrogen in aluminium

    International Nuclear Information System (INIS)

    Mahajan, S.; Prakash, S.

    1984-01-01

    The heat of solution of hydrogen in aluminium is investigated accounting for both, the lattice dilation and its relaxation. The lattice contribution is evaluated using a linearly screened local model potential for the ions. The non-linear screening in the density functional formalism along with the exchange and correlation corrections in the jellium model is used to evaluate the proton contribution. The dilation enhances the lattice contribution by about 12 % and decreases the protonic contribution by about 5 %. The relaxation energy is reduced by about 40 % for the dilated lattice. Adding all the contributions, the heat of solution is found to be 20 % larger for the dilated lattice than that for the undilated lattice. The calculated heat of solution is found in good agreement with the experimental value. Comparing the results with the calculations of Perrot and Rasolt, the spherical solid model correction is estimated and it is found that it further improves the results. (author)

  19. Solidification microstructures of aluminium-uranium alloys

    International Nuclear Information System (INIS)

    Ambrozio Filho, F.; Vieira, R.R.

    1976-01-01

    The solidification of microstrutures of aluminium-uranium alloys in the range of 4 to 20% uranium is investigated. The solidification was obtained both in ingot molds and under controlled directional solidification. The conditions for the presence of primary crystals and eutectic are discussed and an analysis of the influence of variables (growth rate and thermal gradient in the liquid) on the alloy structure is made. The effect of cooling rate on the alloy structures has been determined. It is found that the resulting structure can be derived from the kinectics concept, as required by the coupled-zone theory. Suggestions on the qualitative intervals of composition and temperatures with eutectic growth are presented [pt

  20. Slag corrosion of gamma aluminium oxynitride

    Energy Technology Data Exchange (ETDEWEB)

    Wang Xidong; Li Wen Chao [Beijing Univ. of Science and Technology, BJ (China). Dept. of Physical Chemistry of Metals; Sichen Du; Seetharaman, S. [Royal Inst. of Tech., Stockholm (Sweden). Dept. of Materials Science and Technology

    2002-03-01

    Corrosion of {gamma}-aluminium oxynitride (AlON) by CaO-MgO-''FeO''-Al{sub 2}O{sub 3}-SiO{sub 2} melts corresponding to blast furnace slag was examined from 1693 to 1753 K under static and forced convection conditions. An intermediate layer was observed between the unreacted oxynitride and slag. After a certain time interval, the rate of the growth of this layer was found to be equal to the rate of the dissolution of the layer. Slag corrosion of AlON is a strongly thermally activated process, the overall activation energy being 1002 kJ/mol. The rate of corrosion was found to be significantly enhanced by the addition of ''FeO''. (orig.)

  1. Study of hydrogen implanted in aluminium

    International Nuclear Information System (INIS)

    Bugeat, J.P.; Chami, A.C.; Danielou, R.; Ligeon, E.

    1976-01-01

    An aluminium sample was implanted with deuterium and hydrogen at 5keV and 10keV respectively. The 1 H( 11 B,α) 8 Be* and D( 3 He,p) 4 He reactions were used for the analysis of H and D respectively. The implanted deuterium was shown to be as a whole in a tetrahedral site as far as the implantation temperature is lower than 175K, beyond that temperature the deuterium is randomly located. When the implantation temperature increases from 33K up to 275K the tetrahedral siting remains during annealing. The migration temperatures of hydrogen (or temperature of transition from the tetrahedral siting to a random distribution) experimentally observed during annealing (300K) and for increased implantation temperatures, show that the tetrahedral site is associated with a monovacancy migrating at 300K, the diffusion temperature of hydrogen being lower than 180K [fr

  2. Orbital friction stir welding of aluminium pipes

    International Nuclear Information System (INIS)

    Engelhard, G.; Hillers, T.

    2002-01-01

    Friction stir welding (FSW) was originally developed for flat plates. This contribution shows how it can be applied to the welding of aluminium pipes. Pipes made of AlMG 3 (EN5754), AlMg 4.5Mn (EN5083) and AlMgSi 0.5 (EN6106) with dimensions of Da 600 and 520 x 10-8 mm were welded. The FSW orbital system comprises an annular cage with integrated FSW head, a hydraulic system, and a control unit. The welds were tested successfully according to EN 288. The mechanical and technical properties of the welds were somewhat better than with the TIG orbital process, and welding times were about 40 percent shorter [de

  3. COMPARATION BETWEEN NONDESTRUCTIVE TESTING METHODS FOR THE ALUMINIUM BRAZED PIECES

    Directory of Open Access Journals (Sweden)

    Dan NIŢOI

    2014-05-01

    Full Text Available Presented paper refers to different control methods used in aluminium brazed joining because of possible defects. Low joining complexity permits exact damages position in relation with materials geometry.

  4. Aluminium alloys in municipal solid waste incineration bottom ash.

    Science.gov (United States)

    Hu, Yanjun; Rem, Peter

    2009-05-01

    With the increasing growth of incineration of household waste, more and more aluminium is retained in municipal solid waste incinerator bottom ash. Therefore recycling of aluminium from bottom ash becomes increasingly important. Previous research suggests that aluminium from different sources is found in different size fractions resulting in different recycling rates. The purpose of this study was to develop analytical and sampling techniques to measure the particle size distribution of individual alloys in bottom ash. In particular, cast aluminium alloys were investigated. Based on the particle size distribution it was computed how well these alloys were recovered in a typical state-of-the-art treatment plant. Assessment of the cast alloy distribution was carried out by wet physical separation processes, as well as chemical methods, X-ray fluorescence analysis and electron microprobe analysis. The results from laboratory analyses showed that cast alloys tend to concentrate in the coarser fractions and therefore are better recovered in bottom ash treatment plants.

  5. Ultraviolet sensing properties of polyvinyl alcohol-coated aluminium ...

    Indian Academy of Sciences (India)

    Electrochemical; aluminium-doped zinc oxide; PVA-coated; UV sensing. 1. Introduction ... Metal oxides having good optical and structural proper- ties also require good .... close to the calculated defect level due to zinc interstitial. PL spectra of ...

  6. Oxygen–induced barrier height changes in aluminium – amorphous ...

    African Journals Online (AJOL)

    Se) films by exposing the samples to oxygen before the aluminium contacts were deposited. Current – voltage (I-V) measurements were carried out on the samples. The results show that the application of voltage causes charge exchange ...

  7. Aluminium effect on the physical properties of titanium

    International Nuclear Information System (INIS)

    Nazimov, O.P.; Il'in, A.A.; Zvonova, L.N.

    1977-01-01

    The effect of aluminium on the physical properties of titanium was investigated. Within the framework of the configuration model of matter it is shown that a change in physical properties with an aluminium content of up to 7.5 wt.% in alloys depends on the phase composition and electron structure. In interacting with titanium, aluminium exhibits acceptor properties, causing d→s electron transitions. The electrons which have shifted to the s-state are partly collectivized and partly localized into quasistable sp 3 configurations, with the resulting increase of the interatomic forces. An intensification of d→s transitions in alloying of titanium with aluminium stabilizes the α-phase. Predominance of d 1 configurations in the intermediate spectrum in the region of the α-solution increases the ratio of the axes of the HCP lattice and determines the electron type of conduction of alloys of the Ti-Al system

  8. Analogy and differences between aluminium and titanium electrowinning

    CSIR Research Space (South Africa)

    Van Vuuren, DS

    2006-09-01

    Full Text Available larger market. The authors have tested this route experimentally, but could not produce pure titanium. The failure of electrowinning pure, molten titanium has been interpreted in terms of the analogy and differences between aluminium and titanium...

  9. Deposition of aluminium nanoparticles using dense plasma focus device

    International Nuclear Information System (INIS)

    Devi, Naorem Bilasini; Srivastava, M P; Roy, Savita

    2010-01-01

    Plasma route to nanofabrication has drawn much attention recently. The dense plasma focus (DPF) device is used for depositing aluminium nanoparticles on n-type Si (111) wafer. The plasma chamber is filled with argon gas and evacuated at a pressure of 80 Pa. The substrate is placed at distances 4.0 cm, 5.0 cm and 6.0 cm from the top of the central anode. The aluminium is deposited on Si wafer at room temperature with two focused DPF shots. The deposits on the substrate are examined for their morphological properties using atomic force microscopy (AFM). The AFM images have shown the formation of aluminium nanoparticles. From the AFM images, it is found that the size of aluminium nanoparticles increases with increase in distance between the top of anode and the substrate for same number of DPF shots.

  10. Manufacturing and Machining Challenges of Hybrid Aluminium Metal Matix Composites

    Science.gov (United States)

    Baburaja, Kammuluri; Sainadh Teja, S.; Karthik Sri, D.; Kuldeep, J.; Gowtham, V.

    2017-08-01

    Manufacturing which involves material removal processes or material addition processes or material transformation processes. One or all the processes to obtain the final desired properties for a material with desired shape which meets the required precision and accuracy values for the expected service life of a material in working conditions. Researchers found the utility of aluminium to be the second largest after steel. Aluminium and its metal matrix composite possess wide applications in various applications in aerospace industry, automobile industry, Constructions and even in kitchen utensils. Hybrid Al-MMCconsist of two different materials, and one will be from organic origin along with the base material. In this paper an attempt is made to bring out the importance of utilization of aluminium and the challenges concerned in manufacturing and machining of hybrid aluminium MMC.

  11. Finite size melting of spherical solid-liquid aluminium interfaces

    DEFF Research Database (Denmark)

    Chang, J.; Johnson, Erik; Sakai, T.

    2009-01-01

    We have investigated the melting of nano-sized cone shaped aluminium needles coated with amorphous carbon using transmission electron microscopy. The interface between solid and liquid aluminium was found to have spherical topology. For needles with fixed apex angle, the depressed melting tempera...... to the conclusion that the depressed melting temperature is not controlled solely by the inverse radius 1/R. Instead, we found a direct relation between the depressed melting temperature and the ratio between the solid-liquid interface area and the molten volume.......We have investigated the melting of nano-sized cone shaped aluminium needles coated with amorphous carbon using transmission electron microscopy. The interface between solid and liquid aluminium was found to have spherical topology. For needles with fixed apex angle, the depressed melting...

  12. Verification of Some Vegetable Oils as Cutting Fluid for Aluminium

    African Journals Online (AJOL)

    Akorede

    kerosene (due to the gummy nature of aluminium metal). The parameters ... In the cutting of metals, work is done in the plastic deformation of the layer being cut at the primary shear ... Lathe machine – Model: Metalx WARSZAWA,. Serial No.

  13. Spectrographic determination of trace impurities in reactor grade aluminium

    International Nuclear Information System (INIS)

    Chandola, L.C.; Machado, I.J.

    1975-01-01

    A spectrographic method enabling the determination of 21 trace impurities in aluminium oxide is described. The technique involves mixing the sample with graphite buffer in the ratio 1:1, loading it in a graphite electrode and arcing it for 30 sec. in a dc arc to 10 A current against a pointed graphite cathode. The spectra are photographed on Ilford N.30 emulsion employing a large quartz spectrograph. The aluminium line at 2669.2 A 0 serves as the internal standard. The impurities determined are Ag, B, Bi, Cd, Co, Cr, Cu, Fe, Ga, In, Mg, Mo, Ni, Pb, Sb, Si, Sn, Ti, V and Zn. The sensitivity varies from 5 to 100 ppm and the precision from +- 5 to +- 22% for different elements. A method for converting aluminium metal to aluminium oxide is described. It is found that boron is not lost during this conversion. (author)

  14. Aluminium leaching from red mud by filamentous fungi.

    Science.gov (United States)

    Urík, Martin; Bujdoš, Marek; Milová-Žiaková, Barbora; Mikušová, Petra; Slovák, Marek; Matúš, Peter

    2015-11-01

    This contribution investigates the efficient and environmentally friendly aluminium leaching from red mud (bauxite residue) by 17 species of filamentous fungi. Bioleaching experiments were examined in batch cultures with the red mud in static, 7-day cultivation. The most efficient fungal strains in aluminium bioleaching were Penicillium crustosum G-140 and Aspergillus niger G-10. The A. niger G-10 strain was capable to extract up to approximately 141 mg·L(-1) of aluminium from 0.2 g dry weight red mud. Chemical leaching with organic acids mixture, prepared according to A. niger G-10 strain's respective fungal excretion during cultivation, proved that organic acids significantly contribute to aluminium solubilization from red mud. Copyright © 2015 Elsevier Inc. All rights reserved.

  15. Aluminium localization and toxicity symptoms related to root growth ...

    Indian Academy of Sciences (India)

    2012-10-26

    Oct 26, 2012 ... Aluminium localization and toxicity symptoms related to root growth inhibition in rice (Oryza sativa ... growth of this cultivar when submitted to Al3+ stress. Moreover ..... Caiapó. Previous work has shown the IAC cultivar to be.

  16. On the microstructure analysis of FSW joints of aluminium components made via direct metal laser sintering

    Science.gov (United States)

    Scherillo, Fabio; Astarita, Antonello; di Martino, Daniela; Contaldi, Vincenzo; di Matteo, Luca; di Petta, Paolo; Casarin, Renzo; Squillace, Antonino; Langella, Antonio

    2017-10-01

    Additive Manufacturing (AM), applied to metal industry, is a family of processes that allow complex shape components to be realized from raw materials in the form of powders. The compaction of the powders can be achieved by local melting of the powder bed or by solid state sintering. Direct Metal Laser Sintering (DMLS) is an additive manufacturing process in which a focalized laser beam is the heat source that allows the powders to be compacted. By DMLS it is possible to realize complex shape components. One of the limits of DMLS, as for every additive layer manufacturing techniques, is the unfeasibility to realize large dimension parts. Due to this limit the study of joining process of parts made via ALM is of great interest. One of the most promising options is the Friction Stir Welding (FSW), a solid state welding technique that has been proven to be very effective in the welding of metals difficult to weld, above all aluminium alloys. Since FSW is a solid-state technique, the microstructure of the various zone of the weld bead depends not only by the process itself but also by the parent microstruct ure of the parts to be welded. Furthermore, parts made of aluminium alloy via DMLS have a particular microstructure that is the result of repeated severe thermal cycles. In the present work the authors, starting from the description of the parent microstructure of parts made of AlSi10Mg aluminium alloy, study the microstructure evolution occurred within the joint made by Friction Stir Welding, analysing in details the microstructure of the main well recognized zone of the weld bead. The structure of the parent material is characterized by the presence of melting pools with a very fine microstructure. In the joint the recrystallization, the grain refinement and, above all, the redistribution of intermetallic phases occurs, resulting in an homogenization of the microstructure and in an increase of micro hardness.

  17. Residual Stress Measurement of Coarse Crystal Grain in Aluminium Casting Alloy by Neutron Diffraction

    International Nuclear Information System (INIS)

    Nishida, Masayuki; Watanabe, Yoshitaka; Hanabusa, Takao

    2009-01-01

    Full text: Neutron stress measurement can detect strain and stress information in deep region because of large penetration ability of neutron beams. The present paper describes procedure and results in the residual stress measurement of aluminium casting alloy by neutron diffraction. Usually, the aluminium casting alloy includes the large crystal grains. The existence of large crystal grains makes it difficult to estimate the residual stresses in highly accuracy. In this study, the modified three axial method using Hook's equation was employed for neutron stress measurement. These stress measurements were performed under the two kinds of new techniques. One is a rocking curve method to calculate the principal strains in three directions. The peak profiles which appear discretely on rocking curves were translated to principle stresses by the Bragg law and the basic elastic theory. Another is the consideration of measurement positions and the edge effect in the neutron irradiated area (volume gage). The edge effect generates the errors of 2θ-peak position in the neutron stress measurement. In this study, the edge effect was investigated in detail by a small bit of copper single crystal. The copper bit was moved and scanned on three dimensionally within the gage volume. Furthermore, the average strains of symmetrical positions are measure by the sample turning at 180 degrees, because the error distributions of the 2θ-peak position followed to positions inside the gage volume. Form these results of this study, the residual stresses in aluminium casting alloy which includes the large crystal grains were possible to estimate by neutron stress measurement with the rocking curve method and the correction of the edge effect. (author)

  18. Adhesive Bonding of Aluminium Alloy A5754 by Epoxy Resins

    Directory of Open Access Journals (Sweden)

    Ivan Michalec

    2013-01-01

    Full Text Available Joining thin sheets of aluminium and its alloys is a promising area in the field of joining materials. Nowadays, joining methods that do not melt the material itself are increasingly being utilised. This paper deals with adhesive bonding of aluminium alloy A5754 by two-component epoxy resins. Theresults show that joints bonded by Hysol 9466 have appropriate mechanical properties, but that joints bonded by Hysol 9492 have better thermal stability.

  19. Purity and surface roughness of vacuum deposited aluminium films

    Energy Technology Data Exchange (ETDEWEB)

    Dhere, N G; Arsenio, T P [Instituto Militar de Engenharia, Rio de Janeiro (Brazil); Patnaik, B K [Pontificia Universidade Catolica do Rio de Janeiro (Brazil). Instituto de Fisica; Assuncao, F C.R.; de Souza, A M [Pontificia Universidade Catolica do Rio de Janeiro (Brazil). Departamento de Ciencia dos Materiais e Metalurgia

    1975-04-01

    The authors studied the purity, surface roughness and grain size of vacuum-deposited aluminium films, using an intermetallic crucible and a continuous feed of pure aluminium wire. The grain size and roughness were studied by electron difraction, X-ray diffraction and the scanning electron microscope. Purity was determined by X-ray fluorescence produced by proton bombardment in the Van de Graaff accelerator and by X-ray and optical emission spectrometry.

  20. Aluminium-rich corner in Al-Cu-La system

    International Nuclear Information System (INIS)

    Yunusov, I.; Ganiev, I.N.

    1990-01-01

    Aluminium corner of Al-Cu-La system are investigated by means of microstructural and differential thermal analysis. Existence of LaCu 2 Al 10 and LaCu 0.5 Al 3.5 ternary compounds in the system is confirmed and it is shown, as well, both compounds are in two-phase equilibrium with aluminium solid solution and form with it and between each other eutectic type state diagrams. State diagrams for quasibinary sections are plotted

  1. Twenty years of isotope applications in the Hungarian aluminium industry

    International Nuclear Information System (INIS)

    Bujdoso, E.

    1982-01-01

    After a short review of the isotope techniques applied in the Hungarian aluminium industry some special applications and their results are briefly outlined. Industrial and laboratory scale trace constituent determinations, isotope and activation analytical methods and the application of sealed radiation sources are discussed. It has been shown that the related R+D activity followed closely the development trends of the aluminium industry. The references given is a comprehensive bibliography of Hungarian publications in this field. (author)

  2. Dependence of the phosphate sorption capacity on the aluminium and iron in Finnish soils

    Directory of Open Access Journals (Sweden)

    Armi Kaila

    1963-12-01

    Full Text Available An attempt was made to study to what extent the capacity of the more or less acid soils in Finland to sorb phosphate may be explained on the basis of their content of aluminium and iron. The indicator of the phosphate sorption capacity was calculated on the basis of the Freundlich adsorption isotherm according to the procedure proposed by TERÄSVUORI (8. The material consisted of 390 samples from cultivated and virgin soils representing both topsoils and subsoils. The indicator of the phosphate sorption capacity, the coefficient k, varied in the present material from 40 to 1510. The mean values (with the confidence limits at the 95 per cent level were for the 109 samples of sand and fine sand soils 290 ± 17, for the 103 samples of loam and silt soils 201 ± 24, for the 151 clay soils 308 ± 20, and for the 27 humus soils 236 ± 41. The total linear correlation coefficients between k and the soil pH, and its contents of organic carbon or clay were low or negligible in most of the soil groups. The correlation of k with the content of aluminium extracted by Tamm’s acid ammonium oxalate was fairly close in the clay soils (r = 0.84***, lower in the sand and fine sand soils (r = 0.77***, and in the loam and silt soils, and in the humus soils it was rather poor (r = 0.65*** and 0.63*** resp.. The elimination of the effect of the ammonium oxalate soluble iron decreased the correlation in the two latter groups quite markedly (to 0.32** and 0.37 resp., while the corresponding decrease in the coefficients for the former groups was less significant (to 0.64*** and 0.75*** resp.. The elimination of the effect of the ammonium oxalate soluble aluminium, on the other hand, decreased the correlation coefficients between k and the ammonium oxalate soluble iron in the sand and fine sand soils from 0.59*** to 0.26**, in the loam and silt soils from 0.73*** to 0.54***, in the clay soils from 0.70*** to 0.51***, and in the humus soils from 0.68*** to 0.49*. The

  3. Effect of iron and silicon in aluminium and its alloys

    International Nuclear Information System (INIS)

    Kovacs, I.

    1990-01-01

    The iron and silicon are the main impurities in aluminium, they are always present in alloys made from commercially pure base material. The solid solubility of iron in aluminium is very low, therefore its largest amount forms intermetallic compounds the kind of which depends strongly on the other impurities of alloying elements. Although the solid solubility of silicon is much larger than that of the iron, it is the constituent of both the primary and the secondary particles, the structure of which depends in general on the iron-silicon concentration ratio. These Fe and Si containing particles can cause various and basic changes in the macroscopic properties of the alloy. Since commercially pure aluminium has extensive consumer and industrial use, it is very important to know, not only from scientific but also from practical point of view, the effect of iron and silicon on the physical and mechanical properties of aluminium and its alloys. The aim of the ''International Workshop on the Effect of Iron and Silicon in Aluminium and its Alloys'' was to clarify the present knowledge on this subject. The thirty papers presented at the Workshop and collected in this Proceedings cover many important fields of the subject. I hope that they will contribute to both the deeper understanding of the related phenomena and the improvement of technologies for producing better aluminium alloys

  4. Investigation of different anode materials for aluminium rechargeable batteries

    Science.gov (United States)

    Muñoz-Torrero, David; Leung, Puiki; García-Quismondo, Enrique; Ventosa, Edgar; Anderson, Marc; Palma, Jesús; Marcilla, Rebeca

    2018-01-01

    In order to shed some light into the importance of the anodic reaction in reversible aluminium batteries, we investigate here the electrodeposition of aluminium in an ionic liquid electrolyte (BMImCl-AlCl3) using different substrates. We explore the influence of the type of anodic material (aluminium, stainless steel and carbon) and its 3D geometry on the reversibility of the anodic reaction by cyclic voltammetry (CV) and galvanostatic charge-discharge. The shape of the CVs confirms that electrodeposition of aluminium was feasible in the three materials but the highest peak currents and smallest peak separation in the CV of the aluminium anode suggested that this material was the most promising. Interestingly, carbon-based substrates appeared as an interesting alternative due to the high peak currents in CV, moderate overpotentials and dual role as anode and cathode. 3D substrates such as fiber-based carbon paper and aluminium mesh showed significantly smaller overpotentials and higher efficiencies for Al reaction suggesting that the use of 3D substrates in full batteries might result in enhanced power. This is corroborated by polarization testing of full Al-batteries.

  5. Compressive Behaviour and Energy Absorption of Aluminium Foam Sandwich

    Science.gov (United States)

    Endut, N. A.; Hazza, M. H. F. Al; Sidek, A. A.; Adesta, E. T. Y.; Ibrahim, N. A.

    2018-01-01

    Development of materials in automotive industries plays an important role in order to retain the safety, performance and cost. Metal foams are one of the idea to evolve new material in automotive industries since it can absorb energy when it deformed and good for crash management. Recently, new technology had been introduced to replace metallic foam by using aluminium foam sandwich (AFS) due to lightweight and high energy absorption behaviour. Therefore, this paper provides reliable data that can be used to analyze the energy absorption behaviour of aluminium foam sandwich by conducting experimental work which is compression test. Six experiments of the compression test were carried out to analyze the stress-strain relationship in terms of energy absorption behavior. The effects of input variables include varying the thickness of aluminium foam core and aluminium sheets on energy absorption behavior were evaluated comprehensively. Stress-strain relationship curves was used for energy absorption of aluminium foam sandwich calculation. The result highlights that the energy absorption of aluminium foam sandwich increases from 12.74 J to 64.42 J respectively with increasing the foam and skin thickness.

  6. Surface roughness when diamond turning RSA 905 optical aluminium

    Science.gov (United States)

    Otieno, T.; Abou-El-Hossein, K.; Hsu, W. Y.; Cheng, Y. C.; Mkoko, Z.

    2015-08-01

    Ultra-high precision machining is used intensively in the photonics industry for the production of various optical components. Aluminium alloys have proven to be advantageous and are most commonly used over other materials to make various optical components. Recently, the increasing demand from optical systems for optical aluminium with consistent material properties has led to the development of newly modified grades of aluminium alloys produced by rapid solidification in the foundry process. These new aluminium grades are characterised by their finer microstructures and refined mechanical and physical properties. However the machining database of these new optical aluminium grades is limited and more research is still required to investigate their machinability performance when they are diamond turned in ultrahigh precision manufacturing environment. This work investigates the machinability of rapidly solidified aluminium RSA 905 by varying a number of diamond-turning cutting parameters and measuring the surface roughness over a cutting distance of 4 km. The machining parameters varied in this study were the cutting speed, feed rate and depth of cut. The results showed a common trend of decrease in surface roughness with increasing cutting distance. The lowest surface roughness Ra result obtained after 4 km in this study was 3.2 nm. This roughness values was achieved using a cutting speed of 1750 rpm, feed rate of 5 mm/min and depth of cut equal to 25 μm.

  7. The binding, transport and fate of aluminium in biological cells.

    Science.gov (United States)

    Exley, Christopher; Mold, Matthew J

    2015-04-01

    Aluminium is the most abundant metal in the Earth's crust and yet, paradoxically, it has no known biological function. Aluminium is biochemically reactive, it is simply that it is not required for any essential process in extant biota. There is evidence neither of element-specific nor evolutionarily conserved aluminium biochemistry. This means that there are no ligands or chaperones which are specific to its transport, there are no transporters or channels to selectively facilitate its passage across membranes, there are no intracellular storage proteins to aid its cellular homeostasis and there are no pathways which evolved to enable the metabolism and excretion of aluminium. Of course, aluminium is found in every compartment of every cell of every organism, from virus through to Man. Herein we have investigated each of the 'silent' pathways and metabolic events which together constitute a form of aluminium homeostasis in biota, identifying and evaluating as far as is possible what is known and, equally importantly, what is unknown about its uptake, transport, storage and excretion. Copyright © 2014 Elsevier GmbH. All rights reserved.

  8. Effects of Aluminium Sulfate on Cadmium Accumulation in Rice

    International Nuclear Information System (INIS)

    Khamvarn, Vararas; Boontanon, Narin; Prapagdee, Benjaphorn; Kumsopa, Acharaporn; Boonsirichai, Kanokporn

    2011-06-01

    Full text: Cadmium accumulation in Pathum Thani 1 and Suphan Buri 60 rice cultivars was investigated upon treatment with aluminium sulfate as a precipitant. Rice was grown hydroponically in a medium containing 4 ppm cadmium nitrate with or without 4 ppm aluminium sulfate. Root, stem with leaves and grain samples were collected and analyzed for cadmium content using atomic absorption spectroscopy and inductively coupled plasma atomic emission spectroscopy. Without the addition of aluminium sulfate, Pathum Thani 1 and Suphan Buri 60 accumulated 24.71∫ 3.14 ppm and 34.43 ∫ 4.51 ppm (dry weight of whole plant) of cadmium, respectively. With aluminium sulfate, cadmium accumulation increased to 40.66 ∫ 2.47 ppm and 62.94 ∫ 10.69 ppm, respectively. The addition of aluminium sulfate to the planting medium did not reduce cadmium accumulation but caused the rice to accumulate more cadmium especially in the shoots and grains. This observation might serve as the basis for future research on the management of agricultural areas that are contaminated with cadmium and aluminium

  9. The effect of aluminium nanocoating and water pH value on the wettability behavior of an aluminium surface

    Science.gov (United States)

    Ali, Naser; Teixeira, Joao A.; Addali, Abdulmajid; Al-Zubi, Feras; Shaban, Ehab; Behbehani, Ismail

    2018-06-01

    Experimental investigation was performed to highlight the influence of ionic bounding and surface roughness effects on the surface wettability. Nanocoating technique via e-beam physical vapor deposition process was used to fabricate aluminium (Al) film of 50, 100, and 150 nm on the surface of an Al substrate. Microstructures of the samples before and after deposition were observed using an atomic force microscopy. A goniometer device was later on used to examine the influence of surface topography on deionised water of pH 4, 7 and 9 droplets at a temperature ranging from 10 °C to 60 °C through their contact angles with the substrate surface, for both coated and uncoated samples. It was found that, although the coated layer has reduced the mean surface roughness of the sample from 10.7 nm to 4.23 nm, by filling part of the microstructure gaps with Al nanoparticles, the wettability is believed to be effected by the ionic bounds between the surface and the free anions in the fluid. As the deionised water of pH 4, and 9 gave an increase in the average contact angles with the increase of the coated layer thickness. On the other hand, the deionised water of pH 7 has showed a negative relation with the film thickness, where the contact angle reduced as the thickness of the coated layer was increased. The results from the aforementioned approach had showed that nanocoating can endorse the hydrophobicity (unwitting) nature of the surface when associated with free ions hosted by the liquid.

  10. Stable beams

    CERN Multimedia

    2015-01-01

    Stable beams: two simple words that carry so much meaning at CERN. When LHC page one switched from "squeeze" to "stable beams" at 10.40 a.m. on Wednesday, 3 June, it triggered scenes of jubilation in control rooms around the CERN sites, as the LHC experiments started to record physics data for the first time in 27 months. This is what CERN is here for, and it’s great to be back in business after such a long period of preparation for the next stage in the LHC adventure.   I’ve said it before, but I’ll say it again. This was a great achievement, and testimony to the hard and dedicated work of so many people in the global CERN community. I could start to list the teams that have contributed, but that would be a mistake. Instead, I’d simply like to say that an achievement as impressive as running the LHC – a machine of superlatives in every respect – takes the combined effort and enthusiasm of everyone ...

  11. Lake restoration with aluminium, bentonite and Phoslock: the effect on sediment stability and light attenuation

    DEFF Research Database (Denmark)

    Egemose, Sara; Reitzel, Kasper; Flindt, Mogens

    treatments on aluminium mobility, sediment stability or light climate. A laboratory flume experiment including three shallow Danish lakes was conducted. We measured the effects of aluminium, Phoslock (a commercial product), bentonite, and a combination of bentonite/aluminium. Each treatment caused a varying...... consolidation of the sediment. The largest consolidation occurred using Phoslock- and bentonite-addition followed by bentonite/aluminium-addition, whereas aluminium alone had no effect. Sediment stability thresholds were measured before and after addition. Especially Phoslock, but also bentonite and bentonite....../aluminium increased sediment erosion threshold, with respectively 200%, 43% and 57%. Aluminium, bentonite/aluminium, and Phoslock improved the light conditions in the water phase, with respectively 60%, 57% and 50%, whereas bentonite created higher turbidity. Conclusively aluminium improved the light conditions...

  12. Investigation of aluminium state in some popular food, which are cooked in aluminium vessels, using spectroscopic analysis methods

    International Nuclear Information System (INIS)

    Al-Shahneh, M.; Saheune, Kh.

    2009-01-01

    Aluminium and lead elements were determined in drinking water and salt solution from chick-pea and faba-bean cooked in aluminium vessels and others from teflon for comparison using atomic absorption spectroscopy by graphite furnace. The relationship between heating time and aluminium quantities transferred to these food solutions was investigated. The lead element was determined taking into consideration the fact that this element may enter in these vessels somehow during the manufacturing process. Results show that the highest value of aluminium quantities was recorded in salt solution ( 17.022 μg/ml) without heating , followed by chick-pea solution (9.95 μg/ml), then faba-bean solution (2.81 μg/ml) when the heated period was 120 minutes. (author)

  13. Wear behavior of carbon fiber/aluminium-composites during abrasive loading; Verschleissverhalten von Kohlenstoffaser/Aluminium-Verbunden unter abrasiver Beanspruchung

    Energy Technology Data Exchange (ETDEWEB)

    Wielage, B.; Dorner, A. [Technische Univ. Chemnitz (Germany). Lehrstuhl fuer Verbundwerkstoffe

    1998-07-01

    Abrasive wear resistance of aluminium is significantly improved by the reinforcement with a high volume percentage of carbon fibres. The wear of unreinforced aluminium after scratching by a diamond indenter can be described as pure microgrooving without any micro-chipping. After integration of 70 vol.-% carbon fibers the damage mechanism is considerably altered and a great amount of micro-chipping occurs. The abrasive wear is strongly influenced by the fiber orientation. The best wear resistance is observed when the fibers are orientated perpendicular to the wear surface. (orig.) [Deutsch] Die Verstaerkung von Aluminium mit einem hohen Volumengehalt endloser Kohlenstoffasern verbessert erkennbar dessen Resistenz gegenueber Abrasionsverschleiss. Der Verschleiss von unverstaerktem Aluminium infolge des Ritzens mit einem Diamantindenter erfolgt in Form von reinem Mikrofurchen ohne Spanbildung. Aufgrund der Integration von 70 Vol.-% Kohlenstoffasern wird eine erhebliche Zunahme des Schaedigungsmechanismus Mikrospanen festgestellt. Die Faserorientierung hat merklichen Einfluss auf die Sensibilitaet gegenueber Abrasion. Orientierung der anisotropen Kohlenstoffasern senkrecht zur Verschleissoberflaeche bedingt den geringsten Abrasionsverschleiss. (orig.)

  14. Acute aluminium phosphide poisoning: Can we predict mortality?

    Directory of Open Access Journals (Sweden)

    Ashu Mathai

    2010-01-01

    Full Text Available In India, acute aluminium phosphide poisoning (AAlPP is a serious health care problem. This study aimed to determine the characteristics of AAlPP and the predictors of mortality at the time of patients′ admission. We studied consecutive admissions of patients with AAlPP admitted to the intensive care unit (ICU between November 2004 and October 2006. We noted 38 parameters at admission to the hospital and the ICU and compared survivor and non-survivor groups. A total of 27 patients were enrolled comprising5 females and 22 males and the mean ingested dose of poison was 0.75 ± 0.745 grams. Hypotension was noted in 24 patients (89% at admission and electrocardiogram abnormalities were noted in 13 patients (48.1%. The mean pH on admission was 7.20 ± 0.14 and the mean bicarbonate concentration was 12.32 ± 5.45 mmol/ L. The mortality from AAlPP was 59.3%. We found the following factors to be associated with an increased risk of mortality: a serum creatinine concentration of more than 1.0 mg % (P = 0.01, pH value less than 7.2 (P = 0.014, serum bicarbonate value less than 15 mmol/L (P = 0.048, need for mechanical ventilation (P = 0.045, need for vasoactive drugs like dobutamine (P = 0.027 and nor adrenaline (P = 0.048 and a low APACHE II score at admission (P = 0.019. AAlPP causes high mortality primarily due to early haemodynamic failure and multi-organ dysfunction

  15. Electrical connection for aluminium conductors in automotive applications : Prestudy of available solutions for electrical connection methods of aluminium cables

    OpenAIRE

    Hamedi, Emilia

    2017-01-01

    Due to increasing weight of electrical component and wiring harnesses in a vehicle contrary to the demand of light constructed vehicles as well as the constantly increasing and fluctuating price of copper compared to aluminium’s stable and far lower price, the use of aluminium conductors as an alternative have been promoted.  This thesis work lay theoretical research of the available methods used for electrical connection of aluminium conductors in order to increase the knowledge about the av...

  16. Half value layer determination of Al and Cu for different x-ray beams and establishing a relationship between them

    International Nuclear Information System (INIS)

    Kharita, M. H.; Takeyeddin, M.; Wali, K.; Zahili, M.

    2005-03-01

    The Half Value Layer (HVL) of copper and aluminium for special standard x-rays beams (emitted from x-ray machine type Philips MGC30 used in Secondary Standard Dosimetry Laboratory (SSDL) have been determined. The relationship between HVL values of aluminium and copper was established. This relationship can be represented by a non-linear fit. These results are valuable for x-ray workers especially those working in the field of radiation calibration for beam energy determination. Using the results of this study, unavailable thickness of one metal can be replaced by the corresponding thickness of the other metal, for filtration and measurement of x-ray beam. (Authors)

  17. Crack growth behaviour of aluminium wrought alloys in the Very High Cycle Fatigue regime

    Directory of Open Access Journals (Sweden)

    Bülbül Fatih

    2018-01-01

    Full Text Available Investigations have shown that in the regime of Very High Cycle Fatigue (VHCF “natural” crack initiation often takes place underneath the material surface leading to crack propagation without contact to atmospheric components. In order to elucidate the environmental damage contribution and its effect on the VHCF long crack propagation, fatigue experiments with alternating environment (vacuum and laboratory air were performed. An ultrasonic fatigue testing system (USFT equipped with a small vacuum chamber was applied that enables the in-situ examination of the long fatigue crack propagation at a resonance frequency of about 20 kHz by using a long distance microscope. By means of the Focused-Ion-Beam technique, micro-notches were prepared in the USFT specimens. The tests were carried out on the aluminium alloys EN-AW 6082 and 5083 in different conditions. It has been found that the atmosphere has a significant influence on the VHCF long crack propagation which manifests itself in the crack path as well as in the crack growth rates. Because of pronounced single sliding in vacuum, shear-stress-controlled crack propagation was detected whereas in laboratory air normal-stress-controlled crack propagation occurred. Furthermore, it has been proven that the secondary precipitation state of the aluminium alloy significantly influences the VHCF long crack propagation in vacuum.

  18. Process optimization in Nd:YAG laser microdrilling of alumina–aluminium interpenetrating phase composite

    Directory of Open Access Journals (Sweden)

    Ranjib Biswas

    2015-07-01

    Full Text Available In laser beam micromachining process, the quality of the drilled hole is of great importance. The quality of the microdrilled hole mainly depends on appropriate selection of process parameters. Predefined diameter of hole with minimum taper is of today's demand. The composite used for microdrilling operation is alumina–aluminium (Al2O3–Al interpenetrating phase composite (IPC, which is widely used in aircraft and space stations. Until date, no experimental study has been done to obtain microdrilled hole of desired diameter. In the present paper three hole qualities such as hole diameter at entry, at exit and hole taper have been optimized individually as well as simultaneously using a central composite design (CCD based on response surface methodology (RSM during pulsed Nd:YAG laser microdrilling operation on alumina–aluminium IPC sheet of 1.14 mm thickness. The analysis of variance (ANOVA test has also been done to identify the process parameters that contributed the most to get desired hole quality.

  19. Radiographic and ultrasonic testings of welded joints of 6063 aluminium alloy

    International Nuclear Information System (INIS)

    Oliveira e Silva Mury, A.G. de.

    1980-05-01

    A study on evaluation of weld defects in aluminium butt joints was made in a comparative way through the radiographic and ultrasonic testing. This work was conducted with pipes 5 IPS (6,35 mm thickness) of 6063 aluminium alloy, circumferential TIG welded, due to the difficulty on performing non-destructive testing with this schedule. It was concluded thta ultrasonic testing has adequate sensitivity when setting gain adjustment is made with aid of a reference curve constructed by using a Reference Block (among others studied) with 1,5 mm dia. Hole as reference reflector, and a 5 MHz angle beam search-unit. In this case the ultrasonic testing is more accurate than radiographic testing to detect planar defects like lack of fusion and lack of penetration. Defect sizing by ultrasonic methods employed were 6 and 20 dB drop methods. In spite of your observed limitations concerning the establishment of the real size of defects, the procedure applied was precise for locate and define the weld defects that where found in this study. (author) [pt

  20. Determination of trace concentrations of aluminium in rice samples by INAA and PIGE methods

    International Nuclear Information System (INIS)

    Nanda, B.B.; Biswal, R.R.; Acharya, R.; Pujari, P.K.

    2015-01-01

    Aluminium is one of the toxic elements entering human body mainly through food and food products. Though its bioavailability is very less, it is necessary to evaluate its total concentrations in food and food products entering to the body through. In order to evaluate total aluminium contents in various food items for daily dietary intake of aluminum, authors have systematically planned to carry out experiments in various food items including rice. Rice is the main food in many parts of India as well as in Odisha. Rice samples under study belong to three categories; (i) various rice samples from local market, (ii) various rice samples grown in similar irrigation (soil and water) conditions and (iii) same variety of rice with different irrigation conditions. Solid samples (pre-cleaned) were powdered, homogenized and taken for analysis by two nuclear analytical techniques (NATs) namely instrumental neutron activation analysis (INAA) using reactor neutrons at BARC and particle induced gamma ray emission (PIGE) using 4 MeV proton beam (20 nA current) from 3 MV Tandetron at IOP, Bhubaneswar in conjunction with high resolution gamma-ray spectrometry. Samples of 10-50 mg for INAA and 250 mg (pelletized in cellulose) for PIGE were used for experiments. For INAA, samples were irradiated at PCF, Dhruva reactor for 1 minute

  1. Irradiation effects on aluminium and beryllium

    International Nuclear Information System (INIS)

    Bieth, M.

    1992-01-01

    The High Flux Reactor (HFR) in Petten (The Netherlands) is a 45 MW light water cooled and moderated research reactor. The vessel was replaced in 1984 after more than 20 years of operation because doubts had arisen over the condition of the aluminium alloy construction material. Data on the mechanical properties of the aluminium alloy Al 5154 with and without neutron irradiation are necessary for the safety analysis of the new HFR vessel which is constructed from the same material as the old vessel. Fatigue, fracture mechanics (crack growth and fracture toughness) and tensile properties have been obtained from several experimental testing programmes with materials of the new and the old HFR vessel. 1) Low-cycle fatigue testing has been carried out on non-irradiated specimens from stock material of the new HFR vessel. The number of cycles to failure ranges from 90 to more than 50,000 for applied strain from 3.0% to 0.4%; 2) Fatigue crack growth rate testing has been conducted: - with unirradiated specimens from stock material of the new vessel; - with irradiated specimens from the remnants of the old core box. Irradiation has a minor effect on the sub-critical fatigue crack growth rate. The ultimate increase of the mean crack growth rate amounts to a factor of 2. However crack extension is strongly reduced due to the smaller crack length for crack growth instability (reduction of K IC ). - Irradiated material from the core box walls of the old vessel has been used for fracture toughness testing. The conditional fracture toughness values K IQ ranges from 30.3 down to 16.5 MPa√m. The lowermost meaningful 'K IC ' is 17.7 MPa√m corresponding to the thermal fluence of 7.5 10 26 n/m 2 for the End of Life (EOL) of the old vessel. - Testing carried out on irradiated material from the remnants of the old HFR core box shows an ultimate neutron irradiation hardening of 35 points increase of HSR 15N and an ultimate tensile yield stress of 589 MPa corresponding to the

  2. Trace aluminium determination and sampling problems of archeological bone employing destructive neutron activation analysis

    International Nuclear Information System (INIS)

    Blotcky, A.J.; Rack, E.P.; Recker, R.R.; Leffler, J.A.; Teitelbaum, S.

    1978-01-01

    A destructive neutron activation analysis procedure was developed for determining trace aluminium content in bone. The method is based on a carefully planned sample preparation, irradiation at a neutron flux for 3.1x10 11 nxcm -2 xs -1 for 5 minutes, and chemical separation based on ion exchange. It was found that bone samples soaked in aluminium containing soil gave highly elevated aluminium values as a result of the aluminium adsorption into the bone matrix. The maximum aluminium content values for prehistoric bones are larger than those of modern bones and comparable to aluminium levels present in bone from renal patients. (T.G.)

  3. Ion beam analysis

    International Nuclear Information System (INIS)

    Bethge, K.

    1995-01-01

    Full text: Ion beam analysis is an accelerator application area for the study of materials and the structure of matter; electrostatic accelerators of the Van de Graaff or Dynamitron type are often used for energies up to a few MeV. Two types of machines are available - the single-ended accelerator type with higher beam currents and greater flexibility of beam management, or the tandem accelerator, limited to atomic species with negative ions. The accelerators are not generally installed at specialist accelerator laboratories and have to be easy to maintain and simple to operate. The most common technique for industrial research is Rutherford Back Scattering Spectrometry (RBS). Helium ions are the preferred projectiles, since at elevated energies (above 3 MeV) nuclear resonance scattering can be used to detect photons associated with target molecules containing elements such as carbon, nitrogen or oxygen. Due to the large amount of available data on nuclear reactions in this energy range, activation analysis (detecting trace elements by irradiating the sample) can be performed with charged particles from accelerators over a wider range of atoms than with the conventional use of neutrons, which is more suited to light elements. Resonance reactions have been used to detect trace metals such as aluminium, titanium and vanadium. Hydrogen atoms are vital to the material performance of several classes of materials, such as semiconductors, insulators and ceramics. Prudent selection of the projectile ion aids the analysis of hydrogen composition; the technique is then a simple measurement of the emitted gamma radiation. Solar cell material and glass can be analysed in this way. On a world-wide basis, numerous laboratories perform ion beam analysis for research purposes; considerable work is carried out in cooperation between scientific laboratories and industry, but only a few laboratories provide a completely commercial service

  4. Aluminium based amorphous and nanocrystalline structure

    Energy Technology Data Exchange (ETDEWEB)

    Sitek, Jozef; Degmova, Jarmila, E-mail: jarmila.degmova@stuba.sk [Slovak University of Technology, Department of Nuclear Physics and Technology, Faculty of Electrical Engineering and Information Technology (Slovakia)

    2005-09-15

    Aluminium based rapidly quenched alloys of nominal composition Al{sub 90}Fe{sub 7}Nb{sub 3} and Al{sub 94}Fe{sub 2}V{sub 4} were studied by Moessbauer spectroscopy. Samples annealed up to 573 K showed amorphous structure represented by quadrupole doublet. From corrected spectra areas the values of f-factor were calculated. In the case of AlFeNb samples f-factor was estimated as f = 0.26 and for AlFeV f = 0.31. The corresponding Debye temperatures were also calculated. Higher temperature annealing at 773 and 873 K induced deformation of nano- and microcrystalline state. Moessbauer spectra of samples of both compositions (with vanadium as well as with niobium) annealed at 773 K showed superposition of crystalline phases with dominant role of Al{sub 3}Fe alloy. During annealing at 873 K, phases with large grains and small amount of FeAl metastable phase were developed (Das et al. Mat. Sci. Eng., A304-A306, 159, 2001; Illekova et al. Mat. Sci. Eng., A375-A377, 946, 2004).

  5. Aluminium based amorphous and nanocrystalline structure

    International Nuclear Information System (INIS)

    Sitek, Jozef; Degmova, Jarmila

    2005-01-01

    Aluminium based rapidly quenched alloys of nominal composition Al 90 Fe 7 Nb 3 and Al 94 Fe 2 V 4 were studied by Moessbauer spectroscopy. Samples annealed up to 573 K showed amorphous structure represented by quadrupole doublet. From corrected spectra areas the values of f-factor were calculated. In the case of AlFeNb samples f-factor was estimated as f = 0.26 and for AlFeV f = 0.31. The corresponding Debye temperatures were also calculated. Higher temperature annealing at 773 and 873 K induced deformation of nano- and microcrystalline state. Moessbauer spectra of samples of both compositions (with vanadium as well as with niobium) annealed at 773 K showed superposition of crystalline phases with dominant role of Al 3 Fe alloy. During annealing at 873 K, phases with large grains and small amount of FeAl metastable phase were developed (Das et al. Mat. Sci. Eng., A304-A306, 159, 2001; Illekova et al. Mat. Sci. Eng., A375-A377, 946, 2004).

  6. Acute aluminium phosphide poisoning, what is new?

    Directory of Open Access Journals (Sweden)

    Yatendra Singh

    2014-01-01

    Full Text Available Aluminium phosphide (AlP is a cheap solid fumigant and a highly toxic pesticide that is commonly used for grain preservation. AlP has currently generated interest with increasing number of cases in the past four decades because of its increased use for agricultural and nonagricultural purposes, and also its easy availability in the markets has led to its increased misuse to commit suicide. Ingestion is usually suicidal in intent, uncommonly accidental and rarely homicidal. The poison affects all systems, shock, cardiac arrhythmias with varied ECG changes and gastrointestinal features being the most prominent. Diagnosis is made on the basis of clinical suspicion, a positive silver nitrate paper test to phosphine, and gastric aspirate and viscera biochemistry. Treatment includes early gastric lavage with potassium permanganate or a combination of coconut oil and sodium bicarbonate, administration of charcoal and palliative care. Specific therapy includes intravenous magnesium sulphate and oral coconut oil. Unfortunately, the lack of a specific antidote Results in very high mortality and the key to treatment lies in rapid decontamination and institution of resuscitative measures. This article aims to identify the salient features and mechanism of AlP poisoning along with its management strategies and prognostic variables.

  7. Corrosion of aluminium in soft drinks.

    Science.gov (United States)

    Seruga, M; Hasenay, D

    1996-04-01

    The corrosion of aluminium (Al) in several brands of soft drinks (cola- and citrate-based drinks) has been studied, using an electrochemical method, namely potentiodynamic polarization. The results show that the corrosion of Al in soft drinks is a very slow, time-dependent and complex process, strongly influenced by the passivation, complexation and adsorption processes. The corrosion of Al in these drinks occurs principally due to the presence of acids: citric acid in citrate-based drinks and orthophosphoric acid in cola-based drinks. The corrosion rate of Al rose with an increase in the acidity of soft drinks, i.e. with increase of the content of total acids. The corrosion rates are much higher in the cola-based drinks than those in citrate-based drinks, due to the facts that: (1) orthophosphoric acid is more corrosive to Al than is citric acid, (2) a quite different passive oxide layer (with different properties) is formed on Al, depending on whether the drink is cola or citrate based. The method of potentiodynamic polarization was shown as being very suitable for the study of corrosion of Al in soft drinks, especially if it is combined with some non-electrochemical method, e.g. graphite furnace atomic absorption spectrometry (GFAAS).

  8. Oxidation of {phi}'-aluminium oxynitride

    Energy Technology Data Exchange (ETDEWEB)

    Xolin, E. [Universite de Lyon, INSA-Lyon, MATEIS, UMR CNRS 5510, 20, av Albert Einstein, F-69621 Villeurbanne cedex (France); Jorand, Y., E-mail: Yves.Jorand@insa-lyon.f [Universite de Lyon, INSA-Lyon, MATEIS, UMR CNRS 5510, 20, av Albert Einstein, F-69621 Villeurbanne cedex (France); Olagnon, C.; Gremillard, L. [Universite de Lyon, INSA-Lyon, MATEIS, UMR CNRS 5510, 20, av Albert Einstein, F-69621 Villeurbanne cedex (France)

    2011-03-15

    Research highlights: Oxidation of {phi}'-AlON has been studied for the first time. First corrosion products are {gamma}-alumina. Low density {alpha}-alumina is formed at high temperature. Grains are extensively cracked after oxidation. The low density of the {alpha}-alumina is due to a network of nanometric porosities. - Abstract: The oxidation in air of single crystal {phi}'-aluminium oxynitride (AlON) grains has been characterized by thermogravimetry and X-ray diffraction in the 1273-1673 K range. Two oxidation stages have been observed, suggesting the formation of a transitional phase. Below 1473 K, oxidation results in the apparition of platelets and noodle-like crystals on the surface of the initially faceted single crystals. Above 1473 K, low density {alpha}-alumina polycrystals start forming on the grain surface and grow towards the grain core with increasing temperature or time. Their low density is mainly due to the presence of a network of nano-porosities.

  9. Development and applications of ultrafine aluminium powders

    International Nuclear Information System (INIS)

    Kearns, Martin

    2004-01-01

    Over the last 20 years or so, a variety of new technologies has been developed to produce sub-micron powders. Among the products attracting interest is nanoaluminium which is being evaluated in specialist propulsion and exothermic end-uses. This paper examines the advances made in 'nanopowder' production in the context of the existing aluminium powder industry where finest commercial grades have a median size of ∼6 μm (one or two orders of magnitude coarser than nanopowders) and which today supplies the markets being targeted by nanopowders with coarser, but effective products. Are there genuine market opportunities for nanoaluminium and if so, how will they be produced? One the one hand there are the novel nanopowder production methods which are high yielding but generally slow and costly, while on the other, there is the very fine fraction from conventional atomising routes which generate a very low yield of sub-micron powder but which nevertheless can translate into a meaningful rate as part of the bulk production. Can conventional routes ever hope to make sufficient volumes of nanopowders cost effectively and which will be the favoured routes in future? Moreover, what of the 'ultrafine' size range (∼0.5-5 μm) which is of more immediate potential interest to today's powder users. This paper seeks to identify the near term opportunities for application of low volume/high value ultrafine and nano powders

  10. Design of Grain Refiners for Aluminium Alloys

    Science.gov (United States)

    Tronche, A.; Greer, A. L.

    The efficiency of a grain refiner can be quantified as the number of grains per nucleant particle in the solidified product. Even for effective refiners in aluminium, such as Al-5Ti-1B, it is known from experiments that efficiencies are very low, at best 10-3 to 102. It is of interest to explore the reasons for such low values, and to assess the prospects for increased efficiency though design of refiners. Recently it has been shown [1] that a simple recalescence-based model can make quantitative predictions of grain size as a function of refiner addition level, cooling rate and solute content. In the model, the initiation of grains is limited by the free growth from nucleant particles, the size distribution of which is very important. The present work uses this model as the basis for discussing the effect of particle size distribution on grain refiner performance. Larger particles (of TiB2 in the case of present interest) promote greater efficiency, as do narrower size distributions. It is shown that even if the size distribution could be exactly specified, compromises would have to be made to balance efficiency (defined as above) with other desirable characteristics of a refiner.

  11. Bioaccumulation of Aluminium in Hydromacrophytes in Polish Coastal Lakes

    Directory of Open Access Journals (Sweden)

    Senze Magdalena

    2015-03-01

    Full Text Available The research on aluminium content was conducted in water and on aquatic flora of Polish lakes in the central part of the coast. The study included the lakes Sarbsko, Choczewskie, Bia.e, K.odno, D.brze and Salino investigated in the summer of 2013. The examined lakes belong mainly to the direct basin of the Baltic Sea. Samples of aquatic plants and lake waters were collected. In the water samples pH and electrolytic conductivity were measured. The aluminium content was determined both in water and aquatic plants. Submerged hydromacrophyte studies included Myriophyllum alterniflorum L., Potamogeton perfoliatus L. and Ceratophyllum demersum L. Emergent hydromacrophyte studies included Phragmites australis (Cav. Trin. ex Steud., Juncus bulbosus L., Iris pseudacorus L., Eleocharis palustris (L. Roem. % Schult., Phalaris arundinacea L., Carex riparia Curt., Mentha aquatic L., Stratiotes aloides L., Alisma plantago-aquatica L., Glyceria maxima (Hartman Holmb., Sagittaria sagittifolia L., Scirpus lacustris L. and Typha angustifolia L. The purpose of this investigation was the determination of the aluminium content in submerged and emergent hydromacrophytes and also the definition of their bioaccumulative abilities. The average concentration of aluminium in water was 2.68 fęg Al dm.3. The average content of aluminium in plants was 2.8015 mg Al kg.1. The bioaccumulation factor ranged from BCF=19.74 to BCF=16619. On the basis of the analysis of the aluminium content in water and aquatic plants results show that both water and plants were characterized by a moderate level of aluminium. The recorded concentrations indicate a mid-range value and are much lower than those which are quoted for a variety of surface waters in various parts of the world.

  12. Magnetic field dependence observed by {sup 27} Al NMR of species contained in alumina colloidal dispersions; Dependencia de campo magnetico observada por RMN {sup 27} Al de especies presentes em dispersoes coloidais de alumina

    Energy Technology Data Exchange (ETDEWEB)

    Morgado Junior, Edisson; Menezes, Sonia M.C. [PETROBRAS, Rio de Janeiro, RJ (Brazil). Centro de Pesquisas; San Gil, Rosane [Universidade Federal, Rio de Janeiro, RJ (Brazil). Inst. de Quimica

    1995-12-31

    The behaviour of some aluminium species front a magnetic field have been investigated by {sup 27} Al NMR analysis, this method was used for characterization of an octahedric aluminium specie from sols prepared by bohemite acid peptization. X-ray diffraction data have identified the mineral structure. The results have been shown and discussed, and NMR spectra were also presented and studied. Concluding this work, the nature of a colloidal specie of alumina was clarified through the dependence research of magnetic field by {sup 27} Al NMR 12 refs., 4 figs., 2 tabs.

  13. Recuperative aluminium recycling plant. A demonstration at J. McIntyre (Aluminium) Ltd. [Nottingham (GB)

    Energy Technology Data Exchange (ETDEWEB)

    1991-04-01

    Direct energy savings worth up to 470,000 pounds/year are being achieved by J McIntyre (Aluminium) Ltd in the United Kingdom as a result of the development of a recuperative aluminium recycling plant. The overall design incorporates a novel version of a closed-well furnace coupled with a radically improved design of dry hearth furnace. The plant not only treats clean scrap more efficiently than at present, but will also treat contaminated scrap which has not previously been recycled in an environmentally acceptable way. This is because the plant incorporates fume pyrolysis, afterburning of organics, recuperation and fume treatment. At 1987 prices the total installed plant cost was 1.3M.pounds. The direct energy saving at 1987 fuel prices was between 294,000 and 470,000pounds/year. Also, the improved melting technique has reduced metal lost as dross by 2 - 8% (420 -1,680 tonnes/year) when compared to other furnace operations. The improved metal recovery (1987 prices) was worth a further 400,000 pounds - 1,600,000 pounds. Taking median figures for the total fuel-plus-metal savings results in a payback on the project of only 14 months, some six months less than anticipated. Other consequential benefits which have also helped in reducing operating costs have been improvements in output per man, reductions in sickness and absenteeism, and reduced down-time for maintenance and repair. (author).

  14. Microstructure and properties of aluminium-aluminium oxide graded composite materials

    Science.gov (United States)

    Kamaruzaman, F. F.; Nuruzzaman, D. M.; Ismail, N. M.; Hamedon, Z.; Iqbal, A. K. M. A.; Azhari, A.

    2018-03-01

    In this research works, four-layered aluminium-aluminium oxide (Al-Al2O3) graded composite materials were fabricated using powder metallurgy (PM) method. In processing, metal-ceramic graded composite materials of 0%, 10%, 20% and 30% weight percentage of ceramic concentration were prepared under 30 ton compaction load using a cylindrical die-punch set made of steel. After that, two-step pressureless sintering was carried out at sintering temperature and time 600°C and 3 hours respectively. It was observed that the sintered cylindrical specimens of 30 mm diameter were prepared successfully. The graded composite specimens were analysed and the properties such as density, microstructure and hardness were measured. It was found that after sintering process, the diameter of the graded cylindrical structure was decreased. Using both Archimedes method and rule of mixture (ROM), he density of structure was measured. The obtained results revealed that the microvickers hardness was increased as the ceramic component increases in the graded layer. Moreover, it was observed that the interface of the graded structure is clearly distinguished within the multilayer stack and the ceramic particles are almost uniformly distributed in the Al matrix.

  15. Aluminium alloys containing iron and nickel; Alliages d'aluminium contenant du fer et du nickel

    Energy Technology Data Exchange (ETDEWEB)

    Coriou, H.; Fournier, R.; Grall, L.; Hure, J. [Commissariat a l' Energie atomique, Centre d' Etudes Nucleaires de Saclay, Departement de Metallurgie et de Chimie Appliquee (France); Herenguel, J.; Lelong, P. [Centre de Recherches d' Antony, des Trefileries et Laminoirs du Havre (France)

    1958-07-01

    The first part of this report addresses mechanism, kinetics and structure factors of aluminium alloys containing iron and nickel in water and high temperature steam. The studied alloys contain from 0.3 to 0.7 per cent of iron, and 0.2 to 1.0 per cent of nickel. Corrosion resistance and corrosion structure have been studied. The experimental installation, process and samples are presented. Corrosion structures in water at 350 C are identified and discussed (structure of corrosion products, structure of metal-oxide interface), and then in steam at different temperatures (350-395 C). Corrosion kinetics is experimentally studied (weight variation in time) in water at 350 C and in steam at different temperatures. Reactions occurring at over-heated steam (more than 400 C) are studied, and the case of welded alloys is also addressed. The second part addresses the metallurgical mechanism and processes influencing aluminium alloy resistance to corrosion by high temperature water as it appeared that separated phases protect the solid solution through a neighbourhood action. In order to avoid deep local corrosions, it seems necessary to multiply protective phases in an as uniform as possible way. Some processes enabling this result are described. They belong to conventional metallurgy or to powder metallurgy (with sintering and extrusion)

  16. Aluminium Matrix Composites Reinforced with Co-continuous Interlaced Phases Aluminium-alumina Needles

    Directory of Open Access Journals (Sweden)

    Elvio de Napole Gregolin

    2002-09-01

    Full Text Available An Al-5SiO2 (5 wt% of SiO2 aluminium matrix fiber composite was produced where the reinforcement consists of fossil silica fibers needles. After being heat-treated at 600 °C, the original fiber morphology was retained but its microstructure changed from solid silica to an interconnected (Al-Si/Al2O3 interlaced structure named co-continuous composite. A technique of powder metallurgy, using commercial aluminium powder and the silica fibers as starting materials, followed by hot extrusion, was used to produce the composite. The co-continuous microstructure was obtained partially or totally on the fibers as a result of the reaction, which occurs during the heat treatment, first by solid diffusion and finally by the liquid Al-Si in local equilibrium, formed with the silicon released by reaction. The internal structure of the fibers was characterized using field emission electron microscope (FEG-SEM and optical microscopy on polished and fractured samples.

  17. Influence of nanoporous structure on mechanical strength of aluminium and aluminium alloy adhesive structural joints

    International Nuclear Information System (INIS)

    Spadaro, C; Dispenza, C; Sunseri, C

    2006-01-01

    The influence of surface treatments on the mechanical strength of adhesive joints was investigated. The attention was focused on AA2024 alloy because it is extensively used in both the automotive and aerospace industries. Adhesive joints fabricated with pure aluminium were also investigated in order to evidence possible differences in the surface features after identical treatments. Before joining with a commercial epoxy adhesive, metal substrates were subjected to different kinds of treatment and the surfaces were characterized by SEM analysis. The formation of a microporous surface in the AA2024 alloy, upon etching and anodizing, is discussed on the basis of the role of the intermetallic particles and their electrochemical behaviour with respect to the aluminium matrix. Moreover, nanostructured porous oxide layers on both type of substrate were also formed, as a consequence of the anodizing process. Differences in their morphologies were revealed as a function of both the applied voltage and the presence of alloying elements. On this basis, an explanation of the different values of fracture energy measured by means of T-peel tests carried out on the corresponding joints was attempted

  18. Bond quality control of aluminium stabilised superconductors with ultrasonic phased-array technology

    International Nuclear Information System (INIS)

    Neuenschwander, J.; Luethi, T.; Horvath, I.L.

    2001-01-01

    Novel aluminium stabilised superconductors are currently being produced for the Large Hadron Collider detectors ATLAS and CMS. For a satisfying service of the conductor an intact bonding between the different constituents must be guaranteed. We have shown previously that ultrasonics is a powerful tool for checking the bond quality. However, up to now the full width of the bond could be inspected only on short samples with a mechanical scanner. The essence of this presentation is the introduction of the phased-array technique which allows a continuous analysis of the complete bond over km-long conductor units during their manufacture. For now, more than 50 km of conductor have been tested during co-extrusion. Disbondings are detected as regions with enhanced echo-amplitudes. We are about to set-up a second system for the control of an electron beam welding process which is used for the reinforcement of the CMS conductor. (orig.)

  19. Aluminium recovery from waste incineration bottom ash, and its oxidation level.

    Science.gov (United States)

    Biganzoli, Laura; Grosso, Mario

    2013-09-01

    The recovery of aluminium (Al) scraps from waste incineration bottom ash is becoming a common practice in waste management. However, during the incineration process, Al in the waste undergoes oxidation processes that reduce its recycling potential. This article investigates the behaviour of Al scraps in the furnace of two selected grate-fired waste-to-energy plants and the amount recoverable from the bottom ash. About 21-23% of the Al fed to the furnace with the residual waste was recovered and potentially recycled from the bottom ash. Out of this amount, 76-87% was found in the bottom ash fraction above 5 mm and thus can be recovered with standard eddy current separation technology. These values depend on the characteristics and the mechanical strength of the Al items in the residual waste. Considering Al packaging materials, about 81% of the Al in cans can be recovered from the bottom ash as an ingot, but this amount decreases to 51% for trays, 27% for a mix of aluminium and poly-laminated foils and 47% for paper-laminated foils. This shows that the recovery of Al from the incineration residues increases proportionally to the thickness of the packaging.

  20. EXPERIMENTAL INVESTIGATION ON TRIBOLOGICAL CHARACTERISTICS OF SILICON NITRIDE REINFORCED ALUMINIUM METAL MATRIX COMPOSITES

    Directory of Open Access Journals (Sweden)

    D. BHUVANESH

    2017-05-01

    Full Text Available Aluminium alloy (LM25 reinforced with silicon nitride was fabricated by liquid metallurgy route. The fabricated composite was investigated for dry sliding wear behaviour by conducting experiments using pin-on-disc tribometer. Set of experiments were planned using Taguchi’s technique and data analysis was carried out using L27 orthogonal array. Analysis of Variance (ANOVA technique was used to determine the significance of parameter with respect to wear rate. Signal-to-Noise ratio was employed to detect the most and least influential parameter as well as their level of influence. ‘Smaller the wear’ characteristic was chosen for the analysis of dry sliding wear. Results implied that, the load has the primary effect on the wear succeeded by the effect of sliding velocity and sliding distance. Scanning Electronic Microscopic studies were carried out on worn surfaces to understand the wear mechanism.Tribological results indicated that LM25 aluminium alloy could be better utilized as a material for piston, rotor and bearings for long life in low speed applications.

  1. Aluminium concentration versus the base cation to aluminium ratio as predictors for aluminium toxicity in Pinus sylvestris and Picea abies seedlings

    NARCIS (Netherlands)

    Schöll, van L.; Keltjens, W.G.; Hoffland, E.; Breemen, van N.

    2004-01-01

    Aluminium (Al) toxicity is considered an important factor in forest deterioration caused by soil acidification. A ratio of base cations (BC) to Al in the soil solution lower than 1 is widely used as an indicator for potentially adverse effects on tree health. In our view, the validity of the

  2. Property enhancement by grain refinement of zinc-aluminium foundry alloys

    International Nuclear Information System (INIS)

    Krajewski, W K; Piwowarski, G; Krajewski, P K; Greer, A L

    2016-01-01

    Development of cast alloys with good mechanical properties and involving less energy consumption during their melting is one of the key demands of today's industry. Zinc foundry alloys of high and medium Al content, i.e. Zn-(15-30) wt.% Al and Zn-(8-12) wt.% Al, can satisfy these requirements. The present paper summarizes the work [1-9] on improving properties of sand-cast ZnAl10 (Zn-10 wt.% Al) and ZnAl25 (Zn-25 wt. % Al) alloys by melt inoculation. Special attention was devoted to improving ductility, whilst preserving high damping properties at the same time. The composition and structural modification of medium- and high-aluminium zinc alloys influence their strength, tribological properties and structural stability. In a series of studies, Zn - (10-12) wt. % Al and Zn - (25-26) wt.% Al - (1-2.5) wt.% Cu alloys have been doped with different levels of added Ti. The melted alloys were inoculated with ZnTi-based refiners and it was observed that the dendritic structure is significantly finer already after addition of 50 - 100 ppm Ti to the melted alloys. The alloy's structure and mechanical properties have been studied using: SEM (scanning electron microscopy), LM (light microscopy), dilatometry, pin-on-disc wear, and tensile strength measurements. Grain refinement leads to significant improvement of ductility in the binary high-aluminium Zn-(25-27) Al alloys while in the medium-aluminium alloys the effect is rather weak. In the ternary alloys Zn-26Al-Cu, replacing a part of Cu with Ti allows dimensional changes to be reduced while preserving good tribological properties. Furthermore, the high initial damping properties were nearly entirely preserved after inoculation. The results obtained allow us to characterize grain refinement of the examined high-aluminium zinc alloys as a promising process leading to the improvement of their properties. At the same time, using low melting ZnTi-based master alloys makes it possible to avoid the excessive melt

  3. Characterisation of weld zone reactions in dissimilar glass-to-aluminium pulsed picosecond laser welds

    Energy Technology Data Exchange (ETDEWEB)

    Ciuca, Octav P., E-mail: octav.ciuca@manchester.ac.uk [School of Materials, University of Manchester, Manchester, M13 9PL (United Kingdom); Carter, Richard M. [Institute of Photonics and Quantum Sciences, Heriot-Watt University, Edinburgh, EH14 4AS (United Kingdom); Prangnell, Philip B. [School of Materials, University of Manchester, Manchester, M13 9PL (United Kingdom); Hand, Duncan P. [Institute of Photonics and Quantum Sciences, Heriot-Watt University, Edinburgh, EH14 4AS (United Kingdom)

    2016-10-15

    Precision welded joints, produced between fused silica glass and aluminium by a newly-developed picosecond-pulse laser technique, have been analysed for the first time using a full range of electron microscopy methods. The welds were produced as lap joints by focusing a 1.2 μm diameter laser beam through the transparent glass top sheet, slightly below the surface of the metal bottom sheet. Despite the extremely short interaction time, extensive reaction was observed in the weld zone, which involved the formation of nanocrystalline silicon and at least two transitional alumina phases, γ- and δ-Al{sub 2}O{sub 3}. The weld formation process was found to be complex and involved: the formation of a constrained plasma cavity at the joint interface, non-linear absorption in the glass, and the creation of multiple secondary keyholes in the metal substrate by beam scattering. The joint area was found to expand outside of the main interaction volume, as the energy absorbed into the low conductivity and higher melting point silica glass sheet melted the aluminium surface across a wider contact area. The reasons for the appearance of nanocrystalline Si and transitional alumina reaction products within the welds are discussed. - Highlights: •Pulsed laser welding of dissimilar materials causes extensive chemical reactivity. •Metastable Al{sub 2}O{sub 3} phases form due to laser-induced highly-transient thermal regime. •Fused silica is reduced by Al to form nanocrystalline Si. •Mechanism of joint formation is discussed.

  4. The structure of high-quality aluminium cast iron

    Directory of Open Access Journals (Sweden)

    D. Kopyciński

    2012-01-01

    Full Text Available In this study presents the analyse of aluminium iron cast structure (as-cast condition which are used in high temperature. While producing the casts of aluminium iron major influence has been preserve the structure of technological process parameters. The addition to Fe-C-Al alloy V, Ti, Cr leads to the improvement of functional and mechanical cast qualities. In this study, a method was investigated to eliminate the presence of undesirable Al4C3 phases in a aluminium cast iron structure and thus improve the production process. V and Ti additions in aluminium cast iron allows to development of FeAl - VC or TiC alloys. In particular, V or Ti contents above 5 wt.% were found to totally eliminate the presence of Al4C3. In addition, preliminary work indicates that the alloy with the FeAl - VC or TiC structure reveals high oxidation resistance. The introduction of 5 wt.% chromium to aluminium cast iron strengthened Al4C3 precipitate. Thus, the resultant alloy can be considered an intermetallic FeAl matrix strengthened by VC and TiC or modified Al4C3 reinforcements.

  5. Computer modelling of age hardening for cast aluminium alloys

    International Nuclear Information System (INIS)

    Wu, Linda; Ferguson, W George

    2009-01-01

    Age hardening, or precipitation hardening, is one of the most widely adopted techniques for strengthening of aluminium alloys. Although various age hardening models have been developed for aluminium alloys, from the large volume of literature reviewed, it appears that the bulk of the research has been concentrated on wrought aluminium alloys, only a few of the established precipitation models have been applied to the casting aluminium alloys. In the present work, there are two modelling methods that have been developed and applied to the casting aluminium alloys A356 and A357. One is based on the Shercliff-Ashby methodology to produce a process model, by which we mean a mathematical relationship between process variables (alloy composition, ageing temperature and time) and material properties (yield strength or hardness) through microstructure evolution (precipitate radius, volume fraction). The other method is based on the Kampmann and Wagner Numerical (KWN) model which deals with concomitant nucleation, growth and coarsening and is thus capable of predicting the full evolution of the particle size distribution and then a strength model is used to evaluate the resulting change in hardness or yield strength at room temperature by taking into account contributions from lattice resistance, solid solution hardening and precipitation hardening.

  6. Cancer risk among workers of a secondary aluminium smelter.

    Science.gov (United States)

    Maltseva, A; Serra, C; Kogevinas, M

    2016-07-01

    Cancer risk in secondary aluminium production is not well described. Workers in this industry are exposed to potentially carcinogenic agents from secondary smelters that reprocess aluminium scrap. To evaluate cancer risk in workers in a secondary aluminium plant in Spain. Retrospective cohort study of male workers employed at an aluminium secondary smelter (1960-92). Exposure histories and vital status through 2011 were obtained through personal interviews and hospital records, respectively. Standardized mortality (SMRs) and incidence ratios (SIRs) were calculated. The study group consisted of 98 workers. We found increased incidence and mortality from bladder cancer [SIR = 2.85, 95% confidence interval (CI) 1.23-5.62; SMR = 5.90, 95% CI 1.58-15.11]. Increased incidence was also observed for prostate cancer and all other cancers but neither were statistically significant. No increased risk was observed for lung cancer. Results of this study suggest that work at secondary aluminium smelters is associated with bladder cancer risk. Identification of occupational carcinogens in this industry is needed. © The Author 2016. Published by Oxford University Press on behalf of the Society of Occupational Medicine. All rights reserved. For Permissions, please email: journals.permissions@oup.com.

  7. Impact properties of aluminium - glass fiber reinforced plastics sandwich panels

    Directory of Open Access Journals (Sweden)

    Mathivanan Periasamy

    2012-06-01

    Full Text Available Aluminium - glass fiber reinforced plastics (GFRP sandwich panels are hybrid laminates consisting of GFRP bonded with thin aluminum sheets on either side. Such sandwich materials are increasingly used in airplane and automobile structures. Laminates with varying aluminium thickness fractions, fiber volume fractions and orientation in the layers of GFRP were fabricated by hand lay up method and evaluated for their impact performance by conducting drop weight tests under low velocity impacts. The impact energy required for initiating a crack in the outer aluminium layer as well as the energy required for perforation was recorded. The impact load-time history was also recorded to understand the failure behavior. The damage depth and the damage area were measured to evaluate the impact resistance. Optical photography and scanning electron micrographs were taken to visualize the crack and the damage zone. The bidirectional cross-ply hybrid laminate (CPHL has been found to exhibit better impact performance and damage resistance than the unidirectional hybrid laminate (UDHL. Increase in aluminium thickness fraction (Al tf and fiber volume fraction (Vf resulted in an increase in the impact energy required for cracking and perforation. On an overall basis, the sandwich panels exhibited better impact performance than the monolithic aluminium.

  8. AE Monitoring of Diamond Turned Rapidly Soldified Aluminium 443

    International Nuclear Information System (INIS)

    Onwuka, G; Abou-El-Hossein, K; Mkoko, Z

    2017-01-01

    The fast replacement of conventional aluminium with rapidly solidified aluminium alloys has become a noticeable trend in the current manufacturing industries involved in the production of optics and optical molding inserts. This is as a result of the improved performance and durability of rapidly solidified aluminium alloys when compared to conventional aluminium. Melt spinning process is vital for manufacturing rapidly solidified aluminium alloys like RSA 905, RSA 6061 and RSA 443 which are common in the industries today. RSA 443 is a newly developed alloy with few research findings and huge research potential. There is no available literature focused on monitoring the machining of RSA 443 alloys. In this research, Acoustic Emission sensing technique was applied to monitor the single point diamond turning of RSA 443 on an ultrahigh precision lathe machine. The machining process was carried out after careful selection of feed, speed and depths of cut. The monitoring process was achieved with a high sampling data acquisition system using different tools while concurrent measurement of the surface roughness and tool wear were initiated after covering a total feed distance of 13km. An increasing trend of raw AE spikes and peak to peak signal were observed with an increase in the surface roughness and tool wear values. Hence, acoustic emission sensing technique proves to be an effective monitoring method for the machining of RSA 443 alloy. (paper)

  9. Coherent beam-beam effects

    International Nuclear Information System (INIS)

    Chao, A.W.

    1992-01-01

    There are two physical pictures that describe the beam-beam interaction in a storage ring collider: The weak-strong and the strong-strong pictures. Both pictures play a role in determining the beam-beam behavior. This review addresses only the strong-strong picture. The corresponding beam dynamical effects are referred to as the coherent beam-beam effects. Some basic knowledge of the weak-strong picture is assumed. To be specific, two beams of opposite charges are considered. (orig.)

  10. Photodynamic effect of aluminium and zinc tetrasulfophthalocyanines on melanoma cancer cells

    CSIR Research Space (South Africa)

    Maduray, K

    2010-06-01

    Full Text Available Aluminium and zinc tetrasulfophthalocyanines were activated with a 672nm wavelength laser to investigate the photodynamic effects on melanoma cancer, dermal fibroblast and epidermal keratinocyte cells. Aluminium tetrasulfophthalocyanine was more...

  11. Study of ionic movements during anodic oxidation of nitrogen-implanted aluminium

    International Nuclear Information System (INIS)

    Terwagne, G.; Lucas, S.; Bodart, F.; Sorensen, G.; Jensen, H.

    1990-01-01

    In recent years there has been a considerable interest in synthesizing aluminium nitrides by ion implantation in order to modify the tribological properties of aluminium. The growth of an oxide layer by anodic process on these synthesized aluminium nitrides gives an interesting oxide-on-semiconductor material with surprising dynamic and decorative properties. During the anodic oxidation, ionic movements are involved in the near-surface region of the aluminium material; these ionic movements have been studied by Rutherford backscattering spectrometry (RBS) and nuclear reaction analysis (NRA) on thin aluminium foils (7000 A) preimplanted with nitrogen and post-oxidized in an ammonium pentaborate solution. The growth of the oxide layer is reduced when the aluminium is preimplanted with nitrogen: the speed of oxidation depends on the implantation conditions (energy and fluence). Moreover, the aluminium nitride can be dissolved when all metallic aluminium staying between the surface and the AlN are consumed by the anodic process. (orig.)

  12. 27 CFR 27.60 - Beer.

    Science.gov (United States)

    2010-04-01

    ... 27 Alcohol, Tobacco Products and Firearms 1 2010-04-01 2010-04-01 false Beer. 27.60 Section 27.60... TREASURY LIQUORS IMPORTATION OF DISTILLED SPIRITS, WINES, AND BEER General Requirements Marking and Labeling of Wines and Beer § 27.60 Beer. All imported beer is required to be released from customs custody...

  13. 27 CFR 27.42 - Wines.

    Science.gov (United States)

    2010-04-01

    ... TREASURY LIQUORS IMPORTATION OF DISTILLED SPIRITS, WINES, AND BEER Tax On Imported Distilled Spirits, Wines, and Beer Wines § 27.42 Wines. All wines (including imitation, substandard, or artificial wine, and... 27 Alcohol, Tobacco Products and Firearms 1 2010-04-01 2010-04-01 false Wines. 27.42 Section 27.42...

  14. 27 CFR 5.27 - Formulas.

    Science.gov (United States)

    2010-04-01

    ... 27 Alcohol, Tobacco Products and Firearms 1 2010-04-01 2010-04-01 false Formulas. 5.27 Section 5.27 Alcohol, Tobacco Products and Firearms ALCOHOL AND TOBACCO TAX AND TRADE BUREAU, DEPARTMENT OF THE TREASURY LIQUORS LABELING AND ADVERTISING OF DISTILLED SPIRITS Formulas § 5.27 Formulas. Formulas are...

  15. Development of picosecond pulsed electron beam monitor. 2

    International Nuclear Information System (INIS)

    Hosono, Y.; Nakazawa, M.; Ueda, T.

    1994-01-01

    A picosecond pulsed electron beam monitor for a 35 MeV linear accelerator has been developed. The monitor consists of an electric SMA connector and aluminium pipe(inner diameter of 50mm). The following characteristics of this monitor were obtained, (a) the rise time is less than 17.5 ps (b) linearity of the monitor output voltage is proportional to the peak current of beam. It is shown that this monitor can be successfully used for bunch measurements of picosecond pulsed electron beam of 35 MeV linac. (author)

  16. Measurements and FLUKA simulations of bismuth and aluminium activation at the CERN Shielding Benchmark Facility (CSBF)

    Science.gov (United States)

    Iliopoulou, E.; Bamidis, P.; Brugger, M.; Froeschl, R.; Infantino, A.; Kajimoto, T.; Nakao, N.; Roesler, S.; Sanami, T.; Siountas, A.

    2018-03-01

    The CERN High Energy AcceleRator Mixed field facility (CHARM) is located in the CERN Proton Synchrotron (PS) East Experimental Area. The facility receives a pulsed proton beam from the CERN PS with a beam momentum of 24 GeV/c with 5 ṡ1011 protons per pulse with a pulse length of 350 ms and with a maximum average beam intensity of 6.7 ṡ1010 p/s that then impacts on the CHARM target. The shielding of the CHARM facility also includes the CERN Shielding Benchmark Facility (CSBF) situated laterally above the target. This facility consists of 80 cm of cast iron and 360 cm of concrete with barite concrete in some places. Activation samples of bismuth and aluminium were placed in the CSBF and in the CHARM access corridor in July 2015. Monte Carlo simulations with the FLUKA code have been performed to estimate the specific production yields for these samples. The results estimated by FLUKA Monte Carlo simulations are compared to activation measurements of these samples. The comparison between FLUKA simulations and the measured values from γ-spectrometry gives an agreement better than a factor of 2.

  17. PEMBINAAN PENGERAJIN BOKOR ALUMINIUM DI DESA MENYALI

    Directory of Open Access Journals (Sweden)

    I NYOMAN GDE ANTARA, dkk.

    2014-04-01

    Full Text Available Alluminium bowl craft industrial center is located in Menyali village Sawan district Buleleng regency of Bali province. In this business development, they faced some problems such as increasingly expensive alluminium plate raw materials, decreasing selling product prices due to competition among craftsmen, difficulty in extending the marketing, lack of capital, lack of knowledge in business management, and lack of technical capacity and production innovation. Currently the organization has been formed aluminum bowl craftsmen groups, they are “Sumber Urip” and “Sumur Jaya”. This organization is still limited to tradisional associations such as a community organization, has not led to organize in a micro-enterprise or cooperation. Their organization management should not be arranged. Therefore, they need helps from the government and other institutions to build this bowl craftsmen in developing their businesses through a group of micro-enterprises or cooperations. Wishly, with formal business entity that would facilitate access to a variety of coaching and help governments andother institutions. From the SWOT analysis, it is found some problems and solutions that should be done. Alluminium bowl craftsmen groups, named “Sumber Urip” and “Sumur Jaya” is not in the form of business entity or cooperation yet, so that the results of coaching have agreed to form a cooperation. Venture capital assistance for the development and production are still needed and to be an absolute given, but a way to market more absolute yield is given, through participation in various events exhibition to introduce the product is expected to expandits market share up to overseas or exports. In the production process it has been introduced that is appropriate technology for instant a rolling tool to make a wiring groove on the outside of the bowl, so that it will simplify and speed up the process, especially by aged mothers.Keywords: aluminium bowl, Menyali

  18. Stimulation of eryptosis by aluminium ions

    International Nuclear Information System (INIS)

    Niemoeller, Olivier M.; Kiedaisch, Valentin; Dreischer, Peter; Wieder, Thomas; Lang, Florian

    2006-01-01

    Aluminium salts are utilized to impede intestinal phosphate absorption in chronic renal failure. Toxic side effects include anemia, which could result from impaired formation or accelerated clearance of circulating erythrocytes. Erythrocytes may be cleared secondary to suicidal erythrocyte death or eryptosis, which is characterized by cell shrinkage and exposure of phosphatidylserine (PS) at the erythrocyte surface. As macrophages are equipped with PS receptors, they bind, engulf and degrade PS-exposing cells. The present experiments have been performed to explore whether Al 3+ ions trigger eryptosis. The PS exposure was estimated from annexin binding and cell volume from forward scatter in FACS analysis. Exposure to Al 3+ ions (≥ 10 μM Al 3+ for 24 h) indeed significantly increased annexin binding, an effect paralleled by decrease of forward scatter at higher concentrations (≥ 30 μM Al 3+ ). According to Fluo3 fluorescence Al 3+ ions (≥ 30 μM for 3 h) increased cytosolic Ca 2+ activity. Al 3+ ions (≥ 10 μM for 24 h) further decreased cytosolic ATP concentrations. Energy depletion by removal of glucose similarly triggered annexin binding, an effect not further enhanced by Al 3+ ions. The eryptosis was paralleled by release of hemoglobin, pointing to loss of cell membrane integrity. In conclusion, Al 3+ ions decrease cytosolic ATP leading to activation of Ca 2+ -permeable cation channels, Ca 2+ entry, stimulation of cell membrane scrambling and cell shrinkage. Moreover, Al 3+ ions lead to loss of cellular hemoglobin, a feature of hemolysis. Both effects are expected to decrease the life span of circulating erythrocytes and presumably contribute to the development of anemia during Al 3+ intoxication

  19. Decomposition of pre calcined aluminium silicate ores of Afghanistan by hydrochloric acid

    International Nuclear Information System (INIS)

    Khomidi, A.K.; Mamatov, E.D.

    2015-01-01

    Present article is devoted to decomposition of pre calcined aluminium silicate ores of Afghanistan by hydrochloric acid. The physicochemical properties of initial aluminium silicate ores were studied by means of X-ray phase, differential thermal and silicate analysis. The chemical composition of aluminium containing ores was determined. The optimal conditions of interaction of initial and pre calcined siallites with hydrochloric acid were defined. The kinetics of acid decomposition of aluminium silicate ores was studied as well.

  20. SU-F-T-461: Dosimetric Evaluation of Indigenous Farmer Type Chamber FAR65- GB for Reference Dosimetry of FFF MV Photon Beam

    Energy Technology Data Exchange (ETDEWEB)

    Patwe, P; Mhatre, V; Dandekar, P [Sir HN RF Hospital, Mumbai, Maharashtra (India)

    2016-06-15

    Purpose: Indigenous Farmer type chamber FAR 65 GB is a reference class 0.6 cc ion chamber. It can be used for dosimetric evaluation of photon and high energy electron beams. We studied dosimetric characteristics of the chamber for 6MV and 10MV Flattening filter free FFF photon beams available on trueBEAM STx Linac. Methods: The study was carried out on trueBEAM STx Linac having 6 and 10 MV FFF photon beam with maximum dose rate 1400 and 2400 MU per min respectively. The dosimetric device to be evaluated is Rosalina Instruments FAR 65-GB Ion Chamber with active volume 0.65 cc, total active length 23.1cm, inner diameter of cylinder 6.2mm, wall thickness 0.4mm, inner electrode diameter 1mm. Inner and outer electrodes are made from Aluminium 2.7 gm per cc and graphite 1.82 gm per cc respectively. The ion chamber was placed along central axis of beam at 10cm depth and irradiated for 10cm × 10cm field size at SAD of 100 cm in plastic phantom. We studied Precision, Dose Linearity, Dose Rate dependence, directional dependence, Recombination effect. Recombination effect was determined using standard two-voltage method. Results: 1. Measurements were reproducible std deviation of 0.0105 and type A uncertainty 0.003265 under same set of reference conditions 2. Chamber exhibit dose linearity over a wider dose range. 3. Chamber shows dose rate independence for all available dose rate range. 4. Response of chamber with the angle of incidence of radiation is constant. 5. Recombination correction factors were 1.01848 and 1.02537 for dose rate 1400 and 2400 MU per min resp. Conclusion: Our study reveals that the chamber is prone to saturation effect at dose rate of 2400 MU per min. FAR 65-GB can be used for reference dosimetry of FFF MV photon beam with proper calculation of recombination effect.

  1. Sinter aluminium as cladding material for fuel elements; Aluminium fritte comme materiau de gainage pour les elements combustibles

    Energy Technology Data Exchange (ETDEWEB)

    Mann, K E; Boudouresques, M B [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires; Otto Fuchs, Meinerzhagen, Westfalen (Germany)

    1961-07-01

    1. Survey of the production process of sinter aluminium. 2. Description of the forming processes (extrusion, forging and rolling), whereby the production of tubing for atom piles will be explained in detail. 3. Production of ribbed tubes and tubes with close tolerances of sizes. 4. The different SAP-qualities and their properties under special consideration of the properties at elevated temperatures and the creep properties. 5. Diffusion behaviour of SAP with Be, Mg, Al, U and UO{sub 2}. 6. Corrosion behaviour in CO{sub 2} atmosphere at high temperature and in water. 7. Weldability. 8. Effect of irradiation on the mechanical properties. 9. Superiority of SAP compared with normal wrought alloys of the same composition. (author) [French] 1. Apercu des processus de production de l'aluminium fritte. 2. Expose des operations de transformation (filageries, forgeage et laminage), avec explication detaillee de la fabrication de gaine pour reacteurs. 3. Fabrication de tubes canneles et de tubes avec de faibles tolerances. 4. Diverses proprietes de l'aluminium fritte SAP, notamment proprietes aux temperatures elevees et proprietes de fluage. 5. Diffusion de l'aluminium fritte SAP en presence de Be, Mg, Al, U et UO{sub 2}. 6. Resistance a la corrosion dans une atmosphere de CO{sub 2} a temperature elevee et dans l'eau. 7. Possibilites de soudage. 8. Effet de l'irradiation sur les proprietes mecaniques. 9. Superiorite de l'aluminium fritte SAP sur les alliages forges normaux de meme composition. (auteur)

  2. Determination of ultratrace amounts of uranium and thorium in aluminium and aluminium alloys by electrothermal vaporization/ICP-MS

    International Nuclear Information System (INIS)

    Nakamura, Yasushi; Kobayashi, Yoshio; Kakurai, Yousuke

    1993-01-01

    A method has been developed for determining the 0.01 ng g -1 level of uranium and thorium in aluminium and aluminium alloys by electrothermal vaporization (ETV)/ICP-MS. This method was found to be significantly interfered with any matrices or other elements contained. An ion-exchange technique was therefore applied to separate uranium and thorium from aluminium and other elements. It was known that uranium are adsorbed on an anion-exchange resin and thorium are adsorbed on cation-exchange resin. However, aluminium and copper were eluted with 6 M hydrochloric acid. Dissolve the sample with hydrochloric acid containing copper which was added for analysis of pure aluminium, and oxidize with hydrogen peroxide. Concentration of hydrochloric acid in the solution was adjusted to 6 M, and then passed the solution through the mixed ion-exchange resin column. After the uranium and thorium were eluted with 1 M hydrofluoric acid-0.1 M hydrochloric acid, the solution was evaporated to dryness. It was then dissolved with 1 M hydrochloric acid. Uranium and thorium were analyzed by ETV/ICP-MS using tungsten and molybdenum boats, respectively, since the tungsten boat contained high-level thorium and the molybdenum boat contained uranium. The determination limit of uranium and thorium were 0.003 and 0.005 ng g -1 , respectively. (author)

  3. Determination of aluminium in groundwater samples by GF-AAS, ICP-AES, ICP-MS and modelling of inorganic aluminium complexes.

    Science.gov (United States)

    Frankowski, Marcin; Zioła-Frankowska, Anetta; Kurzyca, Iwona; Novotný, Karel; Vaculovič, Tomas; Kanický, Viktor; Siepak, Marcin; Siepak, Jerzy

    2011-11-01

    The paper presents the results of aluminium determinations in ground water samples of the Miocene aquifer from the area of the city of Poznań (Poland). The determined aluminium content amounted from aluminium determinations were performed using three analytical techniques: graphite furnace atomic absorption spectrometry (GF-AAS), inductively coupled plasma atomic emission spectrometry (ICP-AES) and inductively coupled plasma mass spectrometry (ICP-MS). The results of aluminium determinations in groundwater samples for particular analytical techniques were compared. The results were used to identify the ascent of ground water from the Mesozoic aquifer to the Miocene aquifer in the area of the fault graben. Using the Mineql+ program, the modelling of the occurrence of aluminium and the following aluminium complexes: hydroxy, with fluorides and sulphates was performed. The paper presents the results of aluminium determinations in ground water using different analytical techniques as well as the chemical modelling in the Mineql+ program, which was performed for the first time and which enabled the identification of aluminium complexes in the investigated samples. The study confirms the occurrence of aluminium hydroxy complexes and aluminium fluoride complexes in the analysed groundwater samples. Despite the dominance of sulphates and organic matter in the sample, major participation of the complexes with these ligands was not stated based on the modelling.

  4. Tailored Aluminium based Coatings for Optical Appearance and Corrosion Resistance

    DEFF Research Database (Denmark)

    Aggerbeck, Martin

    potential differences in the microstructure, and protection from the network of the Al3Ti phases precipitated during the heat treatment. Laser surface cladding of aluminium containing up to 20 wt. % Ti6Al4V were studied focusing on the microstructure and the alkaline corrosion properties. Due......The current project investigated the possibility of designing aluminium based coatings focusing on the effect of composition and surface finish on the optical appearance and on the alkaline corrosion properties using titanium as the main alloying element. The main results and discussions...... that the roughness after etching increases with higher amounts of alloying elements (especially iron and silicon). Proper polishing requires some alloy hardness, while alloy purity is required for a glossy appearance after anodisation. Magnetron sputtered aluminium based coatings containing up to 18 wt. % titanium...

  5. Comparative performance of aluminium copper and iron solar stills

    International Nuclear Information System (INIS)

    Dioha, I.J.; Nwagbo, E.E.; Gulma, N.A.

    1990-12-01

    Three different metal sheets have been used in the fabrication of three different single sloping solar stills of the same surface geometry. The metals were galvanized iron, aluminium and copper. This paper presents the performance of the different stills operating under the same environmental conditions. The observed distillate yields was greatest for copper, then aluminium and lastly, iron still. The differences in the yields is attributed to the differences in the thermal conductivities of the metals. The equivalent local costs for the fabrication of the copper, aluminium and iron stills are respectively $160, $95 and $60. Taking the long run costs into consideration, the copper still is preferred because of its availability, durability, weldability and relatively higher conductivity of 380Wm -1 K -1 value. (author). 9 refs, 2 figs, 2 tabs

  6. Application of Anodization Process for Cast Aluminium Surface Properties Enhancement

    Directory of Open Access Journals (Sweden)

    Włodarczyk-Fligier A.

    2016-09-01

    Full Text Available An huge interest is observed in last years in metal matrix composite, mostly light metal based, which have found their applications in many industry branches, among others in the aircraft industry, automotive-, and armaments ones, as well as in electrical engineering and electronics, where one of the most important issue is related to the corrosion resistance, especially on the surface layer of the used aluminium alloys. This elaboration presents the influence of ceramic phase on the corrosion resistance, quality of the surface layer its thickness and structure of an anodic layer formed on aluminium alloys. As test materials it was applied the aluminium alloys Al-Si-Cu and Al-Cu-Mg, for which heat treatment processes and corrosion tests were carried out. It was presented herein grindability test results and metallographic examination, as well. Hardness of the treated alloys with those ones subjected to corrosion process were compared.

  7. Effect of microcrystallization on pitting corrosion of pure aluminium

    International Nuclear Information System (INIS)

    Meng Guozhe; Wei Liyan; Zhang Tao; Shao Yawei; Wang Fuhui; Dong Chaofang; Li Xiaogang

    2009-01-01

    A microcrystalline aluminium film with grain size of about 400 nm was prepared by magnetron sputtering technique. Its corrosion behaviour was investigated in NaCl containing acidic solution by means of potentiodynamic polarization curves and electrochemical noise (EN). The polarization results indicated that the corrosion potential of the sample shifted towards more positive direction, while its corrosion current density decreased compared with that of pure coarse-grain Al. The EN analysis based on stochastic model demonstrated that there existed two kinds of effect of microcrystallization on the pitting behaviour of pure aluminium: (1) the rate of pit initiation is accelerated, (2) the pit growth process was impeded. This leads to the enhancement of pitting resistance for the microcrystallized aluminium.

  8. Modelling of micro- and macrosegregation for industrial multicomponent aluminium alloys

    International Nuclear Information System (INIS)

    Ellingsen, K; M'Hamdi, M; Mortensen, D

    2015-01-01

    Realistic predictions of macrosegregation formation during casting of aluminium alloys requires an accurate modeling of solute microsegregation accounting for multicomponent phase diagrams and secondary phase formation. In the present work, the stand alone Alstruc model, a microsegregation model for industrial multicomponent aluminium alloys, is coupled with the continuum model ALSIM which calculates the macroscopic transport of mass, enthalpy, momentum, and solutes as well as stresses and deformation during solidification of aluminium. Alstruc deals with multicomponent alloys accounting for temperature dependent partition coefficients, liquidus slopes and the precipitation of secondary phases. The challenge associated with computation of microsegregation for multicomponent alloys is solved in Alstruc by approximating the phase diagram data by simple, analytical expressions which allows for a CPU-time efficient coupling with the macroscopic transport model. In the present work, the coupled model has been applied in a study of macrosegregation including thermal and solutal convection, solidification shrinkage and surface exudation on an industrial DC-cast billet. (paper)

  9. Different Approach to the Aluminium Oxide Topography Characterisation

    International Nuclear Information System (INIS)

    Poljacek, Sanja Mahovic; Gojo, Miroslav; Raos, Pero; Stoic, Antun

    2007-01-01

    Different surface topographic techniques are being widely used for quantitative measurements of typical industrial aluminium oxide surfaces. In this research, specific surface of aluminium oxide layer on the offset printing plate has been investigated by using measuring methods which have previously not been used for characterisation of such surfaces. By using two contact instruments and non-contact laser profilometer (LPM) 2D and 3D roughness parameters have been defined. SEM micrographs of the samples were made. Results have shown that aluminium oxide surfaces with the same average roughness value (Ra) and mean roughness depth (Rz) typically used in the printing plate surface characterisation, have dramatically different surface topographies. According to the type of instrument specific roughness parameters should be used for defining the printing plate surfaces. New surface roughness parameters were defined in order to insure detailed characterisation of the printing plates in graphic reproduction process

  10. Quantitative electron probe microanalysis of borides in aluminium

    International Nuclear Information System (INIS)

    Karduck, P.; Schuerhoff, H.J.; Burchard, W.G.

    1983-01-01

    A procedure for the quantitative analysis of borides in aluminium was introduced. For this purpose the optimal apparative boundary conditions for the EPMA of boron were worked out. With these conditions a satisfactory peak to background ratio of 57 could be achieved for B-Kα-radiation. By application of this method the following conclusion should be drawn concerning the kind of nuclei during grain refinement of aluminium with titanium and boron: For grain refinement of aluminium with titanium and boron in the hypoperitectic region of the binary system Al-Ti TiB 2 -particles in clusters provide the high efficiency of refinement. This entails that the TiB 2 -particles already present in the master alloy remain inert in the melt. Hence, the good efficiency of refinement in this region cannot be attributed to the presence of particles like Al 3 Ti, AlB 2 or (Al, Ti) B 2 . (Author)

  11. Thermodynamic properties of uranium in gallium–aluminium based alloys

    International Nuclear Information System (INIS)

    Volkovich, V.A.; Maltsev, D.S.; Yamshchikov, L.F.; Chukin, A.V.; Smolenski, V.V.; Novoselova, A.V.; Osipenko, A.G.

    2015-01-01

    Activity, activity coefficients and solubility of uranium was determined in gallium-aluminium alloys containing 1.6 (eutectic), 5 and 20 wt.% aluminium. Additionally, activity of uranium was determined in aluminium and Ga–Al alloys containing 0.014–20 wt.% Al. Experiments were performed up to 1073 K. Intermetallic compounds formed in the alloys were characterized by X-ray diffraction. Partial and excess thermodynamic functions of U in the studied alloys were calculated. - Highlights: • Thermodynamics of uranium is determined in Ga–Al alloys of various compositions. • Uranium in the mixed alloys interacts with both components, Ga and Al. • Interaction of U with Al increases with decreasing temperature. • Activity and solubility of uranium depend on Al content in Ga–Al alloys.

  12. Thermodynamic properties of uranium in gallium–aluminium based alloys

    Energy Technology Data Exchange (ETDEWEB)

    Volkovich, V.A., E-mail: v.a.volkovich@urfu.ru [Department of Rare Metals and Nanomaterials, Institute of Physics and Technology, Ural Federal University, Ekaterinburg, 620002 (Russian Federation); Maltsev, D.S.; Yamshchikov, L.F. [Department of Rare Metals and Nanomaterials, Institute of Physics and Technology, Ural Federal University, Ekaterinburg, 620002 (Russian Federation); Chukin, A.V. [Department of Theoretical Physics and Applied Mathematics, Institute of Physics and Technology, Ural Federal University, Ekaterinburg, 620002 (Russian Federation); Smolenski, V.V.; Novoselova, A.V. [Institute of High-Temperature Electrochemistry UD RAS, Ekaterinburg, 620137 (Russian Federation); Osipenko, A.G. [JSC “State Scientific Centre - Research Institute of Atomic Reactors”, Dimitrovgrad, 433510 (Russian Federation)

    2015-10-15

    Activity, activity coefficients and solubility of uranium was determined in gallium-aluminium alloys containing 1.6 (eutectic), 5 and 20 wt.% aluminium. Additionally, activity of uranium was determined in aluminium and Ga–Al alloys containing 0.014–20 wt.% Al. Experiments were performed up to 1073 K. Intermetallic compounds formed in the alloys were characterized by X-ray diffraction. Partial and excess thermodynamic functions of U in the studied alloys were calculated. - Highlights: • Thermodynamics of uranium is determined in Ga–Al alloys of various compositions. • Uranium in the mixed alloys interacts with both components, Ga and Al. • Interaction of U with Al increases with decreasing temperature. • Activity and solubility of uranium depend on Al content in Ga–Al alloys.

  13. Aluminium supplier selection for the automotive parts manufacturer

    Directory of Open Access Journals (Sweden)

    M. Cieśla

    2016-04-01

    Full Text Available This paper presents a methodology for selection of the optimal sources of supply, which is also known as the problem of supplier selection. Theoretical considerations are expanded with research related to aluminium supplier selection for a hypothetical manufacturer of aluminium parts for transportation equipment located in Poland. Evaluation of five suppliers of aluminium from Poland, Germany and Slovenia has been conducted using a weighted scoring method, a strengths and weaknesses method and a graphical method. Choosing the best offer and prioritizing suppliers allows not only the most rational decision in the field of supply logistics to be taken but also the quality of service in the metallurgical industry to be improved.

  14. Production of Inorganic Thin Scintillating Films for Ion Beam Monitoring Devices

    CERN Document Server

    Re, Maurizio; Cosentino, Luigi; Cuttone, Giacomo; Finocchiaro, Paolo; Hermanne, Alex; Lojacono, Pietro A; Ma, YingJun; Thienpont, Hugo; Van Erps, Jurgen; Vervaeke, Michael; Volckaerts, Bart; Vynck, Pedro

    2005-01-01

    In this work we present the development of beam monitoring devices consisting of thin CsI(Tl) films deposited on Aluminium support layers. The light emitted by the scintillating layer during the beam irradiation is measured by a CCD-camera. In a first prototype a thin Aluminium support layer of 6 micron allows the ion beam to easily pass through without significant energy loss and scattering effects. Therefore it turns out to be a non-destructive monitoring device to characterize on-line beam shape and beam position without interfering with the rest of the irradiation process. A second device consists of an Aluminium support layer which is thick enough to completely stop the impinging ions allowing to monitor at the same time the beam profile and the beam current intensity. Some samples have been coated by a 100 Å protective layer to prevent the film damage by atmosphere exposition. In this contribution we present our experimental results obtained by irradiating the samples with proton beams at 8.3 and 62 Me...

  15. Light-weight aluminium bridges and bridge decks. An overview of recent applications

    NARCIS (Netherlands)

    Maljaars, J.; Soetens, F.; Kluyver, D. de

    2008-01-01

    The last decades have shown a large increase in the application of aluminium alloys for light-weight bridges. For bridge construction, aluminium alloys have some specific advantages, but also some points of attention. This paper deals with some recent projects of aluminium bridges, and for these

  16. Structural perturbation of diphtheria toxoid upon adsorption to aluminium hydroxide adjuvant

    NARCIS (Netherlands)

    Regnier, M.; Metz, B.; Tilstra, W.; Hendriksen, C.; Jiskoot, W.; Norde, W.; Kersten, G.

    2012-01-01

    Aluminium-containing adjuvants are often used to enhance the potency of vaccines. In the present work we studied whether adsorption of diphtheria toxoid to colloidal aluminium hydroxide induces conformational changes of the antigen. Diphtheria toxoid has a high affinity for the aluminium hydroxide

  17. Pemanfaatan serat silicon carbon dan partikel alumina pada matrik aluminium untuk meningkatkan sifat mekanis material komposit

    Directory of Open Access Journals (Sweden)

    Ketut Suarsana

    2017-03-01

    Full Text Available Abstrak: Pemanfaatan penguat material komposit berbasis serat dan juga partikel pada pembuatan bahan komposit sekarang ini sangatpotensial untuk dikembangkan dan diteliti. Beragam sumber serat dan juga penguat dalam bentuk partikel bisa didapat dari seratalami dari tumbuh-tubuhan dan juga serat yang sudah dikenakan perlakuan sebelumnya. Indonesia memiliki potensi sumberalam yang sangat potensial terutama sebgai sumber serat dari tumbuhan juga berupa logam aluminium (bauxite dari fosil.Bahan ini dapat dimanfaatkan untuk kebutuhan masyarakat industri sebagai bahan dasar pembuatan komposit bermatrikAluminium dan sebagai penguat berupa serat maupun partikel alumina. Metode pembuatan Aluminum Matrix Composite (AMCdengan proses metalurgi serbuk pada gaya tekan/kompaksi 2,5 ton mengunakan alat press hydrolik, waktu penahanan 15menit, serta proses perlakuan pada variasi komposisi berat (%wt. Variasi komposisi penguat serat Silicon Carbon (SiC danAl2O3 (alumina pada matrik Aluminium adalah : 30% SiC + 0% Al203, 27% SiC + 3% Al203, 24% SiC + 6% Al203 dan 21% SiC+ 9% Al203 dengan matrik 70% Al, pada kondisi tempertaur 500oC, 550oC dan 600oC. Setelah material komposit terbentuk, diujiuntuk mengetahui sifat mekanik akibat pengaruh variasi komposisi antara matrik dan penguatan pada komposit. Uji karakteristikdilakukan di laboratorium untuk menggetahui sifat kekuatan dan kekerasan material komposit. Selanjutnya dicari hubunganantara sifat masing-masing komposisi penguat serat SiC dan Al2O3 pembentuk komposit yang dibuat untuk mengetahui manfaatdari penguat serat dan partikel alumina.Kata Kunci: Sifat kekuatan, kekerasan, serat SiC dan Al2O3 Abstract: Utilization reinforcement fiber-based composite material and particles in the manufacture of composite materials now havepotential to be developed and researched. Various sources of fiber and reinforcement in particle form can be obtained fromnatural fibers from plants and fiber that has been subjected to a

  18. Analytical methodologies for aluminium speciation in environmental and biological samples--a review.

    Science.gov (United States)

    Bi, S P; Yang, X D; Zhang, F P; Wang, X L; Zou, G W

    2001-08-01

    It is recognized that aluminium (Al) is a potential environmental hazard. Acidic deposition has been linked to increased Al concentrations in natural waters. Elevated levels of Al might have serious consequences for biological communities. Of particular interest is the speciation of Al in aquatic environments, because Al toxicity depends on its forms and concentrations. In this paper, advances in analytical methodologies for Al speciation in environmental and biological samples during the past five years are reviewed. Concerns about the specific problems of Al speciation and highlights of some important methods are elucidated in sections devoted to hybrid techniques (HPLC or FPLC coupled with ET-AAS, ICP-AES, or ICP-MS), flow-injection analysis (FIA), nuclear magnetic resonance (27Al NMR), electrochemical analysis, and computer simulation. More than 130 references are cited.

  19. Simultaneous determination of aluminium and phosphorus by neutron activation analysis

    International Nuclear Information System (INIS)

    Gatschke, W.; Gawlik, D.

    1980-01-01

    With the use of the pneumatic tube system of the BER II reactor, the irradiation position of which is equipped with a movable cadmium shield, the aluminium and phosphorus levels in bone powder and in human bone biopsies were determined. The contribution of aluminium and phosphorus to the 28 Al activity could be separated mathematically after the samples had been irradiated with and without cadmium shielding. The sensitivity and limit of quantitative determination of the analytical procedure were determined using the addition method and the fact that the levels of each element measured was independent of the amount of the other element was proved. (author)

  20. Electrochemical noise from corroding carbon steel and aluminium

    International Nuclear Information System (INIS)

    Singh, P.R.; Gaonkar, K.B.; De, P.K.; Banerjee, S.

    1997-05-01

    Electrochemical noise measurements were conducted on carbon steel and aluminium in sodium chloride solutions. Noise parameters like standard deviation of potential and current, noise resistance, pitting index, noise power were studied for the purpose of measuring corrosion rate. These parameters compared well with the corrosion rate. Pitting index was not very reliable. Current noise was more close to the corrosion rates. General corrosion gave rise to white noise type of power spectrum while flicker noise type of spectrum was obtained from pitting attack. Sodium nitrite is shown to inhibit the corrosion of carbon steel. Aluminium corrodes in the early period of exposure and passivates during long exposure

  1. Spectrofluorimetric determination of microquantities of aluminium in uranium

    International Nuclear Information System (INIS)

    Gomiero, L.A.; Nascimento, M.R.L. do; Abraao, A.

    1976-01-01

    A rapid and sensitive method for the separation and spectrofluorimetric determination of microamounts of aluminium in uranium compounds is described. In sodium carbonate solution at pH 9.5-10.0, the uranyl ion forms a very stable anionic complex with the carbonate ion. In these conditions, uranium is not extracted by a chloroform oxine solution, while alumium is isolated as the tris(oxinate)aluminium(III) form. The interferences are previously extracted with chloroform as diethylditiocarbomates in the same tris(oxinate)aluminum(III) pH extraction. The sensitivity is 0,005 μ Al/ml of organic phase and the relative standard deviation is 10% [pt

  2. Determination of cadmium in aluminium by atomic absorption spectrometry

    International Nuclear Information System (INIS)

    Batistoni, D.A.; Erlijman, L.H.

    1978-12-01

    A direct method for the determination of cadmium in elemental aluminium is described. Metal samples are dissolved in diluted hydrochloric acid and cadmium is determined by atomic absorption spectrometry in an air-acetylene flame. Interference by non-specific absorption observed at the analytical wavelength incorrected for by means of a non-absorbing line emitted by the hollow-cathode lamp. Relatively large amounts of arsenic do not interfere. The minimun determinable concentration of cadmium for this procedure is 2-3 ppm, expressed on aluminium basis. (author) [es

  3. Materials and ceramics on the base of aluminium titanate

    International Nuclear Information System (INIS)

    Gulamova, D.

    1997-01-01

    The influence of the doping and technological parameters on the thermodynamical stability of the aluminium titanate is investigated. The condition necessary to make aluminium titanate stable and established. it is shown, how the condition of the synthesis and the content of the admixture phases affect the stability of the solid solutions. The technology of obtaining the ceramics stable with respect to decay (with thermal expansion coefficient CTE = 26x10/sup -6/ grad/sup -1/ and thermoresistancy > 80 heating cycles, sigma curve equal or greater than 80 Mpa) is worked out. (author)

  4. Prevention of Dealloying in Manganese Aluminium Bronze Propeller: Part II

    Directory of Open Access Journals (Sweden)

    Napachat Tareelap

    2014-03-01

    Full Text Available Due to the failure of manganese aluminium bronze (MAB propeller caused by dealloying corrosion as described in Part I [1], this work aims to study the prevention of dealloying corrosion using aluminium and zinc sacrificial anodes. The results indicated that both of the sacrificial anodes could prevent the propeller from dealloying. Moreover, the dealloying in seawater was less than that found in brackish water. It was possible that hydroxide ions, from cathodic reaction, reacted with calcium in seawater to form calcium carbonate film protecting the propeller from corrosion.

  5. Towards an understanding of the adjuvant action of aluminium

    Science.gov (United States)

    Marrack, Philippa; McKee, Amy S.; Munks, Michael W.

    2011-01-01

    The efficacy of vaccines depends on the presence of an adjuvant in conjunction with the antigen. Of these adjuvants, the ones that contain aluminium, which were first discovered empirically in 1926, are currently the most widely used. However, a detailed understanding of their mechanism of action has only started to be revealed. In this Timeline article, we briefly describe the initial discovery of aluminium adjuvants and discuss historically important advances. We also summarize recent progress in the field and discuss their implications and the remaining questions on how these adjuvants work. PMID:19247370

  6. Silver coated aluminium microrods as highly colloidal stable SERS platforms.

    Science.gov (United States)

    Pazos-Perez, Nicolas; Borke, Tina; Andreeva, Daria V; Alvarez-Puebla, Ramon A

    2011-08-01

    We report on the fabrication of a novel material with the ability to remain in solution even under the very demanding conditions required for structural and dynamic characterization of biomacromolecule assays. This stability is provided by the increase in surface area of a low density material (aluminium) natively coated with a very hydrophilic surface composed of aluminium oxide (Al(2)O(3)) and metallic silver nanoparticles. Additionally, due to the dense collection of active hot spots on their surface, this material offers higher levels of SERS intensity as compared with the same free and aggregated silver nanoparticles. This journal is © The Royal Society of Chemistry 2011

  7. High-purity aluminium creep under high hydrostatic pressure

    International Nuclear Information System (INIS)

    Zajtsev, V.I.; Lyafer, E.I.; Tokij, V.V.

    1977-01-01

    The effect of the hydrostatic pressure on the rate of steady-state creep of high-purity aluminium was investigated. It is shown that the hydrostatic pressure inhibits the creep. The activation volume of the creep is independent of the direction in the range of (4.7-6.2) kg/mm 2 and of the pressure in the range of (1-7.8000) atm. It is concluded that self-diffusion does not control the creep of high-purity aluminium at room temperature in the investigated stress and pressure range

  8. Bioactive type glass-ceramics within incorporated aluminium

    International Nuclear Information System (INIS)

    Volzone, C.; Stabile, F.M.; Ortiga, J.

    2012-01-01

    Bioactive glass-ceramics are used as biomaterials for the reparation of bone tissue. They are prepared, generally, by bioglass of specific composition for each particular use. The aluminium addition in the formulation at very small quantities influences on the structural properties. Two glass-ceramics obtained by P 2 O 5 -Na 2 O-CaO-SiO 2 formulation within aluminium (0.5 % in Al 2 O 3 base) added through a reactive alumina and purified feldspar were analyzed. The results showed structural differences between both glass-ceramics. (author)

  9. Do oral aluminium phosphate binders cause accumulation of aluminium to toxic levels?

    Directory of Open Access Journals (Sweden)

    Roberts Norman B

    2011-10-01

    Full Text Available Abstract Background Aluminium (Al toxicity was frequent in the 1980s in patients ingesting Al containing phosphate binders (Alucaps whilst having HD using water potentially contaminated with Al. The aim of this study was to determine the risk of Al toxicity in HD patients receiving Alucaps but never exposed to contaminated dialysate water. Methods HD patients only treated with Reverse Osmosis(RO treated dialysis water with either current or past exposure to Alucaps were given standardised DFO tests. Post-DFO serum Al level > 3.0 μmol/L was defined to indicate toxic loads based on previous bone biopsy studies. Results 39 patients (34 anuric were studied. Mean dose of Alucap was 3.5 capsules/d over 23.0 months. Pre-DFO Al levels were > 1.0 μmol/L in only 2 patients and none were > 3.0 μmol/L. No patients had a post DFO Al levels > 3.0 μmol/L. There were no correlations between the serum Al concentrations (pre-, post- or the incremental rise after DFO administration and the total amount of Al ingested. No patients had unexplained EPO resistance or biochemical evidence of adynamic bone. Conclusions Although this is a small study, oral aluminium exposure was considerable. Yet no patients undergoing HD with RO treated water had evidence of Al toxicity despite doses equivalent to 3.5 capsules of Alucap for 2 years. The relationship between the DFO-Al results and the total amount of Al ingested was weak (R2 = 0.07 and not statistically significant. In an era of financial prudence, and in view of the recognised risk of excess calcium loading in dialysis patients, perhaps we should re-evaluate the risk of using Al-based phosphate binders in HD patients who remain uric.

  10. Accumulation of Aluminium and Physiological Status of Tree Foliage in the Vicinity of a Large Aluminium Smelter

    Directory of Open Access Journals (Sweden)

    E. D. Wannaz

    2012-01-01

    Full Text Available A pollution gradient was observed in tree foliage sampled in the vicinity of a large aluminium production facility in Patagonia (Argentina. Leaves of Eucalyptus rostrata, and Populus hybridus and different needle ages of Pinus spec. were collected and concentrations of aluminium (Al and sulphur (S as well as physiological parameters (chlorophyll and lipid oxidation products were analyzed. Al and S concentrations indicate a steep pollution gradient in the study showing a relationship with the physiological parameters in particular membrane lipid oxidation products. The present study confirms that aluminium smelting results in high Al and sulphur deposition in the study area, and therefore further studies should be carried out taking into account potentially adverse effects of these compounds on human and ecosystem health.

  11. Corrosion of research reactor aluminium clad spent fuel in water

    International Nuclear Information System (INIS)

    2003-01-01

    This report describes research performed in ten laboratories within the framework of the IAEA Co-ordinated Research Project on Corrosion of Research Reactor Aluminium Clad Spent Fuel in Water. The project consisted of exposure of standard racks of corrosion coupons in the spent fuel pools of the participating research reactor laboratories and the evaluation of the coupons after predetermined exposure times, along with periodic monitoring of the storage water. A group of experts in the field contributed a state of the art review and provided technical supervision of the project. Localized corrosion mechanisms are notoriously difficult to understand, and it was clear from the outset that obtaining consistency in the results and their interpretation from laboratory to laboratory would depend on the development of an excellent set of experimental protocols. These experimental protocols are described in the report together with guidelines for the maintenance of optimum water chemistry to minimize the corrosion of aluminium clad research reactor fuel in wet storage. A large database on corrosion of aluminium clad materials has been generated from the CRP and the SRS corrosion surveillance programme. An evaluation of these data indicates that the most important factors contributing to the corrosion of the aluminium are: (1) High water conductivity (100-200 μS/cm); (2) Aggressive impurity ion concentrations (Cl - ); (3) Deposition of cathodic particles on aluminium (Fe, etc.); (4) Sludge (containing Fe, Cl - and other ions in concentrations greater than ten times the concentrations in the water); (5) Galvanic couples between dissimilar metals (stainless steel-aluminium, aluminium-uranium, etc); (6) Scratches and imperfections (in protective oxide coating on cladding); (7) Poor water circulation. These factors operating both independently and synergistically may cause corrosion of the aluminium. The single most important key to preventing corrosion is maintaining good

  12. Experimental weathering rates of aluminium silicates

    International Nuclear Information System (INIS)

    Gudbrandsson, Snorri

    2013-01-01

    The chemical weathering of primary rocks and minerals in natural systems has a major impact on soil development and its composition. Chemical weathering is driven to a large extent by mineral dissolution. Through mineral dissolution, elements are released into groundwater and can readily react to precipitate secondary minerals such as clays, zeolites, and carbonates. Carbonates form from divalent cations (e.g. Ca, Fe and Mg) and CO 2 , and kaolin clay and gibbsite formation is attributed to the weathering of aluminium-rich minerals, most notably the feldspars. The CarbFix Project in Hellisheidi (SW-Iceland) aims to use natural weathering processes to form carbonate minerals by the re-injection of CO 2 from a geothermal power plant back into surrounding basaltic rocks. This process is driven by the dissolution of basaltic rocks, rich in divalent cations, which can combine with injected CO 2 to form and precipitate carbonates. This thesis focuses on the dissolution behaviour of Stapafell crystalline basalt, which consists of three major phases (plagioclase, pyroxene, and olivine) and is rich in divalent cations. Steady-state element release rates from crystalline basalt at far-from-equilibrium conditions were measured at pH from 2 to 11 and temperatures from 5 to 75 C in mixed-flow reactors. Steady-state Si and Ca release rates exhibit a U-shaped variation with pH, where rates decrease with increasing pH at acid condition but increase with increasing pH at alkaline conditions. Silicon release rates from crystalline basalt are comparable to Si release rates from basaltic glass of the same chemical composition at low pH and temperatures ≥25 C but slower at alkaline pH and temperatures ≥50 C. In contrast, Mg and Fe release rates decrease continuously with increasing pH at all temperatures. This behaviour is interpreted to stem from the contrasting dissolution behaviours of the three major minerals comprising the basalt: plagioclase, pyroxene, and olivine. Element

  13. 27 CFR 27.40 - Distilled spirits.

    Science.gov (United States)

    2010-04-01

    ... OF THE TREASURY LIQUORS IMPORTATION OF DISTILLED SPIRITS, WINES, AND BEER Tax On Imported Distilled Spirits, Wines, and Beer Distilled Spirits § 27.40 Distilled spirits. (a) A tax is imposed on all... 27 Alcohol, Tobacco Products and Firearms 1 2010-04-01 2010-04-01 false Distilled spirits. 27.40...

  14. 27 CFR 27.121 - Containers.

    Science.gov (United States)

    2010-04-01

    ... 27 Alcohol, Tobacco Products and Firearms 1 2010-04-01 2010-04-01 false Containers. 27.121 Section... Spirits In Bulk § 27.121 Containers. Imported distilled spirits may be bottled in either domestic or imported containers conforming to the provisions of subpart N of this part. (72 Stat. 1374; 26 U.S.C. 5301...

  15. 27 CFR 27.185 - Customs release.

    Science.gov (United States)

    2010-04-01

    ... 27 Alcohol, Tobacco Products and Firearms 1 2010-04-01 2010-04-01 false Customs release. 27.185... Distilled Spirits From Customs Custody Free of Tax for Use of the United States § 27.185 Customs release. (a) Upon receipt of appropriate customs entry and a photocopy of a permit, Form 5150.33 or previous...

  16. 27 CFR 4.27 - Vintage wine.

    Science.gov (United States)

    2010-04-01

    ... 27 Alcohol, Tobacco Products and Firearms 1 2010-04-01 2010-04-01 false Vintage wine. 4.27 Section... THE TREASURY LIQUORS LABELING AND ADVERTISING OF WINE Standards of Identity for Wine § 4.27 Vintage wine. (a) General. Vintage wine is wine labeled with the year of harvest of the grapes and made in...

  17. Deformation twinning in zinc-aluminium single crystals after slip

    International Nuclear Information System (INIS)

    Lukac, P.; Kral, F.; Trojanova, Z.; Kral, R.

    1993-01-01

    Deformation twinning in Zn-Al single crystals deformed by slip in the basal system is examined. The influence of temperature and the content of aluminium in zinc on the twinning stress is investigated in the temperature range from 198 to 373 K. It is shown that the twinning stress rises with increasing temperature and increases with the concentration of Al atoms. (orig.)

  18. Ultraviolet sensing properties of polyvinyl alcohol-coated aluminium ...

    Indian Academy of Sciences (India)

    Undoped and aluminium (Al)-doped zinc oxide (ZnO) nanorods have been synthesized by electrochemical route. The synthesized materials have been characterized by X-ray diffraction, UV–visible spectrometer and scanning electron microscope. The Al-doped ZnO nanorods have been coated with polyvinyl alcohol.

  19. Oxygen–induced barrier height changes in aluminium – amorphous ...

    African Journals Online (AJOL)

    The results show that the application of voltage causes charge exchange between the surface states and the semiconductor leading to a change in the height of the potential barrier for electrons passing from aluminium into the a-Se films. The empirically determined values of barrier height of Al/a-Se diodes with thin and ...

  20. Microstructure and defect chemistry of yttrium aluminium garnet ceramics

    International Nuclear Information System (INIS)

    Schuh, L.H.

    1989-01-01

    This thesis describes basic aspects concerning the defect chemistry and the microstructure of yttrium aluminium garnet ceramics. The work consists of three parts: a literature study, an experimental part and a section giving computer simulation data of defects. (author). 320 refs.; 68 figs.; 72 schemes; 32 tabs

  1. Optimization of aluminium stressed skin panels in offshore applications

    NARCIS (Netherlands)

    Hove, van B.W.E.M.; Soetens, F.; Songmene, V.

    2013-01-01

    Since the introduction of Eurocode 9 specific design rules for the calculation of aluminium stressed skin panels are available. These design rules have been used for optimization of two extrusions: one for explosions and wind loading governing and one for explosions and floor loading governing. The

  2. Pressurized air ionization chamber with aluminium walls for radiometric dosimetry

    International Nuclear Information System (INIS)

    Rodrigues, R.G.S.; Pela, C.A.; Netto, T.G.

    1996-01-01

    A pressurized air ionization chamber with 23 cm 3 and aluminium walls is evaluated concerning its sensitiveness in low exposure rate. Considering conventional ionization chambers, this chamber shows a better performance since the air pressure of 2500 kPa minimizes the energy dependence to less than 5% between 40 and 1.250 keV

  3. Differential effects of aluminium on the seedling parameters of wheat ...

    African Journals Online (AJOL)

    Differential effects of aluminium on the seedling parameters of wheat. ... African Journal of Biotechnology ... and Maroon (Al tolerant) were grown on hydroponic solution (non modified Hoagland) containing AlCl3 (0-100-200-300 μM). Factorial ...

  4. Novel package for inhibition of aluminium corrosion in alkaline solutions

    International Nuclear Information System (INIS)

    Abdel-Gaber, A.M.; Khamis, E.; Abo-Eldahab, H.; Adeel, Sh.

    2010-01-01

    Inhibition of aluminium corrosion in 2 M sodium hydroxide solution by a package composed of the cationic surfactant cetyl trimethyl ammonium bromide (CTAB) and lupine seed extract has been investigated employing different electrochemical techniques and chemical gasometry measurements. Potentiodynamic polarization curve measurements showed that lupine seed extract controls both the anodic dissolution of aluminium and the hydrogen gas evolved at the cathodic sites of aluminium surface. Nyquist plots showed two capacitive semicircles in the high and low frequency regions separated by an inductive loop at intermediate frequencies. The inductive loop may be explained by the occurrence of adsorbed intermediates on the surface. A proposed equivalent circuit was used to analyse the impedance spectra for aluminium in NaOH solutions. The corrosion inhibition data have been analysed using different isotherms. The results showed excellent agreement between the kinetic-thermodynamic model and Flory-Huggins isotherm. Gasometry measurements showed that the Inhibitive effect of the surfactant increases at a composition around its critical micelle concentration (cmc). The presence of both the surfactant and lupine seed extract did not indicate synergistic action between them. The mode of adsorption of the surfactant molecules corresponding to their structure is also discussed.

  5. Determination of parameters in elasto-plastic models of aluminium.

    NARCIS (Netherlands)

    Meuwissen, M.H.H.; Oomens, C.W.J.; Baaijens, F.P.T.; Petterson, R.; Janssen, J.D.; Sol, H.; Oomens, C.W.J.

    1997-01-01

    A mixed numerical-experimental method is used to determine parameters in elasto-plastic constitutive models. An aluminium plate of non-standard geometry is mounted in a uniaxial tensile testing machine at which some adjustments are made to carry out shear tests. The sample is loaded and the total

  6. Effects of Aluminium in Forest. Results of a pilot experiment

    Energy Technology Data Exchange (ETDEWEB)

    Mulder, J; Wit, H de; Nygaard, P H

    1996-01-01

    This conference paper deals with an Norwegian pilot project which started in 1995 and finishing early 1999, investigates the solubility and phyto-toxicity of aluminium (Al) in mature forest ecosystems. The project consists of three major parts, including field manipulation study of Norwegian spruce stands, laboratory experiments and modelling Al chemistry in the root zone. 15 refs.

  7. Establishment of Integrated Information Displays in Aluminium Surfaces Using Nanomanufacturing

    DEFF Research Database (Denmark)

    Prichystal, Jan Phuklin; Bladt, Henrik Henriksen; Hansen, Hans Nørgaard

    2005-01-01

    Bang & Olufsen has been working with a method for manufacturing ultra-thin structures in Aluminium that can be penetrated by light. This has resulted in a patent describing how to obtain this effect by etching of local areas in a solid material. The idea behind an invisible display in Aluminum......-short pulses, selective etching + anodizing, and electrochemical machining....

  8. Superhydrophobic coatings for aluminium surfaces synthesized by chemical etching process

    Directory of Open Access Journals (Sweden)

    Priya Varshney

    2016-10-01

    Full Text Available In this paper, the superhydrophobic coatings on aluminium surfaces were prepared by two-step (chemical etching followed by coating and one-step (chemical etching and coating in a single step processes using potassium hydroxide and lauric acid. Besides, surface immersion time in solutions was varied in both processes. Wettability and surface morphologies of treated aluminium surfaces were characterized using contact angle measurement technique and scanning electron microscopy, respectively. Microstructures are formed on the treated aluminium surfaces which lead to increase in contact angle of the surface (>150°. Also on increasing immersion time, contact angle further increases due to increase in size and depth of microstructures. Additionally, these superhydrophobic coatings show excellent self-cleaning and corrosion-resistant behavior. Water jet impact, floatation on water surface, and low temperature condensation tests assert the excellent water-repellent nature of coatings. Further, coatings are to be found mechanically, thermally, and ultraviolet stable. Along with, these coatings are found to be excellent regeneration ability as verified experimentally. Although aforesaid both processes generate durable and regenerable superhydrophobic aluminium surfaces with excellent self-cleaning, corrosion-resistant, and water-repellent characteristics, but one-step process is proved more efficient and less time consuming than two-step process and promises to produce superhydrophobic coatings for industrial applications.

  9. Novel package for inhibition of aluminium corrosion in alkaline solutions

    Energy Technology Data Exchange (ETDEWEB)

    Abdel-Gaber, A.M., E-mail: ashrafmoustafa@yahoo.com [Chemistry Department, Faculty of Science, Alexandria University, Ibrahimia, P.O. Box 426, Alexandria 21321 (Egypt); Khamis, E.; Abo-Eldahab, H.; Adeel, Sh. [Chemistry Department, Faculty of Science, Alexandria University, Ibrahimia, P.O. Box 426, Alexandria 21321 (Egypt)

    2010-11-01

    Inhibition of aluminium corrosion in 2 M sodium hydroxide solution by a package composed of the cationic surfactant cetyl trimethyl ammonium bromide (CTAB) and lupine seed extract has been investigated employing different electrochemical techniques and chemical gasometry measurements. Potentiodynamic polarization curve measurements showed that lupine seed extract controls both the anodic dissolution of aluminium and the hydrogen gas evolved at the cathodic sites of aluminium surface. Nyquist plots showed two capacitive semicircles in the high and low frequency regions separated by an inductive loop at intermediate frequencies. The inductive loop may be explained by the occurrence of adsorbed intermediates on the surface. A proposed equivalent circuit was used to analyse the impedance spectra for aluminium in NaOH solutions. The corrosion inhibition data have been analysed using different isotherms. The results showed excellent agreement between the kinetic-thermodynamic model and Flory-Huggins isotherm. Gasometry measurements showed that the Inhibitive effect of the surfactant increases at a composition around its critical micelle concentration (cmc). The presence of both the surfactant and lupine seed extract did not indicate synergistic action between them. The mode of adsorption of the surfactant molecules corresponding to their structure is also discussed.

  10. AC-Conductivity measurements on γ-aluminium oxynitride

    NARCIS (Netherlands)

    Willems, H.X.; Hal, van P.F.; Metselaar, R.; With, de G.

    1995-01-01

    AC-conductivity measurements were performed on aluminium oxynitrides (Alons) because of their interesting defect structure. Although it became apparent that these Alons are not stable in the temperature range used, the electrical properties of the materials could be measured with impedance

  11. Sol–gel preparation of selected lanthanide aluminium garnets

    Czech Academy of Sciences Publication Activity Database

    Dubnikova, N.; Garskaite, E.; Pinkas, J.; Bezdička, Petr; Beganskiene, A.; Kareiva, A.

    2010-01-01

    Roč. 55, č. 2 (2010), s. 213-219 ISSN 0928-0707 Institutional research plan: CEZ:AV0Z40320502 Keywords : lanthanide aluminium garnets * sol-gel processing Subject RIV: CA - Inorganic Chemistry Impact factor: 1.525, year: 2010

  12. Hydrogen evolution from aluminium in reactor containment spray solutions

    International Nuclear Information System (INIS)

    Karlberg, G.; Sundvall, S.-B.

    1982-01-01

    Three different aluminium alloys were exposed to conditions similar to BWR and PWR containment spray waters at 50, 100 and 150 0 C. BWR deionized water gives corrosion rates of at most 0.05 mm/year and hydrogen concentrations less than 0.1-1%. On the contrary PWR alkaline solutions give very high corrosion rates and hydrogen contents. (Auth.)

  13. Hydrogen generation from aluminium corrosion in reactor containment spray solutions

    International Nuclear Information System (INIS)

    Frid, W.; Karlberg, G.; Sundvall, S.B.

    1982-01-01

    The aluminium corrosion experiments in reactor containment spray solutions, under the conditions expected to prevail during LOCA in BWR and PWR, were performed in order to investigate relationships between temperature, pH and hydrogen production rates. In order to simulate the conditions in a BWR containment realistic ratios between aluminium surface and water volume and between aluminium surface and oxygen volume were used. Three different aluminium alloys were exposed to spray solutions: AA 1050, AA 5052 and AA 6082. The corrosion rates were measured for BWR solutions (deaerated and aerated) with pH 5 and 9 at 50, 100 and 150 0 C. The pressure was constantly 0.8 MPa. The hydrogen production rate was measured by means of gas chromatography. In deionized BWR water the corrosion rates did not exceed about 0.05 mm/year in all cases, i.e. were practically independent of temperature and pH. Hydrogen concentrations were less than 0.1 vol.% in cooled dry gas. Corrosion rates and hydrogen production in PWR alkaline solution measured at pH 9.7 and 150 0 C were very high. AA 5052 alloy was the best material

  14. Contribution to comprehensive study of aluminium alloy Aa 5083 ...

    African Journals Online (AJOL)

    PROMOTING ACCESS TO AFRICAN RESEARCH ... Corrosion induced by elemental mercury in aqueous media of industrial Aluminium alloys AA5083 used in heat exchanger industries of natural gas liquefaction has been studied by linear sweep voltammétry on ... EMAIL FREE FULL TEXT EMAIL FREE FULL TEXT

  15. Aluminium Structures in Building and Civil Engineering Applications

    NARCIS (Netherlands)

    Soetens, F.

    2010-01-01

    Structural applications of aluminium are considered in this paper. Although the discussion is mainly devoted to Europe, the paper also refers, where possible, to developments in other parts of the world. The problems faced by a designer in creating an optimum design are described, followed by a

  16. Sensitivity analysis on ultimate strength of aluminium stiffened panels

    DEFF Research Database (Denmark)

    Rigo, P.; Sarghiuta, R.; Estefen, S.

    2003-01-01

    This paper presents the results of an extensive sensitivity analysis carried out by the Committee III.1 "Ultimate Strength" of ISSC?2003 in the framework of a benchmark on the ultimate strength of aluminium stiffened panels. Previously, different benchmarks were presented by ISSC committees on ul...

  17. Aluminium dissolution for spray pulverization with nitric acid

    International Nuclear Information System (INIS)

    Rodrigo Otero, A.; Rodrigo Vilaseca, F.; Morales Calvo, G.

    1977-01-01

    A comparative study of the nitric acid dissolution of aluminium, by immersion and spray pulverization has been carried out in laboratory scale. As a result, the optimum operation conditions to control reaction in the plant are fixed. Operation costs are also evaluated. (author) [es

  18. Modelling aluminium wire bond reliability in high power OMP devices

    NARCIS (Netherlands)

    Kregting, R.; Yuan, C.A.; Xiao, A.; Bruijn, F. de

    2011-01-01

    In a RF power application such as the OMP, the wires are subjected to high current (because of the high power) and high temperature (because of the heat from IC and joule-heating from the wire itself). Moreover, the wire shape is essential to the RF performance. Hence, the aluminium wire is

  19. Diamond turning and polishing tests on new RSP aluminium alloys

    NARCIS (Netherlands)

    Horst, R. ter; Haan, M. de; Gubbels, G.P.H.; Senden, R.; Venrooy, B.W.H. van; Hoogstrate, A.M.

    2012-01-01

    For years now conventional aluminium 6061 T6 has widely been used for mirrors in astronomical instruments, being diamond turned or since a few years also being optically polished. This allows the development of optical systems that can be tested and operated at any temperature, without being

  20. The effect of atmospheric corona treatment on AA1050 aluminium

    DEFF Research Database (Denmark)

    Jariyaboon, Manthana; Møller, Per; Dunin-Borkowski, Rafal E.

    2010-01-01

    The effect of atmospheric corona discharge on AM 050 aluminium surface was investigated using electrochemical polarization, SEM-EDX, FIB-SEM. and XPS. The corona treatment was performed with varying time (1, 5, and 15 min) in atmospheric air. A 200 nm oxide layer was generated on AA1050 after...

  1. Structure analysis of 3104 aluminium alloy applied to deep drawing

    Energy Technology Data Exchange (ETDEWEB)

    Klyszewski, A.; Lech-Grega, M.; Zelechowski, J.; Szymanski, W. [Light Metals Div., Skawina (Poland). Inst. of Non-Ferrous Metals

    2000-07-01

    Optical and electron microscopy observations and X-ray investigations of 3104 aluminium alloy ingots and bands after experimental heat treatment were carried out. The influence of ingots homogenisation temperature and parameters of material heat treatment after hot rolling on structure, texture and earing of band 0.3 mm thick was analysed. (orig.)

  2. Effect of strain path on severely deformed aluminium

    Czech Academy of Sciences Publication Activity Database

    Kunčická, L.; Kocich, R.; Král, Petr; Pohludka, M.; Marek, M.

    2016-01-01

    Roč. 180, OCT (2016), s. 280-283 ISSN 0167-577X Institutional support: RVO:68081723 Keywords : Twist channel angular pressing * Aluminium * Texture * Microstructure Electron microscopy * Metal forming and shaping Subject RIV: JG - Metallurgy Impact factor: 2.572, year: 2016

  3. Elaboration in the area of aluminium containing alloys

    International Nuclear Information System (INIS)

    Mirsaidov, U.M.

    2002-01-01

    In the Institute of Chemistry was elaborated the experimental-industrial installation and technology of deep aluminium purification by the methods of zone melting and recrystallization. The developed technology let receive the metal of model A5 N A6 N dependence from number of induction zone passage

  4. Cavitation-aided grain refinement in aluminium alloys

    NARCIS (Netherlands)

    Atamanenko, T.V.

    2010-01-01

    This thesis deals with grain refinement under the influence of ultrasonic-driven cavitation in aluminium casting processes. Three major goals of this research were: (1) to identify the mechanism of the cavitation-aided grain refinement at different stages of solidification; (2) to reveal the

  5. Local electrochemical behaviour of 7xxx aluminium alloys

    NARCIS (Netherlands)

    Andreatta, F.

    2004-01-01

    Aluminium alloys of the 7xxx series (Al-Zn-Mg-Cu) are susceptible to localized types of corrosion like pitting, intergranular corrosion and exfoliation corrosion. This represents a limitation for the application of these alloys in the aerospace components because localized corrosion might have a

  6. Synthesis, properties, and assimilation methods of aluminium hydride

    International Nuclear Information System (INIS)

    Mirsaidov, U.M.

    2013-01-01

    We have discovered a new source of aluminium hydride-conversion of tetrahydrofurane under influence of halogenous alkyls. We have proposed the chlorbenzene method of synthesis of AlH 3 , which excludes adhesion and ensure high quality of the product with respect to its purity, thermal stability, habits of crystals (round shape), and granulometric composition. We determined capability of benzyl chloride to fix AlH 4 -groups by the way of complexes formation. This allows increasing efficient concentration of AlH 3 solutions and their productivity. We have carried out 'direct' crystallization of aluminium hydride in one stage using interaction of binary metal hydride with aluminium chloride in the medium of ether-toluene at 60-100 d ig C a nd using solvent distillation. In the reaction of Li H with AlCl 3 , we achieved output of pure crystal AlH 3 of hexagonal modification, which was close to quantitative. We have discovered the assimilation methods of aluminium hydride in carrying out of solid-phase chemical reactions. (author)

  7. On the anodic aluminium oxide refractive index of nanoporous templates

    International Nuclear Information System (INIS)

    Hierro-Rodriguez, A; Rocha-Rodrigues, P; Araujo, J P; Valdés-Bango, F; Alameda, J M; Teixeira, J M; Jorge, P A S; Santos, J L; Guerreiro, A

    2015-01-01

    In the present study, we have determined the intrinsic refractive index of anodic aluminium oxide, which is originated by the formation of nanoporous alumina templates. Different templates have been fabricated by the conventional two-step anodization procedure in oxalic acid. Their porosities were modified by chemical wet etching allowing the tuning of their effective refractive indexes (air-filled nanopores  +  anodic aluminium oxide). By standard spectroscopic light transmission measurements, the effective refractive index for each different template was extracted in the VIS–NIR region. The determination of the intrinsic anodic aluminium oxide refractive index was performed by using the Maxwell–Garnett homogenization theory. The results are coincident for all the fabricated samples. The obtained refractive index (∼1.55) is quite lower (∼22%) than the commonly used Al 2 O 3 handbook value (∼1.75), showing that the amorphous nature of the anodic oxide structure strongly conditions its optical properties. This difference is critical for the correct design and modeling of optical plasmonic metamaterials based on anodic aluminium oxide nanoporous templates. (paper)

  8. Electrochemical Characterisation of Filiform Corrosion on Aluminium Rolled Products

    NARCIS (Netherlands)

    Huisert, M.

    2001-01-01

    When aluminium is protected by an organic coating a special form of corrosion can occur underneath the organic coating; filiform corrosion. This form of corrosion manifests itself as threadlike filaments under the coating, it causes local delamination of the coating and the coating cannot protect

  9. Impact toughness of laser alloyed aluminium AA1200 alloys

    CSIR Research Space (South Africa)

    Mabhali, Luyolo AB

    2013-08-01

    Full Text Available ),. 559-563. [2] T. Tomida, K. Nakata, S. Saji, T. Kubo, T, Formation of metal matrix composite layer on aluminium alloy with TiC-Cu powder by laser surface alloying process; Surface and Coatings Technology; vol. 142-144, 2001, 585-589. [3] L. A. B...

  10. Aluminium localization and toxicity symptoms related to root growth ...

    Indian Academy of Sciences (India)

    We correlated root growth inhibition with aluminium (Al3+) localization and toxicity symptoms in rice roots using seedlings of two genotypes (tolerant and sensitive) that were exposed to different AlCl3 concentrations. Al3+ localization was evaluated by hematoxylin in primary roots and by morin in cross-sections of the root ...

  11. Friction factor of CP aluminium and aluminium–zinc alloys

    Indian Academy of Sciences (India)

    zinc alloys using ring compression test at different temperatures from 303 K to 773 K. It is found that CP aluminium exhibits stick- ing whereas Al–Zn alloys do not exhibit sticking at elevated temperatures. Hot working of Al–Zn alloy is easier.

  12. STRUCTURE OF ECAP ALUMINIUM AFTER DIFFERENT NUMBER OF PASSES

    Directory of Open Access Journals (Sweden)

    Lucia Ilucová

    2011-05-01

    Full Text Available The structure of high purity (99.99% aluminium processed by equal channel angular pressing in the as pressed state after different number of passes was examined using various stereological methods. An extreme inhomogeneity and complicated anisotropy was observed along the body of rod-like specimens.

  13. Examples on cold forged aluminium components in automotive industry

    DEFF Research Database (Denmark)

    Bay, Niels; Kolsgaard, A.

    2000-01-01

    The present paper describes the possibilites of applying cold forging for manufacturing of light weight components in aluminium. A short description of the basic cold forming processes forms the basis for describing the great variety in design of cold forged components. Examples are mainly taken ...... from automotive industry but in a few cases also from other industrial sectors to show the possibilities....

  14. Development of aluminium-26 accelerator mass spectrometry for biological and toxicological applications

    Science.gov (United States)

    Barker, James

    Aluminium is now recognised as a toxic element. Its accumulation in the body leads to serious conditions in renal failure patients on haemodialysis, and there is suspected involvement in the aetiology of Alzheimer's Disease. Although uptake from food and water are important exposure pathways, there is so far little quantitative knowledge about gastrointestinal absorption of aluminium, its general speciation in the blood or its metabolism. This is partly because seven of aluminium's eight radioisotopes have half-lives too short to conduct accurate biochemical studies. The use of [67]Ga as a tracer for aluminium begs the question of its biochemical similarity. Radiotracer studies on aluminium are possible with [26]Al (T[2] = 716,000 years), but a comparatively large amount of this scarce and expensive radioisotope (price ca. 50 pence per Bq) would be needed to measure by normal counting techniques. Use of conventional mass spectrometry is impracticable due to [26]Mg interference (comprises 11 % of total stable Mg and inherent in all biological or environmental samples), but high energy Accelerator Mass Spectrometry (A.M.S.), resulting in some fully-stripped ions (Al[13+], Mg[12+]) , potentially overcomes this problem. [26]Al is particularly attractive in human toxicology because of its negligible natural abundance and low radiological hazard. We have used the 20 MV tandem Van De Graaff accelerator (S.E.R.C. Daresbury) to conduct 1A1 A.M.S. measurements in biological media. Stable currents of ALQ[-](100 nA for > 5 hours) were obtained from a modified Middleton ion source, using alumina/silver ion source preparations of 50 mug Al. [26]Al is unambiguously identified from and [26]Mg [27]AlO[-] is repeatedly measured on a Faray Cup placed in the beamline after adjusting the ion source magnet. Linear calibration (C.V. range tested ([26]Al/[27]Al ratios from 10[-6] to 10[-11]) and a detection limit (2?) of ca. 7 x 10[-18]g (5 nBq) [26]Al ratio [26]Al/[27]Al limit of 1.4 x

  15. Corrosion of research reactor aluminium clad spent fuel in water

    International Nuclear Information System (INIS)

    2009-12-01

    A large variety of research reactor spent fuel with different fuel meats, different geometries and different enrichments in 235 U are presently stored underwater in basins located around the world. More than 90% of these fuels are clad in aluminium or aluminium based alloys that are notoriously susceptible to corrosion in water of less than optimum quality. Some fuel is stored in the reactor pools themselves, some in auxiliary pools (or basins) close to the reactor and some stored at away-from-reactor pools. Since the early 1990s, when corrosion induced degradation of the fuel cladding was observed in many of the pools, corrosion of research reactor aluminium clad spent nuclear fuel stored in light water filled basins has become a major concern, and programmes were implemented at the sites to improve fuel storage conditions. The IAEA has since then established a number of programmatic activities to address corrosion of research reactor aluminium clad spent nuclear fuel in water. Of special relevance was the Coordinated Research Project (CRP) on Corrosion of Research Reactor Aluminium Clad Spent Fuel in Water (Phase I) initiated in 1996, whose results were published in IAEA Technical Reports Series No. 418. At the end of this CRP it was considered necessary that a continuation of the CRP should concentrate on fuel storage basins that had demonstrated significant corrosion problems and would therefore provide additional insight into the fundamentals of localized corrosion of aluminium. As a consequence, the IAEA started a new CRP entitled Corrosion of Research Reactor Aluminium Clad Spent Fuel in Water (Phase II), to carry out more comprehensive research in some specific areas of corrosion of aluminium clad spent nuclear fuel in water. In addition to this CRP, one of the activities under IAEA's Technical Cooperation Regional Project for Latin America Management of Spent Fuel from Research Reactors (2001-2006) was corrosion monitoring and surveillance of research

  16. Beam loading

    OpenAIRE

    Boussard, Daniel

    1987-01-01

    We begin by giving a description of the radio-frequency generator-cavity-beam coupled system in terms of basic quantities. Taking beam loading and cavity detuning into account, expressions for the cavity impedance as seen by the generator and as seen by the beam are derived. Subsequently methods of beam-loading compensation by cavity detuning, radio-frequency feedback and feedforward are described. Examples of digital radio-frequency phase and amplitude control for the special case of superco...

  17. Molecular beams

    International Nuclear Information System (INIS)

    Pendelbury, J.M.; Smith, K.F.

    1987-01-01

    Studies with directed collision-free beams of particles continue to play an important role in the development of modern physics and chemistry. The deflections suffered by such beams as they pass through electric and magnetic fields or laser radiation provide some of the most direct information about the individual constituents of the beam; the scattering observed when two beams intersect yields important data about the intermolecular forces responsible for the scattering. (author)

  18. Cleaning method of aluminium surface by argon discharge for photon factory

    International Nuclear Information System (INIS)

    Mizuno, Hajime; Yamaguchi, Hiroshi; Watabe, Hiromi; Horikoshi, Gen-ichi; Mathewson, A.G.

    1978-01-01

    In the Photon Factory program of High Energy Research Laboratory, in which the electron storage ring as a photon source stores the electron beam of 2.5 GeV and 500 mA, beam intensity the probability of gas discharge from the inner surface of doughnut wall due to electron bombardment (for 100 eV electorns) must be limited to 1 x 10 -6 or less, according to the estimation by A.G. Mathewson and others. The pressure inside the ring can be maintained at 1 x 10 -9 Torr only with the above probability value. The standard surface treatment of degreasing and evacuation for 24 hours with heating at 150 deg. C can be of no practical use. Since the ion bombardment of surfaces by argon glow discharge is effective for decreasing the probability, the reduction of the probability by argon discharge cleaning was measured with the surface of aluminium, which is planned to be used as the doughnut material. Two methods were employed for the measurement; the one is analysis of gases being discharged, by introducting them to the analyzing chamber during argon discharge and the other is the measurement of the probability when bombardment with electrons of 100 eV is applied, after stopping argon introduction and evacuating after argon discharge had been performed for a definite period. As a result, the probability of approximately 2 x 10 -5 at the beginning of electron beam incidence was obtained by adding argon discharge cleaning to the standard method. This is estimated to correspondent to approximately 25 mA of beam intensity, which is equivalent to 1/20 of the planned value. (Wakatsuki, Y.)

  19. Aluminium - Cobalt-Pillared Clay for Dye Filtration Membrane

    Science.gov (United States)

    Darmawan, A.; Widiarsih

    2018-04-01

    The manufacture of membrane support from cobalt aluminium pillared clay has been conducted. This research was conducted by mixing a clay suspension with pillared solution prepared from the mixture of Co(NO3)2.6H2O and AlCl3.6H2O. The molar ratio between Al and Co was 75:25 and the ratio of [OH-]/[metal] was 2. The clay suspension was stirred for 24 hours at room temperature, filtered and dried. The dried clay was then calcined at 200°C, 300°C and 400°C with a ramp rate of 2°C/min. Aluminium-cobalt-pillared clay was then characterized by XRD and GSA and moulded become a membrane support for subsequent tests on dye filtration. The XRD analysis showed that basal spacing (d 001) value of aluminium cobalt was 19.49 Å, which was higher than the natural clay of 15.08Å however, the basal spacing decreased with increasing calcination temperature. The result of the GSA analysis showed that the pore diameter of the aluminium cobalt pillared clay membrane was almost the same as that of natural clay that were 34.5Å and 34.2Å, respectively. Nevertheless, the pillared clay has a more uniform pore size distribution. The results of methylene blue filtration measurements demonstrated that the membrane filter support could well which shown by a clear filtrate at all concentrations tested. The value of rejection and flux decreased with the increasing concentration of methylene blue. The values of dye rejection and water flux reached 99.89% and 5. 80 x 10-6 kg min-1, respectively but they decreased with increasing concentration of methylene blue. The results of this study indicates that the aluminium-pillared clay cobalt could be used as membrane materials especially for ultrafiltration.

  20. Adsorption of lithium ion to amorphous hydrous aluminium oxide

    International Nuclear Information System (INIS)

    Wada, Hideo; Kitamura, Takao; Fujii, Ayako; Katoh, Shunsaku

    1982-01-01

    Adsorption process of lithium ion to amorphous hydrous aluminium oxide (a-HAO) was investigated by pH titration method with lithium chloride-lithium hydroxide mixed solution and X-ray diffraction analysis of a-HAO after pH titration. In the pH titration, the addition of hydroxide ion in amount from 0 to 4.0 mmol.g -1 gave no change to the pH of the solution and caused adsorption of lithium ion equivalent in amount to added hydroxide ion. X-ray diffraction analysis showed the formation of lithium hydrogenaluminate LiH (AlO 2 ) 2 .5H 2 O (LHA) in the a-HAO after pH titration. These results showed that adsorption of lithium ion by a-HAO was related to a reaction which consumed hydroxide ion and formed LHA. In order to elucidate detail process of the reaction, changes of pH, aluminium concentration and lithium concentration of the solution, respectively with time, were determined. The pH of the solution decreased in two stages. At the first stage of the pH decrease, the aluminium concentration increased whereas the lithium concentration did not change. At the second stage, the lithium concentration decreased together with the decrease of the aluminium concentration. It was inferred that adsorption of lithium ion proceeded through dissolution of a-HAO and precipitation of LHA. Theoretical adsorption capacity calculated from the above formula for LHA and aluminium content in a-HAO was 4.7 mmol.g -1 and agreed fairly well with observed value 4.0 mmol.g -1 . (author)

  1. Galvanic corrosion study of aluminium alloy plates mounted to stainless and mild steel bolts by accelerated exposure test

    OpenAIRE

    MREMA, Emmanuel; ITOH, Yoshito; KANEKO, Akira; HIROHATA, Mikihito

    2016-01-01

    Despite the fact that aluminium alloy members have a proven durability over stainless steel members, their joint fasteners like bolts, nuts and washers are drawn from steel material due to aluminium alloy inferior mechanical properties. Bare contact between aluminium alloy members and stainless steel fasteners results to galvanic corrosion of aluminium alloy members. A corrosion behaviour study was carried out on different aluminium alloy types with different surface treatments mounted to sta...

  2. Design of the MI40 beam-abort dump

    International Nuclear Information System (INIS)

    Bhat, C.M.; Martin, P.S.; Russell, A.D.

    1995-05-01

    A beam-abort dump for the Fermilab Main Injector to handle 3E13 protons per pulse at 150 Gev has been designed. A 120 GeV beam line goes through the beam-dump off-set by 27cm from its center. The design and the environmental safety aspects of the beam-dump are described here

  3. Decreased toxicity of aluminium when the ionic strength increases in water; Blir aluminium mindre toksisk naar ionestyrken i vannet oeker?

    Energy Technology Data Exchange (ETDEWEB)

    Alstad, E W [Oslo Univ. (Norway)

    1996-01-01

    The conference paper evaluates the acute mortality of fish caused by the toxicity of aluminium in water. The evaluation is based on the polymerization hypothesis. According to the author, the level of toxicity decreases when the concentration and charge of ions increase. The paper presents the preliminary results from the executed experiment. 2 refs., 2 figs., 1 tab.

  4. Corrosion of aluminium in copper-aluminium couples under a marine environment: Influence of polyaniline deposited onto copper

    International Nuclear Information System (INIS)

    Vera, Rosa; Verdugo, Patricia; Orellana, Marco; Munoz, Eduardo

    2010-01-01

    Research highlights: → The presence of Polyaniline in the Al-Cu system produces a decrease in the oxygen reduction reaction. → In the marine enviroment, aluminium in Al-Cu couples, suffers pitting and exfoliation. → The aluminium deterioration increases with chloride and enviromental sulphur dioxide presence, mainly when it is united to bare copper. - Abstract: In this study, we examined how aluminium corrosion in Al-Cu/PANI galvanic couples in a marine environment is influenced by deposition of polyaniline (PANI) on copper. Polarization curves and immersion assays in 0.1 M NaCl were performed. The morphologies of etched Al and corrosion products were observed by SEM, and the Al ions in solution were quantified by atomic absorption spectroscopy. A reduction in aluminium damage due to galvanic corrosion was observed as a result of decreased effective area for the oxygen reduction reaction on Cu/PANI electrode. Furthermore, an electrochemical reduction of PANI from leucoemeraldine to emeraldine base is proposed.

  5. Energy conversion from aluminium and phosphate rich solution via ZnO activation of aluminium

    Energy Technology Data Exchange (ETDEWEB)

    Slaughter, Gymama, E-mail: gslaught@umbc.edu; Sunday, Joshua; Stevens, Brian

    2015-08-01

    Electrochemical power sources have motivated intense research efforts in the development of alternative ‘green’ power sources for ultra-low powered bioelectronic devices. Biofuel cells employ immobilized enzymes to convert the available chemical energy of organic fuels directly into electricity. However, biofuel cells are limited by short lifetime due to enzyme inactivation and frequent need to incorporate mediators to shuttle electrons to the final electron acceptor. In this context, other electrochemical power sources are necessary in energy conversion and storage device applications. Here we report on the fabrication and characterization of a membrane-free aluminium/phosphate cell based on the activation of aluminium (Al) using ZnO nanocrystal in an Al/phosphate cell as a ‘green’ alternative to the traditional enzymatic biofuel cells. The hybrid cell operates in neutral phosphate buffer solution and physiological saline buffer. The ZnO modifier in the phosphate rich electrolyte activated the pitting of Al resulting in the production of hydrogen, as the reducing agent for the reduction of H{sub 2}PO{sub 4}{sup −} ions to HPO{sub 3}{sup 2−} ions at a formal potential of −0.250 V vs. Ag/AgCl. Specifically, the fabricated cell operating in phosphate buffer and physiological saline buffer exhibit an open-circuit voltage of 0.810 V and 0.751 V and delivered a maximum power density of 0.225 mW cm{sup −2} and 1.77 mW cm{sup −2}, respectively. Our results demonstrate the feasibility of generating electricity by activating Al as anodic material in a hybrid cell supplied with phosphate rich electrolyte. Our approach simplifies the construction and operation of the electrochemical power source as a novel “green” alternative to the current anodic substrates used in enzymatic biofuel cells for low power bioelectronics applications. - Graphical abstract: Display Omitted - Highlights: • ZnO activation of metallic Al for generating electricity for

  6. Beam diagnostics

    International Nuclear Information System (INIS)

    Bogaty, J.; Clifft, B.E.; Zinkann, G.P.; Pardo, R.C.

    1995-01-01

    The ECR-PII injector beam line is operated at a fixed ion velocity. The platform high voltage is chosen so that all ions have a velocity of 0.0085c at the PII entrance. If a previous tune configuration for the linac is to be used, the beam arrival time must be matched to the previous tune as well. A nondestructive beam-phase pickup detector was developed and installed at the entrance to the PII linac. This device provides continuous phase and beam current information and allows quick optimization of the beam injected into PII. Bunches traverse a short tubular electrode thereby inducing displacement currents. These currents are brought outside the vacuum interface where a lumped inductance resonates electrode capacitance at one of the bunching harmonic frequencies. This configuration yields a basic sensitivity of a few hundred millivolts signal per microampere of beam current. Beam-induced radiofrequency signals are summed against an offset frequency generated by our master oscillator. The resulting kilohertz difference frequency conveys beam intensity and bunch phase information which is sent to separate processing channels. One channel utilizes a phase locked loop which stabilizes phase readings if beam is unstable. The other channel uses a linear full wave active rectifier circuit which converts kilohertz sine wave signal amplitude to a D.C. voltage representing beam current. A prototype set of electronics is now in use with the detector and we began to use the system in operation to set the arrival beam phase. A permanent version of the electronics system for the phase detector is now under construction. Additional nondestructive beam intensity and phase monitors at the open-quotes Boosterclose quotes and open-quotes ATLASclose quotes linac sections are planned as well as on some of the high-energy beam lines. Such a monitor will be particularly useful for FMA experiments where the primary beam hits one of the electric deflector plates

  7. Formation of disorder aluminium zones in an immiscible lead-aluminium system

    International Nuclear Information System (INIS)

    Huang, R Z; Zhang, L H; Sui, M L; Wang, Y M

    2004-01-01

    High resolution transmission electron microscopy (HRTEM) observations show evidence for the formation of disorder Al zones around some faceted Pb inclusions embedded in an Al matrix in immiscible lead-aluminium samples, which were prepared by a melt-spun method and then aged for about two months at room temperature. Furthermore, it is found that, both before and after ageing, all such Pb inclusions have a cube-cube orientation relationship with the Al matrix. The results of molecular dynamics (MD) simulations give an extensive analysis of the formation of the disorder Al zones and provide a reasonable explanation for the HRTEM finding: the existence of oxygen soluted in the Pb inclusions at higher temperatures may lead to the formation of the disorder Al zone in the aged sample. The dependence of the thickness of the disorder Al zone on the amount of oxygen soluted in the Pb inclusion at higher temperatures, and the average stress in the equilibrium configuration of a MD cell, is discussed

  8. Metal impurity injection into DIVA plasmas with a Q-switched laser beam

    International Nuclear Information System (INIS)

    Yamauchi, Toshihiko; Nagami, Masayuki; Sengoku, Seio; Kumagai, Katsuaki

    1978-08-01

    Metal impurity injection into DIVA plasmas with a Q-switched ruby laser beam is described. Metal materials used are aluminium and gold. The Q-switched laser beam is incident onto a thin metal film thickness about 0.2 μm coated on pyrex glass plate surface. The metal film is vaporized by the laser beam and injected into DIVA plasma. The laser-beam injection method has advantages of sharp profile of vaporized metal, easy control of vaporized metal quantity and injection rate control of metal vapor. (author)

  9. Recycled Aluminium Cans/Eggshell Composites: Evaluation of Mechanical and Wear Resistance Properties

    Directory of Open Access Journals (Sweden)

    J.O. Agunsoye

    2015-03-01

    Full Text Available Aluminium based metal matrix composites have been produced from recycled aluminium cans and 150µm sized eggshell particles using a stir cast process. The mechanical properties of the control and aluminium can/eggshell composites produced have been investigated. The microstructures of the aluminium can/eggshell composites were examined with the aids of Scanning Electron Microscope (SEM after the sample surfaces have been carefully prepared and etched with aqueous solution of 0.5 cm3 nitric acid. Micrographs revealed that there was a homogenous distribution of eggshell particles within the aluminium can matrix. An indication of effective stirring action during the melting process. The wear resistance was also investigated under different applied loads (6 to 14 N on an abrasive surface emery paper of grade 220. The results revealed an increase in Young’s modulus of elasticity and yield stress from 1,206.45 and 50.23 Mpa respectively of the cast aluminium can with 0 % eggshell particle to the maximum of 3,258.87and 73.2 MPa of aluminium can/12 % eggshell composites. The hardness values increased from 66.23 to 75.13 VN. There was a gradual increase in wear rate of the tested samples as the applied load increased. However, the wear resistance of the aluminium can/6 % eggshell and aluminium can/12 % eggshell composites increased significantly. Hence, recycling of aluminium cans and eggshells can be harnessed into development of useful engineering metal matrix composite materials.

  10. Aluminium tolerance in rice is antagonistic with nitrate preference and synergistic with ammonium preference.

    Science.gov (United States)

    Zhao, Xue Qiang; Guo, Shi Wei; Shinmachi, Fumie; Sunairi, Michio; Noguchi, Akira; Hasegawa, Isao; Shen, Ren Fang

    2013-01-01

    Acidic soils are dominated chemically by more ammonium and more available, so more potentially toxic, aluminium compared with neutral to calcareous soils, which are characterized by more nitrate and less available, so less toxic, aluminium. However, it is not known whether aluminium tolerance and nitrogen source preference are linked in plants. This question was investigated by comparing the responses of 30 rice (Oryza sativa) varieties (15 subsp. japonica cultivars and 15 subsp. indica cultivars) to aluminium, various ammonium/nitrate ratios and their combinations under acidic solution conditions. indica rice plants were generally found to be aluminium-sensitive and nitrate-preferring, while japonica cultivars were aluminium-tolerant and relatively ammonium-preferring. Aluminium tolerance of different rice varieties was significantly negatively correlated with their nitrate preference. Furthermore, aluminium enhanced ammonium-fed rice growth but inhibited nitrate-fed rice growth. The results suggest that aluminium tolerance in rice is antagonistic with nitrate preference and synergistic with ammonium preference under acidic solution conditions. A schematic diagram summarizing the interactions of aluminium and nitrogen in soil-plant ecosystems is presented and provides a new basis for the integrated management of acidic soils.

  11. Investigations concerning the effect of aluminium toxicity on the physiology and fine structures of oat plants. Physiologische und feinstrukturelle Untersuchungen zur Aluminium-Toxizitaet an Haferpflanzen

    Energy Technology Data Exchange (ETDEWEB)

    Marienfeld, S.

    1992-06-30

    In order to test the toxicity of aluminium to plants, two-week-old oat seedlings were exposed to aluminium concentrations of 0-400 [mu]M in the culture broth. Already after 12-24 hours a decrease in longitudinal root growth is to be noted, resulting from impaired mitosis activity of the root tip. This, and the observed premature cell differentiation are not aluminium-specific but unspecific reactions to unfavourable conditions. Shoot growth is only reduced after 3-4 days, and less so. Magnesium and calcium fertilization did enhance the growth of aluminium-stressed plants, but not to the level of the control plants, although the mineral concentration in the leaves reached normal values. Phosphate concentration in the root increased because of aluminium phosphate precipitation in the cell walls, which has detoxifying effect along with aluminium fixation to negative charges in the cell walls. Aluminium remains almost quantitatively in the cell wall area of the roots and is not accumulated in the cell core. Aluminium stress causes transpiration and CO[sub 2] uptake to be impaired as a reaction to the growth depression in the root area, even before the mineral concentration in the shoots is lowered. Later there follow chlorophyll depletion, chloroplast degradation, and a reduction of the leaf area. (UWA)

  12. Method of preparing an Al-Ti-B grain refiner for aluminium-comprising products, and a method of casting aluminium products

    NARCIS (Netherlands)

    Brinkman, H.J.; Duszczyk, J.; Katgerman, L.

    1999-01-01

    The invention relates to a method of preparing an Al-Ti-B grain refiner for cast aluminium-comprising products. According to the invention the preparation is realized by mixing powders selected from the group comprising aluminium, titanium, boron, and alloys and intermetallic compounds thereof,

  13. Hot Press as a Sustainable Direct Recycling Technique of Aluminium: Mechanical Properties and Surface Integrity.

    Science.gov (United States)

    Yusuf, Nur Kamilah; Lajis, Mohd Amri; Ahmad, Azlan

    2017-08-03

    Meltless recycling technique has been utilized to overcome the lack of primary resources, focusing on reducing the usage of energy and materials. Hot press was proposed as a novel direct recycling technique which results in astoundingly low energy usage in contrast with conventional recycling. The aim of this study is to prove the technical feasibility of this approach by characterizing the recycled samples. For this purpose, AA6061 aluminium chips were recycled by utilizing hot press process under various operating temperature (T s = 430, 480, and 530 °C) and holding times (t s = 60, 90, and 120 min). The maximum mechanical properties of recycled chip are Ultimate tensile strength (UTS) = 266.78 MPa, Elongation to failure (ETF) = 16.129%, while, for surface integrity of the chips, the calculated microhardness is 81.744 HV, exhibited at T s = 530 °C and t s = 120 min. It is comparable to theoretical AA6061 T4-temper where maximum UTS and microhardness is increased up to 9.27% and 20.48%, respectively. As the desired mechanical properties of forgings can only be obtained by means of a final heat treatment, T5-temper, aging after forging process was employed. Heat treated recycled billet AA6061 (T5-temper) are considered comparable with as-received AA6061 T6, where the value of microhardness (98.649 HV) at 175 °C and 120 min of aging condition was revealed to be greater than 3.18%. Although it is quite early to put a base mainly on the observations in experimental settings, the potential for significant improvement offered by the direct recycling methods for production aluminium scrap can be clearly demonstrated. This overtures perspectives for industrial development of solid state recycling processes as environmentally benign alternatives of current melting based practices.

  14. Electron beam generated in low pressure noble gas atmosphere – Compact device construction and applications

    International Nuclear Information System (INIS)

    Zawada, A.; Konarski, P.

    2013-01-01

    During the process of low vacuum electron beam welding the energy of electrons is lower than the energy of electrons in the classical electron beam welding equipment. The classical electron beam welding can not always be used to weld of small work-piece details. Sometimes it’s impossible to reduce the electron beam energy because of poor focusing in the conventional electron beam welding machines. Low vacuum electron beam welding technique is well suitable to several niche products, such as thermocouples or aluminium seals. It also allows to treat the surface of dielectric materials, which is not possible using classical electron beam welding technique. The costs of low vacuum electron beam welding process are very low. (authors)

  15. Nanosized f.c.c. thallium inclusions in aluminium

    International Nuclear Information System (INIS)

    Johnson, E.; Johansen, A.; Thoft, N.B.; Andersen, H.H.; Sarholt-Kristensen, L.

    1993-01-01

    Ion implantation of pure aluminium with thallium induces the formation of nanosized crystalline inclusions of thallium with a f.c.c. structure. The size of the inclusions depends on the implantation conditions and subsequent annealing treatments and is typically in the range from 1 to 10 nm. The inclusions are aligned topotactically with the aluminium matrix with a cube-cube orientation relationship and they have a truncated octahedral shape bounded by {111} and {001} planes. The lattice parameter of the f.c.c. thallium inclusions is 0.484 ± 0.002 nm, which is slightly but significantly larger than in the high-pressure f.c.c. thallium phase known to be stable above 3.8 GPa. (Author)

  16. Economic cost of electricity sold to new aluminium smelters

    International Nuclear Information System (INIS)

    Belanger, G.; Bernard, J.T.

    2008-01-01

    Low cost electricity was a key factor for establishing an aluminium industry in Quebec. Smelters in the province use 50 terawatt hours of electricity per year, which represents 25 per cent of the total consumed in Quebec. This article assessed the profitability of new industrial projects that require large quantities of electricity at a time when the cost of new power plants is increasing. However, electricity is being sold below cost and the difference is subsidized by the government. The investment is justified by the government because these new projects create high paying jobs. The authors presented cases of 2 new aluminium plants, and concluded that they represented a very high economic cost for the province. 1 tab

  17. Optically Designed Anodised Aluminium Surfaces: Microstructural and Electrochemical Aspects

    DEFF Research Database (Denmark)

    Gudla, Visweswara Chakravarthy

    is not possible as the anodic pore sizes are an order of magnitude smaller than the traditional white pigments. The approaches presented in this thesis focus on different techniques like modification of the aluminium microstructure, engineering of the aluminium surface, and application on non...... the microstructure in order to impart light scattering ability to the anodised layer. Coatings based on Al-Zr and Al-Ti binary system were studied for their anodising behaviour with and without heat treatment. The structure evolution of the Al-Zr sputtered coatings and the effect of Si during heat treatment...... Emission Spectroscopy, and Scanning Kelvin Probe Force Microscopy. Optical characterization was performed using integrating sphere measurements. Combining the results and understanding obtained from anodising of magnetron sputtered coatings, Al-TiO2 surface composites and their electrochemical behaviour...

  18. Results of the Experiment: Welding of Aluminium Alloy in Microgravity

    Science.gov (United States)

    Ferretti, S.; Amadori, K.; Boccalatte, A.; Alessandrini, M.; Freddi, A.; Persiani, F.; Poli, G.

    2002-01-01

    An experiment on "dendritic growth in aluminium alloy welding" was performed by the UNIBO team during the 3rd Student Parabolic Flight Campaign and the 30th Professional Parabolic Flight Campaign organised by ESA. Its purpose was to achieve a better understanding of crystal growth during tungsten inert gas (TIG) welding of an aluminium alloy to define the main parameters affecting the process under microgravity condition. The experiment had 4 phases : The paper discusses different aspects of the research, paying particularly attention not only to the influence of gravity, but also to other factors influencing welding microstructure, such as the Marangoni effect and the thermal transfer from the electrode to the material. The paper conclude the dissertation of the results offering new perspectives for welding studies and proposing a new approach to the scientific community to investigate this materials processes for manufacturing.

  19. Metallurgical aspects of corrosion resistance of aluminium alloys

    Energy Technology Data Exchange (ETDEWEB)

    Reboul, M.C. [Pechiney Voreppe Research Centre France (France); CNRS-INP Grenoble, SIMAP-INP Grenoble, Universite France, Saint Martin d' Heres Cedex (France); Baroux, B. [SIMAP-INP, Grenoble University, 1130 rue de la piscine, Saint Martin d' Heres Cedex (France)

    2011-03-15

    Aluminium is the second most often used metal after steel. In this paper, the most current uses of aluminium alloys are first summarised. Then, their different corrosion modes, i.e. pitting, crevice, filiform, galvanic and structural corrosion (including inter-granular, exfoliation and stress corrosion cracking) are reviewed, with particular attention paid to metallurgical factors controlling the corrosion process. For each mode, some instances of possible in-service failure are given, followed by the discussion of the involved mechanisms and the presentation of appropriate solutions to prevent corrosion. Last, passivity and polarisation behaviour are discussed with reference to stainless steels. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  20. Analysis of the dynamics of liquid aluminium: recurrent relation approach

    International Nuclear Information System (INIS)

    Mokshin, A V; Yulmetyev, R M; Khusnutdinoff, R M; Haenggi, P

    2007-01-01

    By use of the recurrent relation approach (RRA) we study the microscopic dynamics of liquid aluminium at T = 973 K and develop a theoretical model which satisfies all the corresponding sum rules. The investigation covers the inelastic features as well as the crossover of our theory into the hydrodynamical and the free-particle regimes. A comparison between our theoretical results with those following from a generalized hydrodynamical approach is also presented. In addition to this we report the results of our molecular dynamics simulations for liquid aluminium, which are also discussed and compared to experimental data. The results obtained reveal (i) that the microscopical dynamics of density fluctuations is defined mainly by the first four even frequency moments of the dynamic structure factor, and (ii) the inherent relation of the high-frequency collective excitations observed in experimental spectra of dynamic structure factor S(k,ω) with the two-, three- and four-particle correlations

  1. Establishment of integrated information displays in aluminium surfaces using nanomanufacturing

    DEFF Research Database (Denmark)

    Prichystal, Jan; Hansen, Hans Nørgaard; Bladt, Henrik H.

    2006-01-01

    Bang & Olufsen has been working with a method for manufacturing ultra-thin structures in aluminium that can be penetrated by light. This work has resulted in a patent describing how to obtain this effect by material removal in local areas in a solid material. The idea behind an invisible display...... in aluminium concerns the processing of a metal workpiece in such a way that microcavities are formed from the backside of the workpiece. The microcavities must not penetrate the metal front side, but an ultra-thin layer of metal is left. It is possible to shine light through this layer. By ordering...... microcavities in a matrix, different symbols can be obtained by shining light from the backside of the workpiece. When there is no light from the backside, the front surface seems totally untouched. Three different manufacturing processes were investigated to achieve the desired functionality: laser...

  2. Persistent Skin Reactions and Aluminium Hypersensitivity Induced by Childhood Vaccines.

    Science.gov (United States)

    Salik, Elaha; Løvik, Ida; Andersen, Klaus E; Bygum, Anette

    2016-11-02

    There is increasing awareness of reactions to vaccination that include persistent skin reactions. We present here a retrospective investigation of long-lasting skin reactions and aluminium hypersensitivity in children, based on medical records and questionnaires sent to the parents. In the 10-year period 2003 to 2013 we identified 47 children with persistent skin reactions caused by childhood vaccinations. Most patients had a typical presentation of persisting pruritic subcutaneous nodules. Five children had a complex diagnostic process involving paediatricians, orthopaedics and plastic surgeons. Two patients had skin biopsies performed from their skin lesions, and 2 patients had the nodules surgically removed. Forty-two children had a patch-test performed with 2% aluminium chloride hexahydrate in petrolatum and 39 of them (92%) had a positive reaction. The persistent skin reactions were treated with potent topical corticosteroids and disappeared slowly. Although we advised families to continue vaccination of their children, one-third of parents omitted or postponed further vaccinations.

  3. Buffering effects on electrograining of aluminium in nitric acid

    International Nuclear Information System (INIS)

    Koroleva, E.V.; Thompson, G.E.; Skeldon, P.; Hollrigl, G.; Lockwood, S.; Smith, G.

    2005-01-01

    Electrograining of a binary Al-Si alloy has been undertaken in nitric acid based electrolytes, with the resultant surfaces examined by scanning and transmission electron microscopies. Depending on electrograining conditions, the pit appearance varies from hemispherical to large lateral pits, with the latter favoured in relatively acidic electrolytes. The conditions prevailing in the pit have been explored through use of aluminium ion additions to the nitric acid electrolyte as well as additions of species which influence the precipitation and dissolution of aluminium hydroxide. These confirm that control of the pit solution pH, through hydroxide generation, as a result of the selected electrograining conditions and consequent anodic and cathodic polarisation, enables tailoring of the resultant electrograined surface appearance

  4. Spall behaviour of single crystal aluminium at three principal orientations

    Science.gov (United States)

    Owen, G. D.; Chapman, D. J.; Whiteman, G.; Stirk, S. M.; Millett, J. C. F.; Johnson, S.

    2017-10-01

    A series of plate impact experiments have been conducted to study the spall strength of the three principal crystallographic orientations of single crystal aluminium ([100], [110] and, [111]) and ultra-pure polycrystalline aluminium. The samples have been shock loaded at two impact stresses (4 GPa and 10 GPa). Significant differences have been observed in the elastic behaviour, the pullback velocities, and the general shape of the wave profiles, which can be accounted for by considerations of the microscale homogeneity, the dislocation density, and the absence of grain boundaries in the single crystal materials. The data have shown that there is a consistent order of spall strength measured for the four sample materials. The [111] orientation has the largest spall strength and elastic limit, followed closely by [110], [100], and then the polycrystalline material. This order is consistent with both quasi-static data and geometrical consideration of Schmid factors.

  5. Environment pollution with aluminium around a coalburning electric power plant

    International Nuclear Information System (INIS)

    Hermann, J.

    1997-01-01

    The experiments were carried out from November 1991 till November 1993 on the area surrounding an electric power plant within the circle of 20 km diameter and five geographical directions (N, S, SE, E, W). The results presented in this paper have indicated the threats caused by emissions of the power plant ashes and dusts. Mean aluminium content in soil has been multiply surpassed on the area studied. This must have as impact on fauna and flora. The distribution and intensity of pollution is determined first of all by the distance from the emitters and direction of prevailing winds. A part of aluminium contained in water soluble compounds can be distributed on large areas, what adds a lot to the threat to animals. That is why high chimneys do not solve the problem of pollution around big industrial plants. (author)

  6. Mechanisms of de cohesion in cutting aluminium matrix composites

    International Nuclear Information System (INIS)

    Cichosz, Piotr; Karolczak, Pawel; Kuzinovski, Mikolaj

    2008-01-01

    In this paper properties and applications of aluminium matrix composites are presented with a composite reinforced with saffil fibres selected for topical study. Behavior of matrix and reinforcement during machining with a cutting tool is analyzed. The paper presents an explosive quick-stop device designed to obtain undisturbed machined surface for examination. Meso hardness measurements of deformed structure, resultant chips and built-up-edge were carried out. Scanning micrographs of machined surface are presented with morphology and types of chips analysed. Values of the fibrousness angle ψ and thickening index k h of chip are evaluated. The research performed has enabled the authors to define mechanisms of e cohesion during cutting aluminium matrix composites. The results received for composite material are compared with those pertinent to aluminum alloys.

  7. Beam loading

    CERN Document Server

    Gamp, Alexander

    2013-01-01

    We begin by giving a description of the radio-frequency generator-cavity-beam coupled system in terms of basic quantities. Taking beam loading and cavity detuning into account, expressions for the cavity impedance as seen by the generator and as seen by the beam are derived. Subsequently methods of beam-loading compensation by cavity detuning, radio-frequency feedback and feedforward are described. Examples of digital radio-frequency phase and amplitude control for the special case of superconducting cavities are also given. Finally, a dedicated phase loop for damping synchrotron oscillations is discussed.

  8. Beam loading

    International Nuclear Information System (INIS)

    Gamp, Alexander

    2013-01-01

    We begin by giving a description of the radio-frequency generator-cavity-beam coupled system in terms of basic quantities. Taking beam loading and cavity detuning into account, expressions for the cavity impedance as seen by the generator and as seen by the beam are derived. Subsequently methods of beam-loading compensation by cavity detuning, radio-frequency feedback and feedforward are described. Examples of digital radio-frequency phase and amplitude control for the special case of superconducting cavities are also given. Finally, a dedicated phase loop for damping synchrotron oscillations is discussed. (author)

  9. Numerical modeling of aluminium foam on two scales

    Czech Academy of Sciences Publication Activity Database

    Němeček, J.; Denk, F.; Zlámal, Petr

    Roč. 267, September (2015), s. 506-516 ISSN 0096-3003 R&D Projects: GA ČR(CZ) GAP105/12/0824 Institutional support: RVO:68378297 Keywords : closed-cell aluminium foam * Alporas * multiscale modeling * homogenization * FFT * finite element modeling Subject RIV: JI - Composite Materials Impact factor: 1.345, year: 2015 http://www.sciencedirect.com/science/article/pii/S0096300315001162

  10. Study of twist boundaries in aluminium. Structure and intergranular diffusion

    International Nuclear Information System (INIS)

    Lemuet, Daniel

    1981-01-01

    This research thesis addresses the study of grain boundaries in oriented crystals, and more particularly the systematic calculation of intergranular structures and energies of twist boundaries of <001> axis in aluminium, the determination of intergranular diffusion coefficients of zinc in a set of twist bi-crystals of same axis encompassing a whole range of disorientations, and the search for a correlation between these experimental results and calculated structures

  11. Prediction of deformation textures in asymmetric rolling of aluminium alloys

    OpenAIRE

    Shore, Diarmuid; Nguyen-Minh, Tuan; Kestens, Leo; Van Bael, Albert

    2015-01-01

    Asymmetric cold rolling (ASR) has been shown to have potential to improve the formability of aluminium sheet alloys in deep drawing by increasing the normal plastic anisotropy, mainly as a result of the additional shear strains it imposes and the consequent alteration of the crystallographic texture. It is generally found that the process produces shear strains that vary across the sheet thickness, resulting in heterogeneity of the texture and related properties. While it may be a typical des...

  12. Methods for production of aluminium powders and their application fields

    Energy Technology Data Exchange (ETDEWEB)

    Gopienko, V.G.; Kiselev, V.P.; Zobnina, N.S. (Vsesoyuznyj Nauchno-Issledovatel' skij i Proektnyj Inst. Alyuminievoj, magnievoj i ehlektrodnoj promyshlennosti (USSR))

    1984-12-01

    Different types of powder products made of alluminium and its alloys (powder, fine powders, granules and pastes) as well as their basic physicochemical properties are briefly characterized. The principle methods for alluminium powder production are outlined: physicochemical methods, the melt spraying by compressed gas being the mostly developed among them, and physico-mechanical ones. Main application spheres for powder productions of aluminium and its alloys are reported in short.

  13. Methods for production of aluminium powders and their application fields

    International Nuclear Information System (INIS)

    Gopienko, V.G.; Kiselev, V.P.; Zobnina, N.S.

    1984-01-01

    Different types of powder products made of alluminium and its alloys (powder, fine powders, granules and pastes) as well as their basic physicochemical properties are briefly characterized. The principle methods for alluminium powder production are outlined: physicochemical methods, the melt spraying by compressed gas being the mostly developed among them, and physico-mechanical ones. Main application spheres for powder productions of aluminium and its alloys are reported in short

  14. Modelling the strength of an aluminium-steel nailed joint

    Science.gov (United States)

    Goldspiegel, Fabien; Mocellin, Katia; Michel, Philippe

    2018-05-01

    For multi-material applications in automotive industry, a cast aluminium (upper layer) and dual-phase steel (lower layer) superposition joined with High-Speed Nailing process is investigated through an experimental vs numerical framework. Using FORGE® finite-element software, results from joining simulations have been inserted into models in charge of nailed-joint mechanical testings. Numerical Shear and Cross-tensile tests are compared to experimental ones to discuss discrepancy and possible improvements.

  15. Development of Niobium Boron grain retainer for aluminium silicon alloys

    OpenAIRE

    Nowak, Magdalena

    2011-01-01

    This thesis was submitted for the degree of Doctor of Philosophy and awarded by Brunel University Aluminium castings with a large grain structure have poor mechanical properties which are primarily due to casting defects as opposed to fine grain structure. The grain refinement practice using chemical addition is well established for wrought alloys, however in the case of casting alloys, the practice of adding grain refiners and the impact on castability is not well established. The additio...

  16. Mechanical Properties of Spray Cast 7XXX Series Aluminium Alloys

    OpenAIRE

    SALAMCI, Elmas

    2014-01-01

    Mechanical properties of spray deposited and extruded 7xxx series aluminium alloys were investigated in peak aged condition. To study the influence of Zn additions on the mechanical behaviour of spray deposited materials, three alloy compositions were selected, namely: SS70 (11.5% Zn), N707 (10.9% Zn) and 7075 (5.6% Zn). After ageing treatment, notched and unnotched specimens of spray deposited alloys were subjected to tensile tests at room temperature. Experimental results showed...

  17. Aluminium, extractable from soil samples by the acid ammonium acetate soil-testing method

    Directory of Open Access Journals (Sweden)

    Osmo Mäkitie

    1968-05-01

    Full Text Available The extractant, 0.5 M acetic acid –0.5 M ammonium acetate at pH 4.65, which is used in soil-testing, extracts relatively high amounts of aluminium from acid soils. The mean values of acetate-extractable aluminium at pH 4.65, 1.75 meq Al/100 g of soil, and of exchangeable aluminium (M KCI extraction, 0.41 meq Al were obtained from a material of 30 samples of acid soils (Table 2. Several other acetic acid ammonium acetate extractants, from M acetic acid to M ammonium acetate solution were also used for studying the extractability of soil aluminium. The soil-testing extractant can be used for the estimation of the soluble amounts of aluminium in acid soils, however, further studies are needed for a better interpretation of the ammonium acetate extractable (at pH 4.65 aluminium in our soils.

  18. Disruption of an Alumina Layer During Sintering of Aluminium in Nitrogen

    Directory of Open Access Journals (Sweden)

    Pieczonka T.

    2017-06-01

    Full Text Available Aluminium oxide layer on aluminium particles cannot be avoided. However, to make the metal-metal contacts possible, this sintering barrier has to be overcome in some way, necessarily to form sintering necks and their development. It is postulated that the disruption of alumina layer under sintering conditions may originate physically and chemically. Additionally, to sinter successfully non alloyed aluminium powder in nitrogen, the operation of both types mechanism is required. It is to be noted that metallic aluminium surface has to be available to initiate reactions between aluminium and the sintering atmosphere, i.e. mechanical disruption of alumina film precedes the chemical reactions, and only then chemically induced mechanisms may develop. Dilatometry, gravimetric and differential thermal analyses, and microstructure investigations were used to study the sintering response of aluminium at 620°C in nitrogen, which is the only sintering atmosphere producing shrinkage.

  19. Aluminium in food and daily dietary intake assessment from 15 food groups in Zhejiang Province, China.

    Science.gov (United States)

    Zhang, Hexiang; Tang, Jun; Huang, Lichun; Shen, Xianghong; Zhang, Ronghua; Chen, Jiang

    2016-06-01

    Aluminium was measured in 2580 samples of 15 food groups and dietary exposure was estimated. Samples were purchased and analysed during 2010 to 2014. High aluminium levels were found in jellyfish (mean 4862 mg/kg), laver (mean 455.2 mg/kg) and fried twisted cruller (mean 392.4 mg/kg). Dietary exposure to aluminium was estimated for Zhejiang residents. The average dietary exposure to aluminium via 15 food groups in Zhejiang Province was 1.15 mg/kg bw/week, which is below the provisional tolerable weekly intake of 2 mg/kg bw /week. Jellyfish is the main Al contributor, providing 37.6% of the daily intake via these 15 food groups. This study provided new information on aluminium levels and assessment of aluminium (Al) dietary exposure in Zhejiang Province of China.

  20. In vivo monitoring of skeletal aluminium burden in patients with renal failure

    International Nuclear Information System (INIS)

    Ellis, K.J.; Kelleher, S.; Raciti, A.; Savory, J.; Wills, M.

    1988-01-01

    In vivo neutron activation analysis was used to examine the total body and partial body (hand) aluminium levels in patients with end-stage renal failure. Patients maintained on chronic hemodialysis had higher mean body burdens of aluminium than did those clinically managed without dialysis. Approximately 70% of the patients examined indicated elevated levels of body or skeletal aluminium. A significant correlation was observed between the in vivo aluminium/calcium ratio obtained for the hand measurement and the increase in serum aluminium levels following a disferroxamine infusion test. The direct in vivo monitoring of hand Al/Ca values in patients may provide an alternate choice to bone biopsy for the detection of aluminium intoxication. (author) 15 refs.; 5 figs.; 2 tabs

  1. "INHIBITORY EFFECT OF ALUMINIUM ON KCL AND PHENYLEPHRINE INDUCED CONTRACTION IN ISOLATED RAT AORTA"

    Directory of Open Access Journals (Sweden)

    T. Mashhoodi

    2004-10-01

    Full Text Available It has been shown in some investigations that cardiovascular events are the main causes of death in hemodialysis patients. The exact etiology is unknown but some of the articles have reported a relation between aluminium ions in the dialysis solution and cardiovascular disorders. To determine the probable effect of aluminium on vasculature function, in vitro effects of aluminium ion on vasoconstriction induced by KCl (30 mM or phenylephrine (10 µM were investigated using isolated rat aorta. AlCl3 (1-4 mM decreased both KCl and phenylephrine induced contractions in a dose dependent manner (P<0.01. Complete inhibition of the contractions occurred using the higher doses of aluminium. Results of this study suggest that because of inhibitory effects of aluminium on vascular contractions, the probable cardiovascular dysfunction must be considered in aluminium intoxication.

  2. Aluminium intake by INAA of hair: The aerosol intoxication pathway

    International Nuclear Information System (INIS)

    Preoteasa, E.A.; Ionescu, A.; Pantelica, A.; Salagean, M.; Rusu, C.; Moldovan, O.; Ghiordunwscu, Vl.; Marusca, D.

    1997-01-01

    Aluminium is present in healthy human organisms in concentrations that appear to be neither useful nor noxious. However, long term higher Al levels can produce severe bone, renal and cerebral troubles. Here we report the results of the first investigation using the Instrumental Neutron Activation Analysis of human hair aimed to assess the Al contamination in workers from aluminium industry due to aerosol inhalation. Seventy five subjects working at 'Alprom' Inc., Slatina, Romania aluminium processing plant were included in this study. The exposed subjects were casters, crane operators and rolling mill operators. Hair samples were washed with acetone-water-water-water-acetone using bi-distilled water and re-distilled-purified p.a. grade acetone and irradiated for 3 min at a thermal neutron flux of 2.3 x 10 12 n/cm 2 s in the VVR-S reactor. Student's t-test showed the arithmetical mean values of all exposed groups to differ of the control group's one with a good statistical confidence level. In most workers the Al concentration in hair is 2 times higher than normal but in one third of the casters and in two of the rolling mill operators it is on average up to 7 times higher. Substantial Al overload can cause severe osteoporosis or encephalopathies even after retirement from activity. Protection filtering masks and medical therapy based on strong chelant drug deferoxamine are recommended, (authors)

  3. Recycling of aluminium scrap for secondary Al-Si alloys.

    Science.gov (United States)

    Velasco, Eulogio; Nino, Jose

    2011-07-01

    An increasing amount of recycled aluminium is going into the production of aluminium alloy used for automotive applications. In these applications, it is necessary to control and remove alloy impurities and inclusions. Cleaning and fluxing processes are widely used during processing of the alloys for removal of inclusions, hydrogen and excess of magnesium. These processes use salt fluxes based in the system NaCl-KCl, injection of chlorine or mixture of chlorine with an inert gas. The new systems include a graphite wand and a circulation device to force convection in the melt and permit the bubbling and dispersion of reactive and cleaning agents. This paper discusses the recycling of aluminium alloys in rotary and reverberatory industrial furnaces. It focuses on the removal of magnesium during the melting process. In rotary furnaces, the magnesium lost is mainly due to the oxidation process at high temperatures. The magnesium removal is carried out by the reaction between chlorine and magnesium, with its efficiency associated to kinetic factors such as concentration of magnesium, mixing, and temperature. These factors are also related to emissions generated during the demagging process. Improvements in the metallic yield can be reached in rotary furnaces if the process starts with a proper salt, with limits of addition, and avoiding long holding times. To improve throughput in reverberatories, start the charging with high magnesium content material and inject chlorine gas if the molten metal is at the right temperature. Removal of magnesium through modern technologies can be efficiently performed to prevent environmental problems.

  4. Toxicity of indium arsenide, gallium arsenide, and aluminium gallium arsenide

    International Nuclear Information System (INIS)

    Tanaka, Akiyo

    2004-01-01

    Gallium arsenide (GaAs), indium arsenide (InAs), and aluminium gallium arsenide (AlGaAs) are semiconductor applications. Although the increased use of these materials has raised concerns about occupational exposure to them, there is little information regarding the adverse health effects to workers arising from exposure to these particles. However, available data indicate these semiconductor materials can be toxic in animals. Although acute and chronic toxicity of the lung, reproductive organs, and kidney are associated with exposure to these semiconductor materials, in particular, chronic toxicity should pay much attention owing to low solubility of these materials. Between InAs, GaAs, and AlGaAs, InAs was the most toxic material to the lung followed by GaAs and AlGaAs when given intratracheally. This was probably due to difference in the toxicity of the counter-element of arsenic in semiconductor materials, such as indium, gallium, or aluminium, and not arsenic itself. It appeared that indium, gallium, or aluminium was toxic when released from the particles, though the physical character of the particles also contributes to toxic effect. Although there is no evidence of the carcinogenicity of InAs or AlGaAs, GaAs and InP, which are semiconductor materials, showed the clear evidence of carcinogenic potential. It is necessary to pay much greater attention to the human exposure of semiconductor materials

  5. Research progress of aluminium alloy endplates for PEMFCs

    Energy Technology Data Exchange (ETDEWEB)

    Fu, Yu.; Hou, Junbo [Fuel Cell system and Engineering Laboratory, Dalian Institute of Chemical and Physics, Chinese Academy of Sciences, Dalian 116023 (China); Graduate University of Chinese Academy of Sciences, Beijing 100049 (China); Hou, Ming; Yan, Xiqiang; Luo, Xiaokuan; Shao, Zhigang; Yi, Baolian [Fuel Cell system and Engineering Laboratory, Dalian Institute of Chemical and Physics, Chinese Academy of Sciences, Dalian 116023 (China)

    2007-04-15

    The endplate is a crucial component in a proton exchange membrane fuel cell (PEMFC) stack. It can provide the necessary rigidity and strength for the stack. An aluminium alloy is one of the ideal materials for PEMFC endplates because of its low density and high rigidity. But it does not meet the requirements of corrosion resistance and electrical insulation in PEMFC environments. In this work, methods of sealing treatments and the conditions of aluminium alloy anodization were investigated. Corrosion resistances of the samples prepared by different technologies were evaluated in simulated PEMFC environments. The results showed that the corrosion resistance of the samples sealed by epoxy resin was greatly improved compared with those sealed in boiling water, and the samples anodized at a constant current density performed better than those anodized at a constant voltage. By insulation measurements, all of the samples showed good electrical insulation. The aluminium alloy endplate anodized at a constant current density and sealed with thermosetting bisphenol-A epoxy resin exhibited promising potential for practical applications by assembling it in a PEMFC stack and applying a life test. (author)

  6. Hydrogen Incorporation during Aluminium Anodisation on Silicon Wafer Surfaces

    International Nuclear Information System (INIS)

    Lu, Pei Hsuan Doris; Strutzberg, Hartmuth; Wenham, Stuart; Lennon, Alison

    2014-01-01

    Hydrogen can act to reduce recombination at silicon surfaces for solar cell devices and consequently the ability of dielectric layers to provide a source of hydrogen for this purpose is of interest. However, due to the ubiquitous nature of hydrogen and its mobility, direct measurements of hydrogen incorporation in dielectric layers are challenging. In this paper, we report the use of secondary ion mass spectrometry measurements to show that deuterium from an electrolyte can be incorporated in an anodic aluminium oxide (AAO) layer and be introduced into an underlying amorphous silicon layer during anodisation of aluminium on silicon wafers. After annealing at 400 °C, the concentration of deuterium in the AAO was reduced by a factor of two, as the deuterium was re-distributed to the interface between the amorphous silicon and AAO and to the amorphous silicon. The assumption that hydrogen, from an aqueous electrolyte, could be similarly incorporated in AAO, is supported by the observation that the hydrogen content in the underlying amorphous silicon was increased by a factor of ∼ 3 after anodisation. Evidence for hydrogen being introduced into crystalline silicon after aluminium anodisation was provided by electrochemical capacitance voltage measurements indicating boron electrical deactivation in the underlying crystalline silicon. If introduced hydrogen can electrically deactivate dopant atoms at the surface, then it is reasonable to assume that it could also deactivate recombination-active states at the crystalline silicon interface therefore enabling higher minority carrier lifetimes in the silicon wafer

  7. Aluminium base amorphous and crystalline alloys with Fe impurity

    International Nuclear Information System (INIS)

    Sitek, J.; Degmova, J.

    2006-01-01

    Aluminium base alloys show remarkable mechanical properties, however their low thermal stability still limits the technological applications. Further improvement of mechanical properties can be reached by partial crystallization of amorphous alloys, which gives rise to nanostructured composites. Our work was focused on aluminium based alloys with Fe, Nb and V additions. Samples of nominal composition Al 90 Fe 7 Nb 3 and Al 94 Fe 2 V 4 were studied in amorphous state and after annealing up to 873 K. From Moessbauer spectra taken on the samples in amorphous state the value of f-factor was determined as well as corresponding Debye temperatures were calculated. Annealing at higher temperatures induced nano and microcrystalline crystallization. Moessbauer spectra of samples annealed up to 573 K are fitted only by distribution of quadrupole doublets corresponding to the amorphous state. An increase of annealing temperature leads to the structural transformation, which consists in growth of nanometer sized aluminium nuclei. This is partly reflected in Moessbauer parameters. After annealing at 673 K intermetallic phase Al 3 Fe and other Al-Fe phases are created. In this case Moessbauer spectra are fitted by quadrupole doublets. During annealing up to 873 K large grains of Fe-Al phases are created. (authors)

  8. Laser synthesis of aluminium nanoparticles in biocompatible polymer solutions

    Science.gov (United States)

    Singh, Rina; Soni, R. K.

    2014-08-01

    Pulsed laser ablation of Aluminium (Al) in pure water rapidly forms a thin alumina (Al2O3) layer which drastically modifies surface plasmon resonance (SPR) absorption characteristics in deep-UV region. Initially, pure aluminium nanoparticles (NPs) are generated in water without any stabilizers or surfactants at low laser fluence which gradually transform to stable Al-Al2O3 core-shell nanostructure with increasing either residency time or fluence. The role of laser wavelength and fluence on the SPR properties and oxidation characteristics of Al NPs has been investigated in detail. We also present a one-step in situ synthesis of oxide-free stable Al NPs in biocompatible polymer solutions using laser ablation in liquid method. We have used nonionic polymers (PVP, PVA and PEG) and anionic surfactant (SDS) stabilizer to suppress the Al2O3 formation and studied the effect of polymer functional group, polymeric chain length, polymer concentration and anionic surfactant on the incipient embryonic aluminium particles and their sizes. The different functional groups of polymers resulted in different oxidation states of Al. PVP and PVA polymers resulted in pure Al NPs; however, PEG and SDS resulted in alumina-modified Al NPs. The Al nanoparticles capped with PVP, PVA, and PEG show a good correlation between nanoparticle stability and monomeric length of the polymer chain.

  9. Thermodynamics of carbon deoxidation and aluminium deoxidation of refractory metals

    International Nuclear Information System (INIS)

    Garg, S.P.; Sundaram, C.V.

    1975-01-01

    Carbon has been used for removing the last traces of oxygen from many refractory metals by evaporation of CO at high temperature and vacuum. Similar purification can also be achieved employing aluminium deoxidation by evaporation of Al 2 Osub(g). In the present paper a theoretical thermodynamic approach has been attempted to evaluate the deoxidation tendencies of refractory metals of groups IV to VI by these two processes. Expressions have been theoretically derived, relating the concentration product of carbon and oxygen in the metal (which is a measure of the carbon deoxidation tendency of the metal) with temperature and pressure, for various M-C-O systems. Similarly the relative vapour pressure values of Alsub(2)Osub(g),Alsub(g)andMO(g) (suboxide of the metal) over various M-Al-O systems have been calculated as a function of aluminium and oxygen contents of the metal. From these analyses, it has been shown that a substantial amount of oxygen can be removed from M-Al-O alloys by aluminium deoxidation. The estimated values are compared with the reported values based on experiment. (author)

  10. Effects of aluminium oxide nanoparticles on bacterial growth

    Directory of Open Access Journals (Sweden)

    Doskocz Nina

    2017-01-01

    Full Text Available Production and wide application of nanomaterials have led to nanotechnology development but their release to environment and the induction of toxic reactions, affects the natural microbial communities. Therefore, studies on the impact of nanoparticles on microorganisms and environment are required and needed. The aim of this study was to assess the impact of aluminium oxide nanoparticles on the growth of Pseudomonas putida. To compare the harmfulness of different forms of aluminium oxide, the ecotoxicity of its macro-forms was also evaluated in the study. Research showed that the exposure to nanoparticles can negatively influence microorganisms. The EC50-16h determined in this study was 0.5 mg/l, and NOEC equaled 0.19 mg/l. Nano-Al2O3 proved to be more toxic to P. putida than aluminium oxide. This indicates that the nano-form of a given substance demonstrates different properties and may constitute a far greater danger for the environment than the same substance in the large form. According to EU and US EPA criteria, nano-Al2O3 proved to be very toxic and highly toxic, respectively. Changes in bacterial communities caused by nanoparticles may affect the normal biological, chemical and nutrient cycle in the ecosystem and the effect triggered by nanomaterials in relation to other organisms is unpredictable.

  11. Numerical simulation of the laser welding process for the prediction of temperature distribution on welded aluminium aircraft components

    Science.gov (United States)

    Tsirkas, S. A.

    2018-03-01

    The present investigation is focused to the modelling of the temperature field in aluminium aircraft components welded by a CO2 laser. A three-dimensional finite element model has been developed to simulate the laser welding process and predict the temperature distribution in T-joint laser welded plates with fillet material. The simulation of the laser beam welding process was performed using a nonlinear heat transfer analysis, based on a keyhole formation model analysis. The model employs the technique of element ;birth and death; in order to simulate the weld fillet. Various phenomena associated with welding like temperature dependent material properties and heat losses through convection and radiation were accounted for in the model. The materials considered were 6056-T78 and 6013-T4 aluminium alloys, commonly used for aircraft components. The temperature distribution during laser welding process has been calculated numerically and validated by experimental measurements on different locations of the welded structure. The numerical results are in good agreement with the experimental measurements.

  12. Aluminium and Aroma Compound Concentration in Beer During Storage at Different Temperatures

    Directory of Open Access Journals (Sweden)

    Marija Soldo Gjeldum

    2006-01-01

    Full Text Available Problem of aluminium in beer has been elaborated in several papers over the last decade. However, the effect of aluminium on organoleptic properties of beer has been observed in few papers where it has been stated that aluminium gives beer a »metallic« and bitter flavour without any observations on particular aroma compound changes. Also, the number of reports on precise changes of aroma components throughout different storage conditions is surprisingly scarce. In order to investigate the changes of aluminium concentration along with aroma compound changes, graphite furnace-atomic absorption spectrophotometry (GF-AAS with Zeeman background correction and gas chromatography with static headspace sampler (GC-HSS were used in this work. Analyses were conducted periodically throughout seven months of storage on three different brands of beer from name breweries. Samples were taken before and after filling in aluminium cans. One part of samples was stored in a refrigerator (4 °C and the other in a thermostatic chamber (22 °C. The effects of beer brand and storage conditions on aluminium concentration and level of aroma compounds were measured. To prove the effect of aluminium concentration on the changes of aroma compounds, the adequate level of aluminium sulphate was added to bottled beer samples stored at 28 °C. Although different beer types showed significantly different aluminium concentration, it could be the result of other factors (different batches of identical beer type showed significantly different aluminium concentration as well. Samples that were stored in the refrigerator were protected from aluminium migration from the can to the beer and showed increased aroma stability. Level of aroma constituents of analyzed beer brands was significantly different. Elevated aluminium concentration did not have any noticeable effect on the level of aroma compounds in beer samples stored at 28 °C.

  13. A note on the behind armour effects from perforated alumina/aluminium targets

    OpenAIRE

    Hazell, P. J.; Fellows, N. A.; Hetherington, J. G.

    1998-01-01

    A thin, ceramic-faced armour, separated from a thick metal block, has been subjected to high-velocity impact by a 6.35 mm diameter steel sphere. Experimental work was carried out which compared firings into ceramic-faced aluminium armour, separated from thick aluminium witness blocks, with firings into the thick aluminium blocks alone. The depth of penetration and the area of damage were measured and an estimated percentage weight saving due to the inclusion of the ceramic-f...

  14. Cashew Nut Testa Tannin: Assessing its Effects on the Corrosion of Aluminium in HCl

    OpenAIRE

    Nnaji, Nnaemeka J. N; Obi-Egbedi, Nelson O; Okoye, Chukwuma O. B

    2014-01-01

    Cashew nut testa tannin (CASTAN) has been found to inhibit the corrosion of aluminium in hydrochloric acid solutions using gravimetric, thermometric and UV/visible spectrophotometric techniques. CASTAN inhibition was by adsorption on aluminium following Temkin isotherm in 0.1 M HCl and Langmuir isotherm in 0.5 M and 2.0 M HCl at 303 Kelvin. Physical adsorption on aluminium has been proposed in studied HCl solutions; therefore, CASTAN is a cathodic inhibitor. Earlier reports (1) showed CASTAN ...

  15. The effects of radiation on aluminium alloys in the core of energy nuclear reactors

    International Nuclear Information System (INIS)

    Petrossian, V.G.

    1995-01-01

    One of the attractive directions in the worldwide practice of nuclear installations is the replacement of expensive zirconium alloy with more cheap materials, particularly aluminium allo. For Heat Supply Nuclear Plants (HSNP) with approximately 473 K core temperatures, the use of heat-resistant aluminium alloys seems to be reasonable. The present work is concerned with the studies on radiation effects on aluminium alloy, and interaction between the alloy and coolant in the reactor core. (author). 2 refs., 3 figs., 1 tab

  16. Grain Refinement of Commercial EC Grade 1070 Aluminium Alloy for Electrical Application

    OpenAIRE

    Hassanabadi, Massoud

    2015-01-01

    The aluminium alloys for electrical conductivity applications are generally not grain refinedsince the addition of grain refiners drops the electrical conductivity by introducing impuritiesinto the melt. Non-grain refined aluminium may lead to bar fracture and cracks during themetalworking process. The present study focuses to find an optimum balance between the grain refiner addition andthe electrical conductivity of commercial EC grade 1070 aluminium alloy for electricalapplication. In orde...

  17. Study of computerized tomography using neutron beam

    International Nuclear Information System (INIS)

    Pereira, W.W.

    1991-05-01

    This paper aims to demonstrate the advantages, shortcomings and complementaries of a tomography development using neutrons over the one employing gamma rays in the context of their applications to non destructive essays. A simulated experimental study was performed in order to compare the two aforementioned tomographic procedures as applied to some materials. These materials were chosen for their clear advantages and complementaries as, for instance, aluminium, iron, plastic and aluminium hydroxide. In this work two tomographic systems, are employed both with parallel beams. The first with a gamma radiation source (Caesium-137), with an energy of 662 KeV and an activity of 3,9 x 10 9 Bq (100 mCi) and the second one employing a neutron source, the Argonaut Reactor of the Instituto de Engenharia Nuclear, IEN/CNEN, from where the thermal neutron beam of about 10 5 n/(cm.s) was obtained. It is possible to conclude from the simulated and experimental results, by means of image analysis and distortion measurements, that for a given material the adequate radiation and its energy may be chosen so as to better characterize it. (author)

  18. [Severity factors of aluminium phosphide poisoning (Phostoxin)].

    Science.gov (United States)

    Hajouji Idrissi, M; Oualili, L; Abidi, K; Abouqal, R; Kerkeb, O; Zeggwagh, A A

    2006-04-01

    To determine characteristics of acute aluminum phosphide poisoning (AAlPP) and to evaluate its severity factors. Retrospective cohort study. Consecutive cases of AAlPP admitted in medical ICU (Hospital Avicenne, Rabat, Morocco) between January 1992 and December 2002 were studied. AAlPP was identified by history, symptoms and toxicological results. Almost 50 parameters have been collected and compared between survivors and non-survivors groups. Data were analyzed using Fisher exact test and Mann-Whitney test. Twenty-eight patients were enrolled: 17 female and 11 male, average age = 24+/-11 years, SAPS II = 24.4+/-14.5. The ingested dose was 3.3+/-1.8 g. The self-poisoning was observed in 27 cases and delay before hospital admission was 11+/-13 hours. Mean Glasgow coma scale was 14+/-2. Shock was found in 22 (79%) cases. Average pH was 7.1+/-0.4 and bicarbonate concentration was 16.3+/-8.8 mmol/l. The ECG abnormalities were noted in 20 (72%) cases. The average mortality rate was 61%. The prognostic factors were SAPS II (p = 0.031), Apache II (p = 0.037), shock (p = 0.022), ECG abnormalities (p = 0.05), use of vasoactive drugs (p = 0.05) and use of mechanical ventilation (p = 0.003). AAlPP induced a significantly high mortality and haemodynamic disturbances were a risk factor of poor outcome.

  19. Low temperature oxidation of niobium alloy with silicon-aluminium coating

    International Nuclear Information System (INIS)

    Lazarev, Eh.M.; Sapozhnikova, L.V.; Shabanova, M.E.; Pod'yachev, V.N.; Kornilova, Z.I.

    1987-01-01

    Using the gravimetry methods heat resistance of niobium-titanium-aluminium alloy in the air and at 700 deg C in the initial state and when it is protected by silicide-aluminium coatings (with variable content of aluminium) is investigated. Using X-ray diffraction and micro X-ray diffraction analyses, mechanisms of the alloy oxidation and the coating protective effect are studied. The role of aluminium in the formation of coatings is analyzed and according to bend tests the plasticity of the coatings is evaluated

  20. Improving the wettability of 2024 aluminium alloy by means of cold plasma treatment

    Science.gov (United States)

    Polini, W.; Sorrentino, L.

    2003-05-01

    Aluminium alloys are heavily used to manufacture structural parts in the aeronautic industry because of its lightness and its corrosion resistance. These alloys are successfully used in other industrial fields too, such as railway, automotive and naval industries. The need to contrast the severe use conditions and the heavy stresses developing in aeronautic field implies to protect the surfaces of the structures in aluminium alloy by any deterioration. To preserve by deterioration, it is necessary to make aluminium more suitable to be coated by protective paint. In the aeronautic industry, a complex and critical process is used in order to enhance both wettability and adhesive properties of aluminium alloy surfaces. Cold plasma treatment represents an efficient, clean and economic alternative to activate aluminium surfaces. The present work deals with air cold plasma treatment of 2024 aluminium alloy surfaces. The influence of dc electrical discharge cold plasma parameters on wettability of 2024 aluminium alloy surfaces has been studied. A set of process variables (voltage, time and air flow rate) has been identified and used to conduct some experimental tests on the basis of design of experiment (DOE) techniques. The experimental results show that the proposed plasma process may considerably increase aluminium alloy wettability. These results represent the first step in trying to optimise the aluminium adhesion by means of this non-conventional manufacturing process.